Plastic vessel preform and a mold for molding a plastic vessel preform.

Abstract: A preform for molding a resin vessel and a mold for molding said preform, wherein said preform is provided with a mouth part (32) whose outer periphery is composed of an insert piece (20) made of resin excellent in resistance to heat, and a joint-reinforcing part (36) composed of resin to be used for injection molding of the preform proper (34) is formed integral with a support ring (28) of said insert piece (20), whereby excellent resistance to heat at the mouth part (32) and sufficient mechanical strength of said preform are possible; and said mold for molding the preform is provided with a screw-escape groove (12) in the mouth-forming part (10) thereof for preventing interference of the mold with the screw threads (22a) of said insert piece (20) to thereby simplify the molding device and the process.

Description: The invention relates to a plastic vessel preform according to the preamble of claim 1, and a mold for molding a plastic vessel preform according to the preamble of claim 10. Vessels molded from plastic materials such as polyethylene terephthalate (PET) and the like and each having a neck over which a screw cap can be mounted are currently used for soft drinks and other beverages. The soft drinks and particularly soft drinks with fruit juice contained therein are generally sterilized with high-temperature before they are charged into plastic vessels. Thus, the plastic vessels are required to have a sufficient heat resistance. Particularly, the non-stretched mouths of the plastic vessels must have a higher heat resistance such that any heat distortion will be prevented since the screw caps are to be fitted thereover. One of the plastic vessels having their mouths which fulfill the above requirement is proposed, for example, in Japanese Patent Publication No. Sho 61-35056. As shown in Fig.11, this technique provides a plastic vessel 1 which comprises a biaxially stretched vessel body 2 and neck portion 5. The neck portion 5 includes a thread 3 formed on the outer periphery thereof and a support ring 4. The heat resistance in the neck 5 is increased by once heating it up to a preselected temperature and then gradually cooling the neck to whiten and crystallize it. The plastic vessel 1 has an advantage that the neck portion 5 thereof is difficult to be distorted at raised temperatures and can maintain its dimensional accuracy at higher levels. However, such a prior art has a problem in that if the degree of crystallization at the neck portion 5 is to be sufficiently increased, a portion of the vessel body 2 adjacent the neck portion 5 can be undesirably crystallized since the neck portion 5 is continuously connected to the vessel body 2. In other words, a portion of the vessel body 2 adjacent to the neck portion 5 will be undesirably crystallized when the neck portion 5 is crystallized in the preform forming step. The crystallized portion of the vessel body 2 becomes difficult to be biaxially stretched in the subsequent step. If the neck portion 5 is crystallized in such a step that the plastic vessel 1 has been biaxially stretched and blow molded, even a portion of the shoulder or barrel of the vessel body 2 in addition to the neck portion 5 can be crystallized and whitened. Japanese Patent Publication No. Hei 2-5564 or the US 4,715,504 discloses a preform comprising an outwardly threaded insert piece made of a plastic material having an increased heat resistance and the neck and body portions of the preform other than the insert piece formed of another plastic material such as PET or the like. Such a preform is formed by first injection molding the insert piece from the increased heat resistant plastic material and then injection molding the PET material so that the insert piece will be embedded into the outer periphery of the neck portion. The preform formed by the use of such an insert piece can overcome the aforementioned problem associated with the undesirable crystallization of a portion of the vessel body when the whole neck portion is crystallized and increase the heat resistance of the neck portion to a practically satisfactory level. However, the use of the insert piece does not necessarily provide a sufficient bonding strength between the insert piece and the preform body. In the worst case, the insert piece may be partially separated from the vessel body due to load on fitting the screw cap. A preform having the pre-characterizing features is known from the EP-A-0 302 117. This known preform comprises a reinforcing portion of the preform body at the bottom of a support ring of the insert piece. Such an arrangement provides a reliable bonding between the insert piece and the preform body. However, due to the injection molding process of this preform undesired sharp edges may occur at the circumferential contact area between the insert piece and the preform body. A similar problem occures at the two-layered neck construction of the PET bottle disclosed in the EP-A-0 144 450. A mold according to the preamble of claim 10 is known from the US 4,715,504. An insert piece is hold in this known mold by applying a pressing force on the thread rings of the insert piece. However, this way of fixation could lead to a deformation of the threads. It is a first object of the invention to provide a preform of good quality to which an insert piece is firmly bonded. It is a second object of the invention to provide a mold by which a preform of good quality, particulary with a reliable thread portion, can be produced. The first object is solved by the characterizing features of claim 1, while the second object is solved by the characterizing features of claim 10. In accordance with the invention, a plastic vessel preform comprises a sleeve-like preform body, an insert piece having its properties different from those of said preform body and a neck portion including an outer layer formed with said insert piece and an inner layer at least partially formed of the same plastic material as that of said preform body, said insert piece including an outer and upper layer section having a thread portion on the outer periphery thereof and an outer and lower layer section located below said outer and upper layer section and having at least a support ring, said insert piece being formed of a crystallized plastic. In such an arrangement, since the insert piece required to have its dimensional stability on heating is formed of the crystallized plastic, the neck portion of the vessel very superior in heat resistance can be provided by the present invention. Even if a liquid is to be charged, at a raised temperature, into the plastic vessel through the neck portion thereof or even if the vessel itself and its contents are heated for sterilization, the neck of the plastic vessel can be prevented from being shrink distorted by heat. A perfect seal can be provided between the neck of the plastic vessel and the cap. The invention also provides a plastic vessel preform comprising a sleeve-like preform body, an insert piece having its properties different from those of said preform body and a neck portion including an outer layer formed with said insert piece and an inner layer at least partially formed of the same plastic material as that of said preform body, said insert piece including an outer and upper layer section having a thread portion on its outer periphery and an outer and lower layer section located below said outer and upper layer section and having a support ring, the support ring of said insert piece also including a bond reinforcing portion injection molded together with said preform body and extending in a direction perpendicular to the axis of said preform body. In such an arrangement, since the bond reinforcing portion is integrally formed in the support ring at the same time as the preform body and inner neck layer are injection molded, a contact area between the insert piece and the remaining plastic layers can be increased to improve the bond therebetween. Since the bond reinforcing portion extends in a direction perpendicular to the axis of the preform body, the bond in the insert piece can be improved not only in the axial direction but also in the radial direction of the preform body. More particularly, the insert piece can be more firmly bonded to the neck portion of the preform by bonding the inner wall of the insert piece with the inner plastic neck layer in the axial direction and also by bonding the support ring with the bond reinforcing portion in the radial direction. This results in epoch-making improvement with respect to buckling strength at the neck portion and also peel strength at the insert piece. The invention further provides a mold usable in forming a plastic vessel preform, said mold comprising a neck forming mold section, a cavity mold section and a core mold section, said neck forming mold further comprising an insert piece including an outer and upper layer having an outer thread on the outer periphery thereof and an outer and lower layer at least having a support ring and an engaged recess, said insert piece being held within said neck forming mold section when a preform is to be injection molded, the inner wall of said neck forming mold including a thread relief groove having a depth equal to or larger than the height of the outer thread in the insert piece and an engaging portion insertable into the engaged recess in the outer and lower layer of said insert piece, whereby said insert piece can be inserted into and held within said neck forming mold section in any circumferential direction. The thread relief groove in said neck forming mold section serves as means for avoiding any interference between the neck forming mold section and the outer thread. On setting said insert piece, thus, it can be properly positioned within the neck forming mold section in the circumferential direction of the insert piece without need of any positioning device and/or process. Furthermore, the neck forming mold section can reliably hold the insert piece at its outer and lower layer by causing said engaging portion to engage in the engaged recess of the insert piece. The invention is further described by way of preferred embodiments shown in the accompanying drawings. Fig. 1 is a fragmentary cross-section of the primary part of an embodiment of the mold according to the invention. Fig. 2 is a diagram illustrating a process of making a plastic vessel. Figs. 3A, 3B and 3C illustrate the eject and insert step in the process of Fig. 2. Fig. 4 is a schematic cross-sectional view illustrating the preform injection molding step. Fig. 5 is a fragmentary cross-section of the primary part of another embodiment according to the invention. Fig. 6 is a fragmentary cross-section of the primary part of a further embodiment according to the invention. Fig. 7 is a bottom view of the insert piece shown in Fig. 6. Fig. 8 is a diagrammatic view of a device for testing the strength of a neck portion in a preform which utilizes an insert piece having a support ring without any bond reinforcing section. Fig. 9 is a diagrammatic view similar to Fig. 8, the device being used to test the strength of a neck portion in a preform which has a support ring provided with a bond reinforcing portion. Fig. 10 is a fragmentary cross-section of the primary part of an embodiment of a preform according to the invention. Fig. 11 is an elevational side view of the outline of a plastic vessel constructed according to the prior art. Referring first to Fig. 1, there is shown a neck forming mold 10 which forms part of a preform forming mold according to the invention, and an insert piece 20 held within the neck forming mold 10. The insert piece 20 is in the form of a hollow sleeve which comprises an upper half forming an outer and upper layer section 22 with an outer thread section 22a formed therein at the outer periphery thereof and a lower half forming an outer and lower layer section 24 with locking and support rings 26, 28 formed therein. The wall thickness of the outer and upper layer section 22 is equal to that of the neck portion of a preform 30 to be formed. At this location, the preform 30 is a single-layer structure. On the other hand, the outer and lower layer section 24 is reduced in wall thickness to provide an internal diameter larger than that of the outer and upper layer section 22. The insert piece 20 must be formed of a plastic material having various properties such as heat resistance and others which are required by the neck portion of a plastic vessel. The heat resistance used herein is a property of a plastic material that it will not be distorted under the temperature of the contents in a plastic vessel to be formed, that is, the sterilizing temperature as ranged between 70° C and 95° C. Such a plastic material superior in heat resistance may be selected from a group consisting of polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polypropylene, polyamide, polyacrylonitrile, polyvinylidene chloride, nylon, polyethylene, polycarbonate and the like. Among them, any crystalline plastic material may be crystallized to improve its heat resistance. If the insert piece 20 is formed of a plastic material different from that of the preform body 34, the insert piece 20 may be formed of a blend of this different plastic material with that of the preform body. The insert piece may be formed with the same plastic material as the preform body, and then, be crystallized. When the insert piece and preform body are formed of the same plastic material, it provides advantages in that the bond between the insert piece 20 and the preform body 34 may be increased in strength and that the resulting vessel can be more easily recycled. The neck forming mold 10 functions to hold the insert piece 20 and is used to mold the neck portion 32 of the preform 30. The neck forming mold 10 is of a split sleeve-like member consisting of two or more sections which are movable in the radial direction by any drive means. The neck forming mold 10 includes a ring-like thread relief groove 12 formed therein for preventing any interference between a thread section 22a on the outer periphery of the outer and upper layer section 22 and the inner wall of the neck forming mold 10 when the insert piece 20 is mounted in the neck forming mold 10. The groove 12 extends along the inner circumference of the neck forming mold 10 opposed to the thread section 22a of the outer and upper layer section 22 and has a depth larger than the height of the thread section 22a. When the neck forming mold 10 is closed to hold the insert piece 20 therein, the insert piece 20 is not required to be subjected to any circumferentially positioning step. When the insert piece 20 is to be mounted in the neck forming mold 10, means for holding and moving the insert piece 20 is only required, leading to a simplification in the neck forming mold and process. The upward movement of the insert piece 20 relative to the neck forming mold 10 is restricted by the top face 22b of the insert piece 20 being engaged by the lower end of a first engaging section 14 in the neck forming mold 10. The elevational and transverse positioning operations of the insert piece 20 are accomplished by the engagement relationship between the locking and support rings 26, 28 of the insert piece 20, a second engaging section 16 of the neck forming mold 10 inserted between the rings 26 and 28, and a third engaging section 18 inserted below the support ring 28. Therefore, the insert piece 20 can be set within the neck forming mold 10 in a stable and accurate manner. A process of forming a plastic vessel preform which uses the insert piece 20 and the neck forming mold 10 will be described with reference to Figs. 2 through 4. Referring to Fig. 2, there is shown a cycle including all the steps of injection, stretch and blow molding a plastic vessel during one stage. The cycle includes an eject and insert step 140, a preform injection molding step 142, a temperature adjusting step 144 and a stretch and blow molding step 146. Figs. 3A, 3B and 3C illustrate the eject and insert step 140. In Fig. 3A, a finished plastic vessel 100 is ejected out of the neck forming mold 10 when the latter is opened, with the neck forming mold 10 also serving as means for carrying and holding the finished product. In Fig. 3B, the next insert piece 20 is being mounted into the neck forming mold 10. As described above, the insert piece 20 is previously injection molded from the aforementioned thermoplastic and heat-resistant plastic material. The insert piece 20 is moved to a position at which it is to be held in the neck forming mold 10 by the use of piece conveying means 52. As shown in Fig. 3C, the neck forming mold 10 is then closed so that the insert piece 20 will be reliably held in place under the aforementioned engagement relationship. Fig. 4 illustrates the preform injection molding step 142 in which the insert piece 20 is inserted into a cavity mold 60 while being held within the neck forming mold 10. A core mold 62 is also inserted into the cavity mold 60. Under such a situation, any suitable plastic material such as PET is injected into the cavity mold 60 through a gate 60a so as to form a preform 30 which is continuously connected with the insert piece 20. Thus, the preform 30 will be composed of the closed-end sleeve-like PET preform body 34 and the neck portion 32 in which the insert piece 20 is embedded. As best seen from Fig. 1, the upper half of the neck portion 32 is defined by the outer and upper layer section 22 of the insert piece 20 which is of a single-layer structure. The lower half of the neck portion 32 includes a double-layer structure which has an outer layer defined by the outer and lower layer section 24 of the insert piece 20 and an inner layer 32a formed of the same plastic material, PET, as used to form the preform body 34 of the preform 30. In this embodiment, the wall thickness of the outer and upper layer section 22 of the insert piece 20 is equal to that of the neck portion 32 of the preform 30. The upper half of the neck portion 32 is formed only by this outer and upper layer section 22. On injection molding of the preform, therefore, the flow of the molten plastic material will be stopped below the outer and upper layer section 22, that is, inside the outer and lower layer section 24. Thus, the molten plastic material will not flow inside the outer and upper layer section 22 during the injection molding process. Consequently, the outer and upper layer section 22 will not be distorted into the thread relief groove 12 under the pressure of the molten plastic material, with the dimensional accuracy of the outer and upper layer section 22 being not damaged. After the preform 30 has been injection molded, it is moved to the temperature adjusting step 144 while being held by the neck forming mold 10, as shown in Fig. 2. At the temperature adjusting step 144, the preform 30 is adjusted to a temperature suitable for stretching. Thereafter, the preform 30 will be stretch blow molded into a final product at the final step, that is, the stretch blowing step 146 by the use of the well-known technique. More particularly, the preform is biaxially stretched and blow molded into a vessel 100 within a blow cavity mold by axially moving a stretching rod and blowing pressurized air into the mold. Fig. 5 is a fragmentary cross-section of another embodiment of the invention, in which components substantially similar to those of the embodiment shown in Fig. 1 are denoted by similar reference numerals and will not be further described. The embodiment of Fig. 5 is similar to the firstly shown embodiment with respect to the structure holding the insert piece 20 relative to the neck forming mold 10, but different from the firstly shown embodiment in that the outer and upper layer section 22 of the insert piece 20 is reduced in wall-thickness except the top end thereof to provide a reduced wall-thickness equal to the wall-thickness of the outer and lower layer section 24. On injection molding a preform, the molten plastic material will flow not only inside the outer and lower layer section 24 but also inside the outer and upper layer section 22 except the top end thereof. In such a manner, the neck portion 32 of the preform 30 will have a double-layer structure including the insert piece 20 and an additional plastic layer 32a defining the preform body 34 inside the insert piece 20. In this embodiment, the thread relief groove 12 in the neck forming mold 10 has its depth L equal to the height of the thread portion 22a of the outer and upper layer section 22 in order to prevent any distortion in the outer and upper layer section 22 required to have a higher dimensional accuracy due to the pressure of the molten plastic material injected, associated with the fact that the molten plastic material flows inside the insert piece 20 except the top end thereof. In such a manner, the outer and upper layer section 22 will not be undesirably distorted even if any outwardly urging force due to the flow of the molten plastic material acts on the outer and upper layer section 22, since the outermost side of the thread portion 22a is placed into abutment with the bottom of the thread relief groove 12. Fig. 6 is a fragmentary cross-section of another embodiment of the invention while Fig. 7 is a bottom view of an insert piece used in this embodiment. In this embodiment, the insert piece 20 has its inner non-stepped wall such that the wall-thickness of the outer and upper layer section 22 is equal to that of the outer and lower layer section 24. On injection molding a preform, thus, the molten plastic material will enter inside the inner wall of the insert piece 20 from the top end to the bottom end thereof to provide a neck portion 32 which is of a double-layer structure consisting of the insert piece 20 and the inner layer 32a. This embodiment is characterized by that the bottom face of the support ring 28 includes a recess 40 formed therein to be communicate with the interior of the insert piece 20. The recess 40 is a ring-like configuration which is formed by the raised margin 28a of the support ring 28. The recess 40 includes a plurality of recessed engaging portions 42 (four in this embodiment) which are angularly disposed by 90 degrees, as shown in Fig. 7. When a preform is molded, the molten plastic material flows into both the recess 40 and recessed engaging portions 42. After solidified, the plastic material will form a bond reinforcing portion 36 integrally connected with the preform body 34 and support ring 28. This bond reinforcing portion 36 increases the contact area between the insert piece 20 and the preform body 34 so that they will be bonded to each other more firmly. Since the recess 40 extends in a direction perpendicular to the axis of the preform body 34, the bond reinforcing portion 36 will be formed to extend in the radial direction relative to the preform body 34. The bond between the insert piece 20, the preform body 34 and the inner layer 32a will be further increased in the axial and radial directions. It is preferred in the standpoint of aesthetics that the marginal section 28a of the support ring 28 is formed if the insert piece 20 is different in color from the preform body 34. The marginal section 28a serves to unify the neck portion 32 in color. In this embodiment, the insert piece 20 is wholly reduced in wall-thickness in comparison with those of the previous embodiments. If the wall-thickness of the insert piece 20 is too small, the insert piece 20 itself may be distorted by the pressurized plastic material on the injection molding process. The minimum wall-thickness of the insert piece 20 should be equal to 1.2 mm and preferably ranged between 1.3 mm and 1.5 mm. Preforms using insert pieces formed according to the embodiment shown in Fig. 6 and Fig. 7 were measured with their buckling load and peel strength. Fig. 8 illustrates a device for testing preforms having no bond reinforcing section in the support ring 28 while Fig. 9 illustrates a preform having a bond reinforcing portion 36 formed at the support ring 28, which is set in the testing device. (1) Object It is to verify how much the preform having the bond reinforcing section 36 at the support ring 28 is different from the preform having no bond reinforcing section with respect to the peel strength in the insert piece 20 and the buckling load in the neck portion 32. The peel strength of the insert piece 20 used herein means the magnitude of a load when the insert piece 20 begins to peel from the inner layer 32a. (2) Process The measuring system used was a compression testing machine "TCM 500" manufactured by SHINKO TSUSHIN KOGYO Company. This compression testing machine comprises a base 60 including a central hollow portion into which the preform body 34 is to be inserted, and a pressing portion 70. A preform to be measured is set in the central hollow portion of the base 60 with the support ring 28 thereof being placed on the end face of the base 60. The pressing portion 70 is placed on the top face of the neck portion 32. Measurements were carried out at room temperature or 90° C with the compression rate equal to 10 mm/minute. The neck portions 32 of the preforms measured had sizes a to f as follows: a : 24.94 mm b : 22.36 mm c : 22.52 mm d : 33.00 mm e : 5.03 mm f : 0.50 mm The preform bodies 34 of the preforms were formed of PET while the insert pieces 20 were made of polycarbonate. (3) Results a. The preform shown in Fig. 8 exhibited the following results when they were measured at room temperature. Peel Strength: 263 kg/cm 2 ; and Buckling Load: 468 kg/cm 2 . b. Results of the preform shown in Fig. 9 when it was measured at room temperature: Even when the preform was subjected to a load equal to 500 kg/cm 2 which was the maximum compressive force in the compression testing machine, no peeling and buckling were found in the insert piece. Although we did not find any accurate measurement, it is certain that the peel strength and buckling load exceed 500 kg/cm 2 . c. Results of the preform shown in Fig. 9 when it was measured at 90° C: The buckling load measured was equal to 280 kg/cm 2 and no peeling was found in the insert piece when the buckling created. From the above results, it will be apparent that the buckling strength in the neck portion can be greatly improved with the peel strength of the insert piece at room temperature by providing the bond reinforcing portion 36 in the support ring 28. Furthermore, the sufficiently large buckling strength will be provided even at raised temperatures while at the same time the bonding strength in the insert piece is very high. Fig. 10 is a fragmentary cross-section of a further embodiment of the invention. This embodiment is basically similar to the embodiment shown in Fig. 6 and Fig. 7, except that the insert piece 20 of this embodiment includes a top tapered end 50 formed therein. The top tapered end 50 is formed by a ring-like slope having its diameter which gradually linearly increases toward the top end. In order not to reduce the mechanical strength in the thread portion which is subjected to load when a cap is fitted over the neck portion, the top tapered end 50 is located above the top end of the thread portion 22a. The top tapered end 50 of the insert piece functions to facilitate the perfect ingress of the molten plastic material into the top end of the neck portion 32 when the preform body 34 is injection molded. This prevents any failure in molding. In another embodiment being basically similar to the embodiment shown in Fig. 10 the top tapered end 50 of the insert piece 20 is formed by an inwardly concave curve. The top tapered end having an inwardly concave curve provides a further improved anti-peel property in comparison with the top linearly tapered end 50 of the embodiment shown in Fig. 10 since the insert piece 20 can more effectively disperse forces when it is subjected to the top pressure for a capper. In the embodiment shown in Fig. 10, the raised margin section 28a of the support ring 28 extending along the circumference thereof tends to create a peel adjacent the corner thereof. Generally, the insert piece 20 may take various constructions and forms at least comprising the outer and upper layer section 22 having the thread portion 22a and the outer and lower layer section 24 mountable into the neck forming mold 10. The thread relief groove 12 in the neck forming mold 10 is not limited to a particular configuration unless it can receive the thread portion 22a. The necessary properties of the neck portion in the preform include not only the heat resistance but also the safeness, mechanical strength and so on. The insert piece may be formed of any suitable plastic material selected depending on these necessary properties. As it is apparent from the foregoing, the invention can provide a plastic vessel preform which includes an insert piece formed of a plastic material having an increased heat resistance and more firmly connected with the neck portion through an improved bonding strength, and a mold usable in molding such a preform.

Claims: A plastic vessel preform comprising: a sleeve-like preform body (34), an insert piece (20) having its properties different from those of said preform body (34), and a neck portion (32) including an outer layer formed by said insert piece (20) and an inner layer (32a) at least partially formed of the same plastic material as that of said preform body (34), said insert piece (20) including an outer and upper layer section (22) having a thread portion (22a) on its outer periphery, and an outer and lower layer section (24) located below said outer and upper layer section (22), said outer and lower layer section (24) includes at its bottom a support ring (28) extending in a direction perpendicular to the axis of said preform body (34), and a reinforcing portion (36) injection molded together with said preform body (34), at the bottom of said support ring (28), characterized therein said support ring (28) includes a recess (40) at its bottom face, said recess (40) is formed by a raised margin (28a) extending along the circumference of said supporting ring (28), and said reinforcing portion (36) is a plastic layer formed by charging plastic material into said recess, whereby said margin (28a) forming a peel adjacent to the corner of said support ring (28). A plastic vessel preform as defined in claim 1, wherein the surface of said recess (40) of said support ring (28) includes concave and/or convex portions (42) for reinforcing the bond between said insert piece (20) and said neck portion (32). A plastic vessel preform as defined in claim 1 or 2, wherein said neck portion (32) is of a double-layer structure consisting of an inner layer formed of the same plastic material as that of said preform body (34) and said insert piece (20), which structure extends along the axis of said neck portion (34) and wherein the top end of said insert piece (20) has its internal diameter gradually increasing in the upward direction. A plastic vessel preform as defined in claim 3, wherein the top end of the insert piece (20) has an inner tapered wall having a linearly variable diameter. A plastic vessel preform as defined in claim 3, wherein the top end of said insert piece (20) is formed by a curved face having an arcuated cross-section. A plastic vessel preform as defined in anyone of claims 1 to 5, wherein the plastic material forming said piece may be selected from a group consisting of polyethylene terephthalate , polybutylene terephthalate, polyethylene naphthalate, polypropylene, polyamide, polyacrylonitrile, polyvinylidene chloride, nylon, polyethylene, polycarbonate. A plastic vessel preform as defined in anyone of claims 1 to 6, wherein said insert piece (20) is crystallized. A plastic vessel preform as defined in anyone of claims 1 to 7, wherein said insert piece (20) is formed of a plastic material obtained by crystallizing the same plastic material as that of said preform body (34). A plastic vessel preform as defined in anyone of claims 1 to 8, wherein said insert piece (20) has its minimum wall-thickness at least equal to 1.2 mm. A mold for molding a plastic vessel preform (30) and integrally connecting with an insert piece (20) including at least a thread section (22a) on its outer periphery, said mold comprising a neck forming mold (10), a cavity mold section (60) and a core mold section (62), said neck forming mold (10) comprising an inner wall for holding said insert piece (20) at its outer periphery, characterized therein said neck forming mold (10) comprising a ring-like groove (12) extending along the inner circumference of said neck forming mold (10) opposed to said thread section (22a), said groove (12) having a depth equal to or larger than the height of the outer thread section (22a) for preventing any interference between said thread section (22a), and said neck forming mold (10) comprising an engaging portion (16) insertable into an engaging recess of said insert piece (20), whereby said insert piece (20) can be inserted into and hold within said neck forming mold (10) in any circumferential direction.

Inventors: AMARI FUMIYA, ORIMOTO HIROYUKI, AMARI, FUMIYA, ORIMOTO, HIROYUKI
Applicants: NISSEI ASB MACHINE CO LTD, NISSEI ASB MACHINE CO., LTD.
Application year: 1991
Main classification: B29B11
IPC codes: B29C49, B29B11, B29C45, B65D1