ALUMINUM-FREE MONOCYCLOPENTADIENYL METALLOCENE CATALYSTS FOR OLEFIN POLYMERIZATION

Abstract: The invention is a catalyst system including a Group IV-B transition metal component and an activator component which may be employed to polymerize olefins to produce a high molecular weight polymer. The Group IV-B transition metal component contains a single cyclopentadienyl ligand and a single heteroatom ligand, which ligands may be bridged one to another; the activator component comprises a cation, which may be a Bronsted acid capable of donating a proton (hereafter denoted as L'-H wherein L' is a neutral Lewis base and H is hydrogen), and a compatible noncoordinating anion.

Description: ALUMINUM-FREE MONOCYCLOPENTADIENYL METALLOCENE CATALYSTS FOR OLEFIN POLYMERIZATION SPECIFICATION FIELD OF THE INVENTION This invention relates to certain transition metal compounds of the Group IV-B metals of the Periodic Table of Elements, to a catalyst system comprising such Group IV-B transition metal compounds and an ion-exchange activator compound, and to a process using such catalyst system for the production of polyolefins, particularly polyethylene, polypropylene, and ethylene-α-olefin copolymers. BACKGROUND OF THE INVENTION As 1s well known, various processes and catalysts exist for the homopolymerization or copolymerization of olefins. Traditional Ziegler-Natta catalyst systems—a transition metal compound cocatalyzed by an aluminum alkyl—are capable of producing polyolefins having a high molecular weight but a broad molecular weight distribution. Traditional types of Ziegler-Natta catalysts have very high activities, and the polyolefins produced therewith have low catalyst residues and do not require a subsequent catalyst residue deashing treatment. More recently a "metallocene" type catalyst system has been develope —one wherein the transition metal compound has cyclopentadienyl ring ligands, preferably at least two; such transition metal compound being referred to as a "metallocene"—which catalyzes the production of olefln monomers to polyolefins. Accordingly, metallocene compounds of the Group IV-B metals, particularly bis(cydopentadlenyl) tltanocenes and zirconocenes, have been utilized as the transition metal component in such "metallocene" containing catalyst system for the production of polyolefins and ethylene-α-olefin copolymers. When such metallocenes are cocatalyzed with an aluminum alkyl—as is the case with a traditional type Ziegler-Natta catalyst system—the catalytic activity of such metallocene catalyst system 1s generally too low to be of any commercial interest. It has since become known that such metallocenes may be cocatalyzed with an alumoxane—rather than an aluminum alkyl—to provide a metallocene catalyst system of high activity for catalyzing the production of moderately high molecular weight polyolefins. Unfortunately, the amount of alumoxane cocatalyst required to provide the metallocene component with high activity is generally high, generally expressed as a molar ratio of Al to transition metal, hence a polyolefin produced from such metallocene-alumoxane catalyst may contain an undesirable amount of catalyst residue (or ash content, measured as the nonvolatile aluminum and transition metal content). More recently, a new method of activating Group IV-B metallocene alkyl complexes was disclosed in European Patent Applications Nos.277,003 and 277,004. The improved metallocene catalysts are prepared by combining at least two components. The first component is a bis(cyclopentadlenyl) derivative of a Group IV-B metal containing at least one ligand which will combine with the cationlc portion of the second component. The second component 1s an Ion-exchange reagent comprising a cation which will Irreversibly react with at least one ligand contained in said Group IV-B metal compound (first component) and a non-coordinating anlon which Is bulky, labile and stable. Suitable non-coordinating anions disclosed in these applications Include: 1) anionlc coordination complexes comprising a plurality of lipophlUc radicals covalently coordinated to and shielding a central charge-bearing metal or metalloid core, and 2) anions comprising a plurality of boron atoms such as carboranes, metallocarboranes and boranes. Upon combination of the first and second components, the cation of the second component reacts with one of the ligands of the first component, thereby generating an ion-pair consisting of a Group IV-B metallocene cation with a formal coordination number of 3 and a valence of 4+ and the aforementioned non-coordinating anlon. The disclosures are limited to catalyst systems derived from Group IV-B metallocene complexes containing at least two cyclopentadienyl ligands. Aluminum alkyl-free olefin polymerization catalysts derived from transition metal complexes containing fewer than two cyclpentadiene have been relatively unexplored. John Bercaw reported [Organometallics, 1990, 9, 867] the synthesis of a monocyclopentadienyl scandium polymerization catalyst, [Me 2 S1(C 5 Me 4 )(N-Bu t )ScH(PMe 3 )2 2 This neutral Group III catalyst has a low activity and is very expensive due to the high cost of scandium metal. The need exists to provide a method of preparing highly active, versatile, aluminum alkyl-free olefin polymerization catalysts derived from monocyclopentadienyl ligand systems. SUMMARY OF THE INVENTION The catalyst system of this invention comprises a transition metal component from Group IV B of the Periodic Table of the Elements (CRC Handbook of Chemistry and Physics. 68th ed. 1987-1988) and an Ion-exchange reagent which may be employed 1n solution, slurry, gas phase or bulk phase polymerization procedure to produce a polyolefln of high weight average molecular weight and relatively narrow molecular weight distribution. In general the Group IV B transition metal component can be a polyalkyl or hydride complex containing fewer than two cyclopentadienyl groups. The "Group IV B transition metal component" of the mono-cyclopentadlenyl catalyst system is represented by the general formula: JR, z-l-y wherein: M is Zr, Hf or Ti and 1s in its highest formal oxidation state (+4, d complex); C j -H c χ R χ ) is a cyclopentadienyl ring which is substituted with from zero to five substituent groups R, "x" 1s 0, 1, 2, 3, 4 or 5 denoting the degree of substitution, and each substituent group R is, independently, a radical selected from a group consisting of ,-C 2Q hydrocarbyl radicals, substituted C,-C 20 hydrocarbyl radicals wherein one or more hydrogen atoms is replaced by a halogen atom, C j -C.^ hydrocarbyl-substltuted metalloid radicals wherein the metalloid 1s selected from the Group IV A of the Periodic Table of Elements, and halogen radicals; or (C C H C ., W R„) is a cyclopentadienyl ring 1n which two adjacent o o— -x x R-groups are joined forming a C 4 -C 2Q ring to give a polycyclic cyclopentadienyl ligand such as indenyl and fluorenyl derivatives. (JR* , ) 1s a heteroatom ligand 1n which J is an element with a coordination number of three from Group V A or an element with a coordination number of two from Group VI A of the Periodic Table of Elements, preferably nitrogen, phosphorus, oxygen or sulfur, and each R' 1s, Independently a radical selected from a group consisting of C j -C 20 hydrocarbyl radicals, substituted ^-Cg Q hydrocarbyl radicals wherein one or more hydrogen atoms is replaced by a halogen atom, and M z" is the coordination number of the element J; each 0 may be Independently, hydride, ,-C 5Q hydrocarbyl radicals, substituted hydrocarbyl radicals wherein one or more hydrogen atoms 1s replaced by an electron-withdrawing group such as a halogen atom, or alkoxide radical, or C,-C 50 hydrocarbyl-substltuted metalloid radicals wherein the metalloid is selected from the Group IV-A of the Period Table of Elements, provided that were any 01s a hydrocarbyl such 01s different from ^gH 5 χ R χ ), or both 0 together may be an alkylidene, olefin, acetylene or a cyclo etallated hydrocarbyl. "y" is 0 or 1; when "y" 1s 1, B is a covalent bridging group containing a Group IV A or V A element such as, but not limited to, a dialkyl, alkylaryl or diaryl silicon or germanium radical, alkyl or aryl phosphine or amlne radical, or a hydrocarbyl radical such as methylene, ethylene and the like; L Is a neutral Lewis base such as dlethylether, tetrahydrofuran, dlmethylanillne, aniline, trimethylphosphine, n-butylamine, and the like; and "w" is a number from 0 to 3; L can also be a second transition metal compound of the same type such that the two metal centers M and M' are bridged by Q and Q', wherein M' has the same meaning as M and Q' has the same meaning as Q. Such compounds are represented by the formula: The second component 1s an 1on-exchange compound comprising a cation which will Irreversibly react with at least one ligand contained 1n said Group IV-B metal compound and a noncoordinating anion which is bulky, labile, and stable. Upon combination of the first and second components, the cation of the second component reacts with one of the ligands of the first component, thereby generating an 1on pair consisting of a Group IV-B metal cation with a formal coordination number of 3 and a valence of +4 and the aforementioned anion, which anion is compatible with and non-coordinating toward the metal cation formed from the first component. Illustrative but not limiting examples of cations of the second component Include Bronstead adds such as ammonium ions or reducible Lewis adds such as Ag + or ferrocenium ions. The anion of the second compound must be capable of stabilizing the Group IV-B metal cation complex without interfering with the Group IV-B metal cation's or Its decomposition product's ability to function as a catalyst and must be sufficiently labile to permit displacement by an olefin, diolefin or an acetylenlcally unsaturated monomer during polymerization. Catalyst systems of the Invention may be prepared by placing the "Group IV B transition metal component" and the ion-exchange component in common solution 1n a normally liquid alkane or aromatic solvent, which solvent Is preferably suitable for use as a polymerization diluent for the liquid phase polymerization of an olefin monomer. Suitable catalysts can also be prepared by reacting the components and adsorbing on a suitable support material (Inorganic oxides or polymers, for example) or by allowing the components to react on such support. A typical polymerization process of the invention such as for the polymerization or copolymerization of ethylene comprises the steps of contacting ethylene alone, or with other unsaturated monomers Including Cg-C 20 α-olefins, C c - 20 dloleflns, and/or acetylenlcally unsaturated monomers either alone or in combination with other olefins and/or other unsaturated monomers, with a catalyst comprising, 1n a suitable polymerization diluent, the Group IV B transition metal component Illustrated above; and the ion-exchange activator component in an amount to provide a molar transition metal to activator ratio of from about 1:10 to about 200:1 or more; and reacting such monomer 1n the presence of such catalyst system at a temperature of from about -100 * C to about 300*C for a time of from about 1 second to about 10 hours to produce a polyolefin having a weight average molecular weight of from about 1,000 or less to about 5,000,000 or more and a molecular weight distribution of about 1.5 or greater. DESCRIPTION OF THE PREFERRED EMBODIMENT Ionic Catalyst System - General Description The process of this Invention 1s practiced with that class of ionic catalysts prepared by combining at least two components. The first of these 1s a monocyclopentadienyl derivative of a Group IV-B metal compound containing at least one ligand which will combine with the second component or at least a portion thereof such as a cation portion thereof. The second component 1s an ion-exchange compound comprising a cation which will Irreversibly react with at least one ligand contained in said Group IV-B metal compound and a noncoordinating anion which 1s bulky, labile, and stable. Upon combination of the first and second components, the cation of the second component reacts with one of the ligands of the first component, thereby generating an ion pair consisting of a Group IV-B metal cation with a formal coordination number of 3 and a valence of +4 and the aforementioned anion, which anlon 1s compatible with and non-coordinating towards the metal cation formed from the first component. The anion of the second compound must be capable of stabilizing the Group IV-B metal cation complex without Interfering with the Group IV-B metal cation's or its decomposition product's ability to function as a catalyst and must be sufficiently labile to permit displacement by an olefin, diolefln or an acetylenlcally unsaturated monomer during polymerization. A. Catalyst Component The Group IV-B transition metal component of the catalyst system is represented by the general formula: ^'z-l-y* wherein: M is Zr, Hf or Ti and Is in its highest formal oxidation state (+4, d complex); CgHg R χ ) is a cyclopentadienyl ring which 1s substituted with from zero to five substituent groups R, "x" Is 0, 1, 2, 3, 4 or 5 denoting the degree of substitution, and each substituent group R 1s, Independently, a radical selected from a group consisting of j -C 20 hydrocarbyl radicals, substituted C j -C 20 hydrocarbyl radicals wherein one or more hydrogen atoms Is replaced by a halogen atom, C j -C 20 hydrocarbyl-substituted metalloid radicals wherein the metalloid is selected from the Group IV A of the Periodic Table of Elements, and halogen radicals; or (C g H 5 R χ ) Is a cyclopentadienyl ring 1n which two adjacent R-groups are joined forming a C 4 -C 2Q ring to give a polycycllc cyclopentadienyl ligand such as Indenyl and fluorenyl derivatives; (JR' ^ ) 1s a heteroatom Ugand in which J Is an element with a coordination number of three from Group V A or an element with a coordination number of two from Group VI A of the Periodic Table of Elements, preferably nitrogen, phosphorus, oxygen or sulfur with nitrogen being preferred, and each R' Is, independently a radical selected from a group consisting of C ι-C 20 hydrocarbyl radicals, substituted C j -C 20 hydrocarbyl radicals wherein one or more hydrogen atoms Is replaced by a halogen atom, and "z" 1s the coordination number of the element J; each 0 may be Independently, hydride, ,-C 50 hydrocarbyl radicals, substituted hydrocarbyl radicals wherein one or more hydrogen atoms 1s replaced by an electron-withdrawing group such as a halogen atom, or alkoxide radical, or C,-C 5Q hydrocarbyl-substituted metalloid radicals wherein the metalloid 1s selected from the Group IV-A of the Periodic Table of Elements, provided that where any 0 Is a hydrocarbyl such 0 is different from (C 5 H 5_y- χ 'V• or botn °- together may be an alkylldene olefin, acetylene or a cyclometallated hydrocarbyl; "y" is 0 or 1; when "y" is 1, B Is a covalent bridging group containing a Group IV A or V A element such as, but not limited to, a dialkyl, alkylaryl or diaryl silicon or germanium radical, alkyl or aryl phosphine or amine radical, or a hydrocarbyl radical such as methylene, ethylene and the like. Examples of the B group which are suitable as a constituent group of the Group IV B transition metal component of the catalyst system are identified in Column 1 of Table 1 under the heading "B". L 1s a neutral Lewis base such as diethylether, tetrahydrofuran, di ethylaniline, aniline, trimethylphosphine, ll-butylamine, and the like; and "w" is a number from 0 to 3; L can also be a second transition metal compound of the same type such that the two metal centers M and M' are bridged by Q and Q\ wherein M' has the same meaning as H and Q' has the same meaning as Q. Such compounds are represented by the formula: Exemplary hydrocarbyl radicals for the Q are methyl, ethyl, propyl, butyl, amyl, isoamyl, hexyl, isobutyl, heptyl, octyl, nonyl, decyl, cetyl, 2-ethylhexyl, phenyl and the like, with methyl being preferred. Exemplary substituted hydrocarbyl radicals include trifluoromethyl, pentafluorphenyl, trimethylsllylmethyl, and trimethoxys11yl ethyl and the like. Exemplary hydrocarbyl substituted metalloid radicals Include trimethylsilyl, tri ethylgermyl, triphenylsllyl, and the like. Exemplary alkyldiene radicals for both 0 together are ethylidene, ethyϋdene and propyl1dene. Examples of the Q group which are suitable as a constituent group or element of the Group IV B transition metal component of the catalyst system are Identified in Column 4 of Table 1 under the heading "Q". Suitable hydrocarbyl and substituted hydrocarbyl radicals, which may be substituted as an R group for at least one hydrogen atom in the cyclopentadienyl ring, will contain from 1 to about 20 carbon atoms and include straight and branched alkyl radicals, cyclic hydrocarbon radicals, alkyl-substituted cyclic hydrocarbon radicals, aromatic radicals and alkyl-substituted aromatic radicals. Suitable organometallic radicals, which may be substituted as an R group for at least one hydrogen atom in the cyclopentadienyl ring, include trlmethylsllyl, triethylsllyl, ethyldl ethylsilyl, methyld1ethylsilyl, triphenylgermyl, trimethylgermyl and the Hke. Examples of cyclopentadienyl ring groups < C 5 H 5_ y _ x R x > wn1cn are suitable as a constituent group of the Group IV B transition metal component of the catalyst system are identified 1n Column 2 of Table 1 under the heading (C 5 H 5-y-x R x } ' Suitable hydrocarbyl and substituted hydrocarbyl radicals, which may be substituted as an R' group for at least one hydrogen atom in the heteroatom 3 ligand group, will contain from 1 to about 20 carbon atoms and include straight and branched alkyl radicals, cyclic hydrocarbon radicals, alkyl-substituted cyclic hydrocarbon radicals, aromatic radicals and alkyl-substituted aromatic radicals. Examples of heteroatom ligand groups (JR* « ) which are suitable as a constituent group of the Group IV B transition metal component of the catalyst system are identified 1n Column 3 of Table 1 under the heading (JR' 2 _ι „ . Table 1 depicts representative constituent moieties for the "Group IV B transition metal component", the list 1s for Illustrative purposes only and should not be construed to be limiting in any way. A number of final components may be formed by permuting all possible combinations of the constituent moieties with each other. Illustrative compounds are: dimethylsllyltetra- methylcyclopentadienyl-iexi-butylamldo zirconium dimethyl, dimethyls1lyltetramethylcyclopentadienyl-i≤ri-butylamido hafnium diethyl, d1methylsilyl-i£ri-butylcyclopentadienyl-±£τt-butyl- amldo zirconium d1hydride, dimethylsllyl-±-ϋ-±-butylcyclopenta¬ dienyl-±ejr£-butylamido hafnium diphenyl, dimethylsilyltr1methyl- s1lylcyclopentad1enyl-±eχt-butylamido zirconium dihydride, dimethylsilyltetra ethylcydopentadlenylphenyl mido titanium dimethyl, dimethylsilyltetramethylcyclopentadienylphenylamldo hafnium dltolyl, methylphenylsilyltetramethylcyclopentadienyl- ±firt-butylamldo zirconium dihydride, methylphenylsilyltetra- methylcyclopentad1enyl-lsιt-butylamido hafnium dimethyl, d1methy1s11y1fluorenyl-cyc1ohexylam1de titanium dimethyl, d1phenylgermyl1ndenyl-t-butyl phosphldo dihydride, methylphenylsilyltetramethylcyclopentadlenyl-iert-butylamldo hafnium dimethyl, dimethylsllyltetramethylcyclopentadienyl-p-n- butylphenylamido zirconium d1hydr1de, dimethylsllyltetramethyl- cyclopentadlenyl-p-n-butylphenylamido hafnium ditrlmethylsilyl. For Illustrative purposes, the above compounds and those permuted from Table 1 do not include the neutral Lewis base ligand (L). The conditions under which complexes containing neutral Lewis base Ugands such as ether or those which form dimers is determined by the steric bulk of the ligands about the metal center. Similarly, due to the decreased steric bulk of the trlmethylsllylcyclopentadienyl group 1n [Me 2 Si(Me 3 S1C 5 H 3 )(N-i-Bu)ZrH 2 3 2 versus that of the tetramethylcyclopentadienyl group in Me 2 Si(Me 4 C 5 )(N-i-Bu)- ZrH 2 , the former compound 1s dimerle and the latter 1s not. Generally the bridged species of the Group IV B transition metal compound ("y"-l) are preferred. A preferred method of preparing these compounds is by reacting a cyclopentadienyl lithium compound with a dihalo-compound whereupon a lithium hallde salt Is liberated and a monohalo substituent becomes covalently bound to the cyclopentadienyl compound. The so substituted cyclopentadienyl reaction product 1s next reacted with a lithium salt of a phosphide, oxide, sulflde or amide (for the sake of Illustration, a lithium amide) whereupon the halo element of the monohalo substituent group of the reaction product reacts to liberate a lithium hallde salt and the amine moiety of the lithium amide salt becomes covalently bound to the substituent of the cyclopentadienyl reaction product. The resulting amine derivative of the cyclopentadienyl product 1s then reacted with an alkyl Hthlum reagent whereupon the labile hydrogen atoms, at the carbon atom of the cyclopentadienyl compound and at the nitrogen atom of the amine moiety covalently bound to the substituent group, react with the alkyl of the Hthlum alkyl reagent to liberate the alkane and produce a diHthlum salt of the cyclopentadienyl compound. Thereafter the bridged species of the Group IV B transition metal compound 1s produced by reacting the d1Hthlum salt cyclopentadienyl compound with a Group IV B transition metal preferably a Group IV B transition metal hallde. This procedure yields the d1chloro-der1vat1ve of the monocydopentadlenyl-amldo Group IV-B compound. The dlchlorlde complex 1s then converted Into the appropriate hydrocarbyl derivative using the corresponding Grignard, Hthlum, sodium or potassium salt of the hydrocarbyl ligand. The procedures used are analogous to those developed for alkylat ng the Group IV-B metallocene complexes (I.e., the bls- cyclopentadlenyl) systems). ϋnbrldged species of the Group IV B transition metal compound can be prepared from the reaction of a cyclopentadienyl lithium compound and a lithium salt of an amine with a Group IV B transition metal hallde. Suitable, but not limiting, Group IV B transition metal compounds which may be utilized 1n the catalyst system of this Invention include those bridged species ( M y H «l) wherein the B group bridge 1s a dlalkyl, dlaryl or alkylaryl silane, or βiethylene or ethylene. Examples of the more preferred species of bridged Group IV B transition metal compounds are dimethylsilyl, methylphenylsllyl, d1ethylsilyl, ethylphenylsllyl, dlphenylsllyl, ethylene or methylene bridged compounds. Most preferred of the bridged species are dimethyls1lyl, diethylsllyl and methylphenylsllyl bridged compounds. Suitable Group IV B transition metal compounds which are Illustrative of the unbrldged ( M y M -0) species which may be utilized In the catalyst systems of this Invention are exemplified by pentamethylcyclopentad1enyld1-i-butylphosph1nod1methyl hafnium; penta ethylcyclopentadlenyld1-t-butylphosphlnomethylethyl hafn1um; cydopentad1enyl-2-methylbutox1de dimethyl titanium. To Illustrate members of the Group IV B transition metal component, select any combination of the species 1n Table 1. An example of a bridged species would be dimethylsilyl- cyclopentad1enyl-i-butyl m1dod1methy1 zirconium; an example of an unbrldged species would be cyclopentadienyldi-i-butylam1dod1hydr1de zirconium. B. The Activator Component Compounds useful as an activator component in the prepara¬ tion of the catalyst of this invention will comprise a cation, which may be a Bronsted acid capable of donating a proton, and a compatible noncoordinating anlon which anlon 1s relatively large (bulky), capable of stabilizing the active catalyst species (the Group IV-B cation) which Is formed when the two compounds are combined and said anlon will be sufficiently labile to be displaced by oleflnlc, dloleflnlc and acetylenlcally unsaturated substrates or other neutral Lewis bases such as ethers, nitrlles and the like. Two classes of compatible non-coordinating anions have been disclosed In our European Patent Applications 277,003 and 277,004: 1) anlonlc coordination complexes comprising a plurality of HpophiHc radicals covalently coordinated to and shielding a central charge-bearing metal or metalloid core, and 2) anions comprising a plurality of boron atoms such as carboranes, metallacarboranes and boranes. In general, activator compounds containing single anionic coordination complexes which are useful in this Invention may be represented by the following general formula: C(L'-H) + ], | [( M' )m *0 1 Q a ...Q n 3 d" Wherein: L 1 is a neutral Lewis base; H is a hydrogen atom; [L'-H] is a Bronsted acid; M* 1s a metal or metalloid selected from the Groups subtended by Groups V-B to V-A of the Periodic Table of the Elements; I.e.. Groups V-B, VI-B, VII-B, VIII, I-B, II-B, III-A, IV-A, and V-A; Q χ to Q n are selected, Independently, from the Group consisting of hydride radicals, dialkylamido radicals, alkoxlde and aryloxide radicals, hydrocarbyl and substltuted-hydrocarbyl radicals and organometallold radicals and any one, but not more than one, of Q 1 to Q n may be a hallde radical, the remaining Q to Q n being, Independently, selected from the foregoing radicals; m 1s an integer from 1 to 7; n is an Integer from 2 to 8; and n - m - d. As indicated above, any metal or metalloid capable of forming an anionic complex which Is stable In water may be used or contained In the anlon of the second compound. Suitable metals, then, Include, but are not limited to, aluminum, gold, platinum and the like. Suitable metalloids include, but are not limited to, boron, phosphorus, silicon and the like. Compounds containing anions which comprise coordination complexes containing a single metal or metalloid atom are, of course, well known and many, particularly such compounds containing a single boron atom 1n the anlon portion, are available commercially. In light of this, salts containing anions comprising a coordination complex containing a single boron atom are preferred. The preferred activator compounds comprising boron may be represented by the following general formula: 5A. [L'H] + [BAr 1,Ar2X3X41 " Wherein: L' is a neutral Lewis base; H is a hydrogen atom; [L'-H] + is a Bronsted add; B is boron in a valence state of 3; Ar and Ar are the same or different aromatic or substituted-aromatic hydrocarbon radicals containing from about 6 to about 20 carbon atoms and may be linked to each other through a stable bridging group; and X j and X 4 are radicals selected, independently, from the group consisting of hydride radicals, hallde radicals, with the proviso that X f and X 4 will not be hallde at the same time, hydrocarbyl radicals containing from 1 to about 20 carbon atoms, substltuted-hydrocarbyl radicals, wherein one or more of the hydrogen atoms 1s replaced by a halogen atom, containing from 1 to about 20 carbon atoms, hydrocarbyl-substituted metal (organometallold) radicals wherein each hydrocarbyl substitution contains from 1 to about 20 carbon atoms and said metal is selected from Group IV-A of the Periodic Table of the Elements and the like. In general, Ar χ and Ar 2 may. Independently, be any aromatic or substituted-aromatic hydrocarbon radical containing from about 6 to about 20 carbon atoms. Suitable aromatic radicals Include, but are not limited to, phenyl, naphthyl and anthracenyl radicals. Suitable substituents on the substituted-aromatic hydrocarbon radicals, include, but are not necessarily limited to, hydrocarbyl radicals, organometalloid radical , alkoxy radicals, alkylamido radicals, fluoro and fluorohydrocarbyl radicals and the like such as those useful as X and X . The substituent may be ortho, meta or para, relative to the carbon atoms bonded to the boron atom. When either or both X and X are a hydrocarbyl radical, each may be the same or a different aromatic or substituted-aromatic radical as are Ar and Ar , or the same may be a straight or branched alkyl, alkenyl or alkynyl radical having from 1 to about 20 carbon atoms, a cyclic hydrocarbon radical having from about 5 to about 8 carbon atoms or an alkyl-substituted cyclic hydrocarbon radical having from about 6 to about 20 carbon atoms. X and X may also, independently, be alkoxy or dialkylamido radicals wherein the alkyl portion of said alkoxy and dialkylamido radicals contain from 1 to about 20 carbon atoms, hydrocarbyl radicals and organometalloid radicals having from 1 to about 20 carbon atoms and the like. As indicated above, Ar 1, and Ar2 may be linked to each other. Similarly, either or both of Ar and Ar could be Hnked to either X or X . Finally, X or X may also be linked to each other through a suitable bridging group. Illustrative, but not limiting, examples of boron compounds which may be used as an activator component in the preparation of the improved catalysts of this Invention are trlalkyl-substltuted ammonium salts such as triethylammonium tetra(phenyl)boron, tr1propylammonium tetra(phenyl)boron, tr1(n-butyl)ammonium tetra(pheny1)boron, trimethylammonium tetra(p-tolyl)boron, trlmethylammonium tetra(o-tolyl)boron, tr1butylammonium tetra(pentafluorophenyl)boron, tripropylammonium tetraCo,p-d1methylphenyl)boron, tr1butylammonium tetradn,m-d1methylphenyl)boron, tr1butylammonlum tetra(p-tri-f1uoromethylphenyl)boron, tr1(n-butyl)ammonium tetra(o-tolyl)boron and the like; N.N-dialkyl anilinium salts such as N,N-d1methylanilinium tetra(pentafluoro phenyDboron, N,N-d1ethylanl11n1um tetra(phenyl)boron, N,N-2,4,6-pentamethy1an1l1n1um tetra(phenyl)boron and the Hke; dialkyl ammonium salts such as did-propyl)ammonium tetra(pentafluorophenyl)boron, dlcyclohexylammonlum tetra(phenyl)boron and the Hke; and trlaryl phosphonium salts such as triphenylphosphonium tetra(phenyl)boron, tri(methylphenyl)phosphon1um tetra(phenyl)boron, tri(dimethylphenyl)phosphon1um tetra(phenyl)boron and the like. Similar lists of suitable compounds containing other metals and metalloids which are useful as activator components may be made, but such lists are not deemed necessary to a complete disclosure. In this regard, it should be noted that the foregoing list is not intended to be exhaustive and that other useful boron compounds as well as useful compounds containing other metals or metalloids would be readily apparent to those skilled in the art from the foregoing general equations. Activator components based on anions which contain a plurality of boron atoms may be represented by the following general formulae: 6. [L , -H] c [(CX) a )(M ,, X , ) m X , b 3 c" 7. [L'-H] d C[C( 3) a ,(M"X 4 ) mI (X 5 ) b ,] c" ] 2 M n+ ] d" wherein [L'-H] 1s a cation, e.g., H + , ammonium or a substituted ammonium cation having up to 3 hydrogen atoms replaced with a hydrocarbyl radical containing from 1 to about 20 carbon atoms or a substltuted-hydrocarbyl radical, wherein one or more of the hydrogen atoms 1s replaced by a halogen atom, containing from 1 to about 20 carbon atoms, phosphonium radicals, substituted-phosphonlum radicals having up to 3 hydrogen atoms replaced with a hydrocarbyl radical containing from 1 to about 20 carbon atoms or a substltuted-hydrocarbyl radical, wherein 1 or more of the hydrogen atoms 1s replaced by a halogen atom, containing from 1 to about 20 carbon atoms and the like; C Is carbon; H" 1s boron or phosphorus; each of X, X', X", X, X 4 and X § are radicals selected, independently, from the group consisting of hydride radicals, hallde radicals, hydrocarbyl radicals containing from 1 to about 20 carbon atoms, substltuted-hydrocarbyl radicals, wherein one or more of the hydrogen atoms 1s replaced by a halogen atom, containing from 1 to 20 carbon atoms, organometalloid radicals wherein each hydrocarbyl substitution In the organo portion contains from 1 to about 20 carbon atoms and said metal is selected from Group IV-A of the Periodic Table of the Elements and the like; M 1s a transition metal; "a" and "b" are integers > 0; "c" is an Integer > 1; a + b + c - an even-numbered Integer from 2 to about 8; and "m" 1s an integer ranging from 5 to about 22; "a"' and "b"* are the same or a different integer > 0; M c' H Is an integer > 2; a' + b* + c' ■ an even-numbered integer from 4 to about 8; "m 1 " 1s an integer from 6 to about 12; "n" 1s an integer such that 2c' - n » d; and M d" is an integer greater than or equal to 1. Illustrative, but not limiting, examples of second components which can be used in preparing catalyst systems utilized in the process of this invention wherein the anion of the second component contains a plurality of metalloid atoms (as in formulae 5 and 6) are ammonium salts such as ammonium 1-carbadodecaborate (using 1-carbadodecaborate as an illustrative, but not limiting, counterlon for the ammonium cations listed below): monohydrocarbyl-substltuted ammonium salts such as methylammonium 1-carbadodecaborate, ethylammonium 1-carbadodecaborate, propylammonium 1-carbadodecaborate, isopropylammonium 1-carbadodecaborate, (n-butyl)ammonium 1-carbadodecaborate, anilinium 1-carbadodecaborate, and (p-tolyl)ammonium 1-carbadodecaborate and the like; dihydrocarbyl-substituted ammonium salts such as dimethylammonium 1-carbadodecaborate, d1ethylammonium 1-carbadodecaborate, dipropylammonium 1-carbadodecaborate, diIsopropylammonium 1-carbadodecaborate, di(n-butyl) ammonium 1-carbadodecaborate, diphenylammonium 1-carbadodecaborate, d1(p-toly1)ammon1um 1-carbadodecaborate and the Hke; trihydrocarbyl-substituted ammonium salts such as trimethylammonium 1-carbadodecaborate, triethylammonium 1-carbadodecaborate, tripropyl-ammonium 1-carbadodecaborate, tr1(n-butyl) ammonium 1-carbadodecaborate, triphenylammonium 1-carbadodecaborate, tri(p-tolyl)ammon1um 1-carbadodecaborate, N,N-d1methylan1Hn1um 1-carbadodecaborate, N,N-d1ethylanilinium 1-carbadodecaborate and the like. Illustrative, but not limiting examples of second compounds corresponding to Formula 5 [using tr1(n-butyl)ammon1um as an Illustrative, but not limiting, counterlon for the anions listed below] are salts of anions such as bis[tri(n-butyl)ammon1um] nonaborate, b1s[tr1(n-butyl)ammon1um]decaborate, b1s[tr1(n-butyl) ammonium]undecaborate, b1s[tr1(n-butyl)ammonium] dodecaborate, bis[tri(n-butyl)ammon1um]decachlorodecaborate, tr1(n-butyl)ammon1um dodecachlorododecaborate, tri(n-butyl)ammonium 1-carbadecaborate, tri(n-butyl) ammonium 1-carbaundecaborate, tri(n-butyl)ammon1um 1-carbadodecaborate, tr1(n-butyl)ammon1um 1-trimethylsllyl-l-carbadecaborate, tr1(n-butyl)ammon1u-a d1bromo-1-carbadodecaborate and the Hke; borane and carborane complexes and salts of borane and carborane anions such as decaborane(14), 7,8-dicarbaundecaborane(13), 2,7-d1carbaundecaborane(13), undecahydr1do-7,8-dimethyl-7,8-d1carbaundecaborane, dodecahydr1do-l1-methyl-2,7-di-carbaundecaborane, tr1(n-butyl) ammonium undecaborate(14), tri(n-butyl)ammon1um 6-carbadecaborate(12), tri(n-butyl)ammonium 7-carbaundecaborate(13), tri(n-butyl)ammonium 7,8-d1carbaundecaborate(12), tr1(n-butyl)ammon1um 2,9-dicarbaundecaborate(12), tri(n-butyl)ammon1um dodecahydr1do-8-methyl-7,9-dicarbaundecaborate, tr1(n-butyl)ammonium undecahydrldo-8-ethy1-7,9-dicarbaundecaborate, tri(n-butyl) ammonium undecahydrldo-8-butyl-7,9-dicarbaundecaborate, tri(n-butyl)ammonium undecahydrldo-8-allyl-7,9-dicarbaundecaborate, tri (n-butyl) ammonium undecahydrl do-9-tri methyl sllyl -7 , 8-d1 carbaundecaborate , tr1 ( n-butyl )ammon1 um undecahydrl do-4 , 6-d1 bromo-7-carbaundecaborate and the Hke; boranes and carboranes and salts of boranes and carboranes such as 4-carbanonaborane(14), 1 ,3-d1carbanonaborane(l3), 6 , 9-di carbadecaborane( 14) , dodecahydr 1 do-1 -phenyl -1 , 3-di carbanonaborane , dodecahydrl do-1 -methyl -1 , 3-di carbanonaborane , undecahydr1do-l,3-d1methyl-l,3-dicarbanonaborane and the like. Illustrative, but not limiting, examples of second compounds corresponding to Formula 7 [using trK n-butyl) ammonium as an Illustrative, but not limiting, counterion for the anions listed below] are salts of metal lacarborane and metal laborane anions such as tri (n-butyl) ammonium b1s(nonahydrido-l ,3-dicarbaunaborato) cobaltate(III), trK n-butyl) ammonium bi s ( undeca-hydri do-7 , 8-di carbaundecaboratof errate( I II), trK n-butyl ) am oni um bl s(undecahydrido-7 , 8-di carbaundecaborato)cobal tatedll ) , tri (n-butyl )ammoni um bi s(undecahydri do-7 , 8-di carbaunaborato) nlkelate(III), tri (n-butyl )ammonium bis(nonahydr1do-7, 8-di methyl 1 -7 , 8-di carbaundecaborato) f errate( I II), tri ( n-butyl ) ammoni um b1s(nonahydr1do-7, 8-di methyl 1-7, 8-di carbaundecaborato)chromate(III), tr1 (n-butyl ) ammonium b1s(tribromooctahydr1do-7, 8-di carbaundecaborato) cobal tatedll), tr1 (n-butyl )ammonium bis(dodecahydrldodicarbadodecaborato) cobal tatedll), tr1s[ tri (n-butyl) ammonium] bis (undecahydrido-7-carbaundecaborato)chromate(III) , b1 s[tr1 (n-butyl ) ammonium] b1s(undecahydrido-7-carbaundecaborato)manganate(IV), b1 s [ tri (N-butyl ) ammoni um] bl s( undecahydrl do-7-carbaundecaborato) cobal tatedll), b1s[tr1 (n-butyl) ammonium] b1s( undecahydrl do-7-carbaundecaborato) nlckelate(IV) and the like. A similar list of representative phosphonium compounds can be recited as Illustrative second compounds, but for the sake of brevity, it is simply noted that the phosphonium and substHuted-phosphonlum salts corresponding to the listed ammonium and substituted-ammonium salts could be used as second compounds In the present Invention. Process of Catalyst Preparation The catalyst systems employed in the method of the Invention comprise a complex formed upon admixture of the Group IV-B transition metal component with the activator component. The catalyst system may be prepared by addition of the requisite Group IV-B transition metal and activator components to an inert solvent in which olefin polymerization can be carried out by a solution polymerization procedure. The catalyst system may be conveniently prepared by placing the selected Group IV-B transition metal component and the selected activator component, in any order of addition, in an alkane or aromatic hydrocarbon solvent — preferably toluene. The catalyst system may be separately prepared, 1n concentrated form, and added to the polymerization diluent 1n a reactor. Or, If desired, the components of the catalyst system may be prepared as separate solutions and added to the polymerization diluent in a reactor, in appropriate ratios, as 1s suitable for a continuous liquid polymerization reaction procedure. Alkane and aromatic hydrocarbons suitable as solvents for formation of the catalyst system and also as a polymerization diluent are exemplified by, but are not necessarily limited to, straight and branched chain hydrocarbons such as Isobutene, butane, pentane, hexane, heptane, octane and the like, cyclic and allcyclic hydrocarbons such as cyclohexane, cycloheptane, methylcyclohexane, methyleyeloheptane and the like, and aromatic and alkyl-substituted aromatic compounds such as benzene, toluene, xylene and the Hke. Suitable solvents also Include liquid olefins which may act as monomers or comonomers ncluding ethylene, propylene, butene, 1-hexene and the like. In accordance with this invention optlmuα results are generally obtained wherein the Group IV-B transition metal compound Is present in the polymerization diluent in concentration of from about 0.01 to about 1.0 millimoles/liter of diluent and the activator component 1s present in an amount to provide a molar ratio of the transition metal to activator component from about 1:1 to about 200:1. Sufficient solvent should be employed so as to provide adequate heat transfer away from the catalyst components during reaction and to permit good mixing. The catalyst system ingredients — that 1s, the Group IV-B transition metal and activator components, and polymerization diluent can be added to the reaction vessel rapidly or slowly. The temperature maintained during the contact of the catalyst components can vary widely, such as, for example, from -10* to 300 # C. Greater or lesser temperatures can also be employed. Preferably, during formation of the catalyst system, the reaction 1s maintained within a temperature of from about 25 * to 100 # C, most preferably about 25*C. At all times, the Individual catalyst system components, as well as the catalyst system once formed, are protected from oxygen and moisture. Therefore, the reactions are performed 1n an oxygen and moisture free atmosphere and, where the catalyst system is recovered separately, 1t is recovered 1n an oxygen and moisture free atmosphere. Preferably, therefore, the reactions are performed In the presence of an inert dry gas such as, for example, helium or nitrogen. The Catalyst System: Characterization and Properties of the Active SΔlS. The reaction of the two catalyst components can be viewed as a simple acid-base reaction where the Q " -ligand bound to the transi¬ tion metal center of (CN)HQ2 (where (CN) - Cp and J-ligands) re¬ acts with the cation of the second component,which may be acidic, [L'H + ][A] " (where A " is the non-coordinating anlon), to give the 1on1c catalyst [(CN)MQ + [A]~ and neutral biproducts 0-H and L'. The overall catalytic performance of the catalyst depends on the choice of metal, the specific (CN)-ligand set, the structure and stability of A " , and the coordinating ability of the cation or Lewis base L" . For conventional applications where a high productivity homopolymerization or random copolymerization catalyst is desired, the cation is a proton donor and the Q-ligand of the transition metal component is chosen so that: 1) the metal complex 1s easy to prepare and Is low cost, 2) (CN)HQ 2 1s sufficiently basic to deprotonate the a dle cation of the activator component, and 3) 0-H 1s an unreactlve biproduct such as an alkane so that the activation reaction 1s irreversible. For a particular (CN)H-system the L' and A~ portions of the activator component "tune" the stability and overall performance of the catalyst system. The ability of L* and A " to modify the behavior of a catalyst site increases the versatility of the polymerization system which is an important advantage over conventional methods of activation (e.g. methylalumoxane, and other aluminum alkyl cocatalysts). In general, and while most transition metal components Identified above may be combined with most activator components Identified above to produce an active olefin polymerization catalyst, 1t is Important for continuity of the polymerization operations that either the metal cation initially formed from the first component or a decomposition product thereof be a relatively stable catalyst. It is also Important that the anlon of the activator compound be stable to hydrolysis when an ammonium salt 1s used. Further, it is important that the positive charge of the activator component be sufficient, relative to the metal component, to facilitate the needed cation, e.g., proton transfer. Activator compounds containing aryl-ammonium salts such as N,N-dimethy1an111um are more acidic than tr1alkylammonium salts and therefore are useful with a wider variety of transition metal components. The basicity of the metal complex must also be sufficient to facilitate the needed proton transfer. In general, transition metal compounds which can be hydrolyzed by aqueous solutions can be considered suitable as metallocene components to form the catalysts described herein. With respect to the combination of the transition metal component with the activator component to form a catalyst of this invention, it should be noted that the two compounds combined for preparation of the active catalyst must be selected so as to avoid transfer of a fragment of the anlon to the metal cation, thereby forming a catalytically Inactive spedes. This could be done by steric hindrance, resulting from substitutions on the Cp- and/or J-Hgands of the first component, as well as substitutions on the non-coordinating anion. As the amount and size of the substitutions on the transition metal components are reduced, more effective catalysts are obtained with activator compounds containing non-coordinating anions which are larger In size and more resistant to degradation. In the case where the non-coordinating anion 1s an anionic coordination complex, such as a tetraphenylboron derivative, substitutions on the phenyl rings can be used to prevent the transfer of a proton or an entire phenyl group from the anion to the metal. This can be accomplished by alkyl substitution in the ortho positions of the phenyl groups, or, more preferably, by perfluoro-substltutions on the anlon. Thus, anionic coordination complexes containing perfluorphenyl-, tr1f1uoromethylphenyl-, or bis-tr1fluormethylphenyl rings are preferred for this subgenus of activator components. When the non-coordinating anion contains a plurality of boron atoms as described in general formulae 6 and 7, more effective catalysts are obtained with activator compounds containing larger anions, such as those encompassed by Equation 7 and those having larger m values in Equation 6. In these cases It is further preferable when using second compounds which are encompassed by Equation 6, that a + b + c - 2. Second compounds in which a + b + c « even-numbered integers of 4 or more have acidic B-H-B moieties which can react further with the metal cation formed, leading to catalytically Inactive compounds. Several new compositions of matter have been Identified using high field NMR spectroscopy. The reaction between Me 2 S1(Me 4 C 5 )(N-t-Bu)ZrMe 2 and [DMAH][B(pfp) 4 ] (where DMAH ♦ 8 - PhMe 2 NH and pfp - g F 5 ) In d -toluene produces a two phase system. The top layer is largely d -toluene with only a very small amound of DMA (DMA - PhNMe,) present. The lower layer 8 13 contains the 1on1c catalyst and d -toluene. The high field C NMR spectrum of the lower layer suggests the reaction proceeds to give the DMA-adduct as shown below. The NMR data clearly suggest that the amine is Indeed coordinated to the zirconium atom, but that it is fluxlonal and probably has two orientations of coordination, most likely in the form of rotational isomers. The Ionic catalysts species can be crystallized out at -40*C giving a pale powder. The solid state NMR spectrum of this material revealed amine coordination to the zirconium atom with more o than one orientation. Addition of d -thf (thf - tetrahydrofuran) o to the catalyst solution or solid produces the d -thf adduct, [Me 2 S1(Me 4 C 5 )(N-t-Bu)ZrMe(d 8 -thf) χ ][B(pfp) 4 ] and free DMA. This was expected since d -thf 1s a much stronger base than DMA. Ion-exchange activators with different basicities have also been investigated. An amine which 1s a stronger base than DMA, such as DMT (Me 2 N-p-Me-Ph) provides complete coordination to the zirconium atom with no fluxionallty. This catalyst was produced from the reaction of [DMTH][B(pfp) 4 ] with Me 2 S1(Me 4 C 5 )(N-t-Bu)ZrMe 2 . Very little, 1f any, free DMT was observed 1n the 13 C NMR spectrum of the catalyst solution. The use of [Bu 3 NH][B(pfp) 4 ] as the activator provided a more Interesting result. It appears that when Cn-Bu-NH][B(pfp) 4 ] is reacted with Me 2 S1(Me 4 C 5 )(N-t-Bu)ZrMe 2 , the amine does not coordinate to the zirconium atom as Illustrated In the equation below. The fact that the amine Is not coordinated to the metal Is evidenced by the fact that the chemical shift of the amine signals are unchanged from free-amine. From a purely electronic point of view one would predict that Bu^ would be a better Hgand for the cation!c metal center than DMA. The reverse 1s the case in this system Indicating that steric forces dominate the coordination chemistry. The observation of two Cp-methyl signals and one Me-Si-signal suggests that the cation is a symmetric three coordinate cation and that anlon and the amine Hgand to not coordination strongly with the metal to destroy the plane of symmetry through the metal, the Cp-centro1d, and the silicon atom. The reaction of Me 2 S1(Me 4 C 5 )(N-t-Bu)ZrMe 2 with [DMAH][(C 2 B g H.-) 2 Co] was also Investigated by high field NMR. In this case the amine, DMA, 1s not coordinated to the metal. The fact that one observes four Cp-methyl signals and two Me 9 S1 signals In the 13 C NMR spectrum suggests that the metal lacarborane I s coordinated to the metal center. This 1s consi stent with Its high solubility and low activity relative to the B(pfp) 4 system. Polymerization Process In a preferred embodiment of the process of this invention the catalyst system Is utilized In a liquid phase polymerization of an olefin monomer. The liquid phase process comprises the steps of contacting an olefin monomer with the catalyst system in a suitable polymerization diluent and reacting said monomer in the presence of said catalyst system for a time and at a temperature sufficient to produce a polyolefin. The monomer for such process may comprise ethylene alone, for the production of a homopolyethylene, or ethylene In combination with an α-olefin having 3 to 18 carbon atoms for the production of an ethylene-α-olefin copolymer. Conditions most preferred for the homo- or copolymerization of ethylene are those wherein ethylene 1s submitted to the reaction zone at pressures of from about 0.019 psi to about 50,000 ps1 and the reaction temperature 1s maintained at from about -100 * C to about 300'C, preferably -10* to 220'C. The mole ratio of transition metal component to activator component 1s preferably from about 1:1 to about 200:1. The reaction time 1s preferably from about 1 second to about 1 hour. Without limiting in any way the scope of the invention, one means for carrying out the process of the present Invention 1s as follows: 1n a stlrred-tank reactor liquid 1-butene monomer Is Introduced. The catalyst system Is Introduced via nozzles in either the vapor or liquid phase. Feed ethylene gas 1s Introduced either into the vapor phase of the reactor, or sparged Into the liquid phase as 1s well known 1n the art. The reactor contains a liquid phase composed substantially of liquid 1-butene together with dissolved ethylene gas, and a vapor phase containing vapors of all monomers. The reactor temperature and pressure may be controlled via reflux of vaporizing α-olefin monomer (autorefrlgeratlon), as well as by cooling colls, jackets, etc. The polymerization rate 1s controlled by the rate of catalyst addition, or by the concentration of catalyst. The ethylene content of the polymer product Is determined by the ratio of ethylene to 1-butene In the reactor, which Is controlled by manipulating the relative feed rates of these components to the reactor. Eamle? In the examples which Illustrate the practice of the Invention the analytical techniques described below were employed for the analysis of the resulting polyolefln products. Molecular weight determinations for polyolefin products were made by Gel Permeation Chromatography (GPC) according to the following technique. Molecular weights and molecular weight distributions were measured using a Waters 150 gel permeation chromatograph equipped with a differential refractive Index (DRI) detector and a Chromatix KMX-6 on-line light scattering photometer. The system was used at 135 * C with 1,2,4-tr1chlorobenzene as the mobile phase. Shodex (Showa Denko America, Inc.) polystyrene gel columns 802, 803, 804 and 805 were used. This technique Is discussed in "Liquid Chromatography of Polymers and Related Materials III", 0. Cazes, Editor, Marcel Dekker, 1981, p. 207 which 1s incorporated herein by reference. No corrections for column spreading were employed; however, data on generally accepted standards, e.g. National Bureau of Standards Polyethylene 1484 and anionically produced hydrogenated polyisoprenes (an alternating ethylene-propylene copolymer) demonstrated that such corrections on Mw/Mn (-MWD) were less than 0.05 units. Mw/Mn was calculated from elution time. The numberical analyses were performed using the commercially available Beckman/CIS customized LALLS software in conjunction with the standard Gel Permeation package, run on a HP 1000 computer. The following examples are intended to Illustrate specific embodiments of the invention and are not Intended to limit the scope of the Invention. All procedures were performed under an Inert atmosphere of helium or nitrogen. Solvent choices are often optional, for example, in most cases either pentane or 30-60 petroleum ether can be Interchanged. The choice between tetrahydrofuran (thf) and d1ethyl ether 1s more restricted, but in several reactions, either could be used. The lithiated amides were prepared from the corresponding amines and either n-BuL1 or MeLi. Published methods for preparing L1HCgMe 4 include CM. Fendrick et al. Oroanometalllcs.1,819 (1984) and F.H. Kohler and K.H. Doll, I * Naturtorsch.376, 144 (1982). Other lithiated substituted cyclopentadienyl compounds are typically prepared from the corresponding cyclopentadienyl Hgand and BuLI or MeL1, or by reaction of MeL1 with the proper solvene. ZrCl 4 and HfC1 4 were purchased from either Aldrich Chemical Company or Cerac. Amines, sllane and Hthlum reagents were purchased from Aldrich Chemical Company or Petrarch Systems. Activator components were prepared by known literature methods. EXAMPLES Synthesis of Mono-Cvclopentadienyl Complexes 1. Me 2 S1(C 5 Me 4 )(N-i-Bu)ZrMe 2 Part 1. Me 4 HC 5 L1 (10.0 g, 0.078 mol) was slowly added to a Me 2 S1Cl 2 (11.5 ml, 0.095 mol, in 225 ml of tetrahydrofuran (thf) solution). The solution was stirred for 1 hour to assure complete reaction. The thf solvent was then removed via a vacuum to a cold trap held at -196'C. Pentane was added to precipitate out the L1C1. The mixture was filtered through Cellte. The solvent was removed from the filtrate. Me 4 HC 5 S1Me 2 Cl (15.34 g, 0.071 mol) was recovered as a pale yellow liquid. Part 2. Me 4 HC 5 S1Me 2 Cl (10.0 g, 0.047 mol) was slowly added to a suspension of L1HN-i-Bu (3.68 g, 0.047 mol, -100 ml thf). The mixture was stirred overnight. The thf was then removed via a vacuum to a cold trap held at -196*C. Petroleum ether (-100 ml) was added to precipitate out the L1C1. The mixture was filtered through Cellte. The solvent was removed from the filtrate. Me 2 S1(Me 4 HC 5 )(HN-i-Bu) (11.14 g, 0.044 mol) was Isolated as a pale yellow liquid. Part 3. Me 2 S1(Me 4 HC 5 )(HN-i-Bu) (11.14 g, 0.044 mol) was diluted with -100 ml Et 2 0. MeLI (1.4 M, 64 ml, 0.090 mol) was slowly added. The mixture was allowed to stir for 1/2 hour after the final addition of MeL1. The ether was reduced 1n volume prior to filtering off the product. The product, [Me 2 S1(Me 4 C 5 )(N-i-Bu)]L1 2 , was washed with several small portions of ether, then vacuum dried. Part 4. [Me 2 S1(Me 4 C 5 )(N-i-Bu)]L1 2 (3.0 g, 0.011 mol) was suspended in -150 ml Et 2 0. Zrtt . (2.65 g, 0.011 mol) was slowly added and the resulting mixture was allowed to stir overnight. The ether was removed via a vacuum to a cold trap held at -196*C. Pentane was added to precipitate out the L1C1. The mixture was filtered through Cellte twice. The pentane was significantly reduced in volume and the pale yellow solid was filtered off and washed with solvent. Me 2 S1(Me 4 C 5 )(N-i-Bu)ZrCl 2 (1.07 g, 0.0026 mole) was recovered. Additional Me 2 Si(Me 4 C 5 )(N-i-Bu)ZrCl 2 was recovered from the filtrate by repeating the recrystallization procedure. Total yield, 1.94 g, 0.0047 mol). Part 5. Me 2 S1(C 5 Me 4 )(N-i-Bu)ZrMe 2 was prepared by adding a stoichiometric amound of MeLi (1.4 M in ether) to Me 2 S1(C 5 Me 4 )(N-i-Bu)ZrCl 2 suspended 1n ether. The white solid was isolated In an 83% yield. 2. MePhSi(C 5 Me 4 )(N-i-Bu)HfMe 2 Part 1. MePhSiCl 2 (14.9 g, 0.078 mol) was diluted with -250 ml of thf. Me 4 C 5 HL1 (10.0 g, 0.078 mol) was slowly added as a solid. The reaction solution was allowed to stir overnight. The solvent was removed via a vacuum to a cold trap held at -196*C. Petroleum ether was added to precipitate out the L1C1. The mixture was filtered through Cellte, and the pentane was removed from the filtrate. MePhSi(Me 4 C 5 H)Cl (20.8 g, 0.075 mol) was Isolated as a yellow viscous liquid. Part 2. L1HN-i-Bu (4.28 g, 0.054 mol) was dissolved 1n -100 ml of thf. MePhS1(Me 4 C 5 H)Cl (15.0 g, 0.054 mol) was added drop wise. The yellow solution was allowed to stir overnight. The solvent was removed via vacuum. Petroleum ether was added to precipitate out the L1C1. The mixture was filtered through Cellte, and the filtrate was evaporated down. MePhS1(Me 4 C 5 H)(NH-i-Bu) (16.6 g, 0.053 mol) was recovered as an extremely viscous liquid. Part 3. MePhS1(Me 4 C 5 H)(NH-i-Bu) (16.6 g, 0.053 mol) was diluted with -100 ml of ether. MeLI (76 ml, 0.106 mol, 1.4 M) was slowly added and the reaction mixture was allowed to stir for -3 hours. The ether was reduced in volume, and the Hthlum salt was filtered off and washed with pentane producing 20.0 g of a pale yellow solid formulated as L1 2 CMePhS1(Me 4 C 5 )(N-±-Bu)]-3/4Et 2 0. Part 4. L1 2 [MePhS1(Me 4 C 5 )(N-i-Bu)] » 3/4Et 2 0 (5.00 g, 0.0131 mol) was suspended 1n -100 ml of Et 2 0. HfCl 4 (4.20 g, 0.0131 mol) was slowly added and the reaction mixture was allowed to stir overnight. The solvent was removed via vacuum and petroleum ether was added to precipitate out the L1C1. The mixture was filtered through Celite. The filtrate was evaporated down to near dryness and filtered off. The off white solid was washed with petroleum ether. MePhS1(Me 4 C 5 )(N-i-Bu)HfCl 2 was recovered (3.54 g, 0.0058 mole). Part 5. MePhSi(Me 4 C 5 )(N-i-Bu)HfMe 2 was prepared by adding a stoichlometric amount of MeLI (1.4 M 1n ether) to MePhS1(Me 4 C 5 )(N-i-Bu)HfCl 2 suspended In ether. The white solid could be isolated in near quantitative yield. POLYMERIZATIONS Example 1. A catalyst solution prepared from 19.7 mg of Me 2 S1(Me 4 C 5 )(N-t-Bu)ZrMe 2 and 6 mg of [DMAH] [B(pfp) 4 ] 1n 20 mis of toluene was added to a 1 liter stainless-steel autoclave containing 400 mis of hexane. The reactor temperature was maintained at 40*C and stirred vigorously while ethylene was added at 90 psi. After 30 minutes the reaction was stopped giving 30 grams of HDPE after work-up. The GPC analysis showed a bimodal distribution with modes centered at 900,000 and 2,000. Example 2. A catalyst solution prepared from 28.6 mg of Me 2 S1(Me 4 C 5 )(N-t-Bu)ZrMe 2 and 9 mg of [DMAH] [B(pfp)] 4 1n 20 mis of toluene was added to a 1 liter stainless-steel autoclave containing 400 mis of hexane. The reactor temperature was set at 50'C and was stirred vigorously while 100 mis of butene and 60 ps1 of ethylene were added. Following the addition of butene and ethylene, an 1nstantan1ous Increase in temperature to 90 # C was observed. After 30 minutes the reaction was stopped, yielding 130 grams of a waxy ethylene-butene copolymer. 6PC analysis showed a bimodal distribution with modes centered at 27,000 and 2,000 in approximately equal ratios. IR spectroscopy showed the presence of butene in the copolymer. Example 3. A catalyst solution prepared from 40 mg of MePhS1 (C 5 Me 4 )(N-i-Bu)HfMe 2 and 11 mg of [DMAH] [B(pfp 4 ] in 20 mis of toluene was added to a 1 l iter autoclave containing 400 mis of hexane. The reactor temperature was set at 40*C, stirred vigorously and pressurized with ethylene (90 psD for 15 minutes . The reactor temperature increased from 40 to 97*C during the polymerization. The reactor was stopped and 98 grams of polyethylene was I solated having a Mw « 47.7K and a MWD - 3.0. Example 4. A catalyst solution prepared from 50 mg of Me 2 S1(C 5 Me 4 )(N-i-Bu)ZrMe 2 and 68 mg of [D AH][(C 2 B 9 H ) 2 Co] in 20 mis of toluene was added to a 1 liter autoclave containing 400 mis of hexane. The reactor temperature was set at 60*C, stirred vigorously and pressurized with ethylene (120 psD for 60 minutes. The reactor was stopped and 0.44 grams of polyethylene was Isolated having a Mw-538 and a MWD - 1.90.

Claims: CLAIMS: 1. A catalyst system for the production of polyolefins comprising: A. a Group IV-B transition metal component of one of the two general formulae I. wherein M i s Zr, Hf or Ti and i s 1n its highest formal oxidation state (+4, d complex) ; (CgHg R χ ) 1s a cyclopentadienyl ring which is substituted with from zero to five radical R groups, "x" is 1, 2,3, 4 or 5 denoting the degree of substitution, and each R 1s, and each substituent group R Is, independently, a radical selected from a group consisting of C j -C 2Q hydrocarbyl radicals, substituted ^1" C 20 hydrocarbyl radicals wherein one or more hydrogen atoms is replaced by a halogen atom, C,-C 2Q hydrocarbyl-substltuted metalloid radicals wherein the metalloid Is selected from the Group IV A of the Periodic Table of Elements, and halogen radicals; or (CrHD c —y w — W Rx„) 1s a cydopentadienly ring 1n which two adjacent R-groups are joined forming a 4 -C 2 Q ring to give a polycydlc element with a coordination number of two from Group VI-A of the Periodic Table of Elements, and each R' 1s, independently a radical selected from a group consisting of C j -C 20 hydrocarbyl radicals, substituted ^-^ ^ roc&r ^ radicals wherein one or more hydrogen atoms 1s replaced by a halogen atom, and "z" 1s the coordination number of the element 0; each 0 may be independently, hydride, C,-C- 0 hydrocarbyl radicals, substituted hydrocarbyl radicals wherein one or more hydrogen atoms is replaced by an electron-withdrawing group such as a halogen atom, or alkoxide radical, or C,-C« 0 hydrocarbyl-substltuted metalloid radicals wherein the metalloid 1s selected from the Group IV-A of the Periodic Table of Elements, provided that where any 01s a hydrocarbyl such Q 1s different from C 5 H 5-y-x R x ) * or botn 9 together may be an alkyHdene, olefin, acetylene or a cy o etallated hydrocarbyl; "y" Is 0 or 1; when "y" 1s 1, B 1s a covalent bridging group containing a Group IV A or V A element; "w" is a number from 0 to 3; and L is a neutral Lewis base; or L represents a second transition metal compound of the same type such that the two metal centers M and M' are bridged by Q and Q 1 , wherein M' has the same meaning as M and Q * has the same meaning as Q, as represented by the formula II; and B. an activator compound comprising (1) a cation (with or without a donatable proton) and (2) a labile, bulky anion which is either a single coordination complex having a plurality or lipophilic radicals covalently coordinated to and shielding a central charge-bearing metal or metalloid atom, or an anionic complex containing a plurality of boron atoms, the bulk of said anlon being such that upon reaction of the cation of the activator SUBSTITUTE SHEET compound with a cation reactable substituent of said Group IV-B transition metal so that a Group IV-B metal cation is formed, said anion is sterically hindered from covalently coordinating to the Group IV-B metal cation, and the lability of said anion is such that said anion is displaceable from said Group IV-B metal cation by an unsaturated hydrocarbon having a Lewis base strength equal to or greater than ethylene. 2. The catalyst system of claim 1 wherein the heteroatom l igand group 3 element 1 s nitrogen, phosphorous , oxygen or sulfur. 3. The catalyst system of claim 2, wherein "y" « s 1 and "B" i s a l inear, branched or cycl ic alkyl ene group having from 1 to 6 carbon atoms, an alkyl substi tuted si laalkylene group having from 1 to 2 silicon atoms in place of carbon atoms In the bridge, or a Sl -Sl j alkyl substituted sl lanylene group. 4. The catalyst system of claim 3 wherein the heteroatom l igand group J element I s nitrogen. 5. The catalyst system of claim 4 wherein "y" i s 1 and "B" i s an alkyl substituted silaalkylene group having from 1 to 2 si 11 cone carbon atoms In the bridge, or a SI , -SI, alkyl substituted sl lanylene group. 6. The catalyst system of claim 2, wherein said activator compound i s represented by the formula: [(L'-H) + ] d C(M , ) m *0 1 0 2 ..0 n ] d' herein: L* i s a neutral Lewis base; H I s a hydrogen atom; [L'-H] 1s a Bronsted add; M* I s a metal or metal loid selected from the subtended Groups V-B to V-A of the of the Periodic Table of the Elements; i .e.. Groups V-B. BI-B, VII-B, VIII , I-B, II-B. III-A. IV-A, and V-A; 0 1 to Q n are a, Independently, hydride, dialkylamido, alkoxide, aryloxlde, hydrocarbyl substltuted-hydrocarbyl and organometal loid radicals and any one, SUBSTITUTE SHEET but not more than one of 0. to Q may be a hallde radical; "m" is an Integer from 1 to 7; "n" is an Integer from 2 to 8; and n - - "d M . 7. The catalyst system of claim 6, wherein said activator compound 1s represented by the formula: CL'-H] + [BAr 1 AR 2 X 3 X 4 ] wherein: L' 1s a neutral Lewis base, H 1s a hydrogen atom, and CL'-H] + Is a Bronsted add; wherein: B is boron in a valence state of three; Ar j and Ar 2 are the same or different aromatic or substituted-aromatic hydrocarbon radicals which radicals may be linked to each other through a stable bridging group; and X, and X 4 , are Independently, a hydride, halide, hydrocarbyl, substltuted-hydrocarbyl, or an organometalloid radical. 8. The catalyst of claim 7, wherein said activator compound Is represented by the formula: wherein L' 1s a neutral Lewis base, H 1s a hydrogen atom, [L'H] 1s a Bronsted add, and B is a boron 1n a valence of 3+. 9. The catalyst system of claim 7 wherein the heteroatom Hgand group 0 element is nitrogen. 10. The catalyst system of claim 7 wherein M 1s zirconium. 11. The catalyst system of claim 7 wherein the cyclopentadienyl ring group contains four substituent R groups, "x" 1s 4. 12. The catalyst system of claim 7 wherein M 1s hafnium. 13. The catalyst system of claim 7 wherein the cyclopentadienyl group contains one substituent R group, "x" 1s 1. 14. The catalyst system of claim 6 wherein said*activator compound 1s represented by the formulae: [L'-H] c [(CX) a )(M"X') m X" b ] C" [L'-H] d [[(CX 3 ) a ,(M"X 4 ) |n ,(X 5 ) b ,] c -] 2 M n+ ] d - wherein [L'-H] is either H + , ammonium or a substituted ammonium cation having up to 3 hydrogen atoms replaced with a hydrocarbyl radical containing from 1 to about 20 carbon atoms or a substltuted-hydrocarbyl radical, wherein one or more of the hydrogen atoms 1s replaced by a halogen atom, containing from 1 to about 20 carbon atoms, phosphonium radicals, substituted-phosphonium radicals having up to 3 hydrogen atoms replaced with a hydrocarbyl radical containing from 1 to about 20 carbon atoms or a substltuted-hydrocarbyl radical, wherein 1 or more of the hydrogen atoms is replaced by a halogen atom, containing from 1 to about 20 carbon atoms and the Hke; C Is carbon; M" is boron or phosphorous; each of X, X', X", X 3 , X 4 and X g are radicals selected, independently, from the group consisting of hydride radicals, hallde radicals, hydrocarbyl radicals containing from 1 to about 20 carbon atoms, substltuted-hydrocarbyl radicals, wherein one or more of the hydrogen atoms 1s replaced by a halogen atom, containing from 1 to 20 carbon atoms, organometalloid radicals wherein each hydrocarbyl substitution 1n the organo portion contains from 1 to about 20 carbon atoms and said metal 1s selected from Group IV-A of the Periodic Table of the Elements and the like; M 1s a transition metal; "a" and "b" are Integers > 0; "c" 1s an Integer > 1; a + b ♦ c - an even-numbered Integer from 2 to about 8; and "m" 1s an Integer ranging from 5 to about 22; "a"* and "b'" are the same or a different Integer > 0; "c" is an Integer > 2; 'a ♦ b' + c' - an even-numbered Integer from about 4 to about 8; "ra" 1s an Integer from 6 to about 12; "n" is an Integer such that 2c' - n - d; and "d" Is an Integer greater than or equal to 1. 15. The catalyst of claim 14 wherein the activator component is represented by the following formula: [L'H] + [(C 2 B g H n ) 2 Co] " wherein L' is a neutral Lewis base, H is a hydrogen atom and [L'H] + is a Bronsted acid. 16. A composition of matter comprising the following general formula: wherein: M is Zr, Hf or Ti and is 1n its highest formal oxidation state (+4, d complex); (CgH j R χ ) 1s a cyclopentadienyl ring which is substituted with from zero to five substituent groups R, "x" 1s 0, 1, 2, 3, 4 or 5 denoting the degree of substitution, and each substituent group R is, Independently, a radical selected from a group consisting of -Cg Q hydrocarbyl radicals, substituted C j -Cg Q hydrocarbyl radicals wherein one or more hydrogen atoms 1s replaced by a halogen atom, C,-C 2 Q hydrocarbyl-substltuted metalloid radicals wherein the metalloid 1s selected from the Group IV A of the Periodic Table of Elements, and halogen radicals, or (CgHg R χ ) Is a cyclopentadienyl ring In which two adjacent R-groups are joined forming a 4 -C 2Q ring to give a polycycllc cyclopentadienyl ligand. (JR* , ) Is a heteroatom Hgand in which J Is an element with a coordination number of three from Group VA or an element with a coordination number of two from Group VI A of the Periodic Table of Elements, and each R' Is, Independently a radical selected from a group consisting of CJ-CJQ hydrocarbyl radicals, substituted C,-C 2Q hydrocarbyl radicals wherein one or more hydrogen atoms 1s replaced by a halogen atom, and "z" 1s the coordination of number of the element 0; each 0 may be Independently, hydride, j -C 50 hydrocarbyl radicals, substituted hydrocarbyl radicals wherein one or more hydrogen atom 1s replaced by an electron-withdrawing group such as a halogen atom, or alkoxide radical, or C,-C 5Q hydrocarbyl-substltuted metalloid radicals wherein the metalloid 1s selected from the Group IV-A of the Periodic Table of Elements, provided that where any Q 1s a hydrocarbyl such 01s different from (C 5 H 5-y-x R x 5, or botn together may be an alkyHdene, olefin, acetylene or a cyclometallated hydrocarbyl. "y" Is 0 or 1; when "y" 1s 1, B Is a covalent bridging group containing a Group IV A or V A element. L Is a neutral Lewis base; and "w" is a number from 0 to 3, [A] ' is a labile bulk anion which is either a single coordination complex having a plurality of LipophiHc radical covalently coordinated to and shielding a charge bearing metal or metalloid center or an anionic complex containing a plurality of boron atoms. 17. The composition of matter of claim 16 wherein [A] " 1s represented by the following general formula [(M') m+ Q.Q 2 ...Q n 3 d ~ wherein M' is a metal or metalloid selected from the Groups subtended by Groups V-B to V-A of the Periodic Table of the Elements; I.e., Groups V-B, VI-B, VII-B, VIII, I-B, II-B. III-A, IV-A, and V-A; Oi to Q_ are selected. Independently, from the Group consisting of hydride radicals, dialkylamido radicals, alkoxide and aryloxide radicals, hydrocarbyl and substltuted-hydrocarbyl radicals and organometalloid radicals and any one, but not more than one, of 0 1 to 0 n may be a hallde radical, the remaining Q j to Q n being, Independently, selected from the foregoing radicals; m Is an Integer from 1 to 7; n 1s an Integer from 2 to 8; and n - m - d. 18. The composition of matter of claim 16 wherein [A]~ 1s represented by the following general formula: ) b ,] c -] 2 M n+ ] d - C is carbon; M" is boron or phosphorous; each of X, X', X", X 3 , X 4 and X g are radicals selected, Independently, from the group consisting of hydride radicals, halide radicals, hydrocarbyl radicals containing from 1 to about 20 carbon atoms, substltuted-hydrocarbyl radicals, wherein one or more of the hydrogen atoms 1s replaced by a halogen atom, containing from 1 to 20 carbon atoms, organometalloid radicals wherein each hydrocarbyl substitution in the organo portion contains from 1 to about 20 carbon atoms and said metal is selected from Group IV-A of the Periodic Table of the Elements and the like; M is a transition metal; "a" and "b" are integers > 0; "x" is an Integer > 1; a + b + c « an even-numbered Integer from 2 to about 8; and "m" Is an integer ranging from 5 to about 22; "a'" and "b"* are the same or a different integer > 0; "c*" is an integer >2; a' + b* + c* - an even-numbered Integer from about 4 to about 8; "m'" 1s an Integer from 6 to about 12; "n M 1s an Integer such that 2c' - n - d; and "d" 1s an Integer greater than or equal to 1. 19. The composition of matter of claim 17 wherein [A] " is B(C 6 F 5 ) 4 -. 20. The composition of matter of claim 18 wherein [A] "" Is [(C 2 B g H ) 2 Co] " . 21. A composition of matter of formula 22. A method of producing a catalyst system of claim 1 which comprises admixing the Group IV-B transition metal component A and the activator compound B to form the desired catalyst system. 23. A catalyst system according to claim 1 or a method according to claim 22 wherein A and B are in a molar ratio of from 1:1 to 200:1. 24. A process for producing a homo- or co-polyolefin which comprises (co)polymerizing one or more olefinically unsaturated monomer(s) in the presence of a catalyst system according to any of claims 1 to 15 and 23 or a composition of matter according to any of claims 16 to 21. 25. A process according to claim 24 when performed in the liquid phase. 26. A process according to claim 24 or 25 wherein the catalyst system or composition of matter is introduced into the monomers per se or is formed in situ in the polymerization mixture.

Inventors: CANICH JOANN MARIE, HLATKY GREGORY GEORGE, TURNER HOWARD WILLIAM, CANICH, JOANN, MARIE, HLATKY, GREGORY, GEORGE, TURNER, HOWARD, WILLIAM
Applicants: EXXON CHEMICAL PATENTS INC, EXXON CHEMICAL PATENTS INC.
Application year: 1991
Main classification: C08F4
IPC codes: B01J31, C07F17, C08F4, C08F10, C08F110, C08F210