Method for manufacturing superconducting device having a reduced thickness of oxide superconducting layer and superconducting device manufactured thereby

Abstract: For manufacturing a superconducting device, a first c -axis orientated oxide superconductor thin film having a very thin thickness is formed on a principal surface of a substrate, and a stacked structure of a gate insulator and a gate electrode is formed on a portion of the first oxide superconductor thin film. An a -axis orientated oxide superconductor thin film is grown, using the gate electrode as a mask, so that a second and third superconducting regions having a relatively thick thickness are formed at both sides of the gate electrode, electrically isolated from the gate electrode. The superconducting device thus formed can functions as a super-FET.

Description: SPECIFICATION Background of the Invention Field of the invention The present invention relates to a method for manufacturing a superconducting device, and more specifically to a method for manufacturing a superconducting device including an oxide superconducting layer having a partially reduced thickness portion forming a superconducting channel controlled by a gate electrode, and a superconducting device manufactured by the method. Description of related art Typical three-terminal devices which utilize a superconductor include a so called superconducting-base transistor and a so called super-FET (field effect transistor). The superconducting-base transistor includes an emitter of a superconductor or a normal conductor, a tunnel barrier of an insulator, a base of a superconductor, a semiconductor isolator and a collector of a normal conductor, stacked in the named order. This superconducting-base transistor operates at a high speed with a low power consumption, by utilizing high speed electrons passing through the tunnel barrier. The super-FET includes a semiconductor layer, and a superconductor source electrode and a superconductor drain electrode which are formed closely to each other on the semiconductor layer. A portion of the semiconductor layer between the superconductor source electrode and the superconductor drain electrode has a greatly recessed or undercut rear surface so as to have a reduced thickness. In addition, a gate electrode is formed through a gate insulator layer on the recessed or undercut rear surface of the portion of the semiconductor layer between the superconductor source electrode source and the superconductor drain electrode. A superconducting current flows through the semiconductor layer portion between the superconductor source electrode and the superconductor drain electrode due to a superconducting proximity effect, and is controlled by an applied gate voltage. This super-FET also operates at a high speed with a low power consumption. In addition, in the prior art, there has been proposed a three-terminal superconducting device having a channel of a superconductor formed between a source electrode and a drain electrode, so that a current flowing through the superconducting channel is controlled by a voltage applied to a gate formed above the superconducting channel. Both of the above mentioned superconducting-base transistor and the super-FET have a portion in which a semiconductor layer and a superconducting layer are stacked to each other. However, it is difficult to form a stacked structure of the semiconductor layer and the superconducting layer formed of an oxide superconductor which has been recently advanced in study. In addition, even if it is possible to form a stacked structure of the semiconductor layer and the oxide superconducting layer, it is difficult to control a boundary between the semiconductor layer and the oxide superconducting layer. Therefore, a satisfactory operation could not been obtained in these superconducting devices. In addition, since the super-FET utilizes the superconducting proximity effect, the superconductor source electrode and the superconductor drain electrode have to be located close to each other at a distance which is a few times the coherence length of the superconductor materials of the superconductor source electrode and the superconductor drain electrode. In particular, since an oxide superconductor has a short coherence length, if the superconductor source electrode and the superconductor drain electrode are formed of the oxide superconductor material, a distance between the superconductor source electrode and the superconductor drain electrode has to be not greater than a few ten nanometers. However, it is very difficult to conduct a fine processing such as a fine pattern etching so as to ensure the very short separation distance. Because of this, in the prior art, it has been impossible to manufacture the super-FET composed of the oxide superconductor material. Furthermore, it has been confirmed that the conventional three-terminal superconducting device having the superconducting channel shows a modulation operation. However, the conventional three-terminal superconducting device having the superconducting channel could not realize a complete ON/OFF operation, because a carrier density is too high. In this connection, since an oxide superconductor material has a low carrier density, it is expected to form a three-terminal superconducting device which has a superconducting channel and which can realize the complete ON/OFF operation, by forming the superconducting channel of the oxide superconductor material. In this case, however, a thickness of the superconducting channel has to be made on the order of 5 nanometers. Summary of the Invention Accordingly, it is an object of the present invention to provide a method for manufacturing a superconducting device, which have overcome the above mentioned defects of the conventional ones. Another object of the present invention is to provide a method for manufacturing an FET type superconducting device including an oxide superconducting layer having an extremely thin portion forming a superconducting channel, with a good repeatability by using existing established processing techniques. Still another object of the present invention is to provide an FET type superconducting device having a unique structure which have overcome the above mentioned defects of the conventional ones. The above and other objects of the present invention are achieved in accordance with the present invention by a method for manufacturing a superconducting device, the method comprising the step of preparing a substrate having a principal surface thereof, forming a c -axis orientated oxide superconductor thin film having a very thin thickness on the principal surface of the substrate, forming on a portion of the c -axis orientated oxide superconductor thin film a stacked structure including a gate insulator formed directly on the c -axis orientated oxide superconductor thin film and a gate conductor formed on the gate insulator, growing an a -axis orientated oxide superconductor thin film, using the gate electrode as a mask, so that superconducting regions having a relatively thick thickness are formed of a -axis orientated oxide superconductor thin films at both sides of the gate electrode, electrically isolated from the gate electrode, and forming a superconducting source region and a superconducting drain region, respectively. According to another aspect of the present invention, there is provided a superconducting device which comprises a substrate having a principal surface, a first oxide superconducting region of an extremely thin thickness formed on the principal surface of the substrate, second and third oxide superconducting regions of a relatively thick thickness formed near each end of the first oxide superconducting region separated from each other, the first oxide superconducting region being electrically connected to the second and third oxide superconducting regions to bridge the second and third oxide superconducting regions and to form a superconducting channel between the second and third oxide superconducting regions, so that a superconducting current can flow through the superconducting channel between the second and third oxide superconducting regions, and a gate electrode formed on a gate insulator placed on the first oxide superconducting region controlling the superconducting current flowing through the superconducting channel, the first oxide superconducting regions being formed of a c -axis orientated oxide superconductor thin film, the second and third oxide superconducting regions being formed of a -axis orientated oxide superconductor thin films, and the gate electrode being electrically isolated from the first, second and third oxide superconducting regions. In a preferred embodiment, the oxide superconductor thin film is formed of a material selected from the group consisting of a Y-Ba-Cu-O type compound oxide superconductor material, a Bi-Sr-Ca-Cu-O type compound oxide superconductor material, and a Tl-Ba-Ca-Cu-O type compound oxide superconductor material. In addition, the substrate, on which the oxide superconductor thin film is deposited, can be formed of an insulating substrate, preferably an oxide single crystalline substrate such as MgO, SrTiO₃, CdNdAlO₄, etc. These substrate materials are very effective in forming or growing a crystalline film having a high orientation property. However, the superconducting device can be formed on a semiconductor substrate if an appropriate buffer layer is deposited thereon. For example. the buffer layer on the semiconductor substrate can be formed of a double-layer coating formed of a MgAl₂O₄ layer and a BaTiO₃ layer if silicon is used as a substrate. In the superconducting device manufactured in accordance with the present invention, the superconducting current flowing between the second and third oxide superconducting regions through the superconducting channel formed of the first oxide superconducting region is controlled by a voltage applied to the gate electrode. Namely, the superconducting device constitutes the super-FET. In order to ensure that the superconducting channel can be turned on and off by a voltage applied to the gate electrode, a thickness of the superconducting channel has to be on the order of 5 nanometers in the direction of an electric field created by the voltage applied to the gate electrode. This extremely thin Superconducting channel can be easily realized or formed in accordance with tho method of the present invention. For example, the c -axis orientated oxide superconductor thin film is formed to have the thickness on the order of about 5 nanometers. This extremely thin oxide superconductor thin film can be formed in a conventional process by precisely controlling both of the thin film growth speed and the growth time. For this purpose, a sputtering can be used. However, since the oxide superconductor crystal has a multi-layer structure in which respective constituent elements are stacked in a layered structure, it is possible to stack a desired number of unit cells of oxide superconductor, by using a MBE (molecular beam epitaxy). In another preferred embodiment, the c -axis orientated oxide superconductor thin film is formed to have the thickness on the order of about 20 nanometers. An upper portion of the c -axis orientated oxide superconductor thin film having a thickness of more than 10 nanometers is changed into an oxide insulating layer so that a lower portion of the c -axis orientated oxide superconductor thin film becomes a superconducting channel having a thickness of about 5 nanometers. To change the upper portion of the c -axis orientated oxide superconductor thin film to the oxide insulating layer, the c -axis orientated oxide superconductor thin film is heated under high vacuum. Oxygen of crystals of an oxide superconductor escapes when the oxide superconductor is heated under vacuum. Superconducting properties of an oxide superconductor is sensitive to amounts of oxygen which is included in the crystals of the oxide superconductor. If the crystals of the oxide superconductor lack oxygen, the critical temperature of the oxide superconductor lowers considerably or the oxide superconductor loses its superconductivity. Therefore, the upper portion of the c -axis orientated oxide superconductor thin film is changed into an oxide insulating layer substantially and the extremely thin oxide superconductor thin film can be formed. The thickness of the oxide insulating layer is controlled by the heat process time. It is preferable to etch the oxide superconductor film so that side surfaces of a portion which will be changed into the oxide insulating layer, which are parallel to the c -axes of crystals of oxide superconductor, are exposed, since the oxygen of crystals of oxide superconductor migrates to a direction perpendicular to the c -axis of crystals of oxide superconductor easier. The extremely thin c -axis orientated oxide superconductor thin film thus formed or deposited is very preferable in thickness and the crystal orientation to form a superconducting channel, but insufficient in thickness and inadequate in the crystal orientation to form a superconducting source region and a superconducting drain region. Therefore, the superconducting layer in the superconducting source region and the superconducting drain region must be further thickened and formed of an a -axis orientated oxide superconductor thin film. The above mentioned method in accordance with the present invention is very effective in forming the superconducting source region and the superconducting drain region of an a -axis orientated oxide superconductor thin film having enough thickness while maintaining the thickness of the extremely thin oxide superconductor thin film constituting the superconducting channel. Namely, in one preferred embodiment, a gate electrode is formed on the extremely thin c -axis orientated oxide superconductor thin film at a position corresponding to the superconducting channel, and the c -axis orientated oxide superconductor thin film is selectively etched and removed excluding the superconducting channel so that a portion of the substrate is exposed and the a -axis orientated oxide superconductor thin film is deposited or grown on the exposed substrate, using the gate electrode as a mask. It is preferable that normal conductor members which are formed of a metal stable to the oxide superconductor such as Au, Pt are arranged between the superconducting channel and the superconducting source region and between the superconducting channel and the superconducting drain region. These normal conductor members prevent oxygen of the superconducting channel from escaping while the superconducting source region and the superconducting drain region are formed, and prevent the c -axis orientated oxide superconductor thin film from interfering the a -axis orientated oxide superconductor thin films. Therefore, the c -axis orientated oxide superconductor thin film and the a -axis orientated oxide superconductor thin films have high degree of crystallinity and orientation. The normal conductor members have thickness which may not disturb the superconducting current flow by penetrating between the superconducting channel and superconducting source region and between the superconducting channel and superconducting drain region. In another preferred embodiment, a gate electrode is formed on the rather thin c -axis orientated oxide superconductor thin film at a position corresponding to the superconducting channel, and at the same time, the c -axis orientated oxide superconductor thin film is selectively etched so that the portion under the gate electrode projects from an etched portion and the a -axis orientated oxide superconductor thin film is deposited or grown on an etched surface of the c -axis orientated oxide superconductor thin film. In one preferred embodiment, both side surfaces of the gate electrode are covered with insulating side-walls, and the second deposition or growth of the a -axis orientated oxide superconductor thin film is performed until the gate electrode is completely embedded in the a -axis orientated oxide superconductor thin film, and thereafter, the a -axis orientated oxide superconductor thin film is planarized until an upper surface of the gate electrode is exposed at the planarized upper surface of the a -axis orientated oxide superconductor thin film. In this process, although the gate electrode is embedded in the a -axis orientated oxide superconductor thin film, the gate electrode is electrically isolated from the oxide superconductor thin film by the gate insulator and the side insulating layer. As seen from the above, the method in accordance with the present invention includes no process which requires high-precision for forming the superconducting channel. Therefore, the limitation in the fine processing techniques required for manufacturing the super-FET can be relaxed. The above and other objects, features and advantages of the present invention will be apparent from the following description of preferred embodiments of the invention with reference to the accompanying drawings. Brief Description of the Drawings Figures 1A to 11 are diagrammatic sectional views for illustrating a first embodiment of the method in accordance with the present invention for manufacturing the superconducting device; and Figures 2A to 2F are diagrammatic sectional views for illustrating featured steps of a second embodiment of the method in accordance with the present invention for manufacturing the superconducting device. Description of the Preferred embodiments Referring to Figures 1A to 1I, the process in accordance with the present invention for manufacturing the super-FET will be described. As shown in Figure 1A, a substrate 5 having a substantially planar principal surface is prepared. This substrate 5 is formed of for example, an insulator substrate such as a MgO (100) substrate, a SrTiO₃ (100) substrate, a CdNdAlO₄ (001) substrate or others, or a semiconductor substrate such as a silicon substrate having a principal surface coated with a buffer layer composed of an insulating film. In the case of the silicon substrate, the principal surface of the silicon is preferably coated with MgAl₂O₄by a CVD (chemical vapor deposition) and also with BaTiO₃ by a sequential sputtering process. As shown in Figure 1B, an extremely thin c -axis orientated Y₁Ba₂Cu₃O 7-δ oxide superconductor thin film 11 having a thickness on the order of about 5 nanometers is deposited on the principal surface of the substrate 5, by for example an off-axis sputtering, a reactive evaporation, an MBE (molecular beam epitaxy), a CVD, etc. This extremely thin oxide superconductor thin film 11 forms a superconducting channel 10 when the super-FET is completed. The superconducting channel is preferably formed of c -axis orientated thin film, since the c -axis orientated thin film has a large critical current density in the direction in parallel to the substrate surface. A condition of forming the c -axis orientated Y₁Ba₂Cu₃O 7-δ oxide superconductor thin film 11 by off-axis sputtering is as follows: The oxide superconductor thin film is preferably formed of, for example, a Bi-Sr-Ca-Cu-O type compound oxide superconductor material, or a Tl-Ba-Ca-Cu-O type compound oxide superconductor material other than Y-Ba-Cu-O type compound oxide superconductor material. Then, as shown in Figure 1C, an insulating layer 16 is deposited on the oxide superconductor thin film 11. The insulating layer 16 is deposited to have a thickness of not less than 10 nanometers which is sufficient to prevent a tunnel current. In addition, the insulating layer 16 is formed of an insulating material such as MgO, which does not form a large density of energy levels between the superconductor thin film 11 and the insulating layer 16. Furthermore, from the viewpoint of a mechanical stress, it is preferred to form on the oxide superconductor thin film 11 an insulating layer having a composition similar or analogous to that of the oxide superconductor thin film 11, without taking out the substrate 5 from a film deposition apparatus of chamber after the oxide superconductor thin film 11 is deposited on the substrate 5. Thereafter, as shown in Figure 1D, a normal conducting layer 17 is deposited on the insulating layer 16 and a refractory layer 9 is deposited on the normal conducting layer 17. The normal conducting layer 17 can be deposited by a vacuum evaporation or any other suitable process, so as to have a thickness of about 200 nanometers. The normal conducting layer 17 can be formed of Au, or a refractory metal such as Ti, W or a silicide thereof. The insulating layer 16 and the normal conducting layer 17 are preferably deposited continuously on the oxide superconductor thin film 11, without taking out the substrate 5 from a film deposition apparatus or chamber. The refractory layer 9 is formed of a refractory metal such as Mo etc., a refractory resist, an insulating layer and can be deposited by a vacuum evaporation etc. The refractory layer 9 is selectively etched so as to remove all of the refractory layer excluding a portion 91 which is above the super conducting channel and to form a gate electrode pattern, as shown in Figure 1E. Thereafter, as shown in Figure 1F, the stacked layer of the oxide superconductor thin film 11, the insulating layer 16 and the normal conducting layer 17 is selectively removed so as to form a superconducting channel 10, a gate insulator 6 and a gate electrode 4. For this purpose, the normal conducting layer 17, the insulating layer 16 and the oxide superconductor thin film 11 are selectively etched in a self alignment to the patterned refractory mask 91, so as to remove all of the metal layer excluding a portion which becomes the gate electrode on the superconducting channel 10, so that the gate electrode 4 is formed, and a gate insulator 6 is left on the oxide superconductor thin film 11 and only under the patterned gate electrode 4, and a superconducting channel 10 is left on the substrate 5, and the substrate 5 is exposed excluding a portion under the superconducting channel 10. In this connection, it is desired that the gate electrode 4 and the gate insulator 6 are side-etched in comparison with the superconducting channel 10, so that the gate electrode 4 has a length shorter than that of the superconducting channel 10 and the gate insulator 6 has a length shorter than that of the gate electrode 4. Thereafter, as shown in Figure 1G, normal conductor members 12 and 13 are formed on the both ends of the superconducting channel 10. These normal conductor members 12 and 13 can be formed by depositing an Au layer covering the superconducting channel 10 and exposing portion of the substrate 5, and etching back deposited Au layer by means of an anisotropic etching so that the Au layer remains only on the side surfaces of the superconducting channel 10. Then, as shown in Figure 1H, a superconducting source region 2 and a superconducting drain region 3 of an a -axis orientated Y₁Ba₂Cu₃O 7-δ oxide superconductor thin film are formed on the substrate 5 at both sides of the superconducting channel 10, respectively. An a -axis orientated Y₁Ba₂Cu₃O 7-δ oxide superconductor thin film can be formed by an off-axis sputtering process which is carried out under a condition that the substrate temperature is not higher than 650°C. A sputtering condition under which the superconducting source region 2 and the superconducting drain region 3 are formed is as follows: At the same time, an a-axis orientated oxide superconductor thin film 20 is deposited on the refractory mask 91, however, the refractory mask 91 which is formed of Mo sublimates while the oxide superconductor thin film is deposited. With this the super-FET in accordance with the present invention is completed, as shown in Figure 1I. The oxide superconductor thin film 20 can be left above the gate electrode 4, in the case of using an insulator as the refractory mask 91. As explained above, if the super-FET is manufactured in accordance with the first embodiment of the method of the present invention, the limitation in the fine processing technique required for manufacturing the super-FET is relaxed. Since the flatness of the upper surface of the superconducting device can be improved, it become easy to form conductor wiring in a later process. Accordingly, it is easy to manufacture the super-FET with good repeatability, and the manufactured super-FET has a stable performance. Referring to Figures 2A to 2G, a second embodiment of the process for manufacturing the superconducting device will be described. In this second embodiment, the same processings as those shown in Figures 1A to 1B are performed except that the c -axis oxide superconductor thin film 11 is formed having a thickness on the order of 20 nanometers. After the c -axis orientated oxide superconductor thin film 11 is deposited,as shown in Figure 2A, a normal conducting layer 17 is deposited on the oxide superconductor thin film 11 by a CVD, a sputtering, etc. The normal conducting layer 17 can be formed of Au, or a refractory metal such as Ti, W or a silicide thereof. As shown in Figure 2B, the normal conducting layer 17 is selectively etched so as to remove all of the normal conducting layer excluding a portion which becomes the gate electrode on the superconducting channel 10, so that the gate electrode 4 is formed. Then, the oxide superconductor thin film 11 is selectively etched more than 10 nanometers in a self alignment to the patterned gate electrode 4, so that a portion under the patterned gate electrode 4 projects from the etched portion of the oxide superconductor thin film 11. Thereafter, the substrate 5 is heated to more than 400°C under a pressure of 10⁻⁵ Pa. Then, as shown in Figure 2C, oxygen of the crystals of the portion of the oxide superconductor thin film 11 under the patterned gate electrode 4 escapes through side surfaces 18 and 19 so that the portion changes to the gate insulator 6. The portion of the oxide superconductor thin film 11 under the gate insulator 6 becomes superconducting channel 10. An oxide superconductor loses its superconductivity when it lacks oxygen of its crystals. Therefore, after the process, the oxide which forms gate insulator 6 becomes an oxide insulator for lack of oxygen. In above the process the oxygen of the crystals of the oxide superconductor escapes only through sides 18 and 19, since the oxide superconductor has larger diffusion coefficients of oxygen along the a -axis and the b -axis of the crystal than along the c -axis. After the process, as shown in Figure 2D, an insulating layer 16 which covers the extremely thin oxide superconductor thin film 11 and the gate electrode 4 is deposited. The insulating layer 16 is formed of an insulating material such as MgO by a sputtering etc. Then as shown in Figure 2E, the insulating layer 16 is etched by an anisotropic etching so that the insulating layer remains only on the side surfaces of the gate electrode 4 to form the gate insulating side-walls 14 and 15. Finally, as shown in Figure 2F, a superconducting source region 2 and a superconducting drain region 3 of an a -axis orientated oxide superconductor thin film are formed on the oxide superconductor thin film 11 at both sides of the gate electrode 4 and of gate insulator 6, respectively. In the process, in order to planarize an upper surface of the deposited a -axis orientated oxide superconductor thin film and to shape the superconducting source region 2 and the superconducting drain region 3, a photoresist layer (not shown) is deposited on the a -axis orientated oxide superconductor thin film is such a manner that the deposited photoresist layer has a flat upper surface, and then, the deposited photoresist layer and the deposited a -axis orientated oxide superconductor thin film are etched back, until the upper surface of the a -axis orientated oxide superconductor thin film is planarized and the gate electrode 4 is exposed at the planarized upper surface of the a -axis orientated oxide superconductor thin film as shown in Figure 2F. With this, the super-FET in accordance with the present invention is completed. As explained above, if the super-FET is manufactured in accordance with the second embodiment of the method of the present invention, the limitation in the fine processing technique required for manufacturing the super-FET is relaxed, similarly to the first embodiment. In addition, since the upper surface of the superconductor thin film is planarized, it become easy to form conductor wirings in a later process. Accordingly, it is easy to manufacture the super-FET with good repeatability, and the manufactures super-FET has a stable performance. The super-FET manufactured in accordance with the method of the present invention comprises the superconducting channel 10 formed on the substrate 5 and the gate electrode 4 arranged on the superconducting channel 10. The superconducting channel 10 is formed of a c -axis orientated oxide superconductor thin film which is as extremely thin as about 5 nanometers. Both sides of the superconducting channel 10, the superconducting source region 2 and the superconducting drain region 3 are located, respectively. The superconducting source region 2 and the superconducting drain region 3 are formed of a a -axis orientated oxide superconductor thin films, which are directly formed on the substrate 5 in the embodiment shown in Figure 1I or formed on the c -axis orientated super conductor thin film 11 in the embodiment shown in Figure 2F. On the other hand, the gate electrode 4 is located on the gate insulator 6 formed directly on the superconducting channel 10. The invention has thus been shown and described with reference to the specific embodiments. However, it should be noted that the present invention is in no way limited to the details of the illustrated structures but changes and modifications may be made within the scope of the appended claims.

Claims: A method for manufacturing a superconducting device, the method comprising the step of preparing a substrate (5) having a principal surface thereof, forming a c -axis orientated oxide superconductor thin film (11) having a very thin thickness on the principal surface of the substrate, forming on a portion of the c -axis orientated oxide superconductor thin film a stacked structure including a gate insulator (6) formed directly on the c -axis orientated oxide superconductor thin film and a gate electrode (4) formed on the gate insulator, growing an a -axis orientated oxide superconductor thin film, using the gate electrode as a mask, so that superconducting regions having a relatively thick thickness are formed of a -axis orientated oxide superconductor thin films at both sides of the gate electrode, electrically isolated from the gate electrode, and forming a superconducting source region (2) and a superconducting drain region (3), respectively. A method claimed in Claim 1 wherein the c -axis orientated and a -axis orientated oxide superconductor thin films (11) are formed of the same oxide superconductor material selected from the group consisting of a Y-Ba-Cu-O type compound oxide superconductor material, a Bi-Sr-Ca-Cu-O type compound oxide superconductor material, and a Tl-Ba-Ca-Cu-O type compound oxide superconductor material. A method claimed in Claim 2 wherein the gate electrode (4) is formed of a refractory metal or a silicide thereof. A method claimed in Claim 2 wherein the gate electrode (4) is formed of a material selected from the group consisting of Au, Ti, W, and a silicide thereof. A method claimed in Claim 2 wherein the substrate (5) is formed of a material selected from the group consisting of a MgO (100) substrate, a SrTiO₃ (100) substrate and a CdNdAlO₄ (001) substrate, and a semiconductor substrate. A method claimed in Claim 2 wherein the substrate (5) is formed of a silicon substrate having a principal surface coated with an insulating material layer which is formed of a MgAl₂O₄ layer and a BaTiO₃ layer. A method claimed in Claim 2 wherein when the stacked structure including the gate insulator (6) and the gate electrode (4) is formed on the portion of the c -axis orientated oxide superconductor thin film, the c -axis orientated oxide superconductor thin film is selectively etched so that a portion of the c -axis orientated oxide superconductor thin film (11) is completely removed and a surface of the substrate is exposed excluding a portion under the stacked structure, and a side surface of the remained c -axis orientated oxide superconductor thin film is coated with an normal conductor member, and wherein the a -axis orientated oxide superconductor thin film is grown on an exposed surface of the substrate, A method claimed in Claim 7 wherein the gate insulator (6) is formed of an insulating material which does not form a large density of energy levels between the oxide superconductor material of the c -axis orientated oxide superconductor thin film (11) and the insulating material of the gate insulator. A method claimed in Claim 7 wherein the c -axis orientated oxide superconductor thin film (11) is formed to have a thickness of about 5 nanometers and the gate insulator (6) is formed of MgO to have a thickness of not less than 10 nanometers. A method claimed in Claim 2 wherein after the gate electrode (4) is formed, the c -axis orientated oxide superconductor thin film (11) is selectively etched so that a portion under the gate electrode (4) projects from the etched portion of the oxide superconductor thin film (11), the substrate (5) is heated under high vacuum to make oxygen of the oxide superconductor crystals of the projecting portion escape and the oxide of the projecting portion becomes an oxide insulating layer (16), and a side surface of at least the gate electrode (4) is covered with an gate insulating side-wall (14, 15), the a -axis orientated oxide superconductor thin film is grown on an exposed surface of the c -axis orientated oxide superconductor thin film (11) until the stacked structure is completely embedded in the a -axis orientated oxide superconductor thin film, and the a -axis orientated oxide superconductor thin film is planarized until an upper surface of the gate electrode is exposed at the planarized upper surface of the a -axis orientated oxide superconductor thin film. A method claimed in Claim 10 wherein the gate insulator (6) is formed of an oxide which is made of the same composition and has same crystal structure as those of the oxide superconductor constituting the c -axis orientated oxide superconductor thin film (11). A method claimed in Claim 10 wherein the c -axis orientated oxide superconductor thin film (11) is formed to have a thickness of about 20 nanometers and the gate insulator is formed (6) to have a thickness of not less than 10 nanometers. A superconducting device comprising a substrate (5) having a principal surface, a first superconducting region formed on the principal surface of the substrate, second and third superconducting regions formed near each end of the first superconducting region separated from each other and electrically connected by the first superconducting region, and a gate electrode (4) formed on a gate insulator (6) placed on the first superconducting region for controlling the superconducting current flowing through the first superconducting region, characterized in that the first superconducting region is formed of an extremely thin c -axis orientated oxide superconductor thin film (11) each of the second and third superconducting region is formed of a relatively thick a -axis orientated oxide superconductor thin film in which the first superconducting region being electrically connected to the second and third oxide superconducting regions to form a superconducting channel (10) between the second and third oxide superconducting regions and the gate electrode (4) being electrically isolated from the first, second and third superconducting regions. A superconducting device claimed in Claim 13 wherein the oxide superconductor thin film (11) is formed of an oxide superconductor material selected from the group consisting of a Y-Ba-Cu-O type compound oxide superconductor material, a Bi-Sr-Ca-Cu-O type compound oxide superconductor material, and a T1-Ba-Ca-Cu-O type compound oxide superconductor material. A superconducting device claimed in Claim 14 wherein the gate electrode (4) is formed of a refractory metal or a silicide thereof. A superconducting device claimed in Claim 14 wherein the gate electrode (4) is formed of a material selected from the group consisting of Au, Ti, W, and a silicide thereof. A superconducting device claimed in Claim 14 wherein the substrate (5) is formed of a material selected from the group consisting of a MgO (100) substrate, a grTiO₃ (100) substrate and a CdNdAlO₄ (001) substrate, and a semiconductor substrate. A superconducting device claimed in Claim 14 wherein the substrate (5) is formed of a silicon substrate having a principal surface coated with an insulating material layer which is formed of a MgAl₂O₄ layer and a BaTiO₃ layer. A superconducting device claimed in Claim 14 wherein the gate insulator (6) is formed of a material stable to the oxide superconductor material of the first, second and third oxide superconducting regions. A superconducting device claimed in Claim 14 wherein the gate insulator (6) is formed of an oxide which is made of the same composition and has same crystal structure as those of the oxide superconductor constituting the first oxide superconductor region. A superconducting device claimed in Claim 14 wherein the first oxide superconducting region has a thickness of about 5 nanometers and the isolation region is formed of MgO or an oxide which is stable to the oxide superconductor material of the first, second and third oxide superconducting regions and has a thickness of not less than 10 nanometers. A superconducting device claimed in Claim 14 wherein the gate insulating side-walls (14, 15) are provided on the both side surfaces of the gate electrode (4) and formed of an insulator material, and the gate electrode (4) is embedded in the oxide superconducting regions so that the gate electrode is isolated from the first, second and third oxide superconducting regions by the gate insulator (6) and the gate insulating side-walls (14-15) formed of the insulator material.

Inventors: IIYAMA MICHITOMO, INADA HIROSHI, NAKAMURA TAKAO, IIYAMA, MICHITOMO, INADA, HIROSHI, NAKAMURA, TAKAO
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1991
Main classification: H01L39
IPC codes: H01L39