Integrated type solar battery

Abstract: An integrated type solar battery comprises a plurality of solar batteries serially connected. An upper electrode of one of adjacent solar batteries and a lower electrode of the other solar battery are connected via a lead wire. A groove portion of a boundary of the adjacent solar batteries is filled with an insulative material to a thickness enough to cover edge portions of the adjacent solar batteries. A conductive material is arranged so as to connect an upper portion of the insulative material and the upper electrode of one of the adjacent solar batteries. The lead wire is arranged over the insulative material along the groove portion of the boundary of the adjacent solar batteries so as to be connected to the conductive material. The lead wire is connected to the lower electrode of the other solar battery.

Description: BACKGROUND OF THE INVENTION Field of the Invention The invention ralates to a solar battery which is used in various kinds of electronic apparatuses and an electric power and, more particularly, to an integrated type solar battery in which a plurality of solar batteries are serially connected. The invention further relates to an integrated type solar battery using a thin film semiconductor. Related Background Art Generally, in the case of using a solar battery as a power source, a practical output voltage is not derived when only a single solar battery element is used. Therefore, a plurality of solar battery elements are serially connected and used. The serial connection of the solar battery is a common subject irrespective of the kind of semiconductor material of the solar battery. For instance, in a solar battery using monocrystalline silicon or polycrystalline silicon as a semiconductor layer, as shown in Fig. 6, adjacent solar batteries 601 and 602 are serially connected by connecting a collecting electrode 603 of one of the solar batteries 601 and 602 and the back surface of a wafer of the other solar battery by lead wires 604. According to the above method, however, there is a problem such that an output is lost by the shadows of the lead wires which are connected to the collecting electrode. On the other hand, since the lead wires are connected to the back surface of the wafer and the front and back surfaces of the wafer are filled with a resin, there are also problems such that the assembling steps are complicated and the manufacturing costs are high. As a solar battery using a conductive substrate and also using an amorphous material as a semiconductor layer, there is a solar battery in which a plurality of solar batteries are serially connected by using lead wires 705 as shown in Fig. 7. That is, for instance, a collecting electrode 703 of one (e.g., 701) of adjacent solar batteries 701 and 702 is connected to an edge portion 707 of the substrate of the other solar battery (e.g., 702) by the lead wires 705. In this case, however, there is also a problem such that the output is lost by the shadows of the lead wires 705. There is also a fear such that edge portions 708 and 709 of the conductive substrate are short-circuited or the substrate edge portions 708 and 709 and the lead wires 705 are short-circuited. On the other hand, in a solar battery formed on an insulative substrate made of glass or the like by using an amorphous semiconductor material, there is used a method of serially connecting a plurality of solar batteries on an integrated substrate without using any lead wire. As shown in Fig. 8, there is a method whereby in boundary portions of solar battery elements which are obtained by dividing a solar battery into a plurality of portions on an integrated substrate 801, an upper electrode 805 of one of the solar battery elements is connected to a lower electrode 804 of the other solar battery element, thereby serially connecting the solar battery elements. According to this method, an electric power is not lost by the shadows of lead wires and by optimizing a width of solar battery element between the connecting portions, an electric power loss due to resistances of transparent electrodes 802 and 805 and a reduction of the light receiving area by the connecting portions can be decreased. According to the above method, however, since all of lower electrodes 805 and 807, semiconductor layers 803 and 806, and upper electrodes 802 and 805 must be individually patterned, there are problems such that the number of steps is large and the manufacturing costs rise. On the other hand, to increase the light receiving area by narrowing a width of connecting portion, a line width of patterning is narrowed. Therefore, there are problems such that a positioning accuracy of the patterning must be raised and a manufacturing apparatus becomes expensive. Further, according to the patterning method, there are problems such that the insulation of the connecting portion is insufficient and a leak current easily occurs. For instance, the above method is disclosed in JP-B-62-5353. An integrated type solar battery according to the preamble of claim 1 is disclosed in JP-A-62 113 483. SUMMARY OF THE INVENTION It is an object of the present invention to provide an integrated type solar battery in which a plurality of solar batteries are serially connected and an upper electrode of one of the adjacent solar batteries is connected to a lower electrode of the other solar battery by a lead wire 110, wherein a groove portion 107 at a boundary of the adjacent solar batteries is filled with an insulative material 108 so as to cover the edge portions of the adjacent solar batteries, a conductive material 109 is arranged so as to connect the upper portion of the insulative material and the upper electrode of one of the adjacent solar batteries, the lead wire 110 is arranged on the insulative material 108 along the groove portion 107 of the boundary of the adjacent solar batteries so as to be connected to the conductive material, and the lead wire is connected to the lower electrode of the other solar battery, so that a loss of electric power by the shadows of the lead wires doesn't occur, a fear of short-circuit is very small, a disconnection of the conductive material can prevented, and the integrated type solar battery can be manufactured by low costs. This object is achieved with an integrated type solar battery as defined in claim 1. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is an explanatory diagram showing an example of an integrated type solar battery according to the invention and corresponds to an enlarged diagram of the portion surrounded by a broken line in Fig. 2; Fig. 2 is an external view of an example of the integrated type solar battery according to the invention; Fig. 3 is a cross sectional view of another example of an integrated type solar battery according to the invention; Fig. 4 is an explanatory diagram of a still another example of an integrated type solar battery according to the invention and corresponds to an enlarged diagram of the portion surrounded by a broken line in Fig. 5; Fig. 5 is an external view of still another example of an integrated type solar battery according to the invention; Fig. 6 is an explanatory diagram of a conventional integrated type solar battery; Fig. 7 is an explanatory diagram showing another example of a conventional integrated type solar battery; and Fig. 8 is an explanatory diagram showing further another example of a conventional integrated type solar battery. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS A construction of an integrated type solar battery according to the invention will now be described with reference to the drawings. Figs. 1 and 2 are explanatory diagrams showing an example of the integrated type solar battery of the invention. In the diagrams, a plurality of solar batteries 105 and 106 are serially connected. An upper electrode 103 of one (105) of the adjacent solar batteries 105 and 106 is connected to a lower electrode 111 of the other solar battery 106 by a lead wire 110. A groove portion 107 of a boundary of the adjacent solar batteries is filled with an insulative material 108 so as to cover the edge portions of the adjacent solar batteries. A conductive material (collecting electrode) 109 is arranged so as to connect an upper portion of the insulative material 108 and the upper electrode 103 of the solar battery 105. The lead wire 110 is arranged on the insulative material 108 along the groove portion 107 of the boundary so as to connect to the conductive material 109. Edge portions 201 and 202 of the lead wire are connected to exposed portions 203 and 204 of the lower electrode of the other solar battery. Lower electrodes 101 and 111 are formed on conductive solar battery substrates 101' and 111', respectively. Those conductive substrates construct parts of the lower electrodes. Reference numeral 104 denotes a supporting member. At least an upper surface of the supporting member 104 has an insulative property. According to the invention, since the lead wire 110 to connect the adjacent solar batteries 105 and 106 doesn't exist over a semiconductor layer 102, an electric power is not lost due to the shadow of the lead wire 110 and a photoelectric converting efficiency of the integrated type solar battery can be improved. Since the groove portion 107 of the boundary is filled with the insulative material 108, a fear such that portions between the lead wire 110 and the lower electrodes 101 and 111 or portions between the lead wire 110 and the solar batteries 105 and 106 are short-circuited is eliminated and the reliability is improved. The lead wire 110 and the conductive material 109 of the collecting electrode are connected at a position over the insulative material 108 instead of the solar batteries, so that there is no fear of damage to the solar batteries due to the heat which is generated in the connecting operation or the like. In addition, there is no need to connect the lead wire on the back surface and to individually pattern the lower electrodes, semiconductor layer, and upper electrode. The solar battery can be manufactured by simple processing steps. Consequently, the integrated type solar battery can be manufactured by low costs. By properly selecting a thickness of insulative material to fill the groove portion of the boundary, a level difference in the edge portion of the solar battery between the upper electrode and the upper surface of the insulative material can be reduced. A disconnection of the conductive material 109 can be prevented while keeping the insulation between the lead wire and the edge portion of the solar battery. Each section of the construction of the invention will now be described further in detail hereinbelow. As an integrated type solar battery of the invention, it is possible to use a solar battery of the type in which solar batteries whose substrates 101' and 111' are also divided are serially connected as shown in Fig. 1 or a solar battery of the type in which a solar battery formed on the integrated substrate is divided into a plurality of portions and those plurality of portions are serially connected as shown in Figs. 3 and 4. In the case of dividing the solar battery formed on an integrated substrate 301 into a plurality of portions, at least a lower electrode 303 and an upper electrode 306 must be separated. However, a semiconductor layer 305 is not necessarily separated so long as a conductivity in the lateral direction has an enough high resistance. In the case of dividing the substrate, a proper material can be used as a substrate material of the integrated type solar battery of the invention. However, in the case of using an integrated substrate, an insulative substrate or a substrate which is formed by coating an insulative layer onto a conductive substrate is used. As an insulative substrate, an inorganic insulative material such as non-alkali glass or the like can be also used or a heat resistant synthetic resin such as polyimide, polyethylene terephthalate, or the like can be also used. A metal such as stainless steel, Al, Fe, etc. can be used as a material of the conductive substrate. As an insulative layer which is coated onto the conductive substrate, a thin film of an inorganic material such as SiO 2 , Si 3 N 4 , Al 2 O 3 , etc. is formed or the above-mentioned synthetic resin may be also coated. As a semiconductor layer to generate a photo electromotive force in the invention, there is preferably used an amorphous semiconductor such as amorphous silicon (hereinafter, abbreviated to a-Si), amorphous silicon alloy, or the like, polycrystalline silicon, monocrystalline silicon, a semiconductor of the II-VI groups such as CdS, CdTe, or the like, or a semiconductor such as CuInSe 2 or the like. The semiconductor layer is valence electron controlled to the p type and n type and a pn junction, a pin junction, pin/pin double cells, triple cells, or the like is formed. In the invention, the upper electrode is formed on the incident side of the solar light for the semiconductor layer. Therefore, what is called a transparent conductive film having a high transmittance of the light such as ITO, In 2 O 3 , SnO 2 , TiO 2 , ZnO, etc. is preferably used. In the invention, the lower electrode is formed on the side opposite to the incident side of the solar light for the semiconductor layer. A metal of Al, Ag, Cr, Ni, Au, Pb, Sn, Zn, Mg, Cu, Fe, W, Mo, etc. or an alloy such as a stainless steel or the like is preferably used as a lower electrode. When a conductive substrate is used, the substrate can also commonly function as a lower electrode. It is also possible to construct the lower electrode by two or more layers by forming a conductive film of ZnO or the like between such a lower electrode material and the semiconductor layer. In the invention, as an insulative material to fill the groove portion of the boundary of the adjacent solar batteries, an insulative material of an inorganic material such as SiO 2 , Si 3 N 4 , Al 2 O 3 , or the like may be also used. Or proper one of the various synthetic resins such as epoxy resin, polyamide, polyester, silicone resin, and the like can be also selected and used. In the invention, the insulative material covers the edge portions of the adjacent solar batteries. When a thickness of insulative material is too thin, there is a fear such that the portion between the lead wire or the conductive material and the edge portions of the solar batteries is short-circuited. When the thickness is too thick, a level difference between the insulative material and the upper electrode of the solar battery is large, so that there is a fear such that the conductive material to connect the lead wire and the upper electrode is disconnected. Therefore, it is desirable to form the insulative material having a thickness within a range from 0.2 µm to 1 mm when it is measured from the upper surface of the upper electrode. More preferably, it is desirable to set a thickness within a range from 0.5 µm to 0.5 mm, optimally, 1 µm to 100 µm. In the invention, as a conductive material to connect the lead wire and the upper electrode, it is possible to use a conductive resin using a metal such as Al, Ag, Cr, Ni, Au, Pb, Sn, Zn, Mg, Cu, Fe, W, Mo, etc., an alloy such as a solder or the like, or a powder metal such as an Ag paste or the like. An arrangement shape of the conductive material can be set into a comb shape as shown in Fig. 2. In this case, a material having a resistance lower than that of the upper electrode is used as a conductive material. The conductive material also commonly functions as a collecting electrode of the solar battery. When a width of groove portion 406 of the boundary of the divided portions of the solar batteries which are serially connected is sufficiently narrow and a width of solar battery between the connecting portions is narrow and a loss of electric power due to the resistance of the upper electrode is sufficiently small, it is also possible to arrange the lead wire in parallel with the groove of the boundary as shown in Fig. 4. A suitable value of the thickness of conductive material also differs because the resistance value differs in accordance with the material. However, when the thickness is too thin, there is a fear of disconnection. When it is too thick, the line width must be also made thick and the light receiving area is reduced. Therefore, it is desirable to set the thickness of conductive material to a value within a range from 0.2 µm to 2 mm, more preferably, 0.5 µm to 1 mm, and optimally, 1 µm to 500 µm. In the invention, the lead wire is arranged over the insulative material to fill the groove portion of the boundary of the adjacent solar batteries and is connected to the cnnductive material. One or both edges of the lead wire is/are connected to the lower electrode of the solar battery. Although the conductive material and the lead wire are connected at a position over the insulative material, a conductive resin using an alloy such as a solder or the like or a powder metal such as an Ag paste or the like is preferably used for such a connection. The lead wire and the lower electrode are connected in the exposed portion of the lower electrode in which the semiconductor layer of the solar battery and the upper electrode are not formed. As a connecting method, a welding method can be used or a conductive resin such as an alloy of a solder or the like or a powder metal can be used. As a material of the lead wire, it is possible to use a conductive resin using a metal such as Al, Ag, Cr, Ni, Au, Pb, Sn, Zn, Mg, Cu, Fe, W, Mo, etc., an alloy such as a solder or the like, or a powder metal such as an Ag paste or the like. To reduce the electric power loss, it is desirable to set a resistivity of the lead wire to a value which is equal to or less than 0.1 Ω·cm, more preferably, 0.05 Ω·cm or less, optimally, 0.01 Ω·cm or less. Although the invention has been shown and described with respect to the case of the serial connection, it is also possible to use a combination of both of the serial connection of the solar battery elements and the parallel connection of the solar battery elements. In this case, for instance, two or more solar batteries shown in Fig. 2 are arranged in a manner such that the same solar battery elements are located just beside on the extension line of the solar battery elements and the boundary portion of the solar batteries arranged just beside is filled with the insulative material and is electrically connected to the solar battery elements arranged just beside so as to pass over the insulative material through the lead wire. A manufacturing method of the integrated type solar battery of the invention will now be described. The solar battery is first divided into a plurality of portions. In the case of dividing from the substrates 101' and 111' as shown in Fig. 1, the solar battery is formed up to the upper electrode and, after that, it is cut into desired sizes. It is desirable to eliminate the upper electrode along the cutting line in this instance. The solar batteries can be also formed onto the substrates which have been cut into desired sizes. In the case of integrating the solar batteries onto the integrated substrate 301 as shown in Fig. 3, at least the lower electrode 303 and the upper electrode 306 among the lower electrode 303, semiconductor layer 305, and upper electrode 306 are linearly eliminated and the solar battery is divided into a plurality of solar batteries. When the semiconductor layer 305 has a high resistance and a leak current between adjacent solar batteries 307 and 308 can be ignored, it is not always necessary to eliminate the semiconductor layer 305 in the boundary portion. As a method of linearly eliminating the lower electrode 303, upper electrode 306, and semiconductor layer 305, it is possible to use any one of a method of linearly etching by using a mask, a method whereby an etching paste is linearly coated and an etching is performed, and a method of linearly eliminating them by irradiating an energy beam such as laser beam, electron beam, or the like. Or, it is also possible to use a method whereby portions to be eliminated are masked and a film is formed and no film is formed to the portions to be eliminated. A groove portion 309 of the boundary of the solar batteries which have been divided or cut into a plurality of portions is filled with an insulative material 310. In this instance, as an insulative material 310, a paste-like insulative material is coated by a dispenser or the like and is hardened, or a mask deposition is performed by a CVD method or the like, or after an insulative layer 302 was formed onto the whole surface, the portions other than the groove portion are eliminated by etching. After that, as shown in Fig. 1, the upper electrode 103 of one solar battery 105 and the upper portion of the insulative material when they are seen from the groove portion of the boundary are connected by the conductive material 109. At this time, it is preferable that the conductive material is formed into a desired pattern by a screen printing or the like or is formed by evaporation depositing a metal or the like into a desired pattern by using a mask or, after a conductive film was formed onto the whole surface, it is etched into a desired pattern. After, that, the lead wire 110 is arranged over the insulative material 108 to fill the groove portion 107 of the boundary of the solar battery and is connected to the conductive material 109 by using a conductive resin such as an Ag paste or the like or an alloy such as a solder or the like at a position over the insulative material. As shown in Fig. 2, one or both of the edge portions 201 and 202 of the lead wire 110 are connected to the lower electrodes 203 and 204 of the other solar battery. When connecting the edge portions 201 and 202 to the lower electrodes, in the exposed portions 203 and 204 of the lower electrodes in which the semiconductor layer and the upper electrode are not formed or eliminated, the lead wire 201 and the lower electrodes are connected by using a conductive resin such as an Ag paste or the like or an alloy such as a solder or the like or by welding. The adjacent solar batteries are serially connected by the above processing steps. After that, a surface protective layer, terminals to take out an electric power, and the like are formed, thereby completing an integrated type solar battery module. (Embodiment 1) The integrated type solar battery of the invention of Figs. 1 and 2 in which the solar battery substrate is cut out is manufactured by the following processing steps. The belt-shaped SUS substrate 101' having a thickness of 0.15 mm, a width of 32 cm, and a length of 300 m is cleaned and each layer is formed by a roll-to-roll method. First, an alloy of Al and Si having a thickness of 2000 Å (1 Å = 10 -10 m) is evaporation deposited by an RF sputtering method, a ZnO film having a thickness of 700 Å is evaporation deposited, and the lower electrode 101 is formed. An n type a-Si layer having a thickness of 200 Å, an i type a-Si layer having a thickness of 4500 Å, and a p type crystallite Si layer (hereinafter, abbreviated to a µc-Si layer) having a thickness of 80 Å are deposited by a plasma CVD method. An n type a-Si layer having a thickness of 180 Å, an i type a-Si layer having a thickness of 1000 Å, and a p type µc-Si layer having a thickness of 50 Å are deposited on them, thereby forming the semiconductor layer 102 of the pin/pin structure. An ITO film having a thickness of 700 Å is evaporation deposited by a resistance heating evaporation depositing method and the transparent upper electrode 103 is formed, thereby forming a 2-stacking type solar battery. After that, an etching paste is linearly coated and the upper electrode 103 is linealy etched and is cut into desired sizes along the etched lines up to a position of the substrate 101'. A plurality of cut-out solar batteries are fixed onto the supporting member 104 of the SUS whose surface is coated with EVA as shown in Fig. 1. After that, the groove portion 107 of the boundary of the adjacent solar batteries 105 and 106 is filled with the insulative material 108. As an insulative material, an epoxy resin is used and is linearly coated by a dispenser and is hardened. In this instance, the insulative material is coated so as to be higher than the upper surface of the upper electrode 103 by up to 30 µm, thereby coating the edge portions of the solar batteries 105 and 106. The conductive material 109 is formed by using an Ag paste by the screen printing so as to connect the upper portion of the insulative material 108 and the upper electrode 103 of one solar battery 105. The conductive material 109 also commonly functions as a collecting electrode of the solar battery. The lead wire 110 is fixed over the insulative material 108 along the groove portion 107 of the boundary and is connected to the conductive material 109 by the Ag paste. As shown in Fig. 2, both edge portions 201 and 202 of the lead wire 110 are connected to the exposed portions 203 and 204 of the lower electrode of the other solar battery by spot welding. As a lead wire, a Cu line having a rectangular cross sectional shape as shown in Fig. 1 is used. A plurality of solar batteries are serially connected as mentioned above. Lastly, a surface protective layer is formed by an EVA and tedler i.e., a trade name of Du Pont for (polyvinyl fluoride) and an electric power output terminal is attached, thereby completing an integrated type solar battery module. A photoelectric converting efficiency of an integrated type solar battery module having a size of 30 cm x 40 cm constructed by serially connecting twelve solar batteries was measured by a solar simulator simulating a light of 100 mW/cm 2 and AM (Air Mass) 1.5. AM 1.5 corresponds to a sunlight of incident angle 48°. Thus, the module converting efficiency was 8.1%. (Embodiment 2) The integrated type solar battery of the invention shown in Fig. 3 in which solar batteries which have been divided into a plurality of portions are serially connected onto the integrated substrate is manufactured by the following processing steps. Each layer is formed onto the belt-shaped SUS substrate 301 similar to that of the embodiment 1 by the roll-to-roll method. An SiO 2 film having a thickness of 3 µm is first deposited by a heat CVD method, thereby forming the insulative layer 302. Subsequently, a line-shaped mask is used and an Al film having a thickness of 4000 Å and an Ag film having a thickness of 200 Å are sequentially resistance heat-evaporation deposited in accordance with the above order. A ZnO film having a thickness of 1000 Å is formed by an RF sputtering, thereby forming the lower electrode 303 from which the portion 304 is linearly eliminated. Subsequently, an n type a-Si layer having a thickness of 200 Å, an i type a-SiGe layer having a thickness of 3000 Å, and a p type µc-Si layer having a thickness of 80 Å are deposited by the plasma CVD method. Further, the n type a-Si layer having a thickness of 180 Å, an i type a-Si layer having a thickness of 2000 Å, and a p type µc-Si layer having a thickness of 50 Å are deposited on them, thereby forming the semiconductor layer 305 of the pin/pin structure. An ITO film having a thickness of 700 Å is subsequently evaporation deposited by the resistance heating evaporation depositing method and the transparent upper electrode 306 is formed, thereby forming a 2-stacking type solar battery. After that, an etching paste is coated onto the upper portion of the line-shaped portion 304 which is not coated with the lower electrode and the ITO film in this portion is eliminated, thereby dividing into a plurality of solar batteries. Although the semiconductor layer 305 of the divided solar batteries 307 and 308 is continuous, since the semiconductor layer 305 has an enough higher resistance than that of the upper electrode or lower electrode, a leak current between the solar batteries 307 and 308 is at the level which can be ignored. In a manner similar to the embodiment 1, the groove portion 309 of the boundary of the solar batteries 307 and 308 is coated with polyester and filled with the insulative material 310. The upper portion of the insulative material and the upper electrode 306 of the solar battery 307 are connected by the conductive material 311. In the embodiment 1, however, since the solar battery is divided while including the substrates 101' and 111', a depth of groove portion 107 of the boundary is set to 0.15 mm, which is almost equal to a thickness of substrate. In the embodiment 2, a depth of groove portion 309 of the boundary is equal to merely about 0.6 µm in which film thicknesses of the lower electrode 303 and upper electrode 306 are added. Consequently, a thickness of insulative material to fill the groove is also thin. In a manner similar to that in the embodiment 1, the depth of boundary portion is higher than the upper surface of the upper electrode 306 by up to 30 µm. The conductive material 311 has a comb-like shape in a manner similar to the embodiment 1 and also commonly functions as a collecting electrode. A lead wire 312 is fixed onto the insulative material 310 along the groove portion 309 of the boundary of the solar battery and is connected to a conductive material 311 by an Ag paste. In a manner similar to Fig. 2, both edge portions 201 and 202 of the lead wire 312 are connected to the exposed portions 203 and 204 of the lower electrode of the other solar battery by soldering. A Cu line having a circular cross section as shown in Fig. 3 is used as a lead wire. By the above processing steps, the solar batteries divided into a plurality of portions are serially connected on the integrated substrate and a surface protective layer and an electric power output terminal are lastly formed in a manner similar to the embodiment 1, thereby completing an integrated type solar battery. A photoelectric converting efficiency of the integrated type solar battery module of a size of 30 cm x 40 cm which is constructed by serially connecting fourteen solar batteries was measured by the solar simulator of 100 mW/cm 2 of AM 1.5, so that the module efficiency was equal to 9.3 %. (Embodiment 3) An integrated type solar battery of the invention of Fig. 4 in which solar batteries which have been divided into a plurality of portions are serially connected on the integrated substrate is manufactured by the following processing steps. Each layer is formed onto a belt-shaped SUS substrate 401 by the roll-to-roll method in a manner similar to the embodiments 1 and 2. An Si 3 N 4 film having a thickness of 3 µm is first deposited by a thermal CVD method, thereby forming an insulative layer 402. An Mo film having a thickness of 1 µm is subsequently evaporation deposited as a lower electrode 403 by an electron beam. A CuInSe 2 film having a thickness of 2 µm is evaporation deposited and is heated after that. A CdS film having a thickness of 500 Å is subsequently evaporation deposited and heated thereby forming a semiconductor layer 404 having an n-CdS/p-type CIS (CuInSe 2 ) structure. A ZnO film having a thickness of 1 µm is formed by an RF sputtering, thereby forming a transparent upper electrode 405. A laser beam having a diameter of 50 µm is irradiated from a YAG laser having a wavelength of 1.06 µm and Q switching pulses and is scanned, thereby eliminating a lower electrode, a semiconductor layer, and an upper electrode of the portion 406 and dividing the solar battery formed on the integrated substrate into a plurality of portions 407 and 408. In a manner similar to the embodiments 1 and 2, the groove portion 406 of a boundary of the solar batteries 407 and 408 is coated with polyamide and filled with an insulative material 409. In this instance, a thickness of insulative material 409 from an upper surface of the upper electrode 405 is equal to up to 25 µm. An Ag paste is coated into a shape as shown in Fig. 4 by a screen printing so as to connect an upper portion of the insulative material 409 and an edge portion of one solar battery 407, thereby forming a conductive material 410. After that, over the insulative material 409, a lead wire 411 of Cu having a circular cross section is adhered to the conductive material 410 along the groove portion 406 by an Ag paste and is fixed as shown in Fig. 4. As shown in Fig. 5, in exposed portions 503 and 504 of the lower electrode in which the semiconductor layer and upper electrode of the other solar battery 408 are not formed, both edge portions 501 and 502 of the lead wire 411 are connected to the lower electrode by soldering as shown in Fig. 5. By the above processing steps, the solar batteries divided into a plurality of portions are serially connected on the integrated substrate. In a manner similar to the embodiments 1 and 2, a surface protective layer and an electric power output terminal are lastly formed, thereby completing an integrated type solar battery. A photoelectric converting efficiency of an integrated type solar battery module having a size of 30 cm x 40 cm constructed by serially connecting 35 solar batteries was measured by the solar simulator of 100 mW/cm 2 of AM 1.5, so that the module efficiency was equal to 8.9 %. (Embodiment 4) An integrated type solar battery of the invention in which solar batteries divided into a plurality of portions are serially connected on an integrated substrate was manufactured by the following processing steps. Each layer is formed onto a belt-shaped polyethylene terephthalate substrate having a width of 32 cm, a thickness of 0.25 mm, and a length of 100 m by a roll-to-roll method. An alloy of Al and Si having a thickness of 5000 Å is evaporation deposited by a resistance heating method, thereby forming the lower electrode. In this instance, the alloy is evaporation deposited by using a linear mask and a linear dividing groove is formed on the lower electrode. An n type a-Si layer having a thickness of 250 Å, an i type a-Si layer having a thickness of 4000 Å, and a p type µc-Si layer having a thickness of 50 Å are sequentially deposited by a plasma CVD method in accordance with this order, thereby forming a pin type semiconductor layer. Subsequently, an SnO 2 film having a thickness of 2000 Å is formed by a DC sputtering method, thereby forming a transparent upper electrode. After that, in a manner similar to the embodiment 2, as shown in Fig. 3, the upper electrode existing over the dividing groove of the lower electrode is eliminated by etching, thereby dividing the solar battery on the integrated substrate into a plurality of portions. In a manner similar to the embodiments 1 and 3, the groove portion of the boundary of the solar batteries is coated with a silicone resin and filled with an insulative material. An Ag paste is coated onto the groove portion in a manner similar to the embodiment 3. The upper electrode of one solar battery and the upper portion of the insulative material are connected by a conductive material. After that, in a manner similar to the embodiment 3, a lead wire of Al having a rectangular cross section is connected to the conductive material over the insulative material along the groove portion of the boundary by using an Ag paste. Both edges of the lead wire are connected to the exposed portion of the lower electrode of the other solar battery by an Ag paste. By the above processing steps, solar batteries divided into a plurality of portions on the integrated substrate of the insulative material are serially connected. In a manner similar to the embodiments 1 to 3, a surface protective layer and an electric power output terminal are lastly formed, thereby completing an integrated type solar battery. A photoelectric converting efficiency of an integrated type solar battery module having a size of 30 cm x 40 cm constructed by serially connecting 25 solar batteries was measured by the solar simulator of 100 mW/cm 2 of AM 1.5, so that the module efficiency was equal to 5.0 %. The following points were improved by the integrated type solar battery of the invention characterized in that the groove portion of the boundary of the adjacent solar batteries is filled with the insulative material so as to coat the edge portions of the adjacent solar batteries, the conductive material is arranged so as to connect the upper portion of the insulative material and the upper electrode of one of the adjacent solar batteries, the lead wire is arranged over the insulative material along the groove portion of the boundary of the adjacent solar batteries so as to be connected to the conductive material, and the edge portions of the lead wire are connected to the lower electrode of the other solar battery. First, since the lead wire is not located over the semiconductor layer but exists over the boundary line of the solar batteries which are not concerned with the power generation, an electric power loss by the shadow of the lead wire is eliminated and the module efficiency of the integrated type solar battery is improved. Since the boundary portion of the adjacent solar batteries is filled with the insulative material, a fear such taht the portion between the lead wire and the other solar battery is short-circuited is eliminated, a fear such that the portion between the adjacent solar batteries is short-circuited is eliminated, and the reliability is improved. Since the lead wire and the conductive material are connected over the insulative material instead of the solar battery, even when a heat is applied by soldering or the like, there is no fear of damage to the solar battery due to the heat such as diffusion of the upper electrode, short-circuit with the lower electrode, or damage to the semiconductor layer. By properly selecting a thickness of insulative material which fills the groove portion of the boundary, a level difference between the upper electrode and the upper surface of the insulative material in the edge portion of the solar battery is reduced, and a disconnection of the conductive material can be prevented while keeping the insulation between the lead wire and the solar battery edge portion. An integrated type solar battery comprises a plurality of solar batteries serially connected. An upper electrode of one of adjacent solar batteries and a lower electrode of the other solar battery are connected via a lead wire. A groove portion of a boundary of the adjacent solar batteries is filled with an insulative material to a thickness enough to cover edge portions of the adjacent solar batteries. A conductive material is arranged so as to connect an upper portion of the insulative material and the upper electrode of one of the adjacent solar batteries. The lead wire is arranged over the insulative material along the groove portion of the boundary of the adjacent solar batteries so as to be connected to the conductive material. The lead wire is connected to the lower electrode of the other solar battery.

Claims: An integrated type solar battery in which a plurality of solar batteries are serially connected wherein; an upper electrode (103; 306; 405) of one (105; 307; 407) of a pain of adjacent solar batteries (105, 106; 307, 308; 407, 408), said upper electrode being arranged on the light incidence side, and a lower electrode (111; 305; 403) of the other solar battery (106; 308; 408) are connected via a lead wire (110; 312; 411); and wherein a groove (107; 309; 406) along the boundary between said adjacent solar batteries is filled with an insulative material (108; 310; 409) to a thickness enough to cover edge portions of the adjacent solar batteries, characterised in that a conductive material (109; 311; 410) is arranged so as to connect an upper portion of the insulative material (108; 310; 409) and the upper electrode (103; 306; 405) of one of the adjacent solar batteries (105, 106; 307, 308; 407, 408), the lead wire (110; 312; 411) is arranged over the insulative material (108; 310; 409) and extends along the groove (107; 309; 406) along the boundary between the adjacent solar batteries (105, 106; 307, 308; 407, 408) so as to be connected to the conductive material (109; 311; 410). An integrated type solar battery according to claim 1, wherein said adjacent solar batteries (105, 106; 307, 308; 407, 408) are solar batteries divided on an integrated substrate (104; 301; 401). An integrated type solar battery according to claim 2, wherein the substrate (104; 301; 401) of the solar batteries is an insulative substrate or a substrate formed by coating an insulative layer on a conductive substrate. An integrated type solar battery according to any of claims 1 to 3, wherein the conductive material (109) to connect the lead wire (110) and the upper electrode (103) of one of the adjacent solar batteries (105, 106) also commonly functions as a collecting electrode of said one solar battery. An integrated type solar battery according to any one of claims 1 to 4, wherein amorphous semiconductor is used as a semiconductor layer (102; 305; 404) of the solar battery. An integrated type solar battery according to any one of claims 1 to 5, wherein the thickness of the insulating material (108; 310; 409) covering the edge portions is 0,2 µm to 1 mm. An integrated type solar battery according to any one of claims 1 to 6, wherein said insulating material (108; 310; 409) is made of SiO 2 , Si 3 N 4 , Al 2 O 3 , epoxy resin, polyamide, polyester or silicone resin. An integrated type solar battery according to any one of claims 1 to 7, wherein said conductive material (109, 311, 410) is made of a conductive paste. An integrated type solar battery according to any one of claims 1 to 8, wherein said upper electrode (103; 306; 405) is a transparent electrode. An integrated type solar battery according to any one of claims 1 to 9, wherein said lower electrode (111; 305; 403) of the other of the adjacent pair of solar batteries (105; 307; 407) is electrically connected to said lead wire (110, 312, 411) at both ends (201, 202 ; 501, 502) thereof.

Inventors: MATSUDA KOICHI C O CANON KABUS, MATSUYAMA JINSHO C O CANON KAB, MURAKAMI TSUTOMU C O CANON KAB, MATSUDA, KOICHI, C/O CANON KABUSHIKI KAISHA, MATSUYAMA, JINSHO, C/O CANON KABUSHIKI KAISHA, MURAKAMI, TSUTOMU, C/O CANON KABUSHIKI KAISHA
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1992
Main classification: H01L27
IPC codes: B22F3, B30B11, H01L31, H01L27