Ferroelectric liquid crystal device

Abstract: A ferroelectric liquid crystal device having a pair of substrates each provided with voltage applying means, an orientation control layer (6) formed on at least one of the substrates, and a layer (8) of ferroelectric liquid crystal composition disposed between the pair of substrates, the ferroelectric liquid crystal composition comprising at least one compound (a) having an optically active group of the formula (I): , at least one compound (b) which is reverse to the compound (a) in the direction of a helical pitch induced in a nematic phase and at least one liquid crystal compound (c) exhibiting a smectic C phase, the liquid crystal composition exhibiting at least a smectic C phase, smectic A phase and nematic phase.

Description: 1. Field of the Invention This invention relates to a ferroelectric liquid crystal device and more particularly to a ferroelectric liquid crystal device which comprises substrates, voltage applying means, an orientation control layer and a ferroelectric liquid crystal composition layer and is usable as a liquid crystal shutter, a liquid crystal display device or the like. 2. Description of the Related Art Liquid crystal display devices most widely used at present are those utilizing nematic phase, but they have a drawback such that a display of large capacity such as of 2,000 x 2,000 lines is hard to realize. Specifically, in ordinary twisted nematic (TN) type liquid crystal display devices, contrast decreases as the number of lines increases, so that it is nearly impossible in practice to produce a display device of large capacity such as of 2,000 x 2,000 lines, with a good appearance. In order to eliminate the drawback of the TN type liquid crystal display devices, liquid crystal display devices of super twisted nematic (STN) type and double super twisted nematic (DSTN) type have been developed. However, they also have a drawback such that contrast and response speed decrease as the number of lines increases. Therefore, it is presently the utmost level that such display devices be provided with a display capacity of approximately 800 x 1024 lines. On the other hand, there has been also developed a liquid crystal display device of active matrix type where thin film transistors (TFT) are arranged on a substrate, whereby a large capacity display of 1,000 x 1,000 lines and the like can be realized technically. However, the device has a drawback such that its production process takes a longer time with poor yield, leading to a very high production cost. As means to solve the problems described above, a ferroelectric liquid crystal display device, which is proposed as a liquid crystal display based on a principle different from that for the TN type display device, has been expected to be promising (N.A. Clark, et al, Appl. Phys, Lett., 36, 899 (1980)). In such a display device, a ferroelectric liquid crystal capable of exhibiting chiral smectic C phase, chiral smetic I phase, etc. is utilized for operation. Because the principle of the device is classified in a type utilizing memory characteristics of the liquid crystal, a larger display capacity may potentially be realized if response speed improves. Because the process does not require an active element such as thin film transistor, the cost for producing the liquid crystal device may not rise. Furthermore, the ferroelectric liquid crystal device has also a merit of a wide view angle, so that it is considered promising as a device for a display of a larger capacity of 2,000 x 2,000 lines. Liquid crystal materials used in a ferroelectric liquid crystal display device utilizing the smectic C phase abovesaid is required to exhibit smectic C phase within a wide temperature range of which center is around room temperature. The liquid crystal materials are also required to satisfy various conditions such as high speed response as a device property for realizing a larger capacity display at the first. In this regard, liquid crystal materials are to show large spontaneous polarization and lower viscosity. Furthermore, possessing a phase sequence such as IAC (Isotropic-Smectic A-Smectic C) or INAC (Isotropic-Nematic-Smectic A-Smectic C) is required in order to obtain good orientation and bistability when the ferroelectric liquid crystal is applied to a liquid crystal cell, the good orientation and bistability also requiring a spiral pitch of nematic phase and smectic C phase to be sufficiently longer than the thickness of cell. Also, possessing a large tilt angle is needed in order to improve contract and brightness in liquid crystal display. However, it is impossible at present to satisfy all of such requirements with a single compound. Therefore, a plurality of compounds are mixed together and practically applied as a liquid crystal composition but a sufficiently satisfying liquid crystal composition has not yet been realized. For producing a liquid crystal composition which meets practical requirements, many single liquid crystal compounds having various properties are to be used in combination and it may require as a content of liquid crystal composition a compound without showing any liquid crystal phase. SUMMARY OF THE INVENTION The present invention has been accomplished under the foregoing situations and is to provide a ferroelectric liquid crystal device comprising such a ferroelectric liquid crystal composition as having a wider operable temperature range, a good orientation and memory characteristic, a larger tilt angle, and a high-speed response at room temperature. According to the present invention, there is provided a ferroelectric liquid crystal device having a pair of substrates each provided with voltage applying means, an orientation control layer formed on at least one of the substrates, and a layer of ferroelectric liquid crystal composition disposed between the pair of substrates, the ferroelectric liquid crystal composition comprising at least one compound (a) having an optically active group of the formula (I): , at least one compound (b) which is reverse to the compound (a) in the direction of a helical pitch induced in a nematic phase, and at least one liquid crystal compound (c) exhibiting a smectic C phase, the liquid crystal composition exhibiting at least a smectic C phase, smectic A phase and nematic phase. The ferroelectric liquid crystal device of the present invention has a good orientation characterisitic of the liquid crystal layer, shows a higher contrast developing a bright display and permits a wider operable temperature range with larger tilt angle, so that it is quite useful as a liquid crystal device of large capacity for display and photoswitching. BRIEF DECRIPTION OF THE DRAWINGS Fig.1 is a sectional view illustrating a constitution of a ferroelectric liquid crystal device of an embodiment of the present invention. Fig. 2 is a plan view illustrating a constitution of a large capacity ferroelectric liquid crystal device of another embodiment of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT The compound (a) having an optically active group of the formula (I) defined above, which is used in the ferroelectric liquid crystal device of the present invention, has not been disclosed in any literature. The optically active group (I) may be cis-form or trans-form. Either form may be applicable to the present invention. Groups of two forms may be used in mixture. Preferable examples of the compound (a) having the group (I) are those represented by the following formulae (II) and (III): wherein A¹,A²,A³ are each a group containing a 6-membered ring and having or not having a substituent, X is -O-, -COO-,-OCO- or a single bond, Y¹ and Y² are each -COO-, -OCO, -OCH₂-, -CH₂O-, -CH₂CH₂-, -CH=CH-, -C≡C- or a single bond, R¹and R² are each straight-chain or branched-chain alkyl or alkoxy group having 1 to 15 carbon atoms, and p, q and r are each an integer of 0 or 1, wherein A⁴, A⁵, A⁶ are each a group containing a 6-membered ring and having or not having a substituent, Y⁴ and Y⁵ are each -COO-, -OCO-, -OCH₂-, -CH₂O-, -CH₂CH₂-, -CH=CH-, -C≡C- or a single bond, R³ and R⁴ are each straight-chain or branched-chain alkyl or alkoxy group having 1 to 15 carbon atoms, and p, q and r are each an integer of 0 or 1. R¹, R², R³ and R⁴ in the formulae (II) and (III) each represents an alkyl or alkoxy group having 1 to 15 carbon atoms. Specific examples of the alkyl group include methyl, ethyl, propyl, i-propyl, butyl, i-butyl, pentyl, 1- or 2-methylbutyl, hexyl, 1- or 3-methylpentyl, heptyl, 1- or 4-methylhexyl, octyl, 1-methylheptyl, nonyl, 1- or 6-methyloctyl, decyl, 1-methynonyl, undecyl, 1-methyldecyl, dodecyl, 1-methylundecyl and the like. Specific examples of the alkoxy group include methoxy, ethoxy, propoxy, i-propoxy, butoxy, i-butoxy, pentoxy, 1- or 2-methylbutoxy, hexyloxy, 1- or 3-methypentoxy, heptyloxy, 1- or 4-methylhexyloxy, octyloxy, 1-methylheptyloxy, nonyloxy, 1- or 6-methyloctyloxy, decyloxy, 1-methylnonyloxy, undecyloxy, 1-methyldexyloxy, dedocyloxy, 1-methylundecyloxy and the like. The alkyl or alkoxy group may contain asymmetric carbon(s) in the carbon chains thereof. One or more hydrogen atoms in the alkyl or alkoxy group may be substituted with fluorine, chlorine, bromine, cyano, nitro, trifluoromethyl, methoxy or the like. Examples of the group containing a 6-membered ring for A¹, A², A³, A⁴, A⁵ and A⁶ in the formulae (II) and (III) include benzene ring, pyridine ring, piperazine ring, cyclohexane ring, dioxacyclohexane ring, bicyclo[2.2.2]octane ring, naphthalene ring and the like. One or more hydrogen atoms in this ring may be substituted with fluorine, chlorine, bromine, cyano, nitro, methyl, methoxy or the like. The compound represented by the formula (II) may be prepared by reacting an optically active γ-lactone compound represented by the formula (IIa): wherein the definitions R¹ and R² are the same as above, with CH₃I under the presence of a base. In the reaction, the compound (IIa) is converted by the base (preferably of 1 to 1.5 equivalent amounts) to the corresponding enolate anion which is then reacted with CH₃I (preferably of 1 to 5 equivalent amounts) to produce the compound (II). Preferable examples of the base include lithium diisopropylamide, sodium diisopropylamide, potassium diisopropylamide, lithium 1,1,1,3,3,3-hexamethyldisilazanide sodium 1,1,1,3,3,3-hexamethyldisilazanide, potassium 1,1,1,3,3,3-hexamethyldisilazanide, lithium 1,1,1,3,3,3-hexaethyldisilazanide, sodium 1,1,1,3,3,3-hexaethyldisilazanide, potassium 1,1,1,3,3,3-hexaethyldisilazanide, potassium t-butoxide and the like. The reaction is conducted in an organic solvent. In the case where potassium t-butoxide is used as the base, t-butyl alcohol is preferable as the organic solvent. In another case, ethers such as tetrahydrofuran, ethyl ether, dimethoxyethane, diethylene glycol dimethyl ether, dioxane or the like; non-protonic solvents such as dimethylformamide, dimethylsulfoxide, dimethylacetamide, hexamethyl phosphoric triamide; or the mixture thereof, may be used as the solvent. When potassium t-butoxide is used as the base, the reaction is suitably effected at a temperature of 30 to 90°C for 0.25 to 5 hours. When another base is used, the reaction is completed promptly or within 2 hours at a temperature of -80 to 30 °C, depending upon the kind of the base. The compound (IIa) used as a raw material may be prepared by reacting, in an organic solvent and under the presence of a base, an optically active glycidyl ether represented by the formula (IIb): with a malonate derivertive represented by the formula (IIc): wherein R⁵ denotes a hydrogen atom or an alkyl group having 1 to 15 carbon atoms and R⁶ denotes a lower (carbon number of 5 or less) alkyl group. The above reaction may be completed under reflex for 1.5 to 24 hours using 1 to 5 equivalent amount of the compound (IIb) with 1 to 5 equivalent amount of the compound (IIc). Preferable examples of the base used for this reaction include sodium methoxide, sodium ethoxide, potassium t-butoxide, sodium hydride, lithium hydride, n-butyl lithium and the like. Preferable examples of the organic solvent include alcohols such as methanol, ethanol, t-butyl alcohol and the like; ethers such as tetrahydrofuran, ethyl ether, dimethoxyethane, diethylene glycol dimethyl ether, dioxane or the like; non-protonic solvents such as dimethylformamide, dimethylsulfoxide, dimethylacetamide, hexamethyl phosphoric triamide and the like; or the mixture thereof. The glycidyl ether (IIb) may be prepared by reacting an hydroxy compound R¹OH with optically active epichlorohydrin under the presence of a base. Optically active epichlorohydrin is preferably used at 1 to 10 equivalent amounts to the hydroxy compound in this reaction. The base is preferably used at 1 to 5 equivalent amounts. Examples of the base include sodium hydroxide, potassium hydroxide, potassium t-butoxide and the like. This reaction may be conducted without using any catalyst, but a catalyst of quaternary ammonium salt such as benzyltriethylammonium chloride, benzyltriethylammonium bromide, benzyltrimethylammonium chloride, benzyltrimethylammonium bromide or the like may be used at 0.01 to 0.1 equvalent amounts to the hydroxy compound. The reaction may be effected by using epichlorohydrin as a solvent as it is, but may be effected in an polar organic solvent such as dimethylformamide, dimethylsulfoxide, dimethylacetamide, acetonitrile, t-butyl alcohol, water or the like. The reaction may be completed within 0.5 to 3 hours at a temperature of 50 to 80 °C. On the other side, the compound represented by the formula (III) may be prepared such a method as illustrated by the following scheme. First, an acetophenone derivative (IVa) synthsised by a customary manner is subjected to Willgerodt reaction to produce a phenylacetic acid derivative (VIb) which is then subjected to the reaction with lithium diisopropylamide (LDA) followed by the raction with methyl iodide (MeI) to produce a phenylmethylacetic acid derivative (IVc). The derivative (IVc) is then reacted with lithium diisopropylamide (LDA) of double molar ratio at - 30 to +10 °C followed by an optically active epoxy compound (VId) of 0.3 to 3 molar ratio at -78 °C to room temperature, so that an addition compound (VIe) is produced. The compound (VIe) is then subjected to intramolecular dehydrogenation in solvent such as benzene or toluene under the presence of acid catalyst such as sulfuric acid, hydrochloric acid or p-toluenesulfonic acid to obtain the compound represented by the formula, (III) which is an optically active γ-lactone derivative. The compound (VId)-(1) in which R¹ in the optically active epoxy compound (VId) is an alkyl group may be obtained by the following reaction. wherein R¹ represents an alkyl group, * represents an asymmetric carbon atom and X represents a halogen atom. In this scheme, the reaction of the alkyl halide or halogenated alkenyl (R¹X) with magnesium produces Grignard's reagent which is then reacted with optical active epichlorohydrin under the presence of copper halide (CuX) to produce the optically active epoxy compound (VId)-(1). In the optically acitive epoxy compound (VId), the compounds (VId) - (2) wherein R¹ is an alkyloxy group may be obtained by the following reaction. wherein R¹ represents an alkoxy group, and * represents an asymmetric carbon atom. That is, the reaction may be effected by two steps or a single step method. The two step method is conducted by such a manner that an alcohol (R¹-H) is caused to react with optically active epichlorohydrine under the presence of an acidic catalyst to synthesize chlorohydrine ether (VIf) which is then subjected to cyclization with alkali. The single step method is carried out in such a manner that the alcohol is reacted with optically active epichlorohydrine and a base under the presence of quaternary ammonium salt catalyst. The abovesaid optically active epoxy compound (VId) may also be produced by a method of utilizing the reaction of olefin with air by the use of microorganism. The optical active epichlorohydrine may be employed of high purity as obtained by the method disclosed in Japanese Unexamined Patent Publication Nos.SHO 61-132196 and 62-6697. In the ferroelectric liquid crystal device, the liquid crystal layer is required not only to show a higher response in operation but also to exhibit a mono-domain of ferroelectric liquid crystal phase such as smectic C phase. Typically, such a mono-domain can be developed by using a liquid crystal having a phase sequence of INAC and a longer helical pitch in nematic phase. The compounds represented by the formulae (II) and (III) may include those not exhibiting any liquid crystal phase. Even when exhibiting liquid crystal phase, the compounds are not necessarily pratical alone in a view point of the temperature range in which the liquid crystal phase sequence or smectic C phase is exhibited, so that the compound (II) or (III) may be preferably used with other liquid crystal compounds in comparison with being solely used. Particularly, the compound (II) or (III) may suitably be added at a proper amount into a smectic liquid crystal compound or composition (host liquid crystal) which consists of at least one liquid crystal compound (c) exhibiting a smectic C phase, to thereby provide a ferroelectric liquid crystal composition having a larger spontaneous polarization and showing a high-speed response. In this case, the addition amount of the compound (II) or (III) is preferably 0.1 to 30 wt% and more preferably 0.5 to 10 wt%. When the addition amount is more than 30 wt%, it may often lead to practical problems that the compound added is crystalized in the ferroelectric liquid crystal composition or upper limit temperature of smectic C phase is lowered, while when the addition is less than 0.1 wt%, a sufficient effect cannot be developed in response speed. A relationship between spontaneous direction derivating the compound (II) or (III) being added in a host liquid crystal and the spiral pitch of nematic phase thereof is as shown in Table 1. Compounds Direction of spontaneous polarization Direction of spiral of nematic phase Compound (II) - L + R Compound (III) + L - R Using the compound (II) in combination with the compound (III) enables the directions of spontaneous polarization to be identical with each other and also the spiral pitches of nematic phase to be reversed to each other, resulting in that increase of spontaneous polarization and improvement of response can largely be expected and excellent orientation property can be obtained. Therefore, the combination use of the compounds (II) and (III) in the host liquid crystal is preferable embodiment of the present invention. In this embodiment, either the compound (II) or the compound (III) function as a compound (b) of the present invention. The same effect is obtained by using, in the host liquid crystal, either the compound (II) or (III) with the other compound (b) which is reverse to the compound (II) or (III) in the direction of a helical pitch induced in a nematic phase. As the liquid crystal compound (c) such known compound may be applied as represented by the following general formulae (VII) to (IX): R⁷-Z¹-B¹-D¹-B²-Z²-R⁸ (VII) R⁷-Z¹-B¹-D¹-B²-D²-B³-Z²-R⁸ (VIII) wherein B¹, B² and B³ independently represent a six membered cyclic ring such as benzen ring, cyclohexane ring, bicyclo[2.2.2] octane ring, pyridine ring, pyrimidine ring, pyrazine ring, dioxacyclohexane ring, and naphthalene ring, provided that hydrogen atoms in the ring may be substituted with fluorine atom, chlorine atom, bromine atom, cyano group, nitro group, methyl group, methoxy group, trifluoromethyl group or the like. D¹ and D² each represents a single bond, or a group of -COO-, -OCO-, -CH=CH-, -C≡C-, -CH=CH-COO-,-OCO-CH=CH-, -CH₂CH₂-, -OCH₂-, -CH₂O-, -COS- or -SCO-. Z¹ and Z² each represents a single bond or a group of -COO-, -OCO-, -O-, -S-, -OCOO- or -CO-. R⁷ and R⁸ each represents an alkyl group with straight or branched chain having 1 to 15 carbon atoms which may contain an asymmetic carbon atom and may be substituted with fluorine atom, chlorine atom, bromine atom, cyano group, nitro group, methoxy group, trifluoromethyl group or the like. s represents an interger of 1 or 2.] Among them, the pyrimidine compound represented by the formula (IV): wherein R⁹ and R¹⁰ each represents an alkyl or alkoxy group having 1 to 15 carbon atoms and k denotes an integer of 0 or 1, and the compound represented by the formula (V): wherein R¹¹ and R¹² each represents an alkyl or alkoxy group having 1 to 15 carbon atoms with straight or branched-chain, and each represents a group or l, m and n each denotes an integer of 0 or 1, provided that the total of l, m and n is 1, 2 or 3, are liable to stably exhibit a smectic C phase and therefore may preferably be used in combination with the compounds (II) and/or (III) to produce a ferroelectric liquid crystal composition of good property. Next, examples of the ferroelectric liquid crystal device of the present invention will be detailed. Fig. 1 is a sectional view illustrating an example of a ferroelectric liquid crystal device of the present invention using a ferroelectric liquid crystal composition. Fig. 1 shows an example of transmission type display device, where indicated at 1 and 2 are insulating substrates; at 3 and 4 are conductive films, at 5 is an insulating film; at 6 is an orientation control layer; at 7 is a sealant; at 8 is a ferroelecric liquid crystal composition layer; and at 9 is a polarizer. Photo-transmission substrates are used for the insulating substrates 1 and 2, and generally glass substrates are employed therefor. The conductive films 3 and 4, which are usualy composed of a conductive thin films of In₂O₃, SnO₂ or ITO (Indium-Tin Oxide), are used as transparent electrodes and are each formed with a predetermined pattern on the insulating substrates 1 and 2. On the substrates are each formed an insulating film 5, but the film 5 may be omitted in some cases. As the insulating film 5, there may be used, for example, an inorganic thin film such as of SiO₂, SiN x , Al₂O₃, etc., and an organic thin film such as of polyimide, photoresist resin, polymer liquid crystal, etc. In the case that the insulating film 5 is composed of an inorganic thin film, the film 5 may be formed by vacuum deposition process, sputtering process, CVD (Chemical Vapor Deposition) process or solution coating process. In the case that the insulating film 5 is composed of an organic thin film, the film 5 may be formed by using a solution dissolving an organic substance or a solution of its precursor according to spin-coating process, immersion application process, screen printing process or roller application process and curing it at suitable conditions (heating, photoirradiation, etc.); the thin film may also be formed by LB (Langumuir-Blodgett) process as well as deposition process, sputtering process, CVD process. On the insulating film 5 is formed an orientation control layer 6. In the case where the insulating film 5 is omitted, the orientation control layer 6 may be formed directly on the conductive films 3 and 4. As the orientation control layer 6, inorganic layer may be used in some cases, while organic layer may be also used in other cases. In the case where an inorganic orientation control layer is used, oblique deposition of silicone oxide is commonly employed for the formation thereof. Rotating deposition may be also conducted. In the case where an organic orientation control layer is employed, nylon, polyvinylalcohol, polyimide and the like may be used. In this case, rubbing treatment is usually effected on the layer. The orientation control layer can also be formed by using a polymer liquid crystal or LB membrane with an intended orientation, by using magnetic field orientating technique or by using spacer edge method. Further, SiO₂, SiN x and the like may be formed by deposition process, sputtering process, CVD process and the like, on which rubbing treatment is effected for providing the orientation control layer. The two insulating substrates are laminated together through a predetermined clearance, and then the liquid crystal composition is injected therebetween to produce a ferroelectric liquid crystal device. In Fig.1, although the ferroelectric liquid crystal device of the present invention is explained as a switching element with one pixel, the ferroelectric liquid crystal device of the present invention may be also applied to a display device with a large capacity matrix wherein the wirings (electrodes) on the upper substrate together with the wirings (electrodes) on the lower substrate are inter-sectionally placed as to provide a matrix type device structure, as is shown in a plane schematic view of Fig. 2. Such a matrix-type liquid crystal device may be driven by various driving methods which have been proposed currently [See for example, Wakita, Kamimura, Onishi, Oba, Kobayashi, Ota,National Technical Report, 33, 44 (1987)]. REFERENCE EXAMPLE (Synthesis of compounds of the general formula(II)) Production of Intermediate 1 2.50g of a phenol derivative represented by the following formula: , 4.25g of R-(-)-epichlorohydrin (chemical purity: 98.5% or more, optical purity: 99% or more) and 20mg of benzyltriethylammonium chloride were dissolved in 3ml of dimethylformamide. To the solution was added dropwise 24% by weight sodium hydroxide aqueous solution (1.2 equivalents) at 60°C. The reaction was conducted for 40 minutes at the same temperature, and then the reaction mixture was cooled to room temperature followed by extraction with ether. After evaporating the solvent at reduced pressure, the residue was purified by a silica gel column chromatography to obtain 1.62g of a S-isomer of glycidyl ether represented by the following formula (Intermediate 1). mp: 90°C [α]D²⁵ : +4.44° (C=1.01, CH₂Cl₂) NMR(CDCl₃) δ: 0.50 - 3.00 (19H, m) 3.10 - 3.50 (1H, m) 3.80 - 4.30 (2H, m) 6.75 - 7.60 (8H, m) Production of Intermediate 2 5.28g of a phenol derivative represented by the following formula: ,11.55g of S-(+)-epichlorohydrin (chemical purity: 98.5% or more, optical purity: 99% or more), 3.00g of potassium tert-butoxide and 45ml of tert-butyl alcohol were mixed and stirred for 3 hours at 60°C. After evaporating the solvent from the reaction mixture at reduced pressure, the resultant was subjected to extraction with chloroform followed by evaporation of the solvent. The residue was purified by a silica gel column chromatography to obtain 5.82g of a R-isomer of glycidyl ether represented by the following formula (Intermediate 2). [α]D³¹ : -5.71° (C=1.66, CH₂Cl₂) NMR(CDCl₃) δ: 0.60 - 2.50 (17H, m) 2.60 - 2.95 (2H, m) 3.15 - 3.60 (1H, m) 3.80 - 4.30 (2H, m) 6.76 (2H, d, J=8.4Hz) 7.07 (2H, d, J=8.4Hz) Production of Intermediate 3 406mg of the optical active glycidyl ether obtained in Production of Intermediate 1, (R)-2,3-epoxypropyl 4-(trans-4-n-propylcyclohexyl)phenyl ether, 181mg of potassium tert-butoxide, 666mg of dimethyl nonylmalonate and 3ml of tert-butyl alcohol were mixed and refluxed for 2 hours under stirring. The reaction mixture was allowed to cool to room temperature. After 4N-hydrochloric acid was added dropwise to the mixture to adjust the pH to 1, the mixture was subjected to extraction with chloroform three times and washed once with saturated brine followed by evaporation of the solvent at reduced pressure. The residue was purified with a silica gel column chromatography to obtain two lactone derivatives, i.e., a (2R, 4R)-isomer of the following formula (79mg) and the corresponding (2S, 4R) isomer-(153mg) (Intermediate 3). [(2R, 4R)-isomer] Phase transition temperature: [α]D³² : -31.45° (C=1.43, CH₂Cl₂) NMR(CDCl₃) δ: 0.60 - 3.00 (39H, m) 4.0 - 4.2 (2H, m) 4.4 - 4.95 (1H, m) 6.76 (2H, d, J=8.0Hz) 7.10 (2H, d, J=8.0Hz) IR(KBr) 1762cm⁻¹ [(2S, 4R)-isomer] Phase transition temperature: [α]D²⁸ : -23.48° (C=1.03, CH₂Cl₂) NMR(CDCl₃) δ: 0.65 - 3.00 (39H, m) 4.0 - 4.2 (2H, m) 4.6 - 5.0 (1H, m) 6.76 (2H, d, J=8.0Hz) 7.10 (2H, d, J=8.0Hz) IR(KBr) 1762cm⁻¹ Production of Intermediate 4 370mg of the S-isomer of glycidyl ether obtained in Production of Intermediate 4, 442mg of diethyl n-propylmalonate, 134mg of potassium tert-butoxide and 3ml of tert-butyl alcohol were mixed and refluxed for 10 hours under stirring. The reaction mixture was allowed to cool to room temperature. After 4N-hydrochloric acid was added dropwise to the mixture to adjust the pH to 1, the mixture was washed with water and treated with methanol to give white crystals. The crystals were purified by a silica gel chromatography to obtain two γ-lactone derivatives, i.e., a (2S, 4S)-isomer of the following formula (240mg) and the corresponding (2R, 4S) -isomer (140mg)(Intermediate 4). [(2S, 4S)-isomer] Phase transition temperature: [α]D²⁶ : +32.67° (C=1.081, CH₂Cl₂) NMR(CDCl₃) δ: 0.70 - 3.00 (27H, m) 4.00 - 4.25 (2H, m) 4.40 - 4.85 (1H, m) 6.60 - 7.60 (8H, m) IR(KBr) 1762cm⁻¹ (C = 0) [(2R, 4S)-isomer] Phase transition temperature: [α]D²⁶ : +22.50° (C=0.504, CH₂Cl₂) NMR(CDCl₃) δ: 0.70 - 3.00 (27H, m) 4.00 - 4.25 (2H, m) 4.50 - 5.00 (1H, m) 6.60 - 7.60 (8H, m) IR(KBr) 1762cm⁻¹ (C = 0) Synthetic Example 1 To a solution of lithium diisopropylamide prepared by a customary method from 95mg of diisopropylamine, 0.52ml of n-butyl lithium (1.5mol/l in n-hexane) and 2ml of tetrahydrofuran was added 138mg of hexamethyl phosphoric triamide at -78°C. To the resultant was added dropwise a tetrahydrofuran solution (5ml) containing 269mg of the mixture of the γ-lactone derivatives of (2S, 4S)-isomer and (2R, 4S)-isomer which had been obtained in Production of Intermediate 4. The resultant was stirred for 40 minutes at the same temperature before adding dropwise 185mg of methyl iodide and then further stirred for 2 hours. The reaction mixture was added with a saturated aqueous solution of ammonium chloride, cooled to room temperature and subjected to extraction twice with ether followed by drying on magnesium sulfuric anhydride and evaporating the solvent. The residue was purified by a silica gel column chromatography to obtain γ-lactone derivatives, i.e, a (2S, 4S)-isomer of the following formula (253mg) and the corresponding (2R, 4S)-isomer (37mg). [(2S, 4S)-isomer] Phase transition temperature: [α]D²⁷ : +28.15° (C=1.058, CH₂Cl₂) NMR(CDCl₃) δ: 0.85 - 0.98 ( 6H, m) 1.18 - 1.73 (19H,m) 2.00 - 2.21 (2H, m) 2.62 (2H, t, J= 7.70Hz) 4.04 - 4.17 (2H, m) 4.71 - 4.80 (1H,m) 6.93 (2H, d, J = 8.79Hz) 7.21 (2H, d, J = 7.33Hz) 7.44 (2H, d, J = 8.06Hz) 7.49 (2H, d, J = 8.79Hz) [(2R, 4S)-isomer] Phase transition temperature: [α]D²⁷ : +20.76° (C=1.247, CH₂Cl₂) NMR(CDCl₃) δ: 0.86 - 0.98 (6H, m) 1.27 - 1.64 (19H, m) 2.03 (1H, dd, J = 8.8Hz, J = 12.8Hz) 2.35 (1H, dd, J = 7.5Hz, J = 12.8Hz) 2.62 (2h, t, J = 7.3 Hz) 4.06 - 4.18 ( 2H,m) 4.71 - 4.80 (1H, m) 6.95 (2H, d, J = 8.79Hz) 7.22 (2H, d, J = 8.43Hz) 7.45 (2H, d, J = 8.06Hz) 7.50 (2H, d, J = 8.79Hz) Synthetic Example 2 The same operation as the Example 1 was made except using 70mg of diisoprypylamine, 0.30ml of n-butyl lithium (1.5mol/l in n-hexane), 1ml of tetrahydrofuran, 100mg of hexamethyl phosphoric triamide, 130mg of methyl iodide and a tetrahydrofuran solution (2ml) containing 163mg of a mixture of a (2R,4R)-isomer and a (2S, 4R)-isomer of γ-lactone derivative obtained in Production Intermediate 3, to obtain γ-lactone derivatives, a (2R, 4R)-isomer of the following formula (130mg) and the corresponding (2S, 4R)-isomer (22mg). [(2R, 4R)-isomer] Phase transition temperature: [α]D²⁵ : +25.95° (C=1.013, CH₂Cl₂) NMR(CDCl₃) δ: 0.87 - 1.66 (34H, m) 1.85 (2H, s) 1.88 (2H, s) 2.05 (1H, dd, J= 6.96Hz, J=12.45Hz) 2.17 (1H, dd, J= 9.89Hz, J=12.82Hz) 2.42 (1H, t, J = 12.09Hz) 4.04 - 4.15 (2H, m) 4.71 - 4.81 (1H, m) 6.83 (2H, d, J = 8.43Hz) 7.13 (2H, d, J = 8.8Hz) (Synthesis of the compound of the formula (III)) Production of Intermediate 5 (Formula (VI d)) (i) synthesis of (R)-1.2-epoxynonane A suspension of 1.9g (10m mol) of cuprous iodide in 75ml of ether was placed in a reactor, to which suspension was added Grignard's reagent which had been prepared from 12.38g (75m mol) of hexylbromide and 2g (82.5m mol) of magnesium in 75ml of tetrahydrofuran at - 30°C under a nitride gas flow. After stirring for 30 minutes, the suspension was added with 4.63g of (R)-epichlorohydrin (50m mol, chemical purity more than 98.5%, optical purity more than 99%, [α]D²⁵=-34.0°, C=1.2,methanol) in 100ml of a mixture of tetrahydrofuran and ether (1 : 1) and stirred for 2 hours at the same temperature. After completion of the reaction, the reaction mixture was added with 100ml of saturated aqueous ammonium chloride, cooled to room temperature, subjected to extraction with ether and washed with saturated brine followed by drying the organic layer on magnesium sulfuric anhydride. The residue after evaporating the solvent at reduced pressure was purified by vacuum distillation to obtain 6.29g of (R)-chlorohydrin (35.2m mol, 70% yield) represented by the following formula. [α]D²⁵: +8.20 (neat) bp: 60 - 66°C (14mmHg, Kugelrohr) IR: νmax (neat) 3380cm⁻¹ NMR(CDCl₃) δ: 0.7 - 1.8 (15H, m) 2.2 (1H, brd) 3.3 - 3.9 (3H, m) A mixture of 4.99g of the above R-chlorohydrin and 50ml of 43% aqueous sodium hydroxide was refluxed for 2 hours under stirring. After completion of the reaction, the reaction product was subjected to extraction with ether and the extract was fractionated to obtain 3.97g of (R)-1,2-epoxy-n-nonane. [α]D²⁵: +10.87° NMR(CDCl₃) δ: 0.88 ( 3H, t) 1.2 - 1.6 (12H, m) 2.46 (1H, m) 2.74 (1H, m) 2.91 (1H, m) (ii) Synthesis of R-methylglycidyl ether To a solution of 0.98g of sulfuric acid and 100 ml of methanol, the solution having been refluxed under stirring, was added dropwise a solution of 23.66g of (R)-epichlorohydrin and 20ml of methanol used in the synthetic example 1 for 20 minutes, and the mixture was refluxed under stirring for 20 minutes. The reaction mixture was then cooled to 10 - 15°C, added dropwise with a solution of 31g of potassium hydroxide in 150ml of methanol, and stirred for 10 minutes. The reaction mixture was placed in a saturated brine and the product was extracted with methylene chloride. Then, the extract was fractinated (bp 110°C) to obtain 4.14g of (R)-methylglycidyl ether. [α]D²⁸: +6.49° (C = 1.086, CH₂Cl₂) NMR(CDCl₃) δ: 2.63 (1H, dd) 2.82 (1H, m) 3.16 (1H, m) 3.34 (1H, dd) 3.42 (3H, S) 3.71 (1H, dd) (iii) Synthesis of (R)-n-hexylglycidyl ether 6ml of n-hexanol was added dropwise to a mixture of 40g of sodium hydroxide, 24g of (R)-epichlorohydrin as used in Synthetic Example 1 and 400mg of tetra-butylammonium hydrogensulfate under cooling at 20 to 25°C. The reaction mixture was stirred for 3 hours at the same temperature, to which water was added. The product was extracted with ether, and the extract was purified by vacuum distillation to obtain 3.35g of (R)-n-hexylglycidyl ether. [α]D³⁷: +2.48° (C = 1.048, CHCl₃) bd: 52°C/4mmHg NMR(CDCl₃) δ: 0.89 (3H, m) 1.2 - 1.4 (6H, m) 1.58 (2H, m) 2.58 (1H, dd) 2.77 (1H, dd) 3.12 (1H, m) 3.36 (1H, dd) 3.48 (2H, m) 3.70 (1H, dd) (iv) Synthesis of (S)-allylglycidyl ether To a solution of 0.5g of sulfuric acid in 100ml of allyl alcohol, the solution having been refluxed under stirring, was added dropwise a solution of 19.54g of (S)-epichlorohydrin (more than 98.5% in chemical purity, more than 99% in optical purity ([α]D²⁵ = +34.0°, C = 1.2, methanol)) in 20ml of allyl alcohol. The mixture was refluxed for further 20 minutes under stirring. The reaction mixture was cooled to 10 - 15°C, to which a solution of 25.2g of potassium hydroxide in methanol (130ml) was added dropwise for 10 minutes. The reaction mixture was placed in a saturated brine and the product was extracted with methylene chloride and fractionated to obtain 9.51g of (S)-allylglycidyl ether. [α]D³⁰: -9.24° (C = 1.075, CH₂Cl₂) NMR(CDCl₃) δ: 2.61 (1H, dd) 2.80 (1H, t) 3.16 (1H, m) 3.40 (1H, dd) 3.73 (1H, dd) 4.05 (1H, m) 5.20 (1H, dd) 5.29 (1H, d) 5.91 (1H, m) Production of Intermediate 6 (Formula (VI b)) (i) Synthesis of 4-(4'-n-heptyl)-biphenyl acetate 10.85g of 4-acetyl-4'-n-heptylbiphenyl and 2.36g of sulfur were refluxed in 20ml of morpholine for 9 hours under stirring. To the reaction mixture was added a solution of 29.5g of sodium hydroxide, 30ml of water and 100ml of ethanol, and the reaction mixture was stirred for 9 hours. Then, the reaction mixture was placed in water, to which hydrochloric acid was added to acidify the medium to precipitate a solid. The solid was then subjected to filtration to obtain 13.51g of a crude product. The crude product was purified by a silica gel column chromatography to obtain 8.29g of the objective compound. mp: 154 - 162°C IR (Nujol): 1724cm⁻¹ NMR(CDCl₃) δ: 0.88 (3H, md) 1.2 - 1.4 (8H, m) 1.64 (2H, m) 2.63 (2H, t) 3.68 (2H, s) 7.23 (2H, d) 7.33 (2H, d) 7.48 (2H, d) 7.54 (2H, d) (ii) Synthesis of 4-(4'-n-nonyloxy)-biphenyl acetate 10.14g of 4-acetyl-4'-n-nonyloxybiphenyl and 1.536g of sulfur were refluxed in 20ml of morpholine for 15 hours under stirring. A solution of 25g of sodium hydroxide, 65ml of water and 100ml of ethanol was added to the reaction mixture, which was stirred for 9 hours and then placed in water to be acidified by the addition of hydrochloric acid to obtain a precipitate. The precipitated solid was subjected to filtration to obtain a crude product which was then purified by a silica gel column chromatography to obtain 12.84g of the objective compound. mp: 175 - 176°C IR (Nujol): 1704cm⁻¹ NMR(CDCl₃) δ: 0.89 (3H, m) 1.2 - 1.5 (12H, m) 1.80 (2H, m) 3.69 (2H, s) 3.99 (2H, t) 6.95 (2H, d) 7.33 (2H, d) 7.49 (2H, d) 7.52 (2H, d) (iii) Synthesis of 4-(4'-n-butyltranscyclohexyl) phenyl acetate 5g of 4-(4'-n-butyl-trans-cyclohexyl) acetophene and 1.24g of sulfur were refluxed in 7.5ml of morpholine for 11 hours under stirring. A solution of 16.75g of sodium hydroxide, 43.4ml of water and 67ml of ethanol was added to the reaction mixture which was then stirred for 7 hours and placed in water to be acidified by the addition of hydrochloric acid. The product was extracted with ether and the crude product extracted was purified by a silica gel column chromatography to obtain 3.33g of the objective compound. mp: 72 - 74°C IR (Nujol): 1718cm⁻¹ NMR(CDCl₃) δ: 0.89 - 1.5 (14H, m) 1.86 (4H, m) 2.44 (1H, t) 3.59 (2H, s) 7.17 (4H, m) Production of Intermediate 7 (Formula (IV c)) Synthesis of 2-(4'-nonyloxy-4-biphenyl) propionic acid In a vessel cooled at -78°C and containing 506mg of diisopropylamine and 10ml of tetrahydrofuran was added dropwise a solution of 15% n-butyllithium in 3ml of hexane. After raising temperature gradually to 0°C, the mixture was stirred for 30 minutes. To the reaction mixture was added dropwise a solution of 708mg of 4-(4'-n-nonyloxy)-biphenyl acetate prepared in Production of Intermediate 6 and 8ml of tetrahydrofuran, and the mixture was stirred for 1 hour. To the reaction mixture after being cooled to -78°C was added dropwise a solution of 426mg of methyl iodide and 2ml of tetrahydrofuran. The reaction mixture was stirred for 6 hours with temperature being gradually raised to room temperature, and thereafter water was added followed by acidification by hydrochloric acid. The reaction mixture was subjected to extraction with chloroform to obtained 730mg of the objective compound. NMR(CDCl₃) δ: 0.89 (3h, t) 1.2 - 1.6 (12H, m) 1.55 (3H, d) 1.80 (2H, m) 3.79 (1H, q) 3.99 (2H, t) 6.95 (2H, d) 7.37 (2H, d) 7.4 - 7.6 (4H, m) Synthesis 1 of the compound for liquid crystal composition In a vessel cooled at -78°C and containing 113mg of diisopropylamine and 2ml of tetrahydrofuran was added dropwise a solution of 15% n-butyllithium in 0.7ml of hexane. After raising temperature gradually to 0°C, the mixture was stirred for 30 minutes. To the reaction mixture was added dropwise a tetrahydrofuran solution (2ml) containing 177mg of 4-(4'-n-nonyloxy)-biphenyl acetate prepared in Production of Intermediate 6, and the mixture was stirred for 1 hour. To the reaction mixture after being cooled to -78°C was added dropwise a tetrahydrofuran solution (2ml) containing 35mg of (R)-1,2-epoxynonane prepared in Production of Intermediate 5. The reaction mixture was stirred for 6 hours with temperature being gradually raised to room temperature, and thereafter water was added followed by acidification by hydrochloric acid. The product was extracted with chloroform, which extract was added with dry benzene and catalytic sulfuric acid, and stirred for 6 hours under heating with benzene being evaporated gradually. After cooled, the resultant was subjected to vacuum distillation, and then the residue was purified by a silica gel chromatography to obtain the following γ-lactone derivatives, a (2R, 4R)-isomer (35mg) and the corresponding (2S, 4R)-isomer (104mg). [(2R, 4R)-isomer] Phase transition temperature: [α]D³⁴ : -5.42° (C=1.66, CH₂Cl₂) NMR(CDCl₃) δ: 0.89 (6H, m) 1.2 - 1.9 (26H, m) 2.05 (1H, td) 2.74 (1H, ddd) 3.88 (1H, dd) 3.98 (2H, t) 4.48 (1H, m) 6,95 (2H, d) 7.31 (2H, d) 7.48 (2H, d) 7.53 (2H, d) IR(Nujol): 1750cm⁻¹ [(2S, 4R)-isomer] Phase transition temperature : [α]D³⁴ : +29.33° (C=0.95, CH₂Cl₂) NMR(CDCl₃) δ: 0.89 (6H, m) 1.2 - 1.9 (26H, m) 2.41 (1H, ddd) 2.53 (1H, dt) 3.93 (1H, dd) 3.99 (2H, t) 4.66 (1H, m) 6.96 (2H, d) 7.32 (2H, d) 7.48 (2H, d) 7.53 (2H, d) IR(Nujol): 1750cm⁻¹ Synthesis 2 of the compound for liquid crystal composition In a solution cooled at -78°C and containing 339mg of diisopropylamine and 6ml of tetrahydrofuran was added dropwise a solution of 15% n-butyllithium in 3ml of hexane. After raising temperature gradually to 0°C, the mixture was stirred for 30 minutes. To the reaction mixture was added dropwise a tetrahydrofuran solution (5ml) containing 531mg of 4-(4'-n-nonyloxy)-biphenyl acetate prepared in Production of Intermediate 6, and the mixture was stirred for 1 hour. To the reaction mixture after being cooled to -78°C was added dropwise a tetrahydrofuran solution (1ml) containing 256mg of (R)-n-hexylglycidyl ether prepared in Production of Intermediate 5. The reaction mixture was stirred for 6 hours with temperature being gradually raised to room temperature, and thereafter water was added followed by acidification by hydrochloric acid. The product was extracted with chloroform, which extract was added with dry benzene and catalytic sulfuric acid and stirred for 6 hours under heating with benzene being evaporated gradually. After cooled, the resultant was subjected to vacuum distillation, and then the residue was purified by a silica gel chromatography to obtain the following γ-lactone derivatives, a (2R, 4S)-isomer (259mg) and the corresponding (2S, 4S)-isomer (207mg). [(2R, 4S)-isomer] Phase transition temperature: [α]D²³ : +1.36° (C=1.06, CH₂Cl₂) NMR(CDCl₃) δ: 0.89 (6H, m) 1.2 - 1.5 (18H, m) 1.58 (2H, m) 1.78 (2H, m) 2.32 (1H, td) 2.66 (1H, ddd) 3.51 (2H, t) 3.61 (1H, dd) 3.70 (1H, dd) 3.89 (1H, dd) 3.97 (2H, t) 4.63 (1H, m) 6.95 (2H, d) 7.23 (2H, d) 7.48 (2H, d) 7.52 (2H, d) [(2S, 4S)-isomer] Phase transition temperature: [α]D³² : +29.27° (C=1.16, CH₂Cl₂) NMR(CDCl₃) δ: 0.89 (6H, m) 1.2 - 1.5 (18H, m) 1.58 (2H, m) 1.78 (2H, m) 2.47 (1H, td) 2.65 (1H, ddd) 3.49 (2H, t) 3.59 (1H, dd) 3.63 (1H, dd) 3.97 (2H, t) 4.06 (1H, t) 4.72 (1H, m) 6.94 (2H, d) 7.30 (2H, d) 7.48 (2H, d) 7.52 (2H, d) Synthesis 3 of the compound for liquid crystal composition In a vessel cooled at -78°C and containing 505mg of diisopropylamine and 10ml of tetrahydrofuran was added dropwise a solution of 15% n-butyllithium in 3ml of hexane. After raising temperature gradually to 0°C, the mixture was stirred for 30 minutes. To the reaction mixture was added dropwise a tetrahydrofuran solution (6ml) containing 700mg of 4-(4'-n-heptyl)-biphenyl acetate prepared in Production of Intermediate 6, and the mixture was stirred for 1 hour. To the reaction mixture after being cooled to -78°C was added dropwise a solution of 260mg of a commercially available (R)-1,2-epoxyheptane ([α]D²⁵+15.0°〈neat〉) and 1ml of tetrahydrofuran. The reaction mixture was stirred for 6 hours with temperature being gradually raised to room temperature, and thereafter water was added followed by acidification by hydrochloric acid. The product was extracted with chloroform, which extract was added with dry benzene and catalytic sulfuric acid, and stirred for 6 hours under heating with benzene being evaporated gradually. After cooled, the resultant was subjected to vacuum distillation, and then the residue was purified by a silica gel chromatography to obtain the following γ-lactone derivatives, a (2R, 4S)-isomer (330mg) and the corresponding (2S, 4S)-isomer (383mg). [(2R, 4R)-isomer] Phase transition temperature: [α]D²⁷ : -5.66° (C=1.089, CH₂Cl₂) NMR(CDCl₃) δ: 0.90 (6H, m) 1.2 - 1.85 (18H, m) 2.08 (1H, dt) 2.63 (2H, t) 2.78 (1H, m) 3.92 (1H, dd) 4.51 (1H, m) 7.25 (2H, d) 7.34 (2H, d) 7.49 (2H, d) 7.57 (2H, d) [(2S, 4R)-isomer] Phase transition temperature: [α]D²⁸ : +33.48° (C=1.027, CH₂Cl₂) NMR(CDCl₃) δ: 0.90 (6H, m) 1.2 - 1.9 (18H, m) 2.35 - 2.68 (4H, m) 3.94 (1H, dd) 4.67 (1H, m) 7.25 (2H, d) 7.34 (2H, d) 7.48 (2H, d) 7.57 (2H, d) Synthesis 4 of the compound for liquid crystal composition In a vessel cooled at -78°C and containing 505mg of diisopropylamine and 10ml of tetrahydrofuran was added dropwise a solution of 15% n-butyllithium in 3ml of hexane. After raising temperature gradually to 0°C, the mixture was stirred for 30 minutes. To the reaction mixture was added dropwise a tetrahydrofuran solution (3ml) containing 600mg of 4-(4'-n-butyl-trans-cyclohexyl )-phenyl acetate prepared in Production of Intermediate 6, and the mixture was stirred for 1 hour. To the reaction mixture after being cooled to -78°C was added dropwise a tetrahydrofuran solution (1ml) containing 275mg of (S)-allylglycidyl ether prepared in Production of Intermediate 5. The reaction mixture was stirred for 6 hours with temperature being gradually raised to room temperature, and thereafter water was added followed by acidification by hydrochloric acid. The product was extracted with chloroform, which extract was added with dry benzene and catalytic sulfuric acid, and stirred for 6 hours under heating with benzene being evaporated gradually. After cooled, the resultant was subjected to vacuum distillation, and then the residue was purified by a silica gel chromatography to obtain the following -lactone derivatives, a (2S, 4R)-isomer (320mg) and the corresponding (2R, 4R)-isomer (246mg). [(2S, 4R)-isomer] Phase transition temperature: [α]D²⁶ : -3.22° (C=1.033, CH₂Cl₂) NMR(CDCl₃) δ: 0.8 - 1.5 (14H, m) 1.86 (4H, m) 2.30 (1H, dt) 2.45 (1H, m) 2.68 (1H, m) 3.62 - 3.76 (2H, m) 3.86 (1H, dd) 4.09 (2H, m) 4.65 (1H, m) 5.22 (1H, m) 5.30 (1H, m) 5.91 (1H, m) 7.20 (4H, s) [(2R, 4R)-isomer] Phase transition temperature: [α]D²⁸ : -40.42° (C=1.024, CH₂Cl₂) NMR(CDCl₃) δ: 0.80 - 1.5 (14H, m) 1.86 (4H, m) 2.37 - 2.55 (2H, dt) 2.65 (1H, m) 3.60 - 3.76 (2H, m) 3.95 - 4.1 (3H, m) 4.75 (1H, m) 5.22 (1H, m) 5.29 (1H, m) 5.91 (1H, m) 7.19 (4H, s) Synthesis 5 of the compound for liquid crystal composition In a vessel cooled at -78°C and containing 505mg of diisopropylamine and 10ml of tetrahydrofuran was added dropwise a solution of 15% n-butyllithium in 3ml of hexane. After raising temperature gradually to 0°C, the mixture was stirred for 30 minutes. To the reaction mixture was added dropwise a tetrahydrofuran solution (3ml) containing 600mg of 4-(4'-n-butyltranscyclohexyl)-phenyl acetate prepared in Production of Intermediate 6, and the mixture was stirred for 1 hour. To the reaction mixture after being cooled to -78°C was added dropwise a solution of 477mg of a commercially available (R)-1,2-epoxytridecane ([α]D²⁵ +9.8° (neat)) and 1ml of tetrahydrofuran. The reaction mixture was stirred for 6 hours with temperature being gradually raised to room temperature, and thereafter water was added followed by acidification by hydrochloric acid. The product was extracted with chloroform, which extract was added with dry benzene and catalytic sulfuric acid, and stirred for 6 hours under heating with benzene being evaporated gradually. After cooled, the resultant was subjected to vacuum distillation, and then the residue was purified by a silica gel chromatography to obtain the following γ-lactone derivatives, a (2S, 4R)-isomer (320mg) and the corresponding (2R, 4R)-isomer (246mg). [(2R, 4R)-isomer] Phase transition temperature: [α]D²⁸ : -3.57° (C=1.035, CH₂Cl₂) NMR(CDCl₃) δ: 0.8 - 1.9 (41H, m) 2.02 (1H, dt) 2.45 (1H, m) 2.72 (1H, m) 3.83 (1H, dd) 4.47 (1H, m) 7.20 (4H, s) [(2S, 4R)-isomer] Phase transition temperature : [α]D²⁴ : +31.02° (C=1.038, CH₂Cl₂) NMR(CDCl₃) δ: 0.80 - 1.9 (41H, m) 2.28 - 2.55 (3H, m) 3.87 (1H, dd) 4.62 (1H, m) 7.19 (4H, s) Synthesis 6 of the compound for liquid crystal composition In a vessel cooled at -78°C and containing 505mg of diisopropylamine and 10ml of tetrahydrofuran was added dropwise a solution of 15% n-butyllithium in 3ml of hexane. After raising temperature gradually to 0°C, the mixture was stirred for 30 minutes. To the reaction mixture was added dropwise a tetrahydrofuran solution (3ml) containing 700mg of 4-(4'-n-heptyl)-biphenyl acetate prepared in Production of Intermediate 6, and the mixture was stirred for 1 hour. To the reaction mixture after being cooled to -78°C was added dropwise a solution of 212mg of (R)-methylglycidyl ether and 1ml of tetrahydrofuran. The reaction mixture was stirred for 6 hours with temperature being gradually raised to room temperature, and thereafter water was added followed by acidification by hydrochloric acid. The product was extracted with chloroform, which extract was added with dry benzene and catalytic sulfuric acid, and stirred for 6 hours under heating with benzene being evaporated gradually. After cooled, the resultant was subjected to vacuum distillation, and then the residue was purified by a silica gel chromatography to obtain the following γ-lactone derivatives, a (2R, 4S)-isomer (113mg) and the corresponding (2S, 4S)-isomer (255mg). [(2R, 4S)-isomer] Phase transition temperature: [α]D²¹ : +0.35° (C=1.01, CH₂Cl₂) NMR(CDCl₃) δ: 0.88 (3H, m) 1.2 - 1.45 (8H, m) 1.65 (2H, m) 2.34 (1H, dt) 2.6 - 2.8 (3H, m) 3.46 (3H, s) 3.67 (2H, s) 3.94 (1H, dd) 4.67 (1H, m) 7.25 (2H, d) 7.36 (2H, d) 7.49 (2H, d) 7.58 (2H, d) [(2S, 4S)-isomer] Phase transition temperature: [α]D²³ : +34.16° (C=1.013, CH₂Cl₂) NMR(CDCl₃) δ: 0.88 (3H, m) 1.2 - 1.45 (8H, m) 1.65 (2H, m) 2.52 (1H, dt) 2.59 - 2.75 (4H, m) 3.44 (3H, s) 3.65 (2H, m) 4.08 (1H, t) 4.77 (1H, m) 7.24 (2H, d) 7.33 (2h, d) 7.48 (2H, d) 7.57 (2H, d) Synthesis 7 of the compound for liquid crystal composition In a vessel cooled at -78°C and containing 505mg of diisopropylamine and 10ml of tetrahydrofuran was added dropwise a solution of 15% n-butyllithium in 3ml of hexane. After raising temperature to 0°C, the mixture was stirred for 1 hour. To the reaction mixture was added dropwise a tetrahydrofuran solution (3ml) containing 682mg of 4-(4'-n-heptyl)-biphenyl acetate prepared in Production of Intermediate 6, and the mixture was stirred for 1 hour. To the reaction mixture after being cooled to -78°C was added dropwise a solution of 445mg of (S)-n-hexylglycidyl ether in 1ml of tetrahydrofuran. The reaction mixture was stirred for 6 hours with temperature being gradually raised to room temperature, and thereafter water was added followed by acidification by hydrochloric acid. The product was extracted with chloroform, which extract was added with dry benzene and catalytic concentrated sulfuric acid, and stirred for 6 hours under heating with benzene being evaporated gradually. After cooled, the resultant was subjected to vacuum distillation, the residue was purified by a silica gel chromatography to obtain the following γ-lactone derivatives, a (2S, 4R)-isomer (401mg) and the corresponding (2R, 4R)-isomer (465mg). [(2S, 4R)-isomer] Phase transition temperature: [α]D²² : -2.17° (C=1.07, CH₂Cl₂) NMR(CDCl₃) δ: 0.86 - 0.91 (6H, m) 1.29 - 1.61 (18H, m) 2.28 - 2.42 (1H, m) 2.61 - 2.76 (3H, m) 3.52 (2H, t, J = 6.60Hz) 3.61 - 3.75 (2H, m) 3.92 (1H, dd, J = 9.16, 12.09Hz) 4.62 - 4.67 (1H, m) 7.24 (2H, d, J = 8.06Hz ) 7.35 (2H, d, J = 8.42Hz ) 7.48 (2H, d, J = 8.42Hz ) 7.57 (2H, d, J = 8.06Hz ) [(2S, 4R)-isomer] Phase transition temperature: [α]D²² : -37.95° (C=1.003, CH₂Cl₂) NMR(CDCl₃) δ: 0.86 - 0.90 (6H, m) 1.29 - 1.60 (18H, m) 2.45 - 2.57 (1H, m) 2.61 - 2.74 (3H, m) 3.51 (2H, t, J = 6.68Hz) 3.60 - 3.75 (2H, m) 4.09 (1H, t, J = 9.35Hz) 4.74 - 4.78 (1H, m) 7.24 (2H, d, J = 8.06Hz ) 7.33 (2H, d, J = 8.43Hz ) 7.48 (2H, d, J = 8.43Hz ) 7.57 (2H, d, J = 8.06Hz ) Synthetic Example 3 In a vessel cooled at -78°C and containing 505mg of diisopropylamine and 10ml of tetrahydrofuran was added dropwise a solution of 15% n-butyllithium in 3ml of hexane. After raising temperature gradually to 0°C, the mixture was stirred for 30 minutes. To the reaction mixture was added dropwise a tetrahydrofuran solution (8ml) containing 730mg of 2-(4'-n-nonyloxy-4-biphenyl) propionic acid prepared in Production of Intermediate product 7, and the mixture was stirred for 1 hour. To the reaction mixture after being cooled to -78°C was added dropwise a solution of 312mg of (R)-1,2-epoxynonane (see Production of Intermediate 5) and 1ml of tetrahydrofuran. The reaction mixture was stirred for 6 hours with temperature being gradually raised to room temperature, and thereafter water was added followed by acidification by hydrochloric acid. The product was extracted with chloroform, which extract was added with dry benzene and catalytic sulfuric acid, and stirred for 6 hours under heating with benzene being evaporated gradually. After cooled, the resultant was subjected to vacuum distillation, and then the residue was purified by a silica gel chromatography to obtain the following γ-lactone derivatives, a (2R, 4R)-isomer (408mg) and the corresponding (2S, 4R)-isomer (280mg). [(2R, 4R)-isomer] Phase transition temperature: [α]D²⁵ : +13.24° (C=1.06, CH₂Cl₂) NMR(CDCl₃) δ: 0.88 (6H, m) 1.2 - 1.7 (24H, m) 1.67 (3H, s) 1.79 (2H, m) 2.33 (1H, dd) 2.50 (1H, dd) 3.99 (2H, t) 4.57 (1H, m) 6.96 (2H, d) 7.45 - 7.55 (6H, m) [(2S, 4R)-isomer] Phase transition temperature: [α]D²³ : +25.11° (C=1.017, CH₂Cl₂) NMR(CDCl₃) δ: 0.88 (6H, m) 1.15 - 1.70 (24H, s) 1.61 (3H, s) 1.78 (2H, m) 1.99 (1H, dd) 2.77 (1H, dd) 3.99 (2H, t) 4.24 (1H, m) 6.96 (2H, d) 7.35 - 7.60 (6H, m) EXAMPLES Liquid crystal compositions were prepared by using the compounds produced in accordance with the aforesaid Synthetic Examples and represented by Nos. 1 to 3 and 14 and 15 of the formula (I), and by Nos. 4 to 13 in Tables 2 and 3. Example 1 Produced was liquid crystal composition No. 16 of non-chiral smectic C phase shown in Table 4. To the liquid crystal composition No. 16 was added 2 wt% of each of the compounds Nos. 1 to 15 shown in Tables 2 and 3 to form 15 kinds of ferroelectric liquid crystal compositions. Next, on two glass substrates were each deposited ITO film and further formed SiO₂ on which PVA film was coated and rubbing was effected thereover. Then, the two glass substrates were laminated with each other as having 2µm of cell thickness and the same rubbing direction, and the 15 kinds of ferroelectric liquid crystal compositions corresponding to the compounds Nos. 1 to 15 were each injected between the substrates. After injection of the compositions, the cell was first heated to the temperature enabling to the liquid crystal composition to change to isotropic liquid, and then cooled to room temperature at 1°C/min to obtain a ferroelectric liquid crystal device of good orientation. Properties of the ferroelectric liquid crystal device are as shown in Table 5. Properties of Ferroelectric Liquid Crystal Compositions provided by addition of 2wt% optically active compound into liquid crystal composition No.16 Added Compound No. Phase Transition temperature (°C) Response speed (µ sec) Tilt angle Θ Memory angle 2Θ S C →S A →N→I 1 · 50 · 61 · 67 · 116 21 12 2 · 48 · 60 · 66 · 90 21 13 3 · 45 · 59 · 67 · 101 20 11 4 · 52 · 61 · 68 · 100 21 12 5 · 52 · 62 · 69 · 138 21 12 6 · 53 · 62 · 69 · 325 8 11 7 · 51 · 61 · 68 · 750 10 15 8 · 50 · 60 · 68 · 139 20 14 9 · 52 · 60 · 67 · 146 19 11 10 · 51 · 60 · 67 · 230 17 11 11 · 53 · 61 · 68 · 132 19 14 12 · 53 · 61 · 68 · 214 16 12 13 · 49 · 59 · 67 · 236 19 12 14 · 50 · 60 · 67 · 266 19 13 15 · 47 · 59 · 66 · 124 18 11 The response speed was measured in a time when transmitted light changes by 50% from application of rectangular wave voltage of V P-P = 20V. Example 2 The compounds Nos. 1 to 15 shown in Tables 2 and 3 and those Nos. 17 to 34 shown in Tables 6 to 8 were used in combination to prepare the ferroelectric compositions Nos. 35 and 36 shown in Table 9 as having a sufficiently longer sprical pitch of nematic phase in comparison with cell thickness. Compounds Composition No. 35 Composition No. 36 No. 1 1.8 1.1 No. 2 2.8 1.6 No. 9 3.2 1.9 No.17 4.1 N0.18 2.1 No.19 6.2 10.7 No.20 2.6 1.5 No.21 9.7 10.3 No.22 13.3 7.8 NO.23 6.2 9.0 No.24 12.4 7.3 No.25 12.3 25.6 No.26 6.2 3.6 No.27 2.6 1.5 No.28 3.5 2.0 No.29 3.5 2.0 No.30 2.6 1.5 No.31 3.5 2.0 No.32 3.5 2.0 No.33 2.6 1.5 No.34 1.5 2.1 Ferroelectric liquid crystal devices were fabricated similarly with the Example 1 and evaluated in their properties. Table 10 shows phase transition temperature and properties of the ferroelectric liquid crystal compositions. No. Phase transition temperature ( °C) S C →S A →N→I Response speed (µsec) Tilt angle Θ(deg) Memory angle 2Θ(deg) 35 58 69 72 33 24 17 36 55 67 72 58 24 14 The ferroelectric liquid crystal devices has a longer spiral pitch of nematic phase to thereby achieve good orientation and high speed response, so that they are applicable to a ferroelectric liquid crystal device of a large capacity.

Claims: A ferroelectric liquid crystal device having a pair of substrates each provided with voltage applying means, an orientation control layer formed on at least one of the substrates, and a layer of ferroelectric liquid crystal composition disposed between the pair of substrates, the ferroelectric liquid crystal composition comprising at least one compound (a) having an optically active group of the formula (I): , at least one compound (b) which is reverse to the compound (a) in the direction of a helical pitch induced in a nematic phase and at least one liquid crystal compound (c) exhibiting a smectic C phase, the liquid crystal composition exhibiting at least a smectic C phase, smectic A phase and nematic phase. A device as defined in claim 1 wherein the compound (a) is an optically active compound of the formula (II): wherein A¹,A²,A³ are each a group containing a 6-membered ring and having or not having a substituent, X is -O-, -COO-,-OCO- or a single bond, Y¹ and Y² are each -COO-, -OCO, -OCH₂-, -CH₂O-, -CH₂CH₂-, -CH=CH-, -C≡C- or a single bond, R¹and R² are each straight-chain or branched-chain alkyl or alkoxy group having 1 to 15 carbon atoms, and p, q and r are each an integer of 0 or 1. A device as defined in claim 1 wherein the compound (a) is an optically active compound of the formula (III): wherein A⁴, A⁵, A⁶ are each a group containing a 6-membered ring and having or not having a substituent, Y⁴ and Y⁵ are each -COO-, -OCO-, -OCH₂-, -CH₂O-, -CH₂CH₂-, -CH=CH-, -C≡C- or a single bond, R³ and R⁴ are each straight-chain or branched-chain alkyl or alkoxy group having 1 to 15 carbon atoms, and p, q and r are each an integer of 0 or 1. A device as defined in claim 1 in which the ferroelectric liquid crystal composition comprises the optically active compounds (II) and (III) as defined in claims 2 and 3, one of the compounds being act as the compound (a) and another being act as the compound (b). A device as defined in claim 1 in which the liquid crystal compound (c) is represented by the formula (IV): wherein R⁹ and R¹⁰ each represents an alkyl or alkoxy group having 1 to 15 carbon atoms and k denotes an integer of 0 or 1. A device as defined in claim 1 in which the liquid crystal compound (c) is represented by the formula (V): wherein R¹¹ and R¹² each represents an alkyl or alkoxy group having 1 to 15 carbon atoms with straight or branched-chain, and each represents a group or l, m and n each denotes an integer of 0 or 1, provided that the total of l, m and n is 1, 2 or 3. A device as defined in claim 2,3 or 4 in which the content of the compounds (II) and (III) are each 0.5 to 30 wt% in the ferroelectric liquid crystal composition. A device as defined in claim 7 in which the content of the compounds (II) and (III) are each 0.5 to 10 wt% in the ferroelectric liquid crystal composition.

Inventors: FUNADA FUMIAKI, KITAMURA TOHRU, KODEN MITSUHIRO, KURATATE TOMOAKI, SAKAGUCHI KAZUHIKO, SHIOMI YUTAKA, FUNADA, FUMIAKI, KITAMURA, TOHRU, KODEN, MITSUHIRO, KURATATE, TOMOAKI, SAKAGUCHI, KAZUHIKO, SHIOMI, YUTAKA
Applicants: DAISO CO LTD, SHARP KK, DAISO CO., LTD., SHARP KABUSHIKI KAISHA
Application year: 1991
Main classification: C09K19
IPC codes: G02F1, C09K19