Method of producing a coated optical fiber

Abstract: A coated optical fiber of the invention is constructed by coating an energy beam curable resin onto the outer periphery of a wiredrawn optical fiber and curing the resin by radiating an energy beam to the resin to thereby provide a coating layer on the optical fiber. The peak temperature of the mechanical loss tangent Tan δ of the energy beam curable resin prior to curing is 25°C or lower.

Description: BACKGROUND OF THE INVENTION The present invention relates to a method for producing a coated optical fiber including a coating layer formed by curing a resin on the outer periphery of an optical fiber by means of radiation of energy beams such as an ultraviolet ray. In more detail, the present invention relates to the improvement in the coating resin used in said method. An optical fiber is used in such a manner that it is coated with a resin for the purpose of mechanical protection and, as the coating resin, from the viewpoint of productivity, there is generally used an energy beam curable resin which can be cured by radiation of ultraviolet ray or the like. Fig. 1 is a schematic view showing the outline of an apparatus for manufacturing a general coated optical fiber. In Fig. 1, to manufacture a coated optical fiber 7, a wiredrawn optical fiber 3 is coated with an energy beam curable resin by a resin coating device 4 mainly consisting of a die and a point, and the curable resin is cured within a curing device 5 to thereby provide a single coating layer or a plurality of coating layers of resin, and then the optical fiber with such resin coating layer or layers is taken up by a take-up device 8. Fig. 2 shows an example of a section of the coated optical fiber 7 manufactured in this manner. In general, the coated optical fiber has a double coating structure consisting of a buffer layer 10 and a protective layer 11 which are respectively made of an energy beam curable resin applied to and cured on the periphery of the optical fiber 3 composed of glass. On the other hand, in recent years, with the spread of the amounts of production of optical fibers, the wire-drawing speeds of the optical fibers have been steadily increasing. For this reason, such a strong need is requested for a resin to be used as a coating material that it can be coated to the surface of the glass in good and uniform condition within a wide range of wiredrawing speeds. There is disclosed in the publication presented in Applied optics, Volume 20, Number 23 (1981) by U.C. Peak et al, a newly designed apparatus including a UV energy curing system which is capable of coating a fiber with a 50µm thickness UV curable resin at a speed in excess of 5m/s. Normally, if the wiredrawing speed of the fiber is increased, then there arises a phenomenon that the resin is hard to attach to the glass, because the fiber enters a die for a first layer before the glass melted in a furnace is cooled down perfectly. Consequently, on the high speed side, the coating diameter of the resin is decreased and, as a result of this, the coating resin is caused to vary in thickness according to the wiredrawing speeds. In order to solve this problem, for example, in Japanese Patent Unexamined Publication No. 55-10470, there is proposed a method in which glass is forcibly cooled down prior to entrance into a die to thereby prevent a resin from being coated poorly, and the temperature of the glass is controlled to thereby control the covering diameter to a desired thickness. However, if the glass is actually cooled down and is then wiredrawn at a high speed, then the covering diameter of the first coating layer tends to be larger than that obtainec at a low speed. It is believed that this is because the pulling force of the glass is increased due to the increased wiredrawing speed and thus a larger quantity of resin is coated to the glass when compared with coating at the low speed. As a result, in order to keep the covering diameter constant in a wide range of wiredrawing speeds, the temperature of the glass must be frequently and finely adjusted, which requires a very complicated controlling operation. SUMMARY OF THE INVENTION Thus, it was the object of the present invention to overcome the limitations of the prior art and to provide a method of producing a coated optical fiber which allows the fiber to obtain a constant diameter covering over a wide range of wiredrawing speeds. The present invention achieves its object by a method comprising the steps set out in claim 1. The present inventors, after the investigation of the above-mentioned problems from various aspects, have found that by measuring the dynamic viscoelasticity property of an energy beam curable resin in the liquid state thereof, which is coated on an optical fiber, selecting only the resin with a peak of the mechanical loss tangent Tan δ, Tan δ being defined by the complex modulus of elasticity, occurring at a temperature of 25°C or lower and conducting the wire-drawing, a coated optical fiber having a constant covering diameter can be produced in a wide range of wiredrawing speeds without requiring the fine adjustments of the glass temperature specially. In this manner, the present inventors have completed the present invention. In other words, according to the present invention as defined in claim 1, a coated optical fiber is manufactured by coating an energy beam curable resin onto the outer periphery of a wiredrawn optical fiber and curing the resin by radiation of energy beams, whereby the resin has a peak of the mechanical loss tangent Tan δ, defined by the complex modulus of elasticity, this peak occurring at a temperature of 25°C or lower. The optical fiber is wiredrawn preferably at a production speed of 10 m/s (600 m/min), or more. The viscosity of the energy beam curable resin at a temperature of 25°C is preferably in the range of 2 Pa s to 3 Pa s (2,000 cps - 3,000 cps). BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a schematic view showing the outline of an apparatus for manufacturing a general coated optical fiber; Fig. 2 is a section view of a general coated optical fiber; Fig. 3 is a graphical representation of the temperature-loss tangent Tan δ curves of coating resins employed in the illustrated embodiment of the invention; and Fig. 4 is a schematic view of an example of device for obtaining the Tan δ. DETAILED DESCRIPTION OF THE INVENTION The present invention will be described below in detail. In the present invention, in order to provide a coated optical fiber having a stable covering diameter in a wide range of production speeds, for example, in a range of 3.3 m/s (200 m/min), or more, preferably 10 m/s (600 m/min), or more, the peak of mechanical loss tangent Tan δ of the energy beam curable resin prior to curing thereof must occur at temperature of 25°C or lower. The mechanical loss tangent Tan δ is obtained from the dynamic viscoelasticity of a sample evaluated by, for example, an oscillating coaxial cylinder viscometer as shown in Fig. 4 in which an outer cylinder 22 is vibrated and a shear stress applied to an inner cylinder 23 with a spring 21 is detected. When the shear strain ε and the shear stress a generated in a sample 24 are expressed by ε = ε 0 exp (iωt) and σ = σ 0 exp (iωt), where, i: imaginary number unit, ω: angular velocity, and t: time, a complex modulus of elasticity G *(ω) and the mechanical loss tangent Tan δ of the sample are given by the following equation: G*(ω) = σ/ε = G'(ω) + iG"(ω) Tan δ = G"(ω)/G'(ω) where, G'(ω): storage modulus of elasticity and G''(ω): loss modulus of elasticity. The value of Tan δ of a resin is varying not only with angular velocity but also with the temperature of the resin greatly. The tendency of the values, as can be understood from a graph shown in Fig. 3, provides an upwardly projecting curved line having the maximum peak at a certain temperature. In general, the resin shows its property as an elastic body (a non-Newtonian fluid) more outstandingly as the temperature at the peak of Tan δ is higher than a working temperature. The lower the temperature for the peak of Tan δ of the energy beam curable resin, serving as a coating resin, in the liquid state thereof prior to curing is, the smaller the variations of the covering diameter are. If the peak temperature is 25°C or lower, then the diameter variations can be reduced down to a very small level such as ± 2 µm or less in a range of wiredrawing speeds of 3.3 - 16.6 m/s (200 - 1,000 m/min). If a coating resin having the Tan δ peak temperature exceeding 25°C is used, then the variations of the covering outside diameter are increased. The increment in the variations makes it impossible to manufacture the coated optical fiber stably in a wide range of production speeds, with the result that it is difficult to produce the coated optical fiber of high quality. It should be noted here that the temperature-Tan δ characteristic of the coating resin in the present invention is an invariable index independent of the composition of the resin. For this reason, the invention can be applied to all of coating resin materials for the optical fiber manufactured generally in such a method as shown in Fig. 1. The Tan δ peak temperature of the resin can be realized by changing the cohesive power of an oligomer and the forms and lengths of chains forming the skeleton of the resin. However, it is difficult to calculate the value of the peak temperature with accuracy only by means of a theoretical design. On the other hand, Tan δ can be measured easily by use of a concentric double cylinder method as disclosed in the "Rheology, second edition" written by Tsurutaro Nakagawa and published by Iwanami Zensho, at page 205, or a cone plate method which is an improved version of the concentric double cylinder method. Although the viscosity of the energy beam curable resin serving as the coating resin is not limited specially, in order to control the outside diameter of the coating resin to a set value, it is desirable that the viscosity of the resin is 5 Pa s (5,000 cps) or less, preferably in a range of 2 - 3 Pa s (2,000 cps - 3,000 cps). For example, if the resin viscosity is high and on the order of 6 Pa s (6,000 cps), then the variations of the resin outside diameter remain in an allowable range, but the absolute value of the outside diameter tends to be higher than the set value. As the energy beam curable resin used to coat the optical fiber, in general, there is available a resin which can be easily cured by means of light such as an ultraviolet ray, heat or the like. The resin includes, as the represent-ative thereof, an ultraviolet ray curable urethane (meta-)acrylate resin, an ultraviolet ray curable silicone resin, a thermosetting silicone resin, an ultraviolet ray curable epoxy (meta-)acrylate resin, an ultraviolet ray curable silicone (meta-)acrylate resin, an ultraviolet ray curable ester (meta-)acrylate resin, a polyvinylidene fluoride resin, and the like. The resin coating may be a single layer or a plurality of layers. In the case of two layers, one of the layers is composed of a relatively soft resin material acting as a protective layer (a primary coating layer) to protect the surface of the bared optical fiber, and the other is formed of a relatively hard resin material acting as a buffer coating (a secondary coating) to facilitate the handling of the optical fiber. It is well known that the composition of the energy beam curable resin affects the rheology characteristic in the liquid state. For example, in a thesis titled as "Rheology of a UV Ray Curable Coating in the Optical Fiber High-speed Wiredrawing" written by Hiroyuki Ito and other three persons, which was provided as previous information to the Fifth Photopolymer Conference, 1988, there is obtained a conclusion that, from the measurement of the angular velocity-Tan δ properties of resins having different compositions prior to curing, in order to suppress the vibration of the bared optical fiber when the resin is coated thereto, a resin having a small Tan δ in a high angular velocity area is desirable. As a result of the examination of a relationship between the optical fiber wiredrawing speeds and the covering diameters (that is, the actually attached amounts of the resin), the present inventors have found that the reason why the covering diameter of the resin is increased as the optical fiber wiredrawing speeds are increased is a Barus effect. In other words, when the coating resin is passing through a die hole, if the passing time of the coating resin is short, then a molecular chain is not loosened completely under a shearing stress to thereby store part of a shearing energy as an elastic deformation, with the result that the compression stress of the resin is released at the exit of the die hole to thereby cause the covering diameter to increase. The increase of the diameter due to the Barus effect is larger as the passing time of the covering resin through the die hole is shorter and, therefore, the diameter is increased as the wiredrawing speed is higher. In view of the above, in order to minimize the influences of the Barus effect, it is effective to select, as a resin used to coat the optical fiber, a resin having a small elastic property, that is, a low Tan δ peak temperature. After several repeated experiments conducted from the above viewpoint, the present inventors have found the fact that, by selecting a resin having the Tan δ peak temperature of 25°C or lower in the liquid state, the variations of the covering (coating) diameter can be suppressed within ± 2 µm in a wide wiredrawing speed range of 3.3 - 16.6 m/s (200 - 1,000 m/min). [Examples] Description will be given below of examples of a coated optical fiber according to the present invention. However, the scope of the present invention is not limited to the examples illustrated in this specification. As a coating resin to be used as a buffer coating layer 10, there are employed five kinds of ultraviolet ray curable resins as shown in Table 1. Five kinds of coated optical fibers 7 as shown in Fig. 2 are manufactured by an optical fiber manufacturing method as shown in Fig. 1. For reference, in Fig. 3, there are shown curved lines for the temperature-Tan δ of resins A - C. The resins used are all composed mainly of an ultraviolet ray curable urethane acrylate resin and the structure of an oligomer and the density of a monomer are changed to thereby vary the values of the viscosities and the Tan δ peak temperatures of the resins. Here, the Tan δ peak temperatures were measured with constant angular velocity by use of an MR-3000 liquid meter manufactured by Rheology Co. (that is, according to the cone plate method). Protective coating layers 11 are all formed of ultraviolet ray curable urethane acrylate resins having the same Young's modulus of 70 kg/mm 2 . Glass having a diameter of 125 µm was used, the diameter of a hole in a die was selected in such a manner that the buffer coating layer 10 has a set outside diameter of 195 µm and the protective coating layer 11 has a set outside diameter of 250 µm, the above-mentioned coating resins were used, and the wiredrawing speeds were changed in the range of 3.3 - 16.6 m/sec (200 - 1,000 m/min), whereby coated optical fibers were manufactured. In Table 1, there are shown the measured results of the coated diameters (outside diameters) of the respective coated optical fibers. From Table 1, it is found that the variations of the outside diameters are reduced as the Tan δ peak temperatures of the coating resins are lowered and, if the peak temperature goes down to a temperature of 25°C or less, then the diameter variations can be suppressed to a value of ± 2 µm or less in a wiredrawing speed range of 3.3 - 16.6 m/s (200 - 1,000 m/min). Especially, due to the fact that the outside diameter of the coated optical fiber constructed according to the present invention varies little even at a high wiredrawing speed of 10 m/s (600 m/min), or more, the present invention can produce a coated optical fiber of very high quality even if the wire-drawing speeds are varied. However, in the case of the resin E which has a high viscosity of 6 Pa s (6,000 cps), although the variation of the outside diameter was found in the allowable range, the absolute values of the coating outside diameter were found to show a tendency to be slightly higher than the set values. Therefore, for the absolute value of the coating outside diameter, in order to finish the coating outside diameter as desired, the viscosity of the resin is desired to be 5 Pa s (5,000 cps) or less. In the above examples, evaluation was conducted only on the buffer coating layer 10. However, of course, a similar effect can be expected of the protective coating layer 11 as well. Also, in the above examples, as the coating material resin, the ultraviolet ray curable urethane acrylate resin is used. However, a similar effect can also be expected when other energy beam curable resins are used, which include an ultraviolet ray curable silicone resin, a thermosetting silicone resin, an ultraviolet ray curable epoxy acrylate resin, an ultraviolet ray curable silicone acrylate resin and the like. As has been described heretofore, the present invention can provide a coated optical fiber having a coating diameter which is stable in a wide range of producing (wire-drawing) speeds.

Claims: A method of producing a coated optical fiber, comprising the steps of: forming an optical fiber by wiredrawing; coating said optical fiber with an energy beam curable resin; and curing said energy beam curable resin by irradiation of an energy beam, characterized by carrying out said optical fiber coating step with an energy beam curable resin having a peak of the mechanical loss tangent Tan δ, defined by the complex modulus of elasticity and being measured by a dynamic viscoelasticity measuring method using a constant angular velocity, this peak occurring at a temperature of 25°C or less prior to being cured. A method of producing a coated optical fiber as claimed in claim 1, wherein said optical fiber is formed at wiredrawings speeds of 10m/s or higher. A method of producing a coated optical fiber as claimed in claim 1, wherein the viscosity of said energy beam curable resin at a temperature of 25°C is selected in the range of 2 Pa s to 3 Pa s (2,000 cps to 3,000 cps). A method of producing a coated optical fiber as claimed in claim 1, wherein said energy beam curable resin is one selected from a group consisting of an ultraviolet ray curable urethane acrylate resin, an ultraviolet ray curable silicone resin, a thermosetting silicone resin, an ultraviolet ray curable epoxy acrylate resin, an ultraviolet ray curable silicone acrylate resin, an ultraviolet ray curable ester acrylate resin, and a polyvinylidene fluoride resin.

Inventors: HATTORI TOMOYUKI, HOSOYA TOSHIFUMI, KOBAYASHI KOHEI, HATTORI, TOMOYUKI, HOSOYA, TOSHIFUMI, KOBAYASHI, KOHEI, HATTORI, TOMOYUKI, YOKOHAMA WORKS OF SUMITOMO, HOSOYA, TOSHIFUMI, YOKOHAMA WORKS OF SUMITOMO, KOBAYASHI, KOHEI, YOKOHAMA WORKS OF SUMITOMO
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD
Application year: 1992
Main classification: G02B6
IPC codes: B29C35, C03C25, G02B6