Semiconductor device having a charge transfer device, mosfets, and bipolar transistors -- all formed in a single semiconductor substrate

Abstract: A semiconductor device having a semiconductor substrate (10) of a first conductivity type, an epitaxial layer (12) of a second conductivity type formed on a major surface of the semiconductor substrate (10), an isolation layer (14) of the first conductivity type formed in the epitaxial layer (12) and extending from a surface thereof to the major surface of the semiconductor substrate (10). The isolation layer (14) divides the epitaxial layer (12) into first, second, and third islands (16, 18, 20). The device further has two wells (22, 24) of the first conductivity type, formed in the first and second islands (16, 18), respectively, and extending to the substrate (10), a charge transfer device having a back gate formed of the first well (22), an insulated-gate FET of the first conductivity type, having a back gate formed of the second island (18), an insulated-gate FET of the second conductivity type, having a back gate formed of the second well (24), and a bipolar transistor having a collector formed of the third island (20). The first island (16) surrounds the first well (22) which serves as back gate of the charge transfer device, and thus blocks the noise generated in the first well (22). Hence, the other islands (18, 20) are free from the influence of the noise.

Description: The present invention relates to a semiconductor device having a charge transfer device, and a bipolar transistor formed in a single semiconductor substrate, and to methods of manufacturing such devices. US-A-4 152 715 discloses a semiconductor device comprising a semiconductor substrate of a first conductivity type having a major surface, a region of a second conductivity type formed on the major surface of said semiconductor substrate, a first well of the first conductivity type formed in said region, a charge transfer device having a back gate formed of said first well, and a bipolar transistor having a collector formed of said region. US-A-4 646 124 discloses a method of manufacturing a semiconductor device, comprising the steps of: (a) forming an epitaxial layer on a major surface of a semiconductor substrate of a first conductivity type; (b) forming an isolation layer of the first conductivity type in said epitaxial layer, said isolation layer extending from a surface thereof to the major surface of said semiconductor substrate and dividing said epitaxial layer into first, second, and third islands (c) forming a second well in said second island, said second well being of the first conductivity type and extending into said substrate, and (d) forming an insulated-gate FET of the first conductivity type having a back gate formed of said second island (18), an insulated-gate FET of the second conductivity type having a back gate formed of said second well, and a bipolar transistor having a collector formed of said third island. The CCD delay lines are designed to delay signals by a predetermined period of time. Most circuits for processing the signals thus delay are bipolar transistor ICs which are formed on separate chips. Let us assume that the CCD and bipolar transistors are formed in the same semiconductor substrate, thus replacing the operational amplifiers having MOSFETs, such as the sample-and-hold circuit and the output circuit, with operational amplifiers comprising the bipolar transistors which operate at higher speed than the MOSFETs. In this case, the operational amplifiers have better output linearity, and the semiconductor device having the CCD and these operational amplifiers can be manufactured with higher yield and can operate with higher efficiency. In addition, the use of the bipolar transistor IC, which processes the signals output by the CCD, results in space merit, reduction of manufacturing cost, increased function, and simplified system. To make the CCD transfer an electrical charge, a transfer clock signal is supplied to the CCD. Some part of this clock signal leaks and makes noise, while being supplied through the semiconductor substrate. The noise adversely influence the bipolar transistors. In view of this, it is far from advisable to form bipolar transistors, together with a CCD, in the same semiconductor substrate. If influenced by the noise, bipolar transistors will fail to exhibit good characteristic, and the semiconductor device comprising the CCD and the bipolar transistors will have but insufficient reliability. Accordingly it is the object of this invention to provide semiconductor device which comprises a charge transfer device, bipolar transistors, and also MOSFETs -- all formed in a single semiconductor substrate -- and which operates with sufficient reliability. According to one aspect of the invention, there is provided a semiconductor device comprising, a semiconductor substrate of a first conductivity type having a major surface, a region of a second conductivity type formed on the major surface of said semiconductor substrate, a first well of the first conductivity type formed in said region, a charge transfer device having a back gate formed of said first well, and a bipolar transistor having a collector formed of said region, characterised by said region being an epitaxial layer, an isolation layer of the first conductivity type, formed in said epitaxial layer, extending from a surface thereof to the major surface of said semiconductor substrate and dividing said epitaxial layer into first, second, and third islands, said first well being in said first island and extending to said substrate, a second well of the first conductivity type formed in said second island and extending to said substrate, an insulated-gate FET of the first conductivity type having a back gate formed of said second island, an insulated-gate FET of the second conductivity type having a back gate formed of said second well, and said collector being formed of said third island. According to another aspect of the invention, there is provided a method of manufacturing a semiconductor device comprising the steps of: (a) forming an epitaxial layer on a major surface of a semiconductor substrate of a first conductivity type; (b) forming an isolation layer of the first conductivity type in said epitaxial layer, said isolation layer extending from a surface thereof to the major surface of said semiconductor substrate, and dividing said epitaxial layer into first, second, and third islands (c) forming a first well and second well in said first and second islands respectively, said first and second wells being of the first conductivity type and extending into said substrate, and (d) forming an insulated-gate FET of the first conductivity type having a back gate formed of said second island, an insulated-gate FET of the second conductivity type having a back gate formed of said second well, a bipolar transistor having a collector formed of said third island, and a charge transfer device having a back gate formed of said first well. This invention can be more fully understood from the following detailed description when taken in conjunction with the accompanying drawings, in which: Fig. 1 is a plan view showing the general structure of a semiconductor device according to a first embodiment of the present invention, in particular, an element-forming region of the device; Fig. 2 is a sectional view,- taken along line 2-2 in Fig. 1; Figs. 3A to 3D are plan views representing the electrode patterns and explaining the steps of manufacturing the device shown in Fig. 1; Figs. 4A to 4I are sectional views, explaining the steps of manufacturing the device shown in Fig. 1, Figs. 4A to 4D being taken along lines 4A-4A to 4D-4D which are shown in Figs. 3A to 3D, respectively; Figs. 5A to 5D are plan views, explaining the steps of manufacturing the second embodiment semiconductor device; and Figs. 6A to 6E are sectional views, explaining the steps of manufacturing the second embodiment device, Figs. 6A to 6D being taken along lines 6A-6A to 6D-6D shown in Figs. 5A to 5D, respectively. Several embodiments of the present invention will now be described, with reference to the accompanying drawings. [Embodiment 1] Fig. 1 is a plan view showing the general structure of a semiconductor device according to a first embodiment of the present invention. In particular, it shows the element-forming region of the semiconductor device. Fig. 2 is a sectional view, taken along line 2-2 in Fig. 1. As Figs. 1 and 2 show, an N-type silicon epitaxial layer 12 is formed on a P-type silicon substrate 10. A P-type isolation diffusion layer 14 is formed in the layer 12 by diffusing a P-type impurity into the layer 12. As is evident from Fig. 2, the layer 14 extends from the upper surface of the silicon epitaxial layer 12 to the upper surface of the silicon substrate 10, dividing the layer 12 into three N-type islands 16, 18, and 20. P-type semiconductor regions 22 and 24 are formed in the islands 16 and 18, respectively. Both regions 22 and 24 reach the P-type substrate 10. An N-channel CCD is formed on the semiconductor region 22, which serves as back gate of the N-channel CCD. A P-channel MOSFET is formed on the island 18, which serves as back gate of the p-channel MOSFET. An N-channel MOSFET is formed on the semiconductor region 24, which serves as back gate of the N-channel MOSFET. An NPN bipolar transistor is formed on the island 20, which serves as collector of the NPN bipolar transistor. As is shown in Fig. 1, the N-type island 16 surrounds the semiconductor region 22 on which the N-channel CCD is formed. Hence, the N-type island 16, 20 blocks the noise generated from the transfer clock signal supplied to the CCD, and the bipolar transistor is free of the influence of that noise. The bipolar transistor operates reliably despite that the bipolar transistor, the CCD, and the MOSFETs are formed in the same substrate 10. The islands 16, 18 and 20 are electrically floating from the substrate 10. Various potentials are applied to these islands 16, 18, and 20. More precisely, potentials VDD1, VDD2 and VDD3 are applied to the islands 16, 18, and 10 through terminals 26A, 26B and 26C, respectively. Potential VSS is applied to the substrate 10 via a terminal 26D. The potentials VDD1 to VDD3 can be varied, thereby to change the back-gate bias of the P-channel MOSFET and the collector bias of the NPN bipolar transistor. In addition, since the island 20 serves as collector of the NPN bipolar transistor, the breakdown voltage thereof can be varied to any desired value, merely by changing the thickness of the N-type epitaxial layer 12. Therefore, the characteristics of these active elements can be easily changed in accordance with the design characteristics of the semiconductor device comprising the CCD, the MOSFETs and the bipolar transistor -- all formed in the same substrate 10. The potential VDD1 is one which can absorb the noise the CCD generates. The potential VDD2 is optimal as the back-gate bias of the P-channel MOSFET. The potential VDD3 is optimal as the collector bias of the NPN bipolar transistor. With reference to Figs. 3A to 3D and Figs. 4A to 4I, it will be explained how the semiconductor device shown in Figs. 1 and 2 is manufactured, thus describing the device in greater detail. Figs. 3A to 3D are plane views representing the electrode patterns and explaining the steps of manufacturing the device shown in Fig. 1. Figs. 4A to 4I are sectional views, explaining the steps of manufacturing the device shown in Fig. 1. Figs. 4A to 4D are sectional views taken along lines 4A-4A to 4D-4D which are shown in Figs. 3A to 3D, respectively. In these figures, the component identical to those shown in Figs. 1 and 2 are denoted at the same reference numerals. As is illustrated in Figs. 3A and 4A, the surface region of the P-type silicon substrate 10, which has resistivity of 25 Ω·cm, is heated at about 1000°C and thermally oxidized, thus forming a silicon oxide film 30 having a thickness of about 1 µm. The silicon oxide film 30 is patterned by means of photoetching, thus forming windows 32 in the film 30. Antimony is diffused through these windows 32 into the P-type substrate 10, thereby forming N⁺-buried layers 34₁ to 34₃ in the substrate 10, the layers 34₁ to 34₃ having a sheet resistance of 20 Ω/□. Then, the silicon oxide film 30 is removed from the substrate 10. Then, as is shown in Figs. 3B and 4B, an N-type silicon epitaxial layer 12 containing phosphorus and having resistivity of about 5 Ω·cm is grown to the thickness of about 5 µm, on the upper surface of the resultant structure. While the layer 12 is growing, the impurities diffuse into the layer 12 from the portions forming N⁺-buried layers 34₁, 34₂ and 34₃ between the substrate 10 and the epitaxial layer 12. Theses layers 34₁, 34₂ and 34₃ have impurity concentrations higher than that of the epitaxial layer 12. Further, the surface of the epitaxial layer 12 is subjected to thermal oxidation at 1000°C, thereby forming a silicon oxide film (not shown) having a thickness of about 500 Å and serving as a photoresist pad. Then a photoresist (not shown) is formed on the silicon oxide film, a portion of the photoresist is removed by photoetching, thus forming an opening. Phosphorus ions, for example, are injected through the opening into the epitaxial layer 12, thereby forming a collector region. The remaining photoresist is removed from the silicon oxide film. Next, a photoresist is formed on the silicon oxide film. The photoresist is photo-etched, thereby openings made in the photoresist. Boron ions, for example, are injected through these openings into the epitaxial layer 12, thereby forming P-type wells and P-type isolation diffusion layers in the layer 12. The photoresist removed from the silicon oxide film. Further, an undoped CVD oxide film (not shown) having a thickness of about 3000 Å is formed on the upper surface of the resultant structure by means of a CVD method. The structure is subjected to cap annealing at about 1190°C, thereby forming, as is shown in Figs. 3C and 4C, an N⁺-collector region 42 reaching the N⁺-buried layer 34₂ two P-type wells 22 and 14, both reaching the P-type substrate 10, and also P⁺-type isolation layers 14 reaching the substrate 10. The P⁺-type isolation layers 14 isolate three islands 16, 18, and 20. The island 16 is formed of a part of the N-type epitaxial layer 12. The island 18 consists of a part of the N-type epitaxial layer 12 and N⁺-buried layer 34₁ which are electrically combined. The island 20 consists of a part of the N-type epitaxial layer 12 and N⁺-buried layer 34₂ which are electrically combined. Further, as is illustrated in Figs. 3D and 4D, a field oxide film 44 having a thickness of about 9000 Å is formed by the known LOCOS method on the upper surface of the resultant structure. Before forming the field oxide film 44, boron or phosphorus can be ion-injected into those surface portions of the structure on which the film 44 is to be formed, thereby to form channel stoppers 46 beneath the field oxide film 44. Next, as is shown in Fig. 4E, the exposed surface portion of he silicon epitaxial layer 12 are thermally oxidized at 950°C, forming a silicon oxide film 48 having a thickness of about 700 Å. This oxide film 48 will be used as the gate insulating film of the MOSFETs and as the first gate insulating film of the CCD. Boron or phosphorus is ion-injected through the film 48 into the upper surface of the structure, thus performing channel-doping. Further, a first polysilicon layer having a thickness of about 4000 Å is formed by the CVD method on the upper surface of the structure. Phosphorus is diffused into the first polysilicon layer at 950°C, using phosphoryl chloride (POCl₃) as impurity source. The first polysilicon layer is thereby rendered conductive, or made into an N⁺-type layer. Then, a photoresist is coated on the first polysilicon layer, and the photoresist is photo-etched, thus forming a mask. Using this mask, reactive ion etching (RIE) is performed on the first polysilicon layer. As a result, the first polysilicon layer is patterned, forming the first transfer gate 50₁ of the CCD, the gate 50₂ of the P-channel MOSFET, and the gate 50₃ of the N-channel MOSFET. Then, the silicon oxide film 48 is removed, by applying ammonium fluoride (NH₄F), using the gates 50₁, 50₂ and 50₃ as mask. Next, as is shown in Figs. 4F, the exposed surface portions of the silicon layer are thermally oxidized at 950°C, forming a silicon oxide film 52 having a thickness of about 700 Å. Boron ions, for example, are injected the resultant structure, by using the first transfer gate 50₁ and a photoresist (not shown) as mask, thereby forming a barrier layer (not shown) of the CCD. Further, boron ions were injected into selected portions of the silicon epitaxial layer 12 by means of photoetching, in order to form the base of the NPN bipolar transistor. The structure is annealed at 900°C, forming a P⁻-inner-base layer 54. Then, a second polysilicon layer having a thickness of about 4000 Å is formed on the upper surface of the resultant structure by, for example, the CVD method. Phosphorus diffused into the second polysilicon layer at 950°C, using phosphoryl chloride (POCl₃) as impurity source, whereby the second polysilicon layer is made conductive, or becomes an N⁺-type layer. Then, a photoresist is coated on the second polysilicon layer, and the photoresist is photoetched, thus forming a mask. Using this mask, reactive ion etching (RIE) is performed on the second polysilicon layer. As a result, the second polysilicon layer is patterned, forming the second transfer gates 56 of the CCD. Thereafter, as is shown in Fig. 4G, arsenic ions, for example, are injected into selected portions 58 of the silicon epitaxial layer 12 by means of photoetching, in order to form the N⁺-emitter of the NPN bipolar transistor, the N⁺-source/drain of the N-channel MOSFET, and the N⁺-source/drain of the CCD. Next, the exposed surface portions of the silicon layer are thermally oxidized at 900°C, forming a silicon oxide film 60 on the second transfer gates 56. Boron ions, for example, are injected to selected portions 62 of the silicon epitaxial layer 12 by means of photoetching, in order to form the P⁺-outer base of the NPN bipolar transistor, the P⁺-source/drain of the N-channel MOSFET and the N⁺-source/drain of the CCD. Then, as is shown in Fig. 4H, an interlayer insulator film 64 consisting of a silicon oxide film and a BPS (Boro-Phospho Silicate) glass film is formed on the resultant structure by means of the CVD method. More specifically, the silicon oxide film is formed on the upper surface of the structure, and then the BPS glass film is formed on the silicon oxide film. The silicate glass of the insulator film 64 is melted at about 950°C, thus performing not only glass-flowing but also phosphorous gettering. Simultaneously, the arsenic and boron, both ion-injected, are activated. As a result, there are formed the N⁺-source/drain layer 58₁ of the CCD, the N⁺-contact layer 58₂ of the island 16, the N⁺-source/drain layer 58₃ of the N-channel MOSFET, and the N⁺-emitter layer 58₄ of the NPN bipolar transistor. Also, the P⁺-source/drain 62₁ of the P-channel MOSFET, and the P⁺-outer-base layer 62₂ of the NPN bipolar transistor are formed. Further, photoetching is applied, thereby forming contact holes 66 in the interlayer insulator film 64, exposing the N⁺ layers 58₁ to 58₄ and the P⁺ layers 62₁ and 62₂. Next, as is illustrated in Fig. 4I, a metal layer made of aluminum-silicon (1%) alloy and having a thickness of about 8000 Å is formed on the upper surface of the resultant structure by means of, for example, spattering. Then, a photoresist is coated on the metal layer, and the photoresist is photo-etched, thus forming a mask. Using this mask, reactive ion etching (RIE) is performed on the metal layer. As a result, metal wirings 68₁ to 68₇ are formed. The two wirings 68₁ the source and drain wirings of the CCD, the wiring 68₂ is the bias wiring of the island 16, the two wirings 68₃ are the source and drain wirings of the P-channel MOSFET, the two wiring 68₄ are the source and drain wirings of the N-channel MOSFET. The three wirings 68₅, 68₆ and 68₇ are the emitter, base and collector wirings of the NPN bipolar transistor. Forming (?) process is performed at about 430°C, thus imparting desired characteristic to each active element. Thus manufactured is the semiconductor device according to the first embodiment of the invention, which is illustrated in Fig. 4I. This device have the advantages explained with reference to Figs. 1 and 2. [Embodiment 2] With reference to Figs. 5A to 5D and Figs. 6A to 6E, it will be explained how a semiconductor device according to a second embodiment. Figs. 5A to 5D are plane views representing the electrode patterns and explaining the steps of manufacturing the semiconductor device. Figs. 6A to 6E are sectional views, explaining the steps of manufacturing the second embodiment device. Figs. 6A to 6D are sectional views taken along lines 6A-6A to 6D-6D which are shown in Figs. 5A to 5D, respectively. The components shown in these figures, which are identical to those shown in Figs. 3A to 3D and Figs. 4A to 4I are denoted at the same reference numerals, and will not be described in detail. First, as is shown in Figs. 5A and 6A, N⁺-buried layers 34₁ and 34₂, each having a sheet resistance of 20 Ω/□, are formed in a P-type silicon substrate 30 which has a sheet resistance of 25 Ω/□. Then, as is shown in Figs. 5B and 6B, a photoresist 35 is coated on the resultant structure. A selected portion of the photoresist 35 is removed by means of photoetching, thereby forming a window 36 in the photoresist 35. Boron ions are injected into the selected portions 38A and 40 of the substrate 30 through the windows 36. Thereafter, the remaining photoresist 35 is removed from the structure. Next, as is shown in Figs. 5C and 6C, an N-type silicon epitaxial layer 12 containing phosphorus and having resistivity of about 20 Ω·cm is grown to the thickness of about 5 µm, on the upper surface of the resultant structure. While the layer 12 is growing, boron diffuses from the portions 38A and 40A of the substrate 30. As a result of this, N⁺-buried layers 34₁ and 34₂ and P⁺-buried layers 38 and 40 are formed between the substrate 30 and the epitaxial layer 12. The N⁺-buried layers 34₁ and 34₂ have impurity concentrations higher than the epitaxial layer 12, and the P⁺-buried layers 38 and 40 have impurity concentrations hither than that of the substrate 30. Thereafter, as is shown in Figs. 5D and 6D, a N⁺-type collector region 42, P-type wells 22 and 24, and a P⁺-type isolation layer 14 are formed by the same method explained with reference to Figs. 3D and 4D. The N⁺-type collector region 42 extends from the upper surface of the epitaxial layer 12 to that of the N⁺-buried layer 34₂ The P-type well 22 extends from the upper surface of the layer 12 to that of the P-type substrate 30. The P-type well 24 extends from the upper surface of the layer 12 to that of the P⁺-buried layer 40. The P⁺-type isolation layer 14 extends from the upper surface of the layer 12 to that of the P⁺-buried layer 38. The P⁺-type isolation layer 14 is divided into three islands 16, 18, and 20, in the same way as in Embodiment 1. Next, as is illustrated in Fig. 6E, a CCD whose back gate is the first well 22, a P-channel MOSFET whose back gate is the second island 18, an N-channel MOSFET whose back gate is the second well 24, and an NPN bipolar transistor whose collector is the third island 20 are formed by the same method explained with reference to Figures 4F to 4I. Thus manufactured is the semiconductor device according to the second embodiment of the invention, which is illustrated in Figure 6E. The device have the same advantages as have been described with reference to Figures 1 and 2. In addition, this device is advantageous in that it is hardly latched up and operates with high reliability since the P⁺- buried layers 38 and 40, which are formed between the P-type substrate 30 and the P-type isolation diffusion layer 14 and has an impurity concentration higher than that of the diffusion layer 14. It will be appreciated that the first island surrounds the first well which serves as back gate of the charge transfer device. Hence, the first island blocks the noise generated in the first well, and the noise influences no other islands. The device is therefore reliable despite that the charge transfer device and the bipolar transistor are formed on the same chip. Further, since the collector of the bipolar transistor is formed of the second island which, in turn, is made of epitaxial layer, the breakdown voltage of the bipolar transistor can be varied, merely by changing the thickness of the epitaxial layer. In addition, since the first and second island are electrically isolated, the collector bias of the bipolar transistor can be made to differ from the back-gate bias of the insulated-gate FET whose back gate is formed of the first island. Therefore, considerable design freedom is available.

Claims: A semiconductor device comprising: a semiconductor substrate (10) of a first conductivity type, having a major surface; a region (12) of a second conductivity type, formed on the major surface of said semiconductor substrate (10); a first well (22) of the first conductivity type, formed in said region (12); a charge transfer device having a back gate formed of said first well (22); and a bipolar transistor having a collector formed of said region (12) ; characterised by: said region (12) being an epitaxial layer; an isolation layer (14) of the first conductivity type, formed in said epitaxial layer (12), extending from a surface thereof to the major surface of said semiconductor substrate (10), and dividing said epitaxial layer (12) into first, second, and third islands (16,18,20); said first well (22) being in said first island (16) and extending to said substrate (10); a second well (24) of the first conductivity type, formed in said second island (18) and extending to said substrate (10); an insulated-gate FET of the first conductivity type, having a back gate formed of said second island (18); an insulated-gate FET of the second conductivity type, having a back gate formed of said second well (24); and said collector being formed of said third island (20). The semiconductor device according to claim 1, further comprising first and second buried layers (34₁,34₂) formed between said substrate (10) and said epitaxial layer (12) and having impurity concentrations higher than that of said epitaxial layer (12), said first and second buried layers (34₁, 34₂) being formed in said first and second islands (16,18), respectively. The semiconductor device according to claim 1 or 2, further comprising a third buried layer (38) of the first conductivity type, formed between said substrate (20) and said isolation layer (14) and having an impurity concentration higher than that of said isolation layer (14). The semiconductor device according to any preceding claim, further comprising a fourth buried layer (40) of the first conductivity type, formed between said substrate (10) and said epitaxial layer (12) and having an impurity concentration higher than that of said substrate (10). The semiconductor device according to any preceding claim wherein said charge transfer device is a CCD, and said insulated-gate FETs are MOSFETs. The semiconductor device according to any preceding claim wherein said bipolar transistor is a vertical-type bipolar transistor having a base layer (54) of the first conductivity type formed in said third island (20) of the second conductivity type, and an emitter layer (58₄) of the second conductivity type formed in said base layer (54). The semiconductor device according to any preceding claim, wherein said first, second and third islands (16,18,20) having first, second and third terminals (26A,26B,26C) to which potentials (VDD1, VDD2, VDD3) are to be applied, said potentials (VDD1 to VDD5) being different from one another. A method of manufacturing a semiconductor device, comprising the steps of: (a) forming an epitaxial layer (12) on a major surface of a semiconductor substrate (10) of a first conductivity type; (b) forming an isolation layer (14) of the first conductivity type, in said epitaxial layer (12), said isolation layer (14) extending from a surface thereof to the major surface of said semiconductor substrate (10), and dividing said epitaxial layer (12) into first, second, and third islands (16,18,20) (c) forming a first well (22) and second well (24) in said first and second islands (16,18) respectively, said first and second wells (22,24) being of the first conductivity type and extending into said substrate (10); and (d) forming an insulated-gate FET of the first conductivity type having a back gate formed of said second island (18), an insulated-gate FET of the second conductivity type having a back gate formed of said second well (24), a bipolar transistor having a collector formed of said third island (20), and a charge transfer device having a back gate formed of said first well (22).

Inventors: TAGUCHI MINORU, TAGUCHI, MINORU, TAGUCHI, MINORU, C/O INTELLECTUAL PROP. DIV.
Applicants: TOSHIBA KK, KABUSHIKI KAISHA TOSHIBA
Application year: 1991
Main classification: H01L27
IPC codes: H01L27, H01L21, H01L29