A suspending medium for water soluble polymer

Abstract: A new stable liquid suspension of water soluble polymer, and a method of preparation are provided. Such compositions comprise of at least an iso-parrafinic oil medium, one styrene/isoprene copolymer, a water soluble polymer and preferably some hydrophobic fumed silica mixed together in the appropriate quantities and conditions.

Description: Background of the invention This invention relates to preparing stable suspensions of water soluble polymers. Water soluble polymers suspensions are commonly used for oil field drilling fluids and cementing applications. The industry goal has been, and still is, to improve on the process of making and using these suspensions, and also to improve on their intrinsic efficiency. By the term intrinsic efficiency is meant to eliminate or substantially minimize the formation of agglomerates that do not hydrate easily. Attemps to meet the above stated goals are known in the art. Such efforts have employed a wide variety of methods and agents inclusive of organophyllic clay, water, surfactants, fatty acids, and a specially prepared controlled moisture content polymer. US patent 4 726 912 for example discloses stable suspension of carboxymethyl cellulose (CMC) and a process for their preparation, wherein the CMC must have a moisture content of 12-25 weight% water. To prepare this suspension hydrocarbon arts, anionic surfactants (sulfonates) and suspending agents (silica) are utilized. French patent 1 569 499 is another attempt of providing a water soluble polymer suspension. Although these methods and/or compositions individually and collectively have improved on the art, the ultimate goal of providing an ideal suspension i.e. one which is easy to manufacture, remains stable and is useable over a wide temperature range, remains to be met. Summary of the Invention It is an object of this invention to provide a stable liquid suspension of a water soluble polymer. It is a further object of this invention to provide stable liquid suspensions of water soluble polymers that are useable over a wide temperature range. It is also another object of this invention to provide a process for making an improved composition of a stable liquid suspension of a water soluble polymer. It is a further object of this invention to provide a process which is easier to practice than prior art processes. Detailed Description of the Invention According to the present invention a stable liquid suspension of water soluble polymer as provided, comprising: a) an oil selected from the group consisting of diesel, kerosene, heating oil, decane, tetradecane, hexadecane, dodecane, mixed C 13 -C 14 isoparaffins, C 14 isoparaffins and C 16 isoparaffins soybean oil and corn oil, wherein said oil is present in the range of from 40 weight percent to 95 weight percent; b) an oil soluble resin selected from the group consisting of styrene-isoprene copolymers, hydrogenated styrene-isoprene block copolymers, styrene ethylene/propylene block copolymers, styrene isobutylene copolymers, styrene butadiene copolymers, polybutylene, polystyrene, and polyethylene-propylene copolymers, wherein said oil soluble resin is present in the range of from 0.2 weight percent to 10 weight percent; c) a water soluble polymer selected from the group consisting of Xanthanthin gum biopolymers, polyacrylamides, carboxymethylcellulose, and carboxymethylhydroxyethylcellulose, wherein said water soluble polymer is present in the range of from 3 weight percent to less than 60 weight percent, wherein the total of all weight percentages equals 100 weight percent. In a preferred embodiment the composition also includes silica. These compositions do not generally require additional processing in order to be used. Because of its exceptional stability the liquid suspension of the invention can be prepared and shipped to customers ready to use and do not need to be prepared in the field. Preferred, however, are block copolymers, examples of which include but are not limited to styrene ethylene/propylene block copolymer, hydrogenated styrene-isoprene block copolymers and styrene butadiene copolymer. Most particularly preferred are hydrogenated styrene-isoprene block copolymers, examples of which include but are not limited to materials sold under the trademarks "BARARESIN VIS" (trademark of Baroid Corporation), "SHELLVIS 40" and "SHELLVIS 50" (both trademarks of Shell Chemical Company). Examples of water soluble polymers useful in the practice of this invention and the methods for producing and/or obtaining them are disclosed in Bishop U.S. Patent 4,735,659. (See in particular column 1, line 45 to column 2, line 60.) Particularly preferred is carboxymethyl cellulose (CMC). Also useful are water soluble Xanthanthin gum biopolymers, polyacrylamides, and carboxymethylhydroxyethylcellulose. The silica useful for the practice of this invention generally includes fumed silicas, colloidal silicas, and precipitated silicas. Preferred, however, are fumed silicas, hydrophyllic fumed silica, and hydrophobic fumed silica. Distinctly preferred is hydrophobic fumed silica. Examples of this class of silica, method for making it, and other pertinent information relating to its useage is disclosed in Bishop U.S. Patent 4,735,659. (See in particular column 2, lines 61-68.) The ranges of the ingredients listed above useful in the practice of this invention are as shown in Table 1 below. Composition Components Broad (%) Preferred (%) Most Preferred (%) Oil 40-95 55-60 57-59 Resin 0.2-10 1.8-5 2-2.5 Water Soluble Polymer 3-less than 60 37-less than 45 38-40 Silica 0-10 0.5-1 0.7-1.0 The reaction conditions for carrying out the practice of the invention are as follows: The temperature is generally in the range of about -10°C to about 200°C, with a preferred range of about 0°C to about 150°C, and a most preferred range of about 60°C to about 70°C. The reaction time is generally in the broad range of about 0.05 hours to about 200 hours, with a preferred range of about 0.25 hours to about 20 hours, and a most preferred range of about 1 hour to about 2 hours. It is noted that the reaction time is generally inversely proportional to the reaction temperature i.e., the lower the temperature the more time is required. In one embodiment, the process of this invention comprises introducing a suitable oil into a suitable mixing device and adding a suitable resin to the oil in the mixing device. The oil-resin mixture is then mixed for about 30-45 minutes at a temperature range of about 60°C to about 70°C. To this oil-resin mixture is then added a polymer blend comprising about 98 weight percent of a water soluble polymer and 2 weight percent hydrophobic fumed silica. The end product of this process comprising a stable liquid suspension of a water soluble polymer can then be collected by any technique known in the art. While the order of mixing is not a critical aspect of this invention, it is preferred to add the oil first and the polymer last. The addition of an anitoxidant, a surfactant, a biocide, or even a minimal amount of an organophyllic clay to these basic ingredients is an option which will be frequently exercised by those of skill in the art. The product of this invention normally has a gel strength that is capable of suspending particulate matter. Additionally, this gel strength develops very rapidly or almost immediately and is of the type referred to in the art as flat gels. By this is meant that unlike normal gels, its gel strength stays constant or increases only slightly with time and that it has desirable fragile properties evidenced by the ease with which it pours. The product of this invention is primarily tested by observation for syneresis, pour point, and stability over a wide temperature range. Syneresis can be measured by means of a ruler or other such graduated device. This can be accomplished by inserting the ruler or graduated device through the clear liquid portion of the suspension until it contacts the interface that separates this portion, from the layer containing suspended solids. The thickness of the clear liquid layer, the measure of syneresis, can then be determined directly on the ruler or graduated device. The following examples further illustrate the various aspects of this invention. Inventive Composition 1 This example includes the following components: light isoparrafin oil 700 g oil soluble resin 20 g water soluble polymer (CMC) 387 g Total 967 g The oil soluble resin was sheared into the light isoparrafin oil with a Ross mixer at a setting of 5 until the temperature reached 140°F (60°C). The mixer was then shut off and the mixture allowed to cool to near room temperature. Shearing was then continued until all of the oil soluble resin was incorporated (visual observation). The carboxymethyl cellulose (CMC) was then blended into the mixture. The sample was then split into three (3) 1-pint (0,473 l) units. Unit 1 was then vibrated for three (3) days to simulate transport. Very slight syneresis was noted but no settling was observed. Unit 2 was placed in a freezer at -20°F (-29°C) until the temperature stabilized. No syneresis or settling was observed and the sample remained pourable. Unit 3 was placed in an oven at 120°F (49°C) and static aged for six months. About 1/8" (0,32 cm) syneresis was observed but no hard settling was observed. This demonstrates that a stable liquid suspension of a water soluble polymer is obtained. While some syneresis occurred, no precipitation occurred. This composition has better stability than presently commercially available suspensions of water soluble polymers. Inventive Composition 2 This composition comprises the following components: light isoparrafin oil 9845g oil soluble resin 351.6g water soluble polymer and silica 6803.5g The oil soluble resin was added to the isoparrafin oil and mixed on a Ross mixer until the mixture temperature reached 62°C (143.6°F). The mixture of water soluble polymer and silica was then added to the oil/resin mixture and blended well. Three 1-pint (0,473 l) samples were then taken from the mixture. Sample No. 1 of these three samples was vibrated for three (3) days to simulate transport. No syneresis or settling was observed after a six month period. A portion of Sample No. 1 was also heat aged at 120°F (49°C) for six months with no syneresis or settling observed. The temperature was then increased to 150°F (66°C) and no syneresis or settling was observed after a two month period. Sample No. 2 of these three samples was placed in a freezer at -20°F (-29°C) until the temperature stabilized. No syneresis or settling was observed and the sample remained pourable during the six month period of the tests. The third sample was static shelf aged for 6 months with no syneresis or settling observed. This demonstrates that the addition of silica to the basic inventive composition is a desirable and useful improvement. This results in a suspension of even greater stability and better properties than the basic inventive composition as shown in Inventive Composition 1. Inventive Composition 3 This composition was made identical to Inventive Composition 2 above, except for the omission of silica. Three 1 pint (0,473 l) samples were also collected and subjected to the same respective conditions as with those of Inventive Composition 2. No hard settling was observed in any of these samples. However, about 1/8" (0,32 cm) syneresis was observed in the samples that were heat aged and/or static shelf aged for six months. This demonstrates that this composition although stable, is less so than the composition containing silica. Inventive Composition 4 This composition comprises the following components: light isoparrafin oil 560g oil soluble resin 20g water soluble polymer 387g silica 2 wt% The light isoparrafin oil was blended with the oil soluble resin on a high shear Ross mixer until all the resin predusted with the silica, was incorporated and the temperature stabilized at 62°C (143.6°F). A split of the sample was taken and placed in a freezer at -20°F (-29°C) for test of pour point. It poured at -20°F (-29°C) and remained pourable after 6 months. A split of the sample was taken and placed in an oven at a temperature of 120°F (49°C) for six months. No syneresis or settling was observed. After 6 months, the oven temperature was increased to 150°F (66°C). No increase in syneresis and no settling was observed eight weeks later. This demonstrates that stable liquid suspensions of xanthan gum biopolymers can be made by employing the method and components of this invention. Inventive Composition 5 This formulation was made identical to that of Inventive Composition 4 except for the substitution of the xanthan gum biopolymer with a polyacrylamide. The samples were tested under similar conditions as in Inventive Composition 4. Results obtained were similar to those of Inventive Composition 4. This example further demonstrates that another kind of water soluble polymer is useful in the practice of this invention. Inventive Composition 6 This formulation was made identical to that of Inventive Composition 4 except for the substitution of the xanthan gum biopolymer with carboxymethyl hydroxyethyl cellulose. The samples were likewise tested under similar conditions as those of Inventive Composition 4. Similar results were obtained.

Claims: A stable liquid suspension of water soluble polymer comprising: a) an oil selected from the group consisting of diesel, kerosene, heating oil, decane, tetradecane, hexadecane, dodecane, mixed C 13 -C 14 isoparaffins, C 14 isoparaffins and C 16 isoparaffins soybean oil and corn oil, wherein said oil is present in the range of from 40 weight percent to 95 weight percent; b) an oil soluble resin selected from the group consisting of styrene-isoprene copolymers, hydrogenated styrene-isoprene block copolymers, styrene ethylene/propylene block copolymers, styrene isobutylene copolymers, styrene butadiene copolymers, polybutylene, polystyrene, and polyethylene-propylene copolymers, wherein said oil soluble resin is present in the range of from 0.2 weight percent to 10 weight percent; c) a water soluble polymer selected from the group consisting of Xanthanthin gum biopolymers, polyacrylamides,carboxymethylcellule, and carboxymethylhydroxyethylcellulose, wherein said water soluble polymer is present in the range of from 3 weight percent to less than 60 weight percent, wherein the total of all weight percentages equals 100 weight percent. The stable liquid suspension of claim 1, wherein optionally there is present a silica selected from the group consisting of fumed silica, colloidal silicas and precipitated silicas, wherein said silica is present in the range of from 0 weight percent to 10 weight percent, wherein the total of all weight percentages is 100 weight percent. The stable liquid suspension of claim 2, wherein: said oil is present in an amount within the range of 55 to 60 weight percent; said oil soluble resin is present in an amount within the range of 1.8 to 5 weight percent; said water soluble polymer is present in an amount within the range of 37 to less than 45 weight percent; and said silica is present in an amount within the range of 0.5 to 1 weight percent wherein the total of all weight percentages equals 100 weight percent. A stable liquid suspension of claim 2 wherein: said oil is present in an amount within the range of 57 to 59 weight percent; said oil soluble resin is present in an amount within the range of 2 to 2.5 weight percent; and said water soluble polymer is present in an amount within the range of 38 to 40 weight percent; said silica is present in an amount within the range of 0.7 to 1 weight percent. A stable liquid suspension of water soluble polymer as in claim 1 or 2 wherein: said water soluble polymer is carboxymethylcellulose (CMC) present in an amount within the range of 38 to 40 weight percent; said oil soluble resin is a hydrogenated styrene-isoprene block copolymer present in an amount within the range of 2 to 2.5 weight percent; and said oil is an isoparaffinic oil as defined in claim 1 present in an amount within the range of 57 to 59 weight percent. The stable liquid suspension of one of the claims 2 to 4 wherein the silica is a fumed silica, in particular a hydrophobic fumed silica. A stable liquid suspension of water soluble polymer as in one of claims 1 to 7 wherein the silica is hydrophobic fumed silica, the water soluble polymer is carboxymethycellulose (CMC), the oil is an isoparrafinic oil as defined in claim 1, and the oil soluble resin is a hydrogenated styrene-isoprene block copolymer. A process for preparing a stable liquid suspension of a water soluble polymer comprising the following (sequential) steps: a) mixing an oil soluble resin into an oil; b) adding a water soluble polymer into a) to form a composition; c) prior to step b) optionally blending silica into the mixture of a) and/or into said water soluble polymer; d) heating said composition of b) to form a stable liquid suspension; and e) collecting the resulting suspension, wherein the kinds and quantities of materials used are as defined in any one of claims 1 to 7.

Inventors: BISHOP MARSHALL D, HOSTETTLER JOHN EDWARD, BISHOP, MARSHALL D., HOSTETTLER, JOHN EDWARD
Applicants: PHILLIPS PETROLEUM CO, PHILLIPS PETROLEUM COMPANY
Application year: 1991
Main classification: C08L1
IPC codes: C09D191, C04B28, C08J3, C08L5, C08F2, E21B21, C09K8