Process for alkylation of aromatic diamines and catalyst for said process

Abstract: Production of alkyl substituted aromatic diamines by reacting triethlyaluminum with an aromatic diamine and a chloride ion source in the presence of an olefin is disclosed. The alkyl substituted aromatic diamines are useful as chain extenders in polyurethane processes.

Description: This invention relates to a process for producing aromatic diamines and is more particularly concerned with a novel catalyst for said process. Aromatic amines having unsubstituted hydrogen atoms in positions ortho to amino groups may be alkylated in the ortho position in a number of ways. Kolka, et al, U.S. Pat. No. 2,814,646, describes alkylation of aromatic amines having unsubstituted ortho positions by reacting the aromatic amine with an aliphatic olefin in the presence of an aluminum trianilide catalyst. The aromatic amine may have additional substituents provided that there is an unsubstituted position ortho to an amino group available for alkylation. The catalyst of Kolka, et al, is prepared in a process which reacts the aromatic amine, having at least one hydrogen bonded to the amino nitrogen, with aluminum metal, aluminum alkyl, aluminum amide, and the like. Between 0.1-20% of the aromatic amine is converted to the aluminum anilide type catalyst. The Kolka, et al, process may be conducted between the temperatures of about 250°C up to decomposition temperature, e.g., 400°C, under olefin pressure. Stroh, et al, U.S. Pat. No. 3,275,690, is an improvement over the Kolka, et al, process by including a small amount of Friedel-Crafts catalyst as a promoter. Stroh, et al, mentions aluminum chloride, aluminum bromide, iron chloride, boron trifluoride, zinc chloride, stannic chloride, and the like as examples of promoters. The amount of promoter used is disclosed to be between 0.05 and 10 wt. % of the amount of aromatic amine utilized. The alkylation temperature is between 150°C and 400°C under olefin pressure. Klopfer, U.S. Pat. No. 3,923,892, provides a similar method of ortho alkylation of aromatic amines utilizing an alkyl aluminum halide catalyst, such as diethylaluminum chloride or ethylaluminum sesquichloride. The amount of catalyst required provides about one gram atom of aluminum per each 5-40 gram moles of aromatic amine. A portion of the aluminum may be provided by reacting aluminum metal with the aromatic amine. Governale, et al, U.S. Pat. No. 4,128,582, describes a process of selective ortho-alkylation of aromatic amines using an aluminum anilide catalyst in which the reaction rate is increased by addition of a hydrogen halide to the alkylation mixture. The process is conducted by reacting an aromatic amine with an olefin in the presence of the aluminum anilide catalyst at a temperature of between 200-500°C. A hydrogen halide may be added to the reaction mixture as a promoter in an amount to provide up to two halogen atoms per aluminum atom. According to the present invention, there is provided an improved process for alkylation of aromatic diamines. The process of this invention comprises reacting triethylaluminum with an aromatic diamine and a chloride ion source in the presence of an olefin. For the purposes of this application, the term chloride ion source shall refer to sources which will provide chloride ions in the reaction medium. The ratios listed involving chloride ion sources shall refer to sources which will provide chloride ions in the molar ratio indicated. In the process of alkylation, the best results are obtained when the aromatic diamine has two primary amino groups and a replaceable hydrogen on the ring in an ortho position relative to such amino groups. One embodiment of this invention involves a catalyst of triethyl aluminum (TEA) and a chloride ion source in a ratio of TEA to chloride ion source of between 0.9:0.01 and 1.0:0.9, preferably in a ratio of 1.0:0.5. In the above embodiment of the present invention, the process is conducted at an elevated temperature. The process is usually carried out at a temperature between 250°C and 350°C. Preferably, the process of the present invention is carried out at an elevated temperature in the range of between 280°C and 320°C, most preferably at between 290°C and 310°C. A further preferred embodiment of the present invention involves conducting the process under an elevated pressure. While the reaction may be conducted at lower pressures (i.e., above atmospheric pressure), the reaction rate, and therefore yield, are generally not sufficiently high at lower pressure. In contrast, the use of relatively high pressures does not inhibit the process, but tend to be confined by equipment limitations. The pressure falls in a range of between 4.83 to 34.48 MPa (700 psi and 5000 psi). Preferably, the process is conducted at a pressure of between 6.21 to 7.58 MPa (900 psi and 1100 psi). Most preferably, the process is conducted at a pressure of between 950 psi and 1050 psi. In the process of this invention, various aromatic diamines may be used providing that each aromatic diamine contains two replaceable hydrogens on the ring, each in an ortho position relative to an amino group. These aromatic diamines include those having the structure: wherein X and X' are alkyl groups of 1 to 6 linear or branched chain carbon atoms and n is an integer that is 0 or 1. X and X' are the same or different and further are exemplified by the group of methyl, ethyl, propyl, butyl, pentyl, hexyl, isopropyl, isobutyl, isopentyl, isohexyl, sec-butyl, neopentyl, tert-pentyl, 1-methylpentyl, 2-methylpentyl, 3-methylpentyl, 1-methylbutyl, 2-methylbutyl, 1,2-dimethylbutyl, 2,3-dimethylbutyl, 1-ethylbutyl, 1-ethylpropyl, phenyl, phenoxy, hexyloxy, pentyloxy, butoxy, propoxy, ethoxy, methoxy, allyloxy, isopropoxy, isobutoxy, sec-butoxy, tert-butoxy, and the like. Of the above described aromatic diamines, the toluene diamines (i.e., 2,4-toluenediamine, 2,5-toluenediamine, 2,6-toluenediamine, 3,5-toluenediamine, and 3,4-toluenediamine) are preferred. The chloride ion sources useful in the process include compounds that will not produce a counter ion which will inhibit the reaction (i.e., alkali metal chlorides). Examples of useful sources are hydrogen chloride, aluminum chloride, ethylaluminum chloride, diethylaluminum chloride and ethylaluminum sesquichloride. In addition, compounds that will decompose to give hydrogen chloride or ionize to give a chloride ion, such as acyl halides, benzyl chloride and allyl chloride, may be utilized. The olefins useful in the process include olefins which are both mono- or polyunsaturated, cyclic or acyclic, substituted or unsubstituted, and both terminal and internal olefins. Examples of acyclic monoolefins are ethylene, propylene, butene-1, butene-2, isobutene, pentene-1, isopentene, pentene-2, hexene-1, hexene-2, 2-methyl-pentene-1, 2-methyl-pentene-2, n-decene-1, 2-ethyloctene-1, 2-ethyloctene-2, n-decene-2, dodecene-1, 2-ethyldecene-1, 2-ethyldecene-2, and the like. Examples of cyclic monoolefins are cyclopentene, cyclohexene, cyclooctene, 1-methylcyclohexene, 1-butylcyclohexene, 1-methylcyclooctene, and the like. Useful acyclic polyenes include 1,3-butadiene, 2-methyl-1,3-butadiene, 2,3-dimethyl-1,3-butadiene, 1,4-pentadiene, and the like. Some useful cyclic polyenes are cyclopentadiene, dicyclopentadiene, 1,3-cyclooctadiene, 1,3-cyclopentadiene, 1,4-octadiene, 1,3,5-cyclooctatriene, and the like. The substituted olefins can have any substituents that do not interfere with the reaction. Examples of such groups are halogens, alkoxy groups, aryloxy groups, aryl radicals, and the like. Illustrative examples of such olefins are 2-chloro-1,3-buta-diene, vinyl chloride, vinyl bromide, indene, α-methyl-styrene, 4-dodecylstyrene, 4-sec-octyl-α-methylstyrene, and the like. The preferred olefin reactants are acyclic monoolefins containing from 1-6 carbon atoms, cyclic olefins containing 5 to 8 carbon atoms and aryl-substituted monoolefins containing from 8 to 12 carbon atoms. Especially preferred are the lower hydrocarbon monoolefins containing from 1-6 carbon atoms such as ethylene, propylene, butene-1, isobutene, pentene-1, pentene-2, isopentene, hexene-1, hexene-2, 2-methylpentene-1, cyclohexene, and the like. The amount of olefin added to the aromatic diamine will vary depending upon whether mono- or dialkylation is desired. The precise amount is not a critical feature of the process as long as sufficient olefin is present to provide at least a monoalkylated product. Generally, from 2 mole equivalents to 20 mole equivalents of olefin are added for each mole of aromatic amine. A more preferred range is from 3 mole equivalents to 5 mole equivalents of olefin for each mole equivalent of aromatic amine. The amount of catalyst used in the process should be sufficient to catalyze the alkylation at a reasonable rate. The amount of catalyst can be expressed in terms of moles of aromatic diamine per mole of aluminum in the catalyst. Satisfactory results are generally obtained when 3 to 18 moles of aromatic diamine are used per mole of aluminum in the catalyst system. A more preferred range is from 7 to 13 moles of aromatic diamine per mole of aluminum in the catalyst system. The process should be conducted under a substantially inert atmosphere. Excessive amounts of oxygen or moisture will destroy the catalyst and halt the alkylation. The reactants, however, do not have to be completely anhydrous, but should be substantially anhydrous. Also, the amount of oxygen and moisture can be minimized. This is generally accomplished by flushing the reaction vessel with an inert gas such as nitrogen, neon, methane, ethane or propane prior to conducting the reaction. For the purposes of this application, "inert" shall refer to any substance that is resistant to chemical or physical action under the conditions of the present invention. The reaction can be conducted in the presence of an inert solvent. Suitable solvents include aliphatic and aromatic hydrocarbons. Examples of aliphatic hydrocarbons that may be used include decane, undecane, dodecane, tridecane, tetradecane, pentadecane and hexadecane, among others. Useful aromatic hydrocarbons include toluene, xylene, mesitylene, and the like. The catalyst system is readily prepared from commercial stock of each component. The components may be mixed and the mixture is either used immediately or stored for later use. In addition, the catalyst components may be added to the reaction vessel either as a mixture or separately. It is the stoichiometric relationship of the catalyst to the reactants that is controlling. The time required for alkylation depends upon the reaction conditions, such as reaction temperature, pressure, amount of catalyst and ratio of catalyst components, as well as the particular aromatic diamine and olefin used. Alkylation generally requires from 1 to 4 hours, with a preferred reaction time being from 1.5 to 3 hours. The alkylation catalyst is prepared by reacting the aromatic diamine with an alkylaluminum chloride or with a mixture of aluminum alkyl and a chloride ion source. After mixing the reagents, the reaction mixture is heated to about 150°C to insure complete reaction. The mixture is then charged to an autoclave and heated to the reaction temperature. The olefin is introduced to the autoclave starting at about 200°C and the pressure is adjusted to the desired reaction pressure at the reaction temperature. Additional olefin is added during the course of the reaction to maintain the desired pressure. After the alkylation reaction is completed, the reaction vessel is cooled and the excess olefin is vented off. An excess of 25% sodium hydroxide is then added to hydrolyze the aluminum salts. The resulting aqueous phase consisting of water, sodium hydroxide and sodium aluminate is separated from the organic phase. The organic phase is then transferred for distillation. The present invention provides an improved process for alkylation of aromatic diamines and reducing the amount of heavy end formation. The term "heavy end formation" refers to products formed by various condensations or polymerizations such as the formation of dimer, trimer, or tetramer, such reactions producing compounds with molecular weight in excess of about 220. The following examples are provided as illustrations of the present invention but are not intended to limit the present invention to the conditions illustrated. It should be noted that a relatively low chloride ion concentration in the reaction vessel substantially increases the rate of reaction. However, larger concentrations tend to reduce the reaction rate and therefore reduce yield. EXAMPLE I 170.8 grams of premelted toluenediamine (about 80% 2,4-toluenediamine and 20% 2,6-toluenediamine) were added into a 500 ml 4-neck flask equipped with a stirrer, condenser, thermometer and dropping funnel. To this was added, dropwise, 13.0 g of diethylaluminum chloride. The temperature was raised to about 150°C and held for 15 minutes. This mixture was transferred to an autoclave and held at 1000 psig N₂. The N₂ was vented and heating begun up to about 300°C as ethylene was added to bring the pressure up to about 1000 psig. These conditions were maintained for about 4 hours with samples taken at half hour intervals. The samples were subjected to area % gas chromatography to determine the reaction mixture compositions of toluenediamine (TDA), monethyl TDA, and 2,4- and 2,6-diethyl toluenediamine (DETDA). Kugelrohr distillation was utilized to determine amounts of heavy end formation. The percent compositions of each sample were as follows: Sample Time of Reaction (Hours) Diamine (TDA) Monoethyl TDA 2,4-DETDA 2,6-DETDA 1 1/2 42.30 41.42 8.05 1.89 2 1 33.34 45.09 11.84 2.76 3 1-1/2 29.91 45.06 13.16 3.11 4 2 28.22 45.01 13.84 3.28 5 2-1/2 26.14 45.17 14.84 3.52 6 3 24.73 44.96 15.37 3.68 7 3-1/2 23.83 45.19 15.97 3.81 8 4 23.77 44.93 15.93 3.81 A Kugelrohr distillation was conducted at about 140°C and less than 1 mm of mercury on a 92.32 g sample of the final DETDA mixture from Example I. The distillation revealed heavy end formation of approximately 13.63% of the DETDA mixture by weight. EXAMPLE II Into a 500 ml 4-neck flask equipped with a stirrer, condenser, thermometer and dropping funnel was added 170.8 g of toluenediamine (approximately 80% 2,4-toluenediamine and 20% 2,6-toluenediamine). To this was added 12.4 g of triethylaluminum, dropwise. This mixture was raised to a temperature of about 150°C for about 15 minutes and then transferred to an autoclave and held at 1000 psig N₂. The N₂ was vented and temperature raised to about 300°C as ethylene was added to bring the pressure up to about 1000 psig. These conditions were maintained for about four hours with samples removed hourly to determine reaction mixture composition by area percentage gas chromatography. The percent composition of toluene diamine (TDA) monoethyl TDA and 2,4- and 2,6-diethyltoluenediamine (DETDA) were determined. The percent compositions of each sample were as follows: Sample Time of Reaction (Hours) Diamine (TDA) Monoethyl TDA 2,4-DETDA 2,6-DETDA 1 1 4.40 29.52 49.68 14.17 2 2 0.38 4.00 73.76 19.17 3 3 0.23 2.65 74.55 19.07 4 4 0.14 1.92 74.43 18.77 A Kugelrohr distillation of a 99.70 g sample of the final DETDA mixture of Example II conducted at about 140°C and less than 1 mm of mercury indicated heavy end formation amounting to 3.73% of DETDA compounds by weight. EXAMPLE III Into a 500 ml 4-neck flask equipped with a stirrer, condenser, thermometer and dropping funnel was added 170.8 g of toluenediamine (approximately 80% 2,4-toluenediamine and 20% 2,6-toluenediamine). To this was added a mixture of 9.3 g triethylaluminum (TEA and 3.25 g diethylaluminum chloride (DEAC). The TEA/DEAC mixture was added dropwise to control the rate of gas formation. The mixture was then transferred to an autoclave and held overnight at 1000 psig N₂. The N₂ was vented and temperature raised to about 300°C as ethylene was added to bring the pressure up to about 1000 psig. These conditions were maintained for about three hours with samples removed at half-hour intervals to determine reaction mixture composition by area percentage gas chromatography. The percent compositions of toluenediamine (TDA), monoethyl TDA and 2,4- and 2,6-diethyltoluenediamine (DETDA) for each sample were as follows: Sample Time of Reaction (Hours) Diamine (TDA) Monoethyl TDA 2,4-DETDA 2,6-DETDA 1 1/2 18.72 48.66 24.24 6.04 2 1 2.36 19.59 59.60 15.54 3 1-1/2 0.27 1.73 75.41 19.08 4 2 0.17 0.95 75.62 19.04 5 2-1/2 0.15 0.84 75.37 18.94 4 3 0.13 0.77 75.11 18.80 A Kugelrohr distillation was conducted at about 140°C and less than 1 mm of mercury on a 99.83 g sample of the final DETDA mixture from Example III. The distillation revealed heavy end formation amounting to 4.98% of the DETDA mixture by weight. EXAMPLE IV Into a 500 ml 4-neck flask equipped with a stirrer, condenser, thermometer and dropping funnel was added 170.8 g of premelted TDA (same composition as Examples I-III). To this was added dropwise a mixture of 6.17 triethylaluminum and 6.51 g diethylaluminum chloride. The mixture was then transferred to an autoclave and pressurized to 1000 psig under nitrogen. The nitrogen was vented and the temperature raised to about 300°C as ethylene was added to bring the pressure up to about 1000 psig. These conditions were maintained for about two hours with samples taken at half-hour intervals to determine reaction mixture composition by area percentage gas chromatography. The percent composition of toluenediamine (TDA), monoethyltoluenediamine (METDA) and 2,4- and 2,6-diethyltoluenediamine (DETDA) for each sample were as follows: Sample Time of Reaction (Hours) Diamine (TDA) Monoethyl TDA 2,4-DETDA 2,6-DETDA 1 1/2 9.30 42.50 36.39 9.11 2 1 0.35 3.10 74.08 19.10 3 1-1/2 0.19 1.01 75.25 19.15 4 2 0.11 0.74 74.81 18.98 A Kugelrohr distillation was conducted at about 140°C and less than 1 mm of mercury on a 100.02 g sample of the final DETDA mixture of Example IV. The distillation revealed heavy end formation of approximately 3.64% of the DETDA mixture by weight.

Claims: A catalyst formed by reacting triethylaluminum with an aromatic diamine and a chloride ion source in a molar ratio of triethylaluminum to chloride ion source from 1.0:0.9 to 0.9:0.01. The catalyst of Claim 1 wherein the molar ratio of triethylaluminum to a chloride ion source is 1.0:0.5. A process for alkylating aromatic diamines and inhibiting heavy end formation which comprises treating a mixture of an aromatic diamine and an olefin with a catalyst comprising triethylaluminum and a chloride ion source wherein the molar ratio of triethylaluminum to chloride ion source is from 0.9:0.01 to 1.0:0.5, preferably 1.0:0.5. The process of Claim 3 wherein said process is conducted under pressure above 2.76 MPa (400 psi). The process of Claim 4 wherein said process is conducted under pressure in the range of above 4.83 to 34.48 MPa (700 psi to about 5000 psi) at a temperature in the range of 250°C to 350°C. The process of Claim 5 wherein the process is conducted under pressure in the range of 6.21 to 7.58 MPa (900 psi to 1100 psi) at a temperature in the range of 280°C to 320°C. The process of any of claims 3-6 wherein said aromatic diamine is a C₁-C₆ linear or branched alkyl substituted diamine of the formula: wherein X and X' are the same or different alkyl groups of 1 to 6 linear or branched chain carbon atoms, n is an integer that is 0 or 1, and the aromatic ring contains two replaceable hydrogen atoms, each in an ortho position relative to an amino group and wherein said olefin is propylene, isobutylene or ethylene. The process of Claim 7 wherein said alkyl group is methyl or ethyl. The process of any of claims 3-8 wherein the reaction is conducted without the presence of a solvent. A process for alkylating a toluenediamine and inhibiting heavy end formation which comprises treating a mixture of a toluenediamine and ethylene at 280-320°C under a pressure of 6.21 to 7.58 MPa (900-1100 psi) with a catalyst formed by reacting triethylaluminum with a toluenediamine in the presence of a chloride ion source, the ratio of triethylaluminum to chloride ion source in the catalyst being 1.0:0.5.

Inventors: IHRMAN KRYN GEORGE, MITCHELL OLAN WAYNE, WILSON RILEY WOODROW JR, IHRMAN, KRYN GEORGE, MITCHELL, OLAN WAYNE, WILSON, RILEY WOODROW, JR.
Applicants: ALBEMARLE CORP, ALBEMARLE CORPORATION
Application year: 1991
Main classification: B01J31
IPC codes: C07C209, C07C211, B01J31, C07B61