Process for dehydration of organic oxygenates

Abstract: A polyethylenimine membrane which has been cross-linked by heat treating at 100°C-200°C for 3-20 minutes may be used to dewater isopropanol or methyl ethyl ketone/toluene mixtures.

Description: This invention relates to the dehydration of organic oxygenates such as isopropyl alcohol. More particularly it relates to a membrane technique for effecting separation of water from an aqueous mixture containing isopropyl alcohol. As well known to those skilled in the art, it is possible to remove water from mixtures thereof with organic liquids by various techniques including adsorption or distillation. These conventional processes, particularly distillation, are however, characterized by high capital cost. In the case of distillation for example the process requires expensive distillation towers, heaters, heat exchangers (reboilers, condensers), together with a substantial amount of auxiliary equipment typified by pumps, collection vessels, vacuum generating equipment. Such operations are characterized by high operating costs: principally costs of heating and cooling - plus pumping. Furthermore the properties of the materials being separated, as is evidenced by the distillation curves, may be such that a large number of plates may be required, etc. when the material forms an azeotrope with water, additional problems may be present which, for example, would require that separation be effected in a series of steps (e.g., as in two towers) or by addition of extraneous materials to the system. There are also comparable problems which are unique to adsorption systems. It has been found to be possible to utilize membrane systems to separate mixtures of miscible liquids by pervaporation. In this process, the charge liquid is brought into contact with a membrane film; and one component of the charge liquid preferentially permeates the membrane. The permeate is then removed as a vapor from the downstream side of the film - typically by sweeping with a carrier gas or by reducing the pressure below the saturated vapor pressure of the permeating species. JP-A-59005304 (Agency of Ind. Sci. Tech.) discloses that a mixture of water and an organic liquid may be separated by pervaporation using a composite membrane obtained by cross-linking polyethyleneimine and a di-functional aromatic cross-linking agent containing acid halide groups and/or isocyanate groups on a microporous supporting membrane. US-A-4659590 (Neidlinger) describes a method for concentrating an aqueous mixture of ethanol by pervaporation, using a membrane similar to that disclosed in JP-A-59005304. JP-A-56129007 describes a composite membrane comprising a porous support coated with a thin film of a heat-crosslinkable polymer (polyethyleneimine) which has been heated to obtain a cross-linked polyethyleneimine film having small pores, and finally coated with a dense (i.e. non-porous) layer. Illustrative membranes which have been employed in prior art techniques include those set forth in the following list: Separating Layer References Nafion™ brand of perfluorosulfonic acid Cabasso and Liu J. Memb. Sci. 24, 101 (1985) Sulfonated polyethylene Cabasso, Korngold & Liu J. Pol. Sci Letters, 23, 577-581 (1985) Fluorinated polyether or Carboxylic Acid fluorides USP 4,526,948 to Dupont as assignee of Resnick Selemion™ AMV brand of Asahi Glass cross-linked styrene butadiene (with quaternary ammonium residues on a polyvinyl chloride backing) Wentzlaff Boddeker & Hattanback, J. Memb. Sci. 22, 333 (1985) Cellulose triacetate Wentzlaff, Boddeker & Hattanback, J. Memb. Sci. 22, 333 (1985) Polyacrylonitrile Neel, Aptel & Clement Desalination 53, 297 (1985) Crosslinked Polyvinyl Alcohol EP-A-0096339 (GFT) Poly(maleimideacrylonitrile) Yoshikawa et al J. Pol. Sci. 22, 2159 (1984) Dextrine - isophorone-diisocyanate Chem. Econ. Eng. Rev. Vol.17. No. 12, p.34 (1985) The cost effectiveness of a membrane is determined by the selectivity and productivity. Of the membranes commercially available, an illustrative membrane of high performance is that disclosed in EP-A-0096339 (GFT). EP-A-0096339 discloses, as cross-linking agents for the polyvinyl alcohol membrane, diacids (typified by maleic acid or fumaric acid); dihalogen compounds (typified by dichloroacetone or 1,3-dichloroisopropanol); aldehydes, including dialdehydes, typified by formaldehyde. These membranes are said to be particularly effective for dehydration of aqueous solutions of ethanol or isopropanol. This reference discloses separation of water from alcohols, ethers, ketones, aldehydes, or acids by use of composite membranes. Specifically, the composite includes (i) a backing typically about 120 µm in thickness, on which is positioned (ii) a microporous support layer of a polysulfone or a polyacrylonitrile of about 50 µm thickness, on which is positioned (iii) a separating layer of cross-linked polyvinyl alcohol about 2 microns in thickness. US-A-4,728,429 to Cabasso et al, US-A-4,067,805 to Chiang et al, US-A-4,526,948 to Resnick, US-A-3,750,735 to Chiang et al, US-A-4,690,766 to Linder et al, and US-A-4,798,674 to Pasternak, Bartels and Reale, Jr. provide additional background. See also Yamamoto et al JP-A-61 161 109 of 21 July 1986 Preparation of Separation Membranes . It is an object of this invention to provide a novel composite membrane able to effect separation of water from organic oxygenates such as isopropyl alcohol. Other objects will be apparent to those skilled in the art. The present invention relates to a membrane comprising a porous support and a non-porous separating layer of a polyimine polymer which has been thermally cross-linked, with the proviso that said membrane does not include a cross-linking agent, for use in separating water from an aqueous charge mixture of organic oxygenate, and the use of such a membrane in separating water from an aqueous charge mixture of organic oxygenate by pervaporation. The invention further provides a method of concentrating an aqueous charge mixture of organic oxygenate which comprises passing said aqueous charge into contact with the high pressure side of a non-porous separating layer of a membrane comprising a porous support and a non-porous separating layer of a polyimine polymer which has been thermally cross-linked, with the proviso that said membrane does not include a cross-linking agent, and maintaining a pressure drop across said layer whereby at least a portion of said water and a lesser portion of organic oxygenate from said aqueous charge pass by pervaporation through said separating layer as a lean mixture containing more water and less organic oxygenate than are present in said aqueous charge and leaving a rich liquid containing less water and more organic oxygenate than are present in said aqueous charge, recovering from the low pressure side of said non-porous polyimine separating layer said lean mixture containing more water and less organic oxygenate than are present in said charge aqueous mixture, said lean mixture being recovered in vapor phase at a pressure below the vapor pressure thereof; and recovering from the high pressure side of said non-porous polyimine separating layer said rich liquid containing a lower water content and a higher organic oxygenate content than are present in said charge aqueous mixture. In accordance with certain of its other aspects, this invention is directed to a membrane comprising a porous support and a non-porous separating layer of thickness of 0.2-10.0 µm of polyimine polymer of molecular weight M n of 40,000 - 100,000 which has been thermally cross-linked, without the addition of a cross-linking agent. The composite structure of this invention includes a multi-layer assembly which in the preferred embodiment preferably includes a porous carrier layer which provides mechanical strength and support to the assembly. THE CARRIER LAYER This carrier layer, when used, is characterized by its high degree of porosity and mechanical strength. It may be fibrous or non-fibrous, woven or non-woven. In the preferred embodiment, the carrier layer may be a porous, flexible, non-woven fibrous polyester. A preferred non-woven polyester carrier layer may be formulated of non-woven, thermally-bonded strands and characterized by a fabric weight of 80 ± 8 grams per square yard (96 ± 9.6g/m²), a thickness of 4.2 ± 0.5 mils (106.7 ± 12.7 µm), a tensile strength (in the machine direction) of 31 psi (213 kPa) and (in cross direction) of 10 psi (69 kPa) and a Frazier air permeability of 6 cuft/min/sq. ft. @ 0.5 inches of water (182 cm³/min/cm² @ 125 Pa). THE POROUS SUPPORT LAYER The porous support layer of this invention is preferably formed of a sheet of polysulfone polymer or more preferably of polyacrylonitrile. Typically, the polysulfone layer may be of thickness of 40-80 µm , say 50 µm and the polysulfone of molecular weight M n of 5,000-100,000, preferably 20,000-60,000 say 40,000. The polysulfone layer is preferably characterized by a pore size of less than about 5 x 10⁻⁸m (500A) and typically about 2 x 10⁻⁸m (200A). This corresponds to a molecular weight cut-off of less than about 25,000 typically about 20,000. The sulfone polymers which may be employed may include those made from cumene containing isopropylidene groups in the backbone; e.g. These isopropylidene sulfones containing repeating units including ether-aromatic-isopropylidene-aromatic-ether-aromatic-sulfone-aromatic groups may typically have a molecular weight M n of 15,000-30,000, a water absorption (at 20°C) of about 0.85w%, a glass transition temperature of 449 K, a density of 1.25 mg/m³, a tensile strength (at 20°C) at yield of 10,000 psi, (69000 kPa) and a coefficient of linear thermal expansion of 2.6 x 10⁻⁵ mm/mm/°C. It is found, however, that when the sulfone polmers are employed in practice of the process of this invention, it is preferred to use those which are free of isopropylidene moieties in the backbone chain and wherein the phenylene groups in the backbone are bonded only to ether oxygen atoms and to sulfur atoms. These preferred sulfone polymers, which may be typically prepared from may be characterized by a backbone containing the following repeating group: A preferred sulfone polymer may be a polyether sulfone which is free of isopropylidene moieties in the backbone chain and wherein the phenylene groups in the backbone are bonded only to ether-oxygen atoms and to sulfur atoms. This polymer may be characterized by molecular weight M n of 25,000, water absorption @ 20°C of 2.1w%, glass transition temperature of 487 K, tensile strength at yield of 2530 MPa (12,200 psig) at 20°C; and coefficient of linear thermal expansion of 5.5 x 10⁻⁵ mm/mm/°C. This polymer layer has a molecular weight cut off of about 20,000 and has a pore size of about 2 x 10⁻⁸m (200A). It is, however, preferred to use, as the porous support layer, a polyacrylonitrile polymer typically having a molecular weight cut off of about 40,000 THE SEPARATING LAYER The separating layer which permits attainment of separation in accordance with the process of this invention includes a non-porous film or membrane of 0.2-10.0 µm , say about 3.0 µm of a polyimine polymer of molecular weight M n of about 40,000-100,000, say about 60,000 (prior to cross-linking), which is thermally cross-linked without the addition of a cross-linking agent. Polyimine polymers are characterized by the presence of recurring -N-R''- groups as integral parts of the main polymer chain. Typical structural formula of linear polyimines may be represented as H₂N-R''[N-R''] n -NH₂ wherein n represents the degree of polymerization or number of recurring groups in the polymer chain. In the above formula, R'' may preferably be a hydrocarbon group selected from the group consisting of alkylene, aralkylene, cycloalkylene, arylene, and alkarylene, including such radicals when inertly substituted. When R'' is alkylene, it may typically be methylene, ethylene, n-propylene, iso-propylene, n-butylene, i-butylene, sec-butylene, amylene, octylene, decylene, octadecylene, etc. When R'' is aralkylene, it may typically be benzylene, beta-phenylethylene, etc. When R'' is cycloalkylene, it may typically be cyclohexylene, cycloheptylene, cyclooctylene, 2-methylcycloheptylene, 3-butylcyclohexylene, 3-methylcyclohexylene, etc. When R'' is arylene, it may typically be phenylene, naphthylene, etc. When R is alkarylene, it may typically be tolylene, xylylene, etc. R'' may be inertly substituted i.e. it may bear a non-reactive substituent such as alkyl, aryl, cycloalkyl,ether, etc. typically inertly substituted R'' groups may include 3-methoxypropylene, 2-ethoxyethylene, carboethoxymethylene, 4-methylcyclohexylene, p-methylphenylene, p-methylbenzylene, 3-ethyl-5-methylphenylene, etc. The preferred R'' groups may be phenylene or lower alkylene, i.e. C₁-C₁₀ alkylene, groups including e.g. methylene, ethylene, n-propylene, i-propylene, butylene, amylene, hexylene, octylene, decylene, etc. R'' may preferably be phenylene or ethylene -CH₂CH₂-. Illustrative polyimine polymers include those of molecular weight M n of 40,000-100,000, say 60,000. Suitable polyimines may include the following, the first listed being preferred: A. Virginia Chemical Company Corcat™ P-600 brand of polyethylenimine ( M n of 60,000) in 33 w% aqueous solution - Brookfield viscosity @ 25°C of 5000 cP, Sp.Gr at 25°C of 1.04-1.06, and pH of 10-11, having the formula wherein R is H or (CH₂CH₂N) x (containing 30% primary, 40% secondary, and 30% tertiary amines). B. Dow Chemical Co Tydex™ 12 brand of polyethyleneimine ( M n of 50,000) in 30w% aqueous solution having the same formula as the Corcat™ P-600 membrane. The separating layer may be formed on the porous support layer (preferably mounted on the carrier layer) as by coating with a 5-20w%, say 15w% solution of the polyimine in water/isopropanol solvent. Preferred solvent may include 0-100w%, say 15w% isopropanol. Thermal cross-linking of the polyimine membrane may be effected by heating the membrane to 100°C-200°C, typically 120°C-140°C, say 125°C for 3-20 minutes, typically 5-15 minutes, say 10 minutes. THE COMPOSITE MEMBRANE It is a feature of this invention that it may utilize a composite membrane which comprises (i) a carrier layer characterized by mechanical strength, for supporting a porous support layer and a separating layer (ii) a porous support layer such as a polyacrylonitrile membrane of 40-80 µm and of molecular weight cut off of 25,000-100,000, and (iii) as a non-porous separating layer a polyimine of molecular weight M n of 40,000-100,000, which has been thermally cross-linked without the addition of a cross-linking agent. It is possible to utilize a spiral wound module which includes a non-porous separating layer membrane mounted on a porous support layer and a carrier layer, the assembly being typically folded and bonded or sealed along all the edges but an open edge - to form a bag-like unit which preferably has the separating layer on the outside. A cloth spacer, serving as the permeate or discharge channel is placed within the bag-like unit. The discharge channel projects from the open end of the unit. There is then placed on one face of the bag-like unit, adjacent to the separating layer, and coterminous therewith, a feed channel sheet - typically formed of a plastic net. The so-formed assembly is wrapped around a preferably cylindrical conduit which bears a plurality of perforations in the wall - preferably in a linear array which is as long as the width of the bag-like unit. The projecting portion of the discharge channel of the bag-like unit is placed over the perforations of the conduit; and the bag-like unit is wrapped around the conduit to form a spiral wound configuration. It will be apparent that, although only one feed channel is present, the single feed channel in the wound assembly will be adjacent to two faces of the membrane layer. The spiral wound configuration may be formed by wrapping the assembly around the conduit a plurality of times to form a readily handleable unit. The unit is fitted within a shell (in manner comparable to a shell-and-tube heat exchanger) provided with an inlet at one end and an outlet at the other. A baffle-like seal between the inner surface of the shell and the outer surface of the spiral-wound unit prevents fluid from bypassing the operative membrane system and insures that fluid enters the system principally at one end. The charge passes from the feed channel, into contact with the separating layer and thence therethrough, into the permeate channel and thence therealong to and through the perforations in the conduit through which it is withdrawn as net permeate. In use of the spiral wound membrane, charge liquid is permitted to pass through the plastic net which serves as a feed channel and thence into contact with the non-porous separating membranes. The liquid which does not pass through the membranes is withdrawn as retentate. The liquids which permeates the membrane passes into the volume occupied by the permeate spacer and through this permeate channel to the perforations in the cylindrical conduit through which it is withdrawn from the system. In another embodiment, it is possible to utilize the system of this invention as a tubular or hollow fibre. In this embodiment, the polyacrylonitrile porous support layer may be extruded as a fine tube with a wall thickness of typically 0.001-0.1 mm. The extruded tubes are passed through a bath of polyethyleneimine which is cross-linked and cured in situ. A bundle of these tubes is secured (with an epoxy adhesive) at each end in a header; and the fibers are cut so that they are flush with the ends of the header. This tube bundle is mounted within a shell in a typical shell-and-tube assembly. In operation, the charge liquid is admitted to the shell side and passes around the tubes and exits as retentate. During passage, permeate passes through the non-porous separating layer and permeate is collected in the tube side. PERVAPORATI0N It is a feature of the non-porous polyimine polymer separating layer that it is found to be particularly effective when used in a pervaporation process. In pervaporation, a charge liquid containing a more permeable and a less permeable component is maintained in contact with a non-porous separating layer; and a pressure drop is maintained across that layer. The charge liquid dissolves into the membrane and diffuses therethrough. The permeate which passes through the membrane and exits as a vapor may be recovered by condensing at low temperature or alternatively may be swept away by use of a moving stream of gas. Preferably, the permeate side of the membrane is maintained-at a low pressure, typically 0.66 kPa (5 mm. Hg). For general background on pervaporation, note US-A-3,950,247; US-A-4,035,291. It is a feature of the process of this invention that the novel membrane may be particularly useful in pervaporation processes for dewatering aqueous mixtures of organic oxygenates. It may be possible to utilize the process of this invention to remove water from immiscible mixtures therewith as in the case of ethyl acetate (solubility in water at 15°C of 8.5 parts per 100 parts of water). It will be apparent to those skilled in the art that it may be desirable to separate large quantities of water from partially miscible systems as by decantation prior to utilizing the process of the invention to remove the last traces of water. The advantages of the instant invention are more apparent when the charge liquid is a single phase homogeneous aqueous solution as is the case for example with isopropanol. The system may also find use in the case of slightly soluble liquids wherein two phases are present (i) water-oxygenate first phase and, ash a second phase (ii) either water or oxygenate. Clearly those charge liquids which contain only a small portion of an immiscible second liquid phase may benefit most from the process of this invention. It is also a feature of this invention that it may be particularly useful to separate azeotropes such as isopropanol-water. The charge organic oxygenates which may be treated by the process of this invention may include alcohols, glycols, acids, esters, ketones, aldehydes, etc. It will be apparent to those skilled in the art that the charge organic oxygenates used should be inert with respect to the separating membrane. Clearly a system wherein the membrane is attacked by the components of the charge liquid will not yield significant separation for any reasonable period of time. Best results may be achieved when treating alcohols (such as isopropanol) or ketones (such as methyl ethyl ketone). Results achieved with acids are generally less satisfactory. Illustrative alcohols may include ethanol, propanol, n-butanol, i-butanol, t-butanol, amyl alcohols, hexyl alcohols. Illustrative glycols may include ethylene glycol, propylene glycols, butylene glycol or glycol ethers such as diethylene glycol, triethylene glcol, or triols, including glycerine. Illustrative acids may include formic acid, oxalic acid, acetic acid, propionic acid. Illustrative esters may include ethyl acetate, methyl acetate, butyl acetate, methyl benzoate, ethylene glycol mono acetate, propylene glycol monostearate. Illustrative ethers may include tetrahydroforan, diethyl ether, and diisopropyl ether. Illustrative ketones may include acetone, methyl ethyl ketone, acetophenone. Illustrative aldehydes may include formaldehyde, acetaldehyde, propionaldehyde. It is believed that the advantages of this invention are most apparent where the organic oxygenate is a liquid which is infinitely miscible with water - typified by isopropyl alcohol. A typical charge may be an aqueous solution containing 70% - 95%, say 80 w% isopropanol. In practice of the pervaporation process of this invention, the charge aqueous organic oxygenate solution typically at 40°C-120°C, say 80°C may be passed into contact with the non-porous separating layer of the membrane of this invention. A pressure drop of about one atmosphere is commonly maintained across the membrane. Typically, the feed or charge side of the membrane is at about atmospheric pressure and the permeate or discharge side of the membrane is at a pressure of about 0.26-6.64, preferably 0.66-2.65, say 1.33 kPa (2-50 preferably 5-20, say 10 mm Hg). The permeate which passes through the membrane includes water and a small proportion of the organic oxygenate from the charge liquid. Typically, the permeate contains 80 - 99.0, say 99w% water. Permeate is recovered in vapor phase. Pervaporation may typically be carried out at a flux of 0.01-10, say 1.9 gallons per square foot per day which corresponds to about 0.17-16.9, say 3.2 kilograms per square meter per hour (kg/m².h). Typically, the units may show good separation (measured in terms of w% organic oxygenate in the permeate during pervaporation of an aqueous solution of organic oxygenate through a polyimine separating layer. DESCRIPTION OF SPECIFIC EMBODIMENTS Practice of the process of this invention may be apparent to those skilled in the art from the following examples wherein, as elsewhere in this specification, all parts are parts by weight unless otherwise stated. An asterisk (*) indicates a control example. EXAMPLE I In this example which represents the best mode of carrying out the process of this invention, the carrier layer is the woven polyester backing described supra. The porous support layer is the commercially available layer of Daicel DUY-L™ polyacrylonitrile of molecular weight cut off of 40,000. The polyethyleneimine PEI separating layer is fabricated from the Corcat™ P-600 brand of polyethyleneimine of the Table supra ( M n of 60,000). This 33 w% aqueous solution is diluted to 15.0 w% by addition of IPA/water. This solution is deposited on the porous support layer and is then thermally cross-linked. The assembly containing the preferred microporous polyacrylonitrile supra as porous support layer and the woven polyester backing supra as carrier layer (total area Ca 45 cm²) is contacted with the dilute aqueous solution of polyethyleneimine. The assembly is then thermally cross-linked in an oven at 125°C for 5 minutes. The membrane is mounted in a standard cell. There is admitted to the cell and to the non-porous polyethyleneimine separating layer a charge liquid containing methyl ethyl ketone and toluene in 2:1 weight ratio plus 3.0w% water - at 70°C. Separation is carried out at 70°C and a permeate pressure is 0.66 kPa (5 mm Hg). Selectivity is measured and reported as % water in permeate. Clearly a higher selectivity is desired, as this means that the retentate desirably contains less water and the permeate desirably contains more water. Flux is measured as kilograms per square meter per hour (kg/m².h). In this Example, the Selectivity is 98.5% water and the Flux is 3.2 kg/m².h. EXAMPLES II - IV In this series of Examples, the procedure of Example I is duplicated, except that the time of thermal cross-linking is 7, 9 and 10 minutes in Examples II, III and IV, respectively. Example Time Permeate Conc. w% Water Flux (kg/m².h) I 5 98.5 3.2 II 7 94.3 1.4 III 9 98.1 2.1 IV 10 97.8 2.2 EXAMPLES V - VIII In this series of Examples, the charge liquid contains 14.4w% water and 85.6w% isopropanol at 70°C. Example Time Permeate Conc. w% Water Flux (kg/m².h) V 5 76.1 3.5 VI 7 91.0 3.6 VII 9 96.8 3.1 VIII 10 97.5 2.8 Results comparable to the above may be attained it the charge is Example Charge IX 95w% ethanol 5w% water X 80% ethylene glycol 20% water XI 70% acetic acid 30% water XII 70% ethyl acetate 30% water XIII 90% methyl isobutyl ketone 10% water XIV Although this invention has been illustrated by reference to specific embodiments, it will be apparent to those skilled in the art that various changes and modifications may be made which clearly fall within the scope of the invention as defined by the claims.

Claims: A membrane comprising a porous support and a non-porous separating layer of a polyimine polymer which has been thermally cross-linked, with the proviso that said polyimine polymer has not been crosslinked with a cross-linking agent, for use in separating water from an aqueous charge mixture of organic oxygenate. A membrane as claimed in Claim 1 wherein said polyimine polymer is polyethyleneimine. A membrane as claimed in Claim 1 or Claim 2 wherein said polyimine polymer has been thermally cross-linked at 100°C-200°C. A membrane as claimed in any one of Claims 1 to 3 wherein said polyimine polymer has been thermally cross-linked from 3 to 20 minutes. A method of concentrating an aqueous charge mixture of organic oxygenate which comprises: passing said aqueous charge mixture into contact with the high pressure side of a non-porous separating layer of a membrane, maintaining a pressure drop across said layer whereby at least a portion of said water and a lesser portion of organic oxygenate from said aqueous charge mixture pass by pervaporation through said separating layer as a lean mixture containing more water and less organic oxygenate than are present in said aqueous charge mixture and leaving a rich liquid containing less water and more organic oxygenate than are present in said aqueous charge mixture, recovering from the low pressure side of said non-porous separating layer said lean mixture containing more water and less organic oxygenate than are present in said charge aqueous mixture, said lean mixture being recovered in vapor phase at a pressure below the vapor pressure thereof, recovering from the high pressure side of said non-porous separating layer said rich liquid containing a lower water content and a higher organic oxygenate content than are present in said charge aqueous mixture, and wherein said membrane is a membrane as claimed in any one of the claims 1 to 4. A method as claimed in Claim 5 wherein said charge aqueous composition comprises a ketone. A method as claimed in Claim 6 wherein said ketone is methyl ethyl ketone or methyl isobutyl ketone or a mixture thereof. A method as claimed in any one of the claims 5 to 7 wherein said charge aqueous composition contains a ketone and toluene. A method as claimed in any one of the claims 5 to 8 wherein said charge aqueous composition contains an alcohol. The method as claimed in Claim 9 wherein said charge aqueous composition contains isopropanol. The use of a membrane as claimed in claim 1, in separating water from an aqueous charge mixture of organic oxygenate by pervaporation.

Inventors: REALE JOHN JR, REALE, JOHN, JR.
Applicants: TEXACO DEVELOPMENT CORP, TEXACO DEVELOPMENT CORPORATION
Application year: 1991
Main classification: B01D61
IPC codes: B01D71, B01D61, C07C45, C07C29, B01D69