METHOD AND MEANS FOR COATING A SURFACE WITH A RESISTANT FACING BY CHEMICAL-VAPOR DEPOSITION

Abstract: A substrate is provided with a resistant coating by the chemical-vapor deposition of hard material, by passing a gaseous mixture of a precursor of the material, an accelerant, an oxidant, and a carrier gas over the substrate surface, and then removing the by-products and unreacted materials; mixtures of hard materials are obtained by using a co-reagent in the gaseous mixture. The substrate is preferably heated. The figure shows a schematic of the apparatus which includes the precursor (102), the accelerant (104) which are vaporized and transferred to a reactor (120). A mixture of chromium oxide and tin oxide is the preferred coating material, obtained by decomposition of chromyl chloride and monobutyltintrichloride on the substrate surface in the presence of methylisobutylketone and air. Other metal mixtures can also be used.

Description: METHOD AND MEANS FOR COATING A SURFACE WITH A RESISTANT FACING BY CHEMICAL-VAPOR DEPOSITION BACKGROUND OF THE INVENTION Cross-Reference to Related Application. This application is a continuation-in- part of our copending United States Patent Application, Serial Number 814,367, filed 12/26/92. Field of the Invention. This invention is in the field of improving the wear- and chemical-resistant characteristics of materials by providing a resistant surface coating. More particularly, the present invention is in the field of applying a wear-resistant, and generally hard, metal-oxide or other facing by deposition of a coating from the vapor phase. Description of the Prior Art. Materials chosen for engineering functions necessarily have mechanical characteristics suitable for the applications for which they are selected; these materials include, e.g., glass, aluminum, steel, brass, and a wide variety of polymers. However, it is rare that a particular material has optimal characteristics for all of the operational parameters to which the particular item or part will be subjected. Thus, some modification to the base material may be required to provide optimal working characteristics for the finished item. For instance, a plastic part can be metal-coated by vacuum sputtering, to furnish a conductive, reflective or decorative surface not inherent in the base material, and a pump housing or reciprocating-engine block may be formed of cast iron, aluminum, or steel for strength, but because the wear- resistance characteristics in the cylinder area are rarely adequate, some modification has to be made for that purpose. In cast-iron and aluminum engine blocks specifically, it is common to provide an insert cylinder sleeve of, e.g., hard alloy steel in which the piston travels and against which the piston rings bear, both for acceptable wear life of the unit and for operating efficiency resulting from the relatively low sliding friction between the matching parts. The same principle holds true for the combustion-chamber wall and the apex seal in rotary engines. SUBSTITUTE SHEET In the matter of combustion engines, the heat-transfer characteristics of the structural components are also of importance; if the engine operating temperature is maintained at too low a temperature, operating efficiency suffers, and exhaust emissions increase. From the viewpoint of net energy efficiency, the hotter the engine is able to run, the lower is the requirement to discard parasitic heat, and the greater is the engine efficiency. However, if the interface between a piston ring and the cylinder wall becomes too hot, the lubricant film can thin out and permit seizing and galling of the respective surfaces, with concomitant rapid increase of wear and decrease of the effective operational life of the engine. One approach to the problem of increasing the operational temperature of a combustion engine has been to make a cylinder with a hard, refractory and corrosion-resistant surface having a low coefficient of friction against which the piston ring runs in juxtaposition to that surface. A method known in the present art is that of applying an aqueous solution of a chromium salt to a cylinder wall, and thereafter heating the wall to drive off the water and to convert the salt to Cr 2 0 3 . An engine thus treated is capable of ranning at higher temperatures than is an untreated one, with a resultant improvement in operating efficiency. The method of coating by the application of a solution of a chromium salt is effective for the purpose described here, but may require more than ten repetitions of the steps of applying the solution and subsequent heating. As a result, the process is relatively labor-intensive, time-consuming and costly. Methods of vapor-phase deposition, known also as chemical-vapor deposition (CVD) of hard materials are known in the art. Stemmler, et aL, in US 4,525,389, describe the coating of a workpiece by a volatile chromium compound and steam. In US 4,310,567, Tasata, et aL, disclose the deposition of a material on a heated substrate by directing a stream of the material or its precursor onto the substrate under conditions where coating or reaction occurs at the substrate surface. SUBSTITUTE SHEET In British patent 1,408,294, there is described at page 3, lines 100 et seq., the deposition of a Cr 2 O 3 coating on a cemented carbide cutting tool by the oxidation of a halogenated chromium compound. Powell, et al., in Vapor Deposition, (John Wiley & Sons, New York, 1966; p. 402), have reported that codeposition of boric and chromic oxides improved adhesion and cohesion, but provided a coating with some solubility in water. In the described prior art, however, no system has yet produced a functional wear- or chemical-, and specifically corrosion-resistant, coating with acceptable economics. SUMMARY OF THE INVENTION The present invention is the coating of a substrate by CVD of a hard or wear-resistant material, which comprises treating the substrate with a gaseous mixture of a precursor of the material in the presence of an accelerant and one or more carrier or reactant fluids, and thereafter removing by-products and unreacted materials. In a preferred embodiment, the substrate is heated. BRIEF DESCRIPTION OF THE DRAWING The drawing figure shows a schematic representation of the process of the invention. DISCUSSION OF THE INVENTION This invention is the method and composition of coating on a substrate with a hard or wear-resistant material, which comprises treating the substrate surface, at a temperature high enough to provide reaction or decomposition on that surface, with a mixture of at least one precursor of that material, and at least one accelerant, in the presence of material such as oxygen, to cause formation of the hard material. A carrier fluid can be used to transport materials to the substrate surface. Wear-resistant materials useful in this invention, termed "hard materials" for the purposes of this specification, comprise hard metal compounds generally, such as oxides, nitrides, oxynitrides and the like. In the preferred SUBSTITUTE SHEET case of metal oxides, the reaction of the precursor takes place with an oxygenating substance; the oxides are formed at or near, and deposited on, the substrate surface by reaction of a precursor of the hard material; further, the hard material can be a mixture of different oxides, nitrides, oxynitrides, and other deposited hard materials. A carrier fluid such as air serves to transport reagents to the substrate surface, and to remove reaction products and unreacted reagents. Precursors for deposition include metal compounds generally which are capable of reacting to provide the desired material on the substrate surface. Precursors useful in the present invention include, e.g., compounds of aluminum, cadmium, chromium, cobalt, germanium, indium, iridium, molybdenum, nickel, tantalum, titanium, tungsten, vanadium, zinc and zirconium. Preferred precursors are chromium, titanium and tungsten compounds. Compounds from which the hard materials of this invention can be deposited include, e.g., aluminum alkyls and alkoxides, cadmium alkyls, chromyl chloride, germanium halides and alkoxides, nickel alkyls and carbonyl, indium alkyls, titanium alkoxides and halides, tungsten oxychloride, vanadium halides, zinc alkyls, zirconium alkoxides, and mixtures thereof. Specific and non-limiting examples of such compounds include, e.g., CrO 2 Cl 2 , GeBr 4 , Ti(OC 3 H 7 ) 4 , TiCl 4 , TiBr 4 , Ti(C 6 H 9 0 2 ) 4 , Zr(OC 5 H u ) 4 , Ni(CO) 4 , VC1 4 , Zn(CH 3 ) 2 , WOCI 3 and the like, and mixtures of these materials. Preferred compounds are chromyl chloride, titanium alkoxides and halides, and tungsten oxychloride. Those skilled in the art will understand that precursors discussed in this specification must be sufficiently volatile, alone or with other materials, and sufficiently stable under the process conditions, to be a part of the composition from which the desired hard materials are deposited. A preferred hard material of this invention comprises chromium oxide, deposited from a precursor mixture containing chromyl chloride. The CVD coating process of this invention comprises treating the substrate with a gaseous mixture of at least one precursor of the hard material and a co-reagent, and optionally an accelerant, and removing reaction by-products and unreacted materials, whereby the hard material is formed by reaction or decomposition of the precursor and the co-reagent at the substrate surface so treated. "Co-reagent," as used herein, means a material which, in combination with the precursor, provides a deposited hard material on the substrate under the conditions of deposition. For the purposes of this specification, an "accelerant" is defined as a material whose presence in the system serves to increase the rate of deposition of the hard material onto the substrate; i.e., a rate which is greater than has heretofore been achieved in commercial practice. The accelerant may also serve as a co-reagent, to provide a deposit comprising oxides of the constituent metals; thus, the composition of the gaseous mixture at or near the substrate can comprise the precursor and a co-reagent in the carrier fluid, or it can comprise the precursor, a co-reagent and an accelerant in the carrier fluid. Where the co-reagent serves also as an accelerant, the composition can then comprise two or more components in addition to the carrier fluid. Materials useful as either or both co-reagents and deposition-rate accelerants include tin, titanium, nickel, vanadium and zirconium compounds and mixtures thereof; as heretofore noted, such materials must also be sufficiently volatile to provide an adequate quantity of material at the substrate surface for CVD of the desired coating. Illustrative examples of accelerants and co-reagents include, without limitation herein, SnCl 4 , SnBr 4 , Snl 4 , (CH 3 ) 2 SnCl 2 , (CH 3 ) 3 SnCl, (C 2 H 5 ) 3 SnH, (C 6 H 5 ) 2 SnCl 2 , (C 2 H 5 ) 2 SnCl 2 , (C 4 H 9 )SnCl 3 , TiCl 4 , TiBr 4 , Ti(C 6 H 9 O 2 ) 4 , Ti(OC 3 H 7 ) 4> Ni(CO) 4 , VC1 4 , and the like, and mixtures of these materials. Preferred compounds include SnCl 4 , (CH 3 ) 3 SnCl, MBTC, TiCl 4 , Ti(OC 3 H 7 ) 4> and Ni(CO) 4 . Those skilled in the art will recognize that the carrier fluid will most probably be in the gaseous phase in the vicinity of the substrate surface, due SUBSTITUTE SHEET to the elevated temperature in that region. The carrier fluid preferably has an oxygenating capability, but can be any material capable of transporting the precursor, co-reagent and accelerant, or any of them, to the reaction site, and is gaseous under the process conditions. The carrier fluid can be a substance selected from the group consisting of air, nitrogen, oxygen, C0 2 , water, noble gases, and mixtures thereof. Oxygenation of the precursor can be effected by supplying a source of oxygen, either as such or in air, or in a material having oxygen in the molecule, wherein the material has the formula R m C(OR' n ) p , where R and R 1 are independently chosen from hydrogen; substituted and unsubstituted straight, cyclic, or branched-chain alkyl or alkenyl of from one to about six carbons; phenyl, substituted phenyl, or R"CH 2 CH 2 -, where R" is MeO 2 C-, EtO 2 C-, CH 3 CO-, or HO 2 C-, m is 1, 2 or 3, n is zero or 1, and p is 1 or 2, provided that m+p cannot exceed 4. The source of oxygen can be selected from the group consisting of alcohols with from 1 to about 8 carbons, aldehydes and ketones with from 1 one to about 8 carbons, and ethers, esters and acid anhydrides with from 1 to about 6 carbons in each moiety of the molecule. Those skilled in the art will realize that the coating produced in accordance with this invention can also provide resistance to general chemical and corrosive attack on the coated surface. Coating effected by this invention comprises deposition onto a substrate from a composition of at least one volatile compound of a metal precursor of the hard material, an accelerant, a co-reagent or both, in a molar ratio of from 0.1-1/0.1-1/0.1-1, the composition being mixed in a carrier fluid at from about 0.05 to about 1 molar, and applied to a substrate at from about 150 degrees Celsius (°C) to a higher temperature limited only by the decomposition or deformation of the substrate material. DESCRIPTION OF THE PREFERRED EMBODIMENTS A preferred embodiment of the present invention is the CVD coating of a substrate with a refractory or wear-resistant material. More preferably, this SUBSTITUTE SHEET invention comprises the deposition of the refractory or wear-resistant material onto the substrate surface from a gaseous mixture of at least one precursor of the material and an accelerant, and removing reaction by-products and unreacted materials, where during at least the deposition step, the surface of --> 5 the substrate is maintained at an effective temperature high enough to cause decomposition of the precursor on or near the substrate surface, i.e., by direct heating of the substrate, or by plasma deposition. Alternatively, the temperature of the precursor or mixture of precursor, co-reagent and accelerant can be established in a manner to cause decomposition of the 10 mixture at or near the substrate surface. In normal plant practice, the process comprises the steps of separating reaction products and unreacted materials, and recycling the unreacted materials. Most preferably, the components of the present invention comprise a volatile chromium compound and a co-reagent gas selected from the group 15 consisting of at least one volatile tin or titanium compound, or mixtures of those compounds, and an accelerant, deposited onto a substrate at an elevated temperature; the accelerant is optionally oxygenating, and a carrier fluid can be used as a vehicle. The accelerant and the carrier can, in some embodiments, be the same material; further, combinations of accelerants are 20 within the spirit and scope of this invention. Deposition can be carried out below, at, or above atmospheric pressure. A preferred embodiment of this invention comprises a hard coating formed by deposition onto a substrate from a composition of at least one volatile compound of a metal precursor of the hard material, an accelerant, a 25 co-reagent or both, in a molar ratio of from 0.1-1/0.1-1/0.1-1, the composition being mixed in a carrier fluid at from about 0.05 to about 1 molar, and applied to a substrate at from about 150°C to a higher temperature limited y. only by the decomposition or deformation of the substrate material. The most-preferred embodiment of the invention comprises the 30 composition CrO 2 Cl 2 , methyl isobutyl ketone (MIBK) and monobutyltintrichlorids (MBTC) in a molar ratio of 1:1:1 applied from a SUBSTITUTE SH gaseous solution of 0.2 mol percent of the 1:1:1 mixture in dry air at a flow rate of about 25 standard liters per minute (SLM), at a gas velocity of from about 0.1 to about 10 meters per second, to a substrate maintainted at a temperature of from about 600 to about 700°C. For the purposes of this specification, the term "volatile compound" is chosen to mean a compound having a vapor pressure high enough to permit its conversion to the vapor phase without significant decomposition in the course of the process described herein; the vapor pressure can be a partial pressure in association with another material, such as can be obtained with steam- or other co-distillation. The coating of this invention can also be applied by ion sputtering of precursor materials onto the substrate, and by the use of precursor materials having relatively low volatility by entraining them in carrier-fluid streams. The carrier fluid is preferably gaseous. The composition of the coating is a mixture of chromium and tin oxides, and can be a solid solution which is either crystalline or amorphous to x-rays. In the drawing figure, apparatus for effecting CVD of an exemplary hard material in accordance with this invention comprises containers 102 for the precursor of the refractory substance deposited, 104 for the accelerant, and 106 for a co-reagent if used. Transport lines 202, 204 and 206 convey the respective materials through suitable mass-flow meters 112, 114 and 116 to vaporizer 110. Carrier fluid is also conveniently measured by meter 118 from source 108 through transport line 208 into vaporizer 110. Source 108 can include, e.g., compressed air, steam or nitrogen, bottled CO 2 and the like. Transport line 210 carries the mixture of reagents, co-reagents and carrier fluid to reactor 120; that reactor has means, not shown but well known to those skilled in the art, for establishment and maintenance of an elevated temperature above about 150 degrees Centigrade (°C). The reagents, upon encountering heated substrate surfaces either in reactor 120 or on articles contained therewithin, react to form a hard coating, optionally admixed with compounds, typically oxides, of e.g., tin or titanium. SUB Transport line 220 serves to convey waste products from the reaction in reactor 120 to waste-treatment means 122. Treatment means 122 is conveniently a scrubber or other device serving to keep deleterious materials from being exhausted into the atmosphere. Duct 240 and blower 140 are provided to recycle reagents and carrier gas if desired to improve the overall efficiency of the process. Although one application of the process of this invention is generally sufficient to provide the desired coating thickness, the application can be repeated as often as desired in order to build up successive layers, to insure that no uncoated areas remain on the substrate, or to provide a specified thickness, as the process or product may reqire. In an illustration of the utility of the present invention, a single-cylinder cast-iron diesel-engine block is prepared by acid-etching the cylinder, rinsing it with tap water, and then drying it, preferably by heating. The cylinder, as reactor 120, is then connected to transport line 210 with gas-tight fittings known to those skilled in the art. Chromyl chloride, Cr0 2 Cl 2 , from container 102, is admixed in the vapor phase in vaporizer 110 with MIBK from container 104 and with MBTC from container 106, and air from source 108, each of the gases being conducted through its respective transport line. The gaseous mixture from vaporizer 110 is then caused to pass over the surface of the cylinder 120, maintained at 450°C. An oxidation reaction occurs at the heated surface of the cylinder to deposit a layer of mixed chromium and tin oxides approximately 20 micrometers (μm) in thickness. Reaction by-products and unreacted materials are removed through transport line 220 to waste- treatment means 122. Compounds useful in the method of the present invention are precursors of the hard material whose vapor pressures, alone or in admixture with other materials, are adequate to provide a useful quantity of refractory or wear- resistant material at the surface of the article to be treated; such materials are within the broad range of metal compounds which provide hard materials upon reaction under the CVD process conditions. SUBS I Combinations of accelerants are within the spirit and scope of this invention; thus, a gaseous mixture containing, e.g., both MBTC and Ni(CO) 4 has utility in the CVD of a hard coating on, e.g., a steel, cast-iron or other substrate. In a further application of the utility of this invention, the surface of a cylinder liner is anodically etched, followed by a water rinse. The cylinder liner is heated to 150°C, and CrO 2 Cl 2 , MIBK and MBTC in a 1:1:1 molar ratio, admixed at 0.2 molar in air are then caused to pass over the heated surface as set forth hereinabove. The resultant Cr 2 O 3 layer is found to be about 25 μ thick. From the description of the invention, those skilled in the art will now also realize that the coating method and materials taught herein are applicable to a variety of substrates, including, e.g., brass, bronze, aluminum, cast iron, castable and stainless steel, titanium, polymeric materials and the like. Those skilled in the art will further understand that the surface of a given substrate must generally be prepared prior to the coating method set forth here, and that the preparation may vary with the material being treated or the nature of the coating. One embodiment of this invention comprises CrO 2 Cl 2 , MIBK, and MBTC in the molar ratio of from about 0.01 to about 1 Cr0 2 Cl 2 , to about 0.01 to about 20 MIBK, to about 0.01 to about 20 MBTC, the composition being mixed with air at about 0.01 to about 10 molar, applied to a substrate at a temperature above about 150°C. The most-preferred embodiment comprises Cr0 2 Cl 2 , MIBK, and MBTC being applied from a gaseous solution of 0.2 mole percent in dry air at about atmospheric pressure to a substrate having a surface temperature of from about 600 to about 700 °C. The utility of this invention is demonstrated by the following examples. Example 1 A cast-iron cylinder liner is prepared by acid-etching, rinsing and then drying. The liner is heated to a temperature between 400 and 650°C and allowed to come to thermal equilibrium. The heated surface is then treated by passing Cr0 2 Cl 2 , admixed in the vapor phase with MIBK, MBTC and air, over that surface. An oxidation reaction occurs at the heated surface of the cylinder to deposit a layer of mixed chromium and tin oxides approximately 25 μm. in thickness. Example 2 The surface of the cylinder liner of Example 1 is prepared by anodically etching, followed by a water rinse and then drying. The liner is heated to a temperature between 400 and 650°C and allowed to come to thermal equilibrium. CrO 2 Cl 2 , admixed in the vapor phase with MIBK, MBTC and air, is then caused to pass over the heated surface. An oxidation reaction occurs at the heated surface of the cylinder to deposit a layer of mixed chromium and tin oxides approximately 25 nm in thickness. Example 3 A 3.2 millimeter (mm)-thick by 32 mm-diameter disk of cast iron is anodically etched and then heated in air at 700°C for 20 minutes (min). The substrate is subsequently placed in a reactor whose temperature is such that the substrate temperature is 625°C. A 1:1:1 molar mixture of chromyl chloride, MIBK, and MBTC at 0.2 mol percent of the mixture in dry air is vaporized and caused to impinge upon the surface at 40 SLM for 25 min. An adherent coating of about 25μm in thickness is obtained. The substrate is allowed to cool, and is analyzed. The coating is found to consist of chromium oxide and tin oxides. Example 4 A 3.2 mm-thick by 32 mm-diameter disk of 17-4 stainless steel is liquid- honed and heated in air. The substrate is heated to 625°C, and coated by a gas phase consisting of one part by volume of hydrogen gas, 44 parts of nitrogen gas, and five parts by volume of a 1/1/1 molar mixture of oxygen, acetone and chromyl chloride. The resulting coating is found to consist of chromium oxide. SUBS Example 5 A 3.2 mm-thick by 32 mm-diameter disk of cast iron is plated with chromium. The sample is oxidized in a furnace at 750°C. Subsequently, the disk is placed on a nickel block heated to 650°C. Coating vapors as described in example 3, maintained at 100°C, are passed over the surface of the substrate, whereby the process results in a deposit as discussed in reference to examples 2 and 3. Example 6 A 3.2 mm-thick by 32 mm-diameter disk of brass is liquid-honed and heated in air. The substrate is coated by the application of a gaseous mixture as in example 3; the coating temperature of 550°C provides a deposit as in example 3. Example 7 A gaseous mixture consisting of nitrogen, MIBK and chromyl chloride is passed over a stainless-steel substrate prepared as in Example 6. The temperature of the substrate is 625°C. The resulting coating is smooth, hard and adherent. Example 8 A 95 mm x 540 mm cast-iron substrate is anodically etched and heated to 500°C in air. A gas-phase composition as in Example 3 is passed over the substrate. The sample is wear-tested against zirconia, and found to impart significant wear resistance to the cast iron by reducing the wear rate by a factor of about 30. Those skilled in. the art will realize that proper pretreatment of the surface is necessary to secure the optimum adherence of the coating to the substrate, and that the step of anodically etching the cylinder walls set forth above is only exemplary. Other methods could include, e.g., electroless or electrolytic deposition of a preplate material, acid washing, surface ablation, and the like. SUBSTITUTE SHEET Example 9 A 3.2 mm-thick by 32 mm-diameter disk of cast iron is prepared as in Example 3. A 1:1:1 molar mixture of Cr(NO 3 ) 3 7V2H 2 O, SnCl 4 and propyl pentanoate at 0.2 mol percent of the mixture in dry air is vaporized and impinged upon the surface at 40 SLM for 25 min. Analysis shows an adherent coating of about 20 μm in thickness, consisting of chromium and tin oxides. Example 10 The surface of the cylinder liner of Example 1 is prepared by anodically etching, followed by a water rinse and then drying. The liners are heated to a temperature between 400 and 650°C and allowed to come to thermal equilibrium. CrO 2 Cl 2 , admixed in the vapor phase with MIBK, Ti(C 5 H 7 O 2 ) 4 , and air, is then caused to pass over the heated surface. An oxidation reaction occurs at the heated surface of the cylinder to deposit a layer of mixed chromium and titanium oxides approximately 25 μm. in thickness. Examples 11 through 26 A 3.2 mm-thick by 32 mm-diameter disk of cast iron is prepared as in Example 3. A 1:1:1 molar mixture of a metal compound, a co-reagent and an oxygen-containing compound at 0.2 mol percent of the mixture in a dry carrier gas is vaporized and caused to impinge upon the surface at 40 SLM for 25 min. Adherent coatings from about 20 to about 30 m in thickness are obtained; the coatings contain mixtures of oxides of the metals used in the example. SUBSTITUTE SHEET Modifications and improvements to the preferred forms of the invention disclosed and described herein may occur to those skilled in the art who come to understand the principles and precepts hereof. Accordingly, the scope of the patent to be issued hereon should not be limited solely to the embodiments of the invention set forth herein, but rather should be limited only by the advance by which the invention has promoted the art. S

Claims: What is claimed is: 1. The method of coating a substrate by the deposition of a hard material onto the substrate which comprises treating the substrate with a gaseous mixture comprising at least one precursor of the hard material and at least one accelerant. 2. The method of claim 1 wherein the deposition is by chemical-vapor deposition. 3. The method of claim 2 wherein the gaseous mixture further comprises a carrier fluid. 4. The method of claim 2 wherein the gaseous mixture comprises a metal compound. 5. The method of claim 2 wherein the gaseous mixture comprises at least one material selected from the group consisting of compounds of aluminum, cadmium, chromium, cobalt, germanium, indium, iridium, molybdenum, nickel, tantalum, titanium, tungsten, vanadium, zinc and zirconium. 6. The method of claim 2 wherein the gaseous mixture comprises at least one material selected from the group consisting of aluminum alkyls and alkoxides, cadmium alkyls, chromyl chloride, germanium halides and alkoxides, nickel alkyls and carbonyl, indium alkyls, titanium alkoxides and halides, tungsten oxychloride, vanadium halides, zinc alkyls, zirconium alkoxides, and mixtures thereof. 7. The method of claim 2 wherein the gaseous mixture comprises at least one material selected from the group consisting of Al^H^, Cr0 2 Cl 2 , GeBr 4 , Ti(OC 3 H 7 ) 4 , TiCl 4 , TiBr 4 , Ti(C 5 H 7 0 2 ) 4 , Zr(OC 5 H n ) 4 , Ni(CO) 4 , VC1 4 , Zn(CH 3 ) 2 , WOCl 3 , and mixtures thereof. 8. The method of claim 2 wherein the gaseous mixture further comprises a co-reagent. 9. The method of claim 2 wherein the gaseous mixture further comprises a material selected from the group consisting of tin, titanium, nickel, vanadium and zirconium compounds, and mixtures thereof. SUBSTITUTE SHEET 10. The method of claim 2 wherein the gaseous mixture further comprises a material selected from the group consisting of SnCl 4 , SnBr 4 , Snl 4 , (CH 3 ) 2 SnCI 2 , (CH 3 ) 3 SnCl, ( H^SnH, (C 6 H 5 ) 2 SnCl 2 , (C,H 5 ) 2 SnCl 2 , C 4 H 9 SnCl 3 , TiCl 4 , TiBr 4 , Ti( H 9 0 2 ) 4 , Ti(OC 3 H 7 ) 4> Ni(CO) 4 , VC1 4 , and mixtures thereof. 11. The method of claim 2 wherein the gaseous mixture further comprises a material of the formula R m C(OR' n ) p , where R and R 1 are independently chosen from hydrogen; substituted and unsubstituted straight, cyclic, or branched-chain alkyl or alkenyl of from one to about six carbons; phenyl, substituted phenyl, or R"CH 2 CH 2 -, where R" is MeO 2 C-, EtO 2 C-, CH 3 CO-, or HO 2 C-, m is 1, 2 or 3, n is zero or 1, and p is 1 or 2, provided that m+p cannot exceed 4. 12. The method of claim 2 wherein the gaseous mixture further comprises a material selected from the group consisting of alcohols with from 1 to about 8 carbons, aldehydes and ketones with from 1 one to about 8 carbons, and ethers, esters and acid anhydrides with from 1 to about 6 carbons in each moiety of the molecule. 13. The method of claim 2 wherein the gaseous mixture further comprises at least one carrier fluid selected from the group consisting of air, nitrogen, oxygen, C0 2 , water, noble gases, and mixtures thereof. 14. The method of claim 3 wherein the gaseous mixture comprises a chromium, titanium or tungsten compound, a co-reagent selected from the group consisting of SnCI 4 , (CH 3 ) 3 SnCl, MBTC, TiCl 4 , Ti(OC,H 7 ) 4ι and Ni(CO) 4 , and mixtures of those compounds, and an oxygenating carrier fluid. 15. The method of claim 3 wherein the gaseous mixture comprises a chromium compound, a co-reagent selected from the group consisting of volatile tin and titanium compounds and mixtures of those compounds, and an oxygenating carrier fluid. 16. The method of claim 2 wherein treating the substrate comprises passing the gaseous mixture over the substrate, the surface temperature of the substrate being maintained above about 150°C and below the deformation or decomposition temperature of the substrate. 17. The method of claim 2 wherein the substrate is cleaned prior to the step of treating with the gaseous mixture. 18. The method of claim 2 wherein the hard material comprises chromium oxide. 19. The method of claim 2 wherein the hard material is an x-ray- crystalline mixture comprising chromium oxide and tin oxide or titanium oxide. 20. The method of claim 2 wherein the precursor of the hard material is a chromium compound. 21. The method of claim 2 wherein the precursor of the hard material is chromyl chloride. 22. The method of claim 2 wherein the co-reagent is a tin compound. 23. The method of claim 2 wherein the co-reagent is monobutyltin trichloride. 24. The method of claim 2 wherein the precursor comprises chromyl chloride and the co-reagent comprises monobutyltin trichloride. 25. The method of claim 2 further comprising the step of removing reaction products and unreacted materials. 26. The method of claim 2 further comprising the steps of separating reaction products and unreacted materials, and recycling the unreacted materials. 27. A coating on a substrate obtained by the deposition of a hard material onto the substrate from a gaseous mixture comprising at least one precursor of the hard material. 28. The coating of claim 27 wherein the deposition is by chemical- vapor deposition. 29. The coating of claim 27 wherein the gaseous mixture further comprises a carrier fluid. 30. The coating of claim 27 wherein the gaseous mixture comprises a metal compound. 31. The coating of claim 27 wherein the gaseous mixture comprises at least one material selected from the group consisting of compounds of SUBSTITUTE SHEET aluminum, cadmium, chromium, cobalt, germanium, indium, iridium, molybdenum, nickel, tantalum, titanium, tungsten, vanadium, zinc and zirconium. 32. The coating of claim 27 wherein the gaseous mixture comprises at least one material selected from the group consisting of aluminum alkyls and alkoxides, cadmium alkyls, chromyl chloride, germanium halides and alkoxides, nickel alkyls and carbonyl, indium alkyls, titanium alkoxides and halides, tungsten oxychloride, vanadium halides, zinc alkyls, zirconium alkoxides, and mixtures thereof. 33. The coating of claim 27 wherein the gaseous mixture comprises at least one material selected from the group consisting of A1(C 2 H 5 ) 3 , Cr0 2 Cl 2 , GeBr 4 , T O H^, TiCl 4 , TiBr 4 , Ti(C 5 H 7 O 2 ) 4 , Zr(OC 5 H n ) 4 , Ni(CO) 4 , VC1 4 , Zn(CH 3 ) 2 , WOCl 3 , and mixtures thereof. 34. The coating of claim 27 wherein the gaseous mixture further comprises a co-reagent. 35. The coating of claim 27 wherein the gaseous mixture further comprises a material selected from the group consisting of tin, titanium, nickel, vanadium and -rirconium compounds, and mixtures thereof. 36. The coating of claim 27 wherein the gaseous mixture further comprises a material selected from the group consisting of SnCl 4 , SnBr 4 , Snl 4 , (CH 3 ) 2 SnCl 2 , (CH 3 ) 3 SnCl, ^H^SnH, (C 6 H 5 ) 2 SnCl 2 , (C 2 H 5 ) 2 SnCl 2 , C 4 H 9 SnCl 3 , TiCl 4 , TiBr 4 , Ti(C 6 H 9 0 2 ) 4 , Ti(OC 3 H 7 ) 4> Ni(CO) 4 , VC1 4 , and mixtures thereof. 37. The coating of claim 27 wherein the gaseous mixture further comprises a material of the formula R m C(OR' n ) p , where R and R' are independently chosen from hydrogen; substituted and unsubstituted straight, cyclic, or branched-chain alkyl or alkenyl of from one to about six carbons; phenyl, substituted phenyl, or R"CH 2 CH 2 -, where R" is MeO 2 C-, Et0 2 C-, CH 3 CO-, or H0 2 C-, m is 1, 2 or 3, n is zero or 1, and p is 1 or 2, provided that m+p cannot exceed 4. 38. The coating of claim 27 wherein the gaseous mixture further comprises a material selected from the group consisting of alcohols with from SUBSTITUTE SHEET 1 to about 8 carbons, aldehydes and ketones with from 1 one to about 8 carbons, and ethers, esters and acid anhydrides with from 1 to about 6 carbons in each moiety of the molecule. 39. The coating of claim 27 wherein the gaseous mixture further comprises at least one carrier fluid selected from the group consisting of air, nitrogen, oxygen, C0 2 , water, noble gases, and mixtures thereof. 40. The method of claim 27 wherein the gaseous mixture comprises a chromium, titanium or tungsten compound, a co-reagent selected from the group consisting of SnCl 4 , (CH 3 ) 3 SnCl, MBTC, TiCl 4 , Ti(OC 3 H 7 ) 4> and Ni(CO) 4 , and mixtures of those compounds, and an oxygenating carrier fluid. 41. The coating of claim 27 wherein the gaseous mixture comprises a chromium compound, a co-reagent selected from the group consisting of volatile tin and titanium compounds and mixtures of those compounds, and an oxygenating carrier fluid. 42. The coating of claim 27 wherein treating the substrate comprises passing the gaseous mixture over the substrate, the surface temperature of the substrate being maintained above about 150°C and below the deformation or decomposition temperature of the substrate. 43. The coating of claim 27 wherein the substrate is cleaned prior to the step of treating with the gaseous mixture. 44. The coating of claim 27 wherein the hard material comprises chromium oxide. 45. The coating of claim 27 wherein the hard material is an x-ray- crystalline mixture comprising chromium oxide and tin oxide or titanium oxide. 46. The coating of claim 27 wherein the precursor of the hard material is a chromium compound. 47. The coating of claim 27 wherein the precursor of the hard material is chromyl chloride. 48. The coating of claim 27 wherein the co-reagent is a tin compound. 49. The coating of claim 27 wherein the co-reagent is monobutyltin trichloride. SUBSTITUTE SHEET 50. The coating of claim 27 wherein the precursor comprises chromyl chloride and the co-reagent comprises monobutyltin trichloride. 51. The coating of claim 27 further comprising the step of removing reaction products and unreacted materials. 52. The coating of claim 27 further comprising the steps of separating reaction products and unreacted materials, and recycling the unreacted materials. 53. A coating on a substrate obtained by the deposition of a hard material onto the substrate from a gaseous mixture comprising at least one precursor of the hard material. 54. A coated substrate obtained by the deposition of a hard material on the substrate from a mixture of at least one precursor of the material. 55. The substrate of claim 54 wherein the gaseous mixture comprises at least one material selected from the group consisting of compounds of aluminum, cadmium, chromium, cobalt, germanium, indium, iridium, molybdenum, nickel, tantalum, titanium, tungsten, vanadium, zinc and zirconium. 56. The substrate of claim 54 wherein the gaseous mixture comprises at least one material selected from the group consisting of aluminum alkyls and alkoxides, cadmium alkyls, chromyl chloride, germanium halides and alkoxides, nickel alkyls and carbonyl, indium alkyls, titanium alkoxides and halides, tungsten oxychloride, vanadium halides, zinc alkyls, zirconium alkoxides, and mixtures thereof. 57. The substrate of claim 54 wherein the gaseous mixture comprises at least one material selected from the group consisting of A^C j H^, CrO 2 Cl 2 , GeBr 4 , Ti(OC 3 H 7 ) 4 , TiCl 4 , TiBr 4 , Ti(C 5 H 7 O 2 ) 4 , Zr(OC 5 H u ) 4 , Ni(CO) 4 , VC1 4 , Zn(CH 3 ) 2 , WOCl 3 , and mixtures thereof. 58. The substrate of claim 54 wherein the gaseous mixture further comprises a co-reagent. SUB 59. The substrate of claim 54 wherein the gaseous mixture further comprises a material selected from the group consisting of tin, titanium, nickel, vanadium and zirconium compounds, and mixtures thereof. 60. The substrate of claim 54 wherein the gaseous mixture further comprises a material selected from the group consisting of SnCl 4 , SnBr 4 , Snl 4 , (CH 3 ) 2 SnCl 2 , (CH 3 ) 3 SnCl, (C 2 H 5 ) 3 SnH, (C 6 H 5 ) 2 SnCl 2 , (C 2 H 5 ) 2 SnCl 2 , C 4 H 9 SnCl 3 , TiCl 4 , TiBr 4 , Ti(C 6 H 9 O 2 ) 4 , Ti(OC 3 H 7 ) 4 Ni(CO) 4 , VC1 4 , and mixtures thereof. 61. The substrate of claim 54 wherein the gaseous mixture further comprises a material of the formula R m C(OR * n ) p , where R and R' are independently chosen from hydrogen; substituted and unsubstituted straight, cyclic, or branched-chain alkyl or alkenyl of from one to about six carbons; phenyl, substituted phenyl, or R"CH 2 CH 2 -, where R" is Me0 2 C-, Et0 2 C-, CH 3 CO-, or HO 2 C-, m is 1, 2 or 3, n is zero or 1, and p is 1 or 2, provided that m+p cannot exceed 4. 62. The substrate of claim 54 wherein the gaseous mixture further comprises a material selected from the group consisting of alcohols with from one to about eight carbons, aldehydes and ketones with from one to about eight carbons, and ethers, esters and acid anhydrides with from one to about six carbons in each moiety of the molecule. 63. The substrate of claim 54 wherein the gaseous mixture further comprises at least one carrier fluid selected from the group consisting of air, nitrogen, CO 2 , water, noble gases, and mixtures thereof. 64. The substrate of claim 54 obtained by the chemical-vapor deposition of a hard material on the substrate from a gaseous precursor of the material. 65. The substrate of claim 54 obtained by the chemical-vapor deposition of a hard material on the substrate from a gaseous mixture of a precursor of the material and a co-reagent. 66. The substrate of claim 54 obtained by the chemical-vapor deposition of a hard material on the substrate from a gaseous mixture of a precursor of the material and an accelerant. SUBSTITUT 67. The substrate of claim 54 obtained by the chemical-vapor deposition of a hard material on the substrate from a gaseous mixture of a precursor of the material, a co-reagent and an accelerant. 68. The substrate of claim 54 wherein the gaseous mixture comprises a chromium compound, an accelerant, a carrier fluid, and a co-reagent comprising a tin or titanium compound. 69. The substrate of claim 54 wherein the carrier fluid comprises air. 70. The substrate of claim 54 wherein treating the substrate comprises passing the gaseous mixture over the substrate, the surface temperature of the substrate being maintained at above about 150°C and below the deformation or decomposition temperature of the substrate. 71. The substrate of claim 54 wherein the substrate is cleaned prior to the step of treating with the gaseous mixture. 72. The substrate of claim 54 wherein the hard material comprises chromium oxide. 73. The substrate of claim 54 wherein the hard material is a mixture comprising chromium oxide and tin oxide. 74. The substrate of claim 54 wherein the hard material is a mixture comprising chromium oxide and titanium oxide. 75. The substrate of claim 54 wherein the precursor is chromyl chloride. 76. The substrate of claim 54 wherein the co-reagent is monobutyltin trichloride. 77. The substrate of claim 54 wherein the precursor is chromyl chloride, and monobutyltin trichloride is present as an accelerant. 78. A composition comprising a mixture of chromium oxide and tin oxide. 79. The composition of claim 78 produced by chemical-vapor deposition onto a substrate. 80. The composition of claim 78 produced by the chemical-vapor deposition of chromium and tin oxides onto a substrate from a gaseous mixture of precursors of the oxides. 81. The composition of claim 78 produced by the chemical-vapor deposition of chromium and tin oxides onto a substrate from a gaseous mixture of precursors of the oxides, and an accelerant. 82. The composition of claim 78 produced by the chemical-vapor deposition of a hard material onto a substrate from a gaseous mixture of chromyl chloride, monobutyltin trichloride and methyl isobutyl ketone. 83. The composition of claim 78 produced by the chemical-vapor deposition of a hard material onto a substrate from a gaseous mixture of chromyl chloride, monobutyltin trichloride and methyl isobutyl ketone in a carrier fluid. 84. The composition of claim 78 produced by the vacuum deposition of chromium oxide and tin oxide. SUBSTITUTE SHEET

Inventors: BUCHANAN JEROME LAWRENCE, DIRKX RYAN RICHARD, BUCHANAN, JEROME, LAWRENCE, DIRKX, RYAN, RICHARD
Applicants: ATOCHEM NORTH AMERICA ELF, ELF ATOCHEM NORTH AMERICA, INC.
Application year: 1992
Main classification: C23C16
IPC codes: C23C16, F02F1