Abrasive articles incorporating abrasive elements comprising abrasive particles partially embedded in a metal binder

Abstract: To avoid pull-out of abrasive particles from a binder, the abrasive article of the invention has abrasive elements dispersed in a binder matrix, the abrasive elements having individual particles of abrasive material, all of which are partially embedded in a metal binder. The abrasive particles, when introduced into an electrolyte bath only during the final stages of an electrodeposition process, are embedded only on a major surface of the metal binder.

Description: This invention relates to abrasive articles comprising a thermoplastic or thermoset binder which binds abrasive elements to a backing. The abrasive elements comprise abrasive particles partially embedded into a major surface of a metal binder. It is commonplace in both domestic and industrial applications to abrade the surface of a workpiece to achieve a desired finish. Conventional abrading operations are performed by the rapid rotation or reciprocation of abrading tools of various configurations, such as wheels, discs, belts and the like, against the surface to be finished. These tools include at least one abrasive surface comprising particles of an abrasive material embedded in a binder matrix which presents a multiplicity of tiny cutting edges to the workpiece. During the abrading operation, individual abrasive particles are occasionally removed from the surface of the abrasive tool as a result of drag forces produced by contact between the tool and workpiece, which loosen and ultimately unseat the particles. This is referred to as "pull-out" or "shelling", the effects of which can vary from a simple reduction in cutting efficiency to uneven wear and the spoiling of the finish of the workpiece. For example, loose abrasive particles can mark the surface of the workpiece, necessitating further finishing operations to restore the desired finish. Pull-out is most pronounced with coarse grain abrasives, especially when abrading hard materials, as larger particles are more susceptible to abstractive forces. Consequently, pull-out is a particular problem in the stoneworking industry where abrasive tools are used to shape and finish stone, such as marble, granite and the like. The present invention seeks to provide abrasive articles having a reduced susceptibility to pull-out. U.S. Pat. No. 4,256,467 (Gorsuch et al.) describes flexible abrasive articles and methods for their production. In one method, a stainless steel or other electrically conductive metal cylinder is coated with a resist material except at discrete areas. The cylinder is then wrapped in an electrically insulating mesh material, the cylinder and mesh emersed in an electrolytic bath, and metal deposited electrolytically from the bath over areas of the cylinder not having been coated with resist. The metal is deposited through the mesh material, and abrasive particles are added to the bath toward the end of the deposition time period, thereby providing areas of metal deposits having abrasive particles partially embedded therein. U.S Pat. No. 5,127,197 (Bruxvoort et al.) describes similar articles, wherein the metal deposits are adhered to a backing using a metallic adhesive. Also of background interest are U.S. Pat. Nos. 2,820,746; 2,492,143; 3,860,400; 4,047,902; 4,078,906; 4,111,667; 4,214,877; 4,288,233; 4,576,612, 4,798,026; 4,826,508; 4,863,573; 4,874,478; and 5,011,511, World Patent Application WO 90/00105 (published January 11, 1990); UK Patent Applications 2 200 920 A (published August 17, 1988) and 2 164 053 A (published March 12, 1986); and British Patent Specifications 760,526 (published October 31, 1956); 1 247 764 (published September 29, 1971); and 1 458 236 (published December 8, 1976). The background art discloses variations of and improvements to the Gorsuch et al. technology previously discussed; however, they do not disclose abrasive elements such as formed by Gorsuch et al. dispersed in a non-metallic binder in an abrasive article. GB-A-1534448 discloses an abrasive product comprising, a conductive backing sheet member with a surface thereon to which are attached non-ferromagnetic abrasive particles, a masking means overlying the conductive backing sheet member and providing exposed spaced apart portions on the backing sheet member, a plurality of the abrasive grit particles positioned on each of the exposed portions, and a metal plating deposit on the conductive backing sheet member at said exposed portions for holding said abrasive particles in position, said metal deposit having been applied by an electrolytic, electroless, or vacuum deposition plating technique, the grit particles and the metal plating having been applied to the product substantially simultaneously in a substantially static plating technique. World Patent Application WO 79/00778 (published October 18, 1979) discusses U.S. Pat. No. 2,216,728, which discloses abrasive aggregates comprised of diamond abrasive particles held together by sintering in the presence of metals such as nickel having an embrittling additive therein. The aggregates are said to be useful in resin bonded grinding wheels wherein the aggregates are surrounded by a resin phase. The provision of a patterned abrasive surface to enhance grinding results is known in the art, as disclosed in the above-mentioned U.S. Pat. No. 2,820,746 and World Patent Application WO 90/00105, and more recently with the introduction of "structured" or "patterned" abrasives made using rotogravure methods, such as those disclosed in U.S. Pat. Nos. 4,773,920 (Chasman et al.) and 5,014,468 (Ravipati et al), and assignee's copending United States Application serial number 07/651,660, filed February 6, 1991. The above-mentioned U.S. Pat. No. 2,216,728 describes metal-bonded diamond aggregate abrasives surrounded by a resin binder, the addition of embrittling additives (such as tin) to copper is apparently used to control the "slow but necessary breakdown of the metal bonded aggregate during use." This effectively increases, rather than decreases, pull-out of the abrasive particles, an objective diametrically opposed to that of the present invention. According to the present invention there is provided an abrasive article comprising a plurality of elements dispersed in a resin binder matrix, each of the elements consisting of particles of abrasive material which are partially embedded in a metal binder. By use of the phrase "partially embedded in a metal binder" it is meant that substantially all of the abrasive particles are deposited onto a surface of the metal binder, but not completely surrounded by metal binder, although a small percentage of abrasive particles may indeed be totally surrounded by metal binder. By use of the phrase "dispersed in a resin binder matrix" is meant that substantially all of the abrasive elements are surrounded by binder matrix, where "binder matrix" comprises an organic (e.g., thermoplastic, thermoset, or mixture thereof) resin, with the understanding that as abrasion begins, the abrasive elements are gradually exposed to the workpiece. The abrasive elements are preferably formed by electrodeposition of the metal in the presence of the abrasive particles. The abrasive articles of the invention may be molded or formed in any of a wide variety of sizes, shapes and configurations, including wheels, discs, plain and tapered cups, sheets, pads, blocks, belts etc., and can be used to abrade a wide range of materials including metal, stone (such as marble and granite), glass and other materials which are normally difficult to abrade. The abrasive articles of the invention find particular utility with coarse abrasive materials and are suitable for use under both wet and dry abrading conditions. The term "element" is used herein to describe a discrete structure formed by a plurality of abrasive particles bound together by a metal binder. The surface area of each element is greatly increased relative to the individual abrasive particles making up the element. The binder matrix is able to penetrate into the gaps and interstices formed between adjacent abrasive particles, effectively increasing the purchase (holding force) of the binder matrix on the element and rendering it less susceptible to abstractive forces. The elements may take a wide variety of sizes and shapes including both regular and irregularly shaped elements. The elements are ordinarily preformed and introduced into the uncured binder matrix. One method of making the abrasive elements includes the steps of: (a) applying a nonconductive coating partially over a conductive surface to provide exposed separated conductive areas; (b) depositing metal from a deposition solution of metal ions onto the surface to provide a plurality of separated metal bodies upon which will be deposited additional metal and abrasive particles; (c) introducing abrasive particles into the deposition solution while continuing to deposit metal in an amount sufficient to anchor a plurality of abrasive particles to each metal body without entirely covering the abrasive particles; and (d) removing the abrasive elements from the surface. Preferred are those methods wherein the nonconductive coating is an insulating solder resist material, and those methods wherein after step (a) but prior to step (b) the exposed separated conductive areas are coated with a release material, such as wax. Another method of making the elements comprises the steps of: (a) applying a mesh material over a conductive surface, the mesh material having discrete nonconductive and conductive areas; (b) placing the wrapped conductive surface of step (a) in a solution having metal ions therein capable of being electroplated or electroless plated; (c) depositing metal ions onto and through the nonconductive areas of the mesh; (d) introducing abrasive particles into the solution toward the end of the deposition period to form areas of deposited metal having abrasive particles partially embedded therein; (e) removing the conductive surface of step (d) from the solution and subsequently removing the mesh material therefrom; and (f) exposing the mesh material of step (e) to conditions sufficient to dissolve the mesh, thereby forming individual abrasive elements. Preferred are those methods wherein the mesh is a thermoplastic material dissolvable by acids, bases, and/or organic solvents. Particularly preferred are those methods wherein the thermoplastic material is polyester cloth and the exposure conditions include exposing the polyester cloth to an aqueous basic solution having a concentration and for a time sufficient to dissolve the polyester. The electrodeposition steps of the methods of making the abrasive elements can be any suitable electrodeposition technique known in the art, including those disclosed in Belgian Patent No. 622162, German Patent No. 1059754 and British Patent Nos. 1375571 and 1458236. Preferred electrodeposition techniques are disclosed in U.S. Pat. No. 4,256,467, described hereinafter with reference to FIGs. 2b to 2d. The abrasive elements are incorporated into abrasive articles. Methods include dispersing abrasive elements in a binder precursor, the abrasive elements having individual particles of abrasive material, all of which are partially embedded in a metal binder, the abrasive elements being formed as above described, and exposing the binder precursor to conditions sufficient to cure the binder precursor. Binder materials used as the binder matrix may comprise any resin binder useful in making abrasive products. The binder used to form the abrasive element may comprise any metal capable of being electrodeposited. Preferred metals include copper, silver and especially nickel. Combinations of metals produced by successive electrodeposition of two or more different metals may also be employed. The abrasive material may comprise any material useful in making abrasive products including alumina (Al 2 0 3 ) and diamond, although non-conductive materials are preferred for use with the electrodeposition techniques employed in the present invention. Diamond is the preferred abrasive material, as well as coated diamonds. Further aspects and advantages of the invention will now be described by way of example and with reference to the accompanying drawings. FIG. 1 is a cross-sectional view of a hemispherical abrasive element for use in the present invention; FIG. 2a is a cross-sectional view of a mesh material onto which have been formed a plurality of the abrasive elements of FIG. 1; FIG. 2b is a perspective view of a cylinder on which the abrasive elements of FIG. 1 can be made; FIG. 2c is a cross-sectional view illustrating, on an exaggerated scale, another embodiment of abrasive element formed on the cylinder of FIG. 2b; FIG. 2d is a view similar to Figure 2c of yet another embodiment of abrasive element; FIG. 3 is a plan view of an abrasive disc in accordance with the invention; FIG. 4 is a cross-sectional view of the abrasive disc of FIG. 3; FIG. 5 is a side elevation view of the abrasive disc of FIG. 3; and FIG. 6 is a graph comparing the abrading efficiency of an abrasive disc in accordance with the invention with a conventional abrasive disc. FIG. 1 is a cross-sectional illustration of a single abrasive element (denoted generally by 1). Abrasive element 1 comprises particles 3 of an abrasive material partially embedded in a metal binder 5. Abrasive particles 3 project outwardly from binder 5 to provide a multiplicity of cutting edges. The binder matrix of the abrasive surface is able to penetrate the gaps and interstices formed between adjacent abrasive particles in the element, thereby increasing the holding capacity of the binder matrix on the elements when compared with individual abrasive particles. Typically only from 30% to 50% of the individual abrasive particle is embedded in the metal binder. In the embodiment illustrated in FIG. 1, abrasive element 1 is substantially hemispherical, but any useful size, shape and configuration of element may be employed. As "pull-out" is more prevalent with coarse abrasives, the present invention finds particular utility in the preparation of such materials, generally where the average size of the abrasive particles is 250 micrometers. The size of the abrasive elements will vary somewhat with the grade of abrasive desired, but hemispherical elements having an average diameter ranging from 0.5 to 3 mm are usually adequate for most purposes. More preferably the elements have an average diameter ranging from 0.5 to 2 mm. Generally, each element contains at least five abrasive particles, preferably from 10 to 20 particles. The amount of abrasive material incorporated into each element will vary with the grade of abrasive desired and the intended application of the abrasive article, but generally, each element comprises from 0.5 to 10%, preferably 0.5 to 5% by weight of the abrasive material. The abrasive elements may be formed using any appropriate electrodeposition technique. In a method described in U.S. Pat. No. 4,863,573, the abrasive elements are formed by laying a length of mesh material onto an electrically conducting surface and electrodepositing a metal onto the mesh material in the presence of an abrasive mineral such that the mineral becomes partially embedded in the metal. An insulating material (sometimes referred to in the art as a "resist") is selectively applied to the mesh material before deposition of the metal such that the metal can only deposit onto the mesh in those areas not covered by the insulating material, thereby defining the shape and size of the abrasive elements. FIG. 2a illustrates this method of making an electrodeposited abrasive layer. A mesh material 4 in the form of a woven fabric of electrically insulating material, such as polyamide, cotton, polyesters such as copolymers of terephthalic acid and ethylene glycol (such as that known under the trade designation "Terylene") or the like, is screen printed with insulating material in the form of ink. The ink, may be a resin based or oil based ink. The screen printing may be conducted by conventional screen printing techniques in such a manner to ensure that the ink penetrates into and is absorbed onto defined areas of the mesh material leaving discrete areas without any insulating material which define the abrasive element. Such discrete areas may be of any convenient shape and size, e.g., circular, diamond-shaped, rectangular etc. The mesh material is laid onto an electrically conductive, preferably smooth, surface and metal 5 electrodeposited directly onto the surface through the mesh material so that mesh material 4 becomes embedded in and adhered to the metal layer. Abrasive particles 3 are added to the electrolytic bath toward the end of the deposition period. Mesh 4 and associated metal layer 5 with embedded abrasive particles 3 is readily stripped from the electrically conductive surface. While it is possible to form the abrasive elements directly onto the electroconductive surface without using the mesh material by applying an electrically insulating material over selected areas of the surface so that the metal layer is deposited only over the remaining uncoated areas, the removal of the particles is more difficult and can damage the surface. A particularly preferred electrodeposition technique will now be described with reference to FIGs. 2b to 2d. The electrodeposition technique is known in the art and disclosed in U.S. Pat. No. 4,256,467, previously incorporated by reference. Referring to FIG. 2b, a cylinder 7 formed of stainless steel or other electrically conductive metal having a smooth cylindrical surface 9 is coated with an electrically insulating acid resist at areas denoted as 10 except for discrete, spaced, in this case circular, areas 11. The surfaces of these areas 11 are treated with a relaese material in known manner to prevent the adhesion of electro-plated metal. Typical release materials include the automobile wax known under the trade designation "Minute Wax", available from Turtle Wax Manufacturing Ltd., England. A length of flexible mesh (not shown) is then stretched tightly around cylinder 7 which is then immersed in an electrolyte bath (again not shown) of known form containing a metal electrolyte of any metal capable of being electro-plated or electroless plated, preferably nickel or copper. In one method, described with reference to FIG. 2c, metal 13 is deposited electrolytically onto and through mesh 15 onto cylinder 7 so that mesh 15 becomes embedded in the metal 13. A thickness of metal 13 is deposited until almost the full eventual, desired thickness is reached. Abrasive particles 3, in the form of diamond, cubic boron nitride, silicon carbide or other suitable abrasive material, are then introduced into the electrolyte bath in suspension whereupon such material becomes randomly deposited on the metal 13. Deposition of metal 13 then continues until abrasive particles 3 are partially embedded in the outer layer of metal 13. The cylinder, now having a covering of mesh, metal and abrasive particles, is then removed from the bath and rinsed before stripping the mesh material. In another method, described with reference to Figure 2d, the same cylinder 7 is immersed in the electrolyte solution and deposition of metal over the exposed surfaces 11 of the cylinder 7 is commenced. Abrasive particles 3 present in the electrolyte solution simultaneously settle onto the exposed surfaces 11 so that during deposition abrasive particles 3 become embedded in a thin layer 17 of metal. When sufficient abrasive particles 3 have been embedded in the initial metal layer 17, cylinder 7 is removed from the solution and washed and dried. A length of mesh 15 is wound tightly around cylinder 7 having its layer 17 of metal and abrasive particles 3 in place. Cylinder 7 is replaced in the electrolyte solution and electroplating is recommenced, this time laying down a second layer 19 of metal, onto and through mesh 15 and onto the previously-formed layer 17 to form an integral layer 21. On completion of the second layer 19 of metal, i.e., when it has reached its desired thickness, cylinder 7 is removed and rinsed and the mesh 15 stripped from the cylinder. In the latter case, the operative points of the abrasive particles 3 are on one surface of the material 18 and all lie on substantially the same plane, flush with the surface in contact with the smooth surface(s) of cylinder 7. As the abrasive particles are not as exposed as in the method described with reference to FIG. 2c, the method and abrasive element of FIG. 2d are not as preferred. In the deposition methods described herein the electrolytic bath typically consists essentially of water and the metal ion(s) to be deposited. In embodiments wherein nickel is deposited, the bath will preferably contain from 30 to 50 weight percent nickel sulfamate, more preferably from 35 to 45 weight percent nickel sulfamate. An important aspect of the invention for all embodiments is that the abrasive elements so formed on the mesh material may have the mesh material 15 dissolved therefrom by immersing (or spraying followed by immersing) the abrasive element-laden mesh material with a solvent, an acid, a base, or a combination thereof. As used herein, "acid" is defined as an aqueous composition having negative base ten logarithm of the hydrogen ion concentration of less than 7.0, while "base" is defined as an aqueous composition having negative base ten logarithm of the hydrogen ion concentration of greater than 7.0. Of course, it will be appreciated by those skilled in the art that acids, bases, and solvents which might have an adverse effect on the metal and/or abrasive particles are to be avoided, those having an adverse effect being easily found with minimum experimentation. Acids which may be used for dissolving the mesh include hydrochloric acid, sulfuric acid, nitric acid, combinations thereof, and the like, while suitable basic materials include sodium hydroxide, potassium hydroxide, and the like. Suitable organic solvents include lower aliphatic and cyclic hydrocarbon solvents such as hexane, heptane, cyclohexane, and the like. One particularly preferred method of mesh dissolution, used when the mesh material is polyester, is to soak the abrasive element-laden mesh in a 40% by weight aqueous sodium hydroxide (NaOH) solution. FIGs. 3-5 illustrate one embodiment of an abrasive article in accordance with the invention namely, an abrasive disc (denoted generally by 23) for use with a rotary sander (not shown). The abrasive disc 23 generally comprises a backing layer 25 having on one side thereof an abrasive layer 27 comprising a binder matrix 29 into which is dispersed the abrasive elements 1 (see FIG. 4). Aside from the presence of the abrasive elements, the disc is entirely conventional. Examples of such discs are commercially available from Interface Developments Ltd., under the trade name "Flexible Resin Diamond Disc." The abrasive layer 27 is formed with a plurality of interconnecting annular 31 and radial 33 channels or grooves which facilitate the removal of abraded material and coolant from the work surface and allow the disc 23 a degree of flexure. These grooves are formed by the mold cavity used to produce the abrasive article. Typically and preferably the channels have a depth of 0.25 to 0.5 times the thickness of the disc, while the width of the channels can vary considerably but are preferably from 1 mm to 1 cm. It should be understood that the channels may or may not be utilized in every case, and that the width, depth, and other design details are largely a function of the particular job to be performed. The rear, non-coated side 35 of the backing layer 25 may optionally be provided with means (not shown) to secure disc 23 to the back-up pad of the sander, e.g., the backing layer may be provided with one portion of a conventional hook and loop type fastener, or with a pressure-sensitive adhesive. As previously noted, binder materials used as the binder matrix may comprise any resin binder useful in making abrasive products, including both natural and especially synthetic resins. Particularly preferred resins include well known cross-linked resins, such as acrylic resins, epoxy resins, phenolic resins, phenolaldehyde resins, melamine-aldehyde resins and urea-aldehyde resins, although the choice of resin will depend to a large extent on the intended use of the abrasive article. Preferred resins are epoxy resins, including epoxy novolacs. Other useful resin systems include thermostable resins, such as polybenzmidazoles, e.g., as disclosed in US Patent No. 3,329,489; polyimides, e.g., as disclosed in US Patents Nos. 3,295,940 and 3,385,684; polysulfides, e.g., as disclosed in US Patent No. 3,303,170, and polypyrrones. For use in making coated abrasive products, such as discs or belts, liquid resin systems are usually preferred. Preferred resin binders are phenolic and epoxy binders. Examples of suitable epoxy binders include those commercially available from Ciba Geigy under the trade designations "AV 119", "AV 129/HV 935B" and "AV 129/HV 997." An example of a suitable phenolic binder is that known under the trade designation "XDF 4252", commercially available from Dynochem. The binder matrix of the abrasive articles of the invention may also include one or more additives known in the art including fillers, lubricants, anti-loading agents, thickeners, anti-static agents, defoamers, wetting agents, and pigments, such as talc, titanium dioxide and carbon black. Although the abrasive articles of the invention are most typically used under wet abrading conditions, additives such as metal flakes, carbon black and graphite are particularly useful for dry abrading as they confer antistatic properties to the abrasive articles. The abrasive material may comprise any material useful in making abrasive products including alumina (Al 2 0 3 ), alumina zirconia, aluminum boride, beryllium carbide, beryllium oxide, boron nitride, boron phosphide, ceramic aluminum, diamond, emerald, flint, garnet, hematite, hafnium carbide, magnesium oxide, molybdenum carbide, niobium carbide, pumice, quartz, ruby, silica sand, silicon, silicon boride, silicon carbide, silicon nitride, tantalum boride, titanium boride, titanium carbide, tungsten carbide, vanadium boride, vanadium carbide, vermiculite and zirconium carbide, although non-conductive materials are preferred for use with the electrodeposition techniques employed in the present invention. Diamond is the preferred abrasive material. Coated diamonds, e.g., as disclosed in Belgian Pat. Nos. 683508 and 698428 and French Pat. Nos. 1142688 and 1522735 are also useful. Suitable coating materials include both metals, such as copper, nickel, silver, cobalt and molybdenum, and non-metals. The abrasive particles will preferably have an average particle size ranging from 100 to 300 micrometers. A particularly preferred average particle size is 250 micrometers. The discs are conveniently produced by dispersing abrasive elements into an uncured binder precursor, pouring the resulting mixture into a suitable mold and allowing the mixture to cure. The morphology and abrasive content of the abrasive element will vary depending on the intended use of the abrasive disc but, by way of example, a disc suitable for sanding granite has been obtained by incorporating abrasive elements of the type described previously having the following specification: Shape : hemispherical Size : 1 mm (largest dimension) Abrasive material : diamond (uncoated) Total Abrasive content: 2% (w/w) Avg. abrasive content per element : 21.65% (w/w) Avg. Size of abrasive particles : 250 micrometers Average no. of particles per element : 10 to 20 Binder : nickel The present invention will now be described with reference to the accompanying Examples, wherein all parts and percentages are by weight unless otherwise specified. Examples Example 1: Method of Making Abrasive Elements Abrasive elements useful in the invention and described hereinabove with reference to FIG. 2c were made by the following method. A stainless steel cylinder, 40 cm diameter, was patterned with a series of 1 mm circular non-coated areas using an insulating solder resist known under the trade designation "XZ15T", available from Coates Circuit Products, Ltd. The circular non-coated areas were then coated with an automobile wax known under the trade designation "Minute Wax." The partially coated cylinder was wrapped tightly with a woven polyester cloth positioned fully emersed in an electrolyte bath which had 40 weight percent nickel sulfamate dissolved in water. The woven polyester cloth was that known under the trade designation "PES 55/27", available from Sericol. The cylinder was electrically connected as the cathode to a 12 volt power source and the power supplied to the system. After 75 minutes of only metal deposition, diamond abrasive particles having 250 micrometer avg. particle size were introduced into the bath. After a further 190 minutes of abrasive particle/metal deposition (to a total thickness of 1 mm), the power was turned off and the cylinder removed from the bath and rinsed with tap water. The cylinder then appeared as illustrated in FIG. 2c. The woven polyester cloth was then peeled from the cylinder. A 40 weight percent aqueous solution of NaOH was then prepared and used to dissolve the woven polyester cloth. The cloth as peeled from the cylinder was simply soaked in the NaOH solution at room temperature until the polyester material was fully dissolved, yielding abrasive elements consisting of nickel binder and diamond abrasive particles partially embedded in the surface of the nickel. Example 2 and Comparative Example A: Comparative Abrasion Testing This Example serves to illustrate the advantages of abrasive discs prepared in accordance with the invention, using the abrasive elements prepared in Example 1. The following comparative test was conducted using two 10 cm abrasive discs of the type illustrated in FIGs. 3-5, identical in all respects save the disc (hereinafter "Abrasive Disc Comparative Example A") contained 2% by weight of 250 micrometer diamond grit and the other (hereinafter "Abrasive Disc Example 2") 2% by weight of the same diamond grit but partially embedded in nickel pellets as described in Example 1 and with reference to FIG. 2c. Each disc was mounted onto a hand-operated rotary angle grinder known under the trade designation "Flex 1103" running at 3600 rpm and used to flat sand 15 cm square blocks of black granite known under the trade designation "NERO IMPALA" (also known as "BON ACCORD"), available from most stone suppliers, for a period of 10 minutes. Water was used as the coolant for both sanding operations. A hand pressure of 2.5 psi (176 g/cm 2 ) was used, and the stock removed (in grams) was recorded at 1 minute intervals, as measured by subtracting the weight of the sample after grinding from that before grinding. The grinding results obtained are shown in FIG. 6 of the accompanying drawings. After 10 minutes grinding time, Abrasive Disc Example 2 had removed a total of 426 g whereas the Abrasive Disc Comparative Example A had removed only 52 g, clearly illustrating the increased abrading efficiency of discs prepared in accordance with the invention.

Claims: An abrasive article comprising a plurality of elements dispersed in a resin binder matrix, each of the elements consisting of particles of abrasive material which are partially embedded in a metal binder. An abrasive article as claimed in Claim 1 further characterized by the abrasive material being selected from alumina, alumina zirconia, aluminum boride, beryllium carbide, beryllium oxide, boron nitride, boron phosphide, ceramic aluminum, diamond, emerald, flint, garnet, hematite, hafnium carbide, magnesium oxide, molybdenum carbide, niobium carbide, pumice, quartz, ruby, silica sand, silicon, silicon boride, silicon carbide, silicon nitride, tantalum boride, titanium boride, titanium carbide, tungsten carbide, vanadium boride, vanadium carbide, vermiculite and zirconium carbide, and a combination thereof. An abrasive article as claimed in Claim 1 or Claim 2 further characterized in that the abrasive particles have an average particle size ranging from 100 to 300 micrometers. An abrasive article as claimed in any preceding Claim further characterized in that the metal is selected from copper, nickel, silver, and a combination thereof. An abrasive article as claimed in any preceding Claim further characterized in that the binder matrix comprises a resin binder selected from the group consisting of acrylic, epoxy, melamine- aldehyde, phenolic, phenol-aldehyde, and urea-aldehyde resin, and a combination thereof. An abrasive article as claimed in any preceding Claim further characterized in that the abrasive particles are from 0.5 to 10% by weight of the abrasive element. An abrasive article as claimed in any preceding Claim further characterized by each element having on average at least 5 abrasive particles. An abrasive article as claimed in any preceding Claim further characterized by the elements being hemispherical and having an average diameter ranging from 0.5 to 3 mm. An abrasive article as claimed in any preceding Claim characterized in that the elements were formed by electrodeposition of the metal in the presence of the abrasive particles. An abrasive article as claimed in any preceding Claim attached to a backing layer. An abrasive article as claimed in any preceding Claim in the form of a wheel, disc, cup, block, sheet, pad or belt.

Inventors: GORSUCH IAN, LAWSON TIMOTHY, GORSUCH, IAN, LAWSON, TIMOTHY, Gorsuch, Ian, c/o Minnesota Mining Man. Co., Lawson, Timothy, c/o Minnesota Mining Man. Co.
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1992
Main classification: B24D18
IPC codes: B24D18, B24D3, C09K3