Cosmetic

Abstract: Cosmetics comprising a fluorine compound-treated powder, and a liquid perfluoro organic compound are disclosed. These cosmetics are excellent in water repellency, water resistance, sebum resistance and oil resistance, prevent cosmetic components from the removal due to sweat or sebum, show a good spreadability on the skin and give a desirable feel at the use, for example, a moist and refreshing feel.

Description: FIELD OF THE INVENTION This invention relates to a cosmetic. More particularly, it relates to a cosmetic which is excellent in water repellency and water resistance, further has an oil resistance, prevents cosmetic components such as pigments from the removal due to sweat or sebum and thus gives long-lasting makeup effect. BACKGROUND OF THE INVENTION Many water and oil repellent powders obtained by treating powders with a fluorine compound have been known as disclosed, for example, in JP-A-55-167209 (the term "JP-A" as used herein means an "unexamined published Japanese Patent Application"), JP-A-62-250074, JP-A-1-180811 and U.S. Patent 3,632,744. On the other hand, there has been required cosmetics, in particular, makeup cosmetics, which are excellent in, for example, water repellency and long-lasting makeup effect. When it is attempted to blend an oil commonly employed in these cosmetic products with a powder surface-treated with a fluorine compound in order to improve water repellency, however, the powder cannot be uniformly dispersed in the oil and thus any cosmetic having a good water repellency can be hardly obtained. Accordingly, there has been required to develop a cosmetic, wherein a powder is uniformly dispersed, having a good water repellency, a good water resistance and a good long-lasting makeup effect. On the other hand, powders have been added to cosmetics in order to color the skin or hair, to cover spots and freckles and to protect the skin from, for example, UV rays. In particular, an emulsified cosmetic, which shows a good feel and multi-functions, is blended with a powder to thereby give various cosmetic products including emulsified foundations, UV-protective emulsions and creams. Recently, hydrophobic powders and hydrophobic-treated powders have been used in order to improve the adhesiveness to the skin and to impart water (sweat) resistance. When such a hydrophobic powder is to be stably blended with an emulsified cosmetic, however, it is required to thicken an oily phase used as a dispersion medium or to increase the amount of an emulsifier or a dispersant. Thus it is very difficult to obtain a product which shows a good feel and sustains powders in a stable state. Further, in recent years, it has been attempted to use liquid perfluoro organic compounds in order to impart sebum and oil resistance to cosmetics, to make the skin or hair moist and smooth and to protect the skin and hair, as disclosed, for example, in JP-A-61-234928 and JP-A-63-107911. However, these perfluoro organic compounds are incompatible with other components commonly employed in cosmetics and thus it is difficult to obtain a stable emulsified cosmetic by using them. Accordingly, there has been required to develop an emulsified cosmetic which has the desired characteristics of a liquid perfluoro organic compound and a hydrophobic powder, shows a good feel at the application and remains stable. On the other hand, silicone oils, which have a smooth feel at the application compared with hydrocarbon oils and a good water repellency, have been frequently employed. In particular, a volatile silicone oil is used in cosmetics since it shows a good spreadability on the skin, a good adhesiveness due to the volatilization, and a high resistance against sweat. However, conventional cosmetics comprising a silicone oil is disadvantageous in that cosmetic components are easily removed by sebum and that they lack a moist feel at the application. Accordingly, it is an object of the present invention to provide a cosmetic which is excellent in water repellency, water resistance, sebum resistance and oil resistance, prevents cosmetic components such as pigments and UV absorbers from the removal due to sweat or sebum, shows a good spreadability on the skin and gives a desirable feel at the application, for example, a moist and refreshing feel. SUMMARY OF THE INVENTION Under these circumstances, the present inventors have conducted extensive studies. As a result, they found that a cosmetic, in which a powder is uniformly dispersed in an oil, having a markedly improved effect of preventing cosmetic components such as pigments from the removal due to sebum and an improved long-lasting makeup effect can be obtained by using a fluorine compound-treated powder in combination with a liquid perfluoro organic compound. Thus the present invention has been completed. Accordingly, the present invention provides, as the first embodiment of the invention, a cosmetic which comprises the following Components (A) and (B): (A) a fluorine compound-treated powder; and (B) a liquid perfluoro organic compound; wherein said fluorine compound-treated powder amounts from 5 to 95 % by weight and said liquid perfluoro organic compound amounts from 5 to 95 % by weight. The present invention further provides, as the second embodiment of the invention, a cosmetic which comprises the following Components (A), (B) and (C): (A) a fluorine compound-treated powder; (B) a liquid perfluoro organic compound; and (C) a silicone oil. DETAILED DESCRIPTION OF THE INVENTION A cosmetic, which is the first embodiment of the present invention, comprising the following Components (A) and (B) will be described below in detail: (A) a fluorine compound-treated powder; and (B) a liquid perfluoro organic compound, wherein said fluorine compound-treated powder amounts from 5 to 95 % by weight and said liquid perfluoro organic compound amounts from 5 to 95 % by weight. The fluorine compound-treated powder to be used as Component (A) in the first and second embodiments of the present invention is a powder treated with a fluorine compound. The fluorine compound-treated powder may be obtained by treating a powder with a fluorine compound, for example, a polyfluoroalkylphosphate as disclosed, for example, in U.S. Patent 3,632,744, which is represented by the following general formula (I): [C s F 2s+1 C t H 2t O] ℓ PO(OM) 3-ℓ wherein s represents an integer of from 4 to 14; t represents an integer of from 1 to 16; ℓ represents a number of from 1 to 2.5 on the average; and M, which may be the same or different from each other when ℓ represents a number less than 2, each independently represents a hydrogen atom, an alkali metal, an ammonium group or a substituted ammonium group such as protonated mono-, di- or tri-ethanol amine; provided that the total of s and t is at least 8; a resin having a fluoroalkyl group as disclosed, for example, in JP-A-55-167209; a ethylene tetrafluoride resin; a perfluoroalcohol; a perfluoroepoxy compound; a sulfoamide fluorophosphoric acid or a salt thereof; a perfluorosulfuric acid or a salt thereof; a perfluorocarboxylic acid or a salt thereof; and a perfluoroalkylsilane as disclosed, for example, in JP-A-2-218603 (e.g., silane coupling agents available from Shin-Etsu Silicone Co., Ltd. under the tradenames of LP-1T, LP-4T and LP-8T). Examples of the salt as mentioned above include an alkali metal salt, an alkaline earth metal salt, an ammonium salt, an alkanolamine salt, and the like. Among these fluorine compounds, the polyfluoroalkylphosphate of the general formula (I) is preferred for the fluorine compound-treated powder to be used as Component (A) in the first and second embodiments of the invention. The material of the powder to be treated with the fluorine compound is not particularly restricted so long as it is substantially insoluble in water and oils (for example, pigments, UV absorbers). The form of the powder to be treated is not particularly restricted. For example, those of plate form, amorphous form, scale form, spherical form or the like, or those having or not having pores can be used in the present invention. However, the powder of plate form or spherical form is preferred. Also, the primary particle size of the powder to be treated is not particularly restricted so long as the powder is in the form of a powder. However, in the first and second embodiments of the invention, a powder having a primary particle size of from 0.01 to 80 µm is preferred and of from 0.1 to 20 µm is more preferred in view of the feel at the use. Examples of the powder include inorganic pigments such as titanium oxide, iron oxide, ultramarine blue, zinc white, magnesium oxide, zirconium oxide, mica, sericite, talc, silica, kaolin, chromium hydroxide and carbon black; organic powders such as nylon powder, polymethyl methacrylate, styrene/divinylbenzene copolymer and polyethylene powder; and UV absorbers such as ultra-fine titanium dioxide powders, ultra-fine zinc oxide powders and fine zinc oxide flakes. The method for treating the powder with the fluorine compound is not particularly restricted. For example, the fluorine compound is dissolved in an organic solvent (for example, benzene, toluene, acetone) with heating and then the powder is added thereto followed by stirring. After distilling off the solvent, the powder is coated with the fluorine compound. After the completion of the coating, the powder may be baked at a temperature higher than the melting point of the fluorine compound so as to achieve well drape. Prior to the coating with the use of an organic solvent, the powder may be dried by baking at 110°C under reduced pressure for about 30 minutes to 80 hours. Thus the water repellency after the coating can be further improved. In these coating procedures, a mixture of two or more powders may be used. Furthermore, the powder may be simultaneously treated with known coating agent(s) other than the fluorine compound (for example, silicon, higher fatty acids, higher alcohols, esters, waxes), so long as the effects of the present invention are not deteriorated thereby. The amount of the fluorine compound may vary depending on the kind of the compound. It is preferable to use the fluorine compound in an amount of from 0.1 to 50 % by weight, more preferably from 2 to 20 % by weight, based on the powder(s). When the amount of the fluorine compound is excessively small, a sufficient water repellency may not be obtained. When the amount of the fluorine compound is excessively large, on the other hand, the inherent good spreadability of the extender tends to be deteriorated. These fluorine compound-treated powders can be used either alone or a mixture of two or more of them in the present invention. The fluorine compound-treated powders may be used in the first embodiment of the present invention in an amount of from 5 to 95 % by weight, preferably from 5 to 70 % by weight, based on the total weight of the composition. The liquid perfluoro organic compound to be used as Component (B) in the present invention is a perfluoro organic compound which is in the form of a liquid at room temperature. Examples thereof include perfluorodecalin, perfluoroadamantane, perfluorobutyltetrahydrofuran, perfluorooctane, perfluorononane, perfluoropentane, perfluorodecane, perfluorododecane and a perfluoro polyether represented by the following general formula (II): wherein R 1 , R 3 , R 4 and R 5 may be either the same or different and each represents a fluorine atom, a perfluoroalkyl group containing 1 to 5 carbon atoms or a perfluoroalkyloxy group containing 1 to 5 carbon atoms; R 2 represents a fluorine atom or a perfluoroalkyl group containing 1 to 5 carbon atoms; and p, q and r represent each a number of 0 or above value; provided that the molecular weight of the compound of the general formula (II) is from 500 to 100,000 and that all of p, q and r do not represent 0 at the same time. It is not always necessary that these perfluoro groups given in parentheses in the general formula (II) align in that order. Further, either random polymerization or block polymerization may be employed. Among these perfluoro polyethers, liquid ones having a viscosity of from 5.10 -6 to 5.10 -3 m 2 /s (5 to 5,000 cs) are preferable. More useful examples thereof include the compounds represented by the following general formula (III): wherein x and y represent each such a number as to give a molecular weight of from 500 to 10,000, provided that x/y is from 0.2 to 2, which are available from Montefluos Co., Ltd. under the tradenames of FOMBLIN® HC-04 (average molecular weight: 1,500), FOMBLIN® HC-25 (average molecular weight: 3,200) and FOMBLIN® HC-R (average molecular weight: 6,600); and the compounds represented by the following general formula (IV): F(CF 2 CF 2 CF 2 O) z CF 2 CF 3 wherein z represents a number of from 4 to 500, which are available from Daikin Industries, Ltd. under the tradenames of Demnum S-20 (molecular weight (Mw): 25,000), Demnum S-65 (molecular weight (Mw): 4,500), Demnum S-100 (molecular weight (Mw): 5,600) and Demnum S-200 (molecular weight (Mw): 8,400). These liquid perfluoro organic compounds can be used either alone or a combination of two or more of them. The liquid perfluoro organic compound(s) may be used in the first embodiment of the present invention in an amount of from 5 to 95 % by weight, preferably from 5 to 60 % by weight, based on the total weight of the composition. In addition to the aforesaid essential Components (A) and (B), the cosmetic of the first embodiment of the present invention may further contain other components commonly employed in cosmetics, so long as the effects of the present invention are not deteriorated thereby. Examples of such components include solid/semisolid oils such as vaseline, lanolin, ceresin, microcrystalline wax, carnauba wax, candelilla wax, higher fatty acids and higher alcohols; liquid oils such as olive oil, jojoba oil, castor oil, squalane, liquid paraffin, ester oil, diglycerides, triglycerides and silicone oil; water-soluble and oil-soluble polymers; colorants such as inorganic and organic pigments, metal soap-treated or silicone-treated inorganic and organic pigments and organic dyes; surfactants such as anionic surfactants, cationic surfactants, nonionic surfactants and dimethylpolysiloxane/polyoxyalkylene copolymer; water; preservatives; pigments; thickeners; pH controllers; perfumes; UV absorbers; humectants; blood flow enhancing agents; agents causing cold sensation; antiperspirants; bactericides; and skin activators. The cosmetic of this embodiment may be formulated into makeup cosmetics (for example, liquid foundation, powder foundation, rouge, eye shadow), medical cosmetics (for example, sunscreen) and medicines for external use (for example, antiinflamatry agent, skin protector) in a conventional manner. The cosmetic of this embodiment, in which a fluorine compound-treated powder is uniformly dispersed, is excellent in water repellency and water resistance, has a good oil resistance, can prevent cosmetic components such as pigments from the removal due to sweat or sebum and shows an improved long-lasting makeup effect. Now, a cosmetic, which is the second embodiment of the present invention, comprising the following Components (A), (B) and (C) will be described in detail: (A) a fluorine compound-treated powder; (B) a liquid perfluoro organic compound; and (C) a silicone oil. As the silicone oil to be used as Component (C) in this embodiment, any silicone oil commonly used in cosmetics may be used. It is particularly preferable to use a volatile low molecular silicone oil or a cyclic silicone oil, from the viewpoint of the feel at the application. Examples of such silicone oils include low molecular silicone oils such as a methylpolysiloxane, a dimethylpolysiloxane and a methylphenylpolysiloxane, whose viscosity are from 0.65 to 10 cs, and cyclic silicone oils such as a decamethylcycopentasiloxane and an octamethylcyclotetrasiloxane. Either one of these silicone oils or a combination of two or more of them may be used in the present invention. The content of these silicone oils in the second embodiment of the present invention may preferably range from 1 to 70 % by weight, more preferably 5 to 50 % by weight, based on the total weight of the composition. When the content thereof is smaller than 1 % by weight, the feel at the application tends to be deteriorated. When it exceeds 70 % by weight, on the other hand, the long-lasting makeup effect tends to be deteriorated. As the fluorine compound-treated powder to be used as Component (A) in this embodiment, those described above as the fluorine compound-treated powders may be used. As the powder to be treated with a fluorine compound in Component (A), it is preferable to use those having a primary particle size of from 0.01 to 80 µm, more preferably from 0.1 to 20 µm. Either one of these fluorine compound-treated powders or a combination of two or more of them may be used. These fluorine compound-treated powders may be preferably used in the second embodiment of the present invention in an amount of from 0.01 to 95 % by weight, more preferably from 0.1 to 85 % by weight, based on the total weight of the composition. When the content thereof is smaller than 0.01 % by weight, the effects of this embodiment tends to be deteriorated. When it exceeds 95 % by weight, on the other hand, the feel at the application tends to be deteriorated. As the liquid perfluoro organic compound to be used as Component (B) in this embodiment, those described above as the liquid perfluoro organic compounds may be used. Either one of these liquid perfluoro organic compounds or a combination of two or more of them may be used in this embodiment. These liquid perfluoro organic compounds may be used in the second embodiment of the present invention in an amount of from 1 to 70 % by weight, more preferably from 5 to 50 % by weight, based on the total weight of the composition. When the content thereof is smaller than 1 % by weight, the dispersibility of the fluorine compound-treated powder in the cosmetic of this embodiment tends to be deteriorated. When it exceeds 70 % by weight, on the other hand, the feel at the application of the cosmetic of this embodiment tends to be deteriorated. In addition to the aforesaid essential Components (A), (B) and (C), the cosmetic of this embodiment may further contain, if required, various components commonly used in cosmetics as cited above, so long as the effects of the present invention are not deteriorated thereby. The cosmetic of this embodiment may be formulated into any form (for example, powder, emulsion), without restriction. From the viewpoint of the feel at the application and effects, however, it may be preferably formulated into an emulsified cosmetic. In this case, it is recommended to add from 10 to 80 % by weight, preferably from 20 to 50 % by weight, of water and from 0.1 to 10 % by weight, preferably from 0.5 to 5 % by weight, of surfactant(s), each based on the total weight of the composition, in addition to the aforesaid essential components. The cosmetic of the present invention may be produced in a conventional manner. It is applicable as makeup cosmetics (for example, liquid foundation, powder foundation, rouge, eye shadow) and medical cosmetics (for example, sunscreen). The cosmetic of this embodiment of the present invention can prevent cosmetic components such as pigments and UV absorbers from the removal due to sweat and sebum, shows a good spreadability on the skin and gives a good texture such as an appropriate moist and refreshing feel. To further illustrate the present invention, the following Examples will be given. PRODUCTION EXAMPLE 1 150 g of a powder was introduced into a round bottom flask (or a kneader) and heated to 60°C while mixing. Next, 13 g of (C 6 F 13 CH 2 CH 2 O) 2 P(O)OH, which had been dissolved in 1500 g of isopropyl ether and heated to 50°C, was added thereto followed by mixing at 60°C for 4 hours. After distilling off the isopropyl ether at 50 to 60°C under reduced pressure, the residue was dried. Thus 157 g of a fluorine compound-treated powder was obtained. PRODUCTION EXAMPLE 2 17 g of (C 8 F 17 CH 2 CH 2 O) 2 P(O)OH and 1500 g of isopropyl alcohol were added to a round bottom flask (or a kneader) and dissolved by heating to 60°C. Then 150 g of a powder was added thereto followed by mixing at 60°C for 4 hours. After distilling off the isopropyl ether at 50 to 60°C under reduced pressure, the residue was dried. Thus 161 g of a fluorine compound-treated powder was obtained. EXAMPLE 1 (Two-layered liquid foundation) A two-layered liquid foundation of the composition as given in Table 1 was prepared and the long-lasting makeup effect, aggregation and stability of this product were evaluated. Table 2 shows the results. (Production method) The oily phase was molten at room temperature and the pigment was added thereto followed by dispersing with a disper. Then the aqueous phase was added to the oily phase under stirring and thus the mixture was emulsified to thereby give the aimed liquid foundation. Component Example 1 Comparative Example 1-1 Comparative Example 1-2 (1) Octamethylcyclotetrasiiloxane 15.0 15.0 15.0 (2) Dimethylpolysiloxane (KF-96A, tradename, a product of Shin-Etsu Silicone Co., Ltd.; 6cs) - - 15.0 (3) Perfluoro polyether (FOMBLIN HC-04, tradename, a product of Montefluos Co., Ltd.) 15.0 15.0 - (4) Dimethylpolysiloxane polyoxyalkylene copolymer (SH377fc, tradename, a product of Toray Silicone Co., Ltd.) 1.0 1.0 1.0 (5) Glycerol 2.0 2.0 2.0 (6) Ethanol 10.0 10.0 10.0 (7) Water balance balance balance (8) Fluorine compound-treated pigment (Production Example 2) Titanium oxide 6.0 - 6.0 Sericite 8.0 - 8.0 Iron oxide (red, black, yellow) 1.5 - 1.5 (9) Silicone-treated pigment (marketed product treated with polymethylhydrogensiloxane) Titanium oxide - 6.0 - Sericite - 8.0 - Iron oxide (red, black, yellow) - 1.5 - (10) Perfume appropriate amount appropriate amount appropriate amount Note: All values indicated in Table 1 above are % by weight based on the total weight of the composition. (Evaluation method) Long-lasting makeup effect: The long-lasting makeup effect of a sample was organoleptically evaluated by 10 skilled panelists in accordance with the following criteria: A : Evaluated as high by 8 or more panelists B : Evaluated as high by 4 to 7 panelists C : Evaluated as high by less than 4 panelists Aggregation: The aggregation in a liquid foundation was examined with the naked eye immediately after the production. A : Not aggregated B : Aggregated Stability: A liquid foundation was stored at 40°C for a month and then evaluated in accordance with the following criteria. A : Uniformly dispersed by shaking lightly B : Never uniformly dispersed even by shaking vigorously Long-lasting make-up effect Aggregation (immediately after production) Stability (40°C, 1 month) Example 1 A A A Comparative Example 1-1 B A B Comparative Example 1-2 C B B As Table 2 clearly shows, the liquid foundation of the present invention was superior in long-lasting makeup effect and stability to those containing either fluorine-treated pigment or the fluorine oil alone. EXAMPLE 2 (Powder foundation) (Composition) Component Content (% by weight) (1) Fluorine compound-treated powder (Production Example 2) Titanium oxide 10.0 Sericite 30.0 Mica balance Kaolin 5.0 Red iron oxide 2.5 Yellow iron oxide 2.0 Black iron oxide 0.1 (2) Polyethylene powder 8.0 (3) Squalane 2.0 (4) Perfluoro polyether (FOMBLIN HC-04, tradename, a product of Montefluos Co., Ltd.) 10.0 (5) Preservative 0.1 (6) Perfume appropriate amount (Production method) The pigment components were mixed together and ground in a mill. Then the ground mixture was transferred into a high-speed blender. The binder and other components were mixed uniformly and then added to the pigment. The obtained mixture was treated with a mill and dressed by sieving. After allowing to stand for several days, the mixture was compression molded in a container such as a metal dish to thereby give a powder foundation. EXAMPLE 3 (Rouge) The procedure of Example 2 was repeated to thereby give a rouge. (Composition) Component Content (% by weight) (1) Fluorine compound-treated powder (Production Example 1) Kaolin balance Mica 13.0 Titanium oxide 12.0 Iron oxides (red, black, yellow) 5.0 (2) Organic pigment (Red No. 202) 2.4 (3) Squalane 7.5 (4) Perfluoro polyether (FOMBLIN HC-04, tradename, a product of Montefluos Co., Ltd.) 15.0 (5) Preservative 0.1 (6) Perfume appropriate amount EXAMPLE 4 (Powder eye shadow) (Composition) Component Content (% by weight) (1) Fluorine compound-treated powder (Production Example 1) Mica titanium 35.0 Sericite 24.0 Mica 10.0 Coloring pigment 15.0 (2) Zinc stearate 5.0 (3) Zinc laurate 3.0 (4) Perfluoro polyether (FOMBLIN HC-04, tradename, a product of Montefluos Co., Ltd.) 8.0 (Production method) The powder components other than mica titanium were mixed together and ground. Then the mica titanium was added thereto. Next, the procedure of Example 2 was repeated to thereby give the target powder eye shadow. EXAMPLE 5 (Sunscreen emulsion (W/O type)) The procedure of Example 1 was repeated to thereby give a sunscreen emulsion. (Composition) Component Content (% by weight) (1) Octamethylcyclotetrasiloxane 25.0 (2) Perfluoro polyether (FOMBLIN HC-04, tradename, a product of Montefluos Co., Ltd.) 10.0 (3) Dimethylpolysiloxane/polyoxyalkylene copolymer (SH3775C, product of Toray Silicone Co., Ltd.) 1.0 (4) Glycerol 2.0 (5) Ethanol 5.0 (6) Water balance (7) Fluorine compound-treated zinc oxide (Production Example 1) 7.5 (8) Octyl methoxycinnamate 2.0 (9) Perfume appropriate amount Each of the cosmetics of Examples 2 to 5 was excellent in the long-lasting makeup effect and the stability. EXAMPLE 6 AND COMPARATIVE EXAMPLES 2-1 TO 2-4 (Two-layered liquid foundation) A two-layered liquid foundation of each composition as given in Table 3 was prepared in the following production method and the long-lasting makeup effect, aggregation, feel at the application and stability of each product were evaluated in the following evaluation method. Table 4 shows the results. (Production method) The oily phase was molten at room temperature and the pigment was added thereto followed by dispersing with a disper. Then the aqueous phase was added under stirring and thus the mixture was emulsified to thereby give the aimed liquid foundation. (Evaluation method) Long-lasting makeup effect: The long-lasting makeup effect of a sample was organoleptically evaluated by 10 skilled panelists in accordance with the following criteria: A : Evaluated as high by 8 or more panelists B : Evaluated as high by 4 to 7 panelists C : Evaluated as high by less than 4 panelists Aggregation: The aggregation in a liquid foundation was examined with the naked eye immediately after the production. A : Not aggregated B : Aggregated Feel at the application: The feel at the application of a liquid foundation was organoleptically evaluated by 10 skilled panelists based on the same criteria as those used in the evaluation of the long-lasting makeup effect. Stability: A liquid foundation was stored at 40°C for a month and then evaluated in accordance with the following criteria. A : Uniformly dispersed by shaking lightly B : Never uniformly dispersed even by shaking vigorously Long-lasting makeup effect Aggregation (immediately after production) Feel at the application Stability (40°C, 1 month) Example 6 A A A A Comparative Example 2-1 A B C B Comparative Example 2-2 B B C B Comparative Example 2-3 C A B A Comparative Example 2-4 C A C B As Table 4 clearly shows, the liquid foundation of the present invention (Example 6) was superior in long-lasting makeup effect, feel at the application and stability to those containing either fluorine-treated pigment or the fluorine oil alone (Comparative Examples 2-1 to 2-4). EXAMPLE 7 (Creamy foundation) The procedure of Example 6 was repeated to thereby give a creamy foundation of the following composition. (Composition) Component Content (% by weight) (1) Fluorine compound-treated powder (the following pigments were treated in accordance with Production Example 2) Titanium oxide 6.0 Sericite 8.0 Iron oxide (red, yellow, black) 1.2 (2) Decamethylcyclopentasiloxane 15.0 (3) Dimethylpolysiloxane (KF-96A, tradename, a product of Shin-Etsu Chemical Co., Ltd.; 6 cs) 10.0 (4) Dimethylpolysiloxane polyoxyalkylene copolymer 1.0 (5) Perfluoro polyether (FOMBLIN HC-04, tradename, a product of Montefluos Co., Ltd.) 20.0 (6) Glycerol 2.0 (7) Water balance (8) Perfume appropriate amount EXAMPLE 8 (Powder foundation) The powders given in the following composition were mixed together and ground with a mill. The ground mixture was then transferred into a high-speed blender and other components including the binder were uniformly mixed therewith. After uniformly mixing, the mixture was treated with a mill and dressed by sieving. Then it was allowed to stand for several days and compression-molded in a container such as a metal dish. Thus a powder foundation was obtained. (Composition) Component Content (% by weight) (1) Fluorine compound-treated powder (the following pigments were treated in accordance with Production Example 2) Titanium oxide 10.0 Sericite 30.0 Talc 30.0 Kaolin 5.0 Red iron oxide 2.0 Yellow iron oxide 2.5 Black iron oxide 0.1 Polyethylene powder 4.0 (2) Squalane 2.0 (3) Dimethylpolysiloxane (KF-96A, tradename, a product of Shin-Etsu Chemical Co., Ltd.; 6 cs) 7.0 (4) Perfluoro polyether (FOMBLIN HC-25, tradename, a product of Montefluos Co., Ltd.) 7.0 (5) Preservative appropriate amount (6) Perfume trace EXAMPLE 9 (Rouge) The procedure of Example 8 was repeated to thereby give a rouge of the following composition. (Composition) Component Content (% by weight) (1) Fluorine compound-treated powder (the following pigments were treated in accordance with Production Example 2) Kaolin 50.0 Mica 13.0 Titanium oxide 12.0 Iron oxide (red, yellow, black) 5.0 (2) Organic pigment (Red No. 202) 2.4 (3) Dimethylpolysiloxane (KF-96A, tradename, a product of Shin-Etsu Chemical Co., Ltd.; 6 cs) 7.4 (4) Perfluoro polyether (FOMBLIN HC-04, tradename, a product of Montefluos Co., Ltd.) 10.0 (5) Preservative appropriate amount (6) Perfume trace EXAMPLE 10 (Powder eye shadow) The procedure of Example 8 was repeated except that the pigments other than the mica titanium were preliminarily mixed and ground followed by adding the mica titanium. Thus a powder eye shadow of the following composition was obtained. (Composition) Component Content (% by weight) (1) Fluorine compound-treated powder (the following pigments were treated in accordance with Production Example 2) Mica titanium 5.0 Sericite 36.0 Mica 24.0 Iron oxide (red, yellow, black) 2.0 Ultramarine blue 10.0 Prussian blue 6.0 (2) Dimethylpolysiloxane (KF-96, tradename, a product of Shin-Etsu Chemical Co., Ltd.; 6 cs) 6.0 (3) Perfluoro polyether (FOMBLIN HC-04, tradename, a product of Montefluos Co., Ltd.) 6.0 (4) Squalane 3.0 (5) Sorbitan trioleate 1.0 (6) Preservative appropriate amount (7) Perfume trace EXAMPLE 11 (Sunscreen emulsion) The procedure of Example 6 was repeated to thereby give a sunscreen emulsion of the following composition. (Composition) Component Content (% by weight) (1) Octamethylcyclotetrasiloxane 25.0 (2) Perfluoro polyether (FOMBLIN HC-04, tradename, a product of Montefluos Co., Ltd.) 10.0 (3) Dimethylpolysiloxane polyoxyalkylene copolymer 1.0 (4) Glycerol 2.0 (5) Ethanol 5.0 (6) Water balance (7) Fluorine compound-treated zinc oxide (zinc oxide was treated in accordance with Production Example 1) 7.5 (8) Octyl methoxycinnamate 2.0 (9) Perfume appropriate amount Each of the cosmetics of Examples 7 to 11 was excellent in the long-lasting makeup effect and feel at the application and the fluorine compound-treated powder was well dispersed therein. The cosmetic of the present invention is excellent in water repellency, water resistance, sebum resistance and oil resistance. It prevents cosmetic components such as pigments and UV absorbers from the removal due to sweat or sebum. Further, it shows a good spreadability on the skin and gives an excellent feel, for example, an appropriate moist and refreshing feel.

Claims: A cosmetic comprising the following components (A) and (B): (A) from 5 to 95% by weight of a powder treated with a fluorine compound being selected from the group consisting of a polyfluoroalkylphosphate represented by the following general formula (I): [C s F 2s+1 C t H 2t O] ℓ PO(OM) 3-ℓ wherein s represents an integer of from 4 to 14; t represents an integer of from 1 to 16; ℓ represents a number of from 1 to 2.5 on the average; and M, which may be the same or different from each other when ℓ represents a number less than 2, each independently represents a hydrogen atom, an alkali metal, an ammonium group or a substituted ammonium group; provided that the total of s and t is at least 8; a resin having a fluoroalkyl group; an ethylene tetrafluoride resin; a perfluoroalcohol; a perfluoroepoxy compound; a sulfoamide fluorophosphoric acid or a salt thereof; a perfluorosulfuric acid or a salt thereof; a perfluorocarboxylic acid or a salt thereof; and a perfluoroalkylsilane; ( B ): from 5 to 95% by weight of a liquid perfluoroorganic compound selected from perfluorodecalin, perfluoroadamantane, perfluorobutyltetrahydrofuran, perfluorooctane, perfluorononane, perfluoropentane, perfluorodecane, perfluorododecane and a perfluoropolyether represented by the following general formula (II): wherein R 1 , R 3 , R 4 and R 5 may be either the same or different and each represents a fluorine atom, a perfluoroalkyl group containing 1 to 5 carbon atoms or a perfluoroalkyloxy group containing 1 to 5 carbon atoms; R 2 represents a fluorine atom or a perfluoroalkyl group containing 1 to 5 carbon atoms; and p, q and r represent each a number of 0 or above value; provided that the molecular weight of the compound of the general formula (II) is from 500 to 100,000 and that all of p, q and r do not represent 0 at the same time. A cosmetic according to claim 1, wherein said liquid perfluoro organic compound is a perfluoro polyether represented by the following general formula (II): wherein R 1 , R 3 , R 4 and R 5 may be either the same or different and each represents a fluorine atom, a perfluoroalkyl group containing 1 to 5 carbon atoms or a perfluoroalkyloxy group containing 1 to 5 carbon atoms; R 2 represents a fluorine atom or a perfluoroalkyl group containing 1 to 5 carbon atoms; and p, q and r represent each a number of 0 or above value; provided that the molecular weight of the compound of the general formula (II) is from 500 to 100,000 and that all of p, q and r do not represent 0 at the same time. A cosmetic according to claim 1, wherein said fluorine compound-treated powder is a powder treated with a polyfluoroalkyl-phosphate represented by the following general formula (I): [C s F 2s+1 C t H 2t O] ℓ PO(OM) 3-ℓ wherein s represents an integer of from 4 to 14; t represents an integer of from 1 to 16; ℓ represents a number of from 1 to 2.5 on the average; and M, which may be the same or different from each other when ℓ represents a number less than 2, each independently represents a hydrogen atom, an alkali metal, an ammonium group or a substituted ammonium group; provided that the total of s and t is at least 8. A cosmetic according to any of the claims 1 to 3 comprising the following component (C): (C) a silicone oil. A cosmetic comprising the following components (A), (B) and (C): (A) from 0.01 to 95% by weight of a powder treated with a fluorine compound being selected from the group consisting of a Polyfluoroalkylphosphate represented by the following general formula (I): [C s F 2s+1 C t H 2t O] ℓ PO(OM) 3-ℓ wherein s represents an integer of from 4 to 14; t represents an integer of from 1 to 16; ℓ represents a number of from 1 to 2.5 on the average; and M, which may be the same or different from each other when ℓ represents a number less than 2, each independently represents a hydrogen atom, an alkali metal, an ammonium group or a substituted ammonium group; provided that the total of s and t is at least 8; a resin having a fluoroalkyl group; an ethylene tetrafluoride resin; a perfluoroalcohol; a perfluoroepoxy compound; a sulfoamide fluorophosphoric acid or a salt thereof; a perfluorosulfuric acid or a salt thereof; a perfluorocarboxylic acid or a salt thereof; and a perfluoroalkylsilane; (B) from 1 to 70% by weight of a liquid perfluoroorganic compound selected from perfluorodecalin, perfluoroadamantane, perfluorobutyltetrahydrofuran, perfluorooctane, perfluorononane, perfluoropentane, perfluorodecane, perfluorododecane and a perfluoropolyether represented by the following general formula (II): wherein R 1 , R 3 , R 4 and R 5 may be either the same or different and each represents a fluorine atom, a perfluoroalkyl group containing 1 to 5 carbon atoms or a perfluoroalkyloxy group containing 1 to 5 carbon atoms; R 2 represents a fluorine atom or a perfluoroalkyl group containing 1 to 5 carbon atoms; and p, q and r represent each a number of 0 or above value; provided that the molecular weight of the compound of the general formula (II) is from 500 to 100,000 and that all of p, q and r do not represent 0 at the same time, and (C) from 1 to 70% by weight of a silicon oil.

Inventors: KOMORI TAKASHI, NAGATANI NOBORU, TORIZUKA MAKOTO, KOMORI, TAKASHI, NAGATANI, NOBORU, TORIZUKA, MAKOTO
Applicants: KAO CORP, KAO CORPORATION
Application year: 1991
Main classification: A61K7
IPC codes: A61K8, A61Q1