Mold for molding glass and method of producing the same

Abstract: A water-soluble, high molecular weight dispersing agent, such as carboxmethyl cellulose, is present in a dispersion coating bath of a solution of a water-soluble nickel salt containing graphite dispersed therein, and a mold for molding a glass is immersed therein in a manner that the mold serves as the cathode and the nickel metal serves as the anode in order to effect the plating while suppressing nickel or a nickel-based alloy in the film from growing in a vertical direction or in the direction of the plane thereof. On the inner surfaces of the mold is formed a film which comprises a matrix of nickel or the nickel-based alloy which as a whole has a flake-like form that is continuous and exists in an open cellular form and a graphite granule phase which is held in the open cells and is outwardly exposed on the surface. Since nickel is suppressed from growing like granules, the film exhibits excellent lubricating property, heat resistance, parting property, abrasion resistance and durability in combination.

Description: The present invention relates to a mold for molding glass and to a method of producing the same. More specifically, the invention relates to a mold which is used for molding a parison from molten glass (gob), and which features long life, excellent moldability and smoothness of the glass molded articles. When molding glass, masses of glass melted at a high temperature is injected into a mold (blank mold and neck ring). In this case the glass does not often completely flow into the mold or wrinkles develop due to frictional resistance. In order to prevent this as well as to remove the molded glass easily from the mold, an oil (swabbing compound) containing graphite is applied onto the inner surfaces of the mold which can maintain lubricating properties for several tens of minutes. However, since the mold is usually heated to a temperature as high as about 500°C, oil soot is generated which deteriorates the working environment. Moreover, any excess graphite applied adheres to the surface of the glass container causing the products to be fouled and deteriorating the yields of the products. In order to solve these problems, there have been proposed a variety of lubricating/parting agents to substitute for the swabbing compounds. For instance, Japanese Laid-Open Patent Publication No 127111/1976 discloses a lubricating/parting agent used in an apparatus for producing glass containers, comprising 5 to 30% by weight of graphite or a mixture of graphite and a boron nitride, 5 to 30% by weight of at least one compound selected from the group consisting of aluminium biphosphate, aluminium primary phosphate and magnesium biphosphate, and 40 to 90% by weight of an aqueous solution containing acid. Japanese Laid-open Patent Publication No 10207/1974 discloses a mold for molding glass articles in which a nickel film containing phosphorus in an amount of 3 to 13% by weight is nonelectrolytically plated onto the inner surfaces of the mold maintaining a thickness of 5 to 300 µm to impart lubricating and parting properties to the inner surface of the mold. Japanese Patent Application No 63 100 027 filed by the present inventors describes a mold for molding glass the inner surfaces of the mold being coated with a film of nickel or nickel based alloy and with graphite granules. Some of the granules are outwardly exposed on the film surface. This application also describes a method of forming a mold for molding glass by immersing the mold in a coating bath containing a solution of a water soluble nickel salt with graphite dispersed therein. The mold is made cathodic relative to a nickel anode and the electric current precipitates nickel and graphite on the mold. However, the former lubricating/parting agent is poor in regard to heat resistance and abrasion resistance, and has a life of about 1 to 3 days. The alloy coating method mentioned above is excellent in regard to the durability of the film but still has a problem with respect to lubricating property which is very poor. The nickel film dispersed with graphite exhibits excellent lubricating and durability properties compared with those of the above prior art, but still tends to develop fine scars on the glass surfaces. The scars on the surface of the molded glass gradually increase after use over extended periods of time. That is, the film of the graphite-dispersed nickel plating exhibits the excellent lubricating property possessed by graphite and excellent heat resistance and abrasion resistance possessed by nickel. In effecting the dispersive plating, however, the nickel plated on the surfaces of the mold tends to granular growth. Thus, scars develop in the surface of the glass being caused by nickel that undergoes granular growth. The object of the present invention therefore is to provide a mold for molding glass in which nickel or a nickel-based alloy comprising chiefly nickel serving as a matrix and graphite granules are dispersively plated on the inner surfaces of the mold for molding a glass, wherein granular growth of nickel is suppressed in order to obtain excellent lubricating property, heat resistance, parting property abrasion resistance and durability combination, eliminating the aforementioned defects in the prior art. The invention further provides a method of producing such a mold. According to one aspect of the present invention, there is provided a mold for molding glass the inner surfaces of the mold being coated with a film of nickel or nickel based alloy chiefly comprising nickel and with graphite granules, the film comprising a matrix of nickel or nickel based alloy with graphite granules outwardly exposed on the film surface wherein the nickel or nickel based alloy being present in the form of flakes forming a matrix of open cells with graphite received in the cells at least 50 number percent of the flakes being not more than 20 µm long when measured in the plane of the film or normal to the plane. According to the present invention, furthermore, there is provided a method of producing a mold for molding glass comprising immersing the mold in a coating bath containing a solution of a water soluble nickel salt with graphite dispersed therein with the mold as a cathode and nickel metal as an anode and passing an electric current to precipitate nickel and graphite on the mold, wherein the presence in the bath of a water-soluble high molecular weight dispersing agent thereby suppressing growth of dispersively placed nickel or nickel based alloy in the film in the film plane or normal to the film. A preferred embodiment of the water-soluble high molecular weight dispersing agent is an anionic high molecular weight dispersing agent. Preferred dispersing agents include ammonium salts of anionic high molecular weight dispersing agents or ammonium salts of carboxy methyl cell-base. Particularly distinguished effects are obtained when the graphite granules are treated in advance. Fig. 1 is a electron microphotograph of the inner surface in cross section of a metal mold for molding glass according to the present invention. According to the present invention, the inner surfaces of the mold are coated with a film of nickel or a nickel-based alloy comprising chiefly nickel and graphite granules formed by nickel-graphite dispersion coating. This film exhibits excellent lubricating, heat resistance, parting property and abrasion property in combination during glass molding. As pointed out already, however, the film formed by the nickel-graphite dispersion coating exhibits the excellent lubricating properties possessed by graphite and the excellent heat resistance and abrasion resistance possessed by nickel. In effecting the dispersion coating, however, the nickel-plated layer tends to granular growth like in a direction perpendicular to the surface of the mold or in the further in the direction of the plane thereof, and fine scars inevitably develop in the surface of the glass due to granular nickel. According to the present invention, it was discovered when water-soluble high molecular weight dispersing agents are present in a dispersive plating bath which contains a solution of a water-soluble nickel salt with graphite being dispersed therein, nickel or the nickel-based alloy in the film suppressed from granular growing perpendicular to the mold or in the direction of the plane thereof, and a film, having a novel and fine structure is formed on the inner surface of the mold. The film that exists on the inner surface of the mold according to the present invention comprises (1) a matrix of nickel or a nickel-based alloy (hereinafter simply referred to as nickel) which is in the form of thin flakes and is continuous as a whole but exists in the form of open cells, and (2) a graphite granule phase which is held in the open cells and is outwardly exposed on the surface. Even in this dispersively plated film, the nickel matrix is formed through a step in which nickel granules precipitated by plating on the nickel granules undergo granular growth. Therefore, the nickel matrix as a whole is in a continuous form. In the film of the present invention, however, the nickel is suppressed from granular growth perpendicular to the mold or in the plane thereof, but assumes the form of thin flakes forming open cells, creating a distinctive feature. The open cell is similar to the structure of a wall (cell) found in a communicating bubble-type foamed material:- though the walls are continuous, there necessarily exists open portions. Graphite granules are held in the open cells and are further outwardly exposed on the surface of the film. The accompanying Fig. 1 is an electron microphotograph (magnification, 200 times) of a cross section of the surface of a mold the present invention. The lower continuous portion is an underlying metal, the white thin flake-like portions in the upper film represent nickel-plated layer, and grey granules represent a graphite granule phase. It will be better understood from this drawing that the film on the mold has the fine structure as described above. As will be seen from Fig. 1 the nickel is in the form of flakes. At least 50 number percent are not more than 20µm long in the film plane or perpendicular to the plane. In this specification, the flake length stands for the lengths of the flakes in the nickel-plated layer that are found by taking a photograph of the cross section of the film using a scanning electron microscope (SEM) and subjecting it to an image processor. The magnification of the SEM image is 700 times, the cutting width of the image processing is 0.3 µm. In the film on the surface of the mold of the present invention, nickel exists in the form of fine open cells and graphite granules are held in the cells. Therefore, the film has a mechanically rigid structure and exhibits excellent abrasion resistance, durability and heat resistance. Moreover, the graphite granules that are outwardly exposed in the open cells exhibit excellent lubricating properties, for extended periods of time. Moreover, since nickel exists in the form of thin flakes, molded articles of glass are not scratched even when the film is worn out; i.e. the molded articles have a smooth and high quality appearance. In the method of the present invention, the fact was discovered as a phenomenon in that a high molecular weight dispersing agent blended in the dispersive plating bath suppresses the nickel from granular growth, and brings about in open cellular form and thin flake structure. Though the reason is not yet clear, it is thought that the dispersing agent present in the plating bath promotes the graphite granules to adhere to the active points of the granular plated nickel. Particularly great effect for suppressing the growth of nickel granules are exhibited when an anionic high molecular weight dispersing agent is used as the dispersing agent probably due to the fact that graphite granules precipitate on the above-mentioned active points through the anionic dispersing agent. Because of this, the graphite granules are better treated in advance with the anionic high molecular dispersing agent. (Mold for molding glass) Examples of the mold include molds such as blank mold, finish mold, neck ring, bottom plate, baffle, press mold, etc. that are used for the production of bottles or jars, parisons thereof, dishes or any other molded articles by subjecting a mass of molten glass (or a so-called gob) to a molding method as as press molding, blow molding, press and blow process or blow and blow process. (Dispersive plating) The film is formed on the above-mentioned mold by the dispersive plating method that will be described below in detail. First, prior to effecting the dispersive plating, the inner surfaces of the mold are cleansed by dewaxing with an alkali, washing with an acid, polishing with emery, or shot blasting. The mold is immersed in the plating bath in a manner that the mold serves as a cathode and nickel serves as an anode which are opposed to each other, and an electric current is permitted to flow, so that graphite is precipitated together with nickel to form a film. It is important that the water-soluble high molecular weight dispersing agent and, in particular, the anionic high molecular weight dispersing agent is present in the dispersive plating bath. The water-soluble high molecular weight dispersing agent is extensively used for the purpose that the graphite granules are stably dispersed or suspended in the aqueous medium. According to the present invention, however, the above dispersing agent is used not only to improve the dispersion or suspension property but also to suppress the nickel granular growth which is a quite different action. Preferred examples of the water-soluble high molecular weight dispersing agent include anionic water-soluble polymers such as carboxymethyl cellulose, carboxymethyl starch, alginate, maleic acid-vinyl ether copolymer, (meth)acrylic acid-(meth)acrylic acid ester copolymer, (meth)acrylic acid-vinyl acetate copolymer, cellulose derivatives obtained by graft-polymerizing (meth)acrylic acid or (anhydrous) maleic acid, partly or completely saponified vinyl polyacetate, and other polymers. Examples of the water-soluble high molecular weight dispersing agent may further include other water-soluble high molecules such as methyl cellulose, ethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, starch, cyanoethylated starch, polyvinyl alcohol, casein, polyvinyl ether, polyethylene glycol, gum arabi, polyvinyl pyrrolidone, and the like, which may be used alone or in combination. In the present invention, it is preferred to use an anionic water-soluble high molecular dispersing agent from the standpoint of effectively suppressing the granular growth of the nickel. The anionic dispersing agent has anionic groups such as sulfonic acid group, phosphoric acid group or like groups. However, those dispersing agents having anionic groups other than carboxylic acid groups such as sulfonic acid group or phosphoric acid group, may contaminate the graphite granules. It is therefore desired to use dispersing agents having carboxylic anionic groups. The high molecular dispersing agent may have other hydrophilic groups such as hydroxyl group, ether group, ester group and like groups. When expressed as a mol number per unit weight, the concentration of the carboxyl groups in the water-soluble high molecular dispersing agent should range from 100 to 1200 millimols/100 g, and particularly from 200 to 1000 millimoles/100 g. When the concentration of the carboxyl groups lies outside the above-mentioned range, little suppression of a granular growth of the nickel layer effect is exhibited. The molecular weight of the dispersing agent should be as great as what is generally regarded to be high, such as 1000 or greater and, particularly, 2000 or greater. The counter ions of the anionic water-soluble high molecular dispersing agent, i.e., cations constituting the base, may be any cations. From the standpoint of preventing the graphite granules from being contaminated and of improving heat resistance and durability, however, the cations should desirably be those of an ammonium salt or an amine salt. Even when adhered to the film, the cations of these salts easily diffuse upon heating and do not contaminate graphite granules. Examples of the amine component of the salt include alkylamines such as trimethylamine, triethylamine and n-butylamine, and alcoholamines such as 2-dimethylamino ethanol, diethanolamine, triethanolamine, aminomethylpropanol and dimethylaminomethylpropanol. There can further be used polyhydric amines such as ethylene diamine, diethylene triamine, and the like. There can further be preferably used an amine having a branched-chain alkyl group and a heterocyclic amine. Examples of the amine having branched-chain alkyl group include branched-chain alkylamines having 3 to 6 carbon atoms such as isoamylamine and, particularly, 3 to 4 carbon atoms such as isopropylamine, sec-butylamine, tert-butylamine, and the like. Examples of the heterocyclic amine include saturated heterocyclic amines having a nitrogen atom such as pyrrolidine, piperidine, morpholine, and the like. Ammonia and amines should desirably be used in amounts of at least 0.3 chemical equivalent and, particularly, in amounts of from 0.7 to 1.3 chemical equivalent with respect to the carboxyl groups of the dispersing agent. In the film of the present invention, graphite should exist in an amount of from 5 to 70% by weight and, preferably, in an amount of 10 to 50% by weight with respect to the whole amount. When the amount of graphite is smaller than the above-mentioned range, the film loses lubricating property. When the amount of graphite exceeds the above range, on the other hand, the film becomes brittle and loses abrasion resistance. Examples of graphite include a variety of natural graphites and synthetic graphites. Generally, however, it is desired to use a natural graphite having a grain size of from 0.3 to 90 µm. When the grain size is smaller than the above range, the granules tend to be coagulated. When the particle size is greatar than the above range, on the other hand, the film adheres less intimately to the metal and becomes brittle. Most preferably, the graphite should have a particle size within a range or from 0.3 to 20 µm. The graphite should not be reduced by more than 50% by weight when it is exposed to the open air and heated at 550°C for 24 hours, from the standpoint of maintaining lubricating property of the film despite the lapse of time. Loss of graphite granules due to oxidation is greatly affected by the presence of alkali metals, alkaline earth metals, metal oxides or metal salts that are contained in graphite since they work as a catalyst. The life of the film can be extended by using graphite granules which are highly purified to contain ash components in amounts smaller than 100 ppm. The matrix may be made of nickel or a nickel-based alloy comprising chiefly nickel. An example of the nickel-based alloy may be the one which consists of nickel and at least one of such alloy elements as P, B, Co, Mo, Cr, W and Fe. These alloy elements may be contained in amounts of 0 to 40% by weight and, particularly, in amounts of 0.2 to 30% by weight with respect to the alloy. A preferred alloy is a nickel-phosphorus alloy in which the atomic ratio of nickel to phosphorus ranges from 99.5 : 0.5 to 80 : 20 (on the basis of weight). This nickel-phosphorus alloy exhibits particularly excellent abrasion resistance. The dispersion coating bath employed in the present invention contains the above-mentioned nickel or nickel-based alloy component, graphite and dispersing agent as essential components. As the plating bath, there can be used any known bath such as Watts bath, sulfamic acid bath or chloride bath. In this case, an Ni-P alloy-plated film can be formed if phosphorous acid, hypophosphorous acid or salts thereof are added to the plating bath. The plating bath may, of course, be blended with a variety of plating additives which are known per se. , such as a variety of surfactants and, particularly, nonionic surfactants in order to improve dispersing property of the graphite. The dispersing agent should be used in an amount or 2 to 50 parts by weight and, particularly, 5 to 30 parts by weight with respect to 100 parts by weight or graphite that is used. A representative example of the plating bath composition is described below. Component General range Preferred range Water-soluble nickel salt 50 to 300 g/l 100 to 200 g/l Phosphorous acid 0 to 40 g/l 3 to 10 g/l Boric acid 0 to 80 g/l 20 to 50 g/l Dispersing agent 0.1 to 25 g/l 0.5 to 12 g/l Surfactant 0 to 20 mg/l 3 to 10 mg/l Graphite 3 to 50 g/l 10 to 40 g/l pH 1.5 to 4 2 to 3.5 To effect the dispersion coating, the mold to be treated is immersed in the plating bath in a manner that the mold serves as a cathode and a nickel rod serves as an anode, and an electric current is permitted to flow to form a predetermined film. The current density `should generally range from 0.5 to 10 A/dm² and, particularly, from 1 to 8 A/dm². The voltage for plating should be so selected as to create the above current density, and generally ranges from 0.5 to 5 V. In order that the film contains graphite in large and uniform amounts, the surface of the mold to be coated is placed on the lower side with respect to the anode to utilize the sedimentation tendency of graphite granules for codeposition. In order that the interior of cavity of the mold is uniformly plated (codepositon), the plating operation is carried out while shaking the mold up and down with the anode as a center. Furthermore, the stirring operation is intermittently carried out since the graphite granules precipitate little if the liquid continues to flow. It is further recommended to disperse the deposited graphite granule layer at predetermined time intervals since an increase in the deposited amount of graphite granules due to precipitation makes the formation of a dense film difficult. This is accomplished by effecting the above stirring operation. According to the present invention, the graphite-dispersed nickel film on the inner surface of the mold should usually have a thickness of from 10 to 600 µm. When the thickness is smaller than 10 µm, the film is not desirable from the standpoint of durability. When the thickness is greater than 600 µm, on the other hand, difficulty is involved from the standpoint of forming the film and from an economical point of view. According to the present invention as described above, the graphite-dispersed nickel film plated on the inner surfaces of the mold, i.e., formed on the surfaces of which the molten glass comes in contact, comprises matrix of nickel or a nickel-based alloy which as a whole has a flake-like form that is continuous and exists in the form of open cells and graphite granule phase that is held in the open cells and is outwardly exposed on the surface. In accordance with the invention at least 50 number percent of the flakes are not more than 20µm long when measured in the film plane or normal to the plane. Preferably at least 20 number percent of the flakes are not more than 10µm long when measured in the film plane or normal to the plane. Moreover nickel or the nickel-based alloy should occupy 20 to 70% of the area on the cross section of the film. The lubricating property of graphite is strongly exhibited in the direction of plane of the carbon 6-member ring (generally, in the direction of the plane of a crystal). At least 50 number % of the graphite granules should have an angle of inclination of the graphite plane of less than 30% from the film surface. Such a film can be easily formed by precipitating the graphite and by preventing the graphite from coagulating. Next, working examples of the present invention will be described. (Examples) (Mold Example 1) A mold was dewaxed with a 1,1,1-trichloroethane, electrolytically dewaxed in an electrolytic dewaxing solution containing 40 g of sodium hydroxide per liter at a temperature of 50°C with a cathode current density of 5 A/dm² for one minute, washed with water, and was then washed with an acid by immersing it in a 5% hydrochloric acid solution at room temperature for 5 seconds. After further washing with water, the mold was set horizontally in a plating bath having a pH of 2.5, a temperature of 65°C and the below-described bath composition and graphite such that the inner surface (to be plated) of the mold facing upwards. An anode nickel rod located at the center of the inner surface of the semi-cylindrical mold, and the plating was effected with a current density of 5 A/dm² for 30 minutes. While the plating was being effected, the plating bath was stirred at a speed of revolution of 600 rpm for three seconds. The stirring was then discontinued for 15 seconds. The above stirring operations were repeated. Furthermore, the mold was tilted by 45 degrees toward the right with the anode as a center when the stirring was effected. At the following stirring, the mold was so tilted that the inner surface thereof faced upwards and at the next stirring, the bold was then tilted by 45 degrees toward the left. Thus, the mold was intermittently and reciprocally turned from the rightwardly tilted angle of 45 degrees to the leftwardly tilted angle of 45 degrees in a manner of 45 degrees toward the right, 0 degree, 45 degrees toward the left, 0 degree in synchronism with the stirring operation. Moreover, a homogenizer was applied to the plating bath in order to prevent graphite from coagulating. Plating bath. Bath composition Hexahydrated nickel sulfate 200 g/l (118 g/l) Hexahydrated nickel chloride 100 g/l (55 g/l) Boric acid 40 g/l Phosphorous acid 5 g/l Carboxymethyl cellulose 2.5 g/l ACNA SD-1 (Okuno Seiyaku Co.) 7 ml/l Graphite 25 g/l Values in parentheses represent those reckoned as anhydrates. Graphite Average particle size 5 µm Ash 50 ppm Iron content 30 ppm or smaller Alkali metal + alkaline earth metal 10 ppm or smaller (Mold Example 2) The mold was dewaxed with a 1,1,1-trichloroethane, polished on its surfaces to be plated with emery, and was set horizontally in the plating bath having the same bath composition, and graphite conditions as those of Mold Example 1. The inner surface of the mold faced upwards and the anode nickel rod was located at the center of the inner surfaces of the semi-cylindrical mold. The mold was plated with a current density of 5 A/dm² for 30 minutes while stirring the pacing bath at a speed of revolution of 800 rpm maintaining an on-off interval of 3 seconds on and 15 seconds off and tilting the mold in synchronism with the stirring operation in the same manner as in Mold Example 1. Further, the homogenizer was applied, prior to effecting the plating. (Mold Example 3) The plating was effected under the same conditions, i.e., same pretreatment, bath composition, graphite conditions as those of the Mold Example 1, with the exception of employing a current density of 1 A/dm² for a period of 150 minutes. (Mold Example 4) The plating was effected under the same conditions as those of Mold Example 1 but changing the stirring and mold revolution interval into a 3 second-on-5 second-off cycle. (Mold Example 5) The pretreatment was carried out under the same conditions as in Mold Example 1, and the plating was effected, in a plating bath having a pH of 3, a temperature of 55°C and the below-described bath composition (homogenized prior to effecting the plating) and graphite under the same conditions (stirring, stirring and mold interval, current density and time) as those of Mold Example 1. Plating bath. Bath composition Hexahydrated nickel sulfate 160 g/l (94 g/l) Hexahydrated nickel chloride 120 g/l (66 g/l) Boric acid 40 g/l Phosphorous acid 5 g/l Polyvinyl alcohol 2 g/l SD-1 (Okuno Seiyaku Co.) 7 ml/l Graphite 30 g/l Graphite Average particle size 3 µm Ash 70 ppm Iron content 30 ppm or smaller Alkali metal + alkaline earth metal 10 ppm or smaller (Mold Example 6) The pretreatment was carried out under the same conditions as in Mold Example 1, and the plating was effected under the following plating conditions by setting the mold in the plating bath having the below-described bath composition, conditions and graphite in the same manner as in Mold Example 1. Plating bath. Bath composition Hexahydrated nickel sulfate 180 g/l (106 g/l) Hexahydrated nickel chloride 40 g/l (22 g/l) Boric acid 40 g/l Phosphorous acid 7 g/l Methyl cellulose 2.5 g/l SD-1 (Okuno Seiyaku Co.) 7 ml/l Graphite 20 g/l Bath condition. Bath temperature 60°C Bath pH 2.5 Homogenized in advance Graphite Average particle size 10 µm Ash 40 ppm Iron content 30 ppm or smaller Alkali metal + alkaline earth metal 10 ppm or smaller Plating condition Stirred at 700 rpm maintaining an interval of 3 second-on and 10 second-off cycle. Mold rotated Tilted intermittently toward the right and left by 45 degrees like in Mold Example 1, and the plating was effected for 37 minutes. (Comparative Mold Example 1) The plating was effected under the same pretreatment, bath composition and graphite conditions as those of Mold Example 1 but continuously tilting the mold by 45 degrees toward the left and right (5 rpm). (Comparative Mold Example 2) The plating was effected under the same pretreatment and graphite conditions as those of Mold Example 1 but employing the following plating bath composition. Plating bath. Bath composition Hexahydrated nickel sulfate 200 g/l (118 g/l) Hexahydrated nickel chloride 100 g/l (55 g/l) Boric acid 40 g/l Phosphorous acid 5 g/l SD-1 (Okuno Seiyaku Co.) 7 ml/l Graphite 25 g/l Bath temperature 60°C Bath pH 2.5 (Comparative Mold Example 3) The plating was effected under the same pretreatment, plating bath composition and graphite conditions as those of Comparative Mold Example 2, but effecting the stirring at 850 rpm and maintaining a stirring and mold rotating interval of 4 second-on and 15 second-off cycle. (Comparative Mold Example 4) The plating was effected under the same pretreatment, plating bath composition and graphite conditions as those of Mold Example 5, but without effecting the homogenization. (Comparative Mold Example 5) The plating was effected under the same pretreatment, plating bath composition and plating conditions as those of Mold Example 5 but using graphite that is described below. Graphite Average particle size 3 µm Ash 9000 ppm containing Fe₂ 2600 ppm SiO₂ 4500 ppm Al₂ 900 ppm CaO 400 ppm MgO 300 ppm SO₄ 300 ppm The results obtained are tabulated below.

Claims: A mold for molding glass the inner surfaces of the mold being coated with a film of nickel or nickel based alloy chiefly comprising nickel and with graphite granules, the film comprising a matrix of nickel or nickel based alloy with graphite granules outwardly exposed on the film surface characterised by the nickel or nickel based alloy being present in the form of flakes forming a matrix of open cells with graphite received in the cells, at least 50 number percent of the flakes being not more than 20µm long when measured in the plane of the film or normal to the plane. A mold as claimed in claim 1 wherein at least 20 number percent of the flakes are not more than 10µm long when measured in the film plane or normal to the plane. A mold as claimed in claim 1 wherein the nickel or nickel based alloy occupies 20 to 70% of the cross sectional area of the film. A mold as claimed in claim 1 wherein at least 50 number percent of the graphite granules have an angle of inclination of the graphite plane of less than 30 degrees from the film plane. A mold as claimed in claim 1 wherein the graphite contains less than 100ppm by weight of ash component. A method of producing a mold for molding glass comprising immersing the mold in a coating bath containing a solution of a water soluble nickel salt with graphite dispersed therein with the mold as a cathode and nickel metal as an anode and passing an electric current to precipitate nickel and graphite on the mold, characterised by the presence in the bath of a water-soluble high molecular weight dispersing agent thereby suppressing growth of dispersively plated nickel or nickel based alloy in the film in the film plane or normal to the film. A method as claimed in claim 6 wherein the dispersing agent is water soluble ammonium salt of an anionic high molecular weight dispersing agent. A method as claimed in claim 6 wherein the dispersing agent is an ammonium salt of a carboxymethyl cellulose. A method as claimed in any one of claims 6 to 8 wherein the graphite is treated with the dispersing agent. A method as claimed in any one of claims 6 to 9 wherein the graphite contains less than 100ppm by weight ash components.

Inventors: KOBAYASHI AKIRA, SANO HIROKI, SASAKI TATEYUKI, KOBAYASHI, AKIRA, SANO, HIROKI, SASAKI, TATEYUKI
Applicants: TOYO SEIKAN KAISHA LTD, TOYO SEIKAN KAISHA LIMITED
Application year: 1992
Main classification: C03B9
IPC codes: C25D15, C03B9