Silicones which contain lateral peripheral vinyl ether groups crosslinkable by cationic photoinitiators and their application for coatings and antiadhesive products for paper

Abstract: The invention relates to copolymers of siloxanes with the formula: (R a )₃SiO(V) v -(W) w -(Y) y -(Z) z -Si(R a )₃ where V = -SiR a R b O-; W = -SiR' a (R c -R d -OCH=CH₂)O-; Y = -SiR a R g O-; Z = -R a R g SiC n H 2n R' f C n H 2n SiR a R g O- where n = 2, 3 or 4; v, y, z = 0 or an integer, w ≠ 0 with v + y + z ≠ 0; R a = alkyl or phenyl; R b = R a ; R' a = R a or alkoxy; R c = alkylene, for example: R d = -OCONHR e NHCO-, -NH-COOC₂H₄-or -NHCOOC₃H₆-; R e = divalent hydrocarbon radicals; R g , R f and R' f are fluorinated or perfluorinated radicals. Use for the preparation of antiadhesive coatings, for example, on paper.

Description: The invention relates to copolymers which contain siloxane units which are crosslinkable as a result of the action of a photosensitive cationic catalyst such as salts of sulfonium or iodonium. These siloxane units contain a lateral peripheral vinyl ether group connected by a bridge group to a silicon atom, this bridge group having the structure of an aliphatic or aromatic urethane. The substituent groups on the siloxane, which carries peripheral vinyl ether, have the structure of trimethylene urethane-2-ethyl vinyl ether, trimethylene-m-toluenediurethane vinyl ether or 3-thia-1,5-pentanediyl-m-toluenediurethane vinyl ether, as nonlimiting examples. The vinyl ether group unit alternates along the polysiloxane chain with dimethylsiloxane or methylphenylsiloxane or alkylfluoralkylsiloxane units or tetraalkylalpha,omega-fluoroalkylenedisilaoxane units or polymer sequences thereof. Said fluoroalkyl or alpha,omegafluoralkylene group can be obtained by telomerization of tetrafluoroethylene. The proposed silicones can be, for example, crosslinked in the presence or absence of air by conventional irradiation using a mercury vapor lamp or in the presence of salts of sulfonium or iodonium, such as hexafluoroantimonate of triphenylsulfonium. The films of crosslinked polymers are characterized by hydrophobicoleophobic properties and by antiadhesive properties as well as by good heat resistance and they are useful as protecting insulation layers or as antiadhesive products for paper. These properties are particularly pronounced when the structure contains fluoroalkyl or fluoroalkylene groups. The antiadhesive property with respect to strong adhesive ribbons is particularly effective at high temperature. The copolymers of the invention have an average molecular weight ( M n of from 5000 to 100,000, preferably from 5000 to 50,000 and they have formula (I): (R a )₃SiO(V) v -(W) w -(Y) y -(Z) z -Si(R a )₃ where V = -SiR a R b O-; W = -SiR' a (R c -R d -OCH=CH₂)O-; Y = -SiR a R g O-; Z = -R a R g SiC n H 2n R' f C n H 2n SiR a R g O- with n = 2, 3 or 4; v, y, z are identical or different numbers, which can not, however, be zero simultaneously; w is always different from zero; and the ratio v+y+z/w is between 1 and 100; the R a groups represent, independently of each other, a radical selected from the group consisting of CH₃, C₂H₅, n-C₃H₇, n-C₄H₁₀ radicals and phenyl, with not more than one phenyl radical being attached to a given silicon atom; R b = R a ; R ' a = R a '-OCH₃ or OC₂H₅; R c = -C₂H 4-, -C₃H₆-, -C₂H₄- or -C₃H₆-S-C₂H₄-; R d = -OCONHR e NHCO-, -NH-COOC₂H₄ or -NHCOOC₃H₆-; R e = -C₆H₃(CH₃)-, -C₆H₄CH₂C₆H₄-, -(CH₂)₆-, -C₆H₁₀-CH₂-C₆H₁₀- or -CH₂-[(CH₃)₃C₆H₇]-; R g = -C k H 2k -R f where k = 2, 3 or 4; R f is a perfluoroalkyl group with 1 to 12 carbon atoms such as -CF₃, -C₂F₅, -C₃F₇, -C₃F₉, -C₆F₁₃ or -C₈F₁₇, where the higher perfluoralkyl groups can be formed by telomerization of tetrafluoroethylene (TFE) or a monovalent radical of an oligomer of fluorated oxetanes or oxiranes; R' f is a perfluoroalkylene group containing from 4 to 10 carbon atoms such as -C₄F₈-, -C₆F₁₂- or C₈F₁₆- or an alpha,omegafluoralkenyl group formed by the telomerization of tetrafluoroethylene or a divalent telochelating radical of an oligomer derived from fluorinated oxetanes or oxiranes or a m-phenylenedi(hexafluoroisopropoxy) radical; the units V, W, Y and Z can be arranged randomly, in order or alternated along the polymer chain. DE-4009889 describes curable organopolysiloxanes having Si-C linked oxyalkylene chains bearing vinyl ether groups in which the vinyl groups may be substituted by alkyl residues and the use of such polysiloxanes as anti-adhesive coating media. The copolymers of the present invention differ essentially from those of DE 4009889 in the nature of the groups linking vinyl ether groups to the siloxane chains. The use of isocyanates to bond cross-linking groups such as vinyl ether groups to siloxane chains with appendant polyoxyalkylene moieties is broadly described in EP-A-0176481, particularly in the context of synthesizing polymers for use in various kinds of contact lenses. Of the claimed structures, the siloxane units V are obtained by methods which are well known to an expert in the field of commercial silanes. The siloxane units W are obtained, as nonlimiting examples, either by condensation of 3-acetoxypropyl-methyldicholorosilane with units of the disilanol type and/or hydrolysis of the acetoxy group and condensation of the hydroxyl group released with alpha,omega-monoisocyanato-m-tolylurethane-ethylene-2-vinyl ether (pathways a, b). OCN-R e -NCO + HOC₂H₄OCH=CH₂----> OCNR e NHCOOC₂H₄OCH=CH₂ where R e has the above-mentioned structure, said reaction of diisocyanates with hydroxyl groups is catalyzed by dilauryldibutyltin at a temperature of 50 to 60°C.; or by addition of 2-thioethanol to sequences of methylvinylsiloxane, catalyzed by a free radical initiator such as azobisisobutyronitrile at 70°C. (pathway c). [SiCH₃(CH=CH₂)O] + n HSC₂H₄OH ----> -[SiCH₃(CH₂CH₂SC₂H₄OH)O] n - The sequences (c1) are then reacted with alpha,omega-monoisocyanatourethane-ethyl vinyl ether (a1) (a1) + (c1) ----> [OSiCH₃-(C₂H₄SC₂H₄OCONHR e NHCOOC₂H₄OCH=CH₂)] or by reacting 3-isocyanatopropyltriethoxysilane with 2-hydroxyethyl vinyl ether (pathway e). (e) (EtO)₃SiC₃H₆NCO+HOC₂H₄OCH=CH₂ ----> (EtO)₃SiC₃H₆-NHCOO-C₂H₄OCH=CH₂ The fluorinated organosilicon reactive compounds having the formulas X₂R¹ ₂Si or XR² ₂Si(R³SiR² ₂) z X are intermediate compounds for the siloxane units of the invention corresponding to Y and Z, where X represents a reactive group selected from the group consisting of halogens, preferably chlorine, the hydroxyl, alkoxy, acetoxy, amino, alkylamino and dialkylamino groups, z has values from 1 to 5 inclusively, at least one radical R¹ with formula II and at least one of the radicals R² connected to each one of the silicon atoms of formula III is selected from the group: 1) The fluoroalkyl groups with formula -C K H 2k R f where R f is a perfluoroalkyl group with from 1 to 12 carbon atoms, such as -CF₃, -C₂F₅, -C₃F₇ or -C₄F₉, where the higher perfluoroalkyl groups can be obtained by telomerization of tetrafluoroethylene and k = 2, 3 or 4. 2) The radicals of monovalent oligomers of fluorinated oxetanes and oxiranes, said radicals being attached to the silicon by a group which contains a nonhalogenated ethylene radical or a nonhalogenated trimethylene radical; all the possible other radicals R¹ and R² are selected from the group consisting of alkyl radicals with 1 to 4 carbon atoms, alkenyl radicals, perfluoroalkyldimethylene, -trimethylene or -tetramethylene, phenyl or phenyl substituted by a perfluoralkyl group, with the perfluoralkyl fragment of said radicals being substituted by a perfluoralkyl group which contains from 1 to 4 carbon atoms; and R³ is a divalent radical with the formula -C k H 2k -R' f -C k -H 2k - where R ' f contains a radical -(C₂F₄)- n - obtained by telomerization of tetrafluoroethylene or a divalent radical derived from oligomers of fluorinated oxetanes or fluorinated oxiranes or it is a metaphenylenedi(hexafluoroisopropoxy) radical. The oligomer radicals represented by R¹ and R² have the formulas: R f " O(C₃F₆O) m CF(CF₃)CA₂OC₃H₆-, C₃F₇O(C₃H₂F₄O) m -CH₂CF₂CA₂OC₃H₆-, or R f " O(CF₃C₂H₃O) m C₃H₆-. In the preceding formulas, "A" represents hydrogen or fluorine and R f " is -CF₃, -C₂F₅ or -C₃F₇; all the possible radicals R¹ and R² which do not represent a fluoroalkyl radical or a TFE telomer or an oligomer radical as defined above each represent preferably a methyl radical, 3,3,3-trifluoropropyl, phenyl or phenyl substituted by a perfluoralkyl group, where said perfluoralkyl group contains from 1 to 3 carbon atoms. R³ is selected preferably from the group consisting of -C k H 2k -(C₂F₄) n -C k H 2k - -C₃H₆O(CF₃)₂C-C₆H₄-C(CF₃)₂OC₃H₆-, -C₃H₆OCA₂CF₂CH₂O(C₃H₂F₄O) g T'O(C₃H₂F₄O) g - CH₂CF₂CA₂OC₃H₆-, -C₃H₆OCH₂CF₂O(C₂F₄O) h (CF₂O) i CF₂CH₂OC₃H₆- or -C₃H₆OCA₂-CF(CF₃)O(C₃F₆O) g T'O(C₃F₆O) g - CF(CF₃)CA₂OC₃H₆-. T' is selected from the group consisting of -C₂F₄-, -C₄F₈-, -C₅F₁₀- and -(C₂F₄)₂O-; the recurrent units are arranged randomly or in succession along the chain; the value of k is 2, 3, 4; the value of n is from 2 to 20 inclusively, preferably from 2 to 10; the value of m is from 1 to 20 inclusively, preferably from 1 to 10; the value of g is from 1 to 20 inclusively, preferably from 2 to 10; and the value of h/i is from 0.5 to 20 inclusively and the value of h+i is from 8 to 100 inclusively, preferably from 8 to 20. The different recurrent fluorinated organosilicon units are arranged randomly or in sequence in the molecules and the silicon atoms of these units are connected by a nonhalogenated linear alkylene radical which contains 2, 3 or 4 carbon atoms with fluoralkyl groups R f or by a bivalent group which contains a nonhalogenated dimethylene radicals or halogenated trimethylene with the divalent group R³ defined above. One of the radicals R¹ present in formula II and one of the terminal radicals R² located on each of the silicon atoms in formula III can represent alkyl, alkenyl, aryl radicals, phenyl substituted with a perfluoralkyl group and/or monovalent fluorinated alkyl groups corresponding to the formula -C k H 2k R⁴, where k is 2, 3, 4 and R⁴ is a perfluoralkyl radical containing from 1 to 4 carbon atoms. R³ can be a telomer or a divalent oligomer as defined above or it can be -[(CH₂)₃OC(CF₃)₂]₂Ph, where Ph stands for the m-phenylene radical. The polysiloxane chain (I) is obtained by hydrolysis or cohydrolysis or polymerization by condensation of silane intermediates of the types: X₂SiR a R b X₂SiR' a (R c -R d -OCH=CH₂) X₂SiR a R g X[R a R g SiC k H 2k R' f C k H 2k SiR a R g ]X X-Si(R a )₃ where X represents a reactive group selected from halogens, preferably chlorine, the hydroxyl, alkoxy, acetoxy, amino, alkylamino and dialkylamino groups and k = 2, 3 or 4. The polyorganosiloxanes prepared using the present organosilicon compounds as at least a part of the organosilicon reactants have a high thermochemical resistance and low surface energy values, which are particularly improved when their structure contains fluorinated groups. One class of the radicals attached to silicon according to the invention is prepared from fluorinated telomers of tetrafluoroethylene. A preferred method for the preparation of telomers of TFE consists of a radical telomerization of TFE. The telomerization of TFE can be initiated by telogens substituted with bromine or iodine, represented by the formula R f X or XR' f X, where R f and R' f are as defined above in the present description and X is bromine or iodine. These telogens belong to a class which includes, without being limited to, CF₃I, C₂F₅I, n- or iso-C₃F₇I, n-C₄F₉I, C₂F₅Br, CF₃CFBrCF₂Br, CF₂Br₂, CF₂ICF₂I, I(C₂F₄) n I (n = 2 to 10). The telomers prepared from monobrominated or monoiodated telogens above are attached to a silicon atom by nonhalogenated alkylene radicals containing 2, 3, 4 carbon atoms and using the methods described in the following paragraphs, to prepare the siloxanes represented by formula I. The telogens which contain two reactive halogen atoms, iodine or bromine, produce alpha,omega-telochelating telomers which can be attached to two different silicon atoms by means of nonhalogenated linear alkylene radicals with 2, 3, 4 carbon atoms to produce fluorinated polysiloxane. To obtain the linear structure and the absence of extensive crosslinking which characterize the present organosilicon compounds, the synthesis must be organized appropriately with regard to the subsequent series of reactions of appropriate silanes with telochelating dihalotelomers and with monoiodo- and/or monobromotelomers or with the other compounds described here. The process of telomerization of TFE initiated by said telogens according to the present invention can be activated by heat or gamma irradiation or ultraviolet irradiation, of initiators of the organic peroxide type or of redox systems. Preferred catalysts for these reactions are benzoyl peroxide, di-t-butyl peroxide, t-butyl peroxypivalate and percarbonates. The reaction can be conducted in the presence of organic solvents including, without being limited to, 1,1,2-trichlorotrifluorethane, t-butyl alcohol, acetonitrile and mixtures thereof. Catalysts such as redox systems with persulfate can also be included and the telomerization can be carried out in an aqueous dispersion. The telomerization temperature is between room temperature and 150°C., if the process is activated by irradiation or by catalysts or between 150°C. and 220°C. if the process is activated thermally. The pressure at which the reaction is conducted can range from atmospheric pressure to approximately 100 atmospheres and one should take care to exclude oxygen from the telomerization reaction. The fluorinated telomers are then attached to the silicon atoms of the present compounds through the intermediary of an alkylene radical without halogen consisting of 2, 3 or 4 carbon atoms, such as the dimethylene or trimethylene or tetramethylene radicals, according to a chain termination process which is carried out appropriately. Ethylene is a reactant which can be used easily in the chain termination reaction. When they are correctly attached to the silicon as described above, the telomer chain imparts to the final fluorinated organosilicon compound high levels of chemical and thermal resistance and of antiadhesive properties. Intermediate oligomer fluorinated polyoxaalkylenes according to the present invention can be prepared using well known methods for the oligomerization of polyfluorooxiranes or fluorooxetanes such as perfluoropropene oxide, 2,2,3,3-tetrafluorooxetane and 3,3,3-trifluoropropene oxide. Some of these oligomers are available commercially. According to a preferred method, the preferred oligomer polyoxaalkylenes are prepared by reacting cesium fluoride or potassium fluoride with perfluorinated carbonyl compounds such as hexafluoroacetone, trifluoroacetyl fluoride, perfluoropropionyl fluoride, carbonyl fluoride, perfluorosuccinyl or 1,5-oxaperfluoroglutaryl fluorides which can initiate the oligomerization of perfluorooxiranes and fluorooxitanes according to a known method. The perfluorinated polyoxaalkylenecarbonyl fluoride must be reacted to form appropriate intermediate compounds which can be attached to the silicon. A preferred method consists of stoichiometric addition of potassium and subsequent substitution with allyl bromide to produce oligomer fluorinated polyoxaalkylenes terminated by allyl groups, which are then made to react with a reactive organohydrosilane. Another pathway to attach the present oligomer fluorinated polyoxaalkylenes to the silicon atom is the metathesis of the fluoride groups of carbonyl acid terminals of these oligomers to methyl esters followed by a reduction to methanol radicals, followed by terminal capping with allyl bromide using the known Williamson synthesis. Fluorinated telomers which are terminated by one or two (XC k H 2k )- where X is bromine or iodine can be converted to an organometallic derivative such as a Grignard reagent, a copper Grignard reagent, an organic lithium, zinc or aluminum compound and they can then be reacted with the silane which contains at least one halogen such as fluorine, chlorine or bromine and at least one alcoholate group. The organometallic compound can be prepared beforehand or it can be formed in the presence of the silane. As a variant, the alpha-iodo or alpha-bromo terminal group of the telomer fluoroalkane terminated by a polymethylene group or the analog of the telechelic alpha,omega-diiodo- or dibromo- or bromoiodopolymethylene-polyfluoroalkane which may be dehydrohalogenated to present, respectively, one or two terminal vinyl groups which can be reacted in a hydrosilylation reaction with silanes which contain at least one hydrogen atom connected to the silicon atom. The reaction is catalyzed by organic peroxides and platinum catalysts. In the case of silanes with formula II, in addition to two atoms or groups required to react with the above-mentioned derivatives of fluorinated telomers and oligomers or other groups, the silanes, after the reaction with the telomers and monofunctional oligomers or with other groups, contain two reactive entities "X" as in formula II which can then be made to react with other silanes to form the sequence of polysiloxane. These two reactive entities include, without being limited to, halogens such as chlorine, alkoxy groups containing 1 to 4 or more than 4 carbon atoms, the hydroxyl group and primary or secondary amino groups. In the case of formula III, the silanes which are reacted with bifunctional derivatives of telomers or oligomers or with other groups and with monofunctional derivatives of telomers or oligomers or with other groups, require one of the above-mentioned reactive entities on each of the two telochelating silicon atoms present at the end of the molecule represented by formula III. These reactive entities X can then be reacted with other silanes to form an elongated chain structure as mentioned above and represented by formula I. The units V, W, Y, Z which have the structures represented in formula I can be homopolycondensed appropriately separately to form a homogenous or copolycondensed sequence with statistical sequences according to the usual techniques in silicon chemistry which are well known to the expert in the field. The crosslinking of said copolymer silicones of formula I which contain a lateral peripheral vinyl ether group is carried out by activation with UV light in the presence of cationic photoinitiators selected from the group of salts of halonium or sulfonium or phosphonium, with the preferred photoinitiators being of the triarylsulfonium hexaflouroantimonate type. One of the techniques proposed in the invention follows pathways (a) and (b). The intermediate 2-hydroxyethyl vinyl ether is prepared from 2-chloroethyl vinyl ether (Aldrich) using a phase-transfer reaction with sodium acetate and hydrolysis under mild conditions with KCN. The monoisocyanato-m-tolylurethaneethylene-2-vinyl ether intermediate (1) is prepared by condensation of tolyl diisocyanate and 2-hydroxyethyl vinyl ether as described in European Patent Application No. 0 398 775, filed November 22, 1990. Next, (1) is reacted with a polysiloxane having the structure (2): C₆H₅-Si(CH₃)₂O[Si(CH₃)₂O] v [CH₃Si(C₃H₆OH)O] v ,Si(CH₃)₂C₆H₅ to yield the product (3) which contains the peripheral vinyl ether group with the following formula: C₆H₅Si(CH₃)₂O-[Si(CH₃)₂O] v [CH₃Si[C₃H₆OCONHC₆H₃(CH₃)NHCOOC₂H₄OCH=CH₂]O] v '-Si(CH₃)₂C₆H₅. Product (3) is then applied in the form of a film onto paper and crosslinked in the presence of triarylsulfonium hexafluoroantimonate to obtain an antiadhesive coating on the paper. According to a variant of the same general technique, triethoxysilane-3-propylurethane-2-ethyl vinyl ether (prepared by condensation catalyzed by dibutyl tin dilaurate of 2-hydroxyethyl vinyl ether with 3-isocyanatopropyltriethoxysilane) was subjected to polycondensation with a polydimethylsiloxanediol in the presence of dimethylphenylchlorosilane as chain termination agent. A product (4) with the following structure was obtained: C₆H₅Si(CH₃)₂O[Si(CH₃)₂O] v -RSi(OC₂H₅)O] v ' (Si(CH₃)₂O) v -Si(CH₃)₂C₆H₅ where R = C₃H₆NCCOC₂H₄OCH=CH₂. After application to paper, this product (4), in the presence of triarylsulfonium salt, was crosslinked by a short exposure to UV light yielding a paper with antiadhesive properties. According to a different technique, a polymethylvinylsiloxane was reacted with thioethyleneglycol to produce a sil-2-thio-4-hydroxy unit which was reacted with isocyanatotolylurethane-2-ethyl vinyl ether to obtain a silanoxy group with the structure (5). The modified polysiloxane which contains peripheral vinyl ether was activated for crosslinking by UV light in the presence of sulfonium salt. Example 1: Preparation of a polysiloxane containing lateral urethanevinyl ether groups. a) Synthesis of hydroxy-2-ethyl vinyl ether a.1) Synthesis of acetoxy-2-ethyl vinyl ether In a 250-mL flask equipped with cooling coil and mechanical stirring system one introduces 50 g of chloro-2-ethyl vinyl ether (Aldrich) (0.47 mol), 39 g sodium acetate (0.47 mol) and 2.2 g TBAH (tetrabutylammonium hydrogen sulfate). The mixture was stirred at 450 rpm for 12 hours at 109°C. It was then filtered and the solid part (primarily NaCl), was washed several times with ether which was then eliminated by evaporation at reduced pressure; the product was finally distilled (bp 20 mm Hg = 72°C.). The yield obtained was 92%. With IR (PERKIN ELMER 398): the presence of vibration bands at 1750 (CO) and 1620 cm⁻¹ (-HC=CH₂) was observed. ¹H-NMR (250 MHz, CHCl₃): the peaks were assigned as follows: a.2) Hydrolysis of acetoxy-2-ethyl vinyl ether In a 250-mL flask equipped with cooling coil and magnetic stirring system one introduces: 13 g acetoxy-2-ethyl vinyl ether (0.1 mol), 1.2 g potassium cyanide (0.018 mol), 150 mL methanol RP and 0.1 g hydroquinone. The mixture was stirred for 12 hours at 25°C.; it was then treated with ether and filtered over Na₂SO₄. The solvent was then eliminated at reduced pressure. The product was prepared with a yield of 90%. The present invention is illustrated by the following examples, in which Examples 1, 2, 4, 6, 8, 9 and 11 are in accordance with the invention and Examples 3, 5, 7 and 10 are outside the scope of the invention and are included for reference only. ¹H-NMR (250 MHz, CHCl₃): the complete disappearance of the peak at 2.07 ppm IR: (Perkin-Elmer 398), observation of the complete disappearance of the band at 1750 cm⁻¹ and the appearance of the band at 3350 cm⁻¹ (C-OH). From this one can conclude that the product obtained had the structure: HO-CH₂-CH₂-O-CH=CH₂ a.3) Synthesis of isocyanatourethane vinyl ether: In a 250-mL flask fitted with nitrogen inlet, tap funnel and a cooling coil, one introduces: 9.88 g TDI (toluene diisocyanate), 100 mL anhydrous toluene, 0.1 DBDLT (dibutyltin dilaurate and 0.1 g hydroquinone. Using a tap funnels one introduces 5 g hydroxy-2-ethyl vinyl ether (7) and 10 mL toluene drop by drop for 30 minutes. The mixture is then heated to 50°C. for 5 hours. At the end of the reaction, toluene and unreacted products are eliminated by evaporation at reduced pressure (yield 98%). The NCO index was 14.2% (by weight). IR analysis revealed: NCO band to 2260 cm⁻¹ Disappearance of OH band at 3350 cm⁻¹ Presence of -C=C band at 1620 cm⁻¹ and NH band at 3320 cm⁻¹. ¹³C-NMR analysis (BRUKER 80 MHz, CHCl₃) permitted the following assignment of peaks: 17.4 115.5 154.0 66.1 63.4 151.3 87.4 δ-ppm aromatic ring: in the range between 127 and 136. a.4) Synthesis of silicone-urethane vinyl ether (10) In a flask with 2 outlets, fitted with cooling coil and a nitrogen inlet, one introduces: 8.2 g of compound (9) prepared as described below, 12 g anhydrous toluene, 2.72 g of compound (8) and 0.1 g hydroquinone. The mixture was maintained at 60°C. for 6 hours and then the solvent was eliminated at reduced pressure. The following product was obtained quantitatively: where R = -C₃H₆-O-CONH-C₆H₄(CH₃)NH COOC₂H₄OCH=CH₂ and = -C₆H₅ IR (Perkin-Elmer 398) results were: absence of OH vibration bands (3350 cm⁻¹) and NCO vibration band (2260 cm⁻¹). presence of bands for NH (3320 cm⁻¹) and for vinyl groups (1620 cm⁻¹). b.1) Synthesis of the compound with formula (9) In a 500-mL flask fitted with cooling coil one introduces: 100 g α,ω-dihydroxypolydimethylsiloxane (product manufactured by the RHONE-POULENC Company: % OH = 5%, M n = 680; n = 8.9), equivalent to 0.147 mol part; 27.65 g acetoxy-3-propylmethyldichlorosilane (supplied by Petrarch System), equivalent to 0.129 mol part, 6.26 g phenyldimethylchlorosilane (supplied by Petrarch System), equivalent to 0.0368 mol part, 200 mL anhydrous toluene and 4 mL pyridine. The mixture was heated to 80°C. for 24 hours, then filtered to eliminate the white precipitate and evaporated at reduced pressure to eliminate the solvent (toluene) and unreacted product. A dilution was then carried out with ethyl ether followed by repeated washing to completely eliminate the pyridine salt. The ether phase was dried over Na₂SO₄, filtered and evaporated at reduced pressure. The product was obtained with a yield of 95%. This compound was analyzed by IR [spectroscopy] (Perkin-Elmer 398): the complete disappearance of the Si-OH band at 3360 cm⁻¹ was observed and the appearance of the C=O band at 1760 cm⁻¹. The intrinsic viscosity was measured in butanone at 30°C. (K = 0.048 mL/g and α = 0.55) n = 8.5 x 10 -3 mL/mg and Mv ≃ 9200 ²⁹Si-NMR (80 MHz, CHCl₃) revealed: presence of central silicon atoms at -21.9 ppm and of terminal Si atoms at -2.5 ppm and absence of (OSi-OH) peaks at -11.8 ppm and of peaks at +37 ppm. ¹³C-NMR (80 MHz, CHCl₃) resulted in the following assignment of the peaks: (132, 9 (c); 129.2 (a); 127.7 (b) for the carbon of the aromatic ring). The hydrolysis of this compound was carried out in the presence of KCN (1 wt%) in methanol at room temperature for 24 hours. The compound was purified by washing with water-ether, then it was dried over Na₂SO₄ and the solvent was evaporated at low pressure. The product was obtained with a yield of 90%. The IR results (Perkin Elmer 398) were: disappearance of the vibration band for the C=O groups (1730 cm⁻¹) and appearance of the vibration band for the OH groups at 3350 cm⁻¹. 1 H-NMR (250 MHz, CHCl₃) result: hydrolysis rate: 95%. The structure of compound (9) is as follows: Example 2: Preparation of the polysiloxane which contains lateral urethane-vinyl ether groups (11) Step 1 - Synthesis of triethoxysilane-propylurethane vinyl ether (12). In a 50-mL flask fitted with a cooling coil one introduces: 6 g (EtO)₃ -Si(CH₂)₃NCO 2.2 g CH₂=CH-O-C₂H₄OH 0.1 g DBDLT 0.05 g hydroquinone. The mixture was stirred for 10 min at room temperature. The formation of this product was accompanied by a high release of heat. Unreacted products were eliminated at reduced pressure. The product yield was more than 95%. IR analysis of the product (Perkin Elmer 398) revealed the disappearance of the NCO vibration band at 2260 cm⁻¹ and the appearance of the NH band at 3320 cm⁻¹. ¹H-NMR (250 MHz, CHCl₃) result; one quadruplet at 6.4 ppm (O-CH=CH₂). ¹³C-NMR (Brucker 80 MHz) results: the peaks were assigned as follows to the structural formula (12): Step 2 - Polycondensation of triethoxysilane-urethane vinyl ether with polydimethylsiloxanediol in the presence of a chain terminating agent (formation of polysiloxane) (11) In a 250-mL flask fitted with cooling coil one introduces: 13.6 g triethoxysilane-urethane vinyl ether (12) (0.0406 mol) 32 g dihydroxypolydimethylsiloxane (M = 680; % OH = 5%; n = 8.9 or 0.048 mol), the structure of this commercial product was as follows: 50 mL toluene. The mixture was stirred for 20 minutes at room temperature. Then 2.3 g of phenyldimethylchlorosilane were added; the mixture was then heated to 90°C. overnight. Unreacted products were evaporated at reduced pressure (0.005 mm Hg at 140°C.). 44 g of (11) were obtained: where R = C₃H₆-NHCOOC₂H₄OCH=CH₂ and  = -C₆H₅. The results of IR analysis (Perkin Elmer 398) were: presence of NH bands (3320 cm⁻¹) and the band for the double bond at 1620 cm⁻¹. ¹³C-NMR (80 MHz, CDCl₃) revealed: peaks at 151.5 and 86.9 ppm (-CH=CH₂), peaks at 11.3; 23.7 and 43.77 for the carbon atoms at α, β and γ of Si and the peak at 1.0 ppm for the different carbon atoms attached to the Si atom. Example 3: Polycondensation of triethoxysilane-urethane vinyl ether with l'α,ω-dihydroxypolydimethylsiloxane without chain terminating agent (polysiloxane (13)) In the same apparatus as above, one introduces 8.04 g triethoxysilane-urethane vinyl ether (12) and 127 g α,ω-dihydroxypolydimethylsilane ( M n = 3580; % OH = 0.95) with the formula HO[(CH₃)₂SiO]₄₈-H, followed by addition of 100 mL of toluene, the mixture is then heated to 80°C. overnight. After elimination of the solvent at reduced pressure, the ether is then diluted and activated charcoal is added; the entire mixture is then heated to the boiling point for 30 minutes. The mixture is then filtered over Na₂SO₄ and silica. The ether is evaporated and the product consists of 130 g of viscous compound (13) with the structure: where R = (CH₂)₃-NHCOOC₂H₄OCH=CH₂ The same IR and ¹³C-NMR characteristics were observed as for the product of Example 2, Step 2. Example 4: Preparation of a polysiloxane which contains lateral thioether-urethane vinyl ether groups (14) Step 1 Preparation of a polydimethylsiloxane (15) which contains primary hydroxy groups. In the 500-mL flask fitted with the cooling coil and a nitrogen inlet one introduces: 100 g of a copolymer of dimethylsiloxane and methylvinylsiloxane (η = 1 Pa·s; %(OSi(CH₃)CH=CH₂] = 7.5%, supplied by Petrarch System) 21.7 g thioethanol (MERCK) and 0.6 g AIBN and 200 mL toluene. The mixture was heated to 70°C. for 6 hours. Then solvent and unreacted products were eliminated by evaporation at reduced pressure. 118 g of product e₁ were obtained. where R = CH₂CH₂-S-CH₂CH₂OH and n₁ = 348 n₂ = 25. ¹H-NMR analysis (250 MHz, CDCl₃) revealed the complete disappearance of vinyl protons at 6.0 ppm and the appearance of multiplets at 0.9 and 2.6 ppm in α and β positions of the Si atom and at 2.7 and 3.6 ppm in the α and βpositions of the hydroxyl group. ¹³C-NMR (80 MHz, CDCl₃) permitted the assignment of the peaks corresponding to group (16) as follows: 1.05 18.6 26.3 35.2 60.2 δ in ppm The content of OH groups of the product was 1.2%. Step 2 - Polysiloxane (14) In a 100-mL flask fitted with cooling coil and a nitrogen inlet, the following quantities of the following ingredients are introduced: 10 g of product (15) prepared in Step 1, 1.9 g of product (8), 50 mL of anhydrous toluene and 0.1 g hydroquinone. The mixture was stirred and heated at 60°C. for 6 hours. The reaction mixture was treated as in Example 1, Step (a₄). The yield was quantitative. IR analysis (Perkin-Elmer 398) results: Disappearance of NCO band at 2260 cm⁻¹ Appearance of NH band at 3380 cm⁻¹ Appearance of vinyl band at 1620 cm⁻¹ The structure of compound (14) was as follows: where n₁ = 348, n₂ = 25 and R=CH₂CH₂-S-CH₂CH₂-OCONHC₆H₃(CH₃)-NHCOO-C₂H₄-O-CH=CH₂. Example 5: Preparation of a polysiloxane which contains fluorinated lateral groups in the chain (product (17)). One introduces into a flask: 37 g of (0.0103 mole), with n = 48 and % OH = 0.95 2.07 g CH₂=CH-O-C₂H₄-OCONHC₃H₆Si(OEt)₃ (product (11) of Example 2) (0.0062 mol). 1.17 g C₆F₁₃C₂H₄OC₃H₆Si(OEt)₃ (0.0021 mol). The reaction is conducted and treated in the same manner as for product (13). ¹H-NMR and ¹³C-NMR confirmed the following structure of the polymer (17) obtained: where R v = C₃H₆ -NHCOOC₂H₄OCH=CH₂ R F = C₃H₆OC₂H₄C₆F₁₃ n = 48. This product is soluble in most organic solvents such as CHCl₃, methyl ethyl ketone, CCl₄ and acetone. IR analysis revealed the presence of vibration bands for vinyl at 1620 cm⁻¹ and for NH at 3300 cm⁻¹. Example 6: Preparation of a polysiloxane which contains fluorinated groups in the chain and at the ends (18) In a 250-mL flask fitted with cooling coil, one introduces: 30 g of (n = 8,9 and % OH = 5%) equivalent to 0.044 mol 11.82 g R V Si(OEt)₃ (12) or 0.035 mol 7.51 g R F Si(OEt)₃ or 0.013 mol and 0.5 g tetramethylguanidine. The reaction is conducted and treated in the same manner as for Example 6. 40 g of a viscous product are obtained, which, as shown by the IR spectrum, agrees with the following formula (18): where R F = C₆F₁₃C₂H₄OC₃H₆ R v = -C₃H₆NHCOOC₂H₄OCH=CH₂ n = 8.9. The theoretical M n was approximately 10,500. Example 7: Preparation of a polysiloxane which contains fluorinated lateral groups and lateral and terminal urethane-vinyl ether groups (19) Step 1 In the same apparatus as above one introduces: 50 g of (n = 8.9 and % OH = 5) ; Mn = 680) (0.073 mol), 11.44 g C₆F₁₃C₂H₄OC₃H₆SiCH₃Cl₂ (0.022 mol), 9.48 g AcOC₃H₆SiCl₂CH₃ (0.0441 mol), 2.86 g AcOC₃H₆SiCl(CH₃)₂ (0,0147 mol) and 1 g tetramethylguanadine. The reaction was conducted and treated as above. The structure of the product obtained was as follows: where R F = C₃H₆-O-C₂H₄-C₆F₁₃ and R = C₃H₆-OCOCH₃ Step 2: hydrolysis of (20) to prepare (21) The product obtained in the first step is reacted in the presence of 0.4 g KCN in 100 mL CH₃OH (RP) for 24 hours at room temperature. Step 3: Grafting of ω-isocyanate vinyl ethers 10 g of product (21) are added to 1.96 g of vinyl ether-ω-isocyanate (8) and 60 mL of toluene in a nitrogen atmosphere. The reaction lasted 5 hours at 40°C. A waxy yellowish product (19), which was soluble in butanone, was obtained. The analysis showed that product (19) agreed with the following formula: where R F = C₃H₆-O-C₂H₄-C₆F₁₃ and Example 8 : Preparation of the polysiloxane which contains fluorinated lateral groups and urethane-vinyl ether and which has dimethylphenylsilane ends (22) One reacts: 50 g (n = 8.9) 0.073 mol), 12.5 g C₆F₁₃C₂H₄OC₃H₆SiCl₂CH₃ (0.024 mol), 9.3 g AcOC₃H₆SiCl₂CH₃ (0.043 mol) and 2.1 g SiCl(CH₃)₂ (0.012 mol). After condensation in the presence of a salt of tetramethylguanadine and hydrolysis in the presence of KCN (CH₃OH) one obtains a fluorinated polysiloxane which contains lateral OH groups (23). One reacts 10 g of this polymer (23) in 20 mL toluene and 1.5 g vinyl ether-ω-isocyanate (8) at 50°C. for 4 hours in nitrogen to obtain a yellowish viscous liquid (22), whose analysis showed that it agreed with the following formula: where R F = C₃H₆-O-C₂H₄-C₆F₁₃ and Example 9: Preparation of a polysiloxane which contains fluorinated groups in the chain, lateral fluorinated and urethane-vinyl ether groups and which has dimethylvinylsilane ends (24) The silanediol CF₃C₂H₄(CH₃)(HO)SiC₂H₄C₆F₁₂C₂H₄Si(CH₃)C₂H₄CF₃(OH) was prepared according to a method described by Y. Kim in Rubber Chem. Technol. (1971), 1350, by hydrosilylation of CH₂=CHC₆F₁₂CH=CH₂ with 3,3,3-trifluoropropylmethylchlorosilane, followed by hydrolysis. One reacts 12 mol parts of silanediol (25) with 4 mol parts C₆F₁₃C₂H₄OC₃H₆SiCl₂CH₃, 7 mol parts AcOC₃H₆SiCl₂CH₃ and 2 mol parts C₆H₅SiCl(CH₃)₂ as described in Example 8. After hydrolysis of the silicone in the presence of KCN/CH₃OH and reaction with compound (8), as described in Example 8, one obtains a product (24) which had the following structure: where R F and R are as described in Example 8. Example 10 : Preparation of the polysiloxane which contains lateral fluorinated groups and lateral and terminal urethane-vinyl ether groups Step 1: One introduces in a 250-mL flask: 15 g of with n = 4.49 and % OH = 9.7%, 19.86 g Cl₂(CH₃)SiC₃H₆OC₂H₄C₈F₁₇ (0.032 mol) (26), 1.53 g Cl₂(CH₃)SiC₃H₆OCOCH₃ (0.0071 mol), 1.384 g Cl(CH₃)₂SiC₃H₆OCOCH₃ (0.0071 mol), 0.1 g tetramethylguanidine. Product (26) was prepared as follows: from C₂F₅I, by telomerization of TFEE at 200°C., one obtains the telomer C₂F₅(C₂F₄)₃I (27) which one separates by distillation from the other telomers. Product (27) was reacted with the C₂H₄ at 120°C. in the presence of CuCl/ethanolamine producing C₈F₁₇C₂H₄I which was hydrolyzed with 30% oleum to be converted to C₈F₁₇C₂H₄OH (28). Product (28) was reacted with allyl chloride in the presence of tetrabutylammonium hydroxide and soda (20N). After distillation, the product obtained is C₈F₁₇C₂H₄OCH₂-CH=CH₂ (29). One reacts product (29) with HSi(CH₃)Cl₂ in the presence of H₂PtCl₆ (at 50% in isopropanol) in hexane at 70°C. for 24 hours and, after distillation of the solvent, one distills the final product in a vacuum (26). The polycondensation reaction between and the precursors mentioned above was conducted at 70°C. for 18 hours while keeping the reaction in a 20 torr vacuum. The product was diluted with ether and filtered and after evaporation of the solvent in a vacuum, one obtains 34.75 g of very viscous product which contains 31.5 wt% fluorine. IR analysis has shown the presence of acetate groups (1740 cm⁻¹ region) and also of other units present in the structure (30). where n = 54; n' = 9, n" = 2 R = C₃H₆OCOCH₃. This structure corresponds to the theoretical percentage by weight of fluorine of 29.9% and to a MW = 9720. Step 2: The product (30) was hydrolyzed in the presence of KCN in methanol to prepare a product (31) which presented a total conversion of acetate groups to free hydroxyl groups. Step 3: Polysiloxane (31) with free, lateral and terminal hydroxyl groups was reacted with vinyl ether-ω-isocyanate (8) to obtain product (32): where R' = C₃H₆OCONHC₆H₃(CH₃)NHCOOC₂H₄OCH=CH₂ and where n, n' and n" are the same as in (30). Example 11 : Use of polymers according to the invention for the production of crosslinked coatings with antiadhesive properties Coating compositions were prepared by dissolving a polymer according to the invention and a photosensitive catalyst in a solvent in the proportions indicated in the table below and these compositions were applied to kraft paper using a manual applicator consisting of a threaded rod, in quantities indicated in said table (in g/m²). The applied coat was crosslinked by exposure to a UV lamp (80 W/cm²) for the time indicated in the table. In all cases, a paper with antiadhesive properties was obtained from which adhesive ribbons could be removed easily. In addition, there was no trace of migration, from the antiadhesive film of the silicon polymer of the invention to the adhesive ribbon, because the latter remained capable of adhering to itself. These antiadhesive properties were preserved even after storage for 24 hours of the treated papers in an oven at 60°C.

Claims: A siloxane copolymer having an average molecular weight ( M n ) of from 5000 to 100,000 and represented by formula (I): (R a )₃SiO(V) v -(W) w -(Y) y -(Z) z -Si(R a )₃ where V = -SiR a R b O-; W = -SiR' a (R c -R d -OCH = CH₂)O-; Y = -SiR a R g O-; Z = -R a R g SiC n H 2n R ' f C n H 2n SiR a R g O- with n = 2, 3 or 4; v, y, z are identical or different numbers, but cannot be simultaneously zero; w is always different from zero; and the ratio v+y+z/w is between 1 and 100; the groups R a represent, independently of each other, a radical selected from the group consisting of CH₃, C₂H₅, n-C₃H₇, n-C₄H₁₀ radicals and phenyl, with not more than one phenyl radical being attached to a given silicon atom; R b = R a ; R' a = R a , -OCH₃ or OC₂H₅; R c = -C₂H₄-, -C₃H₆-, -C₂H₄-S-C₂H₄- or -C₃H₆-S-C₂H₄-; R d = -OCONHR e NHCO-, -NH-COOC₂H₄- or -NHCOOC₃H₆-; R e = -C₆H₃(CH₃)-, -C₆H₄CH₂C₆H₄- ;-(CH₂)₆-, -C₆H₁₀-CH₂-C₆H₁₀- or -CH₂-[(CH₃)₃C₆H₇]-; R g = -C k H 2k -R f where k = 2, 3 or 4; R f is a perfluoroalkyl group with 1 to 12 carbon atoms or a monovalent radical of an oligomer of oxetanes or fluorinated oxiranes; R' f is a perfluoroalkylene group with 4 to 10 carbon atoms or an alpha,omega-fluoroalkenyl group formed by telomerization of tetrafluoroethylene or a telechelic divalent radical of an oligomer derived from fluorinated oxetanes or oxiranes or an m-phenylenedi(hexafluoroisopropoxy) radical; and the units V, W, Y and Z can be arranged randomly, in order or alternated along the polymer chain. A siloxane copolymer according to claim 1, wherein said copolymer contains fluoroalkyl or fluoroalkylene groups. A protecting insulation layer comprising a silicone copolymer according to claim 1 or 2. An antiadhesive product for paper comprising a silicone copolymer according to claim 1 or 2. The use of a silicone copolymer according to claim 1 or 2 for the preparation of antiadhesive coatings.

Inventors: BOUTEVIN BERNARD JEAN LEON, CAPORICCIO GERARDO, YOUSSEF BOULOS, BOUTEVIN, BERNARD JEAN LEON, CAPORICCIO, GERARDO, YOUSSEF, BOULOS
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1992
Main classification: C08G77
IPC codes: C08G77, C09D183, D21H27, D21H19