PROCESS FOR FORMING SILICON OXIDE FILM

Abstract: A process for forming a silicon oxide film comprising the step of depositing a thin film of a silanol, a polymer thereof or a siloxane polymer, each containing an organic group, on a substrate by exciting a gas containing an organosilane or organosiloxane gas and a gas containing H and OH on a substrate in a reaction chamber to cause a reaction in a gas phase or on the substrate and the step of removing the organic group from the thin film by plasma treatment. Preferably the thin film is formed by repeating the depositing step and the removing step in the same chamber and is heat treated at a temperature of 450 °C or below. This process provides a good insulation film having a flatness comparable to that of an SOG film.

Description: The present invention relates to a process for the formation of a silicon oxide film and in particular to a process useful for forming an interlayer insulation film of SiO 2 or the like between layers of a multilayer interconnection of a semiconductor device. In recent years, progress in the miniaturization and multilayer interconnection of semiconductor devices has led to an increase in the aspect ratio, so that uneven portions on the surface of a pattern had a serious influence on the reliability of the device. For this reason, the development of a process for the formation of a semiconductor device which enables an insulating film for protecting and insulating an element and wiring to be planarized has been desired in the art. The SOG (spin-on-glass) process has been widely utilized as a technique for planarizing an interlayer insulation film provided between Al wirings. This technique, however, has many problems, and the development of a novel CVD process capable of providing a conformal or fluid form has been energetically studied in the art. The SOG method is classified into the inorganic SOG and organic SOG methods. In the inorganic SOG method, it is difficult to increase the thickness of the film due to the occurrence of a large film shrinkage, and multi-coating is necessary even for attaining a film thickness of about 300 nm. On the other hand, in the organic SOG method, although an increase in the film thickness is possible, organic groups remaining in the film give rise to rapid oxidation decomposition in O 2 plasma or in an O 2 atmosphere at a high temperature. In general, an SOG film has a much higher hygroscopicity than other CVD oxide films and becomes an adsorption source of moisture when it is exposed to the air. Degassing due to said adsorption of moisture, generation of the formed water from the film due to undercuring, etc. are causative of a lowering in the reliability. For this reason, in order to prevent the SOG film from being exposed on the side wall of a through hole, the combined use of an etch back process is necessary in a process wherein use is made of SOG. An object of the present invention is to provide a process for the formation of a planarized insulation film having a desired thickness and a high reliability. According to the present invention, there is provided a process for the formation of a silicon oxide film, comprising the steps of: exciting an organosilane or organosiloxane gas and a gas containing H and OH above a substrate in a reaction chamber such that the respective gases react with each other in the gaseous phase or on the substrate and thereby deposit a thin film of an organic-group-containing silanol, organic-group-containing silanol polymer, or organic-group-containing siloxane-bonded polymer on the substrate; and removing the organic groups from the thin film to obtain a silicon oxide film. According to a preferred embodiment, the removal of the organic groups is conducted by a plasma treatment. The plasma treatment may be conducted at a temperature in the range of from room temperature to 450°C. In particular, the step of deposition and the step of plasma treatment are alternately repeated in an identical reaction chamber to form a silicon oxide film having a desired film thickness on a substrate. It is preferred to conduct the excitation by means of pulsation. In this case, the excitation time is short to such an extent that the organosilane or organosiloxane gas or its reaction product can still contain organic groups when it reaches the substrate. According to one preferred embodiment, the deposition is conducted through the use of planer-type plasma CVD system under conditions of a pressure of 0.6 to 1.3 kPa (5 to 15 Torr), a temperature of room temperature of 250°C, a distance between electrodes of 6 to 25 mm, a gas flow rate of 100 to 18000 cm 3 /min, a discharge power of 100 to 500W, and a discharge "on" time satisfying a requirement represented by the formula D ≤ 300 P {140 - (140/310)T} wherein D represents a discharge time in terms of % by assuming a time taken for a gas to reach the substrate after the introduction thereof into the plasma region to be 100, P represents an RF powder, and T represents the temperature of the substrate. For a better understanding of the invention, and to show how the same may be carried into effect, reference will now be made, by way of example, to the accompanying drawings, in which:- Figures 1A to 1C are diagrams for illustrating one example of the conventional process; Figs. 2A and 2B are diagrams for illustrating a problem of the conventional process; Figs. 3A and 3B are diagrams for illustrating a problem of the conventional process; Figs. 4A to 4F are diagrams for illustrating another example of the conventional process; Figs. 5A and 5B are diagrams for illustrating the principle of the present invention; Figs. 6A and 6B are diagrams showing a product of a reaction of TEOS with H 2 O for illustrating the present invention; Fig. 7 is a diagram showing a molecular weight distribution in terms of the relationship between the molecular weight distribution and the vapor pressure of the polymer and the number of adsorbed molecules, for illustrating the present invention; Fig. 8 is a schematic diagram of a plasma CVD device used in the first example of the present invention; Figs. 9A to 9D are diagrams showing the form of a deposit of a thin film of silicon oxide in terms of the dependency of the form of the deposit upon the pressure; Fig. 10 is a diagram showing the form of a deposit of a thin film of silicon oxide formed at 1.3 mPa (10 Torr)and a low temperature (-30°C); Fig. 11 is a diagram showing the dependency of the state of a thin film of silicon oxide upon the flow rate ratio and the pulse; Fig. 12 is a diagram showing a relationship between the TEOS flow rate and the growth rate of a thin film of silicon oxide; Fig. 13 is a schematic diagram showing a plasma CVD device used in the second example of the present invention; Figs. 14A and 14B are diagrams showing the form of a deposit of a thin film of silicon oxide deposited through the use of a plasma CVD device in the second example of the present invention; Figs. 15A and 15B are diagrams for illustrating a thin film of silicon oxide in the case where annealing is conducted in an N 2 gas atmosphere after deposition according to the third example of the present invention; Figs. 16A and 16B are schematic diagrams of a CVD device in the case where use is made of microwave excitation applicable to the present invention; Figs. 17A and 17B are diagrams for illustrating a thin film of silicon oxide formed by repeating the formation of a film and a plasma treatment in the fifth example of the present invention; Figs. 18A to 18F are micrographs of a thin film of silicon oxide formed by a method according to the sixth example of the present invention and a model diagram of the thin film; Fig. 19 is a diagram showing the relationship between the substrate temperature and the pulse excitation duty and the planarizing of a film formed by a method according to the sixth example of the present invention; Fig. 20 is a diagram showing the results of thermal analysis of a film formed according to the sixth example of the present invention; Fig. 21 is a diagram showing a molecular weight distribution of a film formed according to the sixth example of the present invention; Figs. 22A and 22B are diagrams showing the percent thermal shrinkage and the etching rate of a film formed without a plasma treatment; Figs. 23A and 23B are respectively a flow diagram of a process wherein a plasma treatment is conducted after deposition according to the seventh example of the present invention and a diagram of the etching rate of a film formed by this process; Fig. 24 is a diagram showing data of infrared absorption of a film after deposition after an H 2 O plasma treatment and after a heat treatment; Fig. 25 is a flow diagram showing a process wherein a thin film of silicon oxide is formed by repeating a deposition and an H 2 O plasma treatment according to the seventh example of the present invention; Fig. 26 is a micrograph of a silicon oxide film formed by a duplication process shown in Fig. 25; Fig. 27 is a schematic diagram showing a film forming device wherein use is made of a planar-type (diode parallel plates) RF discharge applicable to the present invention; Fig. 28 is a schematic diagram showing a film forming device wherein use is made of µ-wave downflow plasma applicable to the present invention; Fig. 29 is a schematic diagram showing a film forming (single wafer treatment) device and an annealing (batch treatment) device applicable to the present invention; Figs. 30A and 30B are diagrams for illustrating a method of applying a high frequency power and a low frequency power in a process for the formation of a film applicable to the present invention; and Fig. 31 is a diagram showing a box for synthesis in the application method shown in Fig. 30B applicable to the present invention. Prior to a description of embodiments of the present invention, the prior art will be described in more detail with reference to the drawings, Figures 1A to 1C are diagrams for illustrating one example of a conventional process for the production of a semiconductor device. In Figs. lA to 1C, 81 designates a substrate comprising Si or the like, 82 an insulating film comprising SiO 2 or the like, 83 a wiring layer comprising Al or the like, 84a an SiO 2 film, 84b an SOG film, 84c an SiO 2 film, 84 a layer insulation film comprising an SiO 2 film 84a, an SOG film 84b, and an SiO 2 film 84c, 85 a resist pattern, 86 an opening formed in the resist pattern 85, 87 a contact hole serving as a through hole formed in the resist pattern 85, and 88 a wiring layer comprising Al or the like. The production process will now be described. At the outset, as shown in Fig. 1A, SiO 2 is deposited on a substrate 81, for example, by CVD to form an insulating film 82, Al is deposited on the insulating film 82, for example by sputtering to form an Al film, the Al film is patterned, for example, by RIE to form a wiring layer 83, and an SiO 2 film 84a is formed so as to cover the wiring layer 83. At that time, a step is formed on the surface of the SiO 2 film 84a. Then, SOG is coated on the SiO 2 film 84a by spin coating so as to make the surface level, thereby forming an SOG film 84b, SiO 2 is deposited on the SOG film 84b, for example, by CVD to form an SiO 2 film 84c, and a resist pattern 85 having an opening 86 is then formed on the SiO 2 film 84c. As shown in Fig. 1B, the interlayer insulation film 84 is etched through the use of the resist pattern 85 as a mask to form a contact hole 87, thereby exposing the wiring layer 83. Then, Al is deposited, for example, by sputtering so that Al comes into contact with the wiring layer 83 through the contact hole 87, thereby forming a wiring structure as shown in Fig. 1c. In the above-described conventional process for the production of a semiconductor device, when an inorganic SOG agent (which does not cause organic groups, such as CH 3 groups, to be retained in the film after curing) is used as the material for a silica glass film to be formed by the SOG process, a thick film cannot be formed because an increase in the film thickness causes cracking to become liable to occur in the SOG film 84b (cracking is liable to occur particularly when the film thickness is 300 nm or more), so that no satisfactory planarization can be realized. On the other hand, in an organic SOG material (which causes organic groups, such as CH 3 groups, to be retained in the film after curing), although it is possible to increase the film thickness (the formation of a film having a thickness of about 500 to 600 nm is possible), since organic groups, such as CH 3 groups, are present in the SOG film 84b, as shown in Figs. 2A and 2B, when the formed film is exposed to an O 2 plasma or an oxygen atmosphere at a high temperature in the subsequent step, the organic groups are subjected to oxidative destruction. This causes the film to rapidly shrink, so that there occur problems such as the occurrence of cracking or peeling 89 in the SOG film 84b and a remarkable increase in the hygroscopicity. When use is made of an organic SOG material, as shown in Figs. 3A and 3B, degassing from within the SOG film 84b occurs, which often gives rise to a contact failure 90. For this reason, when use is made of an organic SOG material, as shown in Figs. 4A to 4F, the SOG film 84b is etched-back so that the SOG film 84b is not exposed on the side wall of the contact hole 87 after the formation of a contact hole 87 (a through hole). However, when an organic SOG material is used, a step of etching-back should be additionally provided and the angle 1 becomes smaller than 2 as shown in Fig. 4B, that is, the flatness after etching-back becomes inferior to that of the coating, which gives rise to a problem that no good planarization can be attained due to a problem of the selection ratio of etching. Examples of conventional means for planarizing the surface other than the SOG process include a method wherein an SiO 2 film, a PSG film, or other film in a conformal or reflow form is formed by an atmospheric pressure CVD process, use being made of TEOS and O 3 , thereby reducing the step of the surface of the semiconductor device. In this case, however, when the film thickness is 500 nm or more, cracking occurs in subsequent steps such as heat treatment. On the other hand, when the film thickness is 500 nm or less, there occurs a problem that a flatness comparable to that attained by SOG cannot be attained by the use of this process alone. In order to realize a flatness comparable to that attained by the SOG, it is necessary to form a film having a thickness of 1 µm or more and to conduct etching-back (a step of etching-back should be additionally provided). Further, a proposal has been made of a process for the formation of an SiO 2 film wherein an SiO 2 film is formed in a single stage by a CVD process through the use of a silicon alcoholate, tetraethoxysilane, as a starting compound gas and 0.05 to 5% of steam and 5 to 90% of hydrogen (see Japanese Unexamined Patent Publication (Kokai) No. 2-285636). Although the purpose of this process is to completely convert a silicon alcoholate as a starting compound to SiO 2 by means of a hydrogen plasma, there is a description to the effect that a small amount of steam plasma is allowed to exist to form an Si(OH) 4 component, thereby facilitating the movement of the SiO 2 component on the growth surface of the film, thus causing the denseness of the film to be increased. In this process, however, since an inorganic SiO 2 film is directly deposited by H 2 plasma CVD, planarization of the film cannot be realized, so that the problem that an increase in the film thickness leads to cracking remains unsolved. On the other hand, processes are known for the formation of an interlayer insulation film for polypolycrystalline silicon wiring provided under Al wiring, which processes are practiced at a relatively high temperature. Examples of the processes known in the art include one wherein PH 3 is added to SiH 4 and O 2 (or N 2 O) to form PSG, one wherein B 2 H 6 is added to SiH 4 and O 2 (or N 2 O) to form BSG, one wherein AsH 3 is added to SiH 4 and O 2 (or N 2 O) to form AsSb, and one wherein PH 3 and B 2 H 6 are simultaneously added to form BPSG. In this case, the flatness is improved by subjecting the film to annealing (reflow) treatment at a high temperature of 900°C or above. In a process where the flatness is improved by an annealing treatment at a high temperature, since the annealing treatment is conducted at a temperature of 900°C or above, the diffusion layer (particularly a source-drain on Pch side) is unfavorably redistributed, so that the source-drain breakdown voltage of a transistor falls due to the occurrence of punch-through. Figures 5A and 5B are diagrams illustrating the principle of the present invention. Figure 5B shows a process for forming a thin film of silicon oxide according to the present invention. For comparison, the conventional SOG process is shown in Fig. 5A. In the conventional SOG process shown in Fig. 5A, use is made of chemical polymerization, which is one of the sol-gel processes. In this process, a silicon alkoxide (Si(OR) 4 or the like wherein O represents an oxygen atom and R represents an alkyl group) and H 2 O are mixed with a solvent such as butyl cellosolve or propylene glycol monopropyl ether. A suitable amount of an acid catalyst, such as HNO 3 , HCl, or H 2 SO 4 , is mixed therewith for the purpose of controlling a hydrolysis reaction and a dehydration condensation reaction. On the other hand, in the present invention, an organic silane (or an organic siloxane) and H 2 O are excited instead of the use of the acid catalyst. Examples of the excitation method include plasma excitation (RF discharge, µ-wave discharge, low-frequency discharge, direct current glow discharge, etc.), light excitation (IR, UV, SOR, laser, X-ray, etc.), thermal excitation, etc. Further, if necessary, use may be made of pulsing excitation wherein the excitation is sequentially turned on and off. As with the SOG process, in the present invention, a filmy gel comprising a low-molecular weight polymer containing organic groups is deposited on the substrate. The filmy gel has fluidity, and the film can be leveled to the equivalent extent as that immediately after SOG coating. Thereafter, an undesirable organic group is removed from the leveled film. In the process of the present invention, the reaction and deposition processes can be widely controlled by varying parameters such as the excitation energy (power, pulse cycle, duty, etc.), pressure, temperature, flow rate, etc. Further, since both a plasma treatment and a heat treatment can be incorporated in said deposition process, it becomes possible to increase the film thickness while maintaining the flatness and good film quality. In an embodiment most relevant to the SOG process, after the organic-group-containing silicon oxide film is deposited, the formed film may be heat-treated to remove the organic groups, thereby causing the organic-group-containing silicon oxide film to be converted to a silicon oxide film. In this embodiment, since the control of the film thickness is easily conducted as compared with the SOG process, the film can be thinly formed and baked or cured. Since organic groups are contained in the film, when a thick film is formed at one time and heat treated, cracking occurs due to the occurrence of a large stress derived from film shrinkage. This embodiment, however, is advantageous in that when a film is formed while controlling the film thickness to a small value, the occurrence of the stress can be minimized and a repetition of the formation of a thin film and the heat treatment enables the film thickness to be increased. Further, the formation of a film and the heat treatment can be conducted in an identical vacuum chamber, which facilitates the above-described repeated treatment. According to a second embodiment, baking or curing can be conducted while conducting the deposition, i.e. deposition is conducted while heating the substrate from the beginning. Further, the planarization can be maintained by controlling the substrate temperature etc. to regulate the degree of baking or curing. According to a third embodiment, the deposition of an organic-group-containing silicon oxide becomes possible at a higher temperature through the modification of the second embodiment, that is, through the excitation of the gas in a pulsing manner. This makes it possible to establish a film forming process wherein the deposition, flow, and baking or curing are controlled at intervals of a short period of time of the order of the pulse time. According to a fourth embodiment, an SiO 2 film which is flat, is converted to an inorganic material, and has a good quality can be formed so as to have a desired film thickness by conducting baking or curing through a plasma treatment and alternately repeating the deposition and the removal of organic groups by plasma treatment in an identical reaction chamber without breaking the vacuum. In the formation of an inorganic SiO2 film by the conventional CVD process or plasma CVD process, since the deposited film has no fluidity, planarization cannot be attained, which renders the present embodiment very useful. In the second to fourth embodiments, in the relationship with the used temperature of heating the substrate, if necessary, the film may be further heat-treated at a high temperature to make the film dense or to remove the remaining organic groups. It is also possible to utilize heat treatment for the reflow. The starting compound gas used in the process of the present invention is an organosilane or an organosiloxane and a compound containing H and OH. The organosilane or organosiloxane is a compound wherein the basic atom or basic skeleton comprises Si or Si-O and all the side groups each comprise organic groups (an alkyl group such as methane or ethane, an alkoxyl group such as a methoxy group, an ethoxy group, an acetoxyl group, an aryl group, or the like), and examples of the starting compound gas include tetraethoxysilane, tetramethoxysilane, tetramethylsilane, tetramethylcyclotetrasiloxane, octomethylcyclotetrasiloxane, and diacetoxy-di-tert-butoxysilane. In this case, part of the organic groups may be substituted. Examples of the substituent include a halogen, a hydrogen atom, a hydroxyl group, an NH 4 (ammonia) group, and an NO 3 group. It is preferred that the organosilane or organosiloxane have a molecular weight in the range of from 50 to 5000, preferably 100 to 1000, that the number of carbon atoms in the organosilane or organosiloxane be 50 or less, preferably 20 or less, than the number of silicon atoms in the organosila or organosiloxane, and that all or substantially all of the Si-bonded groups be in alkoxyl groups. In the present invention, the thin film of silicon oxide may be doped with an impurity such as phosphorus (P), boron (B), or arsenic (As) to form PSG, BSG, AsSG, BPSG, or the like. In this regard, one or more of a phosphorus source, a boron source and an arsenic source may be introduced together with the organosilane or organosiloxane gas and the gas containing H and OH. For example, a phosphorus alkoxide such as P(OCH 3 ) 3 or PO(OCH 3 ) 3 is simultaneously added as a source gas of P, a boron alkoxide such as B(OCH 3 ) 3 or B(OC 2 H 5 ) 3 is simultaneously added as a source gas of B, and an arsenic alkoxide such as As(OCH 3 ) 3 is simultaneously added as a source gas of As. Since the fundamental concept of the reaction is quite the same as that of the alkoxide similar to TEOS, the film can be effectively doped with P, B, and As. The compound containing H and OH is a compound which generates H and OH radicals or H and OH ions upon being excited. The compound is preferably one which generates no other radicals or ions than H and OH radicals or ions. Therefore, H 2 O and H 2 O 2 (hydrogen peroxide) are preferred. However, compounds which generate radicals or ions other than H and OH radicals or ions are not excluded from the present invention. In the present invention, a thin film of silicon nitride oxide may be formed by simultaneously using a gas (NH 3 or the like) containing N (nitrogen) to effectively dope the thin film with N. The formation of a thin film of silicon nitride oxide contributes to an improvement in the moisture resistance and water permeability of the thin film compared with a thin film of silicon oxide and enables a thin film having a high reliability to be formed. As described above, in the present invention, the organic groups remaining in a low-molecular weight polymer or the formed thin film can be effectively removed by oxidative destruction through simultaneous use of O 2 gas (oxygen gas) to form a thin film of silicon oxide having a high reliability. The introduction of O 2 gas may be conducted in a continuous or intermittent manner. The intermittent introduction is preferred from the viewpoint of regulating the molecular weight. Further, a suitable amount of a gas less contributable to the reaction, such as an inert gas (Ne, Ar, or the like), may be mixed as a carrier gas. This enables the reaction of the organosilane gas with a gas of a compound containing H and OH, such as H 2 O, to be controlled and, at the same time, the molecular weight of a low-molecular weight polymer polymerized to be regulated. This makes it possible to form a thin film having an excellent flatness on a wafer. In the present invention, the molecular weight of the polymer formed by the reaction and the state of the thin film of silicon oxide formed on the wafer vary depending upon the flow rate ratio of the H 2 O gas to the organosilane or organosiloxane gas. The flow rate ratio of the H 2 O gas to the organosilane or organosiloxane gas is preferably 1/10 to 50 times the stoichiometric molar ratio (for example, in the case of TEOS and H 2 O, the amount of H 2 O is 4 mol based on one mol of TEOS, and in the case of HMDS and H 2 O, the amount of H 2 O is 6 mol based on one mol of HMDS) in the case where the organosilane or organosiloxane material is hydrolyzed or oxidized through the use of H 2 O This is because it is possible to form a thin film of an organic-group-containing silicon oxide having an excellent surface flatness and high reliability. The flow rate ratio is still preferably in the range of 1/2 to 2 times, particularly preferably about one time, that is substantially the stoichiometric ratio. In order to react an organosilane or an organosiloxane with a compound containing H and OH, such as H 2 O, to form a polymer, it is necessary to excite the gas. Examples of the excitation method include one wherein high-frequency power is supplied, one wherein light energy is supplied, one wherein thermal energy is supplied, and one wherein use is made of a catalyst capable of chemically amplifying the reaction. The term "excitation" used herein is intended to mean that activation is conducted by applying energy from the outside to decompose an organosilane or an organosiloxane or a compound containing H and OH, such as H 2 O, to an atomic level or to bring a ground energy state on an atomic or molecular level into a higher energy state (excited state). For example, in the case of H 2 O, the excitation is to bring H 2 O into such a state that an H 2 O radical, H radical, OH radical, H ion, OH ion, electrons, etc. are formed. A reaction of an organosilane or an organosiloxane with a compound containing H and OH will now be described by taking a reaction of Si(OEt) 4 with water (H 2 O) as an example. The reaction of tetraethoxysilane with water is stoichiometrically represented by the following formula: Si(OEt) 4 + 4H 2 O → Si(OH) 4 + 4EtOH (hydrolysis reaction) Si(OH) 4 → SiO 2 + 2H 2 O (dehydration condensation reaction) However, when the above-described reaction proceeds completely, an inorganic SiO 2 film is deposited, and the deposited film has no fluidity and therefore cannot be planarized. For this reason, in the present invention, Si(OEt) 4 is reacted with H 2 O under such a condition that the hydrolysis of Si(OEt) 4 and the dehydration condensation of the product obtained by the hydrolysis do not proceed completely. A simplified example of the reaction will be described for the purpose of showing this. As is apparent from the above formula, Si(OEt) 4 is oligomerized (forming a (low-molecular weight polymer). In this case, the OEt side groups are not always converted to OH groups, and the OEt substantially remains in the product to continue the reaction. The product thus obtained is not a homogeneous compound and is considered to be an aggregate of compounds polymerized and hydrolyzed to various extents. Therefore, although the compound cannot be simply represented, an example of the compound is as shown in Fig. 6A. Therefore, the low-molecular weight polymer can be regarded as a low-molecular weight polymer of silicon oxide having a siloxane bond (-Si-O-Si-). In the case of an unreacted organic group (TEOS), however, ethoxy groups (OC 2 H 5 or the like) still remain in the inside thereof, and the terminal bond of the low-molecular weight polymer is considered to be capped with not only OH but also an organic group (an ethoxy group (OC 2 H 5 ) or the like in the case of TEOS). Like a compound shown in Fig. 6B, when a silanol is produced in which all the groups are substituted with OH groups, it is liable to easily give rise to a dehydration condensation reaction. Therefore, as soon as such a compound reaches the substrate, it is crosslinked to a thin film formed on the substrate, which remarkably deteriorates the fluidity (migration). In the present invention, deposition of the thin film may be conducted at a temperature in the range of from -50 to 450°C. Thus, when a silanol polymer in which all the groups are substituted with OH groups or a polymer in which most of the groups are substituted with OH groups is produced, as in a compound shown in Fig. 6B, in order to realize the fluidity, it is necessary to lower the rate of the crosslinking reaction on the substrate. Lowering the wafer substrate temperature is considered useful for this purpose. This is because lowering the wafer substrate temperature causes the rate of crosslinking reaction on the substrate to be lowered. In this case, the wafer substrate temperature is preferably 100°C or below, preferably room temperature (25°C) or below. When an organic group is present, as in a compound shown in Fig. 6A, it is possible to realize the deposition of a flat thin film even at room temperature or above, for example, 100°C or above. Therefore, when the low-molecular weight polymer is adsorbed to the wafer, not only the molecular weight of the low-molecular weight polymer but also the bonded state has a significant influence on the fluidity and crosslinking reaction on the surface of silicon oxide. Thus, the silicon oxide film deposited on the substrate according to the present invention has at least an organic group and a suitable molecular weight, which enables the thin film to be flattened. Although the content and molecular weight of the organic group cannot be simply described, it is necessary for at least the surface of the formed thin film to have a flatness to such an extent that it is not discontinuous even in a portion having a step. The amount of organic groups contained in the above-described thin film of silicon oxide having flatness is preferably as small as possible so far as planarization is possible (that is, it is possible to realize a planarized shape). As described above, the amount of organic groups remaining in the film has a mutual relationship with the wafer substrate temperature for the purpose of realizing a planarized shape. In general, when a film is formed at room temperature or above, the organic group remains in an amount of 90% by weight or less, preferably 20 to 60% by weight at the time of deposition, particularly at 100°C or above. Further, in general, when the film is formed at room temperature or below, the residual amount of the organic group is controlled to at most 30% by weight, preferably 10% or less. The low-molecular weight polymer adsorbed on a wafer receives heat from the wafer, accompanying an increase in the wafer temperature, to accelerate the polymerization (crosslinking) reaction. As described above, the Si-OH bond gives rise to a crosslinking reaction through a dehydration condensation reaction, thereby causing the Si-OH bond to be converted to a silicon oxide having a siloxane bond (-Si-O-Si-). However, as described above, organic groups remain within or on the surface of the low-molecular weight polymer. With respect to the bond linked to the organic groups as well, the frequency of the crosslinking reaction varies depending upon the temperature. For example, in the case of a Si-O-C 2 H 5 bond, the decomposition of the organic groups occurs at a temperature in the range of from about 250 to 300°C or above. This is because a dangling bond such as Si-O- is formed to accelerate the crosslinking reaction. Further, the step of removing organic groups from the thin film in the present invention is not limited to the above-described plasma treatment and redox treatment and can be simply practiced by heat treatment. The thin film may be irradicated with ultra violet rays simultaneously with or subsequent to the heat treatment. The temperature of the heat treatment for removing the organic groups is generally 100°C or above, preferably 250°C or above. According to the present invention, since the organic groups can be removed at a low temperature of 450°C or below to form a thin film of silicon oxide, this treatment favorably has no adverse effect on the aluminum wiring. The thin film of a silicon oxide from which the organic groups have been removed by heat treatment at a relatively low temperature exhibits a relatively large etching rate. The reason for this is believed to reside in that the formation of a network structure (a three-dimensional structure) of silicon oxide is unsatisfactory and there exist many dangling bonds. Therefore, the heat treatment may be conducted at a temperature of 600°C or above, preferably 850°C or below. In one embodiment, the thin film is deposited at a temperature in the range of from room temperature to 250°C and the step of removing the organic groups is conducted by a heat treatment at a temperature in the range of from 250 to 450°C. According to the above-described plasma treatment, it is possible to form a network structure of a thin film at a temperature of 450°C or below, for example, even at room temperature. However, as described above, when use is made of an embodiment wherein the deposition and the plasma treatment are repeated within an identical reaction chamber, the temperature is preferably 250°C or below from the viewpoint of the planarization at the time of deposition, and 100°C or above from the viewpoint of the effect of the plasma treatment. Therefore, it is preferred to form a network structure of a silicon oxide film and to increase the denseness of the film through a plasma treatment at 100 to 250°C preferably followed by a heat treatment at 250 to 450°C. Further, if necessary, the film may be reflowed by a heat treatment at a high temperature to form a film having a higher flatness. In this case, the film may be doped with P, B, As, or the like to lower the reflow temperature. According to the present invention, since the reflow is not indispensable, a satisfactory effect can be attained at a reflow temperature of 850°C or below, even at 800°C or below. In the present invention, a thin film of an organic-group-containing silicon oxide is formed on a wafer by exciting a gas of an organosilane or organosiloxane gas, such as TEOS, and a gas of a compound containing H and OH, such as H 2 O, in a gaseous phase to give rise to a hydrolysis or oxidation reaction in a gaseous phase or on the surface of a wafer to form a silanol or its low polymer or a low polymer having a siloxane bond in a gaseous phase or on the surface of the wafer and adsorbing the low polymer as an intermediate product on the wafer. In the intermediate product of the low polymer formed by the excitation reaction, when the degree of polymerization is small (that is, the molecular weight is lower), the state more distinctly changes at room temperature as follows: solid → liquid → gas. Further, the lower the degree of polymerization of the low polymer, the larger the vapor pressure. Therefore, when a thin film of a silicon oxide having an excellent surface flatness and a high reliability is formed by the above-described process, the wafer temperature is a very important factor for adsorbing a polymer having a low molecular weight on the wafer, flowing the low polymer on the wafer, and accelerating the crosslinking reaction. The wafer temperature is determined by taking these matters into consideration. In particular, in a preferred embodiment of the present invention, when the deposition of a thin film of an organic-group-containing silicon oxide is conducted in combination with a plasma treatment for removing organic groups from the thin film and they are repeated in an identical reaction chamber, it is preferred that the substrate temperature be allowed to coincide with the temperature necessary for the plasma treatment (removal of the organic groups). In this case, for example, when the deposition is conducted while heating at 100 to 250°C, it is necessary to form a thin film having a desired fluidity (flattening capability) through the control of other process conditions. In this case, it is particularly useful to conduct the excitation in a pulsing manner. Specifically, intermittent excitation enables a thin film having a fluidity to be deposited even at a high temperature. Thus, a thin film can be converted to silicon oxide by thinly forming an organic-group-containing silicon oxide film having an even surface at a high temperature and subjecting the thin film to a plasma treatment at the same temperature to remove organic groups from the thin film. The plasma treatment can be conducted by stopping the supply of the starting compound gas of an organosilane or organosiloxane gas and generating a plasma through the use of a compound containing H and OH or the introduction of other gases such as O 2 , H 2 , etc. The plasma treatment may be conducted by means of oxygen, hydrogen or water plasma and the substrate temperature may be in the range of from 100 to 250°C. In this embodiment, after the steps of deposition and plasma treatment, the heat treatment is conducted at a temperature in the range of from 250 to 450°C. The organic group is removed by an oxidation reaction or a reduction reaction. The repetition of the deposition of an organic-group-containing silicon oxide film and the plasma treatment makes it possible to form a planar silicon oxide film wherein the occurrence of cracking attributable to a large shrinkage has been prevented. Therefore, it is possible to form an insulating film which has an excellent flatness, enables the thickness of the film to be increased, and has a high reliability. In general, a procedure is repeated in which a thin film is deposited to a thickness of 100 nm or less, that is, the upper limit of the depth treatable by means of a plasma, preferably a thickness of 10 nm or less from the viewpoint of the shrinkage and is exposed to a plasma for about 5 to 60 sec, preferably about 20 to 30 sec. In the above embodiment, although the deposition of an organic-group-containing silicon oxide film and the plasma treatment are alternately repeated within an identical reaction chamber, the present invention is not limited to this embodiment only. Specifically, after the deposition of an organic-group-containing silicon oxide film, it is generally possible to use a plasma treatment and a redox treatment for the purpose of removing organic groups, and there is no need for the reaction chamber, temperature, etc. to be identical. As described above, the possibility of the adsorption of an intermediate product of a low polymer on a wafer by the pressure within the chamber containing the wafer therein varies depending upon the molecular weignt (see Fig. 5). In Fig. 7, the upper graph shows the dependency of the vapor pressure of the polymer upon the molecular weight and the temperature, while the lower graph schematically shows molecular weight distributions of a gaseous polymer and liquid polymer. In order to form a planar thin film of a silicon oxide on a wafer, it is necessary that an intermediate product having a low molecular weight (at least in a liquid form) be adsorbed on the wafer and allowed to migrate on the wafer. Therefore, the pressure within the chamber where the wafer is placed is an important factor and should be at least 1 Torr or more. When plasma excitation by means of high-frequency discharge is used, the pressure is preferably 0.6 to 1.9 kPa (5 to 15 Torr), particularly preferably 0.6 to 1.3 kPa (5 to 10 Torr), from the viewpoint of the stability of the plasma excitation. Further, in the present invention, when an organosilane or an organosiloxane and a compound containing H and OH, such as H 2 O, are excited and reacted with each other to form a low-molecular weight polymer and the low polymer is adsorbed on a wafer to form a thin film of silicon oxide, as described above, the molecular weight of the polymer formed by the excitation is very important to the formation of a planar thin film of an organic-group-containing silicon oxide on the wafer. Therefore, a method of regulating the molecular weight is important. The excitation of the gas in a pulsing manner is useful for regulating the molecular weight. The molecular weight of the polymer formed by the reaction may be regulated through the occurrence of excitation energy or the acceleration of the excitation by means of intermittent pulses. According to this method, it is possible to form a polymer having a low molecular weight, and the adsorption of the polymer on the wafer enables a thin film of an organic-group-containing silicon oxide having an excellent flatness to be formed. In the present invention, examples of the gas used for excitation include a gas consisting of an organosilane- or organosiloxane-containing gas alone, a gas consisting of an H- and OH-containing compound gas, such as H 2 O, and a mixed gas comprising these gases. The selection of the gas can be properly determined by the regulation of the molecular weight of a polymer formed on the surface of a wafer, the apparatus used, ease of the process, etc. In the present invention, the state of the thin film of a silicon oxide having organic groups formed on a wafer varies depending upon the temperature of the wafer on which a polymer is adsorbed. As described above, the vapor pressure of the polymer increases with a decrease in the molecular weight of the polymer. It is a matter of course that the vapor pressure of the polymer varies also varies depending upon the temperature to which the polymer is heated. The vapor pressure increases with an increase in the temperature. Therefore, under constant pressure, the probability of the polymer adsorbing on the wafer by the temperature of the wafer varies depending upon the molecular weight of the polymer. In a polymer having a low molecular weight, the vapor pressure increases with an increase of the temperature of the wafer. The reason for this is that the lower the molecular weight, the lower the probability of the adsorption of the polymer on the wafer (see Fig. 6A). The low polymer adsorbed on the wafer flows (migrates) on the surface of the thin film of an organic-group-containing silicon oxide formed on the wafer and is converted to a thin film of an organic-group-containing silicon oxide while crosslinking with a dangling bond on the surface of the organic-group-containing silicon oxide thin film. The flatness of the thin film of an organic-group-containing silicon oxide is attained by virtue of the fluidity of the low polymer on the surface of the thin film. As described above, the probability of the adsorption of a low-molecular weight polymer on the wafer increases when decreasing the wafer temperature, which contributes to an improvement in the flatness of the formed thin film of organic-group-containing silicon oxide. In this case, however, the frequency of crosslinking on the surface of the organic-group-containing silicon oxide falls. The following treatment conditions are one example of the case where use is made of a diode parallel-plate plasma CVD system as one embodiment of the present invention. Temperature: room temperature to 250°C Pressure: 0.6 to 1.9 kPa (5 to 15 Torr), particularly 1.3 kPa 10 Torr Distance between electrodes: 6 to 25 mm, particularly 10 mm Gas flow rate: 100 to 18000 cm 3 /min Discharge power: 500W or less, particularly 100 to 400W RF (discharge) frequency: 13.56 MHz Pulse frequency (period): 100 times or less, preferably 10 times or less than the time taken for the reaction gas to pass through between the electrodes of the diode parallel plates (for example, time of access between electrodes: 1/70 sec in Fig. 13) Discharge duty: D ≤ {140 - (140/310)T} 300 P wherein T represents a substrate temperature, P represents an RF power (W: watt), provided that when the D value is 100% or more, it is regarded as 100%. The term "discharge duty" used herein is intended to mean the proportion of the "on" time to the pulse period. In the present invention, the embodiment wherein use is made of an unsubstituted organosilane is also applicable to an embodiment wherein, for example, SiX(OC 2 H 5 ) 3 is used instead of TEOS (Si(OC 2 H 5 ) 4 , or X(CH 3 ) 2 SiOSiX(CH 3 ) 2 ) is used instead of HMDS ((CH 3 ) 3 SiOSi(CH 3 ) 3 ). That is, an organosilane having an organic group (in this case, an ethoxy group (OC 2 H 5 ) and a methyl group (CH 3 )) substituted with other element (X) is used as the organosilane or organosiloxane. H (hydrogen), Cl (chlorine), F (fluorine) and other various elements are considered useable as the substituent element (X). In this case, the bonding strength between Si in an excited state and the substituent element (in this case, X) is very important. Specifically, in the excitation reaction in a gas of a compound containing H and OH (for example, H 2 O gas), when the element (in this case, X) does not react, it is a matter of course that the unreacted element is incorporated into the thin film of silicon oxide formed on the wafer. Consequently, this causes the amount of the organic groups remaining in the thin film of silicon oxide, such as alkoxy groups and alkyl groups, to be reduced. Therefore, if the element (X) is also stable in subsequent steps, such as annealing treatment and plasma treatment, it is possible to improve the quality of the film, such as cracking resistance. Thus the use of elements or groups capable of meeting this requirement is preferred. In the present invention, the adsorption of a low polymer occurs not only on the wafer but also in portions exposed to reaction gas, such as thechamber of the film forming device and electrodes, depending upon the temperature. In order to prevent a change in the growth rate of silicon oxide on the wafer and prevent the occurrence of staining and particles due to deposits on chamber walls, electrodes, etc., it is preferred to maintain the temperature of the wafer and portions exposed to reaction gas, such as the chamber other than the stage provided on the wafer and electrodes, at a constant value. Further, in this case, it is preferred to maintain the temperature at room temperature or above for the purpose of controlling the probability of the absorption. In the present invention, organic components are still contained in the formed film depending upon film forming conditions, so that the organic components are contained also in the chamber, electrodes, etc. In the cleaning of the chamber, not only can the cleaning time be shortened but also deposits, such as organic substances, can be completely removed by adding O 2 gas to the cleaning gas, such as NF 3 , or conducting chamber cleaning by the use of a cleaning gas, such as NF 3 , after exposure to O 2 plasma. In the present invention, it is also possible to store the wafer having a thin film of silicon oxide formed thereon in a chamber in an identical apparatus and having a controlled atmosphere, pressure and temperature and to conduct an annealing treatment within the chamber when the number of stored wafers has reached a predetermined value. Further, in the present invention, after the formation of a thin film of a silicon oxide, etching-back may be conducted in an identical chamber within an identical apparatus or within another chamber within an identical apparatus. In this case, a F-containing gas, such as CF 4 , CHF 3 or NF 3 , may be used as a reaction gas for etching-back optionally after the addition of O 2 . Further, according to the present invention, in a planar-type plasma CVD system, it is difficult to obtain a stable plasma discharge under a high pressure of about 10 Torr through the use of a low-frequency power (1 MHz or less) alone. However, when the low-frequency power is applied simultaneously with a high-frequency power (13.56 MHz), not only can a plasma discharge be stably obtained but also an ion bombardment effect can be attained through the use of a low-frequency discharge. This contributes to an improvement in the quality of the thin film of silicon oxide formed on the wafer. In the present invention, with respect to the molecular weight of the polymer polymerized in a gaseous phase or on the surface of the wafer, it is possible to vary the molecular weight distribution of the polymer by varying pulse conditions (period, duty, etc.) so far as other conditions are the same. Fundamentally, pulse conditions capable of providing a larger amount of excitation energy enable the molecular weight to be shifted towards a higher polymer. The higher the molecular weight of the polymer, the smaller the change of weight in the subsequent heat treatment such as annealing, when the polymer is adsorbed on the wafer and the smaller the degree of shrinkage of the film in terms of the thickness. This contributes to an improvement in the reliability, such as cracking resistance. However, the flatness of the film decreases when increasing the molecular weight of the polymer, so that the effect of filling up narrow grooves, holes, etc. is lowered. Therefore, when pulse conditions are properly varied during the process (during the formation of a film), it is possible to form a thin film of silicon oxide having an excellent flatness and a high reliability in respect to cracking resistance etc. The present invention will now be described with reference to the following examples. First Example Figure 8 is a schematic view of an apparatus for practicing embodiments of the present invention, i.e., a planar-type (anode couple) plasma CVD system. A gas is excited through the use of a high-frequency (RF) discharge between electrodes 1,2. In this case, the RF frequency is 13.56 MHz. Both TEOS and H 2 O are introduced in the form of vapor by heating a source tank, piping, etc. N 2 is used as a carrier gas. An electrode 1 on the upper cathode side serves also as a port for introduction of these gases into the chamber and is in the form of a shower device. On the other hand, a heating wire for control of the temperature and piping for a chiller are provided within an electrode 2 on the lower anode side, and the temperature can be varied in the range of from -50°C to +500°C. At the outset, the pressure dependency and temperature dependency were examined. Continuous oscillation and excitation were conducted under conditions of a TEOS flow rate of 4 sccm, an H 2 O flow rate of 600 sccm (flow rate ratio of 1 : 150), an RF frequency of 13.56 MHz, and an RF power of 100W. The distance between electrodes was 18 mm. The water temperature was brought to room temperature, and deposition was initiated. Although the wafer temperature increased due to the RF power as soon as the deposition was initiated, this temperature increase was ignored. The form of a deposit of thin film comprising silicon oxide in terms of the dependency of the form of the deposit upon the pressure of the chamber is shown in Figs. 9A to 9D. In the drawings, 5 designates a silicon substrate, 6 a thermally oxidized film (thickness: 50 nm), 7 a polycrystalline silicon pattern, 8 a CVD-SiO 2 film (thickness: 50 nm), and 9 a thin film of (organic-group-containing) silicon oxide. The deposit formed under a pressure of 1.3 kPa (10 Torr) shown in Fig. 9A is in a reflow form although it resembles an octopus trap in its form. When the pressure of the chamber is further reduced, the form changes as shown in Figs. 9B to 9D. Specifically, the surface of a discontinuity 11 inherent in the CVD film becomes clearly observed at the edge portion in a step (see Fig. 9B), and a further reduction in the pressure leads to the occurrence of cracking 12 (see Figs. 9C and 9D). The above results show that the molecular weight of the polymer adsorbed on the wafer varies depending upon the pressure of the chamber. This is because the lower the molecular weight of the polymer, the higher the liquid fluidity. Thus, it can be estimated that the factor which gives rise to a change in the form is that a polymer having a low molecular weight suitable for exhibiting the fluidity is effectively obtained by means of a plasma under a high pressure of about 1.3 kPa (10 Torr). Under high pressure 1.3 kPa (10 Torr), a low-molecular weight polymer having a high vapor pressure can be more successfully adsorbed on the wafer than under low pressure (0.13 kPa (1 Torr or less)). That a reflow form can be obtained by the flow effect of the low-molecular weight polymer on the wafer is considered another factor. When the wafer temperature alone is lowered from room temperature to -30°C, the form is changed to one having a higher flatness as shown in Fig. 10. The form shown in Fig. 10 is one formed under a chamber pressure of 1.3 kPa (10 Torr). The reason why the flatness is higher than that of the film shown in Fig. 9A is believed to reside in that the cooling of the wafer causes the probability of adsorption of the low-molecular weight polymer on the wafer to be increased. Then, the flow rate dependency and pulse dependency were examined. The chamber pressure, RF, RF power, distance between electrodes, pulse frequency, and duty were set to 1.3 kPa (10 Torr), 13.56 MHz, 300W, 10 mm, 75 Hz, and 30%, respectively. However, the actual RF power was 300W × 30% due to pulse oscillation. The total flow rate and the H 2 O flow rate were maintained at 375 sccm and 300 sccm, respectively, and the TEOS flow rate was varied from 20 sccm to 75 sccm. The total flow rate was kept constant through the use of N 2 gas as a balancing gas. The wafer substrate temperature (deposition temperature) was 37°C. The state of the thin film at that time is summarized in Fig. 11, and the relationship between the TEOS flow rate and the growth rate is shown in Fig. 12. In Fig. 11, the data on a TEOS/H 2 O flow ratio of 1 : 2 was obtained by measurement under conditions of a TEOS flow rate of 30 sccm, an H 2 O flow rate of 60 sccm, and a total flow rate of 550 sccm. As is apparent from Fig. 11, an increase in the flow rate ratio (TEOS/H 2 O) causes the thin film to be changed from a solid phase to a liquid phase. Further, as is apparent from Fig. 12, although the growth rate increases when increasing the TEOS flow rate, when the TEOS flow rate is 50 sccm or more, the growth rate falls. At that time, the state of the thin film of silicon oxide on the wafer is changed from a solid state to a liquid state, so that it is estimated that the molecular weight of the polymer formed by a reaction through plasma excitation falls when increasing the TEOS flow rate (increasing the TEOS/H 2 O flow rate ratio), or the crosslinking reaction of the polymer is unsatisfactory. As a result, it is considered that the molecular weight of the polymer adsorbed on the wafer is selected through the correlation among the vapor pressure, chamber pressure (1.3 kPa (10 Torr)), and wafer substrate temperature (37°C), which gives rise to the formation of a polymer having a low molecular weight unadsorbable on the wafer. This causes the growth rate of a thin film of silicon oxide formed substantially in a wafer form to be lowered. The results of pulse oscillation of RF power under the same conditions are shown in Fig. 11. The state of the silicon oxide on the wafer is clearly different from that in the case of continuous oscillation. Thus, RF pulse oscillation enables the molecular weight of the polymer formed by excitation reaction to be efficiently regulated. Second Example Figure 13 is a schematic view of a plasma CVD device according to the second example of the present invention. In Fig. 13, 15 designates an upper electrode, 16 a lower electrode, 17 a gas feed pipe, 18 a wafer (a substrate), and 19 a heater. The TEOS flow rate, H 2 O flow rate, N 2 flow rate, RF frequency, and RF power were set to 30 sccm, 120 sccm, 200 sccm, 13.56 MHz, and 300W, respectively. However, the actual RF power was 60W (300W x 20%) due to pulse oscillation. Further, the pulse frequency, duty ("on" time), distance between electrodes, L, and pressure in the chamber were set to 100 Hz, 20%, 10 mm, and 1.3 kPa (10 Torr), respectively. Under these conditions, a 1 µm-thick thin film of an organic-group-containing silicon oxide was deposited with the wafer temperature being varied. The forms of the thin films are shown in Figs. 14A and 14B (the wafer temperature was 120°C in the case of Fig. 14A and 150°C in the case of Fig. 14B). The flatness of the formed films is superior to that of the oxide film formed through the use of TEOS-O 3 . When the deposition was conducted at 120°C as shown in Fig. 14A, the organic-group-containing silicon oxide can fill up the grooves, holes, etc. even when the aspect ratio is 10. In Figs. 14A and 14B, 22 designates a silicon substrate, 23 a thermally oxidized film, 24 a polycrystalline silicon pattern, 25 a plasma CVD-SiO 2 film, and 26 a thin film of silicon oxide containing an organic substance. In an apparatus shown in Fig. 13, when the area of the gas introduction port (hole of the upper electrode 15) of the shower device for introducing a gas into a chamber is about 8 cm 2 and the temperature of the gas to be introduced is about 80°C (since both TEOS and H 2 O are liquid, they are gasified), the flow rate of a gas 20 in the ejection port of the shower device becomes 70 cm 3 /sec and the time of access between electrodes becomes 14.3 msec. When the flow rate of N 2 as a carrier gas is doubled, that is, increased to 400 sccm, the flow rate and the time of access between electrodes become about 110 cm 3 /sec and about 9 msec, respectively. In this case, since the time per period of the pulse is 10 msec, the baking time (or curing time) becomes 1 msec. It was confirmed that under these conditions, when there is no excitation by means of RF plasma, no thin film can be formed on the wafer (at least in a period of time practicable from the viewpoint of the process). Therefore, the deposition of the thin film and the crosslinking reaction (baking or curing) are regulated on the order of msec, which contributes to a significant improvement in the quality of the thin film of (organic-group-containing) silicon oxide. Further, since excitation is conducted in a pulsing manner, it is possible to realize not only the regulation of the molecular weight of the polymer but also the above-described process effect. Third Example A thin film of an organic-group-containing silicon oxide was deposited on a wafer through the use of a plasma CVD device shown in Fig. 13 under the conditions of a pressure in a chamber of 1.3 kPa (10 Torr), a TEOS flow rate of 30 sccm, an H 2 O flow rate of 120 sccm, an N 2 flow rate of 400 sccm, an RF frequency of 13.56 MHz, an RF power of 300W, a pulse frequency of 50 Hz (pulse period: 20 msec), a duty of 15% ("on" time: 3 msec), and a wafer temperature of 120°C. Then, the resultant thin film of an organic-group-containing silicon oxide was annealed in an atmospheric horizontal oven at 450°C in an N 2 gas atmosphere for 30 min. As shown in Fig. 15A, in the thin film of silicon oxide formed under these conditions, not only it is possible to realize planarization, but also the organic component can be removed by the annealing treatment without occurrence of cracking, so that the resultant thin film has a high reliability. With respect to the occurrence of cracking, in the present example subjected to the annealing treatment, no cracking was observed in a space portion having a width of 0.5 µm shown in Fig. 15B until the film thickness, a , of the reservoir portion reached 0.6 µm. On the other hand, in the conventional inorganic SOG material subjected to the annealing treatment, although the organic component could be removed, when the film thickness, a , of the reservoir portion was 0.6 µm, there occurred cracking unfavorable from the practical viewpoint. In Fig. 15B, the polycrystalline silicon 24 had a height of 1 µm, and the plasma CVD-SiO 2 film 25 had a thickness of 300 nm. The removal of the organic component was confirmed by FTIR (Fourier transformation infrared analysis) or the like. Fourth Example A thin film of silicon oxide was formed on a wafer through the use of a plasma CVD device shown in Fig. 13 under the conditions of a pressure in a chamber of 1.3 kPa (10 Torr), a wafer substrate temperature of 120°C, a TEOS flow rate of 30 sccm, an H 2 O flow rate of 120 sccm, an N 2 flow rate of 400 sccm, an RF frequency of 13.56 MHz, an RF power of 300W, a pulse frequency of 100 Hz (10 msec), a duty of 20% ("on" time: 2 msec), and an O 2 flow rate of 10 sccm. The thin film of silicon oxide formed under these conditions was free from opacity and had a good surface homology and a high density. When the O 2 flow rate was increased to 30 sccm, although the thin film became opaque, a particulate SiO 2 power was deposited on the wafer. From this fact, it was found that O 2 has the effect of catalytically accelerating the reaction. Thus, a high-density thin film of silicon oxide could be formed through a proper control of the O 2 flow rate. However, when a high-density thin film of silicon oxide was formed with O 2 being added, no filled-up form was obtained in a wiring space at intervals of wiring of 0.5 µm or less and an aspect ratio of 1 to 2 and a void (a hole) was formed in the silicon oxide between the wirings. This suggests that although the addition of O 2 is effective for forming a film having a high density, this means is less effective (or useless) for realizing a planarization comparable to SOG and filling up a wiring space of 0.5 µm or less. This is also true of H 2 gas. Under the above-described process conditions, the introduction of O 2 gas was stopped, the flow rate of (N 2 + H 2 ) gas was maintained at a constant value of 400 sccm, and the H 2 flow rate was varied to 0 sccm (N 2 flow rate: 400 sccm), 50 sccm (N 2 flow rate: 350 sccm), 100 sccm (N 2 flow rate: 300 sccm), 150 sccm (N 2 flow rate: 250 sccm), and 200 sccm (N 2 flow rate: 200 sccm). The other process conditions were the same as those used above. Further, the relationship between the H 2 gas flow rate and the filling-up property of the silicon oxide film was examined in a line & space pattern having a step (height) of wiring of 1 µm and a wiring width of 1 µm with the wiring intervals being varied to 1.0 µm, 0.75 µm, 0.5 µm and 0.2 µm. The results are given in the following table. In the table, o represents that filling-up could be conducted without occurrence of a void (a hole), and X represents that a void (a hole) occurred. No data on the H 2 flow rates of 150 sccm and 200 sccm were given in the table because the thin film became an opaque state due to the deposition of a particulate SiO 2 powder on the wafer. It is estimated that the addition of H 2 enables a high-density film to be formed. However, as is apparent from the above table, it is recognized that, as with the addition of O 2 , the addition of H 2 is ineffective for realizing the formation of a planar thin film. In the case of the addition of H 2 to H 2 O as well, the amount of addition of H 2 is 20% by volume at the largest, still preferably 10% by volume or less, based on the total amount of H 2 O and H 2 . Further, in the present invention, the formation of a thin film may be conducted through the use of CVD devices as shown in Figs. 16A and 16B wherein use is made of excitation by a down flow system through the use of µ-wave power or RF power. In this case, the source gases can be excited separately from each other, which contributes to a further improvement in the controllability of the process. In these drawings, 30 designates an organosilane introduction port, 31 an introduction port for H 2 O, N 2 , or the like, 32 a quartz tube, and 33 a µ-wave tube. Fifth Example Use is made of a planar-type (anode couple) plasma CVD system shown in Fig. 13. A high-frequency (RF) discharge between electrodes is used for the excitation of a gas. In this case, the RF frequency is 13.56 MHz. Both TEOS and H 2 O are introduced in the form of vapor by heating a source tank, piping, etc. N 2 is used as a carrier gas. An electrode on the upper cathode side serves also as a port for introduction of these gases into the chamber and is in the form of a shower device. On the other hand, a heating wire for control of the temperature is provided within an electrode on the lower anode side so that the temperature of the wafer can be controlled. A film is formed under conditions of a TEOS flow rate of 30 sccm, and a H 2 O flow rate of 120 sccm (flow ratio of 1 : 4) while simultaneously passing N 2 as a carrier gas at a flow rate of 400 sccm. Excitation is conducted by pulse oscillation under an RF frequency of 13.56 MHz and an RF power of 300W. In this case, pulse conditions are set to a period of 10 msec, a duty of 20% ("on" time: 2 msec), a distance between electrodes of 10 mm, a pressure within the reaction chamber of 1.3 kPa (10 Torr), and a wafer temperature of 120°C. In the plasma treatment, excitation is conducted by continuous oscillation under conditions of an O 2 flow rate of 80 sccm, an N 2 flow rate of 400 sccm, an RF frequency of 13.56 MHz, and an RF power of 300W. In this case, the distance between electrodes, the pressure within the reaction chamber, and the wafer temperature were 10 mm, 0.2 kPa (1.5 Torr), and 120°C, respectively. Under the above-described conditions, the formation of a film and the plasma treatment were alternatively repeated within an identical chamber. Specifically, a thin film 35 of an organic-group-containing silicon oxide having a thickness of about 100 nm was formed on the wafer under the above-described film forming conditions, and the wafer was exposed to a plasma for 30 sec under the above-described plasma conditions. As a result, no cracking occurred, the organic component contained in the thin film 35 was removed (this was confirmed by FTIR), and the film thickness was reduced as indicated by a broken line (see Fig. 17A). Thus, the repetition of the formation of a thin film and the subsequent plasma treatment (repetition of six times in Fig. 17B) enables a planar thin film 37 of an inorganic silicon oxide having a large thickness (1000 nm or more) to be formed (see Fig. 17B). Sixth Example The dependency of the quality of the film upon the substrate temperature and the oscillation conditions was examined through the use of a CVD device shown in Fig. 13 under conditions of a TEOS flow rate of 30 sccm, an H 2 O flow rate of 120 sccm, an N 2 flow rate of 400 sccm, a pressure of 1.3 kPa (10 Torr), an RF frequency of 13.56 MHz, an RF power of 300W, and a distance between electrodes of 10 mm. As shown in Fig. 18A, a BPSG film (film thickness: 600 nm) 42 was formed on a silicon substrate 41, an aluminum wiring pattern (height: 500 nm) 43 was formed thereon, an SiO 2 film (film thickness: 300 nm) 44 was thinly formed over the whole surface by a CVD process, and an organic-group-containing silicon oxide film 45 was deposited on the SiO 2 film as a base by a TEOS-H 2 O plasma CVD process. The results are shown in Figs. 18B to 18F. As shown in Fig. 18B, a sufficiently flat film is formed at a substrate temperature of 65°C by continuous oscillation. However, when the substrate temperature is raised to 150°C, as shown in Fig. 18C, although a continuous film is formed by continuous oscillation, the flatness of the film falls to a considerable extent. When the substrate temperature is kept constant at 150°C and pulse oscillation is conducted at a pulse frequency of 100 Hz (pulse period: 10 ms) with the duty ("on" time) being lowered to 50%, 40%, and 30%, as shown in Figs. 18D, 18E, and 18F, the flatness increases when reducing the duty. Thus, in the present invention, it was demonstrated that a planar film could be deposited at a higher temperature through a lowering in the duty of the pulse oscillation. Figure 19 is a graph showing, as a function of the substrate temperature and duty, whether or not a good planarized film satisfactory from the viewpoint of practicability can be formed under the same condition as that described above. The practicability was judged based on whether or not a pattern having wiring intervals of 0.5 µm and an aspect ratio of about 1 to 2 can be filled up. Figure 20 shows the results of a thermal analysis of a film immediately after deposition thereof. The results of the measurement of weight loss on heating (TG) and the differential thermal analysis (DTA) are given. Specifically, a solid line represents the results on a film formed by continuous oscillation at a substrate temperature of 60°C, a broken line represents the results on a film formed by continuous oscillation at a substrate temperature of 150°C, and a chain line represents the results of a film formed by pulse oscillation (pulse frequency: 100 Hz) under a substrate temperature of 150°C and a duty of 30%. In all cases, since oxidation reaction is initiated at about 250°C, most of the organic components in the film are estimated to be ethoxy groups. In Fig. 20, the results of DTA are for a film formed by continuous oscillation at 60°C. Figure 21 shows a molecular weight distribution of a film formed under a pulse duty of 30% (pulse frequency: 100 Hz) together with a molecular weight distribution of a film formed by an organic SOG process. In the drawing, the solid line represents the molecular weight distribution of a film formed by the organic SOG process, the broken line represents the molecular weight distribution of a film formed according to the process of the present invention, Mw represents a weight average molecular weight, and Mn represents a number average molecular weight. Seventh Example The heat shrinkage and etching rate of films formed as described in the sixth example are shown in Figs. 22A and 22B. The films were respectively formed by continuous oscillation at 60°C, 120°C, and 150°C. The heat shrinkage of the films was measured by heat-treating the films at 250°C and 400°C in an N 2 atmosphere through the use of an atmospheric pressure horizontal oven in an N 2 atmosphere for one hour. On the other hand, the etching rate was measured by heat-treating the films in an atmospheric pressure horizontal oven in an N 2 atmosphere at 250°C for one hour and 400°C for one hour and then immersing the heat-treated films in 0.5% HF. The heat shrinkage and etching rate were larger than those of the inorganic SOG film and 50% and 1500 nm/min or more, respectively. For example, the heat shrinkage and etching rate of an inorganic SOG film heat-treated in an N 2 atmosphere at 450°C for 30 min were 23.1% and 120 nm/min, respectively. The use of H 2 O plasma was attempted as a means for improving the etching rate. Specifically, as shown in Fig. 23A, in the experiment, a film formed under conditions of a TEOS flow rate of 30 sccm, an H 2 O flow rate of 120 sccm, an N 2 flow rate of 400 sccm, a continuous oscillation at 13.56 MHz and 300W, a pressure of 1.3 kPa (10 Torr), and a temperature of 60°C was baked on a hot plate (at 150°C in an N 2 atmosphere) for 2 minutes, an H 2 O plasma treatment was conducted within the same chamber as that used in the formation of the film, and annealing under reduced pressure (0.13 kPa(1 Torr)), partial pressure of H 2 O: 100%) was then conducted at 250°C and 400°C each for 2 minutes. H2O plasma treatment was conducted under conditions of a temperature of 150°C, a pressure of 0.13 kPa (1 Torr), an H 2 O partial pressure of 100%, a frequency of 13.56 MHz, and a power of 100W with the treatment time being varied. The etching rate of a film subjected to the H 2 O plasma treatment is shown in Fig. 23B. From the results, it is apparent that as compared with a control not subjected to the H 2 O plasma treatment, all the films subjected to the H 2 O plasma treatment under various conditions exhibit a lower etching rate and a better modification effect in a region of 50 to 70 nm on the surface of the film. Figure 24 is an infrared absorption spectrum of a film formed by conducting deposition for 5 seconds through pulse oscillation under conditions of a temperature of 150°C, a pressure of 1.3 kPa (10 Torr), a TEOS flow rate of 30 sccm, an H 2 O flow rate of 120 sccm, an N 2 flow rate of 400 sccm, a frequency of 13.56 MHz, a power of 300W, a pulse frequency of 100 Hz, and a duty of 30% ("on" time: 3 ms), subjecting the deposited film to the above-described H 2 O plasma treatment for one minute and heat-treating the film at 250°C and 400°C. It is recognized that the organic component in the film is reduced by the H 2 O plasma treatment to substantially zero. That is, this shows that the H 2 O plasma treatment is useful for removing the organic groups in the film and, in particular, when the deposition time is short, the modification effect is large because the unit film thickness subjected to the plasma treatment is small. Then, an attempt was made to repeat a unit process wherein a film is thinly deposited and subjected to an H 2 O plasma treatment (repeat process). The sequence of the repeat process is shown in Fig. 25. A film deposited under conditions of a temperature of 150°C, a pressure of 1.3 kPa (10 Torr), a frequency of 13.56 MHz, a power of 300W, a pulse frequency of 100 Hz, and a duty of 30% was subjected to an H 2 O plasma treatment under conditions of a temperature of 150°C, a pressure of 0.13 kPa (1 Torr), an H 2 O partial pressure of 100%, a frequency of 13.56 MHz, and a power of 100W. The unit deposition time was varied in the range of from 5 to 30 sec. A plasma treatment was conducted for one minute each time deposition was conducted, and the formation of a film was conducted so that the total deposition time was 3 minutes. Thereafter, annealing under reduced pressure ( 0.13 kPa(1 Torr)), H 2 O partial pressure: 100%) was conducted at 250°C and 400°C each for 5 minutes. The etching rate and shrinkage of films formed under the above conditions are given in the following table. For comparison, data in the case where an inorganic SOG film was annealed at 450°C in an N 2 atmosphere for 30 minutes was also given in the table. Film conditions Unit deposition time (sec) Unit deposition film thickness (nm) Etching rate (nm/min) Shrinkage (%) Inorganic SOG 120 23.1 Repeat Process 5 23.3 140 4.2 10 46.7 170 12.9 15 70 210 25.3 30 140 550 17.9 No plasma treatment, heat treatment alone (control) 1300 or more 51.4 In the repeat process, the shorter the unit deposition time, the lower the etching rate and the better the film quality. In the film formed in a unit deposition time of 5 seconds, the etching rate is on the same level as that of the inorganic SOG level, and the etching rate is a substantially equal rate from the surface of the film to the inside of the film. The shrinkage of the film formed in a unit deposition time of 5 seconds is 4.2% after annealing at 400°C, that is, 1/5 or less of that of the inorganic SOG (annealed at 450°C for 30 min). Figure 26 is a photograph of a section of a film formed by the repeat process where the deposition and the plasma treatment are repeated. The film forming conditions are the same as those used for the formation of a film in a unit deposition time of 5 seconds. As shown in Fig. 24, this film is converted to an inorganic state, and the etching rate as well is on the same level as that of the inorganic SOG film. This demonstrates that the flattening of the film has been realized. In the present example, although the H 2 O plasma treatment was conducted under conditions of a temperature of 150°C, a pressure of 0.13 kPa (1 Torr), an H 2 O partial pressure of 100%, a frequency of 13.56 MHz, and a power of 100W, the treatment pressure can be properly selected in the range of 13.3 Pa to 1.9 kPa (0.1 Torr to 15 Torr). In particular, with the consideration of the throughput (treatment time) in the process, when use is made of the repeat process wherein the deposition and the plasma treatment are continuously conducted within an identical chamber, it is preferred that the pressure used in the H 2 O plasma treatment be the same as the deposition pressure. In this case, the H 2 O plasma treatment pressure in the present example is 1.3 kPa (10 Torr). It is apparent that the same effect can be obtained at 1.3 kPa (10 Torr). In the H 2 O plasma treatment, although the partial pressure of H 2 O was 100%, it is naturally considered that N 2 or an inert gas, such as He or Ar, can be properly mixed as a carrier gas. In particular, when N 2 and H 2 O gas are simultaneously used, it is generally considered that the plasma treatment causes a layer containing N to be thinly formed on the surface of the thin film of an organic-group-containing silicon oxide, and it is estimated that the whole film can comprise a silicon oxide nitride film (SiON) through the repetition of the deposition and the plasma treatment as in the repeat process. The formation of the SiON film enables the film to have a water resistance superior to that of the silicon oxide film free from N. In the H 2 O plasma treatment, although the RF frequency (high frequency) was 13.56 MHz, it is also possible to use other frequency regions so far as H 2 O plasma can be generated. In the present example, use was made of plasma conditions of a frequency of 13.56 MHz and a power of 100W. Under repeat process conditions of the present example, an H 2 O plasma treatment under conditions of a frequency of 13.56 MHz and a power of 100W and an H 2 O plasma treatment under conditions of a frequency of 13.5 MHz and a power of 300W were compared with each other in a unit deposition time of 15 seconds with all the other conditions being the same. The etching rate and the film shrinkage of the film subjected to the H 2 O plasma treatment under conditions of a frequency of 13.56 MHz and a power of 100W were as given in the above table. On the other hand, the film subjected to the H 2 O plasma treatment under conditions of a frequency of 13.56 MHz and a power of 300W gave rise to cracking during annealing at 250°C and 400°C. The reason for this is believed to reside in that when the H 2 O plasma treatment is conducted through the use of a large RF power (a large excitation energy), since the surface of the film alone is rapidly modified, a dense silicon oxide film is formed on the surface of the film before the organic group within the film is decomposed and removed by the H 2 O plasma treatment. Therefore, in this case, it is necessary to shorten the unit deposition time, that is, to reduce the unit deposition film thickness. The repeat process was conducted in the same manner as that of the present example, except that the H 2 O plasma treatment conditions were changed to a temperature of 150°C, a pressure of 1.3 kPa (10 Torr), an H 2 O partial pressure of 100%, a frequency of 13.56 MHz, and a power of 300W, and the unit deposition time was 10 seconds. As a result, the etching rate and the film shrinkage were substantially the same as those in the case of a unit deposition time of 10 seconds in the above table. This shows that the same effect can be sufficiently attained also under other conditions by properly setting the treatment pressure, RF power, etc. Eighth Example In the present invention, use may be made of a film forming device utilizing a planar-type RF discharge as shown in Fig. 27. In the drawing, 51 designates a wafer, 52 a gas introduction port, 53 an exhaust port, and 54 a plasma region. Further, use may be made of a film forming device as shown in Fig. 28 wherein a µ-wave downflow plasma is utilized. In Fig. 28, 61 designates a gas introduction portion (H 2 O, N 2 , etc.), 62 a gas introduction port (TEOS, N 2 , etc.), 63 a quartz portion, 64 a µ-waveguide, 65 a plasma region, 66 a ringed quartz shower device, 67 a wafer, and 68 an exhaust port. It is a matter of course that a film is formed in a portion exposed to plasma based on the same concept as that on the wafer. Further, a film is formed also in a portion not exposed to plasma depending upon the flow of the gas. Therefore, in order to suppress the adsorption of a polymer formed by the excitation reaction, it is very effective to heat also portions other than the wafer to at least room temperature. In particular, in the case of a planar-type CVD device as a film forming device shown in Fig. 27, the temperature of the counter electrode on which a wafer is placed (the electrode on which a wafer is placed is of course regulated for controlling the wafer temperature) is very important for keeping the growth rate of a film on the wafer constant. When the counter electrode is provided on the side of application of a high-frequency power as in a film forming device shown in Fig. 28, since it is difficult to directly conduct heating and control by means of a heater, heating and control through a medium are considered effective. Further, in the present invention, as shown in Fig. 29, use may be made of a film forming (single wafer treatment) device 72 and an annealing treatment (batch treatment) device 73 through a load-lock chamber 71, and it is possible to store the wafer having the thin film of silicon oxide formed thereon in a chamber having a controlled atmosphere, pressure, and temperature in an identical apparatus and to conduct an annealing treatment within a chamber having a controlled atmosphere, pressure, and temperature in an identical apparatus when the number of stored wafers has reached a predetermined value. In Fig. 29, 74 designates a wafer storage portion, 75 a wafer support portion (carrier), 76 a gate, and 77 an exhaust port. Further, in the present invention, a high-frequency power and a low-frequency power may be applied to the electrode in a simultaneous, continuous or pulsing manner through the use of a planar-type CVD device capable of realizing the above-described film forming process. In this case, an RF power source of 13.56 MHz and a low-frequency power source of 1 MHz or less may be used as the high-frequency power and the low-frequency power, respectively. Specific examples of the method of applying the high-frequency power and the low-frequency power to the electrode include a method as shown in Fig. 30B wherein the high-frequency power and the low-frequency power are simultaneously applied to an identical electrode and a method shown in Fig. 30A wherein the high-frequency power and the low-frequency power are separately and simultaneously applied to two electrodes facing each other. An example of a box for synthesis shown in Fig. 28B is shown in Fig. 29. According to the present invention, an insulating film having a flatness or planarization comparable to that of a silica glass formed by an SOG process, an excellent plasma resistance, and a high reliability can be formed in a desired film thickness, which renders the insulating film useful as an interlayer insulation film of a semiconductor device, etc.

Claims: A process for the formation of a silicon oxide film, comprising the steps of: exciting an organosilane or organosiloxane gas and a gas containing H and OH above a substrate in a reaction chamber such that the respective gases react with each other in the gaseous phase or on the substrate and thereby deposit a thin film of an organic-group-containing silanol, organic-group-containing silanol polymer, or organic-group-containing siloxane-bonded polymer on the substrate; and removing the organic groups from the thin film to obtain a silicon oxide film. A process according to claim 1, wherein said organosilane or organosiloxane gas is one or more of tetraethoxysilane, tetramethoxysilane, tetramethylsilane, tetramethylcyclotetrasiloxane, octomethylcyclotetrasiloxane, diacetoxy-di-tert-butoxysilane, hexamethyldisiloxane, and their substituted compounds. A process according to claim 1 or claim 2, wherein said gas containing H and OH is water vapour or hydrogen peroxide. A process according to claim 1, 2 or 3, wherein said thin film is deposited at room temperature or above and contains 90% by weight or less of the organic groups prior to removing the organic groups from the thin film to obtain a silicon oxide film. A process according to claim 4, wherein said thin film is deposited at room temperature or above and contains 20 to 60% by weight of the organic groups prior to removing the organic groups from the thin film to obtain a silicon oxide film. A process according to claim 1, 2 or 3, wherein said thin film is deposited at room temperature or below and contains 30% by weight or less of the organic groups prior to removing the organic groups from the thin film to obtain a silicon oxide film. A process according to any preceding claim, wherein said excitation is conducted in a pulsing manner. A process according to claim 7, wherein said excitation time is short such that the organosilane or organosiloxane gas or its reaction product still contains the organic group when it reaches the substrate. A process according to claim 1, wherein deposition of said thin film is conducted at a temperature in the range of from -50 to 450°C. A process according to any one of claims 1-8, wherein the step of removing the organic groups is conducted by the use of a heat treatment at a temperature in the range of from 250 to 850°C. A process according to claim 9, wherein the deposition of said thin film is conducted at a temperature in the range of from room temperature to 250°C and the step of removing the organic groups is conducted by the use of a heat treatment at a temperature in the range of from 250 to 450°C. A process according to claim 1, wherein the deposition of said thin film and removal of the organic groups are successively conducted without breaking the vacuum. A process according to claim 11, wherein said thin film is irradiated with ultraviolet rays simultaneously with or subsequent to the heat treatment. A process according to claim 1, wherein the flow rate ratio of the gas containing H and OH to the organosilane or organosiloxane gas is 1/10 to 50 times the stoichiometric molar ratio necessary for completely hydrolyzing or oxidizing the organosilane or organosiloxane with the gas containing H and OH. A process according to any one of claims 1-8 and 10, wherein the step of removing the organic groups comprises subjecting the thin film to a plasma treatment. A process according to claim 15 when dependent on claim 1 only, wherein said plasma treatment is conducted at a temperature in the range of from room temperature to 450°C. A process according to claim 15 or claim 16, wherein a silicon oxide film having a desired film thickness is formed on the substrate by alternatively repeating the step of deposition and the step of plasma treatment in an identical chamber. A process according to claim 16, wherein said plasma treatment is conducted by means of oxygen, hydrogen, or water plasma and the substrate temperature is in the range of from 100 to 250°C. A process according to claim 18, wherein, after the steps of deposition and plasma treatment, heat treatment is conducted at a temperature in the range of from 250 to 450°C. A process according to claim 15, when dependent on claim 1 only, or claim 17, wherein the step of deposition and the step of plasma treatment are alternately conducted by intermittently stopping the supply of the organosilane or organosiloxane gas to the reaction chamber. A process according to claim 15 when dependent on claim 1 only, or claim 17, wherein said excitation is conducted in a pulsing manner. A process according to claim 1, wherein one or more of a phosphorus source, a boron source, and an arsenic source is introduced together with the organosilane or organosiloxane gas and the gas containing H and OH to incorporate one or more of phosphorus, boron, and arsenic into the thin film. A process according to any one of claims 1-8, 10, 15 and 17, wherein a gas containing nitrogen is introduced together with the organosilane or organosiloxane and the gas containing H and OH to incorporate nitrogen into the thin film. A process according to any one of claims 1-8, 10, 15, 17 and 23, wherein oxygen gas is further continuously or intermittently introduced into the organosilane gas or organosiloxane gas and the gas containing H and OH. A process according to claim 1, wherein said deposition is conducted through the use of a planar-type plasma CVD system under conditions of a pressure of 0.6 kPa to 1.9 kPa (5 to 15 Torr), a temperature of room temperature to 250°C, a distance between electrodes of 6 to 25 mm, a gas flow rate of 100 to 18000 cm 3 /min, an RF (discharge) frequency of 13.56 MHz, a pulse period of 100 times or less the time taken for the reaction gas to pass through between electrodes of the parallel plates, a discharge power of 100 to 500W, a discharge "on" time satisfying a requirement represented by the formula D ≤ 300 P {140 - (140/310) T } wherein D represents the length of a discharge "on" time in terms of % by assuming a time taken for a gas to reach the substrate after the introduction thereof into the plasma region to be 100 with the upper limit of the discharge "on" time being 100%, P represents an RF power, and T represents the temperature of the substrate. A process according to claim 1, wherein said silicon oxide film is a layer insulation film for multilayer interconnection of a semiconductor device.

Inventors: FURUMURA YUJI, HATANAKA MASANOBU, TSUKUNE ATSUHIRO, FURUMURA, YUJI, HATANAKA, MASANOBU, TSUKUNE, ATSUHIRO
Applicants: FUJITSU LTD, FUJITSU VLSI LTD, FUJITSU LIMITED, FUJITSU VLSI LIMITED
Application year: 1991
Main classification: H01L21
IPC codes: H01L21