Reinforced thermoplastic composites

Abstract: Reinforced thermoplastic composites comprising a linear alternating polymer of at least one olefinically unsaturated compound and carbon monoxide, and a glass fibre reinforcement having a coating of a sizing material which comprises both aminosilane and uncured epoxy resin functionalities, may be prepared by mixing the components, and converting the resultant mixture by applying heat and/or pressure.

Description: The present invention relates to a reinforced thermoplastic composite and to a process for its preparation. More in particular the invention relates to such a composite based on linear alternating polyketone polymers reinforced with inorganic fibrous materials. Polymers of carbon monoxide and olefinically unsaturated organic compounds, or polyketones, have been known and available in limited quantities for many years. For example, polymers of ethylene or ethylene-propylene which contain small quantities of carbon monoxide are disclosed in U.S. Patent 2,495,286, prepared using free radical catalysts. British Patent 1,081,304 discloses polymers containing higher concentrations of carbon monoxide prepared using alkylphosphine complexes of palladium salts as catalysts. A special class of linear polyketones is disclosed in U.S. 3,694,412, wherein the monomer units of carbon monoxide and olefinically unsaturated hydrocarbons occur in alternating order. Polyketones are of considerable interest because they exhibit good physical properties. In particular, the high molecular weight linear alternating polymers have potential use as engineering thermoplastics due to their high strength, rigidity and impact resistance. These polymers consist of repeating units of general formula which units may be the same or different and wherein A is the moiety obtained by polymerisation of the olefinically unsaturated organic compound through the olefinic unsaturation. Although the properties of the polyketones are suitable for many applications, it would be of advantage to provide polyketone composites which exhibit less mould shrinkage and certain mechanical properties that are improved over the corresponding properties of the polymer alone. It was recently found by the Applicant that a method to improve the performance of such polyketone composites is to incorporate reinforcing materials into the polyketone polymer matrix and especially inorganic fibrous reinforcements. Thus EP-A-322959 describes a reinforced thermoplastic composite comprising a linear alternating polymer of at least one olefinically unsaturated compound and carbon monoxide, and a glass fibre reinforcement. Herein it is mentioned too that glass fibres that are to be used as a reinforcement in plastics, customarily have a coating of a sizing material, also known as a coupling agent. The chemical structure and the manner of deposition of such a sizing material on the glass fibres often is a manufacturer's secret; and most end users have grown accustomed to referring to the code name of the fibre manufacturer rather than to a chemical formula. Nevertheless a number of different chemical compounds are mentioned as suitable sizings in EP-A-322959, e.g. water emulsions of starch and lubricating oil, aqueous dispersions of surface active materials and lubricants, silicon-containing materials such as vinyl silanes, alkyltrimethoxysilanes, aminosilanes, trimethoxysilanes which may also contain urethane, acrylate or epoxy functionalities, and non-polar hydrocarbons. For use in glass fibre based composites, a preference is expressed for polar sizings having a trimethoxysilane end group attached to a hydrocarbon chain with a terminal urethane functionality, for instance the sizing used in the fibres sold by Owens Corning under the code name 492 AA. Whereas the mechanical properties of such composites are quite satisfactory, they could still be improved. Another problem, up to now not recognised, is that certain sizings, by their reactivity with the polymer molecules, cause cross-linking between different polymer molecules. This phenomenon does not occur in polymers like polyethylene or polypropylene, which lack any reactive (carbonyl) groups. If the suitability of a certain fibre-sizing combination for use in polyketone based composites is judged solely on the basis of impact strength and similar mechanical tests, as is customary for conventional polymers, the cross-linked polymer composites will appear very attractive, because of their high scores in such tests. However, as soon as such glass fibre reinforced composites have to be processed, e.g. extruded, from the melt, it is found that their melt viscosity is so high that they are practically unprocessable. This phenomenon of cross-linking was found to occur inter alia with the polar sizing recommended in EP-A-322959, and has now been found to occur with many other sizings. It is an object of the present invention therefore to provide composites as defined hereinbefore, which possess both good mechanical properties and a good melt stability. More specifically, it is an object to provide composites having a low cross-linking tendency, which in turn is reflected by a stable melt flow rate and a stable "cross-over-time" (time available before polymer cross-linking makes processing impossible, cf. H.H. Winter, Polymer Engineering and Science, Vol. 27(22), 1987, p. 1698). As a result of continuing research and experimentation, it was now surprisingly found that the mechanical strength and the melt stability of composites based on glass fibres and polyketones is considerably improved when the fibres have been provided with a sizing having aminosilane and uncured epoxy resin functionalities. Accordingly, the invention relates to a reinforced thermoplastic composite characterised by comprising a linear alternating polymer of at least one olefinically unsaturated compound and carbon monoxide, and a glass fibre reinforcement having a coating of a sizing material, wherein the sizing material comprises both aminosilane and uncured epoxy resin functionalities. The glass fibre reinforcement may conveniently be selected from the group comprising woven and non-woven fibrous reinforcements. Suitable non-woven fibrous reinforcements include continuous and chopped fibres. The precise nature of the sizing agents employed in the reinforced composites of the invention is somewhat uncertain. It is considered likely that the size contains a chain up to 3 methylene groups with a silane functionality (-SiH 3 ) on one end and an epoxy functionality on the other. The silane functionality comprises a mono-, di- or triaminosilane group, or mixtures thereof. The triaminosilane group or mixtures having a high proportion of triaminosilane groups are preferred. The epoxy group is uncured, i.e. not (substantially) cross-linked to its neighbours. In any event, the sizing agents usefully employed in the reinforced polymers are characterised by a combination of aminosilane and uncured epoxy functionality. This combination serves to distinguish the sizing agents of the invention from other related sizing agents. A particularly suitable sizing comprises the surface coating provided on "Owens Corning 429 YZ™ glass fibres. The term "glass" is employed in the conventional meaning to indicate that class of complex metal silicates which are commonly referred to as glasses. Although the addition of rare earth metal oxides or transition metal oxides to other metal silicates on occasion will produce a glass of rather exotic properties, the glass from which the glass fibre of the invention is preferably produced is the more common alkali metal silicate glass, particularly a sodium silicate glass. Fibres produced of such glass are conventional and are commercially available from a number of glass companies. The fibres are useful as reinforcements for polymeric products and are commercially used as such. However, the physical dimensions of the glass fibres are of some importance to successful utilisation in a particular application. In the polyketone/glass fibre compositions of the invention, the glass fibres which contribute the most desirable properties to the composition are chopped glass fibres of circular cross-section. The fibres range preferably in diameter from about 5 µm to about 20 µm micron, more preferably from 10 to 18 µm. Fibres of greater or lesser diameter are satisfactory but fibres of too small a diameter do not provide the desired strength and fibres of too large a diameter contribute too much weight for the resulting strength and may not be economical. Although in some applications the long continuous fibres of glass are satisfactory, in the composites of the invention it is preferred to use short fibres of glass. Lengths of glass fibre from about 2.5 to about 12.5 mm are suitable. While somewhat longer or somewhat shorter lengths are also useful, too long a glass fibre detracts from the processability of the composition while too short a fibre does not provide the desired strength. It is recognised that the actual length of the glass fibres in the composition will depend to some extent upon the method of blending or mixing the components, as this may mechanically break down the length of the glass fibres. More important than fibre diameter or fibre length, however, is the fibre aspect ratio, the ratio of fibre length to diameter. The higher the aspect ratio the better the reinforcing effect. Aspect ratios of above 40 are very suitable. The present invention also relates to a process for the preparation of a reinforced thermoplastic composite, comprising mixing a linear alternating polymer of at least one olefinically unsaturated compound and carbon monoxide and a glass fibre reinforcement having a coating of a sizing material, and converting the mixture to a reinforced composite by application of heat and/or pressure, wherein the sizing material comprises both aminosilane and uncured epoxy resin functionalities. Generally the method employed for the preparation of such reinforced polyketone composites is not critical as long as it provides an intimate mixture of polymer and reinforcement. In one method the solution process which is the subject of EP-A-322959 may be used. Alternatively, the components are contacted in e.g. an extruder or an internal mixer at elevated temperature. This method however, has some limitations in that it is often only possible to employ short inorganic fibres, i.e. chopped fibres, or fibre breakage may occur, while furthermore there often is a limit to the amount of fibres which can be incorporated, in view of viscosity constraints. Obviously the viscosity of such a polymer/fibre mixture may be reduced by raising the temperature, but too high a temperature may result in an unacceptable degree of polymer degradation. Very suitably the preparation is effected by feeding the polymer at an elevated temperature in an extruder onto which a second extruder is mounted near the exit which adds the glass fibres to the polymer melt in the first extruder in a controlled fashion. The thermoplastic polymers which may be employed in the reinforced composites according to the present invention may be true copolymers of carbon monoxide and one particular olefinic compound such as an alkene of up to 12 carbon atoms, preferably ethene or an aryl substituted alkene, preferably styrene, or they can be copolymers of carbon monoxide and more than one olefin e.g. ethene and propene. In the latter case ethene is preferably employed as the main olefin. The relevant alternating copolymers are known per se, for example from EP-A-121965, EP-A-213671, EP-A-229408 and US-A-3914391, likewise, their methods of preparation by catalytic copolymerisation are known from these references. Suitable polymerisation catalysts are based upon palladium/phosphine systems. Particularly suitable thermoplastic polymers to be employed in the composites of this invention are copolymers of ethene and carbon monoxide, terpolymers of ethene, propene and carbon monoxide, preferably those in which the ethylene to propylene molar ratio in the polymer chains is at least 3:1. Other terpolymers are terpolymers of ethylene and carbon monoxide with butene, pentene, hexene, heptene, octene, nonene, decene, dodecene, styrene, methyl acrylate, methyl methacrylate, vinyl acetate, undecenoic acid, undecenol, 6-chlorohexene, N-vinylpyrrolidone and the diethylester of vinyl-phosphonic acid, provided the molar ratio of ethylene to other unsaturated monomer in the polymer macromolecules is at least 3:1, preferably at least 8:1. Especially preferred are thermoplastic polymers as described hereinbefore having a molecular weight which corresponds with a Limiting Viscosity Number at 60 °C (LVN 60) between 1 and 2 dl/g. The reinforcement content of the reinforced thermoplastic composites according to the present invention may vary widely e.g. from as low as 1 to as high as 90%v, but will generable be in the range from 5 to 60%v. On a mass basis, the reinforcement content may suitably be between about 1 and 45%, based on total composition, preferably between 5 and 35%. Said reinforcement content will be determined by the method of preparation as well as by the end use. The composites of the invention may also include conventional additives such as stabilisers, antioxidants, mould release agents, fire retardant materials and processing aids which are designed to improve the processability of the components or reinforced polymer or to improve the properties thereof. Such additives are added together with, prior to, or subsequent to, the mixing of the sized glass fibres and polymer. A particular useful processing aid for non-reinforced polyketone comprises a polymer containing moieties of an α-olefin and an α,β-ethylenically unsaturated carboxylic acid which optionally has been partially neutralised with metal ions. Illustrative of these polymers are the copolymers of ethylene and acrylic acid or methacrylic acid which are commercially available or the class of zinc or calcium partially neutralised corresponding polymers known as ionomers. Such materials are commercially available. A disadvantage of such processing aids, when used with non-reinforced polyketones, is a loss of mechanical strength and melt stability, but when used with polyketones reinforced with glass fibres coated with the polar sizing recommended in EP-A-322959 or other commercial fibres, generally these properties improve. It is thought that the additives both lubricate the melt and increase the degree of bonding between fibres and polymer. However, it has been found rather surprisingly that such processing aids should preferably be absent from the reinforced composites of the present invention, because they have a negative influence both on the melt stability and on the mechanical strength. This is a further indication of the unique nature of the present sizing compared to other conventional sizings. It also presents unexpected advantages, for the costly additive can now be dispensed with, and no additional blending steps are necessary. Thus in a preferred embodiment, processing aids such as a copolymer of an α-olefin and an α,β-ethylenically unsaturated carboxylic acid which optionally has been neutralised partially with metal ions, are substantially absent in the composite. The term "substantially absent" implies a presence of less than 1%, preferably less than 0.1%, on a mass basis. The invention is further illustrated by the following example. EXAMPLE (a) A linear alternating terpolymer of carbon monoxide, ethene and propene was prepared in the presence of a catalyst formed from palladium acetate, the anion of trifluoroacetic acid, and 1,3-bis-(diphenylphosphino)propane. The terpolymer had a crystalline melting point of 220 °C and a limiting viscosity number of 1.1 dl/g. (b) Blends of the terpolymer made in (a) were prepared by dry mixing of polymer nibs with short chopped glass fibres in a hopper, and subsequently extruding the mixture, thereby melting the polymer. The resulting strands were processed to nibs, which in turn were injection moulded into test strips. A total of eight composites were prepared. The first four contained only glass (30 %w) and terpolymer (70 %w). The second group of four contained glass (30 %w), terpolymer (69 %w) and 1 %w of a commercially available processing aid, which is thought to be a copolymer of ethylene and acrylic acid which has been partially neutralised with zinc ions. All eight composites, as well as two non-reinforced samples, one with and one without the processing aid, were extruded, dried and injection moulded into standard test pieces under identical processing conditions. The glass fibres used were: (1) OCF 429 YZ, having a sizing comprising aminosilane and uncured epoxy resin functionalities. (2) PPG 22517, having a sizing comprising aminosilane and polyurethane cured epoxy functionalities, not according to the invention. (3) OCF 492 AA, having a polar sizing, recommended in EP-A-322959, not according to the invention. (4) OCF R23 DX1, not according to the invention. (c) The ten test pieces were subjected to standard mechanical testing. The heat distortion temperatures (at 1.82 MPa) and flexural moduli (at 23 °C) of the reinforced samples were 213 (± 2) °C and 6.8 (± 0.2) GPa respectively, irrespective of the composite formulation. The (tensile) yield strengths were determined according to ASTM D790 method 1, procedure B using a span to depth ratio of 16. In addition thereto, nibs of the ten samples were each subjected to a measurement of melt flow rate (at 250 °C using a 1 kg load) and of cross-over-time (at 275 °C and 1 rad/sec). The results are given below in the Table. Glass Type Processing Aid [1 %w] Melt Flow Rate [g/10 min] Yield Strength [MPa, 23 °C] Crossover Time [min] NONE no 17.4 40.6 56.0 1 no 4.4 126.7 50.0 2 no 3.4 125.5 27.0 3 no 2.6 95.0 18.5 4 no 2.5 114.7 11.0 NONE yes 11.7 26.4 49.0 1 yes 4.3 85.2 39.0 2 yes 3.2 127.1 30.0 3 yes 2.7 109.0 21.0 4 yes 2.1 127.1 10.0 The above data indicate that glass fibres reinforce the polyketone terpolymer. The best tensile yield strengths are obtained with glass types Nos. 1 (without processing aid), 2 (with or without processing aid) and 4 (with processing aid). The results also show the processing aid decreases the yield strengths of the neat terpolymer and the composite according to the invention (No. 1). The melt stabilities of the neat terpolymer and the composite according to the invention (No. 1) are decreased too by the addition of the processing aid, whereas the melt stabilities of the composites Nos. 2 and 3 are increased by such addition. The melt stability of composite No. 4, either with or without the processing aid, is unacceptably low. It is obvious that the melt stability of composite No. 1 without processing aid is best: it shows both the longest cross-over-time and the highest melt flow rate of all tested reinforced composites. In conclusion, the results show that the additive free composite No. 1 is an improvement over the other composites. It appears to be much less able to initiate cross-linking than are the sizings on the other fibres tested, and so it is the easiest composite to melt process, whilst its yield strength is only 0.4 MPa less than that of the best of the other composites. Another advantage it possesses, is that the processing aid does not have to be added.

Claims: Reinforced thermoplastic composite characterised by comprising a linear alternating polymer of at least one olefinically unsaturated compound and carbon monoxide, and a glass fibre reinforcement having a coating of a sizing material, wherein the sizing material comprises both aminosilane and uncured epoxy resin functionalities. A composite as claimed in claim 1, characterised in that the linear alternating polymer is an ethene/carbon monoxide copolymer or an ethene/propene/carbon monoxide terpolymer having an ethene to propene molar ratio of at least 3:1. A composite as claimed in claims 1 or 2, characterised in that in the composite copolymer of an α-olefin and an α,β-ethylenically unsaturated carboxylic acid which optionally has been neutralized partially with metal ions, if present amounts to less than 1% on a mass basis. A composite as claimed in any of claims 1 to 3, characterised in that it comprises between 1 and 45%, by mass, of the glass fibre reinforcement. Process for the preparation of a reinforced thermoplastic composite, comprising mixing a linear alternating polymer of at least one olefinically unsaturated compound and carbon monoxide and a glass fibre reinforcement having a coating of a sizing material, and converting the mixture to a reinforced composite by application of heat and/or pressure, wherein the sizing material comprises both aminosilane and uncured epoxy resin functionalities.

Inventors: JORDAAN JOHANNES CLEMENS MARIA, PROCTOR MICHAEL GAVIN, JORDAAN, JOHANNES CLEMENS MARIA, PROCTOR, MICHAEL GAVIN
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1991
Main classification: C08K9
IPC codes: C08K9, C08L73, C08K7