Electrically connectable module

Abstract: An electrically connectable module is manufactured from a substrate (s) of an electrically insulating polymer matrix doped with an electrically insulating fibrous filler capable of heat conversion to an electrically conductive fibrous filler to form a fibre-doped substrate (s). One end (12) of an electrical connector (10) is embedded in the fibre-doped substrate (s) to locate the one end (12) adjacent the surface (14) of the substrate (s) while exposing an opposite end (16) of the electrical connector (10). The surface (14) of the fibre-doped substrate (s) is locally heated preferably with a laser to form a conductive trace (20) by the in-situ heat conversion of the electrically insulating fibrous filler, the localised heating including the one end (12) of the electrical connector (10) to electrically connect the electrical connector (10) to the conductive trace. In another embodiment, a conductive material is electrodeposited on the conductive trace (20) by applying a voltage to the opposite end (16) of the electrical connector (10). The substrate (s) is moulded into a desired shape to form the module, and a plurality of electrical connectors (10) can be embedded into the substrate (s) in any one of several different standardised arrangements.

Description: The present invention relates to an electrically connectable module and a method for manufacturing same, and more particularly to a module comprising a substrate formed from an electrically insulating polymer matrix doped with an electrically insulating fibrous filler capable of heat conversion to an electrically conductive fibrous filler. In electrical machines such as image reproducing devices, it is necessary to distribute power and/or logic signals to various sites within the machine. Traditionally, this has taken the form of using conventional wires and wiring harnesses in the machine to distribute the power and logic signals to the various functional elements in the machine. As an alternative to wires, it is known to use a CO₂ laser to burn conductive traces in a polymeric material that has been doped with carbon fibres so that the untreated material (not subjected to the laser) is not conductive. When locally heated by the laser, the polymeric material volatilises to leave a conductive network of polymer residue and conductive dopant. U.S. Patent 4,841,099 teaches how an electrically insulating polymer matrix is filled with an electrically insulating fibrous filler capable of heat conversion to an electrically conducting fibrous filler, to form a continuous electrically conductive path by the in-situ heat conversion of the electrically insulating fibrous filler using a laser. The entire disclosure of U.S. Patent 4,841,099 is herein incorporated by reference. In order to make the conductivity of the traces more sufficient for many applications, it has been proposed that metal be electrodeposited onto the traces. One advantage of this electrodepositing approach is to place metal conductors onto the polymeric material in the trough or channel created by the laser with the metal adhering to the polymeric material. However, the prior art has not developed or suggested methods for reliably electroplating the trace, or for connecting the traces to electrical connectors in the polymeric material for distributing power or signals between the trace and an external component. U.S. Patent No. 4,604,678 to Hagner discloses a circuit board plated with high density electrical traces connected to respective terminals of a number of electrical current components mounted on a substrate. Grooves on the substrate can be machined by a laser. The components are assembled before the grooves are plated to minimise production costs and assure electrical connection between the plated laser-formed grooves and the terminals of respective components. The conductive traces overlie and are in electrical contact with chip pads. U.S. Patent No. 3,984,620 to Robillard et al. discloses an integrated circuit chip test and assembly package having a semiconductor interconnection substrate with apertures for integrated circuits. The assembly package includes an interconnection with external leads which are located between insulating layers of the substrate. U.S. Patent No. 3,818,279 to Seeger, Jr. et al. discloses an electrical interconnection and contacting system comprising a flexible plastic insulator, most preferably an elastomeric substrate having at least one layer of electrically conductive elastomeric material embedded therein. The system is useful in coupling integrated circuits to other circuitry. One object of the present invention is to provide an electrically connectable module and method for connecting a trace to an electrical connector in a reliable manner. Accordingly, the present invention provides a method of manufacturing an electrically connectable module from a substrate of an electrically insulating polymer matrix, the method comprising doping the substrate with an electrically insulating fibrous filler capable of heat conversion to an electrically conductive fibrous filler, to form a fibredoped substrate, characterised by embedding one end of an electrical connector into the fibre-doped substrate to locate the one end adjacent a surface of the substrate while exposing an opposite end of the electrical connector; and locally heating the surface of the fibre-doped substrate to form a continuous electrically conductive trace by the in-situ heat conversion of the electrically insulating fibrous filler including the localised heating at the one end of the pre-embedded electrical connector to electrically connect the electrical connector to the conductive trace. The method reliably connects the conductive trace to the electrical connector embedded in the polymeric material. In one embodiment of the invention the method includes the additional step of electrodepositing a conductive material, such as copper, on the conductive trace by applying a voltage to the opposite end of the electrical connector. The conductive material may be electrodeposited initially only on the conductive trace. In another embodiment the conductive material is filled into a channel created by the localised heating during formation of the conductive trace. In another embodiment the conductive material is adhered to the substrate. All of these embodiments provide methods for reliably electroplating a conductive trace formed in a polymeric material by localised laser heating. According to one embodiment there is provided a method of manufacturing an electrically connectable module from a substrate of an electrically insulating polymer matrix comprises the steps of: doping the substrate with an electrically insulating fibrous filler capable of heat conversion to an electrically conductive fibrous filler, to form a fibre-doped substrate; and embedding one end of an electrical connector in the fibre- doped substrate to locate the one end adjacent a surface of the substrate while exposing an opposite end of the electrical connector. The surface of the fibre-doped substrate is then locally heated preferably with a laser to form a conductive trace by the in-situ heat conversion of the electrically insulating fibrous filler, including the localised heating at the one end of the electrical connector to electrically connect the electrical connector to the conductive trace. The opposite end of the electrical connector may be used to apply a voltage to the conductive trace for electrodepositing a conductive material on the conductive trace. In one embodiment the conductive trace and connection between the conductive trace and the one end of the electrical connector are formed by volatilising the polymer matrix in the substrate and the polymer matrix surrounding the one end of the electrical connector. Conveniently the method includes the step of conducting electrical power through the conductive trace by connecting the opposite end of the electrical connector to an electrical component. In a further embodiment the method includes the step of conducting electrical power through the electrical connection by connecting the conductive trace to an electrical component. Conveniently the substrate is moulded into the desired shape prior to the localised heating of the substrate. In a preferred embodiment a plurality of electrical connectors are embedded into the fibre-doped substrate in a standardised arrangement, each electrical connector being connected to a corresponding conductive trace for electrical connection of the electrical connectors and conductive traces to an electrical component. In accordance with another aspect of the invention, an electrically connectable module comprises a substrate formed from an electrically insulating polymer matrix doped with an electrically insulating fibrous filler capable of heat conversion to an electrically conductive fibrous filler, characterised by an electrical connector embedded into the substrate and having one end adjacent a surface of the substrate and an opposite end exposed from the substrate; a continuous electrically conductive trace formed on the surface of the substrate by in-situ heat conversion of the electrically insulating fibrous filler; and a connection formed between the one end of the electrical connector and the conductive trace by the in-situ heat conversion of the electrically insulating fibrous filler in the polymer matrix surrounding the one end of the electrical connector. In one embodiment the module comprises a channel for receiving the conductive trace, the channel being filled with the conductive material to adhere the conductive material to the substrate. The invention will be described further, by way of example, with reference to the following figures wherein: Fig. 1A is a side view of a moulded component doped with carbon fibres and having embedded electrical connectors; Fig. 1B is a top view of the component of Fig. 1A; Fig. 2A is a plan view of one surface of a fibre- doped chip carrier having embedded electrical connectors; Fig. 2B is a side view of the chip carrier of Fig. 2A illustrating the embedded electrical connectors having one end extending to an upper surface of the carrier and an opposite end projecting from the lower surface of the carrier; and Fig. 2C is a plan view of the upper surface of the chip carrier of Fig. 2B illustrating the conductive traces connected to the ends of the electrical connectors. In accordance with preferred embodiments of the invention and as illustrated in Figs. 1A, 1B, 2A, 2B and 2C, an electrical connector 10 is embedded in a substrate S which is preferably an electrically insulating polymer matrix material moulded to a desired shape. The disclosure of U.S. Patent 4,841,099 (which is herein incorporated by reference) describes the polymer materials. One end 12 of the connector 10 is buried at or just below the surface 14 of the polymer, while the opposite end 16 is exposed from the moulded polymeric material. After the process described below, the opposite or exposed end 16 will be available for electrical connection to a component external to the moulded polymeric material. The substrate S has been doped with an electrically insulating fibrous filler capable of heat conversion to an electrically conductive fibrous filler. Typical fibrous fillers are petroleum pitch based carbon fibres which are heat convertible carbonaceous fibres, such as thermally stabilised, polyacrylonitrile fibres which upon heat conversion provide electrically conducting fibres (also known as preox fibres as disclosed in U.S. Patent 4,841,099). Localised heating of the surface 14 of the fibre-doped substrate S with a laser forms conductive traces 20. The disclosure of U.S. Patent 4,841,099 (which is incorporated by reference) describes the materials and processes for doping the fibres in the substrate and forming the conductive traces. In accordance with the invention, the localised heating to form the conductive trace 20 includes localised heating at the buried end 12 of the connector to volatilise the thin layer of polymeric material around the electrical connector 10, thus guaranteeing that the conductive fibre trace 20 will make electrical contact with the one end 12 of the connector 10. The localised heating can begin or end at the buried end 12 of the connector 10 when forming the trace 20. Accordingly, the electrical connector 10 is pre-embedded in the fibredoped polymeric material and the electrical connection between the electrical connector and the conductive trace is formed simultaneously with the formation of the conductive trace by starting or ending the localised laser heating at the buried end 12 of the electrical connector. After electrical connection to the trace, the electrical connector 10 can be used as a reliable connection to the laser buried trace for electrodeposition (which is cheaper than electroless deposition) of a conductive material (preferably copper) onto the trace. In particular, a voltage can be applied to the exposed end 16 of the electrical connector 10 to apply the voltage to the conductive trace for electrodeposition. The process of electrodeposition of conductive materials onto the trace is well known to those skilled in the art as evidenced by U.S. Patent 4,841,099. Figures 1A and 1B and Figures 2A, 2B and 2C show two exemplary electrically connectable modules using the teachings of the present invention. The substrate S is prepared by moulding into the desired shape, for example the prong arrangement of Figs. 1A and 1B, or a standard chip carrier arrangement of Figs. 2A, 2B and 2C. U.S. Patent 4,841,099 discloses moulding techniques. The substrate S is doped with carbon fibres and embedded with the electrical connectors 10. In Figs. 1A and 1B, the electrical connectors 10 are prongs having their buried ends 12 adjacent the surface 14 of the module on which the traces will be formed. The opposite end 16 is exposed. In Figs. 2A, 2B and 2C, the electrical connectors 10 are pins which have their buried ends 12 adjacent the surface 14 on which the conductive traces 20 will be formed with the pins extending to the opposite surface. The conductive trace 20 is then formed on the surface S of the substrate with a laser, preferably by starting at the buried end 12 of the electrical connector 10 to connect the electrical connector 10 to the trace 20. Using the exposed end 16 of the electrical connector 10 to apply a voltage, the conductive material is electrodeposited on the laser trace 20. The electrical connector 10 is now used for connection to the trace 20 when the module is assembled into the machine. The electrical connections such as the prongs of Figs. 1A and 1B or the pins of Figs. 2A, 2B and 2C can be arranged in different standardised forms or predetermined arrangements for ease of connection to various electrical components. For example, in Figs. 1A-1B, the prong arrangement can accept a similar female style connector. In Figs. 2A, 2B, and 2C, the arrangement of pins accepts a carrier for an integrated circuit. It is also noted that the polymer provides mechanical support to the electrical connectors which allows rigid connections to be made when two polymer pieces are connected together. For example, two connector modules can be made in the manner described herein with male and female style connectors, respectively, which can then be mechanically connected together by standard methods to automatically electrically connect the modules together. As an example, a standard four pin connector was embedded into a plastic part (the plastic part being a low cost moulding material including polyphenylene oxides known as General Electric Noryl, and the plastic part being doped with preox fibres in an amount of about 30% by weight of the total filled polymer matrix) with the pins extending through the plastic to the other side. The module formed of the embedded connector and polymer matrix material can be manufactured and processed by any of the methods and examples of U.S. Patent 4,841,099. A poor electrical connection between the pins and the conductive traces resulted if the buried ends of the pins were too deep into the plastic part or stuck too far out of the plastic part. Optimum results were achieved when the top of each pin was flush with the surface of the plastic part. Also, when burning the trace in the plastic part, a higher laser power (by about 30%) helped to make a better electrical connection between the pins and the laser burnt trace. After the laser traces were made and rinsed with a solvent to remove residue, the resistance between a pin and the trace was about 200 ohms. This is equivalent to the resistance of a few inches of the laser trace in the plastic and was found not to limit electrodeposition of copper onto the traces. Traces were easily plated to a resistance of less than an ohm with a few hours of electroplating. Better morphologies were obtained in the electrodeposited copper if the deposition started only on the laser trace (keeping the connector pins out of the plating solution initially). This allowed a good conducting path to be made in the laser trace to reduce the potential drop along the trace which promoted preferential deposition on the pin rather than on the laser trace. The invention has been described with reference to its preferred embodiments which are intended to be illustrative and not limiting. Various changes may be made by those skilled in the art without departing from the scope of the invention as defined in the appended claims.

Claims: A method of manufacturing an electrically connectable module from a substrate (s) of an electrically insulating polymer matrix, the method comprising doping the substrate (s) with an electrically insulating fibrous filler capable of heat conversion to an electrically conductive fibrous filler, to form a fibre- doped substrate, characterised by embedding one end (12) of an electrical connector (10) into the fibre-doped substrate (s) to locate the one end (12) adjacent a surface (14) of the substrate (s) while exposing an opposite end (16) of the electrical connector (10), and locally heating the surface (14) of the fibre-doped substrate (s) to form a continuous electrically conductive trace (20) by the in-situ heat conversion of the electrically insulating fibrous filler including the localised heating at the one end (12) of the pre-embedded electrical connector (10) to electrically connect the electrical connector (10) to the conductive trace (20). A method as claimed in claim 1, characterised by electrodepositing a conductive material on the conductive trace (20) by applying a voltage to the opposite end (16) of the electrical connector (10). A method as claimed in claim 1 or claim 2, characterised in that the one end (12) of the electrical connector (10) is located flush with the surface (14) of the substrate (s). A method as claimed in claim 1 or claim 2, characterised in that the one end (12) of the electrical connector (10) is located below the surface (14) of the substrate (s). A method as claimed in any one of claims 1 to 4, characterised by electrical connectors (10) embedded into the fibre-doped substrate (s) in a standardised arrangement, each electrical connector (10) being connected to a corresponding conductive trace (20) for electrical connection of the electrical connectors (10) and conductive traces to an electrical component. An electrically connectable module comprising: a substrate (s) formed from an electrically insulating polymer matrix doped with an electrically insulating fibrous filler capable of heat conversion to an electrically conductive fibrous filler, characterised by an electrical connector (10) embedded into the substrate (s) and having one end (12) adjacent a surface (14) of the substrate (s) and an opposite end (16) exposed from the substrate (s), a continuous electrically conductive trace (20) formed on the surface (14) of the substrate (s) by in-situ heat conversion of the electrically insulating fibrous filler; and a connection formed between the one end (12) of the electrical connector (10) and the conductive trace (20) by the in-situ heat conversion of the electrically insulating fibrous filler in the polymer matrix surrounding the one end (12) of the electrical connector (10). A module as claimed in claim 6, characterised by a conductive material electrodeposited on the conductive trace (20) by applying a voltage to the opposite end (16) of the electrical connector (10). A module as claimed in claim 6 or claim 7, characterised in that the one end (12) of the electrical connector (10) is located flush with the surface (14) of the substrate (s). A module as claimed in claim 6 or claim 7, characterised in that the one end (12) of the electrical connector (10) is located below the surface (14) of the substrate (s). A module as claimed in any one of claims 6 to 9, characterised by a plurality of electrical connectors is embedded into the substrate (s) in a standardised arrangement, each electrical connector (10) being connected to a corresponding conductive trace (20) for electrical connection of the electrical connectors (10) and conductive traces (20) to an electrical component.

Inventors: MANTELL DAVID ALLEN, MANTELL, DAVID ALLEN
Applicants: XEROX CORP, XEROX CORPORATION
Application year: 1992
Main classification: H05K3
IPC codes: H01R11, H01B5, H01R29, H05K3, H01R43, H01R13, H01L21, H01L23