A COATING COMPOSITION FOR A CLEARCOAT WITH IMPROVED SOLVENT AND ACID RESISTANCE

Abstract: A coating composition for a clearcoat in a multilayer coating system for metallic substrates is described, comprising (a) a resin with epoxy and hydroxy functionality, (b) a resin with anhydride functionality, (c) an aminoplast resin and (d) additives selected from the group consisting of solvents, catalysts, flow agents, hindered amine light stabilizers, ultraviolet absorbers. The clearcoat exhibits superior solvent resistance, acid resistance and hardness.

Description: A O G WITH IMPROVED SOLVENT AND ACID RESISTANCE FIELD OF THE INVENTION The present invention is directed to a coating composition for a clearcoat in multilayer coating system for metallic substrates, more specifically, it is directed to a mixture of resins having epoxy and hydroxy functionality and resins having anhydride functionality crosslinkable with aminoplast resins as a coating composition for the preparation of clearcoats. BACKGROUND OF THE INVENTION Multilayer coating systems are well known in the automotive coating industry. There coating systems comprise a pigmented basecoat and clear topcoat. In U.S. Pat No. 4,598,015 are described a number of basecoat-clearcoat systems, in which both the basecoat and the clearcoat are pigmented in order to be aesthetically pleasing as well as durable. The U.S. Pat. No. 4,728,543 discloses a clear topcoat composition of a film-forming acrylic polymer having a plurality of cross-linkable functional groups, solvents, a cross-linking agent and icrogel particles. But these systems do not meet all requirements of the automotive industry for the topcoat in terms of mechanical properties, more specifically in terms of solvent resistance and acid resistance. An object of the present invention is to provide a multilayer coating system for the automotive coating industry which includes a topcoat which exhibits superior solvent resistance, acid resistance and hardness compared to the aσrylic/melamine clearcoats of the Prior Art. SUBSTITUTESHEE SUMMARY OF THE INVENTION The object of the present invention is achieved with a coating composition comprising A) a resin with epoxy and hydroxy functionality B) a resin with anhydride functionality C) an aminoplast resin and D) additives selected from the group consisting of solvents, catalysts. Additives selected from the group consisting of solvents, catalysts, flow agents, hindered amine light stabilizers, ultraviolet absorbers. Detailed Description of the Invention Suitable resins (A) for the preparation of the coating composition of the present invention are polyacrylate resins having epoxy and hydroxy functionality. These polyacrylate resins are obtainable by polymerizing a.,) about 5 to about 80% by weight of an ethylenically unsaturated monomer having an epoxy group a 2 ) about 5 to about 60% by weight of an ethylenically unsaturated monomer having a hydroxy group a 3 ) about 20 to about 90% by weight of other ehtylenically unsaturated monomers. Preferred polyacrylate resins (A) comprise a 1 ) about 10 to about 60% by weight of an ethylenically unsaturated monomer having an epoxy group a 2 ) about 20 to about 50% by weight of an ethylenically unsaturated monomer having a hydroxy group a,) about 30 to about 80% by weight of other s. Most preferred polyacylate resins (A) comprise a,) about 15 to about 25% by weight of an ethylenically unsaturated monomer having an epoxy group a 2 ) about 30 to about 40% by weight of an ethylenically unsaturated monomer having a hydroxy group a 3 ) about 40 to about 60% by weight of other ehtylenically unsaturated monomers. Suitable ethylenically unsaturated monomers having an epoxy group (a.,) are selected from the group consisting of glycidylacrylat, glycidylmethacrylat or mixtures thereof. Suitable ethylenically unsaturated monomers having a hydroxy group (a 2 ) are selected from the group consisting of hydrocyethylacrylate, hydrocyethylmethacrylate, hydroxypropylacrylate, hydroxypropylmethacrylate, hydroxybutylacrylate, hydroxybutylmethacrylate or mixtures thereof. The other ethylenically unsaturated monomers (a 3 ) may be chosen from acrylic or methacrylic alkyl ester derived from alcohols having 1 ot about 20 carbon atoms, or vinyl monomers. The expression (meth)acrylate with parenthesis as used herein includes methacrylate and acrylate. Suitable examples are methyl(meth)acrylate, ethyl(meth)acrylate, propyl(meth)acrylate, n-butyl(meth)acrylate, isobutyl- ( eth)acrylate, tert.-butyl(meth)acrylate and 2-ethylhexyl- (meth) acrylate, maleic acid or fumaric acid dialkylesters in which the alkyl groups have 1 to 20 carbon atoms, vinylaromatics such as styrene, alpha-methylstyrene, vinyltoluene, tert.-butylstyrene, halogenated vinylbenzenes such as chlorostyrene, and other monomers like vinylchloride, (meth)acrylamide and (meth)-acrylonitrile. SUBSTITUTESHEET Preferred monomers (a n ) , (a 2 ) and (a 3 ) are glycidyl methacrylate, hydroxy ethyl acrylate, hydroxy propyl acrylate, hydroxy butyl acrylate, methy(meth)acrylate, butyl(meth)acrylate, ethylhexyl(meth) crylate. Suitable resin (B) are polyacrylate resins having anhydride functionality obtainable by polymerizing b.,) about 1 to about 50% by weight of an ethylenically unsaturated monomer having an anhydride group b 2 ) about 50 to about 99% by weight of other ethylenically unsaturated monomers. Preferred polyacrylate resins (B) comprise b.,) about 20 to about 40% by weight of an ethylenically unsaturated monomer having an anhydride group b 2 ) about 60 to about 80% by weight of other ethylenically unsaturated monomers. Most preferred polyacrylate resins (B) comprise b.,) about 25 to about 35% by weight of an ethylenically unsaturated monomer having an anhydride group b 2 ) about 65 to about 75% by weight of other ethylenically unsaturated monomers. Suitable ethylenically unsaturated monomers having an anhydride group (b.,) are selected from the group consisting of maleic anhydride, itaconic anhydride or mistrues thereof. Preferred is maleic anhydride. Other ethylenically unsaturated monomers (b 2 ) comprise the ones described unc_r the monomers (a 3 ) and additionally acrylic and methacrylic acid. Preferred are acylic or methacrylic , , , ethylhexyl(meth)acrylate and mixtures thereof. In order to produce the polyacrylic resins (A) and (B) copolymerization of the described monomers is carried out using conventional techniques such as heating the monomers in the presence of a polymerization initiating agent and optionally chain transfer agents. The copolymerization is preferably carried out in solution. Suitable solvents for solution polymerization are ethylene glycol or propylene glycol and their derivatives, such as dipropylene glycol monomethlether and ethylene glycol monobutyl etheracetate; alcohols, such as butyl alcohol and diacetone alcochol; ketones, such as methyl propyl ketone, methyl amyl ketone and acetone; esters, such as butyl acetate, and pentyl propionate; ethers, such as dioxane and tetrahydrofuran; aromatic solvents, such as xylene, toluene, and aromatic solvent blends and mixtures thereof. Typical initiators are peroxides such as dialkylperoxides, peroxyesters, peroxydicarbonates, diacylperoxides, hydroperoxides, and peroxyketals and azo compounds such as 2,2'- azobis(2-methylbutanenitrile) and 1,1'-azobis (cyclohexanecarbonitrile) . Typical chain transfer agents are mercaptans such as octylmercaptan, n- or tert.-dodecylmercaptan; halogenated compounds; thiosalicylic acid, mercaptoacetic acid, mercaptoethanol, buten-1-ol, and dimeric alpha-methylstyrene. Mercaptans are preferred. The reaction is usually carried out at temperatures from about 20°C yo about 200°C. The reaction may conveniently be done at the temperature at which the solvent or solvent mixture refluxes, although with proper control a temperature below the reflux may be maintained. The initiator should be chosen to match the temperature at which the reaction is carried out, so that the half-life of the initiator at that SUBSTITUTESHEET temperature should preferably be between one minute and thirty minutes. The solvent or solvent mixture is generally heated to the reaction temperature and the monomers and initiator(s) are added at a controlled rate over a period of time, usually between 2 and 6 hours. A chain transfer agent or additional solvent may be fed in also at a controlled rate during this time. The temperature of the mixture is then maintained for a period of time to complete the reaction. Optionally, additional initiator may be added to ensure complete conversion. The polyacrylate has a weight average molecular weight of from about 2,000 to about 40,000, perferably from about 2,000 to about 25,000. The theoretical Tg of the polyacrylate (A) is from about -15°C to about 30 β C, preferably from about -5 β C to about 20°C. The theoretical Tg of the polyacrylate (B) is from about 10 to about 100°C, preferably from about 30"C to about 70°C. The aminoplast resin (C) is comprised of a nucleus or nuclei of acetoguanamine, benzoguanamine, adipoguana ine, or melamine, with the preferred being melamine. The aminoplast resin is considered to be fully aklylated, or substantially completely methylolated and subsequently substantially fully etherified with alcohol, with the number of alkyloxymethyl groups ranging from 2n-2 to 2n where n is the number of amino groups on the triazine ring. The preferred degree of polymerization of this aminoplast is from 1 to 3. Suitable additives (D) are selected from the group consisting of solvents, catalysts, flow modifying agents, ultraviolet absorbers, hindered amine light stabilizers, solvents, catalysts mixtures thereof. Suitable solvents for the coating composition are conventional solvents used in the coating industry for . a c hydrocarbons such as hexane and heptane; aromatic hydrocarbons such as toluene, and xylene; various petroleum fractions having a suitable boiling point range; esters such as butyl acetate, ethylene glycol diacetate and 2-ethoxyethyl acetate; ketones such as acetone, methyl ethyl ketone and methyl isobutyl ketone; alcohols such as butanol and mixtures of these solvents. Preferred solvents are xylene, butyl acetate, ethylethoxy proprionate and mixtures thereof. Suitable catalysts are amine blocked sulfonic acids, phenyl acid phosphate (PAP) , triphenyl phosphine, l,4-diazobicyclo[2.2.2]octane (DABCO) , AC-8 from Acids and Anhydrides Inc. Preferred are amine blocked p-toluene sulfonic acid (p-TSA) , amine blocked dodecylbenzene sulfonic acid (DDBSA) . For the preparation of the coating composition all components were mixed together in a range of from about 10 to about 35% by weight, preferable from about 15 to about 25% by weight of component (A) , from about 50 to about 75% by weight, preferable from about 55 to about 60% by weight of component (B) , from about 5 to about 20% by weight, preferable from about 10 to about 15% by weight of component (C) , from about 1 to about 15% by weight, preferable from about 5 to about 12% by weight of component (D) . The solid content of the final coating composition is from about 40 to about 60% by weight, preferable from about 50 to about 60% by weight. The viscosity is 18-30 seconds #4 Ford Cup, preferable 22-28 seconds #4 Ford Cup. This coating composition is applied on a conventional basecoat used in the coating industry, especially on high solids solvent-borne and water-borne basecoat, by conventional methods especially by brushing, roller coating, calendering. SUBSTITUTESHEET dip coating, flow coating or air atomizing, in a thickness of the film of about 0.5 to 2.2 mils, preferably 1.2 to 1.9 mils. The multilayer coating is then cured or dried at temperatures of 100 to 130"C. The resulting multilayer coating exhibits superior solvent resistance, acid resistance and hardness. Example 1 Resin (A) having Epoxy and Hydroxy functionality: A 5 liter reactor equipped with an agitator, straight reflux condenser, thermometer, monomer and intiator addition tanks, and variable heat source is used. The reactor is charged with 912g methylpropyl ketone and 228g of butyl acetate, and heated to reflux, 118 β C. The monomer addition tank is charged with 2 0g butyl acrylate, 838g butylmethacrylate, 838g hydroxy ethyl acrylate, and 479g glycidyl methacrylate. 260g of tert butyl peroctoate. The monomers and initiators are added to the reactor over 4 hours while maintaining reflux. When the monomers and initiator additions are complete the reaction is held at reflux for an additional 2 hours to complete the polymerization. The reaction is cooled and the polymer is filtered. Example 2 Resin (B) having Anhydride Functionality A 5 liter reactor equipped with an agitator, straight reflux condenser, thermometer, monomer and initiator addition tanks, and variable heat source is used. The reactor is charged with 52Og methyl propyl ketone and heated to reflux at 105°C. 616g Maleic anhydride is dissolved in lOOOg methyl amyl ketone. This mixture is charged to the monomer tank in addition to 616g butyl acrylate, 575g butylmethacrylate, 41g acrylic acid, and 205g styrene. 226g of tert butyl peroctoate, is charged to the initiator tank. Monomers and initiators are added to the reactor over 4 hours while maintaining reflux. The reflux temperature will 8 n. en monomers and initiator additions are complete the reaction is held at reflux for an additional 2 hours to complete the polymerization. The reaction is cooled and the polymer is filtered. The resulting anhydride functional polymer (B) has a weight average molecular weight of 2400 by gel permeation chromatography, an acid number of 32, an anhydride equivalent weight of 1.65meq/g and a viscosity of 2.4 dPas. Example 3 Resin (C) for Prior Art A 5 liter reactor equipped with an agitator, straight reflux condenser, thermometer, monomer and initiator addition tanks, and variable heat source is used. The reactor is charged with 712.3g primary amyl acetate, 186.Og of aromatic solvent blend sold under the trade name Aromatic 100 from Exxon, and 77.14g of cumene hydroperoxide and heated to reflux, 151°C. The monomer tank is charged with 513,4g butyl acrylate, 847.4g butyl methacrylate, 898.7g of hydroxyethyl acrylate, 51.3g acrylic acid, and 256.9g styrene. 102.7g of cumene hydroperoxide, 102.7 g of dicumyl peroxide and 51.4g of aromatic solvent blend, sold under the trade name Aromatic 100 form Exxon, are charged to the initiator tank. The monomers and initiators are added to the reactor over 4 hours while maintaining reflux. The reflux temperature will slowly increase to 160°C during the monomer addition. When the monomers and initiator additions are complete the reaction is held at reflux for an additional 2 hours to complete the polymerization. The reaction is cooled and the polymer is filtered. The resulting hydroxyl functional polymer resin (C) has a weight average molecular weight of 4400 by gel permeation chromatography, a hydroxy number of 169, an acid number of 16, and a viscosity of 13 dPas at 23°C. SUBSTITUTE SHEET Example 4 Coating Composition A coating composition with the following composition by weight: Item WT% Description Resin (A) 21.9 Epoxy and Hydroxy Functional Resin from Example 1 Resin (B) 53 Anhydride resin from Example 2 Cymel 303 12.8 hexamethoxy methyl from American Cyanamid Sanduvar 3206 2.3 Oxanilide UV absorber from Sandoz Color and Chemical Tinuvin 440L sol'n 1 ) 2.6 Hindered Amine Light Stabilizer from Ciba Geigy Polybutyl Acrylate 0.5 A620A2 from Cook Paint & Varnish Nacure 5543 5.1 Diisopropylamine block Dodecyl Benzene Sulfonic Acid from King Industries Ethylethoxy 1.8 propionate 1) 30% solution of Tinuvin 440L in Xylene Components are mixed, and adjusted to spray viscosity of 22- 28sec. #4 Ford cup with xylene and sprayed with a siphon or pressure pot gun to a film thickness of 1.4-1.9 mils. Example 5 Preparation of coating composition according to the Prior Art Cost composition for Prior Art 10 Nacure 5543 5.1 Diisopropylamine block Dodecyl Benzene Sulfonic Acid from King Industries Xylene 18.33 1) 30% solution of Tinuvin 440L in xylene Components are mixed, and adjusted to spray viscosity of 22- 28sec. #4 Ford cup with xylene and sprayed with a siphon or pressure pot gun to a film thickness of 1.4-1.9 mils. 11 SUBSTITUTE SHEET Results Test Coating Prior Art described in atent Acid Spot Test: 0.5, 1.0, 2.0, and 4.0% Hydrochlorid Acid backed on film at 185°F for 30 minutes Acid spot rating 1- Poor; 5- Good 12

Claims: 1. A coating composition comprising A) a resin with epoxy and hydroxy functionality B) a resin with anhydride functionality C) an aminoplast resin and D) additives selected from the group consisting of solvents, catalysts, flow agents, hindered amine light stabilizers, ultraviolet absorbers. 2. A coating composition comprising A) about 10 to about 35% by weight of a resin with epoxy and hydrocy functionality B) about 50 to about 75% by weight of a resin with anhydride functionality C) about 5 to about 20% by weight of an aminoplast resin and D) about 1 to about 15% by weight of additives selected from the group consisting of solvents, catalysts, flow agents, hindered amine light stabilizer, ultraviolet absorbers. 3. A coating composition according to claim 1, wherein component (A) is a polyacrylate resin having epoxy and hydroxy functionality. 4. A coating composition according to claim 1, wherein component (B) is a polyacrylate resin having anhydride functionality. 5. A coating composition comprising A) a polyacrylate resin having epoxy and hydroxy functionality obtainable by polymerizing a.,) about 5 to about 80% by weight of an ethylenically unsaturated monomer having an epoxy group 13 SUBSTITUTESHEET a 2 ) about 5 to about 60% by weight of an ethylenically unsaturated monomer having a hydroxy group a 3 ) about 20 to about 90% by weight of other ehtylenically unsaturated monomers. B) a polyacrylate resin having anhydride functionality obtainable by polymerizing t ) about 1 to about 50% by weight of an ethylenically unsaturated monomer with an anhydride group b 2 ) about 50 to about 99% by weight of other ethylenically unsaturated monomers. C) an aminoplast resin and D) additives selected from the goup consisting of solvents, catalysts, flow agents, hindered amine light stabilizers, ultraviolet absorbers. 6. A coating composition according to claim 5, wherein component (a t ) is selected from the group consisting of glycidylacrylat, glycidylmethacylat and mixtures thereof. 7. A coating composition according to claim 5, wherein component (a 2 ) is selected from the group consisting of hydroxyethylacrylate, hydroxyethylmethacrylate, hydroxypropylacrylate, hydroxyproplylmethacrylate, hydroxybutylacrylate, hydroxybutylmethacrylate and mixture thereof. 8. A coating composition according to claim 5, wherein component (b..) is selected from the group consisting of maleic anhydride, itaconic anhydride and mixtures thereof. 9. A method of coating a substrate with multiple layers of coatings comprising applying the coating composition according to claim 1 as a clearcoat on a basecoat. 10. A substrate coated with a least one coating 14 . 15 SUBSTITUTE SHEET

Inventors: SERDIUK PAUL, SERDIUK, PAUL
Applicants: BASF CORP, BASF CORPORATION
Application year: 1992
Main classification: C08L35
IPC codes: C08L33, C08L35, C08L61, C08L63, C09D133, C09D135, C09D161, C09D163