Optically dissimilar compositions for polymeric reflective bodies

Abstract: A multilayered reflective body which is thermoformable and capable of being fabricated into films, sheets and a variety of parts while maintaining a uniform reflective appearance is provided. The reflective polymeric body includes at least first and second diverse polymeric materials of a sufficient number of alternating layers of the first and second polymeric materials such that at least 30 percent of the light incident on the body is reflected. A substantial majority of the individual layers of the body have an optical thickness of not more than 0.09 micrometers or not less than 0.45 micrometers, and adjacent layers of the first and second polymeric materials differ from each other in refractive index by at least 0.1. The reflective body may be fabricated into sheets, mirrors, noncorroding metallic appearing articles and parts, reflectors and reflective lenses.

Description: The present invention relates to a multilayered polymeric body which reflects light and which can be fabricated to have a silvery or hued (that is, copper, gold, etc.) metallic or nonconventional hued (that is, blue, green, etc.) appearance, and to articles produced therefrom which may find use as mirrors, reflectors, lenses and polarizers. Highly reflective articles (that is, articles having a reflectance of 70 to 85 percent or greater) are generally sought by industry for a number of uses. Conventional methods for fabricating reflective surfaces include forming such surfaces of highly polished metals. Because of the high costs and fabricating problems involved in using metals, more recently fabricators have used plastic surfaces which contain thin coatings of metal thereon. Thus, metal coated plastic articles are now commonly found as both decorative and functional items in a number of industries. Such articles are used as bright work for consumer appliances such as refrigerators, dishwashers, washers, dryers and radios. These types of articles are also used by the automotive industry as head lamp reflectors, bezels, radio knobs and automotive trim. Typically, such metal coated plastic articles are formed by electroplating or by the vacuum, vapor, or chemical deposition of a thin metal layer on the surface of the article. Such coatings are subject to the chipping and flaking of the metal coatings as well as corrosion of the metal over time. If additional protective layers must be applied over the metal coating to protect it, additional labor and materials costs are involved. Further, there may be environmental disposal problems with some metal deposition processes. Multilayer articles of polymers are known, as are methods and apparatuses for making such articles. For example, such multilayered articles may be prepared utilizing multilayer coextrusion devices as described in US-A-3,773,882 and US-A-3,884,606. Such devices are capable of simultaneously extruding diverse thermoplastic polymeric materials in substantially uniform layer thicknesses. The number of layers may be multiplied by the use of a device as described in US-A-3,759,647 to Schrenk et al. Im et al, US-A-4,540,623, teach a multilayer laminated article which includes a polycarbonate as one of the alternating layers. The articles of Im et al, however, are intended to be transparent rather than reflective and to exhibit optical properties comparable to a pure polycarbonate polymer. Alfrey, Jr. et al, US-A-3,711,176, teach a multilayered highly reflective thermoplastic body fabricated using thin film techniques. That is, the reflective thin film layers of Alfrey, Jr. et al relied on the constructive interference of light to produce reflected visible, ultraviolet, or infrared portions of the electromagnetic spectrum. Such reflective thin films have found use in decorative items because of the iridescent reflective qualities of the film. However, the films of Alfrey, Jr. et al are extremely sensitive to thickness changes, and it is characteristic of such films to exhibit streaks and spots of nonuniform color. Further, color reflected by such films is dependent on the angle of incidence of light impinging on the film. Thus, such films are not practical for uses which require uniformity of reflectivity. Moreover, such films are not practical to thermcform into articles as localized thinning of the layers during thermoforming causes alterations in the reflective characteristics of the films. In addition to the problems discussed above, many reflective articles such as those used in the automotive industry are exposed to extreme environmental conditions and do not exhibit good weatherability or resistance to solvents. Further, many of the films used in the production of reflective articles exhibit poor ductility and are thus difficult to thermoform into articles. EP-A-0404463 discloses a reflective polymeric body of at least first and second diverse polymeric materials and having a plurality of alternating layers of said first and second polymeric materials differing from each other in refractive index, characterized in that said difference in refractive index is at least 0.03, at least 75 percent of the individual layers of said body have an optical thickness which is either not more than 0.09 micrometers or not less than 0.45 micrometers and there is a sufficient number of said alternating layers that substantially no visibly perceived iridescence is reflected. Reference is made to the use of first and second polymeric materials which differ in refractive index by up to 0.15 and to reflectivity increasing with difference in refractive index. EP-A-0491551 (published 24th June 1992) discloses a reflective polymeric body of at least first and second diverse polymeric materials differing from each other in refractive index by at least 0.03, the body comprising a plurality of alternate respective layers of said first and second polymeric materials having an optical thickness which is either not greater than 0.09 µm or not less than 0.45 µm, wherein the body further comprises at least one group of adjacent alternate respective layers of at least two of said diverse polymeric materials having an optical thickness of between 0.09 and 0.45 µm in such position and amount to increase the reflectance of the body, the total number of layers being sufficient that at least 30 percent of light incident on said body is reflected and there is an absence of visibly perceived color reflected from said body. The terms "reflective", "reflectivity", "reflection", and "reflectance" as used herein refer to total reflectance (that is, ratio of reflected wave energy to incident wave energy) sufficiently specular in nature such that the polymeric body has a metallic appearance. The use of these terms is intended to encompass semi-specular or diffuse reflection such as that of brushed metal and pewter. In general, reflectance measurement refers to reflectance of light rays into an emergent cone with a vertex angle of 15 degrees centered around the specular angle. A specific intensity of reflectance, when used herein, is the intensity of reflection which occurs at a wavelength where negligible absorption occurs. For example, a silver appearing article reflects substantially all visible wavelengths, whereas the introduction of a dye to achieve other metallic hues will necessarily lower reflectivity of the body at the absorbing wavelengths. Wavelengths unaffected by the dye will be reflected at essentially the same intensity as a non-dyed sample, and it is at these unaffected wavelengths to which the intensity of reflection is referring. According to one aspect of the present invention, there is provided a reflective polymeric body of at least first and second diverse polymeric materials (A,B) and having a plurality of alternating layers (ABAB) of said first and second polymeric materials differing from each other in refractive index, at least 75 percent of the individual layers of said body having an optical thickness which is either not more than 0.09 micrometers or not less than 0.45 micrometers, with at least one of the individual layers having an optical thickness not less than 0.45 micrometers and there is a sufficient number of said alternating layers that substantially no perceived iridescence is reflected and/or at least 30 percent of light incident on the body is reflected, characterized in that:- the first polymeric material is selected from (i) a copolycarbonate of thiodiphenol and bisphenol-A and (ii) a bisphenol-A polycarbonate; and the second polymeric material is selected from (i) a copolymer of methyl methacrylate and vinylidene fluoride, (ii) a miscible blend of polymethyl methacrylate and polyvinylidene fluoride, (iii) a miscible blend of polymethyl methacrylate and a fluoropolymer which is a copolymer of vinylidene fluoride and a fluorocarbon monomer selected from chlorofluoroethylene, chlorodifluoroethylene, chlorotrifluoroethylene, hexafluoroacetone, hexafluoropropylene, pentafluoropropylene, trifluoroethylene, tetrafluoroethylene or vinyl fluoride, and, when said first polymeric material is a copolycarbonate, (iv) a copolymer of methyl methacrylate, vinylidene fluoride and a said fluorocarbon monomer, said difference in refractive index being at least 0,131, whereby at least 70 percent of said incident light is reflected. In the invention, highly reflective bodies reflecting from 70-85 percent and greater of light incident on such bodies are provided by selecting polymers having large refractive index mismatches. We have previously described reflective polymeric bodies in which the refractive index mismatch between the first and second polymeric materials is approximately 0.1. To produce highly reflective bodies (that is, 70 to 85 percent or greater reflectance) using these materials requires a large number of alternating layers (that is, 2000 or more). The need for a large number of layers in the body may present processing difficulties in generating that number of layers and maintaining the integrity of each layer without layer distortion, fragmentation, or intermixing. Additionally, the larger the number of layers which are required, the greater the minimum thickness for the body which is produced. By selecting polymers and having a mismatch in refractive index greater than 0.131, highly reflective bodies may be produced which require fewer layers and have a suitable total thicknesses. Certain substantially transparent polymers having either a relatively high refractive index or a relatively low refractive index are suitable for use in the present invention. In one embodiment of the invention, one of the polymeric materials is a copolycarbonate of bisphenol-A and 4,4'-thiodiphenol and the other is polymethyl methacrylate. The copolymer may comprise from 5-80 mole percent 4,4'-thiodiphenol and from 20-95 mole percent bisphenol-A. Preferably, the 4,4'-thiodiphenol is present in a mole ratio of approximately 3 to 1 relative to the bisphenol-A. Such a copolymer has a refractive index of greater than 1.6. In another embodiment of the invention, the first polymeric material is a bisphenol-A polycarbonate or a copolycarbonate derived from thiodiphenol and bisphenol monomers and the second polymeric material is a miscible blend or copolymer of polymethyl methacrylate and polyvinylidene fluoride. The blend may comprise from 95 to 5 weight percent polymethyl methacrylate and from 5 to 95 weight percent polyvinylidene fluoride, while the copolymer may comprise from 95 to 5 mole percent methyl methacrylate and from 5 to 95 mole percent vinylidene fluoride. Preferably, the polymethyl methacrylate is present in the blend in roughly equal proportions with polyvinylidene fluoride. Such a blend has a refractive index of only 1.45. In another embodiment of the invention, the first polymeric material is a copolycarbonate of thiodiphenol and bisphenol-A or a bisphenol-A polycarbonate and the second polymeric material is a miscible blend of polymethyl methacrylate and a fluoropolymer where the fluoropolymer is a copolymer of vinylidene fluoride and a fluorocarbon monomer selected from chlorofluoroethylene, chlorodifluoroethylene, chlorotrifluoroethylene, hexafluoroacetone, hexafluoropropylene, pentafluoropropylene, trifluoroethylene, tetrafluoroethylene, and vinyl fluoride. Preferably, the blend comprises from 95 to 5 weight percent polymethyl methacrylate and from 5 to 95 weight percent fluoropolymer. In yet another embodiment of the invention, the first polymeric material is a copolycarbonate of thiodiphenol and bisphenol-A and the second polymeric material is a copolymer of methyl methacrylate, vinylidene fluoride and a fluorocarbon monomer selected from chlorofluoroethylene, chlorodifluoroethylene, chlorotrifluoroethylene, hexafluoroacetone, hexafluoropropylene, pentafluoropropylene, trifluoroethylene, tetrafluoroethylene, and vinyl fluoride. Preferably, the copolymer comprises from 90 to 10 mole percent methyl methacrylate, from 5 to 45 mole percent vinylidene fluoride, and from 5 to 45 mole percent fluorocarbon monomer. An outer layer may be included as a protective surface or skin layer for the multilayer body and may form both major exterior surfaces for an ABAB repeating unit body. The skin layer may be sacrificial, or may be permanent and serve as a scratch resistant or weatherable protective layer. Further, such skin layers may be post applied to the body after coextrusion. For example, a skin layer may be applied as a sprayed on coating which acts to level the surface of the body to improve optical properties and impart scratch resistance, chemical resistance and/or weatherability. The skin layer may also be laminated to the multilayered body. Lamination is desirable for those polymers which are not readily coextrudable. In a preferred form, the polymeric body is coextruded and every other layer in the ABAB repeating unit is a thick optical layer of 0.45 micrometers or greater while the other layer is a very thin optical layer of 0.09 micrometers or less. In certain embodiments of the invention, to obtain high reflectivity it is desirable to form the reflective polymeric body to comprise at least 500 layers. Increasing the number of layers in the polymeric body has been found to increase its reflectivity (that is, the percentage of incident light reflected from the body). Thus, by controlling the number of layers, the degree of reflectivity of the article may be controlled. In some embodiments of the invention it may be desirable to incorporate coloring agents such as dyes or pigments into one or more of the individual layers of the polymeric body. This can be done to one or both of the outer or skin layers of the body, or alternatively, the coloring agent may be incorporated into one or more interior layers in the body. The coloring agents may be selected to give the polymeric body a metallic appearance other than its normal silvery appearance such as bronze, copper, or gold, for example. Different colors such as black, blue, red, yellow and white may also be incorporated in the body. Typically, it is most desirable to use pigmented coloring agents in the interior layers to provide opaqueness and a mirror-like reflective quality and to use dyes on exterior surface layers. Coloring agents may be used in combination to provide desirable coloring and optical properties. For example, a pigmented white coloring agent may be used in an interior surface while a colored dye, such as blue, yellow, red, or green may be included on one or more surface layers to provide a unique reflective colored effect. Further, while the normal surface of the body is smooth to give a highly reflective silver appearance, in some instances it may be desirable to give the surface of the body a roughened or brushed appearance to simulate a brushed metallic appearance. Further, a solvent may be used to etch the surface of the multilayer body to provide a matte or pewter look to the body. Additionally, the body may be embossed with a variety of patterns to provide desirable optical effects. The polymer systems may be chosen to be semicrystalline to provide a more diffused reflection for aesthetic or functional control of light. The reflective polymeric body of the present invention may find several applications. In another embodiment of the invention, the reflective body may be fabricated as a mirror-like polymeric article having at least first and second major surfaces. In this embodiment of the invention, the first polymeric material suitably comprises a copolycarbonate of bisphenol-A and 4,4'-thiodiphenol and the second polymeric material suitably comprises polymethyl methacrylate. Alternatively the first material can comprise bisphenol-A polycarbonate or a copolycarbonate derived from thiodiphenol and bisphenol monomers and the second polymeric material can comprise a miscible blend or copolymer of polymethyl methacrylate and polyvinylidene fluoride. To provide the mirror-like quality to the article, one of the major surfaces preferably includes a light absorbent layer, such as a layer of a black or other colored pigment. The light absorbent layer may be coextruded or applied as a lacquer, paint, or lamination. Alternatively, increasing the number of individual layers or increasing the refractive index mismatch between polymers results in increased reflectance of incident light from the article resulting in a mirror-like quality in the article. The reflective polymeric body of the present invention may also be fabricated to appear mirror-like on all major surfaces by coextruding a light absorbing layer in the interior of the article. In this embodiment of the invention, the first polymeric material comprises a copolycarbonate of bisphenol-A and 4,4'-thiodiphenol and the second polymeric material suitably comprises polymethyl methacrylate. Alternatively the first material can comprise bisphenol-A polycarbonate or a copolycarbonate derived from thiodiphenol and bisphenol-A monomers and the second polymeric material can comprise a miscible blend or copolymer of polymethyl methacrylate and polyvinylidene fluoride. The reflective polymeric body of the present invention may also be fabricated to act as a birefringent light polarizer which polarizes a broad band of the electromagnetic spectrum. Through proper selection of the polymeric materials making up the layers, a refractive index mismatch in one plane of the polarizer may be achieved. In a preferred method, the refractive index mismatch may be created after fabrication of the reflective polymeric body. The polymeric materials may be selected so that the first material has a positive stress optical coefficient and the second polymeric material has a negative stress optical coefficient. Stretching the body containing the two polymeric materials in a uniaxial direction causes them to orient and results in a refractive index mismatch in the plane of orientation to produce the polarizer. A broad band width of visible light passing through such bodies is polarized. This is in distinction to prior thin film multilayer polarizers which polarized only specific narrow wavelength ranges of light. In a preferred embodiment, the difference in refractive index between the first and second polymeric materials is caused by selecting polymers having differing stress optical coefficients and then stretching those materials in a uniaxial direction to orient the polymeric materials. In this embodiment of the invention, the first polymeric material suitably comprises a copolycarbonate of bisphenol-A and 4,4'-thiodiphenol having a positive stress optical coefficient and the second material comprises a suitably chosen polymer having a negative stress optical coefficient. Alternatively the first material can comprise a suitably chosen polymer having a negative stress optical coefficient and the second polymeric material can comprise of a miscible blend of polymethyl methacrylate and polyvinylidene fluoride. The stress optical coefficient of blends of polymethyl methacrylate and polyvinylidene fluoride may be compositionally adjusted as polymethyl methacrylate has a slightly negative stress optical coefficient while polyvinylidene fluoride has a strongly positive stress optical coefficient. Additionally, the multilayer reflective polymeric bodies of the present invention may be formed into a number of decorative and/or structural parts. The bodies may be formed by coextrusion techniques initially into sheets which may then be post formed. Such post forming operations may include thermoforming, vacuum forming, or pressure forming. Further, through the use of forming dies, the multilayer reflective body may be initially formed into a variety of useful shapes including profiles, tubes, parisons which can then be formed into blow-molded containers. The reflective polymeric bodies of the present invention are also useful in applications such as optical interference films which reflect wavelengths of light in the infrared region of the spectrum while being transparent to wavelengths of light in the visible spectrum. Such optical interference films may be comprised of multiple alternating layers of first, second and third diverse polymeric materials having an optical thickness of between 0.09 and 0.45 micrometers. The present invention provides a highly reflective multilayer polymeric body made up of from a hundred to several thousand alternating layers of polymers which differ from each other in refractive index. A substantial majority of the individual layers of the polymeric materials have an optical thickness of not more than 0.09 micrometers or not less than 0.45 micrometers, where the optical thickness is defined as the product of the individual layer thickness times the refractive index of the polymeric material which makes up that layer. Preferably, the individual layers which make up the multilayer body are substantially continuous. Thus, the multilayer reflective polymeric body of the present invention is made up of multiple alternating optically thick or very thin layers, as opposed to the multilayer "thin film" articles of the prior art. For purposes of optical properties, that is, reflectance and transmittance, a thin film can be described as a film thinner than one wavelength of light at which the film will be applied. Thus, for films to be used in the visible wavelength band, a thin film is described in the literature as one whose thickness, D, is less than 0.5 micrometer or whose optical thickness, ND (where N is the refractive index of the material) is less than 0.7 micrometers. Vasicek, Optics of Thin Films (1960) at pages 100 and 139. Prior art thin film layer articles describe interference films which rely on the constructive optical interference of light to produce intense reflected light in the visible, ultraviolet, or infrared portions of the electromagnetic spectrum for normal incidence according to the equation: λm = (2/m) (N 1 D 1 + N 2 D 2 ), where λm is the reflected wavelength in nanometers, N 1 and N 2 are the refractive indices of the alternating polymers, D 1 and D 2 are the thickness of the respective layers of polymers in nanometers, and m is the order of reflection (m=1,2,3,4,5). Each solution of the equation determines a wavelength at which an intense reflection, relative to surrounding regions, is likely to occur. The intensity of the reflection is a function of the "f-ratio" where, for a two component system, f = N 1 D 1 /(N 1 D 1 + N 2 D 2 ) By proper selection of the f-ratio, one can exercise some degree of control over the intensity of reflection of the various higher order reflections. For example, first order visible reflections of violet (0.38 micrometer wavelength) to red (0.68 micrometer wavelength) can be obtained with layer optical thicknesses between 0.075 to 0.25 micrometers. Iridescent films may also be designed to reflect visible light at higher order reflectances, although at lower intensities. As can be seen, such thin film polymeric bodies are strongly dependent upon film (and individual layer) thickness to determine reflected wavelength. Such thin films are extremely sensitive to thickness changes, and it is characteristic of such thin films to exhibit nonuniform streaks and spots of color. The multilayer bodies of the present invention do not display vivid iridescence. In fact, it is an important object of this invention specifically to avoid layer thicknesses which result in substantial iridescent color. By keeping all layers sufficiently optically thick or optically very thin, higher order reflections are so closely spaced that the human eye perceives the reflection to be essentially silver and non-iridescent. Articles made in accordance with the present invention exhibit a uniform silvery reflective appearance, not the multicolored, iridescent appearance common to prior art thin film multilayer articles. Rather, the reflective characteristics of the multilayer bodies of the present invention are governed by the following equation: R = (kr)/(1 + (k - 1)r) x 100, where R is the amount of reflected light (percent), k is the number of optically thick or optically very thin film layers, and r = [(N 1 - N 2 )/(N 1 + N 2 )] 2 . See Vasicek, Optics of thin Films (1960) at pages 69-70. This equation indicates that the intensity of the reflected light is a function only of r and k, where r and k are defined as above. As a close approximation, R is a function only of the refractive index mismatch of the two polymer components and the total number of layer interfaces. This relationship contrasts greatly with that of prior thin film articles whose reflectivity is highly sensitive to layer thickness and angle of view. Thus, the reflected wavelength of light from the multilayer polymeric body of the present invention is independent of both individual layer and total structure thickness over a wide processing range, so long as a substantial majority of the individual layers has an optical thickness of not less than 0.45 micrometers, or not greater than 0.09 micrometers. Uniformity of reflection is inherent in the design of the body. Moreover, a gradient of layer thickness through the thickness of the body is neither detrimental nor advantageous to the appearance of the body as long as a substantial majority of the individual layers of the polymers maintains an optical thickness as described above. This again contrasts with prior thin film articles which reflect broad or narrow bandwidths depending upon layer thickness gradient. Thus, it is not necessary for all of the layers in the reflective polymeric bodies of the present invention to have optical thicknesses of 0.45 micrometers or greater or 0.09 micrometers or less. The preferred coextrusion process for fabricating the polymeric bodies of the present invention may introduce layer thickness variations both through the thickness of the body and in the plane of individual layers. Variation in layer thicknesses of each polymeric component can be as much as 300 percent or more. However, useful reflective bodies and articles may be made even with such wide variations as long as a substantial majority of the layers have an optical thickness of not more than 0.09 micrometers or not less than 0.45 micrometers. With this condition met, there is an absence of visibly perceived interference colors reflected from bodies and articles of the present invention. The absence of the interference colors which characterize prior art thin films is somewhat subjective to the human eye. However, we have found that 75 percent of the layers in the body must have optical thicknesses greater than 0.45 micrometers or less than 0.09 micrometers to obtain the broad band, visually uniform reflectance of substantially all wavelengths (white light) which characterizes the present invention. A minority of 25 percent or fewer of the layers having optical thicknesses of greater than 0.09 and less than 0.45 micrometers have been found to have interference reflections of a sufficiently low intensity so that the body will have essentially no visibly perceived iridescence. A condition for the selection of the polymers to make up the alternating layers of the body is that the polymers selected have refractive indices which differ from each other by at least 0.131. Further, the polymers should be compatible in processing temperatures so that they may be readily coextruded. By combining thick and very thin layers, it is possible to fabricate polymeric bodies which contain up to 80 percent or more by volume of a first polymer (the thick layers) and 20 percent or less by volume of a second polymer (the very thin layers). This may result in a multilayer structure which has properties similar to the first polymer alone. Further, the resulting laminate may form a structure stronger than would be possible using a combination of alternating thick layers alone. By selecting polymers having relatively large refractive index mismatches, highly reflective multilayer bodies may be produced since reflectance is dependent upon the number of layer interfaces and the refractive index mismatch at each layer interface. A particularly useful class of polymers for use in the present invention are miscible blends of polyvinylidene fluoride and polymethyl methacrylate. Such blends not only have a relatively low range of refractive indices, but also adhere well to polycarbonates having relatively high refractive indices. This eliminates the need for adhesive polymer layers in the body to bond other layers together in the multilayer construction. Additionally, polyvinylidene fluoride is a weatherable polymer possessing outstanding solvent resistance. Further, polyvinylidene fluoride/polymethyl methacrylate blends are significantly more ductile than polymethacrylate alone, which should aid in forming operations. Multilayer bodies in accordance with the present invention are most advantageously prepared by employing a multilayered coextrusion device as described in US-A-3,773,882 and US-A-3,884,606. Such a device provides a method for preparing multilayered, simultaneously extruded thermoplastic materials, each of which are of a substantially uniform layer thickness. Preferably, a series of layer multiplying means as are described in US-A-3,759,647. The feedblock of the coextrusion device receives streams of the diverse thermoplastic polymeric materials from a source such as a heat plastifying extruder. The streams of resinous materials are passed to a mechanical manipulating section within the feedblock. This section serves to rearrange the original streams into a multilayered stream having the number of layers desired in the final body. Optionally, this multilayered stream may be subsequently passed through a series of layer multiplying means in order to further increase the number of layers in the final body. The multilayered stream is then passed into an extrusion die which is so constructed and arranged that streamlined flow is maintained therein. Such an extrusion device is described in US-A-3,557,265. The resultant product is extruded to form a multilayered body in which each layer is generally parallel to the major surface of adjacent layers. The configuration of the extrusion die can vary and can be such as to reduce the thickness and dimensions of each of the layers. The precise degree of reduction in thickness of the layers delivered from the mechanical orienting section, the configuration of the die, and the amount of mechanical working of the body after extrusion are all factors which affect the thickness of the individual layers in the final body. It is necessary, however, that the optical thickness of a substantial majority of the individual layers of polymeric material be not more than 0.09 micrometers or not less than 0.45 micrometers. Reflective polymeric bodies produced by the practice of the present invention may have a wide variety of potentially useful applications. For example, the bodies may be post formed into concave, convex, parabolic, half-silvered, mirrors. If suitably flexible or rubbery polymers (elastomers) are utilized, the bodies may be bent or recoverably stretched into varying shapes. The mirror-like appearance may be accomplished by coextruding a black or otherwise light absorbing layer on one side of the body. Alternatively, one side of the final body may be coated with a colored paint or pigment to provide a highly reflective mirror-like body. Such mirrors would not be subject to breakage as would glass mirrors. The highly reflective polymeric bodies of the invention may be fabricated ass non-corroding metallic appearing articles for indoor or outdoor exposure. For example, the polymeric bodies may be fabricated into signs, or bright work for appliances. The bodies may be post formed into highly reflective parts such as automotive head lamp reflectors, bezels, hub caps, radio knobs, or automotive trim, by processes such as thermoforming, vacuum forming, shaping, rolling, or pressure forming. The bodies may also be formed into silvery or metallic appearing bathroom or kitchen fixtures which do not corrode or flake. A number of different profiles may be coextruded in addition to sheets and films of the reflective polymeric materials. By profiles, we mean shaping of the multilayer body 1) in a forming die into sheets, channels, lenticular cross-sections, round or elliptical tubes, and parisons, or 2) outside of a die by a post forming procedure. For example, decorative moldings such as wall moldings and picture frame moldings, automotive trim and home siding may be readily coextruded through forming dies. Use of a tubular extrusion die produces a multilayered metallic appearing pipe. Such tubular dies may also be used to produce parisons which may then be blow molded into silvery appearing bottles and containers. Because the materials used in the construction of the body may be selected for given desired properties, the final body may be flexible or rubbery, producing an article which could be used as a variable focal length reflector by flexing the article to different degrees. The reflective polymeric bodies of the present invention may also be post formed into a wide variety of items such as two-way mirrors, black bodies for insulation, and solar intensifiers to concentrate solar radiation. The bodies may also be formed into dinnerware, tableware, containers, and packages. By the proper selection of the polymers which were used, such articles may be made to be microwavable. In order that the invention may be more readily understood, reference is made to the following examples, which are intended to be illustrative of the invention, but are not intended to be limiting in scope. Example 1 Employing an apparatus as generally described in US-A-3,773,882 and US-A-3,759,647, a sheet of a reflective polymeric body was prepared. The sheet was approximately 1.2 mm in thickness and had 657 alternating layers (ABABAB) of polycarbonate and a polymethyl methacrylate/polyvinylidene fluoride blend. The respective polymers used were (1) bisphenol-A polycarbonate (BAPC): Calibre 302-22 (trademark of The Dow Chemical Company); (2) polymethyl methacrylate (PMMA): Cyro Acrylite H15-003, (trademark of Cyro Industries); and (3) polyvinylidene fluoride (PVdF): Kynar 720 (trademark of Pennwalt). A substantial majority of the layers in the final sheet had optical thicknesses of at least 0.45 micrometers. The refractive index of BAPC (n 1 ) was 1.590, while the refractive index of PMMA/PVdF (n 2 ) was varied by adjusting the blend composition as shown below. Sample PMMA/PVdF Ratio (weight/weight) Refractive Index (n 2 ) (550 nm) Δn (n 1 -n 2 ) 1 100/0 1.495 0.095 2 80/20 1.479 0.111 3 60/40 1.459 0.131 A series of extruders, gear pumps, and static mixers fed molten polymer streams of BAPC (component A) and PMMA/PVdF blends (component B, which was derived from a salt and pepper extruder feed mixture) to a feedblock which provided a melt stream consisting of 83 alternating layers (ABAB---BABA structure). The layered stream was subsequently passed through three layer multipliers which effected an increase in the total number of layers to 657. An additional extruder provided an outer skin layer of BAPC. The resulting construction was spread in a coathanger style die (width = 40.6 cm, die gap = 3.6 mm) and subsequently passed through cooling rolls in an S-wrap configuration. The BAPC and PMMA/PVdF materials were extruded at a temperature of 260°C. Components A and B were extruded at a rate of 9.5 kg/hr while the skin layer was extruded at a rate of 5.5 kg/hr. The reflectivity of the sheet was determined with a Beckman Model DU-7 spectrophotometer (equipped with a reflectance jig) for wavelengths ranging from 400 nm to 800 nm. The data obtained is shown below. Theoretical reflectivity was calculated using Equation 1, above. Sample PMMA/PVdF Ratio (weight/weight) Percent Reflectivity (550 nm) Theoretical Reflectivity 1 100/0 43 44 2 80/20 50 51 3 60/40 73 58 The results show that as the refractive index mismatch (Δn) between the A and B components is increased, the reflectivity of the body is increased, for bodies having the same number of layers. Example 2 Using the same apparatus and polymers as in Example 1, a reflective multilayer body having 1313 alternating layers was coextruded. The refractive index of the BAPC (n 1 ) was 1.590, while the refractive index of the PMMA/PVdF (n 2 ) was varied by adjusting the blend composition as shown below. Sample PMMA/PVdF Ratio (weight/weight) Refractive Index (n 2 ) (550 nm) Δn (n 1 -n 2 ) 1 100/0 1.495 0.095 2 60/40 1.459 0.131 The BAPC and PMMA/PVdF materials were extruded at a temperature of between 255°C and 265°C. The rates of extrusion were as follows: Sample PC (kg/hr) PMMA/PVdF (kg/hr) Skin (kg/hr) 1 17 8.5 8.0 2 20 6.5 7.5 A reflective sheet was produced in which a substantial majority of the layers had an optical thickness of at least 0.45 micrometers. No iridescent color was observed. The reflectivity of the sheet was determined with a Beckman Model DU-7 spectrophotometer (operating in the transmission mode) for wavelengths ranging from 400 nm to 800 nm. The data obtained is shown below. The theoretical reflectivity was calculated using Equation 1, above. Sample PMMA/PVdF Ratio (weight/weight) Percent Reflectivity (550 nm) Theoretical Reflectivity 1 100/0 60 59 2 60/40 80 73 Again, the results show that by increasing the refractive index mismatch (Δn) between the A and B components, the reflectivity of the body is increased. Example 3 The procedures and equipment described in the preceding examples were used to prepare a sheet of reflective polymeric body. The sheet was approximately 3.2 mm thick and had 2625 alternating layers of PMMA and 4,4'-thiodiphenol/bisphenol-A (TDP/BA) copolycarbonate (coPC). The coPC had a TDP/BA molar ratio of 3/1 and a refractive index of 1.636. BAPC was used to provide protective boundary layers and an outer skin layer. The refractive index mismatch (Δn) for the PMMA and TDP/BA coPC components was 0.141. For comparison, the same procedure was used to prepare a reflective sheet with 2625 alternating layers of PMMA and BAPC and having a thickness of approximately 3.2 mm. The refractive index mismatch (Δn) for the PMMA and BAPC components was 0.095. The reflectivity of these two sheets was determined as described hereinbefore. The data obtained is shown below. Sample PC Type Δn Percent Reflectivity Theoretical Reflectivity 1 TDP/BA 0.141 94 85 2 BA 0.095 72 73 Again, the results show that an increase in the refractive index mismatch (Δn) between the A and B components results in an increase in the reflectivity. While certain representative embodiments and details have been shown for purposes of illustrating the invention, it will be apparent to those skilled in the art that various changes in the methods and apparatus disclosed herein may be made without departing from the scope of the invention, which is defined in the appended claims.

Claims: A reflective polymeric body of at least first and second diverse polymeric materials (A,B) and having a plurality of alternating layers (ABAB) of said first and second polymeric materials differing from each other in refractive index, at least 75 percent of the individual layers of said body having an optical thickness which is either not more than 0.09 micrometers or not less than 0.45 micrometers, with at least one of the individual layers having an optical thickness not less than 0.45 micrometers and there is a sufficient number of said alternating layers that substantially no perceived iridescence is reflected and/or at least 30 percent of light incident on the body is reflected, characterized in that:- the first polymeric material is selected from (i) a copolycarbonate of thiodiphenol and bisphenol-A and (ii) a bisphenol-A polycarbonate; and the second polymeric material is selected from (i) a copolymer of methyl methacrylate and vinylidene fluoride, (ii) a miscible blend of polymethyl methacrylate and polyvinylidene fluoride, (iii) a miscible blend of polymethyl methacrylate and a fluoropolymer which is a copolymer of vinylidene fluoride and a fluorocarbon monomer selected from chlorofluoroethylene, chlorodifluoroethylene, chlorotrifluoroethylene, hexafluoroacetone, hexafluoropropylene, pentafluoropropylene, trifluoroethylene, tetrafluoroethylene and vinyl fluoride, and, when said first polymeric material is a copolycarbonate, (iv) a copolymer of methyl methacrylate, vinylidene fluoride and a said fluorocarbon monomer, said difference in refractive index being at least 0.131, whereby at least 70 percent of said incident light is reflected. A reflective polymeric body as claimed in Claim 1, wherein said first polymeric material is a bisphenol-A polycarbonate. A reflective polymeric body as claimed in Claim 1, wherein the said first polymeric material is a copolycarbonate of bisphenol-A and 4,4'-thiodiphenol. A reflective polymeric body as claimed in Claim 3, wherein the said copolycarbonate comprises from 5 to 80 mole percent 4,4'-thiodiphenol and from 95 to 20 mole percent bisphenol-A. A reflective polymeric body as claimed in Claim 4, wherein the said 4,4'-thiodiphenol is present in a mole ratio of 3 to 1 relative to said bisphenol-A. A reflective polymeric body as claimed in Claim 1, wherein said second polymeric material is selected from:- a. a copolymer comprising in polymerized form from 95 to 5 mole percent methyl methacrylate and from 5 to 95 mole percent vinylidene fluoride, b. a blend which comprises from 95 to 5 weight percent polymethyl methacrylate and from 5 to 95 percent polyvinylidene fluoride, c. a copolymer comprising in polymerised form from 90 to 10 mole percent methyl methacrylate, from 5 to 45 mole percent vinylidene fluoride, and from 5 to 45 mole percent of the said fluorocarbon monomer, and d. a blend which comprises from 95 to 5 weight percent polymethyl methacrylate and from 5 to 95 percent of the said fluoropolymer. A reflective polymeric body as claimed in Claim 6, wherein said material is a miscible blend of polymethyl methacrylate and polyvinylidene fluoride, wherein said polymethyl methacrylate is present in a weight ratio of 1:1 relative to said polyvinylidene fluoride. A reflective polymeric body as claimed in any one of the preceding claims, in which at least 75 percent of said individual layers of said first polymeric material have an optical thickness of at least 0.45 micrometers. A reflective polymeric body as claimed in any one of Claims 1 to 7, in which at least 75 percent of said individual layers of said first polymeric material have an optical thickness of 0.09 micrometers or less. A reflective polymeric body as claimed in any one of the preceding claims, in which said body comprises at least 100 layers. A reflective polymeric body as claimed in any one of the preceding claims, in which said body comprises at least 500 layers. A reflective polymeric body as claimed in any one of the preceding claims, in which said polymeric body is thermoformable. A reflective polymeric body as claimed in any one of the preceding claims, in which a coloring agent is incorporated into at least one layer of said polymeric body. A reflective polymeric body as claimed in Claim 13, in which said coloring agent is a pigment or a dye. A reflective polymeric body as claimed in Claim 13, in which said coloring agent is incorporated into at least one surface layer of said polymeric body. A reflective polymeric body as claimed in Claim 13, in which said coloring agent is incorporated into at least one interior layer of said polymeric body. A reflective polymeric body as claimed in any one of the preceding claims, in which at least one surface layer has a brushed or roughened surface, in which at least one surface layer has been etched to provide a matte or pewter finish, or in which at least one surface layer has been embossed. A reflective polymeric body as claimed in any one of the preceding claims, in which at least one of said first and second polymeric materials is an elastomer. A reflective polymeric body as claimed in any one of the preceding claims, in which said body is in the form of a sheet having two major surfaces, is extruded as a profile, or is post formed into a profile. A reflective polymeric body as claimed in Claim 19, in which said body is in the form of a tube or a blow-molded container. A reflective polymeric body as claimed in any one of the preceding claims, which includes a barrier layer as an exterior layer of said body. A reflective polymeric body as claimed in Claim 21, in the form of a sheet including a permanent protective skin layer on at least one major surface thereof. A reflective polymeric body as claimed in any one of the preceding claims, comprising a mirror like polymeric article having at least first and second major surfaces and including at least one interior light absorbing layer. A reflective polymeric body as claimed in any one of the preceding claims, in the form of a birefringent light polarizer which reflects light anisotropically, wherein said first and second polymeric materials differ from each other in refractive index by at least 0.1 in one plane of the polarizer. The reflective polymeric body as claimed in Claim 24, in which the difference in refractive index between said first and second polymeric materials is caused by stretching said materials in a uniaxial direction to orient said polymeric materials.

Inventors: BALES STEPHEN E, BARGER MARK A, LANGHOFF CHARLES A, RAMANATHAN RAVI, SCHRENK WALTER J, WHEATLEY JOHN A, BALES, STEPHEN E., BARGER, MARK A., LANGHOFF, CHARLES A., RAMANATHAN, RAVI, SCHRENK, WALTER J., WHEATLEY, JOHN A.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1992
Main classification: G02B5
IPC codes: C08L33, C08L27, B32B27, B32B7, G02B5, G02B1