Fabrication methods for micromechanical elements

Abstract: A process in which concave surfaces to form undercut edges can be made and the application of such process to making micromechanical devices. Concave surfaces forming undercut edges are are made in a wall of a stationary structure extending from a planar surface by growing a convex bumper into the wall. The bumper forms a convexo-concave relationship with the wall. The bumper is then removed from the wall in such a manner as to preserve the concave, undercut surface of the wall. The stationary structure and the planar surface is then further processed by coating with a sacrificial layer, and a structural layer. The structural layer is patterned into a movable structure that is held onto the stationary structure by the curved, undercut edge such as the slot in a slider. Final processing includes removing the sacrificial layer to free the movable structure from the stationary structure.

Description: This invention relates generally to micromechanical elements, such as movable joints, gears, and sliders and more particularly concerns fabrication methods for making high precision micromechanical elements. Micromechanical elements with joints that slide or rotate have many uses in miniature pin joints, gears, cranks, slides, and other mechanisms. These elements can be made in a variety of ways. In US-A-4,740,410 by Muller et al., micromechanical sliding or rotating elements are made by following the process steps of: 1 ) depositing a sacrificial layer of glass on a substrate, 2) depositing and forming a structural layer of polysilicon for the sliders or gears, 3) depositing a second sacrificial layer of glass, 4) depositing and forming a second structural layer of polysilicon for the rails or pins, 5) removing the sacrificial layers to free the gears and sliders from both the substrate and the pins and rails. This process results in fixed axle pin joints or fixed rail sliders. Once loosened, the fixed gears and sliders rest on the substrate. In operation, undesirable amounts of friction are generated between the gears and sliders, and the substrate. A process for making self-constraining joints is also disclosed in US-A-4,740,710 Self-constraining joints may slide and rotate at the same time. These joints are constructed using a small variation of the basic process discussed above. The self-constraining joints are differentiated from the fixed joints by constructing a flange on the pins and rails underneath the gears and sliders to keep them in place. The pins and rails can either be fixed to the substrate or left free to slide across the substrate. The pins and rails are constructed using a portion of the normally first sacrificial glass layer to form the pin or rail and the first structural polysilicon layer to form the flange. The flange is formed with an etch undercut process. Etch undercutting processes are in general not easily controllable. The glass/polysilicon joint is also the weakest part of the structure and tends to break under stress. Further information about this process can also be found in a paper by Muller et al: "Integrated Movable Micromechanical Structures for Sensors and Actuators", IEEE Transactions on Electron Devices vol. 35, no. 6, June 1988. Attention is also directed to the following related U.S. application Serial No. 07/725,173, filed 3 July 1991 (corresponding to EP-A-521,713), entitled Manufacture of a Micromechanical Element with Two Degrees of Freedom. Briefly stated and in accordance with the present invention, there is provided a process for making a micromechanical structure comprising (a) forming a concave shaped undercut edge by providing a member having a generally planar surface with wall means extending from said surface, growing bumper means into said wall means and forming a convexo-concave relationship with said wall means, removing said bumper means from said wall means such that said wall means retains a concave shaped undercut edge; characterized by (b) forming a sacrificial layer on at least a portion of the remaining wall means, forming a structural layer on at least a portion of said sacrificial layer, patterning said structural layer, removing said sacrificial layer such that said remaining wall means and said patterned structural layer are movable relative to each other. The undercut edge is made using a two step patterning process. The first step is to define the edge or wall to be undercut using conventional photoresist and etching techniques. The second step is to grow a bumper into the edge or wall to be undercut, the bumper forming a convexo-concave relationship with the edge or wall. That is, the bumper will bulge outward into the edge or wall and the edge or wall will bulge inward to accommodate the bumper. The term convexo-concave as used herein shall mean any curve type relationship which could, for instance, be circular, elliptical, etc. The conclusion of this step is removal of the bumper while the edge or wall retains its concave shape. An undercut edge has now been produced. A first type of sliding or rotating micromechanical element is built on a substrate with a projecting pin or rail and with concave sides built using the convexo-concave, undercutting process described above. Since the sides are concave, the pin or rail is necked. A gear or slider is formed around the pin or rail so that it is restrained from lifting up and off the pin or rail. The gear or slider is formed around the pin or rail by first coating the pin or rail with a relatively uniform sacrificial layer. Then a structural layer is deposited on the sacrificial layer. After a gear or slider is formed out of the structural layer, the sacrificial layer is etched away releasing the gear from the pin or the slider from the rail. By using a sacrificial layer to define the shape of the structural layer, a gear or slider can be built around its pin or rail and will conform to the concave shape of the pin or rail. The gear or slider will be narrower where the pin or rail is narrower and will not be able to move up the wider section and up off the pin or rail. A second type of gear or slider may also be built with this process. Instead of building a pin which projects outward from the substrate, a hole that projects inward towards the substrate is built. The sides of the hole are concave, again made using the convexo-concave undercutting process described above, therefore the width of the hole is narrower at the top of the hole than the width in the middle of the hole. As in the case of a male gear or slider, a relatively uniform sacrificial layer is provided in the hole and on the surrounding area. A structural layer is then deposited on the sacrificial layer and fabricated into a gear or slider. When the sacrificial layer is removed the gear or slider is free to move within the confines of the hole. Again, by using a sacrificial layer to define the shape of the structural layer, a gear or slider can be built around the hole and will conform to the concave shape of the hole. The gear or slider will be wider where the hole is wider and will not be able to move up the narrower section and out of the hole. Preferably, said member includes a second generally planar surface and said wall means is provided by masking and etching said second generally planar surface and said member to expose said first named generally planar surface of said member. According to one embodiment said masking and etching forms a structure protruding from said first named generally planar surface of said member, said wall means being located on said protruding structure. According to another embodiment, said masking and etching forms a depression in said member which is defined by wall means and said first named generally planar surface. Preferably said bumper means is oxide and said sacrificial layer comprises one of silicon oxide or silicon nitride and said structural layer comprises one of polysilicon, silicon nitride, metal silicide, or metal. According to one embodiment, said wall means is annular and said structural layer has an annular recessed cavity receiving said protruding structure. According to another embodiment, said wall means is elongated and said structural layer has a slot receiving said protruding structure. The step of removing one of said means from the other of said means such that the remaining means is attached to said member may comprise removing said bumper means from said wall means, or removing said wall means from said bumper means. Preferably, said step of providing a member includes providing a substrate and forming one or more successive layers on the substrate. Preferably, said step of removing one of said means comprises etching said oxide bumper to remove the same from said wall means of said protruding structure or depression while retaining the concave surface of said wall means. Preferably, said patterning step comprises patterning said structural layer to form a moving structure for movement relative to said protruding structure or depression and exposing portions of said sacrificial layer. Preferably, said step of removing said sacrificial layer comprises etching said sacrificial layer to release said moving structure from said protruding structure or depression and providing for relative movement between said moving structure and said protruding structure or depression. According to one embodiment, said step of forming one or more successive layers on said substrate comprises: forming a first nitride layer upon said substrate; forming a doped polysilicon layer upon said first nitride layer; forming a second nitride layer upon said doped polysilicon layer; said masking and etching step comprises masking and etching said second nitride layer and said doped polysilicon layer to expose at least a portion of said first nitride layer to form (1) a structure with at least one wall means protruding from said exposed portion of said first nitride layer or (2) a depression in said nitride layer and said doped polysilicon layer which is defined by wall means and said exposed first nitride layer; and said step of forming a sacrificial layer comprises forming a sacrificial layer on at least a portion of said exposed portion of said first nitride layer and (1) said protruding structure or (2) said wall means and at least a portion of the remaining portion of the second nitride layer, respectively. In an alternative embodiment said masking and etching step comprises masking and etching said second nitride layer, said doped polysilicon layer and said first nitride layer to expose at least a portion of said substrate and to form (1) a structure with at least one wall means protruding from said exposed portion of said substrate or (2) a depression in said second nitride layer, said doped polysilicon layer and said first nitride layer which is defined by said wall means and said exposed portion of said substrate; and said step of forming a sacrificial layer comprises forming a sacrificial layer on said at least a portion of exposed portion of said substrate and (1) said protruding structure or (2) said wall means and at least a portion of the remaining portion of said second nitride layer, respectively. According to another embodiment, said step of forming one or more successive layers comprises forming a doped polysilicon layer upon said substrate and forming a nitride layer upon said doped polysilicon layer; said masking and etching step comprises masking and etching said doped polysilicon layer and said nitride layer to expose at least a portion of said substrate and to form (1) a structure with at least one wall means protruding from said exposed portion of said substrate or (2) a depression in said nitride layer and said doped polysilicon layer which is defined by wall means and said exposed portion of said substrate; and said step of forming a sacrificial layer comprises forming a sacrificial layer on at least a portion of said exposed portion of said substrate and (1) said protruding structure or (2) said wall means and at least a portion of the remaining portion of said nitride layer, respectively. According to a further embodiment said step of forming one or more successive layers comprises: forming a nitride layer upon said substrate; said masking and etching step comprises masking and etching said nitride layer and the substrate to expose at least a portion of said substrate and to form (1) a structure with at least one wall means protruding from said exposed portion of said substrate or (2) a depression in said nitride layer and said substrate which is defined by wall means and said exposed portion of said substrate; and said step of forming a sacrificial layer comprises forming a sacrificial layer on at least a portion of said exposed portion of said substrate and (1) said protruding structure or (2) said wall means and at least a portion of the remaining portion of said nitride layer, respectively. Figure 1 shows a top view of a gear on a pin; Figure 2 shows a top view of a slider on a rail; Figure 3 shows a cross sectional view of a substrate after first and second nitride deposition and doped polysilicon deposition to form a first structural layer; Figure 4 shows a cross sectional view of the substrate of Figure 3 after masking and etching the first structural layer; Figure 5 shows a cross sectional view of the substrate of Figure 4 after oxide bumpers are grown; Figure 6 shows a cross sectional view of the substrate of Figure 5 after the oxide bumpers have been etched away; Figure 7 shows a cross sectional view of the substrate of Figure 6 after deposition of a sacrificial layer; Figure 8 shows a cross sectional view of the substrate of Figure 7 after deposition of a second structural layer; Figure 9 shows a cross sectional view of the substrate of Figure 8 after patterning the structural layer; Figure 10 is a cross sectional view of the completed gear shown in Figure 1 or the completed slider shown in Figure 2 taken through section line 10-10; Figure 11 is a cross sectional view of an alternative process step for Figure 9; Figure 12 is a cross section of an alternative gear or slider structure built using the alternative process step shown in Figure 11; Figure 13 shows a cross sectional view of a substrate after first and second nitride deposition and doped polysilicon deposition to form a first structural layer; Figure 14 shows a cross sectional view of the substrate of Figure 13 after masking and etching the first structural layer; Figure 15 shows a cross sectional view of the substrate of Figure 14 after oxide bumpers are grown; Figure 16 shows a cross sectional view of the substrate of Figure 15 after the oxide bumpers have been etched away; Figure 17 shows a cross sectional view of the substrate of Figure 16 after deposition of a sacrificial layer; Figure 18 shows a cross sectional view of the substrate of Figure 17 after deposition of a second structural layer; Figure 19 shows a cross sectional view of the substrate of Figure 18 after patterning the structural layer; Figure 20 is a cross sectional view of a completed gear from the sequence of process steps shown in Figures 13-19; Figure 21 shows a cross sectional view of a substrate after nitride deposition and doped polysilicon deposition to form a first structural layer; Figure 22 shows a cross sectional view of the substrate of Figure 21 after masking and etching the first structural layer; Figure 23 shows a cross sectional view of the substrate of Figure 22 after oxide bumpers are grown; Figure 24 shows a cross sectional view of the substrate of Figure 23 after the oxide bumpers have been etched away; Figure 25 shows a cross sectional view of a substrate after nitride deposition; Figure 26 shows a cross sectional view of the substrate of Figure 25 after masking and etching to form a protruding structure; Turning now to Figure 1, a top view of a gear 26 rotating around a pin 28 is shown. Figure 2 depicts a top view of a slider 30 sliding on a rail 32. Both of these structures are built using the same process sequence and have the same cross section as taken through 10-10 and shown in Figure 10, so they will be described together. All of the process steps for deposition of materials, etching and patterning are known in the art. Therefore, the description will focus on the order and results of each step and not on the specific details required to perform each step. The micromechanical elements are built upon a substrate. In this embodiment, silicon is used for the substrate. Silicon is ideal since it is not damaged during high temperature process steps. Other materials, such as ceramics or some metals, could be substituted. Figure 3 illustrates the substrate 10 after depositing a structural layer 12. The structural layer 12 is actually comprised of three layers, a first nitride layer 14, a doped polysilicon layer 16, and a second nitride layer 18. The structural layer 12 undergoes two phases of patterning. The first is done using a conventional photoresist and etching process. The photoresist is used to define those areas that will become pins and/or rails. Those areas of the structural layer 12 that will not become pins and/or rails are completely etched away. When this step is completed, the remaining structural layer 12 will project or protrude from the surface of the substrate 10 as in Figure 4. The projecting or protruding remains of the structural layer 12 will later become the pin 28 shown in Figure 1or the rail 32 shown in Figure 2. As shown in Figure 5, the second patterning phase commences with growing oxide bumpers. Oxide bumpers 20 are grown on the doped polysilicon layer 16 using a conventional oxidation process. The oxide grows on the exposed edge or wall of the doped polysilicon layer 16. The oxide bumper 20 grows both inward and outward in a curved shape since the constraints put on it from the first and second nitride layers 14,18 control the shape of the bumper. The oxidation rate will be slowest at the interface of the doped polysilicon layer 16 with each of the nitride layers 14,18. The oxide bumpers 20 are grown until the profile of the oxide growth is convex and forming a convexo-concave relationship with the doped polysilicon layer 16. Oxidation rates can be controlled by changing the dopant profile of the doped polysilicon layer 16 either by ion implantation or by controlling in situ dopant in the doped polysilicon layer 16. Since control of polysilicon oxidation rates is known, the depth and profile of the oxide bumper 20 can be precisely controlled. Therefore, the concave shape of the pin 28 profile shown in Figure 1 can be precisely controlled. The growth and control of oxide bumpers is discussed in US-A-4,400,866 and US-A-4,375,643 by Bol and Keming, both titled Application of Grown Oxide Bumper Insulators to a High Speed VLSI SASMEFET. Oxide removal as shown in Figure 6 is the last step of patterning the first structural layer 12 which has become either the pin 28 or the rail 32 as shown in Figures 1 and 2. The convexo-concave relationship of the oxide bumper 20 to the doped polysilicon layer 16 allows construction of a pin 28 or rail 32 with concave sides. Since the oxide bumpers had an convex profile, when they are etched. away the resulting wall will have a concave. Any convexo-concave profile, where the oxide bumper 20 bulges outward and the doped polysilicon layer 16 bulges inward , where the head of the pin 28 or rail 32 is larger than the body 31 of the pin 28 or rail 32 will work. Since the pin 28 or rail 32 is wider at the head 29, a gear or slider can be constructed around the pin 28 or rail 32 that will be held on by the head 29 of the pin 28 or rail 32. The next step is forming the sacrificial layer 22 as shown in Figure 7. In this embodiment, thermal oxide growth is used to coat the substrate 10 and the surfaces of the pin 28 or rail 32 to form the sacrificial layer 22. However, any material with a sufficiently high etching rate compared to polysilicon that can withstand the temperatures and processing of the further steps and which conforms to the shape of the pin when deposited may be used. Oxide is grown on the surface of the substrate 10 and the sides of the pin 28 or rail 32 which are made from silicon and doped polysilicon respectively. Since the top surface of the pin 28 or rail 32 is nitride, no oxide can be grown there. To insure that the whole structure is covered with oxide, a TEOS oxide deposition is used after oxide has been grown on the substrate 10 and the side surfaces of the pin 28 or rail 32. The result is that the oxide layer on the top surface of the pin 28 or rail 32 is thinner than the oxide layer on the substrate 10 and the sides of the pin 28 or rail 32, as shown in Figure 7. The structure is now ready for formation of the structural layer 24, as shown in Figure 8. Polysilicon has been used in this embodiment although other materials may be substituted such as silicon, metals, or metal silicides. The structural layer 24 is separated from the pin 28 or the rail 32 and the substrate 10 by the sacrificial layer 22. Once the structural layer 24 has been deposited it is ready for patterning to be finally formed into either the gear 26 or slider 30 shown in Figures 1 and 2. The slider 30, will be slotted to receive the rail 32. Conventional procedures of masking and etching that were used in previous steps to pattern the structural layer 12 are used again here to pattern the structural layer 24. Figure 9 shows the device after patterning the structural layer 24. The gear 26 or slider 30 is now completed but still connected by the sacrificial layer 22 to the substrate 10 and the pin 28 or the rail 32. The final step, shown in Figure 10, is removal of the sacrificial layer 22. In this embodiment an oxide etch is used to wash out the oxide used for the sacrificial layer 22. This step frees the gear 26 or slider 30 from the pin 28 or rail 32 and the substrate 10. The gear 26 may now rotate freely around the pin 28 and the slider 30 may now slide freely on the rail 32. Since the sacrificial layer 22 was thicker on the sides of the pin 28 or rail 32 and the substrate 10, when the sacrificial layer 22 is etched away the gear 26 or slider 30 will rest on the pin 28 or rail 32 but will be suspended above the substrate 10 and constrained by, but separated from, the head 29 and body 31 of the pin 28 or rail 32. Having the gear 26 or the slider 30 held suspended above the substrate 10 eliminates the frictional component between the gear 26 and substrate 10 when in use. An alternative method for further reducing the friction of the parts is shown in Figures 11 and 12. The steps shown in these Figures replace the steps shown in Figures 9 and 10. When patterning the structural layer 24 to form the gear 26 or slider 30, the centre portion 34 of the gear 26 or slider 30 may also be removed as is shown in Figure 11. After the oxide etch to wash out the sacrificial layer 22 is accomplished, the structure then appears as in Figure 12. The removal of the centre portion 34 minimizes contact between the gear 26 or slider 30 and the pin 28 or rail 32, reducing the friction further when the gear 26 or slider 30 is in use. Since silicon is capable of oxidation, it is possible to provide a thicker sacrificial layer on the substrate than on the top of the pin 28 or rail 32 to produce a gear or slider that is suspended above the substrate. A second embodiment may also be built and is shown in Figures 13-20. Equivalent parts of Figures 3-10 are given the same numbers only with "a" affixed thereto. The sequence will also be used to illustrate changes to the process when a substrate that does not form an oxide is used. Figure 13 is identical to Figure 3 in that it illustrates the substrate after deposition of the structural layer 12a which will be patterned to form the recessed pins and/or rails. Figure 14 illustrates the first patterning phase. In contrast to Figure 4, a depression has been defined in the first structural layer. However, the nitride layer 14a has been left on the surface of the substrate 10a. There is no reason to remove the nitride layer 14a since in this embodiment the surface of the substrate 10a does not form an oxide This hole will later become the recessed pin or rail. Oxide bumpers are grown and removed in Figures 15 and 16 identically as in Figures 5 and 6. The result is a recessed pin 28a or rail 32a formed by the hole in the first structural layer 12a. The next step is covering the recessed pins 28a and/or rails 32a with a sacrificial layer 22a as shown in Figure 17. In Figure 7 a two step process of first growing oxide on the substrate and then depositing additional material was used. In this embodiment, only a TEOS oxide deposition is used to insure that the nitride surfaces of the recessed pin 28a or recessed rail 32a are covered and because TEOS oxide deposition is a conformal deposition process. Since the substrate does not oxidize, there is no reason to perform the step of oxidizing the surface of the substrate 10a as in the first embodiment. Deposition and patterning of the second structural layer 24a, as shown in Figures 18 and 19 is identical to Figures 8 and 9. The final step, shown in Figure 20, is an oxide etch to wash out the sacrificial layer 22a. This step frees the gear 26a or slider 30a from the recessed pin 28a or recessed rail 32a and the substrate 10a. The gear 26a may now rotate freely around the recessed pin 28a and the slider 30a may now slide freely on the recessed rail 32a. However, due to the single step process of depositing a sacrificial layer the gear 28a or slider 32a is not suspended above the substrate as in the previous sequence. Other variations of the process are also contemplated including eliminating the nitride layer 14 and patterning and etching the substrate 10 itself to form the structures formed from the first structural layer 12, 12a. Figures 21-24 illustrate the changes in the process described in Figures 3-6 when the nitride layer 14 has been eliminated. Equivalent parts of Figures 3-6 are given the same reference numbers only with "b" affixed thereto. The steps shown in Figures 7-10 will follow the process steps shown in Figure 21-24 to complete the formation of the micromechanical element. Figure 21 illustrates the substrate 10b after the deposition of the first structural layer 12b. The first structural layer 12b comprises of two layers, a doped polysilicon layer 16b and a nitride layer 18b. Figure 22 illustrates the first patterning step of the the first structural layer 12b. It is similar in all respects to the patterning shown in Figure 4. Figure 23 illustrates the growth of the oxide bumpers 20b to achieve the curved sides of first structural layer 12b. Unlike Figure 5, the oxide bumpers 20b do not grow in an approximately circular shape but still form a convexo-concave relationship with the doped polysilicon layer 16b. The growth of the oxide bumpers 20b is merged with the oxide growth on the surface of the substrate 10b since the nitride layer between the doped polysilicon 16b and the substrate 10b was never deposited and therefore does not separate the oxide bumpers 20b from the oxide growth on the surface of the substrate, as in the first embodiment. The resultant oxide bumper growth is relatively flat with a convex bump grown into the doped polysilicon layer 16b. Figure 24 illustrates the pin 28b or rail 32b after the oxide has been removed. Even though the oxide bumpers were only partially circular, enough circular shape remains to insure that the head 29b of the pin 28b or rail 32b is still larger than the body 31b of the pin 28b or rail 32b. The processing steps from this point forward are identical to those illustrated in Figures 7-10. Figures 25 and 26 illustrate the changes in the process described in Figures 3 and 4 when both the nitride layer 14 and the polysilicon layer 16 have both been eliminated. Equivalent parts of Figures 3 and 4 are given the same numbers only with "c" following. The same steps shown in Figures 23 and 24 and Figures 7-10 will follow the process steps shown in Figures 25 and 26 to complete the formation of the micromechanical element. The pin 28c or rail 32c is constructed out of the silicon substrate and has no joints. The entire concave profile that provides for the head 29c to be larger than the body 31c of the pin 28c or rail 32c is located in the doped polysilicon layer 16c only. This is different from the prior art as described in the patent to Muller et al. As disclosed in US-A-4,740,410 Muller et al. constructs his pins and flanges out of two different layers that are apt to separate under stress unlike this construction. Figure 25 shows preparation of the substrate before it is to be patterned to form pins and rails. A nitride layer 18c is deposited on the substrate. Figure 26 shows the substrate after the first phase of patterning. A protruding structure with a nitride cap 18c is etched out of the substrate in the same manner as the first structural layer 12 in Figure 4. The next two steps are identical to those in Figures 23 and 24, and the concluding steps are identical to those in Figures 7-10. Utilizing layers of gears and sliders allows complicated micromechanical structures with interlocking gears and sliders to be built. Self-constraining structures, based on sliding gears interacting with other gears or sliders, can be built.

Claims: A process for making a micromechanical structure comprising (a) forming a concave shaped undercut edge by providing a member (10) having a generally planar surface with wall means (12) extending from said surface, growing bumper means (20) into said wall means (12) and forming a convexo-concave relationship with said wall means (12), removing said bumper means (20) from said wall means (12) such that said wall means retains a concave shaped undercut edge; characterized by (b) forming a sacrificial layer (22) on at least a portion of the remaining wall means (12), forming a structural layer (24) on at least a portion of said sacrificial layer (22), patterning said structural layer (24), removing said sacrificial layer (24) such that said remaining wall means (12) and said patterned structural layer (24) are movable relative to each other. The process in claim 1 wherein said member (10) includes a second generally planar surface and said wall means (12) is provided by: masking and etching said second generally planar surface and said member (10) to expose said first named generally planar surface of said member and to form (i) a structure protruding from said first named generally planar surface of said member, said wall means (12) being located on said protruding structure, or (ii) a depression in said member which is defined by wall means (12) and said first named generally planar surface. The process in claim 2 wherein (i) said wall means (12) is annular, or (ii) said wall means (12) is elongated and/or said wall means (12) is elongated and comprises two walls on opposite sides of said protruding structure. The process according to any of the preceding claims, wherein said bumper means (20) is oxide. The process according to any of the preceding claims, wherein said wall means (12) is provided by: forming a nitride layer (14) on said member (10); and masking and etching said member (10) and said nitride layer (14) to expose at least a portion of said generally planar surface and to form (i) a structure of said member (10) and said nitride layer (14) which protrudes from said exposed portion of said generally planar surface, said wall means (12) being located on the protruding structure, or (ii) a depression in said member and said nitride layer (14) which is defined by said wall means and said exposed portion of said generally planar surface. The process according to any of claims 1 to 4 wherein said wall means (12) is provided by: forming a polysilicon layer (16) on said generally planar surface, forming a nitride layer (18) on said polysilicon layer, and masking and etching said polysilicon layer (16) and said nitride layer (18) to expose at least a portion of said generally planar surface and to form (i) a structure of said polysilicon layer (16) and said nitride layer (18) which protrudes from said exposed portion of said generally planar surface, said wall means (12) being located on the protruding structure, or (ii) a depression in said polysilicon layer (16) and said nitride layer (18) which is defined by said wall means (12) and said exposed portion of said generally planar surface. The process according to any of claims 1 to 4 wherein said member (10) includes a first nitride layer (14) which is said generally planar surface and said wall means (12) is provided by: forming a polysilicon layer (16) on said first nitride layer (14), forming a second nitride layer (18) on said polysilicon layer (16), and masking and etching said second nitride layer (18) and said polysilicon layer (16) to expose at least a portion of said first nitride layer (14) and to form (i) a structure of said second nitride layer (18) and said polysilicon layer (16) which protrudes from said exposed portion of said first nitride layer (14), said wall means (12) being located on the protruding structure or (ii) a depression in said second nitride layer (18) and said polysilicon layer (16) which is defined by said wall means (12) and said exposed portion of said first nitride layer (14). The process according to any of claims 1 to 4 wherein said wall means is provided by: forming a first nitride layer (14) on said member, forming a polysilicon layer (16) on said first nitride layer (14), forming a second nitride layer (18) on said polysilicon layer (16), and masking and etching said first nitride layer (14), said polysilicon layer (16), and said second nitride layer (18) to to expose at least a portion of said generally planar surface to form (i) a structure of said first nitride layer (14), said polysilicon layer (16), and said second nitride layer (18) which protrudes from said exposed portion of said generally planar surface, said wall means (12) being located on the protruding structure or (ii) a depression in said first nitride layer (14), said polysilicon layer (16), and said second nitride layer (18) which is defined by said wall means (12) and said exposed portion of said generally planar surface.

Inventors: BOL IGOR I, BOL, IGOR I.
Applicants: XEROX CORP, XEROX CORPORATION
Application year: 1992
Main classification: G03F7
IPC codes: F16C33, B23P15, C23F17, B23P11, G03F7