Liquid-crystalline and infrared-sensitive liquid-crystalline polyesters suitable for use in optical data storage, processes for the preparation of same, and an apparatus containing an infrared-sensitive liquid-crystalline polyester

Abstract: Disclosed are liquid-crystalline and infrared-sensitive liquid-crystalline polyesters for optical data storage, processes for the preparation of the same, and an apparatus comprising an infrared-sensitive liquid-crystalline polyester. Owing to covalently bonded dye the liquid crystalline polyester is infrared sensitive and high concentrations of dye are obtainable, without having detrimental effects on the properties of the liquid-crystalline polyester. This results in a highly sensitive liquid-crystalline polyester for optical data storage. Infrared dyes which are preferably bonded in liquid-crystalline polyester are croconium, squarilium, azo, and azamethine dyes.

Description: The invention is in the field of liquid-crystalline polyesters suitable for use in optical data processing, more particularly liquid-crystalline polyesters which are infrared-sensitive due to the presence of an infrared-absorbing dye. Liquid-crystalline polymeric compositions containing infrared-absorbing dye are known from the literature. Such polymeric compositions, including polyesters, are described in EP-A-0 302 497. Information can be written in such polymeric compositions with the use of a solid-state laser (λ = 750 to 870 nanometers). The infrared-absorbing dye serves to convert the laser light energy into thermal energy. According to the above-mentioned publication, information is written in films of liquid-crystalline polymers in the following manner. Using a laser the film, which has been aligned in advance, with for instance an electric field, and so consists of one domain and is hence transparent, is heated locally to above a phase transition temperature and then rapidly cooled. As a result of the rapid cooling the heated section of the liquid-crystalline layer is not restored to its original transparent state but remains light-scattering, i.e., opaque. In this way opaque lines can be written in a transparent film. Writing transparent lines in an opaque film is also known from other publications. In those cases an unaligned film is employed, which is heated locally with a laser. During the irradiation with the laser an electric or magnetic field is applied, the heated section of the film thus being aligned and hence rendered transparent. (Cf., e.g., GB-A-2 146 787). When writing data the thing is to have the highest possible concentration of dye in the polymeric composition without, of course, said composition's properties being adversely affected. The drawback to the above-mentioned polymeric composition is that the infrared-absorbing dye is mixed in with the polymer, to form so-called solid solutions. As a rule only low concentrations of dye can be dissolved in these polymers, since otherwise there will be crystallisation or segregation of the dyes, especially on the long term. Moreover, in the case of solid solution polymers it is often hard to make optically transparent films with homogeneous dye distribution. Also, liquid-crystal polymers are known in which the dye is incorporated into the polymer chain. For instance, in DE-OS 3 603 267 dye is incorporated into the polymer chain to adapt the absorption behaviour of liquid-crystalline polymers to the wavelength of the laser to be used. However, the dyes in question are not infrared-absorbing dyes. These known dyes (λ = 633 nm) generally are much more stable than infrared-absorbing dyes, but they are insensitive in the wavelength field of solid-state lasers (λ = 750-870 nm). If it is desired to utilise solid-state lasers, infrared-absorbing dyes have to be added to the polymer. The advantage of solid-state lasers over other lasers is that they are small in size and relatively inexpensive. Further, so-called polymeric dyes, which absorb in the infrared wavelength field, are known. However, these polymers are not liquid-crystalline. For use in optical data storage a thin layer of such a polymeric dye is applied to a film of liquid-crystalline polymer. There is no need to point out that this does not represent an optimum solution to the problem either. The adhesion between the layers and the sensitivity of the resulting film generate a score of problems. To attain the object of the invention, an infrared-sensitive liquid-crystalline polymeric composition suitable for optical data storage in which the dyes are homogeneously distributed and do not segregate or crystallise out, and which has sufficient sensitivity besides, two problems need to be solved. First of all, liquid-crystalline polymeric compositions suitable for optical data storage must be found into which infra-red absorbing dyes can be incorporated without the liquid-crystalline behaviour of the polymeric composition being adversely affected. Secondly, infrared-absorbing dyes must be found which are stable enough for incorporation into liquid-crystalline polymers and also possess good thermal and photochemical stability. Moreover, the dye must be functionalisable, i.e., it must be possible to render the dye co-polymerisable, e.g. esterifiable Polymers The dye-containing liquid-crystalline polymeric composition has to meet various requirements if it is to be used in optical data storage. Needless to say, it will have to contain a mesogenic (liquid crystal-forming) group. Further, the glass transition temperature T g should be above room temperature. Polymers found to be suitable are polyesters not yet described hereinbefore which satisfy the following formula: wherein R₁ = -halogen, -R₂, -OR₂, -CN or -CF₃; R₂ = -H or an alkyl group having 1-3 carbon atoms; R₃ = an alkyl group having 1-24 carbon atoms; T = m = 0 or 1; A = -CN, -NO₂, -CH=C(CN)₂, -H, -OR₃, -CF₃, or x is an integer in the range of 0 through 6 P and Q are groups of the polyester molecule into which the group is incorporated, and the various R₁ and R₂ groups may be the same or different. These polyesters (according to Formula II) have the additional advantage that their T g can be regulated by the selection of the acid chlorides of which they are composed, viz. the radicals P and Q. Examples of suitable acid chlorides are terephthaloyl chloride and adipoyl chloride. Incorporating rigid acid chlorides into the main chain makes it possible to increase the T g to above 60°C. This renders it unnecessary to clamp the polymer films between solid substrates (e.g., glass) in order to prevent the data written in the polymer from being damaged. Such polyesters are so-called free-standing polyesters. This high T g makes it possible to write out data in a new way, which is as follows: The preparative process is such as to give a film composed of small smectic domains, i.e., a light-scattering film. It is heated locally with a laser to above its clearing temperature T c (this is the temperature at which the polymer's liquid-crystalline properties disappear owing to the mesogenic groups' random distribution at such temperatures), and then rapidly cooled to room temperature. The heated section of the film remains in the isotropic, i.e. transparent phase. Since the T g is much in excess of room temperature, there is no longer any conversion from this thermodynamically unfavourable isotropic state into thermodynamically more favourable small domains. In the case of the already known liquid-crystal polymers with, as a rule, a low T g , it was always necessary to employ an electric or magnetic field or an other way of alignment. To write opaque lines in a transparent background required alignment of the film beforehand, while writing transparent lines in an opaque film called for the application of an electric or magnetic field to the film during the writing. The liquid-crystalline polyesters which have now been developed permit recording without the use of an electric or magnetic field or another way of alignment. Dyes The dyes which are to be incorporated have to be chemically stable under the polymerisation conditions and must be fully incorporated into the polyester. I.e., the polymer may not contain any free dye. Of course, to be incorporable into the polyester the dyes must have two esterifiable groups. Between the esterifiable group and the dye spacers can be provided in a known manner. The dyes can be incorporated into the polyester's main chain, but they can also be incorporated as a side chain. Dyes that are incorporated into the polyester's main chain include croconium and squarilium dyes. Depending on the benzene ring substituents at the squarilium ring, squarilium dyes are suitable for use in the red or the infrared field. The formula of a preferred infrared-absorbing squarilium dye is given below in the form of a unit incorporated into the polyester molecule: wherein P and Q represent the groups of the polyester molecule into which the dye is incorporated, S stands for a spacer group, and m = 0 or 1. The formula of a preferred croconium dye is given below in the form of a unit incorporated into the polyester molecule: wherein the symbols have the same meaning as in Formula III. Dyes which can be incorporated into the polyester as side chain include azamethine and azo dyes. Infrared-absorbing azamethine dyes which are pre-eminently suitable for use in the invention satisfy the following formula, in which they are shown in the esterifiable form: wherein R₄ = -H or -NHCOCH₃, R₅ is -CH₂OH if R₄ = -H and -CH₃ if R₄ = -NHCOCH₃, R₆ is -H if R₄ = -H and -CH₂OH if R₄ = -NHCOCH₃. The formula of a suitable infrared-absorbing azo dye in the esterifiable form is shown below: Preparation Polyesters with or without infrared-absorbing dyes according to the invention can be prepared as follows: a compound containing a mesogenic group and two esterifiable groups, diacid chlorides and, optionally, the infrared-absorbent dye in the esterifiable form, are dissolved in a apolar or polar aprotic solvent (depending on the dye used), and stirred at room temperature for some time and subsequently at elevated temperature for several hours. The resulting polymer is precipitated by pouring the reaction mixture in alcohol/water. The glass transition temperature of the infrared-sensitive liquid crystalline polyester can be varied by preparing a low-molecular weight polyester incorporating much dye and blending it with a quantity of liquid-crystalline polyester without dye. Alternatively, of course, it is possible to incorporate mixtures of dyes into the polyester. Manufacturing a film from the polymer may be as follows: the polymer is dissolved in a solvent and then cast onto a flexible polymeric carrier, causing a 5-micrometer thick liquid-crystalline film suitable for data storage to be formed. The solvent is removed and a scattering film is obtained by keeping the formed film for some time at a temperature between the glass transition temperature T g and the clearing temperature T c . The film can be provided with a protective layer to enhance its mechanical strength and its lifetime. If the protective layer is UV-absorbent as well, the photochemical stability will be enhanced also. The invention will be illustrated with reference to a number of examples. The abbreviations used in the examples have the following meanings: PEES-diol = a compound according to Formula II, wherein R₁ = -H, A = -OC₅H₁₁, m = 1, x = 1, P and Q are OH-groups, and T = PEES-polyester = a compound like PEES-diol, except that P and Q stand for groups of the polymer molecule into which the group is incorporated. HEBI-diol = a compound according to Formula II, wherein R₁ = -H, A = -OC₆H₁₃, m = 0, x = 1, and P and Q are OH-groups. HEBI-polyester = a compound like HEBI-diol, except that P and Q stand for groups of the polymer molecule into which the group is incorporated. SQ = a compound according to Formula III, wherein [S] m = (CH₂)₃, and P and Q are OH-groups. CR = a compound according to Formula IV, wherein [S] m = -CH₂-CH₂-, and P and Q are OH-groups. AZ = a compound according to Formula VI. AM1 = a compound according to Formula V, wherein R₄ = -H, R₅ = -CH₂OH, and R₆ = H. AM2 = a compound according to Formula V, wherein R₄ = -NHCOCH₃, R₅ = -CH₃, and R₆ = -CH₂OH. T g = glass transition temperature, with the on-set and off-set temperatures being given. T c = clearing temperature. % dye = the percentages of dye are given in per cent by weight, calculated on the overall percentage of polyester. λ max = the wavelength at which the polyester reaches its absorption maximum (given in nanometers (nm)). Mw = weight average molecular weight (measured by gel permeation chromatography vis-à-vis polystyrene). ε = extinction coefficient. Example 1 a. Synthesis of PEES-diol Synthesis of 4-pentyloxyphenyl-4′-hydroxybenzoate: To a solution of 165 g (0,92 moles) of 4-pentyloxyphenol and 84 g (0,61 moles) of 4-hydroxybenzoic acid in 2 l of toluene were added 3 g of concentrated sulphuric acid and 1,3 g of boric acid. The water was removed by azeotropic distillation over a period of 48 hours. About 1 l of toluene was removed by distillation and the product crystallised at room temperature. The product was filtrated, washed with hexane, and dried. The yield was 145 g (79% of theory). Synthesis of 4-pentyloxyphenyl-4′-oxybenzoylepoxypropyl ether: To a solution of 85 g (0,28 moles) of 4-pentyloxyphenyl-4′-hydroxybenzoate and 0,6 g of benzyltrimethylammononium chloride in 170 ml of epichlorohydrin was added, in 1 hour at 70°C, a solution of 10,5 g (0,26 moles) of sodium hydroxide in 60 ml of water. The reaction mixture was stirred at 70°C for 2 hours. After cooling to room temperature 250 ml of dichloromethane were added. The layers were separated, the organic layer was washed with 100 ml of water, dried with anhydrous magnesium sulphate, and subsequently evaporated, the residue being crystallised from methanol and isopropanol. The yield was 73 g (73% of theory). Synthesis of 4-pentyloxyphenyl-4′-oxybenzoyl-2,3-dihydroxypropyl ether: 35,6 g (100 mmoles ) of 4-pentyloxyphenyl-4′-oxybenzoylepoxypropyl ether were dissolved in 500 ml of tetrahydrofuran (THF) and 75 ml of a 20% aqueous perchloric acid solution added to the whole. The reaction mixture was stirred at room temperature for 24 hours, poured in ice, and extracted with dichloromethane. The organic layer was washed with aqueous potassium bicarbonate and water, dried with anhydrous magnesium sulphate, and subsequently evaporated, the residue being crystallised twice from toluene. The yield was 19,3 g (52% of theory). b. Synthesis of AM1 Synthesis of 4-nitroso-N,N-diethanol-aniline: To 85 ml of concentrated hydrochloric acid were slowly added 45,3 g (250 mmoles) of N,N-diethanol-aniline. The yellow reaction mixture was cooled to 5°C and a solution of 18,0 g (260 mmoles) of sodium nitrite in 40 ml of water added thereto in 30 minutes. On completion of the adding of the nitrite solution the mixture was allowed to stand for 1 hour. The crystalline orange 4-nitroso-N,N-diethanol-aniline hydrochloride was filtered and washed with 50 ml of ether and ethyl acetate. The hydrochloride was stirred in 50 ml of water and 60 ml of a 10% aqueous sodium hydroxide solution were slowly added. The green precipitate was filtered, washed three times with 25 ml of water, and dried. The yield was 40 g (75% of theory). Synthesis of 1,3-bisdicyanovinylindane: For a description of the process reference is made to K.A. Bello, L. Cheng, and J. Griffiths, J. Chem. Soc. Perkin Trans II, 815 (1987). Synthesis of AM1: A solution of 42,2 g (100 mmoles) of 1,3-bisdicyanovinylindane and 25,2 g (120 mmoles) of 4-nitroso-N,N-diethanol-aniline in 400 ml of ethanol was heated over a period of 20 minutes to 60°C, stirred for 15 minutes at this temperature, and in the course of 1 hour cooled to room temperature. 250 ml of water were added and the dark blue product was precipitated. The product was filtered, washed with water, and dried. The yield was 36 g (78% of theory). λ max : 745 nm (in THF) and ε: 25 200 l.mole⁻¹.cm⁻¹ (in THF). c. Synthesis of PEES-polyester containing 4% of AM1 (polymer 1) To a mixture of 2,69 g(7,2 mmoles) PEESdiol, 151 mg (0,347 mmoles) AM1, 0,69 g (3,8 mmoles) adipoyl chloride and 0,77 g (3,8 mmoles) terephthaloyl chloride in 15 ml dry THF was added in 5 minutes, under nitrogen, and at a temperature of 15 °C, 1,7 ml (23 mmoles) pyridine. The mixture was stirred for 1 hour at room temperature, for 1 hour at 50 °C and for 2 hours at reflux temperature. The reaction mixture was cooled to room temperature, filtered and the polymer was precipitated in 150 ml ethanol. The polymer was filtered, washed twice with 50 ml ethanol and dried. The yield was 3,00 g (80 % of theory). T g : 42/52 °C, T c : 67 °C, and Mw: 7400. 3,5% of dye was covalently incorporated, and no free dye remained. λ max : 713 nm (in THF). Example 2 a. Synthesis of HEBI-diol Synthesis of 4-hexyloxy-4′-hydroxybiphenyl: A mixture of 74 g (0,40 moles) of biphenol and 20 g (0,50 moles) of sodium hydroxide in 600 ml of ethanol was refluxed for 1 hour. At reflux temperature 66 g (0,40 moles) of 6-bromohexane were added over a period of 1 hour. The reaction mixture was refluxed for 18 hours and cooled to room temperature, and the precipitate was filtered. The filtrate was treated with 500 ml of water and the precipitated 4-hexyloxy-4′-hydroxybiphenyl was filtered and washed with water. After drying 29 g of product were obtained. An additional amount of product was obtained by refluxing the precipitate collected from the reaction mixture with 45 g of potassium hydroxide in 600 ml of ethanol for 3 hours. This mixture was cooled to room temperature and the insoluble dihexyloxybiphenyl filtered off. The clear filtrate was treated with 200 ml of 6 N hydrochloric acid and the precipitated 4-hexyloxy-4′-hydroxybiphenyl was filtered, washed with water, and dried. The yield was 19 g. The total yield was 48 g (44% of theory). Synthesis of 4-(2,3-dihydroxypropyloxy)-4′-hexyloxybiphenyl: A mixture of 2,70 g (10 mmoles) of 4-hexyloxy-4′-hydroxybiphenyl, 0,50 g (12 mmoles) of sodium hydroxide, 0,70 g of potassium carbonate, and 2,50 g (12 mmoles) of solketal mesylate in 25 ml of DNA was heated to 130°C over a period of 30 minutes and then stirred at this temperature for 1 hour. After cooling the reaction mixture was poured into 200 ml of water. The precipitated product was filtered and washed with water. The crude product was refluxed for 1 hour in a mixture of 35 ml of tetrahydrofuran (THF) and 5 ml of 3 N hydrochloric acid. After cooling 25 ml of water were added, and the product was filtered, washed with water, and dried. The product was crystallised from 150 ml of ethyl acetate. The yield was 2,4 g (70% of theory). b. Synthesis of HEBI-polyester containing 3% of AM1 (polymer 2) To a mixture of 1,16 g (4,8 mmoles) HEBIdiol, 70,4 mg (0,162 mmoles) AM1, 0,47 g (2,5 mmoles) adipoyl chloride and 0,52 g (2,5 mmoles) terephthaloyl chloride in 10 ml dry THF was added in 5 minutes, under nitrogen, and at a temperature of 15 °C, 1,3 ml (15 mmoles) pyridine. The mixture was stirred for 2 hours at room temperature, for 2 hours at 50 °C and for 2 hours at reflux temperature. After cooling to room temperature, the polymer solution was filtered and the polymer was precipitated in 200 ml methanol. The polymer was filtered, washed twice with 50 ml methanol and dried. The yield was 1,96 g (84 % of theory). T g : 48/54°C, T c : 87 °C, and Mw: 7800. 2,9% of dye was covalently incorporated, and no free dye remained. λ max : 719 nm (in THF).

Claims: A liquid-crystalline polyester suitable for use in for optical data storage, characterised in that the polyester comprises a mesogenic group and satisfies the general formula: wherein R₁ = -halogen, -R₂, -OR₂, -CN or -CF₃; R₂ = -H or an alkyl group having 1-3 carbon atoms; R₃ = an alkyl group having 1-24 carbon atoms; T = m = 0 or 1; A = -CN, -NO₂, -CH=C(CN)₂, -H, -OR₃, -CF₃, or x is an integer in the range of 0 to 6 P and Q are groups of the polyester molecule into which the group is incorporated, and the various R₁ and R₂ groups may be the same or different. A liquid-crystalline polyester according to claim 1, characterised in that an infrared-absorbing dye containing two esterifiable groups is covalently incorporated into the polyester. A polyester according to claim 2, characterised in that the infrared-absorbing dye used is a croconium compound. A polyester according to claim 2, characterised in that the infrared-absorbing dye used is a squarilium compound. A polyester according to claim 2, characterised in that the infrared-absorbing dye used is an azamethine dye. A polyester according to claim 2, characterised in that the infrared-absorbing dye used is an azo dye. An apparatus for optical data storage comprising a solid-state laser and a liquid-crystalline polyester, characterised in that the liquid-crystalline polyester is a polyester according to any one of the preceding claims.

Inventors: DE WIT PAULUS PIETER, ERDHUISEN ERWIN WILHELMUS PETR, GRIFFITHS JOHN, DE WIT, PAULUS PIETER, ERDHUISEN, ERWIN WILHELMUS PETRUS, GRIFFITHS, JOHN
Applicants: AKZO NOBEL NV, AKZO NOBEL N.V.
Application year: 1991
Main classification: G11B7
IPC codes: C09K19, G11B7, C08G63