Low modulus silicone sealants

Abstract: A process for producing a silicone sealant, which is stable in the absence of moisture, cures when exposed to moisture, has an elongation at break of greater than 800 percent, and has adhesion to concrete. The silicone sealant is produced by first mixing an alkoxysilethylene endblocked polymer, a dialkyldialkoxysilane, and a titanium catalyst, then mixing in precipitated calcium carbonate filler having a fatty acid surface treatment.

Description: This invention relates to improved neutral curing silicone sealants which cure upon exposure to moisture at room temperature, having low modulus and adhesion to concrete. Silicone sealants which cure through a neutral reaction are known in the art. Examples can be found in U.S. Patent No. 3,856,839, issued December 24, 1974, disclosing alkanedioxy titanium chelates which catalyze the cure of a composition which also contains methyltrimethoxysilane and a silanol chain-stopped polydiorganosiloxane fluid; and U.S. Patent No. 4,143,088, issued March 6, 1985, disclosing use of alkoxylated organosilicon compounds consisting of either monomers or polymers having difunctional, trifunctional,or tetrafunctional molecules, comprising at most 40 percent of difunctional monomers in an organosilicon composition which is storage stable in the absence of moisture and is rapidly curable into elastomers with self-adherent properties in the presence of water at room temperature. The sealants such as described in these references have a tendency to require a longer time to cure as they shelf age. In some cases, the sealant arrives at a point where it no longer cures upon exposure to moisture. This is particularly serious, because the user does not realize the problem until after the sealant is put into place. To correct the problem, all of the uncured sealant must be removed and replaced, a very time consuming and expensive undertaking. A method of improving the storage stability is shown in U.S. Patent No. 4,687,829, issued August 18, 1987. An improved sealant is produced by mixing alkoxy functional polydiorganosiloxane having alkoxysilethylene ends with a combination of trifunctional or tetrafunctional silane crosslinker and difunctional silane chain extender. A method of producing such a sealant having an in situ treated filler is taught in U.S. Patent No. 4,711,928, issued December 8, 1987. US-A-4,888,380 describes a process of producing silicone sealants containing polydiorganosiloxane having alkoxy endblocking, alkoxy functional crosslinker and/or chain extender, and titanium catalyst, wherein the improvement comprises a method comprising: (A) mixing in the absence of moisture (1) 100 parts by weight of a polymer of the formula: where each R is free of aliphatic unsaturation and is at least one selected from the group consisting of monovalent hydrocarbon, monovalent halohydrocarbon, and monovalent cyanoalkyl radicals of 1 to 18 inclusive carbon atoms, each D is selected from the group consisting of hydroxyl radical and radical of the formula: where R'' is at least one selected from the group consisting of methyl, ethyl, propyl, and butyl, Z is a divalent hydrocarbon radical or a combination of divalent hydrocarbon radicals and siloxane radicals, m is 0 or 1, and x is of a value such that the polymer has a viscosity of from 0.5 to 3000 Pa.s at 25°C., (2) from 0.1 to 14 parts by weight of an alkoxysilane of the formula: R' a Si(OR'') 4-a where R' is at least one selected from the group consisting of methyl, ethyl, propyl, phenyl, and vinyl, R'' is as defined above, and a is 0, 1 or 2, and (3) from 0.2 to 6.0 parts by weight of titanium catalyst, and (B) adding after the above are mixed, (4) from 5 to 60 parts by weight of reinforcing filler, then (C) scoring the mixture in the absence of moisture, to give a sealant which is stable in the absence of moisture and has a slump of less than 25.4 mm (less than 1 inch) when measured in accordance with ASTM D 2202. Neutral curing sealants having reinforcing silica fillers have been produced which have a low modulus, but their adhesion to concrete has been marginal. A need exists for a low cost, neutral sealant having a low modulus and good adhesion to concrete for use as a sealant for highways. The method of this invention prepares a sealant by mixing in the absence of moisture an alkoxysilethylene endblocked polydiorganosiloxane, difunctional alkoxysilane, and titanium catalyst, then admixing an extending filler. This invention relates to a process for producing silicone sealants containing polydiorganosiloxane having alkoxy endblocking, alkoxy functional chain extender, and titanium catalyst, comprising: (A) first mixing in the absence of moisture (1) 100 parts by weight of a polymer mixture of the average formula: where each R is free of aliphatic unsaturation and is selected from the monovalent hydrocarbons, monovalent halohydrocarbons, and monovalent cyanoalkyl radicals of 1 to 18 carbon atoms, inclusive, each D is selected from vinyl radicals and radicals of the formula: where each R'' is selected from methyl, ethyl, propyl, and butyl, Z is a divalent hydrocarbon radical having from 2 to 15 carbon atoms or a combination of divalent hydrocarbon radicals and of siloxane radicals represented by the formula: where R is as defined above, b is 0 or 1, and c is from 1 to 6, m is O or 1, and x is of a value such that the polymer has a viscosity of from 0.5 to 3000 Pa·s at 25°C, less than 40 percent of the total of the endblocking radicals D in the polymer mixture being vinyl radicals, (2) from 0.1 to 14 parts by weight of methylvinyldimethoxysilane, and (3) from 0.2 to 6.0 parts by weight of titanium catalyst, (B) adding, after the above ingredients (1) - (3) are mixed, (4) from 10 to 200 parts by weight of precipitated calcium carbonate filler, having surface thereof treated with a fatty acid and having a surface area greater than 20 m²/g, the amount of filler being adjusted to give an elongation at break grater than 800 percent, in accordance with ASTM D412, and (C) storing the resulting mixture in the absence of moisture, to give a sealant which is stable in the absence of moisture, has an elongation at break greater than 800 (ASTM D412), and has adhesion to concrete. The method of this invention uses a polymer mixture of the average formula: where each R is free of aliphatic unsaturation and is selected from monovalent hydrocarbons, monovalent halohydrocarbons, and monovalent cyanoalkyl radicals of 1 to 18 carbon atoms, inclusive, each D is selected from vinyl radicals and radicals of the formula: where each R'' is selected from methyl, ethyl, propyl, and butyl, Z is a divalent hydrocarbon radical or a combination of divalent hydrocarbon radicals and siloxane radicals represented by the formula: where R is as defined above, b is 0 or 1, and c is from 1 to 6, m is O or 1, and x is of a value such that the polymer has a viscosity of from 0.5 to 3000 Pa.s at 25°C, less than 40 percent of the total of the endblocking radicals D in the polymer mixture being vinyl radicals. R may be any of those monovalent hydrocarbons, monovalent halohydrocarbons, or monovalent cyano-alkyl radicals of 1 to 18 carbon atoms, inclusive, which are known to be useful in silicone sealant materials. The preferred radicals are methyl, ethyl, propyl, phenyl, and trifluoropropyl. As stated above, Z is a divalent hydrocarbon radical or a combination of divalent hydrocarbon radicals and of siloxane radicals as defined above. The divalent hydrocarbon radical may be a radical of from 2 to 15 carbon atoms in the form of a divalent alkylene or arylene radical such as ethylene, propylene, hexylene, phenylene, or The polymer mixture of component (1) above may be produced by reacting a vinyl endblocked polydiorganosiloxane of the formula (I): where each R is as defined above, Vi is a vinyl radical, and x is as defined above, with an endcapping composition of the formula (II): where R, R'', and m are as defined above, and c is 1 to 6. This endcapping composition can be produced by a method comprising: (A) mixing 1 mole of a composition (a) of the formula: where R, R'', and m are as defined above, with more than 2 moles of a composition (b) of the formula: where R and c are as defined above, in the presence of a platinum catalyst and allowing to react, then, (B) optionally stripping the excess composition (b) from the product, to give an endcapping composition of the formula as given above. A preferred endcapping composition is that obtained when c is equal to 1 and m is equal to 0. The above endcapping composition, it's method of manufacture, and it's use in the manufacture of silicone sealants, having an alkoxy functional silane crosslinker and a titanium catalyst, is taught in U.S. Patent No. 4,772,675, issued September 20, 1988. The polymer produced from the above reaction of vinyl endblocked polydiorganosiloxane (I) and endcapping composition (II) can be represented by the formula where each R, R'', Vi, m , c , and x , are as defined above, and d and e are chosen so that d is on average less than 40 percent of the total of d plus e . The amount of the endcapping composition (II) used to react with the vinyl endblocked polydiorganosiloxane (I) is chosen so that the desired number of the vinyl endblocking groups are replaced with the alkoxysilethylene endblocking group from (II) on a molar basis. As an example, when the endcapping composition (II) is of the formula: where Me is the methyl radical, and the vinyl endblocked polydiorganosiloxane (I) is a polydimethylsiloxane having a viscosity of about 55 Pa-s at 25°C, then, the degree of endblocking versus the amount of endblocker used can be estimated from the following: Parts by Weight of Endblocker Percent of Alkoxysilethylene Endblocks 0.9 100 0.8 89 0.7 78 0.6 67 0.5 55 The above polymers may also be produced by using similar siloxanes and silanes in which the location of the hydrogen atom and the vinyl group which react together are reversed. Methylvinyldimethoxysilane is added as a modulus control agent. Methylvinyldimethoxysilane and its method of manufacture are well known. The amount of methylvinyldimethoxysilane is preferably from 0.1 to 14 parts by weight, with from 2 to 8 parts being most preferred. The sealants of this invention are cured through the use of a titanium catalyst (3). The titanium catalyst may be any of those known to be useful in catalyzing the moisture induced reaction of alkoxy containing siloxanes or silanes. Preferred is a titanium catalyst such as the beta-dicarbonyl titanium compounds described in U.S. Patent No. 3,334,067, the latter patent shows beta-dicarbonyl titanium catalysts and their methods of manufacture. Preferred catalysts include bis-(acetylacetonyl)-diisopropyltitanate, and 2,5-di-isopropoxy-bis-ethylacetoacetate titanium. The amount of catalyst is from 0.2 to 6.0 parts by weight per 100 parts by weight of polymer (1). Preferred are from 0.5 to 3.0 parts by weight. The filler used in the compositions of this invention is a precipitated calcium carbonate filler, having a fatty acid surface treatment and a surface area greater than 20 m²/g. Precipitated calcium carbonate fillers are man-made materials formed through a "Milk of Lime" process which consists in exposing limestone to very high temperatures to form calcium oxide, then reacting with water and precipitating with carbon dioxide. The process typically gives particle sizes of from 3 to 0.07 micrometers in average diameter. The precipitated calcium carbonates tend to have a higher water content than ground calcium carbonate due to their smaller particle size and the process of manufacture. The precipitate is then treated with a fatty acid, such as stearic acid to improve its compatibility with the polymer in which it is to be used. These treated, precipitated calcium carbonates are commercially available. A preferred filler for this invention is Hakuenka-CCR™, obtained from Shiraishi Kogyo Kaisha, Ltd., having a surface area of about 30 m²/g and about 2.3 percent fatty acid treatment. Another preferred filler is Winnofil-SPM™ obtained from ICI Resins US, having a surface area of about 23 m²/g and about 2.7 percent fatty acid treatment. The filler is preferred in amounts of from 60 to 120 parts by weight per 100 parts by weight of polymer (1), With amounts of from 70 to 90 parts by weight being most preferred. The optimum amount of filler will depend upon the polymer used and the filler used. The amount of filler used has an effect upon the physical properties of the cured sealant, particularly its tensile strength and elongation. As the amount of filler is increased, the elongation is decreased. The silicone sealants claimed in this invention are required to have an elongation at break of greater than 800 percent, so the amount of filler is adiusted to give greater than this elongation. The preferred filler has greater than 22 m²/g surface area. It has also been found that when amounts of the above treated fillers of 70 and 80 parts per 100 parts of polymer are used, up to 50 percent by weight of the filler can be replaced by a surface treated ground calcium carbonate having an average partlcle size of about 3 micrometers. The process of this invention requires that the polymer mixture (1), the methylvinyldimethoxysilane (2), and the titanium catalyst (3) be mixed together before the addition of the precipitated calcium carbonate filler (4). The methylvinyldimethoxysilane (2) must be added to the polymer mixture (1) before or at the same time as the titanium catalyst (3), and they must be mixed together before the filler (4) is added. Since the polymer mixture (1) and the methylvinyldimethoxysilane (2) will react with each other, particularly in the presence of the titanium catalyst (3) in the presence of moisture, it is necessary that moisture should not be present in these ingredients, and that the mixing be carried on without allowing the ingredients to come into contact with moisture from the atmosphere. A preferred procedure adds the polymer mixture to a mixing device which can be subjected to vacuum, then mixes in the methylvinyldimethoxysilane until uniform. The catalyst is then added and mixed until uniform. At this point in the process, it is preferred to draw a vacuum on the mixture while continuing mixing in order to remove residual volatile materials, including any water which may have been introduced and alcohol which is generated. The precipitated calcium carbonate filler is then added and mixed until uniform. A vacuum is again applied to the mixture to remove any volatile materials, including any moisture added with the filler, and to remove air from the mixture. The deaired mixture is then transferred to storage tubes, without exposure to moisture in the air. If the process is changed so that the filler is added before the catalyst and chain extender, the finished sealant is a different product. Sealants made not following the order of mixing of this invention have poorer adhesion to substrates than sealants which are processed according to the process of this invention. The following examples are included for illustrative purposes only and should not be construed as limiting the invention which is properly set forth in the appended claims. All parts are parts by weight. The polymer mixtures used in this invention were produced by placing 100 parts by weight of dimethylvinylsiloxy endblocked polydimethylsiloxane having a viscosity of about 55 Pa.s at 25°C in a mixing vessel and adding 0.01 part of the chloroplatinic acid complex of divinyltetramethyldisiloxane, which had been diluted with dimethylvinylsiloxy endblocked polydimethylsiloxane to provide 0.7 weight percent platinum in the complex, and stirring for 10 minutes. Then 1.1 parts (polymer A) or 0.7 part (polymer B) of a tetramethyldisiloxane having a trimethoxysilylethylene group on one end with the formula was slowly added and agitation was continued for 3 to 4 hours, maintaining the temperature below 50°C at all times. Polymer A, with 1.1 parts of endcapper per 100 parts of polymer would have essentially all of the endgroups blocked with the trialkoxysilethylene group. Polymer B, with 0.7 part of endcapper per 100 parts of polymer would have approximately 80 percent of the endblocks as trimethoxysilethylene groups and 20 percent as vinyl groups. Example 1 A series of sealants were prepared by mixing 100 parts of polymer A with 7 parts of vinylmethyldimethoxysilane and 2 parts of 2,5-di-isopropoxy-bis-ethylacetoacetate titanium in the absence of moisture until uniform, then a vacuum of 67.7 to 84.7 kPa (20 to 25 inches of mercury) was applied, and mixing was continued for about 4 minutes to remove air and volatiles. Then, the amounts of precipitated calcium carbonate shown in Table I were added and mixed in without exposing the mixture to moisture. The mixture was then put under vacuum of 67.7 to 84.7 kPa (20 to 25 inches of mercury) and mixing was continued for 10 to 15 minutes until the mixture was smooth and air free. The sealant was then transferred to a sealed storage tube without exposure to moisture. Test samples were prepared by extruding the sealant from the storage tube into a chase and smoothing the sealant into a slab, 2mm (0.080 inches) in thickness. After curing for 7 days at 50 percent relative humidity and 25°C, test pieces were cut out and tested for durometer in accordance with ASTM D 2240, tensile strength and elongation in accordance with ASTM D 412. The rate of curing of the samples was determined by a tack free time (TFT). The tack free time is defined as the time in minutes required for a curing material to form a non-tacky surface film. A sample is spread on a clean smooth surface and timing is begun. Periodically, a clean strip of polyethylene film is laid upon a fresh surface and a 28.4g (one ounce) weight applied to it. After 4 seconds, the weight is removed and the strip gently pulled off. The time when the strip pulls cleanly away from the sample is recorded as the tack free time. A series of comparative sealants were made in which the vinylmethyldimethoxysilane was replaced with methyltrimethoxysilane, and the polymer B having 20 percent polymer ends which would not be reactive in the curing was substituted for the polymer A having all reactive ends. The results obtained are shown in Table II. The methyltrimethoxysilane does not yield a sealant having the required percent of elongation for the intended use, even though a polymer having less trimethoxysilethylene ends was used. The adhesion of a formulation of this invention was tested by using the first composition of Table I to make 3 tensile adhesion joints. These joints were made by laying 2.5 x 2.5 x 7.6 cm (1 by 1 by 3 inch) concrete blocks, which had been cleaned with water and dried to remove all dust and loose debris, together with their 7.6 cm (3 inch) sides parallel and 1.3 cm (1/2 inch) apart to give a 1.3 x 1.3 x 7.6 cm (1/2 by 1/2 by 3 inch) long space. A 1.3 cm (1/2 inch) diameter polyethylene backer rod was inserted into the bottom of the space, then a bead of the test sealant used to fill the remainder of the space, with the upper surface of the sealant being flat and even with the upper surface of the concrete blocks. The joints were cured for 21 days at standard laboratory conditions, then submerged in water for 7 days. The joints were then flexed to a 45 degree angle and the amount of release of the sealant from the concrete surfaces observed. The average amount of release was about 0.75 cm² out of the total surface area of 32.8 cm². The joints were then placed in a testing machine which compressed the joint 50 percent, then elongated the joint for 100 percent, at a rate of 3.2 mm (1/8 inch) per hour. After a total of ten such cycles, the joint was flexed 45 degrees and an average release of about 1 cm² was observed. The material adhered well to concrete. Example 2 A series of samples were prepared as in Example 1, using polymer B, 70 parts of Winnofil-SPM filler, 2 parts of 2,5-di-isopropoxy-bis-ethylacetoacetate titanium catalyst, and the kind and amount of silane crosslinker or chain extender shown in Table III. Another series was prepared in the same manner, but using 1.6 parts of tetrabutyltitanate as catalyst instead of the 2 parts of 2,5-di-isopropoxy-bis-ethylacetoacetate titanium used above. The results obtained are shown in Table IV. These results show that only the vinylmethyldimethoxysilane in combination with the tetrabutyltitanate catalyst gave the required elongation. This formulation had a longer TFT time with polymer B as compared to use of Polymer A in the second set of samples in Example 3, below. Exampl e 3 A series of samples were prepared as in Example 2, using polymer A, 70 parts of Winnofil-SPM™ filler, first the 2,5-di-isopropoxy-bis-ethylacetoacetate titanium catalyst and then the tetrabutyltitanate catalyst, and the kind and amount of silane crosslinker or chain extender shown in Table V. These results show that only the vinylmethyldimethoxysilane in combination with the 2,5-di-isopropoxy-bis-ethylacetoacetate titanium results in the desired high elongation coupled with a short cure time; a combination of properties making the sealant esspecially useful in the highway sealant market. Example 4 A series of comparative sealants was prepared, but the order of mixing was changed. First, 100 parts of Polymer A and the parts of Winnofil-SPM™ filler shown below in Table VI were mixed together. Then, 2 parts of 2,5-di-isopropoxy-bis-ethylacetoacetate titanium catalyst and 7 parts of vinylmethyldimethoxysilane were added, all done without exposure to moisture and with the deairing steps of Example 1 included. The sealants were tested as in Example 1 with the results shown in Table VI. These results show that the method of this invention must be followed in order to obtain successful results; even though the ingredients used in this example are those required in the method of this invention, the change in method gave sealants with unsatisfactory properties.

Claims: A process for producing silicone sealants containing polydiorganosiloxane having alkoxy endblocking, alkoxy functional chain extender, and titanium catalyst, comprising: (A) first mixing in the absence of moisture (1) 100 parts by weight of a polymer mixture of the average formula: where each R is free of aliphatic unsaturation and is selected from monovalent hydrocarbons, monovalent halohydrocarbons, and monovalent cyanoalkyl radicals of 1 to 18 carbon atoms, inclusive, each D is selected from vinyl radicals and radicals of the formula: where each R'' is selected from methyl, ethyl, propyl, and butyl, Z is a divalent hydrocarbon radical having from 2 to 15 carbon atoms or a combination of divalent hydrocarbon radicals and of siloxane radicals represented by the formula: where R is as defined above, b is 0 or 1, and c is from 1 to 6, m is O or 1, and x is of a value such that the polymer has a viscosity of from 0.5 to 3000 Pa·s at 25°C, less than 40 percent of the total of the endblocking radicals D in the polymer mixture being vinyl radicals, (2) from 0.1 to 14 parts by weight of methylvinyldimethoxysilane, and (3) from 0.2 to 6.0 parts by weight of titanium catalyst, (B) adding, after the above ingredients (1) - (3) are mixed, (4) from 10 to 200 parts by weight of precipitated calcium carbonate filler, having the surface thereof treated with a fatty acid and having a surface area greater than 20 m²/g, the amount of filler being adjusted to give an elongation at break grater than 800 percent, in accordance with ASTM D412, and (C) storing the resulting mixture in the absence of moisture, to give a sealant which is stable in the absence of moisture, has an elongation at break greater than 800 (ASTM D412), and has adhesion to concrete. The silicone sealant produced by the method of claim 1.

Inventors: CHU HSIEN-KUN, KAMIS RUSSELL PETER, LOWER LOREN DALE, CHU, HSIEN-KUN, KAMIS, RUSSELL PETER, LOWER, LOREN DALE
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1991
Main classification: C08K9
IPC codes: C08K5, C08L83, C09K3, C08K9