Polyacetoacetate-containing epoxy resin compositions

Abstract: A coating composition is provided comprising an epoxy resin, a polyacetoacetate, a curing agent for the epoxy resin, and an optional organic solvent. The presence of the polyacetoacetate permits the preparation of a fast-drying high-solids coating formulation.

Description: The invention relates to polyacetoacetate-containing high-solids epoxy-based coating formulations. High-performance coatings for protection of metal surfaces of ships, aircraft, bridges and other structures exposed to corrosive environments must be resistant to the corrosive effects of water and solvents. Excellent coating properties can be obtained from the use of solvent-borne, two-package epoxy coatings cured with amine curing agents. To achieve sufficiently low viscosity to apply high-performance coating formulations, low molecular weight solid epoxy resins may be diluted with solvents. Prohibitions on the use of large quantities of certain solvents for this purpose, however, make it necessary to develop alternate approaches to reducing the viscosity of epoxy-based coating formulations. A conventional technique for viscosity reduction is the addition of a diluent such as dibutyl phthalate, butyl glycidyl ether, cresyl glycidyl ether or aliphatic alpha alcohol glycidyl ether. Such diluents, however, can adversely affect coating properties and in some instances contribute to the volatile organic compound (VOC) content of the coating. Alternatively, a lower molecular weight liquid epoxy resin and blends of such resins with solid epoxy resins may be employed to reduce the volatile content of coating formulations. A related approach includes the use of low viscosity, nonvolatile curing agents to reduce coating formulation viscosities. While all of these approaches reduce the viscosity of the coating formulation, they have a tendency to increase the dry time of the resulting coatings. High-performance coatings for metal surfaces of large structures such as bridges must be cured under ambient conditions, as the application of heat over such a large surface is not practical. Ambient-cure dry time is therefore a very important consideration, because a tacky coating picks up dust and is easily marred. It is therefore an object of the invention to provide a high-solids epoxy-based coating formulation which has a sufficiently low viscosity and which dries rapidly. According to the invention, a composition is provided comprising (a) a polyglycidyl ether having an average of at least 1.5 epoxide groups per molecule and (b) a polyacetoacetate having two to four acetoacetate groups per molecule and a molecular weight within the range of 200 to 800. It was surprisingly found that the presence of the polyacetoacetate provides a high-solids coating having shortened dry times. The coating formulation according to the invention contains an epoxy resin. The epoxy resin can be any curable epoxy resin having, on the average, more than one vicinal epoxide group per molecule. The epoxy resin can be saturated or unsaturated, aliphatic, cycloaliphatic, aromatic or heterocyclic, and may bear substituents which do not materially interfere with the curing reaction. They may be monomeric or polymeric. Particularly suitable epoxy resins include glycidyl ethers prepared by the reaction of epichlorohydrin with a compound containing at least one hydroxyl group carried out under alkaline reaction conditions. The epoxy resin products obtained when the hydroxyl group-containing compound is 2,2 bis(4-hydroxyphenyl)propane (bisphenol-A) are represented below by structure I wherein the average n is zero or a number greater than 0, commonly in the range of 0 to 10, preferably in the range of 0 to 2. Other suitable epoxy resins can be prepared by the reaction of epichlorohydrin with mononuclear di- and trihydroxy phenolic compounds such as resorcinol and chloroglucinol, selected polynuclear polyhydroxy phenolic compounds such as bis(p-hydroxyphenyl)methane and 4,4'-dihydroxybiphenyl, or aliphatic polyols such as polypropyleneglycol and trimethylolpropane. Epoxy resins suitable for high-solids coating formulations have molecular weights generally within the range of from 100 to 4,000, preferably of from 200 to 1500. A commercially available epoxy resin being a reaction product of epichlorohydrin and bisphenol-A having a number average molecular weight of about 350, an epoxide equivalent weight (ASTM D-1652) of 178-185, and an average n value in formula I above of 0.1, is an example of a suitable epoxy resin for such coating formulations. Such low molecular weight resins can also be saturated, as is the case when the starting hydroxyl group-containing compound is hydrogenated bisphenol-A. Such saturated resins provide high-performance coatings but typically suffer from long dry times. Also favoured in high-solids coating formulations, because of the superior coating properties of the resin, are advanced polyglycidyl ethers of polyhydric phenols obtained by the catalyzed reaction of an epoxy resin of relatively low molecular weight with a phenolic compound to produce an epoxy resin having a higher molecular weight. Such an epoxy resin is for example a product of the catalyzed advancement reaction of EPIKOTE 828 (EPIKOTE is a trade mark) with bisphenol-A which has a number average molecular weight of about 505 and an epoxide equivalent weight (EEW) lying in the range of 230-280. The composition according to the invention includes a polyacetoacetate having from two to four functional groups of the formula and a molecular weight within the range of from 200 to 800. Such polyacetoacetates include, for example, the bisacetoacetates of dipropylene glycol, ethylene glycol and neopentyl glycol; the trisacetoacetates of trimethylolpropane, trimethylolethane, glycerol and bis(trimethylolpropane); and the tetrakis acetoacetate of pentaerythritol. The preferred polyacetoacetates are trisacetoacetates because of their non-volatility and their demonstrated ability to impart low viscosity and rapid dry times to high-solids coatings. A particularly preferred trisacetoacetate compound is trisacetoacetate of trimethylolpropane (TMP). The polyacetoacetate will generally be present in the coating formulation in an amount effective to reduce the viscosity of the epoxy resin, generally at least 1 weight percent, preferably within the range of from 2 to 75 weight percent, preferably of from 4 to 40 weight percent, based on the weight of the epoxy resin. The coating formulation of the invention will include a curing agent for the epoxy resin. Curing agents which are particularly suitable for use in high-solids ambient-cure coating systems include aliphatic polyamines, cycloaliphatic amines, aromatic amines, Mannich bases, ketimines, oxazolines, amidoamines, and modified polyamine resins prepared by reacting aliphatic or cycloaliphatic polyamines with compounds containing functional groups which react with the amine group, such as glycidyl ether-containing or carboxy-containing compounds. Reaction products of polyamines with glycidyl ether-group containing compounds are known as "polyamine-epoxy adducts." Reaction products of dicarboxylic acids and polyamines are known as "polyamide resins." The latter are usually prepared by condensation of the dicarboxylic acid with excess amounts of polyalkylene polyamines. Polyamides based on dicarboxylic acids having more than 10 carbon atoms, particularly those based on C₃₆ dicarboxylic acids, are preferred because of the water resistance and flexibility of the resulting coatings. Suitable modified polyamine resins are commercially available from the Pacific Anchor Chemical Corporation as Ancamide amidoamine and polyamide resins (Ancamide is a trade mark), and from Henkel Corporation as Versamid polyamide resins (Versamid is trade mark). The final coating formulations can optionally include additional non-reactive diluents such as dibutyl phthalate or reactive diluents such as monoepoxies (butyl glycidyl ether and cresyl glycidyl ether, for example) and epoxy resins (vinyl cyclohexene dioxide and triglycidyl ether of trimethylol propane, for example). The final coating formulation will include sufficient solvent liquids to reduce the viscosity of the formulation to a level permitting application to a surface as a coating. For some applications, it may be desirable to apply a coating formulation which does not include an organic solvent. Organic solvents such as alcohols; aliphatic, naphthenic and aromatic hydrocarbons; ethers; esters; and ketones can be employed. Specific examples of such organic diluents include ethyl alcohol, isopropyl alcohol, butyl alcohol, the monomethyl ether of diethylene glycol, ethylene glycol of monobutyl ether, tetrahydrofuryl alcohol, ethylene glycol monomethyl ether, ethyl acetate, isopropyl acetate, butyl acetate, amyl acetate, acetone, methyl ethyl ketone, methyl isobutyl ketone, diisobutyl ketone, hexane, heptane, octane, methyl cyclohexane and xylene. Ketones are the preferred organic solvents. The final coating formulation can include conventional coating additives such as accelerators; fillers and extenders, such as silica, mica, quartz, cryolite, Portland cement, limestone, atomized alumina, barytes, talc, zinc powder, pyrophyllite, clay, diatomaceous earth; pigments, such as titanium dioxide, red lead, basic lead silica chromate, basic zinc chromate, zinc, zinc oxide, lead, barium and strontium chromates, calcium plumbate, barium metaborate, and calcium, strontium and zinc molybdates; and resinous modifiers, such as phenolic resins, urea resins, melamine resins, acrylic resins, polyester resins, vinyl resins, bituminous resins, and polystyrene. Coating compositions according to the invention can be provided as a two-container system. The first container contains the epoxy resin component and the second container contains the curing agent for the epoxy resin. Any diluents used may be incorporated into either component, although any amine-reactive diluents are preferably provided with the resin component. Any solvents used and additives such as pigments can be included in either or both containers. When the final coating formulation is prepared by mixing all components, the amount of the curing agent added to the epoxy resin will be that amount which is effective to cure the epoxy resin and the polyacetoacetate under the selected coating/curing conditions. Generally, the amount will be approximately stoichiometric, so that there is of from 0.5 to 1.5 reactive NH group for each epoxy group and each acetoacetate functional group present. The coating composition can be applied by conventional coating methods such as brush-coating, spray coating and air coating. Curing can be generally carried out by exposure of the applied composition to ambient conditions for one hour to one week. Example 1 For the preparation of the trisacetoacetate of trimethylolpropane 235 g of diketene was added to 125 g of 2-ethyl-2-(hydroxymethyl)-1,3-propanediol containing 0.362 g of 4-(dimethylamino)pyridine at 60 °C over a period of one hour. Stirring at 60 °C was continued for an additional hour and the product was subsequently isolated. Example 2 High-solids coating formulations of comparative runs 1-3 and runs 4-5 according to the invention, based on a low-viscosity epoxy were prepared and tested. These coating forumulations were prepared by roll-blending, over a 30-minute induction period at 25 °C, the following constituents: 25.00 parts per weight (ppw) of a liquid diglycidyl ether of bisphenol-A (DGEBPA) having an EEW of 185-192; optionally a monoacetoacetate (runs 2 and 3) or a polyacetoacetate compound (runs 4 and 5) in amounts as indicated in Table 1; 14.7 ppw of a 9:1 blend of methyl isobutyl ketone (MIBK) and methyl normal amyl ketone (MNAK); 18.8 ppw of Versamid 140 (Henkel Corporation) (Versamid is a trade mark), a polyamide resin having an amine value of 370-400; and 0.22 ppw of SR882 flow control agent (a 60% solids solution of a silicon resin flow control agent in xylene). The final formulations had a calculated weight percent solids content of 75%. The formulations were applied to cold-rolled steel panels using a wire-wound drawdown bar to provide a dry film thickness of 1.1± 0.3 mm. Drying, curing and evaluations were carried out at a temperature of 25 °C and humidity of 55%. Panels were aged for 9-12 days. Relevant data in respect of runs 1 to 5 are presented in Table 1. Table 1 shows the drastic effect on the dry time caused by the presence of a polyacetoacetate compound in the film formulation (runs 4 and 5). It also can be seen that the presence of a monoacetoacetate compound results in even longer dry times. Example 3 High-solids coating formulations of comparative run 6 and runs 7-9 according to the invention were prepared by roll-blending, over a 30-minute induction period at 25 °C, the following ingredients: 30.00 parts per weight (ppw) of a diglycidyl ether of a hydrogenated bisphenol-A (DGEHBPA) having an EEW of 210-238; optionally trisacetoacetate of TMP (runs 7-9) in amounts as indicated in Table 2; 17.40 ppw of Versamid 140 polyamide resin; 11.8 ppw of a 9:1 blend of MIBK and MNAK; and 0.40 parts of SR882 flow control agent. The final formulations had a calculated solids content of 80%. The clear coatings had a calculated VOC of 0.17 kg/l of coating. As can be seen from Table 2, run 6, a film prepared from the hydrogenated resin had very long dry time. Inclusion of the trisacetoacetate in varying amounts significantly reduced the dry time of films prepared from the formulations. Run 1 2 3 4 5 DGEDEBA, ppw 25 21.3 21.3 21.3 17.5 Methylacetoacetate, ppw 3.8 1-octanolacetoacetate, ppw 3.8 TMP-trisacetoacetate, ppw 3.8 7.5 Viscosity Z5+ N- T-U Z2 Y+ Viscosity E- D D-E J-K Q-R VOC content, kg/l 0.21 0.26 0.21 0.21 0.21 Dry film thickness, mm 1.4 1.2 1.2 1.4 1.2 Dry time, hours Set to touch 8 8.5 8.5 1.8 0.8 Dust free 11 12.3 12 5.5 2.3 Through dry 11.8 13.5 14.5 8 7 Run 6 7 8 9 DGEHBPA, ppw 30 28.5 27.0 25.5 TMP Trisacetoacetate, ppw 1.5 3.0 4.5 Viscosity Z+ X-Y X W Viscosity E-F F-J L Q-R Dry film thickness, mm 0.9 0.8 0.8 0.8 Dry time, hours Set to touch 15.5 12.5 9 1.5 Dust free 19.5 16 13.5 2.5 Through dry 19.5 16.5 15 5.5

Claims: Claims for the following Contracting States : BE, DE, FR, GB, IT, NL A composition comprising: (a) a polyglycidyl ether having an average of at least 1.5 epoxide groups per molecule and (b) a polyacetoacetate having per molecule two to four acetoacetate groups of the formula and a molecular weight within the range of 200 to 800. A composition as claimed in claim 1 in which the polyacetoacetate is present in the composition in an amount of at least 1 weight percent, based on the weight of the polyglycidyl ether. A composition as claimed in claim 1 or 2 in which the polyacetoacetate is present in the composition in an amount within the range of from 2 to 75 weight percent, based on the weight of the polyglycidyl ether. A composition as claimed in any one of the claims 1 to 3 in which the polyacetoacetate is a trisacetoacetate. A composition as claimed in claim 4 in which the trisacetoacetate is selected from trisacetoacetates of trimethylolpropane, trimethylolethane, glycerol and bis(trimethylolpropane). A composition as claimed in any one of the claims 1 to 5 in which the polyglycidyl ether is a diglycidyl ether of bisphenol-A and the polyacetoacetate is the trisacetoacetate of trimethylolpropane. A composition as claimed in any one of the claims 1 to 6 comprising in addition an effective amount of an amine curing agent. A composition as claimed in claim 7 in which the amine curing agent is selected from the group consisting of polyamine-epoxy adducts, polyamines, cycloaliphatic amines, aromatic amines, polyamides, amidoamines and Mannich bases. A composition as claimed in any one of the claims 1-8 which further comprises up to 50 weight percent, based on the weight of the composition, of an organic solvent. A composition as claimed in claim 9 in which the organic solvent is a ketone. Claims for the following Contracting State : ES A process for the preparation of an epoxy resin composition by mixing at least the following components (a) a polyglycidyl ether having an average of at least 1.5 epoxide groups per molecule and (b) a polyacetoacetate having per molecule two to four acetoacetate groups of the formula and a molecular weight within the range of 200 to 800. A process as claimed in claim 1, in which the polyacetoacetate is used in an amount of at least 1 weight percent, based on the weight of the polyglycidyl ether. A process as claimed in claim 1 or 2, in which the polyacetoacetate is used in an amount within the range of from 2 to 75 weight percent, based on the weight of the polyglycidyl ether. A process as claimed in any one of the claims 1 to 3, in which the polyacetoacetate used is a trisacetoacetate. A process as claimed in claim 4, in which the trisacetoacetate used is selected from trisacetoacetates of trimethylolpropane, trimethylolethane, glycerol and bis(trimethylolpropane). A process as claimed in any one of the claims 1 to 5, in which the polyglycidyl ether used is a diglycidyl ether of bisphenol-A and the polyacetoacetate used is the trisacetoacetate of trimethylolpropane. A process as claimed in any one of the claims 1 to 6 wherein an effective amount of an amine curing agent is used as an additional component. A process as claimed in claim 7 in which the amine curing agent used is selected from the group consisting of polyamine-epoxy adducts, polyamines, cycloaliphatic amines, aromatic amines, polyamides, amidoamines and Mannich bases. A process as claimed in any one of the claims 1-8, wherein up to 50 weight percent, based on the weight of the composition, of an organic solvent, is used as an additional component. A process as claimed in claim 9 in which the organic solvent used is a ketone.

Inventors: PIETRUSZKA RITA DAWN, STARK CHARLES JOHN, PIETRUSZKA, RITA DAWN, STARK, CHARLES JOHN
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1991
Main classification: C09D163
IPC codes: C08G59, C09D163