Electrical connecting method

Abstract: An electrical connecting method connects a first contact (1a, 14) of a first object (4, 11) to a second contact (1b, 22) of a second object (4, 21). The electrical connecting method includes the steps of coating a Ga system liquid metal (2) on at least one of the first and second contacts (1a, 14; 1b, 22), where the Ga system liquid metal (2) includes a predetermined weight percent of Bi, and contacting the first contact (1a, 14) to the second contact (1b, 22) via the Ga system liquid metal (2). The predetermined weight percent of Bi is selected such that the liquid state of the Ga system liquid metal is maintained when the first and second contacts make contact via the Ga system liquid metal.

Description: The present invention relates generally to electrical connecting methods, and more particularly to an electrical connecting method which makes an electrical connection using a gallium (Ga) system liquid metal. Recently, in electronic devices, the number of terminals has increased and the pitch of the terminals has become narrower due to the reduced size of such electronic devices and the high packaging density. For this reason, an important problem to be solved is how detachably to connect a large number of terminals extending from a large scale semiconductor integrated circuit device, a printed circuit and the like. Conventionally, connectors are used detachably to connect the terminals. The connector may have various shapes and configurations depending on the object and use of the connection. However, basically, the connector is made up of a plurality of plugs and a plurality of receptacles. Each plug is inserted into the corresponding receptacle and is held thereby to make the electrical connection. In a conventional connector, the connection and disconnection can be made manually if the number of terminals to be connected is of the order of approximately 100. If the inserting force required per terminal is 0.98N (100 gf), for example, it requires an inserting force of 98N (10 kgf) to connect 100 terminals. However, in a printed circuit having a large number of large scale semiconductor integrated circuit devices mounted thereon, the number of terminals to be connected is of the order of several hundred to several thousand. In this case, the connector cannot be connected and disconnected manually. For this reason, methods such as the so-called low inserting force (LIF) method or the zero inserting force (ZIF) method are employed to facilitate the connection and disconnection of the connector. According to such methods, the contact part of the receptacle opens to facilitate insertion and extraction of the corresponding plug. However, the mechanism required to carry out such methods is complex and is unsuitable for application to small electronic devices. On the other hand, methods using a liquid metal have been proposed to make the electrical connection. For example, a metal which is liquid at room temperature is used for the receptacle, and the plug is inserted into the liquid metal receptacle or, at least one of the two contacts to be connected is coated with a liquid metal before the two contacts are connected. However, methods using such a liquid metal have yet to solve the problems which will be described hereunder. The most familiar metal which is liquid at room temperature is probably mercury (Hg). For example, a method using Hg in the contact part of a connector is proposed in a Japanese Laid-Open Patent Application No. 57-123673. Hg may not have been used for the connector, but it was well known to use Hg for a small number of terminals of experimental devices. However, because Hg is toxic, it is difficult to use Hg in a perfectly sealed environment and the use of Hg in the connector having a large number of terminals is impractical for safety reasons. On the other hand, it is possible to use a eutectic alloy of Ga such as gallium-indium (Ga-In) and gallium-tin (Ga-Sn) which has an extremely low melting point and is liquid at room temperature. The use of Ga-In is proposed in Japanese Laid-Open Patent Application No. 58-130540 disclosing a method according to the preamble of claim 1 and claim 7, for example. It is convenient to use such a eutectic alloy of Ga for electrical connection because the melting point of the eutectic alloy can be varied depending on the composition. For example, it is possible to set the melting point of the eutectic alloy so that, when the temperature rises during operation of the device, the eutectic alloy is melted and, while the device is not being used, the eutectic alloy is solid so as to facilitate moving of the device. Therefore, the use of a eutectic alloy of Ga in a connector is advantageous in that the connection and disconnection can be made without the need of large inserting and extracting forces. However, the easy corrosion of this eutectic alloy makes it difficult to apply the connecting-method to an open system. Accordingly, it is a general object of the present invention to provide a novel and useful electrical connecting method in which the problem described above is eliminated. Also in the prior art, US-A-4966142 discloses electrically conductive alloys including Ga. According to a first aspect of the present invention, there is provided a method for electrically connecting a first contact of a first object to a second contact of a second object via a Ga system liquid metal which is in a liquid phase at room temperature, characterized by: (a) coating said Ga system liquid metal on at least one of the first and second contacts; and (b) contacting the first contact with the second contact via the Ga system liquid metal, said Ga system liquid metal including 0.5 to 1.0 weight percent of Bi. According to a second aspect of the present invention, there is provided a method for electrically connecting a first contact of a first object to a second contact of a second object via a Ga system liquid metal which is in a liquid phase at room temperature, characterized by: (a) coating a first material including Ga and having a weight X on the first contact and coating a second material including In or Sn and having a weight Y on the second contact; and (b) contacting the first contact with the second contact to generate said Ga system liquid metal between the first and second materials, at least one of said first and second materials including Bi having a weight Z so that Z/(X+Y+Z) is 0.005 to 0.01. The method of the first and second aspects of the present invention make it possible to prevent corrosion of the Ga system liquid metal. The method of the first aspect of the invention may further comprise coating a liquid polymer material on a surface of the Ga system liquid metal prior to the step (b). In this way, it is possible to improve further the corrosion resistance of the Ga system liquid metal. The first and second aspects of the invention may further comprise cooling a contact part where the first contact makes contact with the second contact so that the temperature at the contact part is maintained at room temperature. In this way, it is possible to prevent diffusion of the Ga system liquid metal and greatly extend the reliability of the electrical connection. For a better understanding of the invention, and to show how the same may be carried into effect, reference will now be made, by way of example, to the accompanying drawings, in which:- Fig. 1 is a perspective view for explaining a first embodiment in accordance with the first aspect of the present invention; Fig. 2 is a perspective view for explaining a first embodiment in accordance with the second aspect of the present invention; Fig. 3 is a cross sectional view for explaining a second embodiment in accordance with the first aspect of the present invention; Fig. 4 is a side view for explaining a second embodiment in accordance with the second aspect of the present invention; Fig. 5 is a side view of a part of Fig. 4 on an enlarged scale; Fig. 6 is a side view for explaining the state immediately before making an electrical connection in the second embodiment in accordance with the second aspect of the present invention; Fig. 7 is a side view for explaining an electrical disconnection; Fig. 8 is a side view for explaining a third embodiment in accordance with the second aspect of the present invention; Fig. 9 is a side view for explaining a fourth embodiment in accordance with the second aspect of the present invention; and Fig. 10 is a side view for explaining a fifth embodiment in accordance with the second aspect of the present invention. Figs. 1 and 2 respectively are perspective views for explaining first embodiments in accordance with the first and second aspects of the present invention, and Fig. 3 is a cross sectional view for explaining a second embodiment in accordance with the first aspect of the present invention. In Figs. 1 to 3, those parts which are the same are designated by the same reference numerals. In Figs. 1 to 3, electrical contacts 1a extend from one insulator body 4, and electrical contacts 1b extend from another insulator body 4. For example, each electrical contact 1a, 1b is a kovar wire rod having a diameter of 0.5 mm and is made of a Fe-Ni-Co system alloy with a Rh or Au plating of 3 µm provided thereon. For example, each insulator body 4 is made of polybuthylene terephthalate (PBT), and 360 contacts are embedded at lmm intervals and used as a sample for evaluation. First, a first embodiment in accordance with the first aspect of the invention will be described, referring to Fig. 1. In Fig. 1, the ends of the electrical contacts 1a, 1b have thereon a Ga system liquid metal 2, such as Ga-In and Ga-Sn including 0.5 to 1.0 weight percent of Bi. For example, the Bi can be added to the Ga system liquid metal 2 by dissolving small quantities of Bi while heating the Ga system liquid metal 2 to 200°C. The excess Bi separates when the Ga system liquid metal 2 is cooled to room temperature, and the Bi content in the Ga system liquid metal 2 becomes 0.5 to 1.0 weight percent. The tip ends of the contacts 1a and 1b are submerged into the Ga system liquid metal 2 which includes Bi, so as to form a ball of the Ga system liquid metal 2 on the tip end of each of the contacts 1a and 1b. The weight of the Ga system liquid metal 2 deposited on the tip end of each of the contacts 1a and 1b is, for example, approximately 5 mg. When the contacts 1a, 1b having the balls of Ga system liquid metal 2 thereon make contact, each pair of corresponding balls of Ga system liquid metal 2 on the corresponding pair of contacts 1a and 1b unite and form one integral ball of Ga system liquid metal 2. If it is assumed that the load corresponding to the inserting force of a conventional connector is approximately 0.05N (5 gf) per contact in order to obtain a safe conduction, the electrical resistance between the pair of contacts 1a and 1b corresponding to the contact resistance of a conventional connector is approximately 10 mΩ. Accordingly, even when connecting 360 contacts 1a to 360 contacts 1b, a load of approximately 19.6N (2 kgf) is sufficient to realize the connection. In the case of a conventional connector, it would require an inserting force of approximately 490N (50 kgf). Thus, the present method enables electrical connection by a load which is approximately several tens of the inserting force required in the case of the conventional connector. In addition, the load required to disconnect the pair of contacts 1a and 1b, corresponding to the extracting force required to extract the conventional connector, is unnecessary in the present method. The corrosion resistance of the Ga system liquid metal 2 including Bi was tested in a high-temperature and high-humidity environment. The contacts 1a and 1b, connected by the integrated balls of the Ga system liquid metal 2, were left in a high-temperature and high humidity environment of 60°C and 85%RH, and the electrical resistance between the connected pair of contacts 1a and 1b was measured. No change in the electrical resistance of approximately 10 mΩ was detected, even after 1000 hours. On the other hand, in the case where a Ga system liquid metal not including Bi was used to connect the corresponding pair of contacts and left in the above high-temperature and high-humidity environment, it was found that the electrical resistance between the corresponding pair of contacts increased from approximately 10 mΩ to approximately 1Ω after 100 hours. Next, a first embodiment in accordance with the second aspect of the invention will be described, by referring to Fig. 2. In this method, a first material 2a is coated on each tip end of the contacts 1a, while a second material 2b is coated on each tip end of the contacts 1b. The first material 2a is Ga having a weight X, and the second material 2b is In or Sn having a weight Y. In addition, Bi having a weight Z is included in at least one of the first and second materials 2a and 2b so that Z/(X+Y+Z) is 0.005 to 0.01. A eutectic reaction occurs when the first and second materials 2a and 2b on the respective contacts 1a and 1b make contact. As a result, a Ga system liquid metal 2 is generated between each corresponding pair of contacts 1a and 1b, and the corresponding pair of contacts 1a and 1b are electrically connected. Because the Ga system liquid metal 2 which connects the corresponding pair of contacts 1a and 1b includes 0.5 to 1.0 weight percent of Bi, a corrosion resistance which is substantially the same as that obtained in the first embodiment of the first aspect was obtained in this embodiment. This was confirmed by an evaluation experiment similar to that described with reference to the first embodiment of the first aspect. Next, a second embodiment in accordance with the first aspect of the invention will be described referring to Fig. 3. In this embodiment, the Ga system liquid metal 2 is coated on the tip ends of at least one of the contacts 1a and the contacts 1b, and a liquid polymer material 3 is coated on the surface of the Ga system liquid metal 2, as shown in Fig. 3 (A). In this embodiment, the Ga system liquid metal 2 is coated on the tip ends of only the contacts 1a, and the liquid polymer material 3 is coated on the Ga system liquid metal 2 by submerging the tip ends of the contacts 1a in the liquid polymer material 3. The liquid polymer material 3 is, for example, a liquid organic polymer material such as polyphenyl ether or polyperfluoroalkylether. The liquid polymer material 3 acts as a so-called rust preventive agent covering the Ga system liquid metal 2. When the contact 1a having the Ga system liquid metal 2 coated with the liquid polymer material 3 at the tip end thereof connects to the corresponding contact 1b, the film of the liquid polymer material 3 is pushed away by the contact 1b and the contact 1b makes contact with the contact 1a, as shown in Fig. 3 (B). As a result, the contacts 1a and 1b are electrically connected by the Ga system liquid metal 2, and in this state, the liquid polymer material 3 covers the Ga system liquid metal 2. The weight reduction rate of the liquid polymer material 3 used in this embodiment is a maximum of approximately 10% when heated at 100°C for 1000 hours. In other words, the evaporation of the liquid polymer material 3 at room temperature is negligible in this embodiment. The Ga system liquid metal 2 is a liquid at room temperature and the viscosity thereof is a maximum of several cP. On the other hand, the viscosity of the liquid polymer material 3 is several tens to several hundred cP at room temperature. Hence, the viscosity of the Ga system liquid metal 2 is lower than that of the liquid polymer material 3. For this reason, it may be difficult to coat the liquid polymer material 3 on the Ga system liquid metal 2 which is formed at the tip ends of at least one of the contacts 1a and the contacts 1b. In such a case, the Ga system liquid metal 2 is subjected to the atmosphere and-stirred before being coated on the tip ends of the contacts. As a result, an oxide of Ga is generated within the Ga system liquid metal 2, and the viscosity of the Ga system liquid metal 2 gradually increases. It was confirmed that the viscosity of the Ga system liquid metal 2 increases to approximately 500 cP if stirred in the atmosphere at room temperature for approximately 1 hour. This increased viscosity of the Ga system liquid metal 2 is approximately the same as the viscosity of the polyperfluoroalkylether which is 550 cP. In other words, by stirring the Ga system liquid metal 2 in the atmosphere, it is possible to increase the viscosity of the Ga system liquid metal 2 to a value approximately the same as the viscosity of the liquid polymer material 3 used to cover the Ga system liquid metal 2 in the liquid polymer material. Therefore, by increasing the viscosity of the Ga system liquid metal 2 to a value approximately the same as the viscosity of the liquid polymer material 3 before coating the Ga system liquid metal 2 on the tip ends of at least one of the contacts 1a and the contacts 1b, it is possible satisfactorily to coat and cover the Ga system liquid metal 2 with the liquid polymer material 3 by simply submerging the tip ends of the contacts coated with the Ga system liquid metal 2 in the liquid polymer material. By covering the Ga system liquid metal 2 with the liquid polymer material 3, it is possible to seal the Ga system liquid metal 2 from the surrounding environment and improve the corrosion resistance characteristics of the Ga system liquid metal 2. Of course, the Ga system liquid metal 2 may be coated on only one of the contacts 1a and 1b or on both the contacts 1a and 1b, and the same effects are obtained in either case. In addition, because the Ga system liquid metal 2 includes Bi, the corrosion characteristic of the Ga system liquid metal 2 is sufficient, but the corrosion resistance can further be improved by coating the liquid polymer material 3. In the embodiments described above, the contacts 1a and 1b are made of the kovar wire rod having a diameter of 0.5 mm. However, the tip ends of the contacts which make contact with each other contribute to the electrical connection. Accordingly, an Au bump, which is provided as a lead terminal of a semiconductor chip having semiconductor elements, for example, may be used as one of the contacts. In other words, the present invention is applicable to the electrical connection of the semiconductor chips to the package. In operation, certain electronic devices may generate considerable heat. Hence, the liquid metal used for the electrical connection in such electronic devices may diffuse into the contact and eventually disappear with time due to the heat, because the amount of liquid metal coated on the contact is extremely small. If the liquid metal disappears, the contacts are mechanically connected as if the contacts were soldered together. As a result, it becomes extremely difficult to disconnect the electrical connection. Next, a description will be given of embodiments of the second aspect of the invention which can eliminate this problem of decreasing liquid metal due to the heat generated by the electronic device. First, a second embodiment in accordance with the second aspect of the present invention will be described, referring to Figs. 4 to 7. Fig. 5 shows a part of Fig. 4 on an enlarged scale. As shown in Figs. 4 to 7, an electronic circuit module 11 includes a printed circuit substrate 12, and a plurality of large scale integrated circuits (LSIs) 13 mounted on the printed circuit substrate 12. A plurality of pins 14, which are made of Ni, are fixed on the lower surface of the printed circuit substrate 12. A Ga part 15 having a hemispherical shape is provided on a tip end 14a of each pin 14. A Peltier element 16 is provided to cool all of the pins 14. A thermistor 17 is provided at the tip end 14a of one specific pin 14. A driving circuit 18 is provided to drive the Peltier element 16. A control circuit 19 monitors the output of the thermistor 17 and controls the operation of the driving circuit 18. The Peltier element 16, the thermistor 17, the driving circuit 18 and the control circuit 19 form a cooling means 20. This cooling means 20 operates to maintain the tip ends 14a of the terminals 14 at room temperature during operation of the electronic circuit module 11. A plurality of pad-shaped terminals 22 made of Ni are formed on a mother board 21. An In part 23 having a hemispherical shape is provided on top of each pad-shaped terminal 22. Next, the electrical connection of the pins 14 and the corresponding pad shaped terminals 22 will be described. As shown in Fig. 6, the electronic circuit module 11 is first aligned with respect to the mother board 21. Then, as indicated by arrow 25, the electronic circuit module 11 is lowered so that the pins 14 simply make contact with the corresponding pad shaped terminals 22. Hence, even if the number of pins 14 is several thousand, for example, it is possible to realize the electrical connection using a low load. As a result, the electrical connection is made, as shown in Figs. 4 and 5. When the Ga part 15 makes contact with the In part 23, a eutectic reaction occurs. For this reason, a liquid phase Ga-In alloy 26 is generated and covers the periphery of a contact part 27 where the Ga part 15 and the In part 23 make contact. Accordingly, the liquid phase Ga-In alloy 26 exists between the pin 14 and the corresponding pad shaped terminal 22, and the area of the contact part 27 is increased thereby. Thus, the contact resistance between the pin 14 and the pad shaped terminal 22 is approximately 20 mΩ, i.e. relatively small. The melting point of the Ga-In alloy 26 is 15.7°C. Next, the state of the electronic circuit module 11 during operation will be described. When the electronic circuit module 11 operates, the LSIs 13 generate heat and the temperature of the electronic circuit module 11 rises to as much as 80°C. Consequently, the temperature at the tip end 14a of each terminal 14 increases. The temperature at the tip end 14a of the terminal 14 is detected by the thermistor 17. When the temperature detected by the thermistor 17 increases, the Peltier element 16 is operated via the control circuit 19 and the driving circuit 18 in response to the output of the thermistor 17. When the Peltier element 16 operates, the pins 14 are cooled. As a result, the contact part 27 and its periphery are cooled via the pins 14, and the temperature is maintained at room temperature which is slightly higher than 15.7°C. For this reason, diffusion of the liquid phase Ga-In alloy 26 into the Ga part 15 and the In part 23 is suppressed, and the Ga-In alloy 16 maintains a liquid phase and continues to exist between the Ga part 15 and the In part 23. Therefore, the contact resistance between the pin 14 and the pad shaped terminal 22 is maintained at a relatively small value of 20 mΩ. The present inventors have confirmed that the liquid phase Ga-In alloy 26 remains by cooling the pins 14 by the Peltier element 16 even after the electronic circuit module 11 and the mother board 21 are left in an environment of 80°C for 1000 hours. Next, the operation of removing the electronic circuit module 11 from the mother board 21 will be described. The electronic circuit module 11 is removed by pulling the electronic circuit module 11 in the direction of arrow 28 in Fig. 4. When removing the electronic circuit module 11, the liquid phase Ga-In alloy 26 exists at the periphery of the contact part 27, and there is no mechanical connection between the Ga part 15 and the In part 23. In other words, the Ga part 15 and the In part 23 simply make contact with each other. For this reason, no large force is required to separate the pins 14 from the pad shaped terminals 22, and the electronic module 11 can easily be removed from the mother board 21, as shown in Fig. 7, using an extremely small load. If the temperature at the contact part 27 falls below the melting point of the Ga-In alloy 26, the Ga-In alloy 26 will solidify. But if the temperature is returned to room temperature, the Ga-In alloy 26 will return to the liquid phase, and the electrical connection can be disconnected smoothly at room temperature. Next, a description will be given of a third embodiment in accordance with the second aspect of the present invention, referring to Fig. 8. In Fig. 8, those parts which are the same as those corresponding parts in Figs. 4 to 7 are designated by the same reference numerals, and a description thereof will be omitted. In this embodiment, a Sn part 30 is provided on the pad shaped terminal 22 in place of the In part 13 of the second embodiment. A eutectic reaction occurs when the Ga part 15 makes contact with the Sn part 30, and a liquid phase Ga-Sn alloy 31 exists between the Ga part 15 and the Sn part 30. This Ga-Sn alloy 31 has a melting point of 20°C. Next, a description will be given of a fourth embodiment in accordance with the second aspect of the present invention, referring to Fig. 9. In Fig. 9, those parts which are the same as those corresponding parts in Figs. 4 to 7 are designated by the same reference numerals, and a description thereof will be omitted. In this embodiment, a In-Sn part 32 is provided on the pad shaped terminal 22 in place of the In part 13 of the fourth embodiment. A eutectic reaction occurs when the Ga part 15 makes contact with the In-Sn part 30, and a liquid phase Ga-In-Sn alloy 33 exists between the Ga part 15 and the In-Sn part 32. This Ga-In-Sn alloy 33 has a melting point of 15°C. Next, a description will be given of a fifth embodiment in accordance with the second aspect of the present invention, referring to Fig. 10. In Fig. 10, those parts which are the same as those corresponding parts in Figs. 4 through 7 are designated by the same reference numerals, and a description thereof will be omitted. In this embodiment, the pins 14 are made to contact the corresponding pad shaped terminal 22 at a contact part, and the liquid phase Ga-In alloy 26 is 20 deposited on the contact part. Of course, the liquid phase Ga-Sn alloy 31 or the liquid phase Ga-In-Sn alloy 33 may be used in place of the liquid phase Ga-In alloy 26. The cooling materials and methods used in the second to fifth embodiments in accordance with the second aspect of the invention can of course be applied to the first aspect of the invention. In addition, a cooling unit using cooling water or fluorocarbon coolant may be used in place of the Peltier element 16. Moreover, the second to fifth embodiments in accordance with the second aspect of the invention can be applied to the general connector using a plug and socket (or receptacle) combination.

Claims: A method for electrically connecting a first contact (1a;14) of a first object (4;11) to a second contact (1b;22) of a second object (4;21) via a Ga system liquid metal (2) which is in a liquid phase at room temperature, characterized by: (a) coating said Ga system liquid metal (2) on at least one of the first and second contacts (1a,1b); and (b) contacting the first contact (1a) with the second contact (1b) via the Ga system liquid metal (2), said Ga system liquid metal (2) including 0.5 to 1.0 weight percent of Bi. A method as claimed in claim 1, further comprising obtaining said Ga system liquid metal by dissolving Bi in a Ga system liquid metal while heating the Ga system liquid metal to a temperature at which the Bi and the components of the Ga system liquid metal react, and then cooling the heated Ga system liquid metal with Bi dissolved therein to room temperature so that excess Bi separates from the Ga system liquid metal. A method as claimed in claim 1 or claim 2, further comprising coating the surface of the Ga system liquid metal (2) with a liquid polymer material (3) prior to step (b). A method as claimed in claim 3, further comprising stirring the Ga system liquid metal (2) in the atmosphere so that the viscosity of the Ga system liquid metal (2) becomes approximately the same as the viscosity of the liquid polymer material (3) before coating the Ga system liquid metal (2) with said liquid polymer material (3). A method as claimed in claim 3 or claim 4, wherein said liquid polymer material (3) is polyphenyl ether or polyperfluoroalkylether. A method as claimed in any preceding claim, wherein said Ga system liquid metal (2) is coated on the tip end of at least one of the first and second contacts (1a,1b), and the tip end of the first contact (1a) is contacted with the tip end of the second contact (1b) via the Ga system liquid metal (2). A method for electrically connecting a first contact (1a; 14) of a first object (4;11) to a second contact (1b;22) of a second object (4;21) via a Ga system liquid metal (2) which is in a liquid phase at room temperature, characterized by: (a) coating a first material (2a) including Ga and having a weight X on the first contact (1a;14) and coating a second material (2b) including In or Sn and having a weight Y on the second contact (1b;22); and (b) contacting the first contact (1a;14) with the second contact (1b, 22) to generate said Ga system liquid metal (2) between the first and second materials (2a, 2b), at least one of said first (2a) and second (2b) materials including Bi having a weight Z so that Z/(X+Y+Z) is 0.005 to 0.01. A method as claimed in claim 7, wherein said first material (2a) is coated on a tip end of the first contact (1a) and said second material (2b) is coated on a tip end of the second contact (1b), and the tip end of the first contact (1a) is contacted with the tip end of the second contact (1b) via the Ga system liquid metal (2). A method as claimed in any preceding claim, wherein the Ga system liquid metal (2) is a Ga-In alloy, a Ga-Sn alloy or a Ga-In-Sn alloy. A method as claimed in any preceding claim, further comprising cooling a contact part (27) where the first contact (14) makes contact with the second contact (22) so that the temperature at the contact part (27) is maintained at room temperature. A method as claimed in claim 10, wherein the temperature at the contact part (27) is monitored. A method as claimed in claim 10, wherein the temperature at the first contact (14) is monitored. A method as claimed in any preceding claim, wherein the first object (4;11) has a plurality of first contacts (1a;14), the second object (4;21) has a plurality of second contacts (1b;22), said steps (a) and (b) being carried out for each pair of corresponding first (1a;13) and second contacts (1b;22). A method as claimed in claim 13, wherein the first object is an electronic circuit module (11) and the first contacts (14) are pins extending therefrom, and the second object is a mother board (21) and the second contacts (22) are terminals formed thereon.

Inventors: CHIYONOBU TATSUO, HASHIMOTO KAORU, CHIYONOBU, TATSUO, HASHIMOTO, KAORU, Chiyonobu, Tatsuo, c/o Fujitsu Limited, HASHIMOTO, KAORU, C/O FUJITSU LIMITED
Applicants: FUJITSU LTD, FUJITSU LIMITED
Application year: 1992
Main classification: H01R4
IPC codes: B23K35, H01R4, H01L23, H01R13, H05K3