Curable resin compositions

Abstract: A curable resin composition comprises (a) an organic resin containing at least two alkenyl groups per molecule, and havinv a number average molecular weight of 500-100,000, (b) an organohydrogen-polysiloxane containing no less than two Si-H bonds per molecule, and (c) a platinum catalyst. Component (a) is preferably chosen from at least one of acrylic, polyester and epoxy resins. The preferred amount of component (b) is such that there are 0.8-4 hydrogen atoms bonded to silicon atoms per alkenyl group of component (a). The compositions can be cured at low temperatures without shrinking to give a product having good water and chemical resistance, and recoatability.

Description: This invention relates to curable resin compositions, the cured compositions having excellent weatherability and physical properties. In the prior art, curable resin compositions are known comprising a hydroxyl group-containing resin such as an acrylic resin or polyester resin, blended with a melamine resin or polyfunctional isocyanate compound as a curing agent. However, in such melamine-containing compositions curing requires a high temperature of 150 - 230°C resulting in poor workability and economic viability. These compositions also lose lower alcohols, with a corresponding loss of volume; and further, they suffer from the disadvantage of poor weatherability due to the triazine skeleton. In the case of isocyanate-containing compositions there is also the problem of toxicity and poor weatherability. There have been reported attempts to improve weatherability by condensation crosslinkage at room temperature of acrylic resins having alkoxysilyl groups introduced into the molecule (e.g. Japanese Kokai Koho (Unexamined Publication) Nos. 57-36109 and 58-55666), but as the curing rate of such compositions was slow, contamination occurred due to hydrolysis of the remaining alkoxysilyl groups, and they also had poor anti-corrosion properties. Other curing systems have been reported which make use of the reactivity of alkoxysilyl groups and hydroxyl groups in organic resins (e.g. Japanese Kokoku Koho (Examined Publication) No. 63-33512); however, not only was their thermocuring rate slow, but also their resistance to salt water was poor. On the other hand, systems in which a vinylpolysiloxane and organohydrogenpolysiloxane are cured in the present of a platinum catalyst have been known for many years. However, the cured product swells up in solvents and therefore has poor solvent resistance. In addition, it has poor alkali resistance and, as it also has poor recoatability, its use in the paint field has been very limited. It has been proposed to improve recoatability by using alkoxysiloxane-modified polyesters containing propyl groups (e.g. Japanese Patent Kokai Koho No. 62-263265); and adopting a crosslinking method employing polysiloxanes containing alkoxysilylalkyl groups (e.g. Japanese Kokai Koho Nos. 57-139123 and 61-127733). Even using these methods, however, a curing composition which is satisfactory from the viewpoints of mechanical strength, compatibility with other resins and recoatability, has still not been found. Further, in recent years, paints which contain organic solvents have been cited as factors responsible for atmospheric pollution. We have carried out intensive studies to overcome these disadvantages of the prior art compositions, and we have found that by crosslinking an organic resin containing unsaturated groups utilising an addition reaction with an organohydrogenpolysiloxane, the weatherability and physical properties, i.e. solvent resistance, alkali resistance, acid resistance, water resistance, salt water resistance, anti-corrosion properties and contamination resistance could be improved. In addition, recoatability was satisfactory, and when the composition was used as a paint, there was not necessarily any need to use organic solvents. An aim of this invention is therefore to provide a solvent-free or high-solid type curable resin composition which can be cured at low temperature without causing atmospheric pollution due to organic solvents to form a cured product which has excellent weatherability; does not undergo any shrinkage after curing, and can thus be used as a molding resin; and has excellent humidity resistance, water resistance, salt water resistance, solvent resistance, alkali resistance, acid resistance and recoatability. The above aims are attained by a composition comprising (a) at least one resin preferably chosen from acrylic and polyester resins, and having at least two organic groups containing alkenyl groups per molecule and a number average molecular weight of 500 - 100,000; (b) an organohydrogenpolysiloxane containing at least two Si - H bonds per molecule; and (c) a platinum compound. The curing reaction in the composition proceeds at low temperature, and there is practically no shrinkage after curing. Moreover, as the curing is a crosslinking reaction which involves the formation of Si-C bonds, the cured product has very good weatherability, water resistance and solvent resistance. Consequently, it has good recoatability, and its weatherability is further enhanced. The alkenyl groups in the resin used as component (a) of this invention may for example be vinyl, allyl, methylvinyl, dimethylvinyl, cyclohexenyl or butenyl. The acrylic resin containing alkenyl groups may be obtained by copolymerization of an acrylic monomer containing alkenyl groups such as allyl (metha)acrylate or cyclohexenylmethyl methacrylate with another polymerizable monomer. The acrylic monomer containing alkenyl groups may be obtained for example by a reaction involving the elimination of hydrochloric acid from methacrylic acid chloride and an alkenylic alcohol, a reaction involving the elimination of alcohol from a lower ester of methacrylic acid and an alkenylic alcohol, or an addition reaction of an acrylic monomer containing isocyanate with an alkenylic alcohol. As the other polymerizable monomer, an acrylic monomer is particularly to be preferred. The acrylic monomer may for example be methyl(metha)acrylate, ethyl (metha) acrylate, n-butyl (metha)acrylate, i-butyl (metha) acrylate, t-butyl(metha)acrylate, 2-ethylhexyl(metha) acrylate, lauryl(metha)acrylate, phenyl(metha)acrylate, benzyl(metha)acrylate, 2-hydroxyethyl(metha)acrylate, 2-hydroxypropyl(metha)acrylate, 4-hydroxybutyl(metha) acrylate, the addition product of 2-hydroxyethyl(metha) acrylate and ε - caprolactone (e.g. Placcel FM 1 (commercial name) manufactured by Daicell Kagaku Kogyo Inc.), glycidyl (metha)acrylate, 3-trimethoxysilylpropyl (metha)acrylate, 3-triethoxysilylpropyl-(metha)acrylate, 3-dimethoxymethylsilylpropyl-(metha)acrylate, 2-acrylamide-2-methylpropanesulfonic acid (metha)acrylate, acid phosphoxypropyl (metha)acrylate, tributyltin(metha)-acrylate, (metha)acrylamide, (metha)acryloyl isocyanate, or 2-isocyanate ethyl (metha)acrylate. In this invention, in addition to the above, a non-acrylic α, β-unsaturated monomer such as styrene, α-methylstyrene, itaconic acid, maleic acid, vinyl acetate, allyl acetate, vinyl trimethoxysilane, vinyl triethoxysilane, vinyl methyl-dimethoxysilane or vinyl methyl-diethoxysilane, can also be copolymerized. It is however preferable that the proportion of said monomer is no more than 50 wt %. Other methods of synthesizing the acrylic resin containing alkenyl groups are for example, the addition reaction of an acrylic resin containing hydroxyl groups with an alkenylic isocyanate compound and/or anhydride of a carboxylic acid containing alkenyl groups; addition reaction of an acrylic resin containing isocyanate with an alkenylic alcohol; addition reaction of an acrylic resin containing carboxyl groups with an epoxy compound containing alkenyl groups; and addition reaction of an acrylic resin containing epoxy groups with a carboxylic acid containing alkenyl groups. The acrylic resin containing hydroxyl groups may be obtained by copolymerization of an acrylic monomer containing hydroxyl groups such as 2-hydroxyethyl-(metha) acrylate, 2-hydroxypropyl-(metha)acrylate, 4-hydroxybutyl-(metha)acrylate, the addition product of 2-hydroxyethyl-(metha)acrylate and ε-caprolactone (e.g. the Placcel FM Series) with another acrylic monomer, or with a non-acrylic α, β- unsaturated monomer in a proportion of no more than 50 wt %, or by homopolymerization of an acrylic monomer containing hydroxyl groups. The alkenylic isocyanate may for example be allyl isocyanate, (metha)acryloyl isocyanate, or 2-isocyanate ethyl (metha)acrylate. The anhydride of the carboxylic acid containing alkenyl groups may be itaconic anhydride, maleic anhydride or tetrahydrophthalic anhydride. The acrylic resin containing isocyanate may be obtained by copolymerization of an acrylic monomer containing isocyanate such as (metha)acryloyl isocyanate or 2-isocyanate ethyl (metha)acrylate with another acrylic monomer, or with a non-acrylic α, β-unsaturated monomer in a proportion of no more than 50 wt. %, or by homopolymerization of an acrylic monomer containing isocyanate. The alkenylic alcohol may for example be allyl alcohol, 3-butene-1-ol, 2-(allyloxy)ethanol, glycerine diallyl ether, tetrahydrobenzyl alcohol, 3-methyl-2-butene-1-ol, 3-methyl-3-butene-1-ol, 2-methyl-3-butene-2-ol, oleyl alcohol or crotyl alcohol. The acrylic resin containing carboxyl groups may be obtained by copolymerization of an acrylic monomer containing carboxyl groups such as (metha)acrylic acid and/or an acrylic monomer containing carboxyl groups into which an α, β-unsaturated monomer with carboxyl groups such as itaconic acid or maleic acid has been incorporated with another acrylic monomer and/or a non-acrylic α, β-unsaturated monomer, the proportion of α, β -unsaturated monomer in the product being no more than 50 wt %, or by homopolymerization of an acrylic monomer containing carboxyl groups. The acrylic resin containing epoxy groups may be obtained for example by copolymerization of an acrylic monomer containing epoxy groups such as glycidyl (metha) acrylate with another acrylic monomer, or with a non-acrylic α, β-unsaturated monomer in proportion of no more than 50 wt %, or by homopolymerization of an acrylic monomer containing epoxy groups. The carboxylic acid containing alkenyl groups may for example be allyl acetate, (metha)acrylic acid, 2-butenonic acid, 3-butenonic acid, crotonic acid, 10-undecenoic acid or linoleic acid. Further, the polyester resin containing no less than two alkenylic organic groups per molecule may be easily manufactured by condensation polymerization of the above alkenylic alcohols and a polyfunctional alcohol with a polybasic acid. The polyfunctional alcohol may for example be ethylene glycol, propylene glycol, 1,6-hexane diol, diethylene glycol, neopentyl glycol, hydroxypivalic acid neopentyl glycol ester, trimethylolpropane or a dimethylsiloxane containing alcoholic hydroxyl groups at both ends. The polybasic acid may for example be phthalic anhydride, isophthalic acid, terephthalic acid, adipic acid, azelaic acid or trimellitic acid. Further, some monofunctional alcohol or monobasic acid may also be used if necessary. Other methods of synthesizing polyester resins containing alkenyl groups are for example, an addition reaction of the carboxyl groups of the polyester resin obtained by condensation polymerization of said polyfunctional alcohols and polybasic acids, with said epoxy compounds containing alkenyl groups, and an addition reaction of the hydroxyl groups of the polyester resin obtained by condensation polymerization of polyfunctional alcohols and polybasic acids with said alkenylic isocyanates and/or the anhydrides of carboxylic acids containing alkenyl groups. The molecular weight of these acrylic resins or polyester resins is preferably 500 - 100,000, but more preferably 2,000 - 50,000. If the organic resin containing alkenyl groups has a molecular weight of less than 500, it has poor film-forming properties and the film is weak; conversely, if its molecular weight is greater than 100,000, the resin is highly viscous, has poor workability and is unsuitable as a high solid type resin composition - that is, the proportion of non-volatiles is high. Component (b) of this invention is an organohydrogenpolysiloxane containing no less than two Si-H bonds per molecule. It crosslinks the alkenyl groups of component (a) by hydrosilylation. The organohydrogenpolysiloxane of component (b) may be represented by one of the following general formulae (I) - (3) : GENERAL FORMULA (1): where R¹ and R² are phenyl or alkyl groups with 1 - 6 carbon atoms, a is an integer in the range 0 ≦ a ≦ 100, and b is an integer in the range 2 ≦ b < ≦ 100. GENERAL FORMULA (2): where R² and R³ are phenyl or alkyl groups with 1 - 6 carbon atoms, c is an integer in the range 0 ≦ c ≦ 8, d is an integer in the range 2 ≦ d ≦ 10, and 3 ≦ c + d ≦ 10. GENERAL FORMULA (3): where R¹ and R² are phenyl or alkyl groups with 1 - 6 carbon atoms, e is an integer in the range 2 ≦ e ≦ 100, an f is an integer in the range 0 ≦ f ≦ 100. The alkyl groups with 1 - 6 carbon atoms, R¹, R² and R³, may be methyl, ethyl, propyl or butyl, but from an industrial viewpoint, methyl and propyl are to be preferred. Further, the degree of polymerization is specified by a - f. For siloxanes with a higher degree of polymerization than those given by the above ranges, viscosity increases, workability is poor and compatibility with component (a) declines. From the viewpoint of improving compatibility, compounds which include phenyl as the organic group are to be preferred. Examples of component (b) which are partirularly to be preferred are, therefore, methylphenyl hydrogenpolysiloxane and metlhylpropylhydrogenpolysiloxane. We give below the structural formulae of some specific examples of component (b), but this invention is by no means limited to these examples. The amount of component (b) added is preferably such that there are 0.8 - 4, but more preferably 1.0 - 1.5, hydrogen atoms bonded to silicon per alkenyl group of component (a). Hence, by adjusting the amount of component (b) which is added, a cured product with excellent weatherability, lustre and pliability can be obtained. If the number of hydrogen atoms is less than 0. 8 or more than 4, the resin or coating film deteriorates due to reaction of residual alkenyl groups or hydrogen atoms with moisture or contaminants, or due to the action of ultraviolet light. Component (c) of this invention is a catalyst intended to cure components (a) and (b). For this purpose, platinum with valency 0 or 4 may be used, but from an industrial viewpoint chloroplatinic acid is to be preferred. The curing reaction then proceeds at low temperature such as 80 - 180 °C, and there is practically no shrinkage after curing. The amount of platinum atoms is preferably 5 - 1,000 ppm, but more preferably 10 - 500 ppm, with respect to 100 parts by weight of a mixture of components (a) and (b). If it is less than 5 ppm curing properties are poor, while if it is greater than 1,000 ppm the composition tends to cure before application or molding which is undesirable. In this invention, in order to control reactivity, a substance which slows curing by coordinating with the platinum catalyst, for example an acetylenic compound, may also be added in a suitable proportion. This retarding agent should preferably be such that it volatilizes outside the system when vaporized, or such that it is present in a closed system and evaporates when the system is opened so as to activate the platinum catalyst. Examples of such retarding agents are ethynyl alcohol, 3-ol-propyne, 3-ol-3,3-dimethylpropyne, 3-trimethylsiloxy-propyne, and 3-trimethylsiloxy-3,3-dimethylpropyne. The mixture of components (a), (b) and (c) is cured either without a solvent or after dissolving in an organic solvent at room temperature or by heating. The preferable curing temperature is 80 - 180 °C. The crosslinkages formed by the curing reaction are Si-C bonds, unlike the case of the curing reaction which takes place by condensation of silanols and alcohols or alkoxy groups. The cured product therefore has excellent moisture resistance, water resistance and salt water resistance. Further, as the product is cured by crosslinking, it has quite good solvent resistance, alkali resistance and recoatability. Further, pigments and additives may be added to the resin composition of this invention if desired, but the addition of substances or compounds which interfere with the hydrosilylation reaction, for example substances containing elements such as nitrogen, phosphorus and arsenic, is undesirable. By applying to metals such as iron and aluminum, inorganic materials such as slate, concrete and tile or resins such as epoxy resin, acrylic resin, urethane resin and silicone resin, and curing the composition of this invention, a paint film with high durability, weatherability and water resistance is obtained. Further, by molding and curing the composition, a cured product with excellent mechanical properties and pliability is obtained. The composition may therefore be used as for example an external finish for paints, protective coating, electrical insulation material, anti-soiling topcoat and molding resin. Further, by using the composition of this invention, a high solid paint of low viscosity can also be obtained. EXAMPLES This invention will now be described in more detail by means of specific Examples, but it should be understood that the invention is in no way limited to them. All proportions are parts by weight. MANUFACTURING EXAMPLE 1 70 parts of xylene and 20 parts of butanol were introduced into a reaction vessel. After raising the temperature to 110 °C while introducing nitrogen gas, a mixed solution comprising 10 parts styrene, 10.7 parts methacrylic acid, 16.7 parts 2-ethylhexyl methacrylate, 40.1 parts methylmethacrylate, 22.5 parts ethyl acrylate and 1.2 parts t-butylperoxy 2-ethylhexanoate was dripped in over 3 hours. After the addition was complete, the mixture was aged at 105 °C for 1 hour, 10 parts xylene and 0.2 parts t-butylperoxy 2-ethylhexanoate were dripped in over 30 minutes, and the mixture aged at 105 °C for a further 2 hours. The reaction temperature was then raised to 120 °C, then 13 parts of allyl glycidyl ether and 0.2 parts of dimethylbenzylamine were each dripped in over 30 minutes. The yield of the addition reaction of carboxy groups to glycidyl groups was measured by means of acid titration. After 2 hours, an acrylic resin solution [A]was obtained with a yield of 86%. Non-volatiles in the solution [A] accounted for 52.8 wt%. MANUFACTURING EXAMPLE 2 80 parts of xylene were introduced into a reaction vessel while introducing nitrogen gas, and a mixed solution comprising 13.9 parts methacroyl isocyanate, 28.4 parts 2-ethylhexyl methacrylate, 34.6 parts methyl methacrylate, 23.2 parts ethyl acrylate and 1.2 parts t-butylperoxy 2-ethylhexanoate was dripped in over 3 hours. After the addition was complete, the mixture was aged at 105 °C for 1 hour, 20 parts xylene and 0.5 parts t-butylperoxy 2-ethylhexanoate were dripped in over 30 minutes, and ageing carried out at 105 °C for a further 2 hours. 20 parts butyl acetate were then added and after cooling to 50 °C 7.2 parts of allyl alcohol were dripped in over 30 minutes. 30 minutes after this addition was completed, the yield of the reaction between isocyanate and alcohol was measured by IR. It was found that the isocyanate absorption at 2,230 cm-1 had completely disappeared. The solution obtained will be referred to as acrylic resin solution [B]. Non-volatiles in the solution [B] accounted for 47.5 wt%. MANUFACTURING EXAMPLE 3 53.4 parts isophthalic acid, 26.7 parts neopentyl glycol, 17.8 parts hydroxypivalic acid neopentyl glycol ester, 1.6 parts trimethylol propane and 0.05 parts dibutyltin oxide were introduced into a reaction vessel equipped with a dropping funnel. After raising the temperature to 150 °C the temperature was raised to 210 °C over 10 hours, and a dehydration condensation reaction was carried out until the acidity was 5.0. The reaction temperature was then reduced to 120 °C, 17.1 parts anhydrous trimellitic acid were introduced gradually, and the mixture aged for 1 hour. 10.2 parts allyl glycidyl ether, 31 parts xylol and 0.2 parts dimethylbenzylamine were then introduced to carry out the reaction. The reaction was terminated after 2 hours when the acidity of the solid fraction was 5.0. 54 parts xylol were introduced into the reaction product to give a polyester resin solution [A]. Non-volatiles in the solution [A] accounted for 58.3 wt%. MANUFACTURING EXAMPLE 4 35.5 parts bisphenol A diglycidyl ether was introduced into a reaction vessel, and the temperature was raised to 120 °C. 17.2 parts butenonic acid and 0.1 parts dimethylbenzylamine were dripped in over 1 hour, and after ageing for 2 hours, 30 parts of xylol and 5 parts methylisobutyl ketone were added to give an epoxy resin solution [A]. Non-volatiles in the solution [A] accounted for 60.1 wt %. MANUFACTURING EXAMPLE 5 40 parts xylene and 20 parts butanol were introduced into a reaction vessel, and the temperature was raised to 110 °C while introducing nitrogen gas. A mixed solution comprising 15 parts styrene, 3.1 parts methacrylic acid, 34.1parts 2-ethylhexyl methacrylate, 31.6 parts methyl methacrylate, 16.2 parts 2-hydroxyethyl methacrylate and 1.2 parts t-butylperoxy 2-ethylhexanoate was then dripped in over 3 hours. After the addition was complete, the mixture was aged at 105 °C for 1 hour, 6.7 parts xylene and 0.2 parts t-butylperoxy 2-ethylhexanoate were dripped in over 30 minutes, and the mixture was aged at 105 °C for 2 hours to give an acrylic resin solution [C]. Non-volatiles in the solution [C] accounted for 59.7 wt%. MANUFACTURING EXAMPLE 6 53.4 parts isophthalic acid, 26.7 parts neopentyl glycol, 17.8 parts hydroxypivalic acid neopentyl glycol ester, 1.6 parts trimethylol propane and 0.05 parts dibutyltin oxide were introduced into a reaction vessel equipped with a dropping funnel. After raising the temperature to 150 °C, the temperature was raised to 210 °C over 10 hours, and a dehydration condensation reaction was carried out until the acidity was 5.0. 55 parts xylol were introduced into the reaction product to give a polyester resin solution [B]. Non-volatiles in the solution [B] accounted for 64.4 wt%. MANUFACTURING EXAMPLE 7 60 parts xylene were introduced into a reaction vessel, and the temperature was raised to 110 °C while introducing nitrogen gas. A mixed solution comprising 30 parts styrene, 30 parts 2-ethylhexyl methacrylate, 40 parts cyclohexenylmethyl methacrylate, and 2.0 parts azobis-isobutyronitrile was then dripped in over 3 hours. After the addition was complete, the mixture was aged at 110 °C for 1 hour, 6.7 parts xylene and 0.2 parts t-butylperoxy 2-ethylhexanoate were dripped in over 30 minutes, and the mixture was aged at 110 °C for a further 2 hours to give an acrylic resin solution [D]. Non-volatiles in the solution [D] accounted for 58.9 wt%. MANUFACTURING EXAMPLE 8 61.8 parts terephthalic acid, 29.5 parts hydroxypivalic acid neopentyl glycol ester, 9.6 parts trimethylol propane and 0.05 parts dibutyltin oxide were introduced into a reaction vessel equipped with a dropping funnel. After raising the temperature to 150 °C, the temperature was raised to 210 °C over 6 hours, and 20 ml of the mixture was distilled off. After cooling to 140 °C, 18.3 g of glycerine diallyl ether were introduced, the temperature was raised to 220 °C over 5 hours, and having confirmed that 3.4 g of methanol had distilled off, the reaction was terminated. 67 parts xylol was then introduced into the reaction product to give a polyester resin solution [C]. Non-volatiles in the solution [C] accounted for 58.8 wt%. MANUFACTURING EXAMPLE 9 60 parts xylene were introduced into a reaction vessel, and the temperature was raised to 110 °C while introducing nitrogen gas. A mixed solution comprising 30 parts styrene, 20 parts 2-ethylhexyl methacrylate, 50 parts cyclohexenylmethyl methacrylate, and 2.0 parts azobis-isobutyronitrile was then dripped in over 3 hours. After the addition was complete, the mixture was aged at 110 °C for 1 hour, 6.7 parts xylene and 0.2 parts t-butylperoxy 2-ethylhexanoate were dripped in over 30 minutes, and the mixture was aged at 110 °C for a further 2 hours to give an acrylic resin solution [E]. Non-volatiles in the solution [E] accounted for 60.3 wt%. EXAMPLE 1 80 parts of the acrylic resin solution [A], 20 parts of the compound: and 0.1 parts of a 2% ethanolic solution of chloroplatinic acid were mixed well together, applied to an iron plate of thickness 0.3 mm so as to form a dry film of thickness 20 µm, and baked at 180 °C for 20 minutes. The physical properties of the cured film are shown in Table 1. The values of physical properties were measured as follows. Pencil hardness: Measured according to JIS (Japan Industrial Standard) K 5400, pragraph 6 - 14. Xylol rubbing test: The film was rubbed 50 times back and forth with a 1 cm x 1 cm piece of cotton wool impregnated with xylene, and its external appearance was judged visually. Mandrel test: Measured according to JIS K 5400, paragraph 6 - 16. The external appearance of the film was judged visually using a 2 mm mandrel. Impact resistance test: Measured according to JIS K 5400, paragraph 6 - 13. A 300 g weight was dropped from a height of 50 cm, and the external appearance of the film was judged visually. Initial lustre: Titanium oxide (commercial name:TIPAQUE R-820, Ishihara Industries K.K.), was added to each resin in the proportion of 40 parts based on 100 parts by weight of solid resin and dispersed by a Ball Mill. The resulting white paint was cured, and the 60 degree mirror surface lustre (prior to weatherability test) was measured. The curing of the paint film of each Example and Comparative Example was carried out in the same way. Weatherability: Weatherability was measured by visually judging the retention of 60 degree mirror surface lustre and external appearance after exposure to 2,000 hrs of sunshine weather meter. Acid resistance: 0.2 cc of a 0.1N (normal) sulfuric acid solution was applied to each of the cured clear paint films. After leaving at 20 °C and 75% humidity for one day and night, the films were dried at 60 °C for 10 minutes, and their deterioration was visually judged. o ○ : excellent resistance ○ : good resistance Δ : some marks on film X : clouding of film Viscosity test: Each resin system was adjusted with xylol such that non-volatiles accounted for 55 wt %, and its viscosity was measured at 25 °C by an E type viscometer. Example 2 80 parts of the acrylic resin solution [A], 20 parts of 1,3,5,7-tetramethyl-1-propylcyclotetrasiloxane and 0.1 parts of a 2% ethanolic solution of chloroplatinic acid were mixed well together, applied to an iron plate of thickness 0.3 mm so as to form a dry film of thicknes 20 µm, and baked at 180 °C for 20 minutes. The physical properties of the cured film are shown in Table 1. EXAMPLE 3 60 parts of the acrylic resin solution [B], 20 parts of the compound: and 0.1 parts of a 2% ethanolic solution of chloroplatinic acid were mixed well together, applied to an iron plate of thickness 0.3 mm so as to form a dry film of thickness 20 µm, and baked at 180 °C for 20 minutes. The physical properties of the cured film are shown in Table 1. EXAMPLE 4 60 parts of the polyester resin solution [A], 20 parts of the compound: and 0.1 parts of a 2% ethanolic solution of chloroplatinic acid were mixed well together, applied to an iron plate of thickness 0.3 mm so as to form a dry film of thickness 20 µm, and baked at 180 °C for 20 minutes. The physical properties of the cured film are shown in Table 1. EXAMPLE 5 100 parts of the acrylic resin solution [D], 30 parts of the compound: and 0.1 parts of a 2% ethanolic solution of chloroplatinic acid were mixed well together, applied to an iron plate of thickness 0.3 mm so as to form a dry film of thickness 20 µm, and baked at 140 °C for 25 minutes. The physical properties of the cured film are shown in Table 1. EXAMPLE 6 100 parts of the polyester resin solution [C], 30 parts of the compound: and 0.1 parts of a 2% ethanolic solution of chloroplatinic acid were mixed well together, applied to an iron plate of thickness 0.3 mm so as to form a dry film of thickness 20 µm, and baked at 180 °C for 20 minutes. The physical properties of the cured film are shown in Table 1. EXAMPLE 7 100 parts of the acrylic resin solution [E], 30 parts of the compound: and 0.1 parts of a 2% ethanolic solution of chloroplatinic acid were mixed well together, applied to an iron plate of thickness 0.3 mm so as to form a dry film of thickness 20 µm, and baked at 140 °C for 25 minutes. The physical properties of the cured film are shown in Table 1. COMPARATIVE EXAMPLE 1 100 parts of acrylic resin (C) and 43 parts of SUPER BECKAMINE L-127 (a trade name of melamine resin manufactured by Dai Nippon Ink and Chemical Co.) were mixed well together, and cured as in Example 1. The measured physical properties are shown in Table 1. COMPARATIVE EXAMPLE 2 100 parts of acrylic resin (C), 25 parts of BURNOCK D-950 ( a trade name of polyisocyanate manufactured by Dai Nippon Ink and Chemical Co.) and 0.1 parts of dibutyltin dilaurylate were mixed well together, applied to an iron plate of thickness 0.3 mm, and cured at 25 °C for 1 hour. The physical properties of the film are shown in Table 1. COMPARATIVE EXAMPLE 3 100 parts of polyester resin [B] and 43 parts of SUPER BECKAMINE L-127 (a trade name of melamine resin manufactured by Dai Nippon Ink and Chemical Co. ) were mixed well together, and cured as in Example 1. The measured physical properties are shown in Table 1. COMPARATIVE EXAMPLE 4 80 parts of the epoxy resin solution [A], 20 parts of the compound: and 0.1 parts of a 2% ethanolic solution of chloroplatinic acid were mixed well together, applied to an iron plate of thickness 0.3 mm so as to form a dry film of thickness 20 µm, and baked at 180 °C for 20 minutes. The physical properties of the cured film are shown in Table 1. From the results in Table 1, it was confirmed that the curable resin composition of this invention is able to form a cured film which is particularly remarkable for its excellent lustre and weatherability.

Claims: A curable resin composition characterized in that the composition comprises the following components: (a) acrylic and/or polyester resin(s) containing no less than two alkenyl groups per molecule, and having a number average molecular weight of 500 - 100,000; (b) an organohydrogenpolysiloxane containing no less than two Si-H bonds per molecule, wherein the organohydrogenpolysiloxane is in an amount such that there are 0.8 - 4 hydrogen atoms bonded to silicon atoms per alkenyl group of component (a); and (c) a platinum catalyst in an amount of 5 - 1,000 ppm with respect to 100 parts by weight of the total weight components (a) and (b). A composition as claimed in Claim 1, in which the acrylic resins are the copolymerization product of an acrylic monomer containing alkenyl groups and another polymerizable monomer, the addition reaction product of an acrylic resin containing hydroxyl groups and an alkenyl isocyanate compound and/or a carboxylic acid anhydride containing alkenyl groups, the addition reaction product of an acrylic resin containing isocyanate groups and an alkenylic alcohol, the addition reaction product of an acrylic resin containing carboxyl groups and an epoxy compound containing carboxyl groups and an epoxy compound containing alkenyl groups, and the addition reaction product of an acrylic resin containing epoxy groups and a carboxyclic acid containing alkenyl groups. A composition as claimed in Claim 2, in which the other polymerizable monomer, or the acrylic resin forming the addition product, is a copolymer of an acrylic monomer containing the respective functional groups and an α,β-unsaturated monomer. A composition as claimed in Claim 3, in which at least 50 wt% of the α,β-unsaturated monomer constituting said other polymerizable monomer is acrylic acid, and at least 50 wt% of the α,β-unsaturated acid which is copolymerised with an acrylic monomer containing the respective functional groups is an acrylic monomer without the respective functional groups. A composition as claimed in any preceding claim, in which the number average molecular weight of the acrylic resin and polyester resin of component (a) lies in the range 2,000 - 50,000. A composition as claimed in any preceding claim in which the organohydrogenpolysiloxane of component (b) is represented by one of the following general formulae (I), (II) and (III): wherein R¹ and R² are alkyl groups with 1 - 6 carbon atoms or phenyl a is an integer in the range of 0 ≦ a ≦ 100, and b is an integer in the range 2 ≦ b ≦ 100; wherein R² and R³ are alkyl groups with 1 - 6 carbon atoms or phenyl, c is an integer in the range 0 ≦ c ≦ 8, d is an integer in the range 2 ≦ d ≦ 10, and 3 ≦ c + d ≦ 10; and wherein R¹ and R² are as previously defined, e is an integer in the range 2 ≦ e ≦ 100, and f is an integer in the range 0 ≦ f ≦ 100. A resin product obtained by curing a composition as claimed in any preceding claim.

Inventors: OHGAKI ATSUSHI, OHSUGI HIROHARU, TAKAGAWA RYOZO, TAKARADA MITSUHIRO, YAMAMOTO KENJI, YOSHIKAWA YUJI, OHGAKI, ATSUSHI, OHSUGI, HIROHARU, TAKAGAWA, RYOZO, TAKARADA, MITSUHIRO, YAMAMOTO, KENJI, YOSHIKAWA, YUJI
Applicants: NIPPON PAINT CO LTD, SHINETSU CHEMICAL CO, NIPPON PAINT CO., LTD., SHIN-ETSU CHEMICAL CO., LTD.
Application year: 1991
Main classification: C09D201
IPC codes: C08L33, C09D163, C08L101, C08L83, C08K5, C09D133, C08L63, C08L67, C08G59, C09D183