Stacked type CMOS semiconductor device and method of manufacturing it

Abstract: A silicon layer (1) in a lower layer and an interconnection layer (8a) arranged in an upper layer are electrically connected through an opening (16) for contact. A silicon plug layer (15) having the same conductivity type as that of the silicon layer is embedded in the opening. The silicon plug layer is embedded in the opening by an etch back method after deposited using a CVD method. The interconnection layer in the upper layer has conductivity type different from that of the silicon plug layer. A refractory metal silicide layer (11) is formed between the upper interconnection layer and the silicon plug layer. The refractory metal silicide layer prevents pn junction from being formed between the upper interconnection layer and the silicon plug layer.

Description: The present invention concerns stacked type semiconductor devices, in particular devices - e.g. Static Random Access Memories - in which interconnection is provided between complementary MOS transistors at different levels. It is also concerned with their manufacture. A problem arises in that where doped polysilicon is used as means of interconnection, there is a difficulty in connecting transistor regions of opposite conductivity type. Ordinarily a pn junction is defined at a region where the conductivity type is changed from one type to the opposite type. A voltage drop occurs across such junction giving rise to operational problems. Also there is a problem in providing satisfactory interconnection between device elements - e.g. transistors - at different levels due to the need for via interconnection and problems in surface non-planarity of the interlevel insulation as discussed hereinbelow. In the semiconductor technology field, increase of integration density and miniaturisation of element structure are required. In order to meet such requirements, a structure is conceived in which elements are stacked three-dimensionally on a surface of a semiconductor substrate. Such a stacked type semiconductor device increases integration density of a main surface of the semiconductor substrate; however, it has been pointed out that several problems arise from the fact that an interconnection layer is arranged on a region having steps. As one example of a semiconductor device having a structure in which semiconductor elements are stacked on a substrate, a structure of an SRAM (Static Random Access Memory) will be described. Figs. 1 through 3 show a structure of a memory cell of a CMOS type SRAM using a thin film transistor as a load, which is shown in "A Memory Cell with Polysilicon Thin Film Transistor (TFT) for a 4Mbit SRAM", Tsutsumi et al., Institute of Electronics and Communication Engineers of Japan Technical Report, Vol. 90, No. 48, p7 - p13. Fig. 4 is an equivalent circuit diagram of the memory cell of the SRAM. Referring to Fig. 4, a memory cell of a CMOS type SRAM has a pair of CMOS inverters. One CMOS inverter has an n channel MOS drive transistor 20a and a p channel MOS thin film load transistor 21a. The other CMOS inverter has an n channel MOS drive transistor 20b and a p channel MOS thin film load transistor 21b. The gates of transistors 20a, 21a of said one CMOS inverter are cross connected to a store node 25b common to transistors 20b, 21b of said the other CMOS inverter, and the gates of transistors 20b, 21b of said the other CMOS inverter are cross-connected to a stored node 25a common to transistors 20a, 21a of said one CMOS inverter to constitute a flip-flop circuit. The sources of p channel MOS thin film load transistors 21a, 21b are connected to a power supply 23. Each of the sources of n channel MOS drive transistors 20a, 20b is connected to ground. Store nodes 25a, 25b of the flip-flop circuit are connected respectively to n channel MOS transfer transistors 22a, 22b. The gates of n channel MOS transfer transistors 22a, 22b are connected to a word line 27. The drain regions of n channel MOS transfer transistors 22a, 22b are respectively connected to bit lines 26a, 26b. An operation of writing information into the memory cell will be described. For example, if store node 25a is set at a ground potential, and store node 25b at a power supply potential then bit line 26a is set at a ground level, and bit line 26b at a power supply level. N channel MOS transfer transistors 22a, 22b are turned on by applying a prescribed potential to word line 27. An operation of reading information from the memory cell will be described. Bit lines 26a, 26b are connected to a sense amplifier circuit. Under the condition, word line 27 is supplied with a prescribed potential to turn on n channel MOS transfer transistors 22a, 22b. As a result, potentials of store nodes 25a, 25b are read to bit lines 26a, 26b. A specific structure of the memory cell of an SRAM will be described with reference to Figs. 1 through 3. Figs. 2 and 3 are plan structural views of the memory cell. For convenience, the memory cell is divided into a lower layer portion and an upper layer portion of a substrate to show a plan structure of the lower layer portion of the memory cell in Fig. 2 and a plan structure of the upper layer portion in Fig. 3 . Fig. 1 is a sectional structural view taken along line X-X in Figs. 2 and 3.. Referring to Figs. 1 through 3 the memory cell of an SRAM comprises n channel MOS drive transistors 20a, 20b and n channel MOS transfer transistors 22a, 22b, etc. in a lower region closer to a surface of a silicon substrate 1. P channel MOS thin film load transistors 21a, 21b are arranged in an upper region formed on a main surface of silicon substrate 1 with an interlevel insulating layer 9 interposed. Referring mainly to Fig. 1, a p well region 2 is formed on a surface of silicon substrate 1. A field oxide film 4 and a p + isolation region 3 are formed in an isolation region on a main surface of p well region 2. An n channel MOS drive transistor 20a and an n channel MOS transfer transistor 22b each comprises n + source/drain regions 7, 7, a gate oxide film 5 and gate electrode 6. Gate electrode 6 has a polycide structure formed of a polycrystalline silicon layer 6a and a metal silicide film 6b which was formed on a polycrystalline silicon layer 6a. The surface of silicon substrate 1 is covered with a thick interlevel insulating layer 9. The p channel thin film load transistor 21b is formed on a surface of interlevel insulating layer 9. A thin film transistor 14 comprises a gate electrode 8b formed on the surface of interlevel insulating layer 9, a gate oxide film 13 covering a surface of gate electrode 8b, p + source/drain regions 12a, 12c, and a channel region 12b. P + source/drain regions 12a, 12c and channel region 12b are formed in a thin polycrystalline silicon layer having a thickness of about 20nm. Gate electrode 8b includes impurity of p type. An interconnection structure of store node 25b in which n channel MOS drive transistor 20a and n channel MOS transistor 22b are formed in a lower layer, and p channel MOS thin film load transistor 21b is formed in an upper layer will be described. An opening 16 is formed in interlevel insulating layer 9. Inside opening 16, gate electrode 6 of n channel MOS drive transistor 20a and one of n + source/drain regions 7 of n channel MOS transfer transistor 22b is exposed. An interconnection layer 8a of polycrystalline silicon is formed inside opening 16 and connected simultaneously to gate electrode 6 of n channel MOS drive transistor 20a and n + source/drain region 7 of n channel MOS transfer transistor 22b. Such a contact structure is termed a shared contact. A portion of interconnection layer 8a extends to the surface of interlevel insulating layer 9. A polycrystalline silicon layer constituting a p + source/drain region 12a of p channel MOS thin film load transistor 21b is connected to a surface of the interconnection layer 8a. Interconnection layer 8a is formed of polycrystalline silicon, and p type impurity is included therein to provide conductivity. At the bottom portion of opening 16, a titanium silicide layer 11 is formed between interconnection layer 8a and source/drain region 7. Titanium silicide layer 11 prevents the formation of a pn junction caused by direct connection of interconnection layer of p type 8a and source/drain region of n type 7. A structure is termed direct contact in which interconnection layer 8a arranged on the surface of interlevel insulating layer 9 is connected to a lower layer, for example, an impurity region formed on the silicon substrate, through opening 16. However, when a direct contact structure is formed to have large differences of level such as interconnection layer 8a used for the above mentioned memory cell of an SRAM, there is a problem that patterning of an interconnection layer is difficult. Fig. 5 is a sectional view showing a manufacturing step of forming interconnection layer 8a shown in Fig. 3. After opening 16 is formed in interlevel insulating layer 9, polycrystalline silicon layer 8 is deposited on the whole surface using, for example, a CVD method. A resist is applied onto a surface of the polycrystalline silicon layer 8. The resist is developed to have a prescribed pattern shape after exposure, using a photolithography method, to form a resist mask. A polycrystalline silicon layer 8 is etched using a resist mask, and interconnection layer 8a and gate electrode 8b of thin film transistor 14 are formed. Polycrystalline silicon layer 8 is formed on the surface of interlevel insulating layer 9 having steps as shown. There are large steps of the polycrystalline silicon layer in the vicinity of opening 16. It is extremely difficult to form a very small resist mask on the surface of polycrystalline silicon layer 8 having such large steps, using an exposure technology. A recent exposure device particularly tends to reduce depth of focus. Therefore, a resolution of the resist mask deteriorates, which causes a problem that a pattern of interconnection layer 8a formed of the polycrystalline silicon layer becomes indistinct. Degradation of precision of an interconnection pattern hinders miniaturization of interconnection and impairs reliability of interconnection. It is mentioned that the use of a conductive polysilicon plug as means of interconnection between the source/drain region of an MOS transistor and a metal interconnection layer spaced from the transistor by an interlevel insulation layer, is disclosed in EP-A-0380327. The upper portion of the plug fills a funnel shaped aperture and provides effective contact to the interconnection layer. EP-A-0163132 discloses a CMOS memory device having CMOS transistors defined at the surface of a substrate. Interconnection between source/drain regions of the CMOS transistors is provided by a doped polysilicon interconnection layer. This layer is either doped to be of one conductivity type with a tungsten plug between it and a transistor source/drain region of opposite conductivity type, or the polysilicon interconnection layer is doped p-type and n-type in different regions and is shunted by a covering low-resistance layer of e.g. tungsten. This latter provides a short circuit across the pn junction formed. US-A-4829018 discloses a stacked type CMOS transistor device in which the source/drain regions of complementary transistors at respective different levels are directly connected by a conductive via of silicide material. It is said that this via might also be of polysilicon. EP-A-0281711 discloses a static random access memory device in which the gate electrode and source/drain region of an MOS transistor have a shared contact provided by a conductive polysilicon plug in interlevel insulation. This plug also makes direct contact with a conductive polysilicon layer buried in the interlevel insulation. An object of the present invention is to provide an interconnection structure in which conductive regions of different conductivity types and at different levels are connected to provide effective electrical contact. A stacked type semiconductor device and a method of manufacturing the same in accordance with the present invention are defined by the claims appended. The manufacturing method defined by the claims includes the following steps. An interlevel insulating layer is formed on a surface of a first silicon layer. An opening reaching the surface of the first silicon layer is then formed in the interlevel insulating layer. A second silicon layer is formed on a surface of the interlevel insulating layer and within the opening. The second silicon layer is etched back, and a silicon plug of the second silicon layer is formed within the opening. Impurities are introduced into the body of the silicon plug. After activation, the surface of the silicon plug is then implanted with ions of a different dopant impurity to produce a surface layer having a dopant concentration higher than that of dopant impurities included in the body of the silicon plug. On the surfaces of the interlevel insulating layer and the surface layer of high concentration, a polycrystalline silicon layer is formed, and doped to form an interconnection layer. At the junction of said doped polysilicon interconnection layer and said silicon plug a heavily doped pn tunneling junction, p ++ n ++ , is formed. In the above manufacturing method, the silicon plug is formed using an etch-back technique, so that the surfaces of the silicon plug and the interlevel insulating layer are substantially planar. The foregoing and other objects, features, aspects and advantages of the present invention will become apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings. In the accompanying drawings: Fig. 1 is a sectional structural view of a conventional SRAM cell; Fig. 2 is a plan structural view showing a plan structure of a lower portion of the memory cell of Fig.1; Fig. 3 is a plan structural view showing a plan structure of an upper portion of the memory cell of Fig. 1; Fig. 4 is an equivalent circuit diagram of the memory cell of Fig.1; Fig. 5 is a sectional structural view at a stage in the manufacture of the memory cell of Fig. 1; Fig. 6 is a sectional structural view of a memory cell of an SRAM in accordance with a preferred embodiment of the present invention; and Figs. 7 through 14 are sectional structural views showing manufacturing steps of the memory cell of the SRAM shown in Fig. 6. A preferred embodiment of the present invention will be described. Fig. 6 is a sectional structural view of a memory cell of an SRAM according to this embodiment. This embodiment is characterised in that an n ++ impurity layer 120 of a high concentration is formed in a junction portion of silicon plug 15 and interconnection layer 8a. A function of high concentration n ++ impurity layer 120 will be described. If a p type impurity layer is joined to an n type impurity layer having a normal concentration, a pn junction is produced. When current is supplied to the pn junction, a voltage drop of about 0.8V in a forward biased state, or a voltage drop of about 10V in a reverse biased state is caused. Therefore, when silicon plug 15 is directly connected to interconnection layer 8a, a voltage drop described above occurs and a sufficient voltage cannot be supplied to p channel MOS load transistor 14 through interconnection layer 8a. However, if an n type impurity layer having a very high concentration, as n ++ impurity layer 120 of a high concentration, is joined to interconnection layer 8a of a p type impurity layer similarly having a high concentration, a p ++ n ++ junction is formed. If a voltage is applied to the pn junction of a high concentration, for example, 10 20 /cm 3 or more, a tunnel current based on quantum mechanics flows. The tunnel current prevents a large voltage drop. Therefore, voltage can be sufficiently applied to the p channel MOS load transistor through interconnection layer 8a. N ++ impurity layer 120 of a high concentration is formed by an ion implantation method, as described below. Steps of manufacturing the memory cell of the SRAM shown in Fig. 6 will be described. Referring to Fig. 7, p type impurity is implanted in a main surface of a silicon substrate 1 using, for example, an ion implantation method. Subsequently, implanted p type impurity is diffused to the depth of about 2 - 3µm from the main surface of substrate 1 by heat treatment to form a p well 2. A field oxide film 4 and p + isolation layer 3 are formed on a prescribed region of a surface of p well 2 for isolation. Oxide films 5 of 12nm - 15nm thickness are formed on the surface of p well 2 using, for example, a thermal oxidation method. Oxide films 5 form gate oxide films 5,5 of MOS transistors 20a, 22b. A polycide film formed of polycrystalline silicon 6a and refractory metal silicide 6b formed thereon is deposited on the surface of oxide films 5. The polycide film is patterned to a prescribed shape using a photolithography method and an etching method to form gate electrodes 6, 6 of MOS transistors 20a, 22b. N type impurity ions of a dose of 4x10 15 ions/cm 2 are implanted into p well 2 by an ion implantation method using the patterned gate electrodes 6 as masks. Subsequently, heat treatment is performed to activate impurity ions implanted into p well 2. Thus, n + source/drain regions 7 of four MOS transistors 20a, 20b, 22a, 22b are formed. By following the above steps, n channel MOS drive transistors 20a, 20b and n channel MOS transfer transistors 22a, 22b are formed. Subsequently, a BPSG (BoroPhospho Silicate Glass) film is deposited on the whole surface of silicon substrate 1 using, for example, an atmospheric pressure CVD (Chemical Vapour Deposition) method. The BPSG is softened and reflowed by heat treatment, so that the surface of the BPSG film is planarized. In this step, an interlevel insulating layer 9 having a planarized surface is formed. An opening 16 for direct contact is formed in interlevel insulating layer 9 using a photolithography method and an etching method. For the etching method to form opening 16, for example, a reactive ion etching method is used. Referring to Fig. 8, a polycrystalline silicon layer 15a not doped with impurity is formed on a surface of interlevel insulating layer 9 using LPCVD (Low Pressure Chemical Vapor Deposition) method. Polycrystalline silicon layer 15a is deposited so thick as to fill opening 16 completely and make a surface of itself substantially flat in an upper portion of opening 16. A thickness more than a half of a maximum diameter of opening 16 is required as a standard of a thickness of polycrystalline silicon layer 15a to fill opening 16 completely. Referring to Fig. 9, the polycrystalline silicon layer 15a is etched, leaving a portion of the polycrystalline silicon layer only within opening 16 using an etch back method. Isotropic etching is used for the etching. In isotropic etching, polycrystalline silicon layer 15a is isotropically etched on the surface of interlevel insulating layer 9, but in the upper portion of opening 16, it is etched flat. As a result, only in opening 16, polycrystalline silicon layer 15a remains defining thus a plug 15 of polycrystalline silicon. Referring to Fig. 10, a resist pattern 17a having an opening only in the upper portion of opening 16 is formed on the surface of interlevel insulating layer 9. Using resist pattern 17a as a mask, n type impurity ions 18a are implanted into silicon plug 15 to provide n type conductivity. The ion implantation is carried out using, for example, phosphorus (P) ions in a dose of 1.5 x 10 16 ions/cm 2 with implantation energy of 170 keV. In this case, it is important to set implantation energy high in order to implant phosphorus ions so deeply as to reach the central portion of silicon plug 15. Moreover, using phosphorus having a large diffusion coefficient in silicon for impurities in the ion implantation is also important. Phosphorus having a large diffusion coefficient diffuses uniformly in the whole silicon plug 15. Referring to Fig. 11, after resist pattern 17a is removed, the phosphorus ions introduced into silicon plug layer 15 are activated using, for example, a rapid thermal anneal (RTA) method to form an n + silicon plug 15. In the RTA method, heat treatment is carried out, for example, for thirty seconds at a temperature of 1100°C in nitrogen atmosphere using a lamp anneal device having a halogen lamp for a heat source. The reason to remove resist pattern 17a before carrying out the RTA method is that, since the main component of resist pattern 17a is organic substance, harmful substance in the organic substance should be prevented from diffusing in the semiconductor in the heat treatment of the RTA method. Referring to Fig. 12, a resist pattern 17b having the same pattern as resist pattern 17a formed in Fig.10 is formed on the surface of interlevel insulating layer 9. N type impurity ions 18b are implanted into the surface of n + silicon plug 15 using, for example, an ion implantation method. The ion implantation is carried out using arsenic in a dose of 3 x 10 15 ions/cm 2 with implantation energy of 10keV, and n ++ impurity layer 120 of a high concentration (1.5 x 10 21 /cm 3 ) is formed. N ++ impurity layer 120 of a high concentration is formed by implanting arsenic ions. Compared to, for example, phosphorus, arsenic has a smaller diffusion coefficient, so that it can be restrained from diffusing deeply into silicon plug 15 by the influence of heat treatment in the subsequent steps. Implantation energy of arsenic ions 18b is set low to form n ++ impurity layer 120 in a shallow region, that is, at the depth of about 30-50nm. Heat treatment is not carried out after implantation of arsenic ions 18b in order to suppress the diffusion of n ++ impurity layer 120 of a high concentration. Referring to Fig. 13, a polycrystalline silicon layer 8 to which no impurities are introduced is deposited in a thickness of about 100 nm using an LPCVD method on the surfaces of interlevel insulating layer 9 and n ++ impurity layer 120 of a high concentration. Then, p type impurity ions 19 are implanted into polycrystalline silicon layer 8 in a dose of about 1 x 10 16 ions/cm 2 , and the p type impurity ions are activated in heat treatment. The concentration of the p type impurities introduced into polycrystalline silicon layer 8 is high (1 x 10 21 /cm 3 ). This is because a pn junction of high concentration (i.e. p ++ n ++ ) is to be formed at the junction of n ++ impurity layer 120, which has a high concentration, and polycrystalline silicon layer 8. Referring to Fig.14, polycrystalline silicon layer 8 of p type is patterned using a photolithography method and an etching method. A gate electrode 8b of p channel MOS thin film transistor 21b and interconnection layer 8a are formed in this step. A gate oxide film 13 of a thickness of about 20nm is deposited on the whole surface of interlevel insulating layer 9 using, for example, the LPCVD method. One portion of gate oxide film 13 located above opening 16 is opened. A thin polycrystalline silicon layer is formed with a thickness of about 10nm on the whole surface of gate oxide film 13 using, for example, the LPCVD method, and p + source/drain regions 12a, 12c and a channel region 12b of a p channel MOS thin film load transistor 21b are patterned using a photolithography method and an etching method. A resist is formed on regions of the polycrystalline silicon layer which are to be channel regions of p channel MOS thin film load transistors 21a, 21b. P type impurity ion is ion-implanted into the polycrystalline silicon layer in a dose of about 1x10 15 ions/cm 2 using the resist as a mask, so that p + source/drain regions 12a, 12c of p channel MOS thin film load transistors 21a, 21b are formed. The memory cell shown in Fig. 6 is thus completed by following the above described steps. Thus, in the direct contact structure of a semiconductor device in accordance with the present invention, a silicon plug is embedded within a contact hole and an upper interconnection layer is formed on a planarised layer, so that patterning precision of the interconnection layer using a photolithography method is improved and reliability of interconnection is enhanced. By producing a high dopant concentration pn junction (p ++ n ++ ) between the interconnection layer and the silicon plug having different types of conductivity, effective electrical connection is assured. Furthermore, since the silicon plug can be formed using a known CVD method and an etch back method, complicated manufacturing steps are not needed. Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the scope of the present invention being limited only by the terms of the appended claims.

Claims: A stacked type semiconductor device having first and second MOS transistors (22b,21b) of complementary channel conductivity type at respective different levels separated by an interlevel insulation layer (9), in which a doped region (7) of one conductivity type of the first MOS transistor (22b) is interconnected to a doped region (12a) of opposite conductivity type of the second MOS transistor (21b) by a direct contact structure (8a,15) formed of a doped polysilicon interconnection layer (8a) of said opposite conductivity type provided on said interlevel insulation layer (9) and being in direct contact with said doped region (12a) of said second MOS transistor (21b) and of a conductive plug (15) of doped polysilicon of said one conductivity type extending through said interlevel insulation layer (9) and being in direct contact with said doped region (7) of said first MOS transistor (22b), wherein a heavily doped pn tunnelling junction, p ++ n ++ , is formed at the junction of said doped polysilicon interconnection layer (8a) and said conductive plug (15) of doped polysilicon, said conductive plug (15) having two different dopant impurities therein, a first dopant impurity dispersed throughout its body (15) and a second dopant impurity localised in a surface layer (120) thereof, providing a higher concentration of dopant ions than in the body thereof, at said junction. A stacked type semiconductor device as claimed in claim 1 wherein said first dopant impurity is phosphorus and said second dopant impurity is arsenic. A method of manufacturing the stacked type semiconductor device of claim 1 comprising the following steps: providing a substrate (1) having said first MOS transistor (22b) defined in a first silicon layer (2) and having said interlevel insulation layer (9) provided thereon; forming an opening (16) in said interlevel insulation layer (9) to expose said region (7) of said one conductivity type of said first MOS transistor (22b); forming a second silicon layer (15a) on the surface of said interlevel insulation layer (9) and within said opening (16); etching-back said second silicon layer (15a) to remove that portion thereof on the surface of said interlevel insulation layer (9) to leave a plug portion (15) thereof remaining within said opening (16); producing a first mask layer (17a) on the surface of said interlevel insulation layer (9) with an opening exposing said plug portion (15); implanting ions of a first dopant impurity of said one conductivity type into the body of said plug portion (15); removing said first mask layer (17a); diffusing the ions of said first dopant impurity throughout the body of said plug portion (15) and activating said ions to produce said conductive plug (15); producing a second mask layer (17b) on the surface of said interlevel insulation layer (9) with an opening exposing said conductive plug (15); implanting ions of a second dopant impurity of said one conductivity type into the surface of said conductive plug (15) to produce said layer (120) of higher concentration of dopant ions thereat; depositing a third silicon layer (8) on the surface of said interlevel insulation layer (9) and on the surface of said conductive plug (120,15); implanting dopant impurity ions of said opposite conductivity type into said third silicon layer (8) and activating said ions by thermal treatment to produce thus said doped polysilicon interconnection layer (8a) and the heavily doped pn tunnelling junction, p ++ n ++ , at the junction thereof with said conductive plug (120,15); and producing the second MOS transistor (21b) of complementary channel conductivity type with said doped region (12a) of said opposite conductivity type in contact with said doped polysilicon interconnection layer (8a). A method as claimed in claim 3 wherein said first dopant impurity is phosphorus and said second dopant impurity is arsenic.

Inventors: SAKAMOTO OSAMU, SAKAMOTO, OSAMU, Sakamoto, Osamu, c/o Mitsubishi Denki K.K.
Applicants: MITSUBISHI ELECTRIC CORP, MITSUBISHI DENKI KABUSHIKI KAISHA
Application year: 1992
Main classification: H01L27
IPC codes: H01L23, H01L21, H01L27