FIBRES OR FILAMENTS

Abstract: Fibres and filaments of water-absorbent water-insoluble fibrous material have a matrix of a crosslinked copolymer formed from 50 to 95 % by weight of ethylenically unsaturated carboxylic monomer and 5 to 50 % by weight of copolymerisable ethylenically unsaturated monomer. The matrix contains dispersed solid water-insoluble particles of a material which is chemically substantially non-reactive with the matrix copolymer.

Description: FIBRES OR FILAMENTS Technical field This invention relates to fibres or filaments, and it has particular reference to fibres or filaments of water- absorbent water-insoluble material. Water-absorbent water-insoluble materials are of use in many absorbent products, particularly in products for absorbing aqueous body fluids, such as baby diapers, incontinence pads, sanitary napkins and tampons, and in wiping materials for mopp_^g up spills of aqueous fluids. Most water-absorbent water-insoluble materials are only available in powder form. There are problems in retaining an absorbent powder in the desired position in the absorbent product, for example in diapers. Fibres and filaments can be more effectively retained in position by incorporating them in a fabric. Background art EP-A-268498 describes a water-absorbent water-insoluble polymeric fibre, film, coating, bonding layer or foam, made by forming a substantially linear polymer of water-soluble ethylenically unsaturated monomer blends comprising carboxylic and hydroxylic monomers and then reacting the carboxylic and hydroxylic monomers in the linear polymer to form internal crosslinks within the polymer. EP-A-269393 describes a water-absorbent, water- insoluble crosslinked polymer fibre or film made by dry- extrusion of a solution of a substantially linear polymer formed from a water-soluble blend of monoethylenically unsaturated monomers comprising a plasticising monomer and evaporating the solvent. The fibre or film is further plasticised, stretched and then crosslinked. EP-A-342919 describes film or fibre made by extrusion and stretching from a polymer of water-soluble ethylenicall unsaturated monomers that include ionic monomer . counterionic lubricant compound is absorbed into the surfac of the fibre or film before or during the stretching. 5 EP-A-397410 describes a water-soluble linear polymer of carboxylic acid monomers such as acrylic acid and a hydroxylic monomer which can be crosslinked, after being shaped by extrusion of an aqueous solution of the polymer as fibres or films, to form crosslinks between the carboxyl and hydroxyl groups. GB-A-2082614 describes a . dry, solid, water-swellable absorbent comprising a blend of a water-insoluble absorbent polymer, which may be a covalently crosslinked or ionically co plexed anionic polyelectrolyte, and an extender material selected from uncrosslinked derivatives, starch, montmorillonite clay, attapulgite clay, seracite, talc, kaolin, silica and mixtures thereof. It states that the blend may be used as a film, aerated film, powder or fibre, but there is no disclosure as to how a blend of water- insoluble polymer and extender can be made into a fibre. Disclosure of the invention According to the present invention a fibre or filament of a water-absorbent water-insoluble fibrous material has a matrix of a crosslinked copolymer formed from 50 to 95% by weight of ethylenically unsaturated carboxylic monomer and 5 to 50% by weight of copolymerisable ethylenically unsaturated monomer, the matrix containing dispersed solid water-insoluble particles of a material which is chemically substantially non-reactive with the matrix copolymer. The dispersed solid particles are generally chosen to improve the properties of the fibre or filament; for example they may modify the absorption/retention characteristics of the fibre or filament, alter the bulk properties of the fibre or filament such as its electrical conductivity or X- ray opacity, or alter the ability of the fibre or filame to absorb chemicals. The dispersed particles are preferably less than microns in diameter, most preferably less than 5 microns. The dispersed solid particles may be formed inorganic salts or oxides or naturally occurring miner clays, or of any other substantially water-insoluble soli that can be reduced in particle size to a sufficient degre and are chemically substantially non-reactive towards th matrix copolymer. The fibre or filament may be formed by extruding dispersion of the solid water-insoluble particles in a aqueous solution of the matrix copolymer in its non crosslinked state through a spinneret into a gaseou environment to remove the water to form a fibre or filament and subsequently crosslinking the copolymer. The fibre or filament may be stretched subsequent t formation, preferably before the crosslinking system i activated. Although the crosslinking system can be a system tha is activated by irradiation, for instance ultraviolet light preferably it is a thermally activated system, in whic event the rate of crosslinking at the temperature prevailing during the stretching and earlier stages of th process should be such that there is substantially n crosslinking during these stages. By this means it i possible to optimise the stretching of the fibre or filamen while the polymer is linear and then to fix the polymer i its stretched configuration by crosslinking. « As a rule, the non-crosslinked polymer is substantiall linear and is formed from a water-soluble blend of monoethylenically unsaturated monomers that must be selecte such that the final crosslinked polymer is water-absorbent. Ways of selecting monomers for this purpose are known, for example from EP-A-397410 mentioned above. Generally, the water-soluble blend of monoethylenically unsaturated 5 monomers is an anionic blend and it optionally comprises a non-ionic monomer with the carboxylic acid monomer. The monomers used in the invention may be allylic but are generally vinylic, most preferably acrylic, monomers. Preferred carboxylic monomers are methacrylic acid or acrylic acid, but maleic acid or anhydride, itaconic acid or any of the other conventional ethylenically unsaturated carboxylic acids or anhydrides are also suitable. The copolymer can optionally additionally contain monomer units derived from an ethylenically unsaturated sulphonic acid such as 2-acrylamido-2-methylpropane sulphonic acid or allyl sulphonic acid. Carboxylic and sulphonic monomers may be present in the final polymer in free acid or water-soluble salt form, suitable salts being formed with ammonia, an amine or an alkali metal. The proportion of salt and free acid groups can be adjusted after formation of the cross¬ linked polymer or after polymerisation of the linear polymer or before polymerisation. Generally, the molar ratio of free carboxylic acid groups to alkali metal or other carboxylate salt groups in the final polymer (and often also in the monomers that are used to form the linear polymer) is from 1:1 to 1:10. The ratio is usually at least 1:2 and often 1:3. It is usually below 1:6 and often below 1:5. When the crosslinking reaction involves reaction with the carboxylic acid groups it is usually preferred that at least some of the carboxylic acid groups should be present as free acid groups before the crosslinking occurs. For instance, for this purpose, it may be adequate for 10 to 75%, preferably 25 to 75%, of the icid groups to be in free acid form before the crosslinking occurs. Although the linear polymer is generally made b polymerisation of carboxylic acid monomer (in free acid o salt form) , it is also possible to make the polymer b polymerisation of monomer that can be subsequently reacte to form the carboxylic acid monomer. For instance th carboxylic acid groups that are to be present (in free aci or salt form) in the crosslinked monomer may be presen initially in the linear polymer in the form of hydrolysabl ester groups, such as methyl ester groups, that can then b hydrolysed while in the form of a linear polymer to yiel carboxylic acid (free acid or salt) groups. The copolymerisable ethylenically unsaturated monome may be a water-soluble ethylenically unsaturated monome such as acrylamide or may be a water-insoluble monomer. On or more copolymerisable monomers may be present. A monome that will provide groups for internal crosslinking with th carboxylic groups (as discussed below) is usually included. The copolymerisable monomer may comprise an olefin, such a isobutylene (for instance for copolymerisation with malei acid or anhydride), and/or the monomer may be a plasticisin monomer, that is to say a monomer which results in the final polymer being more flexible and plasticised than it would b if the plasticising monomer had been replaced by a corresponding amount of the main anionic monomer that is in the polymer. Suitable plasticising monomers include aromatic ethylenically unsaturated monomers, such as acrylonitrile or styrenes (e.g. styrene or a substituted styrene), but they are preferably alkyl esters of acrylic or methacrylic acid or of another suitable unsaturated carboxylic acid. Vinyl acetate and other vinyl esters may be used. The alkyl group of the ester generally contains less than 24 carbon atoms and usually 2 or more. Preferred alkyl groups contain 1 to 10 carbon atoms, especially ethyl and also higher alkyl groups such as 2-ethylhexyl or other Q -CI Q alkyl groups. Particularly preferred plasticising monomers are methyl or ethyl acrylate or methacrylate, butyl acrylate or methacrylate and 2-ethyl hexyl acrylate or methacrylate. They are generally present in amounts of at least 2% and preferably at least 10% by weight based on the monomers used 5 for forming the copolymer, because lower amounts tend to give inadequate benefit. The amount is below 50%, and generally below 45%, by weight. Other non-ionic monomers that may be used include ethylenically unsaturated monomers that carry a pendent group of the formula -A B A R where B is ethyleneoxy, n is an integer of at least 2, A is propyleneoxy or butyleneoxy, m and p are each an integer less than n and preferably below 2 and most preferably zero, and R is a hydrophobic group containing at least 8 carbon atoms. R is usually a hydrocarbon group,for instance alkyl, aryl, aralkyl, alkaryl or cycloalkyl. The use of 1 to 50% by weight, generally 5 to 30% by weight, of such monomers can give plasticisation and can give improved adsorptive capacity and non-tackiness, especially in aqueous electrolytes. For a full description of suitable values of A, B, R n, m and p, reference should be made to EP-A-213799. Hydroxyalkyl esters of ethylenically unsaturated carboxylic acids, such as hydroxyalkyl methacrylates or acrylates, can also be included as plasticising monomer. For optimum plasticisation the hydroxyalkyl group contains at least 6 carbon atoms, for instance 6 to 10 carbon atoms. These monomers may be used, as plasticising monomers, in place of an equivalent amount of alkyl methacrylate or acrylate but, as explained below, the hydroxyalkyl methacrylate can also be present to serve as internal crosslinking agent. The substantially linear water-soluble copolymer may be formed from the monomer blend in any conventional manner. It may be preformed and then dissolved to form a polymer solution. For instance, it may be made by reverse-phase polymerisation if the ιt--nomer blend is soluble in water o by water-in-oil emulsion polymerisation if the blend i insoluble in water, e.g. at a low pH. However, this ca incur the risk that the polymer may be contaminated b 5 surfactant and this is undesirable. Preferably, therefore the polymer is made by aqueous solution polymerisation o other solution polymerisation methods. It may be drie before further processing, but preferably not. Generally, it is formed by solution polymerisation in the solvent i 10 which is it to be extruded (generally water) . The polymerisation can be conducted in a conventional manner in the presence of conventional initiators and/o chain-transfer agents to give the desired molecular weight. The concentration of polymer in the solution to be 15 passed through the spinneret is generally in the range 5 to 50% by weight and will be selected, having regard to the molecular weight of the polymer, so as to give a solution having a viscosity that is convenient for extrusion. The spinneret can be of the type conventionally used in 20 synthetic fibre production. The concentration of polymer is usually at least 15% by weight, with values of 30% to 45%, e.g. 35% to 40%, by weight often being particularly suitable. The solution that is extruded may have a viscosity as 25 low as, for instance, 20,000mPa.s at 20°C but generally the viscosity is at least 70,000 and usually at least 100,000 and sometimes at least 120,000mPa.s . It can be up to 150,000 or even 200,000mPa.s. Higher values are generally unnecessary. All these viscosities are measured at 20°C 30 using a Brookfield RVT spindle 7 at 20rpm. The viscosity desirably is also relatively high at the extrusion (spinning) temperature, which typically is elevated, for instance above 80°C but below the boiling point of the copolymer solution. Preferably therefore the solution at 35 80°C has a viscosity of at least 5,000 or 10,000mPa.s and most preferably at least 20,000mPa.s. For instance it may be in the range 50,000 to 100,000mPa.s. These values may be obtained by extrapolation from values obtained using a Brookfield RVT visco eter spindle 7 at 20rpm at a range of 5 temperatures somewhat below 80°C. The molecular weight of the linear polymer that is extruded may be as low as, for instance, 50,000 or 100,000 but preferably is above 300,000 and most preferably is above 500,000. For instance, it may be up to 1 million or higher. The solvent of the solution that is extruded is generally water but can be methanol or other suitable organic solvent or may be a blend of water and organic solvent. The solvent must be volatile so as to permit rapid evaporation after extrusion. The gaseous environment into which the solution is extruded to form filaments can be contained in a cell of the type conventionally used for dry spinning, or flash spinning can be used. The spun filaments can be taken up on conventional textile machinery. A conventional spin finish is usually applied to the filaments before they are taken up. The diameter of the final fibres or filaments preferably corresponds to a weight of below 20 decitex per filament, for example in the range 2 to 15 decitex per filament. This is the decitex after stretching; if stretching is used, the decitex per filament after initial extrusion may be higher than the range quoted above. Stretching is carried out before crosslinking. The linear copolymer is crosslinked after extrusion. The crosslinking can be effected by reaction into the backbone of the linear copolymer but preferably is effected by crosslinking through pendent groups provided by one or more of the monomers that have been polymerised to form the linear copolymer. The crosslinking can be ionic, for instance as a result of exposing the linear copolymer to any of the known ionic crosslinking agents, preferabl polyvalent metal comnjunds such as polyvalent aluminiu compounds, for example aluminium sulphate. Organi compounds may be used instead of inorganic compounds t provide the crosslinking. Preferably however the crosslinking is covalent between pendent groups in the linear copolymer. The covalent crosslinking generally arises as a result of the formation of ester, amide (or imide) or urethane groups by reaction with carboxylic acid groups after extruding the copolymer. Ester groups are preferred. The reaction may be with an external crosslinking agent. Various systems for externally crosslinking the copolymer are described in EP-A-269393 and these can be used in the present invention. For example, the carboxyl- functional linear polymer can be crosslinked by a diisocyanate to form urethane crosslinks or by a polyamine such as ethylene diamine to form amide crosslinks or by a polyfunctional reagent containing hydroxyl and/or epoxide groups to form ester crosslinks. Preferably, however, the polymer is internally crosslinked by reaction between reactive groups within the extruded copolymer. Usually, the carboxylic groups act as one type of reactive group and are reacted with hydroxyl, epoxide, amino or blocked isocyanate groups. Particularly preferred systems are described in detail in EP-A-268498. In these systems the extruded copolymer is formed from a monomer blend comprising monomer that provides carboxylic acid monomer groups and monomer that provides hydroxyl groups that can react with the carboxylic acid groups to form ester crosslinkages that contain only carbon and oxygen atoms in the linkages, and these carboxylic and hydroxyl groups are reacted after extrusion to form the said crosslinkages. Generally the carboxylic acid groups are provided by acrylic acid or methacrylic acid and the hydroxyl groups are provided by allyl alcohol, an epoxide-substituted vinyl monomer such as glycidyl methacrylate or a hydroxyalkyl ester of a vinyl carboxylic acid such as 2-hydroxyethyl acrylate, 2- hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate or 5 3-hydroxypropyl methacrylate or by vinyl alcohol groups. Alternative hydroxyl group-containing monomers are those of the formula CHR 1=CR2-Y-M a -0H, where R1 is hydrogen or 2 carboxy, R is hydrogen or methyl, Y is 0, CH,0 or COO, M is alkyleneoxy, for example ethyleneoxy or 1,2-propyleneoxy, and a is an integer greater than 1 and preferably at least 5, as disclosed in EP-A-397410. Alternatively, the comonomer can contain a primary or secondary amino group, for example 2-aminoethyl methacrylate, which reacts to form an amide crosslink, or it can contain an isocyanate group (which may need to be blocked to prevent crosslinking during extrusion), for example 2-isocyanatoethyl methacrylate, to form urethane crosslinks. Reference should be made to EP-A-269393, EP-A-268498 and EP-A-397410 for a full disclosure of suitable materials and methods of extruding filaments and of crosslinking that can be used in the present invention. As stated above, heat- activated crosslinking is preferred. The temperature used to crosslink the fibres or filaments can for example be in the range 150 to 250°C, with the temperatures during extrusion and stretching of the filaments being lower than the crosslinking temperature, preferably at least 30°C lower. The dispersed solid particles are chosen to improve the properties of the fibre or filament; for example they may modify the absorption/retention characteristics of the fibre or filament, alter the bulk properties of the fibre or filament, such as its electrical conductivity or X-ray opacity, or may alter the ability of the fibre or filament to absorb chemicals. The dispersed solid particles may for example be particles of inorganic salts, such as barium sulphate, of carbon, of oxides, such as silica or manganese dioxide, o naturally occurring mineral clays, such as kaolin, or of an other substantially water-insoluble solids than can b reduced in particle size by a sufficient degree and ar chemically substantially non-reactive towards the aqueou solution of the copolymer. According to one aspect of the invention the disperse solid particles improve the absorbency and retentio characteristics of the fibres or filaments for liquids. Th absorbency can be measured by the free swell test, in whic 0.5g fibre is dispersed in 30 ml. aqueous liquid and lef for 5 minutes. The aqueous liquid used is generally 0.9% b weight saline solution, which is generally absorbed to extent similar to body fluids such as urine. The test ca alternatively be carried out with either tap water o demineralised water, but the results quoted below are for 0.9% saline solution. For all absorbency measurements, the fibre is conditioned at 65% relative humidity and 20°C before being tested. The dispersion is then filtered through a sintered Mark 1 funnel of pore size 100-160 microns and is left for 5 minutes or until it stops dripping. The amount of water filtered through the funnel is weighed and the weight of water absorbed by the fibres is calculated by subtraction. In addition to the above test, the retention by the fibre or filament of the aqueous liquid (such as saline solution) after application of pressure is measured in the retention test by weighing the water expressed after application of pressure at about 3.4 KPa for 5 minutes or until dripping stops. The presence of solid particles in the fibres or filaments does not generally affect the free swell absorption of the fibres or filaments, but it may improve the absorption as measured by the retention test. In a further test of absorption, the absorbency under load is measured by maintaining the fibres or filaments in contact with a 0.9% by weight saline solution for an hou while applying a load of 1.7KPa. The presence of soli particles in the fibres or filaments may improve th absorbency under load as measured by this test. 5 A further absorbency/retention property which may be considered important in personal hygiene products is the dryness of the gel to the touch after it has absorbed an aqueous fluid. This may be measured by the following "wetback test", which is generally carried out following the free swell absorbency and retention test. The method consists of spreading a thin coating of swollen gel at its retention capacity evenly onto a 5cm x 5cm square marked on a glass plate. A weighed tissue is then placed lightly in contact with the square of gel for 30 seconds. The weight of liquid picked up by the tissue is then determined, and the results converted to g/square cm of gel. The presence of solid particles in the fibres or filaments can improve the dryness of the gel as measured by the wetback test. Dispersed solid particles which are effective in improving the absorbency and retention characteristics of the fibres or filaments include silica, which can for example be fumed or precipitated silica, a zeolite, for example a molecular sieve zeolite, or a mineral clay such as kaolin or bentonite. The dispersed solid particles can alternatively be used to impart additional properties to the fibres or filaments. For example, the particles can be particles of an intumescent glass such as those sold by I.C.I under the Trademark "Ceepree". Fibres or filaments having a high water absorbency and intumescent properties can thereby be produced, and these can be formed into woven or nonwoven fabrics having a valuable combination of fire-resistant properties. In a fire such a fabric intumesces to an expanded char which acts as an insulating protective layer. If water is played on the fabric in an attempt to put out the fire the fibres or filaments absorb water to form barrier layer which may prevent access of oxygen to th fire. Fibres or filaments containing dispersed intumescen glass can for example be used as a fire blanket or as fire-protective upholstery fabric. The dispersed solid particles can alternatively be particles of a material such as a zeolite having ability to absorb chemicals, so that the fibres or filaments have increased absorption of chemicals, for example increased odour absorption. Alternatively, particles of a zeolite having metal ions which confer antimicrobial properties, for example a zeolite containing copper, silver or zinc ions, can be used to form fibres or filaments having antimicrobial properties. Alternatively, the dispersed solid particles can be particles of a heavy metal salt, for example barium sulphate, to give x-ray opaque fibres, or can be particles of an electrically conductive material such as carbon black to give electrically conductive fibres. The proportion of particles in the fibre or filament is generally up to 10% by weight based on the dry weight of the copolymer. Usually, the proportion of particles is at least 1% by weight to achieve a significant effect. For many purposes the proportion of particles is up to 5% by weight, and preferably at least 1.5%, more preferably at least 2%. The size of the particles can for example be up to about 20 or 25 microns, more usually up to 15 microns. Whilst in general the size of the particles can be up to about half the diameter of the fibre or filament, a relatively low particle size, for example less than 10 microns and preferably less than 5 microns, is preferred when the proportion of particles in the fibre or filament is above 5% by weight. Particles of size less than 1 micron may be preferred, particularly for the purpose of improving the absorbency retention of the fibres or filaments or the strength or dryness of the gel formed when the fibres or filaments have absorbed an aqueous fluid. Prior to extrusion (spinning), it is necessary to produce a dispersion of the solid particles in the aqueous solution of the copolymer. The dispersion can be prepared by mixing the solid particles with the copolymer solution, which optionally may be diluted with water to reduce the viscosity. The fine dispersion can be produced using standard dispersing techniques such as ball milling, bead milling, or high-shear stirring or ultrasonically. It may be preferred to produce the dispersion of the solid particles in the copolymer solution by a two-stage process. In this case a concentrated dispersion of the solid particles in water or in a dilute solution of the copolymer, for example a 5 to 20% by weight solution, is produced and this is subsequently mixed with the main copolymer solution to produce the final solution for extrusion (spinning). The aqueous dispersion of solid particles can conveniently be formed in a high-shear mixer. The mixing of the concentrated dispersion with the copolymer solution can be carried out using standard mixing techniques such as high-shear or low- shear mixing, ultrasonically or by pumping the mixture through a static mixer. It is preferable that the mixture be spun into fibres as soon as possible because there may be a tendency for the dispersed solid particles to agglomerate. It is preferable that the mixing be carried out continuously as part of the spinning process. The polymer solution containing dispersed particles is capable of being converted into a variety of shaped forms such as fibres, filaments, fibrils, pulp, films, sheet or coatings, with evaporation of the solvent after shaping. The fibres or filaments produced can be further processed into milled fibres, chopped fibres, yarns, webs or woven, knitted or nonwoven fabrics. The water-absorbent water-insoluble fibres or filaments of the present invention can be used in various products They can, for example, be used in absorbent persona products such as tampons, disposable diapers, sanitar napkins or incontinence pads. The absorbent fibres o filaments are preferably used in combination with othe fibres, for example cellulosic fibres such as cotton o regenerated cellulose fibres, including multi-limbe cellulose fibres as described in EP-A-301874, o polypropylene or polyester fibres. The absorbent fibres ca be intimately mixed with said other fibres, for example b carding or air laying the fibres together to form a web of mixed fibres. Alternatively, the absorbent fibres or filaments can be used as a layer, for example a non-woven fabric, of absorbent fibres or filaments sandwiched between layers of other fibres. The proportion of absorbent fibres or filaments in a blend with cellulosic fibres for absorbent products can for example be at least 5% by weight and up to 95%, preferably at least 10% and up to 50%, by weight. The absorbent fibres or filaments can also be used at similar levels in conjunction with fluffed wood pulp or synthetic fibre pulp, for example polyolefin pulp, in absorbent products. A yarn, woven fabric or nonwoven fabric comprising the absorbent fibres or filaments can be used as a swellable material which prevents ingress of water in underground cables. A yarn or f bric tape can be used to wrap cable or can be laid longitudinally in the cable. The absorbent fibres or filaments can be used in many other applications of the types described in Research Disclosure, January 1992 at pages 60-61, for example in filters, absorbent liners or mats for packaging, disposable wipes, mats, shoe insoles or bed sheets, swellable gaskets or seals, moisture retention mats in horticulture, moisture- retaining packaging or swellable self-sealing stitching threads. The invention is illustrated by the following Examples, in which parts and percentages are by weight unless otherwise stated:- Example 1 A zeolite with an average particle size of less than 5 microns was dispersed in a 10% aqueous solution of a copolymer of acrylic acid, methyl acrylate and hexapropylene glycol monomethacrylate in a ratio of 60:35:5 using a ball mill to produce a paste containing 30% zeolite. 1 part of the paste was blended with 9 parts of a 40% solution of the copolymer using a barrel mixer. The mixture was directly extruded at 100°C through a spinneret into a gaseous medium to form filaments containing 8% zeolite. The filaments were crosslinked by heating at 200°C. The crosslinked filaments exhibited an enhanced ability to absorb odours from an aqueous liquid compared to a control filament without added zeolite. Example 2 A commercially available dispersion of colloidal silica in water was mixed with the copolymer solution described in Example 1 in a barrel mixer and spun into fibres and crosslinked in the same manner. The resulting fibres, containing 2% silica, exhibited a high gel strength when swollen in water compared to a control fibre without silica. Example 3 39.4g "Ceepree" intumescent glass particles of microfine grade (believed to be of particle size about 5 microns) were added to 300g water and dispersed using a Silverson high-shear mixer for 2 to 3 minutes. This suspension was added to 4.5kg of a 38% aqueous solution of a copolymer of 78 mole % acrylic acid (75% neutralised as sodium salt), 20 mole % methyl acrylate and 2 mole % hexapropylene glycol monomethacrylate. The suspension wa added at 55 to 65°C and stirred with a paddle stirrer. Afte 2 hours an evenly dispersed mixture was obtained, containin approximately 36% solids, with 2% Ceepree on polymer. This dispersion was spun into filaments through a spinneret into a cell where water was evaporated from the filaments. The temperature of the dispersion at the spinneret was between 90 and 100°C. The cell was heated by tube wall heaters at 150°C. The filaments were taken up at approximately 200m/min to give a fibre of approximately 15dtex. Samples of the resulting multifilament tow were crosslinked by heating in air under the conditions mentioned below. The free swell absorbency and absorbency retention of the resulting fibres were measured in each case: Example 3(a) 10 minutes at 200°C Free swell 49.7g/g, retention 35.1g/g. The gel was firm Example 3(b) 12 minutes at 200°C Free swell 42.4g/g, retention 27.9g/g. The gel was firm The fibre containing Ceepree showed a marked resistance to ignition compared to equivalent fibre without Ceepree. This was demonstrated by holding pads of fibre in a flame. The fibre containing Ceepree could be held in the flame indefinitely because of the formation of a protective char. The fibre behind the char showed no propensity to ignite. Fibre without Ceepree had increased fire resistance compared to most natural and synthetic fibres and was self- extinguishing on removal from the flame, but it burnt in the flame and shrank away from the flame. The combination of the intumescent filler and highly water-absorbent polymer in a fibre form shows advantages over either component alone, and could find application in fire barrier end uses. Example 4 31g of finely particuled zeolite (Union Carbide XTG 40) was dispersed in 750g water using a Silverson mixer. This was blended with the aqueous copolymer solution used in Example 3 to give a dispersion containing 2% zeolite on polymer. This dispersion was spun into filaments by the process of Example 3. Crosslinking was carried out by heating under the conditions mentioned below. The filaments were tested for free swell absorbency, retention of absorbency, absorbency under load and wetback using the tests described above, with the following results: The gels produced after swelling of the filaments in the absorbency tests were very dry to the touch and appeared firm. As a comparison, crosslinked filaments produced from the same copolymer solution without zeolite gave a result of 0.012g/cm 2 in the wetback test. The filaments and the gels produced from them had no odour if treated with an amount of a simple ester such as methyl acrylate which caused a noticeable odour when applied to filaments containing no particles, indicating that the zeolite had retained its odour-absorbing properties for simple esters. The results also indicate that the material keeps a high absorbency under load over a range of crosslinking conditions. Example 5 30.08g of Neosil GP (14-16 micron) silica was dispersed in 300g water using a Silverson mixer. This was mixed with the aqueous copolymer solution used in Example 3 to give a dope containing 2% silica on polymer. The dope was spun into filaments by the process of Example 3 and samples were crosslinked by heating under the conditions mentioned below and were tested as described in Example 4. The filaments had high absorbency under load over a range of crosslinking conditions. All of the gels felt and appeared dry to the touch, with the 10 minutes and 12 minutes samples being particularly good. This observation is backed up by the low wetback result for the 12 minutes sample.

Claims: CLAIMS 1. A fibre or filament of a water-absorbent water insoluble fibrous material having a matrix of a crosslinke copolymer formed from 50 to 95% by weight of ethylenicall 5 unsaturated carboxylic monomer and 5 to 50% o copolymerisable ethylenically unsaturated monomer, characterised in that the matrix contains dispersed solid water-insoluble particles of a material which is chemically substantially non-reactive with the matrix copolymer. 2. A fibre or filament according to claim 1, characterised in that the particle size of the dispersed particles is below 20 microns. 3. A fibre or filament according to claim 2, characterised in that the particle size of the dispersed particles is below 5 microns. 4. A fibre or filament according to any of claims 1 to 3, characterised in that the dispersed particles are particles of an intumescent glass, whereby the fibre or filament is useful in forming a fire barrier layer. 5. A fibre or filament according to any of claims 1 to 3, characterised in that the dispersed particles are particles of a zeolite, whereby the fibre or filament has increased ability to absorb odours. 6. A fibre or filament according to any of claims 1 to 3, characterised in that the dispersed particles are particles of silica, a zeolite or a naturally occurring mineral clay, whereby the fibre or filament has improved absorption and retention characteristics for liquids. 7. A fibre or filament according to any of claims 1 to 6, characterised in that the dispersed particles are present at 1 to 10% of the dry weight of the fibre or filament. 8.A fibre or filament according to claim 7, characterised in that the dispersed particles are present a 1.5 to 5% of the dry weight of the fibre or filament. 9. A fibre or filament according to any of claims 1 t 8, characterised in that the copolymer matrix is crosslinke by ester crosslinks. 10. A fibre or filament according to claim 9, characterised in that the copolymerisable ethylenically unsaturated monomer consists at least partly of a hydroxyl- functional or epoxide-functional comonomer, and that the ester crosslinks are formed by reaction between carboxylic acid groups derived from the carboxylic monomer and hydroxyl or epoxide groups derived from the copolymerisable monomer. 11. A process for the production of a fibre or filament as defined in any of claims 1 to 10, characterised in that a dispersion of the solid water-insoluble particles in an aqueous solution of the matrix copolymer in its non- crosslinked state is extruded through a spinneret into a gaseous environment to remove the water to form the fibre or filament, and the copolymer is subsequently crosslinked. 12. A process according to claim 11, characterised in that the concentration of the copolymer in the aqueous solution is 30 to 45% by weight. 13. A process according to claim 11 or 12, characterised in that the dispersion is passed through the spinneret at a temperature which is above 80°C but below the boiling point of the copolymer solution. 14. A process according to any of claims 11 to 13, characterised in that the dispersion has a viscosity at 80°C of at least 20,000 mPa.s. 15. A process according to any of claims 11 to 14, characterised in that the crosslinking is effected b heating the fibre or filament at a temperature in the rang 150 to 250°C. 16. A process according to any of claims 11 to 15, characterised in that the fibre or filament is stretche before effecting the crosslinking of the copolymer.

Inventors: AKERS PAUL JOHN, BRUNSKILL WILLIAM, AKERS, PAUL, JOHN, BRUNSKILL, WILLIAM
Applicants: COURTAULDS PLC
Application year: 1992
Main classification: D01F1
IPC codes: C08F220, C08L101, D01F1, D01F6