METHOD FOR REGENERATING CERTAIN ACIDIC HYDROCARBON CONVERSION CATALYSTS BY SOLVENT EXTRACTION

Abstract: This invention is a process for the regeneration of solid acidic hydrocarbon conversion catalysts, but particularly certain transition aluminas and zeolites promoted with Lewis acids (preferably BF3) which have been used in the alkylation of isoparaffins with olefins. The process involves the removal of some portion of the reaction product residue adhering to the solid catalyst by contact with a solvent to partially recover the catalyst's initial activity.

Description: METHOD FOR REGENERATING CERTAIN ACIDIC HYDROCARBON CONVERSION CATALYSTS BY SOLVENT EXTRACTION (PA-0084) RELATED APPLICATIONS This is a continuation-in-part of U.S. Patent Application Nos. 07/588,448 to Cooper ____§_■ entitled "ISOPARAFFIN ALKYLATION USING LEWIS ACID PROMOTED TRANSITION ALUMINA CATALYST (PA-0017)" fil September 26, 1990; 07/697,318 to Cooper .§t_a!. entitled "ISOPARAFFIN ALKYLATION USING A LEWIS ACID PROMOTED TRANSITION ALUMINA CATALYST (PA-0060)" filed May 7, 1991 ; and 07/697,320 to Cooper ______[• entitled "LEWIS ACID PROMOTED TRANSITION ALUMINA CATALYSTS SUITABLE FOR ISOPARAFFIN ALKYLATION (PA-0051)" filed May 7, 1991 ; entirety of which are incorporated by reference. This application is also related to U.S. Patent Application No. 07/718,394 to Rao et al entitled "A METHOD FOR REGENERATING LEWIS ACID-PROMOTED TRANSITION ALUMINA CATALYSTS USED FOR ISOPARAFFIN ALKYLATION BY CALCINATION (PA-0061)" filed June 20, 1991 ; the entirety of which is incorporated by reference. FIELD OF THE INVENTION This invention is a process for the regeneration of solid acidic hydrocarbon conversion catalysts, but particularly certain transition alumina and zeolites promoted with Lewis acids (preferably BF g ) which have been used in the alkylation of isoparaffin with olefins. The process involves the removal of some portion of the reaction product residue adhering to the so catalyst by contact with a solvent to partially recover the catalyst's initial activity. BACKGROUND OF THE INVENTION There are a wide variety of hydrocarbon conversion processes usin strongly acidic solid acid catalysts at temperatures low enough to maintain reaction medium in a liquid phase. These processes include oligomerizati alkylation, isomerizatioπ, hydroisomer ' ization, etc. The catalysts for these processes include such disparate acidic materials as acidic zeolites, alumi silica-alumina, silica, boron oxides, phosphorus oxides, titanium oxide, zirconium oxide, chromia, zinc oxide, magnesia, calcium oxide, siiica-alumi zirconia, chromia-alumiπa, alumina-boria, silica-zirconia,aluminum phosphat molecular sieves, silicoaluminophosphate molecular sieves, solid polymeric exchange resins, tetravalent metal phosphonates with pendent acid groups sulfated metal oxides (such as alumina), and the like. These catalysts may treated with or compiexed with Lewis acids. A side reaction in many of th processes produces what appears to be a low level polymer or oligomer. Unlike many higher temperature processes, the side products are not coke like in nature. These poorly characterized side reaction products, or "gunk" may be at least partially removed using solvent extraction procedures and carefully chosen solvents. One process, with its concomitant catalyst, to which solvent extraction is especially applicable is isoparaffin/olefin alkylatio using solid acid catalysts particularly zeolites or aluminas which have been treated with Lewis acids. The preparation of high octane blending components for motor fuels using strong acid alkylation processes (notably where the acid is hydrofluori acid or sulfuric acid) is well-known. Alkylation is the reaction in which an al group is added to an organic molecule (typically an aromatic or olefin). For production of gasoline blending stocks, the reaction is between an isoparaffi and an olefin. Alkylation processes have been in wide use since World War when high octane gasolines were needed to satisfy demands from high compression ratio or supercharged aircraft engines. The early alkylation uni were built in conjunction with fluid catalytic cracking units to take advantage the light end by-products of the cracking units: isoparaffins and olefins. Fluidized catalytic cracking units still constitute the major source of feedstoc for gasoline alkylation units. In spite of the mature state of strong acid alkylation technology, existing problems with the hydrofluoric and sulfuric aci technologies continue to be severe: disposal of the used acid, unintentional emission of the acids during use or storage, substantial corrosivlty of the catalyst systems, and other environmental concerns. Although a practical alkylation process using solid acid catalysts ha little or no corrosive components has long been a goal, commercially viabl processes do not exist. The open literature shows several systems used to alkylate various hydrocarbon feedstocks. The American Oil Company obtained a series of patents in the mid- 1950's on alkylation processes involving C 2 -C 12 (preferably C 2 or G j ) olefin and C 4 -C 8 isoparaffins. The catalysts used were BF 3 -treated solids and th catalyst system (as used in the alkylation process) also contained free BF 3 summary of those patents is found in the following list: Patent No. Inventor BF j -Treated Catalyst* fwith free B 2,804,491 Kelly et al. Si0 2 stabilized Al 2 0 3 (10%-60% by weight BF g ) 2,824,146 Kelly et al. metal pyrophosphate hydrate 2,824,150 Knight et al. metal sulfate hydrate 2,824,151 Kelly et al. metal stannate hydrate 2,824,152 Kniαht et al. metal silicate hydrate 2,824,153 Kelly et al. metal orthophosphate hydrate 2,824,154 Knight et al. metal tripolyphosphate hydrate 2,824,155 Knight et al. metal pyroarsenate hydrate 2,824,156 Kelly et al. Co or Mg arsenate hydrate 2,824,157 Knight et al. Co, Al, or Ni borate hydrate 2,824,158 Kelly et al. metal pyroantimonate hydrate salt 2,824,159 Kelly et al. Co or Fe molybdate hydrate 2,824,160 Knight et al. Al, Co, or Ni tungstate hydrate 2,824,161 Kniαht et al. borotungstic acid hydrate or Ni or borotungstate hydrate 2,824,162 Knight et al. phosphomolybdic acid hydrate 2,945,907 Knight et al. solid gel alumina (5%-100% by wei of Zn or Cu fluoborate, preferably anhydrous) "may be supported on Al 2 0 3 None of these disclose a process for regenerating an alkylation catalyst usi a solvent extraction process for regenerating the catalyst. Acid catalysts used to oligomerize olefins are known. U.S. Patent 2,748,090 to Watkins suggests the use of a catalyst made up of a Group metal (preferably nickel), a phosphoric acid (preferably containing phosph pentoxide), placed on an alumina adsorbent, and pretreated with BF 3 . Alkylation of aromatics is suggested. U.S. Patent No. 2,976,338 to Thomas suggests a polymerization catalyst comprising a complex of BF 3 or H 3 P0 4 optionally on an adsorbent (such as activated carbon) or a molecular sieve optionally containing potassium acid fluoride. Certain references suggest the use of alumina-containing catalysts f alkylation of aromatic compounds. U.S. Patent No. 3,068,301 to Hervert et suggests a catalyst for alkylating aromatics using "olefin-acting compounds The catalyst is a solid, silica-stabilized alumina up to 10% Si0 2 , ail of which has been modified with up to 100% by of weight BF 3 . Other BF 3 -treated aluminas are known. For instance, U.S. Patent N 3,114,785 to Hervert et al. suggests the use of a BF 3 -modified, substantiall anhydrous alumina to shift the double bond of 1-butene to produce 2-bute The preferred alumina is substantially anhydrous gamma-alumina, eta-alumi or theta-alumina. The various aluminas will adsorb or complex with up to about 19% by weight fluorine depending upon the type of alumina and the temperature of treatment. In U.S. Patent No. 4,407,731 to Imai a high surface area metal oxide such as alumina (particularly gamma-alumina, eta-alumina, theta-alumina, silica, or a silica-alumina) is used as a base or support for BF 3 . The BF 3 treated metal oxide is used for generic oligomerizatioπ and alkylation reactions. The metal oxide is treated in a complicated fashion prior to bein treated with BF 3 . The first step entails treating the metal oxide with an acid solution and with a basic aqueous solution. The support is washed with an aqueous decomposable salt such as ammonium nitrate. The support is washed using deionized H 2 0 until the wash water shows no alkali or alkalin earth metal cations in the filtrate. The support is dried and calcined. The disclosure suggests generically that BF 3 is then introduced to the treated metal oxide support. The examples show introduction of the BF 3 at elevat temperatures, e.g. 300'C or 350 * C. Similarly, U.S. Patent No. 4,427,791 to Miale et al. suggests the enhancement of the acid catalytic activity of inorganic oxide materials (suc alumina or gallia) by contacting the material with ammonium fluoride or bo fluoride, contacting the treated inorganic oxide with an aqueous ammoniu hydroxide or salt solution, and calcining the resulting material. The inorga oxides treated in this way are said to exhibit enhanced Brόnsted acidity an therefore, is said to have improved acid activity towards the catalysis of numerous and several reactions (such as alkylation and isomerization of various hydrocarbon compounds). A specific suggested use for the treate inorganic oxide is as a matrix or support for various zeolite materials ultima used in acid catalyzed organic compound conversion processes. U.S. Patent No. 4,751,341 to Rodewald shows a process for treatin ZSM-5 type zeolite with BF 3 to reduce its pore size, enhance its shape selectivity, and increase its activity towards the reaction of oligomerizing olefins. The patent also suggests using these materials for alkylation of aromatic compounds. Certain Soviet publications suggest the use of Al 2 0 3 catalysts for alkylation processes. Benzene alkylation using those catalysts (with 3 pp 5 ppm water and periodic additions of BF^ is shown in Yagubov, Kh. M. e al.. Azerb. Khim. Zh„ 1984, (5) p. 58. Similarly, Kozorezov, Yu and Levitski E.A., Zh. Print. Khim. (Leningrad 1 !. 1984, 57 (12), p. 2681, show the use of alumina which has been treated at relatively high temperatures and modifie with BF 3 at 100 * C. There are no indications that BF 3 is maintained in exce Isobutane alkylation using Al 2 0 3 /BF 3 catalysts is suggested in Neftekhimiv 1977, L (3), p. 396; 1979, 19 (3), P. 385. The olefin is ethylene. There is indication that BF 3 is maintained in excess during the reaction. The crystall form of the alumina is not described nor is any method suggested for regeneration of the catalysts. U.S. Patent No. 4,918,255 to Chou et al. suggests a process for the alkylation of isoparafflns and olefins using a composite described as "comprising a Lewis acid and a large pore zeolite and/or a non-zeol ' itic inorganic oxide * . The process disclosed requires isomerization of the olefin feed to reduce substantially the content of alpha-olefin and further suggests that water addition to the alkylation process improves the operation of the process. U.S. Patent No. 4,992,616 to Chou et al. deals with the process note above for alkylation of isoparaffins and olefins using a composite described "comprising a Lewis acid and a large pore zeolite" but requires addition of water for improving the operation of the process. The best Research Octan Number (RON) product shown in the examples and made using the disclos invention is 86.0 (Table 2). Similarly, PCT published applications WO 90/00533 and 90/00534 (which are based in part on the U.S. patent to Chou et al. noted above) suggest the same process as does Chou et al. WO 90/00534 is specific to process using boron trifluoride-treated inorganic oxides including "alumina, silica, boria, oxides of phosphorus, titanium oxide, zirconium oxide, chromia, zinc oxide, magnesia, calcium oxide, silica-alumina-zirconia, chromia-alumina alumina-boria, silica-zirconia, and the various naturally occurring inorganic oxides of various states of purity such as bauxite, clay and diatomaceous earth". Of special note is the statement that the "preferred inorganic oxides are amorphous silicon dioxide and aluminum oxide". The examples show th use of amorphous silica (and BF^ to produce alkylates having an RON of n greater than 94. U.S. Pat. Number 4,935,577 to Huss, Jr. et al. teaches a process for the catalytic distillation of various hydrocarbons by e.g., alkylatio or oligomerization, using a catalyst "consisting essentially of a Lewis acid promoted inorganic oxide." The inorganic oxide may be selected from the non-zeolitic materials discussed above with regard to the Chou et al. published PCT applications. Additionally, the inorganic oxide may be a large pore crystalline molecular sieve. There are a variety of disclosed ways to regenerate catalysts used in alkylation processes or using Lewis acids. Typical of such processes are th following. U.S. Patent No. 3,647,916, to Caesar et al. shows a process for isoparaffin-olefin alkylation using crystalline zeolite catalysts at low isoparaffi to olefin ratios. The zeolite is first steamed to reduce the number of acid sit and so reduce the amount of olefin polymerization which occurs. The isoparaffin is added to the catalyst before the olefin is introduced to further limit the amount of polymerization. There is no discussion of the use of auxiliary Lewis acids in conjunction with the zeolites. Nevertheless, the catalysts are susceptible to deactivation due to the "accumulation in the por thereof of olefin polymerization products". The regeneration is carried out b burning the surface residue "in an oxygen-containing atmosphere at an elevated temperature in the range of about 800 to 1400 * F" followed by a st in which the catalyst is contacted with an aromatic or polar solvent. U.S. Patent No. 3,833,679 to Gardner et al. shows a paraffin isomerization process using an HSbF 6 catalyst supported on a fiuorided alumina. The catalyst was regenerated by introduction of an HF stream sufficient to convert to any SbF 5 to HSbF 6 . No mention is made of removal any hydrocarbonaceous materials from the catalyst using this treatment. U.S. Patent No. 3,893,942 to Yang also shows a process for isoparaffin-olefin alkylation using crystalline zeolite catalysts. A small amoun of a hydrogenation catalyst (Group VIII metal) is included in the zeolite. Hydrogen gas is periodically introduced into the zeolite (apparently after the catalyst has been partially deactivated) and restores the activity of the cataly Yang indicates that the nature of the chemical reaction between the hydrocarbonaceous deposit and the hydrogen is not clear but hydrogen is consumed and the alkylation activity is restored. This procedure is said to avoid "refractory coke deposits" formed when using high temperature inert gas regeneration treatments. Oxidative treatments are then said to be necessary. A paraffinic wash is desirably first applied to the catalyst to assi in the following hydrogenation step. U.S. Patent No. 3,855,343 to Huang et al. teaches an isoparaffin-olefi alkylation process in which the catalyst is a combination of a macroreticular acid cation exchange resin and boron trifluoride. The boron trifluoride is present in an amount in excess of that needed to saturate the resin. This catalyst is said to "age" and after some period of time must be regenerate The catalyst is regenerated by solvent extraction with a polar solvent, preferably a low molecular weight alcohol. The process disclosed in U.S. Patent No. 4,058,575 to Cahn et al. i method of converting hydrocarbons, e.g., by alkylating them, in the prese of a Lewis acid and a strong Brόnsted acid. Partially deactivated catalytic materials are pretreated with a hydrocarbon to remove contaminants and deactivated catalyst species. The U.S. Patent No. 4,308,414 to Madgavkar shows a process for oligomerizing longer alpha-olefins using a paniculate adsorbent (preferably SiOg) and adsorbed boron trifluoride and water. The catalyst is regenerate by the procedure of adding a small amount of water with the feed olefin. The U.S.- Patent Nos. 4,914,256 and 4,992,614 to Rodewald suggest the reactivation of catalysts (particularly supported boron trifluoride-containi alkylation catalysts) used in a variety of hydrocarbon conversion catalysts application of ultrasonic energy to the partially deactivated catalyst. The process is said to eliminate the need for separation of the catalyst from the feedstock nor to subject the catalyst to a "burn-off operation. One disclosure showing the use of S0 2 to regenerate catalysts is Seapan et al. "Decoking and Regeneration of a Hydrotreating Catalyst by Supercritical Extraction", ACS Symposium Series 411, American Chemical Society, Washington, D.C., 1989. This disclosure shows the use of S0 2 (a other solvents) at pressures above their critical pressures to remove coke- type carbon species from hydrotreating catalysts. The use of S0 2 above 1 psig is shown. The disclosure does not suggest the treatment of any catalysts which have non-coke residue. These disclosures do not show the use of our liquid solvent extractio process to revive acidic catalysts having non-coke residue and especially those which are promoted with a Lewis acid (preferably BF g ) and which hav been used in the alkylation of isoparaffin with olefins. SUMMARY OF THE INVENTION This invention is a solvent extraction process for the regeneration of solid acidic hydrocarbon conversion catalysts but particularly those acidic catalysts such as aluminas or zeolites which have been promoted with Lewi acids (preferably BFg) and used in the alkylation of isoparaffins with olefins. The process involves contacting the solid acidic catalyst with a liquid soluti comprising a solvent selected from S0 2 ; oxygenates such as C^C. alcohol ketones, and aldehydes; nitriles such as acetonitrile; and phenolics such as anisole and phenol. When the solid acidic catalyst additionally comprises a Lewis acid the process involves contacting the combination catalyst with a liquid solution comprising a solvent selected from S0 2 or from aromatic eth and phenolics such as anisole and phenol. The catalysts for these processes include such disparate acidic materials as acidic zeolites, alumina, silica-alumina, silica, boron oxides, phosphorus oxides, titanium oxide, zirconium oxide, chromia, zinc oxide, magnesia, calcium oxide, silica-alumina-zirconia, chromia-alumina, alumina- boria, silica-zirconia, aluminum phosphate molecular sieves, silicoaluminophosphate molecular sieves, solid polymeric ion exchange resi tetravalent metal phosphonates with pendent acid groups, sulfated metal oxides (such as alumina), and the like. These catalysts may be treated with or compiexed with Lewis acids. They are all acidic in their functionality as hydrocarbon conversion catalysts. The alkylation process in which certain of the candidate catalysts are used produces alkylates suitable for use as very high octane, non-aromatic blending components in motor fuels. The alkylates are produced from olefi and isoparaffins. The catalyst used comprises one or more transitional aluminas which are treated with at least one Lewis acid, preferably BF 3 . Th process optimally utilizes an amount of free Lewis acid and produces high octane alkylate. The regeneration process includes the steps of separating the solid component from the liquid reaction medium (but preferably maintaining it in the substantial absence of oxygen and water) and contacting the solid with excess of the liquid solvent. The catalyst may be heated at a lower temperature prior to the solvent contact step so to volatilize certain hydrocarbons and to recover any compiexed Lewis acid or may be washe with an inert solvent such as isobutane or other branched alkane. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a graph of the results of the regeneration procedure of t invention as practiced in Example 1 upon an alumina-based alkylation catal over several liquid S0 2 regeneration cycles. Figure 2 is an 11 B NMR graph of the catalyst used in Example 1 following several regeneration cycles. DESCRIPTION OF THE INVENTION This invention is a solvent extraction process for the regeneration of solid acidic hydrocarbon conversion catalysts but particularly those acidic catalysts such as aluminas or zeolites which have been promoted with Lewi acids (preferably BF 3 ) and used in the alkylation of isoparaffins with olefins. The process involves contacting the solid acidic catalyst (which does not contain a significant Lewis acid component) with a liquid solution comprisin solvent selected from S0 2 ; oxygenates such as 0,-0 4 alcohols, ketones, an aldehydes; nitriles such as acetoni rile; and phenolics such as anisole and phenol. When the solid acidic catalyst additionally comprises a Lewis acid, the process involves contacting the combination catalyst with a liquid soluti comprising a solvent selected from S0 2 or from aromatic ethers and phenol such as anisole and phenol. The solid acid catalysts suitable for regeneration using these process include such disparate acidic materials as acidic zeolites, alumina, silica- alumina, silica, boron oxides, phosphorus oxides, titanium oxide, zirconium oxide, chromia, zinc oxide, magnesia, calcium oxide, silica-alumiπa-zirconia, chromia-alumina, alumina-boria, silica-zirconia, aluminum phosphate molecul sieves, silicoaluminophosphate molecular sieves, solid polymeric ion exchan resins, tetravalent metal phosphates with pendent acid groups, sulfated met oxides (such as alumina), and the like. In particular, the zeolites are preferably large pore zeolitic materials such as zeolite L, zeolite X, zeolite ZSM-4, ZSM-5, ZSM-11, ZSM-12, zeolite β, zeolite Ω, mordenite, and faujasi The zeolites must be acidic but may be natural, synthetic, or may have framework substitutions of other metals. These catalysts may be treated or compiexed with Lewis acids. They are all acidic in their functionality as hydrocarbon conversion catalysts. The preferred catalyst system for this regeneration process compris certain transition aluminas which have been treated with one or more Lewi acids in combination with a minor amount of free Lewis acid. The alumina catalyst component is made by contacting free Lewis acid with certain transition alumina substrates. The Alumina Catalyst Component The preferred alumina catalyst component comprises or consists essentially of a major amount of transition aluminas (preferably eta- or gamma-alumina) which has been treated with a Lewis acid, preferably BF 3 . The catalyst component is acidic in nature and contains substantially no metals (except, of course, aluminum and the semi-metal boron) in catalytic amounts except as may be present in trace amounts in the BF 3 or alumina. Alumina Aluminum oxide (alumina) occurs abundantly in nature, usually in th form of a hydroxide in the mineral bauxite, along with other oxidic impuritie such as Ti0 2 , Fe 2 0 3 , and Si0 2 . The Bayer process is used to produce a reasonably pure Al 2 0 3 having a minor amount of Na^. The Bayer proces Al 2 0 3 is further treated to produce a variety of alumina hydroxides: The aluminum hydroxides may then be treated by heating to produ various activated or transition aluminas. For instance, the aluminum hydro known as boehmite may be heated to form a sequence of transition phas aluminas: gamma, delta, theta, and finally, alpha (see Wefers et al.. Oxid and Hydroxides of Alumina", Technical Paper No. 19, Aluminum Company America, Pittsburgh, PA, 1972, pp.1-51). Transition aluminas (and their crystalline forms) include: Activated aluminas and aluminum hydroxides are used in various chemical processes as catalyst and adsorbents. The aluminas suitable for use in thi process include the noted transition aluminas: gamma, delta, eta, theta, ch kappa, or lambda. Especially preferred are gamma- and eta-aluminas. Mixtures of the two are also desirable. Since it is difficult to produce a substantially pure single phase transition alumina, mixtures of various aluminas are tolerable. For instance, the production of eta-alumina, gamma-alumina is often concurrently present the resulting product. Indeed, x-ray diffraction analysis can only detect the difference between the two phases with some difficulty. Aluminum hydroxi (boehmite, gibbsite, etc.) may be present in the predominately transition phase product in more than trivial amounts so long as they do not substantially affect the desired alkylation reaction. The catalyst may be found in any appropriate form such as pellet, granules, bead, sphere, powder, or other shape to facilitate its use in fixed beds, moving beds, or fluidized beds. Lewis Acids If the catalyst system of the regeneration process uses one or more Lewis acids in conjunction with the acidic catalyst noted above, then the Le acids may one of those described below. A Lewis acid is a molecule which can form another molecule or an io by forming a complex in which it accepts two electrons from a second molecule or ion. Typical strong Lewis acids include boron halides such as BF 3 , BCI 3 , BBr 3 , and Bl 3 ; antimony pentachloride (SbF 5 ); aluminum halides (AICI 3 and AIBr g ); titanium halides such as TiBr 4 , TiCI 4 , and TiCI 3 ; zirconium tetrachloride (ZrCI 4 ); phosphorus pentafluoride (PF g ); iron halides such as F and FeBr 3 ; and the like. Weaker Lewis acids such as tin, indium, bismuth, zinc, or mercury halides are also acceptable. Catalyst Preparation The preferred alumina catalyst system may be prepared in situ in an alkylation reactor by passing the Lewis acid in gaseous form through the vessel containing the transition alumina. Alternatively, the alumina may be contacted with the Lewis acid and later introduced into the reactor. In any case, the alumina should be substantially dry prior to contact with the Lewis acid and maintained in that state. Contact temperatures between -25 * C an about 100'C are acceptable; a temperature between -25 * C and 30 * C is preferred. The partial pressure of gaseous Lewis acid added to the alumin not particularly important so long as a sufficient amount of Lewis acid is added to the alumina. We have found that treatment of the alumina with B at the noted temperatures will result in an alumina-BF 3 complex containing sufficient to carry out the alkylation. The alumina contains between 0.5% 30% by weight of BF 3 . Obviously, the alumina or other catalyst may be incorporated into a binder prior to its treatment with Lewis acid. The binders may be clays (s as montmorillonite and kaolin) or silica based materials (such as gels or ot gelatinous precipitates). Other binder materials include carbon and metal oxides such as alumina, silica, titania, zirconia, and mixtures of those meta oxides. The composition of the binders is not particularly critical but care must be taken that they not substantially interfere with the operation of the alkylation reaction. Alkylation Process The alkylation process used in one aspect of the invention involves contacting an isoparaffin with an olefin in the presence of the alumina-base catalyst discussed above and in the presence of some excess free Lewis a Specifically, the catalyst of this invention is active at low temperature (as low as -30 *C) as well as at higher temperatures (nearing 50 * C). Lower temperatures (-5*C to 15'C) are preferred because of the enhanced octan of the alkylate produced and are particularly preferred if the feedstream contains more than about 1% isobutylene. Higher temperatures also tend t produce larger amounts of polymeric materials. The pressure used in the alkylation process is not particularly critical. In general, the pressure must kept high enough to maintain the reactants and products in the liquid phas although the catalyst will produce alkylation products when the feedstock is gaseous. As a practical guideline, the process may be operated at atmospheric pressure to about 750 psig. The amount of catalyst used in th alkylation process depends upon a wide variety of disparate variables. Nevertheless, we have found that the Weight Hourly Space Velocity ("WHSV = weight of olefin feed/hour ÷ weight of catalyst) may effectively be betwee 0.1 and 120, especially between 0.5 and 30. The overall molar ratio of isoparaffin to olefin is between about 1.0 and 50.0. Preferred ranges inclu 2.0 and 25.0; the more preferred include 3.0 and 12.0. The feedstreams introduced into the catalyst desirably comprise isoparaffins having from four to ten carbon atoms and, most preferably, fo to six carbon atoms. Isobutane is most preferred because of its ability to make high octane alkylate. The olefins desirably contain from three to five carbon atoms, i.e., propylene, cis- and trans-butene-2, butene-1, and amylenes. The products of this alkylation process typically contain a complex mixture of highly branched alkanes. For instance, when using isobutane a the alkane and n-butylene as the olefin, a mixture of 2,2,3-; 2,2,4-; 2,3,3-; a 2,3,4-trimethylpentane (IMP) will result often with minor amounts of other isomeric or polymeric products. The process involved may utilize the catalyst in a fixed bed using sin or multiple feeds. That is to say, the feedstocks may be independently introduced at one or more points throughout the bed or between multiple beds. Desirably, the catalyst is contacted with the feedstocks in one or mo of continuously stirred reactors, preferably with feed to each reactor. Regeneration Step As we have discussed above, the regeneration step involves the ste of separating the solid catalytic material from the product of the hydrocarb conversion process by use of a liquid-solid separation technique and follow by the step of contacting the catalytic material with a solvent capable of regenerating the material. The solvent desirably is selected from S0 2 ; oxygenates such as C C 4 alcohols, ketones, and aldehydes; alkylnrtriies s as acetonitrile; and phenolics and aromatic ethers such as anisole and phenol. Most preferably, the solvent comprises S0 2 . The catalyst may be first contacted with an inert gas to strip any excess gaseous Lewis acid and light hydrocarbons from the solid catalyst component. The catalyst may also be treated using a mild heating step (e. 50 * to 75 * C) prior to the solvent contact step to further strip hydrocarbons from the solid. Additionally, the removal of hydrocarbons and excess Lewis acid may be facilitated by contact with an inert gas such as helium, nitrog etc. The hydrocarbons and Lewis acid may be recycled as appropriate. The process involves contacting the solid acidic catalyst with a liqui solution comprising a solvent selected from S0 2 ; oxygenates such as C.-C alcohols, ketones, and aldehydes; n ' rtriles such as acetonitriie; and phenoli such as anisole and phenol. When the solid acidic catalyst additionally comprises a Lewis acid the process involves contacting the combination catalyst with a liquid solution comprising a solvent selected from S0 2 or fro aromatic ethers and phenolics such as anisole and phenol. Specifically, the regeneration step involves the contacting of the soli catalyst component with the liquid solvent stream. Clearly, the choice mad for the step of physically contacting the catalyst is dependent in large part upon the specifics of the catalyst component itself. For instance, if the catalyst is in the form of tablets or extrudates or Pall rings (or the like) and found in a fixed bed, the most appropriate way to contact the catalyst woul be to pass the liquid solvent over the catalyst in the catalyst's fixed bed. If, the catalyst is used as a slurry, the catalyst may be transported to a vessel suitable for contacting the alumina component with a liquid stream and then separating the solid from the liquid. The reactor in such a process would likely be a good choice for such a vessel. We have found it to be desirable that the catalyst be kept out of contact with water and with oxygen. The amount of solvent used should be sufficient to remove at least a portion of the reaction residue found on the catalyst component. The resid is ill-defined but often appears to be a moderately long-chained or polymeri material largely alkane in nature but with a minor olefinic character. The residues also often contain polyolefins and aromatic components in small concentrations. We do not consider this regeneration process to be appropriate for residue caused as a result of high temperature hydrocarbon conversion processes, at least those which produce graphitic or carbonaceous residues on the catalyst. Such residues typically have H/C ratios less than one. Although the amount is not believed to be critical, we have found that for most alumina-based alkylation catalysts, an amount of about 100 gm. of solvent per gm. of catalyst is sufficient to regenerate the catalyst to at least 40 % of the prior activity. The temperature of the contact step is also not critical but for alkylat catalysts, treatment in the range of 0 * C to 50 * C is appropriate. When a solvent comprising S0 2 is utilized in the contact step to regenerate catalysts containing Lewis acids, the solvent should be generall dry; preferably it is substantially free of organic and inorganic bases and S and H 2 S0 4 . The level of these contaminants may be such that they do not substantially affect the level of catalyst activity upon return to the hydrocarb conversion medium. Hydrocarbonaceous diluents, such as are the produc of the accompanying hydrocarbon conversion process often make suitable diluents for the solvent used to regenerate the catalyst. Once the steps outlined above are completed, the solid catalyst component may be again be treated with one or more Lewis acids as specified above and returned to the hydrocarbon conversion step. It may b desirable when using S0 2 as the solvent and a gaseous Lewis acid to overpressure the gaseous Lewis acid (e.g., at a pressure above the pressu at which the reaction and/or the solvent treatment step is carried out) befor returning the catalyst to service; although we do not wish to be bound by t theory, we believe that the overpressure aids in sweeping or displacing the solvent from the catalyst surface. The invention has been disclosed by direct description. Below may found examples showing various aspects of the invention. The examples a only examples of the invention and are not to be used to limit the scope of invention in any way. EXAMPLES Example 1 This example shows the regeneration of an alumina-based catalyst which had been treated with BF 3 and then used with excess BF 3 in an alkylation reaction. The feedstream to the alkylation step was a syntheticall prepared feed simulating the hydroisomerized C 4 effluent from an MTBE un (MTBE effluent). The olefinϊc feedstock was prepared containing (by weight) 94% tran and cis-2-butene, 5% butene-1, and 1% isobutylene. The feedstock was prepared by mixing the olefinic feedstock with isobutane such that the final molar ratio of isobutane to olefin was 6/1. This was fed to the alkylation reactor at a weight hourly space velocity (WHSV - based on olefin) was 10. The reaction temperature was held to O'C. Samples were periodically removed from the reactor for analysis by gas-liquid chromatography. During each reaction step, the alkylation reaction was run until approximately 85 gm of olefin per gram of catalyst (i.e., the catalyst "age") h been processed. At that point, there was some indication of a loss of activit of the catalyst as evidenced by a decreasing amount of product C 8 content and a concomitant increase in the product C 12 + content. Additionally, a decrease in the (R+M)/2 as calculated from the gas-liquid chromatography data using well-known correlations (Hutson and Logan, "Estimate Alky Yield and Quality", Hydrocarbon Processing, September, 1975, pp. 107-108) was noted at about that catalyst age. The catalyst was then regenerated using the following procedure: 1. 50 cc of isobutane were added to the alkylation reactor primaril to raise the liquid level to assist in washing back into solution any catalyst that had accumulated at the top of the reactor, 2. the liquid product and isobutane were removed from the reacto through a filtering frit using pressurized inert gas, 3. the reactor containing the spent catalyst was purged with inert gas at 15 cc/min for thirty minutes until the catalyst had the consistency of a free-flowing powder, 4. 150 ml. SO, were added to the reactor and the contents stirred for 20 minutes, 5. S0 2 was withdrawn from the reactor using pressurized inert g and recovered in a collection vessel. The flow of inert gas w continued until no liquid was present in the reactor, 6. steps 4 and 5 were repeated twice, 7. the system was flushed with flowing inert gas for 15 minutes 15 cc/min., 8. BF 3 was added to the reactor vessel containing the regenerat catalyst and pressurized to a total pressure of 60 psig of BF 3 . This pressure was held for 15 minutes. The reactor was then depressurized and purged with inert gas for five minutes, and 9. step 8 was repeated with the exception that following the depressurization of the BF 3 , the inert gas was allowed to purg the system for 20 minutes. The system was then ready for th next alkylation cycle. Following regeneration, the same procedure to initiate the alkylation reaction was followed as with a fresh catalyst, with the exception that isobutane was added to the reactor containing the catalyst and stirred for approximately 30 minutes prior to addition of the BF 3 . This was to insure t the catalyst was well mixed into the liquid medium. The described procedures of alkylation followed by regeneration we repeated for a total of nine cycles. The results of the product analysis from each cycle are summarized in Tab and Figure 1 , indicating initial and final performance as measured by gas chromatographic analysis of the hydrocarbon effluent. The data clearly sh that the full activity of the catalyst is restored using the regeneration procedure. 20 Following the final alkylation cycle, the catalyst was again regenerat with S0 2 using the noted procedure. Analysis of the recovered catalyst b elemental analysis gave the following results: The low carbon and sulfur content of the catalyst show that the S0 2 regeneration procedure is very efficient. The S0 2 does not accumulate on the surface of the catalyst after regeneration. The boron and fluorine cont of the catalyst are very similar to that found on a fresh catalyst. Analysis o the boron-containing species by solid state NMR of boron (Fig. 2) shows a single resonance peak at about -21 ppm, indicating the presence of a sole active boron species and the absence of any decomposition products arisi from the regeneration procedure. Thus, the regeneration procedure is believed to remove contaminating carbon residues while maintaining intact t important species on the catalyst surface. Example 2 This example demonstrates the S0 2 regeneration step using a commercial MTBE raffinate feedstock which had been hydroisomerized to remove butadiene and to convert a portion of the butene-1 to cis- and tra butene-2. This feedstock has the following composition (in wt% on a total olefin basis): 4.3% isobutene, 4.9% butene-1, 87.2% cis- and trans-butene- 1.9% 2-methyl butene-1 and 2-methyl butene-2, and 1.7% pentene-2. This olefinic feedstock was blended with isobutane to a final isobutane/olefin ratio of 6. Normal butane was added to produce a level o 18% in the total feed. This feedstock was fed to the catalyst at 0 * C at a WHSV (on olefin) of 7.2. Samples were taken periodically and analyzed by gas chromatography. The catalyst was run for a total of five cycles with regeneration betw cycles using liquid S0 2 in the procedure shown in Example 1. The C 8 , C 12 + and (R+M)/2 values measured at the beginning and at the end of each cyc are shown in Table 2. This example shows that the regeneration step using S0 2 performs well on an alkylation catalyst which has been used on a commercial feed. It should be clear that one having ordinary skill in this art would envision equivalents to the processes found in the claims that follow and that those equivalents would be within the scope and spirit of the claimed invention.

Claims: WE CLAIM AS OUR INVENTION: 1. A method for regenerating an acidic, solid, hydrocarbon conversion catalyst which does not contain a significant Lewi acid component comprising the steps of: a. separating the acidic, solid, hydrocarbon conversion catalyst from a hydrocarbon conver reaction medium, b. contacting the acidic, solid, hydrocarbon conversion catalyst with a solvent selected from S0 2 ; oxygenates, alkylnitriles, and phenolics an c. separating the catalyst component from the solvent. 2. The process of claim 1 where the catalyst is selected from ac zeolites, alumina, silica-alumina, silica, aluminum phosphate molecular sieves, silicoaluminophosphate molecular sieves, s polymeric ion exchange resins, tetravalent metal phosphonat with pendent acid groups, and sulfated metal oxides. The process of claim 2 where the catalyst is selected from zeolites, alumina, silica-alumina, and silica. The process of claim 3 where the catalyst comprises alumina The process of claim 2 where the solvent comprises S0 2 . 6. The process of claim 1 additionally comprising the step of heating the solid catalyst to a temperature of up to about 75 * after the separation step to substantially remove volatile hydrocarbons. 7. A method for regenerating an acidic, solid, hydrocarbon conversion catalyst additionally containing a Lewis acid component comprising the steps of: a. separating the acidic, solid, hydrocarbon conversion catalyst from a hydrocarbon convers reaction medium, b. contacting the acidic, solid, hydrocarbon conversion catalyst with a solvent selected from S0 2 and phenolics and aromatic ethers, and c. separating the catalyst component from the solvent. 8. The process of claim 7 where the catalyst is selected from aci zeolites, alumina, silica-alumina, silica, aluminum phosphate molecular sieves, silicoaluminophosphate molecular sieves, so polymeric ion exchange resins, tetravalent metal phosphonate with pendent acid groups, and suifated metal oxides. 9. The process of claim 8 where the catalyst is selected from zeolites, alumina, silica-alumina, and silica. 10. The process of claim 9 where the catalyst comprises alumina. 11. The process of claim 8 where the catalyst comprises a strong Lewis acid selected from BF3, BCI3, BBr3, BI3, SbF5, AICI3, AlBr3, TiBr4, TiCI4, TiCI3, ZrCI4, PF5, FeCI3, and FeBr3. 12. The process of claim 11 where the strong Lewis acid is selecte from SbF5, AICI3, and BF3. 13. The process of claim 12 where the strong Lewis acid is BF3. 14. The process of claim 8 where the solvent comprises S0 2 . 15. The process of claim 7 additionally comprising the step of heating the solid catalyst to a temperature of up to about 75 5 after the separation step to substantially remove volatile hydrocarbons. 16. A method for regenerating an alkylation catalyst component which component comprises a major amount of a transition 10 alumina which has been contacted with a strong Lewis acid produce an alkylation catalyst component containing betwee 0.5% and 30% by weight of Lewis acid and has been partiall deactivated by use in an alkylation reaction medium, compris the steps of: 15 a. separating the alkylation catalyst from the alkyl reaction medium, b. contacting the alkylation alumina catalyst component with a solvent comprising S0 2 , and c. separating the alkylation alumina catalyst 20 component from the S0 2 solvent. 17. The process of claim 16 where the transition alumina is sele from gamma-alumina, eta-alumina, theta-alumina, chi-alumin rho-alumina, and mixtures. 25 18. The process of claim 17 where the transition alumina is sele from gamma-alumina, eta-alumina, and mixtures. 19. The process of claim 16 where the strong Lewis acid is sele 30 from BF 3 , BCI 3 , BBr 3 , Bl 3 , SbF 5 , AICI 3 , AIBr 3 , TiBr 4 , TiCI 4 , TiCI ZrCI 4 , PF 5 , FeCI 3 , and FeBr 3 . 20. The process of claim 19 where the strong Lewis acid is select from SbF 5 , AlCI 3 , and BF 3 . 21. The process of claim 20 where the strong Lewis acid is BF 3 . 22. The process of claim 16 additionally comprising the step of heating the alkylation catalyst component to a temperature of to about 75 * C after the separation step to substantially remov volatile hydrocarbons. 23. An alkylation process comprising the steps of: a. contacting a mixture comprising isoparaffins and olefiπs with an acidic alkylation catalyst system comprising a catalyst system comprising i.) a soli catalyst component of a transition alumina or zeolite which has been previously contacted with Lewis acid, and ii.) free Lewis acid, under alkylatio conditions to produce an alkylate stream, b. separating the alkylate stream from the solid alkylation catalyst system, c. contacting the solid alkylation catalyst with a solvent comprising S0 2 , d. separating the solid alkylation catalyst component from the S0 2 solvent, and d. recycling the solid alkylation catalyst component t the alkylation step. 24. The process of claim 23 where the solid alkylation catalyst comprises one or more of gamma-alumina, eta-alumina, theta- alumina, chi-aiumina, rho-alumina, and mixtures. 25. The process of claim 24 where the transition alumina is gam alumina, eta-alumina, or mixtures. 26. The process of claim 23 where the strong Lewis acid is selec 5 from BF 3 , BCI 3 , BBr 3 , Bl 3 , SbF 5 , AICI 3 , AIBr 3 , TiBr 4 , TiCI 4 , TiCI ZrCI 4 , PF 5 , FeCI 3 , and FeBr 3 . 27. The process of claim 26 where the strong Lewis acid is selec from SbF 5 , AICI 3 , and BF 3 . 10 28. The process of claim 27 where the strong Lewis acid is BF 3 . 29. The process of claim 28 where the BF 3 is contacted with the solid alkylation catalyst at a pressure above the pressure of t 15 reaction before the catalyst is recycled. 30. The process of claim 23 additionally comprising the step of heating the solid alkylation catalyst component to a temperat of up to about 75 * C after the separation step to substantially 20 remove volatile hydrocarbons. 31. The process of claim 23 where alkylation conditions include a temperature in the range of -30 * C to 50 * C. 25 32. The process of claim 23 where the mixture comprises 2-bute and isoparaffin. 33. The process of claim 23 including the step of mixing the alkyl stream with other hydrocarbons to produce a gasoline blendi 30 component or gasoline.

Inventors: COOPER MICHAEL D, KING DAVID L, LOPEZ RONALD R, RAO PRADIP, COOPER, MICHAEL, D., KING, DAVID, L., LOPEZ, RONALD, R., RAO, PRADIP
Applicants: CATALYTICA INC, CATALYTICA, INC.
Application year: 1992
Main classification: C07C2
IPC codes: B01J27, B01J29, B01J38, C07B61, C07C2, C07C9, C10G35, C10G50, C10L1