A METHOD FOR PREPARING ENTERIC-COATED ORAL DRUGS CONTAINING ACID-UNSTABLE COMPOUNDS

Abstract: The present invention relates to a method for preparing enteric-coated oral drugs containing acid-unstable compound, in particular an enteric-coated oral drug prepared in the form of acid-stable dosage units as inclusion complex formed by reacting benzimidazole derivative, acid-unstable compound, with cyclodextrin in alkaline solution.

Description: A METHOD FOR PREPARING ENTERIC-COATED ORAL DRUGS CONTAINING ACID-UNSTABLE COMPOUNDS BACKGROUND OF THE INVENTION The present invention relates to a method for preparing enteric-coated oral drugs containing acid-unstable compounds, in particular an enteric -coated oral drug prepared in the form of acid-stable dosage units as inclusion complex formed by reacting benzimidazole derivative, acid-unstable compound, with cyclodextrin in alkaline solution. Acid-unstable compounds, especially the benzimidazole compounds, are easily discolored and degraded under acidic and neutral conditions. For example, omeprazole, a benzimidazole derivative, has half-life of 10 minutes in medium of below pH 4, but 18 hours at pH 6.8 and about 300 days at pH 11. Omeprazole has been reported to be stable in alkaline condition [Pilbrant A and Cederberg C. Scand. J. Gastroenterology, Suppl. 108, 113-120(1985)]. The acid-unstable compounds when exposed to the environment also get discolored and degraded by getting in contact with moisture and organic solvents. Therapeutic use of the acid-unstable compounds which inhibit gastric acid secretion and are used to cure peptic ulcer and/or duodenal ulcer, requires apprepriate mechanism to protect these compounds from degradation in gastric juice after oral administration. Methods for stabilizing the acid-unstable compound, in particular omeprazole has been known to be as follows ; Omeprazole is combined with alkaline salt such as Na + , K + , Mg +2 , Ca +2 and so on to maintain the stability for compound itself. PCT Publication No. 86-00913(PCT/EP 85/00371) discloses to form a stable complex by mixing and reacting omeprazole with β -cyclodextrin in 96% ethanol and cooling the reactant. The latter process seems to have the problem as the reaction is conducted at a temperature 25 ~ 38t_ for 15 hours in ethanol, during the reaction itself omeprazole can get discolored and degraded. Furthermore, it is difficult to expect the formation of inclusion compound because both omeprazole and cyclodextrin are dispersed in the reaction as solid particles, not dissolved. For forming an inclusion compound of cyclodextrin, the reaction must be carried out in presence of water molecules [K. Hara, H. Hashimoto, J. Jpn. Soc. Starch. Sci., 32(2) 152-161(1986)]. Therefore, the latter method not expected to give inclusion compound since the above reacting condition has not been considered- On the other hand, Unexamined Korean Patent No. 87-9718 and Korean Patent Publication No. 91-4579 disclose processes for preparing omeprazole preparation consisting of mixing omeprazole with alkaline substance to form core material, forming a watersoluble internal layer on the core and forming an enteric coating to stabilize omeprazole. It has, however, been found that the stabilizing methods known in the Korean Patents have several problems as followings ; The process for preparing core material and forming enteric-coating is very complicated. The stabilized omeprazole is discolored and degraded during stay in stomach after oral administration, because gastric juice passes through the enteric-coating to partially dissolve the watersoluble internal layer and then infiltrated into the core to dissolve the alkaline substance partially destroying the enteric-coating. The stability of omeprazole by this process is not secured concretely- For formulating omeprazole, it is necessary to give good attention to omeprazole itself. For example, it must be kept at below -20 . of low temperature and immediately used for formulating after removing moisture, or immediately after synthesis, to maintain the starting stability. After all, for stabilizing the acid-unstable compound a primary factor is not only to secure the stability of preperation but also to stabilize the compound itself. Thus the attempt to stabilize acid-unstable compound must take into account the stability of the compound during the stablization process, its stability against gastric juice and the need to quickly and completely dissolve are made the available main drug for absorption in the intestine. As discussed above most of the previously described methods are either very partialy successful in stabilization or the stable inclusion compound is not produced at all conjugation attempt to add alkaline salt to omeprazole have also been unsatisfactory. SUMMARY OF THE INVENTION The object of the present invention is to obtain oral drugs of acid-unstable compound, having excellent storage stability, dissolution and absorption properties after oral administration and a simplified manufacturing process principally involving formation of inclusion complex by reacting the acid-unstable compound with cyclodextrin to give stabilized compound. The present invention is a method for preparing enteric-coated oral drugs by using cyclodextrin to stabilize acid-unstable compound, characterized in which acid- unstable compound is reacted with cyclodextrin of 1 ~ 10 mole based on lmole of acid-unstable compound in an alkaline solution to obtain inclusion complex without existance of alkaline substance. DETAILED DESCRIPTION OF THE INVENTION The present invention is accomplished by using a new solution system, instead of organic solvent such as ethanol used in prior art, in which acid-unstable compound is reacted with cyclodextrin for stabilizing. The alkaline solution used in the present invention performs a different function from alkaline solvent in prior art. As a result the inclusion complex obtained by the present invention dose not include the alkaline components. According to the present invention when acid-unstable compound is reacted with cyclodextrin in alkaline solution, the reaction is carried out under homogeneous solution system for 1 ~ 30 mins at 40 ~ 701. , and after cooling to room temperature the reacted solution is allowed to stand at 4 . to deposit inclusion complex. The reactant is filtered to remove residual alkaline component and to obtain pured stable inclusion complex as the desired product. In the above reaction, if the temperature is below 40 . , since the solubility of cyclodextrin is decreased and an excessive of alkaline solution is needed, the reation scale becomes unnecessarily large and the yield is decreased, and if the reaction temperature is more than 70"C, acid-unstable compound may be discolored or degraded. Furthermore, under the condition if the reaction time is below 1 min, acid- unstable compound and cyclodextrin not are entirely dissolved in the alkaline solution, and if the reaction time over 30 mins, acid-unstable compound is also discolored and degraded. In the present invention, benzimidazole derivative having the following structural formula(I) and pharmaceutically acceptable salt thereof, especially omeprazole and its sodium salt, is preferably used as acid-unstable compound. Wherein, R x is selected from the group consisting of hydrogen atom, methoxy, trifluoromethyl and tetrafluoroethoxy group ; R^ is selected from the group consisting of hydrogen atom, methylamine and dimethylamine group ; R 3 is selected from the group consisting of hydrogen atom, methoxy, aryloxy and propaziloxy grou ; and R 4 is hydrogen atom or methyl group. A pharmaceutical preparation containing said acid-unstable compounds in pharmaceutically effective amount may be prepared by the present invention in form of dosage units for oral administration such as tablets, granules, capsules, spherical pellets, microgranules, or microcapsules. According to the present invention, acid-unstable compound is reacted with cyclodextrin structurally having hydrophobic cavity of a defined size, and at this time an inclusion complex is obtained because of the property of cyclodextrin to protect hydrophobic compounds from outside by entrapping them into the cavity. Cyclodextrin may be prepared by resolving starch with cyclodextrin glycosyltransferase and are classified according to the properties and size shown as following Table A. In accordance with the present invention, a cyclodextrin(CD) selected from the group consisting of or -, β - and γ -cyclodextrin, and cyclodextrin derivatives such as methyl- β -cyclodextrin, hydroxyethyl β -cyclodextrin, hydroxypropyl ~ -cyclodextrin, hydroxypropyl β -cyclodextrin, hydroxypropyl γ -cyclodextrin, etc. may be used. Table A. Comparison of Properties for Natural Cyclodextrins * (Note) Ring-opening half-life was measured under the condition of 60"C ,1N HCl. In the present invention, to obtain stable inclusion complex powder, the used alkaline solution is a aqueous solution of one selected from the group consisting of hydroxides of alkaline metal, alkaline salts of organic or inorganic acid, amines, buffers and combinations thereof. The alkaline compounds in the present invention as alkaline aqueous solution may be typically illustrated as followings : Hydroxide of alkaline metal may be selected from the group consisting of sodium hydroxide, potassium hydroxide, calcium hydroxide, barium hydroxide and combinations thereof. Alkaline salt may be selected from the group consisting of sodium borate, sodium carbonate, sodium phosphate, potassium borate, potassium carbonate, potassium phosphate, sodium acetate, sodium citrate and combinations thereof. Amines may be selected from the group consisting of diethylamine, triethylamine, butylamine, ethylenediamine, triethanolamine, propylamine, dipropylamine, diethanolamine, monoethanolamine, isobutylamine, diisopropylamine, tert-butylamine, dibutylamine, diisobutylamine, tributylamine, pentylamine, dipentylamine and combinations thereof. Buffer solution may be selected from the group consisting of carbonate buffer, phosphate buffer, borate buffer, amine salt buffer and combinations thereof. When the aqueous solution of hydroxide of alkaline metal, alkaline salt of organic or inorganic acid, or buffer solution are used as alkaline solution, the lower pH of alkaline solution affects the acid-unstable compound which may be discolored or degraded during stabilizing reaction. Also, the higher pH of the reaction solution requires longer water-washing time to obtain neutral inclusion complex of acid-unstable compound included in cyclodextrin and the yield is decreased due to partialy washing out the inclusion complex during the water-washing. Therefore, alkaline solution may be preferably used between pH 8.0 and 12.0. In the case of independently using amine in alkaline solution, an amine water solution of 0.01 — 0.5M may be preferably used to form inclusion complex under stable condition and to reduce after-treatment time. On the other hand, the above cyclodextrin in the present invention is preferably used in a ratio of 1 ~ 10 mole based on 1 mole of acid-unstable compound. If the used amount of cyclodextrin is below 1.0 mole, unincluded acid-unstable compound is remain in excess of quantity, and if over 10 mole, the amount of acid-unstable compound in the obtained inclusion complex is decreased by existance of unre acted cyclodextrins. In accordance with the present invention the clear solution obtained by the above reaction is cooled to low temperature(4'_. ) and maintained for 3 - 15 hours at that temperature to afford the desired inclusion complex formation as microcrystalline powder. The cooling of reaction mixture to give inclusion complex must be very carefully observed to see how the crystalline deposit is formed. If the treating time is below 3hours, inclusion complex is not sufficiently deposited, and if over 15 hours, the productivity of desired product is decreased and the inclusion complex may be discolored in the reacted solution. The obtained inclusion complex is washed with some cooled-water several times to completely remove the remaining alkaline component on the inclusion complex, and then the refined complex of nutrality is obtained. Otherwise, the reacted solution may be purified by spray drying, freeze drying, vacuum evaporating or recrystalline method to obtain a refined inclusion complex power as stable compound, and at this time the refining procss may be carried out as per prior art according to properties of solusion system, namely kind of solution. The above inclusion complex obtained by the present invention is to obviously improve storage stability of compound itself, and simultaneously to entirely maintain the stability during formulating process and in gastric juice with excellent dissolution and absorption properties. In the stabilized inclusion complex, there is no alkaline component, because the alkaline solution according to the present invention was only used as reacting solution in the stabilizing process. This process is different in the used art and objective because the core material obtained is free from alkali component common with prior art. In the formulation of pharmaceutical preparation containing the inclusion complex of the present invention in the form of dosage units for oral administration, the above inclusion complex may be mixed with excipients such as microcrystalline cellulose, starch, manitol, etc., disintegrants such as sodium starch glycolate, etc. and lubricants such as magnesium stearate. The mixture is then pressed into tablets including active component, for example omeprazole of 20mg per tablet. The prepared tablets may be coated with a watersoluble substance selected from the group consisting of hydroxypropyl methylcellulose, hydroxypropyl cellulose, poly vinylidone and polyvinylalcohol, and thereafter coated with an enteric-coating agent selected from the group consisting of hydroxypropylmethyl cellulose phthalate, celluloseacetate phthalate and metacrylic acid-methyl metacrylate copolymer, which is mixed with plasticizer in organic solvent. The enteric-coated oral drugs formulated according to the present invention may be, as stabilized preparation including acid-unstable compound as active component, therapeutically administrated for the treatment of gastrointestinal disorders. The process described herein is successful in improving stability of acid-unstable compounds against acid, improves dissolution properties and improve preservability. Especially in case of omeprazole, this process entirely resolves the problems related to stability. The followings illustrate a preferred embodiment of the present invention without being limited thereto. Preparing Example 1 : Buffer Solution(Phosphate) To prepare an alkaline solution for stabilizing acid-unstable compound, 0.1M NaOH was added in 500τκZ of 0.1M KH^ as following Table 1. Those solutions were diluted with water to obtain phosphate buffer solutions of each 1000._- . Each pH of the resulted buffer solutions was measured to be selectively used for an alkaline solution. Table 1. Preparing Example 2 : Buffer Solution(Borate) O.IM NaOH was added in 500m/ of O.IM H 3 B0 3 -KC1 to obtain borate buffer 5 solutions according to the above Preparing Example 1 as following Table 2. Each pH of the resulted buffer solutions was measured to be selectivly used for an alkaline solution. ι o Table 2. 15 0 5 0 Preparing Example 3 : Tris Buffer Solution O.IM HCl was added in 500ml of O.IM tris(hydroxymethyl) amino methane to 5 obtain amine salt buffer solutions according to the above Preparing Example 1 as following Table 3. Each pH of the resulted buffer solutions was measured to be selectivly used for an alkaline solution. G Table 3. Preparing Example 4 : Buffer Solution (Borate) O.IM HCl was added in 500mZ of 0.025M Na 2 B 4 O 7 to obtain borate buffer solutions according to the above Preparing Example 1 as following Table 4. Each pH of the resulted buffer solutions was measured to be selectivly used for an alkaline solution. Table 4. Preparing Example 5 : Buffer Solution (Borate) O.IM NaOH was added in 500mZ of 0.025M Na^O, to obtain borate buffer solutions according to the above Preparing Example 1 as following Table 5. Each pH of the resulted buffer solutions was measured to be selectivly used for an alkaline solution. Table 5. Preparing Example 6 : Buffer Solution (Carbonate) O.IM NaOH was added in 500mZ of 0.05M NaHC0 3 to obtain carbonate buffer solutions according to the above Preparing Example 1 as following Table 6. Each pH of the resulted buffer solutions was measured to be selectivly used for an alkaline solution. Table 6. Preparing Example 7 : Buffer Solution (Phosphate) O.IM NaOH was added in 500mZ of 0.05M NaJEIP0 4 to obtain phosphate buffer solutions according to the above Preparing Example 1 as following Table 7. Each pH of the resulted buffer solutions was measured to be selectivly used for an alkaline solution. Table 7. Preparing Example 8 : Buffer Solution (Chlorate) 0.2M NaOH was added in 250mZ of 0.2M KC1 to obtain chlorate buffer solutions according to the above Preparing Example 1 as following Table 8. Each pH of the resulted buffer solutions was measured to be selectivly used for an alkaline solution. Table 8. The obtained buffer solutions may be preferably used in range of pH 8.0 - 12.0 for alkaline solution, and hydroxides of alkaline metal or alkaline salt of organic or inorganic salt may be also used by adjusting to range of pH 8.0 - 12.0. But, it is necessary for amines to define the preferable range of alkaline solution by molarity. According to the present invention, water-soluble or water-miscible amines shown on following Table 9, preferably 0.01 ~ 0.5M amines, may be preferably used, but methylamine, dimethyl amine, trimethylamine, ethylamine, isopropylamine, etc. were excluded from studies because of having low boiling point. Table 9. Example 1 β -Cyclodextrin of 24g was dissolved in each 900mZ of buffer solutions according to following Table 10 at 40 . , and 3.4g omeprazole was added in the solution under stirring to react for 15 mins. The reactant was concentrated to lOOmZ in vacuum evaporator, and after cooling to room temperature, it was left for 6 hrs in a refrigerator to deposit inclusion complex. The filtered inclusion complex was washed with water several times and dried under reduced pressure to obtain omeprazole-cyclodextrin inclusion complex. The result of reaction and an amount of the obtained inclusion complex were shown as following Table 10. Table 10. (Note) Non discoloration Light- violet color As the result shown in Table 10, it was found that when pH is low the inclusion complex is discolored to light- violet color, and when pH is high the obtained amount of inclusion complex is decreased due to washing with excess water. Therefore a buffer solution was preferably selected between pH 8.0 andpH 12.0 for an alkaline solution. Example 2 β -Cyclodextrin of 24g was dissolved in each 900mZ of buffer solutions(pH 9.0, pH 10.0, pH 11.0) according to following Table 11 at 40 _ , and 3.4g omeprazole was added in the solution under stirring to react for 15 mins. The reactant was concentrated to 100mZ in vacuum evaporator, and after cooling to room temperature, it was left for 6 hrs in a refrigerator to deposit inclusion complex. The filtered inclusion complex was washed with water several times and dried under reduced pressure to obtain omeprazole-cyclodextrin inclusion complex. The results of reaction were shown as following Table 11. Table 11. Example 1 Buffer solution pH Color of Rate of Inclusion Complex Inclusion(%) 89.0 91.2 90.1 98.6 99.1 98.9 99.2 98.8 As the result shown in Table 11, it is was found that when pH of buffer solution is the same the effectiveness of inclusion is not influenced by kind of buffer solution, and when it is more than pH 10 the rate of inclusion was higher than 98.6%. Example 3 β -Cyclodextrins according to following Table 12 were respectively dissolved in 900mZ of buffer solutions(pH 10.0) prepared by the above Preparing Example 2-11 to add omeprazole, and then the reaction temperature was changed to 40 . , 50 . ,60 . ,and 70 . as the reaction being carried out for 15 mins. The reactant was concentrated to lOO Z in vacuum evaporator, and after cooling to room temperature, it was left for 6 hrs in a refrigerator to deposit inclusion complex. The filtered inclusion complex was washed with water on several times and dried under reduced pressure to obtain omeprazole-cyclodextrin inclusion complex. The results of reaction were shown as following Table 12. Table 12. Example 3 Reaction Amount of Amount of Color of Rate of Temp.CC ) β -CD (g) Omeprazole(g) Inclusion complex Inclusion(%) - 98.6 98.8 99.0 98.0 (Note) - : Non discoloration β -CD : β -cyclodextrin Example 4 β -Cyclodextrines according to following Table 13 were respectively dissolved in 900_zZ of buffer solution(pH 10.0) prepared by the above Preparing Example 2-11 at 50 ... , and omeprazole was added in the solution under stirring to react for 15 mins. The reactant was concentrated to lOOmZ in vacuum evaporator, and after cooling to room temperature, it was left for 6 hrs in a refrigerator to deposit inclusion complex. The filtered inclusion complex was washed with water on several times and dried under reduced pressure to obtain omeprazole-cyclodextrin inclusion complex. The results of reaction were shown as following Table 13. Table 13. Example 5 β -cyclodextrin of 54g was dissolved in each 900mZ of O.IM amine aqueous solutions according to following Table 9 at 50 . , and 8.2g omeprazole was added in the solution under stirring to react for 15 mins. The reactant was cooled to room temperature and or concentrated to 100 m/ in vacuum evaporator, and it was left for 6 hrs in a refrigerator to deposit inclusion complex. The filtered inclusion complex was washed with water several times and dried under reduced pressure to obtain omepra?, le-cyclodextrin inclusion complex. The results of reaction were shown as following Table 14. Table 14. G (Note) Cool : Cooling to room temperature Cone. : Concentrating in vacuum evaporator Example 6 According to following Table 15, β -cyclodextrin was dissolved in 900mZ water, and on the other hand omeprazole was dissolved in 40% (v/v) triethylamine aqueous solution to obtain 27% solution. The resulted omeprazole solution was dropwise added in cyclodextrin aqueous solution. The reactant was cooled to room temperature, and left for 6 hrs in a refrigerator to deposit inclusion complex. The filtered inclusion complex was washed with water several times and dried under reduced pressure to obtain omeprazole-cyclodextrin inclusion complex. The results of reaction were shown as following Table 15. Table 15. Example 6 Reaction Amount of Amount of Rate of Temp, ( . ) β -CD(g) Omeprazole (g) Inclusion (%) Example 7 24g β -cyclodextrin was dissolved in 900 ml of pH 12 aqueous solutions of hydroxide of alkaline metals according to following Table 16, and 3.4g omeprazole was 5 added in this solution under stirring to react for 15 mins. The reactant was concentrated to lOOmZ in vacuum evaporator, and after cooling to room temperature, it was left for 6 hrs in a refrigerator to deposit inclusion complex. The filtered inclusion complex was washed with water several times and dried i o under reduced pressure to obtain omeprazole-cyclodextrin inclusion complex. The results of reaction were shown as following Table 16. Table 16. 5 Example 7 Kind of Reaction Amount of Amount of Rate of Hydroxide Temp.( . ) β -CD (g) Omeprazole(g) Inclusion(%) 0 5 Example 8 This experiment was conducted in same manner as previous Example 7 except that the other alkaline salt solutions according to following Table 17 were used to obtain omeprazole-dextrin inclusion complex. The filtered inclusion complex was washed with water several times and dried under reduced pressure to obtain omeprazole-cyclodextrin inclusion complex. The results of reaction were shown as following Table 17. Table 17. Example 8 Kind of pH Reaction Amount of Amount of Rate of alkaline salts Temp.( . ) β -CD (g) Omeprazole(g) Inclusion(%) [ Methods for measuring rate of inclusion ] Amount of omeprazole in the obtained inclusion complex (g) X 100 = Rate ofinclusion(%) Amount of used omeprazole (g) The amount of omeprazole in the obtained inclusion complex was measured by HPLC under following conditions . • Solvent : pH 9.8 Carbonate buffer solution : ethanol = 80 : 20 • Column : μ -Bondapak C 3.9mm (the inside diameter) X 300mm (length) • Mobile Phase : pH 7.6 Phosphate buffer solution : Acetonitrile = 66 : 34 • Detection Wave-length : 302 nm • Injection Volum : 20/4 • Flow Rate : l.O mZ/min Comparative Example 1 5.67g β -cyclodextrin and 1.73g omeprazole were added in 96% ethanol of 20 ml and stirred at 30 - 32 . for 15 hrs. After leaving at 10 . for 3hrs, the reacted solution was filtered, and washed with ethanol of 10 . , dried under reduced pressure to obtain the desired product of reddish brown color. At this time the reactant solution was of purple color. Comparative Example 2 2.0g Omeprazole was well mixed with 2.0g Na 2 HP0 4 , and the mixed compound was dried under reduced pressure to obtain the stabilized core of omeprazole preparation as a comparative sample. Comparative Example 3 This test was conducted in process of the above Comparative Example 2 except to use 2.0g omeprazole and 2.0g Mg(OH) 2 . The obtained core was used as a 5 comparative sample. Experimental Example 1 (Storage Stability of Inclusion Complex) To verify stabilized result for the above Example 1 to 8 and Comparative o Example 1 to 3, the change of appearance was surveyed with the passing of time under 40 XZ , 75% RH of accelarated condition. The results were shown on following Table 18. Under the above condition, storage stability during 6 months means to secure stability for 3 years at normal condition. As the result of Table 18, it was confirmed 5 that the cases of Example 1 - 8 according to the present invention is obviously showing higher stability than the cases of Comparative Example 1 - 3. Table 18. The Change of Appearance Sample Start After Imonth After 2months After 4months After όmonths Example 1-D Example 2-B Example 2-E Example 2-G Example 3-A Example 3-D Example 4-A Example 4-B Example 4-D Example 4-E Example 4-F Example 4-G Example 4-H Example 5-B Example 5-1 Example 6-A Example 6-D Example 7-A Example 8-C Comp. Ex. 1 ++ ++ Comp. Ex.2 + + ++ Comp. Ex.3 + (Note) Non discoloration + Some discoloration + Discoloration Deep discoloration Formulation of Inclusion Complex To formulate enteric-coated oral drugs, the omeprazole-cyclodextrin inclusion complexs obtained by Example 1 - 8 were used as followings. [ Preparing of Uncoated Tablets ] According to following Table 19, omeprazole of 20mg was homogeneousely mixed with excipients, disintegrants and lubricants, and the mixture was tableted to 230mg per unit by Rotary Tableting Machine. Table 19. In the above, when microcrystalline cellulose and dibasic calcium phosphate anhydrous of an excess of quantity were used, hardness of tablets is excellent but disintegration rate was decreased. Therefore, microcrystalline cellulose of small amount was preferably used, and at that time the used amount of corn starch and/or Mannitol were increased and minimum amount of dibasic calcium phosphate anhydrous was used. [ Coating of Watersoluble Substance ] According to following Table 20, a watersoluble substance was coated on uncoated tablets. Table 20. (Unit : mg ) Components (J.) (T 2 ) (T 3 ) (T 4 ) (T 5 ) (T 6 ) σ 7 ) (T 8 ) σ 9 ) of Watersoluble Substance Hydroxy propylmethyl cellulose 10 9 9 9 9 9 - - - Hydroxypropyl cellulose - - - - - - g . - Polyvinylpynolidone - - - - - - - g . Polyvinylalcohol - - - - - - - - g Propyleneglycol _ i . _ i _ _ _ _ Polyethyleneglycol 600 - - 1 - - 1 1 1 1 Water 190 190 190 38 38 38 38 38 38 Ethanol - - - 152 152 152 152 152 152 In the above test, when water was only used as solvent or excessive water was used, dry time in coating pan was prolonged. Since tablets were observed to stick with each other and rendering the coating 5 surface ununiform, ethanol, preferably 80% ethanol water solution, was used in this process as main solvent. [ Coating of Enteric Substance ] According to following Table 21, an enteric substance was coated on tablets ι o coated with watersoluble substance to obtain the desired enteric-coated oral drug. Table 21. Components of Enteric Substance a b c d e 15 Hydroxypropylmethyl cellulose 18.6 18.6 phthalate Cellulose acetate phthalate 18.6 18.6 Eudragit L100 18.0 Cetylalcohol 1.4 1.4 0 Myvacet 9-40T 1.4 1.4 Dibutylphthalate 2.0 Acetone 152 190 152 152 190 Ethylalcohol 228 190 228 190 Isopropylalcohol 228 5 Experimental Example 2 : Property Test for Oral Drugs The obtained inclusion complexs of Examples were used to formulate enteric- coated oral drugs. To survey the properties for the oral drugs, the watersoluble substance according to the method of Table 20(T 5 ) was respectively coated on tablets prepared from Example 4-A, 5-1, 6-B, 7-A and 8-C, and there after the enteric substance according to the method of Table 21 "d" was coated on the above tablets. The formulated oral drugs were compared with control product, Astra's LOSEC, to survey acid-resistance property, dissolution property, and storage stability as followings. [ Test for Acid-resistance Property ] The formulated oral drugs were put into artificial gastric fluid [USP, 1st solution] without enzyme and stirred at 37 . by paddle at 100 rpm. The test solution was left for 2hrs to survey the change of appearance, and the omeprazole existing in preparation was measured by HPLC. The results were shown on following Table 22. Table 22. The above test showed brown spots on 40 - 75% of pellets for th control(LOSEC), and it was also found that omeprazole content was decreased. But, the oral drugs prepared according to examples were not affected in th 5 appearance and omeprazole content was scarcely decreased, thus giving superior characteristies. [ Test for Dissolution Property ] To survey the rate of dissolution in the small intestines, the formulated oral ι o drugs were added to simulated gastric fluid [USP, 37 . , 100 rpm]. After 2hrs, the above drugs were moved to simulate intestinal fluid [USP, dissolution apparatus No. 2, Paddle Method], and then the amount of dissolved omeprazole was determined by the method of HPLC. The results were shown on Table 23. 15 Table 23. (Unit : %) 0 As the result from the above experiment show, the dissolution rate for all samples was good only Example 4-A and 5-1 produced using dibasic calcium phosphate anhydrous as excipient showed Somewhat slow dissolution rate in first 10 minutes. The rate of dissolution after 20mins and 30mins, testing samples of Examples were obviously higher than the control. [ Test for Storage Stability ] According to the process of Experiment Example 1, the drugs were kept in glass bottle for 6 months under 40 T_ , 75% RH of accelerated condition and 501. , 75% RH of harsh condition. The changes of appearance for the resulted samples were surveyed. The results were shown on Table 24. Table 24. Example 5 - 1 Example 6 - B Example 7 - A Example 8 - C Control (Losec) + ++ (Note) Non discoloration ± Some discoloration + Discoloration ++ Deep discoloration As the result of above, it was confirmed that the storage stabilities of Examples were obviously higher than the control. As the result of Experimental Example 2, it was found that the enteric-coated oral drugs of the present invention formulated with omeprazol-cyclodextrin inclusion complex have excellent stability and dissolution property as compared with known preparations.

Claims: WHAT IS CLAIMED IS : 1. A method for stabilizing an acid-unstable compound comprising : reacting an acid-unstable compound with a cyclodextrin in an alkaline solution, the ratio of =. said acid-unstable compound to said cyclodextrin in said reaction being from about 1 : 1 to about 1 : 10. 2. In the method of claim 1, said acid-unstable compound comprising a benzimidazol derivative having the following structural formula, and pharmaceutically acceptable salts thereof, wherein, R r is selected from the group consisting of hydrogen, methoxy, trifluoromethyl and tetrafluoroethoxy radicals ; Rm. is selected from the group consisting of hydrogen, methylamine and dimethylamine radicals ; R 3 is selected from the group consisting of hydrogen, methoxy, aryloxy and propaziloxy radicals ; and R 4 is selected from the group consisting of hydrogen and methyl radicals. 3. In the method of claim 1, said acid-unstable compound is omeprazole. 4. In the method of claim 1, said alkaline solution consists essentially of an aqueous solution of an alkali selected from the group consisting of alkaline hydroxides, alkaline salts, amines, buffers, and combinations thereof. 5. In the method of claim 4, said alkaline hydroxide is selected from the group consisting of sodium hydroxide, potassium hydroxide, calcium hydroxide, barium hydroxide and combinations thereof. 5 6. In the method of claim 4, said alkaline salt is selected from the group consisting of sodium borate, sodium carbonate, sodium phosphate, potassium borate, potassium carbonate, potassium phosphate, sodium acetate, sodium citrate and combinations thereof. ι o 7. In the method of claim 4, said amine is selected from the group consisting of diethylamine, triethylamine, butylamine, ethylenediamine, triethanolamine, propylamine, dipropylamine, diethanolamine, monoethanolamine, isobutylamine, diisopropylamine, tert-butylamine, dibutylamine, diisobutylamine, tributylamine, pentylamine, dipentylamine and combinations 15 thereof. 8. In the method of claim 4, said buffer is selected from the group consisting of carbonate buffer, phosphate buffer, borate buffer, amine salt buffer, and combinations thereof. 0 9. The method of claim 1 further comprising adjusting the heat content of the reaction mixture in a manner effective to maintain the reaction temperature between about 40 and about 70 _ . 5 0

Inventors: KIM YONG SOO, MIN DONG SUN, PARK PYONG WOOK, UM KEE AN, KIM, YONG, SOO, MIN, DONG, SUN, PARK, PYONG, WOOK, UM, KEE, AN
Applicants: SUNKYONG IND LTD, SUNKYONG INDUSTRIES CO., LTD.
Application year: 1992
Main classification: A61K31
IPC codes: A61K31, A61K47, C08B37