Hydrogel material

Abstract: A polymeric composition suitable for use in ophthalmic devices such as contact lenses, intraocular lenses and other medical and non-medical devices which composition comprises a copolymer that incorporates repeating units containing a solvolyzable group and various desired hydrophilic repeating units in predetermined ratios, which copolymer is mechanically stable and upon hydration the dimensions of polymeric articles which as formed therefrom can be controlled. In particular, the hydrophilic compositions resulting from the invention are useful in applications where stresses and distortions of the polymer article due to water absorption etc must be minimized or, if possible, eliminated.

Description: This invention relates to polymer articles and to controlling dimensional changes in such articles, for example, ophthalmic devices and other suitable medical and non medical devices. In particular, this invention relates to polymer articles in which at least a portion of the article is formed from copolymers containing solvolyzable bulky leaving groups, which copolymers upon solvolysis and hydration yield a hydrogel with a controllable dimensional change on removal of the leaving groups. In return, this enables the minimisation of time stresses and deformations in the polymer article during, and resulting from, hydration. In a second aspect, this invention relates to soft contact lenses and includes lenses having a relatively harder oxygen permeable center portion and a soft hydrophilic peripheral skirt formed from the hydrogels of the present invention. Hydrogels are polymeric materials which are used in the manufacture of medical devices such as soft contact lenses, intraocular lenses, etc. These polymers expand considerably from their xerogel state during hydration. The change in total volume of a polymer article made from the copolymer during water absorption (hydration) depends on the nature and hydrophilicity of the monomers/polymers of the copolymer. In the manufacture of articles requiring exact parameters, such as contact lenses and intraocular lenses, the swelling of the article during hydration can become a serious problem. This is because accurate production requires reasonably precise predictability of the dimensional swelling in order to set the manufacturing parameters. Also the swelling produces distortions and stresses in the hydrated polymer matrix, and hence the article. In fact, substantial residual stresses and the resulting distortions can make the material unacceptable for its intended use. In the production of contact lenses etc, it is unusual to shape the product to its final form from the hydrated hydrogel due to production difficulties. In fact, it is simpler to machine or cast the product in the xerogel state. Now, as the article is to be used in an hydrated state the swelling during hydration of the polymer must also be accounted for in considering the dimensions of an article which is to be produced from the polymer in the non-hydrated or xerogel state. Further if there are any variations in the degree of swelling from batch to batch or within a batch of material, the product will not be manufactured to the desired final dimensions. This may happen in the absence of changes in total water uptake if the ratio of the extent of swelling in the x, y or z directions changes in a fashion which compensates for the total volume increase. Also at times there is a definite need to prepare materials from hydrogels that do not show any change in the volume during hydration. For example, USP 4093361 describes the preparation of a hydrogel with no net swelling during hydration. In this case the monomer was polymerized in the presence of a non-reactive water soluble neutral filler material. After polymerization was complete the neutral filler was washed out with a solvent, thereby leaving the final dimensions of the hydrogels articles unchanged. However, polymers made in this way suffer the disadvantage that parameters such as hardness become unsatisfactory and the mechanical properties (e.g. modulus, tear strength, max. elongation) of the resulting product are no longer optimum. Furthermore, there can be a need to change tne surface characteristics of hydrogels through surface treatments of the polymer in the xerogel state. Substantial volume changes in the hydrogel during hydration can render these surface modifications useless due to the development of cracks and fissures in the surface. In Chemical Patents Index, Basic Abstracts Journal, Derwent Publications Ltd, December 1990, Class A, page 368, AN 91-024932/04 (JP-A-2293817) there is disclosed an oxygen-permeable contact lens which comprises a copolymer of an unsaturated dicarboxylic acid diester monomer. EP-A-0294515 discloses a contact lens material composed of a copolymer of a monomer mixture comprising, as essential monomers, from 5 to 20 parts by weight, based on 100 parts by weight of the total monomer mixture, of a hydrophilic monomer consisting of from 40 to 60 mol% of N-vinyl-2-pyrrolidone and from 40 to 60 mol% of methacrylic acid and from 30 to 95 parts by weight, based on 100 parts by weight of the total monomer mixture, of at least one of a silicon-containing acrylate and a silicon-containing methacrylate. It is an object of the present invention to provide polymer articles constructed at least in part from a co-polymer material which contains solvolyzable bulky leaving groups, and which yields after solvolysis and hydration, hydrogels which have undergone a selected and controlled volume change. Preferred solvolyzable polymers are made from acrylate, methacrylate and vinyl monomers incorporating large leaving groups such as trifluoroacetyl, trichloroacetyl and trimethylsilyl. The co-polymer articles of the present invention exhibit controlled dimensional changes after polymerization and hydration which enables substantial stress and distortion in articles made therefrom to be avoided. A further objective of the present invention is to provide contact lens made in whole, or in part, from novel polymer compositions which are soft and hydrophilic in nature and which after hydration exhibit excellent properties including high strength, no deterioration with time, relatively slow release of hydrated water upon exposure to air, good optical characteristics and which can be easily formed into contact lenses. The present invention provides a polymer article at least a portion of which comprises a solvolysed and hydrated hydrogel which contains water in the range 5 to 95% by weight, which hydrogel is formed from a co-polymer which incorporates ester linking groups which are capable of cleaving into a carboxy containing group and an alcohol in the presence of a nucleophile such as water or a weak base or in the presence of a C 1 - C 4 alcohol, and which can be solvolyzed and hydrated to a hydrogel, and which on solvolysis and hydration undergoes a volume change ranging from a shrinkage of 20% up to an expansion of 40%, the said co-polymer being formed from: (a) two or more monomers selected from a first group I of monomers, each of which monomers having an ethylenically unsaturated group and each of said monomers further having one or more substitutable leaving groups which can be removed by solvolysis wherein said substitutable leaving groups for each of said monomers are different from each other; and (b) one or more monomers selected from a second group II of monomers, each of which monomers is an ethylenically unsaturated monomer without such substitutable leaving groups; the quantity by weight of monomers present in the polymer being chosen so that the quantity of monomers of the first group I of monomers is in the range from 5 to 95% by weight of the co-polymer and the quantity of monomers of the second group II of monomers is from 5 to 95% by weight of the co-polymer. As used in this application "solvolyzable" means an ester linking group capable of cleaving into a carboxy containing compound for example, amide, ester or acid and an alcohol in the presence of a nucleophile, for example, water or a weak base, for example, ammonia or organic amine or in the presence of a lower C 1 to C 4 alcohol. We prefer to form the polymer articles of the invention at least partially from a co-polymer in which the monomers of the first group are selected from monomers of the general formula shown below: CH 2 =C(R 1 )-Y-R x L where R 1 = -H, -alkyl and -substituted alkyl groups, R x L ; Y = -(CH 2 ) k -, -(Ar)- or -substituted (Ar)-, -COO(CP 2 ) j -(CR 2 R 3 ) m -(CP 2 ) n -, where Ar is an aromatic group; P = -H, -alkyl and -substituted alkyl groups, halo (chloro, bromo, iodo) groups, -(Ar) or -substituted (Ar); R 2 , R 3 = -H, -CH 3 , or -OCO(CP 2 ) j -CH 3 ; R x L = -OCOCF 3 , -OCOCCl 3 , -OCOCBr 3 , -O-Si[(CP 2 ) k -CP 3 ] 3 , -OSO 3 -CH 3 , -OSO 3 -Ar-CH 3 ; k = 1-16, preferred values for k are 1-6; j, m, n are 0 or an integer from 1 to 16 with the proviso that j + m + n = 2-16; preferred values for j, m, n are 0-6. The synthesis of monomers with k, j, m, n > 16 results in hydrogels with undesirable properties. Further, x is functionally dependent on Y; for example when Y is difunctional [-CH 2 -], x = 1; when Y is trifunctional aromatic (Ar), x = 2. Other suitable monomers of the first group which can be suitably modified by solvolysis, in these cases to give alcohols or diols, include monomers which include the following groups: Chloroacetyl, dichloroacetyl, trichloroacetyl, fluoroacetyl, methoxyacetyl, triphenylmethoxyacetyl, phenoxyacetyl, silyl ethers such as trimethysilyl, triethylsilyl, isopropyldimethylsilyl, t-butyldimethylsilyl, methyldiisopropylsilyl, tribenzylsilyl, triphenylsilyl, cyclic acetals and ketals incorporating methylene, ethyledene, 2,2,2-trichloroethyledene groups; cyclic orthoesters formed from methoxy methylene, ethoxymethylene, 1-(N,N-dimethylamino)ethyledene derivatives, 1-(N,N-dimethylamino)benzylidene derivatives, and methanesulfonate and toluenesulfonates. Examples of suitable combinations of monomers of the first group I of monomers are:- 1,3-bis-(trichloroacetoxy)propyl -2-methacrylate and 1,3-bis-(trifluoroacetoxy)propyl -2-methacrylate; 1,3-bis-(trimethylsilyl)propyl -2-methacrylate and 1,3-bis-(trifluoroacetoxy)propyl-2-methacrylate; 1,3-bis-(t-butyldimethylsilyl)propyl-2-methacrylate and 1,3-bis-(trifluoroacetoxy)propyl-2-methacrylate; 1,3-bis-(trichloroacetoxy)propyl-2-methacrylate and methyl -α-(trifluoroacetoxy)acrylate; (2'-trifluroacetoxy)ethyl methacrylate and methyl-α- (trifluoroacetoxy)acrylate; and (2'-trichloroacetoxy)ethyl methacrylate and methyl-α-(trifluoroacetoxy)acrylate. Examples of suitable monomers of the second group II of monomers are methyl methacrylate (MMA), trifluoromethylmethacrylate (TFMMA), hydroxymethyl methacrylate (HMMA), 2', 2', 2'-trifluoroethyl methacrylate (TFEMA), hydroxyethyl methacrylate (HEMA) and dimethyl acrylamide (DMA). Preferably, the ratio of the quantity by weight of the monomers of groups I and II ranges from 19:1 to 1:19. The preferred monomers of the first group may be produced by the synthesis shown below by the reaction schemes: The trichloroacetate ester of glyceryl methacrylate (HCE-GMA(2)), a colorless viscous liquid is prepared by the reaction of glycidyl methacrylate (1) with an equivalent of trichloroacetic anhydride (TCAA). The trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA(3)) can be synthesized using trifluoroacetic anhydride. Trifluoroacetate derivative of hydroxyethyl methacrylate (TFA-HEMA, (5)) or trifluoroacetate derivative of hydroxy methacrylate (7) can be synthesized by the reaction of pyridine with hydroxyethyl methacrylate (4) or methyl pyruvate (6) and trapping the corresponding anion with trifluoroacetic anhydride [TFAA]. Now, in a particular example of the present invention, the co-polymerization of HCE-GMA and/or HFE-GMA with methyl methacrylate (MMA) and a suitable cross-linking agent, for example, ethylene glycoldimethacrylate produces a co-polymer or xerogel which on removal of the leaving groups by solvolysis and subsequent hydration yields a hydrogel. The dimensions of an article made from the hydrogel, as compared to that of an article made from the xerogel, as will be appreciated by those skilled in the art, are dependent on the ratio of components of the copolymer, as well as the material components of the copolymer of the hydrogel. In particular, with copolymers of HFE-GMA and HCE-GMA and MMA the final dimensions of the hydrated article were found to be dependent on the weight ratio of HCE-GMA to HFE-GMA at constant MMA concentration. For example, a copolymer of a mixture of HCE-GMA/HFE-GMA in a ratio of 3:1 and MMA resulted in a hydrogel with substantially little change in dimensions from the xerogel to the hydrogel state. However, with the HCE-GMA/HFE-GMA in a ratio by weight of 1:3 (and not 3:1) the change in dimensions of the article can be up to 11%.The monomer of the second group (II) may include any one or more of the following monomer materials Methyl Methacrylate (MMA) Trifluoromethyl methacrylate (TFMMA) Hydroxymethyl methacrylate (HMMA) 2', 2', 2'-trifluoroethyl methacrylate (TFEMA) Hydroxyethyl methacrylate (HEMA) Dimethyl acrylamide (DMA) Contact lenses may be made by machining lens blanks made by cutting small cylinders or buttons from rods of the co-polymer before conversion from the xerogel to the hydrogel form. In one arrangement, the contact lens has a rigid oxygen-permeable centre portion surrounded by a soft hydrophilic peripheral skirt which is the hydrogel portion of the lens. In another arrangement, the contact lens is a composite lens comprising a rigid oxygen-permeable portion and a soft hydrogel portion. The monomers may be co-polymerized with ethylene glycol dimethacrylate (EGMA) as the cross linking agent in the presence of t-butyl peroxy pivalate (TBPP) as the initiator in silylated glass tubes. After the reaction is complete, the glass tubes are broken to provide the xerogel in the form of colorless hard rods which are then cut into buttons which in turn are shaped into contact lenses cn a lathe. The finished lenses are solvolyzed in 5% aqueous ammonia for 24-48h and then allowed to equilibrate in saline solution for 24 hours. Contact lens with a soft peripheral skirt and relatively harder center may be made by forming a rod as above with a size equal to the outside diameter of a lens and then drilling a hole through the center of the rod equal to the diameter of the central portion of the desired lens. This hole is then filled with a polymerizable material which forms a harder non-hydrophilic polymer. By choosing a xerogel with little or no change in dimensions on hydration to form the hydrophilic skirts, any stresses or distortions which might occur if there was a substantial change in dimensions on hydration are eliminated. In other cases it may be desirable to use materials with matched expansions or shrinkage at values varying between a shrinkage of 20% and an expansion of 40%. The present invention will be further illustrated by the examples which are provided for purposes of illustration. Example 1 A mixture of (HCE-GMA:HFE-GMA) 1:3 ratio by weight and MMA with EGDMA crosslinker was prepared and the mixture was stirred for 30 min. After degassing the mixture for 30 seconds in bubbling Argon, TBPP was added. The mixture was transferred to a silylated glass tube and polymerized in a water bath maintained at 50°C for 48h. The partially polymerized material was transferred to an oven maintained at 70°C and allowed to cure for 24h. The polymer was allowed to cool slowly in the oven till it reached room temperature. The glass tubes were broken and the colorless transparent polymer was removed. Disks (0.2-0.5 mm in thickness) were cut from the material and hydrolyzed in aqueous NH 4 OH for 24h. After equilibrating the disks in saline for another 24h its linear expansion was measured. It was found that the disk expanded an average of 11% in diameter. The % hydration was 59%. Example 2 This reaction was repeated in exactly the same reaction conditions as before. However, this time (HCE-GMA:HFE-GMA 3:1) ratio by weight and MMA were polymerized at 50°C and cured at 70°C for 48h in silylated glass tubes. After breaking the glass tubes, the material was isolated and disks were cut from the stress free, colorless, transparent and bubble free rods. These 0.2-0.5 mm thick disks were hydrolyzed in 5% NH 4 OH solution for 24h. Later they were transferred to a saline solution and allowed to equilibrate for 24-28h. Their expansions were measured upon hydration. It was found that the disk expanded an average of 1-2% in diameter. The % hydration was 8% Example 3 This reaction was repeated in exactly the same reaction conditions as before. However, this time (HCE-GMA:HFE-GMA 10:1) ratio by weight and MMA/GMA were polymerized at 50°C and cured at 70°C for 48h in silylated glass tubes. After breaking the glass tubes material was isolated and disks were cut from the stress free, colorless, transparent and bubble free rods. These 0.2-0.5 mm thick disks were hydrolyzed in 5% NH 4 OH solution for 24h. Later they were transferred to a saline solution and allowed to equiliberate for 24-28h. Their expansions were measured upon hydration. It was found that the disk expanded an average of 12-14% in diameter. The % hydration was 40%. Examples 4-19 In the case of examples 4 to 19, the polymerization was carried out at 50°C for 24 hours and curing at 70°C for 48 hours. The reaction mixture contained monomer ratios shown in the accompanying table. The polymerization was carried out in silylated glass tubes, and after completion of polymerization, the tubes were broken to extract the finished rods. These were cut into disks and the solvolysis and hydration was carried out by immersing the disks in 5% NH 4 OH for 24 hours, followed by transfer to a saline solution and equilibration for 24 hours. The change in dimensions was measured upon hydration. The expansion is given in the table below: Monomers (Group I) Composition Comonomer %Expansion 4. HCE-GMA/HFE-GMA 3:1 MMA 0-1% 5. HCE-GMA/HFE-GMA 3:1 TFEMA 0-1% 6. HCE-GMA/HFE-GMA 2:1 MMA 2-4% 7. HCE-GMA/HFE-GMA 1:1 MMA 4-6% 8. HCE-GMA/HFE-GMA 19:1 MMA/GMA 12-14% 9. HCE-GMA/HFE-GMA 19:1 MMA/DMA 6% 10. HCE-GMA/HFE-GMA 3:1 MMA/TFEMA 0-1% 11. HCE-GMA/HFE-GMA 3:1 HMMA 8% 12. HCE-GMA/HFE-GMA 3:1 TFMMA 0-1% 13. HCE-GMA/TFA-MA 3:1 MMA 4% 14. HCE-GMA/TFA-MA 3:1 HMMA 8% 15. TFA-HEMA/TFAMA 3:1 MMA 7% 16. TFA-HEMA/TFAMA 3:1 MMA/TFEMA 6% 17. TCA-HEMA/TFAMA 3:1 MMA/TFEMA 4% 18. TMS-GMA/HFE-GMA 3:1 MMA 0-1% 19. TBDMS-GMA/HFE-GMA 1:0 MMA -20% (minus 20%) Contact lenses can be made from any of the compositions listed in Examples 1 to 17. Typically, the copolymer compositions are cast into rod-like form and then lens blanks are made by cutting small cylinders or buttons from such rods. These lens blanks are then machined to the desired dimensions before they are converted from their xerogel form to the hydrogel form. Such compositions can also be used to make a second type of contact lens as described above having a soft peripheral skirt and a relatively harder center. Typically, such a contact lens comprises a central section made from a standard rigid gas permeable contact lens material, for example Fluoroboro 60, and an outer peripheral skirt which surrounds the central section and is made from HCE-GMA/HFE-GMA(3:1):MMA (i.e. the composition of Example 4).

Claims: Claims for the following Contracting States : AT, BE, CH, LI, DE, DK, FR, GB, GR, IT, LU, NL, SE A polymer article at least a portion of which comprises a solvolysed and hydrated hydrogel which contains water in the range 5 to 95% by weight, which hydrogel is formed from a co-polymer which incorporates ester linking groups which are capable of cleaving into a carboxy containing group and an alcohol in the presence of a nucleophile such as water or a weak base or in the presence of a C 1 - C 4 alcohol, and which can be solvolyzed and hydrated to a hydrogel, and which on solvolysis and hydration undergoes a volume change ranging from a shrinkage of 20% up to an expansion of 40%, the said co-polymer being formed from: (a) two or more monomers selected from a first group I of monomers, each of which monomers having an ethylenically unsaturated group and each of said monomers further having one or more substitutable leaving groups which can be removed by solvolysis wherein said substitutable leaving groups for each of said monomers are different from each other; and (b) one or more monomers selected from a second group II of monomers, each of which monomers is an ethylenically unsaturated monomer without such substitutable leaving groups; the quantity by weight of monomers present in the polymer being chosen so that the quantity of monomers of the first group I of monomers is in the range from 5 to 95% by weight of the co-polymer and the quantity of monomers of the second group II of monomers is from 5 to 95% by weight of the co-polymer. A polymer article as claimed in claim 1, in which the monomer or monomers in the first group I is or are monomers having a general formula: CH 2 = C(R 1 ) - Y - R L x wherein R 1 represents -H, -alkyl or -substituted alkyl groups or a group R L / x as defined below; Y represents -(CH 2 ) k -, -(Ar)- or -substituted (Ar)-, or a group of formula -COO(CP 2 ) j -(CR 2 R 3 ) m -(CP 2 ) n - wherein P represents -H, -alkyl or -substituted alkyl groups, -halo (chloro, bromo, iodo) groups, -(Ar) or -substituted (Ar); and each of R 2 and R 3 independently represents -H, -CH 3 , -OCO(CP 2 ) j or -CP 3 ; R L / x represents the substitutable leaving group which can be removed by solvolysis and is a group selected from -OCOCF 3 , -OCOCCl 3 , -OCOCBr 3 , -O-Si[(CP 2 ) k -CP 3 ] 3 , -OSO 3 -CH 3 , and -OSO 3 -Ar-CH 3 or chloroacetyl, dichloroacetyl, trichloroacetyl, fluoroacetyl, methoxyacetyl, triphenylmethoxyacetyl, phenoxyacetyl, trimethysilyl, triethylsilyl, isopropyldimethylsilyl, t-butyldimethylsilyl, methyldiisopropylsilyl, tribenzylsilyl, triphenylsilyl, cyclic acetals and ketals incorporating methylene, ethyledene, 2,2,2-trichloroethyledene groups; cyclic orthoesters formed from methoxymethylene, ethoxymethylene, 1-(N,N-dimethylamino)ethyledene derivatives, l-(N,N-dimethylamino)benzylidene derivatives, and methanesulfonate and toluenesulfonates and wherein k is an integer of from 1 to 16, each of j, m, n is 0 or an integer of at least 1 provided that j + m + n is greater than or equal to 2 but less than or equal to 16; and x is functionally dependent on Y. A polymer article as claimed in claim 2, in which k has a value of from 1 to 6. A polymer article as claimed in claim 2 or 3, in which each of j, m, and n is 0 or an integer of from 1 to 6. A polymer article as claimed in claim 1, in which the monomers of the first group are formed by one of the following syntheses: wherein TCAA represents trichloroacetic anhydride and TFAA represents trifluoroacetic anhydride. A polymer article as claimed in claim 2, in which R L / x is selected from the group consisting of easily hydrolyzable groups. A polymer article as claimed in any one of the preceding claims, wherein a monomer of the second group II of monomers is methyl methacrylate. A polymer article as claimed in any one of the preceding claims, wherein a monomer of the second group II of monomers is 2',2',2'-trifluoroethyl methacrylate. A polymer article as claimed in any one of the preceding claims, in which the first group monomers are 1,3-bis-(trichloroacetoxy)propyl -2-methacrylate and 1,3-bis-(trifluoroacetoxy)propyl -2-methacrylate. A polymer article as claimed in any one of claims 1 to 8, in which the first group monomers are 1,3-bis-(trimethylsilyl)propyl -2-methacrylate and 1,3-bis-(trifluoroacetoxy)propyl-2-methacrylate. A polymer article as claimed in any one of claims 1 to 8, in which the first group monomers are 1,3-bis-(t-butyldimethylsilyl)propyl-2-methacrylate and 1,3-bis-(trifluoroacetoxy)propyl-2-methacrylate. A polymer article as claimed in any one of claims 1 to 8, in which the first group monomers are 1,3-bis-(trichloroacetoxy)propyl-2-methacrylate and methyl - α -(trifluoroacetoxy)acrylate. A polymer article as claimed in any one of claims 1 to 8, in which the first group monomers are (2'-trifluoroacetoxy)ethyl methacrylate and methyl- α -(trifluoroacetoxy)acrylate. A polymer article as claimed in any one of claims 1 to 8, in which the first group monomers are (2'-trichloroacetoxy)ethyl methacrylate and methyl- α -(trifluoroacetoxy)acrylate. A polymer article as claimed in any one of the preceding claims, in which the ratio of the quantity by weight of the monomers of groups I and II ranges from 19:1 to 1:19. A polymer article as claimed in any one of the preceding claims, wherein the polymer article is a contact lens. A polymer article as claimed in claim 16, in which the contact lens has a rigid oxygen permeable center portion surrounded by a soft hydrophilic peripheral skirt which is the hydrogel portion of the article. A polymer article as claimed in claim 16, in which the contact lens is a composite lens comprising a rigid oxygen permeable portion and a soft hydrogel portion. A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA); and the monomer selected from the second group II is methyl methacrylate (MMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 10:1 or 19:1; and the monomers selected from the second group II are methyl methacrylate and glyceryl methacrylate (MMA/GMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 3:1; and the monomer selected from the second group II is 2',2',2'-trifluoroethyl methacrylate (TFEMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 19:1; and the monomers selected from the second group II are methyl methacrylate and dimethyl acrylamide (MMA/DMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 3:1; and the monomers selected from the second group II are hydroxymethyl methacrylate (HMMA), trifluoromethyl methacrylate (TFMMA), or methyl methacrylate and 2',2',2'-trifluoroethyl methacrylate (MMA/TFEMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of methacrylate (TFA-MA) in a weight ratio of 3:1; and the monomer selected from the second group II is methyl methacrylate (MMA) or hydroxymethyl methacrylate (HMMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trifluoroacetate derivative of hydroxyethyl methacrylate (TFA-HEMA) and the trifluoroacetate derivative of methacrylate (TFA-MA) in a weight ratio of 3:1; and the monomers selected from the second group II are methyl methacrylate (MMA), or methyl methacrylate and 2',2',2'-trifluoroethyl methacrylate (MMA/TFEMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate derivative of hydroxyethyl methacrylate (TCA-HEMA) and the trifluoroacetate derivative of methacrylate (TFA-MA) in a weight ratio of 3:1; and the monomers selected from the second group II are methyl methacrylate (MMA), or methyl methacrylate and 2',2',2'-trifluoroethyl methacrylate (MMA/TFEMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trimethyl silyl derivative of glyceryl methacrylate (TMS-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 3:1; and the monomer selected from the second group II is methyl methacrylate (MMA). Claims for the following Contracting State : ES A polymer article at least a portion of which comprises a solvolysed and hydrated hydrogel which contains water in the range 5 to 95% by weight, which hydrogel is formed from a co-polymer which incorporates ester linking groups which are capable of cleaving into a carboxy containing group and an alcohol in the presence of a nucleophile such as water or a weak base or in the presence of a C 1 - C 4 alcohol, and which can be solvolyzed and hydrated to a hydrogel, and which on solvolysis and hydration undergoes a volume change ranging from a shrinkage of 20% up to an expansion of 40%, the said co-polymer being formed from: (a) two or more monomers selected from a first group I of monomers, each of which monomers having an ethylenically unsaturated group and each of said monomers further having one or more substitutable leaving groups which can be removed by solvolysis wherein said substitutable leaving groups for each of said monomers are different from each other; and (b) one or more monomers selected from a second group II of monomers, each of which monomers is an ethylenically unsaturated monomer without such substitutable leaving groups; the quantity by weight of monomers present in the polymer being chosen so that the quantity of monomers of the first group I of monomers is in the range from 5 to 95% by weight of the co-polymer and the quantity of monomers of the second group II of monomers is from 5 to 95% by weight of the co-polymer. A polymer article as claimed in claim 1, in which the monomer or monomers in the first group I is or are monomers having a general formula: CH 2 = C(R 1 ) - Y - R L wherein R 1 represents -H, -alkyl or -substituted alkyl groups or a group R L as defined below; Y represents -(CH 2 ) k -, -(Ar)- or -substituted (Ar)-, or a group of formula -COO(CP 2 ) j -(CR 2 R 3 ) m -(CP 2 ) n - wherein P represents -H, -alkyl or -substituted alkyl groups, -halo (chloro, bromo, iodo) groups, -(Ar) or -substituted (AR); and each of R 2 and R 3 independently represents -H, -CH 3 , -OCO(CP 2 ) j or -CP 3 ; R L / x represents the substitutable leaving group which can be removed by solvolysis and is a group selected from -OCOCF 3 , -OCOCCl 3 , -OCOCBr 3 , -O-Si[(CP 2 ) k -CP 3 ] 3 , -OSO 3 -CH 3 , and -OSO 3 -Ar-CH 3 or chloroacetyl, dichloroacetyl, trichloroacetyl, fluoroacetyl, methoxyacetyl, triphenylmethoxyacetyl, phenoxyacetyl, trimethysilyl, triethylsilyl, isopropyldimethylsilyl, t-butyldimethylsilyl, methyldiisopropylsilyl, tribenzylsilyl, triphenylsilyl; cyclic acetals and ketals incorporating methylene, ethyledene, 2,2,2-trichloroethyledene groups; cyclic orthoesters formed from methoxymethylene, ethoxymethylene, 1-(N,N-dimethylamino)ethyledene derivatives, l-(N,N-dimethylamino)benzylidene derivatives, and methanesulfonate and toluenesulfonates and wherein k is an integer of from 1 to 16, each of j, m, n is 0 or an integer of at least 1 provided that j + m + n is greater than or equal to 2 but less than or equal to 16; and x is functionally dependent on Y. A polymer article as claimed in claim 2, in which k has a value of from 1 to 6. A polymer article as claimed in claim 2 or 3, in which each of j, m, and n is 0 or an integer of from 1 to 6. A polymer article as claimed in claim 1, in which the monomers of the first group are formed by one of the following syntheses: wherein TCAA represents trichloroacetic anhydride and TFAA represents trifluoroacetic anhydride. A polymer article as claimed in claim 2, in which R L / x is selected from the group consisting of easily hydrolyzable groups. A polymer article as claimed in any one of the preceding claims, wherein a monomer of the second group II of monomers is methyl methacrylate. A polymer article as claimed in any one of the preceding claims, wherein a monomer of the second group II of monomers is 2',2',2'-trifluoroethyl methacrylate. A polymer article as claimed in any one of the preceding claims, in which the first group monomers are 1,3-bis-(trichloroacetoxy)propyl -2-methacrylate and 1,3-bis-(trifluoroacetoxy)propyl -2-methacrylate. A polymer article as claimed in any one of claims 1 to 8, in which the first group monomers are 1,3-bis-(trimethylsilyl)propyl -2-methacrylate and 1,3-bis-(trifluoroacetoxy)propyl-2-methacrylate. A polymer article as claimed in any one of claims 1 to 8, in which the first group monomers are 1,3-bis-(t-butyldimethylsilyl)propyl-2-methacrylate and 1,3-bis-(trifluoroacetoxy)propyl-2-methacrylate. A polymer article as claimed in any one of claims 1 to 8, in which the first group monomers are 1,3-bis-(trichloroacetoxy)propyl-2-methacrylate and methyl -α-(trifluoroacetoxy)acrylate. A polymer article as claimed in any one of claims 1 to 8, in which the first group monomers are (2'-trifluoroacetoxy)ethyl methacrylate and methyl- α -(trifluoroacetoxy)acrylate. A polymer article as claimed in any one of claims 1 to 8, in which the first group monomers are (2'-trichloroacetoxy)ethyl methacrylate and methyl-α-(trifluoroacetoxy)acrylate. A polymer article as claimed in any one of the preceding claims, in which the ratio of the quantity by weight of the monomers of groups I and II ranges from 19:1 to 1:19. A polymer article as claimed in any one of the preceding claims, wherein the polymer article is a contact lens. A polymer article as claimed in claim 16, in which the contact lens has a rigid oxygen permeable center portion surrounded by a soft hydrophilic peripheral skirt which is the hydrogel portion of the article. A polymer article as claimed in claim 16, in which the contact lens is a composite lens comprising a rigid oxygen permeable portion and a soft hydrogel portion. A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA); and the monomer selected from the second group II is methyl methacrylate (MMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 10:1 or 19:1; and the monomers selected from the second group II are methyl methacrylate and glyceryl methacrylate (MMA/GMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 3:1; and the monomer selected from the second group II is 2',2',2'-trifluoroethyl methacrylate (TFEMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 19:1; and the monomers selected from the second group II are methyl methacrylate and dimethyl acrylamide (MMA/DMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 3:1; and the monomers selected from the second group II are hydroxymethyl methacrylate (HMMA), trifluoromethyl methacrylate (TFMMA), or methyl methacrylate and 2',2',2'-trifluoroethyl methacrylate (MMA/TFEMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of methacrylate (TFA-MA) in a weight ratio of 3:1; and the monomer selected from the second group II is methyl methacrylate (MMA) or hydroxymethyl methacrylate (HMMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trifluoroacetate derivative of hydroxyethyl methacrylate (TFA-HEMA) and the trifluoroacetate derivative of methacrylate (TFA-MA) in a weight ratio of 3:1; and the monomers selected from the second group II are methyl methacrylate (MMA), or methyl methacrylate and 2',2',2'-trifluoroethyl methacrylate (MMA/TFEMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trichloroacetate derivative of hydroxyethyl methacrylate (TCA-HEMA) and the trifluoroacetate derivative of methacrylate (TFA-MA) in a weight ratio of 3:1; and the monomers selected from the second group II are methyl methacrylate (MMA), or methyl methacrylate and 2',2',2'-trifluoroethyl methacrylate (MMA/TFEMA). A polymer article as claimed in claim 1, wherein the monomers selected from the first group I are the trimethyl silyl derivative of glyceryl methacrylate (TMS-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 3:1; and the monomer selected from the second group II is methyl methacrylate (MMA). A process for producing a polymer article at least a portion of which comprises a solvolysed and hydrated hydrogel which contains water in the range 5 to 95% by weight, which hydrogel is formed from a co-polymer which incorporates ester linking groups which are capable of cleaving into a carboxy containing group and alcohol in the presence of a nucleophile such as water or a weak base or in the presence of a C 1 - C 4 alcohol, and which can be solvolyzed and hydrated to a hydrogel, and which on solvolysis and hydration undergoes a volume change ranging from a shrinkage of 20% up to an expansion of 40%, wherein said process comprises producing said co-polymer by polymerizing: (a) two or more monomers selected from a first group I of monomers, each of which monomers having an ethylenically unsaturated group and each of said monomers further having one or more substitutable leaving groups which can be removed by solvolysis wherein said substitutable leaving groups for each of said monomers are different from each other; and (b) one or more monomers selected from a second group II of monomers, each of which monomers is an ethylenically unsaturated monomer without such substitutable leaving groups; the quantity by weight of monomers present in the polymer being chosen so that the quantity of monomers of the first group I of monomers is in the range from 5 to 95% by weight of the co-polymer and the quantity of monomers of the second group II of monomers is from 5 to 95% by weight of the co-polymer. A process as claimed in claim 28, in which the monomer or monomers in the first group I is or are monomers having a general formula: CH 2 = C(R 1 ) - Y - R L x wherein R 1 represents -H, -alkyl or -substituted alkyl groups or a group R L / x as defined below; Y represents -(CH 2 ) k -, -(Ar)- or -substituted (Ar)-, or a group of formula -COO(CP 2 ) j -(CR 2 R 3 ) m -(CP 2 ) n - wherein P represents -H, -alkyl or -substituted alkyl groups, -halo (chloro, bromo, iodo) groups, -(Ar) or -substituted (Ar); and each of R 2 and R 3 independently represents -H, -CH 3 , -OCO(CP 2 ) j or -CP 3 ; represents the substitutable leaving group which can be removed by solvolysis and is a group selected from -OCOCF 3 , -OCOCCl 3 , -OCOCBr 3 , -O-Si[(CP 2 ) k -CP 3 ] 3 , -OSO 3 -CH 3 , and -OSO 3 -Ar-CH 3 or chloroacetyl, dichloroacetyl, trichloroacetyl, fluoroacetyl, methoxyacetyl, triphenylmethoxyacetyl, phenoxyacetyl, trimethysilyl, triethylsilyl, isopropyldimethylsilyl, t-butyldimethylsilyl, methyldiisopropylsilyl, tribenzylsilyl, triphenylsilyl, cyclic acetals and ketals incorporating methylene, ethyledene, 2,2,2-trichloroethyledene groups; cyclic orthoesters formed from methoxymethylene, ethoxymethylene, 1-(N,N-dimethylamino)ethyledene derivatives, l-(N,N-dimethylamino)benzylidene derivatives, and methanesulfonate and toluenesulfonates and wherein k is an integer of from 1 to 16, each of j, m, n is 0 or an integer of at least 1 provided that j + m + n is greater than or equal to 2 but less than or equal to 16; and x is functionally dependent on Y. A process as claimed in claim 29, in which k has a value of from 1 to 6. A process as claimed in claim 29 or 30, in which each of j, m, and n is 0 or an integer of from 1 to 6. A process as claimed in claim 28, in which the monomers of the first group are formed by one of the following syntheses: wherein TCAA represents trichloroacetic anhydride and TFAA represents trifluoroacetic anhydride. A process as claimed in claim 29, in which R L / x is selected from the group consisting of easily hydrolyzable groups. A process as claimed in any of claims 28 - 33, wherein a monomer of the second group II of monomers is methyl methacrylate. A process as claimed in any of claims 28 - 34, wherein a monomer of the second group II of monomers is 2',2', 2'-trifluoroethyl methacrylate. A process as claimed in any of claims 28 - 35, in which the first group monomers are 1,3-bis-(trichloroacetoxy)propyl -2-methacrylate and 1,3-bis-(trifluoroacetoxy)propyl -2-methacrylate. A process as claimed in any of claims 28 - 35, in which the first group monomers are 1,3-bis-(trimethylsilyl)propyl -2-methacrylate and 1,3-bis-(trifluoroacetoxy)propyl-2-methacrylate. A process as claimed in any of claims 28 - 38, in which the first group monomers are 1,3-bis-(t-butyldimethylsilyl)propyl-2-methacrylate and 1,3-bis-(trifluoroacetoxy)propyl-2-methacrylate. A process as claimed in any one of claims 28 to 35, in which the first group monomers are 1,3-bis-(trichloroacetoxy)propyl-2-methacrylate and methyl - α - (trifluoroacetoxy) acrylate. A process as claimed in any one of claims 28 - 35, in which the first group monomers are (2'-trifluoroacetoxy)ethyl methacrylate and methyl- α -(trifluoroacetoxy) acrylate. A process as claimed in any one of claims 28 - 35, in which the first group monomers are (2'-trichloroacetoxy)ethyl methacrylate and methyl-α-(trifluoroacetoxy) acrylate. A process as claimed in any of claims 28 - 41, in which the ratio of the quantity by weight of the monomers of groups I and II ranges from 19:1 to 1:19. A process for producing a contact lens, comprising forming a contact lens from a polymer obtainable according to any of claims 28 - 42. A process as claimed in claim 43, in which the contact lens has a rigid oxygen permeable center portion surrounded by a soft hydrophilic peripheral skirt which is the hydrogel portion of the article. A process as claimed in claim 43, in which the contact lens is a composite lens comprising a rigid oxygen permeable portion and a soft hydrogel portion. A process as claimed in claim 28, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA); and the monomer selected from the second group II is methyl methacrylate (MMA). A process as claimed in claim 28, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 10:1 or 19:1; and the monomers selected from the second group II are methyl methacrylate and glyceryl methacrylate (MMA/GMA). A process as claimed in claim 28, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 3:1; and the monomer selected from the second group II is 2',2',2'-trifluoroethyl methacrylate (TFEMA). A process as claimed in claim 28, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 19:1; and the monomers selected from the second group II are methyl methacrylate and dimethyl acrylamide (MMA/DMA). A process as claimed in claim 28, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 3:1; and the monomers selected from the second group II are hydroxymethyl methacrylate (HMMA), trifluoromethyl methacrylate (TFMMA), or methyl methacrylate and 2',2',2'-trifluoroethyl methacrylate (MMA/TFEMA). A process as claimed in claim 28, wherein the monomers selected from the first group I are the trichloroacetate ester of glyceryl methacrylate (HCE-GMA) and the trifluoroacetate derivative of methacrylate (TFA-MA) in a weight ratio of 3:1; and the monomer selected from the second group II is methyl methacrylate (MMA) or hydroxymethyl methacrylate (HMMA). A process as claimed in claim 28, wherein the monomers selected from the first group I are the trifluoroacetate derivative of hydroxyethyl methacrylate (TFA-HEMA) and the trifluoroacetate derivative of methacrylate (TFA-MA) in a weight ratio of 3:1; and the monomers selected from the second group II are methyl methacrylate (MMA), or methyl methacrylate and 2',2',2'-trifluoroethyl methacrylate (MMA/TFEMA). A process as claimed in claim 28, wherein the monomers selected from the first group I are the trichloroacetate derivative of hydroxyethyl methacrylate (TCA-HEMA) and the trifluoroacetate derivative of methacrylate (TFA-MA) in a weight ratio of 3:1; and the monomers selected from the second group II are methyl methacrylate (MMA), or methyl methacrylate and 2',2',2'-trifluoroethyl methacrylate (MMA/TFEMA). A process as claimed in claim 28, wherein the monomers selected from the first group I are the trimethyl silyl derivative of glyceryl methacrylate (TMS-GMA) and the trifluoroacetate derivative of glyceryl methacrylate (HFE-GMA) in a weight ratio of 3:1; and the monomer selected from the second group II is methyl methacrylate (MMA).

Inventors: ASKARI SYED HARA, JEANG SHAO CHANG, NEIDLINGER HERMANN HEINRICH, ASKARI, SYED HARA, JEANG, SHAO CHANG, NEIDLINGER, HERMANN HEINRICH
Applicants: PILKINGTON BARNES HIND INC, PBH, INC.
Application year: 1992
Main classification: C08F246
IPC codes: C08F20, G02C7, C08L101, C08F246, G02B1, C08F220