INDUCTION FURNACE

Abstract: An improved induction furnace is described which is capable to continuously and homogeneously heat a flat product of steel industry, particularly a thin slab from a continouous casting plant, upstream of the final rolling steps during the manufacture of thin steel strips. Owing to the small thickness shown by the product to be heated a furnace of this type will have a reduced size of coils in the strip feeding direction. To avoid that under these conditions the efficiency may decrease and a great leakage flux may be established, with consequent serious drawbacks, the present invention provides for a flux concentrator formed of two continuous packets of lamination having a substantially C-shaped cross section wrapping the inductor coil both at the upper and lower side along the whole length thereof while leaving free only the passage area through which the product to be heated enters the coil.

Description: Induction furnace. The present invention relates to an improved induction furnace for heating or re-heating flat products of steel industry, particularly to re-establish a homogeneous temperature, suitable to rolling thin steel slabs. It is known from the Italian patent application No. 20534 A/89, corresponding to the International publication WO 90/14742, an induction furnace comprising an array of coils, which are separately fed by one or more frequency converters and crossed in succession by the strip being supported and caused to move forward by pairs of rollers between each coil and the subsequent one, wherein flux concentrator devices are provided, mounted in pairs at the ends of each inductor, at least on an upper or lower side, with respect to the plane defined by the strip itself. Although this solution gives best results, as it allows for the first time to exploit satisfactorily the induction heating in connection with longitudinal flat products, whereas the magnetic flux was previously mainly directed such as to cross transversely the strip in the thickness direction, with poor results but for the thermal treatment of the edges only, however some inconveniences have been experienced, mainly due to the great leakage of magnetic flux which, as it closes at the outside of the strip, crosses the structural metal parts of the apparatus , thus causing an undue heating thereof in spite of the presence of lateral flux concentrators , possibly movable. Previous ly, with longer inductors ( along the longitudinal size of the product to be heated) , as it wa.s poss ible for thicker products , the poss ible utilization of concentrators would be useless , since the little improvement in the efficiency and reduction of leakage would not be worth in comparison with the increase of costs . With a short inductor , as necessarily adopted in connection with flat products such as thin slabs , also the presence of lateral flux concentrators according to the above-mentioned previous patent does not solve the problem of flux leakage and leads to relatively low efficiencies , e . g. of 0 . 6 or less , when considering the ratio between power entering the f lat product to be heated, including losses due e . g. to radiation, and supplied active power. As a matter of fact, the longitudinal s ize of coils cannot be made too great , since to keep a reduced value of the space between two subsequent coils , above which the thin product could not be fed forward in a suitable way, a reduced diameter of the rollers would result, which is to be avoided in order not to have a too small bending radius , with consequent stumbling of the flat product and problems of heat transmiss ion . An attempt was then made to modify the mechanical parts to overcome the drawbacks caused by the flux leakage. A solution of this type requires providing rollers coated with refractory material, to prevent sparkling and consequent "dotting" on the strip, and/or making not solid rollers, but formed of isolated sectors to hinder the generation of eddy currents, or finally mounting the rollers on separate pillars, such as of concrete. This way a structure would be obtained not only more complex and costly, but also less solid and compact, certainly not so suitable to this type of processing and steel industry environment. Surprisingly it has now been found that by the use of a flux concentrator extending along the whole coil, being formed e.g. of two lamination packets having a substantially C-shaped cross section, such as to surround the induction coil at both upper and lower side with respect to the plane defined by the product to be heated, whereby only a passage for the product itself is left free, the flux leakage decreases by at least 90% and the above-mentioned efficiency may rise up to about 0.7 and more. In addition to energy saving, a mechanical structure of merely traditional construction can be obtained, i.e. sound and adapted to the steel manufacturing field, where on the contrary the induction furnaces have been usually considered in the past as something estraneous, not integrated in the solid structures adapted in that field. These and additional objects, advantages and features of the improved induction furnace according - __ - to the invention will become apparent to those skilled in the art from the following detailed description of a preferred embodiment thereof, given by way of non-limiting example with reference to the annexed drawings in which: FIGURE 1 shows, in a perspective view, partially br ken-away, a heating element or coil of the furnace; FIGURE 2 shows a schematic side view of an induction furnace of the present invention, formed of four heating elements of Fig. 1; FIGURES 3a and 3b show respectively the magnetic flux path in a traditional inductor and the induced current path in the heated material; and FIGURE 4 shows a schematic sectional view along line IV-IV of Fig. 1 pointing out the path of magnetic flux in the laminations 7 of flux concentrators according to the present invention. Only one heating element 10 of the furnace according to the invention has been schematically illustrated in Fig. 1, in the direction of forward movement of a strip 1, which is comprised between two pairs of rollers 8 mounted on supports 9, as represented in Fig. 2, and is formed of a coil 2 having a substantially rectangular cross section and being embedded in a refractory block 3. In the drawing an end 4 of the coil can be seen, which provides the electrical connection with a power source through sui¬ table conductors or "bus bars" not shown, and with a cooling pipe network. There can be seen in fact holes 4a, 4b, inner and coaxial with the coil, respectively of inlet and outlet of cooling water. While leaving out the description of other structural or auxiliary parts which are well known in the art, according to the present invention Fig. 1 shows the flux concentrator 5 completely enclosing coil 2 as only a gap 6 is left free, between two arms of the loop formed by the coil, which is sufficient for the strip 1 passing therethrough. Flux concentrator 5 is formed of the assembly of two magnetic lamination packets, i.e. an upper one 5a and a lower one 5b, matching together at the ends, whereby coil 2 is completely surrounded while central gap 6 is ketp free. As is better shown for the upper packet 5a, which is represented with a partially broken away housing, laminations or sheet iron 7 forming the same are directed, all parallel each other, at right angles with respect to the plane defined by strip 1 and the respective upper or lower loop of coil 2, thus enhancing, with a high magnetic permeability, the flux concentration at the inside thereof. Upon longitudinally crossing a length of strip 1, as shown in Fig. 4, the flux would have the tendency to close its path at the outside, by linking through the metal structural parts of the furnace itself. Actually the flux leakage flows circularly within each lamination thus closing the magnetic circuit, but at the same time preventing or reducing to the minimum the generation of induced currents in a crosswise direction owing to the high resistance provided by the lamination packet when induced or eddy currents pass from a sheet iron to another. To better explain what above described, with reference to Figs. 3a, 3b, relating to the prior art, there can be observed how the magnetic flux, produced by a coil 2 shown in cross-section, while passing through the material 1 to be heated, closes substantially in the air and produces an induced current in material 1, with the direction illustrated by arrow C. At an early analytical study of flux paths , as theoretically shown in Fig. 3a, negligible values of the magnetic field are detected at a distance of 200 mm from the inductor. However, when examining the actual system, with the supporting structures having a μ r higher than 1, as they are made of steel or in any case define closed rings, it is found that the flux is considerably deflected from these metal parts thus giving rise to power losses which may be estimated as of 20%. In Fig. 4, schematically showing in cross section the flux concentrator 5 with a pair of steel irons, namely an upper one 7a and a lower one 7b, the magnetic flux F substantially closes at the inside thereof, so as to reduce to a minimum the losses due to eddy currents in the coil core. Obviously the magnetic sheet irons will have to be suitably dimensioned to this purpose, with a size choice which has to be the more careful, the higher is the frequency of magnetic field. An example of embodiment, on experimental basis, is reported in the following for an induction furnace system according to the present invention, in order to show the higher efficiency obtained. EXAMPLE An induction furnace for thin slabs was prepared 5 by placing in series four inductor assemblies as above described and shown in the drawings, with applied power of 925 kW on each of them and a working frequency of 6 kHz. The thin slab to be heated, made of Fe 37 steel, was sized 1330 mm in width and 25 mm I Q in thickness. Temperature was detected by means of two termocouples, one of which located at the center of the slab and the second at 2 mm from its surface. By feeding forward the thin slab at a speed of 9 m/min, a temperature gradient of 83°C has been experienced. 1 5 Also by means of tests made previously, it was found that at this temperature the thermal losses due to radiation are equal to 17°C. Therefore the total net difference of temperature is of 100°C, that corresponds, for a value of 0.2 Wh.Kg " .K -1 for the 0 specific heat of the material, to an energy of 25x1330x7.85.10 "6 x9000x60x0.2xl00°C = 2819 kWh. Power losses in the core were of 12 W, i.e. 1% of the total power. Theref o re an induc tor ef f i c i ency may be 5 calculated, as a ratio between applied power and power actual ly rece ived by the s lab : η = 2819 / ( 925x4 ) = 0 . 762 , again a value of about 0 . 6 which would have been obtained under the same conditions , but with two lateral f lux concentrators o f the above-mentioned 0 prior published patent WO 90/14742 instead of the linear flux concentrator encircling each inductor according to the present invention. Possible additions and/or modifications can be adopted into the above-described and illustrated 5 embodiment of the improved induction furnace according to the present invention without exceeding the scope of- the invention itself. It is clear that the number of coils or heating elements which in series form the furnace is not critical and may be chosen at will. 10 15 0 *5 0

Claims: CLAIMS 1. An induction furnace for heating, at homogenous temperature, flat products (1) such as thin slabs or steel strips continuously crossing said furnace, comprising in succession inductor coils (2), each of which is embedded in an inductor assembly with refractory material (3) and is separately fed through frequency converters, there being provided pairs of rollers (8) between each coil and the subsequent one, for supporting and feeding forward the flat product (1), wherein the size of each coil (2) in the feeding direction of the strip is 350 mm or less, characterized in that each coil (2) is enclosed in a linear flux concentrator (5) extending along the whole width of the coil (2) in the crosswise direction with respect to the feeding of flat product (1). 2. An induction furnace according to claim 1, characterized in that said linear concentrator (5) is formed of two portions (5a, 5b), respectively upper and lower portion, being joined at their ends while leaving centrally free a gap (6) for said flat product (1) passing therethrough. 3. An induction furnace according to claim 2, characterized in that each portion (5a, 5b) of the linear concentrator (5) is formed as a packet of magnetic sheet irons (7) arranged side by side, which are substantially C-shaped and all directed at right angles to both the plane of coil (2) and the one defined by the product (1) to be heated, arranged in facing relationship to each other for housing in said gap (6) comprised therebetween said coil (2) which in turn surrounds the flat product (1) .

Inventors: ARVEDI GIOVANNI, GOSIO GIOVANNI, ARVEDI, GIOVANNI, GOSIO, GIOVANNI
Applicants: ARVEDI GIOVANNI, ARVEDI, GIOVANNI
Application year: 1992
Main classification: H05B6
IPC codes: C21D1, C21D9, F27D23, H05B6