Optical mask using phase shift and method of producing the same

Abstract: A phase shift optical mask is used for exposing a pattern using an exposure light. The phase shift optical mask includes a substrate (1, 6) which is transparent with respect to the exposure light, a light-blocking layer (2, 3; 7, 8) which is non-transparent with respect to the exposure light and is provided on the substrate, where the light-blocking layer has an opening (5, 10) having a predetermined shape and size and being defined by a side wall of the light-blocking layer, and a phase shift layer (4, 9) which is transparent with respect to the exposure light and is provided on the light-blocking layer and the substrate which is exposed within the opening. The phase shift layer (4, 9) has a uniform thickness, and the light-blocking layer (2, 3; 7, 8) has a predetermined thickness (PS) so that a phase of the exposure light transmitted through the phase shift layer provided on the side wall of the light-blocking layer is shifted by approximately 180° relative to a phase of the exposure light transmitted through the phase shift layer provided on the substrate.

Description: The present invention generally relates to optical masks and methods of producing the same, and more particularly to an optical mask which uses a phase shift exposure to improve the resolution, and a method of producing such an optical mask. There are demands to increase the operating speed of large scale integrated circuits (LSIs) such as a memory device having a large memory capacity and to improve the integration density of the LSIs. For this reason, there are demands to realize a fine photolithography technique. One prominent means of satisfying the above demands is the phase shift exposure technique which employs an optical mask using a phase shift, and a coherent light source which emits an exposure light having a wavelength which is as short as possible. The optical mask using the phase shift will hereinafter referred to as a phase shift optical mask. FIG.1 shows in cross section an example of a conventional phase shift optical mask. The phase shift optical mask shown in FIG.1 includes a glass substrate 11, a chromium (Cr) layer 12 and a silicon dioxide (SiO 2 ) layer 13 which forms a phase shift part. When producing this phase shift optical mask, the Cr light blocking layer 12 which blocks the exposure light is formed on the entire surface of the glass substrate 11 which is transparent with respect to the exposure light. Then, the SiO 2 layer 13 which is also transparent with respect to the exposure light is formed on the Cr light blocking layer 12 to a thickness such that the phase of the exposure light is shifted by 180°. Thereafter, a resist layer (not shown) with an opening is formed on the SiO 2 layer 13 and the SiO 2 layer 13 is etched using a photolithography technique so as to form an opening 14. This opening 14 has the size and shape of a predetermined main light transmitting part. Next, the SiO 2 layer 13 is used as a mask and the Cr light blocking layer 12 which is within the opening 14 is subjected to an isotropic etching. As a result, the SiO 2 layer 13 overhangs above the Cr light blocking layer 12 to form the phase shift part. However, when the phase shift optical mask is subjected to a cleaning or brushing during the production stage or in a stage before the phase shift optical mask is actually used, there are problems in that the SiO 2 layer 13 easily separates from the Cr light blocking layer 12 and that a part of the SiO 2 layer 13 may become damaged and come off the phase shift optical mask. Further, when producing the phase shift optical mask by the conventional technology, there is a limit to the precision with which the patterns may be formed by the photolithography technique. For this reason, there is problem in that it is extremely difficult to form in the SiO 2 layer 13 an opening which has a desired size and shape. In addition, when subjecting the Cr light blocking layer 12 to a side etching, there is also a problem in that it is difficult to control the side etching quantity. In other words, the light intensity distribution of the exposure light transmitted through the phase shift optical mask is dependent on the width L2 of the SiO 2 layer 13 overhanging the Cr light blocking layer 12, as will be described hereunder. FIG.2A shows the light intensity distribution of the exposure light transmitted through the phase shift optical mask shown in FIG.1 when L1 = 0.50 µm and L2 = 0.15 µm, where L1 denotes the width of the Cr light blocking layer 12. Similarly, FIG.2B shows the light intensity distribution for thecase where L1 = 0.5 µm and L2 = 0.20 µm, and FIG.2C shows the light intensity distribution for the case where L1 = 0.50 µm and L2 = 0.10 µm. In other words, FIGS.2B and 2C respectively show the distributions for the cases where the width L2 of the SiO 2 layer (phase shift part) 13 varies by ±0.05 µm over the wafer. In FIGS.2A to 2C, the solid line indicates the distribution at a defocus of 0.000 µm, the dashed line indicates the distribution at a defocus of 0.300 µm, a fine dotted line indicates the distribution at a defocus of 0.600 µm, the one-dot chain line indicate the distribution at a defocus of 0.900 µm, and the two-dot chain line indicates the distribution at a defocus of 1.200 µm. Further, the wavelength λ of the exposure light is 0.365 µm, the numerical aperture (NA) of the exposure lens is 0.54, and the coherency factor σ is 0.30. In the case shown in FIG.2B, the resist layer on the wafer is exposed by the peaks appearing on both sides of the distribution, and more of the resist layer is developed when compared to the case shown in FIG.2A. The width of the opening in the resist layer after the developing is approximately the distance in the distribution at the light intensity of 0.3. In the case shown in FIG.2B, the width of the opening in the resist layer is 0.35 µm which is slightly smaller than the width of 0.36 µm which is obtained in the case shown in FIG.2A. On the other hand, in the case shown in FIG.2C, the width of the opening in the resist layer is 0.39 µm which is considerably greater than the 0.36 µm obtained in the case shown in FIG.2A. Therefore, it can be seen that the deviation of ±0.05 µm of the width L2 exceeds the tolerable deviation range. The side etching of the Cr layer 12 lacks stability, and the side etching rate is greatly dependent on the conditions of the preprocess carried out before the side etching and also the etching pattern or etching area. Particularly, the side etching rate varies from 0.03 µm/min to 0.07 µm/min, and under this variation range, an error of 0.05 µm appears on the wafer at 3σ. Therefore, as described above, it is extremely difficult to control the width L2 of the SiO 2 layer 13 to a desired value which is within a tolerable range when the side etching of the Cr layer 12 is required. Accordingly, it is a general object of the present invention to provide a novel and useful optical mask and method of producing the same, in which the problems described above are eliminated or reduced. The present invention relates to a phase shift optical mask used for exposing a pattern using an exposure light, comprising a substrate which is transparent with respect to the exposure light, a light-blocking layer which is non-transparent with respect to the exposure light and is provided on the substrate, where the light-blocking layer has an opening having a predetermined shape and size and being defined by a side wall of the light blocking layer, and a phase shift layer which is transparent with respect to the exposure light and is provided on the light blocking layer and the substrate which is exposed within the opening. The phase shift layer has a uniform thickness, and the light blocking layer has a predetermined thickness so that the phase of the exposure light transmitted through the phase shift layer provided on the side wall of the light-blocking layer is shifted by approximately 180° relative to the phase of the exposure light transmitted through the phase shift layer provided on the substrate. The invention is characterised in that the light-blocking layer is made up of a first layer which is non-transparent with respect to the exposure light and a second layer which is provided on the first layer, the said predetermined thickness being the sum of the thicknesses of the first and second layers. With the invention it is possible to improve the resolution and expose a fine pattern exceeding the limit of the conventional photolithography technique. In addition, no damage is made to the optical mask during the cleaning and brushing processes. In a further aspect of the present invention there is provided a method of producing a phase shift optical mask for exposing a pattern using an exposure light, comprising the steps of: (a) forming a light-blocking layer on a substrate, the light-blocking layer being non-transparent with respect to the exposure light while the substrate is transparent with respect to the exposure light, the light-blocking layer comprising a first layer which is non-transparent with respect to the exposure light on said substrate, and an upper layer on the first layer, (b) forming an opening having a predetermined shape and size in the light-blocking layer, defined by a side wall of the light-blocking layer; and (c) forming a phase-shift layer which is transparent with respect to the exposure light on the light-blocking layer and on that part of the substrate which is exposed within the opening, the phase-shift layer being formed to a uniform thickness, the light-blocking layer having a predetermined thickness, being the sum of the thickness of the first and upper layers, such that the phase of the exposure light transmitted through the part of the phase-shift layer provided on the side wall of the light-blocking layer is shifted by approximately 180° relative to the phase of the exposure light transmitted through the part of the phase-shift layer provided on the substrate According to the method of the present invention, it is possible accurately to form an opening using the conventional photolithography technique, and the size of the opening can be reduced to a point exceeding the limit of this technique without the accuracy deteriorating. Embodiments of the present invention, and of a related invention in divisional application No. 98101274.3, will now be described in order to facilitate understanding of the invention. In the drawings:- FIG.1 is a cross sectional view showing an essential part of an example of a conventional phase shift optical mask; FIGS.2A to 2C respectively show light intensity distributions of exposure light transmitted through the phase shift optical mask under different conditions; FIG.3A is a cross-sectional view for explaining an operating principle of an optical mask according to the present invention; FIG.3B shows amplitude and phase characteristicsof transmitted light in correspondence with FIG.3A; FIG.3C shows amplitude and phase characteristicsof synthesized transmitted light in correspondence with FIG.3A; FIG.3D shows the intensity of transmitted light in correspondence with FIG.3A; FIG.4 is a cross-sectional view showing an essential part of a first embodiment of the optical mask according to the invention; FIG.5 generally shows an exposure apparatus to which the first embodiment of the optical mask according to the invention may be applied; FIG.6 is a plan view showing an actual pattern formed on a wafer using the optical mask; FIG.7A is a cross sectional view for explaining a conventional phase shift optical mask; FIG.7B shows amplitude and phase characteristicsof light transmitted through a light-transmitting region of the phase shift optical mask shown in FIG.7A; FIG.7C shows amplitude and phase characteristicsof light transmitted through a phase shift region of the phase shift optical mask shown in FIG.7A; FIG.7D shows the intensity of transmitted light in correspondence with FIG.7A; FIG.8A is a cross sectional view for explaining another conventional phase shift optical mask; FIG.8B shows amplitude and phase characteristicsof light transmitted through a light-transmitting region of the phase shift optical mask shown in FIG.8A; FIG.8C shows amplitude and phase characteristics of light transmitted through a phase shift region of the phase shift optical mask shown in FIG.8A; FIG.8D shows the intensity of transmitted light in correspondence with FIG.8A; and FIGS.9 to 12 are views illustrating an optical mask embodying a related invention as claimed in divided-out application No. 98101274.3. First, a description will be given of the operating principle of an optical mask using the present invention, referring to FIGS.3A to 3D. FIG.3A shows a phase shift optical mask including a glass substrate 1, a light-blocking layer 2, a first inorganic layer 3 and a second inorganic layer 4. A main light-transmitting part A is surrounded by a phase shift part B. The first and second inorganic layers 3 and 4 are respectively made of an inorganic material, and the second inorganic layer 4 has a thickness T. The total thickness PS of the light-blocking layer 2 and the first inorganic layer 3 corresponds to a phase shift of approximately 180°. Next, a description will be given of the resolution improving effect which is obtained by the edge emphasis type phase shift optical mask according to Fig. 3A. FIG.3B shows the amplitude and the phase characteristic of the light which is transmitted through the main light transmitting part A and the phase shift part B of the phase shift optical mask. Curve I indicates the light transmitted through the main light transmitting part A, and curveII indicates the light transmitted through the phase shift part B. As may be seen from FIG.3B, the phase of the light transmitted through the phase shift part B is shifted by 180° with respect to the phase of the light transmitted through the main light transmitting part A. FIG.3C shows the amplitude and the phase characteristic of the synthesized light in which the light transmitted through the main light-transmitting part A and the light transmitted through the phase shift part B are superimposed. The curve III of this synthesized light is sharper than curve I because, at the bottom of curve III, the light transmitted through the main light transmitting part A is cancelled by the light which is transmitted through the phase shift part B and has an inverted phase with respect to the light transmitted through the main light-transmitting part A. In FIG.3D, curve IV indicates the intensity of the transmitted light. This curve IV corresponds to the square of the amplitude indicated by the curve III shown in FIG.3C. The curve IV is very sharp because of the light transmitted through the phase shift part B. Hence, it may be seen from FIG.3D that the resulution is improved when carrying out the exposure. Next, a description will be given of a method of producing the phase shift optical mask shown in FIG.3A. First, the light-blocking layer 2 is formed on the entire surface of the glass substrate 1, and the first inorganic layer 3 is formed on the entire surface of the light blocking layer 2. The total thickness PS of the light blocking layer 2 and the first inorganic layer 3 is set so that the exposure light is shifted by 180° by the second inorganic layer 4 which is later formed. The thickness PS for realizing the 180° phase shift by use of the second inorganic layer 4 is calculated as follows. Since the propagation velocity of the exposure light is inversely proportional to the refractive index of the medium through which the exposure light propagates, the thickness of the medium should be set to λ/2(n-1) when shifting the phase of the exposure light by 180° compared to the exposure light propagating through air, where n denotes the refractive index of the medium and λ denotes the wavelength of the exposure light. It is in principle unnecessary to provide the first inorganic layer 3 if the thickness PS can be realized using only the light blocking layer 2. However, when forming the light blocking layer 2 from a metal, problems are introduced due to a difference between coefficients of thermal expansion of the layers if the metal light blocking layer 2 is made thick. Furthermore, when the metal light blocking layer 2 is thick, the etching of the metal light blocking layer 2 at the later stage becomes that much more difficult. For this reason, there is according to the invention formed on the light blocking layer 2 the first inorganic layer 3 which has approximately the same coefficient of thermal expansion as that of the glass substrate 1, and to adjust the thickness PS by the total thickness of the light blocking layer 2 and the first inorganic layer 3. Second, an opening 5 for exposure is formed in the first organic layer 3 and the light blocking layer 2 by a photolithography technique. The width of this opening 5 is A+2T, where A denotes the width of the main light transmitting part A after completion and T denotes the thickness of the second inorganic layer 4 which is later formed. Hence, the width of the opening 5 is 2T wider than the width of the opening 14 of the conventional phase shift optical mask shown in FIG.1, thereby making it possible to accurately form the opening 5 with a satisfactory reproducibility using the normal photolithography technique. Third, the second inorganic layer 4 is formed on the first inorganic layer 3 and the glass substrate 1 which is exposed within the opening 5, using chemical vapor deposition (CVD) or the like. The thickness of the second inorganic layer 4 which is formed by the CVD is uniform, and the thickness T of the second inorganic layer 4 deposited on the first inorganic layer 3 can be made the same as the width T of the second inorganic layer 4 which is deposited on the inner wall defining the opening 5. In this case, the depression of the stepped part which is formed at the surface of the second inorganic layer 4 is maintained the same as the total thickness PS of the light blocking layer 2 and the first inorganic layer 3. Thus, the depression functions as the main light transmitting part A, and the region of width T that is formed on the outer side of the depression on each side functions as the phase shift part B. Therefore, the size of the completed main light transmitting part A can be controlled accurately using the width A+2T of the opening 5 as a reference, which opening 5 is formed by the normal photolithography technique. Next, a description will be given of an embodiment of the optical mask according to the present invention, by referring to FIG.4. The phase shift optical mask 34 shown in FIG.4 includes a Cr light-blocking layer 7 which is formed on a quartz glass substrate 6, a SiO 2 first inorganic layer 8 which is formed on the Cr light blocking layer 7, an opening 10 which is formed in the SiO 2 first inorganic layer 8 and the Cr light blocking layer 7, and a SiO 2 second inorganic layer 9 which is formed on the SiO 2 inorganic layer 8 and the quartz glass substrate 6 which is exposed within the opening 10. The SiO 2 second inorganic layer 9 is transparent with respect to the exposure light. A main light transmitting part A is surrounded by the phase shift part B. This first embodiment of the optical mask according to the present invention may be produced as follows. According to the first embodiment of the method, the Cr layer 7 is formed on the quartz glass substrate 6 and the SiO 2 layer 8 is formed on the Cr layer 7, so that the total thickness of the Cr layer 7 and the SiO 2 layer 8 becomes 4700 Å. The total thickness of the Cr layer 7 and the SiO 2 layer 8 is calculated as follows. That is, since the propagation velocity of the exposure light is inversely proportional to the refractive index of the medium through which the exposure light propagates, the thickness of the medium should be set to λ/2(n-1) when shifting the phase of the exposure light by 180° compared to the exposure light propagating through air, where n denotes the refractive index of the medium and λ denotes the wavelength of the exposure light. Hence, in the case where the light source is a mercury discharge lamp which emits as the exposure light a g-ray having a wavelength of 4358 Å and the refractive index n of the SiO 2 layer 9 is 1.46, the total thickness of the Cr layer 7 and the SiO 2 layer 8 can be calculated from λ/2(n-1) as 4737 Å or approximately 4700 Å. Next, a resist layer (not shown) is formed on the entire surface of the SiO 2 layer 8, and a resist mask pattern having an opening is formed by a normal electron beam exposure technique. One side of this opening in the resist mask pattern has a length of 1.1 x m µm when a reducing projection magnification of a reducing projection type exposure apparatus used is m. Thereafter, the SiO 2 layer 8 and the Cr layer 7 are selectively removed via this opening in the resist mask pattern using a dry etching, thereby forming an opening 10. Then, the SiO 2 layer 9 is deposited to a thickness of 1 µm on the entire surface of the SiO 2 layer 8 and the quartz glass substrate 6 which is exposed within the opening 10 using a CVD. This thickness of the SiO 2 corresponds to 0.2 x m µm when m = 5. The phase shift optical mask 34 which is produced by the above described processes has a square main light transmitting part A having a side of 0.7 x m µm, and a frame shaped phase shift part B having a width of 0.2 x m µm. When m = 5 in this embodiment, for example, the square opening in the resist mask pattern which is formed on the SiO 2 layer 8 has a side of 5.5 µm, and when the phase shift optical mask 34 is completed, the square main light transmitting part A has a side of 3.5 µm and the frame shaped phase shift part B has a width of 1 µm. When producing a semiconductor device using the first embodiment of the phase shift optical mask described above, a resist layer which is formed on a semiconductor surface is exposed by passing a g-ray having a wavelength of 4358 Å from a mercury discharge lamp through an optical pattern of the phase shift optical mask 34 and projecting the transmitted g-ray on the resist layer with a size reduction to 1/5, for example. In this case, the NA of the exposure lens is 0.45. FIG.5 generally shows an exposure apparatus which is used for carrying out the first embodiment of the method. The g-ray emitted from a mercury discharge lamp 31 irradiates the phase shift optical mask (or reticle) 34 via a condenser lens 32 and an iris 33, and the g-ray transmitted through the phase shift optical mask 34 is converged and irradiates a wafer 36 via a projection lens 35. The wafer 36 corresponds to the semiconductor surface referred above, and the resist layer which is exposed is formed on the wafer 36. According to the first embodiment of the optical mask and the first embodiment of the method, the width T of the SiO 2 layer (phase shift part) 4,9 can be controlled accurately by controlling the deposition thickness of the SiO 2 layer 4,9. Using the existing techniques, the deposition thickness of the SiO 2 layer 4,9 can be controlled within the range ±0.02 µm on the phase shift optical mask 34. However, on the wafer 36, this range is reduced to 1/5 due to the reduced production, and the error on the wafer 36 is of the order of ±0.004 µm at 3σ. This error of ±0.004 µm is considerably smaller than the error of ±0.05 µm which is introduced in the conventional case described above. FIG.6 shows a plan view of an actual pattern which is formed on the wafer 36 using the optical mask 34. For example, the optical mask 34 is particularly suited for use in forming a fine aperture 340 of the pattern shown in FIG.6. As described above in conjunction with the prior art, the phase shift optical mask was developed to improve the resolution of the photolithography technique. The phase shift optical mask includes a first region for transmitting the exposure light as it is and a second region for inverting the phase of the exposure light, and the second region is formed adjacent to or in a vicinity of the first region. The widths of the first and second regions are determined by the wavelength of the exposure light and the NA of the exposure lens, and these first and second regions effectively utilize the light interference. FIG.7A shows a first conventional phase shift optical mask including a glass substrate 21, a Cr light blocking layer 22 and a SiO 2 phase shift layer 23. The amplitude of the exposure light which is transmitted through a light transmitting region 24 of this phase shift optical mask is shown in FIG.7B, while the amplitude of the exposure light which is transmitted through the SiO 2 phase shift layer 23 is shown in FIG.7C. In FIGS.7B and 8C, a positive direction indicates a positive phase and a negative direction indicates an inverted phase. Hence, the light intensity of the exposure light transmitted through the phase shift optical mask, that is, the light intensity of the synthesized light made up of the exposure light transmitted through the light transmitting region 24 and the exposure light transmitted through the SiO 2 phase shift layer 23, becomes as shown in FIG.7D. Therefore, it is possible to draw or expose an extremely thin line using this phase shift optical mask. FIG.8A shows a second conventional phase shift optical mask including a glass substrate 21, a Cr light blocking layer 25 and a SiO 2 phase shift layer 26. The amplitude of the exposure light which is transmitted through a light transmitting region 27 of this phase shift optical mask is shown in FIG.8B, while the amplitude of the exposure light which is transmitted through the SiO 2 phase shift layer 26 is shown in FIG.8C. In FIGS.8B and 8C, a positive direction indicates a positive phase and a negative direction indicates an inverted phase. Hence, the light intensity of the exposure light transmitted through the phase shift optical mask, that is, the light intensity of the synthesized light, made up of the exposure light transmitted through the light transmitting region 27 and the exposure light transmitted through the SiO 2 phase shift layer 26, becomes as shown in FIG.8D. Therefore, it is possible to draw or expose an extremely thin line using this phase shift optical mask. Next, a description will be given of the operating principle of the optical mask according to the divisional application no. 98101274.3, in which the concepts of the first and second conventional phase shift optical masks shown in FIGS.7A and 8A are combined so as to enable drawing or exposure of an even thinner line. Ideally, a phase shift optical mask which combines the concepts of the first and second conventional phase shift optical masks shown in FIGS.7A and 8A has the structure shown in FIG.9. The phase shift optical mask shown in FIG.9 includes a glass substrate 101, a Cr light blocking layer 102 which includes first and second light blocking regions 102A and 102B, a SiO 2 phase shift layer 103 which includes first and second phase shift regions 103A and 103B, and a light transmitting region 104. When the wavelength of the exposure light is 436 nm, the NA of the exposure lens is 0.45 and a line width of 0.4 µm is to be realized, for example, the width of the light transmitting region 104 must be set to m x 0.6 µm, the width of the first phase shift region 103A must be set to m x 0,25 µm, the width of the first light blocking region 102A must be set to m x 0.1 µm, and the width of the second phase shift region 103B must be set to m x 0.1 µm, where m denotes the reducing projection magnification which is normally, 5 or less. However, according to the existing techniques, it is extremely difficult to accurately align the first and second light blocking regions 102A and 102B and the first and second phase shift regions 103A and 103B which have the extremely small widths described above. Therefore, it is extremely difficult, if not impossible, to produce the phase shift optical mask shown in FIG.9. FIG.10 shows an essential part of the optical mask according to the invention claimed in the divisional application. The optical mask shown in FIG.10 includes a light-transmitting substrate 41, a light-transmitting region 42, a first phase shift layer 43, a first light-blocking layer 44, a second phase shift layer 45, and a second light-blocking layer 46. For example, the light-transmitting substrate 41 is made of quartz glass, the first and second phase shift layers 43 and 45 are made of SiO 2 , and the first and second light blocking layers 44 and 46 are made of Cr. The first phase shift layer 43 is provided on the outer side of the light-transmitting region 42. The first light blocking layer 44 is provided on the outer side of the first phase shift layer 43. The second phase shift layer 45 is provided on the outer side of the first light-blocking layer 44. Furthermore, the second light-blocking layer 46 is provided on the outer side of the second phase shift layer 45. The light-transmitting region 42 has a width of the order of m(L + 0.2λ/NA), the first phase shift layer 43 has a width of the order of (mλ/2NA)[1.1 - (NA/λ)(L + 0.2λ/NA)], and the first light-blocking layer 44 has a width of the order of 0.1mλ/NA, where m denotes the reducing projection magnification, L denotes the width of the actual opening which is formed on the wafer, λ denotes the wavelength of the exposure light and NA denotes the numerical aperture of the exposure lens. FIG.11A shows amplitude and phase characteristics of light transmitted through the light transmitting region 42, the first phase shift layer (region) 43 and the second phase shift layer (region) 45 of the optical mask shown in FIG.10, and FIG.11B shows the light intensity of transmitted light in correspondence with FIG.11A. In FIG.11A, G denotes the amplitude of the light transmitted through the light transmitting region 42, H denotes the amplitude of the light transmitted through the first phase shift layer 43, and I denotes the amplitude of the light transmitted through the second phase shift layer 45. Hence, the intensity of the light transmitted through the optical mask shown in FIG.10 as a whole is a synthesized light of G, H and I, as indicated by J in FIG.11B. Hence, the effective exposure width can be set to 0.4 µm, for example, thereby enabling a considerable improvement of the resolution when compared to the conventional phase shift optical masks. Of course, the light amplitudes and the light intensities of the light transmitted through the phase shift optical mask shown in FIG.9 also become as shown in FIGS.11A and 11B. As will be described later in conjunction with FIG.12C, it is also possible to provide a third phase shift layer 47 which covers the light-transmitting region 42, the first phase shift layer 43, the first light-blocking layer 44 and the second phase shift layer 45. Next, a description will be given of the method of producing the optical mask according to Fig.10, referring to FIGS.12A to 12C. In FIGS.12A to 12C, those parts which are the same as those corresponding parts in FIG.10 are designated by the same reference numerals, and a description thereof will be omitted. First, as shown in FIG.12A, a Cr layer 46 is formed on the quartz glass substrate 41 to a thickness of 4700 Å which corresponds to λ/(2n - 2), where λ denotes the wavelength of the exposure light and n denotes the refractive index of SiO 2 which is used as the phase shift material of this optical mask. An opening having a width of 7.5 µm is formed in the Cr layer 46 using a photolithography technique. Then, a SiO 2 layer 45a is formed to a thickness of 5000 Å. This SiO 2 layer 45a covers the Cr layer 46 and the surface of the quartz glass substrate 42 which is exposed within the opening. Thereafter, a Cr layer 44a is formed on the SiO 2 layer 45a to a thickness of 5000 Å. As a result, the width of the side wall at the stepped part of the Cr layer 44a and the width of the side wall at the stepped part of the SiO 2 layer 45a both become 0.5 µm. Next, a reactive etching using a gas mixture of carbon tetrafluoride (CF 4 ) and oxygen (O 2 ) as the reactive gas is carried out to etch back the Cr layer 44a so as to leave the first light-blocking layer 44 at the side wall of the stepped part of the SiO 2 layer 45a as shown in FIG.12B. A SiO 2 layer 43a is thereafter formed on the surface of the structure shown in FIG.12B to a thickness of 1 µm, as shown in FIG.12C. The width of the side wall at the stepped part of this SiO 2 layer 43a is 1 µm. Then, when the SiO 2 layer 43a is etched back by a reactive etching using CF 4 as the reactive gas, the first phase shift layer 43 is left on the side wall at the stepped part of the first light-blocking layer 44 as shown in FIG.10. The SiO 2 layer 45a which remains on the side wall part at the stepped part of the Cr layer (second light blocking layer) 46 forms the second phase shift layer 45. In FIG.10, an opening is formed in the phase shift layers 43 and 45 so as to form the light-transmitting region 42. As a modification of the method, it is possible to omit the process of etching back the SiO 2 layer 43a and stop at the stage shown in FIG.12C. In this case, a part of the SiO 2 layers 43a and 45a becomes the light-transmitting region 47 as indicated in brackets in FIG.12C. Furthermore, as indicated in brackets in FIG.12C, the first phase shift layer 43 in this case has a double-layer structure made up of the original first phase shift layer 43 and the SiO 2 layer 43a, and the second phase shift layer 45 has a double-layer structure made up of the original second phase shift layer 45 and the SiO 2 layer 43a. Since the second embodiment of the method carries out an etch-back process after forming a phase shift layer and a light-blocking layer on a stepped surface, it is possible to form a phase shift layer and a light-blocking layer having an extremely narrow width with a high accuracy. Therefore, it is possible to expose line patterns having a width of 0.4 µm or even less. As may be seen by comparing FIGS.12C and 4, the optical mask shown in FIG.12C may be regarded as the first embodiment of the optical mask shown in FIG.4 with the phase shift layer 43 and the light-blocking layer 44 added.

Claims: A phase-shift optical mask for exposing a pattern using an exposure light, comprising; a substrate (1; 6) which is transparent with respect to the exposure light; a light-blocking layer (2,3; 7,8) on the substrate, which layer is non-transparent with respect to the exposure light and has a side wall defining an opening (5; 10) of a predetermined shape and size; and a phase-shift layer (4; 9) which is transparent with respect to the exposure light and is provided on the light-blocking layer and that part of the substrate (1; 6) which is exposed within the opening (5,10); wherein the phase-shift layer has a uniform thickness, and the light-blocking layer (2,3; 7,8) has a predetermined thickness (PS) such that the phase of the exposure light transmitted through the part (B) of the phase-shift layer (4; 9) provided on the side wall of the light-blocking layer is shifted by approximately 180° relative to the phase of the exposure light transmitted through the part (A) of the phase-shift layer provided on the substrate (1; 6); characterised in that the light-blocking layer (2,3; 7,8) is made up of a first layer (2; 7) which is non-transparent with respect to the exposure light and a second layer (3; 8) which is provided on the first layer, the said predetermined thickness (PS) being the sum of the thicknesses of the first and second layers. A phase-shift optical mask as claimed in claim 1, in which the substrate (1; 6) is made of quartz glass and the phase-shift layer (4; 9) is made of an inorganic material. A phase-shift optical mask as claimed in claim 1 or 2, in which the first layer (2; 7) is made of a metal and the second layer (3; 8) is made of an inorganic material. A phase-shift optical mask as claimed in any of claims 1 to 3, in which the thickness of the phase-shift layer (4; 9) is the same on the substrate (1; 6), on the light-blocking layer (2,3; 7,8) and on the side wall of the light-blocking layer. A phase-shift optical mask as claimed in any preceding claim, in which the said second layer (3; 8) of the light-blocking layer and the phase-shift layer (4; 9) are both made of SiO 2 . A method of producing a phase-shift optical mask for exposing a pattern using an exposure light, comprising the steps of: (a) forming a light-blocking layer (2,3; 7,8) on a substrate (1; 6), the light-blocking layer being non-transparent with respect to the exposure light while the substrate is transparent with respect to the exposure light, the light-blocking layer comprising a first layer (2,7) which is non-transparent with respect to the exposure light on said substrate (1,6), and a second layer (3,8) on the first layer, (b) forming an opening (5; 10) having a predetermined shape and size in the light-blocking layer, defined by a side wall of the light-blocking layer; and (c) forming a phase-shift layer (4; 9) which is transparent with respect to the exposure light on the light-blocking layer and on that part of the substrate which is exposed within the opening, the phase-shift layer being formed to a uniform thickness, the light-blocking layer having a predetermined thickness (PS) being the sum of the thickness of the first and second layers, such that the phase of the exposure light transmitted through the part (B) of the phase-shift layer provided on the side wall of the light-blocking layer is shifted by approximately 180° relative to the phase of the exposure light transmitted through the part (A) of the phase-shift layer provided on the substrate (1,6). A method as claimed in claim 6, in which the substrate (1,6) is made of quartz glass and the phase-shift layer (4,9) is made of an inorganic material. A method as claimed in claim 6 or 7, in which the first layer (2; 7) is made of a metal and the second layer (3; 8) is made of an inorganic material. A method as claimed in any of claims 6 to 8, in which in step (c) the phase-shift layer (4,9) is formed so that its thickness is the same on the substrate (1,6), on the light-blocking layer (2,3; 7,8) and on the side wall of the light-blocking layer. A method as claimed in any of claims 6 to 9, in which the said second layer (3; 8) of the light-blocking layer and the phase-shift layer (4; 9) are both made of SiO 2 .

Inventors: ASAI SATORU, ASAI, SATORU, Asai, Satoru, c/o FUJITSU LIMITED
Applicants: FUJITSU LTD, FUJITSU LIMITED
Application year: 1991
Main classification: G03F1
IPC codes: G03F1