Making method for high-density optical disk

Abstract: In a making method for a high-density optical disk, comprising the step of forming recording pits or recesses (19) for forming the recording pits by etching through apertures (13) of a photoresist layer (12), a light intensity distribution of an exposure beam spot for forming each aperture (13) through the photoresist layer (12) is made different between a circumferential direction (Θ) of the optical disk (17) and a direction (r) perpendicular to the circumferential direction, thereby setting a ratio between a length of each pit and a length of each land in respect of the circumferential direction to about 1:1.

Description: BACKGROUND OF THE INVENTION The present invention relates to a method for making a high-density optical disk in accordance with the method steps specified in the precharacterising part of claim 1 and a high-density optical disk achieved by said making method. Such a making method is known from W0-A-88/09990. In making an optical disk having an information recording portion formed from the presence and absence of recesses or pits, the optical disk is generally obtained by preparing a stamper having a recessed surface according to recording information and molding resin with use of the stamper. Such a conventional making method for an optical disk using the stamper will now be described with reference to Figs. 10A to 10D showing the steps of the making method. Referring to Fig. 10A, a photoresist layer 2 is entirely applied to a smooth surface la of a substrate 1 such as a glass substrate, and the photoresist layer 2 is sequentially exposed by scanning a laser beam modulated according to information to be recorded, e.g. signals of "0" and "1". Subsequently, development is carried out to form a plurality of apertures 3 arranged in a desired pattern according to the recording information. Then, as shown in Fig. 10B, a conductor layer such as Ni is entirely formed on the photoresist layer 2 including the apertures 3 by electroless plating, vapor deposition, sputtering, etc., and a thick metal layer 4 such as Ni is then formed on the conductor layer by electroplating. As shown in Fig. 10C, the metal layer 4 is separated from the glass substrate 1 to prepare a stamper 5. As shown in Fig. 10D, resin such as acrylic resin or polycarbonate resin is molded with use of the stamper 5 to obtain an optical disk 7 having a plurality of recesses 6 as information pits arranged in a reverse pattern as transferred from a recessed surface of the stamper 5. However, each recess or pit 6 of the optical disk 7 thus obtained has a sectionally trapezoidal shape such that opposite side surfaces of each recess 6 are inclined so as to follow the shape of each aperture 3 of the photoresist layer 2. Such inclined side surfaces of each recess 6 causes a problem in reproduction characteristics. Such inclination of the side surfaces of each recess 6 is generated as follows: The formation of each aperture 3 through the photoresist layer 2 by pattern exposure of a laser beam will be described with reference to Figs. 11A and 11B. In general, when a laser beam hν is condensed and irradiated to the photoresist layer 2 on the glass substrate 1, the laser beam hν is distributed as shown in Fig. 11A. In this case, an intensity distribution of the laser beam hν is shown by a one-dot chain line a in Fig. 11A. Further, an area to be exposed to enable the development under the above condition is an area surrounded by a dashed line b in Fig. 11A. This area has a shape according to the intensity distribution of the laser beam hν. Accordingly, when the photoresist layer 2 is developed after the exposure, the exposed area mentioned above is made into the aperture 3, which has a sectionally trapezoidal shape such that a width W 1 on the side of incidence of the laser beam is larger than a width W 2 on the side of the glass substrate 1, that is, at the boundary between the aperture 3 and the glass substrate 1. To solve the problem due to the sectionally trapezoidal shape of each pit in making the optical disk, the present applicant has proposed an improvement in the making method for the high-density optical disk in Japanese Patent Application No. 1-244463. Figs. 12A to 12E show the steps of the making method for the optical disk proposed in the above cited reference. Referring to Fig. 12A, a substrate 1 such as a glass substrate having a surface layer 8 such as Cr is first provided. The surface layer 8 has a thickness t corresponding to a depth of each information pit (recess) to be formed on an intended optical disk, and shows an etching property different from that of the substrate 1. The surface layer 8 is formed by vapor deposition, sputtering, etc. Then, as previously mentioned, a photoresist layer 2 is formed on the surface layer 8, and is exposed and developed to form a plurality of apertures 3. As apparent from Fig. 12A, each aperture 3 has a sectionally trapezoidal shape such that a width W 1 or each aperture 3 on the open side thereof is larger than a width W 2 of each aperture 3 on the bottom side thereof, as similar to the illustration in Figs. 11A and 11B. Then, as shown in Fig. 12B, the surface layer 8 is etched over its whole thickness by perpendicular anisotropic etching such as RIE (reactive ion etching) with the photoresist layer 2 used as a mask. By applying the RIE, the surface layer 8 only is selectively etched, and the substrate 1 itself is not etched or hardly etched. According to this method, the surface layer 8 is etched through the apertures 3 to form a plurality of recesses 9 each having a width corresponding to the small width W 2 of each aperture 3 of the photoresist layer 2 and having opposite substantially vertical side surfaces. Then, as shown in Fig. 12C, after removing the photoresist layer 2, a metal layer 4 such as Ni is entirely formed on the surface layer 8 including the recesses 9, as similar to the illustration in Fig. 10B. Thereafter, the metal layer 4 is separated from the substrate 1 to obtain a stamper 5 having a desired recessed surface according to recording information. The stamper 5 thus obtained has a plurality of projections each having opposite vertical side surfaces. Accordingly, as shown in Fig. 12E, an optical disk 7 molded by using the stamper 5 is formed with a plurality of pits or recesses 6 each having opposite vertical side surfaces and a width corresponding to the small width W 2 . In the optical disk 7 formed in this manner, the pits (recesses) 6 can be made very small to thereby realize high-density recording. In the making method mentioned above, a light intensity distribution of the laser beam modulated according to recording information is symmetrical with respect to an optical axis, that is, the intensity distribution illustrated in Fig. 11A is uniform in any plane containing the optical axis. In other words, each pit (recess) of the optical disk has the same width corresponding to the width W 2 in respect of both a direction of relative movement of a reproducing optical head of an optical disk drive, i.e., a direction along a recording track of the optical disk (which direction will be hereinafter referred to as a circumferential direction or  direction) and a direction perpendicular to the circumferential direction (which direction will be hereinafter referred to as a radial direction or r direction). The apertures 3 of the photoresist layer 2 each aperture having the relation of W 1 > W 2 in accordance with the above method are arranged with a minimum spacing in relation to the function of the etching mask and other conditions, thereby reducing the pitch to realize high-density recording. However, as shown in Fig. 12E, when a width P corresponding to one signal is minimized, that is, when the sum P of a width Wp of a recess 6 corresponding to a recording portion for information "1" and a width W L of a land formed adjacent to the recess 6 is minimized, the width W P becomes smaller than the width W L . Also in respect of the sacanning direction of a reading light on the optical disk (i.e. the  direction), the relation of W P < W L holds, so that a ratio between the width Wp and the width W L in respect of the  direction does not become 1:1, that is, a duty ratio does not become 50 %. Accordingly, when the reading light is irradiated onto the optical disk to read the pits or information, a duty ratio of electrical signals corresponding to the information "0" and "1" does not become 50 %, causing a reduction in S/N (C/N). WO-A-88/09990 describes a method of producing an optical storage disk by means of a stamp. The known stamp has grooves for forming guide tracks in the optical disk, said grooves having edges deviating from the vertical and are formed by exposing and developing selectively a photoresist layer on a substrate according to recording information. Each of said grooves has a width on the side of the substrate smaller than the width on the side of incidence of an exposure beam spot. EP-A-0155000 describes a known method of manufacturing optical memory elements by means of a mask plate having preformed grooves and pits. The pits of the mask plate are elongated in the circumferential direction of the optical disk and the ratio between the length of each pit and the length of each land between each pit in circumferential direction is about 1:1. EP-A-0190774 discloses a known method of providing a record carrier body with preformed optically detectable servo-track portions and sector addresses. Fig. 5 of EP-A-0190774 shows an apparatus by means of which the sector addresses and the servo-track portions can be recorded on a master disk. As it is shown in this Fig. 5, the exposure beam spot in the plane of a photo-sensitive layer on the substrate has an elongate shape and its longitudional direction is extending transverse to the track direction. SUMMARY OF THE INVENTION It is an object of the present invention to set the duty ratio of the pits and the lands in respect of the scanning direction of the reading light on the optical disk, i.e. in respect of the  direction to about 1:1 or 50 %. According to a first aspect of present invention, the above object is solved by a making method specified by the -features of claim 1. Depending claims 2 to 6 are respectively specifying advantageous developments thereof. Independent claim 7 specifies a high-density optical disk achieved by a method of one or more of the preceding claims. As shown in Figs. 1 and 2, the present invention provides a making method for a high-density optical disk, including the steps of forming a photoresist layer 12 on a substrate 11, forming a plurality of apertures 13 through the photoresist layer 12 by selective exposure and development according to recording information, each of the apertures 13 having a width on the side of the substrate 11 smaller than a width on the side of incidence of an exposure beam spot, and etching the subrate 11 through the apertures 13 to form a plurality of recesses 19 corresponding to the apertures 13. While the above method is applied to the radial or r direction of the optical disk to reduce a pitch of the recesses 19, the present invention is characterized in that a light intensity distribution of the exposure beam spot for forming the apertures 13 is different between the radial or r direction and the circumferential or  direction of the optical disk as shown by a solid-line curve and a dashed-line curve in Fig. 3 so that the width of each aperture 13 formed through the photoresist layer 12 is small in the radial or r direction of the optical disk and large in the circumferential or  direction of the optical disk. As shown in Fig. 2, in respect of the  direction of the optical disk, a width W P of each recess 19 is substantially equal to a width W L of each land. That is, as shown in Fig. 4 which is a plan view of a part of the optical disk 17, a width of each pit (recess) 16 of the substrate 11 itself or the optical disk 17 obtained on the basis of the substrate 11 is substantially equal to a width of each land in respect of the  direction of the substrate 11 or the optical disk 17. That is, a duty ratio in respect of the  direction of the optical disk is 1:1. According to the making method of the present invention, the light intensity distribution of the exposure beam spot to be applied to the photoresist layer 12 is different between the r direction and the  direction of the optical disk as shown by the solid-line curve and the dashed-line curve in Fig. 3, so that a width of the exposure beam spot at a light intensity level on the surface of the substrate 11 as shown by a two-dot chain line S in Fig. 3 is small in the r direction and large in the  direction. Accordingly, as shown in Figs. 1 and 2, a width W 2r of each aperture 13 on the side of the substrate 11 in respect of the r direction is smaller than a width W 2c of each aperture 13 on the side of the substrate 11 in respect of the  direction, that is, the relation of W 2r < W 2c is set. The recesses 19 are formed by etching the substrate 11 through the respective apertures 13, and in respect of the  direction only of the optical disk, the width W P of each recess 19 is set to be equal or at least substantially equal to the width W L of each land. As mentioned above, in case of forming the recesses (pits) 16 as a recording portion for information such as "1" or "0" on the optical disk 17 as shown in Fig. 4, the light intensity distribution of exposure beam to be applied to the photoresist layer 12 is set differently between the r direction and the  direction to thereby make the width W P of each recess 19 equal or substantially equal to the width W L of each land, that is, make the duty ratio become 1:1 (50 %). As described above, according to the method of the present invention, the duty ratio in the circumferential direction of the optical disk, that is, in a scanning direction of a reading light on the optical disk can be made to 50 %, thereby improving an S/N (C/N). While the light intensity distribution of the exposure beam is made different between the r direction and the  direction according to the present invention, the exposure operation is effected by the same exposure beam, and it is prevented from becoming complex. Other objects and features of the invention will be more fully understood from the following detailed description and appended claims when taken with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a sectional view of an optical disk along the radical or r direction thereof in one step of the making method according to the present invention; Fig. 2 is a sectional view of the optical disk along the circumferential or  direction thereof in one step of the making method according to the present invention: Fig. 3 is a light intensity distribution diagram of an exposure beam in the making method according to the present invention; Fig. 4 is a plan view of an essential part of the optical disk to be obtained by the making method according to the present invention; Fig. 5 is an iso-intensity diagram of the exposure beam; Fig. 6 is a construction diagram of a preferred embodiment of exposure means; Fig. 7 is an optical path diagram in the cross sections along the r direction and the  direction; Fig. 8 is an elevational view of a preferred embodiment of control means for the exposure beam; Fig. 9 is an optical path diagram of another preferred embodiment of the control means for the exposure beam; Figs. 10A to 10D are sectional views illustrating the steps of the making method for the optical disk in one example of the prior art; Figs. 11A and 11B are sectional views illustrating the formation of an aperture through a photoresist; and Figs. 12A to 12E are sectional views illustrating the steps of the making method for the optical disk in another example of the prior art. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS As shown in Figs. 1 and 2 which are sectional views of the optical disk along the r direction and the  direction thereof, respectively, the photoresist layer 12 of a positive type, for example, is applied on the substrate 11, and it is exposed to light and developed to form the apertures 13. Then, the substrate 11 is etched through the apertures 13 by RIE having a perpendicular anisotropy, for example, to form the recesses 19. Then, the photoresist layer 12 is removed to obtain the optical disk having the recesses 19 as information pits. In another way, a metal layer such as Ni may be formed on the photoresist layer 12 having the apertures 13 by electroless plating or electroplating, and the metal layer is then separated from the substrate 11 to prepare a stamper and mold the optical disk by using the stamper. Alternatively, a master for forming a plurality of stampers may be formed by plating similar to the above, and then the stampers may be formed by using the master to obtain the optical disk. The substrate 11 is formed from a glass substrate, for example, and a surface thereof is treated with a silane coupling agent to ensure tight contact of the photoresist layer 12 on the surface of the substrate 11. Especially in the present invention, the exposure to the photoresist layer 12 is carried out by using a light beam such as a laser beam which is to become on and off or modulated in intensity according to recording information and has different light intensity distributions in respect of the r direction and the  direction. For example, referring to Fig. 3, the light intensity distribution in respect of the r direction is shown by a solid-line curve, and the light intensity distribution in respect of the  direction is shown by a dashed-line curve. As apparent from Fig. 3, both the distributions are substantially identical with each other in light quantity (area defined by each curve) and peak level. However, the distribution in respect of the r direction is such that the curve is sharp near the peak level and wide at the bottom, while the distribution in respect of the  direction is such that the curve is gentle near the peak level. That is, a width of the exposure beam at the light intensity level S on the surface of the substrate 11 is large in respect of the  direction as shown in Fig. 3, and an iso-intensity diagram to be created in this case is shown in Fig. 5. Fig. 6 shows a schematic construction of a preferred embodiment of exposure means for applying an exposure beam to the photoresist layer 12 on the substrate. In this preferred embodiment shown in Fig. 6, a laser 21 is employed as an exposure beam source, and a laser beam hν from the laser 21 is introduced through a condenser lens system 22 into an acoustooptic modulator (AOM) 23. In the AOM 23, the laser beam hν is switched and modulated according to recording information, and it is made into parallel rays of light by a collimator lens system 24. Then, the beam enters control means 25 for providing different spot diameters  r and  c in respect of the r direction and the  direction. Thereafter, a light intensity distribution of the beam having outgone from the control means 25 is made different between the r direction and the  direction by cooperation of a condenser lens system 26 and an objective lens system 27. The beam from the objective lens system 27 is applied to the photoresist layer 12 on the substrate 11 which is rotated, and is spirally scanned on the photoresist layer 12, that is, displaced in both the r direction and the  direction. Fig. 7 is an optical path diagram illustrating a preferred embodiment of a method of differentiating the light intensity distribution between the r direction and the  direction. Referring to Fig. 7, a solid line represents an optical path in a cross section along a direction corresponding to the  direction, and a dashed line represents an optical path in a cross section along a direction corresponding to the r direction. In this case, the exposure beam to be introduced from the control means 25 into the condenser lens system 26 has the spot diameter  c in respect of the  direction and the spot diameter  r in respect of the r direction, wherein the relation between the spot diameters  c and  r is set to  c <  r . Each of the condenser lens system 26 and the objective lens system 27 is symmetrical with respect to an optical axis 0-0 as usual. As the relation between the spot diameters  c and  r of the beam entering the condenser lens system 26 is set to  c <  r , a numerical aperture N.A. of the objective lens system 27 which value is defined as n sinu (n: refractive index; u: angle of incident light with respect to an optical axis) becomes different between the r direction and the  direction. Therefore, the light intensity distribution of the beam spot of the outgoing light from the objective lens system 27 on the photoresist layer 12 becomes different between the r direction and the  direction as shown in Figs. 3 and 5. Fig. 8 shows a preferred embodiment of the control means 25 for making the spot diameter of the beam entering the condenser lens system 26 become different between the r direction and the  direction. Referring to Fig. 8, the control means 25 is formed from a light shielding member 29 having a slit 28. The slit 28 has a width W sr in a direction corresponding to the r direction and a width W sc in a direction corresponding to the  direction, wherein the relation between the widths W sr and W sc is set to W sr > W sc . Fig. 9 shows another preferred embodiment of the control means 25, in which a cylindrical condenser lens 30 and a cylindrical collimator lens 31 having a lens function in respect of the direction corresponding to the r direction are combined, and the relation between a focal distance f 0 of the condenser lens 30 and a focal distance f 1 of the collimator lens 31 is set to f 1 > f 0 . Accordingly, the diameter of the beam having entered the condenser lens 30 can be enlarged only in the direction corresponding to the r direction. Although not shown, as a further embodiment of the control means 25, an AOM having a characteristic that a cross section of an outgoing light therefrom becomes somewhat flat may be located between a cylindrical condenser lens and a cylindrical collimator lens, and a focal distance of the condenser lens may be set to be larger than a focal distance of the collimator lens. The photoresist layer 12 is exposed to light by using the exposure means mentioned above, and subsequent development is carried out to form the apertures 13 each having different widths in respect of the r direction and the  direction as shown in Figs. 1 and 2. Then, anisotropic etching of the substrate 11 through the apertures 13 is carried out with the photoresist layer 12 used as an etching mask, thus forming the recesses 19 on the substrate 11. As shown in Fig. 1, a width of each recess 19 in respect of the r direction can be reduced by the small width W 2r of each aperture 13, so that a pitch P r can be sufficiently reduced. On the other hand, a width of each recess 19 in respect of the  direction can be enlarged by the large width W 2c of each aperture 13, so that the duty ratio can be made to 1:1 in a constant pitch P c . Finally, the optical disk 17 can be made from the substrate 11 having the recesses 19 on the basis thereof. While the recesses 19 are formed on the substrate 11 such as a glass substrate in the above preferred embodiment, various changes and modifications may be made in the present invention. For example, as similar to the construction shown in Figs. 12A to 12E, the substrate 11 may be constituted of a glass substrate and a metal layer with a desired thickness as a surface layer formed on the surface of the glass substrate, and the metal layer may be etched through the apertures 13 of the photoresist layer 12 to form the recesses 19 each having a depth corresponding to the thickness of the metal layer.

Claims: A method for making a high-density optical disk (17) comprises the steps of: forming a photoresist layer (12) on a substrate (11), forming a plurality of apertures (13) through said photoresist layer by selective exposure and development according to recording information, each of said apertures, having a width on the side of said substrate smaller than a width on the side of incidence of an exposure beam spot, and etching said substrate through said apertures, characterized in that a light intensity distribution of said exposure beam spot for forming said apertures is different between the radial direction (r) and the circumferential direction (Θ) of said optical disk (17) wherein both the light intensity distributions have substantially identical light quantity and peak level, and the distribution of the light intensity in respect to the radial direction (r) is such that the distribution curve is sharp near the peak level and wide at the bottom, and the distribution of the light intensity in respect to the circumferential direction () of said disk (17) is such that the distribution curve is gentle near the peak level so that the width of each of said apertures on the side of said substrate gets small (W 2r ) in the radial direction of said optical disk and larger (W 2c ) in circumferential direction of said optical disk (17). The method according to claim 1, wherein a plurality of recesses (19) and lands are formed on said substrate by said etching step, and a width of said each recess and a width of said each land formed between the adjacent ones of said recesses in respect of the circumferential direction (Θ) of said optical disk are substantially equal to each other. The method according to claim 1, wherein the light intensity distribution is made different between the radial direction and the circumferential direction of said optical disk by using control means (25) for differentiating a spot diameter ( r ,c) of light beam entering a condenser lens system (26) in respect of a direction (r) corresponding to the radial direction from a spot diameter of the light beam in respect of a direction () corresponding to the circumferential direction. The method according to claim 3, wherein said spot diameter (r) in respect of the direction corresponding to the radial direction (r) is larger than the spot diameter (c) in respect to the circumferential direction (Θ). The method according to claim 4, wherein said control means comprises a light shielding member (29) having a slit (28), and a width of said slit in respect of the direction corresponding to the radial direction (r) is larger than that in respect of the direction corresponding to the circumferential direction (Θ). The method according to claim 4, wherein said control means comprises a cylindrical condenser lens (30) and a cylindrical collimator lens (31) having a lens function in respect of the direction corresponding to the radial direction, and a focal distance of said cylindrical condenser lens (30) is smaller than that of said cylindrical collimator lens (31). A high-density optical disk achieved by the method of one or more of the preceding claims and comprising: a substrate and a plurality of apertures arranged in a desired pattern according to the recording information on said substrate, wherein the width of said each aperture (13,16) on the side of said substrate (11) in respect of the radial direction (r) of said optical disk (17) is smaller than that in respect of the circumferential direction (Θ) of said optical disk (17) and a ratio between a length of each pit (13) and a length of each land (12) between adjacent pits (13) in respect of the circumferential direction is about 1:1.

Inventors: KASHIWAGI TOSHIYUKI, KASHIWAGI, TOSHIYUKI
Applicants: SONY CORP, SONY CORPORATION
Application year: 1992
Main classification: G11B7
IPC codes: G11B7