Semiconductor device and method of manufacturing such a semiconductor device

Abstract: The invention relates to an integrated circuit having an interconnection pattern which is recessed in the insulating layer, for example, an oxide layer. A groove is etched in the insulating layer corresponding to the metal pattern by means of a mask which is the inverted image of the interconnection pattern during manufacture. Etching is continued until contact windows are fully opened. To prevent the oxide between the contact windows also being removed, an etching stopper layer is provided in the oxide layer. A layer already present in the process may be used for this etching stopper layer, for example, a polycrystalline silicon layer, so that extra process steps are made redundant.

Description: The invention relates to a method of manufacturing a semiconductor device comprising a semiconductor body having at one of its surfaces a circuit element with at least two conductive regions, and source and drain regions of a MOS transistor. It is usual in complicated integrated circuits to use multilayer interconnections with one or several of the lower interconnection layers made of polycrystalline silicon (poly) and/or silicide, and the upper layer or layers made of metal, such as A1. It is usual thereby to connect poly tracks (or silicide tracks) and monocrystalline zones in the body to the first metal layer by means of metal plugs. These mostly contain W, or TiW and W. The first metal layer is also connected to the second metal layer by means of plug connections. From US-A 4,808,552 a method is known wherein the surface being coated with an insulating layer is provided with a conductor track which interconnects the conductive regions through contact windows in the insulating layer and which is recessed into the insulating layer over at least substantially its entire thickness, the insulating layer, in the area between said contact windows and below the conductor track, being provided with an etching stopper layer of a material which is selectively etchable relative to the insulating layer. In this known process, separate steps for providing the etching stopper layer, consisting of siliconnitride, are required. A method according to claim 1 of the invention is comprises the following steps: coating said at least two conductive regions with an insulating material forming a first insulating layer (15a), depositing a first conductive layer (24) on the entire device, said first conductive material being selectively etchable relative to said insulating material, simultaneously forming from said first conductive layer an etching stopper layer (21) and the gate electrode 19 of said MOS transistor, said etching stopper layer being formed in a region between said conductive regions and patterned so that at one of its ends a portion of said first insulating layer overlying one of said conductive regions (3t) is exposed, and at the other end said etching stopper has an interruption (25) exposing a portion of said first insulating layer overlying the other conductive region (3b), covering the entire device with said insulating material forming a second insulating layer (15b), defining contact openings on the second insulating layer by the use of a mask (26) formed thereon so that one opening to contact one of the conductive regions (3f) is defined by one edge of said mask and the end of the etching stopper exposing the portion of the first insulating layer overlying said conductive region, etching the second insulating layer through said mask (26) down to the etching stopper layer, to the gate electrode and to the semiconductor body surface, and at the locations where the first insulating layer is exposed, etching down until portions of the conductive regions are exposed, obtaining thus contact windows (30, 31). depositing a second conductive layer (32) on the entire device, said second conductive layer contacting the exposed conductive regions, the gate electrode and source/drain regions, etching back said second conductive layer to form a recessed conductor track. Thus, it is not necessary to use a separate etching stopper layer and photomask for the etching stopper layer. The invention will be explained in more detail with reference to an embodiment and the accompanying diagrammatic drawing in which Fig. 1 shows the diagram of a charge-coupled image sensor of the raster transfer type; Fig. 2 shows a portion of the device depicted in Fig. 1 with the diagrammatically indicated connections between the clock lines and the clock electrodes according to the invention; Fig. 3 is a cross-section of a portion of the device according to Fig. 2; Fig. 4 is a plan view of the portion shown in Fig. 3; Figs. 5-8 show the device in a number of stages of manufacture thereof; Fig. 9 is a cross-section of a second embodiment of the device. The invention will be explained in more detail with reference to a charge-coupled device, more particularly an imaging device for which the invention is especially important. It will be quite clear from the description, however, that the invention may also be advantageously used in other types of integrated circuits. Fig. 1 shows a diagrammatic plan view of a raster transfer imaging device comprising a system of vertical CCD lines 1 situated next to one another divided into an imaging section A and a memory section B. The imaging section A serves, as is known, for converting a projected image into charge packages. At the end of the imaging period, these charge packages are quickly transported to the memory section B which is screened from incident radiation. At the lower side of the memory section is provided the horizontal readout register C which is provided with an output amplifier 2. The charge packages stored in the B section are transported to the readout register C row by row and read sequentially at the output amplifier 2. The charge transport and charge storage are controlled by clock voltages which are applied to clock electrodes 3, four of which are diagrammatically depicted in Fig. 1, 1, 2, 3 and 4. It is usual for the clock electrodes to be made by the double- or triple-layer poly-Si technology, by means of which an overlapping gate structure is made in two or three layers. A drawback of this technology is that the structure onto which the image is projected is of very imperfect flatness, so that light can be deflected towards insensitive regions. In addition, it is difficult in the case of a colour sensor to provide a colour filter in an accurate manner. The poly layers used are usually 0,3-0,5 µm (1 µm = 10 -6 m) thick, which is too thick for transmitting sufficient blue light. Therefore, a photosensitive surface free from poly-Si is often formed through adaptation of the gate configuration. The thickness of the poly-Si is so great because otherwise, i.e. in the case of a smaller thickness, the resistance becomes too great, and thus the RC time per clock phase. In the embodiment to be described here, a single-layer poly technology will be used for the clock electrodes of at least the A section with a very thin poly layer, approximately 50 nm thick, so that the sensor has a good sensitivity to the entire visible spectrum, there is no overlap between the gates of the various phases, and the structure is topographically very plane. Fig. 2 is a diagrammatic plan view of part of the electrode configuration in the imaging section A. The clock electrodes 3 are formed by non-overlapping polystrips with a thickness of 50 nm situated next to one another. The comparatively high-ohmic tracks 3 are connected to low-ohmic metal tracks 4 which are connected to the polystrips 3 at the areas of the dots. In the embodiment shown of a 4-phase CCD, each metal strip 4 is connected to each fourth clock electrode 3. The metal strips 4 may be made very narrow, so that comparatively wide spaces remain open between the metal strips, through which spaces the light may penetrate into the semiconductor body. As is shown in Fig. 1, the gates 3 may each be connected to the clock lines by a number of interspaced tracks 4 in order to obtain the desired low RC time value. At the upper side of the CCD matrix, the metal tracks 4 may be connected to four clock lines 5, by means of which the clocks 1, 2, 3 and 4 are provided, via connections 6. Fig. 3a shows in cross-section a portion of a semiconductor device in which the invention is incorporated, with a portion of a charge-coupled device to be used in the imaging section A of the imaging device according to Fig. 2, and an MOS transistor which is integrated with the charge-coupled device. Fig. 3b gives a diagrammatic plan view of the portion shown in Fig. 3a. The device comprises a semiconductor body 10 of silicon with a surface 11 at which or near which the charge-coupled device 12 and the MOST 13 are situated. The charge-coupled device comprises a range of clock electrodes 3a, 3b, 3c, etc. formed by thin, approximately 50 nm thick polycrystalline silicon tracks. The gates 3 constitute the conductive regions referred to above and are separated from the surface 11 by the thin dielectric layer 14. In the present embodiment, the gate dielectric only comprises a silicon oxide layer, but it may obviously also consist of a different insulating material or of double layers of, for example, silicon oxide and silicon nitride. The gates 3 are embedded in a dielectric layer 15 which may be entirely of silicon oxide, but which may obviously also be composed entirely or partly of other materials. The layer 15 is composed of two portions 15a and 15b, which will be discussed below. The MOS transistor 13 comprises a source and a drain zone 17, 18 and a gate electrode 19 which is insulated from the subjacent channel region by the gate oxide 14. On the insulating layer 15, or at least on the portion 15a of the insulating layer, a conductor track 4 is formed which interconnects the conductive regions 3b and 3f via contact windows in the insulating layer 15. The conductor 4 is embedded in the layer 15 over at least substantially its entire thickness, so that a practically plane upper surface is obtained. According to the invention, an etching stopper layer 21 separating the conductor track 4 from the subjacent portion 15a of the insulating layer 15 is present in the intermediate region between the conductive regions 3b and 3f. The layer 21 comprises a material which is different from that of the insulating layer 15 and relative to which the layer 15 can be selectively etched. The provision of the etching stopper layer requires no extra process steps since the layer 21 forms part of a layer pattern manufactured from a common layer, which pattern comprises besides the etching stopper layer 21 further portions in the device and which can accordingly be formed simultaneously with these further portions. In the present embodiment, the etching stopper layer 21 is made of polycrystalline silicon which together with the gate 19 of the transistor 13 belongs to the second polycrystalline wiring layer. The thickness of this second layer is approximately 0,4 µm and is chosen to be much greater, for reasons of resistance, than the thickness of the gates 3a, 3b, etc. which is only approximately 50 nm for reasons of photosensitivity. The transistor 13 is further provided with a contact 22 which is connected to the zone 18, and with a contact 23 which is connected to the gate 19, the contacts 22, 23 being formed by plugs. The contact 23 is drawn above the channel region in the drawing. In actual fact, however, it will preferably be provided above the field oxide not shown in the drawing. A few steps in the manufacture of the device according to Figs. 3 and 4 will be described with reference to Figs. 5-7. The device is shown in these Figs. in the same cross-section as in Fig. 3. Fig. 5 shows the stage in which the clock electrodes 3 are formed from an approximately 50 nm thick polycrystalline silicon layer. The gates 3 are then coated with an oxide layer 15a. This layer, which may be provided by, for example, CVD techniques known per se and local removal through etching, has a thickness of approximately 0,3 µm. Then an approximately 0,4 µm thick second polycrystalline silicon layer 24 is provided by deposition. By means of photolithographic steps known per se , on the one hand the gate 19 of the MOST 13 is formed from this layer, and on the other hand the etching stopper layer 21. The width of the etching stopper layer is 1,7 - 2 µm and is chosen to be somewhat greater than the width of the conductor track 4 to be provided in a later stage. The layer 21 has an interruption with a width of approximately 1,1 µm at the area of the connection to be provided between the conductor track 4 and the gate 3b, at a width of approximately 2 µm of the gate 3b. The entire assembly is then covered with a thick oxide layer 15b, having a thickness of approximately 1 µm. A mask 26 in the form of a photoresist layer is formed on the surface of this oxide layer, which mask is complementary to, or the inverted image of, the metal pattern to be obtained at a later stage. The mask 26 has openings 27 at the areas of the contacts 22, 23 and an opening 28 at the area of the connection 4 to be formed. The width of the opening 28, which is situated as symmetrically as possible above the etching stopper layer 21, is approximately 1,1 µm, so that the etching stopper layer projects by approximately 0,3-0,5 µm on either side of the opening 28. In this stage of the process, the source and drain zones 17, 18 of MOSTs and other zones may also be provided. The device is then in the stage as shown in Fig. 6. Then the device is subjected to an etching treatment during which the oxide layer 15a, 15b is removed at the areas of the openings 27, 28. The etching treatment is carried out selectively in that the polycrystalline silicon of the gates 3, 19 and the etching stopper layer 21 are not attacked or at least attacked to a much lesser degree during etching of the oxide. Etching is preferably carried out in an anisotropic plasma etching stage to prevent underetching. Etching of the oxide is continued down to a depth where a different material is present, i.e. for example up to the monocrystalline Si material at the area of the source or drain zone 18, down to the polycrystalline Si material at the area of the gate 19 of the MOST and the etching stopper layer 21. The contact window 30 is formed at the area of the gate 3b, where the etching stopper layer 21 has an interruption 25. Etching of the oxide layer 15 continues down to the polycrystalline Si material of the first poly layer. The width of the window 30 in the direction of the cross-section of Fig. 7 is determined by the width of the interruption 25 in the etching stopper layer 21. The width in the direction transverse to the plane of the drawing is determined by the mask 26. The width of the contact window 31 at the area of the poly track 3f is determined, in the cross-section of Fig. 7, by the spacing between the etching stopper layer 21 to the left of the window 31 and the edge of the mask 26 to the right of the window 31 to be formed. The width of the window 31 in the direction transverse to the plane of the drawing is again determined by the mask 26. After etching, the mask 26 is removed again, upon which a thick metal layer 31 (Fig. 8) is provided, which covers the entire surface. Tungsten is chosen for the layer 32 in the present embodiment. Obviously, other suitable materials may also be chosen. Before the layer 32 is provided, a thin layer of TiW 33 may be provided, for example, by sputtering. The layer 33 ensures a good adhesion of the metal layer 32 and also forms a good barrier against diffusion. After the metal deposition, the metal layer 32/33 is subjected to an etching treatment and etched back to the upper surface of the thick oxide layer 15. The configuration of Fig. 3 is then obtained. The use of the second polycrystalline silicon layer for the etching stopper layer 21 renders an extra mask for masking the oxide layer 15 in the intermediate region between the contact windows 30, 31 to be formed redundant. Only two polycrystalline silicon layers are used in the embodiment described here. Fig. 9 gives in cross-section an embodiment comprising three polycrystalline layers. Only part of a CCD channel is shown in the drawing. The charge-coupled device comprises clock electrodes in two poly layers, i.e. the gates 35a, b, c in poly 1, and the gates 36a, b, c in poly 2. The thickness of the two poly layers is between, for example, 0,3 and 0,5 µm. This thickness is much greater than the thickness of the CCD electrodes 3 in the preceding embodiment, so that the resistance will be much lower. Nevertheless, it may yet be advantageous also in this case to connect the electrodes to low-ohmic bridge connections 4, for example, when the dimensions of the image sensor are very great. In the manufacture of the device shown in Fig. 9, first the electrodes 35a, 35b, 35c are formed from a first polycrystalline silicon layer, with openings between the electrodes. After coating of the gates 35 with an oxide layer, a second polycrystalline silicon layer is deposited, from which the gates 36a, 36b, 36c are formed, which fill up the openings between the gates 35. The gates 36 may overlap the gates 35, as is shown in Fig. 9. In a next stage, the gates 35, 36 are covered with the oxide layer 15a, after which a third polycrystalline silicon layer is deposited, from which the etching stopper layer 21 is formed. Since this third polylayer is necessary elsewhere in any case, inter alia for the parallel-serial interface (not shown in Fig. 9) between the memory section B and the horizontal readout register C (see Fig. 1), the provision of the etching stopper layer 21 does not require an extra deposition step and mask. The gate electrode 19 of MOS transistors (not shown in Fig. 9) may be formed in poly 2 before doping stages for source and drain zones are implemented. When the etching stopper layer 21 has been formed, the manufacture of the device can be continued in a manner analogous to that for the preceding embodiment. A thick oxide layer 15 is then deposited first, in which the pattern of the wiring to be shaped is provided by means of an inverted metal mask. Etching continues at the areas of the gates 35b and 35d down to the polymaterial of these gates. In the area situated between these gates, etching is stopped by the etching stopper layer 21. After the etching treatment, the recessed metal pattern with the bridge connection 4 is formed in the manner described above by means of deposition and etching back. Thus the invention may also be applied in different types of charge-coupled devices as well as in integrated circuits without charge-coupled devices. Besides bridge connections between gate electrodes, connections between surface zones in the semiconductor body or between zones and gates of conductor tracks may also be formed in the manner described here. The etching stopper layer 21 need not necessarily consist of polysilicon, it may alternatively consist of a different material, for example, silicide. Instead of W or TiW, other metals or conductive materials, such as doped semiconductor material, may be used for the connections 4.

Claims: A method of manufacturing a semiconductor device comprising a semiconductor body (10) having at one of its surfaces (11) a circuit element with at least two conductive regions (3b, 3f), and source (18) and drain (17) regions of a MOS transistor (13), further comprising: coating said at least two conductive regions with an insulating material forming a first insulating layer (15a), depositing a first conductive layer (24) on the entire device, said first conductive material being selectively etchable relative to said insulating material, simultaneously forming from said first conductive layer an etching stopper layer (21) and the gate electrode 19 of said MOS transistor, said etching stopper layer being formed in a region between said conductive regions and patterned so that at one of its ends a portion of said first insulating layer overlying one of said conductive regions (3f) is exposed, and at the other end said etching stopper has an interruption (25) exposing a portion of said first insulating layer overlying the other conductive region (3b), covering the entire device with said insulating material forming a second insulating layer (15b), defining contact openings on the second insulating layer by the use of a mask (26) formed thereon so that one opening to contact one of the conductive regions (3f) is defined by one edge of said mask and the end of the etching stopper exposing the portion of the first insulating layer overlying said conductive region, etching the second insulating layer through said mask (26) down to the etching stopper layer, to the gate electrode and to the semiconductor body surface, and at the locations where the first insulating layer is exposed, etching down until portions of the conductive regions are exposed, obtaining thus contact windows (30, 31), depositing a second conductive layer (32) on the entire device, said second conductive layer contacting the exposed conductive regions, the gate electrode and source/drain regions, etching back said second conductive layer to form a recessed conductor track. A method as claimed in Claim 1, characterized in that the etching treatment for removing the insulating layer in the intermediate region and at the areas of the contact windows is carried out anisotropically.

Inventors: PEEK HERMANUS LEONARDUS, PEEK, HERMANUS LEONARDUS
Applicants: KONINKL PHILIPS ELECTRONICS NV, KONINKLIJKE PHILIPS ELECTRONICS N.V.
Application year: 1992
Main classification: H01L21
IPC codes: H01L21, H01L27