Inserts preferably for machining of heat resistant materials and process for producing the same.

Abstract: The present invention relates to whisker reinforced ceramic bodies with new and improved properties. By replacing the tool pressing with injection moulding surprisingly a more homogeneous structure and more advantageous whisker orientation has been obtained. By choosing the conditions of the moulding it is possible to control the whisker orientation to get optimal material properties. Bodies according to the invention are particularly suitable for chip forming machining of heat resistant materials.

Description: The present invention relates to a method of manufacturing cutting tool inserts preferably for machining of heat resistant materials. For machining of cast iron and heat resistant materials ceramic inserts based on alumina are usually used. Such inserts are very sensitive to thermal cracks since the material has relatively low thermal conductivity. This leads to short tool lives under conditions leading to thermal shocks i.e. high edge temperatures, short engagements times and varying cutting depths. To a certain extent the thermal properties can be improved by addition of TiC and/or TiN whereby the thermal conductivity increases. But at the same time the toughness behaviour increases only moderately and the material can only be used at relatively low feeds. A later step in the development comprises additions of finegrained ZrO 2 -particles to the alumina matrix. The transformation of the metastable ZrO 2 -particles during use increases both strength and toughness. The thermal properties are only slightly better. It has recently been shown that the fracture toughness of a ceramic material can be increased by addition of monocrystalline hair crystals (whiskers) and/or platelets. A material consisting of SiC-whiskers in an alumina matrix is disclosed in US 4,543,345. US 4,867,761 discloses the use of carbides, nitrides or borides of Ti and/or Zr in an alumina matrix. Through US 4,849,381 a cutting tool comprising a mixture of whiskers and platelets is known. EP-A-0 444 426 relates to a SiC whisker reinforced Si 3 N 4 composite with uniaxially oriented whiskers. It is made by laminating a plurality of sheets with uniaxially oriented whiskers. The composite is suited for use as automobile engine parts and similar. JP-A-01 278 479 describes a whisker compound ceramic in which the whiskers are uniformly dispersed in a fixed plane direction in a matrix and which is produced by injection or extrusion molding using a polymer as a dispersant for the whiskers. JP-A-900104978 and JP-A-90104979 disclose alumina-based ceramic cutting inserts containing 3-40 weight % SiC whiskers being oriented parallelly or almost parallelly to the face of the insert. The combination Al 2 O 3 -matrix + SiC-whiskers is commercially available as inserts for machining. Such inserts are generally manufactured by uniaxial pressure sintering. This method is, however, unsuitable for inserts with more complex geometries. Inserts in more conventional materials e.g. non-reinforced ceramics and cemented carbide are usually manufactured by tool pressing. In this method powder is compacted to a solid body in a tool comprising a die and two punches. Granulated powder comprising the ceramic material and one or more binders e.g. polyvinylalcohol and with good flow properties is filled into the die and compacted by pressing the upper punch with a certain force against the lower usually fixed punch. Through a suitable shape of the punches the insert is given a suitable chip breaking geometry. A drawback with tool pressing is that the relative density varies within the body. This variation is particularly large for complex bodies with large differences in compacted height. Also material reinforced with whiskers and/or platelets can be tool pressed. Hereby very high compaction pressures are needed in order to obtain a reasonable relative density. In order to obtain an even filling in the tool also in this case granulated powder is needed. The most common method for granulation is spray drying. However, during spray drying the whiskers are drawn into the middle of the granules and the granule borders are depleted of whiskers. In addition, the granules that are armoured by the whiskers and also contain a binder cannot be completely crushed during the compaction. This leads to an uneven structure in the sintered material. Injection moulding is a common production method in the plastics industry for the production of 'net-shape' or 'near-net-shape' parts. A paste comprising thermoplastic or thermohardening polymers, is heated to a suitable temperature and forced through a nozzle into a form with desired geometry. The technique is also used in powder metallurgy for the manufacture of relatively complex metallic or ceramic parts. Hereby, a metallic or ceramic powder is mixed with polymers. After the shaping the polymer is driven off and after that the part is sintered in essentially the same way as for corresponding tool pressed parts. According to the invention there is now provided a way of manufacturing whisker reinforced ceramic inserts with complex geometry with even structure and favourable whisker orientation by injection moulding. Fig 1 shows the microstructure in 200X of a ceramic material consisting of Al 2 O 3 reinforced with SiC-whiskers manufactured by tool pressing. Fig 2 shows the microstructure in 200X of corresponding material manufactured by injection moulding according to the invention. Fig 3 shows in 1000X the whisker orientation in the rake face in a ceramic insert manufactured according to the invention. Fig 4 shows in 1000X the whisker orientation in the clearance face in a ceramic insert manufactured according to the invention. The invention, thus, relates to a way of manufacturing inserts of whisker reinforced ceramics by injection moulding. It has surprisingly turned out that by this method a material is obtained with homogeneous structure essentially free from granule borders and with an essentially one-dimensional whisker orientation. By choosing the conditions of the moulding it is possible to control the whisker orientation to get optimal material properties. The invention also relates to an insert for chip forming machining made in this manner with a polygonal or round shape with an upper face, an opposite face and at least one clearance face intersecting said upper and lower faces to define cutting edges. The insert is provided with devices for good chip breaking and for clamping in a holder. The ceramic material is alumina based and comprises, in addition to conventional sintering aids, 10-40, preferably 25-35 % by volume of single crystals whiskers of carbides, nitrides and/or borides of Si, Ti, Zr, Hf, Ta; and/or Nb or solid solutions thereof. The whisker material consists of hair-shaped monocrystals with a diameter of 0.2-10 µm and a length of 2.5-100 µm and a length/diameter ratio of preferably 5-10. The whisker material can partly be replaced by platelets i.e. monocrystal plates with a diameter of 0.5-40 µm and a diameter/thickness ratio of 5-50, preferably 10-20. The grain size of the ceramic matrix shall be <10 µm, preferably <4 µm. The matrix is essentially ceramic oxides or ceramic oxides mixed with hard carbides and/or nitrides and/or borides and/or binder metal. The ceramic matrix shall preferably contain <20 volume-% ZrO 2 . The relative density shall be at least 95 %, preferably 98 %, most preferably 99 %. The invention further relates to a method of cutting preferably heat resistant alloys wherein a cutting tool is brought into contact with a workpiece and the cutting tool and workpiece move relative to each other whereby material is removed by the cutting tool from the workpiece. The cutting tool has a ceramic matrix with a homogeneous structure essentially free from granule borders and comprising distributed therethrough 10-40 volume-% of single crystal whiskers with an essentially one-dimensional orientation. The method according to the invention prescribes that the ceramic raw materials are thoroughly mixed suitably by dispersion in water or any type of organic solvent. The dispersion can be facilitated/improved by addition of organic solvent and/or by adjustment of the pH-value when dispersing in water. The dispersion is dried e.g. by spray-drying. The well mixed ceramic powder obtained in this way is then mixed with a binder system adapted to injection moulding which binder system is a mixture of at least one additive of the type polyethylene, polypropylene, polystyrene, polyvinylchloride, polyvinylalcohol, polyvinylacatate, wax or stearic acid and, in addition, organic additives with dispersing, wetting, lubricating and/or viscosity adjusting function, as desired. The mixing is performed in a kneader. During said mixing the spray dried granules are completely crushed. A paste is obtained which is filled into the injection molding machine. Injection moulding is performed in a conventional injection moulding machine. The filling rate is kept within the range 0.1-10 cm 3 /s, preferably 0.5-2 cm 3 /s. The pressure is 5-300 MPa, preferably 50-150 MPa and the temperature is chosen within the range 40-200 °C. Preferential whisker orientation parallel with the flow direction is obtained by a convergent flow channel. Alternatively, a whisker orientation perpendicular to the flow direction can be obtained in a divergent flow channel. Both channels are conventional. The flow channel, the inlet and the mould are designed in such a way that the whisker orientation obtained gives optimal cutting properties depending upon the cutting application. When the notch wear is the dominating wear type, the whisker orientation should preferably be perpendicular to the clearance face. This is a common case when machining heat resistant materials. After the injection moulding the polymer is driven off in inert atmosphere, reducing atmosphere or in vacuum by increasing successively the temperature with the speed 1-500 °C/h, preferably 10-50 °C/h depending on the thickness of the body. The final temperature for the debinding lies in the range 400-800 °C. After the debinding, the body can be presintered in a separate step. The presintering is performed in inert atmosphere or in reducing atmosphere with a final temperature of 800-1500 °C after which debound-presintered or only debound body is sintered, hot isostatic pressed, gas pressure sintered or heat treated in any other way. At hot isostatic pressing the method according to Swedish patent application 9004134-4 is particularly suitable. The sintered body is finished to an insert with desired shape and dimension e.g. by grinding. The method according to the invention is particularly suitable for the manufacture of inserts for machining with complex geometry of whisker reinforced ceramics. An almost even density is obtained in the entire injection moulded body. With the method considerably higher relative densities for materials with high whisker content, about 65 % can be obtained than by conventional tool pressing, 45-50 %. The high relative density remains after the debinding whereas tool pressed material expands during the debinding and the relative density decreases to 40-45 %. During this expansion there is a risk for cracks being generated in the tool pressed material especially in parts of the material with a gradient in the relative density. Sintered material made according to the invention becomes more homogeneous and free of granule borders. The invention has above been described with reference to insert for machining. It is obvious to the man of the art that the invention can be applied to other ceramic parts reinforced by whiskers such as seals, gaskets and other wear parts and structural ceramics. Example 1 Three ceramic samples with the same composition i.e. 75 weight-% Al 2 O 3 with sintering aid and 25 weight-% SiC-whiskers were manufactured according to the following: The first sample, referred to as sample A, was manufactured according to conventional technique i.e. uniaxial pressure sintering. After the pressure sintering the sample was cut, surface ground and periphery ground to diameter 6 mm and height 6 mm. Then a chipping angle was ground in the sample with 5° angle and finally the sample was edge treated to an edge radius of about 30 µm. The second sample, B, was manufactured in a so called Q-cut™ geometry by tool pressing. This geometry consists of an insert and a holder. The insert differs from sample A in such a way that Q-cut™ has a chip breaker. Before the spray-drying the ceramic raw materials were mixed with organic binders. The compacted blank was treated in a combined debinding and presintering cycle in a graphite furnace. The final temperature was 1300 °C and the furnace atmosphere was hydrogen. The presintered blank was dipped with a suction cup in a BN-slurry and then in a mullite slurry according to the above mentioned Swedish patent application 9004134-4. The dipping was performed in such a way that first half of the blank was dipped in the BN-slurry, whereafter the layer was allowed to dry and then the other half was dipped. During all dipping steps the sample was evacuated with the aid of the suction cup in order to avoid blistering in the layer. The blank, which now was surrounded by a covering BN-layer and on top of this a covering mullite layer was placed in a glass powder bed and after that sintered by isostatic pressing at high temperature. Before the isostatic pressing the glass was melted in order to isolate the blank from the overpressure in the furnace. The sintering was performed at 1550 °C and 160 MPa. The microstructure of the material was uneven with visible granule structure, see Fig 1. The third sample, C, was manufactured according to the invention in a specially designed mould to get the same shape as sample B. The same powder as that used for sample A was mixed with a mixture of polyethylene, paraffin wax and stearic acid in a kneader and thereafter injection moulded. The injection moulded blank was debound/presintered and hot isostatic pressed in the same way as sample B. The resulting structure was even and without granules, see Fig 2. The finishing of the samples B and C was made at the same time by grinding a V-track in the bottom side and the insert was peripherally ground to 6 mm diameter. Hereby in sample C the part of the material was removed which had preferential whisker orientation parallel with the clearance face. Thus, after the periphery grinding the whisker orientation was preferentially parallel to the rake face, see Fig 3, and perpendicular to the surface of the clearance face, see Fig 4. The samples A, B and C were edge treated in the same way and at the same time. Example 2 The samples from the preceding example were tested in a longitudinal turning operation according to the following: Workpiece: Inconel 718A Cutting speed: 200 m/min Cutting depth: 1 mm Feed: 0.15 mm/rev Result (time to notch wear > 2.5 mm in minutes): Sample A 5 Sample B 6 Sample C 8 The insert manufactured according to the invention, thus, showed about 30 % longer life in Inconel 718 thanks to better resistance against notch wear. This is explained by the more favourable whisker orientation. Example 3 Two ceramic samples with the same composition i.e. 76 per cent by weight Al 2 O 3 and 24 percent by weight SiC-whiskers were manufactured according to following: The first sample, referred to as sample A, was manufactured in a RCGX geometry by tool pressing. The ceramic raw materials were dispersed in water together with organic binders and spray dried whereafter the spray dried powder was tool pressed. The compacted blank was treated in a combined debinding and presintering cycle in a graphite furnace. The final temperature was 1300 °C and the furnace atmosphere was hydrogen. The presintered blank was dipped with a suction cup in a BN-slurry and then in a mullite slurry according to the above mentioned Swedish patent application 9004134-4. The dipping was performed in such a way that first half of the blank was dipped in the BN-slurry, whereafter the layer was allowed to dry and then the other half was dipped. During all dipping steps the sample was evacuated with the aid of the suction cup in order to avoid blistering in the layer. The blank, which now was surrounded by a covering BN-layer and on top of this a covering mullite layer was placed in a glass powder bed and after that sintered by isostatic pressing at high temperature. Before the isostatic pressing the glass was melted in order to isolate the blank from the overpressure in the furnace. The sintering was performed at 1550 °C and 160 MPa. The sintered sample was cut, face ground and peripheral ground to diameter 9.5 mm and clearance angle of 7°. Finally the sample was edge treated to an edge radius of about 30 µm. The second sample, B, was manufactured according to the invention in a specially designed mould. The powder was manufactured in the same way as for sample A but without binders and afterwards mixed with a mixture of polyethylene, paraffin wax and stearic acid in a kneader and thereafter granulated. The granules were fed to a injection moulding machine with a convergent flow channel. The injection moulded blank was debound, sintered, ground and edge treated in the same way and at the same time as sample A. Example 4 The samples from example 3 was tested in a longitudinal turning operation according to the following: Workpiece: Inconel 718A Cutting speed: 300 m/min Cutting depth: 0.9 mm Feed: 0.15 mm/rev Result (time to notch wear > 2.5 mm in minutes): Sample A 4 Sample B 6

Claims: Insert for chip forming machining with a matrix of Al 2 O 3 containing 10-40 volume-% whiskers of carbides, nitrides and/or borides of Si, Ti, Zr, Hf, Ta and/or Nb or solid solutions thereof and in which the cutting part has polygonal or round shape with an upper face, an opposite face and at least one clearance face intersecting said upper and lower faces in a cutting edge characterized in that the whiskers are essentially unidirectionally oriented. Insert according to the preceding claim characterized in that the whiskers are oriented essentially perpendicularly to said clearance face. Method of manufacturing an insert for chip forming machining according to claim 1 with a ceramic matrix containing 10-40 volume-% whiskers of carbides, nitrides and/or borides of Si, Ti, Zr, Hf, Ta and/or Nb or solid solutions thereof and in which the cutting part has polygonal or round shape with an upper face, an opposite face and at least one clearance face intersecting said upper and lower faces in a cutting edge by powder metallurgical methods whereby the powdery raw materials are thoroughly mixed by dispersion in water or organic solvent, the dispersion is dried preferably by spraydrying, the dried powder is mixed with a binder system containing one or more polymers or other organic compounds, granulated, extruded through a flow channel into a mould with desired geometry, the binder is driven off and the body is finished by sintering, hot isostatic pressing or other heat treatment and with subsequent grinding to desired shape characterized in that the flow channel is convergent or divergent resulting in a unidirectional whisker orientation. Method according to the previous claim characterized in that the flow channel and geometry of the mould is chosen in such a way that the whiskers are oriented essentially perpendicularly to said clearance face.

Inventors: COLLIN MARIANNE, COLLIN, MARIANNE
Applicants: SANDVIK AB, SANDVIK AKTIEBOLAG
Application year: 1992
Main classification: C04B35
IPC codes: C04B35, C30B29, B23B27, B28B1