Thermosetting compound and its production method

Abstract: Thermosetting compounds expressed by the general formulas (IA) and (IB) are disclosed; (In the formula, Ar₁, Ar₂ and Ar₄ are divalent organic groups, Ar₃ is a monovalent organic group and Ar₁ , Ar₂ , Ar₃ and Ar₄ may be the same kind or different kind. m is an integer of 1-30.) The above compounds provide hard substances excellent in workability as well as high in heat resistance and mechanical properties.

Description: The present invention relates to a new thermosetting compound and its production method. More particularly, it relates to an esterimideoligomer excellent in heat resistance and having an appropriate reactivity for lamination and molding, and production method thereof. Thermosetting resins have been used for various kinds of electric insulation materials and structural materials, as materials of cast molding, impregnation, lamination and molding. Recently, conditions in these usages have become increasingly severer. Especially, heat resistance of the materials has become an important property. Formerly, for such usage, a thermosetting polyimide resin or a heat-resistant epoxy resin has been used. Among them, as the thermosetting polyimide resin, "Kerimid" (trade name, manufactured by Rhône-Poulenc Chemie) mainly composed of a bismaleimide compound and diaminodiphenylmethane is used (Matsuo Fujisawa, Plastics, Vol.34, No.7, p.75, 1983). However, the thermosetting polyimide resin has a disadvantage of needing a high temperature and a long time heating process during forming. In addition, as diaminodiphenylmethane is harmful to a human body, there is a problem of sanitation in handling. In addition, recently, an acetylene end terminated type polyimide has been put on the market as "Thermid" (trade name, manufactured by Gulf R&D, Japanese Laid-Open Publication No.53-119865). However, as organic solvent solubility is comparatively low, high boiling point organic polarity solvents such as dimethylformamide and dimethylacetamide must be used, and thus, there is a problem in handling. In order to solve the problem encountered with the polyimide, numerous improvement methods have been proposed for the resin, and among them, various kinds of polyesterimide resin have been proposed from viewpoints of molding property (for example, USP No. 4,757,118, No. 4,362,861, No. 3,852,246, or Japanese Laid-Open Publication No.1-123819). However, it is pointed out that generally, the polyesterimide is lower in softening point and more excellent in resin flowing property than the polyimide, but inferior in heat resistance to the polyimide (Keisuke Kurita et al. Polymer Applications, Vol.37, No.2, p.22-26, 1989). Besides, there is only a few knowledge that as in the present invention, a new acid dianhydride with ester bonding was at first synthesized using trimellitic acid anhydride as a starting monomer and paratoluenesulfonic acid chloride/pyridine as a reaction solvent, then polyesterimide is synthesized in the same reaction system by introducing diamine therein (for example, H. Tanaka et al., Proceedings/Abstracts of Third International Conference on Polyimides, pp. 65-68, 1988). Much less, there is no knowledge at all about polyesterimide of thermosetting type or having reactivity such as photoreactivity. An object of the present invention is to provide an esterimideoligomer, which gives hard substances excellent in molding property, and having high heat resistance and mechanical properties. Another object and advantages of the present invention will be made clear through reading of the followng detailed description. The present inventors have found out that the above objects can be attained by, at first, synthesizing a new acid dianhydride with ester bonding using trimellitic acid anhydride as a starting monomer and paratoluenesulfonic acid chloride/pyridine as a reaction solvent, then reacting the acid dianhydride with a diamine, further adding a primary amine or an acid anhydride to terminate its ends, and then ring-closing and dehydrating of the reaction product. The present invention is, in a first aspect, to provide a thermosetting compound shown by the general formula (IA); (In the formula, Ar 1 and Ar 2 are divalent organic groups as defined in claim 1, Ar 3 is a monovalent organic group as defined in claim 1, and Ar 1 , Ar 2 and Ar 3 may be the same kind or different kind. m is an integer of 1-30.) The present invention is, in a second aspect, to provide a thermosetting compound shown by the general formula (IB); (In the formula, Ar 1 , Ar 2 and Ar 4 are divalent organic groups as defined in claim 2, and Ar 1 , Ar 2 and Ar 4 may be the same kind or different kind. m is an integer of 1-30.) The present invention is, in a third aspect, to provide a production method of a thermosetting compound, characterized in the following : a reaction system is kept at room temperature or below in an inert gas atmosphere, trimellitic acid anhydride dissolved in an aprotic polar solvent is added to a solution mixed with paratoluenesulfonic acid chloride and pyridine, then a diol dissolved in advance in the aprotic polar solvent is reacted, then the necessary amount of a diamine dissolved in the aprotic polar solvent, which is required for obtaining both end acid anhydrides-terminated telechelic oligoesteramic acid, is added to allow the reaction proceed, further, a primary amine or an acid anhydride dissolved in the aprotic polar solvent is added to terminate the both ends, then, a non-solvent is added to dehydrate and close the rings of the reaction product. To begin with, a production method of a thermosetting compound of the present invention is described. The necessary quantity of paratoluenesulfonic acid chloride (hereinafter described as TsCl) is weighed in an inert gas atmosphere such as argon or nitrogen, the reaction system is kept at room temperature or below, preferabley below 10°C, more preferably below freezing temperature, and then pyridine is dropped through a cylinder while paying attention to heat generation. After enough reaction, the calculated quantity of trimellitic acid anhydride (hereinafter described as TMA) is dissolved in an aprotic polar solvent and added. Then, a diol shown by the general formula (II) HO - Ar 2 -OH (In the formula, Ar 2 is a divalent organic group.) is dissolved in the same aprotic polar solvent at freezing temperature and then added. To complete the reaction, the reaction is properly accelerated at room temperature. In this step, to obtain a copolymer, it is possible to add organic tetracarboxylic acid dianhydride shown by the general formula (III). (In the formula, Ar 5 is a tetravalent organic group.) Then, the system is again cooled at freezing temperature, and a diamine shown by the general formula (IV), which was dissolved in the same aprotic polar solvent, is added. H 2 N- Ar 1 - NH 2 (In the formula, Ar 1 is a divalent organic group.) It is important to add the calculated quantity of diamine to obtain both end acid anhydride groups-terminated telechelic oligoesteramic acid solution. After the oligoesteramic acid solution is thoroughly reacted, the reaction is further continued in a reaction system. Thereafter, an oligoesteramic acid shown by the general formulas (VIA) or (VIB) is synthesized, wherein the end acid anhydrides are terminated by a primary amine shown by the general formula (VA) or by an aromatic acid anhydride shown by the general formula (VB), dissolved in the same aprotic polar solvent. Ar 3 - NH 2 (In the formula, Ar 3 is a monovalent organic group.) (In the formula, Ar 4 is a divalent organic group.) (In the formula, Ar 1 and Ar 2 are divalent organic groups, Ar 3 is a monovalent organic group and Ar 1 , Ar 2 and Ar 3 may be the same kind or different kind. m is an integer of 1-30.) (In the formula, Ar 1 , Ar 2 and Ar 4 are divalent organic groups, and Ar 1 , Ar 2 and Ar 4 may be the same kind or different kind. m is an integer of 1-30.) Finally, in order to subject said amic acid solution to dehydration and ring closure thermally or chemically, a non-solvent is added to transform it into an esterimideoligomer expressed by the general formula (IA) or (IB) under reflux and azeotrope. The non-solvents used in this step may include aromatic hydrocarbons such as xylene, toluene and benzene, but benzene is preferably used. Upon the reaction, azeotropically distilled water is circulated by Dean-Stark reflux condenser until the theoretical reaction quantity of water is collected. After the reaction, the resulting polyimide solution is poured into violently stirred water or an alcohol-based solvent, and polyimide is precipitated as powder. The powder is collected by filtration and dried for 48 hours at 80°C under reduced pressure. As organic tetracarboxylic acid dianhydrides used in the present invention, those having any structure can be used, but Ar 5 in the above general formula (III) is preferably a tetravalent organic group and aromatic group. This Ar 5 group may be exemplified as follows: These organic tetracarboxylic acid dianhydrides may be used singly or in combination of two or more. More particularly, it is preferable, from the viewpoint of balance of various properties, to use as main composition at least one of the followings; The diols used in the present invention are expressed by the general formula (II), HO-Ar 2 -OH In the formula, Ar 2 is a divalent organic group selected from : Among them, the aromatic group is preferable, and it is preferable to use as a main component at least one of the following: The diamines used in the present invention are expressed by the general formula (IV), H 2 N- Ar 1 - NH 2 In the formula, Ar 1 is a divalent organic group selected from: Among them, the aromatic group is preferable, and it is preferable to use as a main component at least one of the followings; The primary amines for the end termination used in the present invention are expressed by the general formula (VA), - Ar 3 - NH 2 and Ar 3 of the primary amines is selected from: But, the following are especially preferable in respect of cost and handling; The aromatic acid anhydrides for the end termination used in the present invention are expressed by the general formula (VB), and Ar 4 of the acid anhydrides is selected from But, the followings are especially preferable in respect of cost and handling; As the aprotic polar organic solvents used in the reaction for obtaining an oligoesteramic acid solution, there are, for example, sulfoxide solvents such as dimethylsulfoxide and diethylsulfoxide; formamide solvents such as N,N'-dimethylformamide and N,N'-diethylformamide; and acetamide solvents such as N,N'-dimethylacetamide and N,N'-diethylacetamide. These can be used singly or in combination of two or more. Besides, not only these aprotic polar solvents but also their mixture with polyamic acid non-solvents such as methanol, ethanol, isopropanol and benzene methyl cellosolve can be used. It is preferable to use dimethylformamide (hereinafter, described as DMF) in respect of tint and yield of polymer generated. The mechanism is not made clear why an esterimideoligomer with reactivity, relating to the present invention, gives a hard substance with especially high heat resistance. But, it is said that the mechanism is due to benzene skeleton formation by thermosetting (trimerization) of acethylene or tetrabenzocyclooctadiene skeleton formation by thermosetting (dimerization) of biphenylene (for example, Tsutomu Takeich, Polymer forming, Vol.37, No.7, p.347, 1988). In order to control the number average polymerization degree (DP ; P.J.Frolie, Principles of Polymer Chemistry : Cornell University Press : Ithaca, NY, p.91, 1953), the polymerization ratio n is 1-30, preferably 1-25, or more preferably 1-20. If the value is over the upper limit, a problem of lowering organic solvent solubility occurs. If the value is less than the lower limit, there occurs a problem in mechanical strength. Upon obtaining hard substances from an esterimideoligomer of the present invention, epoxy resins, epoxy resin curing agents, hardening accelerators, fillers, flame retarders, reinforcing agents, surface treating agents, pigment and various elastomers can be conjointly used. The epoxy resins are compounds having two or more epoxy (glycidyl) groups in its molecule. Examples are novolak type epoxy resins which are reaction products of formaldehyde, phenols such as phenol and orthocresol, and glycidylether compound derived from halogenated polyphenols such as novolak derived from tetrabromobisphenol A, bromopolyphenols and divalent or more valent phenols such as bisphenol A, bisphenol F, hydroquinone, resorcin, tris-(4-hydroxyphenyl) methane and 1,1,2,2,-tetrakis (4-hydroxyphenyl) ethane ; amine type epoxy resins derived from aniline, paraaminophenol, metaaminophenol, 4-amino-metacresol, 6-amino-metacresol, 4,4'-diaminodiphenylmethane, 3,3'-diaminodiphenylmethane, 4,4'-diaminodiphenylether, 3,4'-diaminodiphenylether, 1,4-bis (4-aminophenoxy) benzene, 1,4-bis(3-aminophenoxy)benzene, 1,3-bis (3-aminophenoxy)benzene, 2,2-bis(4-aminophenoxyphenyl)propane, paraphenylenediamine, metaphenylenediamine, 2,4-toluenediamine, 2,6-toluenediamine, paraxylenediamine, metaxylenediamine, 1,4-cyclohexane-bis(methylamine), 1,4-cyclohexane-bis(methylamine), 5-amino-1-(4'-aminophenyl)-1, 3,3-trimethylindan, 5-amino-1-(4'-aminophenyl)-1-methylindan, 5-amino-1-(4'-aminophenyl)-3,3-dimethylindan, 6-amino-1-(4'-aminophenyl)-1, 3,3-trimethylindan, 6-amino-1-(4'-aminophenyl)-1-methylindan, 6-amino-1-(4'-aminophenyl)-3,3-dimethylindan; hydantoin type epoxy resins derived from aromatic carboxylic acids such as 5,5-dimethylhydantoin and glycidylester compounds derived from aromatic carboxylic acids such as paraoxybenzoic acid, terephthalic acid and isophthalic acid; alicyclic epoxy resins such as 2,2'-bis(3,4-epoxycyclohexyl)propane, 2,2-bis[4-(2,3-epoxypropyl) cyclohexyl]propane, vinylcyclohexenedioxide and 3,4-epoxycyclohexanecarboxylate ; and triglycidylisocyanurate and 2,4,6-triglycidoxy-s-triazine. These compounds may be used singly or in combination of two or more. Example of the epoxy hardening agents are amine type hardening agents such as aromatic amines such as xylylenediamine and aliphatic amines; polyphenol compounds such as phenolnovolak and cresolnovolak; and hydrazide compounds. These may be used singly or in combination of two or more. Example of the hardening accelerators are amines such as benzyldimethylamine, 2,4,6-tris(dimethylaminomethyl) phenol, 1,8-diazabicycloundecene; imidazole compounds such as 2-ethyl-4-methylimidazole ; and borontrifluoride-amine complex. These may be used singly or in combination of two or more. It is effective to add elastomers to improve mechanical strength. The elastomers may be exemplified as follows; Among elastomers described above, Silostic (LS-420) and Sylgord (184) are manufactured by Dow Corning Co., Ltd., Hiker. ATBN (1300× 16 etc.), CTB (2000× 162), CTBN (1300× 13, 1300× 8, 1300× 31) and VTBN (1300× 23) are manufactured by Ube Kosan Co., Ltd, and 3F is manufactured by Monsanto Co., Ltd. Examples of the fillers are aluminum hydroxide, antimony trioxide and red phosphorus. Examples of the reinforcing materials are woven cloth, non-woven cloth and mat made of carbon fiber, glass fiber, aramide fiber and liquid crystal polyester fiber such as vectra, polybenzothiazole (PBT) fiber and alumina fiber, and paper. In the following, the present invention will be explained in more detail by way of examples, but the present invention is not limited thereto. Abbreviations to be used in the examples are as follows. The organic group Ar 2 ( 1 ) of aromatic diol compounds expressed by the general formula (II), are as follows: The organic group Ar 1 ( 3 ) of aromatic diamine compounds expressed by the general formula (IV) are as follows: And, the organic group Ar 3 ( 4 ) of primary amines expressed by the general formula (VA) are as follows: And, the organic group Ar 4 of acid anhydrides (4) expressed by the general formula (VB) are as follows: Example 1 A three way cock, a Dean-Stark distillation device, a Dimroth reflux condenser and a Septum cap were located to a 1-liter four neck flask. The reactor was dried under reduced pressure. After 14.9 g (78 mmol) of TsCl was added to the reaction system, replacement with argon was sufficiently made. The reaction system was cooled to freezing temperature, and 30 ml of dried pyridine was added with paying attention to heat generation. 15 g (78 m mol) of TMA was completely dissolved in 110 ml dried DMF, and then it is added in 30 min. At that temperature, the reaction was continued, and 13.1 g (39 m mol) of the aromatic diol 1aA , which was dissolved in 30 ml dried DMF, was dropped at freezing temperature. After 30 min, an ice bath was taken out, and the reaction was continued for 1 hour at room temperature. Then, the reaction system was again cooled to freezing temperature, and 5.69 g(19.5 mmol) of the aromatic diamine 3aA was added to 50 ml dried DMF. After 30 min, the ice bath was taken out, and the reaction system was heated to 60 °C using an oil bath and the reaction was continued for 30 min. 7.06 g (39.0 mmol) of the aromatic primary amine 4aA was added to 10 ml dried DMF and reacted for 2.6 hours. Then, 200 ml dried benzene was added and 1.2 ml (theoretical quantity: 1.4 ml) of water was taken out at 145 °C (bath temperature) under azeotrope. After the reaction, the resultant reaction solution was poured into 1000 ml methanol and an esterimideoligomer was precipitated. When the precipitated esterimideoligomer 5aA was filtered under reduced pressure and dried for 48 hours at 80 °C in vacuum, 29.6 g ( yield: 74.9 %) of pale yellow powder was obtained. Using 4.5 g of this esterimideoligomer 5aA , press molding was carried out under 170 °C × 10 kg / cm 2 × 1.5 hours. Then, a cast molding plate with 12 mm (width) × 12 cm (length) × 1.5 mm (thickness) was obtained. The results of measurement of various properties of the esterimideoligomer 5aA and the cast molded plate are set forth in Table 1 and Table 2. Example 2 A three way cock, a Dean-Stark distillation device, a Dimroth reflux condenser and a Septum cap were located to a 1-liter four neck flask. The reactor was dried under reduced pressure. After 14.9 g (78 mmol) of TsCl was added to the reaction system, replacement with argon was sufficiently made. The reaction system was cooled to freezing temperature, and 30 ml of dried pyridine was added with paying attention to heat generation. 15 g (78 mmol) of TMA was completely dissolved in 110 ml dried DMF, and then it is added in 30 min. At that temperature, the reaction was continued, and 9.75 g (39 mmol) of the aromatic diol 1bA, which was dissolved in 30 ml dried DMF, was dropped at freezing temperature. After 30 min, an ice bath was taken out, the reaction was continued for 1 hour at room temperature. Thereafter, the reaction system was again cooled to freezing temperature, and 6.51 g (19.5 mmol) of the aromatic diamine 3bA was added to 50 ml dried DMF. After 30 min, the ice bath was taken out, the reaction system was heated to 60 °C using an oil bath and the reaction was continued for 30 min. 5.11 g (39.0 mmol) of the aromatic primary amine 4bA was added to 10 ml dried DMF and reacted for 2.6 hours. Then, 200 ml dried benzene was added and 1.3 ml (theoretical quantity: 1.4 ml) of water was taken out at 145 °C (bath temperature) under azeotrope. After the reaction, the resultant reaction solution was poured into 1000 ml methanol and an esterimideoligomer was precipitated. When the precipitated esterimideoligomer 5bA was filtered under reduced pressure and dried for 48 hours at 80 °C in vacuum, 33.9 g (yield: 96.7 %) of pale yellow powder was obtained. Using 4.5 g of this esterimideoligomer 5bA , press molding was carried out under 180 °C × 10 kg/cm 2 × 1.5 hours. Then, a cast molded plate with 12 mm (width)× 12 cm (length) × 1.2 mm (thickness) was obtained. The results of measurement of various properties of the esterimideoligomer 5bA and the cast molded plate are set forth in Table 1 and Table 2. Example 3 A three way cock, a Dean-Stark distillation device, a Dimroth reflux condenser and a Septum cap were located to a 1-liter four neck flask. The reactor was dried under reduced pressure. After 14.9 g (78 mmol) of TsCl was added to the reaction system, replacement with argon was sufficiently made. The reaction system was cooled to freezing temperature, and 30 ml of dried pyridine was added with paying attention to heat generation. 15 g (78 mmol) of TMA was completely dissolved in 110 ml dried DMF, and then it is added in 30 min. At that temperature, the reaction was continued, and 20.0 g (39 mmol) of the aromatic diol 1cA, which was dissolved in 30 ml dried DMF, was dropped at freezing temperature. After 30 min, an ice bath was taken out, the reaction was continued for 1 hour at room temperature. Thereafter, the reaction system was again cooled to freezing temperature, and 4.84 g (19.5 mmol) of the aromatic diamine 3cA was added to 50 ml dried DMF. After 30 min, the ice bath was taken out, the reaction system was heated to 60 °C using an oil bath and reaction was continued for 30 min. 7.06 g (39.0 mmol) of the aromatic amine 4aA was added to 10 ml dried DMF and reacted for 2.6 hours. Then, 200 ml dried benzene was added and 1.4 ml (theoretical quantity: 1.4 ml) of water was taken out at 145 °C (bath temperature) under azeotrope. After the reaction, the resultant reaction solution was poured to 1000 ml methanol and an esterimideoligomer was precipitated. When the precipitated esterimideoligomer 5cA was filtered under reduced pressure and dried for 48 hours at 80 °C in vacuum, 43.2 g (yield: 94.3 %) of pale yellow powder was obtained. Using 4.5 g of this esterimideoligomer 5cA , press molding was carried out under 180 °C × 10 kg/cm 2 × 1.5 hours. Then, a cast molded plate with 12 mm (width)× 12 cm (length) × 1.3 mm (thickness) was obtained. The results of measurement of various properties of the oligomer 5cA and the cast molded plate are set forth in Table 1 and Table Comparison Example 1 Using 4.5 g of imide type thermosetting type imideoligomer commercially available, press molding was carried out under 230 °C × 10 kg/cm 2 × 1.5 hours. Then, a cast molded plate with 12 mm (width) × 12 cm (length) 1.3 mm (thickness) was obtained. The results of measurement of various properties of the imideoligomer and the cast molded plate are set forth in Table 1 and Table 2. Example 4 A three way cock, a Dean-Stark distillation device, a Dimroth reflux condenser and a Septum cap were located to a 1-liter four neck flask. The reactor was dried under reduced pressure. After 14.9 g (78 mmol) of TsCl was added to the reaction system, replacement with argon was sufficiently made. The reaction system was cooled to freezing temperature, and 30 ml of dried pyridine was added with paying attention to heat generation. 15 g (78 mmol) of TMA was completely dissolved in 110 ml dried DMF, and then it is added in 30 min. At that temperature, reaction was continued, and 13.1 g (39 m mol) of the aromatic diol 1aB , which was dissolved in 30 ml dried DMF, was dropped at freezing temperature. After 30 min, an ice bath was taken out, the reaction was continued for 1 hour at room temperature. Thereafter, the reaction system was again cooled to freezing temperature, and 22.8 g (78.0 mmol) of the aromatic diamine 3aB was added to 5 ml dried DMF. After 30 min, the ice bath was taken out, the reaction system was heated to 60 °C using an oil bath and the reaction was continued for 30 min. 12.8 g (78.0 mmol) of the aromatic acid anhydride 4aB was added to 10 ml dried DMF and reacted for 2.6 hours. Then, 200 ml dried benzene was added and 1.4 ml (theoretical quantity: 1.4 ml) of water was taken out at 145 °C (bath temperature) under azeotrope. After the reaction, the resultant reaction solution was poured into 1000 ml methanol and an esterimideoligomer was precipitated. When the precipitated esterimideoligomer 5aB was filtered under reduced pressure and dried for 48 hours at 80 °C in vacuum, 60.5 g (yield: 97.1 %) of pale yellow powder was obtained. Using 4.5 g of this esterimideoligomer 5aB , press molding was carried out under 230 °C × 10 kg /cm 2 × 1.5 hours. Then, a cast molded plate with 12 mm (width) × 12 cm (length) × 1.3 mm (thickness) was obtained. The results of measurement of various properties of the esterimideoligomer 5aB and the cast molded plate are given in Table 3 and Table 4. Example 5 A three way cock, a Dean-Stark distillation device, a Dimroth reflux condenser and a Septum cap were located a 1-liter four neck flask. The reactor was dried under reduced pressure. After 14.9 g (78 mmol) of TsCl was added to the reaction system, replacement with argon was sufficiently made. The reaction system was cooled to freezing temperature, and 30 ml of dried pyridine was added with paying attention to heat generation. 15 g (78 mmol) of TMA was completely dissolved in 110 ml dried DMF, and then it is added in 30 min. At that temperature, the reaction was continued, and 9.76 g (39 mmol) of the aromatic diol 1bB , which was dissolved in 30 ml dried DMF, was dropped at freezing temperature. After 30 min, an ice bath was taken out, the reaction was continued for 1 hour at room temperature. Thereafter, the reaction system was again cooled to freezing temperature, and 26.1 g (78.0 mmol) of the aromatic diamine 3bB was added to 50 ml dried DMF. After 30 min, the ice bath was taken out, the reaction system was heated to 60 °C using an oil bath and the reaction was continued for 30 min. 13.4 g (78.0 mmol) of the aromatic acid anhydride 4bB was added to 10 ml dried DMF and reacted for 2.6 hours. Then, 200 ml dried benzene was added and 1.1 ml (theoretical quantity ; 1.4 ml) of water was taken out at 145 °C (bath temperature) under azeotrope. After the reaction, the resultant reaction solution was poured into 1000 ml methanol and an esterimideoligomer was precipitated. When the precipitated esterimideoligomer 5bB was filtered under reduced pressure and dried for 48 hours at 80°C in vacuum, 57.6 g (yield: 92.5%) of pale yellow powder was obtained. Using 4.5 g of this esterimideoligomer 5bB , press molding was carried out under 230 °C × 10 Kg/cm 2 × 1.5 hours. Then, a cast molded plate with 12 mm (width)× 12 cm (length) × 1.2 mm (thickness) was obtained. The results of measurement of various properties of the esterimideoligomer 5bB and the cast molded plate are given in Table 3 and Table 4. Example 6 A three way cock, a Dean-Stark distillation device, a Dimroth reflux condenser and a Septum cap were located to a 1-liter four neck flask. The reactor was dried under reduced pressure. After 14.9 g (78 mmol) of TsCl was added to reaction system, replacement with argon was enough made. The reacion system was cooled to freezing temperature, and 30 ml of dried pyridine was added with paying attention to heat generation. 15 g (78 mmol) of TMA was completely dissolved in 110 ml dried DMF, and then it is added in 30 min. At that temperature, the reaction was continued, and 20.3 g (39 mmol) of the aromatic diol 1cB , which was dissolved in 30 ml dried DMF, was dropped at feezing temperature. After 30 min, an ice bath was taken out, the reaction was continued for 1 hour at room temperature. Thereafter, the reaction system was again cooled to freezing temperature, and 19.3 g (78.0 mmol) of the aromatic diamine 3cB was added to 50 ml dried DMF. After 30 min, the ice bath was taken out, the reaction system was heated to 60 °C using an oil bath and the reaction was continued for 30 min. 12.8 g (78.0 mmol) of the aromatic acid anhydride 4aB was added to 10 ml dried DMF and reacted for 2.6 hours. Then, 200 ml dried benzene was added and 1.2 ml (theoretical quantity : 1.4 ml) of water was taken out at 145 °C (bath temperature) under azeotrope. After the reaction, the resultant reaction solution was poured into 1000 ml methanol and an esteimideoligomer was precipitated. When the precipitated esterimideoligomer 5cB was filtered under reduced pressure and dried for 48 hours at 80 °C in vacuum, 58.3 g (yield : 88.3 %) of pale yellow powder was obtained. Using 4.5 g of this esterimideoligomer 5cB , press molding was carried out under 230 °C × 10 Kg/cm 2 × 1.5 hours. Then, a cast molded plate with 12 mm (width) × 12 cm (length) × 1.5 mm (thickness) was obtained. The results of measurement of various properties of the esterimideoligomer 5cB and the cast molded plate are given in Table 3 and Table 4. An esterimideoligomer with reactivity of the present invention is excellent in workability resulting from high resin fluidity and provides hard substances with extremely high heat resistance. In addition, the esterimideoligomer with reactivity of the present invention has excellent mechanical strength, dimensional stability and electric properties. Especially, it is excellent in solubility to solvents, adhesion property with other substances and flexibility, and provides a polyesterimide which is difficult to give birth to voids and cracks in molded products. As mentioned above, an esterimideoligomer with reactivity of the present invention has many characteristics mentioned above, so that it can provide materials extremely high in engineering value for wide usage such as for lamination plates, heat resistant paints, polymer materials for electronic devices and molding materials, and its usefulness is extremely great.

Claims: A thermosetting compound expressed by the general formula(IA): wherein Ar 1 , Ar 2 and Ar 3 may be the same or different and Ar 1 is selected from Ar 2 is selected from Ar 3 is selected from and m is an integer of 1 - 30. A thermosetting compound expressed by the general formula (IB): wherein Ar 1 , Ar 2 and m are as defined in claim 1, Ar 1 , Ar 2 and Ar 4 may be the same or different and Ar 4 is selected from A thermosetting compound as claimed in Claim 1 or 2, wherein Ar 1 is at least one selected from the group consisting of: A thermosetting compound as claimed in Claim 1 or 2, wherein Ar 2 is at least one selected from the group consisting of: A thermosetting compound as claimed in Claim 1, wherein Ar 3 is selected from the following group: A thermosetting compound as claimed in Claim 2. wherein Ar 4 is at least one selected from the group consisting of: A method for producing a thermosetting compound, which comprises the following steps: keeping a reaction system at room temperature or below in an inert gas atmosphere, adding trimellitic acid anhydride dissolved in an aprotic polar solvent to a mixed solution containing paratoluenesulfonic acid chloride and pyridine, adding a diol dissolved in an aprotic polar solvent to cause the reaction proceed, adding the necessary quantity of a diamine dissolved in an aprotic polar solvent for obtaining both end acid anhydride groups-terminated telechelic oligoesteramic acid, adding a primary amine or an acid anhydride dissolved in an aprotic polar solvent to terminate the both ends, and adding a non-solvent to dehydrate and close rings of the reaction product. A method as claimed in Claim 7, wherein the aprotic polar solvent is dimethylformamide. A method as claimed in Claim 7 or 8, wherein the organic tetracarboxylic acid dianhydride is copolymerized.

Inventors: FURUTANI HIROYUKI, FURUTANI, HIROYUKI
Applicants: KANEGAFUCHI CHEMICAL IND, KANEGAFUCHI KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1991
Main classification: C07D209
IPC codes: C08G73, C07D209