Catalyst granules, in particular for the oxidative dehydrogenation of methanol in order to yield formaldehyde

Abstract: A configuration of cylindrical catalyst granules displays a trilobed or triangular cross-section provided with three through-bores equidistant from each other, each of which through-bores has its axis parallel to the axis of the cylindrical granule.

Description: The present invention relates to a novel shape for catalyst granules. In particular, it relates to a cylindrical catalyst granule of the type displaying a cross-section with at least three points of contact with a circumscribed circumference. A catalyst in granular form for use in a fixed-bed reactor, is generally required to comply with the following requirements: --low resistance to gas flow (low pressure drop, with the height of catalytic bed being the same); --large actual surface-area, i.e., high ratio of surface area to volume; --high heat exchange coefficient between catalyst particles and reaction gas; -- good mechanical strength, in order to prevent catalyst particles from undergoing breakage. The catalysts which are normally used in fixed-bed catalytic processes display a spherical, solid-cylindrical or ring-like configuration, of various sizes. By using such shapes known from the prior art, the diffusion of the reactant gases inside the interior of catalyst particles and the back-diffusion of the reaction products into the interior of the particles result often to be very limited. This means that, inasmuch as in heterogeneous systems the reaction occurs more easily and in selective way on external catalyst surface, the catalysts having the shape known from the prior art are not used enough in a reaction. As a consequence, in order to achieve the desired conversion rates, large amounts of catalyst have to be used and, for that purpose, in the case of tube-bundle fixed beds, tubes have to be used, which have an adequate height. With the catalysts having the shapes known from the prior art, this requirement results in a further increase in pressure drops, because the empty spaces intervening between catalyst bodies are small. Furthermore, in exothermic reactions, which generate large heat amounts - such as oxidative dehydrogenation, oxidation, halogenation and hydrogenation reactions - a high value of coefficient of heat exchange between the catalyst and the gas feed is required, in order to secure an adequate removal of reaction heat, and consequently avoid an excessive overheating of the catalytic bed, which often damages the catalyst and/or reduces the catalytic performance thereof. In the case of the catalysts having the traditional shape, in order to accomplish a high heat exchange coefficient, the turbulence of the reaction gas on catalyst particles had to be increased, but such a contrivance would cause a further increase in pressure drops, with a consequent increase in operations costs. Catalysts with different from traditional shapes are disclosed in U.S. patent No. 4,441,990; which relates to tubular extruded granules having an essentially triangular or quadrangular, multilobed cross section. With such catalysts, some advantages are achieved in terms of breakage strength and pressure drop, but the results are really not very different from as obtainable with the traditional catalysts. EP-A-464 633 discloses supported catalysts wherein the carrier shows a cylindrical shape with at least one passing-through channel. The catalysts disclosed in EP-A-355 664 have a ring-like configuration with at least three internal radii. EP-A-417 722 describes supported catalysts with different cylindrical configuration presenting at least one passing-through bore. The above supported catalysts and the ring-like catalysts described in EP-A-355 664 do not allow to obtain high catalytic mass concentration per unit reaction volume. The yield of useful reaction products per unit volume is therefore reduced. The purpose of the present invention is of supplying a configuration for a catalyst granule, which makes it possible the results to be considerably improved, which can be obtained in terms of pressure drop, high ratio of surface area to volume and high heat exchange coefficient. According to the present invention, such a purpose is achieved thanks to the granule or particle displaying three through-bores having axes substantially parallel to each other and to the axis of the particle, and substantially equidistant from each other, as defined in the appended claims. Said through-bores have a circular cross section and, on the cross section of the particle, their axes define vertices of a substantially equilateral triangle, said vertices being orientated towards the points of contact of the cross section of the catalyst particle with the circumscribed circumference. Thanks to the above said characteristics, owing to the particular geometry of the granules, a high turbulence of the reaction gases on the same granules can be promoted under the same operating conditions as customarily adopted in industrial facilities. As said granules display a large free surface area of their cross section, they oppose a lower resistance to the gas flow, with consequent lower pressure drops. Furthermore, their having a short equivalent diameter [equivalent diameter = 6*(volume/total surface area)], results in said catalyst particles displaying a larger actual surface-area, i.e., a higher value of surface-area/volume ratio and, consequently, in a better contact of the reaction gases with the catalyst surface, which favours the conversion of the reactants, and limits the inner diffusion phenomena, with a consequent increase in selectivity. In fact, with the catalysts according to the present invention very high yields of useful product are obtained with half catalyst amounts per volume unit, as compared to catalysts with shapes known from the prior art The bulk density of these catalysts is indeed very low. According to the present invention, the catalyst particle displays substantially circular-cylindical lobes equal to each other, and co-axial with the through-bores. The shape of the catalyst according to the present invention lends itself to be used in a wide range of catalytic processes, such as, e.g., hydrogenation and dehydrogenation of organic compounds, alkylation or dealkylation of benzene derivatives, isomerization, conversion of olefins into methanol, thermooxidation of methane to yield olefins, for example. A particularly advantageous application of the catalyst according to the invention is -- when said catalyst is constituted by iron and molybdenum oxides - the use thereof in formaldehyde production process by means of the oxidative methanol dehydrogenation. According to such a process, one or more reactor(s) is(are) used in parallel, which are constituted by multi-tube bundles which contain the catalyst and operate within the temperature range of from 230 to 450°C. In such reactors, the heat developed during the reaction is exchanged through the walls, with a thermostatting fluid caused to circulate outside the tubes. The reaction tubes have small enough inner diameters (15 - 25 mm) and the circulation of the diathermic fluid is so accomplished, as to cause the catalytic bed to operate under conditions which are as close as possible to isothermal conditions In the feed gases, methanol and oxygen are present at concentrations which are lower than 9 and 12% by volume, respectively, and in such a ratio to each other that in all reactor points, the oxygen content is always higher than as stoichiometric concentration as required by the reaction ( MeOH + ½O 2 → HCHO + H 2 O : in practice, when all methanol has reacted, oxygen concentration should exceed the value of 4% by volume) and, simultaneously, is always lower than that oxygen concentration which would cause the mixture to explode (Bureau of Mines Bull., 279 , 1939, pages 82-foll.). At reactor inlet, the molar fraction of methanol to be oxidized is limited to that value above which the exothermic character of the reaction would not allow a sufficient heat exchange to take place, in order to prevent dangerous local overheating of the catalyst bed to occur ("hot spots'). In such a type of process, as constituted as reported hereinabove, the shape and the size of the catalyst are of basic importance, so that the advantages deriving from the configuration according to the present invention are particularly considerable. Further advantages and characteristics of the catalyst according to the present invention will be evident from the following disclosure in detail, supplied for merely illustrative, non-limitative, purposes, and made by referring to the accompanying drawing, in which: Figure 1 is a plan view of a catalytic granule according to the present invention. Referring to the drawing, with 10 a cylindrical catalyst granule (pellet) is displayed, which is provided with three circular through-bores 12 arranged with their respective centres at the vertices of an equilateral triangle. In the form of practical embodiment illustrated in Figure 1, the pellet shows a trilobed cross section, with circular lobes 10a joining each other at longitudinal grooves 14 arranged along the side surface of the pellet. The bores 12, the diameter of which is indicated with d 1 , are coaxial with the circular lobes 10a and define, together with them, walls of thickness s . With "β", the angle is indicated which is formed between the line which joins the centres of two through-bores 12, and the line which joins the centre of one of said bores with the longitudinal groove defined by the lobes 10a coaxial with both said bores. With p , the pitch between the bores 12 (i.e., the distance between their centres) is indicated, and with d 2 the diameter of the lobes 10a is indicated (the radius of said lobes is indicated with R 1 ). The radius of the circumscribed circumference to the cross section of the pellet is indicated with the reference R . With M 1 and M 2 , the maximal and minimal dimensions of the cross section of the pellet are indicated. In Tables 1 and 2 enclosed with the instant disclosure, the size parameters are reported of catalyst pellets according to Figure 1 and in Table 2, the size parameters are reported of two traditional pellet types of ring-like shape, accomplished by using the fabrication technology as disclosed in the following examples. For some of such catalysts, for oxidative dehydrogenation of methanol the physical-chemical characterizations have been performed (Table 3). From the data relevant to the dimensions and shape of this type of pellets, the volume of the solid body corresponding to the shape of one single pellet ("solid space") and from this, by determining the bulk density of the catalyst, the expected weight for each pellet is calculated. The resulting expected weight compiles with the experimentally found weigh throughout the tested range of equivalent diameter values (2.32 - -1.76 mm). Of course, the bulk density depends on the fabrication pressure, the characteristics of the powder used as the starting material, and the modalities of calcination. The activity, selectivity and pressure drop values were determined in a through-flow reactor according to the procedure as described in the following examples. The operating conditions, and the results of catalyst performances are reported in Table 4. In the same Table, the results are reported which were obtained, under the same experimental conditions, with two different catalysts (Examples 13 and 14) having a traditional (ring-like) shape. By comparing the results, one may dearly infer that with the catalyst according to the present Invention, higher yields and lower pressure drops are obtained, with the catalyst volume being the same. If one considers that these novel catalysts display a lower bulk density (expressed as g/cm 3 ), the advantage results to be even larger. In particular, the catalysts display a high activity (Example 1; Table 4) even at relatively low temperatures; and high selectivity values (Example 9; Table 4) at relatively high temperatures. Examples 1-14 A powder of Fe 2 (MoO 4 ) 3 and MoO 3 was carefully mixed with stearic acid as inner lubricant, and the mixture was submitted to a forming-by-compaction process, by using a special mould in order to obtain pellets having the shape and dimensions as reported in Table 1 or moulds of traditional shape, in order to prepare the catalysts of Comparative Examples 13 and 14 (Table 2). The pellets were subsequently submitted to a calcination process at a temperature comprised within the range of from 500°C to 550°C, for 4 hours. The forming conditions were so regulated, as to obtain catalysts, after the calcination step, having the characteristics as reported in Table 3. For the determination of the values of activity, yield and pressure drops achievable with these catalysts, a steel reactor was used which has an inner diameter of 20.4 mm and a height of 1900 mm, arranged in vertical position inside a molten-salt thermostatting bath kept agitated by means of a nitrogen stream. The catalyst was packed inside the tubular reactor as a fixed bed of 700 mm of height. Through the reactor a gas stream was flown (in down-flow mode) at a linear speed of 1.5 Nm/sec and with a total inlet pressure of 950 mm Hg (1.25 bars), containing a methanol concentration of 6% by volume, and an oxygen concentration of 9.5% by volume. Downstream from the reactor, the outlet gas pressure was determined in order to calculate the pressure drops (Δp). The temperature of the molten salt bath was so adjusted as to reach a methanol conversion of >98%. The reactor exiting reaction gases were analysed by gaschromatography, by using two "Fractovap" (ex Carlo Erba) gaschromatographs. The one of them used a Poropak-T column for CO 2 , CH 2 O, DME (dimethyl ether), H 2 O, unconverted MeOH determination, and on the other, O 2 , N 2 and CO were determined on a column of Type-A molecular sieves. The results are reported in Table 4. Table 2 Catalyst Code X Y Height (mm) 3.80 5.00 Outer diameter (mm) 4.00 5.00 inner diameter (mm) 2.00 2.50 Thickness (mm) 1.00 1.25 Surface area of solid cross section (mm 2 ) 9.42 14.73 Side surface area (mm 2 ) 71.63 117.81 Total surface area (mm 2 ) 90.48 147.26 Volume of space occupied by catalyst granule ("solid space") (mm 3 ) 35.81 73.63 Equivalent diameter (mm) 2.38 3.00 Free surface area of cross section (mm 2 ) 3.14 4.91

Claims: Catalytic material in form of granules of cylindrical shape displaying a cross section with three points of contact with the circumscribed circumference and endowed with three through-bores having a circular cross-section with axes which are substantially parallel to each other and to the axis of the granules and substantially equidistant from each other and defining on the cross-section of the granule vertices of a substantially equilateral triangle, the vertices being oriented towards the points of contact of the cross section with the circumscribed circumference, said granules having three substantially cylindrical-circular lobes equal to each other and coaxial with the through-bores. said granule having the following features : Catalytic material according to claim 1, obtained from powders comprising Fe 2 (Mo0 4 ) 3 and MoO 3 A process for the oxidative dehydrogenation of methanol to formaldehyde, characterized in that said process uses a fixed-bed reactor containing a catalytic material according to any one of claims 1 and 2.

Inventors: BRUSA MASSIMO, GUBITOSA GIUSEPPE, MERIGHI BERNARDO, VIOLA AUGUSTO, BRUSA, MASSIMO, GUBITOSA, GIUSEPPE, MERIGHI, BERNARDO, VIOLA, AUGUSTO
Applicants: SUED CHEMIE MT SRL, SUED CHEMIE MT S.R.L.
Application year: 1992
Main classification: B01J35
IPC codes: B01J35, B01J23, C07C45, C07B61, C07C47, B01J19