Catalyst for treating wastewater, process for producing it, and process for trating wastewater with the catalyst

Abstract: The present invention provides a wastewater treatment, a catalyst therfor, and a production process for the catalyst. The catalyst comprises oxide of iron as an [A] component and at least one element as a [B] component selected from cobalt, nickel, cerium, silver, gold, platinum, palladium, rhodium, ruthenium and iridium. The [A] can be an oxide component containing iron and at least one element selected from titanium, silicon and zirconium.

Description: The present invention relates to a catalyst for wet oxidation treatment of wastewater containing organic compounds etc., to a process for producing the catalyst and a process for treating wastewater with wet oxidation in the presence of the catalyst. There have been hitherto known methods for treating wastewater, such as a biochemical method called the activated-sludge method, and a wet oxidation treatment called the Zimmerman method. The activated-sludge method requires a long time to decompose organic compounds; it also necessitates dilution of wastewater to a concentration suitable for the growth of algae and bacteria, so that it has the defect that a large area is required for the treating facilities. The Zimmerman method comprises treating wastewater in the presence of an oxygen-containing gas under high temperature and high pressure to decompose organic compounds in the wastewater. One proposed method involves use of various kinds of oxidation catalysts to accelerate reaction rate. The oxidation catalyst used here is a catalyst with a compound of a noble metal such as palladium, platinum or the like supported on a carrier such as alumina, silica, silica gel, active carbon or the like. In general, it is rare that the chemical species included in wastewater to be treated is always the same. Thus, there are many cases where a nitrogen-containing compound is included besides a nitrogen-free organic compound. However, wastewater including a nitrogen-containing compound such as an amine compound, an amide compound, an amino acid compound or the like is not treated with satisfactory efficiency by the above-mentioned methods. Wastewater including an amine is usually treated by a binding treating method in which an anionic macromolecule binding agent is used. This method comprises gathering an amine by the anionic macromolecule binding agent and eliminating formed precipitate ( or sludge ) from wastewater. Also, there has been attempted an adsorbent method which comprises bringing wastewater into contact with various kinds of adsorbents such as active carbon, activated clay, silica gel, complex oxide gel and the like, and adsorbing the amine onto the adsorbent for eliminating it from the wastewater. Since sludge formed by the binding treating method contains amines, it should not be disposed of without further treatment to decompose the amines in the sludge . In addition, the macromolecular binding agent is expensive, so cost for the treatment becomes high. Concerning the adsorbent method, the elimination percentage of amines is not satisfactory. Since the adsorbing power of an adsorbent easily decreases, there is a problem in durability of the adsorbent. Since the wet oxidation process is unavoidable in the wastewater treatment, it will be convenient if an arrangement is made so as to decompose nitrogen-containing compound included in the wastewater in the course of the wet oxidation process. On the other hand, treatment for wastewater including sulfur-containing compound has been so far carried out by different methods depending upon the state and nature of the sulfur-containing compound. For example, in the case of wastewater including organic sulfur compound, a biological treatment is generally carried out. However, for wastewater containing thiophene and the like, which badly affects organisms in sludge, biological treatment cannot be applied and, accordingly, combustion treatment etc. is carried out. Wastewater containing a sulfide such as sodium sulfide or the like (for example, wood digestion wastewater in paper and pulp manufacture, wastewater from a coke oven in steel manufacture, wastewater after fiber-washing, wastewater from a plant for petroleum chemical products such as ethylene, BTX and the like, as well as wastewater from a coal gasification plant, a petroleum-refining plant, a rayon factory and a dyeing plant) has been mostly treated by a method which comprises adding iron chloride into the wastewater to solidify sulfur ions, removing solid iron sulfide by solid-liquid separation, adjusting pH of the separated solution, carrying out a biological treatment of the solution, and then discharging the treated wastewater. Also, wastewater containing a sulfite salt and thiosulfate salt (for example, wastewater from a wood kiln of a pulp-making factory, wastewater from photographic developing, wastewater from metal treatment as well as alkaline wastewater used to absorb sulfur dioxide and the like) is treated by a method which comprises subjecting wastewater to neutralization-precipitation treatment followed by biological treatment and then discharging the treated wastewater. When wastewater containing a sulfur-containing compound is treated by either one or both of biological treatment and combustion treatment, there exist the undermentioned problems to be solved. In the biological treatment, it is necessary to adjust the source wastewater by diluting it with water so that organisms are not badly affected. Therefore, the wastewater volume to be treated is high and facilities for the biological treatment must be arranged on a large scale, so that there is a serious problem in the necessary cost and so forth. Also, in the combustion treatment, when the heat amount generated from wastewater is low, a supplementary fuel must be added and also, because a large amount of sulfur is usually included in the wastewater, a large amount of sulfur oxides is formed and, therefore, it is necessary to arrange a desulfurizer. Next, when wastewater including a sulfur-containing compound such as sulfide is treated, if a method which comprises removing the sulfur-containing compound as iron sulfide by adding iron chloride is applied, sludge having iron sulfide as a main component is formed; also, this method is complicated as a treating procedure, because it consists of the following steps: injection of solution of chemicals, solid and liquid separation, pH control and biological treatment. The organic halogen compounds have various kinds of usage because of their stability. Since they are nonflammable and have great capability to degrease, they have been used in large amounts as a degreasing cleaner in metal, machinery and electronics industries as well as a cleaner for dry cleaning. On the other hand, the compounds have brought about problems in various fields. In general, since the organic halogen compounds are difficult to decomposite, they are seriously accumulating in the natural environment and, as a result, ground water pollution has emerged everywhere. Furthermore, some of the organic halogen compounds have been found to have carcinogenic nature against human bodies and, thus, trichloroethylene, tetrachloroethylene, 1,1,1-trichloroethane and the like have been designated as regulation items of the water-pollution preventive law of 1989, because of concern about influence on human health. Concerning treatment of the organic halogen compounds, various methods have been proposed or used, which are roughly classified as degradation and nondegradation methods. Concerning the non-degradation method, there are a packed tower stripping method, a volatilizing method by means of exposing to air or heating, and an adsorption method using active carbon or macromolecules. Concerning the volatilizing method, the operation itself is very simple and of low cost, but the method comprises only evaporating organic halogen compounds from the liquid phase or solution and scattering them in air and, therefore, basically it does not settle environmental pollution caused by organic halogen compounds. Concerning the adsorption method, a secondary processing such as a recording process after adsorption and a process to treat the adsorbent becomes necessary. Concerning the degradation method, there are listed an irradiation method, a microorganism degradation method, a redox method and so forth. The irradiation method, of which representative examples are a photodecomposition method using a semiconductor as a catalyst and a radiation-irradiating method using radiation, is still in an experimental stage and cannot be adopted for practical use. The microorganism degradation method takes a long time for treatment and its efficiency in treatment is unstable and, therefore, there exist many problems for practical use. Concerning the redox method, a method using an oxidizing agent such as ozone, hydrogen peroxide or the like and a method of reductive degradation method using iron have been attempted. However, where an organic halogen compound exists in a high concentration, a method of highly efficient treatment has not yet been invented either as a nondegradation method or as a degradation method. In the volatilizing method, a large amount of organic halogen compounds is discharged into air and, therefore, the method is not a fundamental solution for the organic halogen compounds to be treated. The adsorption method is short in the break-through time in a case of high concentration, so it is not practical. Concerning the degradation method, highly effective decomposition has not yet been practical, and also there exists a problem that harmful decomposition products are secondarily generated. In short, a practical and fundamental method to remove the organic halogen compounds has not yet been developed. WO-A-8908079 discloses various wastewater treatment catalysts; one is Ti0 2 , and another is Fe 2 0 3 /Pt. Derwent Abstract of JP-A-56089893 discloses decomposing organic matter in wastewater by oxidation with H 2 0 2 in presence of magnetic iron oxide catalyst (e.g. Ni-containing ferrite). Derwent Abstract of JP-A-49095462 discloses treating wastewater containing organic or inorganic materials with oxygen-containing gas in the presence of catalyst containing Cu oxide and two metallic oxides selected from Co, Fe, Ce, Sn, Ni and Zn oxides. Derwent Abstract of JP-A-48095388 discloses treatment of water to reduce COD and turbidity with air and catalyst containing Fe 2 0 3 and Ni on an aluminosilicate mineral support. Derwent Abstract of JP-A-58011095 discloses a wastewater treatment catalyst composition (for decomposing PVA) which contains certain metal (Pd, Pt, Ni etc.) with semiconductor which is one or more than two of compounds selected from metal oxides, phosphides, sulphides, arsenides, selenides and tellurides exemplified by Ti0 2 , SrTi0 3 , Zn0, Fe 2 0 3 , CdS, CdSe, CdTe, GaP, GaAs, InP, ZnS, ZnSe etc. The present invention provides a catalyst for treating wastewater, comprising: component [A] comprising an oxide component which contains iron and at least one element selected from titanium, silicon and zirconium; and component [B] comprising at least one element selected from cobalt, nickel, cerium, silver, gold, platinum, palladium, rhodium, ruthenium and iridium; wherein component [A] is contained in a range of from 90 to 99.95% by weight and component [B] in a range of from 0.05 to 10% by weight with the total of components [A] and [B] being 100% by weight, and wherein component [A] contains iron in a range of from 4.95% to 95% by weight as oxide, at least one element selected from titanium, silicon and zirconium in a total range of from 4.95% to 95% by weight as oxide, and iron and at least one element selected from titanium, silicon and zirconium in a total range of from 90 to 99.95% by weight as oxide. The present invention further provides a process for treating wastewater comprising wet oxidation of the wastewater using a solid catalyst according to the invention with an oxygen-containing gas supplied at a pressure maintaining the wastewater in the liquid phase. The present invention also provides a process for producing a catalyst for treating wastewater, comprising obtaining a coprecipitate containing iron and at least one element selected from titanium, silicon and zirconium; calcining the coprecipitate to oxide containing iron and at least one element selected from titanium, silicon and zirconium; and making this oxide contain at least one element selected from cobalt, nickel, cerium, silver, gold, platinum, palladium, rhodium, ruthenium and iridium. It also provides a process for producing a catalyst according to the invention for treating waste water, comprising an oxide component containing iron and at least one element selected from titanium, silicon and zirconium, adding a salt of at least one element selected from cobalt, nickel, cerium, silver, gold, platinum, palladium, rhodium, ruthenium and iridium to said oxide; and calcining the resulting mixture. The oxide component may be obtained by calcining an iron-containing compound and a compound of at least one element selected from titanium, silicon and zirconium. The present invention also provides a process for producing a catalyst according to the invention for treating waste water comprising obtaining a coprecipitate containing iron, at least one element selected from titanium, silicon and zirconium, and at least one element selected from cobalt, nickel, cerium, silver, gold, platinum, palladium, rhodium, ruthenium and iridium, and calcining the coprecipitate. Wastewater to be treated in this invention can include nitrogen-free organic compounds, nitrogen-containing compounds, sulfur-containing compounds or organic halogen compounds or the like. The nitrogen-free organic compounds are, for example, aldehydes, alcohols, lower organic acids such as acetic acid, formic acid and the like. The nitrogen-containing compounds are, for example, amine compounds, amide compounds, amino acid compounds and the like. The amine compounds may be any one of a primary amine, a secondary amine, a tertiary amine, and a quarternary amine salt. Practical examples are alkyl amines such as methylamine, dimethylamine, trimethylamine, propylamine and the like; alkylene diamines such as ethylenediamine, trimethylenediamine and the like; alkanol amines such as ethanolamine, triethanolamine and the like, all of which are aliphatic amines. In addition, examples are aromatic amines such as aniline and the like; and nitrogen-containing heterocyclic compounds such as pyridine, picoline and the like. The amide compounds contain a group ( RCONH- ) made by combining an amino group with an acid group in its molecule. Practical examples are formamide, methylformamide, acetoamide, ethylformamide, methylpropionamide, dimethylformamide, diethylformamide, dimethylacetoamide, N-methylpyrrolidine and the like. The amino acid compounds contain a carboxyl group and an amino group in the same molecule and, are called α-amino acids, β-amino acids, γ-amino acid or the like. Practical examples are aliphatic amino acids such as glycine, alanine, valine, leucine, serine, cystine, aspartic acid, glutamic acid, lysine, arginine and the like; amino acids having an aromatic ring such as phenylalanine, tyrosine and the like; amino acids having a heterocyclic ring such as histidine, tryptophan, proline and the like; and others. The nitrogen-containing compound need not be dissolved in water; even if it is floating or suspended or so forth, it can be decomposed by a treating process of this invention. A nitrogen-containing compound in wastewater may be present alone or in a mixture of plural kinds. The nitrogen-containing compound in wastewater for which the present invention can be applied is not especially limited, but its concentration is usually in a range of from 10 to 100,000 mg/l. The sulfur-containing compounds in the present invention are inorganic or organic compounds containing at least one sulfur atom other than as sulfuric acid ( SO 4 2- ). The compounds include, for example, a sulfide such as hydrogen sulfide, sodium sulfide, potassium sulfide, sodium hydrogen sulfide, sodium polysulfide and the like; thiosulfuric acids and their salts such as sodium thiosulfate, potassium thiosulfate and the like; sulfurous acids and their salts such as sodium sulfite and the like; trithionic acid, tetrathionic acid, and their salts such as sodium trithionate; thiols such as ethylmercaptan, thiophenol, 3,4-mercaptotoluene, dimercaptol, cystein and the like; thioacetals such as diethylthioacetal, 1-ethoxy-1-( methylthio )cyclopentane and the like; thiosulfites such as methyl thiosulfite, ethyl thiosulfite and the like; sulfides such as ethylsulfide, 1-( methylthio )propane, methionine and the like; thiocarbonates and their derivatives such as trithiocarbonate, sodium S-methyldithiocarbonate, diethyl trithiocarbonate, potassium O-ethyldithiocarbonate, S-methyl hydrogen thiocarbonate and the like; thio-acids and their derivatives such as sodium thiosulfate, hexanethio-acid, 1-piperidinecarbodithio-acid, hexanedithio-acid, O-thioacetic acid, S-thioacetic acid, dithiobenzoic acid, sodium dithioacetic acid, a S-ethyl ester of hexanethio-acid, an O-ethyl ester of hexanethio-acid, hexanethioyl chloride, 2-thiophenecarbothioamide, dibenzoic acid thioanhydride, di( thiobenzoic acid ) anhydride and the like; thiocyans, thiocyanic acids and their salts such as rhodan, thiocyanic acid, potassium thiocyanic acid, ammonium thiocyanic acid and the like; thiocyanic acid esters such as methyl thiocyanate, ethyl thiocyanate, allyl thiocyanate and the like; thiosaccharides such as 1-thioglucose, S-methyl-5-thio-D-ribose and the like; thiazyl compounds such as fluorinated trithiazyl and the like; thiazines such as 1,2-thiazine, 1,3-thiazine, methylene blue and the like; thiazoles such as 1,3,4-thiadiazole, 1,3-thiazole, thioflavine, primuline and the like; thiocarbamides such as thiocarbamide, thiosemicarbamide, dithizone and the like; thiopyranes such as α-thiopyran, γ-thiopyran, 3-methyl-4H-thiopyran and the like; thiophenes such as thiophene, methylthiophene, thionaphthene, thiophthene and the like; polysulfides such as diphenyltrisulfide, diphenyldisulfide, 1,4-bis( methyldithio )cyclohexane and the like; thioaldehydes such as hexanethial, cyclohex anecarbothioaldehyde and the like; thioketones such as cyclohexanethione, 1,3-dithiorane-2-thione, 2,4-pentanedithione and the like; sulfinyl compounds such as thionyl chloride, diethylsulfoxide and the like; sulfonium compounds such as trimethylsulfonium iodide and the like; sulfonyl compounds such as sulfuryl chloride, sulfonylamide, diethylsulfone, thiophene-1,1-dioxide and the like; sulfonic acids and their salts such as dodecylbenzenesulfonic acid, sodium p-toluenesulfonate, naphthalinesulfonic acid, sulfanilic acid, sulfobenzoic acid, methyl orange, benzenedithiosulfonic acid and the like; sulfonic acid derivatives such as ethyl methanesulfonate and the like; sulfinic acids and their derivatives such as 1-piperidinesulfinic acid and the like; sulfates such as dimethylsulfate, methyl hydrogen sulfate and the like; sulfamides and their derivatives such as phenylsulfamide and the like. These compounds may be soluble in an aqueous medium or exist as a suspending substance in an aqueous medium. Also, even if sulfuric acid is contained in wastewater, there is no problem for treating it. The organic halogen compounds in this invention are organic compounds containing one or more halogen atoms in the molecule. Preferable examples for this are an aliphatic organic chloro compound such as methyl chloride, ethyl chloride, dichloroethylene, trichloroethylene, tetrachloroethylene, 1,1,1-trichloroethane, vinyl chloride and the like; an aliphatic organic bromo compound such as methyl bromide, ethyl bromide, vinyl bromide and the like; an aromatic organic chloro compound such as monochlorobenzene, dichlorobenzene, benzyl chloride and the like; an aromatic organic bromo compound such as benzyl bromide, benzylidene bromide and the like; flon such as trichlorofluoromethane, dichlorofluoromethane and the like. The catalyst for treating wastewater of this invention uses an oxide as an A component in the catalyst, which includes iron ( hereinafter, referred to as "component ( i )" ) and at least one kind of element ( hereinafter, referred to as "component ( ii )" ) selected from a group consisting of titanium, silicon and zirconium. The catalyst A component is, for example, a mixture of an oxide powder of the component ( i ) with an oxide powder of the component ( ii ). In a preferable case, a precipitate obtained from a solution containing an element in either one member of the components ( i ) and ( ii ) is well mixed with a salt slightly soluble in water containing an element in the other member of the components ( i ) and ( ii ) ( which may be a precipitate obtained from a water-soluble salt containing an element in the other member or may be an oxide containing an element in the other member ), and the obtained mixture is calcinated to convert into an oxide, which is then used as the catalyst A component. The calcinated product of the mixture is an oxide, which is derived from a form of the components ( i ) and ( ii ) mixed at a microscopic level more intimately than mixture of the forementioned oxide powders. A further preferable catalyst A component is an oxide obtained by calcinating a coprecipitate from a solution containing the components ( i ) and ( ii ). This calcinated compound of the coprecipitate is not a simple mixture consisting of an oxide of the component ( i ) and an oxide of the component ( ii ), but it is a compound in which the components ( i ) and ( ii ) are well mixed at a microscopic level to form an oxide. It can be recognized that novel physical properties emerge, which are not observed in an oxide of each component alone. In the catalyst of this invention, the proportions of the components are 90 to 99.95 % by weight for the catalyst A component and 0.05 to 10 % by weight in form of a metal or a compound for the B component. If the B component is out of the above range, the oxidation activity may be insufficient. In addition, if the A component is out of the above range, the hot water resistance and acid resistance may be insufficient, so it is unfavorable in a viewpoint of catalysis durability. Furthermore, in the catalyst A component, the component ( i ) is in a range of from 4.95 to 95 % by weight as an oxide and the component ( ii ) is in a range of from 4.95 to 95 % by weight as an oxide, and the total of the components ( i ) and ( ii ) is in a range of from 90 to 99.95 % by weight. If they deviate from these ranges, the hot water resistance and acid resistance may be insufficient and it is unfavorable in a point of catalyst durability. In this invention, although it is preferable that the catalyst A component is prepared using coprecipitation method, the A component may be made as a complex oxide or the like by other production processes. A method of preparing the A catalyst component by a coprecipitation method is hereinafter explained by taking, as an example, a case where the A component is a TiO 2 - Fe 2 O 3 compound ( this TiO 2 - Fe 2 O 3 compound is, as described above, an oxide that TiO 2 and Fe 2 O 3 make in a closely blended form and, hereinafter, the same ). A precipitate is made by dissolving titanium sulfate (a titanium source compound) and iron nitrate (an iron source compound) in water and mixing them sufficiently, and by adding an aqueous ammonia. This precipitate is taken by filtration, washed, dried, and calcinated at a temperature in a range of from 300 to 750 °C . To present a concrete example, this method is carried out as follows. That is, the above-described titanium source compound and iron source compound are taken so that a weight ratio of TiO 2 and Fe 2 O 3 is in a specific value, and under a condition of an aqueous acidic solution, the titanium and iron are adjusted to a concentration of from 1 to 100 g per liter upon converting into oxides, and the aqueous acidic solution is maintained at a temperature in a range of from 10 to 100 °C . Into this solution is added dropwise with stirring an aqueous ammonia as a neutralizing agent and, an obtained solution is stirred for a period of from further 10 minutes to 3 hours at a pH in a range of from 2 to 10, whereby a coprecipitated compound ( a coprecipitate ) consisting of titanium and iron is formed. The formed precipitate is taken by filtration, well washed, dried at a temperature in a range of of from 80 to 140 °C for a period of from 1 to 10 hours, and calcinated at a temperature in a range of from 300 to 750°C for a period of from 1 to 10 hours, whereby a TiO 2 - Fe 2 O 3 compound is obtained. In this invention, in order to obtain the catalyst A component by a coprecipitation method, it is necessary to dissolve elements of the components ( i ) and (ii ) in water. To dissolve an element of the component ( i ) in water, for example, a water-soluble iron compound may be dissolved in water. To dissolve an element of the component ( ii ) in water, for example, a water-soluble compound or sol of the element may be dissolved in water. A preferable water-soluble iron compound ( an iron source ) is selected from, for example, inorganic iron compounds such as iron nitrate, iron sulfate, iron chloride and the like; and organic iron compounds such as iron oxalate, iron citrate and the like. A preferable water-soluble titanium compound or sol ( a titanium source ) is selected from, for example, inorganic titanium compounds such as titanium chlorides, titanium sulfate and the like; and organic titanium compounds such as titanium oxalate, tetraisopropyl titanate and the like. A preferable water-soluble silicon compound or sol ( a silicon source ) is selected from, for example, inorganic silicon compounds such as colloid type silica, water glass, silicon tetrachloride and the like; and organic silicon compounds such as tetraethyl silicate and the like. A preferable water-soluble zirconium compound or sol ( a zirconium source ) is selected from, for example, inorganic zirconium compounds such as zirconium oxychloride, zirconium nitrate, zirconium sulfate and the like; and organic zirconium compounds such as zirconium oxalate and the like. In a group of these raw materials, although there exist such a member as containing slight amounts of impurities and mingling compounds, the impurities and mingled compounds in a raw material cause no problem as far as they do not affect on physical properties of an obtaining compound. In the group of raw materials, at least one kind of source among the titanium, silicon and zirconium sources is dissolved with an iron source in water and, a precipitate is formed by varying pH with adding a base such as ammonia, urea, sodium hydroxide, potassium hydroxide or the like. The precipitate formed is a coprecipitate containing elements of the components ( i ) and ( ii ) and is usually a hydroxide. This precipitate is dried and calcinated to convert it into an oxide. If necessary, the oxide obtained may be crushed and molded. It is preferred that the calcinating is carried out at a temperature in a range of from 300 to 750°C for a period of from 1 to 10 hours ( more preferably for 2 to 6 hours ) with an air stream. Using the A component ( for example, a TiO 2 - Fe 2 O 3 compound ) prepared by the forementioned process, a completed catalyst is obtained, for example, from the following process. A molding additive is added to a TiO 2 - Fe 2 O 3 compound powder and, an obtained mixture is further mixed with adding a proper amount of water, kneaded, and molded by a molding device to a proper shape such as a pellet, sphere, honeycomb type or the like. A molded product is dried at a temperature in a range of from 50 to 120°C , and calcinated at a temperature in a range of from 300 to 750 °C , preferably at a temperature in a range of from 350 to 700 °C , for a period of from 1 to 10 hours, preferably for a period of from 2 to 6 hours with an air stream, whereby a carrier is obtained. An obtained carrier is soaked in an aqueous solution of a respective metal salt of the catalyst B component to carry the metal salt, then dried and calcinated, whereby a catalyst for treating wastewater of this invention is obtained. Or an aqueous solution of a metal salt of the forementioned B component together with a molding additive may be added to the A component ( for example, a TiO 2 - Fe 2 O 3 compound powder ), and a mixture obtained above may be kneaded, molded, then dried and calcinated. The calcination condition is, for example, similar to a case of calcinating the forementioned moldings. Or again, a metal salt of the B component may be added before or after coprecipitation of the A component. A preferable starting material of the catalyst B component is an oxide, a hydroxide, an inorganic acid salt, an organic acid salt or the like of at least one kind of element selected from a group consisting of cobalt, nickel, cerium, silver, gold, platinum, palladium, rhodium, ruthenium and iridium. For example, it is selected from an ammonium salt, an oxalate, a nitrate, a sulfate, a halogenide or the like of said element. An element of the B component is carried in a condition of a metal, a compound or the like. Concerning the shape of a catalyst of the present invention, although any one of a pellet, sphere, honeycomb, ring type and the like can be used , because blocking in a catalyst layer by a solid, a precipitate or the like may occur in a case of treating wastewater containing a suspension, the honeycomb type is especially preferred. A preferable catalyst used in this invention is such as having a specific composition as mentioned above. A preferable shape of the catalyst is one-body structure such as a pellet, particle and honeycomb type or other several types of structure. A catalyst of the particle type has an average diameter in a range of from 1 to 10 mm, preferably from 2 to 7 mm. If the average diameter is less than 1 mm, pressure loss increases. If it is larger than 10 mm, the geometric surface area is not enough and sufficient treating capability can not be obtained, so that this is unfavorable. Relative surface area by the BET method is in a range of from 5 to 200 m 2 per gram, preferably, 10 to 80 m 2 per gram. If it is less than 5 m 2 per gram, contact efficiency between molecules to be treated and a catalyst lowers and, if it is larger than 200 m 2 per gram, the mechanical strength of a solid catalyst becomes weak, so that this is unfavorable. A catalyst of the pellet type has an average diameter in a range of from 1 to 10 mm, preferably from 3 to 8 mm and a length in a range of from 2 to 15 mm, preferably from 3 to 10 mm. If the average diameter is less than 1 mm or the length is shorter than 2 mm, pressure loss may increase and, if the average diameter is larger than 10 mm or the length is longer than 15 mm, the geometric surface area is not enough, the contact efficiency diminishes, and sufficient treating capability may not be obtained, so that this is unfavorable. It is preferred that relative surface area by the BET method of the pellet type catalyst is in a range similar to that in a case of the particle type. A preferable shape of a honeycomb type catalyst has a penetrating hole-corresponding diameter in a range of from 2 to 20 mm, a cell wall thickness in a range of from 0.1 to 3 mm, and an opening ratio in a range of from 50 to 90 %. A further preferable shape has a penetrating hole-corresponding diameter in a range of from 2.5 to 15 mm, a cell wall thickness in a range of from 0.5 to 3 mm and an opening ratio in a range of from 50 to 90 %. If the penetrating hole-corresponding diameter is less than 2 mm, pressure loss is large and, if it exceeds 20 mm, although the pressure loss becomes small, the contact percentage diminishes and the catalyst activity lowers. In a case where the cell wall thickness is less than 0.1 mm, although there is an advantage that the pressure loss is small and a catalyst can be converted into a light weight one, the mechanical strength of the catalyst may diminish. In a case where the cell wall thickness exceeds 3 mm, the mechanical strength is enough, but the pressure loss may become large. From the same reason to the above-described, a preferable opening ratio is in a range of from 50 to 90 %. To carry out a process for treating wastewater of this invention, for example, there is used a single cylindrical tube reactor for wet oxidation reaction or the like which is commonly used in a hitherto-known process for treating wastewater. A multiple tube reactor for wet oxidation reaction or the like is used depending upon wastewater to be treated. In these reactors, for example, a catalyst for treating wastewater of this invention is arranged in a manner similar to a previous manner, and then wastewater is subjected to a wet oxidation process. Next, one example of treatment condition for wastewater is explained. First, in a case of wastewater including a nitrogen-containing compound, the temperature in the course of wastewater treatment is required to be set at a temperature lower than a critical temperature in order to maintain a liquid phase condition of the wastewater. A temperature lower than the critical one is properly selected, the atmosphere pressure is set at a pressure higher than a pressure under which the wastewater keeps its liquid phase at said temperature. A pressure of this sort is, for example, in a range of from 1 to 200 kgf/cm 2 . According to this invention, the temperature necessary for treating wastewater can be set, for example, in a range of from 100 to 370 °C , but it is possible to set it at a temperature which is about 50 °C lower compared with a case of previous wet oxidation treatment, and in this temperature range, decomposition of an organic compound or the like into carbon dioxide, water or the like as well as decomposition of nitrogen in a nitrogen-containing compound into a nitrogen gas are achieved. Although existence of an oxygen gas is necessary for the reaction of wastewater treatment, air is preferable owing to its cheap cost, except a special case where apparatus-compacting or the like is wanted. A preferable amount of the oxygen gas is from 1 to 1.5 times of the theoretically required oxygen amount. The pH of wastewater necessary for wet oxidation treatment may be set case by case between an acidic region and an alkaline region, and it is, for example, from 1 to 14. Next, in a case of wastewater including a sulfur-containing compound, the wet oxidation process is carried out in the presence of the above-described catalyst at a temperature of 350 °C or lower under a pressure that the wastewater has a liquid phase, preferably, at a temperature lower than 180°C under a pressure less than 10 kg/cm 2 G and also, in the presence of an oxygen gas in an amount of 1 to 5 times of a theoretical oxygen amount which is required for oxidative decomposition of an inorganic compound containing a sulfur atom into an inorganic salt, a carbon dioxide gas, water, a nitrogen gas or the like. Besides, in a case where an organic compound contained in the wastewater is simultaneouly converted into a harmless compound, a theoretical oxygen amount required for oxidative decomposition of the organic compound should be added. It is considered that the sulfur atom constituting an inorganic sulfur compound becomes harmless by being oxidized to a sulfate ion with the wet oxidation. In the present invention, it is preferable to adjust the pH in a range of from a neutral to an alkaline region, after treatment of wastewater including a sulfur-containing compound is finished, by supplying an alkaline component before or during the treatment. This is because the oxidation reaction by a solid catalyst of the sulfur-containing compound is especially accelerated in a range of from a neutral to an alkaline region. Also, that is because, in a wet oxidation process under acidic conditions in which sulfuric acid exists, the material of the wet oxidation reaction tube corrodes very much, so that the apparatus durability is damaged very much. Finally, in a case of wastewater including an organic halogeno compound, the wet oxidation reaction in this invention is carried out in the presence of a specific catalyst, by keeping the wastewater at a temperature in a range of from 100 to 370°C, under a pressure which maintains the wastewater in a liquid phase, and in the presence of an oxygen gas in an amount equal to or more than the theoretically required amount to oxidize the organic halogeno compounds being contained in wastewater into carbon dioxide, water, water-soluble salts, ashes and others. In a case where oxygen-consuming substances ( hereinafter, referred to as " TOD components " ) such as other organic compounds etc. exist, that is a pollution factor of the wastewater, a theoretical amount of oxygen required for oxidative degradation of the TOD component should be added. In a case where the organic halogeno compounds are treated by the present invention, the halogen atom in the wastewater becomes harmless by being converted into a halide ion. That is, the chlorine atom in an organic chloro compound, the fluorine atom in an organic fluoro compound, and the bromine atom in an organic bromo compound are converted into the Cl - ion, F - ion , and Br - ion, respectively, so that said halogen atoms become harmless. In this invention, it is preferred to make salts by adding beforehand into wastewater an equivalent amount or more of cations which make pairs with halide ions from the wet oxidation. In adding cations, it is further preferred that alkali metal ions such as sodium, potassium or other ions are added. By adding the alkali metal ions into wastewater, durability decrease of a reaction tube caused by wastewater becoming acidic in the course of treatment is prevented, and in addition, the reaction rate is accelerated, so that faster treatment becomes possible. As far as the alkali metal ions show an alkaline character by dissolving them into wastewater, any kind of the ions can be used and, for example, there are listed for use sodium hydroxide, potassium hydroxide, sodium carbonate, sodium acetate and the like. In a case where a salt containing an organic acid moiety such as sodium acetate or the like is added into wastewater, the acetate ion is decomposed up to carbon dioxide and water, similarly to the case of organic halogeno compounds. Concerning the oxygen-containing gas in this invention, a gas having any oxygen concentration may be used. As the oxygen concentration in an oxygen-containing gas becomes higher, the reaction rate is more accelerated and faster treatment becomes possible. However, since sufficient efficiency on treatment is obtainable even by the air, the oxygen concentration of an oxygen-containing gas may be properly determined depending upon factors such as cost and the like. In the catalyst for treating wastewater relating to this invention, the B component is at least one kind of element selected from a group consisting of cobalt, nickel, cerium, silver, gold, platinum, palladium, rhodium, ruthenium and iridium. The A component is an oxide containing iron and at least one kind of element selected from a group consisting of titanium, silicon and zirconium. This catalyst maintains its catalytic activity for a long period of time even if wastewater includes a nitrogen-containing compound, a sulfur-containing compound or an organic halogeno compound when the wastewater being treated with wet oxidation. Wastewater can be treated with excellent efficiency for a long period of time, even if the wastewater includes a nitrogen-containing compound, a sulfur-containing compound or an organic halogeno compound, by subjecting the wastewater to wet oxidation treatment using such a catalyst as stated above, similar to a case where the wastewater does not include said compounds. In addition, since nitrogen in the nitrogen-containing compound is decomposed up to a nitrogen gas, post-treatment as carried out in previously-known conventional methods becomes unnecessary. A catalyst for treating wastewater of this invention not only decomposes a nitrogen-free organic compound, but also decomposes nitrogen in a nitrogen-containing compound up to a nitrogen gas. By using this catalyst, whether wastewater includes a nitrogen-containing compound or not, the wastewater treatment can be carried out for a long period of time with excellent efficiency. According to a catalyst for treating wastewater of this invention, a compound containing sulfur and other pollution substances in wastewater can be decomposed by oxidation with excellent efficiency and, it is possible to convert them into inorganic salts, carbon dioxide, water, ash or the like. Then, biological treatment is not required as a post-treatment at all and treated wastewater may be directly discharged, or even if the biological treatment is required as a post-treatment, a substance which may affect badly on an organism has already been decomposed, and it is unnecessary to regulate wastewater on which the wet oxidation process has been carried out, except for a pH adjustment. Therefore, an amount of the treated wastewater becomes small and biological treatment facilities are not necessary at all or they can be very small compared with previous facilities, and treatment process is simplified. Consequently, an advantage comes on the investment and running cost of facilities. According to this invention, it is possible to convert an organic halogeno compound, which is included in wastewater, into carbon dioxide, water, soluble salts, ash or the like with excellent efficiency and whereby to make the compound harmless without secondary forming of harmful substances. According to a process for producing a catalyst for treating wastewater of this invention, a superior catalyst for treating wastewater as described above can be produced with excellent efficiency. According to a process for treating wastewater of this invention, whether or not the wastewater includes a nitrogen-containing compound, a sulfur-containing compound or an organic halogeno compound, it is possible to treat wastewater for a long period of time with excellent efficiency. DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, catalyst preparation examples and wastewater treatment examples relating to practical examples of the present invention and comparative catalyst preparation examples and comparative wastewater treatment examples are shown. Preparation example 1 A compound consisting of titanium and iron was prepared by the undermentioned process and, as a titanium source, an aqueous sulfuric acid having the following composition was used. TiOSO 4 ......... 250 g/l ( as TiO 2 ) total H 2 SO 4 ......... 1,100 g/l Into 100 liter of water were dissolved 5.41 kg of ferric nitrate [ Fe( NO 3 ) 3 · 9H 2 O ] and an obtained solution was well mixed with adding 5 liter of an aqueous sulfuric acid solution of titanyl sulfate ( titanium oxysulfate ) which has the above composition. To this mixture maintained at about 30 °C with well stirring, an aqueous ammonia was gradually added dropwise until pH 8 being indicated, and an obtained mixture was still stood for 15 hours to make a precipitate ( gel ). This gel was taken by filtration, washed with water, and dried at 120°C for 10 hours. Then, it was calculated at 700°C for 5 hours under an air atmosphere. According to a X-ray diffraction analysis, the obtained powder consisted of TiO 2 and Fe 2 O 3 , in which the weight ratio between TiO 2 and Fe 2 O 3 was 53.9 versus 46.1 according to a fluorescence X-ray analysis. Using this obtained powder, a catalyst was prepared by the undermentioned process. Water, the obtained powder and starch were mixed and well kneaded by a kneader. This kneaded product was molded by a molding device to pellets of paticle diameter 5 mm ⊘ and length 6 mm and calcinated at 500°C for 3 hours under an air atmosphere. The pellets thus-obtained were soaked in an aqueous palladium nitrate solution, dried at 120 °C for 6 hours, and calcinated at 400 °C for 3 hours. An obtained, completed catalyst showed composition having a 98 versus 2 ratio by weight between a TiO 2 - Fe 2 O 3 compound and palladium, according to a fluorescence X-ray analysis. Preparation example 2 Into 80 liter of water were dissolved 6.57 kg of ferric nitrate [ Fe( NO 3 ) 3 · 9H 2 O ] and 2.17 kg of zirconium oxynitrate ( zirconium nitrate ) [ ZrO ( NO 3 ) 2 · 2H 2 O ] with well mixing. To this mixture maintained at about 30 °C with well stirring, an aqueous ammonia was gradually added dropwise until pH 8 being indicated, and an obtained mixture was still stood for 15 hours to make a precipitate ( gel ). This gel was taken by filtration, washed with water, and dried at 120°C for 10 hours. Then, it was calcinated at 700°C for 5 hours under an air atmosphere. According to a X-ray diffraction analysis, an obtained powder consisted of ZrO 2 and Fe 2 O 3 , in which the weight ratio between ZrO 2 and Fe 2 O 3 was 43.5 versus 56.5 according to a fluorescence X-ray analysis. Using this obtained powder, a catalyst was prepared by the undermentioned process. Water, the obtained powder and starch were mixed and well kneaded by a kneader. This kneaded product was molded by a molding device to pellets having a particle diameter 5 mm ⊘ and length 6 mm, and calcinated at 500 °C for 3 hours under an air atmosphere. The pellets thus-obtained were soaked in an aqueous ruthenium nitrate solution, dried at 120 °C for 6 hours, and calcinated at 400 °C for 3 hours. An obtained, completed catalyst showed composition having a 95 versus 5 ratio by weight between a ZrO 2 - Fe 2 O 3 compound and ruthenium, according to a fluorescence X-ray analysis. Preparation example 3 Into 100 liter of water were dissolved 6.07 kg of ferric nitrate [ Fe( NO 3 ) 3 · 9H 2 O ] and an obtained solution was well mixed with dissolving 4 liter of an aqueous sulfuric acid solution of titanyl sulfate ( titanium oxysulfate ) having the composition used in the preparation example 1 and 1.34 kg of zirconium oxynitrate ( zirconium nitrate ) [ ZrO ( NO 3 ) 2 · 2H 2 O ] . To this mixture maintained at about 30 °C with well stirring, an aqueous ammonia was gradually added dropwise until pH 8 being indicated, and an obtained mixture was still stood for 15 hours to make a precipitate ( gel ). This gel was taken by filtration, washed with water, and dried at 120°C for 10 hours. Then, it was calcinated at 700°C for 5 hours under an air atmosphere. According to a X-ray diffraction analysis, the obtained powder consisted of TiO 2 , ZrO 2 and Fe 2 O 3 , in which the weight ratios among TiO 2 , ZrO 2 and Fe 2 O 3 were 35.5, 21.9 and 42.6, respectively, according to a fluorescence X-ray analysis. Using this obtained powder, a catalyst was prepared by the undermentioned process. Water, the obtained powder and starch were mixed and well kneaded by a kneader. This kneaded product was molded by a molding device to pellets having a particle diameter 5 mm  and length 6 mm and calcinated at 500°C for 3 hours under an air atmosphere. The pellets thus-obtained were soaked in an aqueous platinum nitrate solution, dried at 120°C for 6 hours, and calcinated at 400 °C for 3 hours. An obtained, completed catalyst showed composition having a 99 versus 1 ratio by weight between a TiO 2 - ZrO 2 - Fe 2 O 3 compound and platinum, according to a fluorescence X-ray analysis. Preparation examples 4 and 5 The procedure of preparation example 1 was repeated except that the ratio between TiO 2 and Fe 2 O 3 was varied as follows. TiO 2 versus Fe 2 O 3 ( weight ratio ) Preparation example 23 ......... 80 versus 20 Preparation example 24 ......... 15 versus 85 Preparation examples 6 to 8 Pellets of the TiO 2 - ZrO 2 - Fe 2 O 3 compound obtained from the preparation example 3 were soaked in each of an aqueous chloroauric acid solution, aqueous rhodium nitrate solution and aqueous iridium nitrate solution, dried at 120 °C for 6 hours, and calcinated at 400 °C for 3 hours. Obtained, completed catalysts had the below-described composition by weight ratios, according to a fluorescence X-ray analysis. Preparation example 6 .... ( TiO 2 -ZrO 2 -Fe 2 O 3 compound ) versus Au = 90 versus 10 Preparation example 7 .... ( TiO 2 -ZrO 2 -Fe 2 O 3 compound ) versus Rh = 99 versus 1 Preparation example 8 .... ( TiO 2 -ZrO 2 -Fe 2 O 3 compound ) versus Ir = 95 versus 5 Treatment examples 1 to 8 Using each of the catalysts obtained from the preparation examples 1 to 8, wastewater treatment was carried out by wet oxidation according to the following procedure. Each of the catalysts ( 1000 cc ) was filled in a reaction tube made of a stainless steel and, from a down part of the reaction tube, preheated wastewater blended with air containing oxygen in a concentration of about 21 % was continuously introduced for 5,000 hours, the COD ( Cr ) concentration and total nitrogen amount were measured at an entrance and exit of the reaction tube to calculate their elimination percentages. Meanwhile, before treatment, wastewater contained 15,000 mg/l of dimethylformamide and showed 20,000 mg/l in the COD ( Cr ) concentration. The reaction conditions were 200°C as a reaction temperature, 40 kg/cm 2 G as a reaction pressure, 2 liter per hour as the rate of supplying wastewater, and 230 N liter per hour as the rate of supplying air. The obtained results are shown in Table 1. kind of catalyst elimination percentage of COD (Cr) (%) elimination percentage of total nitrogen amount (%) treatment example 1 preparation example 1 99.9 99.5 treatment example 2 preparation example 2 99.9 99.1 treatment example 3 preparation example 3 99.9 99.0 treatment example 4 preparation example 4 99.9 99.4 treatment example 5 preparation example 5 99.9 99.6 treatment example 6 preparation example 6 99.6 99.0 treatment example 7 preparation example 7 99.7 98.5 treatment example 8 preparation example 8 99.5 98.3 As seen in Table 1, in a continuous operation for 5,000 hours under the forementioned conditions, decrease in the elimination percentages of the COD ( Cr ) and total nitrogen amount was not recognized. Treatment examples 9 to 13 According to the treatment example 1, wastewater treatment was carried out by wet oxidation using each of the catalysts obtained from the preparation examples 1 to 5. Wastewater to be treated contained 20,000 mg/l of glycine and showed 19,000 mg/l in the COD ( Cr ) concentration. The reaction conditions were 200°C as a reaction temperature, 40 kg/cm 2 G as a reaction pressure, 2 liter per hour as the rate of supplying wastewater, and 160 N liter per hour as the rate of supplying air. The obtained results are shown in Table 2. kind of catalyst elimination percentage of COD (Cr) (%) elimination percentage of total nitrogen amount (%) treatment example 9 preparation example 1 99.8 99.5 treatment example 10 preparation example 2 99.9 99.1 treatment example 11 preparation example 3 99.9 99.0 treatment example 12 preparation example 4 99.9 99.3 treatment example 13 preparation example 5 99.9 99.4 As seen in Table 2, in a continuous operation for 3,000 hours under the forementioned conditions, decrease in the elimination percentages of the COD ( Cr ) and total nitrogen amount was not recognized. Treatment examples 14 to 18 According to the treatment example 1; wastewater treatment was carried out by wet oxidation using each of the catalysts obtained from the preparation examples 1 to 5. Wastewater to be treated contained 10,000 mg/l of ethanolamine and showed 12,000 mg/l in the COD ( Cr ) concentration. The reaction conditions were 200°C as a reaction temperature, 40 kg/cm 2 G as a reaction pressure, 2 liter per hour as the rate of supplying wastewater, and 140 N liter per hour as the rate of supplying air. Obtained results are shown in Table 3. kind of catalyst elimination percentage of COD (Cr) (%) elimination percentage of total nitrogen amount (%) treatment example 14 preparation example 1 99.0 99.0 treatment example 15 preparation example 2 98.8 98.8 treatment example 16 preparation example 3 98.8 98.9 treatment example 17 preparation example 4 99.0 98.6 treatment example 18 preparation example 5 99.0 98.8 As seen in Table 3, in a continuous operation for 3,000 hours under the forementioned conditions, decrease in the elimination percentages of the COD ( Cr ) and total nitrogen amount was not recognized. Comparative preparation example 1 The procedure of preparation example 1 was repeated to obtain a catalyst except that an aqueous solution of ferric nitrate was not used. Composition of an obtained, completed catalyst showed a weight ratio of 98 versus 2 between TiO 2 and palladium. Comparative preparation example 2 Into 4 liter of an aqueous sulfuric acid solution of titanyl sulfate ( titanium oxysulfate ) having the composition used in the preparation example 1 was added with mixing 1.44 kg of zirconium oxynitrate [ ZrO( NO 3 ) 2 · 2H 2 O] . To this mixture maintained at about 30 °C with well stirring, an aqueous ammonia was gradually added dropwise until pH 8 being indicated, and an obtained mixture was still stood for 15 hours to make a precipitate ( gel ). This gel was taken by filtration, washed with water, and dried at 120°C for 10 hours. Then, it was calcinated at 700°C for 5 hours under an air atmosphere. Composition of an obtained powder showed a weight ratio of 60.2 versus 39.8 between TiO 2 and ZrO 2 . Using this obtained powder, a catalyst was prepared by the undermentioned process. Water, the obtained powder and starch were mixed and well kneaded by a kneader. This kneaded product was molded by a molding device to pellets having a particle diameter 5 mm ⊘ and length 6 mm and calcinated at 500°C for 3 hours under an air atmosphere. The pellets thus-obtained were soaked in an aqueous iron nitrate solution, dried at 120°C for 6 hours, and calcinated at 400 °C for 3 hours. An obtained, completed catalyst showed composition having a 85 versus 15 ratio by weight between a TiO 2 - ZrO 2 compound and Fe 2 O 3 . Comparative treatment examples 1 and 2 Wastewater treatment by wet oxidation was carried out by the procedure of treatment example 1 except that each of the catalysts obtained from the comparative preparation examples 1 and 2 was used. Results obtained are shown in Table 4. kind of catalyst initial after 500 hours elimination percentage of COD (Cr) (%) elimination percentage of total nitrogen amount (%) elimination percentage of COD (Cr) (%) elimination percentage of total nitrogen amount (%) comparative treatment example 1 comparative preparation example 1 72.0 75.0 42.0 36.0 comparative treatment example 2 comparative preparation example 2 50.5 47.5 37.0 25.5 As seen in Table 4, in the comparative treatment example 1 where a catalyst not containing the component ( i ) was used as well as in the comparative treatment example 2 where a catalyst containing iron as a B component, the COD ( Cr )-elimination and total nitrogen-elimination percentages are both lower than the cases where the catalysts of this invention were used, and furthermore, a large decrease in the COD ( Cr )-elimination and total nitrogen-elimination percentages was observed in a continuous operation of 500 hours. Preparation example 9 Into 100 liter of water were added 9 liter of an aqueous titanyl sulfate solution (which has the same composition as the solution used in preparation example 1) and 4 liter of an aqueous ferrous sulfate [ FeSO 4 ; 500 g/l ] solution, and these solutions were well mixed each other. To this mixture maintained at about 30 °C with well stirring, an aqueous ammonia was gradually added dropwise until pH 7 being indicated, and an obtained mixture was still stood for 20 hours to make a precipitate ( gel ). This gel was taken by filtration, washed with water, and dried at 120°C for 12 hours. Then, it was calcinated at 700°C for 6 hours under an air atmosphere. According to a X-ray diffraction analysis, the obtained powder consisted of TiO 2 and Fe 2 O 3 , in which the weight ratio between TiO 2 and Fe 2 O 3 was 75.0 versus 25.0 according to a fluorescence X-ray analysis. Using this obtained powder, a catalyst was prepared by the undermentioned process. Water, the obtained powder and starch were mixed and well kneaded by a kneader. This kneaded product was molded by a molding device to a spherical shape of average paticle diameter 5 mm and calcinated at 500°C for 3 hours under an air atmosphere. The thus-obtained, spherical molded product was soaked in an aqueous ruthenium nitrate solution, dried at 120°C for 6 hours, and calcinated at 400°C for 4 hours. An obtained, completed catalyst showed composition having a 99.7 versus 0.3 ratio by weight between a TiO 2 - Fe 2 O 3 compound and Ru, according to a fluorescence X-ray analysis. Treatment example 19 Using the catalyst obtained from preparation example 9, wastewater having the below-mentioned composition was treated. pH 13 Na 2 S 8 % NaSH 3 % NaCO 3 3 % TOD 100,000 mg/l The catalyst ( 500 cc ) was filled in a reaction tube made of a stainless steel of a wet oxidation column and, from a down part of the reaction tube, preheated wastewater blended with air was continuously introduced for 1,000 hours, the concentrations of sulfide ion (S 2- ), thiosulfate ion and COD ( Cr ) were measured at an entrance and exit of the reaction tube. The reaction conditions were 150 °C as a reaction temperature, 9 kg/cm 2 G as a reaction pressure, 0.5 liter per hour as the rate of supplying wastewater, and 200 N liter per hour as the rate of supplying air [ ratio of O 2 /TOD ( amount of oxygen in air / total amount of consumed oxygen ) is 1.2 ]. As a result, treated water was stably obtained, which contained COD (Cr), sulfide ion and thiosulfate ion in concentrations of 3000 mg/l or less, 0.1 mg/l or less and 4500 mg/l or less, respectively. Comparative treatment example 3 The procedure of treatment example 19 was repeated except that any catalyst was not filled in a wet oxidation column and the column was empty. As a result, treated water contained COD (Cr), sulfide ion and thiosulfate ion in concentrations of 23,000 mg/l, 20 mg/l and 30,000 mg/l, respectively. Treatment example 20 Wastewater having the below-mentioned composition was treated by the procedure similar to treatment example 19, except that the catalyst in a wet oxidation column was changed. pH 13 Na 2 S 2 O 3 1.7 % NaOH 1.0 % TOD 8,600 mg/l A catalyst used in the present treatment example was the catalyst obtained from preparation example 9. This catalyst ( 500 cc ) was filled in a wet oxidation column. The above-mentioned treatment resulted in that treated water containing 70 mg/l or less of COD (Cr), 100 mg/l or less of thiosulfate ion was stably obtained. Comparative treatment example 4 The procedure of treatment example 20 was repeated except that any catalyst was not filled in a wet oxidation column and the column was empty. As a result, 4300 mg/l of COD (Cr) and 6,000 mg/l of thiosulfate ion remained in treated water. Treatment example 21 Wastewater having the below-mentioned composition was treated by the procedure similar to treatment example 19, except that the catalyst in a wet oxidation column was changed. pH 13 Na 2 S 2.4 % Na 2 S 2 O 3 0.9 % Na 2 SO 3 0.2 % NaOH 0.5 % TOD 25,000 mg/l A catalyst used in the present treatment example was the catalyst obtained from preparation example 9. This catalyst ( 500 cc ) was filled in a wet oxidation column. The above-mentioned treatment resulted in that treated water containing 230 mg/l or less of COD (Cr), 350 mg/l or less of thiosulfate ion was stably obtained. In addition, both sulfide ion and sulfite ion were 0.01 mg/l or less. Comparative treatment example 5 The procedure of treatment example was repeated except that any catalyst was not filled in a wet oxidation column and the column was empty. As a result, 7,200 mg/l of COD (Cr), 5 mg/l of sulfide ion and 10,000 mg/l of thiosulfate ion remained in treated water. In addition, sulfite ion was 0.01 mg/l or less. Preparation example 10 Into 100 liter of water were added 7 liter of an aqueous titanyl sulfate solution (which has the same composition as the solution used in preparation example 1) and 3.80 kg of ferric nitrate [ Fe(NO 3 ) 3 · 9H 2 O ], and these were well mixed. To this mixture maintained at about 30°C with well stirring, an aqueous ammonia was gradually added dropwise until pH 7 being indicated, and an obtained mixture was still stood for 16 hours to make a precipitate ( gel ). This gel was taken by filtration, washed with water, and dried at 120°C for 20 hours. Then, it was calcinated at 700°C for 6 hours under an air atmosphere. According to a X-ray diffraction analysis, the obtained powder consisted of TiO 2 and Fe 2 O 3 , in which the weight ratio between TiO 2 and Fe 2 O 3 was 70.0 versus 30.0 according to a fluorescence X-ray analysis. Using this obtained powder, a catalyst was prepared by the undermentioned process. Water, the obtained powder and starch were mixed and well kneaded by a kneader. This kneaded product was molded by a molding device to a spherical shape of average paticle diameter 6 mm and calcinated at 500°C for 4 hours under an air atmosphere. The thus-obtained, spherical molded product was soaked in an aqueous chloroplatinic acid solution, dried at 120°C for 6 hours, and calcinated at 400°C for 6 hours. An obtained, completed catalyst showed composition having a 99.6 versus 0.4 ratio by weight between a TiO 2 - Fe 2 O 3 compound and Pt, according to a fluorescence X-ray analysis. Treatment example 22 Using the catalyst obtained from preparation example 10 and according to the below-mentioned procedure, wastewater was treated by a wet oxidation. The catalyst ( 3,000 cc ) was filled in a reaction tube made of a stainless steel and, from a down part of the reaction tube, preheated wastewater blended with air was continuously introduced for 500 hours, a COD ( Cr ) concentration, an amount of thiophene and an amount of sodium dodecyl sulfate were measured at an entrance and exit of the reaction tube to calculate treatment efficiency. Here, conditions of wastewater provided for treatment were 3.5 g/l in an amount of thiophene, 20 g/l in an amount of sodium dodecyl sulfate, 16.2 g/l in other oil content, 21.7 g/l in TOC, and before treatment, caustic soda had been added to the wastewater until pH 13 being indicated. The reaction conditions were 240°C as a reaction temperature, 70 kg/cm 2 G as a reaction pressure, 0.9 per hour as space velocity of wastewater (empty column standard), 6 m per hour as linear velocity of wastewater. Air was introduced to the reaction tube in such an amount that the ratio of O 2 /TOD ( amount of oxygen in air / total amount of consumed oxygen ) is 1.0. As a result, elimination percentages of thiophene, sodium dodecyl sulfate, and TOC were 97.0 %, 89.5 %, and 82.0 %, respectively. In addition, pH of treated water was 8. Comparative treatment example 6 The procedure of treatment example 22 was repeated except that any catalyst was not filled in a wet oxidation column and the column was empty. As a result, elimination percentages of thiophene, sodium dodecyl sulfate, and TOC were 42.0 %, 37.0 %, and 34.5 %, respectively. In addition, pH of treated water was 11. Preparation example 11 Into 100 liter of water were added 5 liter of an aqueous titanyl sulfate solution (which has the same composition as the solution used in preparation example 1), 10.66 kg of ferric nitrate [ Fe(NO 3 ) 3 · 9H 2 O ] and 1.32 kg of cerous nitrate [ Ce(NO 3 ) 3 · 6H 2 O ], and these were well mixed. To this mixture maintained at about 30°C with well stirring, an aqueous ammonia was gradually added dropwise until pH 8 being indicated, and an obtained mixture was still stood for 24 hours to make a precipitate ( gel ). This gel was taken by filtration, washed with water, and dried at 120°C for 16 hours. Then, it was calcinated at 700°C for 6 hours under an air atmosphere. According to a X-ray diffraction analysis, the obtained powder consisted of TiO 2 , Fe 2 O 3 and CeO 2 , in which the weight ratio among TiO 2 , Fe 2 O 3 and CeO 2 was 31.2 : 52.6 : 16.2 according to a fluorescence X-ray analysis. Using this obtained powder, a catalyst was prepared by the undermentioned process. Water, the obtained powder and starch were mixed and well kneaded by a kneader. This kneaded product was molded by a molding device to a spherical shape of average paticle diameter 5 mm and calcinated at 500°C for 4 hours under an air atmosphere. The thus-obtained, spherical molded product was soaked in an aqueous ruthenium nitrate solution, dried at 120°C for 6 hours, and calcinated at 450°C for 4 hours. An obtained, completed catalyst showed composition having a 99.4 versus 0.6 ratio by weight between a TiO 2 -Fe 2 O 3 -CeO 2 compound and Ru, according to a fluorescence X-ray analysis. Treatment example 23 Using the catalyst obtained from preparation example 11, wastewater containing 100 mg/l of ethyl bromide was treated by the below-mentioned process. The catalyst ( 500 cc ) was filled in a reaction tube made of titanium of a wet oxidation column and, from a down part of the reaction tube, preheated wastewater blended with air was continuously introduced for 1,000 hours, the concentrations of ethyl bromide and bromide ion were measured at an entrance and exit of the reaction tube. The reaction conditions were 270 °C as a reaction temperature, 80 kg/cm 2 G as a reaction pressure, 0.5 liter per hour as the rate of supplying wastewater, and 10 N liter per hour as the rate of supplying air. As a result, the elimination percentage of ethyl bromide was 99 %, and any organic bromine compound except ethyl bromide was not detected in treated water by GC-ECD method. In addition, the bromide ion concentration in the treated water was 73 mg/l and ethyl bromide was not detected at all in waste gas. Preparation example 12 Into 100 liter of water were added 5 liter of an aqueous titanyl sulfate solution (which has the same composition as the solution used in preparation example 1). and 7.56 kg of ferric nitrate [ Fe(NO 3 ) 3 · 9H 2 O ], and these were well mixed. To this mixture maintained at about 30°C with well stirring, an aqueous ammonia was gradually added dropwise until pH 7 being indicated, and an obtained mixture was still stood for 16 hours to make a precipitate ( gel ). This gel was taken by filtration, washed with water, and dried at 120°C for 20 hours. Then, it was calcinated at 700°C for 6 hours under an air atmosphere. According to a X-ray diffraction analysis, the obtained powder consisted of TiO 2 and Fe 2 O 3 , in which the weight ratio between TiO 2 and Fe 2 O 3 was 45.5 versus 54.5 according to a fluorescence X-ray analysis. Using this obtained powder, a catalyst was prepared by the undermentioned process. Water, the obtained powder and starch were mixed and well kneaded by a kneader. This kneaded product was molded by a molding device to honeycomb structure having a penetrating hole-corresponding diameter of 10 mm, a cell wall thickness of 1 mm and an opening ratio of 83 %, and then calcinated at 500°C for 4 hours under an air atmosphere. The thus-obtained, honeycomb type molded product was soaked in an aqueous palladium nitrate solution, dried at 120 °C for 6 hours, and calcinated at 400 °C for 4 hours. An obtained, completed catalyst showed composition having a 99.3 versus 0.7 ratio by weight between a TiO 2 -Fe 2 O 3 compound and Pd, according to a fluorescence X-ray analysis. Treatment example 24 According to treatment example 23, the catalyst obtained from preparation example 12 was filled in a wet oxidation column, and wastewater containing 50 mg/l of dichlorobenzene was treated. However, in the present treatment example, a temperature at an entrance of a reaction vessel was 230 °C, reaction pressure was 60 kg/cm 2 , and the air amount was 5 liter per hour. Other conditions were similar to treatment example 23. As a result, the elimination percentage of dichlorobenzene was 89 %, and any organic chlorine compound except dichlorobenzene was not detected in treated water. In addition, the chloride ion concentration in the treated water was 21 mg/l and dichlorobenzene was not detected at all in waste gas. Treatment example 25 The procedure of treatment example 24 was repeated except that a gas containing oxygen in concentration of 70 % was used. As a result, the elimination percentage of dichlorobenzene was 94 %, and any organic chlorine compound except dichlorobenzene was not detected in treated water. In addition, the chloride ion concentration in the treated water was 54 mg/l and dichlorobenzene was not detected at all in waste gas. Preparation example 13 The honeycomb type molded product of a titanium-iron oxide obtained from preparation example 12 was soaked in an aqueous rhodium nitrate solution, dried at 120 °C for 6 hours, and calcinated at at 400°C for 3 hours to obtain a catalyst. Treatment example 26 The catalyst obtained from preparation example 13 was filled in a wet oxidation column, and wastewater treatment was carried out. In addition, wastewater containing 500 mg/l of trichloroethylene was used as model wastewater. The model wastewater did not contain chloride ion. The reaction was carried out under the conditions of 250°C and 70 kg/cm 2 G. Other conditions and flow were similar to treatment example 23. As a result, the elimination percentage of trichloroethylene was 95 %. Comparative treatment example 7 According to treatment example 26, wastewater similar to the wastewater used in treatment example 26 was treated under the conditions similar to treatment example 26. However, any catalyst was not filled in a wet oxidation column and the column was empty. As a result, the elimination percentage of trichloroethylene was 32 %. Preparation example 14 Into 100 liter of water, were added 4 liter of an aqueous titanyl sulfate solution (which has the same composition an the solution used in preparation example 1), and these were well mixed each other. To this mixture maintained at about 30°C with well stirring, an aqueous ammonia was gradually added dropwise until pH 8 being Indicated, and an obtained mixture was still stood for 15 hours to make a precipitate ( gel ). This gel was taken by filtration and washed with water. To the gel, 1.67 kg of a hydroxide of iron (FeOOH) were added and these were mixed and well kneaded by a kneader and dried at 120 °C for 10 hours. Then, the resulting kneaded mixture was calcinated at 700 °C for 5 hours under an air atmosphere to obtain a powder. According to a X-ray diffraction analysis, the obtained powder consisted of TiO 2 and Fe 2 O 3 , in which the weight ratio between TiO 2 and Fe 2 O 3 was 40 versus 60 according to a fluorescence X-ray analysis. Using this obtained powder, a catalyst was prepared by the undermentioned process. Water, the obtained powder and starch were mixed and well kneaded by a kneader. This kneaded product was molded by a molding device to pellets of paticle diameter 5 mm ⊘ and length 6 mm and calcinated at 500°C for 3 hours under an air atmosphere. The pellets thus-obtained were soaked in an aqueous ruthenium nitrate solution, dried at 120 °C for 6 hours, and calcinated at 400 °C for 3 hours. An obtained, completed catalyst showed composition having a 98 versus 2 ratio by weight between a TiO 2 - Fe 2 O 3 compound and ruthenium, according to a fluorescence X-ray analysis. Treatment example 27 Using the catalyst obtained from the preparation example 14, wastewater treatment was carried out by wet oxidation according to the following procedure. The catalyst ( 1000 cc ) was filled in a reaction tube made of a stainless steel and, from a down part of the reaction tube, preheated wastewater blended with air containing oxygen in a concentration of about 21 % was continuously introduced for 5,000 hours, the COD ( Cr ) concentration and total nitrogen amount were measured at an entrance and exit of the reaction tube to calculate their elimination percentages. Meanwhile, before treatment, wastewater contained 15,000 mg/l of dimethylformamide and showed 20,000 mg/l in the COD ( Cr ) concentration. The reaction conditions were 200°C as a reaction temperature, 40 kg/cm 2 G as a reaction pressure, 2 liter per hour at the rate of supplying wastewater, and 230 N liter per hour as the rate of supplying air. The obtained results are shown in Table 5. Treatment example 28 According to the treatment example 1; wastewater treatment was carried out by wet oxidation using the catalyst obtained from the preparation example 14, Wastewater to be treated contained 20,000 mg/l of glycine and showed 19,000 mg/l in the COD ( Cr ) concentration. The reaction conditions were 200°C as a reaction temperature, 40 kg/cm 2 G as a reaction pressure, 2 liter per hour as the rate of supplying wastewater, and 160 N liter per hour as the rate of supplying air. The obtained results are shown in Table 5. Treatment example 29 According to the treatment example 1, wastewater treatment was carried out by wet oxidation using the catalyst obtained from the preparation example 14, Wastewater to be treated contained 10,000 mg/l of ethanolamine and showed 12,000 mg/l in the COD ( Cr ) concentration. The reaction conditions were 200°C as a reaction temperature, 40 kg/cm 2 G as a reaction pressure, 2 liter per hour as the rate of supplying wastewater, and 140 N liter per hour as the rate of supplying air. Obtained results are shown in Table 5. kind of catalyst elimination percentage of COD (Cr) (%) elimination percentage of total nitrogen amount (%) treatment example 27 preparation example 14 99.0 98.7 treatment example 28 preparation example 14 98.5 98.5 treatment example 29 preparation example 14 98.0 98.5

Claims: A catalyst for treating wastewater, comprising: component [A] comprising an oxide component which contains iron and at least one element selected from titanium, silicon and zirconium; and component [B] comprising at least one element selected from cobalt, nickel, cerium, silver, gold, platinum, palladium, rhodium, ruthenium and iridium; wherein component [A] is contained in a range of from 90 to 99.95% by weight and component [B] in a range of from 0.05 to 10% by weight with the total of components [A] and [B] being 100% by weight, and wherein component [A] contains iron in a range of from 4.95% to 95% by weight as oxide, at least one element selected from titanium, silicon and zirconium in a total range of from 4.95% to 95% by weight as oxide, and iron and at least one element selected from titanium, silicon and zirconium in a total range of from 90 to 99.95% by weight as oxide. A process for treating wastewater, comprising wet oxidation of the wastewater using a solid catalyst according to claim 1 with an oxygen-containing gas supplied at a pressure maintaining the wastewater in the liquid phase. A process according to claim 2 wherein the wastewater includes at least one compound selected from nitrogen-containing compounds, sulfur-containing compounds and organic halogen compounds. A process for producing a catalyst for treating wastewater, comprising obtaining a coprecipitate containing iron and at least one element selected from titanium, silicon and zirconium; calcining the coprecipitate to oxide containing iron and at least one element selected from titanium, silicon and zirconium; and making this oxide contain at least one element selected from cobalt, nickel, cerium, silver, gold, platinum, palladium, rhodium, ruthenium and iridium. A process of producing a catalyst according to claim 1 comprising providing an oxide component containing iron and at least one element selected from titanium, silicon and zirconium, adding a salt of at least one element selected from cobalt, nickel, cerium, silver, gold, platinum, palladium, rhodium, ruthenium and iridium to said oxide; and calcining the resulting mixture. A process according to claim 5 wherein the oxide component is obtained by calcining an iron-containing compound and a compound of at least one element selected from titanium, silicon and zirconium. A process for producing a catalyst according to claim 1 comprising obtaining a coprecipitate containing iron, at least one element selected from titanium, silicon and zirconium, and at least one element selected from cobalt, nickel, cerium, silver, gold, platinum, palladium, rhodium, ruthenium and iridium, and calcining the coprecipitate.

Inventors: ISHII TOHRU, MITSUI KIICHIRO, SANO KUNIO, SHIOTA YUSUKE, SHISHIDA KENITI, ISHII, TOHRU, MITSUI, KIICHIRO, SANO, KUNIO, SHIOTA, YUSUKE, SHISHIDA, KENITI
Applicants: NIPPON CATALYTIC CHEM IND, NIPPON SHOKUBAI CO., LTD.
Application year: 1992
Main classification: C02F1
IPC codes: B01J23, C02F1, B01J37