Synthetic resin mass having a low content of short carbon fibres

Abstract: The invention relates to a thermoplastic synthetic resin mass in which the synthetic resin mass comprises 0.3-1.0% by weight of carbon fibres having a length from 1-6 millimetres and a maximum of 5% by weight of dyes and pigments plus stabilisers, release agents, reinforcing fibres, flame retardant agents and fillers. The synthetic resin mass preferably comprises a polyphenylene ether, a polystyrene, a polypropylene, an acrylonitrile-butadiene-styrene terpolymer, an aromatic polycarbonate, a polyalkylene terephthalate, a polyamide, a polyphenylene sulphide, a polyetherimide or a mixture of two or more of these polymers. Articles having a beautiful flocculent structure can be obtained from the synthetic resin mass according to the invention.

Description: The invention relates to a thermoplastic synthetic resin mass comprising dyes and/or pigments to have a pastel colour and comprising carbon fibres. Articles molded out of the resin have a certain surface resembling some types of natural stone. More in particular, articles injection-moulded from the synthetic resin mass according to the invention show a very fine flocculent structure. Synthetic resin masses having a particular surface structure are commercially available. Investigations have demonstrated that the known masses comprise blackened aluminium flocks. However, the known synthetic resin masses are difficult to process; a kind of black stripe formation occurs during injection-molding. Moreover, the injection-moulding conditions must be adapted over and over again as a result of instability of the melt of the known synthetic resin mass. After long-lasting investigations it was found that the desired result, namely a well-processable thermoplastic synthetic resin mass having a flocculent surface structure of the articles formed therefrom, could be obtained by using short carbon fibres, in a very low concentration. The synthetic resin mass according to the invention is characterised in that it comprises 0.3-1.0% by weight of carbon fibres having a length from 1 to 6 millimetres and up to a maximum of 5% by weight of one or more of the following additives: dyes and/or pigments, stabilisers, mould- release agents, reinforcing fibres, flame retardant agents and fillers. The content of carbon fibres is preferably 0.3-0.7, even more preferably 0.4-0.6% by weight. The length of the fibres is preferably 3-6 mm. The synthetic resin mass comprises thermoplastic synthetic resins. The synthetic resin mass preferably comprises a polyphenylene ether, a polystyrene, a polypropylene, an acrylonitrile-butadiene-styrene terpolymer, an aromatic polycarbonate, a polyalkylene terephthalate, a polyamide, a polyphenylene sulphide, a polyetherimide or a mixture of two or more of these polymers. . Even more preferably the synthetic resin mass comprises an acrylonitrile-butadiene-styrene terpolymer or a polyalkylene terephthalate, for example, polybutylene terephthalate. In addition to the carbon fibres and the synthetic resin, the synthetic resin mass may comprise up to a maximum of five procent by weight of further conventionally used additives, for example, dyes and/or pigments, stabilisers, mould-release agents, reinforcing fibres, flame-retardants and fillers. To have a pastel colour most but not all synthetic resin compositions should comprise some dyes and/or pigments. If the content of additives is above five % by weight the effect on the surface appearance of the carbon fibres is masked i.e. not visible by the additives. The use of carbon fibres in synthetic resin masses is known per se. GB-A-1 486 033 describes a liquid coating composition comprising carbon fibres and a heavy loading of fillers. Due to the heavy loading of fillers the special appearance obtained with the mass according to the invention can not be obtained. GB-A-1 570 240 describes a thermosetting resin composition comprising carbon fibres and textile fibres. Due to the presence of textile fibres the special appearance obtained with the mass according to the invention can not be obteined. GB-A-1 437 314 describes a thermosetting resin composition with a high content (over 5%) of glass fibres and a high content (over 5%) of filler. Objects formed out of this composition will not show the desired surface appearance due to the high glass fibre content and due to the high content of filler. EP-A-0 032 379 describes the preparation of films out of a polycarbonate solution which comprises carbon fibres. Polycarbonate is a colourless transparent polymer. The addition of carbon fibres to such polymers, without also adding some dyes and or pigments, does not result in the desired surface appearance. The synthetic resin mass according to the invention is prepared by first compounding the synthetic resin and all other constituents followed by blending the carbon fibres in the melt. This can be effected e.g. by compounding the synthetic resin and the stabilisers thoroughly in a Banburry mixer or an extruder and by adding the carbon fibres shortly before the mass is taken out of the Banburry mixer or before it leaves the extruder. The fineness of the flocculent structure may be controlled by choosing the quantity of the carbon fibres and by choosing the exact instant at which the carbon fibres are added during the preparation of the synthetic resin mass. Dependent on the compounding process chosen, the addition shortly after the melt temperature has been reached during the compounding process results in a finer flocculent structure in the final product which is obtained from the synthetic resin mass, for example, by injection-moulding. Good results have been obtained by mixing powdered constituents based on an acrylonitrile-butadiene-styrene terpolymer and a pigment in a Banburry mixer for such a period of time until a temperature of approximately 190°C is reached. 0.5% By weight of'carbon fibres having a length of 2 mm or 4.5 mm or 6 mm were then added and the mixture was thoroughly mixed. Articles having a beautiful flocculent structure could be obtained from the synthetic resin mass thus obtained by injection-moulding. It has been found that the mechanical properties of the synthetic resin mass and the processing possibilities of the synthetic resin mass (for example, by injection-moulding) were hardly influenced by the presence of the carbon fibres.

Claims: A thermoplastic synthetic resin mass comprising dyes and/or pigments to have a pastel colour and comprising carbon fibres, characterized in that the synthetic resin mass comprises 0.3-1.0% by weight of carbon fibres having a length from 1-6 millimeters and up to a maximum of 5% by weight of one or more of the following additives: dyes and/or pigments, stabilizers, mould-release agents, reinforcing fibres flame retardant agents and fillers. A synthetic resin mass as claimed in Claim 1, characterised in that the synthetic resin mass comprises 0.4-0.6% by weight of carbon fibres. A synthetic resin mass as claimed in Claim 1, characterised in that the synthetic resin mass comprises carbon fibres having a length from 3-6 millimetres. A synthetic resin mass as claimed in Claim 1, characterised in that the synthetic resin mass comprises a polyphenylene ether, a polystyrene, a polypropylene, an acrylonitrile-butadiene-styrene terpolymer, an aromatic polycarbonate, a polyalkylene terephthalate, a polyamide, a polyphenylene sulphide, a polyetherimide or a mixture of two or more of the said polymers.

Inventors: HOL HUBERTUS GE, TIMMERMAN THEODORUS JOHANNUS M, WOLHOFF KORNELIS HENDRIKUS JAC, HOL, HUBERTUS, TIMMERMAN, THEODORUS JOHANNUS, MARIA, WOLHOFF, KORNELIS HENDRIKUS JACOBUS, HOL, HUBERTUS, GE PLASTICS ABS EUROPE B.V.
Applicants: GE PLASTICS ABS EUROP BV, GE PLASTICS ABS EUROPE B.V.
Application year: 1991
Main classification: C08K7
IPC codes: C08K7