Doped sol-gel glasses for obtaining chemical interactions

Abstract: A method for obtaining an interaction between reagent/s in a solid support and diffusible solute/s or components in an adjacent liquid or gas phase wherein said reagent/s are trapped in a sol-gel glass (hereinafter also referred to as doped sol gel glass) which provides the solid support to the reagents, wherin a sol-gel glass is any ceramic or organoceramic material prepared by polymerization of suitable monomers, such as metal alkoxide mixtures, wherein the polymerization is carried out through the sol gel-xerogel stages.

Description: The present invention relates to a doped sol-gel glass for use in obtaining an interaction between reagent/s in said sol-gel support and diffusible solutes or components in an adjacent liquid or gas phase, wherein said reagent/s are trapped in said sol-gel glass (hereinafter also referred to as doped sol-gel glass) which thus provides the solid support to the reagent/s. The doped sol-gel glass according to the present invention can be used for a variety of interactions between the reagent in said doped sol gel glass and reagent/s in an adjacent liquid or gas phase. The present invention can be useful in a myriad of applications: for quantitative and/or qualitative analyses, for extraction or separation of solutes from liquid solutions, and for many other applications. For example, the above glass can be useful for detection of ions by chemical interaction between the ion/s in an aqueous phase and reagents trapped in the "sol-gel" glass, or vice versa, via characteristic "color test" reactions, or other routine detection methods. Another example is utilization of the above glass for qualitative and/or quantitative analyses of pollutants. The sol-gel glass can be applied as well for medical diagnostic purposes e.g. for detecting inorganic ions and/or small organic molecules in blood, urine and other body liquids. Another example, according to the present invention, is a chemical interaction between a substrate/antigen in the liquid phase and an enzyme/antibody trapped in the "sol-gel" glass. For centuries, inorganic glasses have been prepared by high temperature melting methods. This has imposed a major limitation upon the technological application of glasses: additives were restricted to thermally stable inorganic materials, while precluding the incorporation of labile organic molecules. A recent major development in material science has been the preparation of inorganic (silica) glasses through the low temperature "sol-gel" synthesis (Brinker, C.J., Scherer, G.W., Sol-Gel Science, Academic Press, San Diego (1990)). An amorphous bond network of the glassy material is prepared by the room-temperature polymerization of suitable monomers, usually metal alkoxides, according to schemes such as: nSi(OCH 3 ) 4 + mH 2 O → (-O-Si-O-) n + 4nCH 3 OH + (m-2n)H 2 O in which water is consumed by H 2 O + Si(OCH 3 ) 4 → Si-OH + CH 3 OH and released by 2 Si-OH → Si-O-Si + H 2 O. By sol-gel glass one means any ceramic or organoceramic material prepared by polymerization of suitable monomers (e.g. metal alkoxide mixtures) wherein the polymerization is carried out through the sol gel-xerogel stages. The result of the polymerization is a transparent porous solid (xerogel) with surface areas of up to hundreds m 2 /gr and by narrow pores (0.5-500 nm). The low-temperature glass synthesis allows doping inorganic (silica or other) glasses, with essentially any organic molecule. This possibility was used for trapping of e.g. photoactive molecules by adding the compound to the starting mixture at the onset of polymerization (Avnir, D., Levy D., Reisfeld, R., J. Phys. Chem. 88, 5956 (1984)). The compound remained permanently trapped, i.e. non-leachable system have been obtained. These doped sol-gel glasses have been used as photoactive materials, such as: (a) Dye laser materials; (b) Thin-film optical filters; (c) Fluorescent solar collectors; (d) Photochromic and phosphorescent glasses. The interaction between the optical properties of trapped molecules and their environment was employed for monitoring the progress of the glass formation sequence: monomer → oligomer → sol → gel → xerogel. This allowed to scrutinize the evolution of such parameters as porosity, water content and degree of (cage) polarity (Kaufman, V.R., Avnir, D., Structural changes Along the Sol-Gel-Xerogel Transitions, Langmuir 2, 717 (1986); Kaufman, V.R., Avnir, D., Pines-Rojanski, D., Huppert, D., Water Consumption During the Early Stages of the Sol-Gel Polymerization, J. Non-Cryst. Solids 99, 379 (1988). The article by Carturan et al (J. Mol. Catalysis 57 (1989), pages L13 - L16) describes the immobilization of yeasts on silica gel (SiO 2 ). The biomaterial here was whole yeast cell aggregates (clumps) and, as they describe at the end of the paper, the authors express concerns about the clumping effect because it tends to reduce the enzyme activity of the yeast. Clumping reduces the cell surface area which is exposed to the substrate (glucose) and hence the enzyme activity is reduced. The rather obvious answer to this problem is to use the free enzyme rather than the whole yeast cells but this did not work - see page L15 last sentence of first (partial) paragraph. The explanation offered is that the free enzyme reacts with tetraethoxysilane, Si(OEt) 4 . According to one aspect of the present invention there is provided a sol-gel glass for use in obtaining an interaction between at least one first reactant within the sol-gel glass and at least one second reactant that is a diffusible solute or component in an adjacent liquid or gas phase, characterised in that the sol-gel glass is of a ceramic or organo-ceramic porous material prepared by monomer polymerisation conducted through the sol-gel-xerogel stages, in that the interaction is a direct chemical interaction by intimate contact between the first and second reactants, and in that the or each said first reactant is entrapped on a molecular level in the matrix of the porous sol-gel glass. Such sol-gel glasses demonstrate several technologically attractive properties: (a) the ability to isolate a single doping molecule in an individual cage, even at high concentrations of additive, thus avoiding interfering with impurities or photodecomposition products; (b) thermal and photochemical stability as well as transparency in the U.V. range about 250nm. (c) lack of teaching of the trapped compound, simplicity of preparation, and easy technological manipulation allowing production in any desired geometry, including films. Surprisingly, it was found that molecules trapped in sol-gel glasses, may interact with diffusible solutes or components in an adjacent liquid or gas phase in the pore space. Said finding opened a new wide range of applications of doped sol-gel glasses as solid media for chemical interactions. According to another aspect of the present invention there is provided a process for the preparation of a doped, reactive, sol-gel glass according to any preceding claim, wherein metal alkoxides, semi-metal alkoxides, metal esters or semi-metal esters monomers of the formula M(R) n (P) m in which M is a metallic or semi-metallic element, R is a hydrolyzable substituent, n is an integer between 1-6, P is a non-polymerizable substituents and m is an integer between 0-6, are polymerized or co-polymerized in the presence of at least one first reactant with an organic polymer under acidic, neutral or basic conditions resulting in a transparent porous xerogel, wherein said first reactant is able to undergo a direct chemical interaction by intimate contact with a second reactant. Said reagent/s can be any organic compound, organometallic, or inorganic compound, or any biological material capable of being trapped in the sol-gel glass. The diffusible solute/s or components can be any organic compound, stable organic radical, organometallic, or inorganic compound or biological material capable to interact with the trapped reagents. The interaction between the reagent in the solid support and the diffusible solute in the liquid phase or a component in the gas phase can be a chemical interaction such as for analytical tests or chemical reactions. The method according to the present invention can be a specific colour test reaction, N.M.R. or E.S.R. analysis, analysis via emission or absorption, luminescence, fluorescence, phosphorescence tests and/or electrochemical tests. The analytical reagent can be a pH indicator, redox agents or an ion complexant etc. The chemical interaction according to the present invention can take place between anions or cations in a liquid or gas phase and reagents trapped in the sol gel glass or vice versa. For example the interaction may take place between metal ions and a specific reagents via a characteristic colour-test reaction, as in: (1) the determination of Fe +2 cation with o-phenanthrolin, (2) the determination of Co +2 with 1-nitroso-2-naphtol, (3) the determination of Ni +2 wherein the reagent is dimethylglyoxime, (4) the determination of SO 4 -2 anion wherein the reagent is sodium rhodizonate and BaF 2 , or benzoinoxime, (5) the detection of H + is one of many examples for a pH sensors. The analytical test can be carried out by dipping the doped sol gel glass in the solution and observing the resulting color change. The above method can be useful for the analysis of ore contents in soil, sea water, and rocks (e.g. uranium). The sol gel glass according to the present invention can be in any shape suitable for the test. For example it can have the shape of rods, discs, cubes, sieves, powder, or thin films coating conventional glass plates or any other inert solid support. Thus, an electrochemical test according to said invention can be performed by preparing electrodes coated with doped sol gel glass layers. These electrodes may be used for clinical, analytical or industrial purpose, or as biosensors. It should be emphasized that the method according to the invention can be useful for qualitative and for quantitative analysis. The method according to the present invention can be applied to detection and analysis of pollutants in soil, in aquatic environments and characteristic water sources (including waste, industrial and municipal sources, lakes and swimming pools) in food, drugs, or in the air. The method may be applied to qualitative and/or quantitative analysis of pollutants. Said pollutants may be for example chlorides, nitrates, phosphates, herbicides, insecticides, inorganic ions and pollutants of organic origin. Detection devices according to this invention can be utilized as a part of continuous monitoring systems. The present invention can be utilized for extracting or separating molecular solutes from liquid solutions. The doped sol gel glasses can be used according to the present invention for all chromatographic purposes, including liquid, gas and thin layer chromatography. The extraction or separation is performed by passing the solution through columns made from appropriately doped sol gel material. The thin layer chromatography according to this invention can be performed on conventional glass plates, paper or other inert solid support coated with doped sol-gel glass layers. Medical diagnostic is another application of the present invention. For example, detection of inorganic ions, small organic molecules and other components in blood, urine and other body liquids. The invention can be applied also to the fractionation of body fluids. The present invention relates, as well, to a method for preparation of bioactive materials (biocatalysts) by entrapment of enzymes in a forming sol-gel glass, which, following polycondensation of suitable monomers, serves as a solid matrix, bonding the enzyme and conveying to it mechanical, chemical and thermal stabilities. The method, according to the present invention, can be applied to a variety of enzymes or enzyme systems, including co-immobilization of co-factors, organic and inorganic ligands, mono- and polyclonal antibodies, and their detection systems. The method according to the present invention can be useful in a variety of applications, such as: (a) biochemical reactions and other bioconversions in organic and inorganic solvent solutions, (b) detection or qualitative determination of organic and inorganic molecules, which are substrates of the immobilized enzymes, or inhibitors, or modifiers of enzyme activity, (c) construction of bioelectronic detection devices, including construction of enzymes electrodes and biosensors. Commercial applications of enzymes require successful immobilization. Immobilization allows reuse of an enzyme, protects it from harsh external conditions, from microbial contamination, and prolongs their useful lifetime. There are probably as many immobilization methods as there are enzymes. This proliferation of techniques reflects the complexity of the biological material and the variety of its uses. Simple inexpensive general techniques, resulting in stable and active enzyme catalyst are still in great demand (Kennedy, J. F. and White, C. A. in "Handbook of Enzyme Biotechnology" (Wiseman, A. ed.), Ellis Horwood Ltd, Chichester, pp. 147-207 (1985)). An ideal enzyme catalyst should be bound to a mechanically and chemically stable, highly porous carrier. The bond linking the enzyme to the support is required to be stable under the catalyst application conditions to prevent leaching. The strong binding forces also have stabilizing effects on enzyme activity (Martinek, K. and Mozhaev, V. V. Adv. Enzymol. 57 , 179, (1985)). The desired immobilization procedure should be simple, mild (non-denaturing) and generally applicable. Enzymes covalently immobilized on controlled-pore glass beads offer an almost ideal solution to the problems of the support and of the binding force. However the preparation of catalyst by this immobilization technique is neither simple nor generally applicable. The beads are costly, require tedious chemical derivatization procedures, and lack in stability due to the continuous leaching of silica during prolonged usage (Kennedy, J. F. and White, C. A. in "Handbook of Enzyme Biotechnology" (Wiseman, A. ed.), Ellis Horwood Ltd, Chichester, pp. 380-420 (1985)). The most generally applicable immobilization procedure is a simple entrapment of the enzyme in a forming gel of natural or synthetic polymers. The main shortcoming of this technique is the loss of the enzyme by leakage through a nonuniform net of polymer molecules. Rather weak interactions between the enzyme and the matrix result in a relatively nonrestricted diffusional movement of polypeptide chains. This can be of a benefit, whereas conformational transitions are required for successful catalysis. Otherwise, this diffusional freedom of motion can negatively affect immobilized enzyme stability. Several properties of the sol-gel glasses make them especially attractive as possible enzyme catalyst supports: (a) the ability to entrap large amounts of additives; (b) the thermal and chemical stability of the matrix; (c) simplicity of preparation with no need of covalent modification; (d) easy technological manipulation and production in any desired geometry, including thin films. Recently, aggregates of whole yeast cells trapped in thin layers of SiO 2 gels deposited on glass sheets were demonstrated to possess invertase activity. Thin films with cell-free invertase preparation were devoid of activity (Carturan, G., Campostrini, R., Dire, S., Scardi V. and de Alteriis, E. J. Mol. Cat., 57 , L13, (1989)). The present invention relates therefore also to a method for obtaining bioactive materials based on an enzyme molecules trapped within the porous structure of a sol-gel glass. The entrapment is achieved by the addition of a cell-free enzyme to a mixture of monomer or monomers at the onset of polycondensation. In addition to the enzyme and monomer(s), the mixture should contain additives ensuring (1) highly porous nature of the forming glass providing minimal diffusional limitations to the binding of the substrate at the catalytic site and to the removal of the product, (2) the stability of the enzyme during the polymerization and its tight binding preventing leaching of the enzyme. Unexpectedly, we have found (1) that proteins can be trapped within the matrix of a forming sol-gel, (2) that several cell-free enzymes, belonging to various classes: hydrolases, oxidoreductases, lyases etc., can be effectively entrapped in such composite bioactive sol-gel glasses, while retaining high enzymatic activity, (3) that strong binding forces retain the enzyme in the matrix, thus producing a considerable stabilizing effect. The sol-gel immobilized enzymes may be used as biosensors for hormonal tests or for any industrial purposes, including diagnostic and synthetic purposes. Said enzymes can be doped in sol gel glass layers coated on electrodes for probing any substrate. The enzymatic interaction according to the present invention can be applied also to radioactive tests and also for enzymatic column chromatography (crushed powder sol gel glasses may be used as support for enzymatic column chromatography). The sol gel glass can be applied, according to the present invention, as active specific membranes allowing selective incorporation of the trapped molecules or ions or any other species. The abovementioned applications are examples only and do not intend in any way to limit the scope of the invention. The present invention relates also to the application of doped sol gel glasses according to this invention as well as for the preparation of sol gel glasses and doped sol gel glasses for such applications. When prepared as thin film the width of the sol gel glass may be from molecular monolayers up to macroscopic layers. Said thin film can be part of multi-layered array of thin films. Said glasses may be supported on an electrode or optical support. The unique transparency of "sol gel" glasses in the range above 250 nm, makes them highly applicable to quantitative spectrophotometric and spectrofluorimetric tests. Trapping of host molecules is relatively simple and does not require specific synthetic methods such as those associated with covalent linking of reagents to solid supports. Moreover, inherent properties of sol gel glasses such as high surface area, the wide range of available pore sizes and the thin film technology, make them highly attractive for potential applications as solid supports for a variety of reagents. Examples A. Preparation of doped "sol-gel" glasses The polycondensation of alkoxysilans is associated with gelation of the sol, which after drying is densified by a mild heat treatment to form a glass. The properties of the final glass are determined by the chemical and physical conditions during the process of preparation. They depend upon the ratio metal (e.g. silane)/alcohol/water, the alkoxide pH, the presence of a catalyst, the temperature, the drying time and the amounts of organic additives, such as surface active agents. Pore size and surface area are controlled by addition of acid or base (see Scherer and Brinker, 1990, cited above). Addition of NaF to the starting (TMOS, tetramethoxysilane) solution leads to an increase in average pore size. 1. A standard mixture for preparation of doped "sol-gel" glasses contained tetra-methoxy silane (TMOS, 5 ml) H 2 O (2.4 ml) and methanol (6. ml). The appropriate catalyst (examples below) and the desired reagent (examples below) were added in the required amounts (water or methanol solutions). Gels were formed within several minutes (base-catalyzed) or several hours (acid-catalyzed). Gelation was carried out at room temperature in glass bottles covered with aluminium foil. The gels were then transferred to an incubator and kept at 37-45°C. The samples were used after they reached a constant weight (about two weeks). The above procedure yields glass in any desired shape(rods, disks etc.). 2. An alternative technique of preparing sol-gel glasses is based on thin-layer coating of conventional glass supports. A characteristic procedure for the preparation of such thin layers began with a mixture containing methanolic or ethanolic solution of dopant (85 ml), TMOS (10 ml), the surface active agent Triton X-100 (3 g) and 0.03N HCL or 0.01N NaOH (3 ml). After mixing the solution was allowed to stand for 30 min at 25-35°C and was then used for coating. Coating was performed by dipping a glass plate into the solution, followed by drying for several minutes at room temperature. The resulting porous coating layer (0.25-0.5 µm). B. Representative examples of reactivity of reagents trapped in sol-gel glasses 1. Tests were carried out by the immersion for 5 min of an appropriately doped sol-glass in aqueous solutions containing ions or molecules to be detected. Arrows denote transitions from the reagent-doped glass to the same glass after immersion in the tested solution. The doped glasses represent four classes of reactions: (a) a glass-trapped organic reagent with an inorganic cation to be determined in the solution; (b) same with inorganic anions; (c) a glass doped with an inorganic ion, testing a solution containing an organic molecule (reversal of a & b); (d) glass doped with a pH indicator. Representative examples of color tests are shown in Figure 1. Top (left to right): a) Glass doped with 1,10-phenanthrolin after immersion in: b) 10 -5 M Fe 2+ solution, c) 10 -4 M Fe 2+ , d) 10 -2 M Fe 2+ . Glass was prepared in the presence of the reagent (0.005%) and 5x10 -3 M NaOH as catalyst in the starting aqueous solution. Middle : Doped glasses (top) and some glasses after immersion in solutions containing several ions: a) Reagent for A1 3+ was quinalyzarin (1,2,5,8-tetrahydroxyanthraquinone). To the starting solution (see above) 2 drops of a solution with the following composition were added: 18 cc methanol containing 0.01 gr of the reagent, 2 cc pyridine and two drops of 0.1 N NH 4 OH. b) Reagent for Co 2+ was nitroso naphthol. Starting solution contained 0.25% of the reagent and 3 drops of 0.1N HCI as catalyst. c) Reagent for Ni 2+ was dimethylglyoxime (starting solution, contained 0.25% of the reagent and 3 drops of 0.1N NH 4 OH as catalyst. d) Reagent for the SO 4 2- anion was sodium rhodizonate & BaF 2 . Starting solution contained 0.25% sodium rhodizonate, 3,5x10 -3 gr. BaF 2 and 3x10 -3 N NaOH. Bottom left : Glass doped with Fe 2+ (top, yellow) after immersion in a solution containing o-phenanthrolin (bottom, red). The glass, prepared in the presence of an acid catalyst (a few drops of concentrated HCL), was used before complete drying (container was capped after 3 days). Bottom right : Two different reagents for the determination of Cu 2+ (top: glass with reagent, bottom: same after immersion in Cu 2+ solution). Left: Rubeanic acid as a reagent. Starting solution contained 0.15% of the reagent and 0.25% sodium tartaric in the presence of 0.01N NaOH. Right: Benzoinoxime (Cupron) as reagent. Starting solution contained 0.25% of the reagent with one drop of concentrated HCL. After 3 minutes 3 drops of concentrated NH 4 OH were added. C. Representative examples of bioprocesses involving proteins . 1. Preparation of sol-gel immobilized enzymes. Enzyme solutions (0.2 ml, 10 mg/ml) in non-buffered water, which may contain various additives were mixed in the cold (4°C) with either methanol or polyethylene glycol (PEG 400). The concentrations of additives (such as e.g. NaF, NaOH, HCl), the volumes of methanol and PEG 400 were as indicated in the examples below. Tetra-methoxy silane (TMOS, 1 ml) was then added. The tubes containing the reaction mixture were transferred to a shaking water bath at 8°C. The bath was allowed to reach the room temperature during 2-3 h. In samples containing PEG 400, the polymerization was completed in about 3 h. All the liquid remaining on the top of sol-gel was then removed by suction. In methanol-containing mixtures gelation took place in about 4-5 h. The polymerized sol was allowed to dry for a week at 30°C. 2. Retention of protein by the sol-gel glass. All the glasses prepared according to example C1 were ground to a size of about 60-100 mesh and packed in 2 ml-columns. The columns were eluted with 0.5 M NH 4 HCO 3 (250 ml), followed by water (250 ml). This cycle was repeated twice. All washing solutions were collected, concentrated by freeze-drying, and assayed for protein content and for respective enzyme activity. It was found that neither significant enzyme activity nor protein could be detected in the eluates. 3. Entrapment of trypsin in sol-gel glasses. Trypsin (E.C. 3.4.21.4, from bovine pancreas, 11,000 U/mg) was supplied by RAD Chemicals, Rehovot, Israel. Trypsin entrapped in sol-gel was prepared as described in example C1. Assays were performed on the washed glasses at 25°C at pH 8 using N-benzoyl-L-arginine-4-nitroanilide (3.3 mM) as the substrate. The concentration of NaF in the enzyme solution and the addition of methanol or PEG 400 (ml per ml TMOS) as well as the enzymatic activity of the glass catalyst (expressed in per cent of trypsin activity initially added to the condensation mixture are shown in the following Table: NaF (mM) Trypsin Activity (per cent of initial) MeOH (ml/ml TMOS) PEG (ml/ml TMOS) 0.6 0.2 0.4 0.6 0 0.1 11.4 33.0 33.6 1 0.6 16.9 24.7 29.7 10 1.9 10.0 18.2 23.6 100 2.8 4.1 21.6 17.5 4. Entrapment of acid phosphatase in sol-gel glasses. Acid phosphatase (E.C. 3.1.3.2, from wheat germ, 0.45 U/mg) was purchased from Sigma. The acid phosphatase-containing sol-gel glasses were prepared as described in the example C1. The assays were performed on the washed glasses at 25°C at pH 5.6 using p-nitrophenyl phosphate (6 mM) as the substrate. The activity yield, calculated in percents of enzyme activity used initially for the preparation of glasses, is shown in the following Table: SOLVENT NaF, mM 1.0 3.0 10.0 ACID PHOSPHATASE YIELD, % Methanol 0.6 ml/ml 1.9 - 39.2 PEG 400, 0.2 ml/ml 46.6 56.4 21.1 PEG 400, 0.4 ml/ml 39.8 41.0 46.7 5. Thermal stability of immobilized acid phosphatase in different sol-gel glasses. The acid phosphatase-containing sol-gel glasses (example C4) were incubated at 70°C in citrate buffer (pH 5.6, 0.1 M) for various periods of time (up to 5 min). The activity of acid phosphatase was determined, as described in the example C4. The half-life time was calculated assuming the 1 st order inactivation kinetics. The half-life time of the soluble enzyme at the same conditions was below 0.1 min. SOLVENT NaF, mM 1.0 3.0 10.0 HALF-LIFE TIMES AT 70°C, min Methanol 0.6 ml/ml - - 3.9 PEG 400, 0.2 ml/ml 3.3 3.3 12.0 PEG 400, 0.4 ml/ml 3.2 3.1 3.5 6. Entrapment of peroxidase in sol-gel glasses. Peroxidase (E.C. 1.11.1.7, from horseradish, 200 U/mg) was obtained from Sigma. Sol-gels doped with peroxidase were prepared as shown in the example C1. All the glasses prepared with the addition of PEG 400 were active, although it was not possible to determine the extent of their activity quantitatively, since the dye formed by oxidation of several substrates was adsorbed strongly in the glass. Semi-quantitative comparison of the dye stain shortly after the addition of the assay mixture indicated improved activity yields at higher concentrations of PEG 400. In contrast to trypsin and catalase, sol-gel glasses made at elevated concentrations of NaF were more active. Glasses prepared in methanol-containing mixtures were devoid of peroxidase activity. 7. Entrapment of trypsin in sol-gel glasses. Trypsin solution (1.0 ml, 2 mg/ml) in non-buffered water was mixed with either 20 mM NaF (0.1 ml) or the same volume of water, and with one of the following: (1) methanol, (2) polyethylene glycol solution (PEG 6000, 20% w/vol in water), or (3) glycerol solution (75% w/vol in water). The mixture was cooled to 4°C. Tetra-methoxy silane (TMOS, 1 ml) was then added. The tubes containing the reaction mixture were transferred to a shaking water bath and allowed to reach the room temperature. The polymerized sol was allowed to dry for a week at 30°C. The resulting glasses were treated as described (example C2). Trypsin activity of the trypsin-doped sol-gel glasses expressed as the yield of activity used for the preparation of the catalyst is presented in the following Table. ADDITIVES TRYPSIN ACTIVITY, % of initial +NaF -NaF Methanol 17.2 26.8 PEG 6000, 51.3 46.1 Glycerol 82.0 38.1 8. Entrapment of aspartase in sol-gel glasses. Escherichia coli cells (ATCC 11303) were cultured as described (Chibata, I, Tosa, T., and Sato, T. Meth. Enzymol. 44 , 739-746 (1976)). Saline-washed cells (4 g wet weight) were suspended in water (2ml) and disrupted by sonication. The homogenate was cleared by centrifugation (10,000xg, 30 min, 4°C) and used for the preparation of sol-gel glasses. The homogenate (0.5 ml) was mixed with NaF solution (0.2 ml) at the concentrations indicated in the Table below. Methanol (0.6 ml) or PEG 400 (0.2 ml) was then added followed by TMOS (1 ml). All the additions were made at 4°C. The resulting sol was kept overnight at room temperature and then washed with an excess of 50 mM phosphate buffer pH 7. Aspartase activity was measured and expressed in µmoles/min/g cells (wet weight). The results are presented in the Table. For comparison the polyacrylamide gel-entrapped whole cells from the same batch, prepared according to Chibata (1976), possessed aspartase activity of 133 µmoles/min/g cells. NaF solution mM Aspartase Activity, µmole/min/g cells MeOH (ml/ml TMOS) PEG (ml/ml TMOS) 0.6 0.2 0 105.0 79.0 1 15.8 127.7 100 64.5 39.8 9. Preparation of protein-doped glasses by NaOH catalyzed polycondensation. Immobilization of alkaline phosphatase. A mixture of tetra-methoxy silane (TMOS, 5 ml), methanol (6 ml) and 1 mM NaOH in methanol (0.1 ml) was cooled to -20°C and mixed with an ice-cold solution (0.9 ml) of alkaline phosphatase (ALP, E.C. 3.1.3.1 from bovine intestinal mucosa, Type I-S, 8.5 U/mg, Sigma Chem. Co) containing 1.5 mg of the enzyme. A cloudy mixture was allowed to reach room temperature under stirring. The resulting viscous opaque material was kept for 10 days at 37°C. During this time the glass formation was completed and it reached a constant weight. The glass was ground and washed as described in the example C2. The enzyme activity was determined in NaOH-glycine buffer (40 mM, pH 9.5) at 25°C using p-nitrophenyl phosphate as the substrate. The yield of the alkaline phosphatase activity after immobilization was estimated at about 30%. The half-life time of the immobilized enzyme at 70°C (pH 9.0) was 4.7 min, as compared to 2.6 min for the soluble ALP at the same conditions. 10. Immobilization of chitinase The glass trapped enzyme was prepared by adding 1.0 ml of the enzyme chitinase (EC 3.2.1.14, cloned from Serracia marcensens and expressed in E. coli , 200 units) in the phosphate buffer (10 mM, pH 6.3), to a solution obtained by stirring 3.0 ml methanol and 2.ml TMOS for 15 minutes. 11. Antibody reactions Interleukin-2 receptor (IL-2R) is the protein that mediates the action of interleukin-2 (IL-2), an immune system growth hormone. Levels of soluble IL-2R have been shown to be elevated in a number of pathological conditions, and may thus be of significant prognostic value. We have used an Anti-IL-2R monoclonal antibody, trapped in a sol-gel glass, to determine IL- 2R, using a sandwich immuno assay test (cell-free Interleukin-2 Receptor CK 1020, 96 Test kit, T Cell Sciences, Inc., Cambridge, MA, USA). Trapping of Anti-IL-2R monoclonal antibody in a "sol-gel" glass was carried out with a starting solution composed of methanol (3 ml), TMOS (2.5 ml), 6 mM phosphate buffered saline (PBS, 0.25 ml) and Anti-IL-2R antibody (0.25 ml, from the kit). After stirring for 50 min. the sample was allowed to stand for 5 days at 27°C. The resulting glass (4 mg, 0.4% of the total amount) was crushed and washed three times with 350 µl of the "washing solution" from the kit (0.2 ml surfactant in 200 ml PBS). To this solution 100 µl the "sample diluent" (buffered serum protein) and 50 µl of the human IL-2R standard "solution" were added and mixed for 15 sec, followed by covering and incubating for 2 hours at 37°C. After three washings, 100ml peroxidase- conjugated Anti-IL-2R antibody solution was added and incubated at 37°C for 2 hours. After three washings with the "washing solution", 100 µg of o-phenylenediamine dissolved in a "substrate diluent" (buffered H 2 O 2 ) were added and incubated for 20 min at room temperature. An absorbance OD 490 = 0.93 was recorded, compared to OD 490 = 0.357 obtained with the above commercial kit , with a similar amount of Anti-IL-2R monoclonal antibody absorbed into polystyrene microtiter wells. The process for the preparation of a doped, reactive, sol-gel glass embodying this invention can involve metal alkoxides, semi-metal alkoxides, metal esters or semi-metal esters monomers of the formula M(R) n (P) m in which M is a metallic or semi-metallic element, R is a hydrolyzable substituent, n is an integer between 1-6, P is a non-polymerizable substituents and m is an integer between 0-6, which are polymerized or co-polymerized in the presence of at least one first reagent with an organic polymer under acidic, neutral or basic conditions resulting in a transparent porous xerogel. M can be Si or Ti or Pb, R can be alkyl or aryl or alkoxy or aryloxy and n can be 2, 3 or 4; and the sol-gel glass can be a composite of two or more of the M(R) n monomers. With advantage the dopant is trapped in the glass by adding a solution containing the dopant to the starting polymerizing system.

Claims: A sol-gel glass for use in obtaining an interaction between at least one first reactant within the sol-gel glass and at least one second reactant that is a diffusible solute or component in an adjacent liquid or gas phase, characterised in that the sol-gel glass is an insoluble sol-gel glass of a ceramic or organo-ceramic porous material prepared by monomer polymerisation conducted through the sol-gel-xerogel stages, in that the interaction is a direct chemical interaction by intimate contact between the first and second reactants, and in that the or each said first reactant is entrapped on a molecular level in the matrix of the porous sol-gel glass. A sol-gel glass according to Claim 1, characterised in that the said first reactant is a chemically or biochemically active reagent and is entrapped in the matrix of the sol-gel glass without being rendered inactive by the entrapment. A sol-gel glass according to Claim 1 or Claim 2, characterised in that the or each said first reactant comprises: an organic compound, or an organic radical or ion, or an organometallic compound, or an inorganic compound, or a material of biological origin. A sol-gel glass according to any one of Claims 1-3, wherein the sol-gel glass is in the form of a support for the first reactant(s) and is deposited on, coated or mixed with other material, such as fibers, polymeric matrices, metals, glass or other organic and inorganic surfaces. A sol-gel glass according to any one of Claims 1-3, wherein the sol-gel glass is in the shape of a rod, sieve or has the form of a thin film coating a conventional glass plate or a metal support. A sol-gel glass according to any one of Claims 1-3 and formed as an electrode or an electrode coating for use in electrochemical testing. A sol-gel glass according to Claim 6, wherein said electrode is a piezoelectric electrode or an electrode for clinical and/or analytical and/or industrial use or as a biosensor. A sol-gel glass according to any one of Claims 1-3, wherein said entrapped first reactant comprises one or more proteins, immunoglobulins, antigens, or enzymes with enzymes with or without a co-enzyme or other co-factors. A sol-gel glass according to Claim 8, wherein during sol-gel formation the protein is entrapped in the sol-gel in the presence of a solvent or an additive. A sol-gel glass according to any one of Claims 1-3 and formed as an activity specific membrane allowing selective incorporation of the trapped molecules or ions. A sol-gel glass according to any one of Claims 1-3, wherein said first reactant comprises an organic synthesis reagent such as a redox reagent, acid-base reagent, or catalyst. A doped sol-gel glass according to any one of Claims 1-3, wherein said glass is prepared as a thin film forming molecular monolayers to macroscopic layers, or forming a part of an array of thin films. A doped sol-gel glass according to Claim 12, wherein said thin film is supported on a solid support. A doped sol-gel glass according to Claim 13, wherein said solid support includes optically photoactive material. A doped sol-gel glass according to any preceding claim and in which more than one analytical reagent is entrapped to provide a multiple purpose analytical glass. A doped sol-gel glass according to any preceding claim, wherein the distribution of the said first reactant is not homogeneous, but follows a predetermined gradient. A doped sol-gel glass according to any preceding claim and to be swallowed or implanted in the body. A process for the preparation of a doped, reactive, sol-gel glass according to any preceding claim, wherein metal alkoxides, semi-metal alkoxides, metal esters or semi-metal esters monomers of the formula M(R) n (P) m in which M is a metallic or semi-metallic element, R is a hydrolyzable substituent, n is an integer between 1-6, P is a non-polymerizable substituent and m is an integer between 0-6, are polymerized or co-polymerized in the presence of at least one first reactant with an organic polymer under acidic, neutral or basic conditions resulting in a transparent porous xerogel wherein said first reactant is able to undergo a direct chemical interaction by intimate contact with a second reactant. A process according to Claim 18, wherein M is Si or Al or Ti or Pb, R is alkyl or aryl or alkoxy or aryloxy and n is 2, 3 or 4. A process according to Claim 18 or 19, wherein the sol-gel glass is a composite of two or more of the M(R) n monomers. A process according to any one of Claims 18 to 20, wherein the dopant(s) is trapped in the glass by adding a solution containing the dopant(s) to the starting polymerizing system. The use of a sol-gel glass according to any one of Claims 1 to 17 in a method for obtaining a direct chemical interaction by intimate contact between the said at least one first reactant and the said at least one second reactant, characterised in that the or each said second reactant comprises: an organic compound, or an organic radical or ion, or an organometallic compound, or an inorganic compound, or a material of biological origin. The use of a sol-gel glass in the manner specified in Claim 22, wherein said interaction is a chemical interaction for synthesis, for adsorption, or for chemisorption. The use of a sol-gel glass in the manner specified in Claim 23, wherein said chemical interaction is an analytical test for detection or quantitative determination of an organic, inorganic or metalloorganic compound, ion or radical. The use of a sol-gel glass in the manner specified in Claim 24, wherein said chemical interaction takes place between a reactant consisting of solute/s in a liquid phase or components in a gas phase and a reactant consisting of one or more analytical reagent/s, via characteristic color-test reactions, one or other of said reactants constituting the entrapped first reactant(s). The use of a sol-gel glass in the manner specified in Claim 25, wherein the analytical reaction is a pH indicator. The use of a sol-gel glass in the manner specified in any one of Claims 22 to 26, said method for obtaining a direct chemical interaction being followed by a spectroscopic analytical method for detecting the chemical interaction. The use of a sol-gel glass in the manner specified in Claim 27, wherein said spectroscopic analytical method involves absorption or emission of electromagnetic radiation, N.M.R., or E.S.R. The use of a sol-gel glass in the manner specified in any one of Claims 22 to 28, wherein said method for obtaining a direct chemical interaction is for the analysis of ore contents, e.g. uranium in earth, rock or water. The use of a sol-gel glass in the manner specified in any one of Claims 22 to 29, said method for obtaining a direct chemical interaction being for the determination of one or more of Fe 2+ , Al 3+ , Co 2+ , Ni 2+ , SO 4 2- and Cu 2+ ions, and wherein said sol-gel glass is doped with a reagent specific for the or each ion/s. The use of a sol-gel glass in the manner specified in any one of Claims 22 to 29, said method for obtaining a direct chemical interaction being for extracting or separating molecular solutes from liquid solutions. The use of a sol-gel glass in the manner specified in Claim 31, said method for obtaining a direct chemical interaction being a chromatographic method, e.g. liquid, gas or thin layer chromatography, with or without cation and/or anion exchange. The use of a sol-gel glass in the manner specified in any one of Claims 22 to 29, said method for obtaining a direct chemical interaction being for the qualitative analysis of pollutants in food, drugs, air, soil or aquatic environments and characteristic water sources, including waste, industrial and municipal sources, lakes and swimming pools. The use of a sol-gel glass in the manner specified in Claim 33, wherein the pollutants are one or more of chlorides, nitrates, phosphates, herbicides, insecticides, inorganic ions, and pollutants of organic origin. The use of a sol-gel glass in the manner specified in Claim 33 or Claim 34, said method for obtaining a direct chemical interaction including monitoring for food degradation. The use of a sol-gel glass in the manner specified in any one of Claims 22 to 29, said method for obtaining a direct chemical interaction being for detecting inorganic ions and/or small-size organic molecules in blood, urine or other body liquids for the purpose of medical diagnosis. The use of a sol-gel glass in the manner specified in any one of Claims 22 to 29 when dependent from Claim 8, wherein said enzyme/s comprise(s) material of microbial, animal or plant origin displaying enzymatic activity and essentially free of viable cells. The use of a sol-gel glass in the manner specified in Claim 37, wherein the enzyme catalyst is used to carry out a chemical reaction in liquid organic/inorganic solvent or in a gas phase. The use of a sol-gel glass in the manner specified in Claim 37 or Claim 38, wherein the enzyme is a hydrolase e.g. trypsin, alkaline or acid phosphatase, chitinase, lipase, lactase, aminoacrylase, penicillin or cephalosporin acylase. The use of a sol-gel glass in the manner specified in Claim 37 or Claim 38, wherein the enzyme is a lyase e.g. aspartase. The use of a sol-gel glass in the manner specified in Claim 37 or Claim 38, wherein the enzyme is an oxidoreductase e.g. peroxidase, glucose oxidase. The use of a sol-gel glass in the manner specified in Claim 37, said method for obtaining a direct chemical interaction being a hormonal test. The use of a sol-gel glass in the manner specified in Claim 37, wherein one of the first and second reactants is an antibody and the other is its diffusible antigen e.g. monoclonal antibody against interleukin-2 receptor and the interleukin-2 receptor.

Inventors: AVNIR DAVID, BROWN SERGEI, OTTOLENGHI MICHAEL, ZUSMAN RIVKA, AVNIR, DAVID, BROWN, SERGEI, OTTOLENGHI, MICHAEL, ZUSMAN, RIVKA
Applicants: YISSUM RES DEV CO, YISSUM RESEARCH DEVELOPMENT COMPANY OF THE HEBREW UNIVERSITY OF JERUSALEM
Application year: 1991
Main classification: G01N31
IPC codes: C07K1, C12P1, C03C4, C12Q1, G01N33, G01N30, C12N11, G01N31, C07K16, G01N21, B01J20, G01N27, C03B8