ELECTROSTATIC SPRAY PAINT

Abstract: Electrostatic spray paint formulations of alkyds, acrylics, nitrocellulose or polyurethanes having defined viscosity/resistivity values and film-forming solids content.

Description: ELECTROSTATIC SPRAY PAINT FIELD OF THE INVENTION The invention relates to spray paints, for use in particular in electrostatic spraying. BACKGROUND Electrostatic spray heads are described in ICI's U.K. patent specifications Nos. 1 569 707, 2 018 601 and numerous others. Liquid supplied to the head is broken up essentially by the action of a high voltage field to form charged droplets, which are then attracted to and deposit on an earthed target such as a plant crop. The current passing, which is minute and harmless, is supplied for example by dry cells. No impellant gas or mechanical action is involved in transport of the spray. Spraying of paint is mentioned in the above patents, but without discussion of paint compositions or other aspects of successful application of the electrostatic principle to paint. DEVELOPMENT OF THE INVENTION We have sought to apply electrostatic spray generation to paint and other associated products where normally they have been applied using aerosol dispensing systems. We have found that by using the electrostatic system, material can be applied more efficiently with a greater degree of control and accuracy and generate a surface finish comparable to that given by an aerosol. Further, especially as the use of a propellant is not required, a considerable reduction in emissions of solvents and other volatile constituents is achieved when compared to an aerosol spray system. The inherent advantages of electrostatic paint spraying over aerosol paint spraying can be defined thus: i) Directional, targeted spraying with reduced drift and over spray of adjacent areas. ii) Considerable reduction in emissions of volatile constituents when compared to a typical aerosol spray paint. This is because no propellant is required to generate the spray and the paint itself requires a lower proportion of solvent in use, and also because of the inherent transfer efficiency of the system. Typically an automotive spray paint aerosol may contain 22% propellant, 70% solvent, and 8% paint solids compared to the present formulations that contain no propellant and at least double that solids content. Calculations have demonstrated that if used for a similar application, then the system detailed can reduce emissions of volatile organic compounds (VOC's) by up to three quarters when compared to those emitted during application of a paint via an aerosol. In order to achieve satisfactory results attention will be paid to characteristics of the paint, such as viscosity, resistivity, solids content and drying time, and the operating characteristics of the spray gun, such as voltage and flow rate. However we have found that the viscosity and resistivity of the paint formulation are key points. In the context of the present invention, paint formulations consist essentially of pigment, resin, and solvent. The pigment, resin and other non-volatile elements together are the solids of the final paint coat, the pigment giving colour and the resin, which may for example be a nitrocellulose, alkyd, polyurethane, or- acrylic, acting to bind the system, promoting adhesion, gloss, flexibility and wear resistance of the film. The solvent is largely or wholly lost by evaporation from the deposited coat (in some systems part becomes incorporated in the resin), but is essential to formation of the spray and its deposition as a paint coat. In the spraying, the paint must of course be thin enough to form a spray and not merely dust on the work but equally not so thin that it forms runs and sags. However there are special requirements in electrostatic spraying. Ideally the paint fed to the head is broken up, by the electrostatic forces in the head, into a diverging spray that is uniform and of close particle size distribution, and thus the resistivity and viscosity of the paint formulation have to be considered in relation to the generation and transport of the spray. Specifically, the following observations have been made in the development of the formulation. i) Rheology If viscosity is too low, sags form in the paint film on the work. If it is too high then no proper spray cloud forms and spidery filaments of paint are left between droplets on the surface; alternatively a spray cloud may be formed but it is poorly dispersed with long ligaments and is excessively divergent. ii) Resistivity If resistivity is too low the spray cloud may be over- divergent, or a fine mist mixed with coarse droplets may be observed. If the resistivity is too high then the spray cloud may not be divergent enough, or long ligaments with relatively large particles of paint in a low-divergence cloud may be observed. THE INVENTION The invention lies primarily in paint compositions formulated to provide satisfactory finishes in electrostatic spraying, understood as a spraying process in which the spray is generated by forces which are primarily electrostatic (they may be referred to as electrohydrodynamic forces) , rather than by mechanical means or the action of a vaporisable propellant, and the spray particles are attracted to the work by virtue of resulting charges on the particles. So stated the invention provides a spray paint formulation of film-forming solids content by weight, according to the resin system, of alkyds 55% to 75% or higher, 85% up to 90% acrylics 20 or 25% to 35 or 40% nitrocellulose 17.5% to 22.5 or 25% polyurethanes 50% to 60 or 70% and viscosity/resistivity values which in a rectangular plot of viscosity (P) and resistivity (ohm cm) fall within the rectilinear-sided operating envelope defined by the points x/y 0.25 x 10 6 /0.1, 2 x 10 6 /8, 32 x 10 6 /4 and 35 x 10 6 /0.1; or more conveniently 0.25 x 10 6 /0.25, 2 x 10 6 /8, 32 x 10 6 /4 and 35 X 10 6 /0.25. The invention may however also be stated as characterised both by the paint formulation above and the novel technical effect of suitability for successful application in electrostatic spraying, for example at from 1 up to 10 or 15 ml/min, conveniently l to 6 ml/ in, with resulting gloss of over 70, preferably over 80, as defined by ASTM D523,60°. Application rates may be 1.5 to 10 g/s/cm 2 x lθ ""5 dry paint film, preferably 1.7 to 8.4 g/s/cm 2 x 10~ 5 . In other terms again, the invention can be stated as method of spray painting in which electrostatic spraying a defined is employed and the paint formulation is as set out. The solids content of the formulation is defined as wha forms the paint film, whether or not in solid form in the formulation. Its nature in terms of pigment and resin is no central to the invention. EXAMPLES The invention is illustrated in the tables of examples wherein:- Table 1 gives a number of formulations of illustrative compositions; Table 2 lists the materials used in the formulations acknowledging trade marks and giving the function of the materials; Table 3 gives the solids content of the formulations with their resistivity and viscosity and the gloss and covering power at different sprayrates; and Table 4 (Figure 1) is a graph of the relations expressed in the statement of invention above. In formulating the paint compositions there are no special problems, the components simply being brought together and blended until the pigments are uniformly dispersed. The functions of the components are as given broadly in Table 2, and are generally well known in themselves. In the nitrocellulose mix however it may be noted that the "Synolac" is a plasticising alkyd giving durability and flexibility. Similarly the small quantity of nitrocellulose resin in one of the acrylic formulations is to harden -the paint film and improve its resistance to solvent attack. In the compositions further, the solvent properties are primarily as follows, though it will be appreciated that some synergy exists between components in the system:- a) Butanol - provides secondary solvency and prevents damp coalescence b) Methyl ethyl ketone - Assists set up of paint through f st evaporation c) Xylene and toluene - Dilute and assist in solvating the alkyd resin d) Butyl acetate - Balance solvent and flow and resistivity modifier e) Diacetone alcohol - Slow evaporating solvent that prevents blush and chilling of paint film; resistivity modifier f) Acetone - Fast evaporating solvent; viscosity and resistivity modifier g) Ethylene glycol monobutylether and ethyl 3-ethoxy propionate - Slow drying solvents aiding film forming characteristics and improving the surface finish of the paint film In evaluating the formulation spraying was through an electrostatic spray head of the kind described in ICI's patents. Spraying distances between gun and test panels were approximately 6 inches (15 cm). Covering power was evaluated by spraying at various rates as indicated to give a visibly acceptable film and weighing the panels after 16 hours drying under ambient conditions. TABLE 1 - ELECTROOYN PAINT SYSTEHS - FORMULAE SUBSTITUTE SHEET Continued Table 1 continued ÷w w % w/w w/w % w/w % w/w (Uπithant 636H) (Nitrocellulose 2.50 DHX 30-50) (Syrwiac 9285X) (Neocryl B722) 12.98 (Neocryl B735) 8.65 (Panlol B48N) 4.32 (Plasty ϊl AC251J 56.41 (wreslnol 63.12 VAS914Z> fclvacite 2013) 12.67 (Soalkyd 3007) 47.60 (Acetone) 4.00 1.98 4.00 30.00 5.00 (πiicetone 10.00 4.95 13.00 Alcohol) (Ethylenβ glycol 11.56 mσnocutyl ether) Butyl Acetate) 2.30 3.00 9.82 7.00 (X lene) 28.85 18.80 (Toluene) 5.28 5.00 fi.42 (Ethyl 3-ethoxy 4.16 prσ ionati) (hethyl Ethyl 3.57 Ketone) (Butyl Alcohol) 7.14 Continued SUBSTITUTE SHEET Table 1 continued 24.82 22.00 8.43 1.20 100.00 100.00 100.00 100.00 100.00 SUBSTITUTE SHEET Table 1 continued (T ltanlvβ 5.36 30.69 9.14 0.38 34.28 Dioxide) (HlcroHth Blue) rj.84 — (Carbon Black) _ _ _ χ ιo ( ryl Red) O lnacrldone Pink) — — - SMagnacryl — PX 126 ^ iagnacryl fc— PX 1275) (πrconlua Drier) (Manwec Cob lt) — . ^anotec Calciua) _ fcitafor CA80) — (Peren l F40) 0.50 — (Olbutyl — - Phthaiate) (pentoTr SO-2) _ 0.20 wpert 657) __ __ (Methyl Ethyl _ 0.10 0.28 Ketoxfae) ^rσysol 98-C) — — — 0.57 ϊόoTόό " ~ 100.00 100.00 J OO.OO 100.00 SUBSTITUTE SHEET TABLE 2 - RAW MATERIAL DESCRIPTIONS RAW MATERIAL PRODUCT DESCRIPTION Unithane 638W Resin DHX 30-50 * Resin Synolac 9285X * Resin Neocryl B722 * Resin Neocryl B735 * Resin Paraloid B48N * Resin Plastyrol AC251 * Resin Wresinol VAS 9142 * Resin Acetone Solvent Diacetone alcohol Solvent Ethylene glycol monobutyl ether Solvent Xylene Solvent Toluene Solvent Ethyl 3-ethoxy propionate Solvent Methyl ethyl ketone Solvent Butyl alcohol Solvent Titanium dioxide Pigment Microlith Blue * Pigment Carbon black Pigment Tryl Red * Pigment Quinacridone Pink * Pigment Zirconium drier Drier Manosec Cobalt * Drier Manosec Calcium * Drier Byk ES 80 * Conductivity Additive Catafor CA80 * Conductivity Additive Perenol F 40 * Conductivity Additive Dibutyl phthalate Plasticiser Byk P104S * Dispersion Additive Nuosperse * Dispersion Additive Bentone SD2 * Rheology Modifier Methyl ethyl ketoxime Anti Skinning Agent Elvacite 2013 * Resin Soalkyd 3007 * Resin Troysol 98-C * Dispersion/Wetting Additive Magnacryl PX 1264 Pigment Magnacryl PX 1275 * Pigment NB * Denotes Trade Marks SUBSTITUTE SHEET TABLE 3a- ELECTRODYN PAINT SYSTEMS - PERFORMANCE DATA CD C DO ω H H c m CD X m m H * At the different spray rates TABLE 3b - ELECTRODYN PAINT SYSTEMS - PERFORMANCE DATA PAINT SYSTEM ACRYLIC ALKYD ALKYD ACRYLIC ALKYD CODE NUMBER AP10/M/99 AP10/N/ AP10/K/ AP10/LV2 AP10/HS4 70a 12i c SPRAY RATE 1 1 1 2 (mil/min) 2 2 2 2 2 1 3 3 3 3 4 6 6 6 15 6 H RESISTIVITY C (xl0« ohm cm) 1.07 5.90 2.29 3.11 2.53 H rπ VISCOSITY (Poise) 1.60 5.15 3.30 0.163 3.40 X rπ m NON-VOLATILE CONTENT 32.67 70.96 57.68 22 86 <%) GLOSS* (ASTM D523, 86.10 90.40 95.40 84.7 91.5 90.5 60 angle) 85.70 91.60 93.90 85.7 93.2 At spray rate 85.40 92.10 94.20 84.50 84.7 92.20 95.90 91.6 92.3 COVERING *• POWER 4.14 7.91 4.66 3.33 13.2 39.3 (X10-*- g/s/cπr) 6.89 10.29 8.91 4.95 At spray rate 10.37 13.43 13.85 17.9 19.72 21.62 22.78 5.54 25.0 48.8 At the different spray rates

Claims: CLAI ? 1. An electrostatic spray paint formulation of film-forming solids content by weight according to the resin system, of alkyds 55% to 85 or 90% acrylics 20% to 40% nitrocellulose 17.5% to 25% polyurethanes 50% to 70% and viscosity/resistivity values which in a rectangular plot of resistivity (ohm cm x 10 6 ) and viscosity (P) fall within the rectilinear-sided operating envelope defined by the points x/y 0.25 x 10 6 /0.1, 2 x 10 6 /8, 32 x 10 6 /4 and 35 x 10 6 /0.1; or more conveniently 0.25 x 10 6 /0.25, 2 x 10 6 /8, 32 x 10 6 /4 and 35 x 10 6 /0.25. 2. The formulation at claim 1 with alkyd 55 to 75% acrylic 25 to 35% nitrocellulose 17.5 to 22.5% polyurethane 50 to 60% 3. The formulation of claim 1 or 2 when for use in electrostatic spraying, at from 1 to 10 or 15 ml/min, conveniently 1 to 6 ml/min, and with resulting gloss of over 70, preferably over 80 as defined by ASTM D523,60°. 4. Formulations as claimed in claim 3 when for use to give application rates of 1.5 to 10 g/s/cm 2 x 10~ 5 dry paint film, preferably 1.7 to 8.4 g/s/cm 2 x 10~ 5 . 5. A method of spray painting wherein electrostatic spraying is employed and a paint formulation as set out in claim 1 or 2 is used. SUBSTITUTESHEET 6. A method according to claim 5 wherein the formulation is sprayed at from 1 to 10 or 15 ml/min, conveniently 1 to 6 ml/min, with resulting gloss of over 70, preferably over 80 as defined by ASTM D523,60°. 7. A method according to claim 6, wherein the formulation is used to give application rates of 1.5 to 10 g/s/cm 2 x 10 "5 dry paint film, preferably 1.7 to 8.4 g/s/cm 2 x 10~ 5 . U iS3STTISTIUTE SI

Inventors: GRAYSON JULIA PATRICIA ARUNDEL, NOOR NIGHAT, OUTHWAITE ALAN CHARLES COBBLER, SPOWAGE MARK JOHN, GRAYSON, JULIA, PATRICIA, NOOR, NIGHAT, OUTHWAITE, ALAN, CHARLES, SPOWAGE, MARK, JOHN
Applicants: MORGAN CRUCIBLE CO, THE MORGAN CRUCIBLE COMPANY PLC
Application year: 1992
Main classification: C09D175
IPC codes: C09D5, C09D167, C09D175