Novel quarternary ammonium salts

Abstract: Quarternary ammonium salts having a 2, 3, 5, 6-tetrahydroxazolo [2, 3-b] oxazole nucleus, such as 4-aralkyl or alkyl-2, 3, 5, 6-tetrahydroxazolo [2, 3-b] oxazolium salts of formula I are disclosed. These quarternary ammonium salts are useful a cationic polymerization initiator or proton-donating catalyst of the heat latent type to be incorporated heat-curable coating and other resinous compositions.

Description: BACKGROUND OF THE INVENTION This invention relates to a novel class of quarternary ammonium salts which are useful as a cationic polymerization initiator. A variety of cationic polymerization initiators are known including Friedel-Crafts catalysts such as aluminum chloride, boron trifluoride-ether complex, photo-degradable onium salts (S, Se, Te), diallyl iodonium salts and the like. These known initiators are generally not selective with respect to the reaction temperature. Therefore, epoxy resins containing these initiators begin to cure even at room temperature. Japanese Laid Open Patent Application (Kokai) Nos. 37003/83 and 37004/83 disclose another type of cationic polymerization initiators. They are aliphatic or aromatic sulfonium salts capable of generating carbonium cations upon heating to an elevated temperature. Initiators of this type are known as "heat-latent cationic polymerization initiator". Cation-polymerizable resins such as epoxy resins containing the heat-latent initiator are, therefore, normally inactive but capable of curing at a temperature above the cleaving temperature of the initiator. This provides a heat-curable, one-component epoxy resin composion having a greater storage-stability and a longer pot life. Japanese Laid Open Patent Application (Kokai) No. 96169/88 and U.S. Patent No.5,070,161, both assigned to the assignee of this application, disclose heat-latent cationic polymerization initiators having an N-benzyl-pyridinium structure. Unfortunately, the prior art heat-latent initiators suffer from a problem that their decomposition products are malodorous or their cleaving temperature is relatively high. This problem makes them impractical to use in coating compositions where such malodor or high baking temperatures are not desirable. Accordingly, a strong need exists for a heat-latent cationic polymerization initiator which may eliminate or ameliorate this problem. DISCLOSURE OF THE INVENTION This invention provides, as a heat-latent cationic polymerization initiator, a quarternary ammonium salt of the formula I: wherein R 1 is 4-methylbenzyl or 4-methoxybenzyl; R 2 - R 5 and R 7 - R 10 are each a hydrogen atom; R 6 is methyl and Y - is an anion of the formula MX - / n wherein M is Sb, B or P, X is fluorine, an n equals to the valence of element M plus 1. The compounds of the present invention may be synthesized by reacting a compound of the formula: R 1 -Y' wherein R 1 is as defined and Y' is a halogen atom with a bicyclic amide acetal of the formula II: wherein all symbols are as defined, and then exchanging the halide anion of the resulting quarternary ammonium halide with an appropriate anion. The bicyclic amide acetal of the formula II has a 2, 3, 5, 6-tetrahydroxazolo-[2,3-b] oxazole nucleus of the formula: and may be synthesized by reacting a nitrile with a dialkanolamine as reported in e.g. German Patent No. 2,344,607. The quarternary ammonium salts of the present invention are thermally cleaved at an elevated temperature to produce a carbonium cation or proton when an excess of water is present. However, they are substantially inactive at ambient temperatures. Therefore, they may be used as a curing or polymerization catalyst in one-component epoxy-or proton-catalyzed resin compositions where a prolonged storage stability as well as odorless decomposition products are desired. The following examples are intended to further illustrate the present invetion without limiting thereto. Example 1 4-(4-Methoxybenzyl)-7a-methyl-2, 3, 5, 6-tetrahydroxazolo [2, 3-b] oxazolium hexafluoroantimonate 12.9g (0.1 mole) of 7a-methyl-2, 3, 5, 6-tetrahydroxazolo [2, 3-b] oxazole and 15.7g (0.1 mole) of 4-methoxybenzyl chloride were reacted in 40 ml of methanol at 40°C for 20 hours. After the reaction, the solvent was evaporated in vacuo and the residue was extracted with ether/water to remove unreacted reactants in the etherial layer. To the aqueous layer containing the resulting oxazolium chloride was added 25.87g (0.1 mole) of sodium hexafluoroantimonate. The resulting crystals were suction filtered, washed and dried to give the title compound. NMR:2.0 ppm (s, 3H, Me), 3.6 ppm (s, 3H, MeO), 3.9-4.8 ppm (m, 8H,CH 2 ), 7.0-7.1 ppm (d, 2H, Ph), 7.6-7.7 ppm (d, 2H, Ph). Example 2 4-(4-Methylbenzyl)-7a-methyl-2, 3, 5, 6-tetrahydroxazolo [2, 3-d] oxazolium hexafluorophosphate Analogous to Example 1, the title compound was prepared starting from 7a-methyl-2, 3, 5, 6-tetrahydroxazolo [2, 3-b] oxazole, 4-methylbenzyl chloride and sodium hexafluorophosphate. NMR:2.0 ppm (s, 3H, Me), 2.3 ppm (s, 3H, Me), 3.9-4.8 ppm (m, 8H, CH 2 ),7.2-7.3 ppm (d, 2H, Ph), 7.5 ppm (d, 2H, Ph) Example 3 4, 7a-dimethyl-2, 3, 5, 6-tetrahydroxazolo [2, 3-b] oxazolium tetrafluoroborate Analogous to Example 1, the title compound was prepared starting from 7a-methyl-2, 3, 5, 6-tetrahydroxazolo [2, 3-b] oxazole, methyl iodide and sodium tetrafluoroborate. NMR:1.7 ppm (s, 3H, Me), 3.2 ppm (s, 3H, Me), 3.7-4.5 ppm (m, 8H, CH 2 )

Claims: A quarternary ammonium salt of the formula I: wherein R 1 is 4-methylbenzyl or 4-methoxybenzyl; R 2 - R 5 and R 7 - R 10 are each a hydrogen atom; R 6 is methyl and Y - is an anion of the formula MX - / n wherein M is Sb, B or P, X is fluorine, an n equals to the valence of element M plus 1. The quarternary ammonium salt of Claim 1, which is 4-(4-methoxybenzyl)-7a-methyl-2, 3, 5, 6-tetrahydroxazolo [2, 3-b] oxazolium hexafluoroantimonate. The quarternary ammonium salt of Claim 1, which is 4-(4-methylbenzyl)-7a-methyl-2, 3, 5, 6-tetrahydroxazolo [2, 3-b] oxazolium hexafluorophosphate. The quarternary ammonium salt of Claim 1, which is 4, 7a-dimethyl-2, 3, 5, 6-tetrahydroxazolo [2, 3-b] oxazolium tetrafluoroborate.

Inventors: NAKANO SHINJI, URANO SATOSHI, NAKANO, SHINJI, URANO, SATOSHI
Applicants: NIPPON PAINT CO LTD, NIPPON PAINT CO., LTD.
Application year: 1992
Main classification: C07D498
IPC codes: C07D498, C08G59, C08F4