Magneto-optical memory device whereon overwriting operation can be carried out through light intensity modulation and method for recording and erasing using it

Abstract: A magneto-optical memory device is provided with a recording track having a recording film and a guide track wherein a perpendicular magnetic film, whose magnetization direction is arranged in one direction, is formed, the recording track and the guide track being alternately disposed. A recording operation is carried out using a circular magnetic field generated from the perpendicular magnetic film by projecting a light beam only on the recording track so as to raise the temperature of the recording film. When erasing, the light beam is projected on the recording track and respective portions of the guide tracks located on both sides of the recording track so as to raise the temperature thereof. As the temperature rises, the magnetization of the perpendicular magnetic film becomes smaller, and an erasing operation is therefore performed using an external magnetic field.

Description: FIELD OF THE INVENTION The present invention relates to a magneto-optical memory device for use in a magneto-optical recording-reproduction apparatus employing the light intensity modulation, such as a magneto-optical disk, a magneto-optical card, etc., and a method of recording and erasing using the magneto-optical memory device. BACKGROUND OF THE INVENTION For a method of recording and erasing using a magneto-optical memory device, which utilizes magneto-optical effect, various types of overwriting methods have been proposed, such as the magnetic field modulation and the light intensity modulation. With the magnetic field modulation, a recording operation is carried out by reversing the magnetization direction while successively projecting a laser beam. On the other hand, the recording operation is carried out by modulating the intensity of the laser beam with the light intensity modulation. However, with the magnetic field modulation, there is a limit in improving the recording speed because of the time required for reversing the magnetic head which reverses the magnetization direction. Therefore, for high speed memory, the magneto-optical memory device employing the light intensity modulation has been researched and developed. For the magneto-optical memory device which employs the light intensity modulation, a magneto-optical memory device consisting of an initialization-use magnet and a double-layered film has been proposed. (The 53rd meeting on Magnetics by Japan Magnetic Society (1988), p.78.) With the memory device of double-layer structure, an overwriting operation is carried out through the light intensity modulation in the following way. A recording film, whereon information is recorded, consists of a recording layer and a writing layer laminated in a direction perpendicular to the surface of the recording film. The recording layer has its Curie temperature that is below the Curie temperature of the writing layer, and high coercive force at room temperature. Furthermore, the magnetic field to be applied from the initialization-use magnet is greater than the coercive force of the writing layer but smaller than the coercive force of the recording layer. First, the magnetization direction of the writing layer is arranged in the magnetization direction of the initialization-use magnet. Next, a light beam with high level or low level intensity is projected. When projecting the light beam with low level intensity, the temperature of the writing layer is not raised to the Curie temperature. The magnetization direction of the writing layer is therefore maintained and copied to the recording layer by the exchange coupling force. On the other hand, in the case of high level intensity, both recording layer and the writing layer are raised above the respective Curie temperatures. Thus, the writing layer is magnetized in the magnetization direction of an externally-applied recording magnetic field. Thereafter, the magnetization direction of the recording layer is arranged in the same direction. However, the discussed arrangement creates the following problems. Since the magnetic field of the initialization-use magnet, whose intensity is ten times as strong as that of the magnetic field for recording, is required for the initialization-use magnet, the initialization-use magnet becomes larger in size, and therefore the recording-reproduction apparatus becomes larger in size and more complicated. In order to obtain the recording film wherein exchange coupling force is exerted between the two layers, the selection of the composition and the manufacturing process for the recording film are complicated. Furthermore, the material whose Curie temperature is below the Curie temperature of the writing layer must be selected for the recording layer. For this reason, the Kerr rotation angle of the recording layer becomes small, and the high quality reproduction signal may not be obtained. SUMMARY OF THE INVENTION An object of the present invention is to provide a magneto-optical memory device whereon an overwriting operation can be carried out through the light intensity modulation without requiring initialization-use magnetic field, and to provide a method of recording and erasing using the magneto-optical memory device. Another object of the present invention is to provide a magneto-optical memory device which permits the quality of a reproduction signal to be improved and which can be easily manufactured. In one aspect, the present invention provides the magneto-optical memory device defined by claim 1 whose preamble reflect the state of the art according to US-A-4,853,912. In another aspect, the present invention provides the method of recording/erasing defined by claim 10. The sub-claims 2 to 9 and 11 are directed to embodiments of the invention. A method of recording and erasing in accordance with the present invention using the magneto-optical memory device is characterized by the use of a light beam which has a varying diameter. The light beam is projected only on the recording track when recording, and is projected on the recording track and respective portions of the guide tracks located on either side of the recording track when erasing. When projecting the light beam only on the recording track so as to raise the temperature of the recording film, the recording film is magnetized in a direction opposite to the magnetization direction of the guide track magnetic film by a circular magnetic field. The circular magnetic field is generated from the magnetic film formed in the guide tracks located on both sides of the recording track. On the other hand, when erasing, the circular magnetic field of the portion of the guide track magnetic film irradiated with the light beam becomes small. This is because the guide track magnetic film has such a characteristic that the intensity of the magnetization thereof becomes smaller as the temperature rises. In this state, the recording film is magnetized by the external magnetic field in a direction opposite to the magnetization direction when the recording operation is carried out. According to the invention, since the writing layer is not required, the materials having high Curie temperatures can be used for the recording layer. As a result, the Kerr rotation angle becomes larger, and the reproduction signal quality is improved. Moreover, since the above arrangement does not require the initialization-use magnetic field, a recording and reproducing apparatus employing the magneto-optical memory device can be made thinner and more compact. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 through Fig. 4 show one embodiment of the present invention. Fig. 1 is a schematic cross-sectional view showing the configuration of the magneto-optical disk in accordance with the present invention. Fig. 2 is a graph showing the characteristic of the perpendicular magnetic film of Fig. 1. Fig. 3 is a view showing a recording operation on the magneto-optical recording disk of Fig. 1. Fig. 4 is a view showing an erasing operation from the magneto-optical recording disk of Fig. 1. Fig. 5 is a schematic cross-sectional view showing another configuration of the magneto-optical disk of the present invention. Fig. 6 is a schematic cross-sectional view showing a transparent substrate of the magneto-optical disk having another configuration of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The following will describe one embodiment of the present invention referring to Fig. 1 through Fig. 6. As shown in Fig. 1, a magneto-optical disk as an example of the magneto-optical memory device of the present invention is provided with a transparent substrate 1 made of glass or plastic with a thickness of 0.5 - 1.5mm. Further, a recording track 8 and a guide track 9 with a width of 0.5 µm are alternately formed on the transparent substrate 1. In addition, the pitch between guide tracks 9 is 1.5 µm. A perpendicular magnetic film 2 made of TbCo with a thickness of 50 - 500 nm is formed on a portion of the transparent substrate 1 whereon the guide track 9 is formed. A dielectric film 3 made of AlN is formed on the perpendicular magnetic film 2 and on a portion of the transparent substrate 1 whereon the recording track 8 is formed. The recording track 8 is provided adjacent to the guide tracks 9. Further, a dielectric film 4 with a thickness of 70 - 100nm, a recording film 5 mainly made of DyFeCo with a thickness of 20 - 50nm, a dielectric film 6 mainly made of AlN with a thickness of 20 - 50 nm and a reflecting film 7 mainly made of Al with a thickness of 50 nm are laminated in this order on the dielectric film 3. Here, the dielectric film 4 has a greater refractive index than that of the dielectric film 3. As shown in the figure, the dielectric film 3 is also formed on the side faces of the perpendicular magnetic film 2, i.e., the boundary portion from the recording track 8. With this arrangement, a magnetic domain wall between the recording track 8 and the guide track 9 can be prevented from being moved. Therefore, the thickness of the dielectric film 3 is set in the order of several Å - Å multiplied by ten. A manufacturing process of the magneto-optical disk is briefly described below. First, for the perpendicular magnetic film 2, a TbCo film is formed on the transparent substrate 1. Thereafter, a positive-type photo-resist (not shown) is applied on the surface of the TbCo film. Next, using a photomask (not shown) wherein a pattern of the guide track with a thickness of substantially 1µm and the pitch. of substantially 1.5 µm is formed beforehand, the pattern of the guide track is transferred to a photo-resist through the contact exposure method disclosed in US-A-4,778,747. Here, the pattern of the guide track stored in the photomask is formed using a visor film such as Ta. Thereafter, the pattern of the guide track is developed by removing the portion of the photo-resist, the portion corresponding to the recording track. Thereafter, the TbCo film is etched using the remaining photo-resist as a mask. After the etching, the remaining photo-resist is removed, and dielectric film 3 is formed on the transparent substrate I and on the magnetic film with perpendicular magnetization 2 (TbCo film). Furthermore, the previously described dielectric film 4, the recording film 5, dielectric film 6 and the reflecting film 7 are laminated in this order in order to obtain the magneto-optical disk. The following description will discuss a method of recording and erasing with respect to the magneto-optical disk with the above arrangement using the overwriting method. The perpendicular magnetic film 2 exhibits a magnetization characteristic shown in Fig. 2. Namely, the film 2 has a great magnetization at around room temperature T 1 , and the magnetization becomes weaker as the temperature rises. In addition, the magnetization direction is upward in Fig. 1. When recording, first, a light beam 11 is projected on the recording track 8 as shown in Fig. 3. Thus, the temperature of the recording film 5 corresponding to the irradiated portion with the light beam 11 of the recording track 8 is raised above its Curie temperature. In this state, the magnetization direction of a circular magnetic field 10 corresponding to the recording track 8 is opposite to the magnetization direction of the perpendicular magnetic film 2 (downward in the figure). The circular magnetic field 10 is generated from the perpendicular magnetic film 2 formed in the guide tracks 9 located on both sides of the recording track 8. Therefore, when the projection of the light beam 11 is stopped and the temperature of the recording track 8 starts dropping, a downward magnetization is generated on the recording film 5 of the recording track 8, thereby completing the recording operation. In the case of the erasing operation, a light beam 12 is projected on the recording track 8 so that a light spot is formed on the recording track 8 and jutted out into the guide tracks 9 on both sides of the recording track 8 as shown in Fig. 4. In order to achieve this, the diameter of the light beam 12 is set larger than that of the light beam 11 used in recording. When the light beam 12 is projected on portions 2a of the perpendicular magnetic film 2 formed in the guide tracks 9, the temperature of the portions 2a rises, and the magnetization of the portions 2a becomes weaker. Fig. 2 shows a distribution of magnetization intensity of the perpendicular magnetic film 2 ranging from M 2 to M 1 . Here, the temperature of the portion 2a in the vicinity of the recording track 8 is designated by T 2 , and the temperature of the portions 2b, whereon the light beam 12 is not projected, is designated by T 1 . Therefore, the temperature of the recording film 5 of the recording track 8 is raised above the Curie temperature, and the circular magnetic field 10 exerted thereon becomes fairly weak, the circular magnetic field 10 being generated from the perpendicular magnetic film 2. In this state, an external magnetic field 13, which is stronger than the circular magnetic field 10, is applied on the recording track 8 in an upward direction in the figure. Thus, the projection of the light beam 12 is stopped, and the temperature of the recording track 8 starts dropping. As a result, the magnetization in an upward direction is generated on the recording film 5, thereby completing the erasing operation. In addition, in the case of a recording operation, the magnetization is also applied from the external magnetic field 13 to the recording track 8. However, since the magnetization of the circular magnetic field 10 is greater than that of the external magnetic field 13, the magnetization direction of the recording film 5 is downward. With the magneto-optical disk having the described arrangement, the reflective index of the light beam is 50% on the guide track 9, whereas 10 - 20% on the recording track 8. This is because the recording track 8 has a multi-layer structure consisting of the dielectric film 4, the recording film 5, and the dielectric film 6, so as to have a greater Kerr rotation angle of the reflected light. Therefore, a tracking servo signal is obtained from the difference in the reflective indexes between the guide track 9 and the recording track 8. According to the magneto-optical disk of the present embodiment, the dielectric film 3, the dielectric film 4, the recording film 5, the dielectric film 6, and the reflecting film 7 are laminated also on the perpendicular magnetic film 2 formed in the guide tracks 9. However, in the previously described manufacturing process, it may be also arranged such that the TbCo film is etched after the development of the photo-resist, and the above films 3 to 7 are formed without removing the remaining photo-resist; thereafter, both the remaining photo-resist and the above films 3 to 7 laminated on the TbCo film are removed by means of the lift-off. With the above magneto-optical disk, the dielectric film 3 is formed in order to prevent the movement of the magnetic domain wall. However, the movement of the magnetic domain wall can be prevented by other arrangements. For example, as shown in Fig. 5, protrusions and recessions are formed on the transparent substrate 14, and by providing a gap between the guide track 16 and the recording track 15, the movement of the magnetic domain wall can be prevented. In this case, the gap between the recording track 15 and the guide track 16 may be set between 20 - 100 nm, and the film formed on the recording track 15 and the guide track 16 needs to be set thicker than the gap. Other than the above arrangements, the movement of the magnetic domain wall can also be prevented by providing on the transparent substrate 17 a projected portion 17a with a width of 0.1 - 0.3 µm between the recording track 18 and the guide track 19. In this case, the height of the projected portion 17a needs to be set more than half of the film thickness formed in the recording track and in the guide track 19. According to the above arrangement of the magneto-optical disk and the method of recording and erasing with respect to the magneto-optical disk, the conventional multi-layer structure is not required, and information can be recorded on the recording layer 5 of a single-layer structure when the movement of the magnetic domain wall can be prevented, and the recording and erasing operations can be carried out using the external magnetic field 13 or the magnetic field generated from the adjacent guide tracks 9. For this reason, materials having high Curie temperatures may be used for the recording layer 5. The invention may be embodied in other specific forms and manners without departure from the scope thereof as defined by the claims.

Claims: A magneto-optical memory device comprising a recording track (8) having a first magnetic film (5) for recording information, and a magnetic film (2) disposed adjacent to, and substantially co-planar with, said recording track wherein the first magnetic film (5) exhibits magnetization in a direction perpendicular to the first film (5) according to recorded information, characterised in that the adjacent magnetic film is a second magnetic film (2) exhibiting magnetization in a direction perpendicular to the second film (2), the Curie temperature of the first magnetic film (5) being lower than the Curie temperature of the second magnetic film (2), and the magnetization of the second magnetic film (2) falling with rise in temperature, whereby the direction of magnetization of the first magnetic film (5) may be selectively set by a magnetic field (10) generated by the second magnetic film (2) or an external magnetic field (13) in dependence upon whether a light beam (11;12) is incident on the first magnetic film (5) only or on both the first magnetic film (5) and an adjacent portion (2a) of the second magnetic film (2), respectively. A magneto-optical memory device according to claim 1 wherein the second magnetic film covers a guide track (9). A magneto-optical memory device according to claim 2, comprising means for preventing the movement of a magnetic domain wall formed between the recording track (8) and the guide track (9). A magneto-optical memory device according to claim 3, wherein said means for preventing the movement of the magnetic domain wall is a dielectric film (3) formed between the recording track and the guide track. A magneto-optical memory device according to claim 3, wherein said means for preventing the movement of the magnetic domain wall is a portion (17a) of a transparent substrate provided between the recording track (18) and the guide track (19), the first and second magnetic films (5,2) being formed on the transparent substrate (17). A magneto-optical memory device according to claim 3, wherein said means for preventing the movement of the magnetic domain wall comprises a step in the surface of a transparent substrate (14) on which the recording track (15) and the guide track (16) are formed, the step being provided between the recording track and the guide track and causing the first magnetic film (5) to be recessed relative to the second magnetic film (2). A magneto-optical memory device according to any of preceding claims 2-6, wherein the recording track (8;15;18) and the guide track (9;16;19) are formed on a or said transparent substrate (1;14;17), and the recording track comprises a dielectric film (4,6), said first magnetic film (5) and a reflecting film (7) formed on the transparent substrate. A magneto-optical memory device according to claim 7, wherein the guide track (9) has a greater reflective index than the recording track (8). A magneto-optical memory device according to any preceding claim, wherein the first magnetic film (5) is made of DyFeCo, and the second magnetic film (2) is made of TbCo. A method of recording and erasing information on a magneto-optical memory device according to any preceding claim, the method comprising: heating said first magnetic film (5) above its Curie temperature by projecting a light beam (11) only on the recording track (8) when recording, so that the magnetization direction of the first magnetic film (5) is set by a magnetic field (10) generated locally in the adjacent second films (9); and varying the diameter of the light beam so as to project the light beam (12) on the recording track (8) and respective portions (2a) of the adjacent second films (9) when erasing, so that the first magnetic film (5) is heated above its Curie temperature and the magnetic field from the irradiated portions (2a) of the second magnetic film (2) becomes smaller, whereby the magnetization direction of the first magnetic film (5) is set by a bias magnetic field (13). A method of recording information according to claim 10, wherein the bias magnetic field (13) is provided by means external to the memory device.

Inventors: KATAYAMA HIROYUKI, NAKAYAMA JUNICHIRO, OHTA KENJI, KATAYAMA, HIROYUKI, NAKAYAMA, JUNICHIRO, OHTA, KENJI
Applicants: SHARP KK, SHARP KABUSHIKI KAISHA
Application year: 1992
Main classification: G11B11
IPC codes: G11B11