Ionically crosslinked carboxyl-containing polysaccharides for adhesion prevention

Abstract: A method of reducing post-operative adhesion formation by topically applying an ionically crosslinked carboxyl-containing polysaccharide or a pharmacologically acceptable salt thereof, e.g. sodium hyaluronate crosslinked with ferric chloride, to a site of surgical trauma.

Description: BACKGROUND OF THE INVENTION This invention relates to a treatment for preventing post-operative adhesion formation. Adhesions are unwanted tissue growth occurring between layers of adjacent bodily tissue or between tissue and internal organs when the healing process begins following a surgical procedure. More specifically, the invention relates to such a method which employs the use of ionically crosslinked carboxyl-containing polysaccharides to control the incidence and extent of adhesion formation at a site of surgical trauma. The medical and scientific community has extensively studied the therapeutic uses of carboxyl-containing polysaccharides and their water soluble salts for well over a decade. For example, U.S. Patent 4,141,973 (the Balazs patent) discloses the use of a non-inflammatory hyaluronic acid (HA) fraction for numerous therapeutic applications. These applications include, among other things, the prevention of fibrous tissue formation, e.g., the prevention of adhesions; the protection of skin wounds; and the most successful application to date, the use of HA as a viscoelastic ophthalmic during ophthalmic surgery. The prevention or reduction of adhesion formation following surgery requires a therapeutic agent which has an acceptable half life in bodily tissue. HA, in the free acid form or as its salt (sodium, potassium, etc.), is highly soluble in moist environments. This high solubility as well as susceptability to naturally occurring enzymes leads to a very short half life of approximately 1 to 3 days in bodily tissue. While this may be acceptable for prevention of adhesions in some indications, for others a longer half life is desirable. Accordingly, attempts have been made to increase the half life of HA and other carboxyl-containing polysaccharides without sacrificing the therapeutic efficiency of such compounds, particularly for adhesion prevention. For example, U.S. Patent 4,772,419 discloses crosslinking HA with a polyfunctional crosslinking agent which creates ether, ester, or amide linkages. The covalently crosslinked HA forms a gel, and this gel is disclosed as being efficacious for the prevention of adhesions and accretion of tissues. PCT Application WO 89/02445 discloses a water-insoluble derivative of HA prepared by reacting HA with any of a number of different activating agents to prepare a covalently crosslinked HA fraction. PCT Application WO 86/00912 discloses crosslinking HA or other carboxyl-containing polysaccharides with a polyfunctional epoxide to prepare a degradable gel for the prevention of adhesions or accretions of bodily tissue. Although the attempts to enhance the half life of HA as well as other carboxyl-containing polysaccharides by covalently crosslinking the chosen polysaccharide have met with some success, the biocompatibility and toxicity of the crosslinking agents used for the covalent bonding is unknown. Additionally, the degree of reduction in the incidence of adhesion prevention, although slightly better than HA in its uncrosslinked form, is still inadequate for numerous applications. Therefore, in view of the deficiencies of the prior art, it would be desirable to prepare a derivatized carboxyl-containing polysaccharide which is biocompatible with bodily tissue and exhibits a high degree of adhesion prevention or reduction relative to that of either the native or the covalently crosslinked carboxyl-containing polysaccharides described in the literature. CS264719 (Galatik et al), translated by Allen Translation Service, discloses high molecular weight, high viscosity alkali metal hyaluronates cross-linked with Mg 2+ , Al 3+ , Ca 2+ , Cr 3+ , Zn 2+ , or Zr 4+ in dimer, trimer or higher order complexes. The complexes can also be cross-linked with Fe 3+ (not preferred) and can be used to prevent post-operative adhesion. SUMMARY OF THE INVENTION The invention is a treatment reducing the incidence of post-operative adhesion formation. The invention comprises the step of topically applying as an adhesion preventative an effective amount of an ionically crosslinked carboxyl-containing polysaccharide or a pharmacologically acceptable salt thereof to a site of surgical trauma. The adhesion preventative in preferred embodiments of this invention has a half life greater than that of the corresponding uncrosslinked polysaccharide, and comparable to that of a corresponding covalently crosslinked polysaccharide. When the adhesion preventative is topically applied to a site of surgical trauma, it exhibits an increased tendency to reduce the incidence of post-operative adhesion formation relative to that of either an uncrosslinked carboxyl-containing polysaccharide or a covalently crosslinked carboxyl-containing polysaccharide. Additionally, the crosslinking agents used for preparing the adhesion preventative are biocompatible and non-toxic to bodily tissue. The treatment of this invention can be used in those applications requiring a reduction in the incidence of post-operative adhesion formation, or for any other application which could directly or indirectly benefit from such a therapeutic use, e.g. ophthalmic and orthopedic applications. The ionically crosslinked carboxyl-containing polysaccharide may also be useful as a drug delivery system, e.g. for delivery of wound healing agents, antibiotics, etc. DETAILED DESCRIPTION OF THE INVENTION Examples of carboxyl-containing polysaccharides falling outside the scope of the invention include, carboxymethyl cellulose, carboxymethyl chitin, carboxymethyl chitosan, carboxymethyl starch, alginic acid, pectin, carboxymethyl dextran, and glucosaminoglycans such as heparin, heparin sulfate and chondroitin sulfate. The carboxyl-containing polysaccharide of the invention is HA. The adhesion preventative can employ the carboxyl-containing polysaccharide in the free acid form, or alternatively, a pharmacologically acceptable salt of the polysaccharide can be used. Preferably, the adhesion preventative employs the pharmacologically acceptable salt of the carboxyl-containing polysaccharide to prevent the formation of adhesions. This adhesion preventative is sodium hyaluronate. Carboxyl-containing polysaccharides falling outside the scope of the invention which can be used to prepare adhesion preventatives are known compounds that are described, for example, in U.S. Patent Nos. 4,517,295 and U.S. Patent 4,141,973; and Handbook of Water Soluble Gums and Resins , Chapter 4, by Stelzer & Klug, published by McGraw-Hill, 1980. Processes for preparing HA, are illustrated in the Balazs patent, which details a procedure for extracting HA from rooster combs, and in U.S. Patent 4,517,295 which describes a fermentation process for making HA. The HA used to make the adhesion preventative should be highly purified (medical grade quality) for surgical applications. The crosslinking agents which can be used to ionically crosslink the carboxyl-containing polysaccharide are compounds which possess a polyvalent cation, viz. the trivalent cation ferric chloride, because of its low toxicity and biocompatibility with bodily tissue. The crosslinking reaction typically occurs almost instantaneously when an aqueous polycation solution is contacted with an aqueous solution of at least 0.5 weight percent of the carboxyl-containing polysaccharide. The concentration of polycationic species present in the reaction mixture should be a concentration sufficient to crosslink at least 10 percent of the carboxyl groups of the polysaccharide. After the reaction, it is usually desirable to adjust pH to about neutral. In some instances, it is necessary to preadjust the polysaccharide solution pH to an acidic pH to prevent precipitation of the HA upon addition of the polycation solution. This often becomes necessary when strong ionic bonds are created, when the crosslinking agent used is ferric chloride. The crosslinking reaction utilizes a polysaccharide possessing anionic groups at each of the carboxyl sites. These anionic groups are ionically bound to the polyvalent cations. The ionically crosslinked polysaccharide, which represents the adhesion preventative used in the method of the invention, is characterized by its tendency to gradually disassociate into its separate ionic species when placed in an ionic medium, e.g. saline. The viscosity of the adhesion preventative can be controlled by changing the concentration of polysaccharide in solution or by varying the concentration of polycation to control the crosslink density. The adhesion preventative may exist in the form of a gel at relatively high viscosities, or alternately, it may exist as a low viscosity fluid. Regardless of the viscosity which the adhesion preventative exhibits, it may exhibit an increased half life in comparison to an uncrosslinked polysaccharide because of its crosslinked structure. As used herein, topical application refers to the administration of the adhesion preventative nonsystemically to the surface of the bodily tissue to be treated. The term "site of surgical trauma" is meant to include the site of tissue that has been injured in any way, and includes, for example, tissue sites that have undergone incision, drying, suturing, excision, abrasion, contusion, laceration, anastomosis, manipulation, prosthetic surgery, curettage, orthopedic surgery, neurosurgery, cardiovascular surgery, or plastic or reconstructive surgery. "Site of surgical trauma" also includes tissue that is adjacent to the injured tissue. The treatment of this invention can be used to prevent post-operative adhesions in any animal that is susceptible to unwanted adhesion formation following surgery. Advantageously, the method is used to prevent adhesions from developing in mammals, preferably human beings. The treatment of the invention is useful in any surgical procedure in which it is desired to inhibit the formation of post-surgical adhesions. It is thus broadly useful in all types of surgery in which adhesion formation can be a complication. For instance, the invention is useful in abdominal surgery, in gynecological surgery, in thoracic surgery, in orthopedic surgery affecting tendons, ligaments, etc., in neurological surgery affecting the dura mater, in liver surgery, and the like. The adhesion preventative may be administered to the site of surgical trauma by any convenient mode such as, for example, by lavage, by coating directly on the site in a gel, cream, film, or foam, or by any other convenient mode. Preferably, the adhesion preventative is applied directly to the surgical site by injection through a syringe. The administration of the adhesion preventative can occur at any time before significant wound healing has occurred. It is preferred and most convenient to administer the adhesion preventative during surgery or at the conclusion of the surgical procedure just prior to closing of the wound. However, in some cases, it may be desired to administer the adhesion preventative continually over a period of time. An "effective amount" of adhesion preventative topically applied to the site of surgical trauma is an amount necessary to affect a reduction in the incidence of post-operative surgical adhesion formation. The amount applied will depend on numerous factors, most significantly of which is the surface area of the site of surgical trauma. Preferably, the amount of preventative applied should be enough to coat the entire area exposed to the surgical trauma, and if necessary or desired, an additional amount sufficient to coat bodily tissue adjacent to those areas actually exposed to the surgical trauma. The effective amount can be readily determined empirically. The adhesion preventative used to prevent adhesion formation as described in this invention may also be used as a delivery vehicle for other adhesion prevention aids. For example, the preventative can be used as a delivery vehicle for other well known adhesion preventatives, e.g. tolmetin or other non-steroidal anti-inflammatory drugs (NSAIDS) as described in U.S. Patent 4,937,254, or tissue plasminogen activator (tPA) as described in European Patent No. 297860. Such a combination may create a synergistic effect between tolmetin and the adhesion preventative to significantly improve the efficacy of either therapeutic agent used alone. Alternatively, the adhesion preventative can be used not only for reducing adhesions but also as a delivery vehicle for other therapeutic agents, such as antibiotics, growth factors and other medicaments. The following examples are intended to illustrate the claimed invention. EXAMPLE 1 Iron-Crosslinked HA Gel with High Crosslink Density as an Adhesion Preventative (a) Preparation of Gel 0.634 grams of sodium hyaluronate with an average molecular weight of about 600,000 is dissolved in 39.36 gm of water for injection in a glass beaker. After a homogeneous aqueous solution is obtained, 1.2 milliliters of a 1 N HCl is added with agitation to adjust solution pH. Then, 5.2 milliliters of a 1.5% ferric chloride solution is added with agitation. Finally, 2.493 ml of a 1.7 N NH 4 OH solution is added with agitation until a homogeneous gel is obtained with a pH close to neutral. The resulting gel exhibits a viscosity of about 88,600 cps. (b) Testing Protocol and Efficacy of Adhesion Preventative Long Evans rats (each weighs about 250 gm) are used in this study. Anaesthesia is accomplished with Ketamine (60 mg/Kg) and xylazine (10 mg/Kg) given intraperitoneally. To stimulate adhesions, the cecum is exteriorized and abrasions are made by wiping the cecum with gauze until punctate bleeding develops. Three 8 mm lesions are created on each side of the abdominal wall by removing a layer of the peritoneum and transverse abdominal muscle with a stainless steel biopsy punch. All accessible surfaces of the liver are abraded by rubbing them with the wooden end of a sterile swab. Six rats receive the ferric chloride crosslinked HA gel prepared by the process described in subpart (a) above. Three (3) ml of the ferric HA gel is applied to the cecum, biopsy punch sites and liver at closure of the incision. Six rats in this study receive no treatment and serve as the control group. Six rats are treated with a lyophilized porous foam of HA covalently crosslinked with Crosslinker CX-100 Polyfunctional Aziridine Crosslinker (from ICI Resins, U.S.). A 6 cm diameter piece of the covalently crosslinked HA foam is cut up into smaller pieces and then placed over the abraded liver areas. Saline is applied to the foam until saturation to hydrate the foam. Seven days after the surgery, the rats are sacrificed by carbon dioxide inhalation, and the sites are examined for the extent of adhesions. The number of sites and area of cecum adhesions are measured and recorded. The extent of liver adhesions at three sites is graded on a 0-to-6 scale, with a maximum total score of 18 representing the most severe adhesion formation. Ranking of the total scores of the three liver sites is used in statistical analysis of the experimental results. The results are summarized in Table 1. The results indicate that the iron crosslinked HA gel shows significantly lower adhesions to the cecum and between liver lobes relative to the frequency of adhesions exhibited for an untreated control or a covalently crosslinked HA adhesion preventative. EXAMPLE 2 Iron-Crosslinked HA Gel with Low Crosslink Density as an Adhesion Preventative The procedure described in Example 1 for preparing the iron crosslinked HA gel, as well as its testing protocol, are substantially repeated to prepare and evalute an iron crosslinked HA gel with low crosslink density as an adhesion preventative. The following changes are made: (a) Half of the amount of the ferric chloride solution is used to prepare the iron crosslinked HA gel to reduce the crosslink density, e.g. 2.6 ml of a 1.5% ferric chloride solution is added to the HA solution instead of 5.2 ml of solution which results in a gel of lower viscosity, i.e. 60,200 cps.; (b) the adhesion preventative is compared with a lyophilized porous foam of HA which is covalently crosslinked with 1,4 butanediol digylcidyl ether instead of Polyfunctional Aziridine Crosslinker; and (c) the adhesion preventative is additionally compared with non-crosslinked sodium hyaluronate in saline solution exhibiting a viscosity of about 93,800 cps. The results of the study are shown in Table 2. The results indicate that the iron crosslinked HA gel shows significantly lower adhesions to the cecum and between liver lobes relative to the frequency of adhesions exhibited for an untreated control, a non-crosslinked HA adhesion preventative, or a covalently crosslinked HA adhesion preventative. COMPARATIVE EXAMPLE 3 Aluminum-Crosslinked HA Gel as an Adhesion Preventative (a) Preparation of Gel 1.917 grams of sodium hyaluronate is dissolved in 118.1 grams of water for injection in a glass beaker. After a homogeneous aqueous solution is obtained, 7.2 milliliters of a 5% aluminum chloride hexahydrate solution is added with agitation. Then, 2.2 milliliters of a 1.7 N NH 4 OH solution is added with agitation until a homogeneous gel is obtained with a pH close to neutral. (b) Testing Protocol and Efficacy of Adhesion Preventative Female New Zealand white rabbits of reproductive age (each weighed about 3.0 to 3.5 Kg) underwent uterine horn surgery to induce abdominal adhesion. The procedure involved making a midline incision into the abdomen, traumatizing both uterine horns, applying the crosslinked HA gel, and closing the wound. Twenty (20) rabbits are evenly divided into two groups: the control group, which receives no treatment before closing the wound, and aluminum-crosslinked HA treatment group. For the treated group, 10 millilitiers of crosslinked HA gel (prepared according to subpart (a) above) is squirted directly on the uterus wherever adhesions are expected right before closing the wound. Seven days after surgery, each rabbit is sacrificed and a second procedure is performed to evaluate the extent of adhesions. Adhesions are subjectively scored on a scale from 0 (no adhesion) to 4 (severe adhesion) in increments of 0.5 in a blinded randomized manner. Table 3 summarizes the the results. Efficacy of Aluminum Crosslinked HA Gel for Reducing Adhesions Test Group No. of Rabbits Treated Median Score Mean Rank Control 10 3.50 25.0 Aluminum-Crosslinked HA 10 1.00 10.2 The results indicate that the use of an aluminum crosslinked HA gel as an adhesion preventative significantly reduces the incidence of post-operative adhesion formation. EXAMPLE 4 Tissue Reaction and Half-Life of Iron-Crosslinked HA Gel Ferric chloride crosslinked HA gel prepared from Example 2 (referred to as the "test" case) and sodium hyaluronate solution (referred to as the "control" case) are injected into the abdominal subcutaneous tissues of rats and analyzed at 1, 3, 7 and 14 days (4 rats/time period) to determine tissue reaction and absorption characteristics. Each animal has 2 test and 2 control 0.5 cc injection sites. Fixation is either by 10% formalin or a pH 7.4 fixative composed of 3% formaldehyde, 0.5% cetylpyridinium chloride and 30 mM NaCl in a 0.1 M phosphate buffer. The latter fixative forms an insoluble complex with glycosaminoglycans (ref: J. Histochem. and Cytochem., 33: 1060-1066, 1985). Hemantoxylin & eosin (H&E) staining is used with selected sites stained with Alcian blue in order to better visualize the HA. Tissue reaction grading is subjective. Tissue reactions at test and control sites ranged from trace to slight at 1 and 3 days. Neutrophils and macrophages are present at day 1. By day 3 there are predominantly macrophages with smaller numbers of neutrophils and fibroblasts. Frequent macrophages at the day 3 test sites had a fine golden-brown intracytoplasmic pigment. HA is present at the majority of sites at 3 days. At the day 7 test sites, coarse pigment-containing macrophages are the predominant cell type comprising a minimal to slight tissue reaction. The tissue reactions at the control sites are either zero or trace to minimal and composed predominantly of fibroblasts. There is apparent total absorption of HA at all control sites. A minimal amount of HA is still present at 3/7 test sites. By 14 days the reactions at test sites are considered to be minimal with a decrease in the overall numbers of pigment-containing macrophages. The majority of control sites are difficult to localize due to a lack of residual tissue reaction. HA has been totally absorbed at all test and control sites by 14 days. The tissue reactions of both samples are within acceptable limits.

Claims: A composition comprising an ionically crosslinked carboxyl-containing polysaccharide aqueous gel, wherein the carboxyl-containing polysaccharide is medical grade, highly purified hyaluronic acid or sodium hyaluronate having carboxyl groups which are ionically crosslinked with a Fe 3+ cation in an amount which is sufficient to crosslink at least 10 % of the carboxyl groups of the polysaccharide. The composition of claim 1, wherein the carboxyl-containing polysaccharide is sodium hyaluronate. The gel composition of claim 1 or claim 2, wherein the carboxyl-containing polysaccharide is crosslinked with ferric chloride. The composition of any one of claims 1 to 3, further comprising a drug. The composition of claim 4, wherein the drug is an adhesion prevention aid, antibiotic or growth factor. The composition of claim 5, wherein the adhesion prevention aid. is a non-steroidal anti-inflammatory drug, preferably tolmetin. A topically applicable composition for application to a site of surgical trauma for the prevention of adhesion comprising a composition according to any one of claims 1 to 6. The composition of claim 7, which is topically applicable directly to the site of surgical trauma in one application by injection through a syringe. A drug delivery system comprising a composition according to any one of claims 4 to 8. Use of an ionically crosslinked carboxyl-containing polysaccharide composition as defined in any one of claims 1 to 8 in the production of a topically applicable medicament for use in adhesion prevention.

Inventors: HUANG W JAMES, JOHNS DOUGLAS B, KRONENTHAL RICHARD L, HUANG, W. JAMES, JOHNS, DOUGLAS B., KRONENTHAL, RICHARD L.
Applicants: LIFECORE BIOMEDICAL INC, LIFECORE BIOMEDICAL, INC.
Application year: 1992
Main classification: A61K31
IPC codes: A61K31, A61K45, A61P43