N-olefin isomerization process

Abstract: A process for conversion of linear olefins to corresponding iso-olefins of the same carbon number comprises contacting a linear olefin-containing organic feedstock with a catalyst comprising ZSM-22 having a crystal size in which the largest dimension is no greater than 0.5 micron, and in which the ratio of the second largest dimension to the largest dimension ranges from 0.5 to 1.

Description: This invention relates to a process for the isomerization of n-olefins, e.g. the isomerization of n-butene-containing, hydrocarbon streams to isobutene-rich product streams. The demand for iso-alkenes has recently increased. For example, relatively large amounts of isobutene are required for reaction with methanol or ethanol over an acidic catalyst to produce methyl tert-butyl ether (MTBE) or ethyl tert-butyl ether (ETBE) which is useful as an octane enhancer for unleaded gasolines. Isoamylenes are required for reaction with methanol over an acidic catalyst to produce tert-amyl methyl ether (TAME). With passage of the Clean Air Act in the United States mandating increased gasoline oxygenate content, MTBE, ETBE and TAME have taken on new value as clean-air additives, even for lower octane gasolines. Lead phase-down of gasolines in Western Europe has further increased the demand for such oxygenates. An article by J.D. Chase, et al., Oil and Gas Journal , April 9, 1979, discusses the advantages one can achieve by using such materials to enhance gasoline octane. The blending octane values of MTBE when added to a typical unleaded gasoline base fuel are RON = 118, MON = 101, R+M / 2 = 109 . The blending octane values of TAME when added to a typical unleaded gasoline base fuel are RON = 112, MON = 99, R+M / 2 = 106 . Isobutene (or isobutylene) is in particularly high demand as it is reacted with methanol to produce MTBE. The addition of shape-selective zeolite additives such as ZSM-5 to cracking catalysts, e.g. those used in fluidized catalytic cracking (FCC), is beneficial in producing gasoline boiling range product of increased octane rating. However, increased amounts of olefins result, including n-butenes, creating a need for their conversion to higher value products such as isobutene which can be used to produce MTBE. Butene exists in four isomers: butene-1, cis-butene-2, its stereo-isomer trans-butene-2, and isobutene. Conversions between the butenes-2 is known as geometric isomerization, whereas that between butene-1 and the butenes-2 is known as position isomerization, double-bond migration, or hydrogen-shift isomerization. The aforementioned three isomers are not branched and are known collectively as normal or n-butenes. Conversion of the n-butenes to isobutene, which is a branched isomer, is widely known as skeletal isomerization. The reaction of tertiary olefins with alkanol to produce alkyl tertiary alkyl ether is selective with respect to iso-olefins. Linear olefins are unreactive in the acid catalyzed reaction, even to the extent that it is known that the process can be utilized as a method to separate linear and iso-olefins. There is therefore a need to provide a technically and economically practical means to utilize linear olefins, particularly normal butene, in the manufacture of tertiary alkyl ethers. European Patent 0026041 discloses a process for the restructuring of olefins in contact with zeolite catalyst to produce iso-olefins, followed by the conversion of iso-olefins to MTBE and TAME. The restructuring conditions comprise temperature between 204°C and 315°C and pressure below 51 kPa. U.S. Patent 4,922,048 discloses the use of a wide variety of medium pore size zeolites, e.g. ZSM-5, ZSM-11, ZSM-12, ZSM-22, ZSM-23, ZSM-35 and ZSM-48, in low temperature (232-385°C) interconversion of C₂-C₆ olefins to products including tertiary C₄-C₅ olefins and olefinic gasoline. In European Patent 0247802, it is taught that linear olefins can be restructured in contact with a zeolite catalyst, including Theta-1 (ZSM-22) and ZSM-23, to produce branched olefins. The restructuring conditions comprise a temperature between 200-550°C, a pressure between 100 and 5000 kPa and WHSV between 1 and 100. Selectivities to isobutene up to 91.2% are reported using a calcined Theta-1 tectometallosilicate at 400°C and 30.6% 1-butene conversion. The Theta-1 crystals have acicular lathe (needle-like) morphology with a broad distribution of crystal sizes having the largest dimension of up to 1 to 2 microns. Despite the efforts exemplified in the above references, the skeletal isomerization of olefins e.g., of n-butenes to produce isobutene, has been hampered by relatively low conversion and/or selectivity to isobutene perhaps owing to the lability of these olefins. It is further known that skeletal isomerization becomes more difficult as hydrocarbons of lower molecular weight are used, requiring more severe operating conditions, e.g. higher temperatures and lower linear olefin partial pressures. Generally, the conversion of n-butenes to iso-butene is conducted at selectivities below 90%. In order to obtain higher selectivities, operation at high temperatures (>500°C) and with high feed dilution (butene partial pressure, typically less than 5 psia [34.5 kPa]) is generally required. Selectivities of greater than 85%, 90%, 95% or even 99% are highly advantageous in commercial conversion of n-butenes to isobutene in order to avoid the need to separate out materials other than n-butene from the product stream. Such high selectivities will permit direct (cascading) or indirect introduction of the isomerizer effluent to an etherification zone where isobutene is reacted with alkanol to produce alkyl tert-butyl ether, e.g. MTBE. Unconverted n-butenes in the isomerizer effluent can be withdrawn either before the etherification zone or preferably, from the etherification zone effluent insofar as the etherification reaction utilizes only the isobutene component of the isomerizer stream. Unreacted n-butenes from the etherification zone effluent can be recycled to the isomerizer where they are converted to isobutene at high selectivity. If the recycle stream contains not only unconverted linear olefins, e.g. n-butenes, but also by-products such as other olefins (e.g. propylene) or paraffins, they have to be removed from the recycle stream, such as by distillation. These removal steps are expensive and can lead to considerable loss of not only the by-products but butenes as well. These losses are larger when the by-products formed are present in higher concentration. Thus, even small improvements in the isobutene selectivity during n-butene isomerization can have a major effect on the commercial viability of the process. It is therefore an object of the present invention to provide a process for the skeletal isomerization of linear olefins capable of maintaining a high level of conversion as well as high iso-olefin selectivity, even at relatively low temperatures, e.g., no greater than 450°C and high n-olefin space velocities, e.g., no less than 5, e.g., no less than 70. The present invention provides a process for conversion of linear olefins to corresponding iso-olefins of the same carbon number which comprises contacting a linear olefin-containing organic feedstock with a catalyst comprising ZSM-22 having a crystal size in which the largest dimension is no greater than 0.5 micron, and in which the ratio of the second largest dimension to the largest dimension ranges from 0.5 to 1. ZSM-22 is a zeolite having a one-dimensional channel system made up of 10-member rings, elliptical in nature, with a free diameter of 4.7 by 5.5 angstrom units. ZSM-22 and its preparation using hexanediamine as directing agent is more particularly described in U.S. Patent No. 4,556,557 to Dwyer. U.S. Patent No. 4,481,177 to Valyocsik discloses the preparation of microcrystalline ZSM-22 using ethylpyridinium as directing agent and sources of silicon such as colloidal silica or silica sol. For purposes of the present invention, amorphous precipitated silica may also be used as a source of silicon. For present purposes, "ZSM-22" is considered equivalent to its isotypes, which include Theta-1 (S. A. I. Barri, G. W. Smith, D. White and D. Young, Nature 312 , 533 (1984), R. M. Highcock, G. W. Smith and D. Wood, Acta Cryst. C41 , 1391 (1985); ISI-1 (T. Kozo and K. Noboru, European Patent Application 170,003 (1986)); KZ-2 (L. M. Parker and D. M. Bibby, Zeolites 3 , 8 (1983)); and NU-10 (A. Araya and B. M. Lowe, Zeolites 4 , 280 (1984)). The ZSM-22 used in the process of the invention has a crystal morphology whose largest dimension is no greater than 0.5 micron, preferably no greater than 0.3 micron and in which the ratio of the second largest dimension to the largest dimension ranges from 0.5 to 1. Most preferably the ZSM-22 crystals can be described as falling within the range of 0.2 to 0.4 micron by 0.1 to 0.4 micron by < 0.1 micron. The ZSM-22 catalyst used is preferably at least partly in the hydrogen form, but other cations, e.g. rare earth cations, may also be present. When the zeolite is prepared in the presence of organic cations, it may be relatively inactive because the intracrystalline free space is occupied by the organic cations from the forming solution. The zeolite may be activated by heating in an inert atmosphere to remove the organic cations e.g. by heating at over 500°C for 1 hour or more. The hydrogen form can then be obtained by base exchange with ammonium salts followed by calcination e.g. at 500°C in air. Other cations, e.g. metal cations, can be introduced by conventional base exchange or impregnation techniques. In order to obtain desired linear olefin skeletal isomerization activity/selectivity, ZSM-22 should have an alpha value of at least 5, preferably at least 50 when used in the process of the present invention. Alpha value, or alpha number, of a zeolite is a measure of zeolite acidic functionality and is more fully described together with details of its measurement in U.S. Patent No. 4,016,218, J. Catalysis , 6 , pp. 278-287 (1966) and J. Catalysis , 61 , pp. 390-396 (1980). The ZSM-22 may be incorporated in another material usually referred to as a matrix or binder. Such matrix materials include synthetic or naturally occurring substances as well as inorganic materials such as clay, silica and/or metal oxides. The latter may be either naturally occurring or in the form of gelatinous precipitates or gels including mixtures of silica and metal oxides. Naturally occurring clays which can be composited with the zeolite include those of the montmorillonite and kaolin families, which families include the subbentonites and the kaolins commonly known as Dixie, McNamee, Georgia and Florida clays or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite or anauxite. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification. In addition to the foregoing materials, the ZSM-22 employed herein may be composited with a porous matrix material, such as silica, alumina, zirconia, titania, silica-alumina, silica-magnesia, silica-zirconia, silica-thoria, silica-beryllia, silica-titania as well as ternary compositions such as silica-alumina-thoria, silica-alumina-zirconia, silica-alumina-magnesia and silica-magnesia-zirconia. The matrix can be in the form of a cogel. A mixture of these components could also be used. Of all the foregoing materials, silica may be preferred as the matrix material owing to its relative inertness for catalytic cracking reactions which are preferably minimized in the instant isomerization processes. The relative proportions of finely divided ZSM-22, and inorganic oxide gel matrix vary widely with the zeolite content ranging from 1 to 90 percent by weight and more usually in the range of 30 to 80 percent by weight of the composite. The process of the invention is conveniently conducted at a temperature of 100 to 750°C, preferably 200 to 600°C, more preferably 250 to 550°C, a weight hourly space velocity (WHSV) based on linear olefins in the feedstock of 0.1 to 500, preferably 1 to 400, more preferably 5 to 100 and a linear olefin partial pressure of 2 to 2000 kPa, preferably 10 to 500 kPa, more preferably 50 to 200 kPa. Under these conditions the conversion of linear olefin, e.g., n-butene, can be at least 20%, preferably at least 35% and more preferably at least 45%. The selectivity to iso-olefin, e.g., isobutene, is at least 75%, preferably at least 85%, 90%, or even 95%. The present invention is especially suited to processes carried out at high linear olefin to iso-olefin selectivity, e.g, at least 60% at relatively low conversion temperatures and high linear olefin partial pressures. Such processes can maintain selectivities of at least 75, 85 or 95% at a conversion temperature less than or equal to 550, 450, 400 or even 350°C, and linear olefin partial pressures above 2 psia (14 kPa), e.g. above 5 psia (34 kPa). Such processes can be carried out at an overall conversion of linear olefins of at least 30, 35, 40, or 45 wt% or higher. The present method is particularly effective when operating at lower temperatures, e.g. less than 450°C and at relatively high WHSV, e.g. no less than 5, 10, or even 60. Under these conditions is observed a significant improvement in catalytic activity as evidenced by enhanced conversion of linear olefins when compared with methods utilizing Theta-1 materials of the prior art. Preferred feedstreams include C₄ or C₄+ hydrocarbon feedstreams. Linear olefins suited to use in the present invention may be derived from a fresh feedstream, preferably comprising n-butenes and/or n-pentenes, or from the effluent of an iso-olefin etherification reactor which employs alkanol and C₄ or C₄+ hydrocarbon feedstock. Typical hydrocarbon feedstock materials for isomerization reactions according to the present invention include olefinic streams, such as cracking process light gas containing butene isomers in mixture with substantial amounts of paraffins including n-butane and isobutane. The C₄ components usually contain a major amount of unsaturated compounds, such as 10-40% isobutene, 20-55% linear butenes, and small amounts of butadiene. Also, C₄+ heavier olefinic hydrocarbon streams may be used, e.g C₄ to C₁₀, preferably C₄ to C₆ olefinic hydrocarbon streams. The regeneration of spent zeolite catalyst used in the isomerization reaction is carried out oxidatively or hydrogenatively employing procedures known in the art. The catalyst of the present invention can be readily reactivated without significantly reducing selectivity for isobutene by exposing it to hydrogen for a suitable period, e.g. overnight. The invention will now be more particularly described with reference to the examples and the accompanying drawings, in which: Figure 1 is a transmission electron microscopy (TEM) micrograph of a microcrystalline ZSM-22 sample prepared in accordance with the procedure set out in Example 1. Figure 2 is a transmission electron microscopy (TEM) micrograph of the large crystal Theta-1 sample of Example 2. Example 1 Preparation of Microcrystalline ZSM-22 Microcrystalline ZSM-22 was prepared by charging the following to a 19 litre (5 gallon) autoclave: 48 parts deionized H₂O, 1 part Al₂(SO₄)₃ (17% Al₂O₃), 5 parts KOH (45% solution), 8.18 parts Ultrasil™ VN3 precipitated silica (North American Silica Company), 3.63 parts ethylpyridinium bromide (SWAC, 50% aqueous solution,), and 0.5 part ZSM-22 seeds (similarly prepared but on a smaller scale with colloidal silica (Q-Brand) as the silicon source). The mixture was aged with stirring at 93°C for 16 hours at 90 rpm, then crystallized at 160°C while stirring at 180 rpm for 78 hours. The composition of the reactant gel is described in molar quantities as follows: SiO₂/Al₂O₃ 73 OH⁻/SiO₂ 0.23 N/SiO₂ 0.07 H₂O/SiO₂ 23 N/Al₂O₃ 5.4 OH⁻/H₂O 0.01 The product was water washed, then calcined at 540°C, first in N₂ for three hours, then full air for another 6 hours, to decompose the organic directing agent. The calcined product was exchanged with NH₄NO₃ four times to remove the potassium. After complete exchange, the product was dried again in air for 3 hours to decompose the NH₄ leaving the acid form of the zeolite. Product properties are as follows: SiO₂/Al₂O₃ 73 BET Surface Area 230 m²/g Static adsorption: H₂O 6.6 wt% n-hexane 7.7 wt% cyclohexane 4.4 wt% Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) (see Figure 1), on a sample from a different batch made by the same procedure of this Example, indicated that the largest dimension of the product crystals was less than 0.5 micron. The product exhibited the characteristic X-ray diffraction pattern of ZSM-22. The zeolite was then blended 65 parts zeolite and 35 parts Ultrasil™ VN3 and pelleted. The pellets were sized 14/24 mesh and recalcined at 538°C in flowing air for 3 hours. Example 2 Preparation of Theta-1 (TON-C) (Comparative) Sodium aluminate (41% w/w Al₂O₃, 29.6% w/w Na₂O, 29.4% w/w H₂O (2.09 parts) and sodium hydroxide (1.00 part) were dissolved in distilled water (20.9 parts). Diethanolamine (DEA, 26.9 parts) was added and the mixture thoroughly stirred. Distilled water (52.9 parts) was added with stirring, followed by addition of colloidal silica (74.3 parts) (DuPont Ludox AS40 40% w/w SiO₂) to the mixture which was then well stirred to give a homogeneous gel. The gel was charged to a stainless steel autoclave and crystallized for 28 hours at 175°C with stirring after which the product was filtered, washed well with distilled water and dried in an oven at 120°C. The product was next refluxed with aqueous ammonium nitrate solution (10g/200 ml) (1M. 2 x 1 hr.), filtered hot, washed well with distilled water, dried in an oven at 120°C and calcined at 325°C in air for 8 hours. The zeolite was blended 65 parts zeolite and 35 part Ultrasil™ VN3 and pelleted. The pellets were sized 14/24 mesh and recalcined at 325°C in flowing air for 3 hours, packed into a silica reactor and activated overnight in air at 350°C in situ. The system was flushed through with nitrogen and the temperature was increased to 400°C under nitrogen. Scanning electron microscopy and transmission electron microscopy indicate the Theta-1 crystals have acicular lathe (needle-like) morphology with a broad distribution of crystal sizes having the largest dimension of up to 1 to 2 microns. Figure 2 is a TEM micrograph of the Theta-1 thus prepared. This catalyst was prepared in accordance with the procedure set out in European Patent Application 0 247 802 for the material designated TON-C. The resulting product was used to duplicate two runs set out in Table 7 therein, the first with pure 1-butene feed at 13 WHSV (at 100 kPa) and the second with 10% 1-butene, 90% nitrogen at 4.7 WHSV. A comparison of the results under the first set of conditions is presented below: Example 2 Catalyst TON-C NC4=Conv. (%) 58.2 53.0 IC4=Yield (%) 25.8 25.5 IC4=Sel. (%) 44.3 48.1 A comparison of the results under the second set of conditions is also set out below: Example 2 Catalyst TON-C NC4=Conv. (%) 29.4 30.6 IC4=Yield (%) 27.0 27.9 IC4=Sel. (%) 91.6 91.2 The foregoing results show that the catalyst prepared in Example 2 duplicates the performance of the TON-C catalyst. Example 3 Isomerization of 1-Butene with Microcrystalline ZSM-22 and Theta-1 at 550°C The microcrystalline ZSM-22 of Example 1 and Theta-1 of Example 2 were used in butene skeletal isomerization reactions carried out at 400°C and 550°C, and at 75 WHSV and 21 WHSV. Further process conditions and results are provided below: Run No. 1 2 3 4 WHSV (HC) 75 75 21 21 T (°C) 400 550 400 550 P (kPa) 160 160 160 160 N₂/1-C4=(v/v) 3 3 10 10 Microcrystalline ZSM-22 Conv. (%) 44.3 40.6 40.4 39.8 IC4= Yld (%) 27.1 35.8 33.6 37.6 IC4= Sel (%) 61.1 88.1 83.3 94.5 Theta-1 Conv. (%) 3.6 34.9 26.6 35.2 IC4= Yld (%) 3.2 33.0 24.1 33.3 IC4= Sel (%) 87.7 94.5 90.5 94.5 The results indicate that the microcrystalline ZSM-22 catalyst has significantly higher activity than the large crystal Theta-1 catalyst, particularly at lower temperatures (400°C) and higher WHSV. Moreover, total iso-olefin yield is consistently higher with microcrystalline ZSM-22 despite somewhat reduced selectivity at lower temperature and lower WHSV.

Claims: A process for conversion of linear olefins to corresponding iso-olefins of the same carbon number which comprises contacting a linear olefin-containing organic feedstock with a catalyst comprising ZSM-22 having a crystal size in which the largest dimension is no greater than 0.5 micron, and in which the ratio of the second largest dimension to the largest dimension ranges from 0.5 to 1. The process of claim 1 wherein said contacting is carried out at a temperature of 100 to 750°C, a weight hourly space velocity (WHSV) based on linear olefin in said feedstock of 0.1 and 500, and a linear olefin partial pressure of 2 to 2000 kPa. The process of claim 2 wherein said temperature is 200 to 600°C, said weight hourly space velocity (WHSV) is 1 to 400, and said linear olefin partial pressure is 10 to 500 kPa. The process of claim 2 wherein said temperature is 250 to 550°C, said weight hourly space velocity (WHSV) is 5 to 100, and said linear olefin partial pressure is 20 to 200 kPa. The process of any preceding claim wherein said largest dimension of said crystal size is less than 0.3 micron. The process of any preceding claim wherein said crystal size has the dimensions of 0.2 to 0.4 micron by 0.1 to 0.4 micron by ≦ 0.1 micron. The process of any preceding claim wherein said feedstock comprises C₄ to C₁₀ linear olefins. The process of any preceding claim wherein said feedstock comprises C₄ to C₆ linear olefins. The process of any preceding claim wherein the ZSM-22 has an alpha value of at least 50.

Inventors: HUSS ALBIN JR, JOHNSON IVY DAWN, KLOCKE DONALD JOSEPH, LISSY DARIA NOWAKIWSKA, RAHMIM IRAJ, HUSS, ALBIN, JR., JOHNSON, IVY DAWN, KLOCKE, DONALD JOSEPH, LISSY, DARIA NOWAKIWSKA, RAHMIM, IRAJ
Applicants: MOBIL OIL CORP, MOBIL OIL CORPORATION
Application year: 1992
Main classification: C07C11
IPC codes: C07C5, C07B61, B01J29, C07C11