METHOD FOR BINDING TO POLYMERS

Abstract: A method of covalently binding, in aqueous solution, a compound containing at least one nucleophilic group chosen among amines, alcohols or thiols, with amines as preferred group, to an amino and/or hydroxyl group containing polymer. The method is characterized of: (A) (i) that the amine nitrogen and oxygen of the hydroxyl group of the polymer, respectively, is bound to a saturated carbon atom and that the amino groups are primary or secondary; and (ii) that the polymer exhibit a great number of groups containing alkene groups; and (B) (i) that in aqueous solution and at pH 4-8 reacting the polymer with HOX, where X is chlorine, bromine or iodine, so that the double bonds of the alkene groups are transferred to oxirane, vicinal dihalid or halohydrin; and (ii) that reacting the formed oxirane-, vicinal dihalid- or halohydrin group with said compound which exhibit at least one nucleophilic group during conditions such as the compound binds to one of the carbon atoms which is part of the oxirane-, dihalid- or halohydrin structure.

Description: Method for binding to polymers. The present invention relates to a method of covalently binding a compound containing at least one nucleophilic group to a polymer (carrier) which has a great number of amino and/or hydroxyl groups. TECHNICAL BACKGROUND The products obtained with the method can be used in different methods of separation, i.e. liquid chromatography, preferably separation of biomolecules by ion-exchange chromatography, hydrophobic interaction chromatography and affinity chromatography. The products obtained with the method may also be of importance in size-exclusion chromatography. During the past 20-30 years different bifunctional coupling reagents have been used to produce specific separation media for proteins, nucleic acids, polysaccarides and other biomolecules. By use of reagents like bisepoxides, epihalohydrins etc. bioaffine matrices showing antigen (hapten), antibody (and fragments showing antibody activity), Protein A, Protein G, IgG and lectin have been prepared. In analogy ion-exchange and metal ion adsorbents from inorganic and organic reagents has been prepared. To bind biomolecules to soluble polymers and to use such products for separation by distribution between two liquid phases is also known. Bifunctional reagents has also been used to prepare media for size-exclusion chromatography, by reaction of an organic or inorganic polymer containing hydroxyl groups and/or amino groups with a bifunctional cross-linking reagents Uke epihalohydrin, bishalohydrin and bisepoxides. By varying the degree of cross- linking matrices with different exclusion limits may be obtained. A severe disadvantage with these reagents is that the reaction is difficult to control. Matrices with bridges and branches of unknown length and amount of hydroxyl groups may be obtained. The reagents may also be inactivated at the pH used during the reaction. Matrices containing oxirane groups are moisture sensitive (hydrolysis). If they also contain hydroxyl or amino groups spontaneous cross-linking may occur during storage. In a recent patent application (US 4, 973.683) a polymer containing hydroxyl groups is first reacted with an allyl halid or ailyl glycidyl ether. The reaction is easily controlled towards expected amount of hydroxyl groups transferred to allyl ethers (example of an alkene group). In a second reaction HOX (X is equal to chlorine, bromine or iodine) is added to the allyl group giving halohydrin/oxirane groups which at suitable pH will react with adjacent hydroxyl groups in the poly¬ mer. The result is that the polymer is cross-linked in a defined way and the amount of side-reactions are minimized. In an International search report compiled by the Swedish Patent Office EP 203049 (US 4,973,683), see above, EP 87786 and US 4,094,832 have been quoted as publications which define the level of the technique and classified to be without significant importance. It has now been shown that alkene groups bound through a stable bridge (-B-) to a nitrogen atom or an oxygen atom in a polymer showing a great number of amino and/or hydroxyl groups in combination with activation of the alkene groups with HOX or X 2 can be used for coupling of different organic compounds. By choosing the right conditions cross-linking can be minimized. The amount of branches, that is hydroxyalkyl groups of varying length and cross-linking bridges will be low (nought). THE INVENTION The invention is related to a method for coupling according to the introductory part at page 1. A first characterization (A) of the invention is: (i) that the polymer used in the invention shows a great number of alcoholic hydroxyl groups and/or amino groups where oxygen and/or nitrogen bind to a saturated carbon atom, and (ii) that a great number of these hydroxyl groups and amino groups respectively are substituted with an inert and stable bridge -B- which binds directly to an alkene group. The atom of the bridge which bind to a nitrogen of the amine or an oxygen of the polymer is a saturated carbon atom. A second characterization (B) is: that in an aqueous media HOX or X 2 , X is chlorine, bromine or iodine, is added at pH conditions such as the corresponding halohydrin, oxirane or vicinal dihalid is formed (activation). A third characterization iC) is: that after the addition reaction, the thus formed groups are allowed to react with a compound showing at least one nucleophilic group (Nu), which may be chosen among thiol (-SH), amine or alcohol (-OH). Thiol comprises thiolate (-S") and that -SH binds to saturated or aromatic carbon atom. The amino group is alifatic or aromatic and may be a primary, secondary or tertiary amine. Alcohol comprises alcoholate (-O"), where the oxygen atom binds to saturated or aromatic carbon atom. Side reactions are easiest to avoid for amine (primary amine) and thiol. Solubility in water for the compound which reacts with the activated polymer is preferred. The compound which is going to be used in step (C) always contains certain properties ascribed for the polymer. Hydrophobic compounds may be used to produce a hydrophobic polymer. For example benzyl amine, aminopentan, hexyl mercaptan etc. Hydrophilic compounds can be used to hydrophilize the polymer. An example is polyethylene glycol substituted in one end with an amino group and the other end with an ether. If the compound contains charged groups or groups that easily can be transformed to such groups it will give the polymer ion- exchange properties. If the compound contains two functional groups (at least one nucleophilic group, see above) separated by an inert bridge (spacer) one of the groups can be utilized in step (C) and the other one for derivatization. If the compound contains a chelating structure the invention gives a polymer which has affinity for metal ions. Chelating structures always contain at least two hetero atoms with free electron pairs. The most common hetero atoms are N, O and S. For O and S they are preferable negatively charged. The distance between two adjacent hetero atoms should be such that 5- or 6 membered rings will be formed when they in pairs coordinate a mutual metal ion. This implies that in between two chelating hetero atoms should be two or three atoms, which often are carbon atoms (for example three saturated or two saturated and one sp 2 hybridized or one saturated and two sp 2 hybridized atoms). Also other atoms could be anticipated like phosphorous, oxygen and nitro¬ gen. Normally, a chelating compound shows one or several groups - N((CH 2 ) n Ch) 2 if necessary in combination with -N-(CH 2 ) n -Ch ' , where n and n ' is 1 or 2, and Ch and Ch' are chosen among -COO-. -PO 2 " and -OPO 3 2_ . Further examples are crown ethers. Likewise the compound can be one of the parts in a bioaffine pair such as anti- gen/hapten and antibody/antibody active fragment; Protein A,G or L and IgG or an IgG specific fragment; carbohydrate and lectin; biotin and avidin/streptavidin; enzyme and substrate/co-enzyme/inhibitor; hormone and receptor etc. This type of compounds are often biopolymers with polypeptide-/oligopeptide-, polysaccharide-/oligosaccharide- or polynucleotide-/oligonucleotide structure. The compounds may be derivatized. The polymer may be inorganic or organic (synthetic polymer or biopolymer). The hydroxyl group may directly bound to or be part of the monomer unit or indirectly via organic bridges (spacers). The same applies to amino groups which can be primary or secondary. The hydroxyl groups as well as the amino groups are preferahle bound directly to saturated carbon atoms. The most important inorganic polymer is based on silica (for example Kromasil, EKA-Nobel, Sweden). Activated silica reagents are often used for coupling to silica gels. Examples on synthetic organic polymers are polyacrylat, polymetacrylat, polyacrylamide, polymetacrylamide etc. which is O- or N-substituted with hydroxyalkylgroups (C 2 -C ) and if necessary also cross-Hnked via for example 0,0 VN, N'-alkene or O,O'-/N,N'-hydroxyalken. Other examples are polyvinyl alcohol which can be derivatized or cross-linked, hydrophilized polystyrene- or polystyrene/divinylbensen, hydrophilized trimethylolpropantrimethacrylate etc. Biopolymers have a backbone of biological origin with analogous repeating units. Generally they have a polysaccharide as basic structure. Important such biopolymers are cellulose, starch, dextran, agar (agarose) etc., which may be cross-linked or derivatized in the former described way. Commercial available biopolymers are Sephadex and Polydex (cross-linked dextran in a beaded form), Pharmacia Biotechnology Group, Sweden and Polydex Biological, Canada, respectively. Novarose and Sepharose Cl (cross-hnked agarose in a beaded form), Inovata AB, Sweden and Pharmacia Biotechnology Group, Sweden, respectively. The polymer may be soluble or insoluble in water. In many cases the polymer is originally soluble in water but after derivatization insoluble in water (i.e. Sephade ). Insoluble polymers may be of different geometrical and physical form. Examples are paper, beads, layers (if necessary on a support matrix), foam etc. To increase the available surface area towards the surrounding media the insoluble polymer generally forms a porous matrix. That the polymer contains alkene groups refers to the hydroxy or amine hydro¬ gen in the basic polymer being substituted with groups containing one or several isolated carbon-carbon double bonds which carbon atoms only bind to hydrogen, saturated or aromatic carbon atom. The preferred groups containing alkene can be denoted - B - CH = CH 2 (I) -B- is a hydrocarbon chain which is straight, branched or cyclic with 1-15 carbon atoms, preferable at the most 10 and generally below 5. The hydrocarbon chain may be substituted with one or several amino- and/or hydroxyl groups. In the chain one or several nitrogen and/or oxygen atoms may be included (part of secondary amine and ether respectively). In certain specific cases a carbon atom may be replaced by a silicon atom. In general all carbon atoms in -B- are saturated. From a synthetic point of view it is preferred that -B- is equal to methylene (-CH 2 ). Polymers containing said alkene groups have been described earlier. US-A-4, 973,683 and GB 1,511,969 (soluble polymer; allyldextran). The most appropriate production method is by reaction of a basic polymer containing a hydroxyl group or amino group (i.e. P-OH or P-NH 2 , where P is a part of the basic polymer) with a compound of the structure ? 1 - R2 (II) At the reaction L is substituted by P-O (alternatively P-NH). B is earlier said bridge. R l7 R 2 , and R 3 is chosen between hydrogen, shorter alkyl, aryl which may be substituted by shorter alkyl. L is a leaving group, in general a weak nucleophile like iodine, bromine, chlorine, p-toluene sulphonate, groups like oxirane, halohydrin and vicinal dihalid etc. Shorter alkyl refers foremost to C^-Cg alkyl and aryi refer foremost to phenyl. The groups in formula II are chosen in a way that they are compatible to each other, that is during such conditions that L is not reacting with the other groups. In general, for practical, economical and synthetic reasons R j = R 2 = R 3 = H and/ or -B- are equal to -CH 2 -. The substitution reaction normally takes place at strong alkaline pH and during such conditions that side reactions practically do not occur. The contents of alkene group (C=C) of the polymer may vary more widely and are usually determined by what is going to be coupled and the method of application or the final product. A suitable range is often 0.01-3 mmol/g dry gel (polymer). The alkene groups of the polymer are reacted through addition of HOX or X 2 (characteristicum B), whereupon formed halohydrin or vicinal dihalid react with the compound containing the nucleophilic group. If possible the reaction occur through an intermediate formation of oxirane. pH is important and varies with choice of X and nucleophilic group of the compound. At too high pH HOX dispro¬ portionate and will be consumed (side reaction). At too low pH the halogen will exist as X 2 . To summarize, pH as a rule should be 5-8 besides that the extremes in the interval should be avoided for iodine. Below pH 5 mainly X 2 is added and furthermore there is a risk for oxidation if the polymer is a polysaccharide. Preferred halogens are bromine and chlorine. After the reaction of the alkene groups with HOX or X 2 the pH is adjusted to neutral with alkali. Addition of HOX is done to permanent colour which then will disappear during neutralization. The halogen functions as an indicator. If necessary the adduct is washed before the compound containing the nucleophile is added. pH is important. If the compound contains a thiol group the reaction normally comes to an end in neutral environment with an alkaline shift (pH 6-8). As a rule amines can be used without a buffer. The pH value of the amine is normally acceptable (pH 7-11). Extreme pH values according to characteristicum C means that formed halohydrin or vicinal dihalid easily can react through oxirane with water (hydrolysis) or with adjacent hydroxyl groups (cross-Unking). Most sensitive is the reaction for X = iodine. In the pH interval 7-11 potassium iodine may in certain cases catalyse the reaction to increase the yield of the compound. • One aspect of the invention is the final product, that is the polymer containing the bound compound. This is characterized by being well defined (uniform) with reference to cross-linking and spacers (free and bound to the compound) of diffe¬ rent length are missing. Another aspect of the invention is the use of the allyl polymer for activation and coupling mentioned above. The invention is illustrated by following examples. The invention is more closely defined in enclosed claims which are part of the description. 10 Example 1. 1.5 g of dry cellulose (Munktells filter paper no. OOH Sl-80-40) was allowed to swell in 50 g 1 M sodium hydroxide for three hours in presence of 1 ml 14.3 M sodium borohydride. 3.4 ml allyl bromide was added and the reaction mixture was stirred overnight. The activated cellulose was washed with water until neu÷ 15 tral pH and carbonate buffer pH 6 was added. Saturated bromine water was added until the colour of the solution was slightly yellow. The mixture was filte¬ red on a glass filter and washed with water. To the activated cellulose 60 ml of water and 10 g of trimethyl amine was added. Reaction overnight. Elemental analysis of nitrogen resulted in 0.55 . 20 Example 2. 1.5 g of cellulose (Munktells filter paper no. OOH Sl-80-40) was activated according to example 1. To filtered and washed cellulose 60 ml of water and 0.5 g 1 M sodium hydroxide was added followed by 2 g of mercapto ethanol. Reaction 25 overnight. The amount of sulphur was 0.37 % (elemental analysis). Example 3. 1.5 g dried cross-linked dextran beads (PDX Biologicals, Toronto, Canada) were allowed to swell for two hours in 50 g 1 M NaOH in presence of 1 ml 14.3 M 30 sodium borohydrid. Then 3.4 ml allyl bromide was added and the mixture was stirred overnight. The dextran beads were washed until neutral pH and suspended in carbonate buffer pH 6.5. Saturated bromine water was added until a slight yellow colour remained. The activated beads were washed on a glass filter and suspended in 30 ml of water. 5 g of trimethyl amine was added. 35 Reaction overnight whereafter the excess of trimethyl amine was washed away and the amount of nitrogen was determined by elemental analysis. Result 2.0 % of nitrogen. Example 4. Performed according to example 3 but the allyl bromide was replaced by 4.5 g of allyl glycidyl ether. Addition of bromine water followed by mercapto ethanol gave 0.8 % of sulphur (elemental analysis). Example 5. Performed according to example 3 but trimethyl amine was replaced by mercapto ethanol. Elemental analysis resulted in 1.45 % of sulphur. Example 6. 2 gram of Kromasil™-100 A , 10 μm (EkaNobel, Surte, Sweden) was washed with acetone and dried by water suction. The silica acid was suspended in 25 ml dried toluene and 2 ml of allylchlorodimethyl silane and 1 ml of pyridine was added. The mixture was allowed to react at 50 °C overnight. After water suction and washing on a glass filter the allylated silica gel was suspended in 20 ml of water and saturated bromine water was added until the mixture was slightly yellow. The amount of bromine consumed corresponded to 250 μmol/g silica. Example 7. 100 ml of beaded agarose gel (Novarose™ SE-1200, 15-20 μm, Inovata AB, Sol- lentuna, Sweden) was suspended i 100 ml 5 M sodium hydroxide in presence of sodium borohydride and 12 g allyl bromide was added. Reaction overnight whereafter the gel was washed with water until neutral pH. To 10 ml of the activated gel an excess of trimethyl amine was added and allowed to react during stirring overnight. The amount of nitrogen was 1.98 % (determined by elemental analysis). The remaining activated gel was stored in water at neutral pH and in room temperature. During a period of six month samples were taken out and reacted with excess of trimethyl amine and the amount of nitrogen was determined by elemental analysis. The result is shown in the table below. The result shows that the decrease in activity during a six month period is negligeable. Days % N 0 1,96 38 1,87 73 1,83 138 1,80 180 1,79 Example 8. Activated agarose prepared according to example 7 was suspended in carbonate buffer of pH 8 and pH 9, respectively. Bovine serum albumin was added and allowed to react overnight. Result 0.19 % and 0.37 % nitrogen which correspond to about 1 respectively 2 mg protein /ml gel.

Claims: -| Q CLAIMS 1. A method of covalently binding, in aqoueus medium, a compound containing at least one nucleophilic group chosen among amines, alcohols or thiols with amines as the preferred group to an amino and/or hydroxyl group containing polymer which may be soluble or insoluble in water, wherein (A) (i) that the amine nitrogen and hydroxy oxygen of the polymer, respectively, binds to a saturated carbon atom and that the amino groups may be primary or secondary and (ϋ) that the polymer exhibit a great number of groups containing alkene groups, preferable -CH 2 =CH 2 each of them binding to the polymer through a stable and inert bridge (-B-), where the bridge -B- substitute a hydrogen in an amine- or hydroxy group of the polymer, and (B) (i) that in aqoueus environment and at pH 4-8 react the polymer with HOX, where X is chlorine, bromine or iodine sothat the double bonds of the alkene groups are transferred to oxirane, vicinal dihalid or halohydrin, and (ii) that reacting the formed oxirane, vicinal dihalid or halohydrin groups with said compound which contains at least one nucleophilic group during such conditions that the compound, preferable a compound with an amino group, binds to one of the carbon atoms which is included in the structure of the oxirane, dihalid or halohydrin. 2. A method according to claim 1, wherein -B- is a carbon chain which is straight, branched or cyclic with up to 15 carbon atoms, whereupon the carbon chain may be substituted with one or several amino and/or hydroxyl groups and/or interrupted by one or several nitrogen and/or oxygen atoms, whereupon at the most one oxygen and/or nitrogen atom binds to the same carbon atom of -B-. 3. A method according to any of the claims 1-2, wherein -B- contains at the most 10, preferable below 4, nitrogen or oxygen atoms. 4. A method according to any of the claims 1-3, wherein -B- is methylene (-CH 2 -). 5. A method according to any of the claims 1-4. wherein the compound is a biopolymer chosen among proteins (polypeptides), nucleic acids, oligopeptides, oligonucleotides, polysaccharides, oligosaccharides and derivatives of those where the polymeric structure is intact. 6. A method according to any of the claims 1-5, wherein the compound is one of the components in a bioaffine pair. 7. A method according to any of the claims 1-6, wherein the compound is one of the components in a bioaffine pair, such as anti-body or anti¬ body active fragment or Fc-fragment thereof, antigen or hapten, Protein A or Protein G or IgG binding fragments of those, lectin, compounds containing a carbohydrate structure, biotin or (strep)avidin. 8. A method according to any of the claims 1-6, wherein the polymer contains 0.1-3 mmol alkene group (C=C) per ml dry polymer exhibiting alkene groups.

Inventors: LINDGREN GOERAN EINAR SAMUEL, LINDGREN, GOERAN, EINAR, SAMUEL
Applicants: INOVATA AB, LINDGREN GOERAN EINAR SAMUEL
Application year: 1992
Main classification: A61K47
IPC codes: A61K47, B01J20, C08B15, C08B37, G01N33