OPTICAL MIRROR AND OPTICAL DEVICE USING THE SAME

Abstract: An optical mirror which can reflect optical beams of a plurality of wavelengths while satisfying a phase matching condition required for a non-linear optical material, without the optical loss due to a phase error involved in generation of harmonics, optical mixing, etc., thereby improving conversion efficiency; and an optical device using this mirror. The optical mirror includes a transparent substrate coated on one side with a multilayer composed of films (2), (3) that selectively reflect their corresponding wavelengths. A phase control layer (4) is provided between the two films to eliminate the difference in phase between the light reflected by one film (2) and the light reflected by the other (3). According to this optical mirror, reflection can be made while satisfying the phase matching condition required for non-linear optical materials, and conversion efficiency is high. Accordingly, the present invention can be utilized suitably for the generation of the second harmonic, optical mixing, the generation of optical parametric, and so forth.

Description: This invention relates to an optical mirror and an optical device using the same. The mirror, in a preferred application, is incorporated with a plurality of dielectric reflection multilayer film coatings each of which has high reflectance to plural wavelengths or with a combination of dielectric reflection multilayer film coatings and metal reflection film coatings. The optical mirror may be suitable for second harmonic generation, optical mixing, optical parametric generation and the like applying nonlinear optical effects. A nonlinear optical device for converting an optical frequency by applying nonlinear interaction, e.g., second harmonic generation, of an optical wave in a nonlinear optical material, in many cases, uses two concave reflection mirrors for laser-resonating. One of these reflection mirrors is a total reflection mirror (or a high reflection mirror) while the other is a reflection mirror through which a portion of laser beam transmits. The high reflection mirror among them comprises, as shown in, for example, Fig. 4, plural reflection multilayer films 2 and 3 consisting of a plurality of reflection films 2a, 2b, 3a, and 3b laminated on one surface of a transparent substrate 1, each of which multilayer films 2 and 3 corresponds to each wavelength of plural wavelengths of a light beam to selectively reflect one of said plurality of wavelengths, respectively. Each of the reflection multilayer films 2 and 3 is formed by alternately laminating usually different dielectric materials (e.g., SiO 2 and TiO 2 ), as shown herein as the reflection films 2a and 2b or 3a and 3b, at such a film thickness as being capable of providing a maximum reflectance at each specific wavelength. However, in the conventional optical mirror for use in a plurality of wavelengths, as shown in Fig. 4, there is considered only a reflection amplitude, so that a phase matching condition required for nonlinear optical materials is not satisfied. As a result, when the second harmonic generation, the optical mixing or the like is performed using the nonlinear optical material, there occurs a disadvantage that optical loss generates due to a phase shift between an exciting light beam and a newly generated light beam when these light beams are reflected by a mirror. From WO 86/02775 and JP-A-62 148 904 multilayer mirrors are known for the separation of wavelengths. An object of the present invention is to provide an optical mirror and an optical device using the same in which the mirror is capable of reflecting a light beam having a plurality of wavelengths with the phase matching condition required for nonlinear optical materials being satisfied, so that no optical loss due to the phase shift is generated even if the harmonic generation, the optical mixing or the like is performed, thereby being capable of improving conversion efficiency. According to the invention, there is provided an optical mirror comprising a plurality of reflection films formed on one surface of a transparent substrate, each film being arranged to selectively reflect a respective one of a plurality of wavelengths, and a phase difference adjusting layer formed between two of said reflection films for adjusting the relative phase between light beams respectively reflected by the two reflection films in use of the optical mirror. The present invention may apply the following embodiments. (1) The plural wavelengths constituting the light beam are in a relation of a multiple of an integral number or in relation of a reciprocal of an integral number with each other. (2) Said phase difference adjusting layer is made of the same material as any one of said reflection films. (3) Said phase difference adjusting layer consists of an air gap. (4) Said phase difference adjusting layer is formed between adjacent two reflection multilayer films. (5) Said reflection films each are laminated as two layers. Of course, more layers may be applied. (6) Said reflection films consist of multilayer films. (7) Said reflection films consist of multilayer films, and said phase difference adjusting layer is not formed between a first reflection multilayer film for reflecting a light beam having a certain wavelength and a second reflection multilayer film for reflecting a light beam having a wavelength different from the above wavelength but is formed between the multilayer films of the first reflection multilayer film or between the multilayer films of the second reflection multilayer film. (8) The transparent substrate is made of glass, a nonlinear optical crystal, a metal or the like. All possible combinations of (1) to (8) may be also applied. An optical mirror according to the present invention can be applied to various optical devices such as a second harmonic generating device, a multi-wavelengths mixing device, a sum frequency generating device, a difference frequency generating device or a parametric oscillating device. Principles of the present invention will be described with reference to Figs. 1 and 6. As shown in Fig. 1, when the second harmonic generation of a light beam is performed using, for example, KNbO 3 , reflection films 102 for, for example, 860 nmHR are at first formed on both end surfaces of KNbO 3 101, respectively, to trap a fundamental wave of 860 nm between the reflection films for 860 nmHR. This results in generation of a second harmonic (SHG) of 430 nm from the end surfaces. The output thereof is indicated by a line S (□ - □ - □) in Fig. 6. Subsequently, a reflection film 103 for 430 nmHR is laminated on one of the reflection films for 860 nmHR. As a result, the second harmonic of 430 nm is reflected by the reflection film for 430 nmHR and emerges from the other end surface. The output of this case is indicated by a line W (○ - ○ - ○) in Fig. 6. It is because the phase is reversed that the output becomes zero at a wavelength of 1.3. In this event, no gap is especially formed between the left-hand reflection film 102 for 860 nmHR and the reflection film 103 for 430 nmHR in Fig. 1. To match the phase difference between the light beam of 430 nm and that of 860 nm, a phase difference adjusting layer 104 is formed between the reflection film 102 for 860 nmHR and the reflection film 103 for 430 nmHR. The resulting output is as indicated by a line C (Δ - Δ - Δ) in Fig. 6. The film thickness of the phase difference adjusting layer, i.e., a distance between the reflection film for 860 nmHR and the reflecting film for 430 nmHR, which is equal to 4λ/5 (λ = 430 nm) in this example, is determined depending on the phase difference for each case. A preferred embodiment of the present invention will be described below with reference to the drawing. An optical mirror according to the present invention will be described with reference to the drawing in which, Fig. 2 shows an optical mirror according to an embodiment of the present invention when applied to a light beam having two different wavelengths. The optical mirror comprises a first reflection multilayer film 2 for reflecting selectively one wavelength of the two wavelengths of said light beam, formed on one surface of a transparent substrate 1 such as a concave mirror, a second reflection multilayer film 3 adjacent to the reflection multilayer film 2 for reflecting selectively the other wavelength, and a layer 4 positioned therebetween for adjusting phase difference between the light beams reflected by said two reflection multilayer films 2 and 3. The first reflection multilayer film 2 comprises a laminate of two reflection films 2a and 2b each reflecting selectively one wavelength, said laminate being prepared by alternately laminating each reflection film. The second reflection multilayer film 3 comprises a laminate of two reflection films 3a and 3b each reflecting selectively the other wavelength, said laminate being prepared by alternately laminating each reflection film. The method itself for forming the first reflection multilayer film 2 or the second reflection multilayer film 3 may be the same as the conventional method, which can be formed typically by selecting two of the dielectric materials such as SiO 2 and TiO 2 , depending on the selected wavelength to laminate alternately the dielectric materials at such a film thickness providing a maximum reflectance at each specific wavelength as being capable of (generally a film thickness corresponding to 1/2 wavelength) using techniques such as deposition or sputtering. The thickness of the reflection multilayer film 2 or 3 is generally 2 about ∼ 4 µm, though it significantly varies depending on the thickness or the number of layers of the reflection films 2a, 2b or 3a, 3b. In addition, in the present invention, the layer 4 is formed between adjacent two reflection multilayer films 2 and 3, which layer adjusts the phase difference between the light beams reflected by the reflection multilayer films. The layer 4 is a layer for reflecting the light beams having a plurality of wavelengths at a specific phase difference by means of adjusting the interrelation, especially the phase difference between the light beams reflected by the reflection multilayer films and is made of the same dielectric material such as SiO 2 or TiO 2 as the material of the reflection film and preferably the same material as the reflection material of one of the two reflection films. The phase difference adjusting layer 4 may preferably be formed between the two reflection multilayer films 2 and 3, though it may be formed between any adjacent two reflection films 2a and 2b or 3a and 3b composed of the reflection multilayer film 2 or 3 of the adjacent two reflection multilayer films 2 and 3. As a method for preparing the phase difference adjusting layer 4, a method such as deposition or sputtering is generally applied. The thickness of the phase difference adjusting layer 4 is generally 0.2 ∼ 1 µm, though it may be varied depending on the phase difference. Light beams applied to the optical mirror according to the present invention may be those having a plurality of wavelengths. While the optical mirror according to the present invention has thus been described in conjunction with the example of application to the light beam having two wavelengths , it is apparent that the present invention can be applied to a light beam having three or more wavelengths by means of providing all of the reflection multilayer films which has high reflectance corresponding to each wavelength as well as providing all of the above mentioned phase difference adjusting layer formed between the adjacent two reflection multilayer films or between any adjacent two reflection films of either one of the reflection multilayer films among these reflection multilayer films. Further, it is apparent that the reflection films constituting each of the multilayer reflection films may be three or more kinds, though the reflection films are two kinds in said example. Next, an embodiment of the optical mirror according to the present invention applied to an optical device capable of using for second harmonic generation is shown in Fig.3. In Fig. 3, 11 represents a laser diode, 12 represents a Faraday isolator, 17 represents a collimator lens, 13 represents a condenser lens, 14 represents a two-wavelengths high reflection concave mirror (an optical mirror), 15 represents a single wavelength high reflection concave mirror and 16 represents a nonlinear optical monocrystal. The optical mirror according to the present invention is set and used at the position 14. Action of the optical mirror is described in conjunction with an example shown in Fig. 2. One wavelength of a light beam having two wavelengths introduced from the side of the transparent substrate 1 is reflected by the reflection multilayer film 2, during passing therethrough, which is composed of laminated two different reflection films 2a and 2b. The other wavelength transmits through the reflection multilayer film 2 and the phase difference adjusting layer 4 without being substantially reflected, which is then reflected by the reflection multilayer film 3, during passing therethrough, which is comprised of laminated two different reflection films 3a and 3b. In this event, the phase difference between the light beams reflected by both reflection multilayer films 2 and 3 is adjusted by the phase difference adjusting layer 4 formed between these multilayer films. Accordingly, said light beam having a plurality of wavelengths is reflected due to the specific phase difference. This results in prevention of optical loss. In addition, when such an optical mirror is set at 14 of an optical device as shown in Fig.3 to perform the second harmonic generation, the optical mirror reflects the light beam having a plurality of wavelengths while satisfying the phase matching condition required for the nonlinear optical effect, thereby improving conversion efficiency. Brief Description of the Drawing Fig. 1 is a view showing the action principle of an optical mirror according to the present invention; Fig. 2 is a partially cutaway sectional view showing an optical mirror according to an embodiment of the present invention; Fig. 3 is a schematic side view of an optical device using an optical mirror according to the present invention; Fig. 4 is a partially cutaway sectional view showing the conventional optical mirror made in comparative Example; Fig. 5 is a partially cutaway sectional view showing a referential optical mirror made in Reference Example; and Fig. 6 shows high-frequency curves measured using an optical device according to Example 2 in which optical mirrors made in Example 1 and Comparative Examples 1 and 2 are set. Best Mode for carrying out the Invention Practical examples are described where the above mentioned optical mirror is applied. <Example 1> As shown in Fig. 2, a first reflection multilayer film 2 that exhibits a high reflectance at 430 nm was formed on a transparent substrate 1, which is made of a standard glass of BK7 glass produced by Sigma Optical Device Inc., by alternately laminating a reflection film 2a (0.13 µm in thickness) consisting of SiO 2 thin films and a reflection film 2b (0.10 µm in thickness) consisting of TiO 2 thin films using deposition at such a film thickness as being capable of providing a maximum reflectance at a wavelength of 430 nm to produce twenty-nine layers (fourteen cycles plus one layer). SiO 2 was then laminated thereon to form a phase difference adjusting layer 4 (0.21 µm in thickness) according to deposition at a thickness 4λ/5 (λ = 430 nm)-thicker in optical thickness when measured at 430 nm than those of reflection films 3a consisting of SiO 2 thin films at the thirty-first layer and later to be formed thereafter (after forming the phase difference adjusting layer at the thirtieth layer). A second reflection multilayer film 3 that exhibits a high reflectance at 860 nm was formed thereon by alternately laminating reflection films 3a (0.21 µm in thickness) consisting of TiO 2 thin films and reflection films 3b (0.26 µm in thickness) consisting of SiO 2 thin films using deposition at such a film thickness as being capable of providing a maximum reflectance at a wavelength of 860 nm to produce twelve layers (six cycles). Thus, a two-wavelengths high reflection optical mirror (hereinafter referred to as C-coat mirror) was made with the forty-two layers in total. <Comparative Example 1> An optical mirror (hereinafter referred to as W-coat mirror) for comparison as shown in Fig. 4 was made in the same manner as in the Example 1 except that the phase difference adjusting layer was not formed. <Comparative Example 2> An optical mirror (hereinafter referred so as S coat mirror)for comparison as shown in Fig. 5 was made by alternately laminating, on the transparent substrate 1 used in Example 1, reflection films 3a (0.21 µm in thickness) consisting of TiO 2 thin films and reflection films 3b (0.26 µm in thickness) consisting of SiO 2 thin films by means of deposition at such a film thickness as being capable of providing a maximum reflectance at a wavelength of 860 nm to produce twelve layers(six cycles). Then, S-coat mirror, W-coat mirror and C-coat mirror made as mentioned above were alternately applied as the high reflecting concave mirror 14 to the device shown in Fig. 3 to measure second harmonic outputs. Specifications for the device in Fig. 3 are as follows: Laser diode 11: Laser diode SLD7033101 produced by SANYO Co. (The oscillation wavelength was set at around 862 nm) Faraday isolator 12: Faraday isolator ISO-7885 produced by New Port Co. Condenser lens 13: Convex lens having a 62.9 mm focal length prepared by applying low-reflective coating on a standard glass of BK7 glass Single wavelength high reflection concave mirror 15: One having 99.95 % of reflectance at 860 nm with a substance made of a standard glass of BK7 glass Nonlinear optical monocrystal 16: One prepared by optically polishing the a-surface of a KNbO 3 monocrystal having 6 mm length before applying low-reflecting coating. The nonlinear optical monocrystal 16 was held at about 31 °C by adjusting the temperature thereof using a Peltier element. Collimator lens 17: FL-40B convex lens manufactured by New Port Co. Distance between the mirrors 14 and 15: about 13 mm In the optical device as above-mentioned, the harmonic outputs were measured, at a wavelength to which the fundamental wave of the resonator resonates, by means of varying the temperature of the nonlinear optical monocrystal 16 by 0.1 °C, thereby inducing an electric current in the laser diode. The results are shown in Fig. 6 (in the figure, C is for C-coat mirror, W is for W-coat mirror and S is for S-coat mirror). The data obtained by changing the temperature of said monocrystal 9 were converted to the wavelengths based on 0.3nm = 1 °C. As apparent from the results, C-coat mirror according to the present invention provides the harmonic output of about double as compared with W-coat mirror and S-coat mirror. The present Example is an example of the second harmonic generation using KNbO 3 monocrystal, and when the optical mirror of the present invention is used, an optical device such as a highly effective nonlinear optical element can be manufactured because high reflection is obtained while satisfying the phase matching condition required for entire nonlinear optical effects such as multiple wavelengths mixing, sum frequency generation, difference frequency generation and parametric oscillation. Industrial Applicability According to the present invention it is possible to provide an optical mirror and an optical device using the same in which the mirror is capable of reflecting a light beam having a plurality of wavelengths with the phase matching condition required for nonlinear optical materials being satisfied, so that optical loss due to the phase difference does not generate even if second harmonic generation, optical mixing or optical parametric oscillation are performed, thereby being capable of improving conversion efficiency.

Claims: An optical mirror comprising a plurality of reflection films (2,3) formed on one surface of a transparent substrate (1), each film being arranged to selectively reflect a respective one of a plurality of wavelengths, and a phase difference adjusting layer (4) formed between two of said reflection films (2,3) for adjusting the relative phase between light beams respectively reflected by the two reflection films (2,3) in use of the optical mirror. An optical mirror as claimed in Claim 1, wherein the plurality of wavelengths which the reflection films (2,3) are respectively arranged to reflect are in a relation of a multiple of an integral number or in a relation of a reciprocal of an integral number with each other. An optical mirror as claimed in Claim 1 or 2, wherein said phase difference adjusting layer (4) is made of the same material as any one of said reflection films (2,3). An optical mirror as claimed in Claim 1, 2 or 3, wherein said phase difference adjusting layer (4) is formed between adjacent two multilayer reflection films (2,3). An optical mirror as claimed in any one of Claims 1 to 4, wherein said reflection films (2,3) each consist of multilayer films (2a, 2b). An optical mirror as claimed in Claim 5, wherein said phase difference adjusting layer (4) is formed between the multilayer films (2a, 2b) of a first reflection multilayer film (2) or between the multilayer films (3a, 3b) of a second reflection multilayer film (3b). An optical device comprising an optical mirror claimed in any one of Claims 1 to 6.

Inventors: EDA AKIRA, EDA, AKIRA, Eda, Akira, c/o Mitsui Petrochemical Ind., Ltd.
Applicants: MITSUI PETROCHEMICAL IND, MITSUI PETROCHEMICAL INDUSTRIES, LTD.
Application year: 1992
Main classification: G02B5
IPC codes: G02B5, G02F1