Photosensitive materials for electrophotography having a double-layer structure of a charge generation layer and a charge transport layer

Abstract: This invention relates to a A photosensitive material for electrophotography which comprises a conductive support, and a charge transport layer and a charge generation layer formed on the conductive support. The charge generation layer is formed from a dispersion which is obtained by mixing X-type and/or τ -type metal-free phthalocyanine, with or without at least one other charge generation agent, and a resin binder in a solvent, which is capable of dissolving at least a part of X-type and/or τ -type metal-free phthalocyanine, to such an extent that a ratio between X-ray diffraction peak intensities at about 7.5° and at about 9.1° is in the range of 1:1 to 0.1:1. When the at least one other charge generation agent is used in combination, the charge generation layer is formed on the conductive support on which the charge transport layer is formed. If such other agent is not used, the charge generation layer is formed on the charge transport layer with a certain thickness. The photosensitive materials have good photosensitivity, image characteristics and printing resistance.

Description: This invention relates to the art of electrophotography and more particularly, to photosensitive materials which have a double-layer structure of a charge generation layer and a charge transport layer and which are particularly suitable for use in an electrophotographic process including charging, exposing and developing operations to form images. Organic photoconductive conductors using organic photoconductive materials have a number of advantages over inorganic photoconductive conductors, including the ease in preparation of a variety of materials exhibiting high sensitivity at different wavelengths depending on the molecular design, little or no ecological problem, good productivity and economy, and inexpensiveness. Accordingly, extensive studies have been hitherto made on such organic conductors. Some organic conductors are in use and, at present, are being mainly employed as photosensitive materials for electrophotography. Known organic photoconductive conductors are usually arranged to have a double-layer structure which includes a charge generation layer capable of absorbing light to generate carriers and a charge transport layer wherein the generated carriers are transported. Many attempts have been made to increase sensitivity. Known organic conductive materials used to form the charge generation agent include various perylene compounds, various phthalocyanine compounds, thiapyrylium compounds, anthanthrone compounds, squalilium compounds, bisazo compounds, trisazo pigments, azulenium compounds and the like. On the other hand, the materials developed to form the charge transport layer include various hydrazone compounds, oxazole compounds, triphenylmethane compounds, arylamine compounds and the like. The charge generation and transport agents are, respectively, coated along with polymer binders by relatively simple coating techniques on supports such as drums, belts and the like. Examples of the binders used for this purpose include polyester resins, polycarbonate resins, acrylic resins, acryl-styrene resins and the like. In order to attain high sensitivity by the use of the double-layer structure, it is general that the charge generation layer is applied in a thickness of 0.1 to 1 micrometer and the charge transport layer is applied in a thickness of 10 to 20 micrometers. From the standpoint of the physical strength and the printing resistance, the charge generation layer is formed directly on the substrate and the charge transport layer is formed as a surface layer. In this arrangement, charge transport agents which are now in use are those which act by movement of positive holes. Thus, the known photosensitive materials are eventually of the negative charge type. The negative charge systems, however, have involved the problem that images are apt to suffer the influence of a support surface. For instance, if an aluminium drum is used, impurities and especially, inorganic metal impurities inevitably contained in the aluminium and irregularities on the surface influence the image quality. More particularly, such impurities or irregularities reflect on image defects such as white and/or black spot defects on images. This becomes more pronounced under high temperature and high humidity conditions. Thus, satisfactory image characteristics cannot be obtained. Such influences may be mitigated by use of highly pure drum materials, by mirror finish of the drum or by application of an undercoating on the drum, with an increase in production costs. Of these, the undercoating technique is considered to be most suitable. However, a difficulty is involved in an increase of residual potential. In order to solve the above problems, there is known a positive charge system wherein the charge generation layer and the charge transport layer are superposed in a reverse order as of the case of a negative charge system. However, this positive charge system should be very thin in the charge generation layer as set forth before. This leads to poor mechanical strength and a poor printing resistance. Thus, the known positive charge system has little utility in practical applications. If a protective layer is formed on the charge generation layer, the printing resistance may be improved but a residual potential will be increased with a lowering of environment resistance. DE-A-3,813,459 discloses a photosensitive member which has a charge generating layer comprising phthalocyanine pigments including τ-form on modified τ-form phthalocyanine and polyvinyl butyral. US-A-4,755,443 discloses a photoreceptor for electrophotography comprising a substrate incorporating a charge generating substance which is a metal or metal-free phthalocyanine. It is an object of the invention to provide a photosensitive material for electrophotography which has good image characteristics with high sensitivity and a good printing resistance. It is another object of the invention to provide a photosensitive material for electrophotography which has a double-layer structure including a charge generation layer and a charge transport layer wherein the charge generation layer contains X-type and/or τ-type metal-free phthalocyanine at least partially in a molecular state. It is a further object of the invention to provide a photosensitive material for electrophotography which may be either of the positive charge type or of the negative charge type. In accordance with one embodiment of the invention, there is provided an electrophotographic photosensitive material which comprises a conductive support, and a charge transport layer and a charge generation layer formed on the conductive support in this order, the charge generation layer having a thickness of from 10 to 50 micrometers and being formed from a dispersion which is obtained by mixing X-type and/or τ-type metal-free phthalocyanine and a resin binder in a solvent, which is capable of dissolving at least a part of X-type and/or τ-type metal-free phthalocyanine, to such an extent that a ratio between X-ray diffraction peak intensities at about 7.5° and at about 9.1° is from 1:1 to 0.1:1. By the mixing, at least a part of X-type and/or τ-type metal-free phthalocyanine is mixed with the resin binder in a molecular form or may be converted into a new crystal form as will be discussed hereinafter. The conversion of the at least a part of X-type and/or τ-type metal-free phthalocyanine is very effective in attaining high photoconductivity or sensitivity. Accordingly, the charge generation layer which has been conventionally formed as very thin can be made thick as defined above, so that the printing resistance and physical strength are remarkably improved. It will be noted that the photosensitive material of this embodiment is of the positive charge type. Fig. 1 is an X-ray diffraction pattern of X-type metal-free phthalocyanine; and Fig. 2 is an X-ray diffraction pattern of X-type metal-free phthalocyanine after dissolution in a solvent along with a resin binder to a satisfactory extent. The conductive support used in the invention is not critical and includes, for example, metal sheets such as Al sheets, and glass, paper or plastic sheets on which a metal is vapor deposited to form a conductive layer. The support may be in the form of drums, belts, sheets and the like. In the invention, it is essential that the charge generation layer be formed from a dispersion which comprises a dispersion of X-type and/or τ-type metal-free phthalocyanine and a resin binder in a solvent which is capable of dissolving at least a part of X-type and/or τ-type metal-free phthalocyanine. The mixing should be effected to such an extent that the ratio between X-ray diffraction peaks at about 7.5° and at about 9.1° is from 1:1 to 0.1:1. Phthalocyanine compounds are described in detail. Phthalocyanines are broadly classified into two groups including metallo-phthalocyanines and metal-free phthalocyanines. Typical of known metal-free phthalocyanines (which may be hereinafter referred to simply as H 2 -Pc) are α-type and β-type phthalocyanines. Xerox Co., Ltd. developed X-type metal-free phthalocyanine and reported as having excellent electrophotographic characteristics. In US-A-3,357,989, the X-type phthalocyanine is described with respect to its preparation, the relationship between the crystal form and electrophotographic characteristics and the structural analyses. According to this U.S. patent, X-type H 2 -Pc (phthalocyanine) is prepared by subjecting β-type H 2 -Pc prepared by a usual manner to treated with sulfuric acid to obtain α-type H 2 -Pc and then to ball milling over a long time. The crystal structure of X-type H 2 -Pc is apparently different from those of α or β -type H 2 -Pc. According to the X-ray diffraction pattern obtained with use of a CuK α line as shown in Fig. 1, the diffraction lines appear at 2  =7.4, 9.0, 15.1, 16.5, 17.2, 20.1, 20.6, 20.7, 21.4, 22.2, 23.8, 27.2, 28.5 and 30.3°. The most intense diffraction peak appears in the vicinity of 7.5° (corresponding to a lattice spacing, d, = 11.8 angstroms). When this intensity is taken as 1, the intensity of the diffraction line in the vicinity of 9.1° (corresponding to a lattice spacing, d, = 9.8 angstroms) is 0.66. Aside from the above crystal forms, τ-type metal-free phthalocyanine is also known. This phthalocyanine is obtained by subjecting to ball milling α, β or X-type crystals in an inert solvent along with a milling aid at a temperature of 5 to 10°C for 20 hours. The X-ray diffraction pattern is substantially similar to that of the X type provided that the ratio of the diffraction peak intensity at about 7.5° and the diffraction peak intensity at about 9.1° is 1:0.8. The X-type and/or τ-type metal-free phthalocyanine is added to a solvent along with a resin binder and is dispersed therein under mixing or kneading conditions. In order to obtain a stable solution, it takes about one day or over by ordinary agitation techniques. When the mixing under agitation is effected to a satisfactory extent, the X-type and/or τ-type phthalocyanine becomes finer in size and a part thereof is dissolved in the solvent or the resin solution. The dissolution can be confirmed by an increase of the viscosity of the solution. In this state, the phthalocyanine is considered to exist in the solution partly in a particulately dispersed state and partly in a molecularly dispersed state. The molecularly dispersed phthalocyanine is considered to be different in crystal form from the particulately dispersed phthalocyanine. This molecularly dispersed phthalocyanine is assumed to have the charge transport function. When X-type H 2 -Pc is used, the X-ray diffraction pattern of the dissolved X-type phthalocyanine is apparently different from that of X-type H 2 -Pc alone. More particularly, the X-ray diffraction pattern of the molecularly dispersed or dissolved X-type metal-free phthalocyanine shown in Fig. 2 has the tendency that the diffraction lines over 2  =21.4 disappear as compared with a X-ray diffraction pattern of X-type metal-free phthalocyanine per se. The diffraction pattern in the vicinity of 16.5° tends to increase in intensity. The most appreciable variation in the X-ray diffraction pattern is that, of two diffraction lines in the vicinity of 7.5° (d = 11.8 angstroms) and 9.1° (d= 9.8 angstroms), only the diffraction line in the vicinity of 7.5° is selectively decreased. From this, at least a part of the X-type metal-free phthalocyanine which is considered to be molecularly dispersed in the resin solution is believed to be converted into a new crystal form. The degree of mixing or kneading, and the mixing time and temperature depend on the type of solvent. In order to obtain good characteristics as a photosensitive material, the degree of the mixing or kneading can be determined by using the ratio between the diffraction pattern intensities in the vicinity of 7.5° and 9.1°, i.e. I 11.8 /I 9.8 . The ratio should be in the range of from 1:1 to 0.1:1 for both X-type and τ-type phthalocyanines. The solvents capable of dissolving at least a part of X-type and/or τ-type phthalocyanine include, for example, nitrobenzene, chlorobenzene, dichlorobenzene, dichloromethane, trichloroethylene, chloronaphthalene, methylnaphthalene, benzene, toluene, xylene, tetrahydrofuran, cyclohexanone, 1,4-dioxane, N-methylpyrrolidone, carbon tetrachloride, bromobutane, ethylene glycol, sulforane, ethylene glycol monobutyl ether, acetoxyethoxyethane, pyridine, or the like. The above solvents may be used singly or in combination. The binder resins used in the present invention should preferably be ones which can be dissolved in the solvents for the phthalocyanine as mentioned above. The binder resins suitable for this purpose include polyesters, polycarbonates, polyacrylates, polyvinyl acetate, polyvinyl chloride, polyvinylidene chloride, polyvinyl butyral, polyvinyl acetoacetal, polystyrene, polyacrylonitrile, polymethyl methacrylate, polyvinyl carbazoles, copolymers of the monomers used in the above-mentioned polymers, vinyl chloride/vinyl acetate/vinyl alcohol terpolymers, vinyl chloride/vinyl acetate/maleic acid terpolymers, ethylene/vinyl acetate copolymers, vinyl chloride/vinylidene chloride copolymers, melamine resins, alkyd resins, cellulose polymers, various siloxane polymers, and mixtures thereof. If two or more solvents are used in combination, it is possible to dissolve the phthalocyanine in one solvent and a resin binder in the other solvent. When a given resin binder is used, the dissolution and the variation in the X-ray diffraction pattern of the phthalocyanine may be changed depending on the type of solvent. As stated hereinabove, X-type metal-free phthalocyanine and a resin binder are dissolved in a solvent and mixed by means of ball mills, attritors, sand grinders or the like for one day or over. The resultant solution is applied onto a conductive support on which a charge transport layer has been formed. The application is carried out, for example, by bar coaters, calender coaters, spin coaters, blade coaters, dip coaters, gravure coaters or the like. As set out before, it is usual to form a charge generation layer in a thickness of from 0.1 to 2 micrometer. This is because too large a thickness undesirably brings about a lowering of photosensitive characteristics and a lowering of dissolution. In this connection, however, the charge generation layer of the invention obtained from the dispersion or solution mixed in such a manner as stated above exhibits good photosensitive and image characteristics irrespective of the thickness. The thickness of the charge generation layer is generally in the range of from 10 to 50 micrometers, preferably from 20 to 30 micrometers. In this range of the thickness, the printing resistance is good without use of any overcoating layer which would adversely influence the photosensitive and image characteristics. In one embodiment, the ratio by weight of X-type and/or τ-type metal-free phthalocyanine and the resin binder is from 2 : 1 to 1 : 10. The X-type and/or τ-type metal-free phthalocyanine and the binder resin should preferably be mixed at a ratio by weight of 1 : 10 to 1 : 1. The charge transport layer formed directly on the conductive support is made of a dispersion of a charge transport agent in a resin binder. This layer serves as a kind of undercoating for the charge generation layer and acts to eliminate the influences of the surface condition of the conductive support. With aluminium drums, for example, metal impurities and/or surface irregularities influence the image quality, resulting in black spot defects or other defects produced on images. In this embodiment, the charge generation layer is formed on the charge transport layer and suffers the influence. As a matter of course, a blocking layer or conductive layer may be provided between the support and the charge generation layer in addition to the charge transport layer. The charge transport agents may be any known compounds such as various hydrazone compounds, oxazole compounds, triphenylmethane compounds, arylamine compounds and the like, which are ordinarily used for this purpose. Specific examples are those set out in examples. The resin binders may be those used to form the charge generation layer. To prepare a dispersion or solution for the charge transport layer, a charge transport agent and a resin binder are dissolved or dispersed in a solvent for the resin binder. Examples of such binders may be not only those used to form the charge generation layer, but also alcohols such as methanol, ethanol, butanol and the like. The charge transport layer generally has a thickness of from 5 to 40 micrometers, preferably from 10 to 30 micrometers. The photosensitive material obtained in this embodiment has a sensitivity as high as from 0.5 to 2.0 lux.second and exhibits good sensitivity to light with a wide range of wavelength of from 600 to 800 nm. The residual potential is not larger than approximately 30 volts. The present invention is more particularly described by way of examples. Comparative examples are also shown. Example 1 X-type metal free-phthalocyanine (Fastogen Blue 8120B, made by Dainippon Inks Co., Ltd.) and a polyester used as a binder (Vylon 200, available from Toyobo Co., Ltd.) were dissolved in tetrahydrofuran at a ratio by weight of 1 : 5, followed by mixing for two days in a ball mill to obtain a solution for charge generation layer. The solution was subjected to measurement of X-ray diffraction pattern, revealing that the ratio of the diffraction line intensities (I 11.8 /I 9.8 ) was 0.7. From this, it was confirmed that this ratio was significantly different from the ratio of starting X-type metal-free phthalocyanine of 1.5. Separately, a polycarbonate (Iupilon Z, available from Mitsubishi Gas Chem. Co., Ltd.) and 4-dibenzylamino-2-methylbenzoaldehydo-1,1'-diphenylhydrazone (CTC-191, available from Anan Perfume Ind. Co., Ltd.) were dissolved in ethyl alcohol at a ratio by weight of 2:3, followed by agitation over 2 hours to obtain a solution for charge transport layer. The solution for charge transport layer was initially applied onto an aluminium support in a dry thickness of 20 micrometers and dried at 60°C for 30 minutes to form a charge transport layer. Thereafter, the solution for charge generation layer was applied onto the transport layer in a dry thickness of 15 micrometers and dried at 80°C for 2 hours to form a charge generation layer. Thus, a photosensitive material was obtained. Example 2 The general procedure of Example 1 was repeated except that for obtaining the solution for charge transport layer, there was used 1-phenyl-1,2,3,4-tetrahydroquinolin-6-carboaldehydo-1,1'-diphenylhydrazone (CTC-236, available from Anan Perfume Ind. Co., Ltd.) instead of the 4-dibenzylamino-2-methylbenzoaldehydo-1,1'-diphenylhydrazone, thereby obtaining a photosensitive material. Example 3 The general procedure of Example 1 was repeated except that for obtaining the solution for charge transport layer, there was used 9-ethylcarbazol-3-carboxyaldehydo-1-methyl-1-phenylhydrazone (CT-A, available from Anan Perfume Ind. Co., Ltd.) instead of the 4-dibenzylamino-2-methylbenzoaldehydo-1,1'-diphenylhydrazone, thereby obtaining a photosensitive material. Example 4 The general procedure of Example 1 was repeated except that a solution for charge generation layer was obtained by dissolving X-type metal-free phthalocyanine and an acrylic resin used as a binder (Acrydic, available from Dainippon Inks Co., Ltd.) at a mixing ratio by weight of 1:4 in tetrahydrofuran and mixing for two days in a ball mill and that the thickness of the charge generation layer was 20 micrometers, thereby obtaining a photosensitive material. Example 5 The general procedure of Example 2 was repeated except that a solution for charge generation layer was obtained by dissolving X-type metal-free phthalocyanine and an acrylic resin used as a binder (Acrydic, available from dainippon Inks Co., Ltd.) at a mixing ratio by weight of 1:4 in tetrahydrofuran and mixing for two days in a ball mill and that the thickness of the charge generation layer was 20 micrometers, thereby obtain a photosensitive material. Example 6 The general procedure of Example 3 was repeated except that a solution for charge generation layer was obtained by dissolving X-type metal-free phthalocyanine and an acrylic resin used as a binder (Acrydic, available from dainippon Inks Co., Ltd.) at a mixing ratio by weight of 1:4 in tetrahydrofuran and mixing for two days in a ball mill and that the thickness of the charge generation layer was 20 micrometers, thereby obtain a photosensitive material. Example 7 The general procedure of Example 1 was repeated except that there was used, instead of polyester, vinyl chloride/vinyl acetate polymer so that the diffraction line intensity ratio, I 11.8 /I 9.8 , was controlled in the range of from 0.5 to 0.8, thereby obtaining a photosensitive material and that the mixing ratio of the binder and the phthalocyanine was at a ratio by weight of 1:1 and the binder was initially dissolved in tetrahydrofuran, after which the phthalocyanine was added. Example 8 The general procedure of Example 7 was repeated except that vinyl chloride/vinyl acetate/vinyl alcohol polymer was used as the binder, thereby obtaining a photosensitive material. Example 9 The general procedure of Example 7 was repeated except that vinyl chloride/vinyl acetate/maleic acid polymer was used as the binder, thereby obtaining a photosensitive material. Example 10 The general procedure of Example 7 was repeated except that a polycarbonate was used as the binder, thereby obtaining a photosensitive material. Example 11 The general procedure of Example 7 was repeated except that polystyrene was used as the binder, thereby obtaining a photosensitive material. Example 12 The general procedure of Example 7 was repeated except that polymethyl methacrylate was used as the binder, thereby obtaining a photosensitive material. Comparative Example 1 The general procedure of Example 4 was repeated except that n-butyl alcohol was used instead of tetrahydrofuran, thereby obtaining a photosensitive material. n-Butyl alcohol dissolves the acrylic resin but does not dissolve X-type metal-free phthalocyanine, so that the crystal form is not changed but the phthalocyanine is dispersed only in a particulate state. Comparative Example 2 The general procedure of Example 5 was repeated except that n-butyl alcohol was used instead of tetrahydrofuran, thereby a photosensitive material. Comparative Example 3 The general procedure of Example 6 was repeated except that n-butyl alcohol was used instead of tetrahydrofuran, thereby obtaining a photosensitive material. The photosensitive materials obtained in the examples and comparative examples were each subjected to measurement of photosensitivity by the use of Paper Analyzer Model EPA-8100, made by Kawaguchi Denki K.K., in which white light from tungsten was irradiated on the material to measure a photosensitivity by positive charge (half-life exposure, E 1/2 ) and also photosensitivity after repetition of 1000 exposure cycles. In addition, a wavelength characteristic in a range of 400 to 1000 nm was also measured. The results are shown in Table 1. Example No. Charge Potential Photosensitivity Wavelength Characteristic (V) Initial Half-life Exposure (lux.sec) Half-life Exposure After 1000 Cycles (lux.sec) (cm 2 /µJ) 1 910 1.2 1.2 1.6 2 850 1.1 1.0 2.0 3 870 1.5 1.5 1.2 4 950 1.5 1.5 1.4 5 900 1.6 1.5 1.5 6 930 1.5 1.6 1.2 7 950 1.8 1.8 1.2 8 780 1.6 1.7 1.3 9 950 1.8 2.0 1.1 10 700 1.5 1.5 1.5 11 930 2.0 2.0 1.0 12 900 1.8 1.7 1.5 Comparative Example No. 1 850 3.9 4.0 0.5 2 980 3.2 3.8 0.7 3 850 3.4 3.9 0.6 The comparison between the results of Examples 4 and 5 and Comparative Examples 1 to 3 reveals that the photosensitive materials of the examples are better in the photosensitivity and the wavelength characteristic. In addition, with the materials of the invention, the photosensitivity after 1000 exposure cycles is substantially the same as the initial photosensitivity with a very good printing resistance. Moreover, it was confirmed that the photosensitive materials of the examples were substantially free of any image defects such as black spots under high temperature and high humidity conditions. Example 13 The general procedure of Example 1 was repeated except that a solution for charge generation layer was obtained by dissolving X-type metal-free phthalocyanine, 2,7-bis[2-hydroxy-3-(2-chlorophenylcarbamoyl)-1-naphthylazo]-9-fluorene and an acrylic resin used as a binder (Acrydic, available from Dainippon Inks Co., Ltd.) at mixing ratios by weight of 1:1:2 in tetrahydrofuran and mixing, thereby obtaining a photosensitive material. Example 14 The general procedure of Example 13 was repeated except that a solution for charge transport layer was obtained using 1-phenyl-1,2,3,4-tetrahydroquinolin-6-carboaldehydo-1,1'-diphenylhydrazone (CTC-236) instead of 4-dibenzylamino-2-methylbenzoaldehydo-1,1'-diphenylhydrazone, thereby obtaining a photosensitive material. Example 15 The general procedure of Example 13 was repeated except that a solution for charge transport layer was obtained using 9-ethylcarbazol-3-carboxyaldehydo-1-methyl-1-phenylhydrazone (CT-A) instead of the 4-dibenzylamino-2-methylbenzoaldehydo-1,1'-diphenylhydrazone, thereby obtaining a photosensitive material. Comparative Example 4 The general procedure of Example 13 was repeated except that n-butyl alcohol was used instead of tetrahydrofuran, thereby obtaining a photosensitive material. n-Butyl alcohol dissolves the acrylic resin but does not dissolve X-type metal-free phthalocyanine and 2,7-bis[2-hydroxy-3-(2-chlorophenylcarbamoyl)-1-naphthylazo]-9-fluorene, so that the phthalocyanine is dispersed only in a particulate state without any change of the crystal form. Comparative Example 5 The general procedure of Example 14 was repeated except that n-butyl alcohol was used instead of tetrahydrofuran, thereby obtaining a photosensitive material. Comparative Example 6 The general procedure of Example 15 was repeated except that n-butyl alcohol was used instead of tetrahydrofuran, thereby obtaining a photosensitive material. The photosensitive materials obtained in the examples and comparative examples were each subjected to measurement of photosensitivity by the use of Paper Analyzer Model EPA-8100, made by Kawaguchi Denki K.K., in which white light from tungsten was irradiated on the material to measure a photosensitivity by positive charge (half-life exposure, E 1/2 ) and also photosensitivity after repetition of 1000 exposure cycles. In addition, a wavelength characteristic in a range of 400 to 1000 nm was also measured. The results are shown in Table 2. Example No. Charge Potential Photosensitivity Wavelength Characteristic (V) Initial Half-life Exposure (lux.sec) Half-life Exposure After 1000 Cycles (lux.sec) (cm 2 /µJ) 13 780 0.8 0.8 1.4 14 820 0.9 0.9 1.2 15 850 0.9 0.9 1.2 Comparative Example No. 4 850 1.6 1.8 1.0 5 980 2.0 2.0 0.9 6 850 2.0 2.2 0.8 The comparison between the results of Examples 13 to 15 and Comparative Examples 4 to 6 reveals that the photosensitive materials of the examples are better in the photosensitivity and the wavelength characteristic. In addition, with the materials of the invention, the photosensitivity after 1000 exposure cycles is substantially the same as the initial photosensitivity with a very good printing resistance. Also, the photosensitive materials of the invention had good image characteristics under high temperature and high humidity conditions.

Claims: An electrophotographic photosensitive material which comprises a conductive support, and a charge transport layer and a charge generation layer formed on the conductive support in this order, said charge generation layer having a thickness of from 10 to 50 micrometers and being formed from a dispersion which is obtained by mixing X-type and/or τ-type metal-free phthalocyanine and a resin binder in a solvent, which is capable of dissolving at least a part of X-type and/or τ-type metal-free phthalocyanine, to such an extent that a ratio between X-ray diffraction peak intensities at about 7.5° and at about 9.1° is from 1:1 to 0.1:1. A photosensitive material according to Claim 1, wherein a ratio by weight of X-type and/or τ-type metal-free phthalocyanine and the resin binder is from 2:1 to 1:10. A photosensitive material according to claim 1 or 2, wherein the charge generation layer has a thickness from 20 to 30 micrometers. A photosensitive material according to claim 1, 2 or 3, wherein the charge transport layer has a thickness from 5 to 40 micrometers. A photosensitive material according to claim 4, wherein the charge transport layer has a thickness from 10 to 30 micrometers. A photosensitive material according to any one of the preceding claims having a sensitivity from 0.5 to 2.0 lux.second and a residual potential not larger than 30 volts.

Inventors: MURAKAMI MUTSUAKI, OMOTE ATSUSHI, TSUCHIYA SOHJI, MURAKAMI, MUTSUAKI, OMOTE, ATSUSHI, TSUCHIYA, SOHJI
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1991
Main classification: G03G5
IPC codes: G03G5