A PROCATALYST COMPONENT BASED ON A TRANSITION METAL COMPOUND ON A CARRIER OF MAGNESIUM CHLORIDE AND MANGANESE HALIDE

Abstract: Olefin polymerization catalysts the procatalyst component of which comprises a transition-metal compound on a magnesium chloride support material are known to all. Now the procatalyst component has been improved by incorporating a manganese (II) halide into it at a rate of at minimum approx. 0.1 % and at maximum approx. 50 % of the total molar amount of magnesium chloride and manganese (II) halide. The new polymerization catalyst has, among other things, the excellent special property that it yields a polyolefin with a broad molecular weight distribution.

Description: A procatalyst component based on a transition metal compound on a carrier of magnesium chloride and manganese halide. - The invention relates to an olefin polymerization catalyst the *- procatalyst component of which comprises a transition-metal compound on a support material of magnesium chloride. The in¬ vention also relates to a method for preparing a procatalyst component for an olefin polymerization catalyst of the said type, wherein a) a magnesium chloride and a lower alcohol are contacted and the mixture is melted, b) the molten mixture is atomized, and it is solidified by cooling to produce support material particles, and c) the support material particles are caused to react with a transition-metal compound. Furthermore, the invention relates to the use of an olefin polymerization catalyst of the said type for the preparation of polypropylene, and preferably a polypropylene with a broad mo¬ lecular weight distribution. α-olefins are often polymerized using a Ziegler-Natta catalyst system made up of a so-called procatalyst and a cocatalyst. Of these, the procatalyst component is based on a compound of a transition metal belonging to any of Groups IVA - VIII in the Periodic Table of the Elements, and the cocatalyst component is based on an organometallic compound of a metal belonging to any of Groups IA - IIIA in the Periodic Table of the Elements (the groups are defined according to Hubbard, i.e. IUPAC) . The cata¬ lyst system may also include a support material on which the transition-metal compound is deposited and an internal electron donor which enhances and modifies the catalytic properties and is deposited on the support material together with the transition-metal compound. In addition, a separate so-called external electron donor can also be used together with the procatalyst and the cocatalyst. The Ziegler-Natta catalysts used for polypropylene polymeriza¬ tion usually produce a polymer having a narrow molecular weight distribution. This material is very suitable for injection molding purposes. However, there are several uses in which a broad molecular weight distribution is required. Especially if a higher melt strength is desired, a wider range of polymer chain lengths would be an advantage. If it is assumed that polymerization takes place at specific so-called active sites in the catalyst, active sites of the same type will produce a polymer material of the same type, in which case the uniformity is seen as a narrow molecular weight distribution. Since a broader molecular weight distribution is required for a number of uses of polypropylene, efforts have been made to prepare catalysts with active sites of a variety of types. JP application publication 79037911 describes the preparation of a polyolefin having a wide molecular weight distribution by using an active and new procatalyst which is made up of a titanium and/or vanadium compound on a support material. The first component is obtained by treating aluminum oxide with sulfur dioxide, and the other component contains a magnesium halide, a manganese halide, and an organic compound of a metal such as aluminum or zinc, e.g. MgC^MnC^-AMOR β ) . By this known method it has been possible, for example, to improve the casting properties of the polymer, but the process for preparing the catalyst is too complicated and unconven¬ tional in order to be commercially usable. The object of the present invention is to provide a catalyst comprising a transition-metal compound on a magnesium chloride support material for producing polyolefins having a broad mo¬ lecular weight distribution. Another aim is a maximal catalyst activity and a suitable catalyst morphology, which will also be reflected in the morphology of the polymer product. The inven¬ tion also aims at an improved method for the production of an olefin polymerization catalyst of the said type. These objects have now been achieved with a new olefin polymer¬ ization catalyst which is mainly characterized in what is stated in the characterizing clause of Claim 1, and with a new method for preparing the olefin polymerization catalyst which is characterized in what is stated in the characterizing clause of Claim 10. It has thus been realized that an olefin polymerization cat¬ alyst more suitable for the above-mentioned use is obtained if manganese (II) halide is incorporated into its magnesium chlor¬ ide support material at a rate of at minimum approx. 0.1 %, and at maximum approx. 50 %, of the total molar amount of magnesium chloride and manganese (II) halide. It is preferable that the minimum concentration of manganese (II) halide is approx. 5 % of the total molar amount of magnesium chloride and manganese (II) halide. The maximum concentration of manganese (II) halide is preferably approx. 40 % of the total molar amount of mag¬ nesium chloride and manganese (II) halide. It is even more preferable that the maximum concentration of manganese (II) halide is less than 30 %, and preferably approx. 10 %, of the said the said total molar amount. The active part of the catalyst, i.e. the transition-metal compound, is preferably a titanium compound, such as a titanium alkoxide, a titanium alkoxyhalide or a titanium halide, or a vanadium compound, such as a vanadium oxyhalide or a vanadium halide. The most preferable transition-metal compound is titanium tetrachloride. The manganese (II) halide is selected so that with respect to its ion radii it fits as well as possible into the crystal lattice of magnesium chloride. It has been observed that the most advantageous manganese (II) halide is manganese chloride. The said advantageous concentrations have specifically been measured using manganese (II) chloride, but similar results are probably attainable also using other manganese (II) halides. A preferred composition, based on weight, of the procatalyst component for the polymerization catalyst according to the invention is, not including the organometallic cocatalyst used in the polymerization, as follows: magnesium 10-20 %, manganese 1-10 %, titanium 2-4 %, and chlorine 45-60 %, calculated from the total weight of the supported procatalyst component. According to one embodiment of the invention, on the magnesium chloride support material there is, in addition to the transition-metal compound, also an internal donor, which is preferably an aromatic ester of the type of di-isobutγl phthalate. Benzoic acid esters are also possible. The con¬ centration of this internal donor may be 10-25 % of the weight of the procatalyst component in the catalyst. The catalyst according to the invention preferably also con¬ tains an organometallic cocatalyst, which is preferably a tri- alkyl aluminum, preferably triethyl aluminum. In order to im¬ prove, for example, stereoselectivity, a so-called external donor may also be added to the catalyst; the external donor may be silane, cineole or ether, preferably cyclohexyl-methyl- ethoxysilane, cineole, or diphenyl-dimethoxysilane. The solid part of the catalyst according to the invention is in the form of substantially spherical particles having a diameter within a range of approx. 100-400 urn. As was already mentioned, the invention also relates to a meth¬ od for the preparation of a procatalyst component for an olefin polymerization catalyst. In the method, magnesium chloride and a lower alcohol are contacted and melted, the molten mixture is atomized and solidified by cooling to produce support material particles, and the support material particles are reacted with a transition-metal compound to produce an active procatalyst. In the invention it has been realized that a broader molecular weight distribution can be obtained by adding to the magnesium chloride and the lower alcohol a manganese (II) halide at a rate of at minimum approx. 0.1 % and at maximum approx. 50 % of the total molar amount of magnesium chloride and manganese (II) halide. This addition takes place before the solidification and thus yields a homogenous procatalyst doped with manganese. In the first step, i.e. step a), the magnesium chloride and the lower alcohol are contacted and the mixture is melted, and in the second step, i.e. in step b) , the melt is atomized and it is solidified by cooling it to produce support material par¬ ticles. These steps a) and b) are preferably carried out by suspending a finely-divided magnesium chloride and a finely- divided manganese (II) halide, preferably manganese (II) chlor¬ ide, into an inert, heat-resistant medium. Then a lower alcohol is added to the suspension and the suspension is heated until the mixture made up of the said salts and alcohol melts, form¬ ing melt drops in the medium. After the said steps, the medium with its melt drops is contacted with a cold liquid, which dissolves the medium and solidifies the melt drops into finished support material particles. As is evident from the description of the catalyst, compounds of titanium and vanadium are preferred transition-metal com¬ pounds, and the most preferred one is titanium tetrachloride. Manganese (II) chloride is a preferred manganese (II) halide. Manganese (II) halide (preferably chloride) is preferably added to step a) at a rate of at minimum 5 % of the total molar amount of magnesium chloride and manganese (II) halide (prefer¬ ably chloride). Manganese (II) halide (preferably chloride) is added to step a) at a rate of at maximum approx. 40 % of the total molar amount of magnesium chloride and manganese (II) halide (preferably chloride). It is most preferable to add manganese (II) chloride to step a) at a rate of at maximum approx. 30 % and preferably approx. 10 % of the total molar amount of magnesium chloride and manganese (II) chloride. The lower alcohol used in step a) is preferably methanol and/or ethanol, and most preferably ethanol. The solid support material obtained from step b) in the form or particles is caused to react with a transition-metal compound in step c) . As was already mentioned, the most preferred transition-metal compound is titanium tetrachloride. According to one preferred embodiment, step c) is carried out by causing the support material particles to react not only with the transition-metal compound but also with an internal electron donor, in which case the electron donor used is preferably an aromatic ester such as di-isobutyl phthalate. According to one embodiment, the catalyst according to the invention is used for producing a polypropylene having a broad molecular weight distribution. In this case, the said procata¬ lyst is combined with an organometallic cocatalyst and prefera¬ bly also an external donor, which may be, for example, silane, cineole, ether or other such external donor commonly known in the art. Embodiment examples 3, 4 and 5, as well as comparison examples 1 and 6, are presented below in order to elucidate the inven¬ tion. EXAMPLES Examples 1 and 6 are comparison examples, in which the molar concentrations of manganese are respectively 0 and 100 %. In the corresponding embodiment examples 2, 3, 4, and 5, the man¬ ganese concentrations in the support material were respectively 3, 10, 30, and 60 mol-%. The accompanying Figures 1-14 depict the following: Figure 1. The morphology of the MgCl 2 *EtOH support mate¬ rial doped with 3 % MnCl 2 . Figure 2. The morphology of the MgCl 2 «EtOH support material doped with 10 % MnCl 2 . Figure 3. The morphology of the MnCl 2 »EtOH support mate¬ rial. Figure 4. The mean particle diameter of the support ma¬ terial as a function of the Mn concentration (mol-%) in MgCl 2 . Figure 5. The correlation between the molar percentage of the manganese added and the molar percentage detected in the product and in the catalyst. Figure 6. The proportion of donor bound by the metals (Mg+Mn) in the Mn-doped catalyst. Figure 7. The X-ray diffraction pattern of a Ziegler- Natta catalyst doped with 10 % Mn in a MgCl 2 support material. Figure 8. The activities of Mn-doped Ziegler-Natta cata¬ lysts. Figure 9. The isotacticities (A) and isotactic indices (B) of polymers produced using Mn-doped catalysts. Figure 10. The bulk density (B) and the percentage (A) of coarse material (d>l mm) of PP material, as a function of the molar percentage of manganese in the procatalyst. Figure 11. The particle size distribution of a polymer sample produced using a catalyst doped with 30 % manganese. Figure 12. Molecular weights of the polymer samples as a function of the molar percentage of manganese in the procata¬ lyst support material. Figure 13. Polydispersity of the polymer samples as a function of the molar percentage of manganese in the procat¬ alyst support material. Figure 14. Comparison between the molecular weight dis¬ tribution (MWD) of a PP sample produced using a conventional catalyst and the molecular weight distribution of a PP sample produced using a Mn-doped catalyst. Preparation of support material 1-30 g of magnesium chloride and manganese (II) chloride were suspended at room temperature into 600 ml of silicone oil in a reactor. Agitation was continued for half an hour in order to achieve equilibrium conditions. Thereafter 56 ml of dry ethanol was added, drop by drop, and the mixture was gradually heated to 40 °C. The solution was again allowed to reach an equi¬ librium, whereafter the temperature was raised to 123-132 °C. Thereafter, ethanol was added until the salt mixture became liquid. Then vigorous agitation was used in order to distribute the liquid melt drops evenly into the silicone oil. When a clear salt melt had been achieved, the hot silicone oil mixture was siphoned through a teflon tube into a reactor containing 1 liter of cold heptane (-30 °C) . The melt drops of the metal salt mixture solidified in this cold solution. In order to remove the silicone oil, the solids were washed three times with 600 ml of heptane. Ultimately, the support material was vacuum dried. In the preparation of the support material it became evident that manganese (II) chloride had a lower solubility in ethanol than had magnesium chloride. Ethanol must be added to certain mixtures in order to bring the salt into a molten state. Approx. twice as much ethanol had to be added in order to bring mixtures containing more than 10 mol-% manganese into a molten state in a silicone bath. The chemicals added are listed in Table 1, and Table 2 shows the magnesium and manganese concen¬ trations in the support material produced. The molar percent¬ ages in Table 2 were calculated from the total molar amount of the metals, and the corresponding weight percentages from the total weight of the support material. Table 1. Chemicals added in the production of support materials Ethanol added (ml) 56 56 101 56 95 92 Table 2. Calculated chemical composition of the support materi- al as com ared with the concentrations obtained in the roduct The morphology of the support material obtained was such that a higher manganese amount added to the salt mixture hampered the bringing of the mix into a liquid or molten state. The molten material was in this case also more viscous. Since the mixing conditions in the silicone bath in the different examples were identical, a higher melt viscosity also yielded larger support material particles. This increase in the particle diameter continued up to a manganese concentration of 30 %. Thereafter the liquid melt drops were no longer capable of forming spheri¬ cal particles. This change in particle morphology can be seen in Figures 1-3. The first figure shows the morphology of a material doped with 3 per cent manganese. The morphology of this material resembles that of a conventional magnesium chlor¬ ide support material, and the mean particle diameter is approx. 50 μm. The next of these figures shows enlarged particles of a material doped with 10 % manganese, and the last one shows a crystalline material prepared from pure manganese (II) chlor¬ ide. Table 3 lists the mean particle sizes, and they are also shown graphically in Figure 4. Table 3 also shows the general morphological character and color of the products. Table 3. Mean particle size diameter of the support material as a function of the mol-% of Mn in MnCl , as well as the color and morphology of the material Example Mol-ξ Catalyst particle Color Morphol¬ ogy 1 (comp. ) S 2 (emb.) S 3 A 4 " S 5 " G 6 (comp. ) C Color: W = white SG = slightly green LT = light turquoise T = turquoise GR = green Morphology: S = spherical A = agglomerate G = granular C = crystalline Production of procatalyst 0.1 mol of the mixed salt support material prepared in the manner described above was suspended in inert conditions into 150 ml of heptane, and the. suspension was agitated for half an hour. The suspension was cooled to -15 °C. Then 300 ml of cold titanium tetrachloride was added and the temperature was raised slowly to +20 °C. 5.3 ml of an internal donor (di-isobutyl phthalate, DIBP) was added to the reaction mixture. The tem¬ perature was raised, according to the gradient, to the boiling point of the solution. After the boiling point of the reaction solution had been reached, the normal catalyst synthesis path was followed. The catalyst synthesis was carried out without difficulty. The only difference as compared with conventional catalyst syn¬ thesis was in the color of the reaction solution. Thereafter, the chemical composition of the procatalyst was measured. The measurement results are presented in Table 4. Table 4. Chemical com ositions of ma nesium-do ed catal sts The results showed that the amount of manganese fed in along with the support material correlated quite precisely with the amount of manganese detected in the catalyst. This can be seen clearly in Figure 5. In it the molar percentage of manganese is shown as a function of the concentration of manganese added. The manganese concentrations in the support material and in the catalyst correlate almost precisely with each other. This re¬ sult shows that manganese chloride can be added to a mixture of magnesium chloride and ethanol by merely melting the two salts together. Characterization of the procatalyst All of the components of the procatalyst produced were meas¬ ured. It was also interesting to see whether manganese affected the crystal structure of the support material. Therefore X-ray diffraction patterns of all the procatalysts were taken. In addition, the ratio of the complexed internal donor to the total metal amount in the procatalyst was measured. In measuring the titanium concentration it was observed that there was no substantial difference in the ability of the sup¬ port material to bind titanium into the crystal structure when the manganese concentration of the magnesium chloride salt was increased. In the shift from undoped material to the first doped procatalyst (3 mol-%) there occurred a slight decrease from 4.4 weight-% to approx. 3 weight-%, whereafter the tita¬ nium concentration remained unchanged as manganese was added to the support material (cf. Table ) . The donor concentration was also observed by determining the di-isobutyl phthalate concentration in the procatalyst. This was done because it was not known whether manganese was capable of binding internal donor to the same degree as magnesium was. In particular, it was desired to see whether a mixture made up of two salts could retain the normal donor to support material ratio during the synthesis. The ratios are shown in Tables 5 and 6. The final proportion is also seen in Figure 6. According to the results, the ability of the support material to bind the donor decreased sharply within the middle range of the salt mixtμre. Thus, a catalyst doped with 10 % manganese was capable of binding only 50 % of the original donor amount. A 60 % man- ganese (II) chloride material, on the other hand, was capable of binding donor to the same degree as was a pure magnesium chloride material. Table 5. A comparison of the manganese amount added, the man¬ ganese concentration in the support material, and the manganese concentration in the catal st Example 1 2 3 4 5 6 DIBP = di-isobutyl phthalate The dimensions of the doped magnesium chloride crystals were determined by taking X-ray diffraction patterns of all ' the cat¬ alyst samples in order to determine the effect of manganese (II) chloride. It proved to be possible to use manganese up to 30 % without the X-ray diffraction pattern of magnesium chlor- ide changing substantially. With these concentrations a normal amorphous magnesium chloride pattern was obtained, in which there was at 15 degrees a small peak indicating the height of the crystal and at 50 degrees a clear peak indicating the width of the crystal (cf. Figure 7) . At higher manganese concentra¬ tions, the X-ray pattern of manganese (II) chloride was prevalent and a more crystalline structure was obtained. It was possible to calculate the dimensions of magnesium chloride crystals up to a 30 % concentration of manganese. The results are shown in Table 7, and Figure 7 shows the X-ray diffraction pattern of a catalyst sample doped with 10 % manganese. Table 7. Crystal dimensions of Mn-doped catalysts. The heights were measured from a peak at 15° and the widths from a peak at 50°. Example 1 2 3 4 5 6 Test polymerization Test polymerizations were carried out on all of the procata¬ lysts. A two-liter bench reactor was used in the test polymer¬ ization. 20-30 mg of procatalyst was used for the test polymer¬ ization. This amount was mixed with 620 μl of triethyl aluminum and 200 μl of a 25 % solution of the external donor cyclohexyl- methyl-dimethoxysilane (CHMDMS) in 30 ml of heptane. The poly¬ merizations were carried out at +70 °C and at a propylene mono¬ mer pressure of 10 bar. The partial pressure of hydrogen during the polymerization was 0.2 bar. The polymerization was con¬ tinued for 3 hours. The activity was measured on the basis of the polymerization yield. The soluble part of the polymer was measured by evaporating a measured portion out from the poly¬ merization solution. As has been stated, the activity was determined by test poly¬ merizing all of the catalysts in the same conditions. Table 8 shows the polymerization results. Activity is here expressed both in kg PP/g cat. and in kg PP/g Ti. The results are also shown graphically in Figure 8. Table 8. Activit of Mn-do ed catal sts Mn-doping seemed to have a crucial effect on the activity of the catalysts. Doping with 3 % manganese yielded almost the same result as an undoped procatalyst, if only the activity unit kg PP/g cat. is considered, but caused an increase up to 25 % in the activity when expressed in kg PP/g Ti. The activity increase was greatest when a material doped with 10 % manganese was used. In this case activities up to 20 kg PP/g cat. were obtained. Expressed in kg PP/g Ti, the activity increase was in the order of 100 %. With higher doping concentrations there was an almost linear activity decrease with increasing manganese concentrations. When pure manganese (II) chloride was used instead of magnesium chloride, the activity was only 10 % of the original activity. Characterization of the polymer samples Bulk densities and particle size distributions were determined on the polymer samples obtained. Isotacticity was determined by heptane elution, and the isotactic index was determined from the results obtained from evaporation residue measurements. The melt index was determined at 230 °C by using a 2.16 kg weight. To observe the effect of the salt mixture on polydispersity, molecular weight distributions were determined on all of the polymer samples. First, the isotacticity and the isotactic indices of the poly¬ mer samples were measured. The results are presented in Table 9 and are shown graphically in Figure 9. Table 9. Isotactic indicators of polymer samples produced using Mn-doped procatalysts Example Isotactic index (%) 1 (comp.) 98.8 2 (emb. ) 96.2 3 " 97.7 4 " 98.2 5 " 97.3 6 (comp.) 71.2 The results indicate that isotacticity remained stable at a high level up to high Mn-doping percentages. Only at a con¬ centration which was above 60 mol-% Mn was there a drastic de¬ crease in isotacticity. When pure manganese (II) chloride was used as the support material, the isotactic index dropped to 70 %. At lower doping concentrations (below 60 mol-% manganese) the isotactic index varied only slightly, being within the range 97-98 %. Next, the particle size distributions of the polymers were determined. A catalyst particle without mechanical strength usually collapses during polymerization, and the small products of the collapse also produce fines in the polymer produced. Therefore the particle size distribution was determined on all of the polymer samples in order to determine the mechanical strength of the catalyst particles. The results are shown in Table 10. Table 10. Particle size distributions of the polymers produced usin Mn-doped catalysts The polypropylene material produced using Mn-doped catalysts had a very low fines content when the doping percentage was below 30 %. This is clearly visible also in Figure 10. Compared with an undoped catalyst, the catalyst containing manganese 3 % contained hardly any particles with diameters smaller than 1 mm. A catalyst having a doping percentage of 30 % yields even better results. The particle size distribution measurements correlate well with the observations made regarding the morphology of the support material. Good morphology was obtainable with doping values up to 30 %, whereafter the polymer particles showed a collapsing behavior similar to that of procatalyst particles, whereby a large proportion of fines was produced. The best results with respect to the particle size distribution were achieved with a magnesium doping percentage of 30. The particle size distribu- tion of this polymer sample is shown in Figure 11. The bulk densities of the polymer materials are listed in Table 11. The values seem to decrease as the Mn-doping percentages increase. This seems to be due, first, to the fact that an increasing particle size automatically causes a decrease in the bulk density and, second, to the fact that a strongly doped catalyst produces irregular particles which reduce the bulk density. The bulk densities of the polymer samples are shown as a function of the Mn-doping concentration also in Figure 10. Table 11. Bulk densities of polymer samples produced using Mn- doped procatalysts Bulk density g/ml 0.44 0.44 0.37 0.37 0.43 0.29 The melt indices of the polymer samples are shown in Table 12. They seem to vary very little within a range of 0-60 % Mn. Thus it can be stated that the melt index measurements yielded rather satisfactory results, although at 10 % the melt index drops somewhat. Table 12. Melt indices of polymer samples produced using Mn- doped procatalysts Example 1 2 3 4 The specific target of interest in the present work is the mo¬ lecular weight distribution of the polymer produced, for the idea is to produce in the catalyst differentiated active sites and thereby to form in the polymerization polymer chains of a variety of lengths. The analytical results obtained are listed in Table 13, and they are shown graphically in Figure 12. Table 13. Molecular weight distributions of polymer samples produced using Mn-doped procatalysts Example 1 As can be seen in Figure 12, the entire molecular weight, but especially the viscosity average molecular weight ( y ) and the weight average molecular weight (M^,) , increase sharply when the molar percentage of manganese in the procatalyst increases from 0 to 10. At higher doping concentrations, however, there occurs a decrease of the molecular weight. The low molecular weights obtained with pure manganese (II) chloride may explain why the polymer products have a low isotacticity and a high melt index. The number average molecular weight (M n ) drops sharply when the doping concentration increases from zero to three % Mn, but remains thereafter almost unchanged up to 60 % Mn. Polydispersity, i.e. the ratio of weight average molecular weight to number average molecular weight, was also calculated from the molecular weight measurement results. Figure 13 shows the polydispersity values as a function of the manganese con¬ centration in the procatalyst. Polydispersity increased from the conventional value 3 up to 7 when the manganese concentra¬ tion in the procatalyst increased from zero to 10 mol-% man¬ ganese (calculated from Mn + Mg) . Thereafter, polydispersity dropped to a constant value of 5. Figure 14 shows a comparison between a molecular weight distribution obtained with a polymer produced using an undoped procatalyst and the molecular weight distribution of a polymer produced using a procatalyst doped with 10 % manganese. The effect of a magnesium chloride support material doped with manganese can be seen as follows: 1. A very good polymer product morphology is obtained when the concentration of manganese (II) chloride is below 30 %. Specif¬ ically with this manganese concentration the very best par¬ ticular size distribution is obtained, in which case the poly¬ mer contains hardly any fines. 2. With the use of a doped procatalyst, large catalyst par¬ ticles with a high mechanical strength were obtained, which for its part affected the above-mentioned good particle size dis¬ tribution of the polymer. 3. The best activity was obtained with a manganese doping concentration of 10 mol-%, in which case the activity was up to 25 % higher than the activity obtained using an undoped cata¬ lyst. A good activity was obtained without a decrease in iso¬ tacticity. 4. Doping also affected the molecular weight distribution by broadening it. Since obtaining a polymer with a broad molecular weight distribution had been set as a specific object of the invention, the optimal concentration of the doping metal was determined in this respect. The best results were obtained using a procatalyst doped with approx. 10 mol-% manganese (cal¬ culated from the total molar amount of manganese and mag¬ nesium) . In this case, polydispersity increased to 7 from the conventional value 3.

Claims: Claims 1. An olefin polymerization catalyst the procatalyst of which comprises a transition-metal compound on a magnesium chloride support material, characterized in that the magnesium chloride support material contains a manganese (II) halide at a rate of at minimum approx. 0.1 % and at maximum approx. 50 % of the total molar amount of magnesium chloride and manganese (II) halide. 2. A polymerization catalyst according to Claim 1, charac¬ terized in that the transition-metal compound is a titanium compound, and preferably titanium tetrachloride. 3. A polymerization catalyst according to Claim 1 or 2, characterized in that the manganese (II) halide is manganese (II) chloride. 4. A polymerization catalyst according to Claim 1, 2, or 3, characterized in that the minimum concentration of manganese (II) halide is approx. 5 % of the total molar amount of mag¬ nesium chloride and manganese (II) halide. 5. A polymerization catalyst according to any of the above claims, characterized in that the maximum concentration of manganese (II) halide is approx. 40 % of the total molar amount of magnesium chloride and manganese (II) halide. 6. A polymerization catalyst according to any of the above claims, characterized in that its activity is maximized and the molecular weight distribution of the polymer produced by it is broadened by the use of manganese (II) halide at approx. 8-15 % and preferably at approx. 10 % of the total molar amount of magnesium chloride and manganese (II) halide. 7. A polymerization catalyst according to any of Claims 1- 5, characterized in that its effect on the production of large polymer particles is enhanced by the use of a manganese (II) halide concentration which is approx. 25-35 % and preferably approx. 30 % of the total molar amount of magnesium chloride and manganese (II) halide. 8. A polymerization catalyst according to any of Claims 2- 7, characterized in that its procatalyst component contains approx. 10-20 % magnesium, 1-10 % manganese, 2-4 % titanium, and at minimum 45-60 % chlorine, calculated from the total weight of the procatalyst. 9. A polymerization catalyst according to any of the above claims, characterized in that on the magnesium chloride support material there is, in addition to the transition-metal com¬ pound, an internal donor, preferably an aromatic ester such as di-isobutyl phthalate. 10. A polymerization catalyst according to Claim 9, charac¬ terized in that the concentration of internal donor is approx. 10-25 % of the total weight of the catalyst. 11. A polymerization catalyst according to any of the above claims, characterized in that it comprises, in addition to the said procatalyst, also an organometallic cocatalyst, which is preferably a trialkyl aluminum, most preferably triethyl aluminum. 12. A polymerization catalyst according to any of the above claims, characterized in that, in addition to the procatalyst and the cocatalyst, it also contains an external donor, which is preferably silane, cineole, ether, and most preferably cyclohexyl-methyl-dimethoxysilane (CHMDMS), cineole, or di- phenyl-dimethoxysilane (DPDMS). 13. A method for the production of a procatalyst component for an olefin polymerization catalyst, wherein a) magnesium chloride and a lower alcohol are contacted, and the mixture is melted, b) the molten mixture is atomized, and it is solidified by cooling to produce support material particles, and c) the support material particles are caused to react with a transition-metal component, characterized in that manganese (II) halide is added to step a) at a rate of at minimum approx. 0.1 % and at maximum approx. 50 % of the total molar amount of magnesium chloride and man¬ ganese (II) halide. 14. A method according to Claim 13, characterized in that steps a) and b) are carried out: by suspending a finely-divided magnesium chloride and a finely-divided manganese (II) halide into an inert, heat-resistant medium; by adding to the suspen¬ sion a lower alcohol, and by heating until the mixture of the salts and the alcohol becomes liquefied or melts to form melt drops in the medium; and by contacting the medium and its melt drops with a cold material which preferably dissolves the medium and solidifies the melt drops to form finished support material particles. 15. A method according to Claim 13 or 14, characterized in that the transition-metal compound is a titanium compound, preferably titanium tetrachloride. 16. A method according to any of Claims 13-15, characterized in that the manganese (II) halide is manganese (II) chloride. 17. A method according to any of Claims 13-16, characterized in that the manganese (II) halide is added to step a) at a rate of at minimum approx. 5 % of the total molar amount of mag¬ nesium chloride and manganese (II) halide. 18. A method according to any of Claims 13-17, characterized in that the manganese (II) halide is added to step a) at a rate of at maximum approx. 40 % of the total molar amount of mag¬ nesium chloride and manganese (II) halide. 19. A method according to any of Claims 13-18, characterized in that the lower alcohol is methanol and/or ethanol, prefer¬ ably ethanol. 20. A method according to any of Claims 13-19, characterized in that step c) is carried out by causing the support material particles to react also with an internal electron donor, pref¬ erably an aromatic ester, such as di-isobutyl phthalate. 21. The use of a polymerization catalyst procatalyst com¬ ponent according to any of Claims 1-12, or prepared by a method according to any of Claims 13-20, for the production of poly¬ propylene, and preferably a polypropylene having a broad molec¬ ular weight distribution. 22. The use in accordance with Claim 21, characterized in that the production of polypropylene is carried out using a catalyst which, in addition to the procatalyst component, com¬ prises an organoaluminum compound and an external electron donor. AMENDED CLAIMS [received by the International Bureau on 24 February 1993(24.02.93); original claims 1 and 9 amended; other claims unchanged (2 pages)] 1. An olefin polymerization catalyst, the procatalyst com¬ ponent of which has been prepared by (a) contacting magnesium chloride and a lower alcohol and melting the mixture, (b) atomizing the molten mixture and solidifying it by cool¬ ing to produce support materialparticles, (c) reacting the support materialparticles with a transiti- on-metal compound, characterized by adding to stage (a) manganese (II) halide at a rate of at minimum approx. 0.1 % and at maximum approx. 50 % of the total molar amount of magnesium chloride and manganese (II) halide. 2. A polymerization catalyst according to Claim 1, charac¬ terized in that the transition-metal compound is a titanium compound, and preferably titanium tetrachloride. 3. A polymerization catalyst according to Claim 1 or 2, characterized in that the manganese (II) halide is manganese (II) chloride. 4. A polymerization catalyst according to Claim 1, 2, or 3, characterized in that the minimum concentration of man¬ ganese (II) halide is approx. 5 % of the total molar amount of magnesium chloride and manganese (II) halide. 5. A polymerization catalyst according to any of the above Claims, characterized in that the maximum concentration of manganese (II) halide is approx. 40 % of the total molar amount of magnesium chloride and manganese (II) halide. 6. A polymerization catalyst according to any of the above Claims, characterized in that its activity is maximized and the molecular weight distribution of the polymer produced by it is broadened by the use of manganese (II) halide at ap¬ prox. 8-15 % and preferably at approx. 10 % of the total 93/07181 molar amount of magnesium chloride and manganese (II) hali¬ de. 7. A polymerization catalyst according Claims 1-5, charac¬ terized in that its effect on the production of large poly¬ mer particles is enhanced by the use of a manganese (II) halide concentration which is approx. 25-35 % and preferably approx. 30 % of the total molar amount of magnesium chloride and manganese (II) halide. 8. A polymerization catalyst according to any of claims 2- 7, characterized in that its procatalyst component contains approx. 10-20 % magnesium, 1-10 % manganese, 2-4 % titanium, and at minimum 45-60 % chlorine, calculated from the total weight of the procatalyst. 9. A polymerization catalyst according to any of the above claims, characterized in that on the magnesium chloride sup¬ port material, in addition to the transition-metal compound, have been reacted with an internal donor, preferably an aro¬ matic ester such as di-isobutyl phthalate. 10. A polymerization catalyst according to Claim 9, charac¬ terized in that the concentration of internal donor is ap- prox. 10-25 % of the total weight of the catalyst. 11. A polymerization catalyst according to any of the above claims, characterized in that it comprises, in addition to the said procatalyst, also an organometallic cocatalyst, which is preferably a trialkyl aluminium, most preferably triethyl aluminium. 12. A polymerization catalyst according to any of the above claims, characterized in that, in addition to the procata- lyst and the cocatalyst, it also contains an external donor, which is preferably silane, cineole, ether, and most prefe¬ rably cyclohexyl-methyl-dimethoxysilane (CHMDMS) , cineole, or diphenyl-dimethoxysilane (DPDMS) .

Inventors: GAROFF THOMAS, IISKOLA EERO, LEINONEN TIMO, GAROFF, THOMAS, IISKOLA, EERO, LEINONEN, TIMO
Applicants: NESTE OY
Application year: 1992
Main classification: C08F4
IPC codes: C08F4, C08F10, C08F110