Ultrasonic motor with vibrating body and moving body driven thereby

Abstract: An ultrasonic motor which achieves uniform contact between the vibrating body and the moving body and features high output transfer efficiency and high reliability, and by which the manufacturing process for the moving body thereof can be simplified and the moving body made lighter. By comprising the moving body of a carbon fiber reinforced resin composite material reinforced by at least carbon fiber, and constructing the moving body with a both-side supported or single-side supported beam construction, elasticity according to the pressure of the ultrasonic motor can be imparted in the direction of pressure of the moving body. Thus, the undulations in the contact surface of the vibrating body and the moving body can be absorbed and stable, uniform contact can be assured, and long-term maintenance of a stable friction condition can be achieved.

Description: The present invention relates to an ultrasonic motor comprising a vibrating body comprised of an elastic base and a piezoelectric body fixed on said elastic base, a moving body press-contacted against said piezoelectric body by a spring force of a spring means, in which said moving body is driven by friction force between said moving body and said vibrating body by exciting a progressive wave of flexural vibration in said vibrating body. Such ultrasonic motors are known from FR-A-2 579 683 and EP-A-382 563. Ultrasonic motors in which driving forces are generated by exciting a flexual vibration in a vibrating body comprised of a piezoelectric element have gained wide attention in recent years. A prior art ultrasonic motor is described below with reference to Figures 11a and 11b. Fig. 11a is a partially cut perspective view showing essential parts of a conventional ring-shaped ultrasonic motor. Reference numeral 3 denotes a vibrating body comprised of a ring-shaped elastic base 1 with plural projections la and a ring-shaped piezoelectric element 2 attached to the bottom surface of the elastic body 1. Reference numeral 6 denotes a moving body which is comprised of a ring-shaped elastic body 4 with an abrasion resistant friction member 5 attached thereto. In this example of a conventional ultrasonic motor steel or stainless steel is usually used for the material of the elastic body 4, and the friction member 5 is bonded thereto with an adhesive or other means. Fig. 11b shows a schematic cross-sectional view of such conventional ring-shaped ultrasonic motor. The vibrating body 3 supported by a ring-shaped seat 7 and the moving body 6 are held in pressure contact by a ring-shaped disc spring 8 to form an ultrasonic motor thereby wherein the driving force is output at a bearing 9 attached to the moving body 6. The operation of such a conventional ring-shaped ultrasonic motor is described below with reference to Fig. 13 which shows that the moving body 6 and vibrating body 3 are held in pressure contact and a progressive wave of flexural vibration is excited in the vibrating body 3. The progressive wave of flexural vibration is generated as follows. At first, a longitudinal vibration is caused in the piezoelectric element 2 by applying two AC voltages with a predetermined phase shift to two sets of driving electrodes arranged thereto, and, since the elastic base 1 works to resist this longitudinal action, a progressive wave of flexural vibration is set up in the vibrating body 3 by the same effect as in a bimetal. Any given point on the surface of the vibrating body 3 follows an elliptical motion due to the progressive wave of flexural vibration. The projections la enlarge the lateral displacement of this elliptical motion (See ζ in Fig. 13). The moving body 6 pressed in friction contact with projections la of the vibrating body 3 is rotationally driven due to the enlarged lateral displacement. In such motors it is necessary to maintain a good contact between the moving body 6 and vibrating body 3 in order to guarantee a stable drive since the former is driven to rotate by friction forces exerted thereto. Thus, contact surfaces of the moving body 6 and vibrating body 3 must be finished to have a flatness of high precision better than several micron meters. Metal materials usually and ceramic materials sometime are used for the materials of the moving body 6 and vibrating body 3 to yield a rigidity such that the precision of flatness regarding contact surfaces is kept unchanged under pressure and a high precision of finishing. Secondly wear problems between contact surfaces of the moving body 6 and the vibrating body 3 are also important. Since a friction force is exerted between the contact surfaces during the operation of the ultrasonic motor, it is extremely important to minimize the wear due to the friction force in order to guarantee the stable operation of the ultrasonic motor. Wear of the contact surface worsens the flatness and the contact state thereof resulting in bad efficiency of the motor and generation of extraodinary noises. Further, power generated due to the wear lowers the credibility of the ultrasonic motor and a system including the same. The abrasion resistive friction element 5 mentioned above is used for countermeasure to the wear. In JP-A-62-58887 in the name of the assignee of this application, there is proposed a friction element made of a composite material of carbon fibre and resin. While high abrasion resistive materials quite different from materials used for the elastic body 4 are used for the friction element, it is also known to form the elastic body 4 from aluminum and the friction element 5 by oxidizing the surface of the elastic body 4 into an alumilite layer. However the friction element formed by the alumilite layer is far inferior at the abrasion resistivity when compared with the friction element disclosed in the above publication and, accordingly, it is impossible to guarantee the stable operation for a long period. There has been also proposed an ultrasonic motor wherein aluminum and aluminum alloy is used for the material of the moving body 6 and the same is formed to have a cross section of a predetermined configuration as shown in Fig. 12 (See, for example, JP-A-63-174581. This enables to realize a quiet motor with a high efficiency. However, the conventional ultrasonic motors are not satisfactry in efficiency, lifetime and manufacturing cost. As to the efficiency, only 30% has been attained in conventional motors the maximum. In order to increase the efficiency, it becomes necessary to increase the precision in finishing the contact surfaces of the moving body and the vibrating body. However, this contradicts to reduction of the manufacturing cost. FR-A-2 579 683 and EP-A-382 563, as already mentioned at the beginning, disclose an ultrasonic motor of the kind as defined in the preamble of claims 1 and 4. FR-A-2 579 683 discloses a vibration motor in which the moving body (rotor) is made of metal or ceramics. In order to obtain a smooth contact between the vibrating body and the moving body, a part of the rotor is made very thin or is provided with slits in order provide the necessary flexibility. As far as EP-A-382 563 is concerned, it discloses a vibrating motor in which the moving body (rotor) includes an annular frictional member bonded to the annular rotor base. The annular rotor base has a radially outwardly extending flange formed integrally therewith, an outer periphery of said flange being in turn formed integrally with the ring-shaped support member. The rotor is pressed against the vibrating body by pressure applied to the annular upper end face of the support member. It is an object of the present invention to provide an ultrasonic motor which has a high efficiency, long lifetime and low manufacturing costs. In accordance with the present invention an ultrasonic motor as defined in the preamble of claims 1 and 4 is characterized by the features of either claim 1 or claim 4. Preferable embodiments are defined in the dependent claims. According to the present invention, the efficiency and lifetime of the ultrasonic motor can be extremely enhanced due to the following reasons. Because the effect (surface compensation effect) of absorbing the undulations in the contact surface of the vibrating body and the moving body can be imparted, and stable uniform contact can be assured by constructing the moving body with elasticity according to the pressure of the ultrasonic motor in the direction of force to the moving body, a progressive wave of flexural vibration due to the vibrating body can be efficiently transferred to the moving body and thereby, the motor efficiency can be improved much. In addition, because by constructing the moving body of a carbon fiber reinforced resin composite material reinforced using at least carbon fiber the composite material has excellent wear resistance and has the effect of applying an appropriate amount of lubrication to the friction contact surface, stable motor characteristics can be obtained even with long-term drive, and an ultrasonic motor with excellent long-term reliability can be achieved. Moreover, because a simplified manufacturing process can be achieved because the number of parts in the moving body is reduced and an adhesion process can be eliminated by constructing the moving body of a carbon fiber reinforced resin composite material reinforced by at least carbon fiber, the weight of the moving body can be reduced, and therefore a lighter ultrasonic motor can be achieved. In addition to omission of those processes, an advantage such that the moving body is easily formed by molding resulting in an extremely low manufacturing cost as well as a small weight. BRIEF DESCRIPTION OF DRAWINGS The present invention will be understood from the detailed description given below and the accompanying diagrams wherein: Fig. 1a is a partial perspective view of the major components of an ultrasonic motor according to a first preferred embodiment of the present invention, Fig. 1b is an enlarged sectional view of the moving body shown in Fig. 1a, Fig. 1c is a cross-sectional view of the ring-shaped ultrasonic motor embodying the structure shown in Fig. 1a, Fig. 1d is a partial perspective view of the major components of a linear ultrasonic motor according to the first preferred embodiment, Fig. 2a is a partial perspective view of the major components of an ultrasonic motor according to a second preferred embodiment of the present invention, Fig. 2b is an enlarged sectional view of the moving body shown in Fig. 2a, Fig. 2c is a cross-sectional view of the ring-shaped ultrasonic motor embodying the structure shown in Fig. 2a, Fig. 2d is a partial perspective view of the major components of a linear ultrasonic motor according to the second preferred embodiment, Fig. 3a is a partial perspective view of the major components of an ultrasonic motor according to a third preferred embodiment of the present invention, Fig. 3b is an enlarged sectional view of the moving body shown in Fig. 3a, Fig. 3c is a cross-sectional view of the ring-shaped ultrasonic motor embodying the structure shown in Fig. 3a, Fig. 4a is a partial perspective view of the major components of an ultrasonic motor according to a fourth preferred embodiment of the present invention, Fig. 4b is an enlarged sectional view of the moving body shown in Fig. 4a, Fig. 5a is a partial perspective view of the major components of an ultrasonic motor according to a fifth preferred embodiment of the present invention, Fig. 5b is an enlarged sectional view of the moving body shown in Fig. 5a, Fig. 5c is a cross-sectional view of the ring-shaped ultrasonic motor embodying the structure shown in Fig. 5a, Fig. 6a is a partial perspective view of the major components of an ultrasonic motor according to a sixth preferred embodiment of the present invention, Fig. 6b is an enlarged sectional view of the moving body shown in Fig. 6a, Fig. 7a is a partial perspective view of the major components of an ultrasonic motor according to a seventh preferred embodiment of the present invention, Fig. 7b is an enlarged sectional view of the moving body shown in Fig. 7a, Fig. 8a is a partial perspective view of the major components of an ultrasonic motor according to an eighth preferred embodiment of the present invention, Fig. 8b is an enlarged sectional view of the moving body shown in Fig. 8a, Fig. 9a is a partial perspective view of the major components of an ultrasonic motor according to a ninth preferred embodiment of the present invention, Fig. 9b is an enlarged sectional view of the moving body shown in Fig. 9a, Fig. 10a is a partial perspective view of the major components of an ultrasonic motor according to a tenth preferred embodiment of the present invention, Fig. 10b is an enlarged perspective view of the moving body shown in Fig. 10b, Fig. 11a is a disassembled perspective view of the main structural parts of a conventional ring-shaped ultrasonic motor, Fig. 11b is a cross-sectional view of a conventional ring-shaped ultrasonic motor, Fig. 12 is a sectional view of the moving body of a conventional ring-shaped ultrasonic motor, and Fig. 13 is an explanatory view illustrating the operating principle of the ultrasonic motor. DESCRIPTION OF PREFERRED EMBODIMENTS Before entering concrete explanation of the embodiments, technical merits on forming the moving material with a resin material will be explained in detail. The ultrasonic motor is a motor which, using the operating principle shown in Fig. 13, excites a progressive wave of flexural vibration with an amplitude (ξ in Fig. 13) of plural microns in a moving body comprised of a piezoelectric body and elastic circuit board, expands the lateral displacement (ζ in Fig. 13) caused by this progressive wave by means of projecting bodies, and drives a moving body provided with pressurized contact against the ends of the projecting bodies. Therefore, to efficiently transfer to the moving body the progressive wave of flexural vibration induced by the vibrating body and assure long-term reliability, a moving body which meets the following requirements and contact between the moving body and the vibrating body are required. a) The moving body shall have dynamic elasticity in the macro length at the wavelength level of the progressive wave of flexural vibration induced by the vibrating body. This is necessary to achieve uniform contact of the moving body at approximately the apex of all waves in the progressive wave, and to efficiently transfer to the moving body the progressive wave of flexural vibration induced by the vibrating body. As a guide to this dynamic elasticity, the amount of elastic deformation in the vertical direction of the moving body material when pressure is applied shall be within the range of the amplitude of the progressive wave, and is preferably approximately equal to the amplitude of the vibrating body. Therefore, the optimum level of dynamic elasticity cannot be unconditionally defined and is variable with the wavelength of the progressive wave (See λ in Fig. 13) excited by the piezoelectric body and the pressure applied by the ultrasonic motor, and must be optimally designed according to the drive conditions of the ultrasonic motor. b) The moving body must have rigidity through the micro length of a level of approximately the contact area (A in Fig. 13) of the progressive wave of flexural vibration induced by the vibrating body. This is necessary to reduce the output transfer loss due to elastic deformation in the contact area of the moving body. As a guide to this rigidity, it is necessary to suppress as much as possible flexural deformation of the moving body in the lateral direction due to the lateral displacement of the progressive wave, and by way of example it is preferable for the modulus of elasticity of the moving body material to be ≥ 1000 kfg/mm 2 . Moreover, in addition to this lateral displacement, it is necessary to also suppress the elastic deformation in the horizontal direction of the moving body due to external loads, and the ideal rigidity required in the moving body cannot be unconditionally defined and must be optimally designed according to the drive conditions of the ultrasonic motor. c) The moving body shall have a suitable lubricity. This is necessary to maintain a stable friction condition and to reduce wear. As a guide to this lubricity, the coefficient of kinetic friction of the moving body material is preferably in the range 0.15 ∼ 0.40. d) The moving body shall have static elasticity according to the applied pressure of the ultrasonic motor. This is necessary to absorb the undulations in the contact surfaces of the moving body and the vibrating body, and to assure uniform contact. As a guide to this static elasticity, the machining precision of the vibrating body and the molding precision of the moving body shall vary according to the pressure applied by the motor, but distortion of the moving body when pressure is applied is preferably 1 ~ 10 µm. The conventional ultrasonic motor using the elastic body made of a metal material is difficult to satisfy these conditions a) to d) and, accordingly, it is difficult to obtain ultrasonic-motors with a high efficiency and a long lifetime. Farther, as stated above, the conventional ultrasonic motors are not satisfactry at various points such as the manufacturing cost and the like. The present invention is made based on a new idea to form the moving body with a resin material and, therefore, is able to provide ultrasonic motors excellent in various points such as efficiency, lifetime and cost. More concretely, the moving body according to the present invention is made of a carbon fiber reinforced resin composite material which is reinforced using at least carbon fibers and, accordingly, the micro-length rigidity is enhanced by carbon fibers and the macro-length dynamic elasticity is obtained by the resin. Reasons for using carbon fiber include its effectiveness improving rigidity in the moving body when compared with any other type of inorganic fiber such as glass fiber of the same given content, the ability to increase moving body rigidity with a lower fiber content, and to improve the mechanical strength of the moving body. In addition to the above, a suitable lubricity can be achieved in the wear interface by using carbon fiber. Moreover, by constructing the moving body to have elasticity corresponding to the amount of pressure applied to the ultrasonic motor, undulations in the contact surface of the moving body and the vibrating body can be absorbed, and a uniform contact can be assured. Mean while, it is desirable to use the press force between the moving body and the vibrating body smaller than that used in the case of the moving body of a metal material since the moving body is formed with a resin compound in the present invention, and the press force within a range 0.08 to 0.8 kgf/cm 2 is desirable employed. Thus, the ultrasonic motor according to the present invention is especially useful for driving a light load such as lens driver in a photographic camer, VTR camera or the like. The preferred embodiments which achieve the aforementioned moving body construction are described hereinbelow with reference to the accompanying figures. [First preferred embodiment] The major structural components of the ultrasonic motor according to the first embodiment are shown in Fig. 1a. As shown in Fig. 1a; a reference numeral 13 denotes a moving body having a beam structure supported at both ends thereof so as to be elastic in a direction vertical to a horizontal plane indicated by A. The moving body comprises a moving body beam 10, first moving body projections 11 extending at both sides of the moving body beam 10, and a second moving body projection 12 extending from the moving body beam 10 at the side in contact with a vibrating body 16. It is to be noted that the vibrating body 16 is a vibrating body with a piezoelectric body 15 coupled to an elastic base board 14 with rectangularly shaped projections 14a. Moreover, the ultrasonic motor is constructed by applying pressure with the vibrating body 16 at surface A of the first moving body projections 11 to cause contact with the vibrating body 16 at the second moving body projection 12. If the width W, of the second projection 12 is smaller than 0.3 mm, the pressure concentrates thereto resulting in a poor long-term reliability due to a heavy wear thereof. On the other hand, if the width W, is larger than 2.0 mm, it becomes difficult to assure a stable and uniform contact and, thereby, it is difficult to unify the performance of the motor. Thus the width W, should be limited within a range 0.3 mm to 2.0 mm. Fig. 1c is a schematic cross-sectional view of the ring-shaped ultrasonic motor embodying the first preferred embodiment shown in Fig. 1a. As shown therein, the vibrating body 16 supported by an annular seat 33 and the moving body 13 are held in pressure contact by a disc spring 35 to form motor wherein rotation of the moving body 13 is outputted via a bearing 37 as the driving force. The present preferred embodiment is not limited to the ring-shaped motor and is applicable to a linear motor as shown in Fig. 1d. [Second preferred embodiment] Fig. 2a shows the ultrasonic motor according to the second preferred embodiment of the present invention in which a moving body 23 is supported at one side so that it has an elasticity in the direction of press force. Specifically, this moving body comprises a moving body beam member 20, a first moving body projection 21 extending from one side of the beam member 20, and a second moving body projection 22 which extends from the other one side of the beam member 20. It is to be noted that the vibrating body 16 is a vibrating body with a piezoelectric body 15 coupled to an elastic base board 14 with rectangularly shaped projections 14a. Moreover, the ultrasonic motor is constructed by applying pressure with the vibrating body 16 at surface B of the first moving body projections 21 to cause contact with the vibrating body 16 at the second moving body projection 22. Fig. 2b is an enlarged sectional view of the moving body in which the width and thickness of the beam member 20 are given as L and T, respectively and the width and height of the second projection 22 are given as W 2 and H, respectively. Fig. 2c is a schematic cross-sectional view of the ring-shaped ultrasonic motor embodying the second preferred embodiment shown in Fig. 2a. As shown therein, the vibrating body 16 supported by an annular seat 33 and the moving body 23 are held in pressure contact by a disc spring 35 to form motor wherein rotation of the moving body 23 is outputted via a bearing 37 as the driving force. With respect to the ratio (L/T) of the beam member 20, if it is larger than 2, the mechanical strength of the moving body 23 is short and the transmission efficiency of output is undesirably lowered due to co-vibration of the beam member 20. Accordingly, the ratio should be designed to be smaller than 2. With respect to the ratio (H/T) of the height H of the second projection 22 to the thickness T of the beam member 20, if it is larger than 2, the mechanical strength of the moving body 16 is short and the second projection 22 is deformed, when an external load is applied thereto, and, thereby, the transmission efficiency of output is undesirably lowered. Thus, this ratio should be designed to be smaller than or equal to 2. Further, if the width W 2 of the second projection 12 is small than 0.3 mm, the pressure concentrates too much thereto resulting in a poor long-term reliability due to a heavy wear thereof. On the other hand, if it is larger than 2.0 mm, it becomes difficult to assure a stable and even contact and, thereby, it is difficult to unify the performance of the motor. Thus the width W 2 should be designed within a range 0.3 mm to 2.0 mm. The dimensions of the moving body are desirably designed so as to satisfy the above conditions in order to transmit the progressive wave of the flexual vibration of the vibration body efficiently. In addition, because the elasticity in the direction of force and the rigidity required for the moving bodies 13 and 23 differ with the applied pressure of the ultrasonic motor, the rigidity and elasticity in the direction of force moving bodies 13 and 23 can be adjusted by adjusting the width and thickness of the moving body beam member and the carbon fiber content of the carbon fiber reinforced resin composite material. More specifically, the moving body 23 is formed so as to have dimensions such that the ratio (L/T) is 0.88, the ratio (H/T) is 1.18 and the width W 2 is 1.0 mm by injection molding a mixture of 30 wt% carbon fiber and 70 wt% polyphenylene sulfide resin. By setting the moving body 23 pressed in contact with the ring-shaped vibrating body 16 of diameter 48 mm under a press force of 0.13 kgf/cm 2 by means of disc spring (not shown in Fig. 2a), a ring-shaped ultrasonic motor is comprised. The ultrasonic motor thus comprised was tested to estimate the properties thereof. At first, the motor efficiency is improved up to 44 % at the maximum. Thus indicates the improvement of about 50 % is obtained in comparison with the conventional one. Next, it was confirmed that no change in the property of the motor was observed even after 2 x 10 6 revolutions. To compare the ultrasonic motor according to the second embodiment with the conventional motor, especially with respect to the moving body, an ultrasonic motor was fabricated using a moving body made of aluminum having the cross section shown in Fig. 12 which is proposed in the Japanese laid-open publication Sho 63-174581. The ratio of the width L with the thickness t 1 regarding the flange of the moving body is set at 6.5, the ratio of the height t 2 of the contacting part with the thickness t 1 of the flange is set at 2.5 and the height T 1 and the width of the moving body are set at 3.2 and 2.0 mm, respectively so that conditions on dimensions disclosed in the above publication are satisfied. Further the contact surface of the moving body was subjected to alumilite processing at a low temperature to enhance the wear resistance thereof. Other factors such as configuration and dimension of the vibrating body, the press force between the moving body and the vibrating body and the like were made same as those of the motor according to the second preferred embodiment in order to estimate the efficiency and lifetime on the same base. According to the results obtained regarding the conventional ultrasonic motor, the maximum efficiency was 30 % at the most and rotation became unstable when the accumulated number of revolutions exceeded 4 x 10 5 revolutions. Thus, the ultrasonic motor according to the present invention is superior to the conventional one in various factors such as efficiency, lifetime, manufacturing cost, weight and the like. In the second preferred embodiment, the press force between the moving body and the vibrating body can be chosen within a range 0.08 to 0.8 kgf/cm 2 wherein the maximum efficiency more than 40 % can be obtained. The present preferred embodiment is not limited to the ring-shaped motor and is applicable to a linear motor as shown in Fig. 2d. [Third preferred embodiment] The ultrasonic motor according to the third preferred embodiment of the present invention has a fundamental structure such that a moving body 50 is pressed in contact with a vibrating body 32 by a disc spring (not shown), as shown in Fig. 3a. First, the ring-shaped vibrating body 32 was constructed by affixing with adhesive a ring-shaped piezoelectric body 31 to the bottom of a stainless steel, ring-shaped elastic circuit board 30 with plural rectangular projections 30a. By injection molding a mixture of 30 wt% carbon fiber and 70 wt% polyphenylene sulfide resin, a moving body 50 of a carbon fiber reinforced resin composite material with a ring shape and specific gravity of 1.45 is obtained. Fig. 3b shows a cross-section of the moving body in which dimensions of respective parts of the moving body 50 are represented in unit of the width W 3 of the moving body second projection 50b which contacts with the vibrating body 32. Namely, the length of the moving body beam portion 50c and the width of the moving body first projection 50a are 3W 3 and 3/2 W 3 , respectively. As shown in Fig. 3c being a cross-section of the ring-shaped ultrasonic motor embodying the structure shown in Fig. 3a, the vibrating body 32 supported by an annular seat 33 and the moving body 50 are held in pressure contact by a disc spring 35 to form the motor wherein rotation of the moving body 50 is outputted via a bearing 37 as the driving force. The third preferred embodiment of the present invention is also possible to attain same effects as those in the first preferred embodiment by optimizing dimensions of the respective parts in accordance with the press force. [Fourth preferred embodiment] First, a moving body 51 of a carbon fiber reinforced resin composite material with a ring shape and specific gravity of 1.47 is obtained by injection molding a mixture of 30 wt% carbon fiber and 70 wt% polyether sulfone resin. Furthermore, by setting the moving body 51 pressed in contact with the vibrating body 32 by means of disc springs (not shown in the figures) as with the first embodiment, a ring-shaped ultrasonic motor as illustrated in Fig. 4a can be comprised. As shown in Fig. 4b, if the width of the second projection 51b which contacts with the vibrating body 32 is W 4 , the width of the moving body beam member 51c in this moving body 51 is 3W 4 , the first projections 51a have a width of 3/2 W 4 , the second projection 51b has a width of W 4 , and the second projection 51b of the moving body 51 is formed excentrically inside from the center of the beam member 51c to contact the vibrating body 32. Specifically, it is possible to achieve a surface compensation effect greater at the outside circumference side than the inside circumference of the moving body by providing the second projections on the inside circumference of the moving body beam member, and a moving body design which accounts for radial amplitude in which the amplitude in the radial direction of the ring-shaped vibrating body is greater at the outside circumference can be achieved. Merits same as those in the first embodiment can be obtained. [Fifth preferred embodiment] First, a moving body 52 of a carbon fiber reinforced resin composite material with a ring shape and specific gravity of 1.45 is obtained by injection molding a mixture of 30 wt% carbon fiber and 70 wt% polyphenylene sulfide resin. Furthermore, by setting the moving body 52 pressed in contact with the vibrating body 32 by means of disc springs (not shown in the figures) as with the first embodiment, a ring-shaped ultrasonic motor as illustrated in Fig. 5a can be comprised. As shown in Fig. 5b, if the width of the second projection 52b which contacts with the vibrating body is W 5 , the width of the moving body beam member 52c in this moving body 52 is 3W 5 /2 and first projections 52a have a width of 3W 5 /2 projecting from the outside circumference of the beam member. As shown in Fig. 5c being a cross-section of the ring-shaped ultrasonic motor embodying the structure shown in Fig. 5a, the vibrating body 32 supported by an annular seat 33 and the moving body 52 are held in pressure contact by a disc spring 35 to form the motor wherein rotation of the moving body 52 is outputted via a bearing 37 as the driving force. It is to be noted that the width of the moving body beam member shall not be thus limited, but because the optimum width and thickness of the moving body beam member and the optimum height of the second projection of the moving body differ with the pressure applied by the ultrasonic motor, it is necessary to be able to adjust the flexibility in the direction of force of the moving body beam member and the height of the second moving body projections. [Sixth preferred embodiment] First, a moving body 53 of a carbon fiber reinforced resin composite material with a ring shape and specific gravity of 1.44 is obtained by injection molding a mixture of 30 wt% carbon fiber and 70 wt% polyether ether ketone resin. Furthermore, by setting the moving body 53 pressed in contact with the vibrating body 32 by means of disc springs (not shown in the figures) as with the first embodiment, a ring-shaped ultrasonic motor as illustrated in Fig. 6a can be comprised. As shown in Fig. 6b, if the width of the second projection 53b which contacts with the vibrating body 32 is W 6 , the width of the moving body beam member in this moving body 53 is W 6 , the first projections 53a extending from the inside circumference of the beam member have a width of W 6 , a second projection 53b extending from the inside circumference of the beam member has a width of W 6 , and accordingly, the moving body contacts the vibrating body 32 at a width of W 6 . In this preferred embodiment, the second projection 53b is formed on the outer side of the beam member 53c and, therefore, the diameter of the moving body can be reduced to yield a more compact and lighter motor. [Seventh preferred embodiment] First, a moving body 54 of a carbon fiber reinforced resin composite material with a ring shape and specific gravity of 1.47 is obtained by injection molding a mixture of 30 wt% carbon fiber and 70 wt% polyether sulfone resin. furthermore, by setting the moving body 54 pressed in contact with the vibrating body 32 by means of disc springs (not shown in the figures) as with the first embodiment, a ring-shaped ultrasonic motor as illustrated in Fig. 7a can be comprised. As shown in Fig. 7b, if the width of the second projection 54b which contacts with the vibrating body 32 is W 7 , the width of the moving body beam member 54c in this moving body 54 is 3W 7 /4, the first projections 54a projecting from the outside circumference of the beam member have a width of 9W 7 /8, and tapers are provided on both ends of the contact side of the moving body beam member. By thus providing tapers at the contact side of the moving body beam member, the surface compensation effect can be increased and the rigidity in the contact part of the moving body can be increased. [Eighth preferred embodiment] First, a ring-shaped vibrating body 42 was constructed by affixing with adhesive a ring-shaped piezoelectric body 41 to the bottom of a stainless steel, ring-shaped elastic base board 40 with plural trapezoidal projections 40a. By injection molding a mixture of 30 wt% carbon fiber and 70 wt% polyphenylene sulfide resin, a moving body 55 of a carbon fiber reinforced resin composite material with a ring shape and specific gravity of 1.45 is obtained. Moreover, by setting the moving body 55 pressed in contact with the vibrating body 42 by means of disc spring (not shown), a ring-shaped ultrasonic motor as illustrated in Fig. 8a can be comprised. As shown in Fig. 8b, if the width of the beam member contacting the vibrating body 42 is W 8 , the width of the moving body beam member 55c in this moving body 55 is 2W 8 , the moving body projections 55a have a width of W 8 , and, accordingly, the moving body contacts the vibrating body 42 at a width of W 8 . It is to be noted that the widths of the moving body beam member shall not be thus limited, but because the optimum width and thickness of the moving body beam member differ with the pressure applied by the ultrasonic motor, it is necessary to be able to adjust the elasticity in the direction of force of the moving body 55 by adjusting the width or thickness of the moving body beam member. [Ninth preferred embodiment] First, a moving body 56 of a carbon fiber reinforced resin composite material with a ring shape and specific gravity of 1.44 is obtained by injection molding a mixture of 30 wt% carbon fiber and 70 wt% polyether ether ketone resin. Furthermore, by setting the moving body 56 pressed in contact with the vibrating body 42 according to the eighth embodiment of the invention by means of disc spring (not shown), a ring-shaped ultrasonic motor as illustrated in Fig. 9a can be comprised. As shown in Fig. 9b, if the width of the beam member contacting with the vibrating body 42 is W 9 , this moving body 56 has a length of 2W 9 in the moving body beam member, moving body projections 56a with a width of W 9 , taper surfaces on the contact surface side of the moving body beam member, and contacts the vibrating body 42 at a width of W 9 . By thus providing a taper at the contact side of the moving body beam member, the surface compensation effect can be increased and the rigidity in the contact part of the moving body can be increased. [Tenth preferred embodiment] First, a moving body 57 of a carbon fiber reinforced resin composite material with a ring shape and specific gravity of 1.47 is obtained by injection molding a mixture of 30 wt% carbon fiber and 70 wt% polyether sulfone resin. Furthermore, by setting the moving body 57 pressed in contact with the vibrating body 42 according to the eighth embodiment of the invention by means of disc springs (not shown), a ring-shaped ultrasonic motor as illustrated in Fig. 10a can be comprised. As shown in Fig. 10b, if the width of the bottom of the moving body 57 in contact with the vibrating body 42 is W 10 , this moving body 57 has a width of 8W 10 /3 in the moving body beam member, moving body projections 57a with a width of 2W 10 /3, and taper surfaces with different angles on the back side of the moving body beam member. By specifically providing a greater taper at the outside circumference of the moving body than the inside circumference, a greater surface compensation effect can be obtained at the outside than at the inside circumference of the moving body, and a design which allows for radial amplitude in which the amplitude in the radial direction of the ring-shaped vibrating body is greater at the outside circumference can be obtained. As described by means of the above ten embodiments, an adhesive process to bond the friction material to the metallic elastic body is not required as it is with a conventional ring-shaped ultrasonic motor by comprising the moving body of a carbon fiber reinforced resin composite material reinforced by at least carbon fiber, and the moving body can be easily molding using dies by either injection, compression, or other molding process. Moreover, by means of the present invention, the weight of the moving body can be reduced in comparison with the weight of a moving body of equal size constructed of a friction material bonded to a stainless steel elastic body as in a conventional ring-shaped ultrasonic motor. Specific embodiments of the present invention were described hereinabove, but it should be noted that in the above ten embodiments the carbon fiber content of the carbon fiber reinforced resin composite material comprising the moving body is adjustable according to the pressure of the ultrasonic motor, but when the fiber content is ≤ 5 wt% the effect is to reduce the rigidity enhancing effect, and the wear resistance of the friction contact surface of the moving body is insufficient. When the fiber content exceeds 50 wt%, molding becomes difficult, though the specific degree varies with the molding method and fluidity of the resin, and the mechanical strength of the molding becomes brittle. Therefore, the required fiber content range is 5 ≤ 50 wt%. The preferable range is 15 ≤ 35 wt% due to an overall consideration of the material characteristics required in the moving body, the moldability of the moving body, and the cost of the moving body. Furthermore, carbon fiber is used as the type of reinforcing fiber in these embodiments, but it is also possible to use inorganic fibers other than carbon fiber to be used in combination with carbon fiber, and it is also possible to use inorganic fillers such as graphic powder, tetrafluoride ethylene powder, molybdenum sulfide powder, or graphite fluoride powder to adjust the lubricity of the moving body. In addition, thermoplastic resins such as polyphenylene sulfide resin, polyether ether katone resin, and polyether sulfone resin are used as the carbon fiber reinforced resin composite material in the above ten embodiments, but the invention shall not be thus limited. As a guide to the selection of resins to form this carbon fiber reinforced resin composite material, the heat resistance of the material should be ≥ 150°C, and it is preferable to use a resin with a high temperature of heat deformation. This is because when a resin with heat resistance ≦ 150°C and a low temperature of heat deformation, wear of the friction contact surface of the moving body is accelerated and it is difficult to assure long-term reliability because of the resulting deterioration in motor performance. Considering these observations, it is also possible to use, in addition to the resins used in the above embodiments, thermoplastic resins such as polysulfone resin, polyarylate resin, polyamideimide resin, polyetherimide resin, polyimide resin, and all aromatic polyester resins, or thermosetting resins such as phenol resin, bismaleimide-triazine resin, or polyimide resin. The following effects are obtained as the cumulative result of constructing an ultrasonic motor according to the present invention with a moving body of a carbon fiber reinforced resin composite material and rigidity according to the pressure applied by the ultrasonic motor in the direction of force to the moving body: a) an ultrasonic motor with high output transfer efficiency can be achieved, b) an ultrasonic motor with excellent long-term reliability can be achieved, c) the manufacturing process for the moving body can be simplified, and d) the weight of the ultrasonic motor can be reduced.

Claims: An ultrasonic motor comprising a vibrating body (16, 32, 42) comprised of an elastic base (14, 30, 40) and a piezoelectric body (15, 31, 41) fixed on said elastic base, a moving body (13, 50, 51. 55, 56, 57) press-contacted against said piezoelectric body (15, 31) by a spring force of a spring means (35), in which said moving body (13, 50, 51, 55, 56, 57) is driven by friction force between said moving body (13, 50, 51, 55, 56, 57) and said vibrating body (16, 32, 42) by exciting a progressive wave of flexural vibration in said vibrating body (16, 32, 42); characterized in that said moving body (13, 50, 51, 55, 56, 57), in its cross-section normal to the direction of movement, has a double-side supported beam construction comprising a beam member (10, 50c, 51c, 55c, 56c, 57c) and first projections (11, 50a, 51a, 55a, 56a, 57a) projected away from the vibrating body in normal direction with respect to said beam member at both ends of said beam member, respectively; said moving body (13, 50, 51, 55, 56, 57) is made of a carbon fiber reinforced resin composite material reinforced with at least carbon fibers; and that a limited surface area (12, 50b, 51b) of said beam member (10, 50c, 51c; 55c, 56c, 57c) is press-contacted against said vibrating body (16, 32, 42) directly. The ultrasonic motor according to claim 1, wherein said beam member (10, 50c, 51c) of the moving body (13, 50, 51) comprises a second projection (12, 50b, 51b) projected toward said vibrating body (16, 32), the second projection providing said limited surface area press-contacting said vibrating body (16, 32). The ultrasonic motor according to claim 1, wherein said vibrating body (42) is provided with a limited width (W 8 , W 9 , W 10 ) in cross-section, and is press-contacted by said limited surface area of said beam member (55c, 56c, 57c). An ultrasonic motor comprising a vibrating body (16, 32) comprised of an elastic base (14, 30) and a piezoelectric body (15, 31) fixed on said elastic base, a moving body (23, 52, 53, 54) press-contacted against said piezoelectric body (15, 31) by a spring force of a spring means (35) in which said moving body (23, 52, 53, 54) is driven by friction force between said moving body (23, 52, 53, 54) and said vibrating body (16, 32) by exciting a progressive wave of flexural vibration in said vibrating body (16, 32); characterized in that said moving body (23, 52, 53, 54), in its cross-section normal to the direction of movement, has a single-side supported beam construction comprising a beam member (20, 52c, 53c, 54c), a first projection (21, 52a, 53a, 54a) projected away from the vibrating body in normal direction with respect to said beam member at one end of said beam member, and a second projection (22, 52b, 53b, 54b) projected toward said vibrating body at the other end of said beam member; said moving body (23, 52, 53, 54) is made of a carbon fiber reinforced resin composite material reinforced with at least carbon fibers; and that said second projection (22, 52b, 53b, 54b) is press-contacted against said vibrating body (16, 32) directly. The ultrasonic motor according to claim 2 or 4 wherein the width (W 1 -W 7 ) of said second projection (12, 50b, 51b; 22, 52b, 53b, 54b) is set within a range of 0.3 mm to 2.0 mm. The ultrasonic motor according to claim 4 wherein said moving body (23, 52, 53, 54), having said single-side supported beam (20, 52c, 53c, 54c), is constructed to satisfy the following dimensional relationships L/T < 2, H/T ≤ 2, and wherein L is the length of said beam member (20, 52c, 53c, 54c) in cross-section, T is the thickness of said beam member, and H is the height of said second projection (22, 52b, 53b, 54b) including the thickness T.

Inventors: KAWASAKI OSAMU, NISHIKURA TAKAHIRO, SUMIHARA MASANORI, TAKEDA KATSU, KAWASAKI, OSAMU, NISHIKURA, TAKAHIRO, SUMIHARA, MASANORI, TAKEDA, KATSU
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1992
Main classification: H01L41
IPC codes: H02N2, H01L41