PROCESS FOR PREPARING AN ALKANONE AND/OR ALKANOL

Abstract: The invention relates to a process for preparing an alkanone and/or alkanol by oxidizing an alkane with 3-30 C-atoms, using oxygen, to form an alkyl hydroperoxide, followed by a decomposition of the resulting alkyl hydroperoxide in the presence of a metal compound immobilized on a carrier, which carrier carries aliphatic or aromatic amine groups or sulphide groups. The process is preferably applied to cycloalkanes.

Description: PROCESS FOR PREPARING AN ALKANONE AND/OR ALKANOL The invention relates to a process for preparing an alkanone and/or alkanol by oxidizing an alkane with 3-30 C-atoms, using oxygen, to form an alkyl hydroperoxide, followed by a decomposition of the resulting alkyl hydroperoxide in the presence of a metal compound immobilized on a carrier. More in particular, the invention relates to a process for preparing an alkanone and/or alkanol comprising alkane mixture in a solvent by decomposition of an alkylhydroperoxide which is present in an alkylhydroperoxide comprising mixture in a solvent in the presence of a metal compound immobilized on a carrier. Such a process is described in EP-A-367326. According to EP-A-367326 a cyclohexane hydroperoxide obtained by air oxidation can be converted under a high yield into a corresponding ketone (or ketone, K) and an alcohol (or alkanol. A). In literature, frequent attention is given to the oxidation of alkanes such as, for instance, cycloalkanes, particularly cyclohexane, to form a corresponding alkanol and/or alkanone. In the process two process steps can be distinguished: first of all the conversion of the alkane into a mixture substantially containing the corresponding alkyl hydroperoxide, followed by a conversion (decomposition) of this alkyl hydroperoxide into a K/A mixture. Beside the direct conversion of the alkyl hydroperoxide, the alkyl hydroperoxide, in this second step, frequently also reacts with the substantial amount of remaining alkane, which again results in the formation of K and A. In some cases, this so-called alkane participation plays an essential part in the total conversion of the alkane and the yield of the K/A mixture that goes with it. The major difference between the oxidation step and the decomposition step is that the latter is performed at lower temperatures. The difference is generally at least 20°C, preferably at least 40°C. The reason for this is that in the oxidation step, performed essentially without catalyst, a relatively high temperature is maintained to keep an acceptable reaction rate; still relatively few side products are formed. The decomposition step, in which substantial amount of catalyst is used, would - if performed at too high temperature - give rise to much unwanted side products. Many catalyst systems have been suggested for use in the above-mentioned process. GB-A-1212824, for instance, describes a homogeneous catalytic reduction of alkyl hydroperoxides. Homogeneous catalysis for the decomposition of alkyl hydroperoxides is still applied for commercial purposes, in spite of the formation of rather substantial catalyst waste streams. In order to avoid these waste streams, it has been suggested, as in US-A-2851496, to absorb the catalyst on a carrier. The activity of such a catalyst has been found in course of time to deteriorate. Neither does the system described in EP-A-367326 provide a stable catalyst active for a long time. EP-A-367326 describes a cobalt-porphyrin complex, which porphyrin complex is linked with a carrier by means of a covalent bond. The invention provides a process for the decomposition of alkyl hydroperoxides while applying the catalyst, which retains its activity for a long period of time. The invention relates to a process for preparing an alkanone and/or alkanol comprising mixture in a solvent by a decomposition of an alkyl hydroperoxide which is present in an alkylhydroperoxide comprising mixture in a solvent in the presence of a metal compound immobilized on a carrier, the process being characterized in that the carrier carries aliphatic or aromatic amine groups or sulphide groups. Further, the invention relates to a process for preparing an alkanone and/or alkanol by oxidizing an alkane with 3-30 C-atoms, using oxygen, to form an alkyl hydroperoxide, followed by a decomposition of the resulting alkyl hydroperoxide in the presence of a metal compound immobilized on a carrier, and is characterized in that the carrier carries aliphatic or aromatic amine groups or sulphide groups. The carrier preferably has groups with the following structure: where the substrate is silica, alumina, titanate n = 0, 1 or 2 and m = 0, 1 or 2, where n + m - 2 X: Si, Ti or Zr R: H or C 1 _ 12 alkyl or alkoxy R 1 : C 1 _ 18 alkyl, aryl, alkaryl Y: S or NR 3 R 2 , R 3 : H ; C j .u alkyl, R 4 -Z-R 5 where R i = C 2 . 12 alkyl Z = NR 6 or S R 5 , R 6 = H, or C 1 . 6 alkyl where R 1 may comprise ether groups and R 2 , R 3 , R 4 , R 5 and R 6 may additionally contain 1 or 2 ether, alcohol or carboxyl groups. The carrier used, carrying aliphatic or aromatic amine groups or sulphide groups, is preferably a carrier carrying groups with the formula R 1 -Y-R 2 where R 1 , Y and R 2 are described above. On its surface the substrate preferably has groups reacting with an organosilicon compound, an organotitanium compound or with another organometallic compound. Hydroxyl groups are particularly suited. Via, for instance, a silicon compound an aminoalkyl compound, for instance, is then linked to the substrate by means of a covalent bond. The substrate used may, for instance, be silica, zeolite, alumina-silica mixtures or titanium dioxide. As X, for instance. Si, Ti or Zr is highly suited, preference is given to the use of silicon. R is preferably methoxy, ethoxy, methyl, ethyl, isopropoxy, n-propoxy, propyl or butoxy. R 1 is, for instance, an alkyl residue such as ethyl, propyl, isopropyl, n-butyl, 1- or 2-methylpropyl, pentyl, cyclopentyl, n-hexyl, 2-methylpentyl, cyclohexyl, octyl, benzyl, phenyl or 2,2-diphenylpropyl. Preference is given to the use of a C 2 _ 6 alkyl, particularly ethyl or propyl, because these are commercially available. R 1 may further contain inert hetero groups, such as ether-oxygen atoms. As Y a sulphur or nitrogen is highly suited. Preferably nitrogen is chosen as Y. The sulphide or amine may be primary, secondary or, (the amine) also tertiary, as long as a valence remains for a proper coordination with a metal from groups IB, IVB, VB, VIB, VIIB and VIII. With a secondary sulphide or amine or tertiary amine, R 2 and R 3 are independent of each other, for instance methyl, ethyl, propyl, i-propyl, butyl, 2-methylpropyl, t-butyl, hexyl, octyl or, for instance, 2-aminoethyl, 2-sulphidoethyl or 3-aminopropyl. Preferably R 2 is (and, as the case may be, R 3 ) : H, C 1 _ 6 alkyl or R -Z-R 5 , where R 4 is C 2 _ 8 alkyl and Z NR 5 or S and R 5 and R 6 , independently of each other, H or C j . g alkyl. R 2 is particularly H or R 4 -NH 2 where R 4 is C 2 _ 3 alkyl. The carrier used, containing an amino group or a sulphide group, may also be a weak basic ion exchanger such as, for instance, a polystyrene (crosslinked with divinylbenzene) carrying -NR 2 groups (where R = H, methyl or ethyl) or a resin carrying an S-R group. The metal complex or metal salt used is preferably a complex or salt of a metal from the fourth period of groups IB, IVB, VB, VIB, VIB or VIII of the periodic system. Examples of highly suitable metals are cobalt, chromium, vanadium, molybdenum, ruthenium, manganese, titanium and iron, in particular cobalt, chromium, vanadium, molybdenum and iron. Hence, preferably the metal compound used comprises a complex or salt of a metal of this group. Of course, mixtures of metals can be used also. For the periodic system reference is made to the first page of the 'Handbook of Chemistry and Physics', 70th edition (1989-1990), the notation used is according to the 'CAS version' . Such a catalyst - as such - is known, and used e.g. for the oxidation of cyclohexane as is described in J. Org. Chem. Vol. 56 (1991) pp. 1981-1983. However, the oxidation reaction is essentially different from an alkylhydroperoxide decomposition reaction. Furthermore, the use of the catalyst in the present invention appears very advantageous in view of the fact that the catalyst is unexpectedly more stable than prior art heterogeneous catalysts. The catalyst can be made by impregnating the carrier, which contains aliphatic or aromatic amine or sulphide groups, with a metal compound, of which metal compound at least a part of the ligands has a weaker bond with the metal than an amine or sulphide group. The metal ion then complexes with the amine and/or sulphide group of the carrier, so that an unexpectedly stable catalyst is obtained. This comes unexpected, because, for instance, a porphyrin-cobalt complex on a carrier had proved not to be stable for a long time. The metal compound is preferably a metal salt or metal complex soluble in, for instance, alcohol or water, so that the carrier can be impregnated easily. The carrier containing aliphatic or aromatic amine or sulphide groups is commercially available, or it can be synthesized by dispersing a substrate such as, for instance, silica or an alumina-zeolite in an organic liquid such as, for instance, methanol, ethanol, THF, dioxane, DMSO, toluene, cyclohexanol or acetone. To this dispersion an organofunctional silane or titanate can then be added. The silane used may, for instance, be 3-aminopropyltrimethoxy- silane, N-methyl-3-amino-propyltrimethoxysilane, 3-amino- propyl-tris(2-methoxypropyltri-methoxysilane, N-amino- ethyl-3-aminopropyltrimethoxysilane, N-aminoethyl-3-amino- propylmethy1-dimethoxysilane, 3-mercaptopropyl-trimethoxy- silane, 3-mercaptopropyl-triethoxysilane, 3-mercapto-propyl- methyl-dimethoxysilane, p-aminophenyl-triethoxysilane. The titanate used may, for instance, be neoalkoxytri(m-amino- phenyl)titanate. The organosilane or titanate compound is usually reacted with the substrate for a period of 10-300 minutes at a temperature ranging from 0 to 150°C. Optimum conditions can easily be selected by the person skilled in the art. The product can then be filtered off, washed and, if so desired, also be dried. The product can also, without further purification, be further processed. To the resulting carrier with aliphatic or aromatic amine groups or sulphide groups a metal compound is added. To this end the carrier is preferably dispersed in an agent in which the metal compound dissolves. The mixture is preferably stirred. It is also very well possible to perform this process in a fixed bed. The complexing of the metal to the carrier containing the amine or sulphide group usually takes 10-300 min and is effected between 0 and 100°C, preferably between 20-50°C, the time and temperature, however, are not critical and can for practical reasons be chosen rather indiscriminately. The alkylhydroperoxide comprising mixture in a solvent is preferably obtained by oxidizing an alkane with 3-30 carbon atoms using oxygen. In the process according to the invention the oxidation of the alkane is effected in the liquid phase in the manner known in the art using, for instance, air, pure oxygen or a mixture of oxygen and inert gas at temperatures of 120-200°C, particularly 140-180°C, for, for instance, 0.1 to 24 hours, preferably 0.5 to 24 hours. In the process, for instance, 1-50% of the alkane is converted, the amount may also be between 1 and 25%. The pressure in this oxidation process is not critical and is mostly between 0.4 and 5 MPa (4 and 50 bar.) . The oxidation of the alkane is preferably carried out in the absence of substances promoting the decomposition of the alkyl hydroperoxide formed, such as compounds of transition metals, and that is why for this reaction preference is given to the use of a reactor with an inert inner wall, for instance an inner wall of passivated steel, aluminium, glass, enamel and materials like these. If yet the use of an oxidation catalyst is desired, the amount of transition metal must preferably be very small, for instance in the order of 1-10 parts by weight per million. As oxidation catalyst, compounds of, for instance, cobalt, chromium, manganese, iron, nickle, copper or mixtures thereof can be used. The immobilized organometallic complexes described in this application are suitable also. Before the decomposition of the hydroperoxide in the oxidation mixture, the oxidation mixture can be treated, if so desired, with water or an aqueous alkali metal hydroxide or alkali metal carbonate solution for the removal and/or neutralization of the acids formed in the oxidation, for instance to a pH of the aqueous phase of 8-13. Optionally, the mixture containing the alkylhydroperoxide can be concentrated by evaporating some or all the alkane and optionally, the alkane can be replaced by another solvent such as an alcohol. However, it is preferred to have the alkylhydroperoxide dissolved in its corresponding alkane. The mixture furthermore may comprise some alkanol and alkanone. The decomposition of the alkyl hydroperoxide in the oxidation mixture is effected by means of the immobilized metal complexes according to the invention. The decomposition catalyst can be used in various ways. As it is immobilized on a carrier, both slurry reactors and, for instance, packed beds can be used to effect the conversion of the alkyl hydroperoxide. The heat of reaction released in the decompostion must be adequately received and carried off to guarantee a proper process temperature control. This can very effectively be done when using slurry reactors. During the decomposition the desired temperature can then, for instance, be maintained by reflux cooling for at least a part of the heat to be carried off. No recirculation of evaporated products will then be required, which has a slightly favourable effect on the yield of desired product. In such a situation the amount of immobilized complex to be used is, for instance, 5-250 ppm metal calculated on the oxidation mixture. Preference is given to the use of more than 10 ppm. Preferably less than 150 ppm is used. The process can also advantageously be carried out in a fixed bed reactor, because in it a relatively high catalyst concentration is reached, this is particularly advantageous if hydroperoxide mixtures are used having a relatively low concentration. The temperature during the decomposition is generally in the range of 25-200°C, preferably between 50 and 120°C. Preferably, the temperature is at least 20°C lower than the temperature used in the oxidation step, more in particular the temperature is at least 40°C lower. In the decomposition the chosen pressure is usually slightly lower than in the oxidation. The decomposition is effected preferably in the presence of oxygen. This improves the yield of K/A mixture. Depending on the concentration of the transition metal on the carrier, the concentration of the hydroperoxide and the temperature, the decomposition usually takes between 5 and 300 minutes. Preferably the residence time of the reaction mixture in a decomposition reactor is kept at between 15 and 120 minutes, but this is not critical. By means of simple analyses, a person skilled in the art can determine if any hydroperoxide is left in a treated mixture. The reaction mixture obtained in the decomposition of the hydroperoxide is an alkanone and/or alkanol in the solvent used. This solvent generally is the corresponding alkane. Furthermore some side products will be present. The mixture can be further processed by subjecting the organic phase after washing with water, if so desired, to a distillation process while recovering alkane to be returned. Thereafter, destination of the desired products, alkanol and alkanone, can be performed. Generally, the alkanol and the alkanone will be separately obtained. The C 3 _ 30 alkane used may, for instance, be propane, 2-methylpropane, cycloheptane, cyclohexane, methyl- benzene, ethylbenzene, 2-propylbenzene, phenylcyclohexane, cyclohexene, diphenylmethane, phenylcyclododecane, 4-tert.butyl-l-cycloheptylbenzene, 2-isopropylnaphthalene, fluorene, 1,8-dimethylfluorene, 1,2-dicyclohexylmethane. The alkane may comprise aromatic groups and ethylenically unsaturated groups. The alkane may be branched, linear and/or cyclic. The process is particularly suited for the oxidation of cycloalkanes with 4-18 carbon atoms, more particularly for the oxidation of cyclohexane, cyclooctane and cyclododecane, the reaction products of the cyclohexane oxidation being particularly suited for use in the preparation of either caprolactam (for nylon-6) or adipic acid (for nylon-6,6). Resulting cyclohexanol and cyclohexanone obtained after destination of the mixture of alkane with cyclohexanol and cyclohexanon have been found without further processing to be pure enough for further conversion into caprolactam. The invention will be further elucidated by means of the following examples. SYNTHESIS Example I To 100 g of a silica (Grace SG524, BET surface area — 540m 2 /g, particle size = 1-3 mm) 500 ml methanol was added at room temperature. This suspension was stirred for 15 minutes. After that, 250 g 3-aminopropyltrimethoxysilane was added. The suspension was stirred at room temperature for 1 hour. After filtration, the solid was washed with 200 ml toluene. This washing was repeated twice. The product was subsequently dried. The carbon content of the modified silica thus obtained (type A) is 63 g/kg. In the modification of silicas with different BET surface areas, the amount of the aminosilane was ajusted directly proportionate to the surface area of the silica (for, for instance, a silica with a BET surface area of 390 m 2 /g, 180 g of the silane was used). Reaction times and temperature remained the same. Other solvents such as, for instance, ethanol and toluene, were found not to have a significant effect on the result. When using a silica with a different particle size distribution, the results were found to be the same. Other silanes, too, could be used, as is shown by the examples below. Example II To 100 g of a silica (Grace 1000MP, BET surface area = 50 m 2 /g, particle size = 1-3 mm) 500 ml methanol was added at room temperature. This suspension was stirred for 15 minutes. After that, 25 g N-2-aminoethyl-3-aminopropyl- trimethoxysilane was added. The suspension was stirred at room temperature for 1 hour. After filtration, the solid was washed with 200 ml toluene. This washing was repeated twice. The product was subsequently dried. The carbon content of the modified silica thus obtained (type B) was 8 g/kg. Example III To 50 g of a silica (Grace SG254, BET surface area = 540 m 2 /g, particle size - 0.8-1.4 mm) 250 ml methanol was added at room temperature. This suspension was stirred for 15 minutes. After that, 25 g 3-mercaptopropyltrimethoxy- silane was added. The suspension was stirred at room temperature for 1 hour. After filtration, the solid was washed with 200 ml methanol. This washing was repeated twice. The product was subsequently dried. The sulphur content of the modified silica thus obtained (type C) was 32 g/kg. Example IV To 50 g of a silica (Grace SG254, BET surface area = 540 m 2 /g, particle size = 0.8-1.4 mm) 250 ml ethanol was added at room temperature. This suspension was stirred for 15 minutes. After that, 25 g p-aminophenyl-bimethoxysilane was added. The suspension was stirred at room temperature for 1 hour. After filtration, the solid was washed with 200 ml ethanol. This washing was repeated twice. The product was subsequently dried. The nitrogen content of the modified silica thus obtained (type D) was 28 g/kg. Generally, it may be said that, if silanes are used having the general formula R 1 -Si(OR 2 ) 3 , where R 2 stands for a methyl group or an ethyl group, the above procedure can be used to modify a silica surface. Example V To 10 g of type A 165 ml of a solution of Co(II)-acetate-tetrahydrate in water (100 g/1) was added. The suspension was stirred for 3 hours at a temperature of 47°C. After filtration, the solid was washed with 400 ml water. The washing procedure was repeated twice. After drying, the resulting silica (type A-Co-1) contained 33 g Co/kg. By varying particularly the reaction time and the temperature it was found that, on the basis of type A silicas, catalysts could be prepared having a cobalt content ranging from 1% to 8%. In table (1) below a number of these results are shown. Table 1 To 10 g of type B 165 ml of a solution of Co(II)-acetate-tetrahydrate in water (100 g/1) was added. The suspension was stirred for 3 hours at a temperature of 47°C. After filtration, the solid was washed with 400 ml water. The washing procedure was repeated twice. After drying, the silica thus obtained (type B-Co-1) contained 3 g Co/kg. Example VII To 10 g of type C 200 ml of a solution of Co(II)-acetate-tetrahydrate in water (100 g/1) was added.The suspension was stirred at room temperature for 5 hours. After filtration, the solid was washed with 400 ml water. The washing procedure was repeated twice. After drying, the silica thus obtained (type C-Co-1) contained 13 g Co/kg. Example VIII To 10 g of type D 165 ml of a solution of Co(II)-acetate-tetrahydrate in water (100 g/1) was added. The suspension was stirred for 4 hours at a temperature of 47°C. After filtration, the solid was washed with 400 ml water. The washing procedure was repeated twice. After drying, the silica thus obtained (type D-Co-1) contained 45 g Co/kg. Example IX To 15 g of type A 100 ml of a solution of Cr(NO) 3 .9 H 2 0 in water (33 g/1) was added. The suspension was stirred at room temperature for 18 hours. After filtration, the solid was washed with 400 ml water. The washing procedure was repeated twice. After drying, the silica thus obtained (type A-Cr-1) contained 14 g Cr/kg. Example X To 15 g of type A 100 ml of a solution of Fe(II)-sulphate-heptahydrate in water (12 g/1) was added. The suspension was stirred at room temperature for 18 hours. After filtration, the solid was washed with 400 ml water. The washing procedure was repeated twice. After drying, the silica thus obtained (type A-Fe-1) contained 29 g Fe/kg. Example XI To 15 g of type A 100 ml of a solution of Cr(NO) 3 . 9 H 2 0 (33 g/1) and CoS0 4 (23 g/1) in water was added. The suspension was stirred at room temperature for 18 hours. After filtration, the solid was washed with 400 ml water. The washing procedure was repeated twice. After drying, the silica thus obtained (type A-Co-Cr-1) contained 13 g Cr/kg and 12 g Co/kg. Batch Experiments Example XII To 50 g of a cyclohexane oxidation mixture containing 200 mmoles cyclohexyl hydroperoxide (CHHP), 60 m oles cyclohexanol (OL) and 30 mmoles cyclohexanone (ON) per kilogramme, 0.5 g A-Co-1 was added at a temperature of 75°C. This mixture was stirred at said temperature until all CHHP was decomposed. The decomposition was followed by means of an iodometric titration. The first order reaction rate constant k was 2.8 * 10 **3 kg sol/(min*g cat). The selectivity, based on the OL + ON formed in relation to the converted CHHP, was 112%. The OL/ON ratio was 1.6. The catalyst could be used a plurality of times without any significant decline of activity. Comparative experiment A Example XII was repeated, the homogeneous catalyst being Co-2-ethylhexanoate (70 ppm Co in solution). The k was 2.0 * 10- - min- *1 for the first 20 minutes of the decomposition. After 20 minutes, the catalyst showed a strong decline of activity. The selectivity to OL + ON was 91.6%. The OL/ON ratio was 2.2. Re-use was not possible. Examples XIII-XXV Example XII was repeated with the other catalysts, The results are shown in table (2) . Table 2 Results with dif ferent catalysts Example Catalyst Particle Metal Comparative experiment B Example XXIV was repeated, the catalyst being Fe(II)sulphate-heptahydrate (70 ppm in relation to the liquid). In consequence of the fact that the Fe catalyst did not dissolve in the oxidate, the decomposition rate could be ignored. Comparative experiment C Example XXIII was repeated, the catalyst being Cr-2-ethylhexanoate (70 ppm in solution). The k was 0.008 nun * The selectivity to OL + ON was 91.7%. The OL/ON ratio was 0.2. The catalyst could not be used again. Example XXVI Example XII was repeated, but now air was passed through the reaction mixture, too. This caused the yield to rise to 114%. The OL/ON ratio fell to 1.3. Example XXVII To 50 g of a cyclododecane oxidation mixture containing 400 mmoles cyclododecyl hydroperoxide (CDHP), 70 mmoles cyclododecanol (DOL) and 40 mmoles cyclododecanone (DON) per kilogramme 0.5 g A-Co-5 was added at a temperature of 75°C. This mixture was stirred at said temperature until all CDHP was decomposed. The decomposition was followed by means of an iodometric titration. The first order reaction rate constant k was 2.94*10- 3 kg sol/min*g cat. The selectivity, based on the DOL + DON formed in relation to the converted CDHP, was 108%. The DOL/DON ratio was 1.4. The catalyst could be used a plurality of times without any significant decline of the activity. Continuous experiments Example XXVIII Into a column with a diameter of 3 cm and a length of 10 cm 29 g A-Co-8 was introduced. Over this column the oxidate mentioned in example XII was pumped at a velocity of 20 g/hour. The temperature in the column was kept at 75°C. In this manner a conversion was' reached of more than 80%. The catalyst was tested for more than 1000 hours and then still did not show any deactivation; moreover, analyses of the organic effluent revealed that the Co concentration in this effluent was lower than 2 ppb. The selectivity to OL + Comparative experiment D To 10 g of a silica (Grace SG254, BET surface area 540 m 2 /g, particle size 1-3 mm) 165 ml of a solution of Co(II)-acetate-tetrahydrate in water (100 g/1) was added. The suspension was stirred for 19 hours at a temperature of 85°C. After filtration, the solid was washed with 400 ml water. The washing procedure was repeated twice. After drying, the resulting silica contained 92 g Co/kg. Into a column with a diameter of 3 cm and a length of 10 cm 7 g of this catalyst was introduced. Over this column the oxidate mentioned in example XII was pumped at a velocity of 40 g/hour. The temperature in the column was kept at 80°C. In the first instance a conversion was reached in this manner of >80%. The catalyst, however, de-activated clearly so that after 1000 hours its activity had fallen to <20% conversion. The selectivity to OL + ON was 89%. Comparative experiment E On a silica of type A (Grace SG239, BET surface area 390 m 2 /g, particle size 1-3 mm) a Co-tetra-sulpho- chloride-phthalocyanine was bonded (see, inter alia, EP-A-367326) . The Co-content of the catalyst thus obtained was 5 g/kg. Into a column with a diameter of 3 cm and a length of 10 cm 10 g of this catalyst was introduced. Over this column the oxidate mentioned in example XII was pumped at a velocity of 20 g/hour. The temperature in the column was kept at 75°C. In the first instance a conversion was reached in this manner of >90%. The conversion rapidly fell to 20% to remain stable thereafter (duration of test > 500 hours) . Example XXIX Example XXVIII was repeated using catalyst A-Cr-1. In a conversion of 75%, the catalyst still showed no de-activation after 1000 hours.

Claims: C L A I M S 1. Process for preparing an alkanone and/or alkanol comprising mixture in a solvent by a decomposition of an alkyl hydroperoxide which is present in an alkylhydroperoxde comprising mixture in a solvent in the presence of a metal compound immobilized on a carrier, the process being characterized in that the carrier carries aliphatic or aromatic amine groups or sulphide groups. 2. Process according to claim 1, characterized in that the carrier has groups with the following structure. R 1 - Y - R 2 where the substrate is silica, alumina, titanate n: 0, 1, 2 and m: 0, 1, 2 where n + m = 2 X: Si, Ti, Zr R: H or C 1 _ 12 alkyl or alkoxy Rl : c ι-i 8 alkyl, aryl, alkaryl Y: S or NR 3 R 2 , R 3 : H, Ci-C jj alkyl, R 4 ^Z-R 5 where R 4 = C 2 -C 12 alkyl Z = NR 6 or S R 5 , R 6 = H, or C j -C 6 alkyl where R 1 may contain ether groups and R 2 , R 3 , R 4 , R 5 and R 6 may additionally contain 1 or 2 ether, alcohol or carboxyl groups. 3. Process according to any one of claims 1-2, characterized in that the substrate is silica. 4. Process according to any one of claims 2-3, characterized in that X is Si. 5. Process according to any one of claims 2-4, characterized in that R 1 is C 2 -C 6 alkyl. 6. Process according to any one of claims 2-5, characterized in that Y and optionally Z are nitrogen atoms. 7. Process according to any one of claims 2-6, characterized in that R 2 is H, or R 4 -NH 4 , where R 4 is C 2 -C 3 alkyl. 8. Process according to any one of claims 2-6, characterized in that R 3 is H. 9. Process according to any one of claims 1-8, characterized in that the metal compound used is a complex or salt of a metal from the fourth period of groups IB, IVB, VB, VIB, VIIB or VIII of the periodic system. 10. Process according to claim 9, characterized in that the metal compound used comprises a complex or salt of a metal from the group cobalt, chromium, vanadium, molybdenum, ruthenium, titanium, manganese and iron and mixtures thereof. 11. Process according to claims 1-10, characterized in that, for complexing the metal compound to the carrier carrying amine groups or sulphide groups, a metal salt or complex is used which is soluble in the dispersant used for disperging the carrier. 12. Process for preparing an alkanone and/or alkanol by oxidizing an alkane with 3-30 C-atoms, using oxygen, to form an alkyl hydroperoxide, followed by a decomposition of the resulting alkyl hydroperoxide in the presence of a metal compound immobilized on a carrier, the process being characterized in that the carrier carries aliphatic or aromatic amine groups or sulphide groups. 13. Process as described in substance in the specification and/or examples.

Inventors: BAUR HENRICUS ANNA CHRISTIAAN, HOOGENDOORN PETER, JANSSEN LUDOVICUS HUBERTUS WIL, KRAGTEN UBALDUS FRANCISCUS, BAUR, HENRICUS, ANNA, CHRISTIAAN, HOOGENDOORN, PETER, JANSSEN, LUDOVICUS, HUBERTUS, WILHELMUS, KRAGTEN, UBALDUS, FRANCISCUS
Applicants: DSM NV, DSM N.V.
Application year: 1992
Main classification: C07C29
IPC codes: B01J21, B01J27, B01J31, B01J35, C07B61, C07C27, C07C29, C07C45, C07C47, C07C49