Low permeability rubber hose

Abstract: A rubber hose comprising an inner tube (1) of synthetic resin, a silver or silver alloy thin film (2) sputtered or ion plated on the inner tube, and a rubber layer (4) heat cured to the thin film through adhesive (3) exhibits low gas and solvent permeability and high flexibility while maintaining such properties even on angular bending.

Description: This invention relates to a rubber hose having low gas and solvent permeability. In the prior art, rubber hoses were generally used in a wide variety of uses as automobile fuel feed hoses, torque converter hoses, power steering hoses, air conditioner hoses, refrigerator hoses, propane gas feed hoses, hydraulic hoses as well as household utility. A variety of media including water, oil, organic solvents, and gases are conducted through the rubber hoses. Therefore, the rubber hoses are required not only to be flexible, but also to be well resistant to these transfer media and fully impermeable to organic gases and organic solvents. In general, rubber surfaces do not always exhibit high resistance against chemical loads such as organic gases and organic solvents. Prior art approaches for improving the organic gas and solvent resistance of rubber included (1) to use a rubber material having different polarity from the solvent, (2) to increase the degree of crosslinking of rubber, (3) to increase the amount of filler added, and (4) to increase the amount of rubber used, that is, wall thickness. Approach (1) requires expensive rubbers such as chloroprene rubber, butadiene-acrylonitrile rubber, acryl rubber, epichloro-hydrin rubber, and fluororubber. Approach (2) detracts from softness and flexing resistance of rubber. Approach (3) has a limit in conjunction with processability and physical properties. The solvent resistance is improved only in proportion to a volume fraction of the filler. As to approach (4), an increased wall thickness adds to product weight and cost and detracts from softness. In addition to these problems, either of these approaches fails to increase the organic gas and solvent resistance of rubber beyond a certain limit. In order to enhance the performance and the gas and solvent resistance of rubber hoses, a number of proposals were made for composite resin - rubber hoses. Typically a thin resin layer is applied to the inside surface of a rubber hose to be in contact with a transfer medium. In the composite structure, the resin layer serves for such functions as organic solvent resistance, gas impermeability, and chemical resistance while the outer rubber layer is responsible for hose's own functions such as softness and vibration absorption. Composite rubber hoses are typically manufactured by coating a solvent soluble nylon film to the inside surface of a rubber hose as disclosed in Japanese Patent Application Kokai No. 113885/1985. Alternative methods are disclosed in Japanese Patent Publication Nos. 45302/1988 and 125885/1988 wherein a rubber hose is manufactured by extrusion coating a resin on a mandrel or shaping core for the hose to form a resin film. An adhesive is applied to the resin film. After drying, an intermediate rubber composition is coated, a reinforcing layer is braided, and an overcoating rubber layer is further coated. A final vulcanization shaping step completes a hose having improved organic gas and solvent resistance. In the case of composite rubber hoses for accommodating coolant fluid for automobile air conditioners or the like, nylon resins are most often used as the resin forming the inner layer of the hose. A variety of nylon resins are used in practice including nylon 6, nylon 66, nylon 6/nylon 66 copolymer, nylon 11, nylon 12, nylon 4, copolymers thereof, modified ones, blends thereof, and blends of nylons and olefins. The nylon used on the inner surface of rubber hoses for accommodating coolant fluid has to meet the following requirements. (1) Low permeability to Freon gas (gas impermeability). (2) It is not susceptible to hydrolysis by moisture penetrating from outside the hose (moisture resistance). (3) It is resistant to heat. (4) It withstands dynamic motion as in an impulse test. (5) It is gas-tight at a base or connector end. With respect to these requirements, nylon 6, nylon 66, and nylon 6/nylon 66 copolymers are very low in Freon gas permeability, but relatively high in moisture permeability. In turn, nylon 11, nylon 12 and analogs are low in moisture permeability and less susceptible to hydrolysis, but moderately high in Freon gas permeability. Some of these drawbacks may be eliminated by substituting a butyl rubber or Hypalon® (chlorosulfonated polyethylene by E.I. duPont) having low moisture permeability for the rubber portion. The use of butyl rubber can reduce moisture permeation from the exterior. However, if the nylon layer contributing to Freon impermeability fails due to the presence of defects therein, such a failure would cause a serious failure of the entire hose because the butyl rubber layer is not self sustaining. In turn, the use of Hypalon® is limited because it is expensive and difficult to bond. Attempts have been made to blend nylon 6 or nylon 66 or a copolymer thereof having Freon gas impermeability with nylon 11 or nylon 12 having low moisture permeability, or with olefin resins. These attempts improve moisture impermeability and hydrolysis resistance, but with loss of Freon gas impermeability. Therefore, prior art combinations of rubber with nylons or the like were unsuccessful in fully satisfying the requirements of rubber hoses for transfer of coolant and similar fluids. It was thus proposed to wind a length of aluminum or copper strip or a length of plastic tape having such a metal thin film coated thereon around the outer periphery of a resinous inner tube, followed by coating a rubber layer thereon, or to form the inner surface of a rubber hose directly from a length of tape having a metal thin film coated thereon (see the Japanese Utility Model Applications with laid-open Nos. 177620/1979, 198221/1979, 162379/1981, 94975/1983, 99582/1983, and 158879/1983, also JP-A-205144/1982, and JP-B-13812/1988). These proposals take advantage of the barrier nature of a metal film to provide Freon and moisture impermeability, but suffer from various problems. Manufacture of these structures is complicated and thus expensive. When a length of metal foil or metallized tape is used, the seam between adjoining turns is simply a physical overlap. The turns can be displaced to form a gap therebetween under severe service conditions, reducing the barrier nature of the metal thin film so that gas leakage can occur. Reduced softness is also a problem of these rubber hoses. Further, these methods generally use an adhesive in applying rubber on a metal foil or metallized tape wrap on a resinous inner tube to form a composite structure. The adhesive will undesirably lose its adhesive force upon contact with an organic solvent that has penetrated through the resinous inner tube. To overcome these prior art problems, we previously proposed to coat a synthetic resin inner tube on the outer surface with a metal or metal compound by dry plating, as disclosed in JP-A-209224/1990 and JP-A-209225/1990. One of the important features of rubber hoses is flexibility, because rubber hoses are often bent during service. When a rubber hose having an outer diameter of 20 mm and an inner diameter of 10 mm is rounded to a diameter of 100 mm, a strain of about 10% is caused in the hose at the inner surface. According to our study, strains of about 10% would induce cracking and crazing in general metals and metal compounds even in thin film form; these would thus lose their barrier nature. Although these metals and metal compounds are acceptable if hose service conditions such as bending radius are restricted, rubber hoses featuring flexibility are required to maintain gas impermeability even under extremely angular bends. Preferred embodiments of the invention may attain one or more of the following objects: (a) to eliminate the above-mentioned drawbacks of prior art rubber hoses and to provide a novel and improved low permeable rubber hose of the composite structure including a resinous layer and a rubber layer in which solvent and moisture impermeability is improved without losing the softness characteristic of the rubber hose; (b) to provide such a composite rubber hose which is resistant against solvent and moisture and durable against strains by angular bending; (c) to provide such a composite rubber hose which can prevent an adhesive from losing its adhesive force. According to the present invention, a hose may be provided by furnishing an inner tube of a synthetic resin having an outer peripheral surface, forming a thin film of silver or a silver base alloy on the outer surface of the inner tube, and heat curing a rubber layer to the thin film through an adhesive layer, thus integrating into a low permeable rubber hose. We made efforts to solve the abovementioned problems of a rubber hose of a composite structure having a synthetic resin inner layer and a rubber outer layer. A thin film of silver or a silver base alloy is formed on the outer peripheral surface of the inner tube by any desired plating. A rubber layer is heat cured to the thin film through an adhesive. Since this integral coverage of the rubber layer over the inner tube allows the silver or silver alloy thin film to maintain its barrier property to improve organic gas and moisture impermeability, the composite hose has improved solvent and moisture resistance preferably without detracting from the softness characteristic of the rubber hose. Unlike the prior art method involving wrapping of metal or metallized tape, the silver or silver alloy thin film plate does not lose its barrier property so that the synthetic resin inner tube and the rubber layer can maintain their bond via the thin film even in an impulse test. The silver or silver alloy thin film can maintain its barrier property because it well accommodates strains caused by bends and twists so that no cracking occurs at strains as high as about 10%. There is thus obtained a low permeable rubber hose capable of withstanding angular bends. Since the adhesive layer is disposed outside the silver or silver alloy thin film having good barrier property, this configuration eliminates the problem found in the prior art rubber hose having metal or metallized tape wrapped on a resin inner tube that the adhesive will lose its adhesive force upon contact with an organic solvent that has penetrated through the resinous inner tube. The low permeable rubber hose may be continuously manufactured by means of existing installations in an efficient manner since it suffices to add the silver or silver alloy thin film forming step to the composite rubber hose manufacture process between the inner tube resin extrusion step and the adhesive application step. The above and other objects, features, and advantages of the present invention will be better understood from the following description taken in conjunction with the accompanying drawings, in which: FIG. 1 is a transverse cross section of an upper half of a low permeable rubber hose according to one embodiment of the invention. FIG. 2 is a diagram illustrating the steps in the manufacture of the rubber hose. Referring to FIG. 1, there is illustrated in transverse cross section a low permeable rubber hose according to one embodiment of the present invention. The hose includes an inner tube 1 of a synthetic resin having an outer peripheral surface and an inner peripheral surface which is in direct contact with a fluid to be transferred through the hose. A thin film 2 of silver or silver base alloy is formed on the outer peripheral surface of the inner tube 1. An adhesive layer 3 and then a rubber layer 4 are coated onto the thin film 2 whereby the rubber layer 4 is bonded to the inner tube 1. A reinforcing layer 5 and a rubber sheath 6 are provided if desired. Thereafter the structure is heated and pressurized for vulcanization. Resin Inner Tube The low permeable rubber hose includes an inner tube of a synthetic resin. The synthetic resin of the inner tube may be suitably selected depending on the intended application of the hose. Since the silver or silver alloy thin film 2 provides a barrier layer which mitigates the burden imposed on the resin layer, the material may be selected from a wider variety of resins than in the prior art. Examples of the useful resin include polyesters such as polyethylene, polypropylene, polybutene-1, polyallylate, polyethylene terephthalate, polybutylene terephthalate, polyoxybenzoyl, etc.; nylons such as nylon 6, nylon 66, nylon 11, nylon 12, nylon 4, nylon 6/66, nylon 6/10, nylon 6/12, etc.; polyamides such as aromatic polyamides; polyethers such as polyacetal, polyphenylene oxide, polyether ether ketone, polyphenylene sulfide, etc.; polysulfones such as polysulfone, polyether sulfone, etc.; polyimides such as polyether imides, polyamide imides, polybismaleimides, etc.; polycarbonate; fluoro resins such as polyvinyl fluoride, polyvinylidene fluoride, polytrifluoromonochloroethylene, etc.; various copolymers such as ethylene tetrafluoroethylene copolymers, hexafluoropropylene tetrafluoroethylene copolymers, and perfluoroalkoxytetrafluoroethylene copolymers; and thermoplastic urethane, polyvinyl chloride, polyvinylidene chloride, vinyl chloride/vinylidene chloride copolymers, crosslinked vinyl chloride resins, silicone resins, polyurethanes, and the like. These resins may be used alone or as a blend of two or more of the foregoing resins. Also employable are a blend of such a resin with another polyolefin and a blend of such a resin with an elastomer such as rubber. Also useful are composite plastic materials comprising any of the foregoing resins and a reinforcement in the form of highly stiff organic fibers such as glass fibers, carbon fibers, boron fibers, silicon carbide and Kevlar. Blends of any of the foregoing resins with carbon black, silica, calcium carbonate, clay, antioxidants or the like may also be used. The inner tube may have a single layer structure or a laminate structure having two or more layers of the foregoing resins. The inner tube may preferably have a wall thickness of from about 5 to about 300 µm, more preferably from about 10 to about 100 µm. A wall thinner than 5 µm is often difficult to form as a film and has insufficient barrier properties whereas a wall thicker than 300 µm will sometimes lack softness. Prior to formation of a silver or silver alloy thin film on the resin inner tube, a pretreatment, more particularly a wet or dry surface treatment is preferably carried out to activate the surface of the resin tube. The dry surface treatment may be either a mechanical treatment such as buffing or an electrical treatment such as corona discharge treatment, vacuum plasma treatment, and atmospheric plasma treatment. In the latter case, any surface treating gas may be used insofar as it can impart activity and wettability to the resin surface. Preferred surface treating gases include air, argon, oxygen, nitrogen, helium, carbon monoxide, carbon dioxide, carbon tetrafluoride and the like, alone or in admixture. The power source for generating an electric discharge may be any of those commonly used in electric discharge treatment including DC, AC, RF, and microwave power sources. Sputter etching is another useful pretreatment. The wet surface treatment may be carried out in a conventional manner using mineral acids, organic halides or other agents. Ag Thin Film A thin film of silver or a silver-based alloy is formed on the outer peripheral surface of the resinous inner tube. Silver-based alloys used herein are silver alloys containing more than about 50% by weight of silver, preferably more than about 80% by weight of silver, for example, Ag-Au, Ag-Cu, Ag-Zn, Ag-Sb, and Ag-Cd. If desired, another metal, metal alloy or metal compound may be chosen to provide a multiplicity of layers. The thickness of the silver or silver alloy thin film is not particularly limited although a thickness of from 10 Å to 10 µm, especially from 50 Å to 1 µm is preferred for adequate barrier property, efficient thin film production, and no impairment of rubber hose softness. The silver or silver alloy thin films may be formed by any desired methods including wet plating methods such as electroless plating and electric plating and dry plating methods such as ion plating and sputtering, with the dry plating methods being preferred. Electroless plating may be carried out in a conventional manner by forming catalytic metal nuclei such as metallic palladium or silver nuclei prior to electroless plating. If desired, electroless plating may be followed by electric plating. In the case of dry plating, sputtering and ion plating are preferred because closely bonding and crack-free films are obtained without losing the softness of rubber hoses. Any desired techniques may be employed for forming silver or silver alloy thin films by dry plating. Those skilled in the art will make a proper choice for dry plating with respect to operating parameters associated with a dry plating apparatus including high vacuum, introduction of argon, oxygen and other gases, substrate temperature, and annealing. For ion plating, a proper choice may be made with respect to evaporation of a vapor source by resistance heating, induction heating, electron beam heating or the like, and ionization of vapor and acceleration of ionized vapor by RF plasma, DC voltage application, cluster beam, thermionic cathode mode or the like. Also for sputtering, a proper choice may be made of various sputtering modes including DC magnetron, bipolar DC, and RF sputtering. One illustrative dry plating method of forming silver alloy thin films is by providing a plurality of vapor sources which can be independently heated in a dry plating enclosure, and controlledly heating the respective vapor sources to evaporate different metals at desired rates for the alloy composition. In the case of sputtering, an alloy thin film may be formed using an alloy target or a plurality of different targets. For continuously forming thin films on the synthetic resin inner tubes by dry plating, any desired sputtering method may be employed, for example, coaxial sputtering, and two or four side opposed sputtering. In the case of sputtering, plating efficiency can be improved by providing permanent magnets or electromagnets to establish a magnetic field transverse to the electric field on the target surface. In the case of ion plating, an object to be treated, that is, an inner tube is usually traversed above a plating source because it is difficult to place the plating source above the object to be treated. The steps of pretreatment and dry plating on the outer peripheral surface of the resinous inner tube are preferably made consecutive for efficient production. For example, an inner tube is introduced through a differential evacuation system into a vacuum chamber where a surface treatment is carried out by a vacuum plasma or the like followed by dry plating of silver or silver alloy thin film. The low permeable rubber hose is fabricated by forming a silver or silver alloy thin film on the outer periphery of the resinous inner tube, applying an adhesive thereto e.g. in a conventional manner, and applying a rubber layer thereto. Adhesive The adhesive used herein may be selected from those adhesives well known to form a bond between rubber and metal. Examples include isocyanate adhesives, phenol resin adhesives, adhesives based on chlorinated rubber derivatives, cyclized rubber adhesives, rubber latex/protein adhesives, and resorcin-formalin-rubber latex adhesives. The silver or silver alloy thin film may preferably be primed with a silane or titanate adhesive promoter prior to application of the adhesive because a consistent adhesive bond is accomplished. Preferred among the above-mentioned adhesives are organic solvent system adhesives, for example, isocyanate adhesives such as triphenylmethane triisocyanate commercially available as Desmodur R® (Bayer A.G.) and diphenylmethane diisocyanate commercially available as Vulcabond TX® (I.C.I. Co.), a mixture of chlorinated rubber and a nitroso compound commercially available as Chemlok - 220® (Durham Chemical) and Thixon - 511® (Dayton Chemical), and a mixture of an alkyl-modified phenol resin and nitrile rubber. Also useful are aqueous dispersive adhesives, for example, a mixture of a resorcin-formalin precondensate and a rubber latex as well as those described in Japanese Patent Publication No. 24567/1974 and Japanese Patent Application Kokai No. 113882/1985. Preferred examples of the silane adhesive promoters include γ-glycidoxypropyltrimethoxysilane, γ-mercaptopropyltrimethoxysilane, γ-aminopropyltriethoxysilane, γ-methacryloxypropyltrimethoxysilane, and vinyltriethoxysilane. Preferred examples of the titanate adhesive promoters include tetrabutyl titanate and tetraisopropyl titanate. Rubber Layer The rubber compound used to form the rubber layer may be natural rubber or a synthetic rubber having a carbon-to-carbon double bond in its structural formula, alone or as a blend of two or more rubbers. Examples of synthetic rubbers usable herein include homopolymers of conjugated dienes such as isoprene, butadiene, and chloroprene, for example, polyisoprene rubber, polybutadiene rubber, and polychloroprene rubber; copolymers of the conjugated dienes with vinyl compounds such as styrene, acrylonitrile, vinylpyridine, acrylic acid, methacrylic acid, alkyl acrylates, and alkyl methacrylates, for example, styrene-butadiene copolymer rubber, vinyl-pyridine-butadiene-styrene copolymer rubber, acrylonitrile-butadiene copolymer rubber, acrylic acid-butadiene copolymer rubber, methacrylic acid-butadiene copolymer rubber, methyl acrylate-butadiene copolymer rubber, and methyl methacrylate-butadiene copolymer rubber; copolymers of olefins such as ethylene, propylene and isobutylene with diene compounds, for example, isobutylene-isoprene copolymer rubber (IIR); copolymers of olefins with non-conjugated dienes (EPDM), for example, ethylene-propylene-cyclopentadiene terpolymers, ethylene-propylene-5-ethylidene-2-norbornene terpolymers, and ethylene-propylene-1,4-hexadiene terpolymers; polyalkenamers obtained by ring opening polymerization of cycloolefins, for example, polypentenamer; rubbers obtained by ring opening polymerization of oxysilane rings, for example, sulfur-vulcanizable polyepichlorohydrin rubber; and polypropylene oxide rubber. Halogenated products of the foregoing rubbers are also employable, for example, chlorinated isobutylene isobutylene-isoprene copolymer rubber (Cl-IIR) and brominated isobutylene-isoprene copolymer rubber (Br-IIR). Ring-opened polymers of norbornene may be used. Also useful are rubber blends, for example, blends of the foregoing rubbers with saturated elastomers such as epichlorohydrin rubber, hydrogenated nitrile rubber, polypropylene oxide rubber, and chlorosulfonated polyethylene. A rubber composition may be prepared by adding any desired additives to the rubber compound in accordance with an ordinary practice depending on a particular purpose and application intended for the rubber hose. Useful additives include fillers such as carbon black, silica, calcium carbonate, calcium sulfate, clay, diatomaceous earth, and mica; softeners such as mineral oils, vegetable oils, and synthetic plasticizers; vulcanization promoters such as stearic acid; antioxidants; crosslinking agents such as sulfur, and adhesion promoters such as cobalt salts. After the rubber composition is applied to the adhesive layer on the silver or silver alloy thin film on the inner tube, a braid may be applied for reinforcement and a rubber composition may be applied to form a jacket or sheath if desired. The resulting structure is then heated and pressurized in a conventional manner for vulcanization, accomplishing the formation of the rubber layer. To this end, either sulfur vulcanization or vulcanization with organic sulfur compounds such as dithio-dimorpholine and thiuram type vulcanization may be used. The equipment for use in vulcanization may be selected from pressurized can equipment, fluidized bed equipment, and lead and plastic-sheathed microwave curing equipment. The low permeable rubber hose may be fabricated in accordance with the prior art method for fabricating synthetic resin-rubber composite hoses except that a silver or silver alloy thin film forming step is added thereto. Referring to FIG. 2, a method for manufacturing the rubber hose is described. In step (1), a mandrel or core of rubber, iron or plastic material is uncoiled. Step (2) is to coat the mandrel with a resin in an even thin film form to form a resin tube. Step (3) is to form a silver or silver alloy thin film on the outer periphery of the resin tube. Step (4) is to apply an adhesive to the thin film, followed by drying in step (5). Step (6) is to extrude rubber to form a coaxial circular intermediate tube. Optional step (7) is to apply a braid of steel wire or organic fibers or cords onto the intermediate tube to form a reinforcing layer for reinforcement to withstand pressure and external forces. Optional step (8) is to extrude rubber thereon to form a sheath. Step (9) is to apply heat and pressure to the resulting structure for vulcanization. The mandrel is removed from the vulcanized hose in step (10). The completed hose is finally taken up on a reel in step (11). The low-permeability rubber hose may be fabricated in accordance with the conventional rubber hose manufacture method with a simple modification thereto by adding a silver or silver alloy thin film forming step (3) thereto. The existing rubber hose manufacture plant may be used without a substantial modification. Since a silver or silver alloy thin film having a barrier property is formed on the resinous inner tube and a rubber layer is formed on the thin film through an adhesive, the low permeability rubber hose exhibits good solvent resistance, organic gas impermeability, moisture resistance, water resistance, and chemical resistance without a loss of the softness of rubber hose. It also possesses good fatigue resistance and durability against strains caused by bending and twisting forces. Because of the good organic solvent resistance, organic gas impermeability, and moisture impermeability as well as maintained softness, the low permeable rubber hose finds a wide variety of uses as household hoses, hoses in fuel transfer, torque converter, power steering, and air conditioning systems of automobiles, hoses for refrigerant fluid transfer in air conditioners and refrigerators, natural and propane gas transfer hoses, hydraulic hoses, and rubber couplings. EXAMPLE Examples of the present invention are given below by way of illustration and not by way of limitation. Example 1 A low permeable rubber hose exemplifying the invention was manufactured following the procedure shown in FIG. 2. A mandrel was coated with a nylon 6/66 copolymer resin to a thickness of 50 µm and then introduced into a vacuum chamber through a differential evacuation system. The resin tube was surface treated by a vacuum plasma. The resin tube was then coated with a silver film to a thickness of 1,000 Å by magnetron sputtering. The silver-coated resin tube on the mandrel was moved back to the ambient atmosphere through the differential evacuation system. The metallized tube was then coated with a dilute solution of γ-glycidoxypropyltrimethoxysilane and then with an isocyanate adhesive, Desmodur R (registered trade mark, Bayer A.G.). After drying, a rubber composition having the formulation shown in Table 1 was extruded on the tube to a thickness of 2 mm. A reinforcing fiber layer 1 mm thick was braided on the rubber layer and a rubber composition having the same formulation was again extruded to form a sheath having a thickness of 1.5 mm. The structure was vulcanized at 145°C for 40 minutes. Ingredients Parts by weight Natural rubber 85 Styrene-butadiene rubber 15 Carbon black (FEF) 45 Mineral oil 5 Antioxidant 0.7 Stearic acid 0.5 Zinc oxide 5 Vulcanization accelerator 0.8 Sulfur 2 For comparison purposes, a rubber hose designated Comparative Hose (1) was manufactured by the same procedure as above except that the dry plating step was omitted, that is, the silver film was not formed. Another rubber hose designated Comparative Hose (2) was manufactured by the same procedure as above except that an aluminum film was formed by dry plating (and adhesive was applied). Rubber hose samples were measured for Freon permeability and moisture permeability. The Freon permeability is expressed by the quantity (gram/m) of Freon 12 dissipated or volatilized from within the hose at 100°C for 72 hours. The moisture permeability is expressed by the quantity (gram/m) of moisture absorbed in the hose at 60°C and RH 95% for 72 hours. Further the quantities of permeating Freon and moisture were also measured under bent conditions where the hoses were bent at a radius of 200 mm, 100 mm, and 50 mm. The results are shown in Table 2. Hose belnding radius (mm) Strain (%) Example 1 Comparative hose (1) Comparative hose (2) Ag thin film No Ag film Al thin film Freon permeation (g/m) at 100°C/72 hours no 0 0.9 1.8 1.5 200 2.5 0.9 1.8 1.5 100 5.0 0.9 1.8 1.7 50 10.0 1.0 1.8 1.8 Moisture permeation (g/m)at 60°C/RH95%/72 hours no 0 0.3 3.0 1.5 200 2.5 0.3 3.0 1.6 100 5.0 0.3 3.0 1.9 50 10.0 0.4 3.0 2.3 As is evident from Table 2, when straight the rubber hose having a silver thin film showed better impermeability against Freon and moisture than the hose without a silver thin film and the hose having an aluminum thin film. In bent form, the hose having an aluminum thin film showed increasing Freon and moisture permeability as the bending radius was reduced (i.e. strain was increased). In contrast, the hose having a silver thin film showed little change in Freon and moisture permeability even when the bending radius was reduced. At the end of measurement, the hoses were sectioned for observing the inner surface under a microscope. In the hose having an aluminum thin film, the aluminum film contained narrow cracks, which caused a loss of barrier property. No cracks were observed in the silver films of straight and bent hoses. The rubber hose embodying the invention, which could maintain barrier property even at angular bends, satisfied the requirements for automobile air conditioner hoses. Example 2 A rubber hose was manufactured by the same procedure as in Example 1 except that the rubber composition coated on the silver thin film was changed to a nitrile rubber composition as shown in Table 3. Ingredients Parts by weight NBR (acryl nitrile content 35%) 100 Liquid NBR 10 Carbon black (SRF) 100 Antioxidant 1 Stearic acid 0.5 Zinc oxide 1 Vulcanization accelerator 2 Vulcanization accelerator 0.5 Sulfur 2 For performance evaluation, the hose was subjected to a gas permeation test (gas leakage test) and an impulse test. The impulse test was a hydraulic pressure test in which the hose was charged with MIL 5606 oil at 100°C and alternately pressurized to internal pressures of 0 and 30 kg/cm² by means of a pump. The test included 150,000 cycles at a rate of 45 cycles/min. At the end of the test, the hose was disintegrated to examine any damage on the interior wall. In the Freon permeation test, the rubber hose allowed only 1 gram of Freon 12 gas to permeate through during 72 hours at 100°C. In a vacuum test in which the hose interior was evacuated to a vacuum of 20 kPa (150 mmHg), it withstood the test without a separation between the nylon inner tube and the intermediate nitrile rubber layer. It also withstood the impulse test over 150,000 cycles. The following reference examples illustrate the moisture resistance and Freon 12 permeation of synthetic resin/dry plated thin film laminates. Reference Example 1 Disks having a diameter of 70 mm were cut from a nylon 6/66 copolymer film of 50 µm thick (manufactured by Ube Kosan K.K.). The film disk surfaces were degreased with solvent. The disks were rested on a substrate holder in a magnetron sputtering apparatus. The chamber was evacuated to a vacuum of less than 1.3 mPa (10⁻⁵ Torr) and then adjusted to a vacuum of 13 Pa (0.1 Torr) by admitting a minor amount of argon gas. Then the film surface was cleaned by RF glow discharge at 13.56 MHz. After cleaning, the RF glow discharge was ceased. With a DC voltage of -600 V applied to the metal target, sputtering was carried out in argon gas at a target current of 0.5 A, depositing a metal thin film on the film surface. The metals deposited were silver and aluminum, each to a thickness of 1,000 Å . The film disks, with and without metal thin films formed thereon, were examined for moisture resistance by a moisture permeation cup test under strains of 0, 3, 7 and 13%. The test was carried out by sealing a silica-gel-containing cup with the film disk, maintaining the cup at a temperature of 50°C and a humidity of RH 90%, and measuring a weight gain of the silica gel in the cup, the weight gain being expressed in %. The results are shown in Table 4. Strain (%) No metal film (%) Ag thin film 1000 Å (%) Al thin film 1000 Å (%) 0 8.8 0.5 3.0 3 8.8 0.8 3.5 7 8.7 1.0 4.2 13 8.9 1.3 7.0 As seen from Table 4, moisture resistance was improved by dry coating plastic film with metal thin film. The silver coated plastic film showed improved moisture resistance and maintained it upon application of strains, as compared with the aluminum coated plastic film. Reference Example 2 The plastic film used was a nylon 12 film 100 µm thick (manufactured by Ube Kosan K.K.). As in Reference Example 1, silver and aluminum were deposited on the film disks to a thickness of 1,000 Å. The film disks, with and without metal thin films formed thereon, were examined for Freon 12 permeation at 100°C by a gas permeation tester (manufactured by Yanagimoto K.K.) under strains of 0, 3, 7 and 13%. The results are shown in Table 5. The amount of Freon 12 permeated is expressed in units of x 10⁻⁴cm³/cm² per hour (x 10³mm³/m² per hour) Strain (%) No metal film Ag thin film 1000 Å Al thin film 1000 Å 0 25 1 3 3 25 1 5 7 25 1 9 13 25 1.5 15 As seen from Table 5, Freon 12 barrier property was improved by dry coating nylon 12 film with metal thin film. The silver coated plastic film showed Freon impermeability about 25 times better than the control film. Upon application of strains, the aluminum coated plastic film showed increasing permeation in proportion of strain. In contrast, the silver coated plastic film maintained barrier property substantially unchanged upon application of strains, while its barrier property was markedly improved over the aluminum coated and uncoated plastic films. Although some preferred embodiments have been described, many modifications and variations may be made thereto in the light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described.

Claims: A rubber hose comprising: a inner tube of a synthetic resin, having an outer surface, a thin film of silver or silver alloy on the outer surface of said inner tube, and a rubber layer heat-cured onto the thin film through an adhesive layer. A rubber hose according to claim 1 in which the thin film is from 10Å to 10µm thick. A rubber hose according to claim 2 in which the thin film is from 50Å to 1µm thick. A rubber hose of claim 1, claim 2 or claim 3 in which the inner tube is from 5 to 300µm thick. A rubber hose according to any one of the preceding claims in which the synthetic resin of the inner tube is a polyester, nylon, polyamide, polyether, polysulphone, polyimide, polycarbonate, fluororesin or a blend of two or more of these, or a blend of one of these with a polyolefin or with an elastomer. A rubber hose according to claim 5 in which the synthetic resin is polyethylene, polypropylene or polybutylene-1 polyallylate, polyethylene terephthalate, polybutylene terephthalate, polyoxybenzoyl; nylon 6, nylon 66, nylon 11, nylon 12, nylon 4, nylon 6/66, nylon 6/10, nylon 6/12; aromatic polyamide; polyacetal, polyphenylene oxide, polyetheretherketone, polyphenylene sulphide; polysulphone, polyether sulphone; polyether imide, polyamide imide, polybismaleimide; polyvinyl fluoride, polyvinylidene fluoride, polytrifluoro-monochloroethylene; or a said blend thereof. A rubber hose according to any one of claims 1 to 4 in which the synthetic resin of the inner tube is ethylene tetrafluoroethylene copolymer, hexafluoropropylene tetrafluoroethylene copolymer, perfluoroalkoxytetrafluoroethylene copolymer, thermoplastic urethane, polyvinyl chloride, polyvinylidene chloride, vinyl chloride/vinylidene chloride copolymer, crosslinked vinyl chloride resin, silicone resin, polyurethane, or a blend of one of these with a polyolefin or with an elastomer. A rubber hose according to any one of the preceding claims in which the thin film comprises silver alloy containing more than 50wt% silver. A rubber hose according to claim 8 in which the silver alloy contains more than 80wt% silver. A rubber hose according to claim 8 or claim 9 in which the silver alloy is an Ag-Au, Ag-Cu, Ag-Zn, Ag-Sb or Ag-Cd alloy. A rubber hose according to any one of the preceding claims in which the adhesive layer is of an isocyanate adhesive, phenol resin adhesive, chlorinated rubber derivative-based adhesive, cyclised rubber adhesive, rubber latex/protein adhesive or resorcin-formalin-rubber latex adhesive. A method of making a rubber hose as defined in any one of claims 1 to 11, comprising providing the inner tube of synthetic resin; forming the thin film of silver or silver alloy on the outer surface of the inner tube; applying the adhesive layer to the thin film, and heat-curing the rubber layer to the thin film through the adhesive layer. A method according to claim 12 in which, before the thin film is formed thereon, the outer surface of the inner tube is given a wet or dry pretreatment to activate it. A method according to claim 12 or claim 13 in which the thin film is formed on the inner tube by dry plating. A method according to any one of claims 12 to 14 in which the thin film is primed with a silane or titanate adhesive promoter before the adhesive layer is applied.

Inventors: FUKUURA YUKIO, NAITO KAZUO, NIWA HIDEYUKI, YOSHIKAWA MASATO, FUKUURA, YUKIO, NAITO, KAZUO, NIWA, HIDEYUKI, YOSHIKAWA, MASATO
Applicants: BRIDGESTONE CORP, BRIDGESTONE CORPORATION
Application year: 1991
Main classification: F16L59
IPC codes: B32B15, F16L11, B29D23, B32B1