Metal mold with extended heat transfer surface

Abstract: A mold assembly for molding thermoplastic particles into a solid thin shell includes a metal shell (20) having a cavity (24) and including an outer surface (20b) exposed to a heat source and further including an inner surface (20a) on which thermoplastic material is cast and fused to form a thin layer thermoplastic shell. The heat transfer area of the metal shell is increased by providing a plurality of heat transfer pins (30) connected to the outer surface (20b); each of the heat transfer pins (30) has an extended outside surface area exposed to the heat source for heating said metal shell and each of said heat transfer pins further includes a large diameter head portion (30a) which is joined to the metal shell by a capacitive weld nugget (32a) formed solely between the large diameter head portion (30a) and the outer surface (20b) of the metal shell without disrupting the metal shell at surface portions thereof formed between the heat transfer pins (30).

Description: This invention relates to a mold assembly for molding thermoplastic particles into a solid thin shell the assembly including a metal shell (20) having a cavity and including an outer surface exposed (20b) to a heat source and further including an inner surface (20a) on which thermoplastic material is cast and fused to form a thin layer thermoplastic shell. More particularly, this invention relates to metal shell molds having an outer surface exposed to a heat source and an inner surface heated to a temperature at which heat gellable thermoplastic material deposited thereon will fuse into a thin, solid thermoplastic shell. A mold assembly of the type indicated above is known from US-A-4,621,995. Currently thermoplastic powder or thermoplastic slurries, known as dry or liquid plastisol, are cast on the inner surface of a thin metal mold member heated to the fusion temperature of the deposited material to form a gell coat which is cured to form a thin, solid thermoplastic shell. The thin metal mold member remains heated until a thin layer of thermoplastic material is built-up on the inner surface to form a thin plastic shell product suitable for use as an outer skin or shell covering on automotive interior products such as armrests, door panels, instrument panels and on automotive exterior products such as side rail bumpers, moldings or bumper fascias. Examples of such heated mold assemblies and processes are shown in US-A-3,680,629 and US-A-4,389,177. One form of heating is to direct hot gas over a flat outer surface of the heated mold to transfer heat into the metal of the mold for transfer therethrough into the thermoplastic material (sometimes referenced as plastisol material) to cause the plastisol (either wet or dry) to gel and cure. In the gel stage the plastisol is fused together into a thin layer of material. Thereafter the fused material is cured at an elevated temperature to form a finished product with desired physical characteristics. Examples of such gas heated molds are shown in US-A-4,621,995 and US-A-4,623,503. In the past it has been recognized that the heat transfer rate for directing heat from the heat source to the deposited plastisol could be improved by providing fins on the outer surface of the mold and flowing heated air across the fins to increase heat transfer to the plastisol. The fins provided increased heat transfer area for flow of heat from the heat source to the plastisol. The attachment of the fins, however, required soldering, brazing or welding steps that produce excessive heat flow into the thin metal shell of the mold. Such past practices can cause distortion or thermal cracks in the mold during fabrication. Additionally such attachment methods can cause degradation of the properties of the metal in the vicinity of the connections. An example of such property degradation is grain growth in the mold metal which makes the metal susceptible to cracking. It is the object of the present invention is to provide a thin metal mold having an extended heat transfer surface area thereon formed without significantly heating the metal mass comprising the metal mold and without distorting the physical dimensions of the mold and without degradation of the properties of the mold. This object is accomplished by means of a mold assembly of the type indicated at the outset and being characterized in that a plurality of heat transfer pins connected to said metal shell at the outer surface and having an extended outside surface area exposed to the heat source for heating said metal shell the assembly, each of said heat transfer pins further including a large diameter head portion located in juxtaposed relationship with said outer surface and a weld nugget formed solely between said head portion and said metal shell for interconnecting each heat transfer pin to said metal shell; said outer surface of said metal shell having a clean weld-free surface portion formed between said head portions which combines with said extended outer surface areas of said heat transfer pins to define a total heat transfer surface area greater than that of said outer surface for enhancing heat flow from said heat source to thermoplastic material deposited on said inner surface for heating, the thermoplastic material to fuse the material into a thin layer thermoplastic shell. Regarding the present invention as defined in the preceding paragraph it should been noted that GB-A-675,604 discloses a heat exchanger already having an extended surface comprising a base wall of steel or iron and extended pin-like however headless surface elements attached thereto. These elements or pins consist of copper, aluminum or other metal having a high coefficient of thermal expansion and are attached to the base wall by brazing or bolt welding so that the inner ends thereof are annularly upset and spread out radially over the base wall of the completed heat exchanger which requires considerable heat and pressure. Further, DE-A-26 14 655 discloses a bolt welding apparatus inclying a condensor battery as an energy source for a welding operation. According to the cited documents bolts having pointed forward ends which during the welding operation are pressed against a base element to which the bolt is to be welded in the course of a short high current welding operation involving discharge of the condensor battery. The welding methods according to GB-A-675,604 and DE-A-26 14 655 are neither intended for nor useful in the attachment of heat transfer pins to a thinwalled molding shell, especially one produced by electroplating. Further features, objectives and advantages of the present invention will become more apparent in view of the following description when taken in conjunction with the accompanying drawings wherein. Fig. 1 is a diagrammatic view of molding apparatus for casting plastisol against a mold heated by hot air flow thereacross; FIG. 2 is a fragmentary sectional view of the mold showing a deposited layer of fused plastisol thereon; FIG. 3 is a fragmentary perspective view of the underside of the mold in FIG. 2 showing an array of heat transfer pins formed thereon; FIG. 4 is an enlarged fragmentary view of a capacitive weld joint formed between each of the heat transfer pins and the outer surface of the mold in FIG. 2. Description of the Preferred Embodiment Referring now to FIG. 1, a molding apparatus 10 is illustrated. The mold apparatus 10 is representatively shown as including a base 12 having spaced trunnion arms 14, 16 for rotatably supporting a mold support 18. The trunnion arms 14, 16 define an axis about which a thin mold shell 20 is rotated for casting plastisol thereagainst from a powder box 22 connected to the shell 20 as shown in FIG. 1. The mold support 18 defines a mold heating and cooling cavity 24 for directing either heated or cooled air from a heater 26 or a cooler 28. The plastisol is distributed from the box 22 in a dry form. If desired a charge of liquid plastisol would be equally suitable for use with the mold of the present invention. Examples of such sources (either dry plastisol or liquid plastisol) are set forth in U.S.P.N. 4,623,503 which is incorporated herein by reference for purposes of better understanding the operation and structure of the mold apparatus 10 and the plastisol material to be gelled and cured on the mold shell 20. In accordance with the present invention, the mold shell 20 has an inner surface 20a against which the plastisol material is cast. The material is a suitable thermoplastic resin material such as particles of polyvinyl chloride having a core of resin with a suitable plastisizer and having an outer surface of color pigment material thereon as described in greater detail in U.S.P.N. 4,784,911. In order to gell and cure such material, it is necessary to provide an efficient transfer of heat from the gas flow through the cavity 24 into the shell 20, thence through the thickness of the metal in the shell 20 and into the thermoplastic material deposited on the inner surface 20a. To increase the heat transfer from the hot gas flow (or into the cooling gas flow) the shell 20 has its outer surface 20b connected to a plurality of heat transfer pins 30. Each of the heat transfer pins 30 has a large diameter head portion 30a located in juxtaposed relationship with the outer surface 20b. The pins 30 have an extended outer surface area defined by a cylindrical surface 30b and an end surface 30c which substantially increase the outer surface area of metal exposed to air flow through the cavity 24. In accordance with the present invention, the pins 30 have their head portions 30a joined to the outer surface 20b by a weld nugget 32 which is formed by a capacitive discharge welding gun. Such a weld formation is limited solely to the interface 34 between the pins 30 and the shell 20 at the head portion 30a. Consequently, a shell surface region 20c formed between each of the pins 30 is clean of any welding material both during and after formation of the nugget 32. More particularly, the pins 30 are located in a known capacitive discharge welding gun 40 of the type that has a charging circuit 40a; a circuit 40b that applies a low current flow through the pins 30 to form a small weld pool 32a at the interface 34 as shown in FIG. 4 in broken line. Once the small weld part is formed, a gun spring (not shown) forces the head portion 30a against a clean surface portion of the outer surface 20b and a bank of capacitors 40c discharges to direct a large current flow across the small weld pool 32d at the interface 34 to produce a welding arc that will almost instantaneously melt the metal of the shell only at the interface 34. The discharge is accomplished in less than one second for each weld joint. As soon as the capacitor bank is discharged the weld pool cools into the nugget 32. The resultant nugget 32 is hereinafter referred to a capacitive weld joint. The instantaneous melting and rapid cooling from the surrounding metal results in no grain growth in the mold joint area. Such a joint is characterized by being formed in a local region of the metal shell 20 such that the shell 20 will not be heat distorted to thereby retain desired physical dimensions and thereby eliminate the need for additional machining once the pins 30 are connected to the shell. The connected pins 30 form a good heat transfer path from the cavity 24 through the metal of the shell 20 and into the thermoplastic material deposited on the inner surface 20a of the metal shell 20. In addition to providing a good heat transfer path the provision of the pins 30 and capacitive weld joint connection combine to substantially extend the surface area on the gas side of the mold shell 20 thereby to increase the heat transfer rate to the mold so as to reduce part molding cycle times. The capacitive weld step heats only a small portion of the mass of the material as the joints 32 are formed. Consequently, the metal of the shell is not degraded to the same extent as in the case of solder, brazed or gas weld connections between a mold formed as a thin metal shell. An example of thin metal shells to which the pins 30 are connected is a mold which is formed by electroforming a thin layer of nickel against a mandrel. The nickel is deposited in a thickness which will provide sufficient structural strength to hold the part during molding; to have sufficient strength to permit safe connection and disconnection of a metal shell to mold apparatus; and to have sufficient strength to permit the metal shell to be rotated for evenly distributing the plastisol material across the casting surface thereof. The capacitive weld joints 32 provide a strong physical connection between pins 30 and shell 20. The joints 32 also serve as a good heat conductor from the extended outer surface area 30b of the pin 30. The invention has been described in an illustrative manner, and it is to be understood that the terminology which has been used herein is intended to be in the nature of words of description rather than of limitation. Obviously, many modifications and variations of the present invention are possible in light of the aforesaid teachings. It is therefore, to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described.

Claims: A mold assembly for molding thermoplastic particles into a solid thin shell the assembly including a metal shell (20) having a cavity and including an outer surface exposed (20b) to a heat source and further including an inner surface (20a) on which thermoplastic material is cast and fused to form a thin layer thermoplastic shell the assembly characterized by: a plurality of heat transfer pins (30) connected to said metal shell at the outer surface and having an extended outside surface area exposed to the heat source for heating said metal shell the assembly, each of said heat transfer pins (30) further including a large diameter head portion (30a) located in juxtaposed relationship with said outer surface (20b) and a weld nugget (32) formed solely between said head portion (30a) and said metal shell (20) for interconnecting each heat transfer pin (30) to said metal shell; said outer surface (20b) of said metal shell (20) having a clean weld-free surface portion formed between said head portions which combines with said extended outer surface areas of said heat transfer pins (30) to define a total heat transfer surface area greater than that of said outer surface for enhancing heat flow from said heat source to thermoplastic material deposited on said inner surface (20a) for heating the thermoplastic material to fuse the material into a thin layer thermoplastic shell. The mold assembly of claim 1 characterized by the metal shell (20) being formed as a thin metal shell suitable for use in casting and fusing a thin layer thermoplastic shell. The mold assembly of claim 1, characterized by the metal shell (20) being formed by electroplating a thin layer of metal against a mandrel. The mold assembly of claim 1 characterized by the metal shell being formed by electroplating a thin layer of nickel against a mandrel. The mold assembly of claim 1, wherein said weld nugget (32) is characterized by a weld formed solely by welding energy directed through said heat transfer pin (30). The mold assembly of claim 5, characterized by said welding energy being applied by a current discharged from a bank of capacitors (40c) having power released therefrom upon formation of a low current conducting path between said large diameter head portion (30a) and said outer surface of said metal shell (20).

Inventors: JACKSON KENNETH L JR, JACKSON, KENNETH L., JR.
Applicants: DAVIDSON TEXTRON INC, DAVIDSON TEXTRON INC.
Application year: 1991
Main classification: B29C33
IPC codes: B29C39, B29C33, F28F1, B29C41