Method of imparting light resistance and ultraviolet-screening action to fibrous article

Abstract: A durable light resistance and UV-screening action is imparted to a fibrous article by coating the fibrous article with a polymer comprising units derived from at least one monomer selected from those which are represented by the formulae (1) and (2): wherein R is H or CH 3 and X is -O-, -OCH 2 CH 2 O- or -OCH 2 CH(CH 3 )O-, wherein Y is halogen or CH 3 , n is 1 or 2, R 1 is C1-6 hydrocarbyl, m is 1 or 2, R 2 is C1-6 alkylene and R 3 is H or CH 3 .

Description: This invention relates to a method of imparting a light resistance and an ultraviolet-screening action to a fibrous article. Most fibrous articles such as clothes including sports wears, beach umbrellas and curtains are exposed to sunlight in the outdoors. Therefore, the fibers of these articles deteriorate and the dyed fibrous articles discolor due to ultraviolet light. Furthermore, the skin gets sunburn and furnishings are discolored by ultraviolet light transmitted through the fibrous articles. To protect fibrous articles from photo-degradation and dyed fibrous articles from color fading, an ultraviolet absorber is adsorbed in the fibers. As the ultraviolet absorbers used, there can be mentioned 2-hydroxybenzophenones such as 2,4-dihydroxybenzophenone, 2,2',4,4'-tetrahydroxybenzopheneone and 2-hydroxy-4-octoxybenzophenone; and 2-hydroxyphenylbenzotriazoles such as 2-(2'-hydroxy-5'-methylphenyl)benzotriazole, 2-(2'-hydroxy-3'-t-butyl-5'-methylphenyl)-5-chlorobenzotriazole and 2-(2'-hydroxy-3',5'-dibutylphenyl)-5-chlorobenzotriazole. Most known conventional ultraviolet absorbers have a low-molecular-weight and the adsorbed ultraviolet absorbers are dissolved in a laundering bath. Therefore, the ultraviolet screening action does not last over a long period of time. US-A-3629197 discloses solution polymerised copolymers of three species namely a phenolic antioxidant monomer, a UV absorbing monomer such as 4-methacryloyloxy-2-hydroxy benzophenone and an ethylenically unsaturated monomer and application of such materials to fibrous articles. Chemical Abstracts, Vol. 110, No. 8, 1989, Abstract No. 136864g discloses that 2-(2'-hydroxyphenyl)benzotriazole and 2-hydroxybenzophenone groups in polymers impart ultraviolet screening action to such polymers. A primary object of the present invention is to provide a method of imparting a durable light resistance and ultraviolet screening action to fibrous articles. In accordance with the present invention, there is provided a method of imparting a durable light resistance and ultraviolet-screening action to a fibrous article, which comprises coating a fibrous article with an aqueous emulsion of a copolymer as obtained in an emulsion polymerization system, said copolymer being comprised of at least 5% by weight of units derived from at least one monomer selected from monomers represented by the following formulae (1) and (2): wherein R is hydrogen or methyl and X is -O-, -OCH 2 CH 2 O- or wherein Y is halogen or methyl, n is 0, 1 or 2, R 1 is a hydrocarbon group having 1 to 6 carbon atoms, m is 0, 1 or 2, R 2 is a linear or branched chain alkylene group having 1 to 6 carbon atoms and R 3 is hydrogen or methyl, and not more than 95% by weight of units derived from at least one monoethylenically unsaturated monomer selected from acrylic acid, methyacrylic acid, alkyl esters of acrylic acid having 1 to 18 carbon atoms in the alkyl group, alkyl esters of methacrylic acid having 1 to 18 carbon atoms in the alkyl group, alkyl vinyl ethers having 1 to 8 carbon atoms in the alkyl group, and vinyl esters of carboxylic acids having 2 to 18 carbon atoms. Figure 1 is a spectral transmission curve of a fibrous article, which has been treated by the method of the present invention. As typical examples of the monomers represented by the formula (1), there can be mentioned 2-hydroxy-4-acryloyloxybenzophenone, 2-hydroxy-4-methacryloyloxybenzophenone, 2-hydroxy-4-(2-acryloyloxy) ethoxybenzophenone, 2-hydroxy-4-(2-methacryloyloxy)ethoxybenzophenone, 2- hydroxy-4-(2-methyl-2-acryloyloxy)ethoxybenzophenone and 2-hydroxy-4-(2-methyl-2-methacryloyloxy)ethoxybenzophenone. As typical examples of the monomers represented by the formula (2), there can be mentioned 2- [2'-hydroxy-5'-(methacryloyloxyethyl)phenyl]benzotriazole, 2-[2'-hydroxy-5'-(acryloyoxyethyl)phenyl]benzotriazole, 2-[2'-hydroxy-3'-t-butyl-5'-(methacryloyloxyethyl)phenyl]benzotriazole, 2-[2'-hydroxy-3'-methyl-5'-(acryloyloxyethyl)-phenyl]benzotriazole, 2-[2'-hydroxy-5'-(methacryloyloxypropyl)phenyl]-5-chlorobenzotrizole and 2-[2'-hydroxy-5'-(acryloyloxybutyl)phenyl]-5-methylbenzotriazole. The ultraviolet-absorbing polymer used for coating a fibrous article therewith is a copolymer prepared from at least 5% by weight, preferably at least 30% by weight, of at least one of the monomers of the formulae (1) and (2) and not more than 95% by weight, preferably not more than 90% by weight, of the said at least one copolymerizable monoethylenically unsaturated monomer. The alkyl esters of acrylic acid include, for example, methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate and 2-ethylhexyl acrylate. The alkyl esters of methacrylic acid include, for example, methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate and stearyl methacrylate. The alkyl vinyl ethers include, for example, methyl vinyl ether, ethyl vinyl ether, butyl vinyl ether and stearyl vinyl ether. The vinyl carboxylates include, for example, vinyl formate, vinyl acetate, vinyl acrylate, vinyl butyrate, vinyl crotonate and vinyl stearate. The ultraviolet-absorbing polymer used for coating a fibrous article therewith preferably has a weight average molecular weight of about 5,000 to about 1,000,000 more preferably about 10,000 to about 800,000. The polymers to be coated on a fibrous article are prepared in an emulsion polymerization system. The polymerization procedure per se may be conventional. The as-obtained polymer emulsions are used for coating the fibrous articles. It is preferable to effect the emulsion polymerization using an emulsion in water. The fibrous article is coated with the as-obtained polymer emulsion, and a softener and other additives can be incorporated in the polymer emulsion, and consequently, an after-treatment of the fibrous article can be effected simultaneously with the polvmer-coating. The coating with the as-obtained polymer emulsion is usually effected by dipping the fibrous article in the polymer emulsion, and the dipped fibrous article is squeezed and then dried. The fibrous articles treated by the method of the invention are not particularly limited and any articles of woven and knitted fabrics and non-woven fabrics can be treated. As typical examples of the fibrous articles treated by the method of the present invention, there can be mentioned sports wears, curtains and beach umbrellas. The kind of fiber also is not limited and any of natural fibers, synthetic fibers and semi-synthetic fibers can be employed. The coating of a fibrous article can be carried out by a conventional coating procedure such as gravure coating, dip coating or spray coating. The concentration of the ultraviolet-absorbing polymer in the solution or emulsion is not particularly limited, but is preferably 1 to 5% based on the weight of the solution or emulsion. The amount of the ultraviolet-absorbing polymer applied is preferably from 0.1 to 7% by weight o.w.f. The invention will now be described in detail with reference to the following examples that by no means limit the scope of the invention. Example 1 Emulsion Polymerization of 2-Hydroxy-4-(2-methacryloyloxy) ethoxybenzenzophenone with Butyl Acrylate and Acrylic Acid. A pre-emulsion composed of 150 g of 2-hydroxy-4-(2-methacryloyloxy) ethoxybenzophenone, 500 g of butyl acrylate, 10 g of acrylic acid, 25 g of sodium dodecylbenzenesulfonate and 800 g of deionized water was prepared. A separable flask provided with a reflux condenser, a dropping funnel, a thermometer, a nitrogen-gas introducing tube and a stirrer was charged with 100 g of deionized water, 5.2 g of potassium peroxide and 0.5 g of potassium acid sulfite. The temperature of the contents was elevated to 70°C with stirring and the pre-emulsion was added gradually dropwise through the dropping funnel into the flask to effect polymerization. After the completion of the addition, the polymerization was continued further for 3 hours, thus producing a polymer emulsion. Example 2 Emulsion Polymerization of 2-Hydroxy-(2-methacryloyloxy)ethoxybenzenzophenone with Ethyl Acrylate and Acrylic Acid A pre-emulsion composed of 150 g of 2-hydroxy-(2-methacryloyloxy)ethoxybenzophenone, 450 g of ethyl acrylate, 20 g of acrylic acid, 20 g of sodium dodecylbenzenesulfonate, 10 g of an adduct of 1 mole of nonylphenol with 10 moles of ethylene oxide and 900 g of deionized water was prepared. The same separable flask as that used in Example 1 was charged with 200 g of deionized water, 6 g of potassium peroxide and 1 g of sodium acid sulfite, and an emulsion polymerization was effected in the same manner as described in Example 1 and by using the pre-emulsion to produce a polymer emulsion. Example 3 Emulsion Polymerization of 2-[2'-Hydroxy-3'-t-butyl-5'-(methacryloyloxyethyl)phenyl]benzotriazole with 2-Ethylhexyl Acrylate A pre-emulsion composed of 150 g of 2-[2'-hydroxy-3'-t-butyl-5'-(methacryloyloxyethyl)phenyl]benzotriazole, 500 g of 2-ethylhexyl acrylate, 30 g of sodium dodecylbenzenesulfonate and 750 g of deionized water was prepared. The same separable flask as that used in Example 1 was charged with 150 g of deionized water, 5 g of potassium peroxide and 0.7 g of potassium acid sulfite, and an emulsion polymerization was effected in the same manner as described in Example 1 and by using the pre-emulsion to produce a polymer emulsion. Example 4 Emulsion Polymerization of 2-[2'-Hydroxy-5'-(acryloyloxypropyl)phenyl]benzotriazole with Butyl Acrylate and Acrylic Acid A pre-emulsion composed of 200 g of 2-[2'-hydroxy-5'-(acryloyloxypropyl)phenyl]benzotriazole, 600 g of butyl acrylate, 10 g of acrylic acid, 10 g of sodium dodecylbenzenesulfonate and 20 g of an adduct of 1 mole of nonylphenol with 10 moles of ethylene oxide and 1,000 g of deionized water. The same separable flask as that used in Example 1 was charged with 200 g of deionized water, 7.5 g of potassium peroxide and 1.2 g of potassium acid sulfite, and an emulsion polymerization was effected in the same manner as described in Example 1 and by using the pre-emulsion, to produce a polymer emulsion. Comparative Example 1 By using a Mecha-Gaper Grain Mill made by Asada Tekko K.K., 500 g of 2-(2'-hydroxy-3'-t-butyl-5'-methylphenyl)-5-chlorobenzotriazole, 1,500 g of deionized water and 50 g of a condensate of sodium naphthalenesulfonate with formaldehyde were mixed together under agitation for 1 hour to produce an aqueous dispersion of a UV absorber. Comaparative Example 2 An aqueous dispersion of a UV absorber was prepared in the same manner as described in Comparative Example 1 wherein 500 g of 2,2',4,4'-tetrahydroxybenzophenone, 1,500 g of deionized water and 35 g of a condensate of sodium naphthalenesulfonate with formaldehyde were used with all other conditions remaining substantially the same. (1) Evaluation of Light Fastness of Dyed Fiber An acrylic fiber was dyed under the following conditions. Dyestuff: C.I. Basic Yellow 40, 0.3% o.w.f. Acetic Acid: 2.0% o.w.f. Sodium Acetate: 0.5% o.w.f. Catipon LK (leveling agent, supplied by Ipposha Oil Ind.): 1.0% o.w.f. Bath ratio: 1:20 Dyeing temperature & time: 100°C, 30 minutes The polymer emulsions prepared in Examples 1 through 4 and the UV absorber dispersions prepared in Comparative Examples 1 and 2 were diluted to a solid concentration of 2% by weight. The dyed acrylic fiber was dipped in each of the diluted polymer emulsions and UV absorber dispersions, squeezed to a pick-up of 100% by weight, and then dried at 130°C for 5 minutes. Then the light fastness of the dyed acrylic fiber was evaluated according to JIS L-0842. The results are shown in Table 1. Example 1 Example 2 Example 3 Example 4 Comp. Ex. 1 Comp. Ex. 2 Light fastness (Class) 5 4-5 5 4-5 4 2-3 (2) Evaluation of Ultraviolet Screening Action The polymer emulsions prepared in Examples 1, 2 and 4 and the UV absorber dispersions prepared in Comparative Examples 1 and 2 were diluted to a solid concentration of 2% by weight. Cotton muslin and cotton taffeta were dipped in each of the diluted polymer emulsions, and the UV absorber dispersions, squeezed to a pick-up of 100%, and then dried at 100°C for 3 minutes. The ultraviolet transmittances of the thus-treated cotton muslin and cotton taffeta were determined by using an integrating sphere-provided autographic recording spectrophotometer, model U-3210 supplied by Hitachi Ltd. The results are shown in Table 2. The spectral transmission curve of the cotton muslin treated by the polymer emulsion of Example 2 and the spectral transmission curve of the untreated cotton muslin are shown by a dotted line and a solid line, respectively, in Fig. 1. Ultraviolet Transmittance (%) Fibrous article Cotton muslin Cotton taffeta Wave length (nm) 400 330 290 400 330 290 Example 1 27 12 5 30 18 10 Example 2 33 9 5 29 18 11 Example 4 16 10 6 28 16 10 Comp. Ex. 1 29 10 10 37 20 12 Comp. Ex. 2 30 17 10 47 31 10 Control 33 25 13 51 37 15 (3) Evaluation of Ultraviolet Screening Action after Laundering The polymer emulsions prepared in Examples 1, 3 and 4 and the UV absorber dispersions prepared in Comparative Examples 1 and 2 were diluted to a solid concentration of 2% by weight. Cotton taffeta was dipped in each of the diluted polymer solutions and emulsions and the diluted UV absorber dispersions, squeezed to a pick-up of 100% by weight, and then dried at 100°C for 3 minutes. The thus-treated cotton taffeta was cut into a size of 10 cm x 5 cm. The cut taffeta was placed together with 5 g of a powder soap, 100 ml of water and 10 stainless steel balls (SUS 420 J2), in a cylindrical vessel having an inner diameter of 8 cm and a height of 12 cm. A laundering test was conducted according to JIS L-0844, method A-2. The ultraviolet transmissions of the cotton taffeta were measured at a wavelength of 330 nm by the same method as described in the preceding paragraph (2) at the laundering times shown in Table 3. The results are shown in Table 3. Ultraviolet Transmittance after Laundering (%) Laundering times 1 2 3 5 10 20 Example 1 18 18 19 18 18 17 Example 3 16 16 16 16 17 17 Example 4 20 22 21 21 22 22 Comp. Ex. 1 21 29 35 34 36 35 Comp. Ex. 2 30 33 36 36 35 36 Control 36 35 37 34 35 36 The polymeric UV absorbers used in the present invention can be uniformly coated on the entire surface of the fiber. Light is partly reflected on the polymer coating and partly absorbed by the polymer coating, and the light transmitted through the polymer coating is very minor. Therefore, deterioration of fiber and discoloration of colored fiber due to ultraviolet light can be minimized, and sunburn of the skin and discoloration of furnishings can be prevented or minimized. The polymeric UV absorbers firmly adhere to fiber and have a good resistance to laundering, and therefore the UV screening action is durable over a longer period of time.

Claims: A method of imparting a durable light resistance and ultraviolet-screening action to a fibrous article, characterised in that it comprises coating a fibrous article with an aqueous emulsion of a copolymer as obtained in an emulsion polymerization system, said copolymer consisting of monomers represented by the following formulae (1) and (2) and monoethylenically unsaturated monomers selected from acrylic acid, methacrylic acid, alkyl esters of acrylic acid having 1 to 18 carbon atoms in the alkyl group, alkyl esters of methacrylic acid having 1 to 18 carbon atoms in the alkyl group, alkyl vinyl ethers having 1 to 8 carbon atoms in the alkyl group, and vinyl esters of carboxylic acids having 2 to 18 carbon atoms and comprising at least 5% by weight of units derived from the said at least one monomer selected from monomers represented by the following formulae (1) and (2): wherein R is hydrogen or methyl and X is -O-, -OCH 2 CH 2 O- or wherein Y is halogen or methyl, n is 0, 1 or 2, R 1 is a hydrocarbon group having 1 to 6 carbon atoms, m is 0, 1 or 2, R 2 is a linear or branched chain alkylene group having 1 to 6 carbon atoms and R 3 is hydrogen or methyl, and not more than 95% by weight of units derived from at least one of the said monoethylenically unsaturated monomers. A method as claimed in claim 1, characterised in that the said copolymer has a weight-average molecular weight of 5,000 to 1,000,000. A method as claimed in claim 1 or 2, characterised in that the said aqueous emulsion contains 1 to 5% by weight of the copolymer. A method as claimed in any one of claims 1 to 3, characterised in that the amount of the copolymer is 0.1 to 7% by weight based on the weight of the fibrous article.

Inventors: KASHIWAI KAZUTO, KUMAGAE SHINICHI, YAMAMOTO TAKAICHI, KASHIWAI, KAZUTO, KUMAGAE, SHINICHI, YAMAMOTO, TAKAICHI
Applicants: IPPOSHA OIL IND CO LTD, IPPOSHA OIL INDUSTRIES CO. LTD.
Application year: 1992
Main classification: D06M15
IPC codes: D06M15, D06P1