Hydrophilic coating composition

Abstract: Hydrophilic coating compositions including, on a solid basis, (a) 0.3-6 percent by weight of polyvinyl pyrrolidone having a polymerization degree of 10-1000; and (b) 1-10 percent by weight of polyvinyl alcohol having a saponification degree of 80% or more and a polymerization degree of 100-1000, the weight ratio of the component (a) to the components (a) and (b), (a)/[(a)+(b)], being in the range of 0.1-0.9, are useful (a)/[(a)+(b)], being in the range of 0.1-0.9, are useful for imparting corrosion resistance and hydrophilic nature to aluminum articles such as heat exchanger fins.

Description: The present invention relates to a hydrophilic coating composition, to aluminum members such as heat exchanger fins coated therewith and to a bath containing such a hydrophilic coating composition. More particularly, it relates to a hydrophilic coating composition for imparting a good corrosion resistance and a high hydrophilic nature to aluminum members such as fins of heat exchangers while reducing unpleasant odors which are generated from the heat exchangers. Since aluminum and its alloys are light and have good workability and heat conductance, they are widely used for fins of heat exchangers. Recently more and more air conditioners have been used not only for cooling but also for warming and dehumidification; aluminum alloy fins are generally used in the heat exchanger parts of these air conditioners. However, it is observed that moisture tends to be condensed and deposited as water droplets on the fin surfaces of air conditioners during cooling operations. If the fin surface is water-repellent, this condensed water tends to be deposited in a hemispherical form on the fin surface or forms bridges between the fins, preventing smooth air flow, which in turn increases resistance of air flow, thereby decreasing heat exchange efficiency. In addition, although aluminum and its alloys are essentially excellent in corrosion resistance, it is likely that condensed water remaining on the aluminum fin surfaces for a long period of time functions like an oxygen concentration cell, and that contaminants in the air are absorbed and concentrated in the condensed water. As a result, a hydration reaction and a corrosion reaction are accelerated. Corrosion products accumulate on the aluminum fin surfaces, thereby deteriorating heat exchange performance, and are blown out of the air conditioners as white fine powders together with hot air during warming operations in the winter season. This also causes unpleasant odor. To solve these problems, various attempts have been made to form on aluminum fin surfaces coatings for improving their corrosion resistance and hydrophilic nature. For instance, Japanese Patent Laid-Open No. 1-299877 discloses a surface treatment agent comprising fully-saponified polyvinyl alcohol, a water-soluble polyamide resin and a urea resin at a weight ratio of 1 : 0.5-2 : 0.01-0.5, and water. A bath containing 2-10 weight %, on a solid basis, of the surface treatment agent is used for surface treatment of the aluminum fins of heat exchangers. Japanese Patent Laid-Open No. 1-240688 discloses an aluminum fin having a corrosion-resistant chemical primer coating and a hydrophilic coating comprising a benzimidazole compound. Further, Japanese Patent Laid-Open No. 3-49944 discloses a heat exchanger made of aluminum and comprising (a) tubes made of aluminum through which a fluid flows, (b) fins made of aluminum and arranged between the tubes for accelerating heat exchange between the fluid and air, (c) a first protective chemical coating layer formed on the tubes, (d) a second protective layer formed on the first protective layer containing an antimicrobial agent such as 2,2-dithiobis(pyridine-1-oxide). However, each of the coatings disclosed in the above references fails to show a good hydrophilic nature and sufficient effect of preventing unpleasant odor. The conventional surface treatment technologies for heat exchangers fail to provide coatings which have not only sufficient hydrophilic nature, corrosion resistance and strength but also adequate odor-preventing effect. As a result of intense research in view of the above problems, the inventors have found that a combination of polyvinyl pyrrolidone having a particular range of polymerization degree and polyvinyl alcohol having particular ranges of saponification degree and polymerization degree can, at a particular weight ratio, provide a coating having good hydrophilic nature and corrosion resistance with substantially reduced unpleasant odor. The present invention is based on this finding. According to one aspect of the present invention there is provided a hydrophilic coating composition comprising, on a solid basis, (a) 0.3-6 parts by weight of polyvinyl pyrrolidone having a polymerization degree of 10-1000; and (b) 1-10 parts by weight of polyvinyl alcohol having a saponification degree of 80% or more and a polymerization degree of 100-1000, the weight ratio of the component (a) to the components (a) and (b), (a)/[(a)+(b)], being in the range of 0.1-0.9. The balance of the coating composition, e.g. to 100 parts by weight, may include one or more additives as described in greater detail hereinafter, in addition to water and/or other solvents. The invention further provides for use of the coating compositions in a hydrophilic coating bath, preferably formulated such that the solids concentration of the bath is 10-200 g/l, e.g. in the coating of aluminum articles (which term is used herein to include aluminum alloy articles) such as heat exchanger fins, and additionally embraces the novel coated aluminum members obtainable thereby. The hydrophilic coating composition of the present invention comprises (a) polyvinyl pyrrolidone having a polymerization degree of 10-1000; and (b) polyvinyl alcohol having a saponification degree of 80% or more and a polymerization degree of 100-1000. (a) Polyvinyl pyrrolidone A typical example of the polyvinyl pyrrolidone used in the present invention is represented by the following formula: wherein n represents the polymerization degree. The above polyvinyl pyrrolidone may be produced by polymerizing N-vinyl-2-pyrrolidone to a polymerization degree of 10-1000. When the polymerization degree of the polyvinyl pyrrolidone is smaller than 10, the resulting hydrophilic coating composition shows poor film-forming properties and poor unpleasant odor-suppressing effect, and its hydrophilic nature is rapidly deteriorated as the time passes. On the other hand, when the polymerization degree of the polyvinyl pyrrolidone exceeds 1000, good hydrophilic nature does not last long, and the unpleasant odor-suppressing effect is rather reduced. The polymerization degree "n" of the polyvinyl pyrrolidone is preferably 80-600, more preferably 100-360. In order to provide the hydrophilic coating composition with good film-forming properties and long-lasting hydrophilic nature, the polyvinyl pyrrolidone should be contained in the hydrophilic coating composition in an amount of 0.3-6 parts 5 by weight on a solid basis. When the amount of the polyvinyl pyrrolidone is smaller than 0.3 parts by weight, it fails to show a long-lasting hydrophilic nature. On the other hand, when the amount of the polyvinyl pyrrolidone exceeds 6 parts by weight, the film-forming property of the hydrophilic coating composition becomes poor and generates unpleasant odor. The amount of the polyvinyl pyrrolidone is preferably 0.5-5 parts by weight, more preferably 0.6-4 parts by weight. In the present invention, it is preferable to combine two types of polyvinyl pyrrolidone; first one having a lower polymerization degree (hereinafter referred to as "low-polymerization degree polyvinyl pyrrolidone"), and second one having a higher polymerization degree (hereinafter referred to as "high-polymerization degree polyvinyl pyrrolidone"). The low-polymerization degree polyvinyl pyrrolidone has a polymerization degree of 10-50, and the high-polymerization degree polyvinyl pyrrolidone has a polymerization degree of 100-500. By combining the above two types of polyvinyl pyrrolidone, the resulting hydrophilic coating composition shows better film-forming property and longer-lasting hydrophilic nature. This mechanism is not necessarily clear, but it may be considered that when the two types of polyvinyl pyrrolidone having different polymerization degrees are used, the low-polymerization degree polyvinyl pyrrolidone is predominantly cross-linked in the process of a hardening reaction, thereby slowing the cross-linking of the high-polymerization degree polyvinyl pyrrolidone. As a result, a higher hydrophilic nature can be achieved. Unless the polymerization degrees of the two types of polyvinyl pyrrolidone are within the above ranges, either one of the film-forming property and the capability of showing a long-lasting hydrophilic nature may be poor. The total amount of the low-polymerization degree polyvinyl pyrrolidone and the high-polymerization degree polyvinyl pyrrolidone is 0.3-6 parts by weight, preferably 0.6-4 parts by weight, on a solid basis. Advantageously the weight ratio of the low-polymerization degree polyvinyl pyrrolidone to the high-polymerization degree polyvinyl pyrrolidone is 1/1.5 - 1/3.0. When the weight ratio of the high-polymerization degree polyvinyl pyrrolidone to the low-polymerization degree polyvinyl pyrrolidone is lower than 1.5, the hydrophilic coating composition may not exhibit the desired long-lasting hydrophilic nature. On the other hand, when the weight ratio exceeds 3.0 it may detract from the film-forming property of the hydrophilic coating composition. The preferred weight ratio is 1/2 - 1/2.5. Further, three or more types of polyvinyl pyrrolidone having different polymerization degrees may be contained in the hydrophilic coating composition. (b) Polyvinyl alcohol A typical example of the polyvinyl alcohol used in the present invention may be expressed by the following formula: wherein m represents the number of saponified structure units, and n represents the number of unsaponified structure units. The above polyvinyl alcohol should have a saponification degree of 80% or more, and a polymerization degree (m+n) of 100-1000. When the polyvinyl alcohol has a saponification degree lower than 80% or has a polymerization degree larger than 1000, it shows a poor hydrophilic nature. On the other hand, when it has a polymerization degree smaller than 100, it shows poor film-forming property and unpleasant odor-suppressing effect. The preferred saponification degree is 90% or more, and the preferred polymerization degree is 200-600. Incidentally, the saponification degree and the polymerization degree herein are measured according to JIS K6725 5.2 and JIS K6725 5.4, respectively. The polyvinyl alcohol having a saponification degree of 80% or more and a polymerization degree of 100-1000 functions to suppress unpleasant odor and to improve hydrophilic nature. To achieve these functions effectively, the amount of the polyvinyl alcohol should be 1-10 parts by weight on a solid basis. When the amount of the polyvinyl alcohol is smaller than I part by weight, the hydrophilic coating composition shows poor film-forming property and unpleasant odor-suppressing effect. On the other hand, when it exceeds 10 parts by weight, the hydrophilic coating composition fails to have a long-lasting hydrophilic nature (determined by contact angle of water) after it is dipped in flowing water. The preferred amount of the polyvinyl alcohol is 2-7 parts by weight. To provide a hydrophilic coating having the required hydrophilic nature without unpleasant odor, the amounts of the above components (a) and (b) in the hydrophilic coating composition are required to meet, in addition to the above-mentioned conditions, the condition that the weight ratio of component (a) to components (a) and (b), (a)/[(a)+(b)], is in the range of 0.1-0.9 on a solid basis. When the ratio of (a)/[(a)+(b)] is less than 0.1, the hydrophilic nature is insufficient though the unpleasant odor-suppressing effect and film-forming property are sufficient. On the other hand, when it exceeds 0.9, the unpleasant odor-suppressing effects and the film-forming ability become poor. The preferred weight ratio of (a)/[(a)+(b)] is 0.2-0.8. (c) Other components The hydrophilic coating composition for forming a hydrophilic coating according to the present invention may, if necessary or desired, additionally contain materials such as water-soluble polyamides, other water-soluble resins capable of functioning as cross-linking agents, surfactants, mildew-proofing agents, antiseptics (bactericides), water glass and/or colloidal silica in such amounts as not to generate unpleasant odor and small amounts of solvents. (i) Water-soluble polyamides Water-soluble polyamides useful in the present invention may be water-soluble nylons, for instance nylon 6 modified to be soluble in water and/or alcohol. The average polymerization degree of the water-soluble nylons is in the range of 50-300, preferably 80-200. Such water-soluble nylons are commercially available, including, for example, AQ-nylon A-90, A-70 or P-70, (products of Toray Industries, Inc.). The water-soluble nylon may enhance the 5 hydrophilic nature to the coating. To achieve this function most effectively, the amount of the water-soluble nylon is preferably 0.3-5 parts by weight on a solid basis in the hydrophilic coating composition. When the amount of the water-soluble nylon is less than 0.3 parts by weight, the film-forming property is not significantly improved, whereas when it exceeds 5 parts by weight it may detract from the unpleasant odor-suppressing effects. The more preferred amount of the water-soluble nylon is 0.5-3.0 parts by weight. The hydrophilic groups of the water-soluble nylon remain intact even after baking and drying of the coating, so that it does not lose its hydrophilic nature. Such water-soluble nylon has at least one of a hydroxyl group, an amino group, diamines, tertiary amines and alkanol amines. As diamines, aliphatic amines such as ethylenediamine, trimethylenediamine, tetramethylenediamine, pentamethylenediamine (cadaverine), hexamethylenedimaine, 1,7-diaminoheptane, 1,8-diaminooctane, 1,9-diaminononane, 1,10-diaminodecane and aromatic amines such as ophenylenediamine, m-phenylenediamine and p-phenylenediamine may be used. As the tertiary amines, triethyl amine, tripropyl amine, tributyl amine, and dimethylbenzyl amine may be used. As for alkanol amines, ethanol amine, diethanol amine, triethanol amine, amino ethyl ethanol amine and morpholine may be used. (ii) Other water-soluble resins capable of functioning as cross-linking agents Other water-soluble resins, which are capable of functioning as cross-linking agents, include water-soluble amino resins and water-soluble phenol resins. 1. Water-soluble amino resins Water-soluble amino resins useful in the present invention include melamine resins such as n-butylated melamine resins, iso-butylated melamine resins, benzoguanamine resins and urea resins, which are modified to have water solubility. These resins may usually be prepared by carrying out an addition reaction or an addition condensation reaction of amino resins such as melamines and benzoguanamine with aldehydes such as formaldehyde, para-formaldehyde and then subjecting the resulting compound to etherification with monovalent alcohols having 1-4 carbon atoms. Among the water-soluble amino resins mentioned above, the water-soluble melamines are preferable. Specific examples of such melamine resins are alkoxymethyl melamines having alkoxy groups such as methoxy, ethoxy, n-butoxy, i-butoxy and methylated melamines are most preferable. The water-soluble amino resin acts as a cross-linking agent to improve the film-forming property of the hydrophilic coating composition. To achieve this function most effectively, the amount of the water-soluble amino resin is preferably 0.1-5 parts by weight on a solid basis in the hydrophilic coating composition. When the amount of the water-soluble amino resin is less than 0.1 parts by weight, there is no significant increase in film-forming property and unpleasant odor-suppressing effect. On the other hand, when the amount of the water-soluble amino resin is more than 5 parts by weight it may detract from the hydrophilic nature of the coating. The more preferred amount of the water-soluble amino resin is 0.5-2 parts by weight. The hydrophilic groups of the water-soluble amino resin remain intact after baking and drying of the coating, so that it does not lose its hydrophilic nature, like the water-soluble nylon. Such a water-soluble amino resin has at least one of diamines, tertiary amines and alkanol amines, which are listed in (c) (i) above. The water-soluble amino resin may also have hydroxyl groups. 2. Water-soluble phenol resins Water-soluble phenol resins useful in the present invention include polycondensates of compounds containing phenolic OH groups such as phenol, cresol, xylenol, p-alkyl phenol, p-phenyl phenol, chlorophenol, bisphenol A, phenol sulfonic acid, resorcinol and aldehydes such as formalin and furfural, which polycondensates are then modified to have water solubility. These water-soluble phenol resins are generally exemplified as phenolformalin resins, cresol-formalin resins, phenol-furfural resins and resorcinol resins. The water-soluble phenol resins form cross links between resin chains in the hydrophilic coating composition to increase its film-forming property. To achieve this function most effectively, the amount of the water-soluble phenol resin is preferably 0.1-5 parts by weight on a solid basis. When the amount of the water-soluble phenol resin is smaller than 0.1 parts by weight, there is no significant increase in 5 film-forming property and unpleasant odor-suppressing effect. On the other hand, when it exceeds 5 parts by weight it may detract from the hydrophilic nature of the coating composition. The more preferred amount of the water-soluble phenol resin is 0.5-2 parts by weight. (iii). Surfactants Any surfactants may be nonionic, cationic, anionic or ampholytic ones, and any suitable surfactants may be selected by taking into consideration the stability, foamability, coatability, etc. of the hydrophilic coating composition solution. Typical examples of nonionic surfactants which may be used include polyoxyethylene glycol, polyoxypropylene glycol, polyoxyethylene-polyoxypropylene glycol, polyoxyethylene alkylphenyl ether, glycerin-aliphatic acid esters, sorbitan-aliphatic acid esters, pentaerythritol aliphatic acid esters, polyoxyethylene sorbitan aliphatic acid esters, polyoxyethylene alkyl ethers, etc. Typical examples of anionic surfactants which may be used include dialkylsulfosuccinates, alkane sulfonates, alkylbenzene sulfonates, alkylnaphthalene sulfonates, polyoxyethylene alkyl sulfophenyl ether salts, alkyl phosphates, polyoxyethylene alkyl ether-phosphates, aliphatic alkyl ester-sulfates, alkyl sulfates, polyoxyethylene alkyl ether-sulfates and aliphatic acid monoglyceride-sulfates. Typical examples of cationic surfactants which may be used include alkyl amine salts and dialkyl amine salts. Typical examples of ampholytic surfactants may be N,N,N-trialkyl-N-sulfo alkylene ammonium betaine. The amount of the surfactant added is preferably 1.5 parts by weight or less. When it exceeds 1.5 parts by weight, the water resistance of the resulting coating may be decreased. As for the mildew-proofing agents and the antiseptics (bactericides), quaternary ammonium salts, nitrogen-containing sulfur compounds, halogen-containing nitrosulfur compounds, organic iodine compounds, benzimidazole and its derivatives, etc., may be used. (iv) Mildew-proofing agents Typical examples of the mildew-proofing agents include 2-thiazol-4-yl-benzimidazole, methylbenzimidazol-2-yl carbamate, N-dichlorofluoromethyl-thio-N',N'-dimethyl-N-phenylsulfamide, tetramethyl thiuram disulfide, N-(trichloromethylthio)-4-cyclohexene-1,2-dicarboxyimide, 2,4,5,6-tetrachloro-1,3-isophthalonitrile, 2,3,5,6-tetrachloro-4-(methylsulfonyl) pyridine and bis(2-pyridylthio)-zinc-1,1-dioxide. Considering the heat resistance of the resulting hydrophilic coating, 2-thiazol-4-yl-benzimidazole, methylbenzimidazol-2-yl-carbamate, 2,4,5,6-tetrachloro-1,3-isophthalonitrile and bis(2-pyridylthio)-zinc-1,1-dioxide are preferable. (v) Bactericides Typical examples of the bactericides include 1,2-benzo isothiazoline-3-on (BIT), 2,3,5,6-tetrachloro-4-(methylsulfonyl) pyridine and 10,10'-oxybisphenoxyarsine. The preferable amount of the mildew-proofing agent and/or the bactericide is 0.1-2.0 parts by weight. The more preferred amount of the mildew-proofing agent and/or the bactericide is 0.2/1.0 parts by weight. (vi) Water glass and/or colloidal silica The addition of water glass and/or colloidal silica to the hydrophilic coating composition in such amounts as not to generate unpleasant odor may further improve the hydrophilic nature. As the water glass, SiO₂/M₂O (where M represents Li, Na and K) may be used, and SiO₂/K₂O is particularly preferable. Colloidal silica having an average particle diameter of 10-50 µm is preferable. Their total amount is preferably less than 1 part by weight. (vii) Solvents Further, solvents may be added to the hydrophilic coating composition for the improvement of the wettability of the resulting hydrophilic coating. Such solvents include alcohols and cellosolves. Their amounts are preferably less than 7 parts by weight. The hydrophilic coating bath for forming hydrophilic coatings on aluminum members according to the present invention is produced by properly diluting or dispersing the above hydrophilic coating composition with water to form an aqueous solution or dispersion. The percentages of the components in the bath are not different from those as described above. The concentration of the hydrophilic coating composition in the bath is usually adjusted so as to provide a hydrophilic coating of 0.5-2.5 g/m² to an aluminum surface by dipping, spraying, brushing, etc. The concentration of solid components in the bath may generally be 10-200 g/l , preferably 30-100 g/l. If some of the components decrease unproportionally, they should be supplemented in order to maintain the percentage of each component at a proper level. Before forming a coating layer with the hydrophilic coating bath, a degreasing treatment is usually conducted on an aluminum member, and may, for example, include an acidwashing treatment using sulfuric acid and nitric acid ; solvent degreasing using trichloroethylene, perchloroethylene, gasoline, n-hexane and alkali degreasing using alkali solutions of sodium hydroxide, sodium carbonate, sodium silicate and sodium phosphate. After degreasing, a chemical treatment may be conducted to form a corrosion-resistant layer on a degreased aluminum member. The corrosion-resistant layer can be obtained by a chromate treatment. The chromate treatment is conducted with a treatment liquid containing chromic acid and sulfuric acid, nitric acid, fluoric acid, phosphoric acid and proper additives. The chromate treatment is categorized into two groups; a phosphoric chromate treatment using phosphoric acid as an inorganic acid, and a chromium chromate treatment using the other acids. From the viewpoint of corrosion resistance, the latter is better. The chromate treatment can be conducted by immersion in a treatment liquid, or spraying the treatment liquid. However, to fit exchanger fins having complicated shapes, an immersion method is easier. The corrosion-resistant layer so obtained preferably has a Cr content of 30-250 mg/m². When it is less than 30 mg/m², the layer tends not have sufficient corrosion resistance, whereas when it exceeds 250 mg/m², reaction with the hydrophilic layer may take place, resulting in deterioration of its hydrophilic nature. The aluminum member formed with the corrosion-resistant layer is then washed with water. This is preferably done by dipping in flowing water for about 10 seconds to 10 minutes. The hydrophilic coating composition of the present invention is diluted or dispersed properly as an aqueous solution or dispersion, and applied to the aluminum surface already subjected to degreasing and the above chemical treatment. This can be done by any coating method such as a roll-coating method, a bar-coating method, an immersion method, a spraying method and a brushing method. In a case where a treated aluminum member has a complicated shape like heat exchanger fins, the immersion method is preferable. Incidentally, the hydrophilic coating bath of the present invention may be applied not only to shaped aluminum members such as fins but also to aluminum plates which are to be shaped after coating. The present invention will be explained in further detail by way of the following Examples. Examples 1-9, Comparative Examples 1-10 Aluminum plates were degreased and then subjected to a phosphoric chromate treatment by an immersion method with Alsurf 407/47 (tradename, manufactured by Nippon Paint Co., Ltd.) to form a corrosion-resistant coating having 80-120 mg/m² of Cr content. These chromate-treated aluminum plates were washed with tap water for 20 seconds. Each of the aluminum plates was then dipped in a bath having the composition shown in Table 1 for 1 minute at a room temperature, and then dried at 180°C for 20 minutes to form a hydrophilic coating. Each of the resulting hydrophilic coatings was tested with respect to odor, hydrophilic nature (contact angle of water), water dissolution resistance, adhesion and mildew-proofing. The test procedures and the evaluation standards of test results were as follows: (1) Odor test Each aluminum plate formed with a hydrophilic coating (hereinafter referred to simply as "sample") was subjected to an odor test by direct smelling and evaluated as follows: o ○ : No odor; ○: Only slight odor; Δ: Medium odor; and ×: Strong odor. (2) Test of hydrophilic nature (Test of contact angle of water) Each sample was dipped in water flowing from the tap at a flow rate of 5 liter per minute for 480 hours and then dried at 80°C for 10 minutes. Each of the resulting hydrophilic coatings was measured with respect to a contact angle Q of 5 µl of pure water droplet dropped onto each sample positioned horizontally by a goniometer (CA-Z of Kyowa Kaimen Kagaku K. K.). The contact angle Q was classified into the following categories: o ○ : Q<20°; ○: 20≤Q<30°; Δ: 30°≤Q<40°; and ×: 40°≤Q. (3) Water dissolution resistance Each sample was dipped in tap water for 24 hours, and the weight of the coating was measured before and after dipping to determine a water dissolution ratio (R) by the following equation: R (%) = [(Initial coating weight - Coating weight after 24-hour dipping) - Initial coating weight] x 100 The evaluation standards of water dissolution resistance were as follows: o ○ : R< 10%; ○: 10% ≤ R < 30%; Δ: 30% ≤ R < 50%; and ×: 50% ≤ R. (4) Adhesion Test Cross-cut test was performed on each sample by the following procedure: Straight cut lines perpendicular to each other were formed on each sample with an interval of 1 mm to have 100 square cut pieces. An adhesive tape was sticked to the cross-cut surface of each sample and then peeled off. The number of the square pieces of the coating which remained on the aluminum member was counted and classified as follows: o ○ : 100; ○: 99-90; Δ: 89-80; ×: 79-70; and ××: < 70. (5) Mildew-proofing test According to JIS Z 2911, each sample of 3 cm x 3 cm was immersed in flowing water for 250 hours, and then a suspension containing four kinds of spores shown below was sprayed to the sample. The sample was kept for incubation at 27°C for 7 days. After the incubation, the propagation of the fungi on the sample was observed and classified into the following categories: Fungus: Aspergillus niger IFO 4414 Penicillium funiclosum IFO 6345 Cladosporium cladosporioides IFO 6348 Aureobasidium pullulans IFO 6353 Categories: o ○ : No propagation of the fungi observed by the naked eye. ○: Slight propagation of the fungi observed by the naked eye. Δ: Fungi observed by the naked eye covers about 1/3 of the surface of the sample. ×: The fungi observed by the naked eye covers about 2/3 of the surface of the sample. ××: The fungi observed by the snaked eye covers substantially the entire surface of the sample. The results of the tests (1)-(5) are shown in Table 2 below. No. Unpleasant Odor Hydrophilic Nature Water Dissolution Resistance Adhesion Mildew-Proof Example 1 o ○ o ○ ○ o ○ - Example 2 o ○ ○ ○ o ○ - Example 3 ○ o ○ o ○ o ○ - Example 4 ○ o ○ o ○ o ○ - Example 5 o ○ o ○ o ○ o ○ - Example 6 ○ ○ ○ o ○ - Example 7 o ○ o ○ ○ o ○ - Example 8 o ○ o ○ o ○ o ○ - Example 9 o ○ o ○ o ○ o ○ o ○ Com. Ex. 1 ○ Δ Δ × - Com. Ex. 2 ○ × × × - Com. Ex. 3 ○ Δ Δ × - Com. Ex. 4 ○ × × × - Com. Ex. 5 ○ Δ o ○ o ○ Δ Com. Ex. 6 ○ o ○ Δ ○ - Com. Ex. 7 Δ ○ ○ ○ - Com. Ex. 8 o ○ ○ Δ ○ - Com. Ex. 9 o ○ ○ × ○ - Com. Ex. 10 Δ o ○ o ○ o ○ - Examples 10-14 Aluminum plates were degreased and then subjected to a phosphoric chromate treatment by an immersion method with Alsurf 407/47 (tradename, manufactured by Nippon Paint Co., Ltd.) to form a corrosion-resistant coating having 80-120 mg/m² of Cr content. These chromate-treated aluminum plates were washed with tap water for 20 seconds. A hydrophilic coating composition shown in Table 3 was prepared, and it was diluted with water to prepare a bath having a solid concentration of 5 weight %. Each of the aluminum plates was then dipped in the bath for 1 minute at a room temperature, and then dried at 180°C for 20 minutes to form a hydrophilic coating. Each of the resulting hydrophilic coatings was tested with respect to odor, hydrophilic nature (contact angle of water), water dissolution resistance, adhesion and mildew-proofing in the same manner as in Example 1. The results are shown in Table 4. No. Unpleasant Odor Hydrophilic Nature Water Dissolution Resistance Adhesion Mildew-Proof Example 10 o ○ o ○ o ○ o ○ o ○ Example 11 o ○ o ○ o ○ o ○ o ○ Example 12 o ○ o ○ o ○ o ○ o ○ Example 13 o ○ o ○ o ○ o ○ o ○ Example 14 o ○ o ○ o ○ o ○ o ○ As described above in detail, the hydrophilic coatings formed from the hydrophilic coating composition according to the present invention have advantageous hydrophilic nature and water dissolution resistance, and exhibit minimal unpleasant odor. They show good adhesion to aluminum members and may be formulated to be mildew proof. Particularly when two types of polyvinyl pyrrolidone having different polymerization degrees are used, further improvements in hydrophilic nature, water dissolution resistance and odor-suppressing effect may be achieved.

Claims: A hydrophilic coating composition comprising, on a solid basis, (a) 0.3-6 parts by weight of polyvinyl pyrrolidone having a polymerization degree of 10-1000; and (b) 1-10 parts by weight of polyvinyl alcohol having a saponification degree of 80% or more and a polymerization degree of 100-1000, the weight ratio of the component (a) to the components (a) and (b), (a)/[(a)+(b)], being in the range of 0.1-0.9. A composition as claimed in claim 1 additionally containing one or more additives selected from water-soluble polyamides, water-soluble resins capable of functioning as cross-linking agents, surfactants, mildew-proofing agents, bactericides, water glass and/or colloidal silica in such amounts as not to generate unpleasant odor, and solvents. A composition as claimed in claim 2 wherein the additive comprises a water-soluble nylon and/or a water-soluble phenol resin. A composition as claimed in claim 2 or claim 3 wherein the additive comprises a mildew-proofing agent containing an imidazole compound. A composition as claimed in any of claims 1 to 4 wherein said polyvinyl pyrrolidone consists of two types of polyvinyl pyrrolidone, the first one having a polymerization degree of 10-50 and the second one having a polymerization degree of 100-500, and the weight ratio of said first polyvinyl pyrrolidone to said second polyvinyl pyrrolidone being 1/1.5-1/3.0. A composition as claimed in any of claims 1 to 5 in the form of an aqueous hydrophilic coating bath in which the solids concentration is 10-200 g/l. A process for coating an aluminum article to form a hydrophilic coating thereon which comprises applying to said article a coating composition as claimed in any of claims 1 to 6. A process as claimed in claim 7 wherein the coating is applied at a level of 0.5-2.5 g/m². A process as claimed in claim 7 or claim 8 wherein the coating is applied to a finned aluminum heat exchanger component. Coated aluminum articles obtainable by a process as claimed in any of claims 7 to 9.

Inventors: INOUE SUSUMU, KOJIMA MASAHIRO, MIKAMI FUJIO, YASUHARA KIYOTADA, INOUE, SUSUMU, KOJIMA, MASAHIRO, MIKAMI, FUJIO, YASUHARA, KIYOTADA
Applicants: NIPPON PAINT CO LTD, SHOWA ALUMINUM CORP, NIPPON PAINT CO., LTD., SHOWA ALUMINUM CORPORATION
Application year: 1992
Main classification: C09D139
IPC codes: C09D139, B05D5, C08L29, B05D7, C09D129, C08L39