Optical functioning glass, optical fiber waveguide device, and optically active device

Abstract: An optically active device comprising an optical fiber, a light source and a coupler is disclosed. The optical fiber has a core made of a silicate glass containing Rb and/or Cs oxide. The core is doped with Nd³⁺ as an active ion and transmits light at 1.3 µm band. The light source generates excitation light at 0.8 µm. The coupler directs the excitation light from the light source into the core of the optical fiber. A signal light or a spontaneous light at 1.3 µm band which is transmitted in the core stimulates Nd³⁺ to emit light at 1.3 µm band. As a result an optical function such as optical amplification can be effected at 1.3 µm band.

Description: Background of the Invention [Field of the Invention] The present invention relates to an optical functioning glass doped with Nd 3+ , and to an optical fiber, a waveguide device, and an optically active device, all of which use this optical functioning glass. [Related Background Art] Efforts have been made to manufacture an optically active device such as a fiber amplifier, a fiber sensor, and a fiber laser by using a glass doped with a rare-earth element for the application to a light communication at a 1.3-µm wavelength band and the like. For example, a report has been made (ELECTRONICS LETTERS, 1990, Vol. 26, No. 2, pp. 121 - 122) in which an optical functioning glass is prepared by adding neodymium ions (Nd 3+ ) as an active ions to a phosphate glass as a host glass, an optical fiber is formed from this optical functioning glass, and laser oscillation characteristics of the optical fiber are evaluated. It reports about the optical fiber characteristic that a fluorescence peak wavelength caused by Nd 3+ was about 1.32 µm, an absorption peak wavelength caused by ESA (excited state absorption) transition was about 1.31 µm, and an oscillation peak wavelength was about 1.36 µm. However, in the reported optical fiber, a sufficiently high laser oscillation gain cannot be obtained because the absorption peak at the wavelength of 1.31 µm is present near the fluorescence peak at the wavelength of 1.32 µm, and because the intensity of the absorption peak at the 1.31-µm wavelength band is higher than that of the fluorescence peak at the 1.32-µm wavelength band. In addition, since the absorption peak exists at a wavelength shorter than that of the fluorescence peak, the oscillation peak wavelength is shifted to a wavelength longer than the 1.3-µm wavelength band. As a result, a substantial gain of laser oscillation cannot be obtained at the 1.3-µm wavelength band. Summary of the Invention It is an object of the present invention, in consideration of the above situation, to provide an optical functioning glass capable of performing optical amplification and optical oscillation of light at a 1.3-µm wavelength band or other wavelength bands, or improving optical amplification efficiency and optical oscillation efficiency. It is another object of the present invention to provide an optical fiber and a waveguide device, both of which use the optical glass. It is still another object of the present invention to provide an optically active device such as an optical amplifier or a laser, which uses the optical fiber or the waveguide device. According to one aspect, the present invention provides an oxide-based optical glass containing Nd 3+ as an active ion doped in a host glass which includes Rb and/or Cs; characterised in that the host glass comprises at least 10 mol % of Rb and/or Cs and 20-45 mol % of total alkali elements. According to this optical glass, since the host glass consists of an oxide-based multi-component glass containing Rb and/or Cs, the wavelength position of the absorption peak can be largely shifted relative to the wavelength position of the fluorescence peak. As a result, it is found that a glass suitable for optical amplification and optical oscillation at the 1.3-µm wavelength band or other wavelength bands can be obtained, as will be described later. It is preferred that the above optical glass further comprises one or more alkaline-earth elements, such as Mg and/or Ca. By using the host glass containing an oxide of an alkaline-earth element, the chemical stability such as the weather resistance of the optical glass can be improved. In addition, the present invention provides an optical fiber having a core made of the above optical glass. According to this optical fiber, a glass obtained by doping Nd 3+ in a host glass containing Rb and/or Cs is used as a core glass. For this reason, optical amplification and optical oscillation of light propagating in the core glass can be performed at the 1.3-µm wavelength band and other wavelength bands, and the optical amplification gain and the optical oscillation gain can be increased. That is, light is effectively confined in the core by fiber formation, and the loss of the confined light is extremely low, thereby forming an inverted population of Nd 3+ with a low threshold value. In addition, the present invention provides a waveguide device having a planar waveguide made of the above optical glass. Furthermore, the present invention provides an optically active device comprising the above optical fiber or the waveguide device, a light source for generating light for exciting Nd 3+ , and optical means for directing the excitation light from the light source to the optical fiber or the waveguide device. According to the above optically active device, Nd 3+ are excited by the excitation light directed to the optical fiber or the waveguide device. Most of the Nd 3+ are stimulated by light of the 1.3-µm wavelength band or other wavelength bands incident together with the excitation light on the optical fiber or the waveguide device, thereby generating radiation light. Thus, optical functions such as optical amplification, laser oscillation, and optical switching can be performed at this wavelength band. In addition, the present invention provides a fiber amplifier comprising the optical fiber for propagating signal light at a 1.3-µm wavelength band or a band near the 1.3-µm wavelength band, a light source for generating excitation light at an 0.8-µm wavelength band or a band near the 0.8-µm wavelength band, optical means for directing the excitation light from the light source to an optical fiber, and means for coupling the signal light at the 1.3-µm wavelength band or the band near the 1.3-µm wavelength band into the optical fiber. According to this fiber amplifier, Nd 3+ is excited by the excitation light at an 0.8-µm wavelength band or the band near the 0.8-µm wavelength band directed into the optical fiber. Most of the Nd 3+ are stimulated by the signal light of the 1.3-µm wavelength band or the band near the 1.3-µm wavelength band incident together with the excitation light, thereby generating radiation light. Therefore, optical amplification at the 1.3-µm wavelength band or the band near the 1.3-µm wavelength band can be performed. In addition, the present invention provides a fiber laser comprising the optical fiber for propagating signal light at a 1.3-µm wavelength band or a band near 1.3-µm wavelength band, a light source for generating excitation light at an 0.8-µm wavelength band or a band near the 0.8-µm wavelength band, optical means for directing the excitation light from the light source to an optical fiber, and resonator means for feeding the light at the 1.3-µm wavelength band or the band near the 1.3-µm wavelength band back to the optical fiber. According to this fiber laser, Nd 3+ is excited by the excitation light at the 0.8-µm wavelength band or the band near the 0.8-µm wavelength band. Some or most of the excited Nd 3+ are stimulated by the light of the 1.3-µm wavelength band or the band near the 1.3-µm wavelength band present in the optical fiber, thereby generating the radiation light. Optical oscillation at the 1.3-µm wavelength band or the band near the 1.3-µm wavelength band can be performed. In addition, the present invention provides a waveguide amplifier and a waveguide laser, wherein the optical fibers constituting the fiber amplifier and the fiber laser are replaced with the above waveguide devices, respectively. The present invention will become more fully understood from the detailed description given hereinbelow and the accompanying drawings which are given by way of illustration only, and thus are not to be considered as limiting the present invention. Brief Description of the Drawings Fig. 1 is a graph showing a relationship between the types of alkali dopants and Nd 3+ energy levels in a silicate glass; Fig. 2 is a graph showing a relationship between the types of alkali dopants and Nd 3+ energy levels in a phosphate glass; Fig. 3 is a graph showing a relationship between the types of alkali dopants and Nd 3+ fluorescence lifetimes; Fig. 4 is a graph showing a relationship between the types of alkaline-earth dopants and Nd 3+ fluorescence lifetimes; Fig. 5 is a diagram showing an embodiment of a fiber amplifier; Fig. 6 is a diagram showing an embodiment of a fiber laser; and Fig. 7 is a perspective view showing an embodiment of a waveguide laser. Detailed Description of the Preferred Embodiments The principle of the present invention and the process in which the present invention was established will be described below. The present inventor proposed the following assumption and made extensive studies on it. That is, in order to change the wavelength position of an emission peak of an Nd 3+ relative to its absorption peak, it is assumed that effects of a crystalline electric field, Coulomb interaction, and spin-orbit interaction upon electrons in Nd 3+ should be changed. For example, a 4f-orbit electron assumed to be related to light absorption or emission at the 1.3-µm wavelength band is taken into consideration. The crystalline electric field is assumed to have almost no effect on the 4f-orbit electrons because the field is shielded by electrons of the outer shell. On the other hand, it is assumed that the Coulomb interaction and the spin-orbit interaction can be changed by changing the distance between electrons within the 4f orbit or the distance between the atomic nucleus and electrons. By expanding or constricting an Nd 3+ electron cloud, the absorption and emission wavelengths at the 1.3-µm wavelength band are assumed to be shifted. More specifically, it is considered to be preferable to change the bond property between Nd 3+ and atoms located therearound in order to expand or constrict the electron cloud. That is, an oxide of Rb or Cs as a long-period element is used as a component of a host glass, and its concentration is changed to increase or decrease the strength of a covalent bond or an ionic bond between Nd 3+ and the ligands located therearound. As a result, the Nd 3+ electron cloud can be expanded or constricted. In addition, the absorption and emission at and near the 1.3-µm wavelength band are assumed to be shifted. In this case, an alkali element having a high ionicity, such as Rb or Cs, is assumed to strongly act on Nd 3+ . When the concentrations of oxides of these elements are increased or decreased in the host glass, the wavelength shifts of the absorption and emission peaks are nonuniformed. Moreover, the relative wavelength positions of the absorption and emission peaks are expected to be largely changed. The absorption and emission wavelength shifts at the 1.3-µm wavelength band have been described above. A similar assumption can be made for the absorption and emission wavelengths in other wavelength bands. The above conclusion is simply an assumption. The present inventor confirmed improvements of optical amplification and optical oscillation characteristics of an Nd 3+ -doped glass on the basis of experiments (to be described later) and extensive studies based on phenomena derived from the experimental results. Fig. 1 shows changes in Nd 3+ energy levels obtained by changing the types of alkali element oxides R' 2 O added to a silicate glass (20Na 2 O-15R' 2 O-65SiO 2 ). A brief description will be made for a light absorption/emission mechanism of Nd 3+ at the 1.3-µm wavelength band prior to a description of the drawings. An electron set in a ground state level 4 I 9/2 is temporarily excited to a level 4 F 5/2 by excitation light of about 0.8 µm so that a non-radiation process is set such that phonons or the like are emitted. The energy level of the electron is then shifted to a level 4 F 3/2 . By this pumping, when an inverted population is formed between the level 4 F 3/2 and the level 4 I 13/2 , emission having a peak at the 1.32-µm wavelength band can be performed. On the other hand, an electron set in the level 4 F 3/2 absorbs light of the 1.31-µm wavelength band and may be excited to a level 4 G 7/2 . For this reason, in conventional glasses, even if an electron is pumped to the level 4 F 3/2 , efficient emission cannot be performed at the 1.32-µm wavelength band. For this reason, a sufficiently high laser gain cannot be obtained at and near the 1.31-µm wavelength band. The illustrated energy levels, that is the wavenumbers of electrons are calculated from absorption peak wavelengths at and near 530 nm, 800 nm, and 880 nm by using a spectrophotometer. These peaks correspond to the energy levels 4 G 7/2 , 4 F 3/2 , and 4 I 13/2 , respectively. As is apparent from Fig. 1, the energy levels 4 G 7/2 , 4 F 3/2 , and 4 I 13/2 linearly change in accordance with the ionic energies of alkali elements R' used. In this case, although the interval between the energy levels 4 F 3/2 and 4 I 13/2 is not almost changed, the interval between the energy levels 4 G 7/2 and 4 F 3/2 greatly varies. This phenomenon indicates that the energy difference between the levels 4 G 7/2 and 4 F 3/2 corresponding to the ESA at the 1.32-µm wavelength band greatly varies while the energy difference between the levels 4 F 3/2 and 4 I 13/2 corresponding to the fluoresce at the 1.32-µm wavelength band is not almost changed. In particular, when a long-periodic element such as Rb and Cs is used as an alkali element, an ESA peak wavelength is increased to 1.345 µm or more, while the wavelength of the fluorescence peak is limited to about 1.325 µm. Since the ESA wavelength does not interact with the fluorescent wavelength if their difference is 20 nm or more, the phenomenon which causes the ESA to influence the fluorescence (i.e., excited electrons set in the energy level 4 F 3/2 are deenergized by the ESA) can be suppressed by use of an alkali element, Rb or Cs. In addition, when an oxide of an alkali element, Rb or Cs, is used as a dopant to shift the ESA peak to the long-wavelength side of the fluorescence peak, the wavelength band for obtaining the optical amplification and oscillation gains can be relatively shifted to the shorter-wavelength side. As a result, the optical amplification and oscillation gains can be obtained near a wavelength of 1.31 µm shorter than the wavelength of 1.32 µm at which the fluorescence peak is present. Fig. 2 shows changes in Nd 3+ energy levels obtained by changing the types of alkali element oxides R' 2 O added to a phosphate glass (10La 2 O 3 -25R' 2 O-65P 2 O 5 ). In the graph of Fig. 2, the energy levels 4 G 7/2 , 4 F 3/2 , and 4 I 13/2 respectively corresponding to the absorption peaks at the wavelengths of 530 nm, 800 nm, and 880 nm are kept constant regardless of the tapes of alkali elements R' used. In the case of the phosphate glass, it is difficult to change the relationship between the three energy levels associated with optical amplification at the 1.3-µm wavelength band. However, some improvement can be found when a phosphate is partially replaced with a silicate. Fig. 3 shows changes in fluorescence lifetimes for the Nd 3+ energy levels 4 F 3/2 and 4 I 13/2 obtained by changing the types of alkali elements R' added to the multi-component glasses in Figs. 1 and 2. As is apparent from Fig. 3, in both silicate and phosphate glasses, when an alkali element having an ion of a large radius is used, the Nd 3+ fluorescence lifetime can be prolonged. In this sense, a glass containing an oxide of an alkali element, Rb or Cs, is preferably used as the host glass. It is still unclear that the above assumption is appropriate. In any case, according to the experiments and examinations of the present inventor, when an oxide-based multi-component glass containing Rb or Cs is used as the host glass doped with Nd 3+ as an active ion, a promising optical functioning glass which allows optical amplification of Nd 3+ at the 1.3-µm wavelength band or the like or improves its optical amplification efficiency can be obtained. In this case, when a host glass having a large amount of an alkali element added thereto is used so as to obtain an effective shift in ESA peak wavelength, stability of the host glass is degraded. This phenomenon typically occurs when the content of the alkali element exceeds 45 mol%. In particular, when a long-periodic element such as Rb or Cs is used, deliquescence and the like become conspicuous to accelerate degradation If the concentration of Rb or the like is reduced and the content of the oxide of Rb or the like is controlled to be 5 mol% or less in order to improve deliquescence, a typical shift does not occur in the ESA peak wavelength. The present inventor searched for a host material exhibiting chemical stability even if the above long-periodic element is used. In order to improve chemical stability of the glass itself, an alkaline-earth element is preferably used as an additive. It is, however, undesirable, that the ESA peak wavelength tends to return to the original wavelength due to doping of the alkaline-earth element or that the fluorescence peak wavelength tends to be largely shifted to the long-wavelength side. For this reason, the silicate glass in Fig. 1 is used as a starting material, an alkaline-earth element such as Mg or Ca is added thereto or part of the starting material is substituted with Mg or Ca, thereby preparing an optical functioning glass. Tests such as a deliquescence test and weather resistance test of this glass sample were performed, and it was found that these chemical properties were improved, thereby greatly improving chemical stability. Note that the fluorescence peak and the ESA peak were not almost changed as compared with that in Fig. 1. Fig. 4 shows variations in Nd 3+ fluorescence lifetimes in accordance with the types of alkaline-earth elements used. It is found that the fluorescence lifetime is shortened when the radius of an ion is increased. It is therefore found that a preferable composition of the host glass to be doped with Nd 3+ contains Rb and/or Cs and also Mg. The optical functioning glass shown in Fig. 1 to 4 is used as an optical fiber material. For example, this glass material is used to form a planar waveguide or the like. It is preferable to manufacture an optical fiber comprising a core made of the above optical functioning glass and a cladding surrounding the core and having a lower refractive index than that of the core, so as to obtain an elongated optical transmission line. The above optical fiber is manufactured as follows in practice. An optical functioning glass obtained by doping Nd 3+ in a host glass containing Rb or Cs is prepared, and a preform having a core made of this optical functioning glass is formed in accordance with a rod-in-tube method. The prepared preform is set in a known drawing apparatus and is drawn into an optical fiber. The resultant optical fiber comprises a core doped with Nd 3+ and a cladding layer having a lower refractive index than that of the core and not doped with Nd 3+ . The optical fiber having the core made of the optical functioning glass described above can be applied to an optically active device such as a fiber laser, a fiber amplifier, and a fiber detector. More specifically, since the oxide-based multi-component glass containing an oxide of Rb or Cs is used as the host glass for the core glass, sufficiently high optical amplification and oscillation gains can be obtained in, e.g., the 1.3-µm wavelength band or the wavelength band near the 1.3-µm wavelength band. In addition, since light is efficiently confined in the core by fiber formation and its loss is extremely low, an inverted population can be formed with a small threshold value. Therefore, applications for a high-gain fiber amplifier or the like can be made. In addition, the above optical fiber can be used in a fiber amplifier for amplifying light of the 1.3-µm wavelength band as an application example. Fig. 5 shows a 1.3-µm wavelength band fiber amplifier. A laser diode is used as a signal source 11. One end of an optical fiber 18a is optically connected to the output of this signal source 11. The other end of the optical fiber 18a is connected to the input of a coupler 13. A Ti-sapphire laser is used as a laser source 12 as an excitation light source. One end of an optical fiber 19a is connected to the output of the laser source 12. The other end of the optical fiber 19a is connected to the input of the coupler 13. Two optical fibers 18b and 19b extend from the output of the coupler 13. The terminal end of the optical fiber 19b is dipped in a matching oil 17 for preventing return light. The terminal end of the optical fiber 18b is connected to one end of an optical fiber 10 serving as an optical transmission line through a connector or the like. A spectrum analyzer 15 is arranged at the output as the other end of the optical fiber 10. A filter 16 is inserted in the optical fiber 10 and the spectrum analyzer 15. The coupler 13 is obtained by fusing and then stretching the two optical fibers 18 and 19. The coupler 13 and the fibers 18a, 18b, 19a, and 19b constitute an optical means. The optical fiber 10 comprises an SM fiber having a length of 1 m. The optical fiber 10 has an outer diameter of 125 µm and a core diameter of 5 µm. Note that a silicate glass containing an oxide of an alkali element such as Rb or Cs and doped with Nd 3+ as an active ion is used as the host glass. An operation of the fiber amplifier in Fig. 5 will be briefly described below. The laser source 12 outputs excitation light at a 0.80-µm wavelength band. This excitation light is incident on the coupler 13 through the optical fiber 19a and on the optical fiber 10 through the optical fiber 18b. Since the core of the optical fiber 10 on which the excitation light is incident is doped with Nd 3+ as an active ion, the Nd 3+ excited in a predetermined state with this excitation light is set in a state wherein light at a 1.3-µm wavelength band can be emitted. The signal light of the 1.3-µm wavelength band output from the signal source 11 is incident on the fiber coupler 13 through the optical fiber 18a. The signal light incident on the coupler 13 is coupled to the excitation light from the laser source 12 and is then incident on the optical fiber 10. The signal light incident on the optical fiber 10 stimulates the pumped Nd 3+ to emit light at the 1.3-µm wavelength band. The excitation light and the amplified signal light are output from the output of the optical fiber 10. Of these light components, the excitation light is cut off by the filter 16. For this reason, only the amplified signal light is incident on the spectrum analyzer 15. Therefore, the optical amplification gain by the Nd 3+ -doped optical fiber can be measured. Table I below shows measurement results of the optical amplification gains of the fiber amplifier shown in Fig. 5. Amplification Peak [µm] Gain at 1.31 µm Sample 1 1.327 20 dB Sample 2 1.327 17 dB Sample 3 1.320 10 dB Sample 4 1.350 0 dB In this case, K 2 O, Rb 2 O, and Cs 2 O were used as the alkali element oxides R' 2 O. Materials for the core glass of Samples 1 to 4 were blended to obtain the following compositions. These materials were respectively melted in platinum melting pots and were rapidly cooled to be vitrified. (Sample 1) 20Na 2 O-15Rb 2 O-65SiO 2 (Sample 2) 20Na 2 O-15Cs 2 O-65SiO 2 (Sample 3) 20Na 2 O-15K 2 O-65SiO 2 (Sample 4) 20Na 2 O-15Li 2 O-65SiO 2 Nd 3+ serving as an active ion was prepared as an oxide in a material preparation step so as to obtain a concentration of 1 wt%. As is apparent from Table I, in Samples 1 and 2 respectively using Rb and Cs as alkali elements, high gains are obtained. On the other band, in Samples 3 and 4 respectively using K and Li as alkali elements, no gain is obtained or small gains are obtained if any. Table II below shows fluorescence peaks and so on when a host glass having an alkali element oxide , Rb 2 O, and Mg oxide added thereto is used. ESA Wavelength [µm] Fluorescence Wavelength [µm] Deliquescence (Visual Observation) Sample 1 1.353 1.327 None Sample 2 1.344 1.327 None Sample 3 1.351 1.327 None Sample 4 1.346 1.327 Slight In this case, the fluorescence peaks were measured using the fiber amplifier shown in Fig. 5. Materials for the core glass of Samples 5 to 8 were blended to obtain the following compositions and were respectively melted in platinum crucible and rapidly cooled to be vitrified. (Sample 5) 20Na 2 O-10Rb 2 O-10MgO-60SiO 2 (Sample 6) 15Na 2 O-10Rb 2 O-10MgO-65SiO 2 (Sample 7) 10Na 2 O-10Rb 2 O-10MgO-70SiO 2 (Sample 8) 10Na 2 O-15Rb 2 O-10MgO-65SiO 2 Note that Nd 3+ serving as an active ion was prepared as an oxide in a material preparation step so as to obtain a concentration of 1 wt%. As is apparent from Table II, in Samples 5 to 8 using Mg as the alkaline-earth element, the ESA peak wavelengths are 1.344 µm or more. The fluorescence peaks are kept at the wavelength of 1.327 µm. It is therefore assumed that high gains are obtained at and near the 1.32-µm wavelength band. In this case, deliquescence was not almost found in all the samples. These glass samples were excellent in weather resistance. For example, the glass used as the core glass of Sample 5 was cut into a test piece, and this test piece was dipped in water at room temperature for 50 hrs or more. The weight of this test piece was not almost reduced. In the fiber amplifier shown in Fig. 5, the signal light from the signal light source 11 and the excitation light from the laser source 12 are incident on the optical fiber 10. The signal light from the signal light source may be incident on one end of the optical fiber 10, and the excitation light from the laser source may be incident on the other end of the optical fiber 10. In addition, one or a plurality of laser sources for generating excitation light components having predetermined wavelengths capable of performing fluorescent emission of Nd 3+ may be prepared in accordance with signal light components having different wavelengths corresponding to the Nd 3+ fluorescent emission components. Signal light having each wavelength is incident on one end of the optical fiber 10, and at the same time, the excitation light from the laser source may be incident on the other end of the optical fiber to achieve a multi-channel fiber amplifier. Fig. 6 shows an embodiment of a 1.3-µm wavelength band fiber laser. A laser light source 12 is identical to that used in the fiber amplifier shown in Fig. 5. That is, the laser source 12 is a 0.80-µm wavelength Ti-sapphire laser. An optical fiber 10 doped with Nd 3+ is also identical to that used in the optical amplifier. The excitation light having a wavelength of 0.80 µm from the laser source 12 is incident on one end of the optical fiber 10 having the core doped with Nd 3+ by an appropriate means 28 such as a lens or an optical connector. The Nd 3+ contained in the optical fiber is excited to a predetermined state by this excitation light, and light at the 1.3-µm wavelength band can be emitted. Since the input and output ends of the optical fibers 10 are made mirror surfaces, these end faces of the input and output ends constitute a resonator. As a result, when an output of the excitation light exceeds a predetermined value, laser oscillation occurs at any wavelength within the 1.3-µm wavelength band. Fig. 7 shows an embodiment of a waveguide amplifier 100. Planar waveguides 130a, 130b, and 130c are formed on a substrate 120 so that one waveguide is branched into two waveguides. The planar waveguide 130a is made of the glass of the above embodiment doped with Nd 3+ . A filter 136 made of a grating is formed at the other end of the planar waveguide 130a. Signal light at the 1.3-µm wavelength band is incident on the planar waveguide 130b. Excitation light at the 0.80-µm wavelength band is incident on the planar waveguide 130c. A laser source is identical to that shown in Fig. 5. An operation of the waveguide amplifier 100 shown in Fig. 7 will be briefly described. The signal light at 1.3-µm wavelength band is incident on the planar waveguide 130a through the planar waveguide 130b. The excitation light at the 0.80-µm wavelength band from the excitation light source such as a semiconductor laser is also incident on the planar waveguide 130a. The excitation light excites the Nd 3+ serving as the active ion. The excited Nd 3+ is stimulated by the signal light, and radiation light at the 1.3-µm wavelength band is generated. When the excitation light exceeds a predetermined intensity, the signal light is amplified. In those embodiments, the host glass used in the core of the optical fiber or the planar waveguide consists of a silicate multi-component glass. However, the composition of the host glass is not limited to this. For example, a phosphate glass and borate glass may be used or may be added in the above composition. In addition, the resonator used in the fiber laser may be of a type using a dielectric mirror or the like. From the invention thus described, it will be obvious that the invention may be varied in many ways. Such variations are not to be regarded as a departure from the spirit and scope of the invention, and all such modifications as would be obvious to one skilled in the art are intended to be included within the scope of the following claims.

Claims: An oxide-based optical glass containing Nd 3+ as an active ion doped in a host glass which includes Rb and/or Cs; characterised in that the host glass comprises at least 10 mol % of Rb and/or Cs and 20-45 mol % of total alkali elements. An oxide-based optical glass according to Claim 1, which is capable of causing a shift in the ESA peak wavelength in optical amplification and optical oscillation at a 1.3 µm wavelength band when light of the 1.3 µm wavelength band and light of the 0.8 µm wavelength band simultaneously enter the glass. An oxide-based optical glass according to Claim 1 or Claim 2, wherein said host glass further comprises one or more alkaline-earth elements. An oxide-based optical glass according to Claim 3, wherein the alkaline-earth element(s) are at least one of Mg and Ca. An optical fiber comprising a core made of an optical glass according to any preceding claim. An optically active device comprising: (i) an optical fiber according to Claim 5; (ii) a light source for generating excitation light at a 0.80 µm wavelength band or a band near the 0.80 µm wavelength band; and (iii) optical means for directing light emitted from said light source to said optical fiber. A fiber amplifier comprising: (i) an optically active device according to Claim 6; and (ii) coupling means for coupling signal light at a 1.3 µm wavelength band or a band near the 1.3 µm wavelength band into said optical fiber. A fiber laser comprising: (i) an optically active device according to Claim 6; and (ii) a resonator means for feeding light at a 1.3 µm wavelength band or a band near the 1.3 µm wavelength band from said optical fiber back to said optical fiber. A waveguide device comprising a planar waveguide made of an oxide-based optical glass according to any of Claims 1-4. A waveguide device according to Claim 9, wherein said device is capable of propagating light at a 1.3 µm wavelength band or a band near the 1.3 µm wavelength band. An optically active device comprising: (i) a waveguide device according to Claim 9; (ii) a light source for generating light capable of exciting Nd 3+ ; and (iii) optical means for directing light emitted from said light source to said planar waveguide. An optically active device according to Claim 11, wherein the light source generates light at a 0.80 µm wavelength band. A waveguide amplifier comprising: (i) an optically active device according to Claim 12; and (ii) means for coupling signal light at a 1.3 µm wavelength band to said planar waveguide. A waveguide laser comprising: (i) an optically active device according to Claim 12; and (ii) a resonator means for feeding light at a 1.3 µm wavelength band from said planar waveguide back to said planar waveguide.

Inventors: CHIGUSA YOSHIKI, MIYAJIMA YOSHIAKI, NAKAZATO KOJI, ONISHI MASAHI, WATANABE MINORU, CHIGUSA, YOSHIKI, MIYAJIMA, YOSHIAKI, NAKAZATO, KOJI, ONISHI, MASAHI, WATANABE, MINORU, Chigusa, Yoshiki, c/o Yokohama Works of, NAKAZATO, KOJI, C/O YOKOHAMA WORKS OF, Onishi, Masahi, c/o Yokohama Works of, WATANABE, MINORU, C/O YOKOHAMA WORKS OF
Applicants: NIPPON TELEGRAPH & TELEPHONE, SUMITOMO ELECTRIC INDUSTRIES, NIPPON TELEGRAPH AND TELEPHONE CORPORATION, SUMITOMO ELECTRIC INDUSTRIES, LIMITED
Application year: 1991
Main classification: C03C4
IPC codes: H01S3, G02F1, C03C3, G02B1, G02B6, C03C4, C03C13