Liquid crystal display device

Abstract: A liquid crystal display device includes a pair of opposed insulating substrates (50a, 50b) and a liquid crystal layer (51) sandwiched therebetween. One of the insulating substrates (50a) is formed with a first trench (105) for forming a thin film transistor (103) therein and a second trench (112) for forming a capacitor element (104) therein. The thin film transistor is constituted of a semiconductor layer (106) formed along an inner surface of the first trench, a gate insulating layer (107) formed on the semiconductor layer, and a gate electrode (108) formed on the gate insulating layer. The capacitor element (104) is constituted of a first electrode (113) formed along an inner surface of the second trench, a dielectric layer (114) formed on the first electrode, and a second electrode (115) formed on the dielectric layer. The first electrode (113) is formed integrally with the semiconductor layer (107), thereby increasing the aperture ratio. The first trench (105) has a tapering side surface, thereby assisting uniform ion implantation for the semiconductor layer (107). In the case that the substrate has a laminated structure of an insulating substrate (308) and an insulating layer (309), the etching rate of the substrate as a whole can be improved.

Description: The present invention relates to a liquid crystal display device of an active matrix type, and more particularly to a structure of a driving substrate. In Japanese Published Patent Application 01/81262, there is disclosed an active matrix substrate having a large capacitor in a liquid crystal picture element section without reducing aperture ratio. Figure 39 shows a structure of such a capacitor for a thin film transistor (TFT) formed on the active matrix substrate. Referring to Figure 39, a recess (trench) 2 is formed on a quartz substrate 1. A first polysilicon layer 3 is formed on an inner surface of the trench 2, and a second polysilicon layer 6 is formed so as to be opposed to the first polysilicon layer 3 with a silicon oxide insulating film 4a and a silicon nitride insulating film 5a sandwiched therebetween, thus forming the capacitor (trench capacitor). A third polysilicon layer 7 is formed as a semiconductor layer of the TFT on the quartz substrate 1, and a fourth polysilicon gate electrode 8 is formed on top of the semiconductor layer 7 separated by a silicon oxide gate insulating film 4b and a silicon nitride gate insulating film 5b. The TFT further includes an indium tin oxide (ITO) electrode 9 and an aluminium or silicon electrode 10. Reference numerals 11,12 and 13 designate a first interlayer insulating film, a second interlayer insulating film and a passivation film, respectively. In the above structure, the first polysilicon layer 3 of the trench capacitor is formed non-integrally with the third polysilicon layer 7 of the TFT, but it is necessary to form a contact portion for connecting the first polysilicon layer 3 to the third polysilicon layer 7 as shown by a width W in Figure 39. Accordingly, an occupied area W 2 of the contact portion is necessary. Actually, the width W is about 5µm, and accordingly the occupied area W 2 becomes about 25µm 2 . As a result, the aperture ratio is reduced. Further, the contact portion for connecting the capacitor and the TFT is prone to having a multilayer structure with many steps thereby causing disconnection of aluminium wiring or the like. Figure 40 shows a general equivalent circuit of an active matrix type liquid crystal display device. As shown in Figure 40, m gate lines G 1 to G m ) and n source lines (S 1 to S n ) are so arranged as to intersect each other at right angles. At each intersection of the gate lines and the source lines, there are formed a thin film transistor (MOS-FET) 201, a charge storing capacitor 202 as a capacitor element, and a liquid crystal cell 203 constituting a picture element. The active matrix type liquid crystal display device having such a structure is driven in the following manner. A scanning signal having a pulse width set to one horizontal scanning period is sequentially applied to the gate lines G 1 to G m . During the period of selection of one gate line, a sampled display signal is sequentially held in the source lines S 1 to S n . Immediately thereafter, the display signal is written to the corresponding picture element. The display signal written into the picture element is held for one field period by the liquid crystal cell 203 and the capacitor 202, and it is then rewritten to a signal reversed in polarity in the next field. Thus, alternating current drive of the liquid crystal is effected. The larger the picture element capacitance of each liquid crystal cell 203, the more securely a picture element potential can be held, so that non-uniformity of contrast can be suppressed to thereby secure a fixed display quality. Accordingly, in the case that the picture element electrode area is large (for example, 200 2 µm 2 or more), it is unnecessary to provide the capacitor element 202. However, in the case that a picture element is made fine or very fine in a small-sized display device, the picture element electrode area becomes small (for example, 100 2 µm 2 or less), and a capacitor element is therefore needed to supplement the picture element capacitance. In general, the capacitor element 202 is required to have a capacitance about five times the picture element capacitance in order to ensure stable sampling and holding of the display signal. Generally, the capacitor element 202 has a MOS structure, and it is formed on a flat surface of a substrate. To increase capacitance, it is necessary to enlarge electrode area. Accordingly, in the case that the picture element is made fine, the area occupation ratio of the capacitor electrode is increased thereby causing a reduction in aperture ratio (i.e., a ratio of picture element electrode area to display area). Particularly in the case that the picture element electrode area is 50 2 µm 2 or less, the aperture ratio is greatly reduced. As a measure against the above problem, it is known to use a so-called trench type capacitor element as disclosed in Japanese Published Patent Application 1/81262. Figure 41 shows the structure of such a trench type capacitor element in section. As shown in Figure 41, a recess or trench 205 is formed on an upper surface of a quartz substrate 204. A laminated structure consisting of a first electrode film 206, a dielectric film 207 and a second electrode film 208 is formed on an inner wall of the trench 205 to constitute a so-called trench capacitor element 209. As apparent from the drawing, the effective area of the electrode films 206 and 208 is larger that the plane opening area of the trench 205, and capacitance can therefore be increased without enlarging the size of the capacitor element. Accordingly, the use of the trench capacitor element 209 can reduce the area occupation ratio of the capacitor electrode and thereby achieve a desired aperture ratio, even in the case of a very fine picture element. A planar thin film transistor 210 is also formed on a flat upper surface of the substrate 204. That is, a polycrystal silicon thin film 211 constituting a semiconductor region of the transistor 210 is formed on the substrate 204. Two layers of gate insulating films 212 and 213 are formed on the semiconductor region 210, and a gate electrode 214 is formed on the two layers. A picture element electrode 216 is electrically connected through an interlayer insulating film 215 to a drain region of the transistor 210, and an electrode 217 connected to a source line is electrically connected through the interlayer insulating film 215 to a source region of the transistor 210. These laminated structures are covered with a passivation film 218. According to a first aspect of the invention, there is provided a liquid crystal display device comprising a substrate having a plurality of trenches; and a plurality of display elements arranged in a matrix form on the substrate, each of the display elements comprising a picture element electrode, a switching transistor associated with the picture element electrode, and a capacitor element formed in one of said plurality of trenches and associated with the picture element electrode; the capacitor element comprising a first electrode formed integrally with a semiconductor layer of the switching transistor, the first electrode being formed along an inner surface of said one of said plurality of trenches; a dielectric layer formed on the first electrode; and a second electrode opposed to the first electrode through the dielectric layer. It is preferable that the dielectric layer is formed of the same material as that of a gate insulating layer of the switching transistor. It is preferable that the second electrode is formed of the same material as that of a gate electrode of the switching transistor. It is preferable that said plurality of trenches have tapered side walls. With the above preferred construction of the first aspect, the capacitor element is formed in the trench formed in the insulating substrate. Furthermore, the capacitor element comprises the first electrode formed integrally with the semiconductor layer of the thin film transistor in the same step, the second electrode formed of the same material as that of the gate electrode of the thin film transistor, and the dielectric layer sandwiched between the first electrode and the second electrode and formed of the same material as that of the gate insulating layer of the thin film transistor. Accordingly, it is unnecessary to form a contact for connecting the first electrode of the capacitor element to the semiconductor layer of the thin film transistor, a connecting electrode therefor, and an interlayer insulating film in the vicinity thereof, thereby reducing the area occupied for forming such a contact and its associated portions. Further, a step portion on the substrate can be reduced to thereby improve the reliability of wiring formation. According to a second aspect of the invention, there is provided a liquid crystal display device comprising a substrate having a plurality of first trenches; and a plurality of display elements arranged in a matrix form, each of the display elements comprising a picture element electrode, a thin film transistor formed in one of said plurality of first trenches and associated with the picture element electrode, and a capacitor element associated with the picture element electrode. It is preferable that said plurality of first trenches have tapered side walls. It is preferable that the thin film transistor comprises a semiconductor layer formed along an inner surface of one of said plurality of first trenches, a gate insulating layer formed on the semiconductor layer, and a gate electrode formed on the gate insulating layer so as to fill said one of said plurality of first trenches. It is preferable that each of said plurality of first trenches has a structure satisfying the relation of: 0 < tan  ≤ a/2b wherein a represents a width of the first trench; b represents a depth of the first trench; and  represents a tapered angle of the first trench. It is preferable that the substrate has a plurality of second trenches, and the capacitor element is formed in one of said plurality of second trenches. It is preferable that the substrate has a plurality of second trenches formed simultaneous with said plurality of first trenches, the capacitor element being formed in one of said plurality of second trenches. It is preferable that the capacitor element comprises a first electrode formed along an inner surface of one of said plurality of second trenches, a dielectric layer formed of the same material as that of the gate insulating layer, and a second electrode opposed to the first electrode through the dielectric layer. It is preferable that the first electrode is formed of the same material as that of the semiconductor layer, and the second electrode is formed of the same material as that of the gate electrode. It is preferable that the substrate comprises an insulating substrate and an insulating layer formed on the insulating substrate. It is preferable that said plurality of second trenches have tapered side walls. It is preferable that the semiconductor layer is formed of doped polysilicon. It is preferable that the first electrode is formed of doped polysilicon. It is preferable that the polysilicon is doped with a cation selected from the group consisting of Si + , B + , As + and P + . It is preferable that doping of the cation is performed by ion implantation. With the above preferred construction of the second aspect, the thin film transistor and/or the capacitor element are/is formed in the first tapering trench and/or the second tapering trench. In a first step, a first polysilicon film constituting the semiconductor layer of the transistor and the first electrode of the capacitor element is formed along the tapering inner surfaces of the trenches. Thereafter, in performing a solid-phase growth process for the first polysilicon film, silicon ions (Si + ) can be uniformly implanted since the first polysilicon film is substantially completely exposed to the incident direction of the silicon ions. As a result, the solid-phase growth is uniformly performed to obtain a semiconductor layer having a composition close to that of single crystal silicon even on the side walls of the trench. Thus, the electric characteristics of the transistor and/or the capacitor element can be improved. In addition, since the first polysilicon film is formed along the tapering surface, the step coverage can be improved to thereby effectively prevent problems such as disconnection. Further, with the above preferred construction, the substrate has a two-layer structure consisting of the insulating substrate, such as a quartz substrate, and the insulating film, such as a silicon nitride film, having an etching rate higher than that of the quartz substrate, thereby masking the etching rate of the substrate as a whole higher than that of the prior art substrate so that a trench having the required depth can be formed in one step, thereby improving the throughput. Even in the case of anisotropic etching, the trench having a desired tapering shape can be obtained because of a relatively high etching rate, thereby improving the step coverage. Accordingly, problems such as disconnection can be reduced to thereby improve the yield. Embodiments of the invention will now be described, by way of example only, with reference to the accompanying drawings in which: Figure 1 is a sectional view of a thin film transistor (TFT) and a capacitor element therefor in a liquid crystal display device according to a first preferred embodiment of the invention; Figure 2 is a sectional view of a panel portion of the liquid crystal display device; Figure 3 is a perspective view showing a shape of a trench according to the first preferred embodiment by way of example; Figures 4 to 20 are sectional views illustrating the steps of a manufacturing process for the liquid crystal display device according to the first preferred embodiment; Figure 21 is a schematic sectional view, partially cut away, showing a basic construction of a driving substrate employed in a liquid crystal display device according to a second preferred embodiment of the present invention; Figure 22 is a schematic sectional view illustrating the operation of the second preferred embodiment; Figure 23 is a flow diagram illustrating the steps of forming tapering trenches and a first polysilicon film on the driving substrate according to the second preferred embodiment; Figure 24 is a flow diagram illustrating the steps of forming a gate insulating film as continued from Figure 23; Figure 25 is a flow diagram illustrating the steps of forming a second polysilicon film and patterning the same as continued from Figure 24; Figure 26 is a flow diagram illustrating the steps of forming a source region and a drain region of a thin film transistor as continued from Figure 25; Figure 27 is a flow diagram illustrating the steps of forming a wiring electrode as continued from Figure 26; Figure 28 is a flow diagram illustrating the steps of diffusing hydrogen to the first polysilicon film as continued from Figure 27; Figure 29 is a flow diagram illustrating the steps of forming a picture element electrode as continued from Figure 28; Figure 30 is a schematic sectional view, partially cut away, showing a basic construction of a liquid crystal display device according to a third preferred embodiment of the present invention; Figure 31 is a schematic sectional view illustrating the operation of the third preferred embodiment; Figure 32 is a flow diagram illustrating the steps of forming trenches on a driving substrate of the liquid crystal display device according to the third preferred embodiment; Figure 33 is a flow diagram illustrating the steps of forming a gate insulating film as continued from Figure 32; Figure 34 is a flow diagram illustrating the steps of forming a gate electrode as continued from Figure 33; Figure 35 is a flow diagram illustrating the steps of forming a source region and a drain region as continued from Figure 34; Figure 36 is a flow diagram illustrating the steps of forming a wiring electrode as continued from Figure 35; Figure 37 is a flow diagram illustrating the steps of diffusing hydrogen to a semiconductor layer as continued from Figure 36; Figure 38 is a flow diagram illustrating the steps of forming a picture element electrode as continued from Figure 37; Figure 39 is a sectional view of a thin film transistor and a capacitor element therefor in a liquid crystal display device in the prior art; Figure 40 is a circuit diagram showing a general equivalent circuit of an active matrix type liquid crystal display device; Figure 41 is a schematic sectional view, partially cut away, showing a construction of a driving substrate in the prior art; Figure 42 is a schematic sectional view, partially cut away, showing a construction of a driving substrate having a trench type thin film transistor and a trench type capacitor element; Figure 43 is a schematic sectional view illustrating a problem in the construction shown in Figure 42; and Figure 44 is a schematic sectional view illustrating the steps of forming a trench in the prior art. In the structure shown in Figure 41, the capacitor element 202 is formed as a trench structure in order to reduce its plane size. However, the thin film transistor is of a planar type and the aperture ratio of the picture element may be further improved by reducing a plane size of the transistor element. From this viewpoint, the present applicant has proposed that not only the capacitor element but also the thin film transistor is formed in a trench structure. Figure 42 schematically shows such a trench structure in cross section. As shown in Figure 42, a thin film transistor 220 is formed by utilizing a trench 221. On an inner wall surface of the trench 221, there are formed a first polysilicon layer 222 constituting a semiconductor region, a gate insulating film 223, and a second polysilicon layer 224 constituting a gate electrode in such a manner as to fill the trench 221. A leading electrode 226 is connected to a source line. Further, a picture element electrode 227 is connected through the first interlayer insulating film 225 to a drain region of the transistor 220. An upper surface of the transistor 220 is covered with a second interlayer insulating film 228. Similarly, a capacitor element 230 has a trench structure. That is, the first polysilicon layer 222 constituting a first electrode, the dielectric or insulating film 223 and the second polysilicon layer 224 as a second electrode are formed on an inner wall surface of a trench 231. Further, the first interlayer insulating film 225 and the second interlayer insulating film 228 are laminated on the trench structure of the capacitor element. The trench structure of the thin film transistor 220 enables a plane size of the transistor, especially the gate length thereof, to be reduced. Accordingly, the fineness of a thin film transistor can be improved to achieve a small size of not only transistors for switching a picture elements but also of transistors to be used in peripheral circuits, thereby effecting high integration of a shift register or the like. Further, as an effective three-dimensional gate length along the inner wall of the trench can be set to an ordinary size, an ordinary supply voltage level can be used. Further, while apparent two-dimensional gate length is reduced, no measures against a so-called short channel effect or the like are necessary because the actual three-dimensional gate length can be set to the ordinary size. In addition, as the upper surface of the trench element is superior in flatness, rubbing for control of liquid crystal molecule orientation can be more uniformly performed. Accordingly, a region where the trench element is formed need not be shielded especially by a black mask or the like, but can be utilized as an aperture. Figure 43 is an enlarged sectional view showing a shape of the trench 221 for forming the thin film transistor 220 shown in Figure 42. In general, the trench 221 has vertical side walls. the first polysilicon layer 222 is so deposited as to continuously cover an upper surface of a substrate 240, the vertical side walls of the trench 221 and a bottom surface of the trench 221. Since the first polysilicon layer 222 is used as the semiconductor region of the transistor 220, a solid-phase growth process for increasing polysilicon crystal grain size is used. If the solid-phase growth process is not performed, then desired current drive characteristics to be demanded of the transistor may not be obtained leading to variations in Ion/Ioff characteristic and Vth characteristic, for example. In performing the solid-phase growth process, silicon ions (Si + ) are implanted into an upper surface of the first polysilicon layer 222 prior to heating. However, as ion implantation of the silicon ions has anisotropy, a portion of the first polysilicon layer 222 deposited on the vertical side walls of the trench 221 becomes a shadow portion 241 in the process of ion implantation causing non-uniformity of the solid-phase growth. In addition, a so-called step coverage at perpendicular step portions 242 may be sufficiently bad so as to cause frequent disconnection of the first polysilicon layer 222. In the structure shown in Figure 41, the trench 205 is formed on the upper surface of the insulating substrate 204 which is formed of quartz or the like. In general, the formation of the trench 205 is effected by utilizing plasma etching or the like. Figure 44 shows a process of forming such a trench. As shown in Figure 44, a patterned resist 419 is first formed on an upper surface of a quartz insulating substrate 404, and then reactive plasma is irradiated through an opening 420 of the resist 419 to the substrate 404, thereby partially removing the quartz to form a trench 405. In general, the trench 405 is required to have a depth of about 3 µm, so as to form a capacitor element therein. However, a selection ratio of the resist 419 to the insulating substrate 404 in the etching process (i.e., a ratio of an etching rate of the insulating substrate 404 to an etching rate of the resist 419) cannot be made high. That is, the insulating substrate 404 formed of quartz has a dense fine structure, and the resist 419 formed of an quartz has a dense fine structure, and the resist 419 formed of an organic material has a structure not durable against a long-term etching process. For example, at the time the insulating substrate 404 is etched to a depth of above 1 µm, the resist 419 is entirely etched off. Accordingly, in order to obtain a target trench depth of 3 µm, the formation of the resist 419 and the etching process must be repeated and this reduces production efficiency. Figure 1 is a schematic sectional view of a thin film transistor (TFT) and a capacitor element therefor in a liquid crystal display device according to a first preferred embodiment of the invention. As shown in Figure 1, a recess (trench) 22 is formed on a quartz substrate 21, and a capacitor element (trench capacitor) is formed in the trench 22 by sandwiching a silicon nitride insulating film 25a and a silicon oxide insulating film 24a between a first polysilicon layer 23 as a first electrode and a second polysilicon layer 26a as a second electrode. Furthermore, a thin film transistor (TFT) is constructed of the first polysilicon layer 23 as a semiconductor layer, a silicon nitride gate insulating film 25b, a silicon oxide gate insulating film 24b, a second polysilicon gate electrode 26b, and ITO electrode, and an aluminium or silicon electrode 30. That is, the capacitor element is formed in the trench 22, and the semiconductor layer of the TFT and the first electrode of the capacitor element are formed of the first polysilicon layer 23 integrally formed in the same step. In contrast with the structure shown in Figure 39, it will be appreciated that the contact portion having the width W shown in Figure 39 is eliminated. The sectional view shown in Figure 1 corresponds to an enlarged view of a part including a lower quartz substrate 50b and picture element electrodes (TFT array) 53 of the liquid crystal display device shown in Figure 2. That is, Figure 2 is a sectional view of a part of an LCD panel having the structure shown in Figure 1. As shown in Figure 2, an upper quartz substrate 50a is opposed to the lower quartz substrate 50b, and a liquid crystal layer 51 is sandwiched between both the substrates 50a and 50b. The picture element electrodes 53 are arranged in the form of a matrix on the lower quartz substrate 50b, and the TFT (not shown) connected to each picture element electrode 53 is also provided on the substrate 50b. Red, green and blue colour filters 54 and a common electrode 52 connected thereto are provided on the upper quartz substrate 50a. Reference numeral 55 denotes a spacer for defining a uniform space for sealing the liquid crystal layer 51, and reference numeral 56 denotes a polarizing plate for controlling light. According to the trench structure of the first preferred embodiment, an aperture ratio of the LCD panel can be improved over the prior art. An example thereof will now be described. It is assumed that the capacitor element has the following conditions. Thickness of silicon oxide insulating film: 60 nm Thickness of silicon nitride insulating film: 15 nm Capacitance Ci per unit area (cm 2 ): 5.21x10 -8 F/cm 2 Capacitance Ct: 1.2x10 -13 F. Letting S' denote a surface area of the capacitor element, the following equation is given: Ct = CixS' 1.2x10 -13 = 5.21x10 -8 xS' S' = 2.3x10 -6 cm 2 = 230µm 2 . Figure 3 shows an example of a trench for the capacitor element. The trench has a length of 3µm, a width of 8.5µm, and a depth of 10µm. This trench corresponds to the trench 22 shown in Figure 1. An occupied area of the capacitor element to be formed in this trench on the upper surface is 3µmx8.5µm = 25.5µm 2 . In the above conditions, an aperture ratio of a liquid crystal view finder having 77,000 picture elements in the prior art and according to the first preferred embodiment of the present invention will be calculated as follows: Total area of one picture element: 42x48µm 2 ITO display area: 784µm 2 . Accordingly, the aperture ratio in the prior art is: 784µm 2 /(42x48)µm 2 = 0.388 = 38.8%. In contrast, according to the first preferred embodiment of the present invention, the contact portion between the capacitor element and the TFT portion is eliminated as mentioned above. Accordingly, the occupied area of the contact portion, that is, 5µmx5µm = 25µm 2 as shown in Figure 39 is added to the ITO display area, and a total ITO display area therefore becomes 784µm 2 +25µm 2 = 809µm 2 . Accordingly, the aperture ratio in the first preferred embodiment of the present invention is: 809µm 2 /(42x48)µm 2 = 0.401 = 40.1% The above results in the prior art and the first preferred embodiment of the present invention are summarized in Table 1 as follows: Prior Art First Preferred Embodiment ITO display area 784µm 2 809µm 2 Aperture ratio 38.8% 40.1% Now, a manufacturing process for the TFT having the trench capacitor according to the first preferred embodiment will be described with reference to the flow diagrams shown in Figures 4 to 20. First, as shown in Figure 4, the trench 22 is formed on an upper surface of the quartz substrate 21 by wet etching using a mixed solution of HF:NH 4 F = 1:6. As shown in Figure 5, the first polysilicon layer 23 having a thickness of 80 nm is formed on the upper surface of the quartz substrate 21 including an inner surface of the trench 22, by low-pressure chemical vapour deposition (LPCVD). Then, silicon ions (Si + ) are implanted into the first polysilicon layer 23 first under the conditions of an acceleration energy of 30 keV and a dose of 1x10 15 /cm 2 and secondly under the conditions of an acceleration energy of 50 keV and a dose of 1x10 15 /cm 2 . Then, solid-phase annealing is performed at a temperature of 620°C. Thereafter, as shown in Figure 6, the first polysilicon layer 23 is partially removed by etching. This first polysilicon layer 23 will finally become the semiconductor layer of the TFT and the first electrode of the capacitor element. As shown in Figure 7, a silicon oxide film 24 having a thickness of 50 nm is formed on the first polysilicon layer 23 by thermal oxidation at about 1000°C. As shown in Figure 8, a resist 40 is mounted on the silicon oxide film 24 at a TFT forming portion, and arsenic ions (As + ) are implanted into a trench capacitor portion under the conditions of an acceleration energy of 30 keV and a dose of 5x10 14 /cm 2 . After removing the resist 40, a silicon nitride film 25 having a thickness of 30 nm is formed on the silicon oxide film 24 by LPCVD as shown in Figure 9. Then, as shown in Figure 10, a second polysilicon layer 26 having a thickness of 350 nm is formed on the whole upper surface of the work. Thereafter, a reduction in resistivity of the second polysilicon layer 26 is performed by using phosphosilicate glass (PSG). Then, as shown in Figure 11, the second polysilicon layer 26 and the silicon nitride film 25 are patterned by plasma etching using a mixed gas of CF 4 :O 2 = 95:5 to form the second polysilicon gate electrode 26b for the TFT and the second polysilicon layer 26a for the capacitor element, and simultaneously form the silicon nitride gate insulating layer 25b under the second polysilicon gate electrode 26b and the silicon nitride insulating film 25a under the second polysilicon layer 26a. Thereafter, arsenic ions (As + ) are implanted through the silicon oxide film 24 into the first polysilicon layer 23 under the conditions of an acceleration energy of 160 keV and a dose of 1x10 13 /cm 2 to form a lightly doped drain (LDD) in the TFT forming portion. Then, as shown in Figure 12, a resist 41 is mounted so as to cover the second polysilicon gate electrode 26b, and arsenic ions (As + ) are implanted under the conditions of an acceleration energy of 140 keV and a dose of 2x10 15 /cm 2 to form an N-channel. After removing the resist 41, as shown in Figure 13, a resist 42 is mounted on the whole upper surface of the work, and boron ions (B + ) are implanted under the conditions of an acceleration energy of 30 keV and a dose of 2x10 15 /cm 2 to form a P-channel. After removing the resist 42, as shown in Figure 14, an interlayer insulating film 31 of PSG is formed on the whole upper surface of the work by LPCVD. Then, as shown in Figure 15, the interlayer insulating film 31 and the silicon oxide film 24 in the vicinity of the second polysilicon gate electrode 26b are partially removed by wet etching using a mixed solution of HF and NH 4 F to form a first contact hole 32. Then, as shown in Figure 16, an ITO film 29′ having a thickness of 140 nm is formed by sputtering at a temperature of 400°C. Then, as shown in Figure 17, the ITO film 29′ is patterned by wet etching using an etchant of HCL:H 2 :HNO 3 = 300:300:50 to form the ITO electrode 29. Then, as shown in Figure 18, the interlayer insulating film 31 and the silicon oxide film 24 in the vicinity of the second polysilicon gate electrode 26b are partially removed by wet etching using a mixed solution of HF and NH 4 F. Then, an aluminium or silicon film having a thickness of 600 nm is formed on the whole upper surface of the work by sputtering. Thereafter, as shown in Figure 19, the aluminium or silicon film is patterned by wet etching using a mixed solution of H 3 PO 4 :H 2 O = 2:10 to form the aluminium or silicon electrode 30. Finally, as shown in Figure 20, a silicon nitride passivation film 33 having a thickness of 400 nm is formed by atmospheric pressure CVD, and then the silicon nitride passivation film 33 is patterned by plasma etching using a mixed gas of CF 4 :O 2 = 95:5. Thus, the TFT having the capacitor element according to the first preferred embodiment is obtained. A liquid crystal picture element portion having the TFT thus obtained is used as a lower substrate of the liquid crystal display device as shown in Figure 2. Next, there will be described a second preferred embodiment of the invention with reference to Figures 21 to 29. As shown in Figure 21, there are provided on a lower insulating substrate 101 a picture element electrode 102, a thin film transistor 103 connected to the picture element electrode 102, and a capacitor element 104 for holding electric charge of the picture element electrode 102. A trench 105 having tapered side walls is formed on the insulating substrate 101. The thin film transistor 103 is constituted of a semiconductor layer 106 formed along the tapered side walls of the trench 105, a gate insulating layer 107 formed on the semiconductor layer 106, and a gate electrode 108 formed on the gate insulating layer 107. As apparent from Figure 21, the thin film transistor 103 is formed so that the semiconductor layer 106, the gate insulating layer 107 and the gate electrode 108 fill in the trench 105 so as to obtain a substantially flat upper surface. A leading electrode 109 connected to a source line or a signal line is connected through a first interlayer insulating film 110 to a source region of the thin film transistor 103. The picture element electrode 102 is obtained by patterning a transparent conductive thin film such as ITO, and it is electrically connected to a drain region of the thin film transistor 103. Further, a second interlayer insulating film 111 is so formed as to cover the leading electrode 109. The trench 105 is so shaped as to satisfy the relation of 0 < tan  ≤ a/2b, where a represents a width of the trench 105; b represents a depth of the trench 105; and  represents a tapered angle of the trench 105. In the process of element designing, the width a and the depth b of the trench 105 are preliminarily designed to have desired values, respectively. Then, the tapered angle  of the trench 105 is set so as to satisfy the above relation, so that the inclined side walls of the trench 105 can reach the bottom of the trench 105, and no vertical walls are formed in the trench 105. If the above relation is not satisfied, then the inclined side walls of the trench 105 cannot reach the bottom of the trench 105, resulting in a smaller value of the depth b than the previously designed value, so that a desired gate length cannot be obtained, and expected electrical characteristics of the transistor cannot be obtained. On the other hand, another trench 112 having tapered side walls is also formed on the insulating substrate 101 simultaneously with the trench 105. The capacitor element 104 is constituted of a first electrode 113 formed along the tapered side walls of the trench 112, a dielectric film 114 formed on the first electrode 113, and a second electrode 115 formed on the dielectric film 114. The dielectric film 114 is formed of the same material as that of the gate insulating film 107 of the thin film transistor 103. Preferably, the first electrode 113 is formed of a first polysilicon 116 which is the same material as that of the semiconductor layer 106 of the thin film transistor 103, and the second electrode 115 is formed of a second polysilicon 117 which is the same material as that of the gate electrode 108 of the thin film transistor 103. While both the thin film transistor 103 and the capacitor element 104 have a trench structure having tapered side walls in the preferred embodiment shown in Figure 21, either the thin film transistor 103 or the capacitor element 104 may have the trench structure having the tapered side walls according to this embodiment of the invention. The operation of the trench structure shown in Figure 21 will now be described in detail with reference to Figure 22. As mentioned above, the trench 105 having a tapering or substantially V-shaped configuration is formed on the insulating substrate 101, and the first polysilicon 116 is deposited on the inner surface of the trench 105. As the first polysilicon 116 becomes the semiconductor layer 106 of the thin film transistor 103, a solid-phase growth process is carried out by first implanting silicon ions (Si + ) into the first polysilicon 116 to thereby refine crystal grain size of the first polysilicon 116, and thereafter heating or annealing the first polysilicon 116 to recrystallize the same and thereby increase the crystal grain size. As the crystal grain size is increased, charge transferability, or the like, of the semiconductor layer 106 is improved to obtain characteristics closer to those of a single crystal thin film. Further the incident direction of ion implantation is perpendicular to an upper surface of the substrate 101. Accordingly, if there is a shadow portion in the trench as shown in Figure 43, the ion implantation cannot be uniformly performed. In particular, the range of ion implantation employed in manufacture of thin film transistors is short. Therefore, in performing implantation of silicon ions, the first polysilicon 116 is entirely exposed to the incident direction of the ion implantation. That is, the trench shape is set so that no shadow portion of the first polysilicon 116 may be generated in viewing the first polysilicon 116 from the upper side of the substrate. In order to cope with this, the trench 105 has tapered side walls according to the second preferred embodiment. The tapered side walls are formed along a longitudinal direction of a gate wire. Further, in the case of forming tapered side walls of the trench 112 in the capacitor element 104, the tapered side walls are formed along a longitudinal direction of a wire to be connected to the capacitor element. The use of such a tapered structure reduces the generation of any shadow in the trench in the step of implantation of silicon ions to enable the formation of the semiconductor layer 106 or the first electrode 113, each preferably formed of the first polysilicon 116, having a uniform crystal structure along the tapered side walls of the trench. Now, a manufacturing process for a substrate for driving the liquid crystal display device according to the second preferred embodiment will be described with reference to the flow diagrams shown in Figures 23 to 29. Figure 23 shows a step of forming the trenches and the first polysilicon. First, a quartz substrate 131 as the insulating substrate is preferred. A photoresist film is applied to an upper surface of the quartz substrate 131, and patterning is carried out by an exposure and developing process. Then, shallow recesses 132T and 132C each having substantially vertical side walls are formed by wet etching using a mixed solution of HF:NH 4 F = 1:6. Then, substantially tapered trenches 133T and 133C respectively inclusive of the recesses 132T and 132C are formed by plasma dry etching using a mixed gas of CF 4 :O 2 = 95:5 as a reaction gas. As the plasma dry etching has anisotropy unlike isotropic wet etching, the trenches 133T and 133C each having a desired tapering shape can be obtained by suitably setting various parameters such as the acceleration energy of plasma particles and the vapour pressure of the reaction gas. Although the trenches 133T and 133C are formed by the combination of wet etching and dry etching in this preferred embodiment, the tapering shape of each trench may be formed by dry etching only in the case of the quartz substrate. Then, a first polysilicon layer 134 having a thickness of 800A° is deposited on the whole upper surface of the quartz substrate 131 by low pressure chemical vapour deposition (LPCVD). In this step, the first polysilicon layer 134 is formed on not only the flat upper surface of the substrate but also the inner wall surfaces of the trenches 133T and 133C with a uniform film thickness. Then, silicon ions (Si + ) are implanted into the first polysilicon layer 134 to perform the solid-phase growth process therefor. For example, the conditions of the ion implantation may be set to an acceleration energy of 30 keV and a dose of 1x10 15 /cm 2 . Alternatively, the conditions may be set to an acceleration energy of 50 keV and a dose of 1x10 15 /cm 2 . By this ion implantation, the first polysilicon layer having an average crystal grain size of 100-500A° is refined to approach an amorphous state. Then, the first polysilicon layer is heated or annealed at about 620°C for a given period of time. As a result, recrystallization of the first polysilicon layer occurs to obtain a film having an average crystal grain size of about 5000A°. Since this film has a crystal structure close to that of a single crystal, a thin film transistor having superior electrical characteristics can be made. If the solid-phase growth process is not performed, the frequency characteristics of a transistor are degraded. Finally, the first polysilicon layer 134 is patterned into a predetermined shape to simultaneously form a semiconductor layer 135 of the thin film transistor in the trench 133T and a first electrode 136 of the capacitor element in the trench 133C. Figure 24 shows a step of forming the gate insulating film. First, an upper surface of the first polysilicon layer 134 is processed by thermal oxidation to form a silicon oxide film 137 having a thickness of about 500A°. After partially covering the silicon oxide film 137 in a transistor forming area with a photoresist 138, arsenic ions (As + ) are implanted to an exposed area under the conditions of an acceleration energy of 30 keV and a dose of 5x10 14 /cm 2 . This ion implantation causes a reduction in resistivity of the first electrode constituting the capacitor element. This ion implantation is performed through the silicon oxide film 137. Then, after removing the resist 138, a silicon nitride film having a thickness of about 300A° is deposited on an upper surface of the silicon oxide film 137 by LPCVD. Further, an upper surface of the silicon nitride film is processed by thermal oxidation to form a silicon oxide film having a thickness of about 20A°. In this way, a gate insulating film 139 having a three-layer structure is formed on the first polysilicon layer 134. Owing to such a three-layer structure, pressure resistance of the gate insulating film 139 is improved. Figure 25 shows a step of forming the gate electrode of the transistor and the second electrode of the capacitor element. First, a second polysilicon layer 140 having a thickness of about 3500A° is deposited on the gate insulating film 139 by LPCVD. Then, although not shown, a film of phosphorus doped glass (PSG) is deposited on the second polysilicon layer 140, and is then heated to diffuse phosphorus contained in the PSG into the second polysilicon layer 140, thereby reducing a resistivity of the second polysilicon layer 140. After removing the PSG, the second polysilicon layer 140 is patterned to form a gate electrode 141 and a second electrode 142 respectively filling the trenches 133T and 133C in such a manner as to obtain a substantially flat upper surface of each trench. The patterning of the second polysilicon layer 140 is performed by plasma etching using a mixed gas of CF 4 :O 2 = 95:5 as a reaction gas. The gate electrode 141 is connected to a gate line or a scanning line via the trench 133T, and the second electrode 142 is also connected to a predetermined common line via the trench 133C. In this way, a trench type capacitor element 156 consisting of the first electrode 136, the dielectric film or insulating film 134 and the second electrode 142 is formed. As the capacitor element 156 has a trench structure, it has an electrode area larger than an apparent plane area to thereby increase capacitance. Furthermore, as the trench 133C has a tapering shape, disconnection at a step portion is less likely to occur. On the other hand, a basic structure of the transistor consisting of the semiconductor layer 135, the gate insulating film 134 and the gate electrode 141 is formed in the trench 133T. As the transistor has a trench structure similar to the capacitor element 156, the apparent two-dimensional channel length can be made shorter than an actual three-dimensional channel length, thereby attaining a fine structure of the transistor. Furthermore, as the semiconductor layer 135 is formed along the tapered wall surface of the trench 133T, disconnection at a step portion is less likely to occur. In addition, as the semiconductor layer 135 is substantially completely exposed to the upper side of the substrate in the initial stage, the implantation of silicon ions in the solid-phase growth process can be uniformly performed. Figure 26 shows a step of forming source and drain regions of the thin film transistor. First, a resist 143 is so mounted as to cover the upper side of the trench 133T, and arsenic ions (As + ) are implanted under the conditions of an acceleration energy of 160 keV and a dose of 1x10 13 /cm 2 to form a lightly doped drain (LDD) which is doped with the arsenic ions in low concentrations. Such an LDD structure is formed with the aim of reducing any short channel effect. However, as the transistor in this preferred embodiment has a trench structure, a sufficient channel length can be ensured, and the formation of the LDD structure is therefore not essential. Then, the trench 133T is masked by using a resist 144 having a size larger than that of the resist 143, and arsenic ions (As + ) are implanted under the conditions of an acceleration energy of 140 keV and a dose of 2x10 15 /cm 2 to form N-channel type source and drain regions. The N-channel type MOS-FET thus made is used as a picture element driving transistor. On the other hand, as CMOS structures are mostly adopted in peripheral circuits such as a scanning circuit or a driving circuit, it is also useful to be able to make a P-channel type MOS-FET. In this case, boron ions (B + ) are implanted through a resist 145 into a flat portion of the semiconductor layer 134 under the conditions of an acceleration energy of 30 keV and a dose of 2x10 15 /cm 2 to form a source region S and a drain region D both doped with a P-type impurity in high concentrations. Figure 27 shows a step of forming a wire. First, a first interlayer insulating film 146 of PSG is deposited on the flattened insulating film 139 by LPCVD. The first interlayer insulating film 146 is selectedly etched to form a first contact hole 147. This process is performed by wet etching using a mixed solution of HF and NH 4 F. Then, an aluminium thin film or an amorphous silicon thin film 148 having a thickness of about 6000A°, which will become a wire, is deposited by sputtering. At this time, the deposited film fills the first contact hole 147 to effect electrical connection with the source region S of a thin film transistor 149. Finally, the aluminium thin film or the amorphous silicon thin film 148 is selectively etched by using a mixed solution of H 3 PO 4 :H 2 O = 2:10 to perform electrode patterning and form a wire 150 connected to a source line or a signal line. Figure 28 shows a step of hydrogen diffusion to the first polysilicon film 134. First, a second interlayer insulating film 151 of PSG is deposited on the first interlayer insulating film 146 by LPSVD. Then, a silicon nitride film 152 having a thickness of 4000A° as a hydrogen diffusion source is formed on the second interlayer insulating film 151 by physically chemical vapour deposition (PCVD). The silicon nitride film 152 contains about 20% of hydrogen atoms. Then, annealing or heating at 400°C is performed to allow the hydrogen atoms to pass through the second interlayer insulating film 151, the first interlayer insulating film 146 and the gate insulating film 139 and to fill traps contained in the first polysilicon film 134. As a result, the charge transferability of the first polysilicon film 134 is further improved. After the hydrogen diffusion process is terminated, the silicon nitride film 152 as the hydrogen diffusion source is wholly removed. Figure 29 shows a step of forming the picture element electrode. First, the laminated structure of the second interlayer insulating film 151, the first interlayer insulating film 146 and the gate insulating film 139 is partially removed by dry etching or wet etching to form a second contact hole 153 leading to the drain region D of the thin film transistor 149. The dry etching may be plasma etching using a mixed gas of CF 4 and O 2 , and the wet etching may be wet etching using a mixed solution of HF and NH 4 F. Then, an ITO film 154 having a thickness of 1400A° is formed on the second interlayer insulating film 151 at 400°C. At this time, the second contact hole 153 is filled with the ITO film 154 to effect electrical connection with the drain region d. Finally, the ITO film 154 is patterned by wet etching using a mixed solution of HC1:H 2 O:HNo 3 = 300:300:50 to form a picture element electrode 155 electrically connected to the drain region D of the thin film transistor 149. Next, there will be described a third preferred embodiment of the invention with reference to Figures 30 to 38. As shown in Figure 30, a liquid crystal display device according to the third preferred embodiment of the invention is constituted of a pair of substrates 301 and 302 arranged in opposition to each other and a liquid crystal layer 303 sandwiched between both the substrates 301 and 302. A counter electrode 304 is formed on the whole inner surface of the upper substrate 302. On the other hand, there are formed on the lower driving substrate 301 a picture element electrode 305, a thin film transistor 306 connected to the picture element electrode 305, and a capacitor element 307 for holding electric charge through the thin film transistor 306. The driving substrate 301 has a laminated structure consisting of a transparent insulating base 308 such as a quartz substrate and a transparent insulating film 309 such as a silicon nitride film. A trench 310 having tapered side walls is formed in the laminated structure of the transparent insulating base 308 and the transparent insulating film 309. The thin film transistor 306 is constituted of a semiconductor layer 311 formed along the tapered side walls of the trench 310, a gate insulating film 312 formed on the semiconductor layer 311, and a gate electrode 313 formed on the gate insulating film 312 and arranged so as to fill the trench 310. A source line 315 is connected through a first interlayer insulating film 314 to a source region S of the thin film transistor 306. A second interlayer insulating film 316 is deposited on the source line 315. The picture element electrode 305 is electrically connected through the first interlayer insulating film 314 to a drain region D of the thin film transistor 306. Another trench 317 having tapered side walls is formed on the driving substrate 301 simultaneously with the trench 310. The capacitor element 307 is constituted of a first electrode 318 formed along the tapered side walls of the trench 317, a dielectric layer 319 formed on the first electrode 318, and a second electrode 320 formed on the dielectric layer 319. Preferably, the first electrode 318 is formed of the same material, for example a first polysilicon, as that of the semiconductor layer 311; the dielectric layer 319 is also formed of the same material as that of the gate insulating film 312; and the second electrode 320 is also formed of the same material, for example a second polysilicon, as that of the gate electrode 313. While both the thin film transistor 306 and the capacitor element 307 have a trench structure in the third preferred embodiment, either the thin film transistor 306 or the capacitor element 307 may have the trench structure according to this embodiment of the invention. However, owing to the trench structure of not only the capacitor element 307 but also the thin film transistor 306, unlike the prior art shown in Figure 41, the aperture ratio can be further improved. The operation of the trench structure shown in Figure 30 will be described in detail with reference to Figure 31. Figure 31 is a schematic sectional view showing a shape of the trench 310 and a forming process therefor. As described above, the insulating base 308 is formed as a quartz substrate, for example. As the quartz substrate is manufactured at a temperature of about 1200°C, for example, it has a very dense fine structure. On the other hand, the transparent insulating film 309 is formed of a material such a silicon nitride, silicon dioxide, or tantalum oxide. The formation of the insulating layer 309 is performed by deposition of such a material by low pressure chemical vapour deposition (LPCVD) or sputtering. Above all, the use of silicon nitride is preferable because it can exhibit a getting effect to impurities such as sodium ions contained in the quartz substrate. For example, silicon nitride is deposited with a thickness of 1-2µm by LPCVD. However, if the thickness is large, there is a possibility of generation of cracks due to internal stress. Therefore, the thickness is set to preferably about 1µm. As the formation of the insulating film 309 is performed at a temperature of about 600°C, it has a porous fine structure as compared with the quartz substrate, so that a high etching rate for the insulating film 309 can be obtained. The trench 310 is formed in the following manner, for example. That is, a resist film 321 having a predetermined pattern is first formed on an upper surface of the transparent insulating film 309. A thickness of the resist film 321 is set to normally 1-2µm. If the thickness of the resist film 321 is larger than 1-2µm, it is difficult to maintain uniformity of the film thickness. Then, anisotropic etching such as plasma etching is carried out through an opening 322 formed through the resist film 321 against the transparent insulating film 309. Since the insulating film 309 has a porous fine structure as mentioned above, it is quickly etched. Further, since a selection ratio of the resist film 321 to the insulating film 309 is high, the resist film 321 is not damaged during the anisotropic etching. In addition, since an etching rate of the insulating film 309 is high, reactive plasma passes around irrespective of the anisotropic etching, thereby easily obtaining a tapering shape of a trench in the insulating film 309. Thereafter, the plasma etching is continued to form a trench having a tapering shape on an upper surface of the insulating base 308, thus finally obtaining the tapering trench 310 having a depth of about 3µm. While the tapering shape of the trench formed on the insulating base 308 is more sharp than that of the trench formed through the insulating film 309, the trench 310 has a certain tapering shape as a whole. According to the third preferred embodiment, the insulating film 309 having a high etching rate is provided. Accordingly, etching of the insulating substrate 301 can be quickly performed, and it is unnecessary to repeatedly form the resist film 321. Accordingly, the throughput in the trench forming step can be improved. In addition, as a sectional shape of the trench 310 is tapering, the step coverage can be improved to thereby effectively prevent disconnection problems or the like, thus improving the yield. Now, a manufacturing process for a substrate for driving a picture element in the liquid crystal display device according to the third preferred embodiment will be described with reference to the flow diagrams shown in Figures 32 to 38. Figure 32 shows a step of forming the trenches and the first polysilicon film. First, a quartz substrate 331 is prepared on which a transparent insulating film, for example a silicon nitride film 330, is formed. The silicon nitride film 330 may be replaced by a silicon dioxide film, a tantalum oxide film or the like as the transparent insulating film. The silicon nitride film 330 is formed to have a thickness of 1-2µm by LPCVD. Then, a resist film 332 is patterned on an upper surface of the silicon nitride film 330. Then, plasma etching is performed through openings formed through the resist film 332 to simultaneously form trenches 333T and 333C each having a tapering shape. The trench 333T is formed for the formation of the thin film transistor, and the trench 333C is formed for the formation of the capacitor element. The conditions of the plasma etching of the silicon nitride film 330 and the quartz substrate 331 for the formation of the trenches 333T and 333C are such that a mixed gas of CF 4 :O 2 = 95:5 is selected as the reaction gas; gas pressure is set to 0.6 Torr; high-frequency electric power for generation of plasma is set to 1000 W; and substrate temperature is set to 60°C. Under the conditions, the etching rate of the silicon nitride film 330 is 583A°/min, and the etching rate of the quartz substrate 331 is 341A°/min. It is understood from this result that the etching rate of the silicon nitride film 330 having a porous fine structure is about 1.7 times the etching rate of the quartz substrate 331 having a dense fine structure. Accordingly, the silicon nitride film 330 can be quickly etched, and a desired tapering shape of the silicon nitride film 330 can be obtained. During this the resist film 332 is hardly damaged, and therefore the plasma etching may be continued without re-forming the resist film 332 to form the trenches 333T and 333C in one step. After forming the trenches 333T and 333C, the resist film 332 is removed by plasma ashing, for example. Then, a first polysilicon film 334 having a thickness of 800A° is formed on the whole upper surface of the substrate inclusive of the inner surfaces of the trenches 333T and 333C by LPCVD. Then, silicon ions (Si + ) are implanted into the first polysilicon film 334 under the conditions of an acceleration energy of 30 keV and a dose of 1x10 15 /cm 2 or under the conditions of an acceleration energy of 50 keV and a dose of 1x10 15 /cm 2 . Owing to this ion implantation, the first polysilicon film 334 becomes close to an amorphous state. Then, the first polysilicon film 334 is heated or annealed at 620°C to perform a solid-phase growth process of silicon crystals. Owing to this process, a crystal grain size of the first polysilicon film 334 in the nearly amorphous state is increased to approach a crystal grain size close to that of single crystal, thus obtaining high-performance electric characteristics. As each of the trenches 333T and 333C has a tapering shape, the first polysilicon film 334 deposited on the tapered inner surfaces of the trenches 333T and 333C is exposed to the incident direction of the silicon ions. Accordingly, uniform implantation of the silicon ions can be effected to thereby uniformly perform the solid-phase growth process. Finally, the first polysilicon film 334 is patterned to form a semiconductor layer 335 in the trench 333T and a first electrode 336 in the trench 333C. Figure 33 shows a step of forming the gate insulating film. First, an upper surface of the first polysilicon film 334 is processed by thermal oxidation to form a second dioxide film 337 having a thickness of about 500A°. After masking a transistor forming portion inclusive of the trench 333T with a resist 338, arsenic ions (As + ) are implanted into the first electrode 336 formed in the trench 333C under the conditions of an acceleration energy of 30 keV and a dose of 5x10 14 /cm 2 to reduce the resistivity of the first electrode 336. After removing the resist 338, a silicon nitride film having a thickness of 300A° is deposited on the silicon dioxide film 337 by LPCVD. Furthermore, the upper surface of this silicon nitride film is processed by thermal oxidation to form a silicon dioxide film having a thickness of 20A°. In this way, a gate insulating film 339 having a three-layer structure is obtained. Owing to this three-layer structure, pressure resisting characteristic of the gate insulating film 339 is improved. Figure 34 shows a step of forming the gate electrode of the transistor and the second electrode of the capacitor element. First, a second polysilicon film 340 having a thickness of 3500A° is deposited on the whole upper surface of the gate insulating film 339 by LPCVD. Then, although not shown, phosphorous doped glass (PSG) is deposited on the second polysilicon film 340, and is then heated to diffuse phosphorous contained in the PSG into the second polysilicon film 340, thereby reducing the resistivity of the second polysilicon film 340. Finally, the second polysilicon film 340 is patterned by plasma etching using a mixed gas of CF 4 :O 2 = 95:5 as a reaction gas to form a gate electrode 341 filling the trench 333T and a second electrode 342 filling the trench 333C. As a result, a basic structure of the thin film transistor consisting of the semiconductor layer 335, the gate insulating film 334 and the gate electrode 341 is formed in the trench 333T, and a capacitor element 356 consisting of the first electrode 336, the dielectric film 334 and the second electrode 342 is formed in the trench 333C. Figure 35 shows a step of forming source and drain regions of the thin film transistor. First, a resist 343 is so mounted as to cover the upper side of the trench 333T, and then arsenic ions (As + ) are implanted under the conditions of an acceleration energy of 160 keV and a dose of 1x10 13 /cm 2 to form a lightly doped drain (LDD) which is doped with arsenic ions in low concentrations. Owing to such an LDD structure, it is possible to effectively prevent a short channel effect. However, as a sufficient channel length can be ensured along the inner wall of the trench 333T, the formation of the LDD structure is not essential. Then, arsenic ions (As + ) are implanted through a resist 344 having a mask area larger than that of the resist 343 under the conditions of an acceleration energy of 140 keV and a dose of 2x10 15 /cm 2 to form N-type source and drain regions. As a result. an N-channel type transistor for driving a picture element is formed at a portion of the semiconductor layer 335 in the trench 333T. Further, at the same time, a peripheral circuit in addition to the driving transistor is also formed on the substrate. As the peripheral circuit has a CMOS structure, it is necessary to also form a p-channel type transistor. In this case, boron ions (B + ) are implanted through a resist 345 under the conditions of an acceleration energy of 30 keV and a dose of 2x10 15 /cm 2 . As a result, a source drain region S and a drain region D both of a P-type are formed on a flat portion of the semiconductor layer 335. Figure 36 shows a step of forming a wire. First, a first interlayer insulating film 346 of PSG is deposited on an upper surface of the gate insulating film 339 by LPCVD. Then, the first interlayer insulating film 346 is selectively patterned by wet etching using a mixed solution of HF and NH 4 F to form a first contact hole 347. Then, an aluminium or silicon conductive film 348 having a thickness of 6000A° is formed by sputtering on the first interlayer insulating film 346 inclusive of an inner surface of the first contact hole 347. As a result, the conductive film 348 is electrically connected through the first contact hole 347 to the source region S of a transistor 349. Finally, the conductive film 348 is patterned by wet etching using a mixed solution of H 3 PO 4 :H 2 O = 2:10 to form a source line 350. Figure 37 shows a step of diffusing hydrogen to the first polysilicon film 334. First, a second interlayer insulating film 351 of PSG is deposited on the first interlayer insulating film 346 so as to cover the source line 350 by LPCVD. Then, a hydrogen diffusion source 352 is formed on the second interlayer insulating film 351. The formation of the hydrogen diffusion source 352 is performed by depositing a silicon nitride film having a thickness of 4000A° by physically chemical vapour deposition. This silicon nitride film contains a large amount of hydrogen atoms. Then, the hydrogen diffusion source 352 is heated to diffuse the hydrogen atoms through the second interlayer insulating film 351, the first interlayer insulating film 346 and the gate insulating film 339 to the first polysilicon film 334 and to fill traps in the first polysilicon film 334 with the hydrogen atoms. As a result, the charge transferability of the first polysilicon film 334 is improved. Finally, the hydrogen diffusion source 352, now unnecessary, is entirely removed by plasma etching. Figure 38 shows a step of forming the picture element electrode. First, a second contact hole 353 is formed by plasma etching using a mixed gas of CF 4 :O 2 = 95:5 or wet etching using a mixed solution of HF and NH 4 F. Then, a transparent conductive film 354 of ITO or the like having a thickness of 1400A° is deposited on the second interlayer insulating film 351 inclusive of an inner surface of the second contact hole 353 by sputtering at 400°C. As a result, the transparent conductive film 354 is electrically connected through the second contact hole 353 to the drain region D of the transistor 349. Finally, the transparent conductive film 354 is patterned by wet etching using a mixed solution of HC1:H 2 O:HNO 3 = 300:300:50 to obtain a picture element electrode 355 having a predetermined shape and area. In at least some preferred embodiments, this invention to provides a liquid crystal display device having: a capacitor element in a liquid crystal picture element section without significantly reducing aperture ratio; a trench structure which enables uniform solid-phase growth in a polysilicon thin film and which can obtain the desired electric characteristics of a semiconductor thin film; a trench structure which can be formed quickly so as to improve production efficiency; and a trench structure which can improve the step coverage. While the invention has been described with reference to specific embodiments, the description is illustrative and is not to be construed as limiting the scope of the invention. Various modifications and changes may occur to those skilled in the art without departing from the scope of the invention as defined by the appended claims.

Claims: A liquid crystal display device comprising: a substrate (21) having a plurality of trenches (22); and a plurality of display elements arranged in a matrix form on said substrate, each of said display elements comprising a picture element electrode (33), a switching transistor (23, 24b, 25b, 26b) associated with said picture element electrode, and a capacitor element (23, 24a, 25a, 26a) formed in one of said plurality of trenches an associated with said picture element electrode; said capacitor element comprising: a first electrode (23) formed integrally with a semiconductor layer (23) of said switching transistor, said first electrode being formed along an inner surface of said one of said plurality of trenches; a dielectric layer (24a, 25a) formed on said first electrode; and a second electrode (26a) opposed to said first electrode through said dielectric layer. A liquid crystal display device according to claim 1, wherein said dielectric layer (24a, 25a) is formed of the same material as that of a gate insulating layer (24b, 25b) of said switching transistor. A liquid crystal display device according to claim 1, wherein said second electrode (26a) is formed of the same material as that of a gate electrode (26b) of said switching transistor. A liquid crystal display device according to any one of the preceding claims, wherein said substrate comprises an insulating substrate and an insulating layer (309) formed on said insulating substrate (308). A liquid crystal display device according to any one of the preceding claims, wherein said plurality of trenches have tapered side walls. A liquid crystal display device comprising: a substrate (101) having a plurality of first trenches (105); and a plurality of display elements arranged in a matrix form, each of said display elements comprising a picture element electrode (102), a thin film transistor (103) formed in one of said plurality of first trenches and associated with said picture element electrode and a capacitor element (104) associated with said picture element electrode. A liquid crystal display device according to claim 6, wherein said plurality of first trenches (105) have tapered side walls. A liquid crystal display device according to any one of claims 6 and 7 wherein said thin film transistor (103) comprises a semiconductor layer (106) formed along an inner surface of said one of said plurality of first trenches (105), a gate insulating layer (107) formed on said semiconductor layer, and a gate electrode (108) formed on said gate insulating layer so as to fill said one of said plurality of first trenches. A liquid crystal display device according to any one of claims 6, 7 and 8, wherein each of said plurality of first trenches have a structure satisfying the relation of: 0 < tan  ≤ a/2b wherein a represents a width of said first trench; b represents a depth of said first trench; and  represents a taper angle of said first trench. A liquid crystal display device according to any one of claims 6 to 9 wherein said substrate (101) has a plurality of second trenches (112), and said capacitor element (104) is formed in one of said plurality of second trenches. A liquid crystal display device according to claim 8, wherein said substrate (101) has a plurality of second trenches (112) formed simultaneously with said plurality of first trenches (105), said capacitor element (104) being formed in one of said plurality of said second trenches. A liquid crystal display device according to claim 11, wherein said capacitor element (104) comprises a first electrode (113) formed along an inner surface of said one of said plurality of second trenches (112), a dielectric layer (114) formed of the same material as that of said gate insulating layer (107), and a second electrode (115) opposed to said first electrode through said dielectric layer. A liquid crystal display device according to claim 12, wherein said first electrode (113) is formed of the same material as that of said semiconductor layer (106), and said second electrode (115) is formed of the same material as that of said gate electrode (108). A liquid crystal display device according to any one of claims 6 to 13, wherein said substrate comprises an insulating substrate (308) and an insulating layer (309) formed on said insulating substrate. A liquid crystal display device according to any one of claims 10 and 11, wherein said plurality of second trenches (112) have tapered side walls. A liquid crystal display device according to claim 8, wherein said semiconductor layer (106) is formed of doped polysilicon. A liquid crystal display device according to claim 12, wherein said first electrode (113) is formed of doped polysilicon. A liquid crystal display device according to any one of claims 16 and 17, wherein said polysilicon is doped with a cation selected from the group consisting of Si + , B + , As + and P + .

Inventors: INO MASUMITSU, INO, MASUMITSU, Ino, Masumitsu, c/o Patents Division
Applicants: SONY CORP, SONY CORPORATION
Application year: 1992
Main classification: G02F1
IPC codes: G02F1, H01L27