Glass composition and use

Abstract: A glass composition capable of being spun into fibres has the following components expressed as weight percent: SiO₂ - 66 to 73; Al₂O₃ - 0.85 to 5; R₂O (= Na₂O + K₂O) - 14 to 17.5; CaO - 6.5 to 12; and SiO₂ + A₂O₃ - 69 to 74. The composition is free of boric oxide and consequently avoids pollution difficulties associated with that compound, yet it can be used in high temperature spinners to produce durable fibres.

Description: This invention relates to a boric oxide free glass composition capable of being spun into fibres, it also relates to a method of spinning compositions according to the invention in a spinner made from a mechanically alloyed or oxide dispersion strengthened alloy and to glass fibre insulation produced from the compositions according to the invention. Glass compositions are known for use in the technique of fiberizing glass using a centrifugal spinner. The compositions have customarily incorporated boric oxide in order to give them temperature/viscosity characteristics that will enable the glass to pass freely through orifices in the centrifugal spinner wall at a temperature sufficiently low to prevent excessive corrosion and erosion of the spinner. A problem with the use of boric oxide is that boron is volatile and may escape from the glass melting tank to cause pollution problems. Furthermore it tends to condense on regenerators thereby fouling them up and preventing use of such devices to improve the thermal efficiency of fuel fired glass melting tanks. GB 2 041 910 proposes the reduction or elimination of boric oxide with a consequent rise in liquidus temperature and high levels of alumina or baria. These reduced boric oxide compositions are acknowledged to be virtually impossible to fiberize on an industrial basis by the prior art spinning techniques. A technique involving the use of a novel spinner shape is proposed, but, in practice, the corrosion of such a spinner when fabricated from conventional alloy is unacceptably high. Also the glass compositions according to this patent have unacceptably low durability. US Patent 4 402 767 proposes a novel spinner fabrication process to produce a mechanically alloyed or oxide dispersion strengthened alloy by a combination of warm working, annealing and hot forming processes. Such spinners are claimed to have excellent resistance against molten glass attack and are said to be capable of producing glass fibres and mineral wool at temperatures as high as 1315°C. No details of glass fibre production are given in the specification. The problem has been to identify boron free glass compositions which have the required durability and can be used in high temperature spinners such as those described in US 4 402 767. Although the absence of boric oxide gives rise to a deterioration in the aqueous durability of the glass, we have identified a range of compositions for which the durability is satisfactory. According to the present invention insulating glass fibres comprise a boric oxide free glass composition spun into fibres, consisting of the following components expressed as weight percent: SiO 2 66-73 Al 2 O 3 0.8-4 R 2 O = Na 2 O+K 2 O 14-17.5 CaO 6.5-12 SiO 2 + Al 2 O 3 69-74 K 2 O 0.5-2 Na 2 O 13-16.5 and further Fe 2 O 3 , MgO and SO 3 as additional components. Such glasses have a viscosity of 1000 poise or less at temperatures up to about 1200°C and a liquidus at least 130°C below the 1000 poise temperature. The additional components may be present in the following amounts: 0-3.3% Fe 2 O 3 ; 0-5% MgO; 0-0.6% SO 3 , all expressed as weight percent. Preferably the components are present in weight percentages within the following ranges: SiO 2 67-72.4 Al 2 O 3 1-4 R 2 O 14.5-17 K 2 O 0.5-2 Na 2 O 13.5-16.5 CaO 7-11.2 Fe 2 O 3 0.1-2.5 MgO 0.2-4.4 SiO 2 + Al 2 O 3 70-73.7 Most preferably the components are present in weight percentages within the following ranges SiO 2 67-70 Al 2 O 3 2-4 Na 2 O 14-15.5 K 2 O 0.5-1.5 MgO 3-4.5 CaO 7-8.5 Fe 2 O 3 0.3-2 SO 3 0-0.3 SiO 2 + Al 2 O 3 70-72 Na 2 O + K 2 O 15-16.5 A high level of Na 2 O is needed to give a low liquidus temperature but the preferred narrow range of MgO allows the Na 2 O to be kept to a minimum so optimising durability while maintaining liquidus at least 160 centigrade degrees below the 1000 poise viscosity temperature, which is advantageously below 1170°C. The invention will now be described with reference to the following non-limiting examples 1-28. Low levels of SO 3 , K 2 O and Fe 2 O 3 are recorded as a minimum in these examples. In fact they are only present at the lower levels as impurities in the raw materials and do not make a significant contribution to the properties of the glass fibres. Details of the examples and durability tests are given in the Table. It should be noted that Example 18 falls outside the scope of the present invention as its low level of alumina renders it insufficiently durable. There is no established international test procedure for assessing the suitability of a glass for glass fibre insulation applications. It has become the practice to use the laboratory ware test of ISO 719 as it gives a useful guide to the aqueous durability and weathering resistance of the glass. In this test 2g of glass grains are treated with distilled water for 60 mins at 98°C and the extracted alkali titrated against 0.01 M HCL. The durability is described in terms of the alkali extracted per gram of glass as calculated from the acid required to neutralise. The relevant classes for glass wool are ISO Class 3 - from 62 to 264 micrograms of alkali per gram; and Class 4 - from 265 to 620 micrograms per gram. Glass wool is preferably in Class 3 but a good Class 4 may be acceptable because the performance of the insulation is a function of both glass and resin binder, and binders are available for use with higher release glasses. A class 3 rating is good and a class 4 rating is acceptable, but not as good.

Claims: Insulating glass fibres comprising a boric oxide free glass composition spun into fibres, consisting of the following components expressed as weight percent: SiO 2 66-73 Al 2 O 3 0.8-4 R 2 O = Na 2 O+K 2 O 14-17.5 CaO 6.5-12 SiO 2 + Al 2 O 3 69-74 K 2 O 0.5-2 Na 2 O 13-16.5 and further Fe 2 O 3 , MgO and SO 3 as additional components. Insulating glass fibres according to claim 1, wherein the additional components are present in the following amounts expressed as wt %. Fe 2 O 3 0-3.3 MgO 0-5 SO 3 0-0.6 Insulating glass fibres according to claim 1 or 2, wherein the components are present in weight percentages within the following ranges. SiO 2 67-72.4 Al 2 O 3 1-4 R 2 O 14.5-17 K 2 O 0.5-2 Na 2 O 13.5-16.5 CaO 7-11.2 Fe 2 O 3 0.1-2.5 MgO 0.2-4.4 SiO 2 + Al 2 O 3 70-73.7 Insulating glass fibres according to claim 3, wherein the components are present in weight percentages within the following ranges. SiO 2 67-70 Al 2 O 3 2-4 Na 2 O 14-15.5 K 2 O 0.5-1.5 MgO 3-4.5 CaO 7-8.5 Fe 2 O 3 0.3-2 SO 3 0-0.3 SiO 2 + Al 2 O 3 70-72 Na 2 O + K 2 O 15-16.5 An insulating glass fibre production process including the spinning of molten glass at a high temperature in a spinner made from a mechanically alloyed or oxide dispersion strengthened alloy to produce fibres having a composition according to any preceding claim.

Inventors: EDWARDS NORMAN ANTHONY, MASON ALLEN FRANK, SHORROCK PETER, YALE BRIAN, EDWARDS, NORMAN ANTHONY, MASON, ALLEN FRANK, SHORROCK, PETER, YALE, BRIAN
Applicants: OWENS CORNING BUILDING PRODUCT, OWENS-CORNING BUILDING PRODUCTS (UK) LIMITED
Application year: 1992
Main classification: C03C13
IPC codes: C03C13, C03C3, C03C17, C03C25, C03C6, C03C4