Polycarbonate resins having terminal vinyl groups and process for producing the same

Abstract: Novel polycarbonate resins having 2 to 400 structural units of bisphenol carbonate on average and vinylbenzoic acid terminal groups bonded to the bisphenol residues have a high stability and are produced by interfacial polymerization or solution polymerization, using vinylbenzoic acid as a molecular weight modifier.

Description: BACKGROUND OF THE INVENTION 1) Field of the Invention The present invention relates to novel polycarbonate oligomers or resins having terminal vinyl groups and a process for producing the same. By virtue of vinyl groups existing at the polymer terminals, the present polycarbonate oligomers or resin (hereinafter referred to as "polycarbonate resin") are useful for various applications such as raw materials for producing block copolymers with other resins, a reactive resin modifier, or film materials. 2) Prior Art Heretofore, it has been known to use monovalent phenols such as p-tertiary butylphenol, phenol, etc. as a terminating agent or a molecular weight modifier for polycarbonate resins or to use long chain alkylphenols to improve their flowability (Japanese Patent Publication No. 52-50078). The polycarbonate resins produced with these prior art molecular weight modifiers, have essentially inactive polymer terminals, because their molecular chain terminals are closed. Thus, in their modifications by making their compositions with other resins or fillers, their mating resins are limited or the heat resistance of the resulting compositions are deteriorated due to simple blending. Polycarbonate resin block copolymers prepared by addition polymerisation of terminally unsaturated polycarbonate resins with a vinyl compound are disclosed in Japanese Patent Publication No. 48-25076, where aliphatic compounds are exemplified as unsaturated groups and vinylphenol is also disclosed. However, since the vinyl group of vinylphenol as an aromatic compound is highly reactive, gels are formed during the reaction. That is, it has been desired to obtain highly stable polycarbonate resins having vinyl terminals. EP-A-0 072 065 discloses cross-linkable polymers which contain a backbone segment which may be formed from inter alia a polycarbonate chain which have pendent therefrom substituted olefinic groups which may be selected from inter alia p-vinylbenzoic acid. EP-A-0 006 579 discloses high-molecular weight aromatic polycarbonates based on diphenols and monofunctional chain stoppers of the following formula in which m is 0 or 1, and R is either a hydrogen atom or a C 1-3 alkyl group. SUMMARY OF THE INVENTION As a result of extensive studies to alleviate these disadvantages connected with the prior art, the present inventors have found that polycarbonate resins having vinylbenzoic acid terminals have a very good stability. An object of the present invention is to provide highly stable polycarbonate resins having vinyl terminals. Another object of the present invention is to provide a process for producing highly stable polycarbonate resins having vinyl terminals. That is, the present invention provides a polycarbonate resin whose polymer chains contain on average more than 20 to 400 structural units represented by the following general formula (1) and having terminal groups represented by the following general formula (2) bonded to the bisphenol residues of the general formula (1): wherein A represents a straight, branched or cyclic alkylidene group having 1 to 10 carbon atoms, an aryl-substituted alkylidene group, an arylene group, or -O-, -S-, -CO-, -SO- or -SO 2 -; and R 1 , R 2 , R 3 and R 4 are the same or different from one another and each represents hydrogen, halogen, an alkyl group having 1 to 6 carbon atoms or an aryl group. Furthermore, the present invention provides a process for producing a polycarbonate resin having vinyl terminals by: (a) interfacial polymerisation carried out by reacting a divalent phenol compound with phosgene in an inert organic solvent in the presence of an aqueous alkali solution, then adding a molecular weight modifier and a polymerisation catalyst to the reaction mixture, or (b) solution polymerisation carried out by dissolving a divalent phenol compound and a molecular weight modifier in pyridine or a mixture of pyridine and an inert solvent, and introducing phosgene thereto, characterised in that the molecular weight modifier is a vinylbenzoic acid represented by the following general formula (3): DETAILED DESCRIPTION OF THE INVENTION In the present invention, the polycarbonates having structural units of more than 20 to 400 or below on average represented by the formula (1) are called "polycarbonate resins". As well as such resins, the process of the present invention is also capable of producing polycarbonates having 2-20 structural units. These lower molecular weight compounds are called "polycarbonate oligomers". The number of the structural units represented by formula (1) roughly depends on an amount of a molecular weight modifier to be used. Thus, in the production of polycarbonate oligomers, 100 to 10 moles, preferably 40 to 20 moles, of vinylbenzoic acid represented by the general formula (3) is used per 100 moles of a divalent phenol compound. In the production of polycarbonate resins, 10 to 0.5 moles, preferably 7 to 2 moles, of the vinylbenzoic acid is used per 100 moles of the divalent phenol compound. In the present invention, a so far well known molecular weight modifier can be used together with the vinylbenzoic acid represent by the general formula (3). The present polycarbonate resins can be produced in the same manner as in the conventional process for producing polycarbonate resins except that vinylbenzoic acid represented by the general formula (3), for example, 2-vinylbenzoic acid, 4-vinylbenzoic acid, etc. is used as a molecular weight modifier or a terminating agent. That is, the present polycarbonate resins can be produced by interfacial polymerization or solution polymerization, using a vinylbenzoic acid represented by the general formula (3) as a molecular weight modifier or a terminating agent. In the interfacial polymerization, a divalent phenol compound is reacted with phosgene in an inert organic solvent in the presence of an aqueous alkali solution and then the molecular weight modifier and a polymerization catalyst such as a tertiary amine or a quaternary amine are added to the reaction mixture, thereby conducting polymerization. In the solution polymerization using pyridine, a divalent phenol compound and the molecular weight modifier are dissolved in pyridine or a mixture of pyridine with an inert solvent, and phosgene is introduced into the solution, thereby directly producing the polycarbonate resins. In the interfacial polymerization, the molecular weight modifier can be added during the reaction of the divalent phenol compound with the phosgene. The present polycarbonate resins can be used in various applications. In paint applications, polycarbonate oligomers produced by the process of the present invention are used, and preferable divalent phenol compounds for the paint applications include 1,1-bis(4-hydroxyphenyl)cyclohexane, 1,1-bis(4-hydroxyphenyl)-1-phenylethane, 2,2-bis(4-hydroxy-3-methylphenyl)propane, etc. Specifically preferable divalent phenol compounds for the present polycarbonate resins include, for example, bis(4-hydroxyphenyl)methane, bis(4-hydroxyphenyl)ether, bis(4-hydroxyphenyl)sulfone, bis(4-hydroxyphenyl)sulfoxide, bis(4-hydroxyphenyl)sulfide, bis(4-hydroxyphenyl)ketone, 1,1-bis(4-hydroxyphenyl)-ethane, 2,2-bis(4-hydroxyphenyl)propane, 2,2-bis(4-hydroxyphenyl)butane, 1,1-bis(4-hydroxyphenyl)cyclo-hexane, 2,2-bis(4-hydroxy-3,5-dibromophenyl)propane, 2,2-bis(4-hydroxy-3,5-dichlorophenyl)propane, 2,2-bis(4-hydroxy-3-bromophenyl)propane, 2,2-bis(4-hydroxy-3-chlorophenyl)propane, 2,2-bis(4-hydroxy-3-methylphenyl)propane, 2,2-bis(4-hydroxy-3,5-dimethylphenyl)propane, 1,1-bis(4-hydroxyphenyl)-1-phenylethane, bis(4-hydroxyphenyl)diphenylmethane, etc. Inert organic solvents for use in the present invention include, for example, chlorinated hydrocarbons such as dichloromethane, 1,2-dichloroethane, 1,1,2,2-tetrachloroethane, chloroform, 1,1,1-trichloroethane, carbon tetrachloride, monochlorobenzene, dichlorobenzene, etc.; aromatic hydrocarbons such as benzene, toluene, xylene, ethylbenzene, etc.; and etheral compounds such as diethylether, etc., and can be used in a mixture thereof. If desired, solvents with an affinity to water, such as other ethers than the above-mentioned, ketones, esters, nitriles, etc. can be used within such a range that the resulting solvent mixture may not be completely solvent in water. Polymerization catalysts for use in the present invention include, for example, tertiary amines such as trimethylamine, triethylamine, tributylamine, tripropylamine, trihexylamine, tridecylamine, N,N-dimethylcyclohexylamine, pyridine, quinoline, dimethylaniline, etc., and tertiary amines such as trimethylbenzylammonium chloride, tetramethylammonium chloride, triethylbenzylammonium chloride, etc. The present polycarbonate resins are produced from the above mentioned components as essential ones. A branching agent can be used together in the present invention. That is, 0.01 to 3% by mole, particularly 0.1 to 1.0% by mole, of a branching agent can be used on the basis of the divalent phenol compound to produce branched polycarbonates. Branching agents for use in the present invention include, for example, polyhydroxy compounds such as fluoroglycine, 2,6-dimethyl-2,4,6-tri(4-hydroxyphenyl)heptene-3, 4,6-dimethyl-2,4,6-tri(4-hydroxyphenyl)heptene-2, 1,3,5-tri(2-hydroxyphenyl)benzene, 1,1,1-tri(4-hydroxyphenyl)ethane, 2,6-bis(2-hydroxy-5-methylbenzyl)-4-methylphenol, α,α',α''-tri(4-hydroxyphenyl)-1,3,5-triisopropylbenzene, etc.; 3,3-bis(4-hydroxyaryl)oxyindol (=isatinbisphenol), 5-chloroisatinbisphenol, 5,7-dichloroisatinbisphenol, 5-bromoisatinbisphenol, etc. The present polycarbonate resins have highly active terminals and thus can be used as raw materials for copolymerization or for the production of compositions with such resins that are not readily compatible with the conventional polycarbonates, resulting in failure to form useful compositions, that is, for the production of compositions with other polymers readily reactable with vinyl groups by melt mixing. That is, the present polycarbonate resins can be used alone or together with conventional polycarbonate resins. The present polycarbonate resins may further contain an antioxidant, a photo-stabilizer, a coloring agent, an inorganic or organic filler, a reinforcing agent such as carbon fibers, glass fibers, a lubricant, an antistatic agent, etc., when desired in view of end use. PREFERRED EMBODIMENTS OF THE INVENTION The present invention will be described in detail below, referring to Examples and Comparative Examples. Example 1 3.7 kg of sodium hydroxide was dissolved in 42 ℓ of water, and further 7.3 kg of 2,2-bis(4-hydroxyphenyl)propane (which will be hereinafter referred to as "BPA") and 8 g of sodium hydrosulfite were dissolved therein, while keeping the solution at 20°C. Then, 28 ℓ of methylene chloride (which will be hereinafter referred to as "MC") was added thereto, and 156 g of p-vinylbenzoic acid (which will be hereinafter referred to "Al") was added thereto with stirring. Then, 3.5 kg of phosgen was introduced therein over 60 minutes. After the introduction of phosgen, the reaction solution was vigorously stirred to emulsify the solution. After the emulsification, 8 g of triethylamine (which will be hereinafter referred to as "TEA") was added thereto, and stirring was continued for about one hour to conduct polymerization. Then, the polymerization solution was separated into an aqueous phase and an organic phase. The organic phase was neutralized with phosphoric acid and then repeatedly washed with water until the pH of the washing solution became neutral. Then, 35 ℓ of isopropanol was added thereto to precipitate the polymers. Then, the precipitates were recovered therefrom by filtration, and dried, whereby white powdery polycarbonate resin was obtained. Physical properties of the thus obtained polycarbonate resin are shown in Table 1. Comparative Example 1 Polymerization was carried out in the same manner as in Example 1 except that 158 g of p-t-butylphenol (which will be hereinafter referred to as "PTBP") was used in place of 156 g of A1. Physical properties of the resulting resin are shown in Table 1. Examples 2 to 5 Polycarbonate resins were prepared from of various compositions shown in Table 1 in the same manner as in Example 1, and physical properties of the resulting resins are shown in Table 1. Abbreviations used in Table 1 have the following meanings: BPA: 2,2-bis(4-hydroxyphenyl)propane BPZ: 1,1-bis(4-hydroxyphenyl)cyclohexane BPAP: 1,1-bis(4-hydroxyphenyl)-1-phenylethane TBA: 2,2-bis(4-hydroxy-3,5-dibromophenyl)propane A1: 4-vinylbenzoic acid A2: 2-vinylbenzoic acid PTBP: p-tertiary butylphenol Mv: viscosity average molecular weight IR: Infrared absorption spectra by an infrared spectrometer IR-435, made by Shimadzu Seisakusho, K.K., Japan, based on KBr method and film method, where the presence or absence of stretching vibration of ester bond terminal (C=0) is shown. Ex. & Comp. Ex. No. Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Comp. Ex. 1 Divalent phenol BPA BPA BPAP BPA/BPZ =1/1 BPZ BPA Molecular weight modifier (% by mole) A1 3.3 A2 6.4 A1 5.0 A1 3.8 A1 3.3 PTBP 3.3 Mv × 10 4 2.5 1.6 2.0 2.1 2.4 2.5 IR (1740 cm -1 ) occurred occurred occurred occurred occurred none Example 6 3.7 kg of sodium hydroxide was dissolved in 42 ℓ of water, and then 7.3 kg of 2,2-bis(4-hydroxyphenyl)propane (which will be hereinafter referred to as "BPA") and 8 g of sodium hydrosulfite were dissolved therein while keeping the solution at 20°C. Then, 28 ℓ of methylene chloride (which will be hereinafter referred to as "MC") was added thereto, and 1.44 kg of p-vinylbenzoic acid (which will be hereinafter referred to as "A1") was added thereto with stirring, and then 4.4 kg of phosgene was introduced therein over 60 minutes. After the introduction of phosgen, the reaction solution was vigorously stirred to emulsify the solution. After the emulsification, 8 g of triethylamine (which will be hereinafter referred to as "TEA") was added thereto, and stirring was continued for about one hour to carry out polymerization. The resulting polymerization solution was separated into an aqueous phase and an organic phase, and the organic phase was neutralized with phosphoric acid and repeatedly washed with water until the pH of the washing solution became neutral, and then 35 ℓ of isopropanol was added thereto to precipitate the polymers. The precipitates were recovered by filtration and dried, whereby white powdery polycarbonate oligomer was obtained. Physical properties of the thus obtained polycarbonate oligomer are shown in Table 2. Polymerization was carried out in the same manner as in Example 6 except that 1.46 kg of p-t-butylphenol (which will be hereinafter referred to as "PTBP") was used in place of 1.44 kg of A1. Physical properties of the product are shown in Table 2. Ex. & Comp. Ex. No. Ex. 6 Comp. Ex. 2 Divalent phenol BPA BPA Molecular weight modifier (% by mole) A1 PTBP 30.4 30.4 Mv x 10 3 6.2 6.0 IR (1740cm -1 ) occurred none According to the present process, polycarbonate resins having vinyl terminals can be produced in the same manner as in the conventional process for producing an aromatic polycarbonate resin. The present polycarbonate resins having vinyl terminals have a good stability and can be used as blend materials with other resins that cannot produce useful compositions by simple blending due to a poor compatibility or as raw materials for block copolymers, by virtue of the vinyl groups.

Claims: A polycarbonate resin whose polymer chains contain on average more than 20 to 400 structural units represented by the following general formula (1) and having terminal groups represented by the following general formula (2) bonded to the bisphenol residues of the general formula (1): wherein A represents a straight, branched or cyclic alkylidene group having 1 to 10 carbon atoms, an aryl-substituted alkylidene group, an arylene group, or -O-, -S-, -CO-, -SO- or -SO 2 -; and R 1 , R 2 , R 3 and R 4 are the same or different from one another and each represents hydrogen, halogen, an alkyl group having 1 to 6 carbon atoms or an aryl group. A process for producing a polycarbonate resin having vinyl terminals by: (a) interfacial polymerisation carried out by reacting a divalent phenol compound with phosgene in an inert organic solvent in the presence of an aqueous alkali solution, then adding a molecular weight modifier and a polymerisation catalyst to the reaction mixture, or (b) solution polymerisation carried out by dissolving a divalent phenol compound and a molecular weight modifier in pyridine or a mixture of pyridine and an inert solvent, and introducing phosgene thereto, characterised in that the molecular weight modifier is a vinylbenzoic acid represented by the following general formula (3): A process according to Claim 2, wherein polymerisation is carried out in the presence of a branching agent. A process according to Claim 3, wherein the branching agent is fluoroglycine, 2,6-dimethyl-2,4,6-tri(4-hydroxyphenyl)-heptene-3, 4,6-dimethyl-2,4,6-tri(4-hydroxyphenyl)-heptene-2, 1,3,5-tri(2-hydroxyphenyl)benzene, 1,1,1-tri(4-hydroxyphenyl)ethane, 2,6-bis(2-hydroxy-5-methylbenzyl)-4-methylphenol, α,α',α''-tri(4-hydroxyphenol)-1,3,5-tri-isopropylbenzene, isatinbisphenol, 5-chloroisatinbisphenol, 5,7-dichloroisatinbisphenol or 5-bromoisatinbisphenol. A process according to Claim 3 or Claim 4, wherein 0.01 to 3% by mole of the branching agent is used based upon the amount of the divalent phenol compound. A process according to Claim 2, wherein 100 to 10 moles of the vinylbenzoic acid is used per 100 moles of the divalent phenol compound, thereby forming polycarbonate oligomers having vinyl terminals. A process according to Claim 2, wherein 10 to 0.5 moles of the vinylbenzoic acid is used per 100 moles of the divalent phenol compound, thereby forming polycarbonate resins having vinyl terminals.

Inventors: KANAYAMA SATOSHI, KANAYAMA, SATOSHI, Kanayama, Satoshi, c/o Mitsubishi Gas
Applicants: MITSUBISHI GAS CHEMICAL CO, MITSUBISHI GAS CHEMICAL COMPANY, INC.
Application year: 1992
Main classification: C08G64
IPC codes: C08G64