Water soluble algin fibers and production thereof

Abstract: There is disclosed water soluble algin fibers and such fibers which have antibiotics immobilized thereby. The water soluble algin fibers are produced by extruding an aqueous dope which contains water soluble algin into a large quantity of a hydrophilic organic solvent exemplified by acetone. The water soluble algin fibers which have antibiotic immobilized thereby are produced in the same manner by using a dope containing antibiotic.

Description: This invention relates to water soluble algin fibers and such fibers which have antibiotics immobilized thereby, and production thereof. Water insoluble algin fibers have been produced by spinning or extruding water soluble algin solutions into a coagulating bath which is composed of an aqueous solution of multivalent metal ions. When a coagulating bath contains copper or calcium ions, water insoluble copper or calcium algin fibers are obtained, respectively, as disclosed in JP-A-56-169809, EP-A-0 040 048 or US-A-3,446,625. The alginates have haemostatic properties, and therefore fabrics of such algin fibers are used as swabs or dressings and the like suitable for medical, surgical and other purposes. There are disclosed in GB-A-1,231,506 water solubilized calcium/sodium alginate fibers which are produced by acidifying water insoluble calcium alginate fibers and then treating the acidified fibers with an alcoholic solution of sodium hydroxide. Also in EP-A-0 040 048, there is disclosed a process for the production of nonwoven fabrics of calcium/sodium alginate fibers by acidifying calcium alginate fibers with acetic acid to displace in part calcium ions with sodium ions and then treating the fibers with an alcoholic solution of sodium acetate. There is further disclosed in JP-B-27720/1989 a process wherein water insoluble calcium alginate is extruded into a coagulating bath together with enzymes or microorganisms to produce water insoluble alginate fibers by which the enzymes or microorganisms are immobilized and which are useful as a bioreactor. As above described, water insoluble alginate fibers are already known. It is also known that an alginate powder is obtained by adding hydrophilic organic solvent to an aqueous solution of water soluble algin. The production of an alginate film by extruding a soluble alginate into a water-miscible solvent is disclosed in Handbook of Water-Soluble Gums & Resins, Robert L. Davidson , McGraw-hill, New York. However no process has hitherto been known for the production of substantially water soluble algin fibers on account of the high solubility of sodium alginate in water in contrast to calcium alginate which is very slightly soluble in water. The present invention provides water soluble algin fiber wherein the water soluble algin is inorganic salts such as sodium, lithium, potassium, magnesium and ammonium salts, organic amine salts such as triethanol amine salt, and organic esters such as propylene glycol alginate. The water soluble algin may contain different types of salt structures in the molecule, and it also may be a single material or a mixture of two or more (e.g. of the above materials). The invention also provides a method of producing water soluble algin fiber which comprises extruding an aqueous dope containing water soluble algin as defined above into hydrophilic organic solvent; the method preferably involves extrusion of an aqueous spinning solution of water soluble algin or a dope into a coagulating bath of a large quantity of hydrophilic organic solvent in which the water soluble algin is substantially insoluble and the prompt displacement of the water in the dope with the solvent to provide successfully continuous filaments of the water soluble algin. Among the above water soluble algins, sodium alginate is preferred since it provides fibers of high mechanical strength. The potassium salt or propylene glycol ester is preferably used together with the sodium alginate. The water soluble algin fibers are produced in accordance with the invention by extruding an aqueous solution of the water soluble algin or a dope into a coagulating bath of hydrophilic organic solvent. The aqueous dope preferably contains the water soluble algin in an amount of 3-20 %, more preferably 5-10 %, by weight. When the concentration of the water soluble algin in the dope is too small, coagulation and formation of filaments of algin may not take place when the dope is extruded into a coagulating bath. The best organic solvents for the coagulating bath in the invention are hydrophilic and low molecular weight organic solvents in which the water soluble algin is substantially insoluble or only slightly soluble so that the water in the aqueous dope is promptly displaced when the dope is extruded into the coagulating bath and filaments of the water soluble algin are continuously formed. Namely, when the dope is extruded into the coagulating bath, the water in the dope is promptly diffused into the solvent so that the aqueous dope is promptly dehydrated to form continuous filaments of the water soluble algin. The use of a hydrophobic solvent causes no dehydration of the dope and fails to provide the continuous filaments of the water soluble algin. The use of a large molecular weight and hence high viscosity solvent by also fail to provide continuous filaments of the water soluble algin if the dope is very slowly or insufficiently dehydrated in such a bath. Further, a hydrophilic solvent having a large number of hydroxyl groups in the molecule may not be suitable for the coagulating bath in the invention if it has such a large affinity with the water soluble algin that the dope is not readily dehydrated. Preferred hydrophilic organic solvent include, for instance, lower aliphatic alcohols having 1-3 carbons (e.g. methanol, ethanol isopropanol), acetone, dioxane, ethylene glycol monomethyl ether, dimethyl sulfoxide, dimethylformamide, dimethylacetamide, acetonitrile, methyl ethyl ketone and phenol. These solvents may be used singly or as a mixture. Among these solvents, methanol, ethanol or acetone is preferred, and acetone is most preferred since it provides water soluble algin fibers of high mechanical strength. Other solvent such as methyl ethyl ketone, ethylene glycol monomethyl ether or dimethyl sulfoxide is used preferably together with acetone. The coagulating bath inevitably contains water to an extent since aqueous dope is extruded thereinto. Therefore, the bath is allowed to contain water to an extent, though desirably as little as possible. It is of course necessary that the amount of water in the bath is such that the aqueous dope extruded thereinto forms continuous filaments in the bath. The allowed amount of water in the bath depends upon the solvent used and other conditions under which the dope is extruded thereinto. However, it is usually desirable that the bath contains a solvent in an amount of not less than 50 % by weight, preferably not less than 70 % by weight, more preferably not less than 80 % by weight. It is most preferred, as hereinabove set forth, that the bath contains water in an amount as small as possible. When the bath contains water in too large an amount, it may be difficult to obtain continuous filaments of the water soluble algin. From the practical standpoint, the coagulating bath is preferably controlled to contain water in a substantially constant and small amount by connecting the bath to solvent dehydration equipment or dehydrated solvent reservoir through a pump and piping to supply the bath with the dehydrated solvent continuously. The bath may be maintained at a temperature usually in the range of normal temperature to about 100°C, depending upon the solvent used other extrusion conditions. It is important in the invention to extrude an aqueous dope of the water soluble algin into a large quantity of such hydrophilic organic solvent as set out hereinbefore to displace the water in the dope with the solvent promptly, thereby to obtain continuous filaments of the water soluble algin. The diameter of nozzle openings from which the dope is extruded into the coagulating bath and the extrusion rate of the dope are important factors in optimum operation of the method of the invention. It is difficult to predetermine optimum nozzle diameter and and extrusion rate since a large number of factors are involved in a complicated manner, but suitable values are readily ascertained by trial. It is in general preferred to use a nozzle opening diameter of 0.025-1 mm and an extrusion rate of 0.001-1 ml per minute per nozzle. After the water soluble algin fibers are formed in the coagulating bath, they may be dehydrated with dehydrating solvent such as methanol, ethanol or acetone; suitably the fibers are immersed in the dehydrating solvent, and then air dried or heated. The water soluble algin fibers may be formed into nonwoven fabrics, for example, by a dry process such as a carding method. Water soluble algin fibers by which antibiotics are immobilized can be obtained by including antibiotic in the aqueous dope. Hydrophilic and cationic antibiotics are preferably used since they are efficiently immobilized by water soluble algin. Antibiotics for external application are preferably used. Such antibiotics include, for example, cephem antibiotics such as ceftizoxime or cefmenoxime; penicillin antibiotics such as benzylpenicillin, sulbenicillin, ampicillin or penicillin G; aminoglycoside antibiotics such as kanamycin, tobramycin, dibekacin, gentamycin, micronomycin, asomycin or fradiomycin; macrolide-lincomycin antibiotics such as erythromycin or kitasamycin; tetracycline antibiotics such as oxytetracycline, tetracycline or demethylchlortetracycline; antibacterial antibiotics such as colistin, polymyxin B, chrolamphenicol, micomycin, bacitracin, gramicidin S or fusidic acid; and antifungal substances such as amphotericin B, nystatin, trichomycin, pimaricin, variotin, pyrrolnitrin or saccanin. These antibiotics may be used singly or as a mixture. Antibiotics for injection use may also be used. The reason why the antibiotics are immobilized by water soluble algin has not yet been clarified, but it is likely as one aspect that carboxyl groups of the algin act as a medium for cation exchange, and cation exchange reaction between the antibiotic and the cation of the carboxyl groups such as sodium ion take place to combine or immobilize the antibiotic in and/or on the algin. Water soluble algin fibers which have antibiotics immobilized thereby may also be formed into nonwoven fabrics. Water soluble algin fibers by which antibiotics are immobilized may also be produced by first forming algin fibers and then immersing the fibers in a solution of antibiotic. The water soluble algin fibers of the invention may be used as swabs or dressings and the like suitable for medical and surgical purposes. In particular, the fibers which have antibiotics immobilized thereon and/or therein are antimicrobial, and thus can be used suitably as swabs or dressings on burned or scalded skin for prevention of suppuration. The invention is illustrated by the following Examples, but is not limited thereto. In the following Examples, the coagulating bath is composed of three liters of solvent. The fineness and strength of fibers are averages of three measurements, In the accompanying drawings: Fig. 1 shows absorbance at 562 nm of a dope containing polymyxin B and water soluble algin fibers produced from the dope and to which polymyxin B is immobilized in relation to the concentration of polymyxin B in the dope (see Examples 24-27); and Fig. 2 shows absorbance at 361 nm of a dope containing tetracycline and water soluble algin fibers produced from the dope and to which tetracycline is immobilized in relation to the concentration of tetracycline in the dope. (see Examples 28-31). Example 1 Sodium alginate was added to distilled water and stirred for about 4 hours to prepare a 5 % by weight aqueous solution. The solution was filtered through a 200 mesh filter cloth to prepare a dope. The dope was charged into continuous wet spinning machine and defoamed overnight under reduced pressure. The dope was extruded at a rate of 12 g per minute into a coagulating bath of varied solvents at 18°C through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled at a rate of 0.5 m per minute onto a godet roller. The fibers were immersed in acetone, excess acetone removed and the fibers dried at 100°C. The fineness and strength of the fibers are shown in Table 1. Coagulating Bath Fineness (denier) Strength (gf/denier) Methanol 5.463 0.236 Ethanol 4.734 0.250 Isopropanol 4.491 0.338 Acetone 4.410 0.312 Example 2 The same dope as in Example 1 was extruded into ethanol at varied temperatures at a rate of 12 g per minute through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 2. Coagulating Bath Temperature (°C) Fineness (denier) Strength (gf/denier) 15 1.42 0.348 25 1.40 0.336 35 1.30 0.343 45 1.42 0.292 55 1.45 0.247 Example 3 The same dope as in Example 1 was extruded into ethanol at 10°C at varied rates through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 3. Extrusion Rate (g/min.) Fineness (denier) Strength (gf/denier) 3.62 - - 7.95 - - 11.96 - - 16.42 1.43 0.239 20.77 1.81 0.300 Example 4 The same dope as in Example 1 was extruded into acetone at 10°C at varied rates through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 4. Extrusion Rate (g/min.) Fineness (denier) Strength (gf/denier) 3.62 - - 7.95 0.80 0.648 11.96 1.13 0.809 16.42 1.49 0.649 20.77 1.82 0.634 Example 5 The same dope as in Example 1 was extruded into acetone at 10°C at varied rates through a nozzle provided with 1000 openings each having a diameter of 0.055 mm. The resultant fibers were rolled at a rate of 5.7 m per minute onto a godet roller and dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 5. Extrusion Rate (g/min.) Fineness (denier) Strength (gf/denier) 3.62 0.40 0.812 7.95 0.76 0.718 11.96 1.13 0.506 16.42 1.45 0.511 20.77 2.07 0.316 Example 6 The same dope as in Example 1 was extruded into acetone at 10°C at a rate of 12 g per minute through a nozzle provided with openings of varied diameters. The resultant fibers were rolled at a rate of 4.3 m per minute onto a godet roller and dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 6. Opening Diameter (mm) Fineness (denier) Strength (gf/denier) 0.055 2.65 0.309 0.1 4.08 0.368 0.15 3.78 0.429 0.2 16.56 0.026 0.25 10.97 0.026 Example 7 The same dope as in Example 1 was extruded into ethanol at 10°C at a rate of 16 g per minute through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled at a rate of 5.7 m per minute onto a godet roller and then dried in the same manner as in Example 1 with use of varied dehydration solvents. The fineness and strength of the fibers are shown in Table 7. Dehydration Solvent Fineness (denier) Strength (gf/denier) Methanol 1.46 0.503 Ethanol 1.51 0.336 Acetone 1.47 0.280 Example 8 The same dope as in Example 1 was extruded into dimethylacetamide at 15°C at a rate of 16 g per minute through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled onto a godet roller and dried in the same manner as in Example 1. Example 9 The same dope as in Example 1 was extruded into acetonitrile at 15°C at a rate of 16 g per minute through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled onto a godet roller and dried in the same manner as in Example 1. Example 10 The same dope as in Example 1 was extruded into methyl ethyl ketone at 15°C at a rate of 16 g per minute through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled onto a godet roller and dried in the same manner as in Example 1. Example 11 The same dope as in Example 1 was extruded into phenol at 15°C at a rate of 16 g per minute through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled onto a godet roller and dried in the same manner as in Example 1. Example 12 The same dope as in Example 1 was extruded into acetone at 18°C at a rate of 16.4 g per minute through a nozzle provided with 1000 openings each having a diameter of 0.055 mm. The resultant fibers were rolled onto a godet roll of a diameter of 11.2 cm at varied rotation rates and dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Tabe 8 in relation to rotation rates of the godet roller. Rotation Rate (rpm) Fineness (denier) Strength (gf/denier) 2 - - 4 5.01 0.238 8 1.98 0.434 16 1.08 0.774 24 0.72 0.792 32 0.53 0.923 40 0.41 0.879 48 0.27 0.624 56 - - Example 13 The same dope as in Example 1 was extruded into acetone at 13°C at a rate of 16.4 g per minute through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled onto a godet roller of a diameter of 11.2 cm at varied rotation rates and dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 9. Rotation Rate (rpm) Fineness (denier) Strength (gf/denier) 2 - - 4 3.90 0.447 8 2.94 0.811 16 1.54 0.802 24 0.95 0.969 32 0.71 1.100 40 - - Example 14 The same dope as in Example 1 was extruded into ethanol at 17°C at a rate of 16.4 g per minute through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled onto a godet roller of a diameter of 11.2 cm at varied rotation rates and dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 10. Rotation Rate (rpm) Fineness (denier) Strength (gf/denier) 2 - - 4 3.95 0.112 8 2.22 0.080 16 1.20 0.151 24 0.74 0.132 32 - - Example 15 The same dope as in Example 1 was extruded into acetonitrile at 17°C at a rate of 16.4 g per minute through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled onto a godet roller of a diameter of 11.2 cm at varied rotation rates and dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 11. Rotation Rate (rpm) Fineness (denier) Strength (gf/denier) 2 - - 4 4.12 0.210 8 2.00 0.165 16 1.04 0.240 24 0.69 0.286 32 0.45 0.111 40 - - Example 16 The same dope as in Example 1 was extruded into dioxane at 17°C at a rate of 16.4 g per minute through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled onto a godet roller of a diameter of 11.2 cm at varied rotation rates and dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 12. Rotation Rate (rpm) Fineness (denier) Strength (gf/denier) 2 - - 4 4.75 0.413 8 2.30 0.326 16 1.18 0.461 24 0.81 0.415 32 0.56 0.371 40 - - Example 17 The same dope as in Example 1 was extruded into a mixture of acetone and methyl ethyl ketone at 17°C at a rate of 16.4 g per minute through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled onto a godet roller of a diameter of 11.2 cm at a rotation rate of 16 rpm and dried in the same manner as in Example 1. The fineness and strength of the fibers in relation to the volume ratio of acetone to methyl ethyl ketone are shown in Table 13. Volume Ratio Fineness (denier) Strength (gf/denier) 10/0 1.16 0.821 9/1 1.24 0.776 8/2 1.21 0.800 6/4 1.23 0.746 4/6 1.25 0.473 Example 18 Magnesium alginate was added to distilled water and stirred for about 4 hours to prepare a 5 % by weight aqueous solution. The solution was filtered through a 200 mesh filter cloth to prepare a dope. The dope was charged into continuous wet spinning machine and defoamed overnight under reduced pressure. The dope was extruded at a rate of 16.4 g per minute into acetone at 17°C through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled at varied rates onto a godet roller of a diameter of 11.2 cm. The fibers were dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 14. Rotation Rate (rpm) Fineness (denier) Strength (gf/denier) 4 - - 8 2.59 0.228 16 1.24 0.337 24 0.87 0.306 32 0.56 0.301 40 - - Example 19 Lithium alginate was added to distilled water and stirred for about 4 hours to prepare a 5 % by weight aqueous solution. The solution was filtered through a 200 mesh filter cloth to prepare a dope. The dope was charged into continuous wet spinning machine and defoamed overnight under reduced pressure. The dope was extruded at a rate of 16.4 g per minute into acetone at 18°C through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled at varied rates onto a godet roller of a diameter of 11.2 cm. The fibers were dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 15. Rotation Rate (rpm) Fineness (denier) Strength (gf/denier) 4 - - 8 3.41 0.265 16 1.61 0.157 24 1.09 0.278 32 - - Example 20 Ammoium alginate was added to distilled water and stirred for about 4 hours to prepare a 5 % by weight aqueous solution. The solution was filtered through a 200 mesh filter cloth to prepare a dope. The dope was charged into continuous wet spinning machine and defoamed overnight under reduced pressure. The dope was extruded at a rate of 16.4 g per minute into acetone at 18°C through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled at varied rates onto a godet roller of a diameter of 11.2 cm. The fibers were dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 16. Rotation Rate (rpm) Fineness (denier) Strength (gf/denier) 4 - - 8 2.57 0.273 16 1.29 0.327 24 0.85 0.302 32 - - Example 21 Triethanolamine alginate was added to distilled water and stirred for about 4 hours to prepare a 5 % by weight aqueous solution. The solution was filtered through a 200 mesh filter cloth to prepare a dope. The dope was charged into continuous wet spinning machine and defoamed overnight under reduced pressure. The dope was extruded at a rate of 16.4 g per minute into acetone at 13°C through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled at varied rates onto a godet roller of a diameter of 11.2 cm. The fibers were dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 17. Rotation Rate (rpm) Fineness (denier) Strength (gf/denier) 4 - - 8 2.91 0.299 16 1.55 0.207 24 0.86 0.235 32 0.70 0.256 40 - - Example 22 A mixture of sodium alginate and potassium alginate each in the same amount was added to distilled water and stirred for about 4 hours to prepare a 5 % by weight aqueous solution. The solution was filtered through a 200 mesh filter cloth to prepare a dope. The dope was charged into a continuous wet spinning machine and defoamed overnight under reduced pressure. The dope was extruded at a rate of 16.4 g per minute into acetone at 14°C through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled at varied rates onto a godet roller of a diameter of 11.2 cm. The fibers were dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 18. Rotation Rate (rpm) Fineness (denier) Strength (gf/denier) 4 - - 8 3.02 0.299 16 1.27 0.365 24 0.99 0.387 32 0.79 0.404 40 - - Example 23 A mixture of 90 % by weight of sodium alginate and 10 % by weight of propylene glycol alginate was added to distilled water and stirred for about 4 hours to prepare a 5 % by weight aqueous solution. The solution was filtered through a 200 mesh filter cloth to prepare a dope. The dope was charged into continuous wet spinning machine and defoamed overnight under reduced pressure. The dope was extruded at a rate of 16.4 g per minute into acetone at 13°C through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled at varied rates onto a godet roller of a diameter of 11.2 mm. The fibers were dried in the same manner as in Example 1. The fineness and strength of the fibers are shown in Table 19. Rotation Rate (rpm) Fineness (denier) Strength (gf/denier) 4 - - 8 2.68 0.540 16 1.40 0.611 24 0.95 0.704 32 0.69 0.684 40 - - Example 24 An amount of 1214 ml of distilled water was added to 86 g of sodium alginate and the mixture was kneaded with a kneader for about 4 hours to prepare a 6 % by weight aqueous solution. An amount of 1.42 g of polymyxin B sulfate was added to 237 ml of distilled water to prepare an aqueous solution of polymyxin B. An amount of 1183 g of the alginate solution was added to the antibiotic solution, and the mixture was kneaded with a kneader for about 4 hours. The mixture was filtered through a 200 mesh filter cloth to prepare a dope containing 0.1 % by weight of polymyxin B and 5 % by weight of sodium alginate. The dope was extruded at a rate of 16.4 g per minute into acetone through a nozzle provided with 1000 openings each having a diameter of 0.1 mm. The resultant fibers were rolled at a rotaion rate of 16 rpm onto a godet roller of a diameter of 11.2 cm. The fibers were dried in the same manner as in Example 1 to provide water soluble alginate fibers having 0.1 % by weight of polymyxin B immobilized thereto. Example 25-27 The 0.1 % by weight aqueous solution of polymyxin B was diluted with a 5 % by weight aqueous solution of sodium alginate to 0.05 % by weight, 0.025 % by weight and 0.0125 % by weight, respectively. Using these solutions of polymyxin B, there were produced water soluble alginate fibers having polymixin B immobilized thereby. The dopes and the alginate fibers prepared in Examples 24-27 were color-developed with a BCA reagent by a protein colorimetric method, made into a 1 % by weight solution of sodium alginate, and the absorbance at 562 nm was measured with a spectrophotometer. As the results show in Fig. 1, the alginate fibers from either of the dopes showed a high absorbance, and in addition, as apparent from comparison of the absorbances of the fibers with those of the dopes, the antibiotic was found to be immobilized at a high rate. Example 28 An aqueous solution of sodium alginate was prepared in the same manner as in Example 24. An amount of 1.56 g of tetracycline hydrochloride was added to 260 ml of distilled water to prepare an aqueous solution of tetracycline. The alginate solution was added to the antibiotic solution and kneaded with a kneader for about 4 hours. The mixture was filtered through a 200 mesh filter cloth to prepare a dope containing 0.1 % by weight of tetracycline and 5 % by weight of sodium alginate. The dope was treated in the same manner as in Example 24 to provide water soluble alginate fibers having 0.1 % by weigt of tetracycline immobilized thereby. Examples 29-31 The 0.1 % by weight aqueous solution of tetracycline was diluted with a 5 % by weight aqueous solution of sodium alginate to 0.05 % by weight, 0.025 % by weight and 0.0125 % by weight, respectively. Using these solutions of tetracycline, there were produced water soluble alginate fibers having tetracycline immobilized thereby. Making use of the fact that tetracycline has an absorption at 361 nm, the dopes and the fibers prepared in Examples 28-31 were made into 1 % by weight of sodium alginate solutions and the immobilization rate was measured. The results are shown in Fig. 2. Tetracycline was found to be immobilzed by the alginate fibers at a somewhat smaller immobilization rate than polymyxin B; however, the immobilization rate was not less about 65 %. Comparative Example 1 The dope containing 0.1 % by weight of polymyxin B as prepared in Example 24 was extruded into a 5 % by weight aqueous solution of calcium chloride, and otherwise in the same manner as in Example 24, water insoluble algin fibers were prepared. However, the fibers were found to have substantially no polymyxin B immobilized according to the same measurement as before mentioned. Comparative Example 2 The dope containing 0.1 % by weight of tetracycline as prepared in Example 28 was extruded into a 5 % by weight aqueous solution of calcium chloride, and otherwise in the same manner as in Example 28, water insoluble algin fibers were prepared. However, the fibers were found to have substantially no tetracycline immobilized according to the same measurement as before mentioned. Example 32 A 0.05 % by weight aqueous solution of amikacin sulfate was used, and otherwise in the same manner as in Example 24, water soluble algin fibers were prepared which had the antibiotic immobilized thereby. Example 33 A 0.05 % by weight aqueous solution of gramicidin S hydrochloride was used, and otherwise in the same manner as in Example 24, water soluble algin fibers were prepared which had the antibiotic Immobilized thereby. Example 34 An aqueous solution of sodium alginate was prepared in the same manner as in Example 24, and using the solution as a dope, there were prepared water soluble algin fibers in the same manner as in Example 24. The water soluble and water insoluble algin fibers produced in Examples 24-33 and the Comparative Examples 1 - 2 and example 34 were subject to antibacterial tests with Staphylococus aureus (IFO 13216), Pseudomonas aeruginosa (IFO 13275) and Escherichia coli. (IFO 3972) all of which were given by Fermentation Institute Foundation. The microbes were each cultivated on a nutrient agar medium at 37°C over 24 hours, collected, and then about 1 x 10 5 cells each were incubated onto the same medium as above to prepare a plane medium. Then, the algin fibers were each cut to a size of 3 mm in width (1000 of short fibers) and 10 mm in length as test pieces. The test pieces were each placed on the medium, and the microbes were cultivated at 37°C for 24 hours. It was observed whether there were formed blocking areas around each of the test t pieces. When blocking areas were formed and no growth of microbes was observed there, the fibers were taken as antibacterial (positive). The results are shown in Table 20. The antibacterial evaluation was made in four grades based on the short axis of the blocking area formed. +++: not less than 6 mm; ++ : not less than 4 mm and less than 6 mm; + : less than 4 mm; and - : no blocking area formed. Staphylococus aureus Pseudomonas aeruginosa Escherichia coli. Example 24 - +++ -- 25 - ++ ++ 26 - ++ ++ 27 - + ++ 28 - ++ ++ 29 - ++ ++ 30 - ++ ++ 31 - + ++ 32 ++ ++ ++ 33 +++ - - Comparative 1 - ± ± 2 - ± ± Example 34 - - - The algin fibers having polymyxin B immobilized thereby as prepared in Examples 24-27 and the algin fibers having tetracycline immobilized thereby as prepared in Examples 28-31 were all active against Pseudomonas aeruginosa and Escherichia coli. The fibers prepared in Example 32 were active against all the microbes tested. The fibers prepared in Examples 24-33 were found not active against one of the microbes tested possibly because the microbe had resistance to the antibiotic. The fibers prepared in Comparative Examples 1 and 2 were found active to an extent, but not to Staphylococus aureus. The fibers prepared in Example 34 were found active against neither of the microbes tested.

Claims: Water soluble algin fiber wherein the water soluble algin is one or two or more of sodium, lithium, potassium, magnesium and ammonium alginates, algin organic amine salts, and water soluble algin ester derivatives. Water soluble algin fiber having antibiotic immobilized thereon and/or therein wherein the water soluble algin is one or two or more of sodium, lithium, potassium, magnesium and ammonium alginates, algin organic amine salts, and water soluble algin ester derivatives. A method of producing water soluble algin fiber which comprises extruding an aqueous dope containing water soluble algin which is one or two or more of sodium, lithium, potassium, magnesium and ammonium alginates, algin organic amine salts, and water soluble algin ester derivatives into hydrophilic organic solvent. A method according to claim 3 in which the aqueous dope contains 3-20% by weight of the water soluble alginate. A method according to claim 3 or 4 in which the aqueous dope is extruded from at least one nozzle with openings of diameter 0.025-lmm into a coagulating bath containing the hydrophilic organic solvent in an amount not less than 50% by weight, and continuously rolling the resultant fibre for recovery thereof. A method as claimed in any of claims 3-5 wherein the algin organic amine salt is a triethanolamine salt. A method as claimed in any of claims 3-5 wherein the water soluble algin ester derivative is propylene glycol alginate. A method according to any of claims 3 to 7 in which the dope is extruded from at least one nozzle into a coagulating bath containing the hydrophilic solvent at a rate of 0.001- 1 ml per minute per nozzle. A method as claimed in any of claims 3 to 8 wherein the dope contains antibiotic to produce water soluble algin fiber having antibiotic immobilized thereby. A method as claimed inany of claims 3 to 9 wherein the organic solvent is aliphatic alcohol of 1-3 carbons, e.g. selected from methanol, ethanol and isopropanol. A method as claimed in any of claims 3 to 9 wherein the organic solvent is selected from acetone, dioxane, ethylene glycol monomethyl ether, dimethyl sulfoxide, dimethylformamide, dimethylacetamide, acetonitrile, methyl ethyl ketone and phenol.

Inventors: ASAOKA TSUTOMU, FUKUOKA SATOSHI, KAMISHIMA HIROSHI, KOBAYASHI YOSHINARI, OBIKA HIDEKI, TENMA KEISHI, ASAOKA, TSUTOMU, FUKUOKA, SATOSHI, KAMISHIMA, HIROSHI, KOBAYASHI, YOSHINARI, OBIKA, HIDEKI, TENMA, KEISHI
Applicants: AGENCY IND SCIENCE TECHN, SAKAI CHEMICAL INDUSTRY CO, SAKAI CHEMICAL INDUSTRY CO., LTD.,, THE AGENCY OF INDUSTRIAL SCIENCE AND TECHNOLOGY
Application year: 1991
Main classification: D01F9
IPC codes: D01F9, A61L15, D01F1, D01D5