Apparatus for molding polyurethane foam

Abstract: Disclosed herein is a method and apparatus for producing a molded polyurethane foam without using low-boiling solvents such as Fleon and methylene chloride which present problems when used as a blowing agent. The polyurethane foam has the same good appearance and soft feeling as that produced with low-boiling solvents. The apparatus for molding the polyurethane foam comprises: a mold (1) made up of at least two split molds (2, 3) which are opened and closed; a cavity (4) defined in said mold (1); an air vent defined at a periphery of said cavity; a space (6, 7, 8) defined adjacent said air vent, having a volume greater than said cavity (4), and in communication with said cavity via said air vent when said split molds (2, 3) are closed; a depressurizing means operatively connected to said space; and a mechanism (21) for injecting a polyurethane material into said cavity (4).

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention: The present invention relates to an apparatus for molding a polyurethane foam. The apparatus is suitable for reactive injection molding (RIM for short) of polyurethane foams such as automotive steering wheel, steering wheel pad, instrument panel, console boxe lid, glove box lid, headrest, armrest, and air spoiler. 2. Description of the Prior Art: Polyurethane foams are usually produced by injecting a liquid polyurethane material composed of a polyol component, isocyanate component, and blowing agent, into the mold cavity, permitting the polyurethane material to expand, thereby permitting it to flow and fill the mold cavity, and demolding the polyurethane foam after curing. Among the known blowing agents are fluorochlorohydrocarbons (such as "Fleon", a trade name of DuPont), methylene chloride, and water. An adequate one is selected according to the use and kind of the polyurethane foam to be produced. Fleon and methylene chloride (which are low-boiling solvents) expand the polyurethane material when it is vaporized by heat generated by the reaction of the polyol and isocyanate components, whereas water expands the polyurethane material when it evolves carbon dioxide gas upon reaction with the isocyanate component. Heretofore, low-boiling solvents (such as Fleon and methylene chloride) have been the only blowing agent that can be used for the molding of polyurethane foams such as automotive steering wheel and steering wheel pad, which are composed of a surface skin layer of high density (without expansion or with a low expansion ratio) and an internal core of low density (with a high expansion ratio). There are two reasons for this. (1) Low-boiling solvents (such as Fleon and methylene chloride) permit one to control the amount of foaming due to vaporization by the aid of temperature gradient and pressure gradient in the mold cavity, thereby to produce the skin layer and the core part separately with ease. Thus the resulting polyurethane foam has a good appearance and soft feel. (2) Water as a blowing agent has several disadvantages. When used in a small amount (say, 0.1-1.0 part by weight for 100 parts by weight of polyol component), water evolves only a small amount of carbon dioxide gas, giving rise to a foam having a high-density core. This necessitates using a more amount of polyurethane material than necessary. Conversely, when used in a large amount (say, 1.0-2.0 parts by weight for 100 parts by weight of polyol component), water evolves a sufficient amount of carbon dioxide gas, giving rise to a foam having a low-density core as well as a highly expanded skin layer which looks poor. Moreover, the carbon dioxide gaa forms a large number of urea bonds which make the core hard and brittle and hence make the foam as a whole to feel rigid. The problem associated with rigid feeling can be solved by selecting a proper composition for the polyol component and isocyanate component. However, this is not practicable because of the high material cost. As mentioned above, low-boiling solvents (such as Fleon and methylene chloride) have many advantages and find use as an essential blowing agent for the molding of polyurethane foams composed of a skin layer and a core part. Despite their advantages, Fleon and methylene chloride have recently met with the worldwide campaign against their use. It is said that Fleon, once released, diffuses into the atmosphere and destroys the ozone layer of the stratosphere, resulting in an increase of ultraviolet rays reaching the earth's surface. Methylene chloride is considered to be toxic and carcinogenic. GB-A-2 092 509 discloses an apparatus for molding a polyurethane foam comprising a mold made up of at least two split molds which are opened and closed and which define a cavity, a vacuum box surrounding said mold, a space formed between the mold and the vacuum box, a depressurizing means operatively connected to said space, a mechanism for injecting a polyurethane material into the cavity, and a plurality of vent holes for communication of the cavity with the space. Many vent holes are provided and distributed over the upper surface of the split mold. SUMMARY OF THE INVENTION It is an object of the present invention to provide a new apparatus for producing a polyurethane foam without resorting to low-boiling solvents (such as Fleon and methylene chloride) which present the above-mentioned problems when used as a blowing agent, said polyurethane foam having a good appearance and soft feel as if it were produced with a low-boiling solvent as a blowing agent. Incidentally, Japanese Patent Laid-open Nos. 63237/1980 and 63238/1980 disclose a method of producing a polyurethane foam which comprises evacuating the mold through a small groove formed in the mold and connected to a vacuum pump. This method is intended to produce a uniform rigid polyurethane foam free of voids and blisters in the surface layer, but is not intended to eliminate the use of Fleon (as in the present invention). Moreover, they do not specify any substance as the blowing agent. It is only possible to speculate that low-boiling solvents such as Fleon are used as the blowing agent. In addition, they do not disclose the amount of the blowing agent (which is an important factor in the present invention), nor do they suggest the relationship between the atmospheric pressure and the blowing agent. In other words, these Japanese Patents do not disclose or suggest the object, constitution, and effect of the present invention. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a sectional view showing (in half) the vacuum box and mold (in the open state) which are used in the first example of the invention. Fig. 2 is a sectional view showing (in half) the vacuum box and mold (in the closed state) shown in Fig. 1. Fig. 3 is a sectional view taken in the direction of the arrows along the line III-III in Fig. 2. Fig. 4 is a sectional view showing the vacuum box and mold (in the open state) which are used in the second example of the invention. Fig. 5 is a plan view showing the lower case of the vacuum box and the movable half of the mold (in the open state) shown in Fig. 4. Fig. 6 is a sectional view showing the lower case of the vacuum box and the movable half of the mold (in the closed state for molding operation) shown in Fig. 4. Fig. 7 is a sectional view showing the steering wheel being demolded, with the mold opened. Fig. 8 is a partly enlarged sectional view showing the molded steering wheel. Fig. 9 is a sectional view showing an example of the modified mold. DESCRIPTION OF THE PREFERRED EMBODIMENTS The object of the present invention is achieved by the apparatus for molding a polyurethane foam as defined in claim 1. In the apparatus for molding a polyurethane foam, the depressurizing means are capable of lowering the atmospheric pressure in the cavity, and a venting mechanism opens and closes the final fill position of the cavity to the depressurizing means. The depressurizing unit comprises a vacuum box surrounding the mold, with a space interposed between them, and a vacuum pump connected to the vacuum box. The depressurizing unit may comprise a groove formed in the periphery of the mold cavity so as to form a space when the mold is closed, and a vacuum pump connected to the groove. The venting mechanism comprises a vent hole formed at the final fill position of the mold cavity. A hydraulic cylinder may be provided with a plug to open and close the vent hole. The apparatus further comprises a control means which closes the final fill position to the depressurizing unit for a prescribed period of time after the injection of the polyurethane material into the cavity, and opens the final fill position to the depressurizing unit after the prescribed period of time has passed. The polyurethane material undergoes a change which varies from position to position in the cavity. At the central part, which is away from the molding surface, the polyurethane material sufficiently expands to form the core of low density because of the foaming action and expanding action by water which are explained below. For further description about the molding method and the foaming mechanism, it is referred to the publication of the parent application, EP-A-461 522. The apparatus is provided with a depressurizing unit to lower the atmospheric pressure in the cavity during the molding of a polyurethane foam. The apparatus is constructed such that the vacuum box of the depressurizing unit surrounds the mold, with a space interposed between them. The vacuum box is evacuated by a vacuum pump so that air escapes from the cavity through the gap (air vent land) between the mating mold surfaces or through the venting mechanism. The vacuum box surrounding the mold prevents air from entering the evacuated mold cavity. The space between the vacuum box and the mold functions as a buffer for evacuation. The periphery of the mold cavity may have a groove which functions as the space when the mold is closed. It obviates the vacuum box in the apparatus and hence contributes to the reduction of the size of the molding apparatus. Moreover, it also leads to the reduction of the volume of the space, which reduces the time required for evacuation. The venting mechanism is of simple structure which operates surely. The control means controls the venting mechanism so as to close the final fill position to the depressurizing unit for a prescribed period of time after the injection of the polyurethane material into the cavity. This arrangement permits the atmospheric pressure in the cavity to be kept high spontaneously as the polyurethane material flows. The control means controls the venting mechanism so as to open the final fill position to the depressurizing unit after the lapse of the prescribed period of time. This arrangement discharges from the cavity the fore-end of the flow of the polyurethane material which goes beyond the final fill position. Therefore, this apparatus helps practice the molding method. EXAMPLES Example 1 The first example of the present invention which is embodied in the molding of a steering wheel pad will be described with reference to Figs. 1 to 3 showing the molding apparatus used in the example. The molding apparatus is constructed of a mold 1 (composed of 2 split molds), a vacuum box 11 which encloses the mold 1, forming a space K between the vacuum box and the mold, a mechanism 21 attached to the vacuum box 11 which injects the polyurethane material into the cavity 4 of the mold 1, and a vacuum pump (not shown) to evacuate the vacuum box 11. Each part is detailed in the following. The mold 1 has a vent hole 5 at the final fill position L of the polyurethane material in the cavity 4. To be concrete, the mold 1 is made up of 2 split molds, that is, a stationary mold 2 and a movable mold 3. The split molds form the cavity 4, when closed. The split molds also have grooves on their mating mold surfaces 2a and 3a which form, when closed, a sprue 6, runner 7, and gate 8 through which the polyurethane material flows. When the split molds are closed, the mating mold surfaces 2a and 3a form air vent lands with a clearance of 0.03-0.06 mm (which is unavoidable due to the limited machining precision) along the entire periphery of the cavity 4. The air vent lands permit degassing (mentioned later). The vent hole 5 has a diameter of 1-10 mm. With a diameter smaller than 1 mm, the vent hole 5 does not permit complete degassing (because the final fill position of the polyurethane material fluctuates). With a diameter larger than 10 mm, the vent hole 5 leaves an unsightly mark after demolding. The mold 1 may be an inexpensive aluminum mold or electroformed mold because it does not need high pressure resistance. (The foaming pressure is usually 50-500 kPa.) The vacuum box 11 is large enough to enclose the mold 1, forming the space K between the mold 1 and the vacuum box 11. To be concrete, the vacuum box 11 is made up of an upper casing 12 to which is fixed the stationary mold 2, and a lower casing 13 to which is fixed the movable mold 3. To the periphery of the lower casing 13 is fitted a sealing member (O-ring) 14 to facilitate the tight closing of the vacuum box 11. The lower casing 13 is provided with a suction port 16 which is connected to a vacuum pump (not shown) through a suction hose 15. The upper casing 12 is provided with an air cylinder 19 to vertically actuate a plug 18 which opens and closes the vent hole 5. (This is not mandatory.) The injecting mechanism 21 is made up of a mixing head 22 and a injection nozzle 23. The injection nozzle 23 is connected to the sprue 6 of the mold 1 through an O-rings 24. The mixing head 22 is connected to a polyol tank and an isocyanate tank (both not shown) through high-pressure pumps and circulating pipes, so that the polyol component and isocyanate component are vigorously mixed at the time of injection and are recycled to their respective tanks when injection is not performed. The polyurethane material used in this example is composed of 100 parts by weight polyol component, 0.1-0.6 part by weight of water, and an isocyanate component in an amount corresponding to an index of 110. The above-mentioned apparatus (made up of the mold 1 and the vacuum box 11) is used in the following manner to carry out the foaming operation. (1) First, the mold 1 is closed by mating the stationary mold 2 and the movable mold 3 with each other. Before complete mold closing or after complete mold closing (which forms the cavity 4), the vacuum box 11 is tightly closed and evacuated until the pressure inside and outside the cavity 4 decreases to a desired level. When the vacuum box 11 is evacuated, the mold 1 therein is completely closed. In the case where the mold 1 is completely closed before the vacuum box 11 is closed, the cavity 4 of the mold 1 is evacuated through the gap between the mating mold surfaces 2a and 3a as the vacuum box 11 is evacuated. The closing of the vacuum box 11 may be accomplished by raising the lower casing 13 of the vacuum box 11 by means of a hydraulic cylinder ram (not shown) until it comes into contact with the upper casing 12. Tight closing is ensured by the sealing member 14 fitted to the periphery of the lower casing 13. It is possible to close (and open) the vacuum box 11 and the mold 1 simultaneously or separately. A single hydraulic unit suffices for the former case (which is economical), but two hydraulic units are necessary for the latter case.Then, the vacuum pump (not shown) is set in motion to evacuate the vacuum box 11 through the suction port 16. As the vacuum box 11 is evacuated, the cavity 4 is also evacuated because it communicates with the vacuum box 11 through the sprue 6, the vent hole 5, and the gap between mating mold surfaces 2a and 3a. Evacuation is performed until a vacuum of about 10 mmHg (absolute) is attained. (2) With the vacuum box 11 kept at a reduced pressure, a polyurethane material M is injected into the cavity 4 of the closed mold 1 through the mixing head 22 and the injection nozzle 23. This injection is performed while keeping the mold temperature of the mold 1 lower than usual or keeping the viscosity of the polyurethane material M higher than usual so that foaming does not take place on the surface of the polyurethane material M immediately after its injection into the cavity 4. (This differentiates the molding method of the present invention from the ordinary molding method which consists of injecting a nonfoamable thermoplastic resin into an evacuated cavity or injecting a foamable material into a cavity at normal pressure.) As soon as the polyurethane material M is injected into the cavity 4, reactions take place between the polyol component and the isocyanate component, raising the temperature at the center of the polyurethane material M due to reaction heat, and reactions take place also between the water and the isocyanate component, evolving carbon dioxide gas. The amount of carbon dioxide gas is not so large because the amount of water is limited to 0.1-0.6 part by weight; however, the carbon dioxide gas greatly expands according to Boyle-Charles' law, because the cavity 4 is under reduced pressure. This results in a highly expanded core part in the polyurethane material M. This core part is not hard nor rigid because it contains only a small number of urea bonds proportional to the limited amount of water. Therefore, the steering wheel pad thus obtained has the same soft feel as the conventional one produced with a low-boiling solvent such as Fleon. On the surface of the polyurethane material M, the reaction of the isocyanate component with water hardly takes place and very little carbon dioxide gas is evolved, because the reaction heat of the polyol component and isocyanate component escapes to the mold. As the result, the surface part of the polyurethane material forms the skin layer which has almost invisible small foams. Therefore, the steering wheel pad thus obtained has the same good appearance as the conventional one produced with a low-boiling solvent such as Fleon.Evacuating the cavity 4 produces an additional effect of permitting the polyurethane material M to completely fill the cavity 4 even though the cavity 4 has an undercut or branch, because there is no air in the cavity 4 which hinders the free flow of the polyurethane material. A small amount of excess gas evolved by the polyurethane material smoothly escapes through the gap between the mating mold surfaces 2a and 3a as the polyurethane material flows in the cavity. This makes it unnecessary to inject the polyurethane material in large excess of theoretical amount in order to avoid incomplete venting and incomplete mold filling. It is only necessary to inject the polyurethane material M slightly more than the theoretical amount calculated from the intended expansion ratio. Very little of the material flows out of the mold 1 during the molding operation. This reduces the material loss and obviates the deflashing operation, which leads to an increased productivity.It is desirable (although not mandatory) that the vent hole 5 of the mold 1 be kept closed by the plug 18 until the polyurethane material M is about to fill the cavity 4. This prevents the polyurethane material from escaping from the vent hole 5 and contributes to the uniform expansion (and hence the production of a foam of uniform quality). Immediately before the complete filling of the cavity with the polyurethane material (which usually takes about 10-20 seconds after injection of the material into the cavity), the air cylinder 19 is actuated to raise the plug 18 and open the air vent holes 5 for the degassing of the polyurethane material M at its final flow position. (3) After the polyurethane material has cured, the mold 1 and vacuum box 11 are opened and the steering wheel pad is demolded to complete one cycle of the molding operation. Example 2 The second example of the present invention which is embodied in the molding of a steering wheel will be described with reference to Figs. 4 to 8 showing the molding apparatus used in the example. The molding apparatus has many parts common to that in the first example. Basically, it is constructed of a mold 1, a vacuum box 11, a material injecting mechanism 21, and a vacuum pump (not shown). Those parts common to that in the first example are indicated by like reference numbers in Figs. 4 to 7, and their description is not repeated except for the supplementary description that follows. The mold 1 is designed to form the covering 43 on the ring of the steering wheel 41. It is made up of an upper stationary mold 2 and a lower movable mold 3. They have a groove 4a so that they form a circular cavity 4 when they are closed. At the center of the cross section of the cavity is placed the ring of the steering wheel core 42. To this groove 4a is connected a gate 8 (as shown at the left side in Fig. 4). The polyurethane material M is injected into the cavity 4 through the gate 8. In the cavity 4 the polyurethane material M splits into two flows which join at the final fill position L (at the right side in Fig. 6) after filling the cavity 4. At the final fill position L is a venting mechanism which is made up of a vent hole 5 (which leads to the space K in the vacuum box 11) and an air cylinder 19 provided with a plug 18 to open and close the vent hole 5. The rod of the air cylinder 19 passes through a plate 20 which prevents the excess part 46 of the polyurethane material M (mentioned later) from blowing off upward. The venting mechanism is provided with a control means (not shown) which keeps the vent hole 5 closed for a prescribed period of time in which the polyurethane material M injected into the cavity 4 fills the cavity 4, and opens the vent hole 5 after the lapse of a prescribed period of time. Inside the groove 4a of the stationary mold 2 and movable mold 3 are fitting units 31 for the positioning of the molds 2 and 3 (when closed), and a hole 32 and a pedestal 33 which hold the boss of the steering wheel core 42. The pedestal 33 has an ejector pin 34 to demold the steering wheel 41 after molding. Like the first example, the molds 2 and 3 have the mating mold surfaces 2a and 3a which form a gap of 0.03-0.06 mm when they are closed. The stationary mold 2 and the upper casing 12 are integrally constructed, and the movable mold 3 and the lower casing 13 are integrally constructed. The lower casing 13 is attached to a hydraulic cylinder ram (not shown) so that it is moved up and down as the mold is closed and opened. At its raised position, the periphery of the lower casing 13 is in contact with the periphery of the upper casing 12. The injecting mechanism 21 is connected to an injection nozzle 23 (which passes through the lower casing 13 and reaches the movable mold 3) tightly by the aid of a sealing member 24 (O-rings), which prevents the leakage of air through the gap between the lower casing 13 and the injection nozzle 23 when the vacuum box 11 is evacuated. Like the first example, the polyurethane material used in this example is composed of 100 parts by weight polyol component, 0.1-0.6 part by weight of water, and an isocyanate component in an amount corresponding to an index of 110. The above-mentioned apparatus is used in the following manner to carry out the foaming operation. (1) With the stationary mold 2 and movable mold 3 opened as shown in Fig. 4, the steering wheel core 42 is fitted into the movable mold 3 as shown in Fig. 5. (2) The stationary mold 2 and movable mold 3 are closed to form the cavity 4. At the same time, the lower casing 13 is raised until its periphery comes into contact with the periphery of the upper casing 12, so that the vacuum box 11 is sealed. The closing of the molds and vacuum box is accomplished by raising the lower casing 13 of the vacuum box 11 by a hydraulic cylinder ram (not shown) until the lower casing 13 comes into contact with the upper casing 12. (3) Then, the vacuum pump (not shown) is set in motion to evacuate the space K in the vacuum box 11 through the suction port 16 until the atmospheric pressure therein is reduced below 500 mmHg, preferably below 300 mmHg. As the vacuum box 11 is evacuated, the cavity 4 of the mold 1 is also evacuated through the gap between mating mold surfaces 2a and 3a (and also the vent hole 5 if it is open). As the result, the space K in the vacuum box 11 and the cavity 4 are evacuated to a similar level. (4) With the vent hole 5 closed (as shown in Fig. 6), the polyurethane material M is injected into the cavity 4 of the closed mold 1 through the mixing head 22 and injection nozzle 23. The volume of the polyurethane material M to be injected is usually one-fourth to a half of the volume of the cavity. The injection takes 2-4 seconds. It is desirable (although not mandatory) that the polyurethane material M undergo aeration prior to injection into the cavity 4 so that it contains a large number of minute air bubbles which contribute to a great expansion as explained earlier in the section of function. When injected into the cavity 4, the polyurethane material M expands at its central part, as shown in Fig. 8, due to chemical foaming in the same manner as in the first example. This expansion is responsible for the core 44 which has the same soft feeling as that obtained with a low-boiling solvent such as Fleon in the conventional manner. Moreover, it is possible that the temperature at the central part of the polyurethane material M is higher than the boiling point of water if the atmospheric pressure in the cavity 4 is extremely lowered or the injection temperature of the polyurethane material M is raised, because the depression of the boiling point of water takes place in the evacuated cavity, as explained earlier in the section of function. In that case, water vapor augments the expansion of the core part 44 which is due to chemical foaming.The outer part of the polyurethane material M forms the slightly expanded skin layer 45, as shown in Fig. 8, in the same manner as in the first example. The skin layer 45 has almost invisible minute foams; therefore, the steering wheel covering 43 thus molded has the same good appearance as that formed with a low-boiling solvent such as Fleon in the conventional manner.Thus, the polyurethane material M increases in volume and flows in the cavity 4 as it forms the steering wheel covering 43 consisting of the highly expanded core 44 and the slightly expanded skin layer 45, until it reaches the final fill position L, as shown in Fig. 6. Usually, the flow takes 8-20 seconds, from injection to complete filling. During this flow time, the vent hole 5 is kept closed by the plug 18. As the polyurethane material M flows in the cavity 4, it gradually seals the gap between the mating mold surfaces 2a and 3a. Therefore, pressure in the cavity 4 increases spontaneously with the flow of the polyurethane material M. This prevents carbon dioxide gas evolved from infinitely expanding to give rise to coarse cells. As the result, the core 44 has a uniform expansion ratio throughout its periphery. This leads to a uniform quality. (5) When the polyurethane material M has reached the final fill position in the cavity 4, the vent hole 5 is opened automatically by the above-mentioned control mechanism, so that the fore-end of the polyurethane material M is discharged from the cavity 4 through the vent hole 5. (The discharged part 46 is indicated in Fig. 7 which shows the subsequent step.) Usually, the fore-end of the polyurethane material M tends to collect gas which causes pinholes, voids, and short shot. This problem is completely solved in this example because the fore-end is discharged. (6) When the polyurethane material M in the cavity 4 has cured, the stationary mold 2 and movable mold 3 of the mold 1 are opened and, at the same time, the upper casing 12 and lower casing 13 are separated to open the vacuum box 11, as shown in Fig. 7. Curing usually takes 100-180 seconds. In this example, the molded steering wheel 41 is demolded by the ejector pin 34 which is interlocked with the movable mold 3. One cycle of the molding operation is completed by removing the discharged part 46 of the polyurethane material M. In the meantime, the molding of the steering wheel covering 43 presents the following problems (a) and (b) characteristic of the steering wheel, in addition to the above-mentioned problems associated with using Fleon. However, these problems are solved if molding is carried out according to this example. It follows therefore that the method of this example is suitable for molding the steering wheel covering. (a) Since the covering 43 of the steering wheel 41 is formed around the core 42, the polyurethane material M injected into the cavity 4 experiences turbulence by the core 42. This turbulence involves air which causes pinholes, voids, and short shot. According to the conventional technology, it is necessary to make the gate 8 at a position where there is the least possibility of turbulence occurring, and such a position is limited. Moreover, in case turbulence occurs, a remedy for it is necessary. In this example, turbulence is less liable to occur because the polyurethane material M contains a less amount of blowing agent and pressure in the cavity 4 increases as the polyurethane material 4 flows in the cavity 4. This permits a wide selection of the gate location and reduces the amount of the fore-end of the polyurethane material to be discharged. (b) In the molding of the covering 43 of the steering wheel 41, the polyurethane material M injected into the cavity 4 flows in two directions, and the two flows join at the final fill position L, as mentioned above. The confluence tends to form a weld line and collect gas which causes pinholes, voids, and short shot. These problems are completely solved in this example because the cavity 4 is evacuated and the fore-end of the flow (confluence) is discharged. The usefulness of the molding method and molding apparatus is described in Example 3 of EP-A-461 522, incorporated herein by reference, where polyurethane materials of different formulation were tested for flow in the cavity 4 at different pressure under specific conditions. While preferred embodiments have been described, variations thereto will occur to those skilled in the art within the scope of the invention defined in the appended claims, as illustrated in the following. (1) Although the first embodiment employs the mold 1 and the vacuum box 11 which are separate, another embodiment would be possible which employs a mold of double-wall structure, with the outer wall functioning as the vacuum box 11 and the two walls forming the space. (2) The cavity 4 may be provided with a large groove 9 along its entire or partial periphery through which the cavity 4 is evacuated (see Fig. 9). The groove 9 would function as the space K The groove 9 may be formed in either or both of the stationary mold 2 and movable mold 3. Moreover, the periphery of the groove may be provided with a seal member 10 to isolate the cavity from the atmosphere. (3) The mold may be made of ceramics, plastics, or any other material which withstands the foaming pressure. Effects of the invention Being constructed as mentioned above, the present invention produces the following effects. The use of low-boiling solvents such as Fleon and methylene chloride which pose problems when used as a blowing agent is obviated. Nevertheless, it permits the production of a polyurethane foam having the same good appearance and soft feeling as the one produced with a low-boiling solvent. The obtained polyurethane foam has a higher extent of foaming than that in the case of the first molding method. A polyurethane foam is obtained in which the core part has a uniform extent of foaming and hence has a uniform quality. This polyurethane foam is free of pinholes, voids, and short shot. The obtained polyurethane foam has a high extent of foaming. This polyurethane foam is free of pinholes, voids, and short shot, as in the case of the third molding method. The molding apparatus permits the cavity pressure to be reduced easily and keeps the evacuated cavity isolated from the atmosphere. The apparatus provides a space between the mold and the vacuum box which functions as a buffer for evacuation. The molding apparatus can be made simple and small. It permits the reduction of time for evacuation. The molding apparatus provides a venting mechanism which is simple and yet works surely.

Claims: An apparatus for molding a polyurethane foam comprising: a mold (1) made up of at least two split molds (2, 3) which are opened and closed; a cavity (4) defined in said mold (1); a vacuum box (11) surrounding said mold; a space (K) formed between said mold and said vacuum box, adjacent the mating mold surfaces of said split molds; a depressurizing means operatively connected to said space; a mechanism (21) for injecting a polyurethane material into said cavity; a vent hole (5) formed at a final fill position of said cavity and in communication with said space; characterized in that an air vent is defined at a periphery of said cavity by mating mold surfaces (2a, 3a) of said split molds (2, 3) when said split molds are closed, said space being in communication with said cavity via said air vent when said split molds are closed; and means (18, 19) are provided for selectively opening and closing said vent hole (5). An apparatus according to claim 1, wherein said vacuum box (11) is made up of at least two split boxes (12, 13) which are opened and closed simultaneously with said split molds (2, 3) An apparatus according to claim 1, wherein said air vent is defined by air vent lands having a clearance formed therebetween of 0.03-0.06 mm. An apparatus according to claim 1, wherein said vent hole (5) has a diameter of 1-10 mm. An apparatus according to claim 1, wherein said means (18, 19) for selectively opening and closing said vent hole (5) is controllable so as to close said vent hole for a prescribed period of time after said polyurethane material is injected into said cavity (4) and to open said vent hole after said prescribed period of time has passed. An apparatus according to claim 1, wherein said cavity is substantially ring-shaped. An apparatus according to claim 1, wherein said air vent is defined around substantially an entrie periphery of said cavity (4).

Inventors: OKANO HIDENOBU, WATANABE KATSUNORI, OKANO, HIDENOBU, WATANABE, KATSUNORI, OKANO, HIDENOBU, C/O TOYODA GOSEI, WATANABE, KATSUNORI, C/O TOYODA GOSEI
Applicants: TOYODA GOSEI KK, TOYODA GOSEI CO., LTD.
Application year: 1991
Main classification: B29C44
IPC codes: B29C44