SURFACE TREATMENT OF THERMOPLASTIC RESIN MOLDING

Abstract: A method of improving the surface characteristics of a molded article made from a composition comprising a thermoplastic resin and a functionalized polyolefin resin containing at least one member, selected from among a monomer containing a carboxyl, carboxylic ester, or acid anhydride group, an epoxidized monomer, a hydroxylated monomer, an aminated monomer, an alkenyl cyclic imino ether derivative and a poly-functional monomer, said composition optionally containing an inorganic filler or a rubbery substance, without detriment to the excellent properties thereof, such as rigidity, impact resistance, heat resistance, dimensional stability and processability, said method comprising applying an ultraviolet radiation with a wavelength of 300 nm or less thereto.

Description: [Industrial Utilization Field] The present invention relates to a surface treating and coating method for a molded article comprising a thermoplastic resin composition. More particularly, the present invention is concerned with a surface treating and coating method for a molded article comprising a thermoplastic resin composition well-balanced in rigidity, impact resistance, heat resistance dimensional stability and moldability, which composition comprises a thermoplastic resin and a functionalized polyolefin resin containing at least one member selected from the group consisting of carboxylic acid group-, carboxylic ester group- or acid anhydride group-containing monomers, epoxy group-containing monomers, hydroxyl group-containing monomers, amino group-containing monomers, alkenyl cyclic iminoether derivatives, and polyfunctional monomers, or a composition comprising the said composition and an inorganic filler or a rubbery substance incorporated therein. [Prior Art] Heretofore, thermoplastic resins such as polyolefin resins, e.g. polyethylene and polypropylene, and polyester resins, have been used in various fields, including automobile parts, household electric products and electronic devices. In order to enhance the added value of these products there has been conducted surface coating, printing or plating, or lamination thereto of base materials such as woven and non-woven fabrics, foam, and leather, or implantation of feathers therein. However, since polyolefin and polyester resins do not have a polar group, it is difficult to apply coating, bonding or printing thereto. Generally, for the purpose of improving the coatability, etc. of the aforementioned products, there are conducted surface treatments such as physical treatments, e.g. sandblasting, flame treating, corona discharge, and treatment using plasma, or chemical treatments, e.g. treatment using chromic acid mixture or solvent. However, such conventional physical treating methods involve the following problems: 1 ○ the effect obtained is unsatisfactory, 2 ○ the treating speed is low and treating time is long, 3 ○ the apparatus is large-scaled and the process is complicated, and 4 ○ the method is not economical. The foregoing chemical methods also involves problems; for example, 1 ○ environmental pollution, and 2 ○ a considerable burden required for the disposal of liquid wastes used such as chemicals and solvents. Both such conventional methods involve the problem that the coatability, printability and adhesive property in the use of coating materials, inks, and adhesives and base materials are still unsatisfactory. EP-A-430545 discloses a method for surface treating a molded article produced from a resin composition comprising 100 parts by weight of a resin composition comprising (A) 5 to 99.5 % of polypropylene and/or modified polypropylene, and (B) 0.5 to 95% of at least one thermoplastic resin selected from a polyamide resin, a polyphenylene ether resin, a mixture of a polyphenylene ether resin and a styrene resin, a graft copolymer of a polyphenylene ether resin and styrene and a saturated polyester resin and a compatibilizer. The molding is irradiated with ultraviolet light having a wavelength in the region of 300 nm or less. JP-A-60-166 332 discloses a Surface treatment, which comprises irradiating UV ray from a low-pressure mercury lamp having a peak at wavelengths of 1849 and 2537 Angstroms onto the surface of a moulding formed of propylene polymer compsn. composed of (A) 100 pts. wt. of crystalline propylene polymer having a melt flow index of 0.01-100 g/10 min. and (B) 3.0-28.0 pts. wt. of EVA copolymer contg. 5.0-50 wt.% of vinylacetate, ethylene-acrylate copolymer contg. 5.0-40 wt.% of acrylate and/or ethylene-methacrylate copolymer contg. 5.0-40 wt.% of methacrylate. Pref. the propylene polymer includes a monopolymer of propylene and a random or block copolymer of propylene and ethylene and/or 4-12C alpha-olefin. The melt index of the EVA copolymer, ethylene-acrylate copolymer and ethylene-methacrylate copolymer is normally 0.05-100 g/10 min. Strength of the ultra vilet ray is pref. 0.1-100 mW/cm2. Irradiation time is normally 0.6-50 min. ADVANTAGE - Adhesive, printing and coating properties may be improved with no use of primer, and impact resistance is improved without redn. in fluidity and rigidity of the propylene -polymer. [Subject to be Attained by the Invention] In view of the above-mentioned points the present invention aims at providing a surface treating and/or coating method for molded articles extremely superior in coatability, printability and adhesive proeprty. [Means for Attaining the Subject]. Having made extensive studies for achieving the above-mentioned object, the present inventors found out that surface characteristics of molded articles could be improved without deterioration in rigidity, impact resistance, heat resistance, dimensional stability and modability. In this way we accomplished the present invention. More specifically, in a first aspect of the present invention there is provided a surface treating method for a thermoplastic resin molded article, characterized by radiating an ultraviolet light at least 85% of the energy of which has a wavelength shorter than 254 nm and the main operating wavelength near 185 nm, to the molded article, said molded article being formed from a composition containing: (A) 50-95% by weight of a thermoplastic resin, said thermoplastic resin not being a polyethylene resin functionalized by at least one of B1 to B6. (B) 5-50 wt% of a polyethylene resin functionalized by at least one member selected from B1: carboxylic ester group- or acid anhydride group-containing monomers, B2: epoxy group-containing monomers, B3: hydroxyl group-containing monomers, B4: amino group-containing monomers, B5: alkenyl cyclic iminoether derivatives and B6: polyfunctional methacrylate monomers, polyfunctional vinyl monomers, bismaleimides or dioximes, wherein when the polyethylene resin is functionalized by B1 or B6 the functionalisation is carried by graft-modification. The surface treating method preferably further contains: (C) 5-150 parts by weight of an inorganic filler and/or (D) 3-50 parts by weight of a rubbery system, based on 100 parts by weight of the resins (A) and (B). As examples of the thermoplastic resin (A) used in the present invention there are mentioned polyolefin resins such as α-olefin (co)polymers having 2 to 10 carbon atoms, e.g. high and medium density polyethylenes, low density polyethylenes, linear low density polyethylenes, very low density polyethylenes, polypropylenes, poly-1-butene, and poly-4-methyl-1-pentene, and interpolymers of α-olefins, e.g. ethylene, propylene, butene-1, hexene-1 and 4-methyl-1-pentene; polystyrene resins such as polystyrenes, styrene/ acrylonitrile copolymers, styrene/methyl methacrylate/ acrylonitrile copolymer, α-methylstyrene/styrene/acrylonitrile copolymer, ABS, MBS, AES, and AAS; polyacrylonitrile resins, polyvinyl chloride resins, polyvinylidene chloride resins, polymethacrylate resins, polyacetal resins, polyamide resins, polycarbonate resins, polyphenylene ether resins, polyester resins, polysulfone resins, polyether sulfone resins, polyphenylene sulfide resins, polyether ether ketones, polyacrylate resins, polyamide-imide resins, polyimide resins, and fluorine resins. These may be used each alone or as mixtures. As examples of component (B) used in the present invention, i.e., a polyethylene resin containing at least one member selected from B1: carboxylic ester group- or acid anhydride group-containing monomers, B2: epoxy group-containing monomers, B3: hydroxyl groupcontaining monomers, B4: amino group-containing monomers, B5: alkenyl cyclic iminoether derivatives and B6: polyfunctional monomers, they are graft-modified resins obtained by grafting at least one of the above monomers to polyethylene resins. The term "monomer" as referred to herein means a polymerizable monomer having a polymerizable carbon-carbon double bond. As examples of component (B)-B1: carboxylic ester group- or acid anhydride group-containing monomers, there are mentioned esters and anhydrides of α, β-unsaturated dicarboxylic acids such as maleic, fumaric, citraconic and itaconic acids, and of unsaturated monocarboxylic acids such as acrylic, methacrylic, crotonic, vinylacetic and pentenoic acids. As examples of component (B)-B1: epoxy group-containing monomers, there are mentioned glycidyl (meth) acrylate, acryl glycidyl ether, and vinyl glycidyl ether. As examples of component (B)-B3: hydroxyl group-containing monomers, there are mentioned 1-hydroxypropyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, and hydroxypropyl (meth)acrylate. As examples of component (B)-B4: amino group-containing monomers, there are mentioned dimethylaminoethyl (meth)acrylate, diethylaminoethyl (meth)acrylate and dibutylaminoethyl (meth)acrylate. The alkenyl cyclic iminoether derivatives referred to above as (B)-B5 are those represented by the following structural formula: wherein n is 1, 2, or 3, preferably 2 or 3, more preferably 2; R 1 , R 2 , R 3 and R each represent an alkyl group having 1 to 12 carbon atoms and/or hydrogen. The alkyl group may contain an inert substituent group. The term "inert" as used herein means that no bad influence is exerted on the graft reaction and the function of the resulting product. It is not necessary for all of Rs to be the same. Preferable R 1 = R 2 = H, R 3 = H or Me, and R = H, that is, 2-vinyl and/or 2-isopropenyl-2-oxazoline and 2-vinyl and/or 2-isopropenyl-5,6-dihydro-4H-1,3-oxazine. These may be used each alone or as a mixture, with 2-vinyl and/or 2-isopropenyl-2-oxazoline being particularly preferred. Component (B)-B6 is selected from: polyfunctional methacarylate monomers typified by trimethylolpropane trimethacrylate, ethylene glycol dimethacrylate, and diethylene glycol dimethacrylate; polyfunctional vinyl monomers typified by divinylbenzene, triallylisocyanurate, diallyl phthalate and vinyl butyrate; bismaleimides typified by N,N'-m-phenylene bismaleimide and N,N'-ethylene bismaleimide; and dioximes such as p-quinone dioxime. In the case of grafting at least one of the above monomers to the polyolefin resin, it is desirable that this graft-modification be carried out in the presence of a crosslinking agent. As the said crosslinking agent there may be used at least one member selected from organic peroxides such as hydroperoxides, dialkylperoxides, peroxyesters, and ketone peroxides, dihydroaromatic compounds, and vulcanizing agents such as sulfur. The dihydroaromatic compounds just referred to above indicate compounds containing one or more aromatic rings at least one of which is dihydrogenated. The aromatic ring as referred to herein indicates a ring structure wherein the number of π-electrons is 4n + 2 (n is an integer), the π-electrons being shown in the definition of aromaticity [see, for example, "Yuki Kagaku-no Kiso," translated by Toshio Goto, Tokyo kagaku Donin (1976), pp.105-106, (Richard S. Monson & John C. Shelton, "Fundamentals of Organic Chemistry," MacGraw-Hill, Inc. (1974)]. Examples include pyridine and quinoline. Therefore, dihydroderivatives of quinoline are also included as examples of dihydroaromatic compounds empolyable in the invention. Further, the dihydroaromatic compounds employable in the invention may contain substituent groups. There may be used derivatives substituted with alkyl groups, various elements or functional groups. Such dihydroaromatic compounds can be prepared by the application of known chemical reactions. Examples of those available at present include 1,2-dihydrobenzene, cis-1,2-dihydrocatechol, 1,2-dihydronaphthalene, 9,10-dihydrophenanthrene, as well as 1,2-dihydroquinoline compounds such as 6-decyl-2,2,4-trimethyl-1,2-dihydroquinoline, 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline, and 2,2,4-trimethyl-1,2-dihydroquinoline. Polymers of these compounds are also employable. It is presumed that the dihydroaromatic compounds act on the carbon-hydrogen bond of the thermoplastic resin to form carbon radical and per se exhibit a resonant structure after release of the radical and are stabilized. As compared with oxygen radical formed by the cleavage of the foregoing organic peroxides, the carbon radical just referred to above is weak in the hydrogen withdrawing ability from the carbon-hydrogen bond, so does not exhibit an extreme degradation reaction even for a peroxide decomposing type thermoplastic resin such as polypropylene, nor does it exhibit an extreme crosslinking reaction even for a peroxide crosslinking type thermoplastic resin such as polyethylene. Therefore, the control of reaction is easy and it is possible to effect a fine crosslinking which has been considered difficult in the use of an organic peroxide. The crosslinking agent may be used directly as it is, but particularly in the case of a dihydroaromatic compound there may be adopted a method wherein the compound is prepared by a reaction during melt-kneading. The reaction may be selected optionally, but it is preferable that the reaction start from a compound which reacts easily on heating, in order to avoid the addition of the catalyst, etc. Particularly, Diels-Alder reaction is preferred. In this case, however, it is desirable that the compound used be in the form of a dihydroaromatic compound. The mixing ratio of the thermoplastic resin as component (A) to the functional group-containing polyolefin resin as component (B) is (A)/(B) = 50∼95/5∼50 wt%. If the proportion of component (B) is less than 5 wt%, both adhesive property and coatability may be deteriorated, and a proportion thereof exceeding 50 wt% may cause deterioration of the mechanical strength. As the inorganic filler (C) in the invention there may be used any of known ones such as powdered, plate-like, flaky, needle-like, spherical, hollow, and fibrous ones. Concrete examples include powdered fillers such as calcium carbonate, magnesium carbonate, calcium sulfate, siliceous sand calcium, clay, diatomaceous earth, talc, alumina, glass powder, iron oxide, metal powder, graphite, silicon carbide, silicon nitride, silica, boron nitride, aluminum nitride, and carbon black; metallic foils such as mica, glass plate, sericite, pyrophyllite, and alum flake; plate- or flake-like fillers such as graphite; hollow fillers such as Shirasu balloon, metal balloon and pumice; and mineral fibers such as glass fiber, carbon fiber graphite fiber whisker, metallic fiber, silicon carbide fiber, asbestos, and sollastonite. These fillers may be used each alone or as mixtures. The kind and amount of the filler to be used may be determined according to purposes. For improving their dispersibility, the surfaces thereof may be treated with, for example, a silane coupling agent, an organotitanate-based coupling agent, or a metallic salt of a fatty acid. The amount of the inorganic filler (C) to be used is in the range of 5 to 150, preferably 10 to 130, more preferably to 120, parts by weight based on 100 parts by weight of the resin components (A) + (B). If the amount of the inorganic filler is smaller than 5 parts by weight, the effect of the addition thereof will not be satisfactory, and if it exceeds 150 parts by weight, the mechanical strength, particularly the impact strength at low temperatures, will be deteriorated markedly. As examples of the rubbery substance (D) used in the present invention there are mentioned ethylene-propylene random copolymer rubber, ethylene-propylene-diene random copolymer rubber, 1,2-polybutadiene, styrene-butadienestyrene block copolymer rubber, styrene-isoprene-styrene block copolymer rubber, natural rubber, nitrile rubber, and isobutylene rubber. These may be used each alone or as mixtures. Particularly, ethylene-propylene random copolymer rubber and ethylene-propylene-diene random copolymer rubber are preferred. As to the diene component in the ethylene-propylene-diene random copolymer rubber, any of conventional ones may be used, including ethylidene norbornene, 1,4-hexadiene and cyclopentadiene. The amount of the rubbery substance (D) to be used is in the range of 3 to 50 parts by weight based on 100 parts by weight of the resin components (A) + (B). If the amount of the rubbery substance is smaller than 3 parts by weight, it will be impossible to exhibit the effect of its addition, and an amount thereof exceeding 50 parts by weight will result in deterioration of, for example, heat resistance. The molded articles of thermoplastic resins to which the present invention is applicable include primary, intermediate and final molded articles obtained using the composition described above by means of, for example, extrusion, injection molding, rotational molding, compression molding, or blow molding, such as, for example, films, sheets, plates, filaments, non-woven fabrics, pipes, vessels, dolls, special shapes, household electric products, and automobile parts such as bumper and instruments. According to the surface treating and/or coating method of the present invention, a special ultraviolet light having a radiation wave length in the region not longer than 300 nm is radiated to a molded article to activate the surface of the molded article, thereby improving the adhesive property, printability and coatability of the surface. The action of light applied to the surface of a molded article differs depending on the wave length of light, and the shorter the wave length, the more effective. It is desirable that the energy of light is shorter than 254 nm, in wave length occupy 85% or more of the entire energy. Ultraviolet light whose main operating wave length is near 185 nm is most preferable. The material of an ultraviolet radiation lamp which produces an ultraviolet light having a main operating wave length near 185 nm is preferably one which is high in the transmissivity of ultraviolet rays of short wave lengths. This is attained by using a synthetic quartz glass whose purity is higher than that of natural quartz glass. In the present invention, by using such an ultraviolet light of a short wave length, it is made possible to more activate the surface of a molded article and improve, for example the coatability, or adhesive property. At the time of radiating such ultraviolet light to the surface of a molded article, the surface may be treated with a solvent at room temperature or with a heated solvent, or the molded article may be heated and then treated with a solvent. Into the composition used in the present invention there may be incorporated additives within the range not affecting the object of the present invention. Examples of such additives include antioxidants, heat stabilizers (e.g. hindered phenol, phosphite, hydroquinone and thioether compounds), ultraviolet ray absorbers (e.g. benzotriazole, resorcinol and salicylate compounds), dyes or pigments, flame-retardants, antistatic agents, nucleating agents (crystallization accelerating agents), lubricants, foaming agents, crosslinking accelerators, and mold release agents. Several of these additives may be used in combination. [Function and Effect of the Invention] According to the method of the present invention, as set forth above, it is possible to activate surfaces of molded articles formed by resin compositions containing such polar group-free resins as polyolefin resins or polyester resins and difficult to be coated, bonded or printed, without requiring a surface treatment using solvent or plasma or a primer treatment, unlike the prior art. Particularly, it is possible to greatly improve the coatability, printability and adhesive property of molded articles such as automobile parts for which the use of plastic material has recently become very popular, e.g. interior parts such as instruments, trims and pillars, and exterior parts such as bumper and fascia, as well as household electric products. [Examples] The following examples are given to illustrate the present invention more concretely, but it is to be understood that the invention is not limited thereby. Examples 1-18 and Comparative Examples 1-6 Thermoplastic resins (A), functional group-containing polyolefins (B), inorganic fillers (C) and rubbery substances (D) were mixed as shown in Table 1. Test pieces were prepared by injection-molding the resulting compositions followed by annealing, unless otherwise described. How to prepare the compositions, conditions for preparing the test pieces by injection molding, and testing methods, are as follows. Each plate (3 mm thick, 100 × 200 mm) obtained by injection molding was placed in front of an ultraviolet light radiating device equipped with low-pressure mercury vapor lamp (SUV-110, a product of Sen Tokushu Kogen K.K.), and then ultraviolet light was radiated thereto in an air atmosphere for 5 minutes while the distance between the light source and the molded plate surface was kept 5 cm. (The low-pressure mercury vapor lamp had been fabricated using a synthetic quartz having a light transmissivity at a wave length of 185 nm of not less than 85%.) The thus surface-treated plate was coated with an acrylic coating material (manufactured by Shinto Toryo K.K.) by spraying. The resulting coating was dried for 24 hours or longer at room temperature and then cross-cut into 2 mm width. Cellophane tape was brought into pressure contact with the upper surface of the coating and then peeled off. The remaining area was regarded as adhesive property. The results obtained as set set forth in Table 1. The following thermoplastic resins, functional group-containing polyolefins, inorganic fillers and rubbery substances were used. A : Thermoplastic Resins (A1) Polypropylene (trade name: Nisseki Polypro J650G, MFR = 8.0, a product of Nippon Petrochemicals Co., Ltd.) (A2) Polypropylene (trade name: Nisseki Polypro J150G, MFR = 8.0, a product of Nippon Petrochemicals Co., Ltd.) (A3) Polypropylene (trade name: Nisseki Polypro 450H, MFR = 7.0, a product of Nippon Petrochemicals Co., Ltd.) (A4) Polybutylene terephthalate (PBT) (trade name: Valox 310, a product of Engineering Plastic K.K.) B : Functional Group-Containing Polyolefins (B1) Acid-modified polyethylene (trade name: Nisseki N Polymer A1600, MFR = 6.0, a product of Nippon Petrochemicals Co., Ltd.) (B2) Ethylene - Glycidyl methacrylate copolymer (trade name: Nisseki Rexpearl RA, a product of Nippon Petrochemicals Co., Ltd.) (B3) Ethylene - Hydroxyethyl methacrylate copolymer (B4) Ethylene - Dimethylamino methacrylate copolymer (B5) Oxazoline-modified polyethylene (B6) Quinoline-modified polyethylene. C : Inorganic Fillers (C1) Talc (C2) Calcium carbonate (C3) Glass fiber D : Rubbery Substances (D1) Ethylene-Propylene-Diene random copolymer rubber (trade name: EP-57P, a product of Japan Synthetic Rubber Co., Ltd.) (D2) Ethylene-Propylene random copolymer rubber (trade name: EP-07P, a product of Japan Synthetic Rubber Co., Ltd.) (D3) Ethylene-Propylene random copolymer rubber (trade name: EP-02P, a product of Japan Synthetic Rubber Co., Ltd.) Resin Composition Adhesion Component (A) Component (B) Component (C) Component (D) Kind 6 (Wt%) Kind Amount (Wt%) Kind Amount (part) Kind Amount (part) (%) Example 1 A 1 90 B 1 10 100 Example 2 A 1 80 B 1 20 100 Example 3 A 1 70 B 1 30 100 Example 4 A 2 80 B 1 20 100 Example 5 A 3 80 B 1 20 100 Example 6 A 1 80 B 2 20 100 Example 7 A 1 80 B 3 20 100 Example 8 A 1 80 B 4 20 100 Example 9 A 1 80 B 5 20 100 Example 10 A 1 80 B 6 20 100 Example 11 A 1 80 B 1 20 C 1 20 100 Example 12 A 1 80 B 1 20 C 2 20 100 Example 13 A 1 80 B 1 20 C 3 20 100 Example 14 A 1 80 B 1 20 D 1 20 100 Example 15 A 1 80 B 1 20 D 2 20 100 Example 16 A 1 80 B 1 20 D 3 20 100 Example 17 A 1 80 B 1 20 C 1 20 D 1 20 100 Example 18 A 4 90 B 1 10 100 Comparative Example 1 A 1 100 0 Comparative Example 2 A 2 100 0 Comparative Example 3 A 3 100 0 Comparative Example 4 A 1 100 C 1 20 46 Comparative Example 5 A 1 100 D 1 20 20 Comparative Example 6 A 1 100 C 1 20 D 1 20 60 A 1 : P P(J650G) A 2 : P P (J150G) A 3 : P P (F450H) B 1 :MAn-modified B 2 : E t -GMA B 3 : E t -HEMA B 4 : E t -DMAM B 5 : Oxazoline-modified B 6 : Quinoline-modified C 1 : Talc C 2 : Calcium carbonate C 3 : Glass fiber D 1 : E P D M (EP-57P) D 2 : E P M (EP-07P) D 3 : E P M (EP-02P)

Claims: A surface treating method for a themoplastic resin molded article, characterized by radiating an ultraviolet light at least 85% of the energy of which has a wavelength shorter than 254 nm and the main operating wavelength near 185 nm, to the molded article, said molded article being formed by a composition containing: (A) 50-95% by weight of a thermoplastic resin, said thermoplastic resin not being a polyethylene resin functionalized by at least one of B1 to B6. (B) 5-50 wt% of a polyethylene resin functionalized by at least one member selected from B1; carboxylic ester group- or acid anhydride group-containing monomers, B2: epoxy group-containing monomers, B3: hydroxyl group-containing monomers, B4: amino group-containing monomers, B5: alkenyl cyclic iminoether derivatives and B6: polyfunctional methacrylate monomers, polyfunctional vinyl monomers, bismaleimides or dioximes wherein when the polyethylene resin is functionalized by B1 or B6 the functionalisation is carried by graft-modification. A surface treating method as set forth in Claim 1, wherein said composition further contains: (C) 5-150 parts by weight of an inorganic filler, and/or (D) 3-50 parts by weight of a rubbery substance, based on 100 parts by weight of said components (A) + (B). A surface treating method as set forth in Claim 1 or Claim 2 wherein the functionalization of the polyolefin resin (B) is performed by graft-modification with at least one member selected from B2 to B5.

Inventors: IWASAKI YOSHIHARU, KATOH KOHICHIROH, NOGIWA MOTOMI, IWASAKI, YOSHIHARU, KATOH, KOHICHIROH, NOGIWA, MOTOMI
Applicants: AGENCY IND SCIENCE TECHN, NIPPON PETROCHEMICALS CO LTD, JAPAN AS REPRESENTED BY DIRECTOR-GENERAL, AGENCY OF INDUSTRIAL SCIENCE AND TECHNOLOGY, NIPPON PETROCHEMICALS CO., LTD.
Application year: 1991
Main classification: C08J7
IPC codes: B29C59, B29C35, C08J7, B05D3