Magnetoresistive materials

Abstract: A magnetoresistive material comprising a first magnetic thin-film layer mainly composed of Co with a thickness of 10 to 100Å, and a second magnetic thin-film layer mainly composed of Ni X Fe Y Co Z with a thickness of 10 to 100Å, both of which layers are alternately laminated through a non-magnetic metallic thin-film layer sandwiched therebetween, mainly composed of Cu with a thickness of 10 to 35Å, wherein X, Y and Z are 0.6 ≦ X ≦ 0.9, 0 ≦ Y ≦ 0.3, and 0.01 ≦ Z ≦ 0.3, respectively, and a second magnetic thin-film layer mainly composed of 50 atomic% or more of Ni, with a thickness of 10 to 100Å, both of which layers are alternately laminated through a non-magnetic metallic thin-film layer sandwiched therebetween mainly composed of Cu with a thickness of 10 to 35Å, and non-magnetic metallic thin-film layers mainly composed of Cu with a thickness of 10 to 25Å, both of the two kinds of layers being laminated, and non-magnetic metallic thin-film layers mainly composed of Ni-Co containing 50 atomic% or more of Ni with a thickness of 10 to 100Å, and non-magnetic metallic thin-film layers mainly composed of Cu having a thickness of 10 to 25Å, both of the two kinds of layers being laminated.

Description: BACKGROUND OF THE INVENTION FIELD OF THE INVENTION: The present invention relates to magnetoresistive materials for magnetoresistance (MR) heads, sensors or the like. DESCRIPTION OF THE RELATED ART: Magnetoresistance sensors (hereinafter referred to as MR sensors) and magnetoresistance type heads (hereinafter referred to as MR heads) using magnetoresistive elements have been under development up to now. Permalloys® of Ni 0.8 Fe 0.2 are primarily used for the magnetic bodies. However, the ratio of resistance change (hereinafter referred to as ΔR/R) of these materials is approximately 2.5%. To obtain magnetoresistive elements having greater sensitivity, elements having a large ΔR/R are required. A Ni-Co alloy film containing 60 to 80 atomic% of Ni is available as one of these elements. Even if this film is used, the value of ΔR/R is approximately 5.8% at maximum. It was discovered recently that a large magnetoresistance occurs when using a Fe/Cr, artificial superlattice film (Physical Review Letter Vol. 61, p2472, 1988). With this material, however, a large ΔR/R cannot be obtained unless a magnetic field of more than 10 kOe (797,77 kA/m) is applied. Therefore it is difficult to put this film into practical use. These was a report that a resistance change of about 10% as regards (when applying a magnetic field of 3 kOe) ΔR/R was observed, by using an ultra-high vacuum deposition apparatus, on an artificial superlattice film composed of a Ni 0.8 Fe 0.2 (30Å)/Cu(50Å)/Co(30Å)/Cu(50Å)×15 layers (Preliminary Manuscript, Applied Physical Society Meeting, Autumn, 1990). However, there are problems in that a high-cost ultra-high vacuum deposition apparatus is required to produce films and also a large ΔR/R cannot be obtained unless a large magnetic field of approximately 3 kOe is applied. SUMMARY OF THE INVENTION An object of the present invention is to obtain a magnetoresistive material which makes it possible to produce magnetoresistive elements having a large ΔR/R by a practical, low magnatic field. The magnetoresistive materials of the present invention have constitution as specified in the appended claims. The aforementioned and other objects, features and advantages of the present invention will become clear when reference is made to the following description of the preferred embodiments of the present invention, together with reference to the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWING Fig. 1 is a view which illustrates the directions of the spin orientations of each magnetic layer of a magnetoresistive material of the present invention when the applied magnetic field is weak; Fig. 2 is a view, according to a first embodiment, which illustrates the dependence of the MR change ratio of the magnetoresistive material upon the thickness of a Cu layer; Fig. 3 is a view, according to a third embodiment, which illustrates the dependence of the MR change ratio of the magnetoresistive material upon the thickness of a Cu layer; Fig. 4 is a view, according to a fifth embodiment, which illustrates the dependence of the MR change ratio of the magnetoresistive material upon the thickness of a Cu layer; Fig. 5 is a view, according to a seventh embodiment, which illustrates the dependence of the MR change ratio of the magnetoresistive material upon the thickness of a Cu layer; Fig. 6 is a view, according to the first embodiment, which illustrates a magnetoresistant materials produced; and Fig. 7 is a view of a magnetoresistant material produced in the fifth embodiment. DESCRIPTION OF THE PREFERRED EMBODIMENTS It is believed that the material of the present invention shows a large magnetoresistance because an anti-parallel state is achieved between the two adjacent magnetic metallic thin-film layers 1 and 3 separated by a non-magnetic metallic thin-film layer 2, as shown in Fig. 1. If there is no non-magnetic metallic thin-film layer, the magnetic thin-film layers are ferromagnetically connected parallelly, so that an anti-parallel state cannot be obtained with the result that a large magnetoresistance cannot be achieved. The constitution of the present invention will now be explained. The magnetic metallic thin-film layer 1 in the first, second, third and fourth embodiments contains Co as its main component and shows a semi-hard magnetic property. The magnetic metallic thin-film layer 3 is a soft magnetic material of Ni-rich Ni-Fe-Co or Ni-Co. In embodiments 5, 6, 7 and 8, the magnetoresistive materials comprise the magnetic metallic thin-film layers 1 and 3 both of which are Ni-rich Ni-Fe-Co or Ni-Co soft magnetic materials. The non-magnetic metallic thin-film layer 2 herein used is composed of Cu. (First Embodiment) In Fig. 1, the magnetic metallic thin-film layer 1 is mainly composed of Co and shows a semi-hard magnetic property. The magnetic metallic thin-film layer 3 is mainly composed of Ni-rich Ni X Fe Y Co Z . Ni X Fe Y Co Z whose magneto-striction is small and which shows a soft magnetic property is one in which X, Y and Z, expressed by atomic composition ratios, satisfying 0.6 ≤ X ≤ 0.9, 0 ≤ Y ≤ 0.3, and 0.01 ≤ Z ≤ 0.3, and more preferably 0.6 ≤ X ≤ 0.9, 0 ≤ Y ≤ 0.25, and 0.01 < Z ≤ 0.25. When the magnetoresistance effect is taken into consideration, ΔR/R of the Ni-Fe film is smaller than the Ni-Fe-Co film, and therefore Z is larger than 0.01. A typical one which satisfies these conditions is Ni 0.8 Fe 0.15 Co 0.05 . Nb, Mo, Cr, W, Ru or the like may be added to Ni-Fe-Co film to improve the soft magnetic property, and wear and corrosion resistances. If the thickness of each of the magnetic metallic thin-film layers are smaller than 10Å, there occurs in the magnetic metallic thin-film layer such a problem as magnetization at room temperature is reduced due to a decrease in Curie temperature. Further, since a magnetoresistive element practically used has a total film layer thickness of several hundred Å in order to utilize a lamination effect as in the present invention, it is necessary to make each magnetic thin-film layer have a thickness not more than 100Å. Preferably, the thickness of the magnetic metallic thin-film layer is 10 to 100Å. The non-magnetic metallic thin-film layer 2 sandwiched between these magnetic thin films is necessary to hardly react with a Ni-Fe-Co type magnetic thin film at the interface defined by them and to be non-magnetic. Cu is preferable for the film 2 and the most preferable thickness of a Cu layer is about 20Å. The ΔR/R shows the RKKY-like oscillation depending upon the thickness of the Cu layer, as shown in Fig. 2, the reason for it being not clear. When the thickness of Cu layer exceeds 35Å, the magnetoresistance decreases. Therefore, it is preferable for the thickness of the Cu layer to be not greater than 25Å. The advantages of the present invention will now be explained with reference to specific embodiments. There was used a multi-RF sputtering apparatus with Co, Cu and Ni 0.8 Fe 0.15 Ca 0.05 as targets, the inside of which sputtering apparatus was exhausted to 2 x 10 -7 Torr. Thereafter, Ar gas was introduced into the apparatus and the apparatus was set at 8 x 10 -3 Torr. A magnetoresistive material, having a constitution shown below, formed in sequency by sputtering, was produced on a glass substrate, as shown in Fig. 6. [Co(30)/Cu(0 to 55)/NiFeCo(30)/Cu(0 to 55)] x N where parentheses indicate a thickness (Å) and N is a repetition number, which varies from 12 to 33. The thickness of each film was controlled by adjusting the sputtering period of time and by using a shutter. A film having the repetition number (N) of 12 to 33 and a total thickness of approximately 0.2 µm was produced. The characteristics of the produced magnetoresistive material are shown in Fig. 2. ΔR/R was measured by applying a magnetic field of 300 Oe. As is clear from Fig. 2, it became evident that the ΔR/R has a local maximum value when the Cu layer is about 20Å thick. Next, the ΔR/R has a second local maximum value when the Cu layer is about 30Å thick. The ΔR/R has a third local maximum value when the Cu layer is about 40Å thick. Therefore, to obtain a maximum ΔR/R, it is most preferable that the Cu layer is about 20Å thick. In this embodiment, Co and NiFeCo layers were disposed as the outermost layers, however, any one of Co, NiFeCo, and Cu layers may be disposed as the outer most layers. Further, the number of layers laminated depends upon a kind of a product to be produced. For example, in a case of a film of 500Å in thickness used in a MR sensor, N is preferably 5 or so. (Second Embodiment) By using an RF sputtering apparatus and Co, Cu and Ni 0.8 Fe 0.15 Co 0.05 as targets, a film, in which the thickness of the Cu layer was constant and the thicknesses of the magnetic layers were changed, was produced by sputtering in the same manner as in the first embodiment. The characteristics of the produced film are shown in Table 1. The ΔR/R of a comparison sample having the same constitution as that of No. B but using Ni 0.8 Fe 0.2 which is a material used in the prior art in place of Ni 0.8 Fe 0.15 Co 0.05 was 8.8%, while the ΔR/R of a specimen of the invention using Ni 0.8 Fe 0.19 Co 0.01 was 12%. In view of this fact, Co is indispensable from the point of view of obtaining larger ΔR/R. No. Co(Å) Cu(Å) NiFeCo(Å) ΔR/R(%) A 20 20 20 15.8 B 30 20 30 15.5 C 50 20 50 10.6 D 70 20 70 9.5 (Third Embodiment) In Fig. 1, the magnetic metallic thin-film layer 1 has Co as its main component and shows a semi-hard magnetic property. The Ni-rich Ni-Co type alloys of the magnetic metallic thin-film layer 3 has Ni and Co as its main components. If Ni is smaller than 50% or less by an atomic composition ratio, a large ΔR/R is not obtained unless a larger magnetic field is applied. When the ratio of Ni is 90% or more, a large ΔR/R is not obtained either. A typical one which satisfies these conditions is Ni 0.8 Co 0.2 . A small amount of elements may be added to the Ni-Co film to improve the soft magnetic property, and wear and corrosion resistances. In a case where the thickness of each of these magnetic metallic thin-film layers is less than 10Å, there occurs in the metallic thin-film layers such a problem that magnetization at room temperature is reduced due to a decrease in Curie temperature. Further, since a practically used magnetoresistive element has a total thickness of several hundred Å, it is necessary for each magnetic metallic thin-film layer to have a thickness of not more than 100Å in order to produce a lamination effect as in the present invention. Therefore, the thickness of the magnetic metallic thin-film layer is preferably 10 to 100Å. The non-magnetic metallic th in-film layer sandwiched between these magnetic thin films is required to hardly react with a Ni-Fe-Co type magnetic thin film at the interface defined by them and to be non-magnetic. Cu is preferable for the film 2 and the most preferable thickness of a Cu layer is approximately 20Å. The ΔR/R shows a RKKY-like oscillation depending upon the thickness of the Cu layer, as shown in Fig. 3, though the reason for it is not dear. When it exceeds 35Å, the magnetoresistance decreases. Therefore, it is preferable for the thickness of the Cu layer to be not greater than 25Å. There were used a multi-RF sputtering apparatus and Co, Cu and Ni 0.8 Co 0.2 as targets, the inside of which sputtering apparatus was exhausted to 2 x 10 -7 Torr. Thereafter, Ar gas was introduced into the apparatus and the apparatus was set at 6 x 10 -3 Torr. A magneto-resistive material, having a composition shown below, formed in sequence by sputtering, was produced on a glass substrate: [Co(30)/Cu(0 to 35)/NiCo(30)/Cu(0 to 35)] x N where parentheses indicate a thickness (Å) and N is a repetition number. The thickness of each film was controlled by adjusting the sputtering period of time and by using a shutter. A film having the repetition number (N) of 15 to 33 and a total thickness of approximately 0.2 µm was produced. The characteristics of the produced magnetoresistive material are shown in Fig. 3. ΔR/R was measured by applying a magnetic field of 300 Oe. As is clear from Fig. 3, it became evident that the ΔR/R has a local maximum value when the Cu layer is about 20Å thick. Next, the ΔR/R has the second local maximum value when the Cu layer is about 30Å thick. Therefore, to obtain a maximum ΔR/R, it is preferable that the Cu layer be about 20Å thick. (Fourth Embodiment) By using an RF sputtering apparatus and Co, Cu and Ni 0.8 Co 0.2 as targets, a film, in which the thickness of the Cu layer was constant and the thicknesses of the magnetic layers were changed, was produced by sputtering in the same manner as in the third embodiment. The characteristics of the produced films are shown in Table 2. For reference, the ΔR/R of a comparison sample having the same composition as that of No. B but using Ni 0.8 Fe 0.2 which is a material used in the prior art in place of Ni 0.8 Co 0.2 was 8.8%. In view of this fact, Ni-Co type alloys are excellent from the point of view of obtaining larger ΔR/R. No. Co(Å) Cu(Å) NiCo(Å) ΔR/R(%) A 20 20 20 14.5 B 30 20 30 14.6 C 50 20 50 9.6 D 70 20 70 8.9 (Fifth Embodiment) In Fig. 1, the magnetic metallic thin-film layers 1 and 3 are films having Ni-rich Ni X Fe Y Co Z as their main components. Ni X Fe Y Co Z shows a small magnetostriction, a soft magnetic property and magnetoresistance in a case where X, Y and Z, expressed by atomic composition ratios, satisfy 0.6 ≤ X ≤ 0.9, 0 ≤ Y ≤ 0.3, and 0.01 ≤ Z ≤ 0.3, respectively. When magnetoresistance is taken into consideration, the ΔR/R of the entire film is larger for Ni-Fe-Co types than for Ni-Fe types. A typical one which satisfies these conditions is Ni 0.8 Fe 0.15 Co 0.05 , Nb, Mo, Cr, W, Ru or the like may be added to improve the soft magnetic property, and wear and corrosion resistances. In a case where the thickness of each of these magnetic thin-film layers is less than 10Å, there occurs in the magnetic thin-film layers such a problem as magnetization at room temperature is reduced due to a decrease in Curie temperature. Further, since a practically used magnetoresistive element has a total thickness of several hundred Å in order to utilize a lamination effect as in the present invention, the thickness of each magnetic thin-film layer is necessary to be not greater than 100Å. Preferably, the thicknesses of the magnetic metallic thin-film layers is 10 to 100Å. The non-magnetic metallic thin-film layer 2 sandwiched between these magnetic thin films is required to hardly react with a Ni-Fe-Co type magnetic thin film at the interface thereof and to be non-magnetic. Cu is preferable for the film 2 and the most preferable thickness of a Cu layer is approximately 20Å. If the thickness of a Cu layer is smaller than 10Å and the Cu layer becomes no more continuous film, the two adjacent magnetic thin film layers are magnetically coupled, and it is difficult to achieve a state in which the spins between the magnetic layers are anti-parallel as shown in Fig. 1. The ΔR/R shows a RKKY-like oscillation depending upon the thickness of the Cu layer, though the reason for it is not dear. Therefore, it is preferable for the thickness of the Cu layer to be not more than 25Å. The advantages of the present invention will now be explained with reference to specific embodiments. There were a multi-RF sputtering apparatus and Co, Cu and Ni 0.8 Fe 0.15 Co 0.05 as targets, the inside of which sputtering apparatus was exhausted to 2 x 10 -7 Torr. Thereafter, Ar gas was introduced into the apparatus and the apparatus was set at 8 x 10 -3 Torr. A magnetoresistive material having a composition shown below, formed in sequence by sputtering, was produced on a glass substrate as shown in Fig. 7. [NiFeCo(30)/Cu(10 to 32.5)] x N where parentheses indicate a thickness (Å), which varies from 32 to 50. The thickness of each film was controlled by adjusting the sputtering period of time and by using a shutter. A film having the repetition number (N) of 32 to 50 and a total thickness of approximately 0.2 µm was produced. The characteristics of the magnetoresistive material produced are shown in Fig. 4. ΔR/R was measured by applying an applied magnetic field or 300 Oe. As is clear from Fig. 4, the ΔR/R has a local maximum value when the Cu layer is about 20Å thick. It became evident that the thicker the Cu layer is above 20Å thick, the more the ΔR/R decreases. Therefore, to obtain a maximum ΔR/R, it is preferable that the Cu layer is about 20Å thick. (Sixth Embodiment) By using an RF sputtering apparatus and Co, Cu and Ni 0.8 Fe 0.15 Co 0.05 as targets, a film, in which the thickness of the Cu layer was constant and the thicknesses of the magnetic layers were changed, was produced by sputtering in the same manner as in the fifth embodiment The characteristics of the produced film are shown in Table 3. For reference, regarding a comparison sample having the same constitution construction as that of No. B and having Co in place of Ni 0.8 Fe 0.15 Co 0.05 , the ΔR/R value of the comparison sample was 5%. No. Cu(Å) NiFeCo(Å) ΔR/R(%) A 20 20 8.5 B 20 30 9.0 C 20 50 7.5 D 20 70 6.5 (Seventh Embodiment) In Fig. 1, the magnetic metallic thin-film layers 1 and 3 are films composed of Ni-Co containing at least 60 atomic% of Ni with a thickness of 10 to 100Å. A typical one which satisfies these conditions is Ni 0.8 Fe 0.15 Co 0.05 , Nb, Mo, Cr, W, Ru or the like may be added to improve the soft magnetic property, and wear and corrosion resistances. In a case where the thickness of each of these magnetic thin-film layers is less than 10Å, there occurs in the magnetic thin film such a problem as magnetization at room temperature is reduced due to a decrease in Curie temperature. Further, since a practically used magnetoresistive element has a total thickness of several hundred Å in order to utilize a lamination effect as in the present invention, each magnetic thin-film layer is necessary to be not greater than 100Å. Preferably, the thickness of the magnetic metallic thin-film layer is 10 to 100Å. The non-magnetic metallic thin-film layer 2 sandwiched between these magnetic thin films is required to hardly react with a Ni-Fe-Co type magnetic thin film at the interface therebetween and to be non-magnetic. Cu is preferable for the film 2 and the most preferable thickness of a Cu layer is approximately 20Å. If the thickness of Cu is smaller than 10Å and the Cu layer becomes no more continuous film, two adjacent magnetic thin-film layers are magnetically connected, and it becomes difficult to obtain such a state as the spins between the magnetic layers are anti-parallel as shown in Fig. 1. The ΔR/R value showed a RKKY-like oscillation depending upon the thickness of the Cu layer, though the reason for it is not clear. Therefore, in a case where the magnetoresistance up to the first local maximum peak is used, it is preferable for the thickness of the Cu layer to be not greater than 25Å. The advantages of the present invention will now be explained with reference to specific embodiments. There were used a multi-RF sputtering apparatus and Co, Cu and Nio 0.8 Co 0.2 as targets, the inside of which sputtering apparatus was exhausted to 2 x 10 -7 Torr. Thereafter, Ar gas was introduced into the apparatus and the apparatus was set at 8 x 10 -3 Torr. A magneto-resistive material, having a composition shown below, formed in sequence by sputtering, was produced on a glass substrate: [NiCo(30)/Cu(10 to 45)] x N where parentheses indicate a thickness (Å) and N is a repetition number. The thickness of each film was controlled by adjusting the sputtering period of time and by using a shutter. A film having a repetition number (N) of 27 - 50 and a total thickness of approximately 0.2 µm was produced. The characteristics of the produced magneto-resistive material are shown in Fig. 5. ΔR/R was measured by applying magnetic field of 300 Oe. As is clear from Fig. 5, it became evident that the ΔR/R has a local maximum value when the Cu layer is about 20Å thick, and as the thickness of the layer increases more than 20Å, the magnetoresistance decreases. Therefore, to obtain a maximum ΔR/R, it is preferable that the Cu layer is about 20Å thick. (Eighth Embodiment) By using an RF sputtering apparatus and Co, Cu and Ni 0.8 Co 0.2 as targets, a film, in which the thickness of the Cu layer was constant and the thicknesses of the magnetic layers were changed, was produced by sputtering in the same manner as in the seventh embodiment, The characteristics of the produced film are shown in Table 4. The ΔR/R of a comparison sample having the same constitution (construction) as that of No. B and using Co in place of Ni 0.8 Co 0.2 was 5%. No. Cu(Å) Ni-Co(Å) ΔR/R(%) A 20 20 8.5 B 20 30 9.0 C 20 50 7.5 D 20 70 6.5

Claims: A magnetoresistive material comprising first magnetic thin film layers mainly composed of Co with a thickness of 10 to 100Å, and second magnetic thin film layers mainly composed of Ni X Fe Y Co Z in which X, Y and Z are 0.6 ≤ X ≤ 0.9, 0 ≤ Y ≤ 0.3, and 0.01 ≤ Z ≤ 0.3, respectively, with a thickness of 10 to 100Å, both of the first and second layers being alternately laminated through a non-magnetic metallic thin film layer sandwiched therebetween, said non-magnetic layer mainly composed of Cu with a thickness of 10 to 35Å. A magnetoresistive material comprising first magnetic thin film layers mainly composed of Co with a thickness of 10 to 100Å, and second magnetic thin film layers mainly composed of Ni X Fe Y Co Z in which X, Y and Z are 0.6 ≤ X ≤ 0.9, 0 ≤ Y ≤ 0.25, and 0.01 ≤ Z ≤ 0.25, respectively and having a thickness of 10 to 100Å, both of said first and second layers being alternately laminated through a non-magnetic metallic thin film layer sandwiched therebetween, said non-magnetic layer mainly composed of Cu with a thickness of 10 to 25Å. A magnetoresistive material comprising first magnetic thin film layers mainly composed of Co with a thickness of 10 to 100Å, and second magnetic thin film layers mainly composed of Ni-Co containing not less than 50 atomic% of Ni with a thickness of 10 to 100Å, both of said first and second layers being alternately laminated through a non-magnetic metallic thin film layer sandwiched therebetween, said non-magnetic layer mainly composed of Cu with a thickness of 10 to 35Å, said second magnetic thin film layers containing less than 90 atomic% of Ni. A magnetoresistive material comprising first magnetic thin film layers mainly composed of Co with a thickness of 10 to 100Å, and second magnetic thin film layers mainly composed of Ni-Co containing not less than 50 atomic% of Ni, with a thickness of 10 to 100Å, both of said first and second layers being alternately laminated through a non-magnetic metallic thin film layer sandwiched therebetween, said non-magnetic layer mainly composed of Cu with a thickness of 10 to 25Å, said second magnetic thin film layers containing less than 90 atomic % of Ni. A magnetoresistive material comprising magnetic metallic thin film layers mainly composed of Ni X Fe Y Co Z with a thickness of 10 to 100Å, and non-magnetic metallic thin film layers mainly composed of Cu with a thickness of 10 to 25Å, both of the two kinds of layers being alternately laminated, wherein X, Y and Z are, by atomic composition ratios, 0.6 ≦ X ≦ 0.9, 0 ≦ Y ≦ 0.3, and 0.01 ≦ Z ≦ 0.3.

Inventors: SAKAKIMA HIROSHI, SATOMI MITSUO, SAKAKIMA, HIROSHI, SATOMI, MITSUO
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1992
Main classification: H01L43
IPC codes: H01L43, H01F10