Moulding A Reinforced Plastics Component

Abstract: In order to mould structural components where a resin is introduced into a mould containing a preform 24, the mould or tool halves 10, 12 are made as shells and have individually controllable heating circuits 34, 38, 52 around the mould surface. Different parts of the mould can therefore be held at different temperatures in order to ensure adequate resin flow to wet the whole of the preform.

Description: This invention relates to a method of moulding a reinforced plastics component, and to a tool for moulding such a component. The invention is specifically concerned with methods where the reinforcement for the component is made as a preform, and where the preform is placed in the mould cavity before a resin is introduced into the cavity. The preforming of the reinforcement allows the strength of the reinforcement to be designed in accordance with the ultimate loading of the finished component. The position and direction of the reinforcing fibres can be aligned and positioned as desired to achieve the desired structural strength of the finished component. The reinforcement can be made from a wide variety of different reinforcing materials, but typically glass fibres and carbon fibres are used. In the moulding of such a component, it is essential that the plastics resin which is introduced to the mould should thoroughly wet the reinforcement. The resin is conventionally introduced through a gate and flows through the preform to an edge of the mould. Air is displaced through the edges of the mould by the advancing resin front. Various processes are known for moulding reinforced plastics components in this way. The majority of such components falls under the category referred to as resin transfer moulding (RTM) where a polymerised resin is introduced into the mould. Such known moulding methods however have a number of disadvantages. In order to ensure thorough wetting of the preform, particularly around the edges of the mould, many known processes require a slow cure time so that the resin remains liquid and can flow over a long period. Long cycle times however are disadvantageous for volume production. Other methods use an excess volume of resin so that resin bleeds out of the mould around the edges, thus ensuring that the reinforcement at the edges of the mould is fully wetted, but requiring subsequent trimming of considerable flash and resultant wastage. The use of a shell tool for resin transfer moulding is disclosed in an article titled "Erkenntnisse bei der Weiterentwicklung des Vakuum-Injektionsverfahrens zur Herstellung hochleistungsfähiger Bauteile aus CFK" by H. Tengler (Kunststoffe Vol. 75, No. 2, February 1985, Pages 73-75). A method and apparatus for making a fibre reinforced article is proposed in document EP-A-0 320 302, in which a preform is placed in a mould cavity formed between two halves of a mould. Closure of the mould defines a matrix cavity in fluid communication with the mould cavity. Gas pressure causing excess matrix material to be forced into the mould cavity to eliminate voids and internal/external discontinuities. Processes for producing laminated plastics sheets are disclosed in documents DE-A-3536272 and DE-B-2535383 in which a series of plain and resin impregnated sheets are stacked in a mould and compressed. The mould is heated until the viscosity of the resin is reduced allowing the resin to penetrate through all further boards. Moulds are disclosed in documents DE-A-2017402 and JP-A-59-142108 which comprises heating pipes passing embedded in the mould, and in which the pipes may maintain the temperature of the pipes independently. It is an object of the present invention to provide a method and an apparatus for moulding a reinforced plastics component in which the flow of resin introduced into the mould cavity through the preform is controllable. According to the present invention the above object is attained by a method of moulding a reinforced plastics component, the method comprising the steps of placing a reinforcement preform in the mould cavity of a shell tool and introducing a plastics resin to the mould cavity through a gate characterised in that the gate and the edge of the mould are maintained at temperatures above the temperature of the body of the mould, so that the resin is able to flow freely at the edges of the mould to wet the preform. The invention also provides a shell tool for moulding a reinforced plastics component, the tool having an inner surface defining a mould cavity characterised in that the tool outer surface is exposed to ambient conditions and is provided with a plurality of independent heating circuits such that different parts of the tool can be maintained at different temperatures. Particular embodiments of the invention are disclosed in the dependant claims 3 to 7. The combination of a shell tool (which has a low thermal mass) with individual heating circuits for different parts of the tool, allows close local temperature control of the tool to optimise the flow patterns of the resin. Preferably the tool comprises two tool halves which meet around an edge region. The edge region preferably is arranged to leave a passage through which air can be expelled from the mould cavity, the passage being in the form of a narrow gap between the surfaces of the tool halves themselves. The tool, in the edge region, is preferably provided with heating means so that the temperature of the tool in the edge region can be raised. Working outwards from the tool cavity, the passage between the tool halves may include a very narrow gap through which air can flow and through which resin can just flow, followed by an expansion space, followed by a controlled mating face through which air can flow but through which resin cannot flow. The tool halves are preferably mounted in cast aluminium frames which allow the tool halves to be opened and closed. The invention will now be further described, by way of example, with reference to the accompanying drawings, in which: Figure 1 is a cross-section through part of a shell tool in accordance with the invention; Figure 2 is a detail of the tool wall construction, taken in the area indicated by the circle A in Figure 1; Figure 3 is a plan view of a tool in accordance with the invention showing gate and edge heating circuits; Figure 4 is a plan view corresponding to Figure 3 but showing heating circuits for the body of the tool; and Figure 5 shows a section through the tool wall construction of Figure 2, on the line V-V. The tool shown in Figure 1 consists of an upper tool half 10 or mould punch and a lower tool half 12 or mould die. The tool halves are made by electroforming onto a pattern manufactured in accordance with the desired component shape. As can be seen in Figure 2, the walls of the tool halves 10, 12 are made up of an inner skin 14 of nickel which is plated directly onto the pattern to a thickness of about 3mm, and an outer skin 16 of copper plated directly onto the nickel and also having a thickness of about 3mm making a total wall thickness of about 6mm for the shell tool walls. Shell tools are in themselves known. As will be apparent from the above description, they are relatively thin walled, and of a generally constant wall thickness over the whole tool surface. The use of nickel for the inner surface of the wall gives a good surface finish and a high level of hardness. Backing the nickel layer with a copper layer gives additional toughness. Also the copper layer is cheaper to lay down and plates out more quickly than the nickel layer. It is also easier to bond additional components to the copper surface than it would be to a nickel surface. In conventional shell tooling technology, the electrodeposition process is used to define the inner surface of the tool. However the outer surface of the tool is usually backed up with a substantial body of material which is either intended to or has the effect of increasing the thermal mass of the tool. As a result it is difficult to arrange for the tool to be at different temperatures at different points on the tool surface. However in the present invention, a low thermal mass is desirable so that different parts of the mould surface can be maintained at different temperatures, and there is no backing to the tool walls. The tool halves 10 and 12 are supported in cast aluminium backing frames 18, 20 only parts of which are shown in Figure 1. In order to obtain adequate support of the mould surfaces, to maintain seal integrity and to control the part thickness, additional copper is deposited in the regions 23, and these regions are machined flat prior to assembly with the support frames 18, 20. The adjacent surfaces of the support frames are also machined in this region. The interface between the frames and the mould parts is required to transmit compressive loads, to allow thermal movement and to prevent support frame witness marking, whilst providing a means of reacting shell breakaway forces in the event of component adhesion. As shown in Figure 1, this is accomplished by providing a nominal 5mm clearance between the tool halves 10, 12 and the support frames 18, 20 respectively, and filling these clearances with an epoxy resin 22 which is bonded to the support frames but not to the shell. Thus the joint cannot support tension or shear but can transmit compressive loads, allowing differential expansion between the shell and frame to occur unrestrained. The use of an epoxy resin filler also insulates the frame from the shell and prevents witness marking. A number of studs are electroformed into the rear face of the shell to provide fixture points. These studs are passed through holes drilled through bosses cast into the support frame, providing a number of fastening points to react shell breakaway forces. The support frame also includes mould guidance dowel pins, mould fixture holes and a set of handling/transportation clamps. In use, before the tool halves 10, 12 are placed together, a fibre reinforcement preform 24 is placed in the mould cavity. This preform will occupy substantially the whole of the mould cavity, extending up to the edges and to the opposite faces of the cavity and leaving just the interstices between the fibres to be filled with resin. The external surfaces of the tool halves 10 and 12 are in contact with ambient condition, and the temperature at a particular place within the mould cavity is influenced by a number of heating circuits which appear on the surface of the tool halves in the form of pipes 26. As can be seen in Figure 2, the pipes 26 can be attached to the outer surface of the tool by a bandage 28, for example in the form of a strip of resin-impregnated glass fibre or by an aluminium filled epoxy resin. A small thickness of glass fibre or epoxy resin such as the bandage 28, of low thermal mass, will not prevent the outer surface of the tool from being regarded as "exposed to ambient conditions". The preform 24 can be produced from any suitable reinforcing fibre. Carbon fibres or glass fibres are particularly suitable. In order to control the local temperature within the mould, a number of separate heating circuits are provided, as shown in Figures 3 and 4. The heating circuits are intended to be fed with hot oil. These Figures are plan views of a mould for a car body undershield. The outline of the mould itself is shown at 30 with heavy lines. A pin gate 32 is provided near the middle of the mould for the introduction of resin into the mould cavity. A first heating circuit 34 is provided around the gate and is fed with a heating medium through a pipe 36. A second heating circuit 38 is provided around the edge of the mould 30, to heat the flash gap 56, and is fed with heating medium through a pipe 40. The circuits 34 and 38 thus control temperatures of respectively the gate and the edge region. Flow through the pipes 36 and 40 is controlled by independent valves 42, 44. Figure 4 shows a multiplicity of separately controllable heating circuits for the main body of the tool. These circuits are fed from manifolds 48, 50 and each comprise a U-shaped pipe 52 extending over part of the surface of the tool. Each pipe is controlled by an inlet valve 54 which can be regulated in accordance with the desired temperature at which that part of the tool is to be maintained. Generally the temperatures in the manifolds 48, 50 will be lower than the temperatures in the circuits 34, 38. Returning now to Figure 1, the edge region of the tool has a flash gap 56 where the tool halves nearly close but leave a small gap between them. The flash gap is vertical to aid mould cleaning by the self-cleaning action of the component itself upon demoulding. Flash present at the end of the moulding cycle will be removed along with the component, minimising mould cleaning time. The vertical flash gap can also be worked during the final assembly of the mould to provide a restriction to resin flow whilst minimising the volume of resin to be cured. The thin flash on the moulded component can easily be removed by a shearing or similar operation. A large radius around the periphery of the mould die is used to pinch the preform between the punch and the die. This peripheral pinch-off would cause local deformation of the preform, permitting the preform into the cavity in the die. When the resin flows into the flash gap 56, it will do so in a very thin layer. At the same time the heating circuit 38 will ensure that this thin layer is heated to a relatively high temperature so that a rapid cure will take place resulting in a solidification of the resin in this gap 56. If resin flows through the gap 56 before setting occurs, then the excess resin will build up in an expansion gap 58 where the space between the two tool halves is slightly larger than in the gap 56. Beyond the expansion gap 58 is a region 60 where the tool halves 10, 12 are in metal to metal contact with one another. Air vents 59 are however provided through the metal to metal seal. An outer, backup seal 62 is also provided between the tool halves just in case there should be an escape of resin. Should it become desirable to control the cavity pressure subsequent to impregnation, a controllable air vent valve (not shown) can be fitted into the peripheral gallery formed between the metal to metal seal and the backup seal 62. In use, the preform 24 is placed in the mould cavity and the tool halves 10, 12 are closed. Resin is introduced into the mould through the gate 32 and flows radially outwardly in all directions towards the edge region. The resin is initially heated in the gate, to reduce its viscosity and to initiate the curing reaction, As resin flow continues, the hot resin from the gate will encourage flow through the preform 24, and this will be assisted by the heat applied to the rest of mould by the heating circuits 52. However as the resin reaches the edge of the mould, some extra help is needed to ensure that the resin thoroughly wets out the edges of the preform 24, and this is supplied by the heating circuit 38 which once again raises the temperature of the tool and lowers the viscosity so that both the edges of the preform are wetted out and the resin runs into the gap 56 to form a seal at the edges of the mould. Because of the construction of the mould edges with a narrow gap, an expansion space and a controlled mating face, no separate mould seal is required. This is a particular advantage on demoulding, because the mould will be very easy to clean, and any flash will be very easy to, remove. The mould cavity can usually be cleared before being prepared for the next cycle, simply by blowing any debris from around the edges away with an airline. For example, if the resin used has a curing temperature of 80°C, then the gate temperature maintained by the circuit 34 could be 120°C, the edge region temperature maintained by the circuit 38 would be 120°C and the rest of the mould would be maintained at 80°C. This scheme however will need modification and customising to each different shaped mould and different shaped component, to ensure complete wetting of the preform whilst keeping the cycle time as short as possible.

Claims: A method of moulding a reinforced plastics component, the method comprising the steps of placing a reinforcement preform (24) in the mould cavity of a shell tool (10,12) and introducing a plastics resin to the mould cavity through a gate (32) characterised in that the gate (32) and the edge (30) of the mould are maintained at temperatures above the temperature of the body of the mould, so that the resin is able to flow freely at the edges of the mould to wet the preform (24). A shell tool (10, 12) for moulding a reinforced plastics component, the tool (10, 12) having an inner surface defining a mould cavity characterised in that the tool outer surface is exposed to ambient conditions and is provided with a plurality of independent heating circuits (34, 38, 52, 54) such that different parts of the tool can be maintained at different temperatures. A shell tool as claimed in Claim 2, characterised in that an edge region (30) of the tool halves (10,12) defines a passage (56) through which air may be dispelled from the mould cavity. A shell tool as claimed in Claim 3, characterised in that the passage (56) is adapted to restrict the flow of resin therein. A shell tool as claimed in Claim 3 or Claim 4, characterised in that the passage (56) is in communication with an expansion space (58), being in communication with air vents (59) through which air may be dispelled. A shell tool as claimed in Claim 5, characterised in that the expansion space (58) is in communication with a region (60) in which the edges (30) of the tool halves (10,12) mate, the region (60) being adapted to prevent the flow of resin therein. A shell tool as claimed in any one of Claims 2 to 5, characterised in that the tool halves (10,12) are mounted in aluminium support frames (18,20).

Inventors: HARRISON ALAN ROBERTS, KENDALL KENNETH N C O FORD MOT, HARRISON, ALAN ROBERTS, KENDALL, KENNETH N., C/O FORD MOTOR COMPANY
Applicants: FORD FRANCE, FORD MOTOR CO, FORD WERKE AG, FORD FRANCE S. A., FORD MOTOR COMPANY LIMITED, FORD-WERKE AKTIENGESELLSCHAFT
Application year: 1992
Main classification: B29C70
IPC codes: B29C37, B29C33, B29C70