Novel alpha-cyanoacrylate and adhesive composition

Abstract: A novel neopentyl α-cyanoacrylate is provided. It has superior adhesive properties even at high temperatures and whitening-preventing property.

Description: Background of the Invention The present invention relates to a novel α-cyanoacrylate and a cyanoacrylate-based adhesive composition containing same. α-Cyanoacrylates such as methyl α-cyanoacrylate and ethyl α-cyanoacrylate are polymerized and cured rapidly by the action of a small amount of water present on the surface of a material to be bonded and afford an adhesive force of an extremely high strength, so are widely used as room-temperature one-pack type instantaneous adhesives for the bonding of metals, plastics, rubber, wood and the like. As α-cyanoacrylate there are known propyl α-cyanoacrylate, allyl α-cyanoacrylate, propargyl α-cyanoacrylate, 2,2,2-trifluoroethyl α-cyanoacrylate, 2,2,3,3-tetrafluoropropyl α-cyanoacrylate, 2-methoxyethyl α-cyanoacrylate, 2-ethoxyethyl α-cyanoacrylate and the like in addition to the above mentioned methyl and ethyl α-cyanoacrylates. Generally, in the case where an α-cyanoacrylate is used as an adhesive, a portion thereof volatilizes and is polymerized by water contained in the air and adheres as white powder to the surrounding portion of a bonded part (whitening phenomenon), thus impairing the appearance of the bonded material. When used in the assembly of electric and electronic parts, the volatilized monomer contaminates the contact portion and causes defective contact, or cures in a moving part, thereby causing malfunction. Moreover, the thermal stability of the cured product is not sufficient and the bonding strength is reduced rapidly over 100°C. It is known that α-cyanoacrylates having an unsaturated bond in the ester portion have improved thermal stability. In this case the cured or adhered portion is heat treated at an appropriate temperature (100°C - 150°C) in order to improve the thermal stability. However, the adhesive properties at high temperature are not improved. It is the object of the present invention to overcome the above mentioned drawbacks of the prior art. More concretely, it is the object of the present invention to provide a novel compound having superior adhesive properties as an instantaneous adhesive and superior whitening-preventing property and thermal stability including high temperature adhesive properties. Summary of the Invention The present invention resides in a novel neopentyl α-cyanoacrylate having the chemical structural formula: and an adhesive containing the above compound as an essential component. The adhesive may further contain one or more conventional α-cyanoacrylates which may be liquid compound at room temperature. The amount of the neopentyl α-cyanoacrylate is preferably 5 to 85 wt % based on the weight of adhesive components. Detailed Description of the Invention The novel compound, neopentyl α-cyanoacrylate exhibits excellent instantaneous adhesive properties. It has a melting point of 40°C and is a solid at a room temperature It can be used by itself as hot-melt type instantaneous adhesive and also as a liquid instantaneous adhesive in admixture with one or more conventional cyanoacrylates in the same manner as conventional instantaneous adhesives. The instantaneous adhesive containing neopentyl α-cyanoacrylate as an essential component does not induce the whitening phenomenon and is superior in thermal stability, especially in high temperature-bonding strength. Neopentyl α-cyanoacrylate may be used alone or in combination with one or more conventional α-cyanoacrylates. Such conventional α-cyanoacrylates are those represented by the following general formula: wherein R is a hydrocarbon group such as alkyl, alkenyl, or alkynyl, or an alkoxy hydrocarbon group such as alkoxyalkyl. Examples are methyl α-cyanoacrylate, ethyl α-cyanoacrylate, isopropyl α-cyanoacrylate,those wherein R is alkoxyalkyl, e.g. 2-methoxyethyl α-cyanoacrylate and 2-ethoxyethyl α-cyanoacrylate, those wherein R is alkenyl, e.g. allyl α-cyanoacrylate, and those wherein R is alkynyl, e.g. propargyl α-cyanoacrylate. When using conventional cyanoacrylates in combination with neopentyl α-cyanoacrylate, the latter is preferably in an amount of 85 wt% or less, more preferably 5 to 85 wt% based on the weight of adhesive components. If the amount of neopentyl α-cyanoacrylate is more than 85 wt%, the composition becomes a solid at a room temperature (i.e. 20°C). Neopentyl α-cyanoacrylate of the present invention may be prepared by the following reactions. Neopentyl α-cyanoacetate having the following structural formula: is prepared and then it is reacted with formaldehyde or paraformaldehyde in the presence of a basic catalyst to produce a condensation polymer, and then the condensation polymer thus produced is heat-depolymerized or thermally decomposed to produce neopentyl α-cyanoacrylate. Neopentyl α-cyanoacrylate thus obtained is a solid at a room temperature but it is desirable to add thereto a stabilizer in order to store it more stably. Examples of such stabilizer include, as anionic polymerization inhibitors, sulfurous acid (SO₂), sultone compounds, organic sulfonic acids, mercaptans, trifluoroacetic acid, and fluoroboric acid, and as radical polymerization inhibitors, quinones, catechol, pyrogallol, and 2,6-di-t-butylphenol. The amount of these stabilizers differs depending on the respective inhibiting abilities, but is preferably in the range of 1 to 10,000 ppm, more preferably 10 to 1,000 ppm, relative to the monomer. The following examples are given to illustrate the present invention in more detail. The "part" and "%" in the following description are all by weight. Example 1 (Preparation of Neopentyl α-Cyanoacetate) 51g (0.6 mole) of cyanoacetic acid, 74g (0.84 mole) of neopentyl alcohol, 1g of sulfuric acid and 100g of toluene were reacted under reflux and water produced was removed by azeotropic distillation. Thereafter, the mixture thus produced was cooled to room temperature and filtered to remove insoluble matter. The filtrate was washed with water and dried overnight with magensium sulfate. Then, the desiccant was filtered off and the solvent was removed under reduced pressure, followed by vacuum distillation to afford 87.1g of neopentyl α-cyanoacetate (b.p. 79 - 81°C/3mmHg, yield 94%). 1R (neat)cm⁻¹: 2262, 1751 60MHz ¹H-NMR (CDCl₃/TMS) δ(ppm): 3.87 (s, 2H), 3.46 (s, 2H), 0.97 (s, 9H) 90MHz ¹³C-NMR (CDCl₃) δ(ppm): 162.91, 113.06, 75.41, 31.03, 25.86, 24.30 (Preparation of Neopentyl α-Cyanoacrylate) 46.5 (0.3 mole) of neopentyl α-cyanoacetate, 8.1g (0.27 mole) of paraformaldehyde, 140g of toluene and 46.5 mg of triethylenediamine were reacted together under reflux and water was removed by azeotropic distillation. Then, 23.5g of dioctyl phthalate, 0.465g of hydroquinone and 0.93g of phosphorus pentoxide were added and depolymerization allowed to take place at 150 - 210°C under a reduced pressure to afford 21.65g of crude neopentyl α-cyanoacrylate. Redistillation thereof afforded (8.3g of neopentyl α-cyanoacrylate (b.p. 65 - 67°C/2 mmHg, m.p. 40 - 41°C, yield 36%). 60MHz ¹H-NMR (CDCl₃/TMS) δ(ppm): 7.01 (s, 1H), 6.61 (s, 1H), 3.95 (s, 2H) 1.20 (s, 9H) 90MHz ¹³C-NMR (CDCl₃) δ(ppm): 160.14, 142.78, 116.44, 114.08, 75.46, 31.22, 25.95 Example 2 Adhesives were prepared by mixing neopentyl α-cyanoacrylate (NPCA) and ethyl α-cyanoacrylate (ECA) as a conventional α-cyanoacrylate in such proportions as shown Table 1 below and then incorporating therein 20 ppm of BF₃· ethyl ether complex and 1,000 ppm of hydroquinone. Their adhesive properties are as set forth in Table 1. Example 3 Adhesives were prepared by mixing neopentyl α-cyanoacrylate (NPCA) and allyl α-cyanoacrylate (ACA) as a conventional α-cyanoacrylate in such proportions as shown in Table 2 below and then incorporating therein 20 ppm of BF₃· ethyl ether complex and 1,000 ppm of hydroquinone. Their adhesive properties are as set forth in Table 2. Example 4 Adhesives were prepared by mixing neopentyl α-cyanoacrylate (NPCA) and 2-ethoxyethyl α-cyanoacrylate (EECA) as a conventional α-cyanoacrylate in such proportions as shown in Table 3 below and then incorporating therein 20 ppm of BF₃· ethyl ether complex and 1,000 ppm of hydroquinone. Their adhesive properties are as set forth in Table 3. Comparative Example The adhesive properties of neopentyl α-cyanoacrylate were compared with those of n-amyl α-cyanoacrylate (n-AmCA) and iso-amyl α-cyanoacrylate (i-AmCA). The results are as set forth in Table 4. Testing Method Tensile Shear Strength: Measured at 25°C after aging 24 hours at 43 ± 1°C, 60 ± 2% RH, according to JIS K6861. Hot Tensile Shear Strength: Measureds at 150°C x 1 hr after agint 24 hours at 43 ± 1°C, 60 ± 2% RH, according to JIS K6861. Whitening: A schale which had been made clean was placed on black paper, and each adhesive was dropped one drop into the schale. After standing 24 hours at 43°C, 60% RH, the presence or the state of whitening was checked.

Claims: Neopentyl α-cyanoacrylate having the formula An instantaneous adhesive comprising as an essential component neopentyl α-cyanoacrylate having the formula. An instantaneous adhesive as set forth in claim 2, further containing one or more conventional α-cyanoacrylates An instantaneous adhesive as set forth in Claim 3 wherein said one or more conventional α-cyanoacrylates is a liquid compound at a room temperature. An instantaneous adhesive as set forth in Claim 3-or Claim 4 wherein the amount of the neopentyl α-cyanoacrylate is 5 to 85 wt% based on the weight of adhesive components.

Inventors: CHIKUSA TOSHIYUKI, MIKUNI HIROYUKI, CHIKUSA, TOSHIYUKI, MIKUNI, HIROYUKI
Applicants: THREE BOND CO LTD, THREE BOND CO., LTD.
Application year: 1991
Main classification: C07C255
IPC codes: C07C255, C09J4