DENTAL COMPOSITION

Abstract: A composition for preventing the build-up of plaque and other debris along the surface of dentures and dental implants is provided. The composition includes a solvent in an amount between about 46 and 98 weight percent, a volatile compound such as N-methylpyrrolidone in an amount between about 0.5 and 25 weight percent, a polyurethane resin in an amount between about 1 and 35 weight percent and a poly(fluoro) compound such as polytetra-fluoroethylene in an amount between about 0.5 and 20 weight percent.

Description: -1- DENTAL COMPOSITION Background of the Invention This is a continuation-in-part of application Serial No. 669,076, filed March 14, 1991, now aban¬ doned. This invention relates to a dental composition, and more particularly, to a composition which is applied to dentures and other types of artificial teeth as well as to dental implants. The composition is used for preventing the build-up of plaque and other debris. One of the major problems with dentures and other artificial teeth is that they quickly accumulate plaq¬ ue and other debris along the surface of the denture material. This is obviously not desirable since wear¬ er comfort is reduced, distasteful odors are produced and denture wearability is decreased. There are a number of commercial compositions on the marketplace which may be used for cleaning den¬ tures. These compositions include Efferdent, Polident and Dentu-Cre e, and are used on or applied to the dentures when outside the mouth of the wearer. How¬ ever, such compositions are less than satisfactory. These composition are not totally efficient and may not fully clean the dentures because of the excessive build-up of plaque and debris. In some cases, a toothbrush or other manual cleaner may be needed. One of the recurring problems with dental im¬ plants is also the accumulation of plaque, particular¬ ly at t'-e gingival level. To be removed, the dentist must take a Teflon coated instrument and scrape the material away. This results in scratches along the surface of the implant and also promotes furt h er plaque accumulation in the future. SUBSTITUTESHEET -2- In the medical field, there are chemical formu¬ lations that have been used to form a coating along the surface of medical devices such as catheters. This type of coating provides a dry lubricated surface which reduces friction and drag. As a result, per¬ formance of these devices is enhanced. These chemical formulations have in the past comprised a ketone based composition that includes N-methylpyrrolidinone, a polyurethane resin and polytetrafluor-ethylene (Teflon) . In view of the previous success of this composi¬ tion in forming a coating surface on medical equipment which exhibits reduced friction and drag, it would be desirable to determine whether the composition has application in the dental field, specifically as a coating for a denture material or dental implant. airnima y Generally speaking, in accordance with the inven¬ tion, a composition for preventing the build-up of plaque and other debris on artificial teeth and dental implants is provided. The composition includes a solvent in an amount between about 46 and 98 weight percent, a volatile compound such as N-methyl-pyrroli- dinone in an amount between about 0.5 and 25 weight percent, a polyurethane resin in an amount between about 1 and 35 weight percent and a poly(fluoro) com¬ pound such as polytetra-fluorethylene (Teflon) in an amount between about 0.5 and 20 weight percent. The composition of the invention is prepared by mixing the N-methylpyrrolidinone, the polyurethane resin and the polytetra-fluorethylene in the solvent until the chemicals dissolve and a homogeneous materi¬ al is produced. For application to dentures, the composition of the invention is typically sprayed on all external surfaces of the dentures and then allowed to dry. SUBSTITUTE SHEET -3 - For application to a dental implant, the composi¬ tion is applied by dipping the implant in the composi¬ tion (a solution) and then allowing the implant to dry. Alternatively, the composition may be applied to the implant by painting. Accordingly, it is an object of this invention to provide an improved composition for preventing the build-up of plaque and other debris on artificial teeth and dental implants. Another object of the invention is to provide an improved dental composition for preventing the build¬ up of plaque and other debris which may be easily applied by spraying or dipping. A further object of the invention is to provide a dental composition for preventing the build-up of plaque and other debris by forming a coating along the surface of the dental material for reducing friction and drag therealong. Still another object of the invention is to pro¬ vide a dental composition which increases retention of dentures in the mouth of the wearer. Yet a further object of the invention is to pro¬ vide an improved composition which reduces odors in the mouth. Still other objects and advantages of the inven¬ tion will in part be obvious and will in part be ap¬ parent from the following description. The invention accordingly comprises the several steps and the relation of one or more of the steps with respect to each of the others, and the composi¬ tion or compositions having the features, properties, and relation of constituents which are exemplified in the following detailed disclosure, and the scope of the invention will be indicated in the claims. SUBSTITUTE SHEET Detailed Description of the Preferred Embodiment The composition of the invention includes a sol¬ vent in an amount between about 46 and 98 weight per¬ cent. The solvent nay be chosen from water, alcohols and ketones. Suitable alcohols include ethanol, methanol, isopropyl alcohol, 3-pentanol, 2-pentanol, 1-pentanol, 1-hexanol, 2-hexanol, 3-hexanol and isobutyl alcohol. The preferred alcohol is ethanol in an amount between about 50 and 97 weight percent. Suitable ketones include methylethyl ketone, acetone, allylacetone, isopropyl acetone, methylpropyl ketone, 3-pentanone, 3-hexanone and 2-hexanone. The preferred ketone is methylethyl ketone in an amount between about 50-97 weight percent. The preferred amount of water (if chosen as the solvent) _n the inventive denture composition is in an amount between about 50 and 97 weight percent. In order to have a rapid mechanism for drying, the composition of the invention includes a volatile compound in an amount between about 0.5 and 25 weight percent. The volatile compound is chosen from a pyrr- olidone based or an ether based material. The pre¬ ferred compound is a pyrrolidone based material chosen from N-methylpyrrolidinone (NMP) , 2-pyrrolidone, 2- pyrrolidoneacetamide, l-ethyl-2-pyrolidinone and 5- methyl-2-pyrrolidinone. N-methylpyrrolidinone is the preferred pyrrolidone material and may be present in the composition in an amount between about 1 and 20 weight percent. If an ether based material is instead chosen as the volatile compound of the inventive composition, it could be chosen from diethylether, isopropylether and pentylether. SUBSTITUTE SHEET - o ~ As stated above, the purpose of including a vola¬ tile compound such as N-methylpyrrolidinone in the composition is to promote rapid drying of the composi¬ tion when applied to either a denture material or a dental implant. This is achieved by accelerating evaporation at room temperature, thereby leaving a coating on the denture material or dental implant. The inventive composition also includes a polyur¬ ethane resin in an amount between about 1 and 35 weight percent. If the solvent chosen is either water or an alcohol, a water-based aliphatic polyurethane resin is chosen and is preferably present in an amount between about 2 and 25 weight percent. If instead a ketone is used as a solvent, a non-water-based aromat¬ ic polyurethane resin is used and is preferably pres¬ ent in an amount between about 2 and 25 weight per¬ cent. Suitable water-based aliphatic polyurethane res¬ ins include adducts of 1,6-hexane diisocyanate (HDI) and isophorone diisocynate (IPDI), each with any of the following polyols: polyethylene oxide (PEO) , poly¬ propylene oxide (PPO) , polyiosbutylene (PIB) and poly- tetramethylene oxide (PTMO) . Therefore, a water-based polyurethane resin could be HDI/PPO, IPDI/PTMO or any other combination with an alphatic diisocyanate and a polyol group. Suitable non-water based aromatic polyurethane resins include adducts of 2,4 toluene diisocyanate (2,4 TDI) , 2,6 toluene diisocyanate (2,6 TDI) , ethy- lene bis (p-phenylisocyanate) (MDI) , and 1,5-naphatha- lene diisocyanate (NDI) , each with either of the fol¬ lowing polyols: polyethylene oxide (PEO), polypropy¬ lene oxide (PPO) , polyiosbutylene (PIB) and polytetra- methylene oxide (PTMO) . Therefore, a non-water based polyurethane resin could be 2,4 TDI/PPO, 2,4 TDI/PTMO, MDI/PPO, MDI/PEO, NDI/PEO or any other combination SUBSTITUTE SHEET with an aromatic diisocyanate and a polyol group. In addition, the polyurethane resin could also have a chain extender group such as ethylene glycol (EG), hexanediol (HD) , 4,4 methylene bis (2-chloroani- line) (MOCA) and ethylene diamine (ED) . Therefore, the polurethane resin can be HDI/ED/PPO and IPDI/EG/ PTMO (water based polyurethanes) , or 2,4 TDI/ED/PPO, 2,4 TDI/MOCA/PTMO, MDI/EG/PPO: MDI/ED/PEO and NDI/ED/- PEO (non-water based polyurethanes) . The purpose of including a polyurethane resin in the inventive composition is to provide a hard, resis¬ tant coating (a chemical matrix) in order to "lock in" the Teflon on the applied surface of the denture or dental implant. It also increases wearability of the material to which the inventive composition is applied. The inventive dental composition further includes a poly(fluoro) compound such as a fluorinated hydro¬ carbon in an amount between about 0.5 and 20 weight. The preferred fluorinated hydrocarbon is polytetra- fluorethylene (Teflon) in an amount between about 0.5 and 15 weight percent. The purpose of including Teflon in the composition is to prevent the build-up of plaque and other debris and dirt on the surfaces of the denture or dental implant, and also to reduce drag and resistance under normal wear. Instead of using polytetra-fluorethylene in the composition, the composition may include as a fluori¬ nated hydrocarbon polychlorotrifluoroethylene, poly- hexafluoropropylene, polyvinylidine fluoride, polyvi- nylfluoride, copolymer mixtures of tetrafluoroethylene and ethylene, and mixtures of tetrafluoroethylene, propylene and flourinated copolymers of ethylene pro- pylene. In addition to the above identified ingredients, the composition of the invention may also include flavors (artificial or natural) and colorants. In order to prepare the composition of the inven¬ tion, the volatile compound, polyurethane resin and poly(fluoro) compound are dissolved in the solvent until the system is homogenous. Heat may be applied to facilitate dissolution. ~ r application to dentures, the composition shouiα include a solvent in an amount between about 66 and 98 weight percent, a volatile compound such as N- methylpyrrolidinone in an amount between about 0.5 and 15 weight percent, a polyurethane resin in an amount between about 1 and 25 weight percent and a poly- (fluoro) compound such as polytetra-fluorethylene (Teflon) in an amount between about 0.5 and 20 weight percent. Preferably, the solvent is present in an amount between about 75 and 97 weight percent. The preferred volative compound is N-methylpyrrolidinone in an amount between about 1 and 8 weight percent. If the solvent is either water or an alcohol, as stated hereinabove, a water based aliphatic polyure¬ thane resin is chosen and is present in an amount between about 2 and 15 weight percent. If instead a ketone is used as a solvent, a non-water based aromat¬ ic resin is chosen and is present in an amount between about 2 and 20 weight percent. Polytetra-fluoroethylene is the preferred hydro¬ carbon and is present in an amount between about 0.5 and 3 weight percent. In order to better comprehend the composition of the invention as applied to dentures and other artifi¬ cial teeth, the following preferred examples are pro¬ vided. Exainplβ 1 Water 96 weight percent (96 grams) N-methyl-pyrrclidinone 1 weight perce..t (1 gram) Polyurethane 2.4 weight percent (2.4 grams) Polytetra-fluorethylene 0.6 weight percent (0.6 grams) Example 2 Ethanol 96 weight percent (96 grams) N-methylpyrrolidinone 1 weight percent (1 gram) Polyurethane 2.4 weight percent (2.4 grams) Polytetra-fluorethylene 0,6 weight percent (0.6 grams) In order to test the effectiveness of the pre¬ ferred water based (Example l) denture composition, the following experiment was conducted. Ten acrylic disks (diameter 23mm, thickness 4mm) were coated on one side with the denture composition and allowed to dry for two hours (the other side was left the same and uncoated) . The disks were then placed in a 2% solution of Methylene Blue (Basic Blue 9, C.I. 52015) (made up of 2 grams of Methylene Blue with 98 grams of water) in a 400 mL beaker and stirred for two hours. After two hours, the disks were then removed from the methylene blue solution, rinsed with water and air dried. In all cases, the disk sides that were not coated with the denture solution were stained with the methylene blue. Removal of the methylene blue stain SUBSTITUTE SHEET was not possible even by rubbing the disks with a paper towel (the blue stain was permanently fixed on the acrylic disk) . The other sides of the disks with the denture coating of the invention remained un¬ stained, thus demonstrating the effectiveness of the inventive denture composition. In examples 1 and 2, the polyurethane resin is a water based aliphatic polyurethane with an acid group functionality. The following are further examples of the denture composition of the invention: Example 3 Acetone 70% (70 grams) 5-methyl-2-pyrrolidinone 5% (5 grams) Polychlorotrifluorethylene 15% (15 grams) 2,4 TDI/ED/PPO 10% (10 grams) Example 4 Isopropylalcohol 80% (80 grams) l-ethyl-2-pyrrolidinone 12% (12 grams) Polyvinylidine fluoride 5% (5 grams) MDI/EG/PPO 3% (3 grams) Example 5 Isopropylacetone 85% (85 grams) 2-Pyrrolidone 3% (3 grams) Polyvinylfluoride 9% (9 grams) MDI/ED/PEO 3% (3 grams) In order to use the composition of the invention on dentures, the dentures are first removed and then SUBSTITUTE SHEET cleaned and dried. Thereafter, the composition is preferably sprayed on all external surfaces of the denture by means of a pump or aerosol delivery device. Spraying should ta.<e place evenly for between approx¬ imately 2 and 7 seconds. After spraying, the dentures are air dried for at least one hour, and preferably for about two hours. From a practical standpoint, the spraying of the den¬ tures with the dental composition should take place prior to the denture wearer going to bed so that the dentures are sufficiently dry after the spraying pro¬ cess is completed. If that is not convenient, then the sprayed dentures may bs rapidly dried by using a hair dryer or other similar drying or air source. For most denture wearers, application of the composition to one's dentures is required only once a week. If the composition of the invention is properly applied, the accumulation of plaque and other debris along the dentures' surfaces is substantially prevent¬ ed. As a result, routine cleaning of the treated dentures is quicker and more efficient. Moreover, it has been found that the composition of the invention helps maintain retention of the den¬ tures in the wearer's mouth. Furthermore, use of the denture composition reduces mouth odors of the denture wearer. Although the composition of the invention has been described as being suitable for spraying onto a denture material, the composition may be applied to dentures or other artificial teeth in other ways, such as dipping or painting. For application to a dental implant, the composi¬ tion is more concentrated than the composition pre¬ ferred for application to dentures, and preferably includes a solvent in an amount between about 46 and 76 weight percent, a volatile compound such an N- SUEβTITUTS SHEET methylpyrrolidinone in an amount between about 5 and 25 weight percent, a polyurethane resin in an amount between about 10 and 35 weight percent and a poly(fluoro) compound such as polytetra-fluorethylene (Teflon) in an amount between about 5 and 20 weight percent. Preferably, the solvent is present in an amount between about 50 and 66 weight percent. The preferred volative compound is N-methylpyrrolidinone in an amount between about 9 and 20 weight percent. If the solvent is either water or an alcohol, as stated hereinabove, a water based aliphatic polyure¬ thane resin is chosen and is present in an amount between about 5 and 25 weight percent. If instead a ketone is used as a solvent, a non-water based aromat¬ ic resin is chosen and is present in an amount between about 5 and 25 weight percent. Polytetra-fluoroethylene is the preferred hydro¬ carbon and is present in an amount between about 5 and 15 weight percent. In order to better understand the composition of the invention as applied to a dental implant, the following preferred examples are provided: Example 1 Water 66 weight percent (66 grams) N-Methylpyrrolidinone 9 weight percent (9 grams) Polyurethane 20 weight percent (20 grams) Polytetra-fluorethylene 5 weight percent (5 grams) suεετιτuτE SHEET Exanple 2 Water 64 weight percent (64 grams) Ethanol 2 weight percent (2 grams) N-Methylpyrrolidinone 9 weight percent (9 grams) Polytetra-fluorethylene 5 weight percent (5 grams) Polyurethane 20 weight percent (20 grams) Example 3 Acetone 70 weight percent (70 grams) 5-methyl-2-pyrrolidinone 5 weight percent (5 grams) Polychlorotrifluorethylene 15 weight percent (15 grams) 2,4 TDI/ED/PPO 10 weight percent (10 grams) Example 4 Isopropylalcohol 60 weight percent (60 grams) l-ethyl-2-pyrrolidinone 12 weight percent (12 grams) Polyvinylidine fluoride 15 weight percent (15 grams) MDI/EG/PPO 13 weight percent (13 grams) SUBSTITUTE SHEET Example 5 Isopropylacetone 55 weight percent (55 grams) 2-Pyrrolidone 13 weight percent (13 grams) Polyvinylfluoride 9 weight percent (9 grams) MDI/ED/PEO 23 weight percent (23 grams) Example 6 1-pentanol 68 weight percent (68 grams) Diethylether 12 weight percent (12 grams) Polyvinylidine fluoride 10 weight percent (10 grams) NDI/ED/PEO 5 weight percent (5 grams) In order to use the composition of the invention on a dental implant, the implant neck is removed (by the dentist) and then cleaned and dried. Thereafter, the neck of the implant is soaked in the inventive composition for about 10-30 seconds. After dipping, the implant neck is air dried for at least two hours. Alternatively, the inventive composition may be applied to the implant neck by painting. For most implants, application of the more con¬ centrated form of the inventive composition should be about once every three months. If the composition is properly applied, the accumulation of plaque and other debris along the neck of the implant is substantially prevented. Moreover, there would no linger be the need to scrape and thereby possibly damage the implant surface. ετιτuτE SHEET It will thus be seen that the objects set forth above, and those made apparent from the preceding description, are efficiently attained, and since cer¬ tain changes may be made in carrying out the above method and in the composition set forth above without departing from the spirit and scope of the invention, it is intended that all matter contained in the above description shall be interpreted as illustrative and not in a limiting sense. It is also to be understood that the following claims are intended to cover all of the generic and specific features of the invention herein described and all statements of the scope of the invention which, as a matter of language, might be said to fall therebetween. SUBSTITUTE SHEET

Claims: Claims What is claimed is: 1. A composition for preventing accumulation of plaque and other debris on other artificial teeth and dental implants comprising: a solvent in an amount between about 46 and 98 weight percent; a volatile compound in an amount between about 0.5 and 25 weight percent; a polyurethane resin in an amount between about 1 and 35 weight percent; and a oly(fluoro) compound in an amount between about 0.5 and 20 weight percent. 2. The composition of claim 1, wherein the sol¬ vent is selected from the group consisting of water, an alcohol and a ketone. 3. The composition of claim 2, wherein the alco¬ hol is selected from the group consisting of ethanol, methanol, isopropyl alcohol, 3-pentanol, 2-pentanol, 1-pentanol, 1-hexanol, 2-hexanol, 3-hexanol and isobu- tyl alcohol. 4. The composition of claim 3, wherein the alco¬ hol comprises ethanol in an amount between about 50 and 97 weight percent. 5. The composition of claim 2, wherein the ke¬ tone is selected from the group consisting of methyl¬ ethyl ketone, acetone, allylacetone, isopropyl ace¬ tone, methylpropyl ketone, 3-pentanone, 3-hexanone and 2-hexanone. 6. The composition of claim 5, wherein the ke¬ tone comprises methylethyl ketone in an amount between about 50 and 97 weight percent. 7. The composition of claim 1, wherein the vola¬ tile compound is selected from the group consisting of a pyrrolidone based material and an ether based material. SUBSTITUTESHEET -16 - 8. The composition of claim 7, wherein the pyrrolidone based material is selected from the group consisting of N-methylpyrrolidinone, 2-pyrrolidone, 2- pyrrolidoneacetamide, l-e--.yl-2-pyrrclidinone and 5- methyl-2-pyrrolidinone. 9. The composition of claim ' 8, wherein the pyrrolidone based material is N-methylpyrrolidinone in an amount between about 1 and 20 weight percent. 10. The composition of claim 7, wherein the ether based material is selected from the group consisting of diethylether, isopropylether and pentylether. 11. The composi t ion of claim 1, wherein the poly¬ urethane resin is selected from the group consisting of water based aliphatic polyurethane resins and non- water based aromatic polyurethane resins. 12. The composition of claim 11, wherein the solvent is selected from the group consisting of water and alcohol and wherein the resin is water based. 13. The composition of claim 11, wherein the solvent is a ketone and wherein the resin is not water based. 14. The composition of claim l, wherein the poly(fluoro) compound is a fluorinated hydrocarbon selected from the group consisting of polytetra-fluor¬ ethylene, polychlorotrifluoroethylene, polyhexafluor- opropylene, polyvinylidine fluoride, polyvinylfluor- ide, copolymer mixtures of tetra-fluoroethylene and ethylene, and mixtures of tetra-fluoroethylene, pro- pylene and fluorinated copolymers of ethylene propyl- ene. 15. The composition of claim 14, wherein the fluorinated hydrocarbon is polytetra-fluorethylene in an amount between about 0.5 and 15 weight percent. 16. The composition of claim 1, wherein the vola¬ tile compound is N-methylpyrrolidinone and the poly(fluoro) compound is. polytetra-fluorethylene. 17. A method for preventing the build up of plaque and other debris on artificial teeth or a den¬ tal implant comprising applying a composition to the artificial teeth or dental implant containing a sol¬ vent in an amount between about 46 and 98 weight per¬ cent, a volatile compound in an amount between about 0.5 and 25 weight percent, a polyurethane resin in an amount between about 1 and 35 weight percent and a poly(fluoro) compound in an amount between about 0.5 and 20 weight percent, the weight percents based on the weight of the composition. 18. The method of claim 18, wherein said applying step for artificial teeth comprises spraying the arti¬ ficial teeth with said composition. 19. The method of claim 17, wherein said applying step for said dental impla - comprises soaking the implant in said composition. 20. The method of claim 19, wherein said applying step for said dental implant comprises painting the implant with said composition. 21. The method of claim 17, further including the step of cleaning the artificial teeth or dental im¬ plant prior to said applying step. 22. The method of claim 21, further including the step of drying the artificial teeth or dental implant prior to said spraying step. 23. The method of claim 17, further including the step of drying the artificial teeth or dental implant after said applying step. 24. The method of claim 23, wherein said drying step comprises air drying the artificial teeth or dental implant for between one and two hours. 25. The method of claim 23, wherein said drying step comprises drying the artificial teeth or dental implant using a heat or air source. SUBSTITUTE SHEET 26. The method of claiπ 18, wherein said applying step occurs about once a week. 27. The method of claim 19, wherein said soaking step occurs about once every three months. 28. A composition for preventing the accumulation of plaque and other debris on dentures and other arti¬ ficial teeth comprising: a solvent in an amount between about 66 and 98 weight percent; a volatile compound in an amount between about 0.5 and 15 weight percent; a polyurethane resin in an amount between about 1 and 25 weight percent; and a poly(fluoro) compound in an amount between about 0.5 and 20 weight percent. 29. The composition of claim 28, wherein the solution is selected from the group consisting of water, an alcohol and a ketone. 30. The composition of claim 29, wherein the alcohol comprises ethanol in an amount between about 75 and 97 weight percent. 31. The composition of claim 29, wherein the ketone comprises methylethyl ketone in an amount be¬ tween about 75 and 97 weight percent. 32. The composition of claim 28, wherein the volatile compound is selected from the group consist¬ ing of a pyrrolidone based material and an ether based material. 33. The composition of claim 32, wherein the pyrrolidone based material is N-methylpyrrolidinone in an amount between about 1 and 8 weight percent. 34. The composition of claim 28, wherein the fluorinated hydrocarbon is polytetra-fluorethylene in an amount between about 0.5 and 3 weight percent. ^U ?TITUTE SHEET 35. The composition of claim 28, wherein the volatile compound is N-methylpyrrolidinone and the poly(fluoro) compound is polytetra-fluorethylene. 36. The composition of claim 35, wherein the solvent is present in an amount of about 96 weight percent, N-r^thylpyrrolidinone is present in an amount of about 1 weight percent, the polyurethane resin is present in an amount of about 2.4 weight percent and polytetra-fluorethylene is present in an amount of about 0.6 weight percent. 37. A composition for preventing the accumulation of plaque and other debris on a dental implant com¬ prising: a solvent in an amount between about 46 and 76 weight percent; a volatile compound in an amount between about 5 and 25 weight percent; a polyurethane resin in an amount between about 10 and 35 weight percent; and a poly(fluoro) compound in an amount between about 0.5 and 20 weight percent. 38. The composition of claim 37, wherein the sol¬ vent is selected from the group consisting of water, an alcohol and a ketone. 39. The composition of claim 38, wherein the alcohol comprises ethanol in an amount between about 50 and 66 weight percent. 40. The composition of claim 38, wherein the ketone comprises methylethyl ketone in an amount be¬ tween about 50 and 66 weight percent. 41., The composition of claim 37, wherein the volatile compound is selected from the group consist¬ ing of a pyrrolidone based material and an ether based material. SUCΓTITUTEI SHEET 42. The composition of claim 41, wherein the pyrrolidone based material is N-methylpyrrolidinone in an amount between about 9 and 20 weight percent. 43. The composition of claim 37, wherein the fluorinated hydrocarbon is polytetra-fluorethylene in an amount between about 5 and 15 weight percent. 44. The composition of claim 37, wherein the volatile compound is N-methylpyrrolidinone and the poly(fluoro) compound is polytetra-fluorethylene. 45. The composition of claim 16, wherein the solvent is present in an amount of about 66 weight percent, N-methylpyrrolidinone is present in an amount of about 9 weight percent, the polyurethane resin is present in an amount of about 20 weight percent and polytetra-fluorethylene is present in an amount of about 5 weight percent. ΓUTE SHEET

Inventors: COHEN BRETT I, MUSIKANT BARRY L, COHEN, BRETT, I., MUSIKANT, BARRY, L.
Applicants: ESSENTIAL DENTAL SYSTEMS INC, ESSENTIAL DENTAL SYSTEMS, INC.
Application year: 1992
Main classification: A61K31
IPC codes: A61K6, A61K8, A61Q11