Cemented carbide body for rock drilling, mineral cutting and highway engineering

Abstract: The invention relates to a coated cemented carbide body for rock drilling having a substrate containing at least one metal carbide and a binder metal and an at least partly covering coating comprising at least one diamond- or cBN- layer applied by CVD- or PVD-technique. The cemented carbide body has a core of cemented carbide containing eta-phase surrounded by a surface zone of cemented carbide free of eta-phase.

Description: The present invention relates to a cemented carbide body provided with a diamond coating applied by CVD- or PVD-technique to be used in tools for drilling of rock and mineral. The cemented carbide body has an eta-phase containing core surrounded by a zone free of eta-phase. Much effort has been devoted to improving both the wear resistance and the toughness of cemented carbide bodies. The wear resistance is important to prevent the inserts from simply wearing away during rock drilling. Toughness is important to avoid inserts breaking off due to the high impact loads experienced in drilling. In EP-A-0182759 it has been shown that an increased strength was obtained in sintered bodies of cemented carbide being used in tools for rock drilling, but also in wear parts by manufacturing said sintered body so that its core comprises a fine-grained eta-phase, M 6 C (e.g. Co 3 W 3 C) and/or M 12 C (e.g. Co 6 W 6 C), embedded in normal alpha (WC) + beta (Co binder phase) structure at the same time as the sintered body has a surrounding surface zone which consists only of alpha + beta-phase. Furthermore, said surface zone has an outer part with low content of beta-phase (binder phase), and an inner part - between the outer part and the eta-phase containing core - which has a high content of binder phase. In EP-A-0 246 211 it has been shown that the above mentioned structure in cemented carbide cutting tool inserts have shown highly improved cutting performance in chipforming machining, milling and turning, compared to conventional cemented carbide cutting inserts. Inserts according to said invention may further be coated with one or more wear resistant layers. Diamond and cubic boron nitride coatings can be applied on cemented carbide bodies by sintering in the area of high temperature and high pressure in which diamond or cBN are stable. Such coatings are often referred to as high pressure coatings. Another more recent development of cemented carbide bodies for rock drilling and chipforming machining has been the use of diamond coatings deposited by CVD or PVD-technique at low pressure on such bodies. This low pressure synthesis of diamond coatings from vapour phase using a gas mixture of hydrogen and a hydrocarbon was first reported in 1977 by Derjaguin and his coworkers in Moscow. Their findings were later confirmed by a team of Japanese scientists and their first publications in 1982-3 marked the onset of an intense worldwide research effort in CVD diamond synthesis. It has now been shown that high quality diamond coatings can be grown on a wide range of substrates by a number of different deposition techniques. The growth rate, microstructure and properties of the diamond coating can be controlled by variation of the process parameters, in particular by the use of different gas mixtures which may include compounds containing oxygen, nitrogen, boron and/or halogenes but also different inert gas additions. The amount of papers, patents and patent applications in the area in question numbers in thousands. U.S. patent No. 4,707,384 is a relatively old patent which in addition contains a reference list of the early work in CVD diamond. Some of the more recent patent publications are US 4,731,296 and EP 272 418 just to mention a few. The CVD diamond deposition process and the resulting coating adhesion are both strongly influenced by the surface characteristics of the substrate. Formation of voids and non-diamond material at the coating/substrate interface in combination with high compressive stresses in the coating are believed to be the main reason for poor adhesion. Formation of high residual stresses (compressive) is partly due to the low coefficient of thermal expansion of diamond. Surprisingly, it has now been found that cemented carbide bodies manufactured in such a way that they contain a core of cemented carbide containing eta-phase surrounded by a zone free of eta-phase with a coating of diamond applied by CVD- or PVD-technique show highly improved wear resistance and toughness in rock drilling applications compared with conventional diamond coated cemented carbide bodies. Fig 1 shows a cross section of a cemented carbide body according to the present invention. A means cemented carbide comprising alpha-, beta- and eta-phase, B(=B1+B2) means cemented carbide containing alpha- and beta-phase, B3 is a possible intermediate layer and C is the diamond coating. According to the invention there is now provided a cemented carbide body for rockdrilling purposes as claimed in claim 1. The diamond (or cBN) layer(s) is/are deposited by CVD- or PVD-methods. The non-diamond layers include refractory metals such as W, Ta, Zr and Mo, other pure elements such as B and Si, carbides such as WC, SiC, B 4 C and TaC, nitrides such as Si 3 N 4 , oxides and/or borides. In order to increase the adhesion of the innermost diamond or cBN layer to the substrate there may be respectively one or more non-diamond or non-cBN interlayers, B3, between the substrate and the diamond or cBN layer. The outermost layer may be a diamond or cBN layer or a non-diamond or non-cBN layer. The cemented carbide body shall have a core, A, comprising alpha-, beta-, eta- and possibly gamma-phase. The eta-phase in the core shall be finely distributed, usually with a grain size of 0.5-20 µm, preferably 1-10 µm, and the content of eta-phase shall be at least 2 % by volume, preferably at least 10 % by volume, but at the most 60 % by volume, preferably maximally 35 % by volume. The thickness of the eta-phase containing core A shall be 10-95 % preferably 30-65 % of the width of the cemented carbide body to make good results obtainable. In a preferred embodiment the zones free of eta-phase shall have a content of binder phase i.e. in general a content of cobalt in zone B2 of 0.1-0.9 preferably 0.2-0.7 of the nominal content of the binder phase and the binder phase content shall increase in the direction towards the core up to a maximum of at least 1.2 preferably 1.4-2.5 of the nominal content of binder phase. The width of the zone with reduced binder-phase content, B2, shall be 0.2-0.8 preferably 0.3-0.7 of the width of the zone free of eta-phase (B1 and B2) but at least 0.4 mm and preferably at least 0.8 mm. The binder-phase in the surface zone of the cemented carbide body may be removed before the diamond coating is deposited by chemical or electrolytical etching, by ion etching, by mechanical treatment such as blasting, by heat treatment under slightly decarburizing conditions or in vacuum. The cemented carbide may in addition contain <5% by weight of other cubic carbides, whiskers of refractory material or coated or uncoated particles of other hard refractory material such as SiC, TiB 2 etc or mixtures thereof. The diamond layer can be deposited according to CVD- or PVD-methods known in the art such as hot filament, DC, RF and MW plasmas, hollow cathode and arc jet discharges (DC, RF and MW), flame torch etc. In order to improve the properties of the diamond coating dopants such as boron may be added during the deposition to increase the thermal stability. The reason for the improvement of the properties of the diamond coated cemented carbide body according to the invention is believed to be a favourable stress condition as a result of the eta-phase containing core and the binder-phase distribution in the zone free of eta-phase. This favourable stress pattern is the result of the lower content of binder phase in the outer part of the zone free of eta-phase in relation to the inner part which will lead to the formation of compressive stresses in the cemented carbide in the zone nearest to the coating interface. This has a positive effect upon the strength and the toughness of the composite body and the reduced coefficient of thermal expansion in the surface zone of the cemented carbide due to its high content of hard constituents also leads to an improved thermal matching between the coating and cemented carbide body. An increase of the thermoshock resistance is also obtained which results in a reduction of the initiation and growth of thermal cracks. This can be explained by the different levels of thermal expansion of the two zones in the part free of eta-phase. The outer binder phase depleted zone has a smaller thermal expansion than the inner one rich of binder phase. Tools according to the invention can be used for percussive, rotary crushing and cutting rock drilling. Tools for cutting of asphalt are also included. More particularly the invention relates to the field of roller cone type bits and percussion type bits. The invention is particularly useful in tools for oil and gas drilling, geothermal drilling, pilot hole drilling, blast hole drilling etc. as well as in bits for drilling in oil and gas applications, methane drainage etc. Example 1 A diamond coating was deposited directly on cemented carbide buttons for percussive rock drilling using a tantalum hot filament reactor, equipped with an additional heating furnace. The nominal composition of the cemented carbide was 6 % Co and 94 % WC and with an eta-phase containing core surrounded by a surface zone free of eta-phase with a low cobalt content (3%) at the surface and a higher Co-content in a zone close to the eta-phase core. For comparative purposes buttons with the same nominal composition with homogeneous structure and no eta-phase were also coated. The deposition conditions were as follows: Gas composition: 0.8 % methane in hydrogen Pressure: 20 Torr (= 2666 Pa) Gas flow rate: 2000 ml/min Furnace temperature: 800°C Deposition time: 40 h Filament temperature: 2000°C A well-facetted, crystalline coating of 25-30 µm thickness was obtained. Example 2 A diamond coating was deposited on buttons for percussive rock drilling according to Example 1 but with a 4 µm coating of tungsten as an intermediate layer. The tungsten layer was deposited using standard CVD-technique using a gas mixture of WF 6 , H 2 and Ar. Diamond deposition conditions were in this example: Gas composition: 0.8 % ethanol in hydrogen Pressure: 15 Torr (= 2000 Pa) Gas flow rate: 4 l/min Furnace temperature: 865 °C Deposition time: 18 h Filament temperature: 2200°C A diamond coating of 20-25 µm thickness was obtained. Example 3 In a percussive drilling test in a quartzite quarry the penetration rate and the life of bits with buttons according to the invention were compared to bits of prior art. The bit had a special and strong construction for use in very hard rocks (Heavy Duty Design) with six buttons on the periphery according to the following: Bit A: Buttons according to the invention from Example 1. Bit B: Buttons according to the invention from Example 2. Bit C: Coated comparative buttons of Example 1. Bit D: Uncoated buttons corresponding to bits A and B. Bit E: Uncoated buttons corresponding to Bit C. Test data: Application: Bench drilling in very abrasive quartzite Rock drilling: COP 1036 Drilling rig: ROC 712 Impact pressure: 190 bar Stroke position: 3 Feed pressure: 70-80 bar Rotation pressure: 60 bar Rotation: 120 r.p.m Air pressure: 4.5 bar Hole depth: 6-18 m RESULTS Bit Number of bits Ave life, m Average penetration m per minute A 2 436 1.5 B 2 405 1.5 C 2 280 1.3 prior art D 2 180 1.2 prior art E 2 130 1.1 prior art The average life of Bit C was limited because of premature flaking. Example 4 A diamond coating was deposited directly on buttons for rotary crushing rock drilling. The nominal composition of the buttons was 10 % Co and 90 % WC and with an eta-phase containing core surrounded by a surface zone free of eta-phase with a low cobalt content (5%) at the surface and a higher Co-content in a zone close to the eta-phase core. For comparative purposes buttons with the same nominal composition with homogeneous structure and no eta-phase were also coated. The buttons were pretreated by immersion in an ultrasonic 1 µm diamond slurry for 30 minutes in order to enhance nucleation during diamond deposition. A 1.5 kW microwave plasma CVD reactor was used with an independent heating stage. The deposition conditions were as follows: Gas composition: 2 % methane in hydrogen Pressure: 30 Torr (= 4000 Pa) Gas flow rate: 1000 ml/min Substrate temperature: 805 °C Deposition time: 24 h A microcrystalline coating of 18-24 µm thickness was obtained. Raman spectroscopy revealed that the coating had a strong 1332 cm-1 peak in spite of its microcrystalline appearance. Example 5 A wear test was performed with roller bits in an open-cut copper mine. The roller bits were of type 9 7/8" CS with spherical buttons. The diameter of all of the buttons was 12 mm. For one roller bit the buttons according to the invention were placed in each third position of the buttons in row 1. Three types of roller bits were used in the test: Bit A: Buttons according to Example 4 were placed as above and in the excepted positions in row 1 uncoated buttons corresponding to Example 4 were placed. In all other positions comparative buttons of Example 4 were placed. Bit B: Comparative buttons of Example 4 in all positions. Bit C: Uncoated buttons corresponding to Example 4 in row 1 and comparative buttons of Example 4 in all other rows. The wear was measured of all buttons after 800 BM. The drilling data were as follows: Drill rig: 2 pieces BE45R Feed: 50-60000lbs RPM: 60-85 Hole depth: 18-20 m Type of rock: Biotit gneiss, mica schist Results: Bit A: Row 1: Buttons according to the invention: no measurable wear but one button was missing, no flaking Uncoated buttons: Average wear: 1.9 mm Row 2: Average wear: 2.4 mm Row 3: Average wear: 2.1 mm Average penetration: 21 m/h. Bit B: Row 1: Average wear: 3.2 mm Row 2: Average wear: 2.8 mm Row 3: Average wear: 2.4 mm Average penetration: 16 m/h Bit C Row 1: Average wear: 2.6 mm Row 2: Average wear: 2.3 mm Row 3: Average wear: 2.1 mm Average penetration: 18 m/h It is obvious that the wear resistance of the buttons is much improved using diamond coated cemented carbide according to the invention. Example 6 A diamond coating was deposited directly on buttons for highway engineering. The nominal composition of the buttons was 10 % Co and 90 % WC and with an eta-phase containing core surrounded by a surface zone free of eta-phase with a low cobalt content (5%) at the surface and a higher Co-content close to the eta-phase core. For comparative purposes buttons with the same nominal composition with homogeneous structure and no eta-phase were also coated. The buttons were pretreated by immersion in an ultrasonic 1 µm diamond slurry for 30 minutes in order to enhance nucleation during diamond deposition. A 1.5 kW microwave plasma CVD reactor was used with an independent heating stage. The deposition conditions were as follows: Gas composition: 4 % methane and 1.7 % oxygen in hydrogen Pressure: 40 Torr (= 5333 Pa) Gas flow rate: 2000 ml/min Substrate temperature: 885 °C Deposition time: 16 h A nicely facetted, crystalline coating of 15-18 µm thickness was obtained. Raman spectroscopy revealed that the coating had a strong 1332 cm-1 peak in spite of the high methane concentration used. The oxygen addition also had a positive effect on growth rate. The coating adhered well to the substrate. Example 7 In a cutting performance/wear behaviour test in the branch of highway engineering, 800 m 2 of asphalt was milled without preheating. The test was performed with three different grades of cutting tips under the following conditions: Machine: Arrow CP 2000 road planing machine. The machine was four wheel driven, hydraulic and equipped with automatic control system of the cutting depth. Data of the cutting drum: Width: 2 m Diameter including tools: 0.95 m Tool speed: 3.8 m/s Cutting depth: 80 mm During the test 60 tools of the totally 166 tools around the drum were test variants. 20 tools of each grade were placed in pairs uniformly distributed around the drum. All of the tips had a height of 17 mm and a diameter of 16 mm. If test tip or normal tip failed the tool was replaced immediately by a standard tool of a conventional grade. Results Number of tools Type 1 Cutting tips according to Example 6 Average wear: 1.1 mm Two replaced 20 Type 2 Uncoated cutting tips according to Example 7. Average wear: 3.2 mm Three replaced 20 Type 3 Comparative tips of Example 6 with a nominal content of 10 % Co. Average wear: 4.8 mm Six replaced 20 Type 4 Conventional tools with 9.5 % Co No measurements were made on these tools 106 The results of type 1 were uneven because eight of the tools had undamaged diamond layers. Two had lost the tips due to the weariness of the steel body. The rest of the tools was partly covered with diamond after the test. Undoubtly, the cutting tips according to the invention have shown the best results. Example 8 A diamond coating was deposited on cemented carbide buttons used for percussive rock drilling with an eta-phase core using the experimental conditions described in Example 1 with the exception that WF 6 was introduced in the reactor for 15 min after 8, 16, 24 and 32 hours at a concentration of 1.6%. This resulted in well adherent diamond coating of 35-40 µm thickness with four thin interlayers of WC/WC x and a reduced grain size as compared to Example 1.

Claims: A coated cemented carbide body for rock drilling having a substrate containing at least one metal carbide and a binder metal and being at least partly covered by a coating comprising at least one diamond- or cBN-layer deposited by CVD- or PVD-methods, characterized in, that the cemented carbide body has a core of cemented carbide containing eta-phase and a surface zone of cemented carbide free of eta-phase, and that in the case it has a coating of one diamond or one cBN layer the thickness of said one diamond or said one cBN layer is 15 - 300 µm or that in the case it has a coating of several diamond layers or several cBN layers separated respectively by non-diamond or non-cBN layers, said coating has a total thickness of 35 - 300 µm. Cemented carbide body according to claim 1, characterized in, that the binder phase content in a zone close to the eta-phase containing core is higher than the nominal binder phase content. Cemented carbide body according to claim I or 2, characterized in, that the binder phase content in the surface of said body is 0.1 - 0.9 of the nominal binder phase content.

Inventors: EDERYD STEFAN, SOEDERBERG STAFFAN, EDERYD, STEFAN, SOEDERBERG, STAFFAN, Söderberg, Staffan
Applicants: SANDVIK AB, SANDVIK AKTIEBOLAG
Application year: 1991
Main classification: C23C16
IPC codes: C23C16, C23C14, C22C29