Pigment consisting of polyvalent metal salt of amidosulfonic acid and cosmetic composition containing the same

Abstract: sA pigment consisting of a polyvalent metal salt of an amidosulfonic acid represented by the following general formula (I): wherein R¹ represents a straight-chain or branched alkyl, alkenyl or hydroxyalkyl group each having 7 to 21 carbon atoms; R² represents a hydrogen atom or a methyl group; X represents an ethylene group, a propylene group or M represents a polyvalent metal atom; m represents the valence of M: and n is an integer of from 1 to 4; and a pigment consisting of a polyvalent metal salt of an acylated amino acid represented by the following general formula (II): wherein R¹ represents a straight-chain or branched alkyl, alkenyl or hydroxyalkyl group each having 7 to 21 carbon atoms; Y represents a number selected from among 1, 2, 3, 4, 5, 10, and 11; M represents a polyvalent metal atom; m represents the valence of M: and n is an integer of from 1 to 4; as well as cosmetic compositions containing these pigments are disclosed.

Description: FIELD OF THE INVENTION This invention relates to a pigment comprising a polyvalent metal salt of an amidosulfonic acid and an excellent cosmetic composition which contains the pigment, which cosmetic has good spreadability on the skin, high adhesiveness, high smoothness, a good finish, a long makeup life, good molding characteristics and a good feel upon use. BACKGROUND OF THE INVENTION N-acyl-N-alkyl-taurine salts are known as surfactants for cosmetics use as disclosed in, for example, Chemical Abstracts, 110 (16) 141226e (1989) and Chemical Abstracts, 112 (10) 83842f (1990). However, no applications for cosmetics use have been found as far as the water-insoluble salts of an amidosulfonic acid. Known powdery pigments for cosmetics which are insoluble in water or oil include inorganic extender pigments such as talc and mica; inorganic color pigments such as titanium dioxide and zinc oxide; organic color pigments such as organic tar coloring materials; composite pigments such as mica/titanium; resin powders such as nylon powder; and coated powders prepared by treating the surface of these pigments with a known coating agent such as silicone. US-A-4 606 914 also shows coated powders for cosmetics, namely a cosmetic composition containing a pigment or an extender pigment, the surfaces of which are coated with a metal salt of N-acylamino acid. Although these known pigments are employed in cosmetics in an appropriate amount by taking the spreadability, adhesiveness, covering characteristics and molding characteristics thereof into consideration, cosmetics containing them are not always satisfactory in, for example, spreadability, smoothness, adhesiveness, finishing, makeup life, stability and molding characteristics. In the case of a powdery cosmetic containing a common extender pigment such as talc or mica as a base, for example, the use of talc or mica of a large particle size, which are selected in order to enhance smoothness, would make the cosmetic product coarse and, as result, the obtained cosmetic would be poor in, for example, adhesiveness, molding characteristics and makeup life. Sometimes a spherical resin powder such as nylon powder or polystyrene powder has been used. However, such a pigment, which gives a dry feel and has a poor adhesiveness, fails to impart any softness or moist feel to a cosmetic. Further, such powders deteriorate not only the adhesiveness of the cosmetic to the skin but also the molding characteristics thereof. On the other hand, it has been attempted to add a metal soap to a cosmetic in order to improve the adhesiveness, molding characteristics and makeup life of the cosmetic. However, a metal soap cannot impart satisfactory characteristics including smoothness and adhesiveness to a cosmetic. Therefore, the art is in need of a pigment which can provide high spreadability, high smoothness, high adhesiveness, long makeup life, high stability and excellent molding characteristics as well as a cosmetic composition which contains such a pigment and has a good feel upon use. SUMMARY OF THE INVENTION In light of the above, the present inventors have conducted extensive studies, and, as a result, they found that a cosmetic composition containing a pigment comprising a polyvalent metal salt of an amidosulfonic acid represented by the following general formula (I) has excellent properties including spreadability, smoothness and a good feel upon use, to thereby reach the present invention. Accordingly, the present invention provides a pigment consisting of a polyvalent metal salt of an amidosulfonic acid represented by the following general formula (I): wherein R¹ represents a straight-chain or branched alkyl, alkenyl or hydroxyalkyl group each having 7 to 21 carbon atoms; R² represents a hydrogen atom or a methyl group; X represents an ethylene group, a propylene group or a group; M represents a polyvalent metal atom; m represents the valence of M and n is an integer of from 1 to 4; and a cosmetic composition containing such pigment. BRIEF DESCRIPTION OF THE DRAWING Fig. 1 is a scanning electron microscopic photograph showing the crystal structure of N-lauroyltaurine calcium salt obtained in Production Example 1. DETAILED DESCRIPTION OF THE INVENTION As the group R¹ given in the general formula (I), examples of the alkyl group include heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, nonadecyl, eicosyl and heneicosyl groups; examples of the alkenyl group include 2-heptenyl, 2-octen-8-ynyl, 3,4-dipropyl-1,3-hexadien-5-ynyl, 5,5-dimethyl-1-hexyl, 4-vinyl-1-hepten-5-ynyl, 5-(3-pentenyl)-3,6,8-decatrien-1-ynyl, 6-(1,3-pentadienyl)-2,4,7-dodecatrien-9-ynyl and 2-nonyl-2-butenyl groups; and examples of the hydroxyalkyl group include hydroxyheptyl, hydroxydecyl, hydroxytetradecyl and hydroxynonadecyl groups. Among them, straight-chain alkyl group having 9 to 15 carbon atoms are preferred and nonyl, undecyl, tridecyl and pentadecyl groups are more preferred. Examples of the polyvalent metal represented by M include Al, Ca, Zn, Zr, Mg, Fe, Ba and Ti. Among the polyvalent metals, Ca, Zn, Mg and Ba are preferred. Specific and preferred examples polyvalent metal salt of the amidosulfonic acid of formula (I) include, for example, N-lauroyltaurine Ca salt, N-lauroyltaurine Ba salt, N-lauroyltaurine Zn salt, N-palmitoyltaurine Ca salt, N-palmitoyltaurine Ba salt, N-lauroyltaurine Zn salt. The polyvalent metal salt of an amidosulfonic acid (I), which is used as a pigment component of a cosmetic composition herein should be either insoluble or substantially insoluble in water. The polyvalent metal salt of an amidosulfonic acid (I) of the present invention may be produced by, for example, a method similar to those employed for synthesizing common metal soaps. That is to say, the pigment of the present invention comprising the polyvalent metal salt of an amidosulfonic acid may be produced by, for example, dissolving a water soluble salt (e.g., Na salt, K salt, NH₄ salt, alkanolamine salts) of an amidosulfonic acid represented by the formula: wherein R¹, R² and X are as defined above, in water, adding an aqueous solution of a water soluble polyvalent metal salt in a substantially equivalent amount thereto, preferably within a period of time of from 15 to 120 minutes, salt exchanging, thoroughly stirring, filtering, washing with water and then drying. Examples of the water soluble polyvalent metal salt to be used include aluminum sulfate, aluminum chloride, aluminum nitrate, aluminum potassium sulfate, magnesium chloride, magnesium sulfate, magnesium nitrate, magnesium potassium sulfate, calcium chloride, zinc chloride, zinc nitrate, zinc sulfate, zinc acetate, zirconium sulfate, zirconium chloride, titanium oxysulfate and titanium tetrachloride. The particle size of the obtained polyvalent metal salt of an amidosulfonic acid may be increased as the time of adding the water soluble polyvalent metal salt is increased. The powdery crystals of the polyvalent metal salt of an amidosulfonic acid thus obtained are in the form of needles, columns or plates, depending on the reaction conditions and the salt employed. Monoclinic plates are particularly preferable since they can give an excellent feel upon use in a cosmetic. The polyvalent metal salt of an amidosulfonic acid pigment (I) thus obtained may be used in a cosmetic composition as such. Alternately, it may be used for treating some another powders to give hydrophobic powders. Although the particle size of the polyvalent metal salt of an amidosulfonic acid (I) to be used in the cosmetic composition of the present invention is not particularly restricted, the average particle size preferably ranges from 0.1 to 50 µm. When it is smaller than 0.1 µm, a satisfactory smoothness may not be achieved. When it exceeds 50 µm, on the other hand, a coarse feel may become noticeable. The polyvalent metal salt of an amidosulfonic acid (I) is preferably contained in the cosmetic composition of the present invention in an amount of from 0.1 to 99 % by weight based on the total weight of the cosmetic composition. When the content thereof is smaller than 0.1 % by weight, the above-described effects may not be fully achieved. The average particle size used herein means the particle size of 50% cumulative distribution in the cumulative distribution of the volume measured by the laser diffraction method using an SK laser manufactured by Seishin Kigyo K.K. In addition to the above-mentioned polyvalent metal salt of an amidosulfonic acid (I), the cosmetic composition of the present invention may further contain a cosmetic powder as is commonly employed in the art as well as optional components such as various oils, surfactants, wetting agents, water, alcohols, preservatives, UV absorbers, antioxidants and perfumes, if desired or necessary. Any known cosmetic powder may be used so long as the effects of the present invention are not deteriorated thereby. Examples thereof include inorganic extender pigments such as talc, kaolin, mica, sericite and synthetic mica; inorganic colorants such as titanium oxide, zinc oxide, ultramarine chromium oxide and iron oxide; organic colorants such as organic tar coloring materials and lakes; composite cosmetics such as mica/titanium and iron oxide-coated mica; spherical powders such as nylon powder, polymethyl methacrylate (PMMA) and silica beads; and powders prepared by treating the surface of the above-mentioned cosmetic powders with a coating agent such as a silicone, higher fatty acid, higher alcohol, ester or wax. Either one of these materials or a mixture thereof may be used. When a makeup cosmetic or a body cosmetic is to be produced, it is preferable to select an inorganic powder (for example, talc, kaolin sericite, mica, titanium oxide, iron oxide, mica/titanium, iron oxide-coated mica) from among the above-mentioned ones. With respect to optional components, examples of useful oils include liquid paraffin, vaseline, paraffin wax, polyethylene wax, squalane, ceresin wax, beeswax, carnauba wax, candelilla wax, hardened castor oil, olive oil, lanolin, lanolin alcohol, lanolin fatty acids, higher alcohols, fatty acids, synthetic ester oils obtained from higher alcohols and fatty acids and silicone; examples of useful surfactants include anionic surfactants such as soaps, alkyl sulfates and monoalkyl phosphates and nonionic surfactants such as polyoxyethylene alkyl ethers, polyoxyethylene fatty acid esters, polyoxyethylene sorbitan fatty acid esters, sorbitan fatty acid glycerol fatty acid eaters, polyoxyethylene hardened castor oil and polyoxyethylene sorbitol fatty acid esters; examples of useful wetting agents include sorbitol, glycerol, propylene glycol, isopropylene glycol 1,3-butylene glycol, lactic acid and sodium lactate polyethylene glycol; examples of useful preservatives include p-oxybenzoic alkyl esters, sodium benzoate, potassium sorbate and phenoxyethanol; examples of useful antioxidants include tocopherol, sesamol, sesamolin and lecithin; and examples of useful UV absorbers include 2,4-dihydroxybenzophenone and 2,2'-dihydroxy-4-methoxybenzophenone; though the present invention is not restricted thereto. The form of the cosmetic composition of the present invention is not particularly restricted. Namely, components including those described above may be arbitrarily combined and processed in a conventional manner to thereby give cosmetics of various forms (for example, powders, oils, emulsions, solutions, or aqueous dispersions). More particularly, the cosmetic composition of the present invention may be in the form of, for example, a powder foundation, eye shadow, emulsion foundation, lipstick, cosmetic base, nail enamel, eye-liner, body powder, baby powder or rouge. Among these cosmetics, powder cosmetics comprising from 1 to 80% by weight of the pigment of the present invention, from 1 to 80% by weight of an other known cosmetic powder and from 1 to 20% by weight of oils are preferred. When used in a cosmetic composition, the polyvalent metal salt of an amidosulfonic acid of the present invention gives high smoothness, has roughness, gives high transparency and has good water repellency. When spread onto the skin, it furthermore provides highly excellent effects, namely, giving an appropriate moistening effect without any overcoated feel and showing good water repellency. Furthermore, the polyvalent metal salt of an amidosulfonic acid of the present invention may be used as particles in a processing lubricant for molding plastics, an extender pigment for paints, a coating lubricant for paper and in a recording materials and in a lubricant for plastic processing of metals, by taking advantage of the smoothing effect thereof. To further illustrate the present invention, the following Production Examples, Examples and Test Example will be given. The present invention is not restricted by these examples but rather is applicable to any makeup cosmetics. PRODUCTION EXAMPLE 1 20 g of N-lauroyltaurine sodium salt and 380 g of ion exchanged water were introduced into a 1 ℓ four-necked flask provided with a stirrer, a dropping funnel and a thermometer and formulated into a homogeneous solution. The obtained solution was heated to 40°C under stirring and 135 g of a 5 % by weight aqueous solution of calcium chloride was added dropwise thereto from the dropping funnel within 15 minutes while keeping the solution at 40°C. Simultaneously with the addition, crystals of N-lauroyltaurine calcium salt were precipitated. After the completion of the addition, the mixture was further stirred at 40°C for 1 hour to complete the salt exchange. After the completion of the stirring, the mixture was allowed to stand to cool to room temperature. It was then filtered and washed. The crystals thus obtained were dried at room temperature. Thus, 19.4 g of the target N-lauroyl-taurine calcium salt was obtained as white crystals (yield: 98.9 %). When observed with a scanning electron microscope, she N-lauroyltaurine calcium salt thus obtained was in the form of plates, as shown in Fig. 1. Analytical data : Elemental analysis: found calculated Ca (%) 6.1 6.1 N (%) 4.3 4.3 IR (cm⁻¹): CON 1655, 1580 SO₃ 1210 Particle size: Average particle size: 7.9 µm. Determined using an SK LASER MICRON SIZER (manufactured by Seishin Kigyo K.K.), the same will apply hereinafter. Particle size distribution: Particle size (µm) Cumulative distribution of volume at fixed particle size (%) 1.0 1.2 1.5 2.5 2.0 5.9 3.0 12.2 4.0 20.4 6.0 34.5 8.0 50.5 12.0 70.6 16.0 82.2 24.0 95.0 32.0 100.0 48.0 100.0 64.0 100.0 96.0 100.0 128.0 100.0 192.0 100.0 PRODUCTION EXAMPLE 2 20 g of N-palmitoyltaurine sodium salt and 380 g of ion exchanged water were introduced into a 1 ℓ four-necked flask provided with a stirrer, a dropping funnel and a thermometer and formulated into a homogeneous solution. The obtained solution was heated to 40°C under stirring and 115 g of a 5 % by weight aqueous solution of calcium chloride was added dropwise thereto from the dropping funnel within 15 minutes. Simultaneously with the addition, crystals of N-palmitoyltaurine calcium salt were precipitated. After the completion of the addition, the mixture was further stirred at 40°C for 1 hour to complete the salt exchange. After the completion of the stirring, the mixture was allowed to stand to cool to room temperature. Then, it was filtered and washed. The crystals thus obtained were dried at room temperature. Thus, 19.5 g of the target N- palmitoyltaurine calcium salt was obtained as white crystals (yield: 98.3 %). This product was in the form of plates of 2.4 µm in average. Particle size distribution: Particle size (µm) Cumulative distribution of volume at fixed particle size (%) 1.0 9.0 1.5 20.4 2.0 40.4 3.0 66.5 4.0 82.5 6.0 95.3 8.0 100.0 12.0 100.0 16.0 100.0 24.0 100.0 32.0 100.0 48.0 100.0 64.0 100.0 96.0 100.0 128.0 100.0 192.0 100.0 PRODUCTION EXAMPLE 3 Similar to the procedure described in Production Examples 1 and 2, a 5 % by weight aqueous solution of barium chloride was added dropwise to a homogeneous solution of N-lauroyltaurine sodium salt. Thus, the target compound N-lauroyltaurine barium was obtained as white crystals (yield: 98.7 %). The obtained product was in the form of plates of 3.9 µm in average particle size. Particle size distribution: Particle size (µm) Cumulative distribution of volume at fixed particle size (%) 1.0 7.7 1.5 14.4 2.0 24.5 3.0 39.9 4.0 50.8 6.0 64.0 8.0 74.5 12.0 85.0 16.0 91.4 24.0 98.2 32.0 100.0 48.0 100.0 64.0 100.0 96.0 100.0 128.0 100.0 192.0 100.0 TEST EXAMPLE 1 The relative coefficients of friction of the polyvalent metal N-amidosulfonates produced in Production Examples 1 to 3 and those of mica and sericite, which are extender pigments, were determined in the following manner. A definite amount of each sample was applied onto a tracing paper and the coefficient of friction thereof was measured using a surface properties tester Heidon 14 (manufactured by Shinto Kagaku K.K.). The ratio of the coefficient of friction thus measured to that of the tracing paper per se was referred to as the relative coefficient of friction. Table 1 shows the results. EXAMPLE 1 (Powder foundation) Formulation (by weight %) (1) N-lauroyltaurine Ca salt (Product Example 1) 20 (2) talc balance (3) sericite 10 (4) titanium oxide 1 (5) red iron oxide 1.5 (6) black iron oxide 0.2 (7) yellow iron oxide 2 (8) fine wax powder (pressing aid) 10 (9) perfume 0.1 Total 100. The following production method was used. The powdery components were mixed together and ground. Then the mixture was introduced into a Henschel mixer and the oil and the perfume were added thereto. After homogeneously mixing, the mixture was press molded in a metal plate to thereby give the desired product. The foundation thus obtained was excellent in texture including spreadability and had good water repellency and high compatibility with the skin. EXAMPLE 2 (Loose-type face powder) Formulation (% by weight) (1) N-palmitoyltaurine Ca salt (Production Example 2) 50 (2) talc balance (3) titanium oxide 0.5 (4) red iron oxide 0.1 (5) liquid paraffin 1 (6) perfume 0.1 Total 100. The following production method was used. The powdery components (1) to (4) were mixed together and ground. Then the mixture was introduced into a Henschel mixer and the oil and the perfume were added thereto. After homogeneously mixing, the mixture was passed through a sieve to thereby give the desired product. The loose-type face powder thus obtained was an excellent product since it showed good spreadability without a powdery feel as observed with conventional loose-type face powders. EXAMPLE 3 (Oily foundation) Formulation (% by weight) (1) N-lauroyltaurine Ba salt (Production Example 3) 20 (2) talc balance (3) kaolin 5 (4) titanium oxide 5 (5) red iron oxide 1 (6) black iron oxide 0.1 (7) yellow iron oxide 0.6 (8) squalane 25 (9) isopropyl palmitate 15 (10) ceresin 7 (11) perfume 0.1 Total 100. The following production method was used. The powdery components were mixed together and ground. Then the mixture was added to the oily components, which had been separately heated, under stirring. After homogeneously mixing, the mixture was packed in a metal plate and cooled to thereby give the desired product. The oily type face powder thus obtained was excellent in texture including spreadability and had good water repellency and high compatibility with the skin. EXAMPLE 4 (Creamy foundation) Formulation (% by weight) (1) N-palmitoyltaurine Ca salt (Production Example 2) 5 (2) N-lauroyltaurine Ba salt (Production Example 3) 10 (3) titanium oxide 5 (4) red iron oxide 1 (5) black iron oxide 0.1 (6) yellow iron oxide 0.6 (7) water balance (8) preservative 0.1 (9) triethanolamine 1.2 (10) sorbitol 3 (11) stearic acid 5 (12) lipophilic glycerol monostearate 2.5 (13) cetostearyl alcohol 1 (14) propylene glycol monolaurate 3 (15) squalane 25 (16) olive oil 8 (17) perfume 0.1 Total 100. The following production method was used. Powdery components (1) to (6) were mixed together and ground. Separately, a solution comprising the aqueous phase components (7) to (10) was prepared and the ground powdery components were dispersed therein followed by heating to 75°C. Then the oily components (11) to (16) molten by heating to 80°C were added to the aqueous phase prepared above under stirring and emulsified therein. The obtained emulsion was cooled under stirring and perfume (17) was added thereto at 50°C. The mixture was then cooled under stirring to yield the desired product. EXAMPLE 5 (Finishing powder) Formulation (% by weight) (1) mica balance (2) N-lauroyltaurine Ca salt (Production Example 1) 50 (3) talc 20 (4) titanium oxide 0.5 (5) red iron oxide 0.1 (6) yellow iron oxide 0.1 (7) black iron oxide 0.01 (8) liquid paraffin 8 (9) beeswax 2 (10) preservative trace (11) perfume trace Total 100. The following production method was used. Components (1) to (7) were mixed together and ground. Then the mixture was introduced into a high-speed blender and components (8) to (10) which had been mixed and melted by heating to at 80°C were added thereto. After homogeneously mixing, component (11) was further added thereto and the obtained mixture was ground again and passed through a sieve. The mixture was then compression-molded in a metal plate to give the desired product.. EXAMPLE 6 (Creamy foundation) Formulation (% by weight) (1) stearic acid 5.5 (2) lipophilic glycerol monostearate 2.5 (3) cetostearyl alcohol 1 (4) propylene glycol monolaurate 3 (5) squalane 7 (6) olive oil 8 (7) water balance (8) preservative trace (9) triethanolamine 1.2 (10) sorbitol 3 (11) titanium oxide 10 (12) talc 5 (13) color pigment trace (14) N-palmitoyltaurine Ca salt (Production Example 2) 8 (15) perfume trace Total 100. The following production method was used. Compound (11) to (14) were mixed together and ground. Separately, the aqueous phase components (7) to (10) were mixed together to thereby give a solution in which ground components (11) to (14) were dispersed followed by heating to 75°C. The oily phase components (1) to (6) were melted by heating to 80°C and would then added to the aqueous phase prepared above under stirring and emulsified therein. The obtained emulsion was cooled under stirring and then perfume (15) was added thereto at 50°C. The mixture was cooled under stirring to thereby give the desired product. EXAMPLE 7 (O/W type cream) Formulation (% by weight) (1) beeswax 5.5 (2) cetanol 4.5 (3) hydrogenated lanolin 7 (4) squalane 33 (5) fatty acid glycerol 3.5 (6) lipophilic glycerol monostearate 2 (7) polyoxyethylene sorbitan monolaurate (20 E.O.) 2 (8) N-lauroyltaurine Ba salt (Production Example 3) 8 (9) perfume trace (10) preservative trace (11) antioxidant trace (12) propylene glycol 5 (13) water trace Total 100. The following production method was used. An aqueous phase comprising components (8), (10), (12) and (13) was mixed under stirring and maintained at 80°C. The other components were mixed together and melted by heating followed by maintaining those components at 80°C. To the oily phase thus obtained was added the above-mentioned aqueous phase followed by preliminarily emulsifying. After homogeneously emulsifying in a homomixer, the mixture was cooled to 30°C to thereby give the desired product. EXAMPLE 8 (Solid face powder) Formulation (% by weight) (1) mica balance (2) N-lauroyltaurine Ca salt (Production Example 1) 50 (3) talc 20 (4) titanium oxide 0.5 (5) red iron oxide 0.1 (6) yellow iron oxide 0.1 (7) black iron oxide 0.01 (8) liquid paraffin 8 (9) beeswax 2 (10) preservative trace (11) perfume trace Total 100. The following production method was used. Components (1) to (7) were mixed together and ground. Then the ground mixture was introduced into a high-speed blender. The components (8) to (10), which had been mixed and melted at 80°C, were added thereto followed by homogeneously mixing. The component (11) was added to the obtained mixture. The resulting mixture was ground again, passed through a sieve and compression-molded in a metal plate to give the desired product. EXAMPLE 9 (Rouge) Formulation (% by weight) (1) mica balance (2) N-palmitoyltaurine Ca salt (Production Example 2) 50 (3) talc 20 (4) titanium oxide 4 (5) zinc stearate 5 (6) rice starch 5 (7) coloring material 3 (8) liquid paraffin 3 (9) preservative trace (10) perfume trace Total 100. The following production method was used. Components (1) to (7) were mixed together and color developed. Then, components (8) to (10) were added thereto by spraying in a mixer. After homogeneously mixing, the obtained mixture was passed through a sieve and compressed in a metal plate with a press to give the desired product. EXAMPLE 10 (Eye shadow) Formulation (% by weight) (1) mica balance (2) N-lauroyltaurine Ba salt (Production Example 3) 50 (3) talc 5 (4) mica/titanium 5 (5) zinc stearate 5 (6) zinc laurate 3 (7) color pigment 10 (8) liquid paraffin 7.5 (9) preservative trace (10) perfume trace Total 100. The following production method was used. Components (1) to (7) were mixed together and color developed. Then, components (8) to (10) were added thereto by spraying in a mixer. After homogeneously mixing, the mixture was passed through a sieve and compressed in a metal plate with a press to give the desired product. EXAMPLE 11 (Lipstick) Formulation (% by weight) (1) titanium oxide 1 (2) Red No. 201 1 (3) Red No. 202 2 (4) Yellow No. 4 aluminum lake 1 (5) Red No. 223 0.1 (6) N-lauroyltaurine Ca salt (Production Example 1) 5 (7) castor oil balance (8) octyl dodecanol 15 (9) lanolin 5 (10) liquid lanolin 5 (11) beeswax 5 (12) ozokerite 4 (13) candelilla wax 7 (14) carnauba wax 1 (15) antioxidant trace (16) preservative trace (17) perfume trace Total 100. The following production method was used. Components (7) to (14) were melted by heating and homogeneously mixed together. Then, components (1) to (6) were added thereto and the system was homogeneously dispersed by kneading in a roll mill. Next, the dispersion was melted again and components (15) to (17) were added thereto. After defoaming, the mixture was poured into a mold and cooled quickly to mold it. Then, it was taken out and packed in a container. After formulating into a stick, it was passed through a flame to thereby give it a uniform surface. EXAMPLE 12 (Eye liner) Formulation (% by weight) (1) carnauba wax 5 (2) beeswax 1 (3) microcrystalline wax 10 (4) white vaseline 1 (5) light liquid isoparaffin balance (6) organic bentonite 0.5 (7) N-lauroyltaurine Ba salt (Production Example 3) 10 (8) titanium oxide 3 (9) carbon black 2 (10) preservative trace Total 100. The following production method was used. Component (6) was added to a portion of component (5) and the obtained mixture was dispersed through a colloid mill to thereby give a gel. On the other hand, components (1) to (4) and (10) were mixed together and dissolved by heating. After adding the components (7) to (9), the mixture was cooled and kneaded in a roll mill. After melting by heating again, the bentonite gel as obtained above and the balance of component (5) were added followed by cooling under stirring to give the desired product.

Claims: A pigment consisting of a polyvalent metal salt of an amidosulfonic acid represented by the following general formula (I): wherein R¹ represents a straight-chain or branched alkyl, alkenyl or hydroxyalkyl group each having 7 to 21 carbon atoms; R² represents a hydrogen atom or a methyl group; X represents an ethylene group, a propylene group or a group; M represents a polyvalent metal atom; m represents the valence of M and n is an integer of from 1 to 4. A cosmetic composition containing a pigment of claim 1. A cosmetic composition of claim 2, wherein said pigment is contained in an amount of from 0.1 to 99 % by weight. A cosmetic composition containing from 1 to 80 % by weight of a pigment of claim 1, from 1 to 80 % by weight of an other cosmetic powder, and from 1 to 20 % by weight of an oil. Use of a pigment of claim 1 into a cosmetic composition.

Inventors: NOZAKI TOSHIO, SHINOHARA RYUTARO, TACHIZAWA OSAMU, NOZAKI, TOSHIO, SHINOHARA, RYUTARO, TACHIZAWA, OSAMU
Applicants: KAO CORP, KAO CORPORATION
Application year: 1991
Main classification: A61K7
IPC codes: C09B57, C08K9, A61K8, A61Q1