Method for preparing a superconducting thin film of compound oxide

Abstract: Improvement in a method for preparing a superconducting thin film of compound oxide on a substrate (6) by laser evaporation technique. A rear surface of a target (7)used is cooled forcedly by a cooling system (9) during film formation.

Description: Background of the Invention Field of the invention The present invention relates to an improvement in a method for preparing a superconducting thin film of compound oxide having a smooth surface by laser evaporation technique. Description of the related art Superconductivity have been thought, for a long time, to be a phenomenon observable at ultra-low temperatures realized with liquid helium as a cryogen. However, the possibility of an existence of a new type of superconducting material was revealed by Bednorz and Muller, who discovered (La, Sr) 2 CuO 4 which exhibit the superconductivity at 30 K in 1986. C. W. Chu et al. discovered, in the United States of America, another superconducting material of YBa 2 Cu 3 O 7-δ having the critical temperature of about 90 K in 1987. Maeda et al discovered so-called bismuth type superconducting material. And hence, the possibility of an actual utilization of high-Tc superconductors have burst onto the scene because the superconductivity can be realized with cheap cryogen of liquid nitrogen. The new type superconducting materials were obtained in a form of sintered mass prepared by powder metallurgy but now they can be prepared in a thin film form of very high quality. Laser evaporation technique is one of the most promising techniques. In fact, superconducting thin films which exhibit improved superconducting properties can be prepared by the laser evaporation technique with no after-treatment such as annealing of thin films deposited on a substrate see for example EP-A-0 265 886. It is true that a superconducting thin film of the oxide of high quality can be prepared by the laser evaporation technique but the laser evaporation technique have such a disadvantage that undesirable fine particles of oxide are produced on a surface the thin film obtained. Existence of such fine particles is undesirable for fabricating superconducting devices in which smooth ness of the superconducting thin film is requested. Therefore, an object of the present invention is to solve the problem and to provide a novel process for preparing a superconducting thin film of oxide possessing an improved surface property by the laser evaporation technique. Summary of the Invention The present invention provides a process of preparing a superconducting thin film of compound oxide as claimed in claim 1. The present inventors examined the power level of a laser beam impinging onto a target during the laser evaporation and found such a fact the power level fluctuates or varies in time. On the other hand, a laser beam has a power distribution having an intense peak at the center of a spot of the laser beam on a surface of a target. From these facts, a complete plume can not be created at a zone that is not given with enough power of laser. Target material scattered or vaporized from such zone is condensed and deposited on a surface of target to produce undesirable fine particles of oxide. According to the present invention, a rear surface of target is forced to be cooled during the laser evaporation operation so that the target is cooled compulsorily to prevent scattering of target material from the above-mentioned zone where the laser beam has not satisfactory power level, resulting in that formation or deposition of the fine particles of oxide is prevented effectively. In the laser evaporation method, a laser beam impings onto a surface of a target to create a spot of the laser beam on the surface. As stated above, the spot has a predetermined radial distribution of laser power in such a manner that the center of spot has the most intense laser power as well as the power level of laser beam fluctuates or varies in time during the laser evaporation operation. Theoretical explanation of mechanism why the surface property of a thin film obtained is improved by cooling the target according to the present invention can't given at this stage. The cooling of the rear surface of target can be effected by any known technique. In a preferred embodiment, a cooling pipe is installed inside a target holder and cooling liquid such as water is circulated through the cooling pipe. The cooling liquid is circulated through a cooling unit located outside a vacuum chamber. Temperature of the rear surface of target to be cooled can be determined by experiment. For example, the rear surface of target is cooled down to 10 °C when a laser beam having a energy density of 1.5 to 2.0 J/cm 2 is impinged onto an oxide target having a thickness of 2 mm at a distance between the target and the substrate of 50 mm. The power level depend mainly on kinds of target material and can be found easily by experiment. Usually, the rear surface of target is cooled to a temperature lower than 30 °C during the evaporation. There is no special lower limit of this temperature. In a process according to the present invention, a thinner target is advantageously used in order to increase the cooling efficiency from a rear surface to a surface of the target. The target has preferably a thickness of less than 5 mm, more preferably less than 2 mm. The laser evaporation technique itself is well-known and usual operational conditions can be used in the present invention. Followings are typical operational conditions: Substrate temperature 600 to 700 °C Gas pressure in chamber 133.32 to 1333.2 dPa (100 to 1.000 m Torr) Distance between the target and the substrate 40 to 100 mm Laser density 1.0 to 3.0 J/cm 2 Deposition rate: 10 to 1,000 Å/min Any laser can be used but an excimer laser is usually used. The substrate is preferably a single crystal substrate of oxide such as MgO, SrTiO 3 , LaNO 3 , LaGaO 3 and yttrium stabilized zirconia (YSZ). The process according to the present invention can be used for preparing thin films of any known high-Tc superconductors such as La-Sr(Ba)-Cu-O, Y-Ba-Cu-O, Bi-Sr-Ca-Cu-O and TI-Ba-Ca-Cu-O. The process according to the present invention permits to prepare stably or reproducibly a superconducting thin film of compound oxide possessing improves surface condition and superconducting properties Brief Description of the Drawing Fig. 1 illustrates a structure of a film forming apparatus which can be used in the process according to the present invention. The film forming apparatus shown in Fig. 1 comprises a vacuum chamber 1 in which a substrate holder 2 and a target holder 3 are positioned and a laser 5 which emits a laser beam to a target through a transparent window 4 secured to the vacuum chamber 1. The substrate holder 2 and the target holder 3 are constructed in such a manner that each of substrate 6 and target 7 can be positioned at desired level, orientation and angle. The laser beam emitted from the laser 5 is converged by an optical system 8. The target holder 3 is provided with a water jacket 3a communicated with a circulation circuit 9a, 9b and 9c. The circulation circuit 9c has a cooler 9. The target 7 held on the target holder 3 can be cooled effectively by the water jacket 3a during film formation operation. Description of the Preferred Embodiment Now, the present invention will be described with reference to Example, but the scope of the invention should not be limited to the Example. A superconducting thin film of Y-type compound oxide by using the apparatus shown in Fig. 1. A thin film was deposited on a (100) plane of MgO single crystal substrate by laser evaporation method. As a target, a sintered body of compound oxide having a composition of YBa 2 Cu 3 O y was used. Operational conditions used are summarized in Table 1. Substrate temperature 700 (°C) Gas pressure 533.3 dPa (400 (mTorr)) Laser energy density 1.5 to 2.0 (J/cm 2 ) Film thickness 2,000 (Å) The target 7 was secured to the cooled target holder 3 through silver paste so as to realize high thermal conductivity or contact. The distance between the target and the substrate was adjusted to 70 mm and the deposition rate was adjusted to 300 Å/min. In order to evaluate the resulting sample (sample 1), the same procedure as above was repeated to prepare another sample (sample 2) in the same apparatus but the target was not cooled. The density of oxide particles produced on a surface of the substrate was determined by a scanning electron microscopy (SEM) and the superconducting properties were measured by conventional methods. The results are summarized in Table 2. The critical current density (Jc) was determined at 77 K. Sample Critical temperature (K) Critical current density (A/cm 2 ) Density of oxide particle (number/cm 2 ) 1 90 5 x 10 6 5 x 10 5 2 90 2 x 10 6 3 x 10 7

Claims: Method of preparing a superconducting thin film of compound oxide, which is a high-Tc superconductor, on a substrate by laser evaporation technique, characterized in that a rear surface of a target used is cooled forcedly during film formation. The method set forth in daim 1 wherein the rear surface of the target is cooled to a temperature lower than 30 °C during the evaporation. The method set forth in claim 1 or 2 wherein the target has a thickness of less than 5 mm. The method set forth in any one of daim 1 to 3 wherein the laser beam has an energy density of between 1.0 and 3.0 J/cm 2 . The method set forth in any one of daim 1 to 4 wherein the substrate is heated at a temperature between 600 and 750 °C. The method set forth in any one of claim 1 to 5 wherein the gas pressure in the deposition chamber is adjusted between 133.32 and 1333.2 dPa (100 and 1,000 m Torr). The method set forth in any one of claim 1 to 6 wherein the distance between the target and the substrate is adjusted between 40 and 100 mm. The method set forth in any one of claim 1 to 7 wherein the deposition rate is adjusted between 10 and 1,000 Å/min. The method set forth in any of claims 1 to 8 wherein the compound oxide is selected from the group consisting of La-Sr(Ba)-Cu-O, Y-Ba-Cu-O, Bi-Sr-Ca-Cu-O and TI-Ba-Ca-Cu-O.

Inventors: ITOZAKI HIDEO, NAGAISHI TATSUOKI, NAKANISHI HIDENORI, TANAKA SABURO, ITOZAKI, HIDEO, NAGAISHI, TATSUOKI, NAKANISHI, HIDENORI, TANAKA, SABURO, ITOZAKI, HIDEO, C/O ITAMI WORKS OF SUMITOMO, NAGAISHI, TATSUOKI, C/O ITAMI WORKS OF SUMITOMO, NAKANISHI, HIDENORI, C/O ITAMI WORKS OF SUMITOMO, TANAKA, SABURO, C/O ITAMI WORKS OF SUMITOMO
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1992
Main classification: H01L39
IPC codes: H01B13, H01B12, C23C14, H01L21, H01L39, C30B29