Surface treated Al or Al alloy material

Abstract: Surface-treated Al or Al alloy materials which excel in adhesive property, formability, weldability, phosphatability, paint adhesion, and post-painting corrosion resistance are provided by forming a coated layer containing Zn and Fe or one or more of Si oxides, Al, oxides end Al hydroxides together therewith, on the surface of Al or Al alloy base. The surface-treated Al or Al alloy materials are useful as metallic material to be painted and used after press forming and other processing, spot or laser welding and phosphating, including panel materials for automobiles and other various vehicles, shells for housefold electrical apparatus, and building materials.

Description: BACKGROUND OF THE INVENTION Field of the invention The present invention relates to surface-treated Al or Al alloy materials which excel in adhesive property, formability, weldability, phosphatability, paint adhesion, and post-painting corrosion resistance and which are used in the applications wherein they are painted and used after subjected to press forming and other processing, spot or laser welding and phosphate treatment, including panel materials for automobiles and other various vehicles,shells for household electrical apparatus, and building materials. Description of the prior art Al or Al alloy materials (hereinafter identified as Al alloy materials) are lightweight and possess superb corrosion resistance and designability, and have found extensive applications as shells for household electrical appliances and building materials. During recent years, Al alloy materials have come to be employed in automobiles and other vehicles in order to reduce the weight of the body. With this, there have been increasing opportunities for them to be pressed, welded and further painted. However, since Al alloy materials have their surfaces covered with stable oxide film (passsive state coating), they are poor in adhesion, formability, weldability (spot welding and laser welding) and paintability. They have poorer property, which is done as surface treatment before painting, and thus there is a problem that paint adhesion and post-painting corrosion resistance have not been improved. In the field of automobiles, the various parts are press-formed into specified form, assembled with spot welding and laser welding, or joined to the specified locations with adhesive. Al alloy materials possess inferior adhesive property and formability to the ordinary steel plate, and also have inferior spot weldability and laser weldability. During a phosphating process conducted to improve paintability, Al dissolves from the surface of an Al alloy material into a phosphating bath, and the dissolved Al ion impedes to the formation of phosphate coatings on the surface of the metal to be treated. To overcome this problem, in Japanese Patent Publication No. 157693/1986, a process is proposed in which Zn or Fe plating is formed on the surface of Al alloy materials, to prevent the dissolving of Al ions. These coated layers offer poor adhesive property on Al alloy materials, so that there occurs exfoliation of these coatings during a press forming or a spot welding process. Acccordingly, Al dissolves, preventing the formation of fine phosphating coating, or bare Al surface is oxidized resulting in poor phosphating property, if the waiting time from the press forming to phosphating process is longer. SUMMARY OF THE INVENTION The present invention has been made considering the aforestated circumstances. The objective hereof is to provide surface-treated Al or Al alloy materials which are excellent in formability and phosphatability, and also in paint film adhesive property after phosphating and corrosion resistance after painting (filiform corrosion resistance and film blister resistance), Another objective of this invention is to provide Al or Al alloy materials having good weldability and adhesive property. Further objective of the present invention is to provide painted surface-treated Al or Al alloy materials excelling in paint film adhesive property and corrosion resistance by phosphating said surface-treated Al or Al alloy materials to form better conversion coating and painting the same. The other objectives of this invention will be clarified when the following descriptions are read through. DISCLOSURE OF THE INVENTION These objectives are achieved by the features of the present next of claims. The above objectives of the present invention are accomplished by forming on the surface of Al alloy base materials: a coating chiefly comprised of Zn and Fe, that is, a Zn-Fe coating which contains 1 to 99wt% Zn and 99 to 1wt% Fe, is metallographically structured of a mixed phase of η phase of Zn and α phase of Fe and contains no Zn-Fe intermetallic compounds; the average crystal particle size constituting the coating being 0.5 µm or less; the coating weight being in the range of 0.1 to 3g/m². Preferably a Zn-Fe coating may be used which is identified as containing 1 to 25wt% Fe and 99 to 75wt% Zn, in addition to the above requirement. Further, a compound coating may be used comprised of: 1 to 25wt% Fe; 98 to 55wt% Zn; and, 1 to 20wt% compound selected from among Si oxides, Al oxides and Al hydroxides. The above Zn-Fe coating improves the formability, adhesive property, spot weldability, and laser weldability, as well as remarkably enhances phosphatability. Such effect can be displayed most effectively by setting the coating weight of the above Zn-Fe coating at 0.1 to 3g/ m². In phosphating a surface-treated Al alloy material on which the above Zn-Fe coating is formed, all of the Zn and Fe in said coating are converted into chemical conversion coatings consisting of hopeite and/or phosphophyllite at the time of conclusion of the above phosphating process; thereafter, paint coatings are formed. The above mentioned process can give painted Al alloy materials with superb paint adhesion and post-coating corrosion resistance. BRIEF DESCRIPTION OF DRAWINGS FIGS. 1 and 2 show the test results obtained with embodiments of the present invention. FIG. 1 is a graph indicating relationships between the bead drawing load and coating weight in a bead drawning test, while FIG. 2 is a graph depicting relationships between the rectangular tube drawing height and coating weight in a rectangular tube drawing test. DETAILED DESCRIPTION OF THE INVENTION The inventors of the present invention first examined the formation of coated layers primarily composed of Zn and Fe with good lubricating ability on the surface of Al alloy materials, in order to improve the formability thereof. It was found that even with the same Zn-Fe coating composition, formability varies with varying phase structures. In the Zn-Fe coating produced by the normal electroplating, Zn-Fe intermetallic compounds, including Γ phase and δ phase are generated, thereby making it easier for the coating to peel off during a forming. This is presumably due to the fact that since the foregoing Zn-Fe intermetallic compounds are hard and brittle, they are subjected to the so-called powdering phenomenon in which they are cracked during a processing and peel off in a powdery fashion. Nevertheless, where the phase structure of a Zn-Fe coating is of a mixed phase of η phase of Zn and α phase of Fe, and does not contain any Zn-Fe intermetallic compound, it was confirmed that no such powdering phenomenon occurs, giving excellent formability. It was also confirmed that said η phase and α phase in the Zn-Fe coating forms a local cell with the above η phase as anode and α phase as cathode on the surface of the coating during a phosphating process, thus making it easier to form an even and fine phosphated coating. There is no restriction on the procedures for the formation of Zn-Fe coating with the aforestated phase construction. Yet, it can be easily obtained by the use of a displacement plating using plating bath containing Zn and Fe ions. The content of Zn and Fe in said Zn-Fe coating is set in a range as wide as 1 to 99wt% for Zn and 1 to 99wt% for Fe, preferably 80 to 98wt% for Zn and 2 to 20wt% for Fe. The effect on, formability of the phase construction of Zn-Fe coatings have been discussed above. In addition to this, the average grain size of the crystals constituting the Zn-Fe coating is closely associated with formability. The coatings with a mean grain size of 5 µm or less offer good lubricating ability and excellent processability. They can also produce a fine phosphate coating because a greater number of nuclei are generated in the formation thereof during a phosphate treatment due to finer grain sizes of the crystals. As a result, the adhesion of the paint produced thereon is enhanced, and the post-painting corrosion resistance improved. To obtain Zn-Fe coatings with the above mean crystal grain size, the contents of Zn and Fe constituting said coating should be set at 99 to 75wt% for Zn and 1 to 25wt% for Fe, preferably at 98 to 80wt% for Zn and 2 to 20wt% for Fe. Where this Zn-Fe coating that meets such requirement for mean crystal grain size consists of the abovementioned mixture of η phase of Zn and α phase of Fe, it offers much better formability and phosphatability. Al alloy materials on which the Zn-Fe coatings meeting the above constituent requirement is exceedingly good in adhesion property, and they can be adhered strongly on various adherends using known adhesives. As has been discussed previously, according to the present invention, formability, adhesion property and phosphatability of Zn-Fe coatings which are formed on the surface of Al alloy base materials can be improved as noted above by specifying the phase construction or mean crystal grain size thereof. Furthermore, it was confirmed that the coatings whose reflectance of laser on the surface of the Zn-Fe coating is less than 3% provide extremely good laser weldability, and' that reliable welding couplings can be obtained with high-speed welding using laser beams. As other means to improve formability, adhesive property and phosphatability of Al alloy base materials, a procedure to include at least one chemical to be selected from among the Si oxides, Al oxides and Al hydroxides into a Zn-Fe coating can be provided. By leaving these oxides and hydroxides diffused in the Zn-Fe coatings, these offer an action as solid lubricant, and the sliding characteristics of said coating during a forming are improved markedly in combination with the lubricating operation the Zn-Fe coating materials themselves possess, providing superb formability. Si oxides, Al oxides and Al hydroxides have a function to improve affinity with adhesives having a polar group, contributing to the improvement in adhesive property. These oxides and hydroxides have large electrical resistance and helps to increase exothermic efficiency during a spot welding, hence enhancing formability and spot weldability. In such a case, it is preferred that because the Al oxides and Al hydroxides could degrade phosphatability they are caused to disperse into a Zn-Fe coating to prevent, the excessive precipitation thereof to the surface, and that they are allowed to exist in a dispersion state where Zn-Fe is a continuous phase. The Si oxides will not reduce phosphatability, and hence they can be stratified on the surface of Zn-Fe coatings. This permits improving adhesion property, formability and spot weldabilty more effectively. To improve the adhesion of such coating on Al alloy base material, it is preferred to make the interface side thereof Fe-rich. The most preferred coating composition in a composite coating of Zn, Fe and Si oxides is of roughly three-layer structure in which the interface side of the Al alloy base material is of Fe-rich layer, the upper side of Zn-rich layer, and Si oxide layer is formed on the uppermost layer side. It is to be noted that these various layers allow some interdiffusion thereamong. As has been discussed earlier, in a coating in which Si oxides, Al oxides or Al hydroxides are compounded with Zn and Fe, the lubricating action of Si oxides gives better formability, and hence any phase structure and mean crystal grain size of Zn and Fe are applicable. In this case, however, the Zn-Fe phase which constitutes a mixed phase of η phase of Zn and α phase of Fe is structured as previously mentioned, and the mean crystal grain size is made 0.5µ m or less. Such coating can be readily obtained by a displacement plating, as also discussed above. Surface treated Al alloy materials thus obtained are preferred because they exhibit superior laser weldability when the reflectance of laser beams stands at less than 3%, hence allowing efficacious and stable welding with laser welding. The preferable composition ratio is as follows: Zn : 98 to 55wt% (more preferably 95 to 60 wt%) Fe : 1 to 25wt% (more preferably 2 to 20wt%) At least one compound (A) selected from the group consisting of Si oxides, Al oxides and Al hydroxides : 1 to 20wt% (more preferably 3 to 20wt%) If the content of the compound (A) is less than the range as mentioned above, the effect of the addition thereof is not sufficiently exhibited. On the contrary, if it is excessive, the coating becomes brittle, and is more apt to cause powdering during a forming. If the content of Fe in the coating is less than the range as mentioned above, formability and phosphatability are insufficient. If it is beyond the above scope, the adhesiveness of said coating on the Al alloy base material is reduced, causing the peeling of the coating in the press forming. The structure of the coating produced on the surface of Al alloy base materials according to the present invention is as indicated above. It contains Zn and Fe and one or more of the compound (A) to be selected from the group of Si oxides, Al oxides and Al hydroxides together with the Zn and Fe as essential components. The coating may, as other components, contain a very tiny amount of Cu, Mg, Cr, Mn and other metals and oxides and hydroxides thereof as long as they do not adversely affect the aforestated effects. The preferred method of forming said coating is displacement plating, electroplating or a combination of the both, the most preferable of them being displacement plating. If the displacement method is employed, it can be performed normally with an alkaline solution containing Zn ions and Fe ions as plating bath. If Al ions are allowed to exist in this plating bath, a composite coating can be provided in which Zn-Fe is a continuous phase and Al hydroxides are dispersed therein. If silicate is allowed to exist in said plating bath, a coating can be obtained in which a Si oxide layer is formed on the topmost layer thereof made up of Zn-Fe. If an electroplating is conducted while stirring an acid Zn-Fe coating liquid in which Al oxide powder is dispersed, a composit coating can be formed in which Al oxides are diffused in Zn-Fe. There are no special limitations on the kind of Al alloy base materials to which the present invention is applicable. They can include Al and various Al alloys containing more than one of the metals, such as Mg, Cu, Mn, Si, Zn, Cr, and Ni, as alloy element, the most commonly used of which are Al-Mg alloys and Al-Mg-Si alloys. It is also possible that pure Al is employed as base material for the shapes thereof, the plate-shaped objects (thin plates and thick plates), rod shapes, linear shapes and tube shapes can be used depending on applications and objectives. The surface-treated Al alloy materials of the present invention are obtained by being formed with a press, joined with other members due to welding, then forming a chemical conversion coating through phosphate treatments, and then forming a cosmetic coating. In order to improve the paintability, paint adhesion and post-paint corrosion resistance of the paint during the formation of the coating, it has become apparent that all of the Zn and Fe in the aforestated Zn-Fe coating should be converted into a chemical conversion coating which consists of zinc phosphate (hopeite) and/or zinc iron phosphate (phosphophyllite) to eliminate Zn and Fe in a chemically converted state. Galvanized steels is accomplished primarily to use sacrificial anode action of Zn coatings to improve the corrosion resistance thereof, and in order to improve the corrosion resistance (particularly anti-perforating property) of the steel, it is necessary to leave the Zn coating even after a phosphate treatment. Producing Zn-Fe coating on Al alloy base materials according to the present invention is for the purpose of improving phosphatability, as well as adhesion, formability and weldability as previously discussed. Al alloy materials themselves possess good anti-perforation property, and hence it is not required to leave the Zn-Fe coatings even after phosphate treatments are applied to improve paint adhesion for enhanced paint adhesion following a press forming and welding operation. Rather, if the metal Zn and Fe remain after the chemical conversion treatment, they cause a corrosion reaction under corrosive environments, giving rise to blisters. In phosphating the aforestated surface-treated Al alloy materials of the present invention prior to paint application, if all of the Zn and Fe in the Zn-Fe coating is converted into zinc phosphate (hopeite) and/or zinc iron phosphate (phosphophyllite) prior to paint application, then superb paint adhesion can be obtaind, and there is no blister and good post-paint corrosion resistance can be shown even when the painted Al alloy material is exposed to corrosive environments. The composition of chemical conversion coatings (phosphate-treated coatings) provided by phosphate treatment depends on the content of Zn and Fe which constitute Zn-Fe coatings. Where the content of Fe in said coating is less than approximately 70wt%, a chemical conversion coating composed substantially of zinc phosphate is given. Where the content of Fe is beyond 70wt%, a chemical conversion coating consisting of a mixture of zinc phosphate and zin iron phosphate is provided. Both phosphate-treated coatings give peerless paint adhesion and post-paint corrosion resistance. For the surface-treated alloy materials according to the present invention, all of the Zn and Fe in Zn-Fe coatings Subjected . to phosphate treatment must be converted into phosphate. If the thickness of the Zn-Fe coating is too thick, Zn and Fe could remain after the phosphate treatment, making it impossible to fully improve post-paint corrosion resistance. Accordingly, the thickness is controlled to be 0.1 to 3g/m² in the coating weight of Zn-Fe coatings, more preferably to some 2.0 g/m² to 0.1g/m². If the coating weight is too small, it becomes difficult to cover the surface of Al alloy base materials evenly with coating materials, making it difficult to fully improve formability and weldability. The coating weight is therefore 0.1g/ m² or greater, more preferably 0.5g/m² or more. The Al alloy materials covered with the Zn-Fe coating whose weight is 0.1 to 3g/m², more preferably 0.5 to 2.0 g/m² provide excellent formability, weldability and phosphatability due to the action of the coating. The Zn and Fe in said coatings are all converted into chemical conversion coatings, comprised of zinc phosphate or zinc iron phosphate, providing superb paintability and painted Al alloy materials with good post-paint corrosion resistance which causes no blister. There is no special restriction on the kinds of coatings to be applied on the surface of chemical conversion coatings' (phosphate-treated coatings), but especially preferred is the one whose primary component is a resin having polar group, including hydroxyl group and amino group, in the molecule thereof. Use of such resin paint forms a hydrogen bond between the polar group in the coatings and the phosphate-treated coating, giving a high level of paint adhesion, as well as post-paint corrosion resistance. These preferred resin coatings include epoxy resin coatings, alkydmelamine resin coatings,acryl resin coatings, and polybutadiene resin coatings. The epoxy resin coatings and alkydmelamine resin coatins are, among others, excellent in paint film characteristics, and thus are recommended as particularly preferable. Then, examples will be illustrated to give more specific description of the construction and operation of the present invention, which is not restricted by the following embodiments. EXAMPLE EXAMPLE 1 In order to confirm the improvements in formability and phosphatability by structuring the phase of the Zn-Fe coatings formed on the surface of Al alloy base materials in a mixed structure of η phase and α phase, the following experiments were conducted. Using a rolled plate made up of an Al plate, Al-Mg alloy (JIS A 5182) and Al-Si-Mg alloy (JIS A 6009), various Zn-Fe platings as indicated in Table 1 were provided on the surface thereof with a displacement plating or an electroplating to examine the phase structure of the coating with X ray diffraction method. For the coating weight and coating constitution of the coating, the coating weight was determine'd from the reduced amount of the weight after the coating was dissolved and removed with concentrated nitric acid, and the coating composition determined through the chemical analysis of the dissolved coating composition. The formability and phosphatability of the coating materials obtained were examined in the following procedures. The result is shown in Table 1. Formability: evaluated on the basis of the maximum height in an Ericksen cupping test Size of Al alloy base material : 1.0 × 70× 200mm Wrinkle control power: 1.1mmt Punch diameter : 20mm  Evaluation : ○ Max. height: more than 9mm Δ Max. height: 8.5 to 9mm , × Max. height: 8.5mm Phosphatability : evaluated for coated percentage of tage of the phospate-treated coating subjected to a 2-min. phosphate treatment using commercially available immersion type phosphate treatment liquid ("Palbond U" (registered trade mark) by Nihon Parkerizing Co., LTD.) Evaluation : ○ Coating percentage more than 95% Δ Coating percentage 85 to 95% × Coating percentage 85% or less As indicated in Table 1, the embodiments 1 to 9 of the present invention offered superior formability and phosphatability, and no peeling of the coating was found. On the other hand, the poorer formability or phosphatability was shown in reference examples 10, 11 to 14 and 15, respectively because the coating weight was insufficient (for reference example 10), because the coatings were not comprised of η phase and α phase (for reference examples 11 to 14), and because no coatings were formed (for reference example 15). In the reference examples 13 and 14 in which coatings were formed by the normal electroplating method, peeling off of the coatings occurred since Zn-Fe intermetallic compound was contained therein. Example 2 In order to confirm the effect upon formability and post-painting corrosion resistance of the mean crystal grain size in the Zn-Fe coating formed on the surface of Al alloy base materials, the following experiments were conducted. Using the same Al alloy rolled plate as was employed in Example 1, various Zn-Fe coatings as shown in Table 2 were formed on the surface thereof by a displacement plating or an electroplating. As a means to mix SiO₃, Al₂O₃, or Al (OH)₃, in the Zn-Fe coatings, a displacement plating using a bath containing silicate and Al ions and Al2O3 dispersive plating were adopted. The mean crystal grain size in the coatings obtained were examined through the observation with a scanning electon microscope. These coatings were examined for formability and filiform corrosion resistance after coated in the following methods. The results were indicated collectively in Table 2. Formability : evaluated on the basis of drawing height in a rectangular tube drawing test. Shape of Al alloy base material : 1.0 × 90 × 90(mm) Wrinkle control force : 2 ton Punch diameter : 40mm  [Evaluation criteria] ○ Drawing height of rectangular tube more than 13mm Δ Drawing height of rectangular tube 12 to 13mm × Drawing height of rectangular tube 12mm or less Filiform corrosion resistance : The coatings under test were subjected to phosphate treatment, with all the Zn and Fe in the Zn-Fe coatings converted into hopeite or phosphophyllite, forming a paint film by applying 20 µ m epoxy coating (by Nippon Paint Co., LTD.). The paint film was cross-cut to make evaluations based on the length of filiform corrosion which occurs after 8 cycles of the following corrosion tests. Salt spray test (35 °C × 24H) ↓ Humidity cabinet test (80%RH, 50°C × 120H) ↓ Allowed to stand in a room (room temperature × 24H) [Evaluation criteria] ○ Length of filiform corrosion 1mm or less Δ Length of filiform corrosion 1 to 2mm × Length of filiform corrosion 2mm or more As indicated in Table 2, Nos. 1 thru. 7, which meet the specified requirement of the present invention offered superior formability and filiform corrosion resistance, with no peeling of the coating observed. On the contrary, Nos. 8, 9, 10, 11 and 13, and 12 show poorer formability and filiform corrosion resistance. This was due to the following respective reasons: no plating was provided for No. 8, the content of Fe was too low for No. 9, the content of Fe was too high for No. 10, the mean crystal grain size in the coating was too large for Nos. 11 and 13, and the coating weight was too excessive for No. 12. Example 3 To determine the effect exerted upon formability and spot weldability by the co-existence of Si oxides in the Zn-Fe coatings formed on the surface of Al alloy base materials (particularly, the existence of Si oxides on the surface side of said coating), the following test was conducted. After the rolled plate comprised of the same Al alloy as employed in Example 1 was subjected to various surface treatments as indicated in Table 3, coatings of the composition as shown in Table 3 were formed by a displacement plating or an electroplating. Analysis into the surface of the coatings obtained with ESCA confirmed that the coatings of the example of the present invention (Nos. 1 thru. 7) were formed of metal Fe-rich layer, metal Zn-rich layer and Si-oxide-rich layer from the interface therof with the Al alloy base material. The coating weight and composition of the coatings were determined in the same manner as aforestated. The coated materials obtained through the above procedure were examined for formability, phosphatability and post-paint corrosion resistance (filiform corrosion resistance) in the following procedures. Formability: Identical to the evaluation method as indicated in Example 1 above. Phosphatability: Using commercially available immersion-type phosphate treatment solution (same as above), all of the Zn and Fe in the coatings of the metal plated materials involved were put to chemical conversion until they are converted into hopeite or phosphophyllite, to examine the precipitation amount and state of the phosphated coatings (chemical conversion coatings) obtained. Precipitation state: ○ : (The whole portion is covered with chemical conversion coatings.) Δ: (Some portions are left uncovered with chemical conversion coatings.) × : (More than 1/2 of the whole surface remains uncovered with chemical conversion coatings.) Post-paint corrosion resistance (filiform corrosion resistance): After all of the Zn and Fe in the coatings are converted into phosphate through phosphate treatment, 20 µ m thick epoxy resin (by Nippon Paint Co.,LTD.) was applied to form a film. Then, after the coatings were cross cut, post-paint corrosion resistance was evaluated in terms of the length of filiform corrosion that occurs after 5 cycles of the following corrosion tests. This evaluation result was indicated as comparison with the length of filiform corrosion at the test, conducted concurrently by using cold-rolled steel sheet. Salt spray test (5%NaCl, 35 °C × 24H) ↓ Humility cabinet test (50 °C × 85%RH, 6 days) Filiform corrosion resistance ○ (better than with painted cold-rolled plate) ○ (equivalent to when painted cold-rolled plate was used) Δ (somewhat worse than with painted cold-rolled plate) × (worse than with painted cold-rolled plate) As shown in Tables 3 and 4, the examples of the present invention (Nos. 1 thru. 7) offer good formability, with no peeling off of the coatings, and give excellent phosphatability and filiform corrosion resistance after painting. No. 8 offers poor formability, phosphatability and filiform corrosion resistance after painting since it was not subjected to plating. Nos.9 and 10 had excessive coating weights, and thus peeling off of the coatings is easy to occur during a processing, and the post-paint filiform corrosion resistance is insufficient since not all Zn and Fe in the coatings can be converted during a phosphate treatment process. Example 4 To determine the effect on formability and spot weldability of the co-existence of Al oxides or Al hydroxides in the Zn-Fe coatings formed on the surface of Al alloy base materials, the following experiments were conducted. Coatings of various compositions as shown in Table 5 were formed on the surface. of rolled plate made up of the same Al alloy as used in Example 1 by a displacement plating or an electroplating. The coated materials were examined for formability and spot weldability in the following manner. As a procedure to include Al oxides or Al hydroxides in the coatings, the one to leave Al ions and Al₂O₃ particulates mixed in a plating bath. As preferable embodiments, experiment results with the coated materials with coatings on the surface of which Si oxide-rich layer was formed) is indicated in Table 5. Formability: evaluated in terms of the maximum draw load at a draw bead test. Size of Al alloy base material: 10 × 40 × 400mm Drawing velocity : 300mm/min. Bead pressure : 500kgf Evaluation : ○ Maximum drawing load 500kgf or less Δ Maximum drawing load 550 to 650 kgf × Maximum drawing load 650 kgf or more Spot weldability: evaluated on the basis of the number of continuous spots in a spot welding. Welding current : 32kA Welding force : 300kgf Energizing time : 4/50s Electrode : Cu-1%Cr Evaluation: ○ Number of continuous spots 300 or more Δ Number of continuous spots 250 to 300 × Number of continuous spots 250 or less As indicated in Table 5, Nos. 1 thru. 7 which meet the specified requirements of the present invention offerred good formability and spot weldability, with no peeling off of the coatings occurring. On the contrary, no coatings were formed for No. 8; the content of Al hydroxides or Al oxides was insufficient for No. 9; the content of Al hydroxides or Al oxides was excessive for No. 10; the coating weight was insufficcient for No. 11; the content of Fe in the coatings was insufficient for No. 12; the content of Fe was excessive for No. 13; and, the thickness of Si oxides was too much. For these reasons, these metal plated materials offer poorer formability or spot weldability. The metal plated materials at Nos. 1 thru. 7 above were phosphate-treated in the same manner as in Example 2, and applied with epoxy resin paint to examine for filiform corrosion resistance. All of them indicated excellent phosphatability and good filiform corrosion resistance after painting. To confirm the effect of improvements in formability with the Zn-Fe coatings in which SiO₂, and Al₂,O₃, were diffused, the following experiments were conducted further. By using Al alloy (Al-4.5Mg-0.4Cu) as base material, and providing chemical displacement plating onto the surface thereof in similar manner as described above, various coatings with different coating weight (0 to 1.25g/ m² ) comprised of Zn (87.3%)-Fe(3.8%)-SiO₂(3.5%)-A1₃O₈ (5.4%) were formed. With the various metal plated materials obtained, formability tests (bead drawing test and rectangular drawing test) were made in similar manner as described above, giving the results as indicated in FIGS. 1 and 2. FIG. 1 indicates the results of the bead drawning test, which shows the effect of coating weight on bead drawing load. FIG. 2 shows the results of the rectangular drawing test, which indicates the effect of coating weight on rectangular drawing height. As is apparent from these figures, even when lubricating oil is used during a process, the metal plated materials with no coatings formed thereon provide extremely poor formability, but they offer markedly improved formability when coatings are formed. Superb formability can be obtained by making the coating weight 0.5g/ m² or more. Example 5 As has become apparent in Example 4 above, the metal plated materials in which Si oxide-rich layers are formed in the topmost layer of the Zn-Fe coatings exhibit excellent characterisctis in formability and spot weldability. Furthermore it was confirmed that adhesion property is remarkably enhanced, and hence the results will be indicated below. With 0.8mm-thick alloy plate (for T-shaped peeling test) made up of Al-Mg alloy (JIS A 5182) and 1.6mm-thick Al alloy plate (for shearing test), chemical displacement plating was provided on both Al alloy plates using a plating bath containing 5 to 10% SiO₃, together with Zn ions and Fe ions, forming Zn-Fe coatings with compositions as indicated in Table 6. The metal plated materials obtained were subjected to 180° T-shaped peeling tests (adhesion area = 25mm wide × 75mm long) and 180° shearing test (adhesion area = 25mm wide × 12mm long) using epoxy structural adhesive or synethetic rubber adhesive as adhesive, in accordance with the procedures as specified in JIS K 6829, examining the adhesive property based on the broken area of the interface at the adhesive broken surface. The smaller broken area of the interface means the better adhesive property between the material under test and the adhesive. The tensile speed at the time of T-shaped peeling test was 200mm/min and that of the sheer test at 50mm/min. To determine the adhesion of the coatings on Al alloy plates, the peeling area of the coatings when the cellophane tape adhered on the surface thereof is forced off. The smaller peeling area means the better adhesion of the coatings on Al alloy base material. The results are indicated as shown in Table 6 collectively. Zn-Fe metal plated materials having Si oxide-rich layers in the topmost layer thereof are found to offer good adhesion with Al alloy base material and excellent adhesive property when joined with adhesive. Example 6 As has been apprarent from the aforestated Examples 1 to 5, formability, spot weldability, phosphatability and post-paint corrosion resistance, adhesive property and the like have been improved by forming Zn-Fe coatings on the surface of Al alloy base materials. When laser reflectance was also examined, it was confirmed that metal plated materials in which the laser reflectance of the surface of the Zn-Fe coatings is less than 3% shows good laser weldability. The results are indicated below. Zn-Fe coatings of compositions as indicated in Table 7 were formed on the surface of Al-Mg alloy plates (JIS A 5052 or JIS A 5182) (average roughness along the centerline Ra = 0.35 µ m) with an electroplating or a displacement plating. Each of them were measured for laser beam reflectance, and for laser weldability. For Nos. 4, 8, 12 and 16 in Table 7, chemical displacement plating was employed using a plating bath containing SiO2 together with Zn ions and Fe ions. For the other materials, elecroplating was employed using a plating bath containing Zn ions and Fe ions. The laser reflectance was determined from the reflectance when laser beams are radiated parallel with the roll direction at an incidence angle of 45° and a reflection angle of 45°. For laser welding, CO₂ laser was used, with laser output at 2.5 kW, welding speed at lm/min, and with shield gas being 100% Ar, and the flow rate thereof at 30 l/min. The evaluation of laser weldability was made through observations of the appearance of welded portions and internal defects in accordance with the 5-step marking, with the excellent welded portions having no defects marked at 5, and faulty ones having many defects at 1. In Table 7, Nos. 1 to 4 and Nos. 9 to 12 show laser beam reflectance as low as 3% or below, offering good laser weldability both for butt and lap weldings. On the contrary, Nos. 5 to 7 and Nos.13 to 15 have laser beam reflectance of more than 3%, with the consequent poor laser weldability. For Nos.8 and 16, there is too much coating weight, and SiO2 are included in the welded portion as impurities, resulting in degraded weldability. For this reason, to ensure excellent laser weldability, it should be done that the laser beam reflectance on the surface of the coating is 3% or below, and that the coating weight is controlled to 3g/ m² or less. Example 7 In this example, for painted Al alloy materials which are obtained by forming Zn-Fe coatings on the surface of Al alloy base material, phosphating the same into chemical conversion coatings and then applying top coat thereon, it was examined how the metal Zn and metal Fe remaining under the chemical Conversion coating as ground might affect the corrosion resistance of the painted Al alloy material filiform; corrosion resistance and blister). On the surface of rolled plate comprised of the same Al alloy as used in Example 1, 0.01 to 1 µ m Zn-Fe coatings were formed by the identical displacement plating as aforestated, degreasedi and cleaned. Then, all of the Zn and Fe in the coatings were converted into hopeite and/or phosphophyllite with phosphate treatment. As phospate treatment solution, "Palbond U" (registered trade mark) by Nihon Parkerlizing Co.,LTD. was employed. On the surface of the phosphated matter obtained, alkydmelamine resin paint was applied so that the dry film thickness was about 20µ m. The resultant product was subjected to baking finish at 130 °C for 20 minutes to give painted Al alloy plates. As reference example, painted Al alloy plates were obtained in the same manner as above, except that Zn-Fe coatings were applied thereon, and thereafter some degree of phosphate treatment was provided so that some of the metal Zn and metal Fe in said coatings remained. The plates under test obtained were examined for filiform corrosion resistance and blister resistance in the following procedures. Filiform corrosion resistance: The surface of the plates under test was cross cut, and the filiform corrosion resistance was evaluated on the basis of the maximum length of filiform corrosion which occurred after 4 cycles of the same corrosion tests as in Example 2. ○ : Max. filiform length <1mm Δ : Max. filiform length 1 to 4mm × : Max. filiform length 4mm< Blister resistance: The surface of the plates under test were cross cut, and put to 840 hours of salt spray test. The maximum blister width from the cross cut portion was determined, and blister resistance was evaluted according to the following criteria. ○ : Max. blister width <1mm Δ : Max. blister width 1 to 4mm × : Max. blister width 4mm< The results are indicated in Table 8 collectively. As is apparent from Table 8, the plates in which all Zn and Fe in the coatings thereof were converted into phosphate during a phosphate treatment process (Nos. 1 to 10) offer superior filiform corrosion resistance and blister resistance. On the contrary, those in which Zn and Fe remain after phosphate treatment (Nos. 11 to 16) have poor filiform corrosion resistance or blister resistance. As is obvious from the results, to achieve excellent corrosion resistance after painting according to the present invention, all of the metal Zn and the metal Fe in the Zn-Fe coatings are converted during a phosphate treatment process. Surface-treated Al or Al alloy materials which excel in adhesive property, formability, weldability, phosphatability, paint adhesion, and post-painting corrosion resistance are provided by forming a coated layer containing Zn and Fe or one or more of Si oxides, Al oxides and Al hydroxides together therewith, on the surface of. Al or Al alloy base. The surface-treated Al or Al alloy materials are useful as metallic material to be painted and used after press forming and other processing, spot or laser welding and phosphating, including panel materials for automobiles and other various vehicles, shells for housefold electrical apparatus, and building materials.

Claims: A surface-heated Al or Al alloy material characterized by a coating primarily composed of Zn and Fe in an amount of 99 to 1 weight % and 1 to 99 weight %, respectively, and formed on the surface of an Al or Al alloy base material, a mixed phase of eta-phase of Zn and α-phase of Fe without showing Zn-Fe intermetallic compounds, wherein the mean crystal grain size in said coating is 0.5 µm or less, the coating weight is in the range of 0.1 to 3 g/m². A surface-treated Al or Al alloy material according to claim 1, modified in that the content of Zn and the content of Fe in said coating are 98 to 55 weight % and 1 to 25 weight %, respectively and that the coating is furthermore composed of 1 to 20 weight % of a compound of at least one selected from the group of Si oxides, Al oxides and Al hydroxides. A surface-treated Al, or Al alloy material as specified in claim 2, characterized in that the coating comprises Si oxides. A surface-treated Al or Al alloy material as specified in any of claims 2 or 3 , characterized in that the coating is stratified in the order of metal Fe, metal Zn and Si oxides from the interface of an Al or Al alloy base material. A surface-treated Al or Al alloy material according to claim 2, characterized in that the coating comprises Al oxides and/or Al hydroxides. A surface-treated Al or Al alloy material according to claim 2 or 5, characterized in that Al oxides and/or Al hydroxides are dispersed evenly in the coating. A surface-treated Al or Al alloy material as specified in any of claims 2 to 6, characterized in that a layer of Si oxide is formed on the topmoste layer of the coating. A process for producing a surface-treated Al or Al alloy material as specified in any one of claims 1 to 7, wherein said coating is formed by displacement plating. Use of a surface-treated Al or Al alloy material according to any one of claims 1 to 7, wherein said materials are subjected to phosphate treatment, all of the Fe and Zn in the coating are converted into a chemical conversion coating composed of zinc phosphate and/or zinc iron phosphate, and then forming a paint coating thereon.

Inventors: AONO MASAMICHI, CHIKADA TOSHIHIRO, FUJIMOTO HIDEO, HAYASHI SOUICHI, HISAMOTO JUN, IKEDA KOUKI, MOCHIZUKI ASAO, SATO HIROSHI, TAKEI NAGISA, TAKEMOTO MASAO, TOYOSE KIKUO, TSURUNO AKIHIRO, UEDA TOSHIKI, AONO, MASAMICHI, CHIKADA, TOSHIHIRO, FUJIMOTO, HIDEO, HAYASHI, SOUICHI, HISAMOTO, JUN, IKEDA, KOUKI, MOCHIZUKI, ASAO, SATO, HIROSHI, TAKEI, NAGISA, TAKEMOTO, MASAO, TOYOSE, KIKUO, TSURUNO, AKIHIRO,, UEDA, TOSHIKI
Applicants: KOBE STEEL LTD, TOYOTA MOTOR CO LTD, KABUSHIKI KAISHA KOBE SEIKO SHO ALSO KNOWN AS KOBE STEEL LTD., TOYOTA JIDOSHA KABUSHIKI KAISHA
Application year: 1991
Main classification: C23C18
IPC codes: C23C22, C23C18