Optical connector

Abstract: The optical connector comprises a glass ferrule (10) having tapers (20) and (21) and a terminal metal member (12), wherein the glass ferrule (10) is strengthened mechanically by ion-exchange treatment, and an optical fiber (11) exposed from a jacketed optical fiber (14) is inserted to be fixed in a bore (10A) on the center axis of the glass ferrule (10). The jacketed optical fiber (14) is inserted to be fixed in an aperture (14) of the terminal metal member (12). The ion-exchange treatment is that alkali ions Na⁺ or Li⁺ are substituted by alkali ions K⁺ (for Na⁺ , Li⁺) or Na⁺ (for Li⁺ ) having an ionic radius larger than the substituted ions, so that large compression stress occurs on the surface of glass to increase practical mechanical strength. In accordance with the ion-exchange treatment, the features are obtained as set out below. (a) strength of more than two times is obtained as compared with air cooling strengthening. (b) no limitation is applied to configuration, thickness, etc. (c) no deformation occurs to provide high dimensional precision. (d) even small specimen which is difficult to be held is possible to be under this treatment. (e) no tearing off occurs as in case of using a protective film.

Description: This invention relates to an optical connector for connecting optical fibers, and more particularly to, a solidified or strengthened structure of an optical connector ferrule. Optical connectors are optical devices which are used in all kinds of optical communication systems, optically applied equipments, etc., and are indispensable for the connection between optical fibers, and an optical fiber and a light emitting or receiving device. One type of a conventional optical connector comprises a ferrule of a high mechanical strength such as ceramic for fixing an optical fiber exposed from a jacketed optical fiber on the center axis thereof, and a terminal metal member for fixing one end of the ferrule and supporting the jacketed optical fiber having the optical fiber exposed therefrom to be fixed by the ferrule. Another type of a conventional optical connector comprises a glass capillary for fixing an optical fiber exposed from a jacketed optical fiber on the center axis thereof, and a terminal metal member for covering the whole outer surface of the glass capillary and supporting the jacketed optical fiber having the optical fiber exposed therefrom to be fixed by the capillary. The ferrule or the glass capillary is polished on its outer surface to provide a predetermined outer surface precision by use of a whetstone rotated by a grinder, so that a precisely defined center axis is obtained. In these optical connectors, an optical fiber is connected to an optical fiber or an optical device such as a photodiode, a laser device, etc. at mechanically and optically stable state. However, the former optical connector has a disadvantage in that a material of the ferrule is limited to a high strength material such as ceramic. Further, the latter optical connector has a disadvantage in that a manufacturing process is complicated and the manufacturing cost is high, because the glass capillary is totally covered by the terminal metal member. Still further, the former and latter conventional optical connectors have a common disadvantage in that the productivity is low, because the center axis must be defined with high precision by the outer surface polishing. DE-A-1 696 063 discloses a boroaliminum silicate glass for which Li + is ion-exchanged in the fused salt containing ions of Na + at a temperature of at least 530°C. Accordingly, it is an object of the invention to provide an optical connector using a glass ferrule in which the mechanical strength is hightened by compression stress and which is manufactured with low cost and high productivity. This object is solved with the features of the claims. The invention will be explained in more detail in conjunction with appended drawings; wherein: Fig. 1 is a cross-sectional view showing a first conventional optical connector; Fig. 2 is a cross-sectional view showing a second conventional optical connector; Fig. 3 is an explanatory view showing a grinder for polishing an outer surface of a ferrule or a glass capillary for an optical connector; Fig. 4 is a cross-sectional view showing an optical connector of a preferred embodiment according to the invention; Figs. 5 and 6 are explanatory views explaining principle of ion-exchange which is used for mechanically strengthening a glass ferrule applied for the optical connector of the preferred embodiment; Fig. 7 is an explanatory view showing an apparatus for manufacturing a glass ferrule applied for the optical connector of the preferred embodiment; and Fig. 8 is an explanatory view showing an ionexchange apparatus for strengthening a glass ferrule applied for the optical connector of the preferred embodiment. Before explaining an optical connector of a preferred embodiment according to the invention, the aforementioned conventional optical connectors will be explained in Fig. 1 to 3. Fig. 1 shows the first conventional optical connector which comprises a ferrule 2 having a bore 2A made of ceramic and a terminal metal member 4 having an aperture 6, wherein one end of the ferrule 2 is fixed by the terminal metal member 4. In this optical connector, a jacketed optical fiber 5 having an exposed optical fiber 1 is inserted to be fixed in the aperture 6 of the terminal metal member 4, and the optical fiber 1 is fixed in the bore 2A on the center axis of the ferrule 2. Fig. 2 shows the second conventional optical connector which comprises a glass capillary 3 having a bore 3A and a terminal metal member 4 having an aperture 6, wherein the glass capillary 3 is covered on its whole outer surface by an extended portion 4A of the terminal metal member 4. In this optical connector, a jacketed optical fiber 5 having an exposed optical fiber 1 is inserted to be fixed in the aperture 6 of the terminal metal member 4, and the optical fiber 1 is fixed in the bore 3A on the center axis of the glass capillary 3 (see also JP-A-55-67714). In Fig. 3, the ferrule 2(Fig. 1) or the extended portion 4A of the terminal metal member 4 which is incorporating glass capillary 3(Fig. 2) is supported by rotation shafts 7, and is polished on its outer surface by a whetstone 9 which is rotated by a grinder 8. The grinder 8 is controlled to move vertically as indicated by an arrow, so that the contact pressure of the whetstone 9 is controlled on the outer surface of the ferrule 2(Fig. 1) or the extended portion 4A of tile terminal metal member 4 which is incorporating glass capillary 3(Fig. 2). In the first conventional optical connector as shown in Fig. 1, however, the ferrule 2 is required to be of high strength. Therefore, it is limited practically to a high strength material such as ceramic. On the other hand, if the ferrule 2 is made of glass, a glass ferrule of high precision is obtained by glass drawing method. However, cracks tend to occur on the glass ferrule, because glass is brittle. For this reason, a glass ferrule is not used practically. Under this situation, a structure in which the glass capillary 3 covered totally with the extended portion 4A of the terminal metal member 4 has been proposed. However, even this conventional optical connector has disadvantages as explained before. Next, an optical connector of a preferred embodiment according to the invention will be explained in Fig. 4. The optical connector comprises a glass ferrule 10 having tapers 20 and 21 and a terminal metal member 12, wherein the glass ferrule 10 is strengthened mechanically by ion-exchange treatment, and an optical fiber 11 exposed from a jacketed optical fiber 14 is inserted to be fixed in a bore 10A on the center axis of the glass ferrule 10. The jacketed optical fiber 14 is inserted to be fixed in an aperture 14 of the terminal metal member 12. Figs. 5 and 6 show principle of ion-exchange treatment, by which the glass ferrule 10 is strengthened mechanically, wherein the state prior to ion-exchange is shown in Fig. 5, while the state in which ion-exchange is completed is shown in Fig. 6. The ion-exchange treatment is that alkali ions Na + or Li + are substituted by alkali ions K + (for Na + , Li + ) or Na + (for Li + ) having an ionic radius larger than the substituted ions, so that large compression stress occurs on the surface of glass to increase practical mechanical strength. In accordance with the ion-exchange treatment, the features are obtained as set out below. (a) strength of more than two times is obtained as compared with air cooling strengthening. (b) no limitation is applied to configuration, thickness, etc. (c) no deformation occurs to provide high dimensional precision. (d) even small specimen which is difficult to be held is possible to be under this treatment. (e) no tearing off occurs as in case of using a protective film. Here, the ion-exchange treatment which is carried out in the preferred embodiment will be explained in more detail. In the preferred embodiment, borosilicate glass (Na 2 O · B 2 O · SiO 2 ) having annealing point of 570 °C is used, and low temperature type ion-exchange which is defined in that the ion-exchange as shown in Figs. 5 and 6 is carried out at a temperature lower than a glass transition point is adopted. On the other hand, high temperature type ion-exchange is defined to be carried out at a temperature ranging a glass transition point to a softening point. In the high temperature type ion-exchange, strength is largely increased. However, the deformation of glass tends to occurs. For this reason, the low temperature type ion-exchange is adopted in the preferred embodiment, as described above. In this low temperature type ion-exchange, fused salt is prepared by heating and maintaining powder of pottassium nitrate (KNO 3 ) at a temperature of 400 °C . Then, an original pipe of ferrules which is obtained by drawing a glass preform is dipped into the fused salt, and is held therein for several to ten and several hours, so that ions of Na + and those of K + are exchanged as shown in Figs. 5 and 6. After this ion-exchange, the original pipe is pulled up from the fused salt, and is gradually cooled down to the room temperature. Then, the original pipe is cleaned by refined water, and, finally, is cut to have a length of the ferrule. This ion-exchange may be applied not to an original pipe, but to a ferrule. This ion-exchange is expressed by the formula set out below. Na + 2 O - + 2 K + ⇄ K + 2 O - + 2 N a + The ferrules are manufactured in an apparatus as shown in Fig. 7. A glass preform 15 is heated to be drawn by a drawing furnace 16, and the drawn glass preform is cut to have a length of a ferrule 10 by a cutter 17. In this manufacturing process, the glass preform 15 which is provided with an bore 18 is held by a clamp 19. The ferrule 10 is processed to have the taper 20 (Fig. 4) by polishing, and the taper 21 (Fig. 4) by etching. In this manufacturing process, defining the center axis of the ferrule 10 is realized only by glassdrawing. The ferrule 10 is dipped into fused salt 23 in an ion-exchange bath 22. As explained before, the ferrule 10 is of borosilicate glass containing Na 2 O by 3 to 10%. In this fused salt bath 22, the aforementioned ion-exchange is carried out to provide a strengthened ferrule having strength of more than three times as compared with non ion-exchange processed ferrule.

Claims: An optical connector, comprising: a glass ferrule (10) having a center bore (10A) into which an optical fiber (13) is inserted to be fixed characterised in that said glass ferrule is constructed of a glass material containing alkali metal ions and has been subjected to a low temperature type ion-exchange treatment at a temperature below its glass transition temperature to increase its mechanical strength by substituting part of the alkali metal ions by alkali metal ions of larger ionic radius. An optical connector, according to claim 1, further comprising; a terminal metal member for fixing said glass ferrule at one end thereof, said terminal metal member being provided with a center aperture into which a jacketed optical fiber is inserted to be fixed, said optical fiber being exposed from said jacketed optical fiber. An optical connector, according to claim 2, wherein: said glass ferrule is processed by said ion-exchange, whereby ions of Na + in said glass ferrule are exchanged with ions of K + in fused salt. An optical connector, according to claim 2, wherein: said glass ferrule is processed by said ion-exchange, whereby ions of Li + in said glass ferrule are exchanged with ions of Na + in fused salt. An optical connector according to any of claims 1 to 4, wherein: said glass ferrule is of borosilicate glass, and is fabricated by the steps of heat-drawing a glass preform, and exchanging ions of Na + contained in a glass surface layer with ions of K + in a fused salt bath at said low temperature type ion-exchange treatment of a temperature less than the glass transition point of the borosilicate glass.

Inventors: FUNABIKI NOBUO, HADA MASAYO, KURATA KAZUHIKO, UEDA TETSUJI, FUNABIKI, NOBUO, HADA, MASAYO, KURATA, KAZUHIKO, UEDA, TETSUJI, Funabiki, Nobuo, c/o Nippon Elec. Glass Co., Ltd., Hada, Masayo, c/o Nippon Elec. Glass Co., Ltd.
Applicants: NIPPON ELECTRIC CO, NIPPON ELECTRIC GLASS CO, NEC CORPORATION, NIPPON ELECTRIC GLASS COMPANY, LIMITED
Application year: 1992
Main classification: G02B6
IPC codes: G02B6, C03C21