Silicon carbide matrix ceramics containing a dispersed high metal content silicide phase

Abstract: A sintered silicon carbide product having improved fracture toughness contains from 1% to 80% by weight of (a) a uniformly dispersed, nonagglomerated, high metal content silicide of iron, nickel, cobalt or molybdenum in which the metal/silicon ratio is equal to or greater than 1. The silicon carbide starting material can be alpha-phase, beta-phase or a mixture of the two.

Description: This invention relates to silicon carbide matrix ceramics containing a dispersed phase to improve fracture toughness. Silicon carbide powders are not sinterable when they are in a pure form. Previously, boron or boron carbide and carbon were added in order to densify silicon carbide. Usually, the beta phase of silicon carbide is used as the starting material, with transformation into the alpha phase occurring as the densification process continues. Regardless of the starting material, the resulting ceramic has low fracture toughness values of appoximately 4 MPa √m. This low fracture toughness value for monolithic silicon carbide limits its usage. It is known that crack propagation in silicon carbide can be minimized by the inclusion of a dispersed phase, which provides a mechanism for energy diffusion. For example, J. J. Petrovic and R. E. Honnell, "MoSi 2 Particle Reinforced-SiC and Si 3 N 4 Matrix Composites", J. Mat. Sci. Lett. 9 (1990) 1083-1084, disclose mixing SiC and molybdenum disilicide to improve the high temperature mechanical properties of the SiC composite. However, the molybdenum disilicide particles inhibit densification to less than 90% and the dispersion of the molybdenum disilicide is poor with large agglomerations visible in the microstructure. Petrovic et al. disclose in U.S. Patent 5,069,841 that a material comprising a matrix of an alloy of MoSi 2 and another refractory silicide such as Mo 5 Si 3 , with SiC dispersed throughout, has improved high temperature strength and possibly improved fracture toughness. The sintered ceramic product of this invention consists essentially of (1) from 20% to 98% by weight of alpha-phase, beta-phase or a mixture of alpha- and beta-phase silicon carbide, (2) from 1% to less than 80% of a nonagglomerated, uniformly dispersed, high metal content silicide of iron, nickel, cobalt or molybdenum in which the metal/silicon atomic ratio is equal to or greater than one, and (3) 0.02% to 20% of at least one oxide, nitride or silicate of an element selected from IUPAC Groups 2, 3, 4, 13 or the lanthanide series, all percentages being by weight, based on the total weight of the composition. The silicon carbide compositions of the present invention contain only high metal content silicides such as Mo 5 Si 3 and Fe 2 Si. The dispersion of high metal content silicides in the silicon carbide matrix provides an energy diffusing mechanism, thus minimizing crack propagation and improving the fracture toughness of the product. The silicon carbide used in this invention can be any commercial silicon carbide, either of the alpha or beta phases, or a mixture of alpha and beta phases. The silicon carbide is used in an amount of from 20% to 98% by weight, based on the total weight of the composition. Other refractory compounds that are chemically stable in the presence of silicon carbide can be used to replace up to 50% by weight of the SiC, e.g., titanium carbide, titanium diboride, zirconium carbide, and zirconium diboride. In the preparation of the silicon carbide ceramics of this invention, the silicon carbide powder is mixed with from 1% to 50% by weight, preferably 3% to 20%, based on the total weight of the composition, of Mo, Fe, Co or Ni. An oxide of these metals, or an alloy of these metals with each other or with another metal can also be used. The powder mixture also includes 0.02% to 20% by weight, preferably from 0.5% to 10% by weight, of compounds that act as sintering aids. The sintering aid is an oxide, nitride, or silicate of an element from IUPAC Groups 2 (alkaline earth metals); 3 (Sc, Y, La, Ac), 4 (Ti, Zr, Hf), 13 (B, Al, Ga, In, Tl) or the lanthanide series, or mixtures thereof. Oxides of aluminum, magnesium, calcium, strontium, zirconium, and yttrium are preferred. A combination of aluminum oxide and yttrium oxide is most preferred. In order to impart optimum properties to the sintered product, the ingredients used to prepare the initial mixture should be finely divided, preferably having a particle size of less than than five microns, most preferably less than one micron. It is important that the finely divided particles be well dispersed, with no aggregates of like materials contained within the powder. This distribution is accomplished by milling the powders in the presence of a dispersant. Milling can be in aqueous or organic solvents, with the choice of dispersants depending upon the solvent used. Common aqueous dispersants are the DARVAN® series, which are ammonium salts of polyelectrolytes, supplied by R. T. Vanderbilt. The type of mills used can be attrition mills, ball mills, or vibratory mills, with milling times ranging from one hour to 100 hours depending upon the size of the initial powders used. Long milling times result in greater milling media wear and short milling times can result in nonuniform mixing and incomplete reduction of particle size. The preferred milling times range from eight to 24 hours. After milling, the solvent can be removed, for example, by spray drying. Solvent removal must not result in segregation of the constituent materials into aggregates. The powder mixtures of this invention are preferably densified by simultaneously applying heat and pressure. The preferred processing techniques are hot pressing, hot isostatic pressing, and gas pressure sintering. The preferred sintering temperature range is from 1800°C to 2200°C. Higher temperatures may be required in order to densify compositions starting with the alpha phase of silicon carbide. Lower temperatures are desirable when the starting beta phase is also desired in the final material, since higher temperatures will result in the conversion of the beta phase to the alpha phase. The pressure used can range from 35 to 1050 kg/cm 2 (500 to 15,000 psi), preferably 70 to 350 kg/cm 2 (1000 to 5000 psi). A nonoxidizing, nonreactive atmosphere such as argon or helium is used to prevent reactions between the atmosphere and the constituent powders during sintering. During sintering, the metal or metal compound reacts with silicon carbide in situ to form high metal content silicides. High metal content silicides are defined as those in which the metal/silicon atomic ratio is equal to or greater than one, e.g., Mo 5 Si 3 , Fe 2 Si, Co 2 Si, CoSi, Ni 2 Si and Fe 3 Si. When molybdenum is used, a small amount of molybdenum carbide may be formed in addition to Mo 5 Si 3 . This result is unexpected, since existing high temperature thermodynamic data indicate that MoSi 2 should be more stable than MoC. MoSi 2 would also be expected to be more stable than Mo 5 Si 3 . The sintered ceramic product consists essentially of (1) from 20% to 98% of alpha-phase, beta-phase or a mixture of alpha- and beta-phase silicon carbide, (2) from 1% to less than 80% by weight of a nonagglomerated, uniformly dispersed, high metal content silicide of iron, nickel, cobalt or molybdenum in which the metal/silicon atomic ratio is equal to or greater than 1, and (3) from 0.02% to 20% of at least one oxide, nitride or silicate of an element selected from IUPAC Groups 2, 3, 4, 13, or the lanthanide series, all percentages being by weight based on the total weight of the composition. The product is composed of (1) a silicon carbide matrix, (2) well dispersed, nonagglomerated particles of the high metal content silicide, and (3) an oxide, nitride or silicate phase between the matrix and the dispersed silicide. The product is useful for applications in which high fracture toughness is desired in SiC ceramics. In the following examples, powders were milled for 16 hours in a small, vibratory mill, using water and DARVAN® C supplied by R. T. Vanderbilt as the dispersant. The slurries were spray dried in a small laboratory spray dryer and the powders were hot pressed uniaxially in graphite dies under argon. Sintered bulk densities were determined geometrically. The dense sintered samples were then ground flat and polished to a 1 µm diamond finish. The parts were indented with a pyramidal diamond hardness tester (Vickers). The cracks emanating from the corners were used to estimate the fracture toughness of the material. A 1000 g load was applied on the indenter for 15 seconds. After measurement, the sample of Example 2 was further polished to determine the type of crack system that had developed. After about half of the depth of the indent was removed, no cracks remained. The cracks that had developed in these materials were thus what is known as palmqvist cracks. In order to calculate the toughness, equations that have been derived for Palmqvist crack systems were used (see (1) D. K. Shetty et al., J. Mat Sci. , 20, 1873-82 (1985) and (2) J. Lankford, J. Mat. Sci. Lett. , 1, 493-95 (1982)). Example 1 Starting materials: beta-silicon carbide 84.6% by weight cobalt metal (2 µm) 10.0% by weight alumina 3.6% by weight yttria 1.8% by weight Hot Press Conditions Results 2000°C for 2 hours at 280 kg/cm 2 (4000 psi) Density = 3.32 g/cc (95.7 % TD) Phases = beta-SiC + CoSi + small amount of alpha-SiC Rockwell A hardness (Ra) = 93.1 Strength = 380 MPa The microstructure of the densified material shows mainly equiaxed grains of about 2 µm (beta-phase) and occasional elongated grains having dimensions of 2 x 5 µm (alpha-phase). No cracks developed from Vickers indent corners, indicating high toughness. Example 2 Starting materials: beta-silicon carbide 81.9% by weight iron metal ≤45 microns (-325 mesh) 10.0% by weight alumina 2.7% by weight yttria 5.4% by weight Hot Press Conditions Results 2000°C for 1 hour at 280 kg/cm 2 (4000 psi) Density = 3.3 g/cc Phases = beta-SiC + Fe 2 Si Hardness (Ra) = 92.4 Strength = 400 MPa K IC (Ref. 1) = 6.1 MPa √m K IC (Ref. 2) = 5.8 MPa √m The microstructure of the densified material shows some tabular grains 5 µm across by 1 µm thick. The two methods of calculating fracture toughness agree very well. The values obtained are much higher than for monolithic silicon carbide, which has a value of only about 4 MPa √m. Example 3 Starting materials: beta-silicon carbide 85.95% by weight cobalt metal (2 µm) 10.00% by weight alumina 1.35% by weight yttria 2.70% by weight Hot Press Conditions Results 2000°C for 1 hour at 280 kg/cm 2 (4000 psi) Density = 3.3 Phases = beta-SiC + CoSi + alpha-SiC (trace) Hardness (Ra) = 92.8 Strength = 300 MPa The microstructure of the densified material shows equiaxed grains of about 2 µm and occasional larger elongated grains 3 µm by 5-10 µm long. No cracks developed from Vickers indent corners, indicating high fracture toughness. Example 4 Starting Materials: beta-silicon carbide 85.95% by weight molybdenum metal 10.00% by weight alumina 1.35% by weight yttria 2.70% by weight Hot Press Conditions Results 2000°C for 2 hours at 280 kg/cm 2 (4000 psi) Density = 3.4 g/cc Hardness (Ra) = 94.3 Strength = 499 MPa Phases = beta-SiC + small amount of alpha-SiC + MoC + Mo 5 Si 3 K IC (Ref. 1) = 7.1 MPa √m K IC (Ref. 2) = 6.9 MPa √m The two methods for calculating fracture toughness agree very well. These values are higher than those obtained in Example 2, and are also much higher than those for monolithic silicon carbide. It appears that under these hot press conditions, molybdenum reacts with SiC to form both MoC and Mo 5 Si 3 rather than the expected MoSi 2 phase.

Claims: A sintered silicon carbide matrix ceramic product containing metal silicides characterized in that it consists essentially of (1) from 20% to 98% of alpha-phase, beta-phase or a mixture of alpha- and beta-phase silicon carbide, (2) from 1% to less than 80% of a nonagglomerated, uniformly dispersed, high metal content silicide of iron, nickel, cobalt or molybdenum in which the metal/silicon atomic ratio is equal to or greater than 1, and (3) from 0.02% to 20% of at least one oxide, nitride or silicate of an element selected from IUPAC Groups 2, 3, 4, 13, or the lanthanide series, all percentages being by weight based on the total weight of the composition. The ceramic product of claim 1, further characterized by replacing up to 50% by weight of the silicon carbide with at least one refractory boride or carbide other than silicon carbide. The ceramic product of claims 1 or 2, further characterized in that component (3) is a mixture of yttria and alumina. The ceramic product of claim 3, further characterized in that the yttria is present in an amount of 1.0 to 6.0% by weight and the alumina is present in an amount of 1.0 to 4.0% by weight. The ceramic product of any of the preceding claims, further characterized in that the high metal content silicide is Fe 2 Si. The ceramic product of claim 5 wherein the Fe 2 Si is present in an amount of 5.0 to 12.0% by weight. The ceramic product of any one of claims 1 to 4, further characterized in that the high metal content silicide is CoSi. The ceramic product of claim 7, further characterized in that the CoSi is present in an amount of 5.0 to 12.0% by weight. The ceramic product of any one of claims 1 to 4, further characterized in that the high metal content silicide is Mo 5 Si 3 . The ceramic product of claim 9, further characterized in that the Mo 5 Si 3 is present in an amount of 1.0 to 6.0% by weight. The ceramic product of any of the preceding claims, further characterized in that the SiC is completely beta-phase SiC. The ceramic product of any one of claims 1 to 10, further characterized in that the SiC is a mixture of alpha-phase and beta-phase SiC.

Inventors: MATSUMOTO ROGER LEE KEN, MATSUMOTO, ROGER LEE KEN
Applicants: LANXIDE TECHNOLOGY CO LTD, LANXIDE TECHNOLOGY COMPANY, LP
Application year: 1992
Main classification: C04B35
IPC codes: C04B35