Superconducting device having an extremely thin superconducting channel formed of oxide superconductor material and method for manufacturing the same

Abstract: A superconducting device comprising a substrate (5) having a principal surface, a superconducting source region (2) and a superconducting drain region (3) formed of an oxide superconductor on the principal surface of the substrate separated from each other, an extremely thin superconducting channel formed of the oxide superconductor between the superconducting source region and the superconducting drain region. The superconducting channel electrically connects the superconducting source region to a superconducting drain region, so that a superconducting current can flow through the superconducting channel between the superconducting source region and the superconducting drain region. The superconducting device comprises a gate electrode (4) through a gate insulator (7) on the superconducting channel for controlling the superconducting current flowing through the superconducting channel, and non-superconducting oxide layers (22,23) having a similar crystal structure to that of the oxide superconductor. The non-superconducting oxide layers (22,23) contact with at least the superconducting source region (2) and the superconducting drain region (3). In the superconducting device, the superconducting channel, the superconducting source region (2) and the superconducting drain region (3) are formed of one oxide superconductor thin film of which the center portion is c-axis oriented and both ends are a-axis oriented.

Description: Background of the Invention Field of the invention The present invention relates to a superconducting device and a method for manufacturing the same, and more specifically to a superconducting device having an extremely thin superconducting channel formed of oxide superconductor material, and a method for manufacturing the same. Description of related art Devices which utilize superconducting phenomena operate rapidly with low power consumption so that they have higher performance than conventional semiconductor devices. Particularly, by using an oxide superconducting material which has been recently advanced in study, it is possible to produce a superconducting device which operates at relatively high temperature. Josephson device is one of well-known superconducting devices. However, since Josephson device is a two-terminal device, a logic gate which utilizes Josephson devices becomes complicated. Therefore, three-terminal superconducting devices are more practical. Typical three-terminal superconducting devices include two types of super-FET (field effect transistor). The first type of the super-FET includes a semiconductor channel, and a superconductor source electrode and a superconductor drain electrode which are formed closely to each other on both side of the semiconductor channel. A portion of the semiconductor layer between the superconductor source electrode and the superconductor drain electrode has a greatly recessed or undercut rear surface so as to have a reduced thickness. In addition, a gate electrode is formed through a gate insulating layer on the portion of the recessed or undercut rear surface of the semiconductor layer between the superconductor source electrode and the superconductor drain electrode. A superconducting current flows through the semiconductor layer (channel) between the superconductor source electrode and the superconductor drain electrode due to a superconducting proximity effect, and is controlled by an applied gate voltage. This type of the super-FET operates at a higher speed with a low power consumption. The second type of the super-FET includes a channel of a superconductor formed between a source electrode and a drain electrode, so that a current flowing through the superconducting channel is controlled by a voltage applied to a gate formed above the superconducting channel. Both of the super-FETs mentioned above are voltage controlled devices which are capable of isolating output signal from input one and of having a well defined gain. However, since the first type of the super-FET utilizes the superconducting proximity effect, the superconductor source electrode and the superconductor drain electrode have to be positioned within a distance of a few times the coherence length of the superconductor materials of the superconductor source electrode and the superconductor drain electrode. In particular, since an oxide superconductor has a short coherence length, a distance between the superconductor source electrode and the superconductor drain electrode has to be made less than about a few ten nanometers, if the superconductor source electrode and the superconductor drain electrode are formed of the oxide superconductor material. However, it is very difficult to conduct a fine processing such as a fine pattern etching, so as to satisfy the very short separation distance mentioned above. On the other hand, the super-FET having the superconducting channel has a large current capability, and the fine processing which is required to product the first type of the super-FET is not needed to product this type of super-FET. In order to obtain a complete ON/OFF operation, both of the superconducting channel and the gate insulating layer should have an extremely thin thickness. For example, the superconducting channel formed of an oxide superconductor material should have a thickness of less than five nanometers and the gate insulating layer should have a thickness more than ten nanometers which is sufficient to prevent a tunnel current. In the super-FET, since the extremely thin superconducting channel is connected to the relatively thick superconducting source region and the superconducting drain region at their lower portions, the superconducting current flows substantially horizontally through the superconducting channel and substantially vertically in the superconducting source region and the superconducting drain region. Since the oxide superconductor has the largest critical current density J c in the direction perpendicular to c -axes of its crystal lattices, the superconducting channel is preferably formed of a c -axis oriented oxide superconductor thin film and the superconducting source region and the superconducting drain region are preferably formed of a -axis oriented oxide superconductor thin films. In a prior art, such as described in the document EP-A-0 478 465 falling within the terms of Article 54(3) EPC, in order to manufacture the super-FET which has the superconducting channel of c -axis oriented oxide superconductor thin film and the superconducting source region and the superconducting drain region of a -axis oriented oxide superconductor thin films, a c -axis oriented oxide superconductor thin film is formed at first and the c -axis oriented oxide superconductor thin film is etched and removed excluding a portion which will be the superconducting channel. Then, an a -axis oriented oxide superconductor thin film is deposited so as to form the superconducting source region and the superconducting drain region. In another prior art, such as described in the document EP-A-0 480 814 falling within the terms of Article 54(3) EPC, at first an a -axis oriented oxide superconductor thin film is deposited and etched so as to form the superconducting source region and the superconducting drain region, and then a c -axis oriented oxide superconductor thin film is deposited so as to form the superconducting channel. Moreover, the document EP-A-0 502 787 falling within the terms of Article 54(3) EPC discloses a technique of simultaneously forming a-axis oriented and c-axis oriented regions in one oxide superconductor thin film. However, in the prior art, the oxide superconductor thin film is degraded during the etching so that the superconducting characteristics is affected. In addition, the etched surface of the oxide superconductor thin film is roughened, therefore, if another oxide superconductor thin film is formed so as to contact the rough surface, an undesirable Josephson junction or resistance is generated at the interface. By this, the super-FET manufactured by the above conventional process does not have an enough performance. Summary of the Invention Accordingly, it is an object of the present invention to provide an FET type superconducting device having a superconducting region constituted of an extremely thin oxide superconductor film, which have overcome the above mentioned defects of the conventional ones. Another object of the present invention is to provide a method for manufacturing an FET type superconducting device which have overcome the above mentioned defects of the conventional ones. The above and other objects of the present invention are achieved in accordance with the present invention by a superconducting device in accordance with claim 1 comprising a substrate having a principal surface; a non-superconducting oxide layer having a crystal structure similar to that of an oxide superconductor on the principal surface of the substrate ; a superconducting source region and a superconducting drain region formed of an oxide superconductor on the non-superconducting oxide layer separated from each other; an extremely thin superconducting channel formed of the oxide superconductor between the superconducting source region and the superconducting drain region , which electrically connects the superconducting source region and a superconducting drain region, so that a superconducting current can flow through the superconducting channel between the superconducting source region and the superconducting drain region ; and a gate electrode above a gate insulator on the superconducting channel for controlling the superconducting current flowing through the superconducting channel, the device further comprising at least one non-superconducting oxide layer having a similar crystal structure to that of an oxide superconductor on the principal surface of the substrate , which contact with at least the superconducting source region and the superconducting drain region; in said device the superconducting channel , the superconducting source region and the superconducting drain region are simultaneously formed of one oxide superconductor thin film of which the center portion is c -axis oriented and the both ends are a -axis oriented. Dependent claims 2 to 11 describe particular embodiments of the superconductive device according to the present invention. In the superconducting device in accordance with the present invention, the superconducting channel, the superconducting source region and the superconducting drain region are formed of one oxide superconductor thin film of which the center portion is c -axis oriented and the both ends are a -axis oriented and in which there is no grain boundary. Therefore, there is no undesirable resistance nor undesirable Josephson junction between the superconducting channel and the superconducting source region and between the superconducting channel and the superconducting drain region so that the current capability of the super-FET can be improved. The superconducting device in accordance with the present invention may comprise two non-superconducting oxide layers having a similar crystal structure to that of the a -axis oriented oxide superconductor thin film, which contact with the outside surfaces of the superconducting source region and the superconducting drain region. The superconducting device preferably includes a non-superconducting oxide layer having a similar crystal structure to that of the c -axis oriented oxide superconductor thin film under the superconducting channel, the superconducting source region and the superconducting drain region. Of course, the superconducting device may include two non-superconducting oxide layers having a similar crystal structure to that of the a -axis oriented oxide superconductor thin film on the both ends of the non-superconducting oxide layer, which contact with the outside surfaces of the superconducting source region and the superconducting drain region. In one preferred embodiment, the non-superconducting oxide layer includes a hollow at the center portion on which the superconducting channel is positioned. Preferably, the above non-superconducting oxide layers is formed of a Pr 1 Ba 2 Cu 3 O 7-ε oxide. The c -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε thin film has an almost same crystal lattice structure as that of a c -axis oriented oxide superconductor thin film and the a -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε thin film has an almost same crystal lattice structure as that of an a -axis oriented oxide superconductor thin film. In a preferred embodiment, the oxide superconductor is formed of high-T c (high critical temperature) oxide superconductor, particularly, formed of a high-T c copper-oxide type compound oxide superconductor for example a Y-Ba-Cu-O compound oxide superconductor material, a Bi-Sr-Ca-Cu-O compound oxide superconductor material, and a Tl-Ba-Ca-Cu-O compound oxide superconductor material. In addition, the substrate can be formed of an insulating substrate, preferably an oxide single crystalline substrate such as MgO, SrTiO 3 , CdNdAlO 4 , etc. These substrate materials are very effective in forming or growing a crystalline film having a high degree of crystalline orientation. However, the superconducting device can be formed on a semiconductor substrate if an appropriate buffer layer is deposited thereon. For example, the buffer layer on the semiconductor substrate can be formed of a double-layer coating of a MgAlO 4 layer and a BaTiO 3 layer if silicon is used as a substrate. Preferably, the superconducting channel is formed of a c -axis oriented oxide superconductor thin film and the superconducting source electrode and the superconducting drain electrode are formed of a -axis oriented oxide superconductor thin films. According to another aspect of the present invention, there is provided a method of manufacturing a superconducting device in accordance with claim 12, comprising the steps of forming on a principal surface of a substrate a non-superconducting oxide layer having a similar crystal structure to that of an a -axis oriented oxide superconductor thin film, selectively etching a center portion of the non-superconducting oxide layer so that the portion is completely removed and the surface of the substrate is exposed and the non-superconducting oxide layer is divided into two portions separated from each other, forming an oxide superconductor thin film over the exposed surface of the substrate and the two separated portions of the non-superconducting oxide layer so that the portion of the oxide superconductor thin film on the exposed surface of the substrate becomes c -axis oriented and the portions of the oxide superconductor thin film on and near the separated portions of the non-superconducting oxide layer are a -axis oriented, etching back the oxide superconductor thin film and the separated portions of the non-superconducting oxide layer so that the portions of the oxide superconductor thin film on the separated portions of the non-superconducting oxide layer are completely removed and a superconducting channel , a superconducting source region and a superconducting drain region having the same thickness as that of the separated portions of the non-superconducting oxide layer are formed between the separated portions of the non-superconducting oxide layer, and forming a gate insulator and a gate electrode stacked on the gate insulator on a center portion of the superconducting channel. According to still another aspect of the present invention, there is provided a method of manufacturing a superconducting device in accordance with claim 14, comprising the steps of forming on a principal surface of a substrate a non-superconducting oxide layer having a similar crystal structure to that of a c -axis oriented oxide superconductor thin film, forming an a -axis oriented oxide superconductor thin film on the non-superconducting oxide layer, selectively etching a center portion of the a -axis oriented oxide superconductor thin film and the non-superconducting oxide layer so that the portion of the a -axis oriented oxide superconductor thin film is completely removed and a hollow is formed at the portion, forming an oxide superconductor thin film over the a -axis oriented oxide superconductor thin film and the hollow portion of the non-superconducting oxide layer so that the portion of the oxide superconductor thin film on the hollow portion becomes c -axis oriented so as to constitute a superconducting channel and the portions of the oxide superconductor thin film on the a -axis oriented oxide superconductor thin film are a -axis oriented so as to constitute a superconducting source region and a superconducting drain region , and forming a gate insulator and a gate electrode stacked on the gate insulator on a center portion of the superconducting channel. In the above methods, metal electrodes can be formed on the superconducting source region and the superconducting drain region, if necessary. According to the method in accordance with the present invention, the superconducting channel, the superconducting source electrode and the superconducting drain electrode are formed simultaneously of one oxide superconductor thin film which has a c -axis oriented portion and two a -axis oriented portions. Since the c -axis oriented portion and two a -axis oriented portions grows simultaneously, no grain boundary is formed at the interfaces so that the crystal structure is continuous. Therefore, no undesirable resistance and no undesirable Josephson junction is formed inside the oxide superconductor thin film. The above and other objects, features and advantages of the present invention will be apparent from the following description of preferred embodiments of the invention with reference to the accompanying drawings. Brief Description of the Drawings Figures 1A to 1F are diagrammatic sectional views for illustrating a first embodiment of the process in accordance with the present invention for manufacturing the super-FET; and Figures 2A to 2F are diagrammatic sectional views for illustrating a second embodiment of the process in accordance with the present invention for manufacturing the super-FET. Description of the Preferred embodiments Referring to Figures 1A to 1F, the process in accordance with the present invention for manufacturing the super-FET will be described. As shown in Figure 1A, a MgO (100) single crystalline substrate 5 having a substantially planar principal surface ((100) surface) is prepared. As shown in Figure 1B, a c -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 20 having a thickness on the order of about 50 nanometers and an a -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 21 having a thickness on the order of about 300 nanometers are deposited and stacked on a principal surface of a MgO (100) single crystalline substrate 5 by for example a sputtering, an MBE (molecular beam epitaxy), a vacuum evaporation, a CVD, etc. A condition of forming the c -axis oriented Pr 1 Ba 2 Cu 3 O 7- oxide layer 20 by off-axis sputtering is as follows: Temperature of the substrate 750 °C Sputtering Gas Ar: 90% O 2 : 10% Pressure 10 Pa A condition of forming the a -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 21 by off-axis sputtering is as follows: Temperature of the substrate 680°C Sputtering Gas Ar: 90% O 2 : 10% Pressure 10 Pa Then, a center portion of the Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 21 is selectively etched by a reactive ion etching process using a chloric gas, an ion milling using Ar-ions or a focused ion beam etching, so that the portion is completely removed and two oxide layers 22 and 23 are formed separately on the substrate 5, as shown in Figure 1C. The c -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 20 is exposed at the center portion. Thereafter, the substrate 5 is heated to a temperature of 350 to 400 °C under a pressure lower than 1.333 × 10 -7 Pa (1 × 10 -9 Torr) for 5 minutes so as to clean the exposed portion of the c -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 20. As shown in Figure 1D, a Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 1 having a thickness of 300 nanometers is deposited over the c -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 20 and the oxide layers 22 and 23, by an off-axis sputtering. A condition of forming the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 1 is established so that a c -axis oriented Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 1 grows on the MgO substrate 5. A condition of forming the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 1 is by off-axis sputtering is as follows: Temperature of the substrate 700 °C Sputtering Gas Ar: 90% O 2 : 10% Pressure 10 Pa Portions 32 and 33 of the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 1 on and near the a -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε oxide layers 22 and 23 become a -axis oriented, since the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film grows epitaxially to the a -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε oxide layers 22 and 23 at these portions. The rest portion of the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 1 becomes c -axis oriented, since Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film grows epitaxially to the c -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 20 at this portion. The Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 1 has a continuous crystal structure so that there is no grain boundary. Then, the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 1 is etched back by a reactive ion etching process using a chloric gas, an ion milling using Ar-ions or a focused ion beam etching, so that the portions of the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 1 on the oxide layers 22 and 23 are removed and the center portion of the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 1 become a superconducting channel 10 which has a determined thickness, as shown in Figure 1E. A superconducting source region 2 and a superconducting drain region 3 are formed of continuous a -axis oriented Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film portions at the both side of the superconducting channel 10. Finally, as shown in Figure 1F, a gate insulating layer 7 and a gate electrode 4 are formed on the superconducting channel 10 and a source electrode 12 and a drain electrode 13 are formed on the superconducting source region 2 and a superconducting drain region 3. In this connection, portions of the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 1 on the oxide layer 22 and 23 are removed when the gate electrode 4 is patterned. With this, the super-FET in accordance with the present invention is completed. The gate insulating layer 7 is preferably formed of MgO, silicon nitride or SrTiO 3 and the gate electrode 4 is preferably formed of a noble metal such as Au or Pt. The above mentioned super-FET manufactured in accordance with the first embodiment of the method of the present invention has a superconducting channel, a superconducting source region and a superconducting drain region which are formed of a Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film of which the center portion is c -axis oriented and the both ends are a -axis oriented. Therefore, there is no undesirable resistance nor undesirable Josephson junction between the superconducting channel and the superconducting source region and between the superconducting channel and the superconducting drain region. In addition, since the superconducting source region and the superconducting drain region have almost the same thickness as that of the superconducting channel, superconducting current efficiently flows into and flows from the superconducting channel. By this, the current capability of the super-FET can be improved. Embodiment 2 Referring to Figures 2A to 2F, a second embodiment of the process for manufacturing the superconducting device will be described. As shown in Figure 2A, an MgO (100) substrate 5 similar to that of Embodiment 1 was prepared. As shown in Figure 2B, a c -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 20 having a thickness on the order of about 300 nanometers is deposited on a principal surface of a MgO (100) single crystalline substrate 5 by for example a sputtering, an MBE (molecular beam epitaxy), a vacuum evaporation, a CVD, etc. A condition of forming the c -axis oriented Pr 1 Ba 2 Cu 3 O 7- oxide layer 20 by off-axis sputtering is as follows: Temperature of the substrate 750 °C Sputtering Gas Ar: 90% O 2 : 10% Pressure 10 Pa Then, as shown in Figure 2C, an a -axis oriented Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 11 having a thickness of 100 nanometers is formed on the Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 20 by an off-axis sputtering. A condition of forming the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 11 by off-axis sputtering is as follows: Temperature of the substrate 640 °C Sputtering Gas Ar: 90% O 2 : 10% Pressure 10 Pa It is preferable that the a -axis oriented Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 11 is formed successively after the Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 20 is formed and the temperature of the substrate 5 is lowered. Thereafter, as shown in Figure 2D, a portion of the a -axis oriented Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 11 at which a superconducting channel will be positioned is selectively etched by a reactive ion etching process using a chloric gas, an ion milling using Ar-ions or a focused ion beam etching, so that the portion is completely removed and the Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 20 is also etched so as to form a hollow 24 having a depth of 200 nanometers. As shown in Figure 2E, a Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film having a thickness of 300 nanometers is deposited over the a -axis oriented Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film 11 and the hollow portion 21 of Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 20. A condition of forming the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film is established so that a c -axis oriented Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film grows on an ordinary substrate. A condition of forming the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film by off-axis sputtering is as follows: Temperature of the substrate 700 °C Sputtering Gas Ar: 90% O 2 : 10% Pressure 10 Pa Portions of the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film on the a -axis oriented Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin films 11 become a -axis oriented so as to constitute a superconducting source region 2 and a superconducting drain region 3, since the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film grows epitaxially to the a -axis oriented Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin films 11 at the portions. The rest portion of the Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film becomes c -axis oriented so as to constitute a superconducting channel 10, since Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film grows epitaxially to the c -axis oriented Pr 1 Ba 2 Cu 3 O 7-ε oxide layer 20 at the portion. The Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film has a continuous crystal structure so that there is no grain boundary. Finally, as shown in Figure 2F, a gate insulating layer 7 of MgO, silicon nitride or SrTiO 3 and a gate electrode 4 are formed on the superconducting channel 10 and a source electrode 12 and a drain electrode 13 are formed on the superconducting source region 2 and a superconducting drain region 3. With this, the super-FET in accordance with the present invention is completed. The above mentioned super-FET manufactured in accordance with the second embodiment of the method of the present invention has a superconducting channel, a superconducting source region and a superconducting drain region which are formed of a Y 1 Ba 2 Cu 3 O 7-δ oxide superconductor thin film of which the center portion is c -axis oriented and the both ends are a -axis oriented. Therefore, there is no undesirable resistance nor undesirable Josephson junction between the superconducting channel and the superconducting source region and between the superconducting channel and the superconducting drain region. In the above mentioned embodiments, the oxide superconductor thin film can be formed of not only the Y-Ba-Cu-O compound oxide superconductor material, but also a high-T c (high critical temperature) oxide superconductor material, particularly a high-T c copper-oxide type compound oxide superconductor material, for example a Bi-Sr-Ca-Cu-O compound oxide superconductor material, and a Tl-Ba-Ca-Cu-O compound oxide superconductor material. The invention has thus been shown and described with reference to the specific embodiments. However, it should be noted that the present invention is in no way limited to the details of the illustrated structures but converts and modifications may be made within the scope of the appended claims.

Claims: A superconducting device comprising a substrate (5) having a principal surface; a non-superconducting oxide layer (20) having a crystal structure similar to that of an oxide superconductor on the principal surface of the substrate (5); a superconducting source region (2) and a superconducting drain region (3) formed of an oxide superconductor on the non-superconducting oxide layer (20) separated from each other; an extremely thin superconducting channel (10) formed of the oxide superconductor between the superconducting source region (2) and the superconducting drain region (3), which electrically connects the superconducting source region (2) and a superconducting drain region (3), so that a superconducting current can flow through the superconducting channel (10) between the superconducting source region (2) and the superconducting drain region (3); and a gate electrode (4) above a gate insulator (7) on the superconducting channel (10) for controlling the superconducting current flowing through the superconducting channel(10), the device further comprising at least one non-superconducting oxide layer (20, 22, 23) having a similar crystal structure to that of an oxide superconductor on the principal surface of the substrate (5), which contact with at least the superconducting source region (2) and the superconducting drain region (3); in said device the superconducting channel (10), the superconducting source region (2) and the superconducting drain region (3) being simultaneously formed of one oxide superconductor thin film of which the center portion is c -axis oriented and the both ends are a -axis oriented. A superconducting device as claimed in Claim 1, characterized in that the superconducting device comprises two non-superconducting oxide layers (22, 23) having a similar crystal structure to that of an a -axis oriented oxide superconductor thin film, which contact with side surfaces of the superconducting source region (2) and the superconducting drain region (3) opposite to the superconducting channel (10). A superconducting device as claimed in Claim 1 or 2, characterized in that the superconducting device comprises a non-superconducting oxide layer (20) having a similar crystal structure to that of a c -axis oriented oxide superconductor thin film on the principal surface of the substrate (5) and the superconducting channel (10), the superconducting source region (2) and the superconducting drain region (3) are disposed on the non-superconducting oxide layer (20). A superconducting device as claimed in anyone of Claims 1 to 3, characterized in that the superconducting device comprises a non-superconducting oxide layer (20) having a similar crystal structure to that of a c -axis oriented oxide superconductor thin film on the principal surface of the substrate (5), and two non-superconducting oxide layers (22, 23) having a similar crystal structure to that of the a -axis oriented oxide superconductor thin film on the non-superconducting oxide layer (20) separated from each other, which contact with side surfaces of the superconducting source region (2) and the superconducting drain region (3) opposite to the superconducting channel (10). A superconducting device as claimed in anyone of Claims 1 to 3, characterized in that the non-superconducting oxide layer (20) includes a hollow (24) at the center portion in which an oxide superconductor thin film constituting the superconducting channel (10) is positioned. A superconducting device as claimed in anyone of Claims 1 to 5, characterized in that the non-superconducting oxide layer (20, 22, 23) is formed of a Pr 1 Ba 2 Cu 3 O 7-ε thin film. A superconducting device as claimed in anyone of Claims 1 to 6, characterized in that the oxide superconductor is formed of high-T c (high critical temperature) oxide superconductor. A superconducting device as claimed in Claim 7, characterized in that the oxide superconductor is formed of a high-T c copper-oxide type compound oxide superconductor. A superconducting device as claimed in Claim 8, characterized in that the oxide superconductor is formed of oxide superconductor material selected from the group consisting of a Y-Ba-Cu-O compound oxide superconductor material, a Bi-Sr-Ca-Cu-O compound oxide superconductor material, and a Tl-Ba-Ca-Cu-O compound oxide superconductor material. A superconducting device as claimed in anyone of Claims 1 to 9, characterized in that the substrate (5) is formed of a material selected from the group consisting of a MgO (100) substrate, a SrTiO 3 (100) substrate and a CdNdAlO 4 (001) substrate, and a semiconductor substrate. A superconducting device as claimed in Claim 10, characterized in that the substrate (5) is formed of a silicon substrate and a principal surface of the silicon substrate is coated with an insulating material layer which is formed of a MgAl 2 O 4 layer and a BaTiO 3 layer. A method of manufacturing a superconducting device, comprising the steps of forming on a principal surface of a substrate (5) a non-superconducting oxide layer (21) having a similar crystal structure to that of an a -axis oriented oxide superconductor thin film, selectively etching a center portion of the non-superconducting oxide layer so that the portion is completely removed and the surface of the substrate is exposed and the non-superconducting oxide layer is divided into two portions (22, 23) separated from each other, forming an oxide superconductor thin film (1) over the exposed surface of the substrate (5) and the two separated portions (22, 23) of the non-superconducting oxide layer so that the portion of the oxide superconductor thin film on the exposed surface of the substrate becomes c -axis oriented and the portions (32, 33) of the oxide superconductor thin film on and near the separated portions (22, 23) of the non-superconducting oxide layer are a -axis oriented, etching back the oxide superconductor thin film (1) and the separated portions (22, 23) of the non-superconducting oxide layer so that the portions of the oxide superconductor thin film on the separated portions (22, 23) of the non-superconducting oxide layer are completely removed and a superconducting channel (10), a superconducting source region (2) and a superconducting drain region (3) having the same thickness as that of the separated portions (22, 23) of the non-superconducting oxide layer are formed between the separated portions (22, 23) of the non-superconducting oxide layer, and forming a gate insulator (7) and a gate electrode (4) stacked on the gate insulator (7) on a center portion of the superconducting channel (10). A method as claimed in Claim 12 characterized in that the substrate (5) includes an oxide layer (20) having a similar crystal structure to that of a c -axis oriented oxide superconductor thin film and forming said principal surface of the substrate (5). A method for manufacturing a superconducting device, comprising the steps of forming on a principal surface of a substrate (5) a non-superconducting oxide layer (20) having a similar crystal structure to that of a c -axis oriented oxide superconductor thin film, forming an a -axis oriented oxide superconductor thin film (11) on the non-superconducting oxide layer, selectively etching a center portion of the a -axis oriented oxide superconductor thin film (11) and the non-superconducting oxide layer (20) so that the portion of the a -axis oriented oxide superconductor thin film is completely removed and a hollow (24) is formed at the portion, forming an oxide superconductor thin film over the a -axis oriented oxide superconductor thin film (11) and the hollow portion (24) of the non-superconducting oxide layer so that the portion of the oxide superconductor thin film on the hollow portion becomes c -axis oriented so as to constitute a superconducting channel (10) and the portions of the oxide superconductor thin film on the a -axis oriented oxide superconductor thin film are a -axis oriented so as to constitute a superconducting source region (2) and a superconducting drain region (3), and forming a gate insulator (7) and a gate electrode (4) stacked on the gate insulator (7) on a center portion of the superconducting channel (10).

Inventors: IIYAMA MICHITOMO, INADA HIROSHI, NAKAMURA TAKAO, IIYAMA, MICHITOMO, INADA, HIROSHI, NAKAMURA, TAKAO
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1992
Main classification: H01L39
IPC codes: H01L39