SEPARATOR AND ITS MANUFACTURING METHOD

Abstract: A separator interposed between the laminated body of power-generating components comprising a fuel electrode, and electrolyte layer, and an air electrode for supplying a fuel gas to the fuel electrode and an oxidizing agent gas to the air electrode separately, with the passages of the gases isolated from each other. Current collecting plates and edge plates constitute wall faces and its peripheries in contact with the fuel electrode in the passage of the fuel gas and with the air electrode in the passage of the oxidizing agent gas respectively. The plates are made of thin plate materials exhibiting high flexibility. Since the edge plates of the thin plate material can bend easily in a direction in which the power-generating components are laminated, even if the differences in level due to the viriations of the current collecting plate, the support thereof and the edge plate are produced upon manufacturing, the differences in level are eliminated by the bent of the plates. Thus, the contact of the plates with the power-generating components can be uniformalized and local forces can be prevented from exerting on the power-generating componets. A method of manufacturing the separator is characterized in that a metal die and an outer die surrounding the metal die are placed on a press head, a thin plate of a raw material and a flexible plate having a predetermined hardness are put on each other on the metal die, and the thin plate is pressed and formed through the flexible plate. Since when the current collecting plate and the edge plate are manufactured by the press working, no cutting work and no joining work by welding, etc. are required, residual stress caused bt these works is not produced. Thereby, the residual stress, if exists, is released by the temperature rise accompanied by operating a fuel cell, and the members are not deformed. Further, this manufacturing method is excellent in mass productivity.

Description: Technical Field The present invention relates to a fuel cell, particularly to a separator for leading fuel gas and air respectively to a fuel electrode and an air electrode of a molten carbonate fuel cell, which holds high operating temperature and has high efficiency, and for supporting an active component thereof. Related Art Fuel cells are means for directly providing electricity by using electrochemical reactions which take place on electrodes. To continuously perform such an electrochemical reaction, a fuel gas and an oxidant gas have to be separately and respectively supplied to a fuel electrode and an air electrode, these electrodes facing each other with an electrolyte layer. A functional member for use in accomplishing such an object is a separator. When a fuel cell is constructed by laminating a plurality of single cells comprising the fuel electrode, the electrolyte layer, and the air electrode, the separators are disposed between the single cells so as to separately lead the fuel gas and air as the oxidant gas respectively to the fuel electrode and the air electrode. In addition, the separators support the single cells which are laminated and electrically connect in series the single cells which are adjacently disposed. Figs. 7 and 8 show an example of a fuel cell where single cells are laminated. The fuel cells can be roughly categorized by the directions of flows of the fuel gas and the oxidant gas as (1) parallel flow type where the fuel gas and the oxidant gas are flowed in the same direction, (2) opposed flow type where the fuel gas and the oxidant gas are flowed in the opposed directions to each other, and (3) perpendicular flow type where the fuel gas and the oxidant gas are flowed in the perpendicular directions to each other. The construction of each member for use in the parallel flow type is the same as that in the opposed flow type. An single cell 1 is a laminate which is mainly composed of a electrolyte layer 2, an anode 3 contacted intimately on one surface thereof, and a cathode 4 contacted intimately on the other surface thereof. A separator 5 is contacted intimately on the single cell 1. The fuel cell is constructed by alternately laminating the single cells 1. The separator 5 is composed of an interconnector 6, an anode current collector 7, a cathode current collector 8, an anode current collector support 9, a cathode current collector support 10, an anode edge plate 11, and a cathode edge plate 12. The interconnector 6 is constructed in a plate shape and disposed nearly at the center of the thickness of the separator 5. The interconnector 6 separates the flow of the fuel gas 13 from that of the oxidant gas 14. In addition, the anode current collector 7 and the cathode current collector 8 are also constructed in plate shapes. The anode current collector 7 and the cathode current collector 8 have large numbers of small holes 7a and 8a, respectively. The anode current collector 7 and the cathode current collector 8, which are disposed on both the sides of the interconnector 6, equally conduct the electricity which takes place at the single cell 1 to the outside thereof. In addition, the anode current collector 7 and the cathode current collector 8 also support the full surface of the single cell 1 with equal surface pressures. The anode current collector support 9, which is in a corrugated plate shape, is disposed between the anode current collector 7 and the interconnector 6. In addition, the cathode current collector support 10, which is in a corrugated plate shape, is disposed between the cathode current collector 8 and the interconnector 6. Moreover, the anode edge plate 11 and the cathode edge plate 12 are disposed between the interconnector 6 and the single cell 1 so as to support the edge portion of the interconnector 6. The anode current collector support 9, the cathode current collector support 10, the anode edge plate 11, and the cathode edge plate 12 produce spaces between the interconnector 6 and the anode current collector 7 and between the interconnector 6 and the cathode current collector 8 so as to flow the fuel gas 13 and the oxidant gas 14, respectively. Since the anode current collector 7, the cathode current collector 8, the anode current collector support 9, the cathode current collector support 10, and the interconnector 6 electrically connect each of the adjacent single cells 1 in series, they have to be made of metals. Thus, conventionally, the whole separator 5 is constructed of a metal so as to readily connect and assemble each member and to decrease the difference of thermal expansion thereof. To decrease the electric resistance of the separator 5, thin plates are used for the anode current collector 7, the cathode current collector 8, and the interconnector 6. In addition, from the standpoint of productivity, the anode current collector support 9 and the cathode current collector support 10 are conventionally formed by using thin plates. Generally, the separators 5 and the single cells 1 thus constructed are alternately laminated one after the other so as to construct the cell. The cell is used as a fuel cell for generating a large amount of electric power. As was described above, one surface of the single cell 1 is in contact with the anode current collector 7 and the anode edge plate 11, while the other surface thereof is in contact with the cathode current collector 8 and the cathode edge plate 12. In this construction, it is necessary to be careful of production errors of functional elements, in particular, dimensional errors in the direction of thickness thereof. In other words, as shown in Fig. 9, when the heights of the cathode current collector 8, the cathode current collector support 10, and the cathode edge plate 12 are denoted as a, b, and c, respectively, the individual accuracies thereof should be kept high so that the relation of a + b = c is satisfied. However, an error for a tolerance takes place between the dimension of a + b and that of c. Thus, it is very difficult to remove the gap between them. For example, although the inter-connector 6 and the cathode edge plate 12 are jointed by a braze working, it is difficult to control the thickness of the brazing material. Thus, the tolerance tends to become large to some extent. The same situation takes place with respect to the anode current collector 7, the anode current collector support 9, and the anode edge plate 11. Generally, the fuel cell, which is constructed by laminating the single cells 1 and the separators 5 one after the other for predetermined times, is operated with a constant surface pressure affected on each active component 1. Thus, when difference between the current collector level and the edge plate level becomes large, a large stress locally takes place and thereby the single cell 1 may crack. In addition, when the anode 3 and the cathode 4 are not satisfactorily contacted with the anode current collector 7 and the cathode current collector 8, respectively, due to the gap of the contacted surface, the electric resistance thereof will increase, thereby loosing the electric output to some extent. Consequently, the performance of the fuel cell will be degraded. Moreover, when the anode 3 and the cathode 4 are not satisfactorily contacted with the anode edge plate 11 and the cathode edge plate 12, respectively, the fuel gas and the oxidant gas may leak. Furthermore, in the above mentioned construction, the electric connections between the anode current collector 7 and the anode current collector support 9, between the cathode current collector 8 and the cathode current collector support 10, between the anode current collector 9 and the interconnector 6, and between the cathode current collector 10 and the interconnector 6 are made by contacts of the metal surfaces. Thus, when the contacted surfaces get corroded, the electric resistance thereof increases, thereby loosing the electric output. A separator consisting of a main body and wet seal frames arranged at the periphery of the main body formed by press working of thin plates is disclosed in Patent Abstracts of Japan Vol. 13, No.312 (E-788)(3660) JP-A-01-84578. US 4514475 discloses a separator having a plate formed with unitary end portions each folded back over one side of the plate. JP-A-63-53858 discloses a separator comprising a separator plate and a punching metal mounted on the shoulder of an upper manifold. JP-A-63-53857 discloses a separator formed of an interconnecting plate sealed by edge portions. Therefore, an object of the present invention is to provide a separator where there is no difference between the dimension of an current collector and that of an edge plate in the direction of the heights thereof. Another object of the present invention is to provide a separator where the contacts of metal surfaces are decreased as small as possible, thereby preventing an electric output from being lost due to a corrosion of contacted surface. A further object of the present invention is to provide a method of manufacturing a separator suitable for mass-production, the separator where a residual stress involved in a manufacturing thereof decreases, and residual stress is released by temperature rise involved in the operation of the fuel cell, thereby preventing the distortion of members. Disclosure of the Invention A first aspect of the present invention provides a separator of molten carbonate fuel cells disposed between plate-shaped single cells having an electrolyte matrix put between an anode and a cathode, said separator forming gas flow paths for leading a fuel gas and an oxidant gas to said anode and said cathode respectively, connecting said single cells electrically to each other, said separator comprising: a plate-shaped interconnector; current collector supports disposed on both sides of said interconnector; current collectors with large numbers of holes, deposited on both sides of said interconnector, supported by said current collector supports with said gas flow paths therebetween, and being in contact with the centre of said single cell; and edge plates in contact with edge portions of said single cells, provided on periphery of said current collector, wherein said current collector and said edge plate are formed from one thin plate to be flexible, and said current collector and said edge plate are unified. Since the edge plate made of a thin plate can be readily bent in the direction where the active components are laminated, even if gaps between the current collector with the current collector support and the edge plate take place due to tolerance therebetween, either the current collector with the current collector support or the edge plate is bent and thereby the gaps are removed. Thus, the contacted surface with the active component can become flat, thereby preventing a force from being affected locally to the active component. A second aspect of the present invention provides a separator of molten carbonate fuel cells disposed between plate-shaped single cells having an electrolyte matrix put between an anode and a cathode, said separator forming gas flow paths for leading a fuel gas an oxidant gas to said anode and said cathode respectively, connecting said single cells electrically to each other, said separator comprising: a plate-shaped interconnector; current collector supports disposed on both sides of said interconnector; current collectors with large numbers of holes, deposited on both sides of said interconnector, supported by said current collector supports with said gas flow paths therebetween, and being in contact with the centre of said single cell; and edge plates in contact with edge portions of said single cells, provided on periphery of said current collector, wherein said current collector, said edge plate and said current collector support are formed from one plate to be flexible, and said current collector, said edge plate and said current collector support are unified. Since the edge plate is made of a thin plate to be flexible and is equally contacted with the surface of the active component, localized forces on it are diminished. In addition, since three plates of the interconnector and the edge plates which hold the interconnector therebetween are laminated and the outer contour portion thereof is constructed so as to be integrated and keep airtight, they can be readily and securely unified by a seal welding or the like. A third aspect of the present invention provides a method of manufacturing a separator of molten carbonate fuel cells disposed between plate-shaped single cells having an electrolyte matrix put between an anode and a cathode, said separator forming gas flow paths for leading a fuel gas and an oxidant gas to said anode and said cathode respectively, connecting said single cells electrically to each other, said separator comprising: a plate-shaped interconnector; current collector supports disposed on both sides of said interconnector; current collectors with large numbers of holes, deposited on both sides of said interconnector, supported by said current collector supports with said gas flow paths therebetween, and being in contact with the centre of said single cell; and edge plates in contact with edge portions of said single cells, provided on periphery of said current collector, said method comprising the steps of: placing a die and an outer frame for surrounding of the die on a press head; placing a thin plate and a soft plate having a predetermined hardness on said die in the order; and pressing said thin plate through application of pressure on said soft plate, by use of a press ram. When the current collector and the edge plate are made by using a press working, since a joint working by a cut working, a weld working, or the like becomes unnecessary, the residual stress which is caused by such a working can be removed. Thus, little residual stress can be released by the temperature rise involved in the operation of the fuel cell. Consequently, the distortion of the members can be prevented. In addition, high productivity can be accomplished. Brief Description of Drawings Fig. 1 is a view showing a construction of a separator of an embodiment of the present invention; Fig. 2 is a view showing an entire construction of an embodiment where a current collector, a current collector support, and an edge plate are unified; Fig. 3 is a view showing a construction of an embodiment where grooves are provided; Fig. 4 is a view describing a production method by a press working; Fig. 4' is a view describing another production method by the press working; Fig. 4" is a view describing an occurrence of a wrinkle by the press working; Fig. 4'" is a view describing the workability of the press working; Fig. 4"" is a view showing a construction of a female die for use in the press working of an edge plate with grooves; Fig. 5 is a view describing a welding method; Fig. 5' is a view describing another welding method; Fig. 6 is a view describing an etching method; Fig. 6' is a view showing a construction of a current collector where the etch working is performed; Fig. 7 is a view showing a construction of a conventional separator; Fig. 8 is a view showing a construction of the separator shown in Fig. 7; and Fig. 9 is a view describing a gap which takes place in the direction of the height of the conventional separator. Best Modes for Carrying out the Invention Now, the present invention will be described in details referring to the attached drawings. Fig. 1 shows a construction of a separator 21c in stead of a separator 5 in Fig. 8. In this separator 21c, a pair of an anode current-collector 56 and an anode edge plate 58 and a pair of a cathode current collector 57 and a cathode edge plate 59 are drawn from a single thin plate by a press work respectively so that they are integrated. The anode current collector 56 and the cathode current collector 57 have large numbers of small holes 56a and 57a for passing the fuel gas and the oxidant gas to the anode 3 and the cathode 4, respectively. In the separator 21c thus constructed, the pair of the anode current collector 56 and the anode edge plate 58, and the pair of the cathode current collector 57 and the cathode edge plate 59 are continuous. Thus, even if the anode current collector 56 and the cathode current collector 57 are deformed in any shapes, the surfaces thereof in contact with the single cell 1 are continuously curved and thereby no discontinuous surface is formed in any position. In other words, when the anode current collector 56, the anode edge plate 58, the cathode current collector 57, and the cathode edge plate 59 are separately constructed, even if the surfaces thereof in contact with the single cell 1 can be kept in the same level due to the flexibility of the constituent components, the bending angle of the edge portion of the current collector may differ from that of the edge portion of the edge plate. In this situation, a stress may take place intensively in the single cell 1. However, when the above mentioned members are unifiedly constructed in accordance with the present embodiment, it is possible to prevent such a stress from taking place. In addition, the separator 21c does not require a cut working and a joint working by weld working, and so forth. Thus, the separator 21c can be readily produced. Moreover, it is possible to remove the residual stress which takes place in the members involved in such a working. Consequently, it is possible to prevent the members from being deformed by release of stress due to temperature rise involved in the operation of the fuel cell. A separator 21f shown in Fig. 2 is characterized in that an anode current collector 65 and a cathode current collector 66 where an current collector, an current collector support and an edge plate are unifiedly formed are used. The separator 21f can prevent the increase of the electric resistance of the contacting portions due to corrosion. In addition, by the unified construction, the dimensional tolerance can be decreased and thereby the dimensional control can be simplified. Generally, a separator completely separates the fuel gas from the oxidant gas and passes them to the anode and the cathode, respectively. The anode and the cathode are directly and intimately contacted with the separator. Usually by the physical contact or by the presence of electrolyte soaked in the anode and the cathode, the separator seals in the gases on the surface faced an single cell. However, it is very difficult to completely keep the gases sealed in. In other words, the fuel gas and the oxidant gas unavoidably leak out of the separator. In addition, an external gas unavoidably mixes with the fuel gas and the oxidant gas. Then, a separator which can prevent the fuel gas or the oxidant gas from leaking out of the separator will be described in the following. Fig. 3 shows a construction of a separator 21h which was designed to satisfy the above mentioned object. In this embodiment, each of an anode edge portion 81 and a cathode edge portion 82 have grooves 83 on the surface in contact with the single cell. The groove 83 is filled with for example glass powder as a sealing material. The glass powder constantly resides in the groove 83 so as to prevent the fuel gas and the oxidant gas from flowing out of the separator or an external gas from entering therein. Although powder, for example glass powder or fiber material, as the sealing material tends to be lost by the pressure difference of the gases and outer disturbances. However, according to the present embodiment, since the groove 83 prevents the sealing material from moving and constantly holds it between the separator 21h and the single cell 1, it is possible to prevent the fuel gas and the oxidant gas from leaking out of the separator 21h. In addition, when members of the separator are unified by the weld working described later, this groove 83 can also prevent the surfaces of the anode edge portion 81 and the cathode edge portion 82 in contact with the single cell 1 from being distorted by heat applied thereby. At present time, it is estimated that the size of each side of the single cell 1 of the fuel cell which will be commercialized will be in the range from 500 mm to 1000 mm. Thus, the size of the separator which leads the gases to the single cell 1 will exceed the estimated size. In addition, from the standpoint of the strength, the life against corrosion, the weight reduction, and so forth, it is estimated that the thin plate which is used for the separator will be a stainless steel with a thickness in the range from 0.25 mm to 0.5 mm. To improve the dimensional accuracy of such a thin plate, in particular, the dimensional accuracy of the thickness thereof, the working method should be also considered. Then, a press working method for the anode edge plate 58 and the cathode edge plate 59 according to the above mentioned embodiment will be described. For the press working, normally male and female type dies are used together. However, in the following embodiment, methods for using either male or female type die will be described, which characterises the present invention. With reference to Fig. 4, an example where a female type die is used will be described. First, a female type die 32 and an outer frame 33 which surrounds the female type die are set on a press head 31. Thereafter, a material 34 is placed on the female type die 32. In addition, a urethane rubber 35 with a particular hardness is placed on the material 34 as a medium for directly pressuring it. Thereafter, the urethane rubber 35 is pressured with a press ram 36, thereby transferring the pressure to the material 34 through the urethane rubber 35. The material 34 is drawn in accordance with a shape which is carved on the female type die 32. In other words, the urethane rubber 35 is deformed in accordance with the shape of the female type die 32. The outer frame 33 is used to confine the urethane rubber 35, which is plastically deformed, in the outer frame when the urethane rubber 35 is pressured and formed so as to prevent the urethane rubber 35 form extruding out of the outer frame and to reduce the pressure necessary for the forming. Then, with reference to Fig. 4', an example where a male type die is used will be described. Like the example where the female type die 32 was used, a male type die 37 is placed on a press head 31 and then surrounded with an outer frame 33. Thereafter, a material 34 is placed on the male type die 37. Thereafter, a urethane rubber 35 with a particular hardness is placed on the material 34 as a medium for directly pressuring it. Thereafter, the urethane rubber 35 is pressured with the press ram 36 so as to transfer the pressure to the material 34 trough the urethane rubber 35. When the male type die 37 is used and the material 34 is pressured and formed, the urethane rubber 35 is drawn to a material edge portion 39 and thereby the portion 39 is deformed. When the female type die 32 is compared with the male type die 37, the former is more suitable than the latter for forming the anode edge plate 58 and the cathode edge plate 59. When the male type die 37 is used, as shown in Fig. 4', the portion of the material 34 in contact with the male type die 37 is pressured and then the material 34 is deformed with an edge 39 of the extruded portion of the male type die. At this time, the portion of the material 34 which is not in contact with the male type die 37, namely the material edge portion 39 , is not restrained. Thus, a wrinkle 40 as shown in Fig. 4" takes place. On the other hand, when the female type die 32 is used, as shown in Fig. 4, since the outer contour portion (the material edge portion 38) of the material 34 which is in contact with the female type die 32 is first pressured, this portion is restrained and thereby no wrinkle takes place. The advantages for use of the female type die 32 are also valid when the separator is unified by a weld working (described later). Now, the effect of the female type die 32 will be described. In Figs. 4" and 4'", when the radius of curvature 43 of the edge portion 42 of the plate in the side closes to the material edge portion 38 are compared, the radius of curvature 43 in the case where the female type die 32 is used is smaller. Thus, when the outer contour portion 44 of the material is welded in assembling the separator, the deformation of the edge plate due to welding heat can be restrained with the angular portion 42 of the edge plate. Moreover, in the case where the edge plate is formed by using the female type die 32, when the width w of the material edge portion 38 is more than 5 times the height d of the edge plate as shown in Fig. 4'", the material which is being formed can be restrained. In addition, the deformation of the material which is being welded can be prevented. Thus, the height and the flatness of the surface of the edge plate in contact with the single cell (the upper surface of the inner edge portion 41 of the material) can become accurate. When the above mentioned press working is performed, the material 34 is properly stretched. Thus, the bending intrinsic to the thin plate can be decreased and thereby the final dimensional accuracy can be improved. The surfaces of the anode edge plate 58 and the cathode edge plate 59 in contact with the single cell 1 should have high flatness in assembling the stacking of the fuel cell. When the anode edge plate 58 and the cathode edge plate 59 are formed from thin plates, distortion thereof may be large. However, when they are formed in the above mentioned method, the distortion can be kept small. Fig. 4"" shows a construction of principal portions of a die in use for a press working for forming the groove 83. This die is constructed such that an extruded portion 91 for forming grooves is formed on the female type die 32 shown in Fig. 4. By using this die in the above mentioned method, while the anode edge portion 81 and the cathode edge portion 82 are drawn, the grooves 83 are formed. Since each of the anode edge portion 81 and the cathode edge portion 82 have the grooves 83, the distortion and deformation which are intrinsic to thin plates can be minimized. Thus, the flatness of the portions where the anode edge portion 81 and the cathode edge portion 82 contact with the single cell 1 can be kept high, thereby improving the performance of the fuel cell being laminated. Then, a seal welding method for welding the anode edge plate, the inter-connector, and the cathode edge plate will be described. The result of this unification working remarkably affects the finish accuracy of the separator. As shown in Fig. 5, edge plates, for example, the anode edge plate 58 (or another anode edge plate), the interconnector 22, and the cathode edge plate 59 (or another edge plate) are laminated so that their peripheral portions are almost fully matched. The vicinity of an edge connected portion 71 is nipped with heat sink metals 72. Thereafter, while the vicinity of the edge connected portion 71 is pressured with for example a hydraulic jack 74 through a restraining plate 73, the anode edge plate 58, the interconnector 22, and the cathode edge plate 59 are continuously welded along their outer peripheral portions by a welding heat source 75. In this manner, the deformation due to heat by the welding is prevented. As the welding heat source 75, any type which can be used in a conventional welding such as TIG (tungsten inert gas arc), plasma, electron beam, or laser can be used. The edge connected portion 71 to be welded is preferably formed from such three plates being uniformly laminated in terms of the workability and the quality. In addition, the length l of the portion extruded from the heat sink metals 72 is preferably in the range from 0 to 0.2 mm so as to minimize heat exposed thereto by the welding. In addition, as shown in Fig. 5', by laminating the anode edge plate 58 (or another anode edge plate), the interconnector 22, and the cathode edge plate 59 (or another edge plate), any position of an outer contour portion 78 can be seam welded so as to unifiedly construct them. According to this method, since the anode edge plate 58, the interconnector plate 22, and the cathode edge plate 59 can be welded at any position of the outer contour portion 78 of the separator, it is not necessary to preliminary machine the edge connected portion thereof in the same dimensions. Thus, the separator can be readily produced. Then, a method for forming large numbers of small holes 56a and 57a provided respectively on the anode current collector 56 and the cathode current collector 57 will be described. The small holes 56a and 57a are used to pass the fuel gas and the oxidant gas to the single cell 1. Conventionally, the small holes 56a and 57a are made by a machine working such as a punch working. However, when the material is machined, it is distorted. Since the separator is intimately contacted with the single cell, a high surface accuracy is required. Thus, a working method which does not distort the material should be used. Thus, an etch working method for making the small holes 56a and 57a is used so as to decrease the number of machine working steps, thereby providing a separator with a high surface accuracy. Fig. 6 shows an example of the etch working method. In the etch working method shown in the figure, first a plate is washed (Fig. 6 A). Thereafter, a photosensitive agent is coated on the entire surfaces of the plate (Fig. 6 B). Thereafter, the surfaces on which the photosensitive agent is coated are masked with masks having a particular small hole pattern. In this state, the surfaces are exposed (Fig. 6 C). The surfaces are developed so as to transfer the small hole patterns of the masks to the plate (Fig. 6 D). Thereafter, the plate is etched so as to make small holes (Fig. 6 E). Last, the photosensitive agent is removed from the plate (Fig. 6 F). With the above mentioned etch working, the material plate is corroded so as to make the small holes 56a and 57a. Thus, since the steps of shear working for the anode current collector 56 and the cathode current collector 57 can be omitted, the distortion of the members can be prevented. For example, when holes are made by a punch working, only the portions where the holes are made are stretched in the direction of the plate surface and thereby a distortion takes place at a boundary between the worked portions and the non-worked portions. Fig. 6' shows an anode current collector 56 and a cathode current collector 57 which have been etched. In this embodiment, the small holes 56a and 57a are round. However, it is possible to make such holes in any shape in the same manner. As a working for making holes, it is possible to use an electric discharge working which has the same effect as the etch working, the effect preventing the distortion of the members. Industrial Utilization As was described above, the separators and the method of manufacturing the same according to the present invention are suitable for separators of power generating fuel cells and, in particular, of molten carbonate fuel cells.

Claims: A separator (21c, 21h) of molten carbonate fuel cells disposed between plate-shaped single cells (1) having an electrolyte matrix (2) put between an anode (3) and a cathode (4), said separator (21c, 21h) forming gas flow paths for leading a fuel gas and an oxidant gas to said anode (3) and said cathode (4) respectively, connecting said single cells electrically to each other, said separator (21c, 21h) comprising: a plate-shaped interconnector (22); current collector supports (25, 26) disposed on both sides of said interconnector (22); current collectors (56, 57) with large numbers of holes (56a, 57a), deposited on both sides of said interconnector (22), supported by said current collector supports (25, 26) with said gas flow paths therebetween, and being in contact with the centre of said single cells (1); and edge plates (58, 59, 81, 82) in contact with edge portions of said single cells (1), provided on periphery of said current collectors (56, 57), wherein said current collector (56, 57) and said edge plate (58, 59, 81, 82) are formed from one thin plate to be flexible, and said current collector and said edge plate are unified. A separator (21f) of molten carbonate fuel cells disposed between plate-shaped single cells (1) having an electrolyte matrix (2) put between an anode (3) and a cathode (4), said separator (21f) forming gas flow paths for leading a fuel gas and an oxidant gas to said anode (3) and said cathode (4) respectively, connecting said single cells electrically to each other, said separator (21f) comprising: a plate-shaped interconnector (22); current collector supports disposed on both sides of said interconnector; current collectors (65, 66) with large numbers of holes, deposited on both sides of said interconnector (22), supported by said current collector supports with said gas flow paths therebetween, and being in contact with the centre of said single cells; and edge plates in contact with edge portions of said single cells, provided on periphery of said current collectors (65, 66), wherein said current collector (65, 66), said edge plate and said current collector support are formed from one plate to be flexible, and said current collector (65, 66), said edge plate and said current collector support are unified. A separator according to claim 1 or 2, wherein said edge plate (81, 82) is provided with a groove (83) for holding a gas sealing member. A method of manufacturing a separator (21c, 21h, 21f) of molten carbonate fuel cells disposed between plate-shaped single cells (1) having an electrolyte matrix (2) put between an anode (3) and a cathode (4), said separator forming gas flow paths for leading a fuel gas and an oxidant gas to said anode (3) and said cathode (4) respectively, connecting said single cells electrically to each other, said separator comprising: a plate-shaped interconnector (22); current collector supports (25, 26) disposed on both sides of said interconnector (22); current collectors (56, 57, 65, 66) with large numbers of holes (56a, 57a), deposited on both sides of said interconnector (22), supported by said current collector supports (25, 26) with said gas flow paths therebetween, and being in contact with the centre of said single cells (1); and edge plates (58, 59, 81, 82) in contact with edge portions of said single cells (1), provided on periphery of said current collectors (56, 57, 65, 66), said method comprising the steps of: placing a die (32, 37) and an outer frame (33) for surrounding the die on a press head (31); placing a thin plate (34) and a soft plate (35) having a predetermined hardness on said die in the order; and pressing said thin plate through application of pressure on said soft plate, by use of a press ram (36). A method according to claim 4, further characterised in that a total of three plates consisting of an interconnector (22) for separating said different flow paths and said edge plates are laminated and the outer contour portion thereof is jointed by a seal weld working. A method according to claim 4 or 5, further characterised in that said current collector is etched by an etch working to make small holes. A method according to claim 4, further characterised in that said die is a female type die. A method according to claim 4, further characterised in that said die is a male type die.

Inventors: SASAKI MASAKUNI, SHIMIZU YASUSHI, TANAKA KIYOTAKA, YAMAGUCHI TERUO, SASAKI, MASAKUNI, SHIMIZU, YASUSHI, TANAKA, KIYOTAKA, YAMAGUCHI, TERUO
Applicants: TOSHIBA KK, KABUSHIKI KAISHA TOSHIBA
Application year: 1991
Main classification: H01M8
IPC codes: H01M8