Process for preventing consolidation of P-Dichlorobenzene

Abstract: A triethylene glycol derivative is added to p-dichlorobenzene so as to prevent consolidation and improve flowability of p-dichlorobenzene.

Description: BACKGROUND OF THE INVENTION Field of the Invention The invention relates to a process for preventing consolidation and improving flowability of p-dichlorobenzene, and more particularly, to a process for preventing consolidation and improving flowability of p-dichlorobenzene by adding a certain compound thereto. Description of Related Art p-Dichlorobenzene (hereinafter referred to as PDCB) is usually formed into tablet, ball or rod and widely used as a mothball or deodorant for clothing. It is also a useful compound as a raw material for producing some high polymer compounds. PDCB is usually produced by chlorinating benzene, separating p-dichlorobenzene from the chlorination products containing chlorobenzene, o-dichlorobenzene, p-dichlorobenzene and others and purifying the p-dichlorobenzene. Further, the p-dichlorobenzene is taken out in the form of flake, and is directly or after the flakes are formed into particles, shipped to makers for shaping and processing the particles or flakes. Melting point of PDCB is low though it depends on the impurity content, and even the melting point of the pure one is as low as 53°C. Therefore, PDCB products shipped in the form of flake are very liable to consolidate during storing and transportation. When PDCB is shaped and processed, for example, ground and tableted, the flowability and the like are poor and therefore, the processibility is markedly lowered. In order to solve such a problem of consolidation of PDCB, various methods have been tried. As a representative method, it is known to add an additive to prevent the consolidation. For example, Japanese Patent Publication Nos. 10942/1967 and 1006/1967 disclose a method of adding a surface active agent. Japanese Patent Application Laid-open No. 134037/1983 and Japanese Patent Publication No. 34207/1989 disclose a method of adding a volatile silicone oil. However, these methods are not always satisfactory, partly because the vapor pressures of the additives themselves are very low or almost none so that the additives remain after PDCB has sublimed and are liable to stain the cloth, and partly because the actual effect of the additive is not sufficient. As additives for preventing consolidation of PDCB, Japanese Patent Publication No. 4615/1982 discloses benzyl alcohol, Japanese Patent Publication No. 23851/1983 diethylene glycol derivatives, and Japanese Patent Publication No. 11406/1983 both benzyl alcohol and diethylene glycol derivatives at a certain ratio. Among these proposed methods, a method of adding only benzyl alcohol does not sufficiently prevent the consolidation, and a method of adding only diethylene glycol derivatives can markedly prevent the consolidation, but the resulting shaped articles such as tablets are fragile as described in Japanese Patent Publication No. 11406/1983 and therefore, said derivatives alone can not be used as additives. For the purpose of retaining the hardness of the shaped articles and further preventing the consolidation, both a diethylene glycol derivative and benzyl alcohol should be used in combination. Such a method as above is not always preferable since two types of additives should be used. SUMMARY OF THE INVENTION An object of the present invention is to provide a process for preventing consolidation of PDCB. Another object of the present invention is to provide a process for improving flowability of PDCB after ground. A further object of the present invention is to provide a process for retaining a sufficient hardness of shaped articles of PDCB together with attaining at least one object as mentioned above. Still another object of the present invention is to provide a process for preventing consolidation of PDCB and nothing remaining after PDCB has been sublimed. A still further object of the present invention is to provide PDCB having at least one of the improved effects which least long. According to the present invention, there is provided a process for preventing consolidation and improving flowability of p-dichlorobenzene which comprises adding to p-dichlorobenzene a triethylene glycol derivative of the general formula (1), R¹OCH₂CH₂OCH₂CH₂OCH₂CH₂OR² (1) where R¹ and R² are independently selected from the group consisting of hydrogen atom, aliphatic alkyl group having 1 - 10 carbon atoms and aliphatic alkyl carbonyl group having 1 - 10 carbon atoms. DESCRIPTION OF THE PREFERRED EMBODIMENTS Exemplary suitable triethylene glycol derivatives are: triethylene glycol, triethylene glycol monomethyl ether, triethylene glycol monoethyl ether, triethylene glycol monopropyl ether, triethylene glycol monobutyl ether, triethylene glycol monopentyl ether, triethylene glycol monohexyl ether, triethylene glycol monoheptyl ether, triethylene glycol monooctyl ether triethylene glycol monononyl ether, triethylene glycol monodecyl ether, triethylene glycol dimethyl ether, triethylene glycol diethyl ether, triethylene glycol dipropyl ether triethylene glycol dipentyl ether, triethylene glycol dihexyl ether, triethylene glycol diheptyl ether, triethylene glycol dioctyl ether, triethylene glycol dinonyl ether, triethylene glycol didecyl ether triethylene glycol monoacetate, triethylene glycol monopropionate, triethylene glycol monobutyrate, triethylene glycol monopentanoate, triethylene glycol monohexanoate, triethylene glycol monoheptanoate, triethylene glycol monooctanoate, triethylene glycol monononanoate, triethylene glycol monodecanoate, triethylene glycol diacetate, triethylene glycol dipropionate, triethylene glycol dibutyrate, triethylene glycol dipentanoate, triethylene glycol dihexanoate, triethylene glycol diheptanoate, triethylene glycol dioctanoate, triethylene glycol dinonanoate, and triethylene glycol didecanoate. Among these compounds, triethylene glycol or triethylene glycol diacetate exhibits a very excellent effect. These additives are usually used alone, but may be naturally used in combination. When the amount of the additive is too little, the effect is lowered. On the contrary, when the amount is too much, the additive undesirably exudes from the product. Therefore, the amount of the additive is usually used in an amount of 0.005 - 0.5 % by weight, preferably in an amount of 0.01 - 0.3 % by weight based on the weight of PDCB. When the additive is used in an amount of the abovementioned range, various characteristics such as anticonsolidation and the like of PDCB can be improved to a great extent, and further the hardness of the shaped articles such as tablets and the like can be sufficiently retained. In addition, these additives neither remain after PDCB has sublimed, nor stain cloth, and therefore, the additives are very excellent. According to the present invention, PDCB may be treated with the additive, for example, by adding the additive to a molten PDCB in a prescribed amount before taking the PDCB in the form of flakes and crystallizing the PDCB as flake-like crystals by means of a flaker or the like, or by spraying a prescribed amount of the additive to the PDCB product not containing an additive. Or, when PDCB product is taken out by means of recrystallization, the additive may be added to a solvent for recrystallization and then the solution is cooled to separate the PDCB. In the case of diethylene glycol derivatives in prior art, for example, when 0.1 % of diethylene glycol dibutyl ether is added to PDCB, the consolidation force of the resulting PDCB is 1/5 times that of PDCB not containing the additive, but the hardness of the shaped article (e.g. tablets) is also decreased to 1/5. The hardness of tablets can be retained at the substantially same level as that of PDCB not containing an additive by combining the diethylene glycol derivative with benzyl alcohol as disclosed in Japanese Patent Publication No. 11406/1983. On the contrary, when, for example, triethylene glycol diacetate is added in an amount of 0.1 % based on PDCB, the consolidation force is decreased to 1/5 times that of PDCB not containing an additive or less, and further, when formed into tablets, the hardness of PDCB is not so lowered and is substantially the same as that of PDCB article containing no additive. According to the present invention, consolidation of PDCB can be prevented and flowability of PDCB after ground can be improved by the particular triethylene glycol derivative as an additive. And such desirable effects are durable for a long period of time, and even when only a small ammount of the additive is used, the effects are durable. In addition, shaped articles of PDCB retain a sufficient hardness. After sublimation of PDCB, nothing remains, that is, the additive does not stain, for example, cloth. In the following, the present invention is explained referring to examples. In the examples, various tests are as shown below. 1. Preparation of flake product PDCB was melted at 60°C, and a prescribed amount of the additive was dissolved therein and then gradually poured into a stainless steel vat cooled to 10°C in advance. After crystallization, the PDCB was peeled off and formed into flakes. 2. Consolidation force Two cylinders made of a resinous material, each having an inner diameter of 5 cm were prepared. One cylinder (lower cylinder) placed vertically on a flat plate such that one end of the cylinder closely contacts the flat surface. The other cylinder (upper cylinder) was put on the lower cylinder such that the upper end portion of the lower cylinder consists with the lower end portion of the upper cylinder. The inner hollow portion thus formed by the combined two cylinders was filled with ground PDCB having a particle size of 12-20 mesh prepared by grinding PDCB with an automatic mortar followed by screening. Then a load of 1 kg was applied from the top and after the PDCB was allowed to stand for 15 hours, the load was removed . The lower cylinder is fixed to the flat surface, and the upper cylinder was pulled horizontally and the force required for beginning of movement was defined as the consolidation force. 3. Grinding test In an automatic mortar was placed 100 g of PDCB flakes and ground for 5 min., and then the ground particles was discharged by inclining the mortar. The manner in which the particles were discharged was designated as shown below: o ○ : The total amount of the particles was easily discharged only by inclining the mortar. ○ : About 80 % of the amount of the particles was easily discharged, but about 20 % or less remained in the mortar, but remaining amount was wholly discharge by tapping the mortar. ▵ : About 50 % of the amount of the particles was discharged only by inclining the mortar. X : Only 20 % or less of the amount of the particles was discharge by inclining the mortar and a large amount of the particles attached to the mortar. 4. Tablet hardness Various types of PDCB were ground and shaped into tablets of a drum type of 20 mm in diameter and about 9 mm in the central thickness by a molding machine (tableting machine). Then the tablets thus shaped were placed horizontally on a metal plate and a metal ball of 13 g in weight was dropped from various heights through a resin pipe by free falling, and the degree of cracking was examined. The evaluation was as shown below. ○ : No crack was formed though the portion hit by the falling metal ball was depressed somewhat. ▵ : Crack was formed at the upper surface of a tablet, but did not reach the back surface of the tablet. X : Crack reached the back surface. XX : A tablet was completely split. With respect to the hardness of tablet, a hardness testing machine was separately used to measure the actual hardness. EXAMPLES 1 -13 and COMPARATIVE EXAMPLE 1 Various triethylene glycol derivatives were added to PDCB in an amount of 0.1 % based on the weight of PDCB to prepare flake products of PDCB. The results of consolidation force test and grinding test are shown in Table 1. Additive Consolidation force(g) Grinding test Example 1 Triethylene glycol 225 o ○ Example 2 Triethylene glycol diethyl ether 290 ○ Example 3 Triethylene glycol di-n-butyl ether 275 ○ Example 4 Triethylene glycol di-n-decyl ether 260 ○ Example 5 Triethylene glycol mono-ethyl ether 230 ○ Example 6 Triethylene glycol mono-n-butyl ether 235 ○ Example 7 Triethylene glycol mono-n-hexyl ether 255 ○ Example 8 Triethylene glycol mono-acetate 240 ○ Example 9 Triethylene glycol mono-n-propionate 255 ○ Example 10 Triethylene glycol mono-n-butyl ether acetate 230 ○ Example 11 Triethylene glycol mono-n-ethyl ether acetate 245 ○ Example 12 Triethylene glycol diacetate 210 o ○ Example 13 Triethylene glycol di-propionate 290 ○ Comparative Example 1 Not added 1,070 X EXAMPLES 14 - 19 and COMPARATIVE EXAMPLES 2 - 3 The amounts of triethylene glycol or triethylene glycol diacetate added were changed to prepare PDCB flake products. Table 2 shows the test results of the flake products as to various characteristics. In addition, for comparison, PDCB flake product containing no additive and PDCB flake product containing diethylene glycol monobutyl ether acetate disclosed in Japanese Patent Publication No. 23851/1983 were also tested. Example 20, Comparative Example 4 - 5 Triethylene glycol diacetate was added to PDCB in an amount of 0.1% by weight based on PDCB to prepare a PDCB flake product. In a similar manner to above, diethylene glycol monobutyl ether acetate disclosed in Japanese Patent Publication No. 23851/1983 was added to PDCB in the same amount (% by weight) as above to prepare a PDCB flake product. In a similar manner to above, diethylene glycol monobutyl ether acetate and benzyl alcohol disclosed in Japanese Patent Publication No. 11406/1983 were added to PDCB in the same amount (% by weight) as above to prepare a PDCB flake product. The each flake product containing an additive was ground with a mortar and screened to form the particles of 12-20 mesh. The change of consolidation force with time of the products thus ground and screened was investigated according to the method of measurig consolidation force by changing the period of time during which a load was applied thereto. The result is shown in Table 3.

Claims: A process for preventing consolidation and improving flowability of p-dichlorobenzene which comprises adding to p-dichlorobenzene a triethylene glycol derivative of general formula (1), R¹OCH₂CH₂OCH₂CH₂OCH₂CH₂OR² (1) where R¹ and R² are independently selected from the group consisting of hydrogen atom, aliphatic alkyl group having 1 - 10 carbon atoms and aliphatic alkyl carbonyl group having 1 - 10 carbon atoms. The process according to claim 1 in which the triethylene glycol derivative is triethylene glycol or triethylene glycol diacetate. The process according to claim 1 in which the triethylene glycol derivative is added in an amount of 0.005 - 0.5 % by weight based on the weight of p-dichlorobenzene.

Inventors: MITA RYUICHI, NAGATAKE YOSIRO, SHIMUTA NOBUO, TAJIRI TOYOHIRO, UEDA MAMORU, MITA, RYUICHI, NAGATAKE, YOSIRO, SHIMUTA, NOBUO, TAJIRI, TOYOHIRO, UEDA, MAMORU
Applicants: MITSUI TOATSU CHEMICALS, MITSUI TOATSU CHEMICALS, INC.
Application year: 1992
Main classification: C07C17
IPC codes: C07C17