Method for producing glass soot deposit

Abstract: A glass soot deposit is produced at a high deposition rate by blowing a gaseous glass-forming raw material together with a fuel gas from a combustion burner in a closed muffle tube, hydrolyzing the glass-forming raw material in a flame to generate glass soot, and depositing the glass soot on a tip end or a peripheral surface of a starting member which is rotated to form a glass soot deposit . The lowest surface temperature of the muffle tube is maintained at 50°C or higher and an average surface temperature of the muffle tube is maintained in a range between 50°C and 150°C, whereby corrosion of the muffle tube is prevented.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a method for producing a glass soot deposit, in particular, a glass preform for use in the fabrication of an optical fiber. Description of the Related Art In a VAD method which comprises blowing a gaseous glass-forming raw material together with a fuel gas from a combustion burner to form glass soot by a gas phase reaction in a flame and depositing the glass soot on a starting member, environmentally harmful materials such as hydrogen chloride gas are by-produced. To trap the harmful materials effectively or eliminate any outside influence on a reaction system, reactions in the VAD method are carried out in an internal space of a closed reactor such as a muffle tube to deposit the glass soot. Recently, many researches have been made to increase a deposition rate, namely a synthesis speed of a glass soot deposit per a minute (g/min.) in the VAD method. As one of them, Japanese Patent Kokai Publication No. 171938/1987 discloses a technique for cooling a muffle tube surface in order to lower a temperature on a surface of the glass soon deposit, whereby the deposition efficiency will be increased. As disclosed in the above Japanese Kokai Publication, the conventional technique for cooling the muffle tube surface decreases such temperature to about 20°C. However, since an oxyhydrogen flame is generated in the muffle tube, a dew point therein is higher than that in the external atmosphere. Then, if the muffle tube surface is cooled down to about 20°C, dew condensation occurs in the muffle tube. Since hydrogen chloride gas is generated in the muffle tube, it reacts with water generated by dew condensation to form hydrochloric acid, which will corrode a metal muffle tube. Therefore, a life of the muffle tube is shortened and corroded metal contaminates the glass soot deposit (preform). When an optical fiber is fabricated from such contaminated preform, it has increased transmission loss. SUMMARY OF THE INVENTION An object of the present invention is to provide a method for producing a glass soot deposit at an improved productivity, which can avoid the above drawbacks of the conventional cooling technique. According to the present invention, there is provided a method for producing a glass soot deposit, which comprises steps of: blowing a gaseous glass-forming raw material together with a fuel gas from a combustion burner in a closed muffle tube, hydrolyzing said glass-forming raw material in a flame to generate glass soot, and depositing said glass soot on a tip end or a peripheral surface of a starting member which is rotated to form a glass soot deposit, wherein a lowest surface temperature of said muffle tube is maintained at 50°C or higher and an average surface temperature of said muffle tube is maintained in a range between 50°C and 150°C. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a perspective view of an example of a double-wall muffle tube used in the present invention, and Fig. 2 is a perspective view of an example of a muffle tube having a cooling pipe. DETAILED DESCRIPTION OF THE DRAWINGS To maintain the average surface temperature of the muffle tube in the above range, preferably, the muffle tube is constructed in a double-wall structure and a cooling liquid kept at a constant temperature is flowed between the walls (see Fig. 1), or a cooling pipe is provided on the muffle tube surface and a cooling liquid kept at a constant temperature is flowed in the pipe (see Fig. 2). The glass soot is deposited on the starting member by a thermophoresis effect due to a temperature gradient between the flame (a high temperature side) and a depositing surface (a low temperature side). To increase the thermophoresis effect and a deposition efficiency of the glass soot, the temperature gradient is increased. As one measure for increasing the temperature gradient, it is contemplated to lower a temperature of the depositing surface while the same flame is generated. The temperature of the depositing surface is determined by a balance among an amount of dissipating heat from the depositing surface by radiation, an amount of heat received from the flame and an amount of heat incoming from the muffle by radiation. Therefore, when the amount of heat incoming from the muffle tube is decreased by decreasing the temperature of the muffle tube surface, the temperature of the depositing surface is decreased so that the deposition efficiency of the glass soot is improved. In the muffle tube, since water is generated by a reaction between hydrogen (H₂) and oxygen (O₂), a vapor pressure in the muffle tube is higher than that in the external atmosphere. When the temperature of the muffle wall is cooled to room temperature, for example, 20°C, dew condensation occurs on the muffle wall. As explained above, when the dew is formed in the muffle tube, the life of the muffle tube is shortened by corrosion, or the corroded metal is splashed and contaminates the glass soot deposit, namely a glass preform. Then, the optical fiber fabricated from such contaminated preform has large transmission loss. The dew condensation can be prevented by maintaining the surface temperature of the muffle tube at a temperature higher than a dew point. However, when the surface temperature of the muffle tube is raised excessively, the amount of the radiation heat from the muffle tube to the surface of the glass soot deposit increases and then the surface temperature of the glass soot deposit rises. When the surface temperature of the glass soot deposit rises, the thermophoresis effect is decreased so that the deposition efficiency of the glass soot is deteriorated. That is, in order to increase the deposition efficiency of the glass soot while preventing the dew condensation on the muffle wall, the surface temperature of the muffle tube is decreased as low as possible insofar as the surface temperature is not lower than the dew point in the muffle tube. According to the experiments, it has been found that the dew condensation occurs when the surface temperature of the muffle tube is 45°C or lower. According to the study on a relationship between the deposition rate of the glass soot and the average surface temperature of the muffle tube, the deposition rate is substantially the same when the average surface temperature of the muffle tube is in the range between 50°C and 150°C. Accordingly, to increase the deposition rate of the glass soot while preventing the dew condensation, the lowest surface temperature of the muffle tube is at least 50°C, and the average surface temperature of the muffle tube is in the range between 50°C and 150°C. Other conditions for depositing the glass soot on the starting member are substantially the same as those in the conventional methods. PREFERRED EMBODIMENTS OF THE INVENTION The present invention will be illustrated by the following examples. Comparative Example 1 A concentric twelve-port burner was used. From the first port (the center port), a glass-forming raw material (SiCl₄) was supplied at a flow rate of 10 liter/min. From each of the second, sixth and tenth ports, hydrogen gas (H₂) was supplied at a flow rate of 200 liter/min. From each of the fourth, eighth and twelfth ports, oxygen gas (O₂) was supplied at a flow rate of 200 liter/min. From each of the third, fifth, seventh, ninth and eleventh ports, argon was supplied at a flow rate of 40 liter/min. Thereby, a glass soot deposit was produced without cooling the muffle tube. The temperature of the muffle tube was between 350°C and 450°C (average: 400°C), the maximum surface temperature of the deposit was 1080°C, and a deposition rate was 16.1 g/min. Comparative Example 2 In the same manner as in Comparative Example 1 except that a water-cooling muffle tube was used and the muffle temperature was maintained in a range between 10°C and 100°C (average: 50°C), the glass soot deposit was produced. When the muffle tube temperature was 48°C or lower, the dew condensation occurred and the muffle was corroded. The maximum surface temperature of the deposit was 970°C and a deposition rate was 17.3 g/min. Example 1 In the same manner as in Comparative Example 1 except that a water-cooling muffle tube was used and the muffle temperature was maintained in the range between 50°C and 150°C (average 90°C), the glass soot was deposited. No dew condensation occurred. The maximum surface temperature of the deposit was 990°C and a deposition rate was 17.1 g/min. Example 2 In the same manner as in Comparative Example 1 except that a water-cooling muffle tube was used and the muffle temperature was maintained in the range between 90°C and 190°C (average 140°C), the glass soot was deposited. No dew condensation occurred. The maximum surface temperature of the deposit was 1000°C and a deposition rate was 17.0 g/min. As understood from the above results, the deposition rate was smallest in Comparative Example 1 in which the muffle tube was not cooled. In Comparative Example 2, the deposition rate was large but the muffle was corroded. In Examples 1 and 2 according to the present invention, substantially the same deposition rate was achieved as in Comparative Example 2 wherein the muffle tube was cooled to 50°C. Also, in Examples 1 and 2, the corrosion of the muffle tube was prevented. Accordingly, the method of the present invention can increase the deposition rate and prevent the corrosion of the muffle tube.

Claims: A method for producing a glass soot deposit, which comprises steps of: blowing a gaseous glass-forming raw material together with a fuel gas from a combustion burner in a closed muffle tube, hydrolysing said glass-forming raw material in a flame to generate glass soot, and depositing said glass soot on a tip end or a peripheral surface of a starting member which is rotated to form a glass soot deposit, characterized in that a lowest surface temperature of said muffle tube is maintained at 50°C or higher and an average surface temperature of said muffle tube is maintained in a range between 50°C and 150°C. The method according to Claim 1, wherein said muffle tube has a cooling pipe on its outer wall and a cooling liquid which is kept at a constant temperature is flowed in said cooling pipe. The method according to Claim 2, wherein said muffle tube has a double-wall structure and a cooling liquid which is kept at a constant temperature is flowed between the walls.

Inventors: DANZUKA TOSHIO, SAITOH TATSUHIKO, DANZUKA, TOSHIO, SAITOH, TATSUHIKO, DANZUKA, TOSHIO, C/O YOKOHAMA WORKS OF SUMITOMO, Saitoh, Tatsuhiko, c/o Yokohama Works of Sumitomo
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD
Application year: 1992
Main classification: C03B37
IPC codes: C03B37, C03B20, G02B6, C03B8