Novel hydrazine compound, process for the preparation of the same, and non-linear optical organic material

Abstract: A novel hydrazine compound represented by the formula (I) is disclosed. Also disclosed are a process for preparing the novel hydrazine compound comprising reacting a specific hydrazine compound and a specific acid halide, a nonlinear optical organic material comprising the hydrazine compound represented by the above formula (I), and a nonlinear optical organic element comprising the nonlinear optical organic material. The nonlinear optical organic material shows excellent nonlinear optical effect, and the material is favorably applied to nonlinear optical organic elements such as an optical wavelength conversion element and an electrooptical element.

Description: The present invention relates to the use of a hydrazine compound as a nonlinear optical organic material used in the field of optical information communication or optical information processing, and a nonlinear optical element comprising the nonlinear optical organic material, such as an optical wavelength conversion element or an electrooptical element. In the fields of optical information communication, optical information processing, etc., nonlinear optical organic materials have been recently paid attention. The nonlinear laser materials mean materials showing such nonlinear optical effects that they convert a light of a laser into a light having different wavelength and they are varied in the refractive index under application of electric voltage. Particularly, second-order nonlinear optical organic materials having such effect that they convert a light of a laser into a light having a wavelength of 1/2 of the laser wavelength (second harmonic generation) have been paid much attention as materials far superior to inorganic materials since the nonlinear optical organic materials were reported (ACS Symposium Series 233, 1983). For example, KTiOPO 4 (i.e., KTP) is known as the typical inorganic material, but development of a nonlinear optical organic material having higher nonlinear optical properties than KTP is expected. The second-order nonlinear optical organic materials include those containing an aromatic ring, an electron donating substituent group and an electron accepting substituent group and having such a structure that π electrons of the aromatic ring are polarized by the electron donating substituent group and the electron accepting substituent group in the molecule. The materials of this type are assumed to have extremely enhanced nonlinear optical response because nonlinear optical properties are produced on the π electron sites. However, para-nitroaniline which is expected to have high nonlinear optical response takes such a structure that the adjacent two molecules are inverted to each other when it is processed to be in the form of single crystal, this single crystal being essential for the nonlinear optical elements such as an optical wavelength conversion element and an electrooptical element in the practical use, resulting in losing of the nonlinear optical properties. That is, the nonlinear optical organic materials tend to lose the nonlinear optical properties when the adjacent molecules become to be centrally symmetric. For this reason, organic compounds have been synthesized in which is introduced a substituent group for removing the symmetry of the adjacent molecules or a substituent group for imparting optical activity. For example, 2-methyl-4-nitroaniline synthesized as above has been confirmed to show high nonlinear optical properties. The nonlinear optical organic materials tend to have higher nonlinear optical properties as the intramolecular polarizabilities thereof become higher, but when the intramolecular polarizabilities become too high, transference of electric charge occurs, and thereby the materials lose transparency. Further, the wavelength of the second harmonic generation and the maximum absorption wavelength λ max of the nonlinear optical organic material are coincident with each other, so that the second harmonic generation cannot be efficiently taken out. For obtaining nonlinear optical organic materials, there have been proposed compounds in which a nitro group having high acceptability and an amino group having highly electron donating properties are incorporated at the both ends of a linear molecule such as stilbene. However, these compounds have such problems that the adjacent molecules are apt to be centrally symmetric and the transparency is not so high. In order to solve those problems, various methods such as a method of limiting the length of the π electron conjugation system in the molecule and a method of incorporating a hetero atom into the aromatic ring have been tried, but any absolute solution to the problems has not been found out yet. Further, there is other problem that any nonlinear optical organic material in a form of single crystal having suitable size for using as the nonlinear optical element cannot been obtained by the conventional processes. That is, almost all of the conventional nonlinear optical organic materials are extremely small sized needle crystals or single crystals having less than 1 mm 3 , and a nonlinear optical organic material of single crystal having 1 mm 3 , especially more than 5 mm 3 , has been hardly obtained conventionally. Owen, J.R. et al , (J. Materials Science, 12 , 743-6 1977) describes the chemical preparation and crystal growth of 1-formyl 2(4-nitrophenyl) hydrazine. Its refractive indices, crystal structure, optical absorption coefficients and electro optic half-wave voltages are reported. Barinova, V.N. et al (Khim.-Farm. Zh. 22 (11) 1343-7 (1988)) describes the N-acylation of nitrophenyl hydrazines with acyl anhydrides and the subsequent N-acylation of the product for use as an anti-inflammatory. JP-A-201 8549 describes the formation of an image by treating a photosensitive material with a developing solution in the presence of a hydrazine compound. Jain, K. et al (IEEE. J. Quantum Electronics, QE-17 , (9) (1981)), describes the investigation of non-linear organic materials, such as 1-(2,4-dinitrophenyl)semicarbazide. Hegarty, A.F., et al (J. Chem. Soc. Perkin 2 (1972) 1381-6) describes the hydrolytic conversion of N-(4-nitrophenyl)-alkanohydrazonyl bromides into the corresponding alkyl hydrazides. JP-A-228 7536 relates to the preparation of 4-nitrophenyl hydrazonyl compounds from a hydrazine compound and an acid chloride. OBJECT OF THE INVENTION The present invention is made in the light of such circumstances as mentioned above, and the object of the invention is to provide the use of a hydrazine compound employable for the above-mentioned nonlinear optical materials, a process for preparing the hydrazine compound, and a nonlinear optical organic material in which the adjacent molecules are hardly made centrally symmetric and which shows high transparency and excellent nonlinear optical properties, particularly a nonlinear optical organic material of single crystal having more than 1 mm 3 when the material is a single crystal. Further, the object of the invention is to provide a nonlinear optical element comprising the nonlinear optical organic material, such as a wavelength conversion element or an electrooptical element, and an optical modulation device provided with the nonlinear optical element. The present invention provides use of a hydrazine compound of formula I as a non-linear optical material, wherein R 1 is hydrogen or methyl; R 4 is C 1 -C 4 alkyl which may be substituted by hydroxyl or interrupted by -O-, -CO-or -S-, C 2 -C 5 alkenyl or phenyl; B is a direct bond or an oxygen atom. The hydrazine compound represented by the above formula (I) is prepared by a process comprising a step of causing a hydrazine compound represented by the following formula (III) to react with an acid halide represented by the following formula (IV): wherein R 1 has the same meanings as defined above; X-CO-B-R 4 wherein R 4 and B have the same meanings as defined above, and X is a halogen atom. The nonlinear optical organic material used according to the invention comprises the hydrazine compound represented by the above formula (I). The nonlinear optical element of the invention is an element comprising the above-mentioned nonlinear optical organic material. BRIEF DESCRIPTION OF THE DRAWING Fig. 1 is a view illustrating an example of an optical modulation device according to the invention. Fig. 2 is a view illustrating another example of an optical modulation device according to the invention. Fig. 3 is a view illustrating another example of an optical modulation device according to the invention. Fig. 4 is a 1 H nuclear magnetic resonance (NMR) spectrum chart of 4'-nitrophenyl-ethylcarbohydrazide, a novel hydrazine compound of the invention. Fig. 5 is an infrared (IR) absorption spectrum chart of 4'-nitrophenyl-ethylcarbohydrazide, a novel hydrazine compound of the invention. Fig. 6 is a 1 H NMR spectrum chart of 4'-nitrophenyl-n-propylcarbohydrazide, a novel hydrazine compound of the invention. Fig. 7 is an IR absorption spectrum chart of 4'-nitrophenyl-n-propylcarbohydrazide, a novel hydrazine compound of the invention. Fig. 8 is a 1 H NMR spectrum chart of 4'-nitrophenyl-t-butylcarbohydrazide, a novel hydrazine compound of the invention. Fig. 9 is an IR absorption spectrum chart of 4'-nitrophenyl-t-butylcarbohydrazide, a novel hydrazine compound of the invention. Fig. 10 is a 1 H NMR spectrum chart of methyl-3-(p-nitrophenyl)carbazate, a novel hydrazine compound of the invention. Fig. 11 is an IR absorption spectrum chart of methyl-3-(p-nitrophenyl)carbazate, a novel hydrazine compound of the invention. Fig. 12 is a 1 H NMR spectrum chart of ethyl-3-(p-nitrophenyl)carbazate, a novel hydrazine compound of the invention. Fig. 13 is an IR absorption spectrum chart of ethyl-3-(p-nitrophenyl)carbazate, a novel hydrazine compound of the invention. Fig. 14 is a 1 H NMR spectrum chart of n-propyl-3-(p-nitrophenyl)carbazate, a novel hydrazine compound of the invention. Fig. 15 is an IR absorption spectrum chart of n-propyl-3-(p-nitrophenyl)carbazate, a novel hydrazine compound of the invention. Fig. 16 is a 1 H NMR spectrum chart of 4'-nitrophenyl-methoxyacetyl carbohydrazide, a novel hydrazine compound of the invention. Fig. 17 is an IR absorption spectrum chart of 4'-nitrophenyl-methoxyacetyl carbohydrazide, a novel hydrazine compound of the invention. Fig. 18 is a 1 H NMR spectrum chart of 4'-nitrophenyl-3-methylthiopropyl carbohydrazide, a novel hydrazine compound of the invention. Fig. 19 is an IR absorption spectrum chart of 4'-nitrophenyl-3-methylthiopropyl carbohydrazide, a novel hydrazine compound of the invention. Illustration of numerical symbols 10, 20: second harmonic generation device 30: optical modulation device 11, 21, 31: laser beam source 12, 14, 22, 32: condenser lens 13: nonlinear optical element 15: infrared rays cut-off filter 23: core material 24: cladding material 33: wave-guiding path 34: substrate 35: electrode DETAILED DESCRIPTION OF THE INVENTION The hydrazine compounds used according to the invention, the process for preparing the hydrazine compounds and the nonlinear optical organic material of the invention are described in detail hereinafter. The hydrazine compounds used according to the invention are represented by the above-mentioned formula (I). Concrete examples of the hydrazine compound are the following compounds (1) to (26). The hydrazine compound represented by the above formula (I) is prepared by conducting a condensation reaction of a hydrazine compound having the above formula (III) and an acid halide represented by the above formula (IV) (preferably acid chloride), preferably in the presence of a base. Examples of the base employable for the reaction include pyridine, trimethylamine and triethylamine. Of these, particularly preferred is pyridine or trimethylamine. These bases may be used in combination. The reaction to produce the above-mentioned hydrazine compound presented by the formula (I) is illustrated below using a hydrazine compound represented by the following formula (V) and acid chloride represented by the following formula (VI) as starting materials: Cl-CO-B-R wherein B is a direct bond or an oxygen atom, and R is an alkyl group of 1 - 4 carbon atoms. In this case, the hydrazine compound represented by the formula (I) is synthesized by the reaction of the following formula. As is clear from the reaction formula, HCl is produced in the condensation of the hydrazine compound and the acid chloride, and it is necessary to neutralize HCl to advance the reaction. For neutralization of HCl, a base is generally used in an amount of 1.0 to 5 mol, preferably 2 to 5 mol, per 1 mol of the hydrazine derivative or the acid chloride. The reaction is carried out generally in a liquid phase. In this reaction, a solvent which is chemically inert to the hydrazine derivative and acid chloride used as the starting materials and also inert to the resulting carbohydrazide derivative and capable of dissolving the hydrazine derivative and the acid chloride is used. Examples of the solvents include various solvents such as aromatic hydrocarbon solvents, aliphatic saturated hydrocarbon solvents, aliphatic saturated halogenated hydrocarbon solvents, aliphatic unsaturated hydrocarbon solvents and ether solvents. Particularly preferred are dichloromethane and THF. These solvents can be used singly or in a mixture of two or more kinds. The above-mentioned reaction is carried out at a temperature generally in the range of -20 to 100 °C, preferably in the range of 0 to 100 °C. Further, the reaction can be carried out at a pressure in the range of a reduced pressure to 58,8 bar (60 kg/cm 2 ), but it is preferably carried out at a pressure of 0 - 29,4 bar (0 to 30 kg/cm 2 ), more preferably 0 - 4,9 bar (0 to 5 kg/cm 2 ). The reaction time is appropriately determined in accordance with the reaction temperature, the reaction pressure, etc, and is not specifically limited, but the reaction time is generally in the range of 5 to 100 hours, preferably 1 to 10 hours. The reaction is normally conducted in an inert atmosphere such as an argon atmosphere or a nitrogen atmosphere. The hydrazine compound represented by the formula (I) according to the invention can be also obtained by a dehydration reaction of a hydrazine compound and a carboxylic acid. In this dehydration reaction, a dehydrating agent such as DCC (N,N'-dicyclohexylcarbodiimide) is employed. The nonlinear optical organic material according to the invention comprises the hydrazine compound represented by the above formula (I). By linking the nitro group to the phenyl group, the phenyl group is polarised thereby to accelerate polarization of the whole compound represented by the formula (I). In the compounds as mentioned above, R 1 is preferably configured at the position so that the adjacent molecules are not made centrally symmetric. R 1 is preferably linked to the phenyl group at the ortho-position to the -NR 2 NR 3 CO- group. R 4 in the above formula (I) is C 1 to C 4 alkyl which may be substituted by hydroxyl or interrupted by -O-, -CO-or -S-, C 2 -C 5 alkenyl or phenyl. Each of the alkyl group and the alkenyl group may be of a straight-chain form or a branched-chain form, and may have a hydroxyl group and/or a halogen atom. B in the above formula (I) is a direct bond or an oxygen atom. When -BR 4 is an alkyl group, this alkyl group is preferably an ethyl group or a n-propyl group. When -BR 4 is an alkoxy group, this alkoxy group is preferably a methoxy group. In the case of using the hydrazine compound represented by the formula (I) as a nonlinear optical organic material, the hydrazine compound preferably has at least one heavy hydrogen. The nonlinear optical organic material used according to the invention is composed of a compound represented by the above formula (I), and used in the crystallized form for producing a nonlinear optical element. Generally, the compound represented by the formula (I) is used singly for the nonlinear optical organic material of the invention, but a plurality of the compounds represented by the formula (I) may be used therefor. The crystal of the compound represented by the formula (I) may be a co-crystal of the compound and other component having a similar crystalline structure to that of the compound, or it may be a polycrystal, but preferably it is a single crystal. Further, the nonlinear optical organic material according to the invention is a composite composed of the compound represented by the above formula (I) and a transparent polymer binder. The single crystal as mentioned above can be obtained, for example, by dissolving the compound represented by the formula (I) in an appropriate solvent such as dimethylformamide or ethanol and then vaporizing the solvent, or lowering the temperature of the resulting solution to crystallize the compound contained in the solution. Otherwise, the single crystal can be also obtained by heating and melting the compound of the formula (I) and then cooling the molten compound to crystallize the compound, or by vapor phase growing the compound of the formula (I) by means of vacuum deposition, molecular beam epitaxial method or the like. By the use of the nonlinear optical organic material of the invention, a large sized single crystal of rectangular parallelepiped having not less than 1 mm 3 can be obtained by the above-mentioned processes, and especially by the use of methyl-3-(p-nitrophenyl)carbazate (aforementioned compound (7)) in the compounds represented by the formula (I), a large sized single crystal of having not less than 5 mm 3 can be easily obtained. The large sized single crystal made of the nonlinear optical organic material of the invention is subjected to a cutting procedure and a processing procedure to prepare a nonlinear optical element of the invention. In the case of forming the nonlinear optical element of the invention from the thin film single crystal obtained as above, the thickness of the thin film single crystal is desired to be not less than 1 µm. The composite composed of the compound of one or more kinds represented by the above formula (I) and a transparent polymer can be obtained, for example, by a process comprising the steps of dispersing the compound of at least one kind represented by the formula (I) in a polymer matrix, then applying an electric voltage to the resulting dispersion, with heating of the dispersion at a temperature of not lower than the glass transition point, to orientate the above-mentioned compound contained in the dispersion, and cooling and solidifying the dispersion with keeping the orientation. The nonlinear optical element according to the invention can be obtained by processing the above-obtained composite composed of the compound of at least one kind represented by the formula (I) and the transparent polymer into a desired shape. The optical modulation device according to the invention is provided with the above-described nonlinear optical element of the invention, and is employed as a second harmonic generation device, an optical switch, etc Fig. 1 shows one example of the second harmonic generation device according to the invention. In Fig. 1, the second harmonic generation device 10 includes a laser beam source 11, a condensing lens 12, a nonlinear optical element 13, a condensing lens 14 and an infrared rays cut-off filter 15. In the second harmonic generation device 10, a laser beam released from the laser beam source 11 is converged on the nonlinear optical element 13 by the condensing lens 12. When the laser beam is incident on the nonlinear optical element 13, a light having a wavelength of 1/2 of the laser wavelength is generated by the nonlinear optical element, and the light containing a basic wave of the laser beam and the second-order harmonic wave is released from the nonlinear optical element 13. This light is converted into an approximately parallel light by the condensing lens 14. By passing of the approximately parallel light through the infrared rays cut-off filter 15, a light having the second harmonic is selectively output. A second harmonic generation device 20 shown in Fig. 2 includes a laser beam source 21, a condensing lens 22, a core material 23 made of the nonlinear optical organic element according to the invention, and a cladding material 24 made of a transparent substance having a refraction index different from that of the core material 23, such as a glass. The core material 23 is covered with the cladding material 24. In the second harmonic generation device 20, a laser beam released from the laser beam source 21 is incident on one end of the core material 23 by way of the condensing lens 22. The laser beam entered from one end of the core material 23 is transmitted within the core material 23. During the transmission of the laser beam within the core material 23, a second harmonic generation occurred, and a light having the wavelength of 1/2 of the input laser wavelength is output from the other end of the core material 23. An optical modulation device 30 shown in Fig. 3 includes a laser beam source 31, a condensing lens 32 and a substrate 34 provided with a wave-guiding path 33 made of the nonlinear optical organic element according to the invention. The wave-guiding path 33 is branched on the substrate 34 to form two branched paths having the same optical path length as each other, and these two paths get together again. On the both sides of one of the branched paths are arranged a pair of electrodes 35 connected to an external electric source (not shown). In the optical modulation device 30, a laser beam released from the laser beam source 31 is incident on one end of the wave-guiding path 33 by way of the condensing lens 32 and is branched along the above-mentioned branched paths. Then, the laser beams on the branched paths get together and output from the other end of the wave-guiding path 33. When an electric voltage is applied to a pair of the electrodes 35, the refraction index of the nonlinear optical organic material which forms the branched path sandwiched between a pair of the electrodes 35 varies, and thereby the phase of the laser beam passing through the branched path is modulated. As a result, the phase and the intensity of the output light which is a synthetic light of the laser beams passing through both of the branched paths can be changed. This optical modulation device can be utilized as an optical switch, etc. EFFECT OF THE INVENTION As described above, the nonlinear optical organic material used according to the invention is composed of the compound represented by the above formula (I). In the optical material, a field of resonance is given by the phenyl ring, and the molecular polarization and the molecular configuration are controlled with good balance owing to A and R 1 to R 4 . Moreover, the adjacent molecules are not made centrally symmetric, so that the nonlinear organic optical material shows excellent nonlinear optical effect. Accordingly, the nonlinear optical organic material used according to the invention can be favorably applied to nonlinear optical elements such as an optical wavelength conversion element and an electrooptical element utilizing the second-order nonlinear optical effect. EXAMPLE The present invention is further described by the following examples, but the examples are given by no means to restrict the invention. Example 1 Into a 300 ml three-necked flask were introduced 50 ml of dichloromethane and 1.54 g of p-nitrophenylhydrazine. To the mixture in the flask was added 5 ml (cc) of pyridine under stirring of the mixture at room temperature, and then 1.5 ml (cc) of propionyl chloride having been beforehand dissolved in dichloromethane was slowly dropped into the resulting mixture through a dropping funnel, to immediately give an yellow precipitate. The reaction liquid was further stirred at room temperature for 12 hours, and then completion of the reaction was confirmed by means of thin-layer chromatography. Thereafter, the excess propionyl chloride in the reaction liquid was hydrolyzed, and an aqueous solution of NaHCO 3 was added to the reaction liquid to separate the reaction liquid into an aqueous phase and an oily phase containing a large amount of the reaction product. To the obtained aqueous phase was added dichloromethane to extract the reaction product remaining in the aqueous phase into the dichloromethane, and the dichloromethane containing the reaction product was withdrawn. The dichloromethane containing the reaction product was mixed with the above-obtained oily phase, and the resulting mixture solution was dried under vacuum. The obtained reaction product was precipitated again using acetone, to obtain 1.30 g of a purified product. The purified product obtained as above had a melting point of 209 to 210 °C when measured in accordance with a DSC method. Further, the purified product was dissolved in DMSO (dimethyl sulfoxide). Using the resulting solution, a 1 H NMR spectrum of the purified product was measured. A chart of the obtained 1 H NMR spectrum is shown in Fig. 4. The results obtained by analysis of peaks of this chart are as follows. 1 H NMR (δ p.p.m.) 1.09 (t, 3H, 8Hz, -CH 3 ) 2.24 (q, 2H, 7Hz, -CH 2 -) 6.75 (d, 2H, 9Hz, ring proton) 8.07 (d, 2H, 9Hz, ring proton) 9.02 (s, 1H, -NH-) 9.93 (s, 1H, -NH-) Furthermore, an IR spectrum of the purified product was measured. A chart of the obtained IR spectrum is shown in Fig. 5. From the results obtained in the above, the purified product was identified to be 4′-nitrophenylethylcarbohydrazide (aforementioned compound (2)). Subsequently, a powder of the aforementioned compound (2) was measured on the SHG intensity by a powder method. In this measurement, an YAG laser was employed. The SHG intensity of the powder was 24 times of the SHG intensity of an urea powder measured in the same manner as above. Further, a powder of the aforementioned compound (2) was dissolved in a solvent of dimethylformamide (DMF), and the resulting solution was allowed to stand for about 10 days at room temperature. As a result, a single crystal having a size of 8 × 5 × 2 mm 3 was obtained. The size of the single crystal corresponded to about 5 times of the size of a single crystal obtained by growing 2-methylnitroaniline (MNA) in the similar manner. Furthermore, when the single crystal of the compound (2) was irradiated with an YAG laser (continuous wave, wavelength: 1,064 nm, output: 175 mW), a keen peak of a SH light (532 nm) corresponding to the phase matching was obtained only in the case of a specific incident angle. Then, the intensity of the SH light was measured. As a result, the obtained intensity was a large value which was 3 times of an intensity obtained in the case of using a KTP crystal (sample length: 5 mm). Example 2 Into a 300 ml three-necked flask were introduced 70 ml of dichloromethane and 0.8 g of p-nitrophenylhydrazine. To the mixture in the flask was added 3 ml (cc) of pyridine under stirring of the mixture at room temperature, and then 0.8 ml (cc) of n-butyl chloride having been beforehand dissolved in dichloromethane was slowly dropped into the resulting mixture through a dropping funnel, to immediately give an yellow precipitate. The reaction liquid was further stirred at room temperature for 12 hours, and then completion of the reaction was confirmed by means of thin-layer chromatography. Thereafter, the excess n-butyl chloride in the reaction liquid was hydrolyzed, and an aqueous solution of NaHCO 3 was added to the reaction liquid to separate the reaction liquid into an aqueous phase and an oily phase containing a large amount of the reaction product. To the obtained aqueous phase was added dichloromethane to extract the reaction product remaining in the aqueous phase into the dichloromethane, and the dichloromethane containing the reaction product was withdrawn. The dichloromethane containing the reaction product was mixed with the above-obtained oily phase, and the resulting mixture solution was dried under vacuum. The obtained reaction product was developed by means of column chromatography using acetone/dichloromethane (1/4 volume ratio) as a developing solution. The main component obtained by column chromatography was precipitated again using acetone, to obtain 1.35 g of a purified product. The purified product obtained as above had a melting point of 177 to 178 °C when measured in accordance with a DSC method. Further, a mass spectrum of the purified product was measured. As a result, m/Z of the purified product was 223 (100). Furthermore, the purified product was dissolved in DMSO (dimethyl sulfoxide). Using the resulting solution, a 1 H nucleus magnetic resonance spectrum of the purified product was measured. A chart of the obtained 1 H NMR spectrum is shown in Fig. 6. The results obtained by analysis of peaks of this chart are as follows. 1 H NMR (δ p.p.m.) 0.90 (t, 3H, 8Hz, -CH 3 ) 1.57 (q, 2H, 7Hz, -CH 2 -) 2.18 (t, 2H, 8Hz, -CH 3 ) 6.75 (d, 2H, 9Hz, ring proton) 8.07 (d, 2H, 9Hz, ring proton) 9.06 (s, 1H, -NH-) 9.93 (s, 1H, -NH-) Further, an IR absorption spectrum of the purified product was measured. A chart of the obtained IR absorption spectrum is shown in Fig. 7. From the results obtained in the above, the purified product was identified to be 4′-nitrophenyl-n-propylcarbohydrazide (aforementioned compound (3)). A powder of the obtained compound (3) was measured on the SHG intensity in the same manner as described in Example 1. As a result, the SHG intensity of this powder was 12.1 times of the SHG intensity of an urea powder measured in the same manner as above. Then, a single crystal of the aforementioned compound (3) was prepared in the same manner as described in Example 1. The obtained single crystal had a size of 10 × 6 × 4 mm 3 . Further, the single crystal of the compound (3) obtained as above was subjected to an X-ray structural analysis. As a result, the spatial group belonged to orthorhombic system (P2 1 2 1 2 1 ), and the lattice constants were as follows. a = 12.43 angstroms b = 19.46 angstroms c = 4.67 angstroms Furthermore, using the obtained single crystal, the intensity of the SH light was measured in the same manner as described in Example 1. As a result, the obtained intensity was a large value which was 3.5 times of an intensity obtained in the case of using a KTP crystal (sample length: 5 mm). Example 3 Into a 300 ml three-necked flask were introduced 50 ml of dichloromethane and 0.77 g of p-nitrophenylhydrazine. To the mixture in the flask was added 2.5 ml (cc) of pyridine under stirring of the mixture at room temperature, and then 0.9 ml (cc) of trimethylacetyl chloride having been beforehand dissolved in dichloromethane was slowly dropped into the resulting mixture through a dropping funnel, to immediately give an yellow precipitate. The reaction liquid was further stirred at room temperature for 12 hours, and then completion of the reaction was confirmed by means of thin-layer chromatography. Thereafter, the excess trimethylacetyl chloride in the reaction liquid was hydrolyzed, and an aqueous solution of NaHCO 3 was added to the reaction liquid to separate the reaction liquid into an aqueous phase and an oily phase containing a large amount of the reaction product. To the obtained aqueous phase was added dichloromethane to extract the reaction product remaining in the aqueous phase into the dichloromethane, and the dichloromethane containing the reaction product was withdrawn. The dichloromethane containing the reaction product was mixed with the above-obtained oily phase, and the resulting mixture solution was dried under vacuum. The obtained reaction product was developed by means of column chromatography using acetone/dichloromethane (1/4 volume ratio) as a developing solution. The main component obtained by column chromatography was precipitated again using acetone, to obtain 0.426 g of a purified product. The purified product obtained as above had a melting point of 166 to 167 °C when measured in accordance with a DSC method. Further, the purified product was dissolved in DMSO (dimethyl sulfoxide). Using the resulting solution, a 1 H NMR spectrum of the purified product was measured. A chart of the obtained 1 H NMR spectrum is shown in Fig. 8. The results obtained by analysis of peaks of this chart are as follows. 1 H NMR (δ p.p.m.) 1.21 (s, 9H, -(CH 3 ) 3 ) 6.71 (d, 2H, 9Hz, ring proton) 8.08 (d, 2H, 9Hz, ring proton) 8.96 (s, 1H, -NH-) 9.79 (s, 1H, -NH-) Furthermore, an IR absorption spectrum of the purified product was measured. A chart of the obtained IR absorption spectrum is shown in Fig. 9. From the results obtained in the above, the purified product was identified to be 4′-nitrophenyl-t-butylcarbohydrazide (aforementioned compound (5)). A powder of the obtained compound (5) was measured on the SHG intensity in the same manner as described in Example 1. As a result, the SHG intensity of this powder was 1.0 time of the SHG intensity of an urea powder measured in the same manner as above. Then, a single crystal of the aforementioned compound (5) was prepared in the same manner as described in Example 1. The obtained single crystal had a size of 5 × 3 × 1 mm 3 . Further, using the obtained single crystal, the intensity of the SH light was measured in the same manner as described in Example 1. As a result, the obtained intensity was a value which was 0.5 time of an intensity obtained in the case of using a KTP crystal (sample length: 5 mm). Example 4 Into a 300 ml three-necked flask were introduced 100 ml of dichloromethane and 0.77 g of p-nitrophenylhydrazine. To the mixture in the flask was added 2.50 ml (cc) of pyridine under stirring of the mixture at room temperature, and then 0.8 ml (cc) of methyl chloroformate having been diluted with dichloromethane was slowly dropped into the resulting mixture through a dropping funnel. As the reaction proceeded, precipitation of an yellow product was observed. The reaction liquid was further stirred at room temperature for 12 hours, and then completion of the reaction was confirmed by means of thin-layer chromatography. Thereafter, the excess methyl chloroformate in the reaction liquid was hydrolyzed, and an aqueous solution of NaHCO 3 was added to the reaction liquid to separate the reaction liquid into an aqueous phase and an oily phase containing a large amount of the reaction product. To the obtained aqueous phase was added dichloromethane to extract the reaction product remaining in the aqueous phase into the dichloromethane, and the dichloromethane containing the reaction product was withdrawn. The dichloromethane containing the reaction product was mixed with the above-obtained oily phase, and the resulting mixture solution was dried under vacuum. The obtained reaction product was precipitated again using acetone/dichloromethane, to obtain 0.36 g of a purified product. The purified product obtained as above had a melting point of 180 to 181 °C when measured in accordance with a DSC method, and had m/Z = 211 (100) by mass spectrum analysis. Further, the purified product was dissolved in DMSO (dimethyl sulfoxide). Using the resulting solution, a 1 H NMR spectrum of the purified product was measured. A chart of the obtained 1 H NMR spectrum is shown in Fig. 10. The results obtained by analysis of peaks of this chart are as follows. 1 H NMR (δ p.p.m.) 3.61 (s, 3H, -OCH 3 ) 6.84 (d, 2H, 9Hz, ring proton) 8.08 (d, 2H, 9Hz, ring proton) 9.00 (s, 1H, -NH-) 9.45 (s, 1H, -NH-) Furthermore, an IR absorption spectrum of the purified product was measured. A chart of the obtained IR absorption spectrum is shown in Fig. 11. From the results obtained in the above, the purified product was identified to be methyl-3-(p-nitrophenyl)carbazate (aforementioned compound (7)). A powder of the obtained compound (7) was measured on the SHG intensity in the same manner as described in Example 1. As a result, the SHG intensity of this powder was 19.5 times of the SHG intensity of an urea powder measured in the same manner as above. Then, a single crystal of the aforementioned compound (7) was prepared in the same manner as described in Example 1. The obtained single crystal had a size of 30 × 12 × 6 mm 3 . Further, the single crystal of the compound (7) obtained as above was subjected to an X-ray structural analysis. As a result, the spatial group belonged to orthorhombic system (P2 1 2 1 2 1 ), and the lattice constants were as follows. a = 11.48 angstroms b = 18.51 angstroms c = 4.70 angstroms Furthermore, using the obtained single crystal, the intensity of the SH light was measured in the same manner as described in Example 1. As a result, the obtained intensity was a large value which was 4 times of an intensity obtained in the case of using a KTP crystal (sample length: 5 mm). Example 5 Into a 300 ml three-necked flask were introduced 100 ml of dichloromethane and 0.77 g of p-nitrophenylhydrazine. To the mixture in the flask was added 2.50 ml (cc) of pyridine under stirring of the mixture at room temperature, and then 1.00 ml (cc) of ethyl chloroformate having been diluted with dichloromethane was slowly dropped into the resulting mixture through a dropping funnel. As the reaction proceeded, precipitation of an yellow product was observed. The reaction liquid was further stirred at room temperature for 12 hours, and then completion of the reaction was confirmed by means of thin-layer chromatography. Thereafter, the excess ethyl chloroformate in the reaction liquid was hydrolyzed, and an aqueous solution of NaHCO 3 was added to the reaction liquid to separate the reaction liquid into an aqueous phase and an oily phase containing a large amount of the reaction product. To the obtained aqueous phase was added dichloromethane to extract the reaction product remaining in the aqueous phase into the dichloromethane, and the dichloromethane containing the reaction product was withdrawn. The dichloromethane containing the reaction product was mixed with the above-obtained oily phase, and the resulting mixture solution was dried under vacuum. The obtained reaction product was precipitated again using acetone/dichloromethane, to obtain 0.56 g of a purified product. The purified product obtained as above had a melting point of 200 to 201 °C when measured in accordance with a DSC method, and had m/Z = 225 (100) by mass spectrum analysis. Further, the purified product was dissolved in DMSO (dimethyl sulfoxide). Using the resulting solution, a 1 H NMR spectrum of the purified product was measured. A chart of the obtained 1 H NMR spectrum is shown in Fig. 12. The results obtained by analysis of peaks of this chart are as follows. 1 H NMR (δ p.p.m.) 1.20 (s, 3H, -CH 3 ) 4.09 (s, 2H, -OCH 2 -) 6.72 (d, 2H, 9Hz, ring proton) 8.08 (d, 2H, 9Hz, ring proton) 8.98 (s, 1H, -NH-) 9.39 (s, 1H, -NH-) Furthermore, an IR absorption spectrum of the purified product was measured. A chart of the obtained IR absorption spectrum is shown in Fig. 13. From the results obtained in the above, the purified product was identified to be ethyl-3-(p-nitrophenyl)carbazate (aforementioned compound (8)). A powder of the obtained compound (8) was measured on the SHG intensity in the same manner as described in Example 1. As a result, the SHG intensity of this powder was 1.0 time of the SHG intensity of an urea powder measured in the same manner as above. Then, a single crystal of the aforementioned compound (8) was prepared in the same manner as described in Example 1. The obtained single crystal had a size of 5 × 3 × 1 mm 3 . Further, using the obtained single crystal, the intensity of the SH light was measured in the same manner as described in Example 1. As a result, the obtained intensity was a value which was 0.5 time of an intensity obtained in the case of using a KTP crystal (sample length: 5 mm). Example 6 Into a 200 ml twin-necked flask were introduced 50 ml of dichloromethane and 0.71 g of p-nitrophenylhydrazine. To the mixture in the flask was added 2.50 ml (cc) of pyridine under stirring of the mixture at room temperature, and then 0.8 ml (cc) of n-propyl chloroformate having been beforehand dissolved in dichloromethane was slowly dropped into the resulting mixture through a dropping funnel. As the reaction proceeded, precipitation of an yellow product was observed. The reaction liquid was further stirred at room temperature for 12 hours, and then completion of the reaction was confirmed by means of thin-layer chromatography. Thereafter, the excess n-propyl chloroformate in the reaction liquid was hydrolyzed, and an aqueous solution of NaHCO 3 was added to the reaction liquid to separate the reaction liquid into an aqueous phase and an oily phase containing a large amount of the reaction product. To the obtained aqueous phase was added dichloromethane to extract the reaction product remaining in the aqueous phase into the dichloromethane, and the dichloromethane containing the reaction product was withdrawn. The dichloromethane containing the reaction product was mixed with the above-obtained oily phase, and the resulting mixture solution was dried under vacuum. The obtained reaction product was precipitated again using acetone/dichloromethane, to obtain 0.35 g of a purified product. The purified product obtained as above had a melting point of 125 to 126 °C when measured in accordance with a DSC method. Further, the purified product was dissolved in DMSO (dimethyl sulfoxide). Using the resulting solution, a 1 H NMR spectrum of the purified product was measured. A chart of the obtained 1 H NMR spectrum is shown in Fig. 14. The results obtained by analysis of peaks of this chart are as follows. 1 H NMR (δ p.p.m.) 0.98 (s, 3H, -CH 3 ) 1.59 (s, 2H, -CH 2 -) 4.0 (t, 2H, 7Hz, -OCH 2 -) 6.72 (d, 2H, 9Hz, ring proton) 8.08 (d, 2H, 9Hz, ring proton) 8.98 (s, 1H, -NH-) 9.39 (s, 1H, -NH-) Furthermore, an IR absorption spectrum of the purified product was measured. A chart of the obtained IR absorption spectrum is shown in Fig. 15. From the results obtained in the above, the purified product was identified to be n-propyl-3-(p-nitrophenyl)carbazate (aforementioned compound (9)). A powder of the obtained compound (9) was measured on the SHG intensity in the same manner as described in Example 1. As a result, the SHG intensity of this powder was 2.6 times of the SHG intensity of an urea powder measured in the same manner as above. Then, a single crystal of the aforementioned compound (9) was prepared in the same manner as described in Example 1. The obtained single crystal had a size of 6 × 4 × 2.5 mm 3 . Further, using the obtained single crystal, the intensity of the SH light was measured in the same manner as described in Example 1. As a result, the obtained intensity was a value which was 0.8 time of an intensity obtained in the case of using a KTP crystal (sample length 5 mm). Example 7 Into a 300 ml three-necked flask were introduced 50 ml of dichloromethane and 4.62 g of p-nitrophenylhydrazine. To the mixture in the flask was added 5 ml (cc) of triethylamine under stirring of the mixture at room temperature, and then 4.5 ml (cc) of methoxyacetyl chloride was slowly dropped into the resulting mixture through a dropping funnel, to immediately give an yellow precipitate. The reaction liquid was further stirred at room temperature for 12 hours, and then completion of the reaction was confirmed by means of thin-layer chromatography. Thereafter, the excess methoxyacetyl chloride in the reaction liquid was hydrolyzed, and an aqueous solution of NaHCO 3 was added to the reaction liquid to separate the reaction liquid into an aqueous phase and an oily phase containing a large amount of the reaction product. To the obtained aqueous phase was added dichloromethane to extract the reaction product remaining in the aqueous phase into the dichloromethane, and the dichloromethane containing the reaction product was withdrawn. The dichloromethane containing the reaction product was mixed with the above-obtained oily phase, and the resulting mixture solution was dried under vacuum. The obtained reaction product was precipitated again using acetone, to obtain 5.735 g of a purified product (4′-nitrophenyl-methoxyacetyl carbohydrazide). The purified product obtained as above had a melting point of 149 to 150 °C when measured in accordance with a DSC method. Further, the purified product was dissolved in DMSO (dimethyl sulfoxide). Using the resulting solution, a 1 H NMR spectrum of the purified product was measured. A chart of the obtained 1 H NMR spectrum is shown in Fig. 16. The results obtained by analysis of peaks of this chart are as follows. 1 H NMR (δ p.p.m.) 4.02 (s, 2H, -CH 2 -) 4.13 (s, 3H, -OCH 3 -) 6.75 (d, 2H, 9Hz, ring proton) 8.07 (d, 2H, 9Hz, ring proton) 9.03 (s, 1H, -NH-) 10.14 (s, 1H, -NH-) Furthermore, an IR absorption spectrum of the purified product was measured. A chart of the obtained IR absorption spectrum is shown in Fig. 17. From the results obtained in the above, the purified product was identified to be 4′-nitrophenyl-methoxyacetyl carbohydrazide (aforementioned compound (12)). Example 8 Into a 300 ml three-necked flask were introduced 50 ml of dichloromethane and 1.53 g of p-nitrophenylhydrazine. To the mixture in the flask was added 3 ml (cc) of pyridine under stirring of the mixture at room temperature, and then 1.39 g of 3-methylthiopropyl chloride having been beforehand dissolved in dichloromethane was slowly dropped into the resulting mixture through a dropping funnel, to immediately give an yellow precipitate. The reaction liquid was further stirred at room temperature for 12 hours, and then completion of the reaction was confirmed by means of thin-layer chromatography. Thereafter, the excess 3-methylthiopropyl chloride in the reaction liquid was hydrolyzed, and an aqueous solution of NaHCO 3 was added to the reaction liquid to separate the reaction liquid into an aqueous phase and an oily phase containing a large amount of the reaction product. To the obtained aqueous phase was added dichloromethane to extract the reaction product remaining in the aqueous phase into the dichloromethane, and the dichloromethane containing the reaction product was withdrawn. The dichloromethane containing the reaction product was mixed with the above-obtained oily phase, and the resulting mixture solution was dried under vacuum. The obtained reaction product was precipitated again using methylene chloride/hexane mixed solvent, to obtain 1.91 g of a purified product (4′-nitrophenyl-3-methylthiopropyl carbohydrazide). The purified product obtained as above had a melting point of 126 to 127 °C when measured in accordance with a DSC method. Furthermore, the purified product was dissolved in DMSO (dimethyl sulfoxide). Using the resulting solution, a 1 H NMR spectrum of the purified product was measured. A chart of the obtained 1 H NMR spectrum is shown in Fig. 18. The results obtained by analysis of peaks of this chart are as follows. 1 H NMR (δ p.p.m.) 2.10 (s, 3H, -CH 3 ) 2.51 (t, 2H, 11Hz, -CH 2 -) 2.73 (t, 2H, 13Hz, -CH 2 -) 6.79 (d, 2H, 9Hz, ring proton) 8.04 (d, 2H, 9Hz, ring proton) 9.07 (s, 1H, -NH-) 10.03 (s, 1H, -NH-) Further, an IR absorption spectrum of the purified product was measured. A chart of the obtained IR absorption spectrum is shown in Fig. 19. From the results obtained in the above, the purified product was identified to be 4′-nitrophenyl-3-methylthiopropyl carbohydrazide (aforementioned compound (15)).

Claims: Use of a hydrazine compound of formula I as a non-linear optical material, wherein R 1 is hydrogen or methyl; R 4 is C 1 -C 4 alkyl which may be substituted by hydroxyl or interrupted by -O-, -CO-or -S-, C 2 -C 5 alkenyl or phenyl; B is a direct bond or an oxygen atom. Use according to claim 1 wherein R 1 is hydrogen and R 4 is an alkyl group of 1 to 4 carbon atoms. Use according to claim 1 or 2 wherein the material is bound with a transparent polymer binder. Use according to claim 1 or 2 wherein the material is a crystal having a thickness of 1 µm or more and a volume of 1mm 3 or more. An optical modulation device comprising a laser beam source, a condensing lens and a non-linear optical element comprising a non-linear optical material as defined in any one of the preceding claims, wherein said non-linear optical element is so arranged that a laser beam released from said laser beam source is converged on the element by the condensing lens.

Inventors: HAMA HIDEO, KOIKE TSUNEAKI, YAMANAKA TOORU, HAMA, HIDEO, KOIKE, TSUNEAKI, YAMANAKA, TOORU, Hama, Hideo, c/o MITSUI PETROCHEM. IND. LTD., Koike, Tsuneaki, c/o MITSUI PETROCHEM. IND. LTD., Yamanaka, Tooru, c/o MITSUI PETROCHEM. IND. LTD.
Applicants: MITSUI PETROCHEMICAL IND, MITSUI PETROCHEMICAL INDUSTRIES, LTD.
Application year: 1992
Main classification: C07C243
IPC codes: C07C323, G02F1, C07D213, C07C281, C07C243, C07D239