METHOD OF PRODUCING VERTICAL MOSFETS

Abstract: A vertical power MOSFET which has a markedly decreased on-resistance per unit area. A groove having a gate structure is substantially formed by the LOCOS method prior to forming the p-type base layer and the n⁺-type source layer. Then, the p-type base layer (16) and the n⁺-type source layer (4) are formed by double diffusion being self-aligned with the LOCOS oxide film (65) and, at the same time, a channel (5) is set in the sidewall (51) of the LOCOS oxide film. Then, the LOCOS oxide film is removed to form a U-groove thereby to constitute the gate structure. That is, the channel is set by double diffusion which is self-aligned to the LOCOS oxide film, i.e., the channels are correctly set symmetrically in the sidewalls on both sides of the groove. Therefore, the position of the U-groove is not deviated with respect to the end of the base layer, and the length of the bottom surface of the U-groove can be minimized. This makes it possible to greatly decrease the size of the unit cell and to greatly decrease the on-resistance per unit area.

Description: The present invention relates to a vertical type MOSFET (Metal Oxide Semiconductor Field Effect Transistor) to be used as a semiconductor device for electric power, which is preferable in the case of adoption as MOSIC and the like in which an elemental article thereof or the semiconductor device for electric power is incorporated. The vertical type power MOSFET has many features such that it has excellent frequency characteristics, has a fast switching velocity, can be driven at low electric power and the like, so that it is recently used in many industrial fields. For example, in "Nikkei Electronics" published by Nikkei-McGraw-Hill, Inc. on May 19, 1986, pp. 165-188, it is described that the focus of development of the power MOSFET is migrating to low voltage resistant articles and high voltage resistant articles. Further, it is described in this literature that the ON-resistance of a power MOSFET chip having a voltage resistance not more than 100 V has become low up to a level of 10 mΩ, and it is described as a reason thereof that the channel width per area has been able to be made large by utilizing the fine processing of LSI in the production of the power MOSFET, or by improving the shape of its cell. In addition, in this literature, the description is made using the vertical type power MOSFET as a main topic in which a DMOS type (double diffusion type) cell which is in the main current is used. The reason is that the DMOS type is fabricated by the planar process characterized in that the flat main surface of a silicon wafer is exactly used for a channel portion, so that it has advantages in production of a good yield and a cheap cost. On the other hand, in accordance with popularization of the vertical type power MOSFET, the realization of low loss and low cost is further demanded, however, the reduction in the ON-resistance by the fine processing or the improvement in the shape of the cell has arrived at the limit. For example, according to the official gazette of Japanese Patent Application Laid-open No. Sho 63-266882 (1988), it has been known that the DMOS type has a local minimum point in which the ON-resistance does not further decrease even when the size of the unit cell is made small by the fine processing, and a major cause thereof is the increase in the JFET resistance which constitutes a component of the ON-resistance. In addition, with respect to the DMOS type, as shown in the official gazette of Japanese Patent Application Laid-open No. Hei 2-86136 (1990), the size of the unit cell with which the ON-resistance provides the local minimum point is in the vicinity of 15 µm under the present fine processing technique. In order to break through this limit, various structures have been proposed. The common feature among them is a structure in which a groove is formed on the device surface, and channel portions are formed at side faces of the groove, and owing to this structure, the above-mentioned JFET resistance can be greatly decreased. Further, in the structure in which the channel portions are formed at the side faces of the groove, the increase in the JFET resistance can be neglected even when the unit cell size is made small, so that there is no limit that the ON-resistance provides the local minimum point with respect to the reduction in the unit cell size as described in the official gazette of Japanese Patent Application Laid-open No. Sho 63-266882 (1988), and it can be made small to the limit of the fine processing breaking though 15 µm. The structure, in which the channel portions are formed at the side faces of the groove, is called the R (Rectangular)-MOS or the U (U-shaped)-MOS according to its shape. The structure shown in the official gazette of Japanese Patent Application Laid-open No. Sho 59-8743 (1984) is an example of the R-MOS, which is a structure alternatively called the trench gate type in which a vertical groove is formed at the device surface by means of the anisotropic dry etching method, and channels and a gate are formed at sidewall portions of this groove, and this can completely extinguish the JFET resistance component. On the other hand, the structure shown in the official gazette of Japanese Patent Application Laid-open No. Hei 2-86171 (1990) is an example of the U-MOS in which the anisotropic wet etching of silicon or the LOCOS oxidation (Local Oxidation of Silicon) method is used as a method for processing the channel portion into the U-groove shape, and this can also greatly reduce the JFET resistance component. Typical conventional examples of the vertical type power MOSFET in which the channel portions are formed at the side faces of the groove are shown in Fig. 14 (R-MOS) and Fig. 15 (U-MOS). At first, the R-MOS shown in Fig. 14 will be explained. In this vertical type power MOSFET, at the surface layer portion of an epitaxial layer 2 comprising an n - -type layer provided on a main race of a semiconductor substrate 1 comprising an n + -type silicon, a p-type diffusion layer and an n + -type diffusion layer are successively formed by ion implantation and thermal diffusion. Next, in order to allow parts of these p-type diffusion layer and n + -type diffusion layer to remain as a p-type base layer 16 and an n + -type source layer 4 respectively, the reactive ion etching method is used to perform etching until the penetration though the p-type diffusion layer in the vertical direction with respect to the silicon substrate, so as to form a trench groove 50. A gate oxide film 8 is formed on an inner wall 51 of this trench groove 50, on which a gate electrode 9 is formed. Thus channels 5 are formed at sidewall portions of the inner wall 51, and the channel length is determined by a thickness of the p-type base layer 16. The ohmic contact is made for a source electrode 19 with the n + -type source layer 4, and for a drain electrode 20 with the back face of the semiconductor substrate 1, respectively. In this R-MOS, the ON-resistance between the drain and the source thereof is approximately the same as a sum of a channel resistance and a resistance of the n--type drain layer 6, in which there is no JFET resistance which has been a problem in the above-mentioned DMOS type. Therefore, the ON-resistance monotonously decreases in accordance with the reduction in the unit cell size a'', the reduction can be made up to 5 to 6 µm which is the limit in the present fine processing, and the ON-resistance per area can be greatly reduced as compared with the DMOS type. However, the R-MOS has such drawbacks that the yield and the reliability are low. The cause is that the trench groove 50 is formed by the reactive ion etching method, so that the flatness of the sidewall surface of the inner wall 51 is bad to give many defects, and the film quality of the gate oxide film 8, which is formed by oxidizing the surface thereof, is bad. And the insulation inferiority of the gate oxide film, the decrease in the mobility due to the defect of the interface of the channel portion, and the change in the threshold voltage take place. As described above, the structure of the R-MOS has the advantage to greatly reduce the ON-resistance per area, whereas there are a problem of high cost resulting from the low yield, and a problem of difficulty to ensure the reliability due to the bad stability of the gate oxide film and the channel portion. On the contrary, in the U-MOS shown in Fig. 15, the anisotropic wet etching or the LOCOS oxidation method is used as the step for forming the U-groove instead of the reactive ion etching, so that the flatness of the sidewall surface is good, a U-groove 50 having an inner wall 51 with less defect can be formed, and the film quality of a gate oxide film 8 formed by oxidizing the surface thereof is also good. As a result, as for the fact that no insulation inferiority occurs, the characteristics of the channel portion can be made stable and the like, the vertical type power MOSFET having a high yield and reliability can be obtained. Fablication steps for this U-MOS will be explained in accordance with Fig. 16 to Fig. 19 and Fig. 15. In this vertical type power MOSFET, as shown in Fig. 16, using a mask of an insulation film 22 partially formed with a cycle of a size a' of a cell on the main surface of a wafer 21 provided with an epitaxial layer 2 comprising an n - -type layer provided on a main face of a semiconductor substrate 1 comprising n + -type silicon, boron is double diffused by selective ion implantation and thermal diffusion, so as to form a p-type diffusion layer 23 and a p + -type contact region 17. Next, after removing the insulation film 22, as shown in Fig. 17, using a mask of an insulation film 24 partially formed on the main surface of the wafer 21, phosphorus is diffused so as to form an n + -type diffusion layer 25 to overlap over p-type diffusion layers 23 of adjacent cells 15. Next, after removing the insulation film 24, as shown in Fig. 18, using a mask of an insulation film 26 partially formed on the main surface of the wafer 21, the U-groove 50 is formed by the anisotropic etching or the LOCOS oxidation method. By the formation of this U-groove 50, peripheral edge portions of the adjacent p-type diffusion layers 23 and the central portion of the n + -type diffusion layer 25 are removed, so as to form a p-type base layer 16 and an n + -type source layer 4 separated by the U-groove 50 for every unit cell having a unit cell size of a'. Next, after removing the insulation film 26, as shown in Fig. 19, a gate oxide film 8 is formed on the surface of the U-groove 50, and a gate electrode 9 comprising polysilicon is formed on this gate oxide film 8. Next, as shown in Fig. 15, an interlayer insulation film 18 is formed on the main surface of the wafer 21 so as to cover the gate oxide film 8 and the gate electrode 9, and the interlayer insulation film 18 is subjected to opening formation in order to expose parts of the p + -type base contact layer 17 and the n + -type source layer 4. A source electrode 19, which makes ohmic contact with the p + -type base contact layer 17 and the n + -type source layer 4, is formed on the main surface of the wafer 21. Further, a drain electrode 20 which makes ohmic contact with the back face of the semiconductor substrate 1 is formed, and the vertical type power MOSFET of the U-MOS structure is completed. This U-MOS shown in Fig. 15 has the feature that the yield and the reliability are high in a degree equivalent to the DMOS type, which is extremely excellent in this point as compared with the R-MOS. This is due to the fact that the U-groove 50 is formed by the wet etching of silicon or the LOCOS oxidation method, thereby the flatness of its inner wall 51 is good with less defect, and the film quality of the gate oxide film 8 formed by oxidizing the surface thereof is also good, and it becomes difficult to cause the insulation inferiority of the gate oxide film and the characteristic change of the channel portion. The ON-resistance between the drain ana the source of the U-MOS is approximately the same as a sum of a channel resistance and a resistance of the n - -type drain layer 6 in the same manner as the above-mentioned R-MOS, and the JFET resistance of a JFET portion 7 is sufficiently small. Thus, in the same manner as the above-mentioned R-MOS, the ON-resistance decreases monotonously in accordance with the reduction in the unit cell size a', however, it can be only made slightly smaller than about 15 µm of the DMOS type within the limit of the present fine processing, and cannot be made small into 5 to 6 µm of the R-MOS type. However, since the JFET resistance is sufficiently small, the ON-resistance per area is an intermediate value between those of the R-MOS type and the DMOS type. As described above, the U-MOS has such a structure in which the feature of the low ON-resistance of the R-MOS is partially inherited while maintaining the high production yield and the high reliability of the DMOS. In order to reduce the ON-resistance of the U-MOS to be equivalent to the R-MOS, it is necessary and indispensable to reduce the unit cell size a'. However, in the production method of the U-MOS shown in Figs. 16 to 19 and Fig. 15, the reduction in the unit cell size a' is difficult. The reason thereof will be explained hereinafter. At first, it will be explained in detail that by what the unit cell size of the U-MOS is determined. In Fig. 15, sizes of each of portions have relations as shown as follows. However, a' is a unit cell size, b' is a distance between upper ends of two adjacent U-grooves, c' is a distance between adjacent gate electrodes, d' is a size of a contact hole, and e' is a size of a portion of the base contact layer 17 exposed to the surface. In addition, α' is a plane distance between the center and the upper end of the U-groove 50, β' is a plane distance between the upper end of the U-groove 50 and the end of the gate electrode 9, γ' is a plane distance between the end of the gate electrode 9 and the end of the contact hole, and δ' is a plane distance between the end of the contact hole and the end of the portion of the base contact layer 17 exposed to the surface. In this case, in the present fine processing level, the adjustment accuracy of the mask is about 0.5 to 1 µm, and also considering the size accuracy in the etching processing and the like, each value in the above-mentioned formulae (1) takes, for example, the following value. β' = 1 [µm], γ' =1.5 [µm], δ' = 1 [µm], b' = 8.5 [µm], c' = 6.5 [µm], d' = 3.5 [µm], e' = 1.5 [µm] According to the formulae (1) and (2), the unit cell size a' is a' = b' + 2α' = 8.5 + 2α' [µm] wherein in order to reduce the unit cell size a', the value of the plane distance α' between the center and the upper end of the U-groove 50 is key. According to Figs. 16 to 18, it is understood that the size of α' is determined by the length of the bottom side and the processing accuracy of the U-groove 50, and the adjustment accuracy of the insulation film 26 (the mask for forming the U-groove) with respect to the p-type diffusion layer 23. Fig. 20 is a cross-sectional view of an important part including the U-groove 50 when a center line CL 1 between the two adjacent p-type diffusion layers 23 overlaps a center line CL 2 between the two adjacent insulation films 26, which corresponds to a case in which there is no mask deviation. In this case, α' is given by the following formula (4). α' = α' 1 + α' 2 + α' 3 However, α' 1 is 1/2 of a length with which the bottom side portion of the U-groove 50 contacts with the n--type drain layer 6, α' 2 is a length with which the bottom side portion of the U-groove 50 contacts with the p-type base layer 16, and α' 3 is a length of projection of the sidewall portion of the U-groove 50 onto the main surface of the wafer 21. In this case, the right and left α' 2 s are apparently equal in Fig. 20. However, in fact, due to the presence of the deviation of the mask adjustment, the right and left α' 2 s are different, so that it is necessary that α' 2 in each of the items in the formula (4) is set to be about 1.5 µm. The reason thereof is that when the mask adjustment of the insulation film 26 is the worst, on account of the mask adjustment accuracy in the present circumstance, as shown in Fig. 21, with respect the center line CL 1 between the two adjacent p-type diffusion layers 23, the center line CL 2 between the two adjacent insulation films 26 generates positional deviation (for example, 1 µm) in the right direction, and in order to prevent electric field concentration at the edge portion 12 so as to avoid the inconvenience resulting from dielectric breakdown of the gate portion even when such positional deviation takes place, for allowing the edge portion 12 at the groove bottom of the U-groove 50 not to be exposed to the n - -type drain layer 6 but to be positioned in the p-type base layer 16, it is necessary to make a design in which this positional deviation is taken into account. Therefore, the following formula (5) must be necessarily established with respect to lengths α' 21 and α' 22 with which the bottom side portions of the U-groove 50 contact with the p-type base layers 16. 0 < α' 21 , α' 22 In addition, with respect to α' 1 and α' 3 , both of them are about 0.75 µm in the present fine processing level, so that α' takes the following value according to the formula (4). α' = 0.75 + 1.5 + 0.75 = 3 [µm] Therefore, according to the formulae (3) and (6), the minimum value of the unit cell size a' is a ' = 8.5 + 2 x 3 = 14.5 [µm] As described above, in the production method of the U-MOS shown in Figs. 16 to 19 and Fig. 15, the reduction limit of the unit cell size a' is about 14.5 µm, which is approximately the same as 15 µm of the conventional DMOS type, and it has been difficult to remarkably reduce the ON-resistance per area. JP-A-62 46 569 and JP-A-63 94 687 discloses methods of manufacturing MOSFET's which have the feature that a gate oxide film formed in a groove in a semiconductor substrate is performed in such a manner that the thickness of the gate oxide film on the side walls of the groove is thinner than the thickness of the gate oxide film on the bottom of the groove. Due to this step of manufacturing the ON-resistance of the MOSFET can be reduced. DE-A-34 27 293 and JP-A-62 12 167 discloses methods of manufacturing a semiconductor device which constitute the preamble of claim 1. To further decrease the ON-resistance per area the semiconductor device is formed in such a manner that a base and source layer are formed self-aligned with a local oxide film formed in a groove, thereby the edge portion of the groove can be made with an improved symmetry for each cell resulting in improved properties of the semiconductor device such as an reduced ON-resistance per area. It is the object of the present invention to provide a production method of a vertical type power MOSFET in which the properties of the MOSFET such as the ON-resistance can be further improved. This object is solved by the measures indicated in the characterizing part of claim 1. Further advantage modifications are subject matter of the subclaims. In the drawings: Fig. 1 (a) is a plane view showing a part of a first vertical type power MOSFET useful for explaining the present invention, Fig. 1 (b) is a cross-sectional view taken along A-A in Fig. 1 (a), and Fig. 2 to Fig. 13 are cross-sectional views of important parts to be used for the explanation of production steps of the vertical type power MOSFET of Fig. 1. Fig. 14 is a cross-sectional view of a vertical type power MOSFET of the conventional R-MOS type, Fig. 15 is a cross-sectional view of a vertical type power MOSFET of the conventional U-MOS type, and Fig. 16 to Fig. 19 are cross-sectional views of important parts to be used for the explanation of production steps of the vertical type power MOSFET of the conventional U-MOS type. Fig. 20 is a cross-sectional view of an important part showing an ideal state in which the positional relation between an edge portion of a groove bottom face and a p-type base layer is in bilateral symmetry when the groove is formed in the production of the vertical type power MOSFET of the conventional U-MOS type. Fig. 21 is a cross-sectional view of an important part showing a practical state in which the positional relation between the edge portion of the groove bottom face and the p-type base layer is not in bilateral symmetry due to mask deviation when the groove is formed in the production of the vertical type power MOSFET of the conventional U-MOS type. Fig. 22 is a cross-sectional view of an important part of a second vertical type power MOSFET useful for explaining the present invention, Fig. 23 (a) is an illustrative plane view showing a part of a vertical type power MOSFET according to a second embodiment of the present invention, and Fig. 23 (b) is a cross-sectional view taken along B-B in Fig. 23 (a). Embodiments the present invention will be explained hereinafter with reference to the drawings. Fig. 1 (a) is a plane view of a first vertical power MOSFET comprising rectangular unit cells useful for explaining the present invention, and (b) in the same figure is a cross-sectional view taken along A-A in the same figure (a). Fig. 2 to Fig. 13 are also cross-sectional views of a wafer as a work in each step in the production of the vertical type power MOSFET, which correspond to Fig. 1 (b). Incidentally, Fig. 2 is a cross-sectional view of the wafer subjected to boron ion implantation for the formation of the central portion of a p-type base layer, Fig. 3 is a cross-sectional view of the wafer subjected to patterning of a silicon nitride film at an interval of a unit cell size a for the LOCOS oxidation, Fig. 4 is a cross-sectional view of the wafer in which a window of the silicon nitride film is subjected to wet etching, Fig. 5 is a cross-sectional view of the wafer in which a LOCOS oxide film is formed, Fig. 6 is a cross-sectional view of the wafer subjected to boron ion implantation for the formation of the p-type base layer using the LOCOS oxide film as a mask, Fig. 7 is a cross-sectional view of the wafer in which the p-type base layer is formed by thermal diffusion, Fig. 8 is a cross-sectional view of the wafer subjected to phosphorus ion implantation for the formation of an n + -type source layer using the LOCOS oxide film as a mask, Fig. 9 is a cross-sectional view of the wafer in which the n + -type source layer is formed by thermal diffusion, Fig. 10 is a cross-sectional view of the wafer in which a gate oxide film is formed by thermal oxidation after removing the LOCOS oxide film, Fig. 11 is a cross-sectional view of the wafer in which a gate electrode is formed on the gate oxide film, Fig. 12 is a cross-sectional view of the wafer subjected to boron ion implantation for the formation of a p + -type base contact layer, Fig. 13 is a cross-sectional view of the wafer in which the p + -type base contact layer is formed by thermal diffusion, and Fig. 1 (b) is a completed cross-sectional view of the wafer in which an interlayer insulation film, a source electrode and a drain electrode are formed. The vertical type power MOSFET of Fig. 1 has its important part, that is the unit cell portion which has a structure as shown in Fig. 1, which has a structure in which a large number of the unit cells 15 are regularly arranged vertically and laterally on a plane with a pitch width (unit cell size) a. In Fig. 1, a wafer 21 comprises a semiconductor substrate 1 and an n - -type epitaxial layer 2 thereon. The semiconductor substrate 1 is constituted of n + -type silicon having an impurity concentration of about 10 20 cm -3 and a thickness of 100 to 300 µm and the n - -type epitaxial layer 2 has an impurity concentration of about 10 16 cm -3 and a thickness of about 7 µm. And the unit cells 15 are constituted on the main surface of this wafer 21. In order to form a U-groove 50 on the main surface of the wafer 21 with a unit cell size of about 12 µm, a LOCOS oxide film having a thickness of about 3 µm is formed, and using this oxide film as a mask, the double diffusion in a manner of self-alignment is used to form a p-type base layer 16 having a junction depth of about 3 µm and an n + -type source layer 4 having a junction depth of about 1 µm, thereby a channel 5 is set at a sidewall portion 51 of the U-groove 50. Incidentally, the junction depth of the p-type base layer 16 is set to be a depth with which no destruction occurs due to breakdown at an edge portion 12 of the bottom side of the U-groove 50. In addition, in order to allow the junction depth of the central portion of the p-type base layer 16 to be deeper than those of surroundings, boron is beforehand diffused at the central portion of the p-type base layer 16, so as to be set to allow the breakdown to occur at the central portion of the bottom face of the p-type base layer 16 when a high voltage is applied between the drain and the source. In addition, after the double diffusion, the diffusion mask and the LOCOS oxide film used for the formation of the U-groove 50 are removed, a gate oxide film 8 having a thickness of about 60 nm is formed at the inner wall of the U-groove 50, and a gate electrode 9 comprising polysilicon having a thickness of about 400 nm and an interlayer insulation film 18 comprising BPSG having a thickness of about 1 µm are formed thereon. Further, at the surface of the central portion of the p-type base layer 16, a p + -type base contact layer 17 having a junction depth of about 0.5 µm is formed, and a source electrode 19 formed on the interlayer insulation film 18 makes ohmic contact with the n + -type source layer 4 and the p + -type base contact layer 17 through the contact hole. In addition, a drain electrode 20 is formed to make ohmic contact with the back face of the semiconductor substrate 1. In the vertical type power MOSFET shown in Fig. 1 as explained above, the LOCOS oxide film is used as the mask to double diffuse the p-type base layer 16 and the n + -source layer 4 by the self-alignment, so that it becomes unnecessary to take the adjustment accuracy of the mask into account, and in the above-mentioned formulae (1) to (7) established in the conventional U-MOS shown in Fig. 15, the length α 2 ' to contact with the p-type base layer 16 of the bottom side portion of the U-groove 50 can be neglected. Therefore, when each of the sizes other than α 2 ' is the numerical value as the prior art shown in the numerical formula 2, then in the structure of Fig. 1, according to the formula (7), the plane distance α between the center and the upper end of the U-groove 50 can be reduced from 3 µm up to 1.5 µm. As a result, the unit cell size a can be reduced up to 11.5 µm from 14.5 µm of the conventional U-MOS shown in Fig. 15, and the channel width per area can be taken widely, to make it possible to reduce on-resistance up to a value near the ON-resistance per area of the R-MOS shown in Fig. 14. Next, a production method of the first vertical type power MOSFET useful for explaining the present invention will be explained. At first, as shown in Fig. 2, a wafer 21, in which an n - -type epitaxial layer 2 is grown on the main surface of a semiconductor substrate 1 comprising n + -type silicon, is prepared. This semiconductor substrate 1 has its impurity concentration of about 10 20 cm -3 . In addition, the epitaxial layer 2 has its thickness of about 7 µm and its impurity concentration of about 10 16 cm -3 . The main surface of this wafer 21 is thermally oxidized to form a field oxide film 60 having a thickness of about 60 nm, and then a photoresist film 61 is deposited to perform patterning of the photoresist film 61 into a pattern opening to the central portion of a planned position of cell formation by means of known optical lithography steps. And using this photoresist film 61 as a mask, ion implantation of boron (B + ) is performed. After peeling off the resist, a p-type diffusion layer 62 having a junction depth of about 3 µm is formed by thermal diffusion as shown in Fig. 3. This p-type diffusion layer 62 ultimately becomes a part of a p-type base layer 16 as described hereinafter, and when a high voltage is applied between the drain and the source, the breakdown is allowed to occur stably at the bottom side portion of the p-type diffusion layer 62, thereby an object to increase the surge resistance is achieved. Next, as shown in Fig. 3, a silicon nitride film 63 is deposited on the main surface of the wafer 21 by about 200 nm, and this silicon nitride film 63 is subjected to patterning to form an opening pattern of a lattice shape opening with a pitch width (size of the unit cell 15) a. Incidentally, this opening pattern is subjected to mask adjustment so as to allow the above-mentioned p-type diffusion layer 62 to be positioned at the central portion of its pitch interval. Next, as shown in Fig. 4, the silicon nitride film 63 is used as a mask to etch the field oxide film 60, subsequently the n - -type epitaxial layer 2 is etched into a depth of about 1.5 µm to form a groove 64. Next, as shown in Fig. 5, the silicon nitride film 63 is used as a mask to thermally oxidize the portion of the groove 64. This is an oxidation method well-known as the LOCOS (Local Oxidation of Silicon), and a LOCOS oxide film 65 is formed by this oxidation, simultaneously with which a U-groove 50 is formed on the surface of the n - -type epitaxial layer 2 subjected to erosion by the LOCOS oxide film 65, and the shape of the groove 50 is decided. Namely, the distance b between upper ends of the adjacent U-grooves 50 is determined by a size of the silicon nitride film 63, which becomes slightly short due to side face oxidation by the so-called bird's beak. However, this reduction in the size is about 0.5 µm, and it can be controlled with a high accuracy. Incidentally, it is desirable that an inclination angle of the side face of the U-groove 50 with respect to the main surface or the wafer 21 is not less than 45°, which can be controlled by condition setting of the LOCOS oxidation or depth setting of the groove 64 formed prior to the LOCOS oxidation step. As described hereinafter, the distance b between the upper ends of the adjacent U-grooves 50 is about 8.5 µm. In addition, in Fig. 5, the plane distance a between the center and the upper end of the U-groove 50 is given by the formula (8) in the same manner as the case of the conventional U-MOS to be given by Fig. 20 and the formula (4). α = α 1 + α 2 + α 3 However, α 1 is 1/2 of a length to contact with the n - -type drain layer 6 of the bottom side portion of the U-groove 50, α 2 is a length to contact with the p-type base layer 16 of the bottom side portion of the U-groove 50, and α 3 is a length of projection of the sidewall portion of the U-groove 50 onto the main surface of the wafer 21. However, α 2 in the formula (8) can be omitted as described hereinafter, so that the formula (8) can be rewritten into the following formula. α = α 1 + α 3 Both α 1 and α 3 are about 0.75 µm in the processing technique in the present circumstance, so that a takes the following value. α= 1.5 [µm] Incidentally, the inner wall surface of the U-groove 50 formed by the LOCOS oxidation is flat and has less defect, and the surface has a good surface state in a degree equivalent to the initial main surface of the wafer 21 shown in Fig. 2. Next, as shown in Fig. 6, the LOCOS oxide film 65 is used as a mask to perform ion implantation of boron through the thin field oxide film 60 for forming the p-type base layer 16. At this time, the boundary portion between the LOCOS oxide film 65 and the field oxide film 60 makes a self-aligned position, and the region to be subjected to the ion implantation is exactly defined. Next, as shown in Fig. 7, thermal diffusion is performed to give a junction depth of about 3 µm. Owing to this thermal diffusion, the p-type diffusion layer 62 formed beforehand in the step shown in Fig. 3 is integrated with a diffusion layer of boron implanted in the step shown in Fig. 6, and one p-type base layer 16 is formed. In addition, both end faces of the region of the p-type base layer 16 are defined at the positions of the sidewalls of the U-groove 50 in a manner of self-alignment. Next, as shown in Fig. 8, using masks of both of the LOCOS oxide film 65 and the photoresist film 66 subjected to patterning with a pattern remained at the surface central portion of the p-type base layer 16 surrounded by the LOCOS oxide film 65 having been formed on the surface of the wafer 21 in the lattice-shaped pattern, ion implantation of phosphorus through the thin field oxide film 60 is performed for forming the n + -type source layer 4. Also in this case, in the same manner as the case in which boron has been ion-implanted in the step shown in Fig. 6, the boundary portion between the LOCOS oxide film 65 and the field oxide film 60 makes a self-alignment position, and the region to be subjected to the ion implantation is exactly defined. Next, as shown in Fig. 9, thermal diffusion is performed with a junction depth of 0.5 to 1 µm, so as to form the n + -type source layer 4 and simultaneously set the channel 5. In this thermal diffusion, the end face of the region of the n + -type source layer 4 to contact with the U-groove 50 is defined at the position of the sidewall of the U-grcove 50 in a manner of self-alignment. Setting of a junction depth of the p-type base layer 16 at the time point of completion of this thermal diffusion becomes important. Namely, when a high voltage is applied between the drain and the source of a completed article of the vertical type power MOSFET of the present example, it is important to set the junction depth of the p-type base layer 16 at the value not to be destroyed by the occurrence of breakdown at the edge portion 12 of the bottom face of the U-groove 50. This junction depth can be exactly defined by the thermal diffusion. As described above, in accordance with the steps in Fig. 6 to Fig. 9, the junction depth of the p-type base layer 16 and its shape are decided. The important fact with respect to the shape of this p-type base layer 16 is that the position of the side face of the p-type base layer 16 is self-aligned with the side face of the U-groove 50 and after that thermally diffused so that the shape of the p-type base layer 16 becomes completely bilateral symmetry with respect to the U-groove 50. As a result, the difference between the right and left contact lengths α' 21 and α' 22 resulting from the mask deviation of the bottom side portion of the U-groove 50 and the p-type base layer 16, which has occurred in the conventional U-MOS as shown in Fig. 21, always disappears in accordance with the production steps of the present invention, and the following formula is established. α' 21 = α' 22 Further, the junction depth of the p-type base layer 16 can be exactly determined by condition setting of the thermal diffusion, so that it becomes unnecessary to take the length α' 2 with which the bottom side portion of the U-groove 50 contacts with the p-type base layer 16 into account. Namely, in this case, α 2 can be omitted in the above-mentioned formula (8), and hence the above-mentioned formula (9) is established. Next, as shown in Fig. 10, the LOCOS oxide film 65 is removed by wet etching to make exposure of the inner wall 51 of the U-groove 50, and then the gate oxide film 8 having a thickness of about 60 nm is formed by thermal oxidation. As described above, the inner wall 51 of the U-groove 50 is a good silicon surface havinq good flatness and less defect, so that the film quality of the gate oxide film 8 made by thermally oxidizing this surface, the interface state density of the interface of the channel 5, and the carrier mobility are good in a degree equivalent to the conventional DMOS. Next, as shown in Fig. 11, a polysilicon film having a thickness of about 400 nm is deposited onto the main surface of the wafer 21, to form a gate electrode 9 in which patterning is made so as to be separated by the distance c being shorter than the distance b between the upper ends of the two adjacent U-grooves 50 by 2β. Taking the adjustment accuracy of the mask of 0.5 to 1 µm into account, when β is set to be about 1 µm so as to allow the gate electrode 9 to necessarily terminate at the flat portion of the main surface of the wafer 21, the separation distance c between the two adjacent gate electrodes 9 is 6.5 µm. As described above, the steps shown in Fig. 6 to Fig. 11 are most important parts of the production steps, wherein the LOCOS oxide film 65 is used as the mask for the double diffusion of the manner of self-alignment, the p-type base layer 16, the n + -source layer 4 and the channel 5 are formed, and then the LOCOS oxide film 65 is removed, after which the gate oxide film 8 and the gate electrode 9 are formed. Next, as shown in Fig. 12, using the photoresist film 68 subjected to patterning as a mask, boron is ion-implanted through the oxide film 67 for forming a p + -type base contact layer 17 . Next, as shown in Fig. 13, thermal diffusion is performed with a junction depth of about 0.5 µm, and the p + -type base contact layer 17 is formed. In this thermal diffusion, the size e of exposure of the p + -type base contact layer 17 to the surface is about 1.5 µm, which is determined by a pattern size of the photoresist film 68. And as shown in Fig. 1 (b), an interlayer insulation film 18 comprising BPSG is formed on the main surface of the wafer 21, a part of which is subjected to contact hole opening so as to expose the p + -type base contact layer 17 and the n + -type source layer 4. Further, a source electrode 19 comprising an aluminum film is formed, so as to make ohmic contact of the p + -type base contact layer 17 and the n + -source layer 4 through the above-mentioned contact hole. Further, for protection of the aluminum film, a passivation film (not shown in the figure) comprising silicon nitride or the like is formed by the plasma CVD method or the like, and a drain electrode 20 comprising three-layer film of Ti/Ni/Au is formed on the back face of the wafer 21, so as to make ohmic contact with the n + -type semiconductor substrate 1. As described above, in the structure and the production method of the vertical type power MOSFET explained using Fig. 2 to Fig. 13 and Fig. 1, the following effects are provided. (1) As compared with the conventional U-MOS shown in Fig. 15, a different factor among the conditions for determining the unit cell size a given by the formula (1) to the formula (7) is α shown by the formula (9) and the formula (10), which can be reduced into 1.5 µm from conventional 3 µm. As a result, according to the formula (3), the unit cell size a can be reduced from conventional 14.5 µm up to a value given by the following formula (12), and it is possible to allow the ON-resistance per area to further approach that of the R-MOS. a = 8.5 + 2 x 1.5 = 11.5 [µm] (2) The silicon surface on which the channel portion is formed is the silicon surface made by removing the oxide film formed by the LOCOS oxidation method by means of the wet etching, wherein the flatness of the surface is good, and there is no defect at all. Therefore, in relation to the film quality of the gate oxide film made by thermally oxidizing this surface, the problems of the insulation inferiority, the decrease in the mobility due to defect of the interface of the channel portion, the change in the threshold voltage and the like are small in a degree equivalent to the conventional DMOS type. As a result, the yield is high and the reliability is high. (3) Methods in which delicate management is required in production steps as represented by the reactive ion etching in the R-MOS are not used, but the LOCOS oxidation method, in which management of production is extremely easy and the size accuracy and the reproducibility are good, is used, so that the throughput and the yield in the production steps are high, and the production cost is also cheap. For example, in the structure shown in Fig. 22, a source electrode 19 is allowed to make ohmic contact with an n + -type source layer 4 and a p + -type base contact layer 17 through a groove 52, and especially there is given a structure in which the source electrode 19 makes ohmic contact with the side face of the n + -type source layer 4. In order to fabricate this structure, in the production steps shown in Fig. 2 to Fig. 13, the n + -source layer 4 is diffused and formed on the whole face of the upper face of the p-type base layer 16 to constitute the gate structure, and further when the contact hole is opened through the interlayer insulation film 18, a groove 52 may be formed penetrating through the interlayer insulation film 18 and the n + -type source layer 4 to arrive at the p + -type base contact layer 17. Incidentally, setting can be made variously such that the p + -type base contact layer 17 is formed beforehand before the formation of the n + -type source layer 4, is formed by performing ion implantation of boron with increasing the acceleration voltage after the formation of the n + -type source layer 4, is formed simultaneously with the n + -type source layer 4 by thermal diffusion using ion implantation of boron before thermal diffusion for the formation of the n + -type source layer or the like. According to this structure, it becomes unnecessary to take the plane distance 6 between the end of the contact hole and the end of the portion of exposure of the base contact layer 17 to the surface into account in Fig. 1 (b). Further, it is unnecessary to especially define the size e of the portion of exposure of the base contact layer 17 to the surface, and when the contact hole having a size of d is opened, the base contact layer 17 can be simultaneously exposed. Namely, according to the structure and the production method of the aforementioned structure, a part of the formula (1) to the formula (3) in relation to the conventional U-MOS is changed as follows. Therefore, according to the formula (13) and the formula (10), the unit cell size of the vertical type power MOSFET can be made small into not more than 10 µm as a''' = 6.5 + 2 x 1.5 = 9.5 [µm] the cell size equivalent to the conventional R-MOS becomes possible, and remarkable reduction in the ON-resistance can be contemplated. Moreover, in the same manner as in the first mentioned structure, the vertical type power MOSFET in which the yield and the reliability are high is obtained. Next, a first embodiment of the present invention will be explained. In the following explanation, referring to the production method of the first vertical type power MOSFET useful for explaining the present invention and its structural figures shown in Fig. 1 to Fig. 13, the explanation is made being limited to portions in which the first embodiment is different from the above-mentioned first structure or portions which are newly set in the first embodiment, and since the other portions are the same as those of the above-mentioned first structure, their explanation will be omitted. In the first embodiment, in Fig. 2, the wafer 21 is selected to have the index of plane of its main surface which is (1 1 1) or those near it. Thus the surface of the n - -type epitaxial layer 2 corresponding to the bottom face of the LOCOS oxide film 65 formed on the wafer 21 in the step shown in Fig. 5, that is the bottom face 53 of the U-groove 50 is parallel to the main surface, so that its index of plane is also (111). In addition, in Fig. 1 (a), owing to the optimization of the surface directions of the sides of the rectangular unit cell 15 with respect to the surface direction of the main surface of the wafer 21, and the optimization of the inclination angle of the side face 54 of the U-groove 50 by condition setting in the LOCOS oxidation step shown in Fig. 5, the index of plane of the side face 54 of the U-groove 50 is set to be an index near (1 0 0) in which the interface state density is less. Thus in the step for forming the gate oxide film 8 shown in Fig. 10, depending on the difference in the index of plane between the bottom face 53 (the index of plane is (1 1 1) as described above) of the U-groove 50 and the side face 54 (the index of plane is an index near (1 0 0) as described above), a step condition is selected in which the oxidation velocity is faster at the bottom face 53. Namely, a relatively rapid oxidation time in which the oxidation of silicon is controlled by rate-determination of reaction and a thin oxide film are necessary conditions, wherein the thin gate oxide film formation of about 60 nm satisfies the conditions. According to the conditions, the thickness t B of the gate oxide film formed on the surface of the bottom face 53 of the U-groove 50 becomes thicker than the thickness t S of the gate oxide film formed on the surface of the side face 54 of the U-groove 50. Namely, there is given t S < t B for example, following numerical values are obtained as t S and t B . t S = 60 [nm], t B = 80 [nm] Next, the function will be explained in which the first embodiment is superior to the first structure owing to its modification of its structure. In the first embodiment, as shown in the formulae (15) and (16), the thickness t B of the gate oxide film formed on the surface of the bottom face 53 of the U-groove 50 in Fig. 1 can be made thicker than the thickness t S of the gate oxide film formed on the surface of the side face 54 of the U-groove 50. Thus, even when a high voltage is applied between the drain electrode 20 and the source electrode 19, the electric field in the gate oxide film formed at the surface of the bottom face 53 of the U-groove 50 can be reduced, and the dielectric breakdown of the gate oxide film can be prevented. In addition, the gate input capacity of the bottom face portion of the U-groove 50 constituted by the bottom face 53 of the U-groove 50, the gate oxide film formed on its surface and the gate electrode 9 decreases in inverse proportion to the thickness of the gate oxide film, so that high-speed switching becomes possible. In addition, in the first embodiment, the index of plane of the side face 54 of the U-groove 50 is set to be an index near (1 0 0) in which the interface state density is less so as to provide a low interface state density of the channel portion 5, so that the stability of the threshold voltage is good, the mobility of the channel portion is not decreased, and the resistance to the hot carrier is also strong, so that the long-term reliability in electric characteristics of the vertical type power MOSFET can be maintained. As described above, in the first embodiment, since the explanation has been made only for the case of the rectangular unit cell shown in Fig. 1 (a), it was impossible to set index of planes of all of the side faces 54 of the U-groove 50 to be the (1 0 0) plane. The cause thereof is due to the fact that plane (1 1 1) lies in three-times axial symmetry because of its crystal structure, which did not match the rectangular unit cell with no three-times axial symmetry. A second embodiment in which this has been improved is shown in Fig. 23. Incidentally, Fig. 23 (a) is an illustrative plane view showing a part of a vertical type power MOSFET according to the second embodiment of the present invention, wherein the surface pattern of a gate electrode 9 is given by indication of a part only (the hatched area in the figure) in order to see the figure more easily, and indication of a source electrode 19 is omitted. In addition, Fig. 23 (b) is a cross-sectional view taken along B-B in Fig. 23 (a). In the figure, the same constitution as that in Fig. 1 is designated by the same symbol. In the second embodiment, as shown in Fig. 23 (a), a pattern of a triangular unit cell 15 and a U-groove 50 of a triangular pattern are used, and a face direction of one side of the triangle is set to be <2 1 1>, and further as shown in Fig. 23 (b), in order to provide an angle of 54.7° formed by the main surface of a wafer 21 and a side face 54 of the U-groove 50, the conditions in the LOCOS oxidation step shown in Fig. 5 are set. By doing so, index of planes of all of the side faces 54 of the U-groove 50 can be made (1 0 0) in which the interface state is the smallest, and it is possible to form channels having good characteristics equivalent to those of DMOSFET of the conventional planar type. As described above, in the first and second embodiments explained, the explanation has been made only for the case in which the present invention is applied to the vertical type power MOSFET which performs the unipolar operation, however, there is no limitation thereto, and the application may be available to a power MOSIC in which such a vertical type power MOSFET is incorporated, and further the application is also possible to a gate structure of an insulation gate type bipolar transistor (IGBT) which performs the bipolar operation. In addition, the explanation has been made only for the n-channel type in the first and second embodiments, however, it is needless to say that the same effect can be obtained with respect to the p-channel type in which the type of the semiconductor is exchanged between the n-type and the p-type. Further, the plane shape of the unit cell is not limited to the above-mentioned square and the equilateral triangle, and alternatively it is possible to optionally select rectangles, hexagons and the like. Incidentally, with respect to the change of the plane pattern, the change can be easily made using the formation pattern of the LOCOS oxide film 65. As described above, in the vertical type MOSFET according to the present invention, it is unnecessary to form a U-groove having a sufficiently long bottom face taking the positional deviation of the U-groove with respect to the base layer end into account as in the conventional U-MOS, but the length of the bottom face of the U-groove can be made short into the necessary minimum. As a result, the unit cell size can be greatly reduced, the ON-resistance per area can be reduced into a degree equivalent to the R-MOS, and the production yield and the reliability are high in a degree equivalent to the DMOS type, so that it is extremely effective in adoption as switching devices for electric power and the like as MOSIC in which its elemental article or the device is incorporated.

Claims: A production method of a vertical type MOSFET comprising the steps of: preparing a semiconductor substrate (1); forming a semiconductor layer (2) of a first conductivity type at one main face side of said semiconductor substrate (1), said semiconductor layer (2) having an impurity concentration lower than that of said semiconductor substrate (1) and having a main surface; locally oxidizing a predetermined region of said main surface of said semiconductor layer (2) to form a local oxide film (65) eroding said main surface of said semiconductor layer (2) by a predetermined depth in said predetermined region; forming channels (5) on said semiconductor layer (2) surface contacting a side face (54) of said local oxide film (65) by double diffusing impurities of the second conductivity type and the first conductivity type from said main surface successively in a manner of self-alignment with respect to said local oxide film (65), whereby the length of said channel (5) is determined by the double diffusion and simultaneously therewith a base layer (16) of the second conductivity type and a source layer (4) of the first conductivity type are formed; removing said local oxide film (65) after the double diffusion to form a groove structure (50) having said predetermined depth; oxidizing an inner wall (51) of said groove structure (50) including a portion to become said channel (5) to provide a gate oxide film (8); forming a gate electrode (9) on said gate oxide film (8); forming a source electrode (19) electrically contacting both said source layer (4) and said base layer (16); and forming a drain electrode (20) electrically contacting the other main face side of said semiconductor substrate (1), said production method of a vertical type MOSFET being characterized in that: said semiconductor layer (2) forming step includes a step of forming a silicon layer, an index of plane of said main surface of which is (111) or about (111); said local oxidizing step includes a step of controlling an index of plane of said semiconductor layer (2) surface contacting said side face (54) of said local oxide film (65) to be (100) or about (100); and in that: said step of removing said local oxide film (65) to form said groove structure (50) is performed in such a manner that an index of plane of said bottom face (53) of said groove structure (50) is (111) or about (111) and an index of plane of said side face (54) of said groove structure (50) is (100) or about (100). A production method of a vertical type MOSFET according to claim 1, characterized in that said double diffusing of impurities in the step of forming channels (5) includes the steps of: forming said base layer (16) by diffusing impurities of said second conductivity type in said semiconductor layer (2) in a manner of self-alignment with respect to said local oxide film (65) ; and forming said source layer (4) by diffusing impurities of said first conductivity type in said semiconductor layer (2) in a manner of self-alignment with respect to said local oxide film (65). A production method of a vertical type MOSFET according to claim 1 or 2 characterized in that said step of preparing said semiconductor substrate (1) includes a step of selecting said semiconductor substrate (1) of said first conductivity type. A production method of a vertical type MOSFET according to one of the claims 1 to 3, characterized in that said vertical type MOSFET is an insulated gate type bipolar transistor. A production method of a vertical type MOSFET according to one of the claims 1 to 4, characterized in that it further comprises a step of etching said semiconductor layer (2) to form an initial groove (64) in said surface of said semiconductor layer (2) prior to said step of forming said local oxide film (65). A production method of a vertical type MOSFET according to one of the claims 1 to 5, characterized in that said step of forming a local oxide film (65) includes a step of making a surface pattern shape of said local oxide film (65) an equilateral triangle shape such that one side of said equilateral triangle shape is along a <211> crystal axis. A production method of a vertical type MOSFET according to one of the claims 1 to 6, characterized in that: said local oxidizing step is performed in such a manner, that said local oxide film (65) having a bottom portion (53) and inclined side portions (54) having an inclination angle which is not less than 45 degree; said step of forming channels (5) by double diffusion is performed in such a manner that said channels (5) are disposed to contact with respective inclined side portions (54) of said local oxide film (65); and said step of removing said local oxide film (65) to form said groove structure (50) is performed in such a manner that said groove structure (50) has inclined sidewalls (54) corresponding to said channel (5). A production method of a vertical type MOSFET according to claim 7, characterized in that it comprises a step of forming an initial groove (64) at said main surface of said silicon layer (2) in said region where said local oxide film (65) is formed, prior to said local oxidizing step. A production method of a vertical type MOSFET according to claim 8, characterized in that said local oxidizing step includes a step of making a surface pattern shape of said local oxide film (65) an equilateral triangle shape such that one side of said equilateral triangle shape is along a <211> crystal axis. A production method of a vertical type MOSFET according to claim 8 or 9, characterized in that said step of preparing said semiconductor substrate (1) includes a step of selecting said semiconductor substrate (1) of said first conductivity type.

Inventors: TAKAHASHI SHIGEKI, TOKURA NORIHITO, TAKAHASHI, SHIGEKI, TOKURA, NORIHITO, TAKAHASHI, SHIGEKI NIPPONDENSO CO., LTD., TOKURA, NORIHITO NIPPONDENSO CO., LTD.
Applicants: DENSO CORP, DENSO CORPORATION
Application year: 1992
Main classification: H01L29
IPC codes: H01L29, H01L21