X-ray transmitting window and method of mounting the same

Abstract: An X-ray transmitting window for use in X-ray lithography, for allowing transmission therethrough of X-rays from a vacuum ambience to a different ambience, is disclosed. The window includes an X-ray transmitting film; and a gasket material gas-tightly provided on at least one of opposite surfaces in a peripheral portion of the X-ray transmitting film, the gasket material having a Brinell hardness smaller than that of the X-ray transmitting film. The formed X-ray transmitting window is able to be sandwiched and fastened between a pair of flanges gas-tightly.

Description: This invention relates generally to X-ray lithography or other X-ray technology and, more particularly, to a method of mounting an X-ray transmitting window with an X-ray transmitting film, which serves as a vacuum partition wall, allowing transmission therethrough of X-rays from a vacuum ambience to a non-vacuum ambience. Figure 8 shows a known example of X-ray transmitting window, wherein an X-ray transmitting film 81 made from a beryllium sheet, for example, is gas-tightly fixed to a connecting member 82 which in turn is gas-tightly fixed to an inside cylindrical surface of a ring frame member 83. For the connection, silver brazing, electron beam welding, diffusion welding or the like is usable. This X-ray transmitting film 81 can serve as a vacuum partition wall, when fixed by bolts at bores 84 formed in the ring frame member 83. With this example, however, it is necessary to use a specific large ring frame member in addition to ordinary vacuum flange means, resulting in increased cost and heavy weight. On the other hand, in order to avoid oxidisation and resultant damage of an X-ray transmitting film, it is desirable to keep the X-ray transmitting film in a gas-tight casing. With the structure shown in Figure 8, however, because of the large size of the ring frame member, only a limited number of X-ray transmitting films can be accommodated in the case of a particular size. Further, in such case, there is a high possibility of breakage of the connection between the X-ray transmitting film and the connecting member or the connection between the connecting member and the ring frame member. This causes an inconvenience of small vacuum leakage or damage of the X-ray transmitting film. A method of monitoring an X-ray transmission film is described in Review of Scientific Instruments, Vol. 34, No. 12, December 1963, New York, U.S. Pages 1450 - 1451. R.A. Tobin: "Simple bakeable, thin vacuum window" in which a film with a copper gasket on one side only is mounted between flanges. Also in a method described in International Patent Application WO-A-8600752 a film is mounted between gasket rings located each side of the film and is supported by a ring support member held between flanges with other gasket rings each side of the support member. The problems discussed above have now been addressed. The method of mounting an X-ray transmission film in accordance with the present invention is defined in claim 1 of the claims appended. A particular feature of this method is that the gasket members each side of the X-ray transmission film are gas tightly fixed to the X-ray transmission film before being sandwiched and fastened between the pair of flanges. This assures a vacuum tight arrangement. In the present invention an X-ray transmitting window structure which is light in weight and small in size may thus be used, while nonetheless gas-tightness is positively assured. An X-ray transmitting window structure usable in the method of the present invention may be thinner and may have a higher X-ray transmissivity than used hitherto. On the other hand, since the X-ray transmitting window serves as a vacuum partition wall between a vacuum ambience and a different, non-vacuum ambience, there exists a pressure difference across the X-ray transmitting film. This applies a tensile stress to the X-ray transmitting film. If the tensile stress becomes larger than the breaking stress of the film, the film is broken. In this respect, the X-ray film should have a thickness sufficient for avoiding breakage by the pressure difference. Where a differential pressure p is applied to the opposite surfaces of a very thin film made of a material having a Young's modulus E and a large flexure is caused thereby, if the thickness of the film is h, then the tensile stress σ at the centre of the film of a circular shape is expressed as follows: σ = 0.29 (E·p²·S)/h² where S is the area of the film and S = πa² (wherein a is the radius). Also, the tensile stress at the centre of a film of a square shape is given by: σ = 0.25 (E·p²·S)/h² The tensile stress of the film at the centre of a film where it has an elliptical shape or a oblong shape, is slightly smaller than that of a circular or square film. From the above two equations, it is seen that a smaller tensile stress is attainable by increasing the film thickness. Also, it is attainable by reducing the area of the film. In consideration thereof, an X-ray transmitting film of an X-ray transmitting window for use in the present method should desirably have a size (area) small enough but sufficiently large for attaining the function as an X-ray transmitting window. With regard to the film thickness, the film should desirably be thinnest but of a thickness sufficient large to prevent overcoming of the tensile stress beyond the breaking stress. As an example, the present invention is suitably applicable to an X-ray transmitting window structure in an X-ray lithographic exposure apparatus. Such an X-ray exposure apparatus is suited for manufacture of integrated circuit devices of 64 megabit DRAMs having an expected chip size of 10 x 20 (mm²). Since an X-ray transmitting window is disposed closer to a light source side than a mask is and, generally, X-rays from the light source are divergent, there is a necessity that at the X-ray transmitting window position an X-ray transmission area slightly smaller than the area of 10 x 20 (mm²) is defined. Further, in future X-ray lithography for a 4 gigabit DRAM having an expected chip size of 30 x 60 (mm²), a required X-ray transmission area at the X-ray transmitting window position will be slightly smaller than the chip size. On the other hand, in X-ray lithography, there is a possibility that the X-ray transmitting film is scanningly moved along a one-dimensional direction, for effective expansion of the X-ray transmission area. In such case, in order to assure X-ray irradiation of the whole area of the chip size corresponding to the X-ray irradiation region, an X-ray transmitting window having an X-ray transmission area with a length at either side sufficiently covering only one of the longitudinal side and the transverse side of the chip size, may be prepared and such X-ray transmitting window may be scanningly moved along the longitudinal side or the transverse side by a distance corresponding to the length thereof. In such case by making the scanning distance shorter than the length of the one side of the chip size, it is possible to provide an X-ray transmitting window of increased strength. Since the one side of the chip size has a length in a range of 10 - 60 mm, the longitudinal length of the X-ray transmitting area should be not less than 10 mm. On the other hand, if the X-ray transmitting area has a size larger than required, the strength of the X-ray transmitting window decreases and, in this case, the thickness of the X-ray transmitting film may be made larger to assure a sufficient strength resistive to breakage. However, making the film thickness so large is not desirable. It is therefore preferable that the longitudinal length of the X-ray transmitting area is made not greater than 60 mm. Where an X-ray transmitting window is not scanningly moved, clearly it is necessary to define at the window position an X-ray transmitting area of a size allowing transmission of X-rays for exposure of the chip size. Thus, the longitudinal length should be in a range of 20 - 60 mm. In summary, it can be stated than an X-ray transmitting window should preferably have an X-ray transmitting area of a size ranging from 10 mm to 60 mm. In the X-ray transmitting window structure used in the method of the present invention, a pair of gasket members adjoining an X-ray transmitting film is sandwiched and fastened between a pair of flanges each having a Brinell hardness larger than that of the gasket members. Thus, when fastened between the flanges, there occurs plastic deformation of the gasket members, causing intimate contact of the gasket members with the flanges. Thus, high gas-tightness is ensured. Each flange may be provided with a seal edge (sealing projection) which bites into an opposed gasket member when the latter is sandwiched and fastened between the flanges. This effectively improves the sealing property. Further, where the material of the gasket members has a Brinell hardness smaller than that of the X-ray transmitting film, the fastening of the gasket members between the flanges with resultant deformation of the gasket members or with resultant biting of the seal edges of the flanges into the gasket members, does not cause deformation of the X-ray transmitting film itself which otherwise would result in damage to the strength thereof. These and other features and advantages of the present invention will become more apparent upon a consideration of the following description of the preferred embodiments of the present invention taken in conjunction with the accompanying drawings. In the drawings: Figure 1 is a sectional view of a first X-ray transmitting window structure, mounted in use; Figure 2 is a sectional view of the first window structure consisting of an X-ray transmitting film and a pair of gasket members; Figure 3 is a sectional view of a second X-ray transmitting window structure; Figure 4 is a sectional view of a third X-ray transmitting window structure, mounted in use; Figures 5A-5F are schematic views, respectively, showing examples of openings defined for X-ray transmitting windows; Figure 6 is a sectional view of a fourth X-ray transmitting window structure; Figure 7 is a sectional view of a fifth X-ray transmitting window structure, mounted in use; and Figure 8 is a sectional view of a known example of X-ray transmitting window structure. Preferred embodiments will be described below by way of particular example. The structure shown in figure 1 includes a window member 1 which comprises an X-ray transmitting film 2 and two ring-like outer frame members (gasket members) 3 gas-tightly adjoining to outer peripheral portions of the opposite surfaces of the film 2. The window member 1 is fastened between and fixedly supported by flanges 4 and 5 of tubular members which define an X-ray beam line for an X-ray exposure apparatus, for example. Each of the flanges 4 and 5 is made of a material having a Brinell hardness larger than that of the outer frame members 3. In the contact surfaces of these flanges which are opposed to each other so as to support the window member 1 therebetween, there are formed inside circumferential recesses 4A and 5A for receiving and abutting against portions of the outer frame members 3, respectively. Each recess 4A or 5A has a flat bottom surface extending from a central part of the flange to its inner peripheral edge. At the central part, there is formed a ring-like seal edge 4B (5B) projecting perpendicularly from the flat bottom surface and having a slant surface obliquely extending from the ridge of the projection toward the outer peripheral edge of the flange. The spacing between the opposed flat bottom surfaces of the recesses 4A and 5A as the flanges 4 and 5 are joined to each other, is set to be substantially equal to the thickness of the outer frame 3 portion of the window member 1. The outer peripheral edge of each recess 4A (5A) extends along the outer peripheral edge of the window member 1. In this window member 1, as best seen in Figure 2, the gaskets or outer frame members 3 of a suitable width and a suitable thickness are provided on the both side surfaces of the X-ray transmitting film 2, with the outer peripheral edge of each outer frame member being aligned with the outer peripheral edge of the film 2. In the X-ray transmitting window structure of this embodiment, the window member 1 is sandwiched between the flanges 4 and 5 and fastened therebetween by means of bolts 6 and 8 and nuts 7 and 9, while at the recesses 4A and 5A the seal edges 4B and 5B are press contacted to the outer frame members 3. Since the flanges 4 and 5 each is made of a material having a Brinell hardness larger than that of the outer frame members 3 adjoining to the X-ray transmitting film 2, each seal edge 4B or 5B formed on the flange 4 or 5 bites into corresponding one of the outer frame members 3 while causing plastic deformation thereof. This assures good gas-tightness at the X-ray transmitting window. Figure 3 shows another X-ray transmitting window member that can be used in the present invention. As shown in Figure 3, the window member 31 has an integral outer frame member (a unified pair of gasket members) 33 of a predetermined width, which is provided on an X-ray transmitting film 32 so as to wrap the outer peripheral edge portion of the film 32. The outer frame member has an outer diameter which is larger than that of the film 32, and the thickness of the circumferential outer frame 33 portion is constant. By fastening and fixing this window member 31 by using flanges such as at 4 and 5 shown in Figure 1, good gas-tightness is assured similarly. In the case of Figure 1, there is a possibility that the outer circumferential edge of the X-ray transmitting film 1 is continuously exposed to the atmosphere and, as a result, oxidization and consequent damage occurs at this portion. In the present case, as compared therewith, the outer frame member 33 is provided so as to wrap the peripheral edge portion of the X-ray transmitting film 32. Therefore, the film 32 can be protected against contact to the atmosphere and it is possible to avoid oxidization and resultant damage of the film 32. Here, typical materials usable as the X-ray transmitting film as well as their Brinell hardness are shown in Table 1, below. Also, typical materials usable as the outer frame member (gaskets) to be provided on the film as well as their Brinell hardness are shown in Table 2, below. Further, typical materials usable as the flange as well as their Brinell hardness are shown in Table 3, below. It is to be noted that the outer frame member should preferably be made of a material having a sufficiently small Brinell hardness as compared with that of the material used for the flange. Practical examples of the foregoing embodiment will be explained below. Example 1 First, an X-ray transmitting window structure which uses a window material 1 such as shown in Figure 2, will be explained. The X-ray transmitting film 2 was made from a beryllium film of a circular shape, having a thickness 60 µm and a diameter 82.4 mm. The flanges 4 and 5 each was made of stainless steel (SUS 316L). Each flange is of a known type which is available as Model ICF114 from ANELVA Corp., having a recess (4A or 4B) with a seal edge (4B or 5B) formed at an inside peripheral edge portion of a surface to be opposed to the other flange. In each outer peripheral edge portion of the opposite side surfaces of the X-ray transmitting film 2, electroplating by nickel to a thickness of 20 µm was made to a circumferential area of an inner diameter 63.7 mm and an outer diameter 82.4 mm, along the seal edge 4B or 5B of the flange 4 or 5. Additionally, electroplating by copper was made to the outside surfaces of that portion, to a thickness of 950 µm whereby the outer frame members 3 were formed. The outer frame members 3 and the X-ray transmitting film 2 of the thus formed window member 1 had their outer peripheral edges aligned with each other. The total thickness t of the outer frame member 3 portion, including the thickness of the X-ray transmitting film 2, was 2 mm. The thus formed window member 1 was sandwiched between the flanges 4 and 5, with the seal edges 4B and 5B engaging with the the outer frame members 3 at the opposite sides of the window member, and it was fastened by the bolts 6 and 7 and the nuts 7 and 9 with a screw torque of 120 Kg·cm, whereby a vacuum partition wall was provided. Since each outer frame member 3 provided on the X-ray transmitting film 2 had a surface layer of copper having a Brinell hardness (740 MPa (75 H B )) smaller than that stainless steel (1760 MPa (180 HB)), the seal edges 4B and 5B of the flanges 4 and 5 bit into the outer frame members 3 of the window member 1, with a result of plastic deformation of the outer frame members 3, whereby gas-tightness was assured. Across the obtained X-ray transmitting window, an ultra-high vacuum ambience (not higher than 1.3x10⁻⁶ Pa (1x10⁻⁸ Torr)) and a gas ambience filled with helium gas 20 KPa (150 Torr) were given, and vacuum leakage measurement was effected. The result is that no leakage was measured. Example 2 Next, an X-ray transmitting window structure using a window material 31 such as shown in Figure 3, will be explained. In this example, a circular X-ray transmitting film 32 was formed by a beryllium film of a thickness 20 microns and, to that film, the outer frame member (gasket) 33 was provided so as to wrap the outer peripheral edge portion of the film, whereby the window member 31 was formed. The outer frame member 33 was formed on the X-ray transmitting film 32 by aluminium deposition with uniform thickness, in a concentric ring area of an outer diameter 82.4 mm and an inner (opening) diameter 35 mm. The thickness was 2 mm. In this example, the X-ray transmitting film 32 may have any diameter provided that it is within the range of the outer frame member 33 and, if so, the outer peripheral edge portion of the X-ray transmitting film 32 can be wrapped by the outer frame member 33. In a similar manner as described, the window member 31 having the X-ray transmitting film 32 and the outer frame member 33 provided thereon was sandwiched between the flanges 4 and 5, with their seal edges 4B and 5B engaging with the outer frame member 33, and it was fastened by means of the bolts 6 and 8 and the nuts 7 and 9 with a screw torque 120 Kg·cm, whereby a vacuum partition wall was provided. The outer frame member was made of aluminium whose Brinell hardness 170 MPa (17H B ) was smaller than that of stainless steel (1760 MPa (180 H B )). Thus, the seal edges 4B and 5B of the flanges 4 and 5 bit into the opposite sides of the outer frame member 33 with plastic deformation thereof. Across the obtained X-ray transmitting window, an ultra-high vacuum ambience (not higher than 1.3x¹⁰⁻⁶Pa (1x10⁻⁸ Torr)) and a gas ambience filled with helium gas 20 KPa (150 Torr) were given, and vacuum leakage measurement was effected. The result is that no leakage was measured. Example 3 A third example will be explained with reference to Figure 4. In this example, like the window member 1 shown in Figure 2, a window member 41 has outer frame members 43 which are provided, with desired width and thickness, on both sides of an X-ray transmitting film 42, with the outer peripheral edges of them being aligned with the outer peripheral edge of the film 42. In this window member 41, an opening for transmission of X-rays therethrough which is defined by the provision of the outer frame members 43, is defined so as to have a size slightly larger than the area through which the X-rays should actually be passed. In this example, the length of each side of the opening is made larger by about 1 mm than the length of each side of the area through which the X-rays should actually be passed. This is determined in consideration of the fact that, at the position of the X-ray transmitting film 42, the X-rays are oscillated perpendicularly to the direction of X-ray projection in a range of several hundred µm. Like Example 1, a beryllium film was used as the X-ray transmitting film 42 and copper was used for the outer frame members 43. The opening had a size of 25 mm square which is slightly larger than the size of the area through which the X-rays should actually passed. Since the opening had a size of 25 mm square, it was possible that the beryllium film (X-ray transmitting film) 42 had a thickness of 15 µm. Like Example 1, the thus formed window member 41 was sandwiched between flanges 4 and 5 with their seal edges 4B and 5B engaging with the both sides of the outer frame members 43, and it was fastened to an X-ray exposure apparatus by means of bolts 6 and 8 and nuts 7 and 9, whereby a vacuum partition wall was provided. An X-ray exposure apparatus which utilizes synchrotron radiation as a light source, mainly uses a wavelength range of 0.7 - 1.0 nm. Investigation was made of the transmissivity to soft X-rays of 0.8 nm as an example, with regard to an X-ray transmission window using a beryllium film of a thickness 15 µm (Example 3) and an X-ray transmitting window using a beryllium film of a thickness 60 µm (Example 1). The result is that the beryllium film of 60 µm thickness showed a transmissivity of 17 %, but the beryllium film of 15 um thickness showed a higher transmissivity of 64 %. Since in the X-ray exposure apparatus the X-ray transmissivity, i.e., the intensity of transmitted X-rays, has a direct effect on the throughput of exposure process, the improvement in the transmissivity as described above essentially results in a significant increase in the throughput. While in Example 3 the opening as defined by the outer frame members has a square shape, any other shape may be used. Examples are illustrated in Figures 5A - 5F. Of these drawings, Figure 5A shows a square shape similar to Example 3. Figure 5B shows an oblong shape. Figures 5C and 5D show those shapes as formed by rounding the corners of a square shape and an oblong shape, respectively. Figures 5E and 5F show a circular shape and an elliptical shape, respectively. Other than those, a pentagonal shape or any other polygonal shape or a shape as can be defined by rounding such a polygonal shape, may be used. In Example 3, the outer frame members 43 adjoining the opposite sides of the X-ray transmitting film 42 have the same shape. However, this is not a necessary requirement. That is, as shown in Figure 6, a window member 61 may have an outer frame member 63 formed to adjoin the surface of an X-ray transmitting film 62 which is on the X-ray input side of the film, wherein this outer frame member defines an opening of a size slightly larger than the of the area through which the X-rays should actually be passed. Example 4 A fourth example will be explained with reference to Figure 7. In this example, like the window member 31 shown in Figure 3, an integral outer frame member 73 adjoins to an X-ray transmitting film 72 so as to wrap the outer peripheral edge portion of the film 72. Also, like the window member 41 shown in Figure 4, the opening to be defined for X-ray transmission has a size slightly larger than that of the area through which the X-rays should actually pass. In the window member 71 of this example, a beryllium film is used as the X-ray transmitting film 72, but its outer diameter is made smaller than the seal edge (ring) 4B or 5B formed on the flange 4 or 5. Thus, as the window member 71 is fastened and fixed between the flanges 4 and 5, the seal edges 4B and 5B bites into those portions of the outer frame member 73 whereat no X-ray transmitting film is embedded, as seen in Figure 7. Also in this example, the outer frame member 73 can be provided integrally to the X-ray transmitting film 72 by means of electroless plating, for example. Therefore, a sufficient strength as of an X-ray transmitting film resistive to breakage, is ensured and thus substantially the same advantageous effects as attainable with Examples 1 - 3 are assured. In the examples described hereinbefore, the X-ray transmitting film is provided by a beryllium film. However, in accordance with an X-ray wavelength range to be used, there is or are suitable materials to be used. Thus, depending on a wavelength to be used, a metal material such as silver, nickel, aluminium or the like, an insulative material or a semiconductive material such as silicon, carbon (diamond thin film), silicon nitride, silicon carbide and the like, may of course be used. In the foregoing examples, for a beryllium X-ray transmitting film, copper or aluminium is used as the material for forming the outer frame member (gasket). However, a material having a Brinell hardness not greater than 1180 MPa (120H B ), such as gold, for example, may be used as the outer frame member. Where silver is used as the material for the X-ray transmitting film, a material having a Brinell hardness not greater than 226 MPa (23 H B ) (e.g. aluminium) may preferably be used for the material of the outer frame member. Where nickel is used as the material for the X-ray transmitting film, a material having a Brinell hardness not greater than 1080 MPa (110 H B ) (e.g. aluminium, copper, gold) may preferably used for the material of the outer frame member. Where aluminium is used as the material for the X-ray transmitting film, a material having a Brinell hardness not greater than 170 MPa (17 HB) (e.g. aluminium) may be used for the material of the outer frame member. Where carbon, silicon nitride, silicon carbide or silicon is used as the material for the X-ray transmitting film, a material having a Brinell hardness not greater than 120 H B (e.g. aluminium, copper, gold) may preferably used for the material of the outer frame member. While the vacuum leakage measurements were made under the condition that one side of the X-ray transmitting window was filled with a helium gas of 20 KPa (150 Torr), if the thickness of the X-ray transmitting film is so selected as to sufficiently resist breakage of the film due to the pressure difference, an atmospheric pressure or a pressure higher than this may be set. Further, other than the helium gas ambience, an ambience of nitrogen gas, argon gas or atmospheric gas may be used provided that it does not damage the used X-ray transmitting film. Further, while in the foregoing examples the outer frame member is made by plating or deposition, the outer frame member may be made separately by using a material of copper, for example, and the formed outer frame member may be adhered to the X-ray transmitting film by silver brazing. Alternatively, it may be formed by fusing a material having a melting point lower than that of the used X-ray transmitting film material. While the invention has been described with reference to the structures disclosed herein, it is not confined to the details set forth and this application is intended to cover such modifications or changes as may come within the scope of the following claims.

Claims: A method of mounting an X-ray transmission film functioning as a vacuum partition wall for allowing transmission therethrough from a vacuum ambience to a different ambience, wherein said method comprises providing the X-ray transmission film (2;32;42;62;72), providing a pair of gasket members (3;33;43;63;73) on outer peripheral edge portions of opposite sides of the X-ray transmission film (2;32;42;62;72), and sandwiching and fastening the gasket members (3;33;43;63;73) by a pair of flanges (4,5), and wherein the gasket members (3;33;43;63;73) have a Brinell hardness smaller than that of the flanges (4,5), characterised in that: before sandwiching and fastening the gasket members (3;33;43;63;73), the gasket members (3;33;43;63;73) and the X-ray transmission film (2;32;42;62;72) are gas-tightly fixed to each other into an integral structure, and that the sandwiching and fastening of the gasket members (3;32;42;62;72)are made from opposite sides of the paired gasket members (3;32;42;62;72) having been fixed to the opposite sides of the X-ray transmission film (2;32;42;62;72). A method according to claim 1, wherein the pair of flanges (4,5) have opposed surfaces each having an inside circumferential recess (4A,5A) for receiving the X-ray transmission film (2;32;42;62;72), wherein each recess (4A,5A) has a flat bottom surface extending from a central part to an inside circumferential edge of corresponding one of the opposed surfaces, and wherein each recess (4A,5A) is formed with a seal edge (4B,5B) at a central part thereof which seal edge (4B,5B) is defined by a circumferential projection projecting perpendicularly from the flat bottom surface and having a slant surface inclined from a ridge of said projection toward an outside circumferential edge of the recess (4A,5A). A method according to claim 1 or 2, wherein the Brinell hardness of the gasket members (3;33;43;63;73) is smaller than that of the X-ray transmission film (2;32;42;62;72). A method according to any one of claims 1 to 3, wherein a total thickness of an outside circumferential edge portion of the X-ray transmission film (2;32;42;62;72) and the pair of gasket members (3;33;43;63;73) adjoining thereto is in a range of 0.2 - 10 mm before sandwiched. A method according to any one of claims 1 to 4, wherein a portion of the surface of the X-ray transmission film (2;32;42;62;72) not covered by the gasket members (3;33;43;63;73) has one of a rectangular shape, a pentagonal shape, a polygonal shape, a shape without corner, a circular shape and an elliptical shape, and wherein the portion not covered by the gasket members (3;33;43;63;73) has a longitudinal size in a range of 10-60 mm. A method according to any one of claims 1 to 5, wherein the X-ray transmission film (2;32;42;62;72) is usable in supply of X-rays for X-ray lithography. A method according to any one of claims 1 to 6, wherein said pair of gasket members (33;73) extend beyond the periphery of said X-ray transmission film (32,72) and constitute a single body (33;73).

Inventors: AMEMIYA MITSUAKI, EBINUMA RYUICHI, FUKUDA YASUAKI, MIZUSAWA NOBUTOSHI, UZAWA SHUNICHI, WATANABE YUTAKA, AMEMIYA, MITSUAKI, EBINUMA, RYUICHI, FUKUDA, YASUAKI, MIZUSAWA, NOBUTOSHI, UZAWA, SHUNICHI
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1991
Main classification: H01J35
IPC codes: H01J35, G21K5