Silicone pressure sensitive adhesives having enhanced adhesion to low energy substrates

Abstract: There is disclosed a pressure-sensitive adhesive composition based on a silicone resin and a polydiorganosiloxane polymer wherein the resin component has a number average molecular weight of about 950 to 1,600 and consists essentially of triorganosiloxy (M) units and silicate (Q) units wherein the molar ratio M/Q is in the range 1.1/1 to 1.4/1, inclusive. The adhesives of the invention exhibit improved adhesion to low energy substrates such as polyethylene and polytetrafluoroethylene.

Description: The present invention relates to silicone pressure sensitive adhesives which comprise a resin component and a polymer component, said adhesives having enhanced adhesion to low energy substrates. More particularly, the adhesives of the invention employ silicone resins which have a critical molecular weight as well as a critical ratio of triorganosiloxy units to silicate units in their molecules. Silicone pressure sensitive adhesives (hereinafter also referred to as PSAs) typically contain at least two primary components, namely a linear siloxane polymer and a tackifier resin consisting essentially of triorganosiloxane (M) units (i.e., R₃SiO 1/2 units, in which R denotes a monovalent organic group) and silicate (Q) units (i.e., SiO 4/2 units). Such "MQ" resins which have heretofore been used to prepare silicone PSA compositions generally have M/Q (molar) ratios in the range of about 0.6 to 0.9. Furthermore, the prior silicone PSA art known to applicants generally does not attribute any significance to the molecular weight of these MQ resins. Where the molecular weight is discussed to any extent, the prior art does not suggest any criticality thereof in connection with the above mentioned M/Q ratios. Thus, EPO Publication No. 0 255 226 to Minnesota Mining and Manufacturing Company (Copley et al.) teaches silicone pressure-sensitive adhesives (PSAs) containing (a) a high molecular weight polydimethylsiloxane gum (or copolymer) and (b) an MQ resin having a polydispersity of 2.0 wherein the M/Q ratio is 0.5 to 1.0. In this disclosure, the inventors prepare narrow fractions of a commercial MQ resin (GE-545). When these resin fractions are used in place of the total resin in the formulation of PSA compositions, the former exhibit superior adhesive performance. Likewise, where the prior art does disclose a broader range of the above mentioned M/Q ratio, it does not suggest the combination of a specific ratio range and a specific molecular weight range to obtain improved adhesive characteristics. For example, United States Patent No. 3,929,704 to Horning teaches a silicone PSA comprising MQ resin, silicone gum and a curing agent, wherein the curing agent is a peroxide admixed with a plasticizer and an extender. While the Horning patent teaches the broad range of M/Q of 0.5 to 1.5, it is silent with respect to any molecular weight limitations to be placed on the silicone resin and the preferred range of M/Q is stated to be 0.55 to 0.75. Moreover, the prior art silicone PSA compositions generally employ a resin/polymer ratio of about 40/60 to about 60/40 by weight and do not suggest the relatively high resin/polymer ratios contemplated in the instant compositions. Although molecular weight of the various resin fractions is noted by Copley et al., the focus of these inventors is on the narrow molecular weight distributions of the resins. Moreover, Copley et al. teach away from the use of resins having an M/Q ratio of less than 0.5 or greater than 1.0. There is, therefore, no suggestion provided by this reference to form a silicone PSA using a silicone resin exhibiting a different range of this M/Q parameter, particularly in combination with a critical molecular weight range for said resin. Neither the application to Copley et al., nor any other art known to applicants, suggests the preparation of silicone PSAs from silicone resins having a molecular weight in the range of 950 to 1600 and at the same time having an M/Q ratio of 1.1 to 1.4, wherein the resin/polymer weight ratio is in the range of 60/40 to 90/10. Unlike the resin fractions of Copley et al., the unfractionated resins of the instant invention are not restricted to a polydispersity of 2.0. When formulated into silicone PSAs, these resins impart improved adhesion to low energy substrates, such as polyethylene and polytetrafluoroethylene (e.g., Teflon™). The present invention, therefore, relates to a silicone pressure sensitive adhesive composition which contains: (A) 60 to 90 parts by weight of a soluble organopolysiloxane having a M n value of 950 to 1,600, the peak of the neopentamer of formula (R₃SiO)₄Si being excluded from the measurement, and consisting essentially of R₃SiO 1/2 siloxane units and SiO 4/2 siloxane units wherein each R denotes a monovalent radical selected from the group consisting of hydrocarbon and halogenated hydrocarbon radicals, at least 1/3 of all R radicals being methyl and the mole ratio of R₃SiO 1/2 siloxane units to SiO 4/2 siloxane units in the soluble organopolysiloxane having a value of from 1.1/1 to 1.4/1, wherein the mole ratio represents the ratio of the total number of triorganosiloxy groups of the resinous and neopentamer portions of (A) to the total number of silicate groups of the resinous and neopentamer portions of (A), and wherein component (A) contains a small amount of a low molecular weight material comprised substantially of a neopentamer organopolysiloxane having the formula (R₃SiO)₄Si; and (B) 10 to 40 parts by weight of a polydiorganosiloxane having the general formula R¹R²₂SiO(R²₂SiO) n SiR²₂R¹ wherein each R² denotes a monovalent radical selected from the group consisting of hydrocarbon and halogenated hydrocarbon radicals, at least 1/2 of all R² radicals being methyl, each R¹ denotes a radical selected from the group consisting of R² radicals and OH radicals and the subscript n is a number having an average value of at least 50. FIG. 1 is a plot of peel adhesion of silicone PSAs from a polyethylene substrate as a function of number average molecular weight of resin employed at an optimum loading. FIG. 2 is a plot of peel adhesion of silicone PSAs from a PTFE substrate as a function of number average molecular weight of resin employed at an optimum loading. The silicone pressure sensitive adhesive compositions of the present invention can be grouped into four separate systems: System I relates to silicone pressure sensitive adhesive compositions that provide very high tack and peel adhesion to substrates including low surface energy materials such as polyolefins and polytetrafluoroethylene; System II relates to silicone pressure sensitive adhesive compositions that provide higher temperature cohesive strength than the silicone pressure sensitive adhesives of System I; System III relates to silicone pressure sensitive adhesive compositions that require less solvent for coating viscosity adjustment than the adhesives of System II; and System IV relates to compositions which contain <1% by weight of volatile components. Component (A) of the present invention is a soluble organopolysiloxane consisting essentially of R₃SiO 1/2 siloxane units and SiO 4/2 siloxane units. By the term soluble, it is meant that the organopolysiloxane can be dissolved, substantially completely, in either a hydrocarbon liquid such as benzene, toluene, xylene, heptane and the like or in a silicone liquid such as cyclic or linear polydiorganosiloxanes. Preferably, the resin is soluble in component (B), delineated below. In the formula for component (A), R denotes a monovalent radical selected from the group consisting of hydrocarbon and halogenated hydrocarbon radicals, preferably having less than 20 carbon atoms and, most preferably, having from 1 to 10 carbon atoms. Examples of suitable R radicals include alkyl radicals, such as methyl, ethyl, propyl, pentyl, octyl, undecyl and octadecyl; cycloalphatic radicals, such as cyclohexyl; aryl radicals such as phenyl, tolyl, xylyl, benzyl and 2-phenylethyl; alkenyl radicals such as vinyl; and chlorinated hydrocarbon radicals such as 3-chloropropyl and dichlorophenyl. To enhance the solubility of component (A) in component (B), it is desirable to select the predominant R radicals of the former to match the predominant R² radicals of the latter. Preferably, at least one-third and, more preferably, substantially all R radical in the formula for component (A), are methyl radicals. The methyl radicals can be distributed in any desired arrangement among the R₃SiO 1/2 siloxane units; however, it is preferred that each R₃SiO 1/2 siloxane unit bear at least one and, more preferably, at least two methyl radicals. Examples of preferred R₃SiO 1/2 siloxane units include Me₃SiO 1/2 , PhMe₂SiO 1/2 and Ph₂MeSiO 1/2 where Me hereinafter denotes methyl and Ph hereinafter denotes phenyl. Component (A) includes a resinous portion wherein the R₃SiO 1/2 siloxane units (i.e., M units) are bonded to the SiO 4/2 siloxane units (i.e., Q units), each of which is bonded to at least one other SiO 4/2 siloxane unit. Some SiO 4/2 siloxane units are bonded to hydroxyl radicals resulting in HOSiO 3/2 units (i.e., TOH units), thereby accounting for the silicon-bonded hydroxyl content of the organopolysiloxane and some are bonded only to other SiO 4/2 siloxane unit. In addition to the resinous portion, component (A) contains a small amount of a low molecular weight material comprised substantially of a neopentamer organopolysiloxane having the formula (R₃SiO)₄Si, the latter material being a byproduct in the preparation of the resin according to the methods of Daudt et al., described infra. For the purposes of the present invention, the resinous portion of component (A) must have a number average molecular weight (M n ) of 950 to 1,600 when measured by gel permeation chromatography (GPC), the neopentamer peak being excluded from the measurement. In this molecular weight determination, conventional polystyrene (PS) molecular weight standards are employed to calibrate the chromatographic apparatus. It has also been found that narrow fractions of MQ resins can be used to calibrate the GPC equipment when the absolute molecular weights thereof are first measured by a technique such as vapor phase osmometry. This latter M n is directly related to the value obtained using the PS standards. For example, in the case of MQ resins based on (CH₃)₃SiO 1/2 siloxane units and SiO 4/2 siloxane units, we have determined that the relation between these two standards is: M n (resin) = 2.77 M n (PS) - 736 wherein the correlation coefficient of the linear regression is R = 0.995 and wherein each GPC determination was run using an identical column set, solvent, flow rate and temperature, as described infra. Thus, M n measurements obtained with resin standards in some of the examples shown below are completely convertible to the corresponding M n values using the PS standards. Unless stated to the contrary, the M n values reported hereinbelow refer to the PS standard and are therefore consistent with convention in the art. It is preferred that component (A) has an M n value of from 1,200 to 1,300 and consists of (CH₃)₃SiO 1/2 siloxane units and SiO 4/2 siloxane units, some of which bear silicon-bonded hydroxyl. Another key requirement of the instant invention is that the mole ratio of the total M siloxane units to total Q siloxane units of the resin be between 1.1 and 1.4, preferably about 1.1 to 1.3. Although this ratio is generally inversely related to the molecular size of the average resin particle, the correlation is, at best, only approximate. The above M/Q mole ratios can be easily obtained by ²⁹Si nuclear magnetic resonance, this technique being capable of a quantitative determination of the molar contents of: M (resin), M(neopentamer), Q (resin), Q(neopentamer) and TOH. For the purposes of the present invention, as implicitly stated supra, the ratio of {M(resin) + M(neopentamer)}/{Q(resin) + Q(neopentamer)} must be between 1.1 and 1.4. Hereinafter, for the sake of conciseness and unless indicated to the contrary, M/Q represents the ratio of the total number of triorganosiloxy groups of the resinous and neopentamer portions of (A) to the total number of silicate groups of the resinous and neopentamer portions of (A). Component (A) can be prepared by any method providing said method provides a soluble organopolysiloxane consisting essentially of R₃SiO 1/2 siloxane units and SiO 4/2 siloxane units and having a M n value of from 950 to 1,600 and an M/Q ratio of 1.1. to 1.4. Component (A) is preferably prepared by the silica hydrosol capping process of Daudt et al., U.S. Patent No. 2,676,182; as modified by Brady, U.S. Patent No. 3,627,851; and Flannigan, U.S. Patent No. 3,772,247. Briefly stated, the modified process of Daudt et al. comprises limiting the concentration of the sodium silicate solution and/or the silicon-to-sodium ratio in the sodium silicate and/or the time before capping the neutralized sodium silicate solution to generally lower values than those disclosed by Daudt et al. in order to prevent excessive growth of the silica particles and to obtain a soluble organopolysiloxane having the required M n . Thus, for the purposes of the present invention, the silicate concentration is generally limited to a value of 40 to 120, preferably 60 to 100 and, most preferably, about 75 grams/liter. The neutralized silica hydrosol is preferably stabilized with an alcohol, such as isopropanol and capped with R₃SiO 1/2 siloxane units as soon as possible, preferably within 30 seconds, after being neutralized. The sodium silicate employed preferably has the formula Na₂O xSiO₂, wherein x has a value of 2 to less than 3.5. It is important to note that the level of the silicon bonded hydroxyl groups on the organopolysiloxane, component (A), may be reduced, preferably to less than about 1 weight percent. This may be accomplished, for example, by reacting hexamethyldisilazane with the organopolysiloxane. Such a reaction may be catalyzed, for example, with trifluoroacetic acid. Alternatively, trimethylchlorosilane or trimethylsilylacetamide may be reacted with the organopolysiloxane, a catalyst not being necessary in this case. Such modified forms of component (A) fall within the definitional requirements of component (A). Component (B) of the present invention is a polydiorganosiloxane having the general formula R¹R²₂SiO(R²₂SiO) n SiR²₂R¹. In this formula each R² denotes a monovalent radical selected from the group consisting of hydrocarbon and halogenated hydrocarbon radicals and each R¹ denotes a radical selected from the group consisting of R² radicals and OH radicals. Examples of R² radicals include the hydrocarbon and halogenated hydrocarbon radicals delineated above for R, as well as monovalent hydrocarbon radicals which contain olefinic unsaturation, such as alkenyl and cycloalkenyl radicals, examples thereof being vinyl, allyl, butenyl, hexenyl, cyclohexenyl and beta-cyclohexenylethyl. Component (B) can be comprised of a single polydiorganosiloxane or a mixture of two or more different polydiorganosiloxanes. Component (B) will typically comprise a polydiorganosiloxane in which at least 50%, and preferably at least 85%, of the R² radicals are methyl radicals. The methyl radicals can be distributed in any manner in the polydiorganosiloxane. R¹ can be any R² radical or a hydroxyl radical. For example both R¹ radicals can be R², such as methyl, vinyl or phenyl or hydroxyl. Alternatively, the R¹ radicals can be different, such as methyl and vinyl or methyl and hydroxyl. In addition, component (B) can comprise trace amounts of siloxane branching sites, such as R²SiO 3/2 units and SiO 4/2 units, provided that the component remains flowable. Component (B) preferably consists essentially of a polydiorganosiloxane having the general formula R''R'₂SiO(R'₂SiO) n SiR'₂R'' wherein each R' denotes methyl, phenyl or alkenyl, at least 85 percent of which are the methyl radical and each R'' denotes a radical selected from the group consisting of R' radicals and OH radicals. The average values of the subscript n in the above formula depend on the type of PSA being prepared. For formulations which include sufficient solvent to impart a practical working viscosity to the final PSA composition, such as Systems I to III, the average value of n is typically greater than about 200. On the other hand, when PSA compositions having less than about 1 weight percent volatile compounds are desired (so-called "solventless" or System IV PSAs), the average value of n should be about 50 to about 200 in order to produce a final PSA having a practical working viscosity. For the purposes of the present invention, the volatile content of such a solventless system is determined by heating a two gram sample of the material to 150°C. for one hour and noting the weight of the residue. The average value of n used should preferably provide an organopolysiloxane component (B) having a viscosity at 25°C. of about 50 millipascal-seconds (50 centipoise) to about 100 kilopascal-seconds (100,000,000 centipoise), the viscosity being a function of the R² radicals on this polymer. The preferred viscosity of component (B) depends on the specific properties desired in the silicone pressure sensitive adhesive. System I and II silicone pressure sensitive adhesives utilize a gum based polydiorganosiloxane, component (B), having a viscosity in the range of 300,000 to 10,000,000 mPa·s (centipoise) when measured at 25°C. System III silicone pressure sensitive adhesives utilize a fluid based polydiorganosiloxane, component (B), having a viscosity in the range of about 800 to 300,000 mPa·s (centipoise), preferably 10,000 to 100,000 mPa·s (centipoise) when measured at 25°C. System IV PSAs employ a component (B) having a viscosity of about 50 to 800 mPa·s (cP), preferably 200 to 500, when measured at 25°C. Examples of polydiorganosiloxanes which are suitable for use as component (B) in the compositions of this invention include hydroxyl-terminated polydiorganosiloxanes, alkenyl-terminated polydiorganosiloxanes and polydiorganosiloxanes terminated with hydrocarbon radicals free of olefinic unsaturation. Specific examples of these polydiorganosiloxane include, but are not limited to, ViMe₂SiO(Me₂SiO) n SiMe₂Vi, ViMe₂SiO(Me₂SiO) 0.95n (MePhSiO) 0.05n SiMe₂Vi, Me₃SiO(Me₂SiO) n SiMe₃, HOMe₂SiO(Me₂SiO) n SiMe₂OH, HOR²₂SiO(Me₂SiO) 0.94n (Ph₂SiO) 0.06n SiR²₂OH, HOR²₂SiO(Me₂SiO) 0.95n (MeViSiO) 0.05n SiR²₂OH, ViMe₂SiO(Me₂SiO) 0.98n (MeViSiO) 0.02n SiMe₂Vi, HOR²₂SiO(Me₂SiO) 0.88n (Ph₂SiO) 0.12n SiR²₂OH, Me₃SiO(Me₂SiO) 0.95n (MeViSiO) 0.05n SiMe₃, PhMeViSiO(Me₂SiO) n SiPhMeVi, Me₃SiO(Me₂SiO) 0.5n (MePhSiO) 0.5n SiMe₃, and PhMeViSiO(Me₂SiO) 0.8n (MePhSiO) 0.1n (Ph₂SiO) 0.1n SiPhMeVi, wherein Me, Vi and Ph denote methyl, vinyl and phenyl, respectively and both R² at a terminal portion are the same as those of at least one of the siloxane units present in the polydiorganosiloxane; and n has its previously defined meaning. The optimum relative amounts of components (A) and (B) that are used to form silicone PSA compositions according to the present invention are best determined by routine experimentation since adhesive performance is at least a function of the molecular weights of resin (A) and polymer (B). Typically, the proportions are such that from 60 to 90 parts by weight of component (A) is used for every 100 parts by weight of components (A) + (B). These amounts are non-volatile amounts, as determined with the non-volatile content test, noted below. The preferred amounts of components (A) and (B) depend on the type of silicone pressure sensitive adhesive. Preferably, the System I silicone pressure sensitive adhesives contain approximately 80 parts by weight of component (A) for every 100 parts by weight of components (A) + (B). Preferably, the System II silicone pressure sensitive adhesives contain approximately 75 parts by weight of component (A) for every 100 parts by weight of components (A) + (B). Preferably, the System III silicone pressure sensitive adhesives contain approximately 72 parts by weight of component (A) for every 100 parts by weight of components (A) + (B). Preferably, the System IV silicone pressure sensitive adhesives contain approximately 70 parts by weight of component (A) for every 100 parts by weight of components (A) + (B). Although the PSAs of the present invention can be cured by heating to temperatures of up to about 300°C. for a suitable length of time, it is preferred that a crosslinking agent (C) is also included in the composition in order to obtain superior adhesive properties. Crosslinking agent (C) of the present invention can be any reactive material that is effective to convert component (B) from its normally flowable state to a non-flowable state. Crosslinking agents which are reactive with the alkenyl radicals and/or hydroxyl radicals and/or alkyl radicals are recommended. Preferably, the crosslinking agent is an organic peroxide or an organohydrogenpolysiloxane. For Systems I to III of the present invention wherein the polymer component (B) does not contain unsaturated groups, an organic peroxide is typically used as the crosslinking agent. Organic peroxide crosslinking agents include benzoyl peroxide, dicumyl peroxide, 2,5-dimethyl-2,5-di(t-butylperoxy)hexane and dichlorobenzoyl peroxide. Benzoyl peroxide has been found to be a particularly effective organic peroxide crosslinking agent. The organic peroxide crosslinking agent is used at about 1 to 2 parts per 100 weight parts of components (A) and (B). In general, for PSAs wherein the polymer component (B) contains olefinically unsaturated groups, the preferred crosslinking agent is an organohydrogenpolysiloxane. When component (B) contains an average of at least 3 olefinically unsaturated groups per molecule, this organohydrogenpolysiloxane crosslinker should have an average of at least 2 silicon-bonded hydrogen atoms in each molecule. When component (B) contains an average of at least 2 olefinically unsaturated groups per molecule, this organohydrogenpolysiloxane crosslinker should have average of at least 3 silicon-bonded hydrogen atoms in each molecule. Preferably, this type of crosslinker has at least 3 Si-bonded hydrogens per molecule. Alternatively, a vinyl-specific peroxide could be used as the crosslinking agent for System I to System III PSAs which employ a polymer containing such unsaturated groups. Illustrative of the organohydrogenpolysiloxanes which are generally operative in the present invention are fluid organohydrogenpolysiloxanes such as polymethylhydrogensiloxanes; fluid siloxane copolymer resins comprised of SiO 4/2 units, Me₃SiO 1/2 units and units such as Me₂HSiO 1/2, MeHSiO 2/2 and Me₂SiO 2/2 , etc.; and mixtures thereof. A preferred organohydrogenpolysiloxane crosslinking agent is a linear methylhydrogenpolysiloxane comprised of methylhydrogensiloxane units and, optionally, dimethylsiloxane units. When an alkenyl-functional siloxane (B) is employed, the organohydrogenpolysiloxane crosslinking agent is added in an amount sufficient to provide from 1 to 200 silicon-bonded hydrogen atoms per alkenyl radical in the composition. The preferred ratio depends on the type of composition. For example, 30 to 60 in Systems I and II PSAs and 10 to 30 in System III PSAs are the respective preferred ranges of silicon-bonded hydrogen atom content per alkenyl radical. System IV PSAs of the invention use a polymer component (B) which contains at least two olefinically unsaturated groups in each molecule and these adhesives are cured with the above described organohydrogenpolysiloxane crosslinking agents. In this case, the crosslinker agent (C) must be compatible with and preferably soluble in, the mixture of (A) and (B). By "compatible," it is meant that the required amount of the organohydrogenpolysiloxane is at least partially soluble in the mixture of (A) and (B) and will exist in a uniformly dispersed state in the compositions of this invention while participating in the curing reaction, until the cure has been effected. In these System IV PSAs, polymethylhydrogensiloxanes having a degree of polymerization of less than 80 are preferably employed as the crosslinking agent. More preferably, the polymethylhydrogensiloxanes have a degree of polymerization of less than 10. This crosslinking agent is added in a sufficient amount to provide from 1 to 30 silicon bonded hydrogen atoms for every olefinically unsaturated radical in the total of (A) plus (B). Preferably, there are from 1 to 10 silicone-bonded hydrogen atoms for every olefinically unsaturated radical. When an organohydrogenpolysiloxane crosslinking agent is used, it is recommended that the compositions additionally include a platinum group metal-containing catalyst, described infra. Such platinum group metal-containing catalysts accelerate the reaction of component (B) with the crosslinking agent and permit room temperature or low temperature curing of the composition. The platinum group metal-containing catalyst is added in an amount sufficient to provide 0.1 to 1,000, preferably 1 to 500 and most preferably 10 to 300, parts by weight of platinum for each one million weight parts of the composition. When a platinum group metal-containing catalyst is used, it is recommended that the compositions additionally include a platinum catalyst inhibitor. The platinum catalyst inhibitor can be any platinum-catalyst inhibitor that is known in the art. Preferred platinum catalyst inhibitors include various "ene-yne" systems, such as 3-methyl-3-pentene-1-yne and 3,5-dimethyl-3-hexene-1-yne; acetylenic alcohols, such as 3-methyl-1-butyne-3-ol, 3,5-dimethyl-1-hexyne-3-ol, 3-methyl-1-pentyne-3-ol and phenylbutynol; maleates and fumarates, such as the well-known dialkyl, dialkenyl and dialkoxyalkyl fumarates and maleates; cyclovinylsiloxanes; and benzyl alcohol. The platinum catalyst inhibitor can be used in any amount that will retard the above-described catalyzed addition reaction at room temperature while not preventing said reaction at elevated temperature; the proportion of this ingredient to be used may be readily determined by routine experimentation. Curing of the compositions of this invention can be accomplished by heating at temperatures of up to 300°C., preferably at 80 to 200°C., for a suitable length of time. The compositions may also be cured by ultraviolet light or electron beam radiation. Ultraviolet light may be used to cure the compositions if one or more crosslinking agents is added prior to curing. Suitable sources of UV radiation include a Hanovia 550-watt lamp or a PPG Processor Model QC1202, inter alia. If ultraviolet light is used, the composition should contain a free-radical initiator or a precious metal-containing catalyst. The latter catalysts include all of the well known platinum and rhodium catalysts which are effective for catalysing the reaction of silicon-bonded hydrogen atoms with silicon-bonded alkenyl radicals or hydroxyl radicals. In addition, complexes of the metals ruthenium, palladium, osmium and irridium can be utilized. A preferred platinum-containing catalyst is a chloroplatinic acid-vinylsiloxane complex disclosed by Willing in U.S. Patent No. 3,419,593. Preferred rhodium catalysts are disclosed by Eckberg in U.S. Patent No. 4,347,346. The amount of precious metal or precious metal-containing catalyst is not critical so long as proper crosslinking is achieved. Alternatively, the composition may be cured using electron beam radiation. Electron beam sources of various types such as van de Graaff-type, resonance transformer-type, linear-type, dynatron-type and high frequency-type can be used. Electron beam radiation having energy of from 50 to 1000 KeV, preferably from 100 to 300 KeV discharged therefrom, may be employed in a dose of from 0.1 to 10.0 Mega Rads (MR). A particularly preferred source of electron beam radiation is one wherein a continuous curtain-like beam emanates from a linear filament. Examples of commercially available sources of electron beam are Electro Curtain CB-150 available from Energy Sciences Inc. and NP-ESH 150 available from Otto Durr. The System I to III compositions of this invention are made by homogeneously mixing 60 to 90 parts by weight of component (A) and 10 to 40 parts by weight of component (B) in the presence of a non-reactive solvent. Solvents useful in the present invention include hydrocarbons, such as toluene, xylene, heptane and mineral spirits; volatile siloxanes, such as octamethylcyclotetrasiloxane and hexamethyldisiloxane; halohydrocarbons, alcohols, esters, ketones and combinations of these solvents. The amount of solvent required depends on the viscosity of the polydiorganosiloxane, component (B). Higher viscosity polydiorganosiloxane polymers require more solvent than lower viscosity polydiorganosiloxane polymers to facilitate the preparation, handling and applying of the compositions. Suitable mixing means include a spatula, a drum roller, a mechanical stirrer, a three-roll mill, a sigma blade mixer, a bread dough mixer and a two-roll mill. Preferably, component (C) is added to the above mixture just before the product is to be used in the case of peroxide crosslinking agent, but may be mixed with (A) and (B) in the case of organohydrogenpolysiloxane crosslinking agent. When the crosslinking agent is an organohydrogenpolysiloxane, the platinum catalyst inhibitor can also be mixed in with components (A), (B) and (C) and the platinum group metal-containing catalyst is preferably added last or just prior to use. System IV PSA compositions of the present invention may also be prepared by mixing the components in a solvent. Typically, component (A) is dissolved in about 5 to 15 weight percent of an organic solvent to facilitate mixing and the component (B) is then added. When the viscosity of component (B) is low enough, mixing can be accomplished without the aid of a solvent (i.e., an essentially 100% solids PSA composition is also contemplated herein). To obtain a solventless composition of the present invention, the mixture of components (A), (B) and solvent should be devolatilized under conditions equivalent to vacuum stripping at 130°C. and 1-2 millimeters of mercury in a batch operation. The removal of solvent can also be accomplished by any of the known techniques such as contact with a stream of inert gas, evaporation, distillation, thin film stripping and the like. Excessively high temperatures should be avoided when components (A) and (B) or their mixtures are being devolatilized. A temperature of 200°C., and preferably 150°C., should not be exceeded. The crosslinking agent and any appropriate catalyst are then added to the devolatilized mixture of (A) and (B) to complete the composition. In general, small amounts of additional ingredients may be added to the compositions of this invention. For example, antioxidants, pigments, stabilizers, fillers, etc., may be added as long as they do not materially reduce the pressure sensitive adhesive properties of these compositions. The silicone PSA compositions of this invention are useful as pressure sensitive adhesives and will readily stick to a solid support, whether flexible or rigid. These compositions may be applied to a surface by any suitable means such as rolling, spreading, spraying, etc. and cured as described above. The surface of the support and the substrate to which the support is adhered may be any known solid material such as metals, such as aluminum, silver, copper, iron and their alloys; porous materials such as paper, wood, leather and fabrics; organic polymeric materials such as polyolefins, such as polyethylene and polypropylene; fluorocarbon polymers such as polytetrafluoroethylene and polyvinylfluoride; silicone elastomers; silicone resins; polystyrene; polyamides such as Nylon; polyesters and acrylic polymers; painted surfaces; siliceous materials such as concrete, bricks, cinderblocks and glass such as glass cloth, etc. Porous materials such as glass cloth are often impregnated with a substance that will prevent the migration of the silicone pressure sensitive adhesive from one surface to another surface of the support. In this regard, it is also well known to chemically treat the surface of a fluorocarbon polymer support to enhance the adhesion of the silicone pressure sensitive adhesive to said surface. As noted previously, the PSAs of the invention are particularly suited to applications wherein good adhesion to a low energy surface (e.g., polyethylene or Teflon™) is desired. Useful articles which can be prepared with the silicone pressure sensitive adhesives of this invention include pressure sensitive tapes, labels, emblems and other decorative or informational signs, among others. An especially useful article is one comprising a flexible or rigid support that can withstand extreme temperatures, hot and/or cold and carrying on at least one surface thereof the silicone pressure sensitive adhesives of this invention. Such an article makes full use of the stability at high temperatures and the flexibility at low temperatures that the silicone pressure sensitive adhesives of this invention possess. The following examples are presented to further illustrate the compositions of this invention, but are not to be construed as limiting the invention, which is delineated in the appended claims. All parts and percentages in the examples are on a weight basis and all measurements were obtained at 25°C., unless indicated to the contrary. The apparatus and testing procedures used for the results shown herein are us follows: Viscosities were measured in centipoise at room temperature (25°+/-2°C.) using a Brookfield rotating disc viscometer fitted with an LV-4 spindle. Non-volatile content, i.e. percent solids, of a material was determined by heating a two gram sample of the material to 150°C. for one hour and expressing the weight of the residue as a percentage of the original sample weight. Molecular weights of the soluble organopolysiloxanes were measured by gel-permeation chromatography (GPC) using Varian TSK 4000 + 2500 columns at 35°C., a chloroform mobile phase at 1 mL/min. Polystyrene (PS) or resin standards were used for linear regression calibrations, the M n obtained using each standard being convertible to the other standard, as described supra. A refractive index detector was used in the GPC measurements employing the PS standard calibration and an IR detector set at 9.1 microns to detect Si-O-Si was used in the measurements employing resin standards. When summation end points were selected go as to exclude the neopentamer portion (Me₃SiO)₄Si of the chromatogram from the molecular weight calculations, the molecular weights are designated by the symbols M n , M z , M w and peak M w . When summation end points were selected so as to include the entire chromatogram in the molecular weight calculations, the molecular weights are designated by the symbols M t n , M t z , M t w and peak M t w . When molecular weights were obtained using the resin standard calibrations, the corresponding PS standard values were also calculated in the manner described supra. Adhesion was measured by applying a 6 x 1 inch strip of a Kapton™- or Mylar™-backed adhesive to a clean 2 x 6 inch stainless steel, polyethylene (PE) or Teflon™ panel using two passes of a 2 kg rubber-coated roller. The force required to remove the tape from the panel was measured with a Keil Tester at an peel angle of 180° at a rate of 12 inches per minute. The values recorded are the average of multiple readings taken during the course of one pull per sample. The Keil Tester is described in TAPPI, vol. 43, No. 8., pages 164A and 165A (August 1960). The readings are reported in units of ounces per inch (oz/in). Tack was measured on five one-inch squares of the Kapton™ or Mylar™-backed adhesive using a POLYKEN (R) probe tack tester, available from Testing Machines, Inc., Amityville, NY. The tack tester has a 0.5 cm diameter stainless steel probe. The test procedure used a 20 gram weight, a dwell time of 0.5 seconds and a pull speed of 0.5 cm per second. The results reported represent the average of the five readings, expressed in grams. Finger Tack was a subjective measurement of the stickiness of the adhesive. Finger Tack was determined by an operator who contacted a finger with the adhesive momentarily and rated the adhesive based on stickiness. The following ratings were used; HIGH, AVERAGE, LOW and NONE. Hold Time was measured by placing 4 x 1/2 inch strips of Kapton™-backed adhesive or Mylar™-backed adhesive onto a clean stainless steel plate so as to provide a 1 x 1/2 inch area of contact and secured with two passes of a 2 kg rubber-coated roller. A 500 gram weight was hung from the free end of each strip. The time at a given temperature required to cause the strips to separate from the steel plate was measured. If a data table cites only a temperature or a pass/fail designation that sample passed a five day hold at that temperature. Tensile Modulus and Breaking Stress were measured by removing a sample of a cured silicone pressure sensitive adhesive from a fluorosilicone release liner and testing it with an Instron tester. The stress in pounds per square inch (psi) at 1000 percent extension and at the breaking point, was determined using a standard stress/strain test method. The following resins of the examples were analyzed using ²⁹Si n.m.r. and the mole percentages of the (CH₃)₃SiO 1/2 units (M) and SiO 4/2 units (Q) for the resinous (res) and neopentamer (neo) portions was determined; from these, the ratio of total M/Q was calculated, as described supra. Resin A = a xylene solution of a resin consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units and having M n = 1,963, M w = 5,040, M z = 15,170, M w /M n = 2.57 and a hydroxyl content of 3.45%. M t n = 920, M t w = 4,259, M t z = 14,732 and M t w /M t n = 4.63 (GPC data obtained using PS standards). M(res) = 36.0; M(neo) = 2.2; Q(res) = 46.8; and Q(neo) = 0.6. M/Q = 0.8. Resin B = a xylene solution of a resin consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units and having M n = 1,535, M w = 3,778, M z = 12,810, M w /M n = 2.46 and a hydroxyl content of 2.63% (GPC data obtained using PS standards). M(res) = 36.4; M(neo) = 10.6; Q(res) = 40.3; and Q(neo) = 2.7. M/Q = 1.1. Resin C = a xylene solution of a resin consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units and having M n = 1,304, M w = 2,353, M z = 6,562, M w /M n = 1.80 and a hydroxyl content of 2.11%. M t n = 568, M t w = 1,560, M t z = 3,768 and M t w /M t n = 2.75 (GPC data obtained using PS standards). M(res) = 43.2; M(neo) = 4.5; Q(res) = 42.2; and Q(neo) = 1.1. M/Q = 1.1. Resin D = a xylene solution of a resin consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units and having M n = 1,066, M w = 1,593, M z = 2,848, M w /M n = 1.49 and a hydroxyl content of 2.12%. M t n = 590, M t w = 1,273, M t z = 2,615 and M t w /M t n = 2.16 (GPC data obtained using PS standards). M(res) = 46.1; M(neo) = 7.3; Q(res) = 37.9; and Q(neo) = 1.7. M/Q = 1.3. Resin E = a xylene solution of a resin prepared by reacting Resin C with hexamethyldisilazane in the presence of trifluoroacetic acid to reduce its silicon-bonded hydroxyl content to less than 0.5 percent. Resin F = a xylene solution of a resin prepared by reacting Resin C with 1,3-bis(3,3,3-trifluoropropyl)tetramethyldisilazane in the presence of trifluoroacetic acid to reduce its silicon-bonded hydroxyl content to less than 1.0 percent. Resin G = a resin prepared by removing the xylene solvent from Resin E and replacing it with hexamethyldisiloxane at a solids content of 80 percent. Resin H = a 69% toluene solution of a resin prepared from an acid-catalyzed hydrolysis/condensation of tetraethoxysilane and consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units having M n = 1,385, M w = 1,906, M z = 2,860, M w /M n = 1.38 (GPC data obtained using Resin standards). The corresponding M n based on PS standards was calculated as 766. M(res) = 54.9; Q(res) = 36.9 (no neopentamer produced by this process). M/Q = 1.5. Resin I = a 62% xylene solution of a resin prepared from sodium silicate according to the methods of Daudt et al., cited supra and consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units and having M n = 1,919, M w = 2,833, M z = 4,477, M w /M n = 1.48 (GPC data obtained using Resin standards). The corresponding M n based on PS standards was calculated as 958. M(res) = 41.9; M(neo) = 9.2; Q(res) = 34.3; and Q(neo) = 2.0. M/Q = 1.4. Resin J = a 70% xylene solution of a resin prepared from sodium silicate according to the methods of Daudt et al. and consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units and having M n = 2,136, M w = 3,396, M z = 5,801, M w /M n = 1.59 (GPC data obtained using Resin standards). The corresponding M n based on PS standards was calculated as 1,037. M(res) = 43.5; M(neo) = 6.4; Q(res) = 35.2; and Q(neo) = 1.7. M/Q = 1.4. Resin K = an 80% xylene solution of a resin prepared from sodium silicate according to the methods of Daudt et al. and consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units and having M n = 2,562, M w = 4,719, M z = 9,261, M w /M n = 1.59 (GPC data obtained using Resin standards). The corresponding M n based on PS standards was calculated as 1,191. M(res) = 44.6; M(neo) = 5.0; Q(res) = 38.0; and Q(neo) = 1.4, M/Q = 1.3. Resin L = an 82.5% xylene solution of a resin prepared from potassium silicate according to the methods of Daudt et al. and consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units and having M n = 3,788, Mw = 12,020, M z = 38,530, M w /M n = 3.17 and a hydroxyl content of 2.74% (GPC data obtained using Resin standards). The corresponding M n based on PS standards was calculated as 1,633. M(res) = 40.0; M(neo) = 5.2; Q(res) = 39.9; and Q(neo) = 1.4. M/Q = 1.1. Resin M = a 73.5% xylene solution of a resin prepared from sodium silicate according to the methods of Daudt et al. and consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units and having M n = 4,339, M w = 16,140, M z = 59,620, M w /M n = 3.72 and a hydroxyl content of 2.54% (GPC data obtained using Resin standards). The corresponding M n based on PS standards was calculated as 1,832. M(res) = 39.3; M(neo) = 4.1; Q(res) = 41.4; and Q(neo) = 1.3. M/Q = 1.0. Resin N = a 71% xylene solution of a resin prepared from sodium silicate according to the methods of Daudt et al. and consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units and having M n = 4,364, M w = 15,840, M z = 54,640, M w /M n = 3.63 and a hydroxyl content of 2.55% (GPC data obtained using Resin standards). The corresponding M n based on PS standards was calculated as 1,841. M(res) = 41.6; M(neo) = 2.3; Q(res) = 42.8; and Q(neo) = 0.8. M/Q = 1.0. Resin N-1 = a 75% xylene solution of a resin prepared by fractionating Resin N, this fraction consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units and having M n = 3,317, M w = 5,138, M z = 8,578, M w /M n = 1.55 (GPC data obtained using Resin standards). The corresponding M n based on PS standards was calculated as 1,463. M(res) = 44.3; Q(res) = 44.3; M/Q = 1.0. Resin O = a 78% xylene solution of a resin prepared from potassium silicate according to the methods of Daudt et al. and consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units and having M n = 5,697, M w = 25,400, M z = 88,550, M w /M n = 4.46 and a hydroxyl content of 2.56% (GPC data obtained using Resin standards). The corresponding M n based on PS standards was calculated as 2,322. M(res) = 39.3; M(neo) = 4.1; Q(res) = 41.7; and Q(neo) = 1.1. M/Q = 1.0. Resin P = 90% xylene solution of a resin consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units in a mole ratio of 1.1/1.0 with Mn = 2,708, Mw/Mn = 1.7 and the silanol content is less than 0.5 weight percent (GPC data obtained using resin standards). The corresponding M n based on PS standards was calculated as 1,243. Resin Q = a 73% xylene solution of a resin consisting of (CH₃)₃SiO 1/2 units and SiO 4/2 units in a mole ratio of 1.3/1.0 with Mn = 2,251, Mw/Mn = 2.05 and the silanol content is less than 0.5 weight percent (GPC data obtained using resin standards). The corresponding M n based on PS standards was calculated as 1,078. Polymers A-F, J and K are silicone gums having a plasticity number of 140-165, as measured by ASTM 926-67 and viscosities of at least 10,000,000 mPa·s (centipoise) measured at 25°C. 25°C. Polymer A = a 7.5/1 blend of a dimethylpolysiloxane having dimethylvinylsiloxy endgroups and a vinyl content of 0.02 mole percent and a dimethyl-co-methylvinylpolysiloxane having dimethylvinylsiloxy endgroups and a vinyl (Vi) content of 2.0 mole percent. Polymer B = a dimethyl-co-methylvinylpolysiloxane having dimethylvinylsiloxy endgroups and a methylvinylsiloxy content of 0.11 mole percent. Polymer C = a dimethyl-co-phenylmethyl-co-methylvinylpolysiloxane having dimethylvinylsiloxy endgroups, a methylvinylsiloxy content of 0.14 mole percent and a phenylmethylsiloxy content of 7.5 mole percent. Polymer D = a dimethylvinyl-terminated dimethyl-co-diphenylpolysiloxane having diphenylsiloxy content of 10 mole percent. Polymer E = a dimethyl-co-methylvinylpolysiloxane having dimethylvinylsiloxy endgroups and a vinyl content of 0.14 mole percent. Polymer F = a dimethylpolysiloxane having dimethylvinylsiloxy endgroups and a vinyl content of 0.02 mole percent. Polymer G = a dimethylpolysiloxane having dimethylvinylsiloxy endgroups and a viscosity of 63,000 mPa·s (centipoise) measured at 25°C. Polymer H = a dimethylpolysiloxane having dimethylvinylsiloxy endgroups and a viscosity of 10,000 mPa·s (centipoise) measured at 25°C. Polymer I = a dimethylpolysiloxane having dimethylvinylsiloxy endgroups and a viscosity of 500 mPa·s (centipoise) measured at 25°C. Polymer J = a dimethylpolysiloxane having hydroxyl endgroups. Polymer K = a dimethylpolysiloxane having dimethylvinylsiloxy endgroups. Polymer L = a polydimethylsiloxane of the formula wherein m is a number having an average value of 150. Polymer L has a viscosity of 450 centipoise measured at 25°C. Polymer M = a polydimethylsiloxane of the formula wherein m is a number having an average value of 100 and x is a number having an average value of 4. Polymer M has a viscosity of 300 mPa·s (centipoise) measured at 25°C. Crosslinking Agent A = a trimethylsiloxy terminated dimethyl-co-methylhydrogenpolysiloxane having a methylhydrogensiloxy content of 70 mole percent and an average degree of polymerization of 40. Crosslinking Agent B = a trimethylsiloxy-terminated methylhydrogen-co-dimethylpolysiloxane having a viscosity of about 20 mPa·s (centipoise) and containing 1.03% silicon-bonded hydrogen atoms. Crosslinking Agent C = a dimethylhydrogensiloxy terminated dimethylpolysiloxane with an average degree of polymerization of 15. Crosslinking Agent D = a soluble organopolysiloxane consisting of (CH₃)₃SiO 1/2 units, (CH₃)₂HSiO 1/2 units and SiO 4/2 units in a mole ratio of 0.6/0.9/1.0. Crosslinking Agent E = a soluble organopolysiloxane consisting of (CH₃)₃SiO 1/2 units, (CH₃)₂HSiO 1/2 units and SiO 4/2 units in a mole ratio of 1.2/1.8/1.0. Crosslinking Agent F = a trimethylsiloxy terminated methylhydrogenpolysiloxane having an average degree of polymerization of 40. Crosslinking Agent G = a trimethylsiloxy terminated dimethyl-co-methylhydrogenpolysiloxane having a methylhydrogensiloxy content of 9 mole percent and an average degree of polymerization of 100. Crosslinking Agent H = a trimethylsiloxy terminated dimethyl-co-methylhydrogenpolysiloxane having a methylhydrogensiloxy content of 27 mole percent and an average degree of polymerization of 15. Crosslinking Agent I = a trimethylsiloxy terminated methylhydrogenpolysiloxane having an average degree of polymerization of 5. Crosslinking Agent J = a trimethylsiloxy terminated methylhydrogenpolysiloxane having an average degree of polymerization of 10. Crosslinking Agent K = a trimethylsiloxy terminated methylhydrogenpolysiloxane having an average degree of polymerization of 20. EXAMPLE 1 Mixtures of Resin D (67% in xylene) and Polymer A, in ratios ranging from 43-87 parts of Resin D to 57-13 parts of Polymer A, a trimethylsiloxy-terminated polymethylhydrogensiloxane crosslinking agent (Cross linking Agent F) (SiH/Vi molar ratio = 3/1), toluene (50% based on the total weight), a vinylsiloxane complex of chloroplatinic acid (0.4% based on total weight) and 3,5-dimethyl-1-hexyne-3-ene, were prepared. The compositions were applied to the surface of a 51 µm (2 mil) Mylar™ backing by means of 76 µm (3 mil) Bird bar. The compositions were cured in a laboratory convection oven at 130°C. for four minutes. The test results are summarized in Table I. The different ratios and the results associated with such ratios of Resin D to Polymer A are provided by letters A through I. EXAMPLE 2 Compositions identical to those of Example 1 were prepared, except Resin C (78% in xylene) was substituted for Resin D. The test results are summarized in Table I. EXAMPLE 3 Compositions identical to those of Example 1 were prepared, except Resin B (60% in xylene) was substituted for Resin D. The test results are summarized in Table I. COMPARATIVE EXAMPLE 4 Compositions identical to those of Example 1 were prepared, except Resin A (68% in xylene) was substituted for Resin D. The test results are summarized in Table I. EXAMPLE 5 Mixtures of Resin D (67% in xylene) and Polymer J, in ratios ranging from 43-87 parts of Resin D to 57-13 parts of Polymer A, benzoyl peroxide (2% based on silicone solids) and toluene (50% of total mixture) were prepared. The compositions were applied to the surface of a 51 µm (2 mil) Mylar™ backing by means of 76,2 µm (3 mil) Bird bar. The compositions were cured in a laboratory convection oven for one minute at 70°C. and for two minutes at 178°C. The test results are summarized in Table II. The different ratios and the results associated with such ratios of Resin D to Polymer A are provided by letters A through I. EXAMPLE 6 Compositions identical to those of Example 5 were prepared, except Resin C (78% in xylene) was substituted for Resin D. The test results are summarized in Table II. EXAMPLE 7 Compositions identical to those of Example 5 were prepared, except Resin B (60% in xylene) was substituted for Resin D. The test results are summarized in Table II. COMPARATIVE EXAMPLE 8 Compositions identical to those of Example 5 were prepared, except Resin A (68% in xylene) was substituted for Resin D. The test results are summarized in Table II. Tables I and II illustrate the improved adhesion of the instant PSAs to a low energy substrate (polyethylene). EXAMPLES 9-12 Resin C (78% in xylene) was mixed with Polymer A in a resin/polymer ratio of 81/19 and various amounts of Crosslinking Agent B were added to portions thereof, along with a catalytic amount of a vinylsiloxane complex of chloroplatinic acid and a stabilizing amount of the catalyst inhibitor 3,5-dimethyl-1-hexyne-3-ene were added. The resulting compositions were cast onto 25 µm (1-mil) Kapton™ and cured at 130°C. for 4 minutes. A 38 to 51 µm (1.5 to 2.0 mil) cured adhesive film was formed. The adhesion and tack of the resulting silicone pressure sensitive adhesives is disclosed in Table III. EXAMPLE 13 Example 11 was repeated except Polymer A was replaced with Polymer B. The resulting composition was cast and cured as described in Examples 9-12. The test results are disclosed in Table III. Example Vinyl Mol % SiH/Vinyl Mol Ratio Adhesion, N/cm (oz/in) Tack (gms) Steel PTFE 9 0.28 1.5 2,63 (24) (12) 1,31 835 10 0.28 18.0 7,66 (70) (20) 2,19 325 11 0.28 36.0 8,21 (75) (34) 3,72 1095 12 0.28 60.0 7,66 (70) (20) 2,19 830 13 0.11 38.0 8,21 (75) (30) 3,28 1400 The results in Table III clearly show that different ranges of the polydiorganosiloxane polymer and silicone hydride crosslinker are acceptable in the preparation of silicone pressure sensitive adhesives that have high adhesion to PTFE (Teflon™). EXAMPLE 14 A silicone PSA was prepared using 82.7 parts of a resin having an M n = 1,125 (PS standard GPC), 17.3 parts of Polymer A, 2.45 parts of Crosslinking Agent B, 0.15 part of 3,5-dimethyl-1-hexyne-3-ene inhibitor and 75 parts of toluene. This adhesive was cured with 0.9% of a 50% toluene solution of a chloroplatinic acid-vinylsiloxane complex on a 25 µm (1-mil) Kapton™ backing at an adhesive thickness of 38 to 51 µm (1.5 to 2.0 mils). Adhesion to stainless steel, polytetrafluoroethylene, polyethylene and low (38.6 dyne/cm) energy acrylic panels was determined, the results being presented in Table IV. Adhesion N/cm (oz/in) PTFE Acrylic Steel PE 3,50 (32) 8,76 (80) 8,76 (80) 6,57 (60) EXAMPLE 15 Eight grams (solids basis) of Resin C (71% in xylene) was mixed with 1.7 grams (solids basis) of Polymer C (25% in xylene) to provide a resin/polymer ratio of 82.5/17.5 and 240 microliters of the polymethylhydrogen-co-dimethylsiloxane used in Examples 9-12, was added, along with a catalytic amount (0.4% based on total composition) of a vinylsiloxane complex of chloroplatinic acid and a stabilizing amount of 3,5-dimethyl-1-hexyne-3-ene. The resulting composition was cast onto 1-mil Kapton™ and cured at 130°C. for 4 minutes forming a 38 to 51 µm (1.5 to 2.0 mil) adhesive film. The adhesion of the resulting PSA was 8,32 N/cm (76 oz/in)(steel) and 4,05 N/cm (37 oz/in)(polytetrafluoroethylene); tack was 1,484 g; and hold time at 70°C. was 120-180 minutes. EXAMPLE 16 Four grams (solids basis) of Polymer D (25% in xylene) was mixed with 14.2 grams (solids basis) of Resin C (78% in xylene) to provide a resin/polymer ratio of 78/22 and 3.6 grams of a 10% solution of benzoyl peroxide in toluene was added. The resulting composition was cast onto 1-mil Kapton™ and cured at 70°C. for 1 minute and at 204°C. for 2 minutes. The adhesion and tack of the resulting adhesive was 8,54 N/cm (78 oz/in)(steel) and 3,28 N/cm (30 oz/in)(polytetrafluoroethylene) and the tack was 1578 grams. The results in Examples 15 and 16 illustrate that polymers other than dimethylsiloxanes and methylvinylsiloxanes may be used in the compositions of the present invention. EXAMPLES 17-19 Three compositions were prepared by mixing Resin E (80% in xylene) with various mixtures of Polymers E and F in a resin/polymer ratio of 74/26; a sufficient amount of Crosslinking Agent B to provide a SiH/SiVi molar ratio of 100/1; a sufficient amount of toluene to provide adhesive solutions containing 50 percent solids; a vinylsiloxane complex of chloroplatinic acid (0.4% based on total composition) and a platinum catalyst inhibitor. The compositions were cast as 38 µm (1.5 mil) films on 25 µm (1-mil) Kapton™ backing. The test results are summarized in Table V. Modulus at 1000% and breaking stress for the adhesive of Example 19 is recorded in Table VI. EXAMPLE 20 This example was prepared and is identically described in Example 19, except Resin C (70% in xylene) was substituted for Resin E. The test results are summarized in Tables V and VI. Example Polymer Ratio F/E Resin/Polymer Weight Ratio SiH/SiVi Adhesion, N/cm (oz/in ) 5-day Hold (°F) Tack (gms) Steel PTFE 17 5/0 74/26 100 4,05 (37)a (20)a 2,19 500 1196 18 0/5 74/26 100 4,23 (45)a (18)a 1,97 400 1150 19 1/4 74/26 100 7,55 (69)c (25)a 2,74 400 1445 20 1/4 74/26 100 4,23 (45)a (20)a 2,19 <300 1055 EXAMPLES 21-23 Three compositions were prepared by mixing Resin E (80% in xylene) with Polymer E or Polymer F or a mixture of Polymers E and F, in resin/polymer ratios of 72/28 and 75/25; a sufficient amount of the crosslinking agent used in Examples 17-19 to provide a SiH/SiVi ratio of from 48/1 to 100/1; a sufficient amount of toluene to provide adhesive solutions containing 50 percent solids; a vinylsiloxane complex of chloroplatinic acid (0.4% based on total composition) and a platinum catalyst inhibitor. The Compositions were cast as 38 µm (1.5 mil) films on 25 µm (1-mil) Kapton™ backing. The test results are summarized in Table VII. EXAMPLE 24 This example is similar to those described in Examples 21-23, except Resin C (78% in xylene) was substituted for Resin E. The test results are summarized in Tables VI and VII. Example 1000% Modulus(psi) Stress at Break (psi) 19 84.5 175 25 88.9 107 20 35.4 62 24 6.6 48 Example Polymer Ratio F/E Resin/Polymer Weight Ratio SiH/SiVi Adhesion, N/cm (oz/in ) 5-day Hold (°F) Tack (gms) Steel PTFE 21 5/0 75/25 72 5,08 (46)a (19)a 2,08 400 1000 22 1/4.5 75/25 48 5,03 (46)a (20)a 2,19 400 1052 23 0/5 72/28 100 4,82 (44)a (20)a 2,19 <300 990 24 1/4 80/20 100 7,44 (68)b (28)a 3,06 <200 602 The results in Tables V and VII indicate that silicone pressure sensitive adhesives of System II show superior high temperature shear strength to those of System I. EXAMPLE 25 A composition was prepared by mixing Resin F (70% in xylene) and a 1:4 mixture of Polymer F:Polymer E in a resin/polymer ratio of 74/26; a sufficient amount of a crosslinking agent of Example 17 to provide a SiH/SiVi molar ratio of 100/1; a sufficient amount of toluene to provide adhesive solutions containing 50 percent solids; a vinylsiloxane complex of chloroplatinic acid (0.4% based on total composition) and a platinum catalyst inhibitor. The peel adhesion on steel and polytetrafluoroethylene (PTFE), tack and 5-day hold temperature values for this composition, cast as 38 µm (1.5 mil) films on 25 µm (1-mil) Kapton™ backing, were 6,24 N/cm (57 oz/in); 2,19 N/cm (20 oz/in); 951 grams; and 204°C (400°F.), respectively. A comparison of these values with those of Example 20 in Table V shows the greater shear strength of the composition of the example. Modulus at 1000% and breaking stress for the adhesive of Example 25 are recorded in Table VI, above. EXAMPLES 26-39 Fourteen compositions of this invention were prepared by mixing appropriate amounts of Resin E, 80% in xylene, (except Example 28 which was prepared with Resin G) and Polymers G, H and/or I, to provide a resin/polymer ratio of 72/28 and a sufficient amount of the Crosslinking Agent A, to provide various molar amounts of silicon-bonded hydrogen for every silicon-bonded vinyl radical in Polymers G, H and/or I as noted in Table VIII. The compositions of Examples 26-31 were prepared with Polymer G. The compositions of Examples 34-39 were prepared with Polymer H. The composition of Example 32 was prepared with a 90/10 mixture of Polymers G and H. The composition of Example 33 was prepared with a 97/3 mixture of Polymers G and I. The solvent content of some of the mixtures was reduced by evaporation at reduced pressure and/or elevated temperature, to provide the solids content noted in Table VIII. A catalytic amount of a vinylsiloxane complex of chloroplatinic acid dissolved in Polymer I, a cure inhibiting amount of diethyl fumarate (DEF) and a bathlife extending amount of benzyl alcohol (BzOH) were added, as noted in Table IX, to the resulting compositions. The catalyzed compositions were cast as 38 µm (1.5 mil) films on 25 µm (1-mil) Kapton™ backing and cured by one of three methods as follows. Method 1 consisted of heating the coated film at 130°C. for 6 minutes for compositions having a SiH/SiVi molar ratio of 16 or less and at 130°C. for 4 minutes for compositions having a SiH/SiVi ratio of greater than 16. Method 2 consisted of exposing the coated film 7 times, at a rate of 4,6 m (15 feet) per minute, to a 0,3 m (1-foot) opening of ultraviolet radiation from two mercury vapor lamps each having an output of 79 W/cm (200 watts per inch) and positioned 10,2 cm (4 inches) above the belt. Method 3 consisted of Method 2 followed by Method 1. The peel adhesion, tack, 5-day hold temperature, solids content and composition viscosity values for these compositions are listed in Table VIII. EXAMPLES 40-41 Compositions identical to those of Example 26 were prepared, except Polymers K and B, respectively were substituted for Polymer G. The test results are summarized in Table VIII. Example DEF, % BzOH, % Pt, % Pt/DEF BzOH/DEF 26 2.5 - - 0.00 0.0 27 0.15 0.6 0.375 2.50 4.0 28 2.5 - - 0.00 0.0 29 1.5 3.0 0.75 0.50 2.0 30 0.3 0.3 0.75 2.50 1.0 31 1.5 - 2.25 1.50 0.0 32 0.3 0.6 0.375 1.25 2.0 33 0.3 0.6 0.375 1.25 2.0 34 2.5 - - 0.00 0.0 35 0.75 - 0.75 1.00 0.0 36 1.5 3.0 0.75 0.50 2.0 37 1.5 3.0 0.75 0.50 2.0 38 1.5 - 2.25 1.50 0.0 39 0.75 - 0.75 1.00 0.0 40 0.1 - 0.375 3.75 0.0 41 0.3 0.6 0.75 2.50 2.0 The results in Tables VIII and IX show that the high-solids, low-viscosity silicone pressure sensitive adhesive compositions of this invention have excellent adhesive strength, tack and hold properties. EXAMPLES 42-49 Eight compositions were prepared by mixing appropriate amounts of Resin E (80% in xylene) and Polymer G, to provide a resin/polymer ratio of 72/28 and a sufficient amount of Crosslinking Agent A, to provide molar amounts of silicon-bonded hydrogen for every silicon-bonded vinyl radical in Polymer G which ranged from 1/1 to 128/1, as noted in Table X. A vinylsiloxane complex of chloroplatinic acid and a platinum catalyst inhibitor was also added. The compositions were cast as 38 µm (1.5 mil) films on 25 µm (1-mil) Kapton™ backing and heated at 130°C. for 6 minutes for compositions having an SiH/SiVi ratio of 16 or less and at 130°C. for 4 minutes for compositions having an SiH/SiVi ratio of greater than 16. The test results are summarized in Table X. EXAMPLES 50-57 The compositions of Examples 42-49 were prepared again, except 0.375% of a vinylsiloxane complex of chloroplatinic acid dissolved in Polymer I, 0.3% of diethyl fumarate and 0.6% of benzyl alcohol, all based on the weight of Polymer G, were used. The compositions were cast as 38 µm (1.5 mil) films on 25 µm (1-mil) Kapton™ backing, the films were heated for 2 minutes at 70°C. to remove solvent and the solvent-free films were exposed for 20 seconds to the ultraviolet radiation of two mercury vapor lamps each having an output of 79 w/cm (200 watts per inch). The peel adhesion, tack and 5-day hold temperature values for these compositions are listed in Table X. Example SiH/SiVi Adhesion N/cm (oz/in ) Hold °C (°F) Tack (grams) 42 1/1 1,75 (16)c - 680 43 2/1 1,42 (13)c - 608 44 4/1 6,57 (60)ac - 1250 45 8/1 5,69 (52)a 204 (400) 1340 46 16/1 6,13 (56)a 204 (400) 1134 47 32/1 4,6 (42)a 204 (400) 918 48 64/1 5,25 (48)a 204 (400) 1503 49 128/1 3,06 (28)a 204 (400) 1384 50 1/1 1,64 (15)c - 477 51 2/1 2,41 (22)c - 576 52 4/1 5,25 (48)a 204 (400) 431 53 8/1 5,36 (49)a 204 (400) 703 54 16/1 7,11 (65)ac 204 (400) 878 55 32/1 6,35 (58)a 204 (400) 963 56 64/1 5,69 (52)c 204 (400) 1252 57 128/1 2,85 (26)a 204 (400) 995 The results in Table X indicate that a SiH/Sivi ratio of greater than 4.0 is required to provide both heat-cured and UV-cured silicone pressure sensitive adhesives which possesses predominantly adhesive failure during peel release. EXAMPLES 58-62 Five compositions were prepared by mixing appropriate amounts of Resin E (80% in xylene) and Polymer G to provide compositions having a resin/polymer ratio which ranged from 68/32 to 76/24 and a sufficient amount of Crosslinking Agent A, to provide 44 moles of silicon-bonded hydrogen for every mole of silicon-bonded vinyl radical in Polymer G. A catalytic amount of a vinylsiloxane complex of chloroplatinic acid dissolved in Polymer I, a cure inhibiting amount of diethyl fumarate were added to the resulting compositions. The catalyzed compositions were cast as 76 µm (3 mil) wet films on 25 µm (1-mil) Kapton™ backing and cured by heating the coated film at 130°C. for 4 minutes. The peel adhesion values were 23a, 36a, 42a, 70c and 80c oz/in for compositions having resin/polymer ratios of 68/32, 70/30, 72/28, 74/26 and 76/24, respectively, where c and a have the meanings noted in Table X. The finger tack was judged to be excellent for all but the 76/24 composition which was judged to have good finger tack. EXAMPLE 63 A composition comprising Resin E (80% in xylene) and Polymer H in a resin/polymer ratio of 70/30 and having a sufficient amount of Crosslinking Agent C, to provide 2 moles of silicon-bonded hydrogen for every mole of silicon-bonded vinyl radical in Polymer H. A vinylsiloxane complex of chloroplatinic acid and a platinum catalyst inhibitor were also added. The cured adhesive exhibited a peel adhesion value of 3,39 N/cm (31 oz/in), a tack value of 1223 grams and a hold temperature of 204°C (400°F). EXAMPLE 64 A composition comprising Resin E (80% in xylene) and Polymer I in a resin/polymer ratio of 70/30, a sufficient amount of crosslinking agent consisting of a mixture of Crosslinking Agents A and C, to provide 2 moles of silicon-bonded hydrogen for every mole of silicon-bonded vinyl radical in Polymer I. A vinylsiloxane complex of chloroplatinic acid and a platinum catalyst inhibitor were also added. The cured adhesive exhibited a peel adhesion value of 1,64 N/cm (15 oz/in) and a tack value of 868 grams. EXAMPLES 65-66 Two compositions were prepared using resinous crosslinkers. Resin E (80% in xylene) was mixed with Polymer H in a 70/30 resin to polymer ratio and a sufficient amount of Crosslinking Agent D for Example 65 and Crosslinking Agent E for Example 66, to provide a 10 moles of silicon bonded hydrogen for every mole of silicon bonded vinyl radical in Polymer H. Catalytic levels of a vinylsiloxane complex of chloroplatinic acid and a platinum catalyst inhibitor, diethyl fumerate were also added. The samples were cast as 38 µm (1.5 mil) adhesive films on a 25 µm (1 mil) Kapton™ backing and cured at 130°C. for four minutes. The adhesive from Example 65 had a peel adhesion of 3,39 N/cm (31 oz/in). The adhesive from Example 66 had a peel adhesion of 4,38 N/cm (40 oz/in). EXAMPLES 67-75 Silicone PSAs having resin to polymer ratios in the range 43/57 to 87/13 were prepared according to the procedures of Examples 1-4 using Resins H through O as the organopolysiloxane (A) component and using SiH-functional Crosslinking Agent F. These formulations were cured on 51 µm (2 mil) Mylar™ film and tested as before, adhesion to Teflon™ being added to the evaluations. The results are presented in Tables XI through XIX, respectively. Likewise, PSAs prepared according to the procedures of Examples 5-8 using Resins H through O were prepared using a peroxide cure system. In each of these PSAs only one resin/polymer ratio was employed for each example, this being the ratio which provided the optimum adhesion on Teflon™ for the corresponding SiH-cured system above. The test results of these peroxide-cured PSAs are also presented in Tables XI through XIX, respectively, as indicated by entries displaying an asterisk alongside the resin/polymer weight ratio (first column of each table). (Comparative) Example 67 (Resin H) Resin/Polymer Weight Ratio Adhesion (oz/in) N/cm Probe Tack (g) Steel PE TEFLON™ 43/57 0a 0a 0a 100 50/50 0a 0a 0a 110 56/44 0a 0a 0a 120 62/38 0a 0a 0a 130 67/33 0a 0a 0a 140 72/28 0a 0a 0a 140 77/23 0a 0a 0a 165 82/18 0a 0a 0a 0 87/13 0a 0a 0a 0 82/18 0a 0a 0a 55 Example 68 (Resin I) Resin/Polymer Weight Ratio Adhesion (oz/in) N/cm Probe Tack (g) Steel PE TEFLON™ 43/57 0,22 (2)a 0a 0a 150 50/50 0,33 (3)a 0a 0a 250 56/44 0,33 (3)a 0,11 (1)a 0a 330 62/38 0,33 (3)a 0,22 (2)a 0,11 (1)a 415 67/33 0,55 (5)a 0,66 (6)a 0,44 (4)a 555 72/28 1,97 (18)a 1,86 (17)a 1,20 (11)a 740 77/23 3,72 (34)c 3,06 (28)c 3,28 (30)c 710 82/18 2,63 (24)c 2,85 (26)c 2,63 (24)c 300 87/13 3,39 (31)c 3,50 (32)c 3,50 (32)c 305 77/23 4,82 (44)c 4,93 (45)c 4,71 (43)c 715 Example 69 (Resin J) Resin/Polymer Weight Ratio Adhesion (oz/in) N/cm Probe Tack (g) Steel PE TEFLON™ 43/57 0,11 (1)a 0a 0a 235 50/50 0,22 (2)a 0a 0a 310 56/44 0,33 (3)a 0,22 (2)a 0,11 (1)a 370 62/38 0,44 (4)a 0,44 (4)a 0,33 (3)a 415 67/33 0,88 (8)a 1,42 (13)a 1,09 (10)a 740 72/28 2,63 (24)a 3,72 (34)a 2,41 (22)a 990 77/23 5,25 (48)c 5,03 (46)c 4,38 (40)c 1170 82/18 5,91 (54)c 5,47 (50)c 5,36 (49)c 370 87/13 0c 0a 0 0 77/23 5,91 (54)c 5,36 (49)c 5,14 (47)c 1050 Example 70 (Resin K) Resin/Polymer Weight Ratio Adhesion (oz/in) N/cm Probe Tack (g) Steel PE TEFLON™ 43/57 0a 0a 0a 270 50/50 0,11 (1)a 0a 0a 340 56/44 0,33 (3)a 0,11 (1)a 0,11 (1)a 495 62/38 0,88 (8)a 0,66 (6)a 0,33 (3)a 700 67/33 2,41 (22)a 1,75 (16)a 1,31 (12)a 1140 72/28 4,82 (44)a 3,06 (28)a 1,97 (18)a 1465 77/23 7 (64)c 7,77 (71)c 6,13 (56)c 1260 82/18 7,88 (72)c 0,33 (3)c 0a 65 87/13 0a 0a 0a 0 77/23 7,88 (72)c 7,66 (70)c 5,47 (50)c 1400 (Comparative) Example 71 (Resin L) Resin/Polymer Weight Ratio Adhesion (oz/in) N/cm Probe Tack (g) Steel PE TEFLON™ 43/57 0,88 (8)a 0,22 (2)a 0,22 (2)a 445 50/50 2,19 (20)a 0,55 (5)a 0,44 (4)a 445 56/44 3,61 (33)a 1,42 (13)a 0,99 (9)a 560 62/38 5,91 (54)a 3,06 (28)a 1,86 (17)a 600 67/33 7,88 (72)a 1,31 (12)a 0,55 (5)a 265 72/28 7,88 (72)a 0a 0a 40 77/23 0,88 (8)a 0a 0a 0 82/18 0,88 (8)a 0a 0a 0 87/13 0a 0a 0a 0 62/38 6,46 (59)a 2,41 (22)a 1,75 (16)a 715 (Comparative) Example 72 (Resin M) Resin/Polymer Weight Ratio Adhesion (oz/in) N/cm Probe Tack (g) Steel PE TEFLON™ 43/57 0,77 (7)a 0,44 (4)a 0,33 (3)a 460 50/50 2,63 (24)a 0a 0a 575 56/44 4,27 (39)a 0,66 (6)a 0,66 (6)a 560 62/38 5,58 (51)a 0,88 (8)a 0,22 (2)a 370 67/33 5,91 (54)a 0a 0a 80 72/28 0,44 (4)a 0a 0a 0 77/23 0a 0a 0a 0 82/18 0a 0a 0a 0 87/13 0a 0a 0a 0 56/44 5,91 (54)a 1,31 (12)a 0,99 (9)a 320 (Comparative) Example 73 (Resin N) Resin/Polymer Weight Ratio Adhesion (oz/in) N/cm Probe Tack (g) Steel PE TEFLON™ 43/57 0,88 (8)a 0,11 (1)a 0a 445 50/50 3,39 (31)a 0,55 (5)a 0,33 (3)a 475 56/44 4,82 (44)a 0,77 (7)a 0,55 (5)a 435 62/38 6,57 (60)a 0,88 (8)a 0,33 (3)a 85 67/33 7,88 (72)c 0,11 (1)a 0a 0 72/28 0a 0a 0a 0 77/23 0a 0a 0a 0 82/18 0a 0a 0a 0 87/13 0a 0a 0a 0 56/44 4,71 (43)a 0,88 (8)a 0,44 (4)a 320 (Comparative) Example 74 (Resin N-1) Resin/Polymer Weight Ratio Adhesion (oz/in) N/cm Probe Tack (g) Steel PE TEFLON™ 43/57 0,55 (5)a 0,33 (3)a 0,22 (2)a 340 50/50 1,31 (12)a 0,88 (8)a 0,33 (3)a 525 56/44 2,52 (23)a 1,31 (12)a 1,09 (10)a 700 62/38 6,57 (60)a 3,06 (28)a 2,52 (23)a 1190 67/33 7,88 (72)a 6,13 (56)a 3,72 (34)a 1610 72/28 7,88 (72)c 4,38 (40)c 3,28 (30)c 50 77/23 0c 0a 0a 0 82/18 0a 0a 0a 0 87/13 0a 0a 0a 0 67/33 3,50 (32)c 3,94 (36)c 2,74 (25)a 1161 (Comparative) Example 75 (Resin O) Resin/Polymer Weight Ratio Adhesion (oz/in) N/cm Probe Tack (g) Steel PE TEFLON™ 43/57 1,42 (13)a 0,11 (1)a 0a 570 50/50 3,50 (32)a 0,55 (5)a 0,33 (3)a 480 56/44 3,94 (36)a 0,66 (6)a 0,44 (4)a 230 62/38 4,49 (41)a 0,55 (5)a 0,33 (3)a 160 67/33 3,94 (36)a 0a 0a 50 72/28 0a 0a 0a 0 77/23 0a 0a 0a 0 82/18 0a 0a 0a 0 87/13 0a 0a 0a 0 56/44 4,05 (37)a 0,66 (6)a 0,44 (4)a 260 The above results were repeated using a 25 µm (1 mil) thick KAPTON™ substrate. Table XX presents the peel adhesion results, in summary form, for the optimum resin/polymer ratio PSAs which were cured using the above described SiH crosslinker. The resin M n values reported in Table XX are based on the PS standard, as described supra. Example Resin Resin M n Resin M/Q Ratio Maximum Adhesion To TEFLON™ KAPTON™ (oz/in) N/cm MYLAR™ (oz/in) N/cm 67 H 766 1.5 0 0 68 I 958 1.4 2,41 (22) 3,28 (30) 69 J 1037 1.4 3,61 (33) 4,38 (40) 70 K 1191 1.3 4,38 (40) 6,13 (56) 71 L 1633 1.1 1,31 (12) 1,86 (17) 72 M 1832 1.0 0,77 (7) 0,66 (6) 73 N 1841 1.0 0,88 (8) 0,55 (5) 74 N-1 1463 1.0 1,97 (18) 3,72 (34) 75 O 2322 1.0 0,66 (6) 0,44 (4) The peel adhesion (Mylar™ backing) of the PSAs having optimum resin/polymer ratios and using the SiH cure system shown in the above tables are also plotted against the number average molecular weight (Ps standard) of the respective resin component in Figure 1 (polyethylene substrate) and Figure 2 (PTFE substrate). From the tables, as well as Figures 1 and 2, it can be seen that the silicone PSAs of the present invention exhibit unexpectedly high adhesion to the two low energy substrates relative to systems wherein the resin component is outside the critical M n (PS standard) of 950 to 1600 and the critical M/Q ratio of 1.1 to 1.4. It is noted that (Comparative) Example 74, which employs Resin N-1, also provided relatively good adhesion to PE and Teflon™. However, the resin used to form this PSA was only a fraction of its "as-formed" counterpart, Resin N. The PSA based on Resin N-1, which had an M/Q ratio of 1.00, is thus an illustration of the low polydispersity compositions taught in EPO 0 255 226, cited supra and is outside the scope of the present invention. And, as stated above, this EPO publication teaches away from the use of silicone resins having M/Q ratios exceeding 1.0. COMPARATIVE EXAMPLE 76 A silicone resin was prepared according to the procedure described in Example 1 of United States Patent No. 3,929,704 to Horning, cited supra, as follows. A 1,000 ml flask equipped with a condenser, thermometer and addition funnel was charged with 108 g of trimethylchlorosilane, 374 g of ethylorthosilicate and 250 g of toluene. This solution was stirred and heated to 40°C. over a ten minute period and maintained at 40°C. for an additional five minutes. Water (144 g) was then added at a rate sufficient to maintain the reaction temperature in the range 72-78°C. The resulting mixture was stirred for an additional hour and then phase separated. The resin/solvent phase was neutralized and dried with sodium bicarbonate and magnesium sulfate, respectively. After filtration through a pressure filter, the solution was found to have a solids content of 44%. This solution was partially stripped under vacuum to provide a solution containing 64 weight percent resin solids. Analysis of the above resin by ²⁹Si nmr showed the following mole percentages, wherein R denotes a methyl radical: M units (i.e., R₃SiO 1/2 ) = 40.6% M (neopentamer) units = 0.2% TOH units (i.e., HOSiO 3/2 ) = 18.5% Q units (i.e., SiO₂) = 40.8% Q (neopentamer) <0.1% Thus, according to the previously stated convention used herein, M/Q = (40.6 + 0.2)/40.8 = 1.0 Gel permeation chromatography evaluation of the above resin using the resin calibration showed a M n of 1,771, which corresponds to a M n of 905 on a polystyrene calibration (excluding the neopentamer peak). The above resin solution was employed in the preparation of various silicone pressure-sensitive adhesives; one series of PSAs was prepared using the platinum-catalyzed hydrosilation cure system according to Examples 1-4 while another series of PSAs was formulated with a peroxide cure system according to Examples 5-8. The test results on these PSAs showing adhesion to steel and polyethylene (PE) as well as tack are presented in Table XXI, wherein the first column indicates the weight ratio of resin to polymer (R/P) used. R/P Hydrosilation-Cured PSAs Adhesion (oz/in) N/cm Peroxide-Cured PSAs Adhesion (oz/in) N/cm Steel PE Tack (g) Steel PE Tack (g) 43/57 (1)c 0,11 0c 162 (8)a 0,88 (2)a 0,22 60 50/50 (1)c 0,11 (2)c 0,22 286 (10)a 1,09 (2)a 0,22 85 56/44 0a (2)a 0,22 80 (9)a 0,99 (3)a 0,33 90 62/38 (1)c 0,11 (3)c 0,33 25 (8)a 0,88 (2)a 0,22 40 67/33 0a 0a 15 (7)a 0,77 0a 0 72/28 (3)a 0,33 0c 28 (7)c 0,77 0a 0 77/23 0a 0a 25 0a 0a 0 82/18 0a 0a 50 0a 0a 0 87/13 0a 0a 75 0a 0a 0 The following examples illustrate the preparation and testing of System IV (solventless) PSAs of the present invention. A separate determination on a representative model composition indicated that the stripping conditions reported herein would result in a volatile content of less than 1% by weight. In all of these examples, the adhesion values reported are to steel panels. EXAMPLE 77 A 267 gram mixture of Resin P solution and Polymer L with a resin to polymer ratio of 72/28 based on solids, was prepared. The volatiles were removed by vacuum stripping at 130°C. and 1-2 millimeters of mercury for one hour. To 7.0 grams of the devolatilized mixture was added 0.012 grams of bis-(methoxymethyl)ethyl maleate, 0.06 grams of a platinum complex of a vinylsiloxane and the amount of Crosslinking Agent M as listed in Table XXII for each example. The compositions were cast to give a 38 to 51 µm (1.5 to 2.0 mil) cured film on 25 µm (1-mil) Kapton™. Cure was achieved by heating for six minutes at 130°C. in a laboratory convection oven. The test results are summarized in Table XXII. EXAMPLE X-LINK (gms) SiH/SiV HOLD TIME (400°F) Adhesion FINGER TACK 77A 0.07 1.5/1.0 PASS (28)a 3,06 AVG 77B 0.15 3.4/1.0 FAIL (34)a 3,72 LOW 77C 0.25 5.6/1.0 FAIL (34)a 3,72 LOW-AVG 77D 0.30 6.7/1.0 FAIL (31)a 3,39 AVG 77E 0.35 7.9/1.0 PASS (28)a 3,06 HIGH 77F 0.45 10.1/1.0 ---- (27)a 2,96 HIGH EXAMPLE 78 A 267 gram mixture of Resin P solution and Polymer L with a resin to polymer ratio of 72/28 based on solids, was prepared. The volatiles were removed by vacuum stripping at 130°C. and 133 to 266 Pa (1-2 millimeters of mercury) for one hour. To 7.0. grams of the devolatilized mixture was added 0.012 grams of bis-(methoxymethyl)ethyl maleate, 0.06 grams of a platinum complex of a vinylsiloxane and 0.30 grams of Crosslinking Agent M. The compositions were cast to give a 38 to 51 µm (1.5 to 2.0 mil) cured film on 51 µm (2-mil) Mylar™. Cure was achieved by heating for two to ten minutes at 130°C. in a laboratory convection oven. The test results are summarized in Table XXIII. Composition Cure Time Adhesion Finger Tack 78A 2 min. (47)a 5,14 HIGH 78B 4 min. (53)a 5,80 HIGH 78C 6 min. (55)a 6,02 HIGH 78D 8 min. (53)a 5,80 HIGH 78E 10 min. (53)a 5,80 AVG EXAMPLE 79 A 250 gram mixture of Resin P solution and Polymer L with a resin to polymer ratio of 70/30 based on solids, was prepared. The volatiles were removed by vacuum stripping in a 5,1 x 20,3 cm (2 X 8 inch) vertical thin film stripper at 120°C. and 60 millimeters of mercury for one hour. To 5.0 grams of the devolatilized mixture was added 0.02 grams of diethyl fumerate, 0.02 grams of a platinum complex of a vinylsiloxane and the amount and type of crosslinking agent as listed in Table XXIV for each example. The compositions were cast to give a 38 to 51 µm (1.5 to 2.0 mil) cured film on 25 µm (1-mil) Kapton™ . Cure was achieved by heating for four minutes at 130°C. in a laboratory convection oven. The test results are summarized in Table XXIV. Composition Cross Linking Agent (type) (wt%) SiH/SiVi Adhesion Finger Tack 79A A 1.5/1.0 1,64 (15)c LOW 79B A 2.0/1.0 1,53 (14)c LOW 79C G 2.0/1.0 0,77 (7)a HIGH 79D H 2.0/1.0 1,75 (16)a HIGH EXAMPLE 80 A mixture of 200 grams of the Resin P solution and 65 grams of the Polymer L was prepared. The volatiles were removed by vacuum stripping at 130°C. and 133 to 266 Pa (1-2 millimeters of mercury) for one hour. To 7.0 grams of the devolatilized mixture was added 0.012 grams of bis-(methoxymethyl)ethyl maleate, 0.06 grams of a platinum complex of a vinylsiloxane and the amount and type of crosslinking agent as listed in Table XXV for each example. Crosslinking agents F, I, J and K were used which are trimethylsiloxy terminated methylhydrogenpolysiloxane having an average degree of polymerization of between 5 and 40. Additional amounts of Polymer L were added so as to maintain a constant resin to polymer ratio while varying the SiH to SiVi ratios. The compositions were cast to give a 38 to 51 µm (1.5 to 2.0 mil) cured film on 51 µm (2-mil) Mylar™. Cure was achieved by heating for six minutes at 130°C. in a laboratory convection oven. The test results are summarized in Table XXV. EXAMPLE Cross Linking Agent (type) (gms) SiH/SiVi Adhesion FINGER TACK 80A I 0.05 1.5/1.0 (52)a 5,69 HIGH 80B I 0.10 3.0/1.0 (56)a 6,13 AVG 80C I 0.20 6.0/1.0 (55)a 6,02 AVG 80D J 0.04 1.5/1.0 (52)a 6,02 AVG-HIGH 80E J 0.08 3.0/1.0 (48)a 5,25 LOW 80F J 0.18 6.0/1.0 (46)a 5,03 LOW-NONE 80G K 0.04 1.5/1.0 (40)a 4,38 LOW 80H K 0.08 3.0/1.0 (50)a 5,47 LOW-NONE 80I K 0.15 6.0/1.0 (56)a 6,13 LOW-NONE 80J F 0.04 1.5/1.0 (52)a 5,69 AVG 80K F 0.07 3.0/1.0 (57)a 6,24 LOW 80L F 0.14 6.0/1.0 (61)a 6,68 NONE EXAMPLE 81 A 250 gram mixture of Resin P solution and Polymer L with a resin to polymer ratio of 70/30 based on solids, was prepared. The volatiles were removed by vacuum stripping in a 5,1 x 20,3 cm (2 X 8 inch) vertical thin film stripper at 120°C. and 8 kPa (60 millimeters of mercury) for one hour. To 5.0 grams of the devolatilized mixture was added 0.02 grams of diethyl fumerate, 0.02 grams of a platinum complex of a vinylsiloxane and the amount and type of crosslinking agent as listed in Table XXVI for each example. The compositions were cast to give a 38 to 51 µm (1.5 to 2.0 mil) cured film on 25 µm (1-mil) Kapton™. Cure was achieved by heating for four minutes at 130°C. in a laboratory convection oven. The test results are summarized in Table XXVI. EXAMPLE Cross Linking Agent (type) SiH/SiVi ADHESION TACK (gms) HOLD 5-DAY(°F.) 81A D 2.1/1.0 3,83 (35)a 990 400 81B D 1.8/1.0 4,49 (41)a 1100 400 81C D 1.4/1.0 3,5 (32)a 915 400 81D E 4.9/1.0 3,06 (28)a 650 400 81E E 4.1/1.0 2,85 (26)a 480 --- 81F E 3.1/1.0 2,63 (24)a 440 --- 81G E 1.5/1.0 2,96(27)a 565 --- 81H L 2.5/1.0 3,72 (34)a 775 400 81I L 1.8/1.0 3,61 (33)a 745 <400 81J L 1.1/1.0 3,94 (36)a 1110 --- EXAMPLE 82 A 250 gram mixture of Resin P solution and Polymer L with a resin to polymer ratio of 70/30 based on solids, was prepared. The volatiles were removed by vacuum stripping in a 5,1 x 20,3 cm (2 X 8 inch) vertical thin film stripper at 120°C. and 8 kPa (60 millimeters of mercury) for one hour. To 5.0 grams of the devolatilized mixture was added 0.01 grams of diethyl fumerate, 0.02 grams of benzyl alcohol, 0.01 grams of a platinum complex of a vinylsiloxane and the amount and type of cross linking agent as listed in Table XXVII for each example. The compositions were cast to give a 38 to 51 µm (1.5 to 2.0 mil) cured film on 25 µm (1-mil) Kapton™. Cure was achieved by passing the coated film five times under a pair of mercury vapor lamps, as described in Examples 26-39. EXAMPLE Cross Linking Agent (type) SiH/SiVi ADHESION TACK (gms) HOLD 5-DAY(°F.) 82A M 1.5/1.0 2,63 (24)a 240 --- 82B H 3.0/1.0 2,19 (20)a 995 400 82C L 2.5/1.0 3,5 (32)a 965 --- 82D L 1.8/1.0 4,38 (40)a 350 --- 82E D 2.1/1.0 3,94 (36)a 1110 --- 82F D 1.8/1.0 4,16 (38)a 895 400 EXAMPLE 83 A 100 gram mixture of Resin Q solution and Polymer L with a resin to polymer ratio of 83/17 based on solids, was prepared. The volatiles were removed by vacuum stripping at 130°C. and 266 Pa (2 millimeters of mercury) for two hour. To 5.0 grams of the devolatilized mixture was added 0.02 grams of diethyl fumerate, 0.02 grams of a platinum complex of a vinylsiloxane and the amount and type of crosslinking agent as listed in Table XXVIII for each example. Additional amounts of Polymer L were added to adjust the resin to polymer ratio to the levels indicated in Table XXVIII. The compositions were cast to give a 38 to 51 µm (1.5 to 2.0 mil) cured film on 25 µm (1-mil) Kapton™. Cure was achieved by heating for four minutes at 130°C. in a laboratory convection oven. The test results are summarized in Table XXVIII. EXAMPLE Cross Linking Agent (type) Resin/Polymer SiH/SiVi Adhesion TACK (gms) FINGER TACK 83A D 76/24 1.8/1.0 1,53 (14)a 890 HIGH 83B D 78/22 1.8/1.0 2,63 (24)c 925 HIGH 83C D 80/20 1.8/1.0 3,83 (35)c 990 HIGH 83D D 83/17 1.8/1.0 4,16 (38)c 535 AVG 83E M 78/22 1.8/1.0 1,75 (16)a 880 AVG-HI 83F M 80/20 1.8/1.0 2,52 (23)c 625 AVG 83G M 83/17 1.8/1.0 3,28 (30)c 50 LOW-NO EXAMPLE 84 A 250 gram mixture of Resin P solution and Polymer M with a resin to polymer ratio of 70/30 based on solids, was prepared. The volatiles were removed by vacuum stripping in a 5,1 x 20,3 cm (2 X 8 inch) vertical thin film stripper at 120°C. and 8 kPa (60 millimeters of mercury) for one hour. To 5.0 grams of the devolatilized mixture was added 0.02 grams of diethyl fumerate, 0.02 grams of a platinum complex of a vinylsiloxane and the amount of Crosslinking Agent A as listed in Table XXIX for each example. The compositions were cast to give a 38 to 51 µm (1.5 to 2.0 mil) cured film on 25 µm (1-mil) Kapton™. Cure was achieved by heating for four minutes at 130°C. in a laboratory convection oven. The test results are summarized in Table XXIX. EXAMPLE Cross Linking Agent (type) SiH/SiVi ADHESION Finger Tack 84A M 1.5/1.0 2,3 (21)a AVG 84B M 1.0/1.0 1,86 (17)a AVG

Claims: A silicone pressure sensitive adhesive composition consisting essentially of: (A) 60 to 90 parts by weight of a soluble organopolysiloxane having a M n value of 950 to 1,600, the peak of the neopentamer of formula (R₃SiO)₄Si being excluded from the measurement, and consisting essentially of R₃SiO 1/2 siloxane units and SiO 4/2 siloxane units wherein each R denotes a monovalent radical selected from the group consisting of hydrocarbon and halogenated hydrocarbon radicals, at least 1/3 of all R radicals being methyl and the mole ratio of R₃SiO 1/2 siloxane units to SiO 4/2 siloxane units in the soluble organopolysiloxane having a value of from 1.1/1 to 1.4/1, wherein the mole ratio represents the ratio of the total number of triorganosiloxy groups of the resinous and neopentamer portions of (A) to the total number of silicate groups of the resinous and neopentamer portions of (A), and wherein component (A) contains a small amount of a low molecular weight material comprised substantially of a neopentamer organopolysiloxane having the formula (R₃SiO)₄Si; and (B) 10 to 40 parts by weight of a polydiorganosiloxane having the general formula R¹R²₂SiO(R²₂SiO) n SiR²₂R¹ wherein each R² denotes a monovalent radical selected from the group consisting of hydrocarbon and halogenated hydrocarbon radicals, at least 1/2 of all R² radicals being methyl, each R¹ denotes a radical selected from the group consisting of R² radicals and OH radicals and the subscript n is a number having an average value of at least 50. The composition according to claim 1, further containing an effective amount of a nonreactive solvent. The composition of claim 1, further comprising an effective amount of a crosslinking agent. An article coated with the cured composition of claim 1. A solventless silicone pressure sensitive adhesive composition consisting essentially of: (A) 60 to 90 parts by weight of a soluble organopolysiloxane having a M n value of 950 to 1,600, the peak of the neopentamer of formula (R₃SiO)₄Si being excluded from the measurement, and consisting essentially of R₃SiO 1/2 siloxane units and SiO 4/2 siloxane units wherein each R denotes a monovalent radical selected from the group consisting of hydrocarbon and halogenated hydrocarbon radicals, at least 1/3 of all R radicals being methyl and the mole ratio of R₃SiO 1/2 siloxane units to SiO 4/2 siloxane units in the soluble organopolysiloxane having a value of from 1.1/1 to 1.4/1, wherein the mole ratio represents the ratio of the total number of triorganosiloxy groups of the resinous and neopentamer portions of (A) to the total number of silicate groups of the resinous and neopentamer portions of (A), and wherein component (A) contains a small amount of a low molecular weight material comprised substantially of a neopentamer organopolysiloxane having the formula (R₃SiO)₄Si; and (B) 10 to 40 parts by weight of a polydiorganosiloxane having the general formula R¹₂R²SiO(R¹R²SiO) n SiR²R¹₂ wherein each R¹ individually is a radical selected from the group consisting of methyl, ethyl, propyl and phenyl, each R² individually is an olefinic radical or any R¹ as defined above with the proviso that at least two R² radicals per molecule must be olefinic and n has an average value of 50 to 200; (C) an organohydrogenpolysiloxane compatible with the mixture of (A) and (B) and having an average of at least 2 silicon-bonded hydrogen atoms per molecule, the amount of (C) present in the adhesive composition being sufficient to provide from 1 to 30 silicon bonded hydrogen atoms for every olefinic radical in (B); and (D) a platinum containing catalyst in sufficient quantity to provide at least 0.1 part by weight platinum for every one million parts by weight of the combined weight of (A), (B) and (C). The composition of claim 5, further comprising a platinum catalyst inhibitor. The composition of claim 5, further comprising less than one percent by weight of a solvent. A process for preparing a solventless silicone pressure sensitive adhesive composition comprising: (I) preparing an organic solvent solution of (A) 60 to 90 parts by weight of a soluble organopolysiloxane having a M n value of 950 to 1,600, the peak of the neopentamer of formula (R₃SiO)₄Si being excluded from the measurement, and consisting essentially of Me₃SiO 1/2 siloxane units and SiO 4/2 siloxane units in a mole ratio of 1.1/1 to 1.4/1, wherein the mole ratio represents the ratio of the total number of triorganosiloxy groups of the resinous and neopentamer portions of (A) to the total number of silicate groups of the resinous and neopentamer portions of (A), and wherein component (A) contains a small amount of a low molecular weight material comprised substantially of a neopentamer organopolysiloxane having the formula (R₃SiO)₄Si, in which Me denotes a methyl radical; (B) 10 to 40 parts by weight of a polydiorganosiloxane having the general formula R²(R¹₂SiO) m SiR¹₂R² wherein R¹ is independently selected from the group consisting of methyl, ethyl, propyl and phenyl, R² is an olefinically unsaturated radical and m has an average value of 50 to 200; and (C) an organohydrogenpolysiloxane compatible with the mixture of (A) and (B) and having an average of at least 3 silicon-bonded hydrogen atoms per molecule, the amount of (C) present in the adhesive composition being sufficient to provide from 1 to 30 silicon bonded hydrogen atoms for every olefinically unsaturated radical in the total of (A) plus (B); (II) removing organic solvent from the solution to obtain a devolatilized mixture containing less than one percent by weight, based on the total weight of devolatilized mixture, of volatiles; and (III) mixing the devolatilized mixture with (D) a platinum containing catalyst in sufficient quantity to provide at least 0.1 part by weight platinum for every one million parts by weight of the combined weight of (A), (B) and (C). The process of claim 8, wherein organic solvent is added to produce a composition with less than one percent by weight of said organic solvent. A process for preparing a solventless silicone pressure sensitive adhesive composition comprising: (I) preparing an organic solvent solution of (A) 60 to 90 parts by weight of a soluble organopolysiloxane having a M n value of 950 to 1,600, the peak of the neopentamer of formula (R₃SiO)₄Si being excluded from the measurement, and consisting essentially of Me₃SiO 1/2 siloxane units and SiO 4/2 siloxane units in a mole ratio of 1.1/1 to 1.4/1, wherein the mole ratio represents the ratio of the total number of triorganosiloxy groups of the resinous and neopentamer portions of (A) to the total number of silicate groups of the resinous and neopentamer portions of (A), and wherein component (A) contains a small amount of a low molecular weight material comprised substantially of a neopentamer organopolysiloxane having the formula (R₃SiO)₄Si, in which Me denotes a methyl radical; (B) 10 to 40 parts by weight of a polydiorganosiloxane having the general formula R²(R¹₂SiO) m SiR¹₂R² wherein R¹ is independently selected from the group consisting of methyl, ethyl, propyl and phenyl, R² is an olefinically unsaturated radical and m has an average value of 50 to 200; (II) removing organic solvent from the solution to obtain a devolatilized mixture containing less than one percent of volatiles based on the total weight of devolatilized mixture; and (III) mixing the devolatilized mixture with (C) an organohydrogenpolysiloxane compatible with the mixture of (A) and (B) and having an average of at least 3 silicon-bonded hydrogen atoms per molecule, the amount of (C) present in the adhesive composition being sufficient to provide from 1 to 30 silicon bonded hydrogen atoms for every olefinically unsaturated radical in the total of (A) plus (B) and (D) a platinum containing catalyst in sufficient quantity to provide at least 0.1 part by weight platinum for every one million parts by weight of the combined weight of (A), (B) and (C). The process of claim 10, wherein organic solvent is added to produce a composition with less than one percent by weight of said organic solvent. An article having on at least one surface thereof the cured composition of claim 5. An article having on at least one surface thereof the cured composition of claim 6.

Inventors: BRADY WILLIAM PATRICK, CHUNG KYUHA, SCHMIDT RANDALL GENE, VINCENT GARY ALLAN, BRADY, WILLIAM PATRICK, CHUNG, KYUHA, SCHMIDT, RANDALL GENE, VINCENT, GARY ALLAN
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1992
Main classification: C09J183
IPC codes: C09J183, C09J7, B32B27