Acrylate esters of 1,1,1-trishydroxyphenylethane

Abstract: Novel mono-, di- or tri-acrylate esters of 1,1,1-trishydroxyphenylethane are produced by acrylating 1, 1,1-tris (4′-hydroxyphenyl) ethane. The esters may be polymerized or copolymerized in the presence of a free-radical polymerization initiator.

Description: The present invention relates to acrylate esters of 1,1,1-trishydroxyphenylethane (THPE) or more particularly to mono-, di-, and triacrylated esters of THPE. The invention also relates to a process for their preparation, their use as multifunctional polymerizable monomers, and homo- and copolymers produced therefrom. Such compounds find use in the production of protective coating compositions, adhesives, photosensitive compositions, and the like. Background of the invention Acrylate esters of 1,1,1-trishydroxyphenylethane may be produced by reacting 1,1,1-tris(4′-hydroxyphenyl) ethane with an acrylating agent as hereinafter described. It is known in the art that the intermediate 1,1,1-tris(4′-hydroxyphenyl) ethane may be produced by reacting 4-hydroxyacetophenone with phenol. Typically this is performed with phenol also used as the solvent for the mixture. THPE itself may be produced according to a method described in U.S. patent application 07/478,072, filed February 9, 1990, and European patent application EP-A-0 441 648, filed 8 February 1991. According to that disclosure, very pure THPE is obtained by washing a crude reaction mixture of 4-hydroxyacetophenone and phenol with a THPE saturated wash/methanol liquid prior to a recrystallization. It has been found that by use of such a wash yields of pure white THPE are good, and solvents have a more productive use. As a result of the process, most of the color bodies are removed in the wash stage where the color of the crude THPE changes from a dark rusty color to a light tan. The balance is removed in the recrystallization. With crude THPE washed with recycled recrystallization filtrate, only a single recrystallization from methanol/water is necessary to meet white color and high purity requirements. This recrystallization is basically a precipitation of THPE from the methanol/water solution. By acrylating THPE, one produces the inventive monomeric mono-, di- or tri-acrylate esters of 1,1,1-trishydroxyphenylethane. These may be polymerized, copolymerized and/or crosslinked by the use of known free radical polymerization and crosslinking techniques. Summary of the Invention The invention provides, as a composition of matter, mono-, di- and tri-acrylate esters of 1,1,1-trishydroxyphenylethane. The invention also provides a method for the production of acrylate esters of 1,1,1-trishydroxyphenylethane which comprises acrylating 1,1,1-tris(4′-hydroxyphenyl)ethane. The inventive compounds have the general formula where  = a phenylene group X = -OH or and R = H, alkyl or aryl, preferably C₁-C₆ alkyl or C₆-C₁₀ aryl. The invention also comprises homopolymers and copolymers of these monomers as well as a method for preparing such homopolymers and copolymers by free radical initiating the monomers. Articles may be prepared by disposing such compositions on substrates such as metals, plastics, and the like. Detailed Description of the Preferred Embodiment As hereinbefore mentioned, the production of 1,1,1-tris(4′-hydroxyphenyl)ethane may be performed by the reaction of 4-hydroxyacetophenone with phenol, wherein phenol is the supporting solvent as well as a reagent. The reaction takes place under catalytic conditions, with hydrochloric acid and beta-mercaptopropionic acid as preferred co-catalyst. The resulting reaction product contains significant amounts of impurities which are removed as described hereinafter. An impure, substantially solid crude admixture of freshly produced THPE contains 1,1,1-tris(4′-hydroxyphenyl)ethane (THPE), residual 4-hydroxyacetophenone, phenol, chlorides, THPE isomers, bis-(hydroxyphenyl)ethene isomers, color bodies and other unidentified parts which are sought to be removed. 1,1,1-Tris(4′-hydroxyphenyl)ethane may be obtained from a substantially solid crude admixture containing 1,1,1-tris(4′-hydroxyphenyl)ethane and the impurities resulting from the catalytic production of 1,1,1-tris(4′-hydroxyphenyl)ethane from 4-hydroxyacetophenone and phenol. The THPE purification method proceeds by: a) washing the crude admixture with a saturated solution of 1,1,1-tris(4′-hydroxyphenyl)ethane in a solute comprising from 60% to 75% by weight of water and from 25% to 40% by weight of methanol; and b) isolating the washed crude admixture from the formed effluent washing composition, and dissolving the washed crude admixture in methanol, and c) adding sufficient water and sodium borohydride to the dissolved, washed crude admixture to form a precipitate of 1,1,1-tris(4′-hydroxyphenyl)ethane, and d) filtering the precipitate to thereby form a purified 1,1,1-tris(4′-hydroxyphenyl)ethane and a filtrate; and e) rinsing the resultant filtered precipitate of 1,1,1-tris(4′-hydroxyphenyl)ethane with a solution of sufficient methanol and water, which optionally contains 1,1,1-tris(4′-hydroxyphenyl)ethane up to the saturation point, and conducting the rinsing for a sufficient time to remove substantially all residual colored impurities from the precipitate. In the first step of the purification method, one washes the crude admixture with a saturated solution of 1,1,1-tris(4′-hydroxyphenyl)ethane in a solute comprising from 60% to 75% by weight of water and from 25% to 40% by weight of methanol. Preferably this washing is conducted in several washing steps. It has been found that by employing a saturated solution of THPE in the washing solution, that THPE loss from the crude admixture is substantially reduced. Prior to washing, the crude admixture typically contains from 15% to 30% by weight of residual phenol. Since-phenol is a good solvent for THPE, it is desired to reduce the phenol content prior to the washing step simply by vacuum draw of the phenol. However, it has been found that if too much phenol is drawn off, that although the THPE recovery is good, the purity of the product is unsatisfactory. Loss of THPE during the wash of the crude admixture is basically caused by the presence of phenol although the washing solution is THPE saturated. Phenol content may be controlled by pumping off the crude admixture before the wash or by use of a hot nitrogen flow through the crude admixture to cause the phenol, which is the most volatile component, to leave the system before the wash. Generally it is desired to obtain THPE with a 99.5% or greater purity and having a whiteness measure (APHA) of 200 or less, preferably 150 or less. Therefore a phenol content of at least 1.0% and up to 30.0% based on the weight of the crude admixture is desired. More preferably the phenol content is adjusted to from 4.0% to 10% and most preferably from 4.5% to 7.5%. A single most preferred phenol content is 5.0%. Therefore, in the most preferred case, the phenol content of the crude admixture is first adjusted to these levels before conducting the washing step. Next, after the washing step, one isolates the washed crude admixture from the formed effluent washing composition. This can be done by performing the washing on a filter plate while stirring and then drawing down the filtrate. The solid, washed crude admixture is then dissolved in sufficient methanol to effect a dissolution. One then adds sufficient water and sodium borohydride to reduce the dissolved, washed crude admixture and to form a precipitate of 1,1,1-tris(4′-hydroxyphenyl)ethane. The sodium borohydride also acts as a pH adjusting reagent during the recrystallization. In the preferred embodiment, the amount of sodium borohydride added ranges from 0.0003% to 0.3%, preferably from 0.003% to 0.07% and most preferably from 0.01% to 0.03% based on the weight of methanol and water. If the phenol content in the crude admixture has been reduced prior to washing, it is preferred that sodium borohydride is added to the methanolic solution THPE solution. After stirring, carbon in the form of charcoal, is added to the methanolic THPE solution and filtered off prior to having added more sodium borohydride plus water. This is most advantageous when the phenol content has been reduced to 15% or less in the pre-washed crude admixture. In the preferred embodiment, the amount of carbon added ranges from 0.001% to 1.0%, preferably from 0.01% to 0.8%, and most preferably from 0.05% to 0.3% based on the weight of methanol. One then filters the precipitate to thereby form a purified, recrystallized 1,1,1-tris(4′-hydroxyphenyl)ethane and a filtrate. The next step is rinsing the resultant filtered precipitate of 1,1,1-tris(4′-hydroxyphenyl)ethane with a solution of sufficient methanol and water, which optionally contains 1,1,1-tris(4′-hydroxyphenyl)ethane up to the saturation point, and conducting the rinsing for a sufficient time to remove substantially all residual colored impurities from said precipitate. The rinse mixture preferably comprises water and methanol in a 2:1 to 6:1 weight ratio. One may perform an optional stabilizing rinse with an aqueous sodium dithionate solution at this stage. Typical sodium dithionate solutions may range from 0.01% to 1.0%, preferably from 0.05% to 0.5% by weight in water. Finally, the product is dried. It has been found that one may use this colored, resultant filtrate as the washing solution in the washing step of another crude admixture batch. Although this filtrate contains sodium borohydride and removed, colored bodies and other impurities in addition to water, methanol and THPE, it has been found that these are substantially removed in the effluent of the washing step. If the filtrate color is pink one should treat it with sodium dithionate to change it to a light yellow color prior to using the filtrate to wash the next batch of crude admixture. A suitable amount is about 0.1 weight percent of saturated aqueous sodium dithionate. Therefore, this filtrate serves double duty in the overall process and significantly reduces the amount of fluids which must be recycled or treated before ultimate discharge. The acrylate esters of 1,1,1-trishydroxyphenylethane may be produced by reacting the 1,1,1-tris(4′-hydroxyphenyl)ethane with an acrylating agent under suitable reaction conditions. The degree of esterification may be controlled by regulating the amount of the acrylating agent used. The most preferred acrylating agent is acryloyl chloride. The monomer may be polymerized by a free radical initiation process to produce homopolymers such that it has a molecular weight in the range of from 200,000 to 10,000,000 preferably from 200,000 to 1,000,000 or more preferably 500,000 to 1,000,000. It is predicted that essentially any free radical initiation system will serve for this purpose. One free radical initiation method is by photopolymerization wherein the acrylated THPE is admixed with a photopolymerization initiator in a suitable solvent composition and thereafter exposed to light. One preferred free radical initiator is azoisobutyronitrile. Other azo type initiators are also suitable. Still others non-exclusively include peroxides such as benzoyl peroxide, and di-t-butyl peroxide. Free radical liberating photoinitiators include any compound which liberates free radicals on stimulation by actinic radiation. Preferred photoinitiators nonexclusively include quinoxaline compounds as described in U. S. Patent 3,765,898; the vicinal polyketaldonyl compounds in U. S. Patent 2,367,660; the alpha-carbonyls in U.S. Patents 2,367,661 and 2,367,670; the acyloin ethers in U. S. Patent 2,448,828; the triarylimidazolyl dimers in U. S. Patent 3,479,185; the alpha-hydrocarbon substituted aromatic acyloins in U. S. Patent 2,722,512; polynuclear quinones in U. S. Patents 2,951,758 and 3,046,127; and s-triazines in U. S. Patent 4,656,272. In the practice of the present invention, the photoinitiator component is preferably blended with the acrylated THPE, in a suitable solvent composition, an amount ranging from approximately 2% to 30% based on the weight of the solids in the mixture. A more preferred range is from approximately 6% to 20%. The polymer set forth above is preferably a homopolymer, but it may also be a copolymer wherein the co-monomers are units of styrene, acrylates, methacrylates and maleimides. The co-monomer unit may optionally be substituted with a variety of pendant groups in order to adjust the properties of the compound as desired by the user. Specifically, the aforementioned acrylated THPE monomer may be co- or terpolymerized under the foregoing polymerization conditions in the presence of one or more additional monomers which may be ethylenically unsaturated compounds, acetoxystyrene, substituted acetoxystyrene, hydroxystyrene, substituted hydroxystyrene, maleic anhydride, maleimides, styrene, acrylates and methacrylates such as methyl methacrylate, and butyl acrylate wherein the copolymer or terpolymer has an average molecular weight in the range given above. Preferably the acrylated THPE monomer is co-polymerized with a compound which is an addition polymerizable, nongaseous (boiling temperature above 100°C at normal atmospheric pressure), ethylenically unsaturated compound containing at least two terminal ethylenically unsaturated groups, which is capable of forming a high molecular weight polymer by free radical initiated, chain propagating addition polymerization. Suitable polymerizable materials nonexclusively include triethylene glycol dimethacrylate, tripropylene glycol diacrylate, tetraethylene glycol dimethacrylate, diethylene glycol dimethacrylate, 1,4-butanediol diacrylate, 1,6-hexanediol dimethacrylate, pentaerythritol tetraacrylate, trimethylol propane triacrylate, trimethylol propane trimethacrylate, di-pentaerythritol monohydroxypentaacrylate, pentaerythritol triacrylate, bisphenol A ethoxylate dimethacrylate, trimethylolpropane ethoxylate triacrylate, and trimethylolpropane propoxylate triacrylate. One may employ the foregoing homopolymers, copolymers and terpolymers in protective surface coatings and adhesive blends. They may also be used in admixture with a photosensitizing agent to form a photographic element such as a photoresist. In the production of a photosensitive composition and photographic element, one blends the above produced polymer with a photosensitizer and a suitable solvent until a homogeneous solution is formed. The solution is then coated on a suitable substrate and dried until it is non-tacky. It is then imagewise exposed to light and developed. Photosensitizers are known to the skilled artisan as demonstrated by Light Sensitive Systems, Kosar, J.; John Wiley & Sons, New York, 1965. The monomer may also be used as a component of a photopolymerizable element wherein the monomer, initiator and a solvent are coated on a support, dried, and imagewise exposed to light with subsequent development. In another embodiment, the acrylated polymer may be crosslinked by admixture with a crosslinking agent with subsequent heating. In one case the acrylated THPE polymer and crosslinking agent are mixed, coated on a support, and crosslinked with heat in the presence of a catalytic amount of an acid. The crosslinking component is a compound, which when in the presence of heat, and preferably a catalytic amount of acid, is capable of crosslinking the foregoing acrylated THPE polymer. Crosslinking compounds for such use have the general formula R′O-CH₂-A-CH₂-OR′ wherein A is a monomeric, aromatic hydrocarbon having one or more fused or unfused, separated or unseparated rings and each R unit is independently H, (C₁-C₆)alkyl, (C₃-C₆) cycloalkyl, aryl or arylalkyl. The preferred crosslinking compound is dimethylol paracresol as described in U.S. 4,404,272, and its ether and ester derivatives including phenol, 2,6-bis(hydroxyethyl)-4-methyl; benzene, 1-methoxy-2,6-bis-(hydroxymethyl-4-methyl; phenol, 2,6-bis(methoxymethyl)-4-methyl; and benzene, 1-methoxy-2,6-bis(methoxymethyl)-4-methyl; methyl methoxy diphenyl ether, melamine formaldehyde resins and compounds and alkylated analogous thereof having 1 to about 3 monomer units such as those typically sold under the trade names Cymel from American Cyanamid and Resimene from the Monsanto Company, for example hexamethylol melamine hexamethyl ether. In the preferred photoresist composition, the crosslinking compound is present in a mixture with the acrylated THPE monomer, polymer or copolymer in an amount of from 0.5 to 7 weight percent of the solid components of the composition, more preferably from 2 to 6 weight percent, and most preferably from 3 to 5 weight percent. The following non-limiting examples serve to illustrate the invention. Example 1 1,1,1,-tris(4′-acryloxyphenyl)ethane 318 g (1.04 mol) 1,1,1-Trishydroxyphenylethane, 314 g (3.08 mol) triethylamine, 0.75 g methylhydroquinone and 500 ml of methylene chloride are added to a 5 liter flask and cooled to 0°C. A mixture of 300 g (3.3 mol) of acryloyl chloride, and 1300 ml of methylene chloride are added over a four hour period while maintaining the temperature at 0°C. When the mixing is complete, the mixture is allowed to warm to room temperature and stirred overnight. Several liters of water are added to precipitate triethylammonium hydrochloride. The organic phase is separated and dried over magnesium sulfate. After adding an additional 0.25 grams of methylhydroquinone, the organic phase is evaporated using an air sparge, affording a light yellow viscous liquid. Example 2 1,1,1-tris(4′-acryloxyphenyl)ethane 30.6 g (0.1 mol) of 1,1,1-trishydroxyphenylethane, 30.3 g (0.3 mol) of triethylamine, 0.25 grams of methylhydroquinone and 150 ml of tetrahydrofuran are added to a flask at 0°C. A mixture of 27.5 g (0.3 mol) of acryloyl chloride and 50 ml of tetrahydrofuran are added over three hours and left to stir overnight. 200-300 ml of water are added. The tetrahydrofuran solution is precipitated, evaporated and dried to yield 48-49 grams of a thick, light yellow liquid. Example 3 111.3 grams of 1,1,1-trishydroxyphenylethane, 110.2 grams of triethylamine, 0.25 grams of methylhydroquinone and 200 ml of methylene chloride are added to a flask at 0°C. Then 100 grams of acryloyl chloride, and 500 ml of methylene chloride are added over four hours to yield a light yellow solution with a heavy precipitate. Two liters of water are added. The methylene chloride is extracted and the mixture is dried. 0.25 grams of methylhydroquinone are added and the mixture is evaporated under an oxygen sparge.

Claims: Mono-, di- and tri- acrylate esters of 1,1,1-trishydroxyphenylethane having the formula where  = a phenylene group X = -OH or and R = H, alkyl or aryl. The acrylated esters of claim 1 wherein R is C₁-C₆ alkyl or C₆-C₁₀ aryl. The acrylated esters of claim 1 wherein each X is A composition which comprises in admixture (a) a mono-, di- and tri- acrylate esters of 1,1,1-trishydroxyphenylethane having the formula where  = a phenylene group X = -OH or and R = H, alkyl or aryl (b) one or more compounds selected from the group consisting of free radical polymerization initiators and crosslinking agents. An article which comprises the composition of claim 4 disposed upon a substrate. The composition of claim 4 comprising a free radical polymerization initiator selected from the group consisting of an azo compound, a peroxide, quinoxaline compounds, polyketaldonyl compounds, alpha-carbonyl compounds, acyloin ethers, triarylimidazolyl dimers, alpha-hydrocarbon substituted aromatic acyloins, polynuclear quinones, and s-triazines. The composition of claim 4 comprising a crosslinking compound having the general formula R′O-CH₂-A-CH₂-OR′ wherein A is a monomeric, aromatic hydrocarbon having one or more fused or unfused, separated or unseparated rings and each R′ unit is independently H, (C₁-C₆)alkyl, (C₃-C₆) cycloalkyl, aryl or arylalkyl. The composition of claim 4 wherein R is C₁-C₆ alkyl or C₆-C₁₀ aryl. The composition of claim 4 wherein each X is A polymer or copolymer of the formula Where  = a phenylene group X = -OH, R = H, alkyl or aryl Y is selected from the group consisting of a residue of and the residue of an ethylenically unsaturated compound; and n is selected to yield a polymer having a molecular weight in the range of from 200,000 to 10,000,000. The polymer of claim 10 wherein R is C₁-C₆ alkyl or C₆-C₁₀ aryl. The polymer of claim 10 wherein each X is The polymer of claim 10 wherein Y is a residue of The polymer of claim 13 wherein R is C₁-C₆ alkyl or C₆-C₁₀ aryl. The polymer of claim 13 wherein each X is A copolymer according to claim 10 wherein Y is selected from the group consisting of a residue of acetoxystyrene, hydroxystyrene, maleic anhydride, maleimides, styrene, acrylates and methacrylates. A composition comprising the polymer or copolymer of claim 10 in admixture with a crosslinking compound. The composition of claim 17 wherein the crosslinking compound has the formula R′O-CH₂-A-CH₂-OR′ wherein A is a monomeric, aromatic hydrocarbon having one or more fused or unfused, separated or unseparated rings and each R′ unit is independently H, (C₁-C₆)alkyl, (C₃-C₆) cycloalkyl, aryl or arylalkyl. An article which comprises the composition of claim 17 disposed upon a substrate. A method for the production of mono-, di- and tri-acrylate esters of 1,1,1-trishydroxyphenylethane having the formula where  = a phenylene group X = -OH or and R = H, alkyl or aryl which comprises reacting about one equivalent of 1,1,1-tris(4′-hydroxyphenyl)ethane with from about 1 to about 3 equivalents of an acrylating agent in an amount sufficient and for a sufficient time, and at a sufficient temperature to produce an acrylate ester of 1,1,1-trishydroxyhenylethane. The method of claim 20 wherein R is C₁-C₆ alkyl or C₆-C₁₀ aryl. The method of claim 21 wherein each X is The method of claim 21 wherein the acrylating agent is acryloyl chloride. A method of producing a polymer or copolymer of the formula which comprises free radical polymerizing a compound having the formula with a compound Y which is selected from the group consisting of a residue of and the residue of an ethylenically unsaturated compound; where  = a phenylene group X = -OH, and R = H, alkyl or aryl; and n is selected to yield a polymer having a molecular weight in the range of from 200,000 to 10,000,000. The method of claim 24 which is conducted with a free radical polymerization initiator selected from the group consisting of an azo compound, a peroxide, quinoxaline compounds, polyketaldonyl compounds, alpha-carbonyl compounds, acyloin ethers, triarylimidazolyl dimers, alpha-hydrocarbon substituted aromatic acyloins, polynuclear quinones, and s-triazines.

Inventors: JOHNSON THOMAS S, MOTT GRAHAM N, JOHNSON, THOMAS S., MOTT, GRAHAM N.
Applicants: HOECHST CELANESE CORP, HOECHST CELANESE CORPORATION
Application year: 1991
Main classification: C07C69
IPC codes: C08L33, C08F20, C07C69, C07C67, C08F220