Composition comprising a novel alicyclic compound, a process for the preparation thereof, a curable composition, and a photo-polymerizable composition

Abstract: Disclosed are a composition, and a process for preparation thereof, which composition comprises a novel alicyclic compound and an epoxidized compound thereof represented respectively by formulae (I) and (II) wherein Y¹ represents at least one of the structural groups Y² represents at least one of the the structural groups R a and R b each represent hydrogen or a methyl group, m represents a natural number of from 1 to 7, and n represents a natural number of from 1 to 20. The composition (II) is a multi-functional alicyclic epoxidized compound, which has a property of being high in epoxy group density in a molecule compared with alicyclic conventional epoxy resins, which can provide resins having wide range properties from being hard to being soft.

Description: FIELD OF THE INVENTION The present invention relates to a composition which comprises a novel lactone-modified alicyclic compound, and a novel epoxidized compound thereof, it also relates to a process for its preparation, and further relates to a curable composition and a photo-polymerizable composition. BACKGROUND OF THE INVENTION Hitherto, the alicyclic epoxy resin Y²-CO-O-CH₂-Y² (IV) (wherein Y² represents at least one group selected from has been well-known, and used as a component in a composition for coating, or as a material for electric field, which was used by curing with a polymeric compound having carboxyl groups, with hydrides thereof, or with a compound having hydroxyl groups and or amino groups, and/or with a curing agent. However, the alicyclic epoxy resin (IV) can not provide a diepoxide having a high molecular weight by curing with the above described polymeric compound. Furthermore, the epoxy groups of the alicyclic epoxy resin have the disadvantage of being low in reactivity because of the short intramolecular distance between its ester group and its epoxy group. On the other hand, the compound (V) Y²-CH₂-O-CO-C(CH₂)₄-COO-CH₂-Y² (V) (wherein Y² represents at least one group selected from has also been used in the same fields of uses as described hereinabove. However, the alicyclic epoxy resin (V) lacks flexibility, because it is a monomer having no such distribution of molecular weights as in the case of an oligomer. As a result of an intensive investigation, the inventors of this invention have now found that it is possible not only to solve the problems as described hereinabove, but also to add flexibility, reactivity, and heat resistance in epoxy resins. SUMMARY OF THE INVENTION The present invention is the result of intensive research aiming at developing an excellent component for a coating composition, a curable composition, and a photo-polymerizable composition. It is a primary object of the present invention to solve the problems of the conventional coating compositions, particularly insufficient reactivity and insufficient toughness of the coating layers. The present invention provides a composition and a process for its preparation, said composition consisting essentially of a compound represented by formula (I) wherein Y¹ represents at least one of the structural groups R a and R b each represents hydrogen or a methyl group, m represents a natural number of 1 to 7, and n represents a natural number of 1 to 20. The present composition has excellent properties suitable for use as a resin component, particularly after its transformation in epoxy form, as an epoxy resin component for coating materials, such as a composition for an electro-deposition coating, a powder composition for coating, a baking composition for coating with a high solid content, etc. Furthermore, the present composition can be used as a composition capable of curing in low temperature conditions by addition of a composition composed of a polysiloxane type macromonomer and an organic aluminum or a chelate compound of an organic zirconium compound to obtain an excellent outer appearance and an excellent ductility of the coating layers. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a ¹H-NMR(Nuclear Magnetic Resonance) chart, Figure 2 is an IR(Infra-Red) spectrum chart, Figure 3 is a GPC(Gel Permeation Chromatography) chart relating to the composition obtained in Example 1, respectively. Figure 4 is a ¹H-NMR chart, and Figure 5 is an IR spectrum chart relating to the composition obtained in Example 10, respectively. DETAILED DESCRIPTION OF THE INVENTION The present invention is described hereinafter in more detail. According to a first aspect of the present invention, there is provided a composition comprising, and preferably consisting essentially of, an alicyclic compound represented by general formula (I) described hereinafter. In the formula (I), is a lactone derived ester-bonding unit, Y¹ represents at least one group of , derived from 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate , derived from 1-methyl-1,2,5,6-tetrahydrobenzyl-1-methyl-1,2,5,6-tetrahydrobenzoate, and , derived from 6-methyl-1,2,5,6-tetrahydrobenzyl-6-methyl-1,2,5,6-tetrahydrobenzoate represented by formula (III). Y¹-CO-O-CH₂-Y¹ (III) 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate, 1-methyl-1,2,5,6-tetrahydrobenzyl-1-methyl-1,2,5,6-tetrahydrobenzoate and 6-methyl-1,2,5,6-tetrahydrobenzyl-6-methyl-1,2,5,6-tetrahydrobenzoate, can be prepared by an esterification reaction according to so-called Tischenko reaction of tetrahydrobenzaldehyde, 1-methyl-1,2,5,6-tetrahydrobenzaldehyde and 6-methyl-1,2,5,6-tetrahydrobenzaldehyde, respectively, on a commercial basis, as a starting material for the preparation of compound (IV). Tetrahydrobenzaldehyde, 1-methyl-1,2,5,6-tetrahydrobenzaldehyde and 6-methyl-1,2,5,6-tetrahydrobenzaldehyde can be prepared on a commercial basis by Diels-Alder reaction of butadiene with acrolein, methacrolein, and crotonaldehyde, respectively. In formula (I), R a and R b each represent hydrogen or a methyl group, respectively, both being interchangeable with each other, depending on the starting lactone compounds. For example, in the case of epsilon-caprolactone being used as the starting material, R a and R b represent hydrogen. Further, in the case of beta-methyl-delta-valerolactone being used as the starting material, R a and R b represent a methyl group or hydrogen, respectively. In addition, in the case of 3-methyl-caprolactone being used as a starting material, R a and R b represent a methyl group and hydrogen, respectively. m, which represents a natural number of 1 to 7, is also selected as a function of the starting lactone compounds. For example, if epsilon-caprolactone, beta-methyl-delta-valerolactone or cyclooctanone lactone are used as the starting material, m is 5, 4 or 7, respectively. n corresponds to a mol number of the lactone compound introduced into the alicyclic compound (I), which is a natural number higher than 0. If a lactone compound is not introduced, the mol number n is 0, for example, if 5 mols of the lactone compound are introduced, the mol number n is inevitably 5. It is noted that epsilon-caprolactone can be prepared on a commercial basis by a Baeyer-Villiger reaction, in which cyclohexanone is oxidized by a peracid, etc. Furthermore, it is noted that trimethylcaprolactone can be prepared on a commercial basis by a Baeyer-Villiger reaction, in which trimethylcyclohexanone is oxidized by a peracid, etc. Still further, it is noted that trimethylcyclohexanone can be prepared on a commercial basis by a hydrogenation reaction of isophorone, followed by a Baeyer-Villiger reaction to obtain trimethylcaprolactone with a peracid. Beta-methylgamma-valerolactone can be manufactured from 2-hydroxy-4-methyltetrahydropyran as the starting material. Examples of peracids include an organic carboxylic peracid such as performic acid, peracetic acid, perpropionic acid, perbenzoic acid, m-chloroperbenzoic acid, etc., especially the peracetic acid produced by acetic acid and hydroperoxide or produced by acetic anhydride and sulfuric acid. According to a second aspect of the present invention, there is provided a process for the preparation of a composition consisting essentially of an alicyclic compound represented by formula (I), which process comprises an addition reaction of the compound represented by formula (III) Y¹-CO-O-CH₂-Y¹ ( III) wherein Y¹ represents at least one of the structural group with a lactone compound in the presence of a catalyst. Reaction conditions for introducing lactone units into the compound (III) are described in more detail below. 1 mol of the compound (III) is allowed to react with a fixed amount of a lactone compound, such as between 1 and 20 mols, and preferably between 1 and 10. Where the molar ratio is more than 20, the resulting compound (I) can not provide a resulting epoxy resin with sufficiently good properties, for example, the epoxy resin is too soft. For carrying out the reaction for introducing lactone units into the compound (III), a catalyst can be used. Effective catalysts include an organic tin compound such as stannous or stannic octylate, dibutyl tin oxide, and dibutyl tin laurate, etc., a halogenated tin compound such as stannous chloride, stannous bromide and or stannous iodide, etc. For the purpose of activating the catalyst to be used, an organic acid such as formic acid, acetic acid, propionic acid, etc., can be used together with the catalyst. Furthermore, a heteropoly-acid such as phosphorous tungstic acid, a tungstic silicate, etc., can also effectively be used as the catalyst. Still further, a metal compound such as magnesium chloride, magnesium methoxide, magnesium ethoxide, aluminum isopropoxide, aluminum xanthoxide, tetrabutyl titanate, tetrapropyl titanate, tetraethoxy titanate, etc., can be used as the catalyst. The amount of the catalyst to be used is preferably from 1,000 ppm to 0.1 ppm, more preferably from 200 to 0.1 ppm based on the total amount of the starting materials. Where the amount is more than 1,000 ppm, the reaction velocity is high. However, the final product may be undesirably colored in the case when the catalyst is not removed. On the other hand, where the amount is less than 0.1 ppm, an uneconomically long period of time is required in order to complete the reaction, due to the catalytic effect being too low. The reaction for introducing lactone units into the compound (III) can be preferably carried out at a temperature ranging from 100° to 250°C. Where the temperature is lower than 100° C, the reaction velocity is low. On the other hand, where the temperature is higher than 250° C, coloring of the resulting product is significant, and the result is a tendency to an undesirable decomposition reaction easily occurring. The reaction can be carried out either in the absence or the presence of a solvent such as toluene, xylene and/or an inert solvent having no active hydrogen, such as a hydrocarbon or the like, having high boiling points. If the reaction is carried out in the absence of a solvent, the resulting products can be diluted by various solvents in order to lower their viscosity, rendering thereby the handling easier. The reaction can be surprisingly carried out in the presence of a minor amount of a compound having a hydroxyl group, which enables a considerable increase of reaction velocity. The compound having hydroxyl group includes water, methanol, ethanol, propanol, butanol, ethyleneglycol, diethyleneglycol, triethyleneglycol, propyleneglycol, butanediol, pentanediol, neopentylglycol, 1,6-hexanediol, 3-methylpentanediol, trimethylolpropane, glycerine, trimethylolethane, pentaerythritol, etc. The compound is preferably used in such an amount as to provide a hydroxyl value of the resulting compound (I) within a range of 0.01 to 50, and more preferably 0.1 to 10. Where the hydroxyl value is adjusted to less than 0.01, effects resulting from the use of the compound are low. On the other hand, where the hydroxyl value is adjusted to more than 50, the properties tend to deteriorate in spite of the higher effect. Methods for charging the starting materials are not restricted; for example, any charging order may be used for the starting compound (III), a lactone compound, a catalyst, and a reaction promoter which is a compound having hydroxyl groups described hereinabove. The catalyst can be charged in the form of a solution dissolved in other starting material such as the lactone compound, especially when used in a minor amount, such as a few ppm, which is difficult to charge, in the reaction solution. The reaction is preferably carried out under the presence of nitrogen gas. Although the presence of oxygen in the reaction vessel does not affect reaction velocity, the oxygen tends to give the resulting product an unpreferable color and may also produce, in the atmosphere of the reaction vessel, an undesirable gas composition which can lead to the explosion-inducing range. The resulting crude solution obtained at the end of the reaction is supposed to contain mainly a compound of formula (I), and to contain small or minor amounts of various compounds which are by-products and unreacted starting materials. For example, if one mol of the compound (III) is allowed to react with n1+n2+n3+n4+n5+n6 mols of a lactone compound in the presence of a catalyst and a reaction promoter, which is a diol compound represented by general formula HO-R X -OH, the resulting product is a mixture composed of the following compounds; Y¹-CO-O-CH₂-Y¹ ( III) In formula (I), (III), (VI), (VII), (VIII), and (IX), is a lactone derived ester-bonding unit depending on a lactone compound to be used, Y¹ represents at least one selected from R a and R b each represents hydrogen or a methyl group (i.e., the groups are interchangeable), depending on the starting lactone compounds. m, which represents a natural number of 1 to 7, is also selected as a function of the starting lactone compounds to be used. n1+n2+n3+n4+n5+n6 corresponds to the total mol numbers of the lactone compound introduced into the starting alicyclic compound (III), which is inevitably nearly equal to the mol numbers of the charged lactone compound, which is preferably a natural number between 1 and 20. In the case of n1 being 0 in formula (I), the compound corresponds to the compound (III), which is the unreacted starting material. The resulting product is a mixture composed of the lactone adducts having different numbers of lactone derived ester-bonding unit. That means that n1, n2,n3, n5 and n6 have a distribution in a range of n1-n6=0, 1, 2, 3, ........L, respectively. The main component or primary component in the mixture is compound (I). The resulting product can be used, for example, as a component in coating compositions without carrying out any purification or separation. Furthermore, the resulting product can also be used after optionally carrying out a purification or separation. For example, the product can be washed with water in order to remove low molecular weight components having a hydroxyl group at a terminal position, and can also be separated by a chromatography. Furthermore, the resulting product can also be used after diluting with a solvent. In the case of epsilon-caprolactone being used as a lactone compound, all of the units in (I), (VI), (VII), (VIII) and (IX) are -O-(-CH₂-)₆-CO-. In the case of beta-methylgamma-valero-caprolactone being used as a lactone compound, all of the units in (I), (VI), (VII), (VIII) and (IX) are In the case of 3,5,5-trimethylcaprolactone being used as a lactone compound, all of the units in (I), (VI), (VII), (VIII) and (IX) are In the case of 3,3,5-trimethylcaprolactone being used as a lactone compound, all of the units in (I), (VI), (VII), (VIII) and (IX) are The lactone compound can also be used as a mixture composed of at least two kinds of lactones. In the case of the mixed lactones being used these lactones are randomly introduced into the compounds (I), (VI), (VII), (VIII,) and (IX). According to a third aspect of the present invention, there is provided a composition consisting essentially of an epoxidized alicyclic compound represented by formula (II) In formula (II), is a lactone derived ester-bonding unit ; Y² represents at least one of the structural groups derived from an epoxidation reaction of the double bond in Y¹ described hereinabove; R a and R b each represents hydrogen or methyl group, depending on the starting lactone compounds, as in the case of compound (I). According to a fourth aspect of the present invention, there is provided a process for the preparation of a composition comprising a compound represented by formula (II). A composition consisting essentially of an epoxidized alicyclic compound represented by formula (II) can be prepared by an epoxidation reaction of a composition consisting essentially of an alicyclic compound represented by formula (I). The epoxidation reaction can be carried out using an epoxidation agent such as a peracid or various hydroperoxides. The peracids include performic acid, peracetic acid, perpropionic acid, perbenzoic acid, trifluoroperacetic acid, etc. Of these peracids, peracetic acid is the preferred epoxidizing agent, because it is available on an industrial basis at a moderate price and has a high stability. The hydroperoxides include hydroperoxide, tertiarybutylhydroperoxide, cumenperoxide, metachloroperbenzoic acid, etc. When carrying out the epoxidation reaction, a catalyst can be used when appropriate according to the circumstances. For example, if peracetic acid is used as an epoxidation agent, an alkali such as sodium carbonate, or an acid such as sulfuric acid, can be used as a catalyst. Furthermore, if hydroperoxides are used, it is possible to obtain a catalytic effect, for example, by using a mixture of tungstic acid and sodium hydroxide together with hydrogen peroxide, or hexacarbonylmolybdenum together with tertiary butyl hydroperoxide. The epoxidation reaction is carried out in the absence or the presence of a solvent, while controlling the reaction temperature according to the apparatus to be used and the properties of the raw materials. The temperature region of the epoxidation reaction can be selected according to the reactivity of the epoxidizing agent. In the case of peracetic acid, which is the preferable epoxidizing agent, the preferred temperature is between 0 and 70° C. If the temperature is under 0° C, the reaction velocity is slow, but if the temperature is over 70° C, a decomposition reaction of peracetic acid can occur. In the case of tertiary butylhydroperoxide/molybdenumdioxide diacetyl acetate, which is one example of a hydroperoxide, the preferable temperature is between 20° C and 150° C, based on the same consideration. The use of solvents for dilution is effective for lowering the velocity of reaction of the raw materials and stabilizing the epoxidizing agent. In the case of peracetic acid being used as the epoxidizing agent, preferred solvents include aromatic compounds, an ether compound and ester compounds. The molar ratio of the epoxidizing agent to be used with respect to the unsaturated bonds is selected according to the proportion of the unsaturated bonds which it is desired to retain. When preparing epoxy compositions having many epoxy groups, an equal or higher molar ratio of the epoxidizing agents to the unsaturated bonds is preferably used, but to use amounts of the epoxidizing agents at a molar ratio of more than 10/1 with respect to the unsaturated bonds is not recommended, because of the cost and of the side reactions described hereinafter. In the case of peracetic acid, a preferred molar ratio is 1/1 to 5/1. Substituted groups are produced by the side reaction between epoxy groups and acetic acid is by-produced and contained in the desired product, depending upon the epoxidizing conditions, with a generation of the epoxy groups from double bonds. The product obtained also contains other minor by-products, by which a subsequent or a final product is affected adversely in color hue and acid value. In order to prevent such adverse affects, additives as described hereinafter are preferably used also: phosphoric acid, potassium phosphate, sodium phosphate, ammonium hydrogenphosphate, pyrophosphoric acid, potassium pyrophosphate, sodium pyrophosphate, potassium 2-ethylhexyl pyrophosphate, sodium 2-ethylhexyl tripolyphosphate, potassium 2-ethylhexyl tripolyphosphate, tripolyphosphoric acid, potassium tripolyphosphate and or sodium tripolyphosphate, sodium 2-ethylhexyl tetrapolyphosphate, potassium 2-ethylhexyl tetrapolyphosphate and 2-ethylhexyl pyrophosphate. The amount of the additives used ranges generally from 10 ppm to 10,000 ppm, and preferably from 50 ppm to 1,000 ppm, based on the total weight of the starting materials. It appears that the additives may have a chelating effect on metals which are derived from the reaction vessel or materials. The metals are inactivated by the chelating effect. The epoxidized product obtained can be separated from a crude reaction solution by various procedures. Also, the reaction crude solution obtained can be used, with simple removal of solvents, etc., which are components with a low boiling point, even without any purification process. The removal of the components with a low boiling points is carried out at a temperature of 50° to 200° C., and preferably 80° to 160°C. Also, the degree of pressure reduction in the vessel can be adjusted depending on the boiling points of the solvents used in carrying out the epoxidation reaction. After completion of the epoxidation reaction, flushing the crude solution with water is preferably carried out for removing minor amounts of impure components. When carrying out water flushing of the crude solution, an aromatic compound such as benzene, toluene, xylene, etc., a hydrocarbon such as hexane, heptane, octane, etc., an ester such as ethyl acetate, butyl acetate, etc., can also be used together with water. The amount of water used on flushing is 0.1 to 10 times more, preferably 1 to 5 times more than the crude reaction solution volume Furthermore, an alkali aqueous solution can be used for removing minor amounts of acids, and then water can be used again in order to remove the alkali. Specific preferred alkalis include NaOH, KOH, K₂CO₃, Na₂CO₃, KHCO₃, NaHCO₃ and NH₃. The concentration of the alkali can optionally be selected from a wide range. The aqueous alkali leaching and subsequent water leaching can be carried out in a temperature range of 10° to 90° C., and preferably of 10° to 50° C. After completion of water leaching and settling, the resultant organic layer is separated from water layer, and distilled. This distillation eliminates materials having low boiling points, which are mainly solvents used at the start of the reaction, to obtain a product. Temperatures for distilling out the materials having low boiling points are from 50° to 200° C., and preferably from 80° to 160° C. When distilling out the materials, the degree of reduced pressure can be adjusted depending on the boiling points of the solvents to be used. The reaction can be carried out by either a continuous type process or a batch type process. In the case of the batch type process, starting materials and additives such as solvents, etc., are preferably charged first in a reaction vessel, and then an epoxidizing agent is added dropwise. When the reaction crude solution is washed with water after completion of the epoxidation reaction, the solution is separated into two liquid layers. The organic liquid layer is separated from the water layer, followed by evaporation of components with a low boiling point in an evaporator. In the case of the continuous type process, starting materials, additives such as solvents and an epoxidizing agent are supplied continuously into the reaction vessel, and the product is continuously taken out of the vessel. The reaction vessel used comprises a piston flow type or a completely mixable type vessel. The product obtained is a composition mainly containing the compound represented by the formula (II). The constitution of the composition depends on the constitution of the compound represented by formula (I), which is the starting material in the epoxidation reaction. It appears that the composition obtained in the epoxidation reaction primarily contains the compound of formula (II), with the following various compounds in addition to the above described (I), (III), (VI). (VII), (VIII) and (IX) Y²-CO-O-CH₂-Y² (III)′ Y¹-CO-O-CH₂-Y² (III)″ In the formulae (II)′, (VI)′, (VII)′, (III)′, and (III)″, Y² represents at least one of the epoxidized structural groups , derived from the double bond in Y¹, , R a , R b and m necessarily depend on the lactone compound used, as well as in the compounds (I), (VI), (VII), (VIII) and (IX). In the case of mixed lactones being used in an addition reaction these lactone compounds are randomly introduced. Accordingly, the epoxidized composition is also inevitably composed of various compounds having randomly introduced lactone derived ester-bonding units. Also, n represents the same distributions as those in the compounds (I), (VI), (VII), (VIII) and (IX). Furthermore, it is noted that an epoxy group is generally ring-opened by water or an acid, although its presence may be in a minor amount. Accordingly, Y o is derived from Y² in compounds (II), ( II)′, (VI)′, (VII)′, and (III)′ wherein Y o represents at least one of the structural groups R Y represents hydrogen, acetyl group and or propyl group, etc., depending on the epoxidizing agent used. The composition obtained by the epoxidation reaction, in which the compound of formula (II) is a main and desired component, can be used without any further treatments. Furthermore, the composition can optionally be used after purifying, for example, with a chromatography, etc. According to a fifth aspect of the present invention, there is provided a curable composition consisting essentially of the above described composition which comprises a compound represented by formula (II), and a curing agent for epoxy resins. Specific curing agents include an aromatic acid anhydride such as phthalic anhydride, trimellitic anhydride, pyromellitic anhydride, benzophenonetetracarboxylic anhydride, ethyleneglycol bis(anhydrotrimellitate), glyceroltris(anhydrotrimellitate), an alicyclic acid anhydride such as maleic anhydride, succinic anhydride, tetrahydrophthalic anhydride, methyltetrahydrophthalic anhydride, hexahydrophthalic anhydride, methylhexahydrophthalic anhydride, etc., and amines such as ethylenediamine, diethylenetriamine, triethylenetetramine, isophoronediamine, xylenediamine, methaphenylenediamine, diaminodimethyl sulfone, diaminodiphenyl methane, polymethylenediamine, etc., and or imidazoles such as 2-methylimidazole, 2-ethyl-4-methylimidazole, 2-undecylimidazole, 2-heptadecylimidazole, 2-phenylimidazole, etc. Furthermore, dicyandiamide and derivatives thereof, polyamide resins, an organic acid hydrazide, melamine and derivatives thereof, a trifluoroboric compound such as a trifluoroborate-amine complex, a compound having silanolic hydroxyl groups, etc., can be used as a curing agent for epoxy compounds. Additionally, tertiary amines, esters of boric acid, Lewis acids, organometallic compounds, a salt of an organic acid, etc., can optionally be used together with the above described curing agents as an accelerator for curing. Still further, a conventional modifier for epoxy resins and fillers can be used together with the curing agents. The amount ratio of the curing agent to be used to the present epoxy composition is 1/0.1 to 1/5, preferably 1/0.5 to 1/1.5, based on the chemical equivalence, provided that a trifluoroborate-amine complex or a compound having silanolic hydroxyl groups is used in the chemical equivalence of 1/0.0001 to 1/1.0, and preferably 1/0.001 to 1/1.0. Furthermore, the alicyclic epoxy composition which comprises a compound represented by formula (II) can be used together with other epoxy resins in order to provide ductility to the other epoxy resins. According to a sixth aspect of the present invention, there is provided a photo-polymerizable composition consisting essentially of the above described composition which comprises a compound represented by formula (II) and a photo-cationic polymerization initiator. Specific photo-cationic polymerization initiator includes a diazonium salt such as a sulfonium salt such as R₃-SMX R ⁻ (XII), an iodonium salt such as R-I⁺-R MX R ⁻ (XV), a metal complex such as a sulfonium acetone such as a sulfone compound such as [in formulae (X) to (XX), Ph is Cp is R is selected from hydrogen, an alkyl group, phenyl group, an aryl group and a hydroxyalkyl group, which may be identical or different from one another, MX R is at least one group selected from the group consisting of SbF₆, AsF₆, PF₆ and BF₄], a silicone compound having a property of generating a silanol group, or a complex of an aluminum compound by photo-irradiation. The specific silicone compound is preferably a silicone compound having one group selected from the group consisting of a peroxysilane group, an o-nitrobenzyloxy group, and an alpha-ketosilyl group. Specific silicone compounds having a peroxysilane group are represented by the formula (R x1 ) a -Si (O-O-R x2 ) 4-n [in the formula, R x1 and R x2 hydrogen, a halogen atom, an alkyl group selected from the group consisting of, for example, methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, t-butyl group, sec-butyl group, n-pentyl group, methoxy group, ethoxy group and chloromethyl group or an aryl group selected from the group of, for example, phenyl group, naphthyl group, anthranyl group, benzyl group, which may be identical or different from each other, and which can have a substituent selected from the group of a halogen atom, a nitro group, a cyano group, a methoxy group, etc., and n is an integer between 0 and 3]. Silicone compounds have specific formulae described hereinafter In the above formulae, Ph represents Specific silicone compounds having an o-nitrobenzyloxy group are described hereinafter. In the above formula, R¹, R² and R³ are hydrogen, a halogen atom, vinyl group, an aryl group, a substituted or an unsubstituted alkyl group having a carbon number of 1 to 10, an alkoxy group having a carbon number of 1 to 10, a substituted or an unsubstituted aryl group, a substituted or an unsubstituted aryloxy group and or a siloxy group, respectively, which may be identical or different from one another; R⁴ is hydrogen, a substituted or an unsubstituted alkyl group having a carbon number of 1 to 10, or a substituted or an unsubstituted phenyl group; R⁵, R⁶, R⁷ and R⁸ are hydrogen, nitro group, cyano group, hydroxy group, mercapto group, a halogen atom, an acetyl group, an aryl group, an alkyl group having a carbon number of 1 to 5, an alkoxy group having a carbon number of 1 to 5, a substituted or an unsubstituted aryl group, a substituted or an unsubstituted aryl group and or an aryloxy group, respectively, which may be identical or different from one another; and p, q and r are each an integer of 0 to 3, respectively, and have a relationship of 1≦p+q+r≦3]. Substituted or unsubstituted alkyl groups having a carbon number of 1 to 10 include methyl group, ethyl group, propyl group, n-butyl group, t-butyl group, pentyl group, chloromethyl group, chloroethyl group, fluoromethyl group and cyanomethyl group, etc., and specific alkoxy group having a carbon number of 1 to 10 include a methoxy group, ethoxy group, n-propoxy group and or n-butoxy group, etc. Substituted or unsubstituted aryl groups include a phenyl group, p-methoxyphenyl group, p-chlorophenyl group, p-trifluoromethylphenylvinylmethylphenyl(o-nitrobenzyloxy)silane, t-butylmethylphenyl(o-nitrobenzyloxy)silane, triethyl(o-nitrobenzyloxy)silane, tri(2-chloroethy-1)-o-nitrobenzyloxysilane, tri(p-trifluoromethylphenyl)-o-nitrobenzyloxysilane, trimethyl[alpha-(o-nitrophenyl)-o-nitrobenzyloxy]silane, dimethylphenyl[alpha-(o-nitrophenyl)-o-nitrobenzyloxy]silane, methylphenyldi[alpha-(o-nitrophenyl)-o-nitrobenzyloxy]silane, triphenyl(alpha-ethyl-o-nitrobenzyloxy)silane, trimethyl(3-methyl-2-nitrobenzyloxy)silane, dimethylphenyl(3,4,5-trimethoxy-2-nitrobenzyloxy)silane, triphenyl(4,5,6-trimethoxy-2-nitrobenzyloxy)silane, diphenylmethyl(5-methyl-4-methoxy-2-nitrobenzyloxy)silane, triphenyl(4,5-dimethyl-2-nitrobenzyloxy)silane, vinylmethylphenyl(4,5-dichloro-2-nitrobenzyloxy)silane, triphenyl(2,6-dinitrobenzyloxy)silane, diphenylmethyl(2,4-nitrobenzyloxy)silane, triphenyl(3-methoxy-2-nitrobenzyloxy)silane, vinylmethylphenyl(3,4-dimethoxy-2-nitrobenzyloxy)silane, dimethyldi(o-nitrobenzyloxy)silane, methylphenyldi(o-nitrobenzyloxy)silane, vinylphenyldi(o-nitrobenzyloxy)silane, t-butylphenyldi(o-nitrobenzyloxy)silane, diethyldi(o-nitrobenzyloxy)silane, 2-chloroethylphenyldi(o-nitrobenzyloxy)silane, diphenyldi(o-nitrobenzyloxy)silane, diphenyldi(3-methoxy-2-nitrobenzyloxy)silane, diphenyldi(3,4-dimethoxy-2-nitrobenzyloxy)silane, diphenyldi(2,6-dinitrobenzyloxy)silane, diphenyldi(2,4-dinitrobenzyloxy)silane, methyltri(o-nitrobenzyloxy)silane, phenyltri(o-nitrobenzyloxy)silane, p-bis(o-nitrobenzyloxydimethylsilyl)benzene, 1,1,3,3-tetraphenyl-1,3-di(o-nitrobenzyloxy)siloxane, and 1,1,3,3,5,5-hexaphenyl-1,5-di(o-nitrobenzyloxy)siloxane. Furthermore, a silicone compound can be used, such as a silicone compound produced by a reaction between a SiCl₂-containing silicone resin and o-nitrobenzyl alcohol, a silicone compound having an alpha-ketosilyl group which is represented by the following formula; (wherein L, m and n are each an integer between 0 and 3, respectively; L+m+n is 3 or less than 3; R⁹, R¹⁰ and R¹¹ represent a hydrocarbon group such as an alkyl group having a carbon number of 1 to 10, an aryl group, an allyl group, vinyl group, an allyloxy group and an alkoxy group having a carbon number of 1 to 10, respectively, which can have a substituent such as a halogen atom, nitro group, cyano group and or methoxy group, which substituents may be identical or different from one another). Specific compounds having an alpha-ketosilyl group include The mixing amount of the above described silicone compound is generally between 0.2 and 20 % by weight, and preferably between 1 and 10 % by weight, based on the weight of epoxy resin. Where the amount is smaller than 0.1 % by weight, curing of the epoxy resin is not sufficient. On the other hand, where the amount is larger than 20 % by weight, although possible, it is not recommended because of costs and a problem caused by compounds derived from decomposition of the catalyst. Furthermore, an aluminum compound can also be used as a photocationic polymerization initiator for the present epoxy compositions. Specific aluminum compound includes trismethoxy aluminum, trisethoxy aluminum, trisisopropoxy aluminum, trisphenoxy aluminum, trisparamethylphenoxy aluminum, isopropoxy diethoxyaluminum, trisbutoxy aluminum, trisacetoxy aluminum, trisstearato aluminum, trisbutylate aluminum, trispropionato aluminum, trisisopropionato aluminum, trisacetylacetonato aluminum, tristrifluoroacetylacetonatoaluminum, trishexafluoroacetylacetonato aluminum, trisethylacetonato aluminum, trissalicylaldehydato aluminum, trisdiethylmalolato aluminum, trispropylacetoacetato aluminum, trisbutylacetoacetato aluminum, trisdipivaloylmethanato aluminum, diacetylacetonatodipivaloylmethanato aluminum. The above described compounds are represented by formulae At least one of the above described aluminum compounds can be used, in a general amount of 0.001 to 10 % by weight, and preferably from 1 to 5 % by weight, based on the weight of epoxy composition. Where the amount is less than 0.001 % by weight, sufficient properties in, for example, tensile strength or tensile elongation, etc., can not be attained in the cured products. On the other hand, where the amount is larger than 10 % by weight, costs become disadvantageously high and the resistance to moisture tends to be lowered. Various anti-staining agents can be mixed in the present photo-polym erizable composition for the purpose of increasing a resistance to staining. Specific anti-staining agents include borates, phosphates, chromates, molybdenum salts, etc. The anti-staining agents can be generally used in an amount of 10 to 50 % by weight, based on the weight of epoxy composition. Furthermore, various additives such as coloring dyes or pigments, a silica, an alumina can also be used together therewith. From the viewpoint of practical use, the present photo-polymerizable composition can be coated on a base material, and cured by photo-curing at ordinary temperatures (e.g., 25°C), or by photo-curing during heating, and postcuring after the photo-curing. Although the wavelength of rays to be irradiated for photo-curing depends upon a mixing constituent of the present photo-polymerizable composition and the kind of the above described photo-initiator, it is usually between 180 and 700 nm, and preferably in the ultraviolet wavelength range. The irradiation period also depends upon the mixing constituents of the photo-polymerizable composition, the kind of the above described photo-initiator, and the kind of the irradiation source. Generally, it is between 10 seconds and 30 minutes, and preferably, it is between 20 and 60 seconds. Furthermore, the temperature for photo-curing during heating also depends on the mixing constituent of the photo-polymerizable composition, and the kind of the above described photo-initiator; it is usually between 20 and 200° C, and preferably, is between 60 and 100° C. Still further, the temperature for postcuring after the photo-curing also depends on the mixing constituents of the present photo-polymerizable composition, and the kind of the above described photo-initiator; , it is usually between 50 and 200° C, and preferably, is between 100 and 180° C. There can be used a low-voltage mercury lamp, a high-voltage mercury lamp, a carbon arc lamp, a xenon lamp, an argon glow discharge lamp, a metal halide lamp, etc., as a discharging source of irradiation rays. The following Examples are given to illustrate the practice of this invention but they are not intended in any way to act to limit the scope of this invention. Example 1 A reaction vessel having a capacity of 3 liters equipped with a mechanically-driven stirrer, a reflux condenser, and a thermometer was charged with 1211.7 g. of 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate (above described compound (III)), 626.9 g. of epsilon-caprolactone, 8.51 g. of diethylene glycol, and 9.20 g. of 1 % heptane solution of tetrabutyltitanate as a catalyst. The contents in the vessel were gradually raised to a temperature of 220° C, followed by heating for 27 hours, in the presence of a nitrogen gas stream, to obtain an epsilon-caprolactone adduct. It was confirmed by gas chromatography analysis that 30.17 % of 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate and 0.16 % of unreacted epsilon-caprolactone remained in the epsilon-caprolactone adduct. The lactone adduct having double bonds exhibited the properties such as an outer appearance(APHA), an acid value(mg KOH/g), a hydroxyl value(mg KOH/g), a viscosity value(cp/45° C) and water content(%) as shown in Table 1. Subsequently, the adduct was analyzed with a ¹H-NMR, an I.R. spectrom eter, and GPC (gel permeation chromatography). These spectra are illustrated in Figure 1, Figure 2, and Figure 3, respectively. The ¹H-NMR spectrum chart was obtained with CDCl₃ as a solvent, at room temperature, by using a JNM-EX 90 apparatus (manufactured by Nihon Denshi, Ltd.). In the NMR spectrum chart, a singlet delta 5.67(H a ) is derived from a hydrogen bonded to a carbon atom having double bonds, and a multiplet delta 3.9 to 4.2(H b ,H b′ ) belongs to a hydrogen of methylene group which is adjacent to an oxygen atom. The I.R. spectrum chart was obtained by using an IR-435 spectrometer (manufactured by Shimadzu Seisakusyo, Ltd.), and an NaCl plate on which a sample was coated. An absorption peak was observed at 1728 cm⁻¹, which is derived from carbonyl group, and absorption peaks were observed at 3020 cm⁻¹, 1659 cm⁻¹ and 647 cm⁻¹, which are derived from specific double bonds of cyclohexenyl group. It was confirmed by the presence of a molecular weight distribution in the GPC chart that the esterification reaction as described hereinabove occurred. The above analyses confirmed; that the product is represented by formula described hereinafter. (wherein n=0, 1, 2, 3, 4.........). The mixing constituents of reaction materials and the results obtained in further Examples 2-9 are shown in Table 1. Example 10 A reaction vessel having a capacity of 2 liters equipped with a mechanically-driven stirrer, a reflux condenser, a thermometer, and a muffle was charged with 167.2 g. of the composition containing the compound (I) obtained in Example 1, 150.0 g. of ethyl acetate. The contents in the vessel were maintained at a temperature of 50° C. Successively, peracetic acid solution(concentration of 30 % in ethyl acetate) and 1.48 g. of 2-ethylhexyl sodium tripolyphosphate were added by dropwise to the contents over 2 hours. The contents were further maintained at a temperature of 50° C. for 2 hours, to obtain a crude reaction solution having acetic acid concentration of less than 0.1 %. 320 g. of ion-exchanged water was added into the crude reaction solution obtained, followed by stirring at a temperature of 50° C for 30 minutes. The solution was aged for approximately 40 minutes to separate into two liquid layers. The lower layer liquid was gradually removed from the upper layer liquid over 20 minutes. 150 ml of ethyl acetate was added in the separated upper layer liquid. The same addition processes of ion-exchanged water and separation were repeated twice. Low boiling components in the upper layer liquid obtained were removed with a Smith-type thin layer evaporator made of glass. The evaporation was operated at a heating temperature of 150° C. and a reduced pressure of 1330 Pa (10 Torr). Yield of the epoxidized compound represented by formula (II) was 95 % based on the amount of the upper layer liquid after removing the low boiling components. The properties of the compound are shown in Table 2. The ¹H-NMR spectrum chart was obtained with CDCl₃ as a solvent, under room temperatures by using a JNM-EX 90 apparatus (manufactured by Nihon Denshi, Ltd.). In the ¹H-NMR spectrum chart, it was confirmed that a peak at delta 5.6 derived from a double bond in the raw material shifted to a higher magnetic field, ie. to delta (ppm)3.2(H c ), thanks to the epoxidation of the double bonds. It was confirmed by the NMR data that a double bond was epoxidized. Furthermore, in the NMR spectrum chart, a multiplet delta 3.8 to 4.2(H d ,H d′ ) belongs to a hydrogen of methylene group which is adjacent to an oxygen atom (as shown in Figure 4). An absorption peak in IR spectrum was observed at 1734 cm⁻¹, which is derived from carbonyl group, and absorption peaks were observed at 785 cm⁻¹, 1250 cm⁻¹, which are especially derived from an epoxy group, as shown in Figure 5. The I.R. spectrum chart was obtained by using IR-435 spectrometer (manufactured by Shimadzu Seisakusyo, Ltd.), and NaCl plate on which a sample was coated. The above analyses confirmed that the obtained epoxy compound is represented by the rational formula described hereinafter. (wherein n=approximately 10). The mixing constituents of reaction materials and the results obtained in further Examples 11-15 are shown in Table 2. Example 16 A reaction vessel having a capacity of 3 liters equipped with a mechanically-driven stirrer, a reflux condenser, and a thermometer was charged with 1211.0 g. of 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate [compound (III)], 300.0 g. of epsilon-caprolactone, 326 g. of beta-methyldeltavalerolactone, 8.51 g. of diethyleneglycol, and 9.20 g. of 1 % heptane solution of tetrabutyltitanate as a catalyst. The contents in the vessel were gradually raised to a temperature of 220° C., followed by heating for 27 hours, in the presence of a nitrogen gas stream, to obtain a mixed-lactone adduct. It was confirmed by gas chromatography analysis that 30.0 % of 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate (compound (III)), 0.01 % of unreacted epsilon-caprolactone, and 3.0 % of beta-methyldelta-valerolactone were remained in the mixed lactone adduct. The mixed-lactone adduct having double bonds exhibited the following properties; an outer appearance(APHA) of 100, an acid value(mg KOH/g) of 0.1, a hydroxyl value(mg KOH/g) of 4.86, and a water content of 0.01 %. Example 17 A reaction vessel having a capacity of 3 liters equipped with a mechanically-driven stirrer, a reflux condenser, and a thermometer was charged with 1211.0 g. of 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate (compound (III)), 300.0 g. of epsilon-caprolactone, 326 g. of trimethylcaprolactone(a mixture composed of 3,5,5-trimethylcaprolactone and 3,3,5-trimethylcaprolactone), 8.51 g. of diethyleneglycol and 9.20 g. of 1 % heptane solution of tetrabutyltitanate as a catalyst. The contents in the vessel were gradually raised to a temperature of 220° C., followed by heating for 27 hours in the presence of a nitrogen gas stream to obtain a mixed-lactone adduct. It was confirmed by gas chromatography analysis that 31.0 % of 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate (compound (III)) 0.10 % of unreacted epsilon-caprolactone, 3.0 % of trimethylcaprolactone remained in the mixed-lactone adduct. The obtained mixed-lactone adduct exhibited the following properties; an outer appearance(APHA) of 1000, an acid value(mg KOH/g) of 0.1, a hydroxyl value(mg KOH/g) of 4.86 and a water content of 0.01 %. Example 18 and Example 19 The same procedures as described in Example 10 were repeated, except that the product obtained in Example 16 and the product obtained in Example 17 were used, respectively. The results obtained in Examples 18 and 19 are also shown in Table 2. Comparative Example 1 The same procedures as described in Example 10 were repeated, except that 2-ethylhexylsodiumtripolyphosphate was not used. The product obtained exhibited a high acid value of 2.8. Example 20 A reaction vessel equipped with a tube supplying nitrogen gas, a funnel for dropwise addition, a mechanically-driven stirrer, a reflux condenser, and a thermometer was charged with 440 parts by weight of 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate[a compound represented by formula (III)], 228 parts by weight of epsilon-caprolactone, 2.9 parts by weight of diethyleneglycol and 3.1 parts by weight of heptane solution containing 3 % of tetrabutyltitanate as a catalyst. The contents in the vessel were heated to approximately 220° C. under a nitrogen gas stream for approximately 1 hour, and allowed to react to obtain 668 parts by weight of a lactone adduct [a composition comprising a compound represented by formula(I)] for 27 hours. Unreacted 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate and epsilon-caprolactone remaining in the lactone adduct were 30.2 % by weight and 0.16 % by weight, respectively. The lactone adduct obtained exhibited an acid value of 0.33, a hydroxyl value of 5.0, and a viscosity of 45 cp/45° C. A reaction vessel equipped with a tube supplying nitrogen gas, a funnel for dropwise addition, a mechanically-driven stirrer, a muffle, a thermometer, and a reflux condenser was charged with 500 parts by weight of the lactone adduct, and 450 parts by weight of ethyl acetate, followed by heating to a temperature of 50° C. Successively, 800 parts by weight of ethyl acetate solution containing 30 % of peracetic acid, and 1.5 parts by weight of 2-ethylhexyl sodium tripolyphosphate, were added dropwise to the ethyl acetate solution of the above lactone adduct for 2 hours, and the contents in the reaction vessel were maintained for additional reaction at 50° C for 2 hours. The concentration of peracetic acid was less than 0.6 % after the additional reaction. Subsequently, the crude reaction solution obtained was washed with 960 parts by weight of ion exchanged water and the mixture was separated into two liquid layers. The lower liquid layer was removed from the upper liquid layer. 450 parts by weight of ion-exchanged water were added to the upper layer to wash it again. The same addition processes of ion-exchange water were repeated twice. Low boiling components were removed from the upper layer liquid obtained at a temperature of 150° C., and a reduced pressure of 1330 Pa (10 Torr) to obtain 520 parts by weight of a composition comprising a compound represented by formula (II)(epsilon-caprolactone modified 3,4-epoxycyclohexylmethyl-3′,4′-epoxycyclohexanecarboxylate). It is noted that a specific example of 3,4-epoxycyclohexylmethyl-3′,4′-epoxycyclohexanecarboxylate is Celloxide 2021, manufactured by Daicel Chemical Industries, Ltd., corresponding to the compound represented by formula (IV) having a residual group of cyclohexenemonoepoxide, that is, Y² as epoxide. The epoxidized lactone adduct exhibited an epoxy equivalence of 230, an acid value of 0.90, and a viscosity of 214 cp/45° C. The epoxidized lactone adduct was designated as Epoxy Resin A. Example 21 The same procedures as described in Example 20 were repeated, except that 342 parts by weight of epsilon-caprolactone were added to 252 parts by weight of 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate to obtain a lactone adduct, and the lactone adduct was epoxidised. The epoxidized lactone adduct was designated as Epoxy Resin B. Example 22 The same procedures as described in Example 20 were repeated, except that 570 parts by weight of epsilon-caprolactone were added to 252 parts by weight of 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate to obtain a lactone adduct, and the lactone adduct was epoxidised. The epoxidized lactone adduct was designated as Epoxy Resin C. Example 23 The same procedures as described in Example 20 were repeated, except that 468 parts by weight of trimethylcaprolactone were added to 280 parts by weight of 6-methyl-1,2,5,6-tetrahydrobenzyl-6-methyl-1,2,5,6-tetrahydrobenzoate to obtain a lactone adduct, and the lactone adduct was epoxidised. The epoxidized lactone adduct was designated as Epoxy Resin D. Application Example 1 100 parts by weight of the Epoxy Resin A, 82 parts by weight of methylhexahydrophthalic anhydride as a curing agent and 0.91 parts by weight of N,N′-dimethylbenzyl amine as a catalyst were mixed in a vessel at room temperatures, followed by being cured at the temperature of 100° C. for 5 hours to obtain a cured product. The cured product was further cured at the temperature of 160° C. for 10 hours to obtain a cured product for tests. Application Example 2 100 parts by weight of the Epoxy Resin B, 42 parts by weight of hexahydrophthalic anhydride as a curing agent and 0.74 parts by weight of N,N′-dimethylbenzyl amine as a catalyst were mixed and cured as described in Application Example 1 to obtain a cured product for tests. Application Example 3 100 parts by weight of the Epoxy Resin C, 34 parts by weight of methylhexahydrophthalic anhydride as a curing agent and 0.67 parts by weight of N,N′-dimethylbenzyl amine as a catalyst were mixed and cured as described in Application Example 1 to obtain a cured product for tests. Application Example 4 45 parts by weight of the Epoxy Resin C, 55 parts by weight of 3,4-epoxycyclohexylmethyl-3′,4′-epoxycyclohexanecarboxylate, 66 parts by weight of phthalic anhydride as a curing agent and 0.83 parts by weight of N,N′-dimethylbenzyl amine as a catalyst were mixed and cured as described in Application Example 1 to obtain a cured product for tests. Application Example 5 100 parts by weight of the Epoxy Resin D, 30 parts by weight of methylhexahydrophthalic anhydride as a curing agent and 0.65 parts by weight of N,N′-dimethylbenzyl amine as a catalyst were mixed and cured as described in Application Example 1 to obtain a cured product for tests. Comparative Application Example 1 The same procedures as described in Application Example 1 were repeated, except that 100 parts by weight of 3,4-epoxycyclohexylmethyl-3′,4′-epoxycyclohexanecarboxylate [Celloxide 2021 manufactured by Daicel Chemical Industries, Ltd.], 114 parts by weight of methylhexahydrophthalic anhydride and 1.07 parts by weight of N,N-dimethylbenzylamine as a curing agent were mixed. Comparative Application Example 2 The same procedures as described in Application Example 1 were repeated, except that 31 parts by weight of 3,4-epoxycyclohexylmethyl-3′,4′-epoxycyclohexanecarboxylate [Celloxide 2021 manufactured by Daicel Chemical Industries, Ltd.], 69 parts by weight of a polycaprolactone polyol (PCL-305 manufactured by Daicel Chemical Industries, Ltd.), 38 parts by weight of methylhexahydrophthalic anhydride and 0.69 parts by weight of N,N-dimethylbenzylamine as a curing agent were mixed. Comparative Application Example 3 The same procedures as described in Application Example 1 were repeated, except that 100 parts by weight of bis(3,4-epoxycyclohexyl-methyl)adipate [ERL-4299 manufactured by Union Carbide, Corp.], 81 parts by weight of methylhexahydrophthalic anhydride and 0.91 parts by weight of N,N-dimethylbenzylamine as a curing agent were mixed. The mixing constituents and various properties obtained in Application Examples 1 to 5 and Comparative Application Examples 1 to 3 are shown in Table 3 and Table 4, respectively. Example 24 The same procedures as described in Example 20 were repeated, except that 3 mols of epsilon-caprolactone were added to 1 mol of 1,2,5,6- tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate to obtain an epoxidized lactone adduct. The epoxidized lactone adduct was designated as Epoxy Resin EP-1. Example 25 The same procedures as described in Example 20 were repeated, except that 2 mols of trimethylcaprolactone were added to 1 mol of 1,2,5,6-tetrahydrobenzyl-1,2,5,6-tetrahydrobenzoate to obtain an epoxidized lactone adduct. The epoxidized lactone adduct was designated as Epoxy Resin EP-2. Application Example 6 100 parts by weight of the Epoxy Resin EP-1, 0.5 parts by weight of trisacetyl(acetonato)-aluminum and 3 parts by weight of triphenyl(o-nitrobenzyloxy)silane as a photo-cationic polymerization initiator were mixed and cured to obtain a photocured plate having a thickness of 2 mm under the illuminance of irradiation with a metalhalide lamp having 80 W/cm₂, with an exposing distance of 6.5 cm, for the period of 100 seconds. Application Example 7 The same procedures as described in Application Example 6 were repeated, except that 100 parts by weight of the Epoxy Resin EP-2 and 1 part by weight of trisethyl(acetoacetato)-aluminum were used to obtain a photocured plate. Comparative Application Example 4 The same procedures as described in Application Example 6 were repeated, except that 100 parts by weight of 3,4-epoxycyclohexylmethyl-3′,4′-epoxycyclohexanecarboxylate (Celloxide 2021, manufactured by Daicel Chemical Industries, Ltd.) were used to obtain a photocured plate. Comparative Application Example 5 The same procedures as described in Application Example 6 were repeated, except that 100 parts by weight of Epikote 828 (an epi-bis type epoxy resin manufactured by Ciba-Geigy, Corp.) were used to obtain a photocured plate. The measurements of the properties of the cured plates were carried out under the conditions of temperature of 20° C and relative humidity of 65%. Measurements of the tensile strength and elongation were carried out based on JIS K 6911. The measurements of Tg were carried out with a high performance differential calorimeter (No. DSC 8230B manufactured by Rigaku Denki, Ltd.). The mixing constituents and various properties obtained in Application Examples 6, 7 and Comparative Application Examples 4, 5 are shown in Table 5.

Claims: A composition consisting essentially of an epoxidized alicyclic compound represented by formula (II) wherein Y² represents at least one of the structural groups R a and R b each represents hydrogen or a methyl group, m represents a natural number ranging from 1 to 7, and n represents a natural number ranging from 1 to 20. A curable composition consisting essentially of a composition which comprises a compound represented by formula (II) wherein Y² represents at least one of the structural groups R a and R b each represents hydrogen or a methyl group, m represents a natural number ranging from 1 to 7, and n represents a natural number ranging from 1 to 20, and a curing agent for epoxy resins. A photo-polymerizable composition consisting essentially of a composition which comprises a compound represented by formula (II) wherein Y² represents at least one of the structural groups R a and R b each represents hydrogen or a methyl group, m represents a natural number ranging from 1 to 7, and n represents a natural number ranging from 1 to 20; and a photo-cationic polymerization initiator for epoxy resins. A composition which comprises an alicyclic compound represented by formula (I) wherein Y¹ represents at least one of the structural groups R a and R b each represents hydrogen or a methyl group, m represents a naturel number ranging from 1 to 7, and n represents a natural number ranging from 1 to 20. A process for the preparation of a composition consisting essentially of a compound represented by formula (I) wherein Y¹ represents at least one of the structural groups R a and R b each represents hydrogen or a methyl group, m represents a natural number ranging from 1 to 7, and n represents a natural number ranging from 1 to 20; said process comprising reaction of a compound represented by formula (III) Y¹-CO-O-CH₂-Y¹ (III) wherein Y¹ is the same as defined above, with a lactone compound in the presence of a catalyst. A process as set forth in claim 5, wherein a compound having a hydroxyl group is added so as to provide a hydroxyl value of 0.01 to 50 in the composition obtained. A process as set forth in claim 5, wherein said lactone compound is at least one compound selected from the group consisting of epsilon-caprolactone, trimethyl-caprolactone, and beta-methyldelta valerolactone. A process as set forth in claim 5, wherein a compound having at least one hydroxyl group is used together therewith. A process for the preparation of a composition which comprises a compound represented by formula (II) wherein Y² represents at least one of the structural groups R a and R b each represents hydrogen or a methyl group, m represents a natural number ranging from 1 to 7, and n represents a natural number ranging from 1 to 20; said process comprising an epoxidation reaction of a composition which comprises a compound represented by formula (I) wherein Y¹ represents at least one of the structural groups in the presence of an epoxidation agent, at a temperature between 0 and 70° C. A process as set forth in claim 9, wherein the epoxidation reaction is carried out in the presence of at least one additive selected from the group consisting of phosphoric acid, potassium phosphate, sodium phosphate, ammonium hydrogen phosphate, pyrophosphoric acid, potassium pyrophosphate, sodium pyrophosphate, 2-ethylhexyl pyrophosphate, potassium 2-ethylhexyl phosphate, sodium 2-ethylhexyl phosphate, tripolyphosphoric acid, potassium tripolyphosphate, sodium tripolyphosphate, potassium 2-ethylhexyl pyrophosphate, sodium 2-ethylhexyl tripolyphosphate, potassium 2-ethylhexyl tripolyphosphate, sodium 2-ethylhexyl tetrapolyphosphate, and potassium 2-ethylhexyl tetrapolyphosphate.

Inventors: FUJIWA TAKAAKI, HARANO YOSHIYUKI, TAKEMOTO SHIN, WATANABE SHOJI, FUJIWA, TAKAAKI, HARANO, YOSHIYUKI, TAKEMOTO, SHIN, WATANABE, SHOJI
Applicants: DAICEL CHEM, DAICEL CHEMICAL INDUSTRIES, LTD.
Application year: 1991
Main classification: C07C69
IPC codes: C08G63, C07D303, C07C69, C08G59