Method of producing flexible printed-circuit board covered with cover layer

Abstract: A flexible printed-circuit board covered with a cover layer is produced by bonding (a) a flexible printed-circuit board that comprises a flexible base having a surface bearing a circuit and (b) a polyimide film having a surface treated to increase adhering property and another surface not treated to increase adhering property, each of the surfaces being coated with an adhesive layer, with the adhesive layer on the surface treated to increase adhering property interposed between the polyimide film and the surface bearing the circuit, and then peeling off the adhesive layer coating the polyimide film on the surface not treated to increase adhering property.

Description: BACKGROUND OF THE INVENTION (a) Field of the Invention The present invention relates to a method of producing a flexible printed-circuit board covered with a cover layer, wherein a covering film prevented effectively from curling is used so that it and the flexible printed-circuit board can be located together easily, and the applied cover lay is excellent in heat resistance, flexibility and dimensional stability. (b) Description of the Related Art Cover layer films are for protecting circuits made on flexible printed-circuit boards, and, generally, they are prepared by coating one surface of a base film, such as a polyimide film, with an adhesive, such as an acrylic adhesive or an epoxy adhesive, and are applied to a flexible printed-circuit board by bonding the surface coated with the adhesive to a surface of the flexible printed-circuit board bearing a circuit using heat and pressure. For the purpose of producing flexible printed-circuit boards of improved high efficiency, the use of conventional copper-clad laminates having a three-layer structure of copper foil/epoxy or acrylic adhesive/polyimide film has recently become replaced by the use of those having a two-layer structure of copper foil/polyimide film. However, using the above-described conventional cover layer films has ruined the advantages of copper-clad laminates of two-layer structure, since, after covering with the cover layer, the properties of the flexible printed-circuit boards, including heat resistance, are dominated by the acrylic or epoxy adhesives used for bonding the cover layer films. In order to overcome such a problem, the use of polyimide adhesives was proposed as disclosed in Japanese Patent Application Kokai Koho (Laid-open) No. 3-205474. According to this document, which corresponds to EP-A-0 389 951, the surface of the film bonded to the circuit is plasma treated to improve adherence. However, the use of polyimide adhesives in preparation of cover layer films for flexible printed-circuit boards also encountered a problem that the cover layer films curled when dried after coating, thereby interfering with proper location of them and flexible printed-circuit boards. The causes for the problem include the following (1) and (2). (1) Polyimide adhesives contract severely when dried after application thereof on a base film, since polyimides for adhesives are generally poor in the solubility in solvents as compared with acrylic or epoxy compounds for adhesives so that a large amount of solvents is required for the preparation of polyimide adhesives, with the concentration of the polyimide adhesive components in the polyimide adhesives lowered. (2) In production of two-layer flexible printed-circuit boards, for the purpose of preventing curling thereof, polyimides of low thermal expansion are generally used as base materials in order to make the circuit and the polyimide base similar in linear thermal expansion coefficient. While low thermal expansion is also required of the base films of cover lays, cover lay films themselves are apt to curl due to the difference in linear thermal expansion between the base film and adhesive layer thereof since polyimides for adhesives do not have low thermal expansion. SUMMARY OF THE INVENTION An object of the present invention is to provide a method of producing a flexible printed-circuit board covered with a cover lay, wherein a polyimide adhesive is used as the adhesive of a cover lay film, and the cover lay film is excellent in heat resistance and is prevented effectively from curling. As the results of the inventors' research for preventing cover lay films for flexible printed-circuit boards from curling due to the use of polyimide adhesives, they found that such curling of cover lay films could be prevented by using the generally poor adherence between polyimide/polyimide and by coating both surfaces of a base film with an adhesive to form a sandwich, only one of the surfaces that is to be bonded to the conductor-circuit-bearing surface of a flexible printed-circuit board being treated to improve adhering property prior to the application of the adhesive. The adhesive applied to the other surface that is not treated to improve adhesive property or is subjected to a release treatment prior to the application is peeled off from the base film after the cover lay film is bonded to the flexible printed-circuit board by heating and pressing the sandwich. That is, the present invention provides a method of producing a flexible printed-circuit board covered with a cover lay comprising: assembling (a) a flexible printed-circuit board that comprises a flexible base having a surface bearing a circuit; and (b) a polyimide film having a surface treated to increase adhering property and another surface not treated to increase adhering property, each of the surfaces being coated with an adhesive layer by applying a polyimide adhesive to each of the surface and drying the applied polyimide adhesive by heating, thereby forming on the surface an adhesive layer 1.0 to 1.5 times as thick as the circuit, the polyimide adhesive comprising a compound selected from the group consisting of a polyimide and a polyimide precursor said compound being optionally dissolved in a solvent ; to form a composite wherein the adhesive layer coating the surface treated to increase adhering property is interposed between the polyimide film and the surface bearing the circuit; subjecting the composite to heat and pressure to bond the composite into a laminate structure; and peeling off the adhesive layer coating the polyimide film on the surface not treated to increase adhering property from the laminate structure. DESCRIPTION OF THE PREFERRED EMBODIMENT In the present invention, from the view point of high heat resistance, good flexibility and excellent dimensional stability, a polyimide film is used as a base film for a cover lay film. For the purpose of preventing the produced flexible printed-circuit board covered with a cover lay from curling, it is preferable to use a polyimide film of low thermal expansion which has a similar linear thermal expansion coefficient to that of the circuit materials. Preferred polyimide film has a linear thermal expansion coefficient of not larger than 2.5× 10 -5 deg -1 at a temperature of 50 to 250 °C. Typical examples of the preferred polyimide film include UPILEX-S (produced by Ube Industries, Ltd.), UPILEX-SGA (produced by Ube Industries, Ltd.), APIKAL-NPI (produced by Kanegafuchi Chemical Industry Co., Ltd.), and NOVAX (produced by Mitsubishi Chemical Industries Ltd.). One surface of the polyimide film is treated to improve adhering property. Some examples of the treatment for improving adhering property include a mechanical treatment, such as brushing and sandblasting, and a chemical treatment, such as an alkali treatment, a corona treatment and a plasma treatment. Plasma treatments are preferable because of their high efficiency in improving the adhering property. The plasma treatment may be carried out either continuously or batchwise. From the view point of efficiency, a continuous process is desirable. Some examples of the gas to be used for the plasma treatment include oxygen, nitrogen, helium, argon or CF 4 . These gases may be used individually or as a mixture of two or more kinds of gases. The pressure of the plasma treatment is preferably from 0.08 to 0.15 torr, and the plasma power density (throwing electric power/area of electrode) is preferably from 0.2 to 100 W/cm 2 , more preferably from 0.5 to 50 W/cm 2 . The period of the plasma treatment is preferably from 10 seconds to 30 minutes or more, and it depends on other conditions. The reverse of the surface treated to improve adhering property is not treated to improve adhering property or is subjected to a release treatment. The release treatment is generally performed by application of a release agent, such as a silicone release agent and a non-silicone release agent. Some typical examples of the non-silicone release agent include a polyethylene wax, a polyvinyl carbamate and a polyethylimine/alkyl glycidyl ether. Both surfaces of the polyimide film treated as described above are coated with a polyimide adhesive, and the applied polyimide adhesive is dried to form two adhesive layers coating the surfaces of the polyimide film. In an embodiment, first a polyimide adhesive is applied to the surface that was not treated to improve or was subjected to a release treatment, and is then dried to coat the surface with an adhesive layer. Subsequently, the same polyimide adhesive is applied to the reverse of the surface coated with the adhesive layer, namely the surface treated to improve adhering property, and is then dried to form another adhesive layer coating the surface treated to improve adhering property. The drying is conducted preferably by employing a full-float system so as to prevent contact between the applied polyimide adhesive and conveyer devices, etc. in a drying furnace. It is necessary to adjust the thickness of the applied polyimide adhesive so that, after drying, the adhesive layers are 1.0 to 1.5 times as thick as the circuit. If the thickness of the adhesive layers are smaller than that of the circuit, it will be difficult to bury the circuit completely in the adhesive layer during bonding by heating and pressing. If it is more than 1.5 times as thick as the circuit, reduction of residual volatile matter in the adhesive layers after drying will be difficult, and the cost will be increased. It is preferable to reduce the quantity of the residual volatile matter remaining in the adhesive layers after drying to not more than 1.5 % by weight of the adhesive layers, more preferably not more than 1 % by weight. A large quantity of residual volatile matter is undesirable because it causes void or peeling in the interface between the coverlay polyimide film and the flexible printed-circuit board at the time of bonding to the flexible printed-circuit board or solder-reflowing on the coverlaid flexible printed-circuit board. The polyimide adhesive used in the present invention comprises a compound selected from the group consisting of a polyimide and a polyimide precursor, each of the group members being generally dissolved in a solvent. The preferred examples of the polyimide precursor include a polyamic acid and a bis-maleimide compound. The preferred polyimide adhesive comprises a polyamic acid comprising a repeating unit represented by the following formula (1) wherein R 1 is or or each R 3 , respectively, being hydrogen, a halogen or an alkyl group of from 1 to 4 carbon atoms and each X and Y, respectively, being -O- , -SO 2 - , or -S-, each R 4 , respectively, being hydrogen, an alkyl group of from 1 to 4 carbon atoms or -CF 3 , R 2 is The preferred polyimide is an imidation product of a polyamic acid having the repeating unit represented by the formula (1). It is preferable to use a polyimide adhesive comprising the polyimide and a bis-maleimide compound dissolved in a solvent or a polyimide adhesive comprising the polyamic acid and a bis-maleimide compound dissolved in a solvent. The latter is more preferable. The polyamic acid having the repeating unit represented by the formula (1) is a reaction product of an aromatic diamine represented by the formula: H 2 N-R 1 -NH 2 or a derivative thereof and a tetracarboxylic acid represented by the formula: R 2 (COOH) 4 or a derivative thereof. Some examples of the aromatic diamine include 1,3-bis(3-aminophenoxy)benzene, 1,3-bis(4-aminophenoxy)benzene, 1,4-bis(4-aminophenoxy)benzene, 4,4' -bis(4-aminophenoxy)biphenyl, bis[4-(3-aminophenoxy)phenyl]sulfone, bis[4-(4-aminophenoxy)phenyl]sulfone, 2,2-bis[4-(4-aminophenoxy)phenyl]propane, 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(3-aminophenoxy)phenyl]propane and 2,2-bis[4-(3-aminophenoxy)phenyl]hexafluoropropane. Diisocyanates thereof also may be used. The aromatic diamine or derivative thereof, which provides -R 1 - group, affects largely the glass transition temperature of the produced polyamic acid and polyimide. In order to lower the temperature required for bonding by heating and pressing, it is important that the polyamic acid has a molecular design so that imidation of the polyamic acid provides a polyimide having a low glass transition temperature, and it is preferable to use an aromatic diamine or a derivative thereof containing three or more benzene rings, more preferably, further containing one or more m- bonds. Monocyclic aromatic diamines, such as ophenylenediamine, m-phenylenediamine, p-phenylenediamine, 2,4-diaminotoluene, 2,5-diaminotoluene, 2,4-diaminoxylene and diaminodurene, and bicyclic aromatic diamines, such as benzidine, 4,4' -diaminodiphenylmethane, 4,4' - diaminodiphenyl ether, 3,4' -diaminodiphenyl ether, 4.4' - diaminodiphenyl sulfone and 3,3' -diaminodiphenyl sulfone, may also be used. Some examples of the tetracarboxylic acid containing =R 2 = group include pyromellitic acid, 2,3,3' ,4' -tetracarboxydiphenyl, 3,3' ,4,4' -tetracarboxydiphenyl, 3,3' ,4,4' -tetracarboxydiphenyl ether, 2,3,3' ,4' -tetracarboxydiphenyl ether, 3,3' ,4,4' -tetracarboxybenzophenone and 2,3,3' ,3' -tetracarboxybenzophenone. Derivatives of the tetracarboxylic acid also may be used, and some examples of derivatives include an ester, an anhydride and an acid chloride thereof. These polyamic acids may be used individually or as a blend of two or more of them dissolved in a solvent, and those obtained by copolymerization may also be used. The use of a polyamic acid modified by blending or copolymerization is rather preferable for the purpose of adjusting the glass transition temperature of polyimides derived from polyamic acids at the time of drying. The more preferable polyimide adhesive comprises both the polyamic acid and a bis-maleimide compound in a state dissolved in a solvent. While the polyimide adhesive is being dried by heating to form an adhesive layer on both the surfaces of a polyimide film, the polyamic acid in the polyimide adhesive is imidized by the heating. In preparation of such a polyimide adhesive, it is therefore important for the control of glass transition temperature of the polyimide resulting from the imidation of the polyamic acid to design the molecular structure of the polyamic acid in consideration of the temperature for thermosetting of the bis-maleimide compound and the temperature for bonding to a flexible printed-circuit board. In the case of a polyimide adhesive containing both a polyamic acid and a bis-maleimide compound, the glass transition temperature of the adhesive layer after drying and imidation of the polyamic acid is lower than that of an adhesive layer containing no bis-maleimide compound. However, if the glass transition temperature is nonetheless extremely higher than the temperature for thermosetting of the bis-maleimide compound used, the bis-maleimide compound will be crosslinked in the course of the imidation of the polyamic acid so as to make the bonding with a flexible printed-circuit board by heating and pressing difficult. Further, the higher the glass transition temperature, the higher the temperature required to bond to a flexible printed-circuit board by heating and pressing. In view of these points, it is desirable that the polyimide derived from the polyamic acid has a glass transition temperature not higher than 260 °C. Among the polyamic acids having the repeating units represented by the formula (1), the preferred polyamic acid are those having the repeating units represented by the following formula (2) wherein each R 3 , respectively, is hydrogen, a halogen or an alkyl group of from 1 to 4 carbon atoms, and each R 4 , respectively, is hydrogen, an alkyl group of from 1 to 4 carbon atoms or -CF 3 . The preparation of the polyamic acid is carried out by reacting equimolar quantities of the above-described aromatic diamine or a reactive derivative thereof and the above-described tetracarboxylic acid or a reactive derivative thereof in a solvent, such as N-methylpyrrolidone (NMP), N,N-dimethylformamide (DMF), N,N-dimethylacetamide (DMAc), dimethylsulfoxide (DMSO), phenol, a halogenated phenol, 1,4-dioxane, γ -butyrolactone, tetrahydrofuran and diethylene glycol dimethyl ether, at a temperature ranging from 0 to 150 °C. These solvents may be used individually or as a mixture of two or more of them. Selection of the solvents to be used is also important. It is undesirable to use a solvent the removal of which, at the time of drying of the applied polyimide adhesive, requires an extremely higher temperature than the temperature for thermosetting of the bis-maleimide compound, because the use of such a solvent causes crosslinking of the bis-maleimide compound prior to bonding by heating and pressing and makes adhesion to a flexible printed-circuit board difficult. The bis-maleimide compound which may be used in the present invention is represented by the following formula: Typical examples of the bis-maleimide compound include N,N' -m-phenylene-bis-maleimide, N,N' -p-phenylene-bis-maleimide, N,N' -(oxy-di-p-phenylene)bis-maleimide, N,N' -(methylene-di-p-phenylene)bis-maleimide, N'N' -(sulfonyl-di-p-phenylene)bis-maleimide and 2,2-bis(maleimide-phenoxyphenyl)propane, but the bis-maleimide compounds which may be used in the present invention are not limited to these examples. The quantity of the bis-maleimide compound used is not particularly limited, but the preferred quantity is 10 to 100 parts by weight, more preferably 20 to 60 parts by weight, per 100 parts by weight of the polyamic acid used. The cover lay film thus obtained, namely a polyimide film that has a surface treated to increase adhering property and another surface not treated to increase adhering property and is coated on each surface with an adhesive layer, and a flexible printed-circuit board that comprises a flexible base having a surface bearing a circuit are assembled to form a composite wherein the adhesive layer coating the surface treated to increase adhering property is interposed between the polyimide film and the surface bearing the circuit. The composite is then subjected to heat and pressure to bond the composite into a laminate structure. The bonding is generally carried out at a temperature not lower than the glass transition temperature of the polyimide or the mixture of a polyimide and a bis-maleimide compound in the adhesive layer and not lower than the temperature for thermosetting of the bis-maleimide compound. The pressure is not particularly limited, but it is preferably not lower than 100 N/cm 2 (10 kgf/cm 2 ), more preferable 200 to 400 N/cm 2 (20 to 40 kgf/cm 2 ). The time of the bonding by heating and pressing is not particularly limited so long as secure adhesion of the adhesive layer and, when a bis-maleimide compound is used, thermosetting of the bis-maleimide compound is attained. In an embodiment, preferable time for bonding by heating and pressing is 15 to 60 minutes. The flexible printed-circuit board used in the method of the present invention is not particularly limited so long as it comprises at least one flexible base which has at least one surface bearing a circuit. A typical example of the preferred flexible printed-circuit board is a flexible printed-circuit board having no adhesive layer or a flexible printed-circuit board having at least one adhesive layer therein. The flexible printed-circuit board having no adhesive layer may be produced by making at least one circuit on the copper foil-bearing surface of a copper foil/polyimide film laminate, namely a copper-clad polyimide film having no adhesive layer. The flexible printed-circuit board having at least one adhesive layer may be produced by making at least one circuit on the copper foil-bearing surface of a copper foil/adhesive/polyimide film laminate, namely a copper-clad polyimide film having an adhesive layer, or on both the copper foil-bearing surfaces of a copper foil/adhesive/polyimide film/adhesive/copper foil laminate, namely a double-sided copper-clad polyimide film. The copper-clad polyimide film having at least one adhesive layer may be produced by bonding a copper foil to at least one surface of a polyimide film through an adhesive, and the adhesive preferably has a glass transition temperature of not lower than 200 °C . If the glass transition temperature of the adhesive in a flexible printed-circuit board is lower than 200 °C , the circuit of the flexible printed-circuit board may get out of position by the heating and pressing at the time of bonding with a cover layer film and the flexible printed-circuit board may be deteriorated. In the present invention, bonding by heating and pressing is generally carried out at a temperature approximately 100 to 150 °C higher than the glass transition temperature of the acrylic or epoxy adhesives that have generally been used in the conventional three-layer flexible printed-circuit boards. An example of the copper foil/polyimide film laminate, namely the copper-clad polyimide film having no adhesive layer, is MCF-5000I (Trade name for a copper-clad film produced by Hitachi Chemical Company, Ltd.). An example of the copper foil/adhesive/polyimide film laminate, namely the copper-clad polyimide film having an adhesive layer, is MCF-5010I (Trade name for a copper-clad film produced by Hitachi Chemical Company, Ltd. wherein the adhesive used has a glass transition temperature of not lower than 200 °C ). Prior to the bonding, it is desirable to subject the circuit of the flexible printed-circuit board to be used to a treatment for improving adhering property, such as a browning treatment (cuprous oxide), a blackening treatment (cupric oxide) or a treatment with a coupling agent. Finally the adhesive layer coating the polyimide film on the surface that is not treated to increase adhering property or is subjected to a release treatment is removed from the laminate obtained by bondinq. The removal of the adhesive layer can be performed easily by peeling it from an end of the laminate with hands. According to the method of the present invention, cover lay films which do not curl and are excellent in heat resistance can be obtained. A combined use of such cover lay films and two-layer metal-clad films make it possible to produce heat resistant flexible printed circuit boards covered with cover lay. EXAMPLES 1 TO 3 AND COMPARATIVE EXAMPLES 1 AND 2 PREPARATION EXAMPLE 1 Into a 60-liter stainless reaction vessel equipped with a thermocouple, a stirrer, a nitrogen inlet and a condenser placed were 4.20 kg of 2,2-bis[4-(4-aminophenoxy)phenyl]propane and 42.5 kg of N,N-dimethylacetamide, and were then stirred to dissolve 2,2-bis[4-(4-aminophenoxy)phenyl]propane in N,N-dimethylacetamide, while dried nitrogen was made to flow through the reaction vessel. While the resulting solution was cooled to 20 °C or lower with a water jacket, polymerization was carried out by adding 3.30 kg of benzophenone tetracarboxylic dianhydride slowly into the solution, to obtain a viscous polyamic acid varnish. For the purpose of facilitating the following application operation, the polyamic acid varnish was cooked at 80 °C until the rotating viscosity of the polyamic acid varnish reached about 200 poise. The polyamic acid varnish contained 7.5 kg (15 % by weight) of a polyamic acid. A polyimide having a glass transition temperature of 245 °C was obtained by imidizing the polyamic acid. The polyamic acid varnish was then cooled to 40 °C , and 1.50 kg of N,N' -(methylene-di-p-phenylene)bis-maleimide, which corresponded to 20 parts by weight of N,N' -(methylene-di-p-phenylene)bis-maleimide per 100 parts by weight of the polyamic acid used, was added and dissolved therein to obtain a polyimide adhesive. EXAMPLE 1 A surface of a polyimide film of 25 µm thick (produced by Ube Industries, Ltd., trade name: UPILEX-S) was subjected to an oxygen plasma treatment (pressure: 0.1 torr, plasma power density: 26 W/cm 2 , time: approximately 3 seconds), and the other surface of the polyimide film was kept untreated. The polyimide adhesive prepared in the Preparation Example 1 was applied to both the surfaces of the polyimide film, and was dried at 150 °C for 10 minutes and at 200 °C for 30 minutes, to dry the polyimide adhesive and imidize the polyamic acid therein. Each of the adhesive layers of the cover lay film thus obtained was 40 µm thick and contained 0.3 % by weight of residual volatile matter. A flexible printed-circuit board was produced from a two-layer copper-clad film (copper foil/polyimide film)(Trade name MCF-5000I, produced by Hitachi Chemical Company, Ltd.) by making the copper foil layer of the two-layer copper-clad film into a circuit of stripe lines (line width: 0.050-0.500 mm, thickness: 35 µm) and then subjecting the circuit surface to a browning treatment. The flexible printed-circuit board and the coverlay film were located together to form a composite wherein the circuit surface of the copper-clad film contacted the adhesive layer coating the plasma treated surface. The composite was tightened temporarily and was then pressed at 250 °C for 30 minutes under a pressure of 40 kgf/cm 2 . Subsequently, the adhesive layer coating the untreated surface of the polyimide film of the cover lay film was peeled off, to obtain a flexible printed-circuit board covered with a cover lay. The peel strength between the adhesive layer and the untreated surface of the polyimide film was 0.3 kgf/cm. The peel strength of the cover lay from the flexible printed-circuit board was 0.9 kgf/cm, and no abnormality was recognized after a solder-bath test conducted at 350 °C for three minutes. EXAMPLE 2 A flexible printed-circuit board covered with a cover lay was produced in the same manner as in Example 1 with the exception that a three-layer copper-clad laminate (copper foil/adhesive having a glass transition temperature of 220 °C /polyimide film) (Trade name MCF-5010I, produced by Hitachi Chemical Company, Ltd.) was used in place of the two-layer copper-clad laminate used in Example 1. The peel strength between the adhesive layer and the untreated surface of the polyimide film was 0.3 kgf/cm. The peel strength of the coverlay was 0.9 kgf/cm, and no abnormality was recognized after a solder-bath test conducted at 350 °C for three minutes. EXAMPLE 3 A flexible printed-circuit board covered with a coverlay was produced in the same manner as in Example 1 with the exception that a polyimide film of 25 µm thick having a surface treated to improve the adhering property (Trade name UPILEX-SGA, produced by Ube Industries, Ltd.) was used and no further surface treatment was carried out. The peel strength between the adhesive layer and the untreated surface of the polyimide film was 0.3 kgf/cm. The peel strength of the coverlay was 0.8 kgf/cm, and no abnormality was recognized after a solder-bath test conducted at 350 °C for three minutes. COMPARATIVE EXAMPLE 1 A cover lay film was produced in the same manner as in Example 1 with the exception that a coverlay film was produced by forming an adhesive layer only on the plasma treated surface of a polyimide film. The obtained cover lay film curled severely so as to make it difficult to locate properly it and a flexible printed-circuit board together. A flexible printed-circuit board covered with a cover lay was produced in the same manner as in Example 1 with the exception that the thus obtained cover lay film was used, but, in the produced flexible printed-circuit board covered with a cover lay, the flexible printed-circuit board and the cover lay did not meet each other. COMPARATIVE EXAMPLE 2 A flexible printed-circuit board covered with a cover lay was produced in the same manner as in Example 1 with the exception that a polyimide film having an epoxy adhesive layer on only one surface (Trade name CUSV, produced by Nikkan Kogyo Co., Ltd.) was used as a cover lay film. Delamination of the cover lay occurred after a solder-bath test at 350 °C .

Claims: A method of producing a flexible printed-circuit board covered with a cover layer comprising: assembling (a) a flexible printed-circuit board that comprises a flexible base having a surface bearing a circuit; and (b) a polyimide film having a surface treated to increase adhering property and another surface not treated to increase adhering property, each of the surfaces being coated with an adhesive layer by applying a polyimide adhesive to each of the surface and drying the applied polyimide adhesive by heating, thereby forming on the surface an adhesive layer 1.0 to 1.5 times as thick as the circuit, the polyimide adhesive comprising a compound selected from the group consisting of a polyimide and a polyimide precursor said compound being optionally dissolved in a solvent; to form a composite wherein the adhesive layer coating the surface treated to increase adhering property is interposed between the polyimide film and the surface bearing the circuit; subjecting the composite to heat and pressure to bond the composite into a laminate structure; and peeling off the adhesive layer coating the polyimide film on the surface not treated to increase adhering property from the laminate structure. The method of claim 1, wherein the polyimide film has a linear thermal expansion coefficient of not larger than 2.5×10 -5 deg -1 at a temperature of 50 to 250 °C. The method of claim 1 cr 2, wherein the flexible printed-circuit board is made from a copper-clad polyimide film comprising a polyimide film which bears on one surface directly a copper foil, the flexible base is the polyimide film of the copper-clad polyimide film, and the circuit is made on the copper foil-bearing surface of the copper-clad polyimide film. The method of claim 1 or 2, wherein the flexible base of the flexible printed-circuit board is a polyimide film, and the circuit is a circuit formed by bonding a copper foil to at least one surface of the polyimide film through an adhesive having a glass transition temperature of not lower than 200 °C to form a copper-clad polyimide film, and making the copper foil of the copper-clad polyimide film into a circuit. The method of any of claims 1 to 4, wherein the treatment for increasing adhering property is a plasma treatment. The method of any of claims 1 to 5, wherein the surface of the polyimide film that is not treated to increase adhering property is coated with a release agent. The method of any of claims 1 to 6, wherein the polyimide adhesive comprises a polyamic acid dissolved in a solvent, the polyamic acid having a repeating unit represented by the following formula (1) wherein R 2 is or each R 3 , respectively, being hydrogen, a halogen or an alkyl group of from 1 to 4 carbon atoms and each X and Y, respectively, being -O- , -SO 2 - , or -S-, each R 4 , respectively, being hydrogen, an alkyl group of from 1 to 4 carbon atoms or -CF 3 , R 2 is The method of any of claims 1 to 7, wherein the polyamide adhesive includes 20 to 60 parts by weight of a bis-maleimide compound per 100 parts by weight of the polyamic acid. The method of claim 8, wherein the bis-maleimide compound is selected from the group consisting of N,N' -m-phenylene-bis-maleimide, N,N' -p-phenylene-bis-maleimide, N,N' -(oxy-di-p-phenylene)bis-maleimide, N,N' -(methylene-di-p-phenylene)bis-maleimide, N,N' -(sulfonyl-di-p-phenylene)bis-maleimide and 2,2-bis(maleimide-phenoxyphenyl)propane. The method of claim 7, wherein the polyamic acid has a repeating unit represented by the following formula (2) wherein each R 3 , respectively, is hydrogen, a halogen or an alkyl group of from 1 to 4 carbon atoms, and each R 4 , respectively, is hydrogen, an alkyl group of from 1 to 4 carbon atoms or -CF 3 . The method of claim 7, wherein the polyamic acid is a reaction product of an aromatic diamine selected from the group consisting of 1,3-bis(3-aminophenoxy)benzene, 1,3-bis(4-aminophenoxy)benzene, 1,4-bis(4-aminophenoxy)benzene, 4,4' -bis(4-aminophenoxy)biphenyl, bis[4-(3-aminophenoxy)phenyl]sulfone, bis[4-(4-aminophenoxy)phenyl]sulfone, 2,2-bis[4-(4-aminophenoxy)phenyl]propane, 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(3-aminophenoxy)phenyl]propane, 2,2-bis[4-(3-aminophenoxy)phenyl]hexafluoropropane and a diisocyanate thereof. and a tetracarboxylic acid compound selected from the group consisting of pyromellitic acid, 2,3,3' ,4' - tetracarboxydiphenyl, 3,3' ,4,4' -tetracarboxydiphenyl, 2,3,3' ,4' -tetracarboxydiphenyl ether, 3,3' ,4,4' - tetracarboxydiphenyl ether, 2,3,3' ,4' - tetracarboxybenzophenone, 3,3' ,4,4' - tetracarboxybenzophenone, an ester thereof, an anhydride thereof and an acid chloride thereof. The method of any of claims 7 to 11, wherein the solvent is selected from the group consisting of N-methylpyrrolidone, N,N-dimethylformamide, N,N-dimethylacetamide, dimethylsulfoxide, phenol, a halogenated phenol, 1,4-dioxane, γ -butyrolactone, tetrahydrofuran and diethylene glycol diethyl ether. The method of claim 8, wherein the treatment for increasing adhering property is a plasma treatment, the polyamic acid is a reaction product of 2,2-bis[4-(4-aminophenoxy)phenyl]propane and 3,3' ,4,4' - tetracarboxybenzophenone, the solvent is N,N-dimethylacetamide, the bis-maleimide compound is N,N' - (methylene-di-p-phenylene)bis-maleimide, and the flexible printed-circuit board is made from a copper-clad polyimide film comprising a polyimide film which bears on one surface directly a copper foil, the flexible base is the polyimide film of the copper-clad polyimide film, and the circuit is made on the copper foil-bearing surface of the copper-clad polyimide film. The method of claim 8, wherein the treatment for increasing the adhering property is a plasma treatment, the polyamic acid is a reaction product of 2,2-bis[4-(4-aminophenoxy)phenyl]propane and 3,3' ,4,4' - tetracarboxybenzophenone, the solvent is N,N-dimethylacetamide, the bis-maleimide compound is N,N' - (methylene-di-p-phenylene)bis-maleimide, and the flexible base of the flexible printed-circuit board is a polyimide film, and the circuit is a circuit formed by bonding a copper foil to at least one surface of the polyimide film through an adhesive having a glass transition temperature of not lower than 200 °C to form a copper-clad polyimide film, and making a circuit on the copper foil-bearing surface of the copper-clad polyimide film.

Inventors: IMAIZUMI JUNICHI, KATOH YASUSHI, NAGAO KOUICHI, NOMURA HIROSHI, OTI TAKATO, SATOU EIKICHI, SUZUKI MASAKATSU, IMAIZUMI, JUNICHI, KATOH, YASUSHI, NAGAO, KOUICHI, NOMURA, HIROSHI, OTI, TAKATO, SATOU, EIKICHI, SUZUKI, MASAKATSU
Applicants: HITACHI CHEMICAL CO LTD, HITACHI CHEMICAL CO., LTD.
Application year: 1991
Main classification: H05K3
IPC codes: C08G73, H01B3, C08J7, H05K3, C09J179, B32B15, H05K1