USE OF ALKOXYLATED ALKANOLAMIDE AS FRICTION-REDUCING AGENT

Abstract: Use of an alkoxylated alkanolamide of general formula (I), wherein R is a hydrocarbon group having 7-35 carbon atoms, preferably 9-23 carbon atoms, A is an alkyleneoxy group having 2-4 carbon atoms, and n is 2-20, preferably 3-12, for producing a water-base liquid system with reduced flow resitance between the flowing, water-base liquid system and a solid surface.

Description: USE OF ALKOXYLATED ALKANOLAMIDE AS FRICTION- REDUCING AGENT The present invention relates to the use of an ai oxylated alkanolamide in a water-base system for reduc¬ ing the flow resistance between a solid surface and the water-base liquid system. It is well-known that the flow resistance of a liquid in a conduit is largely due to the turbulence that arises at the conduit wall. However, much of this turbulence can be prevented by adding to the liquid a sufficient amount of elongate particles. The size of these particles may vary within several orders of magnitude, from severed textile fibres, water-soluble chain molecules down to cylindrical surfactant micelles, i.e. within the range of 10 -7-10-2 m. The reduction of the pressure drop that can be achieved by such additions is considerable, and has, in commercial hot-water systems, been assessed at 75%, which involves corresponding savings in supplied pump energy or, alternatively, permits further extension of the distribu¬ tive network with the same pump installations. In most cases, the addition of fibres is inconve¬ nient, since various filters often are incorporated in circulating liquid systems, and the water-soluble chain polymers are torn by the high shear forces in the pumps and thereby lose their effect. Surfactants with the ability to form extremely long, cylindrical micelles have, in recent years, attracted a great interest as friction-reducing additives to systems with circulating water, especially those destined for heat or cold distribution. An important reason for this interest is that, although one desires to maintain a laminar flow in the conduits, one wishes at the same time to have turbulence in the heat exchangers to achieve therein a high heat transfer per unit area. As may easily be understood, fibres or chain polymers are unable to provide this double function which, however, can be achieved with rod-shaped micelles, since the flow rate (the Reynold's number; usually is much higher in the heat exchangers than in the conduit. The rod-shaped micelles are distinguished by operat¬ ing in a fairly disorderly fashion at low Reynol 's nu - 4 bers (below 10 ) and having no or only a very slight effect on the flow resistance. 4 At higher Reynold's numbers (above 10 ), the micelles are paralleled and result in a friction reduction very close to that which is theoretically possible. At even higher Reynold's numbers (e.g. above 10 ), the shear forces in the liquid become so high that the micelles start to get torn and the friction-reducing effect rapidly decreases as the Reynold's numbers increase. The range of Reynold's numbers within which the sur¬ face-active agents have a maximum friction-reducing effect is heavily dependent on the concentration, the range increasing with the concentration. By choosing the right concentration of surface-active agents and suitable flow rates in tubings and heat ex¬ changers, it is thus possible to establish a laminar flow in the tubes and turbulence in the heat exchangers. Thus, the dimensions of both the tubes and the exchangers can be kept at a low level, or the number of pump stations, and consequently the pump work, can alternatively be reduced while retaining the same tubular dimensions. The surface-active agents hitherto used as friction- reducing additives to circulating water systems - mainly destined for heat or cold distribution - are all of the type alkyltrimethyl ammonium salicylate of the chemical formula wherein R represents a long alkyl chain which has 16-22 carbon atoms and which may either be saturated or contain one or more double bonds. This type of surface-active agent functions satisfac- torily already at a concentration of 0.5-1 g/1, but is άegraded very slowly, both aerobically and anaerobically, and further is highly toxic to marine organisms. Since heat-distribution systems for small houses usually suffer from important leaks (it is estimated that in one year 60-100% of the water leaks out), it follows that the added chemicals end up in the ground water and in various fresh-water recipients. This combination of low biodegradability and high toxicity is a fundamental criterion for a product injurious to the environment. Thus, there is a general demand for surface-active agents which are less harmful to the environment but which have the same excellent ability as the quaternary ammonium compounds described above to reduce the flow resistance in circulating water systems. It has now surprisingly been found that a long since well-known type of non-ionic surface-active agents, namely alkoxylated alkanolamides, are capable of forming long cylindrical micelles. In flow tests in water-base systems, they had a friction-reducing effect well up to the effect achieved by the above-mentioned alkyltrimethyl ammonium salicylate. To be more specific, the invention relates to the use of an alkoxylated alkanolamide of the general formula 0 wherein R is a hydrocarbon group having 7-35 carbon atoms, preferably 9-23 carbon atoms, A is an alkyleneoxy group having 2-4 carbon atoms, and n is 2-20, preferably 3-12, for producing a water-base liquid system with reduced flow resistance between the liσuid water-base system and a solid surface. By 'water-base' is meant that at least 50% by weight, preferably at least 90% by weight, of the water-base liquid system consists of water. The alkoxylat¬ ed alkanolamide is especially suited for use in water-base systems flowing in long conduits, e.g. circulating water systems for heat or cold distribution. The amount of alkoxylated alkanolamide may vary within wide limits depending on the conditions, but generally is 100-10,000 g/m of the water-base system. The alkoxylated alkanolamide can be produced by ami- dation of a carboxylic acid of the formula RC00H, wherein R has the meaning stated above, with an alkanolamine of the formula NHAH, wherein A has the meaning stated above, or by aminolysis of a corresponding triglyceride or methyl ester with the above-mentioned alkanolamine followed by alkoxylation of the resulting amide. The alkoxylation may be carried out in the presence of an alkaline catalyst at a temperature of 150-180°C. It is especially suitable to carry out the alkoxyla- tion in the presence of a tertiary amine lacking protons that react with alkylene oxide, or an alk lene-oxide- quaternised derivative of the tertiary amine at a tempe¬ rature ranging from room temperature to 120°C, which results in high yields of the desired product. Suitable tertiary amines include trimethylamine, triethylamine, tributyl mine, dimethyloctylamine, tetramethylethylene- diamine, dimethyl coconut amine, tristearyl amine, dimethyl piperazine and diazabicyclooctane. The alkoxylation may comprise ethoxylation, propoxy- lation, addition of propylene oxide and ethylene oxide in blocks, simultaneous addition of ethylene oxide and pro¬ pylene oxide, or a combination thereof.. The ethylene oxide conveniently amounts to at least 50 mole% of the added alkylene oxide. To use only ethoxylation is preferred. The carboxylic acids of the formula RCOOH, wherein R has the meaning stated above, may be aliphatic, aromatic as well as cycio-aliphatic. Suitable carboxylic acids include the aliphatic carboxylic acids in which the hydro¬ carbon part may be saturated cr unsaturated, straight cr branched. To use conventional fatty acids is especially preferred. Suitable alkoxylated alkanolamides include the fol¬ lowing specific examples: 0 0 RCNΗ(CH.O)„H, wherein RC is derived from rape cil fatty acid, o 0 II I! RCNH(C 2 H 4 0) 7 H, wherein RC is derived from rape oil fatty acid, 0 0 II I! RCNHCO ) HO,0(C- ) H4 / ,0)- ! H, wherein RC is derived from lauri acid, 0 0 II II RCNH(C-H.O).H, wherein RC is derived from lauric aci 0 0 II II RCNHC 2 H 4 0(A).H, wherein RC is derived from stearic acid, and the group A is random added from equal mole parts of ethy¬ lene oxide and propylene oxide 0 0 II II CNHC.HgC C-H.Oh Q H, wherein RC is derived from lino- lenic acid. The choice of chain length and degree of unsaruration is determined by the temperature range in which the alkoxylated alkanolamide is to operate. A higher tempera¬ ture requires a larger hydrocarbon group and less unsatu- ration. The choice of the degree of alkoxylation is determined by the size and degree of saturation of the hydrocarbon group as well as by the temperature. Whether the right degree of alkoxylation has been reached is easily established by determining the cloud point cf the alkoxylated alkanolamide in a 1% solution in the water- base system. Below the cloud point, i.e. the alkoxylated alkanolamide is solved in the water-base system, the ability of the alkoxylated alkanolamide to reduce the flow resistance increases as the temperature increases, whereas this ability decreases at higher temperatures, at which the alkoxylated alkanolamide is precipitated. Thus, the degree of alkoxylation and the alkyleneoxy group present should be selected in such a manner that the cloud point of the alkoxylated alkanolamide is equal to or slightly below the temperature prevailing in the water-base system 4 at laminar flow, e.g. at Reynold's numbers between 10 and 10 . When the temperature of the water-base system varies considerably, e.g. when the system is used as heating medium in long tubings, the cloud point of the alkoxylated alkanolamide should at least exceed the lowest temperature prevailing in the water-base system at laminar flow. Pre¬ ferably, the cloud point should exceed the highest tem¬ perature of the water-base system at laminar flow. Adjust- ment to the desired cloud point may conveniently be per¬ formed by mixing alkoxylated alkanolamides of different cloud points. Such mixtures may also be advantageous when the temperature in the water system at laminar flow varies considerably. When using the water-base system for cold distribu¬ tion, it is essential that the Krafft point of the alkoxylated alkanolamide, i.e. the temperature at which the alkoxylated alkanolamide starts to crystallise in the water-base system, is below the lowest temperature in the water-base system. The Krafft point may be decreased by selecting fatty acids with shorter alkyl chains and/or unsaturated fatty acids. A higher degree of ethyiation as well as incorporation of soluble salts in the water-base system will also decrease the Krafft point. When used as a cooling medium, the temperature of the water-base system is suitably below 30°C, preferably below 20°C. Apart from the alkoxylated alkanolamide, the v.-arer- base system may contain a number of conventional compo¬ nents, such as rust-preventing agents, anti-freeze, and bactericides. The system may also include solubilisers, such as diethylene glycol monobutyl ethers, which may affect the cloud point of the alkoxylated alkanolamides in the water-base system quite considerably. The present invention will now be further illustrated with the aid of the following Example. ExemD -le Measurements were carried out in a 6-m tube loop consisting of two straight and stainless tubes (3 m each), one tube having an inner diameter of 8 mm and the other having an inner diameter of 10 mm. Water was pumped through the tube loop by a centrifugal pump, which was driven by a frequency-controlled motor, for continuous adjustment of the flow rate, which was determined by a rotameter. The straight parts of the tube loop had outlets which, with the aid of valves, could in turn be connected to a differential pressure gauge whose other side was all the time connected to a reference point in the tube loop. Further, the tube loop was heat-insulated, and the suction side of the pump was connected to a thermostatically controlled container with a volume of 20 1, to which the return flow from the tube loop was directed. After the testing compound had been added and the aqueous solution had been thermostatically controlled, measurements began at low flow rates, and the pressure difference from two points on the 10-mm tube and three points on the 8-mm tube were measured for each flow rate. The pressure differences thus measured were then converted into Moody's friction factor Y and are shown in the Table below as a function of the Reynold's number Re. Y = 2D.P diff /V . .d Re = D.V.d/u D = tube diameter V = flow rates L = tube length over which the pressure difference P diff was measure ° d = density of the liquid u = viscosity of the liquid The Table also states the corresponding Prandtl num¬ ber and Virk number. The former corresponds to the fric¬ tion factor of water only, i.e. with turbulence, and the latter corresponds to flow without turbulence. One of the following compounds was added as testing compound A Cetyl trimethyl ammonium salicylate B C 12-14 a l c °h°l + 6 EO C 50% by weight of rape oil fatty acid ethanolamide + 3 EO 50% by weight of rape oil fatty acid ethanolamide + 6 EO (The cloud point of the mixture was 56°C in water) The following results were obtained. Table 1 Compound A, addition of 1000 ppm, temperature of 50°C Moody's friction fractor 10' Reynold's number 10 ' 2x10 4x10 ' 6x10 ' 8x10 Table 2 Compound B, addition of 20 g/1, temperature of 80°C, Moody's friction factor Moody's friction factor . 10 * Reynold's number 1(T 2x10 4x10 6x10 8x10 Prandtl number 30 10 mm 8 mm Virk number 10 Table 3 Compound C, addition of 6000 ppm, temperature of 25°C, Moody's friction factor Moody's friction factor . 10" Reynold's number 10 ' 2x10 ' 4x10 6x10 ' 8x10 As is apparent from these results, the invention gives a friction reduction down to the theoretically pos¬ sible level (the Virk line), in analogy with prior-art results with alkyltrimethyl ammonium salicylate, and this is not possible with common non-ionic surface-active agents of the type fatty alcohol ethoxylate. Compared with the prior-art quaternary ammonium compounds, the friction- reducing agent according to the invention is advantageous in that it is much less toxic to water organisms and is biologically degraded much faster, both aerobically and anaerobically. The friction-reducing agent according to the invention may thus be used as a friction-reducing additive also to heat-distribution systems where there is a certain amount of leakage.

Claims: CLAIMS 1. Use of an alkoxylated alkanolamide of the general formula RCNH(A) H II n O wherein R is a hydrocarbon group having 7-35 carbon atoms, preferably 9-23 carbon atoms, A is an alkyleneoxy group having 2-4 carbon atoms, and n is 2-20, preferably 3-12, for producing a water-base liquid system with reduced flow resistance between the flowing, water-base liquid system and a solid surface. 2. Use as claimed in claim 1, c h a r a c t e r ¬ i s e d in that n is so chosen that the alkoxylated alkanolamide, in the concentration in which it is used in the water-base system, has a cloud point which is higher than the lowest temperature of the water-base system s laminar flow. 3. Use as claimed in claim 2, c h a r a c t e r ¬ i s e d in that the cloud point is higher than the highest temperature of the water-base system. 4. Use as claimed in claim 1, 2 or 3, c h a r a c - t e r i s e d in that the water-base system is a hot- water system with a temperature exceeding 60°C. 5. Use as claimed in claim 1, 2 or 3, c h a r a c ¬ t e r i s e d in that the water-base system is a cooling medium with a temperature below 30°C. 6. Use as claimed in any one of claims 1-5, c h a r ¬ a c t e r i s e d in that the alkoxylated alkanolamide 3 is added in an amount of 100-10,000 g/cm of the water-base system. 7. Use as claimed in any one of claims 1-6, c h a - a c t e r i s e d in that at least half of the alkyleneoxy groups are ethyleneoxy groups. 8. Use as claimed in claim 7, c h a r a c t e r i s e d in that A is an ethyleneoxy group.

Inventors: HARWIGSSON IAN, HELLSTEN MARTIN, HARWIGSSON, IAN, HELLSTEN, MARTIN
Applicants: BEROL NOBEL AB
Application year: 1992
Main classification: C09K3
IPC codes: C07C233, C09K3, C09K5, C10M133, C10M173, C10N30