Antibacterial calcium tertiary phosphate

Abstract: A calcium tertiary phosphate is used as a carrier, and the carrier is caused to carry silver and zinc. The result is an antibacterial ceramic exhibiting an ultra high degree of whiteness and suppressed discoloration. This material may be heat fired at a temperature above 960°C to obtain a further improvement.

Description: This invention relates to an antibacterial calcium tertiary phosphate. More particularly, the invention relates to calcium tertiary phosphate made to carry silver and zinc and/or ions thereof, wherein calcium tertiary phosphate is safe, exhibits a high degree of whiteness and resists discoloration to the maximum extent. It is known from GB-A-2238044 that metals such as silver and zinc as well as ions and salts of these metals exhibit a strong antibacterial property, and various processes have been proposed for utilizing these. However, when these metals are used as is in mixture with a substrate such as resin, fibers or paint, problems arise involving dispersibility with respect to the substrate, the eluting property of the metal ions, tinting and discoloration. For this reason, use in wide fields of application has not been possible. Substances in which antibacterial metals, metal salts or metal ions are carried on highly safe ceramics have recently been proposed as substances which utilize the antibacterial property of the above-mentioned metals. For example, the antibacterial ceramics, in which the antibacterial metal ions are carried on zeolite, is disclosed in Japanese Patent Laid Open Publication Sho 60-181002 and the antibacterial ceramics, in which the antibacterial metal ions are carried on hydroxyapatite, is disclosed in Japanese Patent Laid Open Publication Hei 2-180270. Since these substances exhibit reduced elution of the carried antibacterial metal ions into water and have improved dispersibility with respect to the substrate, they can be utilized comparatively safely and in many fields of application. However, depending upon the medium used, even these substances undergo elution of their metal ions into the medium, and therefore they cannot always be used with complete safety in all types of media. Generally, silver is used as the antibacterial metal, because silver has the strong antibacterial property, however, it is known that silver generally is sensitive to light and will break down and change color to gray or black when exposed to light. Accordingly, silver salts undergo discoloration when used as such. Antibacterial agents in which this metal salt is carried on ceramics or the like can lead to problems not only in terms of discoloration but also in terms of safety since the elution of silver from the silver salt and the release of silver salt from the ceramics cannot be reasonably prevented. Though zeolite made to carry silver by means of ion exchange exhibits less discoloration in comparison to those cases where the silver salt is used as such, discoloration with the passage of time is unavoidable. In comparison with zeolite carrying silver, hydroxyapatite made to carry silver by ion exchange is much improved in terms of discoloration attributable to the silver, but complete suppression of discoloration has still not been realized. Studies have been conducted with a view to improving upon the foregoing, and processes for carrying zinc along with silver on hydroxyapatite and further heat-firing has been considered. However, in cases where zinc is carried together with silver, the antibacterial hydroxyapatite tends to become light gray in color as the amount of silver carried is increased, and even though the color is close to white, the degree of whiteness is low. In addition, discoloration cannot be completely suppressed over an extended period of time. In cases where heat-firing is carried out, discoloration can be suppressed. Nevertheless, the antibacterial agent itself still becomes light brown in color and the degree of whiteness diminishes as the amount of silver carried increases. These problems arise when silver is used as the antibacterial metal, and though improvements have been made by carrying zinc and silver on hydroxyapatite and heat firing thereof, these still have not been resolved the problem totally. Accordingly, an object of the present invention is to provide antibacterial calcium tertiary phosphate, which exhibits a high degree of whiteness, will not undergo discoloration even when stored for very long periods of time, and in which safe calcium tertiary phosphate is used as the carrier. This object is solved by antibacterial calcium tertiary phosphate having the features of claim 1. As mentioned above, an antibacterial agent obtained by having hydroxyapatite carry silver and zinc and/or ions thereof or subsequently being heat-fired is an easy-to-use antibacterial material which also exhibits excellent dispersibility in substrates, discoloration has been seen with the passage of time, and the antibacterial agent becomes light brown in color as a result. As a consequence, problems arise in terms of storage of the antibacterial agent and the color of manufactured articles produced with use of the agent, and therefore the fields of application are limited. Also, when the antibacterial agent, in which silver and zinc are carried on the carrier selected from calcium primary phosphate, calcium secondary phosphate and calcium pyro phosphate, and then the heat fired substances thereof are used, the problems in terms of discoloration, tinting, using and storing are overcome arise in comparision to using hydroxyapatite as the carrier. Accordingly, the inventors have devoted research to silver-containing inorganic antibacterial agents which exhibit an ultra high degree of whiteness and will not undergo discoloration. As a result of this research, the inventors have been able to obtain an antibacterial agent which attains the foregoing object. Specifically, by using calcium tertiary phosphate as the carrier and causing this carrier to carry silver zinc, an antibacterial agent exhibiting an ultra high degree of whiteness and substantially suppressed discoloration has been obtained. By heat-firing calcium phosphate, which has been made to carry silver and zinc, at a temperature above 960°C, an antibacterial agent which exhibits a superior degree of whiteness higher than that of the antibacterial hydroxyapatite heat fired, and which will not undergo discoloration, has been obtained. More specifically, a prescribed amount of calcium tertiary phosphate is added to an aqueous solution, in which the prescribed amounts of silver and zinc salts are dissolved. The mixture is stirred. After sufficient stirring, precipitates are filtered out and the product is washed thoroughly with distilled water and then dried, whereby there is obtained on antibacterial calcium tertiary phosphate. The degree of whiteness of the obtained antibacterial calcium tertiary phosphate ceramics naturally is influenced by the amount of silver carried, just as it is influenced by the adsorption retention ratio of the silver and zinc. That is, in order to obtain an antibacterial calcium tertiary phosphate exhibiting a superior high degree of whiteness and no change in color with the passage of time, the amount of silver adsorbed and retained should be no more than 10% by weight, and preferably no more than 5% by weight, with respect to the calcium tertiary phosphate. On the other hand, in consideration of antibacterial capability, the amount of silver retained preferably is no less than 0.0001%. When the amounts of silver carried on hydroxyapatite are over 0.1% in the antibacterial hydroxyapatite, even if zinc coexists, the color becomes bad, and discoloration occurs with the passage of time. Meanwhile,when calcium tertiary phosphate is used as the carrier, change in color is less. A change in color with the passage of time can be suppressed even further by heat-firing the product at a temperature above 961°C, which is the melting point of silver. The amount of zinc retained in coexistence with silver is required to be at least 5% by weight with respect to the amount of silver retained. The amount of zinc retained can be selected at will. An example of the present invention will now be described in detail. Example 1 1.0kg of calcium tertiary phosphate, 0.002 of silver nitrate and 47g of zinc nitrate were added to 10ℓ of distilled water and stirred. The product was filtered out, washed throughly with distilled water and dried and a portion of the resulting product was powdered to obtain an antibacterial calcium tertiary phosphate carrying silver, about 0.0001% and zinc, about 1% (1-1). The remainder of this product was heat fired at 960°C, and powdered to obtain an antibacterial calcium tertiary phosphate carrying silver, about 0.0001% and zinc, about 1% (1-2). Example 2 1.0kg of calcium tertiary phosphate, 2g of silver nitrate and 0.24g of zinc nitrate were added to 10ℓ of distilled water and stirred. The product was filtered out, washed throughly with distilled water, and dried, and a portion of the resulting product was powdered to obtain an antibacterial calcium tertiary phosphate carrying silver, 0.1% and zinc, 0.005% (2-1). The remainder of this product was heat fired at 1,000°C and powdered to obtain an antibacterial calcium tertiary phosphate carrying silver, 0.1% and zinc, 0.005% (2-2). Example 3 1.0kg of calcium tertiary phosphate, 34g of silver nitrate and 93g of zinc nitrate were added to 10ℓ of distilled water and stirred. The product was filtered out, washed throughly with distilled water, and dried. A portion of the resulting product was powdered and an antibacterial calcium tertiary phosphate carrying silver, about 2% and zinc, about 2% was obtained (3-1). Also the remainder of this product was heat fired at 1,200°C and powdered. An antibacterial calcium tertiary phosphate carrying silver, about 2% and zinc, about 2% was obtained (3-2). Example 4 1.0kg of calcium tertiary phosphate, 82g of silver nitrate and 140g of zinc nitrate were added to 10ℓ of distilled water and stirred. The product was filtered out, washed throughly with distilled water, dreid. A portion of the resulting product was powdered and an antibacterial calcium tertiary phosphate carrying silver, about 5% and zinc, about 3% was obtained (4-1). Also the remainder was heat fired at 1,200°C and powdered. An antibacterial calcium tertiary phosphate carrying silver, about 5% and zinc, about 3% was obtained (4-2). Example 5 1.0kg of calcium tertiary phosphate, 165g of silver nitrate and 233g of zinc nitrate were added to 10ℓ of distilled water and stirred. The product was filtered out, washed thoughly with distilled water and dried. A portion of the resulting product was powdered and an antibacterial calcium tertiary phosphate carrying silver, about 10% and zinc, about 5% was obtained (5-1). The remainder of this product was heat fired at 1,200°C and powdered. An antibacterial calcium tertiary phosphate carrying silver, about 10% and zinc, about 5% was obtained (5-2). Example 6 antibacterial test A solution containing 4.7 x 10 5 colon bacilli was added to a phosphate buffer solution, in which 1 weight% of each of the samples obtained in examples 1 to 5 is added, and the antibacterial property against the colon bacilli was measured for each sample. The result of measurement was that absolutely no bacteria was delected in 24 hours. Example 7 whiteness degree test A spectrophotometer was used to measure the whiteness degree of the antibacterial calcium tertiary phosphate powders produced in examples 1 to 5. Barium sulfate was used as the standard substance. As the control, hydroxyapatites carrying silver and zinc were prepared by the same way as shown in each examples in which hydroxyapatite is used in place of calcium tertiary phosphate. ((Unheat fired (control 1-1 to control 5-1), heat fired (control 2-1 to control 2-5)) and the whiteness degree was measured. Further, the whiteness degree of these sampels were measured after letting them stand in a bright room for 6 months. Similarly, unheat fired and heat fired calcium tertiary phosphates carrying only silver (Unheat fired (T1-1 to T5-1) and heat fired (T1-2 to T5-2)) and unheat fired and heat fired hydroxyapatites carrying only silver (Unheat fired (H1-1 to H5-1) and heat fired (H1-2 to H5-2)) were prepared, and the whiteness degree was measured. The results obtained were shown in Table 1. The effects for the whiteness degree and discoloration are clear, when clacium tertiary phosphate is used as the carrier. Reference Example Calcium secondary phosphate carrying silver 2%, calcium pyro phosphate carrying silver 2%, the heat fired bodies thereof which are heat fired at 1,200°C, calcium secondary phosphate carrying silver, 2% and zinc, 2%, calcium pyro phosphate carrying silver, 2% and zinc, 2%, and heat fired bodies thereof which are heat fired at 1,200°C were prepared and the whiteness degree was measured. The results were shown in Table. 2. metal and amount carried carrier whiteness degree not heat fired 1200°C heat fired original powder after standing for 6 months original powder after standing for 6 months silver 2% calcium secondary phosphate 57.49 25.32 58.16 45.92 calcium pyro phosphate 52.93 27.40 51.36 44.00 silver 2% calcium secondary phosphate 64.32 37.36 76.01 67.33 zinc 2% calcium pyro phosphate 60.06 36.87 69.66 66.18

Claims: An antibacterial calcium tertiary phosphate on which silver and zinc and/or ions thereof are absorbed, characterized in that the amount of silver absorbed is 0.0001-10% by weight with respect to calcium tertiary phosphate and the amount of zinc absorbed is more than 5% by weight with respect to the amount of silver absorbed, wherein the amounts 0.5% AG/1% Zn and 0.8% AG/1% Zn by weight with respect to the amount of antibacterial calcium tertiary phosphate are excepted. The antibacterial calcium tertiary phosphate of claim 1, wherein said antibacterial calcium tertiary phosphate is heat fired at a temperature of not less than 960°C.

Inventors: ATSUMI KIMINORI, KOMORI MASAAKI, SAITO TOMOKI, ATSUMI, KIMINORI, KOMORI, MASAAKI, SAITO, TOMOKI, Atsumi, Kiminori, c/o Kabushiki Kaihsa Sangi, Komori, Masaaki, c/o Kabushiki Kaihsa Sangi, Saito, Tomoki, c/o Kabushiki Kaihsa Sangi
Applicants: SANGI KK, KABUSHIKI KAISHA SANGI
Application year: 1992
Main classification: A01N59
IPC codes: A01N59, A01N25