A pressure-sensitive adhesive and a pressure sensitive construction containing a layer of the adhesive

Abstract: A pressure-sensitive adhesive comprising or consisting of an ethylene-vinyl acetate copolymer having a vinyl acetate content of more than 40% by weight. Preferably the pressure-sensitive adhesive also comprises a plasticizer and a modifying thermoplastic polymer which is a) sufficiently polar to show compatibility with plasticizer and b) sufficiently compatible with the ethylene-vinyl acetate copolymer. A preferred pressure-sensitive adhesive comprises 50-85% by weight of ethylene-vinyl acetate copolymer, 10-30% by weight of plasticizer and 5-20% by weight of the modifying polymer. The pressure-sensitive adhesive may be used for permanently adhering a front layer to a substrate, e.g. plasticized polyvinyl chloride. Pressure-sensitive constructions are also disclosed.

Description: The invention relates to a pressure-sensitive adhesive, to the use thereof for permanently adhering a front layer to a substrate, to a pressure-sensitive construction consisting of at least one front layer and a pressure-sensitive layer, and to a method for preparing such a pressure-sensitive construction. The invention especially relates to a pressure-sensitive adhesive which is suitable for adhering front materials to substrates containing monomeric plasticized polyvinyl chloride. Such vinyl substrates are used on a large scale for indoor surfaces such as wall coverings and outdoor surfaces such as vinyl-coated canvas for trucks. These vinyl substrates contain as much as 25 - 75 parts of monomeric plasticizer per 100 parts of vinyl resin. Letters, figures or drawings can be applied to such vinyl substrates by painting or printing with silk-screen ink. For this purpose a pressure-sensitive film imprinted with letters, figures etc., or cut into the shape of letters, figures, etc. can be used too. The front layer as well as the adhesive layer of such a pressure-sensitive film must meet certain requirements in order to prevent problems occuring by migration of plasticizer out of the substrate into the film. If materials are used which are unsuitable for the front layer and/or the adhesive layer, the front layer may tend to wrinkle or become sticky and the adhesive layer may lose its adhesive strength. European patent application 103.407 discloses a pressure-sensitive film that is suitable for adhesion to a vinyl substrate containing monomeric plasticizer. This film comprises a first layer of poly-vinyl chloride, a second layer of a pasticizer resistant pressure-sensitive adhesive, and a third layer between the first and second layers, serving as a barrier for plasticizer from the substrate. As suitable adhesives polyacrylates are disclosed that are a conbination of the following monomers: a)acrylic acid, methacrylic acid, acrylic amide and/or methacrylic amide, b) an alkyl acrylate and/or alkyl methacrylate and c) at least one additional ethylenically unsaturated monomer. In European patent application 330.272 the suggestion is made to replace the polyvinyl chloride outer layer and the barrier layer of the above-mentioned film by one single layer consisting of a mixture of polyvinyl chloride and chlorinated polyethylene. For the adhesive layer reference is made to the above European patent application. The group of adhesives from which a choice can be made as to the adhesion of front materials that are generally based on plasticized polyvinyl chloride to substrates containing monomeric plasticized polyvinyl chloride, is therefore rather limited. It is now an object of this invention to provide an adhesive for the application stated above, offering a stronger adhesion than the adhesives known sofar. It is a further object of this invention to provide an adhesive that adheres strongly shortly after application to the substrate. Yet another object is to provide an adhesive that presents good properties when applied outside at usual ambient temperatures. Now a new pressure sensitive adhesive has been found comprising a blend of at least 5% by weight of an ethylene-vinyl acetate copolymer having a vinyl acetate content of more than 40% by weight preferably at least 50% by weight, and more preferably 60-80% by weight, 5 to 50% by weight of at least one thermoplastic polymer which fulfills at least one of the following properties: i) the thermoplastic polymer forms a single phase with the ethylene-vinyl acetate copolymer, as indicated by the presence of a single glass-transition temperature, ii) the thermoplastic polymer can be dispersed in the ethylene-vinyl acetate phase to form individual polymer particles smaller than 100 µm, and iii) the thermoplastic polymer can be dispersed in the ethylene-vinyl acetate phase to form a continuous thermoplastic polymer phase in the ethylene-vinyl acetate phase, and optionally a plasticizer. The adhesive according to the invention, applied to various front materials, offers an excellent adhesion to plasticizer containing vinyl substrates, both shortly after application to the substrate (20 min.) and after having aged for several weeks at 70°C. Shortly after application to the substrate the adhesion is so strong that it can be regarded as permanent adhesion. By the expression "permanent adhesion" as used herein it is meant that the peel force required to peel the film from selected substrates amounts at least 8 N/inch if applied during 24 hours and measured according to the procedure as described in PSTC-1. The adhesive according to the invention has been found to offer a permanent adhesion also to a limited group of other substrates, such as polymethyl methacrylate, polystyrene, hard polyvinyl chloride, polycarbonate and polyacrylonitrile-butadiene-styrene. According to another aspect the invention therefore resides in the use of a pressure-sensitive adhesive as described above for permanently adhering a front layer to a substrate, especially a substrate comprising plasticized polyvinyl chloride or any of the above-mentioned materials. If the vinyl acetate content of the ethylene-vinyl acetate copolymer is 45% by weight, a moderate adhesion is obtained. By increasing the vinyl acetate content the adhesion will increase too. Ethylene-vinyl acetate copolymers having a vinyl acetate content of more than 40% by weight are not recommended for application in adhesives, unlike copolymers having a lower vinyl acetate content. For instance, ethylene-vinyl acetate having a vinyl acetate content of 70% by weight, and used in the examples below, is especially recommended as a chlorine-free cable insulation material showing a reduced smoke formation during fire. It is noted that in Japanese patent application 61283677 ethylene-vinyl acetate is mentioned as a synthetic resin coating for rebondable note-papers capable of being repeatedly adhered to and removed from surfaces. In this application no mention is made of the vinyl acetate content and there is no indication that the vinyl acetate content should be high. It can furthermore not be derived from this patent application that an ethylene-vinyl acetate copolymer having a vinyl acetate content of more than 40% by weight can be used for permanently adhering a front layer to a plasticized vinyl substrate. The Japanese patent application only refers to the non-permanent adhering properties of synthetic resins such as ethylene-vinyl acetate. Another mention of ethylene-vinyl acetate copolymer as a pressure-sensitive adhesive is made in European patent application 299.884. However, here the vinyl acetate content is restricted to 25 - 40% by weight. A film consisting of a thermoplastic front material and such an adhesive is applied for temporarily protecting various surfaces. When the film is removed it leaves no trace of adhesive. Therefore, the adhesion in question is a non-permanent one. European patent application 201.890 uses an adhesive which is a solid thermoplastic adhesive at room temperature, e.g. ethylene-vinyl acetate. The adhesive in question is not pressure sensitive, however, as it requires heating in order to obtain adhesive properties. However, according to the present invention melting is not necessary. At ambient temperature, adhesion to the substrate is obtained by simply pressing. The vinyl acetate content of the copolymer used in the examples of the European patent application is not higher than 25% by weight. This is consistent with the recommen- dations of ethylene-vinyl acetate producers. Hot melt adhesives based on ethylene-vinyl acetate have a low vinyl acetate content, in any case less than 40% by weight. European patent application 201.890 mentions metals as the most important substrates. From this patent application it can therefore not be derived either that an ethylene-vinyl acetate copolymer having a vinyl acetate content of more that 40% by weight can be used for permanently adhering a front layer to a plasticized vinyl substrate. The addition of a plasticizer in a quantity of up to 50% by weight, preferably 10 - 30% by weight, has a favourable effect on the properties of the adhesive. The addition of the plasticizer reduces the glass transition temperature. For instance, when dioctyl phthalate, in a quantity of 20% by weight, is added to an ethylene-vinyl acetate copolymer having a vinyl acetate content of 70% by weight, the Tg drops from -12.9 o C to -28.7°C. The addition of plasticizer can therefore be especially favourable when used outdoors during winter season. Besides dioctyl phthalate, other conventional monomeric plasticizers may also be used. Regarding the thermoplastic polymer it should fulfil the properties as mentioned hereinbefore. Such a thermoplastic polymer is also a) sufficiently polar to show compatibility with plasticizer and b) sufficiently compatible with the ethylene-vinyl acetate copolymer. In particular said thermoplastic polymer incorporated in the present adhesive enhances the dimensional stability of a front material, applied on plasticized polyvinyl chloride and similar substrates, even upon ageing at elevated temperature. Said thermoplastic polymer will hereinafter often be referred to as modifier. The presssure-sensitive adhesive may comprise up to 50% by weight of the modifier, the quantity of the ethylene-vinyl acetate copolymer being at least 5% by weight. Preferred pressure-sensitive adhesives of the invention comprise 50-85% by weight of ethylene-vinyl acetate copolymer, 10-30% by weight of plasticizer and 5-20% by weight of the modifier. Generally, the modifiers are tough polymers having a relatively high molecular weight. Particularly suitable modifiers are those selected from the group consisting of cellulose esters, vinyl chloride polymers, acrylate modified styrene-acrylonitrile copolymers and mixtures thereof. Suitable examples of cellulose ester include cellulose acetate butyrate (CAB) and cellulose acetate propionate (CAP), available from e.g. Eastman Kodak Company, for examples CAB-500-5 and CAP-482-20. Suitable examples of vinyl chloride polymers include copolymers of vinyl chloride and vinyl acetate, for example VYNS, commercially available from Union Carbide, containing 90% of vinyl chloride and 10% of vinyl acetate; a terpolymer of vinyl chloride, vinyl acetate and hydroxyethyl methacrylate, for example VROH commercially available from Union Carbide; and a graft polymer of ethylene-vinyl acetate onto polyvinyl chloride, for example VK 801, containing 50% vinyl chloride and 50% grafted ethylene-vinyl acetate copolymer, commercially available from Wacker. Suitable examples of acrylate modified styrene-acrylonitrile copolymers include those commercially available from BASF, Germany, under the trade name Luran, especially Luran S 776 S. According to another aspect of the invention a pressure-sensitive construction is provided consisting of a front layer and an adhesive layer comprising the adhesive described above. The front layer may consist of the usual materials that are suitable for application to plasticized vinyl substrates. As mentioned above, the materials in question are generally thermoplastic materials that usually contain plasticizer. These front materials are often pigmented. Preferred front materials are mixtures of polyvinyl chloride and chlorinated polyethylene optionally containing a monomeric plasticizer, and polyvinyl chloride containing polymeric plasticizers. The thickness of the front layer is not critical, but it generally amounts to 0.01 - 0.15 mm. Other usual materials, e.g. paper, may also be used as the front layer material. The weight of the adhesive layer applied to the front layer is not critical either, but it generally amounts to no more than 100 g/m 2 ; a suitable amount is 30 - 90 g/m 2 . Larger amounts of adhesive result in stronger adhesion. On the side of the adhesive layer that is not covered by the front layer a release liner is usually provided for protection until actual application on a substrate. The pressure-sensitive construction according to the invention may be prepared by various methods. Preferably an adhesive according to the invention, dissolved in an organic solvent, is coated onto a release liner, the solvent is evaporated and a front layer is dry laminated onto the adhesive layer, after which the release liner is removed for use. Other methods for preparing the pressure-sensitive construction are e.g. co-extrusion and heat sealing of the two layers. The ethylene-vinyl acetate copolymer component of the adhesive according to the invention can be applied in all usual forms, for example as emulsion resin, solvent resin, etc. Emulsion resins, however, are less suitable for outdoor application because of poor weathering resistance. The examples below further illustrate the invention but should not be regarded as a restriction thereof. In all examples the pressure-sensitive constructions were made as follows: the adhesive components were dissolved in an organic solvent; the solution obtained was coated onto a release liner; the release liner was dried in a ventilated oven; the front material was heated up to 80°C and dry laminated onto the adhesive layer; the release liner was removed from the laminate and the film obtained was applied to a substrate by means of the adhesive layer. In all cases, the adhesive weight amounted to 40 g/m 2 , unless stated otherwise. The applicant used two front materials. In some of the examples a poly vinyl chloride/chlorinated polyethyleneblend (pvc/cpe) containing a monomeric plasticizer was used and in the other examples a commercially available pigmented Marking Film was used, based on polymeric plasticized polyvinyl chloride. Said front materials were each applied to a specific substrate. Unless stated otherwise, the pvc/cpe was applied to a tarpaulin cover that is usually applied to protect cargo on trucks and consists of plasticized polyvinyl chloride, reinforced with a woven structure. A commercially available blue tarpaulin supplied by Besouw in Goirle was used. Unless stated otherwise, the Marking Film was applied to a reinforced monomeric plasticized polyvinyl chloride which is commercially available from Signtech in London under the name of Signtech 20 AC. After applying the pressure sensitive construction to the substrate, 180° Peel adhesion was usually determined, after 20 min. (no ageing) and/or after ageing (during a certain period of time at 70°C). For this purpose samples of the pressure sensitive films having a length of 150 mm and a width of 25 mm were used. The samples were removed at an angle of 180° and at a speed of 300 mm/min, with the aid of a tensile testing machine at a temperature of 23 ± 2°C. Peel adhesion is indicated in N/inch. Example 1 Pressure-sensitive films were prepared according to the method described above. The adhesive components were ethylene-vinyl acetate copolymer having a vinyl acetate content of 50% by weight (No. IV of Table B) and quantities of dioctyl phthalate (DOP) varying from 0 up to 30% by weight. The pvc/cpe was used as front material (and tarpaulin as substrate). 180 o Peel adhesion was determined after 20 min. and after ageing of the whole for three weeks at 70 o C. The results are shown in Table A. Effect of ageing on adhesion DOP content (% by weight) 180 o Peel adhesion (N/inch) After 20 min. After 3 weeks at 70 o 0 16 22 10 15 23 20 14 21 30 13 19 Example 2 Pressure-sensitive films were prepared according to the method described above. The adhesive components were ethylene-vinyl acetate copolymers having vinyl acetate contents varying from 45 up to 70% by weight and dioctyl phthalate in a quantity of 10 and 20% by weight. The ethylene-vinyl acetate copolymers are mentioned in Table B. The pvc/cpe was used as front material. 180 o Peel adhesion was determined after 20 min. and after ageing of the film applied on tarpaulin for one week at 70 o C. The results are shown in Table C. Ethylene-vinyl acetate (EVA) copolymer I II III IV V Vinyl acetate content (%) 45 45 45 50 70 Melt index 2-5 5-15 15-30 2-5 2-5 Mooney viscosity 22-30 15-22 8-15 20-28 16-28 Effect of vinyl acetate content on adhesion Composition of adhesive 180 o Peel adhesion (N/inch) After 20 min. After 1 week at 70 o C I + 10% DOP 12.5 26 IV + 10% DOP 15 23 II + 20% DOP 11 22 III + 20% DOP 11 22 V + 20% DOP 30 25 Example 3 Pressure-sensitive films were prepared according to the method described above. The adhesive components were ethylene-vinyl acetate copolymer no. IV of Table B, VROH and DOP in various proportions. The pvc/cpe was used as front material. 180 o Peel adhesion was determined after 20 min. and after ageing of the film on tarpaulin for three weeks at 70 o C. The results are shown in Table D. Effect of VROH on adhesion Composition of adhesive (%) 180 o Peel adhesion (N/inch) VROH EVA DOP After 20 min. After 3 weeks at 70 o C 10 80 10 14 17 20 60 20 14 18 20 80 0 12 15 ( 1 week) 30 60 10 12 17 40 40 20 11 14 50 25 25 11 14 Example 4 Pressure-sensitive films were prepared according to the method described above. The adhesive components were ethylene-vinyl acetate copolymer V of Table B, DOP and optionally VROH. Again, the pvc/cpe was used as front material. The dimensional stability on tarpaulin was determined after ageing for 48 hours at 70 o C and after ageing for one week at 70 o C at a sample size of 150 x 150 mm. The results are shown in Table E, in which the total shrinkage is indicated. In machine direction (MD) shrinkage was found. In cross-direction (CD) expansion (negative shrinkage) was found in the absence of VROH. Effect of VROH on dimensional stability Composition of adhesive (%) 48 h, 70 o C 1 week, 70 o C VROH EVA DOP mm MD mmCD mm MD mm CD 0 100 0 1.9 < 0 2.3 < 0 0 80 20 1.9 < 0 1.7 < 0 30 50 20 0.7 0.0 0.9 0.0 Example 5 Pressure-sensitive films were prepared according to the method described above. The adhesive consisted of 70% by weight of ethylene-vinyl acetate copolymer no. V of table B, 15% by weight of VYNS and 15% by weight of DOP. The polyvinyl chloride Marking Film was used as front material and a number of substrates indicated in table F were used as substrates. The adhesive weight was 40 g/m 2 . 180 o Peel adhesion was determined after 20 minutes and 24 hours. The results are shown in table F. Effect of various substrates on adhesion Substrates 180 o Peel adhesion (N/inch) bond time 20 min. bond time 24 h. Hard PVC 17 21 Polystyrene 7 14 PMMA 9 13 Polycarbonate 8 13 ABS 9 13 Stainless Steel 2 4 Painted panel 4 5 Nylon 2 3 Example 6 Pressure-sensitive films were prepared according to the method described above. The adhesive consisted of various types of ethylene-vinyl acetate copolymers of Table B, optionally containing DOP and/or VROH, as indicated in Table G. The polyvinyl chloride Marking Film was used as front material and Signtech 20 AC was used as substrate. The adhesive weight was 32.5 g/m 2 . 180 o Peel adhesion was determined after ageing during 20 min., during 24 hours and during 24 hours + 1 week at 50 o C. The results are shown in Table G. Example 7 Pressure-sensitive films were prepared according to the method described above. The adhesive components were various ethylene-vinyl acetate copolymers of Table B, VYNS copolymer and dioctyl phtalate. Pvc/cpe was used as front material. 180 o Peel adhesion was determined after 20 min. and after ageing of the film applied on tarpaulin for one week at 70 o C. The results are shown in Table H. Composition of adhesive 180 o Peel adhesion (N/inch) After 20 min. After 1 week at 70 o I +10%VYNS+10% DOP 10.5 22 IV +10%VYNS+10% DOP 12.5 20 II +10%VYNS+20% DOP 9 19 III +10%VYNS+20% DOP 9 19 V +10%VYNS+20% DOP 25 21 Example 8 A pressure-sensitive film was prepared according to the method described above. The adhesive consisted of 50% by weight of ethylene-vinyl acetate copolymer no. V of table B, 30% by weight of VYNS and 20% by weight of DOP. The polyvinyl chloride Marking Film was used as front material and Signtech 20 AC was used as substrate. The adhesive weight was 40 g/m 2 . 180 o Peel adhesion was determined after 20 minutes, 24 hours and after 1 week ageing at 70 o C. Dimensional stability was determined after 1 week ageing at 70 o C. The results are shown in table I. 180° Peel adhesion (N/inch) bond time 20 min. 24h. 24h. + 1 week 70°C 8 15 20 Dimensional stability (shrinkage) mm Machine Direction < 0.5 mm Cross Direction < 0.5 Example 9 A pressure-sensitive film was prepared according to the method described above. A number of modifiers were evaluated in adhesive compositions, containing EVA and DOP. EVA grade V of Table B was used. The PVC/CPE was used as front material and a number of substrates indicated in the table were used as substrates. The adhesive weight was 40 g/m 2 . 180 o Peel adhesion was determined after 24 hours. Dimensional stability was determined after 72 hours ageing at 70 o C. The results are shown in table J. Adhesive compositions: MODIFIER (X) EVA/X/DOP % by weight 1 CAB -500-5 80/10/10 2 CAB -500-5 85/5/10 3 CAP-482-20 70/20/10 4 VK 801 70/20/10 5 LURAN S 776 S 70/20/10 6 LURAN S 776 S/CAB -500-5 66.5/19/9.5/5 Effect of various substrates on adhesion Adhesive compositions 180° Peel adhesion (N/inch) 1 2 3 4 5 6 Substrates Tarpaulin 17 20 15 Hard PVC 23ft 21ft 19 25ft 17 >28ft Polystyrene 13 19 12 19 15 14 PMMA 8 14 9 15 12 9 Polycarbonate 23ft 30ft 18 30ft 15 22ft ABS 10 15 9 15 13 12 Dimensional stability (shrinkage) after 72 hours, 70°C Adhesive compositions 1 2 3 4 5 6 mm Machine Direction 0.8 1.2 1.0 1.0 0.4 0.0 mm Cross Direction 0.0 0.0 0.8 0.5 0.6 0.0

Claims: Claims for the following Contracting States : BE, DE, DK, FR, GB, IT, NL, SE A pressure-sensitive adhesive comprising a blend of at least 5% by weight of an ethylene-vinyl acetate copolymer having a vinyl acetate content of more than 40% by weight, 5 to 50% by weight of at least one thermoplastic polymer which fulfills at least one of the following properties: i) the thermoplastic polymer forms a single phase with the ethylene-vinyl acetate copolymer, as indicated by the presence of a single glass-transition temperature, ii) the thermoplastic polymer can be dispersed in the ethylene-vinyl acetate phase to form individual polymer particles smaller than 100 µm, and iii) the thermoplastic polymer can be dispersed in the ethylene-vinyl acetate phase to form a continuous thermoplastic polymer phase in the ethylene-vinyl acetate phase, and optionally a plasticizer. A pressure-sensitive adhesive according to claim 1, characterized in that the vinyl acetate content of the ethylene-vinyl acetate copolymer is at least 50% by weight. A pressure-sensitive adhesive according to claim 2, characterized in that the vinyl acetate content of the ethylene-vinyl acetate copolymer is 60-80% by weight. A pressure-sensitive adhesive according to one of the claims 1 - 3, characterized in that it further com prises a plasticizer in an amount of up to 50% by weight. A pressure-sensitive adhesive according to claim 4, characterized in that the quantity of the plasticizer is 10 - 30% by weight. A pressure-sensitive adhesive according to one of the claims 1 - 5, characterized in that the thermoplastic polymer is a) sufficiently polar to show compatibility with plasticizer and b) sufficiently compatible with the ethylene-vinyl acetate copolymer. A pressure-sensitive adhesive according to claim 6, characterized in that the thermoplastic polymer is selected from the group consisting of cellulose esters, vinyl chloride polymers, acrylate modified styrene-acrylonitrile copolymers and mixtures thereof. A pressure-sensitive adhesive according to claim 7, characterized in that the thermoplastic polymer is cellulose acetate butyrate or cellulose acetate propionate. A pressure-sensitive adhesive according to claim 7, characterized in that the thermoplastic polymer is a copolymer of vinyl chloride and vinyl acetate. A pressure-sensitive adhesive according to claim 7, characterized in that the thermoplastic polymer is a terpolymer of vinyl chloride, vinyl acetate and hydroxyethyl methacrylate. A pressure-sensitive adhesive according to claim 7, characterized in that the thermoplastic polymer is a graft copolymer of ethylene-vinyl acetace onto polyvinyl chloride. A pressure-sensitive adhesive according to any of claims 6-11, characterized in that in comprises 50-85% by weight of ethylene-vinyl acetate copolymer, 10-30% by weight of plasticizer and 5-20% by weight of the thermoplastic polymer. The use of a pressure-sensitive adhesive as specified in one of the claims 1 - 12 for permanently adhering a front layer to a substrate. The use according to claim 13, characterized in that the substrate comprises plasticized polyvinyl chloride, hard polyvinyl chloride, polymethylmethacrylate, polycarbonate, polystyrene or polyacrylonitrile-butadiene-styrene. A pressure-sensitive construction consisting of a front layer and an adhesive layer, characterized in that the adhesive layer comprises an adhesive according to one of the claims 1 - 12. A pressure-sensitive construction according to claim 15, characterized in that the front layer comprises a thermoplastic polymeric material, optionally containing plasticizer. A pressure-sensitive construction according to claim 15 or 16, characterized in that the front layer consists of a mixture of polyvinyl chloride and chlorinated polyethylene. Claims for the following Contracting State : ES A method for preparing a pressure-sensitive adhesive comprising blending at least 5% by weight of an ethylene-vinyl acetate copolymer having a vinyl acetate content of more than 40% by weight, 5 to 50% by weight of at least one thermoplastic polymer which fulfills at least one of the following properties: i) the thermoplastic polymer forms a single phase with the ethylene-vinyl acetate copolymer, as indicated by the presence of a single glass-transition temperature, ii) the thermoplastic polymer can be dispersed in the ethylene-vinyl acetate phase to form individual polymer particles smaller than 100 µm, and iii) the thermoplastic polymer can be dispersed in the ethylene-vinyl acetate phase to form a continuous thermoplastic polymer phase in the ethylene-vinyl acetate phase, and optionally a plasticizer. A method according to claim 1, characterized in that the vinyl acetate content of the ethylene-vinyl acetate copolymer is at least 50% by weight. A method according to claim 2, characterized in that the vinyl acetate content of the ethylene-vinyl acetate copolymer is 60-80% by weight. A method according to one of the claims 1 - 3, characterized in that the pressure-sensitive adhesive further comprises a plasticizer in an amount of up to 50% by weight. A method according to claim 4, characterized in that the quantity of the plasticizer is 10 - 30% by weight. A method according to one of the claims 1 - 5, characterized in that the thermoplastic polymer is a) sufficiently polar to show compatibility with plasticizer and b) sufficiently compatible with the ethylene-vinyl acetate copolymer. A method according to claim 6, characterized in that the thermoplastic polymer is selected from the group consisting of cellulose esters, vinyl chloride polymers, acrylate modified styrene-acrylonitrile copolymers and mixtures thereof. A method according to claim 7, characterized in that the thermoplastic polymer is cellulose acetate butyrate or cellulose acetate propionate. A method according to claim 7, characterized in that the thermoplastic polymer is a copolymer of vinyl chloride and vinyl acetate. A method according to claim 7, characterized in that the thermoplastic polymer is a terpolymer of vinyl chloride, vinyl acetate and hydroxyethyl methacrylate. A method according to claim 7, characterized in that the thermoplastic polymer is a graft copolymer of ethylene-vinyl acetate onto polyvinyl chloride. A method according to any of claims 6-11, characterized in that the pressure-sensitive adhesive comprises 50-85% by weight of ethylene-vinyl acetate copolymer, 10-30% by weight of plasticizer and 5-20% by weight of the thermoplastic polymer. The use of a pressure-sensitive adhesive as specified in one of the claims 1 - 12 for permanently adhering a front layer to a substrate. The use according to claim 13, characterized in that the substrate comprises plasticized polyvinyl chloride, hard polyvinyl chloride, polymethylmethacrylate, polycarbonate, polystyrene or polyacrylonitrile-butadiene-styrene. A method for preparing a pressure-sensitive construction comprising combining a front layer and an adhesive layer, characterized in that the adhesive layer comprises an adhesive prepared according to one of the claims 1 - 12. A method according to claim 15, characterized in that the front layer comprises a thermoplastic polymeric material, optionally containing plasticizer. A method according to claim 15 or 16, characterized in that the front layer consists of a mixture of polyvinyl chloride and chlorinated polyethylene.

Inventors: HEEDERIK PETERJ, HUIZER LEO, VAN DER BENT HUIG, HEEDERIK, PETERJ., HUIZER, LEO, VAN DER BENT, HUIG
Applicants: AVERY DENNISON CORP, AVERY DENNISON CORPORATION
Application year: 1991
Main classification: C09J131
IPC codes: C09J7, B32B7, C08F210, C08K5, C08F218, C08L27, C08L31, C08L23, C09J123, C08F10, C09J131