Microboiologically degradable polymer composition

Abstract: The invention is a degradable polymer composition essentially consisting of a mixture of a thermoplastic polymer composition primarily comprising polylactic acid or lactic acid-hydroxycarboxylic acid copolymer and one or more substance selected from starch and modified starch, and is a degradable polymer which does not cause problems such as environmental pollution and can be used for films, filaments and packaging materials, food packaging materials in particular.

Description: The present invention relates to a degradable polymer composition and more particularly relates to a microbiologically degradable polymer composition consisting essentially of a mixture as defined in claim 1. Attention has recently been focussed on thermoplastic and degradable polymers for use as packaging materials or medical materials. The amount of plastics used for packaging has recently been increased to enhance appearance, sanitation, packing and transport of commodities. At the same time, the amount of refuse discarded from households and factories has been increasing rapidly and causes a serious problem because of the shortage of landfill space in the periphery of large cities. Conventional plastics for use in packaging are polyethylene, polypropylene, polystyrene, polyethylene terephthalate and polyvinyl chloride. However, when these plastics are disposed of in the natural environment, they remain undecomposed because of their stability and spoil scenery, and lead to pollution of living environment for marine life and various other various problems. Many research and development activities have been carried out in order to prepare packaging materials from degradable polymers which do not generate these problems. For example, Japanese Patent Publication Sho 52-21530 and 52-42187 disclose techniques to provide degradability by blending non-degradable polymers, such as polyethylene, polypropylene and polystyrene with startch. The resins prepared by these techniques collapse their shape by degradation of starch. However, non-degradable polymer fragments remain intact and lead to environmental pollution. However, if the amount of starch is too low thenthere exists the problem that the resins retain their original shape after degradation of the starch portion, even though their film strength is decreased. Polymers and copolymers of lactic acid have been known as thermoplastic and degradable polymers. Latic acid polymers completely degrade in the animal body in a period of several months to year. When these polymers are placed in a moist environment such as soil or sea water, then start to decompose within several weeks and disappear in about a year. The decomposition products are lactic acid, carbon dioxide and water, all of which are harmless. The raw material lactic acid can be prepared by fermentation of cheap materials such as corn starch and corn syrup, and can also be obtained from petrochemicals such as ethylene. USP 1,995,970, 2,362,511 and 2,683,136 disclose polymerization process of lactic acid. USP 3,636,956 and 3,797,499 describe processes for preparing copolymers of lactic acid and glycolic acid. Lactic acid polymers are usually prepared from so-called lactide, a cyclic dimer of lactic acid. When glycolic acid is copolymerized, ring opening polymerization is carried out after mixing lactide with glycolide which is a dimer of glycolic acid. When the polymer is directly prepared by dehydrating condensation of lactic acid or a mixture of lactic acid and glycolic acid, a high molecular weight polymer cannot be obtained even if reacted for a long time. On the other hand, the straight chain polyester prepared by ring opening polymerization of lactide or a mixture of lactide and glycolide has a high molecular weight. USP 1,995,970 discloses a formulation in which from 20 to 80 % by weight of polyether antibiotics are incorporated in order to accelerate glowth and feed efficiency in ruminants with a lactic acid-glycolic acid copoolymer consisting of from 60 to 95 % by weight of lactic acid and from 40 to 5 % by weight of glycolic acid and having a weight average molecular weight of from 6,000 to 35,000. The patent describes non auxiliary substances such as diluents, carriers, binders excipients and various other adjuvants can be incorporated in the formulation. Corn starch is one of these auxiliary substances. The degradation rate of a polymer primarily comprising polylactic acid is almost determined by the hydrolysis rate of polylactic acid, and is relatively slow as compared with that of other microbiologically decomposable polymers. Particularly in the case of polylactic acid having a high molecular weight, for example 50,000 or more, the degradation rate is remarkably slow and it is hence desired to find a method for accelerating the decomposition. These polymers are usually processed into filaments or molded articles and utilized for biomedical slow-release materials, bone plates, screws and the above formulation for accelerating the growth and feed efficiency in ruminants. In these applications, the degradation rate in a living body is controlled by the addition of glycolic acid. However, increasing the proportion of glycolic acid causes changes in the polymer properties such as strength, hardness and elongation. Further, deterioration by moisture during use is accelerated and leads to problems. Consequently, embodiments of the invention desirably provide a microbiologically degradable polymer composition as defined in the claims, which can be used for films, filaments and packaging materials, food packaging materials in particular, and has a suitable hardness and quick degradation rate. The present invention is a microbiologically degradable polymer composition comprising a mixture of a thermoplastic polymer composition essentially consisting of polylactic acid having a molecular weight of 50,000 ∼1,000,000 or a copolymer of lactic acid and other hydroxycarboxylic acids having molecular weight of 50,000 ∼1,000,000, and starch and/or modified starch. The degradation rate of the resin composition can be controlled by the addition of starch or modified starch. The starch used in the process of the invention includes, for example, potato starch, corn starch, sweet potato starch, wheat starch, rice starch, tapioca starch, sago starch and other natural starch, decomposition products of starch, amylase and decomposition products of amylopectin. Modified starch means oxidized starch such as dicarboxylic acid starch, esterified starch such as acetylated starch, etherified starch such as carboxymethylated starch, crosslinked starch obtained by treating starch with acetaldehyde or phosphoric acid and cationic starch obtained by tertiary-aminating starch with 2-dimethylaminoethyl chloride. The starch or modified starch used for the process of the invention is used after converting it into soluble starch, if desired. Solubilization can be carried out, for example, by heating at a temperature of 60°C or more in the presence of water or an aqueous solution until starch particles swell sufficiently and burst to form a smooth and viscous dispersion in water. The polymers used in the invention may be a mixture of polylactic acid with a copolymer of lactic acid and other hydroxycarboxylic acid. Useful other hydroxycarboxylic acid includes, for example, glycolic acid, 3-hydroxybutyric acid, 4-hydroxybutyric acid, 4-hydroxyvaleric acid and 6-hydroxycaproic acid. These polymers can be directly prepared by dehydrating polycondesation of lactic acid or other hydroxycarboxylic acid or obtained by ring-opening polymerization of glycolide (GLD), ε-caprolactone (CL) which is a cyclic ester of 6-hydroxycaproic acid or a mixture of these compounds. Another polymer which can also be used is a copolymer obtained by a transesterification reaction of polylactic acid with an other hydroxycarboxylic acid polymer at high temperature. L-lactic acid, D-lactic acid and a mixture of these lactic acid can be used for constituting the polymers. The molecular weight of the polymer is from 50,000 to 1,000,000. Molecular weight smaller than this range leads to unpractically low strength when the polymer is used for a film or for food packaging materials. On the other hand, molecular weight larger than this range result in high melt viscosity and processing becomes difficult. In the process of the invention, degradation rate of the composition obtained can be controlled by changing the content of starch or modified starch in the composition. When the amount of starch is increased, weatherablity and tear resistance decreases. However, a high content of starch is suitable for uses which require high degradation rate. The amount of starch can be suitably decreased when high strength is required. Preferred range of the amount greatly differs depending upon use and must be determined on the basis of achieving a balance between properties such as strength and degradation rate. No particular restriction is imposed upon the method for blending the resin of the invention primarily comprising polylactic acid with starch or modified starch. The resin is usually heated, starch powder is added to the resin, and the resulting mixture is heat-kneaded, for example, with a roll mill. The kneading temperature is generally from 130 to 250 °C, preferably from 130 to 200°C in view of decomposition of the resin, starch or modified starch. The polymer composition of the invention can comprise plasticizer, stabilizer, antioxidant, ultraviolet absorber, colorant and other additives. Compatibility improvers such as ethyl oleate or calcium stearate can also be used in order to enhence compatibility between the polymer primarily comprising polylactic acid and starch or modified starch. The polymer composition of the invention can comprise in addition to polylactic acid, plasticizer, and other reforming additives. The polymer composition thus obtained can be processed by injection molding or extrusion. The polymer composition can also be dissolved in a solvent and cast into a film. EXAMPLES The present invention will hereinafter be illustrated in detail by way of examples. However, these examples are not intended to limit the scope of the present invention. EXAMPLE 1 In a sealed mixer, 90g of poly-L-lactic acid pellet having an average molecular weight of 120,000 and 10g of corn starch were uniformly kneaded at 190 °C, extruded and pelletized. The pellets were hot-pressed at 180°C into a film having a thickness of 25 µm. The film obtained was translucent and had a smooth surface. The film was buried in a compost at 40 °C as a degradation test and disappeared after 6 weeks. EXAMPLE 2 In a sealed mixer, 70g of poly-L-lactic acid pellet having an average molecular weight of 120,000, 20g of corn starch and 10g of ethyl oleate were uniformly kneaded at 190 °C, extruded and cut into pellets. The pellets were hot-pressed at 180°C into a film having a thickness of 25 µm. The film thus obtained was translucent and had a smooth surface. The film was buried in a compost at 40°C as a degradation test and disappeared after 4 weeks. EXAMPLE 3 In a sealed mixer, 60g of poly-L-lactic acid pellets having an average molecular weight of 120,000, 30g of soluble starch and 10g of ethyl oleate were uniformly kneaded at 190 °C, extruded and cut into pellets. The pellets were hot-pressed at 180°C into a film having a thickness of 25 µm. The film thus obtained was translucent and had a smooth surface. The film was buried in a compost at 40°C as a degradation test and disappeared after 3 weeks. EXAMPLE 4 In a sealed mixer, 60g of D,L-lactic acid-glycolic acid copolymer (50:50) pellets having an average molecular weight of 80,000, 30g of soluble starch and 10g of ethyl oleate were uniformly kneaded at 190 °C, extruded and pelletized. The pellets were hot-pressed at 180°C into a film having a thickness of 25 µm. The film thus obtained was translucent and had a smooth surface. The film was buried in a compost at 40°C as a degradation test. The film was broken into pieces after 2 weeks and disappeared after 2 months. EXAMPLE 5 In a sealed mixer, 40g of poly-L-lactic acid pellets having an average molecular weight of 120,000, and 60g of carboxymethylated starch having an etherification degree of 1.4∼1.7 were uniformly kneaded at 190 °C, extruded and cut into pellets. The pellets were hot-pressed at 180°C into a film having a thickness of 25 µm. The film thus obtained was translucent and had a smooth surface. The film was buried in a compost at 40°C as a degradation test and disappeared after a week. EXAMPLE 6 In a sealed mixer, 40g of poly-L-lactic acid pellets having an average molecular weight of 120,000 and 60g of acetylated starch were uniformly kneaded at 190 °C, extruded and cut into pellets. The pellets were hot-pressed at 180°C into a film having a thickness of 25 µm. The film thus obtained was translucent and had a smooth surface. The film was buried in a compost at 40°C as a degradation test and disappeared after a weeks. COMPARATIVE EXAMPLE 1 The poly-L-lactic acid pellets which were used in Example 1 and had an average molecular weight of 120,000 were hot-pressed at 180 °C into a film having a thickness of 25 µm. The film was transparent and had a smooth surface. The film was buried in a compost at 40°C as a degradation test and still retained its shape even after 6 weeks. COMPARATIVE EXAMPLE 2 D,L-lactic acid-glycolic acid copolymer (50:50) pellets which were used in Example 4 and had an average molecular weight of 80,000 were hot-pressed at 180 °C into a film having a thickness of 25 µm. The film thus obtained was transparent and had a smooth surface. The film was buried in a compost at 40°C as a degradation test and still retained its shape even after 2 weeks. COMPARATIVE EXAMPLE 3 In a sealed mixer, 60g of polyethylene pellet MIRASON NEO 23H (Registered Trade mark of Mitsui Petrochemical Industry Co.) and 40g of soluble starch were uniformly kneaded at 190 °C, extruded and cut into pellets. The pellets were hot-pressed at 180°C into a film having a thickness of 25 µm. The film obtained was translucent. The film was buried in a compost at 40°C as a degradation test and maintained its shape even after 6 months. EXAMPLE 7 In a sealed mixer, 60g of poly-L-lactic acid having an average molecular weight of 120,000, 30g of soluble starch and 10g of ethyl oleate were uniformly kneaded at 190°C, extruded and cut into pellets. The pellets obtained were hot-pressed at 180°C into a film having a thickness of 25 µm. The film obtained was translucent and had a smooth surface. The film was buried in a compost at 40°C as a degradation test and disappeared after 6 months. EXAMPLE 8 In a sealed mixer, 60g of L-lactic acid and D,L-hydroxy acetic acid copolymer (90:10) pellet having an average molecular weight of 90,000, 30g of soluble starch and 10g of ethyl oleate were uniformly kneaded at 190 °C, extruded and pelletized. The pellets were hot-pressed at 180°C into a film having a thickness of 25 µm. The film thus obtained was translucent and had a smooth surface. The film was buried in a compost at 40°C as a degradation test. The film was broken into pieces after 6 weeks and disappeared after 2 months. COMPARATIVE EXAMPLE 4 L-lactic acid and D,L-hydroxy acetic acid copolymer (90:10) pellets having an average molecular weight of 90,000, which were used in Example 8 were hot-pressed at 180 °C into a film having a thickness of 25 µm. The film thus obtained was translucent and had a smooth surface. The film was buried in a compost at 40°C as a degradation test and still retained its shape even after 6 weeks.

Claims: A microbiologically degradable polymer composition consisting essentially of a mixture of: a modified starch selected from the group consisting of oxidized starch, acetylated starch, etherified starch, crosslinked starch and cationic starch; and polylactic acid having a molecular weight of 50,000 - 1,000,000 or a copolymer of lactic acid and other hydroxycarboxylic acid having a molecular weight of 50,000 - 1,000,000. A microbiologically degradable polymer composition of claim 1 wherein lactic acid is L-lactic acid, D-lactic acid or a mixture of these lactic acids. A microbiologically degradable polymer composition of any one of the preceding claims wherein the hydroxycarboxylic acid is glycolic acid. A method for the production of a microbiologically degradable polymer composition according to any one of the preceding claims comprising blending the polylactic acid or copolymer of lactic acid and other hydroxycarboxylic acid and modified starch. A method according to claim 4 wherein the modified starch is added to hot polylactic acid or copolymer of lactic acid and other hydroxycarboxylic acid and the mixture heat-kneaded.

Inventors: AJIOKA MASANOBU, ENOMOTO KATASHI, SHINODA HOSEI, YAMAGUCHI AKIHIRO, AJIOKA, MASANOBU, ENOMOTO, KATASHI, SHINODA, HOSEI, YAMAGUCHI, AKIHIRO
Applicants: MITSUI CHEMICALS INC, MITSUI CHEMICALS, INC.
Application year: 1992
Main classification: C08L67
IPC codes: C08L101, C08L67, C08L3