Process for purifying acetic acid and/or acetic anhydride

Abstract: A process for removing iodide derivatives from liquid acetic acid and/or acetic anhydride comprises contacting the liquid acetic acid and/or acetic anhydride with a strong acid cation exchange resin having from about 4% to about 12% crosslinking, a surface area in the proton exchanged form of less than 10m²g⁻¹ after drying from the water wet state and a surface area of greater than 10m²g⁻¹ after drying from a wet state in which water has been replaced by methanol. The resin has at least one percent of its active sites converted to the silver form preferably from 30 to 70 percent.

Description: The present invention relates to a process for removing iodide derivatives, eg alkyl iodides and the like, from acetic acid and/or acetic anhydride. In particular the present invention is suited to purifying acetic acid and/or acetic anhydride prepared by the rhodium catalysed, methyl iodide promoted carbonylation of methanol and/or methyl acetate. It is known that a problem associated with acetic acid and/or acetic anhydride produced by carbonylation of methanol and/or methyl acetate in the presence of a rhodium/methyl iodide catalyst system is that, even after distillation, the acetic acid and/or acetic anhydride frequently contains small amounts of iodide impurities. Whilst the exact nature of these compounds is not known for certain, they probably comprise a mixture of methyl iodide and other higher alkyl iodides e.g. hexyl iodide. Such impurities are particularly troublesome since they poison many of the catalysts which are employed in subsequent chemical conversions of the acetic acid and/or acetic anhydride. A case in point is the catalysts used to prepare vinyl acetate from ethylene and acetic acid which are extremely sensitive to such impurities. Several methods of removing iodine and its compounds from acetic acid and/or acetic anhydride are known. GB 2112394A, for example, teaches the use of anion exchange resins, whilst US 4615806 and EP 296584 disclose the removal of iodide impurities from non-aqueous organic media such as acetic acid by the use of a silver or mercury containing macroreticular strong acid cation exchange resin such as Amberlyst 15 (Amberlyst is a Registered Trade Mark). A problem, however, arises when the silver loaded macroreticular resins described in US 4615806 and EP 296584 are used over a long period of time. This problem is particularly significant when preparing products with very low levels of iodide (e.g. less than 20 parts per billion (ppb)) from feeds containing up to 10 parts per million (ppm). In such cases it is found that, whilst silver loaded macroreticular resins are initially very effective, their efficiency declines significantly over a relatively short time. In practice this decline in efficiency is usually such as to render the resin unusable long before all the silver on it has been utilised. It has now been found that this problem can be overcome by the use of certain ion-exchange resins intermediate in character between macroreticular resins on the one hand and gel resins on the other. Such resins, hereafter termed mesoporous resins, are characterised by a relatively low degree of crosslinking and by the fact that, whilst they have nearly gel structures when dried from a polar solvent such as water, their pore structure can be preserved if prior to drying the water is replaced by a solvent of lower polarity such as methanol. According to the present invention there is provided a process for removing iodide derivatives from liquid acetic acid and/or acetic anhydride which comprises contacting the liquid acetic acid or acetic anhydride with a strong acid cation exchange resin having from 4% to 12% crosslinking, a surface area in the proton exchanged forms of less than 10m²g⁻¹ after drying from the water wet state and a surface area of greater than 10m²g⁻¹ after drying from a wet state in which water has been replaced by methanol, said resin having at least one percent of its active sites converted to the silver form. The process of the present invention is particularly suited to reducing the levels of iodide derivatives, eg C₁ to C₁₀ alkyl iodides, in the acetic acid or acetic anhydride from levels of up to 10 ppm down to levels of less than 10 ppb, most preferably to reducing the iodide content from 500ppb to less than 5ppb. Mesoporous resins are defined as styrene/divinyl benzene copolymers having from about 4 to about 12% preferably from 6 to 10% crosslinking. Such resins are further characterised in that when dried from the water wet state in the proton exchanged form they have a surface area of less than 10m²g⁻¹ preferably less than 8m²g⁻¹ whilst when dried from a wet state in which water has been replaced by methanol, they have a surface area greater than 10m²g⁻¹ preferably greater than 15m²g⁻¹. The surface areas given above are those measured by the nitrogen BET method and the methods used to effect drying are those referred to as METHODS A and B below. Particularily preferred examples of mesoporous resins are those materials which are sold under the trade names Purolite C145, Purolite CT145, Bayer K2441 and Bayer K2411. The amount of silver present on the resin to be used is suitably such that at least one percent of the active sites which can be occupied by metal cations are loaded, preferably 10 to 90 percent of the sites, most preferably 30 to 70 percent. The silver-loaded resins can be prepared by ion-exchange or impregnation techniques, known in the art. A preferred method is that described in EP 296584 involving slurrying a sample of the resin in the proton exchanged form with silver oxide in water and thereafter treating the slurry with a carboxylic acid preferably acetic acid. The process of the present invention is suitably carried out by passing liquid acetic acid or acetic anhydride contaminated with the iodide derivatives through a fixed bed of the resin at a predetermined rate. Preferably the resin bed is graded by backflushing before use. The feed rate used will depend on a number of variables including the amount of iodide impurities in the acetic acid or acetic anhydride, the degree of acid or anhydride purity required and the particular resin employed. Typical flow rates are in the range 0.5 to 50 bed volumes per hour, preferably 5 to 15. Optimum flow rates will depend upon temperature and can be readily determined. The temperature at which the process is carried out must be high enough to prevent acetic acid or acetic anhydride from freezing at one extreme or boiling at the other. Typical ranges are 20 to 120°C preferably 25 to 100°C. Whilst in general it is desirable to operate at as high a temperature as possible, in order to effect maximum removal, it may, in certain circumstances for reasons of economy, be desirable to operate at a lower temperature and modify one of the other process variables to reach the target level of iodide removal. The stability of the resins may also impose an upper limit on the operating temperature. The process of the present invention will now be illustrated by the following Examples. Example 1 Purolite C145 (Mesoporous Resin) 112.5 g (143 ml) of the wet resin (as supplied) was charged to a 500 ml pot equipped with a 5 cm diameter PTFE impeller. Distilled water (100 ml) was added and the mixture stirred at 60 rpm for 15 minutes. The water was then drawn off and another 100 ml of distilled water added. This procedure was then repeated (total washings 3 x 100 ml water). Silver (1) oxide (9.5 g-ex Aldrich) was added together with enough distilled water to cover the solids (ca 100 ml). The mixture was stirred at 60 rpm for 1 h at room temperature to thoroughly mix the reactants. Acetic acid (75 ml) was then added and the mixture heated to 50°C for 3 h whilst being stirred at 60 rpm. The resin was filtered off, washed with acetic acid (2 x 150 ml) and dried under flowing air. Example 2 Bayer K2411 (Mesoporous Resin) The method above was repeated using Bayer K2411 resin 125.0 g (174 ml) and silver oxide (9.5 g). Comparative Test A Amberlyst 15 (Macroreticular Resin) The method above was repeated using Amberlyst 15 resin 87.0 g (100 ml) and silver oxide (7.7 g). Comparative Test B Amberlite IR120 (Gel Resin) The method above was repeated using Amberlite IR120 resin 70 g (82 ml) and silver oxide (6.9 g). The products of Examples 1 and 2 and Comparative Tests A and B were analysed for silver. The results are shown in Table 1 below. Resin Ag (%w/w) H+ Exchange Capacity (mol/L resin ) % of Site Silver Exchanged Purolite C145 12.5 1.6 35.8 Bayer K2411 10.2 1.25 37.7 Amberlyst 15 11.8 1.8 33.5 Amberlite IR120 10.5 1.95 37.2 Surface Area Measurements on Dry Resins a. Methods for Drying the Resin METHOD A - Drying of Resin from Water Wet State A 100 ml sample of the water wet resin as supplied was heated at 105°C to achieve a final pressure of ca 0.5 mbar of mercury after 4 hours. METHOD B - Drying of Resin from Methanol Wet State A 100 ml sample of the water wet resin was washed on a coarse sinter with seven volumes of methanol (approx 5-10 minutes). Thereafter the methanol wet resin was heated to 50°C at a pressure of 20mm of mercury for 30 minutes and then at 105°C to achieve a final pressure of ca 0.5 mbar of mercury after 4 hours. b. Surface Area Measurements Methods A and B were applied to samples of the resins Purolite C145 (mesoporous) Amberlyst 15 (macroreticular), Bayer K2411 (mesoporous) and Amberlite IR 120 (Gel). The products of these experiments were then subjected to N₂ BET to measure their surface areas. Resin Type Surface Area by N₂ BET (m²/g) Drying Method A Drying Method B Purolite C145 Mesoporous 7 ± 1 20 ± 1 Amberlyst 15 Macroreticular 41 ± 1 44 ± 1 Bayer K2411 Mesoporous <5 20 ± 1 Amberlite IR120 Gel <5 <5 General Procedure for Purifying Acetic Acid 25 mls of the silver loaded resin was charged to a column (1 cm diameter) containing acetic acid. The resin bed was then backflushed to remove any fines and to classify the resin particles according to size. Acetic acid dosed with 60 ppm iodide (added as hexyl iodide) was pre-heated to 43°C and passed downflow through the resin bed heated to 43°C. The resin bed was fitted with a weir system to ensure that it operated liquid full. Samples of the treated acetic acid were collected at intervals and analysed for iodide by neutron activation analysis. Using the procedure described above silver loaded versions of the resins were tested as follows: Example 3 - Bayer K2411 (Mesoporous) Comparative Test C - Amberlyst 15 (Macroreticular) Example 4 - Purolite C145 (Mesoporous) Comparative Test D - Amberlite IR120 (Gel). The results given in Table 3 below show that under equivalent conditions the two mesoporous resins (Purolite C145 and Bayer K2411) are superior to both Amberlyst 15 (macroreticular resin) and Amberlite IR120 (gel resin) in terms of lifetime.

Claims: A process for removing iodide derivatives from liquid acetic acid and/or acetic anhydride which comprises contacting the liquid acetic acid or acetic anhydride with a strong acid cation exchange resin having from 4% to 12% crosslinking, a surface area in the proton exchanged form of less than 10m²g⁻¹ after drying from the water wet state and a surface area of greater than 10m²g⁻¹ after drying from a wet state in which water has been replaced by methanol, said resin having at least one percent of its active sites converted to the silver form. A process as claimed in claim 1 wherein the strong acid cation exchange resin has from 6 to 10% crosslinking. A process as claimed in claim 1 or claim 2 wherein the strong acid cation exchange resin has a surface area of less than 8m²g⁻¹ after drying from the water wet state and a surface area of greater than 15m²g⁻¹ after drying from a wet state in which water has been replaced by methanol. A process as claimed in any one of the preceding claims wherein from 10 to 90 percent of the active sites of the strong acid cation exchange resin are converted to the silver form. A process as claimed in claim 4 wherein from 30 to 70 percent of the active sites of the strong acid cation exchange resin are converted to the silver form. A process as claimed in any one of the preceding claims wherein the liquid acetic acid and/or acetic anhydride used as feedstock contains up to 500 parts per billion of the iodide derivatives. A process as claimed in any one of the preceding claims wherein contact between the acetic acid and/or acetic anhydride and the strong acid cation exchange resin is achieved by passing the acetic acid and/or acetic anhydride through a fixed bed of the strong acid cation exchange resin. A process as claimed in claim 7 wherein the fixed bed of the strong acid cation exchange resin is graded by backflushing before use. A process as claimed in either claim 7 or claim 8 wherein the flow rate of acetic acid and/or acetic anhydride through the fixed bed is in the range 5 to 15 bed volumes per hour.

Inventors: JONES MICHAEL DAVID, JONES, MICHAEL DAVID
Applicants: BRITISH PETROLEUM CO, THE BRITISH PETROLEUM COMPANY P.L.C.
Application year: 1991
Main classification: C07C51
IPC codes: C07C53, C07C51, B01J41