Method and apparatus for joining steel pieces in a hot rolling mill

Abstract: Methods and apparatus for joining conveyed steel pieces in a hot rolling mill are disclosed. A joining apparatus having a series of fusing torches (6) extending laterally across the steel path is used, either before a rough rolling stage or between rough rolling and finish rolling. The fusing torches (6) which operate at the side edges of the pieces to be joined are controlled to have independent movement by a controller (37), in such a way that the time elapsing between fusing and pressing together of portions at the lateral edges of the join line does not exceed a critical time for regrowth of oxide scale. Various mounting and control techniques for the fusing torches (6) are proposed, including the possibility of two independently-driveable sets (8,8a) the controller can base its control of the torches (6) on steel strip width information obtained from the processing path.

Description: This invention relates to methods and apparatus for joining steel pieces in a hot rolling mill. A hot rolling mill e.g. a hot steel strip rolling machine, is well known. A typical known machine has a continuous casting unit, a heating furnace, a rough rolling stage and a finish rolling stage. Hot rolled steel slab made by the continuous casting unit is converted to the product by heating in the furnace followed by hot rolling in the rough and finish rolling stages. Because the steel is processed as slabs in the heating process, it is generally rolled with certain intervals between the successive slabs or pieces. Recently, continuous rolling has been proposed. Continuous rolling involves joining together the steel slabs or pieces, either before they are rolled or during the rolling process. The achievement of commercial continuous rolling is expected to enable large savings in energy and labour, improvement in yield and improved productivity. Because of the high speeds, high temperatures and large forces involved in the rolling of steel, it is difficult to achieve continuous rolling. Prior art documents contain a number of proposals. JP-A-60/170581 and JP-A-62/234679 both describe joining successive steel pieces together by fusing their adjacent faces using high frequency induction heating. JP-A-61/253178 describes fusing the adjacent faces by generating an arc using DC current. JP-A-62/127185 describes fusing overlapping surfaces to be jointed while blowing oxide scale from the surfaces using a jet of iron powder in oxygen gas. Despite these prior disclosures, continuous rolling technology has not yet been commercially realised. We believe that this is because the following three conditions have not yet been adequately fulfilled: (1) the end surfaces of the steel pieces must be raised to at least 1500°C; (2) oxide scale on the surfaces to be joined must not exceed a certain limit, and (3) the faces to be joined must be substantially flat. Of the above-mentioned publications, JP-A-62/127185 does give importance to removing oxide scale. However the use of only oxygen gas against the surfaces results in insufficient heating. The other methods, using high frequency induction heating and melting by arcs, tend to be incapable of heating to the centre of a surface to be jointed. Furthermore, they suffer with a problem of oxide scale. CH-A- 248544 discloses joining pieces of metal by melting the surface of each piece using movable blow torches, and then moving the pieces together very quickly to join them. The prior technology does not consider point (3) at all. The end faces of rolled steel pieces are usually sheared by a drum shearing machine, giving sheared faces which are straight neither in width or thickness. Even with adequate heating, such faces will be jointed only at random spot locations, rendering the joint liable to breakdown under the high tensions existing in the material during rolling. A large longitudinal compression can be used to avoid such random point-joining, but this is liable to cause swelling or bending of the steel out of alignment, with subsequent problems. These existing problems have been substantially addressed in our European application EP-A-460655, some of which is in Article 54(3) EPC relation with the present application. In that application which discloses the closest prior art, we describe joining rolled steel pieces by using a lateral series of fusing torches to melt-cut the ends of the steel pieces. The fusing torches may be moved laterally for the melt-cutting, to create a flat melted surface suitable for joining. The pieces may be pressed together during or after the melt-cutting. The present invention aims to provide novel methods and apparatus for joining steel pieces in a hot rolling process. In particular, it is preferably sought to solve the above-mentioned three problems existing in the prior art. It is also sought to address certain problems not addressed in EP-A-460655. The present inventors have devoted further work and thought to the problem of oxide scale. They have found that it is not sufficient merely to remove oxide scale, as has been suggested in the prior art. It is also necessary to take care that oxide scale does not re-form in the time between fusing of the steel and joining of the two pieces. If oxide scale does reform above a certain degree, integrity of the joint is threatened. However, the inventors have made the discovery that, provided that the joint is well made at the lateral extremities of the join between the two pieces, it may keep its integrity despite discontinuities elsewhere along the join. Conversely, poor joining due e.g. to oxide scale regrowth, at the lateral extremities of the join is an important contribution to weakness in the joint in the subsequent procedure, particularly in the finish rolling. Based on this new understanding, we propose the following new method and apparatus aspects in which it is ensured, or made possible to ensure, that the time elapsing between the fusing of steel at the lateral extremities of the join line, and the pressing together of the steel pieces, is not greater than a predetermined critical time t c for reformation of oxide scale. This is achieved using a technique in which a multiplicity of fusing torches are moved laterally along the adjacent ends of the two steel pieces to be joined, preferably with a small gap between those two pieces, in a fusing movement to cause at least partial fusing therealong, following which the two pieces are pressed together longitudinally to form the joint. In one aspect, we provide a method according to claim 1 for joining consecutive pieces of steel being processed in a hot rolling mill. In another aspect, we provide apparatuses according to claims 10, 11 for joining consecutive pieces of steel in a hot rolling mill. Control of the maximum time which passes between fusing and pressing together of the lateral extremities of the joint may be achieved in a number of ways. It is possible to adjust the relationship between the predetermined termination position of a fusing torch at the end of its fusing movement, relative to the side edge of the steel piece. It is possible to adjust the relationship between the side edge of a steel piece and a position where a fusing torch will begin its fusing movement. The fusing torches which fuse the two opposite side edges of the steel may perform their fusing movement in the same lateral direction. They may also perform their fusing movement at the same lateral speed. Indeed, in one preferred embodiment all of the fusing torches pass laterally at the same speed, in the same direction, for the fusing movement. In another possibility, the respective lateral speeds in their fusing movements, of the fusing torches which fuse at the two lateral extremities of the join, are adjusted in dependence on the determined or regulated lateral situation of those edges. Detection means may be provided, preferably both upstream and downstream of the joining location, to determine the positions of the side edges of the pieces to be joined. Additionally or alternatively, at least one side guide may be employed to determine the width centre of a steel piece. Preferably side guides are provided for both the preceding and the following steel pieces. Either of such side guides and detection means is operatively connected to a suitable controller, so that the signal therefrom can be used by the controller in determining control signals which are output to the drive or drives controlling the fusing torches. To achieve the variable fusing movement among the fusing torches which is generally required for the present invention, the fusing torches are preferably distributed among a plurality of sets. Each set will comprise at least one, but more usually at least three fusing torches joined together to move together as a unit. In particular, those fusing torches which are employed at or adjacent the respective lateral extremities of the steel pieces are desirably allotted into two such sets, having some necessary independence of control as mentioned above. For simplicity, it is possible to divide the entire series of fusing torches into just two sets, one set for each side of the processing path. Each set conveniently comprises a unitary mounting, such as a bracket or the like, for holding all of the fusing torches of that set. Two sets may be mechanically separate, and rely on the control of separate drive systems to co-ordinate their effects. In another version, two such sets may be connected by an adjustable connector which itself is controllable. Adjustment of the connector may be used to adjust the spacing between the sets e.g. before a fusing movement is made. During the fusing movement, the two connected sets may then move together as one with the same velocity. Other aspects of the invention, as set out in the claims, relate to those combinations of method and apparatus disclosed herein which are characteristic of the present concept, that is, they enable the independent adjustment of fusing at the lateral join extremities. In other aspects, this invention provides a general method of processing steel in which steel pieces are formed, rough rolled and finish rolled, with consecutive pieces being joined by a method as described above, or using apparatus as described above, either before the rough rolling or between the rough rolling and the finish rolling. Similarly, in a further aspect we provide a hot rolling mill comprising joining apparatus according to any of the aspects disclosed above. The joining apparatus may be before the rough rolling apparatus e.g. just after a heating furnace, or it may be between the rough rolling apparatus and the finish rolling apparatus. The present inventors have clarified that the limit time "t c " for regrowth of oxide scale is generally from 5 to 10 seconds for ordinary hot rolled steel. As mentioned above, it is not always necessary to join together the steel pieces continuously over their entire width. But, we find that a reliable joint can be formed provided that the joint is complete at the side edges thereof i.e. at the ends of the join line. This condition can be ensured, even if the widths and alignments of consecutive steel pieces vary, using appropriate detection or guide means connected to a controller for the fusing torches. If one piece is narrower than the other, then the edges of that piece will determine the extremities of the join line; a controller device may be programmed to recognise this situation and drive the torches accordingly. Other situations can be dealt with in a corresponding way. Side guides enable the setting of an appropriate fusing movement start position, even when a steel piece deviates from the centre of the processing path. Principles relating to the invention are now discussed in more detail, and specific embodiments are described. In the drawings: Figure 1 is a perspective schematic view showing elements of a first joining apparatus embodying the invention; Figure 2 is a schematic side view showing stages of a hot steel strip rolling machine in one embodiment; Figure 3 is a view similar to Figure 2, showing a different embodiment; Figure 4 illustrates, in plan view, stages of a jointing method embodying the invention; Figure 5 is a schematic sectional view at a joint, showing how poor jointing may arise; Figure 6 is a view corresponding to Fig. 5, showing control of the process to achieve a good joint; Figure 7 shows, in plan view, stages of a further joining process embodying the invention; Figure 8 shows, in plan view, stages of a further joining process embodying the invention; Figure 9 is a schematic perspective view similar to Fig. 1, showing a further embodiment of apparatus; Figure 10 shows, in plan view, stages of a further joining process embodying the invention, and Figure 11 is a schematic sectional view at a joint, illustrating a further process embodiment. Figures 2 and 3 show the general features of a typical hot steel strip rolling plant. This comprises, sequentially, a continuous casting machine 51, a heating furnace 52, a rough rolling stage 53 comprising a plurality of stands, a finish rolling stage 54 also comprising a plurality of stands, a cooling furnace 55, shearing machine 56 and winding machine 57. Apparatus 58 for joining together successive steel pieces may be positioned, as shown by arrow J, either between the heating furnace 52 and rough rolling stage 53 (Fig.2) i.e. joining together slab pieces after heating, or between the rough rolling and finish rolling stages 53,54 (Fig. 3) i.e. joining together bar pieces after rough rolling and before finish rolling. For joining together slabs (Fig. 2), it is normally preferred to move the joining apparatus 58 along the processing path with the slabs as joining is done. It is possible to use a similar procedure when joining bars. However it is more preferred to use a looper (this is known to the skilled man) to absorb mismatch of the travelling speeds of preceding and subsequent rolled steel pieces, because the speed of these pieces is fast. If a looper is used, rolled steel pieces can be joined at a lowered speed or even when stopped. A joining apparatus of an embodiment of this invention is explained according to Figs. 1 and 4 to 6. Referring to Fig. 1, 1 is a preceding rolled steel piece and 2 is a following rolled steel piece. The preceding and following pieces 1 and 2 are transferred while supported by a table roller 3 and stopped at a desired position. Two pairs of pinch rollers 4 and 5 are arranged just near the rear end of a preceding rolled steel and front end of a following rolled steel. The pinch rollers 4 and 5 function to hold the preceding rolled steel 1 and following rolled steel 2 and to fix the mutual position of both the materials to secure a specified gap g between both the end faces. They can also function to apply a pressure to both the end faces by moving the rolled steels 1 and 2 relatively in such a direction to decrease the gap g. Multiple fusing torches 6 are fixed on the frames 7 and 7a at a specified height over rolled steels 1 and 2 in the width direction with a specified interval, by torch brackets 8 and 8a, which are divided into two units in the width direction. On the other hand, the frame 7 is connected to the crank shaft 10 through the connecting bar 9 and the crank shaft 10 is connected to the motor 12 while supported rotatably by the bearing 11. When the motor 12 rotates, the frame 7 is reciprocated by the crank shaft 10 in the lateral direction and accordingly, the multiple fusing torches 6 mounted on the torch bracket 8 also reciprocate. On the other side, another frame 7a is connected to another crank shaft 10a through a connecting bar 9a and a crank shaft 10a is connected to a motor 12a while supported by a bearing 11a rotatably. When the motor 12a rotates, the frame 7a reciprocates via the crank shaft 10a and accordingly, multiple fusing torches mounted on the torch bracket 8a reciprocate. The motors 12 and 12a are controlled by a microprocessor controller 37. Each fusing torch 6 is connected to the oxygen cylinder 15 and acetylene cylinder 16 via the hoses 13 and 14, and oxygen and acetylene gas are supplied from these cylinders. Each fusing torch 6 is provided with a fine iron powder supply pipe 19 and this supply pipe 19 is connected to the powder supply unit 22 containing fine iron powder and air or nitrogen cylinder 23 via the hose 20. By feeding air and nitrogen gas from the cylinder 23, fine iron powder 21 is supplied to the fusing torch 6 which produces a flame 24. Such torches are used in EP-A-460 655. The flame needs an oxygen surround to reach the required temperature. Consequently they cannot conveniently be closer than about 30mm. The usual "pitch" is about 35mm. For simplicity, only a few are shown. In reality several tens might be present. The pinch rollers 4 and 5 are connected to individual motors (not shown) and driven independently. Because the pinch rollers 4 and 5 support rolled steels 1 and 2 only when they are jointed together and are kept open at other times, the pinch rollers 4 and 5 are supported by respective actuating cylinders (not shown) by which they can be lifted up and down. An embodiment of a joint method using the above mentioned joint apparatus is explained according to Fig. 4. As shown in Fig. 4 (a), a preceding rolled steel 1 is held firmly by the pinch roller 5 and a following rolled steel 2 is transferred by the table roller 3 (see Fig. 1). After the following rolled steel 2 passes the pinch roller 4, it is moved further while supported by the pinch roller 5 so as to bring the end of the following rolled steel towards the rear end of the preceding rolled steel, located at a fixing position. Then, the gap "g" between the rear end of the preceding rolled steel and the front end of the following rolled steel is set to a specified distance, the following rolled steel is stopped and then both the rolled steels are held by the pinch rollers 4 and 5. Then, the relationship between the side edge of each rolled steel band 1,2 fusing torch passing start positions is matched to a specified relationship. This is done by driving the motors 12a and 12 independently, under control of the preprogrammed controller 37 (see Fig. 1) and adjusting the distance between the torch brackets 8 and 8a depending on the width of the rolled steels 1 and 2. The purpose of this operation is to adjust the time passing between fusing by the fusing torch 6 at the edges of both rolled steels to pressing by the pinch rollers 4 and 5 so as not to exceed the limit time of oxide scale regrowth with the relationship between the side edge of the rolled steel and the position where passing of the fusing torch 6 terminates set at a desired condition. Next, injection flow of cutting gas or fine iron powder is blown against the steels by multiple fusing torches 6 located on the torch brackets 8 and 8a. At the same time, the torch brackets 8 and 8a supporting the multiple torches 6 are moved at the same speed (typically 5 to 15mm/s) from the condition shown in Fig. 4 (b) to the condition shown in Fig. 4 (c). By this time, the shaded portion shown in Fig. 4 (c) has been fused along the overall thickness of the rolled steel, forming faces which can be joined together. When fusing is completed, the pinch rollers 4 and 5 holding the rolled steels 1 and 2 are rotated in the directions indicated by arrows in Fig. 1. Consequently, the rolled steels 1 and 2 are driven in such a direction that they come near and then the faces to be jointed are pressed as shown in Fig. 4 (d) so that both the pieces are jointed together. The principle underlying the joint method of this embodiment is explained in Figs. 5 and 6. Because the joint method of this embodiment presses the steel pieces 1,2 together after the fusing torches 6 travel for a specified distance in the width direction, the time passing from fusing to pressing differs depending on a position in the width direction. Fig. 5 explains an example of time passing from fusing to pressing. In the condition in Fig. 5 (a), cutting gas is injected from multiple fusing torches (marked with a - z) to start fusing. The torch brackets 8 and 8a travel in the width direction and when they reach the position shown in Fig. 5 (b), the two pieces are pressed together. Fig. 5 (c) shows the elapsed time after passage of a torch 6, at each position in the width direction. Both the rolled steels 1 and 2 are pressed after a passage time expressed by the line (a - x) inclined at a certain gradient determined by the torch passing speed. Although a following torch will fuse the same place in all the strokes of the torch bracket, the passage time after fusing by the final torch is expressed by the bold line shown in Fig. 5 (c). We have found that, as the passage time from fusing to pressing extends, oxide scale is regenerated to make a joint incomplete. A certain limit time "tc" exists concerning the regrowth of oxide scale and the joint does not always become complete at a portion where the passage time exceeds this limit time. The portions where this limit time "tc" is exceeded are shown by blank (unhatched) parts in Fig. 5 (b). We have also found that, although rolled steels are not required to be jointed together completely in the overall width in rolling at hot finish mill, there may occur an opening at a joint in following finish rolling because an incomplete joint part exists at the side edge of the rolled steel (to the right in Fig. 5(b)) so that stress is concentrated under tension between stands, thereby sometimes leading to a fracture. To prevent this phenomenon, in this embodiment, the torch brackets 8 and 8a, divided in the width direction are designed to pass laterally independently, and able to correspond to any normal variation of width of rolled steel. The relationship between the edge locations of the rolled steels 1,2 and the passing start positions of the fusing torch 6 is thereby adjusted to a condition as shown in Fig. 6 (a), while the relationship between the edges of the rolled steels and the passage termination positions of the fusing torches 6 is adjusted to such a condition shown in Fig. 6 (b). For this adjustment, optimum passing start positions for the torch brackets 8 and 8a as shown in Fig. 6 (a) are calculated according to rolled steel width information stored in the controller 37 and the motors 12/12a are driven according to the result. Consequently, as shown in Fig. 6 (c), the passage time from fusing to pressing at both the side edges of the rolled steel 2 is incorporated within the limit time "tc" so as to prevent the reduction of joint strength at the ends of the rolled steel joint due to regrowth of oxide scale. A typical torch stroke is from 50 to 100mm. Because both the rear end of a leading rolled steel and the front end of a following rolled steel are fused by injection flow from the fusing torches 6, substantially the entire end faces are fused to an appropriate condition for jointing together in a short time to obtain a clean faces to be joined. A uniform, high precision joint can be achieved by a small pressing force to produce a high strength joint. Because the passage time from fusing to pressing at both the edges of the rolled steels 1 and 2 is adjusted not to exceed the limit time of oxide scale regrowth time "tc" when passing multiple fusing torches laterally, regrowth of oxide scale at the end edge of the rolled steel after fusion is restrained to such an extent to make no influence upon jointing together, so that a joint at the end becomes excellent to intensify joint strength. In this way we have been able to avoid rupture of joints of rolled steel pieces in following finish rolling, so that stabilized continuous rolling is enabled and yield rate is improved. We were able in trials to make a good quality rolled steel. A further embodiment of the joint apparatus of this invention is explained with reference to Fig. 7. In this embodiment, as the previous embodiment, an adjustable cylinder 25 is provided to adjust the distance between two torch brackets 8 and 8a instead of moving the torch brackets 8 and 8a independently in their fusing stroke. With the distance between the two torch brackets 8 and 8a initially determined by the cylinder, the combined torch brackets are then moved so as to take the same procedure as the previous embodiment in fusing, pressing and jointing together. This embodiment has an advantage in that only a pair of drive mechanisms for moving the combined torch brackets, including the crank shafts 10/10a, bearings 11/11a and motors 12/12a can satisfy the requirement for moving the system. Referring to Fig. 8, still another embodiment of this invention is explained. In this embodiment, side guides 33,34 for guiding a preceding steel 1 and following steel 2 are installed in addition to the configuration of the embodiment shown in Fig. 1. They centre the preceding and following steels 1 and 2 so as to determine the relationship between the positions of the torch brackets 8,8a at the start of their fusing strokes and the side edges of the rolled steels. The steps for joining together shown in Fig. 8 (a) / (b) are the same as Fig. 4. If either rolled steel piece 1 or 2 deviates from the center of the path in the width direction, an optimum passing start position as explained in Fig. 6 can be set by centering the steel by means of the side guides 33 and 34. A further embodiment of the joint apparatus of this invention is explained referring to Figs. 9 and 10. In this embodiment, in addition to the configuration of the embodiment shown in Fig. 1, position detectors 35,36 for detecting the lateral positions of a preceding steel 1 and following steel 2 are mounted across the processing path upstream and downstream of the fusing torches 6. They are connected to the controller 37 which receives their detection signals. Suitable detectors are known per se for use in rolling mills. A common type has an elongate light emitter on one face of the path, opposing a series of detectors over the other face. The controller 37 calculates optimum passing start positions of the torch brackets 8 and 8a according to the position information of rolled steels detected by the position detectors 35,36, and controls the motors 12 and 12a accordingly. Consequently when the widths of the rolled steels 1 and 2 change, as well as when they deviate from the center of the path in their width direction, the controller can automatically adjust the passing start positions of the torch brackets 8 and 8a so as still to determine an optimum position such as shown in Fig. 6. The steps for jointing together (a) (d) shown in Fig. 10 are the same as Fig. 4. A still further embodiment of this invention is explained referring to Figs. 9 and 11. In previous embodiments the passing start positions of the torch brackets 8 and 8a are adjusted so that the passage time from fusing to pressing does not exceed the limit time "tc" regardless of the width and position of the rolled steels 1,2. In this embodiment, the passing start positions of the torch brackets 8 and 8a are not adjusted, but instead, the respective passing speeds Va and Vz of the torch brackets 8 and 8a are adjusted so that the passing termination position becomes an optimum position for joining together. Namely, although the passing start positions in Fig. 11 (a) are the same as Fig. 5 (a), the passing termination position in Fig. 11 (b) is the same as Fig. 6 (b), and as expressed by t a and t z in Fig. 11, the passing speed Va of the torch bracket 8 is made slower than the passing speed Vz of the torch bracket 8a just before the passing termination position at latest, to deviate the termination position. In this adjustment, the controller 37 calculates the passing speed Vz according to the position information of the rolled steels detected by the position detectors 35 and 36 so as to obtain optimum passing termination positions of the torch brackets 8 and 8a and control the motors 12 and 12a. This embodiment has an effect of reducing the overall cycle time because the adjustment of the passing start positions of the torch brackets 8 and 8a before start of fusing can be omitted.

Claims: A method of joining consecutive pieces (1,2) of steel passing through a hot rolling mill, in which multiple fusing torches (6) are moved across the mill processing path in a fusing movement at the meeting between the adjacent ends of the pieces (1,2) to cause fusing of at least one said end, and the pieces (1,2) are then pressed together longitudinally to join them, wherein the multiple fusing torches (6) are provided as plural sets (8,8a) each including at least one torch (6), a first said set to fuse at one lateral extremity of the join and a second said set to fuse at the other lateral extremity of the join; the side edge locations of the steel pieces (1,2) are determined; on the basis of the determined edge locations, a controlled adjusting movement of the first and second torch sets (8,8a) is made, being a relative movement between them in a lateral direction, to keep the time between fusing of the steel at the lateral extremities of the join, as a result of the lateral fusing movement of the torches (6), and said pressing together of the steel pieces (1,2), below a predetermined limit time for regrowth of oxide scale after fusing. A method according to claim 1 in which each of the first and second torch sets has at least three torches (6). A method according to claim 1 or claim 2 in which said first and second torch sets (8,8a) move concurrently in the same lateral direction during their fusing movement. A method according to any one of the preceding claims in which said controlled adjusting movement comprises selecting independent respective starting positions for the fusing movements of said first and second torch sets (8,8a). A method according to any one of claims 1 to 4 in which said controlled adjusting movement comprises selecting independent respective speeds for the fusing movements of said first and second torch sets (8,8a). A method according to any one of the preceding claims in which the steel side edge locations are determined by detecting their positions using position detectors (35,36). A method according to any one of the preceding claims in which the steel side edge locations are determined by positioning the steel using side guides (33,34). A method of processing steel, comprising forming steel pieces, rough-rolling the pieces, and finish-rolling the rough-rolled pieces, in which consecutive pieces are joined by a method according to any one of claims 1 to 7 either before the rough-rolling or between the rough-rolling and the finish-rolling. A method according to claim 8, further comprising cooling, shearing and winding the joined steel after the finish-rolling. Apparatus for joining consecutive pieces of steel in a hot rolling mill, comprising first and second torch sets (8,8a) each comprising at least one fusing torch (6), disposed laterally across a processing path of the hot rolling mill for fusing at least respective lateral portions of end edges of steel pieces thereon in use; an adjustable connector (25) linking the first and second sets of fusing torches (6); means for adjusting the length of said connector to vary the spacing between said sets, and means for moving said linked sets (8,8a) together in the same direction in a lateral fusing movement. Apparatus for joining consecutive pieces of steel in a hot rolling mill, comprising first and second torch sets (8,8a) each comprising at least one fusing torch (6), disposed laterally across a processing path of the hot rolling mill for fusing at least respective lateral portions of end edges of steel pieces thereon in use; and respective adjustable drive means for moving the first and second torch sets (8,8a) concurrently, at independently selectable different respective speeds, in respective lateral fusing movements. Apparatus according to claim 10 or claim 11 comprising side guides (33,34) disposed at the sides of the processing path, to determine the width centres of two successive steel pieces thereon in use. Apparatus according to any one of claims 10 to 12 comprising position detection means (35,36) for detecting the lateral edge locations of steel pieces on the processing path in use. A hot-rolling mill comprising joining apparatus according to any one of claims 10 to 13. A hot-rolling mill according to claim 14 in which the joining apparatus is between a heating furnace (52) and a rough-rolling stage (53), or between a rough-rolling stage (53) and a finish-rolling stage (54).

Inventors: KINOSE RYOHEI, SEKIYA TERUO, YOSHIMURA YASUTSUGU, KINOSE, RYOHEI, SEKIYA, TERUO, YOSHIMURA, YASUTSUGU
Applicants: HITACHI LTD, HITACHI, LTD.
Application year: 1992
Main classification: B23K20
IPC codes: B23K5, B21B15, B21B1, B23K7, B23K20, B23K101, B23K37