SUNSCREEN COMPOSITIONS

Abstract: Sunscreen compositions comprising from about 0.5 % to about 30 % by weight of a metal oxide which is titanium dioxide, zinc oxide or a mixture of both these oxides and from about 0.001 % to about 2 % by weight of iron oxide particles having a mean primary particle size of less than about 200 nm are described. The metal oxide may be substantially in the form of particles having a mean primary particle size of less than about 100 nm. The preferred form of iron oxide is iron (III) oxide. Optionally, either the metal oxide or the iron oxide particles or both are coated with a phospholipid such as lecithin. The sunscreen compositions may include phosphate anions. Sunscreen compositions comprising the above ingredients in both oil-in-water and water-in-oil emulsions are also disclosed.

Description: SUNSCREEN COMPOSITIONS The present invention relates to the use of iron oxide particles in sunscreen compositions. The term "sunscreen" is used herein to encompass tanning lotions, sunscreens and sunblockers which are intended for use on the body to provide protection against the sun's rays or other UV sources. The use of titanium dioxide as a sunscreening agent is well known. The amount of titanium dioxide present in a sunscreen composition depends on the use for which the composition is intended. Amounts as low as 1% may be sufficient in the so-called suntanning products which are not intended to prevent the sun's rays reaching the skin whereas the so-called sunblocks which are intended to prevent substantially all of the sun's rays reaching the skin may require levels of 15 to 20%. It has been found that when the amount of titanium dioxide in the sunscreen composition exceeds about 5% the composition exhibits a blue-white pearl effect which is aesthetically unattractive and limits the amount of titanium dioxide which can be incorporated into a sunscreen composition which is acceptable to the user. Use of zinc oxide as a sunscreening agent is also well known, either on its own or combined with titanium dioxide. Hereinafter, throughout the specification and claims the term 'metal oxide' is defined as a metal oxide consisting of titanium dioxide only, zinc oxide only, or a mixture of both these oxides. In preferred sunscreen compositions of the present invention the metal oxide is titanium dioxide only. Pigment grade iron oxides of coarse particle size have been used in sunscreen compositions as tinting agents, typically at a level of 5% w/w, to mask the blue-white pearl effect. However, such compositions suffer from the disadvantage that the iron oxide tinting agent rubs off in use and may cause unacceptable discolouration or staining of clothing. Surprisingly we have found that the use of iron oxide of a particular particle size may be used in sunscreen formulations at comparatively low levels therefore minimising unacceptable rub off yet permitting the use of comparatively high levels of titanium dioxide without the disadvantage of an unacceptable blue-white pearl. The present invention provides a sunscreen composition comprising from about 0.5% to about 30% by weight of metal oxide and from about 0.001% to about 2% by weight of iron oxide particles having a mean primary particle size of less than about 200nm. Preferably the composition comprises metal oxide particles having a mean primary particle size of less than about lOOnm, more preferably from about 5nm to about 50nm and most preferably from about 15nm to about 30nm. Sunscreen compositions have recently become available in which the mean primary particle size of titanium dioxide particles lies in the range 1 to lOOnm. Titanium dioxide of the above mean primary particle size is usually ref rred to as "microfine ,r . A suitable grade of titanium dioxide is available from Degussa under the trade designation P25 and from Tayca Corporation under the trade designation MT150W, MT600B or MT500B. Preferably a composition of the present invention comprises from about 0.1% to about 20%, more preferably from about 1% to about 15% and most preferably from about 4% to about 12% by weight of metal oxide particles having a mean particle size of less than about lOOnm. Preferably a composition of the present invention comprises from about 0.01% to about 1%, more preferably from about 0.02% to about 0.5% and most preferably from about 0.05% to about 0.25% by weight of iron oxide particles having a mean primary particle size of less than about 200nm. Preferably the iron oxide particles have a mean particle size from about O.Olnm to about lOOnm, more preferably from about O.lnm to lOnm and most preferably from about lnm to 5nm. In a preferred form of the present invention the iron oxide particles comprise iron (III) oxide. One particularly preferred iron (III) oxide is available from Mach I Inc. under the trade designation Super-Fine Iron Oxide. Preferably the particles of iron oxide or metal oxide or both can be substantially coated with a phospholipid, such as lecithin. This helps reduce agglomeration of the particles. Sunscreen compositions comprising phospholipids are described in the applicant's international patent application WO 90/06103 the disclosures of which are hereby incorporated by reference. In order to substantially reduce or prevent the discoloration of the metal oxide that may occur during storage of sunscreen compositions, the compositions of the present invention may further comprise from about 0.025% to about 30% by weight of the composition of phosphate anions. Sunscreen compositions containing phosphates are described in the applicants international patent applicaiton WO90/09777, the disclosures of which are hereby incorporated by reference. A further aspect of the present invention provides a sunscreen composition comprising a water-in-oil emulsion which comprises: a) from about 0.5% to about 30% by weight of metal oxide particles having a mean primary size of less than about lOOnm, b) from about 0.001% to about 2% by weight of iron oxide particles having a mean primary particle size of less than about 200nm, c) from about 5% to about 70% by weight of an oil phase, d) from about 1% to about 15% by weight of an emulsifier, and e) at least about 20% by weight of an aqueous phase. A still further aspect of the invention provides a sunscreen composition comprising an oil-in-water emulsion which comprises: a) from about 0.5% to about 30% by weight of metal oxide particles having a mean particle size of less than about lOOnm, b) from about 0.001% to about 2% by weight of iron oxide particles having a mean primary particle size of less than about 200nm, c) from about 5% to about 60% by weight of an oil phase, d) from about 1% to about 20% by weight of an emulsifier, and e) at least about 35% by weight of an aqueous phase. Other sunscreening agents may be incorporated into the sunscreen compositions of the present invention. Examples of suitable further sunscreening agents include a) p-aminobenzoic acids, esters and derivatives (for example, 2-ethylhexyl p-dimethylaminobenzoate, or the octyl ester of p-aminobenzoic acid) , b) methoxycinnamate esters [for example, 2-ethylhexyl p-methoxycinnamate, 2-ethoxyethyl -methoxycinnamate or ,β-di-(p-methoxy- cinnamoyl) - ' - (2-ethylhexanoyl)-glycerin] , c) benzo- phenones (for example oxybenzone) , d) dibenzoylmethanes and e) salicylate esters. Any additional sunscreening agent is present in an amount from about 0.1% to about 10% by weight of the composition. The oil phase of the water-in-oil and oil-in-water emulsions of the present invention may comprise a) hydrocarbon oils such as paraffin or mineral oils, b) waxes such as beeswax or paraffin wax, c) natural oils such as sunflower oil, apricot kernel oil, shea butter or jojoba oil, d) siiicone oils such as dimethicone, cyclomethicone or cetyldimethicone, e) fatty acid esters such as isopropyl palmitate or isopropyl myristate, f) fatty alcohols such as cetyl alcohol or stearyl alcohol, or g) mixtures thereof. In preferred water-in-oil compositions of the present invention, the oil phase comprises from about 5% to about 60% by weight of the composition. In preferred oil-in-water compositions of the present invention, the oil phase comprises from about 10% to about 30% by weight of the composition. The emulsifiers used may be any emulsifiers known in the art for use in water-in-oil or oil-in-water emulsions. It has been found that particularly effective water-in-oil sunscreen compositions can be prepared by using an emulsifier or mixture of emulsifiers selected from: a) ethoxylated fatty alcohols, for example the emulsifier available commercially under the trade name Brij (ICI) b) ethoxylated fatty acids and their esters such as ethoxylated stearates, for example the emulsifier available commercially under the trade name Myrj (ICI) c) sorbitan esters, such as the emulsifier available commercially under the trade name Span (ICI) d) ethoxylated sorbitan esters, such as the emulsifier available commercially under the trade name Tween (ICI) e) ethoxylated mono-, di- and tri-glycerides, for example the emulsifier available commercially under the trade name Arlatone (ICI) f) silicon emulsifiers such as siiicone polyols, available commercially for example under the trade name Abil WS08 g) anionic emulsifiers for example cetylstearyl sulphates available under the trade name Dehydag and anionic esters of mono and diglyercides available under the trade name Grindtek h.) cationic emulsifiers for example dimethyl- distearylammonium chloride available under the trade name Genamin DSAC. Particularly effective oil-in-water sunscreen compositions can be prepared by using an emulsifier or mixture of emulsifiers selected from known cosmetically acceptable emulsifiers which include a) fatty acid soaps such as potassium stearate, b) ethoxylated fatty alcohols, for example the emulsifier available commercially under the trade name Brij (ICI) , c) sorbitan esters, for example the emulsifier available commercially under the trade name Span (ICI) , d) ethoxy¬ lated sorbitan esters, for example the emulsifier available commercially under the trade name Tween (ICI) , e) ethoxylated fatty acid esters such as ethoxylated stearates, for example the emulsifier available commercially under the trade name Myrj (ICI) , f) ethoxylated mono-, di-, and tri-glycerides, for example the emulsifier available commercially under the trade name Arlatone (ICI), or g) mixtures thereof. The amount of emulsifier present in the oil-in-water compositions of the present invention is preferably from about 1% to about 10% by weight of the composition. The compositions of the present invention may additionally comprise other components which will be well known to those skilled in the art for example emollients such as isopropyl myristate or a triglyceride of a fatty acid (e.g. lauric triglyceride or capric/ caprylic triglyceride) , moisturisers such as D- panthen-ol, humectants such as glycerin or 1,3-butylene- glycol, antioxidants such as DL-A-tocopheryl-acetate or butylated hydroxytoluene, emulsion stabilising salts such as sodium chloride, sodium citrate or magnesium sulphate, film formers to assist spreading on the surface of the skin such as alkylated polyvinyl- pyrrolidone, preservatives such as bronopol, sodium dehydroacetate, polyhexamethylenebiguanide hydro- chloride, isothiazolone or diazolidinylurea, perfumes and colouring. The compositions of the present invention described hereinbefore provide adequate protection against both UVA and UVB radiation in a composition which is aesthetically pleasing to the user. Preferred compositions are substantially transparent when applied to the skin. The opacity or whiteness of compositions may be estimated by trained observers by subjective visual analysis of the relative transparency of the composition spread onto skin. However, a quantitative assessment of the opacity or whiteness of compositions may be obtained as follows. A circular area of diameter 31mm was marked on the forearm of a volunteer and the surface reflectance of that area measured with a Minolta chromometer. lOμl of product was then applied to the test site and spread evenly with a glass rod. The product was left to dry for 2 to 3 minutes and then the surface reflectance of the area measured again. Each product was tested on several volunteers. The difference between the mean surface reflectance (L-value) before and after product application gives a quantitative indication of the whiteness of the product. Products giving a mean L-value increase of greater than 5.5 were considered to be cosmetically unaccept¬ able. Preferred compositions according to the invention had a mean L-value increase of less than about 5.0. The efficacy of compositions of the present invention as sunscreens was demonstrated as follows. The Simpson's ratio of UVA to UVB absorption was measured by the method described in full by Diffey and Robson in J. Soc. Cosmet. Chem. , 40., 127-133 (1989) but which is summarised below. Adhesive tape commercially available from 3M- Company, USA, under the trade name Transpore® was used as the medium to which the product was applied. This tape is UV-transparent and has a textured surface which has been found to distribute sunscreen compositions in a way similar to the uneven topography of human skin. A piece of tape (75mm x 65mm) was placed over the input slit of an f 3.4 grating monochromator (Applied Photophysics Ltd, UK) , attached to a photomultiplier detector, and illuminated with "white" light from a 75 xenon arc source. The intensity of the radiation transmitted through the tape was measured by recording the photocurrent in 5nm steps from 290-400nm. lOOμl of sunscreen (2.Omg/crrr') was evenly distributed onto the tape surface, the tape replaced over the monochromator input slit and transmission measurements were repeated. For each product the transmittance was determined at 12 separate subsites within the 77 x 65mm application site. The Simpson's ratio of absorption in the range 320-400nm (UVA) and absorption in the range 290-320nm (UVB) was then calculated from the mean measurement at each wavelength. The invention will now be illustrated by the following non-limiting Examples, which are given by way of example only. Example 1 A sunscreen composition comprising the following constituents was prepared: % w/w 1) Isopropyl palmitate 2) Lecithin (sold under the trade name P Centrolex) 3) Sorbitan sesquioleate (sold under the trade name Arlacel 83) 4) Butylated hydroxytoluene 5) Cetyl Dimethicone 6) A mixture of siiicone copolyol and cyclomethicone (sold under the trade designation Siiicone Fluid 3225 C) 7) Cyclomethicone (sold under the trade designation Siiicone Fluid 345DC) 8) Titanium Dioxide (sold under the trade designation MT 100T) 8.0 9) Iron (III) Oxide (sold under the trade designation Super-Fine) 0.111 10) Bronopol 0.02 11) Sodium Dehydroacetate 0.15 12) Sodium Citrate 4.0 13) Purified Water to 100 Components 1 and 2 were mixed together and heated at 75-80°C until the lecithin dissolved. Components 3 and 4 were mixed together and heated at 50°C to dissolve component 4. Components 5, 6 and 7, the mixture of components 1 and 2 and the mixture of components 3 and 4 were mixed together in a stainless steel beaker. Components 8 and 9 were added to this mixture and dispersed using a high shear mixer/homogeniser (Silverson) to produce the oil phase. Components 10, 11 and 12 were dissolved in water. This aqueous solution was added slowly to the oil phase with paddle stirring. When the addition was complete the mixture was homogenised to a suitable viscosity. Example 2 A sunscreen composition comprising the following constituents was prepared: % w/w 1) Isopropyl palmitate 0.251 2) Lecithin (sold under the trade name P Centrolex) 0.127 3) Sorbitan sesquioleate (sold under the trade name Arlacel 83) 3.0 4) Butylated hydroxytoluene 0.05 5) Cetyl Dimethicone 5.0 6) A mixture of siiicone copolyol and cyclomethicone (sold under the trade designation Siiicone Fluid 3225 C) 12.0 7) Cyclomethicone (sold under the trade designation Siiicone Fluid 345DC) 15.0 8) Titanium Dioxide (sold under the trade designation MT 500B) 8.0 9) Iron (III) Oxide (sold under the trade designation Super-Fine) 0.111 10) Bronopol 0.02 11) Sodium Dehydroacetate 0.15 12) Sodium Citrate 4.0 13) Purified Water to 100 Control Example 1 This was prepared as described for Example 1 but omitting component 9. Control Example 2 This was prepared as described for Example 2 but omitting component 9. RESULTS Diffey Scan (Mean of 3 readings) These results demonstrate the efficacy of Examples 1 and 2 as sunscreens. Chromometer Results MT 10OT MT 50OB L = measure of reflected light. The whiter the surface the higher the value. b = measure of blue/yellow light. The lower the number the more this light is reflected. When the control examples are applied to the skin the amount of whiteness is increased and the amount of blue light reflected is increased. When Examples 1 and 2 are applied the amount of reflected light is reduced along with the amount of blue light almost back to background levels demonstrating the advantage obtained by the incorporation of component 9 in Examples 1 and 2.

Claims: Claims 1. A sunscreen composition comprising from about 0.5% to about 30% by weight of a metal oxide, the metal oxide being titanium dioxide, zinc oxide or a mixture of both oxides and from about 0.001% to about 2% by weight of iron oxide particles having a mean primary particle size of less than about 200nm. 2. A sunscreen composition according to claim 1, in which the metal oxide is substantially in the form of particles having a mean primary particle size of less than about lOOnm. 3. A sunscreen composition comprising a water-in-oil emulsion which comprises: a) from about 0.5% to about 30% by weight of metal oxide particles having a mean primary size of less than about lOOnm, b) from about 0.001% to about 2% by weight of iron oxide particles having a mean primary particle size of less than about 200nm, c) from about 5% to about 70% by weight of an oil phase, d) from about 1% to about 15% by weight of an emulsifier, and e) at least about 20% by weight of an aqueous phase. 4. A sunscreen composition comprising an oil-in-water emulsion which comprises: a) from about 0.5% to about 30% by weight of metal oxide particles having a mean particle size of less than about lOOnm, b) from about 0.001% to about 2% by weight of iron oxide particles having a mean primary particle size of less than about 200nm, c) from about 5% to about 60% by weight of an oil phase, d) from about 1% to about 20% by weight of an emulsifier, and e) at least about 35% by weight of an aqueous phase. 5. A sunscreen composition according to any preceding claim, comprising from about 0.1% to about 20% by weight of metal oxide. 6. A sunscreen composition according to any preceding claim, comprising from about 1% to about 15% by weight of metal oxide. 7. A sunscreen composition according to any preceding claim, comprising from about 4% to about 12% by weight of metal oxide. 8. A sunscreen compsoiton according to any preceding claim, in which the metal oxide is titanium dioxide. 9. A sunscreen composition according to any preceding claim, comprising from about 0.01% to about 1% by weight of iron oxide particles. 10 A sunscreen composition according to any preceding claim, comprising from about 0.02% to about 0.5% by weight of iron oxide particles. 11. A sunscreen composition according to any preceding claim, comprising from about 0.05% to about 0.25% by weight of iron oxide particles. 12. A sunscreen composition according to any preceding claim, in which the iron oxide particles have a mean particle size from about O.Olnm to about lOOnm. 13. A sunscreen composition according to any preceding claim, in which the iron oxide particles have a mean particle size from about O.Olnm to about lOnm. 14. A sunscreen composition according to any preceding claim, in which the iron oxide particles have a mean particle size from about Inm to about 5nm. 15. A sunscreen composition according to any preceding claim, in which the iron oxide particles comprise iron (III) oxide. 16. A sunscreen composition according to any preceding claim, in which the iron oxide particles, or the metal oxide particles, or both, are substantially coated with a phospholipid. 17. A sunscreen composition according to claim 15, in which the phospholipid is lecithin. 18. A sunscreen composition according to any preceding claim comprising, from about 0.025% to about 30% by weight of phosphate anions. 19. Sunscreen compositions substantially as described herein, and with reference independently to each of the examples.

Inventors: FARDELL NICOLA ANNE, NUTHALL TREVOR G, STAMMERS ARIJA MARGARET, FARDELL, NICOLA, ANNE, NUTHALL, TREVOR, G., STAMMERS, ARIJA, MARGARET
Applicants: BOOTS CO PLC, THE BOOTS COMPANY PLC
Application year: 1992
Main classification: A61K7
IPC codes: A61K8, A61Q17