Process for producing a styrenic polymer

Abstract: There are disclosed a catalyst which comprises a specific transition-metal compound (A) and a specific coordination complex compound (B) instead of aluminoxane, and a process for producing a styrene polymer at a reduced cost with improved efficiency by the use of the above catalyst. The catalyst according to the present invention is inexpensive compared with the conventional catalyst containing aluminoxane as the major ingredient, and exhibits a high activity in the polymerization of a styrenic monomer into styrene polymer with a high degree of syndiotacticity as well as a high yield and conversion rate.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a process for producing a styrenic polymer. More particularly, it pertains to a process for efficiently producing a styrenic polymer having a high degree of syndiotactic configuration in the stereochemical structure of the polymer main chain. 2. Description of the Related Arts It has recently been disclosed by the research group of the present inventors that a styrenic polymer having a syndiotactic configuration is obtained by polymerizing a styrenic monomer by the use of a catalyst comprising as primary ingredients a transition-metal compound, especially a titanium compound and an alkylaluminoxane (Refer to Japanese Patent Application Laid-Open Nos. 187708/1987, 179906/1988, and 241009/1988). Methylaluminoxane, particularly suitable as an alkylaluminoxane is obtained usually by the reaction between trimethylaluminum and water. However, the above-mantioned reaction involves the problem that the reaction is difficult to put into practical production because of its violent reaction, and further suffers the disadvantage that in addition to requiring expensive trimethylaluminum as the starting material, an excessively large amount of methylaluminoxane is required as a component of the catalyst as compared with the quantity of a transition metal, thus causing an extremely expensive catalyst. There has recently been reported that a polymerization catalyst not containing aluminoxane is capable of polymerizing α-olefin (principally, ethylene) by R. Taube (J. Organomet. Chem. C9-C11, 347 (1988)), H. Turner (J. Am. Chem. Soc. 111,2728 (1989)), R.F. Jordan (Organomet. 8,2892 (1989)). Nevertheless, investigation has not yet been made on a polymerization catalyst not containing aluminoxane for the polymerization of styrenic monomer, leaving the problem that styrenic monomer, different from α-olefin, is likely to be polymerized into an atactic polymer in the presence of a cationic species. SUMMARY OF THE INVENTION It is an object of the present invention to provide a process for effectively producing a styrenic polymer having a high degree of syndiotactic configuration. Other objects of the present invention will be obvious from the text of the specification hereinafter disclosed. As the result of intensive research and investigation made by the present inventors for the purpose of attaining the above-described object, it has been found that the use of a catalyst combination comprising a specific transition-metal compound and a specific coordination complex compound is capable of efficiently producing the objective styrenic polymer having a high degree of syndiotactic configuration by virtue of its markedly improved activity. The present invention has been accomplished on the basis of the aforestated finding and information. Specifically, the present invention uses a catalyst which comprises as primary ingredients (A) a titanium compound and (B) a coordination complex compound comprising an anion in which a plurality of redicals are bonded to a metal and a nitrogen-containing cation having an acid dissociation constant at 25°C of 7 or less. The present invention also provides a process for producing a styrenic polymer which comprises polymerizing styrene and/or a styrene derivative in the presence of the foregoing catalyst. DESCRIPTION OF PREFERRED EMBODIMENTS The catalyst used according to the present invention comprises as the primary ingredients, components (A) and (B). The titanium component (A) is represented by the formula: TiRXYZ wherein R represents a cyclopentadienyl group, a substituted cyclopentadienyl group or an indenyl group; a substituted indenyl group or a fluorenyl group; X, Y and Z are independently a hydrogen atom, an alkyl group having 1 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, an aryl group having 6 to 20 carbon atoms, an aryloxy group having 6 to 20 carbon atoms, an arylalkyl group having 7 to 20 carbon atoms or a halogen atom. The substituted cyclopentadienyl group represented by R in the above formula is, for example, a cyclopentadienyl group substituted by at least one of an alkyl group having 1 to 6 carbon atoms, more specifically, methylcyclopentadienyl group, 1,2-dimethylcyclopentadienyl group, 1,2,4-trimethylcyclopentadienyl group, 1,2,3,4-tetramethylcyclopentadienyl group, trimethylsilylcyclopentadienyl group, 1,3-di(trimethylsilyl)cyclopentadienyl group, tert-butylcyclopentadienyl group, 1,3-di(tert-butyl)cyclopentadienyl group or pentamethylcyclopentadienyl group. In addition, X, Y and Z are each independently a hydrogen atom, an alkyl group having 1 to 12 carbon atoms (specifically, methyl group, ethyl group, propyl group, n-butyl group, isobutyl group, amyl group, isoamyl group, octyl group and 2-ethylhexyl group), an alkoxy group having 1 to 12 carbon atoms (specifically, methoxy group ethoxy group, propoxy group, butoxy group, amyloxy group, hexyloxy group, octyloxy group and 2-ethylhexyl group), an aryl group having 6 to 20 carbon atoms (specifically, phenyl group and naphthyl group), an aryloxy group having 6 to 20 carbon atoms (specifically, phenoxy group), an arylalkyl group having 7 to 20 carbon atoms (specifically, benzyl group) or a halogen atom (specifically, chlorine, bromine, iodine and fluorine). Specific examples of the titanium component represented by the formula (VIII) include cyclopentadienyltrimethyltitanium, cyclopentadienyltriethyltitanium, cyclopentadienyltripropyltitanium, cyclopentadienyltributyltitanium, methylcyclopentadienyltrimethyltitanium, 1,2-dimethylcyclopentadienyltrimethyltitanium, 1,2,4-trimethylcyclopentadienyltrimethyltitanium, 1,2,3,4-tetramethylcyclopentadienyltrimethyltitanium, pentamethylcyclopentadienyltrimethyltitanium, pentamethylcyclopentadienyltriethyltitanium, pentamethylcyclopentadienyltripropyltitanium, pentamethylcyclopentadienyltributyltitanium, cyclopentadienylmethyltitanium dichloride, cyclopentadienylethyltitanium dichloride, pentamethylcyclopentadienylmethyltitanium dichloride, pentamethylcyclopentadienylethyltitanium dichloride, cyclopentadienyldimethyltitanium monochloride, cyclopentadienyldiethyltitanium monochloride, cyclopentadienyltitanium trimethoxide, cyclopentadienyltitanium triethoxide, cyclopentadienyltitanium tripropoxide, cyclopentadienyltitanium triphenoxide, pentamethylcyclopentadienyltitanium trimethoxide, pentamethylcyclopentadienyltitanium triethoxide, pentamethylcyclopentadienyltitanium tripropoxide, pentamethylcyclopentadienyltitanium tributoxide, pentamethylcyclopentadienyltitanium triphenoxide, cyclopentadienyltitanium trichloride, pentamethylcyclopentadienyltitanium trichloride, cyclopentadienylmethoxytitanium dichloride, cyclopentadienyldimethoxytitanium monochloride, pentamethylcyclopentadienylmethoxytitnaium dichloride, cyclopentadienyltribenzyltitanium, pentamethylcyclopentadienyltribenzyltitanium, pentamethylcyclopentadienylmethyldiethoxytitanium, indenyltitanium trichloride, indenyltitanium trimethoxide, indenyltitanium triethoxide, indenyltrimethyltitanium and indenyltribenzyltitanium. Of these titanium compounds, a compound not containing halogen atom is preferred. Furthermore, the above titanium compounds can be used in the form of a complex formed with an ester or an ether. The component (B) which constitutes the primary ingredients of the catalyst together with the above mentioned component (A) is a coordination complex compound comprising an anion in which a plurality of radicals are bonded to a metal and a nitrogen-containing cation having an acid dissociation constant at 25°C of 7 or less. A variety of such coordination complex compounds are available. The anion in which a plurality of radicals are bonded to a metal is exemplified by those represented by the following general formula (VI): (M 2 X 1 X 2 ---X n ) (n-m)- wherein M 2 is a metal selected from Groups 5 to 15 of the Periodic Table; X 1 to X n are each a hydrogen atom, dialkylamino group, alkoxy group, aryloxy group, alkyl group having 1 to 20 carbon atoms, aryl group having 6 to 20 carbon atoms, alkylaryl group, arylalkyl group, substituted alkyl group, organometalloid group or halogen atom; m is the valency of M 2 , indicating an integer of 1 to 7; and n is an integer of 2 to 8. Specific examples of M 2 include B, Al, Si, P, As and Sb. Specific examples of X 1 to X n include dialkylamino group such as dimetylamino and diethylamino; alkoxyl group such as methoxy, ethoxy and n-butoxy; aryloxy group such as phenoxy, 2,6-dimethylpheoxy and naphthyloxy; alkyl group having 1 to 20 carbon atoms such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, n-octyl and 2-ethylhexyl; aryl group having 6 to 20 carbon atoms, alkylaryl group or arylalkyl group such as phenyl, p-tolyl, benzyl, pentafluorophenyl, 3,5-di(trifluoromethyl)phenyl, 4-tert-butylphenyl, 2,6-dimethylphenyl, 3,5-dimethylphenyl, 2,4-dimethylphenyl and 1,2-dimethylphenyl; halogen such as F, Cl, Br and I; and organometalloid such as pentamethylantimony group, trimethylsilyl group, trimethylgermyl group, diphenylarsine group, dicyclohexylantimony group and diphenylboron group. A variety of nitrogen-containg cations having an acid dissociation constant at 25°C (especially in an aqueous solution) of 7 or less are available and exemplified by pyridinium, 2,4-dinitro-N,N-diethylanilinium, diphenylammonium, p-nitroanilinium, 2,5-dichloroaniline, p-nitro-N,N-dimethylanilinium, quinolinium, N,N-dimethylanilinium, N,N-diethylanilinium, methyldiphenylammonium, 8-chloroquinolinium, etc. The component (B) of the catalyst according to the present invention is the coordination complex compound constituted of the combination of the cation and anion as described above. Among them, examples of preferably usable compounds include N,N-diethylanilinium tetra(pentafluorophenyl)borate, 8-chloroquinolinium tetra(pentafluorophenyl)borate, o-chloroanilinium(hexafluoro) arsenate, pyridinium tetra(pentafluorophenyl)borate, pyrrolinium tetra(pentafluorophenyl)borate, N,N-dimethylanilinium tetra(pentafluorophenyl)borate, and methyldiphenylammonium tetra(pentafluorophenyl)borate. The catalyst used according to the present invention further comprises, as required, (C) a compound having an alkyl group. A variety of compounds having an alkyl group are available, and aluminum compounds having an alkyl group represented by the general formula (VII) are exemplified. R 11 p Al(OR 12 ) q X 1 3-p-q wherein R 11 and R 12 are each an alkyl group having 1 to 8, preferably 1 to 4 carbon atoms; X 1 is a hydrogen atom or a halogen atom; p satisfies the relation 0<p≦3, desirably p=2 or 3, more desirably p=3; and q satisfies the relation 0≦q<3, desirably q=0 or 1. Also exemplified are magnesium compounds having an alkyl group represented by the general formula (VIII) R 11 2 Mg wherein R 11 and R 12 represents the same as above, zinc compounds having an alkyl group represented by the general formula (IX) R 11 2 Zn wherein R 11 represents the same as above, and the like. The above-mentioned compounds having an alkyl group are desirably aluminum compounds having an alkyl group, more desirably trialkylaluminum compounds and dialkylaluminum compounds. Examples of (C) the compounds having an alkyl group to be used in the present invention include trialkylaluminum such as trimethylaluminum, triethylaluminum, tri-n-propylaluminum, triisopropylaluminum, tri-n-butylaluminum, triisobutylaluminum and tri-tert-butylaluminum; dialkylaluminum halide such as dimethylaluminum chloride, diethylaluminum chloride, di-n-propylaluminum chloride, diisopropylaluminum chloride, di-n-butylaluminum chloride, diisobutylaluminum chloride and di-tert-butylaluminum chloride; dialkylaluminum alkoxide such as dimethylaluminum methoxide and dimethylaluminum ethoxide; dialkylaluminum hydride such as dimethylaluminum hydride, diethylaluminum hydride and diisobutylaluminum hydride; dialkylmagensium such as dimethylmagnesium, diethylmagnesium, di-n-propylmagnesium and diisopropylmagnesium; and dialkylzinc such as dimethylzinc, diethylzinc, di-n-propylethylzinc and diisopropylzinc. The catalyst used in the present invention comprises the components (A) and (B) and optionally the component (C) a compound having an alkyl group, each as a primary ingredient, and if desired, may be incorporated with other componets. The compounding ratios of the components (A), (B) and (C) vary depending on the several conditions and can not be unequivocally determined. As a general rule, however, the molar ratio of the component (A) to the component (B) is 0.1 : 1 to 1 : 0.1, and that of the component (A) to the component (C) is 1 : 0.1 to 1 : 1000. As described herebefore, the catalyst used according to the present invention exhibits a high activity for the production of a styrene polymer having a high degree of syndiotactic configuration. Hence, the present invention provides a process for producing a styrene polymer having a high degree of syndiotactic configuration by the use of the above-stated catalyst. The production of a styrene polymer according to the process of the present invention is put into practice by polymerizing or copolymerizing styrenic monomers such as styrene and/or a styrene derivative exemplified by an alkylstyrene, alkoxystyrene, halogenated styrene, and vinyl benzoate. in the presence of the catalyst comprising the foregoing components (A) and (B) and optionally the component (C) each as an essential component. There are available a variety of methods for bringing the catalyst into contact with a styrenic monomer, or monomers, including: (1) A method in which the reaction product of the components (A) and (B) as the catalyst is brought into contact with a monomer or monomers to be polymerized; (2) A method in which the component (C) is added to the reaction product of the components (A) and (B) to prepare the catalyst, which is then brought into contact with a monomer or monomers to be polymerized; (3) A method in which the component (B) is added to the reaction product of the components (A) and (C) to prepare the catalyst, which is then brought into contact with a monomer or monomers to be polymerized; and (4) A method in which each of the components (A), (B) and (C) is added to a monomer or monomers one by one in any order. The reaction product of the components (A) and (B) may be isolated and purified in advance. The polymerization of a styrenic monomer or monomers may be carried out by means of bulk polymerization or solution polymerization by the use of an aliphatic hydrocarbon solvent such as pentane, hexane or heptane, an alicyclic hydrocarbon solvent such as cyclohexane or an aromatic hydrocarbon solvent such as benzene, toluene or xylene. The polymerization temperature is not specifically limited, but is usually in the range 0 to 90°C, preferably 20 to 70°C. The molecular weight of the styrene polymer to be obtained can be effectively modified by means of polymerization reaction in the presence of hydrogen. The styrene polymer thus obtained possesses a high degree of syndiotactic configuration. Here, the styrene polymer having a high degree of syndiotactic configuration means that its stereochemical structure is mainly of syndiotactic configuration, i.e. the stereostructure in which phenyl groups or substituted phenyl group as side chains are located alternately at opposite directions relative to the main chain consisting of caron-carbon bonds. Tacticity is quantitavely determined by the nuclear magnetic resonance method ( 13 C-NMR method) using carbon isotope. The tacticity as determined by the 13 C-NMR method can be indicated in terms of proportions of structural units continuously connected to each other, i.e., a diad in which two structural units are connected to each other, a triad in which three structural units are connected to each other and a pentad in which five structural units are connected to each other. "The styrene polymers having a high degree of syndiotactic configuration" as mentioned in the present invention means polystyrene, poly(alkylstyrene), poly(halogenated styrene), poly(alkoxystyrene), poly(vinyl benzoate), the mixtures thereof, and copolymers containing the above polymers as main components, having such a syndiotacticity that the proportion of racemic diad is at least 75%, preferably at least 85%, or the proportion of racemic pentad is at least 30%, preferably at least 50%. The poly(alkylstyrene) include poly(methylstyrene), poly(ethylstyrene), poly(isopropylstyrene), poly(tert-butylstyrene), poly(halogenated styrene) include, poly(chlorostyrene), poly(bromostyrene), and poly(fluorostyrene). The poly(alkoxystyrene)include, poly(methoxystyrene), and poly(ethoxystyrene). The most desirable styrene polymers are polystyrene, poly(p-methylstyrene), poly(m-methylstyrene), poly(p-tert-butylstyrene), poly(p-chlorostyrene), poly(m-chlorostyrene), poly(p-fluorostyrene), and the copolymer of styrene and p-methylstyrene. The styrene polymer obtained according to the process of the present invention is that with a high degree of syndiotaticity usually having a weight-average molecular weight of 10,000 to 3,000,000, preferably 100,000 to 1,500,000 with a number-average molecular weight of 5,000 to 1,500,000, preferably 50,000 to 1,000,000. Moreover, the styrene polymer having an exceptionally high degree of syndiotacticity as well as an extremely high purity can be obtained by the steps of deashing treatment of the polymer thus obtained, as required, with a washing agent containing hydrochloric acid; additional washing; drying under reduced pressure; cleaning with a solvent such as methyl ethyl ketone for removing solubles therein; and treatment of the insolubles thus oftained by the use of chloroform. The styrene polymer with a high degree of syndiotacticity has a melting point of 160 to 310°C and is remarkably superior to the conventional styrene polymer with an atactic configuration in terms of heat resistance. The catalyst used according to the present invention is inexpensive as compared with the conventional catalyst comprising an aluminoxane as a primany ingredient, exhibits a high activity for the production of a styrene polymer having a high degree of syndiotactic configuration, and is capable of minimizing the total residual content of metallic components and simplifying the production process of the polymer. According to the process of the present invention, therefore, a syndiotactic styrene polymer is obtained at a reduced production cost and with an enhanced efficiency. The present invention will be described in more detail with reference to the following nonlimiting Examples and Comparative Examples. Example 1 In a 20 ml vessel which had been dried and purged with nitrogen were placed 10 ml of styrene, 15 µmol of triisobutylaluminum and 0.25 µmol of N,N-dimethylanilinium tetra(pentafluorophenyl)borate (DMAB) having an acid dissociation constant pKa of 5.2. After one (1) minute, 0.25 µmol of pentamethylcyclopentadienyltrimethyltitanium was gradually added to the resultant mixture to effect polymerization at 70°C for 4 hours. After the completion of the reaction, the reaction product was dried to obtain 3.25 g of polymer, which was sliced to a thickness of 1 mm or less and subjected to extraction with a Soxhlet extractor for 6 hours using methyl ethyl ketone as the solvent to obtain an extraction residue (methyl ethyl ketone insoluble portion; MIP) of 96% by weight. As the result, syndiotactic polystyrene (SPS) was obtained with a yield of 3.12 g, an activity of 261 (kg/g Ti) and a total residual content of metallic components of 133 ppm. Example 2 The procedure in Example 1 was repeated except that 0.25 µmol of pyridinium tetra(pentafluorophenyl)borate (PAB) having an acid dissociation constant pKa of 5.2 was used in place of DMAB, and 0.25 µmol of pentamethylcyclopentadienyl-tribenzyltitanium was used in place of pentamethylcyclopentadienyl-trimethyltitanium to obtain 3.27 g of polymer. The polymer thus obtained was sliced to a thickness of 1 mm or less and subjected to extraction with a Soxhlet extractor for 6 hours using methyl ethyl ketone as the solvent to obtain an extraction residue (methyl ethyl ketone insoluble portion; MIP) of 96% by weight. As the result, SPS was obtained with a yield of 3.14 g, an activity of 263 (kg/g Ti) and a total residual content of metallic components of 133 ppm. Example 3 The procedure in Example 1 was repeated except that 0.25 µmol of m-nitrophenyldimethylammonium tetra(pentafluorophenyl)borate (MNAB) having an acid dissociation constant pKa of 3.0 was used in place of DMAB to obtain 2.21 g of polymer. The polymer thus obtained was sliced to a thickness of 1 mm or less and subjected to extraction with a Soxhlet extractor for 6 hours using methyl ethyl ketone as the solvent to obtain an extraction residue (methyl ethyl ketone insoluble portion; MIP) of 93% by weight. As the result, SPS was obtained with a yield of 2.06 g, an activity of 172 (kg/g Ti) and a total residual content of metallic components of 202 ppm. Example 4 The procedure in Example 1 was repeated except that 0.25 µmol of p-bromophenyldimethylammonium tetra(petnafluorophenyl)borate (PBAB) having an acid dissociation constant pKa of 4.3 was used in place of DMAB to obtain 3.34 g of polymer. The polymer thus obtained was sliced to a thickness of 1 mm or less and subjected to extraction with a Soxhlet extractor for 6 hours using methyl ethyl ketone as the solvent to obtain an extraction residue (methyl ethyl ketone insoluble portion; MIP) of 95% by weight. As the result, SPS was obtained with a yield of 3.17 g, an activity of 265 (kg/g Ti) and a total residual content of metallic components of 131 ppm. Example 5 The procedure in Example 1 was repeated except that triisobutylaluminum was not used to obtain 0.67 g of polymer. The polymer thus obtained was sliced to a thickness of 1 mm or less and subjected to extraction with a Soxhlet extractor for 6 hours using methyl ethyl ketone as the solvent to obtain an extraction residue (methyl ethyl ketone insoluble portion; MIP) of 95% by weight. As the result, SPS was obtained with a yield of 0.63 g, an activity of 53 (kg/g Ti) and a total residual content of metallic components of 18 ppm. Example 6 The procedure in Example 1 was repeated except that 0.25 µmol of pentamethylcyclopentadienyltitanium trimethoxide was used in place of pentamethylcyclopentadienyltrimethyltitanium to obtain 2.53 g of polymer. The polymer thus obtained was sliced to a thickness of 1 mm or less and subjected to extraction with a Soxhlet extractor for 6 hours using methyl ethyl ketone as the solvent to obtain an extraction residue (methyl ethyl ketone insoluble portion; MIP) of 95% by weight. As the result, SPS was obtained with a yield of 2.41 g, an activity of 201 (kg/g Ti) and a total residual content of metallic components of 173 ppm. Example 7 In a 20 ml vessel which had been dried and purged with nitrogen were placed 10 ml of styrene, 8 µmol of triisobutylaluminum, 0.25 µmol of pentamethylcyclopentadienyltrimethyltitanium and 0.25 µmol dimethylanilinium tetra(pentafluorophenyl)borate (DMAB) having an acid dissociation constant pKa of 5.2 to effect polymerization at 70°C for 4 hours. After the completion of the reaction, the reaction product was dried to obtain 3.01 g of polymer, which was sliced to a thickness of 1 mm or less and subjected to extraction with a Soxhlet extractor for 6 hours using methyl ethyl ketone as the solvent to give an extraction residue (methyl ethyl keton insoluble portion; MIP) of 97% by weight. As the result, syndiotactic polystyrene (SPS) was obtained with a yield of 2.91 g, an activity of 243 (kg/g Ti) and a total residual content of metallic components of 78 ppm. Comparative Example 1 The procedure in Example 1 was repeated except that ferrocenium tetra(pentafluorophenyl)borate (FCB) was used in place of DMAB, obtain 5.92 g of polymer. The polymer thus obtained was sliced to a thickness of 1 mm or less and subjected to extraction with a Soxhlet extractor for 6 hours using methyl ethyl ketone as the solvent to obtain an extraction residue (methyl ethyl ketone insoluble portion; MIP) of 42% by weight. As the result, SPS was obtained with a yield of 2.53 g, an activity of 211 (kg/g Ti) and a total residual content of metallic components of 96 ppm. Comparative Example 2 The procedure in Example 7 was repeated except that 0.25 µmol of triethylammonium tetra(pentafluorophenyl)borate (TEAB) having an acid dissociation contact pKa of 10.9 was used in place of DMAB to obtain 1.72 g of polymer. The polymer thus obtained was sliced to a thickness of 1 mm or less and subjected to extraction with a Soxhlet extractor for 6 hours using methyl ethyl ketone as the solvent to obtain an extraction residue (methyl ethyl ketone insoluble portion; MIP) of 93% by weight. As the result, SPS was obtained with a yield of 1.60 g, an activity of 134 (kg/g Ti) and a total residual content of metallic components of 142 ppm. Comparative Example 3 The procedure in Example 1 was repeated except that FCB was used in place of DMAB and triisobutylaluminum was not used to obtain 0.56 g of polymer. The polymer thus obtained was sliced to a thickness of 1 mm or less and subjected to extraction with a Soxhlet extractor for 6 hours using methyl ethyl ketone as the solvent to obtain an extraction residue (methyl ethyl ketone insoluble portion; MIP) of 75% by weight. As the result, SPS was obtained with a yield of 0.42 g, an activity of 35 (kg/g Ti) and a total residual content of metallic components of 61 ppm. Comparative Example 4 The procedure in Example 1 was repeated except that 0.25 mol of tri-n-butylammonium tetra(pentafluorophenyl)borate (TBAB) having an acid dissociation constant pKa of 9.9 was used in place of DMAB to obtain 1.10 g of polymer. The polymer thus obtained was sliced to a thickness of 1 mm or less and subjected to extraction with a Soxhlet extractor for 6 hours using methyl ethyl ketone as the solvent to obtain an extraction residue (methyl ethyl ketone insoluble portion; MIP) of 92% by weight. As the result, SPS was obtained with a yield of 1.01 g, an activity of 84 (kg/g Ti) and a total residual content of metallic components of 421 ppm. Comparative Example 5 The procedure in Example 7 was repeated except that FCB was used in palce of DMAB to obtain 2.98 g of polymer. The polymer thus obtained was sliced to a thickness of 1 mm or less and subjected to extraction with a Soxhlet extractor for 6 hours using methyl ethyl ketone as the solvent to obtain an extraction residue (methyl ethyl ketone insoluble portion; MIP) of 86% by weight. As the result, SPS was obtained with a yield of 2.56 g, an activity of 214 (kg/g Ti) and a total residual content of metallic components of 95 ppm.

Claims: A process for producing a styrene polymer having such a syndiotacticity, that the proportion of racemic diad is at least 75%, which comprises polymerizing styrenic monomer in the presence of a catalyst comprising as primary ingredients (A) a titanium compound represented by the formula: TiRXYZ wherein R represents a cyclopentadienyl group, a substituted cyclopentadienyl group or an indenyl group; a substituted indenyl group or a fluorenyl group; X, Y and Z are independently a hydrogen atom, an alkyl group having 1 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, an aryl group having 6 to 20 carbon atoms, an aryloxy group having 6 to 20 carbon atoms, an arylalkyl group having 7 to 20 carbon atoms or a halogen atom, (B) a coordination complex compound comprising an anion in which a plurality of radicals are bonded to a metal and a nitrogen-containing cation having an acid dissociation constant at 25°C of 7 or less, and optionally (C) an aluminum compound having an alkyl group, a dialkylmagnesium compound or a dialkylzinc compound. The process according to Claim 1, wherein the coordination complex compound is selected from the group consisting of N,N-diethylanilinium tetra(pentafluorophenyl)borate, 8-chloroquinolinium tetra(pentafluorophenyl)borate, o-chloroanilinium (hexafluoro)arsenate, pyridinium tetra(pentafluorophenyl)borate, pyrrolinium tetra(pentafluorophenyl)borate, nitrophenyldimethylammonium tetra(pentafluorophenyl)borate, bromophenyldimethylammonium tetra(pentafluorophenyl)borate, N,N-dimethylanilinium tetra(pentafluorophenyl)borate and methyldihenylammonium tetra(pentafluorophenyl)borate. The process according to claim 1, wherein the catalyst comprises an aluminum compound having at least one alkyl group (C) in addition to the transition-metal compound (A) and the coordination complex compound (B).

Inventors: NAGANUMA SHOJI, TOMOTSU NORIO, WATANABE MASAMI, NAGANUMA, SHOJI, TOMOTSU, NORIO, WATANABE, MASAMI
Applicants: IDEMITSU KOSAN CO, IDEMITSU KOSAN COMPANY LIMITED
Application year: 1992
Main classification: C08F4
IPC codes: C08F4, C08F12