Multifunctional reactive polymeric diluent

Abstract: The present invention is directed to a reactive diluent comprising a backbone portion and a pendant group portion. The backbone portion comprises at least two polymerizable sites, and the pendant group portion comprising a functional group having the following formula: wherein Z is an ethylenically unsaturated hydrocarbyl or substituted hydrocarbyl group containing from 2 to about 12 carbon atoms and wherein said pendant group is capable of a (2 + 2) cyclo-addition with another like pendant group of the above formula. The chain extending reaction site is preferably used in a polymerization reaction to provide a polymeric material, and the cross-linking reactive site is preferably used to create cross-linking as needed or desired.

Description: Field of The Invention The present invention relates generally to a class of reactive diluents useful in networking together macromolecules to provide polymeric compositions having a precise cross-linked structure. More specifically, the multifunctional reactive diluents of the present invention preferably comprise a cross-linking reactive site and more than one chain extending reactive site. The chain extending reaction site is preferably used in a polymerization reaction, and the cross-linking reactive site is preferably used to create cross-linking as needed or desired. Background of the Invention Maleic anhydride is a readily available bulk chemical used in the manufacture of numerous chemical products, such as certain polyester resins, pesticides and preservatives. Maleic anhydride can be used as a reagent in the synthesis of dimethylmaleic anhydride (DMMA) according to the following reaction: DMMA is a useful material, because it can be reacted with an aliphatic or aromatic primary amine to provide N-substituted dimethylmaleimides (DMMI) in high yield. DMMIs are known to be photochemically reactive when irradiated with light of suitable wavelength, typically about 350-430 nanometers (a conventional photo-sensitizer is also often added). When photochemically reacted, the DMMIs typically dimerize in a (2+2) cyclo-addition mode to give substituted cyclobutane derivatives as illustrated in FIGURE 3. The R group of the DMMI molecule shown in Figure 2 can contain a reaction site which is used in a polymerization reaction, and the polymerized material is then typically cross-linked by the photo-reaction cyclo-addition as illustrated in FIGURE 3 above. DMMI monomers are generally synthesized by reacting DMMA with a primary amino-alcohol (NH₂-R-OH wherein R can be virtually any aliphatic or aromatic group) to give an intermediate DMMI-alcohol. The DMMI-alcohol is typically esterified with methacrylic acid and the water by-product is generally removed under azeotropic conditions as illustrated in FIGURE 4. The DMMI-monomer is usually copolymerized with one or more ethylenically unsaturated comonomers in solution with radical initiators such as AIBN (Azo-bisisobutyronitrile) to yield soluble DMMI-copolymers with statistical distribution of the monomer units within the macromolecule. Once the polymer backbone is synthesized, the resulting polymer typically comprises only one readily reactive functional group--the pendant DMMI groups. These groups can be dimerized or reacted together using ultra violet light (and typically also a UV sensitizer) such as is illustrated in FIGURE 3, thereby cross-linking the polymers. Such DMMI polymeric systems are generally advantageous, because the tetrasubstituted carbon-carbon double bond of the DMMI typically does not participate to any extent in the free radical polymerization reaction used to prepare the DMMI containing polymer. Most other known photosensitive functional groups will typically enter into a polymerization reaction, typically causing unwanted gelling and the like. However, synthesizing the polymer backbone is generally not a simple reaction and is oftentimes difficult to perform on an industrial scale. Furthermore, the resulting polymer with DMMI functionality is generally not readily susceptible to variations in cross-linking, and oftentimes a more complex cross-linked network is necessary to achieve desired properties. "DMMI-Photopolymers and Their Technical Application" by M. Roth and B. Muller, Ciba-Geigy AG, is a publication describing DMMI synthesis, DMMI polymer synthesis and cross-linking DMMI polymers by photoreacting the DMMI groups. "A New Class Of Photopolymers With Pendant Dimethylmaleimide Groups- Part I", Die Angewandte Makromolekulare Chemie 128 (1984) 71-97 by Juergen Finter, Edward Widmer, and Hans Zweifel and "A New Class Of Photopolymers With Pendant Dimethylmaleimide Groups- Part II", Die Angewandte Makromolekulare Chemie 133 (1985) 147-170, by Jurgen Finter, Zeppos Haniotis, Friedrich Lohse, Kurt Meier, and Hans Zweifel, are articles which discuss and describe DMMI chemistry. U.S.-A-4,107,174 to Baumann et al. entitled "Imidyl Compounds" is directed to photoreactive imidyl compounds, such as DMMI and is also directed to polymeric imidyl compounds which are photocross-linkable. U.S.-A-4,174,326 to Baumann et al. is also entitled "Imidyl Compounds" and is a divisional of US-A-4,107,174. CH-A-601 364 discloses photochemically curable polymer systems containing substituted maleimide groups. These polymers are derived from difunctional reactive compounds. None of the above-identified prior art is directed to a multifunctional diluent having more than two polymerization sites and which can be advantageously used to provide a quick, simple and easy means to precisely network together diverse functional materials. Objects of the Invention It is an object of the present invention to provide a multifunctional reactive diluent which allows for simple and reliable networking together of dissimilar monomers, macromers or the like. A further object of the present invention is to provide tight polymer networks by means of low molecular weight diluents which are wholly or partially photo-reactive. Other objects and features of the present invention will become apparent to those of ordinary skill upon further reading of this specification and accompanying claims. Summary of the Invention The present invention is directed to a reactive multifunctional diluent comprising the following formula: wherein X₁ and X₂ are organic reactive sites selected from the group consisting essentially of OH, NHR, COOH, SH, H₂C=CH-, Cl and Br with proviso that only one of X₁ or X₂ my be OH; m and n are the same or different and are 0 or 1; R₁ and R₂ are the same or different and represent any organic substituent selected to optimize the properties of said multifunctional monomer depending upon its desired end use while not adversely affecting the reactivity of X₁ or X₂ or the properties of said multifunctional monomer; R and R₃ may be H or any organic substituent selected to optimize the properties of said multifunctional monomer depending upon its desired end use while not adversely affecting the reactivity of X₁ or X₂ or the properties of said multifunctional monomer; and Z is an ethylenically unsaturated hydrocarbyl group wherein at least one alkyl group is bonded to a carbon of the ethylenically unsaturated group and wherein said hydrocarbyl group totals from 3 to 12 carbon atoms and wherein said ethylenically unsaturated group is capable of undergoing a 2+2 cyclo-addition reaction with another like group. The chain extending reaction site is preferably used as part of a polymerization reaction to provide polymeric material, and the cross-linking reactive site is preferably used to create cross-linking as needed or desired. Detailed Description of the Preferred Embodiment The present invention is directed to multifunctional reactive diluents preferably for use with thermoplastic polymeric materials. "Polymeric materials" as used herein is intended to include polymers, oligomers, macromers and monomers. The thermoplastic polymeric materials are preferably converted to thermosetting polymeric materials due in whole or in part to cross-linking via the reactive diluent. The diluent is preferably a low molecular weight material. The preferred material has a molecular weight less than 1000 and most preferably less than 800. The low molecular weight is advantageous in allowing the interdispersing or intermixing of the diluent within a polymeric reagent system prior to or during polymerization. Where the reactive diluent of the present invention has a high molecular weight, such as greater than 5000, a conventional reactive diluent or solvent can be used to aid intermixing and/or lower viscosity. The reactive diluents of the present invention may be synthesized by a variety of methods known to those of ordinary skill in the art. The reactive diluent of the present invention is preferably formed in a series of reaction steps. In a preferred embodiment, a first intermediate having a 2+2 cyclo-addition reaction site is reacted with a second intermediate preferably having a free radical polymerizable reaction site. The reaction product (the reactive diluent) preferably retains both the 2+2 cyclo-addition reaction site of the first intermediate and also the free radically polymerizable reaction sites of the second intermediate. A preferred intermediate having a 2+2 cyclo-addition reaction site is a polyol having a DMMI pendant group. A preferred second intermediate is an acrylate or methacrylate ester, and the reaction is preferably conducted in an organic solvent (active hydrogen solvents are generally not preferred), preferably in the presence of a catalyst, such as a transesterification catalyst. A free radial polymerization site is not critical to the present invention and other reaction sites are certainly possible, such as a condensation polymerization site or the like. What is critical to the present invention is an end-product comprising a backbone portion having two or more reaction sites and a pendant group portion having a 2+2 cyclo-addition site, such as: wherein X₁ and X₂ can be the same or different and comprise organic reactive sites, such as OH, NHR, SH, -CH=CH- or (meth)acrylic. [The advantages and disadvantages of any particular organic reactive site are well understood in the art, but ordinary skill and experimentation may be necessary in determining the optimal reactive site for any particular application of the present invention.] m and n can be the same or different and are either 0 or 1. R₁, R₂ and R₃ can be the same or different and can be any organic substituent, such as substituted or unsubstituted (hetero)alkyl or aryl. If R₁, R₂ or R₃ is aromatic, it will generally improve the photospeed of the photocuring pendant member material. If R₁, R₂ or R₃ comprises a urethane, ether or ester linkage, this will generally increase the flexibility of the material. If R₁, R₂ or R₃ comprise a polyarylene, this will generally add to the rigidity of the material. If R₁, R₂ or R₃ is aliphatic, this will generally add to the environmental stability of the material. R₁, R₂ or R₃ can also be chosen to adjust the organic polarity of the material, and this could aid in the miscibility of material with other organic materials. In short, ordinary skill and experimentation may be necessary to determine the optimal R₁ R₂ or R₃ depending upon the intended end use and desired properties. Z is an ethylenically unsaturated hydrocarbyl or substituted hydrocarbyl group containing from 2 to 12 carbon atoms and is alkyl or cyclic alkyl, whereby the pendant group is capable of a (2+2) cyclo-addition with another like pendant group of the above formula. It is contemplated that the diluent of the present invention will be polymerized in conjunction with any one of a number of monomers, oligomers, macromers or prepolymers, wherein the reactive sites of the diluent backbone will copolymerize with other polymeric reagents to provide a polymeric material comprising the diluent of the present invention. The backbone portion of the preferred embodiment further comprises a photoreactive pendant group which preferably is substantially non-reactive during any polymerization reaction involving the polymer backbone. In other embodiments, the pendant group need not be photoreactive, and need not be substantially non-reactive during any polymerization reaction involving the polymer backbone, provided however that the pendant group is capable of reacting in a 2+2 cyclo-addition reaction. As described above, the preferred photocross-linking pendant group can be broadly defined as follows: wherein Z is an unsaturated divalent hydrocarbyl or substituted hydrocarbyl, aliphatic or cycloaliphatic group containing from 2 to 12 carbon atoms and capable of undergoing cross-linking with another group Z in a 2 + 2 cyclo-addition reaction. More preferred pendant groups are those of the following formula: wherein R₄ and R₅ may be the same or different, and each is hydrogen or a lower alkyl radical containing from 1 to 3 carbon atoms, or R₄ and R₅ may be joined together to form, together with the respective carbon atoms to which they are attached, a cyclic hydrocarbyl or substituted hydrocarbyl radical containing from 2 to 12 carbon atoms. The most preferred pendant group is dimethylmaleimide ("DMMI") having the following structure: The pendant group is bonded directly to the diluent backbone via the nitrogen atom, or alternatively the pendant group is linked to the polymer backbone through a short aliphatic chain containing carbon, hydrogen and optionally any hetero-organic such as oxygen and/or nitrogen. A preferred synthesis of the diluent of the present invention is illustrated in FIGURE 5 below. wherein R₁ and R₂ can be the same or different and are aliphatic and/or aromatic, preferably aliphatic, most preferably CH₂-CH₃, CH₃ or H and wherein X is OH, Br, Cl. Alternatively an α,β-unsaturated acyl halide may be reacted with a polyol having a DMMI pendant group. Generally, this reaction is run in an inert solvent in the presence of a quantity of tertiary amine or other base equimolar to the acyl halide. This synthesis is illustrated in FIGURE 6 below. Alternatively, the reactive diluent of the present invention can be synthesized using an isocyanate as the second intermediate. This alternative synthesis is illustrated in FIGURE 7. An alternative isocyanate based diluent is illustrated in FIGURE 8. The reactive diluent of the present invention can also be made by direct esterification, ester interchange or any other technique known to the art or derived by practitioners to make similar type materials. Ordinary skill and experimentation may be necessary in synthesizing a particular diluent in accordance with the present invention. The reactive diluents of the present invention are preferably incorporated into polymer systems comprising systems capable of undergoing 2+2 cyclo-addition, and the resulting network formation can be illustrated as shown in FIGURE 9. However, the vinyl group is not critical and any polymerizable site is possible such as any free radical polymerization site or a condensation polymerization site. Also, the DMMI pendant group is not critical and any pendant reactive group is possible provided it is capable of reacting in a 2 + 2 cyclo-addition reaction. EXAMPLES Example 1 The efficacy of the present invention has been demonstrated using: 1. a dimethylmaleimide modified polyurethane (PU); 2. a triacrylate reactive diluent, trimethylolpropane triacrylate (TA); and 3. a methacrylate version of the multifunction reactive diluent of the present invention (MRD) having the following structure: The following table shows the sample compositions and their evaluation by % area swell in tetrahydrofuran after UV curing. Sample Composition (wt. %) % Area Swell 100% PU 21 75% TPU/25% MRD 10 75% TPU/25% TA 21 75% TPU/12.5% TA-1/12.5% MRD 10.25 As can be seen by the data provided in Example 1, pure polyurethane (PU) shows 21 % area swell. By incorporating a 25% multi-functional reactive diluent (MRD) of the present invention, a much tighter cross-linked network is formed, resulting in a much lower % area swell value (10%). The mixture of polyurethane (PU) and a conventional diluent triacrylate (TA) results in two cross-linked polymers intermixed but not connected. Therefore since the PU is in the majority, it predominates, and the % area swell is the same as pure PU. However, the 3 component system, comprising polyurethane (PU), the conventional diluent triacrylate (TA) and the multi-functional reactive diluent (MRD) of the present invention, shows that the dual functional reactive diluent allows all the components to be incorporated into a single tightly cross-linked network, resulting in the lower swell reading of 10.25. Consequently, the dual functional reactive diluent of the present invention provides a means for obtaining a tightly cross-linked polymer network, either as the sole cross-linking agent or in combination with a conventional cross-linking agent, such as a conventional multifunctional diluent, most preferred (meth)acrylate functional reactive diluent.

Claims: A reactive multifunctional diluent comprising the following formula: wherein X₁ and X₂ are organic reactive sites selected from the group consisting essentially of OH, NHR, COOH, SH, H₂C=CH-, Cl and Br with proviso that only one of X₁ or X₂ may be OH; m and n are the same or different and are 0 or 1; R₁ and R₂ are the same or different and represent any organic substituent selected to optimize the properties of said multifunctional monomer depending upon its desired end use while not adversely affecting the reactivity of X₁ or X₂ or the properties of said multifunctional monomer; R and R₃ may be H or any organic substituent selected to optimize the properties of said multifunctional monomer depending upon its desired end use while not adversely affecting the reactivity of X₁ or X₂ or the properties of said multifunctional monomer; and Z is an ethylenically unsaturated hydrocarbyl group wherein at least one alkyl group is bonded to a carbon of the ethylenically unsaturated group and wherein said hydrocarbyl group totals from 3 to 12 carbon atoms and wherein said ethylenically unsaturated group is capable of undergoing a 2+2 cyclo-addition reaction with another like group. The diluent of Claim 1 wherein the pendant group is further defined as comprising a functional group having the following formula: wherein R₄ and R₅ are the same or different and are lower alkyl containing from 1 to 3 carbon atoms. The diluent of Claim 2 wherein R₄ and R₅ are further defined as each being methyl. The diluent of anyone of Claims 1 to 3 wherein the reactive sites for the backbone portion are further defined as comprising amine, hydroxyl, carbonyl or vinyl functionality. The diluent of Claim 4 wherein the reaction sites are further defined as comprising vinyl functionality. The diluent of Claim 5 being further defined by the following formula: wherein R₁, R₂, R₃, R₄ and R₅ can be the same or different and are either -H, -CH₃ or -CH₂CH₃. A polymeric material comprising the reaction product of the following: (1) a polymeric material comprising a pendant group having the following formula: (2) a reactive material having the following formula: wherein R₁ aromatic or aliphatic and R₂ is either -H or -CH₃ and m is 1, 2, 3, or 4; and (3) a diluent having the following formula: wherein R₁, R₂ and R₃ can be the same or different and are either -H, -CH₃ or -CH₂CH₃.

Inventors: FARKAS JULIUS, JULIAN GARY LEE, LONG II CARL JOSEPH, MASLER III WILLIAM FRANK, WILBUR WILLIAM ROBERT, FARKAS, JULIUS, JULIAN, GARY LEE, LONG II, CARL JOSEPH, MASLER III, WILLIAM FRANK, WILBUR, WILLIAM ROBERT
Applicants: GOODRICH CO B F, THE B.F. GOODRICH COMPANY
Application year: 1991
Main classification: C08F8
IPC codes: C08G69, C08G18, C08F20, C08F8, C08F220