Catalyst for polymerizing an olefin and method for producing an olefin polymer

Abstract: A catalyst for polymerizing an olefin which consists essentially of a product obtained by contacting (A) a metallocene-type transition metal compound, (B) at least one member selected from silicates other than ion exchanging layered compounds, and (C) an organic aluminum compound of the formula AlR⁶ j X 3-j , wherein R⁶ is a C₁₋₂₀ hydrocarbon group, X is hydrogen, halogen or an alkoxy group, and j is a number satisfying 0 < j ≦ 3.

Description: The present invention relates to a catalyst for polymerizing an olefin and a method for producing an olefin polymer in good yield by means of the catalyst. For the production of an olefin polymer by polymerizing an olefin in the presence of a catalyst, a method has been proposed wherein a catalyst comprising (1) metallocene and (2) aluminoxane is employed (Japanese Unexamined Patent Publications No. 019309/1983 and No. 167307/1990). According to the polymerization method using such a catalyst, the polymerization activities per transition metal are very high as compared with a method of using a conventional Ziegler-Natta catalyst comprising a titanium compound or a vanadium compound and an organic aluminum compound, and it is thereby possible to obtain a polymer having a narrow molecular weight distribution. However, in order to obtain adequate polymerization activities by means of such a catalyst, a large amount of aluminoxane is required, and the polymerization activities per aluminum are low, such being uneconomical. Besides, it is necessary to remove the catalyst residue from the formed polymer. On the other hand, a method has been proposed wherein polymerization of an olefin is conducted by means of a catalyst having one or both of the above transition metal compound and the aluminoxane carried on an inorganic oxide such as silica or alumina (Japanese Unexamined Patent Publications No. 108610/1986, No. 135408/1985, No. 296008/1986, No. 74412/1991 and No. 74415/1991). Further, a method has been proposed wherein polymerization of an olefin is conducted by means of a catalyst having one or both of the above transition metal compound and an organic aluminum compound carried on an inorganic oxide such as silica or alumina or on an organic material (Japanese Unexamined Patent Publications No. 101303/1989, No. 207303/1989, No. 234709/1991 and No. 234710/1991 and Japanese PCT Publication No. 501869/1991). However, by these methods, the polymerization activities per aluminum are still inadequate, and the amount of the catalyst residue in the product is not negligible. The present inventors have conducted extensive studies to solve the above problems, and as a result, have found that a product obtained by contacting a metallocene-type transition metal compound and an organic aluminum compound on a certain specific carrier, exhibits adequately high polymerization activities per transition metal and per aluminum. The present invention has been accomplished on the basis of this discovery. Thus, the present invention provides a catalyst for polymerizing an olefin which consists essentially of a product obtained by contacting (A) a metallocene-type transition metal compound, (B) at least one member selected from silicates other than ion exchanging layered compounds, and (C) an organic aluminum compound of the formula AIR 6 j X 3-j , wherein R 6 is a C 1-20 hydrocarbon group, X is hydrogen, halogen or an alkoxy group, and j is a number satisfying 0 < j ≤ 3. Further, the present invention provides a method for producing an olefin polymer, which comprises homopolymerizing or copolymerizing an olefin in the presence of a catalyst consisting essentially of a product obtained by contacting (A) a metallocene-type transition metal compound, (B) at least one member selected from silicates other than ion exchanging layered compounds, and (C) an organic aluminum compound of the formula AlR 6 j X 3-j , wherein R 6 is a C 1-20 hydrocarbon group, X is hydrogen, halogen or an alkoxy group, and j is a number satisfying 0 < j ≤ 3 and, if necessary, (D) a further organic aluminum compound which is different from (C) of the formula AlR 7 k Y 3-k wherein R 7 is a C 1-20 hydrocarbon group, Y is hydrogen, halogen or an alkoxy group, and k is a number satisfying 0 < k ≤ 3 . Now, the present invention will be described in detail with reference to the preferred embodiments. The metallocene-type transition metal compound of component (A) to be used in the catalyst of the present invention, is an organometallic compound composed of a cyclopentadienyl-type ligand which may be substituted, i.e. a cyclopentadienyl ring-containing ligand wherein substituents may bond to form a ring, and a transition metal of Group 4, 5 or 6 of the long-form Periodic Table. Preferred as such a metallocene-type transition metal compound is a compound of the following formula (1) or (2): R 1 m (CpR 2 n )(CpR 2 n )MR 3 2 [R 1 m (CpR 2 n )(CpR 2 n )MR 3 R 4 ] + R 5- wherein each of (CpR 2 n ) which may be the same or different, is a cyclopentadienyl group or a substituted cyclopentadienyl group, R 1 is a covalent bond crosslinking group containing an element of Group 14 of the long-form Periodic Table such as carbon, silicon or germanium, each of R 2 which may be the same or different, is hydrogen, halogen, a silicon-containing group, a C 1-20 hydrocarbon group which may have a halogen substituent, an alkoxy group or an aryloxy group, provided that when two R 2 are located on two adjacent carbon atoms on the cyclopentadienyl group, they may bond to each other to form a C 4-6 ring, each of R 3 which may be the same or different, is hydrogen, halogen, a silicon-containing group, a C 1-20 hydrocarbon group which may have a halogen substituent, an alkoxy group or an aryloxy group, m is 0 or 1, each n is an integer satisfying m + n = 5, M is a metal of Group 4, 5 or 6 of the long-form Periodic Table, R 4 is a neutral ligand coordinated to M, and R 5- is a counter anion capable of stabilizing said metal cation. In the formula (1) or (2), R 1 is a covalent bond crosslinking group containing an element of Group 14 of the long-form Periodic Table such as carbon, silicon or germanium, and it links two cyclopentadienyl ring-containing groups of the formula CpR 2 n . Specifically, it may be an alkylene group such as a methylene group or an ethylene group, an alkylidene group such as an ethylidene group, a propylidene group, an isopropylidene group, a phenyl methylidene group or a diphenylmethylidene group, a silicon-containing crosslinking group such as a dimethylsilylene group, diethylsilylene group, a dipropylsilylene group, a diisopropylsilylene group, a diphenylsilylene group, a methylethylsilylene group, a methylphenylsilylene group, a methylisopropylsilylene group or a methyl-t-butylsilylene group, a germanium-containing crosslinking group such as a dimethyl germilene group, a diethylgermilene group, a dipropylgermilene group, a diisopropylgermilene group, a diphenylgermilene group, a methylethylgermilene group, a methylphenylgermilene group, a methylisopropylgermilene group or a methyl-t-butylgermilene group, an alkylphosphine, or an amine. Among them, an alkylene group, an alkylidene group and a silicon-containing crosslinking group are particularly preferred. Each of CpR 2 n which may be the same or different, is a cyclopentadietnyl group or a substituted cyclopentadietnyl group. Here, each of R 2 which may be the same or different, is hydrogen, halogen such as fluorine, chlorine, bromine or iodine, a silicon-containing group such as trimethylsilyl, triethylsilyl or triphenylsilyl, a C 1-20 hydrocarbon group which may have a halogen group, such as methyl, ethyl, propyl, butyl, isobutyl, pentyl, isopentyl, hexyl, heptyl, octyl, nonyl, decyl, phenyl, chloromethyl or chloroethyl, an alkoxy group such as methoxy, ethoxy, propoxy or butoxy, or an aryloxy group such as phenoxy, methylphenoxy or pentamethylphenoxy. Here, when two R 2 are located on two adjacent carbon atoms on the cyclopentadienyl ring, they may bond to each other to form a C 4-6 ring, such as indenyl, tetrahydroindenyl, fluorenyl or octahydrofluorenyl. Among them, particularly preferred as R 2 are hydrogen, a methyl group and a hydrocarbon group wherein two R 2 bond to each other to form indenyl, tetrahydroindenyl, fluorenyl or octahydrofluorenyl. Each of R 3 which may be the same or different, is hydrogen, halogen such as fluorine, chlorine, bromine or iodine, a silicon-containing group such as trimethylsilyl, triethylsilyl or triphenylsilyl, a C 1-20 hydrocarbon group which may have a halogen substituent, such as methyl, ethyl, propyl, butyl, isobutyl, pentyl, isopentyl, hexyl, heptyl, octyl, nonyl, decyl, phenyl, chloromethyl or chloroethyl, an alkoxy group such as methoxy, ethoxy, propoxy or butoxy, or an aryloxy group such as phenoxy, methylphenoxy or pentamethylphenoxy. Particularly preferred are hydrogen, chlorine and a methyl group. m is 0 when two cyclopentadienyl rings are not bonded by R 1 and 1 when bonded. Each n is 4 when m is 1 and 5 when m is 0. M is a metal of Group 4, 5 or 6 of the long-form Periodic Table, such as titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum or tungsten. Particularly preferred is titanium, zirconium or hafnium. R 4 is a neutral ligand coordinated to M, such as tetrahydrofuran. R 5- is a counter anion which is capable of stabilizing the metal cation in the above formula (2), such as tetraphenyl borate, tetra(p-tolyl) borate, carbadodeca borate or dicarbaundeca borate. The catalyst of the present invention is capable of producing any one of an isotactic polymer, a syndiotactic polymer and an atactic polymer. Taking zirconium as an example, specific examples of the above metallocene-type transition metal compound corresponding to the formula (1) include bis(methylcyclopentadienyl)zirconium dichloride, bis(ethylcyclopentadienyl)zirconium dichloride, bis(methylcyclopentadienyl)zirconium dimethyl, bis(ethylcyclopentadienyl)zirconium dimethyl, bis(methylcyclopentadienyl)zirconium dihydride, bis(ethylcyclopentadienyl)zirconium dihydride, bis(dimethylcyclopentadienyl)zirconium dichloride, bis(trimethylcyclopentadienyl)zirconium dichloride, bis(tetramethylcyclopentadienyl)zirconium dichloride, bis(ethyltetramethylcyclopentadienyl)zirconium dichloride, bis(indenyl)zirconium dichloride, bis(dimethylcyclopentadienyl)zirconium dimethyl, bis(trimethylcyclopentadienyl)zirconium dimethyl, bis(tetramethylcyclopentadienyl)zirconium dimethyl, bis(ethyltetramethylcyclopentadienyl)zirconium dimethyl, bis(indenyl)zirconium dimethyl, bis(dimethylcyclopentadienyl)zirconium dihydride, bis(trimethylcyclopentadienyl)zirconium dihydride, bis(ethyltetramethylcyclopentadienyl)zirconium dihydride, bis(trimethylsilylcyclopentadienyl)zirconium dimethyl, bis(trimethylsilylcyclopentadienyl)zirconium dihydride, bis(trifluoromethylcyclopentadienyl)zirconium dichloride, bis(trifluoromethylcyclopentadienyl)zirconium dimethyl, bis(trifluoromethylcyclopentadienyl)zirconium dihydride, isopropylidene-bis(indenyl)zirconium dichloride, isopropylidene-bis(indenyl)zirconium dimethyl, isopropylidene-bis(indenyl)zirconium dihydride, pentamethylcyclopentadienyl(cyclopentadienyl)zirconium dichloride, pentamethylcyclopentadienyl(cyclopentadienyl)zirconium dimethyl, pentamethylcyclopentadienyl(cyclopentadienyl)zirconium dihydride, ethyltetramethylcyclopentadienyl(cyclopentadienyl)-zirconiumdihydride, isopropylidene(cyclopentadienyl)(fluorenyl)zirconium dichloride, isopropylidene(cyclopentadienyl)(fluorenyl)zirconium dimethyl, dimethylsilyl(cyclopentadienyl)(fluorenyl)zirconium dimethyl, isoproplylidene(cyclopentadienyl)(fluorenyl)zirconium dihydride, bis(cyclopentadienyl)zirconium dichloride, bis(cyclopentadienyl)zirconium dimethyl, bis(cyclopentadienyl)zirconium diethyl, bis(cyclopentadienyl)zirconium dipropyl, bis(cyclopentadienyl)zirconium diphenyl, methylcyclopentadienyl(cyclopentadienyl)zirconium dichloride, ethylcyclopentadienyl(cyclopentadienyl)zirconium dichloride, methylcyclopentadienyl(cyclopentadienyl)zirconium dimethyl, ethylcyclopentadienyl(cyclopentadienyl)zirconium dimethyl, methylcyclopentadienyl(cyclopentadienyl)zirconium dihydride, ethylcyclopentadienyl(cyclopentadienyl)zirconium dihydride, dimethylcyclopentadienyl(cyclopentadienyl)zirconium dichloride, trimethylcyclopentadienyl(cyclopentadienyl)zirconium dichloride, tetramethylcyclopentadienyl(cyclopentadienyl)zirconium dichloride, bis(pentamethylcyclopentadienyl)zirconium dichloride, tetramethylcyclopentadienyl(cyclopentadienyl)zirconium dichloride, indenyl(cyclopentadienyl)zirconium dichloride, dimethylcyclopentadienyl(cyclopentadienyl)zirconium dimethyl, trimethylcyclopentadienyl(cyclopentadienyl)zirconium dimethyl, tetramethylcyclopentadienyl(cyclopentadienyl)zirconium dimethyl, bis(pentamethylcyclopentadienyl)zirconium dimethyl, ethyltetramethylcyclopentadienyl(cyclopentadienyl)-zirconium dimethyl, indenyl(cyclopentadienyl)zirconium dimethyl, dimethylcyclopentadienyl(cyclopentadienyl)zirconium dihydride, trimethylcyclopentadienyl(cyclopentadienyl)zirconium dihydride, bis (pentamethylcyclopentadienyl)zirconium dihydride, indenyl(cyclopentadienyl)zirconium dihydride, trimethylsilylcyclopentadienyl(cyclopentadienyl)zirconium dimethyl, trimethylsilylcyclopentadienyl(cyclopentadienyl)zirconium dihydride, trifluoromethylcyclopentadienyl(cyclopentadienyl)-zirconium dichloride, trifluoromethylcyclopentadienyl(cyclopentadienyl)-zirconium dimethyl, trifluoromethylcyclopentadienyl(cyclopentadienyl)-zirconium dihydride, bis(cyclopentadienyl)(trimethylsilyl)(methyl)zirconium, bis(cyclopentadienyl)(triphenylsilyl)(methyl)zirconium, bis(cyclopentadienyl)[tris(dimethylsilyl)silyl](methyl)-zirconium, bis(cyclopentadienyl)[bis(methylsilyl)silyl](methyl)-zirconium, bis(cyclopentadienyl)(trimethylsilyl)(trimethylsilyl-methyl)zirconium, bis(cyclopentadienyl)(trimethylsilyl)(benzyl)zirconium, methylene-bis(cyclopentadienyl)zirconium dichloride, ethylene-bis(cyclopentadienyl)zirconium dichloride, isopropylidene-bis(cyclopentadienyl)zirconium dichloride, dimethylsilyl-bis(cyclopentadienyl)zirconium dichloride, methylene-bis(cyclopentadienyl)zirconium dimethyl, ethylene-bis(cyclopentadienyl)zirconium dimethyl, isopropylidene-bis(cyclopentadienyl)zirconium dimethyl, dimethylsilyl-bis(cyclopentadienyl)zirconium dimethyl, methylene-bis(cyclopentadienyl)zirconium dihydride, ethylene-bis(cyclopentadienyl)zirconium dihydride, isopropylidene-bis(cyclopentadienyl)zirconium dihydride and dimethylsilyl-bis(cyclopentadienyl)zirconium dihydride. Further, those corresponding to the formula (2) include a bis(methylcyclopentadienyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, a bis(ethylcyclopentadienyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, a bis(methylcyclopentadienyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, a bis(ethylcyclopentadienyl)zirconium(methyl)tetraphenylborate)tetrahydrofuran complex, a bis(methylcyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, a bis(ethylcyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, a bis(dimethylcyclopentadienyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, a bis(trimethylcyclopentadienyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, a bis(tetramethylcyclopentadienyl)zirconium(chloride)-(tetraphenylborate)tetrahydrofuran complex, a bis(ethyltetramethylcyclopentadienyl)zirconium(chloride)-(tetraphenylborate)tetrahydrofuran complex, a bis(indenyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, a bis(dimethylcyclopentadienyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, a bis(trimethylcyclopentadienyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, a bis(tetramethylcyclopentadienyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, a bis(ethyltetramethylcyclopentadienyl)zirconium(methyl)-tetraphenylborate)tetrahydrofuran complex, a bis(indenyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, a bis(dimethylcyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, a bis(trimethylcyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, a bis(ethyltetramethylcyclopentadienyl)zirconium(hydride)-(tetraphenylborate)tetrahydrofuran complex, a bis(trimethylsilylcyclopentadienyl)zirconium(methyl)-(tetraphenylborate)tetrahydrofuran complex, a bis(trimethylsilylcyclopentadienyl)zirconium(hydride)-(tetraphenylborate)tetrahydrofuran complex, a bis(trifluoromethylcyclopentadienyl)zirconium(methyl)-(tetraphenylborate)tetrahydrofuran complex, a bis(trifluoromethylcyclopentadienyl)zirconium(hydride)-(tetraphenylborate)tetrahydrofuran complex, an isopropylidene-bis(indenyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, an isopropylidene-bis(indenyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, an isopropylidene-bis(indenyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, a pentamethylcyclopentadienyl(cyclopentadienyl)zirconium (chloride)(tetraphenylborate)tetrahydrofuran complex, an ethyltetramethylcyclopentadienyl(cyclopentadienyl)-zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, a pentamethylcyclopentadienyl(cyclopentadienyl)zirocnium-(methyl)(tetraphenylborate)tetrahydrofuran complex, an ethyltetramethylcyclopentadienyl(cyclopentadienyl)-zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, a pentamethylcyclopentadienyl(cyclopentadienyl)zirconium-(hydride)(tetraphenylborate)tetrahydrofuran complex, an ethyltetramethylcyclopentadienyl(cyclopentadienyl)-zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, an isopropylidene(cyclopentadienyl)(fluorenyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, an isopropylidene(cyclopentadienyl)(fluorenyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, an isopropylidene(cyclopentadienyl)(fluorenyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, a bis(cyclopentadienyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, a bis(cyclopentadienyl)(methyl)zirconium(tetraphenylborate)tetrahydrofuran complex, a bis(cyclopentadienyl)(ethyl)zirconium(tetraphenylborate)-tetrahydrofuran complex, a bis(cyclopentadienyl)(propyl)zirconium(tetraphenylborate)tetrahydrofuran complex, a bis(cyclopentadienyl)-(phenyl)zirconium(tetraphenylborate)tetrahydrofuran complex, a methylcyclopentadienyl(cyclopentadienyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, an ethylcyclopentadienyl(cyclopentadienyl)zirconiumchloride(tetraphenylborate)tetrahydrofuran complex, a bis(ethylcyclopentadienyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, a methylcyclopentadienyl(cyclopentadienyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, an ethylcyclopentadienyl(cyclopentadieny)zirconium(methyl)-(tetraphenylborate)tetrahydrofuran complex, a methylcyclopentadienyl(cyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, an ethylcyclopentadienyl(cyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, a dimethylcyclopentadienyl(cyclopentadienyl)zirconium-(chloride)(tetraphenylborate)tetrahydrofuran complex, a trimethylcyclopentadienyl(cyclopentadienyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, a tetramethylcyclopentadienyl(cyclopentadienyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, a bis(pentamethylcyclopentadienyl)zirconium(chloride)-(tetraphenylborate)tetrahydrofuran complex, an indenyl(cyclopentadienyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, a dimethylcyclopentadienyl(cyclopentadienyl)zirconium-(methyl)(tetraphenylborate)tetrahydrofuran complex, a trimethylcyclopentadienyl(cyclopentadienyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, a tetramethylcyclopentadienyl(cyclopentadienyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, a bis(pentamethylcyclopentadienyl)zirconium(methyl)tetraphneylborate)tetrahydrofuran complex, a cyclopentadienyl(indenyl)zirconium(methyl)(tetraphenylborate)tatrahydrofuran complex, a dimethylcyclopentadienyl(cyclopentadienyl)zirconium-(hydride)(tetraphenylborate)tetrahydrofuran complex, a trimethylcyclopentadienyl(cyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, a bis(pentamethylcyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, an indenyl(cyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, a trimethylsilylcyclopentadienyl(cyclopentadienyl)-zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, a trimethylsilylcyclopentadienyl(cyclopentadienyl)-zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, a trifluoromethylcyclopentadienyl(cyclopentadienyl)-zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, a bis(cyclopentadienyl)(trimethylsilyl)zirconium(tetraphenylborate)tetrahydrofuran complex, a bis(cyclopentadienyl)(triphenylsilyl)zirconium(tetraphenylborate)tetrahydrofuran complex, a bis(cyclopentadienyl)[tris(diemthylsilyl)silyl]zirconium-(tetraphenylborate)tetrahydrofuran complex, bis(cyclopentadienyl)(trimethylsilylmethyl)zirconium-(tetraphenylborate)tetrahydrofuran complex, a bis(cyclopentadienyl)(benzyl)zirconium(tetraphenylborate)tetrahydrofuran complex, a methylene-bis(cyclopentadienyl)zirconium(chloride)tetraphenylborate)tetrahydrofuran complex, an ethylene-bis(cyclopentadienyl)zirconium(chloride)tetraphenylborate)tetrahydrofuran complex, an isopropylidene-bis(cyclopentadienyl)zirconium(chloride)tetraphenylborate)tetrahydrofuran complex, a dimethylsilyl-bis(cyclopentadienyl)zirconium(chloride)(tetraphenylborate)tetrahydrofuran complex, a methylene-bis(cyclopentadienyl)zirconium(methyl)(tetraphneylborate)tetrahydrofuan complex, an ethylene-bis(cyclopentadienyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, an isopropylidene-bis(cyclopentadienyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, a dimethylsilyl-bis(cyclopentadienyl)zirconium(methyl)(tetraphenylborate)tetrahydrofuran complex, a methylene-bis(cyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, an ethylene-bis(cyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex, an isopropylidene-bis(cyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex and a dimethylsilyl-bis(cyclopentadienyl)zirconium(hydride)(tetraphenylborate)tetrahydrofuran complex. Further, with respect to compounds of other metals of Group 4, 5 and 6, such as titanium compounds and hafnium compounds, those similar to the above compounds may be mentioned. Further, a mixture of such compounds may also be employed. In the present invention, as component (B), clay, clay minerals, ion exchanging layered compounds, diatomaceous earth, silicates or zeolites are employed. Clay is usually composed of clay minerals as the main constituents. The ion exchanging layered compounds are compounds having a crystal structure in which faces constituted by e.g. ionic bonds are piled in parallel to one another by a weak bonding force and the contained ions are exchangeable. The majority of clay minerals are ion exchanging layered compounds. These clay, clay minerals and ion exchanging layered compounds may not only be natural products but also be artificially synthesized products. The silicates other than ion exchanging layered compounds to be used as component (B) in the present invention may be synthesized products or naturally produced minerals. Further, they may be used as they are without subjecting them to any treatment, or they may be treated by ball milling, sieving, acid treatment or the like before use. Further, they may be treated to have water added and adsorbed or may be treated for dehydration under heating before use. They may be used alone or in combination as a mixture of two or more of them. Specific examples of the silicates include silicates such as lithium silicate, sodium silicate, potassium silicate, magnesium silicate, calcium silicate, barium silicate, aluminium silicate, titanium silicate and zirconium silicate, an olivaine group such as olivaine and fayalite, a garnet group such as garnet, a phenacite group such as phenacite and willemite, zircon, tricalcium silicate, merrillite, gehlenite, benitoite, beryl, cordierite, a pyroxene group such as enstatite, hypersthene, diopside, spondumene, rhodonite and wollastonite, an amphibole group such as anthophyllite, tremolite and actinolite, a feldspar group such as orthoclase, albite, barium feldspar and anorthite, a sodalite group such as sodalite and nocerite, analcite, and natrolite. Component (B) preferably has a pore volume of pores having radii of at least 20 Å as measured by a mercury injection method of at least 0.1 cc/g, more preferably from 0.3 to 5 cc/g. Here, the pore volume is measured within a pore radius being from 20 to 30,000 Å by a mercury injection method employing a mercury porosimeter. In Examples, the pore volume was measured by "Auto Pore 9200" manufactured by Shimadzu Corporation. When a compound having a pore volume of pores having radii of at least 20 Å of less than 0.1 cc/g, is used as component (B), it tends to be difficult to obtain high polymerization activities. Further, component (B) is preferably subjected to chemical treatment. Here, the chemical treatment may be surface treatment to remove impurities deposited on the surface for treatment to give an influence over the crystal structure of clay. Specifically, acid treatment, alkali treatment, salt treatment and organic substance treatment may be mentioned. The acid treatment is intended not only to remove impurities on the surface but also to elute cations such as Al, Fe or Mg in the crystal structure, whereby the surface area is increased. By the alkali treatment, the crystal structure of clay will be destroyed, and a change will be brought about to the structure of clay. Further, by the salt treatment and organic substance treatment, an ion complex, a molecular complex or an organic derivative may be formed, and the surface area and the interlaminar distance may be changed. Further, utilizing ion exchangeability, interlaminar exchangeable ions may be substituted by other large bulky ions to obtain a layered substance having the interlaminar distance enlarged. Namely, the bulky ions play a role of pillars supporting the layered structure, and they are called pillars. Further, introduction of a different substance between the layers of a layered substance is referred to as intercalation. Guest compounds to be intercalated include, for example, cationic inorganic compounds such as TiCl 4 and ZrCl 4 , metal alcholates such as Ti(OR) 4 , Zr(OR) 4 , PO(OR) 3 and B(OR) 3 wherein R is alkyl, aryl, etc., and metal hydroxide ions such as [Al 13 O 4 (OH) 24 ] 7+ , [Zr 4 (OH) 14 ] 2+ and [Fe 3 O(OCOCH 3 ) 6 ] + . These compounds may be used alone, or two or more may be used in combination. During intercalation of these compounds, a polymer obtained by hydrolysis of e.g. a metal alcholate such as Si(OR) 4 , Al(OR) 3 or Ge(OR) 4 , or a colloidal inorganic compound such as SiO 2 , may be present. As an example of pillars, an oxide which will be formed by dehydration under heating after the intercalation of the above hydroxide ions between the layers, may be mentioned. Component (B) may be used as it is, or it may have water added and adsorbed afresh or may be subjected to heat dehydration treatment before use. Further, the above solid materials may be used alone or in combination as a mixture of two ore more of them. Component (C) i.e. an organic aluminum compound to be used in the present invention may be compounds of the formula AlR 6 j X 3-j wherein R 6 is a C 1-20 hydrocarbon group, X is hydrogen, halogen or an alkoxy group, and j is a number satisfying 0 < j ≦ 3, or low molecular weight polymers of organic aluminum compounds in which aluminum atoms are bonded to one another with oxygen or nitrogen interposed therebetween. These materials may be used alone or in combination as a mixture. Specifically, component (C) may, for example, be a trialkylaluminum such as trimethylaluminum, triethylaluminum, tripropylaluminum or triisobutylaluminum, a halogen-containing organic aluminum compound such as diethylaluminium chloride, di-n-propylaluminum chloride or diisobutylaluminium chloride, an alkoxide-containing organic aluminum compound such as dimethylaluminum methoxide or diethylaluminum methoxide, a hydride-containing organic aluminum compound such as dimethylaluminum hydride or diethylaluminum hydride, or an aluminoxane such as methylaluminoxane, ethylaluminoxane or isobutylaluminoxane. Among them, a trialkylaluminum or an aluminoxane is preferred, and a trialkylaluminum is particularly preferred. It is preferred to conduct the contacting reaction so that the weight ratio of the transition metal in component (A) to the aluminum in component (C), per gram of component (B), would be 0.00001-1 (g):0.001-100 (g). The contacting may be conducted in an inert gas such as nitrogen or in an inert hydrocarbon solvent such as pentane, hexane, heptane, toluene or xylene. The contacting is conducted usually at a temperature within a range of from -20°C to the boiling point of the solvent, preferably within a range of from room temperature to the boiling point of the solvent. Further, as the organic aluminum compound of component (D) which is used as the case requires in the present invention, the same compounds as for component (C) may be mentioned. The amount of the organic aluminum compound to be used for this purpose is selected so that the molar ratio of the transition metal in component (A) to the aluminum in component (D) would be 1:0-10,000. The contacting order of the respective components of the catalyst is not particularly limited. However, they may, for example, be contacted in the following orders: 1 ○ Components (A) and (B) are contacted, and then component (C) is added. 2 ○ Components (A) and (C) are contacted, and then component (B) is added. 3 ○ Components (B) and (C) are contacted, and then component (A) is added. Other than the above orders, the three components may simultaneously be contacted. During or after contacting the respective catalyst components, a polymer such as polyethylene or polypropylene, or a solid of an inorganic oxide such as silica or alumina, may be present or contacted. Further, an olefin may be prepolymerized in the presence of components (A), (B) and (C) and, if necessary, an organic aluminum compound of component (D), to form a catalyst, and polymerization of an olefin may be conducted in the presence of this catalyst and, if necessary, an organic aluminum compound. The temperature for the prepolymerization is usually within a range of from -50 to +100°C, and the time for the prepolymerization is usually from 0.1 to 100 hours, preferably from 0.1 to 50 hours. As the organic aluminum compound of component (D) which is used as the case requires at the time of the prepolymerization, the same compounds as for component (C) may be employed. Accordingly, component (D) may be compounds as defined in claim 17, or low molecular weight polymers of organic aluminum compounds in which aluminum atoms are bonded to one another with oxygen or nitrogen interposed there between. The amount of the organic aluminum compound to be used for this purpose is selected so that the molar ratio of the transition metal in component (A) to the aluminum in component (D) would be 1:0-10,000. The olefin to be used for the prepolymerization is preferably the olefin to be used for the subsequent polymerization, but other olefin may be used. Further, two or more olefins may be used in combination as a mixture. The amount of the polymer formed by the prepolymerization is usually within a range of from 0.001 to 1,000 g, preferably from 0.01 to 300 g, more preferably from 0.1 to 300 g, per gram of component (B). The solvent to be used for the production of the catalyst for polymerizing an olefin according to the present invention, may, for example, be butane, pentane, hexane, heptane, octane, cyclohexane, toluene or xylene, or a mixture thereof. The solid catalyst thus obtained, may be used without washing or after washing. The olefin to be used for polymerization may be ethylene, propylene, 1-butene, 1-hexene, 3-methyl-1-butene, 3-methyl-1-pentene, 4-methyl-1-pentene, vinylcycloalkane, styrene or derivatives thereof. This polymerization may suitably be applied not only to homopolymerization but also to usual random copolymerization or block copolymerization. The polymerization reaction is conducted in the presence or absence of a solvent such as a liquefied α-olefin or an inert hydrocarbon such as butane, pentane, hexane, heptane, toluene or cyclohexane. The temperature is usually within a range of from -50° to +250°C. The pressure is not particularly limited, but is preferably within a range of from atmospheric pressure to about 2,000 kgf/cm 2 . Further, hydrogen as a molecular weight controlling agent may be present in the polymerization system. According to the method of the present invention, it is possible to obtain an olefin polymer having a narrow molecular weight distribution, or when applied to copolymerization of two or more olefins, an olefin polymer having narrow molecular weight and compositional distributions, under very high polymerization activities, whereby it is unnecessary to remove the catalyst residue from the obtained polymer. Thus, the present invention is very useful from the industrial point of view. Now, the present invention will be described in further detail with reference to Examples. However, it should be understood that the present invention is by no means restricted by such specific Examples. COMPARATIVE EXAMPLE 1 0.97 mg of biscyclopentadienylzirconium dichloride was preliminarily contacted with a toluene solution of 5.00 mM, as aluminum atom, of methylaluminoxane (molecular weight: 1232; manufactured by TOSO-ACZO) for 30 minutes at room temperature under a nitrogen atmosphere. Into a 2 ℓ induction-stirring type autoclave flushed with purified nitrogen, 500 ml of toluene and a mixed solution of biscyclopentadienylzirconium dichloride and methylaluminoxane were introduced at room temperature under a nitrogen stream. The mixed solution was heated to 70°C, and then ethylene was introduced so that the ethylene partial pressure would be 9 kgf/cm 2 , and polymerization was conducted for one hour. Then, supply of ethylene was stopped, and the content of the autoclave was cooled to 30°C, and the interior gas was purged to obtain 11.6 g of powdery polyethylene. The amount of the polyethylene produced per gram of the zirconium was 3.8 x 10 4 g, and the catalytic activities were 1,300 g-PE/g-cat·h·kgf·cm -2 . Further, the amount of the polyethylene produced per gram of the aluminum derived from methylaluminoxane, was 86 g. Reference Example 1 (1) Preparation of ethylene bis(4,5,6,7-tetrahydroindenyl)zirconium dichloride Preparation of the above complex was conducted in the same manner as disclosed with respect to ethylene bis(4,5,6,7-tetrahydroindenyl)titanium dichloride in Journal of Organometallic Chemistry, 232 (1982) 233. COMPARATIVE EXAMPLE 2 0.82 mg of a racemic modification of ethylene bis(4,5,6,7-tetrahydroindenyl)zirconium dichloride was contacted with 1.9 ml of a toluene solution of 10.10 mM trimethylaluminum for 30 minutes at room temperature in a nitrogen atmosphere, and the mixture was further preliminarily contacted with a toluene solution of 12.5 mM, as aluminum atom, of methylaminoxane (manufactured by TOSO-ACZO). Using the product, polymerization of propylene was conducted. Into a 2 ℓ induction-stirring type autoclave thoroughly flushed with purified nitrogen, 300 ml of toluene and a mixed solution of ethylene bis(4,5,6,7-tetrahydroindenyl)zirconium dichloride and methylaluminoxane were introduced at room temperature under a nitrogen stream. Further, 600 ml of liquid propylene was introduced. The autoclave was heated to 70°C, and polymerization was conducted for one hour. Then, the interior gas was purged to obtain 115 g of a propylene polymer. The amount of the propylene polymer produced per gram of the zirconium was 6.6 × 10 5 g. Further, the amount of propylene polymer produced per gram of the aluminum derived from methylaluminoxane was 340 g. Further, the boiling heptane insoluble content was 96%. Reference Example 2 (1) Preparation of isopropylidene(cyclopentadienyl)(fluorenyl)zirconium dichloride Preparation of the above complex was conducted by the same method as disclosed in Japanese Unexamined Patent Publication No. 41305/1990. COMPARATIVE EXAMPLE 3 0.83 mg of isopropylidene(cyclopentadienyl)(fluorenyl)zirconium dichloride was preliminarily contacted with a toluene solution of 12.5 mM, as aluminum atom, of methylaluminoxane (manufactured by TOSO-ACZO) for 30 minutes at room temperature under a nitrogen atmosphere. Into a 2 ℓ induction-stirring type autoclave thoroughly flushed with purified nitrogen, 300 ml of toluene and a mixed solution of the above isopropylidene(cyclopentadienyl)(fluorenyl)zirconium dichloride and methylaluminoxane were charged at room temperature under a nitrogen stream. Further, 600 ml of liquid propylene was introduced. The autoclave was heated to 70°C, and polymerization was conducted for one hour. Then, the interior gas of the autoclave was purged to obtain 108 g of a propylene polymer. The amount of the propylene polymer produced per gram of the zirconium was 6.2 × 10 5 g. Further, the amount of the propylene polymer produced per gram of the aluminum derived from methylaluminoxane, was 320 g. The rrrr by 13 C-NMR of the obtained polymer was 89%. Example 1 (1) Preparation of a catalyst Into a 100 ml round bottom flask thoroughly flushed with nitrogen, a toluene solution containing 1.48 mg of commercially available biscyclopentadienylzirconium dichloride, was introduced, and 1.3 mM of trimethylaluminum was added thereto under stirring at room temperature. Into a separate 100 ml round bottom flask, 0.55 g of magnesium silicate pentahydrate (manufactured by Wako Junyaku Kogyo K.K.) with a pore volume of pores having radii of at least 20 Å as measured by a mercury injection method being 0.803 cc/g, was introduced, and the interior of the flask was thoroughly flushed with nitrogen. Then, 45 ml of toluene was added thereto to obtain a slurry. 7.5 ml of this slurry was added to the above contacted product of biscyclopentadienylzirconium dichloride and trimethylaluminum, at room temperature. After completion of the addition, stirring was continued at room temperature for one hour to obtain a catalyst slurry. (2) Copolymerization of ethylene and propylene Into a 2 ℓ induction-stirring type autoclave flushed with purified nitrogen, 300 ml of n-hexane, 24 µ mol of trimethylaluminum and then the entire amount of the above catalyst slurry were introduced at room temperature under a nitrogen stream. Further, 600 ml of liquid propylene was introduced. The mixed solution was heated to 70°C. Then, ethylene was introduced so that the ethylene partial pressure would be 7.6 kgf/cm 2 , and polymerization was conducted for one hour. Then, supply of ethylene was stopped, and ethanol was introduced to terminate the polymerization to obtain 75.0 g of an ethylene-propylene copolymer. The amount of the copolymer produced per gram of the zirconium was 1.6 × 10 5 g, the amount of the copolymer produced per gram of the aluminum derived from trimethylaluminum, was 2.1 x 10 3 g, and the amount of the copolymer produced per gram of magnesium silicate was 1.1 × 10 3 g. Further, the propylene content in the obtained polymer was 8.1 mol%. COMPARATIVE EXAMPLE 4 (1) Preparation of a catalyst A catalyst solution was prepared in the same manner as in Example 1 (1) except that no magnesium silicate was employed. (2) Copolymerization of ethylene and propylene Polymerization was conducted in the same manner as in Example 1 (2) except that the catalyst prepared in Comparative Example 4 (1) was used as the catalyst. The obtained polymer was in a trace amount. COMPARATIVE EXAMPLE 5 (1) Preparation of a catalyst Into a 100 ml round bottom flask thoroughly flushed with nitrogen, a toluene solution containing 0.72 mg of commercially available biscyclopentadienylzirconium dichloride was introduced, and a toluene solution containing 3.7 mM as aluminum atom of methylaluminoxane (molecular weight: 1,232, manufactured by TOSO-ACZO) was added thereto under stirring at room temperature. After completion of the addition, stirring was continued at room temperature for one hour to obtain a catalyst. (2) Copolymerization of ethylene and propylene Using the catalyst prepared in Comparative Example 5 (1), polymerization was conducted in the same manner as in Example 1 (2) except that no trimethylaluminum was employed, to obtain 8.3 g of an ethylene-propylene copolymer. The amount of the copolymer produced per gram of the zirconium was 3.7 × 10 4 g, and the amount of the copolymer produced per gram of the aluminum derived from methylaminoxane, was 83 g. Example 2 (1) Preparation of a catalyst A catalyst slurry was prepared in the same manner as in Example 1(1) using 0.83 mg of biscyclopentadienylzirconium dichloride, 1.4 mM of trimethylaluminum, 0.55 g of calcium silicate (manufactured by Wako Junyaku Kogyo K.K.) with a pore volume of pores having radii of at least 20 Å as measured by a mercury injection method being 0.681 cc/g, 24 ml of toluene and 2.0 ml of a calcium silicate slurry. (2) Copolymerization of ethylene and propylene Polymerization was conducted in the same manner as in Example 1 (2) except that the catalyst prepared in Example 2 (1) was used as the catalyst, whereby 47.1 g of an ethylene-propylene copolymer was obtained. The amount of the copolymer produced per gram of the zirconium was 1.8 × 10 5 g, and the amount of the copolymer produced per gram of the aluminum derived from trimethylaluminum, was 1.2 × 10 3 g. Example 3 (1) Preparation of a catalyst Into a 300 ml round bottom flask, 50 ml of toluene was introduced, and 0.3 mM of trimethylaluminum was added thereto. Then, the entire amount of the catalyst slurry prepared in the same manner as in Example 1 (1) except that 1.65 g of magnesium silicate pentahydrate, was used, was added thereto. Then, ethylene was introduced under stirring and prepolymerized at room temperature for one hour. After completion of the reaction, the supernatant was removed, followed by washing with n-hexane. By this reaction, a solid catalyst slurry containing 40.9 µ mol of zirconium, 5.4 mM of aluminum and 2.7 g of polyethylene per gram of magnesium silicate, was obtained. (2) Copolymerization of ethylene and propylene Polymerization was conducted in the same manner as in Example 1 (2) except that the catalyst prepared in Example (1) was used as the catalyst, to obtain 99.2 g of an ethylene-propylene copolymer having a propylene content of 8.0 mol%. The amount of the copolymer produced per gram of the zirconium was 1.3 × 10 5 g, and the amount of the copolymer produced per gram of the aluminum was 3.3 × 10 3 g. Example 4 (1) Preparation of a catalyst A catalyst slurry was prepared in the same manner as in Example 1 (1) except that 2.16 mg of ethylene bis(4,5,6,7-tetrahydroindenyl)zirconium dichloride was used as component (A). (2) Polymerization of propylene Into a 2 ℓ induction-stirring type autoclave thoroughly flushed with purified nitrogen, 300 ml of toluene, 24 µ mol of trimethylaluminum and then the catalyst slurry prepared in Example 4 (1) were introduced at room temperature under a nitrogen stream, and 600 ml of liquid propylene was further introduced. The autoclave was heated to 70°C, and polymerization was conducted for 30 minutes. Then, the interior gas of the autoclave was purged to obtain 63.5 g of a propylene polymer. The amount of the polymer produced per gram of the zirconium was 1.4 × 10 5 g, the amount of the polymer produced per gram of the aluminum derived from trimethylaluminum, was 1.8 × 10 3 g. Further, the boiling heptane insoluble content (value after refluxing for three hours) showing the stereospecificity, was 96%. Example 5 (1) Preparation of a catalyst A catalyst slurry was prepared in the same manner as in Example 1 (1) except that 2.19 mg of isopropylidene(cyclopentadienyl)(fluorenyl)zirconium dichloride was used as component (A). (2) Polymerization of propylene Polymerization was conducted in the same manner as in Example 4 (2) except that the catalyst prepared in Example 5 (1) was used as the catalyst, whereby 67.2 g of a propylene polymer was obtained. The amount of the polymer produced per gram of the zirconium was 1.4 × 10 5 g, the amount of the polymer produced per gram of the aluminum derived from trimethylaluminum, was 1.9 × 10 3 g. Further, the syndiotactic·pentad of the obtained polymer was measured by 13 C-NMR and was found to be 91%. COMPARATIVE EXAMPLE 6 (1) Preparation of a catalyst A catalyst slurry was prepared in the same manner as in Example 1 (1) using 0.73 mg of bis(cyclopentadienyl)zirconium dichloride, 1.3 mM of trimethylaluminum, 1.30 g of silica (Fuji Davison 952, water content: 14.5 wt%), 42 ml of toluene and 5.0 ml of a silica slurry. (2) Copolymerization of ethylene and propylene Polymerization was conducted in the same manner as in Example 1 (2) except that a catalyst prepared in Comparative Example 6 (1) was used as the catalyst, whereby 16.5 g of an ethylene-propylene copolymer was obtained. The amount of the copolymer produced per gram of the zirconium was 7.2 × 10 4 g. Further, the amount of the copolymer per gram of the aluminum derived from trimethylaluminum, was 4.8 × 10 2 g. Example 6 (1) Preparation of a catalyst Into a 300 ml round bottom flask, 15.1 mg of commercially available biscyclopentadienylzirconium dichloride was introduced, and the interior of the flask was thoroughly flushed with nitrogen. Then, 50 ml of n-heptane was added thereto to obtain a slurry. Separately, 1.86 g of trimethylaluminum and 4.86 g of commercially available diatomaceous earth (Kunilite 401, Kunimine Kogyo K.K.; same applies hereinafter) were taken, respectively, and 10 ml and 40 ml of n-heptane were added, respectively. While vigorously stirring the biscyclopentadienylzirconium dichloride slurry, the trimethylaluminum solution was dropwise added thereto at room temperature, and then the diatomaceous slurry was dropwise added. Heat was generated accompanied by generation of gas. After completion of the dropwise addition, stirring was continued for two hours to obtain a gray slurry. The zirconium concentration in the catalyst slurry was 0.47 µ mol/ml. (2) Polymerization of ethylene Into a 2 ℓ induction-stirring type autoclave flushed with nitrogen, 500 ml of n-hexane, 1.9 ml of a toluene solution of trimethylaluminum (10.18 mM) and 5.1 ml of the above catalyst slurry were sequentially introduced at room temperature under a nitrogen stream. The mixed solution was heated to 70°C. Then, ethylene was introduced so that the ethylene partial pressure would be 9 kgf/cm 2 , and polymerization was conducted for one hour. then, supply of ethylene was topped, and ethanol was introduced to terminate the polymerization. Then, the content of the autoclave was cooled to 30°C, and the interior gas was purged. As a result, 46 g of powdery polyethylene with Mw/Mn being 2.3 was obtained. The amount of the polymer produced per gram of the zirconium was 2.1 × 10 5 g, and the amount of the polymer produced per gram of the aluminum derived from trimethylaluminum, was 6,700 g. (3) Copolymerization of ethylene and propylene Into a 2 ℓ induction-stirring type autoclave flushed with purified nitrogen, 300 ml of n-hexane, 1.9 ml of a toluene solution of trimethylaluminum (10.18 mM) and 5.1 ml of the above catalyst slurry were sequentially introduced at room temperature under a nitrogen stream. Further, 600 ml of liquid propylene was introduced. The mixed solution was heated to 70°C. Then, ethylene was introduced so that the ethylene partial pressure would be 7.6 kgf/cm 2 , and polymerization was conducted for one hour. Then, supply of ethylene was stopped, and ethanol was introduced to terminate the polymerization. Then, the content of the autoclave was cooled to 30°C, and the interior gas was purged. As a result, 55 g of an ethylene-propylene copolymer with Mw/Mn being 2.2 was obtained. The amount of the copolymer produced per gram of the zirconium was 2.5 × 10 5 g. Further, the amount of the copolymer per gram of the aluminum derived from trimethylaluminum was 7,900 g. Example 7 (1) Preparation of a catalyst Into a 300 ml round bottom flask, 150 mg of commercially available biscyclopentadienylzirconium dichloride was introduced, and the interior of the flask was thoroughly flushed with nitrogen. Then, 10 ml of n-heptane was added thereto to obtain a slurry. Separately, 1.38 g of triethylaluminum and 9.6 g of commercially available diatomaceous earth were taken, respectively, and 10 ml and 80 ml of n-heptane were added, respectively. While vigorously stirring the biscyclopentadienylzirconium dichloride slurry, the trimethylaluminum solution was dropwise added at room temperature, and then the diatomaceous earth slurry was dropwise added thereto. Heat was generated accompanied by generation of gas. After completion of the dropwise addition, stirring was continued for two hours to obtain a gray slurry. The zirconium concentration in the catalyst slurry was 4.7 µ mol/ml. Into a 300 ml round bottom flask, 60 ml of the above slurry was taken at room temperature under a nitrogen atmosphere, and 2.0 ml of a toluene solution of trimethylaluminum (1.40M) was added thereto. Then, ethylene gas was introduced into the system and prepolymerized at room temperature for one hour. Then, the supernatant was removed, followed by washing with hexane. By this reaction, a solid catalyst containing 34.7 µ mol of zirconium, 3.8 mM of aluminum and 1.1 g of polyethylene per 1 g of diatomaceous earth, was obtained. (2) Polymerization of ethylene Into a 2 ℓ induction-stirring type autoclave thoroughly flushed with purified nitrogen, 150 g of dry sodium chloride, the above solid catalyst in an amount corresponding to 8.5 µ mol of zirconium and 8.4 ml of a toluene solution of trimethylaluminum (10.18 mM) were introduced at room temperature under a nitrogen stream. The content of the autoclave was heated to 70°C. Then, ethylene was introduced so that the ethylene partial pressure would be 9 kgf/cm 2 , and polymerization was conducted for one hour. Then, the content of autoclave was washed with water to remove sodium chloride. Then, the polymer was washed with hexane. As a result, 149 g of powdery polyethylene having a bulk density of 0.45 g/cm 3 and Mw/Mn being 2.3 was obtained. The amount of the polyethylene produced per gram of the zirconium was 1.9 × 10 5 g, and the amount of the polyethylene produced per gram of the aluminum derived from trimethylaluminum, was 5,400 g. Example 8 (1) Preparation of a catalyst Into a 100 ml round bottom flask, 14.8 mg of commercially available bis(cyclopentadienyl)zirconium dichloride was introduced, and the interior of the flask was thoroughly flushed with nitrogen. Then, 10 ml of n-heptane was added thereto to obtain a slurry. Separately, 1.83 g of trimethylaluminum and 3.18 g of zeolite (Zeolite Beta, manufactured by PQ Corporation; same applies hereinafter) were taken, respectively, and 20 ml of n-heptane was added to each of them. While vigorously stirring the bis(cyclopentadienyl)zirconium dichloride, the trimethylaluminum solution was dropwise added thereto at room temperature, and then the zeolite slurry was dropwise added thereto. Heat was generated accompanied by generation of gas. After completion of the dropwise addition, stirring was continued for two hours to obtain a gray slurry. The zirconium concentration in the catalyst slurry was 1.01 µ mol/ml. (2) Polymerization of ethylene Polymerization was conducted in the same manner as in Example 6 (2) except that the amount of the toluene solution of trimethylaluminum was changed to 1.8 ml and the amount of the catalyst slurry introduced, was changed to 1.8 ml, whereby 91 g of powdery polyethylene with Mw/Mn being 2.3 was obtained. The amount of the polymer produced per gram of the zirconium was 5.5 × 10 5 g. Further, the amount of the polymer produced per gram of the aluminum derived from trimethyl aluminum, was 3,600 g. (3) Copolymerization of ethylene and propylene Copolymerization was conducted in the same manner as in Example 6 (3) except that the amount of the toluene solution of trimethylaluminium was changed to 1.8 ml and the amount of the above catalyst slurry introduced, was changed to 1.8 ml, whereby 130 g of an ethylene-propylene copolymer with Mw/Mn being 2.2 was obtained. The amount of the copolymer produced per gram of the zirconium was 7.8 × 10 5 g. Further, the amount of the copolymer produced per gram of the aluminum derived from trimethylaluminum, was 5,200 g. Example 9 (1) Preparation of a catalyst Into a 100 ml round bottom flask, 50 mg of commercially available bis(cyclopentadienyl)zirconium dichloride was introduced, and the interior of the flask was thoroughly flushed with nitrogen. Then, 10 ml of n-heptane was added thereto to obtain a slurry. Separately, 1.25 g of trimethylaluminum and 2.31 g of zeolite were taken, respectively, and 20 ml of n-heptane was added to each of them. While vigorously stirring the bis(cyclopentadienyl)zircondium dichloride slurry, the trimethylaluminum solution was dropwise added thereto at room temperature, and then the zeolite slurry was dropwise added thereto. Heat was generated accompanied by generation of thus. After completion of the dropwise addition, stirring was continued for two hours to obtain a gray slurry. The zirconium concentration in the catalyst slurry was 3.4 µ mol/ml. Into 100 ml round bottom flask, 40 ml of the above slurry was taken at room temperature under a nitrogen atmosphere, and 1.0 ml of a toluene solution of trimethylaluminum (1.40M) was added thereto. Then, ethylene gas was introduced into the system and prepolymerized at room temperature for 3 hours. Then, the supernatant was removed, followed by washing with hexane. By this reaction, a solid catalyst containing 45.9 µ mol of zirconium, 5.9 mM of aluminum and 2.4 g of polyethylene per gram of zeolite, was obtained. (2) Polymerization of ethylene Polymerization was conducted in the same manner as in Example 7 (2) except that the above solid catalyst was employed, whereby 79 g of powdery polyethylene having a bulk density of 0.44 g/cm 3 was obtained. The amount of the polyethylene produced per gram of the zirconium was 1.0 × 10 5 g, and the amount of the polyethylene produced per gram of the aluminum derived from trimethylaluminum, was 2,500 g.

Claims: A catalyst for polymerizing an olefin which consists essentially of a product obtained by contacting (A) a metallocene-type transition metal compound, (B) at least one member selected from silicates other than ion exchanging layered compounds, and (C) an organic aluminum compound of the formula AlR 6 j X 3-j , wherein R 6 is a C 1-20 hydrocarbon group, X is hydrogen, halogen or an alkoxy group, and j is a number satisfying 0 < j ≤ 3. The catalyst according to Claim 1, wherein the pore volume of pores having radii of at least 2nm (20Å) of component (B) is at least 0.1 cm 3 /g (cc/g) as measured by a mercury injection method. The catalyst according to Claim 2, wherein the pore volume is within a range of from 0.3 to 5 cm 3 /g (cc/g). The catalyst according to Claim 1, wherein component (B) is chemically treated. The catalyst according to Claim 4, wherein the chemical treatment is acid treatment, alkali treatment, salt treatment or organic substance treatment. The catalyst according to Claim 1, wherein the metallocene-type transition metal compound of component (A) is an organometallic compound composed of a cyclopentadienyl ring-containing ligand and a metal of Group 4, 5 or 6 of the longform Periodic Table. The catalyst according to Claim 1, wherein component (A) is a compound of the formula (1) or (2): R 1 m (CpR 2 n ) (CpR 2 n )MR 3 2 [R 1 m (CpR 2 n ) (CpR 2 n )MR 3 R 4 ] + R 5- wherein each of (CpR 2 n ) which may be the same or different, is a cyclopentadienyl group or a substituted cyclopentadienyl group, R 1 is a covalent bond crosslinking group containing an element of Group 14 of the long-form Periodic Table such as carbon, silicon or germanium, each of R 2 which may be the same or different, is hydrogen, halogen, a silicon-containing group, a C 1-20 hydrocarbon group which may have a halogen substituent, an alkoxy group or an aryloxy group, provided that when two R 2 are located on two adjacent carbon atoms on the cyclopentadienyl group, they may bond to each other to form a C 4-6 ring, each of R 3 which may be the same or different, is hydrogen, halogen, a silicon-containing group, a C 1-20 hydrocarbon group which may have a halogen substituent, an alkoxy group or an aryloxy group, m is 0 or 1, each n is an integer satisfying m + n = 5, M is a metal of Group 4, 5 or 6 of the long-form Periodic Table, R 4 is a neutral coordinated to M, and R 5- is a counter anion capable of stabilizing said metal. The catalyst according to Claim 7, wherein the cyclopentadienyl group or the substituted cyclopentadienyl group of the formula CpR 2 n in the formulas (1) and (2) is a substituted cyclopentadienyl group, an indenyl group, a tetrahydroindenyl group, a fluorenyl group or an octahydrofluorenyl group. The catalyst according to Claim 7, wherein R 1 in the formulas (1) and (2) is an alkylene group, an alkylidene group or a silicon-containing crosslinking group. The catalyst according to Claim 7, wherein M in the formulas (1) and (2) is titanium, zirconium or hafnium. The catalyst according to Claim 1, wherein the organic aluminum compound is a trialkylaluminum. The catalyst according to Claim 1, wherein the weight ratio of the transition metal in component (A) to the aluminum in component (C), per gram of component (B), is 0.00001-1 (g): 0.001-100 (g). A solid catalyst for polymerizing an olefin, which is formed by prepolymerizing an olefin in an amount of from 0.001 to 1,000 g per gram of the following component (B) by a product obtained by contacting (A) a metallocene-type transition metal compound, (B) at least one member selected from silicates other than ion exchanging layered compounds, and (C) an organic aluminum compound of the formula AlR 6 j X 3-j , wherein R 6 is a C 1-20 hydrocarbon group, X is hydrogen, halogen or an alkoxy group, and j is a number satisfying 0 < j ≤ 3. A method for producing an olefin polymer, which comprises polymerizing or copolymerizing an olefin in the presence of the solid catalyst for polymerizing an olefin as defined in Claim 13 and, if necessary, (D) an organic aluminum compound. The solid catalyst according to Claim 13, wherein the temperature of prepolymerization is within a range of from -50 to +100°C. The solid catalyst according to Claim 13, wherein the amount of the olefin polymer formed by the prepolymerization is from 0.01 to 300 g per gram of component (B). A method for producing an olefin polymer, which comprises homopolymerizing or copolymerizing an olefin in the presence of a catalyst consisting essentially of a product obtained by contacting (A) a metallocene-type transition metal compound, (B) at least one member selected from silicates other than ion exchanging layered compounds, and (C) an organic aluminum compound of the formula AIR 6 j X 3-j , wherein R 6 is a C 1-20 hydrocarbon group, X is hydrogen, halogen or an alkoxy group, and j is a number satisfying 0 < j ≤ 3 and, if necessary, (D) a further organic aluminum compound, which is different from (C), of the formula AlR 7 k Y 3-k , wherein R 7 is a C 1-20 hydrocarbon group, Y is hydrogen, halogen or an alkoxy group, and k is a number satisfying 0 < k ≤ 3. The method according to Claim 17, wherein the olefin is at least one member selected from the group consisting of ethylene, propylene, 1-butene, 1-hexene, 3-methyl-1-butene, 3-methyl-1-pentene, 4-methyl-1-pentene, vinylcycloalkane and styrene. The method according to Claim 17, wherein the polymerization temperature is within a range of from -50 to +250°C. The method according to Claim 17, wherein the polymerization pressure is within a range of from atmospheric pressure to 1960 bar (2,000 kgf/cm 2 ).

Inventors: ISOBE EIJI, MARUYAMA YASUO, SHIMIZU FUMIHIKO, SUGA YOSHINORI, SUZUKI TORU, ISOBE, EIJI, MARUYAMA, YASUO, SHIMIZU, FUMIHIKO, SUGA, YOSHINORI, SUZUKI, TORU
Applicants: JAPAN POLYCHEM CORP, JAPAN POLYCHEM CORPORATION
Application year: 1992
Main classification: C08F10
IPC codes: C08F10, C08F4