Indole compounds and their use

Abstract: Disclosed is a novel UV light absorbing compound which can preferably be employed in the art of colored molding plastics, resin films, heat-sensitive transfer materials, liquid crystal display materials, color photographs and the like, and method for producing thereof. The UV light absorbing compound is characterized by the general formula: wherein R¹ represents linear or branched alkyl or aralkyl group, and R² represents -CN or -COOR³, wherein R³ represents substituted or unsubstituted alkyl or aralkyl group.

Description: The present invention relates to novel indole compounds which are quite useful as a UV light absorbing additive or an anti-halation additive for colored resin compositions, resin films, heat-sensitive recording materials, liquid crystal display materials and the like. UV light is electromagnetic radiation having a wavelength between about 250 nm and about 400 nm. A number of organic compounds are decomposed or degraded by exposure to the UV light. Then, a wide variety of UV light absorbers are generally incorporated into the commercial organic products such as polymeric materials (e.g. natural or synthetic resin and rubber), dyes and cosmetic creams to prevent the degradation of the product such as discoloration, or the suntan of skin. In recent years, UV light absorbers have been incorporated into the heat-sensitive materials widely used as heat-sensitive transfer recording materials for recording devices such as facsimiles and printers to improve the light-resistance of the heat-sensitive transfer recording materials. The UV light absorbers may also be incorporated into the liquid crystal material widely used as display materials for watches and electric calculators or meters for cars. Furthermore, there is a proposal of a method for improving the light-resistance of the color photographic image using a UV light absorber containing transparent film. Therein, the transparent film is superimposed onto the printed surface of the photograph as a protective UV filter layer. Examples of conventional UV light absorbers include salicylates, benzophenones, benzotriazoles, cyanoacrylates and hindered amines. Since many of the compounds are substantially colorless, the incorporation of the UV light absorbers into the products does not affect the transparency or color of the products. Most of these conventional UV light absorbers, however, absorb the UV light of the wavelength ranging between about 290 nm and about 380 nm. There have been no conventional appropriate UV light absorbers which exhibit effective absorptivity in the spectral area ranging between about 380 nm and about 400 nm. FR-A-2 152 995 describes photographic materials comprising, for example, an indole compound. US-A-4,522,808 relates to a cosmetic composition comprising a cosmetic vehicle and at least about 0.05 wt.% of a derivative of 2-phenylindole based on the total weight of said composition. DE-B-10 10 047 describes the use of fluorescent methine compounds having no dye character as brightening agents wherein, e.g., an N-methyl-2-phenylindole derivative is used. US-A-3,109,844 relates to several types of indole derivatives and processes for their preparation. The types include 3-indoylsuccinimide and N-substituted derivatives thereof, and 3-(3'-indolyl)pyrrolidine and N-substituted derivatives thereof. An object of the present invention is to provide novel UV light absorbing compouns which can preferably be employed in the art of colored molding plastics, resin films, heat-sensitive transfer materials, liquid crystal display materials and color photographs and a method for their production. Another object of the present invention is to provide an UV light absorber comprising the abovementioned UV light absorbing compound as an active ingredient, and to provide a resin composition comprising the UV light absorber. In this application. "UV light absorber" means an UV light absorbing composition containing at least one UV light absorbing compound such as an indole compound. According to the present invention, the UV light absorbing compounds having: a) compatibility with wide variety of the organic materials; b) heat-stability (i.e. the UV light absorbing compounds are stable at the thermal molding temperature of the plastic products, or at the thermal transfer temperature of the heat-sensitive transfer recording products); c) light-resistance (i.e. the UV light absorbing compounds neither decompose under photoirradiation as radical species which react with other components contained in the commercial products, nor act under photoirradiation as photosensitizers which activate other components contained in the commercial products); and d) efficient UV light absorptivity in the long wavelength UV light spectral area (i.e. the UV light absorbing compounds have molecular absorptivity coefficient (ε) greater than 2.5x10 4 at maximum absorption wavelength (λ max ) which exists in the spectral range between about 380 nm and about 400 nm), as well as substantial transparency; are provided. Fig. 1 is a near UV-visible light absorption spectrum of the compound 1 according to the present invention. Fig. 2 is a near UV-visible light absorption spectrum of the compound 2 according to the present invention. Fig. 3 is a near UV-visible light absorption spectrum of the compound 6 according to the present invention. Fig. 4 is a near UV-visible light absorption spectrum of the compound 7 according to the present invention. Fig. 5 is a near UV-visible light absorption spectrum of the compound 10 according to the present invention. Fig. 6 is a near UV-visible light absorption spectrum of the mixture prepared from compound 1 according to the present invention and benzotriazole UV light absorber at a weight ratio of 1:1. Fig. 7 is a near UV-visible light absorption spectrum of the mixture prepared from compound 1 according to the present invention and benzotriazole UV light absorber at a weight ratio of 1:2. Fig. 8 is an infrared spectrum of the compound 1 according to the present invention. Fig. 9 is an infrared spectrum of the compound 6 according to the present invention. Fig. 10 is an infrared spectrum of the compound 10 according to the present invention. The UV light absorbing compound according to the present invention is an indole compound of the general formula: wherein R 1 of the general formula I represents a linear or branched alkyl or aralkyl group having 1-12 carbon atoms and R 2 represents -CN or -COOR 3 . Preferably, R 1 of the general formula I is selected from the group consisting of methyl, ethyl, butyl, isobutyl, t-butyl, hexyl, octyl, 2-ethylhexyl, dodecyl and benzyl group. R 3 represents an unsubstituted alkyl or aralkyl group having 1-20 carbon atoms or R 3 is selected from the group consisting of R 1 , β-cyanoethyl, β-chloroethyl, ethoxypropyl, hydroxyalkyl and alkoxyalkyl group, with the proviso that the indole compound is not a compound of the formula The process for producing the indole compound according to the present invention comprises; condensing a compound of the general formula: with a compound of the general formula: NC-CH 2 -R 2 wherein R 1 as well as R 2 represent the groups as defined above respectively. Examples of the compound III include malononitrile (NC-CH 2 -CN) and α-cyanoacetic esters (NC-CH 2 -COOR 3 ), wherein R 3 represents the groups as defined above. Examples of the α-cyanoacetic ester include methyl cyanoacetate, isopropyl cyanoacetate, butyl cyanoacetate, t-butyl cyanoacetate, amyl cyanoacetate, octyl cyanoacetate, esters obtained from cyanoacetic acids and higher alcohols (e.g., undecyl alcohol, dodecyl alcohol, aliphatic alcohols having 13-20 carbon atoms) and benzyl cyanoacetate. In the abovementioned condensation, the preferred amount of compound III is the range between 0.9-1.2 equivalent weight based on the amount of compound II. The condensation reaction may be carried out at the temperature between 10 °C and the boiling point of an employed solvent over 0.5-20 hours. The solvents employed in this reaction include alcohols (e.g., methanol, ethanol) and acetic anhydride. If alcohols are employed as the solvents, bases such as pyridine and triethylamine can be employed as catalysts. After completion of the reaction, the compound I according to the present invention is separated and optionally purified from the reaction mixture. The separation and purification is accomplished by means known to those skilled in the art. For example, the resulting reaction mixture is poured into a solvent such as water, the precipitated compound I is then separated out from the mixture. Generally, the compound I according to the present invention may be purified by solvent (e.g. alcohols) washing, but other purification processes such as recrystallization may be employed. The starting compound II according to the present invention may be prepared by means known to those in the art. For example, the compound II is prepared by formylation of the following compound IV dissolved in dimethylformamide in the presence of phosphorus oxychloride (Vilsmeier reaction). Another procedure for a preparation of compound I according to the present invention comprises, for example, condensing a compound of the general formula: with compound III to obtain a compound of the general formula: and then, reacting the compound VI with an alkylating or aralkylating agent to obtain an N-alkylated or N-aralkylated compound which is a compound I according to the present invention. If R 3 is hydrogen, compound VI may be treated with an alkylating agent to obtain the derivatives thereof. Condensation of compound V with III may be carried out in essentially the same manner as described above. N-alkylation or N-aralkylation may be conducted in usual means known to those in the art. The alkylating or aralkylating agents include alkyl or aralkyl halides (e.g., methyl iodide and benzyl iodide), dialkyl or diaralkyl sulfuric acids(e.g., dimethyl sulfuric acid and dibenzyl sulfuric acid) and aromatic sulfonates. The indole compounds I according to the present invention have the λ max in the spectral range between about 380 nm and about 400 nm. Thus, the long wavelength UV light may effectively be filtered out by the compound I. The compounds I according to the present invention are compatible and stable with a wide variety of organic materials such as organic solvents, plastics, resins and waxes, as well as have heat- and light-stability. Therefore, the indole compounds I according to the present invention can preferably be employed as additive for the wide variety of resin compositions. The resins employed in these resin compositions include polyvinyl butyrals, ethyl hydroxyethyl cellulose, styrene-maleic anhydride copolymers, methyl methacrylate resins, polyester resins, binders for heat-sensitive transfer material such as wax, plastics for molding, resins for plastic film, polymeric liquid crystals. In the photographic art, the indole compound I according to the present invention may be employed into an UV light absorbing top layer superimposed over the photographic film, or may be mixed with colored organic materials such as color photographic pigments or dyes, so that the fastness against UV light as well as visible light of the color photographic film is improved. The indole compounds I according to the present invention may be combined with the anti-halation dyes employed in the color photographic film so as to prevent the adverse effect which accompanies the exposure of the photographic film. The indole compounds I according to the present invention can be employed as UV light absorbing compound for a wide variety of resin compositionsin an amount sufficient to provide a certain level of light resistance to the resin composition. Generally, amounts ranging from about 0.1-10 % by weight and preferably about 0.5-2.0 % by weight based on the solid weight of the composition can be employed. If the content of the compound I is greater than 10 % by weight, a color toning deficiency may occur in colored organic compounds or in a resin composition. Other conventional UV light absorbing compounds can be employed in combination with the indole compound I according to the present invention, so as to provide the wider spectral range of absorptivity. Other additives such as fluorescent whitening agents or radical scavengers may be incorporated into the resin composition according to the present invention. EXAMPLES The present invention will be more specifically described by the following non-limiting examples, wherein all parts are by weight unless otherwise specified. EXAMPLES 1-10 These examples illustrate the preparation of UV light absorbing compounds according to the present invention. Example 1 Preparation of Compound 1 A dye solution was prepared by dissolving 0.10 mol of N-methyl-2-phenyl-3-indolyl aldehyde having the general formula: into 80 ml of ethanol. To this solution were added 0.11 mol of malononitrile, and 0.04 mol (4 parts by weight) of triethylamine. The solution was then heated to reflux, maintained at the temperature over 4 hours, and cooled to the room temperature. The resulting reaction mixture was poured into water to precipitate the condensation product. The precipitated crystals were then filtered off, washed with a little amount of alcohol, and dried to obtain the light-yellow crystals (m.p. 194-196 °C). Example 2 Preparation of Compound 2 A dye solution was prepared by dissolving 0.10 mol of the following compound: into 70 parts by weight of dimethylformamide. To this solution were then added 23 parts by weight of phosphorus oxychloride under externally cooling. Twelve parts by weight of pyridine were further added to the solution. The resulting solution was then heated to 40 °C, maintained at the temperature over 1 hour and cooled to 20-30 °C. Forty parts by weight of methanol, 35 parts by weight of sodium acetate, and a solution of 6.6 parts by weight (0.1 mol) of malononitrile into 5 parts by weight of methanol were added to the cooled solution. The solution was then heated to 70 °C, maintained at the temperature over I hour, and cooled to room temperature. The resulting reaction mixture was poured into water to precipitate the condensation product. The precipitated crystals were then filtered off, washed with water, and dried to obtain 28.5 parts by weight of powder product. Recrystallization of the resulting powder from methyl ethyl ketone gave the light-yellow crystals (m.p. 163-165 °C). Example 3 Preparation of Compound 3 Light yellow crystals were obtained in essentially the same manner as described in Example 1 except that N-butyl-2-phenyl-3-indolyl aldehyde instead of N-methyl-2-phenyl-3-indolyl aldehyde, and 5 hours refluxing were used. Example 4 Preparation of Compound 4 Light yellow powder was obtained in essentially the same manner as described in Example 1 except that N-(2-ethylhexyl)-2-phenyl-3-indolyl aldehyde instead of N-methyl-2-phenyl-3-indolyl aldehyde, and 5 hours refluxing were used. Example 5 Preparation of Compound 5 Light yellow crystals were obtained in essentially the same manner as described in Example 1 except that N-benzyl-2-phenyl-3-indolyl aldehyde instead of N-methyl-2-phenyl-3-indolyl aldehyde, and 5 hours refluxing were used. Reference Example 1 Preparation of Compound 6 Light-yellow crystals (m.p. 140-142 °C) were obtained in essentially the same manner as described in Example 1 except that ethyl cyanoacetate instead of malononitrile, and 4 hours refluxing were used. Example 6 Preparation of Compound 7 Light yellow crystals were obtained in essentially the same manner as described in Example 1 except that butyl cyanoacetate instead of malononitrile, and 5 hours refluxing were used. Example 7 Preparation of Compound 8 Light yellow crystals were obtained in essentially the same manner as described in Example 1 except that the combination of N-octyl-2-phenyl-3-indolyl aldehyde with ethyl cyanoacetate instead of N-methyl-2-phenyl-3-indolyl aldehyde with malononitrile, and 5 hours refluxing were used. Example 8 Preparation of Compound 9 Light yellow crystals were obtained in essentially the same manner as described in Example 1 except that the combination of N-benzyl-2-phenyl-3-indolyl aldehyde with ethyl cyanoacetate instead of N-methyl-2-phenyl-3-indolyl aldehyde with malononitrile. and 5 hours refluxing were used. Example 9 Preparation of Compound 10 Light yellow crystals (m.p. 128-133 °C) were obtained in essentially the same manner as described in Example 1 except that benzyl cyanoacetate instead of malononitrile, and 5 hours refluxing were used. Example 10 Preparation of Compound 11 Light yellow crystals were obtained in essentially the same manner as described in Example 1 except that the combination of N-benzyl-2-phenyl-3-indolyl aldehyde with benzyl cyanoacetate instead of N-methyl-2-phenyl-3-indolyl aldehyde with malononitrile, and 5 hours refluxing were used. The structures, λ and ε at the λ max of the resulting compounds 1-11 are summarized in the following Table 1. Fig. 1, 2. 3, 4 and 5 show near UV-visible light absorption spectra of the compoundsl, 2, 6, 7 and 10 respectively. Fig. 8, 9 and 10 show infrared spectra of the compoundsl. 6 and 10 respectively. EXAMPLE 11 This example illustrates the preparation of the light-resistance evaluation laminate samples which are pieces of magenta printed paper coated with the UV light absorbing coating composition according to the present invention. Example 11 A transparent UV light absorbing coating composition was prepared form the following formulation. Components Parts by Weight DIANAL LR-1065 100 compound 1 1 The UV light absorbing coating composition was applied onto a polyethylene terephthalate (PET) film having a thickness of 100 µm using a bar coater at a final dry coating thickness of about 30 µm. The coated PET film was then dried to provide a transfer sheet material consisting of a PET substrate layer and a UV light absorbing transfer coating layer. On the other hand, the solid printing of magenta onto a piece of paper was carried out using a color ink jet printer. Then, onto the printed surface of the paper, the UV light absorbing transfer coating layer surface of the transfer sheet material was laminated so as to cover the printed magenta pattern. The PET substrate layer was then removed to provide a laminate sample A. Reference Example 2 A laminate sample B was prepared in essentially the same manner as described in Example 11, except that the transparent UV light absorbing composition was prepared form the following formulation. Components Parts by Weight DIANAL LR-1065 100 compound 6 0.5 TINUVIN P328 0.5 EXAMPLE 12 This example illustrates the evaluation in light-resistance of the laminate samples prepared in Example 11 and Reference Example 2. The laminate samples A, B and comparative sample 1 which was a piece of magenta printed paper prepared as described in example 11 (i.e. the comparative sample 1 was not coated with the UV light absorbing coating composition according to the present invention) were irradiated for 20 hours on a long life carbon-arc fadeometer (SUGA TEST INSTRUMENTS Co., Ltd.). Light-resistance of the samples was evaluated by visual inspection of their color change. The results are shown in Table 2. Samples Light-resistance A good B good comparative 1 fail b) EXAMPLE 13 This example illustrates that the UV light absorbing compound according to the present invention is compatible with the conventional UV light absorbing compounds having λ of about 300 nm to about 380 nm. Fig. 6 and 7 show near UV-visible light absorption spectra of the mixture prepared from compound 1 and benzotriazole UV light absorber (TINUVIN P328, Ciba-Geigy Ltd.) at a weight ratio of 1:1 and 1:2 respectively. The wide spectral range in absorption between about 250 nm and about 400 nm was the result of the combination use thereof.

Claims: An indole compound of the general formula: wherein R 1 represents a linear or branched alkyl or aralkyl group having 1-12 carbon atoms and R 2 represents -CN or -COOR 3 , wherein R 3 is selected from the group consisting of β-cyanoethyl, β-chloroethyl, ethoxypropyl, hydroxyalkyl and an alkoxyalkyl group or is an unsubstituted alkyl or aralkyl group having 1-20 carbon atoms, with the proviso that the indole compound is not a compound of the formula The indole compound according to claim 1, wherein R 1 of the general formula I is selected from the group consisting of methyl, ethyl, butyl, isobutyl, t-butyl, hexyl, octyl, 2-ethylhexyl, dodecyl and a benzyl group. A process for producing the compound according to claim 1 or 2, comprising: reacting a compound of the general formula: with a compound of the general formula NC-CH 2 -R 2 wherein R 1 and R 2 represent the groups as defined in claim 1, respectively. The process according to claim 3 wherein compound III is selected from the group consisting of malononitrile and α-cyanoacetic esters. A UV light absorber comprising an indole compound according to claim 1 or 2 as an active ingredient. A resin composition comprising the UV light absorber according to claim 5. A coating composition comprising the UV light absorber according to claim 5.

Inventors: OTSUKA MASAHIRO, OTSUKA, MASAHIRO
Applicants: ORIENT CHEMICAL IND, ORIENT CHEMICAL INDUSTRIES, LTD.
Application year: 1991
Main classification: C07D209
IPC codes: C09K3, C07D209, B41M5, A61K8, C08L101, C08K5, G03C1, A61Q17