Thin film transistor and a method of manufacturing thereof

Abstract: A semiconductor device of a field effect transistor having an SOI structure is formed as below. Using a gate electrode 20 as a mask, n type impurities are implanted into an SOI layer (13) of p type to form additional source/drain regions (15, 16) of intermediate concentration. Then, a relatively thin sidewall spacer (25) is formed at the sidewall of the gate electrode (20). Using the sidewall spacer (25) as a mask, a titanium silicide layer (27) is formed in self-alignment on the surface of the SOI layer (13). Next, a relatively thick sidewall spacer (26) is formed. Using this sidewall spacer as a mask, n type impurities are implanted to form a source/drain region (17, 18) of high concentration. According to this manufacturing step, over-etching of the source/drain region (17, 18) are prevented in performing anisotropic etching at the time of sidewall spacer (25, 26) formation.

Description: The present invention relates to a method of manufacturing a semiconductor-on-insulator device and to a semiconductor-on-insulator device especially one having a relatively thin active region such as a MOS (Metal Oxide Semiconductor) type field effect transistor (referred to as SOI-MOSFET hereinafter). An SOI-MOSFET to which the present invention is mainly applied will be explained first taking a complementary type MOS (referred to as CMOS hereinafter) as an example of the background technology of the present invention. A CMOS having low consumption power and superior noise immunity is important in seeking high integration density and high speed operation. A sectional view of a conventional CMOS of not the SOI type but the so-called bulk type is shown in Fig. 1A. Referring to Fig. 1A, a CMOS has an n well region 2 formed in the proximity of the surface of a p type silicon substrate 1. A p channel type MOSFET 4 comprising a polycrystalline silicon gate 4 as the main element is formed on n well region 2. An n channel type MOSFET 6 comprising a polycrystalline silicon gate 5 as the main element is formed at the surface of p type silicon substrate 1 in the region other than n well region 2. A field oxide film 7 insulates and isolates n well region 2 from the other region. When such a bulk type CMOS is reduced in element size, parasitic thyristor is activated by noise from outside so that abnormal current flows from the power supply terminal to the ground terminal to stop the circuit operation (latch up phenomenon). This also induces problems such as soft error by α-particle. A sectional view of a CMOS having an SOI type structure is schematically shown in Fig. 1B. Referring to Fig. 1B, this SOI type CMOS has semiconductor layers 9 and 10 such as of silicon layers formed island-like by a field insulating film 7 on a silicon substrate 1 with an insulator layer 8 therebetween. Semiconductor layer 9 has an n type channel region and p type source/drain regions of p channel MOSFET 4 formed including polycrystalline silicon gate 3. Semiconductor layer 10 has a p type channel region and n type source/drain regions of n channel MOSFET 6 formed. Such a CMOS of the SOI structure has each element and also the substrate insulation-separated so that there is no current path leading to soft error and latch up. This is advantageous to reduction of element size. It is also advantageous to high speed operation since interconnection capacitance and junction capacitance are reduced by the lower insulating layer (refer to Ouyou Butsuri (Applied Physics) Vol. 54, No. 12 (1985) pp. 1274 - 1283, "SOI Technology"). A structure of a conventional SOI-MOSFET and a method of manufacturing thereof corresponding to the preambles of claims 6 and 1, respectively, will be explained hereinafter with reference to Figs. 2, and 3A - 3F. Referring to Fig. 2, a conventional SOI-MOSFET has an insulator layer 12 formed on a silicon substrate 11. A relatively thin silicon layer 13 of approximately 30-150nm(300-1500Å) is formed on insulator layer 12. Near the centre of silicon layer 13, a channel region 14 having a low p type impurity concentration (for example, 10¹⁶ - 10¹⁷/cm³) is formed.A lightly doped source region 15 and a lightly doped drain region 16 having an n type impurity concentration of the middle degree (for example, 10¹⁸/cm³) are formed adjacent to the sides of channel region 14. Lightly doped source region 15 and lightly doped drain region 16 have a source region 17 and a drain region 18 connected, respectively, each of a high n type impurity concentration (for example 10¹⁹ - 10²⁰/cm³). A gate electrode 20 is formed above channel region 14 with a dielectric thin film 19 therebetween. A sidewall spacer 21 is formed at the sidewalls of gate electrode 20. Silicon layer 13, gate electrode 20 and sidewall spacer 21 are covered with an interlayer insulating film 22. A contact hole 23 is provided in interlayer insulating film 22. An interconnection layer 24 is connected to gate electrode 20, source region 17 and drain region 18 through each contact hole 23. When positive voltage is applied to gate electrode 20 in the SOI-MOSFET of the above structure, carriers (electrons) of the n conductivity type are induced towards the upper layer of p type channel region 14, whereby that upper layer is inverted to an n conductivity type identical to the conductivity of source region 17 and drain region 18, or lightly doped source region 15 and lightly doped drain region 16. This allows current to flow between source region 17 and drain region 18. Because the concentration of the n type carriers induced at the upper layer of channel region 14 varies depending on the gate voltage, the current amount flowing across channel region 14 can be controlled by the gate voltage. This explains the operation of a MOSFET. Lightly doped drain region 16 has the so-called LDD (Lightly-Doped Drain) structure, serving to reduce the electric field in the proximity of the boundary between drain region 18 and gate electrode 20 to suppress generation of electron-hole pairs caused by impact ionization phenomenon. A thin film SOI-MOSFET having a relatively thin silicon layer 13, for example 50-150nm (500-1500Å) thickness, has the following characteristics in comparison with a conventional SOI-MOSFET having a relatively thick silicon layer of, approximately 500nm (5000Å). Since channel region 14 where current flows is very thin, the application of a gate voltage causes channel region 14 to become entirely depleted. This allows the depletion layer of channel region 14 to be controlled reliably by gate electrode 20 independent of the effect of the drain voltage. This reduces the effect of electric field from drain region 18 to channel region 14. As a result, the V D -I D characteristic degradation of Fig. 4A seen in conventional bulk type MOSFETs excluding the SOI type where current increases suddenly by a high drain voltage, i.e. the punch through phenomenon, is suppressed. It will therefore be possible to operate stably a transistor having a short gate length. A method of manufacturing a conventional SOI-MOSFET having the structure of Fig. 2 will be explained hereinafter with reference to Figs. 3A - 3F. First, oxygen ions are implanted into a silicon substrate 11 at an injection energy of 200KeV and a dosage of 2 x 10¹⁸/cm². Then, the substrate is subjected to heat treatment of approximately 1350°C. An insulating layer 12 is formed in silicon substrate 11 leaving a thin silicon layer 13 on the surface. Next, silicon layer 13 is processed in an island-like manner to form an active region (Fig. 3A). Impurities of p type are injected into silicon layer 13 to form a channel region 14. Next, a dielectric thin film 19 is formed by thermal oxidation of the surface of silicon layer 13. Then, a gate electrode 20 such as of polycrystalline silicon is formed. Ion implantation is carried out using gate electrode 20 as a mask. By implanting phosphorus which is an impurity of n type for example, lightly doped source region 15 and lightly doped drain region 16 are formed (Fig. 3B). By depositing a CVD insulating film 21a (Fig. 3C) and then carrying out reactive ion etching, a sidewall spacer 21 is formed at the sidewall of gate electrode 20. Some over-etching is necessary in providing sidewall spacer 21. This is to take into consideration unevenness in the thickness of CVD oxide film 21a which is deposited to approximately 300nm (3000Å) to leave only sidewall spacer 21 while removing the remainder by etching. This over-etching is responsible for some removal of silicon layer 13 to generate a step as shown in Fig.3D by arrow A. Specifically, when the application of reactive ion etching to CVD oxide film 21a of, for example, approximately 300nm (3000Å) in average is carried out with over-etching of approximately 20% on account of variation in thickness and etching characteristic of CVD oxide film 21a. That is to say, 300nm (3000Å) of CVD oxide film 21a is first etched, followed by etching of a time period where 60nm (600Å) of CVD oxide film 21a is over-etched. Silicon layer 13 will be over-etched if the thickness of the CVD insulating film deposited thereabove is exactly 300nm (3000Å). A silicon oxide film is generally used for a CVD insulating film, where the selectivity of reactive ion etching to silicon is approximately 5 : 1. This means that silicon of approximately 12nm (120Å) is etched during the time period where over-etching of 60nm (600Å) is carried out for a silicon oxide film. Following the formation of sidewall spacer 21, arsenic ions of 10¹⁹ - 10 ²⁰/cm³ are injected using sidewall spacer 21 as a mask to form source region 17 and drain region 18 of high concentration, as shown in Fig. 3D. Then, an interlayer insulating film 22 is deposited by CVD, followed by formation of a contact hole 23 in a predetermined position in interlayer insulating layer 22. Some over-etching occurs in forming contact hole 23 to result in a depression indicated by arrow B in Fig. 3E. The formation of an interconnection layer 24 completes the manufacture of a thin film SOI-MOSFET of Fig. 3F. Because a conventional SOI-MOSFET is manufactured having a structure as described above, over-etching occurs in forming sidewall spacer 21 and contact hole 23, resulting in a silicon layer 13 having a thin portion as shown in arrow A of Fig. 3D and arrow B of Fig. 3E. The resistance of this portion is increased and thus degrades the transistor characteristics. The value of drain current I D with respect to a predetermined drain voltage V D is decreased as shown in Fig. 4B. There was-also a problem that the transistor does not operate due to the fact that there is some portion where silicon layer 13 is completely removed to cut off source region 17 or drain region 18. The present invention is intended to provide a semiconductor device improved in transistor characteristics by suppressing decrease of film thickness in the semiconductor layer caused by over-etching, and a method of manufacture thereof. The method of manufacturing a semiconductor-on-insulator device in accordance with the present invention is defined in claim 1 of the claims appended. The semiconductor-on-insulator device of the present invention has a "lightly doped drain" LDD structure. The term "lightly doped" as it applies to source/drain regions in this description and in the appended claims, is to be understood in this specific context. The first sidewall spacers may be formed with a relatively thin thickness, e.g. in which the maximum width is approximately 100 nm (1000Å). Therefore, over-etching of the source/drain regions is suppressed to a very low degree in anisotropic etching of forming the first sidewall spacers. The formation of an etch-resistant metal layer on the source/drain regions prevents over-etching of the source/drain regions in anisotropic etching in forming the second sidewall spacer. The semiconductor-on-insulator device in accordance with the present invention is defined in claim 6 of the claims appended. It is acknowledged that JP-A-62032653 describes a semiconductor silicon on insulator device having insulating film sidewall spacers each side of an insulated gate electrode and a silicide metallic layer formed at each side of the sidewall spacers each defining a source and drain region on the surface of a crystallised silicon layer. The purpose of the silicide metallic layer is to reduce source/drain contact resistance. Also, JP-A-63012168 describes a semiconductor device having silicide layers to reduce source/drain contact resistance. The device is of bulk semiconductor LDD structure and has thermally grown oxide insulation thin film sidewall spacers each side of an insulated gate. Additional spacers are provided each side of the thermally grown oxide insulation thin film spacers and are used as masks during production of self-aligned source/drain ion implants. In the accompanying drawings: Fig. 1A is a sectional view of a conventional bulk type CMOS; Fig. 1B is a sectional view of a conventional SOI-CMOS; Fig. 2 is a sectional view of a conventional thin SOI-MOSFET; Figs. 3A-3F are sectional views of a conventional SOI-MOSFET showing the manufacturing steps thereof; Fig. 4A is a graph showing the V D -I D characteristic degraded by the so-called punch through phenomenon in a conventional bulk type MOSFET; Fig. 4B is a graph of the transistor characteristic where resistance is increased due to a thin silicon layer in source/drain regions in a conventional SOI-MOSFET; Fig. 5 is a sectional view of a SOI-MOSFET according to an embodiment of the present invention; Figs. 6A-6H are sectional views of the SOI-MOSFET of the embodiment showing the manufacturing steps thereof; Fig. 7 is a sectional view of a structure where a titanium silicide layer is formed on the surface of the source/drain regions of a bulk type MOSFET according to conventional technology associated with the present invention. Fig. 8 is a sectional view of a CMOS having the SOI structure in which the present invention is applied to; and Fig. 9 is a graph of the V D -I D characteristic of a thin SOI-MOSFET according to the embodiments of the present invention. A preferred embodiment of the present invention will be explained hereinafter with reference to the drawings. The following description is given by way of example only. Fig. 5 shows a sectional view of a thin film SOI-MOSFET of the present embodiment. Referring to Fig. 5, this thin film SOI-MOSFET has an insulator layer 12 formed on a silicon substrate 11. A thin silicon layer 13 of approximately 30-150 nm (300-1500Å) in thickness is formed as a semiconductor layer-on-insulator layer 12. Silicon layer 13 has a channel region 14 of low p type impurity concentration (for example 10¹⁶ - 10¹⁷/cm³) formed in the proximity of the centre thereof. An additional source region 15 and an additional drain region 16 each having a n type impurity concentration of an intermediate level (for example 10¹⁸/cm³) are formed adjacent to the left and right sides of channel region 14. Additional source region 15 and additional drain region 16 have a source region 17 and a drain region 18, respectively, of high n type impurity concentration (for example 10¹⁹ - 10²¹/cm³) formed adjacent to the sides of channel region 14. A gate electrode 20 is formed above channel region 14 with a dielectric thin film therebetween. The above structure is similar to the aforementioned conventional embodiment of Fig. 2. The present embodiment shows a first sidewall spacer 25 of relatively thin thickness where the maximum width is approximately 100nm (1000Å) at the sidewall of gate electrode 20. A metal layer 27 formed of a thin titanium silicide layer of approximately 50nm (500Å) in thickness, for example, is formed on the surface of silicon layer 13 which is not covered with gate electrode 20 or first sidewall spacer 25, and on gate electrode 20. A second sidewall spacer 26 having a maximum thickness of approximately 300nm (3000Å) is formed at the outer surface of first sidewall spacer 25. An additional source.region 15 or an additional drain region 16 is provided in silicon layer 13 beneath first sidewall spacer 25. A depression or reduction in film thickness due to over-etching is not seen in second sidewall spacer 26 and in silicon layer 13 at the bottom of contact hole 23. Because metal layer 27 of low resistance is provided on silicon layer 13 in the structure, it is possible to reduce resistance of source region 17 and drain region 18. The manufacturing steps of the SOI-MOSFET of the embodiment in Fig. 5 will be explained with reference to Figs. 6A - 6H. According to the method of manufacturing an SOI-MOSFET of the present embodiment, oxygen ions are implanted into silicon substrate 11 at an injection energy of 200KeV and a dosage of 2 x 10¹⁸/cm², followed by a heating process of approximately 1350°C. This forms an insulator layer 12 in silicon substrate 11, leaving a thin silicon layer 13 on the surface thereof. Then, silicon layer 13 is processed in an island-like manner to form an active region (Fig. 6A). A channel region 14 is formed introducing impurities of p type into silicon layer 13. The surface of silicon layer 13 is thermal-oxidized to form a dielectric thin film 19. Then, a gate electrode 20 of polycrystalline silicon is formed (Fig. 6B). Using gate electrode 20 as a mask, n type impurities such as phosphorus ions are implanted at an injection energy of 80KeV and a dosage of 1 x 10¹³/cm² to form a lightly doped source region 15 and a lightly doped drain region 16 of a concentration of approximately 10¹⁸/cm³ (Fig. 6C). The above described manufacturing steps are similar to those of the aforementioned conventional example. In the present embodiment, a CVD oxide film 25a is formed (Fig. 6D), followed by formation of a first sidewall spacer 25 by reactive ion etching (Fig. 6E). If the film thickness of CVD oxide film 25a is approximately set to 100 nm (1000Å) for example, reduction in thickness of silicon layer 13 due to over-etching is very low. This is because the over-etching amount of CVD oxide film 25a is set to be approximately 20 nm (200Å) which is 20% of 100 nm (1000Å) and the etching selectivity of silicon is approximately 1/5 of CVD oxide film 25a, so that the over-etching amount of silicon layer 13 is approximately 4 nm (40Å). A metallic layer 27 of titanium silicide, for example, is formed on silicon layer 13 or on gate electrode 20 by a self-aligning method described hereinafter (Fig. 6F). In forming a titanium silicide layer for metallic layer 27, titanium is deposited all over the surface to a thickness in a range from several tens to one hundred nm (10's nm - 100 nm) (several hundreds to a thousand Å (several 100'sÅ - 1000Å)), followed by heat process to silicide the exposing portion of silicon or polycrystalline silicon, resulting in formation of a titanium silicide layer. Titanium on insulator layer 12 or on the surface of sidewall spacer 25 is left unreacted, or is nitrided to be changed to titanium nitride. By removing the unreacted titanium or titanium nitride with sulfuric acid, metal layer 27 of titanium silicide layer is selectively formed on silicon layer 13 or gate electrode 20. Next, a CVD oxide film of approximately 300 nm (3000Å) thickness is deposited all over the surface to be subjected to anisotropic etching for forming a second sidewall spacer 26. Using sidewall spacer 26 as a mask, n type impurities such as phosphorus ions and arsenic ions are doped to form a source region 17 and a drain region 18 (Fig. 6G). In forming second sidewall spacer 26, over-etching of silicon layer 13 is prevented since metal layer 27 covers silicon layer 13. This is because the etching selectivity of metal layer 27 with respect to the CVD insulating film forming sidewall spacer 26 is decreased to approximately 1/20. The formation of interconnection layer 24 results in the sectional view of Fig. 6H. Interconnection layer 24 is electrically connected to source region 17 and drain region 18 via metal layer 27 in contact hole 23. Although titanium silicide is described as the material of metallic layer 27 in the present embodiment, similar effects can be obtained using other materials such as cobalt silicide or selective tungsten layer as long as the metallic layer has conductivity and etching resistance, and is capable of being formed in self-alignment. Selective tungsten layer takes advantage of the fact that the core of tungsten is easily generated on silicon by the following reaction equation. WF₆ + Si → W + SiF₆ ↑ Although a monocrystalline silicon layer is used as the semiconductor layer in the present embodiment, similar effects can be obtained using a semiconductor layer of polycrystalline silicon or gallium arsenide. Although the present embodiment is described in which an n channel MOSFET is employed, a p channel MOSFET may be used. Identical effects can be obtained with only the conductivity type reversed. As a conventional technology associated with the above described embodiment, a structure where a titanium silicide film is formed on the surface of the source/drain regions of a bulk type MOSFET of Fig. 7 is disclosed in Japanese Patent Laying-Open No. 61-270870. Referring to Fig. 7, the structure disclosed in the aforementioned publication has a gate electrode 103 formed above silicon substrate 101 with an insulating film 102 therebetween. At the left and right sides of gate electrode 103, sidewall spacers 105a and 105b of an insulating film are formed which insulates gate electrode 103 from impurity diffusion layers 104a and 104b which become the source/drain regions. A titanium silicide film 106a is formed on impurity diffusion layer 104a. A titanium silicide film 106c is formed on gate electrode 103. A titanium silicide film 106b is formed on impurity diffusion layer 104b. An oxide titanium film 107a is formed on titanium silicide film 106a, sidewall spacer 105a, and titanium silicide film 106c. An oxide titanium film 107c is formed on titanium silicide film 106b, sidewall spacer 105b, and titanium silicide film 106c. An oxide titanium film 107b is formed on titanium silicide film 106b and on a relatively thick insulating film 108. According to this structure, titanium silicide layers 106a and 106b contribute to reduction in sheet resistance of impurity diffusion layers 104a and 104b. However, impurity diffusion layers 104a and 104b will be over-etched by the anisotropic etching step in forming sidewall spacers 105a and 105b because sidewall spacers 105a and 105b of Fig. 7 are of a single layer structure relatively great in thickness. The application of such a structure in a semiconductor device having an active region of a thin semiconductor layer, such as a thin type SOI-MOSFET, cannot have the problem solved of increase in resistance of the source/drain regions due to over-etching. An embodiment where the present invention is applied to a CMOS having an SOI structure will be explained hereinafter. Fig. 8 shows a sectional view of an SOI type CMOS where the present invention is applied to the conventional structure of Fig. 1A. Referring to Fig. 8, silicon layers 113a and 113b as the semiconductor layer are formed in an island-like manner on a silicon substrate 111 with an insulator layer 112 therebetween. An n channel MOS 101 is formed at silicon layer 113a. A p channel MOS 102 is formed at silicon layer 113b. Specifically, a p channel region 114a is formed in the middle of silicon layer 113a. An n type lightly doped source region 115a and a lightly doped drain region 116a are formed adjacent to the left and right sides of channel region 114a. A source region 117a and a drain region 118a are formed adjacent to the lightly doped source region 115a and the lightly doped drain region 116a, respectively. A gate electrode 120 is formed above channel region 114a with a dielectric thin film 119 therebetween. A first sidewall spacer 125 and a second sidewall spacer 126 forming a double layered structure are formed at the left and right sides of gate electrode 120. A metallic 127 such as of titanium silicide layer is formed on the surface of silicon layer 113a at the region outside first sidewall spacer 125 and on the surface of gate electrode 120. Silicon layer 113b isolated from silicon layer 113a by a field insulating film 103 has a channel region 114b of the n type formed in the middle thereof. An additional source region 115b and an additional drain region 116b of the p type are formed adjacent to the left and right sides of channel region 114b. A high concentration p type source region 117b and a drain region 118b are formed on the further outer left and right sides of additional source and drain regions of 115b and 116b, respectively. The structures of gate electrode 120 and first sidewall spacer 125, and second sidewall spacer 126 and metallic layer 127 are similar to those of the above described n channel MOS 101. According to an SOI type CMOS having the above described structure is free of soft error and latch up phenomenon. Also, resistance of the source/drain regions are held low to improve the current characteristic of the transistor. The V D - I D characteristic of the SOI-MOSFET obtained by the above described embodiment is superior as shown in the graph of Fig. 9.

Claims: A method of manufacturing a semiconductor-on-insulator device comprising the steps of: (a) forming a semiconductor layer (13; 113a; 113b) of a first conductivity type on an insulator layer (12; 112); (b) forming a dielectric thin film (19; 119) on said semiconductor layer (13; 113a; 113b); (c) forming a gate electrode (20; 120) on said dielectric thin film (19; 119); (d) forming lightly doped source/drain regions (15; 16; 115a; 116a; 115b; 116b) by implanting dopant impurities of a second conductivity type into said semiconductor layer (13; 113a; 113b) using said gate electrode (12; 112) as a mask, and (e) forming source/drain regions (17; 18; 117a; 118a; 117b; 118b) adjacent to said lightly doped source/drain regions (15; 16; 115a; 116a; 115b; 116b), said source/drain regions (17;18; 117a; 118a; 117b; 118b) having a dopant impurity concentration higher than that of said lightly doped source/drain regions (15; 16; 115a; 116a; 115b; 116b), by implanting dopant impurities of said second conductivity type into said semiconductor layer (13; 113a; 113b) using said gate electrode (20; 120) and sidewall spacers (25; 125; 26; 126) each side of said gate electrode (20; 120) as a mask; which method is characterised by the following steps which are performed following step (d) and preceding step (e); (f) depositing, by chemical vapour deposition, a thin film of insulator material on the exposed surfaces of said gate electrode (20; 120) and said dielectric thin film (19; 119); (g) etching said thin film of insulator material and dielectric thin film to expose the surface of said gate electrode (12; 112) and the surface of said semiconductor layer (13; 113a; 113b) and to delineate a first sidewall spacer (25; 125) of said sidewall spacers adjacent to each side of said gate electrode (12; 112); (h) forming a metallic layer (27; 127) on said gate electrode (12; 112) and surface of said semiconductor layer (13; 113a; 113b) to the exclusion of the surface of each first sidewall spacer (25; 125); (i) depositing, by chemical vapour deposition, a film of insulator material on the exposed surfaces of said metallic layer (27; 127) and each first sidewall spacer (25; 125); and (j) etching said film of insulator material, using an etchant against which said metallic layer (27; 127) is resistant, to delineate a second sidewall spacer (26; 126) of said sidewall spacers adjacent to each first sidewall spacer (25; 125). A method as claimed in claim 1, wherein said step (a) of forming a semiconductor layer (13, 113a, 113b) of the first conductivity type on said insulator layer (12, 112) comprises the steps of implanting oxygen ions into a silicon substrate (11, 111) at a predetermined injection energy and a predetermined dosage, followed by a heating process, leaving a silicon layer (13, 113a, 113b) of a predetermined depth from the surface of said silicon substrate (11, 111) to form an insulator layer (12, 112) of SiO₂ within said silicon substrate (11, 111); and implanting dopant impurities of the first conductivity type into said silicon layer (13; 113a; 113b) on said insulator layer (12; 112). A method as claimed in claim 1 or 2 wherein said semiconductor layer (13;113a;113b) and gate electrode (20;120) are of silicon and said step (g) of forming said metallic layer (27;127) comprises: depositing titanium metal on the surfaces of said gate electrode (12;112), each first sidewall spacer (25;125) and semiconductor layer (13;113a;113b); heating and forming a titanium silicide metallic layer (27;127) where said titanium metal contacts the surfaces of said gate electrode (20;120) and semiconductor layer (13;113a;113b); and removing unreacted titanium metal. A method as claimed in any preceding claim wherein: said steps (f) and (g) comprise depositing a CVD oxide film (25a) to a thickness of 100 nm (1000Å), and applying reactive ion etching to said CVD oxide film (25a); and said steps (i) and (j) comprise depositing a CVD oxide film of a thickness of 300 nm (3000Å), and applying reactive ion etching to said CVD oxide film. A method as claimed in claim 1, wherein said step (h) of forming said metallic layer (27, 127) comprises forming a WF₆ film, followed by reaction of the same with a layer including silicon to generate a core of tungsten for forming a selected tungsten layer. A semiconductor-on-insulator device comprising: a semiconductor layer (13; 113a; 113b) formed on an insulator layer (12; 112); a channel region of a first conductivity type (14; 114a; 114b) formed in said semiconductor layer (13; 113a; 113b); lightly doped source/drain regions (15, 16; 115a, 116a; 115b, 116b) of a second conductivity type formed in said semiconductor layer (13; 113a; 113b) adjacent to the left and right sides of said channel region (14, 114a, 114b); source/drain regions (17, 18; 117a, 118a; 117b, 118b) outside said channel region adjacent to, and having a concentration higher than that of, said lightly doped source/drain regions (15, 16; 115a, 116a; 115b, 116b), in said semiconductor layer (13; 113a; 113b); and a gate electrode (20, 120) formed above said channel region (14,114a, 114b) with a dielectric thin film (19, 119) therebetween; which semiconductor-on-insulator device is characterised by: first sidewall spacers (25, 125) of CVD-insulation thin film provided respectively on the left and on the right sidewalls of said gate electrode (20; 120); second sidewall spacers (26; 126) of CVD-insulation film covering respectively the outer surface of each of said first sidewall spacers (25, 125), said source/drain regions (17,18; 118a,118a; 117b,118b) lying outside the region where said second sidewall spacers are formed; and a metallic layer (27; 127) at the surface of said semiconductor layer (13; 113a; 113b) in a region outside the region where said first sidewall spacers (25; 125) are formed. A semiconductor-on-insulator device as claimed in claim 6, wherein said semiconductor layer (13; 113a; 113b) comprises a silicon layer of 30-150 nm (300-1500Å) thickness. A semiconductor-on-insulator device as claimed in claim 6, wherein said metallic layer (27; 127) comprises a titanium silicide layer. A semiconductor-on-insulator device as claimed in claim 6, wherein said channel region (14; 114a; 114b) has a p type dopant impurity concentration of 10¹⁶-10¹⁷/cm³; said lightly doped source/drain regions (15, 16, 115a, 115b, 116a, 116b) have an n type dopant impurity concentration of approximately 10¹⁸/cm³; and said source/drain regions (17, 18; 117a, 118a; 117b, 118b) have an n type dopant impurity concentration of 10¹⁹ - 10²¹/cm³. A semiconductor-on-insulator device as claimed in claim 6, wherein said first sidewall spacers (25; 125) have a maximum thickness of 100 nm (1000Å); and said second sidewall spacers (26; 126) have a maximum thickness of 300 nm (3000Å). A semiconductor-on-insulator device as claimed in claim 8, wherein said metallic layer (27; 127) comprises a titanium silicide layer of 50 nm (500Å) thickness. A semiconductor-on-insulator device of complementary type comprising adjacent first and second semiconductor-on-insulator devices (101,102) each as claimed in any one and the same of the preceding claims 6 to 11 and in which the first and second conductivity types of said first semiconductor-on-insulator device (101) are p-type and n-type respectively, and the first and second conductivity types of said second semiconductor-on-insulator device (102) are n-type and p-type respectively.

Inventors: AJIKA NATSUO C O MITSUBISHI DE, YAMAGUCHI YASUO C O MITSUBISHI, YAMANO TSUYOSHI C O MITSUBISHI, AJIKA, NATSUO, C/O MITSUBISHI DENKI K.K., YAMAGUCHI, YASUO, C/O MITSUBISHI DENKI K.K., YAMANO, TSUYOSHI, C/O MITSUBISHI DENKI K.K.
Applicants: MITSUBISHI ELECTRIC CORP, MITSUBISHI DENKI KABUSHIKI KAISHA
Application year: 1991
Main classification: H01L29
IPC codes: H01L29, H01L27, H01L21