Stabilized aqueous solution

Abstract: A stabilized aqueous solution of a C 1 -C 5 alkyl vinyl ether and maleic acid copolymer which includes about 100 to 1,000 ppm of (1) an additive mixture of (a) about 30-70% by weight of ethylenediaminetetraacetic acid EDTA and (b) about 30-70% by weight of a secondary additive which is an organic antioxidant and/or free radical scavenger selected from t-butylhydroquinone, propyl gallate and N,N-diethylhydroxylamine; said stabilized solution exhibiting a retention of at least about 85-90% of its original viscosity after 3 months.

Description: This invention relates to the stabilization of aqueous solutions of polymers. US-A-3 531427 discloses stabilization of polybasic acid/alkyl vinyl ehter copolymer solutions by use of a mixture of EDTA and a second component. What is provided herein is a colorless, stabilized aqueous solution of a C 1 -C 5 alkyl vinyl ether and maleic acid copolymer which includes 100 to 1,000 ppm of an additive mixture of (a) 30-70% by weight of ethylenediaminetetraacetic acid and (b) 30-70% by weight of a secondary additive which is organic antioxidant t-butylhydroquinone, said stabilized solution exhibiting a retention of at least about 90% of its original viscosity after 3 months. Preferably, the stabilized solution is prepared by hydrolyzing the corresponding anhydride in the presence of said additive mixture. In one embodiment, copolymers of maleic anhydride and a C 1 -C 5 alkyl vinyl ether are dissolved in water containing 100-1,000 ppm of an additive mixture of (a) 30-70% by weight of ethylenediaminetetraacetic acid and (b) 30-70% by weight of a secondary additive which is organic antioxidant t-butylhydroquinone. The polymer reaction solution containing the predetermined additive then is hydrolyzed to the corresponding acid form of the polymer to provide the desired colorless, stabilized aqueous solution of maleic acid-C 1 -C 5 alkyl vinyl ether copolymer which includes the additive mixture. While the additive mixture could be added after hydrolysis, it is much preferred to add it directly to the anhydride copolymer before hydrolysis. In this manner, solution relative viscosities of 11-14 measured 1% in water at 25°C., are obtained for a typical high molecular weight maleic acid-C 1 -C 5 -alkyl vinyl ether copolymer instead of the value of 9 when untreated and 9-11 when the additive is included in the solution after hydrolysis. The secondary additive of the additive mixture of the invention has the following particular attributes: (1) effective in stabilizing the viscosity of the interpolymer; (2) useful in small amounts; (3) soluble in water; (4) does not discolor the solution; (5) an effective antioxidant and/or free radical scavenger; and (6) t-butylhydroquinone is suitable for use in denture adhesives and other personal care products. COMPARATIVE EXAMPLES 1. Untreated Copolymer A 1-liter resin kettle equipped with an agitator, a reflux condenser and a water bath was charged with 22.0 g. of methyl vinyl ether/maleic anhydride copolymer (Gantrez ® AN-169, International Specialty Products, Inc.) of specific viscosity of 2.83 (as determined in methyl ethyl ketone at a concentration of 1% at 25°C.) and 178.0 g. of deionized water. While agitating, the mixture was heated to 85°C. and maintained at this temperature for 1.5 hours. During this period the anhydride groups of the copolymer were converted to carboxylic acid groups generating a methyl vinyl ether/maleic acid copolymer. The clear solution which contained 13.02% solids was cooled to room temperature and maintained, in the dark, for 3 months. The stability of the solution was determined by measuring its specific viscosity (1% in H 2 O, at 25°C.) and Brookfield viscosity (Spindle # 3, 5 rpm, 25°C.). The results were the following: Time, months Spec. Viscosity Brookfield Viscosity, cps 0 9.68 2160 3 5.84 600 The data shows that a solution of methyl vinyl ether/maleic acid copolymer, which did not contain any stabilizer, deteriorated to only 40% of its initial specific viscosity, and to about 28% of its initial Brookfield viscosity, after a period of only 3 months. 2. Individual Additives To the solution prepared in Example 1, a number of different additives were added after dissolution of the polymer. The following data show the stabilizing effect of these additives: Additive/ppm Time, months Spec. Viscosity Brookfield Viscosity, cps None 0 9.68 2160 3 5.84 600 Ethylenediaminetetraacetic acid (EDTA)/200 ppm 0 9.68 2160 3 8.65 2050 t-Butyl hydroquinone (TBHQ)/500 ppm 0 9.68 2160 3 8.90 1940 N,N-Diethylhydroxylamine (DEHA)/500 ppm 0 9.68 2160 3 8.78 2000 Propyl gallate (PG)/500 0 9.68 2160 3 8.70 1900 The data above shows that the addition of a stabilizing amount of either a transition metal chelating agent, (EDTA), or of an antioxidant, (TBHQ, PG), or a radical chaser, (DEHA), substantially increased the stability of the acidic copolymer; and, particularly, it degraded to a significantly lesser degree than a nonstabilized copolymer solution of Comparative Example 1. INVENTION EXAMPLES 1. Additive Mixture After Hydrolysis To the solution of Example 1 various stabilizer blends were added. The stabilizing effect is apparent in the data in Table 3 below. Additive Blend/ppm Time, months Spec. Viscosity Brookfield Viscosity, cps None 0 9.68 2160 3 5.84 600 TBHQ/500 + EDTA/200 0 9.68 2160 3 9.00 2200 The data shows an improvement over the individual components of Comparative Example 2. Specifically, the specific viscosity of the copolymer decreased by only 7.6% and the Brookfield viscosity of the copolymer solution was substantially unchanged after standing for 3 months at room temperature. 2. Additive Mixture Before Hydrolysis A copolymer solution as in Example 1 was prepared by dissolving Gantrez® AN-169 in an additive blend of various stabilizers and water prior to beginning of heating. The acid copolymer was made by heating as in Example 1. The results are shown in Table 4 below. Additive Blend/ppm Time, months Spec. Viscosity Brookfield Viscosity, cps TBHQ/75+ 0 11.75 2800 EDTA/75 3 10.87 2900 The data above demonstrates the advantage of adding the stabilizers during dissolution of copolymer. Accordingly, both the specific viscosity and the Brookfield viscosity values of the solution were at least 90% of its initial values after 3 months, and with much higher initial and final viscosities with much lower concentrations of the mixture, than the same additive mixture used after hydrolysis.

Claims: A colorless, stabilized aqueous solution of a copolymer of a C 1 -C 5 alkyl vinyl ether and maleic acid suitable for use in denture adhesives which includes 100 to 1,000 ppm of an additive mixture of (a) 30-70% by weight of ethylenediaminetetraacetic acid and (b) 30-70% by weight of a secondary additive which is the organic antioxidant t-butylhydroquinone, said stabilized solution exhibiting a retention of at least 90% of its original viscosity after a period of 3 months. A solution according to claim 1 wherein said solution is prepared by hydrolyzing a copolymer of a C 1 -C 5 alkyl vinyl ether and maleic anhydride in the presence of said additive mixture. A solution according to claim 2 which includes about 500 ppm of said additive mixture. A solution according to claim 1 which includes about 50% each of (a) and (b).

Inventors: CHUANG JUI-CHANG, PLOCHOCKA KRYSTYNA, CHUANG, JUI-CHANG, PLOCHOCKA, KRYSTYNA
Applicants: ISP INVESTMENTS INC, ISP INVESTMENTS INC.
Application year: 1992
Main classification: C08L35
IPC codes: A61K6, C08K5