PROCESS FOR PREPARING A PROCATALYST COMPOSITION BY IMPREGNATION OF A CARRIER WITH A MAGNESIUM ALKOXIDE, A TITANIUM ALKOXIDE AND AN ALCOHOL SOLUTION

Abstract: The present invention concerns a process for preparing a procatalyst composition suitable for the polymerization of ethene and other (alpha)-olefins, which comprises the steps of: (a) contacting an inorganic oxide carrier, having a low content of surface hydroxyls, with an impregnation solution containing a magnesium compound, an alcohol, and a tetravalent titanium compound, (b) chlorinating the contacted inorganic oxide carrier with a chlorinating agent, and (c) recovering the chlorination product to yield the procatalyst composition. Prior similar processes have the disadvantage of using polar solvents of low volatility and titanium tetrachloride as the source of active centers. Both materials make the process more difficult and contaminate its product. These problems have now been solved in such a manner that the impregnation solution comprises a magnesium alkoxide, a titanium alkoxide and a lower alcohol.

Description: Process for preparing a procatalyst composition by impregnation of a carrier with a magnesium alkoxide, a titanium alkoxide and an alcohol solution. The invention relates to process for preparing a procatalyst composition suitable for the polymerization of ethene and other α-olefins, which comprises the steps of: a) contacting an inorganic oxide carrier, having a low con¬ tent of surface hydroxyls, with an impregnation solution containing a magnesium compound, an alcohol, and a tetrava- lent titanium compound, b) chlorinating the contacted inorganic oxide carrier with a chlorinating agent, and c) recovering the chlorination product to yield the procata¬ lyst composition. In one aspect the invention relates to a procatalyst compo- sition made by such a process and in another aspect the in¬ vention relates to the use of such a procatalyst composition for the polymerization of ethene and other α-olefins. Olefins are traditionally polymerized (i.e. homo- and copo- lymerized) by a Ziegler-Natta catalyst system, which con¬ sists of a so-called procatalyst and a so-called cocatalyst. The procatalyst is based on a compound of a transition metal belonging to any of groups IVA-VIII (Hubbard) of the perio¬ dic table of the elements and the cocatalyst is based on an organometallic compound of a metal belonging to any of groups I (A) -III (Hubbard) of the periodic table of the ele¬ ments. The catalyst system often also includes a solid pro¬ catalyst carrier as well as electron donors which improve and modify the catalytic properties of the system. The catalytic activity of the procatalyst is greatly en¬ hanced by carriers like the magnesium halides, alkoxides, hydroxides and oxides, titanium dioxide, aluminium oxide and silica. In the case of silica, the carrier is usually first treated thermically and/or chemically to remove at least a part of its surface hydroxyl groups. Then the pretreated solid carrier is often treated with one or more liquids which contain a surface modifying magnesium compound, an electron donor/solvent like tetrahydrofuran or butanol, a titanium compound, and, finally, a chlorinating agent. Such procatalysts and their preparation processes are dis- closed, among others, in FI patents 70417, 70418 and 78113, FI applications 895703 and 896323, EP publications 117929, 173102, 173471, 173485, 173488 and 185521, and US patent publications 4 855 271, 4 876 229, 4 833 111 and 4 888 318. US-4 833 111 discloses a process for preparing a procata¬ lyst, wherein calcined silica is treated with a solution of a dialkyl magnesium in a hydrocarbon, then treated with EtOH, then with TiCl 4 , and finally with ethylaluminium di- chloride before recovering the product. US 4 855 271 discloses a process for preparing a procatalyst by impregnating a calcined alumina carrier with a solution of magnesium dichloride and titanium tetraethoxide in an alcohol (example VI) . After evaporation of the alcohol, the resulting solid was treated with titanium tetrachloride, and recovered as a highly active procatalyst. EP-application 173 471 discloses the treatment of dehydrated silica in isopentane with a solution of butylethyl magnesium and butanol in hexane. Then the mixture was treated with titanium tetrachloride, chlorine gas and trialkyl aluminium before drying to yield the expected procatalyst. As a separ¬ ate trialkyl aluminium compound was added just before poly¬ merization, the above mentioned trialkyl aluminium was not acting as a cocatalyst. FI application 896 323 discloses a process for preparing a procatalyst by impregnating silica, dried at 120-800°C and dehydrated with hexamethyl disilazane, with an impregnating solution comprising a mixture of triethyl aluminium in pen- tane, butanol and butyloctyl magnesium in heptane. The alu¬ minium compound, the magnesium compound and the alcohol for- med a bimetallic compound to be impregnated. Treatment with titanium tetrabutoxide was performed either by a subsequent contacting step or by including it in advance into the im¬ pregnation solution. After a drying step the composition was chlorinated with ethylaluminium sesquichloride or ethylalu- minium dichloride to yield the procatalyst. The above processes have either the disadvantage of using large amounts of polar liquids in the impregnation sol¬ ution, like tetrahydrofuran and alcohols, or the disadvan- tage of using titanium tetrachloride as the titanium source of catalytic activity, or both. When polar solvents like tetrahydrofuran and alcohols are used as the major solvent, the drying procedure is often long and tedious. It is especially difficult to remove the last traces of polar solvent. The remaining amounts of polar solvent inside the procatalyst has a clearly negative effect on the activity and performance of the procatalyst. Titanium tetrachloride has, when used, as a titanium source in the prior art, led to a large fraction of inactive ti¬ tanium, which remains in the polymer as a harmful impurity. Further, titanium tetrachloride has the disadvantage, that it does not easily form an impregnation solution together with a magnesium compound and an alcohol, which limits its use as the sole titanium source. The purpose of the present invention is to provide a pro- cess, in which non-polar and volatile solvents can be used at the various impregnating stages of the above procatalyst preparation. The aim is also to avoid the use of titanium tetrachloride as the initial source of titanium in the pro- catalyst. Further, a process is strived for, wherein the procatalyst composition comprising magnesium and titanium o a carrier can be prepared more conveniently than before using a novel technique of contacting the various active components with each other and the carrier. The above purposes of the present invention have now been achieved by providing a process for preparing a procatalyst composition, which is mainly characterized by what is said in the characterizing part of claim l. It has thus been re¬ alized, that a better procatalyst and a more convenient pro¬ cess for preparing it can be achieved, when the solid, an¬ hydrous silica carrier is treated with only one impregnatio solution, which comprises both a magnesium alkoxide, a tita- nium alkoxide and a lower alcohol. Although the magnesium alkoxide, the titanium alkoxide and the lower alcohol can act alone as an impregnation solution, which still has the advantages of homogenously combining th magnesium and titanium components, it is preferable to use hydrocarbon solvent as the medium of the impregnation sol¬ ution. The combination of a magnesium alkoxide, a titanium alkoxide and a lower alcohol has the property of being soluble in hydrocarbons, although e.g. some magnesium alkoxides of the combination are alone insoluble in them. A suitable hydrocarbon solvent has about 4 to 10 carbons in its molecules, like pentane, hexane and/or heptane. As was said above, the use of titanium tetrachloride has some disadvantages, and therefore it is preferable, if es¬ sentially all titanium used as starting material in the pro¬ cess is in the form of titanium alkoxide. It is also conve¬ nient, if essentially all of the magnesium used in the pro¬ cess of the invention is in the form of magnesium alkoxide. In some prior works, titanium alkoxides have been used as process modifying additives (e.g. US 4 855 271) , which of course is not their main purpose in the present invention. In an embodiment of the invention the magnesium alkoxide is represented by the formula (I) g(OR) 2 (I) wherein the groups R can be different or similar alkyl groups, preferably C 2 -C 5 alkyl groups, like magnesium-di-n- propoxide. The titanium alkoxide can e.g. be a partial alkoxide of tet- ravalent titanium, but is rather a titanium tetraalkoxide represented by the formula (II) Ti(0R 1 ) 4 (II) wherein the groups R 1 can be different or similar C 2 -C 8 alkyl groups, preferably C 2 -C 5 alkyl groups and most preferably C 3 or C 4 groups, like titanium tetrabutoxide. The lower alcohol used as a compound in the impregnation solution of the process can be any lower alcohol, that is, mono-, di- or polyhydroxy alcohol, primary, secondary or tertiary alcohol, etc., as long as it forms together with the other components an essentially stable, homogenous and non-viscous solution. The alcohol is preferably a lower mo- nohydroxy alcohol of the following formula (III) R 2 OH (III) wherein R 2 is a C 2 -C 8 alkyl group, most preferably a C 2 -C 5 alkyl group like 1-butanol. According to one embodiment of the present invention the impregnation solution is made by mixing together and op- tionally heating the magnesium alkoxide, the titanium alko¬ xide, the alcohol, and, preferably, the hydrocarbon solvent. The result is a stable, clear and essentially uncolored solution of low viscosity, which easily penetrates the sur¬ face pores of the carrier during impregnation. The molar ratio in the impregnation solution, and in the above mixing, between the magnesium alkoxide and the ti¬ tanium alkoxide, conveniently exceeds 2.5 and is preferably between 2.5 and 4. The corresponding molar ratio between the alcohol and the titanium alkoxide is readily larger than or equal to 1 and preferably between 1.5 and 3. The equivalent molar ratio between the magnesium alkoxide and the alcohol is preferably between 1 and 3, and most preferably between 1 and 2. According to another embodiment of the present invention, the impregnation solution comprising the magnesium alkoxide, the titanium alkoxide, the alcohol, and, preferably, the hydrocarbon solvent, is made in situ. In that connection a magnesium alkyl or a magnesium alkoxy alkyl is e.g. dis¬ solved in a hydrocarbon and then mixed with the alcohol and the titanium alkoxide. Then the mixture is reacted or allo¬ wed to react, whereby the magnesium alkyl or magnesium alko¬ xy alkyl are essentially converted to the desired magnesium alkoxide component of the impregnation solution. Of the ad¬ ded chemicals titanium alkoxide, hydrocarbon, alcohol and magnesium alkyl or magnesium alkoxy alkyl, it is crucial that the magnesium alkyl (or alkoxy alkyl) or the titanium alkoxide is added last. This is to avoid reduction of Ti(IV) species to Ti(III) species and to form a solution of low viscosity. When the impregnation solution is prepared this way in situ, the preferred molar ratio between the alcohol added and the titanium alkoxide added is conveniently larger than or equal to 1 and preferably between 3 and 9. The corresponding pre- ferred molar ratio between the magnesium alkyl or magnesium alkoxy alkyl and the alcohol is between 0.25 and 1, prefer¬ ably between about 0.4 and about 0,8. It must be recognized that the amount of alcohol added depends on whether magne- sium alkyl or magnesium alkoxy alkyl is being used. When magnesium alkoxy alkyl is used, the amount of added alcohol preferably lies between that given for the in situ prepara¬ tion and that given for the mixing preparation of the im- pregnation solution. The alcohol cannot usually be added last when mixing the ingredients. The magnesium alkyl or magnesium alkoxy alkyl used as start¬ ing material in the in situ preparation of the impregnation solution can, in principle be any conventional magnesium alkyl or magnesium alkoxy alkyl. It is suitable, if the al¬ kyl groups is a C 2 -C 8 alkyl. When mixing the ingredients, the magnesium alkyl or alkoxy alkyl is preferably added last. The inorganic oxide carrier used as a carrier in the process of the invention has to be dry and have a low content of surface hydroxyls. As commercial products usually have their surface hydroxyls preserved, they must generally be removed in connection with the process of the present invention. The removal takes place either by a thermal process or a chemi¬ cal process. The thermal and chemical processes can also be combined. Typical inorganic oxide carries are silica, alumi¬ na, their mixed oxides, and other mixed silicates. A preferable inorganic oxide is silicium oxide, i.e. silica. The thermal treatment of silica is by lower temperatures directed to removal of water and by higher temperatures to removal of the surface hydroxyls by calcination. The thermal treatment is preferably carried out at temperatures of about 130-1000°C. According to one embodiment of the invention, silica is first dried at a temperature of about 135-250°C in order to remove physically adsorbed water. Then, silica may be calcinated at higher temperatures in order to remove its hydroxyl groups. This method is especially used at 600- 1000°C if the silica is not chemically treated prior to reaction with the impregnation solution. The silica pre- treated by calcinating for several hours at such high tempe¬ rature contains essentially no surface hydroxyls. The chemical removal of surface hydroxyl groups of the sili¬ ca carrier can also be conducted by using materials reacting with hydroxyl groups. Such materials include organic sili¬ con, aluminium, zinc, phosporous and/or fluorine compounds. Convenient hydroxyl removing agents are hexamethyl disilaza- ne, triethyl aluminium, diethyl aluminium chloride, ethyl- aluminium dichloride and diethyl zinc. The dried silica is typically reacted with the hydroxyl re- moving agent in a hydrocarbon slurry in order to convert the silica hydroxyls to oxygen bridges between the silica and the removing agent and preferably form a non-reducing surfa¬ ce on the silica carrier. Before the thus pretreated silica is fed further to the impregnation step of the process, the hydrocarbon solvent can optionally be removed together with any excess of hydroxyl removing agent. Measures like those mentioned can also be used for the removal of surface hydro¬ xyls from other inorganic oxides than silica. In the impregnation step, the impregnation solution de¬ scribed above is contacted with the pretreated silica or a hydrocarbon slurry thereof and allowed to react over a suit¬ able time. It is possible to remove the hydrocarbon solvent together with any impregnation reaction by-products if this should be considered feasible. The impregnation and chlorination step can be performed in any order. It is preferable, if in the chlorination step, the already impregnated carrier is reacted with chlorinating agent in order to establish an advantageous structure and balance between the elements on the carrier surface. The used agent is generally chlorine or a compound thereof with an element of groups III-V of the table of the elements. Typical chlorinating agents are chlorine, boron trichloride, ethylaluminium dichloride, diethyl aluminiumchloride, ethylaluminium sesquichloride, silicon tetrachloride and phosphorus trichloride. The most preferred agents are the alkyl aluminium chlorides, especially ethylaluminium dichloride. In the present invention, essentially all of the aluminium used in the preparation of the procatalyst composition, at least in its impregnation and chlorination steps, is pre¬ ferably in the form of an alkyl aluminium chloride. The chlorinating agent can be added as a mixture with a hydro¬ carbon liquid. After the chlorination treatment, any solvent is removed together with any reaction by-products and the product is recovered as a catalytically active procatalyst with good morphology. The invention also concerns a novel procatalyst, suitable for the polymerization of ethene and other α-olefins, which has been prepared by a process essentially like that de¬ scribed above. The invention also relates to a method for the polymerization of ethene and other α-olefins. The poly- merization is carried out by means of a procatalyst, prepa¬ red essentically by the above described process, and an or¬ ganic cocatalyst compound of a metal belonging to the groups I(A) -III (Hubbard) of the periodic table of the elements and optionally in the presence of a molar mass regulating agent such as hydrogen and at least one electron donor. The following examples merely illustrate the present inven¬ tion. Experimental part All experiments are performed under an inert atmosphere of dried and deoxygenized nitrogen or argon. All chemicals are dried and flushed with nitrogen or argon to remove oxygen prior to use. Polymerization procedure I. A 3 L reactor was purged with an inert gasflow (nitrogen or argon) and it was charged with 1.8 L of isobutane. To this a 20 % solution of triethyl aluminium in pentane was added as cocatalyst from a feeding funnel followed by 20-50 mg of procatalyst as a slurry in 20 mL of n-pentane with mixing from a to 8 bars pressurized feeding funnel. The tem¬ perature was thereafter raised to 95°C and was kept there during the whole polymerization process. A 500 mL vessel was pressurized with hydrogen to a pressure of 6.2 bars. Hydrogen and ethylene gas were fed into the reactor. The total pressure was raised to 27 bars and was kept there by a continuous feed of ethylene gas. The poly¬ merization was continued for 1 h. After 1 h the reactor was cooled and the pressure was slowly released in order to evaporate the isobutane. II. The copolymerization of ethylene and α-olefins was per¬ formed according to step I above. The reactor was charged with 1.8 L of isobutane, cocatalyst (triethylaluminum) was then added before the addition of the catalyst. Comonomer was added as a mixture together with the ethylene feed. Preparation of the solution A. Solution made from solid magnesium alkoxide 0.214 g of magnesium-di-n-propoxide was charged in a 10 mL sealed bottle equipped with a magnetic stirrer, together with 0.171 mL neat titaniumtetrabutoxide and 0.320 mL neat 1-butanol. 2.0 mL of pentane was added and the formed slurry was heated for 1 h to form a solution of low viscosity. B. Solution made from in situ synthesized magnesium alko¬ xide made from magnesium alkyl and alcohol 2.0 mL pentane is charged in a 30 mL sealed bottle equipped with a magnetic stirrer, together with 0.171 mL neat tita- niumtetrabutoxide and 0,320 mL neat 1-butanol. The mixture is kept well stirred at a temperature between 5-20°C while 1.714 mL of butyl octyl magnesium, 20 % in heptane (Schering A.G.) is added over 15 min. The solution obtained was a clear uncolored liquid of low viscosity. Preparation of catalysts Example 1 1.0 g of silica (Crosfield, grade EP 17, dried at 200°C) was charged into a 30 mL sealed bottle equipped with a magnetic stirrer. 1.83 mL of ethylaluminum dichloride, 20 % in pen¬ tane, was added together with 4.5 mL pentane at room tem¬ perature. The slurry was mixed at the same temperature for 3 h. The solution from (B) was then added at room temperature over a 10 min period and kept with continuous stirring for 1 h. A 0.91 mL aliquot of ethylaluminum dichloride, 20 % in pentane, was added to the slurry at room temperature and was stirred at 50°C for 1 h. The temperature was raised slowly to 85°C, with an argon gas flow through the flask, to evap- orate the solvent leaving a dry material. Elemental analysis of the catalyst is described in table 3. The catalyst was polymerized, table 1 and 2 for the test data. Example 2 4.0 g of silica (Crosfield, grade EP 17, dried at 130°C) was charged into a 60 mL sealed bottle equipped with a magnetic stirrer. 4.5 mL of ethylaluminum dichloride, 20 % in penta¬ ne, was added together with 12 mL pentane at room tempera¬ ture. The slurry was mixed at the same temperature for 1 h. 4 times the amount of the solution from (A) was then added at room temperature over a 10 min period and kept with con¬ tinuous stirring for 2 h. A 9.14 mL aliquot of ethylaluminu dichloride, 20 % in pentane, was added to the slurry at roo temperature and was stirred at 40°C for 2 h. The temperature was raised slowly to 85°C, with an argon gas flow through the flask, to evaporate the solvent leaving a dry material. Elemental analysis of the catalyst is described in table 3. The catalyst was polymerized, table 1 for the test data. Example 3 1.88 g of hexamethyl disilazane was added with stirring at room temperature to a slurry of 10.0 g silica (W.R. Grace & Co., Davison Grade 955, dehydrated and calcinated with a peak temperature at 600°C) in 80 mL of pentane. The slurry was kept stirring at a temperature of 90°C for 1 h, and the solvent was then removed by purging with a stream of nitro¬ gen for 2.5 h and by raising the temperature during this time in stages to 110°C. The obtained product was a dry free-flowing white powder. 2.0 g of the hexamethyl disilazane treated silica was charged, together with 5.5 mL pentane, into a 50 mL sealed bottle equipped with a magnetic stirrer. 2 times the amount of the solution from (B) was then added at room temperature. 5.5 mL of ethylaluminum dichloride, 20 % in pentane, was added to the slurry at 2°C over a period of 25 min with sub¬ sequent stirring at 50°C for 1 h. The temperature was then raised slowly to 100°C, with an argon gas flow through the flask, to evaporate the solvent leaving a dry material. El¬ emental analysis of the catalyst is described in table 3. The catalyst was polymerized, table 1 for the test data. Example 4 3.0 g of silica (Crosfield, grade EP 17) was charged into a 50 mL sealed bottle equipped with a magnetic stirrer. 4.12 mL of ethylaluminum dichloride, 20 % in pentane, was added together with 12 mL pentane at room temperature. The slurry was mixed at the same temperature for 1 h. 3 times the amount of the solution from (A) was then added at room tem¬ perature over a 10 min period and kept with continuous stir¬ ring for 15 min. The solvent was then removed by evaporation at 40-85°C, thus forming a solid particulate material. 12 mL pentane was added after which 6.86 mL of ethylaluminum di¬ chloride, 20 % in pentane, was added to the slurry at room temperature and was stirred at 50°C for 2 h. The temperature was raised slowly to 85°C, with an argon gas flow through the flask, to evaporate the solvent leaving a dry material. Elemental analysis of the catalyst is described in table 3. The catalyst was polymerized, table 1 for the test data. Table 1 Test polymerization results according to method (I) , homo- polymerization Table 2 Comonomer test polymerization according to (II) Table 3 Elemental analysis of catalysts The test data show a polymer product of good morphology and rheology and a satisfyingly low content of titanium. The activity of the procatalyst prepared by the present inven¬ tion is quite satisfying.

Claims: Claims 1. Process for preparing a procatalyst composition suit¬ able for the polymerization of ethene and other α-olefins, which comprises the steps of: a) contacting an inorganic oxide carrier, having a low con¬ tent of surface hydroxyls, with an impregnation solution containing a magnesium compound, an alcohol, and a tetra- valent titanium compound, b) chlorinating the inorganic oxide carrier with a chlori¬ nating agent, the steps a) and b) being performed in any order, and c) recovering the contacted and chlorinated product to yield the procatalyst, characterized in that the impregnation solution comprises a magnesium alkoxide, a titanium alkoxide and a lower alcohol. 2. A process according to claim 1, characterized in that the carrier is an inorganic oxide, from which the surface hydroxyls has been essentially removed thermically and/or chemically. 3. A process according to claim 2, characterized in that the inorganic oxide is silica. 4. A process according to claim 1, 2 or 3, characterized in that the inorganic oxide carrier is dehydrated and cal¬ cinated silica, which for the removal at the surface hydroxyls has been reacted with a convenient silicium com- pound like hexamethyl disilazane, or a convenient aluminium compound, like a trialkyl aluminium, or a chlorinated alu¬ minium alkyl. 5. A process according to any preceding claim, characteri- zed in that the impregnation solution also comprises a hyd¬ rocarbon solvent, preferably a C 4 -C 10 hydrocarbon solvent. 6. A process according to any preceding claim, characteri¬ zed in that essentially all of the titanium used therein is in the form of titanium alkoxide. 7. A process according to any preceding claim, character¬ ized in that essentially all of the magnesium used therein is in the form of magnesium alkoxide. 8. A process according to any preceding claim, character- ized in that the magnesium alkoxide is represented by the formula Mg(0R) 2 wherein R is a C 2 -C 8 alkyl group, preferably a C 2 -C 5 alkyl group, or any mixture of such alkyl groups. 9. A process according to any preceding claim, character¬ ized in that the titanium alkoxide is represented by the formula Ti(0R 1 ) 4 wherein R 1 is a C 2 -C 8 alkyl group, preferably C 2 -C 5 alkyl group, most preferably a C 3 or C 4 alkyl group, or any mixture of such alkyl groups. 10. A process according to any preceding claim, character¬ ized in that the lower alcohol is represented by the formula R 2 0H wherein R 2 is a C 1 -C 8 alkyl group, preferably a C 2 -C 5 alkyl group. 11. A process according to any of claims 5 to 10, charac¬ terized in that the impregnation solution is made by mixing together and heating the magnesium alkoxide, the titanium alkoxide, the lower alcohol and the hydrocarbon. 12. A process according to any preceding claim, characte¬ rized in that the molar ratio in the impregnation solution between the magnesium alkoxide and the titanium alkoxide exceeds 2.5 and is preferably between 2.5 and 4. 13. A process according to any preceding claim, character¬ ized in that the molar ratio in the impregnation solution between the lower alcohol and the titanium alkoxide is larger than or equal to 1 and preferably between 1.5 and 3. 14. A process according to any preceding claim, character¬ ized in that the molar ratio in the impregnation solution between the magnesium alkoxide and the lower alcohol is be¬ tween 1 and 3, preferably between 1 and 2. 15. A process according to any of claims 1-10 and 12-14, characterized in that the impregnation solution is made in situ by mixing together a magnesium alkyl or magnesium alko¬ xy alkyl, dissolved in a hydrocarbon, with the titanium al- koxide and the lower alcohol, and allowing the magnesium alkyl or magnesium alkoxy alkyl to be essentially converted to said magnesium alkoxide. 16. A process according to claim 15, characterized in that the molar ratio between the lower alcohol and the titanium alkoxide is larger than or equal to 1 and preferably between 3 and 9. 17. A process according to claim 15 or 16, characterized in that the molar ratio between the magnesium alkyl or mag¬ nesium alkoxy alkyl and lower the alcohol is between 0.25 and 1, preferably between 0.4 and 0.8. 18. A process according to any of claims 15-17, character- ized in that the alkyl of the magnesium alkyl or magnesium alkoxy alkyl is a C 2 -C 8 alkyl. 19. A process according to any preceding claim, character¬ ized in that the chlorinating agent is an alkyl aluminium chloride, preferably ethylaluminium dichloride. 20. A process according to claim 19, characterized in that essentially all of the aluminium used therein is in the form of alkyl aluminium chloride. 21. A procatalyst composition, suitable for the polymeri- zation of ethene and other α-olefins, characterized in that it has been prepared by a process essentially according to any of claims 1-20. 22. Method for the polymerization of ethene and other α- olefins, characterized in that the polymerization is carried out by means of a procatalyst' composition according to claim 21 or a procatalyst composition prepared essentially by the process according to any of claims 1-20 and an organic coca¬ talyst compound of a metal belonging to the groups IA-IIIA of the periodic table of the elements and optionally in the presence of a molar mass regulator and/or at least one electron donor.

Inventors: ANDELL OVE, ANDELL, OVE
Applicants: ANDELL OVE, NESTE OY
Application year: 1992
Main classification: C08F4
IPC codes: C08F4, C08F10, C08F210