Method of inhibiting corrosion in acidizing wells

Abstract: Corrosion inhibitor additives are added directly to an aqueous acid solution used in acidizing subterranean formations. The additives consist essentially of a metal selected from antimony and antimony mixtures, a quaternary compound, and a surfactant. The corrosion inhibitor is free of toxic acetylenic compounds.

Description: This invention relates generally to corrosion inhibitors and more specifically to the use of corrosion inhibitors containing quaternary/antimony complex in acid solutions used in acid treatment of subterranean formations without acetylenic alcohols. In one aspect, the invention relates to the direct addition of the corrosion inhibitor additives directly to the aqueous acid solution used in well acidizing. Acids and acid solutions have long been used in the stimulation of oil wells, gas wells, water wells, and similar boreholes. Acid stimulation is performed in wells completed in subterranean formations. Acidizing is used in conjunction with hydraulic fracturing techniques and matrix acidizing techniques. In both acid fracturing and matrix acidizing, the well treating acid solutions, usually HCl, HF, or mixtures thereof, are pumped through the well tubular goods and injected into the formation where the acid attacks formation materials increasing its permeability to oil and/or gas. In order to protect the equipment and tubular goods from the corrosive effects of the acid, the well treating acid almost always includes a corrosion inhibitor. Corrosion inhibitors of diverse description and composition have been proposed over the years for use with well treating acids. Corrosion inhibitors that have received wide spread use are those containing metal/quaternary ammonium complexes. Some of these are described in the following U.S. Patents: 3,773,465 (cuprous iodide); 4,498,997; 4,522,658; and 4,552,672 (antimony compounds). EP-A-0390317 discloses corrosion inhibitors for use in acid solutions used in acid treatment of subterranean formations which comprise four essential components: a metal compound, an ammonium quaternary compound capable of forming a complex with the metal compound, a highly polar aprotic solvent and an organic amine dispersant. A method of acidizing a subterranean formation is also disclosed which comprises the direct introduction of the complexing components (the metal and quaternary compounds) into the acid solution. In the past, the metal/quaternary complexes, have been used with an acetylenic compound which apparently contributes to the effectiveness of the complex, particularly at high temperatures and high concentrations. Corrosion inhibitors containing acetylenic compounds are toxic. Therefore, it is desirable to avoid the use of the acetylenics where possible. SUMMARY OF THE INVENTION The method of the present invention comprises the steps of separately adding directly to a well treating aqueous acidizing solution containing a surfactant capable of water wetting the pipe corrosion inhibitor additives consisting essentially of: (a) a surfactant; and (b) an antimony compound or antimony metal mixture. Surprisingly, it has been found that the nonacetylenic corrosion inhibitor additives described above, when separately added directly to the aqueous acid solution, exhibit excellent dispersion and provide improved corrosion protection for the well equipment at relatively low concentrations in comparison to corrosion inhibitors with acetylenics and aromatic hydrocarbons. Although the reasons for the improved performance are not fully understood, it is believed that the acetylenic compound and/or the aromatic hydrocarbon solvent interfere with deposition of the antimony on the well tubulars. The concentrations of the three essential additives in the acid solution are as follows: Component BROAD RANGE (wt%) PREFERRED RANGE (wt%) MOST PREFERRED RANGE (wt%) Metal/Metal Mixture Quaternary .04 to 2.0 .05 to 1.0 .07 to .80 Compound 0.2 to 10 0.4 to 5.0 0.4 to 2.2 Surfactant 0.1 to 25 0.1 to 5.0 0.1 to 1.5 Generally, the component ranges are interchangeable. For example, the most preferred range of a metal component may be used with both the broad and preferred ranges of the other components. The metal compound will always include antimony, either alone or as one compound of a binary or ternary blend. At least 0.04 wt% of antimony should be present in the acid. The corrosion inhibitor components are separately introduced into the well treating acid at a concentration sufficient to coat the well tubulars and equipment. The concentration of each component in the acid solution should generally be sufficient to provide the acid solution with from 0.04 wt% to 0.80 wt% of Sb. The method of the present invention provides effective corrosion high temperature protection associated with metal salt complexes and employs low toxicity additives which are separately dispersible in the aqueous acid solution. The method of the present invention offers the operational advantage of direct addition and dispersion in the acidizing solution without preformulation. The corrosion inhibitors with acetylenic compounds of the prior art generally required solvents and premixture of at least some of the components. DESCRIPTION OF PREFERRED EMBODIMENTS As indicated above the method of the present invention employs only three essential additives which combine in situ when added to a well treating acid solution to provide effective corrosion inhibition. Each of these compounds as well as the acid solution in which they are used are described below. Aqueous Acid Solutions : Any of the known oil field acids may be used. These are referred to herein as "well treating acids" and include aqueous solutions of hydrochloric acid (HCl), hydrofluoric acid (HF), mixtures of HCl and HF (i.e. mud acid), acetic acid, formic acid, and other organic acids and anhydrides. The most common acids are 3% HCl, 7 1/2% HCl, 15% HCl, 28% HCl and blends of HCl and HF (mud acid). Mud acid is normally a blend of 6 to 12% of HCl and 1 1/2 to 6% HF. Antimony Compounds and Mixtures : The function of the antimony and/or the metal mixed therewith is to complex with the quaternary ammonium compound and form a protective deposit on the metal tubulars and equipment. Tests have shown that salts of the following metals and mixtures thereof exhibit corrosion protection when complexed with a quaternary ammonium compound or compounds: Sb, Sb/Al, Sb/Al/Cu + , Sb/Cu + , Sb/Ca/Cu + , and Ca/Sb. The preferred metals are Sb alone and Sb, Cu + , and Ca binary and ternary mixtures. The metal salts or mixtures must be readily dispersible in the aqueous acid solution and form a complex with the quaternary ammonium compound. The term "complex" as used herein means a coordination or association of the metal compound with the quaternary compound. The preferred antimony salts and salts of the mixture are halides, specifically metal chlorides. Some of the salts may be formed in situ, in acid solution. For example, antimony chloride is produced from Sb 2 O 3 in aqueous acid such as HCl. The insoluble Sb 2 O 3 is converted to soluble salt. The antimony compound may comprise, for example, antimony trichloride, antimony pentachloride, antimony trifluoride, alkali metal salts of antimony tartrate, antimony adducts of ethylene glycol, and antimony trioxide or any other trivalent or pentavalent antimony compound and the like. As mentioned above, the antimony oxides may be converted to halide salts in the presence of aqueous acid. The cuprous compound may be cuprous iodide as described in U.S. patent 3,773,465. The binary and ternary metal mixtures are preferred for particularly severe corrosive environments since they appear to combine synergistically to provide protection. The binary and fernary metals may be mixed in any ratio, provided Sb constitutes at least 20 wt%, preferably 30 wt%, of the metal mixture. Quaternary Compounds : The quaternary ammonium compounds (referred to as "quaternary" herein) employed in the present invention must be capable of complexing with the antimony and other metals of the metal mixture (if employed). The preferred quaternary comprise aromatic nitrogen compounds which may be illustrated by alkyl pyridine-N-methyl chloride quaternary, alkyl pyridine-N-benzyl chloride quaternary, quinoline -N-methyl chloride quaternary; quinoline-N-benzyl chloride quaternary, quinoline-N-(chloro-benzyl chloride) quaternary, isoquinoline quaternaries, benzoquinoline quaternaries, chloromethyl napthalene quaternaries and admixtures of such compounds, and the like. The quaternary compound and Sb and Sb mixtures may be used in molar ratios of 1:1 to 5:1. Generally, the quaternary compound, because of its higher molecular weight, will be present in the acid solution at a higher concentration than the metal compound. The weight ratios of the quaternary compound and the Sb and Sb mixtures thereof preferably range from 1:1 to 4:1. The Surfactant: The surfactant serves to wet the tubular goods to permit deposition of the quaternary/metal complex. The preferred surfactants are the nonionics having hydrophilic - lipophilic balance (HLB) numbers of 8 to 18, preferably 9 to 16, such as laurates, stearates, and oleates. Nonionic surfactants include the polyoxyethylene surfactants (such as ethoxylated alkyl phenols, ethoxylated aliphatic alcohols) polyethylene glycol esters of fatty, resin, and tall oil acids. Examples of such surfactants are polyoxyethylene alkyl phenol wherein the alkyl group is linear or branched C 8 - C 12 and contains above about 60 wt% polyoxyethylene. Octyl and nonyl phenols containing 9 to 15 moles ethylene oxide per mole hydrophobe are the preferred ethoxylated alkyl phenol surfactants. The polyoxyethylene ester of fatty acids include the mono and dioleates and sesquioleates wherein the molecular weight of the esterified polyethylene glycol is between about 200 and 1000. Polyoxyethylene sorbitan oleates are also useable. In practice, the nonionics may be blended to provide the desired properties. A particularly useful surfactant is a blend of polyethylene glycol esters of fatty acids and ethoxylated alkylphenols. Operation : In operation, the three essential additives are separately added to the aqueous acid solution at the well site. The additives may be added in any order but preferably are in the following order: (1) surfactant; (2) quaternary compound; (3) and metal compound. The concentration of quaternary/metal complex in the acid solution should preferably provide a metal (including Sb) concentration of at 0.050 wt%. The procedure for preparing the inhibited acid for pumping down the well is preferably by a batch process. In this process, the additives are blended into the aqueous acid solution in a large tank and then pumped into the well. It has been found that the direct addition of the additives requires only a few minutes for dispersion and complexing to occur, so that any pumping process including the continuous process may be employed. The batch process, however, is preferred because it assures adequate conditioning of the corrosion inhibitor in the acid prior to pumping. The method of the present invention can be used in wells to protect tubular goods made of typical oil field tubular steels such as J-55, N-80, P:105, and the like; or made of high alloy chrome steels such as Cr-9, Cr-13, Cr-2205, Cr-2250, and the like. EXPERIMENTS In order to demonstrate the effectiveness of the nonacetylenic corrosion inhibitor additives added directly to the acid solution, several samples with and without acetylenics were tested using various components. The additives used in the tests were as follows. The quaternary ammonium compounds used in the experiments was a quinoline-N-benzyl chloride quaternary (quaternary X). The surfactant was nonylphenol (10 mols EO). The HCl acid was 15% HCl. The mud acid was 12% HCl and 3% HF. The acetylenic compounds were a blend of ethyl octynol and propargyl in wt ratios of 1 to 1 or 2 to 3. The Sb compounds were Sb 2 O 3 . The procedure for preparing the aqueous acid solution with inhibitor and the test procedure was as follows (all % are wt% unless otherwise indicated) 1. The additives were added to the aqueous acid solution [(15% HCl or mud acid, (12% HCl/3% HF)] in the following order (a) surfactant (b) acetylenic alcohol (c) aromatic hydrocarbon solvent (if used) (d) quaternary compound (e) Sb 2 O 3 2. The coupouns (N-80 steel or Cr-2205) were then put in the acid solution with the additives and heated to 177°C (350°F) under 20.7 MPa (3,000 psi) for four hours. 3. The coupouns were then removed and cleaned, the weight loss measured, and the corrosion rate calculated. The composition of the samples tested are shown in Tables I and II. ACETYLENIC SAMPLES Additives (wt%) Sample Surfactant Acet. Solvent Quat. Sb Acid A-1 0.37 0.35-0.40 0.37-0.40 1.12 0.075 HCl A-2 0.37 0.35-0.40 0.37-0.40 1.12 0.15 Mud A-3 0.37 0.35-0.40 0.37-0.40 0.60 0.75 HCl A-4 0.37 0.35-0.40 0.37-0.40 0.60 0.75 Mud NONACETYLENIC SAMPLES Additives (wt%) Sample Surfactant Quat. Sb Acid NA-1 0.37 1.12 0.075 HCl NA-2 0.37 1.12 0.15 Mud NA-3 0.37 0.6 0.75 HCl NA-4 0.37 0.6 0.75 Mud The corrosion rates, expressed in units of kg/m 2 (pound/ft 2 ), using the above samples are presented in Table III. HCl Corrosion Rate In N-80 Cr-2205 Sample kg/m 2 (pound/Ft 2 ) kg/m 2 (pound/Ft 2 ) A-1 3.20x10 -3 0.0156 5.37x10 -3 0.0262 NA-1 2.01x10 -3 0.0098 3.24x10 -3 0.0158 A-3 1.95x10 -3 0.0095 1.82x10 -3 0.0089 NA-3 1.15x10 -3 0.0056 1.23x10 -3 0.0060 Mud Acid Corrosion Rate In N-80 Cr-2205 Sample kg/m 2 (pound/Ft 2 ) kg/m 2 (pound/Ft 2 ) A-2 6.19x10 -3 0.0302 3.73x10 -3 0.0182 NA-2 5.02x10 -3 0.0245 2.19x10 -3 0.0107 A-4 1.60x10 -3 0.0078 2.23x10 -3 0.0109 NA-4 1.07x10 -3 0.0052 1.48x10 -3 0.0072 From the Table III data, it can be seen that the nonacetylenic samples (NA) gave improved results in all tests. Additional samples were prepared and tests were carried out using binary and ternary mixtures of Sb. These samples had the compositions shown in Table IV. The corrosion rates in units of kg/m 2 (1b/ft 2 ) using the binary and ternary mixtures of Sb are shown in Table V. HCl Corrosion Rate N-80 Cr-2205 Sample Metal kg/m 2 (pound/Ft 2 ) kg/m 2 (pound/Ft 2 ) A-3 Sb 1.95x10 -3 0.0095 1.82x10 -3 0.0089 NA-5 Sb/Al 1.95x10 -3 0.0095 1.43x10 -3 0.0070 NA-7 Sb/Al/Cu + 2.36x10 -3 0.0115 2.27x10 -3 0.0111 NA-9 Sb/Ca 1.35x10 -3 0.0066 1.23x10 -3 0.0060 NA-11 Sb/Cu + 1.31x10 -3 0.0064 1.76x10 -3 0.0086 NA-13 Sb/Ca/Cu + 1.41x10 -3 0.0069 1.41x10 -3 0.0069 Mud Acid Corrosion Rate N-80 Cr-2205 Sample kg/m 2 (pound/Ft 2 ) kg/m 2 (pound/Ft 2 ) A-4 1.60x10 -3 0.0078 2.23x10 -3 0.0109 NA-6 2.93x10 -3 0.0143 2.56x10 -3 0.0125 NA-8 1.60x10 -3 0.0078 2.68x10 -3 0.0131 NA-10 1.76x10 -3 0.0086 6.15x10 -4 0.0030 NA-12 1.43x10 -3 0.0070 8.40x10 -4 0.0041 NA-14 8.61x10 -4 0.0042 9.63x10 -4 0.0047 A comparison of the Table V data reveals that the nonacetylenic samples (NA) performed generally as good as, and frequently better, than the acetylenic samples (A-3 and A-4). Samples NA-9 through NA-14, containing the binary and ternary mixtures of Sb, Ca and Cu + , gave exceptional results vis-a-vis Samples A-3 and A-4. Although the nonacetylenic Sb and Al mixtures (Samples NA-5 though NA-8) performed generally the same as Samples A-3 and A-4, it is noted that the total metal content of the acetylenic samples was almost 50% higher than the metal content of the nonacetylenic samples. Moreover, the Sb content of the nonacetylenic samples was one-half or less than the Sb content of Samples A-3 and A-4 with the balance being Al or Al/Cu + . It was surprising that substitutina the less expensive Al and Al/Cu + blend in the nonacetylenic samples gave comparable protection as the acetylenic samples, even at the lower total metal content.

Claims: A method of acidizing a subterranean formation penetrated by a borehole which has a metal pipe positioned therein wherein an aqueous acid solution containing 0.1 to 25 wt% of a surfactant capable of water wetting the pipe is pumped down said pipe and into the formation, characterised in that the method comprises the separate addition of corrosion inhibitor additives directly into the aqueous acid solution at a concentration to inhibit corrosion of the metal, said additives consisting essentially of: (a) from 0.04 to 2.0 wt% of antimony; and (b) from 0.2 to 10 wt% of a quaternary ammonium compound capable of forming a complex with the antimony which is soluble in the aqueous acid solution; the said percentages by weight are based on the weight of aqueous acid solution. The method of claim 1 wherein the antimony is added in the form of Sb 2 O 3 and reacts with the acid solution to form SbCl 3 . The method of claim 1 or 2 wherein the concentration of the antimony in the aqueous acid solution is between 0.070 wt% and 0.8 wt%. The method of any one of claims 1 to 3 wherein the aqueous acid solution is selected from HCl and HCl/HF blends. The method of any one of claims 1 to 4 wherein the pipe is made of high alloy chrome steel. The method of any one of claims 1 to 5 wherein the surfactant is nonionic having an HLB no. between 8 and 18. A method according to any one of the preceding claims wherein the additives consist essentially of: (a) from 0.04 to 2.0 wt% of binary and ternary metal mixtures containing antimony, and one or more of Al, Ca, or Cu+; (b) from 0.2 to 10 wt% of a quaternary ammonium compound capable of forming a complex with said metals which are soluble in the aqueous acid solution; and (c) from 0.1 to 25 wt% of a surfactant capable of water wetting the pipe; wherein the percentages by weight are based on the weight of aqueous acid solution. The method of claim 7 wherein the metal mixture is Sb/Al, Sb/Alcu + , Cu + /Sb, Cu + /Ca/Sb, or Ca/Sb. The method of claim 7 wherein the mixture is Sb/Ca, Sb/Cu + , or Sb/Ca/Cu + . The method of claim 7, 8 or 9 wherein Sb comprises at least 20 wt% of the metal mixture. A liquid system suitable for use in the treatment of a subterranean formation comprising: (a) an aqueous acid solution containing from 0.1 to 25 wt% of a surfactant capable of water wetting metal; and (b) nonacetylenic corrosion inhibitor additives consisting essentially of: (i) from 0.04 to 2.0 wt% of an antimony compound or a binary or ternary metal mixture containing antimony and one or more of Al, Ca or Cu + ; and (ii) from 0.2 to 10 wt% of a quaternary ammonium compound capable of forming a complex with the antimony which is soluble in the aqueous acid solution; . characterised in that the system is obtainable by the separate addition of each of the non-acetylenic corrosion inhibitor additives (i) and (ii) to solution a).

Inventors: HOLIFIELD PHYLLIS KAY, LOONEY JAMES ROBERT, MCDOUGALL LEE ALLEN, WILLIAMS DENNIS ALEXANDER, HOLIFIELD, PHYLLIS KAY, LOONEY, JAMES ROBERT, MCDOUGALL, LEE ALLEN, WILLIAMS, DENNIS ALEXANDER
Applicants: EXXON CHEMICAL PATENTS INC, EXXON CHEMICAL PATENTS INC.
Application year: 1991
Main classification: E21B41
IPC codes: C09K8, C23F11