Process for producing polyoxymethylene copolymer

Abstract: The process comprises copolymerizing a mixture of a cyclic oligomer of formaldehyde or a cyclic acetal as the principal monomer with a comonomer copolymerizable therewith, in the presence of a perfluoroalkylsulfonic acid or a perfluoroalkylsulfonic acid derivative as the polymerization catalyst in an amount of 1x10⁻⁶- 2x10⁻⁵% by mole relative to the principal monomer. The content of water and formic acid in the monomer mixture are, respectively, not more than 40 ppm by weight. The polymerization catalyst in the resulting copoloymer is deactivated by adding and melt-blending at least one ion adsorbent selected from (a) ion adsorbents comprising as the main components at least two kinds of oxides selected from alkali metal oxides, alkaline earth metal oxides, and oxides of trivalent and tetravalent elements, or (b) ion adsorbents represented by the formula M1 1-x M2 x (OH)₂A n- x/n ·mH₂0 wherein M1 denotes at least one divalent metal selected from alkaline earth metals, M2 denotes a trivalent metal, A n- denotes an n-valent anion, x satisfies 0< x ≦ 0.5, and m is a positive number, in an amount of 0.001-0.5% by weight relative to the polymer to obtain the polyoxymethylene copolymer composition.

Description: TECHNICAL FIELD The present invention relates to a process for producing a polyoxymethylene copolymer. BACKGROUND ART Polyoxymethylenes synthesized by prior art techniques are classified broadly into homopolymers and copolymers. Polyoxymethylene homopolymers and polyoxymethylene copolymers of the prior art respectively have only one of the two desirable characteristics, namely either excellent mechanical property or excellent stability. That is, polyoxymethylene homopolymers obtained by homopolymerization of formaldehyde or trioxane are excellent in mechanical properties but are not satisfactory in stability; on the other hand, polyoxymethylene copolymers obtained by copolymerization of formaldehyde or trioxane with a cyclic ether or cyclic formal are excellent in stability but are poor in mechanical properties. With respect to long term resistance to heat or resistance to hot water, furthermore, even polyoxymethylene copolymers are not satisfactory. Polyoxymethylene copolymers are usually obtained by copolymerizing formaldehyde or trioxane with a cyclic ether. U.S.P. No. 3,027,352 describes a copolymer obtained by cationically copolymerizing trioxane with ethylene oxide or 1,4-dioxolane. Further, U.S.P. No. 3,337,503 discloses the use of methylal as a molecular weight controlling agent in the polymerization of trioxane. When methylal is used as the molecular weight controlling agent, the terminal group of the resulting polymer becomes the methoxy group. In the polymerization of formaldehyde or trioxane or the copolymerization thereof with a comonomer using cationic catalyst, hydride shift (i.e., hydrogen abstraction) takes place, which results in scission of the main chain of the polymer and makes it impossible to obtain a high molecular weight polymer. Moreover, it is known that the terminals formed by the scission become the methoxy group and the formate group. Further, when compounds having hydroxyl groups, such as water, methanol, formic acid, etc., are present in polymerization, they function as a chain transfer agent and form unstable terminal structures. A usually adopted remedial method is to decompose these unstable structures and stabilize the terminal groups as hydroxyethoxy groups, by application of post-treatment after polymerization. In the case of formic acid, however, terminal formate groups are formed simultaneously. As described above, in the previous polyoxymethylene copolymers, terminal formate groups are formed during polymerization by chain transfer reaction caused by formic acid, which is an impurity in trioxane, and by hydride shift reaction, which is a side reaction caused by cationic catalyst, so that it has been difficult to reduce terminal formate groups. The present inventors have found that by restricting to a certain range the amount of inserted oxyalkylene units in polyoxymethylene copolymer and the amount of terminal formate groups in the copolymer, a polyoxymethylene copolymer can be obtained which has highly excellent stability and mechanical property and excellent long term resistance to heat and resistance to hot water. Based on this finding, European Patent Application 91902766.4 , based on part of the disclosure of EP-A-0 504 405 , relates to a polyoxymethylene copolymer having a molecular weight of 10,000 - 200,000 which comprises oxymethylene units (-CH 2 O) and oxyalkylene units wherein R and R 0 may be the same or different and are each selected from hydrogen, an alkyl group or an aryl group, n is 1 to 5, and m is 2 to 6, and wherein (a) the proportion of oxyalkylene units to oxymethylene units is 0.07 - 0.5% by mole, and (b) in the infrared spectrophotometry of the polymer, the ratio of absorbance of terminal formate groups to methylene groups is not more than 0.025, (c) the terminal groups are hydroxyalkoxy, alkoxy or formate. The polyoxymethylene copolymer can be obtained by copolymerization, using a cationic catalyst, formaldehyde or trioxane and a cyclic ether or cyclic formal. The copolymer can also be obtained by reacting polyacetal homopolymer and a cyclic ether or cyclic formal mentioned above in the presence of a cationic catalyst Further information can be obtained from EP-A-0 504 405 . The amount of formate terminal groups in the copolymer can be determined by infrared spectrophotometry of the film obtained by hot pressing of the polymer. The absorption wave number (v) due to terminal formate is 1710 cm -1 and that due to the methylene group of polyoxymethylene main chain is 1470 cm -1 . The amount of terminal formate groups in the copolymer can be expressed by the ratio of these absorbances, D 1710 /D 1470 . The amount of formate groups in the copolymer of Application 91902766.4 is desired to be not more than 0.025, preferably not more than 0.020, in terms of D 1710 /D 1470 . When D 1710 /D 1470 is higher than the value, the stability, heat resistance and hot water resistance of the copolymer are deteriorated. SUMMARY OF THE INVENTION The present invention is divided out of the disclosure of EP-A- 0 504 405 . The present invention provides a process for producing a polyoxymethylene copolymer which comprises copolymerizing a mixture of a cyclic oligomer of formaldehyde or a cyclic acetal as the principal monomer and a comonomer which is a cyclic ether represented by the formula wherein R and R 0 may be the same or different and are each selected from hydrogen, an alkyl group and an aryl group, R bound to different carbon atoms and R 0 bound to different carbon atoms may respectively be the same or different and are selected from hydrogen, an alkyl group and an aryl group, and m is 2 to 6; or a cyclic formal represented by the formula wherein R and R 0 may be the same or different and are each selected from hydrogen, an alkyl group and an aryl group, R bound to different carbon atoms and R 0 bound to different carbon atoms may respectively be the same or different and are selected from hydrogen, an alkyl group and an aryl group, and m is 2 to 6; in the presence of a perfluoroalkylsulfonic acid or a perfluoroalkylsulfonic acid derivative as the polymerization catalyst in an amount of 5 x 10 -6 to 2 x 10 -5 % by mole relative to the principal monomer to obtain a copolymer which contains 0.07% - 0.5% by mole of polyoxyalkylene units in proportion to polyoxymethylene units, and wherein the content of water and formic acid in the monomer mixture are, respectively, not more than 40 ppm by weight. The process of the present invention may further comprise deactivating the polymerization catalyst in the resulting polyoxymethylene copolymer, by adding and melt-blending at least one ion adsorbent selected from (a) ion adsorbents comprising as the main components at least two kinds of oxides selected from alkali metal oxides, alkaline earth metal oxides, and oxides of trivalent and tetravalent elements, or (b) ion adsorbents represented by the formula M1 1-x M2 x (OH) 2 A n- x/n .mH 2 O wherein M1 denotes at least one divalent metal selected from alkaline earth metals, M2 denotes a trivalent metal, A n- denotes an n-valent anion, x satisfies 0 < x ≤ 0.5, and m is a positive number, in an amount of 0.001 -0.5% by weight relative to the polymer to obtain the polyoxymethylene copolymer composition. As the example of the cyclic ethers used, mention may be made of ethylene oxide, propylene oxide, butylene oxide, and styrene oxide. As the example of the cyclic formals, there may be mentioned ethylene glycol formal (1,3-dioxolane), diethylene glycol formal, 1,3-propanediol formal, 1,4-butanediol formal, 1,5-pentanediol formal, and 1.6-hexanediol formal. Particularly preferred comonomers are such-cyclic formals as ethylene glycol formal (1,3-doxolane), and 1,4-butanediol formal. As specific examples of suitable catalysts, mention may be made of trifluoromethanesulfonic acid, pentafluoroethanesulfonic acid, heptafluoropropanesulfonic acid, nonafluorobutanesulfonic acid, undecafluoropentanesulfonic acid, and perfluoroheptanesulfonic acid. Suitable derivatives include super-strong acid anhydrides such as trifluoromethanesulfonic acid anhydride, pentafluoroethanesulfonic acid anhydride, heptafluoropropanesulfonic acid anhydride, nonafluorobutane sulfonic acid anhydride, undecafluoropentanesulfonic acid anhydride, and perfluoroheptanesulfonic acid anhydride; alkyl esters of superstrong acids such as methyl trifluoromethanesulfonate, ethyl trifluoromethanesulfonate, ethyl pentafluoroethanesulfonate, methyl pentafluoroethanesulfonate, and methyl heptaflucropropanesulfonate ; and alkylsilyl esters of super-strong acids such as trimethylsilyl trifluoromethanesulfonate, and triethylsilyl trifluoromethanesulfonate. Catalysts conventionally used in polymerization or copolymerization of trioxane are Lewis acids, such as boron trifluoride, tin tetrachloride, titanium tetrachloride, phosphorus pentafluoride, and phosphorus pentachloride, and the compounds or the salts thereof. When these catalysts are used, however, hydride shift, which is a side reaction in polymerization, occurs to a large extent, and the amount of terminal formate groups in the resulting copolymer can satisfy the condition of D 1710 /D 1470 being not more than 0.025 with much difficulty. Further, these catalysts are insufficient in polymerization activity and cannot achieve a satisfactory polymerization unless the catalysts are used in a high concentration, Consequently, the resulting polymer contains a high concentration of residual catalyst and hence has a low heat stability. Therefore, a complicated process becomes necessary including the washing and removal of the catalyst after polymerization. The concentration of the catalyst in the present invention should be in the range from 5 X 10 -6 to 2 x 10 -5 % by mole relative to the principal monomer. At concentrations lower than said range, no polymerization takes place. At concentrations higher than the range, the catalyst remaining in the polymer will cause depolymerization, which results in low heat stability of the polymer. Thus, the present inventors have found that when perfluoroalkylsulfonic acids or their derivatives are used as the catalyst, hydride shift, which is a side reaction in polymerization, can be suppressed and a polyoxymethylene copolymer which satisfies the condition of D 1710 /D 1470 being not more than 0.025 can be obtained. Furthermore, the present inventors have found that when perfluoroalkylsulfonic acids or their derivatives are used as the catalyst, the amounts of water and formic acid contained in the monomer greatly affect the polymerization activity of the catalyst That is, in the present invention, the concentrations of water and formic acid in the monomer must respectively be not more than 40 ppm. When the concentrations are higher than 40 ppm, the polymerization activity lowers markedly. When the catalyst concentration is in the range from 1 x 10 -6 to 2 x 10 -5 % by mole relative to the principal monomer, polymerization does not start at all, or gives a very low polymerization yield, which is unpractical. Molecular weight controlling agents preferably used in the polymerization are alcohols and ethers. Particularly preferred are alkyl ethers, such as methylal. Water, formic acid, and methyl formate, also act as a molecular weight controlling agent besides those mentioned above. In the present invention, however, particularly water and formic acid cannot be used because of their effect on catalyst activity described above. Methyl formate also is unpreferable since it forms terminal formate groups. Therefore, when water, formic acid, or methyl formate is contained as impurities in the monomer, the amounts of these impurities must be reduced as much as possible by purifying the monomer in advance of polymerization. The molecular weight of the polymer of the present invention should be in the range from 10,000 to 200,000. When the molecular weight is not more than 10,000, a satisfactory mechanical property cannot be obtained. On the other hand, when the molecular weight is not less than 200,000, processability of the polymer, such as moldability and extrudability, is markedly poor, which is unpractical. The polymerization apparatus used in the present invention may be either a batch-wise one or a continuous one and is not particularly limited. As a batch-wise polymerization apparatus, there may generally be used a reaction vessel equipped with a stirrer. As a continuous apparatus, there may be used self-cleaning type blenders, e.g., Ko-Kneaders, twin-screw continuous extruder-blenders and double shaft, paddle type continuous blenders. The polymerization temperature may be 60-200°C, preferably 60-140°C. The polymerization time is not particularly restricted but generally selected from the range of not less than 10 seconds and not more than 100 minutes. After polymerization, the catalyst is usually deactivated since the catalyst contained in the polymer produced causes depolymerization. The deactivation is generally conducted by contacting the polymer with an aqueous solution or an organic solvent containing a basic substance such as triethylamine or by adding and melt-blending a basic substance with the polymer to neutralize and deactivate the catalyst. The present inventors have made extensive study on the methods of deactivating the polymerization catalyst and resultantly found, as an utterly novel method, a highly effective method in which deactivation is conducted by adding and melt-blending with the copolymer a crystalline acidic adsorbent comprising at least two kinds of metal oxides or metal hydroxides. In more particular, to 100 parts by weight of polyoxymethylene copolymer, there is preferably added and melt-blended 0.001-0.5% by weight, more preferably 0.005-0.1% by weight, of at least one adsorbent selected from a) ion adsorbents comprising at least two kinds of oxides selected from alkali metal oxides, alkaline earth metal oxides, and oxides of trivalent and tetravalent elements, or b) ion adsorbents represented by the formula M1 1-x M2 x (OH) 2 A n- x/n · mH 2 O wherein M1 denotes at least one divalent metal selected from alkaline earth metals; M2 denotes a trivalent metal; A n- denotes an n-valent anion; x is a number satisfying 0 < x ≤ 0.5; and m is a positive number. The alkali metal oxide may be Na 2 O or K 2 O. The alkaline earth metal oxide may be MgO or CaO. The trivalent and tetravalent element oxide may be Al 2 O 3 , SiO 2 , or TiO 2 . Specific examples of the ion adsorbent comprising at least two types of oxides selected from these oxides include 2.5 MgO·Al 2 O 3 ·nH 2 O, 2MgO·6SiO 2 ·nH 2 O, Al 2 O 3 ·9SiO 2 ·nH 2 O, Al 2 O 3 ·Na 2 O·2CO 3 ·nH 2 O, and Mg 0.7 Al 0.3 O 1.15 . In the above formula M1 1-x M2 x (OH) 2 A n- x/n ·mH 2 O, examples of M1 include Mg and Ca , examples of M2 include B, Al, Ga, In, Ti, and Tl, and examples of A n- include CO 3 2- , OH-HCO 3 - , H 2 PO 4 - , NO 3 - , I - , salicylate ion, citrate ion, and tartrate ion. Particularly preferred examples are CO 3 2- and OH - . Specific examples of ion adsorbent of this kind are natural hydrotalcite represented by Mg 0.75 Al 0.25 (OH) 2 CO 3 0.125 ·0.5H 2 O and synthetic hydrotalcite represented by Mg 4.5 Al 2 (OH) 13 CO 3 · 3.5H 2 O. The amount of these deactivating agents to be added is preferably 0.001-0.5% by weight, more preferably 0.005-0.1% by weight, relative to the polymer. When the amount is not more than 0.001% by weight the polymerization catalyst is not deactivated sufficiently. When the amount is not less than 0.5% by weight, discoloration occurs during molding and the color tone of the molded article becomes poor. The particle diameter of the deactivating agent is not particularly limited, but is preferably not more than 100µm to attain enhanced dispersibility. Further, the deactivating agent may be surface-treated to improve the dispersibility into the polymer. The deactivating agent may be added by feeding it to the polymerization reactor after completion of polymerization or, in a continuous polymerization reactor, by feeding it to the latter stage of the reactor, or by adding and mixing it with the polymer discharged from the reactor. The polymer to which the deactivating agent has been added may be further melt-blended to deactivate the polymerization catalyst more thoroughly. The melt-blending is conducted in the temperature range from the melting point of the polymer to 270°C. The melt-blending apparatus may be, for example, single screw type continuous extruder, Ko-Kneader, twin-screw type continuous extruder, etc. When the copolymer obtained has an unstable terminal hydroxyl group, the unstable part is decomposed and removed by conventional methods, for example, by heat-treating the copolymer with a basic substance, such as an aqueous triethylamine solution. This operation can be conducted simultaneously with the operation of adding and melt-blending the deactivating agent of the catalyst or in the same melt-blending apparatus as used for the above deactivating operation. Example The present invention will be described in more detail below with reference to Examples, but the invention is in no way limited by the Examples. The properties measured in the Examples are determined as follows. 1. Terminal formate: The copolymer is hot-pressed at 200°C to form film of 15 µm thickness. The infrared absorption spectrum of the film obtained is taken, from which the ratio of absorbance at v = 1710 cm -1 to absorbance at ν = 1470 cm -1 . D 1710 /D 1470 . is calculated. (see Table 2) 2. Inserted amount and sequence of oxyalkylene units: Ten grams of the copolymer is put in 100 ml of aqueous 3N HCl solution and is decomposed by heating the solution in a tightly sealed vessel at 120°C for 2 hours. After cooling, the amounts of alkylene glycol, dialkylene glycol and trialkylene glycol in the aqueous solution are determined by gas chromatography (FID), and the amount of oxyalkylene units is expressed in terms of % by mole relative to the oxyalkylene units in the copolymer. (see Table 2) As to the sequence of oxyalkylene units, the amount of monoalkylene glycol corresponds to n=1, the amount of dialkylene glycol to n=2 and the amount of trialkylene glycol to n=3. (see Table 2) 3. MI: This is determined in accordance with ASTM D-1238-86. (see Table 3) 4. Heat stability: Resin is retained in an injection molding machine (Arburg All-rounder 100, a trade name, mfd. by Western Trading K.K.) at a cylinder temperature of 230°C and then formed into test pieces of 12 by 120 by 3 mm. The time at which a silver streak develops on the test piece surface is determined. The higher the value of the time is, the more excellent is the heat stability of the polymer. (see Table 3) 5. Resistance to heat aging: Test pieces in accordance with ASTM D-638 are held in a Geer Oven (type GPS-222, mfd. by Tabai ESPEC CORP.) at 240°C and then examined for retention of tensile strength. (see Table 4) 6. Resistance to hot water: Test pieces in accordance with ASTM D-638 are immersed in hot water (flowing water) adjusted to 120°C and then examined for retention of tensile strength. (see Table 4) Note) Description of abbreviations in the Tables A-1: trifluoromethanesulfonic acid A-2: trifluoromethanesulfonic acid anhydride A-3: methyl trifluoromethanesulfonate A-4: trimethylsilyl trifluoromethanesulfonate A-5: boron trifluoride dibutyl etherate B-1: Mg 0.75 Al 0.25 O 1.125 B-2: Al 2 O 3 ·Na 2 O·2CO 3 ·H 2 O B-3: Mg 4.5 Al 2 (OH) 13 CO 3 ·3H 2 O B-4: Al 2 O 3 ·9SiO 2 ·H 2 O B-5: triethylamine C-1: 1,3-dioxolane C-2: 1.3-propanediol formal C-3: 1,4-butanediol formal C-4: 1,6-hexanediol formal C-5: ethylene oxide Example 1 Two thousand grams of a highly purified trioxane (containing 2 ppm of water and 3 ppm of formic acid), 0.8% by mole per trioxane of 1,3-dioxotane and 0.2% by mole per trioxane of methylal were placed in a jacked kneader having two Σ-shaped blades and the mixture is heated to 70°C. Then a dioxane solution of trifluoromethanesulfonic acid (0.002 mol/ℓ) is added so as to give a proportion of trifluoromethanesulfonic acid to trioxane of 5 x 10 -6 % by mole, and the resulting mixture is allowed to polymerize. Fifteen minutes after the initiation of polymerization, cold water is put into the jacket and the reaction mixture is cooled under nitrogen atmosphere. After 1 hour, the content of the kneader is taken out, and Mg 0.75 Al 0.25 O 1.125 (Kyowaad KW2300, a trade name, mfd. by Kyowa Chemical Industry) is added as a deactivating agent in a proportion of 0.01% by weight relative to the polymer obtained, and the resulting mixture is extruded at 200°C with a vent-type twin-screw extruder. Further, 1 part by weight of triethylamine, 5 parts by weight of water, and 0.2 part by weight of 2,2-methylenebis(4-methyl-6-t-butylphenol) are added to 100 parts by weight of the polymer extruded above and the mixture is extruded with a vent-type image screw extruder (extrusion temperature: 200°C, vent pressure: 267kPa (200 torr)). The copolymer thus obtained is evaluated for its terminal formate, amount of inserted oxyalkylene units, sequence of oxyalkylene units, MI, heat stability, resistance to heat aging and resistance to hot water. The results are shown in Tables 2,3 and 4. The polymerization yield is as high as 89% and D 1710 /D 1470 , which represents the amount of terminal formate groups, is as low as 0.01. With regard to oxyalkylene units, the amount of diethylene glycol relative to the amount of ethylene glycol is as low as 0.3% by mole. With regard to the properties of the polymer, heat stability is good. Further, resistance to heat aging and resistance to hot water are both good, the retentions of tensile strength after the lapse of 2000 hours being 80% or more in both tests. Examples 2 to 18 Polyoxymethylene copolymers are synthesized in the same manner as in Example 1 except for changing the amounts of catalyst, water and formic acid in the monomer, 1,3-dioxolane and methylal and/or varying the type of comonomer and other conditions as shown in Table 1. The polymers obtained are treated and evaluated respectively in the same manner as in Example 1. The results are shown in Tables 2, 3 and 4. Similarly to the results in Example 1, all the copolymers showed a high polymerization yield and a low content of terminal formate groups. Also, they showed a good heat stability. Further, the copolymers were excellent both in resistance to heat aging and in resistance to hot water, the retentions of tensile strength after the lapse of 2,000 hours being both 80% or more. Examples 19 to 23 Polyoxymethylene copolymers are synthesized in the same manner as in Example 1 except for changing the type of catalyst, the amount of catalyst and other conditions as shown in Table 1. The polymers obtained are treated and evaluated respectively in the same manner as in Example 1. The results are shown in Tables 2, 3 and 4. Similarly to the results in Example 1, all the copolymers showed a high polymerization yield and a low content of terminal formate groups. Also, they showed a good heat stability. Further, the copolymers are excellent both in resistance to heat aging and in resistance to hot water, the retentions of tensile strength after the lapse of 2.000 hours being both 80% or more. Comparative Example 1 A polyoxymethylene copolymer was synthesized by using the apparatus of Example 1 and in the same manner as in Example 1 except that boron trifluoride dibutyl etherate (0.02 mol/ℓ benzene solution) is used as the polymerization catalyst and the catalyst concentration is changed to 5 x 10 -3 % by mole relative to trioxane. The polymer taken out from the kneader was melt-blended with a deactivating agent in the same manner as in Example 1. The resulting polymer is treated and evaluated respectively in the same manner as in Example 1. The results are shown in Tables 2, 3 and 4. The polymer showed a high value of terminal formate amount of 0.045 in terms of D 1710 /D 1470 . It showed a heat stability of 48 min, which is markedly lower as compared with the values in Examples. The copolymer is poor both in resistance to heat aging and in resistance to hot water as compared with the polymers of Examples, the retention of tensile strength after the lapse of 2,000 hours being 60% or less. Comparative Examples 2 to 8 Polyoxymethylene copolymers are synthesized by using the apparatus of Example 1 and in the same manner as in Example 1 but under the conditions shown in Table 1. Under the conditions of Comparative Examples 3 and 4, the polymerization activity is insufficient and no polymer could be obtained. Under other conditions, polymers could be obtained although the polymerization yields are lower than in Examples. The polymers obtained are treated and evaluated respectively in the same manner as in Comparative Example 1. The results are shown in Tables 2. 3 and 4. All the polymers showed a high value of terminal formate group amount of 0.040 or more in terms of D 1710 /D 1470 . Also, they showed a heat stability of 50 min or less, which is markedly lower than in Examples. Further, they are poor both in resistance to heat aging and in resistance to hot water, the retentions of tensile strength after the lapse of 2,000 hours being both 50% or less. Comparative Examples 9 and 10 Polyoxymethylene copolymers are synthesized by using the apparatus of Example 1 and in the same manner as in Comparative Example 1 but under the conditions shown in Table 1. Thirty minutes after the initiation of polymerization, 1 ℓ of an aqueous 5% by weight triethylamine solution is added to deactivate the polymerization catalyst and terminate the polymerization. The polymer obtained is collected by filtration and dried by heating under a nitrogen gas stream at 135°C. Then, to 100 parts by weight of the polymer thus obtained were added 1 part by weight of triethylamine, 5 parts by weight of water and 0.2 part by weight of 2,2-mettrylenebis(4-methyl-6-t-butylphenol) and the resulting mixture is extruded with a vertt-type single screw extruder (extrusion temperature: 200°C, vent pressure: 267kPa (200 torr)). The polymers thus obtained are evaluated in the same manner as in Example 1. The results are shown in Tables 2, 3 and 4. The copolymers showed a high value of terminal formate group amount of 0.040 or 0.044 in terms of D 1710 /D 1470 . Also, they showed a heat stability of 35 min or 40 min, which are markedly lower than in Examples. Further, the polymers are very poor both in resistance to heat aging and in resistance to hot water, the determination of tensile strength after the lapse of 2,000 hours being impossible. Comparative Examples 11 to 16 Polyoxymethylene copolymers are synthesized by using the apparatus of Example 1 and under the same conditions as in Example 1 except for changing the amount of trifluoromethanesulfonic acid of polymerization catalyst and the moisture content and the formic acid concentration in the monomer as shown in Table 1. The results are shown in Tables 2, 3 and 4. At a catalyst concentration of 1 x 10 -6 % by mole relative to trioxane, no polymer could be obtained. Also, at catalyst concentrations of 2 x 10 -5 to 5 x 10 -5 % by mole relative to trioxane, no polymer could be obtained or polymerization yield is very poor, when the amount of water or formic acid in the monomer is 50 ppm or more. Further, at a catalyst concentration of 5 x 10 -5 % by mole relative to trioxane, the polymer obtained is very poor in heat stability, resistance to heat aging, and resistance to hot water. Examples 24 to 26 A continuous blending reactor (KRC-Kneader, a trade name, mfd. by Kurimoto Limited) comprised of a barrel of L/D of 14 having a cross section of partially overlapping circles of 50 mm inside diameter and equipped on the outside with a jacket through which a heating medium can be passed, and of two rotating shafts provided inside the barrel and having a number of paddles which engage with one another is used. At a jacket temperature of 80°C and a number of rotation of 78 rpm, trioxane (2 kg/hour). 1,3-dioxotane (3 levels of 0.3, 0.8 and 1.4% by mole relative to trioxane), methylal (0.3% by mole relative to trioxane) and a dioxane solution (0.002 mole/1) of trifluoromethanesulfonic acid are fed continuously into the reactor so as to give a proportion of trifluoromethanesulfonic acid to trioxane of 1 x 10 -5 % by mole, to effect polymerization. The polymer discharged from the polymerization reactor is taken out under nitrogen atmosphere, then Mg 0.75 Al 0.25 O 1.125 (Kyowaad KW2300, a trade name, mfd. by Kyowa Chemical Industry) was added as a deactivating agent to the polymer in a proportion of 0.01% by weight to the polymer, and the resulting mixture is extruded with a vent-type twin-screw extruder at 200°C. To 100 parts by weight of the polymer thus obtained are added 1 part by weight of triethylamine. 5 parts by weight of water and 0.2 part by weight of 2.2-methytenebis(4-methy1-6-t-butylphenol) and the mixture is extruded with a vent-type single screw extruder (extrusion temperature: 200°C, vent pressure: 200 torr). The copolymers thus obtained are evaluated in the same manner as in Example 1. The results are shown in Tables 1 and 2. All the polymers showed a high polymerization yield and a low amount of terminal formate groups. They showed a good heat stability and excellent tensile strength. Further, the copolymers are excellent both in resistance to a heat aging and in resistance to hot water, the retentions of tensile strength after the lapse of 2.000 hours being 80% or more. Examples 27 to 31 Polyoxymethylene copolymers are synthesized under the same conditions as in Example 25. Then, the deactivating agents shown in Table 1 were added to the copolymers, as a deactivating agent used after polymerization, in amounts shown in Table 1, and mett-blended in the same manner as in Example 25. The resulting polymers are treated and evaluated respectively in the same manner as in Example 25. The results are shown in Tables 1 and 2. All the copolymers showed a good heat stability and tensile strength as in Example 1. Further, the copolymers were excellent both in resistance to heat aging and in resistance to hot water, the retentions of tensile strength after the lapse of 2,000 hours being 80% or more. Table 1, Polymerization catalyst Catalyst concentration (mol %) Water in monomer (ppm) Formic acid in monomer (ppm) Comonomer Comonomer amount (mol %) Deactivating agent Amount of deactivating agent added (phr) Example-1 A-1 5.0x10 -6 2 3 C-1 0.8 B-1 0.01 Example-2 A-1 5.0x10 -6 5 10 C-1 0.8 B-1 0.01 Example-3 A-1 1.0x10 -5 11 0 C-1 0.8 B-1 0.01 Example-4 A-1 1.0x10 -5 18 19 C-1 0.0 B-1 0.01 Example-5 A-1 2.0x10 -5 26 0 C-1 0.0 B-1 0.01 Example-6 A-1 2.0x10 -5 12 22 C-1 0.8 B-1 0.01 Example-7 A-1 2.0x10 -5 32 22 C-1 0.8 B-1 0.01 Example-0 A-1 1.0x10 -5 2 3 C-1 0.3 B-1 0.01 Example-9 A-1 1.0x10 -5 3 3 C-1 0.5 B-1 0.01 Example-10 A-1 1.0x10 -5 3 3 C-1 1 B-1 0.01 Example-11 A-1 1.0x10 -5 5 8 C-1 1.4 B-1 0.01 Example-12 A-1 1.0x10 -5 3 0 C-2 0.8 B-1 0.01 Example-13 A-1 1.0x10 -5 3 8 C-3 0.0 B-1 0.01 Example-14 A-1 1.0x10 -5 2 5 C-4 0.8 B-1 0.01 Example-15 A-1 1.0x10 -5 3 8 C-1 0.8 B-1 0.01 Example-16 A-1 1.0x10 -5 3 8 C-1 0.8 B-1 0.01 Example-17 A-1 1.0x10 -5 3 8 C-1 0.08 B-1 0.01 Example-18 A-1 1.0x10 -5 3 8 C-1 0.8 B-1 0.01 Example-19 A-2 5.0x10 -6 2 5 C-1 0.8 B-1 0.01 Example-20 A-2 1.0x10 -5 17 25 C-1 1.4 B-1 0.01 Example-21 A-3 5.0x10 -6 2 8 C-1 0.8 B-1 0.01 Example-22 A-3 1.0x10 -5 28 5 C-1 0.3 B-1 0.01 Example-23 A-4 1.0x10 -5 5 8 C-1 0.8 B-1 0.01 Example-24 A-1 1.0x10 -5 3 8 C-1 0.3 B-1 0.01 Example-25 A-1 1.0x10 -5 3 8 C-1 0.8 B-1 0.01 Example-26 A-1 1.0x10 -5 3 8 C-1 1.4 B-1 0.01 Example-27 A-1 1.0x10 -5 3 8 C-1 0.8 B-1 0.005 Example-28 A-1 1.0x10 -5 3 8 C-1 0.8 B-1 0.05 Example-29 A-1 1.0x10 -5 3 8 C-1 0.8 B-2 0.01 Example-30 A-1 1.0x10 -5 3 8 C-1 0.8 B-3 0.01 Example 31 A-1 1.0x10 -5 3 8 C-1 0.8 B-4 0.02 Comp. Example-1 A-5 5.0x10 -3 2 3 C-1 0.0 B-1 0.01 Comp. Example-2 A-5 2.0x10 -3 2 3 C-1 0.0 B-1 0.01 Comp. Example-3 A-5 1.0x10 -3 2 3 C-1 0.5 == == Comp. Example-4 A-5 1.0x10 -3 2 3 C-1 1.4 == == Comp. Example-5 A-5 2.0x10 -3 2 3 C-1 0.5 B-1 0.01 Comp. Example-6 A-5 2.0x10 -3 2 3 C-1 1.4 B-1 0.01 Comp. Example-7 A-5 2.0x10 -3 2 3 C-5 0.8 B-1 0.01 Comp. Example 8 A-5 2.0x10 -3 2 3 C-5 1.4 B-1 0.01 Comp. Example-9 A-5 2.0x10 -3 2 3 C-5 0.8 B-5 == Comp. Example-10 A-5 2.0x10 -3 2 3 C-5 1.4 B-5 == Comp. Example-11 A-1 1.0x10 -6 2 3 C-1 0.8 == == Comp. Example-12 A-1 2.0x10 -5 52 8 C-1 0.8 Comp. Example-13 A-1 2.0x10 -5 2 55 C-1 0.8 == == Comp. Example-14 A-1 5.0x10 -5 52 8 C-1 0.8 B-1 0.05 Comp. Example-15 A-1 5.0x10 -5 2 55 C-1 0.8 == == Comp. Example-16 A-1 5.0x10 -5 2 3 C-1 0.8 B-1 0.01 Table 2 Polymerization yield Formate terminal Inserted oxyalkylene unit amount Sequence (mol%) (%) D 1710 /D 1470 (mol%) n=1 n>2 Example-1 89 0.010 0.24 99.7 0.3 Example-2 88 0.011 0.25 99.0 0.6 Example-3 92 0.013 0.23 99.4 0.6 Example-4 90 0.018 0.23 99.5 0.5 Example-5 95 0.014 0.22 99.2 0.0 Example-6 93 0.020 0.23 99.4 0.6 Example-7 91 0.024 0.23 99.5 0.5 Example-0 95 0.013 0.08 100 - Example-9 94 0.013 0.15 100 - Example-10 93 0.013 0.31 90.5 1.5 Example-11 90 0.015 0.43 97.2 2.8 Example-12 93 0.014 0.26 == == Example-13 91 0.015 0.27 == == Example-14 91 0.015 0.27 == == Example-15 B9 0.013 0.25 99.5 0.5 Example-16 B9 0.013 0.25 99.4 0.6 Example-17 94 0.015 0.23 99.7 0.3 Example-18 94 0.014 0.22 99.7 0.3 Example-19 88 0.012 0.23 99.5 0.5 Example-20 90 0.010 0.42 97.4 2.6 Example-21 06 0.014 0.22 99.6 0.4 Example-22 89 0.017 0.09 100 - Example-23 92 0.015 0.23 99.5 0.5 Example-24 95 0.012 0.00 100 - Example-25 94 0.012 0.22 99.6 0.4 Example-26 94 0.012 0.42 98.4 1.6 Example-27 == == == == == Example-28 == == == == == Example-29 == == == == == Example-30 == == == == == Example-31 == == == == == Comp. Example 1 84 0.045 0.23 93.6 6.4 Comp. Example-2 72 0.041 0.25 94,3 5.7 Camp. Example-3 Non-polymerizable == == == == Comp. Example-4 Non-polymerizable == == == == Comp. Example-5 61 0.047 0.17 93.8 6.2 Comp. Example-6 55 0.042 0.44 94.1 5.9 Comp. Example-7 56 0.048 0.28 92.2 7.8 Camp. Example-8 52 0.047 0.45 90.8 9.2 Comp. Exainple-9 70 0.040 0.28 93.2 6.8 Camp. Example-10 65 0.044 0.45 89.5 10.5 Comp. Example-11 Non-polymerizable == == == == Comp. Example-12 42 == == == == Comp. Example-13 Non-polymerizable == == == == Comp. Example-14 64 0.030 0.28 90.4 1.6 Comp. Example-15 39 == == == == Comp. Example-16 95 0.030 0. 24 90.9 1.2 Table 3 M.p. (°C) MI (g/10 min) Heat stability (min) Example-1 172.2 10.6 101 Example-2 172.2 10.5 98 Example-3 172.5 9.2 90 Example-4 == 9.5 91 Example-5 172.8 8.8 86 Example-6 == 9.2 85 Example-7 == 9.5 85 Example-8 173.8 8.8 86 Example-9 173.1 9.0 87 Example-10 171.1 9.2 94 Example-11 170.2 10.6 103 Example-12 172.0 9.5 92 Example-13 171.8 9.2 90 Example-14 171.8 9.2 95 Example-15 172.1 45.2 90 Example-16 172.3 32.0 93 Example-17 172.5 3.2 96 Example-18 172.5 1.4 99 Example-19 172.4 9.0 96 Example-20 170.1 9.3 96 Example-21 162.5 8.8 97 Example-22 173.8 9.0 94 Example-23 == 9.5 91 Example-24 173.6 8.9 95 Example-25 172.5 9.2 100 Example-26 170.2 9.2 95 Example-27 == 9.2 91 Example-28 == 9.2 99 Example-29 == 9.2 95 Example-30 == 9.2 93 Example-31 == 9.2 95 Comp. Example-1 172.6 9.8 48 Camp. Example-2 172.5 10.0 53 Comp. Example-3 == == == Comp. Example-4 == == == Comp. Example-5 173.0 11.0 41 Comp. Example-6 170.4 11.2 50 Camp. Example-7 172.2 10.8 44 Comp. Example-8 170.0 10.8 44 Comp. Example-9 172.2 10.8 35 Comp, Example-10 170.5 10.8 40 Comp. Example-11 == == == Comp. Example-12 == == == Comp. Example-13 == == == Comp. Example-14 172.0 38 Comp. Example-15 == == == Comp. Example-16 172.5 52 Table 4 Heat aging resistance (%) Hot water resistance (%) 500 hr 1,000 hr 2,000 hr 500 hr 1,000 hr 2,000 hr Example-1 100 100 90 100 99 86 Example-2 100 100 92 100 98 85 Example-3 100 99 91 100 98 85 Example-4 100 97 90 100 97 84 Example-5 100 98 91 100 97 84 Example-6 100 97 88 100 95 85 Example-7 100 90 90 100 95 85 Example-8 100 96 88 100 96 83 Example-9 100 97 89 100 96 83 Example-10 100 99 94 100 90 87 Example-11 100 100 95 100 90 92 Example-12 100 99 90 100 90 86 Example-13 100 98 90 100 98 85 Example-14 100 98 89 100 99 86 Example-15 100 98 92 100 98 85 Example-16 100 98 92 100 98 85 Example-17 100 99 94 100 98 87 Example-18 100 99 94 100 98 87 Example-19 100 100 94 100 99 86 Example-20 100 98 92 100 98 84 Example-21 100 100 95 100 99 06 Example-22 100 99 92 100 90 85 Example-23 100 98 92 100 98 84 Example-24 100 97 90 100 98 06 Example-25 100 99 94 100 99 90 Example-26 100 100 95 100 100 92 Example-27 100 98 90 100 99 84 Example-28 100 97 89 100 99 92 Example-29 100 98 92 100 99 86 Example-30 100 98 92 100 99 06 Example-31 100 97 90 100 99 88 Comp. Example-1 100 76 52 100 67 26 Comp. Example-2 100 75 48 100 60 Unmeasurable Comp. Example-3 == == == 100 == == Comp. Example-4 == == == 100 == == Comp. Example-5 100 75 49 100 62 22 Comp. Example-6 100 77 50 100 62 25 Comp. Example-7 100 71 43 100 60 22 Comp. Example-8 100 70 45 100 62 27 Comp. Example-9 100 67 Unmeasurable 90 54 Unmeasurable Camp. Example-10 100 70 Unmeasurable 99 50 Unmeasurable Comp. Example-11 == == == == == == Comp. Example-12 == == == == == == Comp. Example-13 == == == == == == Comp. Example-14 100 77 41 100 60 35 Comp. Example-15 == == == == == == Comp. Example-16 100 80 55 100 70 36 INDUSTRIAL APPLICABILITY The copolymer made by the process of the present invention is excellent in strength, rigidity, fatigue characteristic, friction abrasion characteristic, heat stability, etc. The copolymer can be put to various uses for which prior polyoxymethylene homopolymers and copolymers have been used, for example, mechanism elements such as cams, gears, switches, handles, levers, reels, hubs and bearings; miscellaneous goods such as fasteners, buttons and dips; and further a large number of automotive, electric and electronic parts. Further, the copolymer can be used, by virtue of its excellent characteristics, for parts of water treatment, kitchen or toilet goods, such as pump impellers, pump casings, shower nozzles and taps. The copolymer can also be formed into extruded rods or sheets, or blow-molded. It can be incorporated with known additives, for example, various antioxidants, heat stabilizers, pigments, nucleating agents, antistatic agents, weatherproofing agents, etc., and various reinforcing materials, such as carbon fiber, glass fiber, glass beads, talc, mica, etc. Further, the copolymer can be made into polymer blends and polymer alloys with such polymers as polyurethane, PMMA, PE, etc.

Claims: A process for producing a polyoxymethylene copolymer which comprises copolymerizing a mixture of a cyclic oligomer of formaldehyde or a cyclic acetal as the principal monomer and a comonomer which is a cyclic ether represented by the formula wherein R and R 0 may be the same or different and are each selected from hydrogen, an alkyl group and an aryl group, R bound to different carbon atoms and R 0 bound to different carbon atoms may respectively be the same or different and are selected from hydrogen, an alkyl group and an aryl group, and m is 2 to 6; or a cyclic formal represented by the formula wherein R and R 0 may be the same or different and are each selected from hydrogen, an alkyl group and an aryl group, R bound to different carbon atoms and R 0 bound to different carbon atoms may respectively be the same or different and are selected from hydrogen, an alkyl group and an aryl group, and m is 2 to 6; in the presence of a perfluoroalkylsulfonic acid or a perfluoroalkylsulfonic acid derivative as the polymerization catalyst in an amount of 5 x 10 -6 to 2 x 10 -5 % by mole relative to the principal monomer to obtain a copolymer which contains 0.07% - 0.5% by mole of polyoxyalkylene units in proportion to polyoxymethylene units, and wherein the content of water and formic acid in the monomer mixture are, respectively, not more than 40 ppm by weight. A process according to claim 1, in which the amount of comonomer in the polymerisation mixture is from 0.3 to 3.5% by mole of the principal monomer. A process according to claim 1 or 2, further comprising deactivating the polymerization catalyst in the resulting polyoxymethylene copolymer, by adding and melt-blending at least one ion adsorbent selected from (a) ion adsorbents comprising as the main components at least two kinds of oxides selected from alkali metal oxides, alkaline earth metal oxides, and oxides of trivalent and tetravalent elements, or (b) ion adsorbents represented by the formula M1 1-x M2 x (OH) 2 A n- x/n .mH 2 O wherein M1 denotes at least one divalent metal selected from alkaline earth metals, M2 denotes a trivalent metal, A n- denotes an n-valent anion, x is a number that satisfies the expression 0 < x ≤ 0.5, and m is a positive number, in an amount of 0.001-0.5% by weight relative to the polymer to obtain the polyoxymethylene copolymer composition.

Inventors: MATSUZAKI KAZUHIKO, MORISHITA HIROHISA, MATSUZAKI, KAZUHIKO, MORISHITA, HIROHISA
Applicants: ASAHI CHEMICAL CORP, ASAHI KASEI CHEMICALS CORPORATION
Application year: 1991
Main classification: C08G2
IPC codes: C08L59, C08K3, C08G2