Blanking aperture array and method of producing same

Abstract: The array is intended to be used in an electron beam exposure system and is obtained by forming an electrode layer (34) on a substrate (20) having shift register devices (24). An electron beam aperture (38) is formed in a same position through the substrate and electrode layer, so as to effectively form deep electron beam apertures.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a blanking aperture array for an electron beam exposure system, and to a method of producing the blanking aperture array. 2. Description of the Related Art The electron beam exposure systems include a point beam type in which the electron beam is used in the form of a spot, a variable rectangular beam type in which the electron beam is used in the form of a rectangle, the size of which is variable, and a stencil mask type in which a stencil having electron beam apertures formed therein in a desired pattern is used to shape the electron beam in a desired form. The point beam type exposure system is suitable for forming a fine pattern, but since the throughput thereof is very low, this system is used only for research and development. The variable rectangular beam type exposure system has a throughput one or two orders of magnitude higher than that of the point beam type exposure system, but when a patterns as fine as 0.1 µm or at a high density are exposed to an electron beam, the throughput of this variable rectangular beam type exposure system is also low. When a 1-GB DRAM is exposed to the electron beam by this exposure system, the throughput becomes about three degrees less. Methods by which all patterns can be exposed to the electron beam have been proposed; the Applicant's exposure method using a two-dimensional blanking aperture array is one of these methods and is disclosed in Japanese Examined Utility Model Publication Sho 56-19402. The exposure system which implements the Applicant's method of electron beam exposure by the two-dimensional blanking aperture array is schematically shown in Fig. 1. In this electron beam exposure system, the electron beam emitted from an electron gun 51 is shaped into a one-shot beam (as shown by reference numeral 17 in Fig. 3), and thereafter, the beam is passed through lenses 53 and 55 and then projected upon a BAA (blanking aperture array). The electron beam is deflected by deflectors 56 to select an area on the BAA (at the reference numeral 17 in Fig. 3)upon which the electron beam is to be projected. The electron beam, after passing through an aperture in the BAA, is passed through lenses 58 and 60, an aperture 61 and lenses 62 and 65, and is deflected by deflectors 63 and 64 and projected onto a selected position on a sample. A pair of blanking electrodes 59 are provided to deflect the electron beam so that it does not pass through the aperture 61. Namely, in the two-dimensional blanking aperture array, multiple apertures for the passage of the electron beam are two-dimensionally formed in a semiconductor crystal substrate made of silicon or the like, a pair of blanking electrodes are disposed at opposite ends of each aperture, and a pattern data is given according to whether or not a voltage is to be applied between the electrodes. Thus, the electron beam after passing through the aperture is deflected or allowed to pass linearly and independently, whereby it is determined whether or not the beam should finally arrive at the sample. For example, when one of the blanking electrodes of each aperture is connected to the ground potential and a voltage is applied to the other electrode, the electron beam passing between the electrodes is deflected and is cut off by the aperture after passing through the lenses (at the reference numerals 58 and 60 in Fig. 1) located below the blanking aperture array, and thus the electron beam is not made incident on the sample surface. If no voltage is applied to the other electrode, the electron beam passing between the electrodes is not deflected, and thus the beam is not be cut off by the aperture after passing through the lenses provided below the blanking aperture array, and is projected onto the sample surface. Also the information carried by the pattern for each aperture (whether or not the electron beam passing through the aperture is to be deflected) is sequentially transmitted by shift registers formed in the aperture array. For this purpose, devices and wires must accommodated to form the shift registers. Fig. 2 is a schematic diagram of a two-dimensional blanking aperture array. As shown in the Figure, a plurality of apertures 15 are disposed two-dimensionally in the blanking aperture array, and a pair of electrodes 14A formed at each of the apertures. Each lattice 13 is formed of wires and devices by which a voltage is applied to the electrodes of each aperture, independently, according to a given pattern data. The apertures are disposed at regularly spaced intervals of 10 µm and each is 7 µm by 7 µm in size. Also, each electrode is about 1 µm thick, 7 µm wide and 20 µm long (in the depth direction). Fig. 3 is a plan view showing one example of the blanking aperture array 18. In this case, the blanking aperture array 18 consists of four shot areas 17 each having sixteen (4 x 4) apertures 15, and is controlled according to a given pattern data to determine whether or not the electron beam passing through each aperture in one shot area 17 is to be deflected (whether or not a voltage is to be applied between the electrodes of each aperture) when the beam passes through the aperture. At the other three shot areas, the beam passage is controlled according to different pattern data for the passage of the electron beam. The electron beam is deflected to each shot area by the deflector 56 in Fig. 1. The above-mentioned two-dimensional blanking aperture array can be formed by the processes shown in Figs. 4 and 5. As shown in Fig. 4(1), an impurity diffusion layer 12 is formed on a semiconductor substrate 10 by doping impurities, and an epitaxial growth layer 14 is grown on the impurity diffusion layer 12 as shown in Fig. 4(2). Thereafter, other devices are formed in the epitaxial growth layer 14, i.e., MOS transistors, etc., which compose an inverter and a gate. The aperture shown in Fig. 4 is formed as shown in Fig. 5. As shown in Fig. 5(1), a narrow trench 16 is formed by trench etching at opposite sides of each aperture of the epitaxial growth layer, until the trench reaches the substrate 10. Next, an insulation film 18 is formed on the entire surface as shown in Fig. 5(2), and then an electrode material 20 is deposited in each trench 16 as shown in Fig. 5(3). Next, the epitaxial growth layer and impurity diffusion layer between the thus formed electrodes E 1 and E 2 are removed by etching as shown in Fig. 5(4). Furthermore, the semiconductor substrate 10 is taper-etched between the electrodes E 1 and E 2 , from the rear side thereof as shown in Fig. 4(4), whereby the aperture AP is formed. The output of each of the shift register sites is connected to one of the electrodes E 1 and E 2 of each aperture, and the low voltage side GND of the power source or the high voltage side V DD and low voltage side GND are alternately connected to the other electrode. This wiring process is effected at the same time as or separately from the wiring to each device of the shift register and the clock signal wiring. Fig. 6 shows the arrangement of such a blanking aperture array circuit. As seen in the Figure, AP indicates a beam aperture, and a pair of electrodes E 1 and E 2 are formed across each aperture. E 1 is an electrode to which a constant voltage is always applied, and E 2 is an electrode to which a voltage varied in accordance with the given pattern data is applied. When the electron beam is turned on, a same voltage (0 V, for example) is applied to the electrodes E 1 and E 2 so that the beam passes through the aperture 61 in Fig. 1 is not deflected when passing between the electrodes, and arrives at the sample. On the other hand, when the electron beam is turned off, a voltage (+5 V, for example) applied to the electrode E 2 is different from the voltage applied to the electrode E 1 , and thus the beam is deflected when passing through the electrodes and is given a trajectory such that it cannot pass through the aperture 61 in Fig. 1. Thus, in the latter case, the electron beam will not arrive at the sample. The beam on/off data (0 or 5 V) is transferred by the shift register formed in the BAA, to the electrodes of each aperture. Namely, the data supplied from the left by data transfer wires SR 1 to SR 3 is shifted until it is transferred fully to the right by clock signal wires CLK 1 and CLK 2 . During the data transfer, another area (at the reference numeral 17 in Fig. 3) is exposed to the deflected electron beam or a variable rectangular aperture is used. Note that "U" in Fig. 6 indicates an area where a device is formed. As seen from the foregoing, the blanking aperture array is conventionally formed by etching a semiconductor substrate for forming electrodes, implanting electrode materials in the substrate, and thereafter, forming apertures for the electrode surfaces to be exposed. Namely, the conventional method of forming electrodes necessitates the etching of the substrate, and the portions where the electrodes are to be formed must be etched to a great depth compared to the etching area (for example, 7.0 µm (longitudinally) x 1.0 µm (laterally), and 20 to 30 µm in depth). Since the electrode side face is formed along the etched trench wall of the substrate (in effect, an insulation layer is formed on the side face and then an electrode material is implanted to form the electrode side face), the etching must be linear because the electrode side face is defined by the form of the aperture. Also, the insulation layer must be formed in this etched trench and the electrode material implanted in the trench, and unless the electrode material is fully buried in the trench, it cannot operate for the full length of the electrode's life. Accordingly, the electrode materials must be fully buried for 200 apertures x 200 apertures x 2 electrodes, and this process is difficult. It is also very difficult to form many apertures in a limited space, as the aperture must have a substantial size because of the relation with the time of exposure to the electron beam. Furthermore, elaborate devices for the shift registers must be formed in the substrate, to prevent a malfunction of the devices due to exposure to the electron beam. An object of the present invention is to overcome the above-mentioned drawbacks of the conventional techniques by providing an improved and novel blanking aperture array, and a method of producing the blanking aperture array. The inventors have made intensive studies into the above-mentioned drawbacks of the conventional techniques, and as a result, discovered an improved and novel blanking aperture array having a structure which is different from of the conventional structures. EP 0 335 711 discloses a charged particle beam exposure system using a blanking aperture array. The electrodes are formed at an edge portion of a recess extending through the substrate. Thus, EP 0 335 711 shows a blanking aperture array for use in an electron beam exposure system, comprising: a substrate having a plurality of apertures and a plurality of pairs of electrodes, said substrate having first and second, opposed main surfaces and a plurality of apertures extending through the surface, each aperture having a pair of spaced, opposed edge faces transverse to the main surfaces of the substrate. According to the invention, the array further comprises a device serving as a shift register and formed in and connected to the substrate, the device serving as a shift register being formed at a position underneath the electrodes. The invention also provides a method of producing the blanking aperture array, comprising the steps of: providing a substrate with an insulating layer, forming electrode layers on the substrate; selectively etching the electrode layers to form a plurality of openings; and forming a plurality of apertures in the substrate, in such a manner that the center line of each opening coincides with each aperture, the method being characterized by forming a device serving a shift register in the substrate and forming a wire to be connected to the device serving as a shift register; and opening a plurality of windows in the insulating layer in order to expose the device serving as a shift register or the wire, the electrode layers being deposited over the insulation layer and windows to a desired electrode length. The apertures may be formed in the substrate before the openings are formed in the electrode layer. Different from the conventional method, the method according to the present invention essentially lies in (1) forming an electrode layer on the main surface of a semiconductor substrate and (2) forming an electron beam aperture in a same position through the substrate and the electrode layer. The substrate may be provided with an insulating layer, and the method may additionally comprise: forming a device serving as a shift register in the substrate and forming a wire to be connected to the device serving as the shift register; and opening a plurality of windows in the insulating layer in order to expose the device serving as the shift register or the wire, and depositing the electrode layer over the insulation layer and windows to a desired electrode length. The removal by etching of the unnecessary portions of the electrode material may be done in an area other than the area which will be the opening, and before forming the opening as mentioned above or after forming the opening. Also, when an insulation layer is provided the openings can be formed by etching the substrate, insulation layer and electrode layer collectively at areas thereof corresponding to the electron beam aperture. The opening may be formed by etching the substrate, insulation layer and then the electrode layer, in this order, from the rear side of the substrate, or etching in the reverse order from the front side. Alternatively, the opening can be formed by first etching the electrode layer and then the substrate and insulation layer, from the rear side. Furthermore, the opening may be formed by first etching the electrode layer and insulation layer, in this order, from the front surface of the substrate, and then the substrate from the rear side thereof, or in the reverse order. The etching involved in all the above-mentioned methods is preferably an anisotropic etching. In the method according to the present invention, the electrodes are formed simultaneously with the forming of the opening. Moreover, by etching the substrate, insulation layer and electrode layer collectively in one step, to form the opening, an electron beam aperture can be produced as defined by the flush end faces of the openings in the substrate, insulation layer and electrode layer. Further, by etching in two steps as above, the end faces of the openings in the substrate, insulation layer and electrode layer can be made flush with each other as above, or the end face of the opening in the electrode layer may be set back from those of the openings in the substrate and insulation layer. In the latter case, the etching need not be so precise and may be rough, because the opening in the substrate is used only to shape the electron beam. Namely, the opening wall of the electrodes does not have a close relation with the extent of the electron beam deflection. When the end face of the opening in the electrode layer is set back from the openings in the substrate and insulation layer, the set-back portion can be used as a positioning margin for forming the electrodes at the surface by making the openings from the rear side of the substrate. In the method according to the present invention, the electrodes are formed by depositing an electrode material on the insulation layer. The electrode material is deposited by coating in a conventional manner, but a plating method may be adopted to deposit the electrode material on an electrode metal to be plated. Further, in the method according to the present invention, a window for contact is opened in the insulation layer corresponding to a device area formed in the substrate, in such a manner that the device area is positioned under the electrode. An alternative method according to the invention comprises the steps of forming an insulation layer on a main surface of a substrate; forming a pair of openings in the insulation layer; forming a pair of electrodes in the opening portions, by plating; and removing the insulation layer, followed by forming an aperture in the substrate, said aperture being positioned between a pair of electrodes and the center line of said aperture coinciding with the center line of each pair of electrodes. BRIEF DESCRIPTION OF THE DRAWINGS The object as well as advantages of the present invention will be made clear by the following description of the preferred embodiments of the present invention, with reference to the accompanying drawings, wherein: Fig. 1 is a schematic diagram of the overall construction of a known electron beam exposure system; Fig. 2 is a schematic diagram of a known two-dimensional aperture array; Fig. 3 is a plan view of a known blanking aperture array; Fig. 4 is an explanatory drawing showing a known process of producing an aperture array; Fig. 5 is an explanatory drawing showing a known process of forming apertures; Fig. 6 is a plan view showing a known arrangement of the blanking aperture array circuit; Fig. 7 is a process drawing showing one embodiment of the present invention; Fig. 8 is a process drawing showing another embodiment of the present invention; Fig. 9 is a process drawing showing still another embodiment of the present invention; Fig. 10 is a process drawing showing one embodiment of the present invention in which the electrodes are retracted; Fig. 11 is a process drawing showing another embodiment of the present invention in which the electrodes are retracted; and Fig. 12 is a process drawing showing still another embodiment of the present invention in which the electrodes are retracted. Fig. 13 is a process drawing showing another embodiment of the present invention, in which the electrode is formed by a plating method. DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiment 1: Fig. 7 shows the processes of producing the electrodes according to one embodiment of the present invention. Devices for shift registers 24 (referred to as "device" or "devices" hereinafter) are formed on a silicon substrate 20 (at step (1) in Fig. 7). Next, a silicon oxide film (SiO 2 ) is deposited over the silicon substrate 20, patterned and used as mask to form, by etching, 7 x 7 µm trenches in the substrate at the area which will be an opening 26 (at step (2) in Fig. 7). Further, an insulation layer is formed on the entire surface, a window for contact with the device 24 is opened by patterning, and a wiring material (W or the like) is deposited on the entire surface. The wiring material is patterned to form a wire 28. Another insulation film 30 is formed on the entire surface (at step (3) in Fig. 7). The insulation film 30 may be made of SiO 2 and formed by CVD. The insulation film (oxide film) 30 becomes an insulation layer for separating the wires from each other, and therefore, the insulation film 30 need not entirely fill the opening 26. Next, an oxide film is deposited as a mask over both the front and rear sides, a predetermined area at the rear side is patterned, the oxide film is removed, and the rear side is etched (at step (4) in Fig. 7). This etching may be a wet etching in which a KOH solution is used, but not a rough etching. Then, a window 32 for contact with the electrodes and device 24 is formed in the insulation film 30 (at step (5) in Fig. 7). Furthermore, an electrode material (for example, W or the like) is deposited on the insulation film by sputtering (or deposition) in such a manner that a desired length of electrode can be finally assured, thereby forming an electrode material layer 34 (at step (6) in Fig. 7). Note that the electrode material may be filled in the window 32 beforehand in this case. Further, an oxide film is deposited on the entire surface and patterned, and using the patterned oxide film as a mask, unnecessary portions of the electrode material layer 34 are removed by anisotropic etching (at step (7) in Fig. 7). Finally, the insulation film (oxide film) and electrode material layer corresponding to the opening are removed by anisotropic etching from the rear side, with the etching gas changed sequentially, to simultaneously form an electron beam aperture 38 and an electrode 40. It should be noted that the opening 26 is formed at the beginning of the process to facilitate the positioning for etching in the subsequent processes. More particularly, the etching involved in the above-mentioned embodiment can be done, for example, as follows: i) Etching of electrode (W) Since the electrode (W) is about 20 µm thick, it is etched using a CVD oxide film (2 µm) and tri-level photo-resist (lower layer about 5 µm thick) as a mask.First, the CVD oxide film is etched, using the photo-resist as a mask, with a CHF 3 /CH 4 gas. Next, using the remainder of the photo-resist and the CVD oxide film as a mask, the substrate is etched using an SF 6 gas under the low temperature. ii) Etching of insulation film (SiO 2 ) The insulation film is etched using a CHF 3 /CH 4 gas. Either the W of the electrode or Si of the electrode may be used as a mask. The etching may be done from either the rear side or front side of the substrate. iii) Etching of substrate (Si) Using the oxide film (PSG) deposited as a mask on the rear side, the substrate is etched with an HBr gas. Embodiment 2: The second embodiment of the method according to the present invention will be described with reference to Fig. 8. Note that the symbols used in Fig. 8 have the same meanings as those in Fig. 7. In the description of the second embodiment, explanations of similar operations to those in the first embodiment will be simplified. A device 24 is formed on a substrate (silicon) 20 (at step (1) in Fig. 8), a wire (W or the like) 28 is formed on the silicon substrate 20 by patterning, and an insulation film 30 is formed on the wire (at step (2) in Fig. 8). Next, the rear side of the substrate is wet-etched to a predetermined shape by isotropic etching (at step (3) in Fig. 8). The rear side may be etched with an oxide film deposited thereon, after depositing an electrode material (W). Next, a window 32 for contact with the electrode and device is formed on the insulation film 30 (at step (4) in Fig. 8). As at step (5) of the first embodiment, an electrode material (W or the like) is deposited to form an electrode material layer 34 (at step (5) in Fig. 8). Also in this embodiment, the W or the like may be grown in the window beforehand. Then, an oxide film is deposited on the entire surface, patterned, and using the patterned oxide film as a mask, unnecessary portions of the electrode material layer 34 are removed by isotropic etching (at step (6) in Fig. 8). Further, an oxide film (SiO 2 ) is deposited on the rear side of the substrate and patterned, and the portion of the layers to be opened is etched (by anisotropic etching). Next, the opened substrate (Si) is masked, and the insulation film (SiO 2 ) is etched (by anisotropic etching). Using the opened SiO 2 film as a mask, the electrode material layer 34 is etched to form an electron beam aperture 38. An electrode layer 40 is formed simultaneously with the electron beam aperture (at step (7) in Fig. 8). Embodiment 3: Fig. 9 shows a variation of the second embodiment. Since the processes (1) to (5) in this variation are the same as those in the second embodiment, they will not be described. The opening is formed and unnecessary portions of the electrode material layer 34 are removed, as follows. Namely, to form the opening in a linear well-defined form, an oxide film or the like is formed on the electrode material layer 34. Next, the oxide film on a portion which is to be the opening is removed, and an etching is done to at least the insulation film 30 by changing the etching gas or otherwise. Thereafter, the oxide film is removed from the electrode material layer 34, and unnecessary portions are removed from the electrode material layer 34 by etching (at step (6) in Fig. 8). Finally, the insulation film 30 and substrate 20 are etched (by anisotropic etching) from the front side of the substrate, to form an electron beam aperture 38, whereby an electrode layer 40 is formed. Embodiments 4 to 6: Next, the embodiments in which the electrode is set back will be described with reference to Figs. 10 to 12. Note that the symbols used in Figs. 10 to 12 have the same meanings as those in Fig. 7. In the description of the second embodiment, explanations of operations similar to those in the first embodiment will be simplified. The first (fourth embodiment) of these embodiments will be described with reference to Fig. 10. Namely, in the fourth embodiment, the processes (1) to (5) in the second embodiment are also done (steps (1) to (3) in Fig. 10). Next, the substrate 20 and insulation film 24 are etched (by anisotropic etching) (at step (4) in Fig. 10). Finally, a patterning is done in such a manner that the electrode is set back, and an etching is done from the front side of the substrate to form an electron beam aperture 38 and a pair of electrodes 40 (at step (5) in Fig. 10). Note that the electron beam aperture 38 consists of an opening and an aperture. A next (fifth embodiment) of the above-mentioned embodiments will be described with reference to Fig. 11. As can be seen, the production processes (1)' to (3)' in this fifth embodiment are the same as the processes (1) to (3) in the fourth embodiment. After depositing an electrode material, a patterning is made to form the electrode 40. Next, a patterning is done such that the electrode is set back, and the insulation film 30 is etched from the front side of the substrate 20 (at step (4)' in Fig. 11). Then, etching is effected from the rear side of the substrate 20 to form an electron beam aperture 38 in a same position (at step (5)' in Fig. 11). A further (sixth embodiment) of the aforementioned embodiments will be described with reference to Fig. 12. As can be seen, the steps (1)" and (2)" in this sixth embodiment are the same as the processes (1) to (3) in the first and second embodiments. After depositing an electrode material, a patterning is done to form the electrode 40, and then the insulation film is etched, with the etching gas changed, to form a trench in the insulation film (at step (4)" in Fig. 12). Next, a patterning is done for a narrower area than the trench, and an etching is done from the rear side of the substrate 20 to form a electron beam aperture 38. Embodiment 7: Fig. 13 shows a further embodiment of the present invention. In this embodiment, a pair of electrodes are formed by a plating method. These electrodes are not formed at the same time as the etching but when plating. First, devices for shift register 42 are formed on a silicon substrate 40 (at step (1)''' in Fig. 13), then an opening 44 is formed in the substrate (at step (2)''' in Fig. 13), an insulating film 46 is formed on the substrate, a window 48 for contact with the device 42 is opened by etching, and a wire pattern 50 is formed on the insulating film (at step (3)''' in Fig. 13). A material 52 for an electrode is thrown into the window, and a metallic wire for the plating electrode 54 is formed on the surface of the substrate and in contact with the material for the electrode (at step (4)''' in Fig. 13). Next, a resist 56 is coated to a thick thickness corresponding to the thickness of the electrode (at step (5)"' in Fig. 13), and openings 58 for forming the electrode are formed by a patterning process (at step (6)''' in Fig. 13). Next, the device is dipped in a plating bath, to obtain the material for the electrode plate while applying an electric current to the metallic wire for the plating electrode, and the portion 60 corresponding to the electrode is formed (at step (7)''' in Fig. 13). Next, the resist is removed to form a pair of electrodes 62 (at step (8)''' in Fig. 13). Finally, the metallic wire for the plating electrode is separated (at step (9)''' in Fig. 13), followed by etching the substrate, to obtain an electron beam aperture (at step (10)''' in Fig. 13). As described above, according to the present invention, the electrode is not formed on the lateral side of the substrate but on the substrate, and an electron beam aperture is formed in a same position through the substrate and electrode layer. Therefore, a deep electron beam aperture can be formed with a high efficiency. Also, since unnecessary portions of an electrode material deposited on the substrate are removed by anisotropic etching, it is not necessary to form in the substrate, by etching, a trench where an electrode is to be formed and having a small area but a large depth. Further, since it is unnecessary to form an insulation layer on the wall face of the thus formed trench, as in the conventional technique, and to fill an electrode material in the trench, the electrode can be easily formed. Furthermore, unnecessary portions of the electrode material can be removed from an area other than an area which is to be opened, before or after the substrate, insulation film and electrode material are etched collectively at one step in a same position to form the opening, whereby a linear electron beam aperture can be formed without any deviation between the openings in the substrate and electrode material. Also, when building the device in the substrate, the device can be placed in an area under the electrode because of the geometrical relation thereof to the area to be opened. Namely, the device can be hidden behind the electrode, and thus a possible malfunction of the device due to exposure to the electron beam can be avoided. Furthermore, since the electrode is formed on the substrate, the device also can be formed under the electrode, with the result that the lattice portion of the substrate can be made larger, leading to an improved strength of the substrate, and that the device area and electrode area can overlap each other, leading to an easy forming of the device. Further, by etching with the patterning position changed, a blanking aperture array can be provided in which the electrode is set back from the opening position. In this case, the electron beam may be shaped through the opening in the substrate. Therefore, a high precision blanking aperture array can be produced by a rough etching, without considering the shape of the electrode surface.

Claims: A blanking aperture array for use in an electron beam exposure system, comprising : a substrate (20) having a plurality of apertures (38); and a pair of electrodes (40), disposed around each of the apertures (38) on said substrate (20), wherein the center line of the electrodes (40) is coincident with the aperture (38), characterized in that the array further comprises a device (24) serving as a shift register and formed in and connected to the substrate (20), said device serving as the shift register being formed at a position underneath the electrodes (40). A blanking aperture array according to claim 1, wherein openings (26) formed by a pair of electrodes (40) and the aperture (20) are formed respectively in a same position. A blanking aperture array according to claim 3, wherein a shape of the opening (26) is same as that ofthe aperture (38). A blanking aperture array according to claim 3, wherein a size of the opening (26) is larger than that of the aperture (38). A method of producing a blanking aperture array through which electron beams are transmitted, comprising the steps of: providing a substrate (20) with an insulating layer (30); forming electrode layers (34) on the substrate (20); selectively etching the electrode layers (34) to form a plurality of openings (26); and forming a plurality of apertures (38) in the substrate (20), in such a manner that the center line of each opening (26) coincides with each aperture (38), characterized in that the method additionally comprises : forming a device (24) serving as a shift register in the substrate (20) and forming a wire (28) to be connected to the device (24) serving as the shift register; and opening a plurality of windows in the insulating layer (30) in order to expose the device (24) serving as the shift register or the wire (28), and in that the electrode layers (34) are deposited over the insulation layer (30) and the windows (32) to a desired electrode length. A method according to claim 5, wherein a window (32) is opened in the insulation layer correspondingly to a device area formed in the substrate (20). A method according to claim 5, wherein etching is used to form the electrodes simultaneously with the forming of the apertures (38). A method according to any one of claims 5 to 10, in which the apertures (38) in the substrate (20) are each formed between a pair of electrodes.

Inventors: SAITO TOMIYASU, TAKAHASHI YASUSHI, SAITO, TOMIYASU, TAKAHASHI, YASUSHI
Applicants: FUJITSU LTD, FUJITSU LIMITED
Application year: 1991
Main classification: H01J37
IPC codes: H01J37, H01L21