Device having a charge transfer device, MOSFETs, and bipolar transistors -- all formed in a single semiconductor substrate

Abstract: A semiconductor device according to the present invention has a semiconductor body (70) of a first conductivity type, three islands (72, 74, 76) of a second conductivity type, formed in the surface of the semiconductor body (70). Two wells (78, 80) of the first conductivity are formed in the first and second islands (72, 74). The device further has a charge transfer device whose back gate is formed of the first well (78), an insulated-gate FET of the first conductivity type whose back gate is formed of the second island (74), an insulated-gate FET of the second conductivity type whose back gate is formed of the second well (80), and a bipolar transistor whose collector is formed of the third island (76). The first island (72) surrounds the first well (78) which serves as back gate of the charge transfer device, and blocks the noise generated in the first well (78). Hence, the other islands (74, 76) are free of the influence of the noise.

Description: The present invention relates to a semiconductor device, comprising a semiconductor body having a semiconductor substrate and an epitaxial layer formed thereon, a first, second, and third island formed in a major surface of the semiconductor body, the second island having a first well and the first, second, and third islands being isolated from each other to prevent noise interference, a first insulated-gate FET of a first conductivity type formed in the second island and having a back gate of a second conductivity type, a second insulated-gate FET of the second conductivity type formed in the first well and having a back gate of the first conductivity type, and a bipolar transistor formed in the third island and having a collector of the second conductivity type. The present invention also relates to a method of manufacturing such a semiconductor device. A semiconductor device of the type outlined above is known from US-A-4 646 124 describing an integrated circuit comprising small signal MOS logic transistors formed in wells that themselves are formed in islands defined by an enclosing isolation wall. In one island a relatively high current carrying bipolar transistor is formed. The island containing the MOS transistors is tied to one DC voltage so that substrate currents caused by the high current in the bipolar transistor are prevented from inducing voltage changes in the MOS transistors by the island surrounding this transistor. Further, in Electronics International, 28 October 1976, pp. 8 and 10, there is described a process that adapts CCD devices to MOS and bipolar peripheral circuits. The proposed approach uses MOS devices for lower frequencies and bipolar devices in higher frequency regions. Further, in US-A-4 253 168 there is described an apparatus for forming one or more sonar beams in response to acoustic energy received by a transducer array. To minimize volume utilization, a plurality of CCD devices are integrated in a single circuit chip with the CCD devices being of progressively smaller length. In particular, half of the CCD devices are folded over to match the other half so that each CCD device has an opposing CCD device both propagating a signal toward a common output diode. Further, in EP-A-0 245 515 there is described a semiconductor device having a substrate and sources and drains of FET transistors or having collectors, bases and emitters of bipolar transistors in a plurality of isolation layers that are electrically isolated in the substrate. A voltage is applied to the substrate or to the plurality of insulation layers. In particular, the voltage falls outside a range in which the voltage applied to the sources and drains or to the collectors, bases and emitters can be varied. Further, in Patent Abstract of Japan, vol. 12, no. 348; & JP-A-63 107 161, there is described a semiconductor device. Here, the object is to achieve a crystallinity which is excellent and provides a high homogeneity of quality in a wafer. To this end an n-type silicon substrate is coated with a thin silicon dioxide formed by a thermal oxidation. The irregularities on the surface thereof are flattened by polishing. Then, the n-type silicon substrate is made thin by polishing so that there is provided a position in the surface for an element isolating region consisting of a silicon dioxide film. An SOI structure in which element regions are isolated by a dielectric body matching a desired element structure is obtained. Further, Patent Abstract of Japan, vol. 12, no. 481; & JP-A-63 199 454, relates to a semiconductor device, in particular a semiconductor device comprising a power device. Here, a semiconductor device has a single crystal layer surrounded by insulating films in a support substrate. In the different crystal islands elements are formed, such as a power device, a thyristor, a resistor or a MOSFET device of the vertical type. In addition, US-A-4 152 715, relates to a silicon base CCD-bipolar transistor compatible method and product where CCD devices and bipolar transistors are formed together on a silicon chip. For the manufacturing of the CCD devices and the bipolar transistors it is proposed to use only one extra single diffusion step in addition to the diffusions used for the provision of the CCD device. Thus, various charge transfer devices are known, among which is a charge-coupled device (hereinafter referred to as "CCD") as in, e.g., US-A-4 646 124. The CCD is formed in a semiconductor substrate, along with N-type channel MOSFETs which constitute various peripheral circuits for the CCD, such as a circuit for switching CCD delay lines, a CCD-driving circuit, a sample-and-hold circuit, an output circuit and a clock-driving circuit. Hitherto, a 12V or 9V power supply has been used to drive the N-type channel MOSFETs. Recently, a 5V power supply is used instead, to save power, to cope with the increasing use of CMOS including MOSFETs, and to match the power-supply voltage of the MOSFETs with that of bipolar transistors formed on a separate chip. When driven by a voltage of 5V, the sample-and-hold circuit and the output circuit, either formed of N-type channel MOSFETs and being an operational amplifier, fail to produce outputs having a sufficient linearity. The poorer the output linearity of these operational amplifiers, the lower the yield of the semiconductor device having the CCD and these peripheral circuits, as is usually proved by die sort test. The CCD delay lines are designed to delay signals by a predetermined period of time. Most circuits for processing the signals thus delay are bipolar transistor ICs which are formed on separate chips. Let us assume that the CCD and the bipolar transistors are formed in the same semiconductor substrate, thus replacing the operational amplifiers having MOSFETs, such as the sample-and-hold circuit and the output circuit, with operational amplifiers comprising the bipolar transistors which operate at higher speed than the MOSFETs. In this case, the operational amplifiers have better output linearity, and the semiconductor device having the CCD and these operational amplifiers can be manufactured with higher yield and can operate with higher efficiency. In addition, the use of the bipolar transistors IC, which processes the signals output by the CCD, results in space merit, reduction of manufacturing cost, increased function, and simplified system. To make the CCD transfer an electrical charge, a transfer clock signal is supplied to the CCD. Some part of this clock signal leaks and makes noise, while being supplied through the semiconductor substrate. The noise adversely influences the bipolar transistors. In view of this, it is far from advisable to form bipolar transistors, together with a CCD, in the same semiconductor substrate. If influenced by the noise, bipolar transistors will fail to exhibit good characteristic, and the semiconductor device comprising the CCD and the bipolar transistors will have but insufficient reliability. Accordingly, it is the object of this invention to provide semiconductor device which comprises a charge transfer device, bipolar transistors, and also MOSFETs on a single semiconductor substrate wherein the characteristics of the active elements can be varied. To achieve this object the semiconductor device of the type outlined above is provided with a second well of the first conductivity type formed in the first island, a charge transfer device of the second conductivity type formed in the second well and having a back gate of a first conductivity type, and a plurality of terminals to apply different potentials to the islands and wells, respectively, so as to change the characteristics of the active elements of the semiconductor device in accordance with design characteristics. Further, to achieve this object according to the invention there is provided a method of manufacturing a semiconductor device, comprising the steps forming a first semiconductor layer on a substrate to obtain a semiconductor body, forming first, second and third islands in a major surface of the semiconductor body, the first, second, and third islands being isolated from each other to prevent noise interference, forming a charge transfer device of a second conductivity type having a back-gate of a first conductivity type in a well in the first island, a first insulated-gate FET of the first conductivity type having a back-gate of the second conductivity type in the second island, a second insulated-gate FET of the second conductivity type in a further well in the second island, and a bipolar transistor having a collector of the second conductivity type in the third island, wherein the first layer is formed on the substrate after a second layer isolating the first, second and third islands from each other is formed on the substrate, and the islands and the wells are formed with a plurality of terminals to variably change the characteristics of the active elements. According to the invention the characteristics of the active elements can be changed in accordance with the design characteristics of the semiconductor device comprising the CCD, the MOSFETs and the bipolar transistor -- all formed in the same substrate. Further, in the first island surrounds the first well which functions as the back gate of the charge transfer device. Hence, the first island blocks the noise generated in the first well, and the noise influences no other island. The device is therefore reliable despite that the charge transfer device and the bipolar transistor are formed on the same chip. Further, the semiconductor body electrically isolates the first, second and third islands from one another. Naturally, the first well and the second well, which are formed in the first island and the second island, respectively, are also electrically isolated from each other. Hence, any FET, whose back gate is one of the islands or one of the wells, can have a back-gate bias which is different from the collector bias of the bipolar transistor whose collector is the third island. This increases the freedom of designing the semiconductor device, and elements having various characteristics can be formed in the same substrate. This invention can be more fully understood from the following detailed description when taken in conjunction with the accompanying drawings, in which: Fig. 1 is a plane view showing the general structure of a semiconductor device according to the embodiment of the present invention, in particular, an element-forming region of the device; Fig. 2 is a sectional view, taken along line 2-2 in Fig. 1; Figs. 3A to 3E are plane views representing the electrode patterns and explaining the steps of manufacturing the device shown in Fig. 1; Figs. 4A to 4J are sectional views, explaining the steps of manufacturing the device shown in Fig. 1, Figs. 4A to 4E being taken along lines 4A-4A to 4E-4D which are shown in Figs. 3A to 3E, respectively; Fig. 5 is a plan view showing the general structure of a semiconductor device, having an element-forming region of the device; Fig. 6 is a sectional view, taken along line 6-6 in Fig. 5; Figs. 7A to 7E are plane views, explaining the steps of manufacturing the semiconductor device shown in Fig. 6; Figs. 8A to 8F are sectional views, explaining the steps of manufacturing the device shown in Fig. 5, Figs. 8A, 8B, 8C, 8D and 8E being taken along lines 8A-8B to 8E-8E shown in Figs. 7A to 7E, respectively; Fig. 9 is a plane view representing the general structure of a semiconductor device, in particular an element-forming region of the device; Fig. 10 is a sectional view, taken along line 10-10 in Fig. 9; Figs. 11A to 11F are sectional views, explaining the steps of a method of manufacturing the device shown in Fig. 9; Figs. 12 is a plane view, showing the unfinished product at the manufacturing step explained with reference to Fig. 11C; Figs. 13A to 13G are sectional views, explaining the steps of a further method of manufacturing the device shown in Fig. 9; and Fig. 14 is a plane view, showing the unfinished product at the manufacturing step explained with reference to Fig. 13D. Several embodiments of the present invention will now be described, with reference to the accompanying drawings. Fig. 1 is a plane view showing the general structure of a semiconductor device according to a embodiment of the present invention. In particular, it shows the element-forming region of the semiconductor device. Fig. 2 is a sectional view, taken along line 2-2 in Fig. 1. As Figs. 1 and 2 show, an N-type silicon epitaxial layer 12 is formed on a P-type silicon substrate 10. A P-type isolation diffusion layer 14 is formed in the layer 12 by diffusing a P-type impurity into the layer 12. As is evident from Fig. 2, the layer 14 extends from the upper surface of the silicon epitaxial layer 12 to the upper surface of the silicon substrate 10, dividing the layer 12 into three N-type islands 16, 18, and 20. P-type wells 22 and 24 are formed in the islands 16 and 18, respectively. An N-channel CCD is formed on the well 22, which serves as back gate of the N-channel CCD. A P-channel MOSFET is formed on the island 18, which serves as back gate of the P-channel MOSFET. An N-channel MOSFET is formed on the well 24, which serves as back gate of the N-channel MOSFET. An NPN bipolar transistor is formed on the island 20, which serves as collector of the NPN bipolar transistor. As is shown in Fig. 1, the N-type island 16 surrounds the well 22 on which the N-channel CCD is formed. Hence, the N-type island 16 blocks the noise generated from the transfer clock signal supplied to the CCD, and the bipolar transistor is free of the influence of that noise. The bipolar transistor operates reliably despite that the bipolar transistor, the CCD, and the MOSFETs are formed in the same substrate 10. The islands 16, 18 and 20 electrically float, and so do the wells 22 and 24. Various potentials are applied to these five regions. More precisely, potentials VDD1, VDD2 and VDD3 are applied to the islands 16, 18, and 20 through terminals 26A, 26B and 26C, respectively, while potentials VDD4 and VDD5 are applied to the wells 22 and 24 through terminals 26D and 26E, respectively. Potential VSS is applied to the substrate 10 via a terminal 26F. The potentials VDD2, VDD4 and VDD5 can be varied, thereby to change the back-gate biases of the P-channel MOSFET, the CCD, and the N-channel MOSFET. Similarly, the potential VDD3 can be varied, thereby to change the collector bias of the NPN bipolar transistor to a value different from the back-gate biases of the P-channel MOSFET, the CCD, and the N-channel MOSFET. Therefore, the characteristics of these active elements can be changed in accordance with the design characteristics of the semiconductor device comprising the CCD, the MOSFETs and the bipolar transistor -- all formed in the same substrate 10. The potential VDD1 is one which can absorb the noise the CCD generates. The potential VDD2 is optimal as the back-gate bias of the P-channel MOSFET. The potential VDD3 is optimal as the collector bias of the NPN bipolar transistor. The potential VDD4 is optimal as the back-gate bias of the N-channel CCD. The potential VDD5 is optimal as the back-gate bias of the N-channel MOSFET. With reference to Figs. 3A to 3E and Figs. 4A to 4J, it will be explained how the semiconductor device shown in Figs. 1 and 2 is manufactured, thus describing the device in greater detail. Figs. 3A to 3E are plan views representing the electrode patterns and explaining the steps of manufacturing the device shown in Fig. 1. Figs. 4A to 4J are sectional views, explaining the steps of manufacturing the device shown in Fig. 1. Figs. 4A to 4E are sectional views taken along lines 4A-4A to 4E-4E which are shown in Figs. 3A to 3E, respectively. In these figures, the components identical to those shown in Figs. 1 and 2 are denoted at the same reference numerals. As is illustrated in Figs. 3A and 4A, the surface region of the P-type silicon substrate 10, which has resistivity of 25 Ω·cm, is heated at about 1000°C and thermally oxidized, thus forming a silicon oxide film 30 having a thickness of about 1 µm. The silicon oxide film 30 is patterned by means of photoetching, thus forming windows 32 in the film 30. Antimony is diffused through these windows 32 into the P-type substrate 10, thereby forming N + -buried layers 34 1 to 34 3 in the substrate 10, the layers 34 1 to 34 3 having a sheet resistance of 20 Ω/□. Then, the silicon oxide film 30 is removed from the substrate 10. Next, as is shown in Figs. 3B and 4B, a photoresist 35 is coated on the upper surface of the resultant structure. A selected portion of the photoresist 35 is removed by means of photoetching, thus forming windows 36. Boron ions are injected through these windows 36 into the substrate 10, thus forming P + -buried layers 38A in the surface of the substrate 10 and also a P + -buried layer 40A in the surface of the N + -buried layer 34 2 . Then, the photoresist 35 is removed from the substrate 10. Then, as is shown in Figs. 3C and 4C, an N-type silicon epitaxial layer 12 containing phosphorus and having resistivity of about 5 Ω·cm is grown to the thickness of about 5 µm, on the upper surface of the resultant structure. While the layer 12 is growing, the impurities diffuse into the layer 12 from the layers 34 1 , 34 2 , 34 3 , 38A and 40A, forming N + -buried layers 34 1 , 34 2 and 34 3 and a P + -buried layer 38 between the substrate 10 and the epitaxial layer 12. These layers 34 1 , 34 2 and 34 3 and 38 have impurity concentrations higher than that of the epitaxial layer 12. Further, a P + -buried layer 40 is formed between the epitaxial layer 12 and the N + -buried layer 34 2 . Further, the surface of the epitaxial layer 12 is subjected to thermal oxidation at 1000°C, thereby forming a silicon oxide film (not shown) having a thickness of about 500 Å and serving as a photoresist pad. Then a photoresist (now shown) is formed on the silicon oxide film, a portion of the photoresist is removed by photoetching, thus forming an opening. Phosphorus ions, for example, are injected through the opening into the epitaxial layer 12, thereby forming a collector region. The remaining photoresist is removed from the silicon oxide film. Next, a photoresist is formed on the silicon oxide film. The photoresist is photo-elected, whereby opening are made in the photoresist. Boron ions, for example, are injected through these openings into the epitaxial layer 12, thereby forming P-type wells and P-type isolation layers in the layer 12. The photoresist is the removed from silicon oxide film. Further, an undoped CVD oxide film (not shown) having a thickness of about 3000 Å is formed on the upper surface of the resultant structure by means of a CVD method. The structure is subjected to cap annealing at about 1190°C, thereby forming, as is shown in Figs. 3D and 4D, an N + -collector region 42 reaching the N + -buried layer 34 3 , a P-type well 22 reaching the N + -buried layer 34 1 , a P-type well 24 reaching the P + -buried layer 40, and P + -type isolation diffusion layers 14 reaching the P + -buried layers 38. The P + -type isolation layers 14 isolate three islands 16, 18, and 20. The island 16 consists of a part of the N-type epitaxial layer 12 and N + -buried layer 34 1 which are electrically combined. The island 18 consists of a part of the N-type epitaxial layer 12 and N + -buried layer 34 2 which are electrically combined. The island 20 consists of a part of the N-type epitaxial layer 12 and N + -buried layer 34 3 which are electrically combined. Further, as is illustrated in Figs. 3E and 4E, a field oxide film 44 having a thickness of about 9000 Å is formed by the known LOCOS method on the upper surface of the resultant structure. Before forming the field oxide film 44, boron or phosphorus can be ion-injected into those surface portions of the structure on which the film 44 is to be formed, thereby to form channel stoppers 46 beneath the field oxide film 44. Next, as is shown in Fig. 4F, the exposed surface portion of the silicon epitaxial layer 12 are thermally oxidized at 950°C, forming a silicon oxide film 48 having a thickness of about 700 Å. This oxide film 48 will be used as the gate insulating film of the MOSFETs and as the first gate insulating film of the CCD. Boron or phosphorus is ion-injected through the film 48 into the upper surface of the structure, thus performing channel-doping. Further, a first polysilicon layer having a thickness of about 4000 Å is formed by the CVD method on the upper surface of the structure. Phosphorus is diffused into the first polysilicon layer at 950°C, using phosphoryl chloride (POCℓ 3 ) as impurity source. The first polysilicon layer is thereby rendered conductive, or made into an N + -type layer. Then, a photoresist is coated on the first polysilicon layer, and the photoresist is photo-etched, thus forming a mask. Using this mask, reactive ion etching (RIE) is performed on the first polysilicon layer. As a result, the first polysilicon layer is patterned, forming the first transfer gate 50 1 of the CCD, the gate 50 2 of the P-channel MOSFET, and the gate 50 3 of the N-channel MOSFET. Then, the silicon oxide film 48 is removed, by applying ammonium fluoride (NH 4 F), using the gates 50 1 , 50 2 and 50 3 as mask. Next, as is shown in Figs. 4G, the exposed surface portions of the silicon layer are thermally oxidized at 950°C, forming a silicon oxide film 52 having a thickness of about 700 Å. Boron ions, for example, are injected the resultant structure, by using the first transfer gate 50 and a photoresist (not shown) as mask, thereby forming a barrier layer (not shown) of the CCD. Further, boron ions were injected into selected portions of the silicon epitaxial layer 12 by means of photoetching, in order to form the base of the NPN bipolar transistor. The structure is annealed at 900°C, forming a P - -inner-base layer 54. Then, a second polysilicon layer having a thickness of about 4000 Å is formed on the upper surface of the resultant structure by, for example, the CVD method. Phosphorus diffused into the second polysilicon layer at 950°C, using phosphoryl chloride (POCℓ 3 ) as impurity source, whereby the second polysilicon layer is made conductive, or becomes an N + -type layer. Then, a photoresist is coated on the second polysilicon layer, and the photoresist is photoetched, thus forming a mask. Using this mask, reactive ion etching (RIE) is performed on the second polysilicon layer. As a result, the second polysilicon layer is patterned, forming the second transfer gates 56 of the CCD. Thereafter, as is shown in Fig. 4H, arsenic ions, for example, are injected into selected portions 58 of the silicon epitaxial layer 12 by means of photoetching, in order to form the N + -emitter of the NPN bipolar transistor, the N + -source/drain of the N-channel MOSFET, and the N + -source/drain of the CCD. Next, the exposed surface portions of the silicon layer are thermally oxidized at 900°C, forming a silicon oxide film 60 on the second transfer gates 56. Boron ions, for example, are injected to selected portions 62 of the silicon epitaxial layer 12 by means of photoetching, in order to form the P + -outer base of the NPN bipolar transistor, the P + -source/drain of the N-channel MOSFET and the N + -source/drain of the CCD. Then, as is shown in Fig. 4I, an interlayer insulator film 64 consisting of a silicon oxide film and a BPS (Boro-Phospho Silicate) glass film is formed on the resultant structure by means of the CVD method. More specifically, the silicon oxide film is formed on the upper surface of the structure, and then the BPS glass film is formed on the silicon oxide film. The silicate glass of the insulator film 64 is melted at about 950°C, thus performing not only glass-flowing but also phosphorous gettering. Simultaneously, the arsenic and boron, both ion-injected, are activated. As a result, there are formed the N + -source/drain layer 58 1 of the CCD, the N + -contact layer 58 2 of the island 16, the N + -source/drain layer 58 3 of the N-channel MOSFET, and the N + -emitter layer 58 4 of the NPN bipolar transistor. Also, the P + -source/drain 62 1 of the P-channel MOSFET, and the P + -outer-base layer 62 2 of the NPN bipolar transistor are formed. Further, photoetching is applied, thereby forming contact holes 66 in the interlayer insulator film 64, exposing the N + layers 58 1 to 58 4 and the P + layers 62 1 and 62 2 . Next, as is illustrated in Fig. 4J, a metal layer made of aluminum-silicon (1%) alloy and having a thickness of about 8000 Å is formed on the upper surface of the resultant structure by means of, for example, spattering. Then, a photoresist is coated on the metal layer, and the photoresist is photo-etched, thus forming a mask. Using this mask, reactive ion etching (RIE) is performed on the metal layer. As a result, metal wirings 68 1 to 68 7 are formed. The two wirings 68 1 the source and drain wirings of the CCD, the wiring 68 2 is the bias wiring of the island 16, the two wirings 68 3 are the source and drain wirings of the P-channel MOSFET, the two wiring 68 4 are the source and drain wirings of the N-channel MOSFET. The three wirings 68 5 , 68 6 and 68 7 are the emitter, base and collector wirings of the NPN bipolar transistor. Forming process is performed at about 450°C, thus imparting desired characteristic to each active element. Thus manufactured is the semiconductor device according to the embodiment of the invention, which is illustrated in Fig. 4J. Not only does this device have the advantages explained with reference to Figs. 1 and 2, but also is it hardly be latched since the P + -buried layer 38 having an impurity concentration higher than that of the isolation diffusion layer 14 is interposed between the P-type silicon substrate 10 and the P-type isolation diffusion layer 14, and since the P + -buried layer 40 having an impurity concentration higher than that of the well 24 is interposed between the N + -buried layer 34 2 and well 24. The NPN bipolar transistor is a vertical-type bipolar transistor comprising a collector which is the N-type island 20, a P-type base 54 which is formed in the island 20, and an N-type emitter 58 4 formed in the base 54. Since the collector, i.e., the N-type island 20, is part of the N-type epitaxial layer 12, the breakdown voltage of the NPN bipolar transistor can be altered merely by changing the thickness of the N-type epitaxial layer 12. Fig. 5 is a plane view showing another general structure of a semiconductor device according to the present invention. In particular, it shows the element-forming region of the semiconductor device. Fig. 6 is a sectional view, taken along line 6-6 in Fig. 5. As is evident from Figs. 5 and 6, N-type semiconductor regions 72, 74, and 76 are formed in the surface of a P-type silicon semiconductor body 70. P-type islands 78 and 80 are formed in the semiconductor regions 72 and 74, respectively. An N-channel CCD is formed on the island 78, which serves as back gate of the N-channel CCD. An N-channel MOSFET is formed on the island 80, which serves as back gate of the N-channel MOSFET. An P-channel MOSFET is formed on the N-type semiconductor region 74, which serves as back gate of the P-channel MOSFET. An NPN bipolar transistor is formed on the semiconductor region 76, which serves as collector of the NPN bipolar transistor. As is shown in Fig. 6, the N-type semiconductor region 72 surrounds the island 78 on which the N-channel CCD is formed. Hence, the N-type semiconductor region 72 blocks the noise generated from the transfer clock signal supplied to the CCD, and the bipolar transistor is free of the influence of that noise. The bipolar transistor operates reliably despite that the bipolar transistor, the CCD, and the MOSFETs are formed in the same semiconductor body 70. The semiconductor regions 72, 74, and 76 electrically float, and so do the islands 78 and 80. Various potentials are applied to these five regions. More precisely, potentials VDD1, VDD2 and VDD3 are applied to the regions 72, 74 and 76 through terminals 26A, 26B and 26C, respectively, while potentials VDD4 and VDD5 are applied to the islands 78 and 80 through terminals 26D and 26E, respectively. Potential VSS is applied to the semiconductor body 70 through a terminal 26F. The potentials VDD1 to VDD5 and the potential VSS can be changed, as in the embodiment shown in Figs. 1 and 2. With reference to Figs. 7A to 7E and Figs. 8A to 8F, it will be explained how the semiconductor device shown in Figs. 5 and 6 is manufactured, thus describing the device in greater detail. Figs. 7A to 7E are plane views representing the electrode patterns and explaining the steps of manufacturing the device shown in Figs. 5 and 6. Figs. 8A to 8F are sectional views, explaining the steps of manufacturing the device shown in Figs. 5 and 6. Figs. 8A to 8F are sectional views taken along lines 8A-8A to 8E-8E which are shown in Figs. 7A to 7E, respectively. The components shown in these figures, which are identical to those shown in Figs. 1 to 6 are denoted at the same reference numerals, and will not be described in detail. First, as is shown in Figs. 7A and 8A, antimony is diffused through the windows 32 formed in a silicon oxide film 30, in the same way as in the first embodiment, is diffused into the P-type substrate 10, thereby forming N + -buried layers 34 1 to 34 3 in the substrate 10, the layers 34 1 to 34 3 having a sheet resistance of 20 Ω/□. Next, as is shown in Figs. 7B and 8B, a photoresist 35 is coated on the upper surface of the resultant structure. A selected portion of the photoresist 35 is removed by means of photoetching, thus forming windows 36. Boron ions are injected through these windows 36 into the P-type semiconductor substrate 10, thus forming highly ion-implanted regions 38A in the surface of the substrate 10, and also a highly ion-implanted region 40A in the surface of the N + -buried layer 34 2 . Then, as is shown in Figs. 7C and 8C, an P-type silicon epitaxial layer 82 containing boron and having resistivity of about 20 Ω·cm is grown to the thickness of about 5 µm, on the upper surface of the resultant structure. While the layer 82 is growing, N + -buried layers 34 1 , 34 2 and 34 3 , and a P + -buried layer 38 are formed between the substrate 10 and the epitaxial layer 82. At the same time, a P + -buried layer 40 is formed between the N + -buried layer 34 2 and the epitaxial layer 82. The P + -buried layers 38 and 40 have impurity concentrations higher than that of the epitaxial layer 82. In the step explained with reference to Figs. 7C and 8C, the silicon substrate 10 and epitaxial layer 82, which are of the same conductivity type, are electrically combined. The combination of the substrate 10 and the layer 82 is equivalent to the semiconductor body 70 shown in Fig. 6. Further, a silicon oxide film (not shown) is formed on the epitaxial layer 82 in the same way as in the embodiment. Then a photoresist (not shown) is formed on the silicon oxide slim, a portion of the photoresist is removed photoetching, thus forming an opening. Phosphorus ions, for example, are injected through the opening into the epitaxial layer 82, to form N + -type isolation layers and a N + -collector region. The remaining photoresist is removed from the silicon oxide film. Next, a photoresist is formed on the silicon oxide film. The photoresist is photo-etched, thereby openings are made in the photoresist. Phosphorus ions, for example, are injected through these openings into the epitaxial layer 82, thereby to form N-type wells in the epitaxial layer 82. The remaining photoresist is removed from the silicon oxide film. Next, a photoresist is formed on the silicon oxide film. The photoresist is photo-etched, thereby opening. Boron ions, for example, are injected into the layer 82 through this opening, thereby to form P + -surrounding diffusion layer. The resultant structure is subjected to cap annealing at about 1190°C, thereby forming, as is shown in Figs. 7D and 8D, a first N + -type isolation layer 84 1 reaching the N + -buried layer 34 1 , a second N + -type isolation layer 84 2 reaching the N + -buried layer 34 2 , and an N-type well 86 1 . Also, an N + -type collector region 42 reaching the N + -buried layer 34 3 and a P + -type well 86 2 are simultaneously formed. Further, a P + -type surrounding diffusion layer 88 reaching the P + -buried layer 38 is formed at the same time. The N + -type isolation layer 84 1 surrounds and contacts the N + -buried layer 34 1 , and the N + -type isolation layer 84 2 surrounds and contacts the N + -buried layer 34 2 . Thus, the N + -type isolation layers 84 1 and 84 2 divide the epitaxial layer 82 into two islands 78 and 80, which are located on the N + -buried layer 34 1 and 34 2 , respectively. The isolation layer 84 1 and the buried layer 34 1 , which are of the same conductivity type, are electrically combined and are equivalent to the N-type semiconductor region 72 shown in Fig. 6. Similarly, the isolation layer 84 2 and the buried layer 34 2 , which are of the same conductivity type, are electrically combined and are equivalent to the N-type semiconductor region 74 shown in Fig. 6. Further, the well 86 2 and the buried layer 34 3 are electrically combined and are equivalent to the N-type semiconductor region 76 shown in Fig. 6. Further, as is illustrated in Figs. 7E and 8E, a field oxide film 44 having a thickness of about 9000 Å is formed by the LOCOS method of the known type. Next, as is shown in Fig. 8F, the CCD whose back gate is the island 78, the N-channel MOSFET whose back gate is the island 80, the P-channel MOSFET whose back gate is the well 86 1 , and the NPN bipolar transistor whose collector is the well 86 2 are formed. Thus manufactured is the semiconductor device according to the modified embodiment of the invention, which is illustrated in Fig. 8F. Not only does this device have the same advantages as the embodiment, but also is it advantageous in two respects. First, the portion 84 2 A of the isolation layer 84 2 , which has an impurity concentration higher than that of the well 86 1 , prevents the wells 86 1 and the island 80 from being latched up, and the MOSFETs operate with high reliability. Secondly, the P + -type surrounding layer 88, which has an impurity concentration higher than that of the epitaxial layer 82, prevents the N-type semiconductor regions 72, 74 and 76 from latching up one another, and the semiconductor device therefore operates with high reliability. Fig. 9 is a plane view showing the general structure of a semiconductor device according to another modified embodiment of the present invention. In particular, it shows the element-forming region of the semiconductor device. Fig. 10 is a sectional view, taken along line 10-10 in Fig. 9. As is shown in Figs. 9 and 10, an insulating film 102 made of silicon oxide is formed on a silicon substrate 10. As is shown in Fig. 10, an N-type or P-type silicon layer 104 is formed on the insulation film 102. The insulating film 102 divides the silicon layer 104 into three islands 106, 107 and 112. An N-channel CCD is formed on the island 106, which serves as back gate of the N-channel CCD. The island 107 consists of an N-type semiconductor region 108 and a P-type semiconductor region 110. A P-channel MOSFET is formed on the N-type semiconductor region 108, which serves as back gate of the P-channel MOSFET. An N-channel MOSFET is formed on the P-type semiconductor region 110, which serves as back gate of the N-channel MOSFET. An NPN bipolar transistor is formed on the island 112, which serves as collector of the NPN bipolar transistor. As is shown in Fig. 10, the insulating film 102 surrounds the semiconductor region 106 on which the CCD is formed. Hence, the film 102 blocks the noise generated from the transfer clock signal supplied to the CCD, and the NPN bipolar transistor is free of the influence of that noise. The bipolar transistor operates reliably despite that the bipolar transistor, the CCD, and the MOSFETs are formed in one silicon layer 104 which is formed on the semiconductor substrate 100. The islands 106 and 112 which are isolated by the film 102, and the semiconductor regions 108 and 110 which are isolated by a P-N junction, are electrically floating. Potentials VSS1 and VSS2 are applied to the island 106 and the region 110 through terminals 26G and 26I. Potentials VDD6 and VDD7 are applied to the region 108 and the island 112 through terminals 26H and 26J. These potentials VSS1, VSS2, VDD6, and VDD7 can be changed, as in the first embodiment. With reference to Figs. 11A to 11F, Fig. 12, Figs. 13A to 13G, and Fig. 14, it will be explained how the semiconductor device shown in Figs. 9 and 10 is manufactured, thus describing the device in greater detail. Figs. 11A to 11F are plane views representing the electrode patterns and explaining the steps of manufacturing the device shown in Figs. 9 and 10. Fig. 12 is a plan view of the structure at the manufacturing step explained with reference to Fig. 11C. The components shown in these figures, which are identical to those shown in Figs. 9 and 10 are denoted at the same reference numerals, and will not be described in detail. First, as is illustrated in Fig. 11A, the surface of the first silicon substrate 100 is thermal oxidized, thus forming a silicon oxide layer 102A. Then, as is shown in Fig. 11B, the exposed surface of the silicon oxide layer 102A is mirror-polished. In the meantime, a second silicon substrate 104A is prepared which has a mirror-polished surface. The second substrate 104A is jointed to the first substrate 102A, with its mirror surface contacting the mirror surface of the oxide layer 102A. The resultant structure is heated, whereby the first silicon substrate 100 and the second silicon substrate 104A are bonded together. The first substrate 100 can either be an N-type one or a P-type one. Further, it can be replaced by one made of insulating material. Moreover, the second substrate 104A can either be an N-type one or a P-type one. Next, as is shown in Figs. 11C and 12, a groove 114 is formed in the second substrate 104 by means of, for example, photoetching, thus exposing the selected portions of the oxide layer 102A. This groove 114 divides the second substrate 104 into three islands 106, 107, and 112. Further, as is shown in Fig. 11D, a CVD-silicon oxide film on the upper surface of the resultant structure by means of a CVD method. RIE is performed, thus etching back the CVD-silicon oxide film and, subsequently, filling the groove 114 with the CVD silicon oxide 102B. Thereafter, in the case where the substrate 104A is of N type, boron ions are injected into the islands 106 and 107, thereby to render the island 106 a P-type island and to form a P-type semiconductor region in the island 107. Also, boron ions are injected into that portion of the island 112 which is near the oxide layer 102A, to form an N + -type buried layer. Next, phosphorus ions are injected into the island 112, in order to form an N + -type collector region. The resultant structure is heat-treated, whereby the island 106 is changed into a P-type one, a P-type semiconductor region 110 is formed in the island 107, and an N + -type buried layer 116 and a collector region 118 are formed in the island 112. Then, as Fig. 11F shows, the CCD whose back gate is the island 106, the P-channel MOSFET whose back gate is the N-type semiconductor region 108, the N-channel MOSFET whose back gate is the P-type semiconductor region 110, and the NPN bipolar transistor whose collector is the island 112 are formed in the same way as has been explained with reference to Figs. 4F to 4J. The method described with reference to Figs. 11A to 11F is a method of manufacturing the semiconductor device. In the semiconductor device shown in Fig. 11F, the substrate 104A can be a P-type one. If this is the case, phosphorus ions are injected into the islands 107 and 112, thereby changing the island 112 into an N-type one and forming an N-type semiconductor region 108 in the island 107. As a result, a semiconductor device identical in structure to the device illustrated in Fig. 11F will be manufactured. Figs. 13A to 13G are sectional views, explaining the steps of a second method of manufacturing a semiconductor device. More precisely, Figs. 13A to 13G are sectional views explaining the steps of the manufacturing the device, and Fig. 14 is a plan view showing the structure obtained at the step explained with reference to Fig. 13D. The components shown in these figures, which are identical to those shown in Figs. 9 to 10 are denoted at the same reference numerals, and will not be described in detail. First, as is shown in Fig. 13A, oxygen ions is injected into a first P-type silicon substrate 100, thereby forming an oxygen-injected layer 120. Next, the resultant structure is heat-treated, whereby the oxygen-injected layer 120 changes to a silicon oxide layer 102A as is illustrated in Fig. 13B. Then, antimony is diffused into a selected portion of the substrate 100 in the same way as is explained with reference to Fig. 4B. Further, as is shown in Fig. 13C, a P-type or N-type silicon epitaxial layer 104B is made to grow on the substrate 100, by the same method as has been explained with reference to Fig. 4C or 8C. As is illustrated in Figs. 13D and 14, a groove 114 is formed in the epitaxial layer 104B and the surface region of the substrate 100, by the same method as has been explained with reference to Fig. 11C. This groove 114 reaches the upper surface of the oxide layer 102A, and divides the epitaxial layer 104B into three islands 106, 107, 112. Further, as is shown in Fig. 13E, the groove 114 is filled with CVD silicon oxide 102B by the same method as has been explained with reference to Fig. 11D. In the semiconductor device shown in Fig. 13E, the epitaxial layer 104B can be an N-type one or a P-type one. If the layer 104B is of N type, the island 106 is changed to a P-type one, a P-type semiconductor region 11 is formed in the island 107, and an N + -type buried layer 116 and a collector region 118 are formed in the island 112. Then, as Fig. 13G shows, a CCD whose back gate is the island 106, a P-channel MOSFET whose back gate is the N-type semiconductor region 108, an N-channel MOSFET whose back gate is the P-type semiconductor region 110, and an NPN bipolar transistor whose collector is the island 112 are formed in the same way as has been explained with reference to Figs. 4F to 4J. Thus manufactured is the semiconductor device of the invention, which is illustrated in Fig. 13G. This device have the same advantages as the other devices. Although no N-type semiconductor regions are formed which surround the CCD located in the island 106, each of the other islands 107 and 112 is free of the influence of the noise generated by the CCD. This is because the CVD-silicon oxide layer 102B has very little capacitance. There are two alternative methods of imparting little capacitance to the layer 102B. The first is to make the layer 102B narrow. The second is to bury a polysilicon layer in the CVD-silicon oxide layer 102B.

Claims: Semiconductor device, comprising: a) a semiconductor body having a substrate (10; 70; 100) and and epitaxial semiconductor layer (12; 82; 104B) formed thereon, b) a first (16; 72; 106), second (18; 74; 107), and third island (20; 76; 112) formed in a major surface of the semiconductor body, the second island (18; 74; 107) having a first well (24; 80; 110), and the first, second, and third islands being isolated from each other to prevent noise interference, c) a first insulated-gate FET of a first conductivity type (P) formed in the second island (18; 74; 107) and having a back gate of a second conductivity type (N), d) a second insulated-gate FET of the second conductivity type (N) formed in the first well (24; 80; 110) and having a back gate of the first conductivity type (P), and e) a bipolar transistor formed in the third island (20; 76; 112) and having a collector of the second conductivity type (N), wherein f) a second well (22; 78; 106, 108, 110) of the first conductivity type formed in the first island (16; 72; 106), g) a charge transfer device (CCD) of the second conductivity type (N) formed in the second well (22; 78; 106) and having a back gate of a first conductivity type (P), and h) a plurality of terminals (26A-E; 26G-J) to apply different potentials (VDD1-VDD5; VSS1, VSS2, VGG6, VDD7) to the islands (16-20; 72-76; 106-112) and wells (22-24; 78-80; 106-110), respectively, so as to change the characteristics of the active elements of the semiconductor device in accordance with design characteristics. Semiconductor device according to claim 1, characterized in that the first, second and third islands (16-20; 72-76) have first, second and third of said terminals (26A-26C) to which potentials (VDD1-VDD3) are to be applied, and that the first and second wells (22, -24; 78-80) have fourth and fifth of said terminals (26D-26E) to which potentials (VDD4-VDD5) are to be applied, the potentials (Vdd1-Vdd5) being different from each other. Semiconductor device according to claim 1, characterized in that the first (16; 72), second (18; 74) and third (20; 76) islands are isolated from each other by a pn junction. Semiconductor device according to claim 2, characterized in that a buried layer (34 1 ) of the second conductivity type (N) is provided at the bottom of the first island (16; 72) and additional buried layers (34 1 , 34 3 ) of the second conductivity type (N) are provided at the bottom of the second and third island (18, 20; 74, 76), respectively. Semiconductor device according to claim 1, characterized in that the first (106), second (107) and third (112) islands are isolated from each other by an insulator (102B). Semiconductor device according to claim 5, characterized in that an insulation layer (102A) is formed at least between the bottom of the first island (16; 72) and the substrate (100). Semiconductor device according to claim 6, characterized in that the insulation layer (102A) also extends below the bottom side of the second and third island (18, 20; 74, 76). Method of manufacturing a semiconductor device, comprising the steps: a) forming a first semiconductor layer (12; 82; 104) on a substrate (10; 70; 100) to obtain a semiconductor body (10, 12; 70, 82; 100, 104), b) forming first (16; 72; 106), second (18; 74; 107) and third islands (20; 76; 112) in a major surface of the semiconductor body, the first, second, and third islands (16-20; 72-76; 106-112) being isolated from each other to prevent noise interference, c) forming a charge transfer device (CCD) of a second conductivity type (N) having a back-gate of a first conductivity type (P) in a well (22; 78; 106) in the first island (22; 78; 106), a first insulated-gate FET of the first conductivity type (P) having a back-gate of the second conductivity type (N) in the second island (18; 74; 107), a second insulated-gate FET of the second conductivity type (N) in a further well (24; 80; 110) in the second island, and a bipolar transistor having a collector of the second conductivity type (N) in the third island (20; 76; 112), wherein d) the first layer (12; 82; 104) is formed on the substrate (10; 100) after a second layer (34 1 , 34 2 , 34 3 ; 102A) isolating the first (16; 72; 106), second (18; 74; 107) and third islands (20; 76; 112) from each other is formed on the substrate (10; 70; 100), and e) the islands (16-20; 72-76; 106-112) and the wells (22-24; 78-80; 106-110) are formed with a plurality of terminals (26A-E; 26G-J) to variably change the characteristics of the active elements. Method of manufacturing a semiconductor device according to claim 8, characterized in that the second layer (34 1 , 34 2 , 34 3 ) is formed as a buried layer of the second conductivity type (N). Method of manufacturing a semiconductor device according to claim 8, characterized in that the second layer (102A) is formed as an insulator.

Inventors: KIHARA KAZUO, TAGUCHI MINORU, KIHARA, KAZUO, TAGUCHI, MINORU, KIHARA, KAZUO, C/O INTELLECTUAL PROPERTY DIV., TAGUCHI, MINORU, C/O INTELLECTUAL PROPERTY DIV.
Applicants: TOSHIBA KK, KABUSHIKI KAISHA TOSHIBA
Application year: 1991
Main classification: H01L27
IPC codes: H01L27, H01L21, H01L29