Contrast enhancement filter glass useful for color CRT displays

Abstract: A colored contrast enhancement glass comprises, in wt%: having color properties corresponding to values of (x,y) of the larger quadrangle of Figure 1.

Description: Background of the Invention For some time, CRT manufacturers have used filters to obtain contrast enhancement for full color displays. Useful filters transmit light of frequencies corresponding to the phosphor emission frequencies and absorb all other unwanted light. This substantially reduces glare in full sun applications, e.g., when combined with a front surface AR coating. The most commonly used phosphors for color displays at present are P43 and P22. Their primary emission bands are 544 nm (P43) and 445, 525 and 630 nm (P22), etc. Thus, the optimum contrast enhancement filter would have transmission windows of any desired level around these three wavelengths and would be opaque at all other wavelengths. The first types of contrast enhancement filters utilized were composite filters. The major disadvantage of a composite filter is the high cost of fabrication. This arises from the necessity to prepare a high optical finish on each of the filter surfaces and because the laminate must be bonded together with optical cements to eliminate Fresnel losses. Another significant disadvantage is the increased weight of a composite filter compared to a single glass filter. A typical prior art composite filter is disclosed in U.S. Patent No. 4,245,242. Because of the high fabrication cost of composites, single glasses which combine all required transmission characteristics (as much as possible) have been developed, relying for contrast enhancement primarily on neodymium. Relevant prior art glasses are disclosed in U.S. Patent Nos. 4,521,524; 4,769,347; 4,288,250; 4,376,829; 4,769,347; 3,143,683; 4,520,115 (concerned with X-ray absorption); 4,405,881; and 4,390,637. In addition, such prior art glasses also incorporate various colorants such as Ce0₂, Sm₂0₃, Fe₂0₃, Co0, Ni0, Cu0, Er₂0₃, Mn0₂, V₂0₅, Cr₂0₃, etc. for purposes of obtaining a desired color. The colorants are normally utilized in combinations. Ce0₂ is also well known as a solarization inhibitor. See, e.g., the above-mentioned patents. Various of these conventional ingredients are also known to absorb short wavelength radiation, e.g., UV radiation, e.g., Ce0₂, Ti0₂, etc. It is usually most difficult to achieve a desired color in such glasses since the colorants are often incompatible and can adversely affect contrast efficiency and since the primary contrast enhancement component, i.e., Nd₂0₃, itself is highly colored (purple). Thus, it is often difficult to achieve the given combination of desired color and contrast enhancement properties for a particular end use, e.g., for the color space shown in Figure 1. x, y and z are defined as such by the Handbook of Colorimetry , Arthur C. Hardy, c. 1936, pp. 9-10 x = X X + Y + Z y = Y X + Y + Z z = Z X + Y + Z X, Y, Z are the conventional Tristimulus Values Summary of the Invention This invention provides a colored contrast enhancement glass useful, e.g., for achieving a color in the color space of Figure 1, consisting essentially of, in weight percent: The general composition range given above corresponds to the color space of the large quadrangle of Figure 1 while the preferred range corresponds to that of the smaller quadrangle of Figure 1. Er and Cr oxides are optional (0-1.0 for Er₂O₃ and 0-0.0300 for Cr₂O₃). As can be seen, generally the values of x and y are: x 0.2705-0.2900 0.2767-0.2825 y 0.2710-0.2910 0.2748-0.2835 The above color and transmission properties are measured at a nominal thickness of 3.5 mm. The ranges of glass constituents indicated above are determined by practical glass-making considerations and by their effects on color, contrast and/or transmission properties. Silica levels of greater than 60 wt% cause melt viscosities and forming temperatures to become undesirably high. Below 40 wt%, chemical durability becomes undesirably low and the necessarily high levels of modifier cations can lead to phase separation or devitrification. While boric oxide is not necessary to the present invention, its incorporation is desirable in glasses having Si0₂ levels within the higher portion of the range in order to reduce melt viscosity to desirable levels. If B₂0₃ content is raised above 6 wt%, chemical durability decreases and the glass becomes more prone to phase separation. Aluminum oxide is added to enhance chemical durability. If Al₂0₃ content is above 2 wt%, there are undesirable increases in melt viscosity. Alkali is added to control melt viscosity and to stabilize high concentrations of lanthanide ions. If alkali content is below 24 wt%, melt viscosity becomes undesirably high and the glass becomes more prone to phase separation. At alkali levels above 30 wt%, chemical durability becomes undesirably low, and/or needed amounts of other oxides cannot be incorporated Na₂0 (e.g., 10-18 wt%) and K₂0 (e.g., 8-16 wt%) are preferred. Alkaline earths and zinc are added to improve chemical durability. At levels above 10 wt%, glasses become prone to devitrification and phase separation. Ba0 is preferred. Ti0₂ and Ce0₂ are added to suppress near-UV. They are each unsatisfactorily effective at levels below 1 wt%. At levels above 3 wt% they tend to increase refractive index above desired levels which typically are less than 1.57. An approximately equimolar combination of Ti0₂ and Ce0₂ is a most desirable combination. Nd₂0₃ is the primary contrast enhancement ion in the present invention. Its purpose is to give intense multiband absorption which acts to separate the spectral regions of interest. Levels below 4 wt% do not give adequate contrast enhancement. It has been discovered when the amount of Nd₂0₃ is greater than 12 wt%, a color satisfying the color spec requirements of Figure 1 is generally not achieved in combination with the other necessary colorants for this invention. At a Nd₂O₃ content above the preferred value of 8.5 wt%, the ability to achieve the color spec of Figure 1 becomes more difficult as can be seen by comparing, e.g., Examples 9, 11 and 13 with 10 and 12. Nevertheless, without undue experimentation, the color spec can be achieved throughout the range of Nd of this invention, e.g., by incorporating, less Er₂O₃ and/or CuO, and/or by increasing the amount of V₂O₅. The ability of V₂O₅ incorporations to facilitate attainment of the color spec of this invention is unexpected and can be seen further, for example, by comparing the properties of Example 16 versus those of Examples 4, 5 and 17 per Table 3. Thus, which compositions within the general range of the invention have the desired color properties can be determined routinely without undue experimentation using the guidance of this invention. These other colorants (in addition to any of the above ingredients which inherently produce color, e.g., Nd) include Mn0₂, Er₂0₃, Cu0, Co0, Cr₂O₃ and V₂0₅. As long as these ingredients are maintained within the defined ranges, satisfaction of the color spec of figure 1 can be achieved with at most routine testing. This particular combination of coloring components has not heretofore been suggested as being effective to achieve the desired color characteristics. Glasses meeting the color spec of Figure 1 are generally bluish-purple. La₂0₃ is included in the glass primarily as a replacement for Nd₂O₃ and also for Er₂O₃, e.g., to maintain essentially constant rare earth content between compositions where desired thereby minimizing stability effects and changes in optical and/or physical properties with changes in Er or Nd contents. Copper oxide is added in part to absorb wavelengths above ∼650 nm because of the absorption of Cu²⁺. Levels of Cu0 below 0.1 wt% do not give requisite absorption in this region. Levels above 0.5 wt% reduce the transmission at the 618 or 620 nm phosphor emission wavelength to undesirably low values. Manganese oxide is added in part to absorb unwanted frequencies in the range 470-500 nm, which is the range of maximum absorption of Mn³⁺. Levels of <0.1 wt% do not provide needed absorption intensity when combined with the other colorants above. At levels above 1.0 wt%, transmission at the 445 and 525 nm phosphor emission wavelengths becomes undesirably low. It is also possible to include in the glass very minor amounts of conventional colorants where these do not cause the glass to fall outside of the color space achieved with the necessary ingredients recited above. Such conventional colorants, e.g., include those mentioned above and, e.g., Fe₂0₃, Ni0, Cr₂0₃, in small amounts, e.g., less than 0.030 wt%, preferably less than 0.0005 wt%, etc. These wt% additions are optional intentional inputs into the glass and are not measured trace impurities. The glasses of this invention can be prepared to use in conventional melting techniques and can be molded into any desired shape using conventional glass handling techniques, e.g., faceplates, windows, lenses, etc., especially for use in full sun applications such as in CRT displays in airplane cockpits. The glasses of this invention can also be coated with conventional coatings such as AR coatings. Without further elaboration, it is believed that one skilled in the art can, using the preceding description, utilize the present invention to its fullest extent. The following preferred specific embodiments are, therefore, to be construed as merely illustrative, and not limitative of the remainder of the disclosure in any way whatsoever. In the foregoing and in the following examples, all temperatures are set forth uncorrected in degrees Celsius and unless otherwise indicated, all parts and percentages are by weight. The entire disclosures of all applications, patents and publications, if any, cited above and below, and of corresponding application, are hereby incorporated by reference. The examples disclosed below were melted from conventional glass-making oxide and carbonate/nitrate raw materials in induction-heated platinum crucibles. The mixed batch was typically melted at around 1350°C, refined for three hours at 1450°C and cast at around 1100°C. Glasses were held for two hours at their individual transition temperatures (T g ) being annealed at 30°C/hour to provide stress-free glass. Typical properties are indicated in Table 2: The parameters of analysis introduced in Table 2 and 3 are explained as follows: Photopic relates to the integrated percent transmission over the entire visible range %T relates to the percentage of transmission at the specified wavelength @ at (a wavelength of) DWL (nm) D ominant W ave l ength % Purity relates to the nature of the mix of the colour components. The preceding examples can be repeated with similar success by substituting the generically or specifically described reactants and/or operating conditions of this invention for those used in the preceding examples. From the foregoing description, one skilled in the art can easily ascertain the essential characteristic of this invention, and without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various usages and conditions.

Claims: A contrast enhancement glass composition consisting essentially of, in wt%, Si0₂ 40-60 B₂0₃ 0-6 Al₂0₃ 0-2 ΣLi₂0, Na₂0, K₂0 = R₂0 24-30 ΣMg0, Ca0, Sr0, Zn0, Ba0 = R0 0-10 Ti0₂ 1-3.5 Ce0₂ 1-3.5 Nd₂0₅ 4-12 La₂0₃ 1-11 Mn0₂ 0.1-1.0 Er₂0₃ (when included) 0.2-1.0 Cu0 0.1-0.5 Co0 0.0005-0.0040 V₂0₅ 0.05-0.50 Cr₂0₅ (when included) 0.0005-0.0300 Photopic (%T) 12-24 %T @ 445 nm 20-30 %T @ 555 nm 26-36 %T @ 580 nm 0-3 %T @ 618 nm 23-35 %T @ 620 nm 23-34 having color properties corresponding to values of (x,y) of the larger quadrangle of Figure 1. A glass of claim 1 consisting essentially of, in wt%, Si0₂ 40-48 B₂0₃ 3-6 Al₂0₃ 0-1 ΣLi₂0, Na₂0, K₂0 = R₂0 25-28 ΣMg0, Ca0, Sr0, Zn0, Ba0 = R0 3-5 Ti0₂ 2-3 Ce0₂ 2-3 Nd₂0₅ 6-8.5 La₂0₃ 4-8 Mn0₂ 0.2-0.8 Er₂0₃ (when included) 0.3-1.0 Cu0 0.15-0.40 Co0 0.0010-0.0035 V₂0₅ 0.10-0.40 Cr₂0₅ (whene included) 0.005-0.0150 Photopic (%T) 15-21 %T @ 445 nm 22.6-28.6 %T @ 555 nm 30.5-33.5 %T @ 580 nm 0-2 %T @ 618 nm 26.3-32.7 %T @ 620 nm 25.5-31.5 having color properties corresponding to values of (x,y) of the smaller quadrangle of Figure 1. A glass of claim 1, having the following properties: Photopic (%T) 12-24 %T @ 445 nm 20-30 %T @ 555 nm 26-36 %T @ 580 nm 0-3 %T @ 618 nm 23-35 %T @ 620 nm 23-34 A glass of claim 2 having the following properties: Photopic (%T) 15-21 %T @ 445 nm 22.6-28.6 %T @ 555 nm 30.5-33.5 %T @ 580 nm 0-2 %T @ 618 nm 26.3-32.7 %T @ 620 nm 25.5-31.5 A glass of any of the foregoing claims wherein R₂O is Na₂O and K₂O. A glass of any of the foregoing claims wherein RO is BaO. A glass of claim 1 also containing up to 0.0150 wt% Cr₂O₃. In a color CRT device comprising a color CRT and a filter glass, the improvement wherein the filter glass is one of any of the foregoing claims.

Inventors: CIOLEK SALLY, KRASHKEVICH DAVID, CIOLEK, SALLY, KRASHKEVICH, DAVID
Applicants: SCHOTT GLASS TECH INC, SCHOTT GLASS TECHNOLOGIES, INC.
Application year: 1991
Main classification: C03C3
IPC codes: C03C3, C03C4