PROCESS FOR PRODUCING LIQUID-CRYSTAL CELLS

Abstract: A process for producing a liquid-crystal cell which comprises the steps of: a) providing a curable sealant portion in the periphery of the side of an electrode plate that has an electrode or electrodes; b) (i) coating a ferroelectric liquid-crystal composition on the portion surrounded by said sealant portion, with a spacer being preliminarily provided in said portion; (ii) coating spacer-containing ferroelectric liquid-crystal composition on the portion surrounded by said sealant portion; or (iii) coating a ferroelectric liquid-crystal composition on the portion surrounded by said sealant portion and thereafter providing a spacer over said composition; c) defoaming the coated layer of the liquid-crystal composition by heating during or after evacuation; d) placing the other electrode plate in such a way that the side of said other electrode plate which has an electrode or electrodes faces the side of said one electrode plate containing the thermally defoamed coated layer of the liquid-crystal composition and compressing the two electrode plates together; and e) curing said sealant. A process according to claim 1 which further includes the step of heating the liquid-crystal cell after step (e) is disclosed.

Description: SPECIFICATION PROCESS FOR PRODUCING LIQUID-CRYSTAL CELLS FIELD OF THE INVENTION: The present invention relates to a process for producing liquid-crystal cells using ferroelectric liquid crystals (FLC) . BACKGROUND OF THE INVENTION: Liquid-crystal cells using FLC have drawn increasing attention as elements that can be used as displays in watches, hand-held calculators, various OA (office automation) equipment and television sets. A liquid-crystal cell using FLC is currently manufactured by a process that comprises the steps of placing a pair of electrode plates in such a way that their electrode sides face each other, bonding the plates together by means of a sealant provided in the periphery to leave a central hollow portion that is to be filled with a liquid crystal, and injection FLC into the follow portion through an inlet in the sealed portion by capillary action under high-temperature and high-vacumm conditions. A problem with this method is that since the gap between the two electrode plates for the FLC liquid- crystal cell is so small (ca. 2 μm) compared to cells using conventional twisted nematic liquid crystals that it takes quite a long time for filling the cell with FLC even if pressure is applied. Further, FLC is so viscous compared to nematic liquid crystals even if it is heated for injection that defoaming (removal of air and other gases that are contained in the liquid crystal) is difficult to achieve or can only be performed unevenly. SUMMARY OF THE INVENTION: The present invention has been accomplished under these circumstances on the basis of the finding that excellent liquid-crystal cells for use of ferroelectric liquid crystals can be produced by combining the following two techniques, i.e., preliminarily forming a coated FLC layer on electrode plates without injecting FLC by capillarity, and heating said coated FLC layer for deforming and to provide homogeniety in its structure. The present invention relates to a process for producing a liquid-crystal cell which comprises the steps of: (a) Providing a curable sealant portion in the periphey of the side of an electrode plate that has an electrode; (b) (i) coating a ferroelectric liquid-crystal composition on the portion surrounded by said sealant portion, with a spacer being preliminarily provided in said portion; (ii) coating spacer-containing ferroelectric liquid- crystal composition on the portion surrounded by said sealant portion; or (iii) coating a ferroelectric liquid-crystal composition on the portion surrounded by said sealant portion and thereafter providing a spacer over said composition; (c) defoaming the coated layer of the liquid-crystal composition by heating during or after evacuation; (d) placing the other electrode plate in such a way that the side of said other electrode which has an electrode faces the side of said one electrode containing the thermally defoamed coated layer of the liquid-crystal composition and compressing the two electrode plates together; and (e) curing said sealant. BRIEF DESCRIPTION OF THE DRAWINGS: Figs, la - lc show schematically the major steps of the process of the present invention, in which Fig. la and lb are plan views and Fig. lc is a perspective view. DETAILED DESCRIPTION: In step (b) , the spacer can be provided by one or more of the following methods: i) the spacer is sprayed before the composition is coated; ϋ) the composition containing the spacer is coated to form a layer that contains it; iii) the spacer is sprayed over the coated layer of the composition; iv) a photosensitive resin layer is provided on the electrode plate and partially exposed to light, followed by development of the exposed or non-exposed area to form a spacer (directly) , which is then coated with the composition (the photosensitive resin may be positive-type or negative- type action) ; and v) the surface of the substrate which is typically made of glass is partially etched to form a spacer (directly) and the composition is subsequently coated. The purpose of providing the spacer is to provide a cell of uniform thickness. Methods i) and iii) may be implemented by either a wet system (using Freon gases as a carrier) or a dry system (dusting air) . In method iv) , either positive-type or negative- type photoresists can be used as photosensitive resins. An example of the positive-type photosensitive resins is AZ 1300 SF of Hoechst AG and an example of the negative-type photosensitive resins is 0ZATEC NL 143 of Hoechst AG. The photosensitive resin is coated in a thickness of 0.5 - 10 μm, preferably 1.5 - 3 μm, as measured after development. Except in method iv) , the spacer has a diameter of 0.5 - 10 μm, preferably 1.5 - 3 μm, and may be made of an inorganic material such as silicon oxide, or a polymer selected from among acrylic resins and epoxy resins. The shape of the spacer is not limited in any particular way and it may be in the form of a true sphere, a rod, a prism, etc., with a true spherical shape being preferred. The spacer is used in an amount of 0.1 - 10 wt%, preferably 1 - 5 wt%, of the total amount of the composition. The preferred embodiment of the present invention is described below in greater detail with reference to the accompanying drawings. A glass or plastic-plate is used as the electrode plate and a transparent electrode such as ITO is provided on one side of the plate. The electrode on one of the electrode plates that make up a cell may be opaque. The side of each electrode plate which has an electrode is overlaid with an alignment film made of a polymer coat such as polymide or polyamide or an inorganic coat such as silicon oxide. As shown in Fig. la, a curable sealant such as a uv curable sealant (e.g. epoxy resin) or low- temperature (heat) curable sealant (e.g. epoxy resin that cures at ca. 100 - 150°C) is screen printed onto the periphery of the side of an electrode plate 1 that includes an electrode (not shown) , whereby a sealant portion 2 is provided. Then, as shown in Fig. lb, FLC composition containing a spacer is printed (e.g. by intaglio), roll coated or otherwise applied to the portion surrounded by the sealant portion 2, so as to form a coated layer of FLC composition 3. The FLC composition may be composed of ingredients in various combinations. To prepare the composition, a basic formulation consisting of the following eight components (their contents shown in mol%) is first provided: 13.39 H 1 7C8 -O-" -0-C 6 Hι 4.49 Hι 14.78 H17C8 — 0-C 4 H £ 8.14 Hi 7 C8 -0- Q >-{ V-0-C I OH 2 : 20 .00 Hi 7C 8 - θ )~ O — OCO-CeHi s This basic formulation undergoes the following phase transfer: S C 71S A 78N93I Chiral dopants may be added to this basic formulation and the following are examples of the compounds that can be used as chiral dopants: Dopant DI: (S) Dopant D2: C3H7 cis Dopant D3: trans By adding these dopants to the basic formulation, an FLC composition having the following formula (the contents being shown in mol%) is obtained: Basic formulation 87.67 Dopant DI 4.53 Dopant D2 2.70 Dopant D3 5.10 This composition experiences spontaneous polarization of 30 nC x cm" 2 at 25 °C and exhibits the phase transfer series of S C *61S A *69N*85I. In the next step, the coated layer of the FLC composition is heated, during or after evacuation, up to the temperature at which the FLC composition exhibits an isotropic liquid or a nematic phase, whereby the coated layer of the composition is deformed and rendered to have a homogeneous structure. Subsequently, as shown in Fig. lc, the other electrode plate 4 which is neither printed with a sealant nor coated with a liquid crystal is placed either in vacuo or at atmospheric pressure in such a way that the side of said plate which has an electrode (not shown) faces the side of the electrode plate 1 that includes the coated layer of the defoamed FLC composition, and the two electrode plates are compressed together. By applying pressure 5 until the gap between the two plates reaches a desired value, a cell is fabricated. As the cell is compressed or after it has been compressed, an ultraviolet radiation or heat is applied to cure the sealant, whereby a complete liquid-crystal cell is produced. If thermal defoaming is found to be insufficient to provide a homogeneous structure in the coated layer of the FLC composition, the liquid- crystal cell may be re-heated up to the temperature at which the FLC composition exhibits an isotropic liquid or a nematic phase. An example of the present invention is described below. Example ITO transparent electrode and polymide orientation membrance were placed on a glass plate. An ultraviolet- curable epoxy resin (Hoechst AG, Epoxy Resin Beckopox) was applied on the periphery of the orientation membrance by using screen printing at a thickness of 10 μ without installing an opening for injection of FLC. FLC composition (V) incorporating a spacer (Si0 as true spherical beads of 2 μm in diameter) in an amount of 3 wt% of the total composition was coated on the portion surrounded by the epoxy resin (sealing portion) by using a roll coater at a thickness of 2 μ. The electrode plate thus treated and the other electrode plate not having a coating of sealing agent and an FLC coating, were charged into a vacuum chamber, which was evacuated to 10" 2 Torr. The two electrode plates were heated at 90 - 100°C in vacuum to defoam the FLC composition. Air in the FLC composition was completely removed in 10 minutes. The two electrode plates were compressed together by a pressing means provided in the vacuum chamber so that the gap between the two electrode plates decreased to 2 μ, and then the sealing agent was cured by exposure to ultraviolet radiation while compressing the plates, whereby the liquid-crystal cell of the present invention was fabricated.

Claims: CLAIMS 1. A process for producing a liquid-crystal cell which comprises the steps of: (a) providing a curable sealant portion in the periphey of the side of an electrode plate that has an electrode or electrodes; (b) (i) coating a ferroelectric liquid-crystal composition on the portion surrounded by said sealant portion, with a spacer being preliminarily provided in said portion; (ii) coating a spacer-containing ferroelectric liquid-crystal composition on the portion surrounded by said sealant portion; or (iii) coating a ferroelectric liquid-crystal composition on the portion surrounded by said sealant portion and thereafter providing a spacer over said composition; (c) defoaming the coated layer of the liquid-crystal composition by heating during or after evacuation; (d) placing the other electrode plate in such a way that the side of said other electrode plate which has an electrode or electrodes faces the side of said one electrode plate containing the thermally defoamed coated layer of the liquid-crystal composition and compressing the two electrode plates together; and (e) curing said sealant. 2. A process according to claim 1 which further includes the step of heating the liquid-crystal cell after step (e) .

Inventors: ESCHER CLAUS, HARADA TAKAMASA, ILLIAN GERHARD, OHLENDORF DIETER, RIEGER HEINZ, ROESCH NORBERT, ESCHER, CLAUS, HARADA, TAKAMASA, ILLIAN, GERHARD, OHLENDORF, DIETER, RIEGER, HEINZ, ROESCH, NORBERT
Applicants: HOECHST JAPAN, HOECHST JAPAN LIMITED
Application year: 1991
Main classification: G02F1
IPC codes: G02F1