Semiconductor laser and manufacturing method of the same

Abstract: A semiconductor laser comprises an optical wave guide layer (6) including an AlGaInP active layer (62) and AlGaInP optical confinement layers (61, 63) holding the active layer (62) therebetween. A well structure of an energy band is formed and a compressive stress is applied to the activation layer by the difference between the compositions of the activation layer and the optical confinement layers. Since the compressive stress is applied to the activation layer, the oscillation threshold is lower than that of an un-strained device. Accordingly, the rise of the oscillation threshold due to the addition of Al is compensated and continuous oscillation at room temperature is attained and visible light having a wavelength of 0.67 µm or lower, which has been difficult to attain in the past, is produced. The semiconductor laser having a multi-quantum well structure is manufactured by using AlGaInP or GaInP as a semiconductor material of the multi-quantum well structure and epitaxially growing by periodically changing a supply rate of only In. Through a very simple method of periodically changing the supply rate of only In, a well layer having a compressive stress applied thereto and a barrier layer having a tensile stress applied thereto are alternately grown and the activation layer having the desired strained multi-quantum well structure is produced.

Description: The present invention relates to a semiconductor laser and a manufacturing method of the same, and more particularly to a semiconductor laser suitable for the emission of visible light and a manufacturing method of the same. A strained single quantum well visible laser diode is described in Electronic Letters, Vol. 26, No. 17, pp 1375-1377. Another laser diode is described in EP-A-0 456 429 (a reference under Art. 54(3)). Several years ago, a He-Ne gas laser was used in most cases to generate a bright red laser beam. Recently, the practical use of a visible light semiconductor laser which uses GaInP as an active layer has been so advanced that a light having a wavelength of 0.67 µm is generated by the semiconductor laser. However, since the wavelength of 0.67 µm is longer than the wavelength of 0.6328 µm of the He-Ne gas laser, the visual sensitivity thereto is lower than that of the He-Ne gas laser. As a result, in the field of the semiconductor laser, there is a demand for further shortening the wavelength to approach to the wavelength of 0.6328 µm of the He-Ne gas laser. On the other hand, it has been proved that the emission wavelength can be further shortened by adding Al to the active layer. However, when Al is added to the active layer, non-radiative recombination centers associated with A1 increase and the confinement of carriers is diminished by the large band gap of the active layer. As a result, the laser oscillation is hard to be obtained and it is difficult to continuously oscillate at room temperature, or the durability is short even if the continuous oscillation is attained. According to one aspect of the present invention, there is provided a semiconductor laser using a GaAs substrate comprising an optical waveguide layer disposed between a pair of cladding layers, the waveguide layer having an (Al x Ga 1-x ) y In 1-y P active layer where x>0 and AlGaInP optical confinement layers holding said active layer therebetween, wherein an energy band having a well structure is formed and a compressive stress is applied to said active layer by a difference between the compositions of said active layer and said optical confinement layers wherein the value x is selected in accordance with a desired oscillation wavelength of equal to or shorter than 0,67 µm and the value y is selected such that, the lattice constant A of the active layer and the lattice constant B of said GaAs substrate satisfy the relation 0.003 <(A-B)/B < 0.01, and wherein said well structure is a multi-well structure including well layers and barrier layers, the barrier layers isolating the well layers and the lattice constants of the epitaxial layers other than the active layer including the AlGaInP optical confinement layers and the cladding layers are substantially equal to that of the GaAs substrate and the active layer is than to the extent that mis fit dislocations are not generated. Since the compressive stress is applied to the active layer in the present invention, the oscillation threshold is lower than that of an unstrained type. Accordingly, it can oppose the rise of the oscillation threshold due to the addition of Al and continuous oscillation at room temperature is attained. Thus, visible light having a wavelength of 0.67 µm or smaller, which has not been attainable in the past, is produced. The compressive stress is imparted by strain due to a difference between lattice constants of the active layer to the GaAs substrate. Thus, it should be thin to the extent that misfit dislocations are not generated. Since the optical confinement layers are provided above and below the active layer, the total thickness of the optical waveguide layer is sufficiently large. The present invention is applicable to a laser which continuously oscillates at a room temperature at a wavelength of 0.64 µm or shorter. According to another aspect of the present invention, there is provided a method of manufacturing a semiconductor laser according to said one aspect having a multi-quantum well (Al x Ga 1-x ) y In 1-y P active layer where x>0, comprising the step of epitaxially growing the multi-quantum well structure by periodically changing the supply rate of only In. When organo-metallic vapor phase epitaxy (OMVPE) is used in the epitaxial growth, the supply rate of only In is periodically changed by periodically changing a flow rate of organic In gas. When molecular beam epitaxy (MBE) is used in the epitaxial growth, two In injection cells are provided and one of the In injection cells is kept active while the other In injection cell is periodically activated and deactivated to periodically change the supply rate of only In. By periodically changing the supply rate of In, a well layer having a compressive stress applied thereto and a barrier layer having a tensile stress applied thereto are alternately grown to form a strained multi-quantum well structure. Thus, the active layer having the desired strained multi-quantum well structure is formed by a very simple method of periodically changing the supply rate of In, and a semiconductor laser having a low threshold and a high power can be easily manufactured. The present invention will become more fully understood from the detailed description given hereinbelow and the accompanying drawings which are given by way of illustration only, and thus are not to be considered as limiting the present invention. Further scope of applicability of the present invention will become apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and specific examples, while indicating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the scope of the invention as defined by the claims will become apparent to those skilled in the art from this detailed description. In the drawings: Fig. 1 shows a sectional structural view of an illustrative example of a semiconductor laser; Fig. 2 shows an energy band thereof; Fig. 3 shows a current-photo-output characteristic; Fig. 4 shows a perspective view of a laser light emitting device; Fig. 5 shows a sectional structural view of an embodiment of the present invention; Fig. 6 shows an energy band of the embodiment in Fig. 5; and Fig. 7 shows a graph of flow rate control of raw material gas in manufacturing the semiconductor laser of the embodiment in Fig. 5. By way of example useful for understanding the invention, Fig. 1 shows a sectional structural view of a semiconductor laser, not forming part of the claimed invention. A semiconductor laser 1 uses an n-GaAs substrate 2. An n-type electrode 3 is formed on a rear side of the n-GaAs substrate 2, and on an upper side thereof, an n-AlGaInp cladding layer 5, an AlGaInP optical waveguide layer 6, a p-AlGaInP cladding layer 7 and a p-GaInP layer 9 are sequentially grown on an n-GaAs barrier layer 4 by epitaxial growth. The AlGaInP optical waveguide layer 6 is of three-layer structure which comprises an AlGaInP optical confinement layer 61, an AlGaInP strained active layer 62 and an AlGaInP optical confinement layer 63. Since the refractive index of the optical waveguide layer 6 is higher than those of the n-AlGaInP cladding layer 5 and the p-AlGaInP cladding layer 7, the laser beam generated in the AlGaInP strained active layer 62 is confined in the optical waveguide layer 6. The p-AlGaInP cladding layer 7 has both shoulders thereof etched away as shown to form a mesa which extends normally to the plane of the drawing. The n-GaAs blocking layers 8 are buried in the etched-away areas to the substantially same height as that of the surface of the p-GaInP layer, and a p-GaAs contact layer 10 and a p-electrode 11 are formed thereon. Carrier concentrations of the respective layers are n = 2 x 10 18 cm -3 for the n-GaAs substrate 2 and the n-GaAs barrier layer 4, n = 2 x 10 17 cm -3 for the n-AlGaInP cladding layer 5, p = 5 x 10 17 cm -3 for the p-AlGaInP cladding layer 7, and p = 2 x 10 18 cm -3 for the p-GaInP layer 9 and the p-GaAs contact layer 10. The thicknesses of the respective layers are 80 µm for the n-GaAs substrate 2, 0.5 µm for the n-GaAs buffer layer 4, 1 µm for the n-AlGaInP cladding layer 5, 0.21 µm for the optical waveguide layer 6, 1 µm for the p-AlGaInP cladding layer 7 (0.5 µm at the opposite shoulders), 0.2 µm for the n-GaAs blocking layer 8, and 0.3 µm for the p-GaAs contact layer 10. Fig. 2 shows the energy band in the n-AlGaInP cladding layer 5, the AIGaInP optical waveguide layer 6 and the p-AlGaInP cladding layer 7. A well structure of the energy band is formed in the optical waveguide layer 6. When OMVPE is used in the epitaxial growth, such a well structure is formed by temporarily increasing the supply rate of the organic In gas when the AlGaInP strained active layer 62 is formed. Accordingly, the electrons and holes injected from the n-electrode 3 and the p-electrode 11 are confined in the cell, that is, the AlGaInP strained active layer 62 and the light is emitted therein. A characteristic feature of the present example is that a lattice constant of the AlGaInP strained active layer 62 is larger than the lattice constant a of the n-GaAs substrate 2 by Δa. Specifically, Δa/a = 0.3 % to 1%. On the other hand, the lattice constant of the epitaxial layer other than the AlGaInP strained active layer 62 including the AlGaInP optical confinement layers 61 and 63 is substantially equal to that of the n-GaAs substrate 2. As a result, a compressive stress is always applied to the AlGaInP strained active layer 62. Accordingly, the oscillation threshold is lower than that of the unstrained condition. This is very effective to the visible light semiconductor laser which uses the AlGaInP active layer in which the continuous oscillation is very difficult to attain due to the rise of the oscillation threshold by the addition of Al. When a strain is applied by the difference between the lattice constants, a transition occurs unless the thickness of the layer to which the strain is applied is sufficiently small. A relation between the strain and the maximum film thickness (critical film thickness) to prevent the generation of misfit dislocations, for GaInP is reported in "5th OMVPE International Conference (1990)" and it is considered that the same is generally applicable to AIGaInP. In the example according to Figs. 1 and 2, the composition of the AlGaInP strained active layer 62 for (Al x Ga 1-x ) y In 1-y P is x = 0.26 and y = 0.43, the composition of the AlGaInP optical confinement layers 61 and 63 is x = 0.45 and y = 0.5, and the composition of the n-AlGaInp cladding layer 5 and the p-AlGaInP cladding layer 7 is x = 0.7 and y = 0.5. The deviation of the lattice constant of the AlGaInP mixed crystal semiconductor from that of the GaAs semiconductor is determined by y which is selected to be no greater than 0.45. As a result, the lattice constant of only the AlGaInP strained active layer 62 deviates from that of the n-GaAs substrate 2 in a preferred manner. The value x is selected in accordance with a desired oscillation wavelength. In the structure of the semiconductor laser of the present example, the transition does not occur when the thickness of the AlGaInP strained active layer 62 is 0.01 µm (100 Å). When the well is thin, it becomes a quantum well but the quantum effect is not so important in the present invention and the application of the strained is important. In general, when the active layer is too thin, the emitted light is vertically spread by a diffraction effect. In the structure of the present example, since the optical confinement layers 61 and 62 are provided and the optical waveguide layer 6 is sufficiently thick, the spread of the emitted light is suppressed. However, when the semiconductor layer of the present example was experimentarily operated, it was proved that not only the continuous oscillation was attained but also it exhibited a very unique characteristic. Namely, when the semiconductor laser of the present example was operated at -6°C, a current-photo-output characteristic showed an inversed S-shape as shown in Fig. 3A. Such a report has not been made heretofore and it is considered that it shows that a light emission process which is different from a usual one takes place in the strained active layer 62. The stripe width of the semiconductor laser used in the experiment is 5 µm and the wavelength of the emitted laser beam is approximately 0.62 µm. This phenomenon is not only novel but also useful to the industry. For example, when it is paired with a conventional laser having a characteristic shown in Fig. 3B, a total current-photo-output characteristic is one shown in Fig. 3C. In a region A shown therein, the photo-output is stable to the change of current. An example of a construction of such a laser light emitting apparatus is shown in Fig. 4. A laser chip 21 has an inverted S-shaped current-photo-output characteristic as shown in Fig. 3A. A laser chip 22 has a conventional current-photo-output characteristic as shown in Fig. 3B. Sizes of those chips 21 and 22 are approximately 300 µm x 300 µm, respectively, and they are arranged in pair with a spacing of approximately 100 µm. A Si photo-sensing device 23 is arranged in the apparatus. Those devices are connected to an external circuit through lead rods 24. In the present construction, the photo-outputs of the laser chips 21 and 22 are combined to produce a current-photo-output characteristic of the entire laser light emitting apparatus 25 as shown in Fig. 3C. Thus, a stable photo-output is attained in the region A. Fig. 5 shows a sectional view of a structure of a preferred embodiment of the present invention. The like elements to those shown in Fig. 1 are designated by the like numerals and the explanation thereof is omitted. In the preferred embodiment, an AlGaInP strained active layer 62 of an optical waveguide layer 6 is of multi-layer well structure in order to produce a high power from the laser. Namely, the AlGaInP optical waveguide layer 6 comprises AlGaInP optical confinement layers 61 and 63 and an AlGaInP strained active layer 62, and the AlGaInP strained active layer 62 is constructed three strained quantum wells. Fig. 6 shows an energy band diagram which more clearly shows the strained multi-quantum well structure. It shows the energy band of the AlGaInP strained active layer 62 as well as the AlGaInP optical confinement layers 61 and 63, the n-AlGaInP cladding layer 5 and the p-AlGaInP cladding layer 7. The composition of the well layers 65 and the barrier layers 66 is given by (Al x Ga 1-x ) y In 1-y P, x=0.2 and y=0.43 for the well layers 65, and x=0.2 and y=0.64 for the barrier layers 66. The composition y of the well layers 65 is selected to be no greater than 0.45 and the composition x is selected in accordance with the oscillation wavelength. The compositions of the AlGaInP optical confinement layer 61, the AlGaInP optical confinement layer 63, the n-AlGaInP cladding layer 5 and the p-AlGaInP cladding layer 7 are identical to those of the first embodiment. The thickness of the optical waveguide layer 6 is 0.3µm, and the thicknesses of the well layers 65 and the barrier layers 66 are 10 nm and 5 nm (100 Å and 50 Å) respectively. In general, in the multi-layer well structure, the larger the total thickness of the well is, the easier the misfit dislocations takes place even if the thickness of the individual well is less than the critical thickness. On the other hand, in the present embodiment, the lattice constant is selected such that a stress which is of opposite direction to that of the well layer 65, that is, a tensile stress is applied to the barrier layer 66. As a result, the stress of the entire AlGaInP strained active layer 62 is suppressed and no transition takes place. The lattice constant of the barrier layers 66 may be one which matches to that of the GaAs substrate 2. A tensile stress is also applied to the barrier layer 66 so that no misfit dislocation takes place. In the present embodiment, since the optical waveguide layer 6 is sufficiently thick, the spread of the emitted light is suppressed. The multi-layer well structure semiconductor laser of the present embodiment also exhibits the current-photo-output characteristic as shown in Fig. 3(a), and when it is paired with a semiconductor laser having a conventional current-photo-output characteristic, a laser light emitting apparatus which shows a stable current-photo-output characteristic is attained. The multi-layer well structure semiconductor laser of the present embodiment may be manufactured in the following manner. The semiconductor laser 31 uses the n-GaAs substrate 2 having the n-electrode 3 formed on the rear surface thereof, as it does in the example according to Figs. 1-4. On the upper surface of the n-GaAs substrate 2, the n-GaAs barrier layer 4, the n-AlGaInP cladding layer 5, the AlGaInP optical waveguide layer 6, the p-AlGaInP cladding layer 7 and the p-GaInP layer 9 are sequentially grown by OMVPE. After the epitaxial growth of those layers, portions of the p-GaInP layer 9 and the n-AlGaInP cladding layer 7 are etched away to form a mesa which extends normal to the plane of the drawing. The n-GaAs blocking layer 8 is grown in the etched-away regions to a height which is substantially equal to that of the p-GaInP layer 9 to bury the mesa which comprises the p-GaInP layer 9 and the p-AlGaInP cladding layer 7. The p-GaAs contact layer 10 and the p-electrode 11 are epitaxially grown thereon to complete the semiconductor laser 31. The laser beam is emitted from the optical waveguide layer 6 along the mesa, that is, normal to the plane of the drawing, when a forward bias is applied across the electrodes 3 and 11. The most characteristic feature of the present manufacturing method is the method for manufacturing the AlGaInP strained active layer 62. Basically, it is formed by OMVPE. As source gasses, trimethyl indium (TMI), triethyl gallium (TEG), trimethyl aluminum (TMA), arsine, phosphine, hydrogen selenide, and diethyl zinc are used. The gas pressure is 60 Torr. What is important is that the flow rate of only the TMI gas is changed as shown in Fig. 7 and the flow rates of other gasses are kept constant during the epitaxial growth. In Fig. 7, the abscissa represents a time (in second) and the ordinate represents the flow rate (in cc/min) of TMI. In regions A, C and E in Fig. 7, the TMI gas flow rate is set to 200 cc/min to form the well layer 65, and in regions B and D, the TMI gas flow rate is set to 65 cc/min to form the barrier layer 66. In this manner, the well layer 65 having x=0.2 and y=0.43 and the barrier layer 66 having x=0.2 and y=0.64 in the composition of (AlGa x-1 ) y In y-1 P were formed. The multi-layer structure thus formed exhibits an energy band of the multi-quantum well structure as shown in Fig. 6, and the lattice constant of the well layer 65 is larger than that of the n-GaAs substrate 2 so that the well layer 65 receives compressive stress. On the other hand, the lattice constant of the barrier layer 66 is smaller than that of the n-GaAs substrate 2 and the barrier layer 66 receives a tensile stress. The flow rates of the other gases are fixed and selected to grow a crystal which has a lattice-matching with the n-GaAs substrate 2 at a growth rate of 1.8 µm/min when the TMI gas flow rate is 140cc/min. Since the source flow rate of In is larger than those of Ga and Al, the control is relatively easy. Alternatively, the TMI gas flow rate may be set to 140 cc/min in the regions B and D so that the barrier layer 66 matches to the GaAs substrate 2. In this case, the barrier layer 66 receives a tensile stress. The time from the change of the TMI gas flow rate to the reflection to the change in the composition of the crystal varies from apparatus to apparatus. The required time may be preexamined. It is assumed 5 seconds herein. In order to make specific settings to the time, a timing of the flow rate change is varied to prepare a number of strained multi-quantum wells, an average lattice constant is determined by an X-ray diffraction, and a condition to match it to the n-GaAs substrate 2 is determined. In the present embodiment, OMVPE may be used to epitaxially grow the AlGaInP strained active layer 62 although molecular beam epitaxy may be used. In the latter case, two In injection cells may be prepared, and one of the In injection cells is always activated while the other In injection cells is controlled between activation and deactivation during the growth of the AlGaInP active layer 62. In this manner, the supply of In can be changed. As a result, the AlGaInP strained active layer 62 having the some strained multi-quantum well structure as that of the described embodiment is produced. While AlGaInP is used as the material for the strained active layer, GaInP may also be used. In this case, the strained multi-quantum well structure is produced by controlling the supply of In in the same manner. In general, when GaInP is used, the wavelength is longer than when AlGaInP is used. The invention thus described may be varied in many ways. Such variations are not to be regarded as a departure from the scope of the invention as defined by the following claims.

Claims: A semiconductor laser using a GaAs substrate (2) comprising: an optical waveguide layer (6) disposed between a pair of cladding layers (5,7), said waveguide layer (6) having an (Al x Ga 1-x ) y In 1-y P active layer (62) where x>0, and AlGaInP optical confinement layers (61, 63) holding said active layer (62) therebetween, wherein an energy band having a well structure is formed and a compressive stress is applied to said active layer (62) by the difference between the compositions of said active layer (62) and said optical confinement layers (61,63), wherein the value x is selected in accordance with a desired oscillation wavelength of equal to or shorter and the value y is selected such tat the lattice constant A of the active layer (62) and the lattice constant B of said GaAs substrate satisfy the relation: 0.003 <(A-B)/B < 0.01; and wherein said well structure is a multi-well structure (65,66) including well layers (65) and barrier layers (66), the barrier layers (66) isolating the well layers (65) and the lattice constants of the epitaxial layers other than the active layer (62) including the AlGaInP optical confinement layers (61, 63) and the cladding layers are substantially equal to that of the GaAs substrate and the active layer is thin to the extent that misfit dislocations are not generated. A semiconductor laser according to Claim 1, wherein said barrier layers receive a tensile stress. A semiconductor laser according to Claim 1 or 2 wherein for said active layer x is selected in accordance with a desired oscillation wavelength and y is no greater than 0.45. A semiconductor laser according to Claim 3 wherein the well layers (65) have a composition of (Al x Ga 1-x ) y In 1-y P), where x>0. A semiconductor laser according to Claim 3 or 4 wherein the lattice constant of the barrier layers (60) is selected such that a tensile stress opposing to the compressive stress applied to the well layers (65) is applied to the barrier layers (66). A semiconductor laser according to any of Claims 3 to 5 wherein the lattice constant of the barrier layers is selected to match to that of the GaAs substrate. A method of manufacturing a semiconductor laser according to any preceding claim having a multi-quantum well (Al x Ga 1-x ) y In 1-y P active layer (62) where x>0, comprising the step of: epitaxially growing the multi-quantum well structure by periodically changing the supply rate of only In. A method for manufacturing a semiconductor laser according to Claim 7 wherein the epitaxial growth is done by OMVPE, and the supply rate of In is periodically changed by periodically changing the flow rate of organic In source gas. A method for manufacturing a semiconductor laser according to Claim 8 wherein the organic In source gas is trimethyl indium.

Inventors: KATSUYAMA TSUKURU, YOSHIDA ICHIRO, KATSUYAMA, TSUKURU, YOSHIDA, ICHIRO, Katsuyama, Tsukuru, c/o Yokohama Works, Yoshida, Ichiro, c/o Yokohama Works
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LIMITED
Application year: 1991
Main classification: H01S5
IPC codes: H01S5, H01L33