Spiral filtration module with strengthened membrane leaves and method of constructing same

Abstract: The subject of the present invention is an improved leaf packet useful in forming a spiral filtration module, and an improved module which results from utilization of the leaf packet and a method of preparing the leaf packet. The membrane sheet (10) utilized in forming a spiral filtration module is fused and densified in the area of its fold to increase the sheet density in this area and thus provide protection against mechanical failure. The densification includes the application of heat and pressure to the membrane surface (12) of the sheet so as to densify the membrane surface and seal it against the penetration of feed stream liquid while also densifying the membrane, the backing and an optional reinforcing strip (18).

Description: This invention relates generally to ultrafiltration technology and, more particularly, to a spiral wound filtration module for use in cross-flow filtration and to a method of constructing same. The term "ultrafiltration" as used in the present application is intended to encompass microfiltration, nanofiltration, ultrafiltration and reverse osmosis and gas separation. A typical ultrafiltration device comprises a plurality of spiral wound filtration modules through which a fluid to be filtered passes. Such a module is made by winding one or more membrane leaves and permeate envelopes around a permeate tube. The membrane leaves are separated by feed spacer screens which are of a relatively large mesh size to accommodate fluid flow. The permeate passes through the membrane surface of the membrane leaves and is directed to the permeate tube by a permeate carrier sheet. Some type of external restraining means such as a hard shell, straps or a bypass screen, or a combination thereof may be used to hold the spirally wound leaves in tight formation around the tube. The spiral module is then loaded into a housing or pressure vessel which is operated at a slight pressure drop across the module as the fluid being filtered flows through. Concentrate is removed from one end of the module and permeate is removed from the permeate tube. Many applications of ultrafiltration technology involve food processing where sanitary conditions must be maintained at all times. This necessitates periodic cleaning with relatively harsh chemicals such as (by way of example only) chlorine containing compounds, other oxidizing agents, acids, alkalies and surfactants. These chemicals tend to degrade the membrane material, particularly in areas that are subject to stress. A typical procedure for constructing spiral filtration modules includes folding a membrane sheet in the area that is to be adjacent to the permeate tube. This fold area creates mechanical stresses in the membrane sheet both at the crease and at the point of the contact with the adjacent permeate carrier sheet. Other stress areas in a spiral wound membrane include the location of overlap between two membrane leaves and the overlap of the membrane with any underlying stitching or mechanical fastening devices. It is typical to employ some type of reinforcing in the fold area so as to reduce the mechanical stresses and prolong the life of the membrane. Two primary techniques are well known to those skilled in the art. The first is the utilization of reinforcing tape which is applied at the crease and extends outwardly from the crease a short distance over what is typically referred to as the fold area of the membrane. The second method of membrane reinforcement is to apply an adhesive in generally the same area as that to which the tape is applied and for the same effect. An example of this second method is contained in US-A-4842736. This patent further discloses a modification of the second method wherein, in place of a flowable adhesive, a soft melt thermoplastic material is employed from the backing a side of the membrane to fill the interstices of the backing material and penetrate the thickness of the backing all the way to the actual membrane material. The difficulties with these prior art techniques for strengthening the fold area of a spiral membrane are that the tape tends to eventually lose its adhesion and peel away, and glue is applied at a thickness such that, while the membrane is strengthened in the fold area, the glue has a tendency to create new stress points especially along its terminal edge. Both prior art techniques increase the thickness of the membrane leaf at the line of transition between reinforced and unreinforced membrane which is also a factor in introducing new stress points. Also, when either tape or glue is applied to the membrane surface (as opposed to the membrane backing), failure of either material may expose a "dead area" between the membrane surface and the failed glue or tape where the fluid being filtered may collect causing sanitation and eventual leakage problems. If the reinforcing is applied to the backing of the membrane, as contemplated in the referenced patent to Bray et al., there is no protection against surface cracks in the membrane itself at the crease or fold creating small crevices where fluid can collect and under some conditions create sanitation problems. It is therefore an object of the present invention to provide an improved ultrafiltration module and method of constructing same wherein the membrane material is strengthened in the area adjacent to the permeate tube which strengthening is accomplished without introducing stress points which can result in degradation and failure. Another one of the objectives of our invention is to provide an improved ultrafiltration module and method of constructing same which avoids the use of glue or tape in the area adjacent to the permeate tube and the inherent problems associated with these materials. It is also one of the aims of this invention to provide an improved ultrafiltration module and method of constructing same wherein the filtration membrane is strengthened without introducing physical discontinuities into the membrane which may eventually result in membrane leakage. US-A-4842736 discloses a leaf packet, useful in forming a spiral filtration module, which comprises a membrane sheet formed of a membrane material integrally joined to a backing material and presenting first and second sheet sections positioned substantially parallel to each other with the membrane surfaces thereof being adjacent; each section having at least one end in planar alignment with an end of the other section; and according to a first aspect of the present invention such a leaf packet is presented, whereby the sections are densified in the area of the aligned ends throughout their cross sections and the membrane material and the backing material are fused in the area of the aligned ends. The invention also includes a spiral filtration module for separating a fluid into a filtrate portion and a permeate portion, the module comprising a permeate carrier tube having a plurality of openings in the tube wall for receiving the permeate portion; at least one leaf packet spirally wound around the tube, the packet being in accordance with the first aspect of the invention; and permeate carrier means spirally wound around the tube between each of the leaf packets and joined to each adjacent ultrafiltration sheet along the sides and across the width of the carrier means. According to a second aspect of the present invention a method of preparing a leaf packet, useful in forming a spiral filtration module, comprises providing a membrane sheet formed of a membrane material integrally joined to a backing material and arranged to present first and second sheet sections positioned substantially parallel to each other with the membrane surfaces thereof being adjacent; each section having at least one end in planar alignment with an end of the other section; comprising densifying the sections throughout their cross sections in the area of the aligned ends so that their surface is rendered impermeable; fusing the backing material and the membrane material in the area of the aligned ends by the application of sufficient heat and pressure to raise the sheet to at least the glass transition temperature of the membrane material; and joining the sections together to provide the leaf packet. The invention thus offers an improved ultrafiltration module and method of constructing same which has had the membrane sheet densified through a fusion process to alter the physical properties of the membrane material by collapsing the membrane structure at the membrane surface while also densifying the membrane and providing structural reinforcing. A membrane reinforcing member may be fused to the membrane backing in the area adjacent to the permeate tube. The densifying and sealing of the membrane surface greatly reduces the chances for liquid to become trapped in small crevices or voids beneath or adjacent to the membrane surface. In the accompanying drawings: FIG. 1 is a fragmentary exploded perspective view of an ultrafiltration sheet to which a reinforcing material is to be applied; FIG. 2 is another perspective view showing a leaf packet prepared according to the present invention; FIG. 3 is a fragmentary perspective view of a permeate tube around which a plurality of leaf packets and feed channel spacers are positioned; FIG. 4 is a perspective view similar to FIG. 3 showing further details of construction of the individual leaf members which make up the ultrafiltration module; FIG. 5 is a fragmentary perspective view of a completed module; FIG. 6 is an exploded fragmentary perspective of a membrane leaf sandwiched between two feed channel spacers; and FIG. 7 is a perspective view of an alternative form of the invention. Referring initially to FIG. 1, an ultrafiltration membrane sheet is designated generally by the numeral 10 and comprises an ultrafiltration membrane 12 and a backing material 14. The membrane and the backing are integrally joined by techniques well known in the art to form the membrane sheet. Acceptable membrane materials include a wide range of thermoplastic resins which can be fabricated into a sheet having a pore structure and filtration capability. Known thermoplastic membrane materials include polysulfone, polyvinylidene fluoride, polyethersulfone, polyarylsulfone, polyvinylchloride, polyamides, cellulose acetate, polycarbonates, polytetrafluoroethylene, polyphenylene sulfide, polyethylene, polyethyleneterephthalate, polyamide-imide and polypropylene. Natural membrane materials such as cellulose may also be employed. A preferred material is polyethersulfone. Acceptable backing materials are woven or nonwoven synthetic materials having the strength necessary to reinforce the membrane and the ability to be integrally bound to the membrane while not interfering with the passage of permeate through the membrane. Suitable backing materials include polyester, polypropylene, polyethylene, and the family of polyamide polymers generally referred to as "nylon". Following accepted practice for constructing spiral wound ultrafiltration modules, a membrane leaf packet designated generally by the numeral 16 (FIG. 2) is prepared in the following manner. Membrane sheet 10 is divided to present first and second sheet sections 1O-X and 1O-Y. This may be accomplished by cutting across membrane sheet 10 or by folding across the sheet width as indicated in the drawings. The two sheet sections are then positioned with their ends overlying one another in alignment (i.e. the ends of the sections terminate subststantially with their end edges in a common plane extending perpendicularly to the planes of the sections), with backing 14 to the outside and the two membrane surfaces 12 facing each other. A relatively large mesh screen material presents a channel feed spacer 17 which is inserted between sheet sections 1O-X and 1O-Y. In most instances, the feed spacer will be utilized but it is possible to construct a module without this component. Prior to folding the membrane sheet 10 to form the leaf packet 16, aforedescribed, the sheet is densified in the fold area which is also the area of the aligned ends so as to provide increased strength and durability. Densification is preferably carried out by utilizing a thermoplastic or thermoset reinforcing material such as strip 18 that is compatible with and will fuse to membrane sheet 10, preferably to backing 14. Suitable reinforcing materials include polypropylene, polyethylene, and polyvinylbutyral and ionomer resins. A preferred material is an ionomer resin sold under the trademark Surlyn by E.I. DuPont de Nemours and Company of Wilmington, Delaware, U.S.A. The reinforcing strip 18 is placed on backing material 14 and then is fused to the sheet 10 by the application of heat and pressure from the membrane side of sheet 10. It may be desirable to wash or apply other surface treatment to the membrane or backing prior to fusing. Surface treatments may include solvents, surfactants or other chemicals alone or in combination. For most of the known membrane polymers and backing materials previously noted, a temperature of between 121°C (250°F) and 260°C (500°F) applied for one to six minutes along with a pressure which may be nominal (such as results from the weight of the heat source on the membrane) up to 1.38x10⁶Pa (200 pounds per square inch (p.s.i.)) will achieve an integral fusing of the reinforcing strip and the membrane sheet. A temperature range of 204°C (400°F) to 260°C (500°F) and a pressure of 1.38x10⁵Pa (20psi) to 6.89x10⁵Pa (100 p.s.i.) is the preferred operating range. For the preferred material (Surlyn) noted above, a temperature of approximately 204°C (400°F) applied for about 60 seconds along with a pressure of 5.17x10⁵Pa (75 p.s.i.), followed by gradual cooling under the same pressure for approximately 60 additional seconds, presents a product meeting the objectives of the invention. Generally, it is highly desirable to utilize relatively high melting point materials or materials having a relatively high glass transition temperature (e.g., above 204°C (400°F)) for the membrane material since the heat and pressure are applied to the membrane side. The glass transition temperature of the preferred membrane material, polyethersulfone, is approximately 210°C (410°F). To accomplish fusing of the backing 14 to the membrane material 12 the backing will normally have a somewhat lower glass transition temperature so that the heat from the membrane side, after passing through the membrane, will yield a temperature that is at least equal to or slightly above the backing glass transition temperature. This ensures fusing of the backing to the membrane. The preferred backing material, polyester, has a glass transition temperature of approximately 77°C (170°F). The glass transition temperature of the reinforcing strip 18 should also be substantially below that of the membrane material so that the heat from the membrane side will be sufficient to fuse the reinforcing to the backing. The glass transition temperature of the preferred reinforcing material, an ionomer resin, is approximately -40°C (-40°F) and the melting point of this material is 85°C (185°F). The heat source applied to the membrane side of the sheet 10 should be sufficient so that the temperature at the interface of the backing and reinforcing approaches the melting point of the ionomer being utilized as the reinforcing material. A thermal impulse sealer utilizing a nichrome wire shielded inside of a Teflon (registered trademark of E.I. DuPont de Nemours and Co. of Wilmington, Delaware, U.S.A.) covered flat bar and operated by a skilled technician is an acceptable and efficient means for accomplishing the fusing. The amount of pressure applied is less critical than the application temperature and it will be appreciated that wide variations in pressure are possible depending upon the particular materials that are employed. In some instances the weight of the heating source on the material may be sufficient. It is important that the application of heat and pressure be made from the membrane side 12 of sheet 18 to accomplish the desired densification of the membrane material as well as fusing of the membrane backing and reinforcing materials. By densification, is meant that the membrane surface pores are sufficiently collapsed so as to render the membrane surface impermeable. This densification of the membrane material strengthens it and, by rendering the membrane impermeable, precludes the substance being filtered from entering structural voids in the membrane where it can collect and create sanitation problems. A reliable indication of when the desired level of densification has been achieved for the preferred polyethersulfone membrane is when the membrane appearance changes from milky white to highly translucent. The densification step also encompasses an increase in the density of the backing and reinforcing materials to such an extent that the final thickness of the densified composite is approximately the same as the thickness of the unreinforced membrane sheet 10. The term "fusing" is meant to encompass the joining of separate, independent materials by the application of heat and at least minimal pressure to reach or exceed the glass transition points of the materials such that the final composite which is substantially homogeneous at the interface of the different materials cannot be separated without at least partial destruction of the joined materials. It is, of course, to be understood that the "fusing" may be accomplished utilizing a variety of heat sources including ultrasonic welding, radiation, and other known techniques or a combination of any heat and pressure sources which will bring about the physical change defined above. The fusing and membrane densification will generally occur substantially simultaneously. Returning now to the drawings, reinforcing strip 18 as it appears after sheet 10 is folded to present packet 16 is shown in FIG. 2. It is to be understood that the thickness of strip 18 and the demarcation between it and backing 14 have been exaggerated in FIG. 2 for purposes of illustration while in actual practice the fusing of the strip 18 to the sheet 10 simultaneously with the densification of the sheet will result in the membrane, membrane backing and reinforcing strip all being substantially integrally fused together with virtually no increase in total thickness of the reinforced sheet over the original thickness of sheet 10. Turning now to FIG. 3, a permeate tube 20 is shown with four leaf packets 16 circumferentially spaced around it. Permeate carrier sheets 24 are placed between each two leaf packets 16 to direct permeate to the interior of tube 20 through openings 26. Referring to FIG. 4, once leaf packet 16 and permeate carrier sheet 24 are in place on tube 20, the membrane leaves of the completed spiral module are formed in the following manner. A membrane sheet 1OA from one leaf packet is laid on a flat supporting surface and is then overlaid with a permeate carrier sheet 24A. A quantity of adhesive 28 is applied along the edges and across the width of carrier sheet 24A in the manner illustrated in FIG. 4. A membrane sheet 1OB from the next adjacent leaf packet 16 is then brought into contact with adhesive 28 so as to form a completed membrane leaf comprised of the two membrane sheets 1OA and 1OB separated by permeate carrier sheet 24A. Each membrane leaf is separated from an adjacent leaf by a feed channel spacer 17 from the previously assembled leaf packet. This construction is most clearly shown in the exploded view of FIG. 6. The final spiral wound assembly utilizes restraining bands 30 (FIG. 5) to hold the membrane leaves in place and an outerwrap 32 may be used to complete the module; the completed module being designated by the number 34. In the alternative embodiment of the invention shown in FIG. 7, membrane sheet 110 comprising membrane 112 and backing 114 has been treated to fuse and densify the area between the two broken lines (the fold area and the area of planar alignment of the ends of the two sheet sections 11O-X and 11O-Y) by the application of heat and pressure to the membrane side 112. While not accomplishing the same degree of densification as in the embodiment previously described, for some applications sheet 110 will prove to be adequate. A leaf packet is prepared from sheet 110 in the same manner as described previously for packet 16. Likewise, formation of the completed module utilizing sheet 110 to form the membrane leaves will be identical to the procedure described for the embodiment of FIGS. 1-6. The invention thus encompasses a method of preparing a leaf packet useful in forming a spiral filtration module which comprises providing two membrane sheet sections that have their ends in planar alignment (such as by folding a large sheet along the width to present two equal size sheet sections), optionally fusing a reinforcing material to the membrane sheet in the area of the aligned ends, simultaneously densifying the sheet along with the reinforcing, and providing a feed channel spacer (if desired) and locating it between the two sheet sections, followed by joining the sheet sections (such as by stapling the sections together) to present the leaf packet. The densification treatment includes the application of both heat and at least nominal pressure, to a sufficient extent to bring the membrane material and the backing to their glass transition points so that the heat reaches the backing material to fuse the backing and membrane materials at the fold area (or its equivalent in the case of two separate sheets), and may also include fusing a reinforcing material to the backing of the membrane. It is desirable to carry out the fusing to such an extent that the membrane 12, backing 14, and the reinforcing material (if utilized) are "fused" as that term is defined herein and also to accomplish densification of the membrane surface. It is inherent in any porous material that is utilized to make membrane surface 12 that certain voids will be present in the finished product. In the event of membrane failure these voids present areas for accumulating feed stream liquid which can cause serious sanitation problems in some applications. The present method and article densify the membrane to such extent that the membrane surface is sealed to the passage of fluid thus greatly reducing the possibility of contamination from liquid accumulating in any of the membrane void areas. The densification will also reduce the size of some subsurface voids while completely eliminating others to further reduce the risk of contamination. The fact that the present invention provides for a combination of fusing and densification of the membrane sheet greatly reduces the chances of membrane failure not only through strengthening the membrane but by sealing the membrane surface to the passage of liquid. It is particularly surprising that the fusing step encompassed by the invention has the desired strengthening effect, especially at the leading edge of the fuse, since it is well known that the application of heat to polymer materials may cause stresses which weaken the polymer once the heat is removed.

Claims: A leaf packet, useful in forming a spiral filtration module, comprising a membrane sheet (10) formed of a membrane material (12) integrally joined to a backing material (14) and presenting first and second sheet sections (10-X, 10-Y) positioned substantially parallel to each other with the membrane surfaces thereof being adjacent; each section having at least one end in planar alignment with an end of the other section; characterised by the sections being densified in the area of the aligned ends throughout their cross sections and the membrane material and the backing material being fused in the area of the aligned ends. A packet according to claim 1, wherein there is included a reinforcing material (18) fused to the backing material (14). A packet according to claim 2, wherein the reinforcing material (18) is fused to the backing material (14) of the sheet in the area of the aligned end. A packet according to any one of the preceding claims, wherein there is included a feed channel spacer (17) sandwiched between the first and second sheet sections (10-X; 10-Y). A packet according to any one of the preceding claims, wherein the membrane material (12) has a glass transition temperature that is higher than the glass transition temperature of the backing material (14). A spiral filtration module for separating a fluid into a filtrate portion and a permeate portion, the module comprising a permeate carrier tube (20) having a plurality of openings (26) in the tube wall for receiving the permeate portion; at least one leaf packet (16) spirally wound around the tube, the packet being in accordance with any one of the preceding claims; and permeate carrier means (24) spirally wound around the tube between each of the leaf packets and joined to each adjacent ultrafiltration sheet along the sides and across the width of the carrier means. A method of preparing a leaf packet, useful in forming a spiral filtration module, the method comprising providing a membrane sheet (10) formed of a membrane material (12) integrally joined to a backing material (14) and arranged to present first and second sheet sections (10-X; 10-Y) positioned substantially parallel to each other with the membrane surfaces thereof being adjacent; each section having at least one end in planar alignment with an end of the other section; characterised by densifying the sections throughout their cross sections in the area of the aligned ends so that their surface is rendered impermeable; fusing the backing material and the membrane material in the area of the aligned ends by the application of sufficient heat and pressure to raise the sheet to at least the glass transition temperature of the membrane material; and joining the sections together to provide the leaf packet. A method according to claim 7, wherein the fusing comprises the application of heat and pressure to the membrane side of the sheet. A method according to claim 7 or claim 8, wherein the fusing step comprises fusing a reinforcing material (18) to the backing material (14). A method according to any one of claims 7 to 9, wherein the sheet comprises an ultrafiltration membrane (12) and a membrane backing (14). A method according to any one of claims 7 to 10, wherein the densifying and the fusing steps occur simultaneously.

Inventors: MCDERMOTT THOMAS C, SKELTON DANIEL F, MCDERMOTT, THOMAS C., SKELTON, DANIEL F.
Applicants: KOCH MEMBRANE SYSTEMS INC, KOCH MEMBRANE SYSTEMS, INC
Application year: 1991
Main classification: B01D63
IPC codes: B01D63, B01D65