Treating solution for contact lenses

Abstract: A highly hydrous soft contact lens comprising a copolymer which contains as an ingredient a monomer having constitution similar to that of phospholipid represented by the following general formula: wherein X is and R₁ is hydrogen or methyl, Y is -CH₂-, -CH₂-O-, -CH₂CH₂-O-, -CH₂CH₂CH₂-O-, or -CH₂CH₂CH₂CH₂-O-, n is an integer of 1-20, and, R₂, R₃ and R₄ are the same or different groups and alkyl or hydroxyalkyl of 1-8 carbon atoms. Further, a treating solution for contact lenses which comprises a polymer containing as an ingredient the above monomer and a solvent which can dissolve the polymer.

Description: The present invention relates to treating solutions for contact lenses, more particularly, to treating solutions for contact lenses such as hard contact lenses, anhydrous soft contact lenses and hydrous soft contact lenses to give stain resistance and hydrophilic nature to these lenses. A highly hydrous soft contact lens is characterized in that it gives little feeling of physical disorder to the eyeball in comparison with a hard contact lens not containing water which essentially comprises a monomer such as methyl methacrylate, and siloxanylalkyl methacrylate (Japanese Patent Publication Sho 52-33502 (1977)). As for a hydrous contact lens, a lens essentially containing 2-hydroxyethyl methacrylate supplies little oxygen and gives feeling of physical disorder to the eyeball. Recently, to increase the percentage of water content, a contact lens comprising a copolymer of N-vinyl-pyrrolidone and methyl methacrylate, 2-hydroxyethyl methacrylate or methacrylic acid was proposed, However, the above contact lens has the disadvantage that stains are easily adhered to the lens to lower the strength and the lens grows yellowish by repeated heat treatment for sterilization. Conventionally used contact lenses may be classified into two groups, anhydrous hard or soft contact lenses and hydrous soft contact lenses. These anhydrous lenses having advantages over the hydrous lenses in terms of stability of materials and simple care are lenses principally containing methylmethacrylate or lenses made of silicone rubber. Lately, a hard contact lens having high oxygen permeability principally containing silyl type methacrylate or fluoric type methacrylate which gives moderate effects to eyes has been used. However, the anydrous lenses have problems that the hydrophobic surface gives a feeling of physical disorder to the eyeball and has a bad influence on the cells in the eyeball. In particular, the lenses having high oxygen permeability and containing silicone or fluorine in large quantities are highly hydrophobic, and there are problems of feeling of physical disorder, lowering of adhesion properties and staining of proteins and lipids. Therefore, to change the hydrophobic surface into a hydrophilic surface, it is known to treat with plasma or chemically treat with acid or basic materials. These methods have problems in the maintenance of the hydrophilic nature, the denaturation after the treatment, and troublesome treating steps. As the other method, for example, there is a method disclosed by Japanese Patent Publication No. 48-37910 (1973) in which a contact lens is immersed into a solution containing a water-soluble polymer of polyvinyl alcohol, hydroxyethyl cellulose, polyvinylpyrrolidone or the like. There are disadvantages that hydrophilic contact lenses are not always obtained by the method and the method is not effective for prevention of stains such as proteins and lipids. In the other hand, the hydrous soft contact lenses give a good fit to eyes and have no problems. However, these lenses are hydrogel lenses principally constituting 2-hydroxyethyl methacrylate, vinylpyrrolidone or the like, and there are disadvantages of adhesion of proteins, lipids and the like to the lenses, and increase of bacteria for sanitary reasons, and lowered mechanical strength for increased water content. Therefore, sanitary care is commonly required for the lenses by boiling, sterilization or by using a care product such as germicides or detergent liquids. WO-A-92/07885 was published on 14 May 1992 and claims priority from an application filed on 29 October 1990. It discloses as a contact lens material cross-linked copolymers which are obtainable by polymerising a neutral diluent monomer or monomers, a monomer or monomers bearing a centre of permanent positive charge, and a bifunctional and/or trifunctional cross-linking agent and processes for the preparation thereof. An object of the present invention is to provide a treating solution for a contact lens, the solution being capable of giving a surface hydrophilic nature to anhydrous contact lenses or high water content to hydrous contact lenses, improving the fit or feeling to eyes, and preventing the adhesion or deposit of stains of proteins and lipids. The present invention provides a treating solution for contact lenses which comprises 0.01 to 10% by weight of a polymer obtained by polymerisation of one or more monomers according to formula (1) below or by copolymerization of 1 to 95% by weight of the said monomer(s) and 99 to 5% by weight of a copolymerizable monomer, and a solvent which can dissolve the polymer: wherein X is and R 1 is hydrogen or methyl, Y is -CH 2 -, -CH 2 -O-, -CH 2 CH 2 -O-, -CH 2 CH 2 CH 2 -O-, or -CH 2 CH 2 CH 2 CH 2 -O-, n is an integer of 1-20, and, R 2 , R 3 and R 4 are the same or different groups and alkyl or hydroxyalkyl of 1-8 carbon atoms. The present invention may be embodied as follows. In the present invention, the monomer having phospholipid-like constitution which is used as an essential ingredient is a monomer represented by the above general formula (1). In the formula, n is an integer of 1-20. If n is more than 20, the hydrophilic nature of the polymer is undesirably lowered. Carbon atoms of alkyl groups of R 2 -R 4 are 1-8. If the carbon atoms are more than 8, a significant decrease of the hydrophilic nature of the polymer or polymerizability of the monomer is observed, so that such a compound is unsuitable for the use. As the monomer represented by the above general formula (1), 2-(methacryloyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 3-(methacryloyloxy)propyl 2'-(trimethylammonio)ethyl phosphate, 4-(methacryloyloxy)butyl 2'-(trimethylammonio)ethyl phosphate, 5-(methacryloyloxy)pentyl 2'-(trimethylammonio)ethyl phosphate, 6-(methacryloyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(N-methyl-N,N-diethylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(N,N-dimethylethylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(triethylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(N,N-dimethylpropylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(N,N-dipropyl-N-methylammonio)ethyl phosphate, 2-(methacryloyloxy) ethyl 2'-(tributylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(tricyclohexylammonio)ethyl phosphate, 2-(vinyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(allyloxy) 2'-(trimethylammonio)ethyl phosphate, 2-(p-vinylbenzyl)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(vinylbenzoyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(styryloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(allyloxycarbonyl)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(vinyloxycarbonyl)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(acryloylamino)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(allyloxycarbonylamino)ethyl 2'-(trimethylammonio)ethyl phosphate, (methacryloyloxy)methyloxy 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyloxy 2'-(trimethylammonio)ethyl phosphate, 3-(methacryloyloxy)propyloxy 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)isopropyloxy 2'-(trimethylammonio)ethyl phosphate, and 4-(methacryloyloxy)butyloxy 2'-(trimethylammonio)ethyl phosphate are exemplified. Moreover, 2-(methacryloyloxy)propyl 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)butyl 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)pentyl 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)hexyl 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(triphenylammonio)ethyl phosphate, 2-(methacryloyoxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(vinyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(allyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(p-vinylbenzyl)oxy 2'-(trimethylammonio)ethyl phosphate, 2-(p-vinylbenzoyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(p-vinylbenzyl)ethyl 2'-(trimethylammonio)ethyl phosphate can be exemplified. These compounds can be used alone or two or more to a mixture. The polymers obtained have water solubility and hydrophilic nature. When the polymers are used in the treating solution for contact lenses of the present invention, such compounds adhere or deposit on the surface of contact lenses, and the contact lenses become hydrophilic and prevent stain adhesion. The (meth)acrylates represented by the formula (1) which are characteristically used in the present invention can be synthesized by several kinds of commonly known methods. For example, hydroxyalkyl (meth)acrylate is reacted with 2-chloro-2-oxo-1,3,2,-dioxaphosphorane in the presence of amine, the obtained (2-oxo-1,3,2,-dioxaphosphoroyloxy)alkyl (meth)acrylate is reacted with a certain tertiary amine. In the other method, hydroxyalkyl (meth)acrylate is reacted with 2-bromoethylphosphoryl dichloride, and the obtained (meth)acryloyloxyalkyl 2'-bromoethyl phosphate is reacted with a certain tertiary amine. Before the polymerization, it is desired to purify the products by a known method such as recrystalization. Preparation of the treating solution for contact lenses To prepare the treating solution of contact lenses of the present invention, the polymer used in the treating solution for contact lenses can be obtained by polymerization of (meth)acrylic monomers represented by the formula (1), and also by copolymerization of 1 to 95% by weight of the monomers with 99 to 5% by weight of a copolymerizable monomer. As such copolymerizable vinyl monomers, styrene, methylstyrene, chloromethylstyrene, methyl (meth)acrylate, ethyl (meth)acrylate, n-butyl (meth)acrylate, (meth)acrylic acid, (meth)acrylamide, 2-hydroxyethyl (meth)acrylate, ethyl vinyl ether, n-butyl vinyl ether, N-vinyl pyrrolidone, vinyl chloride, vinylidene chloride, ethylene, propylene, isobutylene, acrylonitrile, or mixtures of these compounds can be exemplified. These monomers are preferably used at a proportion of 10000 to 5 parts by weight per 100 parts by weight of the (meth)acrylate (1). If the monomer is more than 10000 parts by weight, sufficient water solubility and stain resistance given by the (meth)acrylic monomer (1) is not observed. If the monomer is less than 5 parts by weight, the polymerization effects are not observed. The polymers which are characteristically used in the present invention can be obtained by the polymerization or copolymerization of the above monomers. In this case, the polymerization can be effected in the presence of a radical polymerization initiator, by a radical polymerization method such as known block polymerization, suspension polymerization, emulsion polymerization, solution polymerization and the like. As the radical polymerization initiator, benzoyl peroxide, lauroyl peroxide, diisopropyloxy dicarbonate, t-butylperoxy-2-ethylhexanoate, t-butylperoxy pivalate, t-butylperoxydiisobutylate, azobisisobutylonitrile, azobisdimethylvaleronitrile, persulfate, and persulfate-bisulfite types can be used. The usage of the polymerization initiators is usually 0.01 to 10 parts by weight per 100 parts by weight of the total amount of monomers, preferably 0.1 to 5 parts by weight. The polymerization or copolymerization can be conducted by replacing the polymerization atmosphere with an inert gas such as nitrogen, carbon dioxide, helium or the like. The polymerization conditions are preferably a temperature of 30-100°C for 5-72 hours. The molecular weight of the polymer, which is obtained by the radical polymerization and used in the treating solution for contact lenses of the present invention, can be changed by the polymerization temperature, the usage of the initiator and the presence or absence of a polymerization regulator. The number-average molecular weight of the polymer obtained is preferably 1000 to 300,000 and more preferably 2000 to 200,000 in consideration of the solubility in the treating solution, viscosity of the treating solution and adhesion of the solution to contact lenses. As a solvent used in the treating solution for contact lenses of the present invention, it can be used on conditions that the solvent can dissolve the above polymers and is harmless to contact lenses, and it is usable by simple operation such as immersion, washing, or mixing with water. For example, water, methanol, isopropanol, ethylene glycol, polyethylene glycol, glycerine, ethylene glycol monomethyl ether, dimethyl sulfoxide, tetrahydrofuran, acetone and mixtures of these solvents are exemplified. The polymer concentration in the solvent is usually 0.01 to 10 parts by weight. When the polymer concentration is less than 0.01 parts by weight, the solvent insufficently exerts its effect. When contact lenses are treated by the solution, the contact lenses are immersed in the solution or contacted with the solution at a temperature of 20 to 70°C, and then washed with water, physiological saline or a suitable washing liquid before the use. Accordingly, the contact lenses become hydrophilic, and they are prevented from stains of proteins and lipids. The treating solution for contact lenses of the present invention can, if necessary, be used with a surfactant, a germicide, an antiseptic and the like, or it can be used as washing liquid or storage liquid. When the treating solution for contact lenses of the present invention is used, a phospholipid polar polymer adheres to the lenses by simple steps of immersion or coating by the solution and rinsing with water. As a result, the hydrophilic nature and water content of the surface of anhydrous contact lenses or hydrous soft contact lenses are improved and the fitness to eyes is improved. Furthermore, adhesion and deposit of stains such as proteins and lipids can be controlled, so that the denaturation of the lenses can be prevented and the safety to eyes can be improved. The following examples illustrate the present invention more specifically. However, the present invention is not limited by these examples. The contact lenses of Examples 1-10 fall outside the invention as claimed. Highly hydrous soft contact lenses Example 1 Starting monomers as shown in Table 1, namely, 20 parts by weight of 2-(methacryloyloxy)ethyl 2′-(trimethylammonio)ethyl phosphate, 80 parts by weight of 2-hydroxyethyl methacrylate, 2 parts by weight of allyl me thacrylate, 0.2 parts by weight of azobisisobutyronitrile were injected into a test tube-like glass form. After repeating replacement with nitrogen and degassing in the form, the form was sealed and the materials were heated and polymerized. The heat was effected by a rise in temperature of 50-100°C for 50 hours in a thermostat. After finishing the polymerization, transparent colorless polymer was taken out of the form. Obtained polymer was machined by conventional grinding and abrasion to form the desired test film pieces. The following physical properties were evaluated. The results are shown in Table 2. (1) Water content After the product film was immersed in 0.9% by weight of physiologic saline and saturated with the saline, the product film was weighed and the water content was determined by the following equation. Water content (% by weight) = (W 1 -W 2 ) W 1 X 100 W 1 : weight of saturated conditions W 2 : initial weight of a film piece (2) Oxygen permeability Oxygen permeability was determined at 35°C in 0.9% by weight of physiologic saline by using a Seikaken's measuring equipment of film oxygen permeability. (3) Tensile strength The test pieces which were an array type of plates having a constricted center were immersed in 0.9% by weight of physiologic saline at 20°C to be saturated with water, and then these pieces were tested at a stress rate of 60 mm/min. (4) Stain resistance After a contact lens is immersed for two weeks at 35°C in a physiologic saline solution of 0.39% (w/v) of albumin, 0.17% (w/v) of lysozyme and 0.105% (w/v) of γ-globulin, the contact lens was washed with physiologic saline to separate proteins adhered to the contact lens, and a reagent which was quantifiable the proteins was injected into the wash water to determine the amount of the proteins. Examples 2-10 Using the same method as used in Example 1, starting monomers as shown in Table 1 were polymerized and the physical properties were determined. The results are shown in Table 2. Comparison examples 1-3 Using the same method as used in Example 1, starting monomers as shown in Table 1 were polymerized and the physical properties were determined. The results are shown in Table 2. In the table, abbreviations are as follows. HEMA : 2-hydroxymethyl methacrylate METMAEP : 2-(methacryloyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate DEGMA : diethyleneglycol dimethacrylate AMA : allyl methacrylate MMA : methyl methacrylate MPTMAEP : 3-(methacryloyloxy)propyl 2'-(trimethylammonio)ethyl phosphate METEAEP : 2-(methacryloyloxy)ethyl 2'-(triethylammonio)ethyl phosphate NVP : N-vinylpyrrolidone Treating solutions for contact lenses Preparation example 1 Starting monomers, namely 40 parts by weight of 2-(methacryloyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 60 parts by weight of n-butyl methacrylate and 0.1 parts by weight of azobisisobutylonitrile were dissolved in 300 parts by weight of ethanol/tetrahydrofuran (a 50/50 mixture), and the mixture solution was charged into a glass tube. After the atmosphere was replaced with nitrogen, the glass tube was hermetically sealed and heated at a temperature of 60°C for 12 hours in a thermostatic chamber. After polymerization, the product was diluted with 50 ml of ethanol, the solution was added to one liter of diethyl ether to preciptate a polymer. Then, the polymer obtained by suction filtration was dried under reduced pressure at room temperature for 12 hours. The polymer was dissolved in ethylene glycol to prepare a treating solution for contact lenses. Preparation example 2 Using the same method as described in Preparation example 1 except that 40 parts by weight of 2-(methacryloyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate and 60 parts by weight of 2-hydroxyethyl methacrylate as monomers and 300 parts by weight of ethanol as a solvent were used, a treating solution for contact lenses was prepared. Preparation example 3 Using the same method as described in Preparation example 1 except that 90 parts by weight of 2-(methacryloyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate and 10 parts by weight of styrene as monomers and 300 parts by weight of ethanol as a solvent were used, a treating solution for contact lenses was prepared. Example 11 A common contact lens was prepared by the following method. Starting monomers, namely 99 parts by weight of methyl methacrylate, one part by weight of diethyleneglycol dimethacrylate and 0.2 parts by weight of azobisisobutyronitrile were injected into a test tube-like glass form, and the atmosphere was replaced with nitrogen and degassed by repetition. After sealing the form, the compounds were heated at a temperature of 50 to 100°C for 50 hours in a thermostatic chamber. After polymerization, a colorless and transparent polymer was taken out of the form. The polymer obtained was cut and abraded to obtain desired test pieces. The pieces and a holder were immersed in the solution obtained in Reference example 1 which was charged into a stock case for contact lenses. The pieces and the holder were taken out of the case and thoroughly washed with tap water to obtain hydrophilic contact lenses. Then, the following physical properties were determined. The results are shown in Table 3. Example 12 An oxygen-permeable hard contact lens was prepared by the following method. The same procedure as in Example 11 was repeated except that the monomers were changed to 40 parts by weight of tris (trimethylsiloxy)silylpropyl methacrylate, 30 parts by weight of trifluoroethyl methacrylate, 10 parts by weight of methyl methacrylate, 15 parts by weight of triethyleneglycol dimethacrylate and 5 parts by weight of methacrylic acid. The contact lens obtained was subjected to hydrophilicity treatment. Then, the following physical properties were determined. The results are shown in Table 3. Example 13 A soft contact lens was prepared. The same procedure as in Example 11 was repeated except that the monomers were changed to 99 parts by weight of 2-hydroxyethyl methacrylate and one part by weight of ethyleneglycol dimethacrylate. Then, the contact lens obtained was subjected to hydrophilicity treatment. Then, the following physical properties were determined. The results are shown in Table 3. Examples 14-16 Using the same method as used in Example 11, each hydrophilic contact lens was obtained except that the solution of Preparation example 2 was used. Then, the following physical properties were determined. The results are shown in Table 3. Example 17-19 Using the same method as used in Example 11, each hydrophilic contact lens was obtained except that the solution of Preparation example 3 was used. Then, the following physical properties were determined. The results are shown in Table 3. Comparison example 4 Using the same method as used in Example 11, a hydrophilic contact lens was obtained except that an aqueous solution of polyvinyl alcohol (saponification rate : about 88%) was used. Then, the following physical properties were determined. The results are shown in Table 3. Comparison example 5 Using the same contact lens as used in Comparison example 4, except that the contact lens was not treated with polyvinyl alcohol, the physical properties were determined. The results are shown in Table 3. Further, contact angles and stain resistance in the table were determined by the following method. (I) Contact angle After contact lenses were subjected to hydrophilicity treatment and the surface was dried, the contact angle were determined by a water dropping method. (II) Stain resistance After contact lenses were immersed in a physiological saline solution of 0.39% (w/v) of albumin, 0.17% (w/v) of lysozyme and 0.105% (w/v) of γ-globulin at a temperature of 35°C for two weeks, the contact lenses were washed with physiological saline. Proteins sdhered on the contact lenses were peeled off with a surface-active agent, and a reagent for protein determination was injected into the protein solution. Then, the protein adsorption on the surface of the contact lenses was determined.

Claims: A treating solution for contact lenses which comprises 0.01 to 10% by weight of a polymer obtained by polymerisation of one or more monomers according to formula (1) below or by copolymerization of 1 to 95% by weight of the said monomer(s) and 99 to 5% by weight of a copolymerizable monomer, and a solvent which can dissolve the polymer: wherein X is and R 1 is hydrogen or methyl, Y is -CH 2 -, -CH 2 -O-, -CH 2 CH 2 -O-, -CH 2 CH 2 CH 2 -O-, or -CH 2 CH 2 CH 2 CH 2 -O-, n is an integer of 1-20, and, R 2 , R 3 and R 4 are the same or different groups and alkyl or hydroxyalkyl of 1-8 carbon atoms. A treating solution for contact lenses as claimed in claim 1, wherein the monomer represented by the formula (1) is one or more compounds selected from the group consisting of 2-(methacryloyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 3-(methacryloyloxy)propyl 2'-(trimethylammonio)ethyl phosphate, 4-(methacryloyloxy)butyl 2'-(trimethylammonio)ethyl phosphate, 5-(methacryloyloxy)pentyl 2'-(trimethylammonio)ethyl phosphate, 6-(methacryloyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(N-methyl-N,N-diethylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(N,N-dimethylethylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(triethylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(N,N-dimethylpropylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(N,N-dipropyl-N-methylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(tributylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(tricyclohexylammonio)ethyl phosphate, 2-(vinyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(allyloxy) 2'-(trimethylammonio)ethyl phosphate, 2-(p-vinylbenzyl)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(vinylbenzoyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(styryloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(allyloxycarbonyl)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(vinyloxycarbonyl)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-2-(acryloylamino)ethyl )ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(allyloxycarbonylamino)ethyl 2'-(trimethylammonio)ethyl phosphate, (methacryloyloxy)methyloxy 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyloxy 2'-(trimethylammonio)ethyl phosphate, 3-(methacryloyloxy)propyloxy 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)isopro pyloxy 2'-(trimethylammonio)ethyl phosphate, 4-(methacrylloyloxy)buthyloxy 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyeoxy)propyl 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)butyl 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)pentyl 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)hexyl 2'-(trimethylammonio)ethyl phosphate, 2-(methacryloyloxy)ethyl 2'-(triphenylammonio)ethyl phosphate, 2-(methacryloyoxy)ethyl 2'-(trimethylammonio)ethy phosphate, 2-(vinyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(allyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, 2-(p-vinylbenzyl)oxy 2'-(trimethylammonio)ethyl phosphate, 2-(p-vinylbenzoyloxy)ethyl 2'-(trimethylammonio)ethyl phosphate, and 2-(p-vinylbenzyl)ethyl 2'-(trimethylammonio)ethyl phosphate. A treating solution for contact lenses as claimed in claim 1 or 2, wherein the copolymerizable monomer is one or more compounds selected from the group consisting of styrene, methylstyrene, chloromethylstyrene, methyl (meth)acrylate, ethyl (meth)acrylate, n-butyl (meth)acrylate, (meth)acrylic acid, (meth)acrylamide, 2-hydroxyethyl (meth)acrylate, ethyl vinyl ether, n-butyl vinyl ether, N-vinyl pyrrolidone, vinyl chloride, vinylidene chloride, ethylene, propylene, isobutylene, and acrylonitrile. A treating solution for contact lenses as claimed in any of claims 1 to 3, wherein the solvent is one or more compounds selected from the group consisting of water, methanol, isopropanol, ethylene glycol, polyethylene glycol, glycerine, ethylene glycol monomethyl ether, dimethyl sulfoxide, tetrahydrofuran, and acetone.

Inventors: ISHIHARA KAZUHIKO, KOINUMA YASUMI, MATSUMOTO TAKEO, MURATA YOSHISHIGE, NAKABAYASHI NOBUO, NAKADA NOBUHARU, ISHIHARA, KAZUHIKO, KOINUMA, YASUMI, MATSUMOTO, TAKEO, MURATA, YOSHISHIGE, NAKABAYASHI, NOBUO, NAKADA, NOBUHARU
Applicants: NAKABAYASHI NOBUO, NOF CORP, NAKABAYASHI, NOBUO, NOF CORPORATION
Application year: 1992
Main classification: G02B1
IPC codes: G02B1, C08F230, C11D3