Fabrication of defect free silicon on an insulating substrate

Abstract: A method for fabricating silicon on insulator structures having a dislocation free silicon layer. The method utilizes low temperature UHVCVD to deposit a very heavily doped etch stop layer (12) having a very steep doping profile onto a substrate (10) and a lightly doped active layer (14) onto the etch stop layer. An insulator (16) is formed on the active layer and a carrier wafer (18) is formed on the insulator layer. The original substrate is removed in a first etch and the etch stop layer is removed in a second etch resulting in a thin, uniform active layer. In one embodiment, a small percentage of germanium is added to the etch stop layer to produce a defect free epitaxial active layer.

Description: The present invention relates to silicon on insulator structures and more particularly to a method for fabricating such structures with a defect free silicon active area. Those skilled in the art have long recognized the desirability of silicon-on-insulator structures for fabricating semiconductor devices. The resulting circuit and device isolation can eliminate latchup problems and reduce soft errors from alpha particles (or other ionizing radiation) while reducing intrinsic and parasitic capacitance. During the past several years, there has been an increase in efforts to improve the electronic quality of silicon on insulator (SOI) structures for VLSI applications. One method of fabricating such a device comprises forming a silicon layer above an existing oxide layer. Examples are laser or strip heater recrystallization and selective epitaxial methods. Generally, the quality of the silicon layer is inferior to that normally associated with silicon processing. A second technique in fabricating SOI structures comprises forming an oxide layer beneath an existing high quality silicon layer. Examples are oxidized porous silicon and oxygen ion implantation. Generally these methods result in an inferior oxide and the quality of the SOI may be degraded during oxide formation. Another technique for forming silicon on insulator structures is disclosed by Lasky et al. IEDM Technical Digest, page 684 (1985). The Lasky et al. process as shown in Figure 1, comprises growing a lightly doped epitaxial layer 2 on a heavily doped substrate 4 and growing a thermal oxide 6 on the lightly doped layer 2. Thereafter, a lightly doped carrier wafer 8 is bonded to the oxide layer 6. A preferential etch is used to remove the heavily doped substrate 4 leaving the thin lightly doped epitaxial layer above the thermally growing oxide layer. The Lasky et al. process and variations thereof have not been actively integrated into commercial device manufacturing because of the difficulty in achieving thickness uniformity over the wafer surface and problems in obtaining thin layers of controlled doping profile. These problems are partly due to the wide doping gradient which characterizes the etch stop region and the stress produced at the epitaxial layer-substrate interface. The stress produces defects in a resultant thin active area. Thus, there is a need to reduce defects and improve the thickness control in the fabrication of thin silicon layers on an insulating substrate. The present invention is directed to a method for making high quality silicon on insulator structures according to claim 1. The method of the present invention utilizes the advantages of thin epitaxial films produced by ultra high vacuum chemical vapor deposition (UHVCVD) to enable the formation of SOI layers without the problems previously encountered. UHVCVD is a low temperature process that allows the formation of layers with very high doping, approximately 10 21 cm -3 or greater and very steep doping profiles, approximately 1 nm per decade of a dopant concentration. In accordance with the method of the present invention, a very heavily doped etch stop layer of silicon is formed on a lightly doped silicon substrate. A lightly doped active layer of silicon is then formed on the etch stop layer. Both the very heavily doped etch stop layer and the lightly doped active layer are formed by UHVCVD. An insulator layer is then formed on the active layer and a carrier substrate is bonded to the insulator layer either by growing a layer of polysilicon to substrate thickness or using bonding layers to attach a wafer. Thereafter, the silicon substrate is removed in a first etch with the heavily doped layer acting as an etch stop during this step. Subsequently, the etch stop layer is removed in a second etch resulting in the SOI structure. The use of UHVCVD allows the etch stop layer to be very heavily doped. In addition, UHVCVD allows the etch stop layer to be very thin due to the extreme sharpness of the gradient of the doping level in the layer. Thus, an ideal, uniform etch stop layer is provided resulting in a much improved control of the thickness of the active layer of the SOI structure. In addition, the use of UHVCVD permits germanium to be added to the etch stop layer in order to create stress free layers by compensating for the stress that would otherwise normally occur due to the high doping levels in this layer. In turn, the stress at the interface between the heavily doped etch stop layer and the lightly doped active layer is compensated, resulting in a final active device layer which can be very thin while being dislocation free. Figure 1 is a cross-sectional view of an intermediate step in the fabrication of a silicon on insulator structure in accordance with a prior art method. Figures 2-7 are cross-sectional views of various steps in the method of fabrication of the silicon on insulator structures in accordance with the present invention. Figure 8 is a cross-sectional view showing a bonding step in the formation of the silicon on insulator structures of the present invention. Figure 9 is another embodiment of the bonding step in the formation of the silicon on insulator structures of the present invention. Figure 10 is a graph showing the doping profile of the active layer formed by UHVCVD of the SOI of the present invention. In the following description of the invention, specific p and n conductivity type materials and regions are indicated. These indications are by way of example and shall not be deemed to limit the teachings of the present invention. It will be understood that devices having opposite p and n arrangements are considered equivalent in all pertinent respects to the structures described herein. In addition, well known lithographic masking, patterning and etching steps are employed in the method of fabrication and are therefore not described in detail herein. Turning now to Figures 2-7, there is shown in Figure 2 a lightly doped substrate 10 on which is epitaxially deposited a heavily doped layer 12 by UHVCVD. The UHVCVD process used herein is described in detail by Meyerson et al., Appl. Phys. Lett., Vol. 50, No. 2, pp. 113-115 (1987), said article being incorporated herein by reference. As will be described in more detail below, the UHVCVD process employed herein permits layer 12 to be very heavily doped in the range of 10 21 cm -3 or greater and with an extremely abrupt gradient. As shown in Figure 3, a lightly doped layer 14 of silicon is then grown by UHVCVD on layer 12. The UHVCVD process permits layers to be grown with small concentrations of germanium added. In the fabrication of the SOI structures of the present invention, it is advantageous to provide layer 12 with germanium added in order to compensate for the stress normally induced by the high level of dopant introduced into layer 12. Typically, about 2% Ge is needed to compensate for the strain. In addition, active layer 14 is also deposited with germanium added. As shown in Figure 4, an insulator layer 16 is then formed on the lightly doped layer 14. The insulator layer 16 may be a typical insulating material such as a silicon oxide or a silicon nitride. For example, layer 16 may be silicon dioxide deposited by plasma enhanced chemical vapor deposition (PECVD). It is important that this process be carried out at moderately low temperatures in order to avoid significant diffusion of impurities from layer 12, which would destroy the sharp doping gradient. Alternatively, all or portions of layer 16 may be thermally grown oxide. As shown in Figure 5, a carrier wafer 18 is formed on the insulator layer 16. The carrier wafer 18 may be comprised of a layer of polysilicon deposited by PECVD. Alternatively, the carrier wafer 18 may be a separate structure that is bonded to the insulator layer 16 by any suitable bonding technique. Examples of several bonding techniques will be described hereinafter. After the carrier wafer 18 is formed on the insulator layer 16, the structure is inverted as shown in Figure 6 and the original substrate 10 is removed by etching, or a combination of mechanical grinding followed by etching. For greatest accuracy, the last step in this removal process should use a preferential etch solution such as KOH which will stop etching at the interface to the heavily doped layer 12. Layer 12 is an excellent etch stop because of its high doping concentration which occurs abruptly at the interface. Thereafter, as shown in Figure 7, the etch stop layer 12 is removed using a preferential etch solution such as a mixture of HF/nitric acid/acetic acid in a ratio of 1:3:8 by volume. This solution will etch the heavily doped layer 12 with a high etch rate and thereafter will remove only a small portion of layer 14 because the lighter doped layer 14 is etched at a much slower rate. Layer 12 can be etched away cleanly and uniformly because of its sharp doping gradient. The abrupt doping profile allows layer 12 to be made very thin, so that the etch time to remove it can be made small. The underlying layer 14 is then subjected to this etch process for a short time after layer 12 is removed. This results in layer 14 having a uniform thickness and a smooth planar surface 20 so that layer 14 can be made very thin, for example on the order of 50 nm (500 angstrom). The uniformity of layer 14 is much improved over that found in the Lasky et al. structure of Figure 1 which does not have an etch stop layer between the substrate 4 and active layer 2. As shown in Figure 7, the resulting structure is a silicon on insulator structure comprised of active silicon layer 14 and insulator layer 16 on a carrier wafer 18. Layer 14 can then be used as a template for the deposition of subsequent epitaxial layers required in forming various devices. Examples of various structures that can be formed include lateral bipolar transistors and field effect devices. In addition, a series of thin silicon layers can also be deposited to form superlattice structures. As mentioned above, the carrier wafer may be bonded to the oxide layer 16 by any suitable technique. One embodiment for bonding as shown in Figure 8 is to deposit a layer of polysilicon 22 on the insulator 16 as a thin layer, approximately 25 µm (one mil), and to coat the polysilicon layer with a thin layer of germanium 24. The carrier wafer 18 is comprised of silicon and is also coated with a thin layer of germanium 26. The two germanium layers 24 and 26 are then placed in contact with each other and the structures are exposed to temperatures sufficient to bond the wafer 18 to the insulator 16. The temperatures must be sufficient to melt the germanium to form a weld-like bond. However, the time of exposure or the temperature must not be such as to adversely affect the doping profile of layer 12. Alternatively, the germanium layer 24 could be left out so that the germanium layer 26 could bond directly to polysilicon layer 22 by interdiffusion. An alternative embodiment is shown in Figure 9 in which the carrier wafer may be a glass ceramic substrate. The glass ceramic substrate should have the same expansion coefficient as silicon. Examples of such glass ceramic materials are cordierite and mullite. Bonding agents would be silicon dioxide or glass layers deposited on both surfaces by the sol-gel or spray pyrolysis techniques where particle size is small and sintering temperature is low. Sol-gel layers 28 and 30 are deposited onto the insulator layer 16 and glass ceramic substrate 18 respectively, the sol-gel layers are placed in contact and the structure is sintered causing the sol-gel to bond the substrate 18 to the insulator 16. The UHVCVD process utilized in the method of the present invention is a low temperature process that permits very thin layers to be deposited with uniform thickness and very heavy doping, with a very sharp doping profile. For example, the heavily doped etch stop layer 12 may be deposited to a thickness of about 200 nm (about 2,000 angstroms) with an abrupt doping profile as that shown in Figure 10 and with a doping level of 10 21 cm -3 or greater. The active lightly doped layer 14 may be deposited to a thickness of about 100 nm (about 1,000 angstroms) or less and the insulator layer 16 can be deposited to a thickness of about 1000 nm (about 10,000 angstroms). Because of the etch selectivity of the etch stop layer 12, the active silicon layer 14 may be formed to a thickness in the range of 50 to 100 nm (500 to 1,000 angstroms). The UHVCVD process uses temperature of 550°C or less. The low temperature processing avoids interdiffusion of dopants which would reduce the resolution of the selective etching processes. In addition, the UHVCVD process permits germanium to be added to both of the etch stop layer 12 and active layer 14. The addition of a small percentage of germanium to layer 12 will compensate for the stress produced normally by high doping levels. In a preferred embodiment, approximately two percent germanium is added. In turn, the stress at the interface between the etch stop layer 12 and active layer 14 is compensated resulting in a final active layer 14 which can be very thin while being dislocation free. For example, a 200 nm (2,000 angstrom) etch stop layer 12, containing 2% germanium and a doping level of boron about 10 21 cm -3 , and an active layer 14 having a doping level of about 10 17 cm -3 and a thickness of 100 nm (1,000 angstroms), the dislocation level of the active layer would be ≤10 2 and the thickness uniformity of layer 14 would be ±5%. Various structures can be formed using epitaxial SiGe for active layer 14. The amount of germanium added to layer 14 will depend on the device application, but will typically be between 10 and 20% for most applications. In addition, layer 14 could include SiGe quantum wells in order to utilize the epitaxial layer for optical electronic structures such as waveguides and modulators. SiGe channels can also be formed in the active layer 14 to make HEMT type devices.

Claims: Method of forming a silicon on insulator structure comprising the steps of: forming an etch stop layer (12) of silicon doped to an extent of 10 21 cm 3 or greater on a silicon substrate (10) by means of UHVCVD; forming an active layer (14) of lightly doped silicon on said etch stop layer by means of UHVCVD; said etch stop layer and said active layer each including about 2 percent germanium; forming an insulator layer (16) on said active layer; forming a carrier substrate (18) on said insulator layer; removing said silicon substrate (10); and removing said etch stop layer (12). The method of claim 1 wherein said step of forming a carrier substrate on said insulator layer includes bonding a carrier wafer to said insulator layer, wherein said bonding step includes forming a layer of polysilicon on said insulator layer, forming a layer of germanium on said polysilicon layer, forming a layer of germanium on a silicon wafer, contracting the germanium layers and exposing said layers to temperatures sufficient to bond the carrier substrate to said insulator layer. The method of claim 1 wherein said carrier substrate is comprised of polysilicon and said forming step includes depositing said polysilicon by PECVD. The method of claim 1 wherein said carrier substrate is a glass ceramic material and said forming step includes bonding said glass ceramic material by bonding agents such as silicon dioxide or glass layers deposited on both surfaces by the sol-gel or spray pyrolysis techniques. The method of any one of claims 1 to 4 wherein said etch stop layer and said active layer are formed by epitaxially growing silicon including about 2% germanium. The method of any one of the preceding claims wherein said insulator layer is one of silicon oxide and a silicon nitride. The method of claim 6 wherein said insulator layer is formed by depositing an insulator material by PECVD, or by thermal oxidation.

Inventors: DENNARD ROBERT H, MEYERSON BERNARD S, ROSENBERG ROBERT, DENNARD, ROBERT H., MEYERSON, BERNARD S, ROSENBERG, ROBERT, MEYERSON, BERNARD S,
Applicants: IBM, INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1992
Main classification: H01L21
IPC codes: C30B29, H01L21, H01L27, C30B25