Fluoroelastomers based on vinylidene fluoride, hexafluoropropene and tetrafluoroethylene

Abstract: The invention relates to new fluoroelastomers endowed with both a low Tg and a low compression set at low temperature, characterized by the following monomeric composition: vinylidene fluoride: 60.5 to 64% by weight hexafluoropropene: 30 to 33% by weight tetrafluoroethylene: 5 to 8% by weight.

Description: The present invention relates to new fluoroelastomers, i.e., terpolymers of vinylidene fluoride, hexafluoropropene and tetrafluoroethylene. US-A-4,123,603 discloses elastomeric terpolymers having the following monomeric composition: vinylidene fluoride: 57 to 61% by weight hexafluoropropene: 27 to 31% by weight tetrafluoroethylene: 10 to 14% by weight. These terpolymers are endowed with a low glass transition temperature (Tg) and a low compression set at low temperature. The preferred product according to the above patent has the following monomeric composition by weight: 59% of vinylidene fluoride, 29% of hexafluoropropene and 12% of tetrafluoroethylene. The average Tg of four samples of this product is 24.75°C. The compression set of the above samples, after a 70-hour compression test at 0°C (according to ASTM-D 395, method B) is lower than or equal to 20%, when measured at room temperature within one hour after completion of the test. The above patent states and proves by means of several comparison examples that within the compositional range disclosed therein it is not possible to obtain, at the same time, a low Tg and a low compression set at low temperature. US-A-2,968,649 discloses an elastomeric terpolymer consisting of 3 to 35% by weight of tetrafluoroethylene units and 97 to 65% by weight of vinylidene fluoride and hexafluoropropene units, said vinylidene fluoride and hexafluoropropene units being present in a weight ratio within the range of 2.33:1.0 to 0.667:1.0. It has now surprisingly been found that there is another compositional range of terpolymers with which said two properties can be obtained simultaneously. Thus, it is an object of the present invention to provide new fluoroelastomers based on vinylidene fluoride, hexafluoropropene and tetrafluoroethylene which are simultaneously endowed with both a low Tg and a low compression set at low temperature. Another object is to provide fluoroelastomers of the above type which exhibit also a very low crystallinity, lower than that of the above known product, and low TR (temperature retraction) values. A further object is to provide fluoroelastomers of the above type which furthermore exhibit a higher vulcanization rate than that of the above known product. These and still other objects are achieved by the fluoroelastomers according to the present invention which are characterized by the following monomeric composition: vinylidene fluoride: 60.5 to 64% by weight hexafluoropropene: 30 to 33% by weight tetrafluoroethylene: 5 to 8% by weight. These fluoroelastomers are endowed with a glass transition temperature (Tg) which is lower than or equal to about -25°C and show a compression set, after a 70-hour compression test at 0°C on a disc (according to ASTM D 395, method B), lower than or equal to about 18%, when measured at 23°C after 30 minutes. Furthermore, they are endowed with a low crystallinity and low TR values. In addition they exhibit, as compared to the above known terpolymer, a higher vulcanization rate, which results in a higher productivity of the corresponding apparatus for the production of shaped articles. They are particularly suitable for those applications in which a low Tg and a low compression set at low temperature are required, in particular for the manufacture of O-rings and shaft seals. In these applications a lowering of the Tg and, even more important, of the TR values without adversely affecting the compression set values is a need particularly felt by the users, for which a gain of a few degrees centigrade represents substantial technological progress. The terpolymers according to the present invention may be prepared by means of known methods such as, for example, those described in Kirk Othmer, Encyclopaedia of Chemical Technology, vol. 8, pages 500 ff., 1979. Examples of suitable polymerization methods are, in particular, bulk polymerization, polymerization in a solution of organic solvents and polymerization in a water emulsion or suspension. Examples of suitable radical polymerization initiators are inorganic peroxides such as ammonium or potassium persulphates, redox systems such as persulphate-bisulphite and organic peroxides such as, for example, benzoyl peroxide and dicumyl peroxide. As chain transfer agents it is possible to use, for example, ethyl acetate and/or diethyl malonate. Preferably it is operated in an aqueous emulsion, at temperatures ranging from about 25 to about 150°C and under a pressure ranging from 8 to 80 x 10⁵ Pa (8 to 80 atmospheres). Another object of the present invention is represented by the articles manufactured from the terpolymers according to the present invention. The following examples are given for merely illustrative purposes and are not to be construed as being a limitation of the scope of the present invention. Examples 1 and 2 are within the compositional range of the present invention, while example 3 relates to the preferred composition of the above US-A-4,123,603. The preparation of the polymers by means of the emulsion polymerization process was carried out in a manner such as to achieve, for all elastomers of the present examples 1 to 3, the same average molecular weight (deduced from the Mooney viscosity ML (1+10) at 121°C and the intrinsic viscosity) and the same molecular weight distribution. Therefore, the chemico-physical properties indicated in Table 1 depend exclusively on the monomeric composition of the polymers. EXAMPLE 1 Employed was a 10-liter reactor equipped with stirrer. After vacuum had been applied 6,500 g of water were fed and pressure was generated in the reactor by means of a monomeric mixture having the following molar composition: vinylidene fluoride: 58% hexafluoropropene: 38% tetrafluoroethylene: 4% The reactor was heated up to 85°C, reaching a pressure of 19 bar. Then there were added 260 ml of ethyl acetate as an aqueous solution at 66 ml/l and 13 g of ammonium persulphate as an aqueous solution at 150 g/l. During polymerization, the pressure was maintained constant by feeding the monomers in the following molar ratio: vinylidene fluoride: 78.5% hexafluoropropene: 16.5% tetrafluoroethylene: 5% After obtainment of 2,800 g of polymer with a polymerization time of 55 minutes, the whole system was cooled to room temperature. The emulsion was discharged and then coagulated by addition of an aqueous aluminium sulphate solution. The polymer was separated, washed with water and dried in an air-circulation oven at 60°C until its water content was below 0.2% by weight. According to ¹⁹F-NMR analysis, the polymer exhibited the following monomeric composition: vinylidene fluoride: 63% by weight hexafluoropropene: 30.6% by weight tetrafluoroethylene: 6.4% by weight The polymer was subjected to several determinations and tests, which are reported in Table 1. A vulcanization blend was prepared by using a master batch M1 containing 50% of bisphenol AF and 50% of the fluoroelastomer and a master batch M2 containing 30% of an accelerator and 70% of the fluoroelastomer. The accelerator had the formula: The blend contained: terpolymer 100 parts by weight M1 4 parts by weight M2 1.5 parts by weight Ca(OH)₂ 6 parts by weight MgO 3 parts by weight MT black 25 parts by weight EXAMPLE 2 The procedure of example 1 was followed, except that the reactor was pressurized with the following monomeric mixture: vinylidene fluoride: 59% by mols hexafluoropropene: 36% by mols tetrafluoroethylene: 5% by mols During polymerization, the pressure was maintained constant by feeding the monomers in the following molar ratio: vinylidene fluoride: 77.2% hexafluoropropene: 16.5% tetrafluoroethylene: 6.3% There were obtained 2,800 g of a terpolymer which, according to ¹⁹F-NMR analysis, exhibited the following monomeric weight composition: vinylidene fluoride: 61.4% hexafluoropropene: 30.8% tetrafluoroethylene: 7.8% The terpolymer was subjected to the same determinations and tests as that of example 1. The results are reported in Table 1. EXAMPLE 3 For comparison purposes, the preferred terpolymer of US-A-4,123,603 was prepared. The modalities were identical with those of example 1, with the exception that: (a) the reactor was pressurized with a monomer mixture of the following molar composition: vinylidene fluoride: 56% hexafluoropropene: 36% tetrafluoroethylene: 8% (b) during polymerization, the pressure was maintained constant by feeding the monomers in the following molar ratio: vinylidene fluoride: 74.7% hexafluoropropene: 15.6% tetrafluoroethylene: 9.7% There were obtained 2,800 g of terpolymer which, according to ¹⁹F-NMR analysis, exhibited the following monomeric weight composition: vinylidene fluoride: 59.5% hexafluoropropene: 28.6% tetrafluoroethylene: 11.9% The results obtained with the above terpolymers and the products made therefrom are summarized in the following Table 1. From a comparison of results obtained with the terpolymers according to the present invention (examples 1 and 2) and with that of the art (example 3) the following can be derived: 1. the Tg and TR values of the products according to the present invention are as low as, and often lower than those of the known product; 2. the data relating to DH1+DH2 and DMS show that the products according to the present invention exhibit a lower crystallinity; 3. the compression set after compression tests at 0°C and 23°C is lower for the products of the present invention; 4. in spite of a lower tendency to scorch (see the Mooney Scorch data at 135°C; tΔ15), the vulcanization rate of the terpolymers according to the present invention is higher (see ODR data at 177°C:V max ). EXAMPLES 4 to 6 It was operated as in example 1, except that the reactor was pressurized with the following monomeric mixtures: Ex. 4 Ex. 5 Ex. 6 vinylidene fluoride 58.5% by mols 57 % by mols 57.5% by mols hexafluoropropene 36.5% by mols 38.5% by mols 39 % by mols tetrafluoroethylene 5 % by mols 4.5% by mols 5.5% by mols and except that, during the polymerization, the pressure was maintained constant by feeding the monomers in the following molar ratios: Ex. 4 Ex. 5 Ex. 6 vinylidene fluoride 76.7% by mols 77.8% by mols 78.2% by mols hexafluoropropene 17.5% by mols 17.0% by mols 17.2% by mols tetrafluoroethylene 5.8% by mols 5.2% by mols 4.6% by mols In each instance there were obtained 2800 g of terpolymer which, according to ¹⁹F-NMR analysis, exhibited the following weight composition: Ex. 4 Ex. 5 Ex. 6 vinylidene fluoride 61% by mols 62 % by mols 62.5% by mols hexafluoropropene 32% by mols 31.5% by mols 32 % by mols tetrafluoroethylene 7% by mols 6.5% by mols 5.5% by mols The terpolymers were subjected to the same determinations and tests as those of examples 1 to 3. The results are reported in Table 2.

Claims: Claims for the following Contracting States : AT, BE, CH, DE, FR, GB, IT, LI, NL, SE Fluoroelastomers having a low Tg and a low compression set at low temperature, characterized by the following monomeric composition: vinylidene fluoride: 60.5 to 64% by weight hexafluoropropene: 30 to 33% by weight tetrafluoroethylene: 5 to 8% by weight. Articles manufactured from a fluoroelastomer according to claim 1. Claims for the following Contracting State : ES Process for the preparation of fluoroelastomers having a low compression set at low temperature, characterized by the polymerization of vinylidene fluoride, hexafluoropropene and tetrafluoroethylene in relative amounts such as to result in a terpolymer having the following monomeric composition: vinylidene fluoride: 60.5 to 64% by weight hexafluoropropene: 30 to 33% by weight tetrafluoroethylene: 5 to 8% by weight Process according to claim 1 wherein the polymerization is a bulk polymerization, a polymerization in a solution of organic solvents or a polymerization in a water emulsion or suspension. Process according to claim 2 wherein the polymerization is carried out in an aqueous emulsion, at temperatures ranging from 25 to 150°C and under a pressure ranging from 8 to 80 x 10⁵ Pa (8 to 80 atmospheres). Articles manufactured from fluoroelastomers obtainable according to the process of any one of claims 1 to 3.

Inventors: ALBANO MARGHERITA, ARCELLA VINCENZO, BRINATI GIULIO, ALBANO, MARGHERITA, ARCELLA, VINCENZO, BRINATI, GIULIO
Applicants: AUSIMONT SPA, AUSIMONT S.P.A.
Application year: 1991
Main classification: C08F214
IPC codes: C08F214, C08F14