Cylinder block

Abstract: A cylinder block (B C ) comprising a cylinder block body (1) and a cylinder liner block (B L ) filled in the cylinder block body (1) in a cast-in manner. The cylinder liner block (B L ) is formed from a material having a rigidity larger than that of the cylinder block body (1), and the cylinder liner block (B L ) comprises a liner section (4) filled in a cylinder barrel portion (1 U ) of the cylinder block body (1) in a cast-in manner, and a reinforcing wall section filled in a bearing wall of a crank case portion (1 L ) of the cylinder block body (1) in a cast-in manner. Thus, it is possible to increase the wear resistance of cylinders in the cylinder block (B L ), as well as to provide an increase in performance by reductions in vibration and noise of the cylinder block (B L ), and to provide reductions in size, weight and cost of the cylinder block (B L ) by a reduction in thickness of the bearing walls (13).

Description: The present invention relates to a cylinder block for an internal combustion engine. A cylinder block for an internal combustion engine is produced by a high-pressure casting process such as a die casting process. In such a case the cylinder block includes a cylinder liner block mounted therein at cylinder barrel portions of a cylinder block body which forms a main portion of the cylinder block. The cylinder liner block comprises cylinder liners connected so as to define cylinders in the cylinder block (see Japanese Utility Model Publication No. 28289/89). The conventional cylinder liner block is formed mainly for the purpose of increasing the wear resistance of the cylinder on which a piston slides, but this cylinder liner block does not contribute to an increase in rigidity of the cylinder block itself and particularly to an increase in rigidity of the bearing wall which supports the crankshaft in a crank case portion of the cylinder block. Such a cylinder liner block is known from EP-A-0 411 785 where is also the fact disclosed to form the cylinder liner block from a material having a rigidity larger than a material forming the cylinder block body to increase the wear resistance of the cylinder liner block. The cylinder block known from EP-A-0 411 785 also defines the preamble parts of claims 1 and 7. From DE-A-37 41 838 it is known to provide a cylinder liner block with cooling ribs extending from the cylinder liner block into a cooling water jacket of an internal combustion engine. These cooling ribs are designed to increase the heat transfer from the combustion chamber of a cylinder to the cooling water provided in the cooling water jacket during operation of the internal combustion engine. The conventional cylinder block body is formed into a complicated shape having cylinder barrel portions including a plurality of cylinders, and a crank case portion provided with a plurality of bearing walls for supporting the crankshaft. Therefore, the cylinder block body has both thin and thick portions and hence, it is difficult to make the solidifying rate uniform over the entire region during solidification of the cylinder block. For example, a base portion of the bearing wall is formed thick and hence, has a volume larger than those of other portions, thereby bringing about casting defects such as sink marks due to shrinkage effects. Thereupon, in order to prevent such casting defects, there is conceived an approach for partially accelerating the solidifying rate by additionally using a chiller metal or other partial chiller means. However, such an approach results in complicated casting equipment and processes, thereby bringing about an increase in cost. Accordingly, it is an object of the present invention to provide a new cylinder block comprising a cylinder block body and a cylinder liner block mounted by casting in the cylinder block body for an internal combustion engine with an increased performance, especially by providing an improved bearing support for the crankshaft, especially with respect to improving the rigidity and the alignment of the bearing support for the crankshaft. According to a first aspect and feature of the present invention, there is provided a cylinder block comprising a cylinder block body and a cylinder liner block mounted in the cylinder block body by casting the cylinder block body with the cylinder liner block positioned in the cylinder block body, said cylinder liner block being formed from a material having a rigidity larger than a material forming the cylinder block body, and said cylinder liner block comprising a liner section mounted by casting in position in a cylinder barrel portion of said cylinder block body, wherein the cylinder liner block further comprises a reinforcing wall section mounted by casting in position in a bearing wall of a crank case portion of said cylinder block body. With the above arrangement, the cylinder liner block can provide not only an increase in the wear resistance of cylinders in the cylinder block, but also a substantial increase in the rigidity of the bearing walls, which contributes to reductions in vibration and noise of the cylinder block and to an increase in performance of the engine. As a result, the conventionally thick portions forming the crank case portion which are integral to the cylinder block body can be reduced in thickness and, thus, allow for a solidification rate which is more uniform over the entire region of the cylinder block body, thereby reducing casting defects and increasing the alignment of the bearing walls supporting the crankshaft. In addition, this arrangement makes it possible to reduce the thickness of the bearing walls of the crank case portion, thereby contributing to reductions in size, weight and cost of the cylinder block. According to a second aspect and feature of the present invention, there is provided a cylinder block comprising a cylinder block body and a cylinder liner block mounted in the cylinder block body by casting the cylinder block body with the cylinder liner block positioned in the cylinder block body, said cylinder liner block defining a plurality of cylinder bores, said cylinder liner block being comprised of cylinder liners arranged in a line, adjacent ones of said cylinder liners being connected in series through a common boundary wall, wherein said boundary wall is integrally provided with a chiller metal portion having at least one chiller fin, said chiller fin extending in a direction substantially perpendicular to said line of cylinder liners, said chiller metal portion and said chiller fin being embedded in the cast material of a thick wall portion of said cylinder block body. In the region of two adjacent cylinders the cylinder block body has relatively thick walls which naturally solidify more slowly than the adjacent region of the cylinder block body. By providing the at least one chiller fin as a heat sink in this region, a solidifying rate which is more uniform over the entire region of the cylinder block body can be achieved. In addition, the portions of the cylinder block body where two cylinders are adjacent to one another are those portions from where the bearing walls supporting the crankshaft extend. Casting defects in these regions would particularly reduce the alignment of the bearing walls supporting the crankshaft. Thus, it is possible to provide a multi-cylinder block having a high accuracy and a high quality at low cost as a whole. The above and other objects, features and advantages of the invention will become apparent from the following description of a preferred embodiment, taken in conjunction with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS Fig.1 is a plan view of a cylinder block according to the present invention; Fig.2 is a sectional view taken along a line 2-2 in Fig.1; Fig.3 is a sectional view taken along a line 3-3 in Fig.1; Fig.4 is a sectional view taken along a line 4-4 in Fig.1; Fig.5 is a front view of a quadruple wet liner block; Fig.6 is a partially cross-sectional plan view taken along a line 6-6 in Fig.5; Fig.7 is a sectional view taken along a line 7-7 in Fig.6; Fig.8 is a sectional view taken along a line 8-8 in Fig.5; Fig.9 is a sectional view taken along a line 9-9 in Fig.5; Fig.10 is a sectional view taken along a line 10-10 in Fig.9; Fig.11 is a partially cross-sectional bottom view taken along a line 11-11 in Fig.5; and Figs.12 to 14 are views illustrating steps for casting a cylinder block in a metal mold. DESCRIPTION OF THE PREFERRED EMBODIMENT The present invention will now be described by way of a preferred embodiment in connection with the accompanying drawings. A cylinder block B C for a serial four-cylinder internal combustion engine is constructed as an open deck type having a quadruple wet cylinder liner block B L . A cylinder block body 1 forming a main portion of the quadruple wet cylinder liner block B L is made by a die-casting of aluminum alloy. The cylinder block body 1 is comprised of an upper portion, i.e., a cylinder barrel portion 1 U and a lower portion, i.e., a crank case portion 1 L . The upper portion 1 U is provided with a quadruple barrel bore 3 opened at a deck surface 2 of the cylinder block body 1. A liner section 4 of the quadruple wet cylinder liner block B L made of cast iron which will be described hereinafter is integrally mounted by casting in the barrel bore 3. The liner portion 4 of the cylinder liner block B L is comprised of first, second, third and fourth wet liners 4 1 , 4 2 , 4 3 and 4 4 connected to one another. A cylinder bore 21, in which a piston (not shown) is slidably received, is made in each of the wet liners 4 1 , 4 2 , 4 3 and 4 4 . A water jacket 5 is defined between an outer wall surface of the quadruple wet cylinder liner block B L and an inner wall surface of the barrel bore 3 and is opened at the deck surface 2. As usual, cooling water is circulated through the water jacket 5. Provided in an outer wall of the cylinder barrel portion 1 U are bolt bores 6 for coupling a cylinder head (not shown) on the deck surface 2, an oil passage 7 through which lubricating oil flows, and the like. The crank case portion 1 L constituting the lower portion of the cylinder block body 1 includes left and right skirt walls 8 and 9 integrally extending from a lower portion of the cylinder barrel portion 1 U , and a plurality of first, second, third, fourth and fifth bearing walls 13 1 , 13 2 , 13 3 , 13 4 and 13 5 provided to extend downwardly from constricted portions 12 between longitudinally opposite end walls 10 and 11 of the cylinder barrel portion 1 U and the first to fourth wet liners 4 1 , 4 2 , 4 3 and 4 4 , so as to integrally connect the left and right skirt walls 8 and 9 with each other. First, second, third, fourth and fifth reinforcing walls 27 1 , 27 2 , 27 3 , 27 4 and 27 5 (which will be described hereinafter) of the crank case portion 1 L of the cylinder liner block B L are mounted by casting in the bearing walls 13 1 , 13 2 , 13 3 , 13 4 and 13 5 , respectively, and provided with a semi-circular bearing bore 14 for supporting a crankshaft S C of the engine, a pair of bolt bores 15 for mounting a bearing cap (not shown) on a lower surface thereof, and the like. The structure of the quadruple wet cylinder liner block B L of the cast iron which is integrally mounted by casting in the cylinder block of the aluminum alloy during the production of the cylinder block B C , in the die casting process will be described in detail with reference to Figs.5 to 11. The quadruple wet cylinder liner block B L includes a liner section 4 and a reinforcing wall section 27. The liner section 4 is comprised of the first, second, third and fourth cylindrical wet liners 4 1 , 4 2 , 4 3 and 4 4 connected to one another, with the adjacent wet liners being connected through a common boundary wall 20 and therefore, they are formed into a so-called siamese type. The cylinder bore 21, in which the piston (not shown) is slidably received, is made in each of the wet liners 4 1 , 4 2 , 4 3 and 4 4 . As best shown in Figs.5, 8 and 9, a seal flange 22 is integrally formed on an outer periphery of a lower portion of the liner section 4 to extend over the entire periphery substantially horizontally in a direction substantially perpendicular to a cylinder axis 1-1, and an upper surface of the seal flange 22 is formed into a flat sealing surface 22 1 . Longitudinal and transverse ribs 23 and 24 form a rib structure serving as a spacer and also serving as a reinforcing member are integrally provided around an outer periphery of the liner section 4 above the seal flange 22. Each of these ribs 23 and 24 is formed at a height above that of the seal flange 22. A plurality of reinforcing small ribs 30 are integrally provided on the liner section 4 at a location above, the seal flange 22 to project therefrom substantially in parallel to the seal flange 22. The reinforcing wall section 27 of the crank case portion 1 L of the cylinder liner block B L is comprised of the first to fifth reinforcing walls 27 1 to 27 5 integrally juxtaposed to extend in parallel to one another from lower portions of the boundary walls 20 provided between the longitudinally opposite end walls 25 and 26 and the first to fourth four cylindrical wet liners 4 1 to 4 5 of the liner section 4. These reinforcing walls 27 1 to 27 5 are integrally mounted by casting in the first to fifth bearing walls 13 1 to 13 5 , respectively. Each of the reinforcing walls 271 to 275 is provided at its lower surface with a bonding surface 31, the bearing bore 14 and the bolt bores 15 for bonding a bearing cap (not shown). As shown in Fig.10, the boundary walls 20 of the liner section 4 and the first to fifth reinforcing walls 27 1 to 27 5 are integrally interconnected by connecting walls 28, respectively. The connecting wall 28 is made thick in a widthwise direction so as to insure a relative large volume. A plurality of relatively long heating-absorbing fins 29 are projectingly provided on an outer periphery of the connecting wall 28. The connecting wall 28 of the large volume serves as a chiller metal to improve a cooling rate in solidification of the molten aluminum alloy during the die casting production of the cylinder block B C of the aluminum alloy. A metal mold for producing the cylinder block B C in the die-casting process and steps for casting the same are shown in Figs.12 to 14. Referring to these Figures, the metal mold M is comprised of a stationary die 40, top and bottom movable dies 41 and 42 capable of moving vertically toward and away from each other, and a side movable die 43 capable of moving laterally relative to the stationary die 40. The stationary die 40 is provided with a shaping surface 40 1 formed into a convex shape. The top and bottom movable dies 41 and 42 have shaping surfaces 41 1 and 41 2 formed thereon in an opposed relation to each other. The side movable die 43 has a shaping surface 43 1 formed in an opposed relation to the shaping surface 40 1 of the stationary die 40. The shaping surface 43 1 has cylindrical bore pins 44 dependingly provided thereon in a longitudinal arrangement for shaping the cylinder bores 21. A hollow cylindrical jacket pin 45 is integrally provided in a depending manner to surround each of the bore pins 44 with an annular clearance 46 left therebetween and extends to the halfway of the bore pin 44. As shown in Figs.12 and 13, the cylinder bore 21 in the cylinder liner block B L is fitted over each of the bore pin 44 from the left. And the wet liner section having the longitudinal and transverse ribs 23 and 24 projecting therefrom is fitted in the jacket pin 45. A free end of the jacket pin 45 is mated with the sealing surface 22 1 of the seal flange 22. A mating surface of the jacket pin 45 is formed into a flat sealing surface so that the molten metal does not flow in nor out between the mating sealing surfaces during the die casting. A small gap (in a range of 0.2 to 0.3 mm) is provided between the bore pin 44 and the wet liner section 4, Outer surfaces of the longitudinal and transverse ribs 23 and 24 of the wet liner section 4 are confronted or mated with the inner peripheral surface of the jacket pin 45 with a small gap (in a range of 0.2 to 0.3 mm) left therebetween. A void 48 is defined between the outer surface of the liner section 4 and the inner peripheral surface of the jacket pin 45, so that the molten aluminum alloy is prevented from flowing into the void 48 by the longitudinal and transverse ribs 23 and 24. After the first to fourth wet liners 4 1 to 4 4 of the liner section 4 are fitted into the bore pin 44 as described above, the top and bottom movable dies 41 and 42 are moved in a closing direction. Then, by moving the side movable die 43 in a closing direction, the metal mold M is closed as shown in Fig.13. Thus, a cavity 49 is defined by the shaping surface of the metal mold M and the cylinder liner block B L . The molten aluminum alloy is poured under a predetermined pressure into the cavity 49 through a gate 50. If this molten alloy is cooled, the cylinder block B C , is formed with the cylinder liner block B L integrally mounted by casting in an aluminum alloy matrix In pouring the molten alloy into the cavity 49 in the above-described casting process, the molten alloy cannot penetrate between the sealing surface 22 1 of the seal flange 22 and the free end of the jacket pin 45, because Jacket pin 45 is mated to the sealing surface 22 1 . Therefore, the void 48 with no molten alloy flowing thereinto is maintained between the jacket pin 45 and the first to fourth wet liners 4 1 to 4 4 . After releasing of the metal mold M, this void 48 forms a portion of the water jacket 5. An edgewise pressure is applied to the outer peripheral surface of the jacket pin 45, as shown by an arrow a in Fig.13, by the pressurized pouring of the molten alloy into the cavity 49, but is transmitted through the liner section 4 to the bore pin 44 having a large rigidity, thereby preventing the jacket pin 45 and the wet liner section 4 from being deformed. The first to fifth reinforcing walls 27 1 to 27 5 of the reinforcing wall section 27 which is the lower portion of the cylinder liner block B L are mounted by casting in the first to fifth bearing walls 13 1 to 13 5 of the crank case portion 1 of the cylinder block body 1. After cooling of the molten metal, the metal mold M is released, as shown in Fig.14, and the cylinder block B C completely molded is removed from the metal mold M. Thus, the water jacket 5 opened at the deck surface 2 is formed by the jacket pin 45 and the void. In the wet cylinder liner block B L of the iron mounted by casting in the cylinder block body 1 of aluminum alloy, it is possible to improve the intrinsic function of the wet liner, i.e., the wear resistance of the cylinder bore on which the piston slides, as well as to substantially increase the rigidity of the cylinder block B C itself and particularly the bearing wall 13 of the crank case portion 1 L thereof and to reduce the vibration and noise of the cylinder block. It is also possible to reduce the thickness of the bearing wall, which contributes to reductions in size, weight and cost of the cylinder block B C . In addition, it is possible to reduce the phenomenon of wrapping of the crankshaft S C due to the thermal shrinkage of the cylinder block of the aluminum alloy having a high coefficient of thermal expansion, when the cylinder block B C is it a low temperature, such as at the start of the engine. This contributes to a reduction in the resistance to the rotation of the crankshaft S C , thereby substantially enhancing the performance of the engine in cooperation with the increase in rigidity of the bearing wall. In the cylinder block B C cast in the above-described manner, the connecting portion between the bearing wall 13 and the boundary wall 20 between the adjacent cylinder bores 21 is made larger in both volume and thickness than those of the other portions of the cylinder block B C . However, the chiller metal 28 of the wet multiple cylinder liner 4 having the chiller fins 29 is mounted by casting into this connecting portion, as shown in Fig.4, and therefore, the chiller metal 28 effects its function during the casting, thereby accelerating the solidification of the aluminum alloy matrix therearound. Therefore, it is possible to substantially equalize the solidifying rate for the thick connecting portion to the solidifying rate for the other thinner portions, so that casting defects such as sink marks cannot be brought about. Moreover, it is possible to increase the anchoring effect between the chiller metal 28 having the chiller fins 29 and the aluminum alloy of the cylinder block B C . In the above embodiment, the cylinder block has been described as being made of aluminum alloy, and the cylinder liner block as being made of cast iron. Alternatively, the cylinder block and the cylinder liner block may be formed by combination of other materials and in this case, the rigidity of the material for the cylinder liner block should be larger than that of the cylinder block. In addition, although the cylinder liner block according to the present invention has been applied to the four-cylinder block in the above embodiment, it is a matter of course that the cylinder liner block according to the present invention can be applied to another multi-cylinder or single-cylinder block. Further, although the cylinder liner block according to the present invention has been constructed as the quadruple wet type, it is a matter of course that the cylinder liner block can be constructed as a multiple or single dry type.

Claims: A cylinder block comprising a cylinder block body (1) and a cylinder liner block (B L ) mounted in the cylinder block body (1) by casting the cylinder block body (1) with the cylinder liner block (B L ) positioned in the cylinder block body (1), said cylinder liner block (B L ) being formed from a material having a rigidity larger than a material forming the cylinder block body (1), and said cylinder liner block (B L ) comprising a liner section (4) mounted by casting in position in a cylinder barrel portion (1 U ) of said cylinder block body (1), characterized in that the cylinder liner block (B L ) further comprises a reinforcing wall section (27) mounted by casting in position in a bearing wall (13 1 -13 5 ) of a crank case portion (1 L ) of said cylinder block body (1). A cylinder block according to claim 1, wherein in said cylinder block body (1) is made of light alloy, and said cylinder liner block (B L ) is made of iron. A cylinder block according to claim 1, wherein said cylinder liner block (B L ) is made of cast iron. A cylinder block according to claim 1, wherein said cylinder liner block (B L ) includes a plurality of cylinder liners (4 1 -4 4 ) in said liner section (4), adjacent cylinder liners (4 1 -4 4 ) being connected in series through a series of common boundary walls (20), and said reinforcing wall section (27) includes a reinforcing wall (27 1 -27 5 ) extending downwardly from each said common boundary wall (20) for supporting a crank shaft (S C ). A cylinder block according to claim 1, wherein said cylinder liner block (B L ) has an open deck surface (2) and at least one cylinder liner (4 1 -4 4 ) extending downwardly from said open deck surface (2), each said cylinder liner (4 1 -4 4 ) having a seal flange (22) projecting outwardly around an outer periphery of a lower portion of said cylinder liner (4 1 -4 4 ) for forming a lower end of a cooling water space (5) between the cylinder liner (4 1 -4 4 ) and the cylinder block body (1). A cylinder block according to claim 5, wherein each said cylinder liner (4 1 -4 4 ) is provided with a rib structure (23, 24) projecting outwardly on said outer periphery between said open deck surface (2) and said seal flange (22), said rib structure (23, 24) projecting outwardly less than said seal flange (22). A cylinder block comprising a cylinder block body (1) and a cylinder liner block (B L ) mounted in the cylinder block body (1) by casting the cylinder block body (1) with the cylinder liner block (B L ) positioned in the cylinder block body (1), said cylinder liner block (B L ) defining a plurality of cylinder bores (21), said cylinder liner block (B L ) being comprised of cylinder liners (4 1 -4 4 ) arranged in a line, adjacent ones of said cylinder liners (4 1 -4 4 ) being connected in series through a common boundary wall (20), characterized in that said boundary wall (20) is integrally provided with a chiller metal portion (28) having at least one chiller fin (29), said chiller fin (29) extending in a direction substantially perpendicular to said line of cylinder liners (4 1 -4 4 ), said chiller metal portion (28) and said chiller fin (29) being embedded in the cast material of a thick wall portion of said cylinder block body (1). A cylinder block according to claim 7, wherein said cylinder liner block (B L ) is formed from a material having a rigidity larger than a material forming the cylinder block body (1). A cylinder block according to claim 7, wherein said cylinder liner block (B L ) has a reinforcing wall section (27) mounted by casting in portion in a bearing wall (13 1 -13 5 ) of a crank case portion (1 L ) of said cylinder block body (1) for said reinforcing wall section (27) to support a crank shaft (S C ). A cylinder block according to claim 7, wherein said cylinder block body (1) is made of light alloy, and said cylinder liner block (B L ) is made of iron. A cylinder block according to claim 7, wherein said cylinder liner block (B L ) is made of cast iron.

Inventors: GOTO TOMOYUKI, HATA TSUNEHISA, KATOH HISASHI, KODA SHINSUKE, MIYANO HIDEYO, NAKAJIMA TADAYOSHI, GOTO, TOMOYUKI, HATA, TSUNEHISA, KATOH, HISASHI, KODA, SHINSUKE, MIYANO, HIDEYO, NAKAJIMA, TADAYOSHI, GOTO, TOMOYUKI, HONDA GIKEN KOGYO K.K., Hata, Tsunehisa, c/o K.K. Honda Gijutsu Kenkyusho, Katoh, Hisashi, c/o K.K. Honda Gijutsu Kenkyusho, Miyano, Hideyo, c/o K.K. Honda Gijutsu Kenkyusho, NAKAJIMA, TADAYOSHI, HONDA GIKEN KOGYO K.K.
Applicants: HONDA MOTOR CO LTD, HONDA GIKEN KOGYO KABUSHIKI KAISHA
Application year: 1992
Main classification: F02F1
IPC codes: F02F7, F02F1, F02B75, B22D19