Resorbable fixation device with controlled stiffness for treating bodily material in vivo and introducer therefor

Abstract: The resorbable fixation device is useful for treating torn bodily material in vivo. It has a tip (1), a head (2), and a cylindrically shaped shaft portion (3) lying between said tip (1) and said head (2). The shaft portion (3) has at least one retention element (4) protruding radially therefrom to facilitate insertion of said shaft portion (3) longitudinally into said bodily material in a forward axial direction extending from said tip (1) to said head (2) and to restrict movement of said shaft portion (3) through said bodily material in a backward axial direction opposite to said forward direction. The shaft portion (3) has further a hollow body (9) with at least one radial opening (5) extending transversely through the walls (6) surrounding said hollow body (9) and rendering said shaft (3) radially elastic. The walls (6) surrounding said hollow body (9) are provided with at least one stiffening element (7) providing a controlled stiffness to the fixation device.

Description: This invention relates to a resorbable fixation device for treating torn bodily material in vivo according to the preamble of claim 1 and an introducer for implanting the device according to the preamble of claim 15. Internal fixation of facial bones is usually performed using various types of metallic dynamic compression plates, mini-plates and adequate screws. Although metallic implants give satisfactory fixation and good fracture healing, it is recommended to remove them after the fracture healing is completed. This is basically due to potential corrosion of the implants, bone resorption under the implant and possible inflammatory response to the implant. The use of resorbable implants with adequate mechanical properties and rate of resorption might allow to overcome these problems. Traumatic injury and/or heavy load applied to the knee may result in torn menisci. The early methods of treatment of the torn menisci involved partial or total meniscectomy. The long term results of the latter technique proved to be disappointing, and often led to osteoarthritis and instability of the knee. The new techniques of menisci lesions repair involve meniscus suturing using arthrotomy and arthroscopy. An arthrotomy is quite traumatic, as it requires large incision to gain access to the joint. An arthroscopy allowing guiding the suture under arthroscopic visualization is less traumatic, although it also requires incision which is larger than the standard one used in arthroscopy. From US 4,884,572 BAYS ET AL. a fixation device is known for repairing torn cartilaginous or other bodily tissue, particularly torn meniscus tissue during arthroscopic surgery. This known repair device in the form of a tack has a shaft portion with radially projecting barb members and a longitudinal bore. It is made from resorbable or biodegradable material as polyhydroxyacids, polydioxanone, polyesteramides, polycaprolactone, copolyoxaltes, polycarbonates or poly (glutamic-co-leucine). These materials have a Young's modulus of 3 to 15 GPa, a tensile strenght of 80 - 2000 MPa, a polydispersity of 1.5 to 4.2 and a degradation rate of 1 month to 5 years. This known device of conventional design seems to improve the torn meniscus treatment technique because it requires only a small incision. From US 3,848,080 SCHMIDT a metallic non-resorbable wire clip for the attachment of wires to wooden poles is known. From US 3,350,976 TOPF a one piece plastic expansion fastener is known having two distinct legs. It defines two combined elements, an inner and an outer one, which are movable with respect to each other axially. The fastener is split at its tip in order to allow a relative displacement of the two legs upon insertion into a hole thereby producing fixation within the hole. The split tip renders insertion rather difficult because the split fastener tends to bend. Furthermore due to the split construction the stiffness of this fastener is very poor. It is further known to use resorbable pins (marketed under the trademarks ORTHOSORB, ETHIPIN and BIOFIX) for the fixation of small fragments, treatment of fractures of the ankle, talus, patella, condylar fractures of the femur, fractures of the metacarpals and phalanges of the hand, condylar fractures of the humerus, a.s.o. These known pins have a circular cross-section and a smooth surface. The latter may give rise to pin loosening due to the slippage of the smooth surface through the bone hole. In addition, in their present design and sizes, they are available only with one stiffness. The invention as claimed is intended to remedy these drawbacks. It solves the problem of how to design a resorbable fixation device with a controlled stiffness for treating torn bodily material in vivo. The invention solves the problem with a device comprising the features of claim 1 and an introducer comprising the features of claim 15. In a preferred embodiment of the fixation device according to the invention its stiffening elements are arranged along the inner side of the walls surrounding its hollow body and protrude therein. The number and geometrical shape of the stiffening elements can be varied over a great range. The resulting overall stiffness of the fixation device can be varied, by varying the number of stiffening elements and their shape, and this can be adjusted to a particular application. For fixation devices with stiffening elements of the same thickness or diameter, increasing the number of stiffening elements being located within the hollow body, i.e. decreasing the distance between the individual elements, increases the overall stiffness of the respective device. Fixation devices having stiffening elements with rectangular shape, or solid cross-sections have higher stiffness, than those having X-type, S-type and D-type shapes and hollow cross-sections. In a further preferred embodiment of the invention the head of the fixation device is divided by the radial opening or slit through the shaft thereby allowing lateral movement of the two lateral segments formed by the slit and rendering the device expandable. The use of the hollow body which has a radial opening or slit reduces the amount of polymer necessary for producing the implant, and thus diminishes the chance of the long -term tissue inflammation. Furthermore resorbability of the polymer material which through the opening is accessible from all sides to the bodily fluids is enhanced. The shape of the retention elements can be varied to achieve best contact between the tissue and the implant and thus, fixation stability. In a further preferred embodiment of the invention the orientation of the retention elements in the upper shaft portion adjacent to the head is reversed in the opposite direction. This design enhances fixation stability of the tissue and allows compression of the fracture fragments. The fixation device according to the invention can be used with a grip portion attached to the head or without, depending on the area of application. The grip portion allows controlled handling and inserting of the fixation device into bodily tissues with the aid of a hollow introducer allowing a releasable engagement with the fixation device. The grip portion is preferably provided with a predetermined breaking point and is finally cut or broken out, once the device is introduced in the tissue. The various features of novelty which characterize the invention are pointed out with particularity in the claims annexed to and forming part of this disclosure. For the better understanding of the invention, its operating advantages and specific objects attained by its use, reference should be had to the accompanying drawings and descriptive matter in which are illustrated and described preferred embodiments of the invention. In the drawings: Fig. 1 shows a perspective view of a fixation device according to the invention. Figs. 2 to 12 show longitudinal sections and cross-sectional views of various fixation devices according to the invention having various arrangements of stiffening elements and retention elements; Fig. 13 shows a longitudinal section of a fixation device according to the invention with a split head portion and expandable shaft segments; Fig. 14 shows a side view of a screw-actuated introducer to be used for inserting the fixation devices according to the invention; Fig. 15 shows a longitudinal section of the introducer according to Fig. 14; Fig. 16 shows a longitudinal section of a spring-actuated introducer to be used for inserting the fixation devices according to the invention with a grip portion; Fig. 17 shows a side-view of a spring-actuated introducer according to Fig. 16; and Fig. 18 shows a cross-section of the introducer to be used for inserting the fixation devices according to the invention without a grip portion. As shown in Fig. 1, the fixation device according to the invention basically consists of an elongated cylindrical body 10 with a tip 1, a head 2, and a cylindrically shaped hollow shaft portion 3 lying between said tip 1 and said head 2. The shaft portion 3 is rectangular in cross-section, but could also be circular. The length of the shaft 3 is predetermined and depends from the area of application. The shaft portion 3 has a plurality of retention elements 4 protruding radially therefrom to facilitate insertion of said shaft portion 3 longitudinally into said torn bodily material in a forward axial direction extending from said tip 1 to said head 2 and to restrict movement of said shaft portion 3 through said bodily material in a backward axial direction opposite to said forward direction. The shaft portion 3 contains a hollow body 9 with a radial opening 5 in the form of a longitudinal slit extending transversely through the walls 6 surrounding said hollow body 9. This construction of the shaft 3 with the radial opening 5 which divides it into two lateral segments 31 and 32 - connected at the tip 1 and at the head 2 - provides it with radial elasticity. Along the inner side of said walls 6 surrounding said hollow body 9 a number of stiffening elements 7, in the form of hollow tube segments, are arranged and protrude into the hollow body 9. The stiffening elements 7 are arranged in a regular pattern along the axial direction of the shaft portion 3 and are connecting the two lateral segments 31 and 32 providing a controlled stiffness of the shaft portion 3. The stiffening elements 7 can have various shapes as illustrated in Figs. 1 to 12. Instead of the hollow tube segments - as illustrated in Figs. 1, 5 6, 9 and 12 - a multitude of other stiffening elements are suitable, e.g. with rectangular shape (Fig. 10), solid cross-sections (Fig. 11), X-type structure (Fig. 7 and 8), Z-type structure (Fig.3), S-type structure (Fig. 4) or lattice structure ((Figs. 2). All embodiments according to Figs. 1 to 12 have an integral head 2 which preferably is provided with a grip portion 8 (Figs. 1 to 8 and 10 to 12). The grip portion is designed for releasable engagement by a hollow introducer as explained below, said grip portion 8 being preferably provided with a predetermined breaking or cutting point. In Fig. 13 a preferred embodiment of a fixation device is illustrated with a head 2 which is also divided by said radial opening 5 in the form of a longitudinal slit allowing lateral movement of said two lateral segments 31 and 32 around said tip 1 which connects them. In a preferred embodiment illustrated in Fig. 8 the orientation of the retention elements 4 in the upper shaft portion 3 adjacent to said head 2 is reversed in the opposite direction adjacent to the tip 1. The screw-activated introducer 20 shown in Figs 14 and 15 consists of a threaded pusher 21 engaging with the upper portion of a threaded hollow cylindrical member 22 having longitudinal cuttings 26 in the lower conical part and a load transmitting ball 23. By screwing in the pusher 21, it pushes the load transmitting ball 23 in the forward direction, which in turn pushes the lower conical part of the hollow cylindrical member 22 and opens the jaws 25 for receiving the grip portion 8 of the fixation device 10. By screwing out the pusher 21, the load transmitting ball 23 is pushed backward by the opened jaws 25, the latter clamping releasably the grip portion 8 of the fixation device 10 as represented in Fig. 15. Next the fixation device 10 can be implanted in the tissue and the grip portion 8 can be cut out. The spring-activated introducer 40 shown in Figs. 16 and 17 consists of a spring-activated pusher 41 with an annular stop 47 for a spring 44 engaging with the upper portion of a hollow cylindrical member 42 with an annular stop 48 for the spring 44 and having longitudinal cuttings 46 in the lower conical part, and a load transmitting ball 43. It uses the same principle as the screw-activated introducer 20 except that opening and closing of the jaws 45 of the introducer 40 are activated by the spring 44, and under action of the spring 44, the pusher 41 returns to its dwelling position. The spring-activated introducer 50 shown in Fig. 18 consists of a spring-activated pusher 51 with an annular stop 57 for a spring 54 engaging with the upper portion of an unslitted hollow cylindrical member 52 with an annular stop 58 for the spring 54 and with a cylindrical implant chamber 56 adapted to receive a fixation device 17 which does not have a grip portion attached to the head 2. The introducers 20, 40 and 50 allow good handling and easy implantation of the fixation devices according to the invention. The resorbable materials to be used for preparing of the fixation devices according to the invention are polymers chosen from highly purified polyhydroxyacids, polyamines, polyaminoacids, copolymers of amino acids and glutamic acid, polyorthoesters, polyanhydrides, polyamides, polydioxanone, polydioxanediones, polyesteramides, polymalic acid, polyesters of diols and oxalic and/or succinic acids, polycaprolactone, copolyoxalates, polycarbonates or poly (glutamic-co-leucine). Preferably used polyhydroxyacids comprise polycaprolactone, poly(L-lactide), poly(D-lactide), poly(L/D-lactide), poly(L/DL-lactide) polyglycolide, copolymers of lactide and glycolide of various compositions, copolymers of said lactides and/or glycolide with other polyesters, copolymers of glycolide and trimethylene carbonate, poly (glycolide-co-trimethylene carbonate), polyhydroxybutyrate, polyhydroxyvalerate, copolymers of hydroxybutyrate and hydroxyvalerate of various compositions. Further materials to be used as additives are composite systems containing resorbable polymeric matrix and resorbable glasses and ceramics based e.g. on tricalcium phosphate and/or hydroxy-apatite, admixed to the polymer before processing. The rate of resorption and the loss of mechanical properties of the fixation device according to the invention in vivo has to be adapted to allow maintenance of its functionality during the healing period. The rate of resorption can be controlled taking into account that such factors as polymer weight, crystallinity, polymer chain orientation, material purity, the presence of copolymer unit in the chain and presence of voids (porosity) will affect the rate of resorption. In general the rate of resorption increases in the presence of a material with voids, pores, impurities, copolymer units. The rate of degradation decreases with the increase of polymer molecular weight, crystallinity and chain orientation. The polymeric material must have a degradation rate in vivo in the range of 6 weeks to 24 months. Viscosity-average molecular weight of polymers to be suitable for preparation of the fixation device according to the invention should be in the range of 30'000 to 900'000 and preferably 150'000 for soft tissue implants, and preferably 300'000 to 400'000 for hard tissue implants. Concentration of the copolymer unit in the polymer should be in the range of 1 to 99 % and preferably in the range of 5 to 35 %. The polymeric material must have a polydispersity in the range of 1,2 to 100,0 and preferably is in the range of 1,5 to 3,0. The flexural strength of the fixation devices according to the invention must exceed 60 MPa and preferably exceeds 100 MPa. Its modulus of elasticity must exceed 7 MPa and preferably exceeds 10 MPa. The resorbable or degradable polymeric and/or polymeric-ceramic materials to be used for the fixation device according to the invention must have a Young's modulus in the range of 1 to 50 GPa and a tensile strength in the range of 0,1 to 20,0 GPa. The Young's modulus should preferably be in the range of 5 to 15 GPa, most preferably in the range of 7 to 10 GPa. The tensile strength should preferably be in the range of 0,5 to 3,0 GPa, most preferably in the range of 0,7 to 2,5 GPa. The polymeric material should preferably have a at least partially oriented structure. Resorbable fixation devices according to the invention can be produced using standard techniques of polymer processing, mainly by injection-moulding, compression-moulding and in-mould polymerization. Typical absolute dimensions of the fixation device according to the invention, e.g. for maxillofacial surgery are: length 6 to 8 mm; diameter 1,8 to 2,5 mm. Dimensions of fixation devices for treatment of small fragments and/or osteochondral defects are: length 20 to 40 mm; diameter 1,5 to 4,0 mm.

Claims: A resorbable fixation device for treating torn bodily material in vivo having a tip (1), a head (2), and a hollow cylindrically shaped shaft portion (3) lying between said tip (1) and said head (2), said shaft portion (3) having at least one retention element (4) protruding radially therefrom to facilitate insertion of said shaft portion (3) longitudinally into said bodily material in a forward axial direction extending from said tip (1) to said head (2) and to restrict movement of said shaft portion (3) through said bodily material in a backward axial direction opposite to said forward direction, and wherein A) said shaft portion (3) has a hollow body (9) with at least one radial opening (5) extending transversely through the walls (6) surrounding said hollow body (9) and rendering said shaft (3) radially elastic; B) said walls (6) are provided with at least one stiffening element (7) arranged along the inner side of said walls (6) surrounding said hollow body (9) and protruding therein; C) said radial opening (5) is in the form of a longitudinal slit dividing said shaft (3) into two lateral segments (31,32) connected at least at said tip (1); D) the flexural strength of the fixation device exceeds 60 MPa; E) the modulus of elasticity of the fixation device exceeds 7 MPa; F) it comprises resorbable or degradable polymeric and/or polymeric-ceramic material, having a Young's modulus in the range of 1 to 50 GPa; and a tensile strength in the range of 0,1 to 20,0 GPa; G) said polymeric material has a polydispersity in the range of 1,2 to 100,0; H) said polymeric material comprises highly purified polyhydroxyacids, polyamines, polyaminoacids, copolymers of amino acids and glutamic acid, polyorthoesters, polyanhydrides, polyamides, polydioxanone, polydioxanediones, polyesteramides, polymalic acid, polyesters of diols and oxalic and/or succinic acids, polycaprolactone, copolyoxalates, polycarbonates or poly(glutamic-co-leucine); and I) said polymeric material has a degradation rate in vivo in the range of 6 weeks to 24 months. Device according to claim 1, characterised in that a plurality of said stiffening elements (7) is arranged, preferably in a regular pattern, in said axial direction. Device according to claim 1 or 2, characterised in that said stiffening elements (7) are connecting said two lateral segments (31,32). Device according to one of the claims 1 - 3, characterised in that said head (2) is also divided by said radial opening (5) in the form of a longitudinal slit allowing lateral movement of said two lateral segments (31,32) around said tip (1) which connects them. Device according to one of the claims 1 - 4, characterized in that its flexural strength exceeds 100 MPa. Device according to one of the claims 1 - 5, characterized in that its modulus of elasticity exceeds 10 MPa. Device according to one of the claims 1 - 6, wherein said Young's modulus is in the range of 5 to 15 GPa, preferably in the range of 7 to 10 GPa. Device according to one of the claims 1 - 6, wherein said tensile strength is in the range of 0,5 to 3,0 GPa, preferably in the range of 0,7 to 2,5 GPa. Device according to one of the claims 1 - 8, wherein at least 90 weight percent of said polymeric material has a molecular weight in the range of 30'000 to 900'000, preferably in the range of 200'000 to 350'000. Device according to one of the claims 1 - 9, wherein said polymeric material has a polydispersity in the range of 1,5 to 3,0. Device according to on of the claims 1 - 10, wherein said polyhydroxyacids comprise poly (L-lactide), poly(D-lactide), poly(L/D-lactide), poly(L/DL-lactide) polyglycolide, copolymers of lactide and glycolide, poly(DL-lactide-co-glycolide), poly(DL-lactide-co-caprolactone), copolymers of glycolide and trimethylene carbonate, poly(glycolide-co-trimethylene carbonate), polyhydroxybutyrate, polyhydroxyvalerate, copolymers of hydroxybutyrate and hydroxyvalerate. Device according to one of the claims 1 - 11, wherein the polymeric material has a at least partially oriented structure. Device according to one of the claims 1 - 12, characterized in that said head (2) is designed as a grip portion (8) for releasable engagement by a hollow introducer, said grip portion (8) being preferably provided with a predetermined breaking or cutting point. Device according to claim 12, characterised in that orientation of said retention elements (4) in the upper shaft portion (3) adjacent to said head (2) is reversed in the opposite direction adjacent to the tip (1). Introducer for implanting a resorbable fixation device according to one of the claims 1 - 14, characterized in that it has an elongated cylindrical shape with a grip portion and that it comprises a threaded pusher (21) engaging with the upper portion of a threaded hollow cylindrical member (22) having longitudinal cuttings (26) in the lower conical part and a load transmitting ball (23) which by screwing forward the pusher (21) presses the lower conical part of the hollow cylindrical member (22) and opens the jaws (25) for receiving the grip portion (8) of the fixation device (10) and by screwing backward the pusher (21) is pushed backward by the opened jaws (25), the latter clamping releasably the grip portion (8) of the fixation device (10). Introducer according to claim 15, characterized in that it further comprises a spring-activated pusher (41) with an annular stop (47) for a spring (44) engaging with the upper portion of a hollow cylindrical member (42) with an annular stop (48) for the spring (44) and having longitudinal cuttings (46) in the lower conical part and a load transmitting ball (43) which by pushing forward the pusher (41) against the force of the spring (44) presses the lower conical part of the hollow cylindrical member (42) and opens the jaws (45) for receiving the grip portion (8) of the fixation device (10) and by releasing backward the pusher (41) is pushed backward by the opened jaws (45), the latter clamping releasably the grip portion (8) of the fixation device (10). Introducer according to claim 15 or 16, characterized in that it further comprises a spring-activated pusher (51) with an annular stop (57) for a spring (54) engaging with the upper portion of an unslitted hollow cylindrical member (52) with an annular stop (58) for the spring (54) and with a cylindrical implant chamber (57) adapted to receive a full fixation device (17) without grip portion.

Inventors: GOGOLEWSKI SYLWESTER, PERREN STEPHAN, GOGOLEWSKI, SYLWESTER, PERREN, STEPHAN
Applicants: SYNTHES AG, SYNTHES AG, CHUR
Application year: 1992
Main classification: A61B17
IPC codes: A61B17, A61L31