Polymer mixture which comprises polyphenylene ether, polyoctenylene and TiO2 or BaSO4

Abstract: The invention relates to polymer mixtures which comprise a polyphenylene ether, a polyoctenykene and TiO₂ or BaSO₄. The presence of TiO₂ or BaSO₄ leads to an improvement of the mechanical properties.

Description: The invention relates to a polymer mixture which comprises A. a polyphenylene ether and B. a polyoctenylene. Polymer mixtures which comprise a polyphenylene ether and a polyoctenylene are known from DE-A-3518277. The known polymer mixtures have a favourable notched impact value, a good resistance to thermal deformability and a good processability. It has been found that the mechanical properties of the said known polymer mixtures, in particular also the notched impact strength, can be considerably improved by the addition of TiO₂ or BaSO₄. The polymer mixture according to the invention comprises per 100 parts by weight of A + B, 1-60 parts by weight of TiO₂ or BaSO₄. Due to the presence of the TiO₂ or BaSO₄ the polymer mixture according to the invention has better mechanical properties. The improvement of the mechanical properties which are obtained as a result of incorporating TiO₂ or BaSO₄ in the polymer mixture according to the invention is of a very surprising nature. In fact, the addition of TiO₂ and BaSO₄ generally leads to a deterioration of the mechanical properties, in particular of the notched impact strength. The polymer mixture according to the invention comprises at any rate the following constituents: A. one or more polyphenylene ethers B. one or more polyoctenylenes, and C. TiO₂ and/or BaSO₄. A. Polyphenylene ether Polyphenylene ethers are generally known polymers. All the polyphenylene ethers known per se may be used in the polymer mixtures according to the invention. An elaborate enumeration of suitable polyphenylene ethers is to be found, for example, in WO 87/00540. Particularly suitable are poly(2,6-dimethyl-1,4-phenylene) ether, poly(2-methyl-6-ethyl-1,4-phenylene) ether. It is also possible to use copolymers, for example, copolymers which comprise units derived from 2,3,6-trimethylphenol and from 2,6-dimethylphenol. B. Polyoctenylene Polyoctenylenes are known per se. For this puropose, reference may be made to DE-A-3518277 and to the literature mentioned therein. Polyoctenylenes are generally prepared by a polymerisation reaction of cyclo-octene, in which ring opening and ring expansion, respectively, may occur. All the types of polyoctenylenes mentioned in DE-A-3518277 may be used in the polymer mixture according to the invention. C. BaSO₄ and/or TiO₂ All the conventional qualities of BaSO₄ and/or TiO₂ as they are used in polymer mixtures may be used in the polymer mixture according to the invention. The polymer mixture according to the invention preferably comprises A. 75-99.5 parts by weight of polyphenylene ether and B. 25-0.5 parts by weight of polyoctenylene. In addition to the constituents mentioned herein-before the polymer mixture according to the invention may comprise conventional additives. The quantity of additives is preferably 0-50 parts by weight per 100 parts by weight of A + B. Suitable additives are, for example, agents to improve the flame retarding properties, stabilisers, pigmenmts, dyes, agents to improve the flow properties (for example, small concentrations, i.e. not more than 10 parts by weight, of polystyrene), reinforcing fibres, for example, glass fibres or synthetic resin fibres and mould-release agents. The polymer mixture according to the invention can be obtained accrding to any known technique of preparing polymer mixtures which comprise a polyphenylene ether. The individual constituents are preferably mixed in the melt (compounded) collectively in an extruder. The extrudate (in strand form) emanating from the extruder is then chopped up to form pellets. The pellets may be further processed, for example, in an injection moulding machine. Examples I to VI and comparative examples A and B Various polymer mixtures were prepared while using the following constituents: PPE: a polyphenylene ether, namely poly(2,6-dimethyl-1,4-phenylene)ether, having an intrinsic viscosity of 40 ml/g measured in chloroform at 25°C. PO: a polyoctenylene, namely a product which is commercially available as "VESTENAMER®". SEBS: a styrene-ethylene butylene-styrene triblock copolymer having a styrene content of approximately 29% and an overall molecular weight of approximately 110.000. PE: a polyethylene, namely an LPDE having a melt index of approximately 20 g/min. measured according to ISO R 292. RDP: tetraphenyl resorcinol diphosphate. H₃BO₃: a master batch with boric acid/polystyrene/polyethylene in the ratio of 30/65/5. TiO₂: conventional quality. BaSO₄: conventional quality. The various constituents were compounded in the quantities as indicated in the table hereinafter in a Werner Pfleiderer double blade extruder (adjusted at 300 (average) °C; speed of revolution of blade: 250 rpm). Furthermore, rods were injection-moulded to determine the Izod notched impact strength. The results obtained in the measurement (room temperature) are also recorded in the table. It may be seen from the table that the addition of TiO₂ or BaSO₄ to polymer mixtures which comprise a polyphenylene ether and a polyoctenylene leads to an increase of the notched impact strength. This applies in particular to TiO₂. The addition of too large quantities of BaSO₄ (example VI) or TiO₂ (example IV) leads to a decrease. Based on the recorded results (examples III and IV on the one hand and V and VI on the other hand) there exists an optimum for the quantity of TiO₂ or BaSO₄. It is therefore recommendable to add not more than 20 parts by weight of TiO₂ or BaSO₄ per 100 parts by weight of polyphenylene plus polyoctenylene.

Claims: A polymer mixture which comprises A. a polyphenylene ether and B. a polyoctenylene, in which the polymer mixture comprises 1-60 parts by weight of TiO₂ or BaSO₄ per 100 parts by weight of A + B. A polymer mixture as claimed in Claim 1, characterised in that the polymer mixture comprises A. 75-99.5 % by weight of polyphenylene ether and B. 25-0.5% by weight of polyoctenylene, calculated with respect to the sum of the parts by weight of A + B. A polymer mixture as claimed in Claim 2, characterised in that the polymer mixture comprises 0-50 parts by weight of additives per 100 parts by weight of A + B. Articles formed from the polymer mixture according to the invention.

Inventors: BAILLY CHRISTIAN MARIA EMILE, HOEKS THEODORUS LAMBERTUS, LOHMEIJER JOHANNES HUBERTUS GA, ROOVERS WILHELMUS MARINUS MARI, BAILLY, CHRISTIAN MARIA EMILE, HOEKS, THEODORUS LAMBERTUS, LOHMEIJER, JOHANNES HUBERTUS GABRIEL MARIE, ROOVERS, WILHELMUS MARINUS MARIA
Applicants: GEN ELECTRIC, GENERAL ELECTRIC COMPANY
Application year: 1991
Main classification: C08L71
IPC codes: C08L65, C08L71, C08K3