PROCESS FOR FABRICATING INSULATION-FILLED DEEP TRENCHES IN SEMICONDUCTOR SUBSTRATES

Abstract: A method for forming an isolation wall in a silicon semiconductor substrate (10) wherein a trench (12) is etched into the silicon using a hard mask (30), a layer of silicon dioxide (14) is formed on the side walls of the trench, a filling of polysilicon (16) is placed in the region between the side wall layers, the polysilicon is planarized by etching while the hard mask remains in place, and the hard mask then is stripped from the silicon, permitting field oxide (18) to be grown over the trench region.

Description: PROCESS FOR FABRICATING INSULATION-FILLED DEEP TRENCHES IN SEMICONDUCTOR SUBSTRATES BACKGROUND OF THE INVENTION 1. Field of the Invention This invention relates to processes for develop¬ ing isolation walls in semiconductor devices such as inte¬ grated circuit (IC) chips. More particularly, this inven¬ tion is related to so-called trench isolation, wherein a trench is formed in the semiconductor device and filled with an insulating material. 2. Description of the Prior Art It frequently is necessary to electrically isolate adjacent portions of an integrated circuit, and various techniques have been developed for this purpose. One such technique that has practical advantages is that of forming a trench at the place where isolation is needed, and filling the trench with an insulating material. Although a variety of proposals have been put forward for such purpose, important problems have arisen with all of those proposals. For example, when a field oxide is thermally grown over a trench isolation region, a large step can (with prior art techniques) develop in the field oxide just above the trench edge, due to the usual difference in height between the insulation surface and the surrounding silicon, and the commonly lower oxidation rate of the insulating material as compared to the surrounding bulk material. Another problem is that notches can develop in the field oxide if the trench filling is layered in such a way that differential etching occurs at one or more layers. Such notches can attract residues from subsequent layers deposited over the trench (to form portions of the integrated circuit) such that conductive lines crossing the trench become electrically inter-connected, thereby resulting in a defective part. Also, when using trench isolation with a Silicon On Insulation (SOI) substrate, the removal of the trench hard mask after trench etch can lead to unintended etching of the buried insulating layer which can cause defective parts. Efforts have been made by others to solve some of these and still further problems. For example, it has been proposed to use a combination of additional oxide steps and a nitride/oxide sandwich layer, as described in U.S. Patent 4,791,073. Such a procedure however is excessively com¬ plex. Moreover, the additional thermal steps can adversely affect the characteristics of the final product, and such procedure would not in any event solve the problem of etch¬ ing of the buried oxide layer of a Silicon-On-Insulation substrate. SUMMARY OF THE INVENTION In a preferred embodiment of the invention, to be described in detail hereinafter, a process is employed wherein a sacrificial layer is maintained in place during the basic formative steps so as to provide important protec¬ tions from adverse effects, and then is removed just prior to completion of the trench isolation portions of the pro¬ cess. This sacrificial layer in the preferred embodiment is the hard mask used to establish the etch opening for forming the trench. This hard mask is not, as is conven¬ tional, stripped after trench etch, but is retained in place to provide protection as will be apparent from the following description. At the end of the process, after planarization of the trench filling dielectric, the hard mask is stripped away, and the substrate is in condition to have field oxide thermally grown over the trench without the problems previously encountered. Other objects, aspects and advantages of the invention will in part be pointed out in, and in part apparent from, the following detailed description of a preferred embodiment of the invention, considered together with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS FIGURE 1 is a sectional view of a semiconductive substrate with a buried insulator and showing the kinds of adverse characteristics that can develop when following conventional practices; FIGURE 2 is a sectional view of a semiconductive substrate with a buried insulator and having an oxide mask with an opening for a trench to be processed in accordance with the present invention; FIGURE 3 shows the substrate of Figure 2 with an etched trench; FIGURE 4 shows the substrate of Figure 3 after formation of side wall dielectric layers and filling with deposited polysilicon; FIGURE 5 shows the substrate of Figure 4 after planarization of the polysilicon; FIGURE 6 shows the substrate of Figure 5 after stripping of the hard mask; and FIGURE 7 shows the substrate of Figure 6 with thermally grown field oxide. DETAILED DESCRIPTION OF A PREFERRED EMBODIMENT Figure 1 has been included to illustrate the nature of some of the problems which can occur by following conventional processing techniques. This figure shows in cross-section a substrate 10 of the Silicon-On-Insulator (SOI) type after it has been processed to form a trench 12 having insulative layers 14 (such as silicon dioxide) side walls of the trench and an insulative filling 16 (such as polysilicon) in the central region between the side wall layers 14. It particularly will be seen that the thermally-grown field oxide 18 is formed with a large step 20 at the trench edge due to the difference in height between the upper surface of the insulative filling 16 and the surrounding surface of the silicon, and also due to the (usual) lower oxidation rate of the central filling 16 as compared to the surrounding bulk material. Notches 22 also can develop at the trench edges due to differential etching of the relatively thin layers forming part of the trench fill. Such notches can retain residues from subsequent layers that are deposited over the trench and patterned and removed to form portions of the integrated circuit. Such residues can cause inter-connec¬ tions between conductive lines formed in such subsequent layers and crossing the trench region. Such inter-connec- . tions would of course almost certainly result in defective parts. If the hard mask (not shown in Figure 1) for forming the trench 12 is removed immediately after trench etch (as is conventional) etching of the buried insulating layer can occur, as illustrated at 26 in Figure 1. Such etching can lead to defective parts. Referring now to Figure 2, in carrying out the preferred method of the invention, a layer of silicon dioxide 30 first is deposited on the principal surface of a silicon substrate 10. This layer is patterned, using standard lithography procedures with photo-resist, and etched to define an etch opening 32 for a trench to be formed in the substrate. This etch may for example be carried out with a plasma etch, such as SF 6 and CF 4 together. The resist is removed at this stage. A trench 12 then is etched, as shown in Figure 3, as by means of a reactive ion etch (RIE) , for example, HBr. The trench etch stops at the upper surface of a buried oxide insulator 34 forming part of the Silicon-On-Insulator substrate. Referring next to Figure 4, a dielectric 14 then is formed on the side walls of the trench. Preferably, this dielectric is silicon dioxide, thermally grown on the trench side walls. Thereafter, the interior region between the side wall dielectric layers is filled with a thick polysilicon layer 16, in order to completely fill the trench. This polysilicon is applied so as to extend above the trench and out laterally over the adjacent surfaces of the hard mask 30. Next, the polysilicon layer 16 above the hard mask 30 is planarized by etching it away by a blanket etching process. A mixed chemistry plasma etch such as CF 4 and Cl 2 can be used for this purpose. This etch results in a configuration as shown in Figure 5, where the upper surface of the polysilicon 16 is below the surface of the hard mask, and just a bit above the adjacent surface of the substrate 10. The mask oxide acts as an etch stop layer, and its thickness is adjusted to provide that the surface of the silicon substrate is protected during planariza io . The surface of the polysilicon inside the trench is higher than the surrounding silicon, thereby to prevent etching of the side wall oxide 14 to a level below the silicon surface during the subsequent mask strip step. By suitable choice of the height "h" of the polysilicon above the silicon surface, an essentially planar surface can be obtained after developing the field oxide, as by LOCOS oxidation. The hard mask 30 is stripped by etching, result¬ ing in the configuration shown in Figure 6. This can be effected by a wet etch such as HF. By carrying out the mask strip at this stage, etching of the buried oxide layer 34 is avoided. The next step is to subject the trench isolation region to an oxidation to form the field oxide region 18. The upper surface of the field oxide as finally developed is essentially planar notwithstanding that the polysilicon is higher than the silicon surface. This planar field oxide surface is achievable because the rate of oxidation of the polysilicon is lower than that of the surrounding silicon surface. Thus, by proper selection of the height "h" (Figure 6) , the end result will be a generally flat field oxide surface. Although a preferred embodiment of the invention has been disclosed herein in detail, it is to be understood that this is for the purpose of illustrating the invention, and should not be construed as necessarily limiting the scope of the invention since it is apparent that many changes can be made by those skilled in the art while still practicing the invention claimed herein.

Claims: What is Claimed is: 1. A method for forming an isolation wall in a semiconductor substrate having a principal surface, comprising: forming a mask layer on said principal surface with an opening outlining a trench to be formed in said substrate; etching said substrate through said mask opening to develop said trench; applying a layer of dielectric material to the side walls of said trench while leaving the interior regions of the trench within said side wall layers free of said dielectric; filling said interior regions with additional dielectric material, said additional material being applied so as to extend above said trench and along the adjacent upper surfaces of said mask layer; planarizing said additional dielectric material to remove that material from above said mask layer while leaving said additional material in said trench with an upper surface no higher than the level of said mask layer; and stripping said mask layer from said principal surface. 2. The method of Claim 1 including the step of forming a field oxide over said trench and said principal surface. 3. The method of Claim 1, wherein said substrate is silicon. 4. The method of Claim 3, wherein said side wall layer is thermally-grown silicon dioxide. 5. The method of Claim 3, wherein said additional dielectric material is polysilicon. 6. The method of Claim 3, wherein said mask layer is deposited silicon dioxide. 7. The method of Claim 6, wherein said mask layer is stripped by etching. 8. The method of Claim 1, wherein said additional material in said trench has, after planarization, a height which is above the surface of said substrate but below the surface of said mask layer. 9. The method of Claim 1, wherein said planarizing is effected by etching. 10. The method of Claim 1, wherein said substrate is formed with a buried insulating layer; the etching of said substrate through said mask opening being controlled so that the bottom of the trench just reaches the upper surface of said buried insulating layer. 11. A method for forming an isolation wall in a semiconductor substrate including a buried insulator and having a principal surface, said method comprising: forming a mask layer on said principal surface with an opening outlining a trench to be formed in said substrate; etching said substrate through said mask opening to develop said trench; filling said trench with dielectric material, said dielectric material being applied so as to extend above said trench and along the adjacent upper surfaces of said mask layer; planarizing said dielectric material to remove the portions of that material from above said mask layer while leaving said dielectric material in said trench with an upper surface no higher than the level of said mask layer; and stripping said mask layer from said principal surface. 12. The method of Claim 11, including the step of forming a field oxide over said trench and said principal surface. 13. The method of Claim 11, wherein said substrate is silicon. 14. The method of Claim 13, including the step of applying a layer of insulating material to the side walls of said trench prior to filling said trench with dielectric material. 15. The method of Claim 1, wherein said mask layer is an oxide-only film. 16. The method of Claim 1, wherein said planarization is carried out by an etch arranged to effect removal of said dielectric material above said mask layer while leaving said upper surface of said additional material in said trench at a predetermined height "h" above said principal surface. 17. The method of Claim 16, wherein said mask layer is an oxide-only film and said interior regions of said trench are filled with polysilicon. 18. A method for forming an isolation wall in a semiconductor substrate including a buried insulator and having a principal surface, said method comprising: forming a mask layer on said principal surface with an opening outlining a region where a trench is to be formed in said substrate; etching said substrate through said mask opening to develop said trench; filling said trench with dielectric material, said dielectric material being applied so as to extend above said trench and along the adjacent upper surfaces of said mask layer; planarizing said dielectric material to remove the portions of that material from above said mask layer; stripping said mask layer from said principal surface; and thereafter forming a field oxide over both said trench and said principal surface.

Inventors: YALLUP KEVIN, YALLUP, KEVIN
Applicants: ANALOG DEVICES INC, ANALOG DEVICES, INCORPORATED
Application year: 1992
Main classification: H01L21
IPC codes: H01L21