Bitumens modified with recycled and/or virgin polymers and their applications

Abstract: Bitumens modified with recycled and/or virgin polymers, such as polyethylene (PE) and ethylene-vinylacetate copolymer which, having special structural and morphological characteristics, give an improved performance with respect to bitumen as such or modified with traditional polymers; the mixtures thus obtained are used for street paving or different kinds of waterproofing.

Description: The present invention relates to bitumens modified with recycled and/or virgin polymers, such as PE and ethylene-vinyl acetate copolymer which, having special structural and morphological characteristics, give a better performance compared to bitumen as such or modified with traditional polymers; the mixtures thus obtained are used for street paving or different kinds of waterproofing. It is generally known that a minimum thermal susceptibility is required in the use of bitumens; in fact the use of bitumen as such causes stiffening at low temperatures making it fragile to light impacts, whereas at temperatures higher than 30-40°C its viscosity is so low that it flows spontaneously or becomes permanently deformed even under slight mechanical stress. From the economical point of view, it should be noted that the cost of modifying polymers is by far the highest of the formulation components; the incidence of the cost of the polymer on the total mass will obviously depend on the formula used. To overcome these limits, research in the field has proposed bituminous compositions wherein a bitumen is mixed with an organic polymer, especially elastomers of the styrene-butadiene family or atactic polypropylene (PPa). In fact, Patent EP 315.239 in the name of the same Applicant, claims a bituminous composition for waterproofing sheaths composed of bitumen and virgin LLDPE (linear low density polyethylene). Also Patents GB 2.219.802 and GB 2.223.229 use virgin LDPE (low density polyethylene) in the bituminous composition; in addition, in these Patents, the Melt-Flow Index of the composition ranges from 0.2 to 2. EP Patents 205.774 and EP 205.796 claim bituminous masses composed of a bitumen, obtained with a Visbreaking process, modified with styrene-butadiene rubbers and with PE which is not better identified from a structural point of view. In a single example and single Claim it is specified that the bituminous mass contains the PE alone in a weight percentage, with respect to the total mass, of up to 12%. The addition of these polymers improves various characteristics of the bitumen, and the bituminous mixtures obtained have an interesting applicative performances but are extremely viscous in the processing phase. These compositions are coupled with lithic materials having a special morphology, for the preparation of bituminous conglomerates or, at times, with the addition of a mineral charge and combined with a reinforcement, in the form of waterproofing sheaths used in construction for floor lining. In the field of bituminous conglomerates for street paving, the applicative problem lies in the necessity of having bituminous binders which are very slightly susceptible to the effects of temperature. For this reason polymers, and particularly elastomers, are used for modifying the bitumens. FR-A-2,152,090 discloses bituminous compositions containing, in addition to bitumen, 1-8% wt.% of polyethylene and/or polypropylene. Moreover the added polyolefin, e.g. PE, may be either virgin or recycled. WO-A-87 04174 relates to a composition comprising a bituminous material and 1-50 wt.% of an olefinic polymer selected from olefin homopolymers, such as PE, and an interpolymer of an olefin and at least one comonomer, e.g. vinyl acetate. EP-A-0 299 700 relates to a composition comprising bitumen and a linear PE compound up to 25 wt.%, having the desired melt flow index and density. FR-A-2 263 103 relates to a composition comprising bitumen, an EVA copolymer and optionally a polyethylene having a density between 0.918 and 0.965 g/cm 3 . It discloses also water-proofing membranes comprising a tape from the bituminous composition reinforced by a woven or non-woven fabric associated with a lining mat. US-A-2 871 212 deals with asphalt compositions comprising a minor amount of polyethylene having a molecular weight within the range from 500 to 12000 and more specifically of from 1000 to 9000. The Applicant has recently proposed, in Application IT 19732 A/88, the use of mixtures of plastic materials deriving from solid urban residues for modifying the bitumens used in the above bituminous conglomerates which bring an improvement even in the technological performance. The use of bituminous binders with a better performance with respect to bitumen as such, is indispensable in the case of phonoabsorbing or self-draining street pavements. In the field of waterproofing and with respect to PPa, this material is capable of giving interesting characteristics to bitumen when it is used in relatively high proportions with respect to the bitumen. Unfortunately bituminous compositions with a high content of PPa do not have sufficient dimensional stability, and can therefore be easily deformed under minimum mechanical stress, under average-high temperatures and, in these conditions, the behaviour to "treading" and spontaneous slipping on an inclined plane is compromised. Attempts have been made in the art to find a solution to this draw-back by adding a fraction of isotactic polypropylene to the composition, in addition to the inorganic charges; this has reduced but not sufficiently solved the problem. Another undesired characteristic of the bitumen/PPa compositions consists in their limited resistance to aging. The necessity has consequently been felt for improving the bituminous compositions and for this purpose attempts have been made to use other polymers in substitution of both PPa and those previously mentioned in the above Patents. This necessity is more widely felt due to the diminished availability of PPa on the market in that its production ceased in all the main industrialized countries at the end of the 70's following the introduction of new catalytic systems with a high yield and stereospecificity and, in fact, the PPa which is still present on the market is that which has been recovered from deposits where it was stored in the past years. However the substitution of PPa by organic polymers which are widely available such as PE and/or its copolymers with vinyl acetate, has not been able to solve the above problems, as specified by F. Schieroni in his article "Bituminous sheaths and waterproofing of viaducts", published by the magazine "Impermeabilizzare" (Waterproofing) n.4 (1977). The reason lies in the difficulty of compatibility between the above polymers and bitumens if the former are not suitably selected in terms of molecular weight and crystallinity. In all cases, substitution with virgin polymers has not proved to be advantageous, so far, from an economical point of view, because of the high costs of these, and above all of elastomers, with respect to PPa. This approach has consequently not been significantly established so far for industrial production. To overcome the above draw-backs, the Applicant has now found that by modifying the bitumen with virgin polymers and mainly recycled polymers which have special structural and morphological characteristics, it is possible to obtain formulations which can guarantee a technological-applicative performance similar or better than with those presently being used and at a more advantageous cost due to the fact, naturally, that recycled polymers are used and also because the above polymers are virgin, which are definitely more economical compared to elastomers, for example. The present invention consequently relates to bitumens modified with recycled and/or virgin polymers, such as PE and ethylene-vinyl acetate copolymer which, having special structural and morphological characteristics, give a better performance with respect to bitumen as such or modified with traditional polymers; the mixtures thus obtained are used for street paving or different kinds of waterproofing. In accordance with this the bituminous composition of the present invention is characterized in that it contains: a) bitumen; b) a recycled polyethylene (PE), alone or in admixture with a virgin PE, having a density of from 0,870 to 0,970 g/ml and a Melt-Flow Index value of between 20 and 70; c) a recycled ethylene-vinyl acetate copolymer (EVA), alone or in admixture with a virgin EVA, having a Melt-Flow Index value of between 0,3 and 500 and a vinyl acetate content of between 1 and 50% by weight with respect to the total copolymer; and d) a PE vax having a molecular weight of between 3,000 and 6,000. According to a preferred method the composition of the present invention contains a PE having a density value ranging from 0.910 and 0.930 g/ml. The composition of the present invention may generally contain from 1 to 30 parts by weight of PE for every 100 parts by weight of bitumen. In the preferred applicative method this composition contains from 15 to 25 parts by weight of PE for every 100 parts by weight of bitumen. According to a preferred applicative method the characteristics of EVA are: Melt-Flow Index within the values 5-50 and vinyl acetate content of 20-40%. These ranges of Melt-Flow Index and vinyl acetate content may be reached by mixing different types of EVA having Melt-Flow Index values and vinyl acetate content outside the above ranges. The composition of the present invention has a ratio between EVA and total polymers, i.e. EVA + PE, ranging from 1 to 50% and preferably between 10 and 40%. If the polymers have been recycled it often happens that their Melt-Flow Index values are outside the above values or that the density is higher than the expected value; in these cases, as the characteristics are not suitable for an optimum modification of the bitumen, they should be modified by "reactive extrusion" or "reactive processing" until they correspond to the previously defined values. When waxes are used, they can be used in a percentage of between 1 and 40 by weight with respect to the total polymers, i.e. PE + EVA + waxes, and preferably between 5 and 10%. Waxes are generally used to reduce the viscosity in the processing phase, without greatly influencing the final performance of the mixture. Bitumens which are suitable for the purpose are those, of various origins, which generally have penetration values ranging from 40 to 300 mm (according to ASTM D-5) and with ball-ring values ranging from 60 to 30°C (according to ASTM D-36); the preferred bitumens are those coming from distillation (from Vacuum). The composition of the present invention may contain, in addition to the bitumen and above polymers, one or more compatibilizing agents usually selected from fillers, pigments, stabilizers and dyes. Among these it is preferable to use 3-methoxy-ethoxyethoxyethoxypropyl-tri(methoxyethoxyethoxy-ethoxy)-silane (MTG Silane), commercially produced under the trade-name HULS. The compositions of the present invention have good general characteristics, including those relating to their processability in the preparation phase and application of the products; in addition, in the waterproofing field, these compositions have much better "treading" characteristics. The basic advantages of using recycled pclymers are that they reduce the volumes of the polymers to be disposed after use, thus contributing to solving problems relating to environmental pollution, and they also improve the applicative performance of the bitumens. A further advantage derives from the fact that in the present formulations continuity in the polymeric phase is reached (inversion point of the matrix) at ratios of polymer/bitumen which are considerably lower than those obtained with the use of PPa; in this composition the ratio polymer/bitumen never exceeds 0.14 whereas in the case of PPa this value is 0.20. As a result in the present composition a typical performance of the polymers is reached using quantities which are much lower than those in the method with PPa. A third advantage lies in an improved behaviour of the composition to treading, as can be seen in Table 4 which shows data relating to mechanical deformation at high temperatures (print). It can be noted from the above table that, to obtain a valid comparison of the behaviour to temperature and charge between the present composition and the mixtures obtained with PPa, it is necessary to considerably increase the concentration of PPa with respect to the concentration of the recycled polymers. The composition is useful for lining and insulating, for example pipes and tanks even underground; this composition can be used mainly for the preparation of waterproofing sheaths, combined with a reinforcement selected from felts, fabrics and laminates of organic and/or inorganic material. The reinforcement is preferably selected from non-woven fabrics of polyester and film-glass. These sheaths have a typical thickness of about 2-8 mm and can be prepared with the usual procedures, known in the art, such as for example that described by G. Bonfiglio in the article "Manti prefabbricati e resine per le coperture" (Prefabricated coatings and resins for lining.) published by the magazine Materie Plastiche ed Elastomeri (Plastic materials and Elastomers), 38 , no.11, November 1972. The sheaths are useful for waterproofing coatings in construction and civil works in general, for example for coating and waterproofing floors, vertical walls, terraces, viaducts and tanks for collecting water. The sheaths can be surface-lined with a metallic sheet (for example of aluminium or copper) for protective and/or aesthetic purposes; in the same way a surface-lining of marble or slate grit can be applied. With respect to the characteristics of the products used, these are summarized in Table 1. The experimental examples which follow provide a better illustration of the present invention but do not limit it in any way. EXAMPLE 1 (comparative) 500 g of bitumen are placed in a 2 litre metallic container, equipped with a mechanical stirrer. The product is heated under stirring up to 180°C, whereupon 100 g of PPa are added and the stirring is continued, keeping the temperature constant, until it has completely melted and is then homogenized for 1 hour. The mixture obtained is poured into suitable containers to supply test samples upon which the characterization tests listed in Table 2 are carried out. The subsequent examples (from 2 to 20) are carried out with the same method used in Example 1; the results are shown in Table 3.

Claims: A bituminous composition consisting of: a) bitumen; b) a recycled polyethylene (PE), alone or in admixture with a virgin PE, having a density of from 0,870 to 0,970 g/ml and a Melt-Flow Index value of between 20 and 70; c) a recycled ethylene-vinyl acetate copolymer (EVA), alone or in admixture with a virgin EVA, having a Melt-Flow Index value of between 0,3 and 500 and a vinyl acetate content of between 1 and 50% by weight with respect to the total copolymer; and d) a PE wax having a molecular weight of between 3,000 and 6,000. The bituminous composition according to Claim 1, wherein PE has a density within the range of 0.910 and 0.930 g/ml. The bituminous composition according to Claim 1, wherein the composition contains from 1 to 30 parts by weight of PE for every 100 parts by weight of bitumen. The bituminous composition according to Claim 1, wherein the composition contains from 15 to 25 parts by weight of PE for every 100 parts by weight of bitumen. The bituminous composition according to Claim 1, wherein the EVA has a Melt-Flow Index of between 5 and 50 and a vinyl acetate content of between 20 and 40%. The bituminous composition according to Claim 1, wherein the composition contains from 1 to 50 parts by weight of EVA for every 100 parts by weight of the total polymers. The bituminous composition according to Claim 6, wherein the composition contains from 10 to 40 parts by weight of EVA for every 100 parts by weight of the total polymers. The bituminous composition according to Claim 1, wherein the composition contains from 1 to 40 parts by weight of PE wax for every 100 parts by weight of the total polymers. The bituminous composition according to Claim 8, wherein the composition contains from 5 to 10 parts by weight of PE wax for every 100 parts by weight of the total polymers. The bituminous composition according to Claim 1, wherein the bitumen has a penetration value of from 40 to 300 dmm according to ASTM D-5 and ball-ring value of from 60 to 30° C according to ASTM D-36. The bituminous composition according to Claim 1, wherein the bitumen is obtained by vacuum distillation. The bituminous composition according to Claim 1, further comprising one or more compatibilizing agents selected from the group consisting of fillers, pigments, stabilizers and dyes. Use of the bituminous composition according to Claims from 1 to 12 for street paving and waterproofing sheaths, wherein said composition is renforced with a member selected from the group consisting of felts, fabrics and laminates of organic and/or inorganic material. A waterproofing sheath according to Claim 13, wherein the reinforcement is non-woven fabric of polyester or a film-glass. A waterproofing sheath according to Claim 14, having a thickness of about 2-8 mm.

Inventors: BELLIO EMANUELE, FICILI MICHELE, PATTI NICOLA, BELLIO, EMANUELE, FICILI, MICHELE, PATTI, NICOLA
Applicants: POLIMERI EUROPA SRL, POLIMERI EUROPA S.R.L.
Application year: 1992
Main classification: C08L95
IPC codes: C08L23, B32B11, D06N5, C08L95