Method and apparatus for sputtering superconducting thin films of niobium on quarter-wave resonant cavities of copper for accelerating heavy ions

Abstract: A method of providing a thin film for lining quarter-wave resonant cavities of copper comprises the deposition of a superconducting material, in particular niobium, in the form of a micro-layer having a substantially constant thickness covering both the cylindrical surface of the cavity and its bottom formed of a plane plate, by biased-diode d.c. sputtering through emitting cathodes in a form fitting geometrically the surfaces to be lined.

Description: The present invention relates to the accelerating cavities for heavy ions and, more particularly, a method and an apparatus for making the accelerating cavities superconductive at radiofrequency. The application of the superconductivity to the accelerating cavities at radiofrequency allows beams of particles or heavy ions to be accelerated to otherwise unpredictable energy levels with a low power consumption. Niobium is the superconducting material which allows the greatest quality factor and the highest accelerating fields to be reached in an accelerating cavity due to its high critical temperature T c as well as the high critical field, the low resistivity under normal conditions, and the slow tendency to surface oxidation. The use of niobium as superconducting material, however, involves a very sophisticated construction technology of the cavities since the superconduction property of niobium is strongly affected by impurities even of little concentration. That is the reason why the cavities of copper are preferably made superconductive by electrodeposition of lead (electroplating), which has, however, a reduced efficiency since the radiofrequency loss is proportional to the exponential of the ratio -T c /T, and T c of niobium is 9.25°K, while T c of lead is 7.2°K. Moreover, as far as the accelerating fields is concerned, the fields provided by niobium are higher than those provided by lead: the critical magnetic field H c of lead is 800 gauss at 0°K and that of niobium is 2000 gauss at 0°K. At the present state of art cavities for heavy ions and in particular quarter-wave cavities or resonators (QWR) of niobium are provided only by electron-beam soldering of rolled sheets of niobium or composite sheets of copper and niobium (c.f. e.g. Proceedings of the Particle Accelerator Conference, San Francisco, May 6-9, 1991, vol. 2 of 5, 6. May 1991, pages 1023-1025) provided by explosion. The results at radiofrequency confirm the absolute superiority of niobium over lead but are heavily conditioned by high cost and the number of electron-beam solderings which causes, when the latter is high, residual radiofrequency loss and makes the mechanical construction process more complex. The invention seeks to avoid the above-mentioned troubles by providing a method and an apparatus for lining the copper quarter-wave cavities with niobium at low cost and for optimizing the performance of the cavities at radiofrequency. This is achieved by the method as defined in claim 1, i.e. by biased-diode d.c. sputtering of a thin film of niobium to the inner surface of the copper resonator and by an apparatus as defined in claim 12. The sputtering of niobium on copper accelerating cavities for electrons is a widely proven technology: niobium cavities provided by sputtering have quite higher efficiency than the corresponding niobium bulk cavities. Such technique, however, has never been applied to accelerating cavities for heavy ions, as the latter have a quite more complex geometry than accelerating cavities for electrons. That is why a less sophisticated technology, such as that of lead electrodeposited on copper mentioned above, is generally accepted for the quarter-wave cavities or resonator (QWR) at the cost of higher power loss, lower accelerating fields at least by a factor of 2, and a surface more inclined to be oxidized and then to be less stable. According to the present invention the technique of depositing superconducting films of niobium by biased-diode d.c. sputtering is extended to quarter-wave resonators of copper for heavy ions by resorting to a number of expedients which satisfactorily solve all of the problems involved by such technology and concerning both the preliminary treatment of the inner surface of the cavity to be lined and the use of special equipment which allows the sputtering of niobium to the bottom plate of the cavity and in the whole cavity to be carried out by different cathodic arrangements applying the same process and assuring an uniform thickness of the deposited film. In order to guarantee such results, according to the invention, a cathode having an axial symmetry is used for the sputtering within the resonator, while a plane cathode is used for the bottom plate. In both cases, the geometry of the cathode fits that of the target. In a preferred embodiment the axial symmetry cathode is only a cylindrical tube having a thickness of about 2 mm. It should be noted that the diameter of such tube plays an important role for improving the uniformity of the thickness of the deposited film: a thickness uniformity of the order of 15% is provided if the diameter of the cathode is the arithmetical mean of the outer and inner diameters of the coaxial line of the quarter-wave resonant cavity on which the film is to be deposited. Another advantage of the selected arrangements is surprisingly based upon the fact that the lines of the electric field at the upper edge of the cylindrical cathode converge and are quite concentrated so that the upper surface of the resonant cavity can be lined without resorting to auxiliary devices. To this end the cylindrical cathode should preferably be axially located so that its upper edge is at the same distance from the upper surface as the radial distance between cathode and side surface of the cavity. Another problem to be solved for using the sputtering technique in QWR consists in suppressing the electronic bombardment due to the plasma at the end of the central shaft of the resonant cavity. The concentration of electrons in this region causes an excessive local heating with the consequence of a film peeling due to the different thermal expansion coefficients of copper and niobium after the cooling of the cavity to the room temperature. Such problem is solved according to the invention by inserting a steel stem at a suitable distance from the end of the central shaft, said stem being grounded and acting as collector of electrons, thus protecting the film which runs the risk of being peeled during the sputtering. It is noted that in this case the best results are achieved when the distance between the stem and the end of the central shaft corresponds to the radial distance between the cathode and the side surface of the cavity. Another problem to be solved is the deposition of the film also in the holes of the beam transit gates. Such problem is solved according to the invention by using a cylindrical magnetron of little diameter and by sputtering the surfaces concerned separately from the cavity. Alternatively, a plasma is formed at the portion of the cathode facing the hole which is to be lined by a thermal electron emitter, for instance a thin niobium filament brought to high temperature. Another alternative is of maintaining the continuity of the plasma also in front of the hole by using a thin grid still preferably of niobium placed before said hole and grounded. In both alternatives the localized deposition of niobium may advantageously be made at the same time as in the whole cavity. A particular attention has to be paid for avoiding that impurities of even little concentrations are captured by the film of niobium during its growth. As already mentioned, the presence of a little amount of impurities strongly reduces both the critical temperature and the resistivity ratio of niobium (the resistivity ratio is the ratio between the resistivity at 300°K and the resistivity at 10°K and generally corresponds to the purity degree of niobium). In order to solve such problem, the method of the present invention provides a bottom plate flanged to an annular substrate so as to increase the surface to be lined, and a cathode dimensioned so as to fit a wider target. In this way the impurities which can sidewise diffuse between cathode and anode are got by the film of niobium due to the optimum getter property of the latter and do not reach the surface which will be exposed to the radiofrequency. In case of cavity sputtering, the getter property of the film is utilized by flanging all of the holes of the cavity and by extending the latter with a body of the same diameter which will get in such case any impurity which can diffuse through the open bottom of the cavity. A further feature of the invention consists in that the used cathodes do not need any cooling since insulators of alumina or boron nitride have been resorted to having low degassing rates even at high temperatures under considerable cleaning conditions. Moreover a power supply is used having a protection circuit capable to discontinue the supply of power whenever an arc occurs. Thus it is assured that any arc does not impair the growth of the film. The cathode configuration is considerably simplified by the lack of cooling. Further features and advantages of the present invention will be more readily apparent from the following description with reference to the accompanying drawings which illustrate a preferred embodiment of the invention by way of a non-limitative example. In the drawings: Fig. 1 is a longitudinal section of a quarter-wave resonant cavity for accelerating heavy ions; Fig. 2 shows schematically the plane cathode for sputtering the bottom of the resonant cavity; Fig. 3 is a longitudinal section of a quarter-wave resonant cavity with a cylindrical sputtering cathode; Fig. 4 is a diagram of the sputtering apparatus; Figs. 5 and 6 show two alternative embodiments for sputtering the holes of the beam transit gates by using a thermal emitter and a thin grid, respectively; Fig. 7 is a diagram of the critical superconductivity transition temperature sampled by inserting sheets of quartz or copper into corresponding points within the cavity of Fig.1. Fig. 8 shows a resonant cavity as in Fig. 1 having regions without plasma caused by an argon pressure lower than the cut-off pressure; Fig. 9 shows connecting corners between short circuit plate and coaxial line having large bending radius; Fig. 10 is a diagram of Q-factor as a function of the accelerating field for the best cavity of sputtered niobium in comparison with the best cavity of lead electrodeposited on copper. With reference to the figures, the quarter-wave resonant cavity or resonator consists of a hollow cylindrical body 20 with a hollow central shaft 21 extending from the upper base. Body 20 is closed at the lower side by a bottom plate 22. The method according to the invention provides the use of two different cathodes for lining both the surface having axial symmetry and the bottom plate having plane symmetry and closing the resonator by a superconducting film of high-purity niobium. The cathode for sputtering inside the resonator has an axial symmetry, for example a cylindrical tube 23 shown in Fig. 3 also showing steel stem 25 acting as collector of electrons which would otherwise damage the film at the end of shaft 21. Cathode 24 for the bottom plate is plane as shown in Fig. 2, and the copper substrate is facing the overlying target in order to prevent dust or flakes of niobium from precipitating onto the surface. Starting cathode 24 is a disc of high-purity niobium (RRR 200, Residual Resistivity Ratio = R 300°K /R 10°K ) with a larger diameter than the bottom plate 22 which has to be lined and is flanged to the annular substrate 35. Cathode 24 is supported by an insulating plug 28 of boron nitride, the lower end of which is fitted in a through hole of a grounded screen 26 preferably of aluminum spaced at a distance of 5 mm from cathode 24. Cable 30 for supplying the cathode is accurately shielded by a steel bellow 32 and insulators 34 of boron nitride or alumina. Figs. 5 and 6 show two possible alternatives for sputtering the holes of the transit gates in the same phase as the whole cavity. In Fig. 5 a thermal emitter of electrons formed of a thin niobium filament 29, which is brought to high temperature by a power supply A, is inserted into the hole of the transit gate 27. In Fig. 6 a thin grid 31 of niobium connected to ground is placed before the hole of the gate facing cathode 23. As already mentioned, the copper surface to be treated should be free from impurities and foreign matters; therefore, it is necessary that the copper cavity is subjected to a hard cleaning treatment before the sputtering. To this purpose one or more per se known methods such as tumbling, electrochemical cleaning, and chemical cleaning can be used. By way of example, a suitable treatment consists of a first tumbling phase followed by a chemical cleaning and then by the introduction of the resonator into an ultrahigh vacuum chamber followed by a hard vacuum degassing phase at 300°C. In Fig. 4 the apparatus for carrying out the method according to the invention is schematically shown. It includes a vacuum desk 40 with a cylindrical support 42 on which the quarter-wave cavity 20 suitably flanged to extension 36 is placed. Insulators 44 are disposed between supports 42 and extension 36. Stem 25 is located on vacuum desk 40 along the axis of cavity 20. The whole assembly is enclosed in an ultrahigh vacuum bell 48. Alternatively, in case of an industrial production, the same resonant cavity can be used as vacuum chamber by flanging it directly through extension 36 to the vacuum pumping system. Fig. 7 shows the map of the critical superconductivity transition temperature (T c ) within the cavity. As it is apparent from said map, all of the values sensed in the indicated zones are greater or equal to the value of the niobium bulk (T c = 9.25°K). The technique of d.c. biased diode sputtering applied to the very particular geometry of the quarter-wave resonator (QWR) allows quarter-wave resonator cavities of niobium deposited on copper to be provided. Such cavities have a number of advantages, among which there are: a) the reduced cost which is much lower than niobium bulk and exploded niobium bonded to copper cavities; b) thermal stability of the composite system formed of a centimeter copper bonded to a few micron niobium; c) easy regeneration of a damaged cavity due to the short time needed for stripping a film to be replaced and sputtering a new niobium film. The present invention illustrates the setup techniques for manufacturing a copper cavity sputtered by niobium. During some researches and in particular during the sample examination tests it has been noted that the final radiofrequency results (Q-factor and accelerating field) depend on some technical factors which impair the quality of the results if they are neglected, and namely: 1) The sputtering should be as steady as possible. Since plasma is not stabilized by a magnetic field and niobium target is not cooled during the deposition, arcs or parasitic discharges may occur. Any current spikes damage either the cathode or niobium film, thus impairing locally both the adhesion to the substrate and the superconducting property. The suppression of any spikes may be possible a) by carefully cleaning the surfaces of the target and the substrate, b) by using a low ripple power supply, and c) by using an ultrahigh vacuum electrical insulating sleeve having the characteristic that the portion under potential is as little as possible. In fact one problem of the d.c. biased diode sputtering is that plasma contacts any surface under potential, and then the insulating sleeve too, as plasma is not restricted by magnetic fields. 2) There is a cut-off level for argon operating pressure. In fact, if the pressure is below such level, the plasma in the cavity is not continuous, i.e. there is an annular region within the cathode about the central shaft at more or less half his length, in which there is no plasma (Fig. 8). Of course the thickness of the film in such region is much lower than elsewhere, and also the superconducting characteristics are very bad. By increasing the pressure of argon above cut-off level, the hole in the plasma is progressively closed until the standard sputtering conditions are reached. Of course the cut-off pressure depends on the geometry of the sputtering system and above all on the distance between the inner surface of the target and the central shaft of the cavity (the lower the target diameter is, the higher the operating pressure should be to suppress the hole in the plasma). For such reason the cut-off pressure has to be determined everytime through the examination of the samples introduced into the cavity. During the present research it has been noted that the argon pressure of 0,2 mbar is high enough to allow the deposition to be carried out without falling into such problem. 3) The bending radius of the corners between the two coaxial conductors and the short circuit plate within the copper cavity impairs considerably the final radiofrequency results in the sputtered quarter-wave resonator more than any other factor. The cathode configuration provided by the present invention is optimized so as to operate with corners as rounded as possible (Fig. 9). A copper cavity having a few millimeter bending radius of the corners will always provide an uneven thickness of niobium deposition. The film is less thick at the corners. As the deposition rate at the corners is extremely lower than elsewhere the film in such region is also less pure. In addition, the high density of film impurities at the corners is promoted by the fact that the sharper the corners are, the lesser the bias is active at such corners. According to the cathode configuration and the size of the resonator, and on the base of experimental tests, corners having a 20 mm bending radius do not give any big problem. A 30 mm bending radius provides the best evenness as well as optimum superconducting characteristics of the deposited film (of course a 30 mm bending radius corresponds to the maximum which can be provided in a cavity as the inner shaft has a diameter of 60 mm and the outer cylinder has an inner diameter of 180 mm). Corners having a smaller bending radius, for example 10 mm, are quite critical as the thickness of the film is very thin; moreover two opaque rings appear at the corner connecting the central shaft as well as at the corner connecting the outer cylinder where the film has a brown, not reflecting colour. RRR value is there about 2, then too low if a Q-factor higher than 2x10 8 and an accelerating field higher than 3 MV/m should be reached (such values are obtained in cavities made by depositing lead on copper). Repeated tests have proved that the presence of such rings considerably impairs the efficiency of sputtered Nb/Cu cavities. Niobium film in such impaired regions analyzed by electron microscope has a column structure with grains of a few tens micron size separated from one another by grain boundaries about one micron large. The brown colour of such film portion may be due to the size of the grain boundaries. The ten µm (micron) size of niobium grains is due to the high temperature reached by the substrate at the end of the deposition process. As the cathode is not cooled and the sputtering is carried out under a "closed configuration", i.e. with substrate embracing about completely the cathode, the temperature of the cavity increases considerably during the deposition. Therefore, starting from a substrate temperature of 300°C the film thickness is limited by the fact that the deposition temperature does not exceed 800°C. Though the superconducting characteristics of the film improves with the increase of the substrate temperature, if the latter is too high there is the risk of a copper diffusion from the substrate through the grain boundaries. The presence of copper between niobium grains within the coherence distance from the surface causes residual radiofrequency losses (not depending on the temperature). Satisfactory results have also been achieved in cavities having a bending radius of 10 mm by a two-step deposition. Before the normal deposition, which is carried out according to the above-described criteria, the short circuit plate of the cavity as well as the connecting corners are covered by niobium sputtered from a niobium disc placed perpendicularly and coaxially to the cavity axis. The temperature of the cavity during the first run does not exceed 400°C. The first niobium layer probably acts as a diffusion barrier to the copper diffusion or to the doping of the film by oxygen or hydrocarbons contained in the copper. 4) A further improvement of RF results can be provided by pre-sputtering the cathode. In fact, the temperature of niobium target certainly exceeds thousand degrees just after sputtering. As soon as the discharge is put out, the target begins to cool. During this step the target will eject any impurity from the chamber. In the same way the impurities are absorbed at the surface of the target whenever the latter is exposed to the atmosphere. There are two possible solutions: a) target is pre-sputtered by a moving cathode system in an extension flanged to the cavity, target is then introduced into the cavity where the film deposition takes place; b) instead of 1 µm (micron) niobium a much thicker layer is deposited so that the surface of the film is as pure as possible. 5) Regarding the beam port problem, the methods outlined above are adapted to cover all of the length of the beam port interior. Of course the Rf fields are attenuated in the beam ports so as to be zero at their ends. Obviously the whole length of any beam port does not need to be perfectly superconductive since the length of the beam ports is overestimated. In such a case a further solution is needed to cover also the interior of the beam ports with niobium. Such solution, which is the easiest solution according to the invention, is based upon two considerations: there is a hole in the plasma just before the beam port. Such hole becomes more and more narrow and tends to be cancelled a) with increasing pressure, b) with increasing distance between cathode and wall port. It may then be possible to deposit the niobium film even in the interior of the beam ports by operating at high argon pressure (range 10 -1 mbar) and narrowing the target near the beam ports by keeping the diameter of the target and by increasing the distance between target and beam port. Of course such technique means that the cavities to be sputtered have all the same dimensions. 6) The researches have been carried out with the cavity placed within an ultrahigh vacuum system. This means that the provision of vacuum levels necessary for sputtering niobium is not trivial, besides it requires a long baking time. Therefore the cavity can be directly flanged to the vacuum pump, thus reducing the volume to be pumped and the dagassing surfaces. 7) Even if not directly detected by the present invention there are good evidences that the best results can be achieved through a composite sputtering technique consisting of biased diode plus magnetron. Higher deposition rates and a greater stability of the sputtering parameters could be provided by assisting the biased-diode discharge with an outer magnetic field. All of the above technical factors have provided a cavity with a low-field Qo of 7e+08 and an accelerating field of 4 MV/m. As a comparison, the best lead cavity produced by the National Laboratories of Legnaro has a maximum Qo of 3e+08 (Fig. 10). Notwithstanding this, since a better result is everytime achieved after a radiofrequency test, such results are considered more and more interesting. The present invention has been illustrated and described with reference to a preferred embodiment thereof but it should be understood that modifications can be made by those skilled in the art without departing from the scope of the present industrial invention.

Claims: A method of depositing a film of superconducting material, in particular niobium, on a copper support formed of a quarter-wave resonant cavity for the acceleration of heavy ions, characterized by the following steps: carrying out the hard cleaning of the copper surfaces to be lined; introducing said surfaces into an ultrahigh vacuum chamber; and biased-diode d.c. sputter depositing a niobium film by means of one or more niobium emitting cathodes shaped so as to fit the geometry of the target. The method of claim 1, characterized in that said one or more emitting cathodes have axial symmetry and are formed of a cylindrical tube coaxially placed within the resonant cavity and having a thickness of about 2 mm. The method of claims 1 and 2, characterized in that the diameter of said one or more cathodes is substantially equal to the arithmetical mean of the outer and inner diameters of the coaxial line of the quarter-wave resonant cavity on which the film is deposited. The method of claims 1 to 3, characterized in that a plane cathode is provided for lining the bottom plate of the resonant cavity, and that said bottom plate is mounted on an annular substrate so as to increase the surface to be lined and to cause the peripheral area of the niobium film to get any impurities. The method of claims 1 to 4, characterized in that the film of niobium is also deposited in the holes of the beam transit gates through a thin cylindrical magnetron of little diameter for the sputtering of said holes independent of the sputtering of the cavity. The method of claims 1 to 5, characterized in that the step of lining the transit gates is alternatively carried out either by a thin filament for the thermal emission of electrons or by a grid, both made of niobium. The method of claims 1 to 6, characterized in that a grounded steel stem collecting electrons is located along the axis of the resonant cavity at a distance from the end of the central shaft in order to protect the portions of the film running the risk of excessive heating due to the electron concentration during the sputtering so as to prevent those portions from being excessively heated with the consequence of a film peeling. The method of claims 1 to 7, characterized in that the distance between the steel stem and the end of the central shaft is generally equal to the radial distance between the cylindrical cathode and the side surface of the resonant cavity. The method of claims 1 to 8, characterized in that in the cavity sputtering step the getter property of the film is used by flanging all of the holes of the cavity and by mounting the latter on an extension with the same diameter having the function of getting impurities entering the open base of the cavity. The method of claims 1 to 9, characterized in that the lining of the upper plate of the cavity is carried out by said cylindrical tube making use of the convergence of the lines of the electric field at the edge of said cylindrical tube. The method of claims 1 to 9, characterized in that all of the sputtering steps are carried out without providing the cooling of the emitter cathode. A biased-diode d.c. sputtering apparatus comprising one or more niobium emitting cathodes for carrying out the method of claims 1 to 11, characterized by a cylindrical cathode to be coaxially mounted within the resonant cavity to be lined, a plane cathode for the sputtering of the bottom plate of said resonant cavity, an annular substrate on which said bottom plate is mounted during the sputtering thereof, a vacuum desk provided with a supporting base connected thereto through insulator means, a resonant cavity to be lined, an extension for flanging said cavity before its assembling on said supporting base, and a steel stem located on said vacuum desk along the axis of said cavity with the function of collecting electrons, the whole assembly being enclosed in a removable vacuum bell.

Inventors: PALMIERI VINCENZO, PRECISO RENATO, RUZINOV VLADIMIR L, PALMIERI, VINCENZO, PRECISO, RENATO, RUZINOV, VLADIMIR L.
Applicants: ISTITUTO NAZIONALE DI FISICA N, ISTITUTO NAZIONALE DI FISICA NUCLEARE
Application year: 1992
Main classification: C23C14
IPC codes: C23C14, H05H7, H01L39