Epoxy resin powder coating composition

Abstract: A thermosetting epoxy resin powder coating composition comprising: a) an epoxy resin having at least one 1,2-epoxy group per molecule, b) isocyanuric acid, and c) 2-phenylimidazoline.

Description: The invention relates to a thermosetting epoxy resin powder coating composition capable of producing a matt finish. Matt finish is defined herein as a matt or semi matt appearance of the cured film. Matt finish films have less than 30% gloss and semi matt finish films have of from 30 to 55% gloss as determined at 60 °C according to ASTM D 523. Use of powder coating compositions is increasingly gaining interest in the coatings industry, because of positive environmental and economical aspects. Powder coating compositions are particulate compositions containing a thermosetting compound, generally an epoxy resin, a cross linking agent and additives such as pigments, dyes, fillers and levelling agents. Commonly applied curing agents in epoxy resin powder coating compositions are amines, acid anhydrides, boron trifluoride complexes, polyaminoamides, dicyandiamide or substituted and acid terminated polyesters. Such powder coating compositions generally produce glossy or semi glossy coatings. However, for some applications, for example as coating of a large surface, coatings producing a matt or semi matt finish are preferred in order to avoid undesirable or unsuitable reflections of light. US patents 3,947,384 and 4,007,299 disclose the use of curing agents comprising a salt of a polycarboxylic acid having three or more carboxyl groups (such as trimellitic anhydride or pyromellitic acid) and an imidazoline derivative (such as 2-phenylimidazoline), in epoxy resin powder coating compositions which produce a matt finish. Said salts are prepared by dissolving the polycarboxylic acid in a polar aprotic solvent, such as dimethylformamide, dimethylacetamide or N-methylpyrrolidone, and then adding the imidazoline compound in the desired molar ratio, by itself or dissolved or suspended in the same solvent, under stirring at temperatures between room temperature and 100 °C. A period of one hour for completion of the salt formation is reported. Japanese patent application No. JP 61,218,578 relates to the use of an imidazoline-isocyanuric acid adduct curing agent in epoxy resin powder coatings. It discloses the preparation of the salt of isocyanuric acid and 2-undecylimidazoline by boiling both components in a molar ratio of 1:1 for 5 minutes in water and recovering the formed adduct. This curing agent is reported to impart i.a. self extinguishing properties to the powder coating formulation. However, as for the combination of low gloss of the cured resin and high reactivity (faster cure at similar or lower temperature), a better performance is continuously being asked for. Therefore, it is an object of the invention to provide an epoxy resin powder coating composition, which enables short cure times at relatively low temperatures and produces an excellent matt or semi matt finish, whilst other favourable properties such as good flow, good storage stability, high impact resistance, good thermal resistance and non yellowing properties are being maintained. The invention provides an epoxy resin powder coating composition comprising: a) an epoxy resin having at least one 1,2 epoxy group per molecule, and as separate chemical compounds b) isocyanuric acid, and c) 2-phenylimidazoline. It was surprisingly found that the combined use of the separate chemical compounds b) and c) as curing agents in the epoxy resin powder coating composition of the invention rather than the use of salts or adducts of these compounds enables shorter cure times and produces a lower level of gloss of the coating. The composition of the invention provides low levels of gloss even without the further use of matting agents like (micro) silicic acid and talcum. The level of gloss and the reactivity of the epoxy resin powder coating composition of the invention were found to depend inter alia on the total amount of compounds b) and c) in the composition, as well as on their relative amounts. Best results are obtained with compositions comprising of from 5 to 55% by weight of c), preferably of from 20 to 35% by weight, based on the total weight of compounds b) plus c) and of from 2 to 10% by weight of compounds b) plus c), based on the weight of a). Substitution of 2-phenylimidazoline for an imidazole compound such as 2-phenylimidazole, was found to cause a significant increase of the gloss level of the cured coatings which proves the superior performance of the coating compositions of the invention. Essentially any epoxy resin having at least one 1,2-epoxy group per molecule, known in the art for use in epoxy resin powder coating formulations, may be used in the curable epoxy resin powder coating composition of the invention. However, particularly preferred are 1,2-epoxy compounds having melting ranges which start above 40 °C, including higher molecular weight compounds (so-called solid resins) and those which are solid as a result of their symmetrical structure or the size of the carbon systems bound to the 1,2-epoxy groups, as well as those which have been prepared by the reaction of liquid 1,2-epoxy compounds having more than one epoxy group per molecule with primary or secondary amines in such quantity that the adduct contains at least an average of more than one 1,2-epoxy group per molecule (so-called adduct hardeners). The 1,2-epoxy compounds may be either saturated or unsaturated and they may be aliphatic, cycloaliphatic, aromatic or heterocyclic. They may further contain substituents which under the conditions of mixture or upon cure do not cause any undesired side reactions, such as alkyl or aryl substituents, hydroxyl groups and ether groups. Of the solid resins 1,2-epoxy compounds having more than one epoxy group per molecule and an epoxy group content (EGC) of between 1000 and 2000 mmol/kg are preferred. Such as for example solid polymeric polyglycidylpolyethers of 2,2-bis(4-hydroxyphenyl)propane (bisphenol A, BPA) which are obtained for example by the reaction of epichlorohydrin in molar ratios of 1:1.9 to 1.2, in the presence of an alkali hydroxide in the aqueous medium. Polymeric polyepoxides of this kind may also be obtained through the reaction of a polyglycidylether of BPA with less than the equimolar amount of bivalent phenol, preferably in the presence of a catalyst such as a tertiary amine, a tertiary phosphine, or a quaternary phosphonium salt. The polyepoxide may also be a solid epoxidized polyester which has been obtained for example through the reaction of a polyvalent alcohol and/or a polybasic carboxylic acid or its anhydride with a low-molecular polyepoxide. Examples of such polyepoxides of low molecular weigth are the liquid diglycidylether of 2,2-bis(4-hydroxyphenyl)propane, diglycidylphthalate, diglycidyladipate, diglycidyltetrahydrophthalate, diglycidylhexahydrophthalate, diglycidylmaleate and the 3,4-epoxycyclohexylmethylester of 3,4-epoxycyclohexanecarboxylic acid. Mixtures of solid polyepoxides may also be used. Various commercially available solid epoxy resins manufactured from BPA and epichlorohydrin which have been developed especially for the production of powder coatings are EPIKOTE 3003 (EGC 1212-1397 mmol/kg), EPIKOTE 3004 (EGC 1000-1150 mmol/kg) and EPIKOTE 3002 (EGC 1450-1700 mmol/kg) (EPIKOTE is a trade mark). In order to improve the levelling characteristics of the powder coating, levelling agents may be added during preparation of the powder coating compositions. These agents may be chemical compounds or mixtures of chemical compounds of widely varying chemical structures such as polymeric or monomeric compounds, acetals such as polyvinylbutyral or polyvinylacetobutyral, ethers such as the polymeric polyethyleneglycols and polypropyleneglycols, copolymers of n-butylacrylate and vinylisobutylether, ketonealdehyde condensation resins, solid silicone resins or mixtures of zinc soaps, of fatty acids and aromatic carboxylic acids. Examples of commercially available levelling agents are e.g. Modaflow (Modaflow is a trade mark) and ACRONAL (ACRONAL is a trade mark). The amount of levelling agent added to powder coating compositions suitably lies in the range of from 1.0 to 1.5% by weight, based on the total weight of the epoxy resin powder coating composition. The powder coating composition may further comprise other components such as pigments, dyes and fillers in a wide range with respect to the amount of 1,2-epoxy resin compound(s). In order to prepare the composition of the invention compounds b) and c) can either be added seperately in either sequence or simultaneously to a). A particularly preferred way to prepare the composition of the invention is to add a physical blend of isocyanuric acid and 2-phenylimidazoline to a). Herein the term physical blend is used to indicate that the constituents of the blend have essentially the same chemical structure after blending as before i.e. the components do not react upon blending. A physical blend of the components b) and c) can suitably be prepared by blending both components in the desired ratio at room temperature for several minutes using a standard type blender and subsequently transforming the blend into a fine powder, a typical particle size being less than 120 microns. This blend is stable and may be stored for some time, typically up to 30 days, before addition of the epoxy resin component. Prior to use the components of the powder coating composition are intimately mixed, extruded and then crushed. In practice a particle size of less than 120 microns, more preferably a particle size in the range of from 30 to 100 microns is applied. The application of the powder coating composition can be accomplished by known methods e.g. by electrostatic/triboelectric spraying, fluidized bed sintering and electrostatic fluidized bed sintering. After the coating composition is applied to the object to be coated the latter is heated to a temperature in the range of from 130 °C to 210 °C, preferably of from 140 °C to 200 °C for curing. Curing may be performed in one or more cycles. The curable powder coating composition of the present invention however allows exceptionally short cure times ideally of from 5 to 10 minutes at temperatures in the range of from 160 °C to 200 °C. The invention is further illustrated by means of the following examples. General description of the methods applied: 1) Preparation of a physical blend of b) and c). Isocyanuric acid was mixed with 2-phenylimidazoline in the desired ratio, the mixture was transformed into a fine powder (particle size less than 120 micron), which can be used as such in powder coating formulations. 2) Preparation of a curable powder coating composition. If not specified otherwise the experiments were performed using the following standard epoxy resin powder coating formulation: Resin EPIKOTE 3003 (EGC 1360 mmol/kg) 900 g Curing compound variable, but if not specified otherwise 100 g Levelling agent EPIKOTE 3003-4F-10 (EGC 1230 mmol/kg) 110 g Pigment TiO 2 CL 2310, (ex KRONOS) 660 g The 1,2-epoxy compound was mixed with the desired amount of curing compound, pigment and levelling agent. This so called premix was then extrudated (e.g using a Buss PLK 46) at an extrusion temperature of around 93 °C. The extrudate was crushed and milled to a fine powder and subsequently sieved to a particle size of less than 100 microns. 3) Application of the powder coating formulation on a steel panel. The powder coating composition was sprayed on a cold rolled steel panel using an electrostatic spray gun (Gema equipment). Curing was performed at a temperature of 180 °C, for a period of time of 5 minutes if not specified otherwise. Tests were carried out on films of 50 to 60 microns thickness after 24 hour storage at 3 °C and 70% humidity. 4) Blocking resistance. The physical stability of the powders was determined by the measurement of their resistance to blocking in an air circulated oven at 40 °C for a period of 7 days. 5) Gelation time. The gelation time was measured with a "Coesfeld" geltimer using the following method: About 0.3 g of the powder coating sample was melted in a small cup which was kept at a temperature of 120, 140, 160, 180 or 200 °C. The time necessary to reach the hard-gel phase in this situation while stirring the molten powder with a wooden stick was recorded. (The hard-gel phase is the situation wherein strings are no longer formed when the wooden stick is pulled out of the stirred mass). The recorded time is a measure for the reactivity of the system. 6) Gloss values. The gloss values after cure of the powder coating composition were measured according to ASTM D523/DIN 67530 using a Byk-Mallinckrodt Multigloss type 4060 reflectometer. The instrument is standardized at 20 and 60 degrees by using a semi gloss reference panel. Examples: 1. Physical blends of isocyanuric acid and 2-phenylimidazoline in various ratios were prepared and standard epoxy resin powder coating compositions, as defined above, were prepared comprising said blends. Gloss and reactivity values of compositions 1 to 7 were determined. Results are presented in table I. Composition 1 2 3 4 5 6 7 2-phenylimidazoline, %w 0 15 20 25 28 50 100 gelation time, at 180 °C (sec.) no 34 32 34 31 19 40 cure time at 180 °C (min.) no <-----------5-----------> gloss 60°, % - 22 17 17 14 25 95 20°, % - 5 4 4 3 5 82 From table I it can be derived that the % by weight of 2-phenylimidazoline, based on the total weight of isocyanuric acid and 2-phenylimidazoline, in the composition has a large impact on the level of gloss and reactivity. Powder coating compositions of the invention 2 to 6 perform particularly well. 2. Determination of reactivity and gloss of standard epoxy resin powder coating compositions, as defined above, comprising the following curing compounds: i) a 1:1 (weight ratio) physical blend of isocyanuric acid and 2-phenylimidazoline. ii) a 1:1 (molar) adduct of isocyanuric acid and 2-phenylimidazoline, iii) a monosalt trimellitic acid and 2-phenylimidazoline. Curing compound ii) was prepared according to the method described in JP 61,218,578 and curing compound iii) was prepared as described in US patent No. 3,947,384. Results are presented in table II. Curing compound Gloss 60°, % Gelation time at 180 °C (sec) i) 25 19 ii) 45 40 iii) 19 248 Table II shows the superior performance of the powder coating composition of the invention comprising curing compound i) in respect of a combination of high reactivity and low gloss over prior art epoxy resin powder coating compositions comprising curing compounds ii) or iii). 3. Physical blends of isocyanuric acid (B) and several imidazole compounds in weight ratios of 1:1 were prepared, and standard epoxy resin powder coating compositions (as defined above) were prepared comprising said curing compounds. Gloss levels were determined. Results are presented in table III. Curing agent gloss 60°, % 2-phenylimidazole/B 80 bis(2-methyl-N-alkyl-imidazole/B 66 2-phenylimidazoline/B 25 Table III shows that undesirably high gloss levels are obtained when isocyanuric acid/imidazole physical blends are used as curing compounds. 4. Standard type epoxy resin powder coating compositions 1 to 6 were prepared by adding a physical blend of isocyanuric acid and 2-phenylimidazoline (compositions 1 to 5) as curing compound or by adding both constituents seperately to the formulation (composition 6). Composition 1 comprises 100 g of an isocyanuric acid/2-phenylimidazoline physical blend having a 2-phenylimidazoline content of 30% by weight, based on the total weight of 2-phenylimidazoline and isocyanuric acid. Composition 2 comprises 80 g of the curing compound used in composition 1. Composition 3 comprises 60 g of the curing compound used in composition 1. Composition 4 comprises 80 g of an isocyanuric acid/2-phenylimidazoline blend having a 2-phenylimidazoline content of 15% by weight, based on the total weight of 2-phenylimidazoline and isocyanuric acid. Composition 5 comprises, instead of EPIKOTE 3003, 900 g of an epoxy resin being a reaction product of bisphenol A and epichlorohydrin having an EGC of 1594 mmol/kg. Composition 6 comprises 56 g of isocyanuric acid and 24 g of 2-phenylimidazoline. Properties of compositions 1 to 6 are shown in table IV. Composition 1 2 3 4 5 6 Gel time (sec) 180 °C 21 25 52 67 61 38 Cure time (min) 8 8 13 8 8 13 Blocking no no no no - no Gloss 60°, % 17 24 14 37 16 20 20°, % 4 5 4 11 4 4 Table IV shows excellent low levels of gloss produced by the epoxy resin powder coating composition of the invention.

Claims: An epoxy resin powder coating composition comprising: a) an epoxy resin having at least one 1,2-epoxy group per molecule, and as separate chemical compounds b) isocyanuric acid, and c) 2-phenylimidazoline. A composition as claimed in claim 1 comprising of from 5 to 55% by weight of compound c) based on the total weight of compounds b) plus c). A composition as claimed in claim 2 comprising of from 20 to 35% by weight of c) based on the total weight of compounds b) plus c). A composition as claimed in any one of the claims 1 to 3 comprising of from 2 to 10% by weight of compounds b) plus c) based on the weight of a). A composition as claimed in any one of the claims 1 to 4 wherein compound a) comprises a 1,2-epoxy compound having a melting range above 40 °C. A composition as claimed in any one of the claims 1 to 5 wherein compound a) is a polyglycidylpolyether of 2,2-bis(4-hydroxyphenyl)propane having an epoxy group content of from 1000 to 2000 mmol/kg. A process for the preparation of an epoxy resin powder coating composition as claimed in any one of the claims 1 to 6 wherein compounds b) and c) are used in the form of a finely divided physical blend as hereinbefore defined.

Inventors: DE COCK CHRISTIAN JEAN CHARLES, GODTS MARIANNE NORBERTINE MARC, JONGEPIER WOUTER WILLEM, KARZIJN WILLEM, DE COCK, CHRISTIAN JEAN CHARLES, GODTS, MARIANNE NORBERTINE MARCELLA, JONGEPIER, WOUTER WILLEM, KARZIJN, WILLEM
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1992
Main classification: C08G59
IPC codes: C08G59