High activity vanadium-based catalyst

Abstract: A vanadium-based catalyst system is treated with an aluminum alkoxide as a means of enhancing catalyst activity and polymer productivity.

Description: This invention relates to a vanadium-based catalyst suitable for producing ethylene polymers at enhanced levels of catalyst activity and polymer productivity. U.S. patent 4,508,842 discloses a highly active vanadium-containing catalyst system suitable for producing ethylene polymers comprising: (A) a solid catalyst component consisting essentially of (1) an inorganic carrier, as support for (2) the reaction product of (a) a vanadium trihalide and (b) an electron donor, and (3) a boron halide or alkylaluminum modifier, (B) an alkylaluminum cocatalyst, and (C) a halohydrocarbon polymerization promoter. U.S. patent 4,232,140 also discloses a highly active vanadium-containing catalyst system for polymerizing ethylene, said catalyst system comprising: (A) a solid catalyst component containing: (a) a vanadium chloride, (b) an alkylaluminum alkoxide, and (c) an inert inorganic support, (B) an alkylaluminum cocatalyst, and (C) a halogenated alkane. The high yields obtained with this catalyst system is, according to the reference, dependent upon the use of a particular halogenated alkane, i.e., trichlorofluoromethane, as a polymerization promoter. Japanese Public Disclosure No. 62-25112 (Application Ser. No. 60-163525) likewise discloses a vanadium-containing catalyst composition useful in the preparation of ethylene polymers. Such composition consists of: (1) a solid catalyst component obtained by precipitating vanadium trihalide from an ether solution onto a silica and/or alumina carrier and then treating the product with an alkylaluminum, (2) an alkylaluminum, (3) an alkyl halide, and (4) an alkoxy compound of silicon. Unfortunately, the presence of the alkoxysilicon compound in such composition has been found to adversely affect polymer productivity. Japanese patent publication 86/130313 (Japanese patent application Ser. No. 84/251743) likewise discloses vanadium-containing catalyst compositions useful in polymerizing olefins. Such compositions are obtained by mixing together a vanadium compound and an organoaluminum compound which has been previously modified with an ether, ester or ketone. The organoaluminum compound may be an alkylaluminum compound or an alkoxyaluminum compound. According to this reference, polymerization activity is adversely affected if the vanadium compound is pre-reacted with the ether, ester or ketone. Japanese patent publication 86/126111-A (Japanese patent application Ser. No. 84/248159) is yet another reference which discloses vanadium-containing catalyst compositions useful in polymerizing olefins. The catalyst compositions of this reference are prepared by combining (a) the reaction product of vanadium tetrachloride with an ether or ester with (b) an organoaluminum compound which has been modified with an ether, ester or ketone. The organoaluminum compound may be an alkylaluminum compound or an alkoxyaluminum compound. According to this reference, polymerization activity is enhanced by the use of such catalyst. However, this activity enhancement appears to be peculiar to vanadium tetrachloride based catalysts. In accordance with the present invention, it has now been discovered that ethylene polymers can be produced at enhanced levels of catalyst activity and polymer productivity employing a vanadium-based catalyst system comprising: (A) a solid catalyst component consisting essentially of (1) a solid, particulate, porous inorganic carrier, as support for (2) the reaction product of (a) a vanadium trihalide and (b) an electron donor, and (3) a boron halide or alkylaluminum modifier, (B) a triethylaluminum cocatalyst, (C) a halohydrocarbon polymerization promoter, and (D) an aluminum alkoxide activity enhancer having the formula: R n Al(OR¹) 3-n wherein: R and R¹ are alkyl radicals containing from 1 to 14 carbon atoms, which radicals may be the same or different, and n is an integer having a value of 0, 1 or 2. The vanadium-containing catalyst systems which contain an aluminum alkoxide activity enhancer in accordance with the present invention have been found to be significantly more active than like catalyst systems which do not contain such aluminum alkoxide. As a result, it is possible to produce ethylene polymers at enhanced levels of catalyst activity and polymer productivity by the use of such catalyst systems. Surprisingly, however, this activity enhancement has been found to be peculiar to catalyst systems employing triethylaluminum as cocatalyst, and such activity enhancement is not obtained when other alkylaluminum compounds are employed as cocatalyst. Catalyst component (A) consists essentially of: (1) a solid, particulate, porous inorganic carrier, as support for (2) the reaction product of (a) a vanadium trihalide and (b) an electron donor, and (3) a boron halide or alkylaluminum modifier. The vanadium trihalide which is reacted with the electron donor in the preparation of catalyst component (A) is preferable vanadium trichloride, although the halogen present in said vanadium trihalide may be chlorine, bromine or iodine, or any mixture thereof. The electron donor employed normally is a liquid, organic Lewis base in which the vanadium trihalide is soluble. Suitable electron donors include alkyl esters of aliphatic and aromatic carboxylic acids, aliphatic ketones, aliphatic amines, aliphatic alcohols, aliphatic ethers and cycloaliphatic ethers. Particularly useful are alkyl esters of saturated aliphatic carboxylic acids containing from 1 to 4 carbon atoms; alkyl esters of aromatic carboxylic acids containing from 7 to 8 carbon atoms; aliphatic ketones containing from 3 to 6 carbon atoms, preferably from 3 to 4 carbon atoms; aliphatic amines containing from 1 to 14 carbon atoms, preferably from 2 to 8 carbon atoms; aliphatic alcohols containing from 1 to 8 carbon atoms, preferably from 2 to 8 carbon atoms; aliphatic ethers containing from 2 to 8 carbon atoms, preferably from 4 to 5 carbon atoms; and cycloaliphatic ethers containing from 4 to 5 carbon atoms, preferably mono- or di- ethers containing 4 carbon atoms. The aliphatic and cycloaliphatic ethers are most preferred, particularly tetrahydrofuran. If desired, these electron donors may be substituted with one or more substituents which are inert under the reaction conditions employed during reaction with the vanadium trihalide, as well as during preparation of and polymerization with catalyst component (A). The modifier employed in the preparation of catalyst component (A) is a boron halide or alkylaluminum compound normally having the formula: MX a wherein: M is boron or AlR² (3-a) wherein each R² is an alkyl radical containing from 1 to 14 carbon atoms, which radicals may be the same or different, X is selected from the group consisting of fluorine, chlorine, bromine and iodine, and mixtures thereof, and a is an integer having a value of 0, 1 or 2, provided that a is 3 when M is boron. Preferably any halide present in the modifier is chlorine, and any alkyl radicals present contain from 1 to 6 carbon atoms. Such alkyl radicals may be cyclic, branched or straight chain, and may be substituted with one or more substituents which are inert under the reaction conditions employed during preparation of and polymerization with catalyst component (A). Diethylaluminum chloride is preferred. A solid, particulate, porous inorganic material is employed as carrier in the preparation of catalyst component (A). The carrier serves as support for the vanadium trihalide/electron donor reaction product, and the boron halide or alkylaluminum modifier. Suitable carriers include such materials as oxides of silicon, aluminum and zirconium, as well as phosphates of aluminum. Usually these materials have an average particle size of from 10 µm to 250 µm, preferably from 20 µm to 150 µm, and a surface area of at least 3 square meters per gram, preferably at least 50 square meters per gram. Polymerization activity of the catalyst can be improved by employing a silica support having an average pore size of at least 8 nm (80 Angstrom units), preferably at least 10 nm (100 Angstrom units). The carrier material should be dry, that is, free of absorbed water. Drying of the carrier material can be effected by heating, e.g., at a temperature of at least 600°C when silica is employed as the support. Catalyst component (A) is prepared by treating a solid, particulate, porous inorganic carrier with: (1) the reaction product of (a) a vanadium trihalide and (b) an electron donor, and (2) a boron halide or alkylaluminum modifier. The vanadium trihalide/electron donor reaction product is prepared by dissolving at least one vanadium trihalide in at least one electron donor at a temperature of from 20°C up to the boiling point of the electron donor. Dissolution of the vanadium trihalide in the electron donor can be facilitated by stirring, and in some instances by refluxing, the vanadium trihalide in the electron donor. Up to several hours of heating may be required to complete dissolution. After the vanadium trihalide has been dissolved in the electron donor, the reaction product is impregnated into the carrier. Impregnation may be effected by adding the carrier to the solution of the vanadium trihalide in the electron donor, and then drying the mixture to remove excess electron donor. The carrier may be added alone as a dry powder or, if desired, as a slurry in additional electron donor. Alternatively, the solution of the vanadium trihalide in the electron donor may be added to the carrier. Ordinarily the carrier and the solution of the vanadium trihalide in the electron donor are mixed together in such amounts that, after drying, the impregnated carrier contains from 0.05 mmole to 1.0 mmole of vanadium per gram, preferably from 0.3 mmole to 0.8 mmole of vanadium per gram, and most preferably from 0.3 mmole to 0.6 mmole of vanadium per gram. The impregnated vanadium trihalide/electron donor reaction product prepared in this manner contains from 1 mole to 5 moles, preferably from 2 moles to 4 moles, and most preferably about 3 moles of electron donor per mole of vanadium trihalide. Excess electron donor not actually complexed with the vanadium trihalide may remain adsorbed on the carrier without ill effects. The boron halide or alkylaluminum modifier is usually added to the carrier after it has been impregnated with the vanadium trihalide/electron donor reaction product. However, if desired, the boron halide or alkylaluminum modifier may be added to the carrier before it is impregnated with the vanadium trihalide/electron donor reaction product. Addition of the modifier to the carrier may be effected by dissolving one or more modifiers in one or more inert liquid solvents capable of dissolving the modifier, immersing the carrier in the solution, and then drying the mixture to remove the solvent. If the modifier is applied subsequent to the vanadium trihalide/electron donor reaction product, the solvent must be one which does not dissolve the vanadium trihalide/electron donor reaction product. The carrier may be added to the solution of the modifier alone as a dry powder or, if desired, as a slurry in additional inert liquid solvent. Alternatively, the solution of the modifier may be added to the carrier. Ordinarily the carrier and the solution of the modifier in the inert liquid solvent are mixed together in such amounts that, after drying, the carrier contains from 0.1 mole to 10 moles, preferably from 1 mole to 5 moles, of modifier per mole of vanadium trihalide/electron donor reaction product present in the carrier (or to be added to the carrier if it is applied subsequent to the modifier). Among the solvents which can be employed to dissolve the boron halide or alkylaluminum modifier are hydrocarbon solvents such as isopentane, hexane, heptane, toluene, xylene and naphtha. Component (B) of the catalyst system of the present invention is triethylaluminum. As previously noted, the activity enhancement of the catalyst system of the present invention is peculiar to the use of triethylaluminum as cocatalyst, and no significant activity enhancement is obtained when cocatalysts other than triethylaluminum are employed. Component (C) of the catalyst system of the present invention is a halohydrocarbon polymerization promoter normally having the formula R³ b CX' (4-b) wherein: R³ is hydrogen or an unsubstituted or halosubstituted alkyl radical containing from 1 to 6 carbon atoms, which radicals may be the same or different, X' is halogen, and b is 0, 1 or 2. Preferred promoters include flouro-, chloro- or bromo- substituted ethane or methane such as CCl₄, CHCl₃, CH₂Cl₂, CBr₄, CFCl₃, CH₃CCl₃, and CF₂ClCCl₃. Particularly preferred promoters are CH₃CCl₃, CFCl₃, and CHCl₃. Component (D) of the catalyst system of the present invention is an aluminum alkoxide having the formula: R n Al(OR¹) 3-n wherein: R and R¹ are alkyl radicals containing from 1 to 14 carbon atoms, which radicals may be the same or different, and n is an integer having a value of 0, 1, or 2. Preferably R and R¹ are alkyl radicals containing from 1 to 6 carbon atoms. Such alkyl radicals may be cyclic, branched or straight chain, and may be substituted with one or more substituents which are inert under the reaction conditions employed during polymerization with the catalyst system of the present invention. Diethylaluminum ethoxide and aluminum tri-isopropoxide are preferred. Polymerization is effected with the catalyst system of the present invention by contacting ethylene, or a mixture of ethylene and at least one alpha-olefin having 3 to 8 carbon atoms, with the four components of the catalyst system, i.e., the solid catalyst component, the triethylaluminum cocatalyst, the halohydrocarbon polymerization promoter, and the aluminum alkoxide activity enhancer. Polymerization can be effected employing either solution, slurry or gas phase techniques. Suitable fluid bed reaction systems useful for gas phase polymerizations are described, e.g., in U.S. patents 4,302,565, 4,302,566 and 4,303,771, the disclosures of which are incorporated herein by reference. The solid catalyst component, triethylaluminum cocatalyst, polymerization promoter, and aluminum alkoxide activity enhancer can be introduced into the polymerization reactor through separate feed lines or, if desired, two or more of the components may be partially or completely mixed with each other before they are introduced into the reactor. Normally, the triethylaluminum cocatalyst, polymerization promoter and aluminum alkoxide are employed in such amounts as to provide a ratio of the promoter to the total number of aluminum atoms in the triethylaluminum cocatalyst and the aluminum alkoxide of from 0.1:1 to 10:1, preferably from 0.2:1 to 2:1, and the triethylaluminum cocatalyst, aluminum alkoxide and the solid catalyst component normally are employed in such amounts as to provide an atomic ratio of total aluminum atoms in the cocatalyst and the aluminum alkoxide to vanadium in the solid catalyst component of from 10:1 to 400:1, preferably from 15:1 to about 60:1. The relative amounts of aluminum alkoxide and triethylaluminum employed in the catalyst system of the present invention depends upon the particular aluminum alkoxide employed and the degree of catalyst activity enhancement desired. Generally, at constant temperature, catalyst activity increases as the ratio of alkoxide groups in the aluminum alkoxide to the total number of aluminum atoms in the triethylaluminum cocatalyst and the aluminum alkoxide increases. However, at a ratio of less than 0.1:1, activity enhancement may be minimal. Further, enhancement of catalyst activity usually begins to diminish as the ratio approaches 0.7:1, and finally at a ratio in excess of 1.0:1, activity decreases to a level well below that of like catalysts which do not contain such aluminum alkoxide. For this reason, the aluminum alkoxide is employed in amounts such as to provide a ratio of alkoxide groups in the aluminum alkoxide to the total number of aluminum atoms in the triethylaluminum cocatalyst and the aluminum alkoxide of from 0.1:1 to 0.8:1, preferably from 0.5:1 to 0.7:1. If polymerization is conducted in gas phase, e.g., in a fluidized bed, however, it may be desirable to employ somewhat greater amounts of aluminum alkoxide to obtain optimum results. The triethylaluminum cocatalyst, polymerization promoter, and aluminum alkoxide activity enhancer may be introduced into the reactor dissolved in an inert liquid solvent, i.e., a solvent which is nonreactive with all the components of the catalyst system as well as all the components of the reaction system. Hydrocarbons such as isopentane, hexane, heptane, toluene, xylene, naphtha and mineral oil are preferred for this purpose. Generally, such solutions contain from 1 weight percent to 75 weight percent of these materials. If desired, less concentrated or more concentrated solutions can be employed, or, alternatively, the triethylaluminum cocatalyst, polymerization promoter, and aluminum alkoxide activity enhancer can be added in the absence of solvent, or, if desired, suspended in a stream of liquified monomer. When a solvent is employed and polymerization is conducted in gas phase, the amount of solvent introduced into the reactor should be carefully controlled so as to avoid the use of excessive quantities of liquid which would interfere with such polymerization. The solvents employed to dissolve the triethylaluminum cocatalyst, polymerization promoter, and aluminum alkoxide activity enhancer may also be employed to introduce the solid catalyst component into the reactor. Higher boiling solvents, such as mineral oil, are preferred for this purpose. While the solid catalyst component may also be introduced into the reactor in the absence of solvent or suspended in liquified monomer, such solvents may be employed to disperse the solid catalyst component and facilitate its flow into the reactor. Such dispersions generally contain from 1 weight percent to 75 weight percent of the solid catalyst component. The alpha-olefins which may be polymerized with ethylene contain from 3 to 8 carbon atoms per molecule. These alpha-olefins should not contain any branching on any of their atoms closer than two carbon atoms removed from the double bond. Suitable alpha-olefins include propylene, butene-1, pentene-1, hexene-1, 4-methyl-pentene-1, heptene-1 and octene-1. The preferred alpha-olefins are propylene, butene-1, hexene-1, 4-methylpentene and octene-1. The temperature employed during polymerization can vary from 10°C to 115°C, preferably from 80°C to 110°C, when polymerization is effected in gas phase or in a slurry, and from 150°C to 250°C when polymerization is effected in a solution. When polymerization is conducted in gas phase, the temperature, of course, must be maintained below the sintering temperature of the polymers produced in order to prevent polymer agglomeration. On the other hand, the temperature employed during gas phase polymerizations must be sufficiently elevated to prevent substantial condensation of the reaction mixture to the liquid state, as such condensation will cause the polymer particles being produced to cohere to each other and likewise aggravate the polymer agglomeration problem. This difficulty is normally associated with the use of alpha-olefins having 5 or more carbon atoms which have relatively high dew points. While some minor condensation is tolerable, anything beyond this will cause reactor fouling. The pressure employed can vary from subatmospheric to superatmospheric. Pressures of up to 7000 kPa, preferably of from 70 kPa to 3500 kPa, are suitable for gas phase, slurry and solution polymerizations. If desired, polymerization may be conducted in the presence of an inert gas, i.e., a gas which is nonreactive under the conditions employed during polymerization. A chain transfer agent, such as hydrogen, may also be present. The reactor should, however, be maintained substantially free of undesirable catalyst poisons, such as moisture, oxygen, carbon monoxide, carbon dioxide and acetylene. When polymerization is conducted in a fluid bed, the superficial gas velocity of the gaseous reaction mixture through the bed must exceed the minimum flow required for fluidization in order to maintain a viable fluidized bed. The polymers produced with the catalyst system of the present invention have a melt index of from greater than 0 g/10 minutes to 500 g/10 minutes, usually of from 0.1 g/10 minutes to 100 g/10 minutes. The melt index of a polymer varies inversely with its molecular weight and is a function of the hydrogen/monomer ratio employed in the reaction system, the polymerization temperature, and the density of the polymer. Thus, the melt index is raised by increasing the hydrogen/monomer ratio, the polymerization temperature, and/or the ratio of higher alpha olefin to ethylene employed in the reaction system. The polymers produced with the catalyst system of the present invention are also characterized by a density of from 0.86 g/cm³ to 0.96 g/cm³. Such polymers generally contain at least 50 mol percent of polymerized ethylene and no more than 50 mol percent of polymerized alpha olefin containing from 3 to 8 carbon atoms and, optionally, polymerized diene. When polymerized diene is present, the polymers ordinarily contain from 0.01 mol percent to 10 mol percent of at least one such diene, from 6 mol percent to 55 mol percent of at least one polymerized alpha olefin containing from 3 to 8 carbon atoms, and from 35 mol percent to 94 mol percent of polymerized ethylene. The following Examples are designed to illustrate the process of the present invention and are not intended as a limitation upon the scope thereof. The properties of the polymers produced in the Examples were determined by the following test methods: Melt Index (MI) ASTM D-1238, Condition E. Measured at 190°C and reported as grams per 10 minutes. Flow Index (FI) ASTM D-1238, Condition F. Measured at 10 times the weight used in the melt index text above. Melt Flow Ratio (MFR) Ratio of Flow Index : Melt Index. Activity Activity values are normalized values based upon grams of polymer produced per mmol of vanadium in the catalyst per hour per 100 psi (1 psi = 6.8g kPa) of ethylene polymerization pressure. Example 1 Impregnation of Carrier with VCl₃/THF Reaction Product To a flask equipped with a mechanical stirrer were added 4 liters of anhydrous tetrahydrofuran (THF), followed by 64 grams (0.406 mole) of solid VCl₃. The mixture was heated under nitrogen at a temperature of 65°C for 5 hours with continuous stirring in order to completely dissolve the VCl₃. Eight hundred grams (800g) of silica gel were dehydrated by heating under nitrogen at a temperature of 600°C for 20 hours. The dehydrated gel was added to the solution prepared as above, and the mixture was refluxed for one hour under nitrogen. At the end of this time, the mixture was heated at a temperature of 55°C for about 6 hours under a purge of dry nitrogen to produce a dry, free-flowing powder containing about 8 weight percent THF. Example 2 Treatment of Carrier with Diethylaluminum Chloride Five hundred grams (500g) of the silica carrier impregnated with VCl₃/THF reaction product in accordance with Example 1 were slurried in 4 liters of anhydrous hexane. The slurry was continuously stirred while a 10 weight percent solution of diethylaluminum chloride in anhydrous hexane was added over a period of 30 minutes. The impregnated carrier and the diethylaluminum chloride solution were employed in amounts that provided an atomic ratio of aluminum to vanadium of 2.5:1. After addition of the diethylaluminum chloride solution was complete, the mixture was heated at a temperature of 45°C for about 6 hours under a purge of dry nitrogen to produce a dry, free-flowing powder. Examples 3-14 Copolymerization of Ethylene With Hexene-1 Examples 3-14 illustrate the copolymerization of ethylene with hexene-1 using the catalyst system of the present invention. Examples 3-6 The solid catalyst component prepared as described in Example 2 was employed together with triethylaluminum, as cocatalyst; chloroform (CHCl₃), as polymerization promoter; and diethylaluminun ethoxide, as activity enhancer, to copolymerize ethylene and hexene-1 in a one-liter autoclave reactor. In each of these Examples, the four catalyst components were pre-mixed in a 6 ounce bottle before being added to the reactor. The solid catalyst component was added to the bottle first, followed by the triethylaluminum cocatalyst (as a 25 weight percent solution in hexane), the chloroform polymerization promoter, and the diethylaluminum ethoxide activity enhancer. Anhydrous conditions were maintained at all times. The polymerization reactor was dried by heating at 96°C under a stream of dry nitrogen for 20 minutes. After cooling the reactor to 50°C, 500 ml of hexane were added to the reactor, followed by twenty mililiters (20.0 ml) of hexene-1. The reactor contents were stirred under a gentle flow of nitrogen, the premixed catalyst components were transferred to the reactor, and the reactor was sealed. The temperature of the reactor was gradually raised to 70°C and the reactor was pressurized to a pressure of 30 kPa with hydrogen and then to 1050 kPa with ethylene. Heating was continued until the desired polymerization temperature of 85°C was attained. Polymerization was allowed to continue for 30 minutes, during which time ethylene was continually added to the reactor to maintain the pressure constant. At the end of 30 minutes, the reactor was vented and opened. Table II below sets forth the details involving the composition of the catalysts employed in these polymerizations, as well as the reaction conditions employed during polymerization, the properties of the polymers produced, and the productivity of each catalyst system. Shorthand designations employed in Table II are defined as follows: Designation Definition THF Tetrahydrofuran DEAC Diethylaluminum chloride TEAL Triethylaluminum TIBA Triisobutylaluminum DEALE Diethylaluminum ethoxide AIP Aluminum tri-isopropoxide Examples 7-12 The solid catalyst component prepared as described in Example 2 was employed together with triethylaluminum, as cocatalyst; chloroform (CHCl₃), as polymerization promoter; and aluminum tri-isopropoxide, as activity enhancer, to copolymerize ethylene and hexene-1 in a one-liter autoclave reactor. The procedure employed in Example 10 was identical to that of Examples 3-6 except that aluminum tri-isopropoxide was substituted for diethylaluminum ethoxide. The procedure of Examples 7-9 and 11-12 was also identical except that the aluminum tri-isopropoxide and the solid catalyst component were physically blended in the bottle before the triethylaluminum cocatalyst and the chloroform polymerization promoter were added. The details of these polymerizations are set forth in Table II below along with the details of Examples 3-6. Comparative Example A For comparative purposes, ethylene was copolymerized with hexene-1 as in Examples 3-12 except that the use of an aluminum alkoxide activity enhancer was omitted. The details of this polymerization are set forth in Table II below along with the details of Examples 3-12. Example 13 The solid catalyst component prepared as described in Example 2 was employed together with triethylaluminum, as cocatalyst; trichlorofluoromethane (CFCl₃), as polymerization promoter; and diethylaluminum ethoxide, as activity enhancer, to copolymerize ethylene and hexene-1 in a one-liter autoclave reactor. The procedure employed in Example 13 was identical to that of Examples 3-6 except that trichlorofluoromethane was substituted for chloroform. The details of this polymerization is set forth in Table II below along with the details of Examples 3-12. Comparative Example B For comparative purposes, ethylene was copolymerized with hexene-1 as in Example 13 except that the use of diethylaluminum ethoxide was omitted. The details of this polymerization are set forth in Table II below along with the details of Example 13. Comparative Examples C-D In Comparative Example C, ethylene was copolymerized with hexene-1 as in Comparative Example A except that triisobutylaluminum was employed as cocatalyst instead of triethylaluminum. In Comparative Example D, the procedure was repeated employing aluminum tri-isopropoxide as an activity enhancer. The aluminum tri-isopropoxide was physically blended with the solid catalyst component prior to being mixed with the other catalyst components. The details of these polymerizations are set forth in Table II below. It is apparent from Comparative Examples C and D that, at best, only a minor activity gain is obtained by the use of an aluminum alkoxide activity enhancer when triisobutylaluminum is employed as cocatalyst. As is apparent from the data in Table II, however, the effect is quite different when an aluminum alkoxide activity enhancer is employed together with a triethylaluminum cocatalyst. Example 14 Homopolymerization of Ethylene The solid catalyst component prepared as described in Example 2 was employed together with triethylaluminum, as cocatalyst; chloroform (CHCl₃), as polymerization promoter; and aluminum tri-isopropoxide, as activity enhancer, to homopolymerize ethylene in a one-liter autoclave reactor. The procedure employed in Example 14 was identical to that of Examples 7-9 and 11-12 except that ethylene was homopolymerized rather than copolymerized. Table III below sets forth the details involving the composition of the catalyst employed in this polymerization, as well as the reaction conditions employed during polymerization, the properties of the polymer produced, and the productivity of the catalyst system. Comparative Example E For comparative purposes, ethylene was homopolymerized as in Example 14 except that the use of aluminum tri-isopropoxide was omitted. The details of this polymerization are set forth in Table III below with the details of Example 14.

Claims: A catalyst system comprising: (A) a solid catalyst component consisting essentially of (1) a solid, particulate, porous inorganic carrier, as support for (2) the reaction product of (a) a vanadium trihalide and (b) an electron donor, and (3) a boron halide or alkylaluminum modifier, (B) a triethylaluminum cocatalyst, (C) a halohydrocarbon polymerization promoter, and (D) an aluminum alkoxide activity enhancer having the formula: R n Al(OR¹) 3-n wherein: R and R¹ are alkyl radicals containing from 1 to 14 carbon atoms, which radicals may be the same or different, and n is an integer having a value of from o, 1 or 2, said aluminum alkoxide activity enhancer being present in an amount sufficient to provide a ratio of alkoxide groups in such aluminum alkoxide to the total number of aluminum atoms in the triethylaluminum cocatalyst and the aluminum alkoxide of from 0.1:1 to 0.8:1. A catalyst system as in claim 1 wherein R and R¹ are alkyl radicals containing from 1 to 6 carbon atoms. A catalyst system as in claim 1 or 2 wherein the aluminum alkoxide activity enhancer is present in an amount sufficient to provide a ratio of alkoxide groups in such aluminum alkoxide to the total number of aluminum atoms in the triethylaluminum cocatalyst and the aluminum alkoxide of from 0.5:1 to 0.7:1. A catalyst system as in any of claims 1-3 wherein the aluminum alkoxide activity enhancer is diethylaluminum ethoxide or aluminum tri-isopropoxide. A process for homopolymerizing ethylene, or copolymerizing ethylene with one or more alpha olefins containing from 3 to 8 carbon atoms, which process comprises using a catalyst system according to any one of claims 1-4. A process as in claim 5 wherein polymerization is effected in a slurry at a temperature of from 10°C to 115°C. A process as in claim 6 wherein polymerization is effected in a slurry at a temperature of from 80°C to 110°C.

Inventors: CANN KEVIN JOSEPH, CANN, KEVIN JOSEPH
Applicants: UNION CARBIDE CHEM PLASTIC, UNION CARBIDE CHEMICALS AND PLASTICS COMPANY, INC.
Application year: 1991
Main classification: C08F4
IPC codes: C08F4, C08F10