Coated abrasive containing erodable agglomerates and manufacture of such abrasive

Abstract: This invention relates to coated abrasives, and, more particularly, to coated abrasive products containing erodable agglomerates. Conventional coated abrasives typically consist of a single layer of abrasive grain adhered to a backing. It has been found that only up to about 15% of the grains in the layer are actually utilized in removing any of the workpiece. It has long been known that a coated abrasive containing an underlayer of conventional aluminum oxide grains and a top layer of individual premium abrasive grains provides satisfactory performance at a lower cost than a coated abrasive using 100% individual premium abrasive grains. However, for certain grinding applications, the conventional abrasive grains prevent maximum utilization of the individual premium abrasive grains that are randomly distributed between the conventional grains. This invention provides a coated abrasive product comprising a backing bearing on at least one major surface thereof a make coat, a multiplicity of erodable agglomerates comprising a resinous binder and at least one inorganic filler material adhered to said make coat, a multiplicity of individual premium abrasive grains adhered to said make coat and disposed between said erodable agglomerates, a multiplicity of individual premium abrasive grains overlying said erodable agglomerates, and a size coat overlying said individual premium abrasive grains, said erodable agglomerates, and said make coat. The coated abrasive products of this invention abrade faster and endure longer than coated abrasive products using individual conventional abrasive grains in place of erodable agglomerates.

Description: This invention relates to coated abrasives, and, more particularly, to coated abrasive products containing erodable agglomerates. Conventional coated abrasives typically consist of a single layer of abrasive grain adhered to a backing. It has been found that only up to about 15% of the grains in the layer are actually utilized in removing any of the workpiece. It follows then that about 85% of the grains in the layer are wasted. Furthermore, the backing, one of the more expensive components of the coated abrasive, must also be disposed of before the end of its useful life. To overcome this problem of waste, many attempts have been made to distribute the abrasive grains on the backing in such a manner so that a higher percentage of the abrasive grains can be utilized, thus leading to extended life of the coated abrasive product. The extended life further leads to fewer belt or disc changes by the operators, thereby saving time and reducing labor costs. It is apparent that merely depositing a thick layer of abrasive grains on the backing will not solve the problem, because the grains lying below the topmost grains are not likely to be used. A highly desirable abrasive grain is marketed under the trademark "Cubitron". "Cubitron" abrasive grain is a non-fused synthetic alumina-based mineral optionally containing certain metal oxide or spinel or both additives. "Cubitron" abrasive grain is described in U.S. Patent No. 4,314,827; 4,744,802; 4,770,671; and 4,881,951. Although "Cubitron" grain provides excellent performance, it is much more expensive than conventional aluminum oxide grain. It has long been known that a coated abrasive containing an underlayer of conventional aluminum oxide grains and a top layer of "Cubitron" grains provides satisfactory performance at a lower cost than a coated abrasive using 100% "Cubitron" grains. However, for certain grinding applications, the conventional abrasive grains prevent maximum utilization of the "Cubitron" grains that are randomly distributed between the conventional grains. If these conventional grains do not break down fast enough, they tend to compete with the "Cubitron" grains for contact with the metallic workpiece and rub rather than remove metal. This prevents the "Cubitron" grains from fully penetrating into the metal to allow them to remove large amounts of metal. EP-A-444,824 which constitutes prior art in respect of all of the designated states except Switzerland/Liechtenstein discloses a coated abrasive article comprising a backing bearing on a major surface thereof a make coat and a multiplicity of erodable agglomerates comprising a resinous binder and abrasive material and optionally an organic filler adhered to said make coat, a multiplicity of individual premium abrasive grains adhered to said make coat and disposed between said erodable agglomerates, a multiplicity of individual premium abrasive grains overlying said erodable agglomerates and a size coat overlying said individual abrasive grains, said erodable agglomerates, and said make coat. EP-A-444,824 also discloses a method of making said coated abrasive in which make coat is applied to a backing and then applied individual premium abrasive grains and erodable agglomerates comprising a resinous binder and abrasive materials and optionally an organic filler, said make coat would be then cured and a size coat applied over the premium grains and erodable agglomerates which is then cured. The invention provides a coated abrasive article comprising a backing bearing on one major surface thereof a make coat, a multiplicity of erodable agglomerates comprising a resinous binder and a filler consisting essentially of inorganic, non-abrasive filler material and optionally an organic filler adhered to said make coat, a multiplicity of individual premium abrasive grains adhered to said make coat and disposed between said erodable agglomerates, and a size coat overlying said individual abrasive grains, said erodable agglomerates, and said make coat. The invention also provides a method of making such a coated abrasive, comprising the steps of: i) providing a backing (12); ii) applying a make coat (14) to said backing; iii) applying individual premium abrasive grains (18) and erodable agglomerates (16) over said make coat, said erodable agglomerates comprising a resinous binder (22) and a filler consisting essentially of inorganic, non-abrasive filler material and optionally an organic filler; iv) curing said make coat; v) applying a size coat (20) over said mixture of individual premium abrasive grains, said erodable agglomerates, and said make coat, and vi) curing said size coat. The coated abrasive products of this invention abrade faster and endure longer than coated abrasive products using individual conventional abrasive grains in place of erodible agglomerates. Preferred embodiments of the invention are described below by way of example only with reference to the accompanying drawings, wherein FIG. 1 is a schematic representation of a cross-section of one embodiment of a coated abrasive product of this invention. FIG. 2 is a schematic representation of a cross-section of another embodiment of a coated abrasive product of this invention. FIG. 3 is a schematic representation of a cross-section of another embodiment of a coated abrasive product of this invention. FIG. 4 is a drawing of an apparatus for testing the abrasiveness of abrasive discs. Materials used in abrasive articles are often categorized according to their ability to abrade a surface. Materials capable of quickly abrading a surface are denoted "premium" while those that abrade a surface slowly, or not at all, are denoted "nonabrasive". Materials capable of abrading a surface at a moderate rate are denoted "conventional". The designation as premium, conventional, or nonabrasive involves a considerable degree of subjectivity, and depends to some degree on the type of workpiece and the abrading conditions employed. Nevertheless, for most commercially significant abrading operations, it has been found that a test involving the abrasion of cold rolled steel with coated abrasive products having only one type of grain, will, when compared to an identical construction involving a different type of grain, yield test results which are highly reliable in categorizing abrasive materials as premium, conventional, or nonabrasive. To classify materials commonly used in abrasive articles as premium, conventional, or nonabrasive, abrasive discs containing Grade 36 abrasive grains (average grain size of 710 micrometers) were prepared. Conventional procedures for preparing coated abrasive products were followed, using conventional 0.76 mm thick vulcanized fiber backings, a conventional calcium carbonate-filled phenolic resin make coat, and a conventional cryolite-filled phenolic resin size coat. The weight of the make coat was 170 g/m 2 . The resin of the make coat was precured for 90 minutes at 88°C and the resin of the size coat precured for 90 minutes at 88°C followed by final curing at 100°C for 10 hours. The make and size coats were applied via conventional techniques in a one-trip operation and were cured in a forced air oven. The cured discs (17.8 cm diameter) were flexed in a conventional manner to controllably break the hard bonding resins, mounted on a beveled aluminum back-up pad, and used to grind a 1.25 cm by 18 cm face of a 1018 cold rolled steel workpiece. Each disc was driven at 5,500 rpm while the portion of the disc overlying the beveled edge of the back-up pad contacted the workpiece at a load of 5.91 kg. Grinding was conducted for one minute time intervals and each disc was used to grind a separate workpiece for a total of 12 minutes or until no more than 5 grams of metal were removed in any one minute grinding cut, whichever came first. This test was performed for different discs, each disc containing undiluted grains of one of the following materials: fused alumina-zirconia, ceramic aluminum oxide, heat-treated fused aluminum oxide, brown fused aluminum oxide, garnet, and marble. The total amount of metal (total cut) removed by using such discs is set forth in Table 1, along with the coating weights of the mineral and size coats. In each case, the total cut figure is the average for at least three discs. Grain Designation Coating Weight Total Cut (g) Grain (g/m 2 ) Size (g/m 2 ) Fused alumina-zirconia 920 700 969 Ceramic aluminum oxide 1060 700 1411 Heat-treated aluminum oxide 900 530 329 Brown-fused aluminum oxide 1060 700 371 Garnet 1270 700 209 Marble 530 540 22 If the total cut of a coated abrasive disc is greater than 500 grams, the abrasive grain is considered premium. If the total cut of a coated abrasive disc is less than 50 grams, the grain is considered nonabrasive. If the total cut of a coated abrasive disc is between 50 grams and 500 grams, the grain is considered conventional. Typically, nonabrasive diluent grains will cut considerably less than 50 grams. The stock removal of 1018 steel by nonabrasive diluent grains is not attributed to its cutting power but solely to the mechanical friction of the workpiece rubbing against the nonabrasive diluent grains. The nonabrasive diluent grains defined above should not be confused with the abrasive grains denoted "inferior" in U.S. Patent No. 4,734,104 and U.S. Patent No. 4,737,163. The designation as a "superior" or "inferior" abrasive in these two references is a relative measurement between two different abrasive grain types. If a coated abrasive product containing one type of abrasive grain cuts over 10% more than an identical coated abrasive product containing a different type of abrasive grain, under identical test conditions, then the first type of abrasive grain is deemed "superior" and the second type "inferior". Thus, the designation as "superior" or "inferior" is a characteristic of the pair of abrasive grain types compared, not a measurement of the ultimate abrasiveness of the abrasive grain type so designated. The abrasive grain types denoted "inferior" are abrasive nonetheless and differ, therefore, from the nonabrasive diluent grains defined above. One embodiment of a coated abrasive that may be produced according to this invention is illustrated in FIG. 1. As illustrated in FIG. 1, coated abrasive article 10 comprises a backing 12. Overlying backing 12 is a make coat 14 to which are adhered erodable agglomerates 16 and individual premium abrasive grains 18. A size coat 20 has been applied over make coat 14, erodable agglomerates 16, and individual premium abrasive grains 18. Erodable agglomerates 16 comprise a resinous binder 22 and inorganic particulate materials 24. Another embodiment of a coated abrasive that may be produced according to this invention is illustrated in FIG. 2. As illustrated in FIG. 2, coated abrasive article 30 comprises a backing 32. Overlying backing 32 is a make coat 34 to which are adhered erodable agglomerates 36 and individual premium abrasive grains 38. A size coat 40 has been applied over make coat 34, erodable agglomerates 36, and individual premium abrasive grains 38. Erodable agglomerates 36 comprise a resinous binder 42 and inorganic powdered materials 44. Another embodiment of a coated abrasive that may be produced according to this invention is illustrated in FIG. 3. As illustrated in FIG. 3, coated abrasive article 50 comprises a backing 52. Overlying backing 52 is a make coat 54 to which are adhered erodable agglomerates 56 and individual premium abrasive grains 58. A size coat 60 has been applied over make coat 54, erodable agglomerates 56, and individual premium abrasive grains 58. Erodable agglomerates 56 comprise a resinous binder 62 and inorganic particulate materials 64. The difference between the embodiments in FIG. 1 and FIG. 2 resides in the nature of the erodable agglomerates. In FIG. 1, erodable agglomerate 16 comprises a resinous binder 22 and inorganic particulate materials 24. In FIG. 2, erodable agglomerate 36 comprises a resinous binder 42 and inorganic powdered materials 44. The difference between the embodiment in FIG. 3 and those of FIGS. 1 and 2 resides in the disposition of the individual premium abrasive grains. In FIG. 3, all of the individual premium abrasive grains are adhered to the make coat; in FIGS. 1 and 2, a portion of the individual premium abrasive grains overlies the erodable agglomerates and are not disposed between adjacent erodable agglomerates. Backing 12, and backings 32 and 52, that are suitable for this invention may be formed from any material that is compatible with the make coat and the components of the erodable agglomerates and that is capable of maintaining its integrity under expected curing and abrading conditions. It is preferable that the backing be in the form of a conformable, flexible sheet. Materials suitable for preparing backings of the coated abrasives of the present invention are well known in the art and include fiber, polymeric film, paper, woven and non-woven fabric, and foils. Erodable agglomerates (16, 36) that are suitable for this invention comprise a resinous binder and a filler consisting essentially of inorganic, non-abrasive filler material in the binder and optionally an organic filler. In order for the agglomerates to be erodable, the resinous binder must be erodable. Representative examples of erodable agglomerates that are suitable for the coated abrasives of the present invention are described in US Patent Nos. US-A-4,652,275 and US-A-4,799,939. An erodable agglomerate preferred for the coated abrasive of the present invention comprises a binder preferably made from phenolic resin, and an inorganic filler, such as sodium cryolite or ammonium cryolite. Other erodable agglomerates suitable for the coated abrasive of the present invention are described in U.S. Patent Nos. Re. 29,808; 4,311,489; and German Auslegeschrift No. 2,417,196. Materials suitable for the resinous binder of the erodable agglomerates include phenolic resins, urea formaldehyde resins, urethane resins, polyester resins, acrylate resins, epoxy resins, and hide glue. Although hide glue is not a resin, it is suitable for use as the resinous binder of the erodable agglomerates. The preferred resin for the erodable binder is phenolic resin. Filler materials suitable for the erodable agglomerate include inorganic powdered materials, inorganic particulate materials, or both. Inorganic powdered filler materials suitable for the erodable agglomerates include conventional filler materials, e.g., cryolites, such as, for example, sodium cryolite, potassium cryolite, ammonium cryolite, fluoroborates, such as, for example, potassium tetrafluoroborate (KBF 4 ), sodium tetrafluoroborate (NaBF 4 ), and ammonium tetrafluoroborate, silicon fluorides, such as, for example, sodium hexafluorosilicate (Na 3 SiF 6 ) and potassium hexafluorosilicate (K 3 SiF 6 ), carbonates, such as, for example, calcium carbonate (CaCO 3 ), sulfates, such as, for example, sodium sulfate (Na 2 SO 4 ), hydroxides, such as, for example, aluminum hydroxide monohydrate (Al(OH) 3 ·H 2 O) and aluminum hydroxide trihydrate (Al(OH) 3 ·3H 2 O), silica, such as, for example, glass beads, and silicates, for example, talc. Inorganic particulate filler materials suitable for the erodable agglomerate include non-abrasive materials, such as, for example, marble (CaCO 3 ), gypsum (CaSO 4 ), and vermiculite. Organic filler materials can optionally be added to the erodable agglomerates. Organic filler materials include such materials as wood pulp and wood flour. The size of the filler materials in the erodable agglomerate depends on their physical form. The size of inorganic powdered filler material can for example range from 0.5 micrometer to 200 micrometers, preferably from 10 micrometers to 50 micrometers. The size of individual abrasive grains in the erodable agglomerate must be small enough to provide multiplicity of individual grains within the erodable agglomerate. The size of inorganic particulate filler material can for example range from 50 micrometers to 700 micrometers, preferably from 170 micrometers to 650 micrometers. These ranges correspond to a screen size of grade 240 and coarser. The size of the powdered filler material is based on a diameter typically measured by means of an aperture technique, such as a Coulter counter. The size of the particulate filler material is based on screen size. The percentage of filler materials in the erodable agglomerate depends on the nature of the filler material. For particulate material only, the filler can comprise from about 5% to about 90% by weight of the agglomerate, for example. For powdered material only, the filler can comprise from about 5% to about 90% by weight of the agglomerate, preferably 50% to 70% by weight of the agglomerate, for example. If an agglomerate contains both particulate filler material and powdered filler material, it is preferred that it contain from about 5% to about 15% by weight powdered filler material. The range of size for the erodable agglomerates is dependent upon the range of size for the individual premium abrasive grains. In general, the ratio of the size of the individual premium abrasive grains, to the size of the erodable agglomerates preferably ranges from about 2.5:1 to about 0.5:1. If the erodable agglomerates are too small, relative to the individual premium abrasive grains, insufficient support will be given to the individual premium abrasive grains and performance will be adversely affected. If the erodable agglomerates are too large, relative to the individual premium abrasive grains, the erodable agglomerates could prevent the individual premium abrasive grains from contacting the workpiece. The size of the erodable agglomerates can for example range from 300 to 1,500 micrometers, and preferably ranges from 500 to 1,200 micrometers. As the size of the erodable agglomerates decreases, their ability to erode also decreases, which results in a decrease in grinding performance. The erodable agglomerates suitable for use in the present invention can be prepared by the following procedure. Inorganic filler materials, e.g., abrasive grains, powdered filler materials, and resin, are introduced into a mixing vessel, and the resulting mixture stirred until it is homogeneous. It is preferred that there be sufficient liquid in the mixture that the resulting mixture not be excessively stiff or excessively runny. Most resins contain sufficient liquid to permit adequate mixing. After the mixing step is complete, the mixture is caused to solidify, preferably by means of heat or radiation. Solidification results from removal of the liquid from the mixture. In the case of resinous binders, solidification also results from curing of the resin. After the mixture is solidified, it is crushed into the form of agglomerates and graded to the desired size. Devices suitable for this step include conventional jaw crushers and roll crushers. The crushing and grading procedures necessary to obtain agglomerates as described frequently results in the agglomerates being of an undesirable size range, and they can either be recycled, e.g., by being added to a new dispersion, or discarded. Abrasive grains that are suitable for the individual premium abrasive grains 18, and abrasive grains 38 and 58, of the present invention include ceramic aluminum oxide (such as for example, "Cubitron", commercially available from Minnesota Mining and Manufacturing Company and described in U.S. Patent Nos. 4,314,827; 4,744,802; 4,770,671; and 4,881,951, alumina zirconia, silicon nitride coated silicon carbide (SNAG), tungsten carbide, cubic boron nitride, boron carbide, and diamond. SNAG can be prepared according to U.S. Patent No. 4,505,720. The coated abrasive of this invention is preferably prepared by applying a make coat over the backing, drop coating the erodable agglomerates over the make coat, electrostatically coating individual premium abrasive grains over the layer of erodable agglomerates, curing the make coat, applying a size coat, and then curing the thus-applied coatings. The make coat and size coat can be made from conventional materials, e.g., phenolic resins, urea-formaldehyde resins, epoxy resins, hide glue, and varnish. Examples of materials suitable for preparing the make coat and size coat of the coated abrasives of this invention are described in Leitheiser. U.S. Patent No. 4,314,827. Care should be taken so that the size coat does not adversely affect erodability of the erodable agglomerates, i.e., the size coat must be very thin so as not to flood the surface of the coated abrasive. It is also contemplated that radiation-curable resins can also be used for the make coat, size coat, or both. Examples of radiation-curable resins are described in U.S. Patent Nos. 4,751,138; 4,903,440, and 4,927,431. It is also within the scope of this invention to apply a supersize coat over the size coat. A supersize coat will typically comprise a binder and a grinding aid. In a preferred supersize coat, the binder is an epoxy resin and the grinding aid is potassium fluoroborate. The coating weight of the erodable agglomerates can for example range from 40 to 150 grains/4 in. x 6 in. (167 to 628 g/m 2 ), preferably 90 to 110 grains/4 in. X 6 in. (377 to 460 g/m 2 ). The coating weight of the individual premium abrasive grains can for example range from 50 to 250 grains/4 in. x 6 in. (209 to 1,047 g/m 2 ), preferably 90 to 100 grains/4 in. X 6 in. (377 to 419 g/m 2 ). The volume of erodable agglomerates to the volume of individual premium abrasive grains can for example range from 0.08:1 to 1.75:1, preferably 0.5:1 to 1:1. The foregoing coating weight ranges are based on agglomerates of grade 24. The individual premium abrasive grains can be applied as either an open coat or a closed coat. It is preferable, from the standpoint of cost, to apply the premium abrasive grains as an open coat. The following non-limiting examples will further illustrate the present invention. The weight expressed in the tables are expressed as weight of material per unit area. In the following examples, three types of tests were employed to evaluate performance of the coated abrasives of this invention. These tests are described below. Edge Test The edge test apparatus included an electric motor which drove a shaft at 3,400 rpm and a 16.5 cm (6.5 inch) diameter back-up plate which was attached for rotation about the shaft. An abrasive disc test sample was held to the back-up pad by a retainer plate. The apparatus was positioned such that the motor shaft made an 18.5° angle with respect to vertical. The edge of a 14 gauge (0.19 cm thick), 30.5 cm (12 inches) diameter plate comprised of either cold rolled steel or 304 stainless steel was contacted with the outer edge of the abrasive disc under 2,896 gram load. The circular plate was rotated at 2 rpm. Flat Test The flat test apparatus was similar to the edge test apparatus except that the motor shaft made a 7° angle with respect to vertical and the abrasive disc was placed in contact with the edge of the circular plate under a 2,670 gram load such that the contact area of the abrasive disc was about 1.3 centimeters (0.5 inches) from the outer edge of the disc. In both tests, the substrate was weighed before and after an eight minute run of the test device to determine the amount of metal removed. Hydraulic Slide Action Test The testing apparatus is depicted in FIG. 4 of the drawing. The apparatus 70 includes air motor 71 which drives a shaft 72 at 5,000 rpm with a 7 inch (17.8 cm) diameter aluminum back-up plate 73 having a beveled face 74 to which test coated abrasive disc 75 is attached and held in place by retainer 76. Back-up plate 78 has a 1 inch (2.5 cm) wide peripheral bevel at an angle of 6° with respect to its back surface. The device was positioned with a hydraulic motor shaft at an angle above a one-half inch wide (1.27 cm) by 8 inch long (20.3 cm) 1018 low carbon steel workpiece bar so that the portion of the abrasive disc on the beveled portion of the back-up plate pad was approximately parallel to the surface of the workpiece to prevent retainer 76 from contacting the surface of the workpiece during grinding. A 13 pound (5.9 kg) load was applied to the grinder while the workpiece was caused to reciprocate 7 inches (17.8 cm) back and forth in a direction perpendicular to the applied load. Under such conditions, the abrasive grinding area was one-half square inch (3.2 square cm), resulting in a load of 26 lbs/in 2 (1.8 kg/cm 2 ). The test was run by grinding a pre-weighed workpiece for 1 minute, then reweighing the workpiece to obtain the weight of metal removed. This procedure was repeated 12 times, using a set of 12 fresh workpiece bars at substantially room temperature and a total was obtained by adding the weight of the steel removed from each of the 12 workpieces. When a test was completed for 12 sequences, the total weight removed for 12 minutes was recorded. EXAMPLE I This example illustrates the effect of the nature of inorganic particles in the erodable agglomerates. Resinous binder (resole phenol-formaldehyde), an inorganic filler (sodium cryolite), and an organic filler (10% aqueous dispersion of wood pulp) were introduced into a Hobart mixer, and the resulting mixture was mixed for five minutes therein. Inorganic non-abrasive filler material was added to the mixture. The inorganic filler material was marble (capable of passing 30 mesh screen, being retained on 80 mesh screen). The amount of each ingredient for each is set forth below: Ingredient Amount (g) Resole phenol-formaldehyde 11.9 Sodium cryolite 11.9 Wood pulp 7.4 Marble 68.8 The resulting mixture was mixed for an additional five to ten minutes. The mixture, which was in the form of a doughy mass, was then spread out onto a sheet of polyethylene and cured for one hour at 65.6°C (150°F), one hour at 88°C (190°F), four hours at 98°C (208°F), and 16 hours at 102°C (215°F). The cured material was run through a jaw crusher to reduce its size and then crushed and screened three times to reduce it to a size capable of passing through a 14 mesh screen, but not capable of passing through a 35 mesh screen. The coated abrasives were prepared by first applying a make coat of uniform thickness to a 0.76mm (30 mil) thick, 178mm (7 inch) diameter vulcanized fiber disc. The make coat was a calcium carbonate filled resole phenolic resin (52% by weight CaCO 3 ). Then the appropriate erodable agglomerates were uniformly drop coated onto the make coat. A layer of "Cubitron" abrasive grains (grade 24), commercially available from Minnesota Mining and Manufacturing Company, was then applied using electrostatic coating techniques. The coating weight of the erodable agglomerates was corrected for bulk density to give approximately the same particle volume as the drop coated mineral of the control discs. Control discs were made in which the layer of drop coated material was heat-treated aluminum oxide (grade 24), instead of erodable agglomerates. The weight of this material was 0.800 kg/m 2 . The make coat was pre-cured for about 20 minutes at 150°F (65.6°C) and three hours at 190°F (87.7°C). Then a size coat was uniformly applied over the layer of "Cubitron" abrasive grains. The size coat was a cryolite filled resole phenolic resin (68% by weight cryolite). The make coat and size coat were cured for 24 hours at 212°F (100°C). These discs were tested by the high pressure edge test, medium pressure flat test at two loads, and on the low pressure hydraulic slide action test. The results are set forth in Table 2. Run no. Weight of make coat (kg/m 2 ) Weight of size coat (kg/m 2 ) Weight of agglomerate coat (kg/m 2 ) Weight of premium grain coat (kg/m 2 ) Control 0.377 0.523 --- 0.393 Example 0.377 0.523 0.398 0.393 Run no. Edge test Flat test Amount removed (g) Percent of control (%) Amount removed (g) Percent of control (%) Control 190 100 118 100 Example 183 96 141 119 Run no. Flat test Hydraulic slide action test Amount removed (g) Percent of control (%) Amount removed (g) Percent of control (%) Control 201 100 1005 100 Example 215 107 1106 110 The foregoing results show that a coated abrasive containing erodable agglomerate outperforms the control. At moderate grinding loads (flat test at 1.1 x 10 5 kg/m 2 , it was also found that the coated abrasives containing erodable agglomerates containing the friable, non-abrasive inorganic particles outperformed those containing tough, abrasive inorganic particles.

Claims: Coated abrasive article comprising a backing (12, 32) bearing on one major surface thereof a make coat (14, 34), a multiplicity of erodable agglomerates (16, 36) comprising a resinous binder (22, 42) and a filler consisting essentially of inorganic, non-abrasive filler material and optionally an organic filler adhered to said make coat, a multiplicity of individual premium abrasive grains (18, 38) adhered to said make coat and disposed between said erodable agglomerates, and a size coat (20, 40) overlying said individual abrasive grains, said erodable agglomerates, and said make coat. A coated abrasive article according to claim 1, wherein a multiplicity of individual premium abrasive grains overly said erodable agglomerates. Coated abrasive article according to claim 1, wherein said resinous binder (22/42) of said agglomerates (16/36) is selected from phenolic resins, urea formaldehyde resins, urethane resins, polyester resins, acrylate resins, epoxy resins and hide glue. A coated abrasive article according to any one of claims 1 to 3, wherein said inorganic filler is in the form of a powder. A coated abrasive article according to any one of claims 1 to 4, wherein said inorganic filler is selected from cryolites, fluoroborates, silicon fluorides, carbonates, sulfates, hydroxides, silica and silicates. A coated abrasive article according to any one of claims 1 to 5, wherein said inorganic filler is in particulate form. A coated abrasive article according to claim 6, wherein said non-abrasive filler is selected from marble, gypsum, and vermiculite. A coated abrasive article according to any preceding claim, wherein the ratio of the size of the individual premium abrasive grains (18) to the size of said erodable agglomerates (16) ranges from 2.5:1 to 0.5:1. A coated abrasive article according to any preceding claim, wherein said erodable agglomerate (16) further includes an organic filler. A coated abrasive article according to any preceding claim, wherein said individual premium abrasive grains (18) are selected from ceramic aluminum oxide, alumina zirconia, silicon nitride coated silicon carbide, tungsten carbide, cubic boron nitride, boron carbide and diamond. A method of making a coated abrasive article as claimed in claim 1, comprising the steps of: i) providing a backing (12); ii) applying a make coat (14) to said backing; iii) applying individual premium abrasive grains (18) and erodable agglomerates (16) over said make coat, said erodable agglomerates comprising a resinous binder (22) and a filler consisting essentially of inorganic, non-abrasive filler material and optionally an organic filler; iv) curing said make coat; v) applying a size coat (20) over said mixture of individual premium abrasive grains, said erodable agglomerates, and said make coat, and vi) curing said size coat.

Inventors: BROBERG DAVID E, COSMANO RICHARD J, DUWELL ERNEST J, BROBERG, DAVID E.,, COSMANO, RICHARD J., DUWELL, ERNEST J., BROBERG, DAVID E., C/O MINNESOTA MINING AND, Cosmano, Richard J., c/o Minnesota Mining and, Duwell, Ernest J., c/o Minnesota Mining and
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1991
Main classification: B24D3
IPC codes: C09C1, B24D3, B24D11, C09K3