Epoxy imidazole adduct and epoxy resin composition

Abstract: An adduct of a glycidyl ester of an alpha,alpha branched saturated monocarboxylic acid containing a total of from 5 to 18 carbon atoms and 2-isopropylimidazole and to epoxy resin compositions comprising said adducts.

Description: The invention relates to an adduct of a glycidyl ester of an alpha,alpha branched saturated monocarboxylic acid containing a total of from 5 to 18 carbon atoms and 2-isopropylimidazole and to epoxy resin compositions comprising said adducts. Imidazole compounds having a secondary amino group in the ring and salts or adducts of such imidazole compounds have been proposed as accelerators in epoxy resin/curing agent systems. US patent No. 3,756,984 relates to the preparation of a whole range of adducts of mono- and polyepoxides with imidazoles having a secondary amino group in the ring and to the use of such compounds alone as curing agent or in combination with other conventional curing agents in epoxy resin compositions, particularly in epoxy resin moulding powders or in epoxy resin powder coating compositions. The epoxy-imidazole adducts reported in said US patent are in general good curing agents and accelerators for the anhydride curing of polyepoxides. However in certain epoxy resin systems, such as for example epoxy resin solventless prepreg matrix systems for fibre reinforced composites, not just any type of epoxy-imidazole adduct can be used effectively as curing compound or accelerator. The object of the invention is to find a compound which is particularly useful for the acceleration of epoxy resin/curing agent systems for solventless prepreg applications. Such systems require an accelerator, which is liquid at room temperature and whereof the mixing ratio is between 0.75% and 10% by weight of accelerator, based on the total weight of the epoxy resin composition, in view of the mixing efficiency and in order to reduce a potential plasticizing effect. Also the epoxy resin/curing agent/accelerator system should have a long shelf life, good reactivity at elevated temperature and high glass transition temperature. The invention therefore relates to an adduct of a glycidyl ester of an alpha,alpha branched saturated monocarboxylic acid containing a total of from 5 to 18 carbon atoms and 2-isopropyl-imidazole and to the epoxy resin compositions comprising said adduct. The invention further relates to epoxy resin compositions comprising one or more epoxy compound(s) having an average of at least 1 epoxide group per molecule and an adduct of the invention. It was found that epoxy resin compositions comprising the adduct of the invention show an outstanding combination of good storage stability, high Tg, and good reactivity. The adducts of the invention are liquid at room temperature and mixing ratios can be applied in epoxy resin formulations which enable the use of commercial mixing equipment. The glycidyl esters to be used in the preparation of the adduct of the invention may suitably be any/ or a mixture of the glycidyl esters of the alpha, alpha branched saturated monocarboxylic acids having a total of from 5 to 18 carbon atoms. Preferably the glycidyl ester used is a mixture of glycidyl esters of alpha,alpha branched saturated monocarboxylic acids having a total of from 9 to 18 carbon atoms whereof the main constituents are the glycidylesters of alpha,alpha branched saturated monocarboxylic acids having a total of from 9, 10 or 11 carbon atoms, known as CARDURA E10 (CARDURA is a trademark). The adducts can be prepared by mixing the glycidyl ester and the imidazole compound in a molar ratio of from 0.5 to 2.0, at a temperature of from room temperature to 150 °C, preferably of from 100 to 150 °C for a period of time which may vary, depending on the temperature, from 0.1 hours to 24 hours, preferably of from 1 to 5 hours. The adduct so obtained can be used in epoxy resin compositions alone or in combination with a co-curing compound. The epoxy resin composition will suitably comprise of from 0.05 to 20 parts by weight (pbw), preferably 0.5 to 10 pbw, of the adduct of the invention per 100 pbw of the epoxy resin plus co-curing compound (if present). The epoxy resins to be used in the epoxy resin composition of the invention are in general those compounds having on average more than one epoxy group per molecule. The number of epoxy groups per molecule is obtained by dividing the average molecular weight of the epoxy resin by its epoxide equivalent weight (EEW). Preferred epoxy resins are glycidyl ethers of polyhydric phenols such as diphenylol alkanes e.g. 2,2-bis(4-hydroxyphenyl)propane (bisphenol-A or BPA), 1,1-bis(4-hydroxyphenyl)ethane, and bis(4-hydroxyphenyl)methane, 4,4'-dihydroxydiphenyl sulphone, hydroquinone, resorcinol, dihydroxydiphenyl, dihydroxy naphthalenes and polyhydric phenols such as novolacs and resols prepared by condensation of phenol or cresols with formaldehyde. Other epoxy resins are glycidyl ethers of halogenated mono, di- or polynuclear phenols such as for example EPIKOTE 1047 or EPIKOTE 1141 (EPIKOTE is a trademark); glycidated amines, aminophenols and amides; glycidated polyacids; and epoxy cyclohexyl and cyclopentyl compounds. Mixtures of polyepoxides as described above and mixtures with monoepoxides may also be used. The choice of epoxy resin(s) depends on the final application of the epoxy resin composition of the invention. Particularly preferred epoxy resins are the polyglycidyl ethers of BPA having an EEW of from 140 to 400, such as for example EPIKOTE 828, a liquid bisphenol A-epichlorohydrin epoxy resin having an EEW of from 182 to 194. The epoxy resin compositions of the invention may further comprise a co-curing compound. Suitable co-curing compounds are phenols, mercaptans, polycarboxylic acids and their anhydrides, phosphines, amino compounds, amine salts and quaternary ammonium salts. Examples of suitable amines that can be used in combination with the adduct of the invention are aliphatic monoamines such as dimethyl ethanolamine, methyl diethanolamine, morpholine, stearyl dimethylamine, tri-n-hexylamine; aliphatic polyfunctional amino compounds such as ethylene diamine, diethylene triamine, N,N-dimethyl aminopropylamine, dicyandiamide, guanidine, and amidines; cycloaliphatic amines such as di(4-aminocyclohexyl)methane, di(3-methyl-4-aminocyclohexyl)methane, and 1-amino-3-aminomethyl-3,5,5-trimethyl cyclohexane (isophoronediamine); aromatic primary and secundary amines such as p,p'-bis-(aminophenyl)methane, p,p'-bis(aminophenyl)sulphone, m-phenylene diamine, diethylene diaminetoluene; ortho alkylated primary aromatic amines such as 4,4'-methylenebis(2,6-diethyl aniline), and 4,4'-methylenebis(2,6-diisopropyl aniline). Polycarboxylic acid anhydrides that can be used in combination with the adduct of the invention are phthalic anhydride, tetrahydrophthalic anhydride and its alkylated compounds, hexahydrophthalic anhydride and its alkylated compounds, succinic anhydride and trimellitic anhydride. Preferred co-curing compounds are dicyandiamide and orthotoluene biguanidine. The co-curing compounds are generally employed in amounts varying according to the nature and the equivalent weights of co-curing agent and epoxy resin present in the epoxy resin composition of the invention. Polycarboxylic acid anhydrides are preferably used in a ratio higher than 0.8 usually between 1.0 and 2.3 acid equivalents per epoxide equivalent. Amino compounds having more than one hydrogen atom attached to nitrogen are preferably used in a ratio of from 0.8 to 1.2 active hydrogen equivalents per epoxide equivalent. The epoxy resin composition of the invention may further comprise other additives such as solvents, diluents, pigments, fillers, fibrous materials, dyes, resins, polyolefins, plasticizers and non-volatile extenders such as coal tar pitch, asphaltic bitumen, pine oil, pine tar, oils and aromatic extracts thereof. In order to improve the storage stability of the epoxy resin composition organic- or inorganic acid compounds can be added thereto in a substantially equivalent amount with respect to the imidazole adduct, examples of such acids are phosphoric acid, benzoic acid, paratoluene sulphonic acid and salicylic acid. In general the epoxy resin composition of the invention can be prepared by mixing the epoxy resin with the adduct of the invention by gentle heating or by dissolving the components in a solvent. Suitable solvents are ketones, such as acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl cyclohexanone and diacetone alcohol, esters such as ethyl acetate, and n-butyl acetate; glycol ethers such as ethylene glycol monomethyl ether and acetates thereof. Suitable diluents are benzene, toluene, xylene and liquid monoepoxides. The temperatures employed during cure may vary over a wide range. Preferred temperatures range of from 50 to 250 °C. The epoxy resin compositions of the invention can be used to make composites such as laminates, castings, moulded articles and coatings. The epoxy resin compositions of the invention are particularly suitable as solventless prepreg matrix systems for fibre reinforced composites. For that purpose fibrous material such as glass filaments, mats or cloth is impregnated with the epoxy resin composition of the invention. The resulting impregnated glass fibre material may be stored for some time. The eventual laminate is made by shaping the fibrous material to a lay-up and curing the resulting lay-up structure at elevated temperature. It was found that lay-up's comprising the epoxy resin composition of the invention show an excellent storage stability and reactivity. Fibre mats or cloth impregnated with the compositions may be superimposed and the assembly, or lay-up cured under heat and pressure at temperatures of from 50 to 300 °C and pressures of from 1.75 to 35 or more kg/cm². The invention is illustrated below. EXPERIMENTAL PROCEDURES (I) Preparation of imidazole/glycidyl ester adduct An amount of imidazole was loaded into a reactor and heated to 135 °C. The temperature was increased to 140 °C while stirring. Next a stoichiometric amount of a glycidyl ester of an alpha,alpha branched saturated monocarboxylic acid was gradually pumped into the reaction mixture over a period of 4 hours, while keeping the reaction mixture at 140 °C. Thereafter a postreaction of 45 minutes at 145 °C was carried out. Then the product was cooled to 100 °C and dumped. (II) Preparation of a prepreg For the determination of the Kofler reactivity and the glass transition temperature (Tg) a sheet of prepreg was prepared using the following procedure: A sheet of release paper was put on a temperature controlled aluminium plate at 50 °C. On top of the release paper a sheet of glass cloth (100 g/cm²) was clamped and allowed to warm up for at least 5 minutes. The epoxy resin composition at room temperature was poured at the top of the sheet of glass cloth and filmed with a bar coater. Then a second sheet of release paper was laid on the film and impregnation was enhanced by rolling the package with a steel handroller. The filming and impregnation procedure was carried out in 60 seconds. (III) Screening tests 1) Brookfield viscosity at 25 °C, to determine the viscosity of the adduct. 2) Tecam gel time at 60 °C (SMS 2381-74), to assess the shelflife of the epoxy resin composition. 3) Hot Plate Gel Time (HPGT) at 150, 160 and 170 °C, the "time to no string" (ttns) is measured to evaluate reactivity of the epoxy resin composition. 4) The Kofler gel temperature after 60, 120, 240 and 480 seconds, to evaluate the reactivity of the prepreg. The procedure for the determination of the Kofler gel temperature was as follows: The temperature gradient of the Kofler bench was set from 250 to 35 °C. Four mm wide strips with a length of 30 cm were placed on the bench. After a predetermined time of 60, 120, 240 and 480 seconds one of the strips was removed from the bench in a ripping movement starting at the low temperature end. The gelation point was defined as the point where the force to remove the strip of prepreg suddenly increases and the matrix system is no longer left on the surface of the bench. At this point the temperature was determined using a thermocouple. 5) Glass rubber transition temperature (Tg) measured by Dynamical Mechanic Analysis (DMA) or Differential Scanning Calorometry (DSC) as indicated. 6) Reaction kinetics were determined using a Dupont 912 DSC, heating rate 10 °C/min. EXPERIMENTS The following adducts (A and B according to the invention and C for comparison) were prepared as described in (I) above. A) CE10/IPI: adduct of CARDURA E10 and 2-isopropyl imidazole B) CE5/IPI: adduct of CARDURA E5 and 2-isopropyl imidazole C) CE10/24EMI: adduct of CARDURA E10 and 2-ethyl-4-methyl imidazole. (CARDURA E5 is a glycidyl ester of an alpha,alpha branched saturated monocarboxylic acid having a total of 5 carbon atoms.) Table 1 shows the viscosities of the adducts A) and C). The (advantageous) lower viscosity of A) in respect of C) is evident. Viscosity data of adducts Compound Brookfield Viscosity at 25 °C Pa.s A) Cardura E10/2-isopropyl imidazole (CE10/IPI) 70 C) Cardura E10/2-ethyl-4-methyl imidazole (CE10/24EMI) 140 Table 2 shows the performance of A) and C) as curing compounds in the homopolymerization of EPIKOTE 828. Formulation 2A clearly has a longer shelflife and a slightly higher Tg than formulation 2C. Comparison of CE10/IPI vs CE10/24EMI in homopolymerization of DGEBPA Components Formulation code 2A 2C (comparative) EPIKOTE 828 (g) 100 100 CE10/IPI (g) 8 CE10/24EMI (g) 8 Total (g) 108 108 Properties Tecam gel time at 60 °C (min) 199 121 Reaction kinetics DSC (10 °C/min) Total heat of reaction (J/g) 367 416 Onset temperature (°C) 119 116 Peak temperature (°C) 132, 225 128 Glass rubber transition temp. (Tg) (Cure: 2h/175 °C) DSC onset (°C) 129 125 DMA E' onset (°C) 141 136 Table 3 shows the performance of A, B, and C as accelerators at equimolar level in E 828/Dicyandiamide (DICY) epoxy resin/curing compositions. Formulations 3A and 3B show a longer shelflife than 3C whereas reactivity and Tg values are at a similar (high) level. Comparison of Accelerators CE10/IPI, CE5/IPI CE10/EMI in dicy cured composition Components Formulation code 3A 3B 3C (comparative) EPIKOTE 828 (g) 100 100 100 DICYANDIAMIDE (g) 7.5 7.5 7.5 CE10/IPI (g) 1.0 CE5/IPI (g) 0.76 CE10/24EMI (g) 1.00 Total (g) 108.5 108.26 108.5 Properties Tecam gel time at 60 °C 1418 1294 1087 Hot plate gel time at 150 °C ttns (s) 278 307 240 160 °C ttns (s) 231 230 203 170 °C ttns (s) 96 105 86 Reaction kinetics (DSC 10 °C/min) Heat of reaction (J/g) 430 434 441 Onset temperature (°C) 142 142 132 Peak temperature (°C) 158 159 156 Glass rubber transition temp. (Tg) Measured with DMA, Heating rate 5 °C/min Cure: gelation at 160 °C + postcure 1h/180 °C E' (flex store modulus) onset temperature (°C) 157 151 153 E" (flex loss modulus) max. temperature (°C) 164 158 161

Claims: An adduct of a glycidyl ester of an alpha,alpha branched saturated monocarboxylic acid, containing a total of from 5 to 18 carbon atoms, and 2-isopropyl imidazole. An adduct as claimed in claim 1 wherein the glycidyl ester is a mixture of glycidylesters of alpha, alpha branched saturated monocarboxylic acids having as main constituents the glycidyl esters of alpha,alpha branched saturated monocarboxylic acids having a total of 9, 10 or 11 carbon atoms. An epoxy resin composition comprising: a) one or more epoxy compound(s) having an average of at least 1 epoxide group per molecule; and b) at least one adduct of a glycidyl ester of an alpha,alpha branched saturated monocarboxylic acid containing a total of from 5 to 18 carbon atoms and 2-isopropyl imidazole. An epoxy resin composition as claimed in claim 3 wherein b) is an adduct as claimed in claim 2. An epoxy resin composition as claimed in claim 3 or 4 which further comprises c) a co-curing compound. An epoxy resin composition as claimed in claim 5 wherein the co-curing compound is selected from the group consisting of phenols, polycarboxylic acids or their anhydrides, phosphines, amino compounds, amine salts and quaternary ammonium salts. An epoxy resin composition as claimed in claim 6 wherein the co-curing compound is dicyandiamide. An epoxy resin composition as claimed in any one of the claims 3 to 7 wherein b) is present in an amount of from 0.05 to 20 parts by weight (pbw) per 100 pbw of a) plus c). An epoxy resin composition as claimed in claim 8 wherein b) is present in an amount of from 0.5 to 10 parts by weight (pbw) per 100 pbw of a) plus c). An epoxy resin composition as claimed in any one of the claims 3 to 9 which further comprises an organic- or inorganic acid compound in a substantially equivalent amount with respect to the imidazole adduct. An epoxy resin composition as claimed in claim 10 wherein the acid compound used is selected from the group consisting of phosphoric acid, benzoic acid, paratoluenesulphonic acid and salicylic acid. An epoxy resin composition as claimed in any one of the claims 3 to 11 wherein a) is a glycidyl ether of a polyhydric phenol. An epoxy resin composition as claimed in claim 12 wherein compound a) is a polyglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane having an epoxy equivalent weight of from 140 to 400.

Inventors: VAN LIEMPD VIRGILIUS CHRISTIAA, WINTRAECKEN JOHANNES JACOBUS M, ZWIJNENBERG ANTONIUS JOHANNES, VAN LIEMPD, VIRGILIUS CHRISTIAAN JOHANNES NICOLAAS, WINTRAECKEN, JOHANNES JACOBUS M. H., ZWIJNENBERG, ANTONIUS JOHANNES MARIA
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1992
Main classification: C08G59
IPC codes: C08G59