Cationic polyurethane compositions, quaternary ammonium salts and methods for their preparation

Abstract: The preparation and use of quarternized bis hydroxy alkyl amines by the reaction of a tertiary amine and an alkylene oxide in a strong acid system are disclosed. Cationic polyurethane compositions containing pendent hydroxy alkyl groups and methods for their preparation are also disclosed, as is also a composition of matter of the formula wherein R and R' are each independently selected from the groups consisting of alkyls having from 1 to about 10 carbon atoms, phenyl, and substituted phenyl groups; R'' is selected from the groups consisting of hydrogen, alkyl having from 1 to about 10 carbon atoms, cycloalkyl having from 5 to 7 carbon atoms in the cycloalkyl group and aryl; R''' is selected from the groups consisting of hydrogen, methyl, ethyl, phenyl, aryl and cyano or nitro substituted alkyl groups; m and n are integers independently selected from 0 to about 15; and X is selected from the ions of an acid having a pK a of less than about 3.

Description: This invention relates to processes for the manufacture of cationic polyurethane compositions and quaternary ammonium salts and to the new compositions prepared thereby. In particular this invention relates to the use of alkylene oxides to prepare cationic polyurethane compositions and quaternary ammonium salt intermediates. An important aspect of the present invention is the use of alkylene oxides such as ethylene oxide and propylene oxide to form cationic ammonium moieties in polyurethanes. It has been known for some time that water dispersible polyurethane compositions can be prepared and used to form films. Various procedures have been disclosed in the literature for making polyurethanes water soluble without diminishing the film forming capabilities of the polyurethanes. US-A-3,470,310 describes the preparation of water dispersions of polyurethanes which contain salt type groups bonded into the polyurethane. US-A-3,873,484 discloses aqueous dispersions of polyurethanes prepared from a quaternized polyurethane prepolymer prepared by reacting from 0.6 to 1.2 equivalents of an alkoxylated diol; one hydroxyl equivalent of an N-alkyl dialkanolamine; about 4 equivalents of an organic diisocyanate and quaternizing with 0.5 equivalents of a dialkyl sulfate quaternizing agent. This quaternized polyetherurethane is chain extended to form a polyurethane-urea and dispersed in water in the presence of a nonionic surfactant belonging to the class of alkoxylated long chain alkyl phenols having an HLB of between about 14 and 16. The use of dialkyl sulfates, such as dimethyl sulfate, and alkyl halides, such as chloroacetoamide, to quaternize tertiary nitrogen atoms is well known. These compositions, however, possess undesirable characteristics limiting their use in the preparation of cationic polyurethanes. Dimethyl sulfate, an often used dialkyl sulfate, is highly toxic and difficult to use on a large scale. Alkyl halides such as chloroacetamide are corrosive and require the use of expensive equipment, such as special types of stainless steel. Therefore a general object of the present invention is to provide a method of making polyurethane latices avoiding these disadvantages of the prior art, and providing polyurethane latices that form stable films. Concerning such compositions, US-A-3873484 has already been referred to. EP-A-165150 shows another quaternized polyurethane latex. US-A-4046725 shows a polyurethane for fixing heparin with a generally similar structure to the present, and suggests that a sulfonate anion may be exchanged onto it. EP-A-433776 forms a polyurethane mass by reacting a foam with isocyanate prepolymer and water, resulting in a polyurethane-coated foam. In contrast, the present invention is concerned to provide a method of making polyurethane latices. In the method, at least one polyol salt of the structure wherein R and R 1 are each independently selected from C 1 -C 10 alkyl, cycloalkyl, phenyl and substituted phenyl; R 2 is selected from hydrogen, C 1 -C 10 alkyl, C 5 -C 7 cycloalkyl and aryl; m and n are integers independently selected from 0 to 15; and X- is HSO 3 , methyl SO 3 , ethyl SO 3 , phenyl SO 3 , aryl SO 3 and substituted alkyl SO 3 , is reacted with excess polyisocyanate and the product chain-extended by use of an active hydrogen-containing compound comprising water (and which may be water), in the presence of a non-ionic surfactant, to remove residual isocyanate functionality. The yield is a stable, film-forming latex dispersion. Example 1 Preparation of a Quaternary Ammonium Salt Dimethylethanolamine (89 grams) was added to water (207 grams) to prepare a 30 weight percent solution. Ethylene oxide (52.8 grams) was added to this aqueous amine mixture in a reaction vessel equipped with dry ice condenser, thermometer and stirrer. This addition caused a 75° C. exotherm. After the mixture was cooled to room temperature, a methane sulfonic acid solution (70%) was added slowly to lower the pH of the reaction mixture to about 5. Mixing was continued for 2 additional hours after completion of the addition of the methane sulfonic acid and then the mixture was cooled to 28° C. The water was removed on a rotovac at 75° C. under reduced pressure. The oily semicrystalline residue was analyzed by nuclear magnetic resonance and found to be substantially N,N-bis(hydroxyethyl) N,N-dimethyl quaternary ammonium methane sulfonate having the structural formula: Also present in the product were minor amounts of quaternary ammonium salt of the formula: wherein x and y are each a number from 0-15. The same preparation was made by an alternate method by first neutralizing the aqueous tertiary amine with the acid followed by the addition of ethylene oxide. In this method, the higher ethoxylated products were kept to a minimum. The reaction product was subjected to NMR analysis. Table 1 summarizes the results of such NMR analysis. Resonance Signal Ratios CH 2 N + /CH 2 O CH 3 N + /CH 2 O CH 3 S/CH 3 N + %PEG RUN 1 0.99 1.4 0.48 3.9 RUN 2 1.01 1.53 0.49 0.3 TV 1.0 1.5 0.5 0.00 These quaternized ammonium salts are particularly useful for the preparation of polyurethanes because they have two active hydrogen atoms which can be readily reacted with isocyanate groups to form a polyurethane. By using the present quaternary ammonium salts, cationic polyurethane compositions can be prepared directly by reaction with a polyisocyanate. Such compositions can be dispersed in water to form stable latices. The organic polyisocyanates that can be used in this reaction can be aliphatic or aromatic polyisocyanates or mixtures thereof. When color stability is important, aliphatic polyisocyanates are preferred. In general, diisocyanates are preferred. Higher polyisocyanates can be used either alone or in combination with diisocyanates. The selection of the isocyanate or mixture of isocyanates will depend upon many factors, particularly the desired properties of the polyurethane and its ultimate use. Among polyisocyanates that can be used are diisocyanates such as 1,4-cyclohexyl diisocyanate, alpha, alpha-xylene diisocyanate, 4,4'-methylene bis(cyclohexylisocyanate), 1,4-tetramethylene diisocyanate, 1,6-hexylmethylene diisocyanate, isophosphorone diisocyanate and the like; and polyisocyanates such as 1,2,4-benzene triisocyanate, polymethylene polyphenylisocyanate, and the like. Also monoisocyanates can be used in combination with the diisocyanates and/or polyisocyanates to reduce the average functionality of the isocyanate component. Examples of useful monoisocyanates are cyclohexyl isocyanate, phenyl isocyanate and toluene isocyanate. By the process of the present invention, a quaternary ammonium salt of a dialkanolamine prepared as shown in Example 1 can be reacted with a diisocyanate and an alkoxylated diol or triol to prepare a cationic polyurethane prepolymer. Example 2 illustrates this reaction. Example 2 The product of Example 1 (47 grams), polypropylene glycol having a molecular weight of about 1000 (296 grams), trimethylolpropane (4.6 grams), Irganox antioxidant (2.8 grams), Tinuvin® 328 U.V. stabilizer (1.45g) and N-methyl pyrrolidone solvent (254 grams) were placed in a reaction vessel. Desmodur W isocyanate (246.1 grams) was added to the reaction vessel and the reaction mixture was heated to 90-100° C. and maintained in that temperature range for several hours. At that time the reaction product was found to have an isocyanate content of 2.95%. Then the prepolymer of Example 2 was formed into a latex by chain extension through reaction of the residual isocyanate groups with water. This chain extension is performed by agitation, adding the polyurethane prepolymer to the water containing a non-ionic surfactant. A semi colloidal dispersion is formed. Alternatively, the prepolymer product obtained by the reaction of excess polyisocyanate and the cationic quaternary ammonium salt (polyurethane prepolymer) can be chain extended with an active-hydrogen containing compound; such as a diamine. Example 3 illustrates the formation of a stable latex from the cationic polyurethane prepolymer of Example 2. Example 3 The prepolymer prepared in Example 2 (400 grams) was added to water (500 grams) containing a non-ionic surfactant (5.0 grams) with rapid agitation to form a semi-colloidal dispersion. This dispersion was continuously mixed for an additional three hours to complete the reaction of the isocyanate groups with water. Mixing was continued until all of the isocyanate groups had been reacted. The resulting latex was found to have properties as follows: Solids 33.2% pH 7.4 Viscosity 110 cps Appearance Semi-clear, off-white Film's tensile strength about 22.75 MPa (3300 psi) Film's elongation about 460% In accordance with the present invention, polyurethane prepolymers can be prepared containing other desired moieties. For instance, in accordance with the present invention, a polyester reactant containing a sufficient excess of active hydrogen atoms can be used in the reaction process of Example 2 to prepare a cationic polyurethane containing polyester moieties. Example 4 demonstrates the preparation of a polyurethane containing polyester moieties rather than the polyether moieties of the polypropylene glycol reactant used in Example 2. Example 4 Witco Corporation's Formrez® 55-112 brand, neopentyl adipate polyester polyol (prepared from neopentylalcohol and adipic acid) having a hydroxyl number of about 112 (296 grams); N,N-dimethyl (N,N-bishydroxyethyl) quaternary ammonium methane sulfonate (47 grams); trimethyl propane (4.6 grams); Irganox 1010 antioxidant (2.8 grams); Tinuvin® 328 U.V. stabilizer (1.45 grams); and Desmodur W diisocyanate (246 grams) were charged to a resin kettle. The mixture was heated and held at 95-100° for three hours. Propylene carbonate solvent (254 grams) was then added and the reaction mixture was then heated for an additional 1.75 hours. Analysis of a sample showed 3.68% isocyanate (theoretical 3.8%). Then the prepolymer was cooled to 45°C and 800 grams of the prepolymer were added to water (1,000 grams) at 20°C containing as surfactant GAF's Igepal® CO-730 nonyl phenol ethoxylate (10 grams). This addition was carried out a high rate of shearing and mixing. Mixing was continued until the terminal isocyanate group of the prepolymer were completely reacted with water and the polymer was fully extended to its optimum molecular weight. The final latex was colloidal and had the following properties: pH - 7.4 Viscosity (Brookfield) - 50 cps Solids - 31.7% A film was prepared with the aid of a wetting agent and had the following properties: Tensile Strength - about 47.1 MPa (6830 psi) Ultimate Elongation - 380% Examples of alkoxylated diols useful in the preparation of the prepolymer are polyoxyethylene and polyoxypropylene glycol, and/or an alkoxylated triol, such as polypropoxylated trimethyl propane and polypropoxylated glycerol. The presence of a triol is desirable to allow branching of the prepolymer to increase toughness of the film produced by the polyurethane product. Examples of N-alkyl dialkanolamines useful in the preparation of the polyurethane prepolymer are N-methyldiethanolamine, N-methyl dipropanolamine, N-methyl diisopropanolamine, etc. For most purposes, the N-alkyl and N-alkanol groups can have up to 10 carbon atoms. The diisocyanate will be selected based on the desired final properties of the polyurethane. This component can be aromatic, such as toluene diisocyanate, diphenylmethane diisocyanate, xylene diisocyanate, etc. It can also be an aliphatic or cycloaliphatic such as 1,6-hexamethylene diisocyanate, 4,5'-dicyclohexylmethyl diisocyanate, isophorone diisocyanate, etc. Patents disclosing the preparation of the polyurethane prepolymers are US-A-3,874,484 to Bhrestein et al; US-A-3,388,087 and 3,479,310 to Dietrich; US-A-3,410,817 to McClellan; US-A-3,565,844 to Grace et al and US-A-4,147,679 to Scriven et al. It should be noted that the cationic polyurethane prepolymer, regardless of its method of preparation, can be chain extended by reaction with an active hydrogen containing compound, particularly an amine or water. This chain extension can be performed in sufficient water to complete the chain extension. An amine catalyst, such as triethylene diamine may be added to accelerate the chain extension. Dispersions of the quaternized polyurethane prepolymer can be made with the use of a suitable surfactant. Suitable surfactants include ethoxylated octyl phenol, ethoxylated nonyl phenol, ethoxylated dodecyl phenol, ethoxylated fatty alcohols and the like. These types of surfactants are made and sold by Witco Corporation, such as under its trademark, "WITCONOL," and by other manufacturers. A dispersion containing 30-65 weight percent of the chain extended polyurethane is within the present invention. The latex obtained from the present cationic quaternized polyurethane is stable at room temperature and makes excellent films. The present invention also provides radiation curable cationic polyurethane dispersions. Example 5 illustrates the preparation of a radiation curable water-borne cationic polyurethane dispersion in accordance with the present invention. Example 5 To a clean and dry resin kettle polypropylene glycol having a molecular weight of about 1000 (250 grams, 0.50 equiv.) is charged and heated to 85°C (185 degrees F). A vacuum is applied for 1/2 hour to remove moisture from the polyol and the kettle is then blanketed with nitrogen to prevent moisture from reentering the reactor. Trimethylol propane (3.9 grams, 0.088 equiv.), N,N-bishydroxyethyl-N,N-dimethyl quaternary ammonium methane sulfonate (40 grams, 0.35 equiv.) (see Example 1), and dry N-methyl pyrrolidone (160 grams) are added to the kettle. The reaction mixture should be cooled to about 43.3°C (110 degrees F). The kettle is purged with dry air and glycerol monoallyl ether (9.9 grams, 0.15 equiv.) is added to the kettle and the components are mixed well. While purging with air and mixing, Desmodur W. diisocyanate (286 grams, 2.18 equiv.) and about 20 to 30 drops of dibutyl tin dilaurate catalyst are added to the kettle. The reactor is reheated to 71.1-82.2°C (160-180 degrees F) for 2-3 hours and the reaction mixture is analyzed for per cent NCO using standard analytical methods. When the per cent NCO is equal to or slightly below the theoretical value, hydroxy propyl acrylate (143 grams, 1.1 equiv.) and phenothiazine (90.06 grams, 75 ppm) are added and the mixture is heated and mixed under dry air until the NCO groups are substantially reacted. When the NCO groups are substantially reacted, the prepolymer is added with vigorous agitation to about 2000 grams of cold water containing 0.5 per cent p-nonylphenol ethoxylate surfactant such as Witco Chemical Corporation's Witconol NP150 surfactant. Agitation is continued for at least one hour. The resulting product is a stable latex containing polymerizable unsaturated groups. The latex of Example 5 can be prepared for radiation curing by adding with vigorous agitation 300 grams of the latex to 0.5 parts of benzophenone, 0.1 parts of Ionol, 1.0 parts of an additive such as Union carbide's Silwet L-7002 nonionic silicone glycol copolymer surfactant and optionally 10-20 parts of an ethylenically unsaturated monomer such as hexane diacrylate. A film can be drawn down by standard methods and dried so it will have 3 mils or less thickness. The film can be radiation cured by standard techniques such as by subjecting the film to about 300 m watts sec cm-2 for a sufficent time to yield a coating of good properties. The cationic polyurethane compositions of the present invention have many valuable uses. For instance, aqueous dispersion or latex products of this invention are advantageously employed as coating compositions, for which purpose they may be further diluted with water and/or organic solvents, or they may be supplied in more concentrated form by evaporation of water and/or organic components of the liquid medium. As coating compositions they may be applied to any substrate including wood, metals, glass, cloth, plastics, foamed plastics and the like, by any conventional method including brushing, dipping, flow coating, spraying, and the like. The compositions may contain other conventional ingredients including organic solvents, pigments, dyes, emulsifiers/surfactants, thickeners, heat stabilisers, levelling agents/anticratering agents, fillers, sedimentation inhibitors, UV absorbers, antioxidants and the like introduced at any stage of the production process. These latices are preferably applied to substrates in effective film-forming amounts depending on the solids content of the latex, temperature and other conditions, the type of substrate, product desired, etc. The film coating on the substrate may simply be protective, decorative, or the like or serve as an adhesive or other function. Self-supporting thin or thick films or sheets may be produced by applying the latex to a substrate with a release surface from which the cured, hardened film can be removed. Hardening and curing on the substrate is generally accomplished by simply drying under ambient conditions, which may if desired be expedited and/or facilitated by concurrent heating, subsequent baking, etc. The latices of this invention have good storage-stability and yield films and coatings with improved properties such as resistance to water, organic solvents and environmental conditions; flexibility; elasticity and/or tensile strength; and the like.

Claims: A film forming polyurethane latex substantially free of isocyanate residual functionality comprising a dispersion of chain extended isocyanate terminated polyurethane, the latex being formed by the process comprising (1) reacting a polyol with excess polyisocyanate (2) chain extending the product of step (1) in the presence of a non-ionic surfactant and an active hydrogen-containing compound comprising water until removal of any residual isocyanate functionality is substantially complete and a stable latex is formed, wherein said polyol comprises at least one polyol salt having the structure wherein R and R 1 are each independently selected from C 1 -C 10 alkyl, cycloalkyl, phenyl and substituted phenyl; R 2 is selected from hydrogen, C 1 -C 10 alkyl, C 5 -C 7 cycloalkyl and aryl; m and n are integers independently selected from 0 to 15; and X - is HSO 3 , methyl SO 3 , ethyl SO 3 , phenyl SO 3 , aryl SO 3 , and substituted alkyl SO 3 . The film forming polyurethane latex of claim 1, wherein the polyisocyanate is a diisocyanate. The film forming polyurethane latex of claim 1 or claim 2, wherein said polyol in step (1) also contains an alkoxylated diol. The film forming polyurethane latex of claim 1, wherein said polyol in step (1) also contains a hydroxy terminated polyester. The film forming polyurethane latex of claim 3 or claim 5, wherein said polyol in step (1) also contains a 1,1,1-trimethylol-propane. The film forming polyurethane latex of any one of the preceding claims wherein the active hydrogen-containing compound is water. The film forming polyurethane latex of claim 6, wherein the polyol salt in step 1 comprises:

Inventors: BARANOWSKI THOMAS R, BECHARA IBRAHAM, BARANOWSKI, THOMAS R., BECHARA, IBRAHAM
Applicants: WITCO CORP, WITCO CORPORATION
Application year: 1992
Main classification: C07C215
IPC codes: C08G18, C07C217, C07C215, C08G65, C08L71