Method for making ice slab and artificial snow

Abstract: A method for easily making an ice slab serving as the foundation of an artificial snow skiing field and artificial snow whose upper layer is powdery by flooding aqueous slurry made by adding water to granular wet water absorbent polymer on a slope of a natural skiing field or a slant or horizontal surface of a natural skiing field or indoor artificial snow skiing field equipped with a cooling system, obtaining the deposit layer of the granular wet water absorbent polymer in which water is separated from the slurry and freezing the deposit layer.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for making an ice slab covered by artificial snow. 2. Description of the prior art One of the methods for making artificial snow in an artificial skiing field is by freezing spray atomized water using compressed air (or other compressed gas) into an atmosphere having a temperature of freezing point or lower. However, this method is not profitable because the equipments are expensive to install and a lot of compressed air is necessary. Japanese Patent Publication No. 36635/1990 discloses a method for making artificial snow by aerating wet water absorbent polymer having water added at less than its water retention capacity, and thereafter freezing them. In this method, however, the aerated granular wet water absorbent polymer is a gel. Therefore, to scatter the gel on the slope of the skiing field, it is necessary to transfer the gel by compressed air. It is also necessary to separately prepare an ice slab for protecting the coolant circulating pipes installed on the floor for refrigeration. Moreover, to collect melted artificial snow and reuse it by cleaning it with water, it is necessary to adjust the amount of absorbed water after cleaning and dry the collected water absorbent polymer. Therefore, the method is not profitable because operation is complex. U.S.Patent No.3,251,194 discloses a method for making a skating rink by freezing water absorbent polymer and water but it does not disclose a method for making artificial snow using specific water absorbent polymer and specified amount of water. EP-A-0 440 257 which is prior art under Article 54(3)EPC discloses a method of making artificial snow by freezing a water-swollen granular absorbent polymer which maintains its granular shape after water-swelling. The same granular water absorbent polymer may be used in the present invention. The present invention provides a method for simultaneously making an ice slab for protecting a freezing system equipped on the foundation of the artificial snow field and powdery artificial snow covering the ice slab by a simple system and operation. Particularly, the present invention provides a method for making an ice slab and powdery artificial snow with a single operation by freezing a fluid aqueous slurry of granular wet water absorbent polymer which is laid up on a horizontal or sloped floor. SUMMARY OF THE INVENTION As the result of studying a method for simply making an ice slab used for foundation of the skiing field of artificial snow and powdery or hard artificial snow covering said ice slab, the inventors of the present invention completed this invention by finding that artificial snow having a bottom layer formed as an ice slab and an upper layer formed as powdery snow can easily be made by freezing granular wet water absorbent polymer consisting of grains of wet water absorbent polymer, said wet water absorbent polymer meaning water absorbent polymer containing absorbed water or aqueous solution. Moreover, the inventors found that, when the fluid aqueous slurry of granular wet water absorbent polymer made by adding water to granular wet water absorbent polymer is poured on the foundation of the artificial snow skiing field, water easily separates from the aqueous slurry to form a piled up layer of the granular wet water absorbent polymer, and powdery artificial snow can be obtained by freezing the piled up layer. Artificial snow having a bottom part formed as an ice slab and an upper part formed as powdery snow can easily be made by adjusting the amount of water remaining in the piled up layer and then freezing said piled up layer. Based on these findings the invention provides a method for making an ice slab and artificial snow as claimed in claim 1. Claims 2 to 20 relate to further advantageous features of the invention. A definition of the terms used for the present invention and their measuring method are described below in order to describe the present invention in detail and as an aid for understanding the contents of the present invention. However, the contents of the present invention are not limited by the definition of the terms and their measuring method. Therefore, it is possible to use other measuring method unless it deviates from the gist of the present invention. BRIEF DESCRIPTION OF THE PHOTOGRAPHS Photograph No.1 is the microscopic photograph showing a crystalline structure of artificial snow of the present invention. The unit of scale shown in it is 1mm. Photograph No.2 is the microscopic photograph showing a condition wherein the crystalline structure of the artificial snow is melted. The unit of scale shown in it is the same as the photograph No.1. DETAILED DESCRIPTION OF THE INVENTION A. Definition Ice slab : Defined as flat ice or ice-containing material which is mainly provided on the foundation of an artificial snow field and used to reinforce the foundation and/or protect the cooling pipes laid on the foundation. Artificial snow : Defined as powdery ice, ice-containing material, or solid consisting of combined grains of powdery ice or ice-like material, which do not need to have a crystalline structure like natural snow. Water absorbent polymer : Defined as macromolecular compound being capable of absorbing water or aqueous solution. Synthetic-resin-based macromolecular compounds such as polymer, copolymer, and terpolymer of acrylamide, acrylic acid, salt of acrylic acid, salt of methacrylic acid, styrene, and vinyl ether are listed as water absorbent polymer useful for the present invention. To form these water absorbent polymers into a granular water absorbent polymer which is one mode used for the present invention, there is a method to crush these macromolecular compounds and form them into the predetermined size and shape of grains and a method to directly form macromolecular compounds into granular shape by polymerizing or condensing them. Particularly, a preferable method is to saponify the spherical polyacrylate obtained through reversed phase suspension polymerization, copolymer of vinyl alcohol and acrylate, or copolymer of isobutylene and maleic anhydride. Wet water absorbent polymer : Defined as water absorbent polymer after absorbing water or aqueous solution. Granular wet water absorbent polymer : Defined as an aggregate of the wet water absorbent polymer whose shape is granular. Individual grain is expressed as the grain of the granular wet water absorbent polymer. In this case, the term "granular" represents the condition in which voids are existing between the grains when each grain retains its shape and the grains are aggregated. That is, granular wet water absorbent polymer is defined as an aggregate of grains of the wet water absorbent polymer each in which each grain has a distinguishable shape and voids are existing between the grains and there is no water between the grains though a small amount of water is present on the surface of each grain. The granular wet water absorbent polymer used for the present invention is made by adding water to the granular water absorbent polymer, or by adding water to non-granular water absorbent polymer or to granular water absorbent polymer consisting of large grains, and then crushing it, or it may be granular wet water absorbent polymer which already has absorbed water in the grain state when manufacturing the water absorbent polymer. Aqueous slurry of the granular wet water absorbent polymer : Defined as water or aqueous solution in which the granular wet water absorbent polymer is suspended. The aqueous slurry includes the following two types: one consisting of the granular water absorbent polymer and filler water (hereinafter defined) and the other consisting of the granular wet water absorbent polymer, filler water, and free water (hereinafter defined). Water absorption : Defined as increase of weight due to of water or aqueous solution absorbed in the water absorbent polymer over the weight of the water absorbent polymer before absorbing water or aqueous solution, which is measured by the method to be mentioned later. Water for absorption : Defined as water or aqueous solution to be absorbed by the water absorbent polymer. Filler water : Defined as water or aqueous solution present in voids between grains of the granular wet water absorbent polymer. Void index : Defined as increase of weight due to water or aqueous solution filling all voids between grains of the granular wet water absorbent polymer over the weight of the water absorbent polymer contained in the granular wet water absorbent polymer, which is measured by the method to be mentioned later. Free water : Defined as extra water or aqueous solution further added to a mixture of the granular wet water absorbent polymer containing an amount of water or aqueous solution equivalent to the void index. Non-tackiness : Defined as a condition in which grains of the granular wet water absorbent polymer have a high flowability because the interaction of them is small. Non-tackiness degree is not determined by a simple factor because it depends on the integrated result of various actions produced between grains such as grain shape, surface condition of grains, degree of bond strength between grains, and static or dynamic frictional resistance between grains. Therefore, in the present invention, the non-tackiness degree is described by using a quantitative expression indicating the easiness of movement between grains. For convenience sake, however, the non-tackiness degree is expressed as the ratio of the volume of a certain amount of the granular wet water absorbent polymer, which has been subjected to the steps of adequately agitating to increase the voids between grains and to swell the grains and thereafter flowing the grains by vibration to return them to the condition before swelling, to the original volume of the granular wet water absorbent polymer. Thus, it is assumed that the non-tackiness degree increases as the above former volume comes closer to the latter original volume. It is assumed in particular that, when the grains are adequately agitated and swelled and then agitation is stopped, the grain returning to the same condition as before agitation has complete non-tackiness. Measurement is executed by the method to be mentioned later. However, the non-tackiness degree is not necessarily limited to the result of the measurement by this method. Permeability of the granular wet water absorbent polymer Defined as the degree of resistance of water or aqueous solution flowing through the voids between the grains of the granular wet water absorbent polymer, which is measured by the method to be mentioned later for convenience sake. Drainage rate : Defined as degree of difficulty for separation of filler water from an aqueous slurry of the granular wet water absorbent polymer, which is measured by the method to be mentioned later for convenience sake and shown by the ratio of the amount of the filler water separated after 24 hours to the void index. B. Measuring method 1. Preparation for aqueous slurry of granular wet water absorbent polymer 1-1. To make granular water absorbent polymer absorb water From granular water absorbent polymer which is water-free, an aqueous solution of granular wet water absorbent polymer is prepared according to the method below. The necessary amount of the granular water absorbent polymer (A) [Which is determined so that the volume of the granular wet water absorbent polymer ranges between 90 and 100 ml... the necessary amount of the granular water absorbent polymer is 1 g when the water absorption ranges between 90 and 100 times] is suspended in 200 g of water or aqueous solution and left as it is for 24 hours to obtain the aqueous slurry of the granular wet water absorbent polymer. 1-2. For aqueous slurry of granular wet water absorbent polymer The aqueous slurry of the granular wet water absorbent polymer is prepared according to the procedure below to obtain the granular wet water absorbent polymer by adding water to massive the water absorbent polymer and crushing it or by crushing the water absorbent polymer already absorbing water, or to directly obtain the aqueous slurry of the granular wet water absorbent polymer. The granular wet water absorbent polymer is obtained by separating water from the aqueous solution containing the granular wet water absorbent polymer through suction filtration. Then, a specimen of 90 to 100 ml is sampled from thus obtained the granular wet water absorbent polymer, the weight (A') of the specimen is measured, and the specimen is suspended in 200 g of water or aqueous solution and left as it is for 4 hours before obtaining the aqueous slurry of the granular wet water absorbent polymer. Moreover, a certain amount (T) of the granular wet water absorbent polymer is dried through freeze-drying or hot-air drying before measuring the weight (U) thereof. The weight (A) of water absorbent polymer contained in the granular wet water absorbent polymer is determined as A = A' x (U/T) 2. Measurement of water absorption and void index Then, the slurry is put in a 200 ml measuring cylinder having a length of 25 cm or more, a volume of approx. 250 ml, and a known weight (M) and equipped with a filter medium and a drain pipe with a cock for separating water through the filter medium at the bottom of the cylinder. (The measuring cylinder is effective to measure the permeability of the granular wet water absorbent polymer because the height of 1 mm is equivalent to the volume of 1 ml when the pipe diameter is 35.7 mm.) Free water is drained from the drain pipe. When the grains of the granular wet water absorbent polymer in the slurry appear on the water surface, drainage is stopped to measure the weight (B) of the entire measuring cylinder (measuring cylinder, granular wet water absorbent polymer, and filler water) and the volume (b) of the granular wet water absorbent polymer and filler water. It is necessary to strongly secure the filter medium at the bottom of the measuring cylinder so that it will not separate from the bottom for measurement of non-tackiness. Then, the drain pipe is connected to a pressure reducing device to drain filler water from the grains through suction. When drainage of the filler water is completed, the weight (C) of the entire measuring cylinder (measuring cylinder and granular wet water absorbent polymer) and the volume (c') of the granular wet water absorbent polymer are measured. After measurement is completed, the granular wet water absorbent polymer is left for 24 hours. Then, the volume (c) of the granular wet water absorbent polymer and the height (H) of it from the bottom of the measuring cylinder are measured to enter the top position of the granular wet water absorbent polymer on the surface of the measuring cylinder. (Because the volume of granular wet water absorbent polymer decreases depending on the type of granular water absorbent polymer, the volume is measured after 24 hours so as to wait for the decreased volume to recover.) Void index = (B - C) / A Water absorption = (C - M) / A 3. Measurement of non-tackiness After the water absorption is measured, the granular wet water absorbent polymer with the volume (c) is adequately agitated and grains are scattered by closing the opening at the top of the measuring cylinder and repeatedly turning the cylinder upside down. After the grains are adequately scattered by agitating the granular wet water absorbent polymer, the measuring cylinder is set to a vibrator and vertically vibrated to stabilize the grains of the granular wet water absorbent polymer. When the granular wet water absorbent polymer is adequately stabilized, the volume (d) of it is measured. Non-tackiness = d/c 4. Measurement of drainage rate Water or aqueous solution is added to the granular wet water absorbent polymer in the measuring cylinder whose non-tackiness has been measured and the granular wet water absorbent polymer is agitated again to prepare approx. 200 ml of the aqueous slurry of the granular wet water absorbent polymer. Then, a rubber tube is connected to the drain pipe at the bottom of the measuring cylinder and the cylinder is put in a water bath filled with water whose surface is 25 cm high from the bottom of the cylinder in order to produce a pressure difference of 25 cm in water column from the bottom of the cylinder. Then, the drain cock of the measuring cylinder is opened to start draining of water. When the grains of the granular wet water absorbent polymer appear on the water surface of the aqueous slurry, the cock of the cylinder is closed to measure the weight (D) of the entire measuring cylinder (measuring cylinder, granular wet water absorbent polymer, and filler water in all voids). Then, the cock of the drain pipe is opened to start draining. After 24 hours, the weight (E) of the entire measuring cylinder (measuring cylinder, granular wet water absorbent polymer, and remaining filler water) is measured. Then, the drain pipe is connected to the pressure reducing device and the filler water is removed from the granular wet water absorbent polymer by the same method as used for measuring water absorption, and the weight (F) of the entire measuring cylinder (measuring cylinder and granular wet water absorbent polymer) is measured. Drainage rate = (D - E) / (D - F) 5. Measurement of permeability of granular wet water absorbent polymer After measurement of the drainage characteristic, aqueous slurry is prepared by adding 100 g of water to the granular wet water absorbent polymer. Then, when the grains appear on the surface of the slurry of the granular wet water absorbent polymer after draining water from the bottom of the measuring cylinder according to the same procedure as that for measurement of drainage characteristic, the distance (H) between the surface of the slurry and the bottom of the measuring cylinder is measured and a filter paper is put on the granular wet water absorbent polymer. Then, water is slowly added to the polymer through the filter paper so that the water level is 25 cm from the bottom of the measuring cylinder. Then, a rubber tube is connected to the drain pipe at the bottom of the cylinder to put the cylinder in a water bath whose water level is 25 cm below the bottom of the cylinder so that a pressure difference equivalent to 25 cm in water column from the bottom of the cylinder is produced. Therefore, the pressure difference between the surface of the slurry and the water surface of the bath is 50 cm in water column. Then, water is drained by opening the drain cock of the measuring cylinder to measure the time (t) in which the distance between the water surface and the bottom of the cylinder decreases from 25 to 15 cm. After measurement, the granular wet water absorbent polymer is removed from the measuring cylinder and the time (t') in which the water level decreases from 25 to 15 cm is measured by using water instead of slurry and opening the cock of the drain pipe. Permeability of granular wet water absorbent polymer = (t - t') / H The first feature of the present invention lies in the fact that powdery artificial snow can easily be made by freezing granular wet water absorbent polymer. The granular wet water absorbent polymer used for the present invention, as described in the section of terminology, is the aggregate of grains of the wet water absorbent polymer in which each grain keeps its shape, voids are present between the grains, and no water is present in the voids between the grains though a small amount of water is present on the surface of each grain. That is, the granular wet water absorbent polymer of the present invention is granular after absorbing water; it is not restricted to a particular making method and process. For example, the granular wet water absorbent polymer of the present invention may include granular wet water absorbent polymer obtained by adding water to massive water absorbent polymer to make the water absorbent polymer absorb water and then crushing it, or granular wet water absorbent polymer consisting of small grains obtained by crushing granular wet water absorbent polymer consisting of large grains, or granular wet water absorbent polymer which already absorbs water during the water absorbent polymer making process, or granular wet water absorbent polymer obtained by cleaning granular wet water absorbent polymer collected from an artificial snow field with water to eliminate foreign matters and then separating water from the aqueous slurry of the granular wet water absorbent polymer. Preferably, the granular wet water absorbent polymer of the present invention is obtained by separating water from an aqueous slurry of the granular wet water absorbent polymer obtained by adding water or aqueous solution to dry granular water absorbent polymer to make it absorb water or aqueous solution. Though the grain shape is not limited, spherical-shaped or crushed-shaped grain is preferable. Particularly, the spherical-shaped grain is preferable because it provides powdery artificial snow. The crushed-shaped grain also provides powdery artificial snow if it has non-tackiness and has a small frictional resistance between the grains. The spherical-shaped grain is desirable because it provides powdery artificial snow whose grains can smoothly move even if the surface of the grains is slightly tacky. Spherical non-tacky granular wet water absorbent polymer is the most suitable one which very easily becomes powdery artificial snow by freezing it. Granular wet water absorbent polymer with a grain diameter of approx. 0.005 to 5 mm, particularly, 0.05 to 2 mm is preferable for the present invention and granular wet water absorbent polymer consisting of smaller grains is desirable because powdery artificial snow can more easily be obtained. However, granular wet water absorbent polymer consisting of too small grains is not desirable because it takes long time to separate water from the mixture of the granular wet water absorbent polymer and water, and the remaining amount of filler water increases. For granular wet water absorbent polymer consisting of large grains, water is easily separated from the mixture of the granular wet water absorbent polymer and water but artificial snow made by freezing the granular wet water absorbent polymer becomes granular or ice-slab like. Therefore, this granular wet water absorbent polymer is preferable for making an ice slab but it is not preferable for making powdery artificial snow. To make an ice slab and powdery artificial snow, it is desirable to use granular water absorbent polymer with a grain diameter of 0.5 to 2 mm. Granular wet water absorbent polymer with higher water absorption is preferable as long as it has a large strength and non-tackiness. In general, however, when the water absorption increases, the gel strength of granular wet water absorbent polymer decreases, voids between grains decrease, and tackiness between grains increases. Therefore, the preferable water absorption is 10 to 500 times, particularly, 30 to 200 times for water or aqueous solution. Spherical water absorbent polymer is preferable because voids between the grains increase, water is easily separated, and frictional resistance between grains decreases, and artificial snow obtained by freezing it easily becomes powdery. To keep the granular wet water absorbent polymer used for the present invention spherical and non-tacky after it absorbs water, it is necessary to increase the degree of crosslinking of the granular wet water absorbent polymer by polyepoxy or polyamine. However, water absorption decreases with excessive crosslinking. Therefore, it is necessary to control the amount of cross linking agent so that a proper water absorption is obtained. To easily control the water absorption of granular wet water absorbent polymer, there is a method to contact the water or aqueous solution to be absorbed in the granular wet water absorbent polymer with a small amount of alkali metal salt or alkaline earth metal salt such as sodium chloride or calcium chloride. As the contacting method, it is possible to add the salt to the water or aqueous solution used for absorption or to add a salt containing solution to the granular wet water absorbent polymer and thereafter separating the salt containing water. The effect of the present invention appears because it is characterized by using granular water absorbent polymer which is still granular even after absorbing water and has a strength capable of forming voids between the grains which are non-tacky and easily move. Therefore, tacky granular wet water absorbent polymer and/or granular wet water absorbent polymer which cannot hold the grain shape or produce voids between the grains because of an insufficient strength will not show the effect of the present invention. Any method can be used to make the water absorbent polymer absorb water. For example, it is enough to put the water absorbent polymer in agitated water and leave it for several minutes. The water absorbing rate of the water absorbent polymer depends on the water temperature. It decreases as the water temperature decreases and increases as the water temperature increases. For a water temperature of 10°C or lower, for example, it is possible to properly heat the water absorbent polymer before making it absorb water. However, to efficiently freeze the wet water absorbent polymer, it is desirable to make the wet water absorbent polymer absorb water at a low temperature. Granular wet water absorbent polymer can stably be kept without discharging water even if it is left as it is at room temperature. Therefore, the granular wet water absorbent polymer is not affected even if it is left as it is for a while (e.g. two months or more) until it is frozen to produce artificial snow. Because granular wet water absorbent polymer has hygroscopic property, it is desirable to store the granular wet water absorbent polymer in a closed container so that it is not moistened. The second feature of the present invention lies in the fact that the bottom part of granular wet water absorbent polymer, i.e. granular water absorbent polymer already having absorbed water or aqueous solution, forms an ice slab and the upper part of it forms artificial snow upon freezing it under the condition that the voids between the grains of the polymer are only partly filled with water. That is, the second feature is that artificial snow with an optionally setting of the ratio between ice slab and powdery artificial snow can easily be obtained by adjusting the amount of filler water present in the voids between the grains of the granular wet water absorbent polymer. The third feature of the present invention is a method for making an ice slab and artificial snow with the steps of separating water from an aqueous slurry of the granular wet water absorbent polymer which contains a sufficient amount of water or aqueous solution for filling all voids between the grains of the granular wet water absorbent polymer, and freezing the granular wet water absorbent polymer in a state in which a part of voids between the grains are not filled with water. That is, the third feature is that an aqueous slurry of the granular wet water absorbent polymer is made by adding water to the granular wet water absorbent polymer, which is a fluid slurry which can easily be transferred by a pump. Thereafter, because the voids between the grains of the granular wet water absorbent polymer have a high permeability, water is very easily separated from the slurry of the granular wet water absorbent polymer and a deposit layer of the granular wet water absorbent polymer is obtained by flooding the aqueous slurry of the granular wet water absorbent polymer onto slant or horizontal surfaces. After flooding the aqueous slurry made by adding water to the granular wet water absorbent polymer onto slant and horizontal surfaces of a natural skiing field or a natural skiing field provided with a cooling systems or an indoor artificial skiing field, water is separated from the slurry and a deposit layer of the granular wet water absorbent polymer is formed. When more time elapses, filler water between grains of the granular wet water absorbent polymer is also separated and voids are formed between the grains. Therefore, the amount of water present between the grains in the deposit layer before freezing can be adjusted by controlling the time from flooding and laying of the granular wet water absorbent polymer to the start of freezing it and thereby, the ratio between ice slab and artificial snow after freezing can freely be adjusted. In addition, it is possible to control the amount of water to be kept between the grains by mixing granular water absorbent polymers with different grain sizes even if the time from flooding and laying of the polymer to the start of freezing it is the same. Moreover, it is possible to control the amount of water to be kept between the grains by contacting the granular wet water absorbent polymer with a surface active agent. To contact the granular wet water absorbent polymer with the surface active agent, one may add the surface active agent to the water or aqueous solution to be absorbed or add the surface active agent to the granular wet water absorbent polymer. It is possible to use anionic, nonionic, and cationic surface active agents. However, it is preferable to use an nonionic surface active agent which hardly influences the granular wet water absorbent polymer. Particularly, an anionic surface active agent has an influence as a salt, which can also be used for adjustment of water absorption depending on the type of granular wet water absorbent polymer. The present invention can use a method for making an ice slab and artificial snow by laying up granular wet water absorbent polymer or granular water absorbent polymer containing filler water on an artificial snow slope before freezing it, or a method for separately freezing granular wet water absorbent polymer or granular wet water absorbent polymer containing filler water (and free water) and crushing the frozen granular wet water absorbent polymer to scatter or lay up on an artificial snow field when necessary. The most preferable mode of the present invention is a method for making an ice slab band artificial snow by transferring an aqueous slurry, made by adding filler water and free water to granular wet water absorbent polymer, to a skiing field by a pump to form a deposit layer and freezing the deposit layer of the granular wet water absorbent polymer after having removed the free water and part of the filler water separated from the deposit layer. Excessive free water for preparing the slurry of granular wet water absorbent polymer is not preferable because the viscosity of the slurry becomes too low and thus, the deposit layer of the granular wet water absorbent polymer flooded on an artificial snow skiing field becomes too thin. However, insufficient free water would produce a granular slurry, which impairs the operability. Therefore, it is necessary to properly select the suitable amount of water or aqueous solution to be mixed by considering the above points. The desirable amount of free water is 1 to 50% of the sum of absorption water and filler water, more preferably, 5 to 10% of it. When an surface active agent is added to the water to be added to water absorbent polymer, water is easily separated from the granular wet water absorbent polymer, the frictional resistance between grains decreases, non-tackiness is improved, and the artificial snow becomes powdery. Therefore, it is effective to use a surface active agent. To lay up the granular wet water absorbent polymer on an artificial snow skiing field, the following methods are the most convenient and effective ones : a method to pile up a layer of granular wet water absorbent polymer from the bottom to the top of a slope by a pump, a method to lay up the granular wet water absorbent polymer by flooding it from the top of the slope, and a method to scatter the grains of the granular wet water absorbent polymer on the slope by a spray having holes which the grains can pass through. However, if the granular wet water absorbent polymer contains no water or a small amount of water, a high-viscosity, granular, or clay-like slurry is obtained. In this case, a special pump or conveyer should be used. Therefore, these methods are not preferable as the depositing method when constructing a new field. However, they are preferable to lay up the granular wet water absorbent polymer on an existing artificial snow field because they avoid excessive drain (free water and filler water) to be separated, which otherwise may affect the existing artificial snow. It is possible to directly separate the free water and the filler water from the granular wet water absorbent polymer laid up on the foundation of an artificial snow skiing field or on natural or artificial snow. However, it is desirable to equalize the thickness of the laid up granular wet water absorbent polymer by using a rake or doctor-blade-type tool. It is a more preferable method to form grooves in the longitudinal and transverse directions or like a grid when or after equalizing the thickness of the granular wet water absorbent polymer. These grooves have the effect that water is easily separated and the frozen artificial snow becomes powdery. To separate water from the slurry of granular wet water absorbent polymer, it is a preferable method to drain water naturally or by means of suction from the bottom of side of the foundation of an artificial snow field through a permeable material such as wire gauze, paper, woven fabric, or non-woven fabric. However, it is possible to use another method, for example, a method to absorb water by a permeable material set at the bottom of the granular wet water absorbent polymer according to necessity. When flooding or spraying the slurry of granular wet water absorbent polymer on an artificial snow skiing field, the entire free water and most filler water contained in the granular wet water absorbent polymer pass through the voids at the bottom of and inside the granular wet water absorbent polymer and are drained through a drainage system installed on the foundation of the artificial snow slope, and the granular wet water absorbent polymer remains to form a deposit layer. Even if no drainage system is set to the artificial slope, free water and filler water pass through the voids between the grains of granular wet water absorbent polymer and are collected at the granular wet water absorbent polymer layer at the bottom part of the slope, and the deposit layer of the granular wet water absorbent polymer is formed on the slope. Therefore, it is enough to only set a drainage system at the bottom part of the slope. The thickness of the deposit layer increases when the viscosity of the slurry of granular wet water absorbent polymer increases, the speed of the water drained from the artificial snow field increases, and the grain of the granular wet water absorbent polymer is spherical and large. To drain water, no drainage system is necessary for a permeable foundation like when flooding granular wet water absorbent polymer on a slope of natural soil because water is absorbed in the soil. For the foundation made of a nonpermeable material like the foundation of an artificial snow slope, however, it is a preferable method to drain water from the holes formed at the bottom or side of the slope through a permeable material. Moreover, it is possible to use a method to flood the slurry of granular wet water absorbent polymer on a porous metallic plate, wire gauze, powder or grains of an organic or inorganic material, paper, textile product such as woven or non-woven fabric, or permeable material made of granular water absorbent polymer, which already has absorbed water or not and which has the same or different grain size, provided on the surface of the foundation of an artificial snow skiing field, and to transfer the filler water into the permeable material or make the material absorb the filler water; a method to drain water to the outside of the slope through the permeable material; and a method to form grooves or holes at places on the slope and drain water through the grooves or holes or collect water in the grooves or holes to drain the water directly or from the grooves or holes. However, the implementation of the present invention is not restricted to the above methods. To freeze granular wet water absorbent polymer in the present invention, it is possible to use a method to contact the granular wet water absorbent polymer with a solid maintaining a temperature of the freezing point or below, a method to contact the polymer with a gas having a temperature of the freezing point or below, and a method to mix the polymer with a sublimating solid such as solid carbon dioxide or a liquid with a low boiling point such as liquid carbon dioxide or liquid nitrogen. Particularly, a method to freeze granular wet water absorbent polymer by contacting it with a solid set at and/or near the bottom of the granular wet water absorbent polymer and directly or indirectly cooled by a fluid having a temperature of the freezing point or below is preferable because powdery artificial snow can be made. To contact granular wet water absorbent polymer with a solid maintaining a temperature of the freezing point or below, there are methods to set a pipe directly or indirectly cooled by a coolant such as a fluid having a temperature of the freezing point or below at the bottom of or inside the polymer and to freeze the polymer by setting a metallic plate directly or indirectly cooled by the above coolant under the polymer, or through ice alone or an ice slab consisting of ice and an organic or inorganic material. It is permitted that at least part of the solid maintaining a temperature of the freezing point or below is made of a permeable material. It is the most desirable method for freezing granular wet water absorbent polymer to freeze the granular wet water absorbent polymer by a plate directly or indirectly cooled by a fluid having a temperature of the freezing point or below set at the bottom part of the deposit layer of the polymer and/or a pipe directly or indirectly cooled by a fluid having a temperature of the freezing point or below set at or near the bottom part of the deposit layer from the bottom of the deposit layer. Though the detailed mechanism in which powdery artificial snow can easily be obtained by the present invention is unknown, the surface of the granular wet water absorbent polymer of the present invention is covered with a small amount of water and, when freezing starts, the water is first frozen and granular or small-projection-like ice is produced. Then, ice grows by using the produced granular or small-projection-like ice as a core to form projection-like ice and the apparent grain diameter increases by the value equivalent to the outside diameter of the projection. Because the grains of the granular wet water absorbent polymer of the present invention keep an independent shape and they easily move between each other, another grain contacting a frozen grain is pushed by the projection on the surface of the frozen grain and moved outside by the length of the projection. Thus, the void between the grains increases. This action progresses from the bottom to the top layer. Thus, it is estimated that an aggregate of high bulky ice grains (artificial snow of the present invention) is obtained. This phenomenon is estimated because an observation of the aggregate of high bulky ice grains shows that it has grains with a nucleus of water absorbent polymer, whose the diameter is smaller than that before the grain is frozen, at the center of it and ice grains present around it. Especially in case of a grain of the wet water absorbent polymer having a smaller diameter (e.g. that the diameter in a range from 0.1 to 1 mm after absorbing water or aqueous solution), the aggregate is a mixture of grains of the water absorbent polymer having a diameter as before absorbing water or aqueous solution, with ice grains existing around said grains, and further ice grains having no water absorbent polymer. Further, we suppose that the ice is made of water which is absorbed by the water absorbent polymer and the water absorbent polymer is not frozen. Accordingly, the wet water absorbent polymer functions like as carrier of water When rapidly freezing a single grain taken out of the deposit layer, the grain does not have the above structure but it becomes uniform ice. For the aggregate of a few grains, the grains are strongly bonded by ice. When the deposit layer of granular wet water absorbent polymer is rapidly frozen, the bottom layer is frozen and bulky artificial snow is produced. However, the thermal conductivity decreases and, resultingly, rapid freezing does not progress. Therefore, it is estimated that the above bulky artificial snow is obtained. For the present invention, freezing of granular wet water absorbent polymer without applying pressure from the top layer is one of the conditions necessary to make powdery artificial snow. Therefore, when freezing the surface of the deposit layer of granular wet water absorbent polymer by putting a slab or plate directly on the surface, the frozen artificial snow becomes harder in its upper layer due to the pressure of the object put on the surface though the bottom layer is powdery, and the surface may even become an ice plate according to circumstances. To obtain hard artificial snow, however, the above method is effective because the hard artificial snow is obtained by crushing and agitating the surface. Therefore, to obtain powdery artificial snow, it is desirable to use a method to freeze a layer of granular wet water absorbent polymer while contacting the surface of the layer with a gas having a temperature of -5°C or higher, more preferably, a gas having a temperature of the freezing point or higher. For the present invention, it takes time to produce powdery artificial snow because the thermal conductivity of the artificial snow decreases as freezing progresses. Therefore, it is a desirable method to additionally freeze the surface of the layer of granular wet water absorbent polymer by contacting the surface of it with a gas having a temperature of the freezing point of lower at a time when most grains of the polymer are already frozen; in this way artificial snow with an excellent slipping characteristic can be obtained. It is an economically desirable method to agitate and mix frozen artificial snow and unfrozen granular wet water absorbent polymer during freezing and continue freezing again or complete freezing by contacting the surface of the granular wet water absorbent polymer with a gas having a temperature of the freezing point or below. The desirable temperature of the solid used for cooling is -5°C or below, a particularly desirable temperature is -15°C or below. For granular wet water absorbent polymer consisting of large grains or slightly tacky grains, however, a higher temperature (e.g. -3 to -10°C) is preferable. Moreover, a thicker deposit layer is desirable because artificial snow becomes more powdery. However, it takes time to complete freezing. Therefore, it is desirable to use a means for improving the thermal conductivity of artificial snow by agitating frozen artificial snow and unfrozen granular wet water absorbent polymer during freezing as mentioned above. The preferable thickness of the deposit layer is 2 to 20 cm, more preferably, 5 to 10 cm. To contact granular wet water absorbent polymer with a gas having a temperature of the freezing point or below, the preferred method is to flow a gas having a temperature of the freezing temperature of low onto the deposit layer of the granular wet water absorbent polymer. In this case, it is possible to cover the surface of the deposit layer of the granular wet water absorbent polymer with a heat insulating slab. To mix granular wet water absorbent polymer with a sublimating solid such as carbon dioxide, liquid carbon dioxide, or liquid nitrogen, or liquid with a low boiling point, one may scatter the powdered solid carbon dioxide on the surface of the granular wet water absorbent polymer or mix part or the whole of the deposit layer of the granular wet water absorbent polymer with solid carbon dioxide, liquid carbon dioxide, or liquid nitrogen. In this case, it is also possible to use a method to mix them on an artificial snow slope and, at the same time, contact the granular wet water absorbent polymer with a solid maintaining a temperature of the freezing point or below at the inside or bottom of the polymer together with any of the above methods. Commercial liquid carbon dioxide can be used. The latent heat of vaporization of liquid carbon dioxide is 15.1 Kcal/kg at 30°C, 48.1 Kcal/kg at 10°C, and 56.1 Kcal/kg at 0°C. Therefore, liquid carbon dioxide can effectively be used for cooling and freezing. Liquid carbon dioxide is manufactured by compressing and cooling carbon dioxide under approx. 40 atm. The carbon dioxide producing source can use natural gas, off-gas produced by an ammonium plant, off-gas produced as the result of petroleum refining or ethylene decomposition, and extra or surplus gas produced by chemical and steel making plants. It is also possible to freeze granular wet water absorbent polymer by forming a deposit layer of the polymer in a mixing bath, or putting a preformed layer of the polymer in a mixing bath, and mixing it with solid carbon dioxide, liquid carbon dioxide, or liquid nitrogen in the mixing bath, or to freeze the polymer in a mixing bath equipped with a cooling system. The artificial snow made by the above method can be scattered or laid up on the foundation of an artificial snow skiing field or a skiing field where natural snow or artificial snow is already laid up. As a scattering method, scattering artificial snow from the ceiling onto the field is particularly preferable for an indoor artificial snow skiing field because an effective atmosphere as if it snows is shown. Therefore, scattering or laying up artificial snow on the existing skiing field is effective as a method to maintain an artificial snow skiing field or reuse the used granular wet water absorbent polymer by cleaning it with water to eliminate foreign matters before freezing it again as artificial snow. As the method to obtain the granular wet water absorbent polymer before freezing or granular wet water absorbent polymer containing filler water used for the present invention, it is an simple and effective method to separate water from the slurry of the granular wet water absorbent polymer, as in the above mentioned method. However, the method is not limited to the above one. It is also possible to use the following. (1) Method of mixing granular water absorbent polymer with an amount of water or aqueous solution equivalent to the water for absorption and the necessary filler water. (2) Method of adjusting the amount of filler water in the granular wet water absorbent polymer to be frozen to by flowing a slurry of the granular wet water absorbent polymer onto a permeable material. The slurry contains an amount of water or aqueous solution equivalent to a) the water for absorption, b) the necessary filler water and c) a further amount of water or aqueous solution to be absorbed by the permeable material which is equipped on an artificial snow slope. The slurry is flowed on the permeable material and left the slurry as it is whereby free water and unnecessary filler water is transferred into the permeable material. Because the granular wet water absorbent polymer used in the present invention is light-degradable and bio-degradable, there is no problem to discard the polymer after using it. However, to accelerate degradation by light and bio-degradation, it is possible to blend, add, impregnate, or coat a known accelerator, catalyst, or addition agent for light degradation and bio-degradation to or with the granular wet water absorbent polymer of the present invention. Because the granular wet water absorbent polymer of the present invention is safe for human bodies, it is preferable to select any added agent under safety considerations. It is also possible to color the granular wet water absorbent polymer of the present invention by a known method using a pigment or dye. If the artificial snow made of colored granular wet water absorbent polymer is colorful, it is possible to add a new commercial value to it. For example, it is possible to classify the beginners' field and experts' field by colors. This makes skiing more enjoyable. When giving fragrance to the-granular wet water absorbent polymer of the present invention by using a perfume or aromatic, another new commercial value can be added to the polymer. It is free to add, blend, coat, or impregnate an antioxidant, ultraviolet light absorber, fluorescent agent, nucleating agent, ice core forming bacteria, extender, substance having low friction factor, or other additive to or with the granular wet water absorbent polymer of the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENT The following is a description of the present invention with reference to embodiments. However, the present invention is not restricted to the embodiments. The density of the frozen artificial snow in the following embodiments and comparison examples is obtained according to the following operation. A sample of frozen artificial snow whose density and volume are already known is weighed and the weight of the sample is divided by the volume to obtain the density whose unit is g/cm³. When the artificial snow is soft, a sample of the artificial snow whose volume is already known can be obtained by inserting a thin stainless-steel case whose internal volume is already known into the artificial snow. When the artificial snow is hard, it is cut into a cube by a saw and the dimensions of it are measured by a rule to calculate the volume. [Example of synthesizing granular water absorbent polymer] 150 g of de-ionized water is set to a 500 ml flask having an agitator, reflux condenser, dropping funnel, thermometer, and nitrogen gas introduction tube and 0.2 g of partially-saponified polyvinyl alcohol (GH-23 made by Nippon Synthetic Chemical Industry Co., Ltd.,) is added to the water as dispersant to heat and melt the dispersant before nitrogen replacement is executed. Mean while, 22.5 g of laurylacrylate and tridecyl mixed ester (LTA made by Osaka Organic Chemical Industry Co., Ltd.), 10.0 g of hydroxyethyl methacrylate, and 17.5 g of methyl methacrylate are melted in an Erlenmeyer flask together with 1.0 g of azobisdimethylvaleronitrile and dropped into the above separable flask under nitrogen gas bubbling for one hour. Then the mixture is held for 5 hours at 65°C to end the reaction, cooled to filter solid matters, and cleaned before it is dried or vacuumed to obtain bead-like dispersant. 360.7 g of n-hexane and 4.32 g of the above dispersant are set to a 100 ml separable flask having an agitator, reflux condenser, dropping funnel, thermometer, and nitrogen gas introduction tube, heated up to 50°C, and dispersed and melted before nitrogen replacement is executed. Meanwhile, 72.0 g of acrylic acid is partially neutralized by 32.2 g of sodium hydroxide dissolved in 103.6 g of ion exchange water in an Erlenmeyer flask and 0.24 g of potassium persulfate is further dissolved in the solution at the room temperature. This monomer aqueous solution is dropped into the above separable flask under nitrogen gas bubbling for one hour at the agitating speed of 300 rpm. After refluxing for 2 hours, 0.1 g of 30% aqueous hydrogen peroxide is added to the solution and refluxing is further continued for one hour to complete polymerization. Then, 0.73 g of ethylene glycol diglycine ether is added to the solution and removing water by azeotropic distillation is executed to filter the solution before it is dried or vacuumed to obtain bead-like granular water absorbent polymer. [Embodiment 1] The above bead-like water absorbent polymer (BL-100 made by Osaka Organic Chemical Industry Co., Ltd.) consists of grains with the average diameter of 100µm and shows satisfactory flowability. The water absorption of the water absorbent polymer to city water at room temperature is 71 times, the void index of the granular wet water absorbent polymer after absorbing water is 25 times, the non-tackiness of it is 103%, the drainage rate of it is 0.85, and the permeability of it is 5 min/cm. [Embodiment 2] : Artificial snow making example 1 The aqueous slurry of granular wet water absorbent polymer is prepared by mixing and agitating 1 weight part of the bead-like water absorbent polymer in Embodiment 1 and 80 weight parts of water. By flooding the aqueous slurry of the granular wet water absorbent polymer on the slope (inclination of approx. 10°) of the foundation of an artificial snow skiing field where a soft plastic cooling pipe with the inside diameter of approx. 5 mm capable of circulating coolant of -20°C is installed, a deposit layer of the granular wet water absorbent polymer with the thickness of approx. 5 cm is formed. When measuring the amount of filler water of the deposit layer approx. 3 hours after the layer is formed, it is found that approx. 3% of the filler water remains. By freezing the granular wet water absorbent polymer in approx. 12 hours after starting circulation of the coolant while contacting the polymer with a gas having a temperature of -2°C approx. 3 hours after the granular wet water absorbent polymer is deposited, an ice slab with the thickness of approx. 2 cm and powdery artificial snow with the thickness of approx. 15 cm are obtained. The density of the powdery artificial snow is 0.23 g/cm³. Photograph No.1 is a microscopic photograph showing the crystalline structure of the artificial snow, which is an aggregate of crystals of ice having a length of approx. 0.5 mm, which are a mixture of ice grains including grains of the water absorbent polymer (having a length of approx. 0.09 mm) and ice grains not including grains of the water absorbent polymer. Photograph No.2 is a microscopic photograph showing a condition wherein the crystalline structure of the artificial snow shown in photograph No.1 is melted, wherein the water absorbent polymer absorbs water from the melting ice, and unabsorbed water exists between the grains of the wet water absorbent polymer. As the result of treading the artificial snow, satisfactory sliding characteristic is obtained. [Embodiment 3] : Artificial snow making example 2 The slurry of the granular wet water absorbent polymer used for Embodiment 2 is flown onto the surface of the artificial snow slope used for Embodiment 2 to form a deposit layer with the thickness of approx. 5 cm. In this case, freezing is started while part of filler water remains in the layer of approx. 2.5 cm from the bottom by restricting drainage of separated water. Freezing is completed after approx. 5 hr and an ice slab with the thickness of approx. 3 cm and hard artificial snow with the thickness of approx. 5 cm are obtained. The surface of the obtained artificial snow can easily be crushed and powdery artificial snow is obtained. [Embodiment 4] : Artificial snow making example 3 Granular wet water absorbent polymer is frozen by the same method as in Embodiment 2 except, the fact that a nonionic surface active agent (hydro-extracting agent (trade name: DRYWELL) made by Fuji Photo Film Co., Ltd.) is added to city water to be absorbed in granular water absorbent polymer. At a time when a part of the water absorbent polymer up to approx. 2cm from the surface is not yet frozen, frozen artificial snow is mixed and agitated with the unfrozen granular wet water absorbent polymer and then freezing is completed. As a result, the drainage speed of separated water slightly increases and hard artificial snow with satisfactory sliding characteristic is obtained. [Embodiment 5] : Artificial snow making example 4 By adding powdery or solid carbon dioxide to the granular wet water absorbent polymer made by suction-filtering the slurry of the granular wet water absorbent polymer to eliminate most filler water and freezing the polymer, powdery artificial snow is obtained. [Embodiment 6] : Artificial snow making example 5 Slurry is prepared by adding the amount of city water A mixture of water and the granular wet water absorbent polymer is obtained by melting the ice slab and artificial snow made by freezing the granular wet water absorbent polymer in Embodiment 2. A slurry is prepared by adding an equal amount of city water to the mixture. Then, the slurry is filtered to change it to a slurry containing approx. 80 times of water. This is then frozen by the same method as in Embodiment 2. As a result an ice slab and artificial snow same as those in Embodiment 2 are obtained. [Embodiment 7] : Artificial snow making example 6 A slurry of granular wet water absorbent polymer is prepared by mixing and agitating 1 weight part of the bead-like water absorbent polymer in Embodiment 1 with 80 weight parts of 0.1% calcium chloride solution. In this case, the water absorption is 40 times. Then, after flowing the slurry of the granular wet water absorbent polymer on the slope (inclination of approx. 20°) of the foundation of an artificial snow skiing field where a soft plastic cooling pipe with the inside diameter of approx. 5 mm capable of circulating coolant having a temperature of -20°C is installed, a deposit layer of the granular wet water absorbent polymer with a thickness of approx. 5 cm is formed. By freezing the deposit layer of the granular wet water absorbent polymer in approx. 12 hours, starting the circulation of the coolant approx. 3 hours after the granular wet water absorbent polymer is deposited, an ice slab with the thickness of approx. 2 cm and powdery artificial snow with the thickness of approx. 10 cm are obtained. [Advantage of the Invention] The present invention provides a method to simultaneously make an ice slab serving as the foundation of an artificial snow skiing field and artificial snow whose upper layer is powdery to hard; this is obtained freezing a mixture of granular water absorbent polymer and a certain amount of water or flooding the mixture of fluid wet water absorbent polymer and water on a horizontal or slant floor before freezing it. The method for making an ice slab and artificial snow of the present invention has the advantages that the aqueous mixture of granular wet water absorbent polymer and water can easily be transferred by a pump because the aqueous mixture is a fluid slurry, and the rate between the frozen ice slab and upper artificial snow can be adjusted by controlling the amount of water present in voids between the grains of the granular wet water absorbent polymer. Moreover, the method of the present invention makes it possible to easily obtain a deposit layer of granular wet water absorbent polymer in which water is separated from the slurry of the polymer by flooding the aqueous slurry made by adding water to the granular wet water absorbent polymer on the slope of a natural skiing field, or slant and horizontal surfaces of a natural skiing field or indoor skiing field equipped with a cooling system. Therefore, it is possible to easily make an ice slab and artificial snow by freezing this deposit layer. Also, the product according to the present invention has light-degrading and/or bio-degrading characteristics and may provide a colored and/or fragrant recoverable and reusable ice slab and artificial snow.

Claims: A method of making an ice slab and a layer of artificial snow on top of the ice slab, comprising the steps of forming a layer of granular wet water absorbent polymer, the layer comprising a granular water absorbent polymer which is capable of absorbing water while maintaining its granular shape, water absorbed in the grains of the polymer, and an additional amount of water so that the voids between the grains of the polymer are filled with water in a lower part of the layer and not filled with water in the upper part of the layer, and freezing said layer of granular wet water absorbing polymer. A method according to claim 1, comprising the steps of forming said layer of granular wet water absorbent polymer from an aqueous slurry of granular wet water absorbent polymer containing an amount of water or aqueous solution at least sufficient for filling all voids between the grains of the granular wet water absorbent polymer, and separating water from the slurry until a part of the voids between the grains are not filled with water. A method according to claim 1 or 2, wherein the granular wet water absorbent polymer comprises at least one of polymer and/or copolymer selected from the group consisting of acrylamide, acrylic acid, salt of polyacrylic acid, vinyloxazolidine, salt of methacrylic acid, styrene, vinyl ether and styrene sulfonate. A method according to claim 1 or 2, wherein the granular wet water absorbent polymer has spherical-shaped or crushed-shaped grains. A method according to claim 1 or 2, wherein the granular wet water absorbent polymer has non-tackiness between the granular grains. A method according to claim 1 or 2, wherein the granular wet water absorbent polymer has an average grain diameter of 0.005 to 5 mm. A method according to claim 2, wherein water is separated from the aqueous slurry of the granular wet water absorbent polymer naturally or by means of suction. A method according to claim 2, wherein water is separated from the aqueous slurry of the granular wet water absorbent polymer naturally of by means of suction by contacting the aqueous slurry of the granular wet water absorbent polymer with a permeable material. A method according to claim 8, wherein the permeable material is made of textile, granular organic matter, porous metallic plate, and/or wire gauze. A method according to claim 1 or 2, wherein the granular wet water absorbent polymer is frozen by contacting it with a solid maintaining a temperature of the freezing point or below. A method according to claim 10, wherein the solid maintaining a temperature of the freezing point or below comprises a plastic pipe, metallic pipe, plastic plate, metallic plate, ice, ice-containing material, and/or permeable material and is directly or indirectly cooled by a fluid having a temperature at the freezing point or below. A method according to claim 10, wherein the solid maintaining a temperature at the freezing point or below is arranged in or under the granular wet water absorbent polymer. A method according to claim 10, wherein the surface of the granular wet water absorbent polymer contacts a gas having a temperature of -5°C or higher. A method according to claim 1 or 2, wherein the granular wet water absorbent polymer, having its surface contacted with the gas having a temperature of -5°C or higher, is frozen by contacting it with a solid maintaining a temperature at the freezing point, and, when at least part of the granular wet water absorbent polymer is frozen, the surface of the granular wet water absorbent polymer in this state or after mixing unfrozen parts of the polymer with the frozen parts, is frozen by contacting it with a gas having a temperature at the freezing point or below. A method according to claim 1 or 2, wherein the surface of the granular wet water absorbent polymer is frozen by contacting it with a gas having a temperature at the freezing point or below. A method according to claim 1 or 2, wherein the granular wet water absorbent polymer is frozen by contacting it with solid carbon dioxide, liquid carbon dioxide, and/or liquid nitrogen. A method according to claim 1 or 2, wherein part or the whole of the frozen granular wet water absorbent polymer is crushed. A method according to claim 17, wherein the crushed frozen granular wet water absorbent polymer is scattered. A method according to claim 1 or 2, wherein the granular wet water absorbent polymer is is contacted with alkali metal salt and/or alkaline earth metal salt. A method according to claim 1 or 2, wherein the granular wet water absorbent polymer is is contacted with at least one surface active agent.

Inventors: HIRANO KAZUO, KAMBAYASHI TAIJI, KUBOTA KOHEI, NAGAI TOSHITAKE, NAGATA KOITI, SUGIYAMA YASUMASA, TANAKA HARUHIKO, HIRANO, KAZUO, KAMBAYASHI, TAIJI, KUBOTA, KOHEI, NAGAI, TOSHITAKE, NAGATA, KOITI, SUGIYAMA, YASUMASA, TANAKA, HARUHIKO
Applicants: MIURA DOLPHINS KK, OHTSUKA MASAHISA, OSAKA ORGANIC CHEM IND, SANYO ELECTRIC CO, TONEN CORP, TONEN SEKIYUKAGAKU KK, MIURA DOLPHINS CO., LTD., OHTSUKA, MASAHISA, OSAKA ORGANIC CHEMICAL INDUSTRY CO., LTD., SANYO ELECTRIC CO., LTD., TONEN CHEMICAL CORPORATION, TONEN CORPORATION
Application year: 1992
Main classification: C09K3
IPC codes: C09K3, C08L33, C08F220, F25C3