A method for fabricating an optical waveguide

Abstract: In the first step, a fuel and raw material gasses are fed to a burner (4) while flames from the burner scan a Si substrate (1). Synthesized glass fine particles are deposited on the substrate (1) to form a first porous vitreous layer (5) to be a under cladding layer. In the second step, the first porous vitreous layer (5) is heated by the flames. A bulk density of an upper part of the first porous vitreous layer (5) is raised to 0.3 g/cm³. This upper part with a raised bulk density functions as a shield layer against GeO₂. In the third step, a second porous vitreous layer (6) to be a core layer is deposited uniformly on the first porous vitreous layer (5). In the fourth step the first and the second porous vitreous layers (5, 6) are sintered. In this case, the shield layer with a higher bulk density hinders the GeO2 component which has evaporated from the second porous vitreous layer (6) from diffusing into the first porous vitreous layer (5).

Description: This invention relates to a process for forming an optical film structure from which can be manufactured an optical waveguide and to a process for forming an optical waveguide, by means of Flame Hydrolysis Deposition (FHD). JP-A-57 081 213 describes a method for producing thin films for optical waveguides using flame hydrolysis deposition. FIGs. 1A-1C of the accompanying drawings show fabricating steps of another conventional process for fabricating a film structure for an optical waveguide having under and over cladding layers and a core surrounded by them. In the step shown in FIG. 1A, a first porous layer (SiO 2 +B 2 O 3 +P 2 O 5 ) to be the under cladding layer 20 is made of SiCl 4 , BCl 3 and POCl 3 on a substrate. In the step shown in FIG. 1B, a second porous layer (SiO 2 +GeO 2 +B 2 O 3 +P 2 O 5 ) to be the core layer 30 is formed of SiCl 4 , GeCl 4 , BCl 3 and POCl 3 fed from a burner, on the substrate. In the step of FIG. 1C, all the porous layers are sintered to be vitrified and rendered transparent. Subsequently the transparent core layer 30 is patterned as required, and the over cladding layer (not shown) is formed thereon. But in this process for forming optical waveguide films, when all the porous layers are vitrified, the GeO 2 component of the porous layer to be the core layer 30, i.e., core soot, adversely evaporates into the under cladding layer 20. This results in a problem that the GeO 2 component which has evaporated downward diffuses into the under cladding layer 20, and the interface between the core layer 30 and the cladding layer cannot be accurately controlled. FIG. 1C shows such a condition. An object of this invention is to provide a process for forming optical waveguide films, which can accurately control the core/cladding layer interface. According to a first aspect of the invention, there is provided a process for forming an optical film structure from which can be manufactured an optical waveguide having under and over cladding layers and a core surrounded thereby, comprising: a first step of depositing glass soot on a substrate by Flame Hydrolysis Deposition to form a first porous layer to be the under cladding layer with at least the upper part of the under cladding layer having at least a predetermined bulk density; a second step of depositing glass soot with added refractive index increasing dopant onto the first porous layer to form a second porous layer to be the core layer; and a third step, of vitrifying the first and the second porous layers to form transparent glass vitreous layers, said predetermined bulk density being enough to substantially prevent diffusion into the first porous layer of the refractive index increasing dopant added to the second porous layer. The first step of this process may comprise increasing a bulk density of at least some of the layer of the deposited soot above the predetermined bulk density. The first step may comprise depositing soot on the substrate by FHD so that a layer of the deposited soot has a bulk density lower than the predetermined bulk density. The first step may comprise depositing glass soot on the substrate by FHD so that a layer of the deposited soot has a bulk density higher than said predetermined bulk density. The first step may comprise depositing glass soot on the substrate by FHD so that a layer of the deposited soot has a bulk density higher than said set bulk density. The above-described process for increasing the bulk density may include increasing the temperature of an area of the deposited soot, increasing the temperature of the substrate, positioning a burner for glass synthesizing for use in FHD nearer to the substrate, increasing the feed amount of a fuel gas to the burner, or other means. The above-described refractive index dopant may be either of GeO 2 , P 2 O 5 , Al 2 O 3 . The bulk density of at least the upper part of the first porous layer to be the under cladding layer is preferably above about 0.3 g/cm 3 . The bulk density of at least the upper part of the first porous layer is preferably above that of the second porous layer. According to a second aspect of the invention, there is provided a process for forming an optical waveguide comprising: forming an optical film structure on a substrate by the process of the first aspect defined above; etching an optical waveguide pattern from the second vitreous layer; forming a third porous layer to be an over cladding layer on the second vitreous layer by FHD; and vitrifying the third porous layer to form a transparent glass vitreous layer. The present invention will become more fully understood from the detailed description given hereinbelow and the accompanying drawings, which are given by way of illustration only, and thus are not to be considered as limiting the present invention, and in which: FIGs. 1A-1C show a conventional process for forming an optical film structure for an optical waveguide; FIGs. 2A-2G show a process for forming a film structure for an optical waveguide films according to the present invention; FIGs. 3A-3D are views for comparing the conventional process with the process according to the present invention; FIG. 4 is a schematic view of a device for depositing fine particles of glass; FIG. 5 is a view of a refractive index distribution of optical films formed by the process according to one example of the present invention; FIG. 6 is a view of a refractive index distribution of optical waveguide films formed by the process according to one control; FIG. 7 is a view showing relationships between diffusion ratios of Ge and bulk densities of the porous layer to be the under cladding layer; and FIG. 8 is a view defining a parameter X for a diffusion ratio of Ge. The scope of applicability of the present invention will become apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and specific examples, while indicating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the scope of the claims will become apparent to those skilled in the art from this detailed description. The principle of this invention will be briefed below before examples of this invention are explained. FIGs. 2A-2G show fabrication steps of the process for forming optical waveguide having a under cladding layer, a over cladding layer and a core surrounded by them according to the present invention. In the step shown in Fig. 2A, a burner 4 for glass synthesis scans over the surface of a substrate 1 while being fed with a fuel and raw material gasses. Fine particles of quartz glass synthesized in the burner 4 is fed onto the substrate 1 on flames. Thus, a first porous cladding layer 5 to be an under cladding layer 50 is uniformly deposited on the substrate. In the step shown in FIG. 2B, the supply of the raw material gasses to the burner 4 is stopped, and thereafter the flame formed only by the fuel and without including the raw material gases scans a exposed surface of the first porous layer 5 to heat the upper part of the first porus layer 5. As a result, a bulk density of the upper part of the first porous layer 5 is increased. This upper part with an increased bulk density functions as a shield layer against a refractive index raising dopant, such as GeO 2 or others, so that the refractive index raising dopant is prevented from diffusing into the first porous vitreous layer 5. In the step shown in FIG. 2C, the burner 4 scan the substrate while being fed with the fuel and the raw material gasses with the refractive index raising dopant. As a result, a second porous layer 6 to be a core layer 60 is deposited uniformly on the first porous layer 5. In the step of FIG. 2D, the first and the second porous layers 5 and 6 are heated to become vitreous as a under cladding layer 50 and the core layer 60 which are transparent. In this case, the upper part of the first porous layer 5 prevents the evaporated refractive index raising dopant from diffusing into the first porous layer 5. Thus an optical waveguide with the core layer 60 formed on the under cladding layer 50 can be prepared. Subsequently in the step of FIG. 2E, the core layer 60 is etched into a required pattern for a core 61 by RIE or others. In the step of FIG. 2F, a third porous layer 7 to be the over cladding layer 70 is deposited so as to cover the core layer 60. In the step shown in FIG. 2G, the third porous vitreous layer 7 is heated to become vitreous. Thus, an optical waveguide with the core 61 surrounded by the under and the over cladding layers 50 and 70 is prepared. FIGs. 3A-3D show comparisons between the conventional process and the process according to the above embodiment. FIG. 3A is a graph showing bulk densities of the respective layer formed by the conventional process in which a shield layer is not formed. FIG. 3B is a graph showing bulk densities of the respective layers formed by the above mentioned process to the present invention in which the shield layer is formed in the upper part of the first porous layer 5 to be the under cladding layer 50. As shown in FIG. 3B, a part of the higher bulk density is formed in the under cladding layer 50 which is formed by the above-mentioned process. In FIG. 3B, the one-dot chain line schematically indicates an increased bulk density of the whole first porous layer 5 to be the under cladding layer 50. In this case as well, the upper part of the first porous layer 5 functions as a shield layer. It is possible to increase a bulk density of the second porous layer 6. But due to the increased bulk density, in the following sintering step the second porous layer 6 precedes the first porous layer 5 in becoming transparent, and it is more possible that adversely bubbles remain in the first porous layer 5. FIG. 3C shows a distribution of refractive indexes of the respective layers of FIG. 3A after sintered. FIG. 3D shows a distribution of refractive indexes of the respective layers of FIG. 3B after sintered. As apparently shown, in the conventional process in which the shield layer is not formed, the refractive index raising dopant diffuses into the under cladding layer 20, and the refractive index gradually changes at the core layer(30) / the cladding layer(20) interface in optical. On the other hand, in the above-mentioned process according to the present invention, the refractive index raising dopant does not diffuse into the under cladding layer 50, and the refractive index changes in a step at the core layer(60) / the cladding layer(50) interface in optical. That is, it is seen that the process according to the present invention can well control the formation of the core layer(60) / the cladding layer(50) interface in optical. A first embodiment according to the present invention will be explained below. Fine glass particles of SiO 2 as a main component are deposited as a film on a Si substrate by the device of FIG. 4. Here the device of FIG. 4 for depositing fine glass particles will be explained. A reaction vessel has the bottom formed in a rotary turntable 11 (of a 60-mm diameter). A plurality of substrate 1 (silicon wafers of a 3-inch (∼75 mm⊘ diameter) on which fine glass particles should be deposited by the burner 4 are placed in the vessel 12. An exhaust pipe 13 is provided for drawing out fine glass particles which have not been deposited on the substrates 1, and exhaust gas from the vessel 12. The turn-table 11 on which the substrates 1 are mounted on is rotated by a motor (not shown) around respect to a center axis of the reaction vessel 12. The burner 4 reciprocates in the radial direction of the turn-table 11. Thus fine glass particles can be uniformly deposited on the substrates 1. In the bottom of the turn-table 11 there is provided a heater 14 for uniformly heating the substrates 1 mounted on the turn-table 11. Using this device, fine glass particles for forming optical waveguide films are deposited. The turn-table 11 is rotated at a speed of 10 rpm while a fuel and raw material gasses are being fed to the burner 4 for synthesizing fine glass particles. On the other hand, the burner 4 is reciprocated over a 150-mm distance in the radial direction of the turn-table 11 at a speed of 30 mm/min. Thus fine glass particle layers are uniformly deposited on the silicon wafers, which are to be the substrates 1. At this time the silicon wafers are heated up to about 580 °C by the heater 14 in the bottom of the turn-table 11. In this case, the fuel and the raw materials to be fed to the burner 4 for the first step of forming a fine glass particle layer to be the under cladding layer 50 were as follows. The feeding time of the fuel and the raw materials was 10 minutes. SiCl 4 50 cc/min. BCl 3 5 cc/min. POCl 3 3 cc/min. H 2 4 l/min. O 2 6 l/min. Ar 3 l/min. The fuel and the raw materials to be fed to the burner 4 for the second step of forming a glass fine particle layer to be the core layer 60 were as follows. The feeding time of the fuel and the raw materials was 5 minutes. SiCl 4 50 cc/min. BCl 3 5 cc/min. POCl 3 3 cc/min. GeCl 4 14 cc/min. H 2 4 l/min. O 2 6 l/min. Ar 3 l/min. Subsequently, the silicon wafers with the fine glass particle layers formed thereon were heated for 1 hour in at 1300 °C in an ambient atmosphere with a He/O 2 partial pressure ratio of 9/1 to form transparent vitreous under cladding layer 50 and the core layer 60. FIG. 5 shows a film thickness-wise distribution of differences in specific refractive index between the under cladding layer 50 and the core layer 60 prepared in the first embodiment and pure quartz glass. As apparent in FIG. 5, the refractive index changes in a step at the core layer(60)/the cladding layer (50) interface. In this case, the distribution of the refractive indexes were measured by a transference microscope. The fine glass particle layer for the under cladding layer 50 and that for the cobe layer 60, that is, the first and second porous layers 5 and 6, prepared in the first embodiment respectively had bulk densities of 0.32 g/cm 3 and 0.35 g/cm 3 . That is, the bulk densities of the glass fine particle layers for the under cladding layer 50 and the core layer 60 prepared in the first embodiment are generally higher. It is considered that owing to such increased bulk density of the glass fine particle layer, a good interface between the core layer 60 and the cladding layer interface could be prepared. In this case, the determination of the bulk densities were conducted by comparing thicknesses of the glass fine layers and an increase of a weight of the silicon wafer between the first embodiment and a control sample. A second embodiment of this invention will be explained below. The second embodiment is substantially the same as the first embodiment. But in the second step of forming the glass fine particle layer, that is, the second porous layer 6, for the core layer 60, the feed amount of H 2 was decreased to 3 l/min., and that of GeCl 4 was decreased to 10 cc/min. The feed amount of GeCl 4 was decreased, taking into consideration that a sticking probability of the Ge increases accompanying a decrease in a feed amount of H 2 . In the second embodiment as well, a satisfactory specific refractive index difference was obtained between the under cladding layer 50 and the core layer 60. The glass fine particle layer for the under cladding layer 50 and that for the core layer 60, that is, the first and second porous layers 5 and 6, prepared in the second embodiment respectively has specific bulk densities of 0.32 g/cm 3 and 0.23 g/cm 3 . The bulk density of the glass fine particle layer for the under cladding layer 50 prepared in the second embodiment was generally higher, and that of the glass fine particle for the core layer 60 was also generally higher. It is considered that owing to such increased bulk density of the glass fine particle layer for the under cladding layer 50, that is, the first porous layer 5, a satisfactory interface between the core layer 60 and the cladding layer could be prepared. A third embodiment will be briefed below. The process according to the third embodiment is substantially the same as that according to the second embodiment. But in the first step of forming the glass fine particle layer for the under cladding layer 50, the feed amount of H 2 was decreased to 3 l/min. for the initial 8 minutes and increased to 4 l/min. for the last 2 minutes. Subsequently in the same second step as in the second embodiment, the glass fine particle layer for the core layer 60 was formed. The difference in specific refractive index between the under cladding layer 50 and the core layer 60 prepared in the third embodiment was as good as FIG. 5. The bulk density of the glass fine particle layer for the under cladding layer 50 prepared in the third embodiment corresponding to the initial 8 minutes was 0.19 g/cm 3 , and the bulk density of the part corresponding to the last 2 minutes was 0.32 g/cm 3 . That is, the bulk density of the glass fine particle layer for the under cladding layer 50 is higher only in the upper part thereof. It is considered that owing to the increase of the bulk density only in the upper part of the glass fine particle layer, a good interface between the core layer 60 and the cladding layer could be prepared. Now a fourth embodiment of this invention will be described.The process according to the fourth embodiment is basically the same as that according to the third embodiment. In the first step of forming the glass fine particle layer for the under cladding layer 50, the feed amount of H 2 was decreased to 3 l/min. for an entire period of 10 minutes. Following the first step, the feed of the raw materials were stopped with the fuel alone fed, i.e., with H 2 fed by 4 l/min., O 2 fed by 6 l/min. and Ar fed by 3 l/min., so that the glass fine particle layer for the under cladding layer 50 deposited on the silicon wafer is heated. Then the glass fine particle layer for the core layer 60 was formed in the same second step as in the second and the third embodiments. The difference in specific refractive index between the under cladding layer 50 and the core layer 60 prepared in the fourth embodiment was the same as FIG. 5. The bulk density of the whole glass fine particle layer for the under cladding layer 50 prepared in the fourth embodiment was 0.27 g/cm 3 immediately before the formation of the glass fine particle layer for the core layer 60. It is considered that at least the uppermost part of the glass fine particle layer for the under cladding layer 50 was heated, so that the bulk density of the uppermost part has increased. The distribution of the bulk density of the interior of the glass fine particle layer for the under cladding layer 50 is not known. But since the effect of raising a bulk density by the burner with the feed of the raw materials stopped increases toward the uppermost part, the uppermost part of the glass fine particle layer has a bulk density above 0.27 g/cm 3 . Finally controls will be described.The forming conditions of the controls are substantially the same as those of the first to the fourth embodiments. But the fuel and raw materials fed in the first and the second steps are different. In the first step of forming a glass fine particle layer for the under cladding layer 20, the following fuels and raw materials were fed for 10 minutes. SiCl 4 50 cc/min. BCl 3 5 cc/min. POCl 3 3 cc/min. H 2 3 1/min. O 2 6 1/min. Ar 3 l/min. In the second step of forming a glass fine particle layer for the core layer 60, the following fuel and raw materials were fed for 5 minutes. SiCl 4 50 cc/min. BCl 3 5 cc/min. POCl 3 3 cc/min. GeCl 4 10 cc/min. H 2 3 1/min. O 2 6 1/min. Ar 3 l/min. FIG. 6 shows a distribution of specific refractive indexes of the under cladding layer 20 and the core layer 30 prepared in the above-described control. As apparent in FIG. 6, the refractive index smoothly changes in the core layer(30)/the cladding layer(20). The glass fine particle layer for the under cladding layer 20 and that for the core layer 30 respectively had bulk densities of 0.19 g/cm 3 and 0.23 g/cm 3 . A method for measuring a bulk density of the glass fine particle layer will be explained below for reference. The explanation will be made with reference to the control. A glass fine particle layer synthesized under the same conditions as stated above had a thickness of 330 µm. The glass fine particles deposited on a 3 inch (∼75 mm⊘) silicon wafer was totally 290 mg. Accordingly a bulk density of the composite layer of the under cladding layer 20 and the core layer 30 was 0.29 /((0.033 cm) x (7.5 cm) 2 x (3.14/4)) ∼ 0.2g/cm 3 . The glass fine particle layer for the under cladding layer 20 had a thickness of 230 mm and a weight of 190 mg under the same conditions as stated above. Accordingly a bulk density of the glass fine particle layer for the under cladding layer 20 was 0.19 g/((0.023 cm) x (7.5 cm) 2 x (3.14/4)) ∼ 0.19 g/cm 3 a bulk density of the glass fine particle layer for the under cladding layer 20 was estimated to be (0.29 g - 0.19 g)/((0.33 - 0.023)cm x (7.5 cm) 2 x (3.14/4)) ∼ 0.23 g/cm 3 . Finally the relationships between diffusion ratios of Ge measured by electron probe micro-analysis (EPMA) and bulk densities of the porous layer to be the under cladding layer will be explained with reference to FIG. 7. FIG. 8 defines a parameter X for diffusion ratios of Ge. The parameter X is a distance from the position where the Ge concentration is 50 to the position where the Ge concentration is 5, when it is assumed that a peak value of the Ge concentration in the core layer is 100. The Ge concentration measurement was conducted by cutting off the substrate with the glass films which had been formed in transparent glasses, into about 3 mm x 10 mm samples, then the end surfaces of the pieces were polished, and depth-wise Ge concentration distributions of the pieces were measured by EPMA. As such measuring samples, four kinds of samples were prepared in accordance with Embodiment 1 and Control 1, Embodiment 1 with a H 2 flow rate of 4.5 l/min. in the first step, and for Embodiment 1 with a H 2 flow rate of 3.5 l/min. This measuring results are shown in FIG. 7. The parameter X for Ge diffusion ratios defined in FIG. 8 are taken on the vertical axis of FIG. 7, and the bulk densities are taken on the horizontal axis. It is seen in FIG. 7 that when the bulk density of the porous layer to be the under cladding layer is above about 0.3 g/cm 3 , the diffusion of Ge, which is a refractive index increasing dopant, is substantially suppressed substantially within a measuring error (∼µm). This invention is not limited to the above-described embodiments. In the first to the third embodiments, a bulk density of the porous layer is increased by increasing a feed amount of a fuel gas (H 2 in these cases) to the burner. In the fourth embodiment, a bulk density of the porous layer is raised by depositing soot of a low bulk density and heating the surface by the burner. The bulk density is controlled by another method in which a substrate temperature at which the soot sticks is raised. A substrate temperature is raised by the above-described heater in the bottom of the turntable, or by heating from above by a heater, a lamp or other means. In further another possible method for raising a bulk density, in addition to the burner for synthesizing the glass, another burner is provided for the exclusive purpose of heating to assist the former burner in heating the substrate. In a different method it is possible that following sticking of the soot and the formation of the porous glass layer, a substrate temperature is raised by heating by the lower heater in the bottom of the turntable, the upper heater, the lamp or other means so as to increase a bulk density. Otherwise, the burner for synthesizing the glass may be brought near to the substrate upon sticking the soot so as to raise a substrate temperature. The refractive index raising dopant is not limited to GeO 2 , and instead P 2 O 5 , Al 2 O 3 or others may be used. A refractive index lowering dopant may be added to a material of the cladding layer. The substrate is not limited to a Si substrate, and instead Al 2 O 3 substrates, SiC substrates, ZrO 2 substrates, etc. may be used. As described above, a part of the first porous layer near the second porous layer has a higher bulk density. Owing to the shielding effect of the neighboring part of a higher bulk density, a refractive index increasing dopant in the second porous layer, which evaporates when the first and the second porous layers are sintered, is prevented from diffusing into the first porous layer. As a result, an optical film structure for an optical waveguide can be formed with the core/the cladding optical layer interface accurately controlled. From the invention thus described, it will be obvious that the invention may be varied in many ways and all such modifications as would be obvious to one skilled in the art and that fall within the scope of the following claims are intended to be included.

Claims: A process for forming an optical film structure from which can be manufactured an optical waveguide having under (50) and over (70) cladding layers and a core (61) surrounded thereby, comprising: a first step of depositing glass soot (5) on a substrate (1) by Flame Hydrolysis Deposition (FHD) to form a first porous layer (5) to be the under cladding layer (50) with at least the upper part of the under cladding layer having at least a predetermined bulk density; a second step (Fig. 2C) of depositing glass soot (6) with added refractive index increasing dopant onto the first porous layer (5) to form a second porous layer (6) to be the core layer (60); and a third step (Fig. 2D), of vitrifying the first and the second porous layers to form transparent glass vitreous layers (50,60), said predetermined bulk density being enough to substantially prevent diffusion into the first porous layer (5) of the refractive index increasing dopant added to the second porous layer (6). A process for forming an optical film structure according to claim 1, wherein the first step includes increasing the bulk density of at least some of the layer of the deposited soot (5) above the predetermined bulk density. A process for forming an optical film structure according to claim 1, wherein the first step includes depositing glass soot on the substrate by FHD so that a layer of the deposited soot (5) has a bulk density lower than the predetermined bulk density. A process for forming an optical film structure according to claim 1, wherein the first step comprises depositing glass soot on the substrate by FHD so that a layer of the deposited soot (5) has a bulk density higher than said predetermined bulk density. A process for forming an optical film structure according to claim 2, wherein the increase of the bulk density is achieved by raising the temperature of the soot area following the deposition of the soot. A process forming an optical film structure according to claim 3, wherein a glass soot layer (5) of higher than said predetermined bulk density is deposited by raising the temperature of the substrate (1) to a value which is higher while the soot is being deposited than that during deposition of soot with the lower density. A process for forming an optical film structure according to claim 3, wherein the soot of higher than said predetermined bulk density is deposited by positioning a glass synthesising burner (4) for use in FHD at a position nearer to the substrate (1) during the deposition of the soot than during the deposition of the deposited soot layer with the lower bulk density. A process for forming an optical film structure according to claim 3, wherein the soot of density higher than said predetermined bulk density is deposited by feeding a larger amount of a fuel gas to a glass synthesising burner (4) for use in FHD during the deposition of the soot than during the deposition of the deposited soot layer with the lower bulk density. A process for forming an optical film structure according to claim 4, wherein the soot is deposited by increasing the temperature of the substrate (1) during the deposition of the soot so that the layer of the deposited soot has higher bulk density. A process for forming an optical film structure according to claim 4, wherein the soot is deposited by positioning nearer the substrate (1) a glass synthesising burner (4) for use in FHD during the deposition of the soot so that the layer of the deposited soot has higher bulk density. A process for forming an optical film structure according to claim 4, wherein the soot is deposited by feed a larger amount of a fuel gas to a glass synthesising burner (4) for use in FHD so that the layer of the deposited soot has the higher bulk density. A process for forming an optical film structure according to any preceding claim wherein the refractive index increasing dopant is any of GeO 2 , P 2 O 5 , Al 2 O 3 . A process for forming an optical film structure according to any preceding claim wherein said predetermined bulk density is about 0.3 g/cm 3 . A process for forming an optical film structure according to any preceding claim wherein said predetermined bulk density is higher than that of the second porous layer (6). A process for forming an optical waveguide having under and over cladding layers and a core surrounded by them, comprising: forming an optical film structure on a substrate (1) by the process of any preceding claim; etching an optical waveguide pattern (61) from the second vitreous layer (60); forming a third porous layer (7) to be an over cladding layer on the second vitreous layer (61) by FHD; and vitrifying the third porous layer to form a transparent glass vitreous layer.

Inventors: AIKAWA HARUHIKO, HIROSE CHISAI, ISHIKAWA SHINJI, KANAMORI HIROO, SAITO MASAHIDE, URANO AKIRA, AIKAWA, HARUHIKO, HIROSE, CHISAI, ISHIKAWA, SHINJI, KANAMORI, HIROO, SAITO, MASAHIDE, URANO, AKIRA, AIKAWA, HARUHIKO, C/O YOKOHAMA WORKS, Hirose, Chisai, c/o Yokohama Works, ISHIKAWA, SHINJI, C/O YOKOHAMA WORKS, KANAMORI, HIROO, C/O YOKOHAMA WORKS, SAITO, MASAHIDE, C/O YOKOHAMA WORKS, URANO, AKIRA, C/O YOKOHAMA WORKS
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LIMITED
Application year: 1992
Main classification: C03B37
IPC codes: G02B6, C03C17, C03B19