Flame retardant compositions

Abstract: A composition useful in the manufacture of cable comprising: (i) a copolymer comprised of ethylene and vinyl acetate; (ii) a surface treated magnesium hydroxide having (a) a strain in the <101> direction of not more than 3.0 X 10⁻³; (b) a crystallite size in the <101> direction of more than 800 angstroms; and (c) a surface area, determined by the BET method, of less than 20 square meters per gram; and (iii) a silicone fluid.

Description: This invention relates to flame retardant compositions containing an ethylene copolymer and a magnesium hydroxide filler. The compositions are particularly useful in plenum cable. Plenum cable is used to carry power through ducts which are used to ventilate, for example, high-rise buildings. While a fire occurring in these ducts can be dangerous in its own right, such a conflagration is especially insidious because the smoke and other gases resulting from the fire are transported through the ducts throughout the building, even to parts quite remote from the blaze. In some cases, colorless and odorless gases can invade sleeping quarters housing unsuspecting people. The cable used in plenums is generally constructed of metal conductors insulated with a polymeric material. These elements are generally twisted to form a core and are pr-otected by another polymeric sheath or jacket material. In certain cases, added protection is afforded by inserting a wrap between the core and the sheath. To mitigate the dangers of a duct fire, it is important that the cable jacketing is not only flame retardant, but, on burning, produces a minimum amount of smoke, emits low levels of corrosive gases and is self-extinguishing. Further, the cable should not raise installation problems caused by materials, which are toxic to the touch. Ethylene polymers are considered to be deficient insofar as flame retardance or flame resistance is concerned. One method for increasing flame resistance in these polymers is to formulate using metal hydroxides as the flame retardant additive. Both aluminum hydroxide and magnesium hydroxide have been used in this way. Generally, these hydroxides are viewed as equivalents as flame retardants in this context. Aluminum hydroxide is preferred on a cost/performance basis, however. Thus, more than ninety-five percent of all hydrate based commercial formulations use aluminum hydroxide. In spite of the cost advantage of aluminum hydroxide, there is a strong thrust towards improving the flame resistance of plenum cable as well as its smoke, corrosion, self-extinguishing, and toxic characteristics because of the vulnerability of the occupants of buildings containing plenums through which air is transported for heating and cooling. EP-A-369473 discloses a composition useful in the manufacture of plenum cable comprising: (i) a copolymer comprised of ethylene and vinyl acetate wherein the portion of the copolymer attributed to the vinyl acetate is in the range of about 25 to about 60 parts by weight based on 100 parts by weight of the copolymer; and (ii) magnesium hydroxide having (a) a strain in the <101> direction of not more than 3.0 X 10 -3 ; (b) a crystallite size in the <101> direction of more than 800 angstroms; and (c) a surface area, determined by the BET method, of less than 20 square meters per gram, the amount of magnesium hydroxide being in the range of about 180 to about 350 parts by weight based on 100 parts by weight of the copolymer. Said composition may also contain additives such as, e.g., polydimethylsiloxane. An object of this invention is to provide a composition based on a polymer of ethylene, which can be used as jacketing for plenum cable and will furnish the plenum cable with superior flame retardance or resistance, low smoke and corrosive gases emissions, a self-extinguishing characteristic, and essentially no handling toxicity. Other objects and advantages will become apparent hereinafter. According to the invention, a composition has been discovered, which meets the above objective. According to the present invention there is provided a composition for the manufacture of cable comprising: (i) a copolymer comprised of ethylene and vinyl acetate; (ii) magnesium hydroxide having (a) a strain in the <101> direction of not more than 3.0 X 10 -3 ; (b) a crystallite size in the <101> direction of more than 80 nm (800 Angstroms); and (c) a surface area, determined by the BET method, of less than 20 square meters per gram, said magnesium hydroxide having been surface treated with one or more carboxylic acids having 8 to 24 carbon atoms or the metal salts thereof; and (iii)a vinyl-substituted silicone fluid having a viscosity in the range of 10000 to 1,000,000 mm 2 /s (centistokes) in an amount of 0.1 to 5 parts by weight per 100 parts by weight of polymer. Copolymers comprised of ethylene and vinyl acetate are well known and can be prepared by conventional techniques. The portion of the copolymer attributed to the vinyl acetate monomer is generally in the range of 12 to 60 parts by weight based on 100 parts by weight of the copolymer and is preferably in the range of 25 to 52 parts by weight. The magnesium hydroxide defined above and a method for its preparation are disclosed in US-A-4,098,762. A preferred characteristic of the magnesium hydroxide is that the surface area as determined by the BET method, is less than 20, preferably less than 10 square meters per gram. The amount of magnesium hydroxide used in the composition generally is in the range of 50 to 350 parts by weight of magnesium hydroxide per one hundred parts by weight of ethylene/vinyl acetate copolymer and is preferably in the range of 75 to 250 parts by weight of magnesium hydroxide per one hundred parts by weight of ethylene/vinyl acetate copolymer. The magnesium hydroxide is surface treated with a saturated or unsaturated carboxylic acid having 8 to 24 carbon atoms and preferably 12 to 18 carbon atoms or a metal salt thereof. Mixtures of these acid and/or salts can be used, if desired. Examples of suitable carboxylic acids are oleic, stearic, palmitic, isostearic, and lauric acids, examples of metals which can be used to form the salts of these acids are zinc, aluminum, calcium, magnesium, and barium; and examples of the salts themselves are magnesium stearate, zinc oleate, calcium palmitate, magnesium oleate, and aluminum stearate. The amount of acid or salt is generally in the range of 0.1 to 5 parts by weight of acid and/or salt per one hundred parts by weight of magnesium hydroxide and preferably 0.25 to 3 parts by weight per one hundred parts by weight of magnesium hydroxide. The acid or salt can be merely added to the composition in like amounts rather than using the surface treatment procedure, but this is not preferred. Component (iii) is a certain silicone fluid. Silicone fluids are organosiloxane polymers commercially available in a range of viscosities from 0.65 to about 1,000,000 mm 2 /s (centistokes). Viscosities in the range of 10000 to 1,000,000 centistokes are useful in the subject composition. The vinyl substituted silicone fluids are those having one or more vinyl groups. These silicone fluids usually contain 1 to 10 percent by weight vinyl groups and preferably contain 2.5 to 7 percent by weight vinyl groups. One embodiment of a silicone fluid can be represented by the following formula: wherein R is CH 2 =CH- and x plus y can be equal to 1 to 5000. The silicone fluids are preferably characterized by their viscosity, however. The amount of silicone fluid (iii) which can be used in subject composition is in the range of 0.1 to 5 parts by weight of silicone fluid per one hundred parts by weight of polymer and is preferably in the range of 1 to 5 parts by weight per one hundred parts by weight of polymer. Other useful additives for the plenum cable composition are coupling agents, surfactants, free radical generators, reinforcing filler or polymer additives, antioxidants, ultraviolet stabilizers, antistatic agents, pigments, dyes, slip agents, plasticizers, lubricants, viscosity control agents, extender oils, metal deactivators, water tree growth retardants, voltage stabilizers, flame retardant additives, and smoke suppressants. Some of the more important additives are discussed below. A coupling agent is a chemical compound, which chemically binds polymer components to inorganic components. This is effected by a chemical reaction taking place at the temperatures under which the formulation is compounded, about 70°C to about 180°C. The coupling agent generally contains an organofunctional ligand at one end of its structure which interacts with the backbone of the polymeric component and a ligand at the other end of the structure of the coupling compound which attaches through reaction with the surface of the filler. The following silane coupling agents are useful in subject composition: gamma-methacryloxypropyltrimethoxy silane; methyltriethoxy silane; methyltris (2-methoxyethoxy) silane; dimethyldiethoxy silane; vinyltris(2-methoxyethoxy) silane; vinyltrimethoxy silane; and vinyltriethoxy silane; and mixtures of the foregoing. A preferred silane coupling agent is a mixture of gamma-methacryloxypropyltrimethoxy silane and vinyltriethoxysilane. This mixture is described in US-A-4,481,322. Useful reinforcing additives include polymerizable unsaturated organic compounds having at least two polymerizable unsaturated groups. It is believed that the reinforcing additive reacts chemically with the thermoplastic polymer matrix during the hot melt compounding of the filled thermoplastic polymer. It is further believed that the reinforcing additive causes the formation of a strong and tough interphase between the individual filler particles and the surrounding matrix polymer, enabling the polymer to withstand the local stress concentrations caused by the filler particles, which might otherwise result in matrix crack initiation and catastrophic failure. It is believed that such increases in the toughness of the interphase enable the simultaneous achievement of high stress and ductility in the final composite. Filler treatments which rely solely on increased adhesion, i.e., coupling, between the filler surface and the matrix polymer, can increase the composite strength, but, if there is no improvement in interphase toughness, the composite will remain brittle. This concept is discussed in US-A-4,385,136. The reinforcing additives include any organic compounds of the above description which do not contain any group or element adversely affecting the function of the polymer; filler; silane; or any other component of the composition. Suitable unsaturated organic compounds include ester diol 2,4-diacrylate, 1,4 butylene glycol diacrylate, diethylene glycol dimethacrylate, triallyl-s-triazine-2,4,6-(1H, 3H, 5H)-trione, triallyl mellitate, pentaerythritol triacrylate, polycaprolactone triacrylate, m-phenylene bis maleimide, dipentaerythritol pentaacrylate, melamine triacrylate, epoxidized linseed oil/acrylate, triacryloyl hexahydro-s-triazine, trimethylolpropane trimaleate, trimethacryloyl hexahydro-s-triazine, N,N-tetraacryloyl 1,6-diaminopyridine, 1,3-butylene glycol dimethacrylate, 1,3-butylene glycol diacrylate, ethylene glycol dimethacrylate, ethylene glycol diacrylate, diethylene glycol diacrylate, triethylene glycol diacrylate, polyethylene glycol dimethacrylate, polyethylene glycol diacrylate, trimethylol propane trimethacrylate, trimethylol propane triacrylate, divinyl sulfone, dicyclopentadiene, bisalkyl glycol dicarbonate, triallyl cyanurate, acetyl triallyl citrate, divinyl benzene, dialkyl phthalate, tetraallyl methylenediamine, tetraallyl oxyethane, 3-methyl-1,4,6-heptatriene; 1,10-decamethylene glycol dimethacrylate and di-, tri-, tetra-, and penta-acrylates of poly(vinyl alcohol). In addition, the following low molecular weight polyunsaturated polymers may be used: polybutadiene oligomers, hydroxyl terminated polybutadiene oligomers, hydroxyl terminated styrene-butadiene and acrylonitrile-butadiene oligomers, unsaturated polyesters, and partial alkyl esters of styrenemaleic anhydride oligomers. It is preferred to employ polymerizable unsaturated organic compounds that have a high unsaturated level to molecular weight ratio. Therefore, the tri-, tetra-, and penta-acrylates of poly(vinyl alcohol) and the other tri-, tetra-, and penta-acrylates and methacrylates of polyols such as pentaerythritol, trimethylolpropane, and dipentaerythritol, as described above, are preferred. The coupling agent and reinforcing additive are each used in amounts of about 0.05 part by weight to about 0.5 part by weight for each 100 parts by weight of copolymer. The effect can be maximized by the inclusion of suitable surfactants and free radical generators. Examples of antioxidants are: hindered phenols such as tetrakis[methylene(3,5-di-tert-butyl-4-hydroxyhydrocinnamate)]methane and thiodiethylene bis(3,5-di-tert-butyl-4-hydroxy)hydrocinnamate; phosphites and phosphonites such as tris(2,4-di-tert-butylphenyl)phosphite and di-tert-butylphenylphosphonite; various amines such as polymerized 2,2,4-trimethyl-1,2-dihydroquinoline; and silica. A tetrakis methane compound is preferred. Antioxidants are used in amounts of about 1 to about 5 parts by weight per hundred parts by weight of copolymer. The invention is illustrated by the following examples. Examples 1 to 16 The magnesium hydroxide used in the examples is prepared as follows: Five liters of an aqueous solution of magnesium chloride having a concentration of 1.5 moles per liter (the temperature of the solution is 15°C) is placed in a reaction vessel having a capacity of about 10 liters, and the solution is stirred. An ammonia solution with a concentration of 10 moles per liter (the temperature of the solution is 15°C) is added in an amount of 1.35 liters (corresponding to 0.9 equivalent per equivalent of magnesium chloride) over the course of about 10 minutes. A part of the resulting suspension is immediately filtered at reduced pressure, and then washed thoroughly with water and then with acetone. The product is dried for about 2 hours at room temperature, and analyzed by X-ray diffraction and by a chemical analysis method. By the X-ray diffraction, the product is identified as basic magnesium chloride having the structure defined for the magnesium hydroxide. The chemical analysis shows that this product has the composition Mg(OH) 1.903 Cl 0.097 mH 2 O. The presence of water of crystallization was confirmed by DTA and TGA. Immediately after the reaction, a greater portion of the remaining suspension is placed in a 20-liter autoclave, and hydrothermally treated at 180°C for 8 hours. This heat treatment is carried out within about 2 hours after the end of the reaction because this unstable substance has to be treated while it remains undecomposed. After the hydrothermal treatment, the product is filtered at reduced pressure, washed with water and dried. The product obtained is identified as magnesium hydroxide by X-ray diffraction. It has a strain in the <101> direction of 0.970 X 10 -3 , a crystallite size in the <101> direction of 420 nm (4200 angstroms), and a specific surface area by the BET method of 6.7 square meters per gram. DTA = differential thermal analysis TGA = thermal gravimetric analysis BET method = a nitrogen adsorption surface area measurement Sixteen compositions are processed into test specimens as required by the test procedure for the Limiting Oxygen Index (LOI), i.e., ASTM-D 2863-70, and the test procedure is carried out. See, also, US-A-4,446,279, Limiting Oxygen Index measures and quantifies flame resistance. The higher the LOI number the greater the flame resistance or flame retardance and the lower the emissions of smoke and other harmful gases. It is observed that no corrosive gases are present in the emissions; that the samples are self-extinguishing within a reasonable time; and that handling the samples provides no toxic effects on the skin. Components in parts by weight, Limiting Oxygen Index (LOI), tensile strength, and elongation are given in the Table. Examples 4, 10 and 13 to 15 are examples using the composition of the invention. Notes accompanying the Table: EVA = copolymer of ethylene and vinyl acetate. EVA I is based on 28 percent by weight vinyl acetate. EVA II is based on 18 percent by weight vinyl acetate. EEA = copolymer of ethylene and ethyl acrylate based on 35 percent by weight ethyl acrylate. Polyethylene = a copolymer of ethylene and 1-butene having a density of 0.905 g/cm 3 . Mg(OH) 2 = magnesium hydroxide prepared as above. It is surface treated with about 2 parts by weight of stearic acid. Parts by weight of surface treating acid is based on 100 parts by weight of the metal hydrate. Silicone fluid = vinyl modified polydimethylsiloxane having a specific gravity of 0.97 @ 25/25°C and a viscosity of 50,000 to 70,000 mm 2 /s (centistokes). Antioxidant = pentaerythritol tetrakis (3,5-di-tert-butyl-4-hydroxyphenyl propionate). Tensile strength [MPa(psi)] is determined under ASTM D-412. Elongation (%) is determined under ASTM D-412.

Claims: A composition for the manufacture of cable comprising: (i) a copolymer comprised of ethylene and vinyl acetate; (ii) magnesium hydroxide having (a) a strain in the <101> direction of not more than 3.0 X 10 -3 ; (b) a crystallite size in the <101> direction of more than 80 nm (800 Angstroms); and (c) a surface area, determined by the BET method, of less than 20 square meters per gram, said magnesium hydroxide having been surface treated with one or more carboxylic acids having 8 to 24 carbon atoms or the metal salts thereof; and (iii)a vinyl-substituted silicone fluid having a viscosity in the range of 10000 to 1,000,000 mm 2 /s (centistokes) in an amount of 0.1 to 5 parts by weight per 100 parts by weight of polymer. The composition defined in claim 1 wherein the portion of the copolymer attributed to the vinyl acetate is in the range of 12 to 60 parts by weight, based on 100 parts by weight of the copolymer. The composition as defined in claim 2 wherein the vinylacetate is present in the copolymer in an amount of 25 to 52 percent by weight of the copolymer. The composition defined in at least one of the claims 1-3, wherein the carboxylic acids and/or metal salts thereof are present in an amount of 0.1 to 5 parts by weight based on 100 parts by weight of magnesium hydroxide. The composition defined in at least one of the claims 1-4, wherein the magnesium hydroxide is present in an amount of 50 to 350 parts by weight based on 100 parts by weight of the copolymer. The composition as defined in at least one of claims 1 - 5, wherein the magnesium hydroxide has a surface area, as determined by the BET method, of less than 10 square meters per gram. An article of manufacture comprising a metal core conductor and at least one layer surrounding the core comprising the composition defined in at least one of the claims 1-6. The composition defined in at least one of the claims 1-6 additionally containing a coupling agent. The composition defined in at least one of the claims 1-6 additionally containing a reinforcing additive.

Inventors: KEOGH MICHAEL JOHN, KEOGH, MICHAEL JOHN
Applicants: UNION CARBIDE CHEM PLASTIC, UNION CARBIDE CHEMICALS AND PLASTICS COMPANY, INC.
Application year: 1991
Main classification: C08K9
IPC codes: H01B3, C08L31, C08K3, C08L23, C08K9, C08L87, C08L83, H01B7