Coating method and apparatus for magnetic recording medium

Abstract: An apparatus for coating on a support a first magnetic coating solution so as to form a lower layer on the support continuously travelling and then coating a second magnetic coating solution on the first magnetic coating solution, which is in a non-dried state, so as to form an upper layer thereon to thereby produce a two-layer type magnetic recording medium. The apparatus comprises a first die for coating the first magnetic coating solution which includes first and second lip portions, the second lip portion having a top surface curved. The apparatus further comprises a second die for coating the second magnetic coating solution which includes first and second lip portions, the second lip portion similarly having a top surface curved. The first lip portion of each of said first and second dies has an edge A and the second lip portion has at both ends of the curved top surface edges B and C. The edge B is formed to be in confronting relation to the edge A of the first lip portion. The edge A of the first lip portion is arranged to be substantially on a tangential line of the edge B of the second lip portion and the support is arranged to be travelled so as to approach each die at a loading angle to be substantially parallel to the tangential line of the edge B of the second lip portion and to be separated therefrom at an unloading angle to be substantially parallel to an tangential line of the edge C of said second lip portion.

Description: The present invention relates generally to a coating method and apparatus for magnetic recording media such as a magnetic tape and a floppy disk, and more particularly to such a coating method and apparatus for successively forming two layers in a non-dried state. In accordance with the requirement for heightening the performance of the magnetic recording media, there is recently noted a multi-layer-structurized magnetic recording medium such as a video magnetic recording medium having two magnetic layers. As the upper layer there is provided a magnetic layer for the high-density recording which has an excellent characteristic of magneto-electric conversion at higher-frequencies, and as the lower layer there is provided a magnetic layer which has an excellent characteristic of magneto-electric conversion at lower-frequencies Unlike the conventional single-layer structure, this arrangement can provide a magnetic recording medium having an excellent characteristic of magneto-electric conversion over a wide frequency range. In order to simplify the manufacturing process of such a two-layer video magnetic recording medium, it is preferable to form the two layers by performing the coating and drying at the same time such as disclosed in the Japanese Patent Provisional Publication No. 62-124631. There is a problem with such a conventional coating method and apparatus, however, in that fine stripes elongated in the longitudinal directions of a support (a stripe pattern of uneven coating on the coating surface) can appear on the coated surface in cases where the high-density recording magnetic coating solution is coated repeatedly so as to form plural layers. This problem has been revealed by a study made by the inventors of this invention. Fig. 1 shows a coating result obtained by performing the calendering process after coating as the upper layer a magnetic coating solution as shown in a table 1 and successively coating as the lower layer a magnetic coating solution as shown in a table 2 on a polyethylene terephthalate film with a thickness of 14 µm in accordance with the conventional coating technique, the magnetic coating solution for the upper layer being coated thereon so that the layer thickness is 0.5 µm in the dried state and the magnetic coating solution for the lower layer being coated thereon so that the layer thickness is 3 µm in the dried state. In Fig. 1, the coated surface is measured by means of a 3-dimension surface profile analizer. For making obvious the height portions of the coated surface for the 3-dimensional display, there are output only the portions higher than the average value in the height direction. According to the measurement result, the stripe pattern is seen on the coated surface at a pitch of about 50 µm in the longitudinal directions of the support (the base film). Further, in Fig. 1, the average surface roughness (RMS) of the coated surface has been seen to be 15.8 nm. When the characteristic of magneto-electric conversion is measured by means of a MII format deck, the video band output (7 MHz) is -2 dB with respect to the Applicant reference tape and the S/N ratio is -1 dB. It is clear from the aforementioned result that the longitudinally elongated stripes can extremely deteriorate the characteristic of magneto-electric conversion. Magnetic Alloy Powder Lengthwise Size o.18 µm Average Size Ratio 1 : 12 100 wt % σs 128 emu/g Hc 1530 Oe Conductive Carbon 2 wt % Polyeurethane Resin 10 wt % Chloroethylene-vinyl acetate copolymer 10 wt % Alumina (α-Al₂O₃) 5 wt % Stearic Acid 2 wt % Butyl Stearate 2 wt % Methyl Ethyl Ketone 200 wt % Toluene 180 wt % Cyclohexanone 40 wt % According to the research of the inventors of this invention, this is due to the following causes. That is, the magnetic powder particles of the magnetic coating solution tend to be combined with each other by means of the magnetic attraction force, and therefore they are not presented as the first-order particles but form 3-dimensional network structures. In response to a shearing force being applied, the 3-dimensional network structures can be considered to be broken so as to form flocculations having a given size ("Tosokogaku", Vol.21 No.10 P475-479, 1986). since the magnetic coating solution including a magnetic powder such as an magnetic alloy powder having a strong magnetic force or a magnetic powder having a small lengthwise average size of acicular particle has an extremely strong cohesive force, the above-mentioned flocculations can be considered to be present in the flowing magnetic coating solution in orders of several tens to hundred µm. When coating this magnetic coating solution on a support in accordance with the conventional coating technique, as illustrated in Fig. 2 the above-mentioned flocculation is pushed out from a liquid pocket of a die 5 onto a second lip 2. This causes the generation of the stripe pattern of uneven coating on the coating surface. In Fig. 2, numeral 1 represents a first lip, 3 designates a manifold, 4 depicts a slit, 6 denotes a pump, 7 indicates a magnetic coating solution and 8 is a support. In addition, the generation of the stripe pattern tends to more easily and clearly occur as the magnetic powder of the magnetic coating solution to be coated has a stronger magnetic force and a smaller lengthwise average particle size of acicular particle. Recently, in order to meet the requirements to increase the recording density of the video magnetic recording medium, for the upper layer there is used a magnetic coating solution including an extremely fine magnetic powder having a high magnetic force. Thus, the characteristic of magneto-electric conversion such as the video band output and S/N is considerably deteriorated due to the stripe pattern of uneven coating on the coating surface, thereby reducing the quality of the article. It is therefore an aim of the present invention to provide a coating method and apparatus which is capable of making a smooth coated surface of a magnetic recording medium, particularly a multi-layer structurized magnetic recording medium. In accordance with the present invention, there is provided a method of coating a magnetic coating solution on a continuously moving support using a die including a first lip portion, a second lip portion, and a slit and a manifold between the first and second lip portions, the method comprising the steps of: causing the support to approach the first lip portion in a direction substantially parallel to the tangent to the second lip portion at a second edge thereof adjacent to the slit; a first edge of the first lip portion adjacent to the slit lying on said tangent; causing magnetic solution to flow through the slit from the manifold so as to coat the support at the exit of the slit; and causing the support to leave the second lip portion in a direction substantially parallel to the tangent to the second lip portion at a third edge thereof opposite to the second edge beyond a curved top surface of the second lip portion. In accordance with the present invention, there is further provided an apparatus for coating a magnetic coating solution on a continuously moving support comprising: a die including: first and second confronting lip portions; a slit and a manifold between the first and second lip portions; the first lip portion having a first edge adjacent to the slit; the second lip portion having a second edge opposing the first edge across the slit, the first edge lying on a first tangent to the second lip portion at the second edge and the remainder of the first lip portion being spaced from the first tangent; and the second lip portion having a third edge at the other side of a curved top surface of the second lip portion to the second edge; and means for causing the support to approach the first lip portion in a direction substantially parallel to the first tangent and to leave the second lip portion in a direction substantially parallel to a second tangent thereto at the third edge. Preferably, an arc-length BC of the curved top surface of the second lip portion of each of the first and second dies in the travelling direction of the support is determined to be in the range of 2 mm ≤ BC ≤ 7 mm. The radius of curvature R of the curved top surface of the second lip of each of the first and second dies is determined to be in the range of 4 mm ≤ R ≤ 20 mm. Further, the length of the slit of the first and second dies in the travelling direction of the support is determined to be in a range of 0.1 mm and 0.5 mm, and a manifold is formed at a portion of the slit of the first and second dies and a length between the exit of the manifold and the top of the slit is determined to be in a range between 20 mm and 100 mm, and the first and second lip portions are respectively made of a cemented carbide. Still further, the liquid pocket for the magnetic coating solution is formed only at a portion between the exit of the slit and the second lip top surface so as to generate a shearing force between the slit side edge B or top surface of the second lip portion and the support to break the generated flocculations. The aims and features of the present invention will become more readily apparent from the following detailed description of an exemplary embodiment when taken in conjunction with the accompanying drawings in which: Fig. 1 is an illustration of a coated surface to be obtained in accordance with a conventional technique; Fig. 2 is a cross-sectional view showing a coating state due to a conventional die; Fig. 3 is a cross-sectional view showing apparatus according to an embodiment of the present invention; Fig. 4 is a cross-sectional view showing a coating state due to the apparatus according to the embodiment of this invention; and Fig. 5 is an illustration of a coated surface to be obtained in accordance with the embodiment of this invention. Referring now to Fig. 3, there is schematically illustrated a cross section of a first die for coating a magnetic coating solution on a support (base film). A second die substantially has the same structure as the first die and hence the description will be made only in terms of the first die. In Fig. 3, illustrated at numerals 1 and 2 are first and second lips, the top of the second lip 2 having a curved surface and its radius of curvature R being arranged to be 4 to 20 mm. The radius of curvature R is adequately determined under the conditions such as the viscosity of the magnetic coating solution, coating speed, coated-layer thickness and tension of the support. In the case that the radius of curvature R is below 4 mm, difficulty is encountered to float the support from the second lip 2 curved surface because the pressure to be applied to the coating solution from the support becomes excessive with respect to the coating solution flowing through between the second lip 2 curved surface and the support. On the other hand, in the case that the radius of curvature R is above 20 mm, difficulty is encountered to remove air from the coated layer because the pressure to be applied to the coating solution from the support becomes too small with respect to the coating solution flowing therebetween. The adequate determination of the radius of curvature R allows uniformly coating the coating solution with a predetermined thickness without involving air accompanied by the support. As a material for the first and second lips 1 and 2 there is used a cemented carbide. The use of the cemented carbide permits finishing the straightness and flatness of the lips 1 and 2 in units of several µm and further preventing burr and wear which can be developed at the exit end portion of the second lip 2 when machining a stainless steel, for example. As a result, even in the case of performing a thin film coating, the unevenness of the thickness in the width directions of the support does not occur and further lengthwise stripes on a coated film surface which can be developed due to the burr and wear of edge portions do not occur to allow adequate coating. A manifold, illustrated at numeral 3, is arranged so as to penetrate the coating device in directions (coating width directions) perpendicular to the coating direction. The cross-sectional sectional configuration of the manifold 3 may be arranged to be circular or semi-circular. Illustrated at numeral 4 is a slit whose gap length is generally set to be 0.1 to 0.5 mm and whose length in the width directions is substantially equal to the coating width of the coating device. In cases where the gap length thereof is below the aforementioned range, the hydrodynamic resistance of the coating solution flowing through the slit 4 becomes high whereby the discharge of the coating solution in the coating width directions becomes non-uniform so as to result in the unevenness of the film thickness in the coating width direction. Further, when the gap length is above the above-mentioned range, the flow of the coating solution is disordered at the exit end of the slit 4 so as to make it difficult to uniformly coat the coating solution. The length from the manifold 3 to the slit 4 exit may be determined under the conditions such as the viscosity of the coating solution (taking into account the thixotropic nature) and discharging amount of the coating solution from the coating device, generally 20 to 100 mm. The top configuration of a first lip 1 confronting the second lip 2 through the slit 4 is arranged to have any one selected from a curved surface, flat surface, polygon surface and others. Fig. 4 is a cross-sectional view of the first die 5 for describing a coating method and apparatus according to this embodiment where the coating is effected by a first die 5 for the lower layer. In Fig. 4, a support illustrated at numeral 8 approaches the die 5 at an angle (loading angle) so as to be substantially parallel to the tangential line E of a top point B of the second lip illustrated in Fig. 3. The adjustment of the loading angle angle of the support 8 to the die 5 is effected by a guide roller (not shown) provided at the upstream side of the first lip 1. The first lip 1 is arranged so that only its edge portion A is arranged to upwardly exceeds the tangential line E or be on the tangential line E as illustrated in Fig. 3. This arrangement prevents the first lip 1 from coming into contact with the support 8 so as to prevent damages of the support 8. Moreover, the support 8 separates from the die 5 at an angle (unloading angle) so as to be substantially parallel to the tangential line of the other edge portion C (see Fig. 3) of the second lip 2. The adjustment of the unloading angle of the support 8 is made by means of another guide roller (not shown) provided at the downstream side of the second lip 2. A magnetic coating solution 7 for the lower layer is successively supplied into the manifold 3 through a pump 6 by an coating amount for the support 8 and the coating solution is forced out by means of a liquid pressure in the manifold 3 through the slit 4 up to the outside of the die 5. Here, as described above, in the coating solution 7 for the upper layer to be forced out in the subsequent coating process by the second die there are presented the flocculations comprising the magnetic powder particles. However, since the loading angle of the support 8 with respect to the die 5 is arranged as described above, the distance between the lower layer attached to the support 8 and the slit side edge portion B of the second lip 3 can be kept to be substantially twice the coated film thickness for the lower layer in the wet state. That is, since the distance therebetween is smaller as compared with the size of the flocculations, a strong shearing force is applied to the flocculations which are in turn broken finely so as to prevent the great flocculation from advancing onto the top surface of the second lip 2 as it is, thereby suppressing the generation of the above-described stripe pattern on the coated film surface. In addition, according to the researches of this inventors, it is proven that the length BC of the second lip 2 top surface having an arc configuration greatly affects the smoothness of the coated surface and stability of the coating for the multi-layer-structurized magnetic recording medium. That is, in the case that the arc-length BC is shorter than 2 mm, since the time or distance for providing the shearing force with respect to the flocculations in the magnetic coating solution becomes short, it is impossible to sufficiently and finely break the flocculations whereby there is the possibility that there is remained the stripe pattern on the coated surface as illustrated in Fig. 1. On the other hand, when the arc-length BC is longer than 7 mm, the hydrodynamic resistance of the magnetic coating solution flowing through the gap between the support 8 and the second lip 2 curved surface excessively becomes great so as to generate the film thickness unevenness in the coating width directions to impede the stable coating thereon. Thus, the second lip 2 surface arc-length BC is preferable to be determined to be in a range of 2 mm ≦ BC ≦ 7 mm, thereby effectively suppressing the stripe pattern of uneven coating on the coating surface. Similarly, in the case of coating the upper layer by the second die, this arrangement permits preventing the generation of the stripe pattern. Example 1 After the magnetic coating solution for the lower layer as shown in the Table 2 is coated by the first die 5 on the support 8 continuously travelling so that the thickness of the film in the dried state becomes 3 µm, the magnetic coating solution for the upper layer as shown in the Table 1 is coated by the second die so that the thickness of the film in the dried state becomes 0.5 µm. The first and second dies are separated by 1 m from each other. The support 8 used is made of polyethylene terephthalate film and arranged to have a thickness of 14 µm, and the coating speed is 100 m/min, and the support tension is 200 g/cm. The radius of curvature R of the second lip 2 of the first die 5 is set to be 5 mm and the radius of curvature of the second lip of the second die is also set to be 5 mm. The arc-length BC of the second lip of the second die is fixedly set to be 3 mm and the arc-length BC of the second lip 2 of the first die 5 is changed as shown in the following Table 3. Arc-Length BC (mm) 1.5 mm 2 mm 7 mm 8 mm After coated and oriented in the support travelling direction, the drying process is performed. After dried, the smoothing process of the magnetic layer surface is effected by means of a calender and the magnetic layer is slit so as to have a predetermined width to thereby form a magnetic tape. In the case of BC = 8 mm, the film thickness unevenness occurs in the coating width directions. The coating surfaces of tapes formed with BC = 1.5, 2 and 7 mm are measured by means of a 3-dimension surface profile analizer. In the measurement results, in the case of BC = 1.5 mm, a stripe pattern of uneven coating as illustrated in Fig. 1 is generated on the coating surface. This is considered as the stripe pattern of uneven coating of the lower layer surface coated and formed by the first die provides the influence up to the upper layer. In the case of BC = 2 or 7 mm there is no generation of the stripe pattern of uneven coating. For instance, the coating surface state obtained in the case of BC = 2 mm becomes as illustrated in Fig. 5. Unlike the state as illustrated in Fig. 1, there is no stripe pattern of uneven coating on the coating surface, thereby allowing a multi-layer-structurized magnetic recording medium with an extremely smooth coating surface. A table 4 shows the measurement results, using the MII format deck, of the characteristics of magneto-electric conversion, i.e., the S/N ratio and output at the video band frequency 7 MHz, with respect to the magnetic recording media produced according to this embodiment and the magnetic recording medium produced according to the conventional coating technique. For the measurements of the characteristics of magneto-electric conversion, in order to make the comparison easy, a MII tape produced by this applicant is used as the reference tape. In the table 4 there are also shown surface roughnesses (RMS) measured by means of the 3-dimension surface profile analizer. Characteristic of Magneto-Electric Conversion RMS BC (mm) S/N Ratio Output (7 MHz) BC=1.5 -1.0 dB -1.5 dB 13.7 nm BC=2 +0.5 dB +1.0 dB 4.6 nm Example 1 BC=7 +0.5 dB +1.0 dB 5.0 nm BC=8 Uneven Coating Conventional Tape -1.0 dB -2.0 dB 15.8 nm Reference Tape 0 dB 0 dB 7.0 nm Since the coating surfaces of the tapes produced according to the coating technique of this embodiment, i.e., produced by the dies with the arc-lengths BC of 2 and 7 mm, are considerably smooth, as compared with that of the tape produced by the die with BC = 1.5 or produced according to the conventional coating technique, the surface roughness (RMS) is smaller and the reproduction output and S/N ratio are extremely superior. Example 2 After the magnetic coating solution for the lower layer as shown in the table 2 is coated by the first die on a support continuously travelling so that the film thickness in the dried state becomes 3 µm, the magnetic coating solution for the upper layer as shown in the table 1 is coated thereon by the second die so that the film thickness in the dried state becomes 0.5 µm. The distance between the first and second dies is set to be 1 m. The support used is made of a polyethylene terephthalate film and arranged to have a thickness of 14 µm, and the coating speed is 100 m/min, and the support tension is 200 g/cm. The radius of curvature R of the second lip of the first die is set to be 15 mm and the radius of curvature of the second lip of the second die is also set to be 15 mm. The arc-length BC of the second lip of the first die is fixedly set to be 3 mm and the arc-length BC of the second lip of the second die is changed as shown in the following Table 5. Arc-Length BC (mm) 1.5 mm 2 mm 7 mm 8 mm After coated and oriented in the support travelling direction, the drying process is performed. After dried, the smoothing process of the magnetic layer surface is effected by means of a calender and the magnetic layer is slit so as to have a predetermined width to thereby form a magnetic tape. In the case of BC = 8 mm, the film thickness unevenness occurs in the coating width directions. The coating surfaces of tapes formed with BC = 1.5, 2 and 7 mm are measured by means of a 3-dimension surface profile analizer. In the measurement results, in the case of BC = 1.5 mm, a stripe pattern of uneven coating as illustrated in Fig. 1 is generated on the coating surface. In the case of BC = 2 or 7 mm there is no generation of the stripe pattern of uneven coating. For instance, the coating surface state obtained in the case of BC = 2 mm substantially becomes as illustrated in Fig. 5. Unlike the state as illustrated in Fig. 1, according to this embodiment, there is no stripe pattern of uneven coating on the coating surface, thereby allowing a multi-layer-structurized magnetic recording medium with an extremely smooth coating surface. A table 6 shows the measurement results, using the MII format deck, of the characteristics of magneto-electric conversion, i.e., the S/N ratio and output at the video band frequency 7 MHz, with respect to the magnetic recording media produced according to this embodiment and the magnetic recording medium produced according to the conventional coating technique. For the measurements of the characteristics of magneto-electric conversion, in order to make the comparison easy, a MII tape produced by this applicant is used as the reference tape. In the table 6 there are also shown surface roughnesses (RMS) measured by means of the 3-dimension surface profile analizer. Since the coating surfaces of the tapes produced according to the coating technique of this embodiment, i.e., produced by the dies with the arc-lengths BC of 2 and 7 mm, are considerably smooth, as compared with that of the tape produced by the die with BC = 1.5 mm or produced according to the conventional coating technique, the surface roughness (RMS) is smaller and the reproduction output and S/N ratio are extremely superior. Comparison Example In accordance with the conventional coating technique, the magnetic coating solution for the upper layer as shown in the table 1 is coated on a support so that the film thickness in the fried state becomes 0.5 µm and the magnetic coating solution for the lower layer as shown in the table 2 is coated thereon so that the film thickness in the dried state becomes 3 µm. The support used is made of a polyethylene terephthalate film and arranged to have a thickness of 14 µm, and the coating speed is 100 m/min, and the support tension is 200 g/cm. After being calender-processed, it is cut so as to produce a tape. The coating surface of the tape obtained is measured by the 3-dimension surface profile analizer. The measurement result becomes as illustrated in Fig. 1. Further, the characteristics of magneto-electric conversion such as S/N ratio and output at the frequency 7 MHz result is being as shown in the tables 4 and 6. Characteristic of Magneto-Electric Conversion RMS BC (mm) S/N Ratio Output (7 MHz) BC=1.5 -1.0 dB -1.5 dB 14.2 nm BC=2 +0.5 dB +1.0 dB 4.8 nm Example 2 BC=7 +0.5 dB +1.0 dB 4.9 nm BC=8 Uneven Coating Conventional Tape -1.0 dB -2.0 dB 15.8 nm Reference Tape 0 dB 0 dB 7.0 nm It should be understood that the foregoing description relates to only preferred embodiments of the present invention, which is intended to cover all changes and modifications of the embodiments of the invention herein which do not constitute departures from the scope of the invention, which is defined by the appended claims. It should also be understood that, while it has been described in relation to a method and apparatus for making multilayer recording media, the present invention is also applicable to and provides a method of making a single layer magnetic recording medium using a single coating die and an apparatus for making a single layer recording medium, the apparatus comprising a single coating die of the type described herein.

Claims: A method of coating a magnetic coating solution (7) on a continuously moving support (8) using a die (5) including a first lip portion (1), a second lip portion (2), and a slit (4) and a manifold (3) between the first and second lip portions, the method comprising the steps of: causing the support (8) to approach the first lip portion (1) in a direction substantially parallel to the tangent to the second lip portion (2) at a second edge (B) thereof adjacent to the slit (4); a first edge (A) of the first lip portion (1) adjacent to the slit (4) lying on said tangent; causing magnetic solution (7) to flow through the slit (4) from the manifold (3) so as to coat the support (8) at the exit of the slit (4); and causing the support (8) to leave the second lip portion (2) in a direction substantially parallel to the tangent to the second lip portion at a third edge (C) thereof opposite to the second edge (B) beyond a curved top surface of the second lip portion (2). An apparatus for coating a magnetic coating solution (7) on a continuously moving support (8) comprising: a die (5) including: first and second confronting lip portions (1,2); a slit (4) and a manifold (3) between the first and second lip portions (1,2); the first lip portion (1) having a first edge (A) adjacent to the slit (4); the second lip portion (2) having a second edge (B) opposing the first edge (A) across the slit (4), the first edge (A) lying on a first tangent to the second lip portion at the second edge (B) and the remainder of the first lip portion (1) being spaced from the first tangent; and the second lip portion (2) having a third edge (C) at the other side of a curved top surface of the second lip portion (2) to the second edge (B); and means for causing the support (8) to approach the first lip portion (1) in a direction substantially parallel to the first tangent and to leave the second lip portion (2) in a direction substantially parallel to a second tangent thereto at the third edge (C). An apparatus according to claim 2 wherein the width of the slit (4) between the first edge (A) and the second edge (B) is in the range of from 0.1 to 0.5 mm; the length of the top curved surface between the second edge (B) and the third edge (C) is in the range of from 2 to 7 mm; the radius of curvature (R) of the curved top surface is in the range of from 4 to 20 mm; and the distance between the exit of the manifold (£) and the exit of the slit ($) is in the range of from 20 to 100 mm. An apparatus according to claim 2 or 3, wherein the first and second lip portions (1,2) are made of a cemented carbide. An apparatus according to claim 2, 3 and 4 including a second die of the same type as the other.

Inventors: HIROSE SATOSHI, WATANABE MASARU, HIROSE, SATOSHI, WATANABE, MASARU
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1991
Main classification: G11B5
IPC codes: G11B5, B05D1, B05D5