MICROCRYSTALLINE CELLULOSE SPHERONIZATION COMPOSITION

Abstract: A particulate co-processed unattrited microcrystalline cellulose: hydrocolloid composition wherein the respective components are present in a weight ratio of from about 99:1 to 70:30. The composition is useful as a spheronizing agent for producing spheroids of uniform size and sphericity and having high drug loadings. The composition is produced by drying a slurry of the microcrystalline cellulose in an aqueous solution of the hydrocolloid. The preferred hydrocolloid is methyl cellulose.

Description: MICROCRYSTALLINE CELLULOSE SPHERONIZATION COMPOSITION This invention relates to spheronization compo¬ sitions and solid pharmaceutical dosage forms based thereon. More particularly, the invention pertains to a microcrystalline cellulose:hydrocolloid spheronizing composition capable of yielding a high percentage of spheroids of uniform size and sphericity and containing highly elevated drug levels. In the food and pharmaceutical arts, it has long been the practice to prepare and utilize particulate formulations in which the individual particles are of a spherical configuration. Such contoured particulates afford a number of advantages. The sphere has the low¬ est surface to volume ratio. Spheres pack evenly in containers for ease of accurately measuring quantities of particulate materials by volume. In the field of pharmaceuticals, the sphere is the ideal geometric solid for the application of film coatings to effect control¬ led release of drugs and/or medicinals. A number of methods have been developed for pro¬ ducing spheronized pharmaceutical compositions. For instance, the preparation of spherical oral dosage forms in pill molds and pellet presses dates back many years. Since these early times, many improvements have been made in the technology. In recent years, a method of producing spherical particulates that is attracting increased attention of the pharmaceutical community is that of spheronization. The essential features of this technique typically in- volve the steps of: forming a dry blend of powdered components; wetting the dry blend with a liquid, usually aqueous, in the presence of a binding agent to give a plastic-like mass or granulation; extruding the mass through a screen or dye to form a spaghetti extrudate; cutting the extrudate into short cylinders followed by a rounding stage in which the cylinders are rolled on a grooved surface into spheres. For more detailed in- formation on the process reference is made to "A New Technique for the Production of Spherical Particles" by A. D. Reynolds in Manufacturing Chemist & Aerosol News, June 1970. Much of the interest in spheronization as a means of producing spherical particulates, or spheroids as they are commonly known, comes in the wake of the ever growing use of multiparticulate controlled-release oral dosage forms. These pharmaceuticals consist of drug bearing spheroids, generally about 0.8 to 1.2 mm in diameter, contained in capsules or compressed into tab¬ lets. By using a combination of spheroids having dif¬ ferent drug release characteristics, a dosage form can be tailored to provide the desired drug delivery system. In carrying out the spheronization, microcrystal- line cellulose is included in the formulation as a pre¬ ferred carrier or matrix medium for the active compo¬ nents. Microcrystalline cellulose (MCC) is a partially purified depolymerized form of cellulose and is obtained by treating pulps derived from fibrous plant material with mineral acid. The acid preferentially attacks the less ordered or amorphous regions of the cellulose poly¬ mer chain, thereby exposing and freeing the crystalline sites which form cellulose crystallite aggregates. The reaction mixture is washed to remove the degraded by¬ products, the resulting wet-cake freed of water and the dried cellulose crystallite aggregates, or more commonly microcrystalline cellulose, recovered. Microcrystalline cellulose is a white, odorless,tasteless, relatively free-flowing powder, insoluble in water, organic solvents, dilute alkalies and dilute acids. It finds wide use as a pharmaceutical excipient, being particularly effective as a binder in the manufacture of tablets by direct compression. . In formulating a drug delivery system in which the drug composition is composed of spherical particulates. certain properties for the spheroids are desirable. These include low friability, uniformity of size and sphericity or roundness and surface smoothness. Such characteristics ensure that on being coated, a film layer of even thickness will be deposited on the spher¬ oids for precise rate of drug release. Drug bearing spheroids, exhibiting the character¬ istics aforesaid to a considerable degree can be real¬ ized using microcrystalline cellulose as the excipient for the drug carrier and spheronizing agent. A small amount of other cellulose derivatives that absorb water (a hydratable cellulose) may be included in combination with the microcrystalline cellulose. Examples of such cellulosic derivatives are sodium carboxymethyl cellu- lose, hydroxy lower alkyl (C^-Cg) cellulose, e.g., hy- droxypropyl cellulose and hydroxypropylmethyl cellulose. A typical spheroid preparation involves forming a dry blend.of microcrystalline cellulose, a hydratable cellulose derivative and drug. Water is then added to the blend until a densely granulated mass is obtained. This is then passed through a cylinder (usually 1 mm) on an extruder adjusted to give a uniform, free flowing extrudate which is then spheronized. Representative de¬ scriptions of these formulations can be found in U.S. Patent Nos. 4,844,910; 4,867,985 and 4,867,987. Although such formulations and procedures can yield a high percentage of even sized spheroids at low to moderate drug levels, size distribution of the spher¬ oids begins to widen as drug levels exceed about 60%. As drug loadings are further increased above about 80%, the spheroids become even more varied in size and spher¬ icity thereby diminishing their utility as components in controlled release formulations. Spheroids exhibiting good uniformity of size and sphericity and containing elevated drug levels, upwards of 80%, can be produced by carrying out the spheroni¬ zation process with a mixture of drug and a highly modi- fied microcrystalline cellulose of the type described in U.S. Patent No. 3,539,365. This cellulosic derivative is prepared by subject¬ ing the washed filter cake containing about 40% micro- crystalline solids from the acid degradation of cellu¬ lose, to intense attritive forces. The result is a further break up of the cellulose crystallite aggregates and an increase in submicron particles. As the attri¬ tion proceeds, a sufficient amount of sodium carboxy- methyl cellulose is added to the aqueous mixture in order to coat the separated microcrystals. Upon com¬ pletion of the attrition, the mixture is dried and re¬ covered. The dried product is readily redispersible in aqueous media to give gels. It contains about 5% to 15% by weight of sodium carboxymethyl cellulose. The material is made and sold by the FMC Corpor¬ ation in several grades under the Avicel ® RC and CL trademark. Its application in spheronization processes is disclosed in FMC Technical Bulletin "Avicel Spheres." Although the attrited microcrystalline cellulose:- sodium carboxymethyl cellulose composition yields gener¬ ally satisfactory spheroids, it forms a sticky granu¬ lation which clings to the spheronization equipment. In order to maintain spheroid output, the equipment must be periodically disassembled and cleaned. This detracts from the practicality of such microcrystalline cellulose composition for commercial scale production and use as a spheronizing agent. A microcrystalline spheronizing composition has now been found that is surprisingly superior to the prior art compositions. In accordance with the present invention, a microcrystalline spheronizing composition useful in the production of spheroids having high drug loadings, is provided by a particulate co-processed nonattrited microcrystalline cellulose and a non-ionic hydrocolloid, the two components being intimately associated with one another. The invention further includes a process for producing the spheronizing composition, a method of producing solid dosage forms based on the spheronizing composition, and the resulting solid dosage forms. The particulate co-processed spheronizing compo¬ sition of the invention contains as its two essential components, microcrystalline cellulose and a pharma¬ ceutical grade, non-ionic hydrocolloid. As understood herein, hydrocolloid means a hydrophilic resin or poly- mer. Although the percentage of these two components can vary considerably, the weight ratio of microcrystal¬ line cellulose to hydrocolloid is desirably held to a range of from about 99:1 to about 70:30, or, when the hydrocolloid is methyl cellulose, preferably from about 97.5:2.5 to about 90:10 and most preferably from about 96:4 to 94:6. The source of the microcrystalline cellulose is preferably wet cake from a conventional microcrystalline cellulose manufacturing process. Wet cake which has not yet been dried is sometimes referred to as "never dried" or hydrocellulose. The dried microcrystalline cellulose can be used but it must be vigorously agitated in aque¬ ous media to reconstitute the cellulose crystallite aggregates. An economic advantage of the spheronization compo¬ sitions invention is that it can be manufactured without having to employ the more expensive highly attrited microcrystalline cellulose of the prior art composition. The microcrystalline cellulose component of the compo- sitions of the invention, whether in the wet cake or dried stage is understood to be unattrited microcrystal¬ line cellulose. The concentration of the non-ionic hydrocolloid solution should be sufficient to permit interaction of the microcrystalline cellulose with the hydrocolloid. Such interaction is believed to involve adsorption of hydrocolloid molecules on the surface of the cellulose crystallite aggregates which constitutes the structure of nonattrited microcrystalline cellulose. The affinity or attraction or other property of the hydrocolloid for the cellulose crystallites appears to vary from one member to another, as evidenced by differences in spheronization properties. A hydrocolloid which has been found exceptionally effective for preparing the microcrystalline spheroni- zation compositions of the invention is methyl cellu¬ lose. Granulations containing this hydrocolloid process very cleanly in the spheronization equipment with no evidence of sticking while giving a high percentage of spheroids having excellent uniformity of size distri- bution and sphericity. A number of non-ionic hydrophilic polymers are known and have been described in the technical litera¬ ture; many are available commercially as etherified or esterified celluloses and in other synthetic or deriva- tive form. In addition to methyl cellulose, other pre¬ ferred classes and examples of these polymeric entities are the modified (semisynthetic) gums including hydroxy lower alkyl (C^-Cg) celluloses such as hydroxyethyl cellulose, hydroxypropyl cellulose and hydroxy- propylmethyl cellulose, and the synthetic gums including vinyl polymers such as polyvinylpyrrolidone. For other -examples of modified and synthetic gums, see Glicksman, "Gum Technology in the Food Industry" (1969), page 8. To the extent that they may be non-ionic, the water soluble cellulose acetates are also useful. These are the partially hydrolyzed derivatives of cellulose ace¬ tate having an acetyl content in the range of about 17- 27% (calculated as combined acetic acid - U.S. Patent 3,482,011) or 13-19% (Eastman Chemical Products Publi- cation No. E-140B, February 1981, "Eastman ® Cellulose Acetate For Coatings") . In preparing the spheronizing compositions of the invention, microcrystalline cellulose is added to an aqueous solution of the non-ionic hydrocolloid and the mixture formed into a slurry under high energy shear. The microcrystalline cellulose is preferably wet cake formed in the conventional acid hydrolysis of cellulose pulps. Dried microcrystalline cellulose can also be used provided the high shear blending is sufficient to redisperse the cellulose crystallites. Mixing of the microcrystalline cellulose and aque- ous hydrocolloid is continued until interaction of the hydrocolloid with the cellulose crystallites is complete or has reached equilibrium. Normally, this takes about 10 to about 60 minutes. As previously noted, the hydro¬ colloid is believed to form an adsorbed layer on the cellulose crystallite surface. The concentration of microcrystalline cellulose and hydrocolloid in the aqueous slurry is such that the weight ratios of these components in the dried solid will fall within the specified ranges of 99:1 to 70:30, microcrystalline cellulose:hydrocolloid. Generally speaking, total amounts by weight of slurry solids will vary from about 5% to about 25%. Certain of the hydrocolloids may form viscous solutions or even gels in aqueous media making it dif- ficult or impossible to produce a flowable slurry. This can usually be circumvented by employing a more dilute solution of the hydrocolloid; also increasing the tem¬ perature may increase fluidity. For example, methyl cellulose is available in various viscosities, ranging from about 10 to 400 centipoise or higher in aqueous solution. When using the higher viscosity material, lesser concentrations can be employed. After the blending is complete, the slurry is dried, preferably by spray drying. Conventional spray drying equipment and operating procedures are employed. Drying gas outlet temperature is ordinarily used to control residual moisture content of the co-processed particulate material. Moisture levels of about 0.5% to about 8.0% are satisfactory with preferred levels being about 3.0% to about 5.0%. The particle size of the dried spheronizing compo- sition approximates that of the microcrystalline cellu¬ lose, although some of the crystallite aggregates may form clumps of larger particles. Spheroids are produced from the spheronizing mi¬ crocrystalline cellulose compositions of the invention following known spheronization procedures, including extrusion spheronization and rotogranulation/rotopro- cessing techniques. A dry blend of the composition and drug is first prepared. Water is then added slowly, with continuous mixing untii a granulation of the requi- site consistency is obtained. Alternatively, the drug, if it is water soluble, can be dissolved in the water, and this solution added to the MCC:hydrocolloid particu¬ late composition. The amount of the drug to be added is fixed by the loadings to which the spheres are suscepti- ble and may be predetermined by routine testing. The wet granulation is extruded using suitably sized pierced screens and spheronized using a rotating disk having a ground surface. The spheres are then dried in a fluidized bed or other drying means to a suitable moisture level, typically about 0.5% to 5%. As understood in the pharmaceutical art, the term "sphere" or "spheroid" means spherical particles having a diameter in the range of about 0.1 to 2.5 mm, more preferably from 0.5 to 2 mm and most preferably from 0.8 to 1.4 mm. The co-processed microcrystalline cellulose:- hydrocolloid composition of the invention affords a surprisingly higher percentage of spheroids in the nar¬ row 0.8-1.4 mm range than when the spheronization is carried out using a three component granulation of mi¬ crocrystalline cellulose, hydrocolloid and drug as called for in the prior art; see cited U.S. Patent Nos. 4,844,910; 4,867,985 and 4,867,987 supra. For some reason not presently understood, the interaction or affinity between the microcrystalline cellulose and hydrocolloid is not evident in the aforesaid three com- ponent system. Because of their excellent uniformity of size and sphericity, the spheroids produced with the spheronizing compositions of the invention can be evenly coated for precise controlled drug release. A further advantage of the invention is that the granulation of the herein co-processed composition is less susceptible to overwetting than is normally the case. This "forgiving feature" means that fewer batches of unacceptable granulated material will be produced, even with less experienced operators. Still another advantage is that the coprocessed compositions of the invention are not sticky, that is, do not stick to spheronization equipment, and therefore are adaptable to large, commercial scale, multi-batch spheronization operations. The spheronizing compositions of the invention can be used to form spheres with virtually all pharma¬ ceutical preparations and drugs, including combinations of drugs, and whether the drugs are water soluble or water insoluble. Typical of such drugs are the follow¬ ing: o Analgesics - acetaminophen, ibuprofen, keto- profen and the like, indomethacin, naproxen, acetaminophen with codeine and acetaminophen with propoxyphene napsylate. o Antibiotics - erythromycin, cephalosporins, minocyclir_e HC1. o Antiepileptics - phensuximide, phenytoin sodi¬ um and valproate sodium. o Antihista ines - chlorpheniramine maleate, diphenhydraaine hydrochloride, triprolidine hydrochloride. o Cough and Cold Drugs - dextromethorphan hydro- bromide, ephedrine sulfate, guaifenesin, phenylpropanolamine hydrochloride, prometha- zine hydrochloride, and pseudoephedrine hydro- chloride. o Cardiovascular Drugs - captopril, chlor- thiazide and hydrochlorthiazide, diltiazem, nadolol, papaverine hydrochloride, procain- amide hydrochloride, propranolol hydro- chloride, quinidine gluconate, quinidine sul¬ fate. o Gastrointestinal Drugs - cimetidine, loper- amide hydrochloride and ranitidine. o Respiratory Drugs - albuterol sulfate, amino- phylline, theophylline. The following examples illustrate the invention in greater detail. Example 1 PREPARATION OF SPHERONIZING COMPOSITION Methylcellulose (6.3 lb (2.86 kg) at 4% moisture) having a viscosity of 15 centipoise (Dow Chemical Co. Methocel ® A-15LV) was hydrated with 97.9 lb (44.4 kg) of water to form a solution containing 6% solids. The hydrocolloid was added slowly to the water with overhead stirring using a commercially available variable speed mixer. In a separate slurry tank, microcrystalline cellulose (274.7 lb (124.6 kg) of a 41.5% wet cake) was diluted with 287.8 lb (130.5 kg) of water. The microcrystalline cellulose was added to the water and dispersed using a high energy dispersator such as a Cowles mixer at 1500 RPM until a smooth cream-like slurry was formed. The methylcellulose solution was added to the microcrystalline cellulose with continued stirring for 40 minutes using the high energy mixer to form a uniform dispersion. The final slurry had a solids content of 18%. The slurry was then spray dried using a single fluid nozzle for atomization. The con- ditions used during the drying were 1500 psi (10.342 x 10 3 KPa) line pressure and a flow rate of 0.5 gpm. An outlet temperature of 230°F-240°F (110°C-115.6°C) was maintained. The production rate at these conditions was 46 lbs/hr (20.87 kg/hr.). Example 2 A co-processed material containing 95% microcrys¬ talline cellulose and 5% hydroxypropylmethyl cellulose was prepared using process and conditions similar to those described in Example 1. Example 3 A. PREPARATION OF SPHEROIDS OF PRESENT INVENTION The co-processed material described in Example 1 (95/5 microcrystalline cellulose/methylcellulose - MCC/MC) was used in the preparation of spheres contain¬ ing 80% theophylline using the process commonly referred to as extrusion/spheronization. The co-processed 95/5 MCC/MC (200 g) along with 800 g of anhydrous theophyl¬ line was charged into a 12 quart planetary mixer and allowed to mix for a period of 5 minutes until a homo¬ geneous mixture was achieved. To this mixture 600 g of water was added slowly with continued mixing for a period of 15 minutes allowing for sufficient distri¬ bution of the water throughout the mass. This process of wetting powders is commonly referred to as granula¬ tion. The so-obtained wet mass was then charged into the hopper of a Nica extruder. It was extruded through screens having 1.0 mm openings, at a speed of 14-16 RPM to form a pellet-like extrudate having an approximate length between 0.25 and 1.0 cm. The extrudate was then charged into the Nica spheronizer. This piece of equip¬ ment consists of a bowl having stationary side walls and a rotating bottom commonly referred to as the disk. The extrudate was processed in the spheronizer for a period of 8 minutes at a disk speed of 650 RPM. At the end of 8 minutes, the spheres were discharged into an appro¬ priate receptacle. The spheres were then transferred onto trays of a conventional forced air oven and dried at 50°C for a period of 6 hours. 90% of the so obtained spheroids were within the range of 0.8 to 1.4 mm. B. PRIOR ART SPHEROIDS Non-attrited microcrystalline cellulose (Avicel ® PH-101, FMC Corporation, 190 g) , methyl cellulose (10 g) and 800 g of anhydrous theophylline were dry blended and subjected to spheronization following the procedure of Example 3A. 73% of the so-obtained spheroids were within the size range of 0.8 to 1.4 mm. This Example illustrates the spheronizing procedure in which all three components aforesaid are spheronized as disclosed in cited U.S. Patent Nos. 4,867,985 and 4,867,987. C. PRIOR ART SPHEROIDS Non-attrited microcrystalline cellulose (Avicel ® PH-101, FMC Corporation, 200 g) and 800 g anhydrous theophylline were dry blended and subjected to spheronization following the procedure of Example 3A. 68% of the resulting spheroids were within the size range of 0.8 to 1.4 mm. This Example illustrates the spheronizing procedure in which microcrystalline is the sole spheronizing agent. As is readily apparent from the foregoing compara¬ tive Example 3, the percent of spheroids in the desired range of 0.8 - 1.4 mm is surprisingly greater using the spheronizing composition of the invention (Example 3A) than is obtained with the prior art compositions (Ex¬ amples 3B and 3C) .

Claims: CLAIMS : 1. A composition of matter, useful in preparing spheroids by spheronization, characterized by dried particulate particles of co-processed nonattrited micro- crystalline cellulose and a non-ionic hydrocolloid, the ratio of the two components being in a weight ratio of from 99:1 to 70:30 microcrystalline cellulose:hydro¬ colloid, the said components being in intimate associa¬ tion with one another. 2. The composition of claim 1 characterized in that the hydrocolloid is methyl cellulose and the weight ratio of the two components is in the range of from 97.5:2.5 to 90:10 microcrystalline cellulose:hydro¬ colloid. 3. The composition of claim 1 characterized in that the hydrocolloid is methyl cellulose and the weight ratio of the two components is in the range of from 96:4 to 94:6 microcrystalline cellulose:hydrocolloid. 4. The composition of claim 1 characterized in that the source of the microcrystalline cellulose com¬ ponent is wet cake. 5. The composition of claim 1 characterized in that the hydrocolloid is methyl cellulose. 6. The composition of claim 1 characterized in that the hydrocolloid component is hydroxypropylmethyl cellulose. 7. A process for producing a particulate mate¬ rial, useful in the preparation of spheroids by sphe¬ ronization, characterized by: forming a well dispersed slurry of non- attrited microcrystalline cellulose in an aqueous solu¬ tion of a non-ionic hydrocolloid, the amounts of micro¬ crystalline cellulose and hydrocolloid components being such as to provide a component ratio within the range recited below for the particulate co-processed product, and drying the aqueous slurry to yield a par- ticulate co-processed product wherein the weight ratio of nonattrited microcrystalline cellulose to hydrocol- - loid is in the range of from 99:1 to 70:30. 8. The process of claim 7 characterized in that the aqueous slurry is dried by spray drying. 9. The process of claim 7 characterized in that the microcrystalline cellulose is wet cake. 10. The process of claim 8 characterized in that the spray drying is carried out at a drier outlet tem- perature of from 230°F to 240°F (110°C to 115.6°C). 11. A method of producing a particulate sphe- ronized solid dosage form characterized by subjecting a blend of a drug and the composition of claim 1 to spheronization. 12. A method of producing a particulate sphe- ronized solid dosage form characterized by subjecting a blend of a drug and the composition of claim 2 to spheronization. 13. A method of producing a particulate sphe- ronized solid dosage form characterized by subjecting a blend of a drug and the composition of claim 3 to spheronization. 14. A method of producing a particulate sphe- ronized solid dosage form characterized by subjecting a blend of a drug and the composition of claim 4 to spheronization. 15. A method of producing a particulate sphe- ronized solid dosage form characterized by subjecting a blend of a drug and the composition of claim 5 to spheronization. 16. A method of producing a particulate sphe- ronized solid dosage form characterized by subjecting a blend of a drug and the composition of claim 6 to spheronization. 17. A solid dosage form characterized by spheres containing, in combination, the composition of claim l- and a pharmaceutically e fective amount of at least one drug. 18. A solid dosage form characterized by spheres containing, in combination, the composition of claim 2 and a pharmaceutically effective amount of at least one drug. 19. A solid dosage form characterized by spheres containing, in combination, the composition of claim 3 and a pharmaceutically effective amount of at least one drug. 20. A solid dosage form characterized by spheres containing, in combination, the composition of claim 6 and a pharmaceutically effective amount of at least one drug.

Inventors: ERKOBONI DAVID FRANK, FIORE SCOTT ALLAN, WHEATLEY THOMAS ALBERT, ERKOBONI, DAVID, FRANK, FIORE, SCOTT, ALLAN, WHEATLEY, THOMAS, ALBERT
Applicants: FMC CORP, FMC CORPORATION
Application year: 1992
Main classification: A61K9
IPC codes: A61K9, A61K47, C08J3, C08L1