Aliphatic polyurea elastomers

Abstract: Aliphatic spray polyurea elastomers comprising an (A) component including an aliphatic polyisocyanate, and a (B) component including an amine-terminated polyoxyalkylene polyol and a chain extender exhibit UV-stability, increased flexibility and good processing characteristics when the chain extender is a diamine-terminated compound.

Description: The present invention relates to aliphatic polyurea elastomers. Polyurea elastomer systems are commonly used as coating materials, with spray polyurea elastomer systems being particularly useful when employed in this capacity. One of the shortcomings associated with aromatic polyurea elastomer systems, which generally are prepared by reacting an aromatic isocyanate with an active hydrogen component in the presence of an aromatic chain extender, is that they exhibit poor stability when exposed to ultraviolet radiation. This becomes particularly problematic when the substrate to be coated, for example, a rooftop, is continuously subjected to ultraviolet exposure. The resulting ultraviolet degradation of the elastomer system is typically manifested by a change in colour; a general loss of product integrity, such as cracking; and an adverse reduction in properties, such as tensile strength, tear strength and elongation, to name a few. Within this text, 'aliphatic compound' is defined as aliphatic and alicyclic compounds as usually understood, and further includes an aromatic ring-containing isocyanate or amine wherein functional groups such as isocyanate- or amino-groups bond only to carbon atoms outside the aromatic ring; and 'aromatic' isocyanate or amine means compounds wherein the functional groups are bonded to carbon atoms within the aromatic ring. The most widely employed aromatic chain extender is diethylenetoluenediamine (DETDA), a product of Ethyl Corp. In addition to providing an ultraviolet unstable system, DETDA provides a rigid elastomer system which, because of the rigidity, has difficulty in assuming the detail or contour of the substrate to be coated. However, polyurea elastomer systems fabricated from, among other things, DETDA generally exhibit good processing characteristics. Thus, there is a recognized need for a polyurea elastomer system that exhibits ultraviolet stability and increased flexibility, i.e., less rigidity, while exhibiting good processing characteristics. To provide an ultraviolet stable system, however, non-aromatic, i.e., aliphatic, components should be employed. For instance, Rowton, R. L., CYANOETHYLATED POLYOXYPROPYLENEPOLYAMINES: POLYMER FORMERS OF UNIQUE REACTIVITY, Journal of Elastomers and Plastics, Vol. 9, October 1977, describes cyanoethylated polyoxypropylenepolyamines as the hydrogen component in polyurea systems to provide light stable systems. Rowton is silent with respect to employing aliphatic chain extenders. Some of the known aliphatic chain extenders include trans-1,4-diaminocyclohexane and 1,6-diaminohexane. These and other known aliphatic chain extenders react very rapidly with isocyanate and, therefore, cannot be used in spray systems, inasmuch as polymerization occurs so rapidly that the polymer is virtually unsprayable. Therefore, while the aliphatic polyurea elastomers of the present invention can be used in reaction injection molding (RIM) systems, it is to be noted that the advantage provided by the present invention is more noteworthy in spray systems, relative to other elastomer systems where sprayability is not at issue, such as RIM systems. Other low molecular weight, linear primary amine chain extenders exhibit a rapid reactivity that result in poor mixing and elastomer cure. Additionally, elastomer systems prepared with known aliphatic chain extenders have notoriously exhibited processing characteristics inferior to those exhibited by systems fabricated from DETDA. U.S. Patent No. 3,666,788 is directed to cyanoalkylated polyoxyalkylene polyamines which are specifically described as being useful as curing agents in polyurea coatings. Similarly, U.S. Patent No. 3,714,128 describes cyanoalkylated polyoxyalkylene polyamines which are useful for slowing the gelling or hardening of the polyurea component so that good mixing of the isocyanate and amine components can be attained, which gives the sprayed material ample time to adhere and level before gelation of the polyurea coating occurs. Neither of these patents describe the present diamines as chain extenders in aliphatic spray polyurea elastomer systems. Polyoxyalkylene polyamines, particularly JEFFAMINE® T-403, D-400 and D-230, are described as chain extenders in U.S. Patent No. 4,732,919; however, this patent relates to an aromatic system which is to be used in a RIM application. EP-A-416819 describes aliphatic spray polyurea elastomers comprising an (A) component which includes an aliphatic isocyanate and a (B) component which includes (1) an amine terminated polyoxyalkylene polyol, and (2) an amine terminated chain extender. EP-A-0348760 describes a process for the production of films or products based on polyisocyanate poly-addition by thermoplastic moulding at elevated temperatures. Cycloaliphatic polyisocyanates are reacted with compounds reactive towards NCO groups and, optionally, diamines and other auxiliary agents. Accordingly, the present invention relates to an aliphatic spray polyurea elastomer which comprises an (A) component and a (B) component. The (A) component includes an aliphatic isocyanate. The isocyanate of the (A) component preferably comprises a quasi-prepolymer of an aliphatic isocyanate and a material selected from at least one polyol, a high molecular weight polyoxyalkyleneamine, or a combination of these materials. The (B) component includes (1) an amine terminated polyoxyalkylene polyol as defined in claim 1, and (2) a chain extender consisting of cis-1,4-diaminocyclohexane, isophoronediamine, m-xylylenediamine, 4,4'-methylenedicyclohexylamine, menthanediamine, 1,4-diamino-methylcyclohexane. It has advantageously been discovered that the polyurea elastomer system of the present invention is ultraviolet stable, exhibits increased flexibility, and possesses favorable processing characteristics. Additionally, the low temperature elongation and green strength of the present spray polyurea elastomer system are extremely good. Furthermore, since the present elastomer system is 100 percent solids, no solvent is required to promote spraying, when the elastomer is used in that capacity. The aliphatic isocyanates employed in component (A) are those known to one skilled in the art. Thus, for instance, the aliphatic isocyanates are of the type described in U.S. Patent No. 4,748,192. Accordingly, they are typically aliphatic diisocyanates and, more particularly, are the trimerized or the biuretic form of an aliphatic diisocyanate, such as hexamethylene diisocyanate, or the bifunctional monomer of the tetraalkyl xylylene diisocyanate, such as the tetramethyl xylylene diisocyanate. Cyclohexane diisocyanate is also considered a preferred aliphatic isocyanate. Other useful aliphatic polyisocyanates are described in U.S. Patent No. 4,705,814. They include aliphatic diisocyanates, for example, alkylene diisocyanates with 4 to 12 carbon atoms in the alkylene radical, such as 1,12-dodecane diisocyanate and 1,4-tetramethylene diisocyanate. Also described are cycloaliphatic diisocyanates, such as 1,3- and 1,4-cyclohexane diisocyanate as well as any desired mixture of these isomers; 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl-cyclohexane(isophorone diisocyanate); 4,4'-,-2,2'- and 2,4'-dicyclohexylmethane diisocyanate as well as the corresponding isomer mixtures, and the like. The aforementioned isocyanates can be used alone or in combination. It is to be understood that the term "aliphatic isocyanate" also includes quasi-prepolymers of aliphatic isocyanates with active hydrogen-containing materials. The active hydrogen-containing materials can include a polyol or a high molecular weight polyoxyalkyleneamine, also described hereinbelow as amine terminated polyethers, or a combination of these materials. The polyols include polyether polyols, polyester diols, triols, tetrols, etc., having an equivalent weight of at least 500, and preferably at least 1,000 up to 3,000. Those polyether polyols based on trihydric initiators of 4,000 molecular weight and above are especially preferred. The polyethers may be prepared from ethylene oxide, propylene oxide, butylene oxide, or mixtures of propylene oxide, butylene oxide and/or ethylene oxide. Other high molecular weight polyols which may be useful in this invention are polyesters of hydroxyl terminated rubbers, e.g., hydroxyl terminated polybutadiene. Hydroxyl terminated quasi-prepolymers of polyols and isocyanates are also useful in this invention. Especially preferred are amine terminated polyether polyols, including primary and secondary amine terminated polyether polyols of greater than 1,500 average molecular weight having from 2 to 6 functionality, preferably from 2 to 3, and an amine equivalent weight of from 750 to 4,000. Mixtures of amine terminated polyethers may be used. In a preferred embodiment, the amine terminated polyethers have an average molecular weight of at least 2,500. These materials may be made by various methods known in the art. The amine terminated polyether resins useful in this invention are, for example, polyether resins made from an appropriate initiator to which lower alkylene oxides, such as ethylene oxide, propylene oxide, butylene oxide, or mixtures thereof, are added with the resulting hydroxyl terminated polyol then being aminated. When two or more oxides are used, they may be present as random mixtures or as blocks of one or the other polyether. In the amination step, it is highly desirable that the terminal hydroxyl groups in the polyol be essentially all secondary hydroxyl groups for ease of amination. Normally, the amination step does not completely replace all of the hydroxyl groups. However, the majority of hydroxyl groups are replaced by amine groups. Therefore, in a preferred embodiment, the amine terminated polyether resins useful in this invention have greater than 50 percent of their active hydrogens in the form of amine hydrogens. If ethylene oxide is used, it is desirable to cap the hydroxyl terminated polyol with a small amount of higher alkylene oxide to insure that the terminal hydroxyl groups are essentially all secondary hydroxyl groups. The polyols so prepared are then reductively aminated by known techniques, for example, as described in U.S. Patent No. 3,654,370. In the practice of this invention, a single high molecular weight amine terminated polyol may be used. Also, mixtures of high molecular weight amine terminated polyols, such as mixtures of di- and trifunctional materials and/or different molecular weight or different chemical composition materials, may be used. Also, high molecular weight amine terminated polyethers or simply polyether amines are included within the scope of this invention and may be used alone or in combination with the aforementioned polyols. The term "high molecular weight" is intended to include polyether amines having a molecular weight of at least 2,000. Particularly preferred are the JEFFAMINE series of polyether amines available from Texaco Chemical Company; they include JEFFAMINE D-2000, JEFFAMINE D-4000, JEFFAMINE T-3000 and JEFFAMINE T-5000. These polyether amines are described with particularity in Texaco Chemical Company's product brochure entitled THE JEFFAMINE POLYOXY-ALKYLENEAMINES. The (B) component of the present polyurea elastomer system includes an amine terminated polyoxyalkylene polyol and specific cycloaliphatic diamine chain extenders as defined in claim 1. In a most preferred embodiment, the diamine chain extender of component (B) is selected from cis-1,4-diaminocyclohexane and isophoronediamine. These diamine chain extenders give the elastomer system the requisite activity to yield good cure and good spray processing characteristics. Additionally, the thus formed aliphatic system is ultraviolet stable and exhibits improved flexibility so that it can be effectively sprayed onto even the most intricately shaped substrate. Other conventional formulation ingredients may be employed in component (A) or (B) as needed, such as, for example, foam stabilizers, also known as silicone oils or emulsifiers. The foam stabilizers may be an organic silane or siloxane. For example, compounds may be used having the formula: RSi[O-(R 2 SiO) n -(oxyalkylene) m R] 3 wherein R is an alkyl group containing from 1 to 4 carbon atoms; n is an integer of from 4 to 8; m is an integer of from 20 to 40, and the oxyalkylene groups are derived from propylene oxide and ethylene oxide. See, for example, U.S. Patent No. 3,194,773. Pigments, for example, titanium dioxide, may be incorporated in the elastomer system, preferably in the (B) component, to impart color properties to the elastomer. Reinforcing materials, if desired, useful in the practice of our invention are known to those skilled in the art. For example, chopped or milled glass fibers, chopped or milled carbon fibers, and/or other mineral fibers are useful. Post curing of the elastomer of the invention is optional. Post curing will improve some elastomeric properties, such as heat sag. Employment of post curing depends on the desired properties of the end product. The (A) component and (B) component of the present polyurea elastomer system are combined or mixed under high pressure; most preferably, they are impingement mixed directly in the high pressure spray equipment which is, for example, a GUSMER® H-V proportioner fitted with a GUSMER Model GX-7 spray gun. In particular, a first and second pressurized stream of components (A) and (B), respectively, are delivered from two separate chambers of the proportioner and are impacted or impinged upon each other at high velocity to effectuate an intimate mixing of the two components and, thus, the formation of the elastomer system, which is then coated onto the desired substrate via the spray gun. The volumetric ratio of the (A) component to the (B) component is generally from 30 to 70 percent to 70 to 30. Preferably, component (A) and component (B) are employed in a 1:1 volumetric ratio. Advantageously, the (A) and (B) components react to form the present elastomer system without the aid of a catalyst. GLOSSARY OF TERMS AND MATERIALS JEFFAMINE T-5000 - Polypropylene oxide triamine of about 5000 molecular weight; a product of Texaco Chemical Company. JEFFAMINE D-4000 - Polypropylene oxide diamine of about 4000 molecular weight; a product of Texaco Chemical Company. JEFFAMINE D-2000 - Polypropylene oxide diamine of about 2000 molecular weight; a product of Texaco Chemical Company. JEFFAMINE T-403, D-400 and D-230 are described with particularity hereinabove. The following Examples I - X are provided to further illustrate preferred embodiments of the present invention EXAMPLE I The (A) component of an aliphatic polyurea elastomer was prepared by combining 40 parts of a quasi-prepolymer of m-tetramethylxylene diisocyanate (m-TMXDI) with 60 parts of JEFFAMINE D-2000. The (B) component was prepared by combining 44.35 parts of JEFFAMINE T-5000, 44.35 parts of JEFFAMINE D-2000, and 11.30 parts of 1,4-diaminocyclohexane. The 1,4-diaminocyclohexane used in this example was a 50:50 mixture of the trans- (solid) and cis- (liquid) isomer. The components were mixed at a volumetric ratio (A:B) of 1.00 (1.05 A:B weight ratio) in the high pressure spray equipment to produce the aliphatic polyurea elastomer with a gel time of approximately three seconds. The elastomer was slightly tacky (sticky). Good green strength was noted. It was later discovered that the trans-isomer showed some incompatibility in the component, as evidenced by the presence of insoluble solid particles in the elastomer. No physical property testing was done. EXAMPLE II The (A) component of an aliphatic polyurea elastomer was prepared by combining 50 parts of m-TMXDI with 50 parts of JEFFAMINE D-2000. The (B) component was prepared by combining 37.45 parts of JEFFAMINE T-5000, 37.45 parts of JEFFAMINE D-2000, and 25.10 parts of isophorodiamine (IPDA). The (A) and (B) components were mixed as in Example I and at the same volumetric and weight ratios. The isocyanate index was 1.05. The resulting elastomer exhibited a gel time of approximately one second and a tack free time of five seconds. The physical properties of the elastomer produced in Example II were determined; the results are reported in Table I. Tensile strength (psi) 935 (= 6.44 MPa) Elongation (%) 356 Tear (p/i) 306 (= 54.6 kg/cm) Shore D hardness (0 sec) 44 100% modulus (psi) 763 (= 5.26 MPa) 300% modulus (psi ) 890 (= 6.13 MPa) EXAMPLES III - V In these examples, three additional aliphatic polyurea elastomers were prepared in the manner set forth in Examples I and II. In each example (i.e., Examples III, IV and V), the (A) component of the elastomer was prepared by combining 40 parts of m-TDXDI and 60 parts of JEFFAMINE D-2000. Table II is provided below to show the materials used to prepare the (B) component in each of the subject examples. Table II also included other particulars respecting the elastomers prepared in Examples III-V. Example III Example IV Example V Materials (For (B) Component) JEFFAMINE T-5000 44.45 87.7 37.75 JEFFAMINE D-2000 44.45 - 37.75 cis-1,4-diaminocyclohexane 11.1 12.3 - JEFFAMINE T-403 - - 24.5 Processing Particulars (A):(B) Vol. ratio 1.00 1.00 1.00 (A):(B) Weight ratio 1.05 1.05 1.06 Gel time (sec.) <3.0 <3.0 4.0 Tack free time (sec.) 20.00 >60 EXAMPLES VI - VIII In these examples, three additional aliphatic polyurea elastomers were prepared in the manner set forth in Examples I, II, and III-V. In each example (i.e., Examples VI, VII and VIII), the (A) component of the elastomer was prepared by combining 60 parts of m-TMXDI and 40 parts of JEFFAMINE D-2000. Table III is provided below to show the materials used to prepare the (B) component in each of the subject examples. Table III also includes other particulars respecting the elastomers prepared in Examples VI - VIII. Example VI Example VII Example VIII Materials (For (B) Component) JEFFAMINE T-5000 27.3 40.7 36.8 JEFFAMINE D-2000 18.2 27.1 24.6 IPDA - 32.2 19.3 JEFFAMINE T-403 25.0 - - JEFFAMINE D-230 29.5 - 19.3 Processing Particulars Index 1.05 1.05 1.05 (A):(B) Vol. ratio 1.00 1.00 1.00 (A):(B) Weight ratio 1.06 1.02 1.04 Gel time (sec.) 1.5 1.0 1.0 Tack free time (sec.) 2.0 2.0 2.0 The physical properties of the elastomers produced in Examples VI - VIII were determined; the results are reported in Table IV. Properties Example VI Example VII Example VIII Tensile strength (psi) 1583 (10.9 ) 1300 (8.96 ) 1417 (9.77 ) Elongation (%) 395 263 428 Tear (p/i) 347 (62 ) 373 (67 ) 365 (65 ) Shore D hardness (0 sec.) 47 46 43 100% modulus (psi) 1003 (6.91 ) 1105 (7.62 ) 1075 (7.41 ) 300% modulus (psi) 1265 (8.72 ) - 1200 (8.27 ) EXAMPLES IX AND X In these examples, two additional aliphatic polyurea elastomers were prepared in the manner set forth in Examples I, II, III-V and VI-VIII. In each example (i.e., Examples IX and X), the (A) component of the elastomer was prepared by combining 60 parts of m-TMXDI and 40 parts of JEFFAMINE D-2000. Table V is provided below to show the materials used to prepare the (B) component in each of the subject examples. Table V also includes other particulars respecting the elastomers prepared in Examples IX and X. Example IX Example X Materials (For (B) Component) JEFFAMINE T-5000 47.1 23.6 JEFFAMINE D-2000 31.4 55.1 cis-1,4-diaminocyclohexane 21.5 21.3 Processing Particulars Index 1.05 1.05 (A):(B) Vol. ratio 1.00 1.00 (A):(B) Weight ratio 1.04 1.05 Gel time (sec.) 1.0 1.0 Tack free time (sec.) 1.5 2.0 The physical properties of the elastomers produced in Examples IX and X were determined; the results are reported in Table VI. Properties Example IX Example X Tensile strength (psi) 3181 (21.93 ) 1335(9.20 ) Elongation (%) 400 482 Tear (p/i) 314 (56 ) 346 (61 ) Shore D hardness (0 sec.) 32 38 100% modulus (psi) 793 (5.47 ) 812 (5.59 ) 300% modulus (psi) 1062 (7.32 ) 1046 (7.21 )

Claims: A method of preparing a polyurea elastomer coating comprising impingement mixing and spraying of: (A) a component including an aliphatic isocyanate, an alicyclic polyisocyanate, an aromatic ring, containing isocyanate wherein the isocyanate group(s) bond only to carbon outside the aromatic ring, or quasi prepolymers of the isocyanate with active hydrogen containing compounds; and (B) a component including (i) primary and secondary amine terminated polyether polyols of greater than 1.500 average molecular weight having a functionality of 2 to 6 and an amine equivalent weight of 750 to 4000; and (ii) a chain extender characterized in that the chain extender consists of cis-1,4-diaminocyclohexane, isophoronediamine, m-xylylenediamine, 4 ,4'-methylenedicyclohexylamine, menthanediamine, 1,4-diamino-ethylcyclohexane or a mixture thereof. A method as claimed in Claim 1, characterized in that the isocyanate is hexamethylene diisocyanate, tetraalkyl xylylene diisocyanate, cyclohexane diisocyanate, 1,12-dodecane diisocyanate, 1,4-tetramethylene diisocyanate, isophorone diisocyanate, dicyclohexylmethane diisocyanate, a mixture thereof, or a quasi-prepolymer of an aliphatic isocyanate and an active hydrogen containing material. A method as claimed in claim 2, characterized in that the active hydrogen containing material of the quasi prepolymer is a polyol, a polyoxyalkyleneamine of a molecular weight of at least 2.000, or a combination thereof. A method as claimed in claim 3, characterized in that the polyol comprises polyether polyols or polyester polyols having an equivalent weight of at least 500. A method as claimed in claim 4, characterized in that the polyester polyols are polyesters of hydroxyl terminated rubbers. A method as claimed in claim 4, characterized in that the polyether polyols are polyols based on trihydric initiators having a molecular weight of at least 4.000; amine terminated polyether polyols having an average molecular weight greater than 1.500, a functionality of from 2 to 6 and an amine equivalent weight of from 750 to 4.000; or mixtures thereof. A method as claimed in claim 4, characterized in that the polyether polyols are derived from amine terminated polyether resins having greater than 50 percent of their active hydrogens in the form of amine hydrogens. A method as claimed in any one of claims 1 to 7, characterized in that component (A) and/or (B) further comprises pigments and/or reinforcing materials selected from milled or chopped glass fibers or mineral fibers. A method as claimed in any one of claims 1 to 8, characterized in that the volumetric ratio of the (A) component to the (B) component is from 30 to 70 percent of the (A) component to 70 to 30 percent of the (B) component.

Inventors: PRIMEAUX DUDLEY JOSEPH II, PRIMEAUX, DUDLEY JOSEPH II
Applicants: HUNTSMAN CORP, HUNTSMAN CORPORATION
Application year: 1992
Main classification: C08G18
IPC codes: C08G18