Soldering flux

Abstract: A no-clean, thermally dissipated soldering flux is shown which includes hydroabietal alcohol as a flux base, an organic activator and an organic diluent. The hydroabietal alcohol provides a tacky medium which holds a precisely aligned chip in place both during placement and reflow. The nature of the formula renders a reducing atmosphere unnecessary. The composition is thermally dissipated during soldering and leaves no undesirable residue which would require a post-cleaning step.

Description: The present invention relates to soldering fluxes and their use in processes for soldering members, particularly metallic members together. The flux compositions of the invention are particularly useful in the field of microelectronics, such as in the preparation of integrated circuit modules and integrated circuit boards. A common task in the manufacture of microelectronic components involves the manufacture of single chip or multi-chip modules having input/output pins which are inserted into a substrate. The input/output pins provide the needed electrical connections to the integrated circuit chip or chips which are subsequently connected to the substrate or carrier. In other presently known manufacturing processes, a chip is soldered directly to a printed circuit board. With either process, solder flux compositions have typically been applied to the pins in order to connect the component to the selected substrate, for instance, the printed circuit board. Flux compositions are employed to remove oxides from the pins and to prevent the pins from oxidizing when subjected to elevated temperatures for soldering, thereby serving to maintain the solderability of the pins. Once the solder is applied, any flux composition or residue remaining on the pins and substrates must be removed to provide as clean a substrate as possible. In the past, this has meant that an extra step of flux removal was necessary in the manufacturing process. The soldering operation, in general, and flux removal, in particular, is increasingly difficult when applied to microelectronics. The pieces to be joined are extremely small, making cleaning, tinning, post-cleaning and inspection difficult. In some cases, to avoid over heating, only the lead portion of the parts to be joined can be heated during the soldering operation. Cleaning and post-cleaning are difficult due to the small size of the component, their large numbers, and the potential damage to the electronics by the cleaning solutions used, if any. Another problem source results from the fact that many of the known soldering fluxes are corrosive. In the environment of microelectronics, corrosion from any residual flux can ruin an extremely costly device. Many of the organic water soluble fluxes presently available contain corrosive materials such as halides. A flux composition which contains free halogen can result in conversion to hydroacids and corresponding halide ions by hydrolysis at the soldering temperature. Hydroacids can further react with organic materials present in the flux to free halide ions. Accordingly, if the flux residue is not entirely removed, it will lead to corrosion of the parts soldered. Because of these problems, so-called "non-activated" rosin fluxes have been used in the past in the microelectronic environment in conjunction with a reducing atmosphere in the soldering equipment. This has not generally provided an acceptable solution, however, since the pure rosin alone is limited in oxide removal capability, can require rework to produce an acceptable proudct, and often a special soldering atmosphere and/or equipment is required. To improve the pure rosin flux oxide removal capability, a number of "activiated" or "mildly activated" rosin fluxes have been developed (see for example US-4,278,479). These products have several shortcomings, including the necessity of a cleaning step to ensure the removal of corrosive agents left behind after the soldering operation. For instance, it was often necessary to employ specialised water-based detergents followed by a hot water rinse. These cleaning steps were extremely difficult during the assembly of chips to integrated circuit board where the low stand-off height of the chip to the substrate (typically 25-100 micrometers, 0.001 inches - 0.004 inches) made it extremely difficult to clean underneath the chip with an aqueous or non-solvent process. Other of the commercially available low reside fluxes which we have tested have proved to be too thin, running out from under the chip during the manufacturing operation and failing to hold it in place. It is an object of the present invention to provide a soldering flux and a method of using such a flux which minimised the problems and shortcomings identified above. According to the invention there is provided a soldering flux for use in assembling chips to integrated circuit boards, where the stand off height of the chips to the boards is of the order of 25 - 100 micrometers (0.001 to 0.004 inches), the flux comprising: from 5 to 30% by weight based on the total weight of the flux of hydroabietal alcohol as a flux base; from 1 to 6% by weight based on the total weight of the flux of an organic activator; the remainder being at least one organic diluent. There is further provided a method of fluxing the surfaces of a portion on a piece, comprising the steps of contacting the portion to be fluxed with a solution consisting essentially of a mixture of 5 to 30% by weight of hydroabietal alcohol as a flux base, from 1 to 6% of an organic activator, and an organic diluent; and heating the contacted portion to a temperature at which the organic activator reacts with oxides present on the surface and the solution evaporates. The soldering flux of the invention has as its composition hydroabietal alcohol which provides a tacky yet fluid medium as a flux base, a liquid solvent to diluent, such as isopropyl alcohol or other aliphatic alcohol having from about 1 to 4 carbon atoms, and an organic activator composition, such as an aliphatic dicarboxylic acid. By combining these ingredients, a liquid solder flux is produced which remains tacky after application, holding a precisely aligned chip in position for reflow, and which is subsequently thermally dissipated leaving no visible residue which would require a cleaning step. The method of the invention may advantageously be used for fluxing the pin of an integrated circuit chip and/or the circuit pad of the substrate. The portion to be fluxed is contacted with the solder flux of the invention and the contacted portion is then heated to a temperature at which the organic activator reacts with the oxides present on the surface of the portion of the piece and the solution evaporates leaving no residue. In joining the chip to a substrate, such as printed circuit board, the pin and a selected area on the substrate where solder has been previously applied, are fluxed using the composition of the invention. The chip and substrate are contacted and are joined at a temperature above the melting point of a metallic solder and then cooled to a temperature below the melting point of the solder, thereby jointing the contacted portions together without any post-cleaning of the joined components. In order that the invention may be well understood, preferred embodiments thereof will now be described. The soldering flux compositions of the invention comprise: (1) hydroabietal alcohol as the flux base, (2) an organic solvent or diluent and (3) an organic activator of the type which reacts with oxides present on the surface to be fluxed. The flux base of the present soldering flux is a special derivative of the family of rosins used in traditional rosin fluxes. It is a pure component that must be refined since it does not occur naturally in large quantities. It must possess the desired characteristics of forming a tacky vehicle, when combined with the organic activator and diluent in the desired proportions, and be effective to hold a chip or component in place for up to 8 hours after placement on a substrate, and through reflow. Hydroabietal alcohol is a very tacky and extremely viscous substance that usually requires heating before it can be added to the other components of the flux. It will dissipate at temperatures above about 200 degrees centigrade and will not carbonize up to a temperature of 340 degrees centigrade which is appropriate to the temperature ranges for the reflow of solder. It has the structural formulae: and is commercially available from Hercules Corporation of Wilmington, Delaware as "ABITOL". The hydroabietal alcohol component is employed in the composition of the present invention in the range from about 5 to about 30% by weight, based on the weight of the total flux composition. The compositions of the present invention also contain an organic activator which is effective to remove oxides present on the surface to be fluxed and to improve wetting of the substrate. Preferably, the organic activator is ephemeral in nature, completely dissipating when heated in the range of about 200 degrees centigrade and above. Preferred organic activators include, for example, abietic, adipic and citric acids as well as aliphatic dicarboxylic acids having about 2 to 6 carbon atoms. Each of the preferred activators is commercially available. For example, adipic acid is a white crystalline solid having a molecular weight of approximately 146.14 and a melting point of 153 degrees cent. It is found naturally in beet juice and can be prepared by oxidizing cyclohexanol with concentrated nitric acid. It is commonly available from Aldrich Chemical Company, Inc., Sigma Chemical Company and Eastman Kodak Company. The organic activator component of the soldering fluxes of the invention is preferably present in the range from about 1 to 6% by weight of the total flux composition. The compositions of the present invention also contain at least one organic solvent or diluent which will evaporate or dissipate during the reflow operation. A variety of evaporative organic solvents are known, the preferred diluent being an aliphatic alcohol having about 1 to 4 carbon atoms, i.e. methyl alcohol, ethyl alcohol, isopropyl alcohol, n-propyl alcohol, isobutyl alcohol and n-butyl alcohol. Other organic solvents which are known to be operative include tetrahydrofuran, acetone, ethyl acetate, ethyl formate, hexane, gamma-butyrolactone, xylene, cyclohexanone, t-butyl alcohol, and mixtures thereof. The aliphatic alcohols are preferred because of the absence of ojectional odors, the absence of adverse reaction to the other ingredients and because of the lack of environmental and health concerns. The organic diluent component of the solder fluxes of the invention is present in the range from about 64 to 94% by eight of the total flux composition. The following non-limited example is a preferred formulation of the thermally dissipated, no-clean soldering flux of the invention: An invention has been provided with several advantages. The soldering flux of the invention is thermally dissipated during use and leaves no visible residue which would require a post-cleaning operation. The soldering flux exhibits superior wettability, producing the activity needed to effectively remove oxides on the surface to be fluxed. The hydroabietal alcohol component provides a tacky yet fluid medium which holds a precisely aligned chip in place for up to 8 hours after placement and during solder reflow. The composition exhibits no corrosivity even if left on a card for a period of time before or after the soldering operation. The only by-products of the flux of the invention are inert and leave no undesirable residue. The compositions can be formulated without the use of chemicals which are environmental and/or health hazards.

Claims: A soldering flux for use in assembling chips to integrated circuit boards, where the stand off height of the chips to the boards is of the order of 25 - 100 micrometers (0.001 to 0.004 inches), the flux comprising: from 5 to 30% by weight based on the total weight of the flux of hydroabietal alcohol as a flux base; from 1 to 6% by weight based on the total weight of the flux of an organic activator; the remainder being at least one organic diluent. A soldering flux as claimed in claim 1, wherein said organic activator is an aliphatic dicarboxylic acid having 2 to 6 carbon atoms. A soldering flux as claimed in claim 1, wherein said organic activator is selected from the group consisting of abietic, adipic or citric acid. A soldering flux as claimed in any preceding claim wherein said organic diluent is an aliphatic alcohol having 1 to 4 carbon atoms. A soldering flux as claimed in claim 4, wherein said organic diluent is selected from the group consisting of methy alcohol, ethyl alcohol, isopropyl alcohol, isobutyl alcohol and n-butyl alcohol. A method of fluxing the surfaces of a portion on a piece, comprising the steps of contacting the portion to be fluxed with a solution consisting essentially of a mixture of 5 to 30% by weight of hydroabietal alcohol as a flux base, from 1 to 60% of an organic activator, and an organic diluent; and heating the contacted portion to a temperature at which the organic activator reacts with oxides present on the surface and the solution evaporates. A method of claim 6, wherein the organic activator employed is selected from the group consisting of abietic acid, adipic acid and citric acid. The method of claim 6, wherein the organic diluent is an aliphatic alcohol having 1 to 4 carbon atoms. The method of claim 8, wherein the organic diluent is selected from the group consisting of methy alcohol, ethyl alcohol, isopropyl alcohol, n-propyl alcohol, isobutyl alcohol and n-butyl alcohol.

Inventors: GUTIERREZ BARBARA LARISA, SICKLER JANET M, GUTIERREZ, BARBARA LARISA, SICKLER, JANET M.
Applicants: IBM, INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1992
Main classification: B23K35
IPC codes: H05K3, B23K35