Silver halide photographic light-sensitive material

Abstract: A method of manufacturing silver halide photographic light-sensitive material with little habitual curling is disclosed. The material, after being coated with a silver halide emulsion layer and antistatic layer on the polyester support, is rolled around a core with its emulsion side facing outside, and then heated at the temperature not less than 30°C. After the heat-treatment, the material is cut and re-rolled on a commercial size core with its emulsion side facing inside.

Description: FIELD OF THE INVENTION The present invention relates to a silver halide photographic light-sensitive material for film-making process, more specifically a photographic light-sensitive material for film-making process with little habitual curling. BACKGROUND OF THE INVENTION In the printing film-making industry, two types of films are used, namely roll films comprising a long sheet of film rolled around a core and sheet films comprising a sheet of film cut into a given size. Roll films are more commonly used because of their advantages such as easy handling and low price. However, such roll films tend to have habitual curling due to film rolling, which poses a problem of poor handling property in sheet use, demanding improvement. To solve the problem of habitual curling after development, some methods have been proposed, including the method of Japanese O.P.I. Publication No. 244446/1989, which uses a film of copolymerized polyester comprising an aromatic dicarboxylic acid having a metal sulfonate. However against the habitual curling in unprocessed films, there is no effective measure. DE-A-2 514 352 discloses a method for producing thermo-plastic films which exhibit reduced curling. The films are heated, to a temperature range between 30 degrees Celsius and a temperature of 5 degrees Celsius below the glass transition temperature of the thermo-plastic material. The temperatures involved lie in the range 60 to 95 degrees Celsius. OBJECT OF THE INVENTION The object of the present invention is to provide a silver halide photographic light-sensitive material with little habitual curling in unprocessed films. According to the present invention there is a provided a method of manufacturing a silver halide photographic light-sensitive material, the material comprising a polyester support carrying a first hydrophilic layer comprising a silver halide emulsion layer on a first surface of the support, and a second hydrophilic layer comprising an anti-static layer on a second surface of the support, the method comprising the steps of: (a) coating the first hydrophilic layer and the second hydrophilic layer on to the polyester support; (b) drying the coated layers to complete a light-sensitive film; thereafter (c) winding the film on to a first core, the silver halide emulsion layer coated side facing outwardly; (d) heating the wound film at a temperature of 30 to 55 degrees Celcius and at an absolute humidity of not more than 1 per cent, for not less than 12 hours; (e) removing the film from the first core and cutting the film; and thereafter (f) winding the cut film on to a second core, the silver halide layer coated side facing inwardly, characterised in that each of the first hydrophilic layer and the second hydrophilic layer contains gelatin in an amount not more than 2.5 grams per square metre. The amount of hydrophilic colloid layer gelatin coated on the inner side of the polyester support is preferably not more than 2.5 g/m 2 for both faces of the support. DETAILED DESCRIPTION OF THE INVENTION The present invention is hereinafter described in detail. Although the antistatic layer for the present invention is not subject to limitation, it preferably comprises hydrophilic colloid with a metal oxide or a reaction product of a water-soluble polymer, a hydrophobic polymer latex and a hardener. The water-soluble electroconductive polymer has at least one electroconductive group selected from sulfonic acid groups, sulfuric ester groups, quaternary ammonium salts, tertiary ammonium salts and carboxyl groups. The electroconductive group should be present at not less than 5% by weight per polymer molecule. The water-soluble electroconductive polymer may contain a hydroxyl group, amino group, epoxy group, aziridine group, active methine group, sulfinic acid group, aldehyde group and vinylsulfone group. The number-average molecular weight of the polymer is 3000 to 100000, preferably 3500 to 50000. Examples of water-soluble electroconductive polymer compounds include A-1 through A-21 given in Japanese Patent Application No. 146629/1990, pp. 6-11 Japanese Patent O.P.I. Publication 4/39651/1992. Typical examples thereof are given below, which are not to be construed as limitative. With respect to P-1 through P-10, Mn is the average molecular weight (average molecular weight means number-average molecular weight in the present specification) as determined by GPC and expressed as polyethylene glycol. The hydrophobic polymer latex contained in the water-soluble electroconductive polymer layer is substantially insoluble in water. The hydrophobic polymer latex is obtained by polymerizing any combination of monomers selected from styrene, styrene derivatives, alkyl acrylates, alkyl methacrylates, olefin derivatives, halogenated ethylene derivatives, vinyl ester derivatives and acrylonitrile, with preference given to those containing at least 30 mol%, more preferably not less than 50 mol% of a styrene derivative, alkyl acrylate or alkyl methacrylate. Examples of such hydrophobic latexes include L-1 through L-26 given in Japanese Patent Application No. 146629/1990, pp. 13-19 Japanese Patent O.P.I. publication 4/39651/1992. Typical examples thereof are given below. As a hardner, it is preferable to use an epoxy compound. Any epoxy hardener can be used with no limitation, as long as it has an epoxy group. It can be used in combination with one or more other hardeners such as aldehyde hardeners and vinylsulfone hardeners. The epoxy compound preferably contains a hydroxyl group or ether condensation linkage. In the present invention, epoxy equivalence is obtained by the following equation. Epoxy equivalence = molecular weight/number of epoxy groups in one molecule. This value can also be obtained colorimetrically by the method described in "Shin Jikken Kagaku Koza, Vol. 13 (1), Yuki Kozo", p. 58, published by Maruzen. The epoxy equivalence is preferably 50 to 300, more preferably 80 to 210. Epoxy equivalence values exceeding 300 result in insufficient hardening; coatability decreases as the amount increases. Insufficient hardening tends to lead to scratches. Epoxy equivalence values under 50 offer strong hardening but result in haze and residual color deterioration; no improvement is obtained even when the amount is reduced. Examples of epoxy compounds include E-1 through E-11 given in Japanese Patent Application No. 146629/1990 Japanese Patent O.P.I. Publication 4/39651/1992. Typical examples thereof are given below. Figures in parentheses are values for epoxy equivalence. The amount of epoxy hardener added is preferably 5 mg/m 2 to 1 g/m 2 . The above mentioned epoxy compounds are used not only in the antistatic layer but also in an under layer, an emulsion layer, a backing layer, or a protective layer. The epoxy compound is preferably used in the hydrophilic colloid layer in contact with the antistatic layer, as this ameliorates the adhesive property. The metal oxide for the antistatic layer may be indium oxide, tin oxide, vanadium oxide or a metal oxide doped with antimony atom or silver atom, or any combination thereof. Two types of indium oxide, namely indous oxide In 2 O and indic oxide In 2 O 3 are known, but it is preferable to use indic oxide for the present invention. Two types of tin oxide, namely stannous oxide SnO and stannic oxide SnO 2 are known, but it is preferable to use stannic oxide for the present invention. As a vanadium oxide, it is preferable to use a vanadium penta-oxide. Examples of metal oxides doped with antimony atom include tin oxide and iridium oxide and with silver atom, vanadium penta-oxided. To dope these metal oxides with antimony or silver, a halide, alkoxy derivative or nitrate of tin or indium or vanadium and a halide, alkoxy derivative or nitrate of antimony or silver are mixed, oxidized and burnt. These metal compounds are easily available from metal compound manufacturers such as Nippon Yttrium Co., Ltd. The doping antimony or silver content is preferably 0.5 to 10% by weight of tin or indium or vanadium. These inorganic compounds are added preferably in dispersion in a hydrophilic colloid such as gelatin or in a polymeric compound such as acrylic acid or maleic acid. The amount of their addition per binder is preferably 1 to 100% by weight. The film surface pH of the electroconductive layer for the present invention is preferably not more than 8.0, more preferably 3.0 to 7.5. Too low film surface pH values are undesirable from the viewpoint of film stability. The electroconductive layer for the present invention may be on the support side with respect to the lightsensitive layer or on the opposite side of the support. According to the present invention, the film is rolled around a core (the first core) with the emulsion layer side facing outside after coating and drying, which core preferably has an outside diameter of 100 to 500 mm from the viewpoint of the effect and productivity. The rolled film is then cut into given size, 250 mm ~ 700 mm and wound onto a core, 50 mm ~ 100 mm, faceing the emulsion layer inside and packaged. The heat treatment for the present invention is conducted before this cutting. Although heating temperature must be over 30°C to obtain the satisfactory effect, it is preferably in the range from 34°C to 55°C. Although varying depending on temperature, heat treatment time is preferably not less than about 12 hours when the temperature is 40°C. Heat treatment humidity is not more than 1% as of absolute humidity. Absolute air humidity is defined as the weight ratio of water vapor and air; for example, 1% absolute humidity is equivalent to a relative humidity of about 50% RH at 29°C or about 21% RH at 40°C. According to the present invention, the polyester support is coated with hydrophilic colloid layers, including at least one silver halide emulsion layer, on both faces. The amount of binder gelatin coated, including all gelatin used in each face, is preferably not more than 2.5 g/m 2 in total for each face. When using the silver halide photographic light-sensitive material of the present invention for film-making process, it is preferable to obtain images with very high contrast. For this purpose, it is preferable to add a tetrazolium compound or hydrazine compound to at least one layer on the emulsion layer side. Examples of tetrazolium compounds include those represented by Formula I in Japanese Patent Application No. 107056/1990 Japanese Patent O.P.I Publication 3/287158/1991. Examples of tetrazolium compounds which are preferably used include I-1 through I-27 given on Table 1 in the same patent application, page 9. Examples of hydrazine compounds include those represented by Formulas A and B in Japanese Patent Application No. 234203/1990 Japanese Patent O.P.I. Publication 4/114145/1992. Examples of tetrazolium compounds which are preferably used include 1 through 177 in the same patent application, pp. 12-48. The effect of the present invention can be enhanced by bringing into contact the hydrophilic colloid layer solution, including a silver halide emulsion layer, with 35 to 80°C air for a period from 5 seconds to 1 minute within 5 minutes after the average surface temperature of the coating layer has reached the level 1°C below the average temperature of ambient air for drying. After the finish of the above process, the film must be wound up onto the core within 5 minutes. It is not necessarily wound up the emulsion side facing outside, as it can be re-wound the emulsion side facing outside just before the heat treatment, however, the heat treatment must be done as early as possible but not later than 30 days from the date of the adjusting step. EXAMPLES The present invention is hereinafter described in more detail by means of the following examples, but the invention is never limited thereby. Example 1 Preparation of antistatic layer (1) Polymeric antistatic layer (Po) After corona discharge at an energy intensity of 10 W/(m 2 •min), polyethylene terephthalate, previously subbed with vinylidene chloride, was again subjected to corona discharge at an energy intensity of 10 W/(m 2 •min), and then coated with an antistatic layer coating solution with the following composition. Water-soluble electroconductive polymer P-3 2.5 g/m 2 Hydrophobic latex L-3 1.7 g/m 2 Ammonium sulfate 20 mg/m 2 Hardener-I E-6 500 mg/m 2 Hardener-II E-2 200 mg/m 2 Polyethylene glycol 5 mg/m 2 (2) Metal oxide antistatic layer (M) A metal oxide antistatic layer coating solution with the following composition was coated in the same manner as with the polymeric antistatic layer. Gelatin 0.2 g/m 2 Styrene-maleic acid copolymer 50 mg/m 2 Polyethylene glycol 2 mg/m 2 Metal oxide (antimony-doped tin oxide) 0.1 g/m 2 Hardener E-7 50 mg/m 2 Preparation of emulsion A silver chlorobromide emulsion having a silver bromide content of 2 mol% was prepared as follows. A gelatin solution containing 20 mg of rhodium sodium hexabromide, sodium chloride and potassium bromide per 60 g of silver nitrate and an aqueous solution of silver nitrate were mixed and stirred by the double jet method at 40°C for 25 minutes to yield a silver chlorobromide emulsion having an average grain size of 0.2 µm. To this emulsion was added 180 mg of 6-methyl-4-hydroxy-1,3,3a,7-tetrazaindene, followed by washing and desalting by conventional methods. Then, after adding 20 mg of 6-methyl-4-hydroxy-1,3,3a,7-tetrazaindene, the emulsion was subjected to sulfur sensitization and subsequently diluted with water to yield 300 ml of a finished emulsion. Coating of silver halide emulsion layer To the emulsion thus obtained, the following additives were added to the following amounts of coating. After subbing with poly(styrene-butyl acrylate-glycidyl methacrylate) latex, the side opposite to the antistatic layer of the polyethylene terephthalate support was coated with the emulsion. Latex polymer: Styrene-butyl acrylate-acrylic acid terpolymer 1.0 g/m 2 Tetraphenylphosphonium chloride 30 mg/m 2 Saponin 200 mg/m 2 Polyethylene glycol 100 mg/m 2 Sodium dodecylbenzenesulfonate 100 mg/m 2 Hydroquinone 150 mg/m 2 Phenidone 100 mg/m 2 Sodium styrenesulfonate-maleic acid polymer (Mw = 250000) 150 mg/m 2 Butyl gallate 500 mg/m 2 5-methylbenzotriazole 30 mg/m 2 2-mercaptobenzimidazole-5-sulfonic acid 30 mg/m 2 Inert ossein gelatin (isoelectric point 4.9) See Table 1 Silver 2.8 g/m 2 Emulsion layer protective layer An emulsion layer protective layer was coated to have the following coating amounts. Fluorinated dioctyl sulfosuccinate 300 mg/m 2 Matting agent: Methyl polymethacrylate (average grain size 3.5 µm) 100 mg/m 2 Gelatin See Table 1 Amorphous silica (average grain size 4.0 µm) 50 mg/m 2 Sodium styrenesulfonate-maleic acid copolymer 100 mg/m 2 With the following hardeners, emulsion layers or protective layer were hardened. Backing coat and backing coat protective layer After corona discharge at an energy intensity of 25 W/(m 2 ·min) on the antistatic layer side (opposite to the emulsion layer) of the support, a backing coat containing a backing dye with the following composition and a backing coat protective layer were coated. Backing coat Backing coat Hydroquinone 50 mg/m 2 Phenidone 10 mg/m 2 Latex polymer: Butyl acrylate-styrene copolymer 500 mg/m 2 Styrene-maleic acid copolymer 100 mg/m 2 Citric acid 40 mg/m 2 Benzotriazole 100 mg/m 2 Styrenesulfonic acid-maleic acid copolymer 100 mg/m 2 Lithium nitrate 30 mg/m 2 Backing dyes a, b, c, d, e Ossein gelatin See Table 1 Glyoxal 100 mg/m 2 Epoxy hardener (E-8) 50 mg/m 2 The coating solution was previously adjusted to a pH of 5.4 before coating. Backing coat protective layer After adding additives to have the following amounts of coating, the coating solution was coated on the upper face of the backing coat by the double jet method. Dioctyl sulfosuccinate 200 mg/m 2 Matting agent: Polymethyl methacrylate (average grain size 4.0 µm) 50 mg/m 2 Alkali-treated gelatin (isoelectric point 4.9) See Table 1 Fluorinated sodium dodecylbenzenesulfonate 50 mg/m 2 Bis(vinylsulfonylmethyl) ether 20 mg/m 2 After coating the emulsion layer, emulsion layer protective layer, backing coat and backing coat protective layer (coating solution temperature 35°C), the film was treated with 5°C cold air for 6 seconds to cool and set, followed by drying to reach a water content of 1600 in the coating layer gelatin at a coating surface temperature of 10°C using drying air having a dry bulb temperature of 23°C and a relative humidity of 20%, followed by drying using drying air having a dry bulb temperature of 27°C and a relative humidity of 20%, followed by drying to reach an average temperature of 33°C on the coating drying surface using drying air having a dry bulb temperature of 34°C and a relative humidity of 43%. After 5 seconds, the film was treated with drying air having a dry bulb temperature of 60°C and a relative humidity of 5% with a heat conduction coefficient of 100 Kcal/(m 2 ·hr·°C) for 40 seconds. Then, within 5 minutes the film was rolled around a core having an outside diameter of 200 mm with the emulsion layer side facing outside and was heat treated 3 days after. Then, after heat treatment under the conditions shown in Table 1, and further 3 days after, the roll was cut into given size and then rolled around another core having an outside diameter of 76.5 mm with the emulsion layer side facing inside, at 23°C, 50%RH and then packaged. Evaluation of habitual curling The roll film thus obtained was stored at 25°C temperature and 50% relative humidity for 30 days, cut into sheets having a length of 300 mm. Under conditions of 25°C temperature and 50% relative humidity, the curvature of the cut film as measured. From the results shown in Table 1, it is evident that the samples in accordance with the present invention have a small curvature and are hence good in the suppression of habitual curling. Sample Nos. 8 through 10, wherein the amount of gelatin coated was not more than 2.5 g/m 2 , were especially good in the suppression of habitual curling. The present invention provides a silver halide photographic light-sensitive material with little habitual curling especially in unprocessed films.

Claims: A method of manufacturing a silver halide photographic light-sensitive material, the material comprising a polyester support carrying a first hydrophilic layer comprising a silver halide emulsion layer on a first surface of the support, and a second hydrophilic layer comprising an anti-static layer on a second surface of the support, the method comprising the steps of: (a) coating the first hydrophilic layer and the second hydrophilic layer on to the polyester support; (b) drying the coated layers to complete a light-sensitive film; thereafter (c) winding the film on to a first core, the silver halide emulsion layer coated side facing outwardly; (d) heating the wound film at a temperature of 30 to 55 degrees Celcius and at an absolute humidity of not more than 1 per cent, for not less than 12 hours; (e) removing the film from the first core and cutting the film; and thereafter (f) winding the cut film on to a second core, the silver halide layer coated side facing inwardly, characterised in that each of the first hydrophilic layer and the second hydrophilic layer contains gelatin in an amount not more than 2.5 grams per square metre. The method according to claim 1, characterised in that the wound film is heated to a temperature of 34 to 55 degrees Celcius. The method according to claim 1, characterised in that the anti-static layer is a hydrophilic colloidal layer containing a metal oxide, or a reaction product of a water-soluble electroconductive polymer, a hydrophobic polymer latex and a hardener. The method according to claim 3, characterised in that the water-soluble electroconductive polymer contains a sulfonic acid group, a sulfuric ester group, a quaternary ammonium group, a tertiary ammonium group or a carboxyl group. The method according to either of the claims 1 or 4, characterised in that the steps of coating the hydrophilic layers and the drying of the coated layers are followed by an adjusting step for contact with air at 35 to 80 degrees Celcius for 5 to 60 minutes at a timing of when the surface temperature of the layers reaches one degree lower in Celcius of the temperature of the drying air. The method according to claim 5, characterised in that within five minutes after the adjusting step, the film must be taken up by the first core, and the heating step must be carried out within 30 days. The method according to claim 3, characterised in that the hydrophobic polymer latex is a styrene, a styrene derivative, an alkyl acrylate, an alkyl methacrylate, an olefin derivative or an acrylonitrile. The method according to claim 3, characterised in that the hardener is an epoxy compound. The method according to claim 8, characterised in that the epoxy compound contains a hydroxyl group or an ether condensation linkage The method according to claim 9, characterised in that the hardener has an epoxy equivalence, the molecular weight divided by the number of epoxy groups in one molecule, is from 50 to 300. The method according to claim 10, characterised in that the hardener has an epoxy equivalence, the molecular weight divided by the number of epoxy groups in one molecule, from 80 to 210.

Inventors: SAMPEI TAKESHI, TAKAMUKI YASUHIKO, SAMPEI, TAKESHI, TAKAMUKI, YASUHIKO, SAMPEI, TAKESHI, C/O KONICA CORPORATION, TAKAMUKI, YASUHIKO, C/O KONICA CORPORATION
Applicants: KONISHIROKU PHOTO IND, KONICA CORPORATION
Application year: 1992
Main classification: G03C1
IPC codes: G03C3, G03C1