Hydrophilic form of perfluoro compounds and method of manufacture

Abstract: Perfluoro compounds such as C₁₂F₂₀; C₁₂F₂₇N; C₁₂F₂₆O; C₈F₁₇Br; and C₁₄F₂₄ are rendered dispersable colloidally in water or other polar media without the aid of an emulsifying agent by melt spinning a mixture of the compound with a carrier agent, e.g., a saccharide. Thus, a family of new colloidal perfluoro compounds are produced.

Description: Background of the invention The present invention relates to hydrophilic substances containing perfluoro compounds and to methods of making emulsions containing perfluoro compounds. DE-A-2 940 184 discloses a colloidal solution obtained by reacting physiologically compatible water soluble colloids such as dextranes, modified gelatins, hydroxyethyl starches or albumine, with an aliphatic perfluoro compound. After completion of the reaction the solution is neutralized with an isotonic electrolyte. WO-A-8908459 discloses an emulsion which comprises perfluoro chemical particles containing within stabilized vesicles formed of biocompatible polymer. The perfluoro chemical material is combined with a monomeric emulsifying material which is then homogenized in aqueous medium to form an emulsion. EP-A-0 307 087 describes the favorable effect of e.g hexahydric alcohols and certain sugars, which are used as osmotic and buffering agents in fluorocarbon emulsions. The pretended beneficial effect of e.g. glucose sugar on the emulsion stability is explicitly associated with the activity of lecithin, which functions as an emulsifying agent forming a protecting membrane enclosing the fluorocarbon particles. In United States Patent No. 4,855,326 various substances having pharmacological properties were combined with a sugar and spun into fibers to produce a readily water-soluble product. The various examples enumerated in the patent all involved the use of water soluble medicaments and were directed to enhancing the solubility rate of the different substances. The patent describes methods for combining a medicament with any one or more of the water soluble melt spinnable sugars and spinning the combination to produce a readily soluble floss form of the medicament. In United States Patent No. 5,011,532 the disclosure deals with oleaginous substances such as vegetable oil, baby oil, olive oil, margarine, lanolin, cocoa butter, and the like, and how their lack of affinity for water is altered by mixing the oleaginous substance with sugar and melt spinning the mixture in a cotton candy spinning machine or the equivalent. As so modified the products disperse autogenously in water forming a colloidal or pseudo-colloidal dispersion. Such modification enabled such widely disparate procedures as: (a) incorporating shortening oil in a cake mix containing flour but no egg to which water is added to produce a batter; and (b) producing a confection or medicated lozenge by dehydrating the dispersion and allowing the melted residue to solidify. The patent discloses that any oleagiiious substance that can be mixed with a melt-spinnable sugar, when spun in a cotton candy spinning machine, produces a product which, when added to water or has water added to it, forms, virtually autogenously, a uniform dispersion having all the appearances of a colloidal dispersion. Other disclosures dealing with spinning substances with one or more sugars will be found in United States Patent Nos. 4,873,085; 5,034,421; 5,028,632; and 4,997,856. In United States Patent No. 5,034,421 it is explained that a spun product from a combination of a saccharide and a hydrophobic ingredient is hydrophilic with low concentrations of such ingredient but becomes increasingly hydrophobic as the concentration of the hydrophobic ingredient is increased, although the end product nevertheless acts hydrophilically when the water temperature is elevated. Beeswax is disclosed in US-A-5 034 421 as being a moderating agent. As described therein, pure white pharmaceutical grade beeswax, a substance that is essentially hydrophobic, was mixed with sucrose and spun, producing an excellent floss which floated when added to normal room temperature water, but immediately dispersed with the appearance of being colloidal when added to water at about 82.2°C. In the Kirk-Othmer Encyclopedia of chemical Technology, 3rd ed., Suppl. Vol. - Alcohol Fuels to Toxicology, published by John Wiley & Sons, Copr. 1984, there appears, on pp. 159-171, an article entitled "Blood-Replacement Preparations" by Robert Geyer of Harvard University. The article deals with liquid perfluoro compounds which have been investigated for biomedical application. These nonpolar materials dissolve appreciable quantities of gases such as oxygen and carbon dioxide. The article lists 18 different compounds in a table on page 162 which compounds are identified as suitable for blood-replacement preparations. Among the compounds mentioned are: the perfluoro derivatives of dimethyladamantane, formula C 12 F 20 ; tributylamine, formula C 12 F 27 N; dihexyl ether, formula C 12 F 26 O; and 1-bromooctane, formula C 8 F 17 Br. All of the mentioned perfluoro compounds are colorless and odorless liquid organic compounds in which all hydrogens have been replaced with fluorine. They are essentially insoluble in water and other polar liquids. To provide a per fusion liquid the perfluoro compound has to be emulsified and this has required an emulsifying agent. The emulsifying agents must be strictly nontoxic for biomedical use. Frequently used emulsifying agents are phospholipids such as egg-yolk phospholipids. A proprietary product, "Pluronic F-68" produced by BASF Wyandotte Corp., is mentioned in the above article, and stated to be the most frequently used surfactant for blood-replacement preparations. However, the article states that the purified form of the surfactant must be stored at -25°C or lower, preferably under nitrogen. The restriction on utility should be self-evident. Use of the egg-yolk phospholipids has encountered problems in that experiments have uncovered a high rate of adverse human reaction to the phospholipids. Thus, prior to the present invention it has not been possible to produce a satisfactory in vivo perfusion liquid suitable for transfusion which is based on a perfluoro compound. SUMMARY OF THE PRESENT INVENTION It is, therefore, an object of the present invention to provide a mass of spun fibers containing a perfluoro compound but no emulsifying agent which mass of fibers when added to water disperses therein without the aid of an emulsifying agent to form a colloidal dispersion. In accordance with one aspect of the present invention there is provided a mass of spun fibers consisting essentially of one or more sugars where the sugars are capable of being spun into fibers that are readily water-soluble, and a perfluoro compound that in its separate state is essentially insoluble in water and other polar liquids, said compound being distributed on or incorporated in the fibers of said mass. According to a further aspect of the present invention said mass of spun fibers is dispersed in an aqueous medium, e.g. distilled water, to form a colloidal dispersion without employing an emulsifying agent. DETAILED DESCRIPTION OF THE PRESENTLY PREFERRED EMDODIMENTS Typical of the discovery that has given rise to the present invention is that perfluoro compounds of the type and general character identified above can be mixed with a melt-spinnable sugar and thereafter spun in a cotton candy spinning machine to produce a product which, when added to water or has water added to it, forms, with a minimum or no agitation, a uniform dispersion having all the appearances of a colloidal dispersion. Useful perfluoro compounds are selected from perfluoro derivatives of dimethyladamantane, tributylamine, dihexyl ether, 1-bromooctane, tetradecahydrophenanthrene, and combinations thereof. The invention can best be described and understood from a consideration of a number of examples. For the following examples the floss spinning machine used was: Econo Floss Model 3017 manufactured by Gold Medal Products Co. of Cincinnati, Ohio. Unless otherwise stated, reference to sucrose in the examples is to "Domino" granulated sugar. Unless otherwise indicated, the temperature of the grid in the spinning machine was estimated to be at about 82.2°C or somewhat higher while operating at a speed of about 3800 R.P.M. Under static conditions, assuming that the grid is stationary and out of contact with the sugar, the grid temperature was estimated to be at about 260°C. EXAMPLE I One part by volume perfluorooctylbromide marketed by Alliance Pharmaceutical Corp., of San Diego, California under the trademark "Imagent GI" was mixed with three parts by volume sucrose. It was mixed with a spoon in a glass vessel for about 5 minutes. The mixture was then spun using the floss spinning machine. A quantity of floss was produced. When some of this floss was added to a quantity of water at room temperature, the floss immediately dispersed in the water producing a mild to moderate Tyndahl effect characteristic of a colloidal dispersion. Examination by microscope at a magnification of about 1200X reveals complete colloidal dispersion with the suspended particles averaging about 2 micrometer or less. The "Imagent GI" material is supplied as a clear liquid which is intended to be taken orally undiluted prior to an NMR examination of the G.I. tract. Alliance Pharmaceutical also has for limited experimental use a colloidal dispersion form of perfluorooctylbromide intended for intravenous application. This form consists of equal quantities of perfluorooctylbromide and distilled water with sufficient egg yolk phospholipid to cause a complete dispersion. But, as explained previously, the egg yolk phospholipid causes adverse systemic reactions limiting the use of such product. By contrast, the colloidal dispersion that is produced from the floss prepared in the present example, if dispersed in distilled water, can be given intravenously with none of the heretofore involved risks of an adverse reaction otherwise associated with the presence of the phospholipid. Another name for this perfluoro compound is perfluoro 1-bromooctane having the formula, C 8 F 17 Br, and known by the abbreviation, FOB. EXAMPLE II Example I was repeated substituting for the sucrose an equal quantity of dextrose obtained from Sigma Chemical Co. of St. Louis, Missouri. The results were essentially the same. EXAMPLE III The following compounds were obtained under generic labeling: Perfluoro derivative of abbreviation Formula dimethyladamantane FDMA C 12 F 20 tributylamine FC-43 C 12 F 27 N dihexyl ether FHE C 12 F 26 O Each of the above compounds was mixed with sucrose in the same ratio as in Example I and spun into a floss with the same result. That is, an otherwise immiscible perfluoro compound was rendered miscible in water by spinning with sucrose. The perfluoro compounds involved in the examples set forth above are representative of the entire class of such compounds identified in the above-mentioned article by Robert Geyer. All of the other per fluoro compounds identified in said article should spin with sucrose or dextrose in the same manner as described in Examples I, II and III hereof. EXAMPLE IV 10 ml. of perfluoro (tetradecahydrophenanthrene) C 14 F 24 , front PCR Inc. of Gainsville, Florida, was added to 150 g of sucrose which was then mixed thoroughly. The resultant mixture was spun using the floss spinning machine identified above to produce a nice floss. Next, 10 g of the floss was dispersed in 10 g of distilled water by stirring with a pipette. Then 5 drops of the liquid mixture were placed on a glass slide over which was placed a coverglass. Optical examination of the sample on the slide was accomplished using an Olympus Bh2 microscope. Particles were observed ranging in size from 0.2 micrometer to 2 micrometer. EXAMPLE V Example IV was repeated using the perfluorooctylbromide of Example I instead of the perfluoro (tetradecahydrophenanthrene). Similar particle sizes were obtained in the dispersions. From the foregoing it should be appreciated that any of the mentioned perfluoro compounds can be spun with a sugar to produce a floss which when added to distilled water can safely be administered intravenously. Useful sugars include maltose, fructose, sorbitol, dextrose, mannitol, sucrose, lactose and combinations thereof. However, the colloidal dispersions produced from perfluoro compounds in the manner discussed above can also be incorporated in sundry media such as emollients, cosmetic creams and lotions for topical application where the perfluoro compound can release oxygen to the skin. For lanolin or oil based cosmetics or topical medicaments conventional homogenization techniques can be used, while for water based substances the dispersions can be added directly without any additional emulsifying agents or homogenization.

Claims: A mass of spun fibers consisting essentially of one or more sugars where the sugars are capable of being spun into fibers that are readily water-soluble, and a hydrophobic substance which is distributed on or incorporated in the fibers of said mass, characterized in that said hydrophobic substance is a perfluoro compound that in its separate state is essentially insoluble in water and other polar liquids. A mass of spun fibers according to claim 1, characterized in that said perfluoro compound is selected from the group consisiting of perfluoro derivatives of dimethyladamantane, tributylamine, dihexyl ether, 1-bromooctane, tetradecahydrophenanthrene, and combinations thereof. A mass of spun fibers according to claim 1 or 2, characterized in that said sugar is selected from the group consisting of maltose, fructose, sorbitol dextrose, mannitol, sucrose, lactose, and combinations thereof. A method for producing a perfusion product, characterized in that a mass of spun fibers according to any of claims 1-3 is colloidally dispersed throughout an aqueous medium without employing an emulsifying agent. A method for producing a perfusion product according to claim 4, characterized in that said aqueous medium is distilled water. A method for producing a cosmetic composition, characterized in that a mass of spun fibers according to any of claims 1-3 is colloidally dispersed throughout an aqueous medium without employing an emulsifying agent, and the colloidal dispersion thus obtained is dispersed throughout a carrier agent comprising an oil and/or water based cosmetic composition.

Inventors: FUISZ RICHARD C, FUISZ, RICHARD C.
Applicants: FUISZ TECHNOLOGIES LTD, FUISZ TECHNOLOGIES LTD.
Application year: 1991
Main classification: A61K31
IPC codes: A61Q19, A61K8, A61K9, A61K31, A61K47, A61K49