COPYING PAPER IN SHEET FORM

Abstract: The present invention provides a copying paper which both has good printability and which can be run satisfactory in sheet copying machines. The invention relates to copying paper which inlcudes a base paper based on a fibre starting material of which at least 60% is comprised of short fibre pulp refined to 17-22 DEG SR and at least 20% long fibre pulp refined to 25-38 DEG SR, and filler in an amount of 19-28%, calculated on the base paper. At least one side of the base paper is coated to a surface weight of 12-18 g/m<2>. The copying paper is characterized in that the base component(s) of the coating layer includes/include either a) 100 parts of calcium carbonate distributed according to 60-80 parts of calcium carbonate of which 90% have a particle size beneath 2 mu , and 40-20 parts of calcium carbonate of which 95% have a particle size beneath 2 mu ; or b) 60-90 parts of calcium carbonate of which 90% have a particle size beneath 2 mu , and 40-10 parts of kaolin clay of SPC (selected particle size) quality; and in that the surface coating also includes at least binder and hardener.

Description: Copying paper in sheet form Technical field The present invention relates to copying paper in sheet 2 form having a surface weight of from 80 to 200 g/m . The copying paper is comprised of base paper and coating layer applied to at least one side of the base paper, preferably to both sides thereof. The coating layer has a surface 2 weight of 12-18 g/m , which means, that the paper is fully coated, i.e. essentially the whole of the surface of the paper is covered with the coating layer. The above 2 mentioned range of surface weight of from 80 to 200 g/m refers to the surface weight of the base paper plus the surface weight of the coating layer, alternatively, of the coating layers. Background art There has developed over recent years a need for an improved copying paper which will enable other subjects than text to be copied thereon when desired and which will provide high quality print, for example high quality four colour reproduction. The paper is normally pre-printed and then used for copying purposes. One prerequisite for ob- taining good quality print is that the paper is coated with pigment. Conventional copying paper is normally not coated and cannot therefore be used effectively for the intended purpose. Many types of copying paper are surface treated, for instance, with starch, polyvinyl alcohol, carboxymethyl cellulose, synthetic polymers, etc., and this surface treatment sometimes being called coating, but this type of coating in which the coating substances are applied in small quantities is quite different from pigment coating. By the just mentioned is meant the use, for instance, of calcium carbonate, clay, and many more pigments, either individually or in combination with one another and in relatively large quantities. Rolls of paper of conventional offset quality and in¬ tended for combined printing and copying purposes are commercially available today. The use of this paper, how¬ ever, is restricted to those types of copying machines, for instance laser printers, which are constructed for use with paper rolls. All copying machines which are designed for the use of sheet copy are unable to use copy paper in roll form. It has been found that when converting rolls of pre¬ printed paper to sheet form so as to enable said paper to be used with sheet feeding copying machines, problems arise with the runability of the machine, i.e. the sheets repeat¬ edly cause stoppages. Conventional copying paper has the aforesaid drawback, that a high quality print cannot be obtained. Disclosure of the Invention Technical problem It has been found difficult to combine good printabi- lity and good runability for one and the same copying paper in sheet form in copying machines, for example laser printers. One of the problems is that fully coated paper cannot be fed into the copying machine in a satisfactory manner, which results in repeated stoppages. This may be because of the friction of the paper. Another problem is that the paper mentioned is often unable to retain its original flat shape during the copying process, which also results In repeated stoppages. Solution The present invention provides a solution to the afore¬ said problems and relates to a copying paper which com¬ prises a base paper based on a fibre starting material of which at least 60% is comprised of short fibre pulp refined to 17-22°SR and of at least 20% long fibre pulp refined to 25-38° SR, together with filler in an amount of 19-28%, calculated on the base paper, and on at least one side of the base paper a coating layer of a surface weight of 12-18 2 g/m , characterized in that the base component(s) of the coating layer (include) either a) 100 parts of calcium carbonate distributed according to 60-80 parts of calcium carbonate of which 90% have a particle size beneath 2 um and 40-20 parts of calcium carbonate of which 95% have a particle size beneath 2 um; or b) 60-90 parts of calcium carbonate of which 90% have a particle size beneath 2 um and 40-10 parts of kaolin clay of SPC (selected particle size) quality; and in that the surface coating also includes at least binder and hardener. The binder preferably consists of starch and/or latex. It is especially preferred that the starch is oxidized and that the latex is of the open styrene butadiene type. The starch is preferably added in an amount of 5-7% calculated on dry pigment or base component(s) . Latex is preferably added in an amount of 6-8%, calculated on dry pigment or base component(s) . This applies to the addition of both of these chemicals to the coating color and later the paper. If only one of these chemicals is used, the aforesaid quan¬ tity must be increased. It is preferred that the hardener is free from formalin. For instance, glyoxal can be used in an amount of 0.5-1.5% calculated on dry pigment or base component(s) . Other hardeners that can be used are ammonium zirconium carbonate, ethanedial, which is a polymer con- taining tetra-hydro-4-hydroxy-5-methyl-2-(lH) pyrimidinone and which is propoxylated and a hardener retailed under the trade name Nopcote 1670 which contains an imidazoline com¬ pound, which is a reaction product of glyoxal and urea. According to one embodiment of the invention, the coating layer, and therewith the paper, contains 1-3 parts of stearate, preferably calcium stearate or ammonium stearate, calculated on 100 parts of base component(s) . The dry solids content of the coating color, and there- with also of the newly applied coating layer, shall lie within the range 65-70%. It is absolutely preferred that the copying paper shows a coating layer on its both sides. The filler present in the copying paper may be any known filler whatsoever, although calcium carbonate is preferred. With regard to applying print to the copying paper, this is normally done prior to copying. Mentioned printing may be effected either on paper which has already been converted to sheet form or on paper which is in roll form. In this latter case, the paper must be converted to sheet form prior to the copying stage. Coating colors of the aforedescribed kind primarily result in a mat paper, i.e. a paper whose gloss is beneath 20% measured in accordance with Lehman (70-degree incident light). Within the scope of the invention it is " also possible to produce a glossy paper. In this case, the composition of the coating color will differ slightly from the composition which provides an optimal mat copying paper and possibly prefers an extra chemical addition. Advantages The copying paper according to the invention has good printability as well as good runability in copying machines. By choosing the correct base paper and a coating layer of correct composition, it has been found possible to achieve the same reliability in the copying machine with regard to preprinted copying paper as that achieved with conventional copying paper. The frequency at which stoppages occur in the machine when using the copying paper according to the invention is extremely low. Naturally, the paper according to the invention can be run efficiently and effectively through copying machines as unprinted paper. Furthermore, the chemicals from which the coating layer is comprised are relatively inexpensive in combination, therewith enabling the price of the copying paper to be kept at a relatively low level. Best mode of carrying out the invention The copying paper according to the invention will below be described in more detail, and the portion is ended with a working embodiment. As mentioned before, the fibre com¬ position of the base paper shall comprise at least 60% of short fibre pulp and at least 20% of long fibre pulp. By short fibre pulp is meant chemical pulp, preferably sulphate pulp, manufactured for instance from hardwood, such as birch, eucalyptus, beech, aspen, and similar types of wood. By long fibre pulp is meant chemical pulp, pre¬ ferably sulphate pulp, manufactured for instance from soft¬ wood, such as pine, spruce, and other types of wood. ' Another usable chemical pulp is sulphite pulp. The remaining 20% of the fibre composition may consist of one of the two aforesaid types of pulp or of a mixture thereof. It is also fully possible to mix in other types of pulps, such as sulphite pulp and/or high yield pulp, such as mechanical pulp for instance. The fibre composition of the base paper, refinement of the different pulps and the filler content of the paper shall be adapted so that the finished paper has low curling tendencies (reactivity) . By curling is meant that the paper deviates from the flat shape and adopts varying curved shapes. It applies throughout, that the pulps shall be refined only to a moderate extent, i.e. the paper shall be imparted other refinement dependent properties to the best possible extent, while at the same time fulfilling the aforesaid conditions. The various pulps are refined separately to the refinement levels earlier mentioned in °SR, i.e. degrees Schopper-Riegler. The filler shall be present in an amount of 19-28%, preferably 20-25%, calculated on the base paper. The filler is preferably calcium carbonate in different forms, such as chalk, ground marble and calcium carbonate precipitates. It is also possible, however, to use other fillers, either totally or partially, such as kaolin clay, talcum and gypsum (CaSO.). The manner in which the base paper is constructed and produced is highly significant to the ability to run the finished paper in copying machines. The composition of the coating layer is highly significant to the runability of the paper in copying machines, and sometimes a decisive significance. The quantity of coating substance applied is also significant to some extent. The coating layer or layers of the inventive copying paper is/are produced from one of two coating colors. The pigment or base component of one color consists of 100 parts calcium carbonate. Calcium carbonate having different particle size distributions is available and the calcium carbonate is said to have different degrees of fineness, such as fine, superfine, etc. In this case, 60-80 parts of such calcium carbonate is used, of which 90% of the particles have a size beneath 2 um and 40-20 parts of a still finer calcium carbonate, namely a calcium carbonate of which 95% of the particles have a size beneath 2 um. In addition to the earlier mentioned ingredients in the form of binder and hardener, the color may also include an opti- cal whitener, different types of tinting colours, and a substance for adjusting the pH of the color. Examples of such substances Include sodium hydroxide and ammonium. The _ amounts in which the binder and hardener are present have been given in the aforegoing. The remaining chemicals are present in a very small quantity, i.e. in an amount of 1 part or less. Additional chemicals may also be added to the color. The pigment or base component of the other color com¬ prises 60-90 parts calcium carbonate, where 90% of the particles have a size smaller than 2 um, and 40-10 parts of kaolin clay of SPS quality. SPS is an acronym of the English language designation "selected particle size". This color also includes binder and hardener in the aforesaid quantities. The color may also include an optical whitener, tinting color and an alkali for adjusting the pH of the color, etc. The color will also preferably include a com- paratively large quantity of stearate. Mentioned additive has been found to provide the copying paper with good runability in copying machines. The stearate probably assists in imparting the correct surface property to the paper and above all the correct friction. Stearate may also be added to the first color. With regard to the aforesaid two coating colors, it can be mentioned that the use of starch as a binder in top coatings is normally avoided, since starch causes pronounc¬ ed binder migration, which results in mottling. One advan- tage afforded by the addition of starch is that the paper obtains good stiffness and good toner adhesion, and starch " also prevents the paper from becoming sticky and adhering to copying machine surfaces when it is exposed to high temperatures. It is not thought that stearate has earlier been used in coating colors in the aforesaid quantities. According to one preferred embodiment of the invention, both sides of the copying paper are provided with a coating layer. In this case, the paper is coated in a two station coating machine. As previously mentioned, the coating color shall have a relatively high dry solids content, namely within the interval 65-70%. Subsequent to coating the paper, the paper is dried first on the one coated side and then on the other side. The first coated side of the paper is dried in a manner such that the paper will include 6-9% water and drying of the other side of the paper is continu¬ ed until the paper has a water content of 4-5%. Manufacturing and properties of a copying paper in accordance with the invention are below described in an Example In comparison with manufacturing and properties of copying paper outside the invention. Example 1 A base paper was produced on a 6.5 m wide Valmet type paper machine in the following manner: Three different types of pulp fibres were mixed to¬ gether in the following quantities: Birch sulphate pulp = 70%; pine sulphate pulp = 24%; and spruce sulphite pulp = 6%. The three pulps were refined separately to the follow¬ ing degrees of refinement, prior to being mixed together: Birch pulp = 18°SR; pine pulp - 34°SR; and spruce pulp = 18°SR. Filler, mainly calcium carbonate, was supplied in an amount of 21.2% in finished paper. 131 kg of filler were supplied for each tonne of paper in dispersion while the remaining filler was supplied via incoming paper broke. The stock also contained the following chemicals: Starch (cationic active) = 4.5 kg/tonne paper Size (alkyd ketene dimer) = 8.5 Retention agent 1 (poly- acrylamide) = 1.7 Retention agent 2 (bentonite clay) = 0.16 Optical whitener (Blankophor P) = 0.4 Tinting colour (ethyl violet) = 0.02 The paper was surface sized with an 8%-surface sizing 2 starch in a quantity of about 3 g/m . The aforedescribed base paper had a surface weight of 2 97 g/m and the coating colors A, B and C were applied to the paper. The coating color A was applied to the base paper both in a pilot coating machine and in a full scale test, whereas the coating colors B and C were applied to the base paper solely in the pilot coating machine. The three coating colors had the following compositions. A 80 parts calcium carbonate retailed under the trade name Hydrocarb 90, in a 75%-dispersion. 90% of this calcium car¬ bonate has a particle size smaller than 2 um. 20 parts of the SPS-coating clay (kaolin) / which was dispersed with 0.2 parts polyacrylate to a dry solids content of 68%. These two pigments, or base components, were mixed to- gether. There were then added. 6 parts of styrene butadiene latex retailed under the trade name Dow 905; and 6 parts oxidized starch retailed under the trade name Cerestar 05595. boiled to a dry solids content of about 32%. There was then added in the following order: 0.8 parts hardener (glyoxal); 2 parts calcium stearate retailed under the trade name Nopcoat C104; 0.8 parts optical whitener retailed under the trade name Blankophor PC; 0.001 parts tinting colour (levanyl violet). The color was brought to a pH = 8.5, by adding ammo¬ nium. The color had a dry solids content of 65%. B 80 parts calcium carbonate retailed under the trade name Hydrocarb 90 in a 75%-dispersion. 90% of this calcium car¬ bonate has a particle size smaller than 2 um. 20 parts calcium carbonate retailed under the trade name Setacarb in a 75%-dispersion. 95% of this calcium car- bonate has a particle size smaller than 2 um. These two pigments, or base components, were mixed to¬ gether. There were then added: 6 parts styrene butadiene latex, retailed under the trade name Dow 905; and 6 parts oxidized starch, retailed under the trade name Cerestar 05595, boiled to a dry solids content of about 32%. There were then added in the following order: 0.8 parts hardener (glyoxal); 0.8 parts optical whitener retailed under the trade name Blankophor PC; 0.001 parts tinting colour (levanyl violet). The color was brought to pH = 8.5, by adding ammonium. The color had a dry solids content of 68%. C 100 parts SPC-coating clay (kaolin) dispersed with 0.2 parts polyacrylate to a dry solids content of 65%. Added to the clay were: 6 parts styrene butadiene latex retailed under the trade name Dow 905; and 6 parts oxidized starch retailed under the trade name Cere¬ star 05595, boiled to a dry solids content of about 32%. Added in the following order were: 0.8 parts hardener (glyoxal); 0.8 parts optical whitener retailed under the trade name Blankophor PC; 0.001 parts tinting colour (levanyl violet). The color was brought to pH = 8.5 by adding ammonium. The color had a dry solids content of 59%. The coatings were applied under realistic conditions, partly on a pilot coating machine (the colors A, B and C) having curved blades, at a speed of 800 m/minute and partly on a full-scale Jagenberg coating machine (color A) having a width of 3.3 m and curved blads at a speed of 800 m/- minute. The base paper was coated on both sides in all instances, with an amount of color corresponding to 16 2 g/m . The finished, coated paper had a surface weight of 2 130 g/m . All paper coated had a mat finish according to the earier given definition. With regard to the ability of running the paper through copying machines, it has been found that in order to obtain good runability, the friction of different material shall be the following. The friction between the feed belt and the paper shall be greater than the friction between the retard belt and the paper, which in turn shall be greater than the friction between paper and paper. The friction between the different materials, including the four papers, was measured according to ASTM (Americal Society for Testing and Materials) D1894. In one case, friction was measured by measuring the friction generated between the feed belt and the felt side of the paper (FS) and, in the other case, between the feed belt and the wire side (WS) of the paper. Similar measure¬ ment was made with regard to the retard belt and the paper. Both static and kinetic friction were measured on the papers. The results are set forth in the following Table 1. Table 1 Friction in grams Other tests have shown that when mixing solely clay a the pigment or when mixing excessively large quantities o clay in the coating pastes, the runability of the paper i all copying machines is influenced negatively, such as in th case of the paper Pilot C. Furthermore, the exclusion of th stearate addition in the paper produced in accordance wit Full Scale A and Pilot A resulted in impaired runability of the paper in all copying machines. It has been found that the difference between static and kinetic friction of the paper mirrors the runability of the paper in copying machines. Double paper feed and other pheno¬ mena which can cause stoppages in the copying machines have been found to increase with decreasing differences in static and kinetic friction of the paper. The numerical values were repeated from Table 1, and the difference between the numerical values can be seen from the following Table 2. Table 2 Friction in grams Test Color Static/Kinetic Difference 30 23 28 1 The first three papers in the above Tables are in accordance with the invention, whereas the fourth paper was not, i.e. the coating color C was applied to this fourth paper. The difference between the static and kinetic fric¬ tion of the inventive papers is 23 or more, whereas the corresponding difference of the non Inventive paper (0-sample) is as small as 1. In order for the copying paper to be totally satisfactory and to have totally satisfactory runability, a standard has been set whereby 5 000 copies (simplex) and 3 000 copies (duplex) can be copied in sequence without causing a machine stoppage. By simplex Is meant that copies are made on only one side of the paper, while duplex means that copies are made on both sides of the paper. ± All four papers were tested on four Rank Xerox copying machines, designated 4050, 4090, 5090 and 9700. 5 000 copies were taken with the aforesaid three inventive papers without the occurrence of a stoppage, both with simplex and duplex copying, whereas the non inventive paper, i.e. the 0-sample, resulted in more than one stoppage with each 1 000 copies taken, with both simplex and duplex copying. These tests show that the content of the paper coating layer, or in other words the coating layer construction, is decisively significant to the behaviour of the paper when fed into a copying machine and during the document copying process. In this case, the reference sample (0-sample) has also been provided with a base paper constructed in accor¬ dance with the invention. If the coating color C had been applied to some other kind of base paper, the difference in runability of the paper in the copying machine between the papers would have been still more pronounced.

Claims: CLAIMS 1. A copying paper comprising a base paper based on fibre starting material of which at least 60% is a short fibre pulp refined to 17-22°SR and at least 20% is a long fibre pulp refined to 25-38°SR, and filler to an amount of 19-28%, calculated on the base paper, and on at least one side of the base paper a coating layer of a surface weight 2 of 12-18 g/m , c h a r a c t e r i z e d i n that the base component(s) of the coating layer includes (include) either a) 100 parts of calcium carbonate distributed according to 60-80 parts of calcium carbonate of which 90% have a particle size beneath 2 um, and 40-20 parts of calcium carbonate of which 95% have a particle size beneath 2 um; or b) 60-90 parts of calcium carbonate of which 90% have a particle size beneath 2 um, and 40-10 parts of kaolin clay of SPC (selected particle size) quality; and in that the surface coating also includes at least binder and hardener. 2. A copying paper according to Claim 1, c h a r a c t e r i z e d in that the binder consists of starth and/or latex. 3. A copying paper according to Claim 2, c h a r a c t e r i z e d in that the starch is oxidized and the latex is of open styrene butadiene type. 4. A copying paper according to Claim 1, c h a r a c t e r i z e d in that the hardener contains no formalin. 5. A copying paper according to Claims 1-4, c h a r a c t e r i z e d in that the coating layer in¬ cludes 1-3 parts stearate, preferably calcium stearate or ammonium stearate, calculated on 100 parts base compo- nent(s). 6. A copying paper according to Claims 1-5, c h a r a c t e r i z ed in that when newly applied, the coating layer has a dry solids content of 65-70%. 7. A copying paper according to Claims 1-6, c h a r a c t e r i z e d in that the coating layer is applied to both sides of the base paper. 8. A copying paper according to Claims 1-7, c h a r a c t e r i z ed in that the filler is calcium carbonate. 9. A copying paper according to Claims 1-8, c h a r a c t e r i z e d in that the paper is converted to sheet form prior to taking a copy.

Inventors: KARLIN NILS AAKE, KARLIN, NILS, AAKE
Applicants: MO OCH DOMSJOE AB, MO OCH DOMSJOE AKTIEBOLAG
Application year: 1992
Main classification: D21H19
IPC codes: D21H19, D21H21, G03G7