Ceramic filter for molten metal

Abstract: A ceramic filter used for filtering molten metal, particularly molten aluminum, made by sintering the composition comprising 90 parts by weight of electrofused alumina for an aggregate and 5 to 15 parts by weight of an inorganic binder. The inorganic binder comprises 5 to 15 wt% of B₂O₃, 15 to 50 wt% of MgO. 3 to 10 wt% of SiO₂ and the remainder Al₂O₃. This filter has a filtering capacity equal to that of conventional ceramic filters, does not cause the problem of the contamination of molten aluminum, and has an enough strength to endure practical use.

Description: BACKGROUND OF THE INVENTION 1) Field of the Invention The present invention relates to a ceramic filter used for filtering off nonmetallic inclusions mixed in molten metal, particularly molten aluminum. 2) Description of the Prior Art When aluminum (including aluminum alloy) is melted, various nonmetallic inclusions usually mixes in it. The inclusions are removed from molten aluminum by means of filters. A ceramic filter used for this purpose is disclosed in Japanese Patent Provisional Publication gazette No. 22327/1977, which is made by sintering fused alumina for an aggregate and an inorganic binder containing 10 to 50 wt% of SiO₂ and 5 to 20 wt% of B₂O₃. There is a problem with this filter that its constituents such as Ca and Si dissolve into molten aluminum while molten aluminum is passed through it. Though the amount of dissolution is very small, this problem is serious particularly to high purity aluminum. Another type of ceramic filter which does not contain SiO₂ is proposed in Japanese Patent Provisional Publication gazette No. 34732/1990. The binder of this filter comprises 15 to 80 wt% of B₂O₃, 2 to 60 wt% of Al₂O₃, and 5 to 50 wt% of CaO or MgO or both of them. Though there is no problem of the dissolution of the constituents such as Si with this filter, it can break during use because of the lack of strength of the filter itself. Further, since this filter does not contain SiO₂, and in general the filters which do not contain SiO₂ have a poor wettability for molten aluminum, its permeability for molten aluminum is low, and the filtering capacity of this filter is not sufficient for practical use. The low permeability for molten aluminum also causes the rise of the initial head of molten aluminum (the height of the surface of molten aluminum when the molten aluminum is poured on the filter at the beginning of a filtering operation and begins to pass through the filter). Therefore, when conventional filters being used in an existing apparatus are replaced with this filter, the filtering apparatus sometimes must be modified so as to accommodate the rise of the initial head. SUMMARY OF THE INVENTION The object of the present invention is to provide an improved ceramic filter used for filtering molten metal, particularly molten aluminum which has a high filtering capability equal to that of conventional filters, does not cause the problem of contamination, and has an enough strength to endure practical use. The present invention attains the above object by a ceramic filter for molten aluminum made by sintering the composition comprising 90 parts by weight of electrofused alumina particles for an aggregate material and 5 to 15 parts by weight of an inorganic binder, characterized by that the binder comprises 5 to 15 wt% of B₂O₃, 15 to 50 wt% of MgO, 3 to 10 wt% of SiO₂ and the remainder Al₂O₃. This filter has been invented by closely examining the relationship between the SiO₂ content in the inorganic binder and the contamination of molten aluminum by the filter and the strength of the filter at the temperature at which the filter is used. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 shows the relationship between the SiO₂ content in the binder and the height of the initial head of molten aluminum. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS In this invention, the amount of the inorganic binder is 5 to 15 parts by weight to 90 parts by weight of electrofused alumina for the aggregate. If the amount of the inorganic binder is smaller than 5 parts by weight, the strength of the filter is not sufficient; if it is greater than 15 parts by weight, the porosity of the filter obtained is too low and hence the filtering capacity is not sufficient for practical use, though the strength is adequate. The inorganic binder of the present invention comprises 5 to 15 wt% of B₂O₃, 15 to 50 wt% of MgO, 3 to 10 wt% of SiO₂ and the remainder Al₂O₃. The range of each constituent of the inorganic binder is determined by the following reason. It is thought from experience that filters used for filtering molten aluminum must have the modulus of rupture larger than 30 kg/cm² at 800 °C and larger than 100 kg/cm² at room temperature. If the amount of B₂O₃ is smaller than 5 wt%, vitreous material formed in the binder is not sufficient and the strength of the filter at room temperature is too low. If the amount of B₂O₃ is larger than 15 wt%, the strength of the filter at room temperature and that at 800 °C are both too low, and the filter thus is not practically usable. Addition of SiO₂ increases the modulus of rupture of the filter both at room temperature and at 800 °C. However, if the amount of SiO₂ is smaller than 3 wt%, the filter obtained has a poor wettability for molten aluminum. The poor wettability causes the rise of the initial head of molten aluminum. It also decreases the filtering capacity through the lowering of the permeability for molten aluminum. If the amount of SiO₂ is larger than 10 wt%, the dissolution of Si into molten aluminum increases and can cause the problem with the quality of filtered aluminum, particularly that of high purity aluminum. The amount of MgO is determined so that the filter has a desirable strength. If the amount of MgO is smaller than 15 wt% or larger than 50 wt%, the strength of the filter is lower than the desirable value. Examples All examples were made by sintering 90 parts by weight of the aggregate, 10 parts by weight of the inorganic binder, and 5 parts by weight of a combustible material. No. 24 JISA abrasive perticles (electrofused alumina) was used for the aggregate and grain powder for the combustible material. The binder of each example was prepared by mixing SiO₂, B₂O₃, and MgO in the proportion as shown in Table 1. The aggregate, inorganic binder, and combustible material were kneaded, molded, and sintered at a temperature within the range of 1,350 to 1,450 °C. The samples thus obtained were tested on the modulus of rupture. This test was conducted by supporting each sample at two points with a span of 90 mm and applying a load to it at the middle point. The modulus of rupture at 800 °C was also measured by the same method after having placed the samples in an electric furnace and maintained them at 800 °C for 20 minutes. The test results are also shown in Table 1. Samples 6 to 9 were further tested on the Si dissolution by putting the samples in molten 5056 aluminum at 750 °C for 7 days, stirring and leaving still repeatedly. The test results were shown in Table 2. It is known from Tables 1 and 2 that, when the SiO₂ content is within the range of 3 to 10 wt%, the filter has a satisfactory modulus of rupture and, at the same time, the Si dissolution is so small that the contamination of molten aluminum can substantially reduced in comparison to conventional filters. The relationship between the SiO₂ content and the height of the initial head of molten aluminum is shown in Figure 1. It is known from Figure 1 that by addition of a small amount of SiO₂ the filter has the wettability for molten aluminum almost equal to that of conventional filters, and therefore can prevent the rise of the initial head of molten aluminum. According to the present invention, as described above, a filter which has a filtering capacity equal to that of conventional filters, does not cause the problem of contamination, and has an enough strength to endure practical use, is obtained by properly selecting the SiO₂ content in the inorganic binder. Therefore conventional filters being used in an existing apparatus can be replaced with the filter of the present invention without modification of the apparatus and change of the operating conditions. Sample No. Composition of binder Modulus of Rupture (kg/cm²) Al₂O₃ B₂O₃ MgO SiO₂ at Room Temp at 800 °C 1 50 3 42 5 58 48 2 50 5 40 5 110 45 3 50 15 30 5 120 44 4 50 18 27 5 71 12 5 50 10 39 1 85 30 6 50 10 37 3 100 32 7 50 10 35 5 130 35 8 50 10 30 10 139 42 9 50 10 25 15 155 67 10 25 10 60 5 45 22 11 45 10 40 5 133 35 12 55 10 30 5 129 37 13 75 10 10 5 52 25 Sample No. Analyzed Si content (%) Si dissolution (%) 6 0.049 0.001 7 0.049 0.001 8 0.050 0.002 9 0.085 0.037 Conv. filter 0.220 0.172 Blank 0.048 0

Claims: A ceramic filter used for filtering molten metal made by sintering the composition comprising 90 parts by weight of electrofused alumina for an aggregate and 5 to 15 parts by weight of an inorganic binder, characterized by that the inorganic binder comprises 5 to 15 wt% of B₂O₃, 15 to 50 wt% of MgO, 3 to 10 wt% of SiO₂ and the remainder Al₂O₃.

Inventors: SHIRAISHI YUKIHISA C O MITSUI, YOSHISA TADAHIRO C O MITSUI MI, SHIRAISHI, YUKIHISA, C/O MITSUI MINING & SMELTING, YOSHISA, TADAHIRO, C/O MITSUI MINING & SMELTING, Shiraishi, Yukihisa, c/o Mitsui Mining &amp; Smelting, Yoshisa, Tadahiro, c/o Mitsui Mining &amp; Smelting
Applicants: MITSUI MINING & SMELTING CO, MITSUI MINING & SMELTING CO., LTD.
Application year: 1992
Main classification: B01D39
IPC codes: C22B9, C22B21, B01D39, C04B38