PHOTOCURABLE CYCLOBUTARENE COMPOSITIONS

Abstract: Photocurable cyclobutarene compositions having a low dielectric constant, low moisture uptake, enhanced oxidative stability, good processability, good planarization, and a long shelf life are disclosed. These polymer compositions are useful in composites, laminates, membranes, films, adhesives, coatings, and electronic applications such as multichip modules and printed circuit boards. An example of such photocurable cyclobutarene compositions is a mixture of a photosensitive agent such as 2,6-bis(4-azidobenzylidene)-4-methylcyclohexanone and a cyclobutarene such as oligomeric divinyltetramethyldi-siloxane bisbenzocyclobutane.

Description: PHOTOCURABLE CYCLOBUTARENE COMPOSITIONS This invention relates to photocurable polymers and processes for preparing them. Such polymers are used in passivation films, photoresists, as insulating layers in fabricating electrical devices and as protective films for semiconductor elements. Thermal- and/or photo-cured polyimides, which are currently used in many of these applications, have drawbacks, some of which include: a short shelf life, less than desirable thermal oxidative stability, microcracking during thermal cycling, and lack of processability including a high degree of volatile release. Other examples of known light sensitive compositions include the following. U.S. Patent No. 4,243,743 discloses a composition comprising a poly(amic acid), an organic compound having a photosensitive olefinic double bond and an amino group or a quarternary ammonium salt, and Michier's ketone. U.S. Patent No. 4,321 ,319 discloses a composition comprising a poly(amic acid) having a photosensitive olefinic double bond, Michier's ketone, nitrofluorene, and 5-nitroacenaphthalene. U.S. Patent No. 4,366,230 discloses a composition comprising a modified poly(amic acid) obtained by introducing a methacryl or acryl group into the ester residue of the poly(amic) acid and Michier's ketone. The compositions disclosed in these three patents produce less than desirable results since a portion of the compositions exposed to light is released when solvent developed and cured. It would be desirable to have photocurable polymers with one or more improved physical properties or improved combinations of physical properties, compared to the aforementioned polymers. Some of these properties include a low dielectric constant, a low dissipation factor, low moisture uptake, high sensitivity, high contrast, high resolution, thermal stability, enhanced oxidative stability, resistance to chemicals and plasmas, good adhesion, low release of volatiles, good processability, good planarization, a long shelf life, consistency control, high purity, and low cost. This invention, in one aspect, is a photocurable, organic-soluble mixture comprising at least one cyclobutarene as its major component and at least one photosensitive agent in an amount sufficient to convert the mixture to an organic-insoluble solid upon exposing the mixture to photon radiation- Organic-soluble means the portion of the nonpolar mixture not exposed to photons is soluble in hydrocarbons such as Stoddard solvent, xylene, mesitylene, toluene, 2-methoxyethyl ether (diglyme), N-methyi pyrrolidone (NMP), mixtures of NMP and 2-hydroxyethyl 2-pyrrolidone, dipropylene glycol dimethyl ether, n-butyl butyrate or a Stoddard/methanol mixture. When the mixture is polar, organic-soluble means the portion not exposed to photons is soluble in N-methyl pyrrolidone, ethyl lactate, 2-methoxyethyl ether or n-butyl butyrate. In a second aspect, this invention is the photo-cured organic-insoluble solid polymer resulting from photon irradiation of the photocurable mixture. These photocured polymers are useful in applications such as photoresists, etching masks, interlayer dielectrics, liquid crystal displays, and flat panel displays. In a third aspect, the photocurable mixture can be applied to a substrate, portions of the applied mixture are exposed to photon radiation and the substrate is then treated with an organic developing solvent to remove the uncured portion of the mixture; this invention being the pattern-coated substrate resulting from this procedure having the photocurable portion of the mixture adhered thereto. In a fourth aspect, the photocured composition of the second or third aspect is subjected to thermal curing- The photo/thermally cured polymers of this invention have one or more improved physical properties or improved combinations of physical properties, compared to the aforementioned art-known polymers. Such properties may include a low dielectric constant, a low dissipation factor, low moisture uptake, high sensitivity, high contrast, high resolution, thermal stability, enhanced oxidative stability, resistance to chemicals and plasmas, good adhesion, good processability, low release of volatiles, a long shelf life, a high degree of planarization, consistency control, high purity and low cost. These photo/thermally cured polymers are useful in many applications; some of which include composites, laminates, membranes, films, electronics, coatings, and adhesives- The electronic applications include such areas as multichip modules and printed circuit boards- The cyclobutarenes suitably employed as the major component in the photocurable mixtures of this invention correspond to the formula wherein B is a monovalent organic moiety, a direct bond, an n-valent bridging member comprising (1) a polyvalent inorganic moiety, or (2) a polyvalent organic moiety, 10 or B is absent; Ar is a polyvalent aromatic or heteroaromatic moiety, an ar-poly-yl, having three or more valences, provided that the two carbon atoms of the cyclobutane ring on the fused side are bonded to adjacent carbon atoms on the same aromatic ring of Ar; 15 n is an integer of 1 or more; m is an integer of 1 or more; and R 2 is a monovalent moiety. The synthesis and properties of these cyclobutarenes, as well as the terms used to descri be them are found in Gray et al., JACS 100, 2892, (1978); Loon-seng Tan et al., Polymer Preprints, 27(2), 20 240, (1986); U.S. Patent Application Serial Numbers 07/766,392, 07/701,433, 07/703,957, U.S. Patents 4,540,763; 4,783,514 and 4,826,997. The preferred cyclobutarene monomers correspond to the formulae: 25 30 35 0 The more preferred cyclobutarene monomers correspond to the formulae: The most preferred cyclobutarene monomer corresponds to the formula: Suitable photosensitive agents employable in this invention are those which have an absorption maximum nearthe wavelengths of the photon source being used and effect cyclobutarene photocuring. When a photosensitizer is used in conjunction with a photosensitive agent, suitable photosensitive agents are those capable of accepting energy from the photosensitizer. Preferred photosensitive agents include azides, bismaleimides, acrylates, acetylenes, isocyanates, conjugated aromatic ketones, and benzophenone-containing polymers. The most preferred group of photosensitive agents is the azides. The azides employed in preparing the polymers of this invention correspond to the formula Q-(N 3 ), wherein Q is an x-valent organic moiety, and x is an integer of 1 or more. 5 Examples of suitable azides, as well as their synthesis and properties are described in "Azides and Nitrenes, Reactivity and Utility", Academic Press, 1984; "Azides and Amines from Grignard Reagents and Tosyl Azide" Smith etal-, J. Org. Chem., 34, 3430, (1969); "Encyclopedia of Polymer Science and Engineering", 2nd Edition, Volume 1 1 , 186-212; Yang et al., Proc. SPlE-Int.Soc. Opt. Eng., 469(Adv. Resist Technol.), 117-26, 1984; Wolf etal., J. 10 Electrochem. Soc, 131(7), 1664-70, 1984; Tsunoda etal., Photographic Science and Engineering, 17, 390, (1973); Journal of Photographic Science, 29, 188, (1976); "Organic Compounds with Nitrogen-Nitrogen Bonds" Ronald Prez Co., NY, NY, 1966; Boyer etal., Chem. Rev., 54, 1, (1954); Japanese Patent NumberJ01279240-A, U.S. Patents 4,565,767; 4,294,908; 4,354,976, and European Patent Applications 90300546.0, 841 12698-0, 84300837.6, 83810156-6- 15 Preferred azides are aromatic bisazides some examples of which are represented by the following formulae- 2,6-Bis[3-(4-azidophenyl)-2-propenylidene] cydohexanone ,6-Bis[3-(4-azidophenyl)-2-propenylidene]-4-methylcyclohexanone 2,6-Bis(4-azidobenzal)-4-methylcyclohexanone p-Azidophenyl Sulfone m-Azidophenyl Sulfone 4,4' -Diazidostilbene 4,4' -Diazidobenzalacetophenone 2,3-Diazido-1,4-naphthoquinone 4,4' -Diazϊdo diphenyl methane More preferred azides are highly conjugated aromatic bisazϊdes. The most preferred azide is determined by the wavelengths of the photon source employed. One chooses an azide which has an absorption maximum nearthe wavelengths of the photon source being used, or if a photosensitizer is being used in conjunction with the photosensitive agent one chooses an azide that will accept energy from the photosensitizer. Solubility of the azide in the system being used is also a consideration. The amounts of cyclobutarene and photosensitive agent employed in preparing the polymers of this invention can vary- Suitable amounts are those which contain one or more cyclobutarenes as the major component and provide a photocurable mixture from which photocured organic-insoluble polymers can be prepared which have one or more improved physical properties or improved combinations of physical properties, compared to the aforementioned art-known polymers- Such properties include a low dielectric constant, a low dissipation factor, low moisture uptake, high sensitivity, high contrast, high resolution, thermal stability, enhanced oxidative stability, resistance to chemicals and plasmas, good adhesion, low release of volatiles, good processability, a long shelf life, a high degree of planarization, consistency control, high purity, and low cost. A suitable amount of photosensitive agent is that which provides sufficient curing in the photon-exposed portion of the mixture to render it insoluble in the developing solvent. A preferred weight percent (hereinafter weight percent) range of photosensitive agent is 0.1 to 20 based on the sum of the weights of the photosensitive agent and the cyclobutarene. A more preferred weight percent range of photosensitive agent is 1 to 6. The most preferred weight percent range of photosensitive agent is 2 to 4. A preferred weight percent range of the cyclobutarene is 80 to 99.9 based on the sum of the weights of the photosensitive agent and the cyclobutarene. A more preferred weight percent range of the cyclobutarene is 94 to 99. The most preferred weight percent range of the cyclobutarene is 96 to 98. In addition to a cyclobutarene and a photosensitive agent, some embodiments of this invention contain one or more optional components which may be added to tailor the invention's characteristics. Suitable optional components which may be added to increase the monomer formulation's pot life and the cured resin's toughness include free radical inhibitors such as 2, 6-di-tert-butyl-4-methyl phenol, tetrakis [methylene (3,5-di-tert-butyl-4- -hydroxyhydrocinnamate)] methane, tris (2,4-di-tert-butyl-phenyl)phosphite, thiodiethylene bis-(3,5-di-tert-butyl-4-hydroxy) hydrocinnamate, octadecyl 3,5-di-tert-butyl-4-hydroxy) hydrocinnamate, N,N-diphenyl-p-phenylenediamine, 1 ,2-dihydro-2,2,4-trimethyldihydro- quinoline, triphenylmethane, H disulfides such as al ylaryl disulfides, dialkyldisulfides, and diaryldisulfides including and an isomeric mixture of octylated diphenylamines such as The most preferred free radical inhibitor is 2,6-di-tert-butyl-4-methylphenol- A suitable amount of the optional free radical inhibitor is that which provides an increased monomer formulation pot life and increased cured resin toughness compared to a formulation without free radical inhibitor- The preferred weight percent range of optional free radical inhibitor is 0 to 10- The more preferred weight percent range of optional free radical inhibitor is 0 to 5, with the most preferred range being 0 to 2. The monovinylidene mono(cyclobutarene)s that may be added as an optional componeπtto lowerthe polymerization onset temperature and/or improve the cured polymer's toughness are represented by the following formula wherein Ar is a polyvalent aromatic moiety, an ar-poly-yl, having three or more valences, provided that the two carbon atoms on the fused side of the cyclobutane ring are bonded to adjacent carbon atoms on the same aromatic ring of Ar; Y is a covalent bond or a divalent organic or inorganic moiety; m is an i nteger of at least 1 ; R is a monovalent moiety; and R 8 is a monovalent organic moiety or a heteroatom containing monovalent organic moiety- The synthesis and properties of these monovinylidene mono(cyclobutarene)s are described in U.S. Patent Application Serial No. 07/766,392- A suitable amount of the optional monovinylidene mono(cyclobutarene) isthat which measurably lowers the polymerization onset temperature and/or improves the cured polymer's toughness- Preferably, the optional monovinylidene mono(cydobutarene) is employed at a weight percent range of less than 20, more preferably at a weight percent range of less than 15, and most preferably at 1 to 10 weight percent. Preferred monovinylidene mono(cyclobutarene)s are 1,1 -substituted arylethylenes represented by the formula CHR 1 0 Ar — C - wherein Ar is a monovalent aromatic or heteroaromatic moiety; R 10 is H or an alkyl moiety containing 1 to 4 carbon atoms; and Z is a monovalent aromatic or heteroaromatic moiety, provided that it is a cyclobutarene-containing moiety only when Ar is a cyclobutarene-containing moiety. The synthesis and properties of these 1 , 1 -substituted arylethylenes are described in U.S. Patent Application Serial No. 07/701 ,433. An internal olefinic mono(cyclobutarene) may also be added as an optional component to adjust the cured polymer's crosslinking density and/or improve its toughness. Internal olefinic mono(cyclobutarene) herein refers to a cyclobutarene moiety containing a carbon-carbon double bond wherein neither carbon of the double bond occupies a terminal position of the cyclobutarene moiety. Suitable internal olefinic mono(cyclobutarene)s are represented by the formula wherein Ar is a polyvalent aromatic moiety, an ar-poly--yl, having three or more valences, provided that the two carbon atoms on the fused side of the cyclobutane ring are bonded to adjacent carbon atoms on the same aromatic ring of Ar; A is a covalent bond or a divalent organic or inorganic moiety; m is an integer of at least 1 ; R is a monovalent moiety; R 6 anc j 1 * are individually hydrogen or an alkyl moiety; and R 12 is hydrogen or a monovalent organic moiety provided that when R 1 1 is hydrogen R 12 is a monovalent organic moiety. The synthesis and properties of these internal olefinic mono(cyclobutarene)s are described in U-S. Patent Application Serial No. 07/766,392. A suitable amount of optional internal olefinic mono(cyclobutarene) isthat which increases the cured polymer's crossl inking and/or improves its toughness. Preferably, the optional internal olefinic mono(cyclobutarene) is employed at a weight percent range of less than 20, more preferablyata weight percent range of less than 15, and most preferably at 1 to 10 weight percent- Maleimidocyclobutarenes which may be added as an optional component to increase the cured polymer's toughness are represented by the formula wherein X is a direct bond or a divalent organic or inorganic moiety; Ar is a polyvalent aromatic moiety, an ar-poly-yl, having three or more valences, provided that the two carbon atoms on the fused side of the cyclobutane ring are bonded to adjacent carbon atoms on the same aromatic ring of Ar; m, q, and p are integers of 1 or more; and isa monovalent moiety. The synthesis and properties of these maleimidocyclobutarenes are described in U.S. Patents 4,783,51 and 4,826,997. Asuitable amount of the optional maleimidocyclobutarene is that which increases the cured polymer's toughness- Preferably, the optional maleimidocyclobutarene is employed at a weight percent range of less than 20, more preferably at a weight percent range of less than 15, and most preferably at 1 to 10 weight percent. The optional poiymaleimide monomers which may be added to increase the cured polymer's thermal stability and/or improve its toughness correspond to the formula wherein n is an integer of 2 or greater; R 1 is separately and independently in each occurrence, a monovalent moiety, provided that R 1 does not interfere with polymerization; and R 3 is an n-valent bridging member comprising an n-valent organic moiety or heteroatom-containing organic moiety. The synthesis and properties of these optional polymaieimide monomers are described in U.S. Patent Application Serial No. 07/630,902. A suitable amount of the optional polymaieimide monomer is that which increases the cured polymer's toughness and/or thermal stability. Preferably, the optional polymaieimide is employed at a weight percent range of less than 20, more preferably at a weight percent range of less than 15, and most preferably at 1 to 10 weight percent. An antioxidant may be added to increase the formulation's oxidative stability during processing as well as in the cured resin. Antioxidants of the phenol-, sulfide-, phosphite-, and amine type may be employed in this invention. Hindered amines are the preferred antioxidants. Hindered amines with aliphatic and aromatic moieties are more preferred antioxidants. The most preferred antioxidant is polymerized 1 ,2-dihydro-2,2,4- -trimethylquinoline, CAS registry number 26780-96-1. Preferably, the optional antioxidant is employed at a weight percent range of less than 8, more preferably at a weight percent range of less than 7, and most preferably at .001 to 6 weight percent. A photosensitizer may be added to increase the photosensitive agent's photosensitivity. The synthesis and properties of suitable optional sensitizers are disclosed in Specht et al., Tetrahedron, Vol. 38, No. 9, p 1203-121 1 , (1982); Tsunoda et al., Photographic Science and Engineering, 17, 390, (1973); U.S. Patent 4,268,603; and European Patent Application 90300546.0. Suitable photosensitizers are those whose absorption maximum is nearthe wavelengths of the photon source employed. Preferred photosensitizers are represented by the foil owing formulae. where Ar is represented by the following formulae: where R 20 , R 21 , R 22 , R 2 3 are separately and Independantly H, OCH3, and -N(C 2 H5) 2 - where Ar is represented by the following formulae: More preferred photosensitizers are represented by the following formulae. 3 , 3 ' -carbonyl bis ( 7- ethoxycoumarin ) 3,3'-carbonyl bis (7-diethylaminocoumarin) 15 Preferably, the optional photosensitizer is employed at a weight percent range of less than 5, more preferably at a weight percent range of less than 3, and most preferably at .001 to 2 weight percent. Preferably the cyclobutarene-containing portion of the formulation and any _. optional components are oligomerized or B-staged priorto use to improve handling, processing, and performance characteristics. The cyclobutarene may also be oligomerized without any photosensitive agent or other optional components present. The molecular weight of a resin directly impacts its performance in a photoresist system. It is most preferred to have the highest molecular weight possible while maintaining a high solubility level. It is __ further desirable to have low polydispersity (Mw/Mn; where Mw is the weight-average molecular weight and Mn is the number-average molecular weight) so that the sol uble oligomers are easily converted into an insoluble gel when exposed to a photon source. This will result in the maximum solubility difference between the exposed and unexposed areas of the polymer film covering the wafer or substrate. Mw can be controlled by the extent of _. conversion during oligomerization or B-staging. With the most preferred cyclobutarene, divinyitetramethyl-disiloxane bisbenzocyclobutane, represented by the formula the gel point occurs while a significant portion of monomer and low molecular weight oligomers are presentdue to the complex nature of the linking group in this poly(cydobutarene). The extent of conversion also affects the molecularweightdistribution- The average molecular weight and molecularweightdistribution may also be altered by selectively removing some oligomeric mixture components. A wider range of oligomermofecutarweights results in a wider range of oligomer solubilities after photocuring. The lower molecular weight materials remain soluble after photocuring, thus it is desirable to remove them from the formulation priorto coating it on a substrate to minimize losses upon solvent development- The lower molecular weight materials may also be removed rom the oligomerized cyclobutarene prior to adding a photosensitizer or other optional components. Preferably at least 80 weight percent of the cyclobutarene monomer is removed priorto coating the solution on a substrate- More preferably at least 80 weight percent of the cyclobutarene monomer and at least weight 50 percent of the cyclobutarene dimer is removed prior to coating the solution on a substrate- Even more preferably at least 80 weight percent of the cyclobutarene monomer and dimer is removed priorto coating. Most preferably at least 90 weight percent of the cyclobutarene monomer and dimer and at least 50 weight percent of the cyclobutarene trimerare removed. The preferred oligomer may contain 80 weight percent or more of oligomers of a degree of polymerization of three or more. The more preferred oligomer may contain 90 weight percent or more of oligomers of a degree of polymerization of three or more. The most preferred oligomer may contain 95 weight percent or more of oligomers of a degree of polymerization of three or more. By a degree of polymerization of three or more is meant species of the molecular weight of trimers and higher- One may determine the percentage of monomer, dimer and trimer in the oligomerized cyclobutarene by gel permeation chromotography (GPC)- The weight • percentage of monomer, dimer and trimer are approximately equal to the peak areas of the GPC trace. They are not exact because detection is by refractive index and the response factors for the monomer and dimer may vary somewhat from that of the oligomer. The approximation may be used and is used in the data in this specification. For more accurate determinations, the response factors for the monomer and dimer should be determined- A preferred cyclobutarene oligomer may contain 80 weight percent or more of oligomers of a molecular weight of 1,000 or more as determined from peak area percent by GPC, using a refractive index detector, uncorrected for response factors and as measured against polystyrene standards- A more preferred cyclobutarene oligomer may contain 90 weight percentor more as determined from peak area percent of oligomers of a molecular weight of 1,000 or more, similarly determined- A most preferred cyclobutarene oligomer may contain 95 weight percentor more of oligomers of a molecular weight of 1 ,000 or more, similarly determined- Various methods may be used to obtain the preferred molecular weight distribution of the cyclobutarene oligomer. The desired cyclobutarene monomer may be oligomerized or B-staged neat by heating. Then the lower molecular weight fractions may be removed by extraction in a nonsolvent for he higher molecular weight species. For example, one may dissolve the cyclobutarene oligomer in a miscible solvent and then mix it with a nonsolventto precipitate out the higher molecular weight species. Forthe DVS-BCB, mesitylene may be used as the miscible solvent and an alcohol such as t-amyl alcohol may be used as the precipitating solvent. One means of effecting this removal is alcoholic precipitation, as exemplified in Example 16. Other techniques commonly used to separate the fractions of a polymer mixture may also be employed here, such as chromatography and solvent extraction, including supercritical solvent extraction. B-staging of benzocyclobutanes is described in U.S. Patent 4,642,329. When neat B-staging is complete, a solvent, sometimes called a casting solvent, is used to dissolve the B- staged material and thus may be used to facilitate its removal from the B-staging apparatus. Hydrocarbons are suitable solvents for most nonpolar oligomeric cyclobutarene-containing systems. Preferred solvents for most nonpolar oligomeric cyclobutarene-containing systems include xylene and mesitylene. The most preferred solvent is mesitylene. B-staging may also be performed in solution. Suitable solvents for polar oligomeric cyclobutarene-containing systems include N-methyl pyrrolidone, ethyl lactate, 2-methoxyethylether, 2-methoxyethylether, and gamma butyrolactone. The most preferred solvent for polar oligomeric cyclobutarene-containing systems is N-methyl pyrrolidone. Some systems require a small quantity of cosol vent to solubilize the photosensitive agent when it is present at the high end of its specified weight percent range. When the photosensitive agent is an azide, suitable cosoivents include ethers, glycol ethers, ketones, and esters. Preferred cosoivents are 2-methoxyethanol, 2-ethoxyethanol, 2-methoxyethylether, and 2-ethoxyethyl ether. The most preferred cosolvent is 2- ethoxyethylether. The photosensitive agent can be dissolved in the B-staged resin/solvent system by heating in an oven, water bath, or by sonication. The most preferred method is a water bath. All manipulations of the cyclobutarene/photosensitive agent mixture are preferably performed in a darkened environment to prevent premature initiation of the photosensitive reaction by photon radiation. One means of providing a suitable environment is by using working space equipped with amber filtered (yellow) lights. Thin films of the cyclobutarene-containing formulation may be applied to substrates without the use of an adhesion promoter. When desirable, an optional adhesion promoter is formulated as a spray- or spin-on solution which is applied immediately after solvent cleaning of the substrate and immediately before applying the cyclobutarene- containing formulation- Alternatively, the adhesion promoter is added to the cyclobutarene/photocrossl inking agent formulation. The adhesion promoter is designed such that one end of the molecule either covalently attaches or adsorbs to the metal, metal oxide, or ceramic substrate surface, while the second end of the molecule reacts or interacts with the cyclobutarene polymer matrix. Suitable adhesion promoters include trialkoxyvinylsilanes and trialkoxyvinylsilyl benzocyclobutanes. More preferred adhesion promoters include include 3-aminopropyftriethoxysilane, trimethoxyvinylsiIane, triethoxyvinylsϊlane, trimethoxyvinylsilyl benzocyclobutanes, and triethoxyvinylsilyl benzocyclobutanes- The most preferred adhesion promoter is 3-aminopropyltrϊethoxysitane. The preparation and properties of trialkoxyvinylsilyl benzocyclobutanes are described in U.S. Patents 4,831,172 and 5,002,808. Suitable substrates are comprised of silicon, alumina, and a variety of ceramic materials such as aluminum nitride- More preferred substrates are comprised of alumina and silicon. The most preferred substrate is comprised of silicon. The cyclobutarene-containing formulations are applied from solutions containing 10-70 weight percent solids. Solids content and the molecular weight of the cyclobutarene- containing formulation determine the viscosity of the spray- or spin-on solution. Spin time and speed are used to control film quality and thickness at a particular formulation viscosity. Details of substrate coating with benzocyclobutane films can be found in the Journal of Electronic Materials, Vol 19, No. 12, 1990- The-majority of the casting solvent is removed during the spin coating process. A softbake cycle may be required to remove residual solvent. The softbake also relaxes stress resulting from flow of the polymer film, increases the film's adhesion to the substrate, and hardens the film for more convenient handling during processing; for example, to prevent adhesion to a mask when printing in a hard contact mode- A preferred softbake temperature is one sufficient to remove residual solvent, provide stress relaxation which requires a temperature above the polymer's glass transition temperature, but low enough to avoid oxidizing or thermal curing of the resin- The preferred softbake temperature will vary depending in-part on the components of the cyclobutarene-containing formulation. A more preferred softbake temperature ranges from 80°Cto 150°C. The most preferred softbake temperature ranges from 80°C to 120°C When using a photosensitizer it is most preferred to use 80°Casthe softbake temperature because of the thermal instability of the photosensitizer- Apreferred softbake time is one sufficient to remove residual solvent, provide stress relaxation, but short enough to avoid oxidizing or thermal curing of the formulation components. The preferred softbake time will vary depending in partonthe components of the cyclobutarene-containing formulation. A more preferred softbake time ranges from 15 seconds to 60 minutes- The most preferred softbake time range depends on balancing desired performance results with maximizing throughput, may vary from 15 seconds to 30 minutes. To maximize throughput, the minimum time would be optimal. Suitable softbake atmospheres include a vacuum, air, nitrogen, argon, and helium. Nitrogen is the most preferred atmosphere. The manner in which the films are cooled affect their performance. The slower the cooling, the denser the vitrified polymer. A high density, low void volume polymer is resistant to solvent penetration. A decreased solvent penetration rate results in a reduced resist development rate. Exposure dose is dependent upon the photon source being used. An increase in the photon source intensity may help to overcome high optical density problems associated with thick polymeric films up to 30μm(micrometers). Selective removal of various components of a high pressure mercury photon source may provide superior film performance. Suitable photon sources include those for which a suitable photosensitive agent exists that can absorb that photon source's wavelengths of energy. Preferred photon sources include visible light, ultraviolet light, X-rays, and electron beams. More preferred photon sources include ultraviolet and visible light. The most preferred photon source is dependent upon the photosensitive agent being used and should be chosen such that its photon emissions are near the absorption maximum of the photosensitive agent or photosensitizer employed. Following photon exposure, an optional softbake cycle may be employed. This cycle increases the reaction rate of long-lived photochemical ly generated intermediates. These intermediates have increased mobility during this cycle and thus may migrate and find a reactant species. An alternative means of increasing the mobility of these reactive intermediates is heating during photon exposure. Such a procedure increases the photosensitive agent's sensitivity. Once photon exposure is complete, the film is solvent developed. Solvent development comprises removing, using a solubilizing solvent, the material that has not been exposed to photon radiation and thus not photo-cured. Dissolution involves two steps. The first is solvent penetration which converts the glassy polymer to a swollen network. The second step involves extracting low molecular weight oligomers from the gel atthe solution interface. Preferred solvent development methods include spray or immersion techniques. Spray development is the more preferred technique. Suitable developing solvents are those which selectively dissolve the nonphoton-exposed film component. Suitable solvents for nonpolar polymerfilm systems include hydrocarbons such as Stoddard solvent, xylene, mesitylene and toluene, 2-methoxyethyl ether (diglyme), n-butyl butyrate, dipropylene glycol dimethyl ether, N-methyl pyrrolidone (NMP), mixtures of NMP and 2-hydroxyethyl 2-pyrollidone and a Stoddard/methanol mixture. Stoddard solvent as used herein is defined at page 1095, "Hawley's Condensed Chemical Dictionary", 1 1th Edition, Van Nostrand Reinhold Company, New York, 1987- The most preferred solvent for nonpolar polymerfilm systems is n-butyl butyrate- Suitable developing solvents for polar polymer film systems include N-methyl pyrrolidone, mixtures of n-butyl butyrate and ethyl lactate, 2-methoxyethyl ether (diglyme), n-butyl butyrate, dipropylene glycol dimethyl ether, N-methyl pyrrolidone (NMP) and mixtures of NMP and 2-hydroxyethyl 2-pyrollidone- The most preferred solvent for polar polymerfilm systems is n-butyl butyrate- One property that makes polymeric insulators useful in multichip module - fabrication istheirabilityto planarize topographical features. The definition obtainable in photoresists is limited by the wavelength of the photon source employed and thus thickness variations can bedetrimental to the quality of the module produced- For this reason it is important to have good planarization- At this point in the process, the patterned thin film may have additional mϊcrocircuitry and photodefined dielectric layers applied to it or it can be further thermally cured- Procedures for preparing multilayer interconnect units or multichip modules are disclosed in the following references: J.J. Reche, "Fabrication of High Density Multichip Modules", IEEE/CMT 1989 IEMT Symposium, p.104; T- Tessier et al., "Process Considerations in Fabricating Thin Film MCM's", (EPS 1989, p.294; S.F- Hahn et al., "The Fabrication and Properties of Thermoset Films Derived from Bisbenzocyciobutene for Multilayer Applications", Proceedings of the ACS Division of Polymeric Materials: Science and Engineering, 59, 190, 1988; P-H-Townsend etal., "The Processing and Properties of Multilayer Interconnection Structures Using Thermoset Films Derived From Bisbenzocyciobutene", Proceedings of the Materials Research Society, p-47, 1989; J- Reche et al., "High Density Multichip Module Fabrication", The International Journal for Hybrid Microelectronics, Vol. 13, No.4, 1990. Additional information on preparing multichip modules may be found in "Beπzocyclobutene Processing Guide For Multilayer Interconnect Fabrication (Multichip Modules)", The Dow Chemical Company, Midland, Michigan, 1991. The aforementioned photo-cured polymers are then subjected to heat for sufficient time to complete the curing process. The following preferred heating cycle may be employed for further curing in a nitrogen atmosphere- 50°C for 0.5 hour 50°Cto 250°Cover 1 hour 250°C for 1 hour 250°C to 100°C over 2 hours Preferably, cyclobutarenes are cured in an atmosphere of 100 ppm or less of oxygen to minimize oxidation. The following examples are illustrative only, and do not limit the scope of the invention- All percents stated in the following examples are by weight unless otherwise noted- All weight percents stated are relative to the percent of the combi ned weight of polyazide and cyclobutarene present in the system, unless otherwise noted. Example-1 - Preparation of Photosensitive, Patterned Thin Films From 2,6-bis(4- -azidobenzylidene)-4-Methylcyclohexanone and Oligomeric Divinyltetramethyldisiloxane Bisbenzocyclobutane A sufficient quantity of a 2,6-bis(4-azidobenzylidene)-4- -methylcyclohexanone 3AC-M) (347.3 mg, 0.938 mmol) was added to a darkened vial containing oligomeric divinyltetramethyldisiloxane bisbenzocyclobutane (DVS-BCB) (20.0636g, 55 percent solids in mesitylene, 11.035 g polymer, Mw = 31000, Mn = 1300) to form a 3 percent solution of BAC-M. The vial was wrapped in aluminum foil and heated to 60°C for 45 minutes to dissolve the BAC-M. The DVS-BCB/BAC-M mixture was transferred to an Eberbach mixer and shaken for 40 minutes. The DVS-BCB/BAC-M solution was transferred to a class 1000 cleanroom for deposition on bare silicon wafers or substrates. Prior to deposition, the wafers were cleaned using a xylene stream applied to the wafer during a spin cycle. A stream of adhesion promoter, a 0.5 percent solution of triethoxyvinylsilylbenzocyclo-butane(TES-BCB) in water, was applied to the wafer for 2 seconds during a subsequent spin cycle using a syringe connected to a 0.2 μm filter, afterwhich the wafer was spun dry. Applying the DVS-BCB/BAC-M solution to the substrate begins by pouring it onto the center of the stationary silicon substrate, which was then followed by a spin coating step. The spin coating procedure employed for the DVS-BCB/BAC-M solution, using a Solitec Model 5100 spin coater, involveed two steps and produced a 5 μm coating after thermal cure. The first step was a spread cycle during which the substrate or wafer was spun at 500 rpm for 3 seconds to completely cover it with resin. The second step involved accelerating the substrate to 5000 rpm and holding it at that speed for 30 seconds. The film close to the edge of the wafer, often called the edge bead, comprised concentric polymer ri ngs that were somewhat thicker than the remai nder of the f i I m. The edge bead was removed using a xylene stream during a spin cycle. Edge bead removal increased the film thickness uniformity and made manipulating the substrate easier. Residual solvent not removed during the spin coating process was removed using a softbake cycle in an oven containing a nitrogen atmosphere at 80°C for 0.5 hours. After cooling to ambient temperature, the substrate was exposed for 5 minutes using a USHIO 250 watt medium-pressure mercury-xenon lamp contained within a Canon PLA501 FA mask aligner through a patterned chrome-on-glass plated mask in the contact printing mode. The contact printing mode as used herein refered to direct contact between the mask and the film. This mode produced the highest resolution possible. Solvent development, which was the dissolution and removal of film areas not exposed to photons, was effected by swirling the substrate while it was immersed in Stoddard solvent for 1 minute- Development produced the negative image in the film of the pattern contained on the mask which included 10 x 10 μm vias. The substrate was thermally cured under a nitrogen atmosphere using the following cure cycle. 50°Cto 100 c Cover 5 minutes 100°Cfor 15 minutes 100°C to 150°C over 15 minutes 150°C for 15 minutes 150°Cto 250°Cover 1 hour 250°Cfor 1 hour 250°C to 100°C over 2 hours The step height of the film as measured by profilometry, using a Tencor Instruments Alpha-Step 200 computerized surface profiler, was 2.48 μm, which was 48 percent of the control film thickness. The stylus mass used was 5 mg, the scan length 400 μm, and the scan rate 5 μm/second- Example 2- Effect of Exposure Dose on Residual Film Thickness A 3 percent solution of BAC-M in DVS-BCB resin, prepared according to the procedure described in Example 1 , was coated on a series of bare silicon wafers using the procedure described in Example 1. The substrates were exposed to the photon source of Example 1 for 1, 2, 3, 5, 10, and 15 minutes. The photon-exposed coated wafers were solvent developed using two immersion cycles of 30 seconds in Stoddard solvent. After a hard cure using the procedure described in Example 1 , the film thickness was measured by stylus profilometry. Table 1 shows the effect of exposure dose on residual film thickness. Table 1 This data indicated that film thickness was influenced by exposure dose. Exposure time was a function of the photon source and preferably was minimized to increase throughput. The minimum exposure time was that necessary for the photons to penetrate the film sufficiently to cure the bottom layer of the film in contact with the substrate. Crossl inking at this interface prevented delamination of the polymer from the substrate. Example 3 - Effect of Development Solvent Contact Time on Residual Film Thickness A 3 percent solution of BAC-M in DVS-BCB resin, prepared according to the procedure described in Example 1, was coated on a series of bare silicon wafers using the procedure described in Example 1. The films were exposed to the photon source for 15 minutes to ensure completion of the photochemical reaction. The wafers were quartered and one section was not developed thus serving as a control for the initial film thickness. The wafers were immersed in Stoddard solvent for different time periods. The films were dried under a nitrogen stream after development and thermally hard cured using the procedure described in Example 1. The film thickness of each sample, as measured by stylus profilometry, is shown in Table 2. Table 2 Table 2 showed that the majority of film thickness losses occur in the first 20 seconds of solvent development. This characteristic allowed for a wide range of development times with little effect on the film thickness. Example 4- Effect of Photosensitive Agent Concentration on Residual Film Thickness One, two, three, and four percent solutions of BAC-M in DVS-BCB resin were coated on a series of bare silicon wafers using the procedure described in Example 1. The films were solvent developed for 1 minute in Stoddard solvent followed by hard curing. The film thicknesses differ as shown in Table 3. Table 3 Variation in Film Thickness with % BAC-M % BAC-M Film Thickness (μm) 1 0 2 1 .572 3 2.035 4 2. 948 The data shows that film thickness can be increased by increasing the percent BAC-M. Example 5 - Effect of Cosolvent on Normalized Film Thickness BAC-M (315.4 mg, 0-852 mmol, 5.4 percent) was added to a darkened vial containing oligomeric DVS-BCB (9-9974 g, 55 percent solids in mesitylene, 5.498 g polymer, Mw = 27100, Mn = 1300) in a darkened laboratory. A 0.5353 g portion of 2-methoxyethanol was added to dilute the polymerto 52.2 percent solids based on the sum of the weights of polymer and solvents. After shaking on an Eberbach mixer for five minutes at a high setting, the solution was heated at 60°C for 0.5 hours. The sample was shaken on the high setting for 0.5 hours as it is cooled to ambient temperature. The agitation and heating cycles were repeated followed by a 5 hour shake at a low setting, afterwhich the BAC-M was fully solubilized- Additional solutions are prepared at 6.3 percent BAC-M(370.4 mg), and 7.3 percent BAC-M(435.4 mg) using 0-5247 and 0-5314 g of 2-methoxyethanol, respectively. The 6.3 percent sample was almost completely soluble and the 7.3 percent sample even less soluble- Additional methoxyethanol, 0-2858 g and 0.5010 g, was added to the 6.3 percent and 7.3 percent BAC-M samples, respectively- After shaking on an Eberbach mixer for 5 minutes on the high setting, the solutions were heated at 60°Cfor 0.5 hours. The samples were shaken for 0.5 hours ona high setting as they were cooled to ambient temperature- This procedure completely solubϊlizes the 6-3 percent sample, but not the 7.3 percent sample. Film preparation was performed as described in Example 1, except that sol vent development was performed by spraying the wafer with solvent thereby forming a puddle of solvent on the wafer. The wafer was stationary for 5 seconds followed by the spread and spin cycles of Example 1- The samples were thermally hard cured using the procedure described in Example 1- The film thickness of each sample, as measured by stylus profilometry, is shown in Table 4. Table 4 Normalized Fi lm Thickness as a Funct ion of % BAC-M %BAC-M Normalized Film Thickness 1 2 3 4 5 6 7 This data showed that the normalized (compared to a control for each percent BAC-M solution) film thickness increased significantly with increased in the percent BAC-M. Using 2-methoxyethanol permits BAC-M dissolution at 5 and 6 weight percent in a mesitylene solution containing polymer at 55 percent solids. Such levels were not reproducibly attainable using mesitylene alone. Example 6 - Effect of resin Molecular Weight on Film Retention A 27, 100 weight-average molecular weight DVS- -BCB resin was subjected to the same film preparation, exposure, solvent development, and analysis as described in Example 1. The thermal cure cycle is as follows. 50°C for 0.5 hour 50°C to 250°C over 1 hou r 250°C for 1 hour 250°Cto 100°C over 2 hours The residual film thickness of this system was 36.3 percent of the control film thickness. A 44,000 weight-average molecular weight DVS- -BCB resin (Mn = 1360) was prepared by increasing the extent of conversion by B-staging for a longertime period. It was diluted to 55 percent solids to allow a valid film retention comparison to the previously described film system comprising a 27,100 molecular weight polymer. This was done by diluting with mesitylene and shaking for 1 hour using an Eberbach mixer on the high setting prior to adding the 3 percent BAC-M. The light sensitive formulation was prepared by the procedure described in Example 1. The residual film thickness of this system was 48.3 percent of the control film thickness. A 73,000 weight-average molecular weight DVS-BCB resin (Mn = 1400) was prepared by further increasing the extent of conversion by B-staging- This material surpasses its gel point- The gels are removed by filtration- It was diluted to 55 percentsolids with mesitylene and shaken for 1 hour using an Eberbach mixer on the high setting priorto adding the 3 percent BAC-M photosensitive agent. The 3 percent BAC-M was added under amber filtered yellow lights to prevent premature photocuring of the mixture. After dissolving the BAC-M, the mixture was taken to a class 1000 deanroom having filtered amber lights and was subjected to the same coating, softbake, exposure, solvent development, and hard cure as the two previous examples- Surface profilometry indicated the resultant film retained 58.2 percent of the initial film thickness- These three examples demonstrate that film retention was increased by increasing the cyclobutarene resin molecularweight- Example 7 - Effect of Varying the Oligomer Percent Solids Content The 73,000 molecularweight DVS-BCB resin from Example 6 was used at 60 percentsolids, in the following protocol. BAC-M (377.7 mg, 1.02 mmol, 3.0 weight percent) was added to a darkened vial containing oligomeric DVS-BCB (20.0022 g, 60 percent solids in mesitylene, 12.0013 g polymer, Mn = 1 ,400, Mw = 73,000) in a darkened laboratory- The vial was wrapped in aluminum foil and heated for 45 minutes in an oven at60 c C. The sample was removed from the oven and shaken on an Eberbach mixer at a high setting for 20 minutes as it cooled to ambienttemperature. After treatment with spread and spin cycles and softbake conditions as described in Example 1 , the wafer was exposed to the photon source described in Example 1 for 15 minutesthrough a mask- The wafer was quartered and one section not developed thereby serving as a reference for the initial film thickness- One section is immersion developed for 30 seconds in Stoddard solvent- All of the films are thermally hard cured as described in Example 6. The film's masked areas that are solvent developed with Stoddard solvent are 8.4 μm thick as measured by stylus profilometry, which translates to a 27.9 percent film loss relative to the undeveloped portion which measures 1 l.55μm- This film retention of 72.1 percent at 60 percentsolids can be compared to the 58-2 percent film retention of the 55 percent solids 73,000 molecularweightsystem of Example 6. This data indicates that higher polymer solids loadings in mesitylene produces thicker polymer coatings. At excessive solids loadings, fibers form which emanate over the edge of the wafer which can complicate processing. The aspect ratio of this film system, as measured by electron microscopy, is approximately 0.5 for a 9.1 μm high line separated by 18.2 μm from its nearest neighboring feature- Example 8 - Effect of the DVS-BCB Molecular Weight Distribution on Film Retention The oligomeric DVS-BCB of Example 5 (40.0 g, 55 percent solids in mesitylene, 22.0 g polymer, Mn = 1300, Mw = 27100) was placed in an addition funnel positioned high enough above a blender of rapidly stirring isopropanol to prevent oligomer precipitation prior to transferring the oligomer mixture to the blender. The oligomer mixture was added dropwise s xhe blender being operated at a high shear rate over a 75 minute period. A white f-recipitate was formed which was removed from the blender using a spatula and filtered using a msdium porosity fritted funnel and a water aspirator as a vacuum source. The precipitate was dried at 50°C for 8.5 hours in a vacuum oven attached to a vacuum source of less than 30 inches of Hg. The resulting white amorphous glassy material was pulverized using a mortar and pestle thus producing 20.1 g (91.4 percent recovery) of a nontacky white powder. Size exclusion chromatography indicated that the molecular weight distribution (Mn = 1 ,700, Mw = 31 ,000) was changed such that the monomer content was reduced from 12.9 percent to 7.4 percent and the dimer content reduced from 10.7 percent to 9.7 percent. Film retention in this system was 42.7 percent following photon exposure and solvent development procedures described in Example 1. This was in comparison to the film retention of 36.3 percent for the polymer system of Example 6 wherein there was no change of the molecular weight distribution. Example 9 - Comparison of Spray and Immersion Development A series of DVS-BCB oligomeric solutions containing 1-4 percent BAC-M were prepared as described in Example 4. One group was spray developed while the second was immersion developed. The results shown in Table 5 indicate that the two procedures produce similar film thicknesses. Spray development was effected by spraying a stream of Stoddard solvent onto the center of the waf er d u ri ng spi n and spread cycl es of 33 seconds f ol I owed by a spi n cycl e to dry the wafers. Immersion development was effected by swirling the wafers in Stoddard solvent for 60 seconds as described in Example 1 followed by drying the wafers under a nitrogen stream. 0 Example 10 - Effect of Varying The Developing Solution A3.0 percent solution of BAC-M(426.3 mg) in oligomeric DVS-BCB(24.9700 g, 55 percentsolids in mesitylene, 13-7335 g polymer) was prepared by the procedure described in Example 5- Films were prepared from this solution according to the procedure described in 5 Example 1 with the exception that the adhesion promoter in this system wastriethoxyvinyl silane in acetic acid which was prepared as a 0-5 percent solution in deϊonized water. This solution was aged for a minimum of 15 minutes priorto use and can be used for a maximum of 8 hours after preparation- After a thermal cure according to the procedure of Example 6, the film thickness was measured by stylus profilometry relative to a control wafer for each of the 0 developing solutions- The results are shown in Table 6- Table 6 Film Thickness as a Function of Developing Solution Developer Thickness (μm) % Retention Stoddard solvent 1.76 33.1 Mesitylene 1.92 35.6 Xylene 1.68 31.2 0 This data indicates that a variety of materials can be used for solvent development of these films- Optimization of the developing solution was possible by adding nonsolvents such as methanol or isopropanol as a means of slowing the film removal rate, thereby retaining a greater percentage of the initial film thickness- Example 1 1 - Preparation of Photosensitive, Patterned Thin Films From 2,6-bis(4- -azidobenzylidene)-4-Methylcyclohexanone and Oligomeric 3,3'-(ethenyl)bis- -bicyclo(4.2.0)octa-1,3,5-triene A 60 percent solids solution of oligomerized 3,3'-(ethenyl)bis-bicyclo(4.2.0)octa- -1,3,5-triene(9.9722 g total, 5.9833 g polymer, Mn = 600, Mw = 2000) in xylene was combined with 420 mg of 2,6-bis(4-azidobenzylidene)-4-methylcyclohexanone(BAC-M) under amber lights. The solution was shaken for 20 minutes on an Eberbach mixer set on its highest speed. The solution was then heated to 60°C and held at that temperature for 30 minutes thereby producing a homogeneous solution. After cooling to ambient temperature over 30 minutes, additional BAC-M (608.7 mg total, 9.2 percent) was added to the solution which was then heated for an additional 30 minutes at 60°C. The resulting solution, containing some insoluble material, was coated onto substrates using the procedure described in Example 1. The film coated substrates were heated in a nitrogen atmosphere to 120°C and maintained at that temperature for 30 minutes. After a 5 minute cool down period they were immersion- developed for 1 minute in mesitylene. The resulting film coated substrates were cured using -the, thermal cure cycle described in Example 6. Profilometry results indicate that the developed films have step heights of 4.148 μm while the photon-exposed, undeveloped control films have a thickness of 4.147 μm. Example 12 - Preparation of Photosensitive, Patterned Thin Films from 2,6-bis(4- -azidobenzylidene)-4-methylcyclohexanone and an Eqimolar Mixture of Oligomeric 3,3'-(ethenyl)bis-bicyclo(4.2.0)octa-1 , 3, 5-triene and Divinyltetramethyldisiloxane Bisbenzocyclobutane A 55 percent solids solution of oligomerized 3,3'-(ethenyl)bis-bicyclo(4.2.0)octa- 1, 3, 5-triene/divinyltetramethyldisiloxane bisbenzocyclobutane copolymer(EL-BCB/DVS- BCBX9.1922 g total, 5.0557 g polymer) in xylene was combined with 402.5 mg of 2,6-bis(4- -azidobenzylidene)-4-methylcyclohexanone(BAC-M) under amber lights. The solution was shaken for 20 minutes on an Eberbach mixer set on its highest speed. The solution was then heated to 60°C and held at that temperature for 30 minutes thereby producing a homogeneous solution. After cooling to ambient temperature over 30 minutes, additional BAC-M (515.8 mg total, 1 13.3 mg BAC-M, 9.3 percent) was added to the solution which was then heated for an additional 30 minutes at 60°C. The resulting solution, containing some insoluble material, was coated onto substrates using the procedure described in Example 1. The film coated substrates were heated in a nitrogen atmosphere to 120°C and maintained at thattemperature for30 minutes. After a 5 minute cool down period, they were immersion developed for 1 minute in Stoddard solution. The resulting film coated substrates were cured using the hard cure cycle described in Example 6- Profilometry results indicate that the 5 developed films have step heights of 4.135 μm while the photon-exposed, undeveloped control films have a thickness of 5.492 μm. Example 13 - Preparation of Photosensitive, Patterned Thin Films from 2,6-bis(4- -azidobenzylidene)-4-methylcyclohexanone, Oligomeric Divinyltetramethyldisiloxane Bisbenzocyclobutane and Polymerized 10 1,2-dϊhydro-2,2,4-trimethylquinoline Under amber filtered lights BAC-M(174.4 mg, 0.47 mmol, 3.0 weight percent) was added to an amber vial containing a 1 percent solution of polymerized 1,2-dihydro-2,2,4- -trimethylquinoline (PDTQ) in oligomeric DVS-BCB (10.2128 g, 55 percent solution in mesitylene, 5-5614 g polymer, 55.6 mg PDTQ). The mixture was dissolved and processed by the 15 procedure described in Example 10. Stoddard solvent was used as the immersion developerfor 1 minute- A second mixture was prepared using an antioxidant comprising PDTQ modified b aromatization or hydrogenation(PDTQ-M). BAC-M(159.9 mg, 0-43 mmol, 3.1 weight percent) was added to an amber vial containing a 1 percent solution of PDTQ-M in oligomeric 0 DVS-BCB (9.2418 g, 55 percent solution in mesitylene, 5.0327 g polymer, 50.3 mg PDTQ-M). The mixture was processed according to the procedure described for PDTQ. The profilometry results forthese films are shown in Table 8. This data suggests that antioxidants do not drastically affect the film retention of photodefinable mixtures- Example 14- Effect of Photosensitizer 3,3'-Carbonyl bis(7-diethylaminocoumarin) 5 Meta-azidophenyl sulfone (0.4331 g, 300.30 g/mol, 1.44 mmol, 3.0 weight percent) and 3,3'-carbonyl bis(7-diethylaminocoumarin) (0.0730 g, 460.53, 0.16 mmol) were added under amber filtered lights to an amber vial containing a solution of oligomeric DVS- BCB (25.3257g, 55 percent solids in mesitylene, 13.9291 g polymer). The vial was capped and heated in a water bath at 60°C for 1 hour. The bisazide was not completely soluble at this point. The mixture was heated at 60°C for an additional 1/2 hour. The sample was shaken for 1 hour using an Eberbach shaker on a high setting resulting in a homogeneous solution. A 4 inch silicon wafer was spin coated with the solution at a spin speed of 5,000 rpms for 30 seconds. The wafer was softbaked at 80°C for 1/2 hour under nitrogen. Prior to exposure, the wafer was cooled to room temperature. It was exposed to 350 to 450 nm UV light for 15 seconds using a 1 ,000 watt high pressure mercury-xenon arc lamp, and then immersion-developed for 2 minutes using Stoddard solvent. The wafer was then thermally cured (T max = 250°C). After solvent development and cure, profilometry results indicate a film thickness of 4.1 microns. A UV-Vis spectrum of a DVS-BCB solution from 300 nm to 500 nm at a scan rate of 60 nm per minute was very similar to that obtained for a DVS-BCB/bisazide mixture, thus indicating that this bisazide absorbed in the same region as the DVS-BCB, which was at lower wavelength than desired. The significance of these results was that the bisazide (meta-azidophenyl sulfone)/DVS-BCB mixture without photosensitizer was not curable by exposure to 350 to 450 nm U V light, however, when 0.5 percent of photosensitizer was added the sensitivity of the mixture increases significantly. Very similar results were obtained when the 3,3'-carbonyl bis(7- diethylaminocoumarin) photosensitizer was replaced with 3,3'-carbonyl bis(7- -dimethoxycoumarin). Example 15 - Effect OF Precipitating Oligomeric DVS-BCB in Refluxing Alcoholic Solvents Oligomeric DVS-BCB (40.5 g, 60 percent solids in mesitylene, 24.3 g polymer, Mw = 44000, Mn = 1360) was placed in a pressure-equalizing addition funnel connected to a claisen adapter which was inserted into a 3-necked 1000 mL resin kettle containing 700 mL of isopropanol. The resin kettle was equipped with an immersion well to control the solution temperature and a reflux condenser, equipped with a nitrogen outlet, which was connected to the portion of the claisen adapter not directly above the stirring solution. The resin kettle was purged with nitrogen for 15 minutes priorto heating and continuously purged at a slow rate thereafter. The isopropanol was broughtto reflux priorto the addition process. The oligomer was added dropwise over a period of 113 minutes to the solution which was stirred at 300 rpm using a mechanical stirrer equipped with teflon blades at both the bottom and top of the isopropanol solution. After addition was completed, the mixture was stirred for an additional 15 minutes priorto removing the stirring and heating sources. After sitting for 16 hours overnight, the apparatus was disassembled and the mixture filtered. The solids were washed with three 50 mL portions of isopropanol and removed using a spatula. The resin was pulverized using a mortar and pestle to increase the surface area of the solid to facilitate drying. The resin was dried in a vacuum oven at 50°C for 2 hours and then at 90°C for 18 hours to remove any residual isopropanol and consolidate the resin. The resin collapses indicating thatthe polymer's glass transition temperature was 90°C or above- The high molecularweight material recovered weighed 16.4 g (67-5 percent). The soluble components of this separation were concentrated using a rotary evaporator giving 8.1 g of viscous resin for later characterization by size exclusion chromatography- The overall material balance was 16-4 + 8-1 g = 24.5 g (101 percent) indicating that very little isopropanol was left in the low molecular weight component. The resulting change in the molecular eightdistribution was from Mn = 1300, Mw = 40000 to Mn = 4100, Mw = 57000- The polymer was redissolved in mesitylene at 55 percentsolids after heating at 60°C for 1 hour- A 3 weight percent BAC-M formulation was prepared and films produced therefrom by spin coating at 5000 rpm. After immersion development for 1 minute in Stoddard solvent and cure, the film thickness of the patterned film was 7.2 μm (66 percent film retention) with a control film thickness of 10.9 μm compared to the 5 μm coating produced from 55 percent solutions of the unaltered material- Using polymer precipitated in isopropanol results in a nearly complete removal of the monomerϊc and dimeric components of the resin- However, the film loss of approximately 33 percent described above indicated that higher oligomeric materials were responsible for some loss. Therefore, in an effort to remove a greater quantity of the higher molecularweight oligomers, high boiling alcohols are used producing the data in Table 9. Table 9 Polymer Precipitation Results: Characterization of Precipitated B-staged DVS-BCB 20 The most preferred alcohol for precipitating the higher molecular weight oligomeric components of DVS-BCB is t-amyl alcohol (2-methyl 2-butyl), which removes a portion the DVS-BCB trimer. Removing the low molecular weight components results in both greater film retention and greater film thickness atthe same solids concentration. 25 30 35 Example 16 - Effect of Solvent Precipitated DVS-BCB Resin Molecular Weight on Percent Film Retention A 57,000 weight average molecular weight DVS-BCB resin was prepared by the same preparation method as described in Example 15 using isopropyl alcohol as the extraction solvent and was subjected to the same film preparation, solvent development, and analysis as described in Example 1 - 2-methoxyethyl etherwas used as a development solvent for a development time of 90 seconds and the wafers were given an exposure dose of 1 ,000 mJ/cm 2 atthe 365 nm wavelength. The films were spun at a spin speed of 5,000 rpms after a 10 second spread cycle at 500 rpms. The thermal cure cycle was as follows: 50°C for 5 minutes 50°Cto 100°Cover 5 minutes 100°Cfor 15 minutes 100°Cto 150°Cover 15 minutes 150°Cfor 15 minutes 150°C to 250°Cover 60 minutes 250°C for 60 minutes 250°C to 100° over 120 minutes The residual film thickness of this system was 58.8 percent of the control film thickness after development and 60.8 percent after cure. In effort to maximize the film retention after development and cure, other high molecularweight resins that were prepared as described in Example 15 using various alcohols for precipitation. The resins were evaluated producing the data in Table 10. Table 10 Percent Film Retention of Precipitated B-staged DVS-BCB Resins 2ø The most preferred resin for obtaining films with good film retention after development and cure is the resin precipitated in t-amyl alcohol (2-methyl, 2-butyl alcohol) which has a film retention of 86.6 percent after development and 87.5 percent after cure. The higher the weight average and number average molecular weight of the DVS-BCB resin the greater the film retention after development and cure. 2c Example 17 - Effect of Film Thickness on Film Retention Oligomeric DVS-bis-BCB (567.6 g, 56 percent solids in mesitylene, 317.8 g solids was poured into a pressure equalizing addition funnel. The addition funnel was connected to a 5L resin kettle with a bottom drain. T-amyl alcohol (3.5 L, Aldrich, 99percent) was added to the 5L reaction flask. The reactor was purged with nitrogen slowly throughout the remainder n of the procedure. The alcohol was heated to reflux (bp. 102°C) and the polymer solution was added. After the addition was completed, the reactor cooled to 35°C over a period of approximately 3 hours. The homogeneous polymer solution became cloudy at 71°C. A white high density fraction settled to the bottom of the reactor. Subsequently, the viscous white resin was decanted through the stopcock. After the decantation was completed, the material 35 was dried inside a vacuum oven at 1 10°C for 15 h producing 129.8 g (40.8percent) of a white polymer. The procedure was repeated nine additional times and the resultant polymer mixed together to give a masterbatch of material with the following molecular weight distribution: Mn 4800, Mw 95,000 and Mz 295,000- A 3 percent BAC-M formulation was prepared as described in Example 1. Priorto 5 polymer deposition, an adhesion promoter, 3-amϊnopropyltriethoxysilane (3-APS), was applied as a 0.5 percent aqueous solution (w/w) at 5000 rpm. The resin was spin coated on 100 mm silicon wafers using a spread cycle at 500 rpm for 10 seconds in which the polymer solution flowed out to cover the substrate followed by a final spin speed (variable see Table 1 1) which was maintained for 30 seconds. After exposure 10 (1000 mJ/cm2 at 365 nm wavelength), the films were developed using an appropriate solvent- The film thickness was measured after development and after the f i nal cure for developed films- The control film thickness was measured after cure which was preceded by exposure. Table 11: Film Thickness for 3 wt ercent BAC-M DVS- 30 35 Example 18: Thicker Films by Multiple Coatings and Exposures Followed by one Solvent Development Step In an attempt to obtain thicker photopatterned polymer coatings, a multiple photopolymer coating and exposure process was developed. 1.006 grams of an oligomer of 1 ,2-dihydro-2,2,4-trimethylquinoline available as AgeRite MA was added to 199.358 grams of a 50 percent solids DVS-bis-BCB resin (molecular weight of Mn = 4,500 g/mole; Mw = 59,000 g/mole) solution in mesitylene and dissolved with heating at 60°C in a water bath shaker for 1 hour. 3.085 g of BAC-M was added to the solution and dissolved with heating at 60°C in a water bath shaker for 30 minutes. The solution was then filtered through a 0.5 micron filter. A clean silicon wafer with patterned aluminum metal deposited on top of the thermal silicon oxide, was spin coated with a 0.5 percent aqueous solution of 3-aminopropyltriethoxysilane adhesion promoter at a spin speed of 2,500 rpms for 30 seconds. The photodefinable solution was then spin coated using a 10 second spread cycle of 500 rpms followed by a spin speed of 2,500 rpms for 30 seconds to yield a 8.0 micron thick film. The wafer was placed in a nitrogen purged oven at 80°C for 30 minutes. After cooling to room temperature, the wafer was placed in an Oriel mask aligner and the aluminum pattern on the wafer was aligned to the photomask. The photodefinable DVS-bis-BCB film on the wafer was then given an exposure dose of 700 mJ/cm 2 of light measured atthe 365 nm wavelength (broad band source 350-450 nm). A second photodefinable DVS-bis-BCB film was spin coated on the first exposed film at a spin speed of 7,500 rpms to give a film coating thickness of 8.0 microns. The wafer was placed in a nitrogen purged oven at 80°C for 30 minutes. After cooling to room temperature, the wafer was placed in an Oriel mask aligner and the aluminum pattern on the wafer was aligned to the photomask. The second photodefinable film was given an expose dose of 700 mJ/cm 2 measured at the 365 nm wavelength (broad band source 350-450 nm). The wafer was then immersed in 2-methoxy ethyl ether for 90 seconds and sprayed dry with a nitrogen stream. The wafer was placed in a nitrogen purged oven at 80°C for 10 minutes to further dry. The total film thickness for the photodefinable DVS-bis-BCB was measured using a profilometer by draging the profilometer stylus over a via hole patterned into the film. The film thickness after development was approximately 12.23 microns. The film was cured according to the following cure schedule: 50°C for 5 minutes 50°C to 100°C over 5 minutes 100°C for 15 minutes 100°Cto 150°C over 15 minutes 150°C for 15 minutes 150°C to 250°C over 60 minutes 250°C for 60 minutes 250°Cto 100°C over 120 minutes The cured polymerfilm was continuous and of high quality with a film thickness of 12.93 microns. Example 19 Thicker films by use of a DVS-bis-BCB formulation with a mixture of bisazides In an attemptto decrease the optical density and maintain high film retention after development and cure a DVS-bis-BCB formulation with a mixture of bisazides was developed. 0.134 grams of m-azidophenyl sulfone (m-sulfone) was added to 24.040 grams of a 55.6 percentsolids DVS-bis-BCB resin (molecularweight of Mn = 4,500 g/mole; Mw= 59,000 g/mole) solution in mesitylene and dissolved with heating at 60°C in a water bath shaker for 30 minutes. The solution wasthen placed in the sonϊcator for 30 minutes and then back into a water bath shaker at 60°Cfor 30 minutes to help dissolve the m-azidophenyl sulfone. 0.269 grams of BAC-M was added to the solution and dissolved with heating at 60°C in a water bath shaker for 30 minutes- The solution was then placed in the sonicator for 20 minutes and filtered through a 5-0 micron filter into a clean amber bottle- 0.266 grams of BAC-M was added to 23-767 grams of a 55.6 percent solids DVS- bis-BCB resin (molecularweight of Mn =45,00 g/mole; Mw = 59,000 g/mole) solution in mesitylene and dissolved with heating at 60°C in a water bath shaker for 30 minutes. The solution wasthen placed in the sonicator for 20 minutes. Both solutions were formulated at the same time. A clean silicon wafer was spin coated with a 0.5 percent aqueous solution of 3-aminopropyltriethoxysϊlane adhesion promoter at a spin speed of 3,000 rpms of 30 seconds. The 1 percent m-azidophenyl su!fone/2percent BAC-M solution was then spin coated on the wafer using a 10 second spread cycle of 500 rpm followed by a spin speed of 3,000 rpm for 30 seconds to yield a 10.83 micron thick film. The wafer was placed in a nitrogen purged oven at 80°Cfor 30 minutes- After cooling to room temperature, the wafer was placed in an Oriel Mask aligner and the photodefinable DVS-bis-BCB film on the wafer was then given an exposure dose of 1,000 mJ/cm 2 of light, measured atthe 365 nm wavelength, (broad band source 350- 450 nm) through a quartz photomask- The film thickness was measured with a profilometer to be 10-83. The wafer wasthen immersed in 2-methoxy ethyl ether for 90 seconds and sprayed dry with a nitrogen stream- The wafer was placed in a nitrogen purged oven atδOCfor 10 minutes to further dry. After solvent development and drying, the film thickness was 9.22 microns as measured by a profilometer. The film was cured according to the following cure schedule: 50°C for 5 minutes 50°Cto 100°C over 5 minutes 100°C for 15 minutes 100°C to 150°C over 15 minutes 150°C for 15 minutes 150°C to 250°C over 60 minutes 250°C for 60 minutes 250°C to Ϊ00°C over 120 minutes The film thickness after cure was 9.450 microns as determined by a profilometer. In an effort to maximize the film retention and film thickness after development and cure, other wafers were spin coated with the 1 percent m-azidophenyl sulfone/2percent BAC-M solution at various spin speeds. For comparative purposes, the solution with 2 percent BAC-M was also evaluated at the same spin coating conditions. The resins were evaluated for film thickness after each processing step as described above producing the data in Table 12. Table 12 Film Thickness and Percent Film Retention During Processing I rf * -. t I The most preferred resin for obtaining films with good film retention after development and cure is the resin containing 1 percent m-azidophenyl sulfone and 2 percent BAC-M which has a film retention of 85.13percent after development and 87.26 ->ercent after cure for a starting film thickness of 10.83 microns. Example 20 Use of a Bisazide with Extended Conjugation 2,6-Bis[3-(4-azidophenyl)-2-propenylidene]-4]methylcyclohexanone of the structure: ,6-Bis[3-(4-azidophenyl)-2-propenylidene]-4-methylcyclohexanone . (0.110 g, 2 wt percent based on polymer) was added to an ambered vial followed by N-methyl pyrrolidone (2.118 g). The vial was capped and shaken by hand in order to dissolve the -- material. DVS-bis-BCB (10.019 g, 54.5 percent solids, 5.461 g polymer, adjusted percent solids: 45.0, molecular weight: Mn = 4500 g moH, Mw = 59,000 g moM) was added and the mixture was heated at 60°C for 18 min. in a water bath shaker while rotating at 150 rpm. The solution was mixed vigorously be shaking by hand for 1 min. After sonication to remove bubbles for 1 min, a homogeneous solution was obtained. The material was permitted to cool to room -- temperature. Inside the cleanroom, the material was spin coated and processed using conditions similar to Example 20 with the following modifications: 1. A spin speed of 3500 rpm was used. 2. The material was exposed for 1000 mJ/cm2 (measured at 365 nm, 17.9 s) -- followed by development in Stoddard solvent (immersion, 3 min). The film was dried using a stream of nitrogen followed by heating on a hot plate at 80°C for a few minutes to further dry the film. Film thickness was determined after exposure and development or for the control substrate, after bake and exposure. The film thicknesses were also determined after the cure ------ schedule used in Example 19. Film Thickness Results Control After bake and expose: After development 5.15 μm 3-96 μm (77-0percent) After cure After cure 5.59 μm 3.925 μm (70-2percent) Example 21 : n-Butyi n-butyrate was a developing solvent 0.168 grams of 1,2-dihydro 2,2,4-tri methyl quinoline (PDTQ) was added to 33.281 grams of a 50 percentsolids DVS-bis-BCB resin (molecularweightof Mn = 4,500 g/mole; Mw = 59,000 g/mole) solution in mesitylene and dissolved with heating at 60°C in a water bath shaker for 30 minutes- The solution was then filtered through a 5.0 micron filter into a clean amber bottle- 0-463 grams of BAC-M was added to the 30.099 grams of the filtered solution and dissolved with heating at 60°C in a water bath shaker for 30 minutes. A clean silicon wafer was spin coated with a 0.5 percent aqueous solution of 3-aminopropyltriethoxysϊlane adhesion promoter at a spin speed of 3,500 rpms for 30 seconds- The BAC-M solution was then spin coated on the wafer using a 10 second spread cycle of 500 rpm followed by a spin speed of 3,500 rpm for 30 seconds to yield a 6.690 micron thick film. The waferwas placed in a nitrogen purged oven at 80 C C for 30 minutes- After cooling to room temperature, the waferwas placed in an Oriel mask aligner and the photodefinable DVS-bis- BCB film on the waferwas then given an exposure dose of 1 ,000 mJ/cm 2 of light, measured at the 365 nm wavelength, (broad band source 350 to 450 nm) through a quartz photomask. The film thickness was measured with a profilometerto be 6.690 microns. The wafer wasthen immersed in butyl butyrate for 60 seconds and sprayed dry with a nitrogen stream. The wafer was placed in a nitrogen purged oven at80°Cfor 10 minutes to further dry. After solvent development and drying, the film thickness was 5.105 microns as measured by a profilometer. The film was cured according to the following cure schedule: 50°C for 5 minutes 50°Cto 100°C over 5 minutes 100°Cfor 15 minutes 100°Cto 150°C over 15 minutes 150°Cfor 15 minutes 150°Cto 250°C over 60 minutes 250°C for 60 minutes 250°Cto 100°C over 120 minutes The film thickness after cure was 5.170 microns as determined by a profilometer- Example 22: Fabrication of a multiple layer structure consisting of two alternating aluminum and photodefinable DVS-bis-BCB layers 1.006 grams of PDTQ was added to 199.358 grams of a 50 percent sol ids DVS-bis- BCB resin (molecularweight of Mn = 4,500 g/mole; Mw = 59,000 g/mole) solution in mesitylene and dissolved with heating at 60°C in a water bath shaker for 1 hour. 3.085 g of BAC-M was added to the solution and dissolved with heating at 60°C in a water bath shaker for 30 minutes. The solution was then filtered through a 0.5 micron filter into a clean 200 ml amber bottle. A clean silicon wafer with a thermal silicon oxide layer was sputter coated with aluminum metal under typical metal deposition process conditions using a Leybold 560 Box Coater. The aluminum was deposited using a DC Magnetron sputtering in argon at 1500 watts for 60 minutes to yield a metal film of approximately 2.0 microns thick. The aluminum was patterned using Shipley Microposit S 1400-37 positive photoresist. The Microposit S1400-37 photoresist was deposited on top of the aluminum by spin coating using a 3 second spread cycle at 500 rpms followed by a 30 second spin cycle at 2,500 rpm which produced a film thickness of approximately 4.0 microns. The photoresist was placed in a nitrogen purged oven at 100°C or 30 minutes. The wafer was then cooled to room temperature and then placed in a Canon PLA-501 FA Mask Aligner which has a medium pressure Hg lamp as a light source. A photomask was placed on top of the wafer and the photoresist was exposed to the light at 405 nm wavelength for an exposure dose of 47 mJ/cm 2 The exposed positive photoresist was developed using Shipley Microposit 454 Developer (2 percent KOH). The development was done by immersing the substrates in a filtered, circulated developer bath at 18°C for 90 seconds. The patterned film wasthen dump-rinsed in Dl-water and spin-dried. The wafer wasthen flood exposed using the mask aligner light source for 236 mJ/cm 2 at the 405 nm wavelength. The wafer was placed in a nitrogen purged oven at 120°C for 30 minutes. The aluminum metal layer was etched by placing the wafer in an acid bath (48 percent Dl-water, 43 percent phosphoric acid, 4.0 percent acetic acid, and 5.4 percent nitric acid) at 45°C for 15 minutes. The water was then dump-rinsed in Dl-water and spin-rinsed-dried to remove residual acid. The photoresist was stripped off of the substrate by placing the wafer on the spin coater and dynamically rinsing it with acetone, followed by methanol; the wafer was then spun until it was dry. The clean wafer with patterned aluminum metal deposited on top of the thermal silicon oxide, was spin coated with a 0.5 percent aqueous solution of 3-aminopropyltriethoxysilane adhesion promoter at a spin speed of 2,500 rpms for 30 seconds. The photodefinable solution was then spin coated using a 10 second spread cycle of 500 rpms followed by a spin speed of 3,500 rpms for 30 seconds to yield a 6.7 micron thick film. The wafer was placed in a nitrogen purged oven at 80°C for 30 minutes. After cooling to room temperature, the wafer was placed in an Oriel mask aligner and the aluminum pattern on the wafer was aligned to the photomask- The photodefinable DVS-bis-BCB film on the waferwas then given an exposure dose of 700 mJ/cm 2 of light measured atthe 365 nm wavelength (broad band source 350 to 450 nm). The exposed film was developed by immersion into 2-methoxy ethyl ether for 90 seconds and sprayed dry with a nitrogen stream. The wafer was "softcured" at210°Ctn a nitrogen purged oven underthe following conditions: 50°C for 5 minutes 50°Cto 100°C over 5 minutes 100°Cfor 15 minutes 100°Cto 150°C over 15 minutes 150°C for 15 minutes 150°Cto 210°Cover 30 minutes 210°C for 30 minutes 210°Cto 100°Cover 120 minutes The waferwas then oxygen plasma cleaned for 15 minutes, dump-rinsed in Dl-water, and spin- -rinsed dried. Asecond 2.0 micron thick aluminum layer was deposited on top of patterned photodefinable DVS-bis-BCB film and patterned using the same processing conditions as the first metal deposition and patterning. The waferwas then oxygen plasma cleaned for 15 minutes, dϋmp-rinsed in Dl-water, and spin-rinsed dried. The waferwas spin coated with a 0.5 percent aqueous solution of 3- -aminopropyltriethoxysilane adhesion promoter at a spin speed of 2,500 rpms for 30 seconds. Asecond photodefinable DVS-bis-BCB layer was spin coated on the second patterned aluminum layer at a spin speed of 3,500 rpms to give a film coating thickness of 6-7 microns- The wafer was placed in a nitrogen purged oven at 80°C for 30 minutes. After cooling to room temperature, the waferwas placed in an Oriel mask alignerand the aluminum pattern on the waferwas aligned to the photomask- The second photodefinable film was given an exposure dose of 700 mJ/cm 2 measured atthe 365 nm wavelength (broad band source 350 to 450 nm). The wafer was then immersed in 2-methoxy ethyl ether for 90 seconds and sprayed dry with a nitrogen stream. The wafer was placed in a nitrogen purged oven at80°Cfor 10 minutes to further dry. The film on the wafer was cured according to the following cure schedule: SOX for 5 minutes 50°Cto 100°Cover 5 minutes 100°C for 15 minutes 100°C to 150°Cover 15 minutes 150°C for 15 minutes 150°Cto 250°C over 60 minutes 250°C for 60 minutes 250°Cto 100°C over 120 minutes The final multilayered structure was of high quality with good adhesion between the polymer and aluminum layers.

Claims: 1. A photo-curable, organic-soluble mixture comprising at least one oligomerized cyclobutarene as its major component and at least one photosensitive agent in _. an amount sufficient to convert the mixture to an organic-insoluble solid upon exposing the mixture to photon radiation- 2- The mixture of Claim 1 wherein the oligomerized cyclobutarene contains 80 weight percent or more of oligomers of a degree of polymerization of three or more. 3. A photo-cured polymer formed by exposing the mixture of Claim 2 to a 10 curing amount of photon radiation. 4- A photo-cured pattern-coated substrate formed by forming a latent pattern on a thin film of the oligomer of Claim 2 by exposing only a portion the oligomer to a curing amount of photon radiation and then exposing said film to solvent development. 5. A photo- and thermally-cured pattern-coated substrate formed by . j . exposing the photocured pattern-coated substrate of Claim 4 to a thermal cure. 6. The photo- and thermally-cured pattern-coated substrate of Claim 5 wherein the cyclobutarene is divinyltetramethyldisiloxane bisbenzocyclobutane. 7. The photo- and thermally-cured polymer of Claim 6 wherein the photosensitive agent is 2,6-bis(4-azidobenzylidene)-4-methylcyclohexanone. „ 8. The mixture of Claim 1 wherein the photosensitive agent is 2,6-bis(4-azidobenzylidene)-4-methylcydohexanone. 9. The mixture of Claim 1 wherein the photosensitive agent is 2,6-bis[3-(4- azϊdophenyl)-2-propenylidene]-4]methyicyclohexanone- 10. The mixture of Claim 1 wherein the photosensitive agent is a mixture of „ 2,6-bis(4-azidobenzyiϊdene)-4-methylcyclohexanone and m-azidophenyl sulfone- 11- The mixture of Claim 1 containing an antioxidant derived from l,2-dihydro-2,2,4-trimethylquϊnoline- 12. The mixture of Claim 1 containing a photosensitizer- 13. The mixture of Claim 12 wherein the photosensitizer is 3,3'-carbonyl bis(7- diethylaminocoumarin). 14. An electronic device which has dielectric layers produced from the mixture of Claim 1. 15. A process for removing low molecular weight portions of an oligomerized cyclobutarene comprising dissolving the oligomerized cyclobutarene in a solvent and then mixing the resulting solution with a second solvent in which a higher molecular weight fraction of the oligomerized cyclobutarene is precipitated but which the monomer and dimer are soluble. 16. The process of Claim 15 wherein the precipitated oligomerized cyclobutarene is separated from the solvents. 17. The process of Claim 15 wherein the dissolving solvent is a hydrocarbon solvent. 18. The process of Claim 17 wherein the precipitating solvent is an alcohol. 19. The process of Claim 18 wherein the cyclobutarene is divinyltetramethyldisiloxane bisbenzocyclobutane. 20. The process of Claim 19 wherein the dissolving solvent is mesitylene and the precipitating solvent is 2-methyl-2-butanol. 21. An oligomerized cyclobutarene containing 90 weight percent or more of oligomers of a degree of polymerization of three or more. 22. An oligomerized cyclobutarene containing 90 weight percent or more of oligomers of a molecular weight of 1 ,000 or more as determined from peak area percent by GPC, using a refractive index detector, uncorrected for response factors and as measured against polystyrene standards. 23. The oligomerized cyclobutarene of Claim 21 wherein the cyclobutarene is divinyltetramethyldisiloxane bisbenzocyclobutane. 24. The oligomerized cyclobutarene of Claim 22 wherein the cyclobutarene is di vi nyltetramethyldisi loxane bisbenzocycl obutane.

Inventors: HARRIS ROBERT F, MOYER ERIC S, OAKS FRANK L, RUTTER EDWARD W, HARRIS, ROBERT, F., MOYER, ERIC, S., OAKS, FRANK, L., RUTTER, EDWARD, W.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1992
Main classification: C07C
IPC codes: C07C247, C07F7, C08F2, C08F30, C08G61, C08L65, G03F7