Method of producing optical waveguides by an ion exchange technique on a glass substrate

Abstract: The invention relates to a method of producing waveguides (6) by an ion exchange technique on a glass substrate (1). In order to be able to alleviate the tolerances allowed for the ion exchange technique, waveguides (3) are formed by first diffusing ions which increase the refractive index into the glass substrate (1) over an area wider than the optical waveguides to be produced (6). A positive-type ion exchange mask (4) is formed thereon, and finally the ions which increase the refractive index are taken off by using the ion exchange technique in the regions having no mask.

Description: The invention relates to a method of producing optical waveguides by an ion exchange technique on a glass substrate. Interest in the use of ion-exchanged glass waveguides for passive integrated optics has increased considerably recently. Typical examples of such components and devices are single-mode 1/N power dividers and wavelength selective directional couplers. Since the operation of optical glass waveguides is purely passive, and does not allow adjustment after production, accurate control of production parameters is needed to obtain the desired waveguide reproducibility. This is especially important in the case of directional couplers, in which an accurate control of the propagation constant difference between symmetrical and asymmetrical modes is necessary. To produce optical fiber compatible waveguides by an ion exchange technique, two-step processes are generally used. In these processes, waveguides are formed by the exchange of the original ions in the glass (typically sodium ions Na⁺) to ions increasing the refractive index (such as K⁺, Ag⁺, Cs⁺, Rb⁺, Li⁺ or Tl⁺ ions) through a narrow opening in the ion exchange mask, and by using salt melts or a silver film as an ion source. In the second step, thermal treatment or ion exchange in an NaNO₃ melt modifies the refractive index profile of the waveguide to obtain better coupling to optical fiber. As the diffusion during the second step increases the width of waveguides, narrow (≈ 2 - 4 µm) mask openings must be used in the first step. The number of exchanged ions is very sensitive to the mask opening width, wherefore there is a marked need of a new production method which allows a wider range of variation for the mask opening width. As to the basic principles of the ion exchange technique, the following article is referred to: Ion-Exchanged Glass Waveguides: A Review, R.V. Ramaswamy , Journal of Lightwave Technology, Vol. 6, No. 6, June 1988, p.984. The object of the invention is to provide a method which reduces the sensitivity of the optical waveguide production process to variation in the width of mask lines or mask openings. According to the invention, there is provided a method of producing an optical waveguide including a light channel comprising: providing a glass substrate having a first refractive index, diffusing first ions into a surface of said substrate to produce a zone at said surface having a second refractive index greater than said first refractive index, forming an ion diffusion mask on said substrate surface overlying said zone, said mask having a shape narrower than the planar zone, said shape corresponding to a desired light channel in said substrate, and forming the desired light channel by an ion-exchange technique characterised in that said zone is a planar zone and in that said light channel is formed by diffusing said first ions out of the glass substrate, from said surface from portions of said zone not covered by said mask by an ion exchange technique and removing said mask. A method corresponding to the preamble of claim 1 is disclosed in JP-A-58-136 007. A special feature of the method of the invention is that the light channel is not formed until during the second step of the two-step ion exchange process. As a result, the diffusion taking place during the formation of the light channel makes the light channel narrower instead of widening it as in prior art ion exchange techniques. As a consequence, the tolerances allowed for the width of the mask openings and lines in the thin-film mask technique can be considerably alleviated. For example, the width of single-mode diffusion mask openings used in conventional ion exchange technique is about 2 to 4 µm whereas corresponding single-mode channels are achieved with line widths of about 8 to 10 µm by means of the method of the invention. The invention will now be described in greater detail by means of an embodiment with reference to the attached drawing, in which Figures 1 to 5 illustrate the different steps of the method of the invention. In the method of the invention for the production of waveguides by an ion exchange technique on a glass substrate, waveguides are formed by diffusing refractive index increasing ions away from a wider waveguide which has been formed previously on the glass substrate by utilizing an ion exchange technique and a positive-type ion exchange mask. The method thereby typically comprises the steps of forming a planar optical waveguide on a glass substrate by the ion exchange technique (with a negative-type ion exchange mask), forming a positive-type'-'-ion exchange mask on said planar waveguide, and removing ions which increase the refractive index of the planar waveguide by the ion exchange technique from glass substrate regions having no ion exchange mask. The planar waveguide may cover the whole surface of the substrate. Figure 1 illustrates the first step of the method of the invention, in which there is formed in a planar glass substrate 1, a planar zone of higher refractive index than the remainder of substrate 1, by introducing refractive-index-increasing ions to the surface of the glass substrate by using the ion exchange technique. In the preferred embodiment of the invention, this first step utilises solid-phase silver ion exchange. For this purpose, a thin silver film having a thickness of e.g. about 150 nm is formed by sputtering on the glass substrate 1, such as Corning 0211 glass. A metal film (not shown) is formed on the opposite side of the glass substrate 1, and a voltage, e.g. 50 V, is connected between the silver film 2 and the metal film on the opposite side at an elevated temperature (e.g. 350°C). Na⁺ ions thereby start to propagate from the glass substrate 1 to the metal film acting as a cathode, and correspondingly Ag⁺ ions start to propagate from the silver film 2 to the glass substrate 1, so that a planar layer 3 having a higher refractive index than that of the surrounding glass is formed on the glass substrate 1. After the formation of the planar layer or zone 3, the silver film 2 and the metal film on the opposite side of the substrate 1 are removed, which results in the situation shown in Figure 2. Thereafter an ion exchange mask film 4 is formed on the glass substrate 1 upon the planar waveguide 3. The ion exchange mask 4 is of the positive type, that is, it is formed on the substrate 1 at places where the waveguide is to be formed whereas there is no ion exchange mask film at places where no waveguide is to be formed. Thus the positive-type ion exchange mask pattern 4 corresponds to a desired optical waveguide pattern. The ion exchange mask film can be made e.g. of titanium (Ti). Thereafter the glass substrate 1 provided with the ion exchange mask 4 is subjected to ion exchange in a NaNO₃ melt 5. Na⁺ ions thereby propagate from the melt 5 to the surface layer of the glass substrate 1 and to the planar optical waveguide 3. Correspondingly, refractive index increasing ions, such as Ag⁺ ions, propagate from the surface of the glass substrate 1 and the waveguide 3 into the NaNO₃- melt 5. The ion exchange takes place only within glass substrate surface regions where there is no ion exchange mask 4. No ion exchange takes place through the ion exchange mask 4, so that a waveguide channel 6 is formed under the ion exchange mask 4. After the ion exchange is completed within regions having no ion exchange mask 4, the glass substrate 1 is removed from the salt melt 5 and the ion exchange mask 4 is removed, so that the glass substrate now has the desired optical waveguide channel 6, as shown in Figure 5. Thus, in the method described with reference to the drawings, optical waveguides are produced by an ion exchange technique on a glass substrate, wherein the waveguides are formed by diffusing ions increasing the refractive index away from a layer of high refractive index which has been formed previously on the glass substrate and which is wider than the optical waveguides to be produced, the last-noted diffusion step being carried out by using the ion exchange technique and a positive-type ion exchange mask. In the first step of the method, a planar optical waveguide, which is not limited in the sideward direction, i.e. is wider than the final optical waveguide to be formed, is formed on the glass substrate by the ion exchange technique. In the second step, a narrow ion exchange mask film is formed on the glass, whereafter the ion exchange is carried out by diffusing ions increasing the refractive index of the planar waveguide out of the glass in regions where there is no ion exchange mask. A desired sidewardly limited light channel, i.e. a light channel narrower than the planar waveguide, is formed on the glass substrate at places where the ion exchange mask prevents diffusion out of the glass. The attached figures and the description related to them are only intended to illustrate the present invention. In its details, the method of the invention may vary within the scope of the attached claims. For instance, the composition of the ion sources, the glass substrate and the ion exchange masks may vary according to the requirements in each particular application.

Claims: A method of producing an optical waveguide including a light channel comprising: providing a glass substrate having a first refractive index, diffusing first ions into a surface of said substrate to produce a zone at said surface having a second refractive index greater than said first refractive index, forming an ion diffusion mask on said substrate surface overlying said zone, said mask having a shape narrower than the zone, said shape corresponding to a desired light channel in said substrate, and forming the desired light channel by an ion-exchange technique characterised in that said zone is a planar zone and in that said light channel is formed by diffusing said first ions out of the glass substrate, from said surface from portions of said zone not covered by said mask by an ion exchange technique and removing said mask. A method according to claim 1 wherein a salt melt or a silver film is used as an ion source for producing said planar zone. A method according to claim 1, wherein said planar zone covers substantially the whole surface of the substrate. A method according to claim 1 wherein said diffusion of said first ions from said portion of said zone not covered by said mask is performed in an ion exchange process using a NaNO₃ melt placed in contact with said planar zone for providing a source of second ions which are exchanged with said first ions during the second diffusion step. A method according to claim 1, wherein the ion mask is made by sputtering from titanium.

Inventors: HONKANEN SEPPO, TERVONEN ARI, HONKANEN, SEPPO, TERVONEN, ARI
Applicants: NOKIA OY AB, OY NOKIA AB
Application year: 1991
Main classification: G02B6
IPC codes: C03C21, G02B6