Solid golf ball

Abstract: The present invention provides a solid golf ball containing at least one rubber portion formed from a rubber composition comprising a base rubber, aco-crosslinking agent and an organic peroxide characterized in that said base rubber is a mixture of (A) a solid polybutadiene rubber containing cis-1,4 bonds in an amount of at least 40 %, and (B) at least one of a liquid polybutadiene rubber or a liquid isoprene-butadiene copolymer rubber.

Description: The present invention relates to a golf ball, particularly a one-piece solid golf ball. Golf balls are classified into two types. One is thread wound golf balls which comprise a thread wound core and a cover covering the core, and the other is solid golf balls, e.g. one-piece solid golf balls which are integrally composed of rubber and two solid golf balls which are composed of a rubber core and a cover thereon. Solid golf balls contain at least one rubber portion. The rubber portion has been prepared from a rubber composition which mainly contains as base rubber butadiene rubber or a mixture of butadiene rubber and the other rubber (e.g. natural rubber and isoprene rubber). The base rubbers, however, have some problems in processability (for example, mixing process or extruding process), thus resulting in poor production efficiency. These problems are more serious when a polybutadiene having high Mooney viscosity or narrow molecular weight distribution is used to improve the physical properties of golf balls. JP60182969A (Fujikura Rubber Works K K) discloses a solid rubber golf ball which comprises a polybutadiene and a liquid isoprene with filler, reformer, colourant and antioxidant. JP61196980A (Yokohama Rubber K K) discloses a rubber composition for golf balls which comprises a polybutadiene, a polyamide resin, a liquid diene rubber, an unsaturated carboxylic-acid and a metal oxide. The inventors have found that a rubber composition containing as a base rubber a mixture of a solid polybutadiene rubber and a specific liquid polybutadiene rubber significantly improves the processability and surprisingly enhances the physical properties of the resulting solid golf balls (e.g. durability, impact resilience and hit feeling). Accordingly the present invention provides a solid golf ball containing at least one rubber portion formed from a rubber composition comprising a base rubber, a co-crosslinking agent and an organic peroxide wherein the base rubber is a mixture of (A) a solid polybutadiene rubber containing cis-1,4 bonds in an amount of at least 40%, and (B) at least one of a liquid polybutadiene rubber or liquid isoprene-butadiene copolymer rubber wherein the liquid rubber component (B) has an average molecular weight of 1,000 to 50,000 and the rubber composition does not include polyamide resin or liquid isoprene. The polybutadien rubber (A) employed in the present invention is a solid at room temperature and contains cis-1,4-bonds in an amount of at least 40%, preferably at least 80%. If the content of the cis-1,4 bonds is less than 40%, impact resilience is poor. It is preferred that the solid polybutadiene rubber (A) has a high Mooney viscosity or a narrow or sharp molecular weight distribution, especially a Mooney viscosity (ML₁+₄ 100°C) of 43 to 90 or a ratio of weight average molecular weight/number average molecular weight (Mw/Mn) of 4.0 or less. The preferred solid polybutadiene (A) exhibits superior technical effects when combined with the liquid rubber component (B). The polybutadiene (A) is commercially available in the tradenames of Ubepole BR 150 L or Ubepole BR 360L (both Ube Industries, Ltd.), BUNA CB or BUNA CB 10 (both Bayer AG). The rubber component (B) employed in the present invention is either a liquid polybutadiene rubber, a liquid isoprene-butadiene copolymer rubber, or a mixture thereof. The term "liquid" means that the rubber is flowable at room temperature. The liquid rubber component (B) has a number average molecular weight of 1,000 to 50,000. Molecular weights outside the range deteriorate compression and impact resilience of the resulting golf balls or have poor processability. The liquid isoprene-butadiene copolymer rubber preferably contains at least 50% by weight of the butadience component. If the isoprene component is more than 50% by weight, crosslinking efficiency is poor and the physical properties of the resulting rubber are poor. The rubber component (B) is commercially available, for example the liquid polybutadiene is available from Nippon Oil Co., Ltd. as Nisseki Polybutadiene B-3000 and the liquid isoprene-butadiene copolymer rubber is available from Kuraray Co., Ltd. as Kuraprene LIR-390. In the base rubber, it is preferred that a weight ratio of the polybutadiene component (A) / the liquid rubber component (B) is in the range of from 98/2 to 75/25, more preferably 95/5 to 80/20. If the liquid rubber component (B) is less than 2 parts, the technical effects of the present invention are not attained. If it is more than 25 parts, the obtained rubber composition is sticky and adversely makes processability poor. The base rubber of the present invention is mainly composed of the above mentioned two rubber components (A) and (B), but other diene rubbers, such as EPDM, styrene-butadiene rubber, polyisoprene rubber, natural rubber and the like may be added thereto. Polyamide resin and liquid isoprene are excluded from the rubber composition of the golf ball described and claimed herein. The other diene rubber may be present in the base rubber in an amount of 40% by weight or less. The co-crosslinking agent of the present invention can be unsaturated carboxylic acids or metal salts thereof. Examples of the unsaturated carboxylic acids and metal salts thereof are acrylic acid, methacrylic acid, and divalent metal salts thereof (e.g. zinc salts), and mixtures thereof. The co-crosslinking agent is present in the range of from 15-60 parts by weight based on 100 parts by weight of the base rubber. In a further aspect of the present invention the liquid rubber component (B) does not have terminal carboxyl groups. The organic peroxide of the present invention can be one of more of those which are used in this field as a polymerization initiator, including at least one of dicumyl peroxide, 1, 1-bis(t-butylperoxy)-3, 3,5-trimethylcyclohexane, 2,5-dimethyl-2, 5-di(t-butylperoxy) hexane or di-t-butylperoxide. Preferred is dicumyl peroxide. The organic peroxide may be present in the rubber composition in the range of from 0.3 to 3.0 parts by weight, preferably 1.0 to 2.5 pats by weight based on 100 parts by weight of the base rubber. The rubber composition of the present invention may further contain fillers to control the specific gravity of the resulting golf balls. Typical examples of the fillers are zinc oxide, barium sulfate, calcium carbonate, silicate hydrate. The rubber composition may also contain antioxidants, chain transfer agents, or stabilizers to enhance the performance of the resulting golf ball. The rubber composition of the present invention can be prepared by mixing the above mentioned components, using a roll, a kneader, or a Branbury mixer. Mixing temperature and time are parameters known by those skilled in the art. The solid golf balls of the present invention may be obtained by vulcanizing the rubber composition in a mold and optionally covering it with a cover material (e.g. ionomer resin). Vulcanization may be generally conducted at a temperature of 140 to 180 °C for 15 to 55 minutes. The rubber composition of the present invention can be easily processed or treated by mixing the polybutadiene rubber with the specific liquid rubber component (B). It is surprising that the golf balls obtained from the rubber composition have excellent impact durability and hit feeling. EXAMPLES The present invention is illustrated by the following Examples. Examples 1-7 and Comparative Examples 1 and 2 A rubber composition was prepared from the ingredients shown in Table 1, using a kneader and a roller, and then vulcanized in a mold at 168 °C for 25 minutes to obtain a one-piece solid golf ball. The processability of the rubber composition was determined and the result is shown in Table 1. The resulting golf ball was subjected to a measurement of physical properties (ball weight, compression, impact durability and hit feeling) and the results are shown in Table 1.

Claims: A solid golf ball containing at least one rubber portion formed from a rubber composition comprising a base rubber, a co-crosslinking agent and an organic peroxide, wherein the base rubber is a mixture of (A) a solid polybutadiene rubber containing cis-1,4 bonds in an amount of at least 40 %, and (B) at least one of a liquid polybutadiene rubber or a liquid isoprene-butadiene copolymer rubber characterized in that the liquid rubber component (B) has an average molecular weight of 1,000 to 50,000 and the rubber composition does not include polyamide resin or liquid isoprene. A solid golf ball as claimed in Claim 1 wherein the polybutadiene rubber (A) has a Mooney viscosity (ML₁+₄ 100 °C of 43 to 90 and a ratio of weight average molecular weight/number average molecular weight (Mw/Mn) of 4.0 or less. A solid golf ball as claimed in any one of the preceding claims wherein the liquid rubber component (B) does not have terminal carboxyl groups. A solid golf ball as claimed in any one of the preceding claims wherein the weight ratio of polybutadiene component (A) / liquid rubber component (B) is in the range of from 98/2 to 72/25. A solid golf ball as claimed in any one of the preceding claims wherein the cross-linking agent is at least one of acrylic acid, metacrylic acid or a divalent metal salt thereof. A solid golf ball as claimed in any one of the preceding claims wherein the cross-linking agent is present in the range of from 15 to 60 parts by weight based on 100 parts by weight of the base rubber. A solid golf ball as claimed in any one of the preceding claims wherein the organic peroxide is at least one of dicumyl peroxide, 1,1-bis(t-butylperoxy)-3,3,5-trimethylcyclohexane, 2,5-dimethyl-2,5-di-(t-butylperoxy)hexane or di-t-butylperoxide. A solid golf ball as claimed in any one of the preceding claims wherein the organic peroxide is present in the rubber composition in the range from 0.3 to 3.0 parts by weight based on 100 parts by weight of the base rubber.

Inventors: HAMADA AKIHIKO, HIRAOKA HIDENORI, HAMADA, AKIHIKO, HIRAOKA, HIDENORI
Applicants: SUMITOMO RUBBER IND, SUMITOMO RUBBER INDUSTRIES, CO. LTD
Application year: 1991
Main classification: A63B37
IPC codes: A63B37, C08L9