Method for forming patterned tungsten layers

Abstract: The present applicants have discovered that a layer predominantly comprising tungsten can be formed into precise patterns having substantially vertical walls by using titanium as a mask and plasma etching in a fluorine-containing plasma such as CF₄ or SF₆. The success of the process is believed attributable to the occurrence of an etch stop reaction on the sidewalls of the tungsten. The products of the reaction inhibit horizontal etching. After the tungsten is etched, the titanium mask can be selectively removed, as by etching in dilute HF. Each step in the process can be effected without subjecting the workpiece to voltage magnitudes in excess of 200 volts or temperatures outside the range between room temperature and 200°C.

Description: Field of the Invention This invention relates to a method of forming a patterned tungsten layer and, more particularly, to a method for forming precisely patterned tungsten contacts on a III-V semiconductor with minimal damage to the semiconductor. Background of the Invention Because of their reliability and tolerance of high temperature processing, tungsten ohmic and Schottky contacts are highly desirable in III-V microelectronic devices. However, it is difficult to form patterns of tungsten with the precision required in modern microelectronic devices. Tungsten can be readily deposited in thin layers at low temperature using rf sputtering. However efforts to pattern the deposited film encounter the difficulty that tungsten etches isotropically. While it is desired to etch only the tungsten unprotected by a photoresist mask, the tungsten also etches laterally, undercutting the mask. As a consequence, vertical profiles and critical feature dimensions, such as submicron FET gates, cannot be successfully transferred to the underlying tungsten using conventional photolithography. Various attempts have been made to enhance the precision of pattern transfer to tungsten, but none provide a clear solution to the problem of forming tungsten contacts on m-V semiconductors. For example, Shattenburg et al. report using CBrF 3 or CHF 3 to etch tungsten while depositing polymer on the sidewalls to impede horizontal etching ( J. Vac. Sci. Technol. B3, 272 (1985). The result is transferred features which are inflated at the base. Others report that using SF 6 or CF 4 plasma discharges create fluorine radicals which undercut masks and result in loss of feature size. See, for example, Suzuki et al., J. Electrochem. Soc. 129, 2764 (1982). Gas mixes of SF 6 - CBrF 3 or SF 6 -CHF 3 reduce undercut, but nonetheless yield isotropic profiles. (See Tennant et al., J. Vac. Sci. Technol. B7,1836 (1989). Recently vertical etching of tungsten in SF 6 at low temperatures has been reported, but the method requires unique etching equipment and is not well suited for commercial manufacture. See S. Tachi et al., J. Vac. Sci. Technol. A9, 796 (1991). The patent application EP-A- 178 619 discloses the reactive ion etching of tungsten layers using CF 4 and O 2 gaseous mixture with the aid of a mask of titanium deposited by lift-off. According to the present invention, there is provided a method as defined in claim 1. The present applicants have discovered that a layer predominantly comprising tungsten can be formed into precise patterns having substantially vertical walls by using titanium as a mask and plasma etching in a fluorine-containing plasma of CF 4 or SF 6 plus Argon. The success of the process is believed attributable to the occurrence of an etch stop reaction on the sidewalls of the tungsten. The products of the reaction inhibit horizontal etching. After the tungsten is etched, the titanium mask can be selectively removed, as by etching in dilute HF. Each step in the process can be effected without subjecting the workpiece to voltage magnitudes in excess of 200 volts or temperatures outside the range between room temperature and 200°C. Brief Description of the Drawings In the drawings: FIG. 1 is a flow diagram of the preferred method of patterning a tungsten layer. FIG. 2 shows schematic cross sections of the workpiece at various steps in the process of FIG. 1. FIG. 3 is a graphical illustration of etch depth as a function of time; and FIG. 4 is a graphical illustration of etch rate as a function of plasma generator power. It is to be understood that these drawings are for purposes of illustrating the concepts of the invention and, except for graphical illustrations, are not to scale. Detailed Description Referring to the drawings, FIG. 1 is a flow diagram illustrating the process for patterning a tungsten layer. As shown in FIG. 1A the first step involves depositing a layer of tungsten on a substrate. Preferably the substrate is a III-V semiconductor substrate such as gallium arsenide. As a preliminary step the substrate is thoroughly cleaned as by an O 2 plasma de-scumming and followed by dipping in dilute HCl to remove surface oxides. The tungsten layer is then deposited, preferably by low temperature rf sputtering. The substrate and a tungsten target are disposed in a low pressure, inert gas ambient such as argon at 0.133 to 4 Pa (1-30 milliTorr (mT)). An rf plasma is struck and a DC bias of 300V applied to the target induces sputtering of tungsten from the target onto the substrate. The temperature is preferably below about 150°C. For use in the fabrication of microelectronic contacts, the tungsten layer has a thickness of less than a micrometer, and is typically about 4 x 10 -7 m (4000 angstroms). The substrate 10 with a deposited tungsten layer 11 is schematically illustrated in FIG. 2A. The next step shown in FIG. 1B is masking the tungsten layer with a titanium mask. The masking step can be conveniently accomplished by applying a layer of titanium having a thickness of less than a micrometer and using a conventional lift-off process to form the mask pattern. The tungsten layer is coated with EBR-9 resist and the desired pattern for the mask is defined by direct write electron-beam lithography. A layer of titanium, preferably about 400 nm thick, is then deposited onto the workpiece in an Airco 1800 e-beam evaporator. The titanium which contacts unmasked tungsten strongly adheres. The titanium not in contact with the tungsten is lifted off by an acetone solvent spray. The result, shown in FIG. 2B, is a residual titanium mask 12 overlying the tungsten layer 11. As illustrated in FIG. 1C, the third step is etching the mask workpiece to selectively remove the unmasked tungsten. This etching is reactive ion etching in a SF 6 /Ar or CF 4 /Ar plasma. The etching can be conveniently performed in a parallel plate plasma etcher such as a Plasma Therm SL 772, water-cooled a room temperature. Advantageously etching is effected in SF 6 /Ar gas using a 0.133 Pa (1mT) pressure, a DC bias on the sample of -100V, and a plasma frequency of 13.56 MHz. A 25% overetch was performed to allow for nonuniformity of the tungsten film and to compensate for any loading effects. The result of this etching step is removal of the tungsten in those regions where it is not protected by the titanium mask. The resulting structure is shown in FIG. 2C. What is surprising is that the tungsten is etched anisotropically showing vertical side walls and virtually no undercut of the titanium mask. This highly desirable characteristic is believed attributable to the deposition of an involatile species such as TiF 4 on the sidewalls. The TiF 4 inhibits etching at the vertical side walls. The etching is anisotropic so long as titanium remains on the tungsten. FIG. 3 shows the etch depth as a function of time for both tungsten W and titanium Ti at plasma power levels of 75W and 150W. The data was taken using Technics Micro Reactive Ion Etch Series 800 Plasma System utilizing 30 KHz plasma excitation with CF 4 plasma. FIG. 4 shows the etch rate in angstroms per minute as a function of the plasma power. The etch rates of both tungsten and titanium increase as a function of both power and pressure. At lower powers, etch rates of both tungsten and titanium tend to increase gradually and then become more nearly linear. This suggests the existence of native oxides on the surfaces which must be removed by ion bombardment before chemical etching can be initiated. Over the range of pressures examined, the etch rates of both tungsten and titanium generally increase with increasing pressure. Selectivities range from 8:1 to 1.5:1 as a function of power level at a given pressure. SEM examination showed that the anisotropic character of the tungsten etching is not a function of pressure while the titanium mask is present. Vertical profiles were reproduced with no loss of feature dimensions over a wide range of pressure from 0.133 to 18.62 Pa (1 mT to 140 mT). The fact that the tungsten etching can be achieved with low negative DC bias of magnitude less than 200V means that damage to the exposed semiconductor is not significant. The final step shown in FIG. ID is selective removal of the titanium mask. This step is optional depending on the application intended. Titanium removal can be easily achieved without adversely affecting the exposed semiconductor or tungsten by immersing the workpiece in a dilute HF solution. The resulting structure with the mask layer 12 removed is shown in FIG. 2D.

Claims: A method of forming a patterned tungsten layer deposited on a semiconductor substrate comprising the steps of: depositing said tungsten layer on said semiconductor substrate; forming a titanium mask on said tungsten layer, removing the unmasked tungsten by reactive ion etching in a fluorine-containing plasma, CHARACTERIZED IN THAT said fluorine-containing plasma is formed in a mixture of Argon and a gas selected from SF6 and CF4, at a pressure in the range 0.13 Pa (1 mTorr) to 18.6 Pa (140 mTorr), a negative bias voltage of magnitude less than 200 Volts is applied between the substrate and the plasma during etching, to effect ion sputtering of said tungsten said process is conducted without subjecting the semiconductor to temperatures exceeding 200°C. The method of claim 1 wherein said tungsten is deposited by rf sputtering. The method of claim 1 wherein said tungsten layer is masked with titanium by a lift off process. The method of claim 1 wherein the unmasked tungsten is removed by reactive ion etching in Argon and comprising SF 6 . The method of claim 1 wherein the unmasked tungsten is removed by reactive ion etching in Argon and CF 4 . The method of claim 1 including the further step of selectively removing the titanium mask after etching the unmasked tungsten. The method of claim 1 wherein the titanium mask is selectively removed by etching in an HF solution. The method of claim I wherein said substrate comprises gallium arsenide. The method of claim 7 wherein said titanium is deposited in a layer having a thickness of less than one micrometer.

Inventors: FULLOWAN THOMAS ROBERT, PEARTON STEPHEN JOHN, REN FAN, FULLOWAN, THOMAS ROBERT, PEARTON, STEPHEN JOHN, REN, FAN
Applicants: AT & T CORP, AT&T CORP.
Application year: 1992
Main classification: H01L21
IPC codes: H01L21, C23F4