Process for preparing high-temperature superconducting thin films

Abstract: Improvement in a process for preparing a-axis oriented thin film of high-Tc oxide superconducting material by laser evaporation method. Before the a-axis oriented thin film of oxide superconducting material is deposited by laser evaporation method, an under-layer having an a-axis orientation of the crystal of the same oxide superconducting material is deposited on a substrate previously by sputtering.

Description: Background of the Invention Field of the invention The present invention relates to a process for preparing high-temperature superconducting thin films, more particularly to a process for preparing thin films of high-temperature oxide superconductors possessing improved crystallinity and electrical properties on a substrate. High-temperature oxide superconductor means a new type of oxide superconductors possessing a critical temperature (Tc) higher than 30 K such as Y-Ba-Cu oxide, Bi-Sr-Ca-Cu oxide, Ti-Ba-Ca-Cu oxide or the like. Description of the related art These new type high-temperature superconductors are expected to be utilized to fabricate electronics devices such as Josephson elements, superconducting transistors or the like. In order to realize these electronics devices, it is indispensable to prepare their thin films. It is known that these high-temperature oxide superconductors show anisotropy in their superconducting properties. In fact, their crystals show a critical current density (Jc) which is higher along a direction perpendicular to c-axis than along the other directions, namely a-axis and b-axis. Therefore, a variety of studies have been made to prepare c-axis oriented thin films of the oxide superconductors in which electric current flows mainly in parallel with a surface of the thin film. Today, such c-axis oriented single crystal thin films of high quality can be prepared by sputtering, vacuum-evaporation, laser abrasion technique or the like on single crystal substrates such as SrTiO₃ and MgO. The high-temperature superconductors exhibit anisotropy in their coherent length also. Namely, the coherent length along a-axis is longer than that along c-axis. In fact, the coherent length along c-axis is several angstroms (Å) while the coherent length along a-axis is of several tens angstroms (10 Å). In certain applications of oxide superconductors such as electronics devices, for example Josephson Junctions, the a-axis oriented thin films possessing such longer coherent length are requested. An "a-axis oriented thin film" means a thin film made of a crystal whose a-axis is substantially perpendicular to a surface of the thin film. It is known (Extended Abstracts of 1989 International Electronics Conference - ISEC'89 - June 12-13, 1989) that such a-axis oriented thin films of oxide superconductors can be prepared or realized, for example by sputtering, under such a condition that a substrate on which the thin film is deposited is heated to a temperature which is lower by about 10 °C than the temperature which is requested to realize the c-axis oriented thin film. The crystallinity of the resulting thin film of oxide superconductor, however, is spoiled when the substrate temperature is lowered because the oxygen supply into the crystal becomes insufficient. Therefore, the a-axis oriented thin films of oxide superconductors prepared by prior arts show relatively poor electrical properties. In the case of techniques other than sputtering, it is difficult to prepare the a-axis oriented thin films of oxide superconductors directly on a substrate even if the substrate temperature is controlled or lowered. Particularly, it is very difficult to prepare the a-axis oriented thin films of oxide superconductors directly on a substrate by vacuum-evaporation, although the vacuum-evaporation technique has such many merits that the composition in the thin film can be controlled easily and a thin film of large area can be prepared at a relatively high deposition rate. Inventors of the present application proposed, in a copending European patent application No. 91 400 661.4 (published under EP-A-0 446 145), a process for preparing an a-axis oriented thin film of oxide superconductor possessing improved electrical properties by vacuum-evaporation technique by interposing another a-axis oriented intermediate layer between the a-axis oriented thin film and a substrate. Now, inventors of the present application found that the same technique as is disclosed in the European patent application No. 91 400 661.4 is applicable to prepare an a-axis oriented thin film of oxide superconductors by the laser evaporation method which has such many merits that thin films can be prepared rapidly in the absence of electromagnetic field and that deposition conditions can be controlled easily compared to the other techniques. Although the laser evaporation method itself is known and is used for preparing thin films of superconducting oxides, it has been difficult to prepare a-axis oriented thin films of oxide superconductors directly on a substrate by the laser evaporation method for the same reason as above. Therefore, an object of the present invention is to provide a process for preparing a-axis oriented thin films of oxide superconductors possessing improved electrical properties by the laser evaporation method. Summary of the Invention The present invention provides a process for preparing an a-axis oriented thin film of oxide superconducting material on a substrate, characterized in that an under-layer of the oxide superconducting material having an a-axis orientation of crystal is deposited in a first step on the substrate by any physical vapour deposition (PVD) technique other than laser evaporation method at a substrate temperature which is suitable to realize the a-axis oriented thin film, and in that an upper-layer of the same oxide superconducting material is deposited in a second step on the resulting under-layer by laser evaporation method at another substrate temperature which is higher than that substrate temperature used in the first step. "Laser evaporation method" means a deposition technique in which a target is irradiated by a high-energy laser beam so that elements of the target are evaporated instantaneously and the resulting evaporated elements are deposited on a substrate. So-called laser abrasion method is a typical technique of the laser evaporation method. In a preferred embodiment of the process according to the present invention, the under-layer of same oxide superconducting material can be deposited on a substrate by any deposition technique other than laser evaporation method, preferably prepared by sputtering method, under such a condition that the substrate is heated to a temperature which is suitable to realize an a-axis orientation of crystal of the oxide superconducting material before the upper-layer of the same oxide superconducting material is deposited on a surface of the resulting under-layer by the laser evaporation method. The "temperature which is suitable to realize an a-axis orientation of crystal of the oxide superconducting material" means a temperature at which the a-axis of crystals of which the thin film of the oxide superconducting material is made grows preferentially or predominantly along a direction perpendicular to a surface of the substrate. Generally, such a-axis oriented thin films of oxide superconductors can be realized by physical vapour deposition (PVD) technique such as sputtering under such a condition that a substrate on which the thin film is deposited is heated to a temperature which is lower by about 10 °C than the temperature which is requested to realize the c-axis oriented thin film of the same material. For example, in the case that a-axis oriented thin films of Y-Ba-Cu-O type oxide superconductors are produced by sputtering, the substrate must be heated to a temperature between 530 and 620 °C. The term "sputtering" includes all variations thereof such as DC sputtering, RF sputtering, RF-magnetron sputtering or the like. The under-layer has preferably a thickness of 20 to 1,000 Å. If the thickness is not greater than 20 Å, it is difficult to obtain the desired a-axis oriented upper-layer on the under-layer. Thin films over 1,000 Å may not improve substantially the properties of the upper-layer. The thickness of the upper-layer is preferably above 100 Å. In the process according to the present invention, the upper-layer is produced by laser evaporation method. In this case, a substrate having an under-layer which has been prepared in the above-described first step can be heated to a temperature which is higher by 10 to 100 °C than the temperature which is in the first step to prepare the under-layer. The substrate temperature for preparing the under-layer may be a temperature at which the c-axis oriented thin film usually grows directly on the same substrate. An important advantage of this embodiment of the present invention resides in that the a-axis oriented upper-layer of oxide superconducting material can be prepared by using a higher substrate temperature which corresponds to a temperature for realizing the c-axis oriented thin film directly on a substrate and which has not been able to be used to prepare the a-axis oriented thin film by laser evaporation method. In other words, in the process according to the present invention, an upper-layer of a-axis oriented thin film can be grown on an under-layer which is also an a-axis oriented thin film, at an optimum substrate temperature which is indispensable to supply a sufficient amount of oxygen into crystals in order to prepare an oxide superconducting thin film possessing improved crystallinity and electrical properties on a substrate. This merit is obtained by such a fact that the upper-layer grows in the form of an a-axis oriented thin film on an under-layer even if film formation is effected at a relatively higher substrate temperature, because crystal growth of the upper-layer is effected on a crystal structure of the under-layer which has been prepared in the form of an a-axis oriented thin film. The substrate is preferably a single crystal substrate of oxide such as MgO, SrTiO₃, LaAlO₃, LaGaO₃ and yttrium stabilized zirconia (YSZ). The process according to the present invention can be used for preparing thin films of any high-temperature oxide material and is advantageously applicable to oxide superconducting materials of Y-Ba-Cu-O system and Bi-Sr-Ca-Cu-O system of which the composition as well as the manufacturing processes are known. The process according to the present invention has following merits: (1) Laser evaporation method can be used for preparing an a-axis oriented thin film of high-temperature oxide superconductor. Laser evaporation method has such an important merit that proportions of elements in the deposited thin film can be maintained much more uniformly compared to the product prepared by vacuum evaporation method in which a plurality of evaporation sources are evaporated independently or separately, since the elements are evaporated instantaneously by the laser evaporation method. (2) The process according to the present invention can be carried out by changing simply the substrate temperature without modifying the conventional laser evaporation apparatus. (3) The resulting thin films obtained by the process according to the present invention possess uniform quality and improved superconducting properties, so that they can be utilized in practical uses in the field of electronics of high-temperature oxide superconductors. Brief Description of the Drawing Fig. 1 is a diagrammatical cross-sectional view of a product obtained by the process according to the present invention. A thin film of high-temperature oxide superconducting material which is illustrated in Fig. 1 and is prepared in Examples 1 and 2 was prepared by depositing an under-layer 1 on a substrate 3 of MgO (100) single crystal by RF-magnetron sputtering and then by depositing an upper-layer 2 of the same high-temperature oxide superconducting material on the under-layer 1. Description of the Preferred Embodiments Now, the present invention will be described with reference to examples, but the scope of the present invention should not be limited thereto. Example 1 In this Example, an under-layer of a-axis oriented thin film of Y-Ba-Cu-O oxide superconducting material was deposited on MgO (100) single crystal by RF-magnetron sputtering and then an upper-layer of the same Y-Ba-Cu-O oxide superconducting material was deposited thereon by laser deposition method. In the RF-magnetron sputtering used for preparing the under-layer, a sintered oxide target having a composition of Y : Ba : Cu = 1 : 2 : 3 was used. Operational conditions used for preparing the under-layer are summarized in Table 1. Then, on the resulting under-layer of Y-Ba-Cu-O oxide superconducting material, an upper-layer of same Y-Ba-Cu-O oxide superconducting material was deposited by laser evaporation method in the same chamber. In the laser evaporation method used for preparing the upper-layer, the same sintered mass having a composition of Y : Ba : Cu = 1 : 2 : 3 was used as a target. Operational conditions used are summarized in Table 2. After deposition, superconducting properties of the resulting thin film of oxide superconductor was determined to find Tc of 89 K. Crystallinity of the resulting upper-layer prepared by the present invention was analyzed by a reflective high-energy electron diffraction (RHEED) analyzer to find that a long distance structure of the c-axis direction appeared in a direction which is perpendicular to an incident beam. This fact reveals that the resulting upper-layer is an a-axis oriented thin film. Example 2 Example 1 was repeated, but the Y-Ba-Cu-O target was changed to a sintered oxide target having a composition of Bi : Sr : Ca : Cu = 2 : 2 : 2 : 3. Operational conditions used for preparing the under-layer are summarized in Table 3. Then, on the resulting under-layer of oxide superconducting thin film, a thin film of oxide superconductor was prepared by laser evaporation method. As a target, there was used a sintered mass having a composition of Bi : Sr : Ca : Cu = 2 : 2 : 2 : 3. Operational conditions used for preparing the upper-layer are summarized in Table 4. After the deposition, superconducting properties of the resulting thin film of oxide superconductor was determined to find Tc of 101 K. Crystallinity of the resulting upper-layer prepared by the present invention was analyzed by a reflective high energy electron diffraction (RHEED) analyzer to find that a long distance structure of the c-axis direction appeared in a direction which is perpendicular to an incident beam. From this fact, it was revealed that the high-temperature superconducting thin films are a-axis oriented thin films possessing improved superconductivity.

Claims: A process for preparing an a-axis oriented thin film of oxide superconducting material on a substrate (3), characterized in that an under-layer (1) of the oxide superconducting material having an a-axis orientation of crystal is deposited in a first step on the substrate (3) by any physical vapour deposition (PVD) technique other than laser evaporation method at a substrate temperature which is suitable to realize the a-axis oriented thin film, and in that an upper-layer (2) of the same oxide superconducting material is deposited in a second step on the resulting under-layer (1) by laser evaporation method at another substrate temperature which is higher than that substrate temperature used in the first step. The process set forth in Claim 1 wherein said upper-layer (2) is produced to have a thickness of more than 100 Å. The process set forth in Claim 1 or 2 wherein said under-layer (1) is deposited up to a thickness of 20 to 1,000 Å. The process set forth in Claim 3 wherein said under-layer (1) is produced by sputtering method. The process set forth in Claim 4 wherein said sputtering method is RF sputtering. The process set forth in any one of Claims 1 to 5 wherein said substrate (3) is a single crystal substrate of oxide. The process set forth in Claim 6 wherein said substrate (3) is a single crystal substrate of an oxide selected from the group comprising MgO, SrTiO₃, LaAlO₃, LaGaO₃, and yttrium stabilized zirconia (YSZ). The process set forth in any one of Claims 1 to 7 wherein said oxide superconducting material is a compound oxide of Y-Ba-Cu-O system or Bi-Sr-Ca-Cu-O system. The process set forth in any one of Claims 1 to 8 wherein said upper-layer (2) is deposited at a substrate temperature which is higher by 10 to 100°C than the substrate temperature used in the first step. The process set forth in Claim 8 wherein said upper-layer (2) of the oxide superconducting material is deposited under such a condition that said substrate (3) is heated to a temperature corresponding to the temperature at which c-axis oriented thin film is prepared when the same thin film is deposited directly on said substrate (3).

Inventors: ITOZAKI HIDEO C O ITAMI WORKS, NAKANISHI HIDENORI C O ITAMI W, TANAKA SABURO C O ITAMI WORKS, ITOZAKI, HIDEO, C/O ITAMI WORKS, NAKANISHI, HIDENORI, C/O ITAMI WORKS, TANAKA, SABURO, C/O ITAMI WORKS
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1991
Main classification: H01L39
IPC codes: H01L39