Glass joint body and method of manufacturing the same

Abstract: In order to improve a reliability of a glass joint body, first ceramic member (1) and second ceramic member (6) are connected by using (a) glass (9) consisting of 10-65% weight SiO 2 , 30 wt% or less of Na 2 O, and the balance of B 2 O 3 and Al 2 O 3 , (b) glass including less than 10 wt% of SiO 2 , and 30-80 wt% of B 2 O 3 , (c) glass including substantially none of SiO 2 , and 30-80 wt% of B 2 O 3 , or (d) glass consisting of 10-65 wt% of SiO 2 , 20 wt% or less of Na 2 O, 30 wt% or less of Al 2 O 3 , 20 wt% or less of MgO, and the balance of B 2 O 3 . The glass has good resistance to sodium corrosion.

Description: The present invention relates to glass joint bodies which are exposed in corrosive substances, and especially relates to the glass joint bodies to be used for a joint between β alumina and insulation ceramics in Alkali Metal Thermo-Electric Converter (AMTEC) or a secondary cell to be used in high temperatures such as a sodium-sulfur cell and to a method of manufacturing the glass joint bodies mentioned above. Usually, as for one example of glass joint bodies which are exposed in corrosive substances, there is known a sodium-sulfur cell or Alkali Metal Thermo-Electric Converter. The sodium-sulfur cells are high temperature type secondary cells which operate at 300°C ∼ 350°C and composed of metallic sodium as a cathode active material, sulfur and/or sodium polysulfide as an anode active material, a sodium ion conductive ceramic as a solid electrolyte, and a metal container. The structure of a typical sodium sulfur cell is shown in Fig. 1. In Fig. 1, the numeral 1 is a beta alumina tube, 2 metal container functioning as an anode, 3 sulfur or sodium polysulfide, 4 metal container functioning as a cathode, 5 sodium, 6 insulator such as α-alumina, 7 metal lid, 8 welded portion, and a numeral 9 is a joint glass for connecting the beta alumina tube 1 and the insulator 6. As for beta alumina material forming the beta alumina tube 1, use is made of β''-alumina, β-alumina, and mixture of the both, or the like. Processes for manufacturing the above-described sodium-sulfur cells generally comprise the steps of: bonding the open end periphery of the beta alumina tube 1 with the ring insulator 6 made of α-alumina by means of glass or the like; bonding the ring insulator 6 supporting the beta alumina tube 1 with the metal containers 2 and 4 by a solid phase reaction or the like at a high temperature under pressure; supplying the sodium 5 and the sulfur or sodium polysulfide 3 into the metal containers 4 and 2 respectively; and hermetically closing the metal container 4 with the lid 7 by means of the welding to provide a cell. In the sodium-sulfur cells mentioned above, since the joint glass 9 arranged between the beta alumina tube 1 and the insulator 6 made of α-alumina and the like is to be corroded by the sodium, a life of the sodium-sulfur cell is decreased. To eliminate the drawback mentioned above, a conjunction glass having a good durability against sodium corrosion consisting of 1 wt% of alkali earth metal oxides or less, SiO 2 : 65∼75 wt%, B 2 O 3 : 10∼25 wt%, and the balance of Aℓ 2 O 3 and alkali metal oxides is disclosed in Japanese Patent Laid-Open Publication No. 1-54672. The joint glass having the composition mentioned above shows a good durability against sodium corrosion as compared with the known silicate glass and boron silicate glass, but does not show a sufficient durability against sodium corrosion as yet. Therefore, the conjunction glass mentioned above is also corroded by the sodium and thus there is a drawback such that a life of the sodium-sulfur cell is also decreased. It would be desirable at least partly to eliminate the drawbacks mentioned above and to provide a glass joint body having a reliable glass joint portion and a method of the glass joint body mentioned above. In a first aspect of the invention, a glass joint body is provided according to claim 1. In a second aspect of the invention, a method of manufacturing a glass joint body is provided according to claim 7. In the structures of the first aspect of the invention, since the joint glass consisting of 10∼65 wt% of SiO 2 , 20 wt% of Na 2 O or less, 30 wt% of Aℓ 2 O 3 or less, 3 to 20 wt% of MgO, and the remainder of B 2 O 3 is used for a connection between ceramic member and ceramic member, a corrosion rate due to sodium can be controlled to be slow, and thus a reliability of the glass joint portion can be improved. Therefore, a life of the sodium-sulfur cell or the Alkali Metal Thermo-Electric Converter can be increased. In the glass composition of the first aspect of the invention, the reasons for limiting an amount of SiO 2 as 10∼65 wt% and for limiting an amount of Na 2 O as 20 wt% or less are as follows. If an amount of SiO 2 is less than 10 wt%, a thermal expansion coefficient is too increased and a residual stress due to the connection becomes larger, and thus cracks are generated when a connection operation is performed. Moreover, if an amount of SiO 2 is more than 65 wt%, a corrosion generation due to sodium becomes extremely high, and thus cracks are generated, in a short time under Na contacting state. Further, if an amount of Na 2 O is more than 20 wt%, a thermal expansion coefficient is increased and a residual stress due to the connection becomes larger, and thus cracks are generated when a connection operation is performed. Furthermore, it is preferred to limit an amount of SiO 2 as 20∼40 wt%. Moreover, the reason for limiting an amount of Aℓ 2 O 3 as 30 wt% or less and for limiting an amount of MgO as maximum 20 wt% are that, if an amount of Aℓ 2 O 3 is more than 30 wt% or an amount of MgO is more than 20 wt%, the glass crystallizes and cracks are generated. Further, preferable methods of connecting ceramic member to ceramic member are (1) method comprising the steps of arranging a glass frit between an alpha alumina and a beta alumina, and melting the glass by heat to connect the alpha alumina and the beta alumina by reacting glass and alpha alumina and also by reacting glass and beta alumina, or (2) method comprising the steps of arranging a glass block on a space between alpha alumina and beta alumina, melting the glass block by heat to be flowed into the space, and connecting the alpha alumina and the beta alumina by reacting glass and alpha alumina and also by reacting glass and beta alumina. Fig. 1 is a schematic view showing a sodium sulfur cell, as one embodiment of a glass joint body according to the invention; Fig. 2 is a schematic view illustrating an Alkali Metal Thermo-Electric Converter, as another embodiment of a glass joint body according to the invention; Fig. 3 is a cross sectional view depicting one embodiment of a specimen to which an anti-sodium test is performed; Fig. 1 is a schematic view showing one embodiment of a glass joint body according to the invention. In Fig. 1, the present invention is applied to a sodium-sulfur cell, and a construction of the sodium-sulfur cell is explained before, so that the explanation thereof is not repeated here. In this embodiment, as for the joint glass 9, use is made of glass consisting of 10∼65 wt% of SiO 2 , 20 wt% of Na 2 O or less, 30 wt% of Aℓ 2 O 3 or less, 3 to 20 wt% of MgO and the balance of B 2 O 3 . Fig. 2 is a schematic view showing another embodiment of a glass joint body according to the invention. In Fig. 2, the present invention is applied to a thermoelectric converting apparatus. In the Alkali Metal Thermo-Electric Converter shown in Fig. 2, a heat energy is directly converted into an electric energy to generate electricity by utilizing a beta alumina solid electrolyte through which a sodium ion is easily moved. In this embodiment, a numeral 11 is a stainless container, 12 an insulator made of α-alumina and arranged to the stainless container 11, 13 a beta alumina tube, 14 a joint glass for connecting the insulator 12 made of α-alumina and the beta alumina tube 13, 15 a heater for heating a sodium supplied into the beta alumina tube 13, 16 an Mo porous electrode formed on an outer surface of the beta alumina tube 13, 17 a pipe for supplying a sodium in the stainless container 11 into the beta alumina tube 13, 18 an electromagnetic pump for moving a sodium in the pipe 17, and numerals 19-1 and 19-2 are electrodes for output terminals. Also in this embodiment, it is necessary to use the joint glass 14 having a composition mentioned above. In the thermoelectric converting apparatus mentioned above, sodium supplied in the beta alumina tube 13 is heated by the heater 15 and is moved to the Mo porous electrode 16 by means of an ion conductivity, so that an output current is flowed between the electrodes 19-1 and 19-2. Moreover, sodium moved to the Mo porous electrode 16 by means of an ion conductivity is vapored from the Mo porous electrode 16, and is liquefied on an inner surface of the stainless container 17 maintained in low temperatures. In this manner, sodium is circulated in the thermoelectric converting apparatus. Hereinafter, actual embodiments will be explained. Example 1 In order to examine a connection state of a glass joint specimen and durability against sodium corrosion of a glass having various compositions in the first aspect of the invention, the following tests were performed. At first, glass frits having various chemical compositions as shown in Table 1 were prepared by measuring respective raw materials by means of an electric balance, mixing and crushing the raw materials in a mortar made of alumina, melting the mixed and crushed raw materials at 1400°C in a platinum crucible, casting the melted raw materials into a metal saucer whose inner surface is spread by carbon paste to effect a rapid cooling, and crushing the cooled glass. In order to make properties of the glass uniform, the thus prepared glass frits were further crushed in a mortar made of alumina by using an alumina pestle, and were re-melted at 1400°C in a crucible made of platinum. After that, the thus re-melted glass was rapidly cooled, and the cooled glass was further crushed in a mortar made of alumina by using an alumina pestle to obtain glass frits for a connection. By using the thus obtained glass frits, an alpha alumina circular plate 31 having a diameter of 40 mm and a thickness of 5 mm was connected to a beta alumina tube 32 having an outer diameter of 20.0 mm and an inner diameter of 17.5 mm at 1000°C to obtain a glass joint specimen, as shown in Fig. 3. Then, the glass joint specimen was gradually cooled from 700°C to 300°C at a cooling rate of 0.5°C/min to eliminate stresses. After that, the thus formed glass specimen was immersed in sodium at 450°C under N 2 atmosphere every 100 hours, and sodium was eliminated by using methanol. Then, a crack generation was examined by using fluorescent penetrant inspection every 100 hours. The results and the chemical compositions of the joint glasses were shown in Table 1. Specimen No. Chemical composition (wt%) Crack generation time (hr) SiO 2 Na 2 O B 2 O 3 Aℓ 2 O 3 MgO Example of present invention 1 64.0 5.0 13.0 13.0 5.0 500 2 60.0 5.0 17.0 13.0 5.0 800 3 50.0 5.0 27.0 13.0 5.0 1000 4 40.0 3.0 33.0 19.0 5.0 >2000 5 30.0 3.0 39.5 20.0 7.5 >2000 6 20.0 5.0 47.0 20.0 7.5 >2000 7 10.0 8.0 50.0 25.0 7.0 600 8 32.0 4.5 37.0 19.0 7.5 >2000 9 36.0 4.5 33.0 21.0 5.5 >2000 10 35.0 9.0 34.0 16.0 6.0 1700 11 32.0 3.0 33.0 29.0 3.0 1200 12 34.0 3.0 35.0 24.0 4.0 >2000 13 34.0 3.0 38.0 16.0 9.0 >2000 14 34.0 3.0 38.0 16.0 9.0 >2000 15 38.0 3.0 41.0 13.0 5.0 1600 16 35.0 4.0 30.0 12.0 19.0 1600 17 34.0 18.0 30.0 13.0 5.0 1100 Comparative example 18 67.0 4.0 19.0 7.0 3.0 crack generation in case of connection 19 30.0 4.5 30.0 32.0 3.5 crack generation in case of connection 20 35.0 4.0 28.0 10.0 23.0 crack generation in case of connection 21 32.0 22.0 30.0 11.0 5.0 crack generation in case of connection From the results shown in Table 1, it is understood that the specimen Nos. 1∼17 of the first aspect of the invention show good anti-corrosion properties since cracks are not generated at least for 400 hours, but the specimen Nos. 18∼21 of the comparative example generate cracks when the connection operation is performed. The reason of the crack generation in case of the connection operation is that a thermal expansion coefficient of the glass is not equal to that of a beta alumina or an alpha alumina. Example 2 A charge-discharge test was performed with respect to NaS cell using the glass joint body of the first aspect of the invention. That is to say, with respect to the sodium-sulfur cells wherein the beta alumina tube and the insulator made of alpha alumina are connected as shown in Fig. 1 by using glasses of the specimen Nos. 1∼17 in the example 1, the charge-discharge test was performed under a temperature of 350°C and a current density of 150 mA/cm 2 . As a result, all the sodium-sulfur cells can endure until 1000 cycle. Example 3 With respect to the specimen Nos. 4∼6, 8, 9, 12∼14 among the glass joint specimens in the example 1, a temperature ascent and descent test from room temperature to 350°C was performed under N 2 atmosphere, and a crack generation of the connection portion was examined every 5 times. As a result, all the specimens show no crack generation after tests of 10 times. Moreover, the specimen Nos. 4, 6, 12, 13, 14 show a small crack generation after tests of 15 times, and the specimen Nos. 5, 8, 9 show no crack generation even after tests of 30 times. As mentioned above, with the materials described, since ceramics and ceramics are connected with each other by using a glass having a predetermined chemical composition, a durability against sodium corrosion of the glass joint body can be improved. Therefore, if the present techniques are applied to the glass joint body used in the secondary cell of high temperature type such as the sodium-sulfur cell or the Alkali Metal Thermo-Electric Converter, a life of the apparatus can be increased.

Claims: A body including a glass joint, comprising a first ceramic member (1,3) and a second ceramic member (6;12) which are connected by a glass (9,14) consisting of all the components SiO 2 , Na 2 O, Al 2 O 3 , MgO and B 2 O 3 , said components being present in the respective amounts given by: 10-65 wt% of SiO 2 , an amount not exceeding 20 wt% of Na 2 O, an amount not exceeding 30 wt% of Al 2 O 3 , 3 to 20 wt% of MgO, and the balance substantially of B 2 O 3 . A body according to claim 1, wherein said first and second ceramic members are a beta alumina member (1,13) and an insulation ceramic member (6,12) in a secondary cell of high temperature type or in an Alkali Metal Thermo-Electric Converter. A body according to claim 1, used in a device in which the glass joint is subjected to exposure to sodium. A body according to any one of claims 1 to 3, wherein the glass contains not less than 3.0 wt% of Na 2 O. A body according to any one of claims 1 to 4, wherein the glass contains not less than 12.0 wt% of Al 2 O 3 . A body according to any one of claims 1 to 3, wherein the glass contains not less than 3.0 wt% of Na 2 O, not less than 12.0 wt% of Al 2 O 3 . A method of manufacturing a glass joint body comprising the steps of preparing glass consisting of all the components SiO 2 , Na 2 O, Al 2 O 3 , MgO and B 2 O 3 , said components being present in the respective amounts given by: 10-65 wt% of SiO 2 , an amount not exceeding 20 wt% of Na 2 O, an amount not exceeding 30 wt% of Al 2 O 3 , 3 to 20 wt% of MgO, and the balance substantially of B 2 O 3 ; and connecting a first ceramic member and a second ceramic member by using the prepared glass.

Inventors: MURAI MAKOTO, TAKAHASHI TOMONORI, YOSHIDA AKIHIKO, MURAI, MAKOTO, TAKAHASHI, TOMONORI, YOSHIDA, AKIHIKO
Applicants: NGK INSULATORS LTD, NGK INSULATORS, LTD.
Application year: 1991
Main classification: C03C8
IPC codes: H01M10, C03C8, C04B37, H01M2