Thermal transfer sheet

Abstract: An object of the present invention is to provide a thermal transfer sheet wherein a clear image having a sufficient density is formed in a thermal transfer process using a sublimable dye and wherein the formed image exhibits excellent fastnesses, particularly excellent light fastness. The present invention is directed to a thermal transfer sheet comprising a base sheet and a dye-containing layer formed on the one surface of the base sheet wherein a dye included in the dye-containing layer comprises a mixture of two or more specific dyes.

Description: This invention relates to a thermal transfer sheet, and more particularly to a thermal transfer sheet capable of forming a recording image having excellent color density, clearness, and fastnesses, particularly light fastness. Heretofore, various thermal transfer processes have been known. Of these, there has been widely used a sublimation transfer process wherein a sublimable dye is used as a recording agent; it is carried on a base sheet such as paper to form a thermal transfer sheet; this thermal transfer sheet is superposed on a transferable material which can be dyed by the sublimable dye, for example, a polyester woven fabric or the like; and a heat energy is applied in the form of a pattern from the back surface of the thermal transfer sheet to transfer the sublimable dye to the transferable material. Recently, there has been a process for forming various full color images on materials such as paper and plastic films using the thermal transfer process of sublimation type described above. In this case, a thermal head of a printer is used as heating means, multi-color dots such as three-color or four-color dots are transferred to the transferable material by heating for an extremely short period of time, and the full color images of an original are reproduced by the multi-color dots. The images thus formed are very clear since the colorant used is a dye. Because the transparency is excellent, the images obtained have excellent neutral tint reproducibility and gradation, they are similar to the images obtained by the prior offset printing and gravure printing and high performance images comparable to full color photographic images can be formed. However, the most important problems of the thermal transfer process described above are inferior color density and light fastness of the formed images. That is, in the case of high-speed recording, it is required that the impartation of the heat energy be an extremely short period of time of subsecond. Accordingly, the sublimable dye and the transferable material are not sufficiently heated due to such a short period of time and therefore images having a sufficient density cannot be formed. Accordingly, sublimable dyes having an excellent sublimation property have been developed in order to cope with such a high-speed recording process. However, the dyes having an excellent sublimation property have generally a small molecular weight and therefore their light fastness is lack in the transferable material after transfer. Thus, the formed images are liable to be faded. If sublimable dyes having a relatively high molecular weight are used in order to avoid such problems, images having a satisfactory density as described above cannot be obtained since the sublimation rate is inferior in the high-speed recording process as described above. EP-A-0 318 032 describes a thermal yellow-dye transfer sheet hat comprises a base film having thereon a dye layer comprising a yellow-dye dispersed in a binder which comprises at least one dye represented by a specifically defined formula (I) and at least one dye represented by a specifically defined formula (II); see e.g. claim 1. In Example 1 on page 8, the ink composition contains compounds A and B having an octyloxycarbonyl residue and a dipropylaminocarbonyl residue, respectively, at the phthalic acid moiety. An object of the present invention is to provide a thermal transfer sheet wherein clear images having a sufficiently high density are provided in a thermal transfer process using a sublimable dye and wherein formed images exhibit excellent fastnesses, particularly excellent light fastness. The object described above is achieved by the present invention. That is, the present invention is directed to a thermal transfer sheet comprising a base sheet and a dye-containing layer formed on the one surface of said base sheet wherein a dye included in said dye-containing layer comprises a mixture of two or more specific dyes. A mixture of at least one dye represented by the following formulae (1) and (2) with at least one dye represented by the following formulae (3) and (4) is suitable as a yellow dye included in said dye-containing layer: wherein X represents or , which represents a five or six-membered ring reaction residue represented by which may have a fused ring; A represents an electron attractive group; Z represents -CO-, -NR 6 -, -S-, -O- or -NH-; R 1 represents a hydrogen atom, R 6 , a halogen atom, a nitro group, -OR 6 , -SR 6 or an allyl group which may be sustituted; R 2 represents a hydrogen atom, a halogen atom, -OR 6 or -SR 6 ; R 3 represents a hydrogen atom, R 6 , a halogen atom, a nitro group, an allyl group which may be substituted, -OR 6 , -SR 6 , a sulfamoyl group,a carbamoyl group, an acyl group, an acylamide group, a sulfonamide group, an ureido group, or -NR 6 R 6 , wherein R 6 may be the same or different; R 4 represents a hydrogen atom, a halogen atom, -OR 6 , -SR 6 , a cyano group, -COOR 6 , a carbamoyl group, or a sulfamoyl group; R 5 represents a hydrogen atom, a halogen atom, -OR 6 , or -SR 6 ; R 6 represents an alkyl group which may be substituted, an aryl group which may be substituted, a cycloalkyl group which may be substituted, or a heterocyclic ring which may be substituted; and R 7 represents a hydrogen atom, -R 6 , an allyl group which may be substituted, an alkenyl group which may be substituted, a heteroalkenyl group which may be substituted, an arylalkyl group which may be substituted, an alkoxyalkyl group which may be substituted, an oxycarbonylalkyl group which may be substituted, a carboxyalkyl group which may be substituted, an oxycarboxyalkyl group which may be substituted, or a cycloalkylalkyl group which may be substituted; provided that two mutually adjacent substituents R 1 through R 5 may form a ring; wherein R 1 represents a hydrogen atom, an alkyl group having from 1 to 8 carbon atoms, or a cycloalkyl group; R 2 represents a hydrogen atom, a halogen atom, an alkoxy group which may be substituted, an alkylthio group which may be substituted, or an arylthio group which may be substituted; and R 3 represents a branched alkyl group having from 3 to 5 carbon atoms, an o-substituted oxycarbonyl group, N-substituted aminocarbonyl group in which the N-substituent may form a ring, or a substituted or unsubstituted heterocyclic ring having at least two atoms selected from the group consisting of a nitrogen atom, an oxygen atom, a sulfur atom and combinations thereof, provided that when R 1 is hydrogen, R 3 is a branched alkyl group having from 3 to 5 carbon atoms, or a substituted heterocyclic ring having at least two atoms selected from the group consisting of an oxygen atom, a sulfur atom and combinations thereof; wherein Z represents an alkyl group which may be substituted, an aryl group which may be substituted, or a heterocyclic arly group which may be substituted; R represents an alkyl group which may be substituted, a cycloalkyl group which may be substituted, -R 2 , -COR 2 -OSO 2 R 2 , -CO·OR 2 , -OR 2 , -O·COR 2 , -SO 2 R 2 , an aryl group which may be substituted, or a heterocyclic aryl group which may be substituted; R 1 represents a hydrogen atom, an alkyl group which may be sustituted, an aryl group which may be substituted, a cyano group, a nitro group, a halogen atom, a heterocyclic aryl group, a cycloalkyl group which may be substituted, -R 2 , -COR 2 , -OSO 2 R 2 , -CO·OR 2 , -OR 2 , -O·COR 2 , or -SO 2 R 2 , wherein, when n is other than 1, R 1 may be the same or different; R 2 represents an alkyl group containing at least one group selected from the group consisting of -O-, -O·CO-, -CO·O-, -SO 2 -, -OSO 2 -, -NH-, -O·CO·O-, and -OH; and n represents an integer of from 1 to 5; wherein R 1 and R 3 each represents an alkyl group, a hydroxyalkyl group, an alkoxyalkyl group, an alkoxycarbonylalkyl group, an aralkyl group, an alkylcarboxyalkyl group, an alkylaminocarboxyalkyl group, a cycloalkylaminocarboxyalkyl group, a cyanoalkyl group, a cycoalkoxyaralkyl group, an alkoxycarboxyalkyl group, an aryloxycarboxyalkyl group, an alkoxycarbonylalkylcarbonyl alkyl group, a cycloalkylaryloxyalkyl group, a heteroarylalkyl group, an aryl group, an alkoxyalkyloxyalkyl group, or an alkylcarboxyalkoxyalkyl group; Z represents a hydrogen atom, a halogen atom, an alkyl group, or an alkoxy group; R5 represents a hydrogen atom, an alkyl group, an alkylcarbonylamino group, a hydroxy group, a hydroxyalkoxyalkylamino group, an alkoxyalkyloxycarbonylamino group, an alkylsulfonylamino group, or an alkoxycarbonyl group. In order to adjust hue, known yellow dyes, magenta dyes or cyan dyes can also be mixed. Dyes of the formulae (1) through (4) suitable for use in the preseent invention are shown in the following Tables 1 through 8 by expressing them by their substituents: Dye 1-3 No R 1 R 2 R 3 R 4 R 5 R 7 A 1 -H -H -H -H -H -C 2 H 5 -CONHC 2 H 5 2 -H -H -H -H -H -C 2 H 5 2-thiazolyl- 3 -H -H -H -H -H -C 2 H 5 2-pyridyl- 4 -H -H -H -H -H -C 2 H 5 2-benzoxazolyl- 5 -H -H -H -H -H -C 2 H 5 2-benzothiazolyl- 6 -H -H -H -H -H -C 2 H 5 3-ethyl-2-benzimidazolyl- 7 -H -H -H -H -H -C 2 H 5 3,3-dimethyl-3H-indol-2-yl- 8 -H -H -SPh -H -H -C 4 H 8 OH -CONHC 2 H 5 9 -H -H -CH 3 -H -H -C 4 H 8 OH -CONHC 2 H 5 10 -H -H -H -H -H -C 4 H 8 OH 3-ethyl-4,5-dicyano-2-imidazolyl- 11 -H -H -H -H -H -C 4 H 8 OH 5-(4-ethyl-3-cyano-1,2,4-triazolyl)- 12 -H -H -H -H -H -C 4 H 8 OH 2-(5-phenyl-1,3,4-oxadiazolyl)- 13 -H -H -H -H -Cl -C 4 H 8 OH 2-(5-phenyl-1,3,4-oxadiazolyl)- 14 -H -H -H -CONHC 2 H 4 OCH 3 -H -C 4 H 8 OH 2-benzothiazolyl- Dye 1-4 No R 7 X 1 -C 8 H 16 OH 1-phenyl-3-methyl-pyrazolin-5-one-4-ylindene- 2 -C 8 H 16 OH 1-phenyl-3-dimethylamino-pyrazolin-5-one-4-ylindene- 3 -C 8 H 16 OH 1,2-diphenyl-pyrazolidine-3,5-dione-4-ylindene- 4 -C 8 H 16 OH 1-butyl-3,3-dimethyl-2-indolinylidene- 5 -C 8 H 16 OH 3-ethyl-2-benzoxazolinylidene- 6 -C 8 H 16 OH 3-ethyl-2-bezothiazolinylidene- 7 -C 8 H 16 OH 4,6-diphenyl-2H-pyran-2-ylindene- 8 -C 8 H 16 OH 3-methyl-5-phenyl-2-oxadiazolinylidene- 9 -C 8 H 16 OH 3-methyl-5-phenyl-2-thiadiazolinylidene- 10 -C 8 H 16 OH 3-ethyl-4,5-dicyano-2-thiazolinylidene- 11 -C 8 H 16 OH 1,3-diethyl-2-benzimidazolinylidene- 12 -C 8 H 16 OH 1-butyl-2-pyridinylidene- 13 -C 8 H 16 OH 2-phenyl-thiazolin-4-one-5-ylindene- 14 -C 8 H 16 OH 2-diethylamino-thiazolin-4-one-5-ylindene- 15 -C 8 H 16 OH 1-butyl-3-phenyl-imidazolidine-2-thion-4-one-5-ylindene- 16 -C 8 H 16 OH benzo-[b]-thien-3-one-2-ylindene- 17 -C 8 H 16 OH 3-phenyl-thiazolidine-2-thion-4-one-5-ylindene- 18 -C 8 H 16 OH 3-phenyl-thiazolidine-2,4-dione-5-ylindene- 19 -C 8 H 16 OH 3-phenyl-oxazolidine-2-thion-4-one-5-indene- 20 -C 8 H 16 OH 1,3-diphenyl-hexahydropyrimidine-2,4,6-trione-5-ylindene- 21 -C 8 H 16 OH 2H-indene-1,3-dione-2-2-indene- 22 -C 8 H 16 OH 1-phenyl-4-pyridinylidene- Dye 1-5 No R 3 R 4 R 7 X 1 -H -CONHCH 3 -C 8 H 17 1-phenyl-3-methyl-pyrazolin -5-one-4-ylindene- 2 -SPh -H -C 8 H 16 OH 1-phenyl-3-dimethylamino-pyrazolin-5-one-4-ylindene- 3 -H -COOC 2 H 4 OC 2 H 5 -C 8 H 16 OH 1-phenyl-3-dimethylamino-pyrazolin-5-one-4-ylindene- 4 -Cl -H -C 8 H 16 OH 1,2-diphenyl-pyrazolidine-3,5 -dione-4-ylindene- 5 -H -Cl -C 8 H 16 OH 1,2-diphenyl-pyrazolidine-3,5 -dione-4-ylindene- 6 -H -SPh -C 8 H 16 OH 1-phenyl-3-methyl-pyrazolin -5-one-4-ylindene- While the amount of the dyes of the formulae (1) and (2) and the amount of the dyes of the formulae (3) and (4) can vary depending upon the respective specific dyes selected, they are preferably used in a weight ratio of from 10 : 90 to 90 : 10. If the proportion of the dye of the formulae (1) and (2) is larger, the color density will be reduced. If the proportion of the dye of the formulae (1) and (2) is smaller, the light fastness will be reduced. In order to adjust hue, known dyes can be mixed. In general, dyes such as diarylmethane dyes: triarylmethane dyes; thiazole dyes; methine dyes represented by merocyanine; azomethine dyes represented by indoaniline, acetophenoneazomethine, imidazoleazomethine, pyrazoloazomethine, imidazoleazomethine, and pyridoneazomethi ne; xanthene dyes; oxazine dyes; cyanomethylene dyes represented by dicyanostyrene and tricyanostyrene; thiazine dyes; azine dyes; acridine dyes; benzeneazo dyes; heterocyclic azo dyes represented by pyridoneazo, thiopheneazo, isothiazoleazo, pyrroleazo, pyrazoleazo, imidazoleazo, thiadiazoleazo, triazoleazo, and disazo, compounds; spirodipyran dyes; indolinospiropyran dyes; fluoran dyes; rhodamine lactam dyes; naphthoquinone dyes; anthraquinone dyes; and quinophalone dyes are typical. The following dyes can be preferably used: C.I. (COLOR INDEX) C.I. Disperse Yellow 51, 3, 54, 79, 60, 23, 7, 141, 201, and 231; Disperse Blue 24, 56, 14, 301, 334, 165, 19, 72, 87, 287, 154, 26 and 354; Disperse Red 135, 146, 59, 1, 73, 60 and 167; Disperse Violet 4, 13, 26, 36, 56 and 31; Disperse Orange 149; Solvent Violet 13; Solvent Black 3; Solvent Green 3; Solvent Yellow 56, 14, 16 and 29; Solvent Blue 70, 35, 63, 36, 50, 49, 111, 105, 97 and 11; Solvent fled 135, 81, 18, 25, 19, 23, 24, 143, 146, 182; and the like. Examples of such dyes include methine (cyanine) basic dyes such as monomethine, dimethine or trimethine dyes such as 3,3'-diethyloxathiacyanine iodide Astrazon Pink FG (manufactured by Bayer; C.I. 48015), 2,2'-carbocyanine (C.I. 808), Astraphylloxine FF (C.I. 48070), Astrazone Yellow 7GLL (C.I. Basic Yellow 21), Aizen Kachiron Yellow 3 GLH (manufactured by Hodogaya Kagaku; C.I. 48055) and Aizen Kachiron Red 6 BH (C.I. 48020); diphenylmethane basic dyes such as Auramine (C.I. 655); triphenylmethane basic dyes such as Malachite Green (C.I. 42700) Brilliant Green (C.I. 42040), Magenta (C.I. 42510), Metal Violet (C.I. 42535), Crystal violet (C.I. 42555), Methyl Green (C.I. 684) and, Victoria Blue B (C.I. 44045); xanthene basic dyes such as Pyronine G (C.I. 739), Rhodamine B (C.I. 45170), and Rhodamine 6G (C.I. 45160); acridine basic dyes such as Acridine Yellow G (C.I. 785), Leonine AL (C.I. 46075), benzoflavin (C.I.791) and affine (C.I. 46045; quinoneimine basic dyes such as Neutral Red (C.I. 50040), Astrazon Blue BGE/x 125 % (C.I. 51005) and Methylene Blue (C.I. 52015); and other basic dyes such as anthraquinone basic dyes having a quanternary ammonium group. The cyan dyes include Kayaset Blue 714 (manufactured by Nippon Kayaku. Solvent Blue 63), Phorone Brilliant Blue S-R (manufactured by Sand; Disperse Blue 354) and Waxoline AP-FW (manufactured by I.C.I.; Solvent Blue 36); the magenta dyes include MS-RED G (manufactured by Mitsui Toatsu; Disperse Red 60), Macrorex Red Violet R (manufactured by Bayer; disperse Violet 26); the yellow dyes include Phorone Brilliant Yellow S-6GL (manufactured by Sand; Disperse Yellow 231), and Macrorex Yellow-6G (manufactured by Bayer; Disperse Yellow 201); and dyes having the following skeleton can be used herein: These dyes can be used in the form such that they are intact. Alternatively, these dyes can be used in the form wherein they are treated with an alkali. Further, counter ion exchangers or leuco products of these dyes can be used. When leuco dyes which are colorless or light-colored under normal conditions, a developer is included in a thermal transfer image-receptive sheet. Sublimable yellow dyes described in Japanese Patent Laid-Open Publication Nos. 78,895/1984, 28,451/1985, 28,453/1985, 53,564/1985, 148,096/1986, 239,290/1985, 31,565/1985, 30,393/1985, 53,565/1985, 27,594/1985, 262,191/1986, 152,563/1985, 244,595/1986 and 196,186/1987, and International Publication No. WO 92/05032; sublimable magenta dyes described in Japanese Patent Laid-Open Publication Nos. 223,862/1985, 28,452/1985, 31,563/1985, 78, 896/1984, 31,564/1985, 30,391/1985, 227,092/1986, 227,091/1986, 30,392/1985, 30,394/1985, 131,293/1985, 227,093/1986, 159,091/1985 and 262,190/1986, U.S. Patent No. 4,698,651, Japanese Patent Application No. 220,793/1987 and U.S. Patent No. 5,079,365; and sublimable cyan dyes described in Japanese Patent Laid-Open Publication Nos. 78,894/1984, 227,490/1984, 151,098/1985, 227,493/1984, 244,594/1986, 227,948/1984, 131,292/1985, 172,591/1985, 151, 097/1985, 131,294/1985, 217,266/1985, 31,559/1985, 53,563/1985, 225,897/1986, 239,289/1985, 22,993/1986, 19,396/1986, 268,493/1986, 35,994/1986, 31,467/1986, 148,269/1986, 49,873/1986, 57,651/1986, 239,291/1985, 239,292/1985, 284,489/1986 and 191,191/1987, Japanese Patent Application No. 176, 625/1987, and U.S. Patent No. 5, 079,365 also are suitably used. More preferred dyes having the following general formulae are exemplified: wherein R 1 and R 2 represent a substituted or unsubstituted alkyl group, a substituted or unsubstituted cycloalkyl group, or a substituted or unsubstituted aralkyl group; R 3 represents a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkoxy group, a substituted or unsubstituted alkylcarbonylamino group, a substituted or unsubstituted alkylsulfonylamino group, a substituted or unsubstituted alkylaminocarbonyl group, substituted or unsubstituted alkylaminosulfonyl group, or a halogen atom; R 4 represents a substituted or unsubstituted alkoxycarbonyl group, a substituted or unsubstituted alkylaminocarbonyl group, a substituted or unsubstituted alkoxy group, a substituted or unsubstituted alkyl group, a substituted or unsubstituted cycloalkyl group, a heterocyclic group, or a halogen atom; R 5 represents a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkoxycarbonyl group, a substituted or unsubstituted alkylaminocarbonyl group, a substituted or unsubstituted alkoxy group, a substituted or unsubstituted alkylaminosulfonyl group, a substituted or unsubstituted cycloalkyl group, a cyano group, a nitro group or a halogen atom; R 6 represents a substituted or unsubstituted alkyl group, a substituted or unsubstituted aryl group, a substituted or unsubstituted amino group, a substituted or unsubstituted cycloalkyl group, a cyano group, a nitro group, or a halogen atom; R 7 represents a substituted or unsubstituted alkyl group, a substituted or unsubstituted amino group, a substituted or unsubstituted alkoxy group, a substituted or unsubstituted alkoxycarbonyl group, or a halogen atom; R 8 represents a substituted or unsubstituted aryl group, an aromatic heterocyclic group, a cyano group, a nitro group, a halogen atom, or an electron attractive group; R 9 represents CONHR 10 , SO 2 NHR 10 , NHCOR 11 , NHSO 2 R 11 or a halogen atom; R 10 represents a substituted or unsubstituted alkyl group, a substituted or unsubstituted cycloalkyl group, a substituted or unsubstituted aryl group, or a substituted or unsubstituted aromatic heterocyclic group; R 11 represents a substituted or unsubstituted alkyl group, a substituted or unsubstituted cycloalkyl group, a substituted or unsubstituted amino group, a substituted or unsubstituted aryl group, or a substituted or unsubstituted aromatic heterocyclic group; R 12 represents a substituted or unsubstituted alkyl group; R 13 represents an amino group or a hydroxyl group; X represents a halogen atom; and Y represents a substituted or unsubstituted aryl group or a substituted or unsubstituted aromatic heterocyclic group. The thermal transfer sheet of the present invention is characterized in that the specific dye mixture as described above is used. Other constitutions may be similar to those of the prior known thermal transfer sheets. Any prior known material may be used as the base sheet for use in the thermal transfer sheet of the present invention wherein the dye mixture described above is used, provided that the material has a certain measure of heat resistance and strength. Examples of such materials include materials having a thickness of the order of from 0.5 to 50 micrometers, preferably from 3 to 10 micrometers such as papers, various processed papers, polyester films, polystyrene films, polypropylene films, polysulfone films, polycarbonate films, aramid films, polyvinyl alcohol films, cellophane and the like. A particularly preferred material is a polyester film. A dye-containing layer provided on the surface of the base sheet as described above is a layer wherein the dye mixture described above is supported on the base sheet by an optional binder resin. Any prior known binder resin can be used as the binder resin for supporting the dye mixture described above. Examples of the preferred binder resins include cellulosic resins such as ethyl cellulose, hydroxyethyl cellulose, ethyl hydroxyethyl cellulose, hydroxypropyl cellulose, methyl cellulose, cellulose acetate and cellulose acetate butyrate; vinylic resins such as polyvinyl alcohol, polyvinyl acetate, polyvinyl butyral, polyvinyl acetoacetal, polyvinyl pyrrolidone, polyacrylamide and polystyrene; and the like. Of these, polyvinyl butyral and polyvinyl acetal are particularly preferred from the standpoints of heat resistance and dye migration. While the dye-containing layer of the thermal transfer sheet of the present invention is basically formed by the materials described above, it may include various additives similar to the prior known additives as needed. Such a dye-containing layer is preferably formed by adding the dye mixture, the binder resin and optional components to a suitable solvent to dissolve or disperse each component therein to prepare a coating solution or ink composition for forming the dye-containing layer, applying the coating solution or ink composition to the base sheet described above and drying the whole. The dye-containing layer thus formed has a thickness of the order of from 0.2 to 5.0 micrometers preferably from 0.4 to 2.0 micrometers. It is suitable that the dye mixture in the dye-containing layer be present in an amount of from 5% to 70% by weight, preferably from 10% to 60% by weight based on the weight of the dye-containing layer. While the present thermal transfer sheet as described above is sufficiently useful for thermal transfer as it is, the surface of the dye-containing layer may be provided with an antisticking layer i.e., a release layer. Such a layer prevents the sticking between the thermal transfer sheet and the transferable material during the thermal transfer operation. Thus, higher thermal transfer temperatures can be used, and images having an even more excellent density can be formed. When an antisticking inorganic powder is merely deposited, the resulting release layer exerts a relatively high effect. Further, a release layer having a thickness of from 0.01 to 5 micrometers, preferably from 0.05 to 2 micrometers can be formed from resins having excellent releasability such as silicone polymers, acrylic polmyers and fluorinated polymers. Even if the inorganic powder or releasing polymers as described above are included in the dye-containing layer, a sufficient effect can be obtained. Further, the back surface of such a thermal transfer sheet may be provided with a heat-resistant layer in order to prevent adverse effect due to the heat of the thermal head. Any transferable material may be used in forming images using the thermal transfer sheet as described above, provided that its recording surface has a dye receptivity against the dye described above. When the transferable materials are those having no dye receptivity such as papers, metals, glasses and synthetic resins, a dye-receptive layer may be formed on at least one surface thereof. Means for imparting a heat energy used in carrying out thermal transfer using the present thermal transfer sheet as described above and the recordable material as described above may be any of the prior known means. For example, a required purpose can be achieved by imparting a heat energy of the order of from 5 to 100 mJ/mm 2 by controlling the recording time with a recording device such as a thermal printer (e.g., Video Printer VY-100 manufactured by Hitachi Seisakusho). According to the thermal transfer sheet of the present invention, yellow images can be formed. Full color images having excellent color reproducibility can be provided by using the present thermal transfer sheet having the yellow dye-containing layer in combination with a thermal transfer sheet having a cyan dye-containing layer and a thermal transfer sheet having a magenta dye-containing layer. Alternatively, full color images having excellent color reproducibility can be provided by a thermal transfer sheet having a layer formed by superficially successively applying a cyan dye, the yellow dye and a magenta dye. Examples and Comparative Examples illustrate the present invention in more detail. Parts and percentages herein are by weight unless otherwise specified. REFERENCE EXAMPLE 1 16.9 grams of N-ethyl-benz[cd]indol-2(1H) one, 6 grams of malonitrile and 19.4 grams of phosphorus oxychloride were added to 150 mℓ of toluene. The resulting mixture was heated for 4 hours on a water bath with stirring and the reaction mixture was poured into 600 ml of methanol. A deposited crystal was filtered off. The crude product was recrystallized from a chloroform-methanol mixture to obtain a dye of No. 75 of dye 1-1. This dye was a yellow crystal having an absorption maximum wavelength of 441 nm (methanol) and a melting point of 196-197°C. REFERENCE EXAMPLE 2 9.3 grams of a quaternary salt represented by the formula: and 3.4 grams of ethyl cyanoacetate were added to 85 mℓ of acetonitrile. To the resulting mixture was added 5.3 mℓ of triethylamine, and the resulting mixture was heated for 1 hour under reflux. Thereafter, the solvent was distilled off and methanol was added. A crystal obtained was filtered off. This crude product was purified by a column using a silica gel to obtain a dye of No. 1 shown in Table 2. This dye was a yellow crystal having an absorption maximum wavelength of 454 nm (methylene chloride) and a melting point of 86-87 °C. REFERENCE EXAMPLE 3 Dyes shown in Tables 1 through 5 described above were obtained as in Reference Examples 1 and 2 except that starting materials corresponding to the dyes shown in Table 1 through 5. EXAMPLES 1 THROUGH 261 An ink composition for forming a dye-containing layer having the following composition was prepared. The ink composition was applied to a polyethylene terephthalate film having a thickness of 6 micrometers (wherein its back surface had been treated to provide heat resistance) so that the dry coating weight was 1.0 gram per square meter. The whole was dried to obtain a thermal transfer sheet of the present invention. Ink Composition Dye of the formula (1) or (2) "a" parts Dye of the formula (3) or (4) "b" parts Polyvinyl butyral resin 4.5 parts Methyl ethyl ketone 45.75 parts Toluene 45.75 parts When the dyes in the composition described above were insoluble, a solvent such as DMF, dioxane or chloroform was suitably used. (The dyes used and their amounts ("a", "b") are shown in the following Table 9.) Synthetic paper (Yupo FPG #150 manufactured by Oji Yuka) was used as a base sheet. A coating solution having the following compositon was applied to the one surface of the base sheet so that its dry coating weight was 10.0 grams per square meter. The whole was dried for 30 minutes at 100°C to obtain a transferable material. Polyester resin (Vylon 200 11.5 parts manufactured by Toyobo) Vinyl chloride-vinyl acetate copolymer 5.0 parts (VYHH manufactured by U.C.C.) Amino-modified silicone (KF-393 1.2 part manufactured by Shin-etsu Kagaku Kogyo) Epoxy-modified silicone (X-22-343 1.2 part manufactured by Shin-etsu Kagaku Kogyo) Methyl ethyl ketone/toluene/cyclohexanone 102.0 parts (weight ratio of 4:4:2) Thermal Transfer Recording Test The present thermal transfer sheet described above and the transferable material described above were stacked with the dye-containing layer opposing to the dye-receptive surface. Recording was carried out by means of a thermal head from the back surface of the thermal transfer sheet under a head application voltage of 11 V for an application time of 16 msec. The results are shown in Table 9. Light Fastness Test A light fastness test of the yellow images obtained in the thermal transfer test described above was carried out by means of a xenon fadeometer (Ci 35 A manufactured by Atlas) (the black panel temperature being 50°C and the illuminance being 50 kLux). In any case, discoloration and fading did not occur when the irradiation time was 50 hours. Measurement of Color Density The color density was measured by means of a densitometer RD-918 manufactured by U.S. Macbeth Company. COMPARATIVE EXAMPLES 1 THROUGH 20 Example 1 was repeated except that the following dyes were used in place of the dye described in Example. The results are shown in Table 10. Dye of the formulae 1 through 4 "a" parts Polyvinyl butyral resin 4.5 parts Methyl ethyl ketone 46.25 parts Toluene 46.25 parts Com. Ex. Dye Color Density Light Fastness Formula and Number Amount used "a" 1 1-1-1 4.0 1.79 ○ 2 1-1-12 3.0 1.61 ○ 3 1-1-23 2.5 1.53 ○ 4 1-1-45 3.0 1.63 ○ 5 1-2-11 3.0 1.54 ○ 6 1-2-24 3.0 1.74 ○ 7 1-2-45 3.0 1.65 ○ 8 1-2-74 2.5 1.64 ○ 9 1-4-3 2.0 1.74 ○ 10 1-5-4 2.0 1.59 ○ 11 1-6-2 3.0 1.71 ○ 12 2-1 3.0 2.63 X 13 2-4 3.0 2.43 X 14 3-28 3.5 2.41 X 15 3-43 2.0 1.89 X 16 3-59 2.0 1.97 X 17 4-1 2.5 2.30 X 18 4-14 3.0 2.18 X 19 4-23 3.0 2.39 X 20 4-31 3.5 1.98 X According to the present invention as described above, there can be provided the thermal transfer sheets capable of providing full color images having excellent color density, clearness and fastnesses, particularly light fastness by using the mixture of the spesific dyes even if a heat energy is applied for an extremely short period of time.

Claims: A thermal transfer sheet comprising a base sheet and a dye-containing layer formed on one surface of said base sheet wherein said dye-containing layer comprises a yellow dye, said yellow dye being a mixture of at least one dye represented by the following formulae (1) and (2): wherein X represents or which represents a five or six-membered ring reaction residue represented by which may have a fused ring; A represents an electron attractive group; Z represents -CO-, -NR 6 -, -S-, -O- or -NH-; R 1 represents a hydrogen atom, R 6 , a halogen atom, a nitro group, -OR 6 , -SR 6 or an allyl group which may be sustituted; R 2 represents a hydrogen atom, a halogen atom, -OR 6 or -SR 6 ; R 3 represents a hydrogen atom, R 6 , a halogen atom, a nitro group, an allyl group which may be substituted, -OR 6 , -SR 6 , a sulfamoyl group,a carbamoyl group, an acyl group, an acylamide group, a sulfonamide group, an ureido group, or -NR 6 R 6 , wherein R 6 may be the same or different; R 4 represents a hydrogen atom, a halogen atom, -OR 6 , -SR 6 , a cyano group, -COOR 6 , a carbamoyl group, or a sulfamoyl group; R 5 represents a hydrogen atom, a halogen atom, -OR 6 , or -SR 6 ; R 6 represents an alkyl group which may be substituted, an aryl group which may be substituted, a cycloalkyl group which may be substituted, or a heterocyclic ring which may be substituted; and R 7 represents a hydrogen atom, -R 6 , an allyl group which may be substituted, an alkenyl group which may be substituted, a heteroalkenyl group which may be substituted, an arylalkyl group which may be substituted, an alkoxyalkyl group which may be substituted, an oxycarbonylalkyl group which may be substituted, a carboxyalkyl group which may be substituted, an oxycarboxyalkyl group which may be substituted, or a cycloalkylalkyl group which may be substituted; provided that two mutually adjacent substituents R 1 through R 5 may form a ring; wherein R 1 represents a hydrogen atom, an alkyl group having from 1 to 8 carbon atoms, or a cycloalkyl group; R 2 represents a hydrogen atom, a halogen atom, an alkoxy group which may be substituted, an alkylthio group which may be substituted, or an arylthio group which may be substituted; and R 3 represents a branched alkyl group having from 3 to 5 carbon atoms, an o-substituted oxycarbonyl group, N-substituted aminocarbonyl group in which the N-substituent may form a ring, or a substituted or unsubstituted heterocyclic ring having at least two atoms selected from the group consisting of a nitrogen atom, an oxygen atom, a sulfur atom and combinations thereof, provided that when R 1 is hydrogen, R 3 is a branched alkyl group having from 3 to 5 carbon atoms, or a substituted heterocyclic ring having at least two atoms selected from the group consisting of an oxygen atom, a sulfur atom and combinations thereof; with at least one dye represented by the following formulae (3) and (4): wherein Z represents an alkyl group which may be substituted, an aryl group which may be substituted, or a heterocyclic aryl group which may be substituted; R represents an alkyl group which may be substituted, a cycloalkyl group which may be substituted, -R 2 , -COR 2 , -OSO 2 R 2 , -CO·OR 2 , -OR 2 , -O·COR 2 , -SO 2 R 2 , an aryl group which may be substituted, or a heterocyclic aryl group which may be substituted; R 1 represents a hydrogen atom, an alkyl group which may be substituted, an aryl group which may be substituted, a cyano group, a nitro group, a halogen atom, a heterocyclic aryl group, a cycloalkyl group which may be substituted, -R 2 , -COR 2 , -OSO 2 R 2 , -CO·OR 2 , -OR 2 , -O·COR 2 , or -SO 2 R 2 , wherein, when n is other than 1, R 1 may be the same or different; R 2 represents an alkyl group containing at least one group selected from the group consisting of -O-, -O·CO-, -CO·O-, -SO 2 -, -OSO 2 -, -NH-, -O·CO·O-, and -OH; and n represents an integer of from 1 to 5; wherein R 1 and R 3 each represents an alkyl group, a hydroxyalkyl group, an alkoxyalkyl group, an alkoxycarbonylalkyl group, an aralkyl group, an alkylcarboxyalkyl group, an alkylaminocarboxyalkyl group, a cycloalkylaminocarboxyalkyl group, a cyanoalkyl group, a cycoalkoxyaralkyl group, an alkoxycarboxyalkyl group, an aryloxycarboxyalkyl group, an alkoxycarbonylalkylcarbonyl alkyl group, a cycloalkylaryloxyalkyl group, a heteroarylalkyl group, an aryl group, an alkoxyalkyloxyalkyl group, or an alkylcarboxyalkoxyalkyl group; Z represents a hydrogen atom, a halogen atom, an alkyl group, or an alkoxy group; R5 represents a hydrogen atom, an alkyl group, an alkylcarbonylamino group, a hydroxy group, a hydroxyalkoxyalkylamino group, an alkoxyalkyloxycarbonylamino group, an alkylsulfonylamino group, or an alkoxycarbonyl group.

Inventors: EGUCHI HIROSHI, KAFUKU KOMEI, TAKIGUCHI RYOHEI, EGUCHI, HIROSHI, KAFUKU, KOMEI, TAKIGUCHI, RYOHEI, Eguchi, Hiroshi, c/o Dai Nippon Printing Co., Ltd., Kafuku, Komei, c/o Dai Nippon Printing Co., Ltd., Takiguchi, Ryohei, c/o Dai Nippon Printing Co. Ltd
Applicants: DAINIPPON PRINTING CO LTD, DAI NIPPON PRINTING CO., LTD.
Application year: 1992
Main classification: B41M5
IPC codes: B41M5