A-AXIS HIGH TEMPERATURE SUPERCONDUCTING FILMS WITH PREFERENTIAL IN-PLANE ALIGNMENT

Abstract: An a-axis high temperature superconducting film having preferential in-plane orientation is formed. In the preferred embodiment, an a-axis film has substantial amounts of superconductor (12) oriented with its c-axis in a unified direction parallel to the substrate (16). YBCO on neodium gallate (110) plane has resulted in a high temperature superconductor with over 80 % by volume being a-axis with in-plane orientation. These films are epitaxial. The preferred method of film growth is for in situ growth by a laser ablation. Preferably, the a-axis film is nucleated by laser ablation onto a substrate which is at a temperature of 50 to 100 DEG C less than the optimal substrate temperature for c-axis growth. Optionally, once a-axis nucleation has begun, the substrate temperature may be increased to optimize superconductor properties.

Description: DESCRIPTION A-Axis Hiσh Temperature Superconducting Films with Preferential In-Plane Alignment Field of the Invention This invention relates to high temperature supercon¬ ductors and methods for their growth. More particularly, it relates to high temperature superconductors with their a-axis oriented perpendicular to the substrate, and having substantial in-plane alignment of the c-axis of the superconductor. Background of the Invention Starting in early 1986, with the announcement of a superconducting material having a critical temperature (the temperature at which a specimen undergoes the phase transition from a state of normal electrical resistivity to a superconducting state) of 30K (See e.g., Bednorz and Muller, Possible High Tc superconductivity in the Ba-La- Cu-0 System, Z.Phys. B-Condensed Matter 64, 189-193 (1986)) materials having successively higher transition temperatures have been announced. In 1987, the so called YBCO superconductors were announced, consisting of a combination of alkaline earth metals and rare earth metals such as barium and yttrium in conjunction with copper. See, e.g., Wu, et al, Superconductivity at 93K in a New Mixed-Phase Y-Ba-Cu-0 Compound System at Ambient Pressure, Phys. Rev. Lett., Vol. 58, No. 9, pp. 908-910 (1987). Thirdly, compounds containing bismuth were discovered. See e.g, Maeda, A New High-Tc Oxide Superconductor Without a Rare Earth Element, J.J. App. Phys. 37, No. 2, pp. L209- 210 (1988) and Chu, et al, Superconductivity up to 114K in the Bi-Al-Ca-Ba-Cu-0 Compound System Without Rare Earth Elements, Phys. Rev. Lett. 60, No. 10, pp. 941-943 (1988) . Finally, superconductors including thallium have been prepared, generally where the compositions have various s oichiometries of thallium, calcium, barium, copper and oxygen. To date, the highest transition temperatures for superconductors have been observed in thallium containing compounds. See, e.g., G. Koren, A. Gupta and R.J. Baseman, Appl.Phys.Lett. 54, 1920 (1989). A unifying characteristic of these newly discovered superconductors is that they all include copper oxide ("CuO") planes. While the size of the superconducting crystals is often small, sometimes on the order of only microns, when looked at locally, the CuO planes are essentially infinite. If the CuO planes are oriented parallel to the substrate, the film is termed a c-axis film. This plane is sometimes called the basal plane. However, if the CuO planes are oriented perpendicular to the substrate, the film is termed an a-axis film. Fig. 1 shows a c-axis film. The crystal 10 is shown having an array of copper atoms 12. To maintain generality, the other constituents of the superconductor are not shown. The plane 14 shown in phantom is drawn through one of the essentially infinite CuO planes. The plane 14 is substan¬ tially parallel to the surface of the substrate 16. Fig. 2 shows an a-axis high temperature superconduc¬ ting film. Again, copper atoms 12 are shown defining the superconducting crystal structure. The plane 18 shown in phantom shows one of the infinite CuO planes. The c-axis of the superconductor of Fig. 2 is oriented parallel to the substrate 16. As drawn in Fig. 2, the superconductor has a single orientation of the c-axis. However, in the prior art, a-axis films have a plurality of domains, some of which have a c-axis as shown, and some of which have a c-axis at an angle, typically 90°, to the domain shown. When multiple, unoriented domains exist, the film is said to be a polydirectional a-axis films. The crystal structure for the various high tempera- ture superconducting crystals have been characterized. Taking the case of YBCO, it is said to have a perovskite crystal structure, so named after the mineral perovskite (calcium titanite) . Fig. 3 shows the unit cell for a YBCO superconductor. There are three orthoganol axis, the A, B and C axis. The shoe box shaped structure has an A dimension of 3.84A, a B dimension of 3.88A and a C dimen- sion of 11.7A. When formed as a c-axis film, the long c-axis is oriented perpendicular to the substrate 16 (See Fig. 1) . When oriented as an a-axis film, the long C dimension is oriented parallel to the substrate 16 (See Fig. 2). Many applications for high temperature superconduc¬ tors require c-axis oriented films. The superconducting current ("superσurrent") preferentially flows in a direc¬ tion parallel to the CuO plane. In the case of a c-axis film, the supercurrent flows parallel to the substrate 16, and thus, may flow for relatively long uninterrupted dis¬ tances. C-axis films are particularly useful for micro¬ wave device applications. For other applications, it is desirable to have an a-axis oriented film. As shown in Fig. 2, the CuO planes are oriented perpendicular to the substrate. This makes for a large antisotropy in resis¬ tance to supercurrent flow. Flow in the direction paral¬ lel to the CuO plane may be readily accomplished, but flow perpendicular to the CuO plane must be by the tunnelling phenomena due to the nature of weakly coupled supercon- ducting state between adjacent CuO planes, resulting in so called tunneling current. Polydirectional a-axis films have been grown previ¬ ously. Typically, numerous discrete domains exist where the superconductor is a-axis oriented perpendicular to the substrate, but the c-axis of the various domains are not parallel to one another. If the film is epitaxial, the superconductor will be oriented relative to the crystal structure of the substrate, in which case the various domains will be oriented with equal probability in one of two directions. Techniques for growing pure a-axis films used in the past have included: RF Magnetron Sputtering With Post- Annealing on SrTi0 3 (001) , K. Shar, et al, IEEE Trans. Magn. 25, 2422 (1989); Off-Axis Magnetron Sputtering on Both SrTi0 3 (001) and LaA10 3 (001), C.B. Eom, A.F. Marshall, S.S. Laderman, R.D. Jacowitz and T.H. Geballe, Science 249, 1549 (1990) ; and Laser Ablation on PrBa-Cu 3 0-_- Buffered SrTi0 3 (001) , A. Inam, CT. Rogers, R. Remesh, L. Farrow, K. Remcshnig, D. Hart and T. Venjatesan, Applied Physics Letters 57, 2484 (1990) and R. Ramesh, A. Inam, D.L. Hart and CT. Rogers, Physca C 170, 325 (1990) . The in-plane orientation of the superconducting film with respect to the substrate is uncontrolled, with the c-axis of different a-axis domains orienting themselves in two different directions. The C.B. Eom reference, above, suggests use of lower substrate temperatures in a laser ablation device to promote a-axis growth. None of the prior art references has grown a-axis superconducting films with a preponderance of the super¬ conducting domains having their c-axis aligned. This is so despite the clear desirability of such a result. Summary of the Invention An a-axis high temperature superconductor has substantial in-plane alignment. In accordance with this invention, the a-axis high temperature superconducting film is formed on a substrate having an anisotropic surface cell. In the preferred embodiment, a supercon¬ ductor such as YBCO or the thallium containing supercon¬ ductors are grown on the (110) plane of neodium gallate (NdGa0 3) . The surface cell of neodium gallate (110) has an anisotropic surface cell. Epitaxial a-axis YBCO films had been grown on the (110) plane of neodium gallate with substantial in-plane orientation. The preferred method of growing a-axis oriented films utilizes laser ablation onto a substrate at a temperature which promotes a-axis growth. This temperature is typically lower than that which pro- motes c-axis growth. Preferably, a substrate temperature of 50 to 100°C below optimal for c-axis growth is desired to promote a-axis nucleation. Subsequently, the substrate temperature may be raised to improve superconducting properties of the film. It is an object of this invention to grow a-axis high temperature superconducting films with substantial in- plane alignment. It is yet a further object of this invention to grow preferentially oriented high-temperature superconductors on substrates with aniostropically sized surface cells. It is yet a further object of this invention to form an a-axis film of YBCO or thallium superconductor with substantial in-plane alignment on a neodium gallate (110) plane. Brief Description of the Figures Fig. 1 shows a perspective view of a c-axis oriented high temperature superconducting film on a substrate. Fig. 2 shows a perspective view of an a-axis high temperature superconducting film on a substrate. Fig. 3 shows a perspective view of a unit cell for a YBCO superconductor. Fig. 4 shows a perspective view of the reduced unit cell for neodium gallate. Detailed Description Neodium gallate has an orthorhombic perovskite structure with lattice constants a = 5.428A, b — 5.499A, and c = 7.708A. A pseudo-cubic (perovskite-like) unit cell can be constructed with a* - b 1 = 3.863A and c' = 3.854A. Both a' and b'-axis are perpendicular to c'-axis, and the angle θ between a' and b' is 90.74°. The plane defined by the a' and b'-axis defines a rhombus. The structure defined by the b' - c'-axis is a rectangle. Neodium gallate (110) has the plane defined by the b' and c'-axis at its surface. YBCO superconducting films have been grown on the (110) plane of neodium gallate. In the preferred embodi- ment, the films were in situ deposited by laser ablation from a stoichiometric target. A Siemens XP2020 XeCl Excimer Laser (308nm) was used at a repetition rate of 5Hz. The laser fluence on the target was maintained at around 5 joules/cm 2 . The target is commercially available from Superconductive Components Inc. The preferred targets are stoichiometric and are fabricated by cold pressing followed by sintering. The substrate is heated in the laser ablation appara- tus prior to deposition of the film. For films grown with a substrate temperature between 810 and 830 β C, the major¬ ity of the film is c-axis textured, with small amounts of a-axis grains being formed. In the preferred embodiment, the substrate temperature is initially made lower than this temperature, preferably by from 50 to 100'C, to pro¬ mote a-axis nucleation. Since the substrate temperature was measured by a thermocouple attached to the heater block, the actual temperature at the substrate surface may be from 20 to 50 β C lower. In the preferred embodiment, the substrate temperature was held at 700 β C during deposi¬ tion. If desired, following nucleation of the a-axis film, the substrate temperature may be raised to ordinary processing temperatures to enhance the film crystallinity and superconducting properties of the film. For films made to date, the oxygen pressure was maintained at 600 mtorr during film growth and was increased to one atmosphere immediately after deposition. Typical film thicknesses have been between 1,500 and 2,500A. The various processing parameters relating to laser ablation may be chosen as known to those skilled in the art to optimize the properties of the film. Films grown by the above described method have gener¬ ated a-axis films having substantial in-plane orientation. Analysis of these films indicate that the film is predomi- nately a-axis in texture, having greater than 90% a-axis, with the remaining amount being c-axis oriented. Out of the a-axis material, it is believed that over 90% has its c-axis aligned in one direction. Overall, between 80 to 90% by volume of the superconductor has there a-axis grains aligned with their c-axis close to a single direc¬ tion in the plane. Considering superconducting properties, the film had a T c of 89.5K, which is 1 to 2K lower than a typical T c for a c-axis oriented film of the same material on the same substrate. However, the transition width for T c was much broader than is typically observed in a c-axis film of comparable thickness. Though the invention has been described with respect to a specific preferred embodiment, many variations and modifications may become apparent to those skilled in the art. It is therefore that the appended claims be inter- preted as broadly as possible in view of the prior art to include all such various and modifications.

Claims: Claims 1. A superconductive device comprising: a superconductive film having at least 80% by volume a-axis textured material, and a substrate having an anisotropically sized surface cell. 2. The superconductive device of claim 1 wherein the superconductive film is a YBCO superconductor. 3. The superconductive device of claim 1 wherein the superconductive film is a thallium containing superconductor. 4. The superconductive device of claim 1 wherein the substrate is NdGa0 3 (110) . 5. The superconductive device of claim 1 wherein the film is epitaxial to the substrate. 6. A superconductive device comprising: a superconductive film including a-axis textured domains, where there is a preferential in-plane orienta¬ tion of the a-axis domains, and a NdGa0 3 substrate. 7. The superconductive device of claim 6 wherein the superconductive film is a YBCO superconductor. 8. The superconductive film of claim 6 wherein the superconductive film is a thallium containing supercon- ductor. 9. The superconductive film of claim 6 wherein the substrate surface is the (110) plane. 10. A method for producing a-axis superconductive films by laser ablation comprising the steps of: heating the substrate to a first temperature which promotes a-axis nucleation, laser ablating a target to deposit at least a portion of the film on the substrate, and heating the substrate to a second temperature which is higher than the first temperature. 11. The method for producing a-axis superconducting films where the difference between the first and second temperatures is in the range of 50-100"C

Inventors: SUN JONATHAN ZAN-HONG, YOUNG KWO-HSIUNG, SUN, JONATHAN, ZAN-HONG, YOUNG, KWO-HSIUNG
Applicants: SUPERCONDUCTOR TECH, SUPERCONDUCTOR TECHNOLOGIES, INC.
Application year: 1992
Main classification: B32B15
IPC codes: C01G1, C30B23, C30B29, H01L39