Process for manufacture of a moldable biodegradable material

Abstract: A biodecomposable or biodisintegrable moldable material which comprises a mixture of 10-70 vol.% of a natural high molecular substance, 30-70 vol.% of a thermoplastic resin and 0-45 vol.% of a filler.

Description: The present invention relates to a process for manufacturing granules of a biodecomposable material which can be used as a moldable material, and to a molded article produced therefrom. More particularly, the present invention relates to a process wherein certain natural high molecular weight substances, for instance starch or cellulose, are incorporated in a particular manner and in a specific proportion with certain biodecomposable thermoplastic resins. Many synthetic resin (plastic) articles produced heretofore are devoid of any biodisintegrability, unlike products from natural high molecular weight substance such as cellulose, and a serious problem now exists in the treatment of waste plastic articles. For example, plastic bags made of polyvinyl chloride are not biodecomposable by the action of microorganisms. Accordingly, waste bags remain in the soil semi-permanently without undergoing any chemical decomposition. Further, a movement to prohibit or limit the use of plastic as packaging materials is being encouraged in recent years in Europe and America. Thus, this problem of the treatment of waste plastic articles has now become urgent. In the prior art, products heretofore developed and actually put into practice for solving problems in the treatment of waste plastics are articles only in the form of a sheet or film wherein polyethylene is incorporated with 6-25% by weight of starch. However, such products are poor in starch content so that biodecomposition of starch by microorganisms is not completely attained. In addition, the products still maintain their structure and are not disintegrated into pieces even if the contained starch is completely biodecomposed. On the other hand, if the starch content is increased to overcome the above defect, the intended biodisintegration of the products will certainly take place but the starch incorporated in a large amount into plastics is devoid of any plasticity so that the products, for example, in the form of a sheet are significantly inferior in mechanical properties and are hardly used for the manufacture of molded articles where a secondary processing treatment is required. Thus, the known conventional biodisintegrable plastics are utterly unsatisfactory in the degree of biodisintegration itself or otherwise poor in mechanical properties and processability. Under the above circumstances, there is a great demand for developing a new process for manufacturing moldable plastic materials which enable good biodisintegration of and prevent deterioration in mechanical properties and thermoformability of articles molded therefrom. US-A-3850863 discloses moldable biodegradable plastics materials which consist essentially of a uniform blend of thermoplastic oxyalkanoyl polymer and naturally occurring biodegradable product, for instance tree bark, shredded wood and soybean powder. Fillers may be incorporated in the blend if desired. In accordance with the present invention there is provided a process for manufacturing granules of a biodecomposable material, comprising the steps of: (a) charging a high velocity reaction mixer with a mixture of a thermoplastic resin, a natural high molecular weight substance and, optionally, a particulate or fibrous filler, said thermoplastic resin, said natural high molecular weight substance and said filler being present in amounts of 30-70% by volume, 10-70% by volume and 0-45% by volume, respectively; said thermoplastic comprising a biodecomposable resin selected from aliphatic polyesters and cycloaliphatic polyesters; and said natural high molecular weight substance being selected from starch, starch derivatives obtained by copolymerizing starch with a vinyl monomer, cellulose, gum arabic, natural rubber and animal and plant proteins; (b) stirring said mixture in said mixer at a high velocity and with heating whereby there are formed microparticles of the resin to the surfaces of which are attached said natural high molecular weight substance in particulate or fibrous form and said filler if present; and (c) agglomerating said resin microparticles to form granules having a diameter of 0.1-20 mm by fuse bonding the resin microparticles together. The natural high molecular weight substances used in the process of the present invention are starch, e.g. obtained from starch-enriched materials such as potato, rice, wheat, corn and tapioca; starch derivatives obtained by copolymerizing starch with a vinyl monomer such as vinyl acetate or an acrylate; cellulose e.g. plant powders such as sawdust, pulp powder, powdery cellulose and various cellulose fibers e.g. plant fibers such as cotton or hemp; gum arabic; natural rubber; and animal and plant proteins such as casein, gelatin and gluten. The average volume of the particles of these high molecular weight substances is preferably within the range from 4.2 x 1/10 3 µm 3 to 520 x 10 3 µm 3 , more preferably 4.2 x 1/10 3 µm 3 to 2.2 x 10 3 µm 3 . In case of fibrous natural high molecular weight substances, the thickness of the fibers is less than 100 µm, preferably 1-50 µm while the length of the fibers is less than 10 mm, preferably less than 5 mm. These natural high molecular weight substances are employed either alone or in mixtures of at least two of the substances. The second essential starting material in the process of the invention is a thermoplastic resin which comprises a biodecomposable resin selected from aliphatic polyesters, for example polyhydroxybutyrate (PHB), polycaprolactone (PCL), polyethylene adipate (PEA) and polytetramethylene adipate and the like aliphatic polyesters and their derivatives, and cycloaliphatic polyesters and their derivatives such as polycyclohexylenedimethyl adipate. These resins are employed singly or in mixtures of at least two of the resins. The thermoplastic resin may also comprise a non-biodecomposable resin, for example, olefinic resins such as polyethylene, polypropylene, polymethylpentene, ethylene-vinyl acetate copolymer and its saponified product; polyester resins such as polyethylene terephthalate, polybutylene terephthalate, etc; vinyl resins such as polyvinyl chloride, polyvinylidene acetate, their copolymers, etc; styrene resins such as polystyrene and styrene copolymers; and other resins such as polyamide resins and polycarbonate resins. These resins also may be employed singly or in mixtures of at least two of the resins. The filler optionally charged to the reaction mixer includes those of known conventional organic and inorganic nature and may be in the form of particles or fibers. Illustrative of suitable filler in the form of particles are, for example, talc, calcium carbonate, clay, silica, alumina, glass powder, metal powder, powdery thermocurable resin, mica and metal flake. Illustrative of suitable filler in the form of fibers are, for example, glass fibers, carbonaceous fibers, asbestos and mineral fibers. The average volume of the filler particles preferably is within the range from 4.2 x 1/10 3 µm 3 to 910 µm 3 , more preferably 4.2 x 1/10 3 µm 3 to 600 µm 3 . In case of the fibrous fillers, the thickness of the fibers is less than 100 µm 3 , preferably 1-50 µm, while the length of the fibers is less than 10 mm, preferably less than 5 mm. The starting mixture from which the granules are made by the process in accordance with this invention is comprised of 10-70 vol. %, preferably 25-55 vol. % of the natural high molecular weight substance, 30-70 vol. %, preferably 30-50 vol. % of the thermoplastic resin and 0-45 vol. %, preferably 0-20 vol. % of the filler. When the thermoplastic resin is a mixture of the biodecomposable resin and a non-biodecomposable resin, the proportion of the biodecomposable resin based on the mixed resin is suitably within the range of 1-80 vol. %, preferably 20-80 vol. %. It is important that the proportion of the natural high molecular weight substance is at least 10 vol. %, preferably at least 25 vol. %. It has been found by the present inventors that if the proportion of the natural high molecular weight substance is at least 10 vol. % in the starting mixture, then the particles of the natural high molecular weight substance in a molded article made from the resultant granules will directly bind mutually without being interposed with the resin particles, so that the molded article will be furnished with good biodecomposability owing to the natural high molecular weight substance, and also that the biodecomposability or biodisintegrability of the resultant molded article can be controlled by adjusting the proportion of the natural high molecular weight substance. The following table (Table 1) shows the result of measuring the biodisintegrability of a sheet made of a mixture of polypropylene and corn starch relative to the proportion of corn starch therein. In Table 1, TOC stands for total organic carbon quantity dissolved in an aqueous solution as a result of biodecomposition of the corn starch in the sheet. The measurement of TOC is carried out in the same manner as will be described in the Examples except that α-amylase is used as an enzyme, a sheet of 6 cm x 5 cm x 0.5 mm in size is used as a sample and the total reaction time is 256 hours by 16 times repeating the reaction of 16 hours. Corn Starch incorporated (vol. %) TOC formed (ppm) 0 0 10 125 20 410 30 1650 40 4450 50 7470 As indicated above, the moldable granules are made in this invention by charging a high velocity reaction mixer with the natural high molecular weight substance, the thermoplastic resin and the optional filler, and stirring the mixture in the mixer at a high velocity under heating. Any conventional mixer such as a Henshell mixer (manufactured by Mitsui Miike Seisakusho), a super mixer (manufactured by Kawata Seisakusho) or the like high velocity vortex mixer can be used for this purpose. As a large amount of such non-melting solid particles (the natural high molecular weight substance and the optional filler) exists in this high velocity stirring operation under heating, the resin does not form a molten mass even if the temperature reaches the melting temperature of the resin. The resin is divided into microparticles onto the surface of which the solid particles (the natural high molecular weight substance and the filler) are attached. The resin microparticles then mutually combine to form agglomerates of 0.1-20.0 mm in size. In order to form these agglomerates efficiently, the whole mass can be stirred at high velocity for a period of 5-200 seconds, preferably 10-100 seconds at about the melting temperature of the resin. At the time the agglomerates are formed, the mixture is cooled and solidified and any agglomerates of larger than 20 mm in size are pulverized for use in the moldable granular material. As a means for cooling the mixture, any of the known methods can be employed; for example, the mixture is taken out from the mixer and water is sprinkled on the mixture or air is blown while the mixture is stirred, if necessary, at a low velocity, or otherwise the mixture is poured into water or is stirred in a cooling mixer while blowing air. When the natural high molecular weight substance, the thermoplastic resin and the optional filler are mixed, an auxiliary substance or substances may be incorporated into the mixture. Such auxiliary substances include antioxidants, surfactants and coloring materials. The mixture thus obtained comprises resin particles mutually fused to form granules onto the surface of which the natural high molecular weight substance or a mixture of the natural high molecular substance and the filler is bound. These granules are porous and are generally 0.1-20 mm, preferably 0.3-5 mm, in size. The biodecomposable or biodisintegrable molded articles of this invention can be manufactured from the granules of the moldable material by hot molding it into various shapes. Any of the molding methods can be adopted for this purpose, including extrusion molding, injection molding, press molding and calendering. In this invention, a foam-molding method can also be adopted to obtain foamed moldings. A general foam-molding method comprises extruding a molten mass of the moldable material incorporated with a foaming agent from a high pressure zone to a low pressure zone. Preferred examples of the foaming agent include a foaming agent of a thermal decomposition type capable of releasing a gas by heating and an organic liquid such as a hydrocarbon or a halogenated hydrocarbon having a low boiling point. As the moldable granular material may contain a thermally deteriorating natural high molecular weight substance, some expedient is necessary in this invention to prevent such natural high molecular substance from thermal deterioration as far as possible. In general, the natural high molecular weight substances hardly undergo thermal deterioration by heating at a temperature lower than 200°C for about one hour and do not suffer any deterioration of physical properties, although it depends on the kind of the natural high molecular weight substances. At a temperature higher than 200°C, however, the natural high molecular weight substance is easily susceptible of thermal deterioration. Especially at a temperature higher than 230°C, deterioration of the substances in their physical properties becomes distinct even by heating at a temperature as short as about 30 minutes. In case the moldable granular material is to be subjected to a hot molding, therefore, it is necessary in the present invention to limit the molding temperature and the molding time to ranges where thermal deterioration of the natural high molecular weight substance does not take place. If the melting point of the resin contained in the moldable granular material exceeds 250°C so that a higher temperature is needed for hot molding of the material, the use of press molding is recommended to ensure that the hot molding is completed within a short period of time. Among the molded articles obtained as above, those wherein the thermoplastic resin component consists of the biodecomposable resin exhibit biodecomposition to such degree that when the articles are left in the soil or water, the natural high molecular weight substance and the resin component constituting the article are entirely biodecomposed, that is to say, the articles disappear. On the other hand, the molded articles wherein the thermoplastic resin component consists of a mixed resin of the biodecomposable resin and a non-biodecomposable resin, retain the non-biodecomposable resin in unchanged or undissolved state when left in the soil or water. However, as the articles still contain a large amount of the natural high molecular weight substances, they are easily biodecomposed to cause disintegration of the articles so that the volume of the articles is considerably reduced. The molded articles obtained from moldable granular material made by this invention containing 25 vol. % of the natural hig molecular weight substance show significant hygroscopic property due to the substance, so that they absorb moisture in air or use, resulting in deterioration of their mechanical strength. However, this problem can be solved by providing the surface of the articles with a moisture proof film, as will be explained hereinafter. It is desirable that plastic molded articles are generally not decomposed while they are in use, but they must quickly be decomposed after use. As previously discussed, the molded articles of this invention are completely biodecomposable or biodisintegrable and may involve such a problem that if their biodecomposability is too high, biodecomposition of the articles proceeds even during their use and the physical properties of the article are considerably deteriorated. Such problem can be solved by applying a moisture-proof film onto the surface of the articles to inhibit biodecomposition from the surface thereof. The moisture-permeability of such moisture-proof film is desirably less than 50, preferably less than 30 g/(m 2 .24 hours), 40°C 25 µm in film thickness). The moisture-proof film may be a high molecular weight film, a low molecular weight film, a metallic film or a ceramic film, and its thickness is usually 3-60 µm. An adhesive or bonding film may be interposed, if necessary, between the surface of the articles and the moisture-proof film. Illustrative of materials for use as a high molecular weight film are, for example, polyethylene, polymethylpentene, ethylene-vinyl acetate copolymer and the like olefin polymers or copolymers; aromatic polyester resins such as polyethylene terephthalate; vinyl resins such as polyvinyl chloride, polyvinylidene chloride, polytetrafluoroethylene or copolymers thereof; etc. This organic high molecule film can be formed on the surface of the articles by coating or dry laminating. Illustrative of suitable materials for low molecular weight films are, for example, paraffin, a silicone, a low molecular weight polyethylene and a low molecular weight styrene or a copolymer thereof. Illustrative of the material which can be used for metallic films are, for example, aluminum and copper. The metallic film can be formed on the surface of the articles by vacuum vapor deposition or by lamination of a metal film. Illustrative of the materials for forming ceramic films are, for example, alumina, silica and boron oxide. The moisture-proof film is provided at least on one side of the surface of the articles. When the molded articles are a film or sheet, either side of the articles may be provided with the film. In case of the articles being a pipe or a container, it is preferable to form the film on the external surface thereof. The volume of the completely biodecomposable or biodisintegrable molded articles of this invention is reduced significantly by biodecomposition. Thus, the use of the molded articles of this invention can help solve the difficult problem of the treatment of waste plastics. The molded articles of the present invention can simply be disposed after use by pulverizing or burying them in the soil or water. For example, the molding articles of this invention can preferably be dealt with by immersing them in a treatment water tank where microorganisms are previously propagated in water. The articles of the present invention may be in various forms, such as a film, sheet, plate, container, pipe, box, etc. A molded article in the form of a film or sheet can further be processed to form a container or the like article by secondary processing. The following examples will further illustrate the present invention. In the examples, the abbreviations are as follows: PP: polypropylene (EB-4237, manufactured by Mitsui Toatsu Chemicals, Inc.); EVA: ethylene/vinyl acetate copolymer (KA-10, manufactured by Sumitomo Chemical Industries Co., Ltd.); PCL: polycaprolactone (H-7, manufactured by Daicel Chemicals, Inc.); BHT: butylated hydroxy toluene (or 2,6-di-tert-butyl-p-cresol); TOC: total water-soluble organic carbon content. Example 1 A high speed mixer (SUPER MIXER SMG 100, manufactured by Kawata Kabushiki Kaisha, 100 liter volume) was modified so that the mixing vessel thereof permitted the heating of a material to be mixed at a temperature of up to 250 °C. Into this vessel, 4 kg of EVA, 4 kg of PCL, 12 kg of cornstarch (CORNSTARCH W, manufactured by Nippon Shokuhin Kako K. K., average particle size: 16 µm, average volume: 2.14x10 3 µm 3 ), 0.2 kg of BHT, 0.2 kg of distearylthiodipropionate (manufactured by Ohuchi Shinko Inc.) and 0.2 kg of calcium stearate (manufactured by Nihon Yushi K. K.) were placed and mixed with heating. After about 20 minutes from the start of the mixing, the torque in the mixing motor was increased. When the temperature of the mixture was increased to 150 °C, this was transferred to a cooling tank of a low revolution speed type. The mixture was further mixed while blowing air into the tank for cooling, thereby to obtain granules. The granules were processed with an extruder (SE-65, manufactured by Toshiba Kikai K. K.) to form a sheet. Example 2 Example 1 was repeated in the same manner as described except that the 12 kg of cornstarch were replaced by 8 kg of cornstarch and 4 kg of talc (MSA, manufactured by Nippon Talc K. K., average particle size: 9 µm, average volume: 381 µm 3 ). Comparative Example 1 Example 1 was repeated in the same manner as described except that the 12 kg of cornstarch and 4 kg of EVA were replaced by 6 kg of talc and 10 kg of EVA. Example 3 Example 1 was repeated in the same manner as described except that 4 kg of EVA and 4 kg of PCL were replaced by 8 kg of PCL. Example 4 Example 3 was repeated in the same manner as described except that the 12 kg of cornstarch were replaced by 8 kg of cornstarch and 4 kg of talc. Comparative Example 2 Example 3 was repeated in the same manner as described except that the 12 kg of cornstarch and 8 kg of PCL were replaced by 12 kg of talc and 8 kg of EVA. Comparative Example 3 PCL was processed by itself in the manner as described in Example 1 to form a sheet. Comparative Example 4 Example 1 was repeated in the same manner as described except that the 4 kg of EVA and 4 kg of PCL were replaced by 8 kg of PP. Comparative Example 5 Comparative Example 4 was repeated in the same manner as described except that the 12 kg of cornstarch were replaced by 8 kg of cornstarch and 4 kg of talc. Comparative Example 6 Comparative Example 4 was repeated in the same manner as described except that the 8 kg of PP and 12 kg of cornstarch were replaced by 16 kg of PP and 4 kg of cornstarch. Comparative Example 7 Comparative Example 4 was repeated in the same manner as described except that the 12 kg of cornstarch were replaced by 12 kg of talc. Example 5 Example 1 was repeated in the same manner as described except that the 4 kg of EVA, 4 kg of PCL and 12 kg of cornstarch were replaced by 6 kg of PCL, 6 kg of PP and 8 kg of talc. Example 6 Example 5 was repeated in the same manner as described except that the 6 kg of PCL, 6kg of PP and 8 kg of talc were replaced by 8 kg of PCL and 12 kg of talc. Comparative Example 8 Example 5 was repeated in the same manner as described except that the 6 kg of PCL and 6 kg of PP were replaced by 12 kg of PP. The proportions of EVA, PCL, PP, cornstarch and talc in the foregoing examples and comparative examples are shown in Table 1 below. In Table 1, the values in the brackets are contents of the components in terms of % by weight. Example No. Content of Components of Sheet (vol.%) EVA PCL PP Cornstarch Talc 1 29 (20) 23 (20) - 48 (60) - 2 30 (20) 25 (20) - 34 (40) 11 (20) Comp. 1 66 (50) 21 (20) - - 13 (30) 3 - 49 (40) - 51 (60) - 4 - 52 (40) - 37 (40) 11 (20) Comp. 2 66 (40) - - - 34 (60) Comp. 3 - 100 (100) - - - Comp. 4 - - 55 (40) 45 (60) - Comp. 5 - - 58 (40) 32 (40) 10 (20) Comp. 6 - - 88 (80) 12 (20) - Comp. 7 - - 66 (40) - 34 (60) 5 - 35 (30) 45 (30) - 20 (40) 6 - 61 (40) - - 39 (60) Comp. 8 - - 82 (60) - 18 (40) Each of the thus obtained sheets was tested for its tensile strength and biodegradability to give the results summarized in Table 2 (Tables 2-1 and 2-2). The test methods are as follows: Tensile Strength was measured in accordance with Japanese Industrial Standard JIS K-7113. Biodegradability Test was carried out in accordance with an enzyme method. As an enzyme, 324 units of alpha-amylase of bacillus subtilis origin (manufactured by Seikagaku Kogyo K. K.), 30.6 units of purified lipase of Rizopus arrhizus origin (Sigma Inc.) or a mixture of 324 units of alpha-amylase and 30.6 units of lipase was used. The enzyme is added into 10 ml of a solution containing 1 ml of a buffer solution (pH 7.0, KH 2 PO 4 /Na 2 HPO 4 ), 0.5 ml of a 1 % by weight aqueous surfactant solution and 8.5 ml of water. A film sample (1 cm x 3 cm x 0.5 mm) is immersed in the above enzyme solution and shaken at 30 `C for 16 hours. The resulting enzyme solution was filtered and the filtrate was analyzed to determine the concentration (C 1 ) of water-soluble organic carbon. As a control, a film sample is treated in the enzyme-free solution and the concentration (C 2 ) of water-soluble organic carbon is measured. The total water-soluble organic carbon (TOC) which represents the amount of the organic carbon dissolved by the enzyme in solution is obtained by subtracting C 2 from C 1 (TOC = C 1 - C 2 ). The biodisintegrability of the sample is evaluated from TOC, i.e. the greater TOC the higher the biodisintegrability. The sample obtained after the biodegradability test (after repeating the above treatment until no increase in TOC is observed) is dried under vacuum for 24 hours and measured for its tensile strength.

Claims: A process for manufacturing granules of a biodecomposable material, comprising the steps of: (a) charging a high velocity reaction mixer with a mixture of a thermoplastic resin, a natural high molecular weight substance and, optionally, a particulate or fibrous filler, these components being present in amounts of 30-70%, 10-70% and 0-45% by volume, respectively; said thermoplastic comprising a biodecomposable resin selected from aliphatic polyesters and cycloaliphatic polyesters; and said natural high molecular weight substance being selected from starch, starch derivatives obtained by copolymerizing starch with a vinyl monomer, cellulose, gum arabic, natural rubber and animal and plant proteins; (b) stirring said mixture in said mixer at a high velocity and with heating whereby there are formed microparticles of the resin to the surfaces of which are attached said natural high molecular weight substance in particulate or fibrous form and said filler if present; and (c) agglomerating said resin microparticles to form granules having a diameter of 0.1-20 mm by fuse bonding the resin microparticles together. A process according to Claim 1, wherein said step (c) is effected by stirring said resin microparticles at high velocity for from 5-200 seconds at about the melting temperature of the resin. A process according to Claim 1 or Claim 2, wherein said biodecomposable resin is selected from polyhydroxybutyrate, polycaprolactone, polyethylene adipate, polytetramethylene adipate and polycyclohexylenedimethyl adipate. A process according to any preceding claim, wherein said thermoplastic resin also comprises a non-biodecomposable resin selected from polyethylene, polypropylene, polymethylpentene, ethylene-vinyl acetate copolymers and saponified products thereof, polyethylene terephthalate, polybutylene terephthalate, polyvinyl chloride and copolymers thereof, polyvinylidene acetate and copolymers thereof and polystyrene and copolymers thereof. A process according to Claim 7, wherein said biodecomposable resin comprises from 1-80 wt. % based on the total weight of said thermoplastic resin. A process according to any preceding claim, wherein said natural high molecular weight substance is in the form of particles having an average volume within the range of 4.2 x 1/10 3 µm 3 - 520 x 10 3 µm 3 , or in the form of fibers having a diameter of less than 100 µm and a length of less than 10 mm. A process according to any preceding claim, wherein said mixture charged in step (a) comprises a filler which is in the form of particles having an average volume within the range of 4.2 x 1/10 3 µm 3 to 910 x 10 3 µm 3 or in the form of fibers having a diameter of less than 100 µm and a length of less than 10 mm. A molded article obtained by molding granules made by a process according to any preceding claim. A molded article according to Claim 8, wherein the article has a moisture-proof film on the surface thereof.

Inventors: KOYAMA MASATOSHI, SUZUKI MASAHIRO, TOKIWA YUTAKA, KOYAMA, MASATOSHI, SUZUKI, MASAHIRO, TOKIWA, YUTAKA
Applicants: AGENCY IND SCIENCE TECHN, CHUOKAGAKU LTD, CHUOKAGAKU LTD., DIRECTOR-GENERAL OF THE AGENCY OF INDUSTRIAL SCIENCE AND TECHNOLOGY
Application year: 1991
Main classification: C08L101
IPC codes: C08K5, C08L77, C08L101, C08L67, C08L3, C08L89, C08L1, C08K7, C08K3, C08L23