Wear resistant titanium nitride coating and methods of application

Abstract: Wear resistant surfaces can have their service life increased by being coated with a titanium nitride based coating applied by the electric arc thermal spray process using at least one pre-nitrided titanium feed wire and nitrogen in the arc spray gun.

Description: FIELD OF THE INVENTION The present invention pertains to industrial articles such as screens for cominution devices which are normally subject to mechanical wear during use and methods for extending the service life of such parts. BACKGROUND OF THE INVENTION Throughout all of the industrial sectors of the world many mechanical devices are subjected to wear caused by abrasion, erosion, and/or corrosion during their normal service life. Billions of dollars are spent by industry to replace components which fail prematurely because of excessive wear in inert and corrosive service environments. Many parts may be made to last longer if they were manufactured from harder, corrosive resistant materials however, the cost of doing so is often prohibited and can mean the difference between a successful operation and a unsuccessful operation because of excessive costs. A number of methods are available for surface hardening or depositing corrosion and wear resistant materials on industrial parts. The oldest known methods are diffusion treatments, nitriding and carburizing of ferrous based materials. The disadvantage in using these techniques is that they involve subjecting the parts to elevated temperatures. Apart from the high costs associated with the energy and operation time, subjecting a part to elevated temperatures can cause size changes and loss of mechanical properties which would render the part unsuitable for use and/or would require a further heat treating operation and a subsequent cleaning operation to be performed after the surface treatment. Electroplating, most commonly used to produce hard chromium or nickel coatings, involves cleaning the parts to be coated to a high degree and involves toxic solutions which are costly when disposed of in an environmentally safe manner. Chemical and physical vapor deposition of coatings require high capital investment, high processing costs and are limited to very thin coatings and small parts. Of the thermal spray deposition methods which can be used to coat parts of unlimited size with coatings of unlimited thickness flame spraying often yields a porous coating with oxide inclusions. Plasma spraying especially if performed in a vacuum or atmosphere chamber, will yield dense homogeneous coatings but is expensive and therefore limited in use. High velocity detonation guns can deposit dense ceramic coatings on substrates but the equipment, feed powders and processing are very expensive. JP-A-60 092 461 makes use of a Ti powder to produce a coating on the substrate. This powder is reacted with for example nitrogen gas by plasma art discharge and molten by use of high-output laser. After all the resulting coating is cooled with water. Chemical abstracts Vol . 103, 1985, 21 90 12 j, teaches to support Ti coatings by low pressure electric arc spraying on a substrate. According to this disclosure the electric arc spraying, which overcomes some of the deficiencies of the plasma arc discharge, is only applicable in vacuum or under reduced pressure. Electric arc spraying with inert gases can produce dense, homogeneous coatings which bond well to a variety of substrate materials. Arc-sprayed titanium nitride which does not require high enthalpy flame is a cold process compared to the high heat input plasma and flame spray processes which can damage or distort the substrate material. Furthermore, the capital equipment and operating costs are less than one-half that of the plasma high velocity spraying methods and about order of magnitude less than that of the chemical vapor deposition. In electric arc spray of titanium nitride type coatings, disclosed in this invention, the surface to be coated requires no special preparation other than grit blasting. SUMMARY OF THE INVENTION In order to provide improved wear resistance for a part normally subject to abrasion, erosion and/or corrosion during use, it was discovered that a titanium nitride coating can be applied by exposing a substrate to an effluent from an electric arc thermal spray gun operated in the atmosphere with a current supply of between 100 and 400 A and a potential difference ot between 28 and 48 V, using a pretreated titanium wire, said wire being pretreated by annealing in nitrogen to increase the nitrogen content of the wire to at least 500 ppm, and a nitrogen gas as the atomizing/propelling gas being fed to the nozzle as a gas stream at between 206.6 and 894.4 kPa (30 and 130 psia) whereby a substatially titanium nitride coating having a thickness of at least 0.0254 mm (0.001 inch) is produced on said substrate. One embodiement of the invention includes coatings nitrogen arc sprayed using two different wire materials where at least one of them is said nitrogen pretreated titanium wire. BRIEF DESCRIPTION OF THE DRAWING Figure 1 is a schematic representation of a typical electric arc spray system employed to make the articles and practice the process of the present invention. Figure 2 is a photomicrograph of the structure of titanium wire before treatment. Figure 3 is a photomicrograph of the structure of titanium wire after pre-nitriding. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT Increasing the service life of a part normally subjected to mechanical wear during use can provide a manufacturer and user with significant cost savings. For example, in the grinding of materials such as rubber and plastics for reformulating into compounds, doubling the service life of the screens used to classify the material in the impact mill (e.g., Hammermill) would be a significant benefit. One method of enhancing the wear resistance of industrial parts would be to deposit a titanium nitride coating on the surfaces of the parts that are subject to wear. It has been discovered that if the electric arc spray process is used to apply such coatings and high purity nitrogen is substituted for air as a propelling gas the titanium wire is melted and the titanium is nitrided with minimum oxidation between the arc spraying device and the substrate to deposit a titanium nitride coating. The arc spray process can be used without an atmosphere chamber or a furnace or subsequent nitriding of the coating. A particularly effective coating is achieved if the titanium wire is nitrided prior to being used in the electric arc spray device. The nitrogen used as the propelling (atomizing) gas during the electric arc thermal spray process reacts with the titantium feed wire to produce the titanium nitrogen compound in flight. As the molten droplets land on the surface of the article being coated they solidify thus forming a hard titanium nitride base coating that protects against wear and corrosion. Electric arc spraying of a titanium coating utilizing nitrogen as a propelling gas is inexpensive as compared to deposition by plasma, high velocity combustion spraying, chemical vapor deposition and physical vapor deposition techniques. In addition, titanium nitride and titanium oxide are non-toxic as compared to chromium and nickel-phosphorous used in other hard facing techiques, thus the coating is suitable for use in food processing equipment. Furthermore, arc spraying takes minutes rather than hours that may be required for other processes, leaves no toxic byproducts and requires a minimal capital investment. As shown in figure 1 of the drawing, the arc spray system 10 includes an arc gun 12, a constant voltage power source 14, a control console 16 and a wire feed device represented by wire spools 18 and 20 respectively. The arc spray gun 12 includes two sets of feed rollers 22, 24 to move separate wires 26, 28 respectively, through the gun to the nozzle end 30 where due to electrical current of different polarities (e.g., as shown in the drawing) an arc is struck between the wires 26 and 28. As the wires melt due to the influence of the electrical arc, compressed nitrogen gas is introduced into the arc on 12 as shown by the arrow 32. The nitrogen gas exists the nozzle 30, where it causes the molten metal to be broken up into a stream of droplets. The compressed gas, in addition to atomizing the metal, propels the atomized metal (spray stream) toward a substrate 34 such as a conventional Hammermill screen 34. During aerial traverse of the atomized titanium, reaction with nitrogen forms a titanium nitride compound. The substrate 34 can be mounted vertically or horizontally and either it or the arc gun 12 can be oscillated to provide a uniform coating over the length of the electrode. Wire feeders 18 and 20 can also include a pair of rollers 36, 38 to help feed the wire from the spools to the gun 12. The feed rolls in the gun and the wire feeds can either push, pull or use a combination of both techniques to move the wire through the arc gun 12. It was found that while a conventional titanium nitride coating placed on the substrate by the thermal arc spray process using titanium wire and nitrogen gas produced coatings of enhanced wear resistance, if the as-received titanium wire was pretreated to increase the nitrogen content the resultant coating was harder and the life of the parts in service was increased. The titanium wire pre-treatment was developed when it was realized that N₂-sprayed Ti x N coatings were both nitrogen (N) deficient and prone to in-flight oxidation. There were two additional reasons for wire pretreatment: (1) as-supplied Ti-wires were difficult to feed through arc-spray gun conduits, and a nitride coating on the wires was discovered to lower the wire feed-friction, (2) post-deposition nitrogen annealing of arc-sprayed Ti x N may not always be possible; some substrates may be sensitive to elevated temperatures and/or an excessively large mismatch may exist between thermal expansion coefficients of the Ti x N coating and substrate that will damage the coating, (e.g. Ti x N-coating on st. steel-substrate). The Experiments included selection of annealing conditions for Ti-wires, sprayability tests with the annealed wires, and evaluation of the coatings sprayed with the annealed wires. TABLE 1 below presents the selection process. The third step annealing was found to be optional and used for testing. The different microhardness (e.g., 269 vs. 150 VHN) on the cross-section of the N₂ annealed and initially 'hard' and 'soft' Ti-wires indicates that N₂ annealing can be at temperatures higher than 1000°C. TABLE 2 shows the 8-fold [N] pickup in the Ti-wire resulting from our 1000°C N₂ annealing. Initial sprayability tests showed that despite a yellow nitride post-annealing (nitride treated) coating, the N₂-treated Ti-wires can be melted, atomized, and deposited as well as the (untreated) as-supplied wires. Moreover, tests with continuously nitrogen annealed 'soft' wires show that the yellow nitride post-annealing coating actually smoothened the wire feeding into the gun which greatly improved the arc stability during the spraying. Ti x N coatings were deposited using the N₂ annealed wires and compared to the coatings produced previously using the as-supplied wires and/or the N₂ post-deposition annealing. The appearance, surface roughness, self-bonding ability, and adhesion to the substrate (bend test) of the new coatings were the same as in the case of the coatings deposited in the past. However, the Knoop microhardness measurements revealed significant differences between the coatings. In the case of the 'hard' Ti feed wire, the coating deposited using the N₂ annealed wire was as hard as the coating which was applied by depositing essentially pure titanium followed by a post-deposition anneal in N₂ atmosphere. Both these coatings were much harder than the 'basic' coating produced with the as-supplied wire with no post-deposition annealing. Hardness of the Ti x N coating, produced with the N₂ annealed 'soft' Ti-wire, the highest in the series, was compared with those of the stainless and carbon steel substrates. The coating was 6.3 times harder than the stainless and 9 times harder than the carbon steel. The N₂ wire pretreatment was found to improve hardness of the Ti x N coating by increasing the nitrogen content and improving the nitride stoichiometry (lower x). Nevertheless, the increased nitrogen content did not reduce the self-bonding ability of the Ti x N deposits. Microhardness of the new coating is at least equivalent to that of the post-deposition annealed coatings, which makes the annealing of the coated parts unnecessary. Alternatively, both the pretreatment and post-deposition annealing steps can be used as two independent tools for the coating hardness control. It was also observed that the wire pretreatment improved the arc stability by lowering the wire friction in the gun conduits. As to the wire, any technically pure, i.e. unalloyed, titanium wire with no special requirements or specs on purity levels, e.g. no spec. on Fe, V, etc. can be used. Typically, a technically pure titanium wire should have no more than 100 ppm of nitrogen (on wt. basis). Any titanium physical condition, e.g. soft, hard, or half-hard is acceptable. Figure 2 is a photomicrograph of the structure of a typical wire before treatment. Pre-nitriding the wire should impart the following characteristics: (a) develop a golden colored TiN film on the surface of the treated wire, (b) increase nitrogen content, e.g. more than 500 ppm w/o, (c) the core of the treated wire should remain metallic in order to preserve the flexibility of the wire required for the feeding of the arc-spray gun from the reels. This means, the top limit for the nitrogen content in the wire is 20% w/o. As shown in Figure 3 the microstructure of the pre-nitrided (annealed) wire should show coarse circular grain growth from the surface toward the core of the wire with corresponding degrees of hardness (VHN) from the surface to the core. According to the present invention a uniform wear and corrosion resistant coating consisting primarily of titanium nitride can be deposited on a variety of substrate materials. The coating is deposited by electric arc spray using 15.7 or 7.6 mm (0.062 or 0.030 inch) diameter titanium wire that has been pretreated as set out above and nitrogen as the propelling (atomizing) gas. Nitrogen is substituted for high purity air as the propelling gas so that the titanium is further nitrided and oxidation is minimized. Two spools of titanium wire are feed at a constant rate into the gun 12 where they arc across at a potential difference of between 28 and 48 V and 100-400 A. Alternatively one spool of the wire may feed the spraying gun with another coating material which will form with the Ti x N alloyed for pseudo-alloyed coatings. This other material may include hard Fe, Cr, Ni, Mo, and W alloys and compounds as well as soft bonding non-ferrous metals and alloys. The coatings produced by the simultaneous use of the Ti and non-Ti wires offer lower hardness but higher impact resistance. The required spraying conditions remain unchanged. The nitrogen gas stream is feed to the nozzle at between 206.6 and 894.9 kPa (30 and 130 psig). The molten droplets react in flight with the nitrogen gas and form the titanium nitride coating on the substrate 34. The stand-off distance between the gun and a substrate is between 7.6 and 20.3 cm (3 and 8 inches). The substrate is grit blasted before spraying in order to increase the strength of the mechanical bond between the coating and the substrate. The coating itself can be deposited to a thickness ranging from 0.025 mm (0.001 inches) to several mm (inches) in depth. Coated parts have shown increased wear and corrosion resistance. Specifically, screens from Hammermills use to cryogenically grind rubber were coated under the above condition with three passes used to deposit a coating having a nominal thickness of 0.03 cm 0.012 inches. Screens coated according to the invention have shown service lives between 2 and 10 times as long as uncoated screens. Corrosion exposure tests were performed by placing coated parts in seawater for extended periods of time with no apparent effect on the coating. The titanium-nitrogen compound forming the coating which provides increased wear and corrosion-resistance over that of the metallic substrate can show a coating hardness in the range of between 860 to 1500 (VHN) micro hardness as measured by the Vickers method. This is harder by a factor of between 5 and 11 than the normal substrate materials. The process of the present invention can be applied to any material that will accept a titanium nitride bonded coating. The coatings will be effective to increase the wear resistance and can be placed on the substrate by an economical method. In addition to Hammermill screens the process of the present invention was applied to an air-jet pulverizer which is used to grind metal salt material. Previous attempts by the user to grind a metal salt material have resulted in graying of the light material due to erosion of the interior surfaces of the mill. Coating a laboratory mill resulted in grinding of the salt material with no apparent contamination since there was no graying of the white material produced. Wear clips from a centrifugal kelp processing machine were coated according to the present invention and were found to last twice as long as parts which the user had coated with tungsten carbide.

Claims: A method of improving the mechanical wear restistance of a substrate by coating said substrate with a substantially titanium nitride coating applied by the steps of: exposing said substrate to an effluent from an electric arc thermal spray gun operated in the atmosphere with a current supply of between 100 and 400 A and a potential difference ot between 28 and 48 V, using a pretreated titanium wire, said wire being pretreated by annealing in nitrogen to increase the nitrogen content of the wire to at least 500 ppm, and a nitrogen gas as the atomizing/propelling gas being fed to the nozzle as a gas stream at between 206.6 and 894.4 kPa (30 and 130 psia) whereby a substatially titanium nitride coating having a thickness of at least 0.0254 mm (0.001 inch) is produced on said substrate. A method according to claim 1 wherein the distance from the electric arc thermal spray gun to said substrate is set at the minimum spacing to prevent overheating of said substrate. A method according to claim 2 wherein said spacing is between 7.62 and 20.32 cm (3 and 8 inches). A method according to claim 1 wherein only one of the feed wires is titanium wire, and the other feed wire is made of FE, Cr, Ni, Mo, W. lower melting point non-ferrous metals, and their alloys and ceramic or intermetallic compounds. An article of manufacture having at least one surface with improved mechanical wear resistance obtained by the method according to claim 1 comprising in combination: a substrate consisting of an article of manufacture having at least one surface subject to mechanical wear during normal use and a coating of substantially titanium nitride deposited on said surface, said coating being applied by exposing said substrate to an effluent from an electrical arc thermal spray gun operated in the atmosphere with a current supply of between 100 and 400 A and a potential difference of between 28 and 48 V, using a pretreated titanium wire, said wire being pretreated by annealing in nitrogen to increase the nitrogen content of the wire to at least 500 ppm, and a nitrogen gas as the atomizing/propelling gas being fed to the nozzle as a gas stream at between 206.6 and 894.4 kPa (30 and 130 psia) whereby a substantially titanium nitride coating having a thickness of at least 0.0254 mm (0.001 inch) is produced on said substrate. An article of manufacture according to Claim 5 wherein said substrate is a hammermill screen. An article of manufacture according to claim 5 wherein said substrate is a metallic part. An article of manufacturing according to claim 5 wherein said substrate is a ceramic or graphitic part.

Inventors: HAYDUK EDWARD ANDREW JR, NORTH JOHN GREGORY, SWAN ROBERT BRUCE, ZURECKI ZBIGNIEW, HAYDUK, EDWARD ANDREW, JR., NORTH, JOHN GREGORY, SWAN, ROBERT BRUCE, ZURECKI, ZBIGNIEW
Applicants: AIR PROD & CHEM, AIR PRODUCTS AND CHEMICALS, INC.
Application year: 1991
Main classification: C23C4
IPC codes: C23C14, C23C4