Coating blend compositions

Abstract: A coating blend composition is a physical admixture of an adhesion promoter resin and a coating material resin. The blend can be cured by one or more curing agents existing within either the adhesion promoter resin, the coating material resin, or both. The utilization of such a blend eliminates the need for priming a substrate such as a rubber, or a thermoplastic or a thermoset polyolefin. The adhesion promoter resin is a urethane composition containing a blocked polyurethane prepolymer whereas the coating material resin can generally be any compound which has a functional or cosmetic purpose such as a different type of blocked polyurethane, and is generally utilized in a major amount. A particular application of the coating blend compositions of the present invention is to a glass run channel made from, for example, EPDM, as in an automotive door.

Description: This invention relates to coating compositions, their manufacture and use. Use may be as a functional coating for elastomeric substrates, such as an automotive window glass run channel made from ethylene-propylenediene polymers (EPDM). Polyurethane-based adhesives and coatings are known. For example US-A-4898919 describes a polyurethane adhesive comprising (a) a specific block polyurethane polyol produced by reacting a hydrogenated polybutadiene glycol, a polyol having two or more hydroxy groups, and a polyisocyanate, (b) a thermoplastic polyester urethane rubber, and (c) a polyisocyanate compound as a crosslinking agent, said polyurethane adhesive being useful for adhesion of low polar materials, particularly adhesion between polypropylene materials and sheets of polyvinyl chloride. Japanese Patent applications JP 60-173011 (1985), JP 62-41215 (1987), JP 63-130616, and JP 64-6017 (1989), relate to polyurethane compositions made from low molecular weight polyolefin polyols and are directed to adhesives, coatings, and sealants. In Japanese Patent JP 60-179251 (1985), a mixture of a low molecular weight polyolefin polyol and a blocked methylene diphenyl diisocyanate is utilized as an adhesive for splicing an EPDM glass run channel and weather stripping, while JP 60-181137 (1985) suggests that the same composition can be used as an adhesive to obtain adhesion between EPR (ethylene-propylene rubber) and metal as well as between plastics and rubber. JP 61-136528 (1986) relates to a low molecular weight polyolefin polyol mixed with an N-halogenated amide functional compound used as a coating primer for an EPDM glass run channel where the top coat is a polyester-urethane based coating containing silicone oil while JP 61-137735 (1986) discloses the same composition as an adhesive for fiber flocking on an EPDM glass run channel. Japanese patent application JP 60-179470 and patent JP 60-24821 relate to the utilization of greater than 98 percent hydrogenated polyhydroxy polybutadiene as (a) a crosslinking agent, or (b) an additional polyol component in a polyester and/or polyether urethane coating compositions which are applied to flocked substrates to enhance their resistance to abrasion, weathering, and heat. Japanese Application JP 59-201838 relates to a coextruded rubber product having a sliding surface as well as to a fabrication method therefor, wherein a rubber substrate is coextruded with a sliding surface composition which is a mixture of urethane forming components. Subsequently, the substrate as well as the sliding surface are vulcanized and cured at the same time. US-A-4101350 describes polyurethane stoving lacquers in which a urethane prepolymer with blocked excess NCO is made from isophorone diisocyanate and low-molecular polyols. EP-A-107838 discloses the use of polyamines to crosslink end-blocked urethane prepolymers in a polyurethane coating especially on textile substrates. Our own EP-A-430421 describes heat-curable polyurethane compositions containing blocked urethane prepolymer, amine crosslinking agent and silicone oil, in which the OH-functional component of the prepolymer is a hydrogenated polydiene or polyolefin intermediate having at least 1.5 OH groups per molecule and a number average molecular weight in the range 500 to 15000. The present invention provides in one aspect a curable coating composition comprising a curable coating composition comprising a coating resin mixed with an adhesion promoter resin, the adhesion promoter resin constituting from 0.5 to 50 wt% of the combination of the adhesion promoter resin and coating resin and comprising a blocked polyurethane prepolymer which is the reaction product of hydroxy-functional hydrogenated polydiene or polyolefin intermediate, having on average more than 1.5 hydroxyl groups per molecule and a number average molecular weight in the range from 500 to 15000, with at least 1.8 equivalents of polyisocyanate, excess isocyanate groups being blocked with blocking agent, and the coating resin being polyurethane prepolymer, which may be blocked but is not polyurethane prepolymer derived from hydroxy-functional hydrogenated polydiene or polyolefin intermediates. Another aspect is a method of making such a composition, including mixing the polyurethane coating resin and adhesion promoter resin. Further aspects are a coating process in which the composition is applied to a substrate, and a coated substrate obtained thereby. The amount of adhesion promoter resin may be generally small or low in comparison with the amount of the coating material resin. For example, when the coating blend composition is applied to a cured rubber substrate, the amount of the adhesion promoter resin based upon the total amount of the adhesion promoter resin and the coating resin is generally from 0.5 percent to 25 percent by weight, desirably from 1.0 percent to 10 percent by weight, and preferably from 3 percent to 6 percent by weight. When utilized on an uncured rubber substrate, the amount of promoter resin in the blend is generally from 2.0 or 3.0 percent to 50 percent by weight, desirably from 5 to 40, and preferably from 15 to 30 percent by weight. Generally, the coating composition blend can be cured according to a plurality of different methods and/or compounds. It has been found that the above-described polyurethane blocked prepolymer resin when utilized in small amounts acts as an adhesion promoter with other polyurethane coating material resins and forms an effective bond or attachment to substrates such as rubber. When so utilized, the adhesion promoter resin system need not contain silicone oil, fillers, and the like, inasmuch as the same are optional, but only the blocked polyurethane prepolymer. The coating blend resin composition can be cured to the substrate by moisture cure and/or by utilizing one or more curing agents either as part of the prepolymer(s) or as a separate compound, generally in the presence of heat. ADHESION-PROMOTER RESIN A blocked polyurethane can be produced by reacting a hydroxyl terminated hydrogenated diene polymer or polyolefin with excess equivalents of diisocyanate, where the resulting free isocyanate end groups are blocked with a suitable blocking agent which will unblock upon heating. Typical diene monomers used to produce the diene polymers are conjugated dienes, having from 4 to 10 carbon atoms, or combinations thereof, such as 1,3-butadiene, isoprene or dimethyl butadienes and the like. The polymerization of the diene monomer, typically, may be done via anionic initiation (e.g. with di-lithium hydrocarbyl initiators) or via free-radical polymerization, e.g. by initiation with hydrogen peroxide, which also introduces hydroxy end groups. In anionic polymerization, OH-end groups are advantageously introduced by reaction of the polymeric carbon-ion chain ends with ethylene oxide. These techniques are generally well known. The hydroxy-functional polydienes may be hydrogenated, for examnle, partially or substantially (i.e., at least 50, 90 or 95 percent of the unsaturated sites), and even completely hydrogenated, according to any conventional method known to the art. Complete hydrogenation of various diene polymers such as 1,4-polyisoprene is equivalent to an alternating ethylene/ propylene hydrocarbon polymer. The polyolefins are made from monomers having from 2 to 6 carbon atoms such as ethene, propene, and the like. The intermediate hydrocarbon polymers used herein usually have a number average molecular weight from about 500 to 15,000 and preferably from about 1,000 to about 8,000. Intermediates are desirably liquid at room temperature, but can have a melting point up to about 80°C. Preferred intermediates are hydroxyl functional telechelic, completely hydrogenated diene polymers containing 2 to 6 and preferably 2 to 4 hydroxy end groups per polymeric molecule (polymer unit). Preferred hydroxyl functional polyolefins are derived from hydrogenated polybutadiene, poly(butadiene-styrene), polyisoprene, and the like. Particularly preferred intermediates are hydroxy terminated polydienes, which are completely hydrogenated (i.e., have less than 1 or 2 percent unsaturation sites), and contain the desired hydroxyl functionality. Polymers with more than two hydroxyl groups on the average per polymer molecule may be considered as branched or star-type polymers. The hydroxyl functional polyolefins can also be made by utilizing minor amounts (i.e. up to about 50 mole percent and preferably up to 20 mole percent) of ethylenically unsaturated comonomers such as styrene, vinyl toluene, alpha-methylstyrene, divinylbenzene, and similar aromatic monomers; or vinyl monomers, such as acrylonitrile, methacrylonitrile, vinylidene chloride, and similar aliphatic vinyl monomers; or hydroxyl functional ethylenically unsaturated monomers such as 2-hydroxyl ethyl acrylate and methacrylate, 2-hydroxy propyl acrylate and methacrylate and similar hydroxy alkyl acrylates. Regardless of the type of intermediate polyolefin, it should contain at least 1.5 hydroxyl groups from about 1.8 to about 6 hydroxyl groups per average molecule, desirably from about 1.8 to about 2.3, and preferably from about 1.9 to about 2.1 hydroxyl groups. An especially preferred intermediate polyolefin is a hydrogenated butadiene polymer. Such an intermediate is commercially available as Polytail H and Polytail HA from Mitsubishi Kasei Corp. It has the generalized structure: wherein X and Y are randomly distributed and the structure can contain additional -OH groups, and the X/Y ratio, the -OH number per polymeric molecule, the physical state at 25°C, and the melting points are as follows: Polytail H Polytail HA Preferred Range X/Y 2/8 9/1 0.10 to 10.0 OH Number 2.3 1.8 1.5 - 4 Physical State Waxy solid Liquid Liquid to low melting solid (MP ≤ 80°C) The hydroxyl functional polyolefin intermediates, described above, are reacted with excess equivalents of a polyisocyanate R(NCO) n, where n is 2 to 4 and preferably 2.0 (i.e. diisocyanate), or mixtures of various di, triisocyanates, etc. such that n is from about 1.7 to about 2.3, and preferably from about 1.9 to about 2.1, and where R is aliphatic, aromatic, or combinations thereof (e.g., aliphatic substituted aromatics), having from 4 to 100 carbon atoms and preferably from 4 to 20 or 30 carbon atoms to produce an isocyanate terminated functionally reactive urethane prepolymer. At least about 1.8 equivalents and preferably from about 2 to about 8 equivalents of the polyisocyanate reactant are charged per equivalent of hydroxyl functional hydrocarbon polymer to produce the desired urethane prepolymer. Preferred aromatic diisocyanates include 4,4-methylene diphenyl isocyanate (MDI), as well as modified MDI known as Isonates (Dow Chemical), toluene diisocyanate (TDI) such as the 2,4-or 2,6-isomers, as well as mixtures thereof, 1,4-phenylene diisocyanate, m- and p-xylenene diisocyanates (XDI), and the like. Preferred aliphatic diisocyanates include 1,6-hexane diisocyanate, mixed trimethylhexane diisocyanate (TMI), isophorone diisocyanate (IPDI), and the like. An example of a triisocyanate is Desmodur® N-3300, an aliphatic polyisocyanate base upon hexamethylene diisocyanate. Whenever a triisocyanate is utilized, the amount thereof is very small, for example, up to 10 moles, based upon the number of moles of the blocked prepolymer. Mixtures of various polydiisocyanates can be used if desired. Suitable blocking agents for blocking the isocyanate terminated urethane prepolymer are known to the art and to the literature and include various lactams having from 3 to about 12 carbon atoms, such as epsilon-caprolactam, propiolactam, dimethyl propiolactam, 2-pyrrolidone, gamma-valerolactam, epsilon-laurolactam, and the like. Another group of blocking agents include the various ketoximes having from about 3 to about 20 and desirably from 3 to about 15 carbon atoms such as: dimethyl-, methylethyl-, diisopropyl-, dicyclohexylketoximine, benzophenone and the like. Various phenols, such as 4-hydroxy-(methyl) benzoate, methyl salicylate, ethyl salicylate, phenol, o-, m-, and p-cresol, nonylphenols, C 15 H 27 phenols, and the like, containing from 3 to 20 carbon atoms can also be utilized. Various cyclic ureas having a total of from 3 to 12 carbon atoms such as trimethylene or tetramethylene urea can also be utilized. Various enamines having the formula where R 1 and R 2 , independently, is an alkyl having from 1 to 4 carbon atoms can also be utilized. Another group of blocking agents are the various dicarbonyl compounds having the general formula where R 3 and R 4 , independently, is an alkyl having from 1 to 6 carbon atoms, phenyl, or R 5 O, where R 5 is hydrogen or an alkyl having from 1 to 12 carbon atoms such as: acetylacetone, diethylmalonate, dimethylmalonate, acetylethyl acetate, and the like. Still other blocking agents include benzotriazole, the various phenylimidazoles, and the like. The amount of blocking agent utilized should generally be an approximate equivalent ratio of NCO/blocking agent of from about 0.5 to 2.0 and preferably from about 0.9 to about 1.1. Preferred blocking agents include caprolactam and the various ketoximes. An important preferred feature is the use of crosslinking agents to obtain improved physical properties such as abrasion resistance. The various crosslinking or curing agents which can be utilized include those containing -NH 2 , -NHR 6 , etc. groups, where R 6 is an alkyl having from 1 to 4 carbon atoms, -OH, or -SH groups, and the like, which react with the blocked or unblocked isocyanate groups of the urethane prepolymer upon heating. Such crosslinking or curing agents are known to the art and to the literature. Particularly preferred curatives or crosslinking agents comprise aliphatic, primary or secondary di-, tri-, and tetra-functional amines having a boiling point above about 100°C and preferably above 180°C. Useful amine crosslinking agents include, for example, polyoxypropylene- or polyoxy(propylene/ethylene)-based primary di- and triamines sold by Texaco Chemical Company under the tradename "Jeffamine," which are herein fully incorporated by reference, such as T-403 (triamine; MW about 480), EDR-148 (diamine; MW about 150), T-3000 (triamine; MW about 3,000), T-5000 (triamine; MW about 5,000), D-230 (diamine; MW about 200), D-400 (diamine; MW about 400), or D-2000 (diamine; MW about 2,000). Other crosslinking agents include polyamine resins containing amino end groups, sold by Henkel Corporation under the tradenames "Versamid" or "Genamid," which are hereby fully incorporated by reference, such as Versamids 100, 115, 125, 140, 150, 250, or Genamids 250, 747, 2000, and the like. Still other useful amine curatives include isophoronediamine (Huels Co.), mixed trimethylenediamine (TMD; Huels Co.), N,N'-diaminoethylpiperazine, N-aminoethylpiperazine, 1,4-cyclohexanediamine, 1,6-hexanediamine, 1,4-butanediamine, diethylenetriamine, m- or p-xylylenediamine, ethylenediamine, liquid poly(dimethylsiloxane)-diamine; various aromatic di- or triamines, which are liquid, or low melting, soluble or dispersible in the coating mixture, such as a ring methylated phenylenediamine (RDX-66884, sold by Interez Co.) or poly(tetramethylene oxide)-bis-(4-aminobenzoates) (Polyamine-650 and -1000 sold by Air Products), and the like. Other useful crosslinking agents include polyols (diols, triols or tetrols) having a number average molecular weight of from about 200 to about 1,000, which may be used either alone or in combination with diamines, and generally have a total of from 2 to about 100 carbon atoms. Desired polyols have primary hydroxyl groups, as well as tertiary, secondary or primary amino groups in their structures, such as triethanolamine, diethanolamine or ethanolamine. Curatives with two or more sulfuryl groups or combinations of NH 2 , OH and SH can also be utilized. The ratio of blocked isocyanate groups to curative groups (-NH 2 , -NHR 6 , -OH, or -SH) is generally from about 0.8 to infinity, that is, where no curing agent is utilized, desirably from about 1 or 2 to about 20, 30, or 50, more desirably from about 2 to about 10 or from about 2 to about 4, preferably from about 0.8 to about 3.8, and on some occasions, from about 0.8 to about 2.0, and preferably from about 1.0 to about 2.0. Shelf life of coatings containing a crosslinking agent, such as polyamine, is at least about two weeks at ambient temperatures. Although curing of blocked polyurethanes with a polyamine curing agent normally does not require an added catalyst, urethane curing catalysts can be utilized, especially if polyols are used as curatives. Such catalysts are well known to the art and to the literature and include, for example, stannous octoate, various tin catalysts such as dioctyltin dilaurate, dibutytin dilaurate, etc., and various tertiary amines. Advantageously, these catalysts are added during the preparation of the isocyanate terminated hydrocarbon polyols to assist in the formation of the isocyanate terminated prepolymer and/or to facilitate the blocking of the isocyanate groups. The amount of the catalyst is generally from about 0.1 percent to about 5 percent catalyst by weight based upon the total amount, by weight, of reactants which form the blocked polyurethane. Cure, that is, crosslinking of the prepolymers as well as other reactions, is generally carried out at from about 20°C to about 255°C, desirably from about 160°C to about 250°C, and preferably from about 170°C to about 230°C. Variable amounts of silicone oil may be added to the composition or mixture of blocked polyurethane prepolymer and crosslinking agent. Silicone oils are low molecular weight liquids or fluid silicone polymers and generally have a silicone backbone structure comprising alternate silicon and oxygen atoms with the generalized structure (SiR* 2 O) n , where R*, independently is an alkyl group having from 1 to 4 carbon atoms and preferably is methyl, and "n" is from 2 to about 5,000. The silicon polymer can also contain minor amounts, that is up to about 40 percent, or up to 10 percent of repeating units such as fluoroalkyl (1 to 4 carbon atoms), or phenyl, as well as substituted hydrogen, chlorine or alkoxy (1 to 4 carbon atoms) groups. Suitable silicone oils for use herein viscosity from about 0.5 centistokes to about 2,500,000 centistokes and preferably from about 500 to about 1,000,000 centistokes. Preferred silicone oils are linear polydimethylsiloxanes, with trimethylsiloxy terminated polysiloxanes and derivatives thereof being most preferred. Silicone oils are added to the blocked polyurethane and crosslinked mixture at levels from about 1 part to about 100 parts per 100 parts by weight blocked polyurethane, and preferably from about 5 parts to about 80 parts per 100 parts of blocked polyurethane. The blocked polyurethane prepolymer can be prepared by first mixing a hydroxy terminated polyolefin, such as hydrogenated hydroxy terminated polybutadiene with dry toluene. A catalyst, such as dibutyltin dilaurate, may be added, if desired. The dried hydroxy-polyolefin solution is added slowly to a solution of diisocyanate in anhydrous toluene over a time period of about 0.5 to 2 hours, under nitrogen, while vigorously agitating the resulting mixture at temperatures of about 100°C to about 120°C. Agitation can continue until the isocyanate content reaches approximately the calculated theoretical level. Thereafter, a blocking agent is added to the mixture and allowed to react with the terminal NCO groups. The blocking reaction may be monitored by transmission IR or by titration of the NCO with dibutylamine. The resulting blocked polyurethane prepolymer solutions are then compounded with silicone oil and a crosslinking agent to form the thermosetting polymeric binder, in accordance with the present invention. Compounding additives, such as micropowders of fumed silica, nylon, polyethylene, Teflon, polystyrene, molybdenum disulfide, glass beads, and the like, which serve as fillers to control viscosity and provide a flat, non-glossy appearance, proper hardness and toughness, to the applied cured coating film may be added to the polymeric binder mixture. Micropowders may be added on a weight basis, from about 5 to about 60 parts per 100 parts, by weight, of organic coating components (binder). Toluene, xylene, and/or 1,1,1-trichloroethane can be added, if desired, to provide minor adjustments to suit the individual coating process used to apply the coating to the substrate. Pigments such as carbon black, titanium dioxide, or similar color opacifying pigments may be added if desired. COATING RESIN The coating material resin, which is blended with the above-noted adhesion promoter polyurethane is generally a resin which heretofore required a primer on the substrate in order to have good adhesion thereto. That is, according to the present teachings, utilization of small amounts of the above-described adhesion promoter resin eliminates the need to prime the substrate. Such coating material resins are various polyurethanes which serve either as a cosmetic coating or a functional coating, i.e., possess one or more particular end-use properties such as high abrasion resistance, low friction, long shelf life, good release properties, etc. Such polyurethanes are generally known to the art and to the literature and also include conventional types of polyurethanes. Blocked polyurethane resins are preferred. The various one or more coating material resins which are blended with the adhesion promoter resin are applied to the substrate and subsequently cured. Curing, which generally involves crosslinking and/or chain extension, can be achieved in a number of ways by moisture cure and/or by utilizing various one or more types of curing agents. The curing agent can actually be a part (that is, reacted therewith) of the prepolymer of either the adhesion promoter resin, the coating material resin, or both, or separate therefrom. In other words, cure can be effected in any manner known to the art or to the literature. Thus, when moisture cure is utilized, the blocked isocyanate groups of either the adhesion promoter, the coating material resin, or both, are reacted with the moisture in the air and generally chain extend the prepolymer in a known manner as by the formation of amine-terminated compounds. The curing agent can be a triisocyanate which is already contained in the prepolymer as of the adhesion promoter resin, the coating material resin, or both. Additionally, curing agents per se, such as various crosslinking agents, can be added to either the adhesion promoter resin, the coating material resin, or both and, upon cure, serve to generally crosslink or form a branch network. Various types of curing agents and crosslinking agents are discussed hereinbelow. The amount of the curing agent(s) is of sufficient or effective amount to generally cause partial crosslinking or branching. That is, the amount is such that upon cure, the range of desired physical or performance properties sought are improved to a desirable degree. Of course, if desired, the amount of cure can be total. The various known or conventional polyurethanes which can be utilized as the coating material resin are generally urethanes made from hydroxyl-terminated polyester, polyether, or mixed polyester-polyether intermediates. The various hydroxyl terminated intermediates are generally reacted with a polyisocyanate to form a prepolymer which is subsequently blocked. When a hydroxyl-terminated polyether is utilized as an intermediate, the polyether portion is made from oxyalkylene compounds having from 2 to 6 carbon atoms, and preferably 2 or 3 carbon atoms, e.g., ethylene oxide, propylene oxide, butylene oxide, isobutylene oxide, etc., with ethylene oxide, propylene oxide, or combinations thereof being preferred. The weight average molecular weight of such polyether intermediates is generally from about 500 to about 15,000, with from about 1,000 to about 8,000 being preferred. The hydroxyl-terminated polyester intermediates are generally made from glycols having from about 2 to about 10 carbon atoms, and desirably from about 2 to about 6, with specific examples including ethylene glycol, propylene glycol, butylene glycol such as 1,4-butane diol, hexamethylene glycol, and the like, with hexamethylene glycol being preferred. The dicarboxylic acids utilized to form the hydroxyl-terminated polyester intermediate can either be aliphatic, aromatic, or combinations thereof and generally contain 2 to 15 carbon atoms with specific examples including succinic acid, glutaric acid, adipic acid, pimelic acid, azelaic acid, phthalic acid including terephthalic and isophthalic acid, and the like. Generally, adipic acid, terephthalic acid, phthalic acid, or combinations thereof are preferred. The weight average molecular weight of the hydroxyl-terminated polyester intermediate is generally from about 500 to about 15,000, and preferably from about 1,000 to about 8,000. Blends of one or more hydroxyl-terminated polyethers and/or one or more hydroxyl-terminated polyesters can be utilized to form the intermediate material for the polyurethane-type coating material resin. As part of the composition form of the prepolymer, various polyols can be utilized which are often referred to as chain extenders, and/or crosslinking agents. The same is discussed hereinafter in great detail and are utilized in small amounts and generally have an average of greater than two hydroxyl groups whenever it is desired that the prepolymer be branched so that upon curing in the presence of heat, a cured or crosslinked polyurethane is obtained. Examples of such compounds include glycerol, erythritol, trimethylol propane, and the like. Considering the polyisocyanate compounds which can be utilized to form the prepolymer, they can generally be represented by the formula: R(N=C=O) n where n is from about 1.8 to about 4 and preferably from about 2 to about 2.5. When n is greater than 2.0, it serves as a curing agent, that is, a crosslinking or branching agent. Preferably, n is approximately 2.0. The equivalent mole ratio of NCO to OH of the hydroxyl terminated intermediate is generally from about 0.8 to about 4.0, and desirably from about 0.9 to about 1.5 and preferably about 1.0. When moisture cure is desirable, the NCO/OH equivalent mole ratio is generally greater than 1.0, as from about 1.01 to about 3.0, and desirably from about 1.02 to about 1.5. Examples of suitable polyisocyanates include compounds wherein R is an aliphatic such as an alkyl having from 2 to 20 carbon atoms, a cycloaliphatic or, preferably, a cycloalkyl, containing from 4 to about 20 carbon atoms, an aromatic containing from 6 to about 20 carbon atoms, or combinations thereof, e.g., alkyl-substituted aromatic, etc. Suitable diisocyanates include meta- or para-phenylene diisocyanate, diphenyl methane diisocyanates, bitolylene diisocyanates, dianisidine diisocyanates, isophorone diisocyanates, toluene diisocyanates, hexamethylene diisocyanate and pentamethylene diisocyanate. Preferred aliphatic diisocyanates include 1,6-hexane diisocyanate, mixed trimethylhexane diisocyanate (TMI), isophorone diisocyanate (IPDI), and the like. Preferred aromatic diisocyanates include 4,4-methylene diphenyl isocyanate (MDI), as well as modified MDI known as Isonates (Dow Chemical), toluene diisocyanate (TDI) such as the 2,4-or 2,6-isomers, as well as mixtures thereof, 1,4-phenylene diisocyanate, m- and p-xylenene diisocyanates (XDI), and the like. Specific examples of triisocyanates include diphenyl diisocyanates, 2,4,4'-triisocyanatediphenyl ether, triphenyl methane triisocyanate, benzene-1,2,4-triisocyanate, naphthalene-1,3,7-triisocyanate, Desmodur® N-3300, an aliphatic polyisocyanate base upon hexamethylene diisocyanate, and the like. Whenever a triisocyanate is utilized to effect crosslinking, the amount thereof is very small, that is, an effective amount to improve desired processing or coating performance, i.e., physical properties, and can be an equivalent ratio as noted hereinabove. Mixtures of various polydiisocyanates can be used if desired. The polyurethane coating material resin made from a hydroxyl-terminated polyester, polyether, etc., and the polyisocyanate is desirably blocked. Simple blocking agents are the same as set forth hereinabove with regard to the hydroxyl-terminated polyolefin intermediate. Rather than to repeat the same, briefly, such blocking agents include various lactams having from about 3 to about 12 carbon atoms, various ketoximes having from about 3 to about 20 carbon atoms, various phenols containing from 3 to about 20 carbon atoms, various cyclic ureas having from about 3 to about 12 carbon atoms, various enamines having the formula where R 1 and R 2 , independently, is an alkyl having from 1 to 4 carbon atoms can also be utilized. Another group of blocking agents are the various dicarbonyl compounds having the general formula where R 3 and R 4 , independently, is an alkyl having from 1 to 6 carbon atoms, phenyl, or R 5 O, where R 5 is hydrogen or an alkyl having from 1 to 12 carbon atoms such as: acetylacetone, diethylmalonate, dimethylmalonate, acetylethyl acetate, and the like. Still other blocking agents include benzotriazole, the various phenylimidazoles, and the like. Desirably, the amount of blocking agent is an equivalent excess as from about 0.9 to about 1.5, and preferably from about 1.01 to about 1.20 based upon the ratio of blocking agent to NCO groups. The above blocked polyurethane prepolymer generally constitutes the coating material resin when the same is a polyurethane. The coating material polyurethane resin can optionally contain curing agents therein either as part of the blocked prepolymer (that is, reacted therewith) or in addition thereto (that is, in admixture therewith). A specific type of curing agent are the various chain extenders which are generally polyols containing a total of from about 2 to about 15 carbon atoms, and preferably from about 2 to about 6 carbon atoms. The number of active hydroxyl groups therein is generally two, unless it is desired that the chain extender also act as a crosslinking agent wherein the number of hydroxyl groups is generally three, four, or the like. Of course, blends of various polyols can be utilized in which event the number of hydroxyl groups is not necessarily an integer, but some number greater than two. Examples of suitable chain extenders include ethylene glycol, propylene glycol, butane diol such as 1,4-butane diol, dipropylene glycol, diethylene glycol, and the like. Another preferred class are the various polyhydric alcohols having from 3 to 15 carbon atoms and preferably from 3 to 10 carbon atoms and from 3 to 8 hydroxyl groups such as triols, tetraols, pentols, hexols, and the like with specific examples including glycerol, erythritol, pentaerythritol, arabitol, sorbitol, trimethylol propane; and the various ethylene or propylene oxide adducts of trimethylol propane, glycerol, pentaerythritol, sorbitol, and the like. If a chain extender is utilized, the amount thereof is generally less than 10.0 percent by weight based upon the weight of the urethane prepolymer resin, and desirably less than 5.0 percent by weight. When a triol, etc., is utilized to crosslink or branch the prepolymer, the amount thereof is of a sufficient or effective amount to increase the desired physical or processing properties thereof. Such an amount can vary inasmuch as other curing agents can be utilized such as an excessive diisocyanate, crosslinking agents per se, and the like. When the curing agent is a crosslinking agent per se, it is generally the same as noted hereinabove with regard to the polyolefin intermediate, and includes compounds or agents containing -NH 2 , -NHR 6 , etc. groups where R 6 is an alkyl having from 1 to 4 carbon atoms, -OH or -SH groups, and the like. Particularly preferred curatives, or crosslinking agents, can be the same as set forth hereinabove with regard to preparation of the adhesion promoter resin and thus are hereby fully incorporated by reference. Hence, particularly preferred curative, crosslinking, or branching agents include aliphatic, primary or secondary di-, tri-, and tetra-functional amines having a boiling point above about 100°C and preferably above 180°C. Useful amine crosslinking agents include, for example, polyoxypropylene- or polyoxy(propylene/ethylene)-based primary di- and triamines sold by Texaco Chemical Company under the tradename "Jeffamine," which are herein fully incorporated by reference, such as T-403 (triamine; MW about 480), EDR-148 (diamine; MW about 150), T-3000 (triamine; MW about 3,000), T-5000 (triamine; MW about 5,000), D-230 (diamine; MW about 200), D-400 (diamine; MW about 400), or D-2000 (diamine; MW about 2,000). Other crosslinking agents include polyamine resins containing amino end groups, sold by Henkel Corporation under the tradenames "Versamid" or "Genamid," which are hereby fully incorporated by reference, such as Versamids 100, 115, 125, 140, 150, 250, or Genamids 250, 747, 2000, and the like. Still other useful amine curatives include isophoronediamine (Huels Co.), mixed trimethylenediamine (TMD; Huels Co.), N,N'-diaminoethylpiperazine, N-aminoethylpiperazine, 1,4-cyclohexanediamine, 1,6-hexanediamine, 1,4-butanediamine, diethylenetriamine, m- or p-xylylenediamine, ethylenediamine, liquid poly(dimethylsiloxane)-diamine; various aromatic di- or triamines, which are liquid, or low melting, soluble or dispersible in the coating mixture, such as a ring methylated phenylenediamine (RDX-66884, sold by Interez Co.) or poly(tetramethylene oxide)-bis-(4-aminobenzoates) (Polyamine-650 and -1000 sold by Air Products), and the like. Moreover, crosslinking agents can include various compounds having at least one amine group therein and one or more OH, SH, and the like groups therein, with specific examples including triethanolamine, diethanolamine, ethanolamine, and the like. Preferred crosslinking agents include polyoxypropylene triamine, and 2-ethyl-2-hydroxymethyl 1,3-propane diol. The amount of the crosslinking agent is generally sufficient to achieve partial cure and thus is an amount to suitably increase desired processing and/or physical properties. Such an amount will vary with regard to desired end use as well as with regard to whether or not other types of curing agents are utilized. Regardless of the type of curing agent located within the prepolymer or as a separate compound in a system therewith, and regardless of whether it is a triisocyanate, etc., a chain extender, a crosslinking agent per se, or the like, generally the amount thereof is less than 100 parts by weight and desirably less than 30 parts by weight based upon 100 parts by weight of the appropriate resin, that is, the adhesion promoter resin or the coating material resin. A particularly preferred polyurethane coating material resin is made from a blend of the following two formulations wherein the amount of the polyether intermediate is generally from about 2 to about 4, and desirably about 3 times that of the polyester intermediate system: As apparent from the above, the polyether urethane intermediate is a blocked prepolymer which has been blocked with methylethylketoxime and yet contains the indicated amount of reacted trimethylol propane therein as a curing agent. Similarly, the polyester urethane intermediate system also contains a blocked prepolymer which has been blocked with methylethylketoxime, and the indicated reacted amount of trimethylol propane therein as a curing agent. The above blend composition is utilized as a coating material resin containing the indicated curing agents therein in the various examples set forth hereinbelow. The blocked urethane prepolymer resins which are utilized as a coating material resin can contain various additives therein in conventional amounts such as silicone oil, various fillers such as nylon powder to improve abrasion resistance, silica, talcs, clays, and the like, various antioxidants, ultraviolet light stabilizers, various pigments such as titanium dioxide or carbon black, and the like. The blocked urethane prepolymer coating material resins and the adhesion promoter resin are mixed or blended in any conventional manner to form a physical blend which is then applied to a substrate as noted hereinabove. The physical blend or admixture, as noted above, will contain one or more curing agents therein as well necessary or desirable additives, as also noted above. Such curing agents and any optional additives can be added with either the adhesion promoter resin or the coating material resin, or both. If not moisture cure at ambient temperatures, cure of the physical coating blend composition is generally at a temperature of from about 93°C (200°F) to about 232°C (450°F), or higher or lower depending upon the particular composition. The cured physical blend composition is actually the reaction product of the one or more curing agents which exists as a separate compound or as a part of the prepolymer in either the adhesion promoter resin, or in the blocked urethane coating material resin, or both. In other words, the end product is a statistical reaction product in which a particular curing agent (if an unreacted compound is used) can react with either the blocked polyurethane adhesion promoter resin, or with the blocked polyurethane coating material resin, or both. Of course, the curing agent can be part of the blocked polyurethane prepolymer of one or both systems. Thus, it should be appreciated that many generally conventional curing agent routes can be utilized as known to the art and to the literature. If the substrate is a rubber and uncured, it can be co-cured at the same time with the polyurethane coating material resin at generally the same temperature. The coating material containing the adhesion promoter resin therein can provide a functional end use such as low friction, high abrasion resistance, and the like, or serve as a cosmetic coating e.g. to contain a pigment yielding a desirable aesthetic effect. SUBSTRATE Examples of suitable rubber substrates include generally those made from conjugated dienes having from 4 to 12 carbon atoms such as butadiene, isoprene, and the like; copolymers of a rubber made from a conjugated diene having from 4 to 12 carbon atoms as set forth immediately hereinabove and a vinyl substituted aromatic having from 8 to 12 carbon atoms such as styrene, alpha methyl styrene, and the like with a specific example being styrene butadiene rubber; various nitrile rubbers which are generally copolymers of acrylonitrile and a conjugated diene having from 4 to 12 carbon atoms and preferably butadiene; ethylene propylene rubber, ethylene propylene diene-monomer rubber (EPDM) wherein the diene monomer is a non-conjugated diene such as cyclopentadiene, methylnorbornene, ethylnorbornene, and the like. Suitable substrates also include various thermoset or thermoplastic polyolefins containing repeat units having from 2 to 5 carbon atoms, such as polypropylene, polyethylene and the like. The preferred substrate of the present invention is EPDM. The above substrates are well known to the art and to the literature and generally the exact chemical make-up thereof is not critical to the present invention. The present invention will be better understood by reference to the following examples. ADHESION PROMOTER RESIN EXAMPLES Please refer to EP-A-430421, pages 6 to 17 which exemplify preparations and properties of the resins useable as adhesion promoter resins herein. These examples are incorporated herein by reference. COATING COMPOSITION EXAMPLES Example "S" A urethane coating material resin according to the present invention was prepared utilizing the following components: a urethane coating material resin obtained by preparing a urethane having methyl-ethyl-ketoxime blocked NCO groups having the composition of formulation "AA" - 65.57 parts by weight; a urethane coating material resin obtained by preparing a urethane having methyl-ethyl-ketoxime blocked NCO groups having the composition of formulation "BB" - 21.89 parts by weight; silicone oil (Union Carbide L-45) - 6.97 parts by weight; nylon powder (Rilsan 1510/50) - 3.98 parts by weight; fumed silica (Degussa TS100) - 1.00 part by weight. EXAMPLE 1 A two percent toluene solution of MDI-capped and caprolactam-blocked Polytail H urethane prepolymer, prepared in a manner very similar to Resin I set forth in EP-A-430421, was mixed with the coating composition of Example "S" on a 1 to 1 weight ratio. The prepared mixture was brush-applied to a piece of cured EPDM glass run channel, the solvent was flashed off, and the coating heated in a hot air oven at 204°C (400°F) for five minutes. Coating maturation was allowed to occur for one day. The coating-EPDM rubber adhesion strength was then tested by the procedures described in Appendix 1. The failure mode was 100 percent rubber tear (demonstrating coating-rubber adhesion strength higher than rubber cohesive strength) compared with the coating peel-off result when the adhesion promoter resin was not utilized. This test shows that ≤ 1 percent of the adhesion promoter Resin I product is good enough to produce a strong adhesion of the coating to the EPDM vulcanizate. EXAMPLE 2 The blocked urethane coating material resin of Example "S" containing seven different concentrations of the caprolactam-blocked urethane prepolymer resin (which was prepared very similarly to Resin I of EP-A-430421) of 0, 0.5, 1.5, 2.0, 3.0, 4.0, and 5.0 were prepared. Each of the prepared mixtures was brush-applied to a piece of green (uncured) EPDM glass run channel, the solvent was flashed off, and the coating was heated in a hot air oven at 204°C (400°F) for five minutes. Coating maturation was allowed to occur for one day. The coating-EPDM rubber adhesion strength was then tested by the procedures described in Appendix 1. The failure modes were as follows: Amount of the Adhesion Promoter Failure Mode (Adhesion Content (%) 0 Coating-rubber adhesive Failure (poor) 0.5 Coating-rubber adhesive Failure (poor) 1.5 Coating-rubber adhesive Failure (poor) 2.0 Coating-rubber adhesive Failure (poor) 3.0 Coating-rubber adhesive Failure (poor) 4.0 100% rubber tear (good) 5.0 100% rubber tear (good) This test result shows that at least 3 percent of the adhesion promoter resin is necessary to get good adhesion to green EPDM rubber. EXAMPLE 3 Each of 2 percent and 4 percent toluene solutions of MDI-capped and caprolactam-blocked Polytail HA adhesion promoter resin which was prepared very similarly to Resin I of EP-A-430421 was added to the coating composition of Example "S" on a 1 to 1 weight ratio. Each of the mixtures was spray-applied to a piece of cured (vulcanized) EPDM glass run channel, and the solvent was flashed off. Coating maturation was allowed to occur for one day, and the coating adhesion strength was then tested by the procedures described in Appendix 1. The failure mode was 100 percent rubber tear for both of the specimens. Crockmeter abrasion resistance at 3 kg load and 60 cycles per minute were also measured for both of the coating specimens, with the following results: Amount of Polytail HA Version of Resin I Crockmeter Abrasion Resistance (Cycles) 1% 3,255 2% 3,255 Without coatings, the Crockmeter abrasion resistance is very low and friction is very high. EXAMPLE 4 The coating composition of Example "S" with addition of one part by weight of fumed silica (Degussa TS100) per 100 parts of Example "S" coating composition was mixed with 25 percent of MDI-capped methylethyl ketoxime-blocked Polytail H adhesion promoter resin which was prepared very similarly to Resin I in EP-A-430421. The mixture was brush-applied to a piece of green (uncured) EPDM glass run channel, the solvent was flashed off, and the coating was heated at 204°C (400°F) for five minutes in a hot air oven. Coating maturation was allowed to occur for one day. The coating adhesion strength, coating thickness, and Crockmeter abrasion resistance were then measured in accordance with the adhesion test method described in Appendix 1. The coating thickness was measured by an optical microscope. The Crockmeter abrasion resistance was measured at 3 kg load and 60 cycles per minute at 152mm (six-inch) long amplitude. The results were 100 percent rubber tear (good adhesion), 20,400 cycles for Crockmeter abrasion resistance, and 25-50 µm (average 37.5 µm) for the coating layer thickness. The average Crockmeter abrasion resistance index is calculated to be 544 cycles per one µm. EXAMPLE 5 A coating material resin mix was prepared by the following formulation: Example "S" coating composition with additional 0.5 part by weight of fumed silica (Degussa TS100) per 100 parts of Example "S" coating composition - 35.35 (parts by weight); MDI-capped and Methylethylketoxime-blocked Polytail H resin from Example 4 - 3.54 (parts by weight); Toluene 31.8 (parts by weight); 1,1,1-trichloroethane 29.2 (parts by weight). The above blended resin composition was mixed with a triamine crosslinking agent (Jeffamine T403 from Texaco Chemical Company) of eleven different concentrations of 0, 0.2, 0.4,...1.8 parts per 100 parts of the coating material resin. Each of the eleven mixtures was spray-applied to a piece of a precoated EPDM glass run channel with the coating material resin of Example "S" with 5 percent of the adhesion promoter of Example I. After the solvent was flashed off, each of the doubly coated sample specimens was heated for five minutes in a hot air oven at 149°C (300°F) or 204° (400°F). After one day and three days, each of the sample specimens was tested for the coating adhesion strength by the procedures described in Appendix 1. The test results are shown in Table IV. The test results show that the use of methylethylketoxime blocked adhesion promoter together with ≥ 22 percent NH 2 /NCO stoichiometric amount of Jeffamine T403 (≥ 0.60 part) allows the coating to cure at 149°C (300°F) For five minutes, compared with 204°C (400°F) for five minutes when Jeffamine T403 was omitted, and that high levels of Jeffamine T403 (≥1.2 parts, ≥44 percent) do not lower the curing temperature, however, shorten the maturation time. APPENDIX 1 COATING ADHESION TEST Scope: This procedure describes the materials and test method required to measure the adhesion strength of urethane coatings to EPDM substrates. Materials Required: 1. Primer: Loctite Polyolefin Surface Primer Primer Number 757 2. Adhesive: Loctite 454 Gel (Surface Insensitive Cyanoacrylate) 3. Metal Strips: 0.95 x 25 x 102mm (20GA X 1" X 4") Test strips Drill an 8mm (5/16") hole at one end of each strip, centered and approximately 6½mm (1/4") from the end. All metals must be epoxy coated. 4. Medium Binder Clips (3 required per test) 5. 13mm (1/2") Natural Bristle Brush (1 required) 6. Brush Cleaning Solvent: 1,1,1-Trichloroethane Test Method: 1. Apply the primer (757) evenly by brush to both the metal strip and the coated EPDM substrate. Allow at 30 seconds for solvent flash off. 2. Apply a bead of adhesive (454 Gel) [at 2mm in diameter and 75 mm in length] to the coated EPDM substrate. Place primed metal in contact with adhesive, back up rubber with another metal strip and clamp with three medium binder clips for five minutes. 3. Remove binder clips and activate the adhesive squeeze-out with a few drops of 757 primer. Do not stress the bond line for approximately ten minutes. 4. Test the coating adhesion either manually or with an Instron by performing a 180° peel test. Good coating adhesion should result in rubber tearing; poor adhesion will just remove the coating. Note: The cyanoacrylate adhesive reaches optimum cure after 24 hours. Therefore, any quantitative coating peel strength should be measured after 24 hours. As apparent from the above examples and data, it should be apparent that small amounts of an adhesion promoter resin as set forth herein effects a good bond to a rubber substrate when utilizing a polyurethane coating material resin.

Claims: A curable coating composition comprising a coating resin mixed with an adhesion promoter resin, the adhesion promoter resin constituting from 0.5 to 50 wt% of the combination of the adhesion promoter resin and coating resin and comprising a blocked polyurethane prepolymer which is the reaction product of hydroxy-functional hydrogenated polydiene or polyolefin intermediate, having on average more than 1.5 hydroxyl groups per molecule and a number average molecular weight in the range from 500 to 15000, with at least 1.8 equivalents of polyisocyanate, excess isocyanate groups being blocked with blocking agent, and the coating resin being polyurethane prepolymer, which may be blocked but is not polyurethane prepolymer derived from hydroxy-functional hydrogenated polydiene or polyolefin intermediates. A curable coating composition according to claim 1 in which the coating resin is a polyurethane prepolymer made from hydroxy-terminated polyester intermediate and/or hydroxy-terminated polyether intermediate reacted with a polyisocyanate. A curable coating composition according to claim 2 in which the polyester and/or polyether intermediate for the coating resin prepolymer has a molecular weight in the range 500 to 15000. A curable coating composition according to claim 2 or claim 3 in which the polyester and/or polyether intermediate for the coating resin prepolymer has a molecular weight in the range 1000 to 8000. A curable coating composition according to any one of claims 2 to 4, in which said polyether intermediate is a product of ethylene oxide and/or propylene oxide, and/or said polyester intermediate is a product of hexamethylene glycol with adipic acid, terephthalic acid or phthalic acid. A curable coating composition according to any one of claims 2 to 5 in which the polyisocyanate used to form the coating resin prepolymer accords with the formula R(NCO) n in which R has C 2-20 aliphatic, C 4-20 cycloaliphatic or C 6-20 aromatic moieties, or combinations thereof, and n is in the range from 1.8 to 4. A curable coating composition according to claim 6 in which the polyisocyanate used to form the coating resin prepolymer is toluene diisocyanate, 4,4'-methylene diphenylisocyanate, 1,4-phenylene diisocyanate, m- or p-xylenene diisocyanate, 1,6-hexane diisocyanate, mixed trimethylhexane diisocyanate, isophorone diisocyanate or a mixture of any of these. A curable coating composition according to any one of claims 2 to 7 in which the coating resin prepolymer is blocked. A curable coating composition according to any one of the preceding claims adapted for use on an uncured rubber substrate and containing from 5 to 40 wt% of the adhesion promoter resin based on the total weight of the adhesion promoter resin and the coating resin. A curable coating composition according to any one of claims 1 to 8 adapted for use on a cured rubber substrate and containing from 1 to 10 wt% of the adhesion promoter resin based on the total weight of the adhesion promoter resin and the coating resin. A curable coating composition according to any one of the preceding claims in which the polyisocyanate used to make the adhesion promoter resin accords with the formula R'(NCO) n in which R' is aromatic, aliphatic or a combination thereof and has from 4 to 100 carbon atoms, and n is 2, 3 or 4. A curable coating composition according to claim 11 in which R' has from 4 to 30 carbon atoms. A curable coating composition according to claim 12 in which the polyisocyanate used to make the adhesion promoter resin is selected from 4,4-methylene diphenylisocyanate, 2.4-toluene diisocyanate, 2.6-toluenediisocyanate, 1,4-phenylene diisocyanate and mixtures thereof. A curable coating composition according to any one of the preceding claims in which the hydroxy-functional intermediate for the adhesion promoter resin is the product of polymerising C 2-6 olefin monomer or C 4-20 diene monomer, with optionally up to 50 wt% of other ethylenically-unsaturated comonomer. A curable coating composition according to claim 14 in which the hydroxy-functional intermediate for the adhesion promoter resin comprises polydiene which is at least 95mol% hydrogenated. A curable coating composition according to any one of the preceding claims in which the hydroxy-functional intermediate for the adhesion promoter resin has a molecular weight in the range 1000 to 8000 and the approximate general formula in which the x and y units are randomly distributed, there may be additional OH groups, the ratio x/y is from 0.1 to 10 and the average number of OH groups per molecule is from 1.5 to 4. A curable coating composition according to any one of the preceding claims in which the hydroxy-functional intermediate for the adhesion promoter resin has a molecular weight in the range from 1000 to 8000. A curable coating composition according to any one of the preceding claims in which the hydroxy-functional intermediate for the adhesion promoter resin has on average from 1.8 to 6.0 hydroxy groups per molecule and the equivalent ratio of the polyisocyanate to the intermediate is in the range from 2 to 8. A curable coating composition according to any one of the preceding claims including a crosslinking curing agent. A curable coating composition according to any one of the preceding claims, comprising silicone oil and filler. A process comprising the preparation of a composition according to any one of claims 1 to 20 by mixing the adhesion promoter resin and coating resin. A coating process comprising applying a composition according to any one of claims 1 to 20 to a substrate and curing the composition. A coating process according to claim 22 in which the substrate is of rubber or polyolefin. A coating process according to claim 23 in which the substrate is of EPDM rubber. A coated substrate obtainable in accordance with any one of claims 22 to 24.

Inventors: CHIHARA KOHJI J, GOEWEY JAMES R, CHIHARA, KOHJI J., GOEWEY, JAMES R.
Applicants: GENCORP INC, GENCORP INC.
Application year: 1992
Main classification: C08G18
IPC codes: C09D201, C08G18, C09D175