POLYSACCHARIDE AND PRODUCTION THEREOF

Abstract: The invention provides a polymer comprising a polysaccharide excellent in water absorbency, moisture absorbency, moisture retentivity and thickening function. The polysaccharide is produced by the fermentation in a natural or synthetic medium using alcaligenes, and has the following characteristics: (a) it is mainly constituted of rhamnose, fucose, glucose and glucuronic acid in a molar ratio of (1-4):2(1-8):(1-4); (b) its elementary analysis gives a carbon content of 36 ± 3 wt %, a hydrogen content of 7 ± 1 wt %, an oxygen content of 56 ± 4 wt %, and a content of water of crystallization of 9 - 13 %; (c) it is difficultly soluble in water, soluble in alkali, and insoluble in methanol, ethanol and acetone; (d) its UV absorption spectrum has neither an absorption (near 280 nm) characteristic of a protein (peptide) nor an absorption (near 260nm) characteristic of a nucleic acid; and (e) its IR absorption spectrum has an absorption pattern (around 800 -1200 cm⁻¹) characteristic of a polysaccharide.

Description: The present invention relates to a microorganism-derived polysaccharide and a method of producing it, further to water absorbents, moisture absorbents or humectants and thickening agents comprising mainly polysaccharide. The present invention is expected to find use in a broad range of applications including water absorbents, moisture absorbents, humectants and thickening agents such as sanitary articles and paper diapers, cosmetics and even covering humectants for the irrigation of seedlings to be used in the greening of deserts. Background Art With recent changes in life styles, the consumption of sanitary articles and paper diapers is steadily increasing. Most water absorbents, moisture absorbents or humectants and thickening agents used in sanitary articles and paper diapers are based on synthetic high polymer materials. Since currently available sanitary articles and paper diapers are of a disposabie type, they are disposed of in flush toilets and discharged into the environment. However, they are essentially not biodegradable and therefore remain in the environment for a prolonged period of time. This is not only unseemly but also deleterious to the environment. Thus, the development of alternatives that are biodegradable and which are hence compatible with the maintenance of a healthy environment is strongly desired. Similarly, with recent advances in biotechnology, attempts have been made to incorporate biomaterials in cosmetics. However, the use of such "biocosmetics" is very limited and there has been a growing need for the development of new organism-derived moisture absorbents or humectants that can be used as a base for cosmetics. Desertification is an environmental problem affecting the ecology of the entire earth. Japan is making a contribution to the greening of deserts by supplying Egypt and other such countries with synthetic high polymer water absorbents, moisture absorbents and humectants for use to retain water for irrigating seedlings. If such water absorbents, moisture absorbents or humectants are organism-derived and are biodegradable and compatible with the environment, no harm results from their use in the growing of seedlings. However, microorganism-derived biopolymers are usually expensive, in comparison with synthetic high polymers, thereby limiting the range of their utilization. In addition, there are many cases wherein synthetic high polymers are formed into various shapes after they have been dissolved or dispersed in organic solvents in commercial production. Accordingly, it is a general consideration that if microorganism-derived biopolymers are treated with an organic solvent, such functions will be impaired. Hence, the range of their application has been generally limited. If such biodegradable biopolymers which are compatible with the environment are treated with an organic solvent without any deterioration in their functions resulting therefrom, application could be envisaged in various fields, including the field of chemical industries and their use will be remarkably advantageous. Accordingly, in order for biopolymers to be formed in various shapes and to have a wide range of applications, it is essential that their properties should not be caused to deteriorate after they are dissolved or dispersed in organic solvents broadly used in the field of chemical industries. Thus, the biopolymers have come to be used as starting materials for products in various chemical industries. The object of the present invention therefore is to provide a polymer containing a polysaccharide that overcomes and eliminates the problems associated with synthetic high polymer water absorbents, moisture absorbents or humectants and which, hence, is highly biodegradable and can be used without adversely affecting the environment giving problems such as secondary pollution and which, in addition, has a high water absorption capability, moisture absorption capability, moisture retention capability and thickening capability, having resistance to organic solvents. With respect to the fermentation and production of polysaccharides, methods using saccharides (fructose and sucrose), inorganic materials and natural medium components (concretely, yeast extracts) have been reported (Japanese Patent Public Disclosure No. 291292/1990). EP-A-0 379 999 discloses a method of producing a polysaccharide having water absorption properties, moisture absorption properties and thickening properties, said polysaccharide consisting essentially of rhamnose, fucose, glucose, mannose and glucuronic acid which are present in a molar ratio of (1-10:(2-10):(4-20):(1):(1-5). Editorial Committee of Microbiological Handbook, Microbiological Handbook", 4th edition, June 15, 1966, Gihodo, p. 1377, 1382 relates to the composition of growth media for culturing microorganisms. It has also been found that said polysaccharides can be fermented and produced by adding fructose, sucrose and glucose as saccharides to natural medium components such as yeast extracts, polypeptone and CSL. It is anticipated that when natural medium components are used, components may become unhomogeneous and hence the fermentation and production of said polysaccharides may become unstable. The present inventors have conducted studies and aimed at establishing synthetic mediums which contain no natural component, are cheap to produce and have good workability. As a result, they have found that said polysaccharides can be fermented and produced by synthetic mediums comprising a saccharide, an inorganic salt, an amino acid mixed solution and a trace metal salt mixed solution. It is another object of the present invention to determine their conditions. Disclosure of the Invention The present inventors have studied in detail biopolymers having high water absorption properties, moisture retention properties, water retention properties and thickening properties relating to, for example. polysaccharides described in Japanese Patent Public Disclosure No. 291292/1990 which are dissolved or dispersed in organic solvents; namely, active components of polysaccharides described in the above patent application. Consequently, they have invented a method of producing polymers containing polysaccharides having a high moisture absorption capability, moisture retention capability, water absorption capability and thickening capability even after they are dissolved or dispersed in organic solvents and heated, and subsequently solvents are evaporated, by separating components having a molecular weight of 1 × 10 6 or more. The present invention relates to a polymer containing a polysaccharide, namely, a novel material separated from the polysaccharide described in the above patent application. More specifically, the present invention relates to a polymer containing a polysaccharide having water absorption properties, moisture retention properties, moisture absorption properties and thickening properties, which is novelly obtained by separating high molecular components alone from a polysaccharide produced by an Alcaligenes microorganism, typically Alcaligenes latus strain B-16 (FERM BP-2015). In the present invention, investigation of medium components has been carried out in the fermentation and production of said polysaccharide. As a result, it has been found that said polysaccharide can be fermented and produced according to both a natural medium using natural medium components and a synthetic medium comprising a saccharide, an inorganic salt, an amino acid mixed solution and a trace metal salt mixed solution. Brief Description of Drawings Fig. 1 is a high-performance liquid chromatography chart for the polysaccharide described in Japanese Patent Public Disclosure No. 291292/1990. The vertical axis plots the dielectric constant (×10 -1 volt) and the horizontal axis plots the retention time; Fig. 2(A), (B) (C) are high-performance liquid chromatography charts for hyaluronic acid with molecular weights of 2.3 × 10 6 , 3.0 × 10 5 and 8.4 × 10 4 respectively. The vertical axis plots the dielectric constant (×10 -2 volt) and the horizontal axis plots the retention time. Fig. 3 is a high-performance liquid chromatography chart for a polymer containing the polysaccharide of high molecular components of the present invention. The vertical axis plots the dielectric constant (×10 -2 volt) and the horizontal axis plots the retention time. Fig. 4 is an IR absorption spectrum of the material obtained in accordance with the present invention. The vertical axis plots the light transmittance (%) and the horizontal axis plots the wave number (cm -1 ). Fig. 5(A) is a high-performance liquid chromatography chart for standard samples (neutral sugars: glucose, rhamnose and fucose). The vertical axis plots the dielectric constant (×10 -2 volt) and the horizontal axis plots the retention time (×10 1 minutes). Fig. 5(B) is a high-performance liquid chromatography chart for the hydrolyzate of the material obtained in accordance with the present invention. The vertical and horizontal axes plot the same parameters as in Fig. 5(A). Fig. 6 is an HPLC chart for the hydrolyzate of the polysaccharide of high molecular components, showing that impurities are removed and the necessary part (monosaccharide) is taken out. The horizontal axis plots the retention time (minute) and the vertical axis plots the fluorescent strength. Fig. 7(A) is a graph showing the relationship between the fluorescent strength and the retention time (minute) of the standard samples. Fig. 7(B) is a graph showing the relationship between the fluorescent strength and the retention time (minute) of the hydrolyzate of the material obtained in accordance with the present invention. Fig. 8(A) shows a gas chromatography pattern of trimethylsilylated derivatives of standard samples (rhamnose, fucose, glucuronic acid and glucose). Fig. 8(B) shows a gas chromatography pattern of trimethylsilylated derivatives of the hydrolyzate of the material obtained in accordance with the present invention. In both Fig. (A) and (B), the vertical axis plots the peak height and the horizontal axis plots the retention time (minute). Fig. 9(A) shows a mass spectrum for rhamnose of trimethylsilylated derivatives of standard samples. Fig. 9(B) shows a mass spectrum for rhamnose of trimethylsilylated derivatives of the hydrolyzate of the material obtained in accordance with the present invention. In Fig. 9, the vertical axis plots the intensity and the horizontal axis plots m/e. Fig. 10(A) shows a mass spectrum for fucose of trimethylsilylated derivatives of standard samples. Fig. 10(B) shows a mass spectrum for fucose of trimethylsilylated derivatives of the hydrolyzate of the material obtained in accordance with the present invention. In Fig. 10, the vertical axis plots the intensity and the horizontal axis plots m/e. Fig. 11(A) shows a mass spectrum for glucose of trimethylsilylated derivatives of standard samples. Fig. 11(B) shows a mass spectrum for glucose of dimethylsilylated derivatives of the hydrolyzate of the material obtained in accordance with the present invention. In Fig. 11, the vertical axis plots the intensity and the horizontal axis plots m/e. Fig. 12 is an IR absorption spectrum of the polymer of low molecular components obtained in accordance with the present invention. Fig. 13 is a graph showing the relationship between the concentration and the viscosity of the aqueous solution of the material treated with an organic solvent. As controls were used a non-treated high polymer and Kelzan. The vertical axis plots the viscosity (cps) and the horizontal axis plots the polymer concentration (wt/wt%). In Fig 13, (A) shows the viscosity of Kelzan and a non-treated polymer of high molecular components, (B) that of a kerosene-treated polymer, (C) that of a xylene-treated polymer, (D) that of a trichloroethane-treated polymer, (E) that of a formamide-treated polymer and (F) that of a DMSO-treated polymer respectively. Fig. 14 shows fluidity curves for aqueous solutions of polymers. The vertical axes plot the viscosity (cps) and the horizontal axes plot the rotational speed of spindles. In Fig 14, (A) shows the viscosity of Kelzan and a non-treated polymer of high molecular components, (B) that of a kerosene-treated polymer, (C) that of a xylene-treated polymer, (D) that of a trichloroethane-treated polymer, (E) that of a formamide-treated polymer and (F) that of a DMSO-treated polymer, respectively. Fig. 15(A) and (B) show gas chromatography charts for the constituent monosaccharides of the culture products according to a natural medium and a synthetic medium, respectively. Fig. 16(A) and (B) show the relationship between the retention time and the moisture retention ratio at the relative humidity of 64.8% and 33%, respectively. Fig. 17 shows the relationship between the retention time and the moisture absorption ratio. Fig. 18 shows the relationship between the concentration and the viscosity of each thickening agent solution. Fig. 19 shows the non-Newtonian viscosity according to the relationship between the rotational speed and the apparent viscosity. Best Mode for Carrying Out the Invention The present inventors searched for a novel material having resistance to organic solvents and having water absorption properties, moisture retention properties, moisture absorption properties and thickening properties, by using the polysaccharide described in the above Japanese Patent Public Disclosure No. 1291292/1990. As a result, they have obtained a high molecular component with a molecular weight of 1 × 10 6 or more. The separation of high molecular components was carried out according to high-performance liquid chromatography (LC-6A, manufactured by Shimazu Seisakusho). As a column, a gel-filtration type, TSKG600pw × L + TSKG3000pw × L (manufactured by Toso) was used. It was carried out under the conditions of a column temperature of 40°C, a mobile phase of 0.2M, an aqueous NaCl solution and 0.5 mL/min RI. The polysaccharide of the above patent application diluted to 1000 ppm and then measured is shown in Fig. 1 and the hyaluronic acid whose molecular weight is known and which is diluted to 1000 ppm and measured is shown in Fig. 2. As shown in Fig. 1, the polysaccharide described in the above Japanese Patent Public Disclosure is composed of two polymers, each of which shows a peak at the efflux time of 21.627 minutes and at that of 32.305 minutes. The efflux time of the hyaluronic acid having a molecular weight of 2.3 × 10 6 shown in Fig. 2(A) was 23.773 minutes. Compared with the hyaluronic acid with a molecular weight of 3.0 × 10 5 shown in Fig. 2(B) and that with a molecular weight of 8.6 × 10 4 shown in Fig. 2(C), it has been revealed that the polysaccharide of the above patent application is a polymer having a molecular weight of 1 × 10 6 or more. A polymer having a molecular weight of 1 × 10 6 or more was isolated and its physical properties were examined. Consequently, it was revealed that it has remarkably high water absorption properties, moisture absorption properties, moisture retention properties and thickening properties, compared with the polysaccharide described in the above patent application, which has led to the completion of the present invention. The polysaccharide of the present invention has the following properties: (1) sugar composition as determined by thin-layer chromatography, liquid chromatography and gas chromatography: the principal constituents are rhamnose, fucose, glucose and glucuronic acid which are present in a molar ratio of (1-4):2:(1-8):(1-4); (2) elemental analysis (wt%): (said polysaccharide containing 9 - 13% of crystalline water) C: 36 ± 3 H: 7 ± 1 O: 56 ± 4; (3) solubility: slightly soluble in water (neutral); soluble in alkalies; insoluble in methanol, ethanol and acetone; (4) UV absorption spectrum no absorption detected at 280 nm characteristic of proteins (peptides) or at 260 nm characteristic of nucleic acids; and (5) IR absorption spectrum: an absorption pattern characteristic of polysaccharides is observed near 800 - 1200 cm -1 ; CH and CH 2 absorption patterns due to carbohydrates are observed near 2950 cm -1 ; and an OH absorption pattern due to carbohydrates is observed near 3400 ± 20 cm -1 . Any microorganism can be used in the present invention so far as it belongs to the genus Alcaligenes and has the ability to produce the polysaccharide of the present invention. For example, microorganisms belonging to Alcaligenes latus can be used. A concrete, preferable example is Alcaligenes latus strain B-16, which has been deposited with the Fermentation Research Institute, the Agency of Industrial Science and Technology, under accession number FERM BP-2015. The mediums found in accordance with the present invention are a natural medium employing a saccharide such as glucose, fructose, sucrose or maltose, an inorganic salt such as potassium phosphate, sodium phosphate, magnesium sulfate, magnesium chloride, sodium chloride, urea, ammonium chloride or ammonium sulfate, and a natural medium constituent such as yeast extract, peptone, polypeptone, casamino acid or CSL; and a synthetic medium using as basical medium constituents a saccharide such as glucose, fucose, lactose, sucrose or maltose, an inorganic salt such as potassium phosphate, sodium phosphate, magnesium sulfate, magnesium chloride, sodium chloride, urea, ammonium chloride or ammonium sulfate, and an amino acid mixed solution as a natural organic component, and adding a trace metal salt mixed solution and a vitamin mixed solution as a factor for the growth stabilization or the producibility stabilization. As the concentration of each medium constituent, a natural medium constituent can be used in the range of 0.1 - 1%, a saccharide in the range of 1 - 4%, an inorganic salt in the range of 0.01 - 0.1%, an amino acid mixed solution in the range of 10 - 1000 mg/L and each constituent of a trace metal salt mixed solution in the range of 0.03 - 10 mg/L. As amino acids, any amino acid can be used so far as it exists naturally. More specifically, an amino acid which is composed of at least 2 selected from Arg, Cit, Orn, Val, Ile, Met, Gly, Glu, Leu, Pro, His and Tyr can be used. They can be used singly, too. As a trace metal salt, a mixed solution composed of at least one selected from sulfate, hydrochloride and nitrate of Fe, Ca, Mn, Zn and Cu, sodium molybdate, sodium tungsten acid and sodium borate can be mentioned. More specifically, a mixture of ferrous sulfate and calcium chloride can be used. They can be used singly, too. As a vitamin mixed solution, a mixture of vitamin B, nicotinic acid, pantothenic acid, paramino benzoate, ribonic acid and biotin can be used. They can be used singly, too. The cultivation is carried out according to shake incubation or agitation incubation under aerobic conditions usually for 1 - 10 days. The cultivation temperature is preferably in the range of 15 - 40°C. pH is adjusted to 4 - 10, preferably near neutral. After the completion of the cultivation, the recovery of said polysaccharide is performed according to the ethanol precipitation described in Japanese Patent Public Disclosure No. 291292/1990. Examples Hereunder, the present invention will be explained in more detail according to Examples. Example 1 A. Recovery of polysaccharide components with a molecular weight of about 1 × 10 6 or more Sucrose (15 g), KH 2 PO 4 (6.8 g), K 2 HPO 4 (8.8 g), MgSO 4 ·7H 2 O (0.2 g), NaCl (0.1 g), urea (0.5 g) and meat extract (0.5 g) were dissolved in 1,000 mL of distilled water and the medium was adjusted to a pH of 7.4. A portion (150 mL) of the medium was transferred into a 500-mL conical flask and sterilized by autoclaving at 102°C for 15 minutes. Thereafter, a loopful of Alcaligenes latus strain B-16 (FERM BP-2015) was inoculated into the medium in the flask and subjected to rotary shaking culture at 30°C (180 rpm). After 6 days of cultivation, polysaccharide components with a molecular weight of 1 × 10 6 or more were recovered from the culture broth by the following procedure. Namely, 4,000 mL of water was added to 1,000 mL of the culture broth and the medium was adjusted to a pH of 12 with NaOH. Subsequently, the resultant medium was treated in a 1,000-mL column, Diaion HPA-75 (OH - ) (manufactured by Mitsubishi Kasei) at 8 Rv or less. Here, the removal of proteins, nucleic acids and low-molecular components was carried out. Then, the removal of cells was carried out by means of a membrane filter of a filtration auxiliary RL700 (Radiolight) + 5 µm. The cell-free liquid was neutralized to a pH of 7 with HCl and concentrated. The precipitate was recovered with two volumes of acetone. It was washed with ten volumes of acetone five times. Then, the precipitate was vacuum-dried at room temperatures to obtain a white purified high-molecular polymer. In order to determine that high-molecular components alone are separated, an HPLC chart shown in Fig. 3 was prepared. The high-molecular polymer obtained in Example 1 had the following physicochemical properties: (1) Color: white (2) Carbonization temperature: 225 - 280°C (3) Elemental analysis: Carbon and hydrogen contents were determined with a Carlo Erba C & H Analyzer. The oxygen content was calculated by subtracting the sum of C and H contents from 100 (wt%): C: 36 ± 3 H: 7 ± 1 O: 56 ± 4 (4) Solubility: Slightly soluble in water (neutral); soluble in alkalies; insoluble in methanol, ethanol and acetone (5) IR absorption spectrum: As shown in Fig. 4, an absorption pattern characteristic of polysaccharides was observed near 800 - 1200 cm -1 ; an absorption pattern characteristic of uronic acid was observed at 1620 ± 20 cm -1 ; CH and CH 2 absorption patterns due to carbohydrates were observed near 2950 cm -1 ; and an OH absorption pattern due to carbohydrates was observed near 3400 ± 20 cm -1 . These results suggest that the polymer would be an acidic polysaccharide chiefly composed of sugars and other carbohydrates. (6) Qualitative and quantitative reactions on sugars: The high-molecular biopolymer obtained in Example 1 was subjected to qualitative and quantitative reactions on sugars. In the anthrone reaction and the phenol sulfate procedure, the results were evaluated in terms of glucose. In the Elson-Morgan method, hexosamines (e.g., glucosamine and galactosamine) were used as indicators; in the periodic acid-resorcinol reaction, sialic acids (e.g. , N-acetylneuraminic acid and N-glycolylneuraminic acid) were used as indicators; and in the carbazole sulfate reaction, uronic acids (e.g., glucuronic acid and galacturonic acid) were used as indicators. The biopolymers of interest were hydrolyzed by the following scheme. The results of reactions performed on the respective samples are summarized in Table 1. Method of Hydrolyzing Polysaccharides Qualitative and Quantitative Reactions of Constituent Sugars Reaction Sugar content in each sample Anthrone reaction 76% Phenol sulfate procedure 78% Elson-Morgan - Periodic acid-resorcinol reaction - Carbazole sulfate reaction 19% In the anthrone reaction and the phenol sulfate procedure, the results were expressed in percentages in terms of glucose. In the carbazol sulfate reaction, they were expressed in terms of glucuronic acid. The results of the qualitative and quantitative reactions on sugars suggest the possibility that the biopolymers of interest have hexose and uronic acids as constituents. It is, however, clear that the biopolymers do not contain hexamines such as glucosamine or sialic acids such as N-acetylneuraminic acid. (7) Constituent sugars: Once it was established that the biopolymers of interest had sugars such as hexose and uronic acids, they were hydrolyzed with an acid such as hydrochloric acid and subjected to identification of constituent sugars by thin-layer chromatography, liquid chromatography, gas chromatography and mass spectroscopy. (A) Thin-layer chromatography A hydrolyzate of the high-molecular biopolymer obtained in Example 1 was subjected to thin-layer chromatography. Rf values of known sugars, the polysaccharide described in Japanese Patent Public Disclosure No. 291292/1990 and the hydrolyzate of the sample as obtained for various developing solvents are summarized in Table 2 (comparison of Rf values between each standard sugar and the hydrolyzate of the sample). The following conditions were used to identify constituent sugars by thin-layer chromatographic analysis. Identification of sugars by TLC Experimental conditions: 1. TLC plate α) Kiesel Gel 60 of Merck β) Silica gel 60A of Whatman 2. Developing temperature 50°C 3. Color producing agent diphenylamine-aniline-phosphate reagent 4. Developing solvent a) t-butanol/acetone/0.1M lactic acid = 4/4/2 b) isopropanol/acetone/0.1M lactic acid = 4/4/2 5. Preconditioner of TLC plate 0.5M NaH 2 PO 4 The data in Table 2 shows that the biopolymer of interest contains glucose, rhamnose, fucose and glucuronic acid since it has Rf values in agreement with those of glucose, rhamnose, fucose and glucuronic acid, as standard, and accords with the hydrolyzates of the polysaccharide described in Japanese Patent Public Disclosure No. 291292/1990 except mannose. (B) High-performance liquid chromatography The neutral sugars (rhamnose, fucose, mannose and glucose) identified by thin-layer chromatography were analyzed with high-performance liquid chromatography using Amide-80 (manufactured by Tosoh Corp.) as a column: mobile phase, acetonitrile/water = 80/20; flow rate, 1.0 mL/min.; column temperature, 80°C; detector, RI. Liquid chromatographic charts for the standard samples of the neutral sugars and the hydrolyzate of the biopolymer sample prepared in Example 1 are shown in Fig. 5(A) and Fig. 5(B), respectively. Further, the analysis was conducted by replacing the column with µ Bondasphere 5 µ, C 18 , 100A (manufactured by Waters, Inc.). The sample was derivated to a 2-aminopyridine using a fluorescent detector (EX 320 nm, Em 400 nm, GainX100, Attn 16). To 20 mL of an aqueous sample solution were added 100 mL of a mixed solution of 4.25 g of 2-AP, 12.5 mL of deionized water, 12.5 mL of methanol and 2 mL of glacial acetic acid and the mixed solution was heated at 100°C for 20 minutes. To the resultant mixture were added 100 mL of a solution of 1 g of NaBH 3 CN dissolved in 25 mL of methanol. The obtained solution was heated at 100°C for 3 hours and cooled spontaneously. Subsequently, analysis was carried out by using Ultrahydrogel 120 (manufactured by Waters, Inc.) (7.8 nm × 30 cm, mobile phase: 20 mM, ammonium acetate (pH 7.5), flow rate: 1 mL/min, room temperature). The portion shown in Fig. 6 was fractioned. Then, the hydrolyzate of the biopolymer and standard samples of glucose, rhamnose and fucose were compared by high-performance liquid chromatography using µ Bondasphere 5 µ, C 18 , 100A, 3.9 mm × 15 cm three-in-line, mobile phase: 0.1 mol, sodium citrate (pH 4.0)/acetonitrile = 99.3/0.7, flow rate: 0.3 mL/min, room temperature). The results are shown in Fig. 7(A) and (B), which reveal that both had the same retention time. The above results show that peak 1 ○ of the hydrolyzate of the biopolymer corresponds to rhamnose, peak 2 ○ to fucose, and peak 3 ○ to glucose, respectively, according to the analysis by high-performance liquid chromatography. (C) Gas Chromatography and Gas Mass Spectroscopy In order to perform a triple check on the constituent sugars identified by TLC and HPLC, the biopolymer of interest was subjected to gas chromatography and gas mass spectroscopy (GC-MS). Simultaneous analysis of neutral sugars and uronic acid (glucuronic acid) was performed by the following procedure: the sample obtained in Example 1 was hydrolyzed with HCl, silylated with a silylating agent, loaded into a gas chromatographic column (supported by Silicone OV-101), heated to a temperature in the range of 50 - 200°C, and analyzed by FID. Hydrolysis of the sample was conducted in accordance with the method of hydrolyzing polysaccharides as described above. The hydrolyzate was derivated to a trimethylsilyl form by the following scheme. Derivation to Trimethylsilyl A gas chromatographic pattern of the authentic samples of trimethylsilylated derivatives of glucose, mannose, rhamnose, fucose and uronic acid (glucuronic acid) is shown in Fig. 8(A). A gas chromatographic pattern of the hydrolyzate of the purified biopolymer obtained in Example 1 is shown in Fig. 8(B). As these figures show, the silylated derivative of the hydrolyzate of the sample of interest was in complete agreement with the silylated derivatives of glucose, rhamnose, fucose and glucuronic acid. Three peaks that were comparatively large in the gas chromatographic analysis (peak 1, rhamnose; peak 2, fucose; peak 5, glucose) were introduced into a mass spectrograph and subjected to gas mass spectroscopy (GC-MS) analysis. Fig. 9(A) and Fig. 9(B) show the mass spectra of peak 1 and rhamnose for the standard samples and the hydrolyzate of the biopolymer, respectively; Fig. 10(A) and Fig. 10(B) show the mass spectra of peak 2 and fucose for the standard samples and the hydrolyzate, respectively; and Fig. 11(A) and Fig. 11(B) show the mass spectra of peak 5 and glucose for the standard samples and the hydrolyzate, respectively. As these mass spectra show, the fragments of peaks 1, 2 and 5 are in agreement with those of the standard samples. Thus, the results of GC-MS analysis also confirm that the hydrolyzate of the biopolymer of interest contained rhamnose, fucose and glucose as constituent sugars. In summary, the results of gas chromatography (GC) and gas mass spectroscopy (GC-MS) showed that the hydrolyzate of the biopolymer of interest contained glucose, rhamnose, fucose and glucuronic acid as constituent sugars. (8) Molar ratio of constituent sugars: The molar ratio of the four constituent sugars, rhamnose, fucose, glucose and glucuronic acid, was determined from the ratio of areas of individual peaks in high-performance liquid chromatography. The conditions of HPLC were the same as those described in (7)-(B). In order to determine the molar ratio of the constituent sugars, the standard samples of specified concentrations were first subjected to HPLC and the areas of peaks obtained were determined. Then, the hydrolyzate of the purified biopolymer obtained in Example 1 (for the conditions of hydrolysis, see (6)) was subjected to HPLC and the areas of peaks obtained were determined. On the basis of the thus determined peak area, the molar ratio of the constituent sugars under consideration was calculated by means of the following equation: Molar ratio of constituent sugar = Area of hydrolyzate (constituent sugar) Peak area of standard sample × (Number of moles of standard sample) The gas chromatographic pattern of the standard samples used is shown in Fig. 7-(A) and that of the hydrolyzate of the high-molecular biopolymer obtained in Example 1 is shown in Fig. 7-(B). The areas and the number of moles of the standard samples and the hydrolyzate are shown in Table 3. Monosaccharides and Molar Ratios in 100 mL of the Hydrolyzate of the High-Molecular Polysaccharide Glucose Fucose Rhamnose Contents µg/100 mL 608.6 317.0 338.6 Molar ratio 2 1 1 B. Recovery of polysaccharide constituents with a molecular weight of about 5 × 10 4 or less Recovery of low-molecular components Elemental Analysis C H N Moisture Low-molecular polysaccharide 20.28 3.70 0.18 4.1 23.46 4.39 0.18 20.75 3.00 0.15 Further, the IR absorption spectrum of the obtained low-molecular polysaccharide is shown in Fig. 12. Example 2 The high-molecular polymer prepared in Example 1 was made into a powdery, dried material by means of a spray dryer (manufactured by Tokyo Rika, temperature at the inlet: 120°C, temperature at the crown: 80°C). 1 g of the high-molecular polymer powder was put into 1,000 mL of kerosene. It was subjected to an ultrasound homogenizer for 3 minutes so that it should be dispersed well. After it was heated at 70°C for 2 hours, it was cooled spontaneously. Then, the high-molecular polymer was precipitated to be recovered by means of a centrifuge (20,000G, 20 minutes). The resultant polymer was washed with n-hexane several times and vacuum-dried. This was used as a kerosene-treated sample. 1 g of the high-molecular polymer was put into 1,000 mL of xylene. In the same manner as in kerosene, the high-molecular polymer was dispersed and heated, recovered by means of a centrifuge, washed with acetone and vacuum-dried. This was used as a xylene-treated sample. Subsequently, in the same manner as above, the high-molecular polymer was dispersed into trichloroethane, heated, recovered by means of a centrifuge, washed with chloroform, vacuum-dried and recovered. This was used as a trichloroethane-treated sample. 1 g of the high-molecular polymer was put into 1,000 g of formamide, heated at 70°C and stirred for 2 hours. The high-molecular polymer dissolved and its viscosity increased. Subsequently, the high-molecular polymer was vacuum-dried at 70°C to evaporate formamide completely. This was used as a formamide-treated sample. Next, in the same manner as above, 1 g of the high-molecular polymer was put into 1,000 g of dimethyl sulfoxide, heated at 70°C and stirred. It dissolved in the same manner as formamide. Then, dimethyl sulfoxide was completely evaporated. The resultant product was used as a dimethyl sulfoxide-treated sample. Regarding the kerosene-treated sample, the trichloroethane-treated sample, the xylene-treated sample, the formamide (FA)-treated sample and the dimethyl sulfoxide (DMSO)-treated sample prepared in Example 2, their water absorption properties, moisture retention properties, moisture absorption properties and thickening properties were examined. Example 3 Water absorption properties were measured. A method generally referred to as a "tea bag method" was adopted. A container having a capacity of about 20 mL was made from a non-woven fabric ("Kitchen Tauper" of Tokai Pulp Co., Ltd., 100% natural pulp) and charged with a predetermined weight of a sample such as a dried polymer. Then, the container was immersed in pure water for 2 hours, recovered and left to stand for 1 hour to remove the surplus water. The dehydrated sample was put into a constant weight beaker (10 mL) and its weight after water absorption (the weight of water absorbed + sample's weight) was measured exactly. Thereafter, the sample was dried at 105°C for 15 hours to evaporate water completely. The exact weight of the sample was again measured. After these measurements, the amount of water absorption (g) per gram of the dried sample was calculated by the following equation. As comparative samples, five samples shown in Table 5 were selected. Water absorption = [weight after water absorption (g) - weight before water absorption(g)]/dried sample weight (= weight before water absorption) (g) According to Table 6, high-molecular polymers treated with an organic solvent showed high water absorption properties equal to those of non-treated ones. Comparative sample Manufacturer Remarks Silica gel Kanto Chemicals Co., Ltd. Reagent Ion-exchange resin Dow Chemical High-grade water-absorbing polymer Sumitomo Chemical Sumika Gel S-50 PVA Unitika Kasei UP-100G, 8-10 cps, partially saponified Anionic polymer Sumitomo Chemical Sumifloc FA-70 (acrylamide/acrylic acid copolymer; M-7 × 10 6 ) Example 4 Moisture absorbing capability was measured in accordance with the method described in Koshokaishi (J. of Perfume and Cosmetics), Vol. 8, No. 2, p. 131 (1984) as the following. Desiccators respectively containing a saturated solution of potassium nitrate (relative humidity: 91%), a saturated solution of sodium nitrate (relative humidity: 61.8%) and a saturated solution of magnesium chloride (relative humidity: 31.9%) were used as stored in a thermostatic chamber at 37°C. 100 mg of each dry sample were weighed precisely into a plastic cup with an inner diameter of 1.2 cm (manufactured by Sanko Plastics) and left to stand in the desiccator. After 2, 4, 6, 8 and 24 hours, the weights of the samples were measured and the percentages of moisture absorbed by these samples were determined by the following equation. Percentage of moisture absorption (%) = [(W t - W o )/W o ] × 100 W o : weight before standing W t : weight measured at given intervals As shown in Table 7, polymers treated with organic solvents showed high moisture absorption properties equal to those of non-treated ones. Relative humidity Sample Moisture absorption (%) at given intervals (hour) 2 4 6 8 10 24 48 91% High-molecular polymer 42 53 61 65 69 93 105 Kerosene-treated polymer 38 50 58 62 66 87 99 Xylene polymer 39 52 62 61 68 91 104 Trichloroethane polymer 40 53 60 62 67 89 103 61.8% FA polymer 43 51 59 65 69 87 101 DMSO polymer 41 53 60 65 69 92 105 Glycerin 33 49 61 68 76 113 140 PEG 200 27 38 45 50 55 78 92 Anionic polymer 17 28 35 41 46 64 75 Hyaluronic acid 35 61.8% High-molecular polymer 31 33 34 33 34 33 35 Kerosene-treated polymer 28 30 31 32 32 31 30 Xylene polymer 29 32 32 33 33 34 35 Trichloroethane polymer 33 34 35 35 35 35 37 FA polymer 31 32 33 33 34 35 35 DMSO polymer 32 34 34 35 35 35 36 Glycerin 23 30 33 35 36 37 38 PEG 200 18 20 20 20 20 20 22 Anionic polymer 9 13 16 21 21 22 21 Hyaluronic acid 17 31.9% High-molecular polymer 7 9 6 11 12 12 11 Kerosene-treated polymer 9 10 7 14 14 14 14 Xylene polymer 8 9 10 11 12 12 12 Trichloroethane polymer 9 10 11 12 13 14 14 FA polymer 8 9 10 13 14 14 13 DMSO polymer 7 9 10 13 14 14 14 Glycerin 6 9 11 12 13 12 12 PEG 200 3 7 7 7 7 6 7 Anionic polymer 1 1 1 2 1 3 4 Example 5 The method of measuring moisture retention capability is described in Koshokaishi, ibid . Desiccators respectively containing a saturated solution of sodium nitrate (relative humidity: 64.8%), a saturated solution of magnesium chloride (relative humidity: 33%) and phosphorus pentoxide (relative humidity: 34%) were used as stored in a thermostatic chamber at 20°C. Additional desiccators respectively containing a saturated solution of sodium sulfate (relative humidity: 64.8%) and silica gel were used as stored in a thermostatic chamber at 20°C. About 100 mg of each dry sample were weighed precisely into a plastic cup and 20 µL of water was added therein. The resultant mixture was weighed precisely again and left to stand in the desiccator. The weight of each sample after the standing was measured according to the moisture absorption test and moisture retention capability was calculated according to the following equation with the percentage of residual water being used as an index. Percentage of residual water (%) = [1 - (W o - W t )/20] × 100 W o : weight of the hydrous sample before the standing W t : weight of the hydrous sample measured at given intervals As shown in Table 8, samples treated with organic solvents showed high moisture retention capability. Relative humidity Sample Moisture absorption (%) at given intervals (hour) 2 4 6 8 10 24 48 64.8% High-molecular polymer 155 159 162 163 168 167 162 Kerosene-treated polymer 160 161 164 167 172 171 167 Xylene polymer 157 159 162 168 169 168 167 Trichloroethane polymer 158 160 164 168 170 170 165 FA polymer 159 161 163 169 171 171 163 DMSO polymer 160 161 165 170 170 169 168 Glycerin 156 178 189 195 203 207 200 PEG 200 140 141 144 146 150 151 143 Anionic polymer 96 99 103 105 111 111 105 Hyaluronic acid 105 33% High-molecular polymer 100 99 96 95 97 84 82 Kerosene-treated polymer 97 94 89 88 90 86 84 Xylene polymer 98 97 92 91 90 85 83 Trichloroethane polymer 99 98 93 92 93 86 82 FA polymer 99 97 94 91 90 84 81 DMSO polymer 100 95 92 90 89 82 82 Glycerin 79 76 72 72 74 58 55 PEG 200 66 61 57 56 58 46 43 Anionic polymer 43 37 36 35 36 33 33 34% measured under P 2 O 5 High-molecular polymer 51 32 24 26 24 26 9 Kerosene-treated polymer 56 40 36 34 34 26 17 Xylene polymer 52 38 34 29 26 25 11 Trichloroethane polymer 55 32 30 28 24 23 13 FA polymer 53 39 32 28 24 23 14 DMSO polymer 54 31 29 26 23 22 14 Glycerin 39 24 20 18 16 4 -2 PEG 200 23 12 15 19 11 14 -31 Anionic polymer 30 25 22 21 20 16 10 Example 6 The viscosity vs concentration characteristics of the polymers treated with organic solvents prepared in Example 2 were measured. As controls, the polymers containing a high-molecular polysaccharide of Example 1 and Kelzan (general-purpose xanthan gum of Kelco Co.) all particles of which passed a 28-mesh screen were used. Each of the samples and controls was dissolved in pure water at a concentration of 1% (wt/wt) and thereafter diluted with pure water at varying concentration from 0.1 to 1%. The viscosity of the respective dilutions was measured with a Brookfield type viscometer (25°C and 30 rpm on No. 2 spindle). The results are shown in Fig. 13(A) - (F). The samples treated with an organic solvent showed higher thickening effects than Kelzan as non-treated ones. Example 7 Solutions containing 2000 ppm of the polymers treated with organic solvents used in Example 2, an aqueous solution containing 200 ppm of the polymer containing a high-molecular polysaccharide of Example 1 and an aqueous solution containing 4000 ppm of Kelzan were prepared. The rotational speed of No. 2 spindle in a Brookfield type viscometer (pH 7.2 and 25°C) was varied between 6 rpm and 60 rpm and the resulting changes in the viscosity of each solution were measured. The results for the samples treated with organic solvents are shown in Fig. 14(B) - (F) and those for the non-treated sample and Kelzan are shown in Fig. 14(A), from which one can see that pseudoplastic properties are not lost by being treated with an organic solvent. Example 8 I loopful of strain B-16 grown on a buillon agar culture medium (meat extract 0.7%, peptone 1%, NaCl 0.3%, agar 2%) was inoculated into a 300-mL conical flask containing 50 mL of the medium I shown in Table 9 and cultured under shaking at 30°C for 24 hours. 10 mL of the culture broth was inoculated into a II conical flask containing 300 mL of the medium II of the following Table and cultured under shaking at 30°C for 24 hours. Subsequently, the whole culture broth was inoculated into a 5 L jar containing 2700 ml of the medium II shown in Table 9 (concentration: concentration after the inoculation) and cultured at 500 rpm with an air amount of 3 L/min, at a temperature of 30°C for 120 hours. After the completion of the culture, said polysaccharide was obtained according to the ethanol precipitation method described in Japanese Patent Public Disclosure No. 291292/1990. The dry weight was measured and 9.0 g/L of the polysaccharide was accumulated. Example 9 Strain B-16 grown on a buillon agar culture medium (meat extract 0.7%, peptone 1%, NaCl 0.3%, agar 2%) was inoculated into a 300-mL conical flask containing 100 mL of a modified culture medium of the medium II shown in Example 8 (instead of Ile, Met, Pro, Leu and His, amino acids of Ala, Ser, Gly, Val, Lys, Arg, Ile, Met, Pro, Leu, His, Glu, Thr, Asp, Cys, Phe and Trp were added at a concentration of 0.1 g/L, and the concentration of glucose was changed to 10 g/L) and cultured at a temperature of 30°C for 10 days. After the completion of the culture, said polysaccharide was obtained according to the ethanol precipitation method described in Japanese Patent Public Disclosure No. 291292/1990. The dry weight was measured and 2.5 g/L of the polysaccharide were accumulated. Example 10 Strain B-16 grown on a buillon agar culture medium (meat extract 0.7%, peptone 1%, NaCl 0.3%, agar 2%) was inoculated into a 300 mL conical flask containing 100 mL of a modified culture medium of the medium II shown in Example 8 (instead of Ile, Met, Pro, Leu, His and Tyr was added Gly at a concentration of 0.1 g/L, the concentration of glucose was changed to 10 g/L and 10 mg/L of CaCl 2 were added) and cultured at a temperature of 30°C for 10 days. After the completion of the culture, said polysaccharide was obtained according to the ethanol precipitation method described in Japanese Patent Public Disclosure No. 291292/1990. The dry weight was measured and 2.3 g/L of the polysaccharide were accumulated. As a control, culture was conducted on the culture medium except metallic salt mixtures and CaCl 2 . Only 0.5 g/L of the polysaccharide was accumulated. Example 11 Using a medium modifying the composition of the medium II of Example 8 (instead of metallic salt mixtures was added FeSO 4 ·7H 2 O at a concentration of 10 mg/L), the same test as in Example 8 was carried out. As a result, 8.9 g/L of the polysaccharide were accumulated. Example 12 Using a medium modifying the composition of the medium II of Example 8 (instead of Ile, Met, Pro, Leu, His and Tyr, amino acids of Gly, Cit, Arg, Met, Glu, and Ile were added at a concentration of 0.1 g/L, and instead of metallic salt mixtures was added FeSO 4 ·7H 2 O at a concentration of 10 mg/L), the same test as in Example 8 was carried out. As a result, 7.9 g/L of the polysaccharide were accumulated. Example 13 Using a medium modifying the composition of the medium II of Example 8 (instead of Ile, Met, Pro, Leu, His and Tyr was added Gly at a concentration of 0.6 g/L), the same test as in Example 8 was carried out. As a result, 7.7 g/L of the polysaccharide were accumulated. Example 14 Using a medium modifying the composition of the medium II of Example 8 (instead of Ile, Met, Pro, Leu, His and Tyr was added Gly at a concentration of 0.6 g/L and instead of metallic salt mixtures was added FeSO 4 ·7H 2 O at a concentration of 10 mg/L), the same test as in Example 8 was carried out. As a result, 8.9 g/L of the polysaccharide were accumulated. As a control, culture was conducted on the culture medium except FeSO 4 ·7H 2 O. Only 1.1 g/L of the polysaccharlde were accumulated. Example 15 Culture was carried out using the same procedure as in Example 9 except that fructose, sucrose or maltose was used instead of glucose in a modified culture medium of the medium II in Example 9. In the culture broths was accumulated the polysaccharide in an amount of 2.3 g/L, 2.1 g/L and 2.2 g/L, respectively. Example 16 Culture was carried out using the same procedure as in Example 9 except that the modified culture medium of the medium II of Example 9 was replaced with a modified culture medium of the medium I of Table 9 in which yeast extract was changed to polypeptone or CSL. In the culture broths was accumulated the polysaccharide in an amount of 2.1 g/L and 2.0 g/L respectively. Example 17 Culture was carried out using the same procedure as in Example 9 except that the modified culture medium of the medium II of Example 9 was replaced with a modified culture medium of the medium I of Table 9 in which glucose was changed to fructose, sucrose or maltose. In the culture broths was accumulated the polysaccharide in an amount of 1.9 g/L, 2.0 g/L and 2.1 g/L, respectively. Referential Example According to the medium I (natural medium) and the medium II (synthetic medium) of Example 8, the properties of the culture products described in Example 8 are as follows: Elemental analysis Natural medium Synthetic medium C 36.48 35.74 H 6.68 6.29 N 0.05 0.03 Protein (Lowry method) 0.7% 0.4% Nucleic acid 0.2% 0.0% Constituent sugar ratio Natural medium Synthetic medium Fucose 1 1 Rhamnose 1.8 1.7 Glucose 2.2 2.9 Glucuronic acid 1 1 Mannose 0.2 0.1 Glucuronic acid is according to a sulfate carbazole method and others according to gas chromatography. Water absorption properties Natural medium Synthetic medium Water 1.245 g 1.124 g Saline solution (0.9 wt%) 345 g 320 g Water absorbing capability A method generally referred to as a "tea bag method" was adopted. A container having a capacity of about 20 mL was made from a non-woven fabric ("Kitchen Tauper" of Tokai Pulp Co., Ltd.; 100% natural pulp) and charged with a predetermined weight of a sample such as a dried polymer. Then, the container was immersed in pure water for 2 hours, recovered and left to stand for 1 hour to remove the surplus water. The dehydrated sample was put into a constant weight beaker (10 mL) and its weight after water absorption (the weight of water absorbed + sample's weight) was measured exactly. Thereafter, the sample was dried at 105°C for 2 hours to completely evaporate the water. The exact weight of the sample was again measured. After these measurements, the amount of water absorption (g) per gram of the dried sample was calculated by the following equation: Water absorption = sample weight after absorption (g) - sample weight before absorption (g) dried sample's weight (= sample weight before absorption) (g) The gas chromatographic charts of the constituent monosaccharide of the culture products according to the above natural medium and synthetic medium are shown in Fig. 15(A) and (B) respectively. With respect to moisture retention properties, the relationship between the retention time (hour) and the retention percentage (%) is shown by the contrast between Fig. 16(A) (relative humidity: 64.8% - NaNO 3 saturated solution) and Fig. 16(B) (relative humidity: 33% - MgCl 2 saturated solution) at 20°C, sample:water = 1:10 (initial setting), known substance, wherein ○ : B-16 natural, ▵ : PVP,  : B-16 synthetic □ : Glycerin, : Urea, With respect to moisture absorption properties, the relationship between the retention time (hour) and the moisture absorption percentage (%) is shown in Fig. 17, wherein Relative humidity: 61.8% (NaNO 3 saturated solution) 37°C ○ : B-16 natural, ▵ : PVP,  : B-16 synthetic, □ : Glycerin, : Urea With respect to viscosity, the relationship between the concentration (%) and the viscosity (CPS) of each thickening agent solution is shown in Fig. 18, wherein Measurement of viscosity: Brookfield type viscometer, 30 rpm, 30°C ○ : B-16 natural,  : B-16 synthetic, : MC, ▵ : xanthan gum, □ : sodium alginate According to the measurement of the relationship between the rotational speed (rpm) and the apparent viscosity (CPS), the non-Newtonian viscosity is shown as Fig. 19, wherein Measurement of viscosity: Brookfield type viscometer, 30°C ○ : B-16 I 0.2% natural  : B-16 A 0.2% synthetic, ▵ : xanthan gum 0.5% Following are examples of the applications to which the material of the present invention may be put. Food applications : Thickeners, fillers, water retainers, texture improving agents, dietary foods; Feedstuff applications : Thickeners, fillers, water retainers carrier entrapping; Medical applications : Immunoactivators, drug entrapping (e.g., capsules and tablets); Biotechnological applications : Immobilizers for use in bioreactors, etc. , culture bases for microorganisms, plants and animal cells, supports (gels) for separation and purification; Agricultural applications : Capsules of slow release agents (e.g. agrichemicals), suspension stabilizers, emulsion stabilizers, improving adhesion, improving dust-ability, controlling the shape of liquid droplets; Civil engineering : Soil improving agents, soil water retainers, mud stabilizers, soil stabilizers; Distribution : Drip absorbents for use in foods such as fish and meat; Paper coating : Improving the performance of coatings, preventing migration, preventing streaks, preventing pigment sedimentation, improving water retention; Textile dyeing : Preventing pigment sedimentation, preventing migration, improving dye fluidity of space dyeing; Latices : Emulsion stabilizers; Cleaners : Emulsion stabilizers, suspension stabilizers, anti-sagging agents, improving sprayability; Suspension stabilizers : Stabilizing TiO 2 suspensions, stabilizing the suspensions of starch slurry; Foam stabilizers : Foamed cement; Improvement of polishing agents : Buffing agents; Paint improving agents : Improving rheological properties. Industrial Applicability As is apparent from the above, the polymer of the present invention shows an excellent water absorbing capability, moisture absorbing capability, moisture retaining capability and thickening capability even after it is dispersed or dissolved and heated in various organic solvents. Thus, since the polymer of the present invention has excellent microorganism-derived biodegradability and shows resistance to organic solvents, it is a material which has a wide range of applications in the form of synthetic high molecules and can be formed into a safe product free from secondary pollution and which has water absorption properties, water retention properties and moisture retention properties of its original properties. In addition, in the fermentation and production of polysaccharides, they can be produced by using a natural medium or a synthetic medium comprising a saccharide, an inorganic salt, an amino acid mixed solution and a trace metal salt mixed solution as medium components.

Claims: A polysaccharide having the following properties: (A) sugar composition as determined by thin-layer chromatography, liquid chromatography and gas chromatography: the principal constituents are rhamnose, fucose, glucose and glucuronic acid which are present in a molar ratio of (1-4):2:(1-8):(1-4); (B) molecular weight: 1 x 10 6 or more as determined by liquid column chromatography: (C) elemental analysis (wt%): (said polysaccharide containing 9-13% of crystalline water) C: 36 ± 3 H: 7 ± 1 O: 56 ± 4; (D) solubility: slightly soluble in water (neutral); soluble in alkalies; insoluble in methanol, ethanol and acetone; (E) UV absorption spectrum: no absorption detected at 280 nm characteristic of proteins (peptides) or at 260 nm characteristic of nucleic acids; and (F) IR absorption spectrum: an absorption pattern characteristic of polysaccharides is observed near 800 - 1200 cm -1 ; CH and CH 2 absorption patterns due to carbohydrates are observed near 2950 cm -1 ; and an OH absorption pattern due to carbohydrates is observed near 3400 ± 20 cm -1 . A polysaccharide according to Claim 1 which is chiefly composed of a treated product of a culture of an Alcaligenes microorganism. A polysaccharide according to Claim 1 or 2 wherein said Alcaligenes microorganism is Alcaligenes latus strain B-16 (FERM BP-2015). A water absorbent, a moisture absorbent, a humectant and a thickening agent which are chiefly composed of a polysaccharide according to Claims 1 - 3. A method of producing a polysaccharide according to Claims 1 to 3 by a fermentation method using a natural medium or a synthetic medium of an Alcaligenes microorganism and recovering components having a molecular weight of 1 x 10 6 or more.

Inventors: ISHINO SHUICHI, KURANE RYUICHIRO, MURATA HIDEKI, NOHATA YASUHIRO, SHIOMI MICHIO, SUGIMOTO SEIJI, YOTSUJI AKIRA, ISHINO, SHUICHI, KURANE, RYUICHIRO, MURATA, HIDEKI, NOHATA, YASUHIRO, SHIOMI, MICHIO, SUGIMOTO, SEIJI, YOTSUJI, AKIRA, KURANE, RYUICHIRO, FERM. RES. INST. OF AGENCYOF, NOHATA, YASUHIRO, CHUO KENKYUSHO OF HAKUTO CO. LTD
Applicants: HAKUTO KK, KYOWA HAKKO KOGYO KK, STATE OF JAPAN AS REPRESENTED, HAKUTO CO., LTD., KYOWA HAKKO KOGYO CO., LTD., THE STATE OF JAPAN, AS REPRESENTED BY THE DIRECTOR GENERAL OF THE AGENCY OF INDUSTRIAL SCIENCE AND TECHNOLOGY
Application year: 1992
Main classification: C08B37
IPC codes: C08B37, C12P19, B01F17