Novel SOx/NOx sorbent

Abstract: An alumina sorbent capable of adsorbing NOx and SOx from waste gases and being regenerated by heating above 600°C is made by incorporating an alumina stabilizing agent into the sorbent. A preferred method is to add the stabilizer when the alumina is precipitated. The precipitated powder is formed subsequently into a slurry, milled and dripped to form the stabilized spheroidal alumina particles. These particles are impregnated with an alkali metal or alkaline earth metal to form the stabilized sorbent. Alumina stabilizers include one or more of silica, lanthana, other rare earths, titania, zirconia and alkaline earths.

Description: BACKGROUND OF THE INVENTION The Government of the United States of America has rights in this invention pursuant to Contract No. DE-AC22-89PC88889 awarded by the U.S. Department of Energy. 1. Field of Invention This invention relates to an improved sorbent for removing NOx and SOx from exhaust gases and the improved removal process using that sorbent. 2. Description of the Previously Published Art The NOXSO process, described in U.S. Patent No. 4,798,711, uses a porous alumina sorbent containing sodium to adsorb NOx and SOx from flue gases. After the adsorption the nitrogen- and sulfur-laden sorbent is regenerated by heating the sorbent in a reducing atmosphere. In addition to other preferred reducing atmospheres for regenerating, methane gas is also disclosed. However, by using natural gas or methane the regenerator operates at a higher temperature of about 650°C which tends to further reduce the surface area of the alumina beads. As this NOXSO sorbent cycles back and forth from adsorption to regeneration, it undergoes transformations which reduce its surface area. In the fresh condition the alumina sorbent has a surface area on the order of about 200 m 2 /g. After about 100 cycles the surface area of the sorbent is reduced to below 50 m 2 /g. When the surface area becomes that low, the performance becomes unacceptable. FR-A-2 324 361 discloses a sulphur oxide acceptor comprising copper oxide as active ingredient deposited on a porous sintered alumina body. EP-A-0 097 539 relates to a method for preparing spheroidal alumina particulates. The reference is silent with respect to the stabilization of the alumina particles in the corrosive environment of NOx and SOx removal or in the presence of alkali or alkaline earth metals. US-A-4 061 594 describes an alumina-based substance obtained by agglomeration of active alumina whose resistance at high temperatures is increased by the addition of La, Nd, Pr, Th oxides. FR-A-2 189 112 describes the use of a porous alumina sorbent containing a salt of an alkali or alkaline earth metal to adsorb NOx and SOx from flue gases. 3. Objects of the Invention It is an object of this invention to develop a sorbent with a stable surface area and pore volume at regenerator conditions in the presence of sodium or other alkali metals. It is further object of this invention to provide a stabilized surface area sorbent for use in adsorbing NOx and SOx from a flue gas. It is further object of this invention to provide a sorbent with stable surface area under hydrothermal conditions in the presence of sodium. It is further object of this invention to provide a sorbent with stable long term performance with regard to NO x /SO x adsorption after prolonged adsorption/regeneration cycling. It is further object of this invention to provide a sorbent with low attrition characteristics upon adsorption/ regeneration cycling. It is further object of this invention to provide a sorbent which retains its integrity when it is in the bead form. It is further object of this invention to provide alternative processes to produce a stabilized surface area sorbent for use in adsorbing NOx and SOx from a flue gas. It is further object of this invention to provide a process for the continued removal of nitrogen oxides and sulfur oxides from a gas containing them with a stabilized sorbent which can undergo regeneration at high temperatures and under hydrothermal conditions. These and further objects will become apparent as the description of the invention proceeds. Summary of the Invention A sorbent for NOx and SOx has been developed which retains a relatively high surface area after continuous use in a cycled adsorption/regeneration process. The sorbent can also adsorb other impurities such as chlorides, HCl, and heavy metals such as arsenic, lead, etc. The sorbent is made by adding a stabilizer to an alumina forming slurry. A preferred alumina stabilizer is silica which can be added in the form of sodium silicate. When making alumina from a slurry, the slurry conventionally contains, for example, aluminum sulfate and sodium aluminate which react to form alumina. According to the invention, an alumina stabilizer such as silica is further added to this slurry. The three ingredients coprecipitate. This silica alumina coprecipitate is preferably filtered, washed and dried to a powder. The powder is then easily transported to where the beads are to be formed. There the powder is slurried in a water/nitric acid/acetic acid mixture and dripped in a drip column containing a NH 3 -liquid hydrocarbon phase on top of an aqueous ammonia phase. The silica stabilized alumina beads are dried and calcined and then impregnated with up to 1-20 wt % with an active ingredient of either an alkali metal or alkaline earth metal and preferably with sodium at about 4-6 wt %, by the incipient wetness technique. Brief Description of the Drawings Figure 1 is a schematic diagram of the process of making the stabilized alumina containing sorbent. Figure 2 illustrates the stability of the sorbents to steam. Figure 3 illustrates the improved retention of surface area over time for the sorbent according to the present invention in a cycled adsorption/regeneration process. Description of the Preferred Embodiments We have found that for our sorbent use, the alumina stabilizer used can be our preferred silica as well as other alumina stabilizers. For example, lanthana, and other rare earth oxides, either alone or in mixtures can be used to make a stabilized sorbent for our intended purpose. The amount is preferably from an effective amount up to about 30 mole %. We have found at least three techniques to add the stabilizer to the alumina when forming beads by the dripping method. In the event the stabilizer can be mixed with alumina precursor materials without making the solution too viscous, then our preferred first embodiment for production is by co-precipitating to make the sorbent such as by co-gel formation. This technique is described by Nozemack et al in U.S. Patent No. 4,780,446, the entire contents of which is incorporated herein by reference. There a silica stabilized alumina is prepared as a cc-gel by a precipitation process under specific and controlled reactant concentrations and reaction temperature, time, and pH. A source of an acid aluminum salt, preferably an aluminum sulfate solution, a source of alkali metal aluminate, preferably sodium aluminate solution and a source of alkaline metal silicate, preferably sodium silicate solution are combined to obtain a silica-alumina co-gel reaction mixture. The cogellation reaction is conducted in two stages: (1) An initial co-gel is precipitated at a pH of about 7.5 to 8.5 and preferably about 8; and (2) The precipitated co-gel is stabilized at a pH of about 9.6 to 10.3 and preferably about 10. The desired reaction pH is maintained by controlling the flow rate of the aluminum sulfate, sodium aluminate and sodium silicate reactants. Furthermore, sufficient sodium silicate is added to impart a total silica (SiO 2 ) content of the finished precipitated co-gel of from an effective stabilizing amount up to about 30 mole % and more preferably from about 5.5 to 8.5 percent by weight SiO 2 . The alumina stabilizers that can be added by this co-precipitation process include silica, lanthana, or other rare earth oxides. The stabilized alumina powder is then used to make substantially uniform spheroidal alumina particles. A preferred procedure for making the spheres is described in U.S. Patent No. 4,279,779, the entire contents of which is incorporated herein by reference. Following this procedure, a slurry of the stabilized alumina is prepared in an acidic aqueous medium and droplets of the slurry are passed through air into a column containing an upper body of a water immiscible liquid such as a liquid hydrocarbon and ammonia and a lower body of aqueous alkaline coagulating agent. The resulting spheroidal particles are aged in aqueous ammonia to the desired hardness. The aged particles are dried and calcined. The improved process used to manufacture the sorbent is illustrated in Figure 1 and is briefly described below. A slurry is prepared using a mixture of stabilized alumina powder, water, and acids such as acetic acid and nitric acid. The slurry is then preferably reduced in size such as by the preferred method of milling to reduce the average particle size from greater than 10 microns to 2-5 microns. Although the sorbent can be made without the preferred milling step, the resulting beads tend to have a low compacted bulk density, a high attrition rate and a low crush strength. Thus the particle size reduction by milling is the preferred procedure. Other size reduction techniques can be used such as dry milling, hammer milling, ball milling and fluid energy milling. These techniques can be either wet or dry procedures. The slurry is fed to a large, commercial scale Netzsch Mill at a rate of 15 ℓ/min (4 gallons/minute). The mill itself contains from 151-208 ℓ (40-55 gallons) of 1.5 mm Quackenbush beads which are continuously moved around internally by disks attached to a rotating axes. Slurry particles are then grounded down to the desired particle size by the action of the glass beads. Control of particle size is established by withdrawal or addition of specific amounts of glass beads. After milling, the slurry is dripped in a dripping column which preferably consists of ammoniated kerosene on top of an ammoniated water solution. The organic phase is needed to form spheres while the aqueous phase further hardens the beads. After dripping, the beads are transferred to a de-watering system and then passed through a dryer with a flow of air through the beads. After drying, the sorbent is calcined in an indirect fired rotary kiln. Over and undersized particles are removed in a vibratory separator. Next, impregnation with the active ingredient which is an alkali metal or an alkaline earth metal and preferably sodium as Na 2 CO 3 is performed. This can be done in a horizontal rotary drum impregnator. Finally, the sorbent is dried and calcined to yield the final product. The second method of adding the alumina stabilizer is to mix it with the alumina powder prior to dripping to form the particles. All of the stabilizers including clay can be added in this procedure. The third method of adding the alumina stabilizer is to form the alumina particle by the dripping method and to then impregnate the particle with the alumina stabilizer. The stabilizer can be added either before or after the sodium is added or to reduce production costs it can be added along with the sodium. Again, all of stabilizers can be added this way except for clay since it is not soluble. Additional bead forming procedures can be used to make the beads in addition to these dripping methods discussed above. The ingredients can be mixed together and the mixture can be extruded to form extrudates with preferably an approximate 1:1 ratio of length to diameter. The mixture can be placed in an agglomerator to agglomerate the beads. Other mechanical forming methods can be used such as pilling. The NO and SO 2 adsorption performance of the sorbent was measured in an adsorption/regeneration cycling unit. The unit is a batch-operated fluidized bed with flue gas containing 3000 ppm SO 2 , 500 ppm NO, 4% O 2 and 10% H 2 O. The cycle begins with these gases flowing through the fluidized sorbent bed at a temperature of about 140°C. The average conditions over the first 10 minutes of this batch-operated fluidized bed run are approximately equivalent to the conditions the sorbent will experience in intended industrial use with a design sorbent loading of 1.5 wt% sulfur. The run continues for an additional 10 minutes where a sulfur loading of about 2.5% is obtained. The NO adsorption performance over this time period is measured continuously with a Thermo Electron Instruments chemiluminescent NO analyzer. The SO 2 adsorption performance is measured by sulfur analysis of sorbent samples pulled at 2-5 minute intervals from the fluidized bed. The adsorption phase is stopped and the beads are then regenerated in methane for 20 minutes at 650°C followed by a steam treatment for 20 minutes at 650°C. The regenerated beads are allowed to cool down to the adsorption temperature in the range of 120-160°C with the preferred target temperature being 140°C . After a given number of cycles, the beads are removed from the batch adsorption/regeneration apparatus and they are evaluated for surface area. The NO desorption is analyzed by temperature programmed desorption. The beads are also placed in a regenerator connected to a gas chromatograph and the desorption of SO 2 is measured for a 20 minute interval while methane is passed over it at 650°C. This produces a product distribution of S, SO 2 and H 2 S. Then steam is passed over the sorbent at 650°C for 20 minutes to remove any residual H 2 S. The following sections describe the test procedures used and referred to in the claims. For the attrition and crush tests the beads are screened to pass through 10 mesh and remain on 20 mesh. Sorbent Cycle Stability To evaluate the effective life of the sorbents we use a Sorbent Cycle Stability procedure. Under this procedure, we compare the surface area after 20 adsorption/regeneration cycles (a sufficient period of time for the initial high surface area of the fresh sorbent to drop down to a working level) with the surface area after 100 cycles. This is a significantly long period of time to evaluate how the sorbents have stood up to the recycled conditions. For the sorbents made according to the present invention, they typically have their surface area drop from a fresh value of over 200 m 2 /g to about 150 m 2 /g by the 20th cycle. Then after 80 more cycles, the surface area drops less than 60 m 2 /g. Other alumina sorbent particles having the same amount of sodium will loose substantially more than 60 m 2 /g of surface area under this same test condition and they will have a lower total surface area. Crush Strength Crush strength is determined by placing the spheroidal particle between two parallel plates of a testing machine such as Ametek force gauge model ML4434-4 manufactured by AMETEK Co., 8600 Somerset Drive, Largo, Florida, which is mounted on a motorized test platform. The bottom plate is the anvil and the upper is the platen. By pressing the start button the plates are slowly brought together and the force gauge moves down the motorized platform at 0.125 cm/s (.0491 inch/second). The amount of force required to crush the particle is registered on a digital readout which has been calibrated in pounds force. A sufficient number (for example, 25) of riffled particles are each individually crushed to obtain a statistically significant representation of the total population. The average of the individual results is then calculated. To make sure the beads are measured at constant conditions, they are placed in a porcelain evaporating dish and heated by an electric bunsen burner at a temperature of at least 400°C. A bead is then removed from the dish and its crush strength is determined while it is still hot. When the beads are to be used in a fluidized bed environment it is preferred to have an average crush strength of at least 1.81 kg (4 pounds). The significance of having this high crush strength value is that the beads will not break apart during the severe physical treatment they receive in the fluidized bed and the other mechanical devices present in a commercial plant. GM-Attrition The attrition is measured by the Air Jet Attrition procedure which involves placing a set volume (60 cc.) of material to be tested in an inverted Erlenmeyer flask of special construction which is connected to a metal orifice inlet. A large (one inch) outlet covered with 20-mesh screening is located on the flat side (bottom) of the flask. High velocity dry nitrogen gas is passed through the inlet orifice causing the particles to: (1) circulate over one another thus causing attrition, and (2) impact themselves in the top section of the flask thus breaking down as a function of strength. The material is tested for five minutes and the remaining particles are weighed. The loss in weight after testing expressed as percent of the initial charge is designated the attrition loss. The nitrogen flow will be in the range of about 1463 to 1888 cm 3 /s (3.1 to 4.0 cubic feet per minute), depending upon the density of the material. The flow rate must be sufficient for the particles to strike the top section of the flask. The fines produced by attrition are carried out of the flask by the nitrogen flow thus causing a loss in weight of the original material charged. The significance of a low attrition value is that the particles are not easily being attrited away as they are fluidized in the adsorber, the regenerator and the fluidized transport between these two units. In a large scale unit it is expected that an economical sorbent should have less than 1.2% attrition loss per day. In terms of the Air Jet Attrition procedure described above with the Erlenmeyer flask, it is desirable to have less than 2% and for preferable commercially acceptable performance to have less than 1% loss in that accelerated attrition test. Attrition During Adsorption/Regeneration Cycling An adsorption/regeneration cycling test is used to measure the adsorption/regeneration cycling (ARC) attrition of the sorbent. Sorbent that has a size range between 10 and 20 screen mesh is adsorbed at 140°C in a batch-operated fluidized bed with flue gas containing 3000 ppm SO 2 , 500 ppm NO, 4% O 2 and 10% H 2 O until it contains 1.5-2% sulfur. The sorbent is then regenerated with methane for 20 minutes at 650°C followed by stream treatment for 20 minutes at 650°C. This adsorption/regeneration process is repeated a second time. The sorbent is then screened and weighted. All sorbent smaller than 35 mesh in size is considered attrited material. The % attrition per day is based on the percent of the total material that is smaller than 35 mesh and is then normalized to reflect 8 adsorption/regeneration cycles per day. A chemical attrition value of less than 10% per day is clearly needed, preferably less than 5% per day and more preferably less than 1.2% per day on this test for a commercial sorbent which will be subjected to a fluidized bed operation. Surface Area The surface areas referred to throughout this specification and claims are the nitrogen BET surface areas determined by the method described in the article by S. Brunauer, P. Emmett, and E. Teller, J. Am. Chem. Soc., Vol. 60, p. 309(1938). This method depends on the condensation of nitrogen into the pores, and is effective for measuring pores with pore diameters in the range of 10 to 600 Å. The volume of nitrogen adsorbed is related to the surface area per unit weight of the support. Compacted Bulk Density To determine the compacted bulk density a given weight of freshly calcined spheroids is placed in a graduated cylinder sufficient to contain the material within its graduated volume. The cylinder is then vibrated until all settling ceases and a constant volume is obtained. The weight of sample occupying a unit volume is then calculated. Total Porosity The pore size distribution within the activated spheroidal particle and total porosity is determined by mercury porosimetry. The mercury intrusion technique is based on the principle that the smaller a given pore the greater will be the mercury pressure required to force mercury into that pore. Thus, if an evacuated sample is exposed to mercury and pressure is applied incrementally with the reading of the mercury volume disappearance at each increment, the pore size distribution can be determined. The relationship between the pressure and the smallest pore through which mercury will pass at the pressure is given by the equation: r = 2σCOS /P where r = the pore radius σ = surface tension  = contact angle P = pressure Using over pressures up to 4137 bar (pressures up to 60,000 p.s.i.g.) and a contact angle of 130°, the range of pore diameters encompassed is 35-10,000 Å. The mercury porosimetry measures the total mercury pore volume in cm 3 /g. The particle density is also measured in terms of g/cm 3 . By multiplying the two together the total porosity is determined in units of cm 3 /cm 3 . Hydrothermal Stability The BET surface area stability of the sorbent under hydrothermal conditions is measured by subjecting the sorbent beads to a 100 volume % steam atmosphere at 650°C and the surface area is measured at regular intervals. Using this test the sorbent should retain at least 100 m 2 /g of surface area after 1500 hours in the steam and preferably greater than 140 m 2 /g. Having described the basic aspects of our invention, the following examples are given to illustrate specific embodiments thereof. Example 1 Following the procedure described in U.S. Patent 4,780,446 a silica stabilized alumina powder was produced. The powder contained 6.5% silica. This powder is commercially available from Davison Chemical Division of W. R. Grace & Co.-Conn. as silica alumina. The powder contains 28% moisture when heated to 954°C (1750°F). The average particle size of the powder is 15-20 microns when measured by the Malvern Particle Analyzer. Example 2 Following the procedure described in U.S. Patent 4,154,812 an alumina powder was produced. This powder is commercially available as SPA Alumina from Davison Chemical Division of W. R. Grace & Co.-Conn. The powder contains 28% moisture when heated to 954°C (1750°F). The average particle size of the powder is 15-20 microns when measured by the Malvern Particle Analyzer. Example 3 45.4 kg (One hundred pounds) (dry basis) of the silica stabilized alumina made in Example 1 was slurried in a mixture of 113.6 ℓ (30 gallons) water, 2404 grams 70% nitric acid and 3,237 grams of glacial acetic acid and mixed in a high shear mixer for 25 minutes. The slurry was then milled in a 20 liter Netzsch Mill. The average particle size was reduced to less than 5 microns. The slurry was afterwards dripped in a column containing an NH 3 kerosene phase on top of an aqueous NH 3 phase. The wet spheres were then dried and air calcined. The silica stabilized alumina spherical particles were impregnated at two levels of sodium. In one batch they were impregnated to 4 wt % sodium using sodium carbonate with the incipient wetness technique and in the other batch they were impregnated to 6 wt. % sodium. This technique involves permitting the beads to adsorb an amount of liquid equivalent to 80-100% of their pore volume. The particles were then dried at 120°C in a vacuum oven and air calcined for 6 hours at 650°C. The particles impregnated at 4% sodium (to be identified as 3A) had a surface area of 254 m 2 /g, a compacted bulk density of 39 lbs/ft 3 , an average crush of 10.2 pounds, a total porosity measured by mercury of 0.712 cm 3 /cm 3 and a GM attrition loss of 0.2%. The particles impregnated at 6% sodium (to be identified as 3B) had a surface area of 210 m 2 /g, a compacted bulk density of 625 kg/m 3 (40 lbs/ft 3 ), an average crush of 3.6 kg (8 pounds), a total porosity measured by mercury of 0.714 cm 3 /cm 3 , a GM attrition loss of 0.1% and an ARC attrition loss of 0.3%. To test the hydrothermal stability of the beads, the particles were exposed to a 100 vol % steam atmosphere at 650°C and the surface area was measured at regular intervals. Figure 2 shows that the sorbent having the 4% sodium stabilizes at 200 m 2 /g and the sorbent having the 6% sodium stabilizes at 170 m 2 /g. Comparison Example 4 An alumina dripping slurry was prepared in the same manner as given in Example 3, except that the alumina powder from Example 2 was used which does not contain any silica. When it was initially slurried 75.7 ℓ (20 gallons) of water were used instead of 113.6 ℓ (30 gallons) to obtain the desired viscosity. It was dripped and impregnated to the same level of sodium and afterwards dried and calcined as given in Example 3A. Exposure to 100 vol% steam at 650°C then showed a steep decline of surface area as shown in Figure 2. The particles had a surface area of 211 m 2 /g, a compacted bulk density of 575.1 kg/m 3 (35.9 lbs/ft 3 ), an average crush of 3.13 kg (6.9 pounds), a total porosity measured by mercury of 0.676 cm 3 /cm 3 , a GM attrition loss of 0.7%, and an ARC attrition loss of 0.2%. Example 5 The silica containing sorbent of Example 3B and the nonsilica containing sorbent of Comparison Example 4 were evaluated by the Sorbent Cycle Stability procedure. These two samples have different sodium levels. However, it is believed that a comparison between the two is fair with regard to surface area properties. If one had the same substrate with different sodium levels, the sorbent with the higher sodium level would have the lower surface area because the additional sodium would be covering (i.e. taking up) the additional surface area. See Example 3 where the 3A sorbent with 4% Na has a surface area of 254 m 2 /g while the 3B sorbent with the higher Na level of 6% has a lower surface area of 210 m 2 /g. Thus by having the larger amount of sodium for the sorbent according to the present invention, there should be less surface area than the sorbent with the smaller amount of sodium and thus the comparison is believed to be fair because one would expect that the comparison sorbent of Comparison Example 4 would have the greater starting surface area than the sorbent of Example 3B with its higher sodium loading. Note, however, that the fresh sorbent of Example 3B (with the higher amount of sodium) actually has about the same surface area. The reason appears to be because the added silica which acts as the stabilizer also provides additional surface area to make up for the surface area lost by the additional sodium. The sorbent according to the present invention in Example 3B was cycled 232 times and the surface area ultimately decreased to 70 m 2 /g. Sorbent made according to Comparison Example 4 without the stabilizer after being only cycled 100 times already had its surface area down to 60 m 2 /g. The change in surface area over cycles is set forth in Figure 3. The drop off in performance can be further seen from the data taken from Figure 3 and presented in Table 1 below by comparing the surface area of the sorbent after 20 cycles with that after 100 cycles and also comparing the rate of surface area decay between the 20th and 100th cycle. Surface Area, m 2 /g 20 cycles 100 cycles Drop Example 3B 150 100 50 Comp. Example 4 125 60 65 Without the stabilizer the surface area drops off 65 m 2 /g over the 80 cycles to a low level of 60 m 2 /g whereas for the sorbent with the stabilizer present according to the present invention the surface area only drops off 50 m 2 /g during the 80 cycles and the surface area remains at a higher, superior level of 100 m 2 /g. The sorbent according to the present invention with the silica stabilizer has a higher surface area. Although this is very favorable, the even more significant advantage is that the rate of decrease in surface area for the silica stabilized sorbent is slower than the rate of decrease in surface area for the unstabilized sorbent.

Claims: An active ingredient containing stabilized alumina sorbent capable of adsorbing NOx and SOx and other impurities from waste gases and being regenerated by heating above 600°C comprising stabilized spheroidal alumina particles having a surface area of at least 180 m 2 /g; a compacted bulk density of 320 to 721 kg/m 3 (20 to 45 pounds per cubic foot); an average crush strength of at least 1.8 kg (4 pounds), an attrition loss measured by the Air Jet Attrition method of less than 2%; an alumina stabilizer selected from the group consisting of silica, lanthana, other rare earth oxides, and mixtures thereof in an amount from an effective amount up to 30 mole %; and an active ingredient selected from the group consisting of alkali metals, alkaline earth metals and mixtures thereof and present in an amount of from 1 to 20 wt %, said sorbent when subjected to the Sorbent Cycle Stability procedure having its surface area dropping less than 60 m 2 /g from the 20th to the 100th cycle, and when subjected to the Hydrothermal Stability procedure maintaining a BET surface area of at least 100 m 2 /g and which procedure involves subjecting the sorbent to a 100 volume % steam atmosphere at 650°C and measuring the BET surface area after 1500 hours. Sorbent according to Claim 1, wherein the attrition loss measured by the Air Jet Attrition method is less than 1%. Sorbent according to Claim 1, wherein the active ingredient is sodium present in an amount of from 4-6 wt %. Sorbent according to Claim 1, wherein the alumina stabilizer is silica. Sorbent according to Claim 1, wherein the active ingredient is sodium and the alumina stabilizer is silica. Sorbent according to Claim 1, wherein the BET surface area under the Hydrothermal Stability procedure is at least 140 m 2 /g. Sorbent according to Claim 1, wherein the Adsorption/Regeneration Cycling attrition is less than 10% per day, preferably less than 5% per day. Sorbent according to Claim 6, wherein Adsorption/Regeneration Cycling attrition is less than 1.2% per day. A method of producing an active ingredient containing stabilized alumina sorbent in accordance with claim 1 capable of adsorbing NOx and SOx from waste gases and being regenerated by heating above 600°C comprising: (a) co-precipitating alumina forming reactants and an alumina stabilizer material selected from the group consisting of silica, lanthana, other rare earth oxides, and mixtures thereof to form a stabilized alumina powder; (b) reducing the particle size of the powder to obtain an average particle size of less than 10 microns; (c) forming substantially uniform spheroidal alumina particles by forming droplets of a slurry of the powder which are passed through air into a column containing an upper body of a water immiscible liquid and ammonia and into a lower body of aqueous alkaline coagulating agent; (d) drying and calcining the particles; (e) impregnating the calcined particles with an active ingredient selected from the group consisting of an alkali metal, alkaline earth metal and mixtures thereof; and (f) drying and calcining the impregnated particles to form the sorbent. Method according to Claim 9, wherein the alumina forming reactants are aluminum sulfate and sodium aluminate. Method according to Claim 9, wherein the alkali metal impregnating agent is sodium. Method according to Claim 9, wherein the stabilized alumina particles are reduced to an average particle size of 2-5 microns. Method according to Claim 9, wherein the alumina stabilizer material is present in an amount from an effective amount up to 30 mole %. Method according to Claim 9, wherein the alumina stabilizer is silica. Method according to Claim 9, wherein the active ingredient is an alkali metal or alkaline earth metal present in an amount of from 1 to 20 wt %. Method according to Claim 9, wherein step (a) is carried out such that the stabilized alumina powder is formed by forming a slurry of alumina powder and the alumina stabilizer material. Method according to Claim 16, wherein the active ingredient is sodium and the alumina stabilizer is silica. Method according to claim 9, wherein steps (a) and (e) are carried out such that in step (a) a slurry of alumina powder is formed, and in step (e) the calcined particles are impregnated with the following two components: (i) the alumina stabilizer material, and (ii) an alkali metal or alkaline earth metal, said two components being either added together or sequentially in any order. Method according to Claim 18, wherein the active ingredient is sodium and the alumina stabilizer is silica. A method of producing an active ingredient containing stabilized alumina sorbent in accordance with claim 1 capable of adsorbing NOx and SOx from waste gases and being regenerated by heating above 600°C comprising: forming alumina particles from i) an alumina powder having a particle size less than 10 microns; ii) an alumina stabilizer selected from the group consisting of silica, lanthana, other rare earth oxides, and mixtures thereof in an amount from an effective amount up to 30 mole %; and iii) an active ingredient of a metal selected from the group consisting of alkali metals, alkaline earth metals and mixtures thereof and present in an amount of from 1 to 20 wt %; and calcining the particles to form the sorbent. Method according to Claim 20, wherein the forming is done by extrusion, by agglomeration or by pilling.

Inventors: BEECKMAN JEAN WILLEM, HAGER JOHN MICHAEL, PLECHA STANISLAW, ZIEBARTH MICHAEL S, BEECKMAN, JEAN WILLEM, HAGER, JOHN MICHAEL, PLECHA, STANISLAW, ZIEBARTH, MICHAEL S.
Applicants: GRACE W R & CO, W.R. GRACE & CO.-CONN.
Application year: 1992
Main classification: B01J20
IPC codes: B01D53, B01J20