Olefin polymerization catalyst and olefin polymerization

Abstract: A solid catalyst for olefin polymerization comprising [A] a particulate carrier composed of (i) an oxide of at least one element selected from among those belonging to the groups of II, III and IV of the periodic table, and containing (ii) at least 1.0 % by weight of water, [B] an organoaluminum oxy compound, and [C] a transition metal compound of a metal belonging to the group IV B of the periodic table containing a ligand having a cyclopentadienyl skeleton, wherein the organoaluminum oxy compound [B] and the transition metal compound [C] are supported on the particulate carrier [A].

Description: This invention relates to a process for forming olefin polymerization catalysts and to an olefin polymerization processe, more particularly to a process for forming olefin polymerization catalysts capable of providing olefin polymers having excellent melt tension or excellent melt tension, broad molecular weight distribution and excellent moldability, as well as having high polymerization activity. Known catalysts for the preparation of α-olefin polymers, e.g. an ethylene polymer or ethylene/α-olefin copolymer, are titanium based catalysts composed of titanium compound and organoaluminum compounds, or vanadium based catalysts composed of vanadium compounds and organoaluminum compounds. Recently, novel Ziegler type catalysts composed of zirconium compounds and organoaluminum oxy compounds have been developed as catalysts for the preparation of ethylene/α-olefin copolymers, which have a high polymerization activity. Processes for the preparation of ethylene/α-olefin copolymers using these novel catalysts have been proposed, for example, in JP-A-19309/1983, JP-A-35005/1985, JP-A-35006/1985, JP-A-35006/1985, JP-A-35007/1985 and JP-A-35008/1985. These catalysts formed from transition metal compounds and organoaluminum oxy compounds as proposed in the prior art have excellent polymerization activity, especially ethylene polymerization activity, in comparison with the previously known catalysts formed from transition metal compounds and organoaluminum compounds. Nevertheless, the majority of these catalysts are soluble in the reaction system and, in most cases, processes for the preparation of ethylene/α-olefin copolymers using these novel catalysts are applicable only to solution polymerization. When it is intended to prepare polymers having a high molecular weight using these catalysts, there is an inconvenience of a markedly increased viscosity of the solution containing the resulting polymer, which reduces the productivity of the process, or there is a problem that it becomes difficult to obtain spherical olefin polymers having excellent particle characteristics. Attempts have been made to polymerize olefins in a suspension or vapor phase polymerization method using a catalyst composed of a transition metal compound and an organoaluminum oxy compound, at least one of the compounds being supported on a porous inorganic oxide carrier such as silica, alumina or silica alumina. For example, JP-A-35006/1985, JP-A-35007/1985 and JP-A-35008/1985 describe catalysts prepared by supporting transition metal compounds and organoaluminum oxy compounds on silica, alumina or silica alumina, which are useful in the preparation of ethylene/α-olefin copolymers. JP-A-106808/1985 and JP-A-106809/1985 disclose processes for the preparation of compositions containing polyethylene polymers and fillers, wherein ethylene is polymerized or ethylene and another α-olefin are copolymerized in the presence of a product previously obtained by contacting a highly active catalyst component containing a hydro-carbon-soluble titanium compound and/or zirconium compound with a filler, an organoaluminum compound and a filler which has affinity with polyolefins. JP-A-31404/1986 discloses a process for the polymerization of ethylene or copolymerization of ethylene and another α-olefin in the presence of a mixed catalyst comprising a product obtained by the reaction of a trialkylaluminum with water in the presence of silicon dioxide or aluminum oxide, and a transition metal compound. JP-A-276805/1986 discloses the polymerization of an olefin in the presence of a catalyst comprising a zirconium compound and a reaction mixture obtained by reacting a reaction mixture resulting from aluminoxane and a trialkylaluminum with an inorganic oxide having a surface hydroxyl group such as silica. JP-A-108610/1986 and JP-A-296008/1986 disclose processes for the polymerization of an olefin in the presence of a catalyst having a transition metal compound such as a metallocene and aluminoxane supported on a carrier such a an inorganic oxide. However, when olefins were polymerized or copolymerized in the suspension or vapor phase polymerization method in the presence of such solid catalyst components supported by carriers as mentioned above, the polymerization activity attained was very low in comparison with the above-mentioned solution polymerization, and the bulk density of the polymer formed was not sufficiently satisfactory. Further, the polymers formed are required to have various characteristics according to the process by which they are to be molded or to the purpose for which they are to be used. For example, when an inflation film is molded at a high speed from the polymer as formed, the polymer used must have a large melt tension considering its molecular weight in order to carry out a stable molding operation at a high speed without flickering or tearing the bubble. Similar characteristics are necessary for the polymer at the time of blow molding in order to prevent sagging or tearing-off of the polymer or at the time of T-die extrusion in order to keep the shortage in breadth of film to a minimum. The copolymers are required to have a narrow composition distribution when formed into film in order to prevent the film from being sticky. Further, if the polymer has a narrow molecular weight distribution, the molding conditions therefor are sometimes limited, and according to the purposes for which the molded products are used, olefin polymers having a broad molecular weight distribution are required. The solid catalyst components supported on the carriers proposed hitherto were found not to satisfy the above requirements. The present invention has been made in view of the problems of the prior art discussed above, and seeks to provide a process for forming olefin polymerization catalysts capable of producing olefin polymers having excellent melt tension and spherical olefin polymers having excellent particle characteristics and which have a high polymerization activity Moreover, the catalysts produced are capable of forming copolymers having a narrow composition distribution when two or more monomers are copolymerized or are capable of forming olefin polymers having the above-mentioned characteristics, a broad molecular weight distribution and excellent moldability. The present invention provides a process for forming a solid catalyst for olefin polymerization which comprises forming a mixture consisting essentially of [A] a particulate carrier composed of (i) an oxide of at least one element belonging to Group II, III or IV of the Periodic Table, and containing (ii) at least 1.0% by weight of water held by adsorption on the surface of the particulate carrier, [B] an organoaluminum oxy compound, [C] at least one transition metal compound of formula [II] ML x wherein M is a transition metal of IVB group, L is a ligand coordinating to the transition metal, at least one of L is a ligand having a cyclopentadienyl skeleton, L other than the ligand having a cyclopentadienyl skeleton is a hydrocarbon group of 1-12 carbon atoms, an alkoxy group, an aryloxy group, halogen, trialkylsilyl group, SO 3 R (wherein R is a hydrocarbon group of 1 to 8 carbon atoms which may have a substituent such as halogen), or hydrogen, and x is a valence of the transition metal and, optionally, [D] an organoaluminum compound of formula III or IV R 5 n AlX 3-n wherein R 5 is hydrocarbon of 1 to 12 carbon atoms, X is halogen or hydrogen, and n is 1 to 3, R 5 n AlY 3-n wherein R 5 is a hydrocarbon of 1 to 12 carbon atoms, Y is -OR 6 , -OSiR 7 3 , -OAlR 8 2 , -NR 9 2 , -SiR 10 3 , or -N(R 11 ) AlR 12 2 , n is 1 to 2, R6, R 7 , R 8 and R 12 are the same or different and are methyl, ethyl, isopropyl, isobutyl, cyclohexyl or phenyl, R 9 is hydrogen, methyl, ethyl, isopropyl, phenyl or trimethylsilyl, and R 10 and R 11 are the same or different and are methyl or ethyl such that [B] and [C] are supported on the carrier [A]. A prepolymerized catalyst for olefin polymerization may be formed according to the invention by forming a prepolymerized polyolefin on the solid catalyst. The present invention also provides a process for the polymerization of at least one olefin which comprises: a first step of forming a solid catalyst by a process as defined above; and a second step of polymerization of at least one olefin in the presence of the catalyst obtained. The organoaluminum compound [D] may or may not be supported on the particulate carrier [A]. The transition metal compound [C] may include at least two transition metal compounds of metals belonging to group IV of the periodic table. The polymerization process of olefins according to the invention is characterized by polymerizing or copolymerizing the olefins in the presence of the above-mentioned catalyst and, if necessary, the organoaluminum compound. Fig. 1 is a graph showing the relationship between the MFR and melt tension (MT) of the polymers obtained in Examples 1-8 and Comparative Example 1. In this figure, a numeral in a circular mark represents the number of the Example and a numeral in a square mark represents the number of the Comparative Example. Fig. 2 is a graph showing the relationship between the MFR and melt tension (MT) of the polymers obtained in Examples 9-14 and Comparative Example 2. In this figure, a numeral in a circular mark represents the number of the Example and a numeral in a square mark represents the number of the Comparative Example. In the present invention, the term "polymerization" includes not only homopolymerization but also copolymerization, and the term "polymer" includes not only homopolymer but also copolymer. The particulate carrier [A] (hereinafter sometimes called "component [A]") includes particulate inorganic compounds comprising an oxide of at least one element of groups II, III and IV of the Periodic Table. The particulate inorganic compounds mentioned above are preferably porous oxides, such as SiO 2 , Al 2 O 3 , MgO, ZrO 2 , TiO 2 , B 2 O 3 , CaO, ZnO, BaO and ThO 2 , or mixtures of porous oxides, for example SiO 2 -MgO, SiO 2 -Al 2 O 3 , SiO 2 -TiO 2 , SiO 2 -V 2 O 5 , SiO 2 -Cr 2 O 3 and SiO 2 -TiO 2 -MgO. Of these particulate inorganic compounds, preferred are those consisting essentially of at least one component selected from SiO 2 , Al 2 O 3 and MgO as a major component. The particulate carrier [A] desirably has an average particle diameter of 1-300 µm, preferably 10-200 µm, a specific surface area of 50-1000 m 2 /g, preferably 100-700 m 2 /g, and a pore volume of 0.3-2.5 m 3 /g. The particulate carrier [A] used in the present invention contains at least 1.0% by weight, preferably 1.2-20% by weight and especially 1.4-15% by weight of water. The water contained in the particulate carrier [A] is the water held by adsorption on the surface of the particulate carrier. The particulate carrier containing the specific amounts of water mentioned above may be obtained, for example, by the following procedures: (1) a carrier is held in moist air and allowed to undergo moisture adsorption until the moisture content of the carrier becomes the amount specified; (2) a carrier is held in moist air, allowed to undergo moisture adsorption and then dried until the moisture content of the carrier becomes the amount specified; (3) a specific amount of water is adsorbed on the surface of a thoroughly dried carrier. Concretely, in this procedure, the thoroughly dried carrier is stirred with the prescribed amount of water, water vapor, solution or suspension. In this case, the drying of the thus treated carrier at a temperature higher than 200°C usually attends elimination of the adsorbed water along with dehydration due to condensation of the surface hydroxyl groups. The determination of the water content of the particulate carrier may be carried out by the method of loss in weight on heating. The loss in weight of the particulate carrier obtained by drying the carrier under circulation of a dry vapor such as air or nitrogen at 200°C for 4 hours is taken to be the adsorbed water content of said carrier. By virtue of the use of such a particulate carrier containing a specific amount of water as mentioned above, it is possible to obtain olefin polymerization catalyst components capable of preparing olefin polymers having excellent melt tension at high polymerization activity The organoaluminum oxy compound [B] (hereinafter sometimes called "component [B]") may be an aluminoxane hitherto known or a benzene-insoluble organoaluminum oxy compound as exemplified in JP-A-78687/1990. The known aluminoxane may be prepared, for example, by the following methods: (1) suspensions of compounds containing adsorbed water or salts containing water of crystallization, for example magnesium chloride hydrate, copper sulfate hydrate, aluminum sulfate hydrate, nickel sulfate hydrate and ceriun (I) chloride hydrate, in hydrocarbon solvents are reacted with an organoaluminum compound such as a trialkylaluminum, and the desired aluminoxane is recovered in the form of a hydrocarbon solution; (2) an organoaluminum compound such as a trialkylaluminum is treated directly with water, ice or water vapor in a solvent such as benzene, toluene, ethyl ether or tetrahydrofuran, and the desired aluminoxane is recovered in the form of a hydrocarbon solution; (3) an organoaluminum compound such as a trialkylaluminum is reacted with an organotin oxide in a solvent such as decane, benzene or toluene. The aluminoxane as illustrated above may contain small amounts of organometallic components. From the above-mentioned solution containing aluminoxane as recovered, the solvent or unaltered organoaluminum compound is removed by distillation, and the remaining aluminoxane may be dissolved again in a solvent. The organoaluminum compound used in preparing the abovementioned solution of aluminoxane may be, for example, a trialkylaluminum trialkylaluminum such as trimethylaluminum, triethylaluminum, tripropylalminum, triisopropylaluminum, tri-n-butylaluminum, triisobutylaluminum, tri-sec-butylaluminum, tri-tert-butylaluminum, tripentylaluminum, trihexylaluminum, trioctylaluminum, tridecylaluminum, a tricycloalkylaluminum such as tricyclohexylaluminum or tricyclooctylaluminum; a dialkylaluminum halide such as dimethylaluminum chloride, diethylaluminum chloride, diethylaluminum bromide or diisobutylaluminum chloride; a dialkylaluminum hydride such as diethylaluminum hydride or diisobutylaluminum hydride; a dialkylaluminum alkoxide such as dimethylaluminum methoxide or diethylaluminum ethoxide; or a dialkylaluminum aryloxide such as diethylaluminum phenoxide. Of these, particularly preferred are trialkylaluminums. Furthermore, there may also be used as the organoaluminum compound isoprenylaluminum of formula [I]: (i-C 4 H 9 ) x Al y (C 5 H 10 ) z wherein x, y and z are each a positive number, and z ≥ 2x. The organoaluminum compounds mentioned above may be used-either singly or in combination. Solvents used in the solutions of the aluminoxane include aromatic hydrocarbons such as benzene, toluene, xylene, cumene and cymene; aliphatic hydrocarbons such as pentane, hexane, heptane, octane, decane, dodecane, hexadecane and octadecane; alicyclic hydrocarbons such as cyclopentane, cyclohexane, cyclooctane and methylcyclopentane; petroleum fractions such as gasoline, kerosene and gas oil; or haloganated hydrocarbons such as halides, particularly chloride and bromides, of the above-mentioned aromatic, aliphatic and alicyclic hydrocarbons. In addition thereto, there may also be used ethers such as ethyl ether and tetrahydrofuran. Of these solvents, particularly preferred are aromatic hydrocarbons. In the transition metal compound [C], the ligands having a cyclopentadienyl skeleton include, for example, cy- clopentadienyl, alkyl-substituted cyclopentadienyl groups such as methylcyclopentadienyl, dimethylcyclopentadienyl, trimethylcyclopentadienyl, tetramethylcyclopentadienyl, pentamethylcyclopentadienyl, ethylcyclopentadienyl, methyl-ethylcyclopentadienyl, propylcyclopentadienyl, methylpropylcyclopentadienyl, butylcyclopentadienyl, methylbutylcyclopentadienyl, hexylcyclopentadienyl, an indenyl group, a 4, 5, 6, 7-tetrahydroindenyl group and a fluorenyl group. These groups may be substituted by a halogen atom or a trialkylsilyl group. Of these ligands coordinating to the transition metal, the alkyl-substituted cyclopentadienyl groups are most preferred. When the compound represented by the formula [II] contains two or more ligands having a cyclopentadienyl skeleton, at least two ligands having a cyclopentadienyl skeleton may be bonded together via an alkylene group such as ethylene or propylene, an isopropylidene group, a substituted alkylene group such as diphenylmethylene, a silylene group or a substituted silylene group such as dimethylsilylene, diphenylsilylene or methylphenylsilylene. The ligand other than those having a cyclopentadienyl skeleton is a hydrocarbon group of 1-12 carbon atoms, an alkoxy group, an aryloxy group, halogen, trialkylsilyl group, SO 3 R, or hydrogen. The hydrocarbon group having 1-12 carbon atoms includes, for example, alkyl, cycloalkyl, aryl and aralkyl; the alkyl group includes methyl, ethyl, propyl, isopropyl, butyl and pentyl; the cycloalkyl group includes, for example, cyclopentyl and cyclohexyl; the aryl group includes, for example, phenyl and tolyl; and the aralkyl group includes, for example, benzyl and neophyl. The alkoxy group includes, for example, methoxy, ethoxy and butoxy. The aryloxy group includes, for example, phenoxy. The halogen includes, for example, fluorine, chlorine, bromine and iodine. The ligand represented by SO 3 R includes, for example, p-toluenesulfonate, methanesulfonate and trifluoromethanesulfonate. The transition metal M may have, for example, a valence of 4. The transition metal compound [C] may be represented more concretely by formula [II']: R 1 a R 2 b R 3 c R 4 d M wherein M is zirconium, titanium or hafnium, R 1 is a group having a cyclopentadienyl skeleton, R 2 , R 3 and R 4 are each a group having a cyclopentadienyl skeleton, an alkyl, cycloalkyl, aryl, aralkyl, alkoxy or aryloxy group, a halogen, a trialkylsilyl or SO 3 R group or hydrogen, a is an integer of at least 1, and a+b+c+d = 4. In the transition metal compounds of formula [II'], preferably at least one of R 2 , R 3 and R 4 has a cyclopentadienyl skeleton, that is, R 1 and R 2 are each a group having a cyclopentadienyl skeleton. These groups having a cyclopentadienyl skeleton may be bonded to each other via an alkylene group such as ethylene or propylene, a substituted alkylene group such as diphenylmethylene, an alkylidene group such as isopropylidene, a silylene group or a substituted silylene group such as dimethylsilylene, diphenylsilylene or methylphenylsilylene. R 3 and R 4 may also each be a group having a cyclopentadienyl skeleton, an alkyl, cycloalkyl, aryl, aralkyl, alkoxy or aryloxy group, a halogen, a trialkylsilyl or SO 3 R group or hydrogen. Typical representatives of the transition metal compounds [C] in which M is zirconium are: Bis(indenyl)zirconium dichloride, Bis(indenyl)zirconium dibromide, Bis (indenyl) zirconium bis(p-toluenesulfonate), Bis(4,5,6,7-tetrahydroindenyl)zirconium dichloride, Bis(fluorenyl)zirconium dichloride, Ethylenebis(indenyl)zirconium dichloride, Ethylenebis(indenyl)zirconium dibromide, Ethylenebis(indenyl)dimethyl zirconium, Ethylenebis(indenyl)diphenyl zirconium, Ethylenebis(indenyl)methyl zirconium monochloride, Ethylenebis(indenyl)zirconium bis(mehtanesulfonate), Ethylenebis(indenyl)zirconium bis(p-toluenesulfonate), Ethylenebis(indenyl)zirconium bis(trifluoromethanesulfonate), Ethylenebis(4,5,6,7-tetrahydroindenyl)zirconium dichloride, lsopropylidene(cyclopentadienyl-fluorenyl)zirconium dichloride, Isopropylidene(cyclopentadienyl-methylcyclopentadienyl) zirconium dichloride, Dimethylsilylenebis(cyclopentadienyl)zirconium dichloride, Dimethylsilylenebis(methylcyclopentadienyl)zirconium dichloride, Dimethylsilylenebis(dimethylcyclopentadienyl)zirconium dichloride, Dimethylsilylenebis(trimethylcyclopentadienyl)zirconium dichloride, Dimethylsilylenebis(indenyl)zirconium dichloride, Dimethylsilylenebis(indenyl)zirconium bis(trifluoromethanesulfonate), Dimethylsilylenebis(4,5,6,7-tetrahydroindenyl)zirconium dichloride, Dimethylsilylene(cyclopentadienyl-fluorenyl)zirconium dichloride, Diphenylsilylenebis(indenyl)zirconium dichloride, Methylphenylsilylenebis(indenyl)zirconium dichloride, Bis(cyclopentadienyl)zirconium dichloride, Bis(cyclopentadienyl)zirconium dibromide, Bis(cyclopentadienyl)methyl zirconium monochloride, Bis(cyclopentadienyl)ethyl zirconium monochloride, Bis(cyclopentadienyl)cyclohexyl zirconium monochloride, Bis(cyclopentadienyl)phenyl zirconium monochloride, Bis(cyclopentadienyl)benzyl zirconium monochloride, Bis(cyclopentadienyl)zirconium monochloride monohydride, Bis(cyclopentadienyl)methyl zirconium monohydride, Bis(cyclopentadienyl)dimethyl zirconium, Bis(cyclopentadienyl)diphenyl zirconium, Bis(cyclopentadienyl)dibenzyl zirconium, Bis(cyclopentadienyl)zirconium methoxy chloride, Bis(cyclopentadienyl)zirconium ethoxy chloride, Bis(cyclopentadienyl)zirconium bis(mehtanesulfonate), Bis(cyclopentadienyl)zirconium bis(p-toluenesulfonate), Bis(cyclopentadienyl)zirconium bis(trifluoromethanesulfonate), Bis(methylcyclopentadienyl)zirconium dichloride, Bis(dimethylcyclopentadienyl)zirconium dichloride, Bis(dimethylcyclopentadienyl)zirconium ethoxy chloride, Bis(dimethylcyclopentadienyl)zirconium bis(trifluoromethanesulfonate), Bis(ethylcyclopentadienyl)zirconium dichloride, Bis(methylethylcyclopentadienyl)zirconium dichloride, Bis(propylcyclopentadienyl)zirconium dichloride, Bis(methylpropylcyclopentadienyl)zirconium dichloride, Bis(buthylcyclopentadienyl)zirconium dichloride, Bis(methylbuthylcyclopentadienyl)zirconium dichloride, Bis(methylbuthylcyclopentadienyl)zirconium bis(mehtanesulfonate), Bis(trimethylcyclopentadienyl)zirconium dichloride, Bis(tetramethylcyclopentadienyl)zirconium dichloride, Bis(pentamethylcyclopentadienyl)zirconium dichloride, Bis(hexylcyclopentadienyl)zirconium dichloride, Bis(trimethylsilylcyclopentadienyl)zirconium dichloride In the above-mentioned transition metal compound, the di-substituted cyclopentadienyl groups include 1, 2- and 1,3-substituted groups, and the tri-substituted cyclopentadienyl groups include 1, 2, 3- and 1, 2, 4- substituted groups. Also the alkyl groups such as propyl and butyl include n-, i-, sec- and tert- isomers. There may also be used transition metal compounds obtained by replacing the zirconium metal in the above-exemplified zirconium compounds with titanium metal or hafnium metal. These transition metal compounds [C] may be used alone or in combination. When the transition metal compounds [C] are used in combination, it is preferred that at least one member selected from the group consisting of compounds (i) and (ii) as mentioned below is combined with at least one member selected from the group consisting of compounds (iii) and (iv) as mentioned below: (i) a transition metal compound containing two ligands having a cyclopentadienyl skeleton, in which the ligands are bonded together via, for example, a substituted or unsubstituted alkylene group or a substituted or unsubstituted silylene group (hereinafter referred to "bridge type transition metal compound"); (ii) a transition metal compound containing two ligands having a cyclopentadienyl skeleton, in which the ligands are not bonded to each other (hereinafter referred to "non-bridge type transition metal compound"), and the ligands have 2 to 5 substituents; (iii) a transition metal compound containing a ligand having a cyclopentadienyl skeleton, which is the non-bridge type transition metal compound, wherein the ligand has no substituent; (iv) a transition metal compound containing a ligand having a cyclopentadienyl skeleton, which is the non-bridge type transition metal compound, wherein the ligand has one substituent. Of the above combinations the most preferred is (ii) a non-bridge type transition metal compound containing ligands having a cyclopentadienyl skeleton, wherein the ligands have, particularly, 2 to 3 substituents, with (iv) a non-bridge type transition metal compound containing a ligand having a cyclopentadienyl skeleton, wherein the ligand has one substituent. When two compounds [C] are mixed, one compound is preferably used in an amount of from 5 to 95 mol%, more preferably 10 to 90 mol%, and most preferably 20 to 80 mol%. When three or more compounds [C] are mixed, the mixing ratio is not particularly limited, but one is preferably used in an amount of not more than 95 mol% and not less than 5 mol%. When at least two compounds [C] are used, an olefin polymer having a broad molecular weight distribution and excellent moldability can be obtained. The organoaluminum compound [D] (hereinafter referred to as "compound [D]") used in the present invention is of formula [III] or [IV]. In formula [III] R 5 is a hydrocarbon of 1 to 12 carbon atoms, for example alkyl, cycloalkyl or aryl, including concretely methyl, ethyl, n-propyl, isopropyl, isobutyl, pentyl, hexyl, octyl, cyclopentyl, cyclohexyl, phenyl and tolyl. The organoaluminum compounds of formula [III] include the compounds mentioned below: a trialkylaluminum such as trimethylaluminum, triethylaluminum, triisopropylaluminum, triisobutylaluminum, trioctylaluminum or tri-2-ethylhexylaluminum; an alkenylaluminum such as isoprenylaluminum; a dialkylaluminum halide such as dimethylaluminum chloride, diethylaluminum chloride, diisopropylaluminum chloride, diisobutylaluminum chloride or dimethylaluminum bromide; an alkylaluminum sesquihalide such as methylaluminum sesquichloride, ethylaluminum sesquichloride, isopropylaluminum sesquichloride, butylaluminum sesquichloride or ethylaluminum sesquibromide; an alkylaluminum dihalide such as methylaluminum dichloride, ethylaluminum dichloride, isopropylaluminum dichloride or ethylaluminum dibromide; and an alkylaluminum hydride such as diethylaluminum hydride or diisobutylaluminum hydride. The organoaluminum compounds of formula [IV] include the compounds mentioned below: (i) compounds of formula R 5 n Al(OR 6 ) 3-n such as dimethylaluminum methoxide, diethylaluminum ethoxide or diisobutylaluminum methoxide; (ii) compounds of formula R 5 n Al(OSiR 7 3 ) 3-n such as (C 2 H 5 ) 2 AlOSi(CH 3 ) 3 , (iso-C 4 H 9 ) 2 AlOSi (CH 3 ) 3 or (iso-C 4 H 9 ) 2 AlOSi(C 2 H 5 ) 3 ; (iii) compounds of formula R 5 n Al(OAlR 8 2 ) 3-n such as (C 2 H 5 ) 2 AlOAl(C 2 H 5 ) 2 or (iso-C 4 H 9 ) 2 AlOAl(iso-C 4 H 9 ) 2 ; (iv) compounds of formula R 5 n Al(NR 9 2 ) 3-n such as (CH 3 ) 2 AlN(C 2 H 5 ) 2 , (C 2 H 5 ) 2 AlNHCH 3 (CH 3 ) 2 AlNH(C 2 H 5 ), (C 2 H 5 ) 2 AlN(Si(CH 3 ) 3 ) 2 or (iso-C 4 H 9 ) 2 AlN(Si(CH 3 ) 3 ) 2 ; (v) compounds of formula R 5 n Al(SiR 10 3 ) 3-n such as (iso-C 4 H 9 ) 2 AlSi(CH 3 ) 3 ; and (vi) compounds of formula R 5 n Al(N(R 11 )AlR 12 2 ) 3-n such as (C 2 H 5 ) 2 AlN(CH 3 )Al(C 2 H 5 ) 2 or (iso-C 4 H 9 ) 2 AlN(C 2 H 5 )Al (iso-C 4 H 9 ) 2 . Of the organoaluminum compounds of formulae [III] and [IV], preferred are those of the formula R 5 3 Al, A 5 n Al (OR 6 ) 3-n or R 5 n Al(OAlR 8 2 ) 3-n , and particularly preferred are those in which R 5 is isoalkyl and n is 2. These organoaluminum compounds may be used alone or in combination. The olefin polymerization solid catalyst can be prepared by mixing the above-mentioned particulate carrier [A], the organoaluminum oxy-compound [B], the transition metal compound [C] and, if necessary, the organoaluminum compound [D], with or without an inactive hydrocarbon solvent. As the inert hydrocarbon solvent, there may be mentioned an aliphatic hydrocarbon, such as propane, butane, pentane, hexane, heptane, octane, decane, dodecane and kerosene; an alicycloic hydrocarbon, such as cyclopentane, cyclohexane and methylcyclohexane; an aromatic hydrocarbon, such as benzene, toluene and xylene; a halogenated hydrocarbon, such as ethylene chloride, chlorobenzene and dichloromethane; and a mixture thereof. Though the mixing of these compounds [A]-[D] may be conducted in an arbitrarily selected order, the mixing and contacting is preferably conducted as follows: the compound [A] and the compound [B] are mixed and contacted, followed by mixing and contacting the compound [C]; the compound [A] and the compound [B] are mixed and contacted, and compound [C] is mixed and contacted, followed by mixing and contacting the compound [D]; the compound [A] and the compound [B] are mixed and contacted, and compound [D] is mixed and contacted, followed by mixing and contacting the compound [C]; or the compound [A] and the compound [B] are mixed and contacted, followed by simultaneously mixing and contacting the compound [C] and compound [D], the compound [A] and the compound [B] are mixed and contacted, followed by mixing and contacting the premixture of the compound [C] and compound [D]. In the present invention, two or more compounds [C] may be used. When two or more the compounds [C] are used, these are preferably pre-mixed, and further, the mixing and contacting are conducted preferably under stirring. The temperature at mixing and contacting the compounds [A] to [D] is from -100 to 200°C, preferably -70 to 100°C. The order of the mixing the compound [A] and the compound [B] is arbitrarily selected, but it is preferred that the further components are gradually added over 5 minutes to 2 hours. The compound [A] and the compound [B] are mixed and contacted under the conditions mentioned above, and further mixing and contacting at -30 to 200°C, preferably 0 to 120°C, for 10 minutes to 10 hours, preferably 1 to 6 hours, followed by mixing and contacting the compound [C], if necessary, mixing and contacting the compound [D]. When the compounds [A], [B] and [C], and if necessary the compound [D] are mixed and contacted, the molecular ratio (H 2 O:Al) of the compounds [A] : [B] in terms of H 2 O of compound [A] to Al atom of the compound [B] is generally 0.02:1 to 0.8:1 preferably 0.05:1 to 0.6:1. The compound [C] is usually used in an amount of 10 -5 to 5x10 -3 mol, preferably 5x10 -5 to 10 -3 mol, based on 1g of the compound [A], and the concentration thereof is usually 10 -4 to 2x10 -2 mol/l, preferably 2x10 -4 to 10 -2 mol/l. The atomic ratio [Al:(transition metal)] of the aluminum in the compound [B] to the transition metal in the compound [C] is usually 10:1 to 3,000:1, preferably 20:1 to 2,000:1. The atomic ratio (Al D :Al B ) of the aluminum atoms (AID) in the compound [D] optionally used to the aluminum atoms (Al B ) in the compound [B] is usually 0.02:1 to 3:1, preferably 0.05:1 to 1.5:1. The compounds [A], [B] and [C], and if necessary the compound [D] are mixed at a temperature of usually -20 to 150°C, preferably 0 to 120°C, with a contact time of 1 to 300 minutes, preferably 5 to 200 minutes. The mixing temperature and contact time may be appropriately changed within the above ranges. In the solid catalyst for olefin polymerization obtained as described above, the transition metal is generally supported in an amount of 5x10 -6 to 10 -3 g atom, preferably 10 -5 to 3x10 -4 g atom, and aluminum is generally supported in an amount of 10 -3 to 10 -1 g atom, preferably 2x10 -3 to 5x10 -2 g atom, all the amounts being based on 1g of the compound [A]. The prepolymerized catalyst for olefin polymerization may also be prepared by mixing the compound [A], compound [B], the compound [C] and if necessary the compound [D], introducing olefin to the resulting mixture, and carrying out prepolymerization. The order of mixing the compounds [A], [B] and [C], and if necessary compound [D] is the same as for the olefin polymerization solid catalyst. In this instance, the compound [D] is further added during the polymerization. Further, in this prepolymerization, the same inactive solvent as used in the preparation of the olefin polymerization solid catalyst can be used. In the prepolymerization, the compound [C] is generally used in an amount of about 10 -5 to 2x10 -2 mol/l, preferably 5x10 -5 to 10 -2 mol/l. The prepolymerization is generally carried out at a temperature of -20 to 80°C, preferably 0 to 50°C, generally for 0.5 to 100 hours, preferably about 1 to 50 hours. Though the olefin used in the prepolymerization is selected from the olefin used in the polymerization, ethylene or a mixture of ethylene and an α-olefin is preferred. In the prepolymerized solid catalyst for olefin polymerization obtained as described above, the transition metal is generally supported in an amount of 5x10 -6 to 10 -3 g atom, preferably 10 -5 to 3x10 -4 g atom, and aluminum is generally supported in an amount of about 10 -3 to 10 -1 g atom, preferably 2x10 -3 to 5x10 -2 g atom, all the amounts being based on 1 g of the compound [A]. The amount of prepolymerized polyolefin produced in the prepolymerization is, based on 1 g of the compound [A], generally from about 0.1 to 500g, preferably 0.3 to 300g, particularly preferably 1 to 100g. The olefin polymerization catalyst may further contain useful compounds in addition to the above-mentioned compounds. The olefin is polymerized in the presence of the catalyst. The transition metal compound [C] is desirably used in an amount (per liter of the polymerization volume) of 10 -8 to 10 -3 g atom, preferably 10 -7 to 10 -4 g atom, in terms of the transition metal. In the polymerization, an organoaluminum compound and an aluminoxane may be used if necessary Examples of the organoaluminum compound used in the polymerization include compounds similar to the organoaluminum compound [D] described above. The organoaluminum compound is used in an amount of 0 to 500 moles, preferably 5 to 200 moles based on 1g atom of the transition metal. The olefins which can be polymerized include ethylene and olefins having 3 to 20 carbon atoms, for example, propylene, 1-butene, 1-pentene, 3-methyl-1-butene, 1-hexene, 4-methyl-1-pentene, 3-methyl-1-pentene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene, 1-eicosene, cyclopentene, cycloheptene, norbornene, 5-methyl-2-norbornene, tetracyclododecene and 2-methyl-1,4,5,8-dimethano-1,2,3,4,4a,5,8,8a-octahydronaphthalene. In addition, styrene, vinylcyclohexane and dienes may also be employed. The polymerization can be either a liquid phase polymerization such as suspension polymerization, or a gas phase polymerization. In the process for liquid phase polymerization, the same inactive hydrocarbon solvent as employed in the catalyst preparation can be used, and the olefin itself can also be used as a solvent. The olefin polymerization is carried out in the presence of the catalyst as described above for olefin polymerization, usually at a temperature of -50 to 150°C, preferably 0 to 100°C, and usually at a pressure of atmospheric pressure to 100kg/cm 2 (1kg/cm 2 = 98,1 kPa), preferably atmospheric pressure to 50kg/cm 2 . The polymerization reaction can be carried out either batch-wise, semicontinuously or continuously. Moreover, the polymerization may be carried out in two or more steps having different reaction conditions from each other. The molecular weight of the produced polyolefin can be adjusted either by introducing hydrogen into the polymerization system, or by changing the polymerization temperature. The olefin polymers obtained usually have an MFR, as measured according to ASTM D1238-65T at 190°C under a load of 2.16 kg, of 0.001-100 g/10 min. Further, the melt tension (MT) and MFR of the olefin polymers usually satisfy the relation: log Mt ≥ -0.66 log MFR + 0.5 The ethylene polymers prepared according to the present invention have excellent melt tension and favorable moldability. The melt tension is determined by measuring the stress of a molten polymer at the time when it is stretched at a prescribed speed. That is, the resulting polymer particles or pulverized products thereof are dissolved in decane, and the solution is poured in a methanol/acetone (1/1) solution in an amount of more than five times that of the decane to separate the polymer, which is then used as a test sample. Using the test sample, the measurement is conducted by means of a MT measuring device manufactured and sold by Toyo Seiki Seisakusho K.K. under the conditions of a resin temperature of 190°C, extrusion speed of 10 mm/min, take-up speed of 10-20 m/min, nozzle diameter of 2.09 mmØ and nozzle length of 8 mm. At the time of measuring the melt tension, the ethylene polymer has previously had incorporated 0.1 % by weight of 2,6-di-t-butylparacresol as a crosslinking stabilizer. When the olefin polymerization catalysts produced by the process of the present invention are used in the preparation of olefin polymers, the olefin polymers obtained have excellent melt tension, and there can be prepared spherical olefin polymers having excellent particle characteristics with a high polymerization activity. Furthermore, when catalysts comprising at least two transition metal compounds of metals belonging to the group IV of the periodic table and containing a ligand having a cyclopentadienyl skeleton are used, there can be obtained olefin polymers having the characteristics mentioned above and also having a broad molecular weight distribution, excellent melt tension and excellent moldability. The present invention is now further illustrated in the following Examples. Example 1 [Preparation of water adsorbed carrier] A quartz tube of 45 mm inside diameter placed in an electric furnace was charged with 150 g of silica (F-948, a product of Fuji Devison Co.), and the silica was dried under a nitrogen stream at 200°C for 4 hours and then at 700°C. Subsequently, a 500 ml egg-plant type flask was charged with 30 g of the dried silica obtained above, 1.8 ml of water was added and stirred with revolving for 1 hour. In this manner, there was obtained the water adsorbed silica. 20 g of the water adsorbed silica was dried under a nitrogen stream at 200°C for 4 hours, whereby a loss in weight of 1.14 g was observed. Accordingly, the amount of water of the water adsorbed silica amounts to 5.7 % by weight. [Preparation of catalyst component (A-1)] A nitrogen purged 400 ml glass flask was charged with 85 ml of toluene and 65.2 ml of an organoaluminum oxy compound (methylaluminoxane of Schelling Co. dried and then dissolved again in toluene; Al concentration: 1.15 gramatom/l), and the temperature of the system was lowered with stirring to 0°C. To this flask was added in a nitrogen atmosphere over a period of 30 minutes 9.0 g of the water adsorbed silica obtained above. Subsequently, reaction was carried out at 20-25°C for 1 hour and at 80°C for 3 hours. In this manner, there was obtained the catalyst component (A-1). [Preparation of solid catalyst (C-1)] To a nitrogen purged 400 ml glass flask charged with 150 ml of hexane were added with stirring 15 mg-atoms in terms of Al atom of the (A-1) obtained above and 0.06 mmols in terms of Zr atom of bis(cyclopentadienyl)zirconium dichloride, and the mixture was stirred at 30°C for 2 hours. As the result of this operation, there was obtained the solid catalyst (C-1) containing, based on 1 g of silica, 0.033 mg atom of Zr and 8.3 mg atom of Al. [Ethylene/1-butene copolymerization] In a thoroughly nitrogen-purged 2-liter stainless steel autoclave was placed 150 g of sodium chloride (a special grade of Wako Junyaku K.K.) followed by vacuum drying at 90°C for 1 hour. Thereafter, a mixed gas comprising 96.2 mol% of ethylene and 3.8 mol% of 1-butene was introduced into the autoclave to reduce the pressure inside the system to ordinary pressure and the temperature inside the system was decreased to 70°C. Subsequently, the autoclave was charged with 0.5 mmols of triisobutylaluminum and 0.015 mmols in terms of Zr atom of the solid catalyst (C-1) obtained above. Into the autoclave was introduced the above-mentioned mixed gas to carry out polymerization for 1 hour at a total pressure of 8 kg/cm 2 -G and 80°C. After the completion of the polymerization, unaltered sodium chloride was removed by water-washing, and the remaining polymer was washed with methanol, followed by vacuum drying at 80°C overnight. There was obtained 63.7 g of the copolymer. Physical properties of the thus obtained copolymer were measured. Results obtained are shown in Table 1. Example 2 [Preparation of water adsorbed carrier] The same procedure as in the preparation of water adsorbed carrier of Example 1 was repeated to obtain a water adsorbed silica, except that the amount of water added to 30 g of the dried silica was changed from 1.8 ml to 0.45 ml. In this case, the amount of the adsorbed water was 1.48 % by weight. [Preparation of catalyst component (A-2)] A nitrogen purged 400 ml glass flask was charged with 85 ml of toluene and 65.2 ml of an organoaluminum oxy compound (methylaluminoxane of Schelling Co. dried and then dissolved again in toluene; Al concentration: 1.15 gramatom/l), and the temperature of the system was decreased with stirring to 0°C. To the flask was added in a nitrogen atmosphere 9.0 g of the water adsorbed silica obtained above over a period of 30 minutes. Subsequently, reaction was carried out at 20 - 25°C for 1 hour and at 80°C for 3 hours. A supernatant of the reaction mixture was then removed by decantation and the remaining solid portion was rinsed and charged with 85 ml of toluene. In this manner there was obtained the catalyst component (A-2). [Preparation of solid catalyst (C-2)] To a nitrogen purged 400 ml glass flask charged with 150 ml of hexane, were added with stirring 15 mg-atoms in terms of Al atom of the (A-2) obtained above and 0.06 mmol in terms of Zr atom of bis(cyclopentadienyl)zirconium dichloride, followed by stirring at 30°C for 2 hours. As the result of this operation, there was obtained the solid catalyst (C-2) containing, based on 1 g of silica, 0.033 mg atom of Zr. and 6.6 mg atom of Al. [Ethylene/1-butene copolymerization] The same procedure of ethylene/1-butene copolymerization as in Example 1 was repeated except that in place of the solid catalyst (C-1), there was used the solid catalyst (C-2) obtained above. The polymer obtained thereby amounted to 59.9 g. Physical properties of the thus obtained polymer were measured. Results obtained are shown in Table 1. Comparative Example 1 [Preparation of solid catalyst (C-3)] A nitrogen purged 500 ml egg plant type flask was charged with 10 g of the dried silica obtained above (amount of adsorbed water: 0% by weight) and 145 ml of an organoaluminum oxy compound (methylaluminoxane of Schelling Co. dried and then dissolved again in toluene; Al concentration: 1.15 gram-atom/l), and held at room temperature for about 1 hour under reduced pressure until no liquid was observed. In this manner, an aluminoxane supported silica was obtained. Subsequently, to a nitrogen purged 400 ml glass flask charged with 100 ml of hexane, were added with stirring 40 mg-atom in terms of Al atom of the aluminoxane supported silica obtained above and 0.08 mmol in terms of Zr atom of bis(cyclopentadienyl) zirconium dichloride, and the mixture was vacuum dried with stirring at room temperature for 2 hours. As the result of this operation, there was obtained the solid catalyst (C-3) containing, based on 1 g of silica, 0.033 mg atom of Zr and 16.6 mg atom of Al. [Ethylene/1-butene copolymerization] The same procedure of ethylene/1-butene copolymerization as in Example 1 was repeated except that in place of the catalyst (C-1), there was used 0.015 mmol in terms of Zr atom of the solid catalyst (C-3) obtained above. The copolymer thus obtained amounted to 52.2 g. Physical properties of the thus obtained copolymer were measured. Results obtained are shown in Table 1. Example 3 A solid catalyst (C-4) was obtained by repeating Example 1 except that in place of the bis(cyclopentadienyl) zirconium dichloride used as the transition metal compound, there was used ethylenebis (indenyl)zirconium dichloride. [Ethylene/1-butene copolymerization] The same procedure of ethylene/1-butene copolymerization as in Example 1 was carried out except that in place of 0.015 mmol of the solid catalyst (C-1) there was used 0.003 mmol in terms of Zr atom of the solid catalyst (C-4), and 50 ml of hydrogen was added to the polymerization system. The copolymer thus obtained amounted to 25.3 g. Physical properties of the thus obtained copolymer were measured. Results obtained are shown in Table 1. Example 4 A nitrogen purged 1-liter glass polymerizer was charged with 1 liter of purified n-decane, and the temperature inside the polymerizer was elevated up to 70°C while passing therethrough ethylene at a rate of 250 l/hr and hydrogen at a rate of 2 l/hr. Subsequently, 0.02 mmol in terms of Zr atom of the solid catalyst (C-4) obtained in Example 3 was added to the reaction system, and the system was maintained at 75°C to carry out suspension polymerization of ethylene at ordinary pressure for 2 hours. The polymer thus obtained amounted to 24.7 g. Physical properties of the thus obtained polymer were measured. Results obtained are shown in Table 1. Example 5 A solid catalyst (C-5) was obtained by repeating Example 1 except that there were used a water adsorbed silica having 5.71% by weight of adsorbed water and ethylenebis(indenyl) zirconium dichloride as the transition metal compound. Subsequently, suspension polymerization of ethylene at ordinary pressure was carried out in the same manner as in Example 4 except that in place of the solid catalyst (C-4), there was used the solid catalyst (C-5) obtained above, and the flow rate of hydrogen was changed from 2 l/hr to 0.5 l/hr. The polymer obtained amounted to 45.7 g. Physical properties of the thus obtained polymer were measured. Results obtained are shown in Table 1. Examples 6 and 7 Suspension polymerization of ethylene at ordinary pressure was carried out using the solid catalyst (C-5) obtained in Example 5 and varying the flow rate of hydrogen as shown in Table 1. The polymers obtained amounted to 50.7 g and 40.9 g, respectively,. Physical properties of the thus obtained polymers were measured. Results obtained are shown in Table 1. Example 8 A solid catalyst (C-6) was obtained by repeating Example 1 except that there were used a water adsorbed silica having 1.46 % by weight of adsorbed water, and bis(trimethylsilylpentadienyl)zirconium dichloride as the transition metal compound. Subsequently, suspension polymerization of ethylene at ordinary pressure was carried out in the same manner as in Example 4 except that there was used the solid catalyst (C-6) obtained above, and the flow rate of hydrogen was changed from 2 l/hr to 0.15 l/hr. The polymer obtained amounted to 11.0 g. Physical properties of the thus obtained polymer were measured. Results obtained are shown in Table 1. Table 2 shows the composition of the catalysts used in the foregoing examples and comparative example. The relationship between the MFR and melt tension (MT) of the polymers obtained in Examples 1-8 and Comparative Example 1 is shown in Fig. 1. The melt tension of polymers obtained by means of the same catalyst varies relative to the MFR in the manner of straight line as shown in Fig. 1. As can be seen from Fig. 1, the melt tension of every polymer obtained in the Examples is markedly higher than that of the polymer of the Comparative Example. Example 9 [Preparation of water adsorbed carrier] A quartz tube of 45 mm inside diameter placed in an electric furnace was charged with 100 g of silica (F-948, a product of Fuji Devison Co.), and the silica was dried under a nitrogen stream at 200°C for 4 hours and then at 700°C for 7 hours. Subsequently, a 500 ml egg plant type flask was charged with 50 g of the dried silica obtained above, 0.9 ml of water was added and stirred with revolving for 1 hour. In this manner, there was obtained a water adsorbed silica. 20 g of the water adsorbed silica was dried under a nitrogen stream at 200°C for 4 hours, whereby a loss in weight of 0.59 g was observed. Accordingly, the amount of water contained in the water adsorbed silica was 2.95% by weight. [Preparation of catalyst component (A-3] A nitrogen purged 400 ml glass flask was charged with 85 ml of toluene and 65.2 ml of an organoaluminum oxy compound (methylaluminoxane of Schelling Co. dried and then dissolved again in toluene; Al concentration: 1.15 gramatom/l), and the temperature of the system was decreased with stirring to 0°C. To the flask was added in a nitrogen atmosphere 9.0 g of the water adsorbed silica obtained above over a period of 30 minutes. Subsequently, reaction was carried out at 20 - 25°C for 1 hour and at 80°C for 3 hours. In this manner, there was obtained the catalyst component (A-3). [Preparation of prepolymerization catalyst (C-7)] To a nitrogen purged 400 ml glass flask charged with 153 ml of hexane were added with stirring 15 mg-atoms in terms of Al atom of the above-mentioned (A-3), 0.3 mmol in terms of Zr atom of bis(cyclopentadienyl)zirconium dichloride and 1.5 mmol of triisobutylaluminum, and ethylene gas (ordinary pressure) was continuously introduced into the flask to carry out prepolymerization at 30°C for 2 hours. As the result of this operation, there was obtained the prepolymerization catalyst (C-7) containing, based on 1 g of silica, 0.17 mg atom of zirconium, 8.3 mg atom of aluminum and 7.5 g of polyethylene. [Polymerization] To a nitrogen purged 2-liter stainless steel autoclave was fed 150 g of sodium chloride (special grade of Wako Junyaku K.K.) followed by vacuum drying at 90°C for 1 hour. Thereafter, a mixed gas comprising 94.3 mol% of ethylene and 5.7 mol% of 1-butene was introduced into the autoclave to bring the pressure inside the autoclave to ordinary pressure, and the temperature of the system was lowered to 70°C. Subsequently, the autoclave was charged with 0.5 mmol of triisobutylaluminum and 0.01 mmol in terms of Zr atom of the prepolymerization catalyst (C-7). Thereafter, the above-mentioned mixed gas was introduced into the autoclave to carry out polymerization at a total pressure of 8 kg/cm 2 -G and 80°C for 1 hour. After the completion of the polymerization, the reaction mixture was washed with water to remove the sodium chloride therefrom, and the remaining polymer was washed with methanol followed by vacuum drying at 80°C overnight. The polymer obtained amounted to 68.4 g. Physical properties of the thus-obtained polymer were measured. Results obtained are shown in Table 3. Comparative Example 2 [Preparation of prepolymerization catalyst (C-8)] The prepolymerization catalyst (C-8) containing, based on 1 g of silica, 0.12 mg atom of zirconium, 5.9 mg atom of aluminum and 7.5 g of polyethylene was obtained by the same procedure as described in the preparation of (A-3) of Example 9 except that in place of the water adsorbed silica, there was used the dried silica (amount of adsorbed water: 0% by weight). [Polymerization] The same ethylene/1-butene copolymerization as in Example 9 was carried out except that in place of the prepolymerization catalyst (C-7) used in Example 9, there was used 0.02mg atom in terms of zirconium atom of the prepolymerization catalyst (C-8). The polymer obtained amounted 71.5 g. Physical properties of the thus-obtained polymer were measured. Results obtained are shown in Table 3. Example 10 A prepolymerization catalyst (C-9) was prepared by the same procedure as in Example 9 except that there were used the water adsorbed silica having 2.80 % by weight of water and bis(methylcyclopentadienyl)zirconium dichloride as the transition metal compound component. The same ethylene/1-butene copolymerization as in Example 9 was carried out. The copolymer obtained amounted to 84.4 g. Physical properties of the thus-obtained copolymer were measured. Results obtained are shown in Table 3. Example 11 A prepolymerization catalyst (C-10) was obtained by the same procedure as in Example 9 except that there were used the water adsorbed silica having 1.51 % by weight of adsorbed water obtained by using the silica dried at 200°C for 4 hours and bis(1,3-dimethylcyclopentadienyl)zirconium dichloride as the transition metal compound component. Subsequently, the same ethylene/1-butene copolymerization as in Example 9 except that 50 ml of hydrogen was allowed to co-exist with ethylene and 1-butene. The copolymer obtained amounted 39.3 g. Physical properties of the thus-obtained copolymer were measured. Results obtained are shown in Table 3. Examples 12 and 13 Copolymerization of ethylene and 1 -butene was carried out using the prepolymerization catalyst (C-10) obtained in Example 11 and varying the amount of hydrogen to be added as shown in Table 3. The copolymers obtained amounted to 50.5 g and 32.7 g, respectively. Example 14 A prepolymerization catalyst (C-11) was prepared by the same procedure as in Example 9 except that there were used the water adsorbed silica having 5.72 % by weight of adsorbed water and ethylenenbis(indenyl)zirconium dichloride as the transition metal compound component. The copolymer obtained amounted to 40.6 g. Physical properties of the thus-obtained copolymer were measured. Results obtained are shown in Table 3. Table 4 shows the component compositions of the catalysts used in the foregoing examples and comparative example. The relationship between the MFR and melt tension (MT) of the polymers obtained in Examples 9 - 14 and Comparative Example 2 is shown in Fig. 2. The melt tension of polymers obtained by means of the same catalyst varies relative to the MFR in the manner of a straight line as shown in Fig. 2. As can be seen from Fig. 2, the melt tension of every polymer obtained in the Examples is markedly higher than that of the polymer of the Comparative Example. Example 15 [Preparation of water adsorbed carrier] A quartz tube of 45 mm inside diameter placed in an electric furnace was charged with 150 g of silica (F-948, a product of Fuji Devison Co.), and the silica was dried under nitrogen stream at 200°C for 4 hours and then at 700°C for 7 hours. Subsequently, a 500 ml egg plant type flask was charged with 30 g of the dried silica obtained above, 1.6 ml of water was added and stirred with revolving for 1 hour. In this manner, there was obtained a water adsorbed silica. 20g of the water adsorbed silica was dried under a nitrogen stream at 200°C for 4 hours, whereby a loss in weight of 1.00 g was observed. Accordingly, the amount of water contained in the water adsorbed silica was 5.00 % by weight. [Preparation of catalyst component (A-4)] A nitrogen purged 400 ml glass flask was charged with 85 ml of toluene and 65.2 ml of an organoaluminum oxy compound (methylaluminoxane of Schelling Co. dried and then dissolved again in toluene; Al concentration: 1.15 gram atom/1), and the temperature of the system was decreased with stirring to 0°C. To the flask was added in a nitrogen atmosphere 9.0 g of the water adsorbed silica obtained above over a period of 30 minutes. Subsequently, reaction was carried out at 20 - 25°C for 1 hour and at 80°C for 3 hours. In this manner, there was obtained the catalyst component (A-4). [Preparation of solid catalyst (C-12)] To a nitrogen purged 400 ml glass flask charged with 150 ml of hexane were added with stirring 15 mg atom in terms of Al atom of the (A-4) obtained above, 0.02 mmol of bis(n-propylcyclopentadienyl)zirconium dichloride and 0.04 mmol of bis (1,3-dimethylcyclopentadienyl) zirconium dichloride, followed by stirring at 30°C for 2 hours. As the result of this operation, there was obtained the solid catalyst (C-12) containing, based on 1 g of silica, 0.035 mg atom of zirconium and 8.8 mg atom of aluminum. [Suspension polymerization of ethylene at ordinary pressure] A nitrogen purged 1-liter glass reactor was charged with 1 liter of purified n-decane and 0.5 mmol of triisobutylaluminum, and the temperature of the system was elevated up to 70°C while passing therethrough ethylene at a rate of 250 l/hr and hydrogen at a rate of 0.2 l/hr. Subsequently, 0.02 mmol in terms of Zr atom of the solid catalyst (C-12) obtained above, and the system was maintained at 75°C to carry out suspension polymerization of ethylene at ordinary pressure for 2 hours. The polymer obtained thereby amounted to 60.5 g. The polymerization activity in this case corresponds to 3030 g-PE/mmol-Zr. The thus obtained polymer had MFR of 0.8 g/10 min, Mw/Mn of 4.4 and a melt tension of 6.5 g. Example 16 [Preparation of water adsorbed carrier] The water adsorbed carrier was obtained by repeating the same procedure as described in Example 15. [Preparation of catalyst component (A-5)] A nitrogen purged 400 ml glass flask was charged with 85 ml of toluene and 65.2 ml of an organoaluminum oxy compound (methylaluminoxane of Schelling Co. dried and then dissolved again in toluene; Al concentration: 1.15 gram atom/l), and the temperature of the system was decreased with stirring to 0°C. To the flask was added in a nitrogen atmosphere 9.0 g of the water adsorbed silica obtained above over a period of 30 minutes. Subsequently, reaction was carried out at 20 - 25°C for 1 hour and at 80°C for 3 hours. In this manner, there was obtained the catalyst component (A-5). [Preparation of prepolymerization catalyst (C-13)] To a nitrogen purged 400 ml glass flask charged with 150 ml of hexane was added with stirring 15 mg atom in terms of Al atom of the (A-5) obtained above, 0.02 mmol of bis(n-propylcyclopentadienyl)zirconium dichloride, 0.04 mmol of bis(1,3-dimethylcyclopentadienyl)zirconium dichloride and 1.5 mmol of triisobutylaluminum, and ethylene gas (ordinary pressure) was continuously introduced into the flask to carry out prepolymerization at 30°C for 2 hours. As the result of this operation, there was obtained the prepolymerization catalyst (C-13) containing, based on 1 g of silica, 0.033 mg atom of zirconium, 9.0 mg atom of aluminum and 6.9 g of polyethylene. [Suspension polymerization of ethylene at ordinary pressure] A nitrogen purged 1-liter glass polymerizer was charged with 1 liter of purified n-decane and 0.5 mmol of triisobutylaluminum, and the temperature of the system was elevated up to 70°C awhile passing therethrough ethylene at a rate of 250 l/hr and hydrogen at a rate of 0.15 l/hr. Subsequently, 0.02 mmol in terms of Zr atom of the prepolymerization catalyst (C-13) obtained above, and the system was maintained at 75°C to carry suspension polymerization of ethylene at ordinary pressure for 2 hours. The polymer obtained thereby amounted to 72.2 g. The polymerization activity in this case corresponds to 3610 g-PE/mmol-Zr. The polymer thus obtained had MFR of 0.65 g/10 min, Mw/Mn of 4.2 and a melt tension of 7 g.

Claims: A process for forming a solid catalyst for olefin polymerization which comprises forming a mixture consisting essentially of [A] a particulate carrier composed of (i) an oxide of at least one element belonging to Group II, III or IV of the Periodic Table, and containing (ii) at least 1.0% by weight of water held by adsorption on the surface of the particulate carrier, [B] a pre-prepared organoaluminum oxy compound, [C] at least one transition metal compound of formula [II] ML x wherein M is a transition metal of IVB group, L is a ligand coordinating to the transition metal, at least one of L is a ligand having a cyclopentadienyl skeleton, L other than the ligand having a cyclopentadienyl skeleton is a hydrocarbon group of 1-12 carbon atoms, an alkoxy group, an aryloxy group, halogen, trialkylsilyl group, SO 3 R (wherein R is a hydrocarbon group of 1 to 8 carbon atoms which may have a substituent such as halogen), or hydrogen, and x is a valence of the transition metal, and, optionally, [D] an organoaluminium compound of formula III or IV R 5 n AlX 3-n wherein R 5 is hydrocarbon of 1 to 12 carbon atoms, X is halogen or hydrogen, and n is 1 to 3, R 5 n AlY 3-n wherein R 5 is a hydrocarbon of 1 to 12 carbon atoms, Y is -OR 6 , -OSiR 7 3 , -OAlR 8 2 , -NR 9 2 , -SiR 10 3 , or -N(R 11 ) AlR 12 2 , n is 1 to 2, R 6 , R 7 , R 8 and R 12 are the same or different and are methyl, ethyl, isopropyl, isobutyl, cyclohexyl or phenyl, R 9 is hydrogen, methyl, ethyl, isopropyl, phenyl or trimethylsilyl, and R 10 and R 11 are the same or different and are methyl or ethyl, such that [B] and [C] are supported on the carrier [A], which process comprises mixing components [A], [B] [C] and optionally [D]. A process according to claim 1 wherein [C] comprises at least two transition metal compounds. A process according to claim 1 or 2 wherein said organoaluminum compound [D] is supported on the particulate carrier [A]. A process according to any one of the preceding claims which further comprises forming a prepolymerized polyolefin on the solid catalyst as defined in any one of the preceding claims to form a prepolymerized catalyst. A process for the polymerization of at least one olefin which comprises: a first step of forming a solid catalyst by a process as defined in any one of the preceding claims; and a second step of polymerization of at least one olefin in the presence of the catalyst obtained. A process according to claim 5 wherein the polymerization is carried out in the presence of (i) a prepolymerized catalyst as defined in claim 4 which does not contain an organoaluminum compound (D), and (ii) an organoanluminum compound. A process according to claim 5 wherein the polymerization is carried out in the presence of (i) a prepolymerized catalyst as defined in claim 4 which contains an organoaluminum compound (D), and (ii) an organoaluminum compound.

Inventors: OKAWA KAZUNORI, UEDA TAKASHI, OKAWA, KAZUNORI, UEDA, TAKASHI, Okawa, Kazunori, c/o MITSUI PETROCHEM. IND., LTD., Ueda, Takashi, c/o MITSUI PETROCHEM. IND., LTD.
Applicants: MITSUI CHEMICALS INC, MITSUI CHEMICALS, INC.
Application year: 1992
Main classification: C08F10
IPC codes: C08F110, C08F4, C08F10, C08F210