Water- and oil-repelling absorbed film and method of manufacturing the same

Abstract: A water- and oil-repelling adsorbing film formed on a material having active hydrogen such as hydroxyl group, imino group and amino group at the surface. This film is a chemically adsorbed film having surface irregularities exceeding 10 nanometers. It is directly or indirectly covalently bonded to the material surface and includes a monomolecular film or a polymer film with the molecules thereof containing a fluorocarbon group and a -Si- bond. The surface irregularities which exceed the molecular level are at least either those formed on the material surface itself, those due to particles formed on the substrate surface or those due to particles present in the chemically adsorbed film.

Description: The present invention relates to a method of manufacturing a water- and oil- repelling adsorbed film which can be used on electric products, vehicles and industrial apparatus requiring such a film. Heat-, weather- and wear-resistant super-thin coating films are desired for electric products, vehicles, industrial apparatus, mirrors and glass lenses. Hitherto, coatings which have been extensively used for water- and oil-repelling purposes, have been produced by the surface roughening of an Al substrate or the like by means of blasting, a wire brush or chemical etching, and then coating a primer followed by a fluorine enamel coating or like paint. The coatings can be prepared by suspending fine fluorocarbon base particles of polyethylenetetrafluoride in ethanol. followed by drying and baking (or fixing) at about 400 °C for about one hour to affix the fluorocarbon based polymer to the substrate surface. However, while this method permits ready manufacture, the polymer is bonded to the substrate by a mere anchor effect, thus imposing limitations on the adhesion of the polymer to the substrate. In addition, since the coating film surface is baked at a high temperature of 400 °C, it is flattened, and it was impossible to obtain a satisfactorily water- and oil-repelling surface. The method, therefore, was insufficient for electric products, vehicles, industrial apparatus and so forth requiring water- and oil-repelling coating films. The water- and oil-repelling properties have also been required for glass, ceramic, metal and plastic products, typically such glass products as vehicle window glass and front glass, optical lenses, glass lenses and building window glass, such ceramic products as sanitary porcelain, table dishes and flower vases, such construction materials as door and window sashes, metal materials for building exterior walls and such plastic products as furniture, cover films, decoration boards and panels. Further, it has been a sole way of preventing contamination of the glass, ceramic, metal and plastic products to make the surface of the products as smooth as possible. It is a known practice to coat hydrophilic polymer for preventing the fogging of the glass surface. However, this provides only a tentative effect. It is also a known practice to coat a metal surface with a fluorine resin or the like. This is done by thinly coating a fluorine enamel and then baking the same. As another means of resin coating, a paint is dissolved or suspended in a solvent, and the suspension or solution is coated, followed by drying of the solvent and hardening by baking. With the above method of fluorine resin coating, however, the obtained surface has irregularities of the order of several tens of microns, and therefore it is difficult to obtain a surface having excellent luster. In addition, the coating has inferior adhesion to the substrate, and high durability cannot be obtained. Further, other resin coatings are inferior in adhesion strength. posing problems in durability. This is due to the fact that adhesion to the substrate is based on physical adsorption. Therefore, the object underlying the present invention is to solve the above problems inherent in the prior art and to provide a method of manufacturing a coating film, which has strong adhesion to the substrate, is free from pin holes, has desirable surface irregularities and is excellently water- and oil-repelling and durable for improving the performance of products requiring heat-, weather- and wear-resistant water- and oil-repelling coatings such as buildings, electric products, vehicles and industrial apparatus. According to the present invention this object is attained with a method of manufacturing a water- and oil- repelling adsorbing film comprising: providing a substrate surface with active hydrogen groups, before or after making this substrate surface irregular; and contacting said irregular surface with a non-aqueous solution containing an active surface material having a fluorocarbon group and a chlorosilane group or having a fluorocarbon group and an alkoxysilane group. Preferred embodiments of the present invention are set forth in the dependent claims. It is preferable in this invention that the water- and oil-repelling adsorbing film is bonded by covalent bonds of -SiO- or -SiN= to the substrate surface. It is preferable in this invention that a thin layer of polysiloxane or a thin layer of chemically adsorbed monomolecular layer of siloxane is formed on the substrate surface and the water- and oil-repelling adsorbing film is formed on the thin layer or the chemically adsorbed monomolecular layer. It is preferable in this invention that the substrate is made of at least glass, ceramics, metals, plastics, wood, stone and semiconductors. It is preferable in this invention that the substrate surface is provided with irregularities at a level less than the wavelength of visible light, and which is anti-contaminating. It is preferable in this invention that the substrate is a plastic film. It is preferable in this invention that the plastic film has a coarsened surface with surface irregularities at a level of less than 0.3 micrometers. It is preferable in this invention that the method of manufacturing a water- and oil-repelling adsorbing film comprises: forming surface irregularities on the substrate and then providing the substrate surface with active hydrogen groups; contacting the substrate surface with a silane-based surface active material the molecules of said surface active material containing a silyl group at one end and a fluorocarbon group at the other end to adsorb said surface active material to the substrate surface by a dehydrochlorination reaction or a dealcoholation reaction; forming an outer layer by reacting with water with or without previous removal of non-reacted surface active material by washing using a non-aqueous organic solution; and drying or thermally treating the substrate surface. It is preferable in this invention to carry out the following process steps: forming surface irregularities on the substrate and then providing the substrate surface with active hydrogen groups; contacting the substrate surface with a non-aqueous solution containing a surface active material, the molecules of said surface active material having a plurality of chlorosilyl groups to adsorb said surface active material to the substrate surface by a dehydrochlorination reaction; forming an inner layer by reacting with water with or without previous removal of non-reacted surface active material by washing with a non-aqueous organic solvent; contacting the surface of said inner layer with a silane-based surface active material the molecule thereof containing a silyl group at one end and a fluorocarbon group at the other end to adsorb said surface active material to the inner layer substrate surface by a dehydrochlorination reaction or a dealcoholation reaction; forming an outer layer by reacting with water with or without previous removal of non-reacted surface active material by washing with a non-aqueous organic solution; and drying or thermally treating the substrate surface. It is preferable in this invention that the substrate surface is provided or formed with irregularities by: electrolytic etching, chemical etching, sand blasting, spattering, depositing, or rubbing. It is preferable in this invention that the chlorosilyl-based surface active material is one with the molecules thereof having at one end a chlorosilane group represented by a formula: - SiCl n X 3-n where n represents an integer from 1 to 3, and X represents at least one functional group selected from the group consisting of a lower-alkyl group and a iower-alkoxyl group. It is preferable in this invention that the silane-based surface active material is a compound selected from a group consisting of CF 3 -(CF 2 ) n -T-SiY p Cl 3-p where n represents an integer from 1 to 25, T represents a member of the group consisting of an alkyl group, an ethylene group, an acetylene group and a substituted group containing a silicon atom and a hydrogen atom, Y represents a substituted group selected from the group consisting of an alkyl group, a cycloalkyl group, an aryl group and derivatives of these groups, and p represents a number selected from the group consisting of 0, 1 and 2, and CF 3 -(CF 2 ) n -T-SiZ q (OA) 3-q where n represents either 0 or an integer, T represents a member of the group consisting of an alkyl group, an alkylene group, an alkyne group, and a substituted group containing a silicon atom and a hydrogen atom, Z represents a substituted group selected from a group consisting of an alkyl group, a cycloalkyl group, an aryl group and derivatives thereof OA represents an alkoxy group with A representing a hydrogen atom or an alkyl group, and q represents 0, 1 or 2. It is preferable in this invention that the surface active material with the molecules thereof containing a plurality of chlorosilyl groups is a compound selected from the group consisting of SiCl 4 , SiHCl 3 , SiH 2 Cl 2 , and Cl-(SiCl 2 O) n - SiCl 3 , where n is an integer from to 10. It is preferable in this invention that the substrate having hydroxyl groups at the surface is a plastic substrate with the surface thereof treated in an oxygen-containing plasma atmosphere to be hydrophilic. It is preferable in this invention that the active hydrogen group on the substrate surface is a member of the group consisting of a hydroxyl group, an amino group and an imino group. It is preferable in this invention that the non-aqueous solution containing a chlorosilyl-based surface active material contains a crosslinking agent selected from the group consisting of SiP s Cl 4-s where P represents H, a lower-alkyl group and a lower-alkoxy group, and s represents of 0. 1 and 2. and SiQ t (OA) 4-t where Q is at least one substituted group selected from the group consisting of a lower-alkyl group and a lower-alkoxy group, A represents hydrogen atom or a lower-alkyl group, and t represents 0, 1 or 2. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a schematic sectional view, enlarged to a molecular level, showing a water- and oil-repelling coating film in the form of a monomolecular film as in example 2 of the invention; Figure 2 is a sectional view showing a 3 glass substrate having a coarsened surface used as in example 3 of the invention; Figure 3 is a schematic sectional view, enlarged to a molecular level, having the surface of a glass substrate with a monomolecular film formed thereon as in example 3 of the invention; Figure 4 is a schematic view, enlarged to a molecular level, showing the surface of an aluminum substrate prior to the film forming process as in example 4 of the invention; Figure 5 is a schematic sectional view showing a process of manufacturing a siloxane-bonded monomolecular film as in example 4 of the invention; Figure 6 is a schematic sectional view showing a process of manufacturing a fluorine-based monomolecular film as in example 4 of the invention; Figure 7 is a schematic sectional view, to an enlarged scale, showing the surface of a transparent glass plate with a water- and oil-repelling contamination-proof outer surface and an anti-fogging inside surface as in example 4 of the invention; Figure 8(a) is a schematic sectional view showing a polyethylene tetrachloride film prior to formation of a water-and oil-repelling film as in example 5 of the invention; Figure 8(b) is a schematic sectional view, enlarged to a molecular level, showing a portion E of film surface (a) after formation of the water- and oil-repelling film on the polyethylene tetrachloride as in example 5 of the invention; Figure 9(a) is a schematic sectional, enlarged to a molecular level, showing film surface prior to formation of a water- and oil-repelling film on a poly(ethylene terephthalate) film as in example 6 of the invention; Figure 9(b) is a schematic sectional view, enlarged to a molecular level, showing a poly(ethylene terephthalate) film surface during formation of the water- and oil-repelling film as in example 6 of the invention; Figure 9(c) is a schematic sectional view, enlarged to a molecular level, showing the poly(ethylene terephthalate) film surface after formation of the water- and oil-repelling film as in example 6 of the invention; DETAILED DESCRIPTION OF THE INVENTION The present invention relates to the formation of a water- and oil-repelling adsorbing film on a material having active hydrogen groups such as a hydroxyl group, an imino group and an amino group at the surface. This film is a chemically adsorbed film having surface irregularities exceeding 10 nanometers. It is directly or indirectly covalently bonded to the material surface and includes a monomolecular film or a polymer film with the molecules thereof containing a fluorocarbon group and a -Si- group. According to the invention a fluorine-containing chemically adsorbed monomolecular film is formed by siloxane bonds to the surface of a substrate after a surface roughening treatment thereof. It is thus possible to obtain a fluorine-based coating film, which is satisfactorily adhered to the substrate, is substantially pin-hole free, has desirable surface irregularities, has excellent water- and oil-repelling properties, is heat-resistant, weather-resistant, anti-contaminating, wear-resistant, etc. Further, according to the invention by including a step of coarsening the substrate by etching with a sand blast treatment, it is possible to provide the surface of a florocarbon-based coating film produced in a subsequent step with fine surface irregularities. Thus, it is possible to form a fluorocarbon-based coating film, which has desirable surface irregularities and excellent water- and oil-repelling properties. The polymer containing a fluorocarbon group is excellent in adhesion for it is chemically bonded to the substrate by -SiO-or -SiN= covalent bonds. Further, by inserting subsequent to the step of forming surface irregularities a step of contacting the substrate with a non-aqueous solution containing a material having a plurality of chlorosilyl groups to cause precipitation of the material with the molecule thereof containing a plurality of chlorosilyl groups on the substrate surface through a reaction brought about between hydroxyl groups of the substrate surface and chlorosilyl groups of the material and a step of removing excess material with the molecule thereof containing a plurality of chlorosilyl groups remaining on the substrate by washing with a non-aqueous organic solvent and then causing reaction with water, and carrying out a step of causing chemical adsorption to the substrate surface of a chlorosilane-based surface active material having a chlorosilane (-SiCl n X 3-n , n represents from 1 to 3, X represents a functional group) group at one end and a straight chain fluorocarbon group at the other end, a chemically adsorbed monomolecular fluorocarbon film can be produced, which has a higher molecular adsorption density. As the material with the molecule thereof containing a chlorocarbon group and a chlorosilane group may be used CF 3 -(CF 2 ) n -T-SiY p Cl 3-p and as the material with the molecules thereof having a fluorocarbon group and an alkoxyl group may be used CF 3 -(CF 2 ) n -T-SiZ q (OA) 3-q Further, for adjusting the hardness of the fluorocarbon-based polymer film, as the crosslinking agent may be use SiX s Cl 4-s where X represents a hydrogen atom or a substituted group such as an alkyl group and s represents 0, 1, or 2, or SiY t (OA) 4-t where A represents an alkyl group and t represents 0, 1, or 2. By so doing, the density of three-dimensional bridging in the produced fluorocarbon-based polymer film may be adjusted. That is, the hardness of the fluorocarbon-based polymer film having desirable surface irregularities can be controlled. The invention thus seeks to improve the performance of devices requiring heat-resistant, weather-resistant and wear-resistant coatings having excellent water- and oil-repelling properties. Such devices include electric products, vehicles and industrial apparatus. Further, according to the invention a fluorine-containing chemically adsorbed monomolecular film is formed at least via siloxane bonds on the surface of a substrate having surface irregularities less than the wavelength of visible light. It is thus possible to obtain a water- and oil-repelling coating film, which is excellent in luster and has an excellent anti-contaminating effect such that contaminants will not attach without difficulty or will be readily removed if attached. That is, the film is a very thin chemically adsorbed monomolecular film, in which siloxane groups are chemically bonded to the substrate, the outer layer of which has a portion containing fluorine groups. Thus, excellent luster and anti-contaminating effects can be obtained. These properties can be provided to articles in which it has been previously difficult to provide anti-contaminating effects thereto. According to the invention, the substrate is made of a member of the group consisting of glass, ceramics, metals, stone, and plastics. In a further aspect, usual glass, ceramic, stone, or metal products have hydrophilic surfaces containing hydroxyl groups. According to the invention, there is provided a method comprising a step of contacting a product with an aqueous solution containing molecules having a straight carbon chain having a chlorosilane at one end, e.g., a chlorosilane-based surface active material with the molecules thereof having a fluorocarbon group and a chlorosilane group, to precipitate of a monomolecular film of the material on the product surface through a reaction brought about between hydroxyl groups of the product surface and chlorosilyl groups of the material or contacting the product with a non-aqueous solution containing a material with the molecules thereof having a plurality of chlorosilyl groups to precipitate the material on the product surface through a reaction brought about between hydroxyl groups of the product surface and chlorosilyl groups of the material, a step of removing excess material with the molecules thereof having a plurality of chlorosilyl groups remaiming on the product surface by washing with a non-aqueous organic solution, thereby forming a siloxane-based monomolecular film of the material with the molecules thereof having a plurality of chlorosilyl groups on the substrate surface of the product, and a step of chemical adsorbing a silane-based surface active material with the molecules thereof containing a straight carbon fluoride chain having a chlorosilane group at one end to form a lamination chemically adsorbed monomolecular film. Thus, a lamination fluorocarbon chemically adsorbed monomolecular film may be formed on the product surface. In this case, by providing surface irregularities at a level less than the visible light wavelength (under about 400 nm , preferably from 10 to 300 nm (0.01 to 0.3 µm)) without spoiling the intrinsic luster of the product. Thus, it is possible to provide a high performance product having high water- and oil-repelling effects. Further, according to the invention on a coarsened film is formed a fluorine-containing chemically adsorbed monomolecular film via siloxane bonds. Thus, it is possible to obtain a water- and oil-repelling film, which includes a coating film having excellent water- and oil-repelling properties as well as heat-, weather- and wear-resistant properties. Further, according to the invention, the coarsened film has surface irregularities at a level less than 0.3 µm. In addition an excellent light transmission property can be obtained, and the light transmission property of the film in the visible light range is not hindered. Further, according to the invention, the material of the film is a poly(ethylene terephthalate) resin or a polyethylenetetrachloride resin. Thus materials which are suitable for cover films and protective films can be obtained. The invention is applicable to various fields. The invention can be widely applied to the following material surface. Materials made of metals, cermics or plastics, woods and stones etc. are applicable to the substrate. The surface of the substrate can also be coated with paints or the like. Examples of cutlery: a kitchen knife, scissors, a knife, a cutter, a graner, a razor, hair clippers, a saw, a plane, a chisel, a gimlet, a badkin, a bite (cutting tools), the edge of a drill, the edge of a mixer and juicer, a blade of a mill, a blade of a lawnmower, a punch, a straw cutter, a staple of a stapler, a can opener or a surgical knife and the like. Examples of needles: an acupuncture needle, a sewing needle, a matting needle, an injection needle, a surgical needle, a safety pin and the like. Examples of products in the pottery industry: products made of a pottery, a glass, ceramics or enameled products. For example, such as sanitary pottery (a chamber pot, a wash-bowl, a bathtub etc.), tableware (a rice-bowl teacup, a dish (plate), a bowl, a teacup, a glass, a bottle, a coffee-pot (siphon), a pan, an earthenware mortar, a cup and (the like), vases (a flower bowl, a flowerpot, a bud vase and the like), water tanks (a breeding cistern, an aquarium water tank and the like), chemical experiment appliances (a beaker, a reactor vessel, a test tube, a flask, a laboratory dish, condenser, a mixing rod, stirrer, a mortar, a bat, a syringe etc.) a roof tile, enameled ware, an enameled washbowl, and an enameled pan and the like. Examples of mirrors: a hand mirror, a full-length mirror, a bathroom mirror, a lavatory mirror, vehicle mirrors(a rear-view mirror, a side mirror, a door mirror etc.), half mirror, road mirrors such as a curve mirror, a show window glass, a salesroom in the department store, medical care mirrors, a concave mirror, a convex mirror and the like. Examples of molding parts: dies for press molding, dies for cast molding, dies for injection molding, dies for transfer molding, dies for compression molding, dies for transfer molding, dies for inflation molding, dies for vacuum molding, dies for blow forming, dies for extrusion molding, dies for fiber spinning, a calender processing roll and the like. Examples of ornaments: a watch, a jewel, a pearl, a sapphire, a ruby, an emerald, a garnet, a cat's eye, a diamond, a topaz, a bloodstone, an aquamarine, a turquoise, an agate, a marble, an amethyst, a cameo, an opal, a crystal, a glass, a ring, a bracelet, a brooch, a tiepin (a stickpin), an earring, a necklace, jewelry made of platinum, gold, silver, copper, aluminium, titanium, tin and those alloy, stainless steel, a glass frame and the like. Examples of forming molds for food: cake, cookies, breadbaking, chocolate, jelly, ice cream, ovenware, ice trays and the like. Examples of cookware: kitchen utensils (a pan and a pot), a kettle, a pot, a frying-pan, a hot plate, a toasting net, a takoyaki plate and the like. Examples of papers: photogravure paper, hydrophobic and oilphobic paper, poster paper, high-grade pamphlet paper, wrapping paper, package paper, drinking package paper, container paper, printing paper, synthetic insulating paper and the like. Examples of resin(s): a polyolefin such as a polypropylene and polyethylene, a polyvinylchloride plastic, a polyamide, a polyimide, a polyamideimide, a polyester, an aromatic polyester, a polycarbonate, a polystyrene, a polysulfide, a polysulfone, a polyethersulfone, a polyphenylenesulfide, a phenolic resin, a furan resin, a urea, an epoxy resin, a polyurethane, a silicon resin, an ABS resin, a methacrylic resin, an acrylate resin, a polyacetal, a polyphenylene oxide, a polymethylpentene, a melamine resin, an alkyd resin, an unsaturated polyester resin and the like. Examples of rubber: styrene-butadiene rubber, butyl rubber, nitril rubber, chloroprene rubber, polyurethane rubber, silicon rubber and the like. Examples of household electrical appliances: a television, a radio, a tape recorder, an audio device, a compact disc (CD) device, a refrigerator, a freezer, an air conditioner, a juicer, a mixer, a blade of an electric fan, a lighting apparatus, a dial plate, a dryer for perms and the like. Examples of sports articles: skis, fishing rods, poles for pole vaulting, boats, yachts, surfboards, golf balls, bowling balls, fishing line, fishing nets, floats and the like. The examples applying to vehicle parts: (1) ABS resin: a lamp cover, an instrument panel, trimming parts, a protector for a motorcycle. (2) Cellulose plastic: a car mark, a steering wheel (3) FRP (fiber reinforced plastics): a bumper, an engine cover (jacket) (4) Phenolic resin: a brake (5) Polyacetal: wiper gear, a gas valve (6) Polyamide: a radiator fan (7) Polyarylate (polycondensation polymerization by bisphenol A and pseudo phtalic acid): a directional indicator lamp or lens, a cowl board lens, a relay case (8) Polybutylene terephthlate (PBT): a rear end, a front fender (9) Poly(amino-bismaleimide): engine parts, a gear box, a wheel, a suspension drive system (10) Methacrylate resin: a lamp cover lens, a meter panel and its cover, center mark (11) Polypropylene: a bumper (12) Polyphenylene oxide: a radiator grill, a wheel cap (13) polyurethane: a bumper, a fender, an instrument panel, a fan (14) Unsaturated polyester resin: a body, a fuel, tank, a heater housing, a meter pannel. Examples of office supplies: a fountain pen, a ballpoint pen, a propelling pencil (an automatic or a mechanical pencil), a pencil case, a binder, a desk, a chair, a bookshelf, a rack, a telephone stand table, a rule (measure), a drawing instrument and the like. Examples of building materials: materials for a roof, an outer wall and interiors. Roof materials such as a brick, a slate and a tin (a galvanized iron sheet) and the like. Outer wall materials such as wood (including a processed manufactured wood), mortar, concrete, ceramics sizing, a metalic sizing, a brick, a stone, plastics and a metal such as aluminium. Interior materials such as a wood (including processed wood), a metal such as aluminium, plastics, paper, fiber and the like. Examples of building stones: granite, marble and others used for such as a building, a building material, an architectural fixture, an ornament, a bath, a grave, a monument, a gatepost, a stone wall, a paving stone and the like. Examples of musical instruments and sound apparatus: a percussion instrument, a stringed instrument, a keyboard instrument, a woodwind instrument, brass and others, and sound apparatus such as a microphone and a speaker. To be specific, there are musical instruments such as a drum, a cymbal, a violin, a cello, a guitar, a koto (harp), a piano, a flute, a clarinet, a bamboo flute and a horn, and sound apparatus such as a microphone, a speaker and an ear-phone and the like. Examples of a thermos bottle, a vacuum bottle, a vacuum vessel and the like. Examples of a highly resisiting voltage insulator such as a power supplying insulator or a spark plug, which are highly hydrophobic, oilphobic and aid in preventing contamination. Now, examples of the invention will be given. Unless otherwise specified, % is by weight in the examples. Example 1 A processed glass plate was prepared. After washing with an organic solution, its surface was coarsened by sand blasting to form surface irregularities on a sub-micron order of 0.1 to 1.0 microns, for example 0.4 to 0.9 microns. The surface irregularities may also be formed by a chemical etching process using fluorine oxide or a rubbing process using sand paper. Subsequently, the glass plate was dipped and held for about 2 hours in a non-aqueous solution containing a material having a fluorocarbon chain group and a chlorosilane group. For example a solution was obtained by dissolving 1 % by weight of CF 3 (CF 2 ) 7 (CH 2 )SiCl 3 into a solution containing 80 % of n-hexadecane (or toluene, xylene or dicyclohexyl), 12 % of carbon tetrachloride and 8 % of chloroform. As a result, a hydrochloric acid removal reaction (dehydrochlorination) was brought about between the -SiCl groups of the material containing a fluorocarbon group and a chlorosilane group and the hydroxyl groups contained in the surface of natural oxide film formed on the glass plate surface, thus producing bonds of CF 3 (CF 2 ) 7 (CH 2 )Si(O-) 3 over the entire glass plate surface. Thus, a fluorine-containing monomolecular film was formed which was chemically bonded to the glass plate surface and had a thickness of about 15 angstroms. This monomolecular film was chemically bonded and difficult to separate. With a glass plate comprising a plastic material such as an acrylate resin or a polycarbonate resin, the same technique could be used by oxidizing the coarsened surface to be hydrophilic by a plasma process at 300 W for about 10 minutes and using a freon solvent in lieu of the surface active material. The processed glass plate was trial used to find that the attachment of contaminants could be greatly reduced compared to a glass plate which was not processed. Contaminants that were attached could be readily removed by rubbing the glass plate with a brush. At this time, no scar or scratch was produced. Further, oily fat contaminants could be removed by merely water washing. The wetting property with respect to water is similar to that of lotus leaves, and the contact angle was 155 degrees. Example 2 With an aluminum plate, which contains less hydroxyl groups although it remains hydrophilic, surface irregularities of about 0.5 to 0.8 micron are formed by electrolytic etching. Surface irregularities may also be formed by a chemical etching process using fluorine oxide, a plasma spattering process carried out in vacuum or a rubbing process using sand paper. Metal substrates may all be similarly treated. With a substrate of a plastic material such as an acrylate resin or a polycarbonate resin, the same technique is used after coarsening the surface and then oxidizing the surface to be hydrophilic by a plasma process carried out at 200 W for about 10 minutes. Then, the plate is dipped and held for about 30 minutes in a non-aqueous solution containing a material having a plurality of chlorosilyl groups. For example, a solution was obtained by dissolving 1 % by weight of SiCl 4 in a chloroform solvent, and a hydrochloric acid removal reaction was brought about owing to the -OH groups present to a certain extent at the aluminum plate surface. A chlorosilane monomolecular film of the material containing a plurality of chlorosilyl groups was formed. For example, by using SiCl 4 as the material containing a plurality of chlorosilyl groups, a dehydrochlorination reaction is brought about owing to the hydrophilic -OH groups exposed at the aluminum plate surface, and molecules of Cl 3 SiO- or Cl 2 Si(O-) 2 are secured to the surface by -SiO- bonds. By subsequently washing the system with a non-aqueous solvent, e.g., chloroform, and then with water, unreacted SiCl 4 molecules are removed from the aluminum plate to obtain a siloxane monomolecular film of (OH) 3 SiO - or (OH) 2 Si(O-) 2 on the aluminum plate surface. The monomolecular film thus obtained is perfectly bonded to the aluminum plate 46 by chemical bonds of -SiO- and did not separate. In addition, its surface has numerous -SiOH (or silanol) bonds. Further, hydroxyl groups corresponding in number to about three times the initial number are produced. As an example, the aluminum plate 46, provided with a monomolecular film having numerous surface -SiOH bonds, was dipped and held for about one hour in a non-aqueous solution containing a material containing a carbon fluoride group and a chlorosilane group. For example a solution was obtained by dissolving about 1 % of CF 3 (CF 2 ) 7 (CH 2 )SiCl 3 in a solution containing 80 % of n-hexadecane, 12 % of carbon tetrachloride and 8 % of chlorofrom. As a result, bonds of CF 3 (CF 2 ) 7 (CH 2 )Si(O-) 3 were formed on the aluminum plate surface. A fluorine-containing monomolecular film 48 was formed over the entire aluminum plate 46 surface. The film was chemically bonded (i. e., covalently bonded) to the inner siloxane monomolecular film 47 and had a thickness of about 15 angstroms (1.5 nm). It did not separated in a checkerboard test. Its water contact angle was about 155 degrees. Further, using a glass plate in lieu of the aluminum plate in the above Example 8, on the surface desired to remain hydrophilic (for example the inner surface) was formed a hydrophilic coating film insoluble in an organic solvent (for example by coating an aqueous solution of polyvinylalcohol (poval) to a thickness of several microns) for the purpose of imparting an anti-fogging effect before carrying out chemical adsorption of the material containing a carbon fluoride group and a chlorosilane group. After the chemical adsorption, the hydrophilic coating film was removed by water washing, thus obtaining a glass plate provided with a monomolecular film (or siloxane film), which had a water- and oil-repelling contamination free outer layer and hydrophilic hydroxyl groups present at the inner surface. The anti-fogging effect of this glass plate was tested to find that its surface was left hydrophilic and could be readily wetted by water and would not fog. By carrying out the chemical adsoprtion using a mixture of two different surface active materials with different molecular lengths, for example CF 3 (CF 2 ) 7 (C H 2 ) 2 Si(CH 3 ) 2 (CH 2 ) 9 SiCl 3 and CF 3 (C F 2 ) 7 (CH 2 ) 2 Si(CH 3 ) 2 (CH 2 ) 6 SiCl 3 or CF 3 (CF 2 ) 7 (CH 2 ) 2 SiCl 3 and CF 3 (CF 2 ) 5 (CH 2 ) 2 SiCl 3 the mixture being in a ratio of about 3 : 1 to 1:3, the water- and oil-repelling properties are further improved. Example 3 A processed glass plate 61 was washed with an organic solvent, and irregularities of about 0.1 micron were formed at its surface by sand blasting (figure 2). As another means for coarsening the surface, a chemical etching process using fluoric acid or a rubbing process using sand paper may be used. The permissible level of coarsening is within the visible light wavelength range. In this case, substantially all visible light is transmitted. As an example. a glass plate was dipped and held for about 2 hours in a non-aqueous solution containing a material containing a carbon fluoride group and a chlorosilane group. For example a solution was prepared by dissolving 1 % by weight of CF 3 (CF 2 ) 7 (CH 2 ) 2 SiCl 3 in a solution containing 80 % of n-hexadecane (or toluene, xylene or disiclohexyl), 12 % of carbon tetrachloride and 8 % of chloroform. As a result, a dehydrochlorination reaction was brought about between SiCl groups of the material containing a carbon fluoride group and a chlorosilane group and hydroxyl groups numerously contained in the natural oxide film formed on the glass plate, thus producing bonds of CF 3 (CF 2 ) 7 (CH 2 ) 2 Si(O-) 3 over the entire glass plate surface. A fluorine-containing monomolecular film 62 was formed. The film 62 was chemically bonded to the glass plate surface, and its thickness was about 1.5 nm (15 angstroms) (Figure 3). The monomolecular film was firmly bonded by siloxane chemical bonds to the substrate surface and did not separate. In a substrate comprising a plastic material, such as an acrylic acid resin or a polycarbonate resin, the same technique may be used by oxidizing the substrate surface to be hydrophilic by a plasma treatment at 300 W for about 10 minutes and using a freon solution in lieu of the surface active material. The above processed glass plate was actually used to obtain great reduction of the attachment of contaminants compared to a non-processed glass plate. Contaminant attached, if any, could be readily removed by brushing with a brush. At this time, no scar or scratch was caused. The water wetting property was like that of lotus leaves, and the water contact angle was about 155 degrees. Example 4 In this example, an aluminum plate is used, the surface of which contains less hydroxyl groups yet remains hydrophilic. The surface is formed with irregularities of about 0.2 microns by electrolytic etching. The surface irregularities may also be formed by other processes such as a chemical etching process using fluoric acid or a rubbing process using sand paper. Again in this case, the surface irregularities may be within the visible light wavelength range. In this case. substantially all visible light is transmitted. The same technique may be used for all metals. In case of a plastic material such as an acrylic acid resin or a polycarbonate resin, the surface having been coarsened is oxidized to be hydrophilic by a plasma treatment at 200 W for about 10 minutes. The aluminum plate is then dipped and held for about 30 minutes in an aqueous solution containing a material containing a plurality of chlorosilyl groups, e.g., a solution prepared by dissolving 1 % by weight of SiCl 4 , the molecules of which are small and have high activity to hydroxyl groups, in a chloroform solvent. The solution is highly effective for rendering the aluminum plate surface to be uniformly hydrophilic. As a result, a hydrochloric acid removal reaction is brought about owing to the presence of some -OH groups 72 at the aluminum plate surface 71 (Figure 4), thus forming a siloxane-based monomolecular film. By using Sicl 4 as the material containing a plurality of chlorosilyl groups, a hydrochloric acid reaction is brought about on the surface of the aluminum plate 71 owing to hydrophilic -OH groups exposed at the surface. The molecules are secured to the surface via -SiO- bonds such as Cl 3 SiO- and/or Cl 2 Si (O-) 2 . By subsequently washing the system with a non-aqueous solution, e.g., chloroform, and then with water, unreacted SiCl 4 molecules are removed, and a siloxane monomolecular film 73 of (OH) 3 SiO- and/or (OH) 2 S i(O-) 2 is obtained on the aluminum plate surface (Figure 5. The monomolecular film 73 thus formed is perfectly bonded to the aluminum plate by chemical bonds of -SiO- and are difficult to separate. The film surface contains numerous silanol (-SiOH) bonds corresponding in number to about three times the number of initial hydroxyl groups. As an example, the aluminum plate thus obtained, provided with the monomolecular film with numerous -SiOH bonds at the surface, was dipped and held for about one hour in an aqueous solution containing a material containing a carbon fluoride group and a chlorosilane group, e.g., a solution prepared by dissolving about 1 % of CF 3 (CF 2 ) 7 (CH 2 ) 2 SiCl 3 in a solution containing 80 % of n-hexadecane, 12 % of carbon tetrachloride and 8 % of chloroform. As a result, bonds of CF 3 (CF 2 ) 7 (CH 2 ) 2 Si(O-) 3 were formed on the aluminum plate surface. A fluorine-containing monomolecular film 74 thus was formed over the entire aluminum plate surface. It was chemically bonded to the inner siloxane monomolecular film and had a thickness of about 1.5 nm (15 angstroms) (Figure 6). It did not separate in a peel-off test. Its water contact angle was about 155 degrees. Meanwhile, using a glass plate in lieu of the aluminum plate in the above example 4, a hydrophilic coating film insoluble to organic solvents and having a thickness of several microns was formed a surface (for instance the inner surface) which was desired to remain hydrophilic for imparting with an anti-fogging effect. For example an aqueous solution of polyvinylalcohol (poval) or pullulan was coated onto the surface, before chemically adsorbing the material containing a carbon fluoride group and a chlorosilane group. After the adsorption, the hydrophilic coating film was removed by water washing, thus obtaining a transparent glass plate, which had a water- and oil-repelling anti-contaminating monomolecular film 74 formed on its outer surface. A monomolecular film (or siloxane film) 73 having hydrophilic hydroxyl groups was formed on its inner surface, as shown in Figure 7. The anti-fogging effect of this glass plate was checked to find that its surface remained hydrophilic and was readily wetted by water and did not fog. By adsorbing a composition obtained by combining two different surface active materials with different molecular lengths, surface irregularities were obtained at the molecular level, thus further improving the water- and oil-repelling properties and further enhancing the anti-contaminating effects. As shown above, in this example a glass plate or like material is formed with surface irregularities of about 0.1 micron (µm) . The material is dipped in, for example, a fluorine-containing chlorosilane-based surface active agent diluted in an organic solvent. As a result, a hydrochloric acid removal reaction is brought about owing to numerous hydroxyl groups contained at the surface of a natural oxide film formed on the surface of the glass plate or the like. A carbon fluoride-based monomolecular film is thus formed on the substrate surface via siloxane bonds. In this way, surface irregularities less than the visible light wavelength range (400 nm) are formed on the substrate surface, and a carbon fluoride-based monomolecular film with a thickness of a nanometer level is formed on the substrate surface via siloxane bonds, thus obtaining a very highly water- and oil-repelling anti-contaminating film without spoiling the luster of the substrate itself. Example 5 As shown in Figure 8, a polyethylene-trifluorochloride film 81 with a thickness of 100 to 200 mcicrons (µm) was prepared and held in a vacuum chamber at 10 -1 to 10 -2 Pa. Then, its surface was spatter etched in an oxygen-containing plasma atmosphere by RF glow discharge. This process was carried out with a discharge power density of 0.15 W/cm 2 9 for 1 to 10 minutes, thus forming surface irregularities of about 0.1 micron. The film did not become opaque (Figure 8(a). Actually, the surface coarseness may be less than 0.3 micron, which is sufficiently small compared to the wavelength of visible light. Under this condition, the film did not become opaque. The etching condition may be appropriately selected. Subsequently, the film with the surface thereof coarsened was dipped and held for one hour in a non-aqueous solution containing a material having a fluorocarbon group and a chlorosilane group. For example an "Aflood" (a fluorine-based solvent by Asahi Glass Co.,Ltd.) solution was prepared by dissolving about 5 % of a material represented by the formula: CF 3 (CF 2 ) 7 (CH 2 ) 2 SiCl 3 As a result, a dehydrochlorination reaction is brought about on the film surface having been etched in an oxygen plasma owing to hydroxyl (-OH) groups formed at the surface, thus producing bonds represented by the formula [3]: on the film surface. The film was then washed with "Aflood" to remove the unreacted material remaining on the surface, followed by washing with water or exposing to air containing moisture. The -SiCl group was changed to a -SiOH group as the formula [4]. Each silanol group (-SiOH) was then dehydrated and crosslinked to form a siloxane bond (-SiO-) after drying as the formula [5]. Drying temperature may be room temperature or above. The adsorbed monomolecular film 82 has a fluorine group and is chemically bonded (i.e., covalently bonded) to the substrate 1. The chemical bond is via a siloxane bond. The formation of chemically adsorbed monomolecular film 3 was assumed by FTIR spectrometry and the thickness was about 1.5 nanometers (nm). It is firmly bonded such that it will not separate. A fluorine-contaiing monomolecular film 82 was formed which was chemically bonded to the surface and had surface irregularities at the micron level. Figure 8(b) is an enlarged schematic view showing part E in Figure 8(a). In this case, fluorocarbon groups were formed in a regular orientation on the surface, and the surface energy was extremely low. The water contact angle was 135 to 145 degrees. Example 6 A polyethylene terephthalate film 91, for example, was prepared and held in a vacuum chamber at 10 -1 to 10 -2 Pa. Then, the film surface was spatter etched in an oxygen-containing plasma atmosphere based on RF glow discharge, the process was carried out with a discharge power density of 0.1 W/cm 2 for 1 to 5 minutes, thus forming surface irregularities. The surface coarseness obtained was about 0.1 micron, and the film did not become opaque. Actually, the film would not become opaque as so long as the surface coarseness is less than 0.3 micron. The etching condition may be appropriately selected. With a film which need not be transparent, it was possible to coarsen the surface to about several tens of microns to obtain sufficient effects. The film with the surface thereof coarsened was then dipped and held for about one hour in an "Aflood" solution (a fluorine-containing material by Asahi Glass Co., Ltd.) prepared by dissolving about 5 % of SiCl 4 into the "Aflood". As a result, a dehydrochlorination reaction is brought about on the film surface having been etched by oxygen plasma owing to hydroxyl (-OH) groups 92 contained at the surface, as shown in Figure 9(a). Thus, molecules represented by formulas 6 and 7 are secured to the film surface via -SiO- bonds. By subsequently washing the system with a non-aqueous solvent, e.g., "Aflood" (a fluorine-based solvent by Asahi Glass Co., Ltd., and then with water, SiCl 4 molecules which did not react with the film were removed. A siloxane monomolecular film 93 represented by a formula 8 or formula 9 was obtained, as shown in Figure 9(b). It is chemically bonded. As an example, the film provided with the monomolecular film as noted above was dipped and held for about one hour in a non-aqueous solution containing a material having a fluorocarbon group and a chlorosilane group, e.g., a solution prepared by dissolving about 3 % of a material represented by formula: CF 3 (CF 2 ) 7 (CH 2 ) 2 SiCl 3 in "Aflood" (a fluorine-containing solvent by Asahi Glass Co., Ltd.). As a result, a dehydrochlorination reaction was brought about owing to numerous hydroxyl (-OH) groups contained at the film surface, thus producing bonds represented by the formula: CF 3 (CF 2 ) 7 (CH 2 ) 2 Si(O-) 3 on the film surface. A fluorine-containing monomolecular film 94 was formed as shown in Figure 9(c). The film thus obtained was chemically bonded and had surface irregularities at the micron level. It had high density compared to the film in Example 5. This monomoecular film will not separate in a checkerboard test. In addition, fluorocarbon groups were oriented on the surface, and the surface energy was extremely low. The water contact angle was 140 to 150 degrees. Further, using an adhesive, a glass plate was applied to the back surface of the water- and oil-repelling film thus obtained. A very water- and oil-repelling and highly transparent glass plate was obtained. Contaminants did not attach without difficultly, and could be easily removed. Thus, the glass plate was very highly practical. As in the above example, a chlorosilane-based surface active material containing a chlorosilane (SiCl n X 3-n , n representing 1, 2 or 3, X representing a functional group) group at one end and a straight chain carbon fluoride group at the other end is chemically adsorbed via siloxane bonds to a film surface having been coarsened on the order of sub-microns to microns by means of etching, sand blasting or a mold application process, thus forming a carbon fluoride chemically adsorbed monomolecular film. The film is highly water- and oil-repelling and does not separate. The coarseness of the film surface is on the order of sub-microns to microns, and the thickness of the monomolecular film is at the namometer level. Thus, the film has an excellent light transmission property, does not hinder optical characteristics of the film and is excellent in durability. By adding or assembling a vinylene group or ethylene group to the alkyl chain portion, the monomolecular film is crosslinked after formation by irradiating it with an electron beam of about 5 Mrads. Thus, hardness is improved. According to the invention, a very highly water- and oil-repelling carbon fluoride-based chemically adsorbed monomolecular film may be formed on a film surface by a method which comprises a step of coarsening the film surface on the order of sub-microns to microns in advance by means of etching, sand blasting or a mold application process and a step of forming on the film surface a chemically adsorbed monomolecular film by chemically adsorbing a chlorosilane-based surface active material containing a chlorosilane group, SiCl n X 3-n , (where n represents 1. 2 or 3, X represents a functional group) at one end and a straight chain carbon fluoride group at the other end. Further, a fluorine-containing carbon fluoride-based chemically adsorbed monomolecular film having a relating high molecular adsorption density, can be obtained by a method which comprises, subsequent to the step of coarsening the film surface on the order of sub-microns to microns by means of etching, sand blasting a mold application process, a step of contacting the coarsened film surface with a non-aqueous solution containing a material containing a plurality of chlorosilyl groups to cause a reaction between hydroxyl groups at the film surface and the chlorosilyl groups of the material containing a plurality of chlorosilyl groups and a step of removing excess material containing a plurality of chlorosilyl groups remaining on the film by washing with a non-aqueous organic solvent and then reacting with water, before the step of forming a monomolecular film of the material containing a plurality of silanol groups and the step of forming an accumulation of the chemically adsorbed monomolecular film by chemically adsorbing a chlorosilane-based surface active material containing a chlorosilane group at one end and a straight chain carbon fluoride group at the other end to the film surface. The coarseness of the film surface is of the order of sub-microns to microns, preferbly 0.3 microns or less. In this case, an excellent light transmission property is obtained, and light transmission properties of the film in the visible light wavelength range are not hindered. If the coarseness of the film surface is greater than 0.3 microns, the water- and oil-repelling properties are not adversely affected, although optical characteristics are slightly sacrificed. Thus, even in this case, the film can find extensive applications. The surface coarseness is suitable for use in light-blocking films or frost glass. Further, the film may be readily applied by an adhesive on its back surface to an intended object without adversely affecting optical characteristics. A peel-off sheet may be present on the surface of the adhesive. The water- and oil-repelling film according to the invention may be applied to glass products such as vehicle windows or font glasses, glass lenses and building windows glasses, ceramic products such as porcelain articles, dishes, vases and water tanks, metal products such as sashes, doors and exterior walls of buildings, furniture, cover films, etc. Examples of the film are fluorine resin-based films of poly(ethylene trifluorochloride), etc., polyester-based films of poly(ethylene terephthalate), etc., polyimide-based films, polyamide-based films of nylon, etc., polyethylene films and polypropyrene films. The water wetting property was like that of lotus leaves, and the water contact angle was about 155 degrees. As has been shown, the invention is greatly beneficial to industry.

Claims: A method of manufacturing a water- and oil- repelling adsorbing film comprising: providing a substrate surface with active hydrogen groups, before or after making this substrate surface irregular; and contacting said irregular surface with a non-aqueous solution containing an active surface material having a fluorocarbon group and a chlorosilane group or having a fluorocarbon group and an alkoxysilane group. The method of claim 1 wherein said substrate surface is made irregular by electrolytic etching, chemical etching, sand blasting, spattering, depositing or rubbing. The method according to claim 1 comprising the steps of: forming surface irregularities on the substrate and then providing the substrate surface with active hydrogen groups; contacting the substrate surface with a silane-based surface active material the molecules of said surface active material containing a silyl group at one end and a fluorocarbon group at the other end to adsorb said surface active material to the substrate surface by a dehydrochlorination reaction or a dealcoholation reaction; forming an outer layer by reacting with water with or without previous removal of non-reacted surface active material by washing using a non-aqueous organic solution; and drying or thermally treating the substrate surface. The method acording to claim 1 comprising the steps of: forming surface irregularities on the substrate and then providing the substrate surface with active hydrogen groups; contacting the substrate surface with a non-aqueous solution containing a surface active material, the molecules of said surface active material having a plurality of chlorosilyl groups to adsorb said surface active material to the substrate surface by a dehydrochlorination reaction; forming an inner layer by reacting with water with or without previous removal of non-reacted surface active material by washing with a non-aqueous organic solvent; contacting the surface of said inner layer with a silane-based surface active material the molecule thereof containing a silyl group at one end and a fluorocarbon group at the other end to adsorb said surface active material to the inner layer substrate surface by a dehydrochlorination reaction or a dealcoholation reaction; forming an outer layer by reacting with water with or without previous removal of non-reacted surface active material by washing with a non-aqueous organic solution; and drying or thermally treating the substrate surface. The method according to claim 3 or 4 wherein the molecules of said chlorosilyl-based surface active material have at one end a chlorosilane group represented by formula: -SiCl n X 3-n wherein n represents an integer from 1 to 3, and X represents at least one functional group selected from the group consisting of a lower-alkyl group and a lower-alkoxyl group. The method according to claim 3 or 4 wherein said silane-based surface active material is a compound having the formula CF 3 (CF 2 ) n TSiY p Cl 3-p wherein n represents an integer from 1 to 25, T represents a member of the group consisting of an alkyl group, an ethylene group, an acetylene group and a substituted group containing a silicon atom and a hydrogen atom, Y represents a substituted group selected from the group consisting of an alkyl group, a cycloalkyl group, an aryl group and derivatives of these groups, and p represents a number selected from the group consisting of 0, 1 and 2, or having the formula: CF 3 (CF 2 ) n TSiZ q (OA) 3-q wherein n represents either 0 or an integer, T represents a member of the group consisting of an alkyl group, an alkylene group, an alkyne group, and a substituted group containing a silicon atom and a hydrogen atom, Z represents a substituted group selected from a group consisting of an alkyl group, a cycloalkyl group, an aryl group and derivatives thereof, OA represents an alkoxy group with A representing a hydrogen atom or an alkyl group, and q represents 0, 1 or 2. The method according to claim 4, wherein said surface active material is a compound selected from the group consisting of SiCl 4 , SiHCl 3 , SiH 2 Cl 2 , and Cl(SiCl 2 O) n SiCl 3 , wherein n is an integer from 1 to 10. The method according to claim 1, wherein said substrate is a plastic substrate with the surface thereof treated to be hydrophilic in an oxygen-containing plasma atmosphere. The method according to claim 3 or 4 wherein said active hydrogen group on the substrate surface is a member of the group consisting of a hydroxyl group, an amino group and an imino group. The method according to claim 3 or 4, wherein said non-aqueous solution containing a chlorosilyl-based surface active material contains a crosslinking agent having the formula SiP s Cl 4-s wherein P represents H, a lower-alkyl group and a lower-alkoxy group, and s represents of 0, 1 and 2; or having the formula SiQ t (OA) 4-t wherein Q is at least one substituted group selected from the group consisting of a lower-alkyl group and a lower-alkoxy group, A represents a hydrogen atom or a lower-alkyl group, and t represents 0, 1 or 2. The method according to claim 1, wherein said substrate is a plastic film. The method according to claim 11, wherein said plastic film has a coarsened surface with surface irregularities at a level of less than 0.3 µm.

Inventors: MINO NORIHISA, OGAWA KAZUFUMI, SOGA MAMORU, MINO, NORIHISA, OGAWA, KAZUFUMI, SOGA, MAMORU
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD
Application year: 1992
Main classification: C09D183
IPC codes: C09D183, B05D1, C08J7, C03C17, C09D4