Interpolymer-based binders

Abstract: Hydroxyl groups and carboxyl groups containing interpolymers, obtainable by radical solution polymerization of: (a) hydroxyalkyl esters of ethylenically unsaturated acids; (b) an ethylenically unsaturated acid such as specified hereinbefore, in an amount of from 4 to 20 %wt, calculated relative to the weight of the complete monomer mixture; (c) alkyl esters of ethylenically unsaturated acids; (d) VeoVa 10 (a trademark), optionally mixed with VeoVa 9 (a trademark); and (e) alkyl esters of methacrylic acid and/or acrylic acid.

Description: This invention relates to interpolymer-based binders (interpolymers of acrylic acid and comonomers), the process of their preparation, and their uses, in particular their use in aqueous coatings, such as automotive coatings. For economic and ecological reasons, there is a trend towards aqueous coatings. Particular attention is paid to the development of aqueous topcoats. Such topcoats have to meet increasingly severe requirements in respect of their resistance to alkaline and organic solvents (especially brine and gasoline/diesel), and in respect of their weatherability (resistance towards exposure to ultra-violet light and heat fluctuations as encountered near the bonnet). Furthermore, the binders used for such coatings should have excellent adherence to the primer, readily incorporate colourants, metal particles (metallic lacquers) and other common coating additives, and be easily and adequately applied on the substrate in an ecologically acceptable way. Finally, the applied coating must be hard enough to resist being scratched, but be flexible enough not to scatter upon impact. Today, several binders are available that will lead to acceptable results, however, each having one or more slight draw-backs. For instance, the styrene/acrylic acid based binders (e.g., International patent application WO 90/00570) are cheap, hydrophobic, but turn yellow in time and have a pigment wetting ability which is just acceptable. The "all-acrylics" binders (e.g., German patent application No. 2,032,647) have excellent flexibility, but are relatively more expensive, are less hydrophobic and as a consequence thereof, have a poor pigment wetting ability, and their coatings are ecologically suspect due to the residual monomer content. Subject of a recently filed patent application (European patent application No. 91201546.8) are binder systems, wherein the styrene in the styrene/acrylic based systems is replaced by the vinylester of a C 9 tertiary saturated monocarboxylic acid ("VeoVa 9", a trademark). These binders are hydrophobic, have a good pigment wetting ability, do not turn yellow upon exposure to light, have excellent alkali and solvent resistance, and have an excellent resistance towards ultra violet light. Nevertheless, topcoats prepared from these binders, despite the aforementioned advantageous properties in combination with outstanding hardness, may still be further improved in respect of their flexibility and costs. Other coating compositions, such as disclosed in British patents 1,145,564 and 1,087,623, are unsuitable in that they use an organic solvent as vehicle and replacement without any adaptation of such organic solvent by an aqueous vehicle gives only unstable solutions and unattractive coating compositions. It will be appreciated that there is a still growing need for high quality, heat-curable topcoat compositions, which can meet the requirements of the present industrial application. With respect to the automotive industry, where controlled, highly automated standardised coating operations and heat curing (stoving) operations are common, which operations should be carried out in a relatively short and reproducible fashion, relatively cheap and easily prepared topcoat compositions are highly desired. More particularly, due to the ever increasing environmental concern, there is a still growing need for aqueous automotive coatings and more particularly heat curable, automotive topcoats which fulfil the aforementioned requirements, in particular in respect of the balance of hardness and flexibility without the loss of any of the other properties. For such heat curing automotive topcoats the use of any surfactant to disperse the interpolymer and relatively large amounts of ethylenically unsaturated acid comonomer, must be avoided, as it will deteriorate the properties of the final film. Therefore, it is an object of the present invention to provide interpolymers having both the aforementioned properties in combination with an excellent water dispersability. As a result of extensive research and experimentation this aim could surprisingly be reached by providing a hydroxyl groups and carboxyl groups containing interpolymer, obtainable by radical solution polymerization at a temperature in the range of from 110 to 150 °C, in an inert, water-miscible organic solvent system, of: (a) hydroxyalkyl esters of ethylenically unsaturated acids, in particular those esters wherein the acid moiety contains from 2 to 9 carbon atoms, and wherein the hydroxyalkyl moiety contains from 2 to 6 carbon atoms and preferably 2 to 4 carbon atoms in an amount of from 4 to 20 %wt, calculated relative to the weight of the complete monomer mixture; (b) an ethylenically unsaturated acid, in particular such as specified hereinafter, in an amount of from 3 to 20 %wt, calculated relative to the weight of the complete monomer mixture; (c) alkyl esters of ethylenically unsaturated acids, in particular esters of ethylenically unsaturated acids such as specified hereinafter, the alkyl group of which may contain from 4 to 8 carbon atoms and preferably 4 to 6 carbon atoms, in an amount of from 10 to 40 %wt, calculated relative to the weight of the complete monomer mixture; (d) the vinyl ester of a branched saturated monocarboxylic acid, containing in the acid moiety 10 carbon atoms, in an amount of from 10 to 60 %wt, calculated relative to the weight of the complete monomer mixture; and (e) alkyl esters of methacrylic acid and/or acrylic acid, wherein the alkyl group contains from 1 to 3 carbon atoms and preferably represents a methyl group, in an amount of from 15 to 50 %wt, calculated relative to the weight of the complete monomer mixture; the sum of the respective amounts of components being 100%. Suitable examples of ethylenically unsaturated acids containing from 2 to 9 carbon atoms are methacrylic acid, acrylic acid, crotonic acid, isocrotonic acid, ethacrylic acid, phenylacrylic acid, maleic acid, fumaric acid, itaconic acid and citraconic acid. Suitable examples of hydroxyalkyl esters of ethylenically unsaturated acids contain primary or secondary hydroxyl groups, such as hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxybutyl acrylate, hydroxyamyl acrylate, hydroxyhexyl acrylate, hydroxyoctyl acrylate and the corresponding methacrylates, crotonates, isocrotonates, maleates and fumarates, and 2-hydroxypropyl acrylate, 2-hydroxybutyl acrylate, 3-hydroxybutyl acrylate and the corresponding methacrylates, crotonates, isocrotonates, maleate and fumarates. Suitable examples of lower alkyl esters of ethylenically unsaturated acids (component e) are methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, isopropyl (meth)acrylate. Preferred comonomer component (a) is selected from hydroxyethyl esters of the hereinbefore specified ethylenically unsaturated acids and the most preferred comonomers are hydroxyethyl methacrylate ("HEMA") or hydroxyethyl acrylate ("HEA"). Preferred comonomer component (b) is selected from acrylic acid ("AA") and/or methacrylic acid. Preferred comonomer component (c) is selected from n-butyl esters, iso-butyl esters, n-pentyl esters, isopentyl esters or n-hexyl esters of the hereinbefore specified acids and the most preferred comonomers are n-butyl esters of acrylic acid ("NBA") and/or methacrylic acid. As comonomer component (d) preferably solely a vinyl ester of a C 10 saturated tertiary monocarboxylic acid, such as sold under "VeoVa 10" (VeoVa is a trademark) is used. Preferred comonomer component (e) is selected from methyl acrylate, methyl methacrylate ("MMA"), ethyl acrylate or ethyl methacrylate. In more preferred comonomer starting mixture, the amounts of hydroxyalkyl esters of ethylenically unsaturated acid (component (a)) and of ethylenically unsaturated acid (component (b)) are set in the range of from 8-11 and preferably at 9 %wt and in the range of from 4 to 8 and preferably at 6 %wt respectively, whereas the amounts of the components (c), (d) and (e) may vary within the ranges specified in figure 1. It is observed that figure 1 is a superimposition of three regression lines Y 3 , Y 4 , and Y 5 indicating the compositions containing a given amount of the component (c), (d) and (e) that meet the requirements in respect of: the König hardness of the film in sec., as defined hereinafter (Y 3 ), having a value of at least 140; the flexibility in 0.0115 kg.m (inch.lb), to be defined hereinafter (Y 4 ) and having a value of at least 40; and the methyl ethyl ketone resistance in db. rub. to be defined hereinafter (Y 5 ) and having a value of at least 100. In addition by meeting these requirements, simultaneously the requirements in respect of the properties storage stability of the aqueous interpolymer suspension in days as defined hereinafter (Y1) and having a value of at least 42; the conversion degree in %wt (Y 2 ) being at least 99.5 %wt are met. The indicated minimum values of Y 1 -Y 5 relate to requirements made as to the most excellent automotive topcoating characteristics. The equations of the regression lines are the following: (i) Y 3 = 62 X 1 - 60 X 2 + 134 X 3 + 265 X 1 .X 2 + 728 X 1 .X 3 + 946 X 2 .X 3 - 1924 X 1 .X 2 .X 3 ; (ii) Y 4 = 348 X 1 + 56 X 2 - 10 X 3 - 765 X 1 .X 2 - 640 X 1 .X 3 + 187 X 2 .X 3 + 1372 X 1 .X 2 .X 3 ; (iii) Y 5 = -30 X 1 + 38 X 2 + 335 X 3 - 275 X 1 .X 2 + 22 X 1 .X 3 - 837 X 2 .X 3 + 4735 X 1 .X 2 .X 3 ; wherein X 1 represents the weight fraction of component (d), preferably being VeoVa 10; X 2 represents the weight fraction of component (c), preferably being butylacrylate; X 3 represents the weight fraction of component (e), preferably being methyl methacrylate. The most preferred comonomer starting compositions are those comprising: (a) from 4 to 13 %wt hydroxyethylacrylate, (b) from 4 to 11 %wt acrylic acid, (c) from 10 to 15 %wt butyl acrylate, (d) from 40 to 43 %wt VeoVa 10, and (e) from 30 to 35 %wt methyl methacrylate, the total amounting to 100%. The "storage stability" as used for Y 1 is measured at 40 °C. To obtain an indication of interpolymer suspension storage stability, an accelerated test is carried out at 40 °C on a sample of about 100 ml. Viscosity, pH and settlement of solids are noted after various periods of time e.g. 1, 2, 4 and 8 weeks. After 6 weeks the suspension is only allowed to show slight settlement of solids which solids can be easily redispersed, whereas no change in overall viscosity may occur. The "MEK rubs" is the number of double rubs given by hand to the cured coating with a cloth wetted with methyl ethyl ketone until the coating was wiped off. "MEK rubs" greater than 100 is an indication of a good cure and solvent resistance. The "flexibility" or impact strength is measured as reverse impact strength determined according to the British Standard Falling Ball test. The conversion degree is determined by residual monomer measurement by GLC procedure which measures residual monomers separately by using standard calibration of the analysis equipment for each monomer to be included in the comonomer starting mixture. The analysis should be carried out shortly after preparation of interpolymer suspension and before adjustment, if any, of pH. Using this GLC method residual monomer concentrations down to at least 0.1 %wt (free monomer based on interpolymer mass) can be measured separately for the respective monomers. The method makes use of a gas chromatograph equipped as described in principle in Shell Resins, VeoVa Technical Manual VM 2.1 "Principles of design and manufacture of VeoVa latices", issued June 1988, pages 24 and 25. The monomer content is calculated as defined on page 26 of this Technical Manual. The hardness of the film Y 3 is measured as König hardness, determined using an Erichson (trademark) apparatus. The "film thickness" as indicated throughout the present specification was determined with a Permascope ES (trademark) of Fisher. The viscosity values as indicated throughout the present specification were determined using a Brookfield (trademark) viscosimeter at a temperature of 23 °C. The present interpolymers may be prepared by radical solution polymerisation of the monomer components (a) to (e) at a temperature in the range of from 110 to 150 °C in an inert, water miscible organic solvent for which several organic solvents types may be used, such as glycol ethers, esters, and alcohols or mixtures thereof. Examples of suitable solvents are: relatively high boiling alcohols, such as n-hexanol, 2-ethyl hexanol, isooctyl alcohol, isononyl alcohol, isodecyl alcohol, isotridecyl alcohol, cyclohexanol, methylcyclohexanol, tetrahydrofuryl alcohol, diacetone alcohol, 2,6-dimethyl-4-heptanol, 4-methyl-2-pentanol, tridecanol, glycols and glycol derivatives, such as ethyleneglycol, 1,2-propyleneglycol, 1,3-butyleneglycol, butanediol-1,4, hexyleneglycol, 2-ethylhexanediol-1,3, diethyleneglycol, triethyleneglycol, dipropyleneglycol, trihydroxymethyl propane and ethoxylated or ether derivatives thereof. A preferred class of solvents to be used for said radical solution polymerization are diols and those according to the formulae: wherein R 1 and R 2 each may independently represent hydrogen or lower alkyl group having from 2 to 6 carbon atoms and preferably from 3 to 4 carbon atoms, under the proviso that at most one of R 1 and R 2 may represent hydrogen, and wherein R 3 , R 4 and R 5 each may independently represent hydrogen, hydroxyl or ethoxylated hydroxyl, or lower alkyl as specified hereinbefore, under the proviso that at most one of the symbols R 3 , R 4 and R 5 may represent hydroxyl, ethoxylated hydroxyl, or propoxylated hydroxyl. The most preferred class of solvents are those according to the formulae I or II wherein R 3 , R 4 and R 5 are hydrogen and wherein R 1 or R 2 is lower alkyl. As most preferred solvent "BUTYLOXITOL" (ethylene glycol mono-n-butylether; both BUTYLOXITOL and OXITOL are registered trademarks) is used. The solvent is used in an amount of from 10 to 20 %wt of the total weight of the monomers and preferably in an amount of from 12 to 17 %wt. In general the radical solution polymerization is carried out by starting with an initial reactor charge of the solvent in the indicated amount and therein dissolved an amount of from 5 to 15 %wt of the total amount of the VeoVa (tm) and from 1 to 8 %wt of the total amount of the ethylenically unsaturated acids and esters thereof. According to a preferred embodiment amounts of 10 %wt of VeoVa (tm) and 0 to 10% of the total amount of (meth)acrylates and (meth)acrylic acids are used. To this initial reactor charge, heated up to the desired reaction temperature, which is maintained at the same value during the further addition, the remaining VeoVa (tm) and ethylenically unsaturated acids and esters, as specified hereinbefore, and an amount of initiator of from 1 to 5 %wt and preferably of from 2 to 4.5%wt, calculated relative to the total weight of the monomers, are gradually added within a period of from 3 to 5 hours and preferably of from 3.5 to 4.5 hours, followed by a post reaction during from 1 to 3 hours and preferably of 2 hours, after optional addition of an additional smaller proportion of the total initiator amount. As initiator for the radical polymerization a great variety of organic peroxide compounds can be used such as dibenzoylperoxide, dicumylperoxide, cumylhydroperoxide, di-t-butylperoxide, t-butylperoxybenzoate, t-butylhydroperoxide, 2,2-di-t-butylperoxybutane, t-amylperbenzoate, 1,3-bis(t-butylperoxyisopropyl)benzene, diisopropylbenzene monohydroperoxide and diacylperoxide, such as diacetylperoxide; peroxyketal, such as 2,2-di(t-amylperoxy)propane, t-amylperoxy-2-ethylhexanoate and ethyl-3,3-di(t-amylperoxy)butyrate or aliphatic azo compounds such as azobiscyclohexane nitrile. As preferred initiator is used t-butylperoxybenzoate (Trigonox C, a trademark) in an amount of from 2 to 4.5%wt, calculated relative to the total weight of monomers. It will be appreciated that, if necessary, the radical solution polymerization can be carried out in the presence of a small amount of polymerization regulators, such as mercapto compounds and preferably mercapto ethanol, and alkyl mercaptanes, such as t-dodecyl mercaptane, octyl mercaptane, phenyl mercaptane, octyldecyl mercaptane, butyl mercaptane; thiocarboxylic acids such as thioacetic acid or thiolactic acid. These regulators can be applied, if necessary, in an amount of up to 2 %wt, calculated relative to the complete weight of the comonomers. Preferably said regulators are dissolved in the monomer mixture to be gradually added and the concentration of them is kept constant during the polymerization time period. After substantial completion of the polymerization reaction, the reaction mixture is neutralized with an organic base and homogenized, and water is added to the organic phase in a volume of from 10 to 1 times the organic phase volume and preferably of from 5 to 1.5 times the organic phase volume, whereupon a homogeneous, stable aqueous interpolymer dispersion is obtained. Alternatively, the organic base may be dissolved in water, and the reaction mixture may be added to the aqueous organic base solution, whereupon again a stable aqueous interpolymer dispersion is obtained. The neutralization of the carboxyl groups of the initially prepared interpolymers can be carried out by using organic amines such as aminomethylpropanol, aminomethylbutanol, dimethylethanolamine, diethylethanolamine, triethanolamine, monoisopropanolamine, diisopropanolamine, triisopropanolamine, 2-dimethylamino-2-methyl-1-propanol, of which the environmental friendly ones are preferred. It will be appreciated that another aspect of the present invention is formed by curable aqueous coating compositions derivable from the hereinbefore specified aqueous interpolymer compositions. These curable aqueous coating compositions may be prepared from the initially prepared aqueous interpolymer compositions, to which curing agents or cross-linking agents are added. Such curing or cross-linking agents may be selected from aminoplast resins, polyisocyanates or anhydride groups containing compounds. Said curing agents are added in such an amount, that the molar ratio between the hydroxyl groups occurring in the interpolymer and the reactive groups of the curing agent is in the range of from 0.3:1 to 3:1. Attractive curing or cross-linking resins for curable coating systems are for example those disclosed in European patent applications Nos. 244,897 and 281,213. Particularly suitable cross-linking agents are the ambient curing reactive isocyanates and thiols, as well as the high temperature curing aminoplast-type resins, such as alkoxylated reaction products of formaldehyde with melamine or benzoguanamide. Other suitable cross-linking agents include urea-aldehyde resins, phenol-aldehyde resins, bisphenolic or anhydride curing agents, polycarboxylic compounds, dicyandiamide and blocked polyisocyanates. When some types of these cross-linking agents are used, catalysts may be added to the curable coating compositions to reach curing at lower stoving temperatures. Suitable catalysts which may be employed in the curable coating compositions for this purpose are acids such as orthophosphoric acid or p-toluenesulphonic acid. These catalysts may be used in an amount in the range of from e.g. 0.05 to 2 %wt, calculated as pure catalyst relative to the interpolymer and cross-linking agent. The relative weight proportion of the interpolymer resin relative to the weight of interpolymer and curing agent is typically of from 5 to 50 %wt, calculated relative to the total weight of the interpolymer and curing agent. For the most preferred curable aqueous coating compositions the weight proportion of the curing agent, such as hexamethoxymethyl melamine (Cymel 301, a trademark) is from 10 to 30 %wt and most preferably from 13 to 17 %wt. The curable coating compositions according to the present invention can be applied by a variety of methods known in the art, for example by spraying, electrodeposition, dipping or brush- or roller coating. Pigments, fillers, dispersing agents and other components known for coating formulations may be added to the curable binder system comprising the interpolymers according to the present invention. Such curable coating compositions show, after application, preferably by spraying and baking, excellent properties and more particularly when applied as automotive topcoats. Baking will comprise a flash-off step during from 1 to 10 minutes at a temperature of from 60 to 80 °C, and preferably at 70 °C, followed by a curing step of from 5 to 60 minutes and preferably from 20 to 40 minutes and at a temperature of from 100 to 200 °C and preferably of from 120 to 160 °C. Most preferably the flash-off step will be carried out at 70 °C during 5 minutes and the curing step will be carried out at 140 °C during 30 minutes. It will be appreciated that another aspect of the present invention is formed by a process for the preparation of the aforementioned interpolymers and of curable aqueous coating compositions, by: (1) starting with an initial reactor charge of the solvent in an amount of from 10 to 20 %wt of the total weight of the monomers, wherein has been dissolved an amount of from 0 to 15 %wt of the total amount of component (d), and from 0 to 10 %wt of the total amount of each of the components (a), (b), (c) and (e); (2) heating the reactor charge to the desired reaction temperature; and, (3) at this substantially constant temperature, gradually adding the remaining monomers and an amount of initiator of from 1 to 5 %wt and preferably from 2 to 4.5%wt, calculated relative to the total weight of the monomers, within a period from 3 to 5 hours and preferably from 3.5 to 4.5 hours, followed by a post reaction during from 1 to 3 hours and preferably 2 hours. The process for the preparation of curable aqueous coating compositions according to the present invention comprises: (1) preparing the interpolymers according to present invention; (2) neutralizing the reaction mixture after substantial completion of the reaction with a base and preferably an organic base; (3) homogenising and adding water to the organic phase in a volume of from 10 to 1 times the organic phase volume and preferably of from 5 to 1.5 times the organic phase volume; and (4) mixing the obtained homogeneous stable aqueous interpolymer suspension with a curing or cross-linking agent in an amount, such that the molar ratio between the hydroxyl groups occurring in the interpolymer and the reactive groups of the curing agent is in the range of from 0.3:1 to 3:1 and/or the relative weight proportion of the interpolymer is in the range of from 5 to 50 %wt and preferably from 10 to 20 %wt and more preferably from 13 to 17 %wt. The invention is illustrated by the following examples, however, without restricting its scope to these preferred specific embodiments. Example 1 Several interpolymer compositions were prepared (experiments 1-4) in a 1-litre glass reactor, equipped with a thermocouple, a condenser, a stainless steel stirrer and a nitrogen inlet, starting from varying weight proportions of the hereinafter specified comonomers. BUTYLOXITOL (tm) was charged to the reactor and heated to 130 °C, at which point the comonomer mixture and 2% m/m on the monomers of the initiator t-butylperoxybenzoate (Trigonox C, a tm) were added regularly over a period of 4 hours with the aid of a pump. After the addition period, 0.75% m/m on monomers of the initiator was added and the solution temperature is kept at 130 °C for 2 hours. After the period the reactor content is cooled down to room temperature. The respective weight proportions of the comonomers in the total comonomer intake are listed hereinafter in Table I. Comparative Example 2 About the same procedure as described in Example 1 was followed (comparative exp. A-E) with the difference that either a comonomer mixture was used, the amount of ingredients of which was not in accordance with the invention, or the comonomer mixture comprised VeoVa 9 (tm) instead of VeoVa 10 (tm) (cf. European patent application No. 91201546.8). Aqueous binder preparation Aqueous dispersions of the resulting interpolymers were prepared by neutralization of the same with aminomethylpropanol (AMP). The AMP was carefully added and slowly mixed for 30 minutes. Water was then added to obtain a dispersion having a viscosity of about 100 mPa.s (a final solids content of 20-30 %wt). The stability of the aqueous dispersions were assessed by visually observing any phase separation and by regularly measuring the pH and the viscosity upon storage at 40 °C. Both the comparative experiments as the inventive experiments passed the minimum requirement. Coating compositions From the above aqueous dispersions coating compositions were prepared by mixing 20.0 g of interpolymer, 3.5 g of hexamethoxymethylmelamine (Cymel 301, a tm), i.e., in a weight ratio of 85/15, and 0.07 g of p-toluenesulphonic acid. These coating compositions contained about 10 %wt of initially applied solvent. The coating composition of experiment 3, however, is based on a weight ratio of interpolymer/Cymel 301 (tm) of 85/15 (exp. 3a) and 70/30 (exp. 3b). Stoving Some relevant interpolymer properties and film properties of the cured coating films were assessed by applying the coating compositions onto bare steel panels by a barcoater in a dry film thickness of 20 µm, followed by a flash-off at 70 °C for 5 minutes and a stoving at 140 °C for 30 minutes. The properties are listed in Table II. As to cured coating film properties, the coating film was applied after at least three days from the preparation of the curable coating composition. Total comonomer compositions Experiments hydroxyethyl acrylate % m/m acrylic acid % m/m n-butyl acrylate % m/m VeoVa 10 % m/m methyl methacrylate % m/m A 9 6 10 10 65 B 9 6 65 10 10 C 9 6 10 65 10 1 9 6 10 37.5 37.5 2 9 6 28.33 28.33 28.33 3 3 9 32.1 28.3 27.6 4 9 9 28.0 28.3 25.7 VeoVa 9 E 9 6 28.33 28.33 28.33 D 9 6 37.5 23.75 23.75 Experiments Conversion % wt Thickness µm Hardness sec Flexibility kg.m (inch.lb) Solvent MEK db rubs. A 99.5 20 186 0.07(6) >100 B 99.7 20 54 0.40(35) 15 C 99.8 20 109 1.73(150) 25 1 99.7 20 188 0.46(40) >100 2 99.7 20 150 0.52(45) >100 3a 99.5 20 110 0.75(65) >100 3b 99.5 20 145 0.58(50) >100 4 99.7 20 160 0.46(40) >100 D 99.6 21 162 0.35(30) 100 E 99.5 21 139 0.58(50) 90 From Table II it can be clearly seen that the coatings prepared from aqueous dispersions in accordance with the invention have a better balance of properties than the best results of European patent application No. 91201546.8 using VeoVa 9 (tm).

Claims: Hydroxyl groups and carboxyl groups containing interpolymers, obtainable by radical solution polymerization at a temperature in the range of from 110 to 150 °C in an inert, water miscible organic solvent system, of: (a) hydroxyalkyl esters of ethylenically unsaturated acids, wherein the hydroxyalkyl moiety contains from 2 to 6 carbon atoms in an amount of from 4 to 20 %wt, calculated relative to the weight of the complete monomer mixture; (b) an ethylenically unsaturated acid, in an amount of from 3 to 20 %wt, calculated relative to the weight of the complete monomer mixture; (c) alkyl esters of ethylenically unsaturated acids, the alkyl group of which may contain from 4 to 8 carbon atoms, in an amount of from 10 to 40 %wt, calculated relative to the weight of the complete monomer mixture; (d) the vinyl ester of a branched saturated monocarboxylic acid, containing in the acid moiety 10 carbon atoms, in an amount of from 10 to 60 %wt, calculated relative to the weight of the complete monomer mixture; and (e) alkyl esters of methacrylic acid and/or acrylic acid, wherein the alkyl group contains from 1 to 3 carbon atoms, in an amount of from 15 to 50 %wt, calculated relative to the weight of the complete monomer mixture; the sum of the respective amounts of monomer components being 100%. Interpolymers according to claim 1, characterized in that component (a) is hydroxyethyl (meth)acrylate. Interpolymers according to claim 1, characterized in that component (b) is acrylic acid and/or methacrylic acid. Interpolymers according to claim 1, characterized in that as component (c) n-butyl esters of acrylic acid and/or methacrylic acid are used. Interpolymers according to claim 1, characterized in that as component (d) a C 10 saturated tertiary monocarboxylic acid is used. Interpolymers according to claim 1, characterized in that component (e) is selected from methyl acrylate, methyl methacrylate, ethyl acrylate and ethyl methacrylate. Interpolymers according to claim 1, characterized in that the amounts of hydroxyalkyl esters of ethylenically unsaturated acid (component (a)) and of ethylenically unsaturated acid (component (b)) are set in the range of from 8-11 %wt and preferably at about 9 %wt and in the range of from 4 to 8 %wt and preferably at about 6 %wt respectively, whereas the amounts of the components (c), (d) and (e) may vary within the hereinbefore specified ranges while simultaneously fulfilling the following equations: (i) Y 3 = 62 X 1 - 60 X 2 + 134 X 3 + 265 X 1 .X 2 + 728 X 1 .X 3 + 946 X 2 .X 3 - 1924 X 1 .X 2 .X 3 ; (ii) Y 4 = 348 X 1 + 56 X 2 - 10 X 3 - 765 X 1 .X 2 - 640 X 1 .X 3 + 187 X 2 .X 3 + 1372 X 1 .X 2 .X 3 ; (iii) Y 5 = -30 X 1 + 38 X 2 + 335 X 3 - 275 X 1 .X 2 + 22 X 1 .X 3 - 837 X 2 .X 3 + 4735 X 1 .X 2 .X 3 ; wherein X 1 represents the weight fraction of component (d), preferably being VeoVa 10 (tm), (tm); X 2 represents the weight fraction of component (c), preferably being butylacrylate; X 3 represents the weight fraction of component (e), preferably being methyl methacrylate; and wherein Y 1 represents the storage stability of the aqueous interpolymer suspension in days and having a value of at least 42; Y 2 represents the conversion degree in %wt being at least 99.5%; Y 3 represents the König hardness of the film in sec., having a value of at least 140; Y 4 represents the flexibility in 0.0115 kg.m (inch.lb.) and having a value of at least 25; and Y 5 represents the methyl ethyl ketone resistance in db. rub. and having a value of at least 100. Interpolymers according to claim 1, characterized in that they are derivable from comonomer compositions comprising: (a) from 4 to 13 %wt hydroxyethylacrylate, (b) from 4 to 11 %wt acrylic acid, (c) from 10 to 15 %wt butyl acrylate, (d) from 40 to 45 %wt VeoVa 10, and (e) from 30 to 35 %wt methyl methacrylate, the total amounting to 100%. A process for preparing interpolymers according to anyone of claims 1 to 8, comprising radical solution polymerizing the monomer components (a) to (e) at a temperature in the range of from 110 to 150 °C in an inert, water miscible organic solvent system. A process according to claim 9, comprising: (1) starting with an initial reactor charge of the solvent in an amount of from 10 to 20 %wt of the total weight of the monomer components, wherein has been dissolved an amount of from 0 to 15 %wt of the total amount of component (d), and from 0 to 10 %wt of the total amount of each of the monomer components (a), (b), (c) and (e); (2) heating the reactor charge to the desired reaction temperature; and, (3) at this substantially constant temperature, gradually adding the remaining monomer components and an amount of initiator of from 1 to 5 %wt and preferably from 2 to 4.5 %wt, calculated relative to the total weight of the components, within a period from 3 to 5 hours and preferably from 3.5 to 4.5 hours, followed by a post reaction during from 1 to 3 hours and preferably 2 hours. The use of interpolymers according to claims 1 to 8 in curable aqueous coating compositions containing a curing agent or cross-linking agent, and in cured coating compositions obtained upon heat-curing the curable aqueous coating compositions.

Inventors: ANDRE OLIVIER LOUIS PIERRE, GERETS CARINE HELENA PAULA, SCHOLTEN HENRICUS PAULUS HUBER, ANDRE, OLIVIER LOUIS PIERRE, GERETS, CARINE HELENA PAULA, SCHOLTEN, HENRICUS PAULUS HUBERTUS
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1992
Main classification: C08F218
IPC codes: C09D133, C08L61, C08F18, C08F222, C08F218, C08F220, C09D131, C09D5, C08F20, C08F2