Carbon/polymer composite electrode for use in a lithium battery

Abstract: A carbon/polymer composite electrode comprises substantially amorphous carbon entrapped in a polymeric matrix, wherein the matrix further entraps an interpenetrating ionically conducting liquid having an alkali metal salt dissolved therein. Such an electrode may be used as the anode in an electrochemical cell, or battery, which also comprises a polymeric electrolyte and a cathode. The cathode may be a vanadium oxide composition containing intercalated lithium ions or LiCoO₂.

Description: This invention is directed to electrochemical cells and particularly to electrodes used as the negative electrode, or anode, in a rechargeable lithium rocking chair battery. Solid-state electrochemical cells are typically constructed from an alkali metal negative electrode (anode), an ionically conducting polymeric electrolyte containing an ionizable alkali metal salt, and a positive electrode (cathode). The cathode is usually formed by preparing a mixture of an active material, a metal salt, a polymeric electrolyte, and a conductive filler such as carbon black, and coating this mixture on a metal foil which functions as a current collector. Electrochemical cells formed in this fashion using lithium metal as the alkali metal anode have found wide use in numerous applications requiring portable battery power, since lithium batteries formed in this manner have a high energy density. However, lithium metal is widely considered to be the major source of safety-related problems when lithium batteries are made rechargeable. Charging of such batteries converts lithium ions to metallic lithium, and the presence of metallic lithium in undesirable locations in the battery structure can result in the battery exploding. One proposal to overcome this disadvantage is to use an intercalation compound based anode coupled with an intercalation compound based cathode. In electrochemical cells employing such electrodes, the charging and discharging process can be accomplished without the formation of metallic lithium as described below. On discharge of such a cell, lithium which is intercalated in the anode is discharged from that electrode into the electrolyte as lithium ions. The corresponding action at the cathode involves the intercalation of lithium ions into the active cathode material. When the resulting discharged cell is subject to charging conditions, the reverse processes occur at the two electrodes; lithium ions are discharged from the cathode and are intercalated into the active material of the anode. This entire process does not involve the formation of metallic lithium at any stage. Batteries made from such electrodes are referred to as "rocking-chair" batteries, since the alkali metal ions transfer back and forth between the anode and cathode. Intercalation electrodes and rocking-chair batteries are known. For example, the U.S. Patent No. 4,631,810 discloses a method for making an intercalation compound based cathode in which a dispersion of vanadium oxide, acetylene black and polyethylene oxide in acetonitrile is applied to a nickel foil current collector and the solvent removed. However, there is a need for alternative approaches to preparing lithium intercalation electrodes. A composite electrode is known from EP-A-0404478. A carbonaceous material, of which crystalline graphite is exemplified, is combined with a polymeric electrolyte in three alternative ways. In one case the carbonaceous material and the solid electrolyte are mechanically kneaded. In a second case the solid carbonaceous material is coated with dissolved electrolyte. In a third case the carbonaceous solid material is immersed into a liquid electrolyte solution, a chemical reaction binding the solid electrolyte to the boundary thereof. In accordance with the present invention, we provide a carbon/polymer composite electrode characterised in comprising: a polymeric matrix; substantially amorphous carbon, namely carbon which is 80% or more non-crystalline or is microcrystalline in which 80% or more of the carbon microcrystals are in a random arrangement, homogeneously dispersed within and entrapped in said matrix; and, further contained in said matrix, an interpenetrating ionically conducting non-aqueous liquid having an alkali metal salt dissolved therein. We have found embodiments of such electrode to be capable of obtaining current densities as high as or higher than 100 mA/cm 2 and/or storage capacities as high as or higher than 1.4 mAh/cm 2 . An electrochemical cell in accordance with the invention comprises such an electrode, a polymeric electrolyte and a cathode. The polymer and interpenetrating ionically conducting liquid may together represent a polymer-host network electrolyte, such as described in US Patent Nos. 4,925,752 and 4,990413, for example. The positive electrode (cathode) may be a lithium intercalation compound based electrode and is preferably lithium vanadium oxide or lithium cobalt oxide. Embodiments of electrodes in accordance with the invention can sustain a current density as high or higher than 100 mA/cm 2 and have a storage capacity as high as or higher than 1.4 mah/CM 2 . One unusual feature of electrodes in accordance with the present invention is the use of a substantially amorphous or highly disordered form of carbon. Conventional teachings in the battery art indicated that ordered and crystalline forms of graphite and other ordered and crystalline carbon forms were preferred so as to provide ordered structures into which metal ions could intercalate. In contrast, the carbon used in electrodes in accordance with the present invention is substantially amorphous or highly disordered carbon. For example, the amorphous carbon can be activated carbon, acetylene black, Shawinigan black or the like. By a "substantially amorphous carbon" as used herein is meant a carbon in which at least about 80% or more of the carbon is non-crystalline or is microcrystalline in which at least about 80% of the carbon microcrystals are in a random arrangement. The non-crystalline or the microcrystalline random arrangement of the carbon may be at least about 90% or more. 100% of the carbon may be non-crystalline or have a microcrystalline random arrangement. See Pauling, L. "College Chemistry" (1957) W.H. Freeman & Co., San Francisco or Moeller, T. "Inorganic Chemistry" (1958) J. Wiley & Son, London for a discussion on amorphous or microcrystalline carbon as compared to crystalline carbon, such as graphite and diamond. The carbon material in electrodes in accordance with the present invention may have a particle diameter less than about 5mm, preferably less than about 1mm, and may have a surface area greater than about 20 m 2 /g, preferably greater than 50 m 2 g. The polymeric network, which is interpenetrated by the ionically conducting liquid and which serves as a matrix for holding the amorphous carbon to form a composite electrode, can be formed from a conductive polymer or can be a supportive matrix of a non-conductive polymer. Examples of polymers which may be used to form conductive polymeric networks are descnbed in U.S. Patent 4,303,748. These polymers have repeating units containing at least one heteroatom such as an oxygen or nitrogen atom. They can be represented as polymers having the repeating unit wherein R is hydrogen or a group R a , -CH 2 OR a , -CH 2 OR e R a , or -CH 2 N(CH 3 ) 2 in which R a is an alkyl group containing 1 to 16 carbon atoms and preferably 1 to 4 carbon atoms or a cycloalkyl group containing 5 to 8 carbon atoms and R e is an ether group of formula -[CH 2 -CH 2 O] p - wherein p is a number from 1 to 100, preferably 1 or 2: or having the repeating unit wherein R' is R a or R e R a , as defined above; or having the repeating unit wherein R e and R a are defined above. Copolymers of the above polymers may also be useful. In examples of our electrodes such polymers are cross-linked to form a network which is sufficiently rigid to provide physical integrity to the composite electrode as the cell is charged, discharged, and recharged. These polymers may be cross-linked in a number of ways. For example, U.S. Patent No. 4,357,401 to Andre et al. discloses PEO-PPO copolymers which are cross-linked by ethylene diamine. Where the polymer includes moieties of primary or secondary alcohols or amines, the polymer may be cross-linked by reaction with a cross-linking agent such as a polyisocyanate. For example, polyethylene oxides may also be cross-linked by using a cross-linking agent such as poly(ethylene glycol) diacrylate and a thermal free radical initiator such as 2,2'-azobis(2-methyl-propionitrile) as described in U. S. Application Serial Nos. 115,492 filed October 30, 1987 and 173,385, filed March 25, 1988, now U.S. patent 4,830,939. See also U. S. Patent No. 3,734,876. Radiation and thermally initiated free radical addition reactions may also be used to form the cross-linked polymeric network. A particularly useful group of radiation polymerizable compounds for providing a cross-linked conductive matrix is obtained by reacting a low molecular weight polyethylene glycol with acrylic or methacrylic acid. Also, radiation curable materials, such as, for example, acrylated epoxies, e.g. Bisphenol A Epoxy diacrylate, polyester acrylates, copolymers of glycidl ethers and acrylates or a vinyl compound such as N-vinylpyrrolidone may be used. The latter provides a non-conductive matrix. The radiation polymerizable polyethylenically unsaturated compounds may have a molecular weight of about 200 to 2,000 and more preferably 200 to 800. They may be liquid at temperatures less than 30°C. Examples of radiation curable materials include polyethylene glycol-300 diacrylate (average PEO molecular weight about 300), polyethylene glycol-480 diacrylate (average PEO molecular weight about 480) and the corresponding methacrylates. It may be desirable to include a radiation curable comonomer in the composition to reduce the glass transition temperature and improve the conductivity of the polymer. Any suitable monoacrylate such as tetrahydrofurfuryl acrylate, tetrahydrofurfuryl methacrylate, methoxypolyethylene glycol monomethacrylate, 2-ethoxyethyl acrylate, 2-methoxyethyl acrylate or cyclohexyl methacrylate may be used for this purpose. Triacrylates such as TMPTA, trimethylolpropane ethoxylated triacrylates (TMPEOTA) or trimethylolpropanepropoxy triacrylate may be used to introduce cross-linking of the polymer. Monoacrylates may be used in an amount of about 5 to 50% by weight based on the total amount of radiation polymerizable material. The triacrylates may be used in amounts of about 2 to 30% by weight on the same basis. Examples of cross-linked non-conductive supportive polymers are described in U.S. Patent 4,654,279 and include epoxies, polyurethanes, polymethacrylates, polyacrylates, polyacrylonitrile, and polystyrene. The radiation inert liquids which form the ionically conductive liquid interpenetrating phase can be any low volatility aprotic polar solvent capable of dissolving the ionizable alkali metal salt. Suitable solvents may be characterised by a boiling point greater than about 80°C. Low volatility simplifies manufacture and improves shelf life. Representative examples are propylene carbonate, gamma-butyrolactone, 1,3-dioxolane, and 2-2-methyltetrahydrofuran.Less polar solvents having heteroatoms capable of bonding alkali metal cations are also useful. Polyethylene glycol dimethyl ether (PEGDME) is one such example. Glymes such as tetraglyme, hexaglyme, and heptaglyme are also desirable solvents. The liquid may be propylene carbonate. Ionizable alkali metal salts include those salts conventionally used in solid state electrochemical cells, such a lithium, sodium, potassium or ammonium salts. Examples are sodium and lithium salts of less mobile anions of weak bases having a large anionic radius. Examples may be selected from the group consisting of I - , Br - ,SCN - ,C10 4 - ,PF 6 - ,AsF 6 - ,CF 3 COO - ,CF 3 SO 3 - , and the like. Examples of such salts include LiClO 4 , NaClO 4 , LiF 3 CSO 3 , LiBF 4 and the like. The salt may be used up to an amount which does not exceed its solubility limit in the electrolyte. The amount will therefore vary with the nature of the liquid solvent. As a general rule, the maximum amount of salt within its solubility limit should be used to maximise the ionic conductivity of the electrolyte. In most applications, about 10 to 60 parts salt may be used per 100 parts of liquid phase. Intercalation compounds and electronically conductive materials useful in forming the cathode that is used with the anode in an electrochemical cell in accordance with the present invention are well known in the art and include metal oxides, sulfides and selenides. Representative examples of intercalation compounds are V 3 O 8 , V 6 O 13 , V 2 O 5 , MnO 2 , MoO 2 , MoS 3 , Cr 3 O 6 , LiCoO 2 , Li x V 3 O 8 , TiS 2 and the like. The intercalation compound may be a vanadium oxide containing lithium or LiCoO 2 . The intercalation compound may have a particle size of less than about 1 micrometre but can range up to about 20 micrometres Other examples can be found in the aforementioned references, such as U.S. Patents Nos. 4,925,752 and 4,822,701. The conductive filler in the cathode is usually carbon black. Certain conductive polymers (which have a conjugated network of double bonds) such as, for example, polypyrole and polyacetylene may also be used for this purpose. To prepare an anode for an embodiment of an electrochemical cell in accordance with the present invention, a mixture of the uncross-linked polymer or the unpolymerized monomer or oligomer and the initiator or cross-linking agent where needed may be prepared and blended with the ionically conducting liquid, the ionizable salt, and the amorphous carbon. Blending is carried out by agitation, for example, or by stirring and the like, such that the particles of the amorphous carbon particles become individually and homogeneously dispersed in the mixture as described above. This may be done in an inert atmosphere at ambient temperatures of about 60°C. Due to the amorphous nature of the carbon, the viscosity of the resulting solution is higher than about 8,000cp (8 N s/m 2 ) at 75°C, and may be higher than about 10,000 cp (10 N s/m 2 ) at 75°C. The anode may be prepared by coating the mixture on a current collector, such as a metal foil member, and curing the composition. A suitable foil is lithium foil or lithium coated on nickel or copper foil or the like. The composition can be coated by solvent coating using conventional coating techniques such as a doctor blade, for example, or an extrusion method can be used. The anode may be coated to a thickness of about 10 to 100 micrometres typically to about 30 to 60 micrometres. Where a solvent casting technique is used, in addition to the components discussed above, the anode composition will contain a volatile solvent such as tetrahydrofuran. After coating, the solvent is removed if solvent casting method is used, and the composition is cured. Anode compositions in accordance with the present invention contain about 10 to 50 parts by weight of the amorphous carbon and preferably from about 25 to about 35 parts, about 0 to 10 parts of a conductive filler, about 0 to 20 parts of an ionizable metal salt, about 45 to 80 parts of an ionically conducting liquid, and about 20 to 55 parts of the cross-linked polymer preferably 25 to 40 parts, per 100 parts of the final polymer electrolyte composition (all parts by weight) In one embodiment of an electrochemical cell in accordance with the present invention, an amorphous carbon/polymer composite anode prepared by the aforementioned method is coated with a polymer host network electrolyte as previously described. The resulting composite electrode is cured by electron beam radiation. A polymer composite cathode is formed by coating a V 6 O 13 /carbon/polymer composite onto a nickel substrate and curing with electron beam radiation. The cured composite cathode is lithiated by electrochemical means and laminated onto the anode/electrolyte composite surface. The resulting electrochemical cell has an open circuit voltage of about 3 volts and can be cycled between that voltage and 0 volts repeatedly. Another embodiment of an electrochemical cell in accordance with the present invention utilizes the amorphous carbon/polymer composite electrode as both the anode and the cathode. The electrodes are prepared as described above and laminated with a polymer host network electrolyte therebetween. Prior to lamination, the electrode to be utilized as the anode is lithiated by electrochemical means. The resulting electrochemical cell has an open circuit voltage of about 1.5 volts and can be cycled between that voltage and 0 volts repeatedly. The invention will now be described with reference to the following example. Acetylene black (Chevron 100% compress) was dried in vacuum at 100°C for 48 hrs., to a level of water content smaller than 100 ppm. Sixty-two grams of propylene carbonate (PC) of high purity, containing less than 50 ppm of water, was put in a double planetary mixer under inert atmosphere. To this PC, 1.5 g of high molecular weight (MW = 900,000) polyethylene oxide (PEO) containing less than 50 ppm of water was added. The mixer content was then heated to 60°C under an inert atmosphere and stirred at 60 rpm. The PC/PEO mix was stirred for about 0.5 hrs. or until the PEO was completely dissolved. Then 14 g of polyethylene glycol diacrylate (PEGDA), having a MW of 400-600 and a water content less than 50 ppm, and 2.5 g of trimethylolpropane ethoxylate triacrylate (TMPEOTA) of high MW and of water content less than 50 ppm was added and stirred until the mixture is homogenous. To this homogenous mixture, 20 g of the predried carbon material was added. This composite anode precursor mix was stirred for 2 hrs. at 60°C under inert atmosphere so that the amorphous carbon particles became individually and homogeneously dispersed. Due to the nature of the carbon material, the viscosity of the composite anode precursor was higher than 10,000 cp at 75°C. The apparent density of the composite anode precursor was approximately 1.2 g/cm 2 . Approximately 100 mg of this composite anode precursor was coated as a thin (75-85 mm) uniform layer on a 10 cm 2 surface treated nickel current collector of 25 mm thickness. This anode precursor laminate is then either cured through exposure to an electron beam (1-9 Mrad) or overcoated with the polymer electrolyte precursor, then cured by the same means. A lithiated composite Li 8 V 6 O 13 , based cathode (1.5 mAh/cm 2 ) was mounted in front of the carbon based composite anode. The cell was discharged at current density of 100 mA/cm 2 . Approximately 1.4 mAh/cm 2 capacity was observed during the first charge of the carbon based composite anode. Subsequent to this first charge of the carbon composite anode, the anode was discharged at the same current density, and approximately 50-60% of the charge capacity was available. Further cycling shows capacity decrease similar to what was observed in Li/V 6 O 13 cells.

Claims: A carbon/polymer composite electrode comprising: a polymeric matrix; substantially amorphous carbon, namely carbon which is 80% or more non-crystalline or is microcrystalline in which 80% or more of the carbon microcrystals are in a random arrangement, homogeneously dispersed within and entrapped in said matrix; and, further contained in said matrix, an interpenetrating ionically conducting non-aqueous liquid comprising a solvent having an alkali metal salt dissolved therein. An electrode according to Claim 1, further characterised in that the substantially amorphous carbon is acetylene black or Shawinigan black. An electrode according to Claim 1 or 2, further characterised in that the solvent is a low volatility aprotic solvent. An electrode according to Claim 1, 2 or 3, further characterised in that the polymer is a conductive polymer. An electrode according to any preceding claim, further characterised in that the polymer is formed at least in part from polyethylene oxide monomers. An electrode according to any preceding claim, further characterised in that the solvent is selected from propylene carbonate, gamma-butyrolactone, 1,3-dioxolane, and 2-methyltetrahydrofuran. An electrode according to any preceding claim, further characterised in that the substantially amorphous carbon has a surface area greater than about 20m 2 /g. An electrode according to Claim 7, further characterised in that the substantially amorphous carbon has a surface area greater than about 50 m 2 /g. An electrode according to any preceding claim, further characterised in that the substantially amorphous carbon has a particle diameter of less than about 5mm. An electrode according to any preceding claim, further characterised in that the electrode contains intercalated lithium ions. An electrochemical cell comprising a cathode, a polymeric electrolyte and an anode comprising an electrode according to any of Claims 1 to 10. An electrochemical cell according to Claim 11, further characterised in that the cathode is a vanadium oxide composition containing intercalated lithium ions or LiCoO 2 .

Inventors: FAUTEUX DENIS, FAUTEUX, DENIS
Applicants: VALENCE TECHNOLOGY INC, VALENCE TECHNOLOGY, INC.
Application year: 1992
Main classification: H01M4
IPC codes: H01M4, H01M10