Process for producing an optical fiber coupler

Abstract: The present invention relates to a process for producing an optical fiber coupler from a plurality of identical optical fibers comprising the steps of pre-treating at least one but not all of said optical fibers, bringing all said optical fibers into intimate contact with one another such that each pre-treated fiber contacts the other fibers, heating said optical fibers to fuse them together to form a unitary portion and drawing said unitary portion to form a coupling portion. In order to determine the branching ratio of the optical fiber coupler, it is important to carefully adjust the diameter of the core of the bare optical fibers. According to the invention, this is accomplished by said pre-treating step including a step of subjecting said at least one optical fiber to a heat treatment for a predetermined time so that the index profile of said at least one optical fiber is changed, resulting in a modified effective core diameter.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention: The present invention relates to a process for producing an optical fiber coupler according to the preamble of claim 1. 2. Brief Description of the Prior Art: An optical fiber coupler is an optical component that permits light to be branched or coupled between a plurality of optical fibers. Optical fiber couplers are known to be produced by either a melt drawing process or a polishing process. The melt drawing process is said to be best suited for the production of couplers of single-mode fibers (see "Recent Techniques on Optical Fiber Couplers" in Optronics, No. 5, p. 125, 1988). This process starts with stripping part of the coating from a plurality of optical fibers, heating them to fuse the stripped fibers together, forming a bundle by twisting the fibers or arranging them parallel to one another, drawing the bundle under heating until its characteristics such as branching ratio attain predetermined values, and forming a coupling portion. One of the important applications of optical fiber couplers is in branching of optical communication lines. In optical communications, light emitted at a plurality of wavelengths (e.g., 1.31 µm and 1.55 µm) is transmitted along each line. Thus, it is also desirable for optical fiber couplers to have constant branching characteristics over a broad wavelength range including emission wavelengths such as 1.31 µm and 1.55 µm. However, optical fiber couplers produced by the melt drawing process have the disadvantage that their branching ratio is largely wavelength dependent. It has been proposed that this problem be resolved by melt drawing optical fibers having different outside diameters on cladding (see Takeuchi et al., "Broad Wavelength Range Optical Fiber Couplers 1" in C-207 of the Preprint for 1989 Autumn National Conference of the Institute of Electronics, Information and Communication Engineers) or by melt drawing optical fibers having different mode field diameters (see "Broad Wavelength Range Optical Fiber Couplers 2" in C-208 of the same preprint). However, in order to produce optical fiber couplers of a predetermined branching ratio by these prior art methods, it has been necessary to use a plurality of optical fibers having different structures. Hence, it has been difficult to produce a desired optical fiber coupler using common commercially available single-mode optical fibers and this had made it necessary to use optical fibers of special structures. An alternative process is determined in U.S. Patent No. 4,798,438, which shows the features according to the preamble of claim 1. This process uses two optical fibers of identical structure, one of which is drawn preliminarily to a smaller diameter. The process is shown schematically in FIGURE 4, in which numeral 21 refers to an optical fiber, 22a and 22b to a clamper, and 23 to a burner. First, the coating of the optical fiber 21 is partly stripped off. Thereafter, with both ends of the bare portion of the fiber being clamped by the clampers 22a and 22b, tension is applied to the fiber so that it is pulled in opposite directions indicated by arrows 61 and 62 in FIGURE 4, whereby the bare portion is drawn as it is heated with the burner 23. In this process, the diameter of the preliminarily drawn bare portion determines the branching ratio of the optical fiber coupler to be produced and, hence, it is important to draw the bare portion of the fiber with good control and high repeatability. However, the preliminary drawing step involves so many variables in connection with the draw speed, draw length, etc. that it is difficult to attain identically drawn diameters with separate fibers. SUMMARY OF THE INVENTION The present invention was developed under these circumstances and has as an object to provide a process that is capable of producing a wide-band optical fiber coupler using optical fibers having identical structure, said process in particular being capable of producing a wide-band optical fiber coupler with high repeatability. This object is solved by a process comprising the features contained in claim 1. Advantageous embodiments of the invention are defined in the dependent claims. BRIEF DESCRIPTION OF THE DRAWINGS Other objects, features, and characteristics of the present invention, as well as the methods of operation and the function of the related elements of structure, will become apparent upon consideration of the following description and the appended claims with reference to the accompanying drawings, all of which form a part of this specification. In the drawings, like reference numerals designate corresponding parts of the present invention. FIGURE 1 is a flow chart illustrating an example of the process for producing an optical fiber coupler in accordance with the present invention; FIGURES 2(A) and 2(B) are sketches showing the refractive index profile of an optical fiber; FIGURE 3 is a graph depicting the branching ratio as a function of wavelength for a sample of an optical fiber coupler prepared by the process of the present invention; FIGURE 4 is a diagram depicting the step of preliminary drawing in a conventional process for producing an optical fiber coupler; DETAILED DESCRIPTION OF THE PRESENTLY PREFERRED EXEMPLARY EMBODIMENTS The process of the present invention for producing an optical fiber coupler includes preliminary heat treatment for a predetermined time of part of the optical fibers before a plurality of optical fibers are fused together into a unitary portion. To provide the core and the cladding of an optical fiber with a refractive index profile as shown in Fig 2(A), the core forming glass is doped with an element such as Ge or P to provide a higher index, or the cladding glass is doped with an element such as F or B to provide a lower index. If an optical fiber doped in either the core or the cladding or both is heated at elevated temperature, the dopants will diffuse and the index profile changes as shown in FIGURE 2(B), causing a substantial change in the core diameter. Thus, the same optical fiber can produce optical fibers with substantial differences in structure depending upon whether it is given a heat treatment or not. Therefore, if heat-treated optical fibers are combined with non heat-treated optical fibers, followed by melt drawing to form a coupling portion, an optical fiber coupler having a substantially constant branching ratio over a broad wavelength range can be produced. Further, the index profile shown in FIGURE 2(B) can be varied by adjusting the time or temperature for heating optical fibers. Hence, it is possible to control the branching ratio, which can be set at desired values without using a number of optical fibers with different core or cladding diameters. Example 1 FIGURE 1 is a flow chart illustrating an example of the process for producing an optical fiber coupler in accordance with the present invention. In step 1, at least one of the optical fibers to be used is partially stripped of its coating. Then, in step 2, the bare portion of the stripped optical fiber, or fibers, is heated for a predetermined time. In step 3, the other optical fibers which have not been heat-treated are stripped of the coating. In step 4, the bare portions of the optical fibers are heated as they are brought into intimate contact, thereby forming a unitary portion. The process goes to step 5, in which the unitary portion is drawn under heating until a predetermine branching ratio is attained. In step 6, the coupling portion of an optical fiber is formed. If desired, steps 4 and 5 can be performed simultaneously. A sample of an optical fiber coupler was prepared for communications at a wavelength of 1.3 µm using two common single-mode optical fibers (cladding diameter 125 µm; core diameter 9 µm). A propane/oxygen flame was used as a source for heating the optical fibers. First, one of the two optical fibers was stripped of the coating over a length of 40 mm and, thereafter, the bare portion of the fiber was heated for 1 minute with propane and oxygen being supplied at flow rates of 70 cc and 160 cc per minute, respectively. Next, the non heat-treated optical fiber was similarly stripped of the coating and the bare portions of the two optical fibers were heated for 30 seconds to fuse the fibers together as they were brought into intimate contact. In this step, propane and oxygen were supplied at flow rates of 40 cc and 80 cc per minute, respectively. Subsequently, the unitary portion was drawn by 8.5 mm on either side under heating to prepare an optical fiber coupler. For heating the unitary portion, propane and oxygen were supplied at flow rates of 40 cc and 90 cc per minute, respectively. The thus prepared optical fiber coupler had a branching ratio versus wavelength characteristic as shown in FIGURE 3, from which one can see that the coupler exhibited stable branching ratios of 50± 5% over a broad wavelength range of from 1.2 µm to 1.7 µm. As is clear from the foregoing description, the present invention offers the advantage that an optical fiber coupler having stable branching ratios over a broad wavelength range can be produced with high repeatability without using optical fibers of special structures but using optical fibers of identical structure.

Claims: A process for producing an optical fiber coupler from a plurality of identical optical fibers (21), comprising the steps of: pretreating at least one, but not all, of said optical fibers (21), bringing all said optical fibers (21) into intimate contact with one another such that each pretreated fiber contacts the other fibers; heating (44) all said optical fibers (21) to fuse them together to form a unitary portion; and drawing (45) said unitary portion to form a coupling portion; characterized in that said pretreating step comprises a step (2) of subjecting said at least one optical fiber to a heat treatment for a predetermined time so that the index profile of said at least one optical fiber is changed by heat diffusion. A process as claimed in claim 1, further comprising stripping cladding (1, 41) from said at least one optical fiber prior to said heat treatment. A process as claimed in claim 1, wherein cladding is removed from all of said optical fibers prior to said step of bringing said fibers into intimate contact.

Inventors: ARIMOTO KAZUHIKO, HATTORI TOMOYUKI, OKAWA YOSHIHARU, SUGANUMA HIROSHI, TAKIMOTO HIROAKI, YOKOTA HIROSHI, ARIMOTO, KAZUHIKO, HATTORI, TOMOYUKI, OKAWA, YOSHIHARU, SUGANUMA, HIROSHI, TAKIMOTO, HIROAKI, YOKOTA, HIROSHI, Arimoto, Kazuhiko, Sumiden Opcom Ltd., HATTORI, TOMOYUKI, YOKOHAMA WORKS OF SUMITOMO, Okawa, Yoshiharu, Yokohama Works of Sumitomo, SUGANUMA, HIROSHI, YOKOHAMA WORKS OF SUMITOMO, TAKIMOTO, HIROAKI, YOKOHAMA WORKS OF SUMITOMO, Yokota, Hiroshi, Yokohama Works of Sumitomo
Applicants: SUMIDEN OPCOM LTD, SUMITOMO ELECTRIC INDUSTRIES, SUMIDEN OPCOM, LTD., SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1992
Main classification: G02B6
IPC codes: G02B6