Device for testing the handling properties of powders

Abstract: It is known that the properties of powders affect the ease or difficulty of handling in many industrial processes. In may cases, the only way to test the suitability of a particular powder for a given system is to pass a sample of that powder through the system. This involves using a large quantity of the material with the uncertainty that the properties of the material are in fact suitable for that system. Described herein is a test device which allows certain properties of a material in powder form to be determined without the need for large quantities of material. The device (10) comprises a frame (12, 14, 16, 18, 20) in which is mounted a curved test surface (26). An aperture (22) is provided in a top member (14) of the frame (12) to allow the material being tested to fall on to the test surface (26) to form a 'footprint'. The 'footprint' can then be measured to provide an indication of the properties of the material prior to it being introduced into a system in bulk.

Description: This invention relates to testing devices and is more particularly concerned with testing devices for testing the physical properties of powders. Many industrial processes require the conveying, delivering, pouring and dispensing of bulk powders. A number of properties of the powder affect its ease or difficulty of handling and may include electrostatic charge, specific gravity, particle size, particle shape and particle size and shape distributions. Other factors which may affect the handling properties of the powder are the presence of residual amounts of synthetic precursors, particularly solvents, the hygroscopicity of the powder and its degree of aggregation. While it may be theoretically possible to measure all of the parameters quantitatively and then predict how the powder would handle, this rarely happens. In practice, a powder is matched with an appropriate piece of handling equipment using the long and short term experience of the designers of that particular system. It is quite likely that new powder types or batches could be put into an existing system and new or unexpected problems would occur. A powder can form 'bridges' and 'rat holes' in delivery hoppers, build up on sloping surfaces to form unacceptable mounds, stick to walls and billow in clouds into the working environment. All these problems are related in some way to the physical properties mentioned above. As the properties of a powder are so difficult to quantify, it is probable that the only way to check if a new powder type or batch will handle satisfactorily in an existing system is to try it out in that system. This means that a significant quantity of the material, commonly several kilograms, is required with the doubt that the material may not be acceptable and therefore have to be rejected. When it is intended to produce an improvement in the synthesis of preparation of a powder, it is commonly more convenient, and much less expensive, to produce initially just a few grams which can be tested for its handling properties. GB-B-2 060 902 discloses an arrangement and method for measuring the flowability of powders. The arrangement comprises a cylinder into which the powder to be tested is loaded (called the fill), and a series of disks each having a different sized hole drilled therein, the disks being attached to the undersurface of the cylinder and through which the powder is caused to pass. The arrangement operates on the principle that a free flowing powder slowly flows even through small holes until an inverted cone is formed in the whole thickness of the fill while a powder which flocculates into a mass falls as a lump leaving a cylindrical cavity in the fill. A positive result is obtained if the flow of powder begins within 60s and continues until a cavity of conical or cylindrical shape is formed in the whole thickness of the fill. If the test is positive, a smaller-sized hole will be used. Similarly, if the test is negative, a larger-sized hole is used. The method described in GB-B-2 060 902 is time dependent, each run lasting at least 60s, and is repetitive regardless of whether a positive result is obtained during the first run. This method still needs a significant amount of powder and may still not predict how the powder falls past or builds up on a given surface. US-A-3 940 997 discloses a device for measuring the angle of repose of granular material. The device comprises a rectangular body having an open-ended partition located therein for dividing the body into an upper and a lower cell. The partition provides a passage for the granular material to pass from the upper cell to the lower one under the influence of gravity. One of the sides of the body is transparent and has indicator marks formed thereon to aid the measurement of the angle of repose in the upper cell near the open end of the partition. A slidably mounted indicator marker is also provided in the lower cell for measuring the angle of repose. In one embodiment of the device, suitable closures are provided for the top and bottom of the body so that, for a given sample of granular material, the tests can easily be repeated without having to remove the material from, and re-introduce it into, the device. It is therefore an object of the present invention to provide a simpler arrangement in which the properties of small quantities of powder may be tested very simply and non-destructively, in order to predict how the powder will handle in large quantities throughout a piece of equipment. In accordance with one aspect of the present invention, there is provided a testing device for testing the handling properties of a sample of a powder, the device comprising:- a frame comprising at least a substantially vertical member and a substantially horizontal member, the vertical member and the horizontal member being positioned to be substantially orthogonal to one another; a continuous test surface mounted between the vertical member and the horizontal member, an upper portion thereof being located at a first position on the vertical member and in contact therewith and a lower portion thereof located at a second position on the horizontal member and in contact therewith; and aperture defining means located on the vertical member for allowing a sample of powder to be introduced into the device under predetermined conditions and to be incident on the upper portion of the test surface; characterized in that the test surface comprises a substantially curved surface portion intermediate the upper portion and the lower portion. For a better understanding of the present invention, reference will now be made, by way of example only, to the accompanying drawings in which:- Figure 1 is a perspective view of a testing device constructed in accordance with the present invention; Figure 2 is a plan view of a test surface used in the device shown in Figure 1; Figure 3 is a graph showing the calibration of the test surface in terms of grid lines and slope angle; Figure 4 is a graph illustrating a relationship between the highest distance of continuous powder up the test surface and the bulk density of the material being tested; and Figure 5 is a graph illustrating a relationship between the number of aggregated particles falling beyond the test surface and subjective appearance/handling. In Figure 1, a device 10 in accordance with the present invention is illustrated. The device comprises a frame 12 in the form of an open-sided cuboid which includes a horizontal top member 14, a horizontal bottom member 16, and a pair of opposed vertical end members 18, 20. An aperture 22 is formed in the top member 14 adjacent end member 20 and through which the material to be tested is introduced into the device 10. A viewing aperture 24 is also provided in the top member 14. A test surface 26 is positioned within the frame 12 as shown so that one portion 28 lies against the vertical end member 20, another portion 30 lies along the horizontal bottom member 16 and a portion 32 between portions 28, 30 forming a curved surface connecting them. A pair of pegs 34, 36 are attached to the bottom member 16 to provide a stop for the free end of portion 30, and to retain the test surface 26 in the correct position. The test surface 26 may be made of any suitable flexible material, for example, card, polished aluminium plate, brushed aluminium plate, polyethylene teraphthalate, and gelatin-coated polyethylene teraphthalate. In Figure 2, the test surface 26 is shown in plan view. The surface 26 is shown in its position relative to the bottom member 16 and pegs 34, 36. A grid 38 is marked on to the surface 26 so that quantitative information relating to the powder(s) being tested can be derived. The grid shown in this case comprises a series of lines 1cm apart and which run in mutually perpendicular directions extending along and across the test surface 26 to form a series of squares having sides of 1cm. Two further test areas 40, 42 are preferably defined by the bottom member 16 as shown. In operation, powder to be tested is introduced into the device 10 through the aperture 22. This provides a reference point from which the powder can be introduced into the device, the point being at a fixed height and position above the test surface 26. The powder then falls on to the test surface 26 and forms a 'footprint' 44 on the grid 38. One possible 'footprint' is shown in Figure 2. From the grid 38, the following information can be determined (all distances being given in cm):- 1) L 1 is the highest distance of continuous powder up the test surface; 2) L 2 is the lowest distance of continuous powder down the test surface; 3) W 1 is the maximum width of continuous powder; 4) W 2 is the widest spread of powder particles on the test surface (neglecting one or two outlying particles); 5) N 1 is the number of (usually) aggregated particles in area 40; and 6) N 2 is the number of (usually) aggregated particles in area 42. It has been found by experiment that the size and shape of the resulting 'footprint' of powder is very reproducible. Using a powder comprising α-[4-(4-benzyloxyphenylsulphonyl)-phenoxy]-α-(pivalyl)-2-chloro-5-[γ(2,4-ditertamylphenoxy)butyramido]acetanilide and a test surface made of card, the results shown in Table 1 were obtained. RUN POUR RATE L 1 L 2 W 1 N 1 +N 2 1 medium 8.1 3.3 3.0 2 2 fast 8.2 3.3 2.8 1 3 slow 8.0 2.9 3.1 0 4 medium 8.0 3.0 3.3 1 5 medium 8.2 3.1 2.9 2 The mean and standard deviations for L 1 , L 2 and W 1 are 8.1 & 0.10, 3.1 & 0.18, and 3.0 & 0.19 respectively. It is also clear that the rate of pouring of the powder through the aperture has little, if any, effect on the dimensions of the 'footprint'. It was also found by experiment that the properties of the test surface only has a modest effect on the shape of the 'footprint'. Table 2 illustrates the results for three different powders on the four different test surfaces, the same test surfaces being used for each of the three powders. Other powders and other surfaces may produce different results. The three powders are as follows:- Powder A: 1-(2,4,6-trichlorophenyl)-3-(5-[α(3-tertbutyl-4-hydroxyphenoxy)tetradecanamido]-2-chloroanilino)-5-pyrazolone Powder B: α-[4-(4-benzyloxyphenylsulphonyl)phenoxy]-α-(pivalyl)-2-chloro-5-[γ(2,4-ditertamylphenoxy)butyramido]-acetanilide Powder C: 2-[α-(2,4-ditertamylphenoxy)butyramido]-4,6-dichloro-5-ethyl-phenol The four test surfaces are as follows: Surface W: gelatin-coated polyethylene terephthalate Surface X: polished aluminium Surface Y: brushed aluminium Surface Z: card BULK DENSITY (g/cm 3 ) SURFACE L 1 W 1 N 1 N 2 A 0.25 W 9.6 3.3 50 50 A 0.25 X 9.1 ∼4 90 65 A 0.25 Y 8.9 3.5 100 60 A 0.25 Z 9.1 3.2 70 50 B 0.59 W 8.4 3.0 TOTAL 0 B 0.59 X 7.9 3.5 TOTAL 1 B 0.59 Y 8.3 2.8 TOTAL 3 B 0.59 Z 8.1 3.0 TOTAL 2 C 0.5 W 8.3 3.3 7 2 C 0.5 X 8.3 3.0 6 0 C 0.5 Y 8.5 3.3 7 3 C 0.5 Z 8.8 3.2 9 2 Although it was relatively easy to measure the 'footprint' of many samples of powder, it was difficult to relate these measurement to quantitative properties of the bulk powder. Indeed it is the purpose of this device to generate quantitative measures of hitherto subjective or qualitative properties of powders. However, it the observed handling properties of the powder which are of most interest, for example, the 'slumping', 'stickiness', and 'fluffiness', rather than the physical or chemical properties defining, for example, the bulk density, surface charge, residual solvent, particle size and shape. A number of qualitative relationships may be suggested as follows:- PROPERTY POSSIBLE MEASURE adhesion to a sloping surface L 1 spread of particle size L 2 percentage of aggregate particles N 2 size distribution of aggregates N 1 :N 2 lightness/fluffiness W 2 , N 1 , N 2 interparticle repulsion W 1 , W 2 It is not suggested that the above parameters are unique and the only measures of the indicated properties, and more quantitative and qualitative relationships may emerge from experiments using a wider range of compounds. So far, it has been found that for each powder tested a different set of parameters (L, W, N) describe the powder footprint as shown in Table 2. The device of the present invention is small, simple to use and inexpensive. It requires only a small amount of material for the test and enables a quantitative, or semi-quantitative series of measurements to be applied to any given powder sample. Furthermore, it is light and compact, and as no power supply is required, the device can be operated anywhere. It was found that for one particular powder, the application of an ultrasonic probe to the test surface for a few seconds caused the powder to slump rapidly to the bottom of the test surface. This suggests that the application of ultrasonic energy to a feed hopper containing this powder would significantly improve its flow out of the hopper. This indicates that the application of an ultrasonic transducer (possibly one having a variable frequency) to the test surface might enhance the utility of the device. (Although this would introduce the need for an electrical power supply.) Although the device has been applied to powders A, B and C listed above, other powders could equally well be tested in this manner. The size of the device discussed above is approximately 17cm x 13cm x 12cm and is already of a size enabling it to be portable. The device could be folded to be substantially flat or could be dismantled to lie substantially flat thereby making it more portable. Test surfaces could be made of any suitable material, although only three materials and five surfaces have been described herein. Materials such as plastics, and metals other than aluminium, could also be used. Furthermore, the surface properties of the materials used could be rough, polished, electrostatically charged, magnetic, earthed, hydrophobic or hydrophillic or a combination of these, or ultrasonically agitated as mentioned above.

Claims: A testing device (10) for testing the handling properties of a sample of a powder, the device comprising:- a frame (12, 14, 16, 18, 20) comprising at least a substantially vertical member (20) and a substantially horizontal member (16), the vertical member (20) and the horizontal member (16) being positioned to be substantially orthogonal to one another; aperture defining means (22) adjacent to the vertical member (20) for allowing a sample of powder to be introduced into the device under predetermined conditions characterized by a continuous test surface (26, 28, 30) mounted between the vertical member (20) and the horizontal member (16), an upper portion (28) thereof being located at a first position on the vertical member (12) and in contact therewith and a lower portion (30) thereof located at a second position on the horizontal member (16) and in contact therewith; whereby powder introduced through aperture (22) is incident on the upper portion (28) of the test surface (26, 28, 30); the test surface (26, 28, 30) comprising a substantially curved surface portion (26) intermediate the upper portion (28) and the lower portion (30) . A device according to claim 1, wherein the test surface (26, 28, 30) has a grid (38) formed thereon. A device according to claim 4, wherein the grid is linear. A device according to any one of the preceding claims, wherein the frame (12, 14, 16, 18, 20) is substantially rectangular in cross-section and also comprises a top member (14) substantially parallel to the horizontal member (16) and connected to the vertical member (12), and an end member (18) substantially parallel to the vertical member (12), the end member (18) connecting the top member (14) to the horizontal member (16). A device according to claim 4, wherein the horizontal member (16) includes stop means (34, 36) for defining the location of the lower portion (30) of the test surface (26, 28, 30). A device according to claim 5, wherein the aperture defining means (22) is formed in the top member (14) substantially adjacent the upper portion (28) of the test surface (26, 28, 30). A device according to any one of the preceding claims, wherein the device is collapsible for storage or carriage.

Inventors: YOUNG DAVID JOHN, YOUNG, DAVID JOHN, Young, David John, c/o KODAK LIMITED
Applicants: KODAK LTD, KODAK LIMITED
Application year: 1992
Main classification: G01N11
IPC codes: G01N33, G01N15, G01N11