Polymer melt distributor

Abstract: A horizontal polymer melt distributor comprises in combination a prism shaped distributor (10) with a cooperating horizontal tray (20) below the distributor. Polymer melt flows into and expands in the distributor then overflows onto the tray. This design holds the expanded polymer melt in the devolatilizer to reduce the content of monomer, dimers, trimers and residual oil in the polymer.

Description: The present invention relates to horizontal distributors which may be used in the upper end of a devolatilizer. The present invention also relates to a process for using such a distributor in the devolatilization of a polymer melt. In the manufacture of polymers by the bulk, or solution process it is generally required to significantly reduce the amount of residual monomer, and dimers, trimers and other oligomers and diluent, if present. This may be accomplished using a number of methods. For example the unfinished polymer may be passed through an extruder which has a section under vacuum. The polymer melt in the extruder is subject to working by the screw and a large surface area of melt is exposed to the vacuum. While the process is useful it subjects the polymer melt to shear which may cause polymer degradation. Additionally, it is usually carried out as a separate process step and may require additional manpower. In bulk or solution polymerization where the polymer is reacted in the form of a melt, the melt may be heated then passed through a preheater into a devolatilization chamber. The melt also undergoes some shear as it is typically pumped from the reactor to the preheater using a gear pump. However, the shear is lower than that in an extruder. Typically the preheater is on top of the devolatilizer and is a tube and shell type heat exchanger. The polymer flows through the tubes and descends to the bottom of the devolatilizer as continuous strands. Unfortunately, in this process there are competing factors which affect the devolatilization. The residual monomers, dimers, trimers, oligomers, and diluent, if present, will diffuse out of the melt faster at lower polymer melt viscosities. Unfortunately, at lower polymer melt viscosities, the polymer descends to the bottom of the devolatilizer faster and there is less time for the residual monomer, dimer, trimer, oligomers and diluent, if present, to diffuse out of the melt. One method of overcoming this problem is to use a series of devolatilizers in sequence, as disclosed in U.S. patent 4,294,652 issued October 13, 1981. While this approach may permit the polymer to be held in the form of a strand longer it represents an increase in capital cost, and maintenance costs. Another approach is to flow the polymer melt down the surface of a plate heat exchanger as disclosed in U.S. patent 4,153,501 issued May 8, 1979. The present invention does not contemplate such a vertical plate heat exchanger. A third approach is disclosed in applicant's EP-A-0 369 708 published on 23.05.90 (Article 54(3) EPC). The approach in that case is to use a horizontal polymer distributor which comprises a first enclosed section to permit polymer melt expansion and a second section to permit devolatilization and polymer melt strand formation. The apparatus disclosed in the EP-A-0 369 708 (Article 54(3) EPC) does not contemplate the use of a weir. Furthermore, the patent application does not contemplate the use of a horizontal distributor tray as required in the present patent application, European patent application specification EP-A-0 369 708 claims priority from U.S. patent application serial number 271,636. EP-A-0 369 708 describes and claims a process for devolatilizing a polymer melt, characterised by passing said polymer melt through a (e.g. horizontal) preheater and a horizontal distributor into a devolatilizer wherein the preheater is operated at temperatures and pressure conditions such that the vapour pressur of residual monomer, dimers, trimers, and diluents, if present, is greater than the pressure within the preheater and said polymer melt passes from said preheater into the upper end of said devolatilizer through a horizontal distributor means comprising: an inlet means and a die assembly adapted to cooperate with and receive polymer melt from a preheater, said die assembly comprising two oppositely facing flange plates connected about a central die plate said flange plates having essentially or substantially equisized central openings therethrough having an inward taper towards said die plate, said die plate having a number of holes therethrough connecting the central openings through said flange plates, the total cross sectional area of said holes being less than the minimum cross sectional area of the central openings through said flange plates, a heated enclosed first section having a cross sectional area greater than the minimum cross sectional area of said inlet, said first section opening into one or more subsequent at least partially heated venting and distributing sections which bear on their upwardly facing surface at least one aperture and on their downwardly facing surface strand forming holes permitting the exit of said polymer melt at a rate substantially equal to the rate polymer melt enters said distributor, the total cross sectional area of said one or more subsequent sections being at least equal the cross sectional area of said first section, said first and subsequent sections being adapted so that a substantially linial or linear flow of polymer melt is maintained throughout said distributor, e.g. with no stagnant areas. EP-A-0 369 708 also describes and claims a (e.g. horizontal polymer melt distributor adapted to be used in the upper end of a reduced pressure devolatilizer, said distributor comprising: an inlet means and a die assembly adapted to cooperate with and receive polymer melt from a preheater, said die assembly comprising two oppositely facing flange plates connected about a central die plate said flange plates having essentially or substantially equisized central openings therethrough having an inward taper towards said dies plate, said die plate bearing a number of holes therethrough connecting the central openings through said flange plates, the total cross sectional area of said holes being less than the minimum cross sectional area of the central openings through said flange plates, a heated enclosed first section having a cross sectional area greater than the minimum cross sectional area of said inlet, said first section opening into one or more subsequent at least partially heated venting and distributing sections which bear on their upwardly facing surface at least one aperture and on their downwardly facing surface strand forming holes permitting the exit of said polymer melt at a rate substantially equal to the rate polymer melt enters said distributor, the total cross sectional area of said one or more subsequent sections being at least equal the cross sectional area of said first section, said first and subsequent sections being adapted so that a substantially lineal or linear flow of polymer melt is maintained throughout said distributor, e.g. with no stagnant areas. Furthermore, EP-A-0 369 708 describes and claims a process for manufacturing a polystyrene, characterised by a polymer melt prepared in said process is devolatilized by utilising said devolatilizing process or by using a said polymer melt distributor. The present invention provides a novel horizontal distributor to be used in the upper end of a devolatilizer; and a process for its use. The polymer melts devolatilized using the distributor of the invention have a reduced content of residual monomer, dimer, trimer and oligomer and diluent, if present, relative to the use of a devolatiliser where such a horizontal distributor is not used. According to a first aspect of the present invention, there is provided a horizontal polymer melt distributor adapted to be used in the upper end of a reduced pressure devolatilizer, said distributor being characterised by comprising: (i) an inlet means (50) and a die assembly (60,70,80) adapted to cooperate with and receive polymer melt from a preheater, said die assembly comprising oppositely facing flange plates (70) connected about a central die plate (80), said flange plates having essentially equisized openings (90) therethrough and having an inward taper (90) towards said die plate, said die plate bearing a number of holes (100) therethrough connecting the central openings (90) through said flange plates, the total cross sectional area of said holes being less than the minimum cross sectional area of the central openings through said flange plates; (ii)a partially enclosed first section (10) having a cross sectional area greater than the minimum cross sectional area through said flange plates, said first section comprising a polyhedron (10), provided that one or more faces of said polyhedron provide a back wall (165) cooperating with one of said flange plates to provide an inlet for polymer melt into said polyhedron, one or more faces of said polyhedron provide an essentially planar base (120) which relative to said inlet faces downward and gently slopes forward, one or more faces of said polyhedron provide a weir (130) comprising relative to said base and said inlet one or more upwardly, outwardly facing surfaces and a plurality of holes through the base on the foot of the weir so that there are no areas of low flow in said polyhedron, said polyhedron having at least one or more upwardly facing openings (140) relative to said inlet; and (iii) spaced below but positioned to receive polymer melt overflow from said weir, an essentially horizontal tray (20) comprising a base (240) having a plurality of strand forming holes therethrough, a continuous lip extending around the perimeter. According to a second aspect of the present invention, there is provided a process of devolatilizing a polymer melt, characterised characterised by passing said polymer melt through a horizontal preheater and a horizontal distributor means into a devolatilizer wherein the preheater is operated at temperature and pressure conditions such that the vapour pressure of residual monomer, dimers, trimers and diluent, if present, is greater than the pressure within the preheater, and said polymer melt passes from said preheater into said devolatilizer through a horizontal distributor comprising: (i) an inlet means (50) and a die assembly (60,70,80) adapted to cooperate with and receive polymer melt from said preheater, said die assembly comprising oppositely facing flange plates (70) connected about a central die plate (80), said flange plates having essentially equisized openings (90) therethrough and having an inward taper (90) towards said die plate, said die plate bearing a number of holes (100) therethrough connecting the central openings (90) through said flange plates, the total cross sectional area of said holes being less than the minimum cross sectional area of the central openings through said flange plates; (ii) a partially enclosed first section (10) having a cross sectional area greater than the minimum cross sectional area through said flange plates, said first section comprising a polyhedron (10), provided that one or more faces of said polyhedron provide a back wall (165) cooperating with one of said flange plates to provide an inlet for polymer melt into said polyhedron, one or more faces of said polyhedron provide an essentially planar base (120) which relative to said inlet faces downward and gently slopes forward, one or more faces of said polyhedron provide a weir (130) comprising relative to said base and said inlet one or more upwardly, outwardly facing surfaces and a plurality of holes through the base on the foot of the weir so that there are no areas of low flow in said polyhedron, said polyhedron having at least one or more upwardly facing openings (140) relative to said inlet; and (iii)spaced below but positioned to receive polymer melt overflow from said weir, an essentially horizontal tray (20) comprising a base (240) having a plurality of strand forming holes therethrough, a continuous lip extending around the perimeter of said tray. In the first aspect of the present invention, the distributor may be characterised by said holes (100) through said die plate (80) being tapered or partially tapered in the direction of flow of polymer melt through said die plate. The distributor may be further characterised by said tray (20) being positioned so that the major portion of the surface is directly below said polyhedron (10). The distributor may be characterised by a deflector (190) comprising at least one vertical plate (220) spaced apart but in front of said weir (130) and descending to an edge on said tray (20). The distributor may be further characterised by said polyhedron having heating means (170) positioned within it at a height above said base (120) but less than the vertical height of said weir (130), e.g. said heating means may comprise a hot oil heater (170). The distributor may be characterised by having heating means (270) positioned above said base (120) but below the top of said lip of the tray (20), e.g. said heating means may comprise an immersion heater. The distributor may be further characterised by said polyhedron (10) comprises a prism having bases which are parallel and spaced about said inlet to said polyhedron, said bases forming an irregular heptagon defined by the following sequence of of joined edges: (i) a vertical back edge (wall 165); (ii) a downward forward extending edge (wall 400); (iii) a gently downward extending base (120); (iv) an upward forward extending front edge (160); (v) an upward inward extending edge (weir 130); (vi) a vertical edge (opening 140); and (vii) a horizontal top edge (top 150). In the second aspect of the present invention, the process may be characterised by said preheater is operated at any pressure in the range 1.6x10⁵ to 3.0x10⁵ Pa and at any temperature in the range 220 to 250°C. The process may be further characterised by said preheater is operated at any pressure in the range 2.3x10⁵ to 3.0x10⁵ Pa and at any temperature in the range 220 to 240°C. The process may be characterised by said devolatilizer is operated at any pressure in the range 6.65x10² to 33.25x10² Pa and at any temperature in the range 220 to 250°C. The process may be characterised by said polymer melt leaves said tray and descends to the bottom of said devolatilizer in the form of a plurality of continuous strands. In the prior art in the bulk polymerization of a polymer such as polystyrene a mixture of monomer and optionally diluent, such as ethyl benzene, is polymerized to a controlled conversion at a temperature of about 150°C. The material exiting from the reactor may contain up to 30% of monomer, oligomers, and diluent. The mixture leaving the reactor is passed through a preheater or heat echanger, usually a shell and tube tupe heat exchanger up to temperatures of a maximum of 255°C preferably up to 240°C most preferably about 230°C. A high pressure pump such as a gear pump is usually used to force the melt through the heat exchanger. The polymer melt then leaves the preheater and enters the devolatilization chamber. The devolatilization chamber may be operated at temperatures up to about 255°C, typically from 230 to 250°C, and at pressures from 1.33x10² to 66.50x10² Pa, preferably 6.65x10² to 33.25x10² Pa. As the hot melt flows from the preheater in strands into the devolatilization chamber, it foams and the volatile residual materials in the polymer melt are flashed off, The melt then descends to the bottom of the devolatilizer where it collects in a pool and is pumped to the next process stage. The preheater may be operated at temperature and pressure conditions so that the pressure within the preheater is less than the vapour pressure of the residual materials in the polymer melt, e.g. monomers, dimers, trimer, oligomers, and diluent. It is believed that the melt starts to effervesce or froth in the preheater with some of the residual materials forming a discontinuous vapour phase within the continuous polymer melt. These vapour phases (e.g. bubbles) are believed to be sites for further bubble formation or expansion. The pressure of the polymer melt within the preheater may be controlled by a pump and by the number and diameter of the holes in the die plate at the inlet to the devolatilizer. The pressure in the preheater may be controlled such that a substantial amount of residual monomer and diluent evaporate or form a vapour phase in the preheater. The polymer phase of the melt entering the devolatilizer through the die plate may have a dissolved volatile content of 2 to 10, preferably 3 to 7 percent. The pressure of the polymer melt in the preheater may be from 1.6x10⁵ to 3.0x10⁵Pa, preferably 2.3x10⁵ to 3.0x10⁵ Pa, most preferably about 2.6x10⁵ to 2.9x10⁵ Pa, at temperatures up to 255°C, preferably from 220 to 240°C. Care must be taken that the polymer melt is not exposed to too high a temperature for excessive time or degradation and/or oligomerization may tend to occur, The polymer melt may flow from the preheater into a horizontal distribution means at the upper end of the devolatilization chamber. The distributor may comprise a horizontal Inlet from the preheater to receive polymer melt. The first section may be partially enclosed and may have a cross sectional area greater than the minimum cross section area of inlet which permits the polymer melt to expand and foam. The first section may have a cross section area greater than the minimum cross section areas of the inlet (e.g.- the cross section area of holes through, the die plate). The expansion of the polymer melt is due to the reduced pressure within the devolatilizer relative to the pressure in the preheater. The polymer melt expansion provides a larger surface area to permit residual material to volatilize into and also from the foam structure into the devolatilization chamber. The second stage of the distributor may comprise one or more subsequent trays with a series of hold there through. In accordance with a preferred aspect of the present invention either or both of the first section or the tray may be heated. If the heaters are present they are generally used during startup or shut down of the process to ensure that polymer does not stick to the distributor. Without being bound by theory it is believed that the principle of operation is as follows. The pressure of the melt drops gradually in the preheater until the volatile materials start to effervesce or boil. The pressure drop across the die plate is such that the polymer melt leaves the die plate containing 2 to 10, preferably 3 to 7 percent volatiles. The vapours formed in the preheater disengage from the melt, as the melt and entrained vapour crosses the die plate. The remaining volatile materials in the melt start to boil forming foam, which enhances further devolatilization through the increased surface area of the melt. As the foam flows through the first section of the devolatilizer the vapour disengages from the foamed polymer melt and escapes through the openings or apertures in the first section. The melt then flows over the weir and is deposited on the tray. The melt flows across the tray and through strand forming holes in the tray to descend as strands to the bottom of the devolatilizer. The final stage of devolatilization take place from the polymer melt strands and pool in the bottom of the devolatilizer. If the pressure in the preheater is too low, too much of the volatile material in the melt will form the vapour phase. There will not be sufficient volatile material in the polymer melt to froth the melt sufficiently for efficient devolatilization. If the pressure in the preheater is too high, too much volatile material will be in the polymer melt phase. This is detrimental in two ways. First, the dwell time of the polymer melt in the devolatilizer may not be sufficiently long for adequate devolatilization. Secondly, as the volatiles evaporate, they will extract heat from the melt lowering its temperature reducing the diffusion coefficient and increasing the viscosity of the polymer melt. The lower diffusion coefficient retards the devolatilization process while the higher viscosity retards the separation of the vapour bubbles from the melt. If the vapour bubbles do not separate from the melt they may be compressed and condensed by the melt pump at the bottom of the devolatilizer and will raise the concentration of residual volatile material in the finished polymer. In the first section the bubbles within the foamed polymer melt will tend to burst open permitting the volatile residual materials to be drawn off through the devolatilization chamber. The opening or apertures in the first section may face upward and outward relative to the inlet. It goes without saying that the aperture openings are above the weir. The apertures permit the devolatilization of the bubbles of volatile materials from the melt and from the surface of the melt. Preferably, in operation the bottom of the polyhedron is essentially planar with a slight or gentle downward and forward slope relative to the inlet. The polymer melt entering the first section forms a froth which flows forward until it reaches the weir. The level of the froth must rise until the froth flows over the weir. To prevent polymer burning or degrading there are a series of drain holes at the juncture of the weir and the bottom of the polyhedron. This reduces the "dead spots" or areas where there is no or very low flow in the first section. This reduces likelihood of polymer char and the resulting "black speck" formation. Preferably, in front of the weir is a deflector or shield. The deflector plate prevents splatter on the wall of the vessel. This reduces formation of black specks. The deflector may be an essentially planar vertical plate, or an essentially "U" shaped vertical plate. The froth flows over the weir or through the drain holes and is deposited on the upper surface of a tray which has a plurality of strand forming holes in it through which the polymer melt flows and descends as strands to the bottom of the devolatilizer. The selection of hole size and location to produce strands is known to those skilled in the art. Typically the size of holes in the tray will range from about 0.5 inches (1 cm) to about 1.5 inches (about 3.7 cm) most preferably from 0.75 inches (about 1.8 cm) to 1.25 inches (about 3.0 cm). The first section may be heated. A hot oil or electric resistance heater is preferred but other heating means may be suitable. The tray may also be heated. If the tray is heated the heating means should be placed in the tray so that the top of the heater is below the top of the walls of the tray. Preferably the heater will be spaced above the bottom of the first section on spacer bars or ridges. Similarly if the first section is heated the heater will be below the top edge of the weir. The temperature of the distributor may be up to 250, preferably from 230 to 250°C, most preferably from 240 to 250°C. The first section may be of a shape so that there is essentially linear flow within the distributor. The distributor must provide a suitable residence time and fit within the devolatilizer. The temperature, pressure and polymer residence time in the devolatilizer will control the degree of devolatilization of the polymer. Under typical pressures and temperatures in a devolatilizer the residence time in the distributor may be up to about 10 minutes, preferably from about 3 to 8 minutes, most preferably about 5 minutes. Preferably, sharp elbows or joints in the distributor where there would be low polymer flow rates are avoided. A die plate may be provided to serves to maintain the pressure drop from the preheater to the distributor in the devolatilizer. This permits the preheater to be maintained at pressures of 160 to 300 kPa (10 to 30 psig) while the devolatilizer is maintained at pressures as low as 1.3, preferably 6.7 to 33.3 hPa (1, preferably 5 to 25 mm of Hg). The total cross section area of the holes in the die plate should be less than the cross section area of the first section. Preferably the ratio of cross section area of the holes through the die plate to the cross section area of the first section is in the range of 1:5 to 1:10. Preferably the holes are tapered or at least partially tapered reducing in size in the direction of flow of the polymer melt. The die may be mounted at the distributor inlet between a pair of equisized flange plates having central openings therethrough having an inward taper towards the die plate. The apparatus aspect of the present invention will be illustrated by way of example in the accompanying drawings, in which one example of the distributor is in the shape of a candy scoop or dust pan and like parts have like numbers. In the drawings, which are by way of example: Figure 1 is a plan view of one example of a distributor according to the present invention. Figures 2A and 2B are sectional and a front view of the flanges, respectively. Figures 3A and 3B are sectional and a front view of the die plate respectively. Referring to figure 1 it can be seen that the first section 10 and the tray 20 are supported horizontally within the upper end of the devolatilization chamber 30 by support rods 40. A polymer melt inlet 50 passes through the sidewall of devolatilization chamber 30 and is connected to the distributor through die assembly 60. The die assembly 60 comprises a pair of flange plates 70 with a die plate 80 disposed there between. Figures 2A and 2B a sectional and a back view of the flanges respectively, show the flange plates each have an inwardly tapered opening 90 therethrough (e.g. they narrow toward the face of the flange or the die plate). Figures 3A and 3B are a sectional and a front view of the die plate and show that the die plate 80 has a plurality of tapered holes 100 therethrough. The die plate 80 is placed between the flanges so that the holes are tapered in the direction of flow of polymer melt into the distributor. The number and diameter of holes are selected to maintain the pressure on the polymer melt within the preheater and to control the flow of the polymer melt into the distributor. The first section 10 comprises a polyhedron. In the embodiment shown in figure 1 the polyhedron is a prism. That is it has two parallel bases (in this case sides) 110. The bases 110 are equispaced about inlet 50. The polyhedron need not be a prism, for example it could be partially dome shaped. It is, however, necessary that the first section have an essentially planar base 120 which slopes gently, at an angle of not more than about 10° preferably less than 5° below horizontal, toward the front (or away from inlet 50) of the first section. At the front of the first section is a weir 130. In the illustrated embodiment of the present invention the vertical height of the weir 130 is below the bottom of inlet 50. While it is not essential that the weir have a vertical height below the bottom of the inlet, it reduces "dead spots" in the flow of polymer melt in the first section. Additionally, if the weir is relatively low it reduces the volume of polymer melt in the first stage, contributing to a proportionally large exposed surface to the devolatilizer, of polymer melt in the first section. If, however, the weir is too low the polymer melt will flow out of the first section too rapidly and the melt will not have sufficient dwell time in the devolatilizer. On the upper surface of the first section are one or more openings, 140 to permit the escape of volatiles from the melt into the devolatilizer. In the embodiment illustrated, there is also a top 150, to the first section, a back wall 165, and a sharp downward sloping intermediate wall 400 joining the back wall to the base. Inside the first section there are a series of supports 160 which support heating elements 170. The heating elements in this case are hot oil heating tubes, but they could also be electrical heaters or other suitable immersion heaters. The heaters are positioned in the first section at a height below the top edge of the weir 130. In figure 1 the oil input line is partially shown at 180. The heater provides heat to the frothed polymer melt to reduce the heat loss due to evaporation of monomer, dimer, trimer oligomers, and diluent, if present. In front of the opening 140 in the front of the polyhedron there is a deflector 190. The deflector 190 comprises a top plate 200, a back plate 210, two side plates 220, and a sloping bottom plate 230. The top plate 200 also serves as a hanger for the deflector from the polyhedron. The deflector forms a "U" shaped cup or plate in front of the opening 140 in the polyhedron. The deflector could also be an essentially planar vertical plate. The deflector prevents splatter of the foamed polymer melt from the first section to the sides of the devolatilizer 30. Additionally the deflector cooperates with tray 20 below the first section to ensure that polymer froth does not fall outside the tray 20. Thus, tray 20 fits inside the two side plates 220 and above and in cooperating arrangement with sloping base plate 230. The tray 20 comprises a base 240, two side walls 250, a back wall 260, and a front wall (not shown) which cooperates with the deflector. Inside the tray, at a height below the height of the walls of the tray is a suitable immersion heater 270 of the type discussed above. In this particular embodiment the hot oil from the heater in the first section 170 is conveyed to the heater in the second section by a pipe 280. The outlet or return for the hot oil is partially shown at 290. The heating elements rest on a series of spacers 300 and are spaced above the bottom 240 of the tray and below the top of the walls of the tray. There are a series of strand forming holes through the bottom of the tray so the polymer melt will form strands as it descends to the bottom of the devolatilizer. It should be noted that the polymer melt will also continue to devolatilize in the tray prior to forming strands. The distributor of the present invention may provide a dwell or residence time in the distributor of up to 10 minutes, preferably from about 3 to 8 minutes, most preferably about 5 minutes. The distributor of the present invention has been described in association with the devolatilization of polystyrene. The devolatilizer may be used in association with any polymer which is or may be devolatilized using a low pressure devolatilizer. The present invention will be illustrated by the following example, in which parts are parts of weight (e.g. lb.). The example is intended to illustrate and not to limit the invention. Example 1 A distributor in the shape of a "candy scoop" was installed in a polystyrene plant which used a perforated pipe type horizontal distributor, in a falling strand devolatilizer. The average total residuals, styrene monomer residuals and ethyl benzene residuals were measured for the polymer devolatilized using the perforated pipe distributor and the "candy scoop" distributor of the present invention. The results are set forth in Table 1. Distributor Perforated Pipe "Candy Scoop" Average Total Residuals 1100 500 Average Styrene 925 300 Average Ethylbenzene 175 20 The "candy scoop" distributor of the present invention is significantly more efficient in the reduction of monomers, oligomers and diluent, then the conventional prior art pipe distributor.

Claims: A horizontal polymer melt distributor adapted to be used in the upper end of a reduced pressure devolatilizer, said distributor being characterised by comprising: (i) an inlet means (50) and a die assembly (60,70,80) adapted to cooperate with and receive polymer melt from a preheater, said die assembly comprising oppositely facing flange plates (70) connected about a central die plate (80), said flange plates having essentially equisized openings (90) therethrough and having an inward taper (90) towards said die plate, said die plate bearing a number of holes (100) therethrough connecting the central openings (90) through said flange plates, the total cross sectional area of said holes being less than the minimum cross sectional area of the central openings through said flange plates; (ii)a partially enclosed first section (10) having a cross sectional area greater than the minimum cross sectional area through said flange plates, said first section comprising a polyhedron (10), provided that one or more faces of said polyhedron provide a back wall (165) cooperating with one of said flange plates to provide an inlet for polymer melt into said polyhedron, one or more faces of said polyhedron provide an essentially planar base (120) which relative to said inlet faces downward and gently slopes forward, one or more faces of said polyhedron provide a weir (130) comprising relative to said base and said inlet one or more upwardly, outwardly facing surfaces and a plurality of holes through the base on the foot of the weir so that there are no areas of low flow in said polyhedron, said polyhedron having at least one or more upwardly facing openings (140) relative to said inlet; and (iii)spaced below but positioned to receive polymer melt overflow from said weir, an essentially horizontal tray (20) comprising a base (240) having a plurality of strand forming holes therethrough, a continuous lip extending around the perimeter. A distributor according to claim 1, characterised by said holes (100) through said die plate (80) are tapered or partially tapered in the direction of flow of polymer melt through said die plate. A distributor according to claim 2, characterised by said tray (20) is positioned so that the major portion of the surface is directly below said polyhedron (10). A distributor according to claim 3, characterised by a deflector (190) comprising at least one vertical plate (220) spaced apart but in front of said weir (130) and descending to an edge on said tray (20). A distributor according to any one of claims 1 to 4, characterised by said polyhedron having heating means (170) positioned within it at a height above said base (120) but less than the vertical height of said weir (130). A distributor according to claim 5, characterised by said heating means (170) comprises a hot oil heater (170). A distributor according to any one of claims 1 to 4, characterised by having heating means (270) positioned above said base (120) but below the top of said lip of the tray (20). A distributor according to claim 7, characterised by said heating means (270) comprises an immersion heater (270). A distributor according to any one of claims 1 to 8, characterised by said polyhedron (10) comprises a prism having bases which are parallel and spaced about said inlet to said polyhedron, said bases forming an irregular heptagon defined by the following sequence of joined edges: (i) a vertical back edge (wall 165); (ii) a downward forward extending edge (wall 400); (iii) a gently downward extending base (120); (iv) an upward forward extending front edge (160); (v) an upward inward extending edge (weir 130); (vi) a vertical edge (opening 140); and (vii) a horizontal top edge (top 150). A process of devolatilizing a polymer melt, characterised by passing said polymer melt through a horizontal preheater and a horizontal distributor means into a devolatilizer wherein the preheater is operated at temperature and pressure conditions such that the vapour pressure of residual monomer, dimers, trimers and diluent, if present, is greater than the pressure within the preheater, and said polymer melt passes from said preheater into said devolatilizer through a horizontal distributor comprising: (i) an inlet means (50) and a die assembly (60,70,80) adapted to cooperate with and receive polymer melt from said preheater, said die assembly comprising oppositely facing flange plates (70) connected about a central die plate (80), said flange plates having essentially equisized openings (90) therethrough and having an inward taper (90) towards said die plate, said die plate bearing a number of holes (100) therethrough connecting the central openings (90) through said flange plates, the total cross sectional area of said holes being less than the minimum cross sectional area of the central openings through said flange plates; (ii) a partially enclosed first section (10) having a cross sectional area greater than the minimum cross sectional area through said flange plates, said first section comprising a polyhedron (10), provided that one or more faces of said polyhedron provide a back wall (165) cooperating with one of said flange plates to provide an inlet for polymer melt into said polyhedron, one or more faces of said polyhedron provide an essentially planar base (120) which relative to said inlet faces downward and gently slopes forward, one or more faces of said polyhedron provide a weir (130) comprising relative to said base and said inlet one or more upwardly, outwardly facing surfaces and a plurality of holes through the base on the foot of the weir so that there are no areas of low flow in said polyhedron, said polyhedron having at least one or more upwardly facing openings (140) relative to said inlet; and (iii)spaced below but positioned to receive polymer melt overflow from said weir, an essentially horizontal tray (20) comprising a base (240) having a plurality of strand forming holes therethrough, a continuous lip extending around the perimeter of said tray. A process according to claim 10, characterised by said preheater is operated at any pressure in the range 1.6x10⁵ to 3.0x10⁵ Pa and at any temperature in the range 220 to 250°C. A process according to claim 11, characterised by said preheater is operated at any pressure in the range 2.3x10⁵ to 3.0x10⁵ Pa and at any temperature in the range 220 to 240°C. A process according to claim 12, characterised by said devolatilizer is operated at any pressure in the range 6.65x10² to 33.25x10² Pa and at any temperature in the range 220 to 250°C. A process according to claim 12, characterised by said polymer melt leaves said tray and descends to the bottom of said devolatilizer in the form of a plurality of continuous strands.

Inventors: ABOUL-NASR OSMAN TEWFIK, ABOUL-NASR, OSMAN TEWFIK
Applicants: NOVACOR CHEM INT, NOVACOR CHEMICALS (INTERNATIONAL) S.A.
Application year: 1991
Main classification: C08F6
IPC codes: C08F6, B01D3, B01D19