Functional polyesters from glycidyl derivatives and cyclic anhydrides or carbon dioxide

Abstract: New biodegradable functional polyesters and polycarbonates can be produced by copolymerization of cyclic anhydrides or carbon dioxide with the glycidyl ethers of protected alditols, N-glycidyl pyrrolidone and their mixtures with alkylene oxides in the presence of suitable polymerization catalysts. Such polyesters and polycarbonates are constituted by monomeric residues containing one or more isopropylidene group in the side chain. They can be converted, by partial or complete removal of side chain isopropylidene groups, to the corresponding polymers having two or more free hydroxyl units per structural unit derived from the alditol glycidyl ether. The resulting polyhydroxylated polyesters and polycarbonates are well suited for the production of thermoplastics and thermosets and for the formulation of biodegradable systems to be used in pharmaceutics and biomedicine.

Description: The present invention deals with the synthesis of high molecular weight polyesters and polycarbonates. In particular it is related to the preparation of new bioerodible polymers containing two carboxyl groups per repeating unit. One of these groups is bound throughout an ester bond to a variety of functional hydrophilic or potentially hydrophilic groups, whereas the other one is linked to hydrophobic moieties. The resulting polyhydroxylated polyesters and polycarbonates are well suited for the production of thermoplastics and thermosets and for the formulation of biodegradable systems to be used in pharmaceutics and biomedicine. BACKGROUND ART Polyesters are condensation products characterized by a regular distribution of ester bonds along polymer main chain (Goodman e Rhys, in Polyesters, Vol. I -Saturated polymers, The Plastic Institute, Iliffe Books, London, 1965). Formally, they are produced by esterification of dicarboxylic acids with diols or by self-condensation of hydroxyacids. However, a variety of synthetic procedures to polyesters exists, particularly polyaddition reactions in which monomer molecules react by a chain process. Direct esterification of dicarboxylic acids with diols and self-condensation of hydroxyacids, either in the presence or in the absence of suitable catalysts, are not generally used for large scale application, due to the high reaction temperature, that can give rise to appreciable decomposition of both starting monomers and produced polymer, and the difficult stoichiometric dosage of reagents. This last point applies to all polycondensation reactions and can limit severely the attainment of high molecular weight product. To overcome this problem, a two steps reaction scheme can be applied, implying the prior formation of a dihydroxy-diester by reaction of the diacid with two equivalents of the diol, followed by a polycondensation reaction in which a diol molecule is eliminated at each condensation step. In order to attain high molecular weights, the by-product formed must be removed from the reactor. However, better results are generally obtained by replacing carboxylic diacids with dialkyl or diaryl esters, that can be more easily purified and have a larger reactivity. Analogously, polycarbonates can be produced by reacting diols with diesters of carbonic acid, whereas hydroxyesters are more convenient than hydroxy acids in the self-condensation reaction. Also in the case of diesters better results are attained by a two step process in which the polymerizable intermediate is again a dihydroxy-diester. Dicarboxylic acids and diols can be conveniently replaced by the corresponding acid dichlorides and dialkyl carbonates, respectively. Polyesters can be formed also by polyaddition reactions. The most important one is the polymerization of lactones or lactides, that under mild conditions give rise to the same polymeric product in principle attainable by self-condensation of the corresponding hydroxyacid. Other possible routes are based on the alternating copolymerization of cyclic anhydrides with cyclic ethers, such as epoxides and tetrahydrofuran, of dicarboxylic acids with diol divinyl ethers, and of diols with bisketenes. These last can be copolymerized also with aldehydes, ketones, and formates. Some polyesters, such as poly( ε-caprolactone), poly(orthoester)s and copolymers of glycidic acid with lactic acid have been accepted by competent authorities (as FDA) for applications in biomedicine and in the food industry, due to their biocompatibility and biodegradability to non toxic products. The large amount of reports on the degradation of polyesters and their structural analogues has been reviewed by several authors (Reed e Gilding, Polymer, 22, 494, 1981; Jarret et al., in Polymers as biomaterials, Plenum Press, New York, 1984, p. 181; Heller, J. Controlled Release, 2, 167, 1985; Holland et al., J. Controlled Release, 4, 155, 1987; Pitt e Gu, J. Controlled Release, 4, 283, 1987; St.Pierre e Chiellini, J. Bioact. Compat. Polym., 2, 4, 1987). However, only few examples have been reported on polyfunctional synthetic polyesters that due to the presence of hydrophilic substituents are water soluble and therefore well suited to undergo chemical and biochemical degradation processes (Vert e Lenz, U.S. Pat. 4.265.247, Lug. 1981; Braud et al., Polym. Bull., 13,293, 1985, Chiellini et al., J. Bioact. Compat. Polym., 5, 15, 1990). On the other hand, aliphatic polycarbonates have not received much attention, due to their rather low mechanical properties (Carothers e Natta, J. Am. Chem. Soc., 52, 314, 1930). and only the reaction product of allyl alcohol with diethylen chloroformate has received some interest (Watanabe, The chemistry of commercial plastics, Reinhold Pub. Co., New York, 1947). Even though the production of poly(alkyl carbonates) by catalyzed reaction of diols with carbon monoxide is known (US Pat. 4.131.152), the only practical pathway to aliphatic polycarbonates is the method based on the reaction of epoxides with carbon dioxide in the presence of suitable catalysts (Contemporary Topcs in Polymer Science, W.J. Bailey, T. Tsuruta, Eds., Plenum Press, New York, 1984, p. 343). At the present, none of the above materials has found applications in biomedicine or pharmaceutics, mainly due to their hydrophobicity. However, functional polycarbonates should have superior properties for biomedical use. Moreover, even if several polymers have been investigated for the controlled release of drugs, the results obtained are not satisfactory and require for the use of new materials. In this respect, the polycarbonates that are the subject of the present invention appear to be useful due to their large and modulable hydrophilicity and also because they give rise only to natural biodegradation products, such as carbon dioxide and polyols, that are not toxic and can be easily degraded by the human body. DISCLOSURE OF INVENTION The present invention describes new biodegradable functional polyesters and polycarbonates having the following formula: where: R1 is either H, or alkyl, or 1-(2-pyrrolidonyl) alkoxymethyl, or 1-(2- pyrrolidonyl)alkyl; R2 is either H, or alkyl, or aryl; Z is either -CO-R3- residue where R3 is linear or branched alkanediyl or arylalkanediyl or arylenediyl, or is substituted by a carbon-oxygen bond; Y is either glyceryl, or pentitolyl, or heptitolyl; 0 < x ≤ 1; 5 < m < 500. to be used as thermoplastic and thermoset materials and as biodegradable matrices in the controlled release of active principles of biomedical, pharmaceutical and agricultural interest. Due to the presence in the side chain of vicinal hydroxyl groups, their use as heavy metal sequestrants is also possible. According to the invention, a process of production is described by copolymerization of the glycidyl ethers of alditols (having preferably but not exclusively three, five, and seven carbon atoms) protected with isopropylidene groups and their mixtures with alkylene oxides (preferably but not exclusively ethylene oxide and propylene oxide) with either cyclic anhydrided (at 30-150C) or with carbon dioxide (at 30-60C) in the presence of different catalysts, preferably but not exclusively alkylaluminum derivatives in the first case and dialkylzinc/polyhydroxyphenols systems in the second one. The hydrophilicity of the polymeric materials thus obtained, having molecular weight included between 1000 and 100.000, preferably between 2.000 and 30,000, can be modulated by controlled removal, either partial or total, of isopropylidene protecting groups. This reaction is promoted by low and high molecular weight acid catalysts and does not appreciably affect the degree of polymerization of the reacted polymers. Removal of the isopropylidene protecting groups can be carried out by precipitation of the protected polyesters and polycarbonates in methanol containing 5% of concentrated HCl. Alternatively the deprotection reaction can be performed by heating a polymer solution in methanol/chloroform mixtures in the presence of a styrene/divinylbenzene sulphonic resin. Accordingly, it is possible to attain a large number of polyesters and polycarbonates characterized by a different content of hydroxyl groups in the side chains and having a molecular weight included between 800 and 80,000, preferably between 2.000-25.000. DETAILED DESCRIPTION OF THE INVENTION In the following examples detailed description of the preparation of the polyesters of the invention are provided, including also the preparation of glycidyl derivatives. Preparation of Glycidic Monomers Example 1 1-O-Glycidyl-2,3-O-isopropylideneglycerol GIG A suspension of 11.0 g (0,46 mol) of NaH in 600 ml of anhydrous THF was placed under dry nitrogen in a 3-necked 1000 ml flask, equipped with condenser, dropping funnel and mechanical stirrer. Then 50 ml (0.38 mol) of (R),(S)-isopropylideneglycerol (Solketal) were added over 1.5 h under stirring and then refluxed for 3 h. 400 ml (25 mol) of the resulting suspension was added under dry nitrogen over 3 h to 70 ml (0.90 mol) of epichlorohydrin (EPY) in a 3-necked 1000 ml flask, equipped with condenser, dropping funnel and mechanical stirrer. The mixture was stirred overnight at room temperature and then refluxed for 6 h. After cooling, the solid was filtered off. The resulting solution, after removal of the volatile products, was distilled under vacuum over calcium hydride to yield 33.6 g (71%) of a colourless liquid having b.p. 76°C/0.2 mm that was characterized by IR and NMR spectroscopy. IR (liquid film): ν = 3040 (ν CH epoxide), 3000.2800 (ν CH aliphatic), 1456 (δ CH 2 and δ as CH 3 ), 1380 (δ CH 3 ), 1250-1040 (ν C-O-C epoxide ed ether), 904 (ν C-O-C epoxide) and 844 cm -1 (ν epoxide and dioxolane ring). 1 H-NMR (CDCl 3 ): δ = 1.3 and 1.4 (two s, 6H, CH 3 ), 2.6 (m, 1H, CH-9a), 2.8 (dd, 1H, CH-9b), 3.2 (m, 1H, CH-8), 3.4-3.9 (m, 5H. CH 2 and CH-3a), 4.1 (d.d., 1H, CH-3b) and 4.3 ppm (m, 1H, CH-2). 13 C-NMR (CDCl 3 ): δ = 24.87 (C-5), 26.23 (C-6), 43.53 (C-9), 50.23 (C-8), 66.21 (C-7), 71.82, 71.94 and 72.06 (C-1 + C-3), 74.29 and 74.37 (C-2) and 109.11 ppm (C-4). Example 2 1-0-Glycidyl-2,3-0-isopropylideneglycerol GIG A solution of 30.0 g (227 mmol) of solketal and 7.4 g (2.3 mmol) of tetrabutylammonium bromide (TBAB) in 90 ml of toluene was added to 100 ml of 50% NaOH water solution in a 3-necked 500 ml flask, equipped with condenser, dropping funnel and mechanical stirrer. The mixture was stirred at room temperature for 1 h, then 35 ml (0.448 mol) of EPY were added under stirring. The resulting suspension was stirred for additional 26 h, then the organic layer was dried over MgSO4. After removal of the volatile products, the residue was distilled under vacuum over calcium hydride to yield 34.3 g (80%) of colourless liquid having b.p. 76°C/0.2 mm that was characterized by IR and NMR spectroscopy. Example 3 0-Glycidyl-di-0-isopropylidenexylitol XPG A suspension of 110 g of ZnCl 2 in 1.0 l of acetone was stirred for 3 h at room temperature and then left standing overnight. The surnatant was transferred under dry nitrogen into a 2000 ml two-necked flask equipped with mechanical stirrer, then 80.0 g (0.53 mol) of xylitol were added and the reaction mixture was kept under stirring for 17 h. The resulting solution was poured into a 2000 ml flask and 2.01 of 20% NaOH water solution were slowly added. The organic layer was evaporated under vaccum, the residue was dissolved in diethyl ether and filtered. After removal of the volatile products, the oily residue was distilled under vacuum to yield 95.1 g (78%) of a viscous liquid having b.p. 108-113°C/0.2 mm and constituted by a 12:1:8 mixture of three products, as shown by g.l.c. analysis. The mixture was characterized also by IR and NMR spectroscopy. A solution of 77.0 g (0.332 mol) of di-0-isopropylidenexylitol and 10.6 g (33 mmol) of tetrabutylammonium bromide in 200 ml of toluene was added to 250 ml of a 50% NaOH water solution in a 1 l three-necked flask equipped with condenser, dropping funnel and mechanical stirrer. The mixture was stirred at room temperature for 1 h, then 55 ml (0.70 mol) of EPY were added under stirring. The resulting suspension was stirred for additional 28 h, then the organic layer was dried over Na 2 SO 4 . After removal of the volatile products, the residue was distilled under vacuum over calcium hydride to yield 83.7 g (87%) of colourless liquid having b.p. 150-153°C/0.5 mm and constituted by a 2:1 mixture of two isomers, as shown by g.l.c. analysis. The mixture was characterized also by IR and NMR spectroscopy. IR (liquid film): ν = 3052 (ν CH epoxide), 3000-2800 (ν CH aliphatic),1456 (δ CH 2 and δ as CH 3 ), 1380 (δ s CH 3 ), 1250-1040 (ν C-O-C), 904 (ν C-O-C epoxide) and 844 cm -1 (epoxide and dioxolane ring). 1 H-NMR (CDCl 3 ): δ = 1.2-1.4 (m, 12H, CH 3 ), 2.5 and 2.7 (two m, 2H, CH 2 epoxide), 3.1 (m, 1H, CH epoxide) and 3.3-4.2 ppm (m, 7H, CH 2 and CH). 13 C-NMR (CDCl 3 ): δ = 25-27 (CH 3 ), 43.5-44.5 (CH epoxide), 50-51 (CH 2 epoxide), 65-81 (CH-O + CH 2 -O) and 109-110 ppm (O-C-O). Example 4 L-O-Glycidyl-di-O-isopropylidenearabitol APG A suspension of 50 g of ZnCl 2 in 400 ml of acetone was stirred for 3 h at room temperature and then left standing overnight. The surnatant was transferred under dry nitrogen into a 2000 ml two-necked flask equipped with mechanical stirrer, then 25.0 g (0.164 mol) of L-arabitol were added and the reaction mixture was kept under stirring for 17 h. The resulting solution was poured into a 2000 ml flask and 800 ml of a 20% NaOH water solution were slowly added. The organic layer was evaporated under vacuum, the residue was dissolved in diethyl ether and filtered. After removal of the volatile products, the oily residue was distilled under vacuum to yield 23.6 g (69%) of a viscous liquid having b.p. 92-94°C/0.1 mm and constituted by a 20:10:1 mixture of three isomers, as shown by g.l.c. analysis. The mixture was characterized also by IR and NMR spectroscopy. A solution of 23.0 g (99 mmol) of L-di-O-isopropylidenearabitol and 3.2 g (9.9 mmol) of tetrabutylammonium bromide in 60 ml of toluene was added to 110 ml of a 50% NaOH water solution in a 500 ml three-necked flask equipped with condenser, dropping funnel and mechanical stirrer. The mixture was stirred at room temperature for 1 h, then 18.5 ml (0.20 mol) of EPY were added under stirring. The resulting suspension was stirred for additional 42 h, then the organic layer was dried over Na 2 SO 4 . After removal of the volatile products, the residue was distilled under vacuum over calcium hydride to yield 23.0 g (81%) of colourless liquid having b.p. 110-115°C/0.1 mm that gave only one broad peak at the g.l.c. analysis. The mixture was characterized by IR and NMR spectroscopy. IR (liquid film): ν = 3052 (ν CH epoxide), 3000-2800 (ν CH aliphatic), 1458 (δ CH 2 and δ as CH 3 ), 1376 (δ s CH 3 ), 1250-1040 (ν C-O-C), 910 (ν C-O-C epoxide) and 848 cm -1 (ν epoxide and dioxolane rings). 1 H-NMR (CDCl 3 ): δ = 1.2-1.4 (m, 12H, CH 3 ), 2.5 and 2.7 (two m, 2H, CH 2 epoxide), 3.1 (m, 1H, CH epoxide) and 3.3-4.1 ppm (m, 7H, CH 2 and CH). 13 C-NMR (CDCl 3 ): δ = 25-27 (CH 3 ), 43.5-44.5 (CH epoxide),50-51 (CH 2 epoxide), 65-82 (CH-O + CH 2 -O) and 108.5-110 ppm (O-C-O). Example 5 N-Glycidylpyrrolidone NGP A suspension of 21.1 g (0.54 mol) of potassium in 150 ml of anhydrous benzene was placed under dry nitrogen atmosphere in a 500 ml three-necked flask equipped with condenser, dropping funnel and mechanical stirrer, then a solution of 50.6 g (0.58 mol) of 2-pyrrolidone in 110 ml of anhydrous benzene was slowly added under vigorous stirring. The mixture was kept under stirring at room temperature for 3 days and at 40°C one day. The solid product was then filtered, repeatedly washed with anhydrous benzene, and dried under vaccum to yield 65.0 g (98%) of a white hygroscopic powder. A suspension of 69.0 g (.53 mol) of the potassium salt of pyrrolidone in 300 ml of anhydrous THF was slowly added under stirring to 124.0 g (1.35 mol) of epichlorohydrine placed in a 500 ml three-necked flask equipped with condenser and dropping funnel, under dry nitrogen atmosphere. The reaction mixture was heated at reflux for 6 h and then left overnight at room temperature. The solid residue was filtered off, washed with THF and the organic fractions, after removal of the volatile products, were distilled under vacuum to yield 38.5 g (52%) of a colourless liquid having b.p. 97-100°C/0.3 mm. The product was stirred for 3 days at room temperature over CaH 2 . then distilled again (p.b. 95-96°C/0.2 mm) and analyzed by IR and NMR spectroscopy. IR (liquid film): ν = 3050 (ν CH epoxide), 3000-2850 (ν CH aliphatic), 1680 (ν C=O), 1500-1400 (δ CH 2 and ν lactame ring), 1280 (ν C-O-C and ν lactame ring), 850 cm -1 (epoxide ring). 1 H-NMR (CDCl 3 ): δ = 2.0 (m, 2H, CH 2 -5), 2.4 (t, 2H, CH 2 -6), 2.5 (two d, 1H, CH-1b), 2.7 (m, 1H, CH-1a), 3.1 (m, 2H, CH-2c + CH-3e), 3.5 (m, 2H, CH 2 -4) and 3.8 ppm (two d, 1H, CH-3d). 13 C-NMR (CDCl 3 ): δ = 18.1 (C-5), 30.7 (C-6), 44.7 (C-1), 44.8 (C-4), 48-4 (C-3), 50.2, (C-2) and 175.6 ppm (C-7). Preparation of polymerization catalyst Example 6 Mesotetraphenylporfinealuminum chloride/tetrabutylammonium bromide TTPAC/TBAB In a 3000 ml three necked flask equipped with condenser and two dropping funnel, propanoic acid (2 l) was heated at reflux then 54.1 g (800 mmol) of pyrrole and 83.5 g (800 mmol) of benzaldehyde were added at the same time under dry nitrogen atmosphere. After 30 min, the mixture was cooled down to room temperature and filtered. The solid was washed with methanol, hot water and finally dried under vacuum to yield 25.0 g (20%) of violet crystals A solution of 1.23 g (2.0 mmol) of mesotetraphenylporfine in 40 ml of anhydrous dichloromethane was placed under dry nitrogen atmosphere in a 100 ml three necked flask equipped with condenser, dropping funnel and magnetic stirrer, then a solution of 0.29 g (2.4 mmol) of diethylaluminum chloride in 5 ml of anhydrous dichloromethane was slowly added under vigorous stirring. The stirring was continued for 2 h at room temperature, then the solvent was removed and the blue-green solid residue was dissolved in 40 ml of anhydrous dichloromethane. Finally, 0.16 g (0.5 mmol) of tetrabutylammonium bromide was added under vigorous stirring to 10 ml of this solution (corresponding to 0.5 mmol of mesotetraphenylporfinealuminum chloride). The resulting solution was used as a polymerization catalyst immediately after the preparation. Example 7 Diisobutylzinc/pyrogallol DBZ/Pg A solution of 1.61 g (9.0 mmol) of DBZ in 20 ml anhydrous dioxane was placed under dry nitrogen atmosphere in a 50 ml three necked flask equipped with condenser, dropping funnel and magnetic stirrer, then a solution of 0.55 g (4.4 mmol) of pyrogallol in 15 ml of dioxane was slowly added and the mixture was kept under stirring at 45°C for 2 h. The resulting clear solution was used as a polymerization catalyst immediately after the preparation. Example 8 Amberlyst A27 resin, Br- form A27Br Commercial Amberlyst A27 resin (strong anionic type ion exchange resin, exchange capacity 2.6 meq/g) was left for 36 h under slow stirring in 10% sodium bromide aqueous solution. Every 12 h the bromide solution was replaced by a fresh one, then the resin was filtered, washed with water/ethanol mixtures containing 0,50,70,95 and 100% ethanol and finally dried under vacuum. Copolymerization of epoxydes with different anhydrides with different catalyst Example 9 Copolymer of 1-0-glycidyl-2.3-0-isopropyli deneglycerol (GIG) with succinic anhydride. A solution of 3.0 g (16 mmol) of GIG and 1.6 g (16 mmol) of succinic anhydride in 40 ml of anhydrous toluene containing 0.8 ml (0.6 mmol) of bis(diethylaluminum) sulphate solution was placed under dry nitrogen atmosphere in a 100 ml glass vial. The vial was sealed and then kept at 80°C for 48 h. The resulting solution was filtered and the solvent removed under vacuum to yield 4.5 g (conv. 98%) of polymeric product that was characterized by GPC, IR and NMR analysis. An equimolar amount of both monomeric units was detected in the copolymer by 1H-NMR. IR (film): ν = 3000-2800 (ν CH aliphatic), 1740 (ν C=O), 1458 (δ CH 2 and δ as CH 3 ), 1374 (δ s CH 3 ) and 1300-1000 cm -1 (ν C-O-C). 1 H-NMR (CDCl 3 ): δ = 1.2-1.4 (two s, 6H, CH 3 ), 2.6 (s, 4H, CH 2 AS), 3.0-4.5 (m, 9H, CH-O + CH 2 -O + CH 2 -OOC) and 5.1 ppm (s, 1H, CH-OOC). 13 C-NMR (CDCl 3 ): δ = 25.09 and 26.43 (CH 3 ), 28-29 (CH 2 AS), 62-75 (CH-O + CH 2 -O), 109.40 (O-C-O) and 171.5-174ppm (C=O). Example 10 Copolymer of 1-0-glycidyl-2.3-0-isopropylideneglycerol with succinic anhydride. A solution of 3.0 g (16 mmol) of GIG and 1.6 g (16 mmol) of succinic anhydride in 50 ml of anhydrous o-xylene containing 0.8 mmol of TBAB was placed under dry nitrogen atmosphere in a 100 ml glass vial. The vial was sealed and then kept at 120°C for 6 h. The resulting solution was filtered and the solvent removed under vacuum to yield 2.2 g (conv. 48%) of polymeric product that was characterized by GPC, IR and NMR analysis. An equimolar amount of both monomeric units was detected in the copolymer by 1H-NMR. Example 11 Copolymer of 1-0-glycidyl-2.3-0-isopropylideneglycerol with succinic anhydride. A solution of 3.0 g (16 mmol) of GIG and 1.6 g (16 mmol) of succinic anhydride in 45 ml of anhydrous o-xylene containing 0.8 mmol of tributylamine was placed under dry nitrogen atmosphere in a 100 ml glass vial. The vial was sealed and then kept at 90°C for 24 h. The resulting solution was filtered and the solvent removed under vacuum to yield 1.5 g (conv. 33%) of polymeric product that was characterized by GPC, IR and NMR analysis. An equimolar amount of both monomeric units was detected in the copolymer by 1H-NMR. Example 12 Copolymer of 1-0-glycidyl-2.3-0-isopropylideneglycerol with succinic anhydride. A solution of 3.0 g (16 mmol) of GIG and 1.6 g (16 mmol) of succinic anhydride in 40 ml of anhydrous o-xylene containing 0.8 mmol of A27Br resin was placed under dry nitrogen atmosphere in a 100 ml glass vial. The vial was sealed and then kept at 70°C for 40 h. The resulting solution was filtered and the solvent removed under vacuum to yield 2.0 g (conv. 43%) of polymeric product that was characterized by GPC, IR and NMR analysis. An equimolar amount of both monomeric units was detected in the copolymer by 1H-NMR. Example 13 Copolymer of 1-0-glycidyl-2.3-0-isopropylideneglycerol with succinic anhydride. A solution of 3.0 g (16 mmol) of GIG and 1.6 g (16 mmol) of succinic anhydride in 40 ml of anhydrous toluene containing 0.8 mmol of triisobutylaluminum was placed under dry nitrogen atmosphere in a 100 ml glass vial. The vial was sealed and then kept at 80°C for 48 h. The resulting solution was filtered and the solvent removed under vacuum to yield 4.5 g (conv. 98%) of polymeric product that was characterized by IR and NMR spectroscopy. An equimolar amount of both monomeric units was detected in the copolymer by 1H-NMR. Example 14 Copolymer of 1-0-glycidyl-2.3-0-isopropylideneglycerol with succinic anhydride A solution of 3.0 g (16 mmol) of GIG and 1.6 g (16 mmol) of succinic anhydride in 40 ml of anhydrous toluene containing 0.8 mmol of hexaisobutyltetraalumoxane was placed under dry nitrogen atmosphere in a 100 ml glass vial. The vial was sealed and then kept at 80°C for 48 h. The resulting solution was filtered and the solvent removed under vacuum to yield 4.5 g (conv. 98%) of polymeric product that was characterized by GPC, IR and NMR analysis. An equimolar amount of both monomeric units was detected in the copolymer by 1H-NMR. Example 15 Copolymer of 0-glycidyl-di-0-isopropylidenexylitol with succinic anhydride. A solution of 4.6 g (16 mmol) of XPG and 1.6 g (16 mmol) of succinic anhydride in 35 ml of anhydrous toluene containing 0.8 mmol of triisobutylaluminum was placed under dry nitrogen atmosphere in a 100 ml glass vial. The vial was sealed and then kept at 80°C for 62 h. The resulting solution was filtered and the solvent removed under vacuum to yield 5.9 g (conv. 96%) of polymeric product that was characterized by GPC, IR and NMR analysis. An equimolar amount of both monomeric units was detected in the copolymer by 1H-NMR. IR (film): ν = 3000-2800 (ν CH aliphatic), 1740 (ν C=O), 1458 (δ CH 2 and δ as CH 3 ). 1376 (δ s CH 3 ) and 1300-1000 cm -1 (ν C-O-C). 1 H-NMR (CDCl 3 ): δ = 1.2-1.4 (m, 12H, CH 3 ), 2.6 (s, 4H, CH 2 AS), 3.2-4.4 (m, 11H, CH-O + CH 2 -O + CH 2 -OOC) and 5.1 ppm (s, 1H, CH-OOC). 13 C-NMR (CDCl 3 ): δ = 25-27 (CH 3 ), 28-29 (CH 2 AS), 62-82 (CH-O + CH 2 -O), 109-110 (O-C-O) and 171.5-172.5 ppm (C=O). Example 16 Copolymer of L-0-glycidyl-di-0-isopropylidenearabitol (APG) with succinic anhydride. A solution of 4.6 g (16 mmol) of APG and 1.6 g (16 mmol) of succinic anhydride in 35 ml of anhydrous toluene containing 0.8 mmol of triisobutylaluminum was placed under dry nitrogen atmosphere in a 100 ml glass vial. The vial was sealed and then kept at 80°C for 62 h. The resulting solution was filtered and the solvent removed under vacuum to yield 6.0 g (conv. 97%) of polymeric product that was characterized by GPC, IR and NMR analysis. An equimolar amount of both monomeric units was detected in the copolymer by 1H-NMR. IR (film): ν = 3000-2800 (ν CH aliphatic), 1740 (ν C=O), 1458 (δ CH 2 and δ as CH 3 ), 1376 (δ s CH 3 ) and 1300-1000 cm -1 (ν C-O-C). 1 H-NMR (CDCl 3 ): δ = 1.2-1.4 (m, 12H, CH 3 ), 2.6 (s, 4H, CH 2 AS), 3.2-4.4 (m, 11H. CH-O + CH 2 -O + CH 2 -OOC) and 5.1 ppm (s, 1H, CH-OOC). 13 C-NMR (CDCl 3 ): δ = 24-27 (CH 3 ), 28-29 (CH 2 AS), 62-82 (CH-O + CH 2 -O), 109-110 (O-C-O) and 171.5-172.5 ppm (C=O). Example 17 Copolymer of N-glycidylpyrrolidone with succinic anhydride. A solution of 2.0 g (16 mmol) of NPG and 1.6 g (16 mmol) of succinic anhydride in 35 ml of anhydrous toluene containing 0.8 mmol of triisobutylaluminum was placed under dry nitrogen atmosphere in a 100 ml glass vial. The vial was sealed and then kept at 80C for 62 h. The resulting mixture was dissolved in chloroform and poured into excess diethyl ether. The coagulated polymer was dried under vacuum to yield 3.4 g (conv. 95%) of polymeric product that was characterized by GPC, IR and NMR analysis. An equimolar amount of both monomeric units was detected in the copolymer by 1H-NMR. IR (film): ν = 3000-2800 (ν CH aliphatic), 1738 (ν C=O ester), 1688 (ν C=O lactame), 1464 (δ CH 2 and δ as CH 3 ), 1378 (δ s CH 3 ) and 1300-1000 cm -1 (ν C-O-C and ν C-N). 1 H-NMR (CDCl 3 ): δ = 2.0 (m, 2H, CH 2 ), 2.3 (t, 2H, CH 2 -C=O), 2.6 (s, 4H, CH 2 AS), 3.0-3.9(m, 4H, CH 2 -N), 4.0-4.3 (m, 2H, CH 2 -O) and 5.2 ppm (m, 1H, CH-O). 13 C-NMR (CDCl 3 ): δ = 17.76 (C-9), 28.45 (C-2 + C-3), 30.24 (C-10), 42.76 (C-8), 47.89 (C-7 ), 63.10 (C-5), 69.29 (C-6), 171.25 and 171.92 (C-1 + C-4) and 175.95 ppm (C-11). Example 18 Terpolymer of 1-0-glycidyl-2.3-0-isopropyli deneglycerol with propylene oxide (PO) and carbon dioxide. A solution of 1.7 g (29 mmol) of PO and 5.9 g (31.3 mmol) of GIG in 21 ml (1.2 mmol) of the DBZ/Pg dioxane solution was placed under dry nitrogen atmosphere in a 150 ml stainless steel pressure vessel that was filled with carbon dioxide up to 40 atm. The polymerization mixture was kept under stirring for 52 h at 35°C. The orange solid obtained was dissolved in chloroform, washed with 5% NH 4 Cl, water and water in that order and finally poured into a large excess of methanol. The coagulated polymer was dried under vacuum to yield 1.2 g (conv. 12%) of polymeric product that was characterized by GPC, IR and NMR analysis. A 40% molar content of GIG units was detected in the copolymer by 1H-NMR. IR (film): ν = 3000-2800 (ν CH aliphatic), 1748 (ν C=O), 1456 (δ CH 2 and δ as CH 3 ), 1380 (δ s CH 3 ) and 1300-1000 cm -1 (ν C-O-C). 1 H-NMR (CDCl 3 ): δ = 1.2-1.5 (CH 3 ), 3.5 and 3.7 (5H GIG), 4.2 (2H PO and 4H GIG) and 5.0 ppm (1H GIG and 1H PO). 13 C-NMR (CDCl 3 ): δ = 16.03 (CH 3 PO), 25.24 and 26.57 (CH 3 GIG), 65.5-75 (CH-O + CH 2 -O), 109.52 (O-C-O) and 153.5-155.5 ppm (C=O). Example 19 Terpolymer of 1-0-glycidyl-2.3-0-isopropylideneglycerol with propylene oxide and carbon dioxide. A solution of 8.7 g (150 mmol) of PO and 14.5 g (77 mmol) of GIG in 21 ml (5.8 mmol) of the DBZ/Pg dioxane solution was placed under dry nitrogen atmosphere in a 150 ml stainless steel pressure vessel that was filled with carbon dioxide up to 40 atm. The polymerization mixture was kept under stirring for 85 h at 35°C. The orange solid obtained was dissolved in chloroform, washed with 5% NH 4 Cl, water and water in that order and finally poured into a large excess of methanol. The coagulated polymer was dried under vacuum to yield 6.2 g (conv. 19%) of polymeric product that was characterized by GPC, IR and NMR analysis. A 25% molar content of GIG units was detected in the copolymer by 1H-NMR. Example 20 Terpolymer of 1-O-glycidyl-2.3-O-isopropylideneglycerol with propylene oxide and carbon dioxide. A solution of 7.0 g (120 mmol) of PO and 5.2 g (27.4 mmol) of GIG in 21 ml (5.8 mmol) of the DBZ/Pg dioxane solution was placed under dry nitrogen atmosphere in a 150 ml stainless steel pressure vessel that was filled with carbon dioxide up to 40 atm. The polymerization mixture was kept under stirring for 64 h at 35°C. The orange solid obtained was dissolved in chloroform, washed with 5% NH 4 Cl, water and water in that order and finally poured into a large excess of methanol. The coagulated polymer was dried under vacuum to yield 3.3 g (conv. 17%) of polymeric product that was characterized by GPC, IR and NMR analysis. A 15% molar content of GIG units was detected in the copolymer by 1H-NMR. Example 21 Terpolymer of 0-glycidyl-di-0-isopropylidenexylitol with propylene oxide and carbon dioxide A solution of 2.3 g (40 mmol) of PO and 3.4 g (12 mmol) of XPG in 7.5 ml (1.8 mmol) of the DBZ/Pg dioxane solution was placed under dry nitrogen atmosphere in a 150 ml stainless steel pressure vessel that was filled with carbon dioxide up to 40 atm. The polymerization mixture was kept under stirring for 90 h at 35°C. The orange solid obtained was dissolved in chloroform. washed with 5% NH 4 Cl, water and water in that order and finally poured into a large excess of methanol. The coagulated polymer was dried under vacuum to yield 1.4 g (conv. 18%) of polymeric product that was characterized by GPC, IR and NMR analysis. A 7% molar content of XPG units was detected in the copolymer by 1H-NMR. IR (film): ν = 3000-2800 (ν CH aliphatic), 1746 (ν C=O), 1458(δ CH 2 and δ as CH 3 ), 1380 (δ s CH 3 ) and 1300-1000 cm -1 (ν C-O-C). 1 H-NMR (CDCl 3 ):δ = 1.2-1.4 (CH 3 ), 3.4-4.4 (11H XPG and 2H PO) and 5.0 ppm (1H XPG and 1H PO). 13 C-NMR (CDCl 3 ): δ = 15,93 (CH 3 PO), 25-27 (CH 3 XPG), 65.5-81.3 Example 22 Terpolymer of 0-glycidyl-di-0-isopropylidenexylitol with propylene oxide and carbon dioxide . A solution of 1.5 g (26 mmol) of PO and 7.7 g (27 mmol) of XPG in 7.5 ml (1.8 mmol) of the DBZ/Pg dioxane solution was placed under dry nitrogen atmosphere in a 150 ml stainless steel pressure vessel that was filled with carbon dioxide up to 40 atm. The polymerization mixture was kept under stirring for 90 h at 35°C. The orange solid obtained was dissolved in chloroform, washed with 5% NH 4 Cl, water and water in that order and finally poured into a large excess of methanol. The coagulated polymer was dried under vacuum to yield 0.8 g (conv. 7%) of polymeric product that was characterized by GPC, IR and NMR analysis. A 8% molar content of XPG units was detected in the copolymer by 1H-NMR. Example 23 Terpolymer of 0-glycidyl-di-0-isopropylidenexylitol with propylene oxide and carbon dioxide. A solution of 1.4 g (24 mmol) of PO and 7.0 g (24 mmol) of XPG in 7.5 ml (1.8 mmol) of the DBZ/Pg dioxane solution was placed under dry nitrogen atmosphere in a 150 ml stainless steel pressure vessel that was filled with carbon dioxide up to 40 atm. The polymerization mixture was kept under stirring for 95 h at 35°C. The orange solid obtained was dissolved in chloroform, washed with 5% NH 4 Cl, water and water in that order and finally poured into a large excess of methanol. The coagulated polymer was dried under vacuum to yield 0.8 g (conv. 8%) of polymeric product that was characterized by GPC, IR and NMR analysis. A 7% molar content of XPG units was detected in the copolymer by 1H-NMR. Reaction of deprotection Example 24 Copolymer of 1-0-glycidylglycerol with succinic anhydride . A solution of 2.5 g of GIG/SA copolymer in a mixture of 80 ml of methanol and 100 ml of chloroform was placed under dry nitrogen in a 250 ml two necked flask equipped with condenser and magnetic stirring. After addition of 2.5 g of Amberlyst 15, the mixture was kept under stirring at 45°C for 64 h, then the resin was filtered off and the volatile products removed under vacuum to yield 1.9 g of a semisolid product that was characterized by GPC, IR and NMR analysis. IR (film): ν = 3600-3100 (ν O-H), 3000-2800 (ν CH aliphatic), 1740 (ν C=O), 1464 (δ CH 2 and δ as CH 3 ), 1378 (δ s CH 3 ), 1300-1000 (ν C-O-C) and 800-400 cm -1 (δ O-H). 1 H-NMR (CDCl 3 ): δ = 2.7 (m, CH 2 AS), 3.5-4.4 (m, CH-O + CH 2 -O) and 4.9 ppm (s, OH). 13 C-NMR (CDCl 3 ): δ = 25.09 and 26.43 (CH 3 ), 29.5-30.5 (CH 2 AS), 52-75.5 (CH-O + CH 2 -O) and 173.5-175 ppm (C=O). Example 25 Copolymer of 0-glycidylxylitol with succinic anhydride . A solution of 2.5 g of XPG/SA copolymer in a mixture of 80 ml of methanol and 80 ml of chloroform was placed under dry nitrogen in a 290 ml two necked flask equipped with condenser and magnetic stirring. After addition of 2.5 g of Amberlyst 15, the mixture was kept under stirring at 45°C for 64 h, then the resin was filtered off and the volatile products removed under vacuum to yield 1.9 g of a semisolid product that was characterized by GPC, IR and NMR analysis. IR (film): ν = 3600-3100 (ν O-H), 3000-2800 (ν CH aliphatic), 1740 (ν C=O), 1464 (δ CH 2 and δ as , CH 3 ), 1378 (δ s CH 3 ), 1300-1000 (ν C-O-C) and 800-400 cm -1 (δ O-H). 1 H-NMR (CDCl 3 ): δ = 2.7 (m, CH 2 AS), 3.5-4.4 (m, CH-O+CH 2 -O) and 4.9 ppm (s, OH). 13 C-NMR (CD 3 OD): δ =29-30.5 (CH 2 AS), 60-83 (CH-O+CH 2 -O) and 173-175 ppm (C=O). Example 26 Copolymer of 0-glycidylarabitol with succinic anhydride . A solution of 2.0 g of APG/SA copolymer in a mixture of 70 ml of methanol and 70 ml of chloroform was placed under dry nitrogen in a 250 ml two necked flask equipped with condenser and magnetic stirring. After addition of 2.0 g of Amberlyst 15, the mixture was kept under stirring at 45C for 64 h, then the resin was filtered off and the volatile products removed under vacuum to yield 1.5 g of a semisolid product that was characterized by GPC, IR and NMR analysis. IR (film): ν = 3600-3100 (ν O-H), 3000-2800 (ν CH aliphatic), 1740 (ν C=O), 1464 (δ CH 2 and δ as CH 3 ), 1378 (δ s CH 3 ), 1300-1000 (ν C-O-C) and 800-400 cm -1 (δ O-H). 1 H-NMR (CDCl 3 ): δ = 2.7 (m, CH 2 AS), 3.5-4.4 (m, CH-O + CH 2 -O) and 4.9 ppm (s, OH). 13 C-NMR (CD 3 OD): δ=29-30.5 (CH 2 AS), 61-82 (CH-O+CH 2 -O) and 173-175 ppm (C=O). Example 27 Terpolymer of 1-0-glycidylglycerol with propylene oxide and carbon dioxide . A solution of 2.0 g of GIG/PO/CO2 terpolymer containing 15%-mol of GIG units in 70 ml of dichloromethane was poured under vigorous stirring in 300 ml of 20:1 methanol/concentrated HCl mixture and left under stirring for 2 h. The coagulated polymer was then washed with methanol, dissolved in chloroform, precipitated in diethyl ether and finally dried under vacuum to yield 2.9 g of a white powder that was characterized by GPC, IR and NMR analysis. IR (film): ν = 3600-3100 (ν O-H), 3000-2800 (ν CH aliphatic), 1740 (ν C=O), 1464 (δ CH 2 and δ as CH 3 ), 1378 (δ s CH 3 ), 1300-1000 (ν C-O-C) and 800-400 cm -1 (δ O-H). 1 H-NMR (CDCl 3 ): δ = 1.2-1.5 (CH 3 ), 3.3-4.3 (CH 2 -O + CH-O) and 4.9 ppm (CH-OOC). 13 C-NMR (CDCl 3 ): δ = 15.96 (CH 3 PO), 63-75 (CH-O+CH 2 -O) and 153.5-155 ppm (C=O). Example 28 Terpolymer of 1-0-glycidylglycerol with propylene oxide and carbon dioxide . A solution of 4.8 g of GIG/PO/CO 2 terpolymer containing 25%-mol of GIG units in 50 ml of dichloromethane was poured under vigorous stirring in 400 ml of 20:1 methanol/concentrated HCl mixture and left under stirring for 2 h. The coagulated polymer was then washed with methanol, dissolved in chloroform, precipitated in diethyl ether and finally dried under vacuum to yield 3.7 g of a white powder that was characterized by GPC, IR and NMR analysis. Example 29 Terpolymer of 1-0-glycidylglycerol with propylene oxide and carbon dioxide . A solution of 0.8 g of GIG/PO/CO 2 terpolymer containing 40%-mol of GIG units in 20 ml of dichloromethane was poured under vigorous stirring in 100 ml of 20:1 methanol/concentrated HCl mixture and left under stirring for 2 h. The coagulated polymer was then washed with methanol, dissolved in chloroform, precipitated in diethyl ether and finally dried under vacuum to yield 0.4 g of a white powder that was characterized by GPC. IR and NMR analysis. Example 30 Terpolymer of 0-glycidylxylitol with propylene oxide and carbon dioxide . A solution of 0.8 g of XPG/PO/CO 2 terpolymer containing 7% mol of XPG units in 29 ml of chloroform was poured under vigorous stirring in 200 ml of 50:1 methanol/concentrated HCl mixture and left under stirring for 2 h. The coagulated polymer was then washed with methanol, dissolved in chloroform, precipitated in diethyl ether and finally dried under vacuum to yield 0.6 g of a white powder that was characterized by GPC, IR and NMR analysis. IR (film): ν = 3600-3100 (ν O-H), 3000-2800 (ν CH aliphatic), 1740 (ν C=O), 1464 (δ CH 2 and δ as CH 3 ), 1378 (δ, CH 3 ), 1300-1000 (ν C-O-C) and 800-400 cm -1 (δ O-H). 1 H-NMR (CDCl 3 ): δ = 1.2-1.5 (CH 3 ), 3.4-4.4 (CH 2 -O + CH-O) and 5.0 ppm (CH-OOC). 13 C-NMR (CDCl 3 ): δ = 15.93 (CH 3 PO), 25-27 (CH 3 XPG), 65.5-81.5 (CH-O + CH 2 -O), 109-110 (O-C-O) and 153.5-155 ppm (C=O). Example 31 Terpolymer of 0-glycidylxylitol with propylene oxide and carbon dioxide . A solution of 0.5 g of XPG/PO/CO 2 terpolymer containing 8%-mol of XPG units in 20 ml of chloroform was poured under vigorous stirring in 150 ml of 50:1 methanol/concentrated HCl mixture and left under stirring for 2 h. The coagulated polymer was then washed with methanol, dissolved in chloroform, precipitated in diethyl ether and finally dried under vacuum to yield 0.3 g of a white powder that was characterized by GPC, IR and NMR analysis. Example 32 Terpolymer of 0-glycidylxylitol with propylene oxide and carbon dioxide . A solution of 0.3 g of XPG/PO/CO 2 terpolymer containing 11%-mol of XPG units in a mixture of 10 ml of methanol and 20 ml of chloroform was placed under dry nitrogen in a 100 ml two necked flask equipped with condenser and magnetic stirring. After addition of 0.2 g of Amberlyst 15, the mixture was kept under stirring at 45°C for 65 h, then the resin was filtered off and the volatile products removed under vacuum to yield 0.2 g of a semisolid product that was characterized by GPC, IR and NMR analysis. While certain specific considerations have been disclosed and discussed herein, such have been offered solely to exemplify the present invention, and should in no way be considered as limiting the scope and nature of the invention.

Claims: Biodegradable compounds having the following formula where: R1 is either H, or alkyl, or 1-(2-pyrrolidonyl) alkoxymethyl, or 1-(2- pyrrolidonyl)alkyl; R2 is either H, or alkyl, or aryl; Z is either -CO-R3- residue where R3 is linear or branched alkanediyl or arylalkanediyl or arylenediyl, or is substituted by a carbon-oxygen bond; Y is either glyceryl, or pentitolyl, or heptitolyl; O < x ≤ 1; 5 < m < 500. Biodegradable compounds according to claim 1 in which Z is a CO-R3 residue where R3 is a linear o branched alkanediyl or arylalkanediyl or arylenediyl. Biodegeadable compounds according to claim 1 in which Z is substituted by a carbon-oxygen bond. Biodegradable compounds according to any of the previous claims in which R1 is a methyl. Biodegradable compounds according to any of the previous claims characterized by having a molecular weight between 1000 and 100.000. Biodegradable compounds according to claim 5 characterized by having a molecular weight between 2.000 and 30.000. Biodegradable compounds according to any of the previous claims in which 10 < m < 150. Biodegradable compounds having the formula of claim 1 characterized in that they derive by copolymerization of the glycidyl ethers of alditols protected with isopropylidene groups and their mixtures with alkylene oxides with anhydrides, either cyclic anhydrides or carbon dioxide, in the presence of catalysts; and by controlled removal of said isopropylidene groups. Biodegradable compounds according to claim 8 in which said anhydrides are cyclic anhydrides. Biodegradable compounds according to claim 9 in which said cyclic anhydride is succinic anhydride. Biodegradable compounds according to claim 9 or 10 in which said copolymerization is at a temperature between 30C and 150C and for a time comprised between 2 and 120 hrs. Biodegradable compounds according to any of the claims from 9 to 11 in which said catalysts is a alkylaluminum derivative. Biodegradable compounds according to claim 8 in which said anhydride is carbon dioxide. Biodegradable compounds according to claim 13 in which said catalysts is the dialkylzinc/polyhydroxyphenols system. Biodegradable compounds according to any of the claims from 8 to 14 in which said glycidyl ethers of alditols have either three, or five, or seven carbon atoms and said alkylene oxides are either ethylene oxide or propylene oxide. Biodegradable compounds according to claim 15 in which said glycidyl ethers of alditols is chosen in the following groups: 1-0-glycidyl-2,3-0-isopropylideneglycerol, 0-glycidyl-di-0-isopropylidenexylitol, 1-0-glycidyl-di-0-isopropylidenearabitol, N-glycidylpyrrolidone. Process for the production of a biodegradable compound having the following formula where: R1 is either H, or alkyl, or 1-(2-pyrrolidonyl) alkoxymethyl, or 1-(2- pyrrolidonyl)alkyl; R2 is either H, or alkyl, or aryl; Z is either -CO-R3- residue where R3 is linear or branched alkanediyl or arylalkanediyl or arylenediyl, or is substituted by a carbon-oxygen bond; Y is either glyceryl, or pentitolyl, or heptitolyl; O < x ≤ 1; 5 < m < 500 characterized by a copolymerization of the glycidyl ethers of alditols protected with isopropylidene groups and their mixtures with alkylene oxides with anhydrides, either cyclic anhydrides or carbon dioxide, in the presence of catalysts; and by controlled removal of said isopropylidene groups. Process according to claim 17 in which said anhydrides are a cyclic anhydrides. Process according to claim 18 in which said cyclic anhydride is succinic anhydride. Process according to claim 17 to 19 in which said copolymerization is at a temperature between 30C and 150C and for a time comprised between 2 and 120 hrs. Process according to any of claims from 17 to 20 in which said catalysts is a alkylaluminum derivative. Process according to claim 17 in which said anhydride is carbon dioxide. Process according to claim 22 in which said copolymerization is at a temperature between 30C and 60C and for a time comprised between 20 and 120 hrs. Process according to claim 22 or 23 in which said catalysts is the dialkylzinc/polyhydroxyphenols system. Process according to any of claims from 17 to 24 in which said glycidyl ethers of alditols have either three, or five, or seven carbon atoms and said alkylene oxides are either ethylene oxide or propylene oxide. Process according to claim 25 in which said glycidyl ethers of alditols is chosen in the following groups: 1-0-glycidil-2,3-0-isopropylideneglycerol, 0-glycidyl-di-0-isopropylidenexylitol, 1-0-glycidyl-di-0-isopropylidenearabitol, N-glycidylpyrrolidone. Process according to any of claims from 17 to 26 in which said removal of isopropylidene groups is carried out by precipitation in ethanol with 5% concentrated HCl, for a time comprised between 30' and 5 hrs. Process according to any of claims from 17 to 26 in which said removal is carried out by heating at a temperature between 40C and 50C the polymer solution in methanol/chloroform mixtures in the presence of a styrene/divinylbenzene sulphonic resin for a time comprised between 40 and 80 hrs.

Inventors: BEMPORAD LUCA, CHIELLINI EMO, SOLARO ROBERTO, BEMPORAD, LUCA, CHIELLINI, EMO, SOLARO, ROBERTO
Applicants: ISI IST SIEROVACCINOGENO ITAL, ISTITUTO SIEROVACCINOGENO ITALIANO I.S.I. S.P.A.
Application year: 1991
Main classification: C08G63
IPC codes: C08G64, C08G63, A61L27