Method of making polarization retaining fiber

Abstract: Disclosed is a method of making a polarization retaining single-mode optical fiber. Longitudinal grooves are formed on opposite sides of a cylindrically-shaped core preform having a glass core (11') surrounded by cladding glass (12'). The core preform is inserted into a glass tube, the tube is shrunk onto the core preform, and the interface between the core preform and the tube (27) is fused to form a solid preform having longitudinal apertures (14') on opposite sides of the core. An etchant gas is flowed through the apertures to enlarge the apertures into holes having a substantially round cross-section. Inserted into each aperture is a stress rod formed of glass having a coefficient of expansion different from that of the cladding glass. The resultant draw blank is drawn to form a single-mode optical fiber having a core that is subjected to a stress-induced birefringence.

Description: Background of the Invention This invention relates to the manufacture of polarization retaining single-mode optical fibers, and relates particularly to making preforms from which such fibers can be drawn. In many applications of single-mode optical fibers, eg. gyroscopes, sensors and the like, it is important that the propagating optical signal retain the polarization characteristics of the input light in the presence of external depolarizing perturbations. This requires the waveguide to have an azimuthal asymmetry of the refractive index profile. A stress birefringent optical fiber having extremely good polarization retaining characteristics is disclosed in U.S. patent No. 4,478,489. The refractive index asymmetry is obtained by introducing into the cladding region of the fiber on opposite sides of the core longitudinally extending regions of glass having a thermal coefficient of expansion (TCE) different from that of the cladding. Stress birefringent single-mode fibers have been fabricated by a multiple-rod-in-tube technique for several years. One of the disadvantages of this technique is the occurrence of seeds in the fiber due to the many surfaces in the preform from which the fiber is drawn. A further disadvantage is the long duration of the sealing technique that is required to prevent the low melting point stress rod material from flowing laterally between adjacent cladding rods to azimuthal regions of the fiber other than the stress rod regions. The sealing process involves traversing a flame along a rod-in-tube assembly two or three times, each traverse lasting 45 to 60 minutes. Even after subjecting the assembly to the sealing process, stress rod material sometimes leaks past adjacent cladding rods. The aforementioned lateral leakage problem can be avoided by the method disclosed in U.S. patent No. 4,561,871. Longitudinally extending holes are drilled on opposite sides of the core of a single-mode fiber preform. Stress rods are inserted into the holes, and the preform is drawn into a fiber. However, it has been very difficult to drill two holes that are parallel with the core and are not skewed. Also, the rough surfaces of the holes tend to cause seeds. The object of the invention is to provide an improved method of making cylindrical glass articles having at least one aperture parallel to the longitudinal axis. A preferred stress rod material comprises SiO 2 doped with an amount of B 2 O 3 to increase the TCE to a value sufficiently above that of the cladding glass. This dopant is advantageous in that its refractive index is lower than that of silica cladding glass; B 2 O 3 -containing stress rods can therefore be located relatively close to the fiber core. Although polarization retaining single-mode optical fibers have been made with stress rods formed of SiO 2 doped with less than 20 wt. % B 2 O 3 , the stress rods generally contain at least 20 wt. % B 2 O 3 to ensure good polarization retaining properties. Stress rods formed of SiO 2 doped with as little as 15 wt. % B 2 O 3 have a very low viscosity at fiber draw temperatures and would run from the bottom of the preform if they were not prevented from doing so. During the drawing process, the stress rod glass can also be squeezed upwardly from the top of the draw blank as the draw blank diameter is decreased in the root portion. This can alter the geometry of the core and/or the stress rods in the drawn fiber and can result in non-uniform stress on the core. A technique is needed for preventing the flow of stress rod glass from either end of the blank during the fiber drawing process. An object of a preferred embodiment of the invention is to provide a method of making a stress birefringent optical fiber containing stress rods of glass having very low viscosity at draw temperature. EP-A-0 372 450 teaches a method of making a polarization maintaining optical fiber by forming grooves on opposite sides of a core preform that includes a core region surrounded by cladding glass. stress rods are placed in the grooves, and thereafter, a glass tube is placed over that combination and fused at a temperature between 2000°C and 2200°C. At temperatures in that range, the stress rods flow and fill the grooves. Moreover, stress glass from the rods can flow into spaces between the core preform and the tube before the tube completely fuses to the core preform. In no step of EP-A-0 372 450 is there formed a glass rod having a longitudinal aperture that is parallel to its longitudinal axis. Summary of the Invention An object of another preferred embodiment of the invention is to provide a method of making polarization retaining single-mode optical fibers, which method overcomes the disadvantages of the prior art. Yet another object of a preferred embodiment of the invention is to provide a method of making polarization retaining single-mode optical fibers, which method is relatively simple to practice and can employ glasses which do not detrimentally affect light attenuation. The invention relates to a method of forming a cylindrical glass article. At least one longitudinal groove is formed along the outer surface of a cylindrically-shaped glass rod, the groove being parallel to the longitudinal axis of the rod. The rod is inserted into a glass tube. The combination of the grooved rod and tube is heated while a differential pressure is applied across the tube, whereby the pressure on the outer surface of the tube exceeds that on the inner surface thereof, thereby shrinking the tube onto the rod and fusing the interface between the rod and tube. The combination of the at least one longitudinal groove and the adjacent surface of the tube constitutes a longitudinal aperture that is parallel to the longitudinal axis of the rod. EP-A1-0 430 781 is published on 05.06.91 and thus falls within the terms of Article 54 (3) EPC. This document discloses a method of making cylindrical glass articles which is similar to the above method, in which however no differential pressure is applied across the tube during the heating step. In accordance with a preferred embodiment of the invention, the step of providing a glass rods comprises providing a cylindrically-shaped core preform having a glass core surrounded by cladding glass; the step of forming at least one longitudinal groove comprises forming longitudinal grooves on diametrically opposed sides of the core preform; and the steps of heating and applying a differential pressure results in the formation of an assembly having longitudinal apertures that are parallel to the core. A glass stress rod is inserted into each of the longitudinal apertures after the tube has been fused to the core preform, the stress rods having a coefficient of expansion different from that of the cladding glass. The resultant draw blank is drawn into an optical fiber. Brief Description of the Drawings Fig. 1 is a cross-sectional view of a grooved core preform. Fig. 2 is a schematic diagram illustrating the drawing of a rod from a grooved core preform. Fig. 3 illustrates the application of a coatings of glass particles to a glass tube. Fig. 4 is a cross-sectional view illustrating the consolidation and fusion of a first assembly. Fig. 5 is a cross-sectional view taken along lines 5-5 of Fig. 4. Fig. 6 illustrates the connection of a ball joint gas conducting handle to the collapsed preform resulting from the step illustrated in Fig. 4. Fig. 7 is a cross-sectional view of a preform resulting from the consolidation/fusion step illustrated in Fig. 4. Fig. 8 is a cross-sectional view illustrating the enlarged holes produced by the etching step to which the preform of Fig. 6 is subjected. Fig. 9 is a cross-sectional view illustrating the process of making a draw blank having contained stress rods. Fig. 10 is a cross-sectional view of a polarization retaining single-mode fiber produced by the present method. Figs. 11-13 illustrate various stress rod geometries. Fig. 14 is a cross-sectional view illustrating a modification of the process of Fig. 9. Fig. 15 is a cross-sectional view illustrating the application of first and second coatings of porous glass to a mandrel. Fig. 16 is a fragmentary cross-sectional view of a conventional flame hydrolysis burner. Description of the Preferred Embodiment It is to be noted that the drawings are illustrative and symbolic of the invention, and there is no intention to indicate scale or relative proportions of the elements shown therein. Referring to Fig. 1, there is initially provided a glass single-mode core preform 10, i.e. a preform in which the ratio of the diameter of core 11 to the diameter of cladding 12 is greater than that which is required to draw a single-mode fiber from the preform. In order to form a single-mode optical fiber from such a core preform, it is conventionally overclad with additional cladding glass to provide the desired ratio of core diameter to cladding diameter. Preform 10 can be made by any known technique such as modified chemical vapor deposition (MCVD), vapor axial deposition (VAD) and outside vapor deposition (OVD). Whereas core 11 is illustrated as having a circular cross-section, it could have a non-circular cross-section such as oblong. The refractive index profile of the core can be step-type, graded or the like. Longitudinally-extending grooves 14 are formed in cladding 12 on opposite sides of core 11 by means such as grinding, sawing or the like. If the diameter of the grooved core preform too large for subsequent processing, it is inserted into the apparatus of Fig. 2, a conventional draw furnace wherein its tip is heated by means 18. One end of silica rod 19 is fused to the lower end of the preform, and the other end of the rod is engaged by motor-driven tractor 20. A grooved rod 21 having a core 11', cladding 12' and longitudinal grooves 14' is drawn. An end 29 of cladding tube 27 is tapered as shown in Fig. 4, and a glass plug 30 is fused to the tapered end. Referring to Fig. 3, the ends of tube 27 are then mounted in a lathe where it is rotated and translated with respect to soot deposition means 25. Particles 26 of glass soot are deposited on tube 27 to build up coating 28. Soot 26 preferably has the same composition as tube 27, SiO 2 being a preferred composition for stress rod polarization retaining optical fibers. As shown in Fig. 4, a section 22 of the grooved rod 21 is inserted into the end of tube 27 opposite tapered end 29 until it contacts the tapered end, thereby forming assembly 32. End 34 of tube 27 is tapered and is then fused to handle 35. While assembly 32 is lowered into consolidation furnace muffle 31, a drying gas flows upwardly through the muffle (arrows 33). The drying gas conventionally comprises a mixture of chlorine and an inert gas such as helium. As soot coating 28 consolidates, it exerts a force radially inwardly on tube 27, thereby forcing that tube inwardly against section 22. A lower density soot will provide a greater force; however, the soot coating must be sufficiently dense to prevent cracking. As shown in Fig. 7, the resultant consolidated assembly 38 comprises core 11' surrounded by cladding 39. The original cladding region 12 and tube 27 are completely fused at dashed line 40. Porous glass coating 28 has become completely consolidated and fused to tube 27 as indicated by dashed line 41. Grooves 14' have become apertures 37 which are parallel to the longitudinal axis of assembly 38. After consolidation, the end of preform 32 containing tapered end 29 is severed to form planar endface 43 (Fig. 6). Tapered region 34 is severed from handle 35 and is fused to gas-conducting handle 44 to form preform 56. Handle 44 comprises glass tube 45 having a flared joint 48 at its upper end and an annular enlargement 49 spaced from the joint 48. Support tube 46 has a slotted handle formed in the end thereof. One side of end region 47 of tube 46 is removed to accept the upper end of handle 44, enlargement 49 resting on slotted base 50 as the adjacent section of tube 45 is inserted into slot 51. At the end of gas conducting tube 53 is a ball joint 52 which fits into cavity 54 of joint 48. Preform 56 is lowered into consolidation furnace muffle 31 while an etchant gas such as NF 3 , SF 6 or the like flows into the top of tube 27 from tube 53 (arrow 55) and through apertures 37, thereby etching the aperture walls in the heated region of the assembly. A preferred furnace is the scanning consolidation furnace disclosed in U.S. Patent No. 4,741,748 (Lane et al.). Such a furnace is capable of providing a sharp hot zone, and its temperature is readily adjustable. The etching process can be employed to merely smooth the aperture surfaces, or it can enlarge the apertures. The size of the hole formed by the etching process depends on temperature, etchant flow rate and rate at which the heating coil scans upwardly along the preform. Etching with NF 3 can result in the formation of a preform 56 having substantially round holes 58 (Fig. 8). Apertures 14' could also be enlarged by mounting the ends of consolidated assembly 38 in a lathe, passing the etchant gas through the apertures, and heating incremental regions of the assembly by traversing a flame along the surface thereof. To form a stress rod polarization retaining optical fiber from preform 56, glass rods having the required TCE are inserted into holes 58 and the resulting assembly is mounted in a draw furnace where it is drawn into a fiber. The TCE of the rods must be sufficiently different from that of cladding 39 to induce a predetermined azimuthal asymmetry of the refractive index profile in the resultant fiber. If cladding glass 39 is formed of SiO 2 , for example, rods 62 can be formed of SiO 3 doped with an oxide such as B 2 O 3 , Al 2 O 3 or the like which provides the resultant glass with a TCE greater than that of SiO 2 . As stated above, certain stress rod compositions, such as those containing at least 15 wt. % B 2 O 3 , provide good optical characteristics but have a very low viscosity at fiber draw temperatures. During the drawing process such stress rod glass can run from the bottom of the draw blank and can also be squeezed upwardly from the top of the draw blank if it is not prevented from doing so. In a preferred technique for containing the low viscosity stress rod glass within holes 58 during the drawing process, both ends of the borosilicate stress rods are fixed to the preform. If a high boron content stress rod were fused directly to the silica cladding portion of the preform, it would readily fracture when it cooled. Therefore, glass end rods having lower TCE than the stress rod are attached to the ends of the stress rod, and the end rods are fused to the preform. For example, if an end rod of silica doped with approximately 7 wt. % B 2 O 3 is fused to the silica preform, the combination will not fracture when it cools. However, a borosilicate end rod cannot be fused directly to the end of a high B 2 O 3 content stress rod if the B 2 O 3 contents of the two rods differ by more than about 10 WC. %, because of the expansion mismatch between the two rods. To alleviate this problem, glass rods having progressively lower TCE are attached to the stress rod. Thus, sections 63 and 64 of intermediate B 2 O 2 content are employed to connect end rods 65 and 66 to stress rods 62. For example, two stress rods 62 are cut to lengths required to form modified preform 61 of Fig. 9. Fused to opposite ends of each rod 62 are very short sections 63 and 64 of glass having a TCE lower than that of rods 62. Fused to sections 63 and 64 are short rods 65 and 66, respectively, of glass having a TCE between that of sections 63 and 64 and that of the cladding glass. If rods 62 of SiO 2 doped with 25 wt. % B 2 O 3 are to be fused to rods 65 and 66 of SiO 2 doped with 7 wt. % B 2 O 3 , sections 63 and 64 could be formed of SiO 2 doped with 15-17 wt. % B 2 O 3 . To attach sections 63 and 64 to rod 62, a rod of lower TCE glass having the same diameter as rod 62 is fused to the end of rod 62, and the attached rod is scored and broken to provide a section 63 or 64 of desired length. This process is repeated to attach rods 65 and 66. During this attachment process, any bulges are eliminated by heating and pulling to reduce the diameter to one that is equal to or smaller than that of rod 62. After sections 63, 64 and rods 65, 66 are attached, rods 62 are inserted into holes 58 until the ends of rods 65 are flush with endface 43'. Sections 63 and 64 can be a few millimeters in axial length. The combined lengths of rods 62 and 65 and sections 63 and 64 should be such that the interface between section 64 and rod 62 is located within cladding glass 39 just below endface 67. The interface between rods 66 and regions 64 is preferably located within hole 58 as shown. Rods 66 should extend a sufficient distance beyond endface 67 that tube 27 can be locally heated and readily deform inwardly and fuse to regions 68 of rods 66. Additionally, a flame is preferably directed onto the interface between rods 65 and endface 43' to prevent premature sagging of the stress rods beyond endface 43' in the draw furnace. The resultant assembly is then dried by placing it in an oven. Drying can be facilitated by attaching a hose to an end of the assembly and flowing a dry gas such as air, oxygen, nitrogen or the like through it. The resultant draw blank is inserted in a draw furnace, and a vacuum attachment is connected to handle 74. The end of the blank is then sealed; this can be accomplished by heating the end of the blank and dropping a gob therefrom. A vacuum is then applied to tube 34. The rods are fused to the cladding glass prior to the drawing operation. This can be accomplished by passing the draw blank rapidly down through the hot zone of a furnace heated to draw temperature and then rapidly bringing it rapidly back through the hot zone. The blank can be visually inspected, and the procedure can be repeated if inspection reveals incomplete fusion of the rods to the blank. In an alternative method the draw blank is lowered more slowly through a hot zone which is a few hundred degrees below draw temperature. For example, a high silica content draw blank could be inserted through a 1750°C furnace hot zone at a rate of 5 cm/min. During the fusing operation, rods 65 and at least a portion of rods 66 fuse to cladding glass 39, thereby preventing the escape of the low viscosity glass from the preform during the high temperature draw process. If necessary, the furnace temperature is raised to draw temperature, and optical fiber 77 of Fig. 10 is drawn. Draw temperature is typically about 2050-2150°C for high silica content draw blanks. Fiber 77 comprises core 78, cladding 79 and a stress rod 80 on opposite sides of core 78. The combined thicknesses of tube 27 and soot coating 28 are sufficient that, when combined with the thickness of preform cladding layer 12, the resultant optical fiber exhibits the desired single-mode properties. The thickness of cladding layer 12 is sufficient to locate apertures 14' the proper distance from core 11. This distance depends upon the composition and cross-sectional area of the stress rods. Instead of employing soot coating 28 to exert the necessary force to cause complete fusion of tube 27 to preform 10, a low level vacuum could be applied to tube 27 while the assembly of core preform 10 and tube 27 is gradually inserted into a furnace having a narrow hot zone. A vacuum attachment would be affixed to one end of the assembly, and the grooves could be sealed at the opposite end. Alternatively, the ends of tube 27 could be sealed in a chamber that applies pressure to the outside walls of the tube. As tube 27 is heated, the pressure collapses it onto preform 10. The previously described method whereby apertures 37 are enlarged and rounded is advantageous in that it permits the use of round stress rods 62. Processes such as the outside vapor phase oxidation process, which result in the formation of very pure glass rods, easily form round rods. Altering the shape of round rods to shapes such as square, U-shaped, V-shaped or the like, increases the expense of the rods and can result in surface defects that can cause seeds in the resultant fiber. However, fibers having non-circular stress rods can be formed by the present method. Preforms having non-circular holes are shown in Figs. 11, 12 and 13 wherein elements similar to those of Fig. 8 are represented by primed reference numerals. Holes 82 are formed by grinding U-shaped grooves in a core preform, inserting the preform into a tube, and then heating the assembly to collapse the tube and shrink it onto the preform. Holes 83 and 84 are similarly formed except that the core preform is initially provided with V-shaped and square grooves, respectively. If desired, the holes could be subjected to a mild etch to smooth the walls thereof. To form fibers from the preforms of Fig. 11, 12 and 13, rods having the same cross-sectional shape as the holes can be inserted into the holes, and the resultant assemblies can be drawn. Alternatively, circular rods of glass having a melting point much lower than that of cladding 39' can be employed. As the fiber is drawn, the ends of the rods that are in the hot zone melt and fill the holes. This technique is disadvantageous in that a very slow draw rate is required. Techniques other than those discussed in conjunction with Fig. 9 can be used to retain the high TCE, low melting point glass in the holes. In the embodiment of Fig. 14, elements similar to those of Fig. 9 are represented by primed reference numerals. Short rods of cladding glass composition are inserted into the longitudinal center of the preform shown in Fig. 8. A flame is directed onto the preform at the center of the rods, and the two ends are pulled in opposite directions to stretch and sever the preform into two modified preforms 61', one of which is shown in Fig. 14. Tapered end 69 contains plugs 70. If a tube 27 is attached to the preform, it is severed to form an endface 67' that extends across the entire end of the preform. Rods 62' of stress glass composition are inserted into holes 58' until they reach plugs 70. Rods 66', which are preferably formed of cladding glass, are then inserted. The endfaces of rods 66' are at or near endface 67'. At least one point 71 along the interface between each rod 66' and endface 67' is then fused to prevent longitudinal movement of rods 66'. A tapered end tube (see tube 27, 34 of Fig. 6) and evacuation handle (see handle 44) can then be attached to endface 67', and the resultant assembly can be dried and drawn into a fiber as described above. In yet another embodiment, the end of preform 56 (Fig. 8) is tapered by suspending it in a draw furnace until the bottom end sags and becomes detached. The end of the resultant tapered portion is broken off to form a small diameter end in which holes 58 are not quite closed. The tapered region 34 of tube 27 is severed to permit the insertion of the stress rods. The end of tube 27 is thereafter tapered inwardly so that a handle can be fused thereto. A hose can be connected to the tapered end so that dry gas can be flowed into the small diameter ends of holes 58 along the space between the holes and the stress rods to dry the assembly. A torch can then be directed at the tapered end to close the small diameter ends of the holes. Apparatus of the type shown in Fig. 15 can be employed to make the stress rods, special soot laydown and consolidation steps being required to make rods comprising SiO 2 doped with 15 wt. % or more B 2 O 3 . The large diameter end of a tapered mandrel is inserted into a glass tube 88, and the ends of the mandrel are mounted in a lathe where it is rotated and translated. Borosilicate glass compositions containing at least about 15 wt. % B 2 O 3 readily sinter during laydown. Therefore, burner traverse rate, burner-to-mandrel distance and flame gas flows must be such as to provide relatively cool laydown conditions which preclude sintering of the soot deposited by the burner. When conventional traverse speed (1.6 cm/sec) is used in both directions, ripples are produced. The burner should traverse the mandrel at a conventional rate in one direction, and its return speed should be much greater. Appropriate reactant vapors are fed to the burner at sufficient rates to generate soot having the desired concentrations of SiO 2 and B 2 O 3 . As described above, it is advantageous to initially produce soot doped with less B 2 O 3 than the concentration required for the stress rods. After a sufficiently thick graded expansion layer has been deposited, the B 2 O 3 can flow at a substantially constant rate throughout the remainder of the run. The high B 2 O 3 content outer layer will be located close to the core where it will have the greatest effect on birefringence. After the preform is removed from the lathe, the mandrel is removed, and a gas conducting handle is flameworked to the end of tube 88. The preform is then dried and consolidated. A suitable furnace is the aforementioned scanning consolidation furnace disclosed in U.S. Patent No. 4,741,748. A drying gas comprising helium and chlorine flows through the handle and into the preform aperture, and an inert muffle gas flows upwardly through the muffle. The preform is lowered into position in the muffle where it is consolidated by a moving hot zone. A thin layer of very high expansion material develops on the surface of the preform aperture during consolidation. If it were allowed to remain, the consolidated preform would fracture when removed from the consolidation furnace. This high expansion layer can be quickly removed by flowing NF 3 through the aperture while the preform remains in the furnace muffle which is still hot form the consolidation process. The preform is raised a sufficient distance to move the support handle from the heated region of the muffle, thereby preventing that handle from being damaged by the etching process. Because it is extremely reactive, NF 3 etches the entire length of the consolidated preform. The NF 3 etch leaves a relatively unpolished surface. Thus, after the aperture is enlarged and the deleterious high expansion material has been removed, the aperture surface is subjected to an etchant gas comprising SF 6 to provide a very smooth surface. To perform the SF 6 etch, the consolidated preform is lowered to the original consolidation position of the furnace, and a gas mixture comprising SF 6 is flowed through the aperture. During this SF 6 etch, a relatively low temperature hot zone (approximately 1040 o C has been found to be adequate) scans the preform. The hot zone temperature is sufficiently low that only a small amount of the SF 6 fractionates; this gas therefore removes very little material from the aperture surface. The SF 6 etch is not critical; a consolidated preform that has not been subjected to that etch can be removed from the consolidation furnace without fracturing. The consolidated preform is inserted into the draw apparatus of Fig. 2 where a vacuum connection is affixed to its upper end, and the bottom tip is heated. The lower end of the preform is pulled downwardly at a rate sufficient to form an elongated solid rod having a diameter just large enough to fit into holes 58. Examples 1 and 2, which are set forth below illustrate the manner in which the method of the present invention can be employed to produce polarization retaining single-mode optical fibers. Optical fiber core preforms for both examples were formed by a method similar to that disclosed in U.S. patent No. 4,486,212 which is incorporated herein by reference. Referring to Fig. 15, the large diameter end of an alumina mandrel 87 was inserted into glass tube 88 having protrusions 89. The outside diameter of the mandrel tapered from 5.5 mm to 6.5 mm over its 107 cm length. The ends of mandrel 87 were mounted in a lathe where it was rotated and translated. The face of burner 25, shown in greater detail in Fig. 16, was positioned 13.7 cm from mandrel 87. Orifice 94, centrally located in burner face 95, is surrounded by concentric rings of orifices 96, 97 and 98. Reactant compounds emanate from orifice 94 where they are heated by a flame produced by fuel gas and oxygen emanating from orifices 97. The reactant compounds oxidize in the flame to form glass particle stream 26 which is directed toward mandrel 87. An "inner shield" of oxygen emanates from orifices 96 to prevent the reaction of reactant compounds at the burner face. An "outer shield" stream of oxygen emanates from orifices 98. This burner design is somewhat similar to that disclosed in U.S. Patent No. 3,698,936 issued to H.J. Moltzan, the Moltzan patent differing in that it teaches an annular slot for providing the inner shield stream and in that it lacks the outer shield orifices. All of the orifices of burner 25 are supplied by manifolds in a manner similar to that taught in the Moltzan patent. The axes of orifices 96, 97 and 98 are slightly angled or focused so gases emanating therefrom are directed toward the reactant compounds emanating from orifice 94. Shield 99, which is spaced a short distance from face 95, protects the soot stream from ambient ambient air currents and improves laminar flow. Auxiliary burners 90 directed flames toward the ends of the porous glass preform during deposition. The use of auxiliary burners is taught in U.S. Patent No. 4,810,276. The system for delivering the gas-vapor mixture to the burner was similar to that disclosed in U.S. Patent No. 4,314,837. Liquid SiCl 4 was maintained at 79°C in a first container, and liquid GeCl 4 was maintained at 100 o C in second container, thus producing vapor at about 20 psi. During the deposition of coatings 91 and 92, vapors were metered from the first and second containers and were premixed oxygen before being supplied to burner orifice 94. The burner traversed a 49 cm section of mandrel in 25 seconds. An acetylene torch supported on the burner was first employed to deposit carbon particles on the mandrel during one burner pass to facilitate removal of the porous preform. A porous core preform 93 was then formed by traversing burner 25 along mandrel 87 for 400 minutes. Each coating was formed by traversing the mandrel many times with respect to burner 25 to cause a build-up of many layers of soot. The burner made additional passes in the vicinity of protrusions 89 in order to strengthen the bond between the tube and preform. Core region 92 was formed by depositing soot for 160 minutes. During this time, SiO 2 flowed to burner 25 at a rate of 4 slpm and GeO 2 flowed at a rate of 0.47 slpm. Coating 91 was formed by flowing only SiCl 4 to the burner at a rate of 4 slpm for the next 240 minutes. The preform was removed from the lathe, and the mandrel was removed through tube 88, thereby leaving a longitudinal aperture in the porous preform. Protrusions 89 caused tube 88 to adhere to the preform; that tube remained at one end of the preform to provide support for subsequent processing. The preform was then dried and consolidated in accordance with the teachings of U.S. Patent No. 4,125,388 (Powers 2A). A gas conducting handle was flameworked to the end of tube 88. A short length of capillary tube was inserted into bottom of the porous preform aperture. A drying gas consisting of 5 volume percent chlorine and 95 volume percent helium was flowed through the handle and tube 88 and into the preform aperture. A helium flushing gas flowed upwardly through the consolidation furnace muffle. The preform was gradually lowered into a consolidation furnace muffle, thereby forming a consolidated preform having a diameter of 52 mm and a core clad ratio of 0.4. The consolidated preform was inserted into the draw apparatus of Fig. 2 where its tip was heated to 1900°C while a vacuum connection was affixed to its upper end. After the end of preform 36 was stretched so that its aperture was either very narrow or completely closed, the aperture was evacuated. As the lower end of the preform was pulled downwardly at a rate of about 15 cm/min, and its diameter decreased, the evacuated aperture collapsed. The diameter of the resultant rod was 12 mm. A plurality of 90 cm sections were severed from the rod, and one of the sections was supported in a lathe where it functioned as a mandrel for the deposition of additional silica cladding soot. This outer cladding was formed by flowing SiCl 4 vapor to the burner at a rate of 2 slpm for 300 minutes. This overclad process continued until a coating of SiO 2 soot having an outside diameter of 70 mm was deposited to form a composite preform. The composite preform was consolidated at 1450 o while a mixture of 98.75 volume percent helium and 1.25 volume percent chlorine flowed upwardly through the muffle. The resultant consolidated core preform had a diameter of 38 mm. The resultant single-mode core preform 10 is shown in Fig 1. A grinding wheel was employed to form 1.3 cm wide by 6 mm deep longitudinally-extending grooves 14 in cladding 12 on opposite sides of core 11. The grooved core preform was inserted into the apparatus of Fig. 2 where its tip was heated to 1900°C. Grooved rod 21, having an outside diameter of 19.2 mm, was drawn from preform 10. Rod 21 was severed into 30 cm sections 22 which were cleaned with HF for 20 minutes and rinsed in deionized water. One end of a 100 cm long piece of silica cladding tube 27 having a 20 mm inside diameter and 25 mm outside diameter was tapered at end 29 (as shown in Fig. 4), and silica plug 30 was fused to the tapered end. The ends of the resultant structure were mounted in a lathe where it was rotated and translated with respect to flame hydrolysis burner 25 (Fig. 3). Particles 26 of SiO 2 soot entrained in the burner flame were deposited on tube 27 to build up a 1000 gram coating 28 having a length of 70 cm and a outside diameter of 70 mm. The grooved core preform 22 was inserted into the opposite end of tube 27 until it contacted the tapered end. About 40 cm of tube 27 extended beyond the grooved core section 22. End 34 of tube 27 was tapered and was then fused to handle 35. While assembly 32 was rotated at 1 rpm, it was lowered into consolidation furnace muffle 31 at a rate of 5 mm per minute. During consolidation, assembly 32 was subjected to a temperature of 1460°C, and a gas mixture comprising 400 cc chlorine and 20 lpm helium flowed upwardly through the muffle. Soot coating 28 consolidated; tube 27 was forced inwardly against section 22, and the contacting surfaces became fused. Planar endface 43 (Fig. 6) was formed by severing an end from the resultant consolidated preform. Tapered region 34 (Fig. 4) was severed from handle 35 and was fused to gas-conducting handle 44 of Fig. 6. Consolidated assembly 38 was lowered into consolidation furnace muffle 31 at a rate of 5 mm/min while NF 3 flowed into the top of tube 27 from tube 53 at a rate of 1 slpm. That region of assembly 38 that was located in the furnace hot zone was heated it to about 1200°C. This etching step resulted in a preform 56 having 12 mm diameter holes. This type of preform was employed in Examples 1 and 2. Example 1 Two 16 cm long stress rods 62 were severed from an elongated rod composed of SiO 2 doped with about 25 wt.% B 2 O 3 . Each rod was provided with a graded TCE extension as follows. Rods A and B were formed of SiO 2 doped with 15 wt. % B 2 O 3 and 7 wt. % B 2 O 3 , respectively. Rods A and B had the same diameter as the stress rods. Rod A was fused to the end of rod 62, and the attached rod was scored and broken to provide a section 63 that was 4 mm long. This process was repeated at the other end of rod 62 to form a similar section 64. Rod B was fused to section 63, and it was severed to form a rod 65 having a length of 3 cm. The process was repeated to attach a 6 cm long piece of rod B to section 64. Rods 62 were inserted into holes 58 until the ends of rods 65 were flush with endface 43'. A flame was directed onto opposite sides of tube 27, causing it to deform inwardly and fuse to regions 68 of rods 66. The resultant assembly was dried by placing it in a 240 °C oven for about 13 minutes. The resultant draw blank was inserted in a draw furnace, and a vacuum attachment was connected to its handle. The draw blank was moved downwardly at a rate of 30 cm/min through the 2050° hot zone to form a solid blank in which the stress rods were fused to the walls of holes 58. The draw blank was then rapidly brought back through the hot zone to the top of the muffle. This insertion step was repeated to ensure the formation of a solid blank that was substantially free from voids. While the furnace temperature remained at 2050 o C, a polarization retaining single-mode optical fiber was drawn. The resultant fiber had a core diameter of 5.8 µm and an outside diameter of 80 µm. The stress rod diameter was 22 µm, and the distance between each stress rod and core 68 was 2.9 µm. The attenuation of the fiber was 0.8 dB/km at 1550 nm. The beat length was 2.5 mm and the h parameter was equal to or less than 1 x 10 -5 . Example 2 A preform 56 was inserted into the draw apparatus of Fig. 2 where it was stretched to about twice its original length, whereby holes 58 were reduced in diameter to about 7.8 mm, and the preform diameter was reduced to about 25 mm. The tube at the end of the preform (see tube 27 of Fig. 6) was removed, whereby it had two planar endfaces. A 6 cm long silica rod was inserted into the longitudinal center of each hole. A flame was directed onto the preform at the center of the rods, and the two ends were pulled in opposite directions to stretch and sever the preform into two modified preforms 61' (see Fig. 14). Two 14 cm long stress glass rods were inserted into holes 58', and rods 66' were then inserted. The endfaces of rods 66' were flush with endface 67'. A flame was directed onto the interface between each rod 66' and endface 67' to tack the rod to the endface and prevent it from moving longitudinally. A tapered end tube and evacuation handle were attached to endface 67', and the resultant assembly was dried by placing it in a 250 o C oven for about 13 minutes. The resultant draw blank was inserted into a draw furnace, and a vacuum attachment was connected to its handle. The draw blank was moved downwardly at a rate of 5 cm/min through the 1750°C hot zone to form a solid blank in which the stress rods were fused to the walls of holes 58. The draw blank was then rapidly brought back through the hot zone to the top of the muffle. This insertion step was repeated to ensure the formation of a solid blank that was substantially free from voids. The furnace temperature was raised to 2150°C, and a 80 µm outside diameter polarization retaining single-mode optical fiber was drawn. This fiber exhibited attenuation and polarization characteristics similar to those of the fiber produced by Example 1.

Claims: A method of forming a cylindrical glass article comprising providing a cylindrically-shaped glass rod (10) having a longitudinal axis, forming along the outer surface of said cylindrically-shaped glass rod at least one longitudinal groove (14) that is parallel to said axis, inserting said rod into a glass tube (27), heating said rod with said at least one longitudinal groove surrounded by said tube, and simultaneously applying a differential pressure across said tube, whereby the pressure on the outer surface thereof exceeds that on the inner surface thereof, thereby shrinking said, tube onto said rod and fusing the interface between said rod and tube, the combination of said at least one longitudinal groove and the adjacent surface of said tube constituting a longitudinal aperture (14') that is parallel to the longitudinal axis of said rod. A method according to claim 1 wherein the step of providing a glass rod comprises providing a cylindrically-shaped core preform (10) having a glass core (11) surrounded by cladding glass (12), wherein the step of forming at least one longitudinal groove comprises forming longitudinal grooves (14) on diametrically opposed sides of said core preform, and wherein the steps of heating and applying a differential pressure results in the formation of an assembly (38) having longitudinal apertures (37) that are parallel to said core. A method according to claim 2 further comprising the steps of inserting a glass stress rod (62, 62') into each of said longitudinal apertures (58, 58') after said tube (27) has been fused to said core preform (10), said stress rods having a coefficient of expansion different from that of said cladding glass (12), and drawing the resultant draw blank (61, 60') into an optical fiber (77). A method according to claim 3 wherein, prior to drawing said fiber (77), said method comprises evacuating the space between said stress rods (62,62') and the surface of said cladding glass that forms said apertures (58,58'), and heating said draw blank (61,61') to fuse each of said stress rods to the surface of the aperture into which it has been inserted. A method according to claim 3 wherein the step of inserting comprises inserting into each aperture (58,58') a stress rod (62,62') that is shorter than said aperture, inserting into each aperture at each end of a stress rod a length of glass plug (65,66,66',70), and attaching said plugs to said draw blank (61,61') to prevent said stress rod from melting and flowing from said aperture during the step of drawing. A method according to claim 3 wherein the step of inserting comprises inserting into each aperture (58) a composite rod formed by attaching to each end of said stress rod (62) a glass plug (65,66), the thermal coefficient of expansion of which is intermediate that of said cladding glass (12) and said stress rod (62), inserting said composite rod into said aperture, the length of said stress rod being such that a portion of each of said plugs is within said aperture, and attaching said plugs to said draw blank (61) to prevent said stress rod from melting and flowing from said aperture during the step of drawing. A method according to claim 1 or 2 further comprising the step of enlarging the cross-sectional area of said apertures (37). A method according to any of claims 3-6 further comprising the step of enlarging the cross-sectional area of said apertures (37) prior to inserting said stress rods (62,62'). A method according to claim 7 or 8 wherein the step of enlarging comprises flowing an etchant through said apertures (37). A method according to claim 9 wherein the step of flowing comprises heating said tube and flowing a gas phase etchant through said apertures (37). A method according to claim 9 or 10 wherein the step of flowing is continued for a period of time sufficient to enlarge said apertures (37) and change the cross-sectional shape of said apertures to a substantially circular shape, the step of inserting comprising inserting round stress rods (62,62'). A method according to any of the preceding claims wherein the step of applying a differential pressure comprises depositing glass particles (28) on the outer surface of said tube (27), heating the assembly formed by inserting said core preform (10) into said tube (27) to consolidate said particles, the process of consolidating said particles exerting a force radially inwardly on said tube, causing said tube to shrink onto said core preform, the step of heating fusing said tube to said core preform.

Inventors: BERKEY GEORGE EDWARD, BHAGAVATULA VENKATA ADISESHAIA, HAWK ROBERT MARTIN, TARCZA STEVEN HOWARD, BERKEY, GEORGE EDWARD, BHAGAVATULA, VENKATA ADISESHAIAH, HAWK, ROBERT MARTIN, TARCZA, STEVEN HOWARD
Applicants: CORNING INC, CORNING INCORPORATED
Application year: 1991
Main classification: C03B37
IPC codes: G02B6, C03B37, C03C25, C03C15