Manufacturing method for a multigate thin film transistor

Abstract: An SOI-type thin film transistor having: a transparent insulating substrate; a first gate electrode, a first gate insulating film, a semiconductor layer, a second gate electrode and a second gate insulating film which are respectively formed on the transparent insulating substrate, wherein the width of the first gate electrode and that of the second gate electrode are different from each other and as well as the thickness of the first gate insulating film and that of the second gate insulating film are different from each other.

Description: The present invention relates to a manufacturing method of a high performance thin film transistor having an SOI structure. Recently, a thin film transistor has been attracting attention as an element which constitutes a three-dimensional integrated circuit, a contact sensor or a plane display device. In particular, a study has been made in order to improve the performance of a silicon thin film transistor by approximating its crystallinity to that of the monocrystal substance. Another study has been made in order to significantly improve the mobility by utilizing the specific mechanism in such a manner that the thickness of the thin film is considerably reduced (0.1 µm or less). However, although each specific characteristic has attracted attention according to the above-described studies, the relative changes between the other transistor characteristics have not been sufficiently detected. The inventor of the present invention has studied the overall electrical characteristics of the thin film transistor having the SOI structure, resulting in a knowledge to be found from simulations that, if the thickness of the semiconductor layer becomes thinner than a predetermined thickness, the drain voltage resistance at the time when the gate voltage is 0V (when it is turned off) rapidly deteriorates in comparison to that displayed by a thick film semiconductor layer. Another fact was found from simulations that, although the avalanche breakdown, which determines the drain voltage resistance and which takes place at the drain end, arises in the vicinity of the gate interface in a case of a thick semiconductor, the same arises in a vicinity of an interface with the base insulating substrate in a case where the thickness is smaller than a predetermined thickness. More particularly, the conventional simulation made about an SOI-type MIS-FET, which was constituted by forming, on a thick insulating substrate, a thin film semiconductor layer, a gate insulating film and a gate electrode, found a fact that the maximum electric fields were concentrated in a vicinity of the gate interface and the avalanche breakdown was first taken place in the vicinity of the gate interface in such a manner that the above-described tendency was maintained regardless of the thickness of the semiconductor layer. The inventor has made simulations while taking into consideration the fixed charge (Q ss ) at the interface between the base insulating substrate and the semiconductor layer which was considered to be present in an actual SOI structure. As a result, a fact was found that, although the electric field was strong on the gate interface side in comparison to that at the portion adjacent to the base interface, the avalanche breakdown actually took place in the vicinity of the base interface. Although the detail mechanism is being researched now, it can be considered that the avalanche breakdown depends upon not only the electric field but also the number of carriers and thereby the number of the carriers is further affected at the base interface while an assumption is made that the equivalent Q ss is applied to the gate and the portion adjacent to the base interface. The Extended Abstracts of the 22nd Conf. on Solid State Devices and Materials, 1990, pp. 1195 to 1196, discloses a method of producing an ultra-thin double-gated poly-Si TFT comprising the steps of fabricating a p + -poly-Si bottom gate on a thermally grown oxide, a gate insulating layer, an ultra thin Si film by conventional LPCVD system, an upper gate oxide and a p + -poly-Si top gate. After formation of the top gate B + ion implantation is performed to form source and drain regions, wherein the top gate with photoresist is used as a self-aligned mask. Moreover, EP-A-0 304 824 discloses a thin film MOS transistor having a double gate structure, wherein a pair of gate electrodes opposes across a semiconductor layer. In addition, JP-A-2 297 971 discloses a method of producing a thin-film transistor having a double gate structure. Furthermore, JP-A-60 083 370 discloses a method of producing a polycrystalline silicon thin film transistor having a double gate structure, wherein holes are made in a SiO 2 film in order to form a source region and a drain region to be implanted with n and p dopants, respectively. Moreover, EP-A-0 359 528 discloses a method of producing high-voltage thin-film transistors, wherein a positive photoresist layer is exposed by means of backside exposure to pattern photoresist masks which are aligned with gates beneath the photoresist layer. In addition, EP-A-0 338 766 discloses a method for fabricating an active matrix substrate, wherein a photo resist exposed from the substrate back side is used, using the gate electrode pattern made of opaque material on a transparent substrate as the mask. This method uses over exposure. An object of the present invention is to provide a method of manufacturing a thin film transistor having an SOI structure in which the deterioration in the drain voltage resistance at the time of the stop of the operation can be prevented while maintaining excellent characteristics such as the high mobility and a low incidental capacity realized due to the arrangement in which the thickness is reduced. Other and further objects, features and advantages of the invention will be apparent more fully from the following description. Figs. 1A to 1F are schematic views which illustrate an example of a process of manufacturing a thin film transistor according to the present invention; Figs. 2A to 2C are schematic views which illustrate an example of a process of manufacturing a thin film transistor according to the present invention; Figs. 3A to 3C are schematic views which illustrate an explanatory example of a process of manufacturing a thin film transistor which is not according to the present invention; and Fig. 4 is a graph which illustrates the relationship between the amount of exposure and the line pattern width arranged at the time of manufacturing the thin film transistor according to the present invention. According to the present invention, there is provided a method of manufacturing an SOI-type thin film transistor comprising a first gate electrode on a transparent insulating substrate, a first insulating film on said first gate electrode, a semiconductor layer on said first insulating film, a second gate insulating film provided on said semiconductor layer, and a second gate electrode provided on said second gate insulating film, comprising the steps of performing a backside exposure from a side of said transparent insulating substrate using said first gate electrode as an exposure mask to produce an etching mask for defining a second gate electrode, wherein the backside exposure amount using said first gate electrode as the exposure mask is controlled into an under exposure amount, so that said etching mask has a broader width than said first gate electrode, and the deviation of the under exposure amount from an appropriate exposure amount is adjusted so as to make the width of the developed resist pattern and of the second gate electrode defined thereby larger than the width of said first gate electrode by length L. Moreover, the present invention provides a method of manufacturing an SOI-type thin film transistor comprising a first gate electrode on a transparent insulating substrate, a first insulating film on said first gate electrode, a semiconductor layer on said first insulating film, a second gate insulating film provided on said semiconductor layer, and a second gate electrode provided on said second gate insulating film, comprising the steps of performing a backside exposure from a side of said transparent insulating substrate using said first gate electrode as an exposure mask to produce an etching mask for defining a second gate electrode, wherein the backside exposure amount using said first gate electrode as the exposure mask is controlled into an over exposure amount, so that said etching mask has a smaller width than said first gate electrode, said etching mask being used for defining said second gate electrode, and the deviation of the over exposure amount from an appropriate exposure amount is adjusted so as to make the width of the developed resist pattern and of the second gate electrode defined thereby smaller than the width of said first gate electrode by length L. Since the SOI-type thin film transistor which is manufactured by the method according to the present invention enables the incidental capacity between the gate and the drain to be further reduced and thereby enables the operational speed to be raised, the drain rupture voltage resistance at the time when the transistor is turned off can be enlarged. Furthermore, since the two gate electrodes, which are vertically disposed, and the source & drain region are formed in a self-alignment manner, the undesirable dispersion of the characteristics can be prevented and thereby the yield can be improved. Then, the present invention will now be described in detail with reference to the drawings. Fig. 1F is a schematic view which illustrates an example of the cross sectional structure of the SOI-type thin film transistor which is manufactured by the method according to the present invention. The thin film transistor which is manufactured by the method according to the present invention is an MIS-FET formed into a so-called double gate structure. The joining surface of the source and the drain region 110 is arranged in such a manner that the interface with a second gate insulating film 105 is placed at the end portion of the second gate electrode 109 disposed above the source and drain region 110. According to an example shown in Fig. 1, the interface with the first gate insulating film 103 is placed outside the first gate electrode 102 disposed below the source and drain region 110. As a result, a so-called offset gate structure is formed with respect to the first gate electrode 102 disposed below the source and drain region 110. Although the example shown in Fig. 1 is arranged in such a manner that the width of the first gate electrode is narrower than that of the second gate electrode, the present invention is not limited to this. It is necessary for the width of the first gate electrode and that of the second electrode to be different from each other. The transistor which is manufactured by the method according to the present invention is arranged in such a manner that, when the vertically (when viewed in the drawings) disposed gate electrodes 102 and 109 are driven at the same potential, the channel is mainly controlled at the interface between the semiconductor layer 104 and the first gate insulating film when the transistor is turned on because the second gate insulating film 105 is thicker than the first gate insulating film 103. Therefore, the apparent mutual inductance g m is not substantially changed with respect to a sole gate or the same increases by a small quantity which corresponds to the contribution made by the second gate electrode 109. That is, the first gate electrode 102 acts as the main gate. In this case, since the second gate insulating film 105 is thick, its gate film capacity is too small to warp the electric field applied to the channel by the first gate electrode. Therefore, the characteristics (high carrier mobility) obtainable in a case where the thickness of the SOI layer is reduced can be maintained. Furthermore, since the first gate electrode 102 is formed into the offset structure, the incidental capacity between the gate and the drain can further be reduced. Therefore, the operational frequency can be raised in comparison to a case where no offset is made. On the other hand, when the transistor is not operated, the electric field on the interface between the drain joining surface and the first gate insulating film 103 is relaxed by a quantity corresponding to the offset. Therefore, the avalanche breakdown will not easily take place. Furthermore, as for the avalanche breakdown which will take place at the interface between the drain joining surface and the second gate insulating film, a storage layer is formed at the interface between the interface of the second gate insulating film 105 and the channel region to prevent the storage of minority carriers which are present in the vicinity of the drain joining end and which will cause the avalanche breakdown to take place. As a result, the voltage resistance can be improved. As for the above-described first and second gate insulating films, the thickness of the second gate insulating film is defined as follows in a case where interface of the first gate insulating film becomes the main channel region: V +h (1) < V +h (2) < V DD where V +h (2) =  d (2)/C ox (2) + 2 B +  ms -  ss /C ox (2) V +h (1) : threshold voltage in a case where the first gate electrode is made to be the main gate V +h (2) : threshold voltage in a case where the second gate electrode is made to be the main gate C ox (2) : capacity of the second gate insulating film B: Fermi potential ms: work function difference  d (2) : charge in the inversion layer induced by the interface of the second gate insulating film V DD : power supply voltage The quantity of the offset is the distance from the source and the drain end of the main gate electrode and it is effective if it is zero or more. However, if the quantity of the offset is too large, gm of the transistor is undesirably reduced. Therefore, setting may usually be made such that L OFFSET ≦ 5 µm, preferably L OFFSET ≦ 3 µm. The transistor which is manufactured by the method according to the present invention is formed into an offset structure, the overall incidental capacity between the gate and the drain is further reduced at the time of the operation, the operational frequency can be raised in comparison to the case in which no offset is made. On the other hand, when the transistor is not operated, the electric field at the interface between the drain joining surface and the base insulating film 103 is relaxed by a quantity corresponding to the offset. Therefore, the avalanche breakdown will not easily take place. In a case where low-resistance polycrystal silicon or low-resistance amorphous silicon or the like is used as the material for the mask for forming an impurity diffusion layer, either of the above-described layers can be made to serve as the second gate electrode. Therefore, a transistor formed into the double-gate structure can be manufactured. In this case, a channel can be formed at the interface between the upper portion and the lower portion when, for example, the two gates are driven at the same potential at the time of the operation of the transistor. Therefore, apparent gm of the transistor can be doubled. On the other hand, as for the avalanche breakdown which will take place at the interface between the drain joining surface and the upper base insulating film, a storage layer is, at the time of the stoppage of the operation of the transistor, formed at the interface between the interface of the upper base insulating film 105 and the interface of the channel region to prevent the storage of minority carriers which are present in the vicinity of the drain joining end and which will cause the avalanche breakdown to take place. As a result, the voltage resistance can be improved. A method of manufacturing the above-described transistor will now be described with reference to Fig. 1. First, the first gate electrode 102 is formed on the transparent insulating substrate 101 made of quartz by an ordinary photolithography process by using metal such as A l, A l -Si, W, or W-Si or the like as the material. Then, the first insulating film 103 made of any one of an SiO film, an SiN film or an SiON film is formed by, for example, the CVD method or the sputtering method. Then, the semiconductor layer 104 is formed on the first insulating film 103. As the semiconductor layer, monocrystal silicon of a type disclosed by the applicant of the present invention filed in Japanese Patent Laid-Open No. 63-107016 may be used, the monocrystal silicon being arranged in such a manner that monocrysal is grown on an amorphous substrate before the surface of the monocrystal is flattened. As an alternative to this, a material may be used which can be obtained by recrystallizing amorphous silicon film or a polycrystal silicon film with energy beams or the like for melting the amorphous silicon film or a polycrystal silicon film. Then, the second insulating film 105 is formed by the same method as that employed when the first insulating film 103 is formed or by the thermal oxidation method. Then, a second gate electrode material 106 and a photoresist 107 are applied. As the second gate electrode material 106, the low-resistance polycrystal silicon or the low-resistance amorphous silicon prepared by the CVD method may be used. Then, the deposited photoresist or the second gate electrode material is patterned by the ordinary photolithography method. Then, its process will now be described. As shown in Figs. 1C and 1D, the photoresist 107 is spin-applied before exposure (hν) is performed from the portion including the substrate 101. At the time of the exposure, no individual photomask is not used but the first gate electrode 102 is used as the exposure mask. Then, the photoresist which has been irradiated with light and which has thereby been reacted is developed, while a residual resist pattern 108 is used as the mask to remove the second gate electrode material layer 106 by etching. As a result, a second gate electrode 109 is formed in such a manner that the first gate electrode 102 and the second gate electrode 109 respectively have different widths. Specifically, the exposure conditions are set so as to make the width of the developed resist pattern 108 is larger than the width of the first gate electrode 102 by length L. The above-described exposure conditions can be set as follows: as shown in Fig. 4, the appropriate exposure quantity is defined to be a quantity with which the mask dimension becomes the same as the resist line dimension in a case where the positive type resist is employed. If the exposure quantity is under the above-described level, the pattern dimension is thickened. If the same is over the above-described level, the pattern dimension is narrowed. Therefore, the exposure may be performed by an exposure quantity with which the actual pattern dimension is thicker than the mask dimension by L. According to actual data obtained by the inventor of the present invention, the line pattern dimension can be enlarged by 0.2 µm by decreasing the exposure quantity from the appropriate exposure quantity by 10%. In a case where a mirror projection apparatus or a stepper is used as the exposure apparatus, the pattern which is thicker by L can be similarly obtained by a method in which the exposure quantity is set to the appropriate exposure quantity and the focal point of projection light is deflected. In actual, the mirror projection apparatus is used, the line pattern can be thickened by 0.2 µm by performing defocusing by a quantity of 1 µm. Finally, by using the second gate electrode 109 as the mask, impurities are introduced in order to form the impurity diffusion layer as the source and drain region 110 of the transistor. In this case, a method may be employed in which the photoresist which has been patterned for the purpose of forming the second gate electrode is not removed but the same is left as it is. According to the method of manufacturing the thin film transistor according to the present invention, the source and drain region 110 serving as the impurity diffusion layer can be formed in a self-aligned manner by the photoresist formed by the backside exposure or by the second gate electrode 109 formed by its photoresist pattern. On the other hand, also the second gate electrode 109 can be formed in the self-aligned manner by the first gate electrode 102. As a result, all of the first and the second gate electrodes and the source and drain regions can be formed in the self-aligned manner. Therefore, the dispersion of the transistor characteristics can satisfactorily be prevented and thereby the yield can be improved. Then, examples of the present invention will now be described specifically. [Example 1] Figs. 1A to 1F are schematic views which illustrate an example of the process of manufacturing the thin film transistor according to the present invention. First, tungsten (W) was deposited on the quartz substrate 101 by the sputtering method by a thickness of 2000Å before the first gate electrode 102 was formed by the ordinary photolithography process. Then, the first gate insulating film (SiO 2 ) 103 was deposited by 50 nm (500Å) by the atmospheric CVD method performed under conditions that SiH4/02 was used as the reactive gas and the substrate temperature was 400°C. Then, by the reduced-pressure CVD method, an Si 3 N 4 film was deposited by 100 nm (1000Å) before a dot of 1.5 µm x 1.5 µm was left on the first gate electrode 102 by the ordinary photolithography method but the other portions were removed. Then, the crystal was grown by the reduced-pressure CVD method under the following conditions: SiH 2 C l 2 /HC l /H 2 = = 0.53/1.6/100 ( l /min) (1,995 · 10 4 Pa (150 Torr), 990°C, 120 minutes) As a result, monocrystal silicon, the particle size of which was 100 µm, was grown before the surface of it was flattened and smoothed by mechan-o-chemical polishing and etching RIE. As a result, the monocrystal semiconductor layer 104, the thickness of which was 0.1 µm, was formed before etching RIE was again performed to obtain a desired shape (see Fig. 1A). Then, the SiO 2 film 105 was, by the atmospheric CVD method, deposited by 150 nm (1500Å) under the same conditions as those set when the first gate insulating film 103 was formed. Then, low-resistance polysilicon was, as the second gate electrode material layer 106, deposited by 200 nm (2000Å) by the reduced-pressure CVD method. In this case, the deposition conditions were set such that the deposition was performed for 5 minutes while making SiH 4 to be 150 cm 3 /min under standard conditions (sccm), PH 3 (diluted by 0.5% N 2 ) to be 15 cm 3 /min under standard conditions (sccm), the pressure to be 26,6 Pa (0.2 Torr) and the temperature to be 600°C. The positive type photoresist 107 was applied by the spinning application method and the exposure was made while applying light from the portion including the quartz substrate 101. The exposure quantity was set to a value which was under by 10% from the appropriate exposure quantity (see Fig. 1C). Then, the resist was developed (see Fig. 1D) before the residual resist pattern 108 was used as the mask to subject the second gate electrode material layer 106 to etching RIE so that the second gate electrode 109 was formed. In a case of the above-described exposure conditions, the dimension of the second gate electrode 109 could be made to be a value which was larger by 0.2 µm per side than the dimension of the first gate electrode (see Fig. 1E). Finally, by the ordinary ion injection method, P + was injected by IEI5cm -2 at 140 keV so that the source and drain region 110 was formed. Furthermore, annealing was performed at 800°C in order to activate the formed source and drain region. In accordance with the depth of the SIMS and the result of the line analysis, a fact was confirmed that the source and drain region joining surface was set off by 0.1 µm from the end portion of the first gate electrode 102. The manufactured transistor was operated, resulting in 10 6 (A) or more in the on-off ratio which was a satisfactory practical level to be obtained. The drain rupture voltage resistance when the operation of the transistor was turned off was 15V or higher which was substantially two times the value of a single gate structure or a structure in which no offset was made. [Example 2] Figs. 2A to 2C are schematic views which illustrate another example of the process of manufacturing the thin film transistor according to the present invention. First, tungsten (W) was deposited on the quartz substrate 201 by the sputtering method by a thickness of 200 nm (2000Å) before the first gate electrode 202 was formed by the ordinary photolithography process. Then, the first gate insulating film (SiO 2 ) 203 was deposited by 50 nm (500Å) by the atmospheric CVD method performed under conditions that SiH 4 /O 2 was used as the reactive gas and the substrate temperature was 400°C. Then, by the reduced-pressure CVD method, an Si 3 N 4 film was deposited by 100 nm (1000Å) before a dot of 1.5 µm x 1.5 µm was left on the first gate electrode 202 by the ordinary photolithography method but the other portions were removed. Then, the crystal was grown by the reduced-pressure CVD method under the following conditions: SiH 2 C l 2 /HC l /H 2 = 0.53/1.6/100 ( l /min) (1,995 · 10 4 Pa (150 Torr), 990°C, 120 minutes) As a result, monocrystal silicon, the particle size of which was 100 µm, was grown before the surface of it was flattened and smoothed by mechan-o-chemical polishing and etching RIE. As a result, the monocrystal semiconductor layer 204, the thickness of which was 0.1 µm, was formed before etching RIE was again performed to obtain a desired shape. Then, the SiO 2 film 205 was, by the atmospheric CVD method, deposited by 150 nm (1500Å) under the same conditions as those set when the first gate insulating film 203 was formed. The positive type photoresist 207 was applied by the spinning application method and the exposure was made while applying light from the portion including the quartz substrate 201. The exposure quantity was set to the appropriate value in this case. Then, the resist was developed before the residual resist pattern 207 was used as the mask to form the source and drain region 210 by the ordinary ion injection method in which P + was injected by IEI5cm -2 at 140 keV (see Fig. 2A). Furthermore, annealing was performed at 800°C In order to activate the formed source and drain region. Then, low-resistance polysilicon was, as the second gate electrode material layer 206, deposited by 200 nm (2000Å) by the reduced-pressure CVD method. In this case, the deposition conditions were set such that the deposition was performed for 5 minutes while making SiH 4 to be 150 cm 3 /min under standard conditions (sccm), PH 3 (diluted by 0.5% N 2 ) to be 15 cm 3 /min under standard conditions (sccm), the pressure to be 26,6 Pa (0.2 Torr) and the temperature to be 600°C. The positive type photoresist 208 was applied by the spinning application method and the exposure was made while applying light from the portion including the quartz substrate 201. The exposure quantity was set to a value which was over by 10% from the appropriate exposure quantity (see Fig. 2B). Then, the resist was developed before the residual resist pattern 208 was used as the mask to subject the second gate electrode material layer 206 to etching RIE so that the second gate electrode 209 was formed. In a case of the above-described exposure conditions, the dimension of the second gate electrode 209 could be made to be a value which was smaller by 0.2 µm per side than the dimension of the first gate electrode (see Fig. 2C). [Explanatory Example] An explanatory example which is not according to the present invention will now be described with reference to Figs. 3A to 3C. First, tungsten (W) was deposited on the quartz substrate 201 by the sputtering method by a thickness of 200 nm (2000Å) before the gate electrode 202 was formed by the ordinary photolithography process. Then, the gate insulating film (SiO 2 ) 203 was deposited by 50 nm (500Å) by the atmospheric CVD method performed under conditions that SiH 4 /O 2 was used as the reactive gas and the substrate temperature was 400°C. Then, by the reduced-pressure CVD method, an Si 3 N 4 film was deposited by 100 nm (1000Å) before a dot of 1.5 µm x 1.5 µm was left on the gate electrode 202 by the ordinary photolithography method but the other portions were removed. Then, the crystal was grown by the reduced-pressure CVD method under the following conditions: SiH 2 C l 2 /HC l /H 2 = 0.53/1.6/100 ( l /min) (1,995 · 10 4 Pa (150 Torr), 990°C, 120 minutes) As a result, monocrystal silicon, the particle size of which was 100 µm, was grown before the surface of it was flattened and smoothed by mechan-o-chemical polishing and etching RIE. As a result, the monocrystal semiconductor layer 204, the thickness of which was 0.1 µm, was formed before etching RIE was again performed to obtain a desired shape. Then, the SiO 2 film 205 was, by the atmospheric CVD method, deposited by 150 nm (1500Å) under the same conditions as those set when the gate insulating film 203 was formed. The positive type photoresist 207 was applied by the spinning application method and the exposure was made while applying light from the portion including the quartz substrate 201. The exposure quantity was set to a value which was under by 10% from the appropriate exposure quantity (see Fig. 3B). Then, the resists was developed (see Fig. 3C) before the residual resist pattern 208 was used as the mask to form the source and drain region 210 (see Fig. 3A) by the ordinary ion injection method in which P + was injected by IEI5cm -2 at 140 keV. Furthermore, annealing was performed at 800°C in order to activate the formed source and drain region. In accordance with the depth of the SIMS and the result of the line analysis, a fact was confirmed that the source and drain region joining surface was set off by 0.1 µm from the end portion of the first gate electrode 202. The manufactured transistor was operated, resulting in 10 6 (A) or more in the on-off ratio which was a satisfactory practical level to be obtained. The drain rupture voltage resistance when the operation of the transistor was turned off was 15V or higher which was substantially two times the value of a single gate structure or a structure in which no offset was made. Furthermore, the offset structure can be formed by only a single photolithography operation (the necessity of using the mask can be eliminated). In addition, the self-aligned structure with the gate electrode can be formed. As a result, the manufacturing process can be simplified and as well as the characteristics dispersion can be prevented. As described above, since the SOI-type thin film transistor according to the present invention enables the incidental capacity between the gate and the drain to be further reduced and thereby enables the operational speed to be raised, the drain rupture voltage resistance at the time when the transistor is turned off can be enlarged. Furthermore, since the two gate electrodes, which are vertically disposed, and the source & drain region are formed in a self-alignment manner, the undesirable dispersion of the characteristics can be prevented and thereby the yield can be improved. Although the n-channel MOSFET was used as the MOSFET, a similar effect can, of course, be obtained even if the polarity is inverted.

Claims: A method of manufacturing an SOI-type thin film transistor comprising a first gate electrode (102) on a transparent insulating substrate (101), a first insulating film (103) on said first gate electrode, a semiconductor layer (104) on said first insulating film (103), a second gate insulating film (105) provided on said semiconductor layer (104), and a second gate electrode (109) provided on said second gate insulating film (105), comprising the steps of: performing a backside exposure from a side of said transparent insulating substrate (101) using said first gate electrode (102) as an exposure mask to produce an etching mask (108) for defining a second gate electrode (109) ; wherein the backside exposure amount using said first gate electrode (102) as the exposure mask is controlled into an under exposure amount, so that said etching mask (108) has a broader width than said first gate electrode (102); and the deviation of the under exposure amount from an appropriate exposure amount is adjusted so as to make the width of the developed resist pattern (108) and of the second gate electrode defined thereby larger than the width of said first gate electrode by length L. A method of manufacturing an SOI-type thin film transistor comprising a first gate electrode (202) on a transparent insulating substrate (201), a first insulating film (203) on said first gate electrode, a semiconductor layer (204) on said first insulating film (203), a second gate insulating film (205) provided on said semiconductor layer (204), and a second gate electrode (209) provided on said second gate insulating film (205), comprising the steps of: performing a backside exposure from a side of said transparent insulating substrate (201) using said first gate electrode (202) as an exposure mask to produce an etching mask (208) for etching said second gate electrode (209) ; wherein the backside exposure amount using said first gate electrode (202) as the exposure mask is controlled into an over exposure amount, so that said etching mask (208) has a smaller width than said first gate electrode (202); said etching mask (208) being used for defining said second gate electrode (209); and the deviation of the over exposure amount from an appropriate exposure amount is adjusted so as to make the width of the developed resist pattern (208) and of the second gate electrode defined thereby smaller than the width of said first gate electrode (202) by length L. A method according to any of claims 1 and 2, wherein said etching mask (108, 208) includes a photoresist. A method according to any of claims 1 to 3, wherein said semiconductor layer (104, 204) is a silicon layer. A method according to any of claims 1 to 4, wherein said first gate electrode (102, 202) comprises tungsten. A method according to any of claims 1 to 5, wherein said transparent insulating substrate (101, 201) is a quartz substrate. A method according to claim 3, wherein said photoresist is formed by a spin coating process. A method according to any of claims 1 to 7, wherein said first insulating film (103, 203) comprises Si 3 N 4 . A method according to any of claims 1 to 8, wherein said second gate electrode (109, 209) comprises a low resistance polycrystalline silicon. A method according to any of claims 1 to 9, wherein said semiconductor layer (104, 204) is produced by a low pressure CVD process. A method according to any of claims 1 to 10, wherein said semiconductor layer (104, 204) is flattened and smoothed by mechano-chemical polishing, and etched by RIE. A method according to claim 3, wherein said photoresist (108, 208) is used as an etching mask to form said second gate electrode (109, 209) from a gate electrode material layer (106, 206). A method according to claim 1, wherein said etching mask (108) together with the second gate electrode etched thereby are used as an ion injection mask to form an impurity diffusion layer (110) in said semiconductor layer (104).

Inventors: KONDO SHIGEKI, KONDO, SHIGEKI, KONDO, SHIGEKI, C/O CANON KABUSHIKI KAISHA
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1992
Main classification: H01L29
IPC codes: H01L21, H01L29