Components and catalysts for the copolymerisation of olefins

Abstract: Disclosed are catalysts for the polymerisation of olefins obtained by the reaction of an Al-alkyl compound and a silicon compound of the formula where R₁, R₂, R₃, and R₄ are hydrocarbyl radicals, with a solid catalyst component comprising a titanium halide or halogen alcoholate and an electron-donor compound having specific characteristics of extractability with Al-triethyl, supported on an active magnesium halide.

Description: The present invention relates to catalyst components and catalysts for the polymerization of olefins and their use particularly in the polymerization of CH 2 =CHR olefins, where R is a 1-6 carbon linear or branched alkyl radical, an aryl radical or a hydrogen atom. The catalysts comprising titanium compounds supported on magnesium halides in active form are well known in the field of olefins polymers. Catalysts of this type are described, for instance, in USP 4,278,718. Said catalysts, although being highly active in the polymerization of ethylene as well as other alpha-olefins, such as propylene, are not sufficiently stereospecific. The stereospecificity was improved by adding an electron-donor compound to the solid component comprising the titanium compound supported on magnesium halides in active form (US 4,544,713). Further improvements were obtained by using an electron-donor compound added to the solid component (inside donor) as well as one added to the Al-alkyl compound (outside donor) as described in US 4,107,414. Very high performances, both in terms of activity and stereospecificity, are provided by the catalysts described in European patent 0045977. Said catalysts contain, as the solid component, a magnesium halide in active form on which a titanium halide (TiCl 4 ) and an electron-donor compound, selected from specific classes of carboxylic acids esters of which the phthalates are representative, are supported. The co-catalyst used is an Al-alkyl compound to which a silicon compound containing at least one Si-OR bond (R = hydrocarbyl radical) is added. In US 4,522,930 are described catalysts whose solid catalyst component is characterized by the fact that it contains an electron-donor compound extractable with Al-triethyl (under standard extraction conditions) for at least 70% of the moles, and that it has, after extraction, a surface area of at least 20 m 2 /g. Said catalysts comprise, as co-catalyst, an Al-trialkyl compound to which an electron-donor compound is added which does not form complexes with the Al-triethyl which can be detected by potentiometric titration under standard reaction conditions. The electron-donor compounds mentioned above include silicon compounds with Si-OR bonds, such as 2,2,6,6-tetramethylpiperidine, 2,2,5,5-tetramethylpyrrolidine, Al-diethyl-2,2,6,6-tetramethylpiperidide, Al-dichloromonophenoxy, and other compounds. Now unexpectedly a new class of electron-donor compounds has been found, which can be used together with an Al-alkyl to form, in combination with solid catalyst components having the characteristics described in US 4,522,930, highly active and stereospecific catalysts. The compounds of the invention are silanes of the following general formula: where R 1 and R 2 are the same or different and are linear or branched C 1-18 alkyl, C 3-18 cycloalkyl, C 6-18 aryl, C 7-18 alkaryl, or C 7-18 aralkyl radicals, optionally containing O, N, S, P, or halogens; R 3 and R 4 , are the same or different and are linear or branched C 1-18 alkyl, C 3-18 cycloalkyl, C 6-18 aryl, C 7-18 alkaryl or aralkyl radicals, and preferably alkyl radicals with 1-6 carbon atoms, most preferably methyl radicals. In particular R 1 and R 2 are methyl, ethyl, propyl, isopropyl, n-butyl, tert-butyl, sec-butyl, neo-pentyl, 2-ethylhexyl, cyclohexyl, methylcyclohexyl, phenyl, benzyl, p-chlorophenyl, 1-naphthyl or 1-decahydronaphthyl. Examples representative of silanes of the formula above include: 2-ethylhexyl-trimethoxymethylsilane, isopropyltrimethoxymethylsilane, methyl-trimethoxymethylsilane, n-butyl-trimethoxymethylsilane, isobutyl-trimethoxymethylsilane, secbutyl-trimethoxymethyl silane, tert-butyltrimethoxymethylsilane, cyclohexyl-trimethoxymethylsilane, phenyl-trimethoxymethylsilane, cumyl-trimethoxymethylsilane, phenylethyl-trimethoxymethylsilane, cyclohxeylethyltrimethoxymethylsilane,p-chlorophenyl-trimethoxymethylsilane, 1-naphthyl-timethoxymethylsilane, p-fluorophenyltrimethoxymethylsilane, 1-decahydronaphthyltrimethoxymethylsilane, p-tert-butylphenyltrimethoxymethylsilane, dicyclohexyl-dimethoxymethylsilane, dimethyl-dimethoxymethylsilane, diethyl-dimethoxymethylsilane, di-n-propyl-dimethoxymethylsilane, di-isopropyldimethoxymethylsilane, di-n-butyl-dimethoxymethylsilane, diisobutyl-dimethoxymethylsilane, di-sec-butyldimethoxymethylsilane, di-tert-butyl-dimethoxymethylsilane, dimethyl-diethoxymethylsilane, diethyl-diethoxymethylsilane, di-n-propyl-diethoxymethylsilane, di-isopropyldiethoxymethylsilane, di-n-butyl-diethoxymethylsilane, diisobutyl-diethoxymethylsilane, di-sec-butyldiethoxymethylsilane, di-tert-butyl-diethoxymethylsilane, methyl-ethyl-dimethoxymethylsilane, methyl-propyldimethoxymethylsilane, methyl-benzyl-dimethoxymethylsilane, methyl-phenyl-dimethoxymethylsilane, methyl-cyclohexyldimethoxymethylsilane, methyl-cyclohexylmethyldimethoxymethylsilane, bis(p-chlorophenyl)-dimethoxymethylsilane, bis (phenylethyl)-dimethoxymethylsilane, bis(cyclohexyl) -dimethoxymethylsilane, methyl-isobutyldimethoxymethylsilane, methyl-2-ethylhexyldimethoxymethylsilane, bis(2-ethylhexyl)-dimethoxymethylsilane, bis(p-methylphenyl)-dimethoxymethylsilane, methyl-isopropyldimethoxymethylsilane, diphenyl-dimethoxymethylsilane, cyclohexyl-tert-butyl-dimethoxymethylsilane, isopropyl-tertdimethyl-diethoxymethylsilane, dibenzyl-dimethoxymethylsilane, bis(cyclohexylmethyl)-dimethoxymethylsilane, di-isobutyl-diisobutoxymethylsilane, isobutyl-isopropyldimethoxymethylsilane, di-cyclopentyl-dimethoxymethylsilane, di-neo-pentyl-dimethoxymethylsilane, isopentyl-isopropyldimethoxymethylsilane, phenyl-benzyl-dimethoxymethylsilane, cyclohexyl-cyclohexylmethyl-dimethoxymethylsilane, isopropyltertbutyl-dimethoxymethylsilane, isopropyl-tert-butyl-di-n-butoxymethylsilane, isopropyl-tert-butyl-diisobutoxymethylsilane, isopropyl-tert-butyl-di-tert-butoxymethylsilane, methyl-cyclohexyl-diethoxymethylsilane, methyl-cyclohexyl-di-n-butoxymethylsilane, methyl-cyclohexyldi-isobutoxymethylsilane, methyl-cyclohexyl-di-tert-butoxymethylsilane, tetramethoxymethylsilane, tetraethoxymethylsilane, tetra-n-butoxymethylsilane, tetra-ibutoxymethylsilane, tetra-tertbutoxymethylsilane. A general method for the preparation of silicon compounds of the invention comprises in reacting a dialkyldichlorosilane or dialkyldimethoxysilane with the Grignard of the methylchloromethyl ether, or in reacting the dialkylbis(chloromethyl)silane with sodium methylate. The reaction is carried out at temperatures from 40°C to 100°C in an inert solvent. As already indicated, the electron-donor compounds of this invention can be used together with Al-alkyl compounds to form, in combination with the solid catalyst components described in US 4,522,930, highly active and stereospecific catalysts. The catalyst components described in this US patent include a titanium compound containing a Ti-halogen bond and an electron-donor compound at least 70% in moles of which is extractable with Al-triethyl under standard extraction conditions. After extraction, the solid has a surface area (B.E.T.) of at least 20 m 2 /g and usually from 100 to 300 m 2 /g. The electron-donor compounds that can be used in the preparation of the solid catalyst components described in said US patent include ethers, ketones, lactones, compounds containing N, P and/or S atoms, and specific types of esters. Besides the esters of US 4,522,930, the classes of esters described in European patent No. 0045977 can also be used. Particularly suitable are the phthalic acid esters, such as diisobutyl, dioctyl, diphenyl and benzyl-butylphthalate; malonic acid esters, such as diisobutyl and diethylmalonate; the alkyl and arylpivalates; alkyl, cycloalkyl and aryl maleates; alkyl and aryl carbonates, such as diisobutyl carbonate, ethyl-phenyl carbonate and diphenyl carbonate; are succinic acid esters, such as mono and diethyl succinate. The phthalic acid esters are preferred. The electron-donor compound is fixed on the magnesium halide usually in an amount from 5 to 20 mole percent. In the solid catalyst components the Mg/Ti molar ratio is generally from 30:1 to 4:1. In the components supported on porous resins or inorganic oxides the ratio is different and is usually from 10:1 to 2:1. The titanium compounds that can be used for the preparation of the solid catalyst components are the titanium halides and alkoxy titanium halides. The preferred compound is the titanium tetrachloride. Satisfactory results are obtained also with the titanium trihalides, particularly the TiCl 3 HR, TiCl 3 ARA, and with alkoxy titanium halides, such as TiCl 3 OR, where R is a phenyl radical. Reactions which lead to the formation of magnesium halide in active form starting from magnesium compounds which are different from the halides are well known in literature. The active form of the magnesium halide in the catalyst components is identified by the X-ray diffraction spectrum of the solid catalyst component wherein the major intensity reflection which appears in the spectrum of the nonactivated magnesium halides (having surface area smaller than 3 m 2 /g) is no longer present, and in its place there is a halo with the maximum intensity shifted with respect to the position of the major intensity reflection, or the major intensity reflection has diminished in intensity, and gives a half-peak breadth at least 30% greater than the one of the major intensity reflection which appears in the spectrum of the nonactivated Mg halide. The most active forms of magnesium halide are those in which the halo appears in the X-ray spectrum of the solid catalyst component. Among the magnesium halides, the chloride is the preferred compound. In case of the most active forms of the magnesium chloride, in the X-ray spectrum of the catalyst component appears a halo in place of the reflection which in the magnesium chloride spectrum is situated at the interplanar distance of 0.256 nm (2.56 Å). The methods mentioned above can be used also in the case of the solid catalyst components containing electron-donors which have the characteristics indicated in US patent 4,544,713. The catalysts of the invention can be used in the polymerization of CH 2 =CHR olefins, where R is hydrogen, a 1-6 carbon linear or branched alkyl, or an aryl, or mixtures of said olefins or mixtures of one or more of said olefins with diolefins. In the case of polymerization of said CH 2 =CHR olefins, particularly when the olefin is propylene, the Al-alkyl compounds that can be used are selected from Al-trialkyl, such as Al-triethyl, Al-triisobutyl, Al-tri-n-butyl, and linear or cyclic Al-alkyl compounds containing two or more Al atoms linked together through O or N atoms, or SO 4 and SO 3 groups. Examples of said compounds are: (C 2 H 5 ) 2 ―Al-O-Al(C 2 H 5 ) 2 where n is a number from 1 to 20. AlR 2 OR' compounds, where R'is an aryl radical substituted in position 2 and/or 6 and R is a 1-8 carbon alkyl radical, can also be used as well as AlR 2 H compounds where R has the meaning already indicated. The Al-alkyl compound is used in Al/Ti molar ratios usually from 1 to 1000. In the case of the polymerization of propylene and similar alpha-olefins, the trialkyl aluminum compounds can be used in a mixture with Al-alkyl halides, such as AlEt 2 Cl and Al 2 Et 3 Cl 3 . The Al-alkyl compounds indicated above are used with the silicon compounds of the invention. The polymerization of the alpha-olefins is carried out according to known methods operating in liquid phase constituted by the monomer, or monomers, or by a solution of same in an aliphatic or aromatic hydrocarbon solvent, or in gas phase, or also by combining polymerization stages in liquid phase and in gas phase. The (co)polymerization temperature is usually from O° to 150°C; preferably from 60° to 100°C, it is operated at atmospheric pressure or higher. The catalysts can be precontacted with small amounts of olefins (prepolymerization). The prepolymerization improves the performance of the catalysts as well as the morphology of the polymers. The prepolymerization is carried out maintaining the catalyst in suspension in a hydrocarbon solvent (hexane, heptane, etc.) and it is polymerized at a temperature from room temperature to 60°C producing an amount of polymer generally from 0.5 to 3 times the weight of the catalyst. It can also be carried out in liquid propylene, under the temperature conditions indicated above, and producing amounts of polymer which can reach 1000 g per g of catalyst component. In the case of stereoregular polymerization of olefins,the molar ratio between Al-alkyl compound and electron-donor compound is usually from 5:1 to 100:1. The following examples are provided to illustrate and not to limit the invention. EXAMPLES 1-6 1000 ml of n-heptane, 5 mmoles of Al(C 2 H 5 ) 3 , 30 mg of catalyst component and 1 mmole of an electron-donor compound are introduced in propylene gas stream at 25°C in a 2000 ml stainless steel autoclave with an anchor agitator. The autoclave is closed and the pressure brought to 1 bar (1 atm) by feeding propylene, after which a hydrogen overpressure of to 0.2 bar (0.2 atm) is introduced. Then the contents are heated to 70°C and the total pressure is brought to 7 bar (7 atm) with propylene. The polymerization reaction is continued for 2 hours while the monomer is fed continuosly. The polymer obtained is then isolated by filtration. The polymer remaining in the filtrate is precipitated with methanol, vacuum dried and considered in determining the total residue of the n-heptane extraction. The electron-donors used, the polymerization yields and the properties of the polymers obtained are shown in Table 1. The catalyst component used is prepared as follows. In a 500 ml reactor equipped with a filtering baffle 225 ml of TiCl 4 are introduced at 0°C . While agitating, 10.1 g (54 mmoles) of microspheroidal MgCl 2 .2,1C 2 H 5 OH, obtained according to the method of example 1 of US 4,469,648, are added over 15 minutes. Once the addition is completed, the temperature is brought to 40°C and 9 mmoles of diisobutylphthalate are introduced. The temperature is brought to 100°C in 1 hour and it is reacted for 2 hours after which the TiCl 4 is removed by filtration, then another 200 ml of TiCl 4 are added and it is reacted at 120°C for 1 hour; the mixture product is filtered and washed at 60°C with n-heptane until no chlorine ions remain in the filtrate. Ex. no. Donor used Yield gPP/g cat.comp. I.I. % I.V. dl/g 1 methyl-phenyl-dimethoxymethylsilane 1000 92.7 1.60 2 diphenyl-dimethoxymethylsilane 5000 95.3 1.50 3 methyl-cyclohexyl-dimethoxymethylsilane 3800 92.8 1.38 4 di-tert-butyl-dimethoxymethylsilane 3500 92.7 1.30 5 cyclohexyl-tert-butyl-dimethoxymethylsilane 5500 94.2 1.55 6 isopropyl-tert-butyl-dimethoxymethylsilane 4800 95.5 1.50

Claims: A catalyst for the polymerization of olefins comprising the product of the reaction of an Al-trialkyl compound and a silicon compound having the formula where R 1 and R 2 are the same or different and are linear or branched C 1-18 alkyl, C 3-18 cycloalkyl, C 6-18 aryl, C 7-18 alkaryl, or C 7-18 aralkyl radicals, optionally containing O, N, S, P, or halogen, and R 3 and R 4 are the same or different and are linear or branched C 1-18 alkyl, C 3-18 cycloalkyl, C 6-18 aryl, C 7-18 alkaryl, or C 7-18 aralkyl radicals, with a solid catalyst component comprising a magnesium halide in active form, a titanium halide or alkoxy titanium halide and an electron-donor compound at least 70mol% of which is extractable with Al-triethyl under standard extraction conditions, wherein the solid component, after extraction, has a surface area greater than 10 m 2 /g. The catalyst of claim 1, where the electron-donor compound present in the solid component is a phthalic acid ester. The catalyst of claim 2, where the silicon compound is diphenyldimethoxymethylsilane, cyclohexyl-tert-butyldimethoxymethylsilane or isopropyl-tert-butyl-dimethoxymethylsilane.

Inventors: ALBIZZATI ENRICO DR, BARBASSA ELISABETTA DR, BARINO LUISA DR, GIANNINI UMBERTO DR, MORINI GIAMPIERO DR, SCORDAMAGLIA RAIMONDO DR, ALBIZZATI, ENRICO, DR., BARBASSA, ELISABETTA, DR., BARINO, LUISA, DR., GIANNINI, UMBERTO, DR., MORINI, GIAMPIERO, DR., SCORDAMAGLIA, RAIMONDO, DR.
Applicants: MONTELL NORTH AMERICA INC, MONTELL NORTH AMERICA INC.
Application year: 1991
Main classification: C08F4
IPC codes: C08F10