Preparation of poly(silylene)vinylenes from ethynylhydrido- silanes and their use

Abstract: Catalytic polymerization of dialkyl-,alkylaryl- or diaryldiethynylhydridosilanes cleanly affords soluble poly(silylene)vinylenes which can be shaped as fibers, films and bulk objects and thermally converted to silicon carbide.

Description: This invention relates generally to a route to organosilicon polymeric materials which can be converted to silicon carbide upon heating above 700°C. Silicon carbide is a compound shown by a chemical formula of SiC and is usually produced in block form by reactions of SiO₂ with C at high temperature of about 1,900°C-2,200°C. Its chemical inertness, extreme hardness and high temperature oxidative stability finds many uses such as in high temperature electrical heating units, furnace walls, mufflers, abrasives, rocket nozzles, automotive engine parts and turbine parts. In order to produce a silicon carbide molding having a particularly defined shape, the above described block is pulverized, and the resulting mixture is molded and then sintered. Of course, it has been impossible to produce SiC fiber from the above process. Organosilicon polymeric materials have been used as ceramic precursors to SiC fibers. Polysilanes, R. West, L.D. David, P.I. Djurovich and H. Yu, Am. Ceram. Soc. Bull. , 62 899 (1983) and polycarbosilanes, S. Yajima in Handbook of Composites ; Eds, W. Watt arid B.V. Perov; Elsevier, New York; Vol. 1, Ch. VI, pp. 201-37, 1985, are used for this purpose, but multistep preparation processes as well as removal of salts have made these routes lengthy and unattractive. It is a principal object of this invention, therefore, to provide an easy, efficient, clean and fast process for preparing a silylene vinylene polymer in high yield, which polymer can be used directly to form fibers. The silylene vinylene polymer prepared according to the process of the invention undergoes thermolysis to SiC and could be used for densification of silicon carbide bodies. This invention relates to a method of preparing polymeric poly(silylene)vinylene in a single step, one pot synthesis by catalytic self-hydrosilylation of ethynylhydridosilane. The compounds are prepared in high yield, yielding organosilicon polymeric materials which are white, soluble in organic solvents, and having a general average molecular weight of around 20,000. They can be melted reversibly and used to make silicon carbide fibers. According to the present invention there is provided a method of preparing polymeric poly(silylene)vinylene, comprising: polymerizing an ethynylhydridosilane of the formula: in the presence of a polymerizing effective amount of polymerization catalyst, wherein each of R and R' is C₁ to C₂₀ alkyl, C₆ to C₂₀ aryl, or C₇ to C₂₀ alkylaryl, to yield a poly(silylene)vinylene of the formula: wherein R and R' are as defined above and "n" is an integer of from 20 to 500. Also in accordance with the present invention there is provided the use of the poly(silylene)vinylene of the formula: wherein each of R and R' is C₁ to C₂₀ alkyl, C₆ to C₂₀ aryl, or C₇ to C₂₀ alkylaryl, and "n" is an integer of from 20 to 500, obtained according to the method of invention, for the preparation of silicon carbide upon heating the poly(silylene)vinylene above 700°C. V.V. Korshak, A.M. Sladkov and L.K. Luneva, Izv. Akad. Nauk SSSR , 12 2251 (1962) first reported preparing poly(silylene)vinylene in 1962. However, their polymer 1 was only slightly soluble in benzene. However, in 1965 L.K. Luneva, A.M. Sladkov and V.V. Korshak, Vysokomol. soyed. , 7 , 3 , 427 (1965) reported different physical properties for this polymer (brown, soluble in benzene, heptane, toluene) and the related copolymer, 2. In 1966 K.A. Andrianov, V.I. Pakhomov, V.M. Gel'perina and G.A. Semenova, Vysokomol. soyed. , 8 , 9 , 1623 (1966) reported making poly(silylene)vinylenes (psv) from a different route, namely a redistribution reaction. These polymers were not characterized. Thus, in both reported routes to psv's, high temperatures and long reaction times are required. The present invention provides a fast, high-yielding, catalytic route to psv's which requires no added heat, can be conducted with or without solvent, uses only a single bifunctional reagent and requires no product separation step as no by-products are produced. In the present invention the poly(silylene)vinylene polymers are prepared in an efficient route, using monomers with stoichiometrically fixed functionally, to give high molecular weight clean products in high yield, often as much as 90% or greater. Poly(silylene)vinylenes 2 are white and are fully characterized and can be pulled into fibers, cast into films and thermally converted into silicon carbide as revealed by X-ray analysis. Both the process of the present invention and the polymer prepared according to the process are illustrated by the above identified reaction equation. In the formula for the ethynylhydridosilane R and R′ may be the same or different. Generally speaking, they are organic moieties selected from the group consisting of C₁ to C₂₀ alkyl, C₆ to C₂₀ aryl, and C₇ to C₂₀ alkylaryl. Preferably R and R′ are selected from the group consisting of C₁ to C₅. The polymers generally have a molecular weight within the range of about 2,000 to about 120,000. The average molecular weight on a weight average basis is generally around 20,000. The number of recurring units in the polymer will vary, that is "n" may be from as little as 20 up to 500, but preferably will have an average chain length within the range of from about 200 to about 300 recurring units. Further details of the polymer, the polymer characterization and structure will be given in the examples. As illustrated in the above equation, it is preferred that the reaction be conducted in the presence of a catalyst, particularly a noble metal catalyst. Although any of the established hydrosilylation catalysts [e.g., (Ph₃P)₃RhCl, (PhCO)₂O, Ph₃P + Pd, Pd(PPh₃)₄, Ru₃(CO)₁₂] can be employed, most preferably the catalyst is a platinum catalyst and as illustrated in the equation, the most preferred catalyst is chloroplatinic acid. The amount of catalyst will vary within the range of catalytic amounts needed to successfully produce the polymer, but generally low amounts can be used, as low as .01% by weight of the monomer. Generally, the amount of catalyst should be within the range of from .005% by weight of the monomer up to as much as .1% by weight of the monomer. .01% has been found quite satisfactory to achieve up to as high as 90% or greater yields. The reaction may be run in the presence of a solvent or without a solvent. When solvents are employed the solvent may be any suitable inert organic solvent. Preferably the solvent is selected from tetrahydrofuran, diethyl ether, or an aliphatic or aromatic hydrocarbon, for instance benzene and hexane. The reaction is exothermic and it does not appear to be either time or temperature dependent. It can be run at room temperature, for as little as 30 minutes. The polymerization produces a precipitated white polymer, which can be easily separated and dried by conventional techniques. The polymers are converted to the ceramic, silicon carbide, upon heating up to as much as 700°C and the ceramic yields are uniformly high. Many of these polymers can be pulled into fibers. All can be cast into films. The following examples are offered to further illustrate but not limit the product and process of the present invention. Example 1 Polymerization of dimethylethynylsilane : To a dry, argon flushed, 50 mL, two-necked, round-bottomed flask (equipped with a magnetic stirrer and dry ice condenser) was added 0.001 gram of chloroplatinic acid H₂PtCl₆ (known as CPA), then capped with a rubber septum, 10 mL THF added, followed by covering with an argon atmosphere. To this solution was added 5 grams (0.06 mol) of dimethylethynylsilane in a dropwise fashion while stirring the mixture. Exothermic reaction was started after the initial induction period with some reflux. After magnetically stirring the solution at room temperature for 30 minutes, the polymerization was terminated by adding the reaction mixture to 150 mL of methanol. The white polymer which precipitated was separated by centrifugation and dried to a constant weight under vacuum over 24 hours. The polymer yield was about 90%. The above polymer was formed in 5 minutes without solvent. The resulting polymer had the following characterization: Weight average molecular weight, M w = 30,400 FTIR: 2937,2955 cm⁻¹/S C-H 1252 cm⁻¹/S Si-Me ¹H NMR: δ 0.1, 6.6 ppm broad ¹³C NMR: δ-3.4, 150 ppm ²⁹Si NMR: δ-15.37 ppm (All NMR spectra obtained in the liquid solution) Elemental analysis: % C % H Calc. 57.06 9.58 Exp. 56.95 9.32 Furthermore, this white polymer was found to be soluble in a variety of organic solvents and melts reversibly at ca. 105°C. As can be seen from the example illustrated, a simple one-step catalytic polymerization afforded the poly(silylene)vinylene in about 90% yield was formed in about five minutes without solvent being present. It can therefore be seen that the invention clearly accomplishes the objectives earlier enumerated.

Claims: A method of preparing polymeric poly(silylene)vinylene, comprising: polymerizing an ethynylhydridosilane of the formula: in the presence of a polymerizing effective amount of polymerization catalyst, wherein each of R and R' is C₁ to C₂₀ alkyl, C₆ to C₂₀ aryl, or C₇ to C₂₀ alkylaryl, to yield a poly(silylene)vinylene of the formula: wherein R and R' are as defined above and "n" is an integer of from 20 to 500. A method as claimed in claim 1, wherein R and R' are the same. A method as claimed in claim 1, wherein R and R' are different. A method as claimed in claim 1, 2 or 3, wherein the reaction is run in the presence of a suitable inert organic solvent. A method as claimed in claim 4, wherein the reaction solvent is an aliphatic or aromatic hydrocarbon. A method as claimed in claim 5, wherein the reaction solvent is tetrahydrofuran, diethylether, benzene or hexane. A method as claimed in any preceding claim, wherein the catalyst is a noble metal catalyst. A method as claimed in claim 7, wherein the catalyst is a platinum catalyst. The method as claimed in claim 8, wherein the catalyst is chloroplatinic acid. Use of the poly(silylene)vinylene of the formula: wherein each of R and R' is C₁ to C₂₀ alkyl, C₆ to C₂₀ aryl, or C₇ to C₂₀ alkylaryl, and "n" is an integer of from 20 to 500, obtained according to claims 1 to 9, for the preparation of silicon carbide upon heating the poly(silylene)vinylene above 700°C.

Inventors: BARTON THOMAS J, IJADI-MAGHSOODI SINA, BARTON, THOMAS J., IJADI-MAGHSOODI, SINA
Applicants: UNIV IOWA RES FOUND, IOWA STATE UNIVERSITY RESEARCH FOUNDATION, INC.
Application year: 1991
Main classification: C08G77
IPC codes: C01B31, C08G77, C04B35