Latent catalysts

Abstract: Amino resins, e.g., urea-formaldehyde and melamine-formaldehyde thermosetting resins, are cured with a latent catalyst which is a thermally-decomposable adduct of an aromatic sulfonic acid (e.g., p-toluene sulfonic acid) and a bicyclic oxazolidines (e.g., 1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane. The coating compositions can contain other conventional co-reactants, such as polyols, polyacids, alkyd resins, polyester resins, epoxies, acrylics and the like. Coatings containing the amino resin, co-reactant, and latent catalyst have an acceptable viscosity stability, cure rapidly at temperatures lower than some other latent catalysts, and produce films with no wrinkles.

Description: This invention relates to a thermally-decomposable composition comprising a bicyclic oxazolidine adduct of an aromatic sulfonic acid. Background of the Invention Heat-curable products obtained by reacting compounds containing amine or imine groups (e.g., ureas, amides and aminotriazines) with aldehydes (e.g., formaldehyde, glyoxal, and benzaldehyde) have been known for a number of years. Resins obtained by curing such condensation products possess an excellent combination of physical properties and are widely used in glues and molding compounds, as finishes for paper and textiles, and as surface coatings. The curable resins can be used per se or they can be further modified before curing, e.g., by alkylation with an alcohol such as methanol or butanol to provide solubility and compatibility and/or by admixture with other co-reactive materials such as polyfunctional compounds containing hydroxyl groups or carboxyl groups (e.g., glycols, alkyd resins, and polyester resins). Such curable resins commonly comprise urea- or melamine-aldehyde condensation products or the reaction products thereof with alcohols (e.g., methylol ureas or methylol melamines) and alkylated derivatives thereof (e.g, methylated or butylated derivatives) either alone or dissolved in a suitable solvent. These specific amino resins are coated onto three-dimensional substrates (e.g., metal, glass, wood and plastics) and then heat-cured. The curing mechanism is condensation and crosslinking to split out water, alcohol, or formaldehyde. Curing can be effected without a catalyst if the resins are heated for a long enough time, i.e., for hours or days. However, for immediate curing or for curing at more moderate temperatures, an acid is often added to function as a crosslinking catalyst. The acidic catalysts previously used with amino resins include boric acid, phosphoric acids, acid sulfates, sulfonic acids and sulfonyl halides, hydrochlorides, ammonium phosphates and polyphosphates, acid salts of hexamethylene tetramine, phthalic acid and oxalic acid. U.S. Pat. No. 3,979,478 (issued September 7, 1976 to L.V. Gallacher) discloses that high molecular weight polyalkylaromatic polysulfonic acids (e.g., dinonylnaphthalene disulfonic acid) are superior catalysts for curing amino resin systems. These acid catalysts cure the resins in short periods of time and produce products having superior physical properties. These acid catalysts can be stored in the form of thermally-decomposable adducts to provide greater shelf life. U.S. Pat. No. 3,474,054 (issued October 21, 1969 to M.M. White) teaches that amine salts of aromatic sulfonic acids, preferably tertiary amine salts (e.g., pyridine salt of p-toluene sulfonic acid), can be utilized to cure amino resin coating compositions. U.S. Pat. No. 3,293,324 (issued December 20, 1966 to F.E. Tropp et al.) discloses that the 2-dimethylamino-2-methyl-1-propanol salt of p-toluene sulfonic acid can also be utilized to cure thermosetting aminoplast resins. U.S. Pat. No. 4,200,729 (issued April 27, 1980 to L.J. Calbo) and U.S. Pat. No. 4,251,665 (issued February 17, 1981 to L.J. Calbo) disclose particular adducts which impart outstanding resistance properties to the cured resins. Aromatic sulfonic acids in association with oxaazacyclopentanes (e.g., 4,4-dimethyl-1-oxa-3-aza-cyclopentane) are outstanding latent catalysts for curing amino resin compositions. Compositions containing the latent catalysts have exceptional package stability and can be stored ready for use for relatively long periods of time without significantly detracting from the composition's usefulness. It is believed these advantageous results are attributable to a unique combination of the high volatility of the amine component and the low dissociation constant incident to the oxaazacylopentane adducts. This combination, in addition to other factors, may provide for a particularly effective association of the adduct with the resin during the curing process and result in fast curing times and cured resins having superior properties. The cured resins have superior properties, particularly water resistance, compared to resins cured with unneutralized aromatic sulfonic acids and to other amine adducts of the aromatic sulfonic acids. Summary of the Invention It has now been unexpectedly discovered that while the above oxa-azacyclopentane adducts may be useful for curing amino resin compositions, there are selected new amine adducts based on a bicyclic oxazolidine which offer faster cure times at lower temperatures despite the higher boiling point of the amine blocking agent. The present invention provides a thermally-decomposable composition comprising a bicyclic oxazolidine adduct of an aromatic sulfonic acid, the adduct having the formula: wherein A is phenyl or naphthyl; x is 1 to 8; y is 0 to 7; the sum of x and y is no greater than 8; z is 8-x-y when A is naphthyl and z is 6-x-y when A is phenyl; q is equal to or greater than 0.5; R is an alkyl, halogen, haloalkyl, or alkoxy group; R' is an organic group; and R" is hydrogen or a C 1 -C 6 alkyl group. Preferably R is an alkyl or alkoxy group. The organic group represented by R' is a straight or branched organic group such as an alkyl or hydroxyalkyl group, preferably a C 1 -C 6 alkyl or hydroxyalkyl group (e.g., an ethyl or hydroxyalkyl group). The C 1 -C 6 alkyl group represented by R" includes a methyl or isopropyl group. Preferably R" is hydrogen. The preferred sulfonic acid is p-toluene sulfonic acid. The preferred bicyclic oxazolidine is 1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane. Description of the Preferred Embodiments Aromatic sulfonic acids useful in the adduct can vary widely in chemical nature. They can contain one or more aromatic rings (e.g., benzene or naphthalene rings) and one or more sulfonic acid groups. When the acid has a single aromatic ring, the acid is an alkyl-benzene sulfonic acid and the alkyl groups can be positioned on the aromatic ring in the ortho, meta, or para position. Suitable alkyl-benzene sulfonic acids include p-decyl benzene sulfonic acid and p-dodecyl benzene sulfonic acid. The preferred alkyl-benzene sulfonic acid is p-toluene sulfonic acid. When the acids contain a naphthalene ring, the substituents may be in any position and mixed positional isomers are also included. The naphthalenic acids can have one or more sulfonic acid groups as well as straight or branched alkyl groups. Suitable naphthalenic sulfonic acids include dihexyl naphthalene disulfonic acid, diheptyl naphthalene disulfonic acid and dihexyl naphthalene sulfonic acid. The preferred naphthalenic sulfonic acids are dinonylnaphthalene disulfonic acid and dinonylnaphthalene (mono)sulfonic acid. The alkyl-substituted naphthalene polysulfonic acids are described in U.S. Pat. No. 3,979,478 . These acids have at least two straight or branched alkyl groups and two sulfonic acid groups on the naphthalenic nucleus. They have a molecular weight of at least about 500. Best results are obtained with maximum variations in substituent locations and maximum branching. These acids can be prepared, for example, by sulfonating polyalkylnaphthalenes. The polyalkylnaphthalenes can be made by alkylating naphthalene with olefins or alkyl halides in the presence of a suitable catalyst (e.g., hydrogen fluoride or anhydrous aluminum chloride) and a suitable solvent (e.g., naphtha, sulfur dioxide, nitrobenzene or a mixture of benzene and nitrobenzene). See U.S. Pat. No. 2,764,548 (issued September 25, 1956 to Robert G. King and George W. Thielcke and also assigned to the assignee of the present invention). If a branched olefin is used (e.g., propylene trimer or propylene tetramer obtained by polymerizing propylene with an acid catalyst such as phosphoric acid), then the alkyl groups will be highly branched. Sulfonation is accomplished by treating the polyalkylaromatic compound with a sulfonating agent. For example, the dialkylaromatic compound is dissolved in an inert solvent (e.g., petroleum naphtha, hexane, heptane, octane or a chlorinated solvent) and sulfuric acid, preferably oleum, is introduced into the solution at the desired temperature with agitation. After the reaction is complete, the sulfonic acids are recovered by extraction with water and the polysulfonic acid is recovered from the aqueous extract by extraction with a water immiscible solvent (e.g., pentanol, hexanol, heptanol, octanol and decanol). A detailed technique for preparing dinonylnaphthalene disulfonic acid, didodecylnaphthalene disulfonic acid and isomers and analogs thereof is described in the '548 patent. A preferred isolation procedure is described in U.S. Pat. No. 3,957,859 (issued May 18, 1976 to Thielcke). Suitable bicyclic oxazolidines have the formula where R' is a straight or branched organic group such as an alkyl group or hydroxy alkyl group, preferably a C 1 -C 6 alkyl or hydroxyalkyl group and most preferably an ethyl group or hydroxy methyl group and where R" is hydrogen or a C 1 -C 6 alkyl group (e.g., a methyl or isopropyl group) and preferably R" is hydrogen. The preferred bicyclic oxazolidine is 1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane. A review of oxazolidine chemistry is found in the publication Chemical Reviews, E.D. Bergmann, Vol. 53, pp. 309-352 (1953). As discussed above, the thermally-decomposable composition of the present invention are adducts of an aromatic sulfonic acid and a bicyclic oxazolidine. The acid and oxazolidine can form the adducts at varying molar ratios which will depend on the particular compounds employed and their properties. For example, the molar ratio of aromatic sulfonic acid to bicyclic oxazolidines can range from 0.5 to 1.5. The most preferred molar ratio is 1.0. The preferred adduct is an adduct of p-toluene sulfonic acid and 1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane. It is soluble in water; alcohols such as methanol, isopropanol, n-butanol and butyl cellosolve; acetates such as n-butyl acetate and 2-methoxypropyl acetate; ketones such as methyl ethyl ketone, methyl amyl ketone, methyl iso-butyl ketone; and xylene. It is insoluble in mineral spirits and only slightly soluble in high boiling aromatic hydrocarbons. Procedures for preparing the adducts are known to those skilled in the art. They involve treating the aromatic sulfonic acid with the bicyclic oxazolidine to effect neutralization of the acid. The acid can be used per se or it can be diluted in a solvent such as methanol or the solvents discussed above. The bicyclic oxazolidine is added to the acid or acid solution in an amount sufficient to raise the pH of the final catalyst solution to 2 to 4. The preferred pH is 2.5 to 3.5. The amino resin to be cured with the thermally-decomposable composition of the present invention generally comprises an amine- or imine-containing compound condensed with an aldehyde, a dialdehyde, or an aldehyde precursor. In particular, a urea-formaldehyde condensate or a triazine-formaldehyde condensate (e.g., melamine-formaldehyde condensate) can be used. Some of these condensates are soluble in organic solvents can be converted to solvent-soluble derivatives (e.g., ether derivatives). Amino resin condensates particularly suitable in the present invention include those generally described as aklylated-urea-formaldehyde condensates containing subsequently etherified groups derived from alcohols. The urea-formaldehyde condensates are prepared by reacting formaldehyde with urea in the presence of an acid or alkaline medium so that a methylol urea is formed which is then heat cured to a cured resin per se. On the other hand, if an alcohol is not present during the initial acid condensation, an alcohol and acid can subsequently be added after the initial alkaline condensation. The latter procedure is suitable for alkylated urea-formaldehyde condensates derived from saturated C 2 -C 8 aliphatic alcohols. Urea-formaldehyde condensates obtained from methyl or n-butyl alcohol are particularly suitable for impregnation or use in combination with other co-reactants. These alkylated urea-formaldehyde condensates are water-soluble and sometimes soluble in solvents such as hydrocarbons, ketones, esters and alcohols. Preparation of the condensates is not described herein since their preparation is adequately described in U.S. Pat. Nos. 2,222,506; 2,226,518; 2,227,223; 2,322,979; 2,323,357; 2,326,265 and 2,350,894. The preparation of the triazine-aldehyde condensates is also well known. Any triazine having two or more amine groups can be reacted with any aldehyde, preferably in the presence of a mild alkaline catalyst, in an aqueous or nonaqueous media. Alkylated derivatives can be prepared by carrying out the reaction in a solvent (e.g., n-butanol). Suitable amino-triazines include melamine, ammeline, 2-chloro-4,6-diamino-1,3,5-triazine, 2,4-diamino-triazine, N,N-dimethyl-melamine, benzoguanamine and acetoguanamine. Suitable aldehydes include paraformaldehyde, acetaldehyde, glyoxal, paraldehyde, benzaldehyde and furfural. Suitable solvents can vary widely and include inert solvents, preferably easily volatized solvents such as toluene, xylene and benzene. As discussed above, solvents which react with the condensation product to form alkylated products can be used. Water can also be used as a solvent for some of the low molecular weight resins, which are sometimes referred to as cross-linking resins. As with urea resins, the triazine-based amino resins can be the aldehyde-triazine reaction products or reaction products modified by reaction with an alcohol (e.g., methyl or butyl alcohol) in an acidic medium to form the corresponding ethers. The modified resins are also heat curable and somewhat more compatible with solvents and co-reactants. These resins can be made by those skilled in the art and many of them are commercially available from a number of sources. All of the amino resins can be modified using typical amounts of conventional modifiers such as polyols, acetates and alkyd resins. The modifiers add flexibility, vary surface appearance, and improve resistance to chemicals and weathering, as is well known in the art. The curing of the amino resins is effected by admixing the resin with the above described adducts of an aromatic sulfonic acid and a bicyclic oxazolidine. The adduct can be used per se or it can be dissolved in a solvent such as an alcohol and/or water. Upon heating the mixture to the curing temperature, the adduct breaks down into the sulfonic acid and volatile amine. The sulfonic acid then catalyzes the curing reaction. The cure is especially rapid at temperatures below 116°C (240°F), e.g., 10 minutes at 93 to 115°C. It is preferred to use the latent catalyst in an amount sufficient to provide the cured amino resin with 0.1 to 5 wt. %, preferably 1 wt. %, of the aromatic sulfonic acid based on the weight of binder solids. The resulting cured resins exhibit outstanding water resistance including the resistance to rusting. The cured resins are hard, tough, with excellent adhesion to substrates and excellent resistance to the deteriorating and destructive action of heat and chemicals, particularly alkalies. The cured resins are particularly useful as films and impregnants for materials which are repeatedly contacted with water and an alkali (e.g., soapy water). Thus, the present compositions can be used as surface coatings for washing machines and for heat- resistant, paper-based laminates (e.g., countertops). Although not essential, it is generally preferred to mix the latent catalyst, the amino resin condensate, and co-reactants, if any, in water or a solvent. The urea and melamine condensates, as well as co-reactants such as glycols, polyethers, and alkyd resins, are soluble in a variety of solvents. Suitable solvents include ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone and isophorone; esters, such as ethyl acetate, butyl acetate and 2-ethoxyethanol acetate; and ether alcohols, such as the methyl, ethyl or butyl ethers of ethylene glycol or diethylene glycol. Alcohols such as ethanol, isopropanol and n-butanol are also used by themselves in some cases. To save expenses, the most efficient, non-alcoholic solvents are ordinarily used in admixture with diluents which are themselves not universal solvents when used alone, but which may not be incorporated with active solvents. Reference is made in this respect to aromatic hydrocarbons, such as benzene, toluene, xylene and aromatic petroleum thinners, as well as the alcohols discussed above. In order to achieve the desired evaporation and drying characteristics in coatings and impregnants, the solvents are combined and balanced in a manner well known in the lacquer, varnish and laminating arts. It is also often convenient to add the adduct as a solution in an organic solvent such as a glycol ether (e.g., 2-ethoxyethanol), an alcohol (e.g., ethanol, isopropanol, or n-butanol); a ketone (e.g., acetone or methyl ethyl ketone) as well as mixtures of two or more of such solvents. Isopropanol and methanol are especially convenient. Desirable performance properties for amino resin coatings containing latent catalysts include low temperature cure, viscosity stability, and no tendency to produce wrinkling. Coatings containing preferred latent catalyst, i.e., p-toluene sulfonic acid 1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane, have good viscosity stability, which is better at 122% neutralization, and cures at low temperatures (e.g., 10 minutes at 100°C) and when coated on substrates produce films with no wrinkles. Conventionally, the amino resins and co-reactants, if any, may contain various other materials such as pigments, colorants, surfactants and fillers. Pigments such as titanium dioxide, antimony oxide, lead oxide, carbon black, chrome yellow, zinc oxide and para red can be used. Best results in preparing enamels are obtained by grinding the pigment with a portion of the solvent and amino resin and then adding the remainder of the solvent and co-reactant (e.g., a glycol, an alkyd resin, or a polyester resin). The enamel is ready for application after addition of the desired amount of the adduct. When varnishes, lacquers or enamels containing the present composition are prepared, layers of suitable thickness of the film-forming material may be applied to metal, wood, or similar surfaces. Complete curing is attained because the conversion to an insoluble film is not dependent upon contact with air. This fact also makes the compositions valuable in the manufacture of laminates of cloth, paper and glass-cloth. Such laminae are impregnated with a solution of the amino resin, curing catalyst, and optional co-reactants. After drying, the impregnated sheets are stacked and cure is effected in a heated press. Many of the catalyzed amino resin compositions are also suitable for molding operations wherein they are introduced into a mold, compressed, and heat cured. Various fillers, dyes and pigments may be incorporated in the molding compositions such as wood flour, talc, alpha-cellulose and zinc sulfide, All such techniques are well known to those skilled in the art. The following examples illustrate compositions within the scope of the present invention. They are not to be construed as being limiting in any manner. All parts are by weight. Surface properties were evaluated using the Tukon Hardness Test (ASTM test method No. D-1474), the Pencil Hardness Test [ASTM test method No. D-3383-75), the Double Methyl Ethyl Ketone Rubs Test (described below), the Crosshatch Test (ASTM test method No. D-3359), the Cleveland 72 Hour Humidity Test (ASTM test method No. D-2247-87), and the Salt Spray Test (150 hours) (ASTM test method No. B-117). The Double Methyl Ethyl Ketone Rubs Test, abbreviated MEK (2X), is carried out by saturating a cloth with methyl ethyl ketone and rubbing the film to be tested back and forth in double rub fashion until the film surface is noticeably attacked. Example 1 This example describes the preparation of a solution containing the preferred latent catalyst which is an adduct of p-toluene sulfonic acid and l-aza-3,7-dioxa-5-ethybicyclo (3.3.0) octane. A total of 55.1 g of methanol and 5.2 g of water was charged to a suitable reaction vessel equipped with a stirrer and 22.5 g of crystalline p-toluene sulfonic acid were added. The resulting mixture was stirred until it was clear and homogeneous. To this mixture was added slowly 17.2 g of 1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane. After the addition the mixture was stirred for 15 minutes. The solution was approximately 20% active p-toluene sulfonic acid (p-TSA). The amount of amine used was sufficient to provide 100% theoretical neutralization of the acid. Example 2 This example describes the preparation of a solution containing one of the preferred latent catalysts which is an adduct of p-toluene sulfonic acid and the bicyclic oxazolidine 1-aza-3,7,dioxa-5-hydroxymethylbicyclo (3.3.0) octane. A total of 46.6 g of methanol and 13.9 g of water is charged to a suitable reaction vessel equipped with a stirrer and 22.5 g of crystalline p-toluene sulfonic acid is added. The resulting mixture is stirred until it is clear and homogeneous. To this mixture is added slowly 17.0 g of 1-aza-3,7,dioxa-5-hydroxymethylbicyclo (3.3.0) octane. After the addition the mixture is stirred for 15 minutes. The solution should be approximately 20% active p-toluene sulfonic acid. The amount of amine used is sufficient to provide 100% theoretical neutralization of the acid. Example 3 This example describes the preparation of a solution containing one of the preferred latent catalysts which is an adduct of dodecyl benzene sulfonic acid and 1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane. A total of 25.0 g of dodecyl benzene sulfonic acid and 64.0 g of isopropanol was charged to a suitable reaction vessel equipped with a stirrer and was mixed until the mixture was homogeneous. To this mixture was added slowly 11.0 g of l-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane. After the addition the mixture was stirred for 15 minutes. The solution was approximately 25% active dodecyl benzene sulfonic acid. The amount of amine used was sufficient to provide 100% theoretical neutralization of the acid. Example 4 This example describes the preparation of a solution containing one of the preferred latent catalysts which is an adduct of dinonylnaphthalene monosulfonic acid and 1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane. A total of 25.0 g of 2-butoxy ethanol and 42.0 g of isopropanol was charged to a suitable reaction vessel equipped with a stirrer and 25.0 g of dinonylnaphthalene monosulfonic acid was added. To the resulting mixture was added slowly 8.0 g of 1-aza-3,7,dioxa-5-ethylbicyclo (3.3.0) octane. After the addition the mixture was stirred for 15 minutes. The solution was approximately 25% active dinonylnaphthalene monosulfonic acid. The amount of amine used was sufficient to provide 100% theoretical neutralization of the acid. Example 5 This example describes the preparation of a solution containing the latent catalyst which is an adduct of dinonylnaphthalene disulfonic acid and 1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane. A total of 20.5 g of isobutanol, 35.0 g of isopropanol and 6.2 g of water was charged to a suitable reaction vessel equipped with a stirrer and 25.0 g of dinonylnaphthalene disulfonic acid was added. The resulting mixture was mixed until it was homogeneous. To this mixture was added slowly 13.3 g of 1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane. After the addition the mixture was stirred for 15 minutes. The solution was approximately 25% active dinonylnaphthalene disulfonic acid. The amount of amine used was sufficient to provide 100% theoretical neutralization of the acid. Example 6 This example describes the evaluation of the latent catalyst of Example 1, which is an adduct of p-toluene sulfonic acid and 1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane, in a curable amino resin. The amino resin solution was prepared by solvating a butylated urea formaldehyde resin in a suitable solvent, e.g., butanol. Although a butylated urea formaldehyde resin was used for this example, other curable amino resins can be substituted with similar results. These include urea- or melamine-aldehyde condensation products or reaction products thereof with alcohols (e.g., methylol ureas or methylol melamines) and alkylated derivatives thereof (e.g., methylated or butylated derivatives). A sufficient quantity of the catalyst solution of Example 1 was added to the amino resin solution to yield 0.5% p-toluene sulfonic acid based on total resin solids. The amino resin solution was then cast as a film on an iron phosphated steel panel to a wet film thickness of 0.10 mm (4 mils) using a doctor blade. The film was then heated in a forced draft oven for 10 minutes at 104°c. This cure cycle was sufficient to provide curing of the amino resin. The cured amino resin film was hard and tough, with excellent adhesion and excellent resistance to the destructive action of heat and chemicals. Example 7 This example describes the preparation and evaluation of a polyester coating containing the latent catalyst of Example 1 (designated A), p-toluene sulfonic acid (designated B), and other latent catalysts containing p-toluene sulfonic acid (designated C to E). A. Preparation of Catalyst Solutions The catalyst solutions were prepared by dissolving the following catalysts in the indicated solvent: (A) p-toluenesulfonicacid/1-aza-3,7-dioxa-5-ethyl bicyclo (3.3.0) octane adduct of Example 1 in methanol/water (8% water); (B) p-toluenesulfonic acid in isopropanol; (C) p-toluenesulfonic acid/4,4-dimethyl-1-oxa-3-aza-cyclopentane adduct, one of the oxa-azacyclopentane adducts of U.S. Pat. No. 4,200,729 , in isopropanol; (D) p-toluenesulfonic acid/morpholine adduct in methanol/isopropanol (equal parts by weight); and (E) p-toluenesulfonic acid/2-amino-2-ethyl-1,3-propanediol adduct in methanol/isopropanol (equal parts by weight). The active solids content of the catalyst solution was 25% except for (A) where the solids were reduced to 20% to form a stable solution. B. Preparation of Stock Polyester Solution A stock polyester coating solution was prepared by combining 609.04 g of high solids thermosetting, oil-free clear polyester resin having a hydroxyl number of about 150, a maximum acid number of 10 (on a solids basis), and a viscosity of 6000 to 14,000 mPa·s (cps). which is supplied at 85 wt. % solids in n-methoxy propyl acetate by Cargill Inc. as Polyester Resin 5776; 172.55 g of a hexamethoxymethylmelamine crosslinking agent which is supplied in a liquid form at 98% plus non-volatile content by American Cyanamid under the trade name Cymel 303 or by the Monsanto Co. under the trade name Resimene 747; 135.93 g of 2-methoxypropyl acetate; and 2.76 g of leveling agent (DISLON® 1980). Then 79.72 g of 2-methoxypropyl acetate were added to adjust the viscosity. The resulting clear solution had a viscosity of 249 mPa·s (cps). at 25°C, a solids content of 69.3%, and a polyester/amino resin (HMMM) ratio of 75/25. C. Preparation and Evaluation of Coatings To the stock polyester solution was added, with stirring, sufficient quantities of the various catalyst solutions to yield 0.5% p-toluene sulfonic acid based on total resin solids. The various coating solutions are designated A to F to indicate the catalyst used. The coatings were then separately cast as films on iron phosphated steel panels using a doctor blade. The wet films (0.10 mm (4 mils) thick) were cured for 10 minutes at the indicated temperature in a BYK Gradient oven. The films were evaluated for Double MEK Rubs and Tukon Hardness. The results are shown in Tables 1 and 2. Double MEK Rubs Temp. (°C) SAMPLE A SAMPLE B SAMPLE C SAMPLE E 93 14 24 5 11 104 25 34 15 23 116 51 70 35 50 127 100 100 100 100 The results show that the adduct of the present invention exhibited faster cure response than the other amine-neutralized adducts as evidenced by the better solvent resistance of the cured films. Films cast using catalyst solution D (the p-toluene sulfonic acid/morpholine adduct) yellowed badly and were dropped from further evaluation as not being of any practical value. Tukon Hardness Temp. (°C) SAMPLE A SAMPLE B SAMPLE C SAMPLE E 93 2.5 5.8 0 1.09 104 9.62 11.4 3.14 8.11 116 11.8 12.6 9.09 12.5 127 14.3 13.7 12.4 13.8 The results show that the adduct of the present invention exhibited faster cure response than the other amine-neutralized adducts as shown by the higher film hardness of the cured film. Example 8 The viscosity stability at 50°C of the various polyester coatings of Example 7 was evaluated. The results are shown in Table 3. Viscosity Stability [mPa·s (cps)] Hrs Control A B C E 0 250 250 250 250 250 12 --- --- 422 --- --- 24 --- 306 --- 272 284 36 302 --- 528 --- --- 96 --- 955 --- 430 778 108 314 --- 1450 --- --- 120 --- 1080 --- 499 915 132 314 --- 1580 --- --- 288 --- 1490 --- 792 1370 300 296 --- 2200 --- --- 348 --- 1700 --- 1220 1800 360 326 --- 2990 --- --- 492 --- 2590 --- --- 2220 504 332 --- 4830 --- --- Control is the polyester stock solution The results show that the adducts of the present invention exhibited better viscosity stability than the unblocked acid and only slightly less stability than the slower curing adduct (e.g., E). Further addition of the amine portion of the adduct will improve the viscosity stability without necessarily inhibiting the cure response (see Table 4 in Example 9). Example 9 A test was run to determine whether any of the catalysts promote wrinkling. Coatings were prepared by adding solutions of catalysts A to F to the polyester stock solution of Example 7 in amounts sufficient to provide 0.5% p-toluene sulfonic acid based on total resin solids. The coatings were drawn down on iron phosphated panels using a 0.15 mm (6 mil) wet applicator. The panels were immediately placed in gradient ovens with zone settings of 163°C, 177°C, 191°C and 204°C and cured for 10 minutes. None of the coated test panels showed any signs of wrinkling. Catalyst E, the p-toluene sulfonic acid/morpholine adduct, did cause severe yellowing of the cured film at the higher temperatures. Example 10 The polyester stock coating solution of Example 7 was catalyzed with solutions of p-toluene sulfonic acid/1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane adduct from Example 1 which were neutralized to 100% and neutralized to 122%. These polyester coatings are designated A-100% and A-122%. They were evaluated as in Example 7. The results are shown in Table 4 together with the results for a polyester coating containing the solution of catalyst B from Example 7. Double MEK Rubs and Tukon Hardness Temp °C A - 100% A - 122% B MEK (2X) Tukon MEK (2X) Tukon MEK (2X) Tukon 93 17 1.54 13 1.32 45 8.18 104 31 10.40 34 8.60 77 10.40 116 90 13.00 79 11.20 100 11.00 127 100 13.20 100 11.90 100 11.40 The results show that the addition of excess bicyclic oxazolidine did not materially affect the cure response. Example 11 The viscosity stability at 50°C of the polyester coatings of Example 10 was evaluated. The results are shown in Table 5. Viscosity Stability at 50°C [mPa·s (cps)] Hours Control A-100% A-122% SAMPLE B 0 259 214 219 239 72 286 698 678 1270 96 294 700 728 1290 168 286 902 808 1520 264 311 1120 985 1840 648 340 1430 1190 3040 Stock solution is used as the control. The results show that the addition of excess bicyclic oxazolidine improved the viscosity stability. Example 12 This example describes the preparation and evaluation of polyester coatings containing the latent catalyst of Example 3 (designated F) and another latent catalyst (designated G) which is an adduct of dodecylbenzene sulfonic acid and one of the oxa-azacyclopentane adducts of U.S. Pat. No. 4,200,729 . A. Preparation of Catalyst Solutions The catalyst solutions were prepared by dissolving the following catalysts in the indicated solvent system: (F) Dodecylbenzene sulfonic acid/1-aza-3,7-dioxa-5-ethyl bicyclo (3.3.0) octane adduct of Example 3 in isopropanol; (G) Dodecylbenzene sulfonic acid/4,4-dimethyl-1-oxa-3-aza-cyclopentane adduct of '729 patent in isopropanol. The active solids content of both catalyst solutions was 25%. B. Preparation and Evaluation of Coatings To the stock polyester solution of Example 7 was added, with stirring, sufficient quantities of the two catalyst solutions to yield 0.5% dodecyl benzene sulfonic acid based on total resin solids. The two coating solutions are designated F and G to indicate the catalyst used. The coatings were separately cast as films on zinc phosphated steel panels using a doctor blade. The wet films (0.10 mm (4 mils) thick) were cured for 10 minutes at the indicated temperature in a Byk Gradient oven. The films were evaluated for Tukon Hardness and Pencil Hardness. The results are shown in Table 6. Temp (°C) F G Tukon Pencil Hardness Tukon Pencil Hardness 107 1.7 F-H 0.5 HB-F 121 15.0 2-3H 11.7 2-3H The results show that the adduct of the present invention exhibited faster cure response than the other amine neutralized adduct as evidenced by the higher film hardness of the cured film. Example 13 This example describes the preparation and evaluation of a polyarylic coating containing the latent catalyst of Example 1 (designated A), p-toluene sulfonic acid (designated B), and other latent catalysts containing p-toluene sulfonic acid (designated C and E). A. Preparation of Catalyst Solutions Preparation of the catalyst solutions is described in Example 7. B. Preparation of Polyacrylic Stock Solution A stock acrylic solution was prepared by combining 608.69 g. of a high solids, thermosetting, clear acrylic resin having a hydroxyl number of 86, an acid number of 28 (on a solids basis), and a viscosity of 5000 to 9000 mPa·s (cps) which is supplied at 75% wt. % solids in methyl amyl ketone by Rohm & Haas as Acryloid AT 400; 152.17 g of the amino resin crosslinking agent (Cymel 303) described in Example 7; 119.57 g of 2-methoxypropyl acetate; and 119.57 g of methyl isobutyl ketone. The resulting clear solution had a viscosity of 242 mPa·s (cps) at 25°C, a solids content of 60.9%, and an acrylic/amino resin (HMMM) ratio of 75/25. C. Preparation and Evaluation of Coatings Using the catalyst solutions and procedures described in Example 7, acrylic coatings were prepared and evaluated. The Double MEK Rubs and Tukon Hardness test results are shown in Tables 7 and 8. Double MEK Rubs Temp. (°C) SAMPLE A SAMPLE B SAMPLE C SAMPLE E 93 38 45 12 25 104 87 77 21 70 116 100 100 94 100 127 100 100 100 100 The results show that the adduct of the present invention exhibited faster cure response than the other amine-neutralized adducts as shown by the higher film hardness of the cured film. Tukon Hardness Temp. (°C) SAMPLE A SAMPLE B SAMPLE C SAMPLE E 93 6.37 8.18 2.32 5.14 104 9.39 10.4 6.09 9.44 116 10.5 11.0 9.00 10.9 127 11.2 11.4 10.1 11.2 The results show that the adduct of the present invention exhibited faster cure response than the other amine-neutralized adducts as shown by the higher film hardness of the cured film. Example 14 This example describes the evaluation of the catalyst of Example 1 (catalyst A) at 100% and 122% neutralization in another acrylic coating and compares the test results obtained with these coatings (designated A - 100% and A - 122%) with the test results obtained with coatings containing catalyst C of Example 7 and the additional latent catalysts (designated H and I) described below. A. Preparation of Catalyst Solutions The catalyst solutions were prepared by dissolving the following catalysts in the indicated solvent: A-100% p-toluene sulfonic acid/1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane of Example 1 neutralized with 100% amine and dissolved in methanol/water; A-122% p-toluene sulfonic acid/1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane of Example 1 neutralized with 122% amine and dissolved in methanol/water; C - p-toluene sulfonic acid/4,4-dimethyl-1-oxa-3-azacyclopentanol adduct (of Example 7) dissolved in isopropanol; H - p-toluenesulfonic acid/triethylamine adduct dissolved in isopropanol; I - p-toluenesulfonic acid/morpholine adduct dissolved in 2-butoxy ethanol. The active acid content for each catalyst is 20% for A - 100% and A - 122%; 25% for C; 25% for H; 18.5% for I. B. Preparation of Acrylic Stock Solution An acrylic stock solution was prepared by combining 58.33 g of a high solids, thermosetting, clear acrylic resin having a hydroxyl number of 155, an acid number of 5 (on a solids basis), and a viscosity of 6000 to 10,000 mPa·s (cps) which is supplied at 84 wt. % solids in n-butyl acetate by Rohm & Haas as Acryloid QR 1120; 21.00 g of the amino resin crosslinking agent (Cymel 303) described in Example 7; and 20.67 g of a 1:1 mixture (by weight) of xylene and methyl ethyl ketone. The resulting solution had an acrylic to amino resin ratio of 70/30, and a total resin solid of 70%. C. Preparation and Evaluation of Coatings Polyacrylic coatings were prepared by adding the solutions of catalysts A-100%, A-122%, C, H, and I to the stock solutions in amounts sufficient to provide 0.5% p-toluene sulfonic acid based on total resin solids. Films were cast from the acrylic coating at 23-25 µm wet (0.9-1.0 wet mil) on iron phosphated steel panels. The films were tested for Tukon Hardness and Double MEK Rubs. The results are shown in Table 9. Coating H was not evaluated because the film was wrinkled. Temp. (°C) A-100% A-122% C I 93 Tukon 6.98 7.92 4.01 4.19 MEK (2X) 75 100mar 38 70 104 Tukon 10.1 9.55 7.46 7.37 MEK (2X) 100 100 78 84 116 Tukon 11.9 11.7 10.3 10.2 MEK (2X) 100 100 100 100 127 Tukon 13.1 12.5 12.5 12.5 MEK (2X) 100 100 100 100 The coatings were then separately cast at 23-25 µm wet (0.90-1.0 wet mil) on iron phosphated steel panels and cured for 15 minutes at 127° (260°F). The films were tested for Pencil Hardness, Tukon KNH25 Hardness, Double MEK rubs, Crosshatch (% loss), Cleveland Humidity (72 h ), and Salt Spray. The results are shown in Table 10. Test A-100% A-122% C I Pencil Hardness H-2H H-2H H-2H H-2H Tukon KNH25 13.8 12.7 13.9 12.3 MEK(2X) Rub 100 100 99 100 mar Crosshatch (% loss) 0 0 0 0 Cleveland Humidity (72 hrs) 6FM 6M 6MD 6D Salt Spray (150 hrs) 2F/5mm 2F/5mm 3F/5mm 4F/6mm In the above table the abbreviations F, M, D, MD, FM means few, medium, dense, medium dense, and few medium. Blister rating is mm. creepage from the scribe line (ASTM test method No. D-714-8). The results show improvement in cure response, humidity resistance, and salt spray (i.e., corrosion, resistance). Example 15 The viscosity stability of the polyacrylic coating of Example 14 was tested at 50°C. The sample neutralized at 122% was more stable than the sample neutralized at 100%. Example 16 This example describes the evaluation of the catalyst of Example 1 (Catalyst A) at 100% and 122% neutralization in a polyester coating and compares the test results obtained with these coatings (designated A-100% and A-122%) with the test results obtained with coatings containing Catalyst C of Example 7. A. Preparation of Polyester Stock Solution A stock polyester coating solution was prepared by combining 60.9 g of a high solids, thermosetting, oil-free, clear polyester resin having a hydroxyl number of about 150, a maximum acid number of 10 (on a solids basis), and a viscosity of 6000 to 14,000 mPa·s (cps). which is supplied at 85 wt. % solids in n-methoxy propyl acetate by Cargill Inc. as Polyester Resin 5776; 17.3 g of the amino resin crosslinking agent (Cymel 303) described in Example 7; 21.5 g of 2-methoxypropyl acetate; and 0.3 g of flow and leveling agent (Dislon® L-1980). The resulting clear solution had a polyester to amino resin ratio of 80/20 and a total resin solids of 69%. B. Preparation and Evaluation of The Coating To the stock polyester solution was added, with stirring, sufficient quantities of the catalyst solutions A-100%, A-122%, and C to yield 0.5% p-toluene sulfonic acid based on total resin solids. Films were cast from the polyester coatings at 23-25 µm wet (0.9-1.0 wet mil) on iron phosphated steel panels and cured for 10 minutes at the indicated temperature. The films were tested for Tukon Hardness and Double MEK Rubs. The results are shown in Table 11. The results show that the adduct of the present invention exhibited faster cure response than the other amine-neutralized adducts as shown by the higher film hardness of the cured film. The polyester coatings were also evaluated for their viscosity stability at 50°C. The results are shown in Table 12. Viscosity Stability at [mPa·s (cps)] 50°C Time (h) A-100% A-122% C 0 270 270 270 24 422 458 274 48 708 762 421 120 875 914 574 192 964 930 696 285 1090 1080 927 The results show that the long term viscosity stability of the sample neutralized to 122% was not significantly greater than that of the sample neutralized to 100% and that the 100% and 122% neutralized samples were somewhat less stable than sample C (i.e., the p-toluene sulfonic acid/4,4-dimethyl-1-oxa-3-aza-cyclopentane adduct).

Claims: A thermally-decomposable composition comprising a bicyclic oxazolidine adduct of an aromatic sulfonic acid, the adduct having the formula: wherein A is phenyl or naphthyl; x is 1 to 8; y is 0 to 7; the sum of x and y is no greater than 8; z is 8-x-y when A is naphthyl and z is 6-x-y when A is phenyl; q is equal to or greater than 0.5; R is an alkyl, halogen, haloalkyl, or alkoxy group; R' is an organic group; and R" is hydrogen or a C 1 -C 6 alkyl group. The composition of Claim 1, wherein R is an alkyl or alkoxy group; R' is an alkyl or hydroxy alkyl group; and R" is hydrogen. The composition of Claim 1 or 2, wherein the aromatic sulfonic acid is an alkyl-benzene sulfonic acid preferably para-toluene sulfonic acid or dodecylbenzene sulfonic acid or an alkyl-naphthalene sulfonic acid, preferably dinonylnaphthalene sulfonic acid or dinonylnaphthalene disulfonic acid. The composition of Claims 1 to 3, wherein the bicyclic oxazolidine is 1-aza-3,7-dioxa-5-ethylbicyclo (3.3.0) octane. A composition comprising a curable amino resin and a catalytically effective amount of a thermally-decomposable adduct of an aromatic sulfonic acid and a bicyclic oxazolidine adduct according to Claims 1 to 4 and optionally further comprising a polyfunctional co-reactant capable of combining with the amino resin during heat curing. The composition of Claim 5, wherein the amino resin is a urea condensate, a melamine condensate, a benzoguanamine condensate, or an acetoguanamine condensate. The composition of Claim 6, wherein the condensate is dissolved in water and/or a solvent. The composition of Claim 5, wherein the amino resin is modified with an alcohol. The composition of Claim 5, wherein the co-reactant contains hydroxyl, carboxyl, or amide groups or a combination thereof and wherein preferably the co-reactant is a polyacrylic resin or a polyester resin.

Inventors: CALBO LEONARD J, COUGHLIN ROBERT D, CALBO, LEONARD J., COUGHLIN, ROBERT D.
Applicants: KING INDUSTRIES INC, KING INDUSTRIES, INC.
Application year: 1992
Main classification: C08G85
IPC codes: C08K5, C09D161, C08G12, C09D167