Organic molybdenum complexes

Abstract: Novel molybdenum complexes prepared by reacting (a) a fatty oil or acid, (b) 2-(2-aminoethyl)aminoethanol and (c) a molybdenum source are described. The molybdenum complexes impart antifriction, antioxidant, and antiwear properties to lubricating compositions and decrease fuel consumption in internal combustion engines using same.

Description: BACKGROUND OF THE INVENTION The present invention concerns novel organic molybdenum complexes and their use as multifunctional additives for lubricating compositions. Many attempts to reduce fuel consumption in engines have been of mechanical nature. Another approach to the problem is the use of lubricants that reduce the internal friction in the engine, thus resulting in a reduction in the engine's energy requirements. Friction is of particular significance in internal combustion engines, because the loss of substantial amount of theoretical mileage is traceable directly to friction. Friction will increase the power required to effect movement, thus increasing fuel consumption. Therefore, it is advantageous to use lubricants which minimize this friction. Since various antifriction additives act in a different physical or chemical manner, only some satisfy the effectiveness and compatibility criteria leading to a significant energy loss prevention function of the lubricant. Therefore, it is desirable that the additive possess other functional properties, in particular antiwear and antioxidant functionality. Molybdenum compounds known to be useful in engine lubricants include certain molybdenum complexes of fatty alkyl amines with a sulfur donor taught in US-A-4,164,473 and molybdenum complexes of fatty oil and diethanol amine disclosed in US-A-4,889,647. It has been now discovered that a novel class of organomolybdenum complexes imparts antifriction, antioxidant and antiwear properties to lubricants resulting in increased energy efficiency. SUMMARY OF THE INVENTION In accordance with the present invention, there are provided organic molybdenum complexes prepared by reacting (a) a fatty derivative of 2-(2-aminoethyl)aminoethanol and (b) a molybdenum source sufficient to yield 0.1 to 20 percent of molybdenum based on the weight of the complex. Another object of the invention concerns lubricating compositions comprising a major portion of a lubricating oil and a friction reducing amount of said molybdenum complex. DETAILED DESCRIPTION OF THE INVENTION The molybdenum complexes of the invention are reaction products of a fatty derivative of 2-(2-aminoethyl)aminoethanol and a molybdenum source. A specific chemical structure cannot be assigned to the product. It is believed that the major components may have the structural formulae wherein R represents a fatty residue. The fatty residue may be derived from fatty oils or fatty acids. The fatty oils are glyceryl esters of higher fatty acids. Such esters are commonly known as vegetable and animal oils. Vegetable oils particularly useful are oils derived from coconut, corn, cottonseed, linseed, peanut, soybean and sunflower seed. Similarly, animal fatty oils such as tallow may be used. The fatty acids may be saturated or unsaturated. Particularly useful are lauric, palmitic, stearic, oleic, linoleic and linolenic acids. Preferred are fatty residues containing at least 12 carbon atoms and may contain 22 carbon atoms and higher. The source of molybdenum is an oxygen-containing molybdenum compound capable of reacting with the fatty derivative of 2-(2-aminoethyl)aminoethanol to form an ester-type molybdenum complex. The sources of molybdenum include, among others, ammonium molybdates, molybdenum oxides and mixtures thereof. The fatty derivatives of 2-(2-aminoethyl)aminoethanol may be prepared by hydrolysis of fatty derivatives of 1-(2-hydroxyethyl)-2-imidazoline which are available commercially. The formed amine-amide intermediate is then reacted with a molybdenum source. Alternatively, the fatty derivatives may be prepared by reacting about 1.0 to 2.5, preferably 1.0 to 2.0 moles of 2-(2-aminoethyl)aminoethanol per mole of fatty oil. If excess fatty oil is used, part of the monoglyceride formed may react with the molybdenum source to form a molybdenum complex and the remainder will act as a diluent for the product. The entire mixture may be incorporated into the lubricating composition. If fatty acid is used, the preferred mole ratio of fatty acid to the amine is 1:1. The molybdenum source is added in a sufficient quantity to yield 0.1 to 20, preferably 6.0 to 8.5, optimally about 8 percent of molybdenum per total product. The molybdenum complexes are prepared by a condensation reaction. The reaction is conducted at elevated temperatures to accelerate said reaction and remove water of reaction. Temperatures or about 70° C to 160° C are used depending upon the particular reactants. The amount of the molybdenum complex in the lubricating composition may range from 0.01 to 10 percent and preferably, from 0.1 to 1.0 percent. An amount of 0.01 percent of the molybdenum complex is the minimum effective amount for imparting friction reducing properties to lubricating compositions. The lubricating compositions contemplated herein include lubricating oils containing a major amount of base oil. The base oil may be selected from oils derived from petroleum hydrocarbon and synthetic sources. The hydrocarbon base oil may be selected form naphthenic, aromatic and paraffinic mineral oils. The synthetic oils may be selected from, among others, alkylene polymers, polysiloxanes, carboxylic acid esters and polyglycol ethers. The lubricating compositions may contain the necessary ingredients to prepare the composition, as for example, dispersing agents, emulsifiers and viscosity improvers. Depending on the intended use of the lubricant, other functional additives may be added to enhance a particular property of the lubricant. The lubricating compositions may further contain known antioxidants, extreme pressure agents, metal passivators, rust inhibitors and other antiwear and antifriction agents. The following examples are given for the purpose of further illustrating the invention. All percentages and parts are based on weight unless otherwise indicated. EXAMPLE 1 A reactor was charged with 1-(2-hydroxyethyl)-2-(tall oil alkyl)-2-imidazoline, 150g, water, 30g, and molybdenum trioxide, 32g. The reaction was heated to 130°C while distilling water. Vacuum was applied and the reaction was heated at 130 to 140°C for 2 hours. Oil diluent, 50g, was added and the liquid was filtered. The molybdenum content of the product was 9.72 percent. EXAMPLE 2 Friction Test The molybdenum complex of Example 1 was tested for friction reducing properties by a modified Falex ring and block test procedure. This test is believed to simulate the Five Car Fleet Test on laboratory scale. The Falex machine was stabilized by a break-in run with a base oil (Sunvis R 21 manufactured by Sun Oil Company) for 1 hour at 150° C under a load of 4.54 kg and for 5 minutes at 114° C, followed by heating at 150° C. After the break-in period, 100 ml base oil was added and the friction was measured as pound friction force at one minute intervals for 15 minutes at 108° C, 800 rpm and load of 2.27 kg. After draining the base oil and cleaning, the same ring and block was used for testing the sample. The values of pound friction force were converted to coefficient of friction which is defined as a ratio of friction force to applied force and compiled in Table I herein. The results indicate that the molybdenum complex of the invention substantially reduces the coefficient of friction of engine oils. Falex Friction Test Sample Ingredient, Percent 1 2 3 Base Oil 100 99.5 99.0 Molybdenum Complex - 0.5 1.0 Cooeficient of Friction 0.0944 0.0918 0.0867 EXAMPLE 3 Modified Falex Wear Test A laboratory test was conducted by using the original Falex machine to simulate the valve train wear of an automobile engine. The V-blocks and pin were washed in mineral spirits with an ultrasonic cleaner, rinsed with acetone, air-dried and weighed. The test sample (60 g) was placed into the oil cup. The motor was switched on and the loading arm was placed on the ratchet wheel. Upon reaching the reference load of 227 kg, the ratchet wheel was disengaged and the load was maintained constant for 3.5 hours. Thereafter, the motor was switched off. The V-blocks and pin were washed, dried and weighed. The weight loss, a measure of wear, was recorded and compiled in Table II. The test samples were prepared by adding the compound of Example 1 to the base Motor oil SAF 30, SF (containing 0.11 percent phosphorus and no supplemental antioxidant) in the amount given in Table II. The results indicate that the present compound affords good antiwear properties. Modified Falex Wear Test Sample Active Ingredient Percent Total Weight Loss, mg. 4 None --- 73.2 5 Compound of Example 1 0.5 25.6 6 Compound of Example 1 1.0 10.6 EXAMPLE 3 Thin Film Oxygen Uptake Test The test was conducted essentially according to the method described by Chia-Soon Ku et al, J. Am. Soc. Lubricating Eng., 40, 2 75-83, 1984. The oxidation induction time of the lubricant was measured under conditions which simulate the high temperature oxidation processes in automotive engines by a modified rotary bomb oxidation test method ASTM D-2272. The test was conducted with 1.5 gram samples of SAE 30, SF motor oil. The oil was fully formulated (containing 0.11 percent phosphorus and no supplemental antioxidant). The compound of Example 1 was added to the oil in the amount indicated in Table III. The test was conducted at 160° C, and initial oxygen pressure of 620.6 kPa (90 psi). A "pass" oil has a high induction time, while a "fail" oil has a low time. The additive of the invention has good antioxidant properties as indicated by the data compiled in Table III. Thin Film Oxygen Uptake Test Sample Active Ingredient Percent Average Induction Time, Min. 7 None --- 107.5 8 Compound of Example 1 1.0 130.0 The above embodiments have shown various aspects of the present invention. Other variations will be evident to those skilled in the art and such modifications are intended to be within the scope of the invention as defined by the appended claims.

Claims: An organic molybdenum complex preparable by reacting (a) about 1.0 mole of fatty oil having 12 or more carbon atoms, (b) 1.0 to 2.5 moles 2-(2-aminoethyl)aminoethanol and (c) an oxygen-containing molybdenum compound, capable of reacting with the fatty derivative of 2-(2-aminoethyl)-aminoethonol to form an ester type molybdenum complex, sufficient to yield 0.1 to 20.0 percent of molybdenum based on the weight of the complex, the reaction being carried out at 70 to 160° C. The organic molybdenum complex according to claim 1 wherein the fatty oil is coconut oil and the molybdenum content is 7.0 to 8.5 percent based on the weight of the complex. An organic molybdenum complex preparable by (a) hydrolyzing 1-(2-hydroxyethyl)-2-imidazoline substituted by a fatty residue derived from fatty oil or acid and having 12 or more carbon atoms, to form an amine-amide intermediate and (b) reacting with an oxygen-containing molybdenum compound, capable of reacting with the fatty derivative of 2-(2-aminoethyl)-aminoethonol to form an ester type molybdenum complex, sufficient to yield 0.1 to 20.0 percent of molybdenum based on the weight of the complex, the reaction being carried out at 70 to 160° C. The organic molybdenum complex according to claim 3 wherein the fatty residue is derived from tall oil. A lubricating composition comprising a major amount of a lubricating oil and 0.01 to 10.0 percent of an organic molybdenum complex prepared by (a) hydrolyzing 1-(2-hydroxyethyl)-2-imidazoline substituted by a fatty residue derived from fatty oil or acid and having 12 or more carbon atoms, to form an amine-amide intermediate and (b) reacting with an oxygen-containing molybdenum compound, capable of reacting with the fatty derivative of 2-(2-aminoethyl)-aminoethonol to form an ester type molybdenum complex, sufficient to yield 0.1 to 20.0 percent molybdenum based on the weight of the complex, the reaction being carried out at 70 to 160° C. A lubricating composition comprising a major amount of a lubricating oil and 0.01 to 10.0 percent of an organic molybdenum complex prepared by reacting (a) about 1.0 mole of fatty oil having 12 or more carbon atoms, (b) 1.0 to 2.5 moles 2-(2-aminoethyl)aminoethanol and (c) an oxygen-containing molybdenum compound, capable of reacting with the fatty derivative of 2-(2-aminoethyl)-aminoethonol to form an ester type molybdenum complex, sufficient to yield, 0.1 to 20.0 percent of molybdenum based on the weight of the complex, the reaction being carried out at 70 to 160°C. A method of reducing fuel consumption in an internal combustion engine which comprises lubricating said engine with a lubricating composition comprising a major amount of a lubricating oil and 0.01 to 10.0 percent of an organic molybdenum complex prepared by (a) hydrolyzing 1- (2-hydroxyethyl) -2-imidazoline substituted by a fatty residue derived from fatty oil or acid and having 12 or more carbon atoms to form an amineamide intermediate and (b) reacting with an oxygen-containing molybdenum compound, capable of reacting with the fatty derivative of 2-(2-aminoethyl)-aminoethonol to form an ester type molybdenum complex, sufficient to yield 0.1 to 20.0 percent molybdenum based on the weight of the complex, the reaction being carried out at 70 to 160° C. A method of reducing fuel consumption in an internal combustion engine which comprises lubricating said engine with a lubricating composition comprising a major amount of a lubricating oil and 0.01 to 10.0 percent of an organic molybdenum complex prepared by reacting (a) about 1.0 mole of fatty oil having 12 or more carbon atoms, (b) 1.0 to 2.5 moles 2- (2-aminoethyl) aminoethanol and (c) an oxygen-containing molybdenum compound, capable of reacting with the fatty derivative of 2-(2-aminoethyl)-aminoethonol to form an ester type molybdenum complex, sufficient to yield 0.1 to 20.0 percent of molybdenum based on the weight of the complex, the reaction being carried out at 70 to 160°C.

Inventors: KAROL THOMAS J, KAROL, THOMAS J.
Applicants: VANDERBILT CO R T, R.T. VANDERBILT COMPANY, INC.
Application year: 1992
Main classification: C10M159
IPC codes: C10N10, C07F11, C10M139, C10N40, C10M159, C10M133, C07C31, C10N30