Metal oxide material

Abstract: Provided is a metal oxide material represented by the composition formula of Ln a Sr b Cu 3-x M x O c , where 2.7 ≦ a + b ≦ 3.3 ; 0.8 ≦ a ≦ 1.2; 6 ≦ c ≦ 9; and 0.05 ≦ x ≦ 0.7, Ln is at least one element selected from the group of elements of Y and lanthanoids or an atomic group consisting of said elements, and M is at least one element selected from the group of elements of Ti, V, Ga, Ge, Mo, W and Re or an atomic group consisting of said elements.

Description: The present invention relates to a novel metal oxide material which exhibits superconductivity. In particular, the present: invention relates to a metal oxide material that is useful in various application fields of superconductivity such as sensors, electronic devices, computers, medical apparatus, magnets, power transmission lines, energy instruments, and voltage standards. The metal oxide material of the present invention is especially effective when used as a bulk material. The metal oxide material of the present invention can be used in a state of junction or dispersion with another oxide or a metal. Copper-containing oxide superconductors which have been discovered in succession have critical temperatures of superconductivity (Tc) surpassing that of known metal-type superconductors such as niobium. Therefore, applications thereof are intended in various fields. The known copper-containing oxide superconductors include those of Bi-system, Tl-system, Pb-system, Y-system, and La-system. As a kind of the copper-containing oxide superconductors, those composed of Sr, Ln (Y or a lanthanoid element), Cu and oxygen having a composition of YSr 2 Cu 3 O y are disclosed in papers of Japanese Journal of Applied Physics, Vol. 26, L804 (1987); Solid State Communication, Vol. 63, 535 (1987); and Preprint for Autumnal Meeting of Japan Physical Society, Third Part, page 243, [2p-PS-30]. Further, another superconductor having the composition YSr 2 Cu 3-x MO y (M = Al, Fe, Co, or Pb, and 0.4 ≦ x ≦ 1.0) is disclosed in Chemistry of Materials, Vol. 1, 331 (1989). The aforementioned Bi-system, Tl-system, and Pb-system of superconductors have undesirably a specific gravity of as high as from 7 to 8 g/cm 3 , so that a bulk material (for example, a shield material) made therefrom inevitably becomes weighty in its entirety, disadvantageously. A known Sr-based 123-phase material, which has a lower specific gravity than the above-mentioned material, has disadvantages of unavoidable contamination by a large amount of impurities, difficulty in the synthesis, and the low Tc (approximately 20 K). For example, the compositions disclosed in Japanese Journal of Applied Physics, Vol. 26, L804 (1987) and Solid State Communication, Vol. 63, 535 (1987) do not give a single phase high-quality sample of YSr 2 Cu 3 O y , but include many impurities such as SrCuO 2 , Sr 2 CuO 3 , Y 2 SrO 4 , Y 2 CuO 5 , SrCu 2 O 2 , and Sr 1.75 Cu 3 O 5.13 , and therefore the product is not practically useful. Thus the synthesis products of the Sr-based 123-phase material contain the superconducting material only at a small content even though the product is satisfactory in its light weight, and are not useful. The sample described in the aforementioned Preprint for Autumnal Meeting of Japan Physical Society, Third Part, page 243 was synthesized by means of a special apparatus employing conditions of 7.0x10 6 Pa (70 Kbar) and 1380°C which was riot generally available, therefore being unsuitable for practical applications. Furthermore, even with such a special apparatus, the synthesized product exhibited a zero-resistance temperature (the temperature at which the resistance becomes zero) of about 20 K. The material disclosed in Chemistry of Materials, Vol. 1, 331 (1989), which exhibits superconductivity in the case of M = Co or Fe, and has the zero-resistance temperature of as low as 10 K, has a superconductivity volume fraction of about 2 %, thus being unsuitable for a superconducting material. Notice is taken of European Patent Application EP-A-0344352. Therein is disclosed an AA'BB' lattice structure high-T c superconductive material, Sr 2 LaCu 2 WO 9 (Oxides:(A)Sr 2 2 ; (A')La 3+ ; (B) Cu 2 2.5+ ; (B')W 6+ ). An object of the present invention is to provide a superconducting material which is synthesizable without using a special synthesis apparatus, without employing ultra-high pressure, and has a high quality with less impurity. Another object of the present invention is to provide a material which has a high superconductivity transition temperature and a large superconductivity volume fraction, and has superior characteristics as a superconducting material. Copper oxide superconductors of Bi-system, Tl-system, and Pb-system such as the aforementioned YBa 2 Cu 3 0 y , which are obtainable stably at present, have an undesirably high specific gravity of 7 to 8 g/cm 3 , so that a bulk material (for example, a shield material) made therefrom inevitably becomes weighty in its entirety disadvantageously. The examples of the present invention given hereinbelow each provide a material which has a lower specific gravity than known copper-oxide superconductors. Embodiments of the present invention provide a material which does not contain a toxic heavy metal in such a large quantity as in Bi-system, Tl-system, or Pb-system of materials, and does not employ a toxic starting material like barium carbonate. A typical Y-system material, YBa 2 Cu 3 O y , is decomposed readily by moisture or water vapour into Y 2 O 3 , BaCO 3 , and CuO, posing a serious problem in practical use thereof and thin film device preparation therefrom. The examples of the present invention given hereinbelow each provide a material which is not sensitive to moisture and water vapor, and has superior endurance. Furthermore, the above YBa 2 Cu 3 O y characteristic deteriorates by liberation of oxygen at a high temperature. For example, the material having the composition of YBa 2 Cu 3 O y at room temperature will lose at 900°C one oxygen in terms of Y or 2.4% by weight. The examples of the present invention given hereinbelow each provide a material which does not readily release oxygen at a high temperature. According to the present invention, there is provided a metal oxide material represented by the composition formula of Ln a Sr b Cu 3-x M x O c where 2.7 ≦ a + b ≦ 3.3; 0.8 ≦ a ≦ 1.2; 6 ≦ c ≦ 9; and 0.05 ≦ x ≦ 0.7, Ln is at least one element selected from the group of elements of Y and lanthanoids, or an atomic group consisting of said elements, and either M = Ti, with 0.2 ≦ x ≦ 0.5, or M = Re with 0.05 ≦ x ≦ 0.4. In the accompanying drawings: Fig. 1 shows the data for YSr 2 Cu 3-x Fe x O 7 described in Chemistry of Materials, Vol. 1, 331 (1989); Fig. 2 shows the X-ray diffraction pattern for the YSr 2 Cu 2.7 Ti 0.3 0 7.0 prepared in Example 1, employing the CuKα radiation; Fig. 3 shows the temperature dependence of the resistivity of the YSr 2 Cu 2.7 Ti 0.3 0 7.0 prepared in Example 1; Fig. 4 shows the temperature dependence of the magnetic susceptibility of the YSr 2 Cu 2.7 Ti 0.3 0 7.0 prepared in Example 1; Fig. 5 shows the X-ray diffraction patterns of the YSr 2 Cu 2.75 Re 0.25 O 7.2 prepared in Example 7 before and after the water-vapor exposure; Fig. 6 shows the X-ray diffraction patterns of the YBa 2 Cu 3 O y prepared in Comparative Example before and after the water-vapor exposure ; Fig. 7 shows the temperature dependences of the resistivity of the YSr 2 Cu 2.75 Re 0.25 O 7.2 prepared in Example 7 before and after the water-vapor exposure ; and Fig. 8 shows the temperature dependences of TG and DTA of the YSr 2 Cu 2.75 Re 0.25 O 7.2 prepared in Example 7. Examples of the present invention given hereinbelow each provide a metal oxide material having a specific gravity of as low as 5 to 6 g/cm 3 and exhibiting superconductivity transition temperature of not lower than 20 K, preferably not lower than 25 K, by selecting the composition ratio of the constituting elements. The metal oxide material of the present invention has a structure similar to YSr 2 Cu 3 O y which is synthesizable only at an extra-high pressure. Nevertheless it can be synthesized at a normal atmospheric pressure, and has improved characteristics of a superconductor. This can be achieved by introducing a selected transition metal to the Cu site in an optimum replacement ratio. The metal oxide material of the present invention may have any composition within the range described above. In the present invention, particularly preferred are copper oxide materials having a composition of Ln a Sr b Cu 3-x M x O c where a = 1 and b = 2, and Ln is any of Y, Ho, Dy, and Gd. A further particularly preferred superconducting material is the above metal oxide material which has a tetragonal or orthorhombic structure and a lattice constant (c) of not less than 1.1 nm (11Å) and not more than 1.2 nm (12Å). A further preferable material is a metal oxide material of the above-mentioned composition having superconductivity at a temperature of not lower than 20 Kelvin, more preferably not lower than 25 Kelvin. The above-described metal oxide material of the present invention nay be prepared by any of generally employed methods of heating powdery raw materials to cause reaction and sintering. Examples of such methods are disclosed in Material Research Bulletin, Vol. 8, p. 777 (1973); Solid State Communication, Vol. 17, p. 27 (1975); Zeitschrift fuer Physik, B, Vol. 64, p. 189 (1986); Physical Review Letters, Vol. 58, No. 9, p. 908 (1987); etc. These methods are well known as general methods at present. In case of use for a superconducting substrate in electronic devices or as shielding materials, the metal oxide material of the present invention is effectively prepared also by melting the powdery raw materials at a high temperature by use of a flux and subsequently growing a single crystal. For use for thin film electronic devices or shielding materials, the metal oxide material of the present invention can be formed in a thin film state on a substrate or another superconducting thin film by any of sputtering methods such as high frequency sputtering or magnetron sputtering employing a target containing the invented materials; vapor deposition such as electron beam vapor deposition, MBE and ionized cluster beam; CVD employing gases as the raw materials; and plasma CVD. The copper oxide material of the present invention thus prepared has a superconductivity transition temperature depending on the firing conditions and the raw material composition. In particular, a high superconductivity transition temperature is obtained when the element M is Re. Accordingly, the metal oxide of the present invention can be used as a superconductor naturally at the liquid helium temperature, and even with a simple refrigerator. Furthermore, the metal oxide material of the present invention can be supplied at a low price since the raw materials therefor are all inexpensive. The material of the present invention is relatively stable and deteriorates less in the open air. This material is highly safe since a toxic raw material such as a heavy metal is not used. The metal oxide material of the present invention has in general a specific gravity in the range of from 5 to 6 g/cm 3 , which is less by about 20 to 30 % than existing copper oxide superconductors. This is an advantage in the case where the metal oxide material is employed as a bulk material for shielding or magnet. The metal oxide material of the present invention is not in general sensitive to moisture or water vapour which advantageously relaxes the using conditions and broadens the application fields of the product, raising the durability, and stabilizing the surface state in preparation of devices. The metal oxide material of the present invention in general does not readily release oxygen at a high temperature, which is an advantage for use or synthesis of the material. The present invention is described more specifically by reference to the following Examples of superconductive material having a transition temperature of not less than 20 K, and Comparative Examples. Of the examples, examples 1, 7-13, 22, 23, 34 and 35 come within the scope of the present invention as defined in claim 1 attached. Examples 1 to 7 and Comparative Examples 1 to 6 The starting materials used were Y 2 0 3 , SrCO 3 , Cu0, Ti0 2 , V 2 0O 5 , Ga 2 0 3 , Ge0 2 , Mo0 3 , WO 3 , Re0 3 , Al 2 0 3 , Mn0 2 , Ni0, Fe 2 0 3 , and CO 2 0 3 . These materials were weighed out in desired composition ratios, and mixed dry. The respective mixtures were pressed into pellets with 10 mm in diameter and 1 mm thick. Each of the formed pellets was reacted and sintered in an alumina boat at a temperature of 950 to 1100°C in the air or in an oxygen atmosphere to prepare the compounds of Example or Comparative Example of the present invention. The sample prepared in such a manner was subjected to measurement of electric resistivity by a four-probe method and measurement of magnetic susceptibility by means of a SQUID in the temperature range of from room temperature to the liquid helium temperature. Table 1 shows the composition ratios and the transition temperatures (K) of the compounds of Examples 1 to 7. Table 2 shows the nominal compositions and the electric characteristics of the oxides of Comparative Examples 1 to 6. The composition ratios were measured by EPMA, so that the quantity of the oxygen may involve an error of about 20%. The oxygen contents in the compounds of Comparative Examples are represented by y, because those can not be measured due to the impurity phases in the compounds. Example No. Composition Characteristic (Tc) Decrease of Tc after water-vapor exposure test (ΔTc) 1 YSr 2 Cu 2.7 Ti 0.3 O 7.0 35K -3K 2 YSr 2 Cu 2.75 V 0.25 O 7.1 27K -2K 3 YSr 2 Cu 2.65 Ga 0.35 O 7.0 38k -3K 4 YSr 2 Cu 2.8 Ge 0.2 O 6.9 28k -3K 5 YSr 2 Cu 2.85 Mo 0.15 O 7.0 67K -5K 6 YSr 2 Cu 2.85 W 0.15 O 7.1 45K -4K 7 YSr 2 Cu 2.75 Re 0.25 O 7.2 48K -4K Comparative Example No. Nominal composition Characteristic (Tc) 1 YSr 2 Cu 3 O y semi-conductor 2 YSr 2 Cu 2.7 Al 0.3 O y semi-conductor 3 YSr 2 Cu 2.6 Mn 0.4 O y semi-conductor 4 YSr 2 Cu 2.6 Ni 0.4 O y semi-conductor 5 YSr 2 Cu 2.6 Fe 0.4 O y 9K 6 YSr 2 Cu 2.5 Co 0.5 O y 9K Table 1 shows that all of the materials of the Examples are superconductors having Tc = 20 K or higher. The replacement of copper with Mo, W, or Re gives superior characteristics especially suitable for a superconductor. Table 2 shows that the materials prepared in Comparative Examples in which the M is an element other than Ti, V, Ga, Ge, Mo, W, and Re do not exhibit superconductivity, or otherwise have Tc of lower than 10 K. Fig. 2 shows the X-ray diffraction pattern of the metal oxide material prepared in Example 1. From Fig. 2, the sample prepared in Example 1 has a tetragonal structure with lattice dimensions of a = b = 3.83 Å, c = 11.5 Å (1Å = 0.1 nm). The materials prepared in other Examples were found to exhibit nearly the same diffraction pattern, thus having the same structure. Fig. 3 is a graph showing the temperature dependence of the electrical resistivity of this sample, showing that the superconductivity transition begins at approximately 40 K and the resistance reaches zero at 35 K. Hence, the metal oxide materials of the present invention become a superconductor at a temperature much higher than the liquid helium temperature. Fig. 4 shows the result of the measurement of temperature dependence of magnetic susceptibility of the metal oxide material prepared in Example 1. The sample of Example 1 exhibits Meissner signal below 35 K, and the superconductivity volume fraction thereof exceeds 20 % at 10 K. The other metal oxide materials prepared in Examples 2 to 7 give similar results, and have sufficient superconductivity. In comparison of the material of the present invention with the data for YSr 2 Cu 3-x Fe x O y shown in Fig. 1 cited from Chemistry of Materials, Vol. 1, 331 (1989), the material of the present invention has a much higher zero-resistivity-temperature and a much higher superconductivity volume fraction. The specific gravity of the material of Example 1 is 5.5 g/cm 3 , being lower by approximately 30 % than existing copper oxide superconductors such as YBa 2 Cu 3 O 7 . The other materials prepared in Examples 2 to 7 also have a specific gravity of not higher than 6 g/cm 3 , being sufficiently light. Fig. 5 shows the X-ray diffraction patterns of the metal oxide material prepared in Example 7 before and after the water-vapor exposure test as described below. Fig. 6 shows the X-ray diffraction patterns of the YBa 2 Cu 3 O 7 prepared in Comparative Example before and after the water-vapor exposure test. The water-vapor exposure test, namely the test for the durability against water was carried out by exposing the sample to water vapor at 40°C for 50 hours. As the results, in Fig. 5, no change of the X-ray patterns is observed, while, in Fig. 6, the YBa 2 Cu 3 O 7 almost loses the original structure, giving peaks attributed to BaCO 3 , Y 2 O 3 , and CuO. The sample of YBa 2 Cu 3 O 7 came to exhibit no superconductivity. Fig. 7 shows the results of measurement of the electrical resistivity of the material of Example 7 before and after the water-vapor exposure test. This graph shows little change in the superconductivity, which proves the good endurance to water of the material of the present invention. Other typical superconducting oxide materials of Bi-system are known to be more sensitive to water. Table 1 shows the decrease of Tc by the water-vapor exposure test in other Examples, which proves the superior endurance of the material of the present invention. Fig. 8 shows the result of measurement of TG and DTA of the material of Example 7. The amount of the sample used in the measurement was 50.4 mg. From Fig. 8, the loss of the oxygen from the metal oxide material of example 7 at 900°C amounts to 1 % by weight, corresponding to approximately 0.34 oxygen atom in the composition formula. This oxygen loss is about 1/3 as compared with that of the YBa 2 Cu 3 O 7 of Comparative Example which loses oxygen in an amount of 2.4 % by weight corresponding to one oxygen atom. Thus the metal oxide material of the present invention deteriorates less than the ones of Comparative Examples. The same results as in Fig. 5, Fig. 7, and Fig. 8 are obtained in other Examples. Examples 8 to 13 and Comparative Examples 7 to 12 The starting materials used were Y 2 O 3 , Gd 2 O 3 , Er 2 O 3 , Ho 2 O 3 , TiO 2 , Ga 2 O 3 , ReO 3 , SrCO 3 , and CuO. These materials were weighed out in desired composition ratios, arid mixed dry. The respective mixtures were reacted and sintered in the same manner as described above to prepare the compounds of the Examples of the present invention and Comparative Examples. These samples were subjected to measurement of electric resistivity and measurement of magnetic susceptibility. Table 3 shows the compositions and the transition temperature (K) of the compounds of Examples 8 to 13. Table 4 shows the nominal compositions and the electric characteristics of the samples of Comparative Examples 7 to 12. The composition ratios were measured by EPMA, so that the quantity of the oxygen may involve an error of about 20 %. Table 3 shows that the metal oxide materials within the composition ratio range of the present invention all become superconductors having Tc = 20 K or higher. Table 4 shows that the materials of Comparative Examples outside the range of the composition of the present invention do not exhibit superconductivity transition, or come to have zero resistance at a temperature of 10 K or lower if the materials exhibit superconductivity transition. The materials of Comparative Examples have inferior characteristics with the superconductivity volume fraction of not more than 3 %. At the right column of Table 3, the values of decrease of Tc at the water-vapor exposure test conducted in the same manner as in Examples 1 to 7 are shown. It is deduced from these values that the examples have good endurance. Example No. Composition Characteristic (Tc) Decrease of Tc after water-vapor exposure test (ΔTc) 8 YSr 2 Cu 2.92 Re 0.08 O 6.8 40K -3K 9 YSr 2 Cu 2.4 Ga 0.6 O 7.1 25K -3K 10 Gd 0.5 Er 0.5 Sr 2 Cu 2.7 Ti 0.3 O 6.8 27k -2K 11 YSr 2 Cu 2.7 Ga 0.2 Re 0.1 O 7.0 48k -4K 12 Ho 0.9 Sr 1.9 Cu 2.8 Re 0.2 O 7.0 31K -3K 13 Ho 1.1 Sr 2.1 Cu 2.8 Re 0.2 O 7.0 26K -4K Comparative Example No. Nominal composition Characteristic (Tc) 7 YSr 2 Cu 2.97 Re 0.03 O y semi-conductor 8 YSr 2 Cu 2.2 Ga 0.8 O y semi-conductor 9 Y 0.7 Sr 2 Cu 2.6 Ga 0.4 O y 8K 10 Y 1.3 Sr 2 Cu 2.6 Ga 0.4 O y semi-conductor 11 YSr 1.7 Cu 2.6 Ga 0.4 O y 9K 12 YSr 2.3 Cu 2.6 Ga 0.4 O y semi-conductor Example 14 to 21 The starting materials used were Y 2 O 3 , Ho 2 O 3 , Dy 2 O 3 , Gd 2 O 3 , La 2 O 3 , Sm 2 O 3 , Er 2 O 3 , Yb 2 O 3 , Ga 2 O 3 , SrCO 3 , and CuO. These materials were weighed out in desired composition ratios, and mixed at dry. The respective mixtures were reacted and sintered in the same manner as described above to prepare the compounds of the Examples of the present invention and Comparative Examples. The samples were subjected to measurement of electric resistivity and magnetic susceptibility. Table 5 shows the compositions and the electric characteristics of the samples of Examples 14 to 17. Table 6 shows the compositions and the electric characteristics of the samples of Example 18 to 21, and the transition temperatures (K) if the sample is superconducting. The X-ray diffraction patterns of the material of Examples 14 to 17 are nearly the same as that of Fig. 2, showing the similar structures of these material. The superconductivity volume fraction was more than 10 %. The metal oxide materials of Examples 18 to 21 shown in Table 6 are the ones within the present invention. However, these metal oxides, which employ, as Ln, only one element other than Y, Ho, Dy, and Gd, have inferior characteristics. Accordingly, if a lanthanoid element other than Y, Ho, Dy, and Gd is used, it is preferable to use the element in combination with Y or with one or more other lanthanoid elements. When only one lanthanoid element is used, Y, Ho, Dy, or Gd is preferred as the Ln elements. At the right columns of Tables 5 and 6, the values of decrease of Tc at the water-vapor exposure test conducted in the same manner as in Examples 1 to 7 are shown. From the values, the materials of these Examples have a good endurance. Example No. Composition Characteristic (Tc) Decrease of Tc after water-vapor exposure test (ΔTc) 14 YSr 2 Cu 2.6 Ga 0.4 O 7.1 35K -3K 15 HoSr 2 Cu 2.6 Ga 0.4 O 7.1 35K -4K 16 DySr 2 Cu 2.6 Ga 0.4 O 7 31K -2K 17 GdSr 2 Cu 2.6 Ga 0.4 O 7 26K -3K Example No. Composition Characteristic (Tc) Decrease of Tc after water-vapor exposure test (ΔTc) 18 LaSr 2 Cu 2.6 Ga 0.4 O 7.0 20K -4K 19 SmSr 2 Cu 2.6 Ga 0.4 O 7.0 22K -3K 20 ErSr 2 Cu 2.6 Ga 0.4 O 7.0 24K -2K 21 YbSr 2 Cu 2.6 Ga 0.4 O 7.0 20K -3K Examples 22 to 35 and Comparative Examples 13 to 26 The materials shown in Tables 7 and 8 were reacted and sintered in the same manner as describe above to prepare the compounds of Examples of the present invention and Comparative Examples. The X-ray patterns of the materials of Examples 22 to 35 are nearly the same as the one of Fig. 2, showing the similar structures of these materials. The temperature dependence of the magnetic susceptibility of these materials were similar to that of Fig. 4, and the superconductivity volume fractions were more than 10 %, showing superior characteristics. From Tables 7 and 8, satisfactory superconductivity characteristics are obtained with the compound YSr 2 Cu 3-x M x O y within the range of x regarding the element M. M = Ti : 0.2 ≦ x ≦ 0.5 M = V : 0.05 ≦ x ≦ 0.4 M = Ga : 0.25 ≦ x ≦ 0.7 M = Ge : 0.05 ≦ x ≦ 0.4 M = Mo : 0.05 ≦ x ≦ 0.4 M = W : 0.05 ≦ x ≦ 0.4 M = Re : 0.05 ≦ x ≦ 0.4 At the right columns of Table 7, the values of decrease of Tc at the water-vapor exposure test conducted in the same manner as in Examples 1 to 7 are shown. From the values, the materials of the present invention have a good endurance. Example No. Composition Characteristic (Tc) Decrease of Tc after water-vapor exposure test (ΔTc) 22 YSr 2 Cu 2.78 Ti 0.22 O 7.0 26K -3K 23 YSr 2 Cu 2.55 Ti 0.45 O 7.1 31K -2K 24 YSr 2 Cu 2.9 V 0.1 O 7.1 25K - -2K 25 YSr 2 Cu 2.65 V 0.35 O 7.2 26K -3K 26 YSr 2 Cu 2.7 Ga 0.3 O 6.9 31K -4K 27 YSr 2 Cu 2.35 Ga 0.65 O 7.1 27K -3K 28 YSr 2 Cu 2.9 Ge 0.1 O 6.9 31K -3K 29 YSr 2 Cu 2.65 Ge 0.35 O 7 26K -3K 30 YSr 2 Cu 2.9 Mo 0.1 O 6.9 62K -5K 31 YSr 2 Cu 2.65 Mo 0.35 O 7.4 27K -1K 32 YSr 2 Cu 2.9 W 0.1 O 7.1 38K -3K 33 YSr 2 Cu 2.65 W 0.35 O 7.4 25K -2K 34 YSr 2 Cu 2.9 Re 0.1 O 6.9 45K -5K 35 YSr 2 Cu 2.65 Re 0.35 O 7.5 26K -3K Comparative Example No. Nominal composition Characteristic (Tc) 13 YSr 2 Cu 2.85 Ti 0.15 O y 8K 14 YSr 2 Cu 2.4 Ti 0.6 O y semi-conductor 15 YSr 2 Cu 2.97 V 0.03 O y semi-conductor 16 YSr 2 Cu 2.55 V 0.45 O y semi-conductor 17 YSr 2 Cu 2.78 Ga 0.22 O y 9K 18 YSr 2 Cu 2.2 Ga 0.8 O y semi-conductor 19 YSr 2 Cu 2.97 Ga 0.03 O y 9K 20 YSr 2 Cu 2.5 Ge 0.5 O y semi-conductor 21 YSr 2 Cu 2.97 Mo 0.03 O y 9k 22 YSr 2 Cu 2.5 Mo 0.5 O y semi-conductor 23 YSr 2 Cu 2.97 W 0.03 O y 8K 24 YSr 2 Cu 2.5 W 0.5 O y semi-conductor 25 YSr 2 Cu 2.97 Re 0.03 O y 9K 26 YSr 2 Cu 2.5 Re 0.5 O y semi-conductor (1) The metal oxide material of the present invention is synthesizable stably at atmospheric pressure in contrast to conventional superconducting materials that are synthesizable only under a superhigh pressure. (2) The metal oxide material of the present invention is an excellent superconducting material having a superconductivity transition temperature exceeding by far the liquid helium temperature, and having a superconductivity volume fraction of not less than 10 %. Accordingly, the metal oxide material of the present invention is practically usable with a simple refrigeration apparatus. (3) The metal oxide material of the present invention has the lowest specific gravity of known copper oxide materials which are obtained stably, and is particularly effective when used as a bulk material. (4) In the synthesis of the metal oxide material of the present invention, a toxic material such as heavy metal or barium carbonate is not used in contrast to other copper oxide superconductor, and is therefore safe and inexpensive. (5) The metal oxide material of the present invention has a good endurance against moisture and water vapor. Therefore, the metal oxide material is naturally useful under various application conditions and wide application fields, and can effectively be used as a device material. (6) The metal oxide material of the present invention loses oxygen less even at a high temperature. Therefore, less countermeasure is required against the oxygen loss during the production and use of the metal oxide material.

Claims: A metal oxide material represented by the composition formula of Ln a Sr b Cu 3-x M x 0 c , where 2.7 ≦ a + b ≦ 3.3; 0.8 ≦ a ≦ 1.2; 6 ≦ c ≦ 9; and 0.05 ≦ x ≦ 0.7, Ln is at least one element selected from the group of elements of Y and lanthanoids or an atomic group consisting of said elements, and either M = Ti, with 0.2 ≦ x ≦ 0.5, or M = Re with 0.05 ≦ x ≦ 0.4. A metal oxide material according to claim 1, wherein a = 1 and b = 2, and Ln is selected from Y, Ho, Dy and Gd. A metal oxide material according to either preceding claim, which has a tetragonal or orthorhombic structure, and its C-axis length is not less than 1.1 nm (11 Å) and not more than 1.2 nm (12 Å). A metal oxide material according to any preceding claim, which shows superconductivity at a temperature not lower than 20 Kelvin. Use of a material as claimed in any preceding claim as a superconductor in an electronic device. An electronic device including a superconductor of metal oxide material as claimed in any preceding claim 1 to 4.

Inventors: DEN TOHRU, KOBAYASHI TAMAKI, DEN, TOHRU, KOBAYASHI, TAMAKI
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1992
Main classification: C04B35
IPC codes: H01L39, C04B35