METHOD FOR PRODUCING IMAGES USING A PHOTOPOLYMERIZABLE COMPOSITION

Abstract: The present invention provides an imaging element comprising on a support transparent to actinic radiation used for exposing said imaging element in the order given a photosensitive layer containing a photopolymerizable composition and a porous layer containing pigments characterized in that the weight ratio per unit area of said photosensitive layer to said porous layer is at least 1:1. According to the method of the present invention said imaging element is information-wise exposed to actinic radiation and subsequently heated in contact with a receiving element so that the non-hardened parts of the photosensitive layer and corresponding parts of the porous layer are transferred to the receiving element. After separation of the imaging element and receiving element the receiving element is overall exposed to actinic radiation and/or heat. An image with good scratch and wear resistance is thus obtained.

Description: DESCRIPTION METHOD FOR PRODUCING IMAGES USING A PHOTOPOLYMERIZABLE COMPOSITION 1. Field of the invention. The present invention relates to an imaging element comprising a photopolymen ' zable composition and a method for imaging said imaging element using a thermal transfer step. 2. Background of the invention. The use of photopolymen ' zable compositions for the production of images by information-wise exposure thereof to actinic radiation is well known. Several methods for forming images using photopolymen ' zable compositions are known. All these methods are based on the principle of introducing a differentiation in properties between the exposed and non- exposed parts of the photopolymerizable composition e.g. a difference in solubility, adhesion, conductivity, refractive index, tackiness, permeability, diffusibility of incorporated substances e.g. dyes etc.. The thus produced differences may be subsequently employed in a developing step to produce a visible image and/or master for printing e.g. a lithographic or electrostatic printing master. According to a method disclosed in US-P-3,060,023 the adhesion of the photopolymen ' zable composition is modified upon image-wise exposure. After image-wise exposure the non-exposed parts will stick or adhere, during a step of overall heating, to a receiving sheet thus allowing the transfer of the non-exposed parts to the receiving sheet. In EP-A- 502.562 and the corresponding US-A- No. 07/836.231, and EP-A- 92201716.5 and the corresponding US-A- No. 07/897,936 a method is disclosed for obtaining an image using an imaging element comprising a photopolymerizable composition on a transparant support and a porous layer of a color pigment. After information-wise exposure said imaging element is overall heated in contact with a receiving element e.g. paper or a polyester film so that the non-exposed or insufficiently exposed parts of the photopolymerizable composition are transferred together with the pigment layer at these parts to the receiving element. According to this method black/white as well as color images of high resolution can be obtained. The thus transferred images are easily scratched so that the transferred photopolymerizable parts need to be hardened in a subsequent step of overall heating or exposure to actinic radiation. Probably due to the presence of color pigment in the transferred parts the hardening appears to be difficult and often incomplete so that the scratch and wear resistance of the image remains low. 3. Summary of the invention. It is an object of the present invention to provide a method for obtaining an image with good scratch and wear resistance using an imaging element comprising on a support in the order given a layer containing a photopolymerizable composition and a porous layer containing pigments. It is an other object of the present invention to provide an imaging element for use in said method. Further objects will become clear from the description hereinafter. According to the invention an imaging element is provided comprising on a support in the order given a layer containing a photopolymerizable composition and a porous layer containing pigments characterized in that the weight ratio per unit area of said layer containing a photopolymerizable composition to said porous layer is at least 1:1. According to the invention a method is provided for obtaining an image using the above defined imaging element. 4. Detailed description of the invention. According to the present invention an imaging element comprising in the order given on a transparant support a photosensitive layer containing a photopolymerizable composition and a porous layer containing pigments is information-wise exposed to actinic radiation preferably through the back of said support, i.e. the side of said support opposite to the side containing the photosensitive layer, and subsequently heated in contact with an image receiving element so that the non-exposed parts of the photosensitive layer are transferred to the image receiving element thereby penetrating the overlying porous layer so that the parts of said porous layer overlying said non-exposed parts of said photosensiti e layer are transferred together with said non-exposed parts of the photosensitive layer to the image receiving element. After said transfer the imaging element and receiving element are separated from each other and said receiving element is overall heated and/or exposed to actinic radiation to harden said transferred parts of said photosensitive layer. Alternatively said overall exposure may also be carried out while the imaging element and receiving element are still in contact with each other. It has now been found that an image having a good scratch and wear resistance can be obtained according to the above method when the weight ratio per unit area of said photosensitive layer to said porous layer is at least 1:1, preferably at least 2:1. When said weight ratio is less than 1:1 the scratch and wear resistance is unsatisfactory. The maximum weight ratio per unit area is not specifically limited and is determined by such factors as the absolute thickness of the photosensitive layer, composition of the photosensitive layer, composition and thickness of the porous layer, required sensitivety of the imaging element etc. A practical working range for said ratio is preferably between 1:1 and 10:1. According to the present invention the thickness of the photosensitive layer is preferably between 0.25 μm and 10 μm while the thickness of the porous layer is preferably between 0.25 μm and 2 μm. The photopolymerizable composition comprised in the photosensitive layer of the imaging element preferably contains urethane type monomers as disclosed in EP-A- 502.562 and the corresponding US-A No. 07/836.231 and DE-A-4129284.7 filed 3.9.91. These type of monomers offer the advantage that they show a rapid polymerization and solidify even at low conversions of less than 10%. Examples of urethane type monomers are: ) 2 C 2 H 5 -C[CH 2 0-C0-NH-(CH 2 )g-NH-C00-CH-(CH 2 -0-C0-C=CH 2 ) 2 ] 3 CH-: C[CH 2 0-C0-NH-(CH 2 ) 6 -NH-C00-CH-(CH 2 -0-C0-C=CH 2 ) 2 ] 4 CH. CHo C_CH 2 0-C0(CH 2 ) 5 -NH-C00-CH-(CH 2 -0-C0-C=CH 2 ) 2 ] 4 Other types of monomers suitable for use in the photopolymerizable composition used in accordance with the present invention are e.g. the monomers disclosed in DEOS no. 4.005.231, 3,516,256, 3,516.257 and 3.632.657. unsaturated esters of polyols. particularly such esters of the alpha -methyl ene carboxylic acids, e.g. ethylene diacrylate, glycerol tri(meth)acrylate, ethylene dimethacrylate, 1,3-propanediol d.(meth)acrylate 1,2,4-butanetriol tri(meth)acrylate, 1,4-cyclohexanediol di(meth)acrylate. 1,4-benzenediol di(meth)acrylate, pentaerythritol tetra(meth)acrylate, 1,5-pentanediol di(meth)acrylate, the bis acrylates and ethacrylates of polyethylene glycols of molecular weight 200-500, and the like : unsaturated amides, particularly those of the alphamethylene carboxylic acids, and especially those of alpha-omega-diamines and oxygen-interrupted omega-di amines, such as methylene bis-acrylaππ ' de, methyl ene bis-methacryl mide, 1,6-hexamethylene bis-acryl ami e, di ethyl ene triamine tris-methacryl amide, bis(gamma-methacrylamidopropoxy)ethane, beta- methacryl a idoethyl methacryl te, N-(beta-hydroxyethyl )-beta-(methacrylamido)ethyl acrylate and N,N-bis(beta-methacrylolyoxyethyl )acrylamide; vinyl esters e.g. divinyl succinate, divinyl adipate, divinyl phthalate, divinyl butane-l,4-disulfonate: and unsaturated aldehydes, e.g. sorbaldehyde (hexadienal ). The photopolymerizable composition may also comprise polymers and/or oligomers comprising 2 or more polymeπ ' zable functions e.g. acrylated epoxies, polyester acrylates, urethane acrylates etc.. It will be clear that these monomers and/or polymers and/or oligomers can be used in admixture. The photopolymerizable composition used in accordance with the present invention also comprises at least one photoinitiator. Preferably used photoinitiators are polymerization initiators activatable by actinic light and thermally inactive at and below 185°C. Examples of such initiators include the substituted or unsubstituted polynuclear quinones which are compounds having two intracyclic carbonyl groups attached to intracylic carbon atoms in a conjugated six-membered carbocyclic ring, there being at least one aromatic carbocyclic ring fused to the ring containing the carbonyl groups. Such initiators include 9-10-anthraquinone, 1-chloroanthraquinone, 2-chloroanthraquinone, 2-methylanthraquinone, 2-tert-butylanthraqufnone. octamethylanthraquinone, 1,4-naphtoquinone, 9,10-phenanthrenequinone, 1-2 benzanthraquinone, 2,3-dichloronaphthoquinone, sodium salt of anthraquinone alpha-sulfonic acid, 3-chloro-2-methyl anthraquinone, and 1,2.3,4-tetrahydrobenzene a anthracene-7,12-dione. The photointiators which are also useful are described in Plambeck U.S. Patent 2.760.863 and include vicinal ketaldonyl compounds, such as diacetyl. benzil, etc. alpha-ketaldonyl alcohols, such as benzoin, pivalon, etc. acyloin ethers e.g. benzoin methyl and ethyl ethers, etc.; alpha-hydrocarbon substituted aromatic acyloins, including mehtylbenzoin, alpha-allylbenzoin, and alpha-phenylbenzoin. Still further photoinitiators useful in accordance with the present invention are those disclosed in "Photoreactive Polymers" by Arnost Reiser, "Organic photochemical imaging systems" by G.A. Delzenne, in the paper "UV-Curing Chemistry: Past, Present, and Future" by Christian Decker, published in J. of Coatings Technology, Vol.59,N° 751. August 1987, pages 97-106. in EP-A 362,827, and in US-A 3,558,309. To further improve the scratch and wear resistance of the transferred image it has been found that the weight ratio of photoinitiator to the polymerizable compound(s) of said photosensitive layer is preferably between 1:1 and 1:10. According to the present invention thermal polymerization inhibitors may also be added to the photopolymerizable composition. Inhibitors for use in accordance with the present invention are p-methoxyphenol , hydroquinone, alkyl and acyl -substituted hydroquinones and quinones, tert-butylcatechol , pyrogallol, copper resinate, naphtylamines, beta-naphtol , cuprous chloride, 2,6-di-tert-butyl p-cresol , photothiazine, pyridine, nitrobenzene and dinitrobenzene, p-toluquinone and chloranil. According to a preferred mode of the present invention the photosensitive layer containing the photopolymerizable composition is a thermoplastic layer comprising a thermoplastic polymer. Said thermoplastic layer is preferably solid at temperatures below 40°C and is transferable in the non-exposed or insufficiently exposed parts at temperatures between 40°C and 250°C. Suitable thermoplastic polymers for use in accordance with the present invention include : (A) Copolyesters, e.g. those prepared from the reaction product of an alkylene glycol e.g. polymethylene glycol of the formula H0(CH 2 ) v 0H, wherein v is a whole number 2 to 10 inclusive, and (1) hexahydroterephthalic. sebacic and terephthalic acids, (2) terephthalic, isophthalic and sebacic acids, (3) terephthalic and sebacic acids, (4) terephthalic and isophthalic acids, and (5) mixtures of copolyesters prepared from said glycols and (i) terephthalic. isophthalic and sebacic acids and (ii) terephthalic, isophthalic, sebacic and adipic acids. (B) Nylons or polyamides, e.g. N-methoxymethyl polyhexamethylene adipamide; (C) Vinylidene chloride copoly ers. e.g. vinylidene chloπ ' de/acrylonitrile; vinylidene chloride/methylacrylate and vinylidene chloride/vinylacetate copolymers; (D) Ethyl ene/vinyl acetate copolymer; (E) Cellulosic ethers, e.g. methyl cellulose, ethyl cellulose and benzyl cellulose; (F) Polyethylene; (G) Synthetic rubbers, e.g. butadiene/acrylonitrile copolymers, and chloro-2-butadiene-l,3 polymers: (H) Cellulose esters, e.g. cellulose acetate, cellulose acetate succinate and cellulose acetate butyrate, cellulose nitrate; (I) Polyvinyl esters, e.g. polyvinyl acetate/acrylate, polyvinyl acetate/methacrylate and polyvinyl acetate; (J) PoIy(meth)acrylate and alpha-alkyl po!y(meth)acrylate esters, e.g. polymethyl methacrylate and polyvinyl acetate; (K) High molecular weight polyethylene oxides of polyglycols having average molecular weights from about 4,000 to 1,000,000; (L) Polyvinyl chloride and copolymers, e.g. polyvinyl chloride/acetate, polyvinyl chloride/acetate/alkohol ; (M) Polyvinyl acetal , e.g. polyvinyl butyral, polyvinyl formal; (N) Polyformaldehydes; (0) Polyurethanes and copolymers; (P) Polycarbonate and copolymers; (Q) Polystyrenes and copolymers e.g. polystyrene/acrylonitrile, polystyrene/acrylonit ile/butadiene. To the thermoplastic polymer constituent of the photosensitive layer there can be added non- thermoplastic polymeric compounds to give certain desirable characteristics, e.g. to improve adhesion to the support or underlying layers used in accordance with the present invention, adhesion to the receptor support on transfer, wear properties, chemical inertness, etc. Suitable non-thermoplastic polymeric compounds include polyvinyl alcohol, cellulose, anhydrous gelatin, phenolic resins and melamine-formaldehyde resins, etc. If desired, the photopolymerizable layers can also contain immiscible polymeric or non-polymeric organic or inorganic fillers or reinforcing agents which are essentially transparent at the wave-lengths used for the exposure of the photopoly eric material, e.g. the organophilic silicas, bentonites, silica, powdered glass, colloidal carbon, as well as various types of dyes and pigments in amounts varying with the desired properties of the photopolymerizable layer. The fillers are useful in improving the strength of the composition, reducing tack and in addition, as coloring agents. Agents to improve the wetting and/or adjust the adhesion of the thermoplastic layer may be added. Suitable agents are e.g. silicons, silicon containing polymers e.g. a poly(dimethylsiloxane)-polyether copolymer, poly(dimethylsiloxane)-polyester, silicon containing surfactants, fluor containing copolymers and fluor containing surfactants etc.. Various dyes, thermographic compounds, UV-absorbers, anti-oxidants and color forming components can be added to the photopolymerizable compositions to give a variety of results after the thermal transfer. These additive materials, however, preferably should not absorb excessive amounts of light at the exposure wavelength or inhibit the polymerization reaction. Among the dyes useful in the invention are Fuchsine (C.I. 42510), Auramine Base (C.I. 410003), Calcocid Green S (C.I. 44000), Para Magenta (C.I. 42500), Tryparosan (C.I. 42505). New Magenta (C.I. 42520). Acid Violet RRL (C.I. 42425). Red Violet 5RS (C.I. 42960), C.I. Solvent Blue 36 (C.I. 61551), Nile Blue 2B (C.I. 51185), New Methylene BLue GG (C.I. 51195). C.I. Basic Blue 20 (C.I. 42585. Iodine Green (C.I. 42556). Night Green B (C.I. 42415). C.I. Direct Yellow 9 (C.I. 19540). C.I. Acid Yellow 17 (C.I. 18965). C.I. Acid Yellow 29 (C.I. 18900), Tartrazine (C.I. 19140), Supramine Yellow G (C.I. 19300), Buffalo Black 10B (C.I. 27790). Naphtalene Black 12R (C.I. 20350). Fast Black L (C.I. 51215). and Ethyl Violet (C.I. 42600). Useful thermographic additives, e.g. 3 cyano-4,5-dimethyl - 5-hydroxy-3-pyrrolin-2-one, and activators, e.g. copper acetate, are disclosed in the application of Holland and Wayrynen, Ser. No.807,761. filed April 21. 1959, and the following U.S. Patents : 2,825.494. 2,637.657. 2,665.654. 2.663.655. 2.663.656, and 2,663,657. Suitable color-forming components which form colored compounds on the application of heat or when brought in contact with other color forming components in a receptor material are e.g.: (1) Organic and inorganic components : dimethyl glyoxime and nickel salts; phenolphtalein and sodium hydroxide; starch/potassium iodide and oxidizing agent, i.e. peroxides, phenols and iron salts; thioacetamide and lead acetate, silver salt and reducing agent, e.g. hydroquinone. (2) Inorganic components : ferric salts and potassium thiocyanate; ferrous salts and potassium ferricyanide; copper or silver salts and sulfide ions; lead acetate and sodium sulfide. (3) Organic components : 2,4-dinitrophenylhydrazine and aldehydes or ketones; diazonium salt and phenol or naphtol , e.g. benzenediazonium chloride and B-naphtol ; p-dimethylaminobenzaldehyde and p-diethylaminoaniline. The porous layer used in connection with the present invention is preferably free of binder but may contain small amounts of binder as long as the layer remains sufficiently porous to allow penetration by the heated photosensitive layer. Preferably the amount of binder is less than 10 % by weight. Suitable pigments for use in said porous layer include, e.g. Ti0 , colloidal carbon, graphite, phosphor particles, ceramics, clays, metal powder such as aluminium, copper, magnetic iron and bronze, etc. The present invention is especially effective in case the porous layer contains colored pigments, i.e. pigments that absorb a substantial amount of actinic radiation that may be used for the curing of the transferred image. According to a preferred mode of the present invention a base layer is provided between the support and the photosensitive layer. Said base layer preferably comprises a polymer containing polymerizable ethylenically unsaturated groups. Examples of polymers containing polymerizable ethylenically unsaturated groups for use in said base layer are polymers comprising vinyl groups, ally! groups, (meth)acrylate groups, butadiene groups, isoprene groups etc., e.g. acrylated epoxies. polyester acrylates, urethane acrylates etc.. Further additives may be added to said base layer as disclosed in EP-A-91201824.9. It is however important with respect to the present invention that the base layer is sufficiently transparant to the radiation used for exposure of the photosensitive layer. Suitable supports of the imaging element are supports that are transparant to the radiation used for exposing the imaging element and that are stable at the heating temperatures necessary for transfering the non- exposed or insufficiently exposed parts of the photopolymerizable composition to the receiving material. Examples of useful supports are e.g. polyester film supports e.g. polyethylene terephthalate. glass, cellulose esters e.g. cellulose acetate, cellulose propionate, cellulose butyrate, polycarbonate, polypropylene etc. The support of the imaging element of the present invention preferably has a thickness of 3μm to 60μm. Such is important for contact exposures but is less important for exposures with lasers because the latter can be focussed in the photosensitive layer. The receiving material to which the image is transferred must also be stable at the process temperature. The particular material used is dependant on the adhesion of the image to the support of the imaging element. Suitable receiving materials include paper, cardboard, metal sheets, foils and meshes e.g. aluminium, copper, steel, bronze etc., polyethylene, polyester film supports e.g. polyethylene terephthalate, opaque foamed or pigmented polyester, cellulose esters, silk, cotton, viscose rayon fabrics or screens, polycarbonate, polyvinyl chloride, polypropylene, polyethylene coated paper, supports provided with a thin metal layer e.g. polyester supports provided with a vapour deposited metal layer etc.. The surface of the receiving material may be a hydrophilic surface, a layer showing preferential adhesion towards the non-exposed parts of the layer containing the photopolymerizable composition or contain on its surface compounds that react with compounds being transferred so as to produce difference in color, hydrophilicity, conductivity etc. at the surface of the receiving material corresponding to the exposed and non- exposed parts. The imaging element and receiving material may also be brought in contact before exposure or may together form an integral element. Such an element is called a monosheet material. According to a practical embodiment of the present invention color images can be prepared. According to this embodiment at least three imaging elements comprising respectively a yellow, magenta and cyan dye or dye pigment in the porous layer overlying the photosensitive layer, are image-wise exposed corresponding to respectively the blue, green and red color selection of the original image. Optionally a fourth imaging element comprising a black dye or dye pigment in the porous layer can be used. Each of these imaging elements is successively heated in contact with the same receiving material e.g. a paper material to allow the transfer of each of the different color selections of the image. It is obvious that the transfer of the different color parts of the image must be carried out in register to obtain a faithful reproduction of the original image. The overall exposure to actinic radiation and/or heating according to the method of the present invention may be performed after each transfer step or only after the last color selection has been transferred. According to a further embodiment of the present invention images can be obtained using a monosheet imaging element comprising on a transparant support in the order given an optional base layer as described above, a photosensitive layer, a porous layer containing pigment and a receiving layer. After information-wise exposure of the imaging element and subsequent development by means of heating the non-hardened or insufficiently hardened parts of the photosensitive layer will penetrate into the pigment layer and will be transferred together with said pigment layer to the receiving layer. The receiving layer is e.g. paper or polyester film. By the term transferred should be understood that the photosensitive layer together with the pigment layer adheres to the receiving layer. After the thermal transfer step the receiving layer. is peeled apart from the imaging element and overall exposed to actinic radiation so that a clear image with good scratch and wear resistance is obtained. The overall exposure can also be carried out directly after the transfer step before separating the imaging element and receiving element. According to a variant of the present embodiment a layer similar to the base layer described above may be provided between the pigment layer and the image receiving layer. After information-wise exposure and heat development the imaging element according to this variant is overall exposed to actinic radiation so that the transferred parts of the photosensitive layer are hardened and the adherence of the transferred parts to the image receiving material is enhanced which facilates their peeling apart. An image with good scratch and wear resistance is also obtained. The present invention is illustrated by the following examples without however limiting it thereto. All parts are by weight unless otherwise specified. EXAMPLE 1 to 9 9 pairs of imaging elements were prepared as follows. A subbed polyethylene terephtalate support having a thickness of 100 μm was coated by means of a knife coater with a base layer of polyvinyl alcohol of which 25mol% of the hydroxyl groups were modified with methacryloyl chloride to a thickness of 1.15 g/πr (under dry conditions) and a layer comprising a photochemical imaging composition. For the pairs of imaging elements 1 to 6 said layer containing said imaging composition was coated from a solution in methyl-ethyl keton of 4% of compound n° 2 mentioned above 0.2% by weight of a blue dye (C.I. 61551), 3.7% of bis-imidazole, 0.1% of Michler's keton and 0.2% of mercaptobenzoxazole. For the pairs of imaging elements 7 to 9 the concentration of compound n°2 was 8% instead of 4%. The weigth per unit area under dry conditions of the layer containing the photochemical imaging compositions for each of the pairs of imaging elements is given in table 1 below. For each of the pairs of imaging elements the layer containing a photochemical imaging composition was overcoated with a 10% carbon black dispersion (Derusol C commercially available from Degussa A.G.. Frankfurt, Germany) to an amount of Ig/πr for all the imaging elements except for the pair of example 7 that were coated to an amount of 2g/m . Each of the thus obtained imaging elements was placed in contact with a test target and exposed therethrough to ultraviolet radiation and each was subsequently placed in face-to-face contact with a subbed polyethylene terephthalate support having a thickness of lOOμm as the receiving element. The contacting elements were conveyed through a roll lam nator device at 100°C and at a speed of 0.6 m/min. Next each of the contacting elements were peeled apart. 9 pairs of receiving elements carrying an image were thus obtained. For each pair one of the receiving elements was overall exposed to ultraviolet radiation using a Dupliphot apparatus (commercially available from Agfa-Gevaert) with an output of 300 illumination units and/or to heat by guiding the receiving element 10 times under an infrared lamp of 1200W at a distance of 1cm from said lamp and at a speed of 0.13m/s. Each of the receiving elements was then subjected to a scratch test and a friction test. The scratch test was conducted by a diamant needle loaded with a weight of 15g. The friction test was conducted by rubbing 50 times the image on the receiving element with a stamper having a diameter of 5cm and covered with a paper foil. The evaluation for both tests was done visually and a number from 0 to 3 was given to indicate the resistance of the image against scratches and wear. A large number means a weak resistance. Table 1 ratio MFM/FI scratch wear 3 3 3 3 2 3 1 3 1 3 2 0 1 0 0 2 3 2 1 2 3 3 2 0 0 2 0 1 2 3 2 1 2 0 2 3 2 2 0 0 In the above table 1 in each of the examples A represents an untreated sample, B represents a sample that has been overall exposed to U.V. radiation and C represents a sample overall exposed to U.V. and infrared radiation, FP represents the layer containing the photochemical composition, FP/C represents the weight ratio per unit area of the FP- layer to the layer containing carbon black, MFM represents the multi¬ functional monomer (compound no. 2) and FI represents the photoinitiator (Michler's keton, benzi idazole and mercaptobenzoxazole). It can be seen from the above table 1 that overall exposure of the image to U.V. and/or infrared irradiation results in an improved scratch and wear resistance when the weight ratio per unit area of the layer containing the photochemical composition to the layer containing carbon black is at least 1:1. It can further be seen that an increase in the weight ratio multi-functional monomer to initiator also improves the scratch and wear resitance of the image.

Claims: CLAIMS 1. An imaging element comprising on a support in the order given a photosensitive layer containing a photopolymerizable composition and a porous layer containing pigments characterized in that the weight ratio per unit area of said photosensitive layer to said porous layer is at least 1:1. 2. An imaging element according to claim 1 wherein said photopolymerizable composition comprises a photoinitiator and a compound having at least 2 polymerizable functions. 3. An imaging element according to claim 2 wherein the weight ratio of said compound having at least 2 polymerizable functions to said photoinitiator is between 1:1 and 10:1. " 4. An imaging element according to any of the above claims wherein the thickness of said photosensitive layer is between 0.25 μm and 10 μm and the thickness of said porous layer is between 0.25 μm and 2 μm. 5. An imaging element according to any of the above claims further comprising a base layer containing a polymer comprising ethylenically unsaturated groups between said support and said photosensitive layer. 6. An imaging element according to any of the above claims wherein said support is a polyester film support. 7. An imaging element according to any of the above claims wherein said support is transparant to actinic radiation used for exposing said imaging element and the thickness of said support is between 3μm and 60μm. 8. A method for obtaining an image comprising the steps of: - information-wise exposing to actinic radiation an imaging element as defined in any of the above claims, - heating said imaging element in contact with a receiving element, - separating said imaging element and said receiving element and - overall exposing said receiving element to heat and/or actinic radiation. 9. A method according to claim 8 wherein said imaging element and said receiving element are contacted before said information-wise exposure or form an integral element. 10. A method according to any of claims 8 or 9 wherein said receiving element is paper or a polyester film.

Inventors: PODSZUN WOLFGANG, UYTTERHOEVEN HERMAN JOZEF, PODSZUN, WOLFGANG, UYTTERHOEVEN, HERMAN, JOZEF
Applicants: AGFA GEVAERT NV, AGFA-GEVAERT NAAMLOZE VENNOOTSCHAP
Application year: 1992
Main classification: G03F7
IPC codes: G03F3, G03F7