Heat-resistant adhesive and method of adhesion by using adhesive

Abstract: The heat resistant adhesive of the invention comprises polyamic acid and/or polyimide which are prepared by using 1,3-bis(3-aminophenoxy)benzene as an aromatic diamine component and 3,3', 4,4'-biphenyltetracarboxylic dianhydride, 3,3',4,4'-benzophenonetetracarboxylic dianhydride and/or 3,3',4,4'-diphenylethertetracarboxylic dianhydride as tetracarboxylic acid dianhydrides, and further by blocking the polymer chain end with dicarboxylic anhydride or a monoamine compound ; or comprises a polyimide solution containing the polyimide in a good solvent. The adhesive of the invention is a heat-resistant adhesive capable of adhering under mild temperature/mild pressure conditions. The adhesive of polyimide solution can provide desired adhesion by simple procedures such as applying to the adherend and heating under pressure and exhibits excellent adhesive strength. Consequently, the heat-resistant adhesive of the invention is very useful for the adhesion of structural and electronic materials and other industrial materials.

Description: The present invention relates to a heat-resistant adhesive and a method of adhesion by using the adhesive. More particularly, the invention relates to a polyimide-base adhesive which can adhere under mild temperature and pressure conditions, is excellent in adhesion properties and heat resistance in particular, and can be used in the electric and electronic field, and to a method of adhesion by using the adhesive. Many heat-resistant adhesives composed of synthetic organic high polymers have conventionally been known as adhesives for various high performance materials used in the field of electronics, space and aeronautic equipment and transfer machinery. Adhesives which have high heat resistance are polybenzoimidazol-base and polyimide-base adhesives. Particularly, polyimide-based heat-resistant adhesives which have excellent heat resistance and adhesive strength have been disclosed in USP 4,065,345 and Japanese Laid Open Patent Sho 61-143,477. Although these heat-resistant adhesives are excellent in heat resistance and adhesive strength, adhesion must be carried out at high temperature under high pressure in order to obtain high adhesive strength. When these polyimide-base adhesives are used, a solution of polyamic acid precursor is applied to an adherend surface, subjected to solvent removal and imidization, dried, and adhered to another substrate at high temperature under high pressure. Alternatively, polyimide is processed into films or purified by separating in the form of powder, followed by inserting between the two adherend and adhering at high temperature under high pressure. Polyimide is a high heat-resistant polymer material obtained by polycondensation of aromatic diamine and aromatic tetracarboxylic dianhydride, and many kinds of polyimide have been known. Polyimides obtained by using 1,3-bis(3-aminophenoxy)benzene as a diamine component have been known, for example, as follows. (1) An acetylene radical terminated polyimide oligomer prepared from 1,3-bis(3-aminophenoxy)benzene, 3,3',4,4'-benzophenone tetracarboxylic dianhydride and 3-aminophenylacetylene(N. Bilow et al. USP 3,845,018 and 3,879,349). (2) A polyimide prepared by polycondensation of 1,3-bis(3-aminophenoxy)benzene and pyromellitic dianhydride(T.P. Gannett et al., USP 4,485,140). (3) Heat resistant adhesives prepared from 1,3-bis(3-aminophenoxy) benzene and various kinds of tetracarboxylic dianhydrides (Japanese Laid-Open Patent Sho 61-143,477 and 61-291,670). (1) is an addition type thermosetting polyimide in which the oligomer end is blocked with a 3-aminophenylacetylene radical and the terminal acetylene radical progresses a cross-linking reaction by heat treatment. (2) is a condensation type polyimide obtained by using 1,3-bis(3-aminophenoxy)benzene as a raw material monomer and characterized by using pyromellitic dianhydride as a tetracarboxylic dianhydride component. (3) is heat resistant adhesives composed of 1,3-bis(3-aminophenoxy)benzene and various kinds of tetracarboxylic dianhydrides. However, a reactive radical remains at the end of polymer chain and severe conditions such as high temperature and high pressure are required in order to obtain heat resistant adhesion. An object of the present invention is to provide a polyimide-base adhesive which can adhere under milder conditions as compared with conventional adhesion conditions and has excellent adhesion properties. Also the method of adhesion does not require a complex adhering operation. According to the invention there is provided a polyamic acid and/or polyimide capable of use as a heat-resistant adhesive which is blocked at the polymer chain end with an aromatic monoamine represented by the formula: Q-NH 2 in which Q is a monoaromatic radical, a condensed polyaromatic radical or a noncondensed aromatic radical where the aromatic groups are connected to each other by a direct bond or a bridge member, which consist of recurring structural units represented by the formula: in which Y is: or in which X is a direct bond, -CO- or -O-, and in which the amount of the aromatic diamine is from 0.8 to 0.999 mole per mole of the aromatic tetracarboxylic dianhydride, and the amount of the aromatic monoamine is from 2 to 8 moles per mole of the difference between the molar amounts of aromatic diamine and aromatic tetracarboxylic dianhydride. The invention also extends to a polyimide-based heat-resistant adhesive comprising an organic solvent solution of such a polyimide or polyamic acid. The polyimide according to the invention may contain the polyamic-acid precursor in the range giving no adverse effect on the characteristics of the heat-resistant adhesive of the invention. In the above polyamic acid or polyimide, the polymer chain end is preferably blocked in particular by using aniline as the aromatic monoamine. The polyimide used for the adhesive of the invention differs from known polyimide in the following points. The above described acetylene radical terminated polyimide oligomer (1) which is prepared from 1,3-bis(3-aminophenoxy)benzene, 3,3',4,4'-benzophenonetetracarboxylic dianhydride and 3-aminophenylacetylene differ in that the oligomer is addition type thermosetting polyimide wherein the oligomer end is blocked with 3-aminophenyl-acetylene and the terminal acetylene radical progresses a crosslinking reaction by heat treatment. The polycondensation type polyimide (2) which is prepared from 1,3-bis(3-aminophenoxy)benzene and pyromellitic dianhydride differs in that the tetracarboxylic acid dianhydride is pyromellitic dianhydride. The heat resistant adhesives (3) composed of 1,3-bis(3-aminophenoxy)benzene and various kinds of tetracarboxylic dianhydrides (Japanese Laid-Open Patent Sho 61-143,477 and 61-291,670) differs in that the reactive terminal radical remains at the end of the polymer chain and severe conditions such as high temperature and high pressure are required in order to obtain heat-resistant adhesion. The polyamic acid or polyimide of the invention can be obtained by polycondensation of 1,3-bis(3-aminophenoxy)benzene as an aromatic diamine component with one or more aromatic tetracarboxylic dianhydrides selected from 3,3',4,4'-diphenylethertetracarboxylic dianhydride, 3,3',4,4'-benzophenonetetracarboxylic dianhydride and 3,3',4,4'-biphenyltetracarboxylic dianhydride as aromatic tetracarboxylic dianhydride component. The aromatic diamine component which is used as a monomer in the invention is 1,3-bis(3-aminophenoxy)benzene (hereinafter referred to as APB) having the formula (8) : The aromatic tetracarboxylic dianhydride used as another monomer is the compound represented by the formula (9) : in which X is as defined above, which is 3,3',4,4'-biphenyltetracarboxylic dianhydride (hereinafter referred to as BPDA), 3,3',4,4',-benzophenonetetracarboxylic dianhydride (hereinafter referred to as BTDA) or 3,3',4,4'-diphenylethertetracarboxylic dianhydride (hereinafter referred to as ODPA). The aromatic tetracarboxylic diarhydride can be used singly or as a mixture. The adhesive prepared from the polyamic acid and/or polyimide of the invention comprises the above aromatic diamine component and aromatic tetracarboxylic dianhydride component as primary components. Exemplary aromatic monoamines which can be used to block the polymer chain end aniline, o-toluidine, m-toluidine, p-toluidine, 2,3-xylidine, 2,4-xylidine, 2,5-xylidine, 2,6-xylidine, 3,4-xylidine, 3,5-xylidine, o-chloroaniline, m-chloroaniline, p-chloroaniline, o-bromoaniline, m-bromoaniline, p-bromoaniline, o-nitroaniline, m-nitroaniline, p-nitroaniline, o-aminophenol, m-aminophenol, p-aminophenol, o-anisidine, m-anisidine, p-anisidine, o-phenetidine, m-phenetidine, p-phenetidine, o-aminobenzaldehyde, m-aminobenzaldehyde, p-aminobenzaldehyde, o-aminobenzonitrile, m-aminobenzonitrile, p-aminobenzonitrile, 2-aminobiphenyl, 3-aminobiphenyl, 4-aminobiphenyl, 2-aminophenyl phenyl ether, 3-aminophenyl phenyl ether, 4-aminophenyl phenyl ether, 2-aminobenzophenone, 3-aminobenzophenone, 4-aminobenzophenone, 2-aminophenyl phenyl sulfide, 3-aminophenyl phenyl sulfide, 4-aminophenyl phenyl sulfide, 2-aminophenyl phenyl sulfone, 3-aminophenyl phenyl sulfone, 4-aminophenyl phenyl sulfone, α-naphthylamine, β-naphthylamine, 1-amino-2-naphthol, 2-amino-1-naphthol, 4-amino-1-naphthol, 5-amino-1-naphthol, 5-amino-2-naphthol, 7-amino-2-naphthol, 8-amino-1-naphthol, 8-amino-7-naphthol, 8-amino-2-naphthol, 1-aminoanthracene, 2-aminoanthracene and 9-aminoanthracene. Aniline is usually preferred in these aromatic monoamines. The reaction for forming the polyimide is usually carried out in an organic solvent. Exemplary solvents which can be used include, for example, N-methyl-2-pyrrolidone, N,N-dimethylacetamide, N,N-dimethylformamide, 1,3-dimethyl-2-imidazolidinone, N,N-diethylacetamide, N,N-dimethylmethoxyacetamide, dimethyl sulfoxide, pyridine, dimethyl sulfone, hexamethylphosphoramide, tetramethylurea, N-methylcaprolactam, butyrolactam, tetrahydrofuran, 1,2-dimethoxyethane, bis(2-methoxyethyl) ether, 1,2-bis(2-methoxyethoxy)ethane, bis [2-(2-methoxy)ethoxy) ethyl ether, 1,3-dioxane, 1,4-dioxane, pyridine, picoline, dimethyl sulfoxide, dimethyl sulfone, o-cresol, m-cresol, p-cresol, cresylic acid, p-chlorophenol, phenol and anisole. These organic solvents can be used singly or as a mixture. The polyamic acid and/or polyimide for use in the heat-resistant adhesive of the invention are prepared from the above aromatic diamine and the aromatic tetracarboxylic dianhydride by the following process in the presence of the aromatic monoamine. (A) The polyamic acid precursor of the polyimide is obtained by reacting APB of the formula (8), the aromatic tetracarboxylic dianhydride of the formula (9) and the aromatic monoamine in the above organic solvent. The amount of APB is from 0.8 to 0.999 mole per mole of the aromatic tetracarboxylic dianhydride. The amount of the aromatic monoamine is preferably from 2a to 8a moles for a moles of the difference between APB and the aromatic tetracarboxylic dianhydride. When the amount of the APB is less than 0.8 mole per mole of the aromatic tetracarboxylic dianhydride, the polymerization degree of the polymer is insufficient and heat resistance of the adhesive is impaired. On the other hand, the amount of APB exceeding 0.999 mole makes blocking of the polymer chain end difficult and renders adhesion under mild temperature / mild pressure conditions impossible. When the amount of the aromatic monoamine is less than 2a moles, blocking of polymer chain end cannot be conducted satisfactorily and an adhesive capable of adhering under mild temperature and pressure conditions cannot be obtained. On the other hand, the amount of the aromatic monoamine exceeding 8a moles impairs heat resistance of the adhesive. Particularly preferred amount of APB is from 0.9 to 0.99 mole per mole of the aromatic tetracarboxylic dianhydride, and that of the aromatic monoamine is from 2a to 4a moles for a moles of the difference between APB and the aromatic tetracarboxylic acid dianhydride. In carrying out the process, APB, the aromatic tetracarboxylic dianhydride and the aromatic monoamine are added and reacted in the organic solvent by the following methods. (a) The aromatic tetracarboxylic dianhydride is reacted with APB and successively the aromatic monoamine is added to continue the reaction. (b) The aromatic tetracarboxylic dianhydride is reacted with the aromatic monoamine and successively APB is added to continue the reaction. (c) The aromatic tetracarboxylic dianhydride, APB and the aromatic monoamine are added and reacted at the same time. Any of the above method can be carried out. The reaction temperature for preparing the polyamic acid is usually 60 °C or less, preferably 50 °C or less. No particular limitation is imposed on the reaction pressure. The reaction can be satisfactorily carried out in the atmospheric pressure. The reaction time depends upon the kind of the aromatic tetracarboxylic dianhydride, kind of the solvent and reaction temperature. The reaction is usually carried out for a time enough to completed formation-of the polyamic acid. Sufficient reaction time is usually from 4 to 24 hours. The reaction gives precursor of the polyimide, the polyamic acid represented by the formula (11) : The polyamic acid thus-obtained is further imidized by heating at 100 to 300 °C to obtain polyimide. In the reaction, water generated by imidization can be removed by azeotropic distillation with toluene or other solvents. (B) The polyamic acid is prepared by the above process (A). Imidizing reaction is chemically carried out by the addition of an imidizing agent such as acetic anhydride to obtain polyimide. The imidizing reaction can be carried out, if desired, in the presence of a basic catalyst such as pyridine, picolines, imidazole, triethylamine and other tertiary amines. The imidizing reaction is carried out usually from room temperature to 200 °C, preferably from room temperature to 100 °C. Sufficient reaction time is from 0.5 to 24 hours. (C) In the preparation of polyamic acid by the above process (A), the aromatic tetracarboxylic dianhydride, APB and the aromatic monoamine are suspended or dissolved in the solvent and heated. Thus, the polyimide is obtained by simultaneously carrying out formation and imidization of the polyamic acid. The basic catalyst which can be used for the above process (B) can also be used for the imidizing reaction. Further, water generated in the imidizing reaction can be removed by azeotropic distillation with toluene or other organic solvents. The temperature of the imidizing reaction is usually from 80°C to the refluxing temperature of the solvent used, preferably from 80 to 200 °C. Sufficient reaction time is in the range of 0.5 to 24 hours. By one of the above processes (A) to (C), the polyimide according to the invention and represented by the formula (12) can be obtained: in which X is as defined above, The adhesive of the present invention comprises the polyamic acid and/or the polyimide thus obtained and can be applied to practical use by the following embodiments. (1) A varnish which substantially comprises the above polyamic acid of the invention and a good solvent of the polyamic acid is applied as the heat resistant adhesive. The term a varnish which substantially comprises the polyamic acid and a good solvent of the polyamic acid includes a solution obtained by dissolving polyamic acid in a solvent. The solvent used for the polyamic acid forming reaction is usually applied as intact to the solvent for dissolving the polyamic acid, and hence the varnish comprises as a primary component the polyamic acid obtained by reacting APB, the tetracarboxylic dianhydride, the aromatic monoamine in the organic solvent and can also contain the polyimide which is a cyclized product of the polyamic acid. Consequently, the polyamic acid containing solution includes a solution or suspension containing polyimide as one of the components. The adhesive having such embodiment exhibits excellent bonding effect by applying to adherend and successively converting the polyamic acid to the polyimide with a means such as heating. (2) An adhesive in the form of polyimide is the polyimide itself obtained by subjecting the polyamic acid to thermal or chemical dehydration-ring closure and thereafter processing, for example, into films or pellets. The adhesive can contain the polyamic acid as a part of the component. The adhesive is used by attaching to the adherend, heat-melting and pressing. (3) Polyimide is isolated from the reaction mixture containing the polyimide obtained in one of the processes (A) to (C). Polyimide is precipitated by pouring the reaction mixture into a lean solvent or adding the lean solvent to the reaction mixture. Alternatively, solvent, catalyst and other materials remained in the reaction system except polyimide are removed by heating and/or under reduced pressure. Thus-isolated polyimide is dissolved in a soluble solvent to prepare a solution of polyimide. The polyimide solution is substantially used as the heat-resistant adhesive. Exemplary solvents are the same as the above solvents used for the polymerization, and include N-methyl-2-pyrrolidone, N,N-dimethylacetamide, N,N-dimethylformamide, 1,3-dimethyl-2-imidazolidinone, N,N-diethylacetamide, N,N-dimethylmethoxyacetamide, dimethyl sulfoxide, pyridine, dimethyl sulfone, hexamethylphosphoramide, tetramethylurea, N-methylcaprolactam, butyrolactam, tetrahydrofuran, 1,2-dimethoxyethane, bis(2-methoxyethyl) ether, 1,2-bis(2-methoxyethoxy)ethane, bis [2-(2-methoxy)ethoxy] ethyl ether, 1,3-dioxane, 1,4-dioxane, pyridine, picoline, dimethyl sulfoxide, dimethyl sulfone, o-cresol, m-cresol, p-cresol, cresylic acid, p-chlorophenol, phenol and anisole. These organic solvents can be used singly or as a mixture. Solvents which are suitable for the object are selected from those solvents. The adhesive of the invention is used by dissolving the above-obtained polyimide in an organic solvent in an amount of from 1 to 50 % by weight, preferably from 5 to 30 % by weight. (4) In the preparation of the polyimide by one of the above processes (A) to (C), when the polyimide formed is dissolved in the solvent used for the polymerization and imidization reaction, the reaction mixture obtained after the imidizing reaction can be used as intact for the heat-resistant adhesive. Consequently, the polyamic acid precursor of the polyimide can be contained in the range giving no adverse effect on the characteristics of the adhesive of the invention. The heat-resistant adhesive of the invention can be used for adhesion by the following method. When the adhesive is a varnish containing the polyamic acid or the polyamic acid and polyimide which are prepared by the above process (A) or (C), the varnish is applied in a thin layer to an adherend to be laminated and successively heated at 100 to 300 °C for a prescribed time in the air. Thus, an excessive solvent is removed and the polyamic acid is converted-to more stable polyimide. Thereafter the adherend is pressed under pressure of 1 to 1000 kg/cm 2 at temperature of 100 to 400°C and cured at 100 to 400 °C to obtain firm adhesion. When the adhesive is a film or powder and is substantially composed of polyimide, the film or powder is inserted between the adherends and pressed under pressure of 1 to 1000 kg/cm 2 at temperature of 100 to 400 °C and cured at temperature of 100 to 400 °C to obtain firm adhesion. When the adhesive is a solution containing the polyimide in an organic solvent, the adhesive is applied to an adherend to be laminated and successively heated at temperature of 100 to 300 °C for a prescribed time to remove the solvent. In the case of heat-resistant adhesive of the above (4), the catalyst remained in the system is also removed together with the solvent. Thereafter the coated surface of the adherend is overlapped with another adherend and pressed under pressure of 1 to 1000 kg/cm 2 at temperature of 100 to 400 °C, preferably 150 to 300 °C to obtain firm adhesion of the adherends each other. As to application of the heat-resistant adhesive to the adherend surface to be laminated, good bonding effect can be obtained by applying to one adherend surface alone or by applying to both surfaces of the adherends. The heat-resistant adhesive of the invention can be used by impregnating the adhesive into a glass fiber cloth or a carbon fiber cloth with known methods and successively by inserting the thus-impregnated cloth between the adherends. Alternatively, the adhesive is applied to one of the adherend, a glass fiber cloth or a carbon fiber cloth is submerged into the coated layer of the adhesive and successively another adherend can be overlapped and pressed. Adhesion can also be carried out after chemically or physically treating the adherend surface. Methods of surface treatment include chemical etching with alkali, corona discharge treatment, ultraviolet light irradiation, radiation exposure, sandblasting, heat treatment, plasma treatment, abrasion, honing, plating, surface oxide treatment and degreasing. These methods of surface treatment can be carried out singly or in combination. Other resins can be added to the adhesive so long as giving no adverse effect on the characteristics of the heat resistant adhesive of the invention. The resins which can be added include, for example, nylons, polyacetal, polycarbonate, polyphenyleneoxide, polyethylene terephthalate, polysulfone, polyethyersulfone, polyarylate, polyamideimide, polyetherimide, polyetheretherketone, polyimide exclusive the polyimide of the invention, fluoro resin, polybismaleimide and epoxy resin. Various additives can be added to the heat-resistant adhesive of the invention in the range not impairing the object of the invention. Exemplary additives which can be added include solid lubricants such as molybdenum disulfide, graphite, boron nitride, lead monoxide and lead powder; reinforcements such as glass fiber, carbon fiber, aromatic polyamide fiber, potassium titanate fiber and glass beads; antioxidants, heat stabilizers, ultraviolet absorbers, flame retardants, auxiliary flame retardants, antistatics and colorants. The additives can be used singly or as a mixture. Example 1 To a reaction vessel equipped with a stirrer, reflux condenser and a nitrogen inlet tube, 32.2 g (0.1 mole) of 3,3',4,4'-benzophenonetetracarboxylic dianhydride and 245.6 g of N,N-dimethylacetamide were charged and stirred at the room temperature in the nitrogen atmosphere. To the solution thus obtained, 28.9 g (0.099 mole) of APB was added by portions with caution to prevent temperature rise of the solution and stirred for 20 hours at the room temperature. Thereafter 0.745 g (8×10 -3 mole) of aniline was added and further stirred for 4 hours. The polyamic acid thus obtained had an inherent viscosity of 0.73 d ℓ /g. To the polyamic acid solution, 40.8 g (0.4 mole) of acetic anhydride and 20.2 g (0.2 mole) of triethylamine were dropwise added and stirred for 10 hours at the room temperature. The reaction mixture obtained was poured into 1000 g of methanol with vigorous stirring and resulting precipitate was filtered, washed with methanol, and dried at 180°C for 12 hours. Polyimide powder thus obtained was 56.6 g (98 % yield) and had a glass transition temperature of 191°C according to DSC and an inherent viscosity of 0.74 d ℓ /g at 35 °C in a 0.5 % solution of a p-chlorophenol/phenol = 9/1 by weight mixture. A polyimide solution was prepared by dissolving 20 g of the polyimide powder in 80 g of N-methyl-2-pyrrolidone (concentration was 20%). The polyimide solution was applied to Kapton 200H (manufactured by E.I. Du Pont de Nemours & Co.) which was previously washed with ethanol, dried at 250 °C for 30 minutes in the nitrogen atmosphere, overlapped with a rolled copper foil having a thickness of 25 µm and pressed at 250 °C for 5 minutes under pressure of 50 kg/cm 2 . The coated layer of polyimide had thickness of 10 µm. The specimen had a 180° peel strength of 3.3 kg/cm at the room temperature in accordance with JPCA-BOM 01. The polyimide solution was applied to a cold rolled steel panel (JIS, G3141, spec/SD 25×100×1.6 mm), dried at 250 °C for 30 minutes in the nitrogen atmosphere. The coated steel panel was overlapped with another cold rolled steel panel and pressed at 250 °C for 5 minutes under pressure of 50 kg/cm 2 . The specimen had a tensile shear strength of 320 kg/cm 2 in accordance with JIS K 6848 and K 68501. The results are illustrated in Table 2. Examples 2 and 3 The same procedures as described in Example 1 were carried out except that 3,3',4,4'-benzophenonetetracarboxylic dianhydride was replaced by the tetracarboxylic acid dianhydrides illustrated in Table 1. The results are illustrated in Table 2. Example 4 The same procedures as described in Example 1 were carried out except that 0.745 g (8 × 10 -3 mole) of aniline was replaced by 1.578 g (8 × 10 -3 mole) of 4-aminobenzophenone. The results are illustrated in Table 2. Diamine g(mole) Tetracarboxylic dianhydride g(mole) Blocking agent g(mole) Polyamic acid inherent viscosity (dℓ/g) Polyimide inherent viscosity (dℓ/g) Ex. 1 APB 28.9 (0.099) BTDA 32.2 (0.1) Aniline 0.745(8× 10- 3 ) 0.73 0.74 Ex. 2 ↑ BPDA 29.40 (0.1) ↑ 0.79 0.78 Ex. 3 ↑ ODPA 31.00 (0.1) ↑ 0.85 0.84 Ex. 4 ↑ BTDA 32.20 (0.1) 4-Amino-benzophenone 1.578 (8 × 10 -3 ) 0.74 0.75 Kapton / copper foil Between cold rolled steel panels Application method 180° Peel strength (kg/cm) Application method Tensile shear strength (kg/cm 2 ) Ex. 1 Solution of polyimide powder 3.3 Solution of polyimide powder 320 Ex. 2 ↑ 3.0 ↑ 315 Ex. 3 ↑ 3.1 ↑ 305 Ex. 4 ↑ 3.3 ↑ 325

Claims: A polyamic acid and/or polyimide capable of use as a heat-resistant adhesive which is blocked at the polymer chain end with an aromatic monoamine represented by the formula: Q-NH 2 in which Q is a monoaromatic radical, a condensed polyaromatic radical or a noncondensed aromatic radical where the aromatic groups are connected to each other by a direct bond or a bridge member, which consist of recurring structural units represented by the formula: in which Y is: or in which X is a direct bond, -CO- or -O-, and in which the amount of the aromatic diamine is from 0.8 to 0.999 mole per mole of the aromatic tetracarboxylic dianhydride, and the amount of the aromatic monoamine is from 2 to 8 moles per mole of the difference between the molar amounts of aromatic diamine and aromatic tetracarboxylic dianhydride. A polyamic acid and/or polyimide as claimed in Claim 1 in which the aromatic monoamine is aniline. A polyimide-based heat-resistant adhesive comprising a solution of a polyimide as claimed in either preceding claim. A heat-resistant adhesive comprising a solution of a polyamic acid as claimed in either of claims 1 and 2. A method of adhering two pieces in which an adhesive comprising a polyamic acid and/or polyimide as claimed in either of claims 1 and 2 is used as the adherent. A method of adhering two pieces in which a solution as claimed in Claim 4 is applied as a thin layer to one piece, heated at 100 to 300°C to remove solvent and convert the polyamic acid to the corresponding polyimide, and thereafter that piece is pressed against the other piece under a pressure of 1 to 1000 kg/cm 2 at a temperature of 100 to 400°C. A method of adhering two pieces in which a solution as claimed in Claim 3 is applied to one piece and the two pieces are laminated and heated at a temperature of 100 to 300°C to remove the solvent. A method of adhering two pieces in which a film or powder of a polyimide as claimed in either of claims 1 and 2 is inserted between the two pieces, and the pieces are pressed together under a pressure of 1 to 1000 kg/cm 2 and at a temperature of 100 to 400°C.

Inventors: ASANUMA TADASHI, IIYAMA KATSUAKI, KAWASHIMA SABURO, OIKAWA HIDEAKI, TAMAI SHOJI, YAMAGUCHI AKIHIRO, ASANUMA, TADASHI, IIYAMA, KATSUAKI, KAWASHIMA, SABURO, OIKAWA, HIDEAKI, TAMAI, SHOJI, YAMAGUCHI, AKIHIRO
Applicants: MITSUI CHEMICALS INC, MITSUI CHEMICALS, INC.
Application year: 1992
Main classification: C08G73
IPC codes: C09J179, H05K3, C08G73