A method of coating a substrate with multiple layers of a coating

Abstract: An aqueous coating composition, comprising A) an aqueous anionic polyacrylate or polyurethane dispersion obtainable by dispersing 1) a polyacrylate resin, having functional groups selected from the group consisting of carboxylic acid groups, carboxylic anhydride groups or mixtures thereof in water in the presence of ammonia, or, 2) a fully reacted polyurethane resin, formed from the reaction of a glycol or polyol of polyester or polyether with a diisocyanate, and then neutralized with ammonia or other amine, and dispersed in water B) a phosphorous containing pigment C) additives selected from the group consisting of pigments, solvents, rust inhibitors, dispersants, surfactants or mixtures thereof. The coating composition is useful as a primer for metal substrates in combination with a waterborne basecoat to give a stable metallic effect.

Description: The present invention is directed to a method of coating a substrate with multiple layers of a coating, more specifically it is directed to a method of coating a substrate with multiple layers of a coating whose primary purpose is to prevent the galvanic degradation of overlaying waterborne coatings containing metallic pigments. Multi-layer systems have been utilized to coat automobiles for a number of years, but the early development of these systems necessarily employed organic solvents. As environmental regulations became more stringent organic-borne systems became less desirable. The recent research emphasis in the area of multi-layer systems, especially basecoat systems, has focused on the development of water-borne systems for multi-layer coatings. In particular, as organic-borne systems were formulated to require less and less organic solvent, becoming known in the industry as "high solids" coatings, it became obvious that the appearance, in particular the metallic effect of coatings containing metallic pigments, suffered with the increase in solids. One of the opportunities which water-borne systems presents is that of improving on the metallic effect in a coating which complies with the restrictions on volatile organic content. For example, the U.S. Pat No. 4,880,867 and 4,954,559 discloses an aqueous coating composition comprising a mixture of an acrylic dispersion and a polyurethane dispersion, which can be used as a primer or a basecoat. Water-borne systems, however, resulted in other problems. When waterborne coatings, which contain aluminum pigments are applied over steel substrates, scribed through the coating to bare steel, and exposed to a sodium chloride salt spray (ASTM B-117), the metallic effect disappears, leaving either the solid color of the coating or of the primer, if the coating contains no other pigments than the aluminum. This phenomenon is the result of the sodium chloride solution functioning as an electrolyte in the presence of the two dissimilar metals, e.g., the aluminum pigment and the steel substrate. The phenomenon is described is termed galvanic action. The object of the present invention was to provide a method of coating a substrate with multiple layers of a coating which does not show the above mentioned disappearance of the metallic effect. The objects of the present invention are achieved with a method of coating a substrate with multiple layers of a coating comprising applying a primer coat, topcoating this primer coat with a waterborne metallic basecoat composition and applying a clearcoat on this basecoat wherein an aqueous coating composition, consisting A) 20 to 65 % by weight of an aqueous binder dispersion obtainable by 1) dispersing a solution polymerized and/or bulk polymerized polyacrylate resin, having functional groups selected from the group consisting of carboxylic acid groups, carboxylic anhydride groups or mixtures thereof in water in the presence of ammonia, the polyacrylate resin is obtainable by polymerizing i) 1 to 30 % by weight of an ethylenically unsaturated carboxylic acid or anhydride or mixtures thereof ii) 20 to 90 % by weight other ethylenically unsaturated monomers iii) 0 to 50 % by weight of an ethylenically unsaturated monomer with a functional group other than carboxylic acid group or carboxylic anhydride group and/or 2) dispersing in water a fully reacted polyurethane resin which is neutralized with ammonia or other amine and formed from the reaction of a glycol or polyol of polyester or polyether with a diisocyanate, B) 5 to 15 % by weight of a phosphorous containing pigment which is selected from the group consisting of zinc phosphate, calcium barium phosphosilicate, zinc molybdenum phosphate, calcium strontium phosphosilicate, calcium strontium zinc phosphosilicate, or mixtures thereof and C) 20 to 65 % by weight additives selected from the group consisting of pigments, solvents, rust inhibitors, dispersants; surfactants or mixtures thereof is applied as primer coat. EP-A-157 133 relates to a binder for aqueous anticorrosive paints based on poly(meth)acrylate latices and water soluble zinc complex salts. EP-A-208 194 discloses a binder based on a styrene alkyl(meth)acrylate copolymer dispersion which comprises a monoalkylphosphate and an ethoxylated alkyl phenol. In EP-A-389 653 an anticorrosive pigment composition is disclosed which comprises a slightly water-soluble condensed phosphoric acid salt and at least one compound selected from the group consisting of zinc compounds, boric acid compounds and lead compounds. Suitable polyacrylate resins according to the invention comprise: i) 1 to 30% by weight of an ethylenically unsaturated carboxylic acid or anhydride or mixtures thereof ii) 20 to 90% other ethylenically unsaturated monomers iii) 0 to 50% by weight of an ethylenically unsaturated monomer with a functional group other than the carboxylic acid group or the carboxylic anhydride group. Preferred polyacrylate resins comprise: i) 1 to 20% by weight of an ethylenically unsaturated carboxylic acid or anhydride or mixtures thereof ii) 40 to 85% other ethylenically unsaturated monomers iii) 2 to 40% by weight of an ethylenically unsaturated monomer with a functional group other than the carboxylic acid group or the carboxylic anhydride group. Most preferred polyacrylate resins comprise: i) 3 to 15% by weight of an ethylenically unsaturated carboxylic acid or anhydride or mixtures thereof ii) 55 to 85% other ethylenically unsaturated monomers iii) 5 to 30% by weight of an ethylenically unsaturated monomer with a functional group other than the carboxylic acid group or the carboxylic anhydride group. Suitable ethylenically unsaturated carboxylic acid monomers (i) are acrylic acid, methacrylic acid, acryloxypropionic acid or polyacrylic acid mixtures, methacrylic acid dimer or polymethacrylic acid mixtures, crotonic acid, fumaric acid, maleic acid or maleic anhydride, itaconic acid or itaconic anhydride, and monoalkylesters of maleic, itaconic or fumaric acids. The other ethylenically unsaturated monomers (ii) may be chosen from acrylic or methacrylic alkyl ester derived from alcohols having 1 to about 20 carbon atoms, or vinyl monomers. The expression (meth)acrylate with parenthesis as used herein includes methacrylate and acrylate. Suitable examples are methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, n-butyl (meth)acrylate, isobutyl (meth)acrylate, t -butyl (meth)acrylate and 2-ethylhexyl (meth) acrylate, maleic acid or fumaric acid dialkylesters in which the alkyl groups have 1 to 20 carbon atoms, vinylaromatics such as styrene, α-methylstyrene, vinyltoluene, t -butylstyrene, halogenated vinylbenzenes such as chlorostyrene, and other monomers like vinylchloride, (meth)acrylamide and (meth)acrylonitrile. Examples of ethylenically unsaturated monomers with a functional group other than the carboxylic acid group or the carboxylic anhydride group (iii) are hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, isocyanatoethyl methacrylate, hydroxybutyl (meth)acrylate, propylene glycol monoacrylate, 2,3-dihydroxypropyl methacrylate, pentaerythritol monomethacrylate, propyleneglycol monoacrylates, and m -isopropenyl-α,α-dimethylbenzyl isocyanate. Other examples of (iii) are maleic acid and fumaric acid dihydroxyalkyl esters in which the straight chained, branched or cyclic alkylgroup contains 2 to 20 carbon atoms. N-hydroxyalkyl(meth)acrylamides and N-hydroxyalkylfumaric acid mono- or diamides may also be used, e.g., N-hydroxyethylacrylamide or N-(2-hydroxypropyl)-methacrylamide. Other hydroxyl group containing compounds include allylalcohol, monovinylethers of polyols, especially diols, such as monovinylethers of ethylene glycol and butanediol, and hydroxyl group containing allyl ethers or esters such as 2,3-dihydroxypropylmonoallylether, trimethylolpropane monoallylether or 2,3-dihydroxypropanoic acid allylester. Copolymerization is carried out using conventional techniques such as heating the monomers in the presence of a polymerization initiating agent and optionally chain transfer agents. The copolymerization is be carried out in bulk or solution. For the present invention some solvent is present to act as a cosolvent during dispersion. Suitable solvents for solution polymerization are ethylene glycol or propylene glycol and their derivatives, such as dipropylene glycol monomethyl ether and ethylene glycol monobutyl ether acetate; alcohols, such as butyl alcohol and diacetone alcohol; ketones, such as methyl propyl ketone and acetone; esters, such as butyl acetate and pentyl propionate; ethers, such as dioxane and tetrahydrofuran; and other compatible solvents, such as water and N-methyl pyrrolidone and mixtures thereof. One preferred mixture is ethylene glycol monobutyl ether and water. Typical initiators are peroxides such as dialkylperoxides, peroxyesters, peroxydicarbonates, diacylperoxides, hydroperoxides, and peroxyketals and azo compounds such as 2,2'-azobis(2-methylbutanenitrile) and 1,1'-azobis (cyclohexanecarbonitrile). Typical chain transfer agents are mercaptans such as octylmercaptan, n - or t -dodecylmercaptan; halogenated compounds; thiosalicylic acid, mercaptoacetic acid, mercaptoethanol, buten-1-ol, and dimeric alpha-methylstyrene. Mercaptans are preferred. The reaction is usually carried out at temperatures from about 20°C to about 200°C. The reaction may conveniently be done at the temperature at which the solvent or solvent mixture refluxes, although with proper control a temperature below the reflux may be maintained. The initiator should be chosen to match the temperature at which the reaction is carried out, so that the half-life of the initiator at that temperature should preferably be between one minute and thirty minutes. The solvent or solvent mixture is generally heated to the reaction temperature and the monomers and initiator(s) are added at a controlled rate over a period of time, usually between 2 and 6 hours. A chain transfer agent or additional solvent may be fed in also at a controlled rate during this time. The temperature of the mixture is then maintained for a period of time to complete the reaction. Optionally, additional initiator may be added to ensure complete conversion. The acid number of the polyacrylate is from about 5 to about 230mg KOH/g, preferably from about 7 to about 156mg KOH/g, most preferably from about 23 to about 117mg KOH/g. The polyacrylate has a weight average molecular weight of from about 4,000 to about 2,000,000, preferably from about 20,000 to about 400,000. The theoretical Tg of the polyacrylate is from about -30°C to about 150°C, preferably from about 20°C to about 75°C, and most preferably from about 30°C to about 65°c. The polyacrylate is partially or fully neutralized with ammonia and then diluted with deionized water under agitation to yield a finely divided dispersion. In another method, the polyacrylate is diluted in aqueous ammonia to yield a finely divided dispersion. The aqueous anionic polyacrylate dispersion has a solid content from about 35% to about 65% by weight, preferably from about 40% to about 45% by weight. Examples of commercially available polyacrylate dispersions are Synthemul 40-424 (Reichhold Chemicals Inc., Reaserch Triangle Park, NC), and Rhoplex WL-91 (Rohm & Haas Inc., Philadelphia, PA). Polyurethane dispersions that are used in the invention are formed by reacting a polyester, polyether, polycarbonate, polylactone or polyacrylate containing terminal hydroxy functional groups with a diisocyanate such that the resulting intermediate product has terminal isocyanate groups. These isocyanate groups of the intermediate are then reacted with a compound that is reactive with the isocyanate groups and has at least one group that is capable of forming an anion. This group is subsequently neutralized with a tertiary amine to form a water dispersible polyurethane which is then dispersed in water and chain-extended with a diamine by the reaction of the diamine with unreacted isocyanate groups of the polyurethane A process for making such polyurethanes in aqueous dispersion is disclosed in Drexler et al U.S. Pat No. 4,489,135 issued Dec 18, 1984 which is hereby incorporated by reference. Examples of typical polyester polyols that can be used are formed by the reaction of a polyol with a dicarboxylic acid or an anhydride. Useful acids include succinic acid, adipic acid, maleic acid, azelaic acid, phthalic acid, isophthalic acid and anhydrides of these acids. Useful diols include ethylene glycol, butylene glycol, neopentyl glycol, hexane diol or mixtures of any of the above. Suitable diisocyanates that may be used include toluene diisocyanate, tetramethylene diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate, ethylethylene diisocyanate, 2,3-dimethylethylene diisocyanate, 1-methyltrimethylene diisocyanate, 1,3-cyclopentylene diisocyanate, 1,4-cyclohexylene diisocyanate, 1,3-phenylene diisocyanate, 4,4-biphenylene diisocyanate, 1,5-naphthalene diisocyanate, bis-(4-isocyanatocyclohexyl)-methane, bis-(4-iso-cyanatocyclophenyl)-methane, 4,4-diisocyantodiphenylether, tetramethylxylene diisocyanate and the like. Compounds that are reactive with the isocyanate groups and have a group capable of forming an anion may be chosen from dihydroxypropionic acid, dimethylolpropionic acid, dihydroxysuccinic acid and dihydroxybenzoic acid. Other suitable compounds include the polyhydroxy acids that can be prepared by oxidizing monosaccharides, for example, gluconic acid, saccharic acid, mucic acid, glucuronic acid and the like. Suitable tertiary amines which can be used to neutralize the acid and form an anionic group to enable water dispersability are trimethylamine, triethylamine, dimethylamine, diethylamine, triphenylamine, dimethylethanolamine and the like. Diamines that can be used for chain extension of the polyurethane to give N-alkyurea groups include ethylenediamine, diaminopropane, hexamethylene diamine, hydrazine and aminoethylethanolamine. Typical polylactones that can be used to form the polyurethane can be lactones such as caprolactone reacted with a diol. Other useful lactones can be represented by the formula in which n is preferably 4 to 6 and Z is hydrogen, an alkyl radical, a cycloalkyl radical or an alkoxy radical and does not contain more than 12 carbon atoms. The most preferred lactone is ε-caprolactone since it is readily available and provides a coating with excellent properties. Typical aliphatic diols that can be used to make the polylactone are ethylene glycol, 1,3-propanediol, 1,4-butanediol and dimethylolcyclohexane. Useful polyethers that can be used to form the polyurethane are polypropylene glycols having an average molecular weight of about 400-4500. Typical polypropylene glycols that can be used are those designated as Niax® 425, 2025, 3025, 4025 (available from Union Carbide) and the like. (The numbers designate the molecular weight of the polyproylene glycols). Suitable hydroxyl terminated polyacrylates that can be used to form the polyurethane are prepared by ethylenic polymerization of acrylic esters such as the aforementioned alkyl acrylates or methacrylates with ethylenic unsaturated monomers containing functional groups such as carboxyl, hydroxyl, cyano groups and/or glycidyl groups. Any of the aforementioned alkyl acrylates or methacrylates can be used. These polylactones, polyethers or polyacrylates are reacted as shown above for the polyester to form an aqueous polyurethane dispersion. Examples of commercially available aqueous polyurethane dispersions are NeoRez R-960 (ICI Resins US, Wilmington, Mass.), and Spensol L-52 (Reichhold Chemicals Inc.). Component (A) is used in the coating composition in an amount of 20% to 65%, preferably 30% to 40% by weight, based on the final aqueous coating composition. The phosphorous containing pigment (B) could be an inorganic phosphate or phosphosilicate like zinc phosphate, calcium barium phosphosilicate, zinc molybdenum phosphate, calcium strontium phosphosilicate, zinc aluminum phosphate, calcium strontium zinc phosphosilicate or mixtures thereof. Preferably used are zinc phosphate, calcium strontium phosphosilicate, calcium strontium zinc phosphosilicate and zinc molybdenum phosphate. The component (B) is used in an amount of about 5% to 15% by weight, preferably from 8.5% to 10% by weight, based on the final aqueous coating composition. The additives (C) are selected from the group consisting of pigments, solvents, rust inhibitors, dispersants, surfactants or mixtures thereof. The component (C) is used in the coating composition in an amount of 20% to 65%, preferably 30% to 40% by weight, based on the final aqueous coating composition. All pigments known in the art, could be used in the coating composition of the present invention. Suitable pigments are for example talcum, china clay, titanium dioxide, carbon black, silica, magnesium silicate, barytes and the like. Preferred are talc, clay, titanium dioxide and carbon black. The pigments could be used in an amount of from 5% to 35% by weight of the final coating composition. Suitable solvents for the coating composition of the present invention are aromatics like toluene, xylene or mixtures of aromatics like Solvesso 150 (Chemcentral Company), ether alcohols like butoxy ethanol, methoxy propanol, t -butoxy proponol, butoxy propanol, esters like alkylacetates of C 1 to C 20 alcohols, alcohols such as isopropanol and sec-butanol, and the like. Solvents could be used in an amount of from 3% to 9% by weight, preferably from 5% to 7% by weight, based on the final aqueous coating composition. Other additives like defoamers, rust inhibitors, dispersants, surfactants, plasticizers, rheology modifiers, and others known in the art could be used in an effective amount. To prepare the final aqueous coating composition, component (B) and (C) are mixed in the abovementioned relation into the aqueous anionic polyacrylate dispersion (A) under agitation. The final coating composition is adjusted to a pH of 8 to 9 with ammonia. Viscosity may be adjusted using deionized water. The solid content of the final aqueous coating composition is from 20% to 65% by weight, preferably from 40% to 55% by weight. The aqueous coating composition described hereinabove can be applied as a primer to a variety of substrates, such as cold rolled steel, phosphated steel, previously painted substrates and plastic substrates such as polyester reinforced fiberglass and reaction injection molded urethane, in one or more coats using for example an air atomizer (DeVilbiss Model JGA-502 spray gun, or Model JGHV-530 HVLP spray gun, available from DeVilbiss Company, Toledo, OH.), or by using other conventional spraying means. The coating composition may also be applied electrostatically. The primer is applied in a film thickness (dry film) of 38,1 (1.5) to 76,2 (3), preferably 50,8 (2.0) to 63,5 µm (2.5 mils). The drying conditions are not critical and are between 10 to 93,3°C (50° to 200° F) and 5% to 90% relative humidity for 30 to 90 minutes, dependant on conditions. The VOC (volatile organic content as defined by ASTM D3960) of the primer is less than 252,4 g/l (2.1 lbs/gal) (less water), preferably less than 228,4 g/l (1.90 lbs/gal) (less water). This primer can be topcoated with most refinish coatings known in the art, but especially with waterbome basecoats in order to eliminate the disappearance of the metallic effect. Any clearcoat known in the art may be applied on this basecoat. Preparation of the coating composition. A. Millbase preparation: A coating composition is prepared by first loading the liquid portion of the mill charge into a pebble mill. Then the pigments are loaded into the mill. The mill is then run for 36 hours, or until a pigment grind of 25 - 30 µm (microns) is obtained. B. Primer Preparation: The remaining ingredients were then added to the pebble mill, and the grind portion and letdown portion are mixed in the mill for an additional 2 hours. Properties of the Coating Composition The resulting primer composition(s) had the following physical properties: Viscosity - #4 Ford Cup (25°C) 40-50 seconds pH 9.0 - 9.5 V.O.C. 204,4 - 234,4 g/l (1,70 - 1,95 lbs/gal) Pigment/Binder Ratio 1.80 - 2.00 Weight/l 2,78 - 2,84 Solids by Weight 43.5% - 49.0% The resulting primer was sprayed onto cold-rolled steel panels and dried at ambient conditions 21°C ((70°F) and 50% relative humidity) for 60 minutes. The primer had a dry film thickness of 55,9-63,5 µm (2.2 - 2.5 mils). The primer was then dry sanded with a dual action (DA) orbital sander using 400 grit paper to a thickness of 50,8-55,9 µm (2.0 - 2.2 mils) to obtain an ideal surface for the appearance of the topcoat. (The performance results were the same if the primer is left unsanded). The panels were then coated with a waterborne metallic basecoat composition followed by a two component, low VOC (<420,7 g/l) ((<3.5 Lbs/Gal)) acrylic urethane clearcoat, by spray application, and cured for 7 days at ambient conditions. The basecoat was applied at 10,16-22,86 µm (0.4 - 0.9 mils) dry film thickness and the clear coat had a dry film thickness of 48,26-58,42 µm (1.9 - 2.3 mils). Properties of the Coating's Film The cured panels had the following properties: Primer dry film build 50,8-55,9 µm (2.0 - 2.2 mils) Appearance, visual Excellent Gloss (20° angle) 93 + Distinctness of Image 90 + Adhesion (ASTM D3359) 5B Humidity Resistance (96 hours @ 38°C, 100% RH) Blistering - none Corrosion Resistance (240 hours salt spray, ASTM B-117) Blistering - none Adhesion - 5B No loss of metallic effect Creepage - < 1mm

Claims: A method of coating a substrate with multiple layers of a coating comprising applying a primer coat, topcoating this primer coat with a waterborne metallic basecoat composition and applying a clearcoat on this basecoat wherein an aqueous coating composition, consisting of A) 20 to 65 % by weight of an aqueous binder dispersion obtainable by 1) dispersing a solution polymerized and/or bulk polymerized polyacrylate resin, having functional groups selected from the group consisting of carboxylic acid groups, carboxylic anhydride groups or mixtures thereof in water in the presence of ammonia, the polyacrylate resin is obtainable by polymerizing i) 1 to 30 % by weight of an ethylenically unsaturated carboxylic acid or anhydride or mixtures thereof ii) 20 to 90 % by weight other ethylenically unsaturated monomers iii) 0 to 50 % by weight of an ethylenically unsaturated monomer with a functional group other than carboxylic acid group or carboxylic anhydride group and/or 2) dispersing in water a fully reacted polyurethane resin which is neutralized with ammonia or other amine and formed from the reaction of a glycol or polyol of polyester or polyether with a diisocyanate, B) 5 to 15 % by weight of a phosphorous containing pigment which is selected from the group consisting of zinc phosphate, calcium barium phosphosilicate, zinc molybdenum phosphate, calcium strontium phosphosilicate, calcium strontium zinc phosphosilicate, or mixtures thereof and C) 20 to 65 % by weight additives selected from the group consisting of pigments, solvents, rust inhibitors, dispersants, surfactants or mixtures thereof is applied as primer coat. A method according to claim 1, wherein the ethylenically unsaturated carboxylic acid is selected from the group consisting of acrylic acid, methacrylic acid, acryloxypropionic acid, polyacrylic acid mixtures, methacrylic acid dimer, polymethacrylic acid mixtures, crotonic acid, fumaric acid, maleic acid, monoalkylesters of maleic, fumaric, itaconic acids or mixtures thereof. A method according to claim 1, wherein the ethylenically unsaturated carboxylic anhydride is selected from the group consisting of maleic anhydride, itaconic anhydride or mixtures thereof. A method according to claim 1, wherein said ethylenically unsaturated monomer (iii) is selected from the group consisting of hydroxyethyl acrylate, hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, isocyanatoethyl methacrylate, hydroxybutyl acrylate, hydroxybutyl methacrylate, m-isopropenyl-α,α-dimethylbenzyl isocyanate, allylalcohol, polypropyleneglycol monoallylether or mixtures thereof. A method according to claim 1, wherein the polyacrylate resin has an acid number of 0 to 230 mg KOH/g. A method according to claim 1, wherein the polyacrylate resin has a weight average molecular weight of from 4,000 to 4,000,000. A method according to claim 1, wherein the polyacrylate resin has a theoretical T G of from -30°C to 150°C. A method according to claim 1, wherein the solvents are selected from the group consisting of toluene, xylene, mixtures of aromatics, butoxy ethanol, methoxy propanol, t-butoxy propanol, aceticesters of C 1 to C 20 alcohols, alcohols or mixtures thereof. A method according to claim 1, wherein the pigments are selcted from the group consisting of talcum, titanium dioxide, carbon black, silica, clays, magnesium silicate, barytes, or mixtures thereof. A method according to claim 1, wherein the total solid content is from 20% to 65% by weight of the complete aqueous coating composition.

Inventors: COWLES RICHARD A, FINKENAUER HORST J, KOEVENIG BRIAN P, COWLES, RICHARD A., FINKENAUER, HORST J., KOEVENIG, BRIAN P.
Applicants: BASF CORP, BASF CORPORATION
Application year: 1992
Main classification: C09D5
IPC codes: C08K3, C08G18, C09D133, C09D5, C09D175