Process for preparing borane derived catalysts for preparation of syndiotactic vinyl aromatic polymers

Abstract: A catalyst corresponding to the formula L m MX n + RBY 3 - (wherein L is a delocalized π-bonding group containing up to 50 nonhydrogen atoms; m is 0 or 1; M is a metal of Group 4 of the Periodic Table; X each occurrence is an inert, anionic ligand containing up to 20 nonhydrogen atoms; n is an integer greater than or equal to 1 and the sum of m and n is one less than the valence of M; R is hydrocarbyl, silyl, a combination thereof or a substituted derivative thereof having up to 20 nonhydrogen atoms; B is boron; and Y is an inert covalently bound group having up to 40 atoms and BY 3 is a stable borane compound able to abstract an R group from a compound of the formula L m MX n R) is prepared by contacting a Group 4 metal containing compound L m MX n+1 with a borane compound BY 3 in the presence of an aluminum compound AlR 3 .

Description: The present invention relates to the preparation of alkylalumoxane-free catalyst compositions by abstraction of a leaving group from inert Group 4 metal compounds with a borane. In EP-A-277,004 there are disclosed certain bis(cyclopentadienyl) metal compounds formed by reacting a bis(cyclopentadienyl) metal complex with salts of Bronsted acids containing a non-coordinating compatible anion. The reference discloses the fact that such complexes are usefully employed as catalysts in the polymerization of olefins. In J. Am. Ch. Soc. 113, 3623-3625 (1991) there is disclosed a process for preparation of "cation like" zirconocene polymerization complexes by alkyl abstraction using tris(pentafluorophenyl)borane. The complexes were stated to have olefin polymerization activity roughly comparable to typical zirconocene/alumoxane complexes. According to the present invention there is now provided a process for preparing a metal complex corresponding to the formula I: L m MX n + RBY 3 - wherein: L is a delocalized π-bonding group or substituted group containing up to 50 nonhydrogen atoms; m is 0 or 1; M is a metal of Group 4 of the Periodic Table; X each occurrence is an inert, anionic ligand containing up to 20 nonhydrogen atoms; n is an integer greater than or equal to 1 and the sum of m and n is one less than the valence of M; R is hydrocarbyl, silyl, a combination thereof or a substituted derivative thereof having up to 20 nonhydrogen atoms; B is boron; and Y is an inert covalently bound group having up to 40 atoms and BY 3 is a stable borane compound able to abstract an R group from a compound of the formula L m MX n R, the steps of the process comprising contacting a Group 4 metal containing compound of the formula: L m MX n+1 wherein L, M, X, m and n are as defined above, with a borane compound of the formula: BY 3 wherein B and Y are as defined above, in the presence of an aluminum compound of the formula: AlR 3 wherein R is defined above, in an inert diluent at a temperature from -100°C to 100°C to cause abstraction of at least one R group from the aluminum compound and assimilation thereof in the resulting borane containing complex. The preceding formula I is referred to as the limiting, charge separated structure. However, it is to be understood that, particularly in solid form, the catalyst may not be fully charge separated. That is, the R group may retain a partial covalent bond to the metal atom, M. Thus, the catalysts may be alternately depicted as possessing the formula: L m MX n ····R····BY 3 . The metal complex of formula I is useful for preparing vinyl aromatic monomers having a high degree of syndiotacticity as described in EP-A-0597961 (WO 93/03067). The term "substituted" when used with reference to L or R means inert substituent groups, including such groups as aralkyl, alkaryl, haloalkyl, silylalkyl, haloalkyl, haloaryl, haloalkaryl, halosilyl, haloalkarylsilyl, and alkoxyalkyl. The term "inert" means noninterfering with the desired catalyst preparation or with the use of the resulting metal complex containing compound as a polymerization catalyst. All reference to the Periodic Table of the Elements herein shall refer to the Periodic Table of the Elements, published and copyrighted by CRC Press, Inc., 1989. Also, any reference to a Group or Series shall be to the Group or Series as reflected in this Periodic Table of the Elements, utilizing the IUPAC system for numbering groups. Preferred compositions according to the present invention are those wherein m is 1, n is 2, and L is a cyclopentadienyl or substituted cyclopentadienyl group. Examples of cyclopentadienyl and substituted cyclopentadienyl groups for use according to the present invention are groups depicted by the formula: wherein: R' each occurrence is independently selected from hydrogen, halogen, R, NR 2 , PR 2 ; OR; SR or BR 2 , wherein R is as previously defined. Preferably, R' is alkyl or haloalkyl of up to 6 carbons. Preferred delocalized π-bonding groups are cyclopentadiene and substituted cyclopentadiene, especially pentamethylcyclopentadiene. Most preferably M is titanium. Illustrative but nonlimiting examples of X include R, halo, NR 2 , PR 2 , OR, SR, and BR 2 . Preferably X each occurrence is R, NR 2 or OR. Illustrative, examples of suitable metal derivative compounds include: tetranorborene titanium, tetrabenzyl zirconium, tetraneopentyl titanium, (cyclopentadienyl)dimethyl(isopropoxy)titanium, (cyclopentadienyl)dibenzyl(isopropoxy)titanium, (cyclopentadienyl)dibenzyl(phenoxy)zirconium, (cyclopentadienyl)dibenzyl(isopropoxy)hafnium, (cyclopentadienyl)dimethylzirconium chloride, bis(phenoxy)di(trimethylsilyl)zirconium, phenoxytrimethylzirconium, bis(2,6-diisopropyl-4-methyl)phenoxy)dibenzyltitanium, bis(2,4,6-trimethylphenoxy)dibenzyltitanium, tri(tertiarybutyl)siloxytrimethyl zirconium, bismethoxydi(phenylmethyl)titanium, bis(2,4,6-trimethylphenoxy)dibenzyltitanium, triphenoxybenzyltitanium, butoxytris((trimethylsilyl)methyl)zirconium, dimethoxydimethylzirconium, 4-(1-methyl-1-(4-methoxyphenyl)ethyl)phenoxy tribenzyl titanium, dinorborene dichlorotitanium, tribenzyltitanium hydride, cyclopentadienyltribenzylzirconium, cyclopentadienyltribenzyltitanium, cyclopentadienyltrimethyltitanium, cyclopentadienyltrimethylzirconium, cyclopentadienyltrineopentyltitanium, cyclopentadienyltri(diphenylmethyl)zirconium, cyclopentadienyltriphenylzirconium, cyclopentadienyltrineopentylzirconium, cyclopentadienyltri(m-tolyl)zirconium, cyclopentadienyltri(p-tolyl)zirconium, cyclopentadienyldimethyltitanium hydride, cyclopentadienyltri(diphenylmethyl)zirconium, pentamethylcyclopentadienyltrimethylzirconium, ethylcyclopentadienyltrimethylzirconium, pentamethylcyclopentadienyltribenzylzirconium, n-butylcyclopentadienyltrineopentyltitanium, (t-butylcyclopentadienyl)tri(trimethylsilyl)zirconium, cyclohexylcyclopentadienyltrimethylzirconium, (pentamethylcyclopentadienyl)dimethylzirconium chloride, indenyldibenzyltitanium chloride, (pentamethylcyclopentadienyl)diisopropoxy hafnium chloride, (benzylcyclopentadienyl)di(m-tolyl) titanium chloride, (diphenylcyclopentadienyl)dinorborneylzirconium chloride, pentamethylcyclopentadienyltriphenylzirconium, tetraethylcyclopentadienyltribenzylzirconium, propylcyclopentadienyltrimethylzirconium, (n-butylcyclopentadienyl)dimethyl(n-butoxy)titanium, cyclopentadienyldiphenylisopropoxyzirconium, cyclohexylmethylcyclopentadienyltribenzylzirconium, cyclohexylmethylcyclopentadienyltrimethylzirconium, cyclopentadienylmethylzirconium dihydride, benzylcyclopentadienyltrimethylhafnium, indenyltribenzylzirconium, trimethylsilylcyclopentadienyltrimethylzirconium, trimethylgermylcyclopentadienyl)trimethyltitanium, trimethylstannylcyclopentadienyltribenzylzirconium, (pentatrimethylsilyl)cyclopentadienyltrimethylzirconium, trimethylsilylcyclopentadienyltrimethylzirconium, penta(trimethylsilyl)cyclopentadienyltribenzyltitanium, trimethylgermylcyclopentadienyltriphenylhafnium, trifluoromethylcyclopentadienyltrimethylzirconium, trifluoromethylcyclopentadienyltrinorborneylzirconium, trifluoromethylcyclopentadienyltribenzylzirconium, cyclopentadienyltrimethylsilylzirconium, and cyclopentadienyltri(phenyldimethylsilyl)zirconium. Other compounds which are useful in the catalyst compositions of this invention will, of course, be apparent to those skilled in the art. Suitable borane compounds for use herein particularly include tris(fluoroaryl) and tris (trifluoromethyl substituted aryl) borane compounds, or other suitable inertly substituted borane compounds. Examples include tris(pentafluorophenyl)borane, tris(2,3,5,6-tetrafluorophenyl)borane, and tris(3,5-di(trifluoromethyl)phenyl)borane. Especially preferred are perfluorinated compounds such as tris(pentafluorophenyl)borane. In general, the catalyst is prepared by combining the metal compound, borane compound and AlR 3 in a suitable solvent at a temperature within the range from -100°C to 100°C, preferably 0 to 50°C. The presence of residual aluminum containing species in the catalyst system is not detrimental to catalyst performance. The catalyst system can also form in situ if the components thereof are added directly to the polymerization process and a suitable solvent or diluent, including condensed monomer, is used in said polymerization process. It is, however, preferred to form the catalyst in a separate step in a suitable solvent prior to adding the same to the polymerization step. The catalysts' components are generally sensitive to both moisture and oxygen and should be handled and transferred in an inert atmosphere such as nitrogen, argon or helium. It is believed that a transfer of one or more R groups to the metal compound first occurs. Upon interacting with the borane compound, one of the R groups is then abstracted by the borane to form the ultimate catalytic species. Thus by this technique the metal compound initially utilized may be a metal alkoxide or similar compound which by itself would not be suitable for use in combination with the borane. As previously indicated, the improved catalyst of the present invention will, preferably, be prepared in a suitable solvent or diluent. Suitable solvents or diluents include any of the solvents known in the prior art including straight and branched-chain hydrocarbons such as C 6-12 alkanes (hexane, heptane and octane); C 6-12 cyclic and alicyclic, aliphatic hydrocarbons such as cyclohexane, cycloheptane, methylcyclohexane, and methylcycloheptane; C 6-12 aromatic and alkyl-substituted aromatic compounds such as benzene, toluene, xylene and decalin; and mixtures thereof. In general, catalysts according to the present invention can be selected so as to produce polymer products that will be free of certain trace metals generally found in polymers produced with Ziegler-Natta type catalysts containing cocatalysts such as aluminum or magnesium based compounds. In the practice of the present invention, vinyl aromatic monomers can be polymerized in the presence of the catalyst as mentioned above. Suitable vinyl aromatic monomers which can be polymerized in the process of the present invention include those represented by the formula: wherein each R is independently hydrogen; an aliphatic, cycloaliphatic or aromatic hydrocarbon group having from 1 to 10, more suitably from 1 to 6, most suitably from 1 to 4, carbon atoms; or a halogen atom. Examples of such monomers include, styrene, chlorostyrene, n-butyl styrene, and p-vinyl toluene with styrene being especially suitable. Copolymers of styrene and the above vinyl aromatic monomers other than styrene can also be prepared. The polymerization may be conducted under slurry, bulk or suspension polymerization conditions or other suitable reaction conditions including solid, powdered reaction conditions. The polymerization can be conducted at temperatures of from 0°C to 160°C, preferably from 25°C to 100°C, more preferably from 30°C to 80°C, for a time sufficient to produce the desired polymer. Typical reaction times are from one minute to 100 hours, preferably from 1 to 10 hours. The optimum reaction time or reactor residence time will vary depending upon the temperature, solvent and other reaction conditions employed. The polymerization can be conducted at subatmospheric pressure as well as superatmospheric pressure, suitably at a pressure within the range of 1 to 500 psig (110 kPa-3.5 MPa). The use of ambient or low pressures, for example, 1-5 psig (110-135 kPa) is preferred in view of lower capital and equipment costs. The polymerization may be conducted in the presence of an inert diluent or solvent or in the absence thereof. In the latter event excess monomer serves as a diluent. Examples of suitable, nonreactive diluents or solvents include C 6-20 aliphatic, cycloaliphatic, aromatic and halogenated aliphatic or aromatic hydrocarbons, as well as mixtures thereof. Preferred nonreactive diluents comprise the C 6-10 alkanes, toluene and mixtures thereof. A particularly desirable diluent for the polymerization is iso-octane, iso-nonane or blends thereof such as Isopar-E®, available from Exxon Chemical Company. Suitable amounts of solvent are employed to provide a monomer concentration from 5 percent to 100 percent by weight. The molar ratio of the vinyl aromatic monomer to the catalyst (in terms of metal) may range from 100:1 to 1,000,000:1, preferably from 3,500:1 to 200,000:1. In the case of using a solvent, the catalyst may be used at a concentration with the range from 10 -7 to 10 -1 moles per liter of solvent. As in other similar polymerizations it is highly desirable that the monomers and solvents employed be of sufficiently high purity that catalyst deactivation does not occur. Any suitable technique for monomer purification such as devolatilization at reduced pressures, contacting with molecular sieves or high surface area alumina, and deaeration may be employed. In addition a small amount of an aluminum trialkyl compound or similar scavenger may be added to the reaction mixture to protect the catalyst from deactivation by contaminants in the reaction mixture. Purification of the resulting polymer to remove entrained catalyst may also be desired by the practitioner. Purification of the resulting polymer prepared by the process of this invention is much easier than purification of polymer prepared by a conventional process since the process of this invention does not use polyalkylaluminoxane which is used in large quantities as cocatalyst in conventional processes. Entrained catalyst may generally be identified by residues of ash on pyrolysis of the polymer that are attributable to catalyst metal values. A suitable technique for removing such compounds is by solvent extraction, for example, extraction utilizing hot, high boiling chlorinated solvents, acids or bases, such as caustic, followed by filtration. However, because of the small amounts of catalyst used in the process, polymer purification is normally not necessary. Having described the invention, the following examples are provided as further illustration. Unless stated to the contrary, all parts and percentages are based on weight. Example 1 Preparation of Catalyst A dry 2 ml volumetric flask was charged with 0.70 ml of a 0.0069M toluene solution of pentamethylcyclopentadienyltitanium tribenzyl under an argon atmosphere. Next, 97 µl of a 0.05M solution of tri(pentafluorophenyl) boron in toluene was added. Additional toluene was added to fill the flask. The contents were stirred for one hour at 25°C resulting in the formation of a 0.00241M solution of a composition having a charge separated, limiting structure corresponding to the formula: [CpTiBz 2 ] + [BzB(C 6 F 5 ) 3 ] - wherein Cp is cyclopentadienyl and Bz is benzyl. Preparation of Syndiotactic Polystyrene A dry 20 ml vial was charged with 10.0 ml (87.4 mmol) of purified styrene and 20µl of a 1M solution of triisobutyl aluminum in toluene. The vial was capped with a Teflon™ coated septa and a metal crimp cap, and placed in a water bath at 70°C. After 10 minutes 250µl of the above catalyst composition was added, giving a total molar ratio of styrene:Ti:borane:triisobutyl aluminum of 145,000:1:1:33. After 1 hour the vial was removed from the water bath and the polymerization was stopped by the addition of 2ml of methanol. The off-white, insoluble product was washed with methanol and dried in-vacuo to obtain 5.2 gm of a resultant polymer. The polymer was insoluble in methylene chloride or other common solvents for atactic polystyrene, and had a melting point of 270.4°C (by DSC), consistent with polystyrene having a syndiotacticity of greater than 98 percent. Yield was 0.45 g, 5.0 percent. Molecular weight (Mw) determined by viscosity comparison of o-dichlorobenzene solutions of samples of known molecular weight was 221,000. Example 2 The reaction conditions of Example 1 were repeated excepting that the titanium compound used was pentamethylcyclopentadienyltrismethoxy titanium (4.8 µmol) and 26.5 µl of a 1M toluene solution of triisobutyl aluminum was added to the titanium compound before addition of the borane solution. The mixture of titanium compound, triisobutyl aluminum and tri(pentafluorophenyl)borane was allowed to interact while being stirred for 1.5 hours. The resulting catalyst solution was a medium brown color. The polymerization conditions of Example 1 were substantially repeated. The resulting polymer had a crystalline melting point of 270.2°C, consistent with a polymer having greater than 98 percent syndiotacticity. Yield was 11.5 percent. Mw as determined by viscosity comparison techniques was 814,000. Comparative When the above reaction conditions were repeated without addition of the triisobutyl aluminum solution, no polymerization occurred. Example 3 The reaction conditions of Example 2 were substantially repeated excepting that 48 µl of a 1M toluene solution of triisobutyl aluminum was added to the pentamethylcyclopentadienyltrismethoxy titanium compound before addition of the borane solution. In addition 1.25 ml of the 0.05M solution of tri(pentafluorophenyl) borane was used. The mixture of titanium compound, triisobutyl aluminum and tri(pentafluorophenyl)borane was allowed to interact while being stirred for 1.5 hours. The resulting catalyst solution was a medium brown color. The polymerization conditions of Example 2 were also repeated. The final molar ratio of styrene: Ti:borane:triisobutyl aluminum was 145,000:1:13:43. The resulting polymer had a crystalline melting point of 269.6°C, consistent with a polymer having greater than 98 percent syndiotacticity. Yield was 8.3 percent. Mw was 763,000.

Claims: A process for preparing a composition corresponding to the formula: L m MX n + RBY 3 - wherein: L is a delocalized π-bonding group or substituted group containing up to 50 nonhydrogen atoms; m is 0 or 1; M is a metal of Group 4 of the Periodic Table; X each occurrence is an inert, anionic ligand containing up to 20 nonhydrogen atoms; n is an integer greater than or equal to 1 and the sum of m and n is one less than the valence of M; R is hydrocarbyl, silyl, a combination thereof or a substituted derivative thereof having up to 20 nonhydrogen atoms; B is boron; and Y is an inert covalently bound group having up to 40 atoms and BY 3 is a stable borane compound able to abstract an R group from a compound of the formula L m MX n R, the steps of the process comprising contacting a Group 4 metal containing compound of the formula: L m MX n+1 wherein L, M, X, m and n are as defined above, with a borane compound of the formula: BY 3 wherein B and Y are as defined above, in the presence of an aluminum compound of the formula: AlR 3 wherein R is defined above, in an inert diluent at a temperature from -100°C to 100°C to cause abstraction of at least one R group from the aluminum compound and assimilation thereof in the resulting borane containing complex. A process according to Claim 1, wherein M is titanium. A process according to either of the preceding claims, wherein L is a cyclopentadienyl or substituted cyclopentadienyl group of the formula wherein R' each occurrence is independently selected from hydrogen, halogen, R, NR 2 , PR 2 , OR, SR or BR 2 , wherein R is as defined in Claim 1. A process according to Claim 3, wherein m is 1 and n is 2. A process according to Claim 3 or Claim 4, wherein L is cyclopentadiene or pentamethylcyclopentadiene. A process according to any one of the preceding claims, wherein X is selected from R, halo, NR 2 , PR 2 , OR, SR and BR 2 and wherein R is as defined in Claim 1. A process according to Claim 6, wherein X each occurrence is R, NR 2 or OR. A process according to any one of the preceding claims, wherein each Y is fluoroaryl or trifluoromethyl-substituted aryl. A process according to Claim 8, wherein each Y is perfluorinated. A process according to any one of the preceding claims, wherein the reaction temperature is from 0°C to 50°C.

Inventors: CAMPBELL RICHARD E JR, CAMPBELL, RICHARD E., JR.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1992
Main classification: C07F17
IPC codes: C08F12, C07F17