Adsorbent for purification of automobile exhaust gas and method of controlling emission of unburnt hydrocarbons from internal combustion engine

Abstract: A high-silica zeolite is used as an adsorbent (1) for unburned hydrocarbons in automobile exhaust gas, especially at cold start. The adsorbent (1) may carry a catalyst and be carried on an electrical heater (2), for desorption and reaction of the adsorbed hydrocarbons.

Description: BACKGROUND OF THE INVENTION Field of the Invention: The present invention relates to an adsorbent for purification of automobile exhaust gas comprising a zeolite, an adsorbent structure comprising a honeycomb structure and the adsorbent thereon, to a method of controlling emission of unburnt hydrocarbons from an internal combustion engine and to apparatus for purifying automobile exhaust gas. Description of the Prior Art: Catalytic converters used for purification of automobile exhaust gas or the like must be heated to a certain temperature or higher in order to exhibit their catalytic activities. Accordingly, when they are not sufficiently heated as in the start-up of automobile, it is necessary to heat them. As the technique for heating a catalytic converter, there is known, for example, a technique proposed in Japanese Utility Model Application Laid-Open No. 67609/1988. This document discloses a catalytic converter comprising (a) a ceramic monolith catalyst and (b) an electrically heatable metal monolith catalyst provided upstream of the ceramic monolith catalyst (a) in close vicinity thereto, consisting of a metal carrier and alumina coated thereon. Of the harmful compounds (HC's, CO and NOx) present in automobile exhaust gases, particularly HC's (hydrocarbons) produce photochemical smog (oxidant); accordingly, regulation therefor has been tightened, and proposals have been made to purify the HC's discharged in a large amount at the engine start-up, by the utilization of the adsorbability of zeolite. For example, there has been proposed apparatuses for purification of automobile exhaust gas, arranged in the exhaust gas system of automobile, which comprise (a) a purification catalyst and (b) an adsorbent (e. g. zeolite) or a catalyst-supporting adsorbent provided upstream of the purification catalyst (a) [reference is made to, for example, Japanese patent Application Laid-Open Nos. 75327/1990, 173312/1990 and 135126/1990]. Further, an adsorbent comprising a metal carrier and zeolite coated thereon is disclosed in Japanese Patent Application Laid-Open No. 126937/1990. The above proposals, however, each have a problem. The catalytic converter disclosed in Japanese Utility Model Application Laid-Open No. 67609/1988 consists of a metal monolith catalyst as a preheater and a main monolith catalyst; with this catalytic converter, it is difficult to purify hydrocarbons in exhaust gas, at the start-up of engine. With the apparatus for purification of automobile exhaust gas arranged in the exhaust gas system of automobile (disclosed in Japanese Patent Application Laid-Open No. 75327/1990), comprising a purification catalyst and an adsorbent (e.g. zeolite) provided upstream of the purification catalyst, even if HC's are adsorbed by the adsorbent provided upstream of the purification catalyst, the HC's are desorbed from the adsorbent with the warm-up of engine; as a result, a considerable amount of HC's pass through the purification catalyst which is not yet heated sufficiently, without being burnt. Japanese Patent Application Laid-Open No. 173312/1990 discloses a technique comprising a main exhaust gas passage containing a catalyst and a by-pass passage containing an adsorbent, in which technique an exhaust gas is passedthrough the by-pass passage during the start-up of engine, using a switching means and, when the temperature of the exhaust gas has reached the working temperature of the catalyst provided in the main passage, the exhaust gas is passed through the catalyst of the main passage using the switching means. With this technique, a complicated mechanism is required to enable the switching from the by-pass passage to the main passage when the catalyst in the main passage has been heated sufficiently; moreover, an innegligible amount of an exhaust gas passes through the catalyst of the main passage without being purified, before the catalyst is heated sufficiently. In the apparatus for purification of automobile exhaust gas arranged in the exhaust gas system of automobile (disclosed in Japanese Patent Application Laid-Open No. 135126/1990), comprising a purification catalyst and an adsorbent containing a catalyst supported thereon, provided upstream of the purification catalyst, the start-up of the purification catalyst is delayed because of the heat capacity of the adsorbent; the amount of the catalyst added to the adsorbent has a limitation; thus, no sufficient purification is possible. Japanese Patent Application Laid-Open No. 126937/1990 discloses an adsorbent alone and mentions neither heater nor catalytic converter for exhaust gas including CO, HC's and NO x . EP-A-2791 describes conversion of hydrocarbons and carbon monoxide in admixture with oxygen and water vapour to produce carbon dioxide, using a catalyst based on a zeolite having a Si/Al ratio of for example 20 or 40. Furthermore, a zeolite used as an adsorbent in these references mentioned above is Y type or mordenite. The zeolite is of poor heat resistance, and it fixedly adsorbs water contained in the exhaust gas, with the result that its adsorptive power is lowered. EP-A-0 427 970, published on 22 May 1991, describes a procedure, in the manufacture of a catalyst for purifying exhaust gases, in which an H-type zeolite layer is formed on a honeycomb structure by mixing the zeolite with silica sol, drying and calcining. This document also mentions that the Si/Al ratio of zeolite used is preferred to fall in the range 5 to 100. SUMMARY OF THE INVENTION Objects of the present invention are to solve the above-mentioned problems of the prior art and to provide a heater and catalytic converters. The present invention is set out in the claims. For further description of materials used in the invention, reference should be made to our published application EP-A-485180 filed on the same date as the present application. BRIEF DESCRIPTION OF THE DRAWINGS Figs. 1(a) to 1(f) each illustrate a preferable arrangement and constitution of the catalytic converter for purification of automobile exhaust gas, of the present invention. Fig. 2 illustrates an example of the heater or honeycomb heater of the present invention. In most of the conventional heaters of electrical heating type for purification of automobile exhaust gas, comprising a honeycomb structure not coated with any adsorbent or any adsorbent-catalyst composition, for the saving of power consumption, electricity is passed through the heater for several tens of seconds before the start-up of engine to heat the heater; no electricity is passed during the operation of cell motor; thereafter, electricity is passed again to heat the heater. Meanwhile, in the heaters herein described since an adsorbent or an adsorbent-catalyst composition is coated on a honeycomb structure, or an zeolite adsorbent is used together with a honeycomb heater and at least one main monolith catalyst, no electricity is passed before the start-up of engine; at the start-up of engine driven by cell motor, unburnt HC's in low-temperature exhaust gas are captured by the adsorbability of zeolite; thereafter, electricity is passed through the heater to heat the heater and simultaneously the HC's captured by zeolite begin to be desorbed, and the main monolith catalyst and/or the catalyst supported on the heater, generally arranged downstream of the zeolite adsorbent is momentarily heated, whereby the HC's are reacted and purified. When a catalyst is supported on the zeolite adsorbent, the captured HC's are not only desorbed but also reacted and purified. Incidentally, during the start-up of engine, the exhaust gas is at a fuel-rich side (an air-lean side); therefore, it is necessary to introduce into the exhaust gas an oxidizing gas (e.g., secondary air) to oxidize HC's or CO. In Figs 1(a) to 1(f) are shown preferable arrangements and constitutions of a honeycomb heater 2 (which may contain a catalyst supported thereon), main monolith catalyst(s) 3 and a zeolite adsorbent 1 (which may contain a catalyst supported thereon) constituting a catalytic converter for purification of automobile exhaust gas. Of these constitutions, the constitution of Fig. 1(a) wherein the zeolite adsorbent 1 is located most upstream in the exhaust gas system of an automobile, is preferable because it can carry out adsorption most easily. In this constitution, the honeycomb heater 2 and the zeolite adsorbent 1 may or may not contain a catalyst supported thereon. In the constitution of Fig. 1(b) wherein the honeycomb heater 2, the zeolite adsorbent 1 and the main monolith catalyst 3 are arranged in this order (the heater 2 is located most upstream), HC's can be controlled easily because the HC's adsorbed by the zeolite adsorbent 1 can be desorbed by the electrification and heating of the heater 2. Also in this constitution, the honeycomb heater 2 and the zeolite adsorbent 1 may or may not contain a catalyst supported thereon. The constitutions of Figs. 1(c) to 1 (f) wherein the main monolith catalyst 3 is provided most upstream, are preferable because the zeolite adsorbent 1 and the catalyst on the heater 2 are resistant to deactivation and have excellent durability. In the constitutions of Figs. 1(c) and 1(d), the zeolite adsorbent 1 or the honeycomb heater 2 provided intermediately may or may not contain a catalyst supported thereon; however, the honeycomb heater 2 or the zeolite adsorbent 1 provided most downstream must contain a catalyst supported thereon. In the constitutions of Figs. 1(e) and 1 (f) wherein the zeolite adsorbent 1 and the honeycomb heater 2 are arranged between the main monolith catalysts 3, the zeolite adsorbent 1 and the honeycomb heater 2 may or may not contain a catalyst supported thereon. The zeolite used as an adsorbent in the present invention is particularly selected. In high-silica zeolites, as in the case of well known ordinary zeolite, the minimum unit of the crystal lattices is a crystalline aluminosilicate, and Al 2 O 3 and SiO 2 are continuously bonded via oxygen ion. These high-silica zeolites have a Si/Al ratio of about 10 or more, as compared with the Si/Al ratio of 1-5 of ordinary zeolite. In the present invention, a high-silica zeolite having a Si/Al ratio of 48 or more is used as mentioned above. In view of heat resistance, a Si/Al ratio of 50 or more is especially preferable and a Si/Al ratio of 60 or more is most preferable. When the Si/Al ratio is more than 1,⊘⊘⊘, the zeolite has reduced capacity for adsorption and, when a catalyst component is added thereto, only a small amount of noble metal(s) can be introduced into the zeolite by ion exchange because the zeolite has a small number of ion exchange sites; therefore, such a zeolite is not preferable. The high-silica zeolite used in the present invention is a H (proton) type in view of the heat resistance. In the present invention, it is preferable that the catalyst supported on the adsorbent composed mainly of zeolite, contain a noble metal such as Pt, Pd, Rh or the like. It is also preferable that a heat-resistant oxide having a high specific surface area be added to the catalyst, in view of excellent light-off performance. A noble metal such as Pt, Pd, Rh or the like is supported on the zeolite and/or the heat-resistant oxide. In this case, the noble metal is supported on the zeolite by ion exchange, in view of the zeolite's heat resistance and selective NO x removability [the generation of NH 3 (a by-product) is suppressed]. In view of the desired catalyst properties as mentioned above, as the adsorbent-catalyst composition comprising an adsorbent and a catalyst supported thereon, which is most appropriate for use in the present invention, there can be mentioned a composition comprising (a) a high-silica zeolite of H (proton) type having a Si/Al ratio of 48 or more, ion-exchanged with at least one noble metal selected from Pt, Pd, Rh, Ir and Ru and (b) a heat-resistant oxide containing at least one noble metal selected from Pt, Pd, Rh, Ir and Ru. The component (a) can be obtained by subjecting a high-silica zeolite to ion exchange with at least one noble metal selected from Pt, Pd, Rh, Ir and Ru, in an appropriate aqueous solution. The percent ion exchange of the noble metal is preferably 10-85%, more preferably 30-85% in order to obtain the above-mentioned desired properties. The noble metal introduced into the high-silica zeolite by ion exchange is fixed at the exchange sites of the zeolite in high dispersion and can exhibit the catalytic activity effectively, is resistant to vaporization, causes no agglomeration even at high temperatures, and can maintain a high activity over a long period of time. The zeolite ion exchanged with a noble metal can be prepared, for example, as follows. A high-silica zeolite is immersed in a solution containing 10 -4 to 10 -1 mol/ℓ of a cationic metal ion; the system is allowed to stand or stirred or refluxed at room temperature to 100°C, preferably 80-90°C for about 2 hours or more to subject the zeolite to ion exchange with noble metal ion; if necessary, filtration and water washing are repeated to remove metals other than the ion-exchanged noble metal. After the ion exchange, the resulting zeolite is dried ordinarily at 80-150°C and further fired in an oxidizing or reducing atmosphere at 300-1,000°C for about 1-10 hours, to obtain a zeolite ion-exchanged with a noble metal. When a rare earth metal oxide (e.g. CeO 2 , La 2 O 3 ) and/or an alkaline earth metal oxide is added to the zeolite, the resulting zeolite has a wider three-way catalytic activity owing to the oxygen storability of the rare earth metal and can find wider applications, and moreover has higher heat resistance owing to the addition of the alkaline earth metal. As the component (b) which is a heat-resistant oxide, there can be used Al 2 O 3 , TiO 2 , ZrO 2 or SiO 2 , or a compound oxide thereof. Addition of a rare earth metal oxide (e.g. CeO 2 , La 2 O 3 ) and/or an alkaline earth metal oxide to the above heat-resistant oxide is preferable because, as mentioned above, the resulting oxide can have a wider three-way catalytic activity and higher heat resistance. The component (b) is formed by allowing the above heat-resistant oxide to support at least one noble metal. The weight ratio of the component (a) and the component (b) in the adsorbent-catalyst composition of the present invention is preferably the component (a) : the component (b) = 10 : 90 to 85 : 15. When the content of the component (a) is less than 10% by weight, the resulting composition has no selective NO x removability [the generation of NH 3 (a by-product) is not suppressed]. When the content of the component (a) is more than 85% by weight, the resulting composition has poor light-off performance. In the adsorbent-catalyst composition, the total amount of noble metals loaded is preferably 10-35 g/ft 3 , more preferably 15-30 g/ft 3 . When the total amount of noble metals loaded is less than 10 g/ft 3 , there are problems in light-off performance and durability. When the amount is more than 35 g/ft 3 , a high cost is incurred. In the conventional catalysts for exhaust gas purification, it has been necessary to load Rh in an amount of at least 5 g/ft 3 . Meanwhile, in the catalyst of the present invention using a high-silica zeolite having a Si/Al ratio of 40 or more, Rh loading in an amount of less than 5 g/ft 3 can sufficiently perform selective reduction of NO x to N 2 ,-and further the loading even in an amount of 0-2 g/ft 3 can exhibit practically sufficient selectivity when the resulting catalyst is used under relatively mild conditions (e.g. such conditions as the use temperature is low and the content of poisoning material in exhaust gas is low). The honeycomb structure used in the present invention is preferably produced by shaping a raw material powder into a honeycomb form, followed by sintering. In this case, so-called powder metallurgy and extrusion molding are preferably used in view of the simple process and the low cost. The heater or the catalytic converter used in the present invention is preferably produced in the form of a honeycomb structure (a one-piece structure) using a raw material powder, because such a structure generates no telescope phenomenon and enables uniform heating. In the heater or the honeycomb heater used in the present invention, it is preferable to use a metallic honeycomb structure whose surfaces of partition walls and pores have been coated with a heat-resistant metal oxide such as Al 2 O 3 , Cr 2 O 3 or the like, because the use of such a honeycomb structure has increased heat resistance, oxidation resistance and corrosion resistance. The honeycomb structure may be made of any material as long as the material can generate heat when electrified, and may be a metal or a ceramic. However, a metal is preferable as the material for the honeycomb structure, because of the high mechanical strength. Examples of such a metal include stainless steel and those having compositions of Fe-Cr-Al, Fe- Cr, Fe-Al, Fe-Ni, W-Co and Ni-Cr. Among the above materials, Fe-Cr-Al, Fe-Cr and Fe-Al are preferred because of the low cost and high resistances to heat, oxidation and corrosion. A metallic honeycomb structure of foil type may also be employed. The honeycomb structure employed in the present invention may be porous or non-porous. However, in the case where the honeycomb structure loads thereon a catalyst, an adsorbent composed mainly of zeolite, or an adsorbent-catalyst composition comprising said adsorbent and a catalyst supported thereon, a porous honeycomb structure is preferred because it has high adhesion to the catalyst, the adsorbent or the adsorbent-catalyst composition and gives rise to substantially no peeling of the catalyst, the adsorbent or the adsorbent-catalyst composition caused by a difference in the thermal expansion between the honeycomb structure and the catalyst, the adsorbent or the adsorbent-catalyst composition. Next, description is made on an example of the process for producing a honeycomb structure of the present invention, particularly a metallic honeycomb structure. First, for example, a Fe powder, an Al powder and a Cr powder, or alternatively powders of alloys of these metals are mixed toprepare a raw material metal powder mixture having a desired composition. Subsequently, the raw material metal powder mixture is mixed with an organic binder (e.g. methyl cellulose, polyvinyl alcohol) and water, and the resulting mixture is extrusion-molded to obtain a desired honeycomb form. When the raw material metal powder mixture is mixed with an organic binder and water, an antioxidant (e.g. oleic acid) is preferably added to the raw material metal powder mixture prior to the addition of water. Alternatively, powders of metals subjected to an anti-oxidation process are preferably employed. Next, the shaped honeycomb body is fired in a non-oxidizing atmosphere at a temperature ranging between 1,000 and 1,400°C. This firing is carried out in a non-oxidizing atmosphere containing hydrogen, because the organic binder is decomposed and thereby removed with the aid of Fe or the like which acts as a catalyst, and as a result a good sintered body can be obtained. Firing at a temperature lower than 1,000°C achieves no sintering. Sintering conducted at a temperature higher than 1,400°C gives a deformed sintered body. Preferably, the surfaces of the partition walls and pores of the thus obtained sintered body are coated with a heat-resistant metal oxide by any of the following methods. (1) The metallic honeycomb structure (the sintered body) is subjected to a heat-treatment in an oxidizing atmosphere at a temperature ranging between 700 and 1,100°C. (2) Al or the like is plated (e.g. vapor plating) on the surfaces of the partition walls and pores of the sintered body, and the resulting sintered body is subjected to a heat-treatment in an oxidizing atmosphere at a temperature ranging between 700 and 1,100°C. (3) The sintered body is dipped into a molten metal (e.g. molten Al), and the resulting sintered body is subjected to a heat-treatment in an oxidizing atmosphere at a temperature ranging between 700 and 1,100°C. (4) The surfaces of the partition walls and pores of the sintered body are coated with an alumina sol or the like, and the resulting sintered body is subjected to a heat-treatment in an oxidizing atmosphere at a temperature ranging between 700 and 1,100°C. The above heat treatment is carried out preferably at a temperature between 900 and 1,100°C in view of the heat resistance and oxidation resistance of the resulting honeycomb structure. Next, the obtained metallic honeycomb structure is provided, between the electrodes to be described later, with a resistance-adjusting means of any form. The resistance-adjusting means provided between the electrodes of the honeycomb structure may preferably take, for example, any of the following forms: (1) a slit or slits of any length, formed in any direction at any position, (2) variation in the length of partition walls in the axial direction of passages, (3) variation in the thickness (wall thickness) of partition walls of the honeycomb structure or variation in the cell density of the honeycomb structure, and (4) a slit or slits formed in the partition wall (rib) of the honeycomb structure. The metal honeycomb structure obtained in the manner described above is provided with electrodes, ordinarily on the outer periphery or inside by means of brazing, welding or the like, whereby a heater or a honeycomb heater of the present invention is produced. Incidentally, the electrodes used herein refer to all types of terminals capable of applying a voltage to the heater, and include a terminal obtained by directly joining the outer periphery of a heater to its casing, an earth, etc. The metallic honeycomb structure, when used as a heater, is preferably produced so as to have an overall resistance of 0. 00-0.5 Ω. Whereas the honeycomb structure employed in the present invention may have any form, it is desirable that specifically the cell density is in the range of, for example, 6 to 1,500 cells/in 2 (0.9-233 cells/cm 2 ) with the wall thickness ranging from 50 to 2,000 µm. As stated above, the honeycomb structure employed in the present invention may be porous or non-porous and may have any porosity. However, to achieve sufficient mechanical properties, oxidation resistance and corrosion resistance, the porosity of the metallic honeycomb structure is preferably held between 0 and 50% by volume with the most preferable porosity being less than 25% by volume. In a honeycomb structure having a catalyst, adsorbent or adsorbent-catalyst composition supported thereon, the porosity is preferably held at 5% or above to ensure strong adhesion between the honeycomb structure and the catalyst, adsorbent or adsorbent-catalyst composition. The term "honeycomb structure" used herein refers to an integral body having a large number of passages partitioned by walls. The passages may have any cross-sectional shape (cell shape), for example, a circular, polygonal or corrugated shape. The heater of the present invention can be produced by coating, on the honeycomb structure, the above-mentioned adsorbent composed mainly of zeolite or the above-mentioned adsorbent-catalyst composition comprising said adsorbent and a catalyst component supported thereon. The adsorbent or the adsorbent-catalyst composition is coated on the honeycomb structure in a film thickness of preferably 10-100 µm. When the film thickness is less than 10 µm, the resulting heater has insufficient durability. When the film thickness is more than 100 µm, the heater gives too large a pressure loss. The coating of the adsorbent or the adsorbent-catalyst composition on the honeycomb structure can generally be carried out, for example, by coating a slurry of the adsorbent or adsorbent-catalyst composition on the honeycomb structure or dipping the honeycomb structure in said slurry. As the main monolith catalyst used in the catalytic converter of the present invention, a conventional type may be used, but a three-way catalyst is preferable. The zeolite adsorbent may employ any structure, for example, beads, pellets, a honeycomb structure or the like. But, a honeycomb structure is preferable in view of the pressure loss. In this case, the honeycomb structure itself may be composed mainly of zeolite; however, it is preferable practically that an adsorbent composed mainly of zeolite be loaded on a ceramic or metallic substrate which is heat-resistant and thermanl shock resistance. The present invention is hereinafter described in more detail by way of Examples. However, the present invention is in no way restricted to these Examples. Example 1 A Fe powder, a Fe-Al powder (Al: 50 wt. %) and a Fe-Cr powder (Cr: 50 wt. %) having average particle sizes of 10, 20 and 22 µm, respectively, were mixed to prepare a mixture having a composition of Fe-22Cr-5Al (% by weight). To the mixture were added an organic binder (methyl cellulose), an antioxidant (oleic acid) and water to prepare a readily moldable body. The body was subjected to extrusion molding to obtain a honeycomb structure consisting of square cells having a rib thickness of 4 mil and passages of 400 cells/in 2 (cpi 2 ). The honeycomb structure was dried and then fired in H 2 atmosphere at 1,300°C. Thereafter, the honeycomb structure was subjected to a heat treatment in air at 1,000°C. The resulting honeycomb structure had a porosity of 22% by volume and an average pore diameter of 5 µm. On the above honeycomb structure having an outside diameter of 90 mmØ and a length of 50 mm was coated, in a thickness of 50 µm, a slurry obtained by mixing 95% by weight of H-ZSM-5 having a Si/Al ratio of 48 with 5% by weight of boehmite as a binder and then adding an appropriate amount of nitric acid. The resulting honeycomb structure was dried and fired to obtain a honeycomb structure coated with an adsorbent composed mainly of zeolite. Then, as shown in Fig. 2, two electrodes 11 were provided on the outer wall 10 of the honeycomb structure. Also, as shown in Fig. 2, six slits 12 having a length of 70 mm were formed in the honeycomb structure in the axial direction of the passages (the slits provided at the two ends had a length of 50 mm) at intervals of seven cells (about 10 mm). A zirconia type heat-resistant inorganic adhesive was filled in the outer peripheral portion 13 of each slit 12 to form an insulating portion. Thus, a heater of electrical heating type was produced. The thus obtained heater was provided in front (upstream) of a commercially available three-way catalyst as a main monolith catalyst which was supported on a ceramic honeycomb structure consisting of square cells of 6 mil in rib thickness and 400 cells/in 2 in passage number, whereby a catalytic converter was produced. The catalytic converter was evaluated as follows. That is, in order to examine the performance at engine start-up, the catalytic converter was subjected to Bag 1 test by U.S. FTP, using an automobile of 2,400 cc displacement. The heater was electrified at 12 V. The electrification was started after 10 seconds from engine start-up and stopped after 40 seconds from the start. During the electrification, control was made so that the gas temperature in the heater center became 400°C. Also, secondary air was fed into the catalytic converter at.a rate of 200 ℓ/min for 50 seconds after engine start-up. The results are shown in Table 1. Example 2 The same catalytic converter as in Example 1 was evaluated in the same manner as in Example 1 except that the electrification of the heater was started right after engine cranking. The results are shown in Table 1. Comparative Example 1 A catalytic converter consisting of only the same commercially available three-way catalyst as in Example 1 was evaluated in the same manner as in Example 1 except that no secondary air was fed. The results are shown in Table 1. Comparative Example 2 The same catalytic converter as in Example 1 was evaluated in the same manner as in Example 1 except that no electrification of the heater was conducted. The results are shown in Table 1. Example 3 The zeolite adsorbent of Example 1 was replaced by a zeolite adsorbent-catalyst composition. The zeolite adsorbent-catalyst composition was prepared as follows. H-ZSM-5 (a zeolite having a Si/Al ratio of 48) was immersed in an aqueous solution containing 10 -2 mol/ℓ of cationic platinum complex [(NH 3 ) 4 PtCl 2 ]. The system was refluxed at 90°C for 24 hours to conduct ion exchange. The resulting zeolite was water-washed five times under vacuum filtration; then dried at 100°C for 16 hours, and fired at 550°C for 3 hours to obtain a zeolite ion-exchanged with platinum. There were mixed 40 parts of commercially available γ-Al 2 O 3 (BET specific surface area: 200 m 2 /g), 10 parts (in terms of CeO 2 ) of Cerium acetate and a CeO 2 powder, 50 parts of the above-obtained ion-exchanged zeolite and an appropriate amount of acetic acid, to form a slurry. This slurry was coated on the same honeycomb structure as in Example 1, in a thickness of 50 µm, followed by drying and firing. On the γ-Al 2 O 3 ·CeO 2 of the resulting honeycomb structure were loaded Pt and Rh by impregnation, after which firing was conducted, to finally obtain an adsorbent-catalyst composition composed mainly of zeolite and loading Pt and Rh at a ratio of 19/1 in an amount of 30 g/ft 3 . Using this adsorbent-catalyst composition, a catalytic converter was produced in the same manner as in Example 1 and evaluated in the same manner as in Example 1. The results are shown in Table 1. Example 4 The same catalytic converter as in Example 3 was evaluated in the same manner as in Example 3 except that the electrification of the heater was started right after engine start-up. The results are shown in Table 1. Example 5 The evaluation of catalytic converter was effected in the same manner as in Example 4 except that the same adsorbent-catalyst composition as in Example 4 was provided downstream of the same commercially available three-way catalyst as in Example 4. The results are shown in Table 1. Comparative Example 3 The same catalytic converter as in Example 3 was evaluated in the same manner as in Example 3 except that no electrification of the heater was conducted. The results are shown in Table 1. HC (g) CO (g) NO (g) Example 1 1.35 (53) 11.8 (55) 2.01 (90) Example 2 1.38 (54) 12.0 (56) 2.05 (92) Comparative Example 1 2.56 (100) 21.5 (100) 2.23 (100) Comparative Example 2 2.30 (90) 20.4 (95) 2.19 (98) Example 3 1.02 (40) 10.8 (50) 1.87 (84) Example 4 0.97 (38) 10.0 (47) 1.81 (81) Example 5 1.10 (43) 11.0 (51) 1.83 (82) Comparative Example 3 2.18 (85) 19.4 (87) 2.01 (90) Each of the figures in parentheses indicates a relative value of each exhaust gas when each value of Comparative Example 1 was taken as 100. Examples 6-13 and Comparative Examples 4-5 [Preparation of honeycomb heater] A Fe powder, a Fe-Al powder (Al: 50 wt. %) and a Fe-Cr powder (Cr: 50 wt. %) having average particle sizes of 10, 20 and 22 µm, respectively, were mixed to prepare a mixture having a composition of Fe-22Cr-5Al (% by weight). To the mixture were added an organic binder (methyl cellulose), an antioxidant (oleic acid) and water to prepare a readily moldable body. The body was subjected to extrusion molding to obtain a honeycomb structure consisting of square cells having a rib thickness of 4 mil and passages of 400 cells/in 2 (cpi 2 ). The honeycomb structure was dried and then fired in H 2 atmosphere at 1,300°C. Thereafter, the honeycomb structure was subjected to a heat treatment in air at 1,000°C. The resulting honeycomb structure had a porosity of 22% by volume and an average pore diameter of 5 µm. On the outer wall 10 of the above honeycomb structure having an outside diameter of 90 mmØ and a length of 50 mm were provided two electrodes 11, as shown in Fig. 2. Also, as shown in Fig. 2, six slits 12 having a length of 70 mm were formed in the honeycomb structure in the axial direction of the passages (the slits provided at the two ends had a length of 50 mm) at intervals of seven cells (about 10 mm). A zirconia type heat-resistant inorganic adhesive was filled in the outer peripheralk portion 13 of each slit 12 to form an insulating portion. Thus, a honeycomb heater was produced. [Loading of catalyst A on heater] On the honeycomb heater was coated γ-Al 2 O 3 ·CeO 2 (70:30 by weight). Then, Pt and Rh were loaded in a total amount of 35 g/ft 3 at a ratio of Pt/Rh = 5/1, after which firing was effected to load a catalyst A on the heater. [Loading of catalyst B on heater] On the same honeycomb heater was coated a mixture consisting of 50 parts of H-ZSM-5 (Si/Al ratio = 48) ion-exchanged with Pt and 50 parts of γ-Al 2 O 3 ·CeO 2 (80:20 by weight). Further on the γ-Al 2 O 3 .CeO 2 were loaded Pt and Rh by impregnation to finally load Pt/Rh at a ratio of 19/1 in a total amount of 35 g/ft 3 . The resulting honeycomb heater was fired at 600°C to coat a catalyst B on the honeycomb heater in a film thickness of 50 µm. [Zeolite adsorbent] H-ZSM-5 (Si/Al ratio = 48) was coated, in a film thickness of 50 µm, on a commercially available cordierite honeycomb carrier of 25 mm in length (a honeycomb structure consisting of square cells of 6 mil in rib thickness and 400 cells/in 2 in passage number, a product of NGK INSULATORS, LTD.). Then, firing was effected at 600°C to produce a zeolite adsorbent. [Loading of catalyst B on zeolite adsorbent] The catalyst B was coated and loaded on the above-mentioned cordierite honeycomb carrier of 25 mm in length, in the same manner as in the above-mentioned loading of catalyst B on heater. [Loading of zeolite adsorbent on heater] The zeolite adsorbent was coated and loaded on the honeycomb heater, in the same manner as in the above-mentioned production of the zeolite adsorbent on the cordierite honeycomb carrier. [Main monolith catalyst] There was used a commercially available three-way catalyst whose carrier was a ceramic honeycomb structure consisting of square cells of 6 mil in rib thickness and 400 cells/in 2 in passage number. The above honeycomb heaters, zeolite adsorbents and main monolith catalyst were arranged in the orders shown in Table 2 to assemble catalytic converters. The converters were evaluated as follows. That is, in order to examine the performance at engine start-up, the catalytic converter was subjected to Bag 1 test by U.S. FTP, using an automobile of 2,400 cc displacement. The heater was electrified at 12 V. The electrification was started after 10 seconds from engine start-up and stopped after 40 seconds from the start. During the electrification, control was made so that the gas temperature in the heater center became 400°C. Also, secondary air was fed into the catalytic converter at a rate of 200 ℓ/min for 50 seconds after engine start-up. The results are shown in Table 2. For comparison, the same evaluation as above was made on the case wherein only the main monolith catalyst was used (Comparative Example 4), as well as on the case wherein the zeolite adsorbent and the main monolith catalyst were used but no honeycomb heater was used (Comparative Example 5). The results are shown in Table 2. As is clear from Table 2, the catalytic converters of the present invention can well purify each exhaust gas component such as HC, CO, NO or the like. As stated above, in the present invention, the adsorbability of zeolite and the heat-generatability of heater can greatly improve the purification of exhaust gas components, particularly HC's and CO, whereby the amounts of these components discharged into the atmosphere can be reduced significantly. Also, in the converter using the present invention, the zeolite adsorbent, the heater and the main monolith catalyst (s) can be arranged in the most appropriate order in view of the type of exhaust gas, the purpose of purification, the catalyst life, etc.

Claims: Claims for the following Contracting States: BE, ES, IT, SE An adsorbent structure comprising: a honeycomb structure having a periphery and two ends, including a plurality of passages which are defined by partition walls and extend in an axial direction between the ends; and an adsorbent for purification of automobile exhaust gas coated on the partition walls and comprising a zeolite, characterised in that the zeolite is a high-silica zeolite having a Si/Al ratio of not less than 48 and is an H (proton) type zeolite or a. zeolite obtained by subjecting an H (proton) type zeolite to ion exchange with at least one noble metal selected from Pt, Pd, Rh, Ir and Ru. An adsorbent structure according to claim 1, wherein a catalyst component is supported on the adsorbent. Method of controlling emission of unburnt hydrocarbons from an internal combustion engine at start-up, comprising the steps of:- (1) providing a catalyst for hydrocarbon conversion and an adsorbent capable of adsorbing hydrocarbons when cold, said adsorbent comprising zeolite which has a Si/Al ratio of at least 48 and is an H (proton) type zeolite or a zeolite obtained by subjecting an H (proton) type zeolite to ion exchange with at least one noble metal selected from Pt, Pd, Rh, Ir and Ru, said catalyst and said adsorbent being carried together on a support or carried on respective supports with the catalyst downstream in the exhaust gas flow from the engine relative to the adsorbent, (2) starting the engine when cold, with the adsorbent and the catalyst in a cold state, and (3) starting the engine, heating said catalyst electrically, whereby unburnt hydrocarbons are first adsorbed from the cold exhaust gas by said adsorbent and thereafter desorbed from the adsorbent and reacted by said electrically heated catalyst. Method according to claim 3, wherein the catalyst comprises a heat-resistant oxide loaded with the noble metal. An apparatus for purification of automobile exhaust gas, including an adsorbent structure as defined in claim 1 or claim 2, when arranged in the exhaust gas system of an automobile. An apparatus for purification of automobile exhaust gas, including a catalyst for hydrocarbon conversion and an adsorbent structure as defined in claim 1 or claim 2, when arranged in the exhaust gas system of an automobile. An adsorbent for purification of automobile exhaust gas, comprising a high-silica zeolite characterized in that the zeolite has a Si/Al ratio of not less than 48 and is an H (proton) type zeolite or a zeolite obtained by subjecting an H (proton) type zeolite to ion exchange with at least one noble metal selected from Pt, Pd, Rh, Ir and Ru, when arranged in the exhaust gas system of an automobile. Claims for the following Contracting States: DE, FR, GB An adsorbent structure comprising: a honeycomb structure having a periphery and two ends, including a plurality of passages which are defined by partition walls and extend in an axial direction between the ends; and an adsorbent for purification of automobile exhaust gas coated on the partition walls and comprising a zeolite, characterised in that the zeolite is a high-silica zeolite having a Si/Al ratio of not less than 48 and is either an H (proton) type zeolite, excluding such a zeolite obtained by mixing the zeolite with silica sol, drying and calcining, or a zeolite obtained by subjecting an H (proton) type zeolite to ion exchange with at least one noble metal selected from Pt, Pd, Rh, Ir and Ru, the percent ion exchange of the noble metal being 30 to 85%. An adsorbent structure according to claim 1, wherein a catalyst component is supported on the adsorbent. Method of controlling emission of unburnt hydrocarbons from an internal combustion engine at start-up, comprising the steps of:- (1) providing a catalyst for hydrocarbon conversion and an adsorbent capable of adsorbing hydrocarbons when cold, said adsorbent comprising zeolite which has a Si/Al ratio of at least 48 and is an H (proton) type zeolite or a zeolite obtained by subjecting an H (proton) type zeolite to ion exchange with at least one noble metal selected from Pt, Pd, Rh, Ir and Ru, said catalyst and said adsorbent being carried together on a support or carried on respective supports with the catalyst downstream in the exhaust gas flow from the engine relative to the adsorbent, (2) starting the engine when cold, with the adsorbent and the catalyst in a cold state, and (3) starting the engine, heating said catalyst electrically, whereby unburnt hydrocarbons are first adsorbed from the cold exhaust gas by said adsorbent and thereafter desorbed from the adsorbent and reacted by said electrically heated catalyst. Method according to claim 3, wherein the catalyst comprises a heat-resistant oxide loaded with the noble metal. An apparatus for purification of automobile exhaust gas, including an adsorbent structure as defined in claim 1 or claim 2, when arranged in the exhaust gas system of an automobile. An apparatus for purification of automobile exhaust gas, including a catalyst for hydrocarbon conversion and an adsorbent structure as defined in claim 1 or claim 2, when arranged in the exhaust gas system of an automobile. An adsorbent for purification of automobile exhaust gas, comprising a high-silica zeolite having a Si-Al ratio of not less than 48 and being either a H (proton) type zeolite or a zeolite obtained by subjecting an H (proton) type zeolite to ion exchange with at least one noble metal selected from Pt, Pd, Rh, Ir and Ru, the percent ion exchange of the noble metal being 30 to 85%, when arranged in the exhaust gas system of an automobile.

Inventors: ABE FUMIO, NODA KEIJI, ABE, FUMIO, NODA, KEIJI
Applicants: NGK INSULATORS LTD, NGK INSULATORS, LTD.
Application year: 1991
Main classification: F01N3
IPC codes: F01N7, F01N3, H05B3, B01J35, B01J29, B01D53