REMOVABLE AND GUILLOTINABLE EMULSION PRESSURE-SENSITIVE ADHESIVES

Abstract: There is provided a removable, repositionable and guillotinable pressure-sensitive construction comprising a backing having thereon an acrylic emulsion adhesive modified by a wax surfactant or mixtures thereof. Removability may be enhanced by use of a plasticizer.

Description: 10 REMOVABLE AND GUILLOTINABLE EMULSION PRESSURE-SENSITIVE ADHESIVES Field of the Invention The invention is directed to pressure-sensitive 15 adhesives that exhibit clean removability from various substrates without sacrificing guillotinability. Background of the Invention It is well known in the pressure-sensitive 20 adhesives industry that two approached have been tried to achieve a good removability, namely, the controlled coating processes and/or adhesive rheology. If the coat weight of the adhesive is controlled within a certain range, the adhesive will exhibit a 25 reduced peel force and will have a removable behavior for a short period of time. However, due to the inherent permanent characteristic of most adhesives, the adhesion will grow with age and become a non¬ removable. 30 An alternative is to use a discontinuous coat of a- adhesive segments or miscrospheres providing in effect a reduced coat weight. This approach is based on adhesion microspheres described in U.S. Patent 3,691,140 to Silver, U.S. Patent 4,166,152 to Baker et 35 al, U.S. Patent 4,495,318 and 4,598,212 to Howard, U.S. Patent 4,810,763 to Mallya et al and adhesive segment described in European Patent 0180598, each incorporated herein by reference. The rheological approach has been to design a high gel, low Tg adhesive which has a low tangent delta at the debonding frequency. These rheological properties enable the adhesive to behave like.a soft material and have a low adhesion force during the peel test. This rheological approach, however, generates problems in the guillotine process. In other words, good removability and good guillotinabilty are often properties which are contradictory to each other. The latter is a must requirement for all adhesives used in the offset sheeting business. There have also been other attempts to formulate an adhesive to reduce the bonding between an adhesive and knife during the guillotine process. Polyalkalene glycols such as polyethylene glycol (PEG) has been used to achieve this property with tackified water insoluble elastomers as described in U.S. Patent 4,548,845 to Parsons et al incorporated herein by reference, but phase separation and incompatibility between the adhesive system and PEG have limited its amount and usage. Silicones, as described for instance in U.S. Patents 4,151,319 to Sackoff and 4,346,189 to Laurant, each incorporated herein by reference have also been suggested. The products display good guillotinability, and initial repositionability. Repositionability, however, is lost with time. It would be desirable to provide a pressure- sensitive adhesive composition which exhibits removable and repositionable properties which do not deteriorate with age, as well as good guillotinability for use in offset printing applications. Background of the Invention According to the present invention there is provided pressure-sensitive adhesives which exhibit removable and repositionable characteristics to certain substrates and which retains that property for protracted periods of time and offers, as well, excellent guillotinability. This result is achieved by combining with an emulsion acrylic, tacky pressure- sensitive adhesive with an emulsifiable wax, surfactant or mixtures thereof present in a concentration to reduce adhesivity of the adhesive to a level sufficiently low to allow removability and at the same time provide sufficient lubricity to afford excellent guillotinability including excellent cuttability. The acrylic pressure-sensitive adhesive polymers used in the instant invention may be inherently tacky or tack provided by the inclusion of a tackifier or plasticizer added during the compounding stage. A plasticizer may also be used to enhance removability. The adhesive may be used as such or whose tack is reduced by crosslinking. The wax and/or surfactant are provided during the compounding stage and cast as part of a homogenous emulsion to provide a pressure- sensitive adhesive coating at any desired uniform level of removability, as compared to the unmodified acrylic pressure-sensitive adhesive composition. This is in consequence of a reduction in adhesion level. The additive at the same time imparts excellent guillotinability. It is preferred to use either the wax alone or the surfactant alone with use of a surfactant being presently preferred. Emulsifiable wax can be employed in the amount of about 0.5 to about 1.5% by weight of the acrylic emulsion polymer and wax. A surfactant can be employed in the amount of about 0.5 to about 3.5% by weight of the acrylic emulsion polymer and surfactant. When used in combination the total amount of wax and surfactant present should be less than about 3% by weight of the acrylic emulsion polymer and additive wax and surfactan . It is presently preferred to employ a mixture of polymeric waxes alone or with a disodium n-octadecyl sulfosuccinamate in combination with butyl benzyl phthalate or a surfactant which is an ethyleneoxide- propyleneoxide copolymer with nonionic emulsified waxes. The presently preferred emulsion acrylic adhesive is a crosslinked acrylic polymer based on 2-ethylhexyl acrylate, butyl aerylate and a carboxylic acid or a copolymer of 2-ethylhexyl acrylate, methacrylic acid and acrylic acid. Brief Description of the Drawings Fig. 1 illustrates 90° peel and looptack properties of adhesive compositions which conform to the instant invention in comparison to controls. Fig. 2 illustrates 90° peel adhesion for adhesives of the instant invention used with various backings for face stocks. Detailed Description According to the present invention, there is provided pressure-sensitive adhesives which when cast from an emulsion onto a suitable backing or face stock display the properties of excellent guillotinability and repositionability. Adhesives of the instant invention are based on the combination of an emulsion acrylic polymer preferably crosslinked, compounded in emulsion with an emulsifiable wax, a- surfactant or mixtures thereof which when cast onto a suitable backing enables face stock guillotining for offset printing applications and removability and repositionability. The acrylic emulsion pressure-sensitive adhesive polymers useful in accordance with the instant invention, contain on a percent by weight basis from 30 to about 98% percent by weight of one or more alkyl acrylates containing about 4 to about 8 carbon atoms in the alkyl group. Preferably the total alkyl acrylate concentration is from about 60 to about 95% by weight based on the total weight of the monomers. Useful alkyl acrylates include n-butyl acrylate, 2-ethylhexyl acrylate, isooctyl acrylate and the like, with 2- ethylhexyl acrylate and mixtures of 2-ethylhexyl acrylate and butyl acrylate being preferred. The second component of the acrylate polymers is one of more modifying monomers which affects the performance of the acrylate monomers. Among them there may be included one or more unsaturated carboxylic acids containing from 3 to about 5 carbon atoms normally present in an amount of about 2 to 10% by weight of the monomers forming the acrylic polymers. Unsaturated carboxylic acid, included among others acrylic acid, methacrylic acid, itaconic acid and the like. Acrylic acid and methacrylic acid or mixtures thereof are presently preferred. Other monomers which may be present are one or more vinyl esters which may be present in an amount of from about 15 to about 35% by weight of the total monomers and can include monomers such as vinyl acetate, vinyl butyrate, vinyl propanate, vinyl isobutarate and the like. In addition there may be provided one or more diesters of dicarboxylic acids, such as di-2-ethylhexyl maleate and di-2-ethylhexyl fumarate and the like. The acrylic polymers are normally are prepared by emulsion polymerization in the presence of one or more surfactants including a reactive surfactant which when reacted becomes part of the polymer. The acrylic polymer may be used as formed and, if desired, crosslinked either during or following polymerization by a conventional means and are provided as emulsion of the solids content of 50 or more percent by weight solids , normally 60 or more percent by weight solids. The presently preferred acrylic emulsion polymers are a crosslinked acrylic polymer containing butyl acrylate, 2-ethylhexyl acrylate and an unsaturated carboxylic acid sold by Avery Chemical Company division of Avery Dennison Corporation and a copolymer of about 98% 2-ethylhexyl acrylate, about 1.4% methacrylic acid and about 0.6% acrylic acid. To induce the repositionability and guillotinability the emulsion pressure-sensitive adhesives are combined with an emulsifiable wax, a surfactant or mixtures thereof which are combined with the acrylic pressure-sensitive adhesive polymer at the compounding stage. It is presently preferred that the additive be an emulsified surfactant. A preferred surfactant is a nonionic surfactant known as Pluronic F-108, a normally solid polyoxypropylene-polyoxethylene block copolymer having a molecular weight of about 14600 and an HLB value greater than 24. The surfactant is manufactured and sold by BASF. The most preferred surfactant is disodium n-octadecyl sulfosuccinamate manufactured and sold by American Cyanamid Co. Wax additives not only provide a special lubrication between the knife surface and the adhesive, but also dramatically reduces adhesion level. Wax emulsions include emulsified petroleum resins, paraffin waxes, oxidized paraffin waxes, microcrystalline waxes, carnauba waxes, ontain waxes, polyethylene waxes and the like emulsified to form a nonionic wax emulsion. A preferred wax is ME47950, a nonionic paraffin wax emulsion manufactured and sold by Michelman, Inc. of Cincinnati, Ohio. The most preferred waxes are emulsified mixed modi ied polymeric waxes supplied by BV -Cera B.V. Netherlands. The backing of face stock may vary widely and include paper face stocks, polymeric face stocks such as vinyl and acetate face stock. In the presently preferred construction the face stocks is cast coated high gloss paper, C2S matte litho paper, uncoated offset paper, recycled matte litho paper, latex saturated face paper, clear acetate, matte acetate, vinyl and the like, coated with adhesive to a level of 15 to 21, preferably 18 g/m 2 with the adhesive protected by a silicone release liner. The products of the instant invention as illustrated by - the Examples uniquely provide removability and guillotinability without developing curl even when paper is used as the face stock and in the release liner. It also displayed uniqueness as compared to other removable papers and tapes in that they displayed the ability to be removed from certain substrates without tear of the backing or face stock and yet provide a low enough adhesion to allow removability and repositionability. For purpose of illustrating the invention, there was used for Examples 1 to 3 as the base adhesive the preferred commercial crosslinked acrylic emulsion polymer an emulsion polymerized mix of butyl acrylate, 2-ethylhexyl acrylate and an unsaturated carboxylic acid manufactured by Avery Chemical with the name 220X. For Control 1 the emulsion polymer was used as received. For Examples 1 to 3 there was formulated an emulsion solution of 220X, Pluronic F-108 a normally solid polyoxypropylene-polyoxyethylene block copolymer having an average molecular of 14600 and melting point of 57°C and HLB of greater than 24 manufactured by BASF. It was dissolved in dionized water added to the 22OX emulsion and a coatable mixture having a solids content of about 52% solids and a viscosity of 7,000 cps (desired range 4,000 - 10,000 cps) . The composition contained about 3% by weight surfactant based on the weight or surfactant and polymer (Adhesive A) . Adhesive B was made the same way but contains about 2% surfactant. The formulated emulsion contained 3% surfactant based on the weight of surfactants and polymer when coated on the backing described below in Table I has the following approximate properties at a coat weight of about 18 q/m 2 . TABLE 1 Example Backing Property ∑_[ Y 2 Z 3 Release, gr 30 30 50 (16 hrs. aged) 180° peel lb/in 0.8 0.5 0.6 (16 hrs. aged) 1. Satin lithograph paper 2. Blue-white high gloss 3. Recycled matte litho Table 2 and Fig. 1 compares adhesive coating performance of Control 1, Adhesive A and Adhesive B, Control 2 which contained 3% by weight polyethylene glycol and Control 3 containing 1% by weight polyethylene glycol. Polyethylene glycol was added by a aqueous 50% solution and exhibited phase separation. Table 3 • compares removable performance of the composition of Example 1 from various substrates and aging for the dwell time shown. "Yes" means removability. The conclusion drawn was that performance on glass, stainless steel and corrugated cardboard was good, but not good on painted metal, polyethylene and ABS substrates. Table 4 compares the performance of the adhesive of Example 1 on a matte acetate backing. Based on the results it was concluded priming of the backing is required. Fig. 2 is a block diagram compare peel adhesion in lb/in for Control 1 to the Adhesive A contained 3% surfactant on various backings. When a 100 sheet stack of the construction of Example 1 was guillotined 15 times it was observed that both sides of the knife and stack were rated excellent with no build-up of adhesive on the stack or the blade. Table 5 shows the performance of the adhesive of Control 1 compounded with 1% by weight wax based on the weight of the polymer and wax of a paraffin wax provided as a nonionic emulsion. This is Adhesive C. The emulsion was known as ME47950 paraffin wax having a melting point of 147°F, a solids content of 50% with an average particle size of 0.35 micron. The backing was Matte Litho. Overall guillotinability performance was excellent. Shear, min, 250g, 580/621 425/721 239/324 331/461 451/672 1/2" x 1/2" 24 Hour Removability (2 tests each tear means backing tear) Glass 2 tears 0 tears 0 tears 0 tears 1 tear Painted Steel 2 tears 0 tears 0 tears 1 tear 1 tear Bleed into Paper No No No Yes Yes Face Stock YES: GOOD REMOVABI ITY PT: PAPER TEAR FS: FACE SEPARATION, ADHESIVE IS NOT ADHERED TO THE FACE STOCK YES: GOOD REMOVABILITY PT: PAPER TEAR FS: FACE SEPARATION, ADHESIVE IS NOT ADHERED TO THE BACKING 50°C Aged YES YES: GOOD REMOVABILITY PT: PAPER TEAR FS: FACE SEPARATION, ADHESIVE IS NOT ADHERED TO THE FACE STOCK Attached Table 6 shows the removability performance of the Adhesive C deposited at a coat weight of 25 g/m 2 on Matte Litho backing. Table 7 shows the performance at 0.75% by weight of the wax (Adhesive D) and Table 8 shows performance at 0.5% by weight of the wax (Adhesive E) . Removability and guillotinability were in all instances excellent. In the aging tests, exposure at 50°C for 1 week is equivalent to 6 months at room temperature and 2 weeks at 50°C is equivalent to 1 year at room temperature. Control 4 and Examples 5 to 9 For Control 4 and Examples 5 to 9, there was used as the polymer AVC 3666 at 67% solids acrylic polymer emulsion in which the polymer contains about 98% 2- ethylhexyl acrylate, about 1.4% by weight methacrylic acid and about 0.6% acrylic acid. The wax used was Aquacer 533, an emulsion of mixed polymeric waxes supplied by BYK-Cera B.V. , Netherlands, and as the surfactant Aerosol 18, a paste of 35% disodium n- octadecyl sulfosuccinamate in water provided by American Cyanamid Co. The plasticizer was butyl benzyl phthalate. The following are the presently preferred compositions: A. AVC 3666 (67% TSC) 100 parts wet Aerosol 18 (35% TSC) 5.0 Butyl benzyl phthalate 5.0 B. AVC 3666 (67% TSC) 100 parts wet Aquacer 533 (40% TSC) 2.1 Butyl benzyl phthalate 5.0 TSC = Total Solids Content The control and example compositions are shown in Table 9. Adhesive properties are shown in Table 10. The control displayed a build-up of adhesiON with age. The compositions of Examples 5, 8 and 9 showed no build-up of adhesion to a variety of substrate. The composition of Examples 6 and 7 showed a build-up of adhesion to polymethyl methacrylate at 70°C. It was observed that the mixture of polymer and wax gave adequate removability from most surfaces, but the addition of the plasticizer to the blend gave stable removability from a wider variety of surfaces. As with all other compositions of the invention, the examples gave excellent guillotinability and cutability.

Claims: IN THE CLAIMS 1. Guillotinable and substrate removable pressure-sensitive adhesive composition comprises of a tacky acrylic emulsion pressure-sensitive adhesive in admixture with a modifying agent selected from the group consisting of an emulsifiable wax, a surfactant and mixtures thereof. 2. A composition as claimed in claim 1 in which the surfactant present in an amount of from 0.5 to about 3.5% by weight based on the weight of the nonionic surfactant and the acrylic emulsion polymer. 3. A composition as claimed in claim 1 or 2 in which the surfactant is selected from the group consisting of disodium n-docecyl sulfosuccinamate and a polyoxyethylene-polyoxypropylene block copolymer. 4. A pressure-sensitive adhesive composition as claimed in claim 3 in which the polyoxyethylene- polyoxypropylene surfactant has a HLB value greater than 24. 5. A pressure-sensitive adhesive as claimed in any one of claims 1 to 4 in which the emulsifiable wax is present in an amount from about 0.5 to about 1.5% by weight based on the weight of the acrylic emulsion polymer and emulsifiable wax. 6. A pressure-sensitive adhesive as claimed in any one of the previous claims in which emulsifiable wax is selected from the group consisting of paraffin waxes and mixed polymeric waxes. 7. A pressure-sensitive adhesive composition as claimed in any one of the previous claims in which the additive is a blend in which a plasticizer is present. 8. A pressure-sensitive adhesive as claimed in claim 7 in which the plasticizer is disodium butyl benzyl phthalate. 9. A pressure-sensitive adhesive as claimed in any of the previous claims in which the acrylic emulsion pressure-sensitive adhesive is a copolymer of 2-ethylhexyl acrylate; butyl acrylate and an unsaturated carboxylic acid or a copolymer of 2-ethylhexyl acrylate; methacrylic acid and acrylic acid. 10. A pressure-sensitive adhesive as claimed in any one of the previous claims containing from about 89 to about 99% by weight of a copolymer containing about 94% by weight 2-ethylhexyl acrylate, about 1.4% by weight methacrylic acid and about 0.6% by weight acrylic acid, from 0 to about 1.25% by weight mixed polymeric waxes, 0 to about 2.25% by weight disodium n- octadecyl sulfosuccinamate and about 6.8 to about 10% by weight butyl benzyl phthalate. 11. A guillotinable and removable pressure- sensitive adhesive stock comprising a backing providing a surface having therein a coating thereon a guillotinable and.removable pressure-sensitive adhesive claimed in any one of claims 1 to 10.

Inventors: MAYER ANDRE, REAVES JESSIE COSTON, SHIAONUNG JOHN SU, STIEGER MANFRED KARL, VON KLEIST PETER ROBIN, MAYER, ANDRE, REAVES, JESSIE, COSTON, SHIAONUNG, JOHN, SU, STIEGER, MANFRED, KARL, VON KLEIST, PETER, ROBIN
Applicants: AVERY DENNISON CORP, AVERY DENNISON CORPORATION
Application year: 1992
Main classification: C08K5
IPC codes: C08L71, C08L91, C09D133, C09J7, C09J133