Non-hydrocarbon invert emulsion for use in well drilling operations

Abstract: Brine-in-glycol emulsions are shown for use as well working fluids. The fluids have a glycol external phase and a brine internal phase. The separate phases are emulsified to create an emulsion and weighted with traditional weighting agents. The external phase is soluble or dispersible in sea water when diluted upon discharge.

Description: This invention relates to a well bore fluid useful in drilling, completing or workover of oil and gas wells, and, specifically, to an invert emulsion type fluid having a non-hydrocarbon, non-mineral oil external phase and an aqueous internal phase which provides many of the advantages of an oil-based mud without the attendant adverse environmental effects. During the drilling of oil and gas wells, drilling fluid is circulated through the interior of the drill string and then back up to the surface through the annulus between the drill string and the wall off the borehole. The drilling fluid serves various purposes including lubricating the drill bit and pipe, carrying cuttings from the bottom of the well borehole to the surface of the ground, and imposing a hydrostatic head on the formation being drilled to prevent the escape of oil, gas or water into the well borehole during the drilling operations. Occasionally during drilling, the drill string becomes stuck and cannot be raised, lowered or rotated. There are numerous causes for this problem, one of the most common being differential sticking. Differential sticking usually occurs when drilling permeable formations and borehole pressures are greater than formation pressures and when the drill pipe remains at rest against the wall of the borehole for enough time to allow mud filter cake to build up around the pipe. The pressure exerted by drilling fluid then holds the pipe against the cake wall. For a number of years, oil-based fluids have been popular both as drilling fluids and as stuck pipe fluids. These fluids typically are comprised of a hydrocarbon oil or oils as the major component of the liquid phase to which various materials are added to impart the desired drilling fluid properties. These fluids are well adapted for use in underground formations containing water sensitive clays or shales which swell and disintegrate when contacted by water-based drilling fluids. Such fluids are substantially free of water, lose mostly oil as the filtrate and cause no swelling or disintegration of water sensitive clays and shales. One widely used oil-base fluid is described in U.S. Patent No. 3,099,624. Water-in-oil emulsions are also used as drilling fluids. These fluids contain a high percentage of oil and a lesser percentage of water dispersed in the continuous or external phase of oil. In order to free stuck pipe, prior art treatments involve the placement in and movement through the circulating mud system of a volume of a release agent, known as a spotting fluid, which is sufficient to fully contact the region of the borehole where the pipe is stuck. Thus, a suitably weighted oil-based fluid is circulated in the borehole to a position opposite the stuck interval. Over a period of time, the integrity of the mud filter cake between the drill pipe and borehole is reduced, allowing pressure equalization on all sides of the pipe. The invasion of oil into the filter cake is also thought to reduce the adhesive forces and lubricate the area between the pipe and borehole, resulting in less friction and quicker release. Oil-based formulations used in the past as spotting fluids are described, for instance, in U.S. Patent Nos. 4,436,638 and 4,464,269. Water-based formulations are also known for use in releasing differentially stuck pipe. They are described, for instance, in U.S. Patent Nos. 3,233,622; 4,230,587; 4,466,486; and 4,614,235. To our knowledge, invert emulsions having a non-hydrocarbon, non-mineral oil external phase and an aqueous internal phase have not been utilized. Environmental regulations have recently either prohibited or severely limited the use of oil-based and invert emulsion oil minds as either drilling fluids or as spotting fluids. In many offshore areas, such as the Gulf of Mexico, the use of oil muds is strictly regulated. Restrictive regulations have thus created a need for a novel fluid which will fill the niche formerly occupied by oil muds, i.e., drilling fluids for active argillaceous formations, and spotting fluids used to release drill pipe held by differential pressure. WO 89/01491 discloses a base fluid consisting of 5-100% by volume of 1,2-propanediol which is used for the production of various fluids to be used in drilling, completion, work-over and stimulation of wells drilled for petroleum sources. US-A-4230587 discloses an additive composition effective in the release or stuck pipe in a bore hole during a drilling operation. The present invention has as its object to provide such a replacement fluid for an oil-base mud which has significant advantages over water-based fluids when used in the before mentioned well bore operations, such as improved hole stability, bit lubrication, which minimizes hydration and dispersion of shale within the circulating fluid system, which will perform the function of an oil-based spotting fluid but which does not leave a sheen upon receiving waters and which meets current environmental toxicity standards, thereby eliminating environmental problems caused by oil-based fluids. Said object is achieved by a well bore fluid comprising a brine-in-glycol invert emulsion having a glycol external phase and a brine internal phase, the glycol external phase having a molecular weight in the range from 250 to 1000, a cloud point in the range from 15 to 83°C and being soluble or dispersible in sea water at a salinity of 3% and lower; an emulsifier; and a weighting agent. The present invention also relates to a method of preparing said well bore fluid comprising forming a brine-in-glycol invert emulsion having a glycol external phase and a brine internal phase by combining a brine solution with a glycol having a molecular weight in the range from 250 to 1000, a cloud point in the range from 15 to 83°C and being soluble or dispersible in sea water at a salinity of 3% and lower, thereby rendering the external phase and internal phase immiscible; adding an emulsifier to form an emulsion; and adding a weighting agent to the emulsion to form a weighted well bore fluid, as well as to a method of drilling a well which comprises circulating said well bore fluid in said well. The brine-in-glycol emulsion can be utilized as a spotting fluid for a stuck drill string by incorporating the brine-in-glycol emulsion into a conventional drilling fluid and contacting the borehole zone contiguous to the stuck drill string with the spotting fluid. This is accomplished by circulating the spotting fluid to the borehole zone contiguous to the stuck drill string. The well bore fluids of the invention are invert emulsions which have a glycol external or "continuous" phase and a brine internal phase. The term "emulsion" is commonly used to describe systems in which water is the external or continuous phase and, e.g., oil is dispersed within the external phase. By the term "invert" is meant that the glycol substance is the continuous or external phase and that the aqueous fluid is the internal phase. THE EXTERNAL PHASE The glycol external phase can be any glycol as defined in claim 1 and which forms a stable emulsion with the internal phase, which is less toxic than invert hydrocarbon oil emulsions, which does not leave a sheen upon receiving waters, i.e. , is water soluble or dispersible upon discharge at surface temperature and pressure conditions, as will be presently explained. The material selected for the external phase can be any glycol which is otherwise compatible with the purposes of the invention, as will be explained. The preferred materials for the external phase are selected from the group consisting of polypropylene glycols, polypropylene glycol ethers, and propylene oxide polymeric adducts of alcohols or mixtures of alcohols. Polypropylene glycol and propoxylated tripropylene glycol bottoms are particularly preferred. The molecular weight of these compounds is in the range from 250 to 1000. The molecular weight of the selected material is such that the material is soluble or dispersible in sea water at a salinity of 3% and lower but which is substantially insoluble in a brine such as 20 to 23% (saturated) sodium chloride solution, whereby a stable emulsion can be formed without the selected material forming a homogeneous solution with the aqueous phase. In selecting a candidate material for the external phase, the characteristic "cloud point" of the material provides an indication of its molecular weight and thus of its ability to form a stable emulsion. The cloud point of the candidate material is in the range from 15 to 83°C (59-181°F) for a tent solution comprising at least 1% by weight of the candidate material. The "cloud point" for the candidate material can be determined by preparing a fluid comprising at least 1% by volume of the candidate material in deionized water or salt solution and heating the fluid until it first becomes cloudy. The cloud point is that temperature at which the material begins to come out of solution, thereby becoming immiscible in water and behaving in the nature of a free oil. Particularly preferred materials for the external phase include polypropylene glycol having a cloud point of 50°C (122°F), supplied commercially as ARNOX D-400 by Baker Performance Chemicals and propoxylated tripropylene glycol bottoms having a cloud point in the range from 25-71°C (77-160°F). The most preferred molecular weight range for these materials is 250-600 for the polypropylene glycol and 600-1000 for the propoxylated tripropylene glycol bottoms. The preferred propylene oxide polymeric adducts are condensates of propylene oxide and optionally ethylene oxide with alcohols and include ethylene oxide-propylene oxide block copolymers of alcohol mixtures represented by the structural formula: wherein R represents an alkyl group of from 4-12 carbon atoms and x is an integer from 0 to 10, y is an integer from 5 to 20, and z is an integer from 5 to 25. This preferred class of material can be obtained from Olin Chemicals under the trade name "POLY-TERGENT". The propylene oxide adducts also include ethylene oxide-propylene oxide random copolymers of alcohols or alcohol mixtures having a structural formula: wherein R represents an alkyl group of from 1-10 carbon atoms, n is an integer in the range from 3-10 and m is an integer in the range from 0-10. This preferred class of materials can be obtained from BASF Wyandotte Corporation under the trade name "PLURACOL W". The polypropylene glycol ethers fall within a class of the general formula: wherein R₁ represents hydrogen or a lower alkyl group of from 1 to 8 carbons, R₂ represents a lower alkyl group of from 1 to 8 carbons, R₃ represents hydrogen, methyl and ethyl and n represents an integer of 1 to 16, preferably 1 to 5. Included in this class are the methyl monoether of propylene glycol, ethyl monoether of propylene glycol, propyl monoether of propylene glycol, methyl monoether of dipropylene glycol and the ethyl monoether of dipropylene glycol. Recent environmental regulations for offshore drilling fluids require that: (1) no "sheen" be left upon the receiving waters by the drilling fluid; and (2) that the drilling fluid meet stringent toxicity limits as measured by bioassays of Mysidopsis bahia shrimp. The Generic muds to be used with the Mysidopsis bioassay are described in T.W. Duke et al., "Acute Toxicity of Eight Laboratory Prepared Generic Drilling Fluids to Mysids", 1984, EPA 600, 3-84-067. The Mysid shrimp bioassay measure of toxicity, or LC50, is the lethal concentration to kill 50% of the Mysid shrimp population. Preferably, the lethal concentration of a 10% by volume candidate weighted external phase material in a generic mud, as measured by Mysidopsis bahia bioassay LC50 analysis, should be greater than about 30,000 parts per million for a suitable candidate material. It is also necessary that the external phase not "leave a sheen on receiving waters" upon discharge. That is, the brine-in-glycol invert emulsion, when diluted with sea water upon discharge is water soluble or dispersible and leaves no oil-like sheen. Thus, the candidate material must be immiscible in brine at a salinity of more than 3% but is soluble or disperslble in sea water when salinity is 3% or lower. THE INTERNAL PHASE The brine used in forming the internal phase can be defined as an aqueous solution containing from 100 to 350,000 parts per million metal ions such as lithium, sodium, potassium, magnesium, or calcium ions. The preferred brines used to form the internal phase of the emulsions of the invention contain from 10 to 23% (saturated) by weight sodium chloride and may contain various amounts of other dissolved salts such as sodium bicarbonate, sodium sulfate, sodium acetate, sodium borate, potassium chloride, or calcium chloride. The ratio of brine to glycol in the emulsions of the invention should generally provide as high a brine content as possible while still maintaining a stable emulsion since a high water content drilling fluid is less expensive and less objectionable to work with than a drilling fluid containing a low water content. Glycol/brine ratios in the range from 82:18 to 55:45 have been found to work satisfactorily, depending upon the particular glycol chosen. Thus the water content of a typical drilling fluid according to the invention will have an aqueous (water) content of 5 to 50 volume percent, with the most preferred range being 20 to 40 volume percent, most preferably 30 volume percent of the drilling fluid. THE EMULSIFIER In order to form a stable emulsion, a surfactant or emulsifier is added to the external, the internal or both phases. The emulsifier can be any of a number of organic acids which are familiar to those skilled in the art, including the monocarboxyl alkanoic, alkenoic, or alkynoic fatty acids containing from 2 to 22 carbon atoms, and mixtures thereof. Examples of this group of acids include acetic, stearic, oleic, caproic, capric, butyric, behenic, palmitic, arachidic, myristoleic, palmitoleic, elaidic, linoleic, linolenic, elaceostearic, and tarinic. Adipic acid, a member of the aliphatic dicarboxylic acids can also be used. The preferred surfactants or emulsifiers are fatty acids, fatty acid mixtures, lecithin and lime. Fatty acid calcium salts are also preferred. Lecithin is a mixture of the diglycerides of stearic, palmitic and oleic acids, linked to the choline ester of phosphoric acid. It is commercially available and is obtained from egg-yolk and soya beans. VISCOSIFIERS Viscosifiers can also be added to improve the solids suspending ability of the wall bore fluid. Suitable viscosifiers include the commercially available organophilic clays, bentonites, attapulgite clays, sepiolite, guar, carboxymethyl guar, hydroxypropyl guars, fumed silicas and fumed alumina. Preferred viscosifiers include sepiolite, attapulgite, organophilic clay and treated fumed silica. WEIGHTING AGENTS Weighting material are also used to weigh the well bore fluids of the invention to a density in the range from 1.0 to 180 g/cm³ (8.33 pounds per gallon to 15 pounds per gallon) and greater. Weighting materials which are known in the art include barite, ilmenite, calcium carbonate, iron oxide and lead sulfide. The preferred weighting material is commercially available barite. Three exemplary formulations follow which have produced weightable, stable emulsions. These formulations are based on three different suspending agents - sepiolite, organophillic clay, and treated fumed silica. The method of forming these three types of glycol emulsions can be briefly described as follows: (1) Sepiolite Formulation Salt water (20% aqueous sodium chloride) is viscosified by mixing sepiolite with the salt water in a blender. The brine/sepiolite slurry is added to a blend of polypropylene glycol, crude tall oil fatty acid, lecithin (CLEARATE B-60 from W.A. CLEARY CORP.) and lime. The combined mixture is blended vigorously to produce an invert emulsion. Preferably, the emulsion is prepared using a high glycol-to-brine ratio such as 82:18. The glycol/brine ratio may be reduced to 55:45 by the addition of 20% (aq) sodium chloride. (2) Organophilic Clay Formulation A mixture of polypropylene glycol, crude tall oil fatty acid, lecithin (CLEARATE B-60 from W.A. CLEARY CORP.) and lime is mixed for several minutes in a blender. Organophilic clay is added and the mixture is blended at high shear for ten minutes. Salt water is then added during high shear to produce the emulsion. Barite must be added immediately to maintain the emulsion. (3) Treated Fumed Silica Formulation Propoxylated tripropylene glycol bottoms, molecular weight around 600, is viscosified with a treated fumed silica (CAB-O-SIL TS - 610 from CABOT CORP.). This glycol has a relatively low cloud point of 26°C (78°F) (50% solution in deionized water). A typical formulation includes crude tall oil fatty acid, lime, and 20% (aq) sodium chloride. Glycol/brine ratios range from 60/40 to 80/20. Preparation requires moderate shear, and emulsions are stable without barite. Rheological properties of the brine-in-glycol emulsions were measured with a Fann 35 Viscometer following API RP 13B. Most samples were aged statically and sometime dynamically at 66°C (150°F). The following examples are intended to be illustrative of the invention. EXAMPLE I A brine-in-glycol emulsion with a glycol/brine ratio of 82:18 (Table 1) was made by first preparing a sepiolite/brine suspension by mixing a sepiolite/20% (aq) sodium chloride slurry for several minutes in a bar mixer or blender. The sepiolite suspension was then added to a mixture of polypropylene glycol 400 (cloud point 50°C (122°F) for 50% in deionized water), crude tall oil fatty acid, CLEARATE B-60 (W.A. CLEARY CORP.) and lime, and shearing the mixture for several minutes to emulsify the brine. Higher brine content emulsions were prepared by adding while mixing 20% (aq) sodium chloride to produce 70:30 and 55:45 brine-in-glycol emulsions. The densities of the 55:45, 70:30, and 82:18 emulsions were increased by the addition of barite. Rheological properties of these emulsions are listed in Tables 2 and 3. FORMULATION AND 49°C (120°F) RHEOLOGY OF 12 PPG BRINE-IN-GLYCOL EMULSION Example IB IC PPG/Brine Ratio, v/v 55/45 82/18 Formulation Emulsion, g 334 334 Barite, g 169 179 Rheology at 49°C (120°F) AV,Pa.s (cP) 0.113 (113) 0.0565 (56.5) PV,Pa.s (cP) 0.085 (85) 0.056 (56) YP,Pa(lb/100 ft²) 26.8 (56) 0.5 (1) 10 Sec Gel,Pa (lb/100 ft²) 5.7 (12) 0.9 (2) 10 Min Gel,Pa (lb/100 ft²) 7.7 (16) 1.4 (3) FORMULATION AND 49°C (120°F)RHEOLOGY OF WEIGHTED 70:30 BRINE-IN-GLYCOL EMULSIONS Example ID IE IF Density, g/cm³ (lb/gal) 1.44 (12) 1.68 (14) 1.80 (15) Formulation 70:30 Emulsion, g 326 298 284 Barite, g 177 289 345 Rheology at 49 °C (120°F) Av,Pa.s (cP) 0.0865 (86.5) 0.116 (116) 0.1435 (143.5) PV,Pa.s (cP) 0.079 (79) 0.099 (99) 0.120 (120) YP,Pa (lb/100 ft²) 7.2 (15) 16.3 (34) 22.5 (47) 10 Sec Gel,Pa (lb/100 ft²) 1.9 (4) 3.8 (8) 6.7 (14) 10 Min Gel,Pa (lb/100 ft²) 2.4 (5) 5.7 (12) 10.5 (22) EXAMPLE II In order to evaluate the emulsions of the invention as drilling fluids, approximately 110 l (29 gallons) of 56:44 brine-in-glycol emulsion containing 4% (v/v) REV-DUST to simulate the effects of drill cuttings, and having a density of 1.14 g/cm³ (9.50 lb/gal) were prepared for microbit drilling tests. An 82:18 (glycol/brine) emulsion was made by the addition of a previously prepared sepiolite-in-brine suspension to a mixture of polypropylene glycol 400, crude tall oil fatty acid, CLEARATE B-60, and lime. The fluid was stirred vigorously with two Dispersators for approximately 30 minutes. The 82:18 emulsion was cut to a 56:44 glycol/brine emulsion by adding more 20% (aq) sodium chloride. The fluid was completed by the addition of 102.7 g/l (36 lb/bbl) (4% by volume) REV-DUST. Ingredients used to make the glycol emulsion are listed in Table 4. Properties of the glycol emulsion are contained in Table 5. PROPERTIES OF MICRO-BIT TEST FLUIDS Example IIA Example IIB Density, g/cm³ (lb/gal) 1.14 (9.5) 1.14 (0.5) PV,Pa.s (cP) 0.013 (13) 0.075 (75) YP,Pa (lb(100 ft²) 2.4 (5) 25.4 (53) 10 Sec Gel,Pa (lb/100 ft²) 1.0 (2) 3.4 (7) 10 Min Gel,Pa (lb/100 ft²) 4.3 (9) 4.3 (9) The invert glycol emulsion was used in a microbit drilling testor to measure the ability of glycol emulsions to reduce bit bailing on a polycrystalline diamond (PDC) bit when drilling a Pierre shale core. Tests were run on a lignosulfonate fluid for comparison to the performance of the invert glycol emulsion. A formulation and properties of the lignosulfonate mud are listed in Tables 4 and 5 respectively. Tests were conducted using a 2-cutter PDC microbit (2.86 cm (1.125" O.D.)) equipped with two 0.24 cm (0.094" O.D.)) nozzles. Rotary speed was kept constant at 103 rev/min, and rate of penetration was kept at 762 to 914 cm/h (25 to 30 ft/h). Maximum flow rate was 56.8 l/min (15 gal/min). During the evaluation of each fluid, flow rate was reduced until bit balling was observed. Under the same experimental conditions, a fluid that prevents bit bailing at a lower flow is considered to be more effective than a fluid that requires a higher flow rate to keep the bit clean. The test results in Table 6 indicate that when the glycol emulsion fluid was used, extensive balling occurred when the flow rate was reduced to 12.1 l/min(3.2 gal/min). In contrast to the relatively low flow rate required for bit cleaning while drilling with the glycol emulsion, extensive bit balling was observed with the lignosulfonate mud using a flow rate as high as 49.2 l/min (13 gallon/minute). MICRO-BIT TEST RESULTS Flow Rate l/min (gal/min) Observed Balling Example IIA (Invert Glycol Emulsion) Example IIB (Lignosulfonate Mud) --- moderate 56.8 (15) --- extensive 49.2 (13) none extensive 41.6 (11) slight extensive 34.1 (9) none --- 15.1 (4) none --- 13.2 (3.5) extensive --- 12.1 (3.2) EXAMPLE III Brine-in-glycol emulsions can be prepared by adding 20% (aq) sodium chloride to a mixture of PPG 300 (cloud point of 71°C (159°F) for 50% solution in deionized water) or PPG 400, tall oil, lecithin (CLEARATE B-60), and lime. First, an organophilic clay such as Bentone SD-1, SD-2, SD-3, or EW (NL Chemicals) is added to a mixture of polypropylene glycol, tall oil, lecithin, and lime. The mixture is sheared for approximately ten minutes with a blender on high speed. Next, aqueous sodium chloride is added with vigorous mixing for several minutes. Finally, barite is added and the emulsion is mixed for several minutes to insure adequate suspension of the barite. These brine-in-glycol emulsions are not stable until solids such as barite are added. Formulations for these emulsions are listed in Tables 7 and 9 while rheological properties of these emulsions are listed in Tables 8 and 10. FORMULATIONS FOR 12 PPG, 70:30 PPG-400 EMULSIONS Example IIIA IIIB IIIC IIID PPG 400, g 237 237 237 237 Tall Oil, g 5 5 5 5 CLEARATE B-60, g 5 5 5 5 Lime, g 4 4 4 4 Organophilic Clay, g 8 SD-1 8 SD-2 8 SD-3 8 EW 20% (aq) NaCl, ml 100 100 100 100 Barite, g 198 198 198 198 49°C (120°F) RHEOLOGY OF 12 PPG, 70:30 PPG 400 EMULSIONS AFTER 16 H STATIC AGING AT 66°C (150°F) Example IIIA IIIB IIIC IIID AV,Pa.s (cP) 0.0765 (76.5) 0.084 (84) 0.0895 (89.5) 0.0755 (75.5) PV,Pa.s (cP) 0.063 (63) 0.069 (69) 0.070 (70) 0.052 (52) YP,Pa (lb/100 ft²) 12.9 (27) 14.4 (30) 18.7 (39) 22.5 (47) 10 Sec Gel, Pa (lb/100 ft²) 2.4 (5) 2.4 (5) 2.9 (6) 1.9 (4) 10 Min Gel, Pa (lb/100 ft²) 3.4 (7) 3.8 (8) 4.3 (9) 2.9 (6) FORMULATIONS FOR 12 PPG, 70:30 PPG 300 EMULSIONS Example IIIE IIIF IIIG IIIH PPG 300, g 237 237 237 237 Tall Oil, g 5 5 5 5 CLEARATE B-60, g 5 5 5 5 Lime, g 4 4 4 4 Organophilic Clay, g 8 SD-1 8 SD-2 8 SD-3 8 EW 20% (aq) NaCl, ml 100 100 100 100 Barite, g 198 198 198 198 EXAMPLE IV Brine-in-glycol emulsions can be prepared using organophilic silicas such as CAB-O-SIL TS-610 from Cabot Corporation. These emulsions are made by preparing a blend of CAB-O-SIL TS-610 or another organophilic silica, a propoxylated tripropylene glycol bottoms, tall oil, and lime. After the organophilic silica is dispersed in the fluid by mixing, 20% (aq) sodium chloride is added, and the mixture is sheared in a blender or bar mixer to produce a stable emulsion. Formulations and properties, both before and after heat aging, of unweighted examples are listed in Tables 11 and 12. The densities of these brine-in-glycol emulsions may be increased by the addition of barite, as illustrated in Table 13. These emulsions were found to be stable during either static or dynamic aging. These emulsions were prepared with a propoxylated tripropylene glycol bottoms having an approximate molecular weight of 600 and a cloud point of 26°C (78°F) for a 50% solution in deionized water. FORMULATIONS FOR 12 PPG, PPG 600 EMULSIONS Example IVH IVI Glycol/Brine Ratio, v/v 60:40 70:30 Formulation PPG 600, g 180 211 CAB-O-SIL TS-610, g 0.88 1.76 Tall Oil, g 8.8 8.8 Lime, g 3.5 3.5 20% (aq) NaCl, ml 119 88 Barite, g 173 177 EXAMPLE V In order to test the effectiveness of the additive compositions of the invention to release differentially stuck drill pipe, a filter cake was formed in an API filter press at 689 kPa (100 psi) using a 1.59 g/cm³ (13.3 lb/gal) gypsum mud. The formulation and typical properties of the gypsum mud are listed in Table 15. After 8 ml of filtrate was collected, the filter cell was opened and a 316SS cone 2.54 cm (1 inch) high, 4.13 cm (1 5/8 inches) in diameter at the base and 2.54 cm (1 inch) in diameter at the base and 2.54 cm (1 inch) in diameter at the top, and having a convex base was placed so that the convex base of the cone rested on top of the filter cake. The filtration cell was reassembled and filtration was continued until a total of 20 ml of filtrate was collected. After pressure filtration was completed, excess mud was poured from the cell and the filter cake and attached cone were carefully removed. The cake/cone assembly was then placed in the bed of a Buchner funnel and seated under a vacuum of 10 kPa (29.8 inches of Hg). After the cake was seated, excess fluid which had been removed from the filter press was poured on top of the filter cake. Vacuum filtration was performed for fifteen minutes, after which excess mud was removed from the Buchner funnel. The additive composition of the invention (Table 16) was then placed in the Buchner funnel, and a 2 kg counterweight was suspended from the cone by means of a pulley. The time required for the additive composition to effect release of the cone was measured. The results of the release times tests (Table 17) illustrate the ineffectiveness of the base mud and deionized water versus the effectiveness of the compositions of the invention. RELEASE TIMES FOR STUCK PIPE SIMULATION TEST Sample Release Time (min) Deionized Water 90 (No Release) 13.3 PPG Test Mud 90 (No Release) Example VA 8.3 Example VB 7.6 The stable invert emulsion drilling fluid of the invention may be used in a process for drilling or completing a well where the emulsion drilling fluid is circulated down through the interior of the drill pipe and then back up to the surface through the annulus between the drill pipe and the wall of the borehole. Alternatively, the invert emulsions of the invention may be used as spotting fluids. By this technique, a weighting material is mixed with the emulsion to produce a weighted spotting fluid. The weighted spotting fluid is then circulated downhole so as to position it to contact the drill string in the area adjacent the stuck zone. Such a fluid is effective as a spotting fluid which can be positioned in the borehole by techniques well known in the art. An invention has been provided with significant advantages. When used as a drilling fluid, brine-in-glycol emulsions will have significant advantages over water-based drilling fluids. The emulsions will provide improved hole stability, and bit lubrication, and will minimize hydration and dispersion of shale within the mud system. As spotting fluids the glycol emulsions will perform the same function as that provided by oil-based spotting fluids, but without the environmental problems of oil-based fluids.

Claims: A well bore fluid comprising a brine-in-glycol invert emulsion having a glycol external phase and a brine internal phase, the glycol external phase having a molecular weight in the range from 250 to 1000, a cloud point in the range from 15 to 83°C and being soluble or dispersible in sea water at a salinity of 3% and lower; an emulsifier; and a weighting agent. The well bore fluid of claim 1, wherein the glycol is selected from the group consisting of polypropylene glycol and propoxylated tripropylene glycol bottoms. The well bore fluid of claim 1 or 2, wherein the emulsifier is selected from the group consisting of lime, lecithin, fatty acids and fatty acid mixtures. The well bore fluid of any of claims 1 to 3, wherein the weighting agent is barite. The well bore fluid of any of claims 1 to 4, further comprising a viscosifier selected from the group consisting of sepiolite, attapulgite, organophilic clay and treated fumed silica. A method of preparing a well bore fluid according to any of claims 1 to 5 comprising forming a brine-in-glycol invert emulsion having a glycol external phase and a brine internal phase by fist combining a brine solution with a glycol having a molecular weight in the range from 250 to 1000, a cloud point in the range from 15 to 83°C and being soluble or dispersible in sea water at a salinity of about 3% and lower, thereby rendering the external phase and internal phase immiscible; adding an emulsifier to form an emulsion; and adding a weighting agent to the emulsion to form a weighted well bore fluid. A method of drilling a well which comprises circulating an invert emulsion well bore fluid according to any of claims 1 to 5 in said well.

Inventors: BLAND RONALD C, CLAPPER DENNIS K, BLAND, RONALD C., CLAPPER, DENNIS K.
Applicants: BAKER HUGHES INC, BAKER-HUGHES INCORPORATED
Application year: 1991
Main classification: C09K7
IPC codes: C09K8