Catalyst carrier, composition and process for making same

Abstract: Catalyst carrier or support consisting of: (a) at least 85 % by weight of alpha alumina, (b) 0.01-6 % of an alkaline earth metal oxide, (c) 0.01-5 % of silicon oxide and (d) 0-10 % of zirconium oxide (optional). The carrier is suitable for preparing silver containing ethylene oxide catalysts. A method for making the carrier is also disclosed.

Description: The invention relates to a catalyst carrier as well as to a compostion and a process for making same. Catalysts for the production of ethylene oxide from ethylene and molecular oxygen generally comprise silver supported on a carrier formed substantially of alpha alumina. Such catalysts are typically promoted with alkali metals. Other co-promoters, such as rhenium, or rhenium along with sulfur, molybdenum, tungsten and chromium can also be utilized. See, for example, U.S. 4,766,105, issued August 23, 1988. While much research has been focused on promoters, more recently, work has been focused on the alumina supports and ways to modify them to produce improved catalysts. European Patent Application 247,414, published December 2, 1987, discloses the addition of silica to an alpha alumina carrier. U.S. Patent No. 4,428,863, issued January 31, 1984, discloses the addition of barium aluminate or barium silicate to alumina carriers during their manufacture. In U.S. Patent No. 4,728,634, issued March 1, 1988, silicon dioxide and an alkali metal salt are mixed with water and an aluminum compound and calcined to produce a silica- and alkali metal-containing alpha alumina support. In U.S. Patent No. 4,874,739, October 17, 1989, a tin compound and an alkali metal compound are incorporated in to an alpha alumina carrier. US-A-3,725,307 relates to a silver-supported catalyst used in the production of the ethylene oxide by the vapor phase oxidation of ethylene. The catalyst disclosed in US-A-3,725,307 has a selectivity in the range of 70%. The carrier of this catalyst contains a large amount of silicon oxide (11.65%). The invention provides a catalyst carrier according to independent claims 1 and 2, a carrier composition suitable for preparing a catalyst carrier according to independent claims 3 and 4, and a method for making catalyst carriers according to independent claim 7. Further advantageous features, aspects, and details of the invention are evident from the dependent claims, the description and embodiments and tables. The invention provides a novel alpha alumina carrier useful in conjunction with silver-containing catalysts in the preparation of ethylene oxide. The invention provides an alpha alumina based carrier comprising at least 85% by weight of alpha alumina, from 0.05 to 6% by wt. (measured as the oxide) of a calcium or magnesium oxide which is defined to include mixed oxides such as the preferred silicate; from 0.05 to 5% by weight, (measured as silica) of a silicon oxide, including mixed oxides such as the silicates, and from 0.3 to 5% by wt. (measured as the oxide) of a zirconium oxide. According to the invention, the carrier compositions comprise the calcium, magnesium and the silicon containing compounds in the form of a single compound, an alkaline earth metal silicate, which is added as an original component or generated in situ by the reaction of silica or silica generating compounds with compounds that decompose to calcium or magnesium oxide upon heating, with the amount of the oxide formed being in stoichiometric excess over the silica so as to leave essentially no residual base-soluble silica in the final composition. The alkaline earth metal component of the catalyst is chosen between calcium and magnesium with the former being the most preferred. In the further description of this invention reference will frequently be made to the calcium form for the sake of simplicity. The preferred carriers may be prepared by mixing a powdered alpha alumina, calcium silicate and zirconia with water and a binder and/or burnout material to prepare a mixture which is then extruded and calcined at a temperature ranging from 1350°C to 1500°C. The novel carrier of the invention may be prepared from high purity alpha alumina powder, a calcium or magnesium oxide-providing compound, a silica-providing compound; a zirconia-providing compound and conventional binders/burnout agents. The alpha alumina used in the carrier preparation generally has a purity greater than 98%, preferably greater than 98.5% and less than 0.06% by weight such as from 0.02 to 0.06% by weight of soda impurities. The alumina has the form of a fine powder, preferably one having an average particle size of from 0.5 to 5µm and more preferably from 1 to 4µm. The average crystallite size, which can be from 0.1 to 5µm and more preferably from 2 to 4µm, is determined by measuring the maximum dimension of a number of crystallites and taking the average thereof. The alpha alumina will be present in the calcined carrier in an amount greater than 85%, preferably 90, and more preferably 95% by weight of the total carrier. The calcium or magnesium component of the carrier composition of the invention is present in an amount that represents from 0.05 to 6% by weight (measured as the oxide, MO,) of the carrier weight but preferably the amount present is from 0.05 to 5.0% and especially from 0.05 to 4.0% by weight. Calcium or magnesium amounts present of 0.05 to 2% weight are also preferred. Where a silicate is formed in situ, the weights of the components used are selected with these limitations in mind and so as to avoid the presence of base-soluble silica in the finished composition. The alkaline earth compounds that may be used to prepare the carriers of the invention are compounds that are decomposable to or which form oxides upon calcination. Examples include carbonates, nitrates, and carboxylates. Other suitable compounds include mixed oxides such as the silicates, zirconates and the like. The preferred compound is calcium silicate. The silicon compounds used to prepare the carriers of the invention are oxides or compounds decomposable to the oxides upon calcination. Suitable compounds include silicon dioxide itself, as well as the mixed oxides such as the alkaline earth metal silicates, zirconium silicates, aluminosilicates such as zeolites, hydrolyzable silicon compounds, polysiloxanes and the like. The amount used is such as to provide, in the final carrier composition, from 0.05 to 5.0%, such as from 0.05 to 4.0% and most conveniently from 0.05 to 3.0% by weight, (measured as silica). The zirconia component, is present in an amount that is from 0.3 to 5.0% and especially to 2.0% by weight based on the carrier weight. Where the zirconia is generated in situ, the amount used should be selected to give a final proportion within these parameters. The zirconium compounds which are used to prepare the carriers are oxides or compounds which are decomposable to or which form oxides upon calcination. Examples include carbonates, nitrates and carboxylates. Suitable compounds include zirconium nitrate, zirconium dioxide, as well as the mixed oxides such as zirconium silicates, zirconium aluminosilicates, zirconates and the like. The preferred compound is zirconium dioxide. The alpha alumina powder is most preferably combined with calcium silicate itself but, as indicated above, it is also possible to use a calcium oxide-generating compound and silica or a silica-generating compound in such proportions that on heating calcium silicate is produced with essentially no base soluble silica. These components are mixed with zirconia or a zirconia-generating compound, a burnout/binding agent and water, formed into shapes and calcined. The burnout agent is a material that is added to the mixture such that upon calcination, it is completely removed from the carrier, leaving a controlled porosity in the carrier. These materials are carbonaceous materials such as coke, carbon powders, graphite, powdered plastics such as polyethylene, polystyrene and polycarbonate, rosin, cellulose and cellulose based materials, sawdust and other plant materials such as ground nut shells, e.g. pecan, cashew, walnut and filbert shells. Carbon-based binding agents can also serve as burnout agents. The burnout agents are provided in an amount and size distribution to provide a final carrier having a water pore volume preferably ranging from 0.2 to 0.6 cm 3 /g. Preferred burnout agents are cellulose-derived materials, such as ground nut shells. The term "binding agent" as used herein refers to an agent that holds together the various components of the carrier prior to calcination to form an extrudable paste, i.e, the so-called low temperature binding agent. The binding agent also facilitates the extrusion process by adding lubricity. Typical binding agents include alumina gels, particularly in combination with a peptizing agent such as nitric or acetic acid. Also suitable are the carbon based materials that can also serve as burnout agents, including celluloses and substituted celluloses such as methylcellulose, ethylcellulose and carboxyethylcellulose, stearates such as organic stearate esters, e.g. methyl or ethyl stearate, waxes, polyolefin oxides and the like. Preferred binding agents are polyolefin oxides. The use of calcium silicate, whether prepared directly or in situ with the constraints described above, allows the use of bonds containing, overall, a lower amount of silica then is present in conventional bonds. It also permits the avoidance of an excess of silicon dioxide which typically contains deleterious amounts of sodium, iron and/or potassium impurities, especially when present in clays, bentonite and the like. The role of the zirconia is not fully understood but it appears to stabilize certain partial oxidation catalyst recipes. Calcium silicate also appears to stabilize at least a proportion of the zirconia in the more active tetragonal form instead of the monoclinic form to which the mixed phase reverts when heated in the absence of calcium silicate. After the components of the carrier are mixed together, say by milling, the mixed material is extruded into shaped pellets, for example, cylinders, rings, trilobes, tetralobes and the like. The extruded material is dried to remove water that would convert to steam during calcination and destroy the physical integrity of the extrudate shapes. Typically the drying and calcination are combined in one step by suitable programming of the time and temperature. Calcining is carried out under conditions sufficient to remove burnout agents and binding agents and to fuse the alpha alumina particles into a porous, hard mass. Calcination is typically carried out in an oxidizing atmosphere, say oxygen gas or preferably air and at a maximum temperature over 1300°C and preferably ranging from 1350°C to 1500°C. Times at these maximum temperatures can range from 0.5 to 200 minutes. The calcined carriers will typically have pore volumes (water) ranging from 0.2 to 0.6, and more preferably from 0.3 to 0.5 cm 3 /g, and surface areas ranging from 0.15 to 3.0, and preferably from 0.3 to 2.0 m 2 /g. The carrier formulation preferably has a low soda content which is less than 0.06% by wt. In practice it is very difficult to obtain a sodium-free formulation and soda contents from 0.02 to 0.06% by wt. are usually found acceptable. The carriers described above are particularly suited for preparing ethylene oxide catalysts which have high initial selectivities and long lives (enhanced stability). In a preferred application of silver catalysts carried on carriers according to the present invention, ethylene oxide is produced when an oxygen-containing gas is contacted with ethylene in the presence of the catalyst/carrier at a temperature in the range of from about 180 °C to about 330 ° C and preferably about 200 °C to about 325 °C. Illustrative Embodiments Carrier Preparation Carrier A: An alpha alumina powder having the properties listed in Table 2 below was used to prepare the carrier. Table 2 Median Particle Size 3.0-3.4 µ m Average Crystallite Size 1.8-2.2 µ m Soda Content 0.02-0.06% by wt. This powder was used to prepare a formulation of the following ceramic components: Alpha Alumina 98.8% Zirconia 1.0% Calcium Silicate 0.2% Based on the weight of this formulation, the following were added in the indicated proportions: Burn-out (walnut shell flour) 25.0% Boric Acid 0.1% Extrusion Aid* 5.0% *Polyolefin oxide After the above had been mixed for 45 seconds, enough water was added to give an extrudable mixture, (about 30% in practice), and mixing was continued for a further 4 minutes. At this point 5% (based on the weight of the ceramic components), of vaseline was added and mixing was continued for a further 3 minutes. This material was extruded in the form of .79cm x .79cm (5/16 x 5/16 inch) hollow cylinders and dried to less than 2% moisture. These were then fired in a tunnel kiln to a maximum temperature of 1390 °C for about 4 hours. After processing in this manner the carrier had the following properties: Water Absorption 40.8% Crush Strength 8.48Kg (18.7 lbs.) Surface Area 0.56 m 2 /g. Total Pore Volume (Hg) 0.43 cm 3 /g. Median Pore Diameter 4.6µm Leachable Cations (in nitric acid) in ppm: Na 141 K 55 Ca 802 Al 573 SiO 2 1600 Additional carriers were prepared in a manner similar to the method described above with the exception that different starting materials were used. The properties of the different starting aluminas are shown in Table 3 below. Table 3 Properties for Aluminas Nos. 11 and 49 #11 #49 Median Particle Size 3.0-3.6 3.0-4.0 µm Average Crystallite size 1.6-1.8 1.0-1.4 µm Soda Content 0.02-0.06% 0.02-0.06% by wt. The water pore volumes, surface areas and firing temperatures are shown in Table 4 and the other starting materials and their amounts are shown in Table 5 below. A comparative carrier was made with alumina #10 in the same manner described above for carrier A except that no zirconia or calcium silicate were added. This comparative carrier was denoted as Com-A. Its properties are provided in Table 4 below. Table 4 Carrier Pore Vol. cm 3 /g Surface Area m 2 /g (water) Firing Temp. Degrees °C Com-A 0.46 0.52 1371 A 0.41 0.54 1388 B 0.42 0.52 1371 C 0.39 0.49 1371 F 0.30 0.34 1371 G 0.27 0.25 1371 I 0.43 0.60 1400 K 0.37 0.50 1371 L 0.42 0.59 1371 M 0.38 0.51 1371 P 0.50 0.66 1413 Q 0.47 0.68 1413 R 0.51 0.81 1413 S 0.43 0.45 1413 T 0.43 0.38 1413 X 0.42 0.41 1400 Z 0.41 0.44 1371 AA 0.40 0.46 1371 Table 5 Carr. Alumina Compound A* Compound B* Compound C* Com-A #10 A #10 ZrO 2 (1.0) CaSiO 3 (0.20) B #10 ZrO 2 (1.0) CaSiO 3 (0.10) C #10 ZrO 2 (1.0) CaSiO 3 (0.40) F #10 ZrO 2 (1.0) CaSiO 3 (2.00) G #10 ZrO 2 (1.0) CaSiO 3 (4.00) I #10 ZrO 2 (1.0) Ca(NO 3 ) 2 (0.28) SiO 2 (0.10) K #10 ZrO 2 (1.0) CaSiO 3 (0.20) Ca(NO 3 ) 2 (0.29) L #10 ZrO 2 (1.0) MgSiO 3 (0.20) M #10 ZrO 2 (1.0) MgSiO 3 (2.20) P #49 ZrO 2 (1.0) CaSiO 3 (0.30) Q #49 ZrO 2 (1.0) CaSiO 3 (0.30) Ca(NO 3 ) 2 (0.29) R #49 ZrSiO 4 (0.46) Ca(NO 3 ) 2 (0.44) S #49 ZrSiO 4 (0.46) Ca(NO 3 ) 2 (0.73) T #49 ZrSiO 4 (0.46) Ca(NO 3 ) 2 (1.02) X #11 ZrO 2 (1.0) Mullite (0.07) Ca(NO 3 ) 2 (0.22) Z #10 ZrO 2 (5.0) CaSiO 3 (0.20) AA #10 ZrO 2 (10.0) CaSiO 3 (0.20) *Weight percent basis alumina. Catalyst Preparation Carrier A described above is a preferred carrier and was used to prepare an ethylene oxide catalyst, into a solution of water and ethylenediamine were dissolved silver oxalate, cesium hydroxide, ammonium perrhenate, lithium sulfate and lithium nitrate in amounts sufficient to provide in the impregnated carrier (basis dry weight of carrier) 13.2 %wt silver, 440 ppm cesium, 1.5 micromoles/g of ammonium perrhenate, 1.5 micromoles/g of lithium sulfate and 4 micromoles/g of lithium nitrate. Approximately 30 g of the carrier were placed under 25 mm vacuum for 3 minutes at room temperature. Approximately 50 g of the impregnating solution were then introduced to submerge the carrier, and the vacuum was maintained.at 25 mm for an additional 3 minutes. At the end of this time, the vacuum was released, and the excess impregnating solution was removed from the carrier by centrifugation for 2 minutes at 500 rpm. The impregnated carrier was then cured by being continuously shaken in a 8.4 cu.m./hr (300 cu.ft./hr.) air stream at 250°C for 5 minutes. The cured catalyst, denoted as C-A', is ready for testing. The actual silver content of the catalyst can be determined by any of a number of standard, published procedures. The actual level of rhenium on the catalysts prepared by the above process can be determined by extraction with 20 Mm aqueous sodium hydroxide solution, followed by spectrophotometric determination of the rhenium in the extract. The actual level of cesium on the catalyst can be determined by employing a stock cesium hydroxide solution, which has been labeled with a radioactive isotope to cesium, in catalyst preparation. The cesium content of the catalyst cari then be determined by measuring the radioactivity of the catalyst. Alternatively, the cesium content of the catalyst can be determined by leaching the catalyst with boiling deionized water. In this extraction process cesium, as well as the other alkali metals, is measured by extraction from the catalyst by boiling 10 grams of whole catalyst in 20 milliliters of water for 5 minutes, repeating the above two more times, combining the above extractions and determining the amount of alkali metal present by comparison to standard solutions of reference alkali metals using atomic absorption spectroscopy (using Varian Techtron Model 1200 or equivalent). It should be noted that the cesium content of the catalyst as determined by the water leaching technique may be lower than the cesium content of the catalyst as determined by the radiotracer technique. The carriers listed in Table 4 and 5 were used to prepare the catalysts listed in Table 6. C-A and C-A' refer to a catalyst prepared with Carrier A, C-B and C-B' refer to a catalyst prepared with carrier B, etc. Table 6 Catalyst Ag Wt% Cs ppm NH 4 ReO 4 µ mol/g Li 2 SO 4 µ mol/g LiNO 3 µ mol/gC- C-Com-A 13.2 501 1.5 1.5 4 C-A 13.5 463 1.5 1.5 4 C-A' 13.5 437 1.5 1.5 12 C-B 13.2 506 1.5 1.5 4 C-C 13.2 480 1.5 1.5 4 C-F 12.0 277 1.0 1.0 4 C-G 12.0 306 1.0 1.0 4 C-I 13.2 665 2.0 2.0 4 C-K 13.2 442 1.5 1.5 4 C-L 13.2 540 1.5 1.5 4 C-L' 13.2 481 1.5 0 4 C-M 13.2 415 1.5 1.5 4 C-M' 13.2 382 1.5 0 4 C-P 14.5 599 2.0 2.0 4 C-Q 14.5 572 1.5 1.5 4 C-R 14.5 795 2.0 2.0 4 C-S 13.2 510 1.5 1.5 4 C-T 13.2 520 1.5 1.5 4 C-X 13.3 500 1.5 1.5 4 The Process The following describes the standard microreactor catalyst test conditions and procedures used to test the catalyst for the production of ethylene oxide from ethylene and oxygen. Three to five grams of crushed catalyst (14 filaments warp direction, 20 filaments shute direction per 2.54cm (14-20 mesh) are loaded into a .58cm (0.23 inch) diameter stainless steel U-shaped tube. The U tube is immersed in a molten metal bath (heat medium) and the ends are connected to a gas flow system. The weight of catalyst used and the inlet gas flow rate are adjusted to achieve a gas hourly space velocity of 3300 cc of gas per cc of catalyst per hour. The inlet gas pressure is 14.49 bar guage (210 psig). The gas mixture passed through the catalyst bed (in once-through operation) during the entire test run (including startup) consists of 30% ethylene, 8.5% oxygen, 5-7% carbon dioxide, 54.5% nitrogen, and 0.5 to 5 ppmv ethyt chloride. The initial reactor (heat medium) temperature is 180°C. After one hour at this initial temperature, the temperature is increased to 190 °C for one hour, followed by 200 °C (1hour), 220 °C (1 hour), 227 °(2 hours), 235 °C (2 hours), and 242 °C (2 hours). The temperature is then adjusted so as to achieve a constant oxygen conversion level of 40% (T 40 ). The moderator level is varied and run for 4-24 hours at each level to determine the optimum moderator level for maximum selectivity. Performance data at the optimum moderator level and at T 40 are usually obtained when the catalyst has been onstream for a total of about 24 hours and are provided in the examples given below. Due to slight differences in feed gas composition, gas flow rates, and the calibration of analytical instruments used to determine the feed and product gas compositions, the measured selectivity and activity of a given catalyst may vary slightly from one test run to the next. To allow meaningful comparison of the performance of catalysts tested at different times, all catalysts described in this illustrative embodiment were tested simultaneously with a standard reference catalyst. All performance data reported in this illustrative embodiment are corrected to conform to the average initial performance of the reference catalyst which was S 40 = 81.0% and T 40 = 230°C). The catalysts prepared above were tested using the above procedure and the results are given in the table below. Table 7 Catalyst S 40 '% T 40 ,°C C-Com-A 85.1 261 C-A 85.8 258 C-A' 86.0 258 C-B 86.3 261 C-C 85.8 256 C-F 85.6 259 C-G 85.0 276 C-I 85.2 263 C-K 87.4 258 C-L 87.1 250 C-L' 87.3 252 C-M 86.8 260 C-M' 86.0 252 C-P 84.3 247 C-Q 85.5 252 C-R 86.6 260 C-S 83.8 250 C-T 85.7 264 C-X 85.9 254

Claims: A catalyst carrier based on alpha alumina comprising at least 85% by weight of alpha alumina, from 0.05 to 6% by weight (measured as the oxide) of calcium or magnesium oxide; from 0.05 to 5% by weight (measured as silica) of a silicon oxide, and from 0.3 to 5% by weight (measured as the oxide) of a zirconium oxide, wherein the calcium or magnesium and silicon containing compounds in the carrier are in the form of a single alkaline earth metal silicate which was added as an original component. A catalyst carrier based on alpha alumina comprising at least 85% by weight of alpha alumina, from 0.05 to 6% by weight (measured as the oxide) of calcium or magnesium oxide; from 0.05 to 5% by weight (measured as silica) of a silicon oxide, and from 0.3 to 5% by weight (measured as the oxide) of a zirconium oxide, comprising an alkaline earth metal silicate prepared in situ by the reaction of silica or silica generating compounds with compounds that decompose to calcium or magnesium oxide upon heating, with the amount of the oxide formed being in stoichiometric excess over the silica, so as to leave essentially no residual base-soluble silica. A carrier composition for preparing a catalyst carrier comprising at least 85% by weight of alpha alumina powder, from 0.05 to 6% by weight (measured as the oxide, MO) of a calcium or magnesium oxide, from 0.05 to 5% by weight (measured as silica) of a silicon oxide, and from 0.3 to 5% by weight (measured as the dioxide) of zirconium in the form of an oxide, a binding agent and a burnout agent, wherein the calcium or magnesium and the silicon containing compounds are in the form of a single alkaline earth metal silicate. A carrier composition for preparing a catalyst carrier comprising at least 85% by weight of alpha alumina powder, from 0.05 to 6% by weight (measured as the oxide, MO) of calcium or magnesium compounds that decompose to calcium or magnesium oxide upon heating, from 0.05 to 5% by weight (measured as silica) of silica or silica generating compounds, and from 0.3 to 5% by weight (measured as the dioxide) of zirconium in the form of an oxide, a binding agent and a burnout agent, wherein said calcium or magnesium oxide by the reaction with silica forms an alkaline earth metal silicate, and wherein said compounds that decompose to calcium or magnesium oxide upon heating are present in such amounts that the amount of the oxide formed is in stoichiometric excess over the silica, so as to leave essentially no residual base-soluble silica. The composition according to claim 3, comprising at least 95 percent by weight of alpha alumina, from 0.05 to 4 percent by weight of calcium silicate, and from 0.3 to 5 percent by weight of zirconia. The composition according to one of claims 3 to 5, in which the alumina has a soda content of less than 0.06% by weight. A process for preparing a catalyst carrier comprising the following steps: (a) mixing: (i) an alpha alumina powder having a purity of greater than 98 percent and having an average crystallite size between 0.1 and 5 µ m, (ii) a calcium or magnesium compound which is decomposable to or forms oxide upon calcination, (iii) a silicon oxide or compound which is decomposable to or forms an oxide upon calcination and (iv) a zirconium oxide or compound which is decomposable to or forms an oxide upon calcination, with water and a binder/burnout agent in amounts sufficient to provide in the finished carrier alpha alumina in an amount greater than 85 percent by weight, a calcium or magnesium oxide in an amount ranging from 0.05 to 6% by weight, silicon oxide in an amount ranging from 0.05 to 5% by weight, and zirconium oxide in an amount ranging from 0.3 to 5% by weight, (b) extruding the resulting mixture of step (a) to form pellets; and (c) calcining the pellets at a temperature greater than 1300°C for a time sufficient to produce a carrier having a surface area ranging from 0.3 to 2 square meters per gram and a water pore volume ranging from 0.2 to 0.6 cubic centimeters per gram, and to generate in situ an alkaline earth metal silicate by the reaction of the compounds (ii) and (iii) wherein in step (a) compound (ii) is added in such an amount that the amount of the oxide formed is in stoichiometric excess over the silica, so as to leave essentially no residual base-soluble silica.

Inventors: DODDATO CARMINE M, GERDES WILLIAM H, MALONE PATRICK F, DODDATO, CARMINE M., GERDES, WILLIAM H., MALONE, PATRICK F.
Applicants: NORTON CO, NORTON COMPANY
Application year: 1992
Main classification: B01J21
IPC codes: C07D301, B01J37, B01J21, B01J23, B01J32, B01J33