Adducts of diaminodiphenyl sulfone compounds as hardeners for epoxy resins

Abstract: The present invention relates to a hardener for polyfunctional epoxy resins comprising the adduct obtained from the reaction of (1) a diaminodiphenyl sulfone of the formula wherein R₁, R₂, R₃ and R₄ are independently hydrogen, C₁-C₄alkyl or halogen and (2) a cycloaliphatic diepoxide at a ratio of aminohydrogen equivalent of said sulfone to said epoxy equivalent of said diepoxide from 2.5:1 to 75:1.

Description: The present invention relates to amino groups containing adducts of a diaminodiphenyl sulfone a cycloaliphatic diepoxide. Adducts of diaminodiphenyl compounds and diglycidyl ethers of polyhydric phenols are described in U.S. Patent No. 4,330,659. These hardeners for epoxy resins exhibit improved processability in prepregging compared with unmodified diaminodiphenyl sulfones, but suffer from the disadvantage that the cured resins exhibit comparatively low modulus and strength and the decreased thermal performance (i.e. modulus retention at temperatures greater than 100°C). The melt viscosity of compositions containing the foregoing adducts is considerably higher in comparison to compositions containing the unmodified diaminodiphenyl sulfones. Due to the aforementioned disadvantages, these adducts cannot be used in certain processes such as resin transfer molding or filament winding. Accordingly, it is a primary object of the present invention to provide a modified hardener system for epoxy resins which overcones the disadvantages of the prior art unmodified diaminodiphenyl sulfones and the adducts thereof with diglycidyl ethers of polyhydric phenols in accordance with U.S. Patent No. 4,330,659. It is a further object of the present invention to provide a modified hardener system for matrix epoxy resins for prepregging, laminating, filament winding and resin transfer molding. It is a still further object of the present invention to provide a modified hardener system which provides cured epoxy resin systems exhibiting improved modulus, mechanical strength and thermal performance. Various other objects and advantages of the present invention will become apparent from the following description and examples. It has now been surprisingly discovered that the reaction product of diaminodiphenyl sulfone and cycloaliphatic diepoxides provides hardeners for epoxy resin systems which epoxy resin system cured therewith exhibit improved performance characteristics, such as modulus and strength retention at 100 - 150°C. The present invention relates to a hardener for polyfunctional epoxy resins comprising the adduct obtained from the reaction of (1) a diaminodiphenyl sulfone of the formula wherein R 1 , R 2 , R 3 and R 4 are independently hydrogen, C 1 -C 4 alkyl or halogen and (2) a cycloaliphatic diepoxide at a ratio of aminohydrogen equivalent of said sulfone to said epoxy equivalent of said diepoxide from 2.5:1 to 75:1. The modified hardeners of the present invention are prepared by reacting cycloaliphatic epoxy resins with a diaminodiphenyl sulfone compound. Suitable diaminodiphenyl sulfones are of the formula wherein R 1 , R 2 , R 3 and R 4 are independently hydrogen, C 1 -C 4 alkyl or halogen. Preferably, R 1 , R 2 , R 3 and R 4 are independently C 1 -C 4 alkyl, most preferably, methyl or ethyl, or halogen, most preferably, chlorine, bromine or fluorine. Commercially available sulfones include the 4,4′-, 2,4′- and 3,3′-diaminodiphenyl sulfones. The preferred sulfone is 3,3′-diaminodiphenyl sulfone. Suitable cycloaliphatic epoxy resins are diepoxides having at least one epoxy group attached to the cycloaliphatic moiety, selected from the group consisting of vinyl-cyclohexene dioxide, 7-oxabicycloheptane-3-carboxylic acid 7-oxa-bicyclohept-3-ylmethyl ester, bis(3,4-epoxycyclohexylmethyl)adipate, 3,4-epoxycyclohexyloxirane, 2-(3′,4′-epoxycyclohexyl)-5,1″-spiro-3″,4″-epoxycyclohexane-1,3-dioxane. Examples of commercially available cycloaliphatic diepoxides are 7-oxabicycloheptane-3-carboxylic acid 7-oxa-bicyclohept-3-ylmethyl ester (e.g. CY-179® from CIBA-GEIGY Corporation, Ardsley, New York), vinyl-cyclohexene dioxide (e.g. ERL 4206® from Union Carbide Corporation, Danbury, Connecticut) and cycloaliphatic diepoxide having a spiro structure, for example 2-(3′,4′-epoxy cyclohexyl)-5,1″-spiro-3″,4″-epoxycyclohexane-1,3-dioxane (ERL 4234® from Union Carbide Corporation, Danbury, Connecticut). The structures of these cycloaliphatic diepoxides are shown below: The hardeners of the present invention are prepared by admixing the diaminodiphenyl sulfone compound with the cycloaliphatic epoxy resin and heating the mixture at about 140 - 220°C, preferably at 170 - 190°C for about 1-8 hours, preferably about 2-3 hours. The reaction can be carried out in solution (applicable solvents include ketones, esters and ethers with subsequent removal of the solvent by evaporation. Ratios of aminohydrogen equivalent of the diaminodiphenyl sulfone to the epoxy group equivalent of cycloaliphatic epoxy resin are in the range of 2.5:1 to 75:1, preferably 5:1 to 15:1. The diaminodiphenyl sulfone adducts of this invention are suitable as hardeners for epoxy resins selected from a broad range of aliphatic and aromatic epoxies having a functionality of at least two. Typical materials include glycidylated hydantoin epoxy resins, amino phenol epoxy resins, aromatic amine epoxy resins, polyglycidyl esters, cycloaliphatic epoxy resins, tetraglycidylated methylene dianiline derivatives, diglycidyl ether of bisphenol A, epoxy phenol novolacs, 1,4-butane diol diglycidyl ether, epoxy cresol novolacs, trimethylolpropane triglycidyl ether, triglycidyl tris(p-hydroxyphenyl)methane, tetraglycidyl-1,1,2,2 tetrakis(p-hydroxyphenyl)ethane, vinyl cyclohexene dioxide, N,N,N 1 ,N 1 -tetraglycidyl-4,4 1 -methylene bis-benzeneamine, N,N,N 1 N 1 -tetraglycidyl metaxylene diamine, diglycidyl aniline, resorcinol diglycidyl ether, the diglycidyl ethers of catechol and hydroquinone, diglycidyl ortho-toluidine, diglycidyl isophthalate, bisphenol A, F or S epoxy resins, triglycidyl isocyanurate, and N,N,N 1 ,N 1 -tetraglycidyl 1,3 bis-amino-methylcyclohexane. The various ethers may be substituted on the respective phenyl rings by such non-reactive substituents as alkyl and halogen. Tetraglycidylated methylene dianiline derivatives are preferred. The preparation of such materials is well-known in the art. The hardener is present in epoxy resin compositions in accordance with the present invention in stoichiometric amounts ±50% relative to the epoxy resin component, with 85-100% of stoichiometry being preferred. The epoxy resin compositions of the invention may also contain other conventional modifiers such as extenders, fillers and reinforcing agents, pigments, dyestuffs, organic solvents, plasticizers, tackifiers, rubbers and diluents. As extenders, reinforcing agents, fillers and pigments which can be employed in the compositions according to the invention there may be mentioned, for example: glass fibers, glass balloons, boron fibers, carbon fibers, cellulose, polyethylene powder, polypropylene powder, mica, asbestos, quartz powder, gypsum, antimony trioxide, bentones, talc, silica aerogel ("Aerosil"), fumed silica, lithopone, barite, calcium carbonate, titanium dioxide, carbon black, graphite, iron oxide, or metal powders such as aluminum powder or iron powder. It is also possible to add other usual additives, for example, agents for conferring thixotropy, flow control agents such as silicones, cellulose acetate butyrate, polyvinyl butyral and stearates. A vertical type high-speed agitator, kneading machine, roll machine, ball mill or any other suitable mixing and agitating machine may be used for dispersion of the components of the composition of the present invention. The compositions of the present invention are suitable for use in various heat cured applications, such as resin transfer molding or filament winding. Additionally, such compositions are useful as matrix resins for composites, adhesives, coatings, molding and casting. The following examples serve to give specific illustrations of the practice of this invention but they are not intended in any way to limit the scope of this invention. EXAMPLE 1 This example illustrates the preparation of a typical hardener of the present invention. A 1 liter flask is charged with 100g of cycloaliphatic epoxy resin, CY 179® from CIBA-GEIGY Corporation, Ardsley, New York. The resin is heated to 140°C under nitrogen. 600g of 3,3'-diaminodiphenyl sulfone (13:1 amine : epoxy equivalent ratio) is added in aliquots over 1 hour with stirring while maintaining the temperature of the reaction mixture at 145-155°C. The mixture is then heated to 180°C and maintained at 180-185°C for 3 hours. The resulting product is a transparent amorphous solid resin " having a Tg of 46°C (DSC) and melting point of 76°C. FT-IR spectroscopy shows no epoxy groups in the product. Determination of amino groups by titration with perchloric acid in acetic acid solutions shows 98.7 of theoretical amount (calculated amino equivalent of the reaction product is 78, e.g. one aminohydrogen in 78 g of the product). The adduct has a viscosity of 2.37 Pa·s (2,370 cps) at 125°C and 0.38 Pa·s (380 cps) at 150°C (Brookfield). 100 parts of tetraglycidylated 4,4'-diamino-3,3'-diethyldiphenyl methane (MY 722® Epoxy resin from CIBA-GEIGY Corporation, Ardsley, New York) is mixed with 54.3 parts of the modified diaminodiphenyl sulfone prepared above (1: 0.87 epoxy : amine equivalent ratio). The mixture is stirred at 100-110°C until the hardener is completely dissolved and then degassed at 110-120°C under vacuum (400 Pa). The resulting mixture has a viscosity of 0.34 Pa·s (340 cps) at 100°C. The mixture is poured in a mold and cured at 177°C for 6 hours. The cured resin is characterized by Dynamic Mechanical Analysis (DMA) using a DuPont 983 Dynamic Mechanical Analyzer. Sample dimensions are 12.7 mm wide x 76.0 mm long x 3.2 mm thick. Samples are heated from 30°C to 350° at 10°C/min under nitrogen. Modulus retention as a function of temperature is measured under dry and wet (48 hours in boiling water prior to testing) conditions. Tg (dry and hot/wet) is determined as E" peak temperature. Flexural and tensile properties are tested according to ASTM D790 and D638, respectively. Control Sample #1 is obtained by curing epoxy resin MY 722 with 3,3'-diaminodiphenyl sulfone using a 1:0.87 epoxy-amine ratio at 177° for 6 hours. The data in Table 1 illustrates the significant increase in modulus and, especially in flexural strength for the resin cured with the diaminodiphenyl sulfone modified by cycloaliphatic diepoxide in accordance with the present invention. Modulus retention under hot/wet conditions is also considerably higher for the latter. Cured resins properties Property Example 1 Sample #1 Resin System Control Tg, °C Dry 230 230 Wet 196 198 DMA Modulus, Kpsi at 30°C dry/wet 653/600 650/580 at 120°C dry/wet 539/473 530/435 DMA Modulus, MPa at 30°C dry/wet 4502/4137 4481/3999 at 120°C dry/wet 3716/3261 3654/2999 Flexural Strength, Kpsi 25.5 19.7 Modulus 682 621 Flexural Strength, MPa 175,8 135,8 Modulus 4702 4281 Tensile strength, Kpsi 9.4 8.2 Modulus 670 625 Tensile strength, MPa 64.8 56.5 Modulus 4620 4309 Elongation, % 1.6 1.5 EXAMPLES 2-4 These examples illustrate the preparation of other typical hardeners of the present invention. Adducts of 3,3'-diaminodiphenyl sulfone and cycloaliphatic epoxy resin CY-179 with various ratios of the components are prepared using the procedure of Example 1. Data on properties of the adducts of Examples 2-4 and MY 722® epoxy resin (from CIBA-GEIGY Corporation, Ardsley, New York) cured with the adducts are presented in Tables 2 and 3, respectively. The data shows that epoxy compositions containing the hardeners of this invention exhibit good processability (low viscosity of resin-hardener mixtures), high modulus and strength, and high modulus retention under hot/wet conditions up to 150°C. Properties of the adducts of 3,3'-diaminodiphenyl sulfone (DDS) and cycloaliphatic epoxy resin CY-179® Property Example 2 Example 3 Example 4 WEIGHT RATIO DDS:CY-179® Amine:epoxy equivalent ratio 7:1 5:1 4:1 15.2:1 11:1 8.8:1 Tg, °C (DSC) 45 49 61 Viscosity at 125°C, cps 1700 4840 -- At 150°C -- 500 1070 Viscosity at 125°C, Pa·s 1.7 4.8 -- At 150°C -- 0.5 1.07 Reactivity with MY-722 epoxy resin Reaction onset temp. °C 203 198 196 Reaction peak temp. °C 253 250 244 Gel-time at 177°C, min 29 33 32 Viscosity of MY-722 adduct mixture at 100°C, cps 240 700 1380 at 100°C, Pa·s 0.24 0.7 1.38 Examples 5 and 6 Mixtures of 4,4'-diaminodiphenyl sulfone (4,4' DDS) and cycloaliphatic diepoxide CY-179 at weight ratio 6:1 (Example 5) and 5:1 (Example 6) are heated at 195-200°C under N 2 with stirring for 2 hours. Properties of the resulting adducts are presented in Table 4. Properties of the adducts of 4,4'-diaminodiphenyl sulfone (4,4'-DDS) and cycloaliphatic epoxy resin C4-179 Property Example 5 Example 6 Amine:epoxy equivalent ratio 13:1 Amine:epoxy equivalent ratio 11:1 Tg, °C (DSC) 61 72 Viscosity, cps at 125°C 17400 53100 150°C 1040 2290 Viscosity, Pa·s at 125°C 17.4 53.1 150°C 1.04 2.29 Reactivity with MY 722 epoxy resin Reaction onset temp., °C 215 217 Reaction peak temp., °C 261 265 Gel-time at 177°C, min 48 46 EXAMPLE 7 A mixture of 3,3'-diaminodiphenyl sulfone and vinylcyclohexene dioxide (Union Carbide epoxy resin ERL 4206) at 7:1 weight ratio (8:1 amine:epoxy equivalent ratio) is heated at 175-180° under N 2 with stirring for 3 hours. The resulting amorphous transparent glassy solid has a Tg of 47°C. 50 g of the adduct are dissolved in 100 g of epoxy resin MY 722® at 90°C. The resulting mixture exhibits a viscosity of 0.35 Pa·s at 100°and Gel Time of 28 min at 177°C. Properties of the cured resin (177°C, 6 hours) are presented in Table 5. Properties of MY 722 epoxy resin cured with the adduct of 3,3'-di-aminodiphenyl sulfone and cycloaliphatic epoxy resin ERL 4 206 (Example7) Property Tg °C, dry/wet 225/196 DMA Modulus dry/wet, Kpsi at 30°C 648/625 120°C 520/485 150°C 464/414 DMA Modulus dry,wet, MPa at 30°C 4468/4309 120°C 3585/3344 150°C 3199/2855 Flexural Modulus, Kpsi 760 Strength 27.8 Flexural Modulus, MPa 5240 Strength 192 Tensile Modulus, Kpsi 665 Strength 9.0 Tensile Modulus, MPa 4585 Strength 62 Elongation, % 1.5 EXAMPLES 8 AND 9 Mixtures of 3,3'-diaminodiphenyl sulfone and epoxy resin ERL 4234 (Union Carbide) at weight ratio 6:1 (Example 8) and 4:1 (Example 9) are heated at 185-195°C under N 2 with stirring for 3 hours. Properties of the obtained adducts are presented in Table 6 and properties of cured MY 722® epoxy resin using these adducts (cure cycle 177°C for 6 hours) are presented in Table 7. The data shows that the cured resin has extremely high flexural modulus and strength, high tensile modulus and excellent modulus retention. Properties of the adducts of 3,3'-diaminodiphenyl sulfone and cycloaliphatic epoxy resin ERL 4234 Property Example 8 Example 9 Amine:epoxy equivalent ratio 14.2:1 Amine:epoxy equivalent ratio 9:1 Tg, °C (DSC) 48 53 Viscosity at 125°C, cps 1500 -- Viscosity at 125°C, Pa·s 1.5 -- Reactivity with MY 722 epoxy resin Reaction onset temp., °C 203 196 Reaction peak temp., °C 250 245 Gel-time at 177°C, min 27.5 16.3 Viscosity of MY-722-adduct mixture, cps at 100°C 330 4700 125°C 210 1100 Viscosity of MY-722-adduct mixture, Pa·s at 100°C 0.33 47 125°C 0.21 11 Properties of MY 722 epoxy resin cured with the adducts of Examples 8 and 9 Property Example 8 Example 9 Tg dry/wet, °C 230/199 230/196 DMA Modulus, dry/wet, Kpsi at 30°C 641/602 663/622 120°C 516/468 542/483 150°C 461/400 488/413 DMA Modulus, dry/wet, MPa at 30°C 4420/4151 4571/4289 120°C 3558/3227 3737/3330 150°C 3179/2758 3365/2848 Flexural Modulus, Kpsi 759 767 Strength 28.5 29.3 Flexural Modulus, MPa 5233 5288 Strength 197 202 Tensile Modulus, Kpsi 680 696 Strength 8.1 10.5 Tensile Modulus, MPa 4689 4799 Strength 55.8 72.4 Elongation, % 1.3 1.7

Claims: A hardener for polyfunctional epoxy resins comprising the adduct of (1) a diaminodiphenylsulfone of the formula wherein R 1 , R 2 , R 3 and R 4 are independently hydrogen, C 1 -C 4 alkyl or halogen and (2) a cycloaliphatic diepoxide wherein the ratio of aminohydrogen equivalent of said sulfone to epoxy equivalent of said diepoxide is from 2.5:1 to 75:1. The hardener of claim 1 wherein said sulfone is 3,3′-diaminodiphenyl sulfone. The hardener of claim 1 wherein said cycloaliphatic diepoxide is selected from the group consisting of vinyl-cyclohexene dioxide, 7-oxabicycloheptane-3-carboxylic acid 7-oxa-bicyclohept-3-ylmethyl ester, 3′,4′-epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate, bis(3,4-epoxycyclohexylmethyl)adipate, 3,4-epoxycyclohexyloxirane, 2-(3′,4′-epoxycyclohexyl)-5,1″-spiro-3″,4″-epoxycyclohexane-1,3-dioxane. A curable mixture comprising (a) a polyepoxide compound and (b) a hardener according to claims 1. A curable mixture according to claim 4, wherein said hardener and said polyepoxide compound are present in stoichiometric amounts ±50%. A curable mixture according to claim 4 wherein said hardener is present in 85-100% of stoichiometry relative to said polyepoxide compound. The curable mixture of claim 4, wherein said polyepoxide compound is selected from the group consisting of glycidylated hydantoin epoxy resins, amino phenol epoxy resins, aromatic amine epoxy resins, polyglycidyl esters, cycloaliphatic epoxy resins, tetraglycidylated methylene dianiline derivatives, diglycidyl ether of bisphenol A, epoxy phenol novolacs, 1,4-butane diol diglycidyl ether, epoxy cresol novolacs, trimethylolpropane triglycidyl ether, triglycidyl tris(p-hydroxyphenyl)methane, tetraglycidyl-1,1,2,2 tetrakis (p-hydroxyphenyl)ethane, vinyl cyclohexene dioxide, N,N,N 1 ,N 1 -tetraglycidyl-4,4 1 -methylene bis-benzeneamine, N,N,N 1 N 1 -tetraglycidyl metaxylene diamine, diglycidyl aniline, resorcinol diglycidyl ether, the diglycidyl ethers of catechol, hydroquinone, diglycidyl ortho-toluidine, diglycidyl isophthalate, bisphenol A, F or S epoxy resins, triglycidyl isocyanurate, and N,N,N 1 ,N 1 -tetraglycidyl 1,3 bis-aminomethylcyclohexane. The curable mixture of claim 4, wherein said polyepoxide compound is a tetraglycidylated methylene derivative. A hardener according to claim 1 wherein the radio of aminohydrogen equivalent of said sulfone to epoxy equivalent of said diepoxide is from 5:1 to 15:1.

Inventors: BLYAKHMAN YEFIM, BLYAKHMAN, YEFIM
Applicants: CIBA GEIGY AG, CIBA-GEIGY AG
Application year: 1992
Main classification: C08G59
IPC codes: C08G59, C07C317