A composite layer, a glass composite material and a method of manufacturing the same

Abstract: The composite layer according to the present invention comprises a substrate and a colored layer formed on the surface of this substrate. This colored layer contains a transparent layer and a coloring agent dispersed within the transparent layer, and this transparent layer is made of an inorganic gel or glass material, while the coloring agent contains dyes or pigments. The composite layers of the present invention are suitable for use in products such as construction materials with the appearance of marble, colored glass materials for decorative purposes, or color filters.

Description: The present invention relates to a process for preparing a color filter which can be employed for purposes such as color compensation in VTR cameras, color separation used in colored copying machines such as input colored scanners, etc., RGB color separation in liquid crystal color matrices, general photographic applications, special purposes such as UV cutoff, etc., which process is defined in claim 1, as well as a color filter itself as defined in claim 9. The coloring of glass arises from a nonuniformity in the degree to which light of the various wave lengths contained in the visible spectrum is transmitted when visible light passes through the glass. Utilizing this property, four principal methods of manufacturing colored glass have hitherto been developed and used, as follows. (a) Ions of transition metals or rare earth elements are confined within the glass, and the light of prescribed wave lengths is absorbed by electron transitions in these metal ions. (b) Minute particles of chemical elements or compounds are dispersed within the glass in colloidal form, and light is scattered and/or absorbed by these colloids. (c) Light is absorbed by color centers created by exposing the glass to radiation, etc. (d) Color is imparted by coating the surface of the glass with coating materials containing organic dyes, pigments, etc., or by vapor deposition of a metallic film. Metal ions such as titanium, vanadium, or chromium, etc., are used as a colorant in the aforesaid method (a). When this method is employed, the colors change in a complex manner owing to the changes in coordination numbers of the metal ions which are determined by the specific composition of the glass. In method (b), coloration is effected through colloid precipitation induced by heat treatment. Copper and gold are used to create red colors, while silver is used for yellow coloration. Method (c) is used for the creation of certain special colors. Method (d) is the so-called coating method, and involves no coloration arising from the composition of the glass itself. The formation of composite materials consisting of glass and synthetic resins from compositions containing, e.g., glass particles, reaction hardened synthetic resins, and flaky aluminum powder, has previously been proposed (Japanese Laid-Open Patent Publication No. 55-20222). The range of colors which can be obtained by conventional methods of coloring glass with metallic ions or metallic colloids is limited. That is, the arbitrary control of the wave length peak of the light absorbed or transmitted by the glass is difficult. Moreover, colored glass fabricated by the aforementioned coating method, based upon application of coating materials containing dyes or pigments, is subject to fading when exposed to ultraviolet radiation, heat, or moisture, etc. In the case of composite materials prepared with finely powdered glass, since the glass powder is colored with organic pigments, the weather resistance of the product with respect to ultraviolet radiation is poor. As for composite materials for color filters prepared with crushed glass colored with metallic ions or colloids, the range of color selection for such composite materials is limited. Lastly, since composite materials prepared with aluminum hydroxide powder are generally colored with organic pigments, such composite materials are subject to considerable fading. Next, the use, as color filters, of a composite layer comprising a transparent substrate and a colored layer superposed upon this substrate will be explained below. Color filters are classified in accordance with their uses, as follows; (1) Color correction filters in VTR cameras, facsimile machines, illumination meters, etc. (2) Color separation filters in liquid crystal displays, CRT displays, etc. (3) Contrast correction, color temperature conversion and neutral density filters in general photographic applications. (4) Special purpose filters for ultraviolet cutoff, etc. (5) Color filters for traffic lights and window glass. For example, with the color correction filters for a VTR camera, color corrections thereof are necessary due to the large difference between human visibility and the sensitivity of a photoelectric conversion element (solid image pick-up element). For example, color correction filters appropriate for the brightness of the scene and the color of the light source are necessary for photography. The types of filters used for color correction in recent years comprise near infrared cutoff filters, ultraviolet cutoff filters, and three color filters, i.e., red (R), green (G), and blue (B). Figures 10, 11, and 12 illustrate cross-sections of representative light receptors of conventional color sensors. The color sensor light receptor illustrated shown in Figure 10 comprises a photomask IC 20 with spacers 19 arranged on its surface, and a film filter 21 located above the photomask IC 20, with a red (R), a green (G), a blue (B) filter arrayed in a plane on the surface of the film filter for the purpose of color separation, above which are situated an ultraviolet cutoff filter 22 and a near infrared cutoff filter 23. Translucent glass or a vapor deposition film is used as the near infrared cutoff filter 23, while translucent glass or an organic film is used as the ultraviolet cutoff filter 22. The sensor light receptor illustrated in Figure 11 has, in place of the film filter 21 shown in Figure 10, a printed filter 25. On this printed filter 25, red, green, and blue colored layers 21 are formed by the printing of dyes on the surface of the translucent glass substrate 24 opposing the photomask IC 20. The light sensor receptor illustrated in Figure 12 employs, in place of the film filter shown in Figure 10 or the printed filter 25 shown in Figure 11, a glass filter 26 comprising red, green, and blue colored glass filter elements. The colored elements of this glass filter 26 do not fade upon exposure to ultraviolet rays, and therefore the above-mentioned ultraviolet cutoff filter 22 is not required in this case. Conventional color filters may be classified as follows; (1) Organic film filters, formed by dispersing a coloring dye or pigment in an organic resin film, such as a polyethylene film, etc. (2) Filters formed on a glass substrate by printing or electrodepositing and drying a mixture of gelatin or an organic resin binder, such as a polyester resin, and a coloring dye or pigment. (3) Glass filters colored by ions of transition metals such as Cuo or La 2 O 3 or rare earths, or precipitation of colloidal metals such as Au, or CdS, or colloidal compounds. (4) Vapor deposited metal filters, utilizing the light transmission characteristics of vapor deposited metals films. The various problems associated with conventional color filters are as follows; Organic film filters, printed filters, electrodeposited filters, etc., all employ organic substances as binders for dyes or pigments. Consequently, such filters are prone to fading upon exposure to ultraviolet rays. If dyes are used as a colorant, since the binder possesses no ultraviolet cutoff effect, then the dyes themselves are substantially faded by ultraviolet rays, and as a result the peak absorption wave length of the filter changes with the passage of time. In order to prevent this, the filter is covered with a substance such as crystal or quartz which can absorb ultraviolet radiation, or is placed in a vacuum to ensure long-term reliability, etc. On the other hand, in glass filters, since the glass itself is colored by metal or metal ions contained in the glass, almost no fading results from exposure to ultraviolet radiation, however, as illustrated in Figure 12, the glass filter requires a holder 28. Moreover, arbitrary control of the peak transmission wave length is more difficult compared with filters employing organic dyes or pigments. The fabrication of vapor deposited filters demands a great deal of time and labor, moreover, the range of absorption wave lengths and other optical characteristics of such filters is limited. US-A-3,421,921 discloses films on glass, which are fabricated using transparent durable titania. Organic colorants are used in connection with copper salts or other salts to prevent the titania from precipitating from the solution which provides the color for the transparent glass articles. It is disclosed that the coloring titania film would be deteriorated if the copper salt or comparable other salts to stabilize the titania film should be omitted. To prepare the colorant according to this prior art document, temperatures of more than 200°C are used. Film thicknesses of 0.02 to 0.05 µ are disclosed. According to US-A-4,421,803 pigment grains are baked to a glass sinter layer to provide a color layer. However, since a glass sinter layer includes hollow spaces between the adjoining pigment grains forming the color layer, baking temperatures of 200°C or more are disclosed. The grains have diameters from about 0.1 to 5 microns. US-A-3,087,829 discloses pigment compositions on the basis of metal oxides and according to this prior art calcination temperatures or baking temperatures of more than 300°C are used. It is the object of the present invention to provide a process for preparing a color filter which is more efficient in its filter characteristics. In addition, it is another object of the present invention to provide a corresponding color filter. The above objects are solved by a process for preparing a color filter according to claim 1 and a color filter according to claim 9. Useful variants on the process according to the present invention are defined in the subclaims. According to the present invention a process is claimed for preparing a color filter comprising a substrate and a colored layer formed on the surface of said substrate, wherein said colored layer contains the transparent layer and coloring agent dissolved or dispersed within said transparent layer, comprising the steps of preparing a colorant solution or dispersion by dissolving or dispersing the coloring agent in an alkoxide solution, wherein the coloring agent contains at least one element selected from the group consisting of dyes and pigments, and wherein the alkoxide solution contains an alkoxide of at least one element selected from the group consisting of silicon, germanium, titanium, zirconium, lead, boron, aluminium, phosphorus and arsenic; of applying said colorant solution or dispersion to the substrate; of forming the colored layer on the surface of the substrate in a thickness of 10 µm or less by heating the substrate which the colorant solution or dispersion is applied; and of heating the colored layer at temperatures from 60°C to 150°C. According to another aspect of the present invention, a color filter is provided comprising a substrate and a colored layer formed on the surface of said substrate, wherein said colored layer contains a transparent layer and a coloring agent dissolved or dispersed within said transparent layer, and has a thickness of 10 µm or less, said transparent layer being made from an alkoxide solution of at least one element selected from the group consisting of silicon, germanium, zirconium, lead, boron, aluminium, phosphorus and arsenic; and said coloring agent consists of at least one element selected from the group consisting of dyes and pigments, where the colored layer is heated on the surface of the substrate at temperatures from 60°C to 150°C. In a preferred embodiment, the substrate is made of glass or plastic material. In a preferred embodiment, the inorganic material contains at least one element selected from the group consisting of silicon, germanium, titanium, zirconium, lead, boron, aluminum, phosphorus, arsenic, magnesium, calcium, strontium, barium, lithium, sodium, potassium, sulphur, selenium, tellurium, and fluorine. In a preferred embodiment, the coloring agent is an organic dye. In a preferred embodiment, the coloring agent is an organic pigment. In a preferred embodiment, the coloring agent is formed from several kinds of dyes and/or several kinds of pigments having absorption peaks at different wave lengths. In a preferred embodiment, the transparent layer is capable of absorbing ultraviolet radiation. In a preferred embodiment, the applying and the forming are performed at least twice. In a preferred embodiment, colorant solution contains, as a film-forming auxiliary, an organic compound selected from the group consisting of hydroxypropyl cellulose and hydroxyethyl cellulose. In a preferred embodiment, the substrate forming the composite layer is made of glass. In a preferred embodiment, further comprising a process for treating the surface of the substrate with a coupling agent prior to the application of the colorant solution to the substrate. In a preferred embodiment, the colorant solution further contains a coupling agent. The color filter of the invention have a transparent substrate and a colored layer formed on the surface of the substrate, wherein the colored layer contains a transparent layer and a coloring agent dispersed within the transparent layer, the transparent layer is made of an inorganic gel or glass material, and the coloring agent contains at least one selected from the group consisting of dyes and pigments. Thus, the invention described herein makes possible the objectives of (1) Providing a composite layer so that no fading results from exposure to ultraviolet radiation, heat, or moisture (i.e., possessing excellent weather resistance); (2) Providing a composite layer permitting an extremely great freedom of selection of the wave length peak of transmitted light when organic dyes or organic pigments are used for coloration; (3) Providing a composite layer which can be fabricated with comparative ease; (4) Providing color filters possessing the various aforesaid characteristics; (5) Providing glass composite materials comprising the various aforesaid characteristics; and (6) Providing glass composite materials characterized by strong adhesion between the composite layers and synthetic resin layers. This invention may be better understood and its numerous objects and advantages will become apparent to those skilled in the art by reference to the accompanying drawings as follows: Figure 1 shows a cross-sectional view of the essential portion of one embodiment of the type of composite layer according to the present invention. Figure 2 shows a cross-sectional view of the essential portion of one embodiment of the type of glass composite material according to the present invention. Figure 3 shows an oblique view of an ornament fabricated using the type of composite layer according to the present invention. Figure 4 shows a cross-sectional view of one embodiment of the type of color filter according to the present invention. Figure 5 shows a schematic diagram of a color filter for liquid crystal display obtained in Example 9. Figure 6 shows a graph of the transmittance-wave length relationship of the color filter obtained in Example 15. Figure 7 shows an example of a spectrum luminous efficiency function and a color correction. Figure 8 shows a graph of the transmittance-wave length relationship of the color filter obtained in Example 16. Figure 9 shows a graph of the transmittance-wave length relationship of the color filter obtained in Example 16. Figure 10 shows a cross-sectional view of a color sensor light receptor fabricated using a conventional type of color filter. Figure 11 shows a cross-sectional view of a color sensor light receptor fabricated using another conventional type of color filter. Figure 12 shows a cross-sectional view of a color sensor light receptor fabricated using still another conventional type of color filter. As indicated in Figure 1, a composite layer of the present invention comprises a substrate 1 and a colored layer 4 formed on the surface of the substrate 1. When the substrate 1 assumes the form of a plate, the colored layer 4 may be formed on either one or both sides of the substrate 1. The substrate 1 may be formed from transparent glass or plastic. The colored layer 4 contains a transparent layer 2 and a coloring agent 3 dispersed within the transparent layer 2. The transparent layer 2 is composed of an inorganic gel or glass material, while the coloring agent 3 contains at least one selected from the group consisting of dyes and pigments. The colored layer is formed in the following manner. A colorant solution is prepared by dissolving or dispersing a coloring agent in an alkoxide or mercaptide solution. Next, the colorant solution is coated onto the substrate, then the substrate, coated with the colorant solution, is dried and/or heated. This drying and/or heating process results in the formation of a transparent layer of inorganic gel or glass from the alkoxide or mercaptide by a dehydration-condensation reaction If the dehydration-condensation reaction is incomplete, then a transparent layer of gel is formed, whereas if the said dehydration-condensation reaction is complete, then a transparent layer of glass is formed. The coloring agent is uniformly dispersed within the aforesaid transparent layer. Since the dehydration-condensation reaction is conducted at relative low temperature, the coloring agent is sealed into the transparent layer without decomposition. The thickness of the colored layer is 10 micrometers or less. The materials from which the transparent layer is formed may contain one or more elements selected from the group consisting of silicon, germanium, titanium, zirconium, lead, boron, aluminum, phosphorus and arsenic. The transparent layer may be formed from soda glass, borosilicate glass, lead glass, or natural quartz. Thus, the transparent layer is formed of inorganic materials, hence, weather resistance is superior to that of transparent layers formed of conventional organic materials such as alkyd resins. Moreover, since a transparent layer formed from inorganic materials can prevent the passage of ultraviolet rays, fading effects can also be diminished. The coloring agent used for the purposes of the present invention is preferably an organic dye or organic pigment. For example, organic dyes or organic pigments in the category of azo, anthraquinone, naphthoquinone, perylene, indigo, fluorenone, phenazine, phenothiazine, polymethine, polyene, diphenylmethane, triphenylmethane, acridine, phthalocyanine can be used. Examples of organic dyes or pigments suitable for the purpose of the present invention are as follows. (a) Methylene blue (b) 2-(p-dimethylaminostyryl)-3-ethylbenzooxazolium iodide (c) 3-(4'-dimethylaminophenylazo)-pyridinium chloride (d) Copper phthalocyanine (e) Phthaloperinone (f) 4, 5, 6, 7,-tetrachloroquinophthalone (g) An azo type dye (h) A mixture of Direct Blue 86 and C. I. Acid Yellow (i) A triphenylmethane dye In addition, inorganic pigments may also be used as coloring agents for this purpose. In the sequel, the present invention will be described in further detail with reference to specific examples. Example 1 0.1 g of methylene blue was dissolved in 50 ml of ethanol, 25 g of tetraethoxysilane was added to this solution, and the mixture was thoroughly agitated. Next, 23.5 g of an aqueous solution containing 0.3 ml of hydrochloric acid was added, and the mixture was stirred at room temperature for 10 minutes, thereby preparing a solution designated as A-1. Also, another solution, designated as B-1, was prepared in entirely the same manner as A-1, except for the use of 2-(p-dimethylaminostyryl)-3-ethyl-benzooxazolium iodide in place of methylene blue. Likewise, still another solution, designated as C-1, was prepared in entirely the same manner as A-1, except for the use of 3-(4'-dimethylaminophenylazo)-pyridinium chloride in place of methylene blue. Then, 200 g of crushed glass particles with a grain size of 3 mm were immersed in each of the solutions A-1, B-1, and C-1 obtained as indicated above. After drying at room temperature, the mixtures were heated for 60 minutes at 100°C, thereby forming a gel film on the surfaces of the glass particles. The colored glass particles formed using the solutions A-1, B-1, and C-1 displayed blue, red, and yellow colors, respectively. Example 2 0.2 g of copper phthalocyanine was dispersed in a mixed solution of 50 ml of ethanol and 40 g of hydroxypropyl cellulose, then this solution was added to 25 g of tetraethoxysilane and the mixture was thoroughly stirred. Next, 23.5 g of an aqueous solution containing 0.3 ml of hydrochloric acid was added, and the mixture was stirred at room temperature for 10 minutes, thereby preparing a solution designated as D-1. Also, another solution, designated as E-1, was prepared in entirely the same manner as D-1, except for the use of phthaloperinone in place of copper phthalocyanine. Likewise, still another solution, designated as F-1, was prepared in entirely the same manner as D-1, except for the use of 4, 5, 6, 7, -tetrachloroquinophthalone in place of copper phthalocyanine. Then, glass filaments of 0.3 mm diameter and 500 mm in length were coated with each of the solutions D-1, E-1, and F-1 obtained as indicated above, and heated for 60 minutes at 100°C, thereby forming a gel film on the surfaces of the glass filaments. The colored glass filaments formed using the solutions D-1, E-1, and F-1 displayed blue, red, and yellow colors, respectively. Table 1 shows the peak absorption wave length of the colored glass filements obtained by the method of the present Example 2. Figure 3 shows an example of an ornament employing the colored glass filaments obtained by the method of the present Example 2. This ornament is composed of a group (15, 16, 17) of glass filaments with three colors and a light-emitting unit 18. Pigment added Peak absorption wave length Copper phthalocyanine 660 nm Phthaloperinone 520 nm 4,5,6,7-tetrachloroquinophthalone 430 nm Example 3 The colored glass particles obtained as indicated in the description of Example 1 above were mixed with an unsaturated polyester resin in a weight ratio of 50:50, then, 2 weight parts each of a cure accelarator, a catalyst, and a low shrinkage agent were added to 100 parts of the mixture so obtained, and the mixture was thoroughly stirred. The constituents mixed in this manner were then poured into a mold, and thermally hardened for 100 minutes at 100°C. The hardened mass was then removed from the mold, and the surface of the mass was polished, thus obtaining a glass composite material. Example 4 Acetylacetone was added to an ethanol solution of titanium tetrabutoxide, then methylene blue was added, and the solution was agitated for 20 minutes. Then, to the solution so obtained were added glass particles of a mean grain size of 0.5 mm. Next, the glass particles were lifted out of the solution and heated for 5 hours at 120°C. The colored glass particles so obtained were then mixed with an unsaturated polyester resin, a silicone coupling agent, a curing averator, and a low shrinkage agent in the weight ratio 50:50:2:2:2. The constituents mixed in this manner were poured into a mold, and thermally hardened for 100 minutes at 100°C. The hardened mass was then removed from the mold, and the surface of the mass was polished, thus obtaining a glass composite material. Example 5 A composite glass material was obtained by the same procedure as was used in the preparation of Example 4, except that the solution for immersion of the glass particles was prepared with added hydroxypropyl cellulose. Example 6 Water was added to a mixed solution of tetramethoxysilane and methanol, thereby obtaining a methanol solution wherein a portion of the tetramethoxysilane had been hydrolyzed. Then, this methanol solution was mixed with a solution obtained by dissolving tetramethoxytitan in methanol, and the preparation of the solution was completed by adding 4, 5, 6, 7,-tetrachloroquinophthalone to this mixture. Next, gloss in the form of 1 mm x 10 mm flakes, after prior surface treatment with a silicone coupling agent, were immersed in the aforesaid solution, after which a glass composite material was obtained by processing the colored glass so obtained by the same procedure as that used in the fabrication of Example 5. Example 7 0.2 g of 3-(4'-dimethylaminophenylazo)-pyridinium chloride was added to 50 ml of an ethanol solution of methyltriethoxysilane, then 0.3 ml of hydrochloric acid was added to the mixture. Next, chip fiber glass was immersed for 10 minutes in the solution so obtained, then lifted out of the solution and dried at 100°C for 60 minutes. Next, this glass was surface-coated with a silicone coupling agent. Finally, a glass composite material was obtained by processing the colored glass chip fibers obtained in this manner by the same procedure as that used in the fabrication of Example 5. The principal characteristics of the layered materials and glass composite materials obtained in the Examples described above are shown in Table 2, along with two comparative examples. Comparative Example 1 is a glass bead material colored with an organic pigment, while Comparative Example 2 is an artificial marble composed of an organic pigment, glass powder, and a synthetic resin. Range of color section Mechanical strength Weather resistance Embodiment 1 Arbitrary ------ High 2 Arbitrary ------ High 3 Arbitrary High High 4 Arbitrary Extremely high High 5 Arbitrary Extremely high High 6 Arbitrary Extremely high High 7 Arbitrary Extremely high High Comparative examples 1 Limited ------ Low 2 Limited High Low Example 8 0.1 g of the azo type dye with the structure shown in diagram (a) above was dissolved in 50 ml of ethanol, then this solution was added to 25 g of tetraethoxysilane and the mixture was thoroughly stirred. Next, 23.5 g of an aqueous solution containing 0.3 ml of hydrochloric acid was added and the mixture was agitated at room temperature for 10 minutes, thereby preparing a solution designated as A-2. In addition, a solution designated as B-2 was obtained by the same procedure as was used in the preparation of solution A-2, except that a mixture of Direct Blue 86 and C. I. Acid Yellow, with the structures shown in diagram (b) above, was used in place of the dye (a) which was used in solution A-2. Furthermore, a solution designated as C-2 was obtained by the same procedure as was used in the preparation of solution A-2, except that the triphenylmethane type dye with the structure shown in diagram (c) above was used in place of the dye (a) which was used in solution A-2. Each of the solutions A-2, B-2, and C-2 so obtained were coated onto the portions (a), (b), (c), respectively, of a #7059 glass substrate 30, as illustrated in Figure 4, and after drying in air, the coated substrate was heated for 30 minutes in an electric oven, thereby forming the red, green, and blue colored films 35, 36, and 37, respectively. The thickness of the films 35, 36, and 37 so obtained was 500 nm, i.e. 0,5 µm. The filter obtained in this manner was the color separation filter 34, with the component red, green, and blue filters formed by the portions (a), (b), and (c), respectively. A color sensor receptor was constructed by assembling this color separation filter with a photomask IC 31, spacers 32, and a near infrared cut off filter 33. Example 9 Using a printing method, the solutions A-2, B-2, and C-2 obtained in Example 8 were coated onto a glass substrate 45, as illustrated in Figure 5. Then, the substrate was heated in the same manner as in the preparation of Example 8, thereby forming red, green, and blue colored films 46, 47, and 48, respectively, and so obtaining a color filter suitable for liquid crystal displays. Example 10 0.1 g of methylene blue was dissolved in 50 ml of ethanol, then this solution was added to 25 g of tetraethoxysilane and the mixture was thoroughly agitated. Next, 23.5 g of an aqueous solution containing 0.3 ml of hydrochloric acid was added, and the mixture was stirred at room temperature for 10 minutes, thereby preparing a solution designated as D-2. Also, another solution, designated as E-2, was prepared in entirely the same manner as D-2, except for the use of 2-(p-dimethylaminostyryl)-3-ethyl-benzooxazolium iodide in place of methylene blue. Likewise, still another solution, designated as F-2, was prepared in entirely the same manner as D-2, except for the use of 3-(4'-dimethylaminophenylazo)-pyridinium chloride in place of methylene blue. Then, each of the solutions D-2, E-2, and F-2 was applied to a #7059 glass substrate of thickness 0.5 mm by a dipping method, and the respective substrates were heated for 60 minutes at 100°C thereby forming a gel films. Table 3 shows the peak absorption wave lengths of the respective filters obtained in this manner. Dye added Peak absorption wave length Methylene blue 620 nm 2-(p-demethylaminostyryl)-3-ethyl-benzooxazolium iodide 500 nm 3-(4'-dimethylaminophenylazo)-pyridinium chloride 440 nm Example 11 0.2 g of copper phthalocyanine was dispersed in a mixed solution of 50 ml of ethanol and 40 g of hydroxypropyl cellulose. Then this solution was added to 25 g of tetraethoxysilane and the mixture was thoroughly stirred. Next, 23.5 g of an aqueous solution containing 0.3 ml of hydrochloric acid was added, and the mixture was stirred at room temperature for 10 minutes, thereby preparing a solution designated as G. Also, another solution, designated as H, was prepared in the same manner as G, except for the use of phthaloperinone in place of copper phthalocyanine. Likewise, still another solution, designated as I, was prepared in the same manner as G, except for the use of 4, 5, 6, 7,-tetrachloroquinophthalonone in place of copper phthalocyanine. Then, each of the solutions G, H, and I was applied to both surfaces of a #7059 glass substrate with a thickness of 0.5 mm by a dipping method, and the respective substrates were heated at 100°C for 60 minutes, thereby forming gel films. The peak absorption wave lengths of the respective color filters obtained in this manner were the same as those shown in Table 1. Example 12 A solution was prepared by adding acetylacetone to an ethanol solution of zirconium tetrabutoxide, and then adding methylene blue to the mixture. The solution so obtained was sprayed onto a #7059 glass substrate with a thickness of 0.5 mm by a spray method and then was heated at 100°C for 30 minutes, thereby forming a colored film. Example 13 Water was added to a mixed solution of tetramethoxysilane and methanol, thereby obtaining a methanol solution in which a portion of the tetramethoxysilane had been hydrolyzed. Then, this methanol solution was mixed with a solution obtained by dissolving tetramethoxytitanium in methanol, and the preparation of the solution was completed by adding 4, 5, 6, 7,-tetrachloroquinophthalone to this mixture. This solution was applied to the surface of a #7059 glass substrate with a thickness of 0.5 mm by a spin-coating method (3000 revolutions), and this coated substrate was heated at 150°C for 60 minutes, thereby obtaining a colored film. Example 14 A solution was prepared by adding 3-(4'-dimethylaminophenylazo)-pyridinium chloride and terpineol, as a thickener, to a ethanol solution of methyltriethoxysilane. This solution was applied to one surface of a transparent acrylic resin plate 1 mm in thickness by a screen printing technique, after which the plate was dried at 60°C for 60 minutes, thereby forming a colored film. Example 15 Figure 6 is a graph showing the transmittance-wave length relationship of a color filter fabricated with the solution D-2 obtained in Example 10. This filter exhibits an absorption at around 620 nm, while light of the other wave lengths is transmitted very well. Therefore, this filter can be effectively used for luminosity correction. That is, as shown in Figure 7, by using the aforesaid filter, the relative luminosity curve (indicated by the solid line (b)), which, owing to high sensitivity at 620 nm, deviates from a curve (showing the standard relative luminous efficiency function V(lambda)) indicated by the broken line (a), can be corrected so as to coincide with the latter curve (a). Thus, filters fabricated by the methods of the present invention are effective for applications requiring absorption only of specified wave lengths. Example 16 The absorption wave lengths of the color filters can be adjusted by mixing a plurality of dyes. Figure 8 is a graph showing the transmittance-wave length relationship of a color filter fabricated with the solution E-2 obtained in Example 10, while Figure 9 is a graph showing the transmittance-wave length relationship of a color filter fabricated by coating and drying a mixture of solutions E-2 and D-2 onto a glass substrate. The transmittance curve (d) shown in Figure 9 corresponds to the sum of the transmittance curve (a) of a filter fabricated using solution D-2 and the transmittance curve (c) of a filter fabricated using solution E-2. Thus, by using mixed solutions of several dyes with different absorption wave lengths, the absorption wave lengths of the color filters so obtained can be controlled. The same effect as above can also be obtained by superimposing a filter fabricated from solution D-2 and a filter fabricated from solution E-2. The principal characteristics of the color filters obtained in the Examples 8-14 described above are shown in Table 5, along with two comparative examples. Comparative Example 3 is a color sensor light receptor employing an organic film filter of the type illustrated in Figure 10, while Example 4 is a color sensor light receptor employing a printed film of the type illustrated in Figure 11. Changes in wave length dependence of transmittance at 70°C and 90% relative humidity Long-term reliability Embodiment 8 None No fading by UV radiation 9 None No fading by UV radiation 10 None No fading by UV radiation 11 None No fading by UV radiation 12 None No fading by UV radiation 13 None Extremely high weather resistance 14 None Excellent adhesion to plastic substrates Comparative examples 3 Transmitted wave lengths shifted UV cutoff filter required 4 Transmitted wave lengths shifted UV cutoff filter required

Claims: A process for preparing a color filter comprising a substrate (1) and a colored layer (4) formed on the surface of said substrate (1), wherein said colored layer (4) contains a transparent layer (2) and a coloring agent (3) dissolved or dispersed within said transparent layer (2), which process comprises: (i) preparing a colorant solution or dispersion by dissolving or dispersing the coloring agent (3) in an alkoxide solution, wherein the coloring agent contains at least one element selected from the group consisting of dyes and pigments, and wherein the alkoxide solution contains an alkoxide of at least one element selected from the group consisting of silicon, germanium, titanium, zirconium, lead, boron, aluminum, phosphorus and arsenic; (ii) applying said colorant solution or dispersion to the substrate (1); (iii) forming the colored layer (4) on the surface of the substrate (1) in a thickness of 10 µm or less by heating the substrate to which the colorant solution or dispersion is applied; and (iv) the colored layer (4) is heated at temperatures from 60°C to 150°C. A process as claimed in claim 1, wherein said substrate (1) is made of glass or plastic material. A process according to claims 1 or 2, wherein said coloring agent (3) is formed from several kinds of dyes and/or several kinds of pigments having absorption peaks at different wave lengths. A process according to one of claims 1 to 3, wherein said transparent layer (2) is capable of absorbing ultraviolet radiation. A process according to claim 4, where the applying and the forming are performed at least twice. A process according to claim 4 or 5, wherein said colorant solution contains, as a film-forming auxiliary, an organic compound selected from the group consisting of hydroxypropyl cellulose and hydroxyethyl cellulose: A process according to any of claims 1 to 6, further comprising the treatment of the surface of the substrate (1) with a coupling agent prior to the application of the colorant solution to the substrate (1). A process according to claim 7, wherein said colorant solution contains a coupling agent. A color filter comprising a substrate (1) and a colored layer (4) formed on the surface of said substrate (1), wherein said colored layer (4) contains a transparent layer (2) and a coloring agent (3) dissolved or dispersed within said transparent layer (2), and has a thickness of 10 µm or less, said transparent layer is made from an alkoxide solution of at least one element selected from the group consisting of silicon, germanium, zirconium, lead, boron, aluminum, phosphorus and arsenic; and said coloring agent consists of at least one element selected from the group consisting of dyes and pigments, where the colored layer (4) is heated on the surface of the substrate (1) at temperatures from 60°C to 150°C. A color filter claimed in claim 9, wherein said substrate (1) is made of glass or plastic material. A color filter according to claims 9 or 10, wherein said coloring agent (3) is formed from several kinds of dyes and/or several lands of pigments having absorption peaks at different wave lengths. A color filter according to one of claims 9 to 11, wherein said transparent layer (2) is capable of absorbing ultraviolet radiation. A color filter according to claim 12, wherein said colorant solution contains, as a film-forming auxiliary, an organic compound selected from the group consisting of hydroxypropyl cellulose and hydroxyethyl cellulose. A color filter according to any of claims 9 to 13, further comprising the treatment of the surface of the substrate (1) with a coupling agent prior to the application of the colorant solution to the substrate (1). A color filter according to claim 14, wherein said colorant solution contains a coupling agent.

Inventors: IKEDA MASAKI, KIMURA KUNIO, MINAMI TSUTOMU, NAKAZUMI HIROYUKI, NISHINO ATSUSHI, TOHGE NOBORU, YOSHIDA AKIHIKO, IKEDA, MASAKI, KIMURA, KUNIO, MINAMI, TSUTOMU, NAKAZUMI, HIROYUKI, NISHINO, ATSUSHI, TOHGE, NOBORU, YOSHIDA, AKIHIKO
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1991
Main classification: C03C17
IPC codes: C03C17