A thin film of superconductor and a process for preparing the same

Abstract: A thin film of oxide superconductor deposited on a single crustal substrate of silicon wefer. A buffer layer of (100) or (110) oriented Ln₂O₃, in which Ln stands for Y or lanthanide elements is interposed between the thin film of oxide superconductor and the silicon wafer. A surface of silicon wafer is preferably cleaned satisfactorily by heat-treatment in vacuum before the buffer layer is deposited. An under-layer of metal oxide ; ZrO₂, YSZ or metal Y, Er is preferably interposed between the Ln₂O₃ buffer layer and the silicon wafer.

Description: Background of the Invention Field of the Invention The present invention relates to an improved thin film of oxide superconductor and a process for preparing the same, more particularly, an improved thin film of Cu-containing compound oxide such as YBCO having controlled crystal orientation deposited on a substrate of silicon wafer and a process for preparing the same. Description of the related art Superconducting phenomenon has been explained as unique phenomenon which can be observed only at extremely low temperatures which can be realized with liquid helium. However, a new type superconducting compound oxide of (La, Sr) 2 CuO 4 which exhibits the superconductivity at 30 K was reported in 1986 by Bednorz and Müller (Z. Phys. B64, 1986, 189). Then, another superconducting material of YBa 2 Cu 3 O y having higher critical temperature of about 90 K was reported in 1987 by C. W. Chu et al. (Physical Review letters, Vol. 58, No. 9, p. 908) and then Maeda et al. reported so-called bismuth type compound oxide superconductor having the critical temperature of about 100 K in 1988 (Japanese Journal of Applied Physics. Vol. 27, No. 2, p.1209 to 1210). These superconducting compound oxides are expected to be applied to actual uses since the superconducting phenomenon can be realized with relatively cheap cryogen of liquid nitrogen. In early stage of development, these superconducting compound oxides were prepared in a sintered body form by solid reaction and now, it has become possible to prepare thin films of high quality from these superconducting compound oxide materials. When thin films of oxide superconductor are used in electronics, it is requested to prepare their thin film whose crystals are well-oriented. In fact, oxide superconductors possess high anisotropy in their superconducting properties and hence it is necessary to control crystal orientation at film-forming stage so as to adjust to applications. In the thin films of oxide superconductors, higher current flows to a direction which is perpendicular to c-axis. For example, when the thin film of oxide superconductor is used as superconducting wiring lines in a circuit, it is required to pass superconducting current along a direction which is in parallel with a surface of substrate. In this case, the c-axis of crystals of the thin film must be perpendicular with respect to the surface of substrate. In other words, (001) oriented thin films of oxide superconductor are required in these applications. In another application such as layered SIS (superconductorinsulator-superconductor) type device, it is required to pass superconducting current along a direction which is perpendicular to the surface of substrate. In this case, the c-axis of crystals of the thin film prepared must be in parallel with the surface of substrate. In other words, (100) oriented thin film or (110) oriented thin films of oxide superconductor is required in these applications. Importance of selection of deposition plane in substrate or optimization of deposition conditions, particularly substrate temperature for realizing a desired crystal orientation in a thin film of oxide superconductor was reported by many papers including Enomoto et al., Japanese Journal of Applied Physics, Vol. 26, No. 7, July 1987, pp.L1248-L1250, Asano et al. in Japanese Journal of Applied Physics, Vol. 28, No. 6, June 1989, pp.L981-L983 or the like. It is also known that each of oxide superconductors possesses a complicated crystal structure and hence a desired crystal orientation can be realized only under a special deposition condition. In fact, the substrate on which a thin film of oxide superconductor is deposited must be selected from such substrates that have well-matched lattice constants with oxide superconductors and do not diffuse or migrate into the superconductor. From this point of view, MgO (100) single crystal or SrTiO 3 (100) or (110) single crystal are used as the substrate. Use of these substrates, however, has a demerit in industrial applications of oxide superconductors because they are costly material and are not produced in mass production. Still more, since diameters of these oxide single crystal substrates are limited, it is impossible to produce a thin film of oxide superconductor having a large area. It is also proposed to use, as substrate, a silicon single crystal substrate (Si wafer) which is less expensive and is available stably on market so as to prepare a thin film of oxide superconductor thereon. However, it is known that, when a thin film of oxide superconductor is deposited on the silicon single crystal substrate, superconducting properties of the deposited thin film are seriously deteriorated or lost due to chemical reaction between oxide of which the superconducting thin film is made and silicon of which the substrate is made. In order to solve this problem, it is proposed to interpose a buffer layer between the substrate and the thin film of oxide superconductor so as to prevent the diffusion. However, all of known buffer layers are not satisfactory to control or adjust crystal orientation of a thin film of oxide superconductor deposited on a silicon wafer. MYOREN and al., in Japanese Journal of Applied Physics, vol. 29, N° 6, June 1990, pp. L955-L957, have described a thin film of Ba 2 YCu 3 O x (c-axis oriented) deposited on a single crystal (100)-silicon wafer, with a buffer layer interposed between them. This buffer layer is constituted by a Y 2 O 3 film grown on a YSZ (yttrium-stabilized zirconia) layer, the Y 2 O 3 film being (100)-oriented. A good growth behaviour is obtained, but the applicability of the Ba 2 YCu 3 O x film is limited by the orientation of the film. JP 1-100094 discloses a Si substrate with a Y 2 O 3 buffer layer and a YBCO supraconductor layer. It is mentioned a (110) Y 2 O 3 silicon substrate. The article "Heteroepitaxial growth of Y 2 O 3 films on silicon", Applied Physics Ietters, Vol 55, N°4, 1989 discloses Si (111) and Si (100) substrate coated with Y 2 O 3 (111) and Si (100) substrate coated with YSZ.(100) oriented Y 2 O 3 films could not be grown directly Si (100) substrate. Therefore, an object of the present invention is to solve the problems presented above, and to provide a process which permits to prepare a thin film of oxide superconductor having a desired crystal orientation on a substrate of silicon wafer. Summary of the invention The present invention provides a thin film of (110)-oriented Y-Ba-Cu oxide superconductor deposited on a single crystal substrate of silicon wafer according to claim 1 with a buffer layer of (110) oriented Ln 2 O 3 in which Ln stands for Y or lanthanide elements, being interposed between the thin film of oxide superconductor and the silicon wafer. In an advantageous mode of realization, the lanthanide element of said buffer layer belong to a set including La and Er. An under-layer as an additional buffer layer has to be interposed between the buffer layer of Ln 2 O 3 and the silicon wafer. In any case, the thin film of oxide superconductor is deposited directly on and is contacted with the buffer layer of Ln 2 O 3 . The under-layer is of metal such as Y and lanthanide elements. The present invention provides also a process for preparing a thin film of Y-Ba-Cu oxide superconductor on a single crystal substrate of silicon wafer, comprising by the steps of cleaning satisfactorily a surface of the silicon wafer, depositing a buffer layer of (110) oriented Ln 2 O 3 , in which Ln stands for Y or lanthanide elements, on the cleaned silicon wafer and thereafter depositing the thin film of oxide superconductor on the buffer layer. The cleaning of the surface of silicon wafer can be effected by heat-treatment in vacuum effected under a pressure of lower than 1.4 x 10 -4 Pa (1 x 10 -6 Torr) and at a temperature of above 900°C. Above-mentioned under-layer is preferably deposited on said silicon wafer before the buffer layer of Ln 2 O 3 is deposited. The buffer layer of Ln 2 O 3 and the under-layer of metal such as Y and lanthanide elements can be prepared by vacuum deposition method, while the thin film of oxide superconductor is preferably prepared by sputtering method. Successive deposition operations of both of the buffer layer of Ln 2 O 3 and the under-layer and the thin film of oxide superconductor are preferably carried out in an identical vacuum chamber. An essence of the present invention resides in that a buffer layer of Ln 2 O 3 having a layered structure is deposited on a silicon single crystal substrate before a thin film of oxide superconductor is deposited. The term "buffer layer" means a layer of Ln 2 O 3 on which a thin film of oxide superconductor is deposited directly. As is stated above, it is known that effective thin films of all oxide superconductors can be deposited only on predetermined crystalline surfaces and that diffusion of silicon into the thin film of oxide superconductor results in deterioration and loss of superconducting properties. Several materials for the buffer layer are proposed. Known materials for the buffer layer are selected from those that can produce crystalline surfaces which are suitable for realizing thin films of oxide superconductor thereon and which function as a diffusion barrier to silicon and constituent elements of oxide superconductor. In fact, known buffer layers are satisfactory to prevent diffusion of silicon but contribute little to crystal growth of the thin film of oxide superconductor to be deposited directly thereon. According to the present invention, the buffer layer on which a thin film of oxide superconductor is deposited is made of a material which does not or little react with superconductor, has well-matched lattice constants with crystals of the superconductor and also has a predetermined crystal orientation, so that the thin film of oxide superconductor deposited on the buffer layer grows epitaxially and possesses a well-ordered crystal orientation. Inventors of the present invention found that such epitaxial growth can be realized by selecting, as the buffer layer, Ln 2 O 3 , in which "Ln" stands for Y or lanthanide elements such as La, Er. As a substrate on which thin films grow, (100) single crystal silicon wafer is usually used because of cost and easy of matching in lattice constants. A thin film deposited on this (100) single crystal silicon wafer is expected to have identical crystal orientation of (100). However, actually obtained thin film by known technique doesn't possess crystal orientation of (100) but possesses a crystal orientation of (111). This fact is reported by Fukomoto et al. in Appl. Phys. Lett. 55(4) 24, July 1989, pp 360-361. This (111) oriented thin film, however, is not suitable to effect epitaxial growth of oxide superconductor because (100) or (110) oriented thin films is demanded in actual applications of thin films of oxide superconductor. The (110) oriented thin film as a buffer layer can be prepared from Ln 2 O 3 according to the present invention. In the process according to the present invention, one of following methods is preferably adopted in order to realize the (110) oriented thin film: A surface of a silicon wafer to be used is cleaned satisfactorily. In practice, this cleaning operation can be carried out, for example, by heat-treatment in a high-vacuum chamber with observing a surface condition of a silicon wafer. This heat-treatment can be carried out until a characteristic "2x1" structure which means that the surface becomes clean is observed by a reflection high-energy electron diffraction (RHEED) analyzer. In practice, the heattreatment is carried out preferably at a pressure of lower than 1.4 x 10 -4 Pa (1 x 10 -6 Torr) and at a temperature of above 900°C. An additional buffer layer (hereinafter, under-buffer layer) is interposed between the Ln 2 O 3 buffer layer on which a thin film of oxide superconductor is deposited directly and the silicon wafer, in other words, the buffer layer has a two-layered structure. The under-buffer layer used as additional buffer layer is selected so as to satisfy such two requirements that the under-layer is well-matched with the (100) crystal orientation of silicon wafer and that the under-layer possesses a (100) or (110) plane. This under-buffer layer is made of metal elements such as Y, Er, Pr, Dy, Ho, Yb, Gd, Sm or the like. Crystal orientation of the under-layer on which the Ln 2 O 3 buffer layer is deposited directly can be controlled by using the method according to claim 4. As a conclusion, according to the present invention, thin films of Y-Ba-Cu oxide superconductors having controlled (110) crystal orientation can be prepared on a silicon wafer substrate. Thin films of oxide superconductors according to the present invention possess effective crystalline structure which starts just from an interface with the buffer layer and shows improved critical current density (Jc). Use of silicon single crystal wafer as a substrate is very advantageous in the field of electronics devices since a variety of fine processing technology of silicon wafer are known and applicable in addition to such merits that single crystal wafer is less expensive and is available stably on market. And also. a thin film having a large area can be prepared because a silicon wafer having a large diameter is available on market. Description of the Preferred Embodiments Now, the present invention will be described with reference to Examples, but the scope of the present invention should not be limited thereto. Example 1 Six silicon wafers each having a diameter of 3 inch (1 inch = 2.54 cm) were used. Three silicon wafers were subjected to cleaning treatment which was effected at 900 °C under 6.7 x 10 -5 Pa (5 x 10 -7 Torr) for 10 minute until the characteristic "2x1" structure was observed on the silicon wafer by RHEED. Then, an under buffer layer of ZrO 2 (not included in the invention) or Y was deposited on two silicon wafers which were not heat-treated and on two silicon wafers which were cleaned by the heat-treatment. The under buffer layers of ZrO 2 and Y were deposited by vacuum deposition technique. In the case of two cleaned silicon wafers vacuum deposition was carried out continuously in the same chamber as the cleaning chamber without exposing the heat-treated silicon wafers to air. Film-forming conditions of the under buffer layers are summarized in table 1 Buffer layer ZrO 2 Y vapour source sintered ZrO 2 metal Y substrate temperature (°C) 800 700 pressure (Pa) 6.7 x 10 -4 ( 5 x 10 -6 Torr) 6.7 x 10 -5 (5 x 10 -7 Torr) film thickness (Å) 200 50 The results of six silicon wafers are summarized in Table 2 in which film-growth planes of obtained buffer layers are also shown. Sample No. Cleaning treatment buffer layer growth plane 1 no none ---- 2 no ZrO 2 (100) 3 no Y (100) 4 yes none ---- 5 yes ZrO 2 (100) 6 yes Y (100) Then, an upper buffer layer of Y 2 O 3 was deposited by vacuum evaporation technique on the six wafers obtained under the condition shown in Table 3. vapour source metal Y substrate temperature (°C) 760 °C partial pressure of oxygen (Pa) 6.7 x 10 -2 (5 x 10 -4 Torr) film thickness (Å) 300 Crystal orientation of upper buffer layers of Y 2 O 3 obtained under the above condition was evaluated by X-ray diffraction analyzer. The results are summarized in Table 4. Samples No. 1, 2, and 5 do not possess the desired (110)-orientation and serve for illustration only. Sample No film growth plane 1 (111) 2 (100) 3 (110) 4 (110) 5 (100) 6 (110) Finally, a thin film of Y-Ba-Cu oxide superconductor was deposited on the resulting upper buffer layer by sputtering technique under conditions shown in Table 5: composition in a target Y 1 Ba 2 Cu 4 O x substrate temperature (°C) 700 sputtering gas Ar+O 2 (20 vol %) pressure (Pa) 13.3 (0.1 Torr) film thickness (Å) 2,000 Superconducting properties and crystal orientation of the resulting six thin films of oxide superconductor are summarized in Table 6. The critical current density (Jc) was determined at liquid nitrogen temperature with current passing along a direction which is perpendicular to c-axis of crystal of which the thin film is made. Again, samples No. 1, 2, and 5 serve for illustration only and do not fall within the scope of the appending claims. Sample No. Critical temperature (K) Critical current density (A/cm 2 ) Orientation of crystal 1 78 1 x 10 2 polycrystal 2 85 8 x 10 5 (001) 3 84 5 x 10 5 (110) 4 85 4 x 10 5 (110) 5 89 2 x 10 6 (001) 6 88 1 x 10 6 (110)

Claims: A thin film of Y-Ba-Cu oxide superconductor deposited on a (100) single crystal substrate of silicon wafer, with a buffer layer interposed between said thin film of oxide superconductor and said silicon wafer, characterized in that said buffer layer contains (110) oriented Ln 2 O 3 , in which Ln stands for Y or lanthanide elements, in that the Y-Ba-Cu oxide superconductor film is (110)-oriented, and in that an under-layer as an additional buffer layer is interposed between said buffer layer of Ln 2 O 3 and said silicon wafer, said under-layer being a layer made of a metal selected from the group comprising Y and lanthanide elements. The thin film set forth in claim 1, wherein said lanthanide elements of said buffer layer belong to a set including La and Er. The thin film set forth in claim 1 or 2, wherein said thin film of oxide superconductor is directly deposited on and contact with said buffer layer of Ln 2 O 3 . A process for preparing a thin film of Y-Ba-Cu oxide superconductor on a (100) single crystal substrate of silicon wafer comprising by the steps of cleaning satisfactorily a surface of said silicon wafer, depositing a buffer layer on the cleaned silicon wafer, and then depositing said thin film of oxide superconductor on said buffer layer, characterized in that said buffer layer contains (110) oriented Ln 2 O 3 , in which Ln stands for Y or lanthanide elements, in that the Y-Ba-Cu oxide superconductor film is (110)-oriented, wherein an under-layer as an additional buffer layer is deposited on said silicon wafer and said buffer layer of Ln 2 O 3 is deposited on said under-layer, said under -layer being a layer made of a metal selected from the group comprising Y and lanthanide elements. The process set forth in claim 4, wherein the cleaning of said surface of silicon wafer is effected by heat-treatment in vacuum. The process set forth in claim 5, wherein said heat-treatment is effected under a pressure of lower than 1.4 x 10 -4 Pa (1 x 10 -6 Torr) and a temperature of above 900°C. The process set forth in any one of claims 4 to 6, wherein said buffer layer of Ln 2 O 3 and said under-layer are prepared by vacuum deposition method. The process set forth in any one of claims 4 to 7, wherein said thin film of oxide superconductor is prepared by sputtering method. The process set forth in any one of claims 4 to 8, wherein deposition operations of said buffer layer of Ln 2 O 3 and said under-layer and said thin film of oxide superconductor are carried out in a same vacuum chamber successively.

Inventors: HARADA KEIZO, ITOZAKI HIDEO, NAKANISHI HIDENORI, HARADA, KEIZO, ITOZAKI, HIDEO, NAKANISHI, HIDENORI
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1991
Main classification: H01L39
IPC codes: C01G1, C30B29, H01L39, C01G3