Polystyrene modified with silicone rubber powder

Abstract: A crumb-like silicone rubber powder is uniformly dispersed in a polystyrene polymer using conventional equipment, such as a twin screw extruder, to provide a resin having up to a ten fold improvement in impact strength over the unmodified polymer. The novel silicone rubber powder of the invention is prepared by isolating the particles obtained from a polymerization of an unsaturated monomer in the presence of an aqueous emulsion of a hydroxyl-functional polydiorganosiloxane which has been precured using an organotin curing catalyst and a crosslinker which contains unsaturated functionality.

Description: The present invention relates to polystyrene polymer compositions having high impact strength. More particularly, the invention relates to polystyrene polymers which are modified with a silicone rubber powder prepared by polymerizing an unsaturated monomer in the presence of an aqueous emulsion of a precured polydiorganosiloxane. Polystyrene (PS) is one of the largest volume thermoplastic resins in commercial production today. This ubiquitous material is well suited to many "low performance" applications wherein its brittle nature is of little consequence. Additionally, many other applications requiring greater impact resistance have been uncovered by the advent of various modifications of these plastics. Thus, styrene-based copolymers, and particularly PS resins which are modified with organic rubber particles, have been a commercially viable alternative to some of the more exotic and expensive engineering plastics for certain applications. One such system, known in the art as high impact polystyrene (HIPS), can have an impact strength which is an order of magnitude greater than the virgin resin but suffers from poor thermal stability, particularly in the presence of oxygen. These modified PS resins are typically prepared by polymerizing a solution of an unsaturated organic rubber, such as polybutadiene, in styrene monomer. EP-A-0 166 900 discloses polystyrene which is modified by a polysiloxane-based graft polymer. These materials also show improved impact resistance. The addition of various rubber compositions to other thermoplastic resin systems has also proved beneficial. For example, Japanese Kokai Patent Application No. Hei 2(1990)-263861 to Mitsubishi Rayon Co., Ltd. discloses a thermoplastic resin composition having a high impact strength, high heat resistance and good resistance to organic solvents. This composition comprises a blend of polyphenylene ether (PPE) resin, a polyester resin and a rubber-like elastomer and/or modified rubber-like elastomer. A preferred elastomer component of this prior art disclosure is obtained by the graft copolymerization of at least one vinyl monomer with a composite rubber consisting of a silicone rubber and a polyalkyl methacrylate "interlocked with each other in an inseparable way." In the production of the composite rubber component, a cyclic diorganosiloxane is emulsion polymerized with a crosslinker and, optionally, with a graft crosslinking agent using a sulfonic-acid-series emulsificating agent. In a subsequent step, a combination of an alkyl (meth)acrylate, a crosslinker and a graft crosslinking agent is used to swell the silicone particles of the above emulsion and an initiator is then introduced to polymerize this system. In a similar approach, United States Patent No. 5,047,472 to Alsamarraie et al. teaches thermoplastic molding compositions comprising PPE resin or a PPE resin containing a polystyrene resin, which is modified with a multi-stage polyorganosiloxane/ vinyl-based graft polymer. These compositions are stated to have improved impact resistance, flame resistance and moldability. In this case, the graft copolymer is prepared by a "co-homopolymerization" technique wherein an emulsion containing a diorganosiloxane, a crosslinker and a graft-linker is polymerized concurrently with the polymerization of a vinyl monomer. The resulting first stage polymeric co-homopolymerized substrate is then grafted with a vinyl polymer in at least one subsequent stage. This multi-stage polydiorganosiloxane polyorganosiloxane/vinyl-based graft polymer formed according to the methods described by Alsamarraie et al. was also employed by Derudder et al. in United States Patent No. 4,939,205 to augment the impact resistance of polycarbonate resin compositions. The graft polymer was further used by Wang in United States Patent No. 4,939,206 to modify various thermoplastic resins with the object of providing flame retardant compositions having improved impact resistance. It has now been discovered that certain silicone rubber powders can be used to advantageously modify polystyrene resins and thereby impart improved impact resistance to the PS resins. The particular silicone rubber powder used in this modification is produced by polymerizing an unsaturated monomer in the presence of an aqueous emulsion of precured polydiorganosiloxane particles, whereupon the resulting particles are harvested from the emulsion. For its part, the aqueous polydiorganosiloxane emulsion employed is produced according to the methods disclosed by Liles in United States Patent No. 4,954,565 and by Schoenherr in United States Patent No. 4,618,642. Unlike the polydiorganosiloxane emulsions of the prior art cited above, wherein the particles of the polydiorganosiloxane emulsion are concurrently polymerized and crosslinked, the instant systems are based on an emulsion wherein a diorganosiloxane is first polymerized and subsequently crosslinked. It has surprisingly been found that a substantial improvement in the impact resistance of polystyrene polymers is obtained when the silicone rubber powder used to modify PS is made from particles of the precured polydiorganosiloxane emulsions taught by Liles and Schoenherr and subsequently modified with the unsaturated monomer rather than from an emulsion wherein diorganosiloxanes are simultaneously polymerized and crosslinked. Moreover, the instant method does not contemplate the inclusion of the vinyl monomer required in the first stage polymeric co-homopolymerized substrate as taught by Alsamarraie et al., Derudder et al. and Wang, cited supra. This further simplifies the production of the silicone rubber powder which is used to modify the PS resins of the invention. Polystyrene resins modified with the silicone rubber powders of the present invention exhibit up to a ten-fold improvement in impact resistance over the virgin polystyrene. The rubber powders of the present invention are also readily dispersible in the polystyrene resins using conventional process equipment, such as a twin screw extruder. This offers a significant advantage to a plastics manufacturer since both resin and modifying rubber ingredients can be handled as particulate solid feeds and are therefore amenable to facile introduction to mixing equipment (e.g., from a hopper). These powdered rubbers can also be formulated as a "master batch" and used as a concentrate to further modify styrenic plastics. The present invention, therefore, relates to a composition consisting essentially of a uniform blend of (A) a polystyrene polymer; and (B) a silicone rubber powder uniformly dispersed in said polystyrene polymer, said silicone rubber powder being prepared by the steps comprising (I) forming an aqueous emulsion consisting essentially of a plurality of particles of a hydroxyl-terminated polydiorganosiloxane having a weight average molecular weight greater than 50,000, wherein the average particle size is from 0.1 to 10 microns, (II) precuring the polydiorganosiloxane particles within said emulsion with an organotin curing catalyst and a crosslinker selected from the group consisting of a silane having the general formula QSi(X)₃ and partial hydrolysis condensation products thereof, wherein X is a hydrolyzable group selected from the group consisting ofalkoxy radicals having 1 to 6 carbon atoms, chloro, hydrido, acetoxy, diorganoamino, oximato and amido groups and in which Q represents a monovalent radical which contains an unsaturated group, (III) thereafter polymerizing an unsaturated monomer in the presence of the emulsion of precured polydiorganosiloxane particles formed in step (II) and (IV) harvesting the particles resulting from step (III), wherein said composition contains from 5 to 50 parts by weight of said polydiorganosiloxane for each 100 parts by weight of said polystyrene polymer. The polystyrene (PS) polymer (A) of the present invention is well known in the art and is a homopolymer or copolymer of styrenic monomers. For the purposes of the present invention, styrenic monomers are substituted or unsubstituted versions of the basic structure Examples of such monomers are styrene, alpha-methylstyrene, chloromethylstyrene and divinyl benzene, inter alia. These monomers are well known in the art and further description thereof is not considered necessary, the interested reader being referred to pages 1-246 of volume 16 of the "Encyclopedia of Polymer Science and Engineering" published by John Wiley & Sons (1989). General purpose polystyrene, which is basically an atactic homopolymer, is the most commercially significant PS type and is a preferred component (A). It is, however, also contemplated that the less prevalent syndiotactic and isotactic homopolymers, as well as copolymers of styrene with such monomers as acrylates, acrylonitrile and butadiene, also derive significant benefit from modification according to the present invention. Component (B) is a silicone rubber powder which is prepared by harvesting precured silicone emulsion particles, which particles have an unsaturated monomer copolymerized therewith. This component is prepared by the following sequence. First, an aqueous silicone emulsion (i) of a hydroxyl-terminated polydiorganosiloxane is prepared by methods well known in the art. In addition to the polydiorganosiloxane and water, component (i) also contains at least one surfactant which stabilizes the dispersed polydiorganosiloxane particles in the emulsion. In order to achieve the intended impact modification characteristics, described infra, the polydiorganosiloxane particles of this emulsion should have an average size of 0.1 to 10 microns, preferably from 0.5 to 1 micron and be characterized by a weight average molecular weight of greater than 50,000, preferably greater than 100,000. It is preferred that the above described emulsion have a solids content ranging from 20 to 70 weight percent, most preferably 65%. These emulsions are well known in the art and may be prepared, for example, by methods wherein cyclic or linear diorganosiloxane species are dispersed in an aqueous continuous phase with the aid of the above mentioned surfactant and are thereafter emulsion polymerized by the introduction of an acid or base catalyst. These methods can be illustrated by the disclosures of United States Patent No. 3,294,725 to Findlay et al. and United States Patent No. 2,891,920 to Hyde et al., among others. In preferred embodiments of emulsion (i), the surfactant employed is an anionic type, such as sodium lauryl sulfate or ammonium lauryl sulfate and the catalyst is dodecylbenenzene sulfonic acid, the latter also acting as a surfactant in the system. For the purposes of the present invention, the organic groups of the polydiorganosiloxane of emulsion (i) are independently selected from hydrocarbon or halogenated hydrocarbon radicals such as alkyl and substituted alkyl radicals containing from 1 to 20 carbon atoms; cycloalkyl radicals, such as cyclohexyl; and aromatic hydrocarbon radicals, such as phenyl, benzyl and tolyl. Preferred organic groups are lower alkyl radicals containing from 1 to 4 carbon atoms, phenyl and halogen-substituted alkyl such as 3,3,3-trifluoropropyl. Thus, the polydiorganosiloxane can be a homopolymer, a copolymer or a terpolymer containing such organic groups. Examples include systems comprising dimethylsiloxy units and phenylmethylsiloxy units; dimethylsiloxy units and diphenylsiloxy units; and dimethylsiloxy units, diphenylsiloxy units and phenylmethylsiloxy units, among others. Most preferably, the polydiorganosiloxane is a polydimethylsiloxane which is terminated with a hydroxyl group at each end of its molecule. In the second step in the production of the silicone rubber powder, an organotin curing catalyst (ii) and a crosslinker (iii) are added to the above described aqueous emulsion (i) to crosslink the hydroxyl-terminated polydiorganosiloxane particles dispersed therein. The organotin curing catalyst (ii) is an organic salt of tin and may be illustrated by tin (II) carboxylates, such as stannous oleate and stannous naphthanate; dialkyl tin (IV) carboxylates, such as dibutyltin diacetate and dibutyltin dilaurate; and tin (IV) stannoxanes, as exemplified by the structure (Bu)₂SnC1-O-Sn(Bu)₂OH, in which Bu denotes a butyl radical, as taught by Stein et al. in United States Patent No. 5,034,455. In preferred embodiments, catalyst (ii) is stannous octoate. Crosslinker (iii) is a silane having the general formula QSi(X)₃ or a partial hydrolysis condensation product thereof. In the above formula, X is a hydrolyzable group selected from the group consisting of alkoxy radicals having 1 to 6 carbon atoms, chloro, hydrido, acetoxy, diorganoamino of the structure -NR₂, oximato of the structure ON=CR₂ or amido of the structure -N(R)C(O)R, in which each R is independently selected from hydrogen, alkyl radicals having 1 to 6 carbon atoms or a phenyl radical and Q represents a monovalent radical which contains at least one unsaturated group capable of free-radical polymerization, preferably having the structure -CA=CH₂, in which A is hydrogen or an alkyl radical having 1 to 6 carbon atoms. This group is attached to the silicon atom of the crosslinker through a divalent organic connecting group having up to about 6 carbon atoms. The exact nature of this connecting group is not critical as long as it does not interfere with the other components and operations of the invention. Preferably, the crosslinker is a silane having the general formula Q'Si(OR')₃ in which R' is an alkyl radical having 1 to 6 carbon atoms and Q' is selected from the group consisting of acryloxypropyl, methacryloxypropyl, vinyl, allyl, hexenyl, acrylamidopropyl and a moiety containing vinylbenzyl functionality. In highly preferred silane crosslinkers, R' is a methyl radical and Q' is a methacryloxypropyl group. Specific examples of suitable silane crosslinkers include gamma-acryloxypropyltrimethoxysilane, gamma-methacryloxypropyltrimethoxysilane, vinyltrimethoxysilane, 5-hexenyltrimethoxysilane, allyltrimethoxysilane, acrylamidopropyltrimethoxysilane and silanes represented by the formulas and HCl · ZN(H)-CH₂CH₂-N(H)-CH₂CH₂CH₂-Si(OMe)₃, wherein Me hereinafter denotes a methyl radical and Z is a vinylbenzyl group having the formula Although order of addition in this second step is not considered critical, it is preferred to first add from 0.05 to 2 parts by weight, preferably from 0.3 to 0.6 parts, of the catalyst (ii) to 100 parts by weight of the hydroxyl-terminated polydiorganosiloxane in emulsion (i). From 0.1 to 10 parts by weight, preferably about 1 part, of the crosslinker (iii) is then added to this mixture for each 100 parts by weight of the polydiorganosiloxane and the resultant emulsion is allowed to age to precure the polydiorganosiloxane within the emulsion. When the silane crosslinker content is less than about 0.1 part, incomplete cure is observed; when this component exceeds about 10 parts, the byproducts formed when the hydrolyzable group X is reacted destabilize the emulsion. During the aging process, which can take place at room temperature as well as at elevated temperatures, the pH of the emulsion should be maintained between about 4 and 10.5. Aging is deemed sufficient when an aliquot of the emulsion forms an elastomeric film after being cast upon a substrate and dried thereon. In order to be within the scope of the invention, this elastomeric film must only be swollen by a good solvent for the polydiorganosiloxane (such as hexane or toluene) but must not be totally dissolved thereby. Generally, the gel fraction of this film should be greater than 50 weight percent and preferably in the range of 80 to 90% by weight. Further details regarding the above three steps used to prepare the silicone rubber powder of the invention may be found in previously cited United States Patent No. 4,618,642 to Schoenherr and United States Patent No. 4,954,565 to Liles, which patents teach these precured systems in combination with fillers for use as elastomeric coatings. In a third step, at least one unsaturated monomer (iv) is polymerized in the presence of the emulsion of precured polydiorganosiloxane particles formed in the second step. The unsaturated groups of this monomer must be capable of reacting with the unsaturated groups of the silane crosslinker (iii). Further, the monomer (iv) is selected such that, when it is homopolymerized using a conventional free-radical initiator, it results in a polymer having a glass transition temperature of at least 0°C. Preferably, component (iv) is a styrenic monomer of the type described in connection with component (A). Examples of other suitable unsaturated monomers include acrylates, methacrylates, acrylonitrile and vinyl acetate. In a preferred procedure for the third step, a free-radical initiator (iv) is added to the emulsion resulting from the above described second step and at least one unsaturated monomer, preferably a styrenic monomer, is gradually introduced. The preferred styrenic monomer is of the same type described above for use in the manufacture of component (A) and is compatible therewith. Most preferably, it is chemically identical to the monomer used to produce component (A). It is preferred that from 10 to 80 parts by weight, most preferably from 25 to 55 parts by weight, of the unsaturated monomer is added to the emulsion based on 100 parts by weight of the polydiorganosiloxane content thereof. Suitable initiators to be used in this third step are those which are known to polymerize the unsaturated monomer (iv). These include azo compounds, such as azobisisobutyronitrile and 2,2'-azobis(2-methylbutyronitrile), organic peroxides, such as acetyl peroxide, cumene hydroperoxide and benzoyl peroxide and inorganic compounds such as potassium persulfate and ammonium peroxydisulfate, the azo compounds being preferred. The initiator is typically employed at a level of 0.05 to 0.2 parts by weight for each 100 parts by weight of the monomer (iv) and is introduced as an organic solvent solution or, preferably, admixed with a portion of the monomer. In this polymerization step, the emulsion containing the initiator is preferably stirred at a temperature of 60 to 70°C. while the monomer is slowly added thereto, a typical addition period being in the range of 2 to 3 hours at the above noted temperatures, whereupon the resulting emulsion is heated for an additional 2 to 3 hours. The fourth and final step in the preparation of the silicone rubber powder of the invention involves the "harvesting" or isolation of the above prepared particles from the emulsion. This can be accomplished by first coagulating the particles by any of the standard methods for breaking emulsions, such as freezing, freeze drying, spray drying or the addition of a salt such as calcium chloride. A favored method is one wherein the above formed emulsion is added, at room temperature, to a stirred excess of a watersoluble organic solvent such as acetone, ethylene glycol, ethanol or isopropyl alcohol, the later being preferred. The precipitated particles are then filtered and dried to form a crumb-like silicone rubber powder (B). A composition of the present invention may then be prepared by thoroughly dispersing silicone rubber powder (B) in polystyrene polymer (A) at such a level that from 5 to 50 parts by weight of the polydiorganosiloxane present in (B) are present for each 100 parts by weight of the polystyrene (A). This mixing can be accomplished at elevated temperatures by any of the conventional methods used to disperse various components in thermoplastic resins. The temperature and other conditions to be used in such a mixing operation depend on the particular polymer selected and may be determined by routine experimentation by those skilled in the art. For example, the polystyrene polymer may be mixed according to this method at a temperature from about 180°C. to about 210°C. Alternatively, the silicone rubber powder can be premixed with the polystyrene polymer, which mixture is then fed to an extruder. Examples of suitable equipment for this purpose include such machines as twin screw extruders and single screw extruders, inter alia. In order to obtain optimum impact resistance in the modified PS polymer, sufficient silicone rubber powder is used so as to result in a polydiorganosiloxane content of 10 to 25 parts by weight for each 100 parts by weight of the polystyrene. After components (B) and (A) are thoroughly mixed to provide a uniform blend, this composition can be further processed by conventional techniques, such as extrusion, vacuum forming, injection molding, blow molding or compression molding, to fabricate plastic parts which have significantly improved impact resistance over the unmodified polymer. It is also contemplated herein that the compositions of the invention may further contain fillers and other additives normally employed in conventional styrenic polymers of the art. It is preferred that these systems contain a glass fiber filler which further improves the mechanical properties of fabricated products, particularly when a silane coupling agent is also used, as well known in the art. The compositions find utility in various industrial applications where improved toughness is desired in a PS polymer system. Examples include electrical and electronic insulation components, such as motor, coil and transformer insulation; housings for various electrical and electronic equipment, such as machines and hand tools; structural members, such as foam board insulators; furniture; automotive components, such as engine and interior structural components; aircraft interior components; and freezer-to-oven cookware, inter alia. The following examples are presented to further illustrate the compositions of this invention, but are not to be construed as limiting the invention. All parts and percentages in the examples are on a weight basis and all measurements were obtained at 25°C., unless indicated to the contrary. Example 1 A silicone rubber powder of the present invention was prepared by first forming an anionically stabilized aqueous emulsion of a non-crosslinked, hydroxyl-terminated polydimethylsiloxane according to the method of Example 1 of previously cited United States Patent No. 4,618,642 to Schoenherr, wherein 0.3 parts of a silicone antifoam agent (based on 100 parts of the polydimethylsiloxane) was included in the composition and the solids content was about 67%. This silicone emulsion had a final pH of about 10. Next, the particles of the above silicone emulsion were precured by adding dropwise 6 parts of stannous octoate while stirring a mixture of 1284 parts of the above emulsion diluted with 200 parts of water. This procedure took about five minutes and was followed by the dropwise addition of 13.8 parts of gamma-methacryloxypropyltrimethoxysilane while stirring was continued for three more minutes. After aging overnight at room temperature, the above emulsion was further diluted with 1150 parts of water while being stirred under a nitrogen purge and a solution of 0.3 part of azobisisobutyronitrile (AIBN) in 30 parts of styrene monomer was added dropwise. The emulsion was heated to 70°C. and styrene monomer was added thereto over a period of five hours, the total styrene added, including that associated with the AIBN solution, being 300 parts. After heating the stirred emulsion for three hours, 2.5 liters of the emulsion was poured through a fine screen into the vortex of a stirred alcohol bath containing 5 liters of isopropyl alcohol. The coagulated emulsion was stirred for an additional 30 minute period, whereupon the solids were separated by centrifugation and washed three times with fresh isopropyl alcohol before being dried at 80°C. for one hour. A white silicone rubber powder was obtained which consisted of crumb-like particles. The above silicone rubber powder was used to modify a general purpose polystyrene (PS) polymer (STYRON™ 685D; Dow Chemical Co., Midland, MI) using a Haake System 90 TW100 extruder (Haake/Fisons Instruments, Paramus, NJ) to form a composition of the present invention containing about 18 parts of polydimethylsiloxane per 100 parts of PS (i.e., 15% polydimethylsiloxane). The extruder conditions employed were: Feed zone 1 temperature =180°C.; Mixing zone 2 temperature = 210°C.; Mixing zone 3 and exit zone 4 temperature = 210°C.; Screw speed = 50 revolutions per minute (rpm); Die = 3.18mm (1/8 inch) diameter strand die. The extrudate from the above mixing operation was cooled, chopped into pellets, dried for 2.5 hours at 100°C..and fabricated into impact test bars measuring 12.7 x 127 x 3.18 mm (1/2 x 5 x 1/8 inch) using a Boy model 15S screw type injection molding machine (Boy Machine Corp., Exton, PA). The molding parameters used were: Mixing zone 1 temperature = (400°F.)204°C Mixing zone 2 temperature = (465°F.)241°C Nozzle zone 3 dial setting = 52. Mold temperature = (110°F.)43°C Injection pressure =(1,800 psi.) 1.24 x 10⁴ KPa Screw discharge set point = 3.0. Mold clamp pressure = (3,700 psi.)2.55 x 10⁴ KPa Screw speed = 100 rpm. Shot size dial = 36. Mold time = 30 seconds. The above described impact bars were notched and tested for Izod impact strength according to ASTM D 256 (American Society for Testing Materials). A value of 130.78 Nm/m (2.45 ft-lb/in) was obtained, this being about a ten-fold improvement over the virgin PS. Example 2 Another silicone rubber powder was produced according to the methods outlined in Example 1, wherein 428 parts of the anionically stabilized polydimethylsiloxane emulsion were crosslinked with 2 parts of stannous octoate and 4.8 parts of methacryloxypropyltrimethoxysilane. The resulting emulsion was aged 15 minutes at room temperature, diluted with 400 parts of water and aged overnight. Five hundred parts of water were then added and 0.1 part of AIBN in 3 cc of styrene were mixed in at a temperature of 50°C. and under a nitrogen purge. Styrene monomer was then introduced over about a four hour period as the temperature of the emulsion was maintained between 50 and 65°C. (total styrene added = 100 parts). After standing at room temperature for two days, silicone rubber powder was recovered by pouring the above emulsion into isopropyl alcohol, washing the coagulated solids followed by drying in ambient air. The silicone rubber powder had a measured polydimethylsiloxane content of 74.3%. Various proportions of the above harvested powder were used to modify general purpose PS, as described in Example 1. Impact resistance of the molded and notched test bars derived therefrom is presented in Table 1, wherein the first column indicates the calculated parts by weight of polydimethylsiloxane present in the modified PS system per 100 parts by weight of polystyrene polymer. Parts Polydimethylsiloxane Per 100 Parts of Polystyrene Polymer Percent Polydimethylsiloxane in Modified Polystyrene Polymer Notched Izod Impact Strength (ft-lb/inch)Nm/m 0 (Control) 0 (0.23) 12.28 11 10 (1.21) 64.59 15 13 (1.35) 72.06 18 15 (2.25) 120.10 21 17 (1.96) 104.62 25 20 (2.14) 114.23 33 25 (1.68) 89.68 (Comparative) Example 3 A silicone rubber powder was prepared according to a method suggested by the prior art wherein a low molecular weight hydroxyl-terminated polydimethylsiloxane was emulsified together with crosslinkers and then polymerized, to form a precured silicone emulsion as follows. Six hundred and eighty one parts of a hydroxylendblocked polydimethylsiloxane having a viscosity of about 0.08 Pa·s (80 cP), 34 parts of n-propyl orthosilicate, 6.8 parts of methacryloxypropyltrimethoxysilane, 28 parts of a 30% aqueous solution of sodium lauryl sulfate surfactant and 325 parts of water were stirred together for 30 minutes. This mixture was then emulsified in two passes in a Manton-Gaulin homogenizer at 5.2 x 10⁴ KPa (7,500 psi). The above emulsified product was shaken with 10 parts of 4 normal hydrochloric acid and the resultant emulsion was allowed to polymerize for 48 hours at room temperature to form a precured emulsion. The latter was then neutralized with 14% ammonium hydroxide to provide a 60% solids emulsion having a pH of 7-8. When this emulsion was cast on a substrate and allowed to dry for 48 hours, it yielded a tacky elastomeric film. One hundred parts of the above precured emulsion was diluted with 128 parts of water and 0.05 part of 2,2'-azobis(2-methylbutyronitrile) dissolved in 1 cc of styrene was introduced as the contents were heated to 65°C. under a nitrogen purge. To the above emulsion, 20 parts of styrene was added at a rate of 0.6 cc/minute (total styrene = 20.9 parts). The above temperature was maintained for an additional three hours and the contents were then allowed to stand overnight at room temperature. The above emulsion was then added to an equal volume of isopropyl alcohol, aged 15 minutes and the particles collected on filter paper and dried in air and in a vacuum oven at 133.3-266.6 Pa (1-2 mm Hg). A tacky white solid (77.5 parts) was recovered. The above material was mixed with general purpose PS as previously described to provide a modified system which contained 15% polydimethylsiloxane (i.e., 18 parts polydimethylsiloxane per 100 parts of polystyrene). This material was tested as before and exhibited an Izod impact strength of only 23.00 Nm/m (0.43 ft-lb/inch). A similar procedure to the above resulted in an impact strength of 17.61 Nm/1m (0.33 ft-lb/inch) for the modified PS containing 15% polydimethylsiloxane, a value comparable to that obtained with unmodified polystyrene (i.e., about 12.28 Nm/1m (0.23 ft-lb/inch)).

Claims: A silicone rubber powder prepared by the successive steps comprising (I) forming an aqueous emulsion consisting essentially of a plurality of particles of a hydroxyl-terminated polydiorganosiloxane having a weight average molecular weight greater than 50,000 wherein the average particle size is from 0.1 to 10 microns, (II) precuring the polydiorganosiloxane particles within said emulsion with an organotin curing catalyst and a crosslinker selected from the group consisting of a silane having the formula QSi(X)₃ and partial hydrolysis condensation products thereof, wherein X is a hydrolyzable group selected from the group consisting of alkoxy radicals having 1 to 6 carbon atoms, chloro, hydrido, acetoxy, diorganoamino, oximato and amido groups and in which Q represents a monovalent radical which contains an unsaturated group, (III) thereafter polymerizing an unsaturated monomer in the presence of the emulsion of precured polydiorganosiloxane particles formed in step (II) and (IV) harvesting the particles resulting from step (III). A silicone rubber powder according to claim 1 wherein in step (III) a free-radical initiator is added and said unsaturated monomer is selected such that when it is homopolymerised it results in a polymer having a glass transition temperature of at least 0°C. A composition consisting essentially of a blend of (A) a polystyrene polymer; and (B) a silicone rubber powder as defined in claim 1 or 2 uniformly dispersed in said polystyrene polymer, wherein said composition contains from 5 to 50 parts by weight of said polydiorganosiloxane for each 100 parts by weight of said polystyrene polymer. A method for using a silicone rubber powder as defined in claim 1 or 2 to modify a polystyrene polymer to augment the impact resistance of the polystyrene by blending the silicone rubber powder and the polystyrene polymer so that the composition comprises from 5 to 50 parts by weight of polydiorganosiloxane for each 100 parts by weight of polystyrene polymer.

Inventors: LEE KENNETH MICHAEL, LILES DONALD TAYLOR, ROMENESKO DAVID JOSEPH, WHITE JAMES WILLIAM, LEE, KENNETH MICHAEL, LILES, DONALD TAYLOR, ROMENESKO, DAVID JOSEPH, WHITE, JAMES WILLIAM
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1992
Main classification: C08F299
IPC codes: C08L25, C08F290, C08L55, C08F283, C08L73, C08L83, C08G77, C08L51, C08J3