FINISHING COMPOSITION

Abstract: A finishing composition and the use of the composition for finishing fibre-glass fabric are disclosed. On the basis of dry weight, the composition contains about 60-95 % by weight of starch, about 4-30 % by weight of a hydrophobicity-imparting agent, about 1-10 % by weight of a metallic salt, and about 1-5 % by weight of citric acid. Preferably, the hydrophobicity-imparting agent is a paraffin wax, and the metallic salt is an aluminium salt, such as aluminium hydroxy chloride. The composition preferably is a two-component composition, in which the starch is combined with the citric acid to form a first component, and the paraffin wax is combined with the metallic salt to form a second component. After mixing of the components and dilution by water, the ready-to-use finishing composition is a suspension of 10-15 % by weight. Advantageously, the composition is used for finishing so-called bituminous fabric, i.e. fibre-glass fabric used for making roofing felt.

Description: FINISHING COMPOSITION The present invention relates to a finishing composi¬ tion. It is previously known to finish a textile material in order to improve one or more of its qualities. Thus, it is possible to improve e.g. the handle, the water resis¬ tance and the flame-proofness of the textile material by applying a suitable finishing composition. The textile material may be woven or non-woven and be made of natural and/or synthetic fibres. In particular, it is known to finish fibre-glass fab¬ ric in order to give the initially rather shapeless fabric a firmer and better handle. The finishing composition employed may also impart flame-proofness. If the fabric is to be exposed to moisture and damp, the finishing composi¬ tion may also impart hydrophobicity to the fabric. This is the case e.g. when glueing and/or painting woven wall¬ paper, and is of particular interest for so-called bitu- minous fabrics, i.e. fibre-glass fabrics currently used instead of paper or paperboard for making roofing felt. In the finishing of bituminous fabric, use has hit¬ herto been made of finishing compositions based on syn¬ thetic binders, such as polyvinyl alcohol, polyvinyl ace- tate and polyvinyl chloride, combined with hydrophobicity- imparting agents, such as paraffin. Quality requirements on roofing felt are extremely high, and have, in general opinion, only been met by finishing compositions based on synthetic binders imparting satisfactory water resistance and hydrophobicity. It has not been considered possible to use starch-base finishing compositions, since starch in itself has poor water resistance and hydrophobicity, and also is liable to be attacked by bacteria, fungi and mould, especially where the air is humid. The object of the present invention is to obviate the inconveniences mentioned above and provide a finishing composition which is to be applied to textile materials and which is based on starch but nevertheless imparts satisfactory water resistance and hydrophobicity to the textile material. According to the invention, this object is achieved by a finishing composition which, on the basis of dry weight, contains about 60-95% by weight of starch, about 4-30% by weight of a hydrophobicity-imparting agent, about 1-10% by weight of a salt of metals in groups 3a, 3b, 4a, 4b, 5a, 5b of the Periodic Table, and about 1-5% by weight of citric acid. Other features of the invention appear from the fol¬ lowing description and the appended claims. The main ingredient of the finishing composition according to the invention is starch, which may be based on various raw materials, such as potato, wheat, maize, waxy maize, tapioca barley, and/or combinations thereof. Further, the starch can be modified in different ways, e.g by acid degradation, oxidation, esterification, etherifi- cation, cross-linking, and/or combinations thereof. Pre- ferably, the starch is soluble in cold water, but also starch that is soluble in hot water can be used. Starch is the main ingredient in the finishing compo¬ sition according to the invention, and constitutes about 60-95% by weight, preferably about 75-85% by weight, and most preferred about 80% by weight of the composition, as based on dry weight. The hydrophobicity-imparting agent in the composition according to the invention makes up about 4-30% by weight, preferably about 16-22% by weight, and most preferred about 19% by weight of the composition, as based on dry weight. The hydrophobicity-imparting agent can be selected from known agents, such as oils, waxes and fluorinated, preferably perfluorinated, organic compounds. At present, paraffin wax is the most preferred hydrophobicity-impart- ing agent. The composition further contains 1-10% by weight, preferably about 4-8% by weight, and most preferred about 6% by weight of a salt of metals in groups 3a, 3b, 4a, 4b, 5a, 5b of the Periodic Table, i.e. the one referred to in the Handbook of Chemistry and Physics, 49th Edition, 1968, published by the Chemical Rubber Co. Generally, the metals at issue can form ions having a valency of 3 or more. The metals being part of the above groups include aluminium, zirconium and antimony. Aluminium is the metal currently preferred. It is assumed that the nature of the salt is not especially critical, but the salt can be chosen from those salts which are completely or partly dissociated in an aqueous solution. At present, aluminium hydroxy chlo¬ ride (Al 2 (OH) 5 C1.2H 2 0) is especially preferred. Under the conditions described, the metallic salt in the composition according to the invention is supposed to serve as a mor¬ dant for the starch component to make the latter adhere better to the textile material to which the finishing com¬ position is applied, and as a cross-linking agent for the starch component. Finally, also citric acid is a component of the com¬ position according to the invention. The citric acid con¬ stitutes about 1-5% by weight, preferably about 2-3% by weight, and most preferred about 2.5% by weight of the composition, as based on dry weight. The citric acid adjusts the pH of the composition, but probably performs other important functions as well, since it has been found in tests that only citric acid functions satisfactorily in the invention. The use of other acids, such as adipic acid, fumaric acid, maleic acid, oxalic acid as well as acetic acid, has given unsatisfactory results. It is pre¬ sumed that the citric acid forms a complex with metal ions of the metallic salt, but this is not absolutely certain. It should be pointed out that the sum of the indicat- ed contents in per cent of the components of the composi¬ tion amounts to 100% by weight. It has been found that it is advantageous to the pro¬ duction and handling of the finishing composition accord¬ ing to the invention to combine the starch with the citric acid to form one component, and to combine the hydrophobi- city-imparting agent with the metallic salt to form one component, so that the composition in practice is a two- component composition. The starch and the citric acid are combined by being mixed and dried together to a dry starch powder of which the citric acid forms part. The hydropho- bicity-imparting agent and the metallic salt are mixed in water to form an emulsion having a solids content of about 30-40% by weight, preferably about 34-36% by weight. When the composition is to be used for finishing tex¬ tile materials, the components are mixed in water to form a suspension having a solids content of about 10-30% by weight, preferably about 15-20% by weight. Normally, the starch is first dissolved in water, whereupon the other components are admixed. In the preferred mode of execu¬ tion, in which the starch is combined with the citric acid and the hydrophobicity-imparting agent is combined with the metallic salt, the starch and the citric acid are first dissolved in water, whereupon the hydrophobicity- imparting agent and the metallic salt are added as an emulsion. Conveniently, the ready-to-use composition contains a sufficient amount of an emulsifier to form a stable emul¬ sion. However, the amount of emulsifier is negligible in relation to the entire composition and is therefore not referred to in the following. When the finishing composition has been prepared as above, the suspension is applied to the textile material in known manner, e.g. by a foulard method, whereupon the thus-finished textile material is dried at about 140-160°C for about 1-3 min. The invention will now be elucidated further by the following, non-restricting Examples. EXAMPLE 1 Finishing compositions according to the invention were prepared. The starch component employed consisted of oxidised and acetylated potato/wheat starch of the type Perlgum SB from Lyckeby StarkelsefCradling .AB, Kristian- stad, Sweden. This starch also contained about 2.5% by weight of citric acid. The hydrophobicity-imparting agent and the metallic salt employed consisted of a combination of paraffin wax and aluminium hydroxy chloride as an aqueous emulsion having a solids content of about 34% by weight, this emulsion being marketed under the name of Perltex E by Lyckeby StSrkelseforadling .AB, Kristianstad, Sweden. Perltex E contains about 25% by weight of paraffin wax and about 8% by weight of aluminium hydroxy chloride, as based on the total Perltex E emulsion. In addition, it contains a negligible amount of emulsifier. Ready-to-use finishing compositions were prepared by first dissolving the starch powder in water and stirring it for about 0.5 h. Then, a given amount of the Perltex E emulsion was added under agitation, which continued until a homogenous suspension had been obtained. The solids con¬ tent of the prepared suspension was about 10-15% by weight. The composition of the different finishing compo¬ sitions appear from Table 1. The amounts of starch, citric acid, paraffin wax and aluminium salt are given within parentheses in Table 1. TESTS Perlgum SB (g) starch (g) (97.5) (117) (97.5) (97.5) (117) (97.5) citric acid (g) (2.5) (3) (2.5) (2.5) (3) (2.5) Perltex E (g) 40 60 60 80 80 100 paraffin wax (g) (10.4) (15.6) (15.6) (20.8) (20.8) (26) Al salt (g) (3.2) (4.8) (4.8) (6.4) (6.4) (8) Water to 1000 ml The resulting finishing suspensions had excellent flow properties and contained no agglomerates. All the suspensions showed thixotrope qualities. The suspension was subsequently used for finishing a textile material in the form of a fibre-glass fabric of the type used for bituminous fabrics. Finishing was per- formed by manually applying to the fibre-glass fabric and with the aid of a spreading rod such an amount of the sus¬ pension that the finished fabric contained about 15% by weight of the finishing composition after drying at about 150°C for 3 min. Then, samples were taken of the fibre- glass fabrics in the form of strips measuring 3 x 10 cm. These strips were put standing in coloured water in a 100-ml glass jar. Depending on the degree of water resis¬ tance or hydrophobicity of the finished fibre-glass fab¬ ric, the strips sink about 5-7 cm in the water at the beginning of the test. If the water resistance or hydro¬ phobicity is to be regarded as satisfactory, the fabric must not absorb any water above the surface of water when stored thus for 24 hours. If the fabric absorbs the water, the coloured water can be seen to rise in the fabric above the water surface. If the water resistance is extremely poor, the fabric under water will divide. When applying compositions 1-6, above, excellent results as to water resistance and hydrophobicity were obtained in all cases, and the hydrophobicity increased from composition 1 to composition 6. Especially advan- tageous results as to water resistance and hydrophobicity were obtained with compositions 3-5. When the citric acid was replaced with other organic acids and the tests were repeated, the results were unsa¬ tisfactory and involved e.g. gelation, agglomeration, as well as poor water resistance and hydrophobicity. The acids tested were acetic acid, adipic acid, fumaric acid, maleic acid and oxalic acid. EXAMPLE 2 Example 1 was repeated, but with the finishing compo- sitions indicated in Table 2. TESTS Perlgum SB (g) starch (g) citric acid (g) Perltex E (g) paraffin wax (g) Al salt (g) Water The finishing compositions in Tests 7 and 8 contained a high amount of starch and a low amount of hydrophobi¬ city-imparting agent, and consequently resulted in a lower water resistance and hydrophobicity than did the composi¬ tions in Tests 9 and 10 when applied to fibre-glass fab- ric, as indicated in Example 1.

Claims: CLAIMS 1. A finishing composition for textile materials, c h a r a c t e r i s e d in that it, on the basis of dry weight, contains about 60-95% by weight of starch, about 4-30% by weight of a hydrophobicity-imparting agent, about 1-10% by weight of a salt of metals in groups 3a, 3b, 4a, 4b, 5a, 5b of the Periodic Table, and about 1-5% by weight of citric acid. 2. A finishing composition as claimed in claim 1, c h a r a c t e r i s e d in that the hydrophobicity- imparting agent is a paraffin wax. 3. A finishing composition as claimed in claim 1 or 2, c h a r a c t e r i s e d in that the metal in the metallic salt is chosen from aluminium, zirconium and antimony. 4. A finishing composition as claimed in claim 3, c h a r a c t e r i s e d in that the metallic salt is an aluminium salt. 5. A finishing composition as claimed in claim 4, c h a r a c t e r i s e d in that the aluminium salt is aluminium hydroxy chloride. 6. A finishing composition as claimed in any one of the preceding claims, c h a r a c t e r i s e d in that it contains about 75-85% by weight of starch. 7. A finishing composition as claimed in any one of the preceding claims, c h a r a c t e r i s e d in that it is a two-component composition, the starch being com- bined with the citric acid, and the hydrophobicity-impart¬ ing agent being combined with the metallic salt. 8. A finishing composition as claimed in claim 7, c h a r a c t e r i s e d in that the hydrophobicity- imparting agent and the metallic salt are in the form of an aqueous emulsion of about 30-40% by weight. 9. A finishing composition as claimed in any one of the preceding claims, c h a r a c t e r i s e d in that the ready-to-use composition is a suspension of about 10-30% by weight. 10. Use of a finishing composition as set forth in any one of the preceding claims for finishing fibre-glass fabric.

Inventors: BJOERKLUND HANS, PETTERSSON LENA, BJOERKLUND, HANS, PETTERSSON, LENA
Applicants: SVERIGES STAERKELSEPRODUCENTER, SVERIGES STAERKELSEPRODUCENTER FOERENING UPA
Application year: 1992
Main classification: D06M15
IPC codes: C03C25, C09D103