Method for forming crystal article

Abstract: A method for forming a crystal article comprises forming a plurality of monocrystals with a desired size at a desired position on a substrate comprising an amorphous insulating material and having a non-nucleation surface by crystal forming treatment, wherein prior to the crystal forming treatment a plurality of concavities with a desired size and form are formed respectively in a region to be covered with a single monocrystal on the substrate, and a single monocrystal is formed to full the plurality of concavities by the crystal forming treatment and thereafter the monocrystal is flattened by removing it to the same level as the upper surface of the substrate.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a method for forming a crystal article, and particularly relates to a method for forming a crystal article comprising forming a plurality of monocrystals with controlling their positions and sizes on an amorphous insulating substrate, and then flattening the monocrystals. The present invention is applicable to a method for forming crystal articles which are used in semiconductor integral circuits, magnetic circuits and so on. Related Background Art In the field of SOI (Silicon On Insulator) technology that a plurality of monocrystals is grown on an insulating substrate, for example, as the first method, there is proposed a method for forming crystals based on selective nucleation due to the difference of nucleation density between the surface materials (T. Yonehara et al. (1987) Extended Abstracts of the 19th SSDM. 191). This method for forming crystals is described with reference to Figs. 2A to 2C. As shown Fig. 2A, first, regions 207 and 207' which have the surfaces with a larger nucleation density than that of a surface 203 are arranged on a substrate 201 having the surface 203 with a small nucleation density, a diameter of a and an interval of b. When this substrate is crystal-forming treated, nuclei 209 and 209' of deposite are deposited only on the surfaces of the regions 207 and 207', and nuclei are not deposited on the surface 203 (Fig. 2B). Therefore, the surface of regions 207 and 207' are called as nucleation surfaces, and the surface 203 is called as non-nucleation surface. When the nuclei 209 and 209' generated on the nucleation surfaces 207 and 207' are further grown, crystal grains 210 and 210' are grown beyond the regions 207 and 207' until on the non-nucleation surface 203, and at last the crystal grain 210 grown from the nucleation surface 207 is contacted with the crystal grain 210' grown from the nucleation surface 207' to form a grain boundary 211 (Fig. 2C). As the above method for forming crystals in the prior art, there have been reported an example in which a plurality of Si monocrystals is formed by a CVD method using amorphous silicon nitride as the nucleation surfaces 207 and 207' and silicon oxide as the non-nucleation surface 203 (see the above paper); and an example in which silicon oxide is used as the non-nucleation surface 203, and Si ions are implanted into the non-nucleation surface 203 by convergent ion beam to form the nucleation surfaces 207 and 207', and a plurality of Si monocrystals is formed by CVD method (35th Meeting of Unions of Applied Physics, 28p-M-9, (1988)). As the second method, there has been reported an example that seed crystals are arranged on a non-nucleation surface instead of nucleation surfaces, and single crystal grains are grown by growing the seed crystals (Meeting of Physical Society, Preliminary Abstracts II, 27a-C-2, (1990)). Relating to flattening of crystal groups obtained by the above-mentioned methods for forming crystals, for example, Japanese Patent Application Laid-Open No. 2-209730 has proposed a selective polishing. This is a technique which comprises conducting the selective polishing by making use of the difference in mechanical processing speeds to grinding particles. Specifically, the surface of a body to be polished in which the surface of region having a higher processing speed is higher in level than the surface of region having a lower processing speed, is mechanically polished with a processing liquid containing the above-mentioned grinding particles, and the region having a higher processing speed is flattened to the region having a lower processing speed, where the latter is used as a stopper. Flattening treatment of crystals formed by the above first and second methods for forming crystals, for example was carried out as follows by use of the above-mentioned technique. Figs. 3A to 3C are cross-sectional views for illustrating flattening processes. As shown in Fig. 3A, concavities are previously formed on a substrate 301 having a lower processing speed compared with that of crystal, and then nucleation surfaces or seed crystals (in this case, a nucleation surface 307 is used) are formed. Next, as shown in Fig. 3B, a single monocrystal at the center of the nucleation surface 307 is grown to the non-nucleation surface 303, and the concavity is filled with the grown monocrystal 310. Then, as shown in Fig. 3C, the monocrystal 310 is flattened by polishing until all the upper surface 313 of the substrate 301 is exposed. In the case of forming an integral circuit having a higher integral degree on an amorphous insulating substrate, insulator region of device is required with a smaller area than that of insulator region of device ordinarily required. So as to do that, each of device regions need to be formed separately from insulator regions. On the other hand, the forms of crystal regions required for individual devices used in integral circuits are not only square, but also are rectangular, a shape of ⊐ and so on, and are not necessary consistent with the forms of monocrystals obtained by the above first and second methods. In order to maintain high characteristics of devices, it is required that a crystal grain boundary is not contained in device region. However, when such great monocrystal is grown so as to contain no crystal grain boundary within the region required for a device, parts not capable of being used as the device region are present in one single crystal region, resulting in increasing the area required for forming a total integral circuit, and also making longer wiring between devices. In EP-A-0 276 959 a process for producing crystal articles is disclosed comprising the step of preparing a substrate having a concavity and a nucleation surface provided thereon, that nucleation surface being a material which is greater in nucleation density than the substrate material. On that nucleation surface a single nucleus is formed and starting from that single nucleus a single crystal is grown by applying crystal growth treatment. After crystal growth the portion of the single crystal projecting over the concavity is selectively polished. This method has the disadvantage that the nucleation surface (seed crystal) has to be arranged within the concavity to be covered but cannot be arranged at any position within a region containing a plurality of concavities to be covered with a single monocrystal. Therefore, it is impossible to form semiconductive devices with different sizes and forms while carrying out electrical separation of the devices. SUMMARY OF THE INVENTION An object of the present invention is to provide a method for forming a crystal article by forming a plurality of monocrystals with the desired size on the desired positions of a substrate, which comprises forming flat monocrystals in a concavity having the desired form and size so as to be able to form a device at the desired position required in integral circuits. The present invention to solve the above problems is a method for forming a crystal article comprising the steps of a) providing a substrate having a non-nucleation surface comprising an amorphous insulating material, b) forming a plurality of concavities with a desired size and form in a region to be covered with a single monocrystal on the substrate, c) forming a seed crystal or nucleation surface for monocrystal formation at any position within the region on the substrate, d) growing a monocrystal from the seed crystal or nucleation surface to cover the plurality of concavities with the monocrystal, and e) flattening the monocrystal by removing it to the same level as the upper surface of the substrate, wherein in the step b) the plurality of concavities have different sizes and forms. When a crystal is grown from the upper part to the lower part of a level-difference beyond the level-difference, there is a case that a void or a defect is formed at the level-difference. In the case, when a device is formed using that part, the characteristics of device are deteriorated such as low mobility and increase of leak current. The present inventor has considerably examined methods for forming crystal articles. As the result, he has found that when the level-difference is shallow or has a slope with an obtuse angle, a void or a defect is prevented at the level-difference, and a single crystal can be formed beyond the level-difference over a plurality of concavities. In this case, the depth of concavity is 2 µm or less, preferably 1 µm or less. Moreover, when the side wall of the concavity was perpendicular, preferably had a slope which shifts to the upper perifery of the concavity at an obtuse angle, crystallinity of such slope was better at the periphery of the side wall. Accordingly, the starting point of crystal growth is not limited to the inside of concavity, and may be the upper surface of a substrate. Using the desired position of the substrate as the starting point, a single monocrystal can be grown so as to fill a plurality of concavities, whereby flat monocrystal regions required for integral circuits can be formed at the concavities having the desired positions, forms and sizes. Further, by arranging devices with a high density on the flat single crystal regions, a circuit having good performances can be formed. BRIEF DESCRIPTION OF THE DRAWINGS Figs. 1A to 1C are cross-sectional views illustrating one embodiment of the present invention and steps of forming a crystal thin film according to an Example. Figs. 2A to 2C are cross-sectional views illustrating steps of forming crystals according to the prior art. Figs. 3A to 3C are cross-sectional views illustrating steps of flattening treatment. Figs. 4A and 4B are plane views illustrating a crystal thin film according to the present invention and a circuit formed on the crystal thin film. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS One embodiment of the method for forming a crystal article of the present invention is described with reference to Figs. 1A to 1C. Substrate A substrate 101 to be used in the present invention may consist of a material (a stopper material) which acts as a non-nucleation surface in crystal forming treatment, and has a slower mechanical processing speed than that of deposited crystal to grinding particles in flattening step, or may consist of such material formed on a subbing substrate. The form of substrate 101 is not limited, so far as it is proper for a crystal forming treatment and flattening step. Materials to act as a non-nucleation surface and also as stopper material, are different depending on deposited materials. For example, when a material to be deposited is silicon, glass such as quartz, etc. or alumina is used, and the surface of it is made a non-nucleation surface by treatment such as oxidation, nitriding, etc. Stopper materials include silicon, metals and so on. Concavity In the present invention, monocrystals finally remain only at the concavity formed on a substrate. The concavities are formed on a substrate so as to be filled with a monocrystal formed with controlling its position in crystal forming treatment. The concavities are formed with the position, number, form and size required in the following formation of integral circuit, etc. within the region filled with a single monocrystal. The method for forming the concavities is not particularly restricted unless it is responsible for contamination by impurities in the next step. For example, there is a method comprising forming a pattern by lithography used in the ordinary silicon process, followed by etching by wet etching or reactive ion etching. In the case of forming concavities on a substrate, the concavities may be formed on a subbing substrate, followed by forming non-nucleation surfaces or nucleation surfaces thereon, or a material having non-nucleation surfaces or nucleation surfaces is deposited on a subbing substrate, followed by forming the concavities on the upper surface of the material. Crystal Forming Treatment A method for forming a monocrystal grain on a substrate include, for example, the above-mentioned first and second methods, but are not limited to these methods. In the first method, a non-nucleation surface 103 and nucleation surfaces 107-1, 107-2 and 107-3 are formed on a subbing substrate to form a substrate (Fig. 1A). The nucleation surfaces may be present on the upper surface of the subbing substrate or on the surface of a film newly deposited on the subbing substrate. The nucleation surface should have a larger nucleation density for a material constituting a monocrystal than that of the non-nucleation surface, and also have a sufficiently small area so as to form only a single nucleus from which a monocrystal is grown. The nucleation density of the nucleation surface may be 10² times, preferably 10³ times more than that of the non-nucleation surface. For example, in the case that the non-nucleation surface comprises silicon oxide film or quartz glass, materials for nucleation surface include silicon nitride film and silicon oxide, silicon nitride, etc. containing excess of Si, but are not limited to them. As shown in Fig. 1B, the following step is a crystal forming step. Methods for forming a crystal include chemical vapor deposition (CVD) method, MOCVD method, plasma CVD method, etc. In the second method a non-nucleation surface is formed on a subbing substrate, followed by arranging seed crystals on the non-nucleation surface instead of nucleation surfaces 107 to form a substrate. The seed crystals are grown in the same manner as in the first method to form monocrystals. The non-nucleation surface may be the surface of the substrate itself or the surface of a material deposited on the subbing substrate. The material is not restricted so far as it is an amorphous insulating material. It is essential in the present invention that nuclei are not grown on the non-nucleation surface during crystal growth. For example, the material for non-nucleation surface includes a silicon oxide film, quartz glass, a silicon nitride film and so on. Prior to crystal forming treatment, minute monocrystals which are a material constituting the crystal, are arranged at the desired positions as seed crystals. For example, this method comprises arranging primary seeds having a sufficiently small surface area so as to aggregate (agglomerate) a material constituting the crystal by heat treating at the desired positions on the non-nucleation surface with a minute size, and then heat treating the primary seeds at a lower temperature than the melting temperature of them under hydrogen atmosphere to to grow monocrystals from the primary seeds. In addition, seed crystals may be formed by heat treating a polycrystalline semiconductor film added with a high concentration of impurity such as phosphorus, boron, arsenic, etc. This method is due to monocrystallize by abnormal grain growth of a grain in the polycrystalline film. The crystal forming treatment is the same as in the first method. As the result of the crystal forming treatment, a monocrystal having the desired size is obtained. In any crystal forming method, the starting point for crystal growth may be within the concavities or outside the concavities (the upper surface of the substrate). Flattening Process After forming crystals on a substrate, flattening treatment is carried out. The flattening is conducted by polishing in this case. For example, using a polishing apparatus used usually in polishing of silicon wafers, polishing is conducted by use of a polishing liquid comprising a suspension of grinding particles such as colloidal silica, etc. Crystal grains formed by crystal forming treatment of the present invention have a peak form. As progress of polishing, the crystal grains are polished from their tops parallel to the surface of the substrate, and polishing is completed when the upper surfaces of the crystal grains has the same level as the upper surface of the substrate which acts as a stopper (Fig. 1C). When a field-effect transistor is formed in the crystal layer formed thus having a size of from several µm to several tens µm and containing no crystal grain boundary, for example a single crystal silicon layer, the transistor exhibits performances comparable to that of a transistor formed on a monocrystal silicon wafer. Constructed complementary field-effect transistors (C-MOS transistors) do not interfere with each other because adjacent monocrystal silicon layers are electrically separated by silicon oxide. Moreover, because the thickness of the active layer of device is thinner than that of Si wafer, erroneous working by charge in the wafer generated by irradiation of radiation does not occur. In addition, a speeding-up of the device is possible because the parasitic capacity of the device is reduced. Monocrystal layers are economically formed on a substrate having a great area compared with using Si wafers because any substrate can be used. Also, because monocrystals can be formed on other substrates such as semiconductor, piezoelectric element, dielectric etc., three dimensional integral circuits with multiple-functions can be realized. Examples of the present invention are described in detail with reference to Figs. 1A to 1C and Fig. 4A and Fig. 4B. Example 1 An example in which a plurality of Si monocrystal thin films was formed according to the present invention is described below. (1) On a fused quartz glass substrate 101 comprising a square having sides of 30 µm, a concavity comprising an area of 10 µm x 26 µm and a depth of 1,000 nm (10,000 Å) and two concavities comprising an area of 10 µm x 12 µm and a depth of 1,000 nm (10,000 Å) were formed by photolithography and etching with a buffered hydrofluoric acid as shown Fig. 4A. In this case, the side walls of the concavities were sloped by side-etching. The surface formed thus was a non-nucleation surface (Fig. 1A). For comparison, a substrate having a surface comprising concavities with the same size as in the above surface and a depth of 4 µm formed by reactive ion etching, was prepared. (2) Next, a silicon nitride film was deposited to 100 nm (1,000 Å) thickness as a nucleation surface thin film by reduced CVD method using dichlorosilane and ammonia. By patterning this silicon nitride film, as shown in Fig. 4A, silicon nitride comprising a square having sides of 2 µm was arranged as a nucleation surface 107 at the stopper position between the above three concavities (Fig. 1A). (3) When these substrates were set on a CVD apparatus, by crystal forming treatment under the conditions of 10666 Pa (80 Torr), 1050 °C and SiH₂Cl₂/HCl/H₂ = 0.53/1.5/100 (l/min), Si nucleus was formed only on the silicon nitride area. As continuing crystal growing, the crystal was isotropically grown from the nucleation surface, contacted with the adjacent crystal, and further filled the void of the concavity to form a square having sides of 30 µm of which shape was a peak shape having a height of 20 µm (Fig. 1B). (4) Then, monocrystals were polished using a processing liquid containing colloidal silica (an average particle size: 0.1 µm) comprising silicon oxide by use of an ordinary silicon wafer surface-polishing apparatus under a pressure of 100 g/cm² at 30 °C to 40 °C. As the result, as shown in Fig. 1C, Si monocrystals were polished, and polishing was completed when Si monocrystals became the same level as the stopper 113 to give a flat Si monocrystal thin film having a thickness of 1,000 ± 40 nm (10,000 Å ± 400 Å) on the 4 inch fused quartz glass substrate. In other 9 sheets of substrate simultaneously polished, the obtained Si monocrystal thin films had a thickness of 1,000 nm ± 50 nm (10,000 Å ± 500 Å). When the cross-section of the monocrystals were observed by defect actuarizing etching, that is, secco etching, defects were not found particularly near the side walls, voids were not generated, and the crystals had good crystallinity. On the other hand, for comparison, when the cross-section of monocrystals formed on the comparative substrate containing concavities having a depth of 4 µm were observed similarly by secco etching, a void had been formed under the lower part of the side wall of concavity, and a defect had been formed on the upper part of the level-difference, which is assumed to be introduced when the crystal get over the level-difference. (5) A NAND circuit was formed on these monocrystals using MOS transistors prepared by use of ordinary semiconductor process as shown in Fig. 4B. In Fig. 4B, two n-MOS transistors were formed on the concavity 401, and p-MOS transistor was formed in the concavities 402 and 402', respectively. 403, 404, and 405 are a p-type semiconductor region comprising source and drain of n-MOS transistor. 406, 407, 408 and 409 are an n-type semiconductor region comprising source and drain of p-MOS transistor. The above regions were formed by ion implanting As and B into monocrystals in the concavities, respectively. 410 and 411 are gate electrodes formed on the gate oxide film. A gate length L and a gate width W were L/W = 6 µm/10 µm in n-MOS and L/W = 3 µm/10 µm in p-MOS, respectively. Therefore, although the concavities were different in size and form, no crystal grain boundary was present in the concavities because the crystals were grown to fill all the three concavities, and performances of the transistors were comparable to that of transistors formed monocrystal silicon wafers. Example 2 Example 2 in which a plurality of Si monocrystal grains was formed according to the present invention is described below. (1) On an Si wafer substrate, a silicon oxide film was deposited to 1,300 nm (13,000 Å) thickness by heat oxidation method, and then rectangular concavities having an area of 8 µm x 28 µm and a depth of 500 nm (5,000 Å) were formed at 2 µm intervals by photolithography and etching with a buffered hydrofluoric acid. The surface formed thus was a non-nucleation surface (Fig. 1A). (2) Next, a silicon nitride film was deposited to 30 nm (300 Å) thickness on the substrate by LPCVD method. Then, by patterning this silicon nitride film by photolithography used in the ordinary semiconductor process and reactive ion etching (RIE), squares of SiN₄ having sides of 2 µm were arranged as nucleation surfaces 107 in lattice pattern at 30 µm intervals, where the nucleation surface was placed at the each center of the concavities (Fig. 1A). (3) On the above substrate, crystal forming treatment was carried out by CVD method using dichlorosilane, hydrogen chloride and hydrogen. The conditions for crystal growth were as follows. SiH₂Cl₂/HCl/H₂ = 0.53/1.4/100 (l/min), 990 °C, 10,666 Pa (80 Torr). As the result, a crystal was isotropically grown from the nucleation surface, contacted with the adjacent crystal, and further filled the void of the concavity to form a square having sides of 30 µm, where the crystal shape was a peak form having a height of about 20 µm. (4) Then, Si monocrystals were polished using a processing liquid containing colloidal silica (an average particle size: 0.1 µm) of SiO₂ by an ordinary silicon wafer surface-polishing apparatus under a pressure of 100 g/cm² at 30 °C to 40 °C. As the result, as shown in Fig. 1C, Si monocrystals were polished, and polishing was completed when Si monocrystals had the same level as the stopper 113 which was the silicon oxide film region directly formed on the substrate to give a flat Si monocrystal thin film having a thickness of 500 nm ± 20 nm (5,000 Å ± 200 Å) in each concavity on the 4 inch Si wafer substrate. In other 9 sheets of substrate simultaneously polished, the obtained Si monocrystal thin films had a thickness of 500 nm ± 25 nm (5,000 Å ± 250 Å). Example 3 (1) On a fused quartz glass substrate 101, rectangular concavities having an area of 5 µm x 15 µm and a depth of 500 nm (5,000 Å) were formed at 5 µm intervals by photolithography and reactive ion etching. The surface formed thus was a non-nucleation surface (Fig. 1A). (2) Next, a polycrystalline silicon film was deposited to 200 nm (2,000 Å) thickness on the surface by LPCVD, and then ³¹P⁺ (phosphorus) was implanted as an impurity into the silicon film at an acceleration voltage of 30 KeV and 2 x 10¹⁵cm⁻². Then, by patterning the silicon film by photolithography used in the ordinary semiconducter process and reactive ion etching (RIE), squares of polycrystalline silicon film having sides of 1.2 µm were arranged as primary seeds at 20 µm intervals in lattice pattern, where each primary seed was placed at the stopper region between the adjacent concavities (Fig. 1A). (3) Next, the substrate was heat treated at 1,100 °C under hydrogen atmosphere for 3 min. As the result, each primary seed was aggregated to form a monocrystal seed. (4) On the above substrate, crystal forming treatment was carried out by CVD method using dichlorosilane, hydrogen chloride and hydrogen. The conditions for crystal growth were as follows. SiH₂Cl₂/HCl/H₂ = 0.53/1.6/100 (l/min), 1,040 °C, 10,666 Pa (80 Torr). As the result, a monocrystal having a particle size of 28 µm was formed from each nucleation surface as the starting point. (5) Then, Si monocrystals were polished using a processing liquid containing colloidal silica (an average particle size: 0.1 µm) of SiO₂ by an ordinary silicon wafer surface-polishing apparatus under 100 g/cm² at 30 °C to 40 °C. As the result, as shown in Fig. 1C, Si monocrystals were polished, and polishing was completed when Si monocrystals became the same level as the stopper 113 to give a Si monocrystal thin film having a thickness of 500 nm ± 20 nm (5,000 Å ± 200 Å) each on the 4 inch fused quartz glass substrate. In other 9 sheets of substrate simultaneously polished, the obtained Si monocrystal thin films had a thickness of 500 nm ± 25 nm (5,000 Å ± 250 Å). Example 4 (1) On a Si wafer substrate, a silicon oxide film was deposited to 1,000 nm (10,000 Å) thickness by heat oxidation method, and then rectangular concavities having an area of 5 µm x 15 µm and a depth of 800 nm (8,000 Å) were formed on the substrate at 5 µm intervals by photolithography and etching with a buffered hydrofluoric acid. Then, a silicon nitride film was formed to 100 nm (1,000 Å) thickness on the concavities by LPCVD method. The surface formed thus was a non-nucleation surface (Fig. 1A). (2) Next, a polycrystalline silicon film doped with P (phosphorus) of 3 x 10¹⁵ cm⁻² was deposited to 25 nm (250 Å) thickness on the surface by LPCVD method. By patterning this silicon film by EB (electron beam) exposure method, squares of polycrystalline silicon film having sides of 0.3 µm were arranged as primary seed at 20 µm intervals, where each primary seed was placed at the stopper region between the adjacent concavities (Fig. 1A). Next, the substrate was heat treated at 990 °C under hydrogen atmosphere for 2 min. to convert the primary seeds to monocrystal seeds. (3) On the above substrate, crystal forming treatment was carried out by CVD method using dichlorosilane, hydrogen chloride and hydrogen. The conditions for crystal growth were as follows. SiH₂Cl₂/HCl/H₂ = 0.53/2.0/100 (l/min.), 990 °C, 10,666 Pa (80 Torr). As the result, a monocrystal having a particle size of 28 µm was formed from each nucleation surface as the starting point. (4) Then, Si monocrystals were polished using a processing liquid containing colloidal silica (an average particle size: 0.01 µm) of SiO₂ by an ordinary silicon wafer surface-polishing apparatus under a pressure of 100 g/cm² at 30 °C to 40 °C. As the result, as shown in Fig. 1C, Si monocrystals were polished, and polishing was completed when Si monocrystals had the same level as the stopper 113 which was the silicon oxide film region directly formed on the substrate to give a flat Si monocrystal thin film having a thickness of 800 nm ± 40 nm (8,000 Å ± 400 Å) in each concavity on the 4 inch Si wafer substrate. In other 9 sheets of substrate simultaneously polished, the obtained Si monocrystal thin films had a thickness of 800 nm ± 45 nm (8,000 Å ± 450 Å). As described above, according to the method for forming crystal articles of the present invention, monocrystal thin films can be formed on an amorphous substrate in the state that each monocrystal thin film is surrounded by an insulator region and is flat and precisely controlled at the desired positions with the desired form. Accordingly, integral circuits can be formed without lengthening wiring and also with small limitation in device arrangements. Integral circuits utilizing characteristics of monocrystal thin film can be formed without variation of the performances and also with a higher integral degree and yield. A method for forming a crystal article comprises forming a plurality of monocrystals with a desired size at a desired position on a substrate comprising an amorphous insulating material and having a non-nucleation surface by crystal forming treatment, wherein prior to the crystal forming treatment a plurality of concavities with a desired size and form are formed respectively in a region to be covered with a single monocrystal on the substrate, and a single monocrystal is formed to fill the plurality of concavities by the crystal forming treatment and thereafter the monocrystal is flattened by removing it to the same level as the upper surface of the substrate.

Claims: A method for forming a crystal article comprising the steps of: a) providing a substrate having a non-nucleation surface comprising an amorphous insulating material, b) forming a plurality of concavities with a desired size and form in a region to be covered with a single monocrystal on the substrate, c) forming a seed crystal or nucleation surface for monocrystal formation at any position within the region on the substrate, d) growing a monocrystal from the seed crystal or nucleation surface to cover the plurality of concavities with the monocrystal, and e) flattening the monocrystal by removing it to the same level as the upper surface of the substrate, wherein in the step b) the plurality of concavities have different sizes and forms. The method according to claim 1, wherein flattening of the monocrystal is carried out by mechanically polishing the monocrystal to the same level as the upper surface of the substrate by using a processing liquid containing grinding particles, utilizing the upper surface of the substrate comprising a material having a lower mechanical processing speed than that of the monocrystal to the grinding particles as a stopper. The method according to claim 1, wherein the substrate having a free surface being the non-nucleation surface and a nucleation surface having a larger nucleation density than that of the non-nucleation surface for a material constituting the monocrystal and a sufficiently small area so as to form only a single nucleus from which a monocrystal is grown are arranged adjacent to each other, is subjected to the crystal forming treatment to form a nucleus on the nucleation surface, and the nucleus is grown to a single monocrystal. The method according to claim 1, wherein the non-nucleation surface and a single monocrystal seed are formed on the substrate and a single monocrystal is grown from the seed as the starting point. The method according to claim 3, wherein the non-nucleation surface comprises an amorphous material. The method according to claim 4, wherein the monocrystal seed is formed by heat treating a primary seed having a sufficiently small area so as to agglomerate by heat treatment at a lower temperature than the melting temperature of the primary seed under hydrogen atmosphere to form a monocrystal. The method according to claim 3 or 6, wherein the monocrystal is silicon.

Inventors: SATO NOBUHIKO C O CANON KABUSH, SATO, NOBUHIKO, C/O CANON KABUSHIKI KAISHA
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1991
Main classification: C30B25
IPC codes: H01L29, C30B25, H01L21, H01L27, C30B29