Method and apparatus for fabrication of three-dimensional articles by weld deposition

Abstract: In a method and apparatus for forming a three-dimensional object, successive layers (2) of metal are welded together to build the object. After each weld deposited layer (2) is formed, a complementary material (6) is placed adjacent the layer. In this manner, layers of material form a block of welded metal and complementary material. Then, all or a portion of the complementary material (6) which serves as a support structure during forming, can be removed. The welded layers (2) are milled to a final shape either after each layer (2) is formed or after all layers (2) have been made. Existing CNC machines (20) can be easily modified to practice the method.

Description: Field of Invention The invention relates to a method and apparatus for creating a three-dimensional object by welding successive layers of metal. Background of the Invention Several methods have been proposed and utilized for creating three-dimensional objects by the incremental material build up of thin layers. These processes include lamination, selective laser sintering, ballistic powder metallurgy, three-dimensional printing, stereolithography and near net thermal spraying. Lamination involves the simple process of cutting layers of a selected material and then bonding those layers together. The layers may be pre-cut to shapes corresponding to a cross section through the article to be created. Alternatively, standard shapes of material can be stacked and bonded together. Then, the assembled structure is cut or machined to produce the desired shape. In. United States Patent No. 4,752,352, Michael Feygin proposes a computer controlled method and apparatus for forming a laminated object. He provides a supply station, a work station for forming a material into a plurality of layers for lamination, an assembly station for stacking the layers in sequence into a three-dimensional object, a station for bonding the laminations to complete the formation of the three-dimensional object and a control station. In his patent, Mr. Feygin discloses a method in which the laminations are cut from a roll of material, lifted, stacked and bonded under the direction of a computerized controller. The layers are bonded together by adhesive or brazing. This and other lamination techniques have several disadvantages. First, the bond between layers is critical and limits the strength of the object. Second, creation of each layer of the laminate also results in the production of significant amounts of waste materials. Finally, lamination is suitable for only those materials which can be formed into thin layers which can be bonded together. In laser sintering, a laser is used to cure a starting material into a certain configuration according to the manner in which the laser is applied to that material. Products formed with this method are porous. Stereolithography is a more recent yet similar process which creates plastic prototype models directly from a vat of liquid photocurable polymer by selectively solidifying it with a scanning laser beam. An example of this method is described in European Patent 322 257. Both of these methods require a substantial amount of curable raw material. In both cases the laser must be carefully controlled to achieve the desired shape. In some applications, the laser typically does not fully cure each cross section. Rather, the laser cures the boundary of a section and then cures an internal structure or honeycomb that traps the uncured fluid. Thereafter, the article must be subjected to final curing under separate ultraviolet lights or heat treatment. Additional post processing, such as careful sanding and grinding, is required for making smooth, accurate surfaces. In ballistic powder metallurgy beams of particles are directed to the coordinates of a three-dimensional object in a three-dimensional coordinate system. A physical origination seed to which the particulate matter is attracted is required. The process may use a beam of particles directed to the origination seed which builds the particles upward from that seed. Alternatively, one can use an energy beam which attracts the particulate matter already in the environment to the seed or another coordinate. Such a system is disclosed by William E. Masters in United States Patent No. 4,665,492. This method cannot be used to make objects having undercuts therein without creating support structures at the same time. Normally, the support structures are created with the particle beam during the creation of the object. Such support structures must be removed by cutting, grinding or machining. Three-dimensional printing is another technique similar to ballistic powder metallurgy. One variation of this technique creates layers of particles to produce a three-dimensional image in much the same manner that an ink jet printer produces two-dimensional images. The technique relies upon thermal shock or drop on demand material delivery techniques. A thermal shock technique forms a particle by vaporizing a small area of the fluid directly behind the nozzle. The drop on demand nozzle includes a piezo electric element to constrict the cavity thereby forcing a drop past the nozzle plate. In both instances the material is directed to a work surface in a manner to build up the article. This technique can only be used for certain kinds of materials and produces porous products. In another variation of three-dimensional printing a series of two-dimensional layers are created by adding a layer of powder on top of a work surface. The powdered layer is selectively joined where the part is be formed by ink jet printing of a binder material. The work surface is then lowered and another layer of powder is spread out and selectively joined. The layering process is repeated until the part is completely printed. Following a heat treatment the unbonded powder is removed leaving the fabricated part. Although this technique has been proposed for metal, ceramic and plastic materials, it is limited to those materials to which a reliable binder can be applied and produces porous products. Yet another method which has been proposed for forming metal articles is DC arc-plasma spraying. In this process a plasma is generated between to concentric water cooled electrodes which form a chamber into which an inert gas is injected. Fine metal particles are injected into the plasma by means of a mechanical feeder and carrier gas. The particles are sprayed onto a substrate by the plasma torch. None of the just described layered fabrication techniques have been successfully used to make quality steel parts. Of the previously described layering processes only laser sintering and ballistic particle manufacturing have been proposed for steel part fabrication. However, objects made from laser sintering are porous. Such porosity is not acceptable for most metal parts. Ballistic particle manufacturing utilizes a particle beam. It is difficult to define the beam cross-section to acceptable levels of accuracy. The products made with this method generally have internal weakness caused by porosity and weak bonds. Metal tubular shapes have been made by shape melting. Shape melting is a process whereby structural components are manufactured by depositing weld material layer-upon-layer until the desired geometry is achieved. Weld build-up operations like Shape Melting require a preform which is generally a machined piece of metal onto which the first layer of the build-up is deposited. It is termed a "preform" because its form and machined shape reflects an intended final shape of the build-up. A preform serves as the support for the the molten as-deposited weld metal, as the conduit for conduction cooling of the freshly deposited weld metal, as the means for restraining weld contraction stresses thereby limiting distortion of the build-up, and as the general cross-sectional shape for the weld build-up, e.g., a cylindrical build-up would require a cylinder in the starting preform. All of the described prior art techniques require expensive and sometimes custom-made motion control equipment. None are adaptable for use on existing metal forming or fabricating equipment such as computer numerical controlled (CNC) machines. The art has attempted to make objects by spraying layers of metal on a substrate. Bonding between layers is often questionable. The layer interfaces are often weak points in the object. The interface between the substrate and the first layer is also weakly bonded in many articles. Problems have occurred in that the layers have tended to camber and possibly to peel apart from the substrate. Therefore, one must have a release agent or compatible substrate. WO-A-90/15375 and US-A-4621762 both disclose methods and apparatus for making objects by welding successive layers of metal onto a substrate. FR-A-2569136 is a french language equivalent of US-A-4621762. The methods disclosed require the use of multidirectional welding robot arms to permit the welded material to be deposited on the top, sides or even beneath undercut portions of the article being formed. There is a need for a method and apparatus to manufacture quality metal parts by incremental laminar build-up of material. The method and apparatus should be capable of producing articles having undercuts and irregular shapes. The method and apparatus should also be usable with existing equipment. Brief Description of the Invention We provide a method and apparatus to manufacture a three-dimensional object by incremental material build up of thin layers. Each layer is composed of two portions. A first portion represents a cross sectional slice of the three dimensional object being built. The second portion is the complement of the object shape of the first portion and serves as a structure which supports the growing object form. Both portions are built on a substrate. The first portion is formed by welding successive layers of metal to build the article. The second portion is a complementary material which can be applied by spraying, for example. Each welded layer corresponds to a cross sectional slice through an article such that there is at least one layer for every parallel cross section normal to a centre line through the article. Complementary material is placed adjacent each layer after it is formed. The layers are milled to a final dimension either after all layers have been formed or individually before a successive layer is formed thereon. Hereinafter, we will use the term milled and milling to encompass all techniques involving use of a tool to remove material including use of a grinding wheel or a cutting wheel. After a layered structure is built up which contains the object made of the welded material surrounded by the complementary material, the complementary material is then removed leaving the created object. The complementary material can easily be removed by chemical etching or machining. If the complementary material is sufficiently brittle, all or most of it can be easily broken away. Other objects and advantages of the invention will become apparent in connection with the description of the preferred embodiments shown in the following figures in which comparable parts carry the same reference numerals. Description of the Drawings Figure 1 is a cross-sectional view of an article being created on a substrate using a first preferred embodiment of our method. Figure 2 is a diagram showing a present preferred embodiment of our apparatus for making three-dimensional objects using our method. Figure 3 is a cross sectional view of the block of an article being created using alternative preferred embodiments of our method. Figure 4 is a cross-sectional view of an article being made with our method showing the edge of a layer being milled. Figure 5 is a cross-sectional view of an article being made with our method showing the top of a layer being milled. Figure 6 is a cross-sectional view of an article being made with our method showing the article being contoured to a desired shape. Figure 7 is a cross-sectional view showing placement of complementary material adjacent to each layer. Description of the Preferred Embodiments In Figure 1 we show an article 1 which can be manufactured in accordance with our method and apparatus. This article is formed from several layers 2 welded together on a substrate 3 placed on a work surface 4. Iron-based alloys, nickel based alloys, aluminum-based alloys and titanium based alloys can be used to form the layers 2. To make the object of Figure 1 we use a weld head 10 which can be attached to a CNC machine 20 as shown in Figure 2. The work surface 4 is a table 22 that is capable of moving in two or three directions as indicated by arrows x, y and z. The weld head 10 is attached to a head 21 of a CNC machine 20. Such heads are normally movable in a vertical plane as indicated by the z arrow. In some machines the head is also movable in the x and y directions. The head 21 is designed to hold cutting tools (not shown) for cutting a workpiece (also not shown) on table 22. To make the article we place or form a substrate 3 on the work table 22. The substrate 3 should be made of a conductive material to which one can weld. The substrate could be the weld metal. The substrate 3 is electrically connected to earth 23. Then, the weld head 10 can be used to electrically arc weld a metal which is fed onto the substrate. If desired, more than one metal could be used to produce an article. Preferably the metal is in the form of welding rods or weld wire which can be automatically fed to a position under the weld head from supply 24. The table 22 or head 21 is moved in a manner to direct the delivery of the metal being welded in a predetermined pattern to form each layer 2. A complementary material is placed adjacent each layer by spray gun 26. Other techniques could also be used to place the complementary material. Such techniques include thermal sprays, delivery of the complementary material in a carrier such as an air stream or liquid slurry, feeding the complementary material from a gravity feed device, and use of a manual device such as a hand sifter to place the material by hand. After each layer is completed, work table 22 is dropped to allow for deposition of the next layer. Although we prefer to move the weld head 10 and spray gun 26 during formation of each layer one could also use a fixed spray gun and move the work surface 22. If the complementary material 6 is applied in a liquid or powder form, it is desirable to provide a frame 8 around the article 1 being formed. This frame could be made of the same material as the article and welded in place using the same technique as is used to from the article 1. As shown in Figure 3 it may be desirable to extend the frame into the area 9 adjacent the frame. In that event, complementary material would only be placed in the area 7 adjacent the articles. In other circumstances one may wish to apply the complementary material in powder form and bond only that portion of the complementary material adjacent the article. In that event area 7 in Figure 3 would be bonded complementary material and area 9 would be powdered complementary material. The complementary material could be bonded by selective heating techniques or by addition of a binder or catalyst. The art has observed in some metal spray processes that residual stress develops in the sprayed metal layer causing the layer to camber and possibly to peel. To relieve the stress the art has shot peened such layers. The technique is only successful in situations where shot is evenly applied over the layer. Since our layers are flat, we can use this technique. Therefore, we prefer to provide a shot peener 25 for shot peening each layer. It is also possible to relieve the stress by induction heating. Therefore, we alternatively provide an induction heater 27 which we move over each layer to selectively heat the surface. Such heating is easier to accomplish on flat layers rather than on curved and irregular surfaces. Upon completion of the process, one will have a block of material. Because we have deposited a complementary material 6 with the deposition material, we are able to create intricate shapes and parts having undercut portions. For the particular object of Figure 1, the complementary material 6 in each layer supports the the ends of the welded material above that layer. We prefer that the complementary material have either very high electrical conductivity, such as copper, or very low electrical conductivity, such as ceramics. These types of material will not generate or retain significant amounts of heat. We also prefer to use a brittle material such as most ceramics. If that type of material is used the complementary material 6 can be easily broken away from the object 1 by vibration, ultrasonic vibration and heating of the article to cause thermal expansion of the article. We have found that if the article is to be fabricated in steel or other metal alloy most ceramics, copper and copper alloys make a suitable complementary material. We have found that ceramic comprised of 60% Fascote Refractory and 40% Fastcote Binder works well as a complementary material. These products are sold by the Ransom and Randolph Division of Dentsply International. As shown in Figure 7 the complementary material can be sifted, blown or sprayed over each layer of welded metal filling in the region adjacent to the just welded metal as well as covering the top of each layer 2. Then squeegee 12 is drawn across the layer to remove excess material. Alternatively, one could cure the ceramic and mill away excess material. We further prefer to provide a milling head or a grinding wheel 14 (or a combination of these) as shown in Figures 4, 5 and 6. In Figure 5 this head 14 passes over each layer trimming that layer to an exact thickness. The process is then repeated for each layer until the final block of material is produced. In Figures 4 and 6, the mill head 14 having tools 15 or 16 is used to shape the periphery of each layer 2. One could contour the article to any desired configuration through the use of appropriately shaped tools. Beveled tool 16 is used to produce a sloped side rather than a vertical edge as is made with tool 15. Moreover, one could make an article having an irregular configuration which might include undercuts and overlaps. In some applications it may be desirable to mill the article after it has been completely formed. The solid-freeform fabrication system disclosed here would also permit the fabrication of complete functional assemblies containing two or more mating parts in one process without the requirement of discrete assembly operations. For example, the article 1 in Figure 1 could be formed in the shape of a ball head and the frame 8 could be formed as a ball socket. After forming, the complementary material 6 is removed leaving a ball joint. As can be seen from Figure 2, our method can be followed using a CNC machine modified to include a weld head. Welding rod, weld wire and complementary material could be automatically or manually supplied. Even if the method is fully automated into a CNC machine, the cost of modifying such a machine is substantially less than the capital costs for other automated equipment for making articles by incremental build up of thin layers. Because our layers are formed by welding there will be perfect fusion bonding between layers. As a result the object formed by our method will have high density and metallic bonds.

Claims: A method for the fabrication of a three-dimensional metal article comprising the steps of: (a) positioning a substrate on a work surface; (b) welding a layer of metal onto the substrate or onto a previous layer of metal formed thereon; (c) placing or forming a layer of complementary material alongside the metal layer of step (b) so that the complementary material is adjacent to each layer to form a complement of the object shape of the adjacent layer of weld deposited metal and serve as a structure which supports the growing object form; (d) repeating steps (b) and (c) to build up a number of successive layers, each layer corresponding to a respective cross sectional slice through the article; (e) removing the complementary material; and (f) removing the substrate. A method according to claim 1, wherein each step (b) is followed by a step of milling the edge and top surfaces of the metal layer just deposited, the edge milling being such as to provide a vertical or non-vertical edge to the layer. A method according to claim 1 or claim 2, wherein each step (b) is followed by a step of shot peening and/or heating some or all of the welded layer that has just been applied. A method according to any preceding claim, wherein the metal of the metal layer of step (b) is an iron-based alloy, a nickel-based alloy, an aluminium-based alloy, a titanium-based alloy or two or more such alloys. A method according to any preceding claim, wherein the complementary material of step (c) is a ceramic, a cermet, copper or a copper alloy. A method according to any preceding claim, wherein the complementary material of step (c) is a powder and a portion of the powder adjacent the welded metal (b) of the same layer is bound together into a mass and optionally hardened whereas another portion of the powder is not bound together. A method according to any preceding claim, wherein in step (e) and/or step (f) the complementary material and/or the substrate are removed by etching, milling, vibration, ultrasonic vibration and/or thermal expansion of the article. A method according to any preceding claim, wherein a frame is placed or formed around the successive layers of step (b) before performing step (c) so that the complementary material of step (c) can be placed between the frame and the associated layer of welded metal. A method according to any preceding claim, wherein step (c) further comprises hardening at least a portion of the complementary material by adding a binder, using a catalyst and/or applying heat. An apparatus for forming an integral three-dimensional article by welding successive layers of material comprising: (a) a work surface (22) for supporting a substrate (3); (b) a work head (21) over the work surface (22) carrying welding means (10) for welding successive layers (2) of metal onto a substrate (3) thereon; and (c) means (26) for placing a layer (6) of complementary material adjacent to each successive layer (2) of the weld deposited metal to form a complement of the object shape of the adjacent layer of weld deposited metal and serve as a structure which supports the growing object form; An apparatus according to claim 10, wherein the means (26) for placing a layer (6) of complementary material adjacent to each successive layer (2) of the weld deposited metal is carried by the work head (21). An apparatus according to claim 10 or claim 11, wherein the work head (21) carries, in addition to the welding means (10): a milling head (14) for edge and face dressing the side edges and/or top faces of successive layers (2) of weld deposited metal; a shot peening head (25) for shot peening the weld deposited metal (2) of successive layers; and/or an induction heater (27) for heating the weld deposited metal (2) of successive layers to relieve residual stress therein, the work head (21) and/or the work surface (22) being optionally movable in a desired manner in three mutually perpendicular directions by a computerized numerical controller.

Inventors: PRINZ FRITZ B, WEISS LEE E, PRINZ, FRITZ B., WEISS, LEE E.
Applicants: PRINZ FRITZ B, WEISS LEE E, PRINZ, FRITZ B.
Application year: 1992
Main classification: G05B19
IPC codes: B23K9, G05B19, B23K37, B29C67, B22F3