Polymers of carbon monoxide with styrene

Abstract: Novel linear alternating polymers of carbon monoxide with styrene and/or with one or more substituted styrenes, having a number average molecular weight above 30,000, can be prepared by polymerizing the monomers using a catalyst composition based upon: a) a Group VIII metal compound, b) a nitrogen bidentate ligand with the general formula in which X and Y represent identical or different organic bridging groups which each contain three or four atoms in the bridge, of which at least two are carbon atoms, c) an acid with a pKa < -3, and d) an organic oxidizing agent.

Description: The invention relates to novel polymers of carbon monoxide with styrene and/or with one or more substituted styrenes. It is known that linear polymers of carbon monoxide with one or more olefinically unsaturated aliphatic compounds in which polymers the units from carbon monoxide on the one hand and the units from the olefinically unsaturated compounds on the other hand are present in a substantially alternating arrangement can be prepared by contacting the monomers at elevated temperature and pressure with a catalyst composition on the basis of a Group VIII metal compound, a phosphorus bidentate ligand, an acid with a pKa < 2 and an organic oxidizing agent. For some applications it may be desirable to have such linear alternating polymers in which optionally substituted phenyl groups occur as side groups linked to the main chains. Attempts, using the above-mentioned catalyst compositions, to prepare such polymers from a monomer mixture that besides carbon monoxide contains styrene and/or one or more substituted styrenes have had little success up to now. Although these catalyst compositions are eminently suitable for the preparation of linear alternating polymers of carbon monoxide with one or more olefinically unsaturated aliphatic compounds, they have been found rather unsuitable for the preparation of linear alternating polymers of carbon monoxide with styrene and/or with one or more substituted styrenes. In the course of investigations concerning these polymers carried out by the applicant some time ago it was found that starting from monomer mixtures which besides carbon monoxide contain styrene and/or one or more substituted styrenes, linear alternating polymers can be prepared, provided that the phosphorus bidentate ligand in the above described catalyst compositions is replaced by one of the following three bidentate ligands: 1) a nitrogen bidentate ligand with the general formula wherein X and Y represent identical or different organic bridging groups which each contain three or four atoms in the bridge, at least two of which are carbon atoms, 2) a sulphur bidentate ligand with the general formula (R 1 )S-R-S(R 2 ) in which R 1 and R 2 represent identical or different optionally polar-substituted hydrocarbyl groups and R is a divalent organic bridging group containing at least two carbon atoms in the bridge, and 3) a nitrogen bidentate ligand in which a (R 3 )N group occurs, the nitrogen atom of which is connected solely via a non-aromatic double bond with a carbon atom of a hydrocarbon bridging group R 4 and in which moreover either a (R 5 )N group occurs, the nitrogen atom of which is connected via a double bond with a carbon atom of the bridging group R 4 , or a (R 5 ) (R 6 )N group, the nitrogen atom of which is connected via a single bond with a carbon atom of the bridging group R 4 , wherein in the above-mentioned groups R 3 represents a monovalent hydrocarbyl group and R 5 and R 6 are identical or different hydrocarbyl groups, optionally the same as R 3 . In the polymer preparations carried out until recently (cf. for example EP-A-229408), use was made of, inter alia, catalyst compositions which contained one of the following bidentate ligands: 2,2'-bipyridyl, 1,10-phenanthroline, 1,2-bis(ethylthio)ethane, cis-1,2-bis(benzylthio)ethene and bis(cyclohexylimino)ethane. Trifluoroacetic acid or para-toluenesulphonic acid were used as acids. The quantity of organic oxidizing agent in the catalyst compositions was 100-300 mol per g.atom Group VIII metal. The above-mentioned polymerizations were performed at a temperature selected between 50 and 100°C so as to satisfy the practical requirement that the resulting reaction rate should be at least 50 g polymer/(g Group VIII metal.hour). Polymers were obtained from these polymerizations having a number average molecular weight ( M n ) of less than 20,000. For some applications it may be desirable to have such polymers with an M n of above 30,000. An investigation has now been carried out by the applicant concerning the preparation of these polymers. This showed that it is not possible to prepare such polymers at an acceptable reaction rate using the above-mentioned catalyst compositions. Although it is possible, by reducing the reaction temperature, to obtain some increase in the M n of the polymers, this is accompanied by such a sharp reduction in the reaction rate that very soon the requirement of 50 g/(g.hour) is no longer satisfied. In general, it can be stated that with the catalyst compositions used to date it has not appeared possible to prepare linear alternating polymers of carbon monoxide with styrene and/or with one or more substituted styrenes, both at a reaction rate of least 50 g/(g.hour), and having an M n above 30,000. However, it has now surprisingly been found that both previously mentioned criteria can be satisfied if a catalyst composition is used which contains a nitrogen bidentate ligand mentioned under 1) and an acid with a pKa < -3. Polymers of the present type with an M n above 30,000 have utility as thermoplastics of good processability. The patent application relates to a process for the preparation of linear polymers of carbon monoxide with styrene and/or with one or more substituted styrenes in which polymers the units from carbon monoxide on the one hand and the units from the styrene monomers on the other hand are present in a substantially alternating order and which polymers have an M n above 30,000, by contacting the monomers at elevated temperature and pressure with a catalyst composition on the basis of a) a Group VIII metal compound, b) a nitrogen bidentate ligand with the general formula wherein X and Y are as defined hereinbefore, c) an acid with a pKa < -3, and d) an organic oxidizing agent in a quantity of 2.5-30 mol per g.atom of Group VIII metal. The patent application further relates to the polymers obtainable by the invented process, on the understanding that in said process trifluoromethanesulphonic acid is used as the acid with a pKa < -3. Preferably the polymers have an M n of at least 33,000 and in particular above 50,000. Finally the patent application relates to the catalyst compositions which can be applied in the invented process. As substituted styrenes which can be used in the preparation of the polymers according to the invention, compounds are eligible which consist solely of carbon and hydrogen such as 2-methylstyrene, 4-methylstyrene and 4-ethylstyrene, as well as compounds which besides carbon and hydrogen also contain one or more heteroatoms such as 4-methoxystyrene and 4-chlorostyrene. The invention is of particular interest for the preparation of high molecular weight copolymers of carbon monoxide with styrene. In this patent application, Group VIII metals are understood to be the noble metals ruthenium, rhodium, palladium, osmium, iridium and platinum, as well as the iron group metals iron, cobalt and nickel. In the catalyst compositions used in the polymer preparation according to the invention the Group VIII metal is preferably selected from palladium, nickel and cobalt. Palladium is particularly preferred as Group VIII metal. The incorporation of the Group VIII metal in the catalyst compositions preferably takes place in the form of a salt of a carboxylic acid, in particular in the form of an acetate. In the nitrogen bidentate ligands which are eligible for use as component b) in the catalyst compositions, the bridging groups X and Y are connected with each other via the two carbon atoms depicted in the general formula. Besides this connection, there may additionally exist between the bridging groups X and Y a second connection like in 1,10-phenanthroline and derivatives. If the bridging groups X and Y also contain other atoms in the bridge besides carbon atoms, these atoms are preferably nitrogen atoms. There is additionally preference for nitrogen bidentate ligands in which the bridging groups X and Y are identical. Examples of suitable nitrogen bidentate ligands are 2,2'-bipyridyl and derivatives like 3,3'-azo-2,2'-bipyridyl and 4,4'-dimethyl-2,2'-bipyridyl, 1,10-phenanthroline and derivatives like 4,7-dimethyl-1,10-phenanthroline, and also 2,2'-biquinolyl and 2-(2-pyridyl)benzimidazole. The use of 2,2'-bipyridyl and 1,10-phenanthroline as component b) is preferred. The nitrogen bidentate ligand is preferably present in the catalyst compositions in a quantity of 0.5-100 and in particular 1-50 mol per g.atom Group VIII metal. The acids which are eligible for use as component c) in the catalyst compositions should have a pKa < -3. Examples of such very strong acids are tetrafluoroboric acid (HBF 4 ), hexafluorophosphoric acid (HPF 6 ), hexafluoroantimonic acid (HSbF 6 ), hexafluorosilicic acid (H 2 SiF 6 ), para-nitrobenzenesulphonic acid (p-O 2 N-C 6 H 4 -SO 3 H), trifluoromethanesulphonic acid (F 3 C-SO 3 H), methyl bisulphate (CH 3 O-SO 3 H), sulphuric acid (H 2 SO 4 ) and fluorosulphurous acid (FSO 3 H). The use of trifluoromethanesulphonic acid as component c) is preferred. The acid is preferably present in the catalyst compositions in a quantity of 1-100 and in particular 2-50 mol per g.atom Group VIII metal. Besides the components a)-c) the catalyst compositions should contain as component d) an organic oxidizing agent. Examples of suitable organic oxidizing agents are 1,2- and 1,4-quinones, aliphatic nitrites such as butyl nitrite and aromatic nitro compounds such as nitrobenzene and 2,4-dinitrotoluene. 1,4-benzoquinone or 1,4-naphthoquinone is preferably used as component d). As mentioned above, for the preparation of linear alternating polymers of carbon monoxide with styrene and/or with one or more substituted styrenes with an M n < 20,000, catalyst compositions were used in the past which contained 100-300 mol organic oxidizing agent per g.atom Group VIII metal. In the applicant's research that led to the invention to which the present patent application relates, it has surprisingly been found that the use of such large quantities of organic oxidizing agent in the catalyst compositions is by no means necessary. It has been discovered that a drastic reduction in the quantity of organic oxidizing agent in the catalyst compositions leads to a substantial increase in the M n of the prepared polymers. On the basis of the results of this research there is preference, in the preparation of the present high molecular weight polymers, for catalyst compositions containing 5-25 mol organic oxidizing agent per g.atom Group VIII metal. The preparation of the polymers according to the invention is preferably carried out by contacting the monomers with a solution of the catalyst compositions in a diluent in which the polymers are insoluble or virtually insoluble. Lower aliphatic alcohols such as methanol are very suitable as diluents. In the applicant's research that led to the invention to which the present patent application relates it has surprisingly been found that the quantity of water present in the reactor has an influence on the M n of the prepared polymers. It has been found that in the preparation of linear alternating polymers of carbon monoxide with styrene and/or with one or more substituted styrenes polymers with a higher M n are obtained the less water is present in the reactor. The water that may be present in the reactor can result from the use of water-containing styrene or water-containing substituted styrenes or by the use of a water-containing diluent such as water-containing methanol. From the research carried out by the applicant it has been found that, if no special precautions are taken, the polymerization mixture contains more than 100 ppmw water. On the basis of the results of the research, there is preference in the preparation of the present high-molecular weight polymers for the use of mixtures to be polymerized which preferably contain less than 50 and in particular less than 25 ppmw water. This low water content can be achieved by using carefully dried starting materials, in particular dried styrene and/or dried substituted styrenes and, if a diluent is used, also drying this beforehand. A simpler solution to this problem is to perform the drying in situ by adding, before polymerization, a drying agent to the mixture to be polymerized. A mixture of trimethyl orthoformate (trimethoxymethane) and para-toluenesulphonic acid has been found to be very suitable for this purpose. The quantity of catalyst composition used in the preparation of the polymers can vary within wide limits. Per mol of styrene and/or substituted styrene to be polymerized, a quantity of catalyst composition is preferably used which contains 10 -7 -10 -3 and in particular 10 -6 -10 -4 g.atom Group VIII metal. The preparation of the polymers is preferably carried out at a temperature of 25-150°C and a pressure of 2-150 bar and in particular at a temperature of 30-120°C and a pressure of 5-100 bar. The polymers according to the invention can be prepared both batchwise and continuously. If desired, the polymer preparation can also be carried out in the gaseous phase, i.e. in the absence of a liquid diluent. The invention will be illustrated further by the following examples: Example 1 A carbon monoxide/styrene copolymer was prepared as follows. Into a stirred autoclave with a volume of 300 ml which contained 100 ml styrene a catalyst solution was introduced consisting of: 20 ml methanol, 0.2 mmol palladium acetate, 4.4 mmol 2,2'-bipyridyl, 6.0 mmol para-toluenesulphonic acid, and 20.0 mmol 1,4-naphthoquinone. After removing air from the autoclave, 40 bar carbon monoxide was forced in. The temperature was then raised to 70°C. The pressure was kept constant during polymerization by forcing in carbon monoxide. After 5 hours the polymerization was terminated by cooling to room temperature and releasing the pressure. The polymer was filtered off, washed with methanol and dried. 42.0 g copolymer with an M n of 10,100 was obtained. The polymerization rate was 395 g copolymer/(g palladium.hour). Example 2 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) the reaction temperature was 46°C instead of 70°C, and b) the reaction time was 18 hours instead of 5 hours. 13.7 g copolymer with an M n of 19,000 was obtained. The polymerization rate was 36 g copolymer/(g palladium.hour). Example 3 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 1.3 mmol 2,2'-bipyridyl, 1.7 mmol para-toluenesulphonic acid, and 9.5 mmol 1,4-naphthoquinone, b) after addition of the catalyst solution, the water content of the autoclave contents was reduced from > 200 ppmw to < 25 ppmw by addition of 18 mmol trimethyl orthoformate and 0.01 mmol para-toluenesulphonic acid, and c) the reaction time was 3.6 hours instead of 5 hours. 14.3 g copolymer with an M n of 11,600 was obtained. The polymerization rate was 622 g copolymer/(g palladium.hour). Example 4 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 1.9 mmol 2,2'-bipyridyl, 1.25 mmol para-toluenesulphonic acid, and 9.5 mmol 1,4-naphthoquinone, b) after addition of the catalyst solution, the water content of the autoclave contents was reduced from > 200 ppmw to < 25 ppmw by addition of 35 mmol trimethyl orthoformate and 0.02 mmol para-toluenesulphonic acid, c) the reaction temperature was 72°C instead of 70°C, and d) no carbon monoxide was forced in during the polymerization. 26.6 g copolymer with an M n of 13,000 was obtained. The polymerization rate was 833 g copolymer/(g palladium.hour). Example 5 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 1.9 mmol 2,2'-bipyridyl, 1.25 mmol para-toluenesulphonic acid, and 1.3 mmol 1,4-naphthoquinone, b) the water content was reduced to < 25 ppmw as in example 3, c) the reaction time was 6 hours instead of 5 hours, and d) no carbon monoxide was forced in during the polymerization. 15.2 g copolymer with an M n of 16,000 was obtained. The polymerization rate was 396 g copolymer/(g palladium.hour). Example 6 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 1.9 mmol 2,2'-bipyridyl, 1.25 mmol para-toluenesulphonic acid, and 0.6 mmol 1,4-naphthoquinone, b) the water content was reduced to < 25 ppmw as in example 3, and c) no carbon monoxide was forced in during the polymerization. 8.9 g copolymer with an M n of 18,300 was obtained. The polymerization rate was 278 g copolymer/(g palladium.hour). Example 7 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) the catalyst solution contained 6.0 mmol trifluoromethanesulphonic acid instead of para-toluenesulphonic acid, b) the reaction temperature was 71°C instead of 70°C, and c) the reaction time was 2.9 hours instead of 5 hours. 37.7 g copolymer with an M n of 31,000 was obtained. The polymerization rate was 611 g copolymer/(g palladium.hour). Example 8 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 0.31 mmol 2,2'-bipyridyl, 1.13 mmol trifluoromethanesulphonic acid, and 0.63 mmol 1,4-naphthoquinone, b) 42 bar carbon monoxide was forced into the autoclave instead of 40 bar, c) the reaction temperature was 52°C instead of 70°C, d) the reaction time was 14.6 hours instead of 5 hours, and e) no carbon monoxide was forced in during the polymerization. 7.8 g copolymer with an M n of 38,500 was obtained. The polymerization rate was 84 g copolymer/(g palladium.hour). Example 9 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 8, but with the following differences: a) the water content was reduced to < 25 ppmw as in example 3, b) 39 bar carbon monoxide was forced into the autoclave instead of 42 bar, c) the reaction time was 14.3 hours instead of 14.6 hours. 8.2 g copolymer with an M n > 50,000 was obtained. The polymerization rate was 90 g copolymer/(g palladium.hour). Example 10 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 1.9 mmol 2,2'-bipyridyl, 1.25 mmol trifluoromethanesulphonic acid, and 9.5 mmol 1,4-naphthoquinone, b) the water content was reduced to < 25 ppmw as in example 3, c) the reaction temperature was 51°C instead of 70°C, and d) the reaction time was 15.4 hours instead of 5 hours. 6.3 g copolymer with an M n of 32,000 was obtained. The polymerization rate was 64 g copolymer/(g palladium.hour). Example 11 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 1.9 mmol 2,2'-bipyridyl, 1.25 mmol trifluoromethanesulphonic acid, and 0.63 mmol 1,4-naphthoquinone, b) the water content was reduced to < 25 ppmw as in example 3, c) the reaction temperature was 50°C instead of 70°C, and d) the reaction time was 12.2 hours instead of 5 hours. 8.1 g copolymer with an M n of 40,000 was obtained. The polymerization rate was 104 g copolymer/(g palladium.hour). Example 12 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 0.31 mmol 2,2'-bipyridyl, 1.13 mmol trifluoromethanesulphonic acid, and 0.63 mmol 1,4-naphthoquinone, b) the water content was reduced to < 25 ppmw as in example 3, c) the reaction temperature was 53°C instead of 70°C, and d) the reaction time was 12 hours instead of 5 hours. 4.2 g copolymer with an M n of 45,000 was obtained. The polymerization rate was 55 g copolymer/(g palladium.hour). Example 13 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol 0.06 mmol palladium acetate, 0.31 mmol 2,2'-bipyridyl, 0.25 mmol trifluoromethanesulphonic acid, and 0.63 mmol 1,4-naphthoquinone, b) the water content was reduced to < 25 ppmw as in example 3, c) the reaction temperature was 50°C instead of 70°C, and d) the reaction time was 15 hours instead of 5 hours. 6.2 g copolymer with an M n of 44,000 was obtained. The polymerization rate was 65 g copolymer/(g palladium.hour). Example 14 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 0.12 mmol 2,2'-bipyridyl, 0.12 mmol trifluoromethanesulphonic acid, and 0.63 mmol 1,4-naphthoquinone, b) the water content was reduced to < 25 ppmw as in example 3, c) the reaction temperature was 51°C instead of 70°C, and d) the reaction time was 14 hours instead of 5 hours. 7.2 g copolymer with an M n of 38,000 was obtained. The polymerization rate was 80 g copolymer/(g palladium.hour). Example 15 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 0.06 mmol 2,2'-bipyridyl, 0.06 mmol trifluoromethanesulphonic acid, and 0.63 mmol 1,4-naphthoquinone, b) the water content was reduced to < 25 ppmw as in example 3, c) the reaction temperature was 50°C instead of 70°C, and d) the reaction time was 14.9 hours instead of 5 hours. 5.0 g copolymer with an M n of 33,000 was obtained. The polymerization rate was 52 g copolymer/(g palladium.hour). Example 16 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) the catalyst solution was the same as that used in example 8, b) the water content was reduced to < 25 ppmw as in example 3, c) carbon monoxide was forced into the autoclave to a pressure of 20 bar instead of 40 bar, d) the reaction temperature was 50°C instead of 70°C, and e) the reaction time was 15.5 hours instead of 5 hours. 12.8 g copolymer with an M n > 50,000 was obtained. The polymerization rate was 129 g copolymer/(g palladium.hour). Example 17 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) the catalyst solution was the same as that used in example 8, b) the water content was reduced to < 25 ppmw as in example 3, c) carbon monoxide was forced into the autoclave to a pressure of 70 bar instead of 40 bar, d) the reaction temperature was 51°C instead of 70°C, and e) the reaction time was 15.6 hours instead of 5 hours. 5.7 g copolymer with an M n of 46,000 was obtained. The polymerization rate was 57 g copolymer/(g palladium.hour). Example 18 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 0.31 mmol 3,3'-azo-2,2'-bipyridyl, 0.31 mmol trifluoromethanesulphonic acid, and 0.63 mmol 1,4-naphthoquinone, b) the water content was reduced to < 25 ppmw as in example 3, c) the reaction temperature was 50°C instead of 70°C, and d) the reaction time was 15.4 hours instead of 5 hours. 9.3 g copolymer with an M n of 35,000 was obtained. The polymerization rate was 92 g copolymer/(g palladium.hour). Example 19 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 0.31 mmol 2,2'-bipyridyl, 1.13 mmol hexafluorophosphoric acid, and 0.63 mmol 1,4-naphthoquinone, b) the water content was reduced to < 25 ppmw as in example 3, c) the reaction temperature was 50°C instead of 70°C, and d) the reaction time was 15 hours instead of 5 hours. 5.0 g copolymer with an M n of 31,000 was obtained. The polymerization rate was 51 g copolymer/(g palladium.hour). Example 20 A carbon monoxide/styrene copolymer was prepared in substantially the same way as in example 1, but with the following differences: a) a catalyst solution was used consisting of: 20 ml methanol, 0.06 mmol palladium acetate, 0.31 mmol 2,2'-bipyridyl, 1.13 mmol sulphuric acid, and 0.63 mmol 1,4-naphthoquinone, b) the water content was reduced to < 25 ppmw as in example 3, c) the reaction temperature was 50°C instead of 70°C, and d) the reaction time was 15 hours instead of 5 hours. 7.3 g copolymer with an M n of 33,000 was obtained. The polymerization rate was 74 g copolymer/(g palladium.hour). Of the examples 1-20, examples 8,9 and 11-20 are according to the invention. In these examples, using catalyst compositions containing as component c) an acid with a pKa < -3, carbon monoxide/styrene copolymers were prepared with an M n > 30,000 at a polymerization rate > 50 g copolymer/(g palladium.hour). Examples 1-7 and 10 have been included for comparison. In examples 1-6, using catalyst compositions containing as component c) an acid with a pKa > -3, carbon monoxide/styrene copolymers were prepared with an M n < 20,000. Comparing the results of examples 1 and 2, carried out using a catalyst composition containing as component c) an acid with a pKa > -3, it can be seen that, although reducing the reaction temperature from 70 to 46°C caused an increase of the M n from 10,100 to 19,000, this increase was accompanied by a decrease in the polymerization rate to a value beneath the practical limit of 50 g/(g.hour). The favourable influence on the M n of the prepared polymers of drying the reactor contents can be seen by comparison of the result of example 8 (without drying: M n = 38,500) with that of example 9 (with drying: M n > 50,000) and by comparison of the result of example 1 (without drying: M n = 10,100) with those of examples 3 and 4 (with drying: M n = 11,600 and M n = 13,000 respectively). The favourable influence of a low molecular ratio of 1,4-naphthoquinone/palladium acetate on the M n of the prepared polymers can be seen by comparison of the result of example 10 (ratio 158: M n = 32,000) with that of example 11 (ratio 11: M n = 40,000) and by comparison of the result of example 4 (ratio 158: M n = 13,000) with those of examples 5 and 6 (ratios 22 and 10 respectively: M n = 16,000 and 18,300 respectively). It was established by 13 C-NMR that the polymers prepared according to examples 1-20 were built up of linear chains in which the units from carbon monoxide on the one hand and the units from styrene on the other hand occurred in an alternating arrangement. The molecular weights were determined by gel permeation chromatography, and by 13 C-NMR (analysing the ratio of end groups to chain groups).

Claims: Claims for the following Contracting States : AT, BE, CH, LI, DE, DK, FR, GB, GR, IT, LU, NL, SE Process for the preparation of linear polymers of carbon monoxide with styrene and/or with one or more substituted styrenes in which polymers the units from carbon monoxide and the units from the styrene monomers occur in a substantially alternating order and which polymers have an M n above 30,000 in which process a mixture of carbon monoxide with styrene and/or with one or more substituted styrenes is contacted at elevated temperature and pressure with a catalyst composition on the basis of: a) a Group VIII metal compound, b) a nitrogen bidentate ligand with the general formula in which X and Y represent identical or different organic bridging groups which each contain three or four atoms in the bridge, of which at least two are carbon atoms, c) an acid with a pKa < -3, and d) an organic oxidizing agent in a quantity of 2.5-50 mol per g.atom of Group VIII metal. Process according to claim 1, characterized in that carbon monoxide/styrene copolymers are prepared. Process according to claim 1 or 2, characterized in that the catalyst composition contains palladium as Group VIII metal. Process according to one or more of claims 1-3, characterized in that the catalyst composition contains as component b) a nitrogen bidentate ligand in which the bridging groups X and Y are identical, such as 2,2'-bipyridyl or 1,10-phenanthroline. Process according to one or more of claims 1-4, characterized in that the catalyst composition contains as component c) trifluoromethanesulphonic acid. Process according to one or more of claims 1-5, characterized in that the catalyst composition contains as component d) a 1,4-quinone such as 1,4-benzoquinone or 1,4-naphthoquinone. Process according to one or more of claims 1-6, characterized in that the catalyst composition contains 0.5-100 mol component b) and 1-100 mol component c) per g.atom Group VIII metal. Process according to one or more of claims 1-7, characterized in that the catalyst composition contains 5-25 mol component d) per g.atom Group VIII metal. Process according to one or more of claims 1-8, characterized in that the mixture to be polymerized contains less than 50 ppmw water. Process according to one or more of claims 1-9, characterized in that the polymerization is carried out at a temperature of 25-150 °C and a pressure of 2-150 bar and that per mol of styrene and/or substituted styrene to be polymerized a quantity of catalyst composition is used which contains 10 -7 -10 -3 g.atom Group VIII metal. Polymers obtainable by a process as claimed in claims 1 and 5. Polymers as claimed in claim 11, characterized in that they have an M n of at least 33,000. Polymers according to claim 12, characterized in that they have an M n above 50.000. Catalyst compositions as defined in one or more of claims 1 and 3-8. Claims for the following Contracting State : ES Process for the preparation of linear polymers of carbon monoxide with styrene and/or with one or more substituted styrenes in which polymers the units from carbon monoxide and the units from the styrene monomers occur in a substantially alternating order and which polymers have an M n above 30,000 in which process a mixture of carbon monoxide with styrene and/or with one or more substituted styrenes is contacted at elevated temperature and pressure with a catalyst composition on the basis of: a) a Group VIII metal compound, b) a nitrogen bidentate ligand with the general formula in which X and Y represent identical or different organic bridging groups which each contain three or four atoms in the bridge, of which at least two are carbon atoms, c) an acid with a pKa < -3, and d) an organic oxidizing agent in a quantity of 2.5-50 mol per g.atom of Group VIII metal. Process according to claim 1, characterized in that carbon monoxide/styrene copolymers are prepared. Process according to claim 1 or 2, characterized in that the catalyst composition contains palladium as Group VIII metal. Process according to one or more of claims 1-3, characterized in that the catalyst composition contains as component b) a nitrogen bidentate ligand in which the bridging groups X and Y are identical, such as 2,2'-bipyridyl or 1,10-phenanthroline. Process according to one or more of claims 1-4, characterized in that the catalyst composition contains as component c) trifluoromethanesulphonic acid. Process according to one or more of claims 1-5, characterized in that the catalyst composition contains as component d) a 1,4-quinone such as 1,4-benzoquinone or 1,4-naphthoquinone. Process according to one or more of claims 1-6, characterized in that the catalyst composition contains 0.5-100 mol component b) and 1-100 mol component c) per g.atom Group VIII metal. Process according to one or more of claims 1-7, characterized in that the catalyst composition contains 5-25 mol component d) per g.atom Group VIII metal. Process according to one or more of claims 1-8, characterized in that the mixture to be polymerized contains less than 50 ppmw water. Process according to one or more of claims 1-9, characterized in that the polymerization is carried out at a temperature of 25-150 °C and a pressure of 2-150 bar and that per mol of styrene and/or substituted styrene to be polymerized a quantity of catalyst composition is used which contains 10 -7 -10 -3 g.atom Group VIII metal. A process for preparing a catalyst composition containing components a), b), c) and d), and using quantities thereof, as defined in one or more of claims 1 and 3-8.

Inventors: DE JONG ABE WIBE, KEIJSPER JOHANNES JACOBUS, DE JONG, ABE WIBE, KEIJSPER, JOHANNES JACOBUS
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1991
Main classification: C08G67
IPC codes: C08G67