Method for producing an anode material and a non-aqueous electrolyte cell employing such anode material

Abstract: A negative electrode material which has as a main component hardly graphitized carbon containing carbon, phosphorus and oxygen as main components, or coke (easily graphitized carbon), and includes 0.2-9.0 weight % phosphorus. The negative electrode material has peaks at ± 100 ppm relative to orthophosphoric acid as the reference in the ³¹P nuclear solid NMR spectrum, and has a peak of 135.0 eV in the 2p orbital spectrum of phosphorus atom in the XPS. The negative electrode material is manufactured by adding phosphoric acid, phsphorus oxide, etc., to an organic material or a carbon material, and by burning the mixture. A nonaqueous electrolyte battery is made from the negative electrode material, a positive electrode including Li, and an electrolyte.

Description: SPECIFICATION Method for Producing an Anode Matinal and a Non-Aqueous Electrolyte Cell Employing Such Anode Material TECHNICAL FIELD This invention relates to a method for producing an anode material and to a non-aqueous electrolyte cell having such material as an anode. BACKGROUND ART The electrical capacity of a carbonaceous material per unit weight is governed by lithium dosage and hence it is desirable that lithium dosage of the carbonaceous material be as large as possible in order to increase the charging/discharging capacity of the cell. (Theoretically, one Li atom per six carbon atoms represents an upper limit.) Up to now, a carbonaceous material obtained by carbonizing an organic material, as described in JP Patent KOKAI Publication No.62-122066 (1986) or JP Patent KOKAI Publication No.62-90863 (1987), has been known as the carbonaceous material employed for the anode for this type of the cell. However, with the above described carbonaceous material, lithium dosage is insufficient and is of the order of about one half of the theoretical value. The EP-A-0 418 514, which is prior art according to Art. 54(3) EPC, discloses a carbonaceous material and a non-aqueous electrochemical cell using the same. The carbonaceous material is obtained by carbonizing starting organic materials, for which examples are presented in the description. The present invention has been proposed for further improving the carbonaceous material. It is an object of the present invention to provide a method for producing an anode material having lithium dosage far exceeding that of the conventional carbonaceous material. It is another object of the present invention to provide a non-aqueous electrolyte cell having a large discharge capacity and superior in cycle life. DISCLOSURE OF THE INVENTION As a result of our eager searches towards achieving the above objects, the present inventors have found that specific compounds containing carbon, phosphorus and oxygen exhibit desirable characteristics as an anode material. Our structural analyses by 31 P solid NMR and XPS (X-ray photoelectron spectroscopy) have revealed that the added phosphorus atoms do not exist as atoms alone or as compounds, such as oxides, alone, but are reacted with oxygen in the course of sintering to generate a compound having carbon-phosphorus or carbon-oxygen-phosphorus bonds. This means that the effect of addition of the phosphorus compounds, producing an increase in lithium dosage, is not displayed simply as lithium doping and undoping with respect to the carbonaceous material, but is displayed by using a special compound mainly consisting of carbon, oxygen and phosphorus, referred to hereinafter as a C-P-O compound. The anode material as produced according to the present invention has been completed on the basis of the above information. The method for producing an anode material according to the present invention comprises the features of the appended claim 1. The method for producing a non-aqueous liquid electrolyte cell according to the present invention is comprises the features of the appended claim 2. By adding a phosphorus compound to the organic material or carbonic material and sintering the resulting mixture in an inert atmosphere, a compound consisting essentially of C, P and Q and having a P-C linkage or a C-O-P linkage is prepared. The compound exhibiting a peak in a 31 P solid NMR spectrum in a range of ±100 ppm based on orthophosphoric acid and a peak in a 2p orbital spectrum of a phosphorus atom of not more than 135 eV in X-ray photoelectron spectroscopy for a carbon-carbon linkage energy in the 1s orbital spectrum of a carbon atom of 284.6 eV has lithium dosage larger than that in a conventional carbonaceous material. By using the material as an anode material, a non-aqueous liquid electrolyte cell having a large charging/discharging capacity may be prepared. By providing a compound containing a phosphorus compound and thus consisting essentially of C, P and O and having a C-P or C-O-P linkage, an anode material may be provided which has a larger lithtum doping quantity(lithium dosage). That is, the anode material as produced according to the present invention is a special compound which, while having an internal composition of (C 6 H 5 O) 2 P(=OH), has a superficial structure of (C 6 H 5 O) 2 P(=O)(OH) and reduced (C 6 H 5 O) 2 P(=O)(OH), (C 6 H 5 O) 3 P(=O) and (C 6 H 5 O) 3 P. It is this special structure that displays the specific effect of increasing the lithium doping quantity. The anode material having superior characteristics may be produced by a simplified operation, and the anode material suitable for a lithium secondary cell may be produced without increasing manufacture costs or lowering the productive efficiency. Besides, with the non-aqueous liquid electrolyte cell as produced according to the present invention, making use of the anode material having the larger lithium doping quantity, a charging/discharging capacity even in excess of a theoretical value possible with the use of the graphite anode may be realized, while the cell exhibits superior cyclic characteristics. The present material renders it possible to produce a non-aqueous liquid electrolyte cell having a larger charging/discharging capacity. BRIEF DESCRIPTION OF THE DRAWINGS Fig.1 is a graph showing charge and discharge curves of Example A and Fig.2 is a graph showing charge and discharge curves of Comparative Example A. Fig.3 is a graph showing cyclic characteristics of cells employing Example A and comparative Example A. BEST MODE FOR CARRYING OUT THE INVENTION The anode material is obtained by adding a phosphorus compound to an organic material or a carbonic material and sintering the resulting mass in an inert atmosphere. An organic material or a carbonic material which is turned into coke on heat treatment at 700°C or lower followed by sintering is employed as a starting material according to the inventive method. By the "coke" is meant a carbonic material which is graphitized on heat treatment at about 3000°C, that is, easily graphitizable carbon. This material is more favorable than the above-mentioned difficultly graphitizable carbon with respect to packing density. That is, in a common tubular cell produced by spirally winding an electrode, it is necessary to increase the electrode area for high efficiency charging and discharging, while more active material needs to be packed into the electrode. However, the carbonic material has a low true density as compared to the active material of the oxide type material. Therefore, if it is possible with a carbonic material with a higher true density, such as coke (having the true density of the order of 2.0 g/cm 3 ) to increase the capacity by the effect of P addition, a higher capacity may be expected to be achieved than if the difficultly graphatizable carbon added with P is employed. For producing the carbonaceous material using the starting organic material as defined in claim 1, the starting material is carbonized at 300° to 700°C in a nitrogen atmosphere, and the carbonized material is sintered in a nitrogen atmosphere under the conditions of the temperature rise rate of 1 to 20°C per minute, the ultimate temperature of 900 to 1500°C and the holding time at the ultimate temperature of 0 to 5 hours. Of course, the carbonization step may be omitted if so desired. According to the present invention, before sintering the starting organic material, or after carbonization of the starting organic material to some extent, a phosphorus compound(s) is added thereto and the resulting mass is sintered to produce a compound which is composed mainly of carbon, phosphorus and oxygen and which has an increased lithium doping quantity. The phosphorus compounds may include oxides such as phosphorus pentaoxide, oxoacids such as orthophosphoric acid, and salts thereof. Phosphoric compounds and phosphoric acid are preferred in view of ease in handling. Above all, if a starting material is employed which is turned into coke (easily graphitizable carbon) after sintering, oxides of phosphorus, such as phosphorus pentaoxide, are preferred. In producing the anode material phosphorus compounds are added to a starting material for a C-P-O material, that is the organic material or the carbonic material, in a quantity of 0.2 to 32 wt%, preferably n a quantity of 1.0 to 15 wt% in terms of phosphorus, whereas the ratio of phosphorus remaining in the produced C-P-O compound is 0.2 to 9.0 wt%, preferably 0.3 to 5.0 wt%. If the quantity of addition of the phosphorus compound(s) is less than the above-mentioned range, such that the ratio of phosphorus in the C-P-O compound is low, the effect of increasing the lithium dosage can be expected only to a limited extent. Conversely, if the quantity of the phosphorus compound(s) is excessive, element phosphorus tends to be increased in quantity to decrease the ratio of the C-P-O compound effectively taking part in lithium doping to lower the characteristics of the anode material. As the starting material is to be turned into coke (easily graphitizable carbon) after sintering, the upper limit temperature of addition of the phosphorus compound is 700°C. If the phosphorus compound is added at a higher temperature, phosphorus may be taken up to some extent, however, the effect on lithium doping and undoping is nil. This indicates that the site of C-P-O linkage in the bulk material which would be produced by the reaction between the-starting material and the phosphorus compound is likely to participate in lithium doping and undoping. The C-P-O compound obtained after sintering is pulverized and classified so as to be used as an anode material. The pulverization process may be carried out before or after sintering or during the temperature raising process. If the above-mentioned C-P-O compound is to be used as an anode of the non-aqueous electrolyte cell, the cathode preferably has increased content of Li. Thus the cathode material is preferably a composite metal oxide having the general formula LiMO 2 , M being at least one of Co and Ni, or an Li-containing inter-layer compound. The most preferred cathode material is LiCoO 2 . The non-aqueous electrolyte cell is intended for achieving a high capacity. It is necessary for the cathode to contain an amount of Li corresponding to a charging and discharging capacity of 250 mAH or higher per gram of the C-P-O compound of the anode in a steady state (that is after five times of the charging and discharging operations). Thus it is preferred for the cathode material to contain an amount of Li corresponding to the charging and discharging capacity of 250 mAH per gram of the C-P-O compound for the anode, while it is more preferred for the cathode material to contain an amount of Li corresponding to the charging and discharging capacity of 300 mAH per gram of the C-P-O compound for the anode. It is not absolutely necessary for Li to be supplied in its entirety from the cathode material, since it suffices that an amount of Li corresponding to the charging and discharging capacity of 250 mAH per gram of the C-P-O compound be present in the cell system. The amount of Li is determined by measuring the discharging capacity of the cell. The non-aqueous electrolyte solution may be adjusted by suitably combining the organic solvent and the electrolyte. Any of the organic solvents and the electrolytes which may be employed in this type of the cell may be employed. Examples of the organic solvents include propylene carbonate, ethylene carbonate, diethyl carbonate, dimethyl carbonate, methyl ethyl carbonate, 1,2-dimethoxyethane, 1,2-diethoxyethane, γ-butyrolactone, tetrahydrofuran, 2-methyltetrahydrofuran, 1,3-dioxolane, 4 methyl, 3 dioxofuran, diethylether, sulforane, methylsulfolane, acetonitrile, propionitrile, anisole, acetate, butyrate or propionate. Examples of the electrolytes include LiClO 4 , LiAsF 6 , LiPF 6 , LiBF 4 , LiB(C 6 H 5 ) 4 , CH 3 SO 3 Li, CF 3 SO 3 Li, LiCl and LiBr. The present invention is hereinafter explained by referring to Examples. It should however be noted that the present invention is not limited to these merely illustrative Examples. First, the methods for measuring the capacity of the anode, 31 P solid NMR spectrum and the X-ray photoelectron spectroscopic spectrum, are explained. Method for Measuring the Capacity The C-P-O material obtained after sintering is pulverized in a mortar and screened to a particle size of not more than 38 µm. Evaluation was made by a test cell. In preparing the test cell, the sorted powders prior to preparation into an anode mix were subjected to a preceding heat treatment in an Ar atmosphere under conditions of the temperature raising rate of about 30°C per minute, an ultimate temperature of 600°C and the holding time at the ultimate temperature of one hour. The anode mix was prepared by adding 10 wt% of polyvinylidene fluoride as a binder and adding dimethylformamide as a solvent, followed by drying. 37 g of the mix were molded into a pellet of 15.5 mm in diameter, along with an Ni mesh as a current collector, to produce an operating electrode. The test cell was constructed in the following manner. Cell Construction coin-type cell (20 mm in diameter, 2.5 mm in thickness) counter-electrode Li metal separator polypropylene porous film electrolyte solution a mixed solvent of propylene carbonate and 1,2-dimethoxyethane (volume ratio of 1:1) to which LiClO 4 is dissolved at a ratio of 1 mol/l current collector copper foil The capacity of the above-described test cell per 1 g of the C-P-O compound was measured. Meanwhile, lithium doping of the operating electrode (charging) was carried out in such a manner that the sequence of operations of charging for one hour followed by a pause of two hours was repeated at the current density of 0.53 mA/cm 2 until the equilibrium potential of 3 mV (Li/Li + ) at a standstill was reached. It is noted that, strictly speaking, the doping process of the C-P-O compound in this testing method is not charging but discharging, however, the present doping process is termed charging and the undoping process is termed discharging, in order to take account of the actual state of the cells. The discharging process (undoping process) was carried out by repeating the sequence of operations of discharging for one hour at a current density of 0.53 mA/cm 2 followed by a pause of two hours, with the terminal voltage of 1.5 V as a cutoff voltage. It has been found that the discharged quantity of electricity is less in any material than the charged quantity of electricity. The non-discharged quantity of electricity is termed a capacity loss for convenience sake. In actual cells, the value of the capacity losses is important in evaluating the anode material. <Method for Measuring 31 P solid High resolution NMR> The powdered sample was mixed with KCl, each in an equal amount. The resulting mixture was charged in a sample tube which was then sealed tightly. Measurements were conducted under the following conditions. <Conditions for Measuring 31 P solid High resolution NMR> apparatus JEOL GSX 270 (solid probe : GSH 27T6) Measurement Nucleus 31 P Measurement Frequency 109.25 MHz Measurement Mode MASGHD Control Material diammonium hydrogen phosphate (1.6ppm) R.P.M. of Sample Tube about 5000 Hz Measurement Temperature room temperature Diluent KCl (two to threefold) <XPS (X-ray Photoelectron Spectroscopy> Using a powdered sample, the spectrum of the P atom on the 2p orbital was measured under the following conditions. <Measurement Conditions for XPS (X-ray Photoelectron Spectroscopy> Apparatus SSI M-PROBE Degree of Vacuum During Measurement After evacuation at 1×10 -9 torr, an argon gas was introduced and measurement was conducted at 2 × 10 -7 torr Neutralizing Electron 2.0 eV Pass Energy 50 eV Photoelectron Taking Angle 35° Charging Homogenization Ni mesh Reference Carbon - Carbon Linkage 284.6 eV Curve Fitting Gaussian 80% + Lorentzian 20% <Control Compound> Since the presence of alkyl chains can hardly be presumed in a carbonic material heat-treated at elevated temperatures, it is more reasonable that the terminal end linked to phosphorus be a benzene ring. The chemical shift of NMR and the binding energy of XPS were compared with the measured values of the aromatic phosphorus compounds to identify the state of presence of phosphorus. Meanwhile, it was confirmed that the above-mentioned aromatic phosphorus compounds could be used as reference compounds from the fact that increase in the number of benzene rings linked to the phosphorus compounds was not effective, as was confirmed by simulation by calculation of molecular orbital. The chemical shift values in the 31 P solid NMR spectrum of each of the phosphorus compounds and the binding energy in the XPS-P (2p) spectrum are shown in Table 1. P compounds chemical shift values(ppm) binding energy(eV) (C 6 H 5 ) 3 P=O 71.7 132.0 (C 6 H 5 ) 2 P(=O)(OH) 28.9 132.8 (C 6 H 5 )P(=O)(OH) 2 21.8 ― (C 6 H 5 )P(=O)(OH)H 19.8 ― (C 6 H 5 ) 3 P -8.2 130.5 (C 6 H 5 O) 2 P(=O)(OH) -12.7 134.3 (C 6 H 5 O) 3 P=O -16.8 133.8 H 3 PO 4 0 134.7 P (element) ― 129.6 An experiment was conducted using petroleum coke as the carbonic material. That is, petroleum coke is pulverized to a mesh size of 200 mesh or less, and 1 g of P 2 O 5 was added to 10 g of the petroleum coke powders. The resulting mixture was heat-treated by maintaining the temperature at 430°C for one hour and then raising the temperature to 1100°C to produce a solid precursor, which was further powdered and, after raising the temperature to 530°C, was heat-treated for one hour and cooled to a powdered sample (Example A). The P content, capacity ahd the capacity loss were measured of the produced sample. A powdered sample (Comparative Example A) was prepared by heat treatment in the same manner as in Example A except not adding P 2 O 5 to the petroleum coke. The P content, capacity and the capacity loss were measured of the produced sample. The results are collectively shown in Table 2. The charge and discharge curves during capacity measurement in Example A and Comparative Example A are shown in Figs.1 and 2, respectively. In the drawing, solid lines indicate closed-circuit voltage in the current-on state, while circle and triangle marks indicate the equilibrium potential after the end of the test. P content(wt%) capacity(mAh/g) capacity loss(mAh/g) comp.Ex.A ― 286 125 Ex.A 1.0 319 100 Using powdered samples of Example and Comparative Example A, a cell was prepared and put to a cyclic test. The cell was obtained by preparing a molded electrode in the same manner as with the capacity testing method, using powders of the C-O-P compound as an active material, and using it as an anode. For preparing a cathode, 6 g of graphite powders and 3 g of polytetrafluoroethylene were added to 91 g of LiCoO 2 , used as an active material, and the resulting mass was mixed thoroughly, 1g of the resulting mixture was charged into a mold and compression molded at a pressure of 2t/cm 2 to produce a disc-shaped electrode. The charging/discharging cyclic test was carried out under the conditions that charging was made at 320 mAh per gram of the active material for the anode and discharging was made to a cutoff of 2.5 V. The results are shown in Fig.3, from which it is seen that the P-containing sample exhibit superior cyclic characteristics. The following are the results of analyses of the state of presence of P in the sample of Example A by 31 P solid high resolution NMR and XPS measurement. Chemical Shift of Peak in 31 P Solid NMR spectrum -11 ppm Surface composition of P by XPS (ratios) (C 6 H 5 O) 2 (P=O)(OH) 12.9% (C 6 H 5 ) 2 (P=O)(OH) 15.5% (C 6 H 5 ) 3 P = O 23.0% (C 6 H 5 ) 3 P 22.3% P 7.5% P having an electron-rich bond 18.7%

Claims: A method for producing an anode material comprising adding a phosphorus compound, in an amount of 0.2 to 32 wt% in terms of phosphorus, to an organic material or a carbonic material heattreated to a temperature of 700°C or less and sintered to a coke to produce a mixture, and sintering the mixture in an inert atmosphere, said organic or carbonic material excluding conjugated resins such as phenolic resins, acrylic resins, halogenated vinyl resins, polyamide-imide resins, polyamide resins, polyacetylene, poly(p-phenylene), cellulose resins; condensed polycyclic hydrocarbon compounds such as naphtalene, phenantrene, anthracene, triphenylene, pyrene, chrysene, naphtacene, picene, perylene, pentaphene, pentacene, etc. and derivatives thereof, various pitches mainly composed of mixtures of the above compounds, and condensed heterocyclic compounds such as indole, iso-indole, quinoline, iso-quinoline, quinoxaline, phthalazine, carbazole, acridine, phenazine, phenantrizine, and derivatives thereof; furan resins such as homopolymers and copolymers of furfuryl alcohol and furfural, specifically polymers of furfural + phenol, furfuryl alcohol + dimethylolurea, furfuryl alcohol, furfuryl alcohol + formaldehyd, furfural + ketones. A method of producing a non-aqueous liquid electrolyte cell comprising forming an anode mainly by producing an anode material according to the steps of claim 1, forming a cathode containing Li, and adding a non-aqueous liquid electrolyte.

Inventors: AZUMA HIDEO, NISHI YOSHIO, OMARU ATSUO, AZUMA, HIDEO, NISHI, YOSHIO, OMARU, ATSUO, OMARU, ATSUO, KORIYAMA PLANT SONY ENERGY TEC INC.
Applicants: SONY CORP, SONY CORPORATION
Application year: 1992
Main classification: H01M4
IPC codes: H01M4