One-piece intraocular lenses

Abstract: A material for one-piece intraocular lenses consisting essentially of a copolymer of which main components are methyl methacrylate and at least one (meth)acrylate selected from an alkyl acrylate having a glass transition temperature of higher than 30°C and up to 100°C and a fluoroalkyl (meth)acrylate having a glass transition temperature of higher than 30°C and up to 100°C is disclosed. The material for one-piece intraocular lenses is excellent in cutting-processability, grindability, machinability and suitable flexibility, and can be suitably used for not only one-piece intraocular lenses but also three-piece intraocular lenses.

Description: The present invention relates to one-piece intraocular lenses. Intraocular lenses are composed of a lens body and a haptic. The intraocular lenses are mainly classified into one-piece intraocular lenses of which lens body is formed integrally with a haptic and three-piece intraocular lenses produced by assembling a lens body and a haptic which are manufactured separately from each other. As the material of the one-piece intraocular lens, a hard-type material composed of a hard material such as polymethyl methacrylate, and a soft-type material composed of a soft material such as a silicone rubber not having water-absorptive property or poly(2-hydroxyethyl methacrylate) having water-absorptive property are known. One-piece intraocular lenses composed of a hard-type material such as polymethyl methacrylate have some advantages that are excellent positioning in eyes, stability for visual acuity and biocompatibility and little degradation in human eyes. However, the intraocular lenses have some disadvantages that the lenses cannot be easily inserted into eyes on operation because the haptic has small flexibility, and that the haptic is easily broken during the implantation of the intraocular lens in eyes because its flexural strength is small. Also, one-piece intraocular lenses composed of a soft-type material have some advantages that the one-piece intraocular lenses mechanically little damage the tissues of eyes even though the intraocular lenses are touched to a corneal endothelium or an iris during their insertion in eyes since the intraocular lenses are generally soft. However, their positioning is insufficient since the haptic is soft, and therefore, the intraocular lenses are easily slidden or defected and visual acuity is apt to be unstable. Accordingly, as a one-piece intraocular lens dissolving the above-mentioned defects, an intraocular lens not having water-absorptive property and having suitable flexibility and excellent mechanical strength has been developed (Japanese Unexamined Patent Publication No. 97559/1987 and Japanese Unexamined Patent Publication No. 158949/1989). The intraocular lenses described in the above-mentioned publications surely do not have water-absorptive property and have suitable flexibility and excellent mechanical strength, but it is difficult to polish its material to give an intraocular lens having a desired lens shape by means of conventional polishing methods. Therefore, the improvement of mechanical processability has been expected. EP-A-0 151 762 discloses copolymers having a glass transition temperature of more than 70 °C, consisting of (A) 10 - 25 mol % vinylpyrrolidone and (B) 90 - 75 mol % of cycloalkyl(meth)acrylates and/or alkyl methacrylates, wherein the molar amount of methyl groups in the ester portion is not more than 80 mol % based on the total of methacrylates and wherein the total of (A) + (B) is 100. Such copolymers can be used for ocular lenses. However, this document does not describe fluoroalkyl(meth)acrylates nor crosslinking of the copolymers. EP-A-0 379 146, a document according to Art. 54(3) EPC, discloses a soft ocular lens material made of a copolymer consisting essentially of (A) 5 to 70 parts by weight of a fluorine-containing (meth)acrylate (B) 5 to 60 parts by weight of an alkyl(meth)acrylate, (C) 3 to 45 parts by weight of a specific polysiloxane macromonomer (d) 3 to 40 parts by weight of another specific polysiloxan macromonomer It is an object of the present invention to provide one-piece intraocular lenses having a hard optical portion and a haptic having suitable elasticity. It is another object of the present invention to provide one-piece intraocular lenses having excellent cutting processabity as well as excellent positioning in eyes. These and other objects of the present invention will become apparent from the description hereinafter. In accordance with the present invention, there is provided a one-piece intraocular lens (A) methyl methacrylate (B) a fluoroalkyl (meth)acrylate as defined in claims 1 or 3. The intraocular lens of the present invention has a characteristic in that methyl (meth)acrylate and a fluoroalkyl (meth)acrylate having a glass transition temperature of higher than 30°C and up to 100°C are used as a monomer for a copolymer constituting the material of one-piece intraocular lenses aforementioned above. Since such a monomer is used in the copolymer, the intraocular lenses having a hard optical portion and a haptic having suitable elasticity and giving positioning can be provided although the optical portion and the haptic are made of a single material. Accordingly, since the one-piece intraocular lenses of the present invention have suitable flexibility, an intraocular lens can be easily inserted in eyes in a state that the incision of a bulbus oculi is small. In addition, since the one-piece intraocular lenses of the preset invention have suitable mechanical strength, the lens is excellent in cutting processability, in particular polishing property. The one-piece intraocular lenses of the present invention consists essentially of a copolymer of which main components are methyl methacrylate (hereinafter referred to as MMA), an optionally alkyl (meth)acrylate having a glass transition temperature of higher than 30°C and up to 100°C (hereinafter referred to as alkyl (meth)acrylate, a fluoroalkyl (meth)acrylate having a glass transition temperature of higher than 30°C and up to 100°C (hereinafter referred to as fluoroalkyl (meth)acrylate), and a crosslinking agent. The MMA used in the present invention is excellent in biocompatibility and shows little degradation in human eyes, and also gives excellent dimensional stability. The amount of the above-mentioned MMA is 53 to 95 parts (parts by weight, hereinafter referred to the same), preferably 55 to 95 parts based upon 100 parts of the components for a copolymer. When the amount of the MMA is less than the above-mentioned range, sufficient hardness endurable for mechanical processing, which is carried out when producing an intraocular lens, is not imparted to the material. When the amount of the MMA exceeds the above-mentioned range, although the obtained material possesses desirable hardness for a optical material, there is a tendency that the material does not have elasticity necessary for a haptic. The fluoroalkyl (meth)acrylate used in the present invention is the component for imparting desirable elasticity necessary for a haptic to an obtained one-piece intraocular lenses. In the present invention, the reason why it is necessitated that the glass transition temperature of the above-mentioned fluoroalkyl (meth)acrylate is higher than 30°C and up to 100°C is to obtain one-piece intraocular lenses having suitable flexibility, which can be polished. There is a necessity that the glass transition temperature of an obtained material is 70° to 105°C so that the material can have suitable flexibility and can be polished. Therefore, the transition temperature of the above-mentioned fluoroalkyl (meth)acrylate is preferably at least 40°C, and more preferably from 50° to 95°C. Concrete examples of the above mentioned alkyl (meth)acrylate are, for instance, t-butyl acrylate (glass transition temperature: 43°C), 2-t-butylphenyl acrylate (glass transition temperature: 72°C ), naphthyl acrylate (glass transition temperature: 85°C), 4-methoxyphenyl acrylate (glass transition temperature: 51°C ), 2-methoxycarbonylphenyl acrylate (glass transition temperature: 46°C ), 2-chlorophenyl acrylate (glass transition temperature: 53°C), 4-chlorophenyl acrylate (glass transition temperature: 58°C ), 2-cyanobenzyl acrylate (glass transition temperature: 44°C), 4-cyanophenyl acrylate (glass transition temperature: 90°C ), isobornyl acrylate (glass transition temperature: 94°C ), ethyl methacrylate (glass transition temperature: 65°C ), propyl methacrylate (glass transition temperature: 35°C ), isopropyl methacrylate (glass transition temperature: 81°C ), sec-butyl methacrylate (glass transition temprature: 60°C), isobutyl methacrylate (glass transition temperature: 53°C), cyclohexyl methacrylate (glass transition temperature: 83°C), benzyl methacrylate (glass transition temperature: 54°C), 2-cyanoethyl methacrylate (glass transition temperature: 91°C ), and the like. These alkyl (meth)acrylates are usually used alone or in admixture thereof. Concrete examples of the above-mentioned fluoroalkyl (meth)acrylate are, for instance, trifluoroethyl methacrylate (glass transition temperature: 80°C ), hexafluoroisopropyl methacrylate (glass transition temperature: 95°C), tetrafluoropropyl methacrylate (glass transition temperature: 75°C), octafluoropentyl methacrylate (glass transition temperature: 36°C ), and the like. These fluoroalkyl (meth)acrylates are usually used alone or in admixture thereof. In the present invention, the above-mentioned fluoroalkyl (meth)acrylate is used alone respectively or in admixture thereof. The amount of the above-mentioned fluoroalkyl (meth)acrylate is 5 to 47 parts, preferably 5 to 45 parts based upon 100 parts of the components for a copolymer. When the amount is less than the above-mentioned range, although an obtained material has desirable hardness as an optical material, the material does not have elasticity necessary for a haptic. When the amount exceeds the above-mentioned range, there is a tendency that sufficient hardness endurable for mechanical processing, which is carried out when an intraocular lens having a desirable lens shape is produced, is not imparted to the material. Since the one-piece intraocular lenses of the present invention comprise the above-mentiond components, their glass transition temperature can be maintained between 70° to 105°C. The preferable glass transition temperature is 80° to 105°C. When the glass transition temperature is lower than 70°C, an obtained lens shows rubber-like elasticity in eyes (having a temperature of about 37°C), and therefore, the positioning of a haptic is insufficient and it is difficult to grind the material, and further such a problem that the generation of deformation of a lens is caused when an obtained one-piece intraocular lens is subjected to thermal treatment in a sterilization process after the one-piece intraocular lens is produced. When the glass transition temperature is higher than 105°C, since an obtained lens has a property similar to polymethyl methacrylate (glass transition temperature: 112°C) solely, and suitable flexibility cannot be imparted to the material, it is apt to occur some problems that it is difficult to insert an obtained intraocular lens into eyes, in particular at the portion of a haptic, and that the haptic is easily broken during implantation in eyes. The one-piece intraocular lens of the present invention is prepared by polymerizing components for a copolymer, of which main components are the MMA, an optional alkyl (meth)acrylate, the fluoroalkyl (meth)acrylate, and the crosslinking agent. However, so long as the objects of the present invention are not prevented, other components can be used in the components for a copolymer. In the present invention a crosslinking agent is used. Examples of the above-mentioned crosslinking agent are, for instance, ethyleneglycol dimethacrylate, allyl methacrylate, trimethylolpropane trimethacrylate, divinylbenzeneallyl phthalate, and the like. These are used alone or in admixture thereof. The amount of the above-mentioned crosslinking agent is usually adjusted so that the amount does not exceeds 10 parts based upon 100 parts of the components for a copolymer. When the amount exceeds 10 parts, an obtained one-piece intraocular lens tends to be brittle. In the present invention, a radical polymerization initiator which is usually used in polymerization of unsaturated hydrocarbons can be used in polymerization of the above-mentioned components for a copolymer. Concrete examples of the above-mentioned radical polymerization initiator are, for instance, benzoylperoxide, azobisisobutyronitrile, azobisdimethylvaleronitrile, and the like. These are used alone or in admixture thereof. The amount of the above-mentioned radical polymerization initiator is usually adjusted so that the amount is 0.01 to 1 part or so based upon 100 parts of the components for a copolymer. When the amount is less than 0.01 part, polymerization reaction is too low, and when the amount exceeds 1 part, there is a tendency that bubbles are produced in an obtained material for one-piece intraocular lenses. In the present invention, an ultraviolet absorber, a coloring agent and the like can be furthermore contained in the material as occasion demands. Concrete examples of the above-mentioned ultraviolet absorber are, for instance, benzophenones such as 2-hydroxy-4-methoxybenzophenone and 2-hydroxy-4-octoxybenzophenone; benzotriazoles such as 2-(2'-hydroxy-5'-methylphenyl)benzotriazole and 5-chloro -2(3'- t - butyl - 2'-hydroxy -5'- methylphenyl)benzotriazole; salicylic acid derivatives; hydroxyl acetophenones, and the like. Also, a reactive ultraviolet absorber both having a chemical structure similar to these ultraviolet absorbers and being copolymerizable with the components for a copolymer according to the present invention can be used. These can be used alone or in admixture thereof. To correct the cyanopsia of a patient not having a crystalline lens after implantation of the intraocular lens, it is desirable that the above-mentioned coloring agent has yellow to orange color. Concrete examples of the coloring agent are, for instance, oil-soluble dyes such as CI Solvent Yellow and CI Solvent Orange which are described in Color Index (CI); dispersed dyes such as CI Disperse Yellow, and CI Disperse Orange; vat dyes, and the like. Reactive coloring agents both having a chemical structure similar to these coloring agents and being copolymerizable with the components for a copolymer used in the lens according to the present invention also can be used. These can be usually used alone or in admixture thereof. Each amount of the ultraviolet absorber agent and the coloring agent is usually adjusted so that each amount of them does not exceed 5 parts or so based upon 100 parts of the components for a copolymer. As a method for copolymerizing the components for a copolymer and a molding method for producing a material for one-piece intraocular lenses according to the present invention, conventional copolymerization techniques and molding techniques can be employed. For instance, the above-mentioned components for a copolymer can be copolymerized in a prescribed mold so that an intraocular lens can be easily produced and then an obtained material can be cut and processed to give an intraocular lens having a shape corresponding to an intraocular lens, and the above-mentioned components also can be previously copolymerized and molded in a mold having a shape corresponding to an intraocular lens. The present invention is not limited to the above exemplified copolymerization methods and molding methods. Further, an obtained intraocular lens can be naturally subjected to properly cutting, polishing, and the like. When the above-mentioned components for a copolymer are copolymerized in a mold, as a mold, for instance, a mold made of glass, polyethylene, polypropylene or the like can be used. The thus obtained one-piece intraocular lenses can suitably be, for instance, one-piece intraocular lenses of which the lens body is formed integrally with a haptic The present invention is more specifically described and explained by means of the following Examples. Examples 1 to 7 and Comparative Example 1 The MMA, an alkyl (meth)acrylate, a fluoroalkyl (meth)acrylate, a crosslinking agent and a polymerization initiator were admixed together to give a composition shown in Table 1. The composition was poured into a tubular glass mold having an inside diameter of 15 mm and a depth of 500 mm. The polymerization reaction was carried out in the mold on a water bath having a water temperature of 35°C for 40 hours and then 50°C for 6 hours. After the polymerization reaction was finished, the mold was taken out from the water bath, and placed in an oven After the mold was heated for each 10°C rise in temperature from 50° to 130°C keeping each temperature for 1.5 hours, the mold was allowed to stand to cool to room temperature. A material for one-piece intraocular lenses was taken out from the mold. As the physical properties of the obtained material for one-piece intraocular lenses, refractive index, hardness, mechanical processability, elasticity, appearance and glass transition temperature were examined in accordance with the following methods. The results are shown in Table 1. (Method for measuring the physical properties of the obtained material for one-piece intraocular lenses) (A) Refractive index The obtained material for one-piece intraocular lenses was processed to give a test piece having a diameter of 13 mm and a thickness of 5 The refractive index was measured in accordance with Japanese Industrial Standards (JIS) K-7105. (B) Hardness After the obtained material for one-piece intraocular lenses was processed to give a test piece having a diameter of 13 mm and a thickness of 5 mm, shore hardness D was measured in accordance with the method prescribed in ASTM D-2240. (C) Mechanical processability The obtained material was processed to the shape of a one-piece intraocular lens by means of a computer aided modeling machine. When the material could be processed accurately to a desired shape, it was judged as Good". When the material could not be processed, it was judged as "Not Good". (D) Elasticity One-piece intraocular lenses produced in the above item "(C) mechanical processability" were used. After the optical portion of the lens was gripped in a vise so that the optical portion could not be moved, the end of the haptic of the lens was held by a pincette for operation. The end of the haptic was bended 100 times to the optical portion. After that, the one-piece intraocular lens was observed by means of a magnifier (x10). When no change was observed in comparison with the lens before the test, it was decided as "Good", and when change was observed, it was decided as "Not Good". (E) Appearance The appearance of each obtained materials was observed with naked eyes. (F) Glass transition temperature After the obtained material for one-piece intraocular lenses was processed to give a test piece having a diameter of 4 mm and a thickness of 0.15 mm, the glass transition temperature of the test piece was measured by means of SSC5200 and DSC220C which were commercially available from Seiko Instruments Inc. As the conditions for measuring the glass transition temperature, the range of the temperature was adjusted to room temperature to 150°C, and the temperature gradient was adjusted to 10°C /min. As is clear from the results shown in Table 1, it can be seen that the one-piece intraocular lenses obtained in Examples 1 to 7 of the present invention are excellent in transparency, hardness and mechanical processability as well as conventional intraocular lenses made of polymethyl methacrylate, and have elasticity suitable for a haptic at the same time. The material for one-piece intraocular lenses of the present invention has transparency required for one-piece intraocular lenses, suitable hardness, elasticity and mechanical strength, and are excellent in mechanical processability such as cutting and polishing. Therefore, the material can be suitably used in particular for one-piece intraocular lenses. Also, since the material for one-piece intraocular lenses consists essentially of a copolymer containing the MMA which is said that the polymethyl methacrylate is excellent in biocompatibility and little degradation in human eyes, the material is excellent in biocompatibility and little degradation in human eyes. In addition to the ingredients used in the Examples, other ingredients can be used in the Examples as set forth in the specification to obtain substantially the same results.

Claims: A one-piece intraocular lens made of a copolymer consisting essentially of: (A) methyl methacrylate, (B) a fluoroalkyl (meth)acrylate having a glass transition temperature of higher than 30 °C and up to 100 °C, and (C) a crosslinking agent, wherein a glass transition temperature of said copolymer is 70° to 105 °C. The one-piece intraocular lens of claim 1, wherein said crosslinking agent is a member selected from the group consisting of ethyleneglycol dimethacrylate, allyl methacrylate, trimethylolpropane trimethacrylate and divinylbenzeneallyl phthalate. A one-piece intraocular lens made of a copolymer consisting essentially of: (A) methyl methacrylate (B) an alkyl (meth)acrylate having a glass transition temperature of higher than 30 °C and up to 100 °C, (C) a fluoroalkyl (meth)acrylate having a glass transition temperature of higher than 30 °C and up to 100 °C, and (D) a crosslinking agent, wherein a glass transition temperature of said copolymer is 70 °C to 105 °C. The one-piece intraocular lens of claim 3, wherein said alkyl (meth)acrylate is ethyl methacrylate. The one-piece intraocular lens of claim 3, wherein said crosslinking agent is a member selected from the group consisting of ethyleneglykol dimethacrylate, allyl methacrylate, trimethylolpropane trimethacrylate, and divinylbenzeneallyl phthalate.

Inventors: NAKADA KAZUHIKO, YOSHIDA KUNIHISA, NAKADA, KAZUHIKO, YOSHIDA, KUNIHISA
Applicants: MENICON CO LTD, MENICON CO., LTD.
Application year: 1991
Main classification: G02B1
IPC codes: A61L27, G02B1