Extrudable curable organosiloxane compositions

Abstract: The tear strength of cured organosiloxane elastomers can be increased and the compression set value reduced without adversely affecting other physical properties if the composition used to prepare the elastomer is curable by a platinum-catalyzed hydrosilation reaction and contains a mixture of two liquid diorganoalkenylsiloxy terminated polydiorganosiloxanes, one of which constitutes from 96 to 99.5 percent by weight of said mixture and contains the alkenyl radicals only at the terminal positions. The second polydiorganosiloxane contains both terminal alkenyl radicals and from 1 to 5 mole percent of alkenyl radicals on non-terminal repeating units.

Description: This invention relates to extrudable organosiloxane compositions. More particularly, this invention relates to extrudable organosiloxane compositions that can be cured by a platinum-catalyzed hydrosilation reaction to form elastomers exhibiting superior physical properties, particularly tear strength and compression set value, without sacrificing other desirable properties such as tensile strength and processability of the curable composition. The present inventors have now discovered how to increase the tear strength of silicone elastomers prepared by curing silica-filled compositions comprising a diorganoalkenylsiloxy terminated polydiorganosiloxane, an organohydrogensiloxane as the curing agent and a platinum group metal-containing hydrosilation catalyst. They have accomplished this by incorporating up to 4 percent of a polydiorganosiloxane B, based on the total weight of polydiorganosiloxanes containing ethylenically unsaturated hydrocarbon radicals. From 1 to 5 mole percent of the silicon atoms of polyorganosiloxane B contain ethylenically unsaturated hydrocarbon radicals. An objective of this invention is to define a class of liquid curable organosiloxane compositions that yield elastomers exhibiting a combination of high tear strength with compression set values less than 35%. A preferred class of the present compositions can be transported by pumping using conventional equipment. The present compositions are cured using a platinum-catalyzed hydrosilation reaction. This invention provides a curable organosiloxane composition comprising the product obtained by mixing to homogeneity: (A) from 96 to 99.5 weight percent, based on the total weight of (A) and (B), of a first diorganoalkenylsiloxy terminated polydiorganosiloxane exhibiting a viscosity of 5 to 20 Pa·s at 25°C. and containing essentially no alkenyl radicals bonded to non-terminal silicon atoms; (B) from 0.5 to 4 weight percent, based on the combined weights of (A) and (B), of a second diorganoalkenylsiloxy terminated polydiorganosiloxane that is miscible with said first polydiorganosiloxane and exhibits a viscosity of from 0.1 to 20 Pa·s at 25°C., where from 1 to 5 percent of the non-terminal repeating units of said second diorganoalkenylsiloxy-terminated polydiorganosiloxane contain an alkenyl radical; (C) an amount sufficient to cure said composition of an organohydrogensiloxane that is miscible with (A) and (B) and contains an average of more than two silicon-bonded hydrogen atoms per molecule, (D) a hydrosilation catalyst comprising a metal from the platinum group of the periodic table or a compound of said metal, the amount of said catalyst being sufficient to promote curing of said composition at a temperature of from ambient to 250°C., and (E) from 10 to 60 weight percent, based on the weight of said composition, of a reinforcing silica filler that is treated with at least one organosilicon compound, a portion of which is sym-tetramethyldivinyldisilazane, where the organic radicals bonded to the silicon atoms of (A), (B) and (C) are monovalent hydrocarbon or halogenated hydrocarbon radicals, wherein the ingredients (A), (B), and (C) are miscible with each other and wherein the molar ratio of silicon-bonded hydrogen atoms to ethylenically unsaturated hydrocarbon radicals in the composition is 0.8 to 3. The present inventors discovered that the preferred silica treating agent further reduces the compression set values of the cured elastomer. The ingredients of the present compositions will now be discussed in detail. The inventive feature considered responsible for the unique combination of physical properties, particularly the high tear strength and low compression set, exhibited by elastomers prepared from the present curable composition is the presence in the composition of two specific types of miscible diorganoalkenylsiloxy-terminated polydiorganosiloxanes in a specified range of relative concentrations. The first of the two polydiorganosiloxanes, referred to hereinafter as ingredient A, exhibits a viscosity of from 5 to 20 Pa·s, contains vinyl or other ethylenically unsaturated radicals only at the terminal positions of the molecule and constitutes from 96 to 99.5 percent of combined weight of the two polydiorganosiloxanes A and B. The second of the two diorganoalkenylsiloxy-terminated polydiorganosiloxanes, referred to hereinafter as ingredient B, contains alkenyl radicals on from 1 to 5 mole percent of the non-terminal repeating siloxane units. Cured elastomers prepared using preferred compositions of this invention exhibit tear strength values of 35-45 kilonewtons/meter. Experimental data for these preferred elastomers demonstrates that the tear strength reaches a maximum as the concentration of ingredient B approaches about 3 weight percent, based on the combined weight of ingredients A and B and decreases with increasing concentration of ingredient B beyond the 3 percent level. The alkenyl radicals present in ingredients A and B contain from 2 to 10 carbon atoms. Preferred alkenyl radicals are terminally unsaturated and include but are not limited to vinyl, allyl and 5-hexenyl. The silicon-bonded organic groups present in ingredients A and B, in addition to alkenyl radicals, are the monovalent hydrocarbon or substituted hydrocarbon radicals described in detail in the following portions of this specification. The term "essential absence of non-terminal ethylenically unsaturated radicals" used to describe ingredient A means that the only ethylenically unsaturated hydrocarbon radicals present on the non-terminal silicon atoms of this ingredient result from impurities present in the reactants used to prepare this ingredient or from undesired rearrangements occurring during preparation of this ingredient. Ingredient A is a diorganoalkenylsiloxy-terminated polydiorganosiloxane and can be represented by the average general formula YR 1 2 SiO(R 2 2 SiO) x SiR 1 2 Y where Y represents an alkenyl radical containing from 2 to 10 carbon atoms, R 1 and R 2 are individually monovalent hydrocarbon radicals or substituted monovalent hydrocarbon radicals containing from 1 to 20 carbon atoms, R 1 and R 2 are substantially free of ethylenic unsaturation and x represents a degree of polymerization equivalent to a viscosity of up to 20 Pa·s at 25°C. In preferred embodiments, the viscosity of ingredient A is from 5 to 15 Pa·s. The R 1 and R 2 radicals can be identical or different. Because ingredient A is an extrudable liquid at 25°C., at least one of the R 2 radicals on each of the non-terminal silicon atoms is lower alkyl, most preferably methyl. The remaining R 2 radical can be alkyl such as methyl or ethyl; substituted alkyl such as chloromethyl, 3-chloropropyl or 3,3,3-trifluoropropyl; cycloalkyl such as cyclohexyl; or aryl such as phenyl. Any R 1 and R 2 radicals other than methyl are preferably phenyl or 3,3,3-trifluoropropyl, this preference being based on the availability of the intermediates used to prepare these polydiorganosiloxanes and the properties of cured elastomers prepared by curing compositions containing these polymers. The alkenyl radical represented by Y have been defined in a preceding section of this specification. Methods for preparing the liquid polydiorganosiloxanes used as ingredients A and B of the present compositions by hydrolysis and condensation of the corresponding halosilanes or cyclic polydiorganosiloxanes are sufficiently disclosed in the patent and other literature that a detailed description in this specification is not necessary. Ingredient B is a liquid diorganoalkenylsiloxy-terminated polydiorganosiloxane that can be represented by the average general formula Y'R 3 2 SiO(R 4 2 SiO) y (Y'R 4 SiO) z SiR 3 2 Y' In this formula, Y' represents an alkenyl radical as defined for the Y radical of ingredient A, R 3 and R 4 are selected from the same group of monovalent hydrocarbon radicals and substituted monovalent substituted hydrocarbon radicals as R 1 and R 2 . Because ingredients A and B should be miscible with one another, the silicon-bonded hydrocarbon radicals present in these ingredients should be selected from the same class, i.e. lower alkyl. These hydrocarbon radicals, including Y and Y' are preferably identical. The degree of polymerization represented by the sum of y and z is equivalent to a viscosity of from 0.1 to 10 Pa·s, preferably from 0.1 to 1 Pa·s and the ratio z/(y+z) is from 0.01 to 0.05, which specifies the requirement for this ingredient that from 1 to 5 mole percent of the non-terminal repeating units contain a vinyl radical. The degree of polymerization of Ingredient B is preferably less than the degree of polymerization of Ingredient A. Preferred embodiments of ingredient A include but are not limited to dimethylvinylsiloxy-terminated polydimethyl-siloxanes, dimethylvinylsiloxy-terminated polymethyl-3,3,3-trifluoropropylsiloxanes, dimethylvinylsiloxy-terminated dimethylsiloxane/3,3,3-trifluoropropylmethylsiloxane copolymers and dimethylvinylsiloxy-terminated dimethylsiloxane/methylphenylsiloxane copolymers. Preferred embodiments of ingredient B encompass all of the preferred polydiorganosiloxanes for ingredient A with the addition of from 1 to 5 mole percent of non-terminal organoalkenylsiloxane units, where the preferred organic group are alkyl containing from 1 to 4 carbon atoms, fluoroalkyl such as 3,3,3-trifluoropropyl and aryl such as phenyl. The vinyl radicals present in preferred embodiments of ingredients A and B can be replaced by other alkenyl radicals such as allyl and hexenyl. The organosiloxane compositions of this invention are cured by a platinum-catalyzed hydrosilation reaction. The curing agent is an organohydrogensiloxane containing an average of more than two silicon-bonded hydrogen atoms per molecule. The organohydrogensiloxane contains from as few as four silicon atoms per molecule up to an average of 20 or more and can have a viscosity of up to 10 Pa·s or higher at 25°C. The repeating units of this ingredient include but are not limited to HSiO 1.5 , R 5 HSiO and/or R 5 2 HSiO 0.5 in addition to one or more of monoorganosiloxy, diorganosiloxane, triorganosiloxy and SiO 4/2 units. In these formulae, R 5 represents a monovalent hydrocarbon or halocarbon radical as defined hereinabove for the R 2 radical of ingredient A. One preferred class of organohydrogensiloxanes are copolymers consisting essentially of the repeating units R 5 3 SiO 1/2 , R 5 2 SiO, R 5 HSiO and R 5 SiO 3/2 units, where the RSiO 3/2 units constitute from 0.5 to 50 mole percent of the copolymer. Copolymers of this type can prepared by a controlled hydrolysis of a mixture comprising the corresponding organosilicon halides, such as the chlorides or the corresponding alkoxides. These and other methods for preparing the preferred organohydrogensiloxanes of this invention are sufficiently well known that a detailed description is not required in this specification. A second preferred class of organohydrogen siloxanes contain repeating units represented by the formulae R 5 2 HSiO 1/2 and SiO 4/2 . The concentration of R 5 2 HSiO 1/2 units is equivalent to a concentration of silicon-bonded hydrogen atoms in the copolymer of from 0.5 to 5 weight percent. Proper curing of the present compositions requires that ingredients A, B and C be miscible with one another. To ensure sufficient miscibility the silicon-bonded hydrocarbon radicals that are present in the highest concentration in these ingredients should be selected from the same class, e.g. alkyl radicals. These hydrocarbon radicals are preferably identical. In particularly preferred compositions, these hydrocarbon radicals are methyl or combinations of methyl with either 3,3,3-trifluoropropyl or phenyl. The molar ratio of silicon-bonded hydrogen atoms to vinyl or other ethylenically unsaturated hydrocarbon radicals in compositions curable by a hydrosilation reaction is critical with respect to the properties of the cured elastomer. The optimum ratio for the present curable compositions will be determined at least in part by the molecular weights of ingredients A and B, the type of curing agent and the concentration of any resinous organosiloxane copolymer described hereinafter. For compositions of this invention, this ratio is from 0.8 to 3. The optimum range of this ratio for other curable compositions of this invention can readily be determined by those skilled in the art with a minimum of experimentation. For particularly preferred compositions of this invention, the molar ratio of silicon-bonded hydrogen atoms to vinyl or other ethylenically unsaturated hydrocarbon radicals is between 1 and 2. Hydrosilation reactions are typically conducted in the presence of a catalyst (Ingredient D) that is a metal from the platinum group of the periodic table or a compound of such a metal. Platinum, rhodium and compounds of these metals have been shown to effectively catalyze hydrosilation reactions. Platinum compounds such as hexachloroplatinic acid and particularly complexes of these compounds with relatively low molecular weight vinyl-containing organosiloxane compounds are preferred catalysts because of their high activity and compatibility with the organosiloxane reactants. These complexes are described in U.S. Patent No. 3,419,593. Complexes with low molecular weight organosiloxanes wherein the silicon-bonded hydrocarbon radicals are vinyl and either methyl or 3,3,3-trifluoropropyl are particularly preferred because of their ability to catalyze a rapid curing of the elastomer at temperatures of at least about 70°C. The platinum containing catalyst can be present in an amount equivalent to as little as one part by weight of platinum per one million parts of curable composition. Catalyst concentrations equivalent to from 5 to 50 parts of platinum per million of curable composition are preferred to achieve a practical curing rate. Higher concentrations of platinum provide only marginal improvements in curing rate and are therefore economically unattractive, particularly when the preferred catalysts are used. Mixtures of the aforementioned vinyl-containing reactants, curing agents and platinum-containing catalysts may begin to cure at ambient temperature. To obtain a longer working time or "pot life", the activity of the catalyst under ambient conditions can be retarded or suppressed by addition of a suitable inhibitor. Known platinum catalyst inhibitors include the acetylenic compounds disclosed in U.S. Patent No. 3,445,420, which issued on May 20, 1969 to Kookootsedes et al. Acetylenic alcohols such as 2-methyl-3-butyn-2-ol constitute a preferred class of inhibitors that will suppress the activity of a platinum-containing catalyst at 25°C. Compositions containing these catalysts typically require heating at temperatures of 70°C. or above to cure at a practical rate. If it is desired to increase the pot life of a curable composition under ambient conditions, this can be accomplished using an olefinically substituted siloxane of the type described in U.S. Patent No. 3,989,667, which issued on November 2, 1976 to Lee and Marko. Cyclic methylvinylsiloxanes are preferred. Inhibitor concentrations as low as one mole of inhibitor per mole of platinum will in some instances impart satisfactory storage stability and cure rate. In other instances inhibitor concentrations of up to 500 or more moles of inhibitor per mole of platinum are required. The optimum concentration for a given inhibitor in a given composition can readily be determined by routine experimentation and does not constitute part of this invention. To achieve the high levels of tear strength and other physical properties that characterize cured elastomers prepared using the compositions of this invention, the compositions must contain a reinforcing silica filler. This type of filler is typically treated with one or more of the known silica treating agents to prevent a phenomenon referred to as "creping" or "crepe hardening" during processing of the curable composition. Any finely divided form of silica can be used as the reinforcing filler. Colloidal silicas are preferred because of their relatively high surface area, which is typically at least 50 square meters per gram. Fillers having surface areas of at least 300 square meters per gram are preferred for use in the present method. Colloidal silicas can be prepared by precipitation or a fume process. Both of these preferred types of silica are commercially available. The amount of finely divided silica used in the present compositions is at least in part determined by the physical properties desired in the cured elastomer. Liquid or pumpable polyorganosiloxane compositions typically contain from 10 to 60 percent by weight of silica, based on the weight of polydiorganosiloxane. This value is preferably from 30 to 50 percent. Silica treating agent are typically low molecular weight organosilicon compounds containing silicon-bonded hydroxyl groups or groups that can be hydrolyzed to hydroxyl groups in the presence of water. Typical hydrolyzable groups include halogen atoms such as chlorine amino and other groups containing a silicon-bonded nitrogen atom. Preferably, at least a portion of the silicon-bonded hydrocarbon radicals present on the treating agent are alkenyl radicals and the remainder are identical to a majority of the hydrocarbon radicals present in ingredients A and B. The present inventors discovered that when a symtetraalkyldivinyldisilazane constitutes a portion of the silica treating agent used to treat the reinforcing silica portion of the present curable compositions, cured elastomers prepared from these compositions exhibit lower values of compression set relative to elastomers prepared from curable compositions employing other conventional silica treating agents such as low molecular weight hydroxyl-terminated polydiorganosiloxanes. In preferred compositions, the alkyl groups on the silazane are methyl. Compression set is typically determined using ASTM test method D395. In accordance with this procedure, a sample of cured elastomer of known thickness, typically 1.25 cm., is compressed to 75 percent of its initial thickness in a suitable clamping device and then heated at a temperature of 177°C. for twenty-two hours. The sample is then allowed to stand for 0.5 hour under ambient conditions, at which time its thickness is measured. Compression set is calculated using the formula (A-C)/(A-B)x100, where A is the initial thickness of the sample, B is the thickness to which the sample is compressed during the test and C is the thickness of the final sample following compression and relaxation. Low values of compression set are required for certain end-use applications during which the cured elastomer is compressed between two mating surfaces to serve as a seal or gasket. In addition to the vinyl-containing polydiorganosiloxanes, curing agent, catalyst and silica filler the organosiloxane compositions of this invention can contain one or more additives that are conventionally present in curable compositions of this type. These materials are added to impart or enhance certain properties of the cured elastomer or facilitate processing of the curable composition. A small amount of water can be added together with the silica treating agent(s) as a processing aid. Typical additives include but are not limited to pigments, dyes, adhesion promoters, flame retardants, heat and/or ultraviolet light stabilizers and resinous organosiloxane copolymers to enhance the physical properties of the cured elastomer. Diatomaceous earth and calcium hydroxide are two preferred additives based on their ability to reduce the degradation in physical properties, particularly tensile strength and modulus and the increase in compression set value that occur when the cured elastomer comes into contact with oil heated to 150°C. or higher. The presence of calcium hydroxide also further reduces the compression set value of the cured elastomer. The silica filler can be treated in the presence of at least a portion of the other ingredients of the present compositions by blending these ingredients together until the filler is completely treated and uniformly dispersed throughout the composition to form a homogeneous material. The ingredients that are present during treatment of the silica typically include the silica treating agents and at least a portion of the polydiorganosiloxanes referred to herein as ingredients A and B. The organohydrogensiloxane and platinum-containing catalyst are typically added after treatment of the silica has been completed. If calcium hydroxide is one of the ingredients, it is also added at this time. Irrespective of the type of mixer used, blending of the silica, filler treating agent(s) and ingredients A and B is continued while the composition is heated at temperatures from about 100 to 250°C. under reduced pressure to remove volatile materials. The resultant product is then cooled prior to being blended with the organohydrogensiloxane (Ingredient C) and/or the platinum catalyst (Ingredient D), depending upon whether it is desired to prepare a one-part or two-part curable composition of this invention. The optional additives referred to hereinbefore can be added at this time or during blending of the silica with ingredients A and B. In-situ treatment of the silica can require anywhere from 15 minutes to 2 hours, depending upon the amount of material being processed, the viscosity of the material and the shear rate to which the material is subjected during processing. Alternatively, treatment of the silica can occur before the silica is blended with other ingredients of the present compositions. Methods for treating finely divided silica fillers prior to incorporating the silica into a polyorganosiloxane composition are known in the art. To ensure adequate blending of all ingredients, the mixing equipment in which the present compositions are prepared should be capable of subjecting the composition to a high rate of shear. The advantage of using this type of a "high intensity" mixer to prepare silica filled polyorganosiloxane compositions is taught in U.S. Patent No. 3,690,804, which issued to Minuto on June 1, 1976. In accordance with the disclosure of this patent, the tip of the stirring device in the mixer is rotated at a speed of from 25 to about 250 feet per second, which would generate considerable shearing forces. The exemplified compositions are blended in a Henschel high intensity mixer wherein the rotor was operated at a speed of 3800 revolutions per minute, equivalent to a rotor tip speed of 157 feet per second. Dough type mixers equipped with "sigma" shape blades, are not as efficient as mixers wherein the mixing surfaces are of a relatively flat "paddle" configuration. Examples of the paddle type mixers include the Henschel mixer disclosed in the aforementioned Minuto patent and certain mixers manufactured by Neulinger A.G. The blade is preferably rotated at a speed of at least 100 revolutions per minute. Curable compositions prepared using the present method typically exhibit viscosities of about 0.5 up to about 10,000 Pa·s at 25°C. Preferred compositions are extrudable. To facilitate blending and transfer of the compositions and minimize entrapment of air during mixing a viscosity of less than about 10 Pa·s at 25°C. is preferred, particularly for extrudable compositions. Because mixtures of ingredients A and/or B with the curing agent (ingredient C) and the platinum-containing catalyst may begin to cure under the conditions encountered during storage of these composition even in the presence of a catalyst inhibitor, to ensure long term storage stability it is desirable to separate the curing agent and the catalyst until it is desired to cure the composition. This can be achieved by packaging the curing agent and curing catalyst in separate containers or by encapsulating the curing catalyst in a thermoplastic organic or silicone resin that melts or softens at the temperature to which the composition is intended to be heated during the curing process. One part compositions curable by a platinum-catalyzed hydrosilation reaction and containing as the hydrosilation catalyst a liquid platinum compound that is microencapsulated within a thermoplastic organic polymer together with methods for preparing the microencapsulated catalyst are described in U.S. Patent No. 4,766,176, which issued to Lee et al. on August 23, 1988. The present curable compositions can be formed into shaped articles by press molding, injection molding, extrusion or any of the other methods used to fabricate organosiloxane compositions. In the absence of one of the aforementioned catalyst inhibitors or an encapsulated catalyst, the compositions will cure at ambient temperature over a period of several hours or days or within several minutes when heated at temperatures of up to 250°C. Compositions containing one of these catalyst inhibitors are typically cured by heating them for several minutes at temperatures of from 50 to about 250°C. A preferred range is from 100 to 200°C. It should be apparent that compositions containing a microencapsulated catalyst must be heated to at least the melting or softening point of the encapsulating polymer to liberate the catalyst. Cured elastomeric articles prepared using the curable compositions of this invention exhibit tear strengths above about 230 pounds per inch (38 kN/m) and low values of compression, that are typicially below 25% without adversely affecting other desirable properties of the cured elastomer or the extrudability of the composition from which it is formed. This unique combination of properties make the elastomers desirable for a number of end use applications, including gaskets and fabricated articles wherein at least a portion of the article is relatively thin and subjected to large amounts of stress. Articles of this type include diaphragms and bladders. The following examples describe preferred curable compositions of this invention and the desirable properties of elastomers, particularly low values of compression set and high tear strength, prepared by curing these compositions. The example is intended to illustrate the present invention and should not be interpreted as limiting the invention as defined in the accompanying claims. Unless indicated to the contrary, all parts and percentages are by weight and all viscosities were measured at 25°C. Example 1 This example demonstrates the improvement in tear strength and compression set of cured elastomers achieved by including from 1 to 3 percent, based on the total weight of vinyl-containing polydiorganosiloxanes, of a polydiorganosiloxane containing vinyl radicals on non-terminal silicon atoms when the viscosity of the polydiorganosiloxane containing vinyl radicals only on the terminal silicon atoms is less than the 20 Pa·s lower limit required by the compositions claimed in U.S. patent No. 4,753,978 to Jensen. Curable organosiloxane compositions were prepared by blending to homogeneity in a dough type mixer the entire quantity (325 parts) of a fume silica having a nominal surface area of 380 m 2 per gram, 62.5 parts of diatomaceous earth, 1.9 parts of sym-tetramethyldivinyldisilazane, 65 parts of hexamethyldisilazane, 9.4 parts water and 422.5 parts of a dimethylvinylsiloxy terminated polydimethylsiloxane having a viscosity of about 10 Pa·s at 25°C. (ingredient A). This mixture was heated for one hour by circulating steam through the jacket of the mixer while volatile materials were removed under reduced pressure. Following completion of the heating cycle the resultant master batch (composition I) was blended to homogeneity with the quantities of ingredients A and B specified in the following Table 1 together with 7.2 parts of a silanol terminated polydimethylsiloxane having a viscosity of about 0.04 Pa·s at 25°C. and containing about 4 weight percent of silicon-bonded hydroxyl groups. Ingredient B was a dimethylvinylsiloxy-terminated dimethylsiloxane/methylvinylsiloxane copolymer exhibiting a viscosity of 0.3 Pa·s and containing 2 mole percent of methylvinylsiloxane units. Two-part curable compositions of this invention and compositions evaluated for comparative purposes were prepared by dividing each of the resultant mixtures (composition II) into 250 gram samples. A 250 gram sample of each composition evaluated was blended to homogeneity with one of two different organohydrogensiloxanes and ingredient D, a reaction product of hexachloroplatinic acid and sym-tetramethyldivinyldisiloxane that had been diluted with a liquid dimethylvinylsiloxy terminated polydimethylsiloxane in an amount sufficient to achieve a platinum content of 0.7 weight percent, based on the weight of both parts of the curable composition. The amount of ingredient D, the catalyst for the curing reaction of the composition, was equivalent to from 5 to 10 parts per million parts by weight of platinum, based on the weight of the complete curable composition. One of the two organohydrogensiloxanes, (C1) contained 0.8 weight percent silicon-bonded hydrogen, exhibited a viscosity of 0.016 Pa·s and corresponded to the general formula (Me 3 SiO 1/2 ) 12.7 (Me 2 SiO) 29.1 (MeHSiO) 54.6 (MeSiO 3/2 ) 3.6 . The second (C2), a contained 1 weight percent of silicon-bonded hydrogen atoms, exhibited a viscosity of 0.024 Pa·s and was represented by the general formula (SiO 4/2 ) 4.4 Me 2 HSiO 1/2 ) 8 . 0.5 grams of methylbutynol as a platinum catalyst inhibitor (ingredient F) was also added to each of the compositions. The amount of ingredient C1 or C2 added was equivalent to a molar ratio of silicon-bonded hydrogen atoms to vinyl radicals in the total curable composition of 1.25. The compositions were cured in the form of sheets having a thickness of 1.9 mm. by confining the compositions in a chase that was then placed in hydraulic press. The compositions were heated for 5 minutes at a temperature of 150°C. Test samples were then cut from each of the sheets to determine the physical properties of the cured materials. The American Society of Testing Procedures (ASTM) method used to measure the various properties evaluated included ASTM-412 for tensile strength and elongation, ASTM-D625, Die B for tear strength, ASTM-D2240, Shore A scale for durometer hardness values and ASTM D395 for compression set values. Table 1 summarizes the parts by weight of ingredients A and B added to composition I and the amounts of ingredient C1 and C2 added to composition II. The physical properties of the cured compositions are summarized in Table 2. Sample No. Ingredient A (parts ) B (parts ) C1 (grams) C2 (grams) 1 196.3 6.3 (1%) 1.98 0 2 183.6 18.8 (3%) 2.15 0 3 171.3 31.3 (5%) 2.32 0 4 158.8 43.8 (7%) 2.48 0 5 202.6 0 1.90 0 6 196.3 6.3 (1%) 0 1.59 7 183.8 18.8 (3%) 0 1.72 8 171.3 31.3 (5%) 0 1.85 9 158.8 43.8 (7%) 0 1.99 10 202.6 0 0 1.51 Sample No. Tear Strength kN/m Hardness (Shore A) Compression Set % Tensile Strength MPa 1 40.4 53 26.8 6.2 2 46.3 56 22.2 5.4 3 42.3 61 28.5 5.4 4 17.5 66 34.1 7.3 5 34.1 52 32.8 8.1 6 14.7 52 22.7 5.9 7 36.5 57 23.1 5.4 8 17.5 60 25.7 5.1 9 20.3 64 29.4 7.0 10 21.2 53 29.2 8.3 The data in Table 2 demonstrate that by using the curable compositions of this invention one is able to substantially improve the tear strength and/or reduce the compression set of cured elastomers relative to prior art materials prepared using extrudable organosiloxane compositions without adversely affecting other desirable properties such as tensile strength, hardness and elongation. While the tear strength exhibited by comparative sample 3 was higher than the value for sample 1, sample 1 exhibited the lower compression set value. Example 2 This example demonstrates the lower compression set values achieved using a silica treating agent of this invention. Curable organosiloxane compositions were prepared using the types and amounts of ingredients and the procedure described in the preceding Example 1. In this instance, the comparative examples replaced the 0.31 parts of sym-tetramethyldivinyl-disilazane (T1) used as the silica treating agent with 0.92 parts of a hydroxyl terminated dimethylsiloxane/methylvinylsiloxane copolymer containing about 10 weight percent vinyl radicals and about 16 weight percent hydroxyl radicals (T2). The concentration of vinyl radicals contributed to the composition by each of these silica treating agents was equal. The amounts of ingredients A and B added to the masterbatch and the amounts of organohydrogensiloxanes C1 or C2 added to prepare the curable compositions are summarized in Table 3 and the compression set values of the cured elastomers are summarized in Table 4. Sample No. Ingredient A Parts B Parts C1 Grams C2 Grams 11a 196.3 6.3 1.98 0 11b 196.3 6.3 0 1.59 12a 183.8 18.8 2.15 0 12b 183.8 18.8 0 1.72 13a 171.3 31.3 2.31 0 13b 171.3 31.3 0 1.82 Sample Treating Agent Compression Set Value (%) 11a T1 26.8 11a T2 62.0 11b T1 22.7 11b T2 63.2 12a T1 22.2 12a T2 69.1 12b T1 23.1 12b T2 72.4 13a T1 28.5 13a T2 49.9 13b T1 25.7 13b T2 63.2 In every instance, the sample prepared using the polyorganosiloxane as the filler treating agent exhibited a higher compression set value than the sample containing the disilazane-treated filler.

Claims: A curable organosiloxane composition comprising the product obtained by mixing to homogeneity: (A) from 96 to 99.5 weight percent, based on the total weight of (A) and (B), of a first diorganoalkenylsiloxy terminated polydiorganosiloxane exhibiting a viscosity of 5 to 20 Pa·s at 25°C. and containing essentially no alkenyl radicals bonded to non-terminal silicon atoms; (B) from 0.5 to 4 weight percent, based on the combined weights of (A) and (B), of a second diorganoalkenylsiloxy terminated polydiorganosiloxane that is miscible with said first polydiorganosiloxane and exhibits a viscosity of from 0.1 to 20 Pa·s at 25°C., where from 1 to 5 mole percent of the non-terminal repeating units of said second diorganoalkenylsiloxy-terminated polydiorganosiloxane contain an alkenyl radical; (C) an amount sufficient to cure said composition of an organohydrogensiloxane that is miscible with (A) and (B) and contains an average of more than two silicon-bonded hydrogen atoms per molecule, (D) a hydrosilation catalyst comprising a metal from the platinum group of the periodic table or a compound of said metal, the amount of said catalyst being sufficient to promote curing of said composition at a temperature of from ambient to 250°C., and (E) from 10 to 60 weight percent, based on the weight of said composition, of a reinforcing silica filler that is treated with at least one organosilicon compound, a portion of which is sym-tetramethyldivinyldisilazane, where the organic radicals bonded to the silicon atoms of (A), (B) and (C) are monovalent hydrocarbon or halogenated hydrocarbon radicals, wherein the ingredients (A), (B), and (C) are miscible with each other and wherein the molar ratio of silicon-bonded hydrogen atoms to ethylenically unsaturated hydrocarbon radicals in the composition is 0.8 to 3.

Inventors: GRAY THOMAS EDWARD, JENSEN JARY DAVID, GRAY, THOMAS EDWARD, JENSEN, JARY DAVID
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1991
Main classification: C08L83
IPC codes: C08K3, C08L83