Process for producing polycarbonate

Abstract: The present invention refers to a process for producing a polycarbonate by transesterification, which comprises reacting a dihydroxyl compound with a diester of carbonic acid in a reactor made of stainless steel and treated by electropolishing on a surface part thereof to contact the reactants.

Description: The present invention relates to a process for producing a polycarbonate by transesterification, particularly a process for producing a polycarbonate, by which a polycarbonate which has little colored and an enhanced molecular weight can be obtained. Polycarbonate is a general-purpose engineering thermoplastic excellent in mechanical properties, optical properties and heat resistance, and is used in extensive fields such as injection molding resin, sheet substitutive for window glass, etc. Polycarbonate has hitherto been produced by interfacial polycondensation or transesterification. Interfacial polycondensation method has widely been utilized in the general production of polycarbonates. However, it is disadvantageous in that toxic phosgene must be used and that the polymer produced by this method is colored when it was molded at high temperatures due to the residual chlorine ion present in the formed polycarbonate. In order to solve these problems, Japanese Patent Laid-Open No. 182336/1988 disclosed a process for producing a polycarbonate by using trichloromethyl chloroformate, which is liquid and a dimer of phosgene instead of toxic phosgene. However, dihydric phenols referred to therein as a starting material are limited to 9,9-bis(4-hydroxyphenyl)fluorenes which are special compounds as a dihydric phenol, so that the process disclosed therein cannot be thought to be a general-purpose process. On the other hand, in Angew. Chem. Vol. 99, Page 922 (1987) and German Patent DE 3440141, a process for producing a polycarbonate from 2,2-bis(4-hydroxyphenyl)propane by using triphosgene instead of toxic phosgene is disclosed. In this process, however, phosgene is generated in the course of reaction. As an example of the methods using transesterification, US Patent No. 4,345,062 discloses a process which comprises synthesizing a prepolymer from diphenyl carbonate and an aromatic dihydroxy compound by heating under reduced pressure in the presence of a transesterification catalyst while distilling out formed phenol, and heating the obtained prepolymer to 270°C or above finally in a high vacuum while distilling out formed phenol to obtain a high molecular weight polycarbonate. This process is advantageous in that it uses no toxic phosgene, the removal of the residual chlorine ion is unnecessary, and the reaction can be carried out in a mode of melt-polycondensation. On the other hand, this process has been known to be disadvantageous in that it generally requires a high reaction temperature of, for example, 270°C or above because polycarbonate increases its melt viscosity to a great extent as its molecular weight increases, unlike other engineering plastics, and that it necessitates a vacuum as high as 10 -2 Torr because of distilling out formed phenol having a high boiling point. For these requirements in this process, the industrialization thereof is difficult from the standpoint of equipment. Further, the hue and physical properties of the obtained polycarbonate are adversely affected by the phenol remaining therein and due to the high reaction temperature. Moreover, the transesterification method has not yet given a polycarbonate of high molecular weight. In spite of the above disadvantages, many studies have been made on the transesterification method, because the method is an industrially economical process which can give a polycarbonate by melt-polycondensation. Particularly, it has been suggested that the material of the reaction vessel used exerts an influence to the coloration of the product. Namely, in Japanese Patent Laid-Open No. 142025/1980, it is suggested that, when stainless steel is used as the material for constructing the reactor used in the preparation of polycarbonate by the transesterification method, the formed polycarbonate is apt to be colored and a polymer of high molecular weight is difficult to obtain, so that the production of a polymer excellent in both properties and color cannot be achieved. Further, the inventors of the present invention found that when a carbon steel or a stainless steel was used as such as the material of the reactor used in the preparation of polycarbonate by transesterification method using a transesterification catalyst, the molecular weight of polycarbonate could not be enhanced enough with the reproducibility thereof being poor and the obtained polycarbonate was significantly colored. To overcome these problems, it has been proposed in U.S. Patent No. 4383092 that the coloration of the product is inhibited by using tantalum, nickel or chromium as the material of the reactor. However, a reactor made of only these metals is too expensive to be practical in this respect. In Japanese Patent Laid-Open No. 72327/1992, published on March 6, 1992, the use of a reactor made of a material comprising Cu and/or Ni in an amount of 85% by weight or above is proposed. Further, in Japanese Patent Laid-Open No. 124934/1990, the use of a reactor made of glass and a stirrer made of nickel is mentioned and in Japanese Patent Laid-Open No. 153923/1990, the use of glass, nickel, tantalum, chromium or polyfluoroethylene as the material of the reactor is mentioned. With the aim of overcoming the above-mentioned faults of transesterification method, a variety of catalysts have also been studied (Japanese Patent Laid-Open No. 142025/1980, for example). However, none of these catalysts can simultaneously fulfil the requirements concerning the properties and color of polycarbonate. It is therefore the object of the present invention to provide an industrial process for producing a polycarbonate having high molecular weight and free from coloration with a high efficiency. This object has been achieved with a process for producing a polycarbonate by transesterification, which comprises reacting a dihydroxyl compound with a diester of carbonic acid in a stainless steel reactor, characterized in that the reactor is treated by electropolishing on a surface part thereof to contact the reactants. In this process, the transesterification is preferably carried out in the presence of (a) a nitrogen-containing, electron-donating compound or (b) a nitrogen-containing, electron-donating compound and an alkali metal compound or an alkaline earth metal compound. Next, the process for producing polycarbonate by transesterification, which comprise reacting reactants in a reactor which is made of stainless steel and treated on a surface part thereof to contact the reactants will be described in detail. These processes are industrially practicable and satisfying the economic requirements since stainless steel is generally usable and inexpensive. The conventional process for the production of polycarbonate using a reactor made of stainless steel by transesterification has a tendency to give yellow or brown products. This coloring might be presumed to result from the acceleration of thermal decomposition and side reaction of the reactants at high temperature by the interaction of a metal component in stainless steel with a transesterification catalyst, though the factors thereof are not apparent. However, the processes of the present invention surprisingly give a colorless and transparent polycarbonate having a high molecular weight by using a reactor which is made of stainless steel and treated by electropolishing. The stainless steel to be used in these invention includes SUS 304, SUS 304 L, SUS 316, SUS 316 L and the like, though it is not restricted to them. The term "electropolishing" used herein means a method for polishing a surface to give a glossy surface by the anodic reaction by using an electrolytic solution which preferentially dissolves minute projections present on the anodic metal surface rather than minute recesses. As the electrolytic solution, a mixture of sulfuric acid or perchloric acid, phosphoric acid, ethanol and glycerol can be referred to. The reactor according to the present invention is treated by the above-described method on a surface part thereof to contact the reactants. Namely, the reactor has a electropolished inner wall where the reactants contact it. In the present invention the herein mentioned additives can be used in combination with the above-described treated reactor for transesterification. At least the surface of the additive is made of a substance which will be explained later. In the present invention, a variety of compounds can be used as the dihydroxy compound. For example, bis(hydroxyaryl)alkanes, bis(hydroxyaryl)arenes, bis(hydroxyaryl)cycloalkanes, dihydroxydiaryl ethers, dihydroxydiaryl sulfides, dihydroxydiaryl sulfoxides, dihydroxydiaryl sulfones, etc., can be used. Among these compounds, preferable dihydroxy compounds are those represented by the following general formulas (I), (II) (III), (IV), (V), (VI) and (VII): wherein R 1 , R 2 , R 3 , R 4 , R 5 and R 6 , which may be the same or different, each represent a hydrogen atom, an alkyl group, a cycloalkyl group, an aralkyl group or an aryl group; X 1 , X 2 , Y 1 , Y 2 , Y 3 , Z 1 and Z 2 , which may be the same or different, each represent a halogen atom, an alkoxy group, an alkyl group, a cycloalkyl group, an aralkyl group or an aryl group; l, m, n, p, q, r and s each represent an integer of 0-4; and t represents an integer of 2-10. wherein R 7 , R 8 , R 9 , R 10 and R 11 each represent a hydrogen atom, a straight-chain or branched alkyl group having 1 to 8 carbon atoms or a phenyl group; X 3 represents a halogen atom; u is 0 to 4; and v is 1 to 4. Examples of the alkyl group include straight-chain or branched alkyl groups such as methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group, t-butyl group, n-pentyl group, isopentyl group, neopentyl group, hexyl group, heptyl group, octyl group, 2-ethylhexyl group, decyl group, undecyl group, dodecyl group and the like, among which preferable alkyl groups are straight-chain or branched alkyl groups having about 1 to 8 carbon atoms. Examples of the cycloalkyl group include cyclopropyl group, cyclopentyl group, cyclohexyl group, cycloheptyl group, cyclooctyl group and the like. Examples of the aralkyl group include benzyl group, phenethyl group, benzhydryl group and the like. Examples of the aryl group include phenyl group, naphthyl group, anthryl group and the like, among which a preferable aryl group is phenyl group. The halogen atom includes fluorine atom, chlorine atom, bromine atom and iodine atom. The alkoxy group includes methoxy group, ethoxy group, n-propoxy group, isopropoxy group, n-butoxy group, isobutoxy group, pentyloxy group, hexyloxy group and the like. The alkyl group, the cycloalkyl group, the aryl group and the aralkyl group may have one or more substituents inert under the conditions of the transesterification reaction. Examples of such substituent include a halogen atom, an alkoxy group, an aryloxy group, an aralkyloxy group, an alkylthio group, a cyano group, a nitro group and the like. As the substituents R 1 to R 6 , a hydrogen atom, an alkyl group (particularly those having 1 to 8 carbon atoms) and an aryl group (particularly a phenyl group) are preferred. As the substituents X 1 , X 2 , Y 1 , Y 2 , Y 3 , Z 1 and Z 2 , an alkyl group (particularly those having 1 to 8 carbon atoms), an aryl group (particularly a phenyl group) and a halogen atom are preferred. Preferable examples of the dihydroxy compound include 2,2-bis(4-hydroxyphenyl)propane, 2,2-bis(4-hydroxyphenyl)butane, 2,2-bis(4-hydroxyphenyl)-4-methylpentane, 2,2-bis(4-hydroxyphenyl)octane, 4,4'-dihydroxy-2,2,2-triphenylethane, 2,2-bis(3,5-dibromo-4-hydroxyphenyl)propane, 2,2-bis(4-hydroxy-3-methylphenyl)propane, 2,2-bis(4-hydroxy-3-isopropylphenyl)propane, 2,2-bis(4-hydroxy-3-sec-butylphenyl)propane, 2,2-bis(3,5-dimethyl-4-hydroxyphenyl)propane. 2,2-bis(4-hydroxy-3-tert-butylphenyl)propane. 1,1'-bis(4-hydroxyphenyl)-p-diisopropylbenzene, 1,1'-bis(4-hydroxyphenyl)-m-diisopropylbenzene, 1,1-bis(4-hydroxyphenyl)cyclohexane and the like. These dihydroxy compounds can be used either alone or in combination of two or more members among them for the production of a copolycarbonate. Examples of the diester of carbonic acid include bisaryl carbonates such as diphenyl carbonate, bis(2,4-dichlorophenyl) carbonate, bis(2,4,6-trichlorophenyl) carbonate, bis(2-cyanophenyl) carbonate, bis(o-nitrophenyl) carbonate, ditolyl carbonate, m-cresyl carbonate, dinaphthyl carbonate, bis(diphenyl) carbonate and the like; dicycloalkyl carbonates such as dicyclohexyl carbonate and the like; and dialkyl carbonates such as dimethyl carbonate, diethyl carbonate and the like. Among these, bisaryl carbonates are preferable, and diphenyl carbonate is particularly preferred. The diester of carbonic acid is used in an amount equimolar to that of the dihydroxyl compound present in the reaction system. Generally, 1 mol of a carbonate compound must be reacted with 1 mol of a dihydroxyl compound in order to form a high-molecular weight polycarbonate. When a bisaryl carbonate is used as the diester of carbonic acid, two molecules of a monohydroxyl compound are liberated by the above-mentioned reaction. According to the present invention, this monohydroxyl compound is distilled out of the reaction system. However, in the industrial process of the prior art, an excess of a diester of carbonic acid is reacted with a dihydroxyl compound. Therefore, the amount of the diester of carbonic acid which is used as a starting material is usually 0.90 to 1.50 mol, preferably 0.95 to 1.25 mol, and still preferably about 1.00 to 1.10 mol, per mole of the dihydroxy compound as other starting material. The substance according to the present invention is one which contains iron in an ammount of 50% by weight or less. The substance may be broadly classified into four groups, i.e., inorganic material, organic material, metal and metal alloy. The metal alloy may be further classified into three groups, i.e., one containing iron in ammount of from 20% to 50% by weight, one containing iron in ammount of from 20% to 40% by weight and one containing iron in ammount of 20% by weight or less. Examples of the inorganic material include silicates such as SiO 2 glass and opaque mullite; oxides such as beryllium oxide, magnesium oxide, spinel and aluminum oxide; carbides such as silicon carbide, boron carbide and tungsten carbide; nitrides such as silicon nitride and boron nitride; borides such as titanium boride; silicides such as molybdenum silicide; and carbons such as graphite. Examples of the inorganic material also include ceramics which exhibit excellent thermal resistance, and examples of the ceramics include oxides ceramics such as aluminium oxide, magnesium oxide, spinel, beryllium oxide, partially stabilized zirconia, zirconia, high-toughness alumina, cordierite, aluminium titanate, mullite, titanium oxide, tin oxide, thorium dioxide and chromium oxide; nitride ceramics such as silicon nitride, boron nitride, aluminium nitride, titanium nitride, zirconium nitride, hafnium nitrideand sialon; carbide ceramics such as silicon carbide, boron carbide and tungsten carbide; silicate ceramics such as stone ware, porcelain, high-refractoriness porcelain and crystallized glass; carbon material such as amorphous carbon and hexagonal system graphite; boride ceramics such as titanium boride; and silicides such as molybdenum silicide. Examples of the organic material include polyfluoroethylene. The term "polyfluoroethylene" used herein means not only polyfluoroethylene alone but also polyfluoroethylene composition, i.e., a composition comprising polyfluoroethylene and other component(s). Examples of the metal include those to which no second component is added intentionally, such as Ni, Cr, Mo, Al, Cu, Zn, Co and Mn. Preferably examples of the metal include Cu, Ni, Cr and Al. The metal alloy according to the present invention includes those which contain iron in ammount of 50% by weight or less and further contain Cr and/or Co in an amount of 50% by weight or above or Al and/or Mn in an amount of 50% by weight or above. Namely, the metal alloy according to the present invention includes, for example, one which contains iron in ammount of 50% by weight or less, and Cr in an amount of 50% by weight or above; one which contains iron in ammount of 50% by weight or less, and Co in an amount of 50% by weight or above; and one which contains iron in ammount of 50% by weight or less, and Cu and Cr in a total amount thereof of 50% by weight or above. The metal alloy according to the present invention includes those which contain iron in ammount of 40% by weight or less and further contain Ni and/or Cr in an amount of 60% by weight or above, Ni and/or C in an amount of 60% by weight or above, Ni and/or Mo in an amount of 60% by weight or above, Ni and/or Al in an amount of 60% by weight or above, Ni and/or Cu in an amount of 60% by weight or above, Cu and/or Al in an amount of 60% by weight or above or Cu and/or Zn in an amount of 60% by weight or above. According to the present invention, a colorless transparent polycarbonate having a high molecular weight is obtained when the substance is a metal alloy containing iron in ammount of 50% by weight or less and further containing Cr and/or Co in an amount of 50% by weight or above or Al and/or Mn in an amount of 50% by weight or above. The content of the total of Cr and Co, or, Al and Mn in a metal alloy is preferably 60% by weight or above, still preferably 70% by weight or above. As the examples of other metallic and nonmetallic components which the alloys can contain, W, Mo, Ti, Zr, Mn, Al, Cu, Fe, Ni, Sn, Zn, Mg, Si, C, P, S and the like can be mentioned. According to the present invention, a colorless transparent polycarbonate having a high molecular weight is obtained when the substance is a metal alloy containing iron in ammount of 40% by weight or less and further containing Ni and/or Cr in an amount of 60% by weight or above, Ni and/or C in an amount of 60% by weight or above, Ni and/or Mo in an amount of 60% by weight or above, Ni and/or Al in an amount of 60% by weight or above, Ni and/or Cu in an amount of 60% by weight or above, Cu and/or Al in an amount of 60% by weight or above or Cu and/or Zn in an amount of 60% by weight or above. A colorless transparent polycarbonate having a high molecular weight is also obtained when the metal alloy, which contains iron in ammount of 40% by weight or less, Ni and/or Cr in an amount of 60% by weight or above and Mo, is selected as the substance. In these alloys, Fe, Pb, Zn, Ti, V and the like may be incorporated as other components. If the content of above-described elements is lower than 60% by weight, the formation of high molecular weight product is obstructed, or the coloration of resin is accelerated. Cases where these "other components" are present in a minute quantity are also included in the scope of the present invention. Further, said "other components" are not limited to the above-mentioned ones. In the present invention, the substance is preferably one selected from the group consisting of metals other than iron and metal alloys containing iron in an ammount of 20% by weight or less. The metal alloy containing iron in amount of 20% by weight or less includes Ni base alloys such as Nickel 200, Nickel 201, Duranickel 301, Monel 400, Nimonic 80A, Inconel 600, Inconel 601, Inconel X-750, Incoloy 800, Inconel 625, Inconel 657, Inconel 671, Hastelloy B-2, Hastelloy C-4, Hastelloy C-276, Hastelloy G-3, Hastelloy X, Nimonic 75, Nimonic 80, Nimonic 80A, Nimonic 90, M-252 Hastelloy C, Hastelloy R-252, Hastelloy W, Hastelloy X, Inconel, Inconel X, Inconel X500, Inconel 700, Waspaloy, Udimet 500, Udimet 700, Unitemp 1753 and Rene 41; Co-Cr-Ni base alloys such as S-816, V-36, L-605, HS-25 and WF-11; Ni base casting alloys such as Hastelloy B, Hastelloy C, Hastelloy X, Inconel 713C, Udimet 500, Thetaloy and GMR-235; Co base casting alloys such as HS-21, HS-31 and HA-36; and Cu base alloys such as phosphorus deoxidized copper, beryllium copper, Admiralty brass, Naval copper, aluminum bronze and Cupronickel. Meanwhile the metal alloy containing iron in amount of from 20% to 50% by weight includes Ni base alloys such as Incoloy 825 and Co-Cr-Ni base alloys such as S-590, N-155 and HS-95. However, the substance is not restricted to them. In the present invention, as described above, it is preferred that the iron component accounts for 20% or less and a further reduced content thereof is still preferred. However, from the viewpoint of industrial profitability, a metal alloy containing the iron component within the range of the present invention is useful as a low-cost material. When the iron component accounts for more than 20% by weight, it may bring about the result that the coloring of the resin obtained by the interaction of the iron component with a catalyst or a raw material cannot be neglected. Also in view of the reaction activity of the catalyst, it may have an unfavorable tendency when the iron component accounts for more than 20% by weight. The shape and morphology of the additive is not critical. Additives made of the substance and having a form of powder, granule, rod, plate, cylinder, mass or ribbon can be used, for example. Among these forms, powdery form is particularly preferred. Additives having a surface layer of the above-described substance are also used. The amount of the additive is about 1 ppm to about 1% by weight, preferably 5 ppm to 5,000 ppm, and still preferably about 20 ppm to about 1,000 ppm, based on the total weight of the reactants. If its amount is larger than 1% by weight, the procedure for separating the additive is complicated. In the process of the present invention, the reaction is carried out usually in the presence of a transesterification catalyst. As typical examples of the transesterification catalyst, the following catalysts (A), (B), (C), (D) and (E) can be mentioned. (A) Metal-containing catalysts The metal-containing catalysts include, for example, metal borohydrides such as lithium borohydride, sodium borohydride, potassium borohydride, rubidium borohydride, cesium borohydride, beryllium borohydride, magnesium borohydride, calcium borohydride, strontium borohydride, barium borohydride, aluminum borohydride, titanium borohydride, tin borohydride, germanium borohydride and the like; metal tetraphenoxides such as tetraphenoxylithium, tetraphenoxysodium, tetraphenoxypotassium, tetraphenoxyrubidium tetraphenoxycesium and the like; sodium thiosulfate; metal oxides such as beryllium oxide, magnesium oxide, antimony trioxide, tin (IV) oxide and the like; dibutyltin oxide; metal hydroxides such as beryllium hydroxide, magnesium hydroxide, germanium hydroxide and the like; metal acetates such as beryllium acetate, zinc acetate, magnesium acetate, tin (IV) acetate and the like; metal carbonates such as lithium carbonate, sodium carbonate, potassium carbonate, beryllium carbonate, magnesium carbonate, tin (IV) carbonate, germanium carbonate and the like; metal nitrates such as tin (IV) nitrate, germanium nitrate and the like; metal phenylacetates such as zinc phenylacetate, lead phenylacetate, tin phenylacetate and the like; bismuth trimethylcarboxylate; etc. (B) Catalysts belonging to nitrogen-containing, electron-donating compounds including primary amines, secondary amines, tertiary amines, nitrogen-containing heterocyclic compounds and the like. Examples of such catalysts include N,N-dimethyl-4-aminopyridine (represented by 4-dimethylaminopyridine, hereinafter), N,N-diethyl-4-aminopyridine, 4-pyrrolidinopyridine, pyridine, 4-aminopyridine, 2-aminopyridine, 2-hydroxypyridine, 4-hydroxypyridine, 2-methoxypyridine, 4-methoxypyridine, picoline, pyrimidine, 2-dimethylaminoimidazole, 2-methoxyimidazole, 2-mercaptoimidazole, aminoquinoline, imidazole, 2-methylimidazole, 4-methylimidazole, pyrazole, benzimidazole, N,N-dimethylaniline, pyrrolidine, morphaline, N-methylmorpholine, piperidine, piperazine, 1,4-diazabicyclo[2.2.2]octane (DABCO), 1,8-diazabicyclo[5.4.0]-7-undecene (DBU), 1,5-diazabicyclo[4.3.0]-5-nonene (DBN) and the like. (C) Salts formed between the above-mentioned nitrogen-containing electron-donating compounds and acids such as carbonic acid, acetic acid, formic acid, nitric acid, nitrous acid, oxalic acid, borofluoric acid, hydrofluoric acid and the like. (D) Catalysts belonging to electron-donating phosphorus compounds Examples of such catalysts include triethylphosphine, tri-n-propylphosphine, triisopropylphosphine, tri-n-butylphosphine, triphenylphosphine, tri-o-dimethoxyphenylphosphine, tri-p-tolylphosphine, tri-o-tolylphosphine, tributyl phosphite, triphenyl phosphite, tri-p-tolyl phosphite, tri-o-tolyl phosphite and the like. (E) Catalysts belonging to borane complexes Examples of such catalysts include complexes formed between borane and ammonia, dimethylamine, trimethylamine, triethylamine, t-butylamine, dimethylaniline, pyridine, dimethylaminopyridine, morpholine, piperazine, pyrrole, tetrahydrofuran, dimethyl sulfide, tri-n-butylphosphine, triphenylphosphine, triphenyl phosphite and the like. These transesterification catalysts may be used either alone or in the form of a mixture of two or more members among them. Among these transesterification catalysts, preferable are (a) a nitrogen-containing, electron-donating compound and (b) a mixture of a nitrogen-containing, electron-donating compound and an alkali metal compound or an alkaline earth metal compound. Among them, 2-methylimidazole, 4-dimethylaminopyridine 4-dimethylaminopyridine and a mixture of and potassium acetate are more preferable. The alkali metal compound and alkaline earth metal compound include oxides, hydroxides, organic acid salts, carbonates, hydrogencarbonates, thiosulfates, borohydrides and the like of alkali metals and alkaline earth metals. As the examples of such compounds, the compounds which have been mentioned in paragraph (A) and fulfil the conditions of this paragraph can be referred to. The amount of the transesterification catalyst may be any so long as the polycondensation reaction is not disturbed by its use. For example, the catalyst is used in an amount of 10 -7 to 10 -1 mol, preferably about 10 -5 to 10 -1 mol, more preferably about 10 -5 to 10 -2 mol, most preferably about 10 -4 to 10 -2 mol, per mole of the dihydroxy compound. If the amount of the catalyst is smaller than 10 -7 mol per mole of the dihydroxy compound, the rate of polymerization reaction forming polycarbonate is low because the catalytic activity is low. If the amount of the catalyst is larger than 10 -1 mol, the catalyst remains in the formed polycarbonate to deteriorate the properties of the polycarbonate. The transesterification reaction is carried out usually at a temperature of about 100°C to 300°C, preferably at about 130°C to 280°C. If the reaction temperature is lower than 100°C, the reaction velocity is low. If the reaction temperature is higher than 300°C, side reactions readily take place. It is also possible to carry out the reaction according to the conventional procedure adopted in melt-polycondensation reactions, i.e. by carrying out the early stage of the reaction at 100°C to 250°C, preferably at about 130°C to 230°C, and thereafter elevating the temperature while reducing the pressure, and finally carrying out the reaction at about 250°C to 300°C. Preferably, the pressure at the completing of the reaction is 0.3 Torr or below, for example. The polycarbonate obtained according to the process of the present invention has a high molecular weight and is freed from coloration and excellent in mechanical and electrical properties, heat resistance, transparency and light resistance. Thus, it can be used as electronic and electric parts, mechanical parts, structural materials, films, sheets, containers, etc. According to the process of the present invention, a transesterification reaction between a dihydroxy compound and a diester of carbonic acid is carried out in a stainless steel reactor treated by electropolishing on a surface part thereof to contact the reactants. Therefore, there can be obtained a colorless, transparent polycarbonate which is freed from coloration in spite of its high molecular weight. The present invention will now be described by referring to the following Examples, though the present invention is not limited to them. In the Example and Comparetive Examples, the viscosity-average molecular weight ( M v) of a polymer was determined by measuring the intrinsic viscosity [η] of a methylene chloride solution of a polycarbonate sample at 20°C with a Ubbellohde viscometer, followed by calculation according to the following equation: [η] = 1.11 × 10 -4 ( M v) 0.82 . The hue of a polymer was evaluated by determining the absorbances of a 10% solution of a polycarbonate sample in methylene chloride at wavelengths of 380 nm and 580 nm with an UV spectrophotometer and calculating the difference between the absorbances. A greater value means a higher extent coloration. Example 1 The following reaction was carried out in a reactor made of stainless steel (SUS316) and the liquid contacting part thereof having been electropolished. The reactor was charged with 4,566 g (20.0 mol) of bisphenol A, 4,392 g (20.5 mol) of diphenyl carbonate, 0.489 g (0.004 mol) of 4-dimethylaminopyridine and 0.039 g (0.0004 mol) of potassium acetate. After replacing the inner atmosphere with nitrogen gas. the temperature was elevated to 180°C, where the contents in the tank were molten to form a uniform mixture under stirring. Then, the temperature was slowly elevated up to 260°C, while reducing the pressure down to 2 Torr. The contents were polycondensed at the condition (260°C and 2 Torr) for 4 hours, while distilling off the phenol formed as a by-product. Thus, a polycarbonate prepolymer having a viscosity-average molecular weight of 15,000 was obtained. The polycarbonate prepolymer thus obtained was sent into a self-cleaning twin-screw extruder regulated at 280°C/0.2 Torr and having a Cr-plated liquid-contacting part, and discharged by means of a gear pump at 850 g/hr. The polymer thus obtained had a viscosity-average molecular weight ( M v) of 28,000 and its time (A 380 -A 580 ) was 0.09. Comparative Example 1 A reaction was carried out in the same manner as that of Example 1, except that the reactor was not treated by electropolishing. The polymer thus obtained had a viscosity-average molecular weight (Mv) of 21,700, and its hue (A 380 -A 580 ) was 1.17. Comparative Example 2 A reaction was carried out in the same manner as that of Example 1, except that the reactor was made of carbon steel and used as it was. The polymer thus obtained had a viscosity-average molecular weight (Mv) of 18,000, and its hue (A 380 -A 580 ) was 2.05.

Claims: A process for producing a polycarbonate by transesterification, which comprises reacting a dihydroxyl compound with a diester of carbonic acid in a stainless steel reactor, characterized in that the reactor is treated by electropolishing on a surface part thereof to contact the reactants. The process according to claim 1, wherein the transesterification is carried out in the presence of (a) a nitrogen-containing, electron-donating compound or (b) a nitrogen-containing, electron-donating compound and an alkali metal compound or an alkaline earth metal compound.

Inventors: FUKUDA YUTAKA, KANNO TATSUYA, KUWANA TAKAAKI, OKANO YOSHIMICHI, OSHINO YASUHIRO, YAMATO TSUTOMU, FUKUDA, YUTAKA, KANNO, TATSUYA, KUWANA, TAKAAKI, OKANO, YOSHIMICHI, OSHINO, YASUHIRO, YAMATO, TSUTOMU
Applicants: DAICEL CHEM, DAICEL CHEMICAL INDUSTRIES, LTD.
Application year: 1992
Main classification: C08G64
IPC codes: C08G64