Polyvinyl chloride resin powder composition and production thereof

Abstract: Disclosed is a polyvinyl chloride resin powder composition containing (A) a granular polyvinyl chloride resin and (B) a fine granular vinyl chloride copolymer resin containing a copolymer composed of a vinyl chloride monomer and a carbonyloxy group-containing vinyl monomer, along with a stabilizer and a plasticizer. The composition is suitable for powder molding to produce covering materials of automotive interiors.

Description: The present invention relates to a polyvinyl chloride resin powder composition and also to a process for producing the same. The recent trend in the automotive interior covering materials for crash pads, armrests, headrests, console boxes, meter hoods, door trim, etc. is toward those which are not only light in weight but also soft to the touch and of quality appearance owing to embossed leather-like finish and stitch-like pattern. These covering materials are conventionally produced by the powder slush molding method which consists of contacting a powder composition with a heated mold, thereby causing particles to fuse together, and removing excess powder remaining unfused, said powder composition being formed by dry-blending polyvinyl chloride resin, plasticizer, stabilizer, pigment. The product from the powder molding is often backed with a polyurethane layer to be made into a covering material. The thus obtained covering material has the disadvantage of poor adhesion between the polyvinyl chloride resin layer and the polyurethane layer. In order to overcome the disadvantage, there has been proposed an improved polyvinyl chloride resin powder composition comprising the above-mentioned composition and a polypropylene glycol or polyether polyol (Japanese Patent Kokai No. 136542/1986). This composition is, however, not satisfactory because it does not adhere uniformly to the mold or the excess composition is not removed uniformly after fusing so that its so-called powder dropping property is poor. Thus, the resulting covering material fluctuates widely in thickness, and when a polyurethane layer is laminated to it, the surface of the laminate product is defectively uneven. With the foregoing in mind, the present inventors carried out a series of researches which led to the finding that a powder composition containing a fine granular vinyl chloride copolymer resin, which contains a specific copolymer composed of vinyl chloride monomer and carbonyloxy group-containing vinyl monomer, has the good property of powder dropping and gives a covering material having uniform thickness and good adhesion to a polyurethane layer. GB-A-576 110 discloses a polyvinyl chloride resin compound containing polyvinyl resin, plasticiser and a copolymer of vinyl chloride and vinyl acetate. Accordingly, the present invention provides a polyvinyl chloride resin powder composition containing (A) granular polyvinyl chloride resin, (B) fine granular vinyl chloride copolymer resin comprising copolymer of vinyl chloride monomer and carbonyloxy group-containing vinyl monomer according to Formula (1), below, along with (C) stabilizer and plasticizer. It also provides a method of producing the composition and a method of producing a covering material from the composition. Suitable granular polyvinyl chloride resins(A) for use in the present invention include, for example, vinyl chloride homo-polymer, copolymer of vinyl chloride with copolymerizable co-monomer(s) (e.g. ethylene, propylene or vinyl acetate) and vinyl chloride graft copolymer formable by grafting vinyl chloride to ethylene-vinyl acetate copolymer; this list is not limitative. A mixture comprising two or more (co)polymers may be used. The granular polyvinyl chloride resin (A) has a particle size of from 100 to 150 µm, and it may be produced, for example, by suspension polymerization or bulk polymerization. The fine granular vinyl chloride copolymer resin (B) for use in the present invention is one for coating the above-mentioned granular polyvinyl chloride resin (A), and it has a particle size of from 0.1 to 10 µm and may be produced, for example, by emulsion polymerization or micro-suspension polymerization. The component (B) is copolymer composed of vinyl chloride monomer and carbonyloxy group-containing vinyl monomer of the following formula (1), or a mixture comprising such copolymer with vinyl chloride homopolymer and/or copolymer of vinyl chloride with co-monomer(s) not of formula (1), such as ethylene or propylene. In the co-monomer according to formula (1) R 1 represents a hydrogen atom, a lower alkyl group or a carboxyl group; R 2 represents a hydrogen atom or a lower alkyl group; and R 3 represents a hydrogen atom or a lower hydroxyalkyl group. In this definition "lower" means "C 1 -C 6 ". R 1 can be, for example, a hydrogen atom, a lower alkyl group such as a methyl, ethyl, propyl, butyl or pentyl group, or a carboxyl group. R 2 can be, for example, a hydrogen atom or the same lower alkyl group as that of R 1 , R 3 can be, for example, a hydrogen atom, or a lower hydroxyalkyl group such as a 2-hydroxyethyl, 2-hydroxypropyl, 3-hydroxypropyl or 3-hydroxybutyl group. Specific examples of the carbonyloxy group-containing vinyl monomer (1) include 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 3-hydroxybutyl acrylate, 2-hydroxybutyl methacrylate, acrylic acid, methacrylic acid, and monobutyl maleate. Of these, preferred are 2-hydroxyethyl acrylate and 2-hydroxyethyl methacrylate. The ratio of component (B) to component (A) in the composition of the present invention is preferably from 3/97 to 20/80 by weight. The content of the carbonyloxy group-containing vinyl monomer is from 0.05 to 1 part by weight per 100 parts by weight of the total polyvinyl chloride resin (sum of the components (A) and (B)). If it is less than 0.05 part by weight, the adhesion of the covering material to be formed from the composition to urethanes may be insufficient, while if it is more than 1 part by weight, the powder dropping property of the composition may be poor. More preferably, it is from 0.1 to 0.6 part by weight. Suitable plasticizers for use in the present invention include; for example, dialkyl phthalates in which each alkyl group has from 9 to 11 carbon atoms, such as diisodecyl phthalate and diisoundecyl phthalate; and trialkyl trimellitates in which each alkyl group has from 7 to 11 carbon atoms, such as trioctyl trimellitate, tri-2-ethylhexyl trimellitate and tridecyl trimellitate. However, these are not specifically limitative and any and every plasticizer of utility in resin compositions for powder molding may be used. The amount of the plasticizer in the composition of the present invention is preferably from 40 to 120 parts by weight per 100 parts of the total polyvinyl chloride resin. Suitable stabilizers for use in the present invention include, for example, compounds of metals such as zinc, barium, sodium, potassium, calcium, lithium and tin, such as metal carboxylates, and composites thereof. Along with the stabilizer, also usable are magnesium oxide, magnesium hydroxide, hydrotalcites, zinc oxide, barium oxide, calcium oxide and barium phosphate. Especially preferred is a combination of zinc-barium composite salt and hydrotalcite, since the heat resistance of the urethane-laminated product from the composition is high. The composition of the present invention may also contain, as a stabilizer, antioxidant such as phenol compounds, thioether compounds and phosphorus compounds, photo-stabilizer such as diketo compounds, salicylic acid compounds, benzophenone compounds, benzotriazole compounds and hindered amine compounds, as well as an epoxy compound. However, these are not specifically limitative and any and every stabilizer of utility in a resin composition for powder molding may be used. The amount of the stabilizer in the composition of the present invention is preferably from 3 to 15 parts by weight per 100 parts by weight of the total polyvinyl chloride resin. The composition of the present invention may further contain, in addition to the plasticizer and stabilizer, other additives such as foaming agent and foaming auxiliary assistant, if desired. Suitable foaming agents, for example, are decomposable foaming agents such as azodicarbonamide, p,p'-hydroxybisbenzenesulfonyl hydrazide, p-toluenesulfonyl hydrazide and benzenesulfonyl hydrazide. These may be used as a mixture of two or more; especially preferred is azodicarbonamide. Where the composition of the present invention contains foaming agent, the content thereof is preferably from 1 to 10 parts by weight per 100 parts by weight of the total polyvinyl chloride resin. If desired, the composition of the present invention may contain a foaming auxiliary assistant along with foaming agent. Suitable foaming auxiliary assistants include, for example, inorganic zinc salts such as zinc flower and zinc nitrate, zinc fatty acid soaps such as zinc octoate and zinc stearate, as well as urea. These may be used as a mixture of two or more. Where the composition of the present invention contains foaming auxiliary assistant, the content thereof is preferably from 0.2 to 3 parts by weight per 100 parts by weight of the total polyvinyl chloride resin therein. The composition of the present invention may further contain, if desired, other additives such as filler (e.g., calcium carbonate) and pigment (e.g., titanium oxide, carbon black), in addition to the above-mentioned components. The composition of the present invention may be produced by dry-blending component (A) and plasticizer and stabilizer (and optionally other additives such as foaming agent and foaming auxiliary assistant) followed by adding the component (B) to the resulting dry blend. The temperature for the first stage dry-blending is preferably from 60 to 130°C, and the temperature for the second stage blending is preferably from 40 to 80°C. Thus, the polyvinyl chloride resin composition for powder molding of the present invention is obtained, and it is industrially advantageous as it has an excellent powder dropping property and may form a covering material having uniform thickness and good adhesion to a polyurethane layer. EXAMPLES The present invention will be explained in more detail by way of the following examples, which, however, are not limitative. Example 1 Preparation of fine granular vinyl chloride copolymer: A 100-liter glass-lining autoclave was charged with 40 kg of ion-exchanged water and 920 g, as the polymer ingredient, of polyvinyl chloride latex having an average particle size of 0.3 µm, and this was sealed with a lid and and subjected to nitrogen substitution under reduced pressure. Afterwards, 34 kg of vinyl chloride monomer was added to the autoclave and the temperature therein was elevated up to 53°C to start the polymerization, whereupon a total of 0.004 wt.% (based on the vinyl chloride monomer) of hydrogen peroxide and a total of 1.0 mol equivalent(based on the hydrogen peroxide) of Rongalit were added thereto via separate lines throughout the whole polymerization period (13 hours), each each at a constate rate. During the period from 12% polymerization to the finish of the polymerization, emulsifier and comonomer were continuously added to the autoclave; sodium laurylsulfate was added as an emulsifier at a rate of 0.03 % an hour and 2-hydroxyethyl acrylate as a comonomer at a rate of 0.5 % an hour, both based on the weight of vinyl chloride monomer. The polymerization was stopped after the polymerization pressure became lower than the saturated vinyl chloride vapor pressure by 1 kg/cm2 at 53°C. The non-reacted monomers were recovered and the resulting copolymer was spray-dried. The contents of sodium lauryl sulfate and 2-hydroxyethyl acrylate in the copolymer thus obtained were 0.3 % by weight and 5 % by weight, respectively. The vinyl chloride copolymer thus obtained had an average particle size of 1.0 µm. Preparation of non-foaming composition for powder molding: A supermixer was charged with 90 parts by weight of granular polyvinyl chloride resin (produced by suspension polymerization, having an average particle size of 120 µm and an average degree of polymerization of 800). After heating to 80°C with uniform stirring, the resin was dry-blended with 70 parts by weight of trimellitic ester plasticizer and 3 parts by weight of Ba-Zn stabilizer. Mixing was continued until the temperature of the mixture reached 125°C. Then the mixture was cooled to 50°C. The mixture was uniformly dispersed with 10 parts by weight of the previously obtained fine granular vinyl chloride copolymer to prepare a resin composition for powder molding. Preparation of single-layer sheet from non-foamable resin composition for powder molding: A nickel flat mold was pre-heated in a Geer oven at 280°C for 10 minutes and taken out therefrom. The mold temperature was about 240°C. Immediately, the previously prepared non-foamable composition was sprinkled over the mold, and the excess composition was discharged therefrom after about 13 seconds. Then, the mold was put in a Geer oven having an ambient temperature of 240°C and again heated therein for one minute and thereafter taken out. After cooling, the layer of the resin composition was released from the mold. Thus, there was obtained a molded sheet. The resin composition was evaluated as follows. The results are shown in Table 1. (1) Powder dropping property (removability of excess powder) 1 ○ Evaluated by observing the back of the molded sheet. ○ : The thickness of the sheet is even. Δ : The thickness of the sheet is somewhat uneven. x : The thickness of the sheet is noticeably uneven. 2 ○ Evaluated by filling the resin composition (level, about 75 g) into an aluminium cup (73 mm in inside diameter and 25 mm high), heating the cup on a hot plate at 240°C for 2 minutes, upsetting the aluminium cup, and measuring the amount of the resin composition remaining in the aluminium cup. (2) Adhesion of the single-layer sheet to semi-rigid polyurethane resin Evaluated by aging the single-layer sheet at 50°C and 50% RH for 7 days, backing the single-layer sheet with an approximately 10 mm thick layer of semi-rigid polyurethane resin in a polyurethane foaming mold, cutting a 25-mm wide test piece out of the sample, and measuring the 180° peel strength between the layer of the polyvinyl chloride resin sheet and the layer of the semi-rigid polyurethane resin at 23°C and a peeling rate of 200 mm/min. O : Peeling occurred in the material. (This indicates good adhesion at the interface.) × : Peeling occurred at the interface. (This indicates poor adhesion at the interface.) Examples 2 and Comparative Examples 1 and 2 Powder compositions .were prepared in the same manner as in Example 1, except that 10 parts by weight of fine granular vinyl chloride copolymer containing 2, 20 and 0 % by weight, respectively, of 2-hydroxyethyl acrylate was used. The compositions were molded in the same manner as in Example 1 to give molded sheets. The sheets were evaluated and the results are shown in Table 1. Comparative Example 3 A resin composition for powder molding was prepared in the same manner as in Example 1, except that 2 parts by weight of polypropylene glycol was incorporated in addition to the plasticizer and the stabilizer in dry-blending and that fine granular vinyl chloride homopolymer was used in place of the fine granular vinyl chloride copolymer. This was molded into a molded sheet. This was evaluated in the same manner as in Example 1, and the results are shown in Table 1. Comparative Example 4 A powder composition was prepared in the same manner as in Example 1, except that 2 parts by weight of polyether polyol (Sumiphen 3063, produced by Sumitomo Bayer Urethane Co.) was incorporated in addition to the plasticizer and the stabilizer in dry-blending and that fine granular vinyl chloride homopolymer was used in place of the fine granular vinyl chloride copolymer. This was molded into a molded sheet in the same manner as in Example 1. This was evaluated in the same manner as in Example 1, and the results are shown in Table 1. Example 3 Preparation of foamable resin composition for powder molding: A supermixer was charged with 90 parts by weight of granular polyvinyl chloride resin (produced by suspension polymerization, having an average particle size of 120 µm and an average degree of polymerization of 800). After heating to 80°C with uniform stirring, the resin was dry-blended with 70 parts by weight of trimellitic ester plasticizer, 3 parts by weight of Ba-Zn stabilizer, 1.5 parts by weight of azodicarbonamide and one part by weight of zinc flower. Mixing was continued until the temperature of the mixture reached 125°C. Then the mixture was cooled to 50°C. The mixture was uniformly dispersed with 10 parts by weight of fine granular vinyl chloride copolymer containing 5 % by weight of 2-hydroxyethyl acrylate to prepare a resin composition for powder molding. Preparation of two-layer sheet from non-foamable resin composition for powder molding and foamable resin composition for powder molding: A nickel flat mold was pre-heated in a Geer oven at 280°C for 10 minutes and taken out therefrom. The mold temperature was about 240°C. Immediately, the same non-foamable powder composition as that obtained in Comparative Example 1 (composition containing no 2-hydroxyethyl acrylate unit) was sprinkled over the mold, and the excess composition was discharged therefrom after about 5 seconds. Then, the previously prepared foamable resin composition was sprinkled thereover, and the excess composition was discharged therefrom after about 15 seconds. The mold was put in a Geer oven having an ambient temperature of 240°C and again heated therein for one minute for foaming and thereafter taken out. After cooling, the molded sheet was released and taken out from the mold. The resin composition was evaluated as follows. The results are shown in Table 1. (1) Adhesion of two-layer sheet to foamed semi-rigid polyurethane Evaluated by aging the two-layer sheet at 25°C and 50% RH for one day, backing the foamed layer of the two-layer sheet with an approximately 10 mm thick layer of foamed semi-rigid polyurethane resin in a polyurethane foaming mold, cutting a 25-mm wide test piece out of the sample, and measuring the 180° peel strength between the polyvinyl chloride resin sheet and the layer of the polyurethane resin at 23°C and a peeling rate of 200 mm/min. Evaluation was effected in the same manner as in Example 1. The results obtained are shown in Table 2. Examples 4 and Comparative Examples 5 and 6 Preparation of foamable resin composition for powder molding: Foamable resin compositions for powder molding were prepared in the same manner as in Example 3, except that 10 parts by weight of fine granular vinyl chloride copolymer containing 2, 20 and 0 % by weight, respectively, of 2-hydroxyethyl acrylate was used. The compositions were molded in the same manner as in Example 1 to give molded sheets. The sheets were evaluated and the results are shown in Table 2. Comparative Example 7 A foamable resin composition was prepared in the same manner as in Example 3, except that 2 parts by weight of polypropylene glycol was incorporated in addition to the plasticizer, the stabilizer, azodicarbonamide and zinc flower in dry-blending and that fine granular vinyl chloride homopolymer was used in place of the fine granular vinyl chloride copolymer. This was molded into a molded sheet. This was evaluated in the same manner as above, and the results are shown in Table 2. Comparative Example 8 A foamable resin composition was prepared in the same manner as in Example 3, except that 2-parts by weight of polyether polyol was incorporated in addition to the plasticizer, the stabilizer, azodicarbonamide and zinc flower in dry-blending and that fine granular vinyl chloride homopolymer was used in place of the fine granular vinyl chloride copolymer. This was molded into a molded sheet in the same manner as in Example 3. This was evaluated in the same manner as above, and the results are shown in Table 2.

Claims: A polyvinyl chloride resin powder composition containing (A) granular polyvinyl chloride resin of particle size 100-150 µm; (B) vinyl chloride copolymer resin containing copolymer of vinyl chloride monomer of particle size 0.1-10 µm for coating granular resin (A) and carbonyloxy group-containing vinyl comonomer(s) component; and (C) stabilizer and plasticizer, said comonomer(s) component being (i) of formula (1) : wherein R 1 represents a hydrogen atom, a C 1 -C 6 alkyl group or a carboxyl group, R 2 represents a hydrogen atom or a C 1 -C 6 alkyl group, and R 3 represents a hydrogen atom or a C 1 -C 6 hydroxyalkyl group, and (ii) constituting from 0.05 to 1 part by weight per 100 parts by weight of the sum of (A) and (B). A composition as claimed in claim 1 in which said comonomer component is at least one mononer selected from 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 3-hydroxybutyl acrylate, 2-hydroxybutyl methacrylate, acrylic acid, methacrylic acid and monobutyl maleate. A composition according to claim 1 or 2 in which the ratio of (B) to (A) is from 3/97 to 20/80 by weight. A composition according to any preceding claim which contains foaming agent. A method of preparing a polyvinyl chloride resin powder composition according to any preceding claim in which resin (A) is dry-blended with stabilizer and plasticizer (C) and the resulting blend is mixed with copolymer resin (B). A method according to claim 5 wherein resin (A) is dry-blended with stabilizer and plasticizer (C) along with foaming agent. A method according to claim 6 wherein the foaming agent is accompanied by a foaming auxiliary assistant. A method of preparing a covering material in which a polyvinyl chloride resin powder composition according to any of claims 1 to 4 is molded by powder molding, optionally followed by backing the powder molded product with a foamed polyurethane layer. A powder-molded product of a composition according to any of claims 1-4. A product according to claim 9 with a foamed polyurethane backing.

Inventors: IGARASHI TOSHIO, NAKATSUJI YOSHIHIRO, SHIDA YUU, SHIMIZU HIKARU, WAKATSUKI AKIRA, IGARASHI, TOSHIO, NAKATSUJI, YOSHIHIRO, SHIDA, YUU, SHIMIZU, HIKARU, WAKATSUKI, AKIRA
Applicants: SUMITOMO CHEMICAL CO, SUMITOMO CHEMICAL COMPANY LIMITED
Application year: 1992
Main classification: C08L27
IPC codes: C08L27, C08J3