Melt processable poly(ester-amide) capable of forming an anisotropic melt

Abstract: A melt processable poly(ester-amide) which is capable of forming an anisotropic melt phase is provided. A poly(ester-amide) of the present invention may have recurring units of: (a) 4-hydroxybenzoyl moiety, (b) 6-oxy-2-naphthoyl moiety, (c) 4,4'-biphenol moiety, (d) terephthaloyl moiety, and (e) an aromatic moiety capable of forming an amide linkage in the proportions indicated. Preferably, the moiety capable of forming an amide linkage is derived from p-aminophenol, p-phenylenediamine, N-acetyl-p-aminophenol, etc. The resulting poly(ester-amide) is capable of undergoing melt-processing in the temperature range of from about 300° to about 400°C.

Description: TECHNICAL FIELD The present invention relates generally to high performance liquid-crystal polyester resins and more specifically to a melt-processable polyester-amide capable of forming an anisotropic melt derived from 4-oxybenzoyl, 6-oxy-2-naphthoyl, terephthaloyl, biphenol and an aromatic moiety capable of forming an amide linkage. BACKGROUND OF THE INVENTION Liquid crystalline or thermotropic polyesters capable of forming an anisotropic melt are known high performance materials useful for manufacturing films, fibers, molded articles and like items. While these materials typically exhibit superior temperature resistance and mechanical properties as compared to commodity resins, they are often times difficult to synthesize and melt-process due to a tendency to become intractable if the composition is not carefully controlled, or alternatively, desirable properties as aforementioned can be lacking if the ratio and/or selection of components is not within critical ranges. Various attempts have been made to improve the processability and/or mechanical properties of liquid crystalline polyesters, including by the incorporation of amide linkages into such polymers. U.S.-A-4,282,842 discloses poly(ester-amides) prepared from an aromatic dicarboxylic acid, ethylene glycol, and a p-acylaminobenzoic acid. A similar disclosure is Japanese Publication 54-125271. European Patent Application No. 79301276.6 (Publication No. 0 007 715) discloses melt processable fiber-forming poly(ester-amides) comprising residues of one or more aminophenols selected from p-aminophenol and p-N-methylaminophenol and residues of one or more dicarboxylic acids. The poly(ester-amide) disclosed contains a balance of linear difunctional residues and dissymmetric difunctional residues derived from either the aminophenols or their acids. The linear difunctional residues and dissymmetric difunctional residues are chosen so as to give a product which melts below its decomposition temperature and exhibits optical anisotropy in the melt. U.S.-A-3,859,251 discloses a poly(ester-amide) which comprises 50 to 100 mole percent of the moiety derived from an acyclic aliphatic dicarboxylic acid. U.S.-A-3,809,679 discloses poly(ester-amides) consisting of 10 to 90 mole percent of recurring structural units derived from a dicarboxylic acid dihalide and a dihydroxy compound of a specified formula and 10 to 90 mole percent of recurring structural units derived from a dicarboxylic acid dihalide and a diamino compound of a specified formula. The poly(ester-amides) described specifically exclude moieties derived from aromatic hydroxyacids, such as the 6-oxy-2-naphthoyl moiety included in the poly(ester-amide) of the present invention. U.S.-A-4,330,457 discloses melt processable poly(ester-amides) capable of forming an anisotropic melt phase derived from 6-hydroxy-2-naphthoic acid, dicarboxylic acid, and aromatic monomer capable of forming an amide linkage. The resulting poly(ester-amide) exhibits a melting temperature below approximately 400° C. Other poly(ester-amides) are disclosed in U.S.-A-4,966,956; 4,355,132 and 4,339,375. The '956 patent teaches a four-component poly(ester-amide) including 4-oxybenzoyl, biphenol, an amide-forming monomer and either terephthaloyl or isophthaloyl moieties. U.S.-A-4,473,682 discloses melt processable polyesters capable of forming an anisotropic melt comprising a relatively low concentration of 6-oxy-2-naphthoyl moiety, 4-oxybenzoyl moiety, 4,4'-dioxybiphenyl moiety, and terephthaloyl moiety. This polyester forms an atypical highly tractable anisotropic melt phase. U.S.-A-4,351,917 discloses a melt processable poly(ester-amide) which is capable of forming an anisotropic melt phase derived from 6-hydroxy-2-naphthoic acid, an aromatic moiety capable of forming an amide linkage, and optionally, other aromatic moieties derived from aromatic hydroxyacid. U.S.-A-4,351,918 shows a melt processable poly(ester-amide) which is capable of forming an anisotropic melt phase derived from 6-hydroxy-2-naphthoic acid, other aromatic hydroxyacid, carbocyclic dicarboxylic acid, and aromatic monomers capable of forming an amide linkage. SUMMARY OF THE INVENTION It has been found that compositions in accordance with the present invention have a unique combination of temperature resistance, mechanical properties and processability at relatively low temperature. A melt processable poly(ester-amide) capable of forming an anisotropic melt phase at a temperature below 400°C. having recurring moieties I, II, III, IV and V wherein: I is II is III is IV is -[Y-Ar-Z]- wherein Ar is a divalent moiety containing at least one aromatic ring, Y and Z are independently selected from the group consisting of O, NH and NR, with the proviso that at least one member is selected from the group consisting of NH or NR where R is a 1-6 carbon containing alkyl moiety or an aryl moiety; and V is the residue of an aromatic di-oyl precursor; and wherein said poly(ester-amide) contains from 1 to 15 mole per cent of moiety I, from 20 to 70 mole percent moiety II, from 5 to 40 mole percent of moiety III, from 1 to 20 mole per cent of moiety IV, and from 5 to 40 mole per cent of moiety V. Typically, the compositions contain from 2.5 to 10 mole percent moiety I, 20 to 70 mole percent moiety II, 5 to 25 mole percent moiety III, 2.5 to 15 percent moiety IV, and 2.5 to 15 percent of moiety V. A preferred composition contains 2.5 to 7.5 mole percent moiety I, at least 50 mole percent of moiety II, from 5 to 20 percent of moiety III, from 2.5 to 10 mole percent of moiety IV, and 15 to 25 mole percent of moiety V. A preferred moiety IV is derived from p-aminophenol or N-acetyl-p-aminophenol. Moiety V is most preferably a terephthaloyl moiety but may be selected from the group consisting of isophthaloyl, terephthaloyl or mixtures thereof. The melt-processable poly(ester-amide) according to the invention is capable of forming an anisotropic melt phase below 350°C. and is capable of undergoing melt-processing in the temperature range of from 300°C to 400°C. A melt processable poly(ester-amide) according to the invention may exhibit an inherent viscosity in the range of 1.0 to 12.0 dl/g when dissolved in a concentration of 0.1 percent by weight in pentafluorophenol at 60°C and may exhibit a melt viscosity in the range of from 50 to 1500 poise at a shear rate of 10 3 sec -1 measured at 365°C in a capillary rheometer. The compositions according to the invention are useful for making shaped articles such as melt-spun fibers and injection-molded articles as will become apparent from the examples hereinafter provided. DETAILED DESCRIPTION The poly(ester-amide) of the present invention includes five recurring moieties which when combined in the poly(ester-amide) have been found to form an atypical highly tractable anisotropic melt phase at a temperature below 400°C., and preferably below 370°C. (e.g., 350°C. in a particularly preferred embodiment). The poly(ester-amide) melt endotherm (T m ) may be confirmed by the use of a differential scanning calorimeter (DSC) employing repeat scans at a 20°C. per minute heat-up rate and observing the peak of the DSC melt transition. The poly(ester-amide) of the present invention may be considered crystalline in the sense that fibers melt extruded therefrom exhibit X-ray diffraction patterns using Ni-filtered CuKα radiation and flat plate cameras characteristic of polymeric crystalline materials. Because of its ability also to exhibit anisotropic properties (i.e., liquid crystalline properties) in the melt, the poly(ester-amide) readily can form a product having a highly oriented molecular structure upon melt processing. Such product has been found to exhibit unusually high tenacity and modulus. Preferred poly(ester-amides) are capable of undergoing melt processing at a temperature in the range of 320°C. to 390°C. (e.g., at approximately 345°C. to 360°C.). As will be readily appreciated by those skilled in the art, the present invention is in no way limited by the examples which follow. Although the invention is illustrated specifically with N-acetyl-p-aminophenol providing an amide linkage, such linkages could be derived from p-aminophenol, p-N-methylaminophenol, p-phenylenediamine, N-methyl-p-phenylenediamine, N,N'-dimethyl-p-phenylenediamine, m-aminophenol, 3-methyl-4-aminophenol, 2-chloro-4-aminophenol, 4-amino-1-naphthol, 4-amino-4'-hydroxydiphenyl, 4-amino-4'-hydroxydiphenyl ether, 4-amino-4'-hydroxydiphenyl methane, 4-amino-4'-hydroxydiphenyl ethane, 4-amino-4'-hydroxydiphenyl sulfone, 4-amino-4'-hydroxydiphenyl sulfide, 4,4'-diaminophenyl sulfide (thiodianiline), 4,4'-diaminodiphenyl sulfone, 2,5-diaminotoluene, 4,4'-ethylenedianiline, or 4,4'-diaminodiphenoxyethane, as well as 3,4'-diaminophenyl X, 3-amino-4'-hydroxyphenyl X, and 3-hydroxy-4'-aminodiphenyl X, wherein X is selected from the group consisting of sulfide, sulfone, ether and methane. The poly(ester-amide) of the present invention may optionally incorporate 1 to 50 percent by weight (preferably 10 to 30 percent by weight), based upon the total weight of the polymers, of a solid filler and/or reinforcing agent when making a molded article. Representative filler materials include calcium silicate, silica, clays, talc, mica, polytetrafluoroethylene, graphite, alumina trihydrate, sodium aluminum carbonate, barium ferrite, wollastonite, etc. Representative reinforcing fibers include glass fibers, graphitic carbon fibers, amorphous carbon fibers, synthetic polymeric fibers, alumina fibers, aluminum silicate fibers, aluminum oxide fibers, titanium fibers, magnesium fibers, rock wool fibers, steel fibers, tungsten fibers, or wollastonite fibers having an aspect ratio greater than 3 to 1. EXAMPLE I This example illustrates the preparation of a poly(ester-amide) from a 6 mole reaction mixture of 4-hydroxybenzoic acid ("HBA"), 6-hydroxy-2-naphthoic acid ("HNA"), 4,4'-biphenol ("BP"), terephthalic acid ("TA"), and N-acetyl-p-aminophenol ("APAP") in the ratio 60.0:5.0:12.5:17.5:5.0 (5.0 mole % HNA and 5.0 mole % APAP). To a 2 litre "Slim Jim" flask equipped with a C-shaped 316 stainless steel, gas inlet tube, thermocouple, a Vigreux column attached to a condenser and receiver were added the following: (a) 496.8 grams of 4-hydroxybenzoic acid (3.6 moles) ; (b) 56.4 grams of 6-hydroxy-2-naphthoic acid (0.3 moles); (c) 139.5 grams of 4,4'-biphenol (0.75 moles); (d) 174.3 grams of terephthalic acid (1.05 moles); (e) 45.3 grams of N-acetyl-p-aminophenol (0.3 moles); the flask was immersed in a sand bath and provided with means to accurately control the temperature. The flask was throughly purged of oxygen by evacuation and flushed with nitrogen three times, and slowly heated in the sand bath; and (f) 10 mls. of a 1.2% (w/v) solution of potassium acetate in acetic acid (60 ppm K + ) were added as a catalyst along with 598.8 grams of acetic anhydride (2.5 % excess). Acetic acid began to distill over and was collected in a graduated cylinder. The contents of the flask were heated while stirring at a rate of 75 rpm (torque = 13 mV) to 152°C. over a period of 111 minutes at which time 100 mls. of acetic acid had been collected. The polymerization temperature was then gradually raised to 350°C. over a period of 215 minutes at which time a total of 660 mls. of acetic acid had been collected. The flask was evacuated to a pressure of less than 1.0 mm at 350°C. while stirring. The polymer was stirred at 350°C. until the desired Δ torque was achieved (i.e., Δ torque = 50 mV for this example). During this period the polymer melt continued to increase in viscosity while the remaining acetic acid was removed from the flask. The resulting poly(ester-amide) had an inherent viscosity (I.V.) of 9.1 dl/g as determined in a pentafluorophenol solution of 0.1 percent by weight concentration at 60°C., and a melt viscosity (M.V.) of 581 poise at a shear rate of 10 3 sec -1 measured at 345°C in a capillary rheometer using an orifice of 0.38 mm (0.015 inch) diameter and 2.54 mm (1.0") length. I.V. = ln(η rel)/c where c = concentration of solution (0.1 percent by weight), and η rel = relative viscosity. The relative viscosity was measured by dividing the flow time in a capillary viscometer of the polymer solution by the flow time for the pure solvent. When the polymer was subject to differential scanning calorimetry (20°C./min. heating rate), it exhibited a melt endotherm (T m ) peak at 343°C. The polymer melt was optically anisotropic. EXAMPLE II - X In accordance with the foregoing example I, nine additional compositions were prepared having different proportions of the five ingredients noted hereinabove. Composition, melting point, I.V. and M.V. for the inventive compositions appear in Table I below. Unless otherwise indicated, properties were measured as in Example I. COMPOSITION MELTING POINT, I.V. AND M.V. OF EXAMPLES I - X COMPOSITION (MOLE PERCENT) EXAMPLE HBA:HNA:BP:TA:APAP T m ,°C I.V. dl/g M.V. POISE I 60:5.0:12.5:17.5:5.0 343 9.1 581 II 60:5.0:15:17.5:2.5 343 9.5 538 III 60:5.0:10.0:17.5:7.5 362 7.8 1015 IV 60:3.5:15.75:18.25:2.5 363 8.5 428 V 60:3.5:13.25:18.25:5.0 359 9.0 365 VI 60:3.5:11.75:18.25:6.5 357 7.1 960 VII 60:3.5:10.75:18.25:7.5 370 7.3 68 VIII 50.0:15.0:7.5:17.5:10.0 323 9.1 976 IX 40:15.0:17.5:22.5:5.0 260 8.8 878 X 30:15.0:22.5:27.5:5.0 327 8.5 567 COMPARATIVE EXAMPLE A This example illustrates the preparation of a polyester from a 7 mole reaction mixture of 4-hydroxybenzoic acid, 6-hydroxy-2-naphthoic acid, 4,4'-biphenol, and terephthalic acid in the ratio 60.0:3.5:18.25:18.25 (3.5 mole % HNA and 0.0 mole % APAP). The procedure of Example I was substantially repeated with the exception that the following components were charged into the flask: (a) 579.6 grams of 4-hydroxybenzoic acid (4.2 moles); (b) 46.1 grams of 6-hydroxy-2-naphthoic acid (0.24 moles); (c) 237.6 grams of 4,4'-biphenol (1.28 moles); (d) 212.1 grams of terephthalic acid (1.28 moles); and (e) 10 mls. of a 1.2% (w/v) solution of potassium acetate in acetic acid (60 ppm K + ) were added as a catalyst along with 598.8 grams of acetic anhydride (2.5 % excess); the desired Δ torque was 50 mV, and the reaction temperature was 355° C. The resulting wholly aromatic polymer had an I.V. of 9.2 dl/g as determined in pentafluorophenol at 60° C., and an M.V. of 492 poise at a shear rate of 10 3 sec -1 measured at 365° C in a capillary rheometer. When the polymer was subjected to DSC, it exhibited a T m of 376° C. COMPARATIVE EXAMPLE B This example illustrates the preparation of a poly(ester amide) from a 6 mol reaction mixture of 4-hydroxybenzoic acid, isophthalic acid, terephthalic acid, 4,4'-biphenol, and N-acetyl-p-aminophenol in the ratio of 50.0:12.5:12.5:20.0:5.0. The following components were charged into the flask: a) 3.0 mole (414.0 g) 4-hydroxybenzoic acid; b) 0.75 mole (124.5 g) isophthalic acid; c) 0.75 mole (124.5 g) terephthalic acid; d) 1.2 mole (223.2 g) 4,4'-biphenol; e) 0.3 mole (45.3 g) N-acetyl-p-aminophenol; and f) 10 ml of a 1.2 (w/v) solution of potassium acetate in acetic acid (60 ppm K + ) were added as a catalyst along with 600 ml acetic anhydride (2.5% excess) and heated to 350°C. The resulting wholly aromatic polymer had an I.V. of 3.6 dl/g as determined in pentafluorophenol at 60°C, and an M.V. in the range of about 500-700 poise at a shear rate of 10 3 sec -1 measured at 340°C in a capillary rheometer. When the polymer was subject to DSC, it exhibited a T m of 281°C. FIBER PROPERTIES Fibers were prepared from the compositions of Examples IV, V, and Comparative Example A. The fibers were heat-treated for eight hours in a nitrogen atmosphere at 300°C in an oven. Tenacity, elongation and modulus were defined in accordance with ASTM D 3822-90 and reported in Table II, below, along with corresponding data for Comparative Example B wherein the heat treatment was in stepwise fashion, 2 hours at 230°C, followed by 16 hours at 270°C. Examples IV, V, A are approximately 0.55 tex (5 denier). The polymer of Example B was difficult to spin; unable to achieve 0.55 tex (5 denier) fiber, but 0.94 tex (8.5 denier) fiber was made. FIBER PROPERTIES AFTER HEAT TREATMENT POLYMER OF EXAMPLE TENACITY g/d MODULUS g/d ELONGATION % IV 29.2 1040 2.5 V 31.9 1060 2.7 A 21-22 910 2.2-2.3 B 16 475 3.0 As may be seen from Table II, compositions in accordance with the present invention exhibit both higher modulus and tenacity than other liquid crystalline polymers. This surprising and highly useful characteristic makes such compounds particularly suitable for high performance applications.

Claims: A melt processable poly(ester-amide) capable of forming an anisotropic melt phase at a temperature below 400°C. having recurring moieties I, II, III, IV and V wherein: I is II is III is IV is -[Y-Ar-Z]- wherein Ar is a divalent moiety containing at least one aromatic ring, Y and Z are independently selected from the group consisting of O, NH and NR, with the proviso that at least one member is selected from the group consisting of NH or NR where R is a 1-6 carbon containing alkyl moiety or an aryl moiety; and V is the residue of an aromatic di-oyl precursor; and wherein said poly(ester-amide) contains from 1 to 15 mole per cent of moiety I, from 20 to 70 mole percent moiety II, from 5 to 40 mole percent of moiety III, from 1 to 20 mole per cent of moiety IV, and from 5 to 40 mole per cent of moiety V. The poly(ester-amide) according to claim 1 wherein moiety IV is The poly(ester-amide) according to claim 2 wherein moiety IV is derived from p-aminophenol or N-acetyl-p-aminophenol. The polyester according to claim 3 wherein moiety IV is derived from N-acetyl-p-aminophenol. The poly(ester-amide) according to claim 1, wherein moiety V is a terephthaloyl moiety. The poly(ester-amide) according to claim 1 wherein moiety V is selected from the group consisting of isophthaloyl, terephthaloyl or mixtures thereof. The melt-processable poly(ester-amide) according to claim 1 which is capable of forming an anisotropic melt phase at a temperature of 350°C. The melt-processable poly(ester-amide) according to claim 1 which is capable of undergoing melt-processing in the temperature range of from 300°C. to 400°C. A fiber which has been melt spun from the poly(ester-amide) according to claim 1. An injection molded article comprising the melt processable poly(ester-amide) according to claim 1. A shaped article consisting of the poly(ester-amide) according to claim 1. A melt processable poly(ester-amide) according to claim 1 which exhibits an inherent viscosity in the range of 1.0 to 12.0 dl/g when dissolved in a concentration of 0.1 percent by weight in pentafluorophenol at 60°C. A melt processable poly(ester-amide) according to claim 1 which exhibits a melt viscosity in the range of from 50 to 1500 poise at a shear rate of 10 3 sec -1 measured at 365°C in a capillary rheometer. A melt processable poly(ester-amide) capable of forming an anisotropic melt phase at a temperature below 400°C consisting essentially of recurring moieties I, II, III, IV and V wherein: I is II is III is IV is -[Y- Ar-Z]- wherein Ar is a divalent moiety containing at least one aromatic ring, Y and Z are independently selected from the group consisting of O, NH and NR, with the proviso that at least one member is selected from the group consisting of NH or NR where R is a 1-6 carbon containing aklyl moiety or an aryl moiety; and V is the residue of an aromatic di-oyl percursor or mixtures of terephthaloyl with other aromatic di-oyls; and wherein moiety I is present in amounts of from 2.5 to 10 mole per cent, moiety II is present in amounts from 20 to 70 mole per cent, moiety III is present in amounts of from 5 to 25 mole per cent, moiety IV is present in amounts of from 2.5 to 15 mole per cent, and moiety V is present in amounts of from 10 to 25 mole per cent. The melt-processable poly(ester-amide) according to claim 14 , wherein moiety V consists of terephthaloyl. The melt-processable poly(ester-amide) according to claim 14, wherein moiety IV is derived from N-acetyl-p-aminophenol. The melt processable poly(ester-amide) according to claim 14 wherein moiety I is present in an amount of from 2.5 to 7.5 mole per cent, moiety II is present in an amount of at least 50 mole per cent, moiety III is present from 5 to 20 per cent, moiety IV is present in an amount of from 2.5 to 10 mole per cent, and moiety V is present from 15 to 25 mole per cent. A fiber spun from the composition of claim 14. A shaped article formed from the composition of claim 14.

Inventors: CHERYLYN LEE, LARRY F CHARBONNEAU, CHERYLYN, LEE, LARRY, F. CHARBONNEAU
Applicants: HOECHST CELANESE CORP, HOECHST CELANESE CORPORATION
Application year: 1992
Main classification: C08G69
IPC codes: D01F6, C08G69