PROCESS FOR PRODUCING FORMED ACTIVE COKE FOR DESULFURIZATION AND DENITRIFICATION WITH HIGH DENITRIFICATION PERFORMANCE

Abstract: A process for producing formed active coke to be used in an apparatus for treating various stack gases and the like, which comprises reacting a dry formed active coke produced from coal with SO₃ at 100 to 300°C, followed by the heat treatment in an inert atmosphere at 300 to 600°C. The coke is suitably used in a moving-bed desulfurization and denitrification apparatus, because it is excellent in not only the resistances to pressure, wearing and impact but also desulfurization and denitrification performances. Since it has, in particular, a high denitrification performance, it is suitable for the denitrification of stack gas generated from a fluidized-bed boiler or cogenerated stack gas containing a reduced amount of SOx.

Description: This invention relates to formed activated coke for SOx and NOx removal, and especially to a production process of formed activated coke for SOx and NOx removal having high NOx-removing ability, said coke being excellent in pressure resistance, abrasion resistance and impact strength and hence usable in large-scale systems. As dry processes for removing NOx from flue gas, it is known to decompose NOx by bringing it into contact with a metallic catalyst at high temperatures in the presence of ammonia or to decompose or adsorb NOx by causing flue gas to pass through a layer of a carbonaceous adsorbent such as activated granular carbon in the presence or absence of ammonia. Among these processes, the process making use of the carbonaceous adsorbent is particularly preferred as a treatment process for a gas, which also contains SOx, such as combustion flue gas because the carbonaceous adsorbent also has excellent SOx-adsorbing ability. These carbonaceous materials are, however, somewhat inferior in NOx-removing ability to metallic catalysts, whereby various attempts have been made to improve their NOx-removing ability. For example, as methods for further improving the NOx-removing ability of a carbonaceous material such as activated carbon, there are methods in which the NOx-removing ability is improved by making a carbonaceous material carry a metal such as Ti, Cr, V, Fe or Cu or by treating a carbonaceous material with an oxidizing solution such as nitric acid, sulfuric acid or hydrogen peroxide or with an oxidizing gas such as O 2 , O 3 , SO 3 or NO in the presence of water vapor to oxidize and reactivate the carbonaceous material (U.S. Patent No. 4,210,628, etc.). From JP-A-56-45 745 and JP-A-58-122042 there is known to activate coke intended for NOx and SOx removal with sulphuric acid. Activated carbon has heretofore been used as a carbonaceous adsorbent for SOx and NOx removal. From a viewpoint different from conventional activated carbon, formed activated coke for SOx and NOx removal excellent especially in SOx- and NOx-removing ability has been developed recently (Japanese Patent Publication No. 51885/1987, etc.). The specific surface area of formed activated coke for SOx and NOx removal of this type is 30 m 2 /g or less, which is smaller compared with the specific surface area of activated carbon, and the pore distribution of the former is also different from that of the latter. For its high strength including high pressure resistance, abrasion resistance and impact strength, the formed activated coke for SOx and NOx removal is suited for use in the practice of a moving-bed or fluidized-bed process in an actual large-scale system while being repeatedly subjected to regeneration after adsorption. There is, however, an increasing demand for an improvement in the NOx-removing ability of even such activated coke. Treatment of formed activated coke for SOx and NOx removal by the process employed above for the improvement of the NOx-removing ability of activated carbon is, however, accompanied by the drawback that, where the coke is metal-bearing activated coke, the metal is converted to a sulfate by SO 2 gas also contained in flue gas and the NOx-removing ability gradually decreases. Further, the oxidizing and reactivating method making use of an oxidizing solution is difficult to effect activation to the interiors of pores so that the oxidizing treatment has to be repeated to significantly improve the NOx-removing activity. In the case of oxidation and activation by an oxidizing gas, on the other hand, it is observed that activation proceeds to the interiors of pores and the NOx-removing ability can be effectively improved. The strength of the resulting activated coke has, however, been reduced, leading to the problem that it can no longer withstand repeated use in an SOx- and NOx-removing system of the moving bed type. It has therefore been found necessary to develop a new treatment method, which is different from those applied to conventional activated carbon, in order to improve the NOx-removing ability of the formed activated coke for SOx and NOx removal described above. An object of this invention is to overcome the above-described drawbacks of the conventional art and to provide an improved process for the production of formed activated coke for SOx and NOx removal having high strength and excellent NOx-removing ability. According to one aspect of the invention there is provided a process for the production of formed activated coke for SOx and NOx removal as set out in claim 1 According to another aspect of this invention there is provided a process for the production of formed activated coke for SOx and NOx removal having high NOx-removing ability, which comprises charging a formed activated coke, which has been produced using coal as a raw material and has been dried to have a water content of not higher than 1 wt.%, in a reactor; as a first step, causing a dried gas, which has been diluted with an inert gas and contains 2-10 vol.% of SO 3 , to pass at a temperature not higher than 250°C for at least 1 hour at an SV value of 300-6000 hr -1 through a layer of the activated coke so that SO 3 gas is adsorbed on the formed activated coke and is allowed to react with the formed activated coke to a certain extent; and, as a second-stage reaction, causing a gas, which has been diluted with an inert gas and contains 2-10 vol.% of SO 3 , to pass at a temperature not higher than 300°C, preferably 100-300°C, more preferably 150-250°C at an SV value of 100-1000 hr -1 for 4 hours or longer so that the SO 3 is reacted, and then subjecting the formed activated carbon to heat treatment at a temperature of 300-600°C in an inert atmosphere. According to another aspect of this invention there is provided a process for the production of formed activated coke for SOx and NOx removal having high NOx-removing ability, which comprises providing a reactor having an upper chamber of a small volume disposed above a lower chamber of a large volume with a flow passage for formed activated coke interposed therebetween, feeding formed activated coke to have a water content of not higher than 1 wt.% to the upper chamber and guiding the formed activated coke out of a system from the lower chamber by way of the flow passage, feeding an SO 3 -containing dried gas first into the lower chamber to cause the gas to flow through a layer of the formed activated coke in the lower chamber as a crossflow relative to the flow of the formed activated coke, then causing the gas to flow through a layer of the formed activated coke in the upper chamber as a crossflow relative to the flow of the formed activated coke, whereby SO 3 is reacted with the formed activated coke and removing SO 3 from the activated product. The processes of the present invention can efficiently produce formed activated coke for SOx and NOx removal, which has excellent pressure resistance, abrasion resistance and impact strength, is practically usable in large-scale systems, has high NOx-removing ability and is not available by any conventional process. Formed activated coke employed as a raw material in the present invention means a porous carbonaceous material having a specific surface area of 100-300 m 2 /g and obtained in a preliminary step by adding a caking additive to crushed coal as a primary raw material and then forming and carbonizing the resultant mass to activate the same or by using semi-coke, which has been obtained by carbonizing coal, as a primary raw material, crushing the semi-coke, adding coal or the like and a caking additive as auxiliary raw materials to the crushed semi-coke, forming the resultant mixture and then carbonizing the so-formed mixture to activate the same. To obtain high-performance, formed activated coke for SOx and NOx removal, in particular, it is preferred to use formed activated coke which has been obtained in a preliminary step by using semi-coke, which has been obtained by carbonizing coal, as a primary raw material, crushing the semi-coke, adding coal or the like and a caking additive as auxiliary raw materials to the crushed semi-coke, forming the resultant mixture and then carbonizing the so-formed mixture to activate the same. Although no particular limitation is imposed on the shape of the formed activated coke, those having a pellet-like shape of 3-20 mm in diameter and 5-25 mm in length are preferred for use in SOx- and NOx-removing systems of the moving bed type. In the carbonization step, pores are formed owing to evaporation of volatile components and activation also proceeds to some extent by gas and water vapor given off, whereby the specific surface area increases to provide formed activated coke whose specific surface area is 100-150 m 2 /g. The process of the present invention will hereinafter be described in detail in the order of its steps. Formed activated coke, which has been dried sufficiently to reduce its water content to 1 wt.% or lower, is first charged as a raw material in a reactor. In a temperature range not higher than 300°C, dried SO 3 -containing gas is caused to pass through the reactor so that SO 3 is reacted with the formed activated coke. If they are reacted quickly at this time, localized evolution of heat may take place, leading to the potential danger that the reaction may proceed out of control. It is therefore preferable to react them in two stages as will be described next. First, as a first stage, a gas diluted with an inert gas and containing 2-10 vol.% of SO 3 is caused to pass at a temperature not higher than 250°C and a high SV value of 3000-6000 hr -1 for 1 hour or longer through the layer of the formed activated coke, whereby SO 3 gas is adsorbed on the formed activated coke and is allowed to react to a certain extent. Next, as a second-stage reaction, a gas diluted with an inert gas and containing 2-10 vol.% of SO 3 is caused to pass at a temperature of 300°C or lower, preferably 100-300°C, more preferably 150-250°C and an SV value of 100-1000 hr -1 for 4 hours or longer so that SO 3 gas is allowed to react. If the SV value is smaller than 3000 hr -1 in the first-stage reaction, extraordinary evolution of heat tends to occur. If the SV value exceeds 6000 hr -1 , on the other hand, less SO 3 is adsorbed so that the effect is reduced. If the temperature is lower than 100°C in the second-stage reaction, the reaction is so slow that a lot of time is required, and SO 3 is adsorbed too much on the formed activated coke so that the resulting formed activated coke for SOx and NOx removal has reduced strength. Such low temperatures are therefore not preferred. On the other hand, temperatures higher than 300°C lead to a very high reaction velocity so that the reaction proceeds only on the surface of the formed activated coke. If the reaction temperature is shorter than 4 hours, activation does not proceed sufficiently to the inside of the formed activated coke so that the NOx-removing ability cannot be improved effectively to any significant extent. Such high temperatures are therefore not preferred. In the process of the present invention, it is necessary to use, as the formed activated coke as a raw material, one having a water content not higher than 1 wt.% and to react it with a dried SO 3 -containing gas. As the SO 3 gas, general SO 3 gas for industrial use can be used by diluting it as needed. A byproduced gas from one of various chemical processes such as a sulfuric acid production plant can also be used insofar as it does not contain water and other harmful substances which adversely affect properties of the formed activated coke. If the content of water in the formed activated coke as a raw material or in the reaction gas becomes higher, the resulting product has lowered strength and, especially, is prone to breakage so that the grain size is reduced. Such high water contents are therefore not preferred. The reaction between the formed activated coke and the SO 3 gas can be carried out by suitably combining a method and an apparatus, which are both employed for general solid-gas reactions. The common practice is, for example, to pass an SO 3 -containing gas through a reactor packed with formed activated coke and maintained at a suitable temperature. Continuous production is, however, feasible when a reactor having an upper chamber of a small volume disposed above a lower chamber of a large volume with a flow passage for formed activated coke interposed therebetween is provided, formed activated coke as a raw material is fed first to the upper chamber and then to the lower chamber through the flow passage, in other words, is caused to flow downwardly and is guided out of a system from the lower chamber, an SO 3 -containing gas is introduced first into the lower chamber to cause the gas to flow through the lower chamber as a crossflow relative to the flow of the formed activated coke, and the gas passed through the lower chamber is next fed to the upper chamber to cause it to flow through the upper chamber as a crossflow relative to the flow of the formed activated coke. This is especially suitable as a process according to this invention. According to this process, the upper chamber is designed small so that the residence time of the formed activated coke as the raw material in the upper chamber is relatively short and, moreover, the SO 3 -containing gas whose SO 3 concentration has become lower as a result of the reaction with the formed activated coke in the lower chamber passes at a high SV value. It is therefore possible to suppress any abrupt reaction between the formed activated coke and SO 3 , thereby making it possible to prevent localized occurrence of hot spots. In the lower chamber, the formed activated coke with SO 3 adsorbed in the upper chamber remains for a relatively long time so that the formed activated coke is brought into contact with an SO 3 -containing gas fed at a low SV value and having a relatively high SO 3 concentration. Since this allows the reaction to proceed sufficiently, a uniform and high-performance product can be obtained. In these reaction steps, the adsorption and desorption of SO 3 (SO 3 + C → SO 2 + C ··· O) repeatedly take place inside micropores in the surface of the formed activated coke whereby oxidation and activation of the formed activated coke proceed. If water is contained in the formed activated coke or SO 3 gas, the SO 3 gas turns to fuming sulfuric acid inside micropores of the formed activated coke and significantly reduces the strength of the formed activated coke. It is therefore necessary to sufficiently remove water in advance. As the formed activated coke reacted with SO 3 still carries extra SO 3 , the formed activated coke is heat-treated at 300-600°C under a stream of an inert gas such as nitrogen so as to desorb SO 3 . In the above heat treatment step, a reaction also takes place between the desorbed SO 3 gas and the formed activated coke so that the NOx-removing ability is improved further. A formed activated coke for SOx and NOx removal excellent in NOx-removing ability can therefore be obtained. By the reaction with SO 3 gas, the quantity of oxygen-containing functional groups on the surface of the formed activated coke is increased. Since these oxygen-containing functional groups significantly improve the ammonia-adsorbing capacity and NO-oxidizing activity of the formed activated coke, the NOx-reducing ability of the formed activated coke can be improved considerably. The formed activated coke for SOx and NOx removal obtained by the process of this invention has a specific surface area of 120-350 m 2 /g and possesses high strength and excellent SOx- and NOx-removing ability. It is therefore suitable for use in SOx- and NOx-removing system of the moving bed type. In particular, those obtained by conducting the reaction at 150-250°C, the preferred temperature range, have the excellent ability that their strength as measured by the measuring method to be described subsequently is 95% or higher and their SOx removal efficiency and NOx removal efficiency as measured under the measuring conditions to be set forth later are both 80% or higher. The formed activated coke for SOx and NOx removal can of course show excellent SOx- and NOx-removing effects when employed in a conventional SOx- and NOx-removing process and, owing especially to its feature of high NOx-removing ability, is also suited for the removal of NOx from flue gas of a fluidized-bed combustion boiler or a cogeneration power plant, said flue gas containing less SOx, thereby making it possible to reduce the size of the system. EXAMPLES The process of the present invention will hereinafter be described more specifically by the following examples, in which the measurements of the strength, SOx removal efficiency and NOx removal efficiency of each formed activated coke for SOx and NOx removal were conducted in accordance with the following methods, respectively. [Strength] The strength of each sample was measured using a Roga index tester employed in JIS M8801. Twenty grams of the sample were placed in a drum which had 30 mm wide baffle plates secured vertically in a symmetrical relationship at two places on the inner wall thereof and was 200 mm in inner diameter and 70 mm in depth. After the drum was rotated 1,000 times in the course of 20 minutes, the sample was sifted through a 6 mm sieve and the weight of the sample remaining on the sieve was measured. The strength of the sample was measured in accordance with the following equation: Strength (%) = Amount remaining on 6 mm sieve (g) ÷ 20 (g) x 100 [SO x -removing ability] Each sample was packed to the height of 125 mm in a glass cylinder having an inner diameter of 55 mm. A gas consisting of 1,000 ppm of SO 2 , 5% of O 2 , 7% of H 2 O and the balance of N 2 was caused to pass at 140°C and SV=400 hr -1 through the glass cylinder to determine the SO 2 removing efficiency. [NO x -removing ability] Each sample was packed to the height of 125 mm in a glass cylinder having an inner diameter of 55 mm. A gas consisting of 200 ppm of NO, 200 ppm of NH 3 , 5% of O 2 , 7% of H 2 O and the balance of N 2 was caused to pass at 140°C and SV=400 hr -1 through the glass cylinder to determine the NO removing efficiency. [Examples] Semi-coke which had been obtained by carbonizing coal was crushed, to which caking coal and a caking additive were added. The resulting mass was formed into a pellet-like shape to provide a forming raw material. The forming raw material was carbonized and activated into formed activated coke whose diameter, length, specific surface area and strength were about 10 mm, about 10-20 mm, about 170 m 2 /g and 96%, respectively. Using a fixed-bed flowing reactor, the formed activated coke was reacted with SO 3 gas under the conditions shown in Table 1. The reaction product was next heated at 400°C for 1 hour under a nitrogen gas stream so that the reaction product was subjected to heat treatment. The results are also given in Table 1. From the results of Table 1, it is understood that the SO 3 treatment by the process of this invention can significantly improve the NOx-removing ability without reduction of the strength of formed activated coke but, in the examples in which water was caused to exist in activated coke or SO 3 gas, the resultant products were substantially reduced in strength and only those unsuitable as formed activated coke for SOx and NOx removal were obtained. INDUSTRIAL APPLICABILITY The process of the present invention can efficiently produce formed activated coke for SOx and NOx removal, which has excellent pressure resistance, abrasion resistance and impact strength, is practically usable in large-scale systems, has high NOx-removing ability and is not available by any conventional process. The process of the present invention therefore has significant industrial utility. The formed activated coke for SOx and NOx removal obtained in accordance with the process of this invention has high strength and excellent SOx- and NOx-removing ability and, therefore, is suitable for use in moving-bed, SOx- and NOx-removing systems. The formed activated coke for SOx and NOx removal can of course show excellent SOx- and NOx-removing effects when employed in conventional SOx- and NOx-removing processes and, moreover, owing to its characteristic high NOx-removing ability, is suited for the removal of NOx from flue gas of a fluidized-bed combustion boiler or cogeneration power plant. As the size of an SOx- and NOx-removing system making use of a carbon material as a catalyst or an adsorbent is primarily governed by the NOx-removing ability of the carbon material, use of the formed activated coke for SOx and NOx removal produced in accordance with the process of this invention enables to substantially reduce the size of the system.

Claims: A process for the production of formed activated coke for SOx and NOx removal having high NOx-removing ability, which comprises reacting dried, formed, activated coke having a water content of not higher than 1 wt.% with dried SO 3 gas at 100 - 300°C, preferably 150 - 250°C; and then subjecting the reaction product to heat treatment at 300 - 600°C in an inert atmosphere. A process for the production of formed activated coke for SOx and NOx removal having high NOx-removing ability, which comprises placing formed activated coke, which has been prepared using coal as a raw material and has then been dried to have a water content of not higher than 1 wt.%, in a reactor; causing, as a first stage, a dried gas - which has been diluted with an inert gas and contains 2 - 10 vol.-% of SO 3 - to pass at a temperature not higher than 250°C and an SV value of 3,000 - 6,000 hr -1 through the reactor for at least one hour, whereby SO 3 gas is adsorbed on the formed activated coke and is allowed to partially react with the formed activated coke; causing, as a second stage, a dried gas - which has been diluted with an inert gas and contains 2 - 10 vol.-% of SO 3 - to pass at a temperature not higher than 300°C, preferably of 100 - 300°C, more preferably of 150 - 250°C and an SV value of 100 - 1,000 hr -1 through the reactor for at least four hours whereby SO 3 gas is allowed to react with the formed activated coke; and then subjecting the reaction product to heat treatment at 300 - 600°C in an inert atmosphere. A process for the production of formed activated coke for SOx and NOx removal having high NOx-removing ability, which comprises providing a reactor having an upper chamber of a small volume disposed above a lower chamber of a large volume with a flow passage for formed activated coke interposed therebetween, feeding formed activated coke having a water content of not higher than 1 wt.-% to the upper chamber and guiding the formed activated coke out of a system from the lower chamber by way of the flow passage, feeding an SO 3 -containing dried gas first into the lower chamber to cause the gas to flow through a layer of the formed activated coke in the lower chamber as a crossflow relative to the flow of the formed activated coke, then causing the gas to flow through a layer of the formed activated coke in the upper chamber as a crossflow relative to the flow of the formed activated coke, whereby SO 3 is reacted with the formed activated coke and removing SO 3 from the activated product. The process according to any one of claims 1, 2 and 3, wherein the formed activated coke is a porous carbon material having a specific surface area of 100 - 300 m 2 /g, said porous carbon material having been obtained in a preliminary step by using, as a primary raw material, semi-coke formed from coal by carbonization, crushing the semi-coke, adding as auxiliary raw materials coal and a caking additive to the thus-crushed semi-coke, forming the resultant mass and then carbonizing and activating the thus-formed mass in accordance with any of claims 1, 2 or 3. The process according to any one of claim 1, 2 3 and 4, wherein the formed activated coke is in a pellet-like form having a diameter of 3 - 20 mm and a length of 5 - 25 mm.

Inventors: MATSUFUJI YOSHIHIRO, NINAGAWA YASUHIKO, SHIRAISHI IKUO, TSUJI KAZUHIKO, MATSUFUJI, YOSHIHIRO, NINAGAWA, YASUHIKO, SHIRAISHI, IKUO, TSUJI, KAZUHIKO, MATSUFUJI, YOSHIHIRO, MITSUI MINING CO., LTD., NINAGAWA, YASUHIKO, MITSUI MINING CO. LTD. KYUSHU, SHIRAISHI, IKUO, MITSUI MINING CO., LTD. KYUSHU, TSUJI, KAZUHIKO, MITSUI MINING CO., LTD. KYUSHU
Applicants: MITSUI MINING CO LTD, MITSUI MINING COMPANY, LIMITED
Application year: 1991
Main classification: C01B31
IPC codes: C10L5, C01B31, C10L10, B01D53, B01J20