COPOLYADIPAMIDE CONTAINING PENTAMETHYLENEADIPAMIDE UNITS AND PRODUCTS PREPARED THEREFROM

Abstract: A copolyadipamide consisting essentially of between about 60 and about 99.5 mole percent hexamethyleneadipamide units and between about 0.5 and 40 mole percent pentamethyleneadipamide units, the copolyamide having an RV greater than about 25, and a melting point of greater than about 220 DEG C.

Description: TITLE Copolyadipamide Containing Pentamethyleneadipamide units and Products Prepared Therefrom BACKGROUND OF THE INVENTION The present invention relates to polymers and more particularly to a copolyadipamide having hexamethyleneadipamide units and a minor portion of pentamethyleneadipamide units, and products prepared therefrom. Polyadipamide polymers, e.g., polyhexamethyleneadipamide (nylon 66) , have a number of positive characteristics, but are thermally unstable at their normal processing temperatures. When kept in the molten state at processing temperature for a long time, polyadipamides form branσhed/crosslinked, insoluble, nonfusible gel. The formation of gel in the polymer product and on the walls of processing equipment can result in deficient product with poor processibility, particularly when fiber spinning is involved. The fiber spinning breaks which may occur due to gel formation are troublesome and make the winding of large packages impractical. Certain remedies to gel-formation have been reported such as in U.S. Patent No. 3,872,055. U.S. Patent No. 3,872,055 discloses a polyamide composition which has a decreased gel-forming property, specifically a copolyamide of the diamine-dicarboxylic acid type containing phosphinic and phosphonous acid compounds together with an alkali metal compound. SUMMARY OF THE INVENTION In accordance with the invention, there is provided a copolyadipamide consisting essentially of between about 60 and about 99.5 mole percent hexamethyleneadipamide units and between about 0.5 and 40 mole percent pentamethyleneadipamide units, the copolyamide having an RV greater than about 25, and a melting point of greater than about 220°C. For convenience, the copolyamide of the invention will be referred to as nylon 66/56. In a preferred form of the invention the copolyadipamide consists essentially of between about 90 and about 99.5 mole percent hexamethylene adipamide units and between about 0.5 and 10 mole percent pentamethyleneadipamide units. Preferably, the RV of the copolyamide is between about 30 and about 80, most preferably between about 30 and about 60. The copolyamide of the invention provides reduced gel formation rate relative to that of nylon 66 and provides improvements in product quality, increases in process continuity, and decreases in equipment maintenance costs. DETAILED DESCRIPTION The copolyadipamides of the invention are substantially linear copolyamides which consist essentially of between about 60 and about 99.5 mole percent hexamethyleneadipamide units and between about 0.5 and 40 mole percent pentamethyleneadipamide (56) units. In the preferred copolyadipamides, the 56 units are generally randomly distributed throughout the copolymer. The copolyamide has properties similar to homopolymer nylon 66, but has significant advantages in product quality, production cost, and processability. Depending on the intended end use of the copolyadipamides of the invention, it is advantageous to employ varying mole percentages of 56 in the copolyadipamide. So that the properties of copolyamide remain similar to the properties of homopolymer poly(hexamethyleneadipamide) , it is preferable for the mole percentage of 56 in the polymer to be between about 0.5 and about 10%. The copolyadipamides in accordance with the invention have a formic acid relative viscosity (RV) greater than about 25. Preferably, the RV of the copolyadipamide is between about 30 and about 80, most preferably, between about 30 and about 60. The melting point of the copolyadipamides in accordance with the invention is greater than about 220°C. The melting points of the copolyadipamides vary with the percentage of 56 and thus range very close to the melting point of homopolymer nylon 66 polymer, about 265°C, when the percentage of 56 is about 0.5%. With increasing 56, the melting point decreases to about 220°C where the 56 percentage is about 40%. Surprisingly, the copolyadipamides of the invention have been found to form "gel" at a substantially lower rate than nylon 66 homopolymer. "Gel" refers to the very high molecular weight, branched/crosslinked polymer which forms in the nylon 66 polymer melt and which collects in the product and on equipment walls in contact with the molten polymer. The gel is essentially insoluble and often can only be removed from equipment using extreme measures such as by burning off of the gel. As shown in Table 1(c), the gelation time (typically a plot of melt viscosity versus time at a particular temperature is made and the time at which a melt viscosity inflection is observed is taken to be the gelation time) increases significantly with increasing percentages of 56. In addition, since the melting point of the copolyamide is lower, and is substantially lower at the greater 56 mole percentages, the gelation time can be further increased without affecting spinning performance by employing lower polymer melt temperatures. The copolyadipamides of the invention can be prepared by condensation polymerization in an aqueous "salt" solution formed by mixing adipic acid with hexamethylenediamine (HMD) and pentamethylenediamine (PMD) in the molar proportions necessary to produce the copolymer with the desired mole percent of 56 units. Adapted as necessary to compensate for the different properties of the PMD, procedures useful for the production of homopolymer poly(hexamethyleneadipamide) can be applied to the production of the copolymer of the invention. A particularly convenient method for making a copolyadipamide in accordance with the invention is to provide two aqueous salt solutions of hexamethylene diammonium adipate and pentamethylene diammonium adipate. Necessary quantities of the two solutions can be readily mixed to produce a salt solution for the desired copolyamide. It is sometimes desirable to add a catalyst to the salt solution. A variety of catalysts are known for use in polymerizing homopolymer nylon 66 such as phenyl phosphinic acid, manganese hypophosphite, etc. The salt solution with or without catalyst is reacted in a suitable reaction vessel such as an autoclave under an inert atmosphere. One preferred procedure is purging the autoclave with nitrogen and increasing the pressure to about 265 psia. The salt solution is heated to a temperature of about 250°C. The pressure is then released over, for example, one hour while increasing the temperature to about 275°C. The reaction temperature is held constant at atmospheric pressure for sufficient time to complete the reaction to the extent desired. The copolyamide can be cooled in the autoclave and ground or can be extruded from the autoclave into water and conveniently chipped and dried to produce flake. The RV of the polymer from the autoclave can be in the range of 25-80 but is typically in the range of 25-45. The copolyamide in accordance with the invention can also be made by any of a variety of continuous polymerization processes. The copolyamide of the invention is useful in a wide variety of known processes for the manufacture of fibers, films, and molded articles. For use of the composition in fibers, any of a variety of known additives such as delustrants, e.g., titanium dioxide, antioxidants, pigments, and other materials may be added to the copolyamide at a suitable point in the polymer preparation or, for example, as the flake is melted in an extruder in advance of spinning. The following example is offered for the purposes of illustrating the invention and is not intended to be limiting. Percentages are by weight except for the mole percentages of 66 and 56 monomer units and as indicated otherwise. The test methods which follow were used for obtaining the results reported. TEST METHODS The formic acid relative viscosity (RV) of the polyamide is measured as described at col. 2, 1. 42-51, in Jennings, U.S. Patent No. 4,702,875. Amine and carboxyl ends are determined by the methods described on pages 293 and 294 in Volume 17 of the "Encyclopedia of Industrial Chemical Analysis" published by John Wiley & Sons, Inc. in 1973. The gel time (reported in hours) is the time required to show a sharp inflection and rise in polymer melt viscosity while heating a polymer sample maintained at a constant temperature and constant steam pressure. A plot of polymer melt viscosity versus time will show a rise or inflection in melt viscosity as formation of polymer gel makes the bulk polymer more viscous. Alternately, gel time can be determined by the method of U.S. Patent No. 3,872,055. This method reports the time required for making the copolyamide insoluble (when only solvent swelling is observed) in anhydrous formic acid after being heated at a given temperature and pressure in a steam atmosphere. EXAMPLE I Into a 300 cc stainless steel autoclave, the following reactants were added in varied amounts as indicated in Table 1(a) to provide the indicated mole% ratios: nylon 66 salt solution (approximately 50% concentration) , adipic acid and pentamethylenediamine (PMD) . For each reaction mixture, the autoclave was purged with nitrogen and sealed. The pressure release valve on the autoclave was set to 265 psia and the clave was heated to 250°C. When the temperature reached 250°C, the pressure reduction cycle was started so that the pressure was reduced to atmospheric over one hour. At the same time, the temperature of the autoclave was raised to 275°C. When the pressure reached atmospheric, it was held for 45 minutes. The polymer was cooled in the autoclave and removed as a solid block attached to the agitator. The polymer was ground to a fine powder and dried at 90°C in a vacuum oven over night. Properties of the compositions prepared are reported in Table 1(b). The gel times of the 66/56 copolymers at 292°C are given in Table 1(c).

Claims: CLAIMS ; 1. A copolyadipamide consisting essentially of between about 60 and about 99.5 mole percent hexamethyleneadipamide units and between about 0.5 and 40 mole percent pentamethyleneadipamide units, said copolyamide having an RV greater than about 25, and a melting point of greater than about 220°C. 2. The copolyadipamide of claim 1 wherein said RV is between about 30 and about 80. 3. The copolyadipamide of claim 1 wherein said RV is between about 30 and about 60. 4. A copolyadipamide consisting essentially of between about 90 and about 99.5 mole percent hexamethylene adipamide units and between about 0.5 and 10 mole percent pentamethyleneadipamide units, said copolyamide having an RV greater than about 25, and a melting point of greater than about 220°C. 5. The copolyadipamide of claim 4 wherein said RV is between about 30 and about 80. 6. The copolyadipamide of claim 4 wherein said RV is between about 30 and about 60.

Inventors: HAMMOND JAMES ALEXANDER JR, MARKS DAVID NEIL, HAMMOND, JAMES, ALEXANDER, JR., MARKS, DAVID, NEIL
Applicants: DU PONT, E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1992
Main classification: C08G69
IPC codes: C08G69