Process for preparing layered thin films

Abstract: A process for depositing successively a plurality of thin films on a bottom superconductor layer made of oxide superconductor deposited on a substrate in a single chamber successively preferably under one of two conditions: in a first condition, deposition of a first thin film to be deposited directly on the bottom super-conductor layer is effected under-such condition that the bottom superconductor layer is heated above the oxygen-trap temperature (T trap ) at which oxygen enter into the oxide superconductor but lower than a film forming temperature of the bottom superconductor layer, and in a second condition, the bottom superconductor layer is heated in ultra-high vacuum at a temperature which is lower that said oxygen-trap temperature (T trap ) but higher than a temperature which is lower by 100 °C than the oxygen-trap temperature (T trap - 100 °C) and then the first thin film is deposited thereon.

Description: Field of the Invention The present invention relates to a process for preparing layered thin films, more particularly, it relates to a process for depositing a plurality of thin films including a bottom superconductor layer on a substrate successively to produce a layered superconducting structure. Description of the related art Oxide superconductors are expected to be used in a variety of applications due to their higher critical temperatures than conventional metal superconductors. In fact, Y-Ba-Cu-O oxide superconductor possess the critical temperature above 80 K and Bi-Sr-Ca-Cu-O and Tl-Ba-Ca-Cu-O oxide superconductors possess that of above 100 K. When the oxide superconductors are used in superconducting devices, it is indispensable to prepare a thin film of oxide superconductor and to laminate a plurality of thin films including a bottom superconductor layer successively on a substrate. For example, in a superconducting junction so-called tunnel type Josephson Junction realized with oxide superconductor, it is required to deposit a bottom superconductor layer, an intermediate layer of non-superconductor and a top superconductor layer on a substrate successively in this order. A Josephson element is a two-terminals element, so that a logical circuit consisting of Josephson elements alone becomes complicated. In order to overcome this demerit of complexity, a variety of ideas of three-terminals elements are proposed. In the superconductor transistors consisting of superconductor and semiconductor which is a typical three-terminals element, it is also required to combine a thin film of semiconductor with a thin film of oxide superconductor and hence successive deposition of thin films each consisting of different material is required. Successive deposition of a thin film of ordinary conductor such as metal onto a thin film of oxide superconductor is required also in the other type superconducting element consisting of superconductor and ordinary conductor. In these superconducting elements, a superconducting current passes through a thin film of non-superconductor sandwiched between two adjacent layers of superconductors positioned close to each other. The distance between the two adjacent superconductors is determined by the coherence length of the superconductor. Since the coherence length of oxide superconductors is very short, the distance between two adjacent superconductors must be several nanometer. In addition to this, from the point of view of performance of the superconducting devices, all thin films in the superconducting device must have high crystallinity, in other words, these thin films are made preferably of a single crystal or polycrystal having crystal orientation which is similar to single crystal. When the superconducting device has thin film(s) made of polycrystal whose crystal orientation is not well-ordered or has amorphous thin film(s), high-performance of the superconducting device can not be expected and hence the function thereof becomes unstable. When a plurality of thin films of oxide superconductors are deposited successively on a common substrate, it is usual practice to subject a surface of a bottom superconductor layer to cleaning operation before a top superconductor layer is deposited, otherwise electrical continuity between the bottom superconductor layer and the top superconductor layer is spoiled due to contaminants adsorbed on the surface of the bottom superconductor layer or undesirable oxides produced on the surface. Discontinuity of two layers result in formation of an undesirable junction between two layers. Superconducting devices or integrated superconducting circuits having such undesirable junction do not show desired performance and sometimes do not work. In particular, the surface condition of the bottom superconductor layer should be considered carefully because the coherence length of oxide superconductors is very short and hence the superconductivity is easily lost. Therefore, the surface of the bottom superconductor layer must be clean and also must have well-ordered crystallinity or superconducting property. In the field of semiconductor industries, surfaces are cleaned with ultra-pure water, by chemical washing, dry or wet etching or the like. In the case of oxide superconductors, however, these cleaning techniques can not be used due to high reactivity of oxide superconductors. If the surface of thin film of oxide superconductor is treated by these known techniques, undesirable reactions occur in the surface, resulting in that cleanness of the surface becomes worse and crystallinity and superconducting property are lost. Patent Applications EP-A-366 949 and JP-A-1 106 481 disclose a process for successively depositing a plurality of thin films layers on a bottom oxide superconductor layer which is itself deposited on a substrate, the successive depositions being carried out in the same chamber. However these documents are silent to heat-treatment in an atmosphere containing oxygen and to oxygen purity. The article published in IEEE Transactions on Magnetics; vol.27, n°2, March 1991, pages 1361-1364 discloses a teaching which is similar to the teaching of the previous cited patent applications. Nevertheless, this document is silent to the purity of oxygen gas. Under certain film forming materials and conditions, constituent elements of the top superconductor layer diffuse or migrate into the bottom superconductor layer, resulting in that an interface between these layers becomes unclear and thin films of oxide superconductor are deteriorated. An object of the present invention is to solve the problems and to provide a process for preparing layered thin films comprising a bottom superconductor layer and the other thin film layers deposited on the bottom superconductor layer and having improved crystallinity and continuity especially at superconducting interfaces. Summary of the Invention The present invention provides a process for depositing successively a plurality of films on a bottom superconductor layer made of oxide superconductor deposited on a substrate, the deposition of said films being carried out in a single chamber successively. The process is characterized in that : prior to deposition of a first film to be deposited directly on said bottom superconductor layer, said chamber is evacuated to a pressure lower than 133.322 x 10 -9 Pa (10 -9 Torr), and then, said first film is deposited in an atmosphere containing oxygen having a purity of higher than 5N (99.999%) and argon, at a temperature lower than the film forming temperature of said bottom superconductor layer and higher than the temperature which is lower by 100°C than the oxygen-trap temperature (T trap ) at which oxygen enters into said oxide superconductor. The oxygen-trap temperature (T trap ) and the film forming temperature are known for respective oxide superconductors. The process according to the present invention is applicable to any known oxide superconductors and is advantageously applicable to Y-Ba-Cu-O oxide superconductor. Bi-Sr-Ca-Cu-O oxide superconductor and Tl-Ba-Ca-Cu-CO oxide superconductor which have the most attractive properties including their high critical temperatures. The substrate is preferably a single crystal of oxide such as MgO, SrTiO 3 , PrGaO 3 or the like. According to the present invention, a layered structure containing at least one thin film of oxide surperconductor of high quality can be produced. Preferably, deposition of the bottom and top superconductor layers and an oxygen-containing thin film to be deposited on the bottom surperconductor layer is carried out in an atmosphere of oxygen having the purity of higher than 5 N (99.999%). Existence of H 2 O and CO 2 in oxygen deteriorate the oxide superconductor because they react easily with the oxide superconductor so that H 2 O and CO 2 should be eliminated as small as possible. In a preferred embodiment, the bottom superconductor layer is a c-axis oriented thin film of Y 1 Ba 2 Cu 3 O 7-x , the first thin film is made of non-superconductor, for example oxide such as MgO or metal such as Ag and a second thin film to be deposited on the first thin film is a top superconductor layer of Y 1 Ba 2 Cu 3 O 7-x . In this preferred embodiment, deposition of all thin films to be deposited on the bottom superconductor layer is effected at a substrate temperature between 400 and 600 °C, and the bottom superconductor layer is heated in ultra-high vacuum of lower than 133.322 x 10 -9 Pa (1 x 10 -9 Torr) at the substrate temperature between 350 and 400 °C before the first thin film is deposited. When deposition of the first thin film is carried out in the temperature range between 400°C and 600°C, enough oxygen enter into the oxide superconductor and diffusion of constituent elements of the first thin film into the bottom superconductor layer can be prevented effectively. For example, when the bottom superconductor layer is a thin film of Y-Ba-Cu-O oxide superconductor, the first thin film of MgO or Ag is deposited at the substrate temperature between 400 and 600 °C. When deposition of the first thin film is carried out in the temperature range between 350°C and 400 °C, oxygen do not escape out of the bottom superconductor layer and constituent elements of the thin film deposited directly on the bottom superconductor layer do not diffuse or migrate into the the bottom surperconductor layer. For example, when the bottom superconductor layer is a thin film of Y-Ba-Cu-O oxide superconductor, the first thin film of MgO or Ag is deposited at the substrate temperature between 350 and 400 °C. In any case, thin films to be deposited on the bottom superconductor layer should not be deposited above the film forming temperature at which the bottom superconductor layer has been deposited. The process according to the present invention is useful for fabricating a superconducting element comprising a bottom superconductor layer, an intermediate layer made of insulator or ordinary conductor and a top superconductor layer having a different crystal orientation. In the process according to the present invention, all layers of bottom superconductor layer and thin films deposited thereon must be produced successively in a single chamber so that the bottom superconductor layer does not contact with air and hence a surface of the bottom superconductor layer is neither contaminated nor deteriorated by a reaction with moisture in air. The stratified thin films prepared by the process according to the present invention show improved crystallinity and continuity especially at superconducting interfaces which are required for realizing superconducting elements or integrated superconducting circuits so that high-performance superconducting systems can be realized. Brief Description of the Drawing Fig. 1A-1D illustrate successive steps for preparing a layered structure containing at least one thin film of oxide superconductor by the process according to the present invention. Fig. 1A shows a substrate (5) on which thin films are to be deposited successively by the process according to the present invention. At first, a bottom superconductor layer (1) is deposited on the substrate (5) preferably in an atmosphere of highly-pure oxygen by off-axis sputtering method, laser abrasion method, reaction evaporation method, MBE or CVD technique (Fig. 1B). According to the present invention, the chamber is evacuated under a background pressure of lower than 133.322 x 10 -9 Pa (1 x 10 -9 Torr) and the temperature of bottom superconductor layer (1) is adjusted within the range determined by the present invention. In the same sputtering chamber, a first thin film (2) such as a thin film of MgO or Ag is deposited by sputtering method, laser abrasion method, evaporation method, MBE or CVD technique or the like (Fig. 1C) under the conditions determined by the present invention. Finally, in the same sputtering chamber, a second thin film (3) such as a top superconductor layer is deposited by off-axis sputtering method, laser abrasion method, reaction evaporation method, MBE or CVD technique (Fig. 1D) under the conditions determined by the present invention. Description of the Preferred Embodiment Now, the present invention will be described with reference to Examples but the scope of the invention should not be limited thereto. Example 1 In this Example 1, three-layered thin films of a bottom superconductor layer of Y 1 Ba 2 Cu 3 O 7-x , an intermediate MgO layer and a top superconductor layer of Y 1 Ba 2 Cu 3 O 7-x are deposited successively on a substrate of MgO(100) under the conditions determined by the present invention whose steps are illustrated in Fig. 1. At first, a substrate (5) of MgO (100) is placed in a ultra-high vacuum chamber which is then evacuated to 133.322 x 10 -9 Pa (1 x 10 -9 Torr). Then, highly pure oxygen having a purity of 99.999 % and argon gas are introduced into the ultra-high vacuum chamber and a thin film of c-axis oriented thin film of oxide superconductor of Y 1 Ba 2 Cu 3 O 7-x (1) having a thickness of 300 nm is deposited on the substrate (5) of MgO (100) by off-axis sputtering method under following operational conditions(Fig. 1B): Sputtering gas Ar 90 % O 2 10 % Pressure 10 Pa Substrate temperature 700 °C After deposition is complete, the substrate temperature is lowered to 500 °C. After that, a thin film of MgO is deposited up to a thickness of 2 nm by evaporation method under following conditions (Fig. 1C): Atmosphere Ar 90 % O 2 10 % Pressure 10 Pa Then, a thin film of oxide superconductor of Y 1 Ba 2 Cu 3 O 7-x (3) having a thickness of 200 nm is deposited on the resulting thin film of MgO (2). Deposition of this top superconductor layer (3) can be carried out by the same method as above but the substrate temperature must be adjusted in a range between 400 and 600 °C. The off-axis sputtering is carried out under following operational conditions: Sputtering gas Ar 90 % O 2 10 % Pressure 10 Pa Substrate temperature 570 °C All procedures are carried out in a single chamber successively. It is confirmed that three layers prepared by the process according to the present invention possess improved crystallinity and continuity especially at superconducting interfaces. Example 2 In this Example 2 also, three-layered thin films of a bottom superconductor layer of Y 1 Ba 2 Cu 3 O 7-x , an intermediate MgO layer and a top superconductor layer of Y 1 Ba 2 Cu 3 O 7-x are deposited successively on a substrate of MgO(100) under the conditions determined by the present invention whose steps are illustrated in Fig. 1. At first, a substrate (5) of MgO (100) is placed in a ultra-high vacuum chamber which is then evacuated to 133.322 x 10 -9 Pa (1 x 10 -9 Torr). Then, highly pure oxygen having a purity of 99.999 % and argon gas are introduced in the ultra-high vacuum chamber and a thin film of c-axis oriented thin film of oxide superconductor of Y 1 Ba 2 Cu 3 O 7-x (1) having a thickness of 300 nm is deposited on the substrate (5) of MgO (100) by off-axis sputtering method under following operational conditions (Fig. 1B): Sputtering gas Ar 90 % O 2 10 % Pressure 10 Pa Substrate temperature 700 °C After deposition is complete, the substrate temperature is lowered to 400 °C in order that oxygen is adsorbed in the oxide superconductor. After this heat-treatment is complete, the substrate temperature is lowered down to 370 °C and the ultra-high vacuum chamber is again evacuated to 133·10 -9 Pa (1 x 10 -9 Torr). At the temperature of 370 °C, oxygen does not escape out of the oxide superconductor. Then, highly pure oxygen having a purity of 99.999 % and argon gas are introduced again into the ultra-high vacuum chamber. After that, the substrate temperature is elevated to 375 °C and a thin film of MgO is deposited up to a thickness of 10 nm by sputtering method under following conditions (Fig. 1C): Then, a thin film of oxide superconductor of Y 1 Ba 2 Cu 3 O 7-x (3) having a thickness of 200 nm is deposited on the resulting thin film of MgO (2). Deposition of this top superconductor layer (3) can be effected by any method. For example, in the case of off-axis sputtering, following operational conditions can be used: Sputtering gas Ar 90 % O 2 10 % Pressure 10 Pa Substrate temperature 700 °C All procedures are carried out in a single chamber successively. It is confirmed that three layers prepared by the process according to the present invention possess improved crystallinity and continuity at interfaces between two adjacent layers.

Claims: A process for depositing successively a plurality of films (2,3) on a bottom superconductor layer (1) made of oxide superconductor deposited on a substrate (5), the deposition of said films (2,3) being carried out in a single chamber successively, characterized in that prior to deposition of a first film (2) to be deposited directly on said bottom superconductor layer (1), said chamber is evacuated to a pressure lower than 133.322 x 10 -9 Pa (10 -9 Torr), and then, said first film (2) is deposited in an atmosphere containing oxygen having a purity of higher than 5 N (99.999%) and Argon, at a temperature lower than the film forming temperature of said bottom superconductor layer (1) and higher than the temperature which is lower by 100°C than the oxygen-trap temperature (T trap ) at which oxygen enters into said oxide superconductor. The process set forth in claim 1 wherein deposition of said bottom superconductor layer is carried out in an atmosphere of oxygen having the purity of higher than 5 N (99.999%). The process set forth in claim 1 or 2 wherein said bottom superconductor layer is a c-axis oriented thin film of Y 1 Ba 2 Cu 3 O 7-x. The process set forth in any one of claims 1 to 3 wherein said first thin film is made of non-superconductor. The process set forth in claim 4 wherein said non-superconductor is oxide such as MgO or metal such as Ag. The process set forth in any one of claims 1 to 5 wherein a second thin film (3) to be deposited on said first thin film (2) is a top superconductor layer of Y 1 Ba 2 Cu 3 O 7-x . The process set forth in any one of claims 1 to 6 wherein said substrate (5) is a single crystal. The process set forth in any one of claims 1 to 7 wherein deposition of said films is effected at a temperature of bottom superconductor layer between 350 and 600 °C.

Inventors: IIYAMA MICHITOMO, NAKAMURA TAKAO, TANAKA SO, IIYAMA, MICHITOMO, NAKAMURA, TAKAO, TANAKA, SO
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1992
Main classification: H01L39
IPC codes: H01L39