Synthesis of poly(vinyl phosphonic acid)

Abstract: Poly(vinyl phosphonic acid) is synthesised by polymerising vinyl phosphonyl dichloride in the presence of a cross-linker such as formaldehyde or 1,3-butadiene di-epoxide, with a free-radical initiator. The product can be reacted with aluminosilicate glass to form an improved cement.

Description: This invention relates to a method of synthesising poly(vinyl phosphonic acid), PVPA, especially with a view to obtaining a product of high molecular weight or a product which will yield strong glass ionomer cements. A known synthesis of PVPA is disclosed in European Patent Application Publication 340016, and is as follows: The first stage is the preparation of a polymer of vinyl phosphonic acid from vinyl phosphonyl dichloride (VPDC). VPDC is dissolved in an equal volume of 1,1,1-trichloroethane and to this solution is added the initiator, azo-bis-isobutyronitrile, at a level of 3% by weight of the monomer. The mixture is heated under nitrogen, with stirring, in a water-jacketed reaction vessel equipped with a reflux condenser to a temperature of 70°C for two hours. If the entire polymerisation (18 hours) were carried out at 70°C, the yield would be 50-60%. Instead, after two hours at 70°C, the temperature is lowered to 40 - 45°C and maintained at this temperature for a further 16-18 hours, whereby the yield is increased to 85-90%. A viscous, orange-brown solution results, which is a solution of the crude polymer of vinyl phosphonyl dichloride. This is then hydrolysed by slow addition into a large volume of chilled water with stirring, removing the bulk of the HCl gas as it is formed by means of a vacuum. The hydrolysed product is then concentrated, and the excess organic solvent removed by vacuum distillation or by means of a rotary evaporator. Analysis of the product typically shows it to contain 85-90% of the desired PVPA - poly(vinyl phosphonic acid), a solid, together with some 10-15% residual monomer. The next stage is the purification of the product prepared as just described. The PVPA must first be isolated by removing the water introduced by the hydrolysis, using a rotary evaporator or similar. The resulting solid is then dissolved in an equal or lesser weight of industrial methylated spirits (other alcohols can be used) with gentle warming as necessary. The solution is then poured slowly into a large excess of a non-solvent, such as ethyl acetate, with stirring. A white precipitate forms, which is isolated from the solvent mixture, and contains some 5% of residual monomer. Repeating the dissolution in industrial methylated spirits and the precipitation with ethyl acetate leaves no residual monomer detectable by P-31 NMR spectroscopy. The purified PVPA is a hygroscopic, off-white solid. It is readily soluble in water up to concentrations greater than 80% by weight when prepared as described. It has been suggested that a higher molecular weight than obtained by that method would be desirable to realise the potential advantages of PVPA glass ionomer cements over current commercial polyacrylic acid glass ionomer cements, such as increased strength and improved handling properties and aesthetics of such cements. According to the present invention, a method of synthesising poly(vinyl phosphonic acid), which may be substituted, comprises polymerising a vinyl phosphonyl compound, characterised in that the polymerisation takes place in the presence of a product-modifying additive, being a cross-linker. Preferably the polymerisation takes place in an aqueous medium and preferably the additive is water-soluble. Preferably the polymerisation is free-radical polymerisation, for which the initiator is preferably azo-bis-iso-butyronitrile. Preferably the vinyl phosphonyl compound is a dihalide such as dichloride. Preferably the additive has at least one reactive end group e.g. consisting of a chalcogenide, preferably either (i) double-bonded to an atom lacking any -OH group bonded thereto (for example =O, as in R 1 R 2 C=O where neither R is -OH) or (ii) bonded to two themselves bonded atoms (for example where preferably no R is -OH) such as an aldehyde (e.g. formaldehyde H 2 C=O, paraformaldehyde -(-CH 2 O-)- n (or glutaraldehyde OCH(CH 2 ) 3 CHO), 1,3-butadiene di-epoxide, 2,2'-sulphonyl diethanol and ethylene glycol dimethacrylate of which formaldehyde and 1,3-butadiene di-epoxide are most preferred and may be present in a proportion of 1-5% by mass of the vinyl phosphonyl compound. The invention will now be described by way of example. In each Example, 3% by mass of a cross-linking additive was added under dry nitrogen to a degassed sample of vinyl phosphonyl dichloride in an equal volume of 1,1,1-trichloroethane as solvent. Immediately afterwards, azo-bis-iso-butyro-nitrile was added as initiator of the process of free radical polymerisation of vinyl phosphonyl dichloride. After polymerisation, the product was spray-dried to a powder. Samples of the polymer so obtained were found, by viscometry, to have mostly a higher molecular weight than the product of EP-A-340016. After polymerisation, the product was made into a 50% by mass aqueous solution containing additionally 10% by mass of amino- tris (methyl phosphonic acid) (sold under the trade mark Dequest 2000 by Monsanto), to which mixture 3g ion-leachable aluminosilicate glass powder were added per 1 ml of liquid, thoroughly mixed and packed into a 6mm x 4mm mould. The glass had been prepared by mixing together 437 parts by weight silica, 230 parts by weight alumina, 129 parts by weight calcium fluoride, 175 parts by weight cryolite and 29 parts by weight aluminium phosphate and heating to 1300°C for 90 minutes. The melt was cooled rapidly by pouring into water. The resulting glass was ground and sieved, and the fraction of particle size less than 45 microns used to prepare the cement. Before use, the glass powder was deactivated by heating in a furnace at 450°C for 90 minutes. The "Dequest" improved the handling properties of the glass/PVPA cement system, and increased both the working time and strength of the cement. The compressive strength of the resulting cement was determined after storage at 100% relative humidity at 37°C for 24 hours, as shown in the following table. Storage under water yielded less impressive results, which however were still as good as or better than without the additive. The additive did not affect the handling properties of the glass/PVPA system.

Claims: A method of synthesising poly(vinylphosphonic) acid, comprising polymerising a vinyl phosphonyl compound, characterised in that the polymerisation takes place in the presence of a cross-linker, whose effect is to raise the molecular weight of the product. A method according to Claim 1, wherein the acid is substituted. A method according to Claim 1 or 2, wherein the polymerisation takes place in an aqueous medium. A method according to Claim 3, wherein the cross-linker is water-soluble. A method according to any preceding claim, wherein the polymerisation is free-radical polymerisation. A method according to Claim 5, wherein the polymerisation initiator is azo-bis-iso-butyronitrile. A method according to any preceding claim, wherein the vinyl phosphonyl compound is a dihalide. A method according to any preceding claim, wherein the cross-linker has at least one reactive end group. A method according to Claim 8, wherein the end group consists of a chalcogenide. A method according to Claim 9, wherein the chalcogenide is double-bonded to an atom lacking any -OH group bonded thereto. A method according to Claim 9, wherein the chalcogenide is bonded to two themselves bonded atoms. A method according to Claim 11, wherein the said themselves bonded atoms lack any -OH group bonded to either of them. A method according to Claim 12, wherein the cross-linker is formaldehyde. A method according to Claim 12, wherein the cross-linker is 1,3-butadiene di-epoxide. A method according to any preceding claim, wherein the cross-linker is present in a proportion of 1-5% by mass of the vinyl phosphonyl compound. A glass ionomer cement comprising the reaction product of glass, water and poly(vinyl phosphonic acid) synthesised by the method of any preceding claim.

Inventors: BRAYBROOK JULIAN HUGH, ELLIS JOHN, BRAYBROOK, JULIAN HUGH, ELLIS, JOHN
Applicants: BRITISH TECH GROUP, BRITISH TECHNOLOGY GROUP LTD
Application year: 1992
Main classification: C08F30
IPC codes: C08F2, C08F30, C04B28, C04B26