Cast product having ceramics as insert and method of making same

Abstract: A cast product made from metallic material and ceramic material with the ceramic material being an insert comprises an aggregated body of capsule particles (74), the capsule particle (74) including a ceramic particle (71) coated with metallic particles (72), and metallic material cast over the aggregated body.

Description: The present invention relates to cast a product having ceramics as an insert such as a cylinder head, a piston and an exhaust manifold which product is repeatedly subjected to high thermal stress and a method of making such a product. Generally, a cylinder head and a cylinder liner which define a combustion chamber of an internal combustion engine are made from casting iron, respectively. Therefore, the combustion chamber is always exposed to a possible breakage due to poor rigidness, which is a characteristic of the casting iron, and due to residual stress at a casting of the cylinder head and the cylinder liner as well as thermal stress and thermal shock exerted on the cylinder head and the cylinder liner during operation of the engine. Particularly, so-called "valve bridge portion" (a portion between an intake port and an exhaust port and a portion between these ports and a precombustion chamber hole or a fuel injection nozzle hole) cannot possess a sufficient size and thickness due to its structure. Thus, the valve bridge portion is structurally weak and crackings may occur in the elements of the valve bridge portion. A conventional measure to overcome the above-described problems as follows: In casting the cylinder head, different metal is inserted to those portions which require high strength as disclosed in Japanese Utility Model Registration Application Second Publication No. 48-25923 and hardening of various degrees is applied to the intermediate product in accordance with thermal stress occurring in the final product during the operation of the engine as disclosed in Japanese Utility Model Registration Application Second Publication No. 63-8831. However, recent engines have very high output and accordingly the thermal stress and mechanical load on the parts around the combustion chamber have increased greatly. Thus, reinforcement of those parts which are subjected to high thermal stress is not enough to eliminate the possibility of cracking. On the other hand, a surface insulation treatment is applied to the parts around the combustion chamber in order to suppress thermal fatigue due to a temperature increase, as one aspect of improving the engine performances. One way of surface insulation is disclosed for instance in Japanese Utility Model Application Laid-Open No. 59-85348. In this application, a part of the cylinder head on the combustion chamber side is formed by ceramic material This prevents cracking and improves a thermal insulation property. Figures 18 and 19 show a cylinder head arrangement in line with the above proposal in a plan view and a sectional view, respectively. As illustrated, a recess portion 5 is formed at a valve bridge portion 4 between an intake port 1 and an exhaust port 2 of a cylinder head. A fuel injection nozzle installation hole 3 is bored in the valve bridge portion 4. The recess portion 5 is filled with ceramic material which forms a ceramic layer 6. However, in a cylinder head made from cast iron, there is no adequate technique to join the cast iron material with the ceramic material. Therefore, the ceramic layer should be applied on the combustion chamber side cylinder head by bolts. The bolting cannot ensure a sufficient joint and consequently the ceramic part, which is a brittle part, may be broken due to vibrations during the engine operation. In another example, a ceramic port liner is inserted in the exhaust manifold in order to raise a turbocharging efficiency by a thermal insulation of internal exhaust gas. In such a structure, the ceramic liner is cast as an insert as the exhaust manifold is cast. This raises a problem that the brittle ceramic part will be broken by thermal expansion difference between the ceramic part and the cast iron part and stress produced upon solidification shrinkage. Even if the cracking does not appear during and after the casting operation. the parts may be broken by vibrations during the engine operation. Another joint technique for the cast iron and the ceramic part has been proposed. An appropriate amount of metallic particles are mixed with ceramic particles and the mixture is sintered. Then, the sintered element is cast as an insert. According to this technique, the metallic particles are metallographically joined with the melt of cast iron. As a result, the ceramics and the cast iron are combined with each other very tightly. The above proposal, however, has following drawbacks: First, if the ceramic particulates and the metallic particulates exist in a segregated state in the product, the thermal strength, the thermal insulation property and a deformation-resistance of the product are lowered and a durability of the product is shortened. In addition, it is very difficult to manufacture the product having the ceramic particulates and the metallic particulates distributed homogeneously. A very strict quality control is required to obtain a homogeneous product. An object of the present invention is to improve a strength and thermal insulation ability of a cast product. Another object of the present invention is to provide a cast product having a ceramic insert whose joint with the cast iron is improved when the ceramic insert of sufficient strength and thermal insulation ability is cast as insert in the cast iron. Still another object of the present invention is to obtain a ceramic product which has no segregation in structure, is suitable for mechanical cutting and has no crackings. Yet another object of the present invention is to obtain a product in which the ceramic particulates and the metallic particulates are homogeneously mixed with each other. The invention is defined in claims 1, 21 and 22. Preferred embodiments are shown in claims 2 - 20 and 23 - 26. According to one aspect of the present invention, there is provided a cast iron product having a ceramic insert, which product comprises a group of capsule particulates of ceramic particulates covered with metallic particulates and metallic material in which the group of capsule particulates is inserted in the casting operation. The group of capsule particulates include capsule particulates of predetermined configuration and the capsule particulates are formed from powder compacts. The group of capsule particulates may be a sintered body made from powder compacts of the capsule particulates. The ceramic particulates are preferably hollow ceramic particulates. A diameter of the ceramic particulate may be approximately between 10 and 500 micrometers. A diameter ratio of the ceramic particulate to the metallic particulate may be about 10 to 1. The ceramic particulate may be Al₂O₃. The ceramic particulates may be volcanic ash sand soil grains. These soil grains may be "Shirasu". "Shirazu" represents layers of volcanic ash and/or pumice stones which can be found in Ohsumi peninsula, Satsuma peninsula and Miyakonojo area of Japan. An accumulation of ejecta from volcanoes in Kagoshima forms "Shirazu". The "Shirazu" may have grain size of 74 micrometers or below for its 40 to 60 weight percent and 74 to 420 micrometers for its 50 to 40 weight percent or 120 micrometers or below as its 30 to 40 weight percent. The metallic particulates may be metal containing iron or stainless material. The metallic particulates may be made from cast iron. The group of particulates are preferably positioned in those portions of the product which are exposed to high thermal stress. The group of particulates may be a sintered body or a compact defining a combustion chamber. The group of particulates may be a sintered body or a compact defining an inner wall of an exhaust manifold of the engine. The inner wall of the exhaust manifold may be the inner wall at the entrance of the exhaust manifold. The group of the particulates may be a sintered body or a compact defining a lower portion of the cylinder head and/or an exhaust port liner. According to another aspect of the present invention, there is provided a method of making the abovementioned product. Specifically, there is provided an improved method of manufacturing a cast iron product having a ceramic member as an insert, comprising the steps of: forming capsule particulates by covering ceramic core particulates with metallic coating particulates, each core particulate being covered with a plurality of coating particles; forming a powder compact of predetermined configuration using the capsule particulates; and casting metallic material such as cast iron over the powder compact and simultaneously sintering the powder compact. According to still another aspect of the present invention, there is provided a method of manufacturing a cast iron product having a ceramic insert, comprising the steps of: forming capsule particles by coating ceramic core particles with metallic coating particles, each core particle being covered with a plurality of coating particles; forming a powder compact of predetermined shape using the capsule particles; forming a sintered body by sintering the powder compact; and casting metallic material much as cast iron over the sintered body to form a ceramics-inserted cast product. The capsule-particle-forming step may include the steps of: forming a powder body to be treated (an intermediate product), by allowing a number of metallic particles to adhere on a surface of a ceramic particle whose diameter is larger than the diameter of the metallic particle; and applying shock or impulsive effect of high speed air flow on the powder body to admit the metallic particles to bite or intrude into the ceramic particles so as to form a capsule particle. The capsule-particle-forming step may be performed by a powder shock applying machine or a rolling machine. The powder-compact-forming step may be a step of pressure-compacting powders of capsule particles. The sintering step may include a sintering operation at a temperature between about 900 °C and about 1,000 °C. According to the present invention, the ceramic elements are added to the product in a desired condition so that the strength and the heat insulation property of the product are improved. In addition, the surface of the powder compact or the sintered body substantially become metallic so that the joint with the cast iron becomes easier or casting of the cast iron over the powder compact or the sintered body becomes easier. Furthermore, the ceramic elements are uniformly distributed in the final product so that the possibility of cracking is eliminated. Moreover, the metallic particles make the machining or the mechanical cutting easier. Particularly, if the ceramic particles have hollow portions to contain air therein, the thermal insulation is further improved by layers of air. Also, if volcanic ash sand soil grains such as "Shirasu" are used as the hollow ceramic particles, a ceramic element manufacturing cost is reduced. Van der Waals forces are used to force the metallic particles to adhere on the surface of the ceramic particle. However, the adhesion between dissimilar particles is not always enough at this point. Therefore, in order to form the capsule powder, the impulsive forces of the high speed air is applied to the surface, which is formed by a number of metallic particles adhering on the ceramic core, of the ceramic core such that the metallic particles intrude into the ceramic core. This provides a strong joint between the dissimilar particles. Specifically, individual ceramic particles are covered with or enclosed by the metallic particles with strong joint force. Therefore, making the powder compact from these capsule powders means the ceramic particles and the metallic particles being homogeneously mixed with each other in the powder compact. At the next step, the compact of capsule powders are sintered to obtain a sintered body. Then, the cast iron is cast over the sintered body. Alternatively, the compact is sintered and at the same time, the cast iron is cast over the compact. At the step of sintering the compact and the step of casting the cast iron over the compact or the sintered body, the metallic particles covering the ceramic particles and the other metallic particles are metallurgically joined with each other, and the combined metal and the cast iron are metallurgically joined with each other, so that the metallic cast product contains the ceramic particles as the insert. This means that the compact of capsule powders and the cast iron are firmly joined with each other. Therefore, the heat resistance, the thermal insulation property and the deformation resistance of the final product are improved. Figure 1 is a perspective view showing a piston head of an embodiment of the present invention; Figure 2 is a perspective view showing a combustion chamber lateral wall of the piston head of Figure 1; Figure 3 is a perspective view of an exhaust manifold according to a second embodiment of the present invention; Figure 4 is a view taken along the line A-A of Figure 3; Figure 5 is a sectional view of major portions of a cylinder head according to a third embodiment of the present invention; Figure 6 is a perspective view of an exhaust port liner of Figure 5; Figure 7 shows a fourth embodiment of the present invention with a section view illustrating a step of metallic particle adhesion on ceramic particle surface; Figure 8 shows a sectional view of a capsule particle; Figure 9 shows a powder impacting machine used to carry out a method of making a cast product having ceramic particles as insert; Figure 10 is a view useful to explain a fifth embodiment of the present invention, showing a sectional view of a particle of a hollow ceramic particle and metallic particles adhering on the ceramic particle; Figure 11 is a sectional view of a capsule particle; Figure 12 depicts a system for manufacturing the capsule particles; Figure 13 depicts a sectional view of a rolling machine of the system of Figure 12; Figure 14 depicts a sintered body of the capsule particles; Figure 15 is a partial sectional view of a piston which is a cast product having a ceramics as an insert according to the fifth embodiment; Figure 16 is an enlarged view of "B" section of Figure 15; Figure 17 schematically illustrates volcanic ash sand soil grains "Shirasu" which are used as hollow ceramic particles; Figure 18 is a plan view of a cylinder head of a conventional arrangement; and Figure 19 is a sectional view taken along the line C-C of Figure 18. Now, preferred embodiments of the present invention will be explained. Figures 1 and 2 illustrate a cast iron piston 11 having ceramic particles as insert according to a first embodiment of the present invention. In a piston head 12 of the piston 11, a powder compact or sintered body 13 made from capsule particles is cast as the insert. The powder compact or sintered body 13 includes ceramic particles (cores) and metallic particles (coating or covering particles) surrounding the ceramic particles. Each ceramic particle (core) are enclosed by a plurality of metallic particles (coating particles). A combustion chamber 14 is defined by the powder compact 13. In other words, a wall 15 of the combustion chamber 14 is formed by homogeneously distributed, firmly added ceramic particles. This piston 11 is exposed to high temperature combustion gas and thermal stress repeatedly, but crackings do not appear in the combustion chamber wall of the cast iron piston since the piston 11 has the above construction. Figures 3 and 4 show a second embodiment of the present invention. Numeral 21 designates an cast iron exhaust manifold having ceramic particles as the insert. A powder compact (sintered body) 23 made from the capsule particles are cast in an inner wall of the exhaust manifold. An inner wall 24 of the powder compact 23 defines an exhaust gas passage 25. A casting location of the powder compact 23 may be in a connecting portion 26 between the exhaust manifold 21 and a cylinder head (not shown) or may be an entire inner wall of the exhaust manifold 21. Figures 5 and 6 show a third embodiment of the present invention. In a lower portion 32 (a valve bridge portion) of a cast iron cylinder head 31 and an exhaust port liner 33 of the cylinder head 31, powder compacts (sintered bodies) 34 and 35 made from the above-described capsule particles are cast as the insert. Since the lower portion 32 of the cylinder head and the exhaust port liner 33 include the powder compacts 34 and 35 respectively, the heat resistance, the thermal insulation ability and the deformation resistance of these elements are improved. In addition, crackings do not appear in these elements even if these elements are subjected to the thermal stress repeatedly. Now, a method of making the cast iron product having a ceramic element as the insert, as mentioned in the first to the third embodiments, will be explained as a fourth embodiment of the present invention. Major steps of the method are: forming capsule particles; forming a powder compact from the capsule particles; and performing a casting with the powder compact as an insert. The capsule particle forming steps may be carried out by a fine-particle shock-applying machine and peripheral equipments thereof (Figure 9) and the shock-applying machine will be explained. As illustrated, a disk 44 is mounted on a shaft 43 rotatably supported by a casing 42 and a plurality of shock-applying pins 45 are provided on the outer periphery of the disk 44 at predetermined intervals and extend in the radial direction of the disk 44. The disk 44 is adapted to rotate at a high speed. A collision or impact ring 46 is provided around the disk 44 with a predetermined clearance. The impact ring 46 is mounted on the inner wall of the casing 42. The impact ring 46 is cut out at a lower portion 47 thereof and a valve 48 is provided at the cut out portion 47 of the ring 46. The valve 48 is connected to a valve stem 50 which serves as a rod of the actuator 49 and a up-and-down movement of the valve stem 50 opens and closes the cut out 47. A clearance between the outer periphery of the disk 44 and the impact ring 46 defines an impact chamber 51 for applying a shock or an impulsive force to the fine particles. The impact chamber 51 has a circulation opening 52 and a circulation passage 53 extends from the opening 52 to a central portion of the disk 44. The fine particles are fed into the chamber 51 through a feed chute 55 connecting the passage 53 with a hopper 54. A predetermined impulsive force is applied to the fine particles and the fine particles are discharged from a discharge chute 56 as the valve 48 moves. The peripheral equipments of the impact machine 41 include a raw material weighing feeder 57 which transfers the fine particles to the raw material hopper 54, a raw material storage 58 provided upstream of the feeder 57 and a preprocessor 59 for feeding the fine particles to the storage 58. Other peripheral equipments are a cyclone 60 for receiving the fine particles discharged from the impact chamber 51, a rotary valve 61 provided for the cyclone 60, a bag filter 63 having another rotary valve 62, a blower 64 and a controller 65 for controlling the raw material weighing feeder 57, the disk 44 and the actuator 49. Next, a process of making the capsule particles will be explained. As Illustrated in Figure 7, ceramic particles 71 of 10-500 micrometer (in diameter) are prepared. These ceramic particles 71 may be fine particles of Al₂O₃. in addition, metallic particles 72 having smaller diameter than the ceramic particle, for example one-tenth of the ceramic particle, are prepared. The metallic particles may be iron metallic particles. The metallic particles 72 are applied on the surface of the ceramic particle 71 such that the metallic particles 72 adhere thereon. The adhesion is carried out by the preprocessor 59 with use of van der Waals forces. Each particle 73 has the alumina particle 71 and the metallic particles 72 around the alumina particle 71. The particles 73 are fed from the preprocessor 59 to the raw material storage 58. At that time, the valve 48 of the impact machine 41 is closed, and inert gas is fed into the machine 41 while the shaft 44 is rotated. The rotational speed of the disk 44 is adjusted between 8,000 to 16,00 rpm by the controller 65. The rotation of the disk 44 rotates the pin 45 mounted on the outer periphery of the disk 44 and produces air flow therearound. A fan effect due to a centrifugal force of the air flow forms a circulation flow extending from the opening 52 of the chamber 51 to the central portion of the disk 44 through the passage 53. After the circulation flow is formed, the treated fine particles. 73 in the storage 58 are thrown into the hopper 54 by the feeder 57. The fine particles 74 enter the impact chamber 51 from the raw material hopper 54 through the chute 55. In the chamber 51, a number of pins 45 of the disk 44 which rotates at a high speed, apply instantaneous shock to the fine particles 73. Then, the fine particles 73 collide against the ring 46 such that a second shock and a strong compressing force are applied to the fine particles 73. After that, the fine particles 73 flow into the circulation passage 53 with the circulating gas flow and reach the chamber 51 again, as indicated by the arrow "a". Then, the fine particles 73 are exposed to the shock again. Therefore, the fine particles 73 face the impulsive force repeatedly within a short period of time. The time required may be about 1 to 10 minutes. During that period of time, the surface of the ceramic particle 71 is given thermal energy so that the metallic particles 72 or the ceramic particle 71 is softened or melt within a short period of time, whereby the metallic particles 72 are distributed homogeneously on the surface of the ceramic particle 71. In other words, the ceramic particle 71 is covered with the metallic particles 72 whereby the coated capsule particle (powder body) 74 which has the ceramic particle 71 as the core and the metallic particles 72 around the ceramic particle 71 is manufactured. After the capsule particle 74 is prepared, the valve 48 is moved to a position indicated by the double-dot line of Figure 9 so that the cut out portion 47 is opened to discharge the capsule particles 74 from the chamber 51. The centrifugal force exerted on the capsule particles 74 and a suction force of the blower 64 discharge the capsule particles 74 from the chamber 51 and the circulation passage 53 within a short period of time (several seconds) , as shown in Figure 8. Then, the capsule particles 74 are introduced to the fine particle collecting mechanism (the cyclone 60 and the gas filter 63) through the discharge chute 56. The capsule particles 74 are expelled outside by the rotary valves 61 and 62. Next, the capsule particles 74 are pressurized and shaped to predetermined configurations. In other words, as shown in Figures 2, 4 or 6, there are formed the powder compact 13 defining the combustion chamber 14 of the piston head 12, the powder compact 24 defining the exhaust gas passage 25 of the exhaust manifold 21 and the powder compact 34 defining the port liner 33 of the cylinder head 31. The powder compacts 13, 24 and 34 are located in respective casting molds (not shown) and metallic melt (iron) are added into the casting molds whereby the desired piston 11, the exhaust manifold 21 and the cylinder head 31 are cast. Therefore, the powder compacts 13, 24 and 34 are sintered by the high temperature molten metal and at the same time, the powder compacts become the inserts of the respective cast products. Alternatively, the powder compacts 13, 24 and 34 may undergo the sintering, like a normal sintering of the metal, by a sintering furnace at a sintering temperature of the metal. The final products obtained are shown in Figures 1 to 6. Since the capsule particles 74 are used, the individual ceramic particles 71 are covered with the metallic particles 72 with strong bonding force. Therefore, there are obtained products having the ceramic particles 71 and the metallic particles 72, both particles being distributed homogeneously in the product, without strict quality control. The product has an excellent thermal resistance, a thermal insulation property and a deformation resistance. In addition, in the product which has the ceramic particles as the inserts, the ceramic particles 71 and the metallic particles 72 covering the ceramic particles 71 are metallurgically combined with each other. Further, when the casting of the cast iron is performed with the powder compacts 13, 24 and 34 as the inserts, the metallic particles around the ceramic particles are metallurgically combined with the cast iron. Therefore, the problem of the brittleness of the ceramics are eliminated. Consequently, the thermal resistance, the thermal insulation and the deformation resistance of the product is improved and the strength and the longevity of the product is also improved. In this way, the manufacturing method of the present invention eliminates all the problems of the conventional cast iron product having the ceramics as the insert. The method of the present invention widens the field of use of the ceramic products remarkably. In the powder compact or the sintered body, since the ceramics is coated with the metal, stress which would be produced upon thermal expansion and solidification shrinkage with respect to the casting base metal. As a result, the castability is improved and the crackings do not appear. In addition, the mechanical cutting of the product becomes as easy as the metal itself. A ratio of the metallic portion to the ceramic portion is 30 to 70 at maximum and the metallic portion may be reduced relative to the ceramic portion. Therefore, if it is desired to further improve the thermal resistance, the thermal insulation ability and the deformation resistance, the metallic portion (metallic particles) will be reduced. On the other hand, if the product is often subjected to vibrations and shocks, the metallic portion is increased in order to reduce the brittleness of the ceramics. The present invention may be applied to products other than those illustrated in Figures 1 to 6. Next, a fifth embodiment of the present invention will be described with Figures 10 to 17. In this particular embodiment, the ceramic particle 82 having a hollow portion 81 is employed, as shown in Figures 10 and 11. Like the forth embodiment, the ceramic particle 82 is coated with the metallic particles 83. The metallic particle 83 has a smaller diameter than the ceramic particle 82, for example one-tenth of the ceramic particle. The metallic particles 83 are forced to adhere on the ceramic particle 82 and the impulsive force is applied to them such that the metallic particles 83 firmly adhere on the ceramic particle 82. In this manner, there is obtained the capsule particle 86 which has the hollow ceramic particle 82 as the core particle 84 and the metallic particles 83 as the coating particles 85, as shown in Figure 11. The capsule particle 86 may be manufactured by the system of Figure 9, but here another system is employed and illustrated in Figures 12 and 13. The system is used to manufacture the capsule particles in a dry manner. The system includes an electrostatic device 91, a feeding apparatus 92, a rolling device (hybridizer) 93 and a powder body collecting device 94. The electrostatic device 91 is used to force small particles to adhere a base particle. The small particle has a diameter smaller than the base particle. The feeding machine 92 is used to transfer the base particles having the smaller particles thereon. The rolling machine 93 is used to apply the shock or the impulsive force to the particles. The collecting machine 94 is used to receive the manufactured capsule particles. These devices 91, 92 and 93 are controlled by a controller 95. As shown in Figure 13, a rotor 98 is rotatably provided in the rolling machine 93. The rotor 98 includes a stator 96 and he stator 96 has blades 97. The particles to be treated, fed from a chute 98 are blown off or scattered by the centrifugal force of the roller 98, as indicated by the broken line "b". During this process, the particles impinge on the inner wall of the stator 96 and the blades 97 so that the impulsive force is applied to the particles, and the particles are repeatedly thrown into the high speed air flow by the circulation passage 100. Then, when a discharge valve 101 of the stator 96 is opened, the capsule particles are discharged from an outlet port 102. The hollow ceramic particles 82 and the metallic particles 83 adhering on the ceramic particles are thrown into the rolling machine 93 and the impulsive force is applied to the particles by the high speed air flow for about 1 to 10 minutes. The rotational speed of the rotor 98 is between 8,000 and 16,000 rpm. The product 86 is the capsule particle whose elements are joined with each other firmly. The method of making the capsule particle 86 is not limited to the above-described method, but may be a known wet method. Next, the fine particles (a number of the capsule particles 86) are shaped to a predetermined configuration, like the normal sintering of the metal, and then sintered by the sintering furnace at the sintering temperature of the metal. The resulting product is the sintered body 87 of Figure 14. In other words, there is obtained an aggregated body of the hollow ceramic particles 82 and the metallic particles (coating particles) 85. The surface of the sintered body 87 is coated with the metal . This is the same situation as that the plating is applied to the ceramics. The sintered body 87 and the cast iron are cast with the sintered body 87 being the insert, like the fourth embodiment, and the cast product having the ceramics as the insert is obtained. In this manner, since the sintered body 87 is formed by the capsule particles 86 which have the hollow ceramic particles 82 as the insert, the cast product having the sintered body 87 as the insert has a further improved thermal insulation ability. Specifically, since the core particles are the hollow particles, the air layers in the hollow portions further improve the thermal insulation ability. Stainless fine particles (SUS 304) may be used as the coating particles 85 for the capsule particles 86. In such a case, the sintering temperature is between about 900 and about 1,000 °C. The fifth embodiment may be used in the same field as the fourth embodiment. For example, the fifth embodiment may be used as the thermal insulation element of the top of the piston (cast iron), as shown in Figure 16. In other words, the sintered body 111 having a shape of combustion chamber at the piston top is made from the capsule particles 86. The sintered body 111 is placed in the casting mold (not shown) for casting the piston body 112 and the molten metal is poured thereinto. At this time, the molten metal reacts with the metal (coated particles 85) in the surface of the sintered body 111 and joined with the surface of the sintered body 111, as shown in Figure 16. Thus, the cast iron 113 is cast over the sintered body or the sintered body becomes the insert of the cast iron product. The sintered body 111 is coated with the metal in terms of particle-level so that the metallic coating layer serves as a stress absorber when the cast iron is solidified. In addition, the thermal expansion of the product is similar to the cast iron (13 x 10⁻⁶ 1/°C) so that there is no possibility of crackings due to the thermal expansion. The hollow ceramic particles may be porous volcanic ash sand soil grains which exist in nature. For example, soil grains 121 ("Shirasu") of Figure 17 may be used. "Shirasu" can be found in Kyushu area of Japan and contain porous pumices and volcanic glasses as its major components The grain size of so-called "fine Shirasu" is below 74 micrometers for 40 to 60 % thereof (weight percent) and between 74 to 420 micrometers for 50 to 40 %. The grain size of so-called "coarse Shirasu" is 120 micrometers for 30 to 40 % of its weight. By using Shirasu, the process of preparing the hollow ceramic particles can be omitted and the manufacturing cost is reduced.

Claims: A cast product made from metallic material and ceramic material with the ceramic material being an insert, characterized in that the cast product comprises: an aggregated body of capsule particles (74), the capsule particle (74) including a ceramic particle (71) coated with metallic particles (72); and metallic material cast over the aggregated body. The cast product of claim 1, characterized in that the aggregated body includes a powder compact which is formed by the capsule particle (74). The cast product of claim 1, characterized in that the aggregated body includes a sintered body which is formed by sintering a powder body of the capsule particle (74). The cast product of claim 1, 2 or 3, characterized in that the ceramic particle (71) is a ceramic particle (82) having a hollow section (81). The cast product of claim 1, 2, 3 or 4, characterized in that a grain size of the ceramic particle (71, 82) is between about 10 to about 500 micrometers. The cast product of any one of foregoing claims, characterized in that a ratio of a grain diameter of the ceramic particle (71, 82) to a grain diameter of the metallic particle (72, 83) is approximately 10 to 1. The cast product of any one of foregoing claims, characterized in that a component ratio of the ceramic particles (71, 82) to the metallic particles (72, 83) is 70 to 30 or less metallic particles are contained. The cast product of any one of foregoing claims, characterized in that the ceramic particles (71, 82) include Al₂O₃. The cast product of any one of claims 1 to 7, characterized in that the ceramic particles (82) include porous volcanic ash sand soil grains. The cast product of claim 9, characterized in that the volcanic ash sand soil grains include "Shirasu" (121). The cast product of claim 10, characterized in that the "Shirasu" (121) includes grains below 74 micrometers in grain size for 40 to 60 % of its weight and grains between 74 to 420 micrometers for 50 to 40 %. The cast product of claim 10, characterized in that the "Shirasu" (121) includes grains below 120 micrometers in grain size for 30 to 40 % of its weight. The cast product of any one of foregoing claims, characterized in that the metallic particles (72, 83) include iron metal. The cast product of any one of claims 1 to 12, characterized in that the metallic particles (72, 83) include stainless steel. The cast product of any one of foregoing claims, characterized in that the metallic material includes cast iron. The cast product of any one of foregoing claims, characterized in that the aggregated body is formed in that part of the product which is exposed to high thermal stress. The cast product of any one of claims 1 to 15, characterized in that the aggregated body includes a compact or a sintered body (13) which defines a combustion chamber (14) formed in a piston head (12). The cast product of any one of claims 1 to 15, characterized in that the aggregated body includes a compact or a sintered body (24) which defines an inner wall (23) of an exhaust manifold (21). The cast product of claim 18, characterized in that the inner wall (23) is an inner wall (23) at an entrance (26) of the exhaust manifold (21) . The cast product of any one of claims 1 to 15, characterized in that the aggregated body is a compact or a sintered body (34, 35) to define a lower portion (32) of a cylinder head (31) and/or an exhaust port liner (33). A method of making a cast product using a metallic material and a ceramic material with the ceramic material being the insert, characterized in that the method comprises the steps of: (A) coating a ceramic particle (71) with metallic particles (72) to form a capsule particle (73); (B) forming a powder compact of predetermined shape from the capsule particles (73); and (C) casting the metallic material over the powder compact and simultaneously sintering the powder compact. A method of making a cast product using a metallic material and a ceramic material with the ceramic material being the insert, characterized in that the method comprises the steps of: (A) coating a ceramic particle (71) with metallic particles (72) to form a capsule particle (73); (B) forming a powder compact of predetermined shape from the capsule particles (73); (C) sintering the powder compact to form a sintered body; and (D) casting the metallic material over the sintered body to form the cast product. The method of claim 21 or 22, characterized in that the capsule particle forming step includes the steps of: (D; E) forcing a number of metallic particles on a surface of the ceramic particle such that the metallic particles adhere on the ceramic particle, a diameter of the metallic particle being smaller than that of the ceramic particle so as to form an intermediate product; and (E; F) applying impulsive or shock effect due to high speed air flow, to the intermediate product such that the metallic particles bite or intrude in the ceramic particle to obtain the capsule particle. The method of claim 23, characterized in that the capsule particle (74) forming step is carried out by a fine-particle shock-applying machine (41) or a rolling machine (93). The method of any one of foregoing claims, characterized in that the powder compact forming step includes pressurizing and shaping the capsule particle (74). The method of any one of claims 22 to 25, characterized in that the sintered body forming step includes a sintering at temperature between about 900 and about 1,000 °C.

Inventors: KAMIMURA TADASHI, TSUJIMURA AKIRA, KAMIMURA, TADASHI, TSUJIMURA, AKIRA
Applicants: ISUZU MOTORS LTD, ISUZU MOTORS LIMITED
Application year: 1991
Main classification: B22D19
IPC codes: C22C1, B22D19, F02F1, B22F1