Allyl cyclosilalactams

Abstract: Cyclosilalactams of the formula and which can be used in the preparation of polyorganosiloxanes which react with moisture and do not have leaving groups. These cyclosilalactams are made using chlorosilabutanoic acid and chlorosilapropanoic acid precusors.

Description: This invention relates to cyclosilalactams. A search for new crosslinkers for use in the preparation of room temperature vulcanizing silicones (RTV's) lead to the discovery of the cyclosilalactams of the present invention. Mironov et al in "Synthesis of Silalactams", Khim. Geterotsikl. Soedin. (Chemistry of Heterocyclic Compounds), 1968, Vol. 6, p. 1124 described the following silalactams of the general formula where R and R' are hydrogen, methyl, ethyl or propyl and m is 0 or 1. Compounds of general formula (I) are made by the following reactions where x is ≧ 2. (III) + R'NH₂ → (I) . This invention relates to a compound which is a cyclosilalactam of general formula in which each of R¹, R³ and R⁴ is independently selected from the group consisting of a hydrogen atom and a monovalent hydrocarbon radical. The monovalent hydrocarbon radicals include methyl, ethyl, propyl, butyl, phenyl, vinyl, allyl, hexenyl, cyclohexyl, tolyl and isopropyl. Preferably, R¹, R³ or R⁴ are methyl. The cyclosilalactams of the present invention can be prepared by a method similar to the above method described by Mironov et al. However, the cyclosilalactams of the present invention of the present invention are prepared by the following methods. The preparation of cyclosilalactam of formula (A) is made by first reacting a diorganosilyl ester of methacrylic acid having the formula with a platinum catalyst exemplified by chloroplatinic acid, complexes of chloroplatinic acid with sym-divinyltetramethyldisiloxane and thionyl chloride (SOCl₂) with heating. The removal of the by-products which can be both solids and liquids produces a chlorosilylpropanoic acid precursor, namely 3-chlorodiorganosilyl-2-methylpropanoic acid chloride of the formula which is then reacted with allylamine producing a cyclosilalactam of formula (A). The cyclosilalactams of formula (B) and (C) can be prepared by a method which produces both at the same time. A chlorosilane of the formula is reacted with trimethylsilyl ester of vinylacetic acid in the presence of a platinum catalyst such as described above with heating. After the reaction, thionyl chloride is slowly added to the solution to give a mixture of chlorosilabutanoic acid chloride represented by the general formula where R² is a hydrogen atom or methyl radical and n is 1 or 2. The mixture of chlorosilylbutanoic acid chlorides preferably have the formulae The addition of allylamine to the above mixture of chlorosilanes produces a mixture of cyclosilalactams of formula (B) and (C). These cyclosilalactams are useful for making polyorganosiloxanes which have reactive endgroups in the presence of moisture and do not produce leaving groups upon reaction. The following examples are presented for illustrative purposes and should not be construed as limiting the present invention which is properly delineated in the claims. Example 1 1-allyl-6,6-dimethyl-6-sila-2-piperidone and 1-allyl-4,5,5-trimethyl-5-sila-2-pyrrolidone were prepared as follows: 112.5 grams of dimethylchlorosilane was slowly added to a solution of 142.48 g (0.900 mol) of the trimethylsilyl ester of vinylacetic acid and 0.05 g of a chloroplatinic acid complex with sym-divinyltetramethyldisiloxane having a platinum content of about 0.7 weight percent in 140 g of toluene while heating between 90°C. to 120°C. After the addition, 129 g of thionyl chloride was slowly added at reflux. A small amount of yellowish precipitate formed. The toluene, excess thionyl chloride and trimethylchlorosilane were distilled at reduced pressure. The product was distilled at 68°C. to 69°C. and 0.05 mm Hg to yield 144 g (73%) of product, which was a mixture of 4-chlorodimethylsilylbutanoic acid chloride and 3-chlorodimethyl-silylbutanoic acid chloride. 17.73 Grams of allylamine was slowly added with cooling and stirring to a solution of 22.27 g (0.1035 mol) of the mixture of above butanoic acid chlorides in 200 ml of diethyl ether. An extremely exothermic reaction occurred with the formation of solid allylammonium chloride which was removed by filtration. The ether was removed at room temperature under vacuum. The residue was distilled at 76°C. and 0.03 mmHg to yield 15.50 g (75.1%) of a 2:1 weight ratio of Example 2 3-chlorodimethylsilyl-2-methylpropanoic acid chloride was prepared via intramolecular hydrosilation of dimethylsilyl ester of methacrylic acid and 1-allyl-3,5,5-trimethyl-5-sila-2-pyrrolidone was prepared as follows: 91.74 g (0.636 mol) of the dimethylsilyl ester of methacrylic acid was slowly added over a 1.5 hour period to a solution of 0.05 g of the platinum complex described in Example 1 in 60 ml of toluene at 110°C. After the addition, 90.8 g (0.763 mol) of thionyl chloride was slowly added over a 25 minute period to the solution at reflux. A considerable amount of black precipitate formed towards the end of the addition. The reaction was heated with stirring at 85°C. overnight. The brown liquid was decanted from the solids and the toluene and excess thionyl chloride were distilled at reduced pressure. The product was distilled at 71°C. to 73°C. and 0.05 mmHg to yield 98.5 g (72% yield) of lemon product identified as 3-chlorodimethylsilyl-2-methylpropanoic acid chloride. 1-allyl-3,5,5-trimethyl-5-sila-2-pyrrolidone was prepared as follows: To a solution of 72.05 g (334.9 mmol) of 3-chlorodimethylsilyl-2-methylpropananoic acid chloride dissolved in 550 ml of diethyl ether was slowly added 63.10 g (1.105 mmol) of allyl amine with stirring over one hour. After stirring overnight, the solids were removed by filtration and washed with two 100 ml portions of diethyl ether. The ether was removed from the combined organic phases and the product distilled at 140°C. and 0.05 mmHg. The yield was 60.88 g (91%) of the product which had the following formula

Claims: A compound selected from the group consisting of a cyclosilalactam of general formula in which each of R¹, R³ and R⁴ is independently selected from the group consisting of a hydrogen atom and a monovalent hydrocarbon radical.

Inventors: KING RUSSELL KEITH, LEE CHI-LONG, KING, RUSSELL KEITH, LEE, CHI-LONG
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1992
Main classification: C07F7
IPC codes: C07F7