Curable resin and composition containing the same

Abstract: The curable resin having a number average molecular weight of 600 to 6000 and at least two hydrolyzable silyl groups which is prepared by reacting an aliphatic polyester resin having acryloyl group and alcoholic hydroxyl group with an isocyanate silane compound: reacting the obtained reaction product with an aminosilane compound: and reacting the obtained reaction product with a monofunctional isocyanate: OCN-R⁵ and/or a polyfunctional isocyanate; and the composition containing the resin. The curable resin and the composition are excellent in acid resistance such as acid resin resistance, scratch resistance, solvent resistance, flexibility, and the like.

Description: The present invention relates to a curable resin and a composition containing the same, and more particularly to a curable resin whose main chain consists essentially of an aliphatic polyester chain and which has on the polymer chain end at least two hydrolyzable silyl groups, and the composition containing the same. The present invention provides a curable resin which is excellent in flexibility, solvent resistance, resistance to acid rain (acid rain resistance), resistance to scratch (scratch resistance), and is low in viscosity, and a composition containing the above-mentioned resin. The curable resin of the present invention is suitable for use as a base resin used in coatings, adhesives, sealing agents and potting agents, or as a polymer to be blended with a cellulose such as nitrocellulose or cellulose acetate butyrate, another polymer such as an epoxy resin, a polyester, an alkyd resin or an acrylic polyol, particularly a hydrolyzable silyl group-containing vinyl resin disclosed in, for instance, Japanese Unexamined Patent Publication No. 54-36395. In a field where a curable resin is used in the state of a solution, particularly in the field of coatings, it is desired to prepare a high solid coating material which can be conformed to effluent regulations to solvents, for instance, prescribed in VOC Regulation provided in United States of America. On the other hand, as to qualities to top coatings required in the market, particularly as to qualities of coatings for automobiles, it is desired to obtain an improved appearance, scratch resistance, so that outside parts of the automobile are not scratched in a car washer, as well as improved resistance to acid rain, derived from the environmental pollution. Melamine coatings are generally used for this purpose at the present time. However, the acid resistance and scratch resistance of melamine coatings of a regular solid type are not necessarily satisfactory. On the other hand, in order to obtain a high solid coating, some efforts have been exerted. However, if the content of the melamine resin component having a low viscosity is increased in the coating composition in order to obtain a high solid coating, the acid resistance and scratch resistance are lowered. An object of the present invention is to provide a curable resin which is improved in flexibility, solvent resistance, acid rain resistance and scratch resistance and is low in viscosity, and which is suitable for use of a blend with another resin. A further object of the present invention is to provide a composition containing the above-mentioned resin which is improved in flexibility, solvent resistance, acid rain resistance and scratch resistance. These and other objects of the present invention will become apparent from the description hereinafter. It has now been found that a resin whose main chain comprises an aliphatic polyester and which has on the polymer chain end a hydrolyzable silyl group is low in viscosity and a cured product thereof is excellent in scratch resistance, flexibility, solvent resistance and acid rain resistance. In accordance with the present invention, there is provided a curable resin having a number average molecular weight of 600 to 6000 and at least two hydrolyzable silyl groups in one molecule, which is obtainable by (i) reacting an aliphatic polyester resin (A) having, in one molecule, both an acryloyl group and an alcoholic hydroxyl group on the polymer ends, with an isocyanate silane compound (B) having the formula (I): wherein R 1 is a bivalent hydrocarbon group having 1 to 10 carbon atoms selected from an alkylene group, a C 6 -C 10 -cycloalkylene group an arylene group and an aralkylene group, R 2 is an alkyl group having 1 to 10 carbon atoms, each X 1 is a hydrolyzable group and m is 1, 2 or 3 to give a reaction product (i); (ii) reacting the obtained reaction product (i) with an aminosilane compound (C) having the formula (II): wherein R 3 is a bivalent hydrocarbon group having 1 to 10 carbon atoms selected from an alkylene group, a C 6 -C 10 -cycloalkylene group an arylene group and an aralkylene group, R 4 is an alkyl group having 1 to 10 carbon atoms, each X 2 is a hydrolyzable group and n is 1, 2 or 3, or a mixture of 10 to 95 % by mole of said aminosilane compound (C) and 5 to 90 % by mole of a mercaptosilane, whereby the amino group in said aminosilane compound (C) is reacted with said acrylolyl group in said reaction product (i), to give an aminosilane-modified resin (ii), and (iii) reacting the aminosilane-modified resin (ii) with a monofunctional organic isocyanate compound (D-1) having the formula (III): OCN-R 5 wherein R 5 is a monovalent hydrocarbon group having 1 to 25 carbon atoms selected from an alkyl group, a C 6 -C 25 -cycloalkyl group an aryl group and an aralkyl group, a group of the formula: (CH 3 O) 3 Si-(CH 2 ) 3 or a group of the formula: (C 2 H 5 O) 3 Si (CH 2 ) 3 and/or a polyfunctional organic isocyanate compound (D-2) in the substantial absence of water. Further preferred embodiments of the present invention are as ¼ follows: The above-mentioned curable resin wherein, in the formula (I), the Group X 1 is a methoxy group and the integer m is 3. The above-mentioned curable resin wherein, in the formula (II), the group X 2 is a methoxy group and the integer n is 3. The above-mentioned curable resin wherein, in the formula (I), the group X 1 is a methyl group and the integer m is 3 and, in the formula (II), the group X 2 is a methoxy group and the integer n is 3. The above-mentioned curable resin wherein, in the formula (I), the group R 2 is a methyl group, the group X 1 is a methoxy group and the integer m is 2. The above-mentioned curable resin wherein, in the formula (II), the group R 4 is a methyl group, the group X 2 is a methoxy group and the integer n is 2. The above-mentioned curable resin wherein, in the formula (I), the group R 2 is a methyl group, the group X 1 is a methoxy group and the integer m is 2 and, in the formula (II), the group R 4 is a methyl group, the group X 2 is a methoxy group and the integer n is 2. Also, in accordance with the present invention, there is provided a composition comprising 95 to 5 parts by weight of the above-mentioned curable resin (b) and 5 to 95 parts by weight of a silyl group-containing vinyl polymer (a) having, in one molecule, at least one silyl group having the formula (IV): wherein R 6 and R 7 are the same or different and each is a hydrogen atom or a monovalent hydrocarbon group having 1 to 10 carbon atoms selected from an alkyl group, an aryl group and aralkyl group, each Y is a halogen atom, an alkoxy group, an acyloxy group, an aminoxy group, a phenoxy group, a thioalkoxy group or an amino group, and at least one Y is an alkoxy group or a phenoxy group, and a is 1, 2 or 3, the total amount of the curable resin (b) and the vinyl polymer (a) being 100 parts by weight. Fig. 1 is a chart of the infrared absorption spectrum of a reaction product (i) obtained in Example 1; Fig. 2 is a chart of the infrared absorption spectrum of a reaction product (ii) obtained in Example 1; and Fig. 3 is a chart of the infrared absorption spectrum of a curable resin obtained in Example 1. In the present invention, firstly, the aliphatic polyester resin (A) having both an acryloyl group and an alcoholic hydroxyl group in one molecule is reacted with the isocyanate silane compound (B). In the present invention, any aliphatic polyester resins can be used as the component (A) without any limitation, so long as the aliphatic polyester resin has both an acryloyl group and an alcoholic hydroxyl group at the polymer ends and has a number average molecular weight of preferably 200 to 5,000, more preferably from 300 to 3,000. Examples of the polyester chain of the aliphatic polyester resin (A) are, for instance, a polyester such as polyethylene adipate, polydiethylene adipate, polypropylene adipate, polytetramethylene adipate, polyneopentylene adipate, polymethylpentanediol adipate, poly-ε-caprolactone or a polyvalerolactone such as polymethylvalerolactone, a copolyester containing components of these polyesters or a polyhexamethylene carbonate. Among them, poly-ε-caprolactone and polymethylvalerolactone are preferable from the viewpoint of weatherability, and polymethylvalerolactone is preferable from the viewpoint of acid rain resistance. Examples of the aliphatic polyester resin (A) are, for instance, poly-ε-caprolactone acrylates such as "Placcel FA-1" commercially available from Daicel Chemical Industries, Ltd., "Placcel FA-2", "Placcel FA-3", "Placcel FA-4", "Placcel FA-8", or polymethylvalerolactone acrylates commercially available from Kabushiki Kaisha Kuraray. The isocyanate silane compound (B) has the formula (I): In the formula (I), R 1 is a bivalent hydrocarbon group having 1 to 10 carbon atoms, concretely, a linear or branched alkylene group having 1 to 10 carbon atoms such as a trimethylene group, hexamethylene group, a cycloalkylene group having 6 to 10 carbon atoms such as cyclohexylene group, an arylene group having 6 to 10 carbon atoms such as a phenylene group or an aralkylene group having 7 to 10 carbon atoms such as a xylylene group, R 2 is an alkyl group having 1 to 10 carbon atoms such as a methyl group or ethyl group, each X 1 is a hydrolyzable group, and m is 1, 2 or 3. Examples of the hydrolyzable group X 1 are, for instance, a halogen atom, an alkoxy group such as a methoxy group, ethoxy group or butoxy group, an acyloxy group such as an acetoxy group, an aminoxy group, a phenoxy group, a thioalkoxy group or an amino group. Among them, the alkoxy group and the acyloxy group are preferable from the viewpoints of the safety and smelling. Examples of the isocyanate silane compound (B) are, for instance, 3-isocyanatopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane and 3-isocyanatopropylmethyldimethoxysilane. It is preferable that the isocyanate silane compound (B) is reacted with the aliphatic polyester resin (A) in an amount of 0.3 to 1.0 mole, more preferably from 0.6 to 1.0 mole, per mole of the alcoholic hydroxyl groups in the aliphatic polyester resin (A). When the amount of the isocyanate silane compound (B) is less than 0.3 mole per mole of the alcoholic hydroxyl groups in the polyester resin (A), many non-reacted hydroxyl groups remain, thus the storage stability tends to lower. On the other hand, when the amount of isocyanate silane compound (B) is more than 1.0 mole, there remains non-reacted isocyanate silane compound (B). The reaction of the aliphatic polyester resin (A) and the isocyanate silane compound (B) can be conducted at a temperature of room temperature to 200°C for 0.5 to 5 hours in the substantial absence of water, and the reaction can easily proceed under the above-mentioned reaction conditions. In the above-mentioned reaction, as a catalyst, an organotin catalyst such as dibutyltin dilaurate, tin octoate or stannous octoate can be used. Also, in order to inhibit the radical polymerization of the acryloyl group in the aliphatic polyester resin (A) during the reaction, it is preferable to add a polymerization inhibitor such as hydroquinone, hydroquinone monomethyl ether or 2,6-di-tert-butyl-4-methylphenol (BHT) prior to the reaction. Thus, the reaction product (i) having urethane bonds formed by the reaction of hydroxyl groups in the component (A) with isocyanato groups in the component (B) is obtained (urethane bond formation). Subsequently, the reaction product (i) is reacted with the aminosilane compound (C) having the formula (II): In the reaction, the acryloyl groups in the reaction product (i) are reacted with the amino group in the aminosilane compound (C). In the formula (II), R 3 is a bivalent hydrocarbon group having 1 to 10 carbon atoms, concretely, is a linear or branched alkylene group having 1 to 10 carbon atoms such as a trimethylene group or hexamethylene group, a cycloalkylene group having 6 to 10 carbon atoms such as a cyclohexylene group, an arylene group having 6 to 10 carbon atoms such as a phenylene group or an aralkylene group having 7 to 10 carbon atoms such as a xylylene group, R 4 is an alkyl group having 1 to 10 carbon atoms such as a methyl group or ethyl group, each X 2 is a hydrolyzable group, and n is 1, 2 or 3. Examples of the hydrolyzable group X 2 are, for instance, a halogen atom, an alkoxy group such as a methoxy group, ethoxy group or butoxy group, an acyloxy group such as an acetoxy group, an aminoxy group, a phenoxy group, a thioalkoxy group, or an amino group. Among them, the alkoxy group and the acyloxy group are preferable from the viewpoints of the safety and smelling. Examples of the aminosilane compound (C) are, for instance 3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane and 3-aminopropylmethyldimethoxysilane. It is preferable that the aminosilane compound (C) is reacted with the reaction product (i) in an amount of 0.7 to 1 mole, more preferably from 0.8 to 1 mole, per mole of acryloyl groups in the reaction product (i). When the amount of the aminosilane compound (C) is less than 0.7 mole per mole of acryloyl groups in the reaction product (i), remaining non-reacted acryloyl groups tend to lower the curability of the curable resin. On the other hand, when the amount of the aminosilane compound (C) is more than 1 mole, there remains non-reacted aminosilane compound. The reaction is conducted, for instance, at a temperature of 10° to 100°C for 0.5 to 2 hours. In the above-mentioned reaction, 5 to 90 % by mole of the aminosilane compound (C) can be replaced by a mercaptosilane compound such as γ-mercaptopropyltrimethoxysilane. Thus, the aminosilane-modified resin (ii) is obtained by an addition reaction of the amino groups in component (C) to acryloyl groups in the reaction product (i) (Michael addition reaction). Finally, the amino groups in the thus obtained reaction product, namely, the aminosilane-modified resin (ii) are reacted with the monofunctional organic isocyanate compound (D-1) and/or the polyfunctional organic isocyanate compound (D-2). The monofunctional organic isocyanate compound (D-1) has the formula (III): OCN-R 5 In the formula (III), R 5 is a linear or branched alkyl group having 1 to 25 carbon atoms such as a hexyl group, octyl group, dodecyl group or stearyl group, a cycloalkyl group having 6 to 25 carbon atoms such as a cyclohexyl group, an aryl group having 6 to 25 carbon atoms such as a phenyl group, an aralkyl group having 6 to 25 carbon atoms such as a benzyl group, the group of the formula: or the group of the formula: Examples of the monofunctional isocyanate compound (D-1) are, for instance, n-butyl isocyanate, n-dodecyl isocyanate, stearyl isocyanate, cyclohexyl isocyanate, phenyl isocyanate, benzyl isocyanate, 3-isocyanatopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane and 3-isocyanatopropylmethyldimethoxysilane. Any polyfunctional organic isocyanate compound (D-2) can be used without particular limitations so long as the isocyanate compound (D-2) has at least two isocyanato groups in one molecule. The preferable polyfunctional isocyanate compounds (D-2) are isocyanate compound having 2 to 3 isocyanato groups in the molecule. Typical examples of the polyfunctional organic isocyanate compound (D-2) are, for instance, hexamethylene diisocyanate, isophorone diisocyanate, 2, 4-toluylene diisocyanate, diphenylmethane-4,4'-diisocyanate, dicyclohexylmethane-4,4 '-diisocyanate, xylylene diisocyanate, lysine methyl ester diisocyanate, and a trimer of isophorone diisocyanate (isocyanurate). When the curable resin of the present invention is used in exterior coatings, use of an aliphatic isocyanate or alicyclic isocyanate is preferable to the use of an aromatic isocyanate, from the viewpoints of weatherability and yellowing resistance. When a hydrolyzable silyl group-containing monofunctional isocyanate such as 3-isocyanatopropyltrimethoxysilane is used as the component (D-1), one further hydrolyzable silyl group is introduced into the curable resin. Also, when the polyfunctional organic isocyanate compound (D-2) such as a difunctional isocyanate is used, two molecules of the aminosilane-modified resin (ii) are linked. Accordingly, the monofunctional organic isocyanate compound (D-1) and the polyfunctional organic isocyanate compound (D-2) can be suitably used alone or as a mixture thereof depending on the purposes. It is preferable that the isocyanate compound (D-1) or (D-2) is reacted with the aminosilane-modified resin (ii) in an amount of 0.7 to 1 gram-equivalent, more preferably from 0.8 to 1 gram-equivalent, of active hydrogen of amino groups in the aminosilane-modified resin (ii). When the amount of the isocyanate compound is less than 0.7 gram-equivalent of active hydrogen of amino groups in the aminosilane-modified resin (ii), the storage stability (increase of viscosity due to moisture) and the yellowing resistance tend to lower. On the other hand, when the amount of the isocyanate compound is more than 1.0 gram-equivalent, free isocyanate will remain. The reaction is conducted in the substantial absence of water, and it can easily and exothermically proceed by only adding the monofunctional isocyanate (D-1) and/or the polyfunctional isocyanate (D-2) to the aminosilane-modified resin (ii) or a solution containing the resin (ii) at a temperature of room temperature to 60°C. As mentioned above, the curable resin of the present invention is prepared by a series of addition reactions (urethane bond formation → Michael addition reaction → urea bond formation). It is not necessary to isolate the product of each addition reaction from the reaction mixture, and the desired curable resin can be easily obtained by controlling the amounts of the reactants and the reaction temperature. In the above-mentioned reactions, it is not necessary to use a solvent. In order to control the reaction temperature or the viscosity, a solvent can be used. As the solvent, a solvent having no active hydrogen such as heptane, toluene, xylene, butyl acetate or methyl ethyl ketone is used. Particularly, if a raw material contains water, it is possible to previously remove water by azeotropic dehydration, using heptane or toluene. The thus obtained curable resin has, in one molecule, an aliphatic polyester chain, at least one, preferably from 1 to 3, urethane bonds and at least one, preferably from 1 to 3, N,N,N'-trisubstituted urea bonds in its backbone and has at least two, preferable from 2 to 6, more preferably from 2 to 4, hydrolyzable silyl groups at the polymer ends. The curable resin has a number average molecular weight of 600 to 6000, preferably from 700 to 4000. When the number average molecular weight is less than 600, the flexibility becomes poor. On the other hand, when the number average molecular weight is more than 6000, the acid resistance and the scratch resistance become poor. The curable resin of the present invention is excellent in flexibility due to the aliphatic polyester chain, is excellent in solvent resistance due to the urethane bonds and the N,N,N'-trisubstituted urea bonds, is low in resin viscosity, and is excellent in compatibility with other polymers. Accordingly, the curable resin of the present invention is most useful as a high solids top coating used for automobiles. Also the top coating containing the curable resin of the present invention is more excellent in acid rain resistance and scratch resistance, which have recently become of more importance for automobile top coatings than the acrylic-melamine coatings which have been generally and widely used. It could be considered that the reason why the curable resin of the present invention is excellent in acid rain resistance is that the coating is not cured (crosslinked) by the formation of ether bonds like in the case of the acrylic-melamine coatings, but cured by the formation of siloxane bonds which are excellent in chemical resistance. Also, though the reason for a good scratch resistance of the curable resin is not clear, it can be considered that the backbone of the curable resin is excellent in elastic restoration. The compositions of the present invention comprise a vinyl polymer (a) containing in one molecule at least one, preferably from 2 to 10, silyl groups having the formula (IV): and the curable resin (b) as mentioned above. In the formula (IV), R 6 and R 7 are the same or different and each is a hydrogen atom or a hydrocarbon group having 1 to 10 carbon atoms selected from an alkyl group such as a methyl group or ethyl group, an aryl group such as a phenyl group and an aralkyl group such as a benzyl group; each Y is a halogen atom or an alkoxy group such as a methoxy group, ethoxy group or butoxy group, an acyloxy group such as an acetoxy group, a thioalkoxy group, an aminoxy group, a phenoxy group or an amino group, and at least one Y is an alkoxy group or phenoxy group; and a is 1, 2 or 3. Examples of the vinyl monomer, constituting the vinyl polymer (a) are for instance, methacrylic monomers such as methyl methacrylate, n-butyl methacrylate or iso-butyl methacrylate, acrylic monomers such as n-butyl acrylate or 2-ethylhexyl acrylate, hydrolyzable silyl group-containing vinyl monomers such as γ-trimethoxysilylpropyl methacrylate, styrene and acrylamide. The vinyl polymer having at least one silyl group (a) can be prepared for instance, as described in Japanese Unexamined Patent Publication No. 54-36395. The composition of the present invention comprises 5 to 95 parts by weight, preferably from 10 to 70 parts by weight, of the vinyl polymer (a) and 95 to 5 parts by weight, preferably from 30 to 90 parts by weight, of the curable resin (b), the total amount of the curable resin (b) and the vinyl polymer (a) being 100 parts by weight. When the amount of the vinyl polymer is less than 5 parts by weight, it tends to lower the effect for improving the acid resistance. On the other hand, when the amount of the vinyl polymer (a) is more than 95 parts by weight, it tends to lower the effect for improving the scratch resistance. The composition of the present invention can further contain other resins or can be blended with other paints. For instance, when an epoxy resin, a polyester alkyd resin or an acrylic polyol resin is blended with the composition of the present invention, flexibility and solvent resistance are improved. Also, when a melamine-alkyd coating composition or a melamine-acrylic coating composition is blended with the composition of the present invention, acid rain resistance and scratch resistance are improved. It is preferable that the other component is blended with the composition of the present invention in an amount of not more than 50 parts by weight, based on 100 parts by weight of the total resin solids from the viewpoints of the characteristic physical properties of the composition of the present invention. The composition of the present invention can further contain known additives such as solvents, dehydrating agents, antoxidants, levelling agents or pigments. The curable resin or the composition containing the resin of the present invention can be cured by using a known curing catalyst. Examples of the curing catalyst are, for instance, organotin compounds such as dibutyltin dilaurate or tin octoate, and acid compounds such as p-toluenesulfonic acid or acid phosphoric esters, amine compounds such as ethylene diamine, isophorone diamine or N,N-dimethyldodecylamine. It is preferable that the amount of the curing catalyst is from 0.005 to 10 parts by weight, more preferably from 0.1 to 8 parts by weight, based on 100 parts by weight of the curable resin (b). The curing of the curable resin (b) proceeds rapidly at room temperature even without using a curing catalyst. The curable resin (b) can be cured more rapidly by heating to 80° to 160°C. The curable resin (b) and the composition of the present invention are excellent in acid rain resistance, scratch resistance, flexibility and weatherability and are particularly suitable for use as exterior coating agents. The present invention is more specifically described and explained by means of the following Examples in which all percents and parts are by weight unless otherwise noted. It is to be understood that the present invention is not limited to the Examples. Reference Example 1 [Preparation of hydrolyzable silyl group-containing acrylic copolymer] A reactor equipped with a stirrer, a thermometer, a nitrogen inlet tube and a condenser was charged with 200 g of "Solvesso 100" commercially available from Exxon Company and the temperature was elevated to 110°C. Then, a mixture of 177 g of n-butyl methacrylate, 177 g of methyl methacrylate, 240 g of trimethoxysilylpropyl methacrylate, 6 g of acrylamide, 32 g azobisisobutyronitrile and 64 g of xylene was continuously added to the reactor for 5 hours with stirring under nitrogen gas. Then, a mixture of 4 g of azobisisobutyronitrile and 40 g of xylene was continuously added for 2 hours, and the post-polymerization was conducted for 1 hour. The obtained reaction mixture was diluted with xylene to give a hydrolyzable silyl group-containing acrylic copolymer solution (1) having a solid concentration of 60 %. The obtained silyl group-containing acrylic copolymer had a number average molecular weight of 3,000 and a solution viscosity of 200 cps (at 23°C ). Example 1 A reactor equipped with a stirrer, a thermometer, a nitrogen inlet tube and a condenser was charged with 284 g of Placcel FA-3 (commercially available from Daicel Chemical Industries, Ltd., polycaprolactone acrylate, M n: 458), 127 g of 3-isocyanatopropyltrimethoxysilane and 200 g of xylene and the mixture was reacted at 100°C for 2 hours with stirring under nitrogen gas. In the infrared absorption spectrum (IR) of the obtained product (i), the absorption band of NCO (2270 cm -1 ) had disappeared completely and the absorption of the urethane bond (1540 cm -1 ) was seen. Also, the absorption of the acryloyl group (1630 to 1640 cm -1 ) remained. The IR spectrum of the reaction product (i) is shown in Fig. 1. Then, after the reaction temperature dropped to 30°C, 116 g of 3-aminopropyltrimethoxysilane was added to the reactor and the reaction was conducted for 1 hour, and was further continued at 60°C for 30 minutes. In IR of the reaction product (ii), the absorption of the acryloyl group (1630 to 1640 cm -1 ) had disappeared. The IR spectrum of the reaction product (ii) is shown in Fig. 2. Subsequently, after the reaction temperature dropped to 30°C, 73 g of cyclohexyl isocyanate was gradually added through a dropping funnel, and the reaction was conducted at 60°C for 30 minutes after completing the addition. The reaction product was diluted with xylene to give a curable resin solution (1) having a solid concentration of 60 %. In the IR of the obtained curable resin, the absorption of the urea bond (1640 cm -1 ) was seen. The IR spectrum of the curable resin is shown in Fig. 3. The curable resin had a number average molecular weight of 1000, measured by gel permeation chromatography (GPC). There was mixed 100 parts of the curable resin solution (1) (solid concentration: 60 %) with 0.5 part of dibutyltin dilaurate, and the mixture was diluted with "Solvesso 100" to give a clear coating having a suitable viscosity for use as a coating. A black melamine-acrylic enamel was spray-coated on a plate (30 cm x 10 cm x 0.08 mm) coated with an electrodeposition intermediate coating so as to give a dry film thickness of 10 to 15 µm, the film was allowed to stand for 1 minute, then the clear coating was spray-coated on the film so as to give a dry film thickness of 40 to 50 µm. The film was allowed to stand for 5 minutes, it was baked at 140°C for 30 minutes, and it was allowed to stand at room temperature for one day. The following physical properties were determined at the obtained test piece and the curable resin solution (1), respectively. [Solution viscosity] The viscosity of the curable resin solution having a solid concentration of 60 % was measured at 23°C by using a Brookfield viscometer. [Pencil hardness] The pencil hardness of the film was measured according to Japanese Industrial Standards (JIS) K 5400. [Acid resistance] The 20°-gloss of the film was measured. The test piece was dipped in a 1 % solution of sulfuric acid for 24 hours, and then the 20°-gloss of the film was measured again. The gloss retention is characterized by the following equation: Gloss retention = 20 o -gloss of the film after dipping 20 o -gloss of the film before dipping x 100 % The higher the gloss retention, the more excellent the acid resistance. [Scratch resistance] The test piece was horizontally set, and an abrasive composed of 1.2 % of a loam having an abrasive grain size of # 8 provided in JIS, 1.2 % of a loam having an abrasive grain size of # 11 provided in JIS, 0.6 % of kaoline, 1.0 % of a neutral detergent and 96.0 % of water was applied onto the coating film of the test piece. A weight (diameter of contact surface: 5 cm a load: 22 g/cm 2 ) covered with a craft paper was stroked against the surface of the coating film. The lightness of the film was measured before stroking and after 12 strokes and 100 strokes by using a differential colorimeter. The scratch resistance is estimated according to the difference (ΔL) between the lightness of the film which was not stroked and the lightness of the film which was stroked 12 times or 100 times. The smaller the ΔL, the more excellent the scratch resistance. [Bending by mandrel] A test piece (30 cm x 10 cm x 0.08 mm) is prepared by coating a mild steel plate with the curable resin or composition so as to get a dry film thickness of 50 µm. The test piece is bended by using a mandrel tester commercially available from Ericksen Corp. and the length (cm) of crack is measured. The results are shown in Table 1. Example 2 The procedure of Example 1 was repeated except that 49 g of hexamethylene diisocyanate was used instead of 73 g of cyclohexyl isocyanate to give a curable resin solution (2) containing a solid concentration of 60 %. In the IR of the curable resin, the absorption band of the urea group (1640 cm -1 ) was seen. The curable resin had a number average molecular weight of 1500 measured by GPC. The physical properties of the curable resin solution (2) and the film were measured in the same manner as in Example 1. The results are shown in Table 1. Example 3 The procedure of Example 1 was repeated except that 98 g of tri(6-isocyanatohexyl)isocyanurate was used instead of 73 g of cyclohexyl isocyanate to give a curable resin solution (3) having a solid concentration of 60 %. In the IR of the obtained curable resin, the absorption band of the urea group (1640 cm -1 ) was seen. The curable resin had a number average molecular weight of 3,000 measured by GPC. The test piece was prepared in the same manner as in Example 1. As to the obtained film and the resin solution (3), the physical properties were measured in the same manner as in Example 1. The results are shown in Table 1. Example 4 A reactor equipped with a stirrer, a thermometer, a nitrogen inlet tube and a condenser was charged with 407.2 g of polymethylvalerolactone acrylate (commercially available from Kabushiki Kaisha Kuraray, M n=1080), 77.3 g of 3-isocyanatopropyltrimethoxysilane and 200 g of xylene, and the reaction was conducted at 100°C for 2 hours with stirring under nitrogen gas. In the IR of the reaction product, the NCO-absorption (2270 cm -1 ) had completely disappeared, the absorption of the urethane bond was seen, and the absorption of the acryloyl group (1630 to 1640 cm -1 ) remained. Then, the reaction temperature was dropped to 30°C, 70.9 g of 3-aminopropyltrimethoxysilane were added, and the reaction was conducted for 1 hour and then was continued at 60°C for 30 minutes. In the IR of the reaction product, the absorption of the acryloyl group (1630 to 1640 cm -1 ) had disappeared. Then, the reaction temperature was dropped to 30°C, and 44.6 g of cyclohexylisocyanate were gradually added through a dropping funnel to the reaction system. After completing the addition, the reaction was conducted at 60°C for 30 minutes and the reaction product was diluted with xylene to give a curable resin solution (4) having a solids concentration of 60 %. In the IR of the obtained curable resin, the absorption of the urea bond (1640 cm -1 ) was seen. The curable resin had a number average molecular weight of 1600 measured by GPC. The test piece was prepared in the same manner as in Example 1. The physical properties of the film and the curable resin solution (4) were measured in the same manner as in Example 1. The results are shown in Table 1. Comparative Example 1 A test price was prepared in the same manner as in Example 1 except that a commercial melamine-acrylic clear coating was used instead of the clear coating obtained in Example 1. The physical properties of the film were measured in the same manner as in Example 1. The results are shown in Table 1. Examples 5 to 7 and Comparative Example 2 The curable resin solution (1) was mixed with the hydrolyzable silyl group-containing acrylic copolymer obtained in Reference Example 1 in amounts shown in Table 2 to give a composition. The test piece was prepared in the same manner as in Example 1 except that the obtained composition was used instead of the curable resin. The physical properties of the film and the resin solution were measured in the same manner as in Example 1. The results are shown in Table 2. In addition to the ingredients used in the Examples, other ingredients can be used in the Examples as set forth in the specification to obtain substantially the same results.

Claims: A curable resin having a number average molecular weight of 600 to 6000 and at least two hydrolyzable silyl groups in one molecule, which is obtainable by (i) reacting an aliphatic polyester resin (A) having, in one molecule, both an acryloyl group and an alcoholic hydroxyl group on the polymer ends, with an isocyanate silane compound (B) having the formula (I): wherein R 1 is a bivalent hydrocarbon group having 1 to 10 carbon atoms selected from an alkylene group, a C 6 -C 10 -cycloalkylene group, an arylene group and an aralkylene group, R 2 is an alkyl group having 1 to 10 carbon atoms, each X 1 is a hydrolyzable group and m is 1, 2 or 3 to give a reaction product (i); (ii) reacting the obtained reaction product (i) with an aminosilane compound (C) having the formula (II): wherein R 3 is a bivalent hydrocarbon group having 1 to 10 carbon atoms selected from an alkylene group, a C 6 -C 10 -cycloalkylene group, an arylene group and an aralkylene group, R 4 is an alkyl group having 1 to 10 carbon atoms, each X 2 is a hydrolyzable group and n is 1, 2 or 3, or a mixture of 10 to 95 % by mole of said aminosilane compound (C) and 5 to 90 % by mole of a mercaptosilane, whereby the amino group in said aminosilane compound (C) is reacted with said acryloyl group in said reaction product (i) to give an aminosilane-modified resin (ii), and (iii)reacting the aminosilane-modified resin (ii) with a monofunctional organic isocyanate compound (D-1) having the formula (III) OCN-R 5 wherein R 5 is a monovalent hydrocarbon group having 1 to 25 carbon atoms selected from an alkyl group, a C 6 -C 25 cycloalkyl group, an aryl group and an aralkyl group, a group of the formula: or a group of the formula : and/or a polyfunctional organic isocyanate compound (D-2) in the substantial absence of water. The curable resin of Claim 1, wherein the backbone of said curable resin is mainly polycaprolactone. The curable resin of Claim 1, wherein the backbone of said curable resin is mainly polyvalerolactone. The curable resin of Claim 1, wherein, in the formula (I), the group X 1 is a methoxy group and the integer m is 3. The curable resin of Claim 1, wherein, in the formula (II), the group X 2 is a methoxy group and the integer n is 3. The curable resin of Claim 1, wherein, in the formula (I), the group X 1 is a methyl group and the integer m is 3 and, in the formula (II), the group X 2 is a methoxy group and the integer n is 3. The curable resin of Claim 1, wherein, in the formula (I), the group R 2 is a methyl group, the group X 1 is a methoxy group and the integer m is 2. The curable resin of Claim 1, wherein, in the formula (II), the group R 4 is a methyl group, the group X 2 is a methoxy group and the integer n is 2. The curable resin of Claim 1, wherein, in the formula (I), the group R 2 is a methyl group, the group X 1 is a methoxy group and the integer m is 2 and, in the formula (II), the group R 4 is a methyl group, the group X 2 is a methoxy group and the integer n is 2. A composition comprising: (a) 5 to 95 parts by weight of a silyl group-containing vinyl polymer having, in one molecule, at least one silyl group represented by the formula (IV): wherein R 6 and R 7 are the same or different and each is a hydrogen atom or a monovalent hydrocarbon group having 1 to 10 carbon atoms selected from an alkyl group, an aryl group and an aralkyl group, each Y is a halogen atom, an alkoxy group, an acyloxy group, an aminoxy group, a phenoxy group, a thioalkoxy group or an amino group and at least one Y is an alkoxy group or phenoxy group, a is 1, 2 or 3 and (b) 95 to 5 parts by weight of a curable resin according to Claim 1, the total amount of the curable resin (b) and the vinyl polymer (a) being 100 parts by weight.

Inventors: FURUKAWA HISAO, KAWAGUCHI HIROTOSHI, NUMBU TOSHIRO, OHNARI HIDEYUKI, OKIMURA YOSHIHIKO, FURUKAWA, HISAO, KAWAGUCHI, HIROTOSHI, NUMBU, TOSHIRO, OHNARI, HIDEYUKI, OKIMURA, YOSHIHIKO
Applicants: KANEGAFUCHI CHEMICAL IND, KANEGAFUCHI KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1991
Main classification: C08G63
IPC codes: C08L67, C08G18, C08G63