Alkoxysilanes

Abstract: Novel alkoxysilanes of the general formula: wherein letter a is equal to 2 or 3, b is equal to 0, 1, 2 or 3, and n is an integer of from 2 to 10 are useful agents for controlling curing reaction of addition type curable silicone compositions.

Description: This invention relates to alkoxysilanes, and to their use for controlling curing reaction of addition type curable silicone compositions. Prior art well-known agents for controlling curing reaction of addition type curable silicone compositions include acetylene alcohols, alkoxysilanes and alkoxysiloxanes derived from acetylene alcohols, and low molecular weight organovinylsiloxanes. These compounds, however, are not fully satisfactory curing control agents. There is a need for different compounds as curing control agents, and also for compounds which are more effective. Making investigations in search of useful agents for controlling curing reaction of addition type curable silicone compositions, the inventors have found that alkoxysilanes conforming with the formula: wherein letter a is equal to 2 or 3, b is equal to 0, 1, 2 or 3, and n is an integer of from 2 to 10 are obtainable, for example, by effecting hydrosilylation between a chlorohydrogensilane and a vinylchlorosilane and effecting dehydrochlorination between the resulting 1,2-bis(chlorosilyl)ethane and 1,1-dimethylpropargyl alcohol. Such alkoxysilanes are useful control agents for curing reaction of addition type curable silicone compositions. The alkoxysilanes of formula (I) may be prepared from two types of readily available monosilane reactants by a relatively simple synthesis process and purified by distillation. Then when added to addition type curable silicone compositions as a curing reaction control agent, a certain amount of the alkoxysilane provides curing reaction control to a constant extent independent of its particular manufacturing lot. Curing of silicone compositions can be precisely controlled in a reproducible manner. Also, we have found that such alkoxysilanes generally have an extremely low vapor pressure at room temperature so that curable silicone compositions containing the alkoxy silane control agent may have a satisfactory life time and little alter their curing behavior when the compositions are subjected to vacuum debubbling prior to their use. When the compositions are heat cured at temperatures between 150°C and 180°C, cured products may then avoid the risk of differential curing between the surface and the interior which would otherwise impair the outer appearance. Although US-A-4 839 452 (equivalent to JP-A-11160/1989) and Japanese Patent Publication No. 2627/1989 disclose α-ethynylalkoxysilanes having a hydrogen atom or a substituted or unsubstituted alkyl or aryl group attached to a silicon atom, the alkoxysilanes of formula (I) characterized by the attachment of an α-ethynylalkoxy group to a silicon atom of silethylene are novel compounds that the inventors have discovered. The present invention provides alkoxysilanes of formula (I). Other aspects are methods of making these alkoxysilanes, and their use as cure control agents in addition-curable silicone compositions. In formula (I), letter a is equal to 2 or 3, b is equal to 0, 1, 2 or 3, and n is an integer of from 2 to 10. Exemplary are α-ethynylalkoxysilanes of the following formulae. We have been able to prepare alkoxysilanes of formula (I) according to the invention, simply by effecting hydrosilylation between a chlorohydrogensilane having a hydrogen atom attached to the silicon atom and an alkenylchlorosilane having a C₂₋₁₀ alkenyl group attached to the silicon atom such as vinyl and allyl to form a bis(chlorosilyl)ethane, and subjecting the bis(chlorosilyl)ethane to dehydrochlorination using 1,1-dimethylpropargyl alcohol. For example, the α-ethynylalkoxysilanes of formulae (Ia) and (Ib) illustrated above may be synthesized according to the following reaction scheme. For reaction between a chlorohydrogensilane and an alkenylchlorosilane, they are preferably mixed in a molar ratio of from 2:3 to 3:2, especially in an equimolar ratio. In general, hydrosilylation occurs in the presence of a platinum group metal addition reaction catalyst. The reaction conditions include 60 to 120°C and 1 to 5 hours although need not be limited thereto. The platinum group metal addition reaction catalysts used herein include platinum group, palladium group and rhodium group catalysts, with the platinum group catalysts being preferred. Examples of the platinum group catalysts include platinum black, solid platinum on alumina, silica or similar supports, chloroplatinic acid, alcohol-modified chloroplatinic acid, chloroplatinic acid-olefin complexes, and platinum-vinylsiloxane complexes. The platinum group metal addition reaction catalysts may be used in a catalytic amount, preferably 0.1 to 500 ppm, especially 2 to 200 ppm of platinum group metal based on the total weight of chlorosilane and alkenylchlorosilane. Hydrosilylation may be effected simply by adding dropwise a chlorohydrogensilane to a reactor charged with an alkenylchlorosilane and a platinum group catalyst, for example, thereby forming a bis(chlorosilyl)ethane. A subsequent step is dehydrochlorination between the bis(chlorosilyl)ethane and 1,1-dimethylpropargyl alcohol. Desirably, 1,1-dimethylpropargyl alcohol is added in a molar amount of 1 to 5 times, especially 1.2 to 2 times the mole of ≡Si-Cl group in the bis(chlorosilyl)ethane. This reaction is preferably carried out in the presence of an agent for promoting dehydrochlorination such as urea, which is preferably added in a molar amount of 1 to 5 times, especially 1.5 to 2.5 times the mole of ≡Si-Cl group in the bis(chlorosilyl)ethane. The preferred reaction conditions include 50 to 70°C and 3 to 6 hours with optional adjustment. Dehydrochlorination may be effected simply by adding dropwise a bis(chlorosilyl)ethane to a reactor charged with 1,1-dimethylpropargyl alcohol and a promoting agent, for example, thereby forming an end alkoxysilane. There have been described novel alkoxysilanes of formula (I), preparable e.g. from two types of readily available monosilane reactants by a relatively simple synthesis process and purified by distillation. By adding a predetermined amount of the alkoxysilane to addition type curable silicone compositions as a curing reaction control agent, curing reaction can be controlled to a consistent extent corresponding to the additive amount regardless of an alkoxysilane manufacturing lot. This enables precise reproducible control on silicone composition curing. In addition, because of their extremely low vapor pressure at room temperature, the alkoxysilanes allow a working life for the curable silicone compositions. When the curable silicone compositions are subjected to vacuum debubbling prior to their use, the compositions do not alter their curing behavior. Upon heat curing at temperatures between 150°C and 180°C, cured products do not undergo differential curing between the surface and the interior and present a good outer appearance. Therefore, the alkoxysilanes which we have made are useful as agents for controlling curing reaction of addition type curable silicone compositions or the like. Eliminated variation in quality of the alkoxysilanes among different manufacturing lots is evident from the fact that these alkoxysilanes are monomers having a definite molecular structure and can be isolated by distillation. EXAMPLE Examples of the present invention are given below by way of illustration and not by way of limitation. Example 1 A reactor was charged with 42.3 grams (0.30 mol) of methylvinyldichlorosilane and 0.1 ml of a 2-ethylhexyl alcohol solution containing 2% chloroplatinic acid. To the reactor was added dropwise 34.5 grams (0.30 mol) of methyldichlorosilane. After the completion of addition, stirring was continued for a further one hour. After cooling, the reaction solution was distilled, obtaining 74.5 grams (yield 97%) of 1,2-bis(methyldichlorosilyl)ethane having a boiling point of 109-110°C/30 mmHg. Next, a reactor was charged with 126.2 grams (1.50 mol) of 1,1-dimethylpropargyl alcohol and 91.3 grams (1.52 mol) of urea and heated to 55°C. To the reactor was added dropwise 64.0 grams (0.25 mol) of 1,2-bis(methyldichlorosilyl)ethane obtained in the previous step. After the completion of addition, the reaction solution was stirred for 3 hours at a temperature of 50 to 60°C, cooled, washed three times with 50 ml of saturated sodium chloride water, dried over 12 grams of anhydrous sodium sulfate, and filtered. Distillation of the filtrate gave 64.7 grams (yield 58%) of a fraction having a boiling point of 127-130°C/3 mmHg. This fraction was examined by infrared absorption spectrum, NMR spectrum, and elemental analysis. The results are shown below, by which the fraction was identified to be a compound of the following formula. (a) to (d) are references for the description of NMR spectrum. IR spectrum: absorption peak, cm⁻¹ 3310 (ethynyl H-C) 2120 (ethynyl C≡C) 1260 (methyl CH₃-Si) 1140 (silethylene Si-CH₂CH₂-Si) NMR spectrum: shift, ppm (δ) (in CCl₄, internal standard CHCl₃) 2.19 (S, 2H) (a) 1.52 (S, 12H) (b) 0.93-0.82 (t, 2H) (c) -0.03 (S, 3H) (d) Example 2 As in Example 1, 53.3 grams (0.33 mol) of vinyl-trichlorosilane was reacted with 46.1 grams (0.34 mol) of trichlorosilane to obtain 96.0 grams (yield 98%) of 1,2-bis(trichlorosilyl)ethane. Next, a reactor was charged with 208.3 grams (2.48 mol) of 1,1-dimethylpropargyl alcohol and 150.2 grams (2.50 mol) of urea and heated to 55°C. To the reactor was added dropwise 81.7 grams (0.28 mol) of 1,2-bis(trichlorosilyl)ethane obtained in the previous step. After the completion of addition, the reaction solution was stirred for 5 hours at a temperature of 50 to 60°C, cooled, washed three times with 75 ml of saturated sodium chloride water, dried over 17 grams of anhydrous sodium sulfate, and filtered. Distillation of the filtrate gave 83.4 grams (yield 52%) of a fraction having a boiling point of 107-110°C/6x10⁻⁴ mmHg. This fraction was examined by infrared absorption spectrum, NMR spectrum, and elemental analysis. The results are shown below, by which the fraction was identified to be a compound of the following formula. (a) to (c) are references for the description of NMR spectrum. IR spectrum: absorption peak, cm⁻¹ 3300 (ethynyl H-C) 2120 (ethynyl C≡C) 1150 (silethylene Si-CH₂CH₂-Si) NMR spectrum: shift, ppm (δ) (in CCl₄, internal standard CHCl₃) 2.26 (S, 3H) (a) 1.58 (S, 18H) (b) 0.91-0.79 (t, 2H) (c) Due to their low vapor pressure, the alkoxysilanes of the present invention are effective as a curing reaction control agent for addition curing silicones. Example 3 shows the effectiveness of the alkoxysilanes as a curing control agent. In Example 3, parts are by weight, and the procedures of mixing, deaeration and viscosity measurement are at 25°C. Example 3 Two mixtures were prepared by mixing 100 parts of dimethylpolysiloxane end capped with a vinyldimethylsilyl group having a viscosity of 1,000 centipoise with 8 parts of methylhydrogenpolysiloxane of the following formula: and further adding thereto 0.01 part of silane compound (a) or (b). Next, compositions A and B were prepared by adding a solution of chloroplatinic acid in 2-ethylhexyl alcohol to each of the mixtures such that the platinum content was 5 ppm based on the total weight and thoroughly milling the mixture. The compositions A and B were deaerated by allowing them to stand in a vacuum for a certain time. After deaeration, compositions A and B were allowed to stand in a constant temperature chamber at 25°C. Table 1 reports the viscosity of the compositions after 30 minutes and 6 hours from the completion of mixing. Separately, deaerated compositions A and B were cured by heating at 150°C. Table 2 reports the time required to complete curing and the appearance of cured products. For comparison purposes, compositions C, D, and E were prepared by the same procedure as above except that the silane compound was replaced by the following silane compounds (c), (d), and (e). The compositions C, D, and E were deaerated in vacuum and then heat cured as in Example 1. The viscosity of the deaerated compositions and the appearance of the cured compositions are reported in Tables 1 and 2. It is evident that a curable silicone composition having an alkoxysilane blended as a curing control agent gives little change in curing behavior when the composition is deaerated in vacuum prior to use. A curable silicone composition having an alkoxysilane blended as a curing control agent can be heat cured at 150°C into a cured product free of a defect in outer appearance which is otherwise induced by uneven curing.

Claims: An alkoxysilane of the general formula: wherein a is 2 or 3; b is 0, 1, 2 or 3, and n is an integer of from 2 to 10. An alkoxysilane according to claim 1 in which n is 2. An alkoxysilane of claim 2 which is of the formula An alkoxysilane of claim 2 which is of the formula Use of an alkoxysilane as defined in any one of claims 1 to 4, as a cure control agent in an addition-curable silicone composition. Use according to claim 5 in which the curable silicone composition mixed with the cure control agent is vacuum-debubbled before cure. A method of preparing an alkoxysilane as defined in any one of claims 1 to 4, comprising a step of effecting hydrosilylation between a chlorohydrogensilane having a hydrogen atom on the silicon atom and an alkenylchlorosilane having a C₂₋₁₀ alkenyl on the silicon atom. A method according to claim 7, in which the hydrosilylation is in the presence of a platinum group metal addition reaction catalyst. A method according to claim 8 or claim 7, further comprising reacting the hydrosilylation product with 1,1-dimethylpropargyl alcohol in a dehydrochlorination reaction to form the alkoxysilane of formula (I). A method according to claim 9, in which the alkoxysilane of formula (I) is purified by distillation.

Inventors: FUJIKI HIRONAO, TAKAHASHI TOSHIAKI, FUJIKI, HIRONAO, TAKAHASHI, TOSHIAKI
Applicants: SHINETSU CHEMICAL CO, SHIN-ETSU CHEMICAL CO., LTD.
Application year: 1991
Main classification: C07F7
IPC codes: C07F7, C08L83