Apparatus for forming metal film and process for forming metal film

Abstract: An apparatus for forming metal film for forming metal films on substrates comprises a reaction chamber (101), a plurality of first and second electrodes (106) alternately arranged in the reaction chamber, an energy supply means (116) that supplies to the first and second electrodes an electrical energy for generating plasma, a heating means (104) for heating a plurality of substrates (105) disposed between the first and second electrodes, and a gas feed means (107-111) that feeds into the reaction chamber a starting material gas for forming metal films; the plasma is generated across the first and second electrodes to form metal films on the plurality of substrates. The apparatus can form metal films at a high throughput at one time process, and at a low cost.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to an apparatus for forming metal film and a process for forming metal film. More particularly, it relates to an apparatus for forming metal film, and a process for forming metal film, that can form a metal film in a high throughput. Related Background Art In electronic devices or integrated circuits making use of semiconductors, aluminum (Al), Al-Si or the like has been hitherto used in their electrodes or wiring. In such use, Al is inexpensive, has a high electrical conductivity and can give a dense oxide film formed on its surface, and hence it has many advantages such that insides can be chemically protected to become stable and it can achieve a good adhesion to Si. Incidentally, with an increase in the degree of integration of integrated circuits such as LSIs, it has become particularly necessary in recent years to make wiring finer or form wiring in multi-layers. Hence, a severe demand that has not been made so far is directed to conventional Al wiring. As the size is made finer with an increase in the degree of integration, the surfaces of LSIs or the like tend to be formed in intense irregularity after going through the steps of oxidation, diffusion, thin-film deposition, etching and so forth. Electrodes or wiring metals, however, must be deposited on stepped surfaces without causing disconnection or must be deposited in via holes that are minute in diameter and deep. In the case of 4 Mbit or 16 Mbit DRAMs (dynamic RAM), the aspect ratio (via hole depth/via hole diameter) of via holes in which metals such as Al must be deposited is 1.0 or more and the via hole diameter itself is 1 µm or less. It is accordingly required to provide a technique that enables good deposition of Al even in the via holes having a large aspect ratio. Besides, Al must be deposited not only to fill up the via holes but also to form wiring on insulating films and besides the resulting deposited films must be in a good quality. For the formation of such deposited films, conventional sputtering can not meet the demand stated above. In conventional sputtering, films are formed in an extremely small thickness at relatively stepped portions or sidewalls of insulating film to cause disconnection in an extreme case, resulting in a greatly low reliability of LSIs. As for bias sputtering, the process has technical problems difficult to solve, e.g., damage by charged particles or a limit in deposition rate. Some techniques are proposed which intend to solve such technical problems. One of them was applied for a patent in the U.S.A. on September 24, 1990 under Serial No. 587,045, entitled "Process for Forming Deposited Film", and is disclosed in European Patent Publication No. 420,595. This process comprises selectively depositing Al in a via hole the bottom of which is formed of an electron donative surface, thereafter generating plasma in the vicinity of the surface of a substrate to modify the electron non-donative surface formed of, e.g., SiO 2 or Si 3 N 4 , and depositing Al on the modified surface. Here, the modification is meant to bring the surface into the state that free electrons are seemingly present even if the surface is electron non-donative, and can participate in the surface reaction. According to plasma surface modification treatment, it is possible to cut off Si-O bonds to generate electrons on account of unbonded arms. Such electrons accelerate chemical reaction as a result of electron transfer between the substrate and starting material gas molecules adsorbed on the substrate surface. Fig. 1 illustrates an apparatus for such conventional metal film formation. Reference numeral 1 denotes a semiconductor wafer on which the metal film is to be formed, and which is placed on a substrate holder 3 provided with a heating means 4. To a reaction chamber 2, an exhaust system is provided via a gate valve 7 and a slow-leak valve 8 so that the inside of the reaction chamber can be evacuated. Above the reaction chamber 2, a bubbler 6 and a mixing device 5 are provided as a starting material gas feeding means that feeds starting material gas into the reaction chamber. Reference numeral 10 denotes a transport chamber through which the wafer 1 is carried in or taken out of the reaction chamber 2, which is provided via a valve 13. The inside of the chamber 10 is connected to an exhaust system 12 via a valve 11 so that the inside of the chamber 12 can be independently evacuated. Reference numeral 16 denotes an electrode that generates plasma; and 14, a power source that supplies an electrical energy for generating the plasma, which is earthed at its terminal end. In the process for forming metal film making use of the apparatus for forming metal film described above, electrons must be supplied uniformly over the whole deposition surface of the substrate, and hence this is a method of processing one sheet of substrate (wafer) at one time deposition process. Thus, it has been difficult to obtain a throughput high enough to achieve mass production. Now, the present inventors have tried a method of forming metal films using the Fig. 1 apparatus whose reaction chamber has been enlarged so that a plurality of substrates can be held. However, compared with the Fig. 1 apparatus, a poor uniformity tended to result with regard to the metal films on different wafers and the metal film on the same wafer which were formed by non-selective deposition utilizing plasma, and it was difficult to make control for obtaining always uniform metal films. In "Symposium on VLSI Technology", 4-7 June 1990, pp. 5 and 6, it is described a method of selective and nonselective deposition of aluminum by LPCVD using dimethylaluminium hydride. The Al is selectively deposited on Si and TiN (electron donative materials). Moreover, Al can be nonselectively deposited on SiO 2 (electron non-donative material) when the SiO 2 has been pretreated with RF plasma before Al deposition. JP-A-58-043508 discloses a mass-production type film fabricating device, wherein thermal electrodes having substrates on both sides thereof are supported on one movable support. These electrodes are alternately arranged with electrodes which do not support a substrate. A reaction gas is decomposed by means of a glow discharge developed between said electrodes, and a film is formed on said substrates. EP-A-0 143 479 discloses a plasma-stimulated chemical vapor deposition device comprising a substrate supporting component. The substrate supporting component comprises a plurality of electrodes, which are alternately arranged in the reaction chamber, supporting a plurality of substrates. This device is used for depositing among others metal films such as Al, Ti or W films. SUMMARY OF THE INVENTION An object of the present invention is to provide an apparatus for forming metal film and a process for forming film that can form metal films in a high throughput and yet can obtain metal films in an excellent uniformity. Another object of the present invention is to provide an apparatus for forming deposited film and a process for forming deposited film that can make excellent control of plasma and can readily carry out changeover between selective deposition and non-selective deposition. The above objects can be achieved by an apparatus for forming metal film for forming metal films on substrates according to claim 7. The above objects can be also achieved by a process for forming metal film according to claim 1. According to the present invention, a uniform plasma can be generated corresponding with all the deposition surfaces of a plurality of substrates, and hence uniform surface modification and/or uniform supply of free electrons can be carried out, so that metal films can be formed selectively. According to the present invention, different from the conventional sheet-by-sheet treating apparatus for forming metal film, a plurality of substrates can be treated at one time film deposition process, and hence good and uniform metal films can be continuously formed over the whole surfaces of the substrates. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a diagrammatic illustration of a conventional apparatus for forming metal film. Fig. 2 is a diagrammatic illustration of a reference example of an apparatus for forming metal film. Fig. 3 is a diagrammatic illustration of the disposition of electrodes in the apparatus for forming metal film according to the reference example. Fig. 4 is a diagrammatic illustration of an embodiment of the apparatus for forming metal film according to the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS The apparatus for forming metal film of the present invention comprises a reaction chamber provided in its inside with a plurality of pairs of electrodes alternately arranged and a plurality of substrates disposed between the electrodes. An electrical energy is applied across the pairs of electrodes to generate plasma across the electrodes. The reaction chamber may be made of quartz or a metal. In the case when the selective deposition as described later is carried out, it is preferred to employ a reaction tube made of quartz. The electrodes may be formed of a conventional conductive metallic material, and may be so constructed as to also serve as substrate holders that holds the substrates. As an energy supply means for supplying the electrical energy, a conventional high-frequency power source can be preferably used. As a means for heating the substrates, a heating element provided inside the reaction chamber or a heating coil or lamp provided outside the reaction chamber may be used. Different from the conventional constitution, it is preferable to use a reaction tube made of quartz which is a transparent insulator, to provide the heating means outside the reaction tube, and to provide electrodes for generating plasma inside the reaction tube. Such a combination is desirable. A gas feed means, which is a means for feeding in the reaction chamber the desired gas alone or a mixture thereof with other gas, may comprise a high-pressure gas bomb, a gas feed pipe, a mass flow controller, a valve, a mixer, a purifier, a filter, a bubbler and so forth, which may be used in appropriate combination according to the gas used. A gas exhaust means may be so constructed that a mechanical booster pump, a turbo molecular drag pump, an oil diffusion pump and so forth are connected to the inside of the reaction chamber via a valve or a filter. Reference Example Fig. 2 is a diagrammatic illustration of an apparatus for forming metal film. Reference numeral 101 denotes a reaction tube made of quartz, which is substantially kept close from the surroundings and forms a space in which the metal films are formed. In the present example, quartz is used as a material for the reaction tube 101, which may alternatively be made of a metal. In the latter case, the reaction tube 101 should be cooled. Reference numeral 102 denotes a metal flange for opening or shutting the reaction tube 101; and 103, a metal flange for introducing starting material gas and reaction gas into the reaction tube 101 or inserting the substrates. Reference numeral 104 denotes a heater that surrounds the periphery of the reaction tube 101. The temperature of substrates 105 can be controlled by controlling the heating temperature of this heater 104. Here, the substrates 105 are fitted to substrate holders (conductive electrodes) 106. A gas feed system is constructed in the following way. Reference numeral 107 denotes a gas mixer, in which reaction gas and carrier gas are adjusted to the desired flow rates and mixed and from which the mixed gas is fed into the reaction tube 101. In instances in which a material kept liquid at room temperature is used as the reaction gas, the gas is introduced into a material vaporizer 109 through a gas feed line 108, and the material as the reaction gas is vaporized there. The carrier gas is sent to a gas mixer 107 through a carrier gas feed line 110. Reference numeral 111 denotes a gas line through which an inert gas such as N 2 is fed into the reaction tube 101 when the inside of the reaction tube 101 having been evacuated is restored to have atmospheric pressure. A gas exhaust system is constructed in the following way. The gasses inside the reaction tube 101 are exhausted by means of an exhaust unit 113 connected through a gas exhaust pipe 112. The exhaust unit 113 is comprised of an exhaust pump such as a turbo molecular drag pump. Reference numeral 114 denotes an exhaust main valve, which is opened when the inside of the reaction tube 101 is evacuated. Reference numeral 115 denotes a control valve, which controls the pressure inside the reaction tube 101 to be an appropriate pressure in the course of metal deposition. A power source as an electrical energy supply means for generating plasma is comprised of a high-frequency power source unit 116. The high-frequency power source line is led to a high-frequency power source terminal 117 and at the same time connected to another high-frequency power source terminal 118 provided on the side of the substrates fitted to the electrodes. Thus the electrical energy is supplied to the substrate holder through a conductive rail 119. Fig. 3 is a diagrammatic illustration to detail the electrode portion in Fig. 2. A plurality of first electrodes 220 and second electrodes 221 are vertically and alternately arranged. In the embodiment shown in Fig. 3, the electrodes should be vertically or non-horizontally arranged. They may alternatively be horizontally arranged. The first electrodes 220 and second electrodes 221 are connected to conductive rails 222 and 223, respectively. The first electrodes 220 connected to the conductive rail 222 are connected to a high-frequency power source unit 226 through a terminal 224 provided at an end of the conductive rail 222, via a terminal 225 on the side of the high-frequency frequency power source. Similarly, the second electrodes 221 are connected to the high-frequency power source unit 226 through a terminal 227 provided at an end of the conductive rail 223, via a terminal 225 on the side of the high-frequency power source. Reference numeral 229 denotes semiconductor substrates provided between the first electrodes 220 and second electrodes 221. Here, a high-frequency voltage is applied across the conductive rails 223 and 222, whereby a uniform plasma can be generated across the respective electrodes 221 and 220 serving also as substrate holders. The application of the high-frequency voltage is controlled by a control circuit provided in the unit 226 to take timing of voltage application and set the time for which the voltage is applied. Example 1 Fig. 4 is a diagrammatic illustration of an embodiment of the apparatus for forming metal film according to the present invention. In the drawing, reference numeral 301 denotes a reaction tube made of quartz, which is substantially kept close from the surroundings and forms a space in which the metal films are formed; 302, a heater for controlling the substrate temperature; 303, electrodes serving also as semiconductor substrate holders; 304, semiconductor substrates (wafers); 305, opposing electrodes with which the electrodes 303 form pairs; 306, a gas inlet for starting material gas; 307, a deposit shield plate; 308, a contact connected with an external power source for the wafer-opposing electrodes; 309, a contact connected with an external power source for the wafer-side electrodes; 310, an exhaust pipe; 311, high-frequency power source unit; 312, a pressure control valve for regulating the pressure in the reaction tube; and 313, an exhaust unit comprised of a turbo molecular drag pump or the like. The substrate-side electrodes 303 serve as wafer boats on both sides of which the wafers are provided, and are connected to the external high-frequency power source unit via the contact 309. The wafer-opposing electrodes 305 are so structured as to have no contact connected with the wafer-side electrodes at all, and in themselves are connected to the external high-frequency power source unit via the contact 308. After the wafer boats having such a structure have been received in the reaction tube 301, the exhaust unit 313 and the pressure control valve 312 are operated to control the pressure inside the reaction tube to be at any desired level suited for the metal film formation. The temperature inside the reaction tube is controlled by the heater 302. Now, after the temperature and pressure have reached predetermined levels, a starting material gas is fed at an appropriate mixing ratio into the reaction tube from the gas inlet 306. Then the high-frequency power source unit 311 is operated to generate plasma across the electrodes 303 and the opposing electrodes 305. Thus, it becomes possible to carry out deposition for the metal film formation. At this stage, the electrodes 303 and the opposing electrodes 305 are completely brought into non-contact with each other interposing the deposit shield plate 307, so that any short between the electrodes 303 and the opposing electrodes 305 can not occur during the application of high-frequency power. The apparatus for forming metal film of the present invention as described is used in a process for forming metal film as described below. The process is a CVD (chemical vapor deposition) process carried out using as a starting material gas a compound containing at least one of metal atoms such as Al, W, Ti, Mo, Cu and Ta. The starting material gas specifically includes trimethylaluminum (TMA), triisobutylaluminum (TiBA), dimethylaluminum hydride (DMAH), monomethylaluminum hydride (MMAH), diethylaluminum hydride (DEAH), triethylaluminum (TEA), trichloroaluminum (TClA), tungsten hexafluoride (WF 6 ), trimethyltungsten (W(CH 3 ) 3 ), triethyltungsten (W(C 2 H 6 ) 3 ), bisacetylacetonatocopper (Cu(C 5 H 7 O 2 ) 2 ), bisdipivaloylmetanitocopper (Cu(C 11 H 19 O 2 ) 2 ), bishexafluoroacetylacetonatocopper (Cu(C 5 HF 6 O 2 ) 2 ), tetrachlorotitanium (TiCl 4 ), tetrabromotitanium (TiBr 4 ), tetramethyltitanium (Ti(CH 3 ) 4 ), and molybdenum calbonyl (Mo(CO) 6 ). The above CVD may be selective CVD that effects selective deposition only on a certain region, or may be non-selective CVD that effects deposition on the whole surface of a wafer. The apparatus described above can best exhibit its performance when the selective CVD is carried out without using plasma and thereafter the non-selective CVD is carried out utilizing plasma. In this case, the process may be carried out in such a way that the plasma is generated only when the wafer surfaces are plasma-treated before the non-selective CVD is carried out, and no plasma is generated thereafter, or in such a way that the plasma is maintained in the course of the non-selective CVD. In the case when both the selective CVD and the non-selective CVD are carried out, the whole surfaces in the reaction chamber except the electrode portions opposing the wafers should be comprised of insulating materials. To get better understanding of this mechanism, changeover between selective deposition and non-selective deposition will be explained by referring an embodiment of Al. - Process for Forming Film - A process of forming metal films mainly composed of Al (including pure Al) that are preferred in the present invention (an Al-CVD process) will be described below. This process is a process suited for burying a metal material in fine and deep openings (contact holes or through-holes) having, for example, an aspect ratio of 1 or more, and is a deposition process with an excellent selectivity. Metal films formed by this process can have a very good crystallinity so that a monocrystalline Al can be formed, and little contain carbon or the like. Similarly, the metal films thus formed have a resistivity as low as 0.7 to 3.4 µΩ·cm, have a reflectance as high as 85 to 95% and have excellent surface properties such that a 1 µm or higher hillock density is about 1 to 100 cm -2 . As to the probability of occurrence of alloy spikes at the interface between the metal film and silicon, it can be equal to substantially zero when a failure probability of a 0.15 µm semiconductor junction is taken. This process is a process in which a deposited film is formed on an electron-donative substrate by the use of an alkylaluminum halide gas and hydrogen gas. In particular, using a methyl group-containing alkylaluminum hydride such as monomethylaluminum hydride (MMAH) or dimethylaluminum hydride (DMAH) as the starting material gas and H 2 as the reaction gas, the substrate surface may be heated in the presence of a mixed gas of these, so that an Al film with a good quality can be deposited. Here, in the case of selective deposition of Al, the surface temperature of the substrate may preferably be maintained at a temperature not lower than the decomposition temperature of the alkylaluminum hydride and lower than 450°C, more preferably from 260°C to 440°C, and most suitably from 260°C to 350°C. A method by which the substrate is heated so as to have the temperature within the above range may include direct heating and indirect heating. Al films with a good quality can be formed at a high deposition rate particularly when the substrate is maintained at the above temperature by direct heating. For example, when the temperature of the substrate surface in the formation of Al films is set within the preferable temperature range of 260°C to 440°C, films with a good quality can be obtained at a deposition rate as high as 300nm to 500 nm/min (3000 Å to 5000 Å/min)which is higher than the case of resistance heating. Such direct heating (the energy from a heating means is directly transmitted to the substrate to heat the substrate itself) may specifically include lamp heating using a halogen lamp or a xenon lamp. The indirect heating may include the resistance heating, which can be carried out using a heater element provided in a substrate holding member disposed in the deposited film formation space to hold the substrate on which the deposited film is to be formed. According to this method, the CVD process may be applied to the substrate on which an electron donative surface portion and an electron non-donative surface portion are present together, so that a monocrystal of Al is formed only on the electron donative surface portion in a good selectivity. An electron donative material and an electron non-donative material are used here. The electron donative material is meant to be a material such that free electrons are present in the substrate or free electrons are intentionally produced therein, and having a surface capable of accelerating chemical reaction on account of electron transfer between the substrate and starting material gas molecules adsorbed on the substrate surface. For example, metals and semiconductors commonly come under this material. A metal or semiconductor on the surface of which a thin oxide film is present can also cause the chemical reaction on account of the electron transfer between the substrate and starting material gas molecules adsorbed thereon, and hence is also included in the electron donative material of the present invention. The electron donative material may specifically include p-type, i-type and n-type conductivity semiconductors as exemplified by Group III-V element compound semiconductors of a double, triple or more, multiple system comprised of a combination of a Group III element such as Ga, In or Al and a Group V element such as P, As or N, or semiconductor materials such as monocrystalline silicon and amorphous silicon; and the following metals, alloys or silicides, as exemplified by tungsten, molybdenum, tantalum, copper, titanium, aluminum, titanium aluminum, titanium nitride, aluminum silicon copper, aluminum palladium, tungsten silicide, titanium silicide, aluminum silicide, molybdenum silicide and tantalum silicide. On the other hand, a material that forms the surface on which Al or Al-Si is not selectively deposited, i.e., the electron non-donative material may include silicon oxide formed by thermal oxidation, CVD or the like and glasses such as BSG, PSG and BPSG, or oxide films, thermal nitride films, and silicon nitride films formed by plasma CVD, reduced pressure CVD, ECR-CVD or the like. According to this Al-CVD process described above, a metal film mainly composed of Al as described below can also be selectively deposited, and shows excellent properties as its film quality. For example, in addition to the alkylaluminum hydride gas and hydrogen, a gas containing Si atoms such as SiH 4 , Si 2 H 6 , Si 3 H 8 , Si(CH 3 ) 4 , SiCl 4 , SiH 2 Cl 2 or SiHCl 3 , a gas containing Ti atoms such as TiCl 4 , TiBr 4 or Ti(CH 3 ) 4 and/or a gas containing Cu atoms such as bisacetylacetonatocopper Cu(C 5 H 7 )O 2 ) 2 , bisdipivaloylmetanitocopper Cu(C 11 H 19 O 2 ) 2 or bishexafluoroacetylacetonatocopper Cu(C 5 HF 6 O 2 ) 2 may be fed into the reaction chamber in an appropriate combination to give a mixed gas atmosphere, and a conductive material as exemplified by Al-Si, Al-Ti, Al-Cu, Al-Si-Ti or Al-Si-Cu may be selectively deposited to form the electrode. The Al-CVD process described above is a film forming process that can achieve an excellent selectivity and can give a deposited film with good surface properties. Hence, when a non-selective film forming process is applied in the subsequent deposition step to also form an Al film or a metal film mainly composed of Al, on the aforesaid Al film formed by selective deposition and SiO 2 .or the like serving as an insulating film, it is possible to obtain a preferable metal film having high general-purpose properties as films for semiconductor device wiring. Such a metal film can be specified as follows: A combination of selectively deposited Al, Al-Si, Al-Ti, Al-Cu, Al-Si-Ti or Al-Si-Cu with non-selectively deposited Al, Al-Si, Al-Ti, Al-Cu, Al-Si-Ti or Al-Si-Cu. It is also possible to utilize the Al-CVD process to form the metal film on an insulating film. For that purpose, the insulating film may be subjected to the step of surface modification to form a substantially electron donative surface portion. Such surface modification can be carried out by plasma CVD or a method in which damage caused by plasma is imparted to the insulating film. Formation of Al films by the use of the metal film forming apparatus of the embodiment described above will be described below. Dimethylaluminum hydride (DMAH) is used as the starting material gas, and H 2 as the carrier gas. The deposition of Al should be carried out at a degree of vacuum of 160 to 400 Pa (1.2 to 3 Torr) and a DMAH partial pressure of 0.15 to 1.68 Pa (1.1 × 10 -3 to 12.6 × 10 -3 Torr), and should be carried out at a deposition temperature of 270 to 290°C. Under such deposition conditions, the deposition rate comes to be about 80 nm/min (800 Å/min) when Al is selectively deposited by organic metal CVD in via holes whose bottoms are comprised of the electron donative material. The deposition time comes to be 7 minutes and 30 seconds when, for example, Al is selectively deposited by organic metal CVD in contact holes of 600nm (6,000 Å). When the deposition of Al is carried out by this organic metal CVD, no high-frequency plasma is generated. Thereafter, the high-frequency power source unit is electrified to generate a high-frequency voltage, so that the plasma is generated across the electrodes and thus the surfaces formed of, for example, SiO 2 electron non-donative material which constitutes the substrates fitted onto the electrodes can be modified to give the surfaces formed of the electron donative material. With regard to the plasma irradiation time, degree of vacuum, partial pressure of DMAH and deposition temperature at this stage, the treatment is carried out under the same conditions as the conditions for the deposition of Al described above. The irradiation with plasma should be carried out for about 1 minute. Plasma electron density should be 5 × 10 8 to 3 × 10 9 cm -3 right above the substrate. The plasma power should be 0.1 to 1 W/cm 3 . The surface modification of SiO 2 by this irradiation with plasma enables formation of dense and uniform Al nuclei, and hence uniform Al films can be formed over the whole surfaces of the substrates. At this stage, this Al films are formed at a deposition rate of about 80 nm/min (800 Å/min). The Al films formed under such conditions have a resistivity of as low as 3 uΩ · cm, and Al films with a good quality can be formed. According to the present embodiment, different from the conventional sheet-by-sheet system, Al films can be formed on a plurality of substrates at one time without any lowering of the Al film deposition rate. Thereafter, in order to fabricate electronic devices or integrated circuits, the Al films are subjected to patterning to form metal wiring and/or electrodes. Experiment As an example of the process for forming metal film according to the present invention, the process for forming Al film will be described with reference to Fig. 4. After the wafer boats on which wafers were held were received in the reaction tube 301, the exhaust unit 313 and the pressure control valve 312 were operated to control the pressure inside the reaction tube to be at any desired level suited for the metal film formation. The temperature inside the reaction tube was controlled by the heater 302. Now, after the temperature and pressure reached predetermined levels, a starting material gas dimethylaluminum hydride (DMAH) and hydrogen gas were fed at an appropriate mixing ratio into the reaction tube from the gas inlet 306. As a result, selective film growth of Al was effected on the conductive regions. Film formation at this stage was carried out under conditions set as follows: Temperatures, 270 to 290°C; pressure inside the reaction tube, 160 Pa (1.2 Torr); and DMAH/H 2 = 1/10. Selective deposition carried out under such conditions resulted in a deposition rate of about 80 nm/min (800 Å/min), and hence it took 7 minutes and 30 seconds to bury Al in 600nm (6,000 Å) contact holes by the selective deposition. After the contact holes had been buried, the high-frequency power source unit 311 was operated to generate plasma across the electrodes 303 and the opposing electrodes 305, to thereby carry out surface modification and deposition of Al also on SiO 2 . Since this surface modification becomes unnecessary once at least one atom layer of Al film has been formed on the surface, the irradiation with plasma was carried out for about 1 minute. For this reason, even though structurally an error or errors were more or less present in the distances between the electrodes 303 and the opposing electrodes 305, the deposition time of about 1 minute at most had no serious influence on the layer thickness distribution among wafers. At the initiation of this non-selective deposition, the deposition at the time of the irradiation with plasma was carried out under the same conditions as the selective deposition with regard to the ratio of DMAH/H 2 and the temperature, and the irradiation with plasma was carried out under conditions of an RF power of 0.1 W/cm 3 as a maximum value and an electron density of about 10 9 cm -3 as a minimum value. The surface modification on SiO 2 by this irradiation with plasma enabled formation of dense and uniform Al nuclei, and uniform Al films with less roughed surfaces and with a good quality were formed on SiO 2 . As described above, the dense and uniform Al nuclei were formed over the whole substrate surfaces on account of the surface modification, and hence, even though the irradiation with plasma was thereafter stopped, the uniform Al films were formed on the whole surfaces. The whole-surface Al deposition was at a deposition rate of about 80 nm/min (800 Å/min). The Al films deposited under such conditions had a resistivity of 3 µΩ · cm and thus it was possible to form Al films with a good quality.

Claims: A process for forming metal film comprising the steps of: providing a plurality of substrates (304) having an electron donative surface and an electron non-donative surface in a reaction chamber (301); feeding into said reaction chamber (301) a starting material gas for forming metal films; selectively forming a metal film on said electron donative surface; and forming thereafter a metal film on said electron non-donative surface, utilizing plasma generated across a plurality of first and second electrodes (303, 305), wherein said plurality of substrates (304) are provided on either the first or second electrodes (303; 305) alternately arranged in said reaction chamber (301); all the surfaces in the reaction chamber comprise an insulator material, except for the portions of said plurality of first and second electrodes (303, 305) which oppose the substrates (304); a shield plate (307) is provided between conductive rails supporting the first electrodes (303) and the second electrodes (305) such that the first and second electrodes do not contact each other; contacts (308, 309) for connecting the first and second electrodes (303, 305) to a power source (311) are separated from the reaction space in which the metal films are formed by means of the shield plate (307). The process for forming metal film according to claim 1, characterized in that said plurality of substrates (304) are disposed on any one sides of either the first or second electrodes (303; 305). The process for forming metal film according to claim 1, characterized in that said plurality of substrates (304) are disposed on both sides of either the first or second electrodes (303; 305). The process for forming metal film according to claim 1, characterized in that said plurality of substrates (304) are disposed in such a state that their deposition surfaces are non-horizontal. The process for forming metal film according to claim 1, characterized in that said electron donative surface is a surface comprising a conductor or a semiconductor, and said electron non-donative surface is a surface comprising an insulating material. The process for forming metal film according to claim 1, characterized in that said electron non-donative surface is subjected to surface modification utilizing said plasma, and thereafter a metal film is formed on said electron non-donative surface without use of said plasma. An apparatus for forming metal films on substrates, comprising: a reaction chamber (301); a plurality of first and second electrodes (303, 305) alternately arranged in said reaction chamber (301); an energy supply means (308, 309, 311) that supplies to said first and second electrodes an electrical energy for generating plasma; a heating means (302) for heating a plurality of substrates (304) disposed between said first and second electrodes (303, 305); a gas feed means (306) that feeds into said reaction chamber (301) a starting material gas for forming metal films; a shield plate (307) provided between conductive rails supporting said first and second electrode (303, 305) such that the first and second electrodes do not contact each other; and contacts (308, 309) separated from the reaction space in which the metal films are formed by means of the shield plate (307) for connecting the first and second electrodes to said power source (311); said plasma being generated across said first and second electrodes (303, 305) to form metal films on said plurality of substrates (304), wherein all the surfaces in the reaction chamber (301) comprise an insulator material, except for the portions of said plurality of first and second electrodes (303, 305) which oppose the substrates (304); said plurality of substrates (304) are provided on either said first or second electrodes (303; 305). The apparatus for forming metal film according to claim 7, wherein in use said plurality of substrates (304) are disposed on any one sides of either the first or second electrodes (303; 305). The apparatus for forming metal film according to claim 7, wherein in use said plurality of substrates (304) are disposed on both sides of either the first or second electrodes (303; 305). The apparatus for forming metal film according to claim 7, wherein in use said plurality of substrates (304) are disposed in such a state that their deposition surfaces are non-horizontal.

Inventors: HAYAKAWA YUKIHIRO, KATAOKA YUZO, HAYAKAWA, YUKIHIRO, KATAOKA, YUZO, HAYAKAWA, YUKIHIRO, C/O CANON KABUSHIKI KAISHA, Kataoka, Yuzo, c/o Canon Kabushiki Kaisha
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1992
Main classification: C23C16
IPC codes: C23C16, H01L21, H01J37