Flat panel display device comprising a strontium aluminosilicate glass substrate

Abstract: The invention is concerned with flat panel display devices which use polycrystalline silicon thin film transistors, in which the substrate glasses are essentially free from alkali metal oxides and MgO and consist essentially, in mole percent, of: SiO₂ 65-75 CaO and/or BaO 0-10 Al₂O₃ 6-10 B₂O₃ 0-5 SrO 15-26 [CaO and/or BaO]+B₂O₃ 0-12

Description: Background of the Invention The present invention relates to glasses suitable as substrates in flat panel display devices. Glass has been chosen as a substrate in liquid crystal display devices for several reasons: (1) it is transparent; (2) it can withstand the chemical and physical conditions to which it is exposed during display processing; and (3) it can be manufactured at reasonable cost in thin sheets with precisely controlled dimensions. Liquid crystal displays are passive displays which are dependent upon external sources of light for illumination. They are fabricated as segmented displays or in one of two basic matrix configurations. The substrate needs of the two types differ. The first type is intrinsic matrix addressed, relying upon the threshold properties of the liquid crystal material. The second type is extrinsic matrix or active matrix addressed in which an array of diodes, metal-insulator-metal devices or thin film transistors (TFTs) supplies an electronic switch to each pixel. In both designs, however, two sheets of glass form the structure of the display. Intrinsically addressed liquid crystal displays are fabricated employing thin film deposition at temperatures of about 350°C, following by photolithographic patterning. Because of the low temperature requirements involved in the process, soda lime silicate glass having a silica barrier layer thereon to prevent migration of Na+ ions has been used extensively as substrates therefor. A higher performance version of intrinsically addressed liquid crystal displays, termed the super twisted nematic, has an added substrate requirement of extremely precise flatness. That requirement has demanded that the soda lime silicate glasses employed in the displays be polished. Alternatively, Corning Code 7059 glass, a barium boroaluminosilicate glass marketed by Corning Incorporated, Corning, New York, which is precision formed into sheet requiring no surface polishing utilizing the downdraw fusion pipe such as is described in US-A-3,338,696 and US-A-3,682,609 (Dockerty) has been employed. Extrinsically addressed liquid crystal displays can be subdivided into two categories: the first based upon metal-insulator-metal or amorphous silicon (a-Si) devices; and the second based upon polycrystalline silicon (poly-Si) devices. Devices formed from poly-Si are processed at substantially higher temperatures than those employed with a-Si thin film transistors. Those temperatures have demanded the use of glasses exhibiting higher strain points than soda lime silicate glasses and Corning Code 7059 glass to preclude thermal deformation of the sheet during processing. The lower the strain point of the glass, the greater this dimensional change. One means for correcting this problem is to anneal the glass sheet after forming; a process adding significant cost. A more economical solution to that problem is to design glasses with high strain points so the dimensional change is minimal during device processing at about 600°C. Contamination of thin film transistors by sodium migrating from the glass substrate is a major concern during processing. That problem has led to the use of a coating on the substrate glass to provide a barrier to the migration of the alkali. Therefore, the principal objective of the present invention was to devise glass compositions operable as substrates in liquid crystal display devices utilizing poly-Si thin film transistors, the glass compositions being essentially free from alkali metal oxides, being relatively inert to the chemicals used in display processing, having a strain point higher than 625°C, and, most vitally, exhibiting long term stability against devitrification when in contact with platinum metal and high temperature refractory ceramic materials utilized in the downdraw fusion pipe referred to above for precision forming thin glass sheeting. Summary of the Invention As has been indicated above, a most critical requirement which the inventive glass must satisfy is its resistance to the development of devitrification when exposed for very long periods to platinum metal and ceramic materials of high refractoriness at temperatures where the glass exhibits a viscosity of about 10 4 -10 6 poises. The drawing of glass sheet utilizing a fusion pipe does not impart the very fast quenching action of conventional pressing processes of shaping glass articles. By the very nature of the process, molten glass may remain in contact with the refractory component of the melting unit for as long as 30 days. It is very difficult to evaluate in the laboratory the tendency of a glass to devitrify under the conditions present in drawing glass sheet. As a first approximation, a "liquidus" measurement is used. In reality, however, because of the method used in the laboratory, this measurement is not a true liquidus. Thus, the measuring technique involves placing crushed glass in a platinum boat which is then introduced into a gradient furnace having a temperature spread spanning the range wherein the liquidus is thought to be located. After 24 hours the boat is removed from the furnace, allowed to cool, the glass removed from the boat, thin sections prepared from the glass, and those thin sections examined microscopically. A measurement is made of the maximum temperature at which crystals are observed. The viscosity corresponding to this "liquidus" temperature provides the first estimate as to whether a particular glass is close to acceptability. The critical viscosity for forming glass sheeting utilizing the downdraw fusion pipe process is about 1-3x10 5 poises. Accordingly, to better evaluate the devitrification proclivity of a glass for use in the process, a solid piece of the glass is heated to temperature well above the liquidus while in contact with platinum or a highly refractory ceramic material, such as alumina or zircon, depending upon the fusion pipe material most suitable for a given glass composition. Thereafter, the molten glass is cooled to a viscosity within the glass forming range and that temperature is held for seven days. The sample is thereafter visually examined for the presence of crystals. Because the inventive glasses are designed to be used in forming sheet via the downdraw fusion pipe process, the glasses will exhibit a viscosity at the liquidus temperature greater than about 1.5x10 5 poises. Corning Code 7059 glass, consisting essentially, expressed in terms of weight percent on the oxide basis, of about 25% BaO, 10% Al 2 O 3 , 15% B 2 O 3 , and 50% SiO 2 , exhibits an annealing point of 639°C, a strain point of 593°C, and a linear coefficient of thermal expansion (25°-300°C) of 46x10 -7 /°C. Because of its freedom from alkali metal oxide and its utility in forming thin glass sheet via the downdraw fusion pipe process, Corning Code 7059 glass has been used extensively as a substrate in a-Si devices. In an effort to devise glasses for use as substrates in poly-Si devices, a research program was initiated to develop glasses demonstrating higher strain points and other properties superior to Code 7059 glass, such as to render them applicable as substrates for liquid crystal displays utilizing polycrystalline silicon thin film transistors. As a result of the above research program, a series of glasses was discovered in the strontium aluminosilicate system demonstrating annealing and strain points substantially higher than those exhibited by Corning Code 7059. Thus, the glasses according to the present invention demonstrate strain points over 675°C and annealing points above 725°C and are capable of being melted at temperatures not exceeding 1600°C, and have a linear coefficient of thermal expansion over the temperature range of 25-300°C between 45-62x10 -7 /°C. They also have a liquidus temperature no higher than 1160°C and a long term stability against devitrification when in contact with platinum metal and high temperature refractory ceramic materials. The glasses are essentially free from alkali metal oxides and MgO and consist essentially, expressed in terms of mole percent on th eoxide basis, of 21-25% SrO, 7-9% Al 2 O 3 , and 67-70% SiO 2 . Maintenance of the individual components within the stated ranges is necessary to assure the development of the desired properties in the glass. For example, excess SiO 2 results in a glass which is too viscous; excess Al 2 O 3 raises the liquidus temperature too high; and excess SrO depresses the strain point to too low a value. The inclusion of minor amounts of BaO, CaO, and B 2 O 3 can be useful in improving certain of the physical properties displayed by the inventive glasses. To illustrate, up to 10% total BaO and/or CaO can act to reduce the liquidus temperature and up to 5% B 2 O 3 can be helpful in improving the meltability of the glasses. Nevertheless, the total of those and any other extraneous addition ought not to exceed about 12% to prevent a negative impact on the glass properties. The invention therefore provides a flat panel display device comprising a glass substrate utilizing polycrystalline silicon thin film transistors in which the glass is as defined above. A very vital discovery derived from the research program was the need for excluding MgO from the glass composition. Thus, it was observed that more magnesium silicate precipitated out of the glass at a higher temperature than the other alkaline earth metal silicates, thereby, in effect, leading to greatly increased crystal growth. Consequently, not only will the inventive glass composition be essentially free from alkali metal oxides to prevent the migration of alkali metal ions, but also will be essentially free from MgO; that is, no substantive amount of an alkali metal-containing material or a magnesium-containing material will be included in the batch materials. US-A-4634684 (Dumbaugh, Jr.) discloses glasses especially designed for use as substrates for flat panel display devices, those glasses consisting essentially, in mole percent, of 9-12% SrO, 9-12% Al 2 O 3 , and 77-82% SiO 2 . As is immediately evident, those glasses contain less SrO and more SiO 2 than the glasses utilized in the present invention. The glasses of the patent demonstrated annealing points of at least 850°C, thus strongly recommending their utility as substrates in displays employing poly-Si thin film transistors. Unfortunately, however, batches for those glasses required melting temperature in the vicinity of 1800°C, thereby rendering them economically unfeasible in current commercial glass melting units. Also disclosed in that specification are comparative Examples 22, 23, 25 and 26 which were melted at 1650°C which is too high. In US-A-4180618 there are described aluminosilicate glasses suitable as a substrate for thin film deposition which consist essentially in percent by weight as calculated on the glass batch on an oxide basis of 55 to 75% SiO 2 , 5-25% Al 2 O 3 and at least one alkaline earth metal oxide selected from CaO (9-15%), SrO (14-20%) and BaO (18-26%) or a mixture of such oxides wherein the total alkaline earth metal oxide content is equivalent on a molar basis to 9-15% CaO. Two respects in which the glasses differ from those of utilized according to the present invention are that thermal expansion is lower and the SrO content is lower. Hence, the glasses utilized according to the present invention are distinctive in exhibiting strain points in excess of 675°C, but yet having the capability of being melted at temperatures not exceeding about 1600°C, thereby enabling them to be melted in current commercial glass melting units. Measurements of liquidus temperatures have ranged between about 1100°-1160°C and linear coefficients of thermal expansion (25°-300°C) have ranged between about 45-62x10 -7 /°C. As indicated the glass compositions consist essentially, in mole percent, of: SiO 2 67-70 CaO and/or BaO 0-10 Al 2 O 3 7-9 B 2 O 3 0-5 SrO 21-25 [CaO and/or BaO]+B 2 O 3 0-12. Whereas it is not possible mathematically to precisely convert mole percent to weight percent, the following ranges represent approximations of the glass compositions in terms of weight percent: SiO 2 50-65 CaO and/or BaO 0-12 Al 2 O 3 8-15 B 2 O 3 0-5 SrO 22-38 [CaO and/or BaO]+B 2 O 3 0-14. Description of Preferred Embodiments Table I below lists a number of glass compositions, expressed in terms of parts by weight on the oxide basis, illustrating the compositional parameters of the present invention. Because the sum of the individual components totals or very closely approximates 100, for all practical purposes the tabulated values may be considered as reflecting weight percent. The actual batch ingredients may comprise any materials, either oxides or other compounds, which, when melted together with the other batch materials, will be converted into the desired oxide in the proper proportions. For example, SrCO 3 and CaCO 3 can provide the source of SrO and CaO, respectively. The batch ingredients were compounded, tumble mixed together thoroughly to aid in producing a homogeneous melt, and charged into platinum crucibles. After placing lids thereon, the crucibles were introduced into a furnace operating at about 1600°C and the batches melted for about 16 hours. Thereafter, the crucibles were withdrawn from the furnace, the melts poured onto steel plates to yield glass slabs having dimensions of about 30 cm x 15 cm x 1 cm, and those slabs transferred immediately to an annealer operating at about 775°C (The Examples labelled 7059, 1733, and 1724 have been inserted as comparative examples and refer to glasses commercially marketed by Corning Incorporated.) Although the above description represents a laboratory melting procedure, it must be recognized that the inventive glasses are capable of being melted and formed utilizing large scale, commercial glass melting and forming equipment. Thus, it will be recalled that the subject glasses were designed to be drawn into thin glass sheet employing the downdraw fusion pipe. Also, whereas not employed in the laboratory melts, conventional fining agents, e.g., As 2 O 3 and Sb 2 O 3 , may be included in the batches in proper amounts where deemed desirable. Table I also records measurements of several physical and chemical properties determined on the listed glasses in accordance with techniques conventional in the glass art. Hence, the annealing point (A.P), strain point (St.P) and internal liquidus temperature (Liq.) employing a platinum boat are tabulated in °C. Also reported are the linear coefficient of thermal expansion (Exp.) over the temperature range of 25°-300°C, expressed in terms of x10 -7 /°C, the density (Den.) in terms of grams/cm 3 , and the viscosity of the glass at the liquidus temperature (Vis.) in terms of poises. Finally, an evaluation of the resistance to attack by acids was determined by measuring the weight loss (W.L.) in terms of mg/cm 2 after an immersion for 24 hours in a bath of 5% by weight aqueous solution of HCl, the bath operating at a temperature of 95°C. Table II records the glass compositions in terms of mole percent. Example 6 constitutes the most preferred composition. Whereas the present invention has been described in detail utilizing the inventive glasses as substrates in liquid crystal display devices, it will be understood that they can be employed in other flat panel display devices such as electroluminescent displays and plasma displays.

Claims: A flat panel display device comprising a glass substrate utilizing polycrystalline silicon thin film transistors, wherein said glass is capable of being melted at a temperature not exceeding 1600°C, exhibits a strain point over 675°C, a linear coefficient of thermal expansion over the temperature range of 25-300°C between 45-62x10 -7 /°C, a liquidus temperature no higher than 1160°C, a long term stability against devitrification when in contact with platinum metal and high temperature refractory ceramic materials, and, being essentially free from alkali metal oxides and MgO, consists essentially, expressed in terms of mole percent on the oxide basis, of SiO 2 67-70 CaO and/or BaO 0-10 Al 2 O 3 7-9 B 2 O 3 0-5 SrO 21-25 [CaO and/or BaO] +B 2 O 3 0-12.

Inventors: DUMBAUGH JR WILLIAM HENRY, LAPP JOSEF CHAUNCEY, DUMBAUGH JR., WILLIAM HENRY, LAPP, JOSEF CHAUNCEY
Applicants: CORNING INC, CORNING INCORPORATED
Application year: 1992
Main classification: C03C3
IPC codes: C03C3, G02F1, H01L29, G09F9