Glass-aluminum nitride composite material

Abstract: A glass-aluminum nitride composite comprising a sintered body is produced by adding glass powder to aluminum nitride grains having an oxygen content of less than 2% and a mean grain diameter of 1.0 µm or more and subjecting the mixture to molding and sintering. A suitable glass is one based on borosilicate and the addition of an AlN whisker serves to improve the strength. The composite material of the present invention has a high heat conductivity, a low permittivity and a high strength and is suitable as a semiconductor packaging material.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a glass-aluminum nitride composite having a high heat conductivity, particularly a glass-aluminum nitride composite having properties suitable for a semiconductor packaging material. 2. Description of the Prior Art An increase in the speed of electronics elements and an increase in the integration density have been rapidly advanced. This has led to a severer demand for an insulating substrate on which the elements are mounted and packaging material. A high heat conductivity for coping with an increase in the density of heat buildup, a low dielectric constant for coping with an increase in the speed, and a lowering in the conductor resistance are particularly required of the packaging material. Regarding the highly heat conductive material, development has been made on an AlN material in addition to BeO and SiC. On the other hand, the demand for a lowering in the dielectric constant and a lowering in the conductor resistance cannot be satisfied by the highly heat conductive material, and priority has been given to the development of a glass-ceramic composite material. In the glass-ceramic composite material, both the heat conductivity and the mechanical strengths are so low that no satisfactory properties are obtained. For this reason, in order to meet the demand, studies have been made on a composite material comprising glass and a highly heat conductive powder. For example, Japanese Patent Laid-Open No. 210043/1988 disclosed a composite comprising glass and aluminum nitride powder. This composite has a permittivity of 5 to 7 and a heat conductivity of 20 W/m·K. Further, in Japanese Patent Laid-Open Nos. 221162/1990 and 196073/1990, corresponding to EP-A-0 374 825, a further slight improvement in the heat conductivity could be attained by specifying the oxygen content in aluminum nitride. The above-described conventional glass-aluminum nitride composite is still unsatisfactory not only in the improvement in the heat conductivity but also in the strength of the substrate, and the improvement achieved therewith is at the most that of the performance of the conventional low temperature fired substrate, so that this composite cannot satisfy a further advanced property requirement. In the present invention, the heat conductivity is further improved particularly in a glass composite having a low permittivity and a high heat conductivity and provides a material having a high strength besides the above-described properties. SUMMARY OF THE INVENTION The present invention relates to a glass-aluminum nitride composite material comprising a sintered body produced by adding glass powder to aluminum nitride grains having an oxygen content of less than 2% by weight and a mean grain diameter of 1.0 µm or more and subjecting the mixture to molding and sintering, the glass-aluminum nitride composite material having a heat conductivity of 30 W/m·K or more and the content of AlN is 50 to 95% by weight based on the whole composite material. The glass powder preferably comprises 30 to 60 wt.% of SiO₂, 10 to 30 wt.% of Al₂O₃, 10 to 30 wt.% of B₂O₃ and 30 wt.% of MO (wherein M represents Mg, Ca or Sr). The addition of an amount of AlN whiskers thereto contributes to a further improvement in the strength. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The AlN grain used in the present invention is required to have an oxygen content of less than 2% by weight. When the oxygen content is 2 wt.% more, the heat conductivity of the composite is so insufficient that effect attained by compositing AlN becomes small. The mean grain diameter is 1.0 µm or more. When it is less than 1.0 µm, the lowering in the heat conductivity is significant due to the diffusion of an element from the matrix glass, so that it is necessary to use a raw material having an at least given grain diameter. The lower the oxygen content, the better the results. In particular, a good heat conductivity can be obtained when the oxygen content is 0.4% by weight or less. When the grain diameter exceeds 10.0 µm, no surface accuracy after sintering can be ensured Further, it is possible to incorporate an amount of AlN whiskers for the purpose of increasing the strength of the composite. For example, it is useful to add an amount of AlN whiskers having a minor diameter of 0.3 µm and a length of about 5 µm in an amount of 5% by volume. The glass powder having the above-described composition constituting the glass matrix is the powder of a known borosilicate glass which is preferred from the viewpoint of sintering temperature, permittivity, etc. The composition is regulated in the above-described range to regulate the sintering temperature. Further, use may be made of a paste having a low electric resistance, such as Ag, Au or Cu, and simultaneous firing can be conducted to from a conductive circuit. Further, it is also possible to regulate the permittivity. Example 1: Each of the AlN samples having properties specified in Table 1 and glass powder (having a composition consisting of 50 wt.% of SiO₂, 15 wt.% of Al₂O₃, 20 wt.% of B₂O₃ and 15 wt.% of CaO) were mixed with an organic binder, etc., in a ball mill according to the formulation specified in the Table to prepare a slurry. The slurry was molded into a tape and fired in a nitrogen stream at 900°C. The resultant glass-aluminum nitride composite had a high heat conductivity as given in Table 2. It was possible to provide internal wiring and lamination before the firing. Further, it was also possible to bake a paste of metal, such as Au, Ag or Cu, in the surface of the sintered body. These render the composite useful as an electrical wiring board. No. Properties of AlN AlN content (wt.%) oxygen content (wt.%) mean grain diameter (µm) 1 0.3 1.5 65 2 0.8 1.5 65 3 1.5 1.5 65 4 2.5 1.5 65 5 1.5 0.5 65 6 1.5 2.5 65 7 1.5 1.5 80 8 1.5 1.5 60 9 1.5 1.5 40 10 0.3 2.0 60 11 0.4 2.0 60 12 0.5 2.0 60 13 0.8 2.0 60 14 AlN sintered body No. Volume specific resistance Ω·cm Heat conductivity W/m·K Relative permittivity Bending strength kg/mm² 1 >10¹³ 35 5.0 25 2 do. 45 do. do. 3 do. 40 do. do. 4 do. 10 do. do. 5 do. 12 do. 20 6 do. 45 do. 25 7 do. 50 5.5 do. 8 do. 35 5.0 do. 9 do. 15 4.5 20 10 do. 50 5.0 25 11 do. do. do. do. 12 do. 45 do. do. 13 do. 40 do. do. 14 do. 180 8.0 35 Example 2: A sintered body was prepared in the same manner as that of sample No. 3 of the Example 1, except that 5% by weight, based on the total weight of the glass and the ceramic component, of an amount of AlN whiskers (major diameter: 10 µm, minor diameter: 0.4 µm, transparent) was further added to the slurry. The resultant sintered body had a bending strength of 40 kg/mm², and no deterioration was observed in the volume specific resistance, heat conductivity and relative permittivity. According to the present invention, it is possible to provide a material having a high heat conductivity, a low permittivity and a high strength. This material is suitable for use in a semiconductor packaging material.

Claims: A glass-aluminum nitride composite material comprising a sintered body produced by adding glass powder to aluminum nitride grains having an oxygen content of less than 2% by weight and a mean grain diameter of 1.0 µm or more, mixing the glass powder and the AlN grains preferably with a binder, and subjecting the mixture to molding and sintering, said glass-aluminum nitride composite having a heat conductivity of 30 W/m.K or more and the content of AlN is 50 to 95% by weight based on the whole composite material. A glass-aluminum nitride composite material according to claim 1, wherein the glass powder consisting of 30 to 60% (% by weight; the same shall apply hereinafter) of SiO₂, 10 to 30% of Al₂O₃, 10 to 30% of B₂O₃ and 30% or less of MO (wherein M represents Mg, Ca or Sr) A glass-aluminum nitride composite material according to claims 1 or 2, whereto an amount of AlN whiskers is further added. A glass-aluminum nitride composite material according to any of claims 1 to 3, wherein the oxygen content of the AlN grains is less than 0.5 % by weight. A glass-aluminum nitride composite material according to any of claims 1 to 4, wherein the grain diameter is 1.0 to 10.0 µm. A glass-aluminum nitride composite material according to any of claims 3 to 5, wherein the AlN whiskers have a diameter of about 0.3 µm and a length of about 5 µm and are added in an amount of 5% by volume.

Inventors: SOGABE KOICHI C O ITAMI WORKS, YAMAKAWA AKIRA C O ITAMI WORKS, SOGABE, KOICHI, C/O ITAMI WORKS OF SUMITOMO ELEC., YAMAKAWA, AKIRA, C/O ITAMI WORKS OF SUMITOMO ELEC.
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1992
Main classification: C03C14
IPC codes: C04B35, C03C14, H01L23