Method of indicating a cure point for ultraviolet radiation curing compositions by color change

Abstract: Adding a dye with a visible color to an ultraviolet radiation curable composition which contains a photoinitiator which generates free radicals upon exposure to ultraviolet radiation produces a composition which changes visible color upon exposure to ultraviolet radiation. This visible color change indicates that the composition has cured. This cure indication is useful for compositions curable by ultraviolet radiation in the electronics and electrical industry.

Description: This invention relates to a method of curing compositions by ultraviolet radiation. The curing of an ultraviolet radiation curable composition upon exposure to ultraviolet radiation varies with the kind of ingredients making up the composition, the kind of equipment used for generating the ultraviolet radiation, the geometry of the device having a film, coating or encapsulant to be cured and the curing conditions to which the device is exposed. These variables make it difficult to determine at what point the composition is sufficiently cured. Many times to avoid the chance that a composition may be under cured, the dosage of ultraviolet (UV) radiation which is given to the items to be cured is excessive. Excessive dosages may not harm the items, but they could and, furthermore, using excessive dosages is expensive and a waste of resource. Therefore, the discovery of the present method permits establishing curing conditions which can result in sufficient cure without either undercuring or overcuring. Materials for the electrical and electronics industry need to meet stricter requirements because the electronic devices are becoming smaller and more complex. The field of printed circuit boards is no exception. The various coatings require that the materials protect the electronic devices and components from the environments which they may encounter either during processing or in use. Coating printed circuit boards with compositions which will cure to a film and which will provide the required protection without changing the designed electronic properties or otherwise damage the boards components is difficult to achieve because the components are very small and often of shapes and design which demands compositions which have special uncured properties, special curing properties and special application properties. Printed circuit boards often need to be protected from contamination of the electrical and electronic components. This protection can be provided by coating or encapsulating the device bearing board with a protective film to avoid or minimize the reduction in the electrical performance due to contamination. Moisture and humidity are considered to be the worst contaminant because it must be dealt with in most environments. Moisture and humidity can drastically lower insulation resistance between conductors, accelerate high voltage breakdown, accelerate dendritic growth and corrode the conductors. Other than moisture, chemical contaminants from the environment such as dust, dirt, solvents, acids, fungus, oils and fuels or those which are used in the manufacturing process such as organic solvents, fluxes, vapors, acids, release agents and metal dust. Handling a printed circuit board can also cause contamination, for example, from fingerprints. Conformal coatings are also used to protect the electronic components from the harmful aspects of extremes in temperature, shock and abrasion. Many conformal coatings and potting compositions are known in the art and are available commercially. Each has its advantages and disadvantages. One prior art conformal coating material is based on acrylics. Acrylic coatings make excellent coating and potting systems because they have desirable electrical and physical properties, are resistant to fungus growth, have a long life, low or no exotherm during cure and have little or no shrinkage during cure. From some viewpoints, the acrylic coating systems have a production advantage because they can be readily applied by spraying, dipping or brushing. However, this is also a disadvantage because the films are formed from solvent containing acrylic systems. The evaporation of the solvent is a slow and expensive step and the solvent vapors need to be controlled for environmental reasons. The solvents typically used are the chlorinated solvents, such as trichloroethane and methylene chloride. The combined impact of high energy costs and more stringent control regulations which restrict emissions of volatile solvents into the atmosphere has created a need in the coatings industry for high solids or solventless systems which do not require a large amount of energy for conversion of the system into a high performance coating. Coatings which are 100% solids are known and have a rapid cure at a relatively low conversion energy demand. Such coatings are acrylated coatings which cure by ultraviolet radiation or by electron beam exposure. These are all reasons why it is important to have the ability to know when a UV curable composition is cured so that extra energy usage is avoided and the cost is kept to a minimum. JP-A-61157557 describes organopolysiloxane compositions comprising polyorganosiloxane, polyorganohydrogen siloxane, a platimium catalyst, and 1 to 2000 ppm based on the polyorganosiloxane of an anthraquinone dye. The addition of the anthraquinone dye to the silicone rubber composition allows the degree of cure and the judgement of the cure state to be determined by the naked eye according to an observed color change. JP-A-01204902 discloses compositions which comprise 100 parts by weight of a photopolymerizable resin component, 0.5-10 parts by weight of a photopolymerization initiator and 0.05-10 parts by weight of a photodiscoloring compound. The photo curing resin composition discolours by irradiation of light and the photopolymerizing resin component of the composition is selected from unsaturated polyester resins, (meta)acryloyl group-containing polymerizing resin, thiol-ene base addition polymerization resins and cationic polymerization resins. A method of indicating a cure point of an ultraviolet radiation curing composition which comprises: adding to an ultraviolet radiation curable composition comprising a photoinitiator which generates free radicals upon exposure to ultraviolet radiation and a composition which cures upon exposure to ultraviolet radiation which consists essentially of a silicone resin having a general average unit formula R i c SiO (4-c)/2 in which each R i in each unit is independently a monovalent organic radical where at least 10 mole percent of the total R i are phenyl radicals and at least two R i per molecule are aliphatic unsaturated radicals which react with mercapto functionality and c has an average value of from 1.2 to 1.8; an organic mercaptan composed of carbon, hydrogen, sulfur and oxygen in which there is at least two mercapto groups per molecule; an acrylate monomer having at least one acrylate group per molecule in an amount of at least one weight percent based on the total weight of the composition; an effective amount of a free radical inhibitor to delay gellation during storage, the composition has more than two aliphatic unsaturated radicals per molecule in the silicone resin when the organic mercaptan has two mercapto groups per molecule or more than two mercapto groups per molecule in the organic mercaptan when the silicone resin has an average of two aliphatic unsaturated radicals per molecule or both more than two aliphatic unsaturated radicals per molecule in the silicone resin and more than two mercapto groups per molecule in the organic mercaptan and amount of silicone resin and organic mercaptan being such that there is from 0.5 to 1.5 aliphatic unsaturated radicals in the silicone resin for each mercapto group in the organic mercaptan, from 10 - 40 ppm based on the weight of the ultraviolet radiation curable composition of a dye with a visible colour selected from anthraquinone dyes and disazo dyes, and thereafter exposing the resulting composition to a dosage of ultraviolet radiation which causes the visible color to either disappear or chance to a different color indicating that cure has occurred coincidentally. The method of the present invention permits a user of ultraviolet radiation curable compositions to be assured that the resulting material is fully cured. This is accomplished without overcuring by observation of visible color change. This color change occurs when a non-inhibiting amount of a dye with a visible color is added to a composition which cures by exposure to ultraviolet radiation. The change can be from blue to yellow, from red to yellow, from blue to clear and from yellow to clear. This color change usually lasts over long time periods and does not return upon standing. If the cure is not sufficiently complete, the original color will return upon standing over a period of time, such as from a few minutes, to an hour or more, to a couple weeks. For purposes of this invention, the use of the term "visible dye" means a dye which will impart a color under ordinary visible light. Also, the color changes are those which are observable in ordinary visible light. The visible dyes useful in the present invention are those which, in the presence of free radical generating photoinitiators, change color upon exposure to ultraviolet radiation. This color change occurs and is essentially permanent at the point that a UV curable composition is cured upon exposure to UV radiation. The visible dyes useful in the present invention include, are anthraquinone dyes and disazo dyes. Examples of anthraquinone dyes include l-amino-2-bromo-4-hydroxy-anthraquinone of which Sandoplast Red 2B powder, sold by Sandoz Chemicals, Charlotte, North Carolina is an example, a proprietary anthraquinone dye sold by Sandoz Chemical as Nitro Fast Blue 2B. An example of a disazo dye is Nitro Fast Yellow B Powder, sold by Sandoz Chemical which has a formula C 37 H 36 N 4 O 2 . The amount of visible dye useful in a particular UV curable composition should be an amount less than that amount which will inhibit the cure of the composition upon exposure to UV radiation. The amount is from 10 ppm to 40 ppm of the visible dye based on the weight of the UV curable composition. It was found that amounts of the visible dye which became too high could inhibit the cure of the UV curable composition. The optimum amounts of visible dye in a given composition can readily be determined by adding a specific amount of visible dye to the composition and observing the color change, or lack thereof, upon exposure to UV radiation. If too much dye is added, no color change takes place, indicating the composition did not cure. At this point, one can increase the dosage of UV to determine whether the reason it did not cure was that the dosage was too low. Further, evaluation can be used to determine whether the amount of visible dye concentration is too high. The UV curable compositions in which this color change can occur are those which contain a photoinitiator which produces free radicals upon exposure to UV radiation and in which there is at least one material which cures upon exposure to UV radiation. Example of photoinitiators which generate free radicals include benzophenone, acetonaphthone, acetophenone, benzoin methyl ether, benzoin isobutyl ether, 2-hydroxy-2-methyl-l-phenylpropan-l-one, 1-hydroxycyclohexylphenyl ketone, 2,2-diethoxyacetophenone, 3-hydroxypropylphenyl ketone, 3-hydroxypropyl-p-isopropylphenyl ketone and mixtures thereof such as a mixture of 50 weight percent of l-hydroxycyclohexylphenyl ketone and 50 weight percent benzophenone. The amount of photoinitiator is that amount which is conventionally required by the particular composition for curing it. The UV curable compositions which can be used in the present invention are those which are curable by photoinitiators which produce free radicals. These compositions can be either silicone compositions, organic compositions or compositions which contain both silicone compounds (includes polymers) which will cure by exposure to UV radiation in the presence of a free radical photoinitiator and organic compounds (includes polymers) which cure by exposure to UV radiation in the presence of a free radical photoinitiator. The compositions containing the visible dye and photoinitiator are exposed to UV radiation from conventional equipment and under conditions normally used for such compositions wherein adjustments are made to reach the cure point by observation of the color change. The point at which cure is achieved results in a color change. Therefore, the length of time or the dosage of UV radiation can be varied to produce the required cure. Compositions curable to gels are those organo-siloxane compositions which retain their gel properties at low temperature. The UV curable compositions which cure to gels and which are useful for the present invention are those which contain photoinitiators which generate free radicals. The photoinitiator is present in an amount sufficient to promote curing of the composition upon exposure to UV radiation. The photoinitiator should be compatible with the other ingredients of the present compositions. Compatibility can readily be determined by blending one weight percent of the candidate photoinitiator with the other liquid ingredients of the UV curable composition and mixing the resultant composition at room temperature or with heating to a temperature of about 80°C. The resultant composition should be optically clear without any dispersed or precipitated material. The photoinitiators are exemplified above. It may be desirable to include an organic peroxide that decomposes at a temperature within the range of from about 100°C. to about 250°C. This is particularly true if the substrate to which the composition will be applied is contoured such that a portion of the curable composition is shielded from the ultraviolet radiation to which the coated substrate is subsequently exposed for the purpose of curing the gel composition. The UV curable compositions can contain a reinforcing filler or other type of reinforcing agent to improve the physical properties of the cured material, In those applications where transparency of the cured gel is a requirement, the reinforcing agent is preferably a finely divided hydrophobic silica of the type described in United States Patent No. 4,344,800, issued to Michael A. Lutz on August 17, 1982. The disclosure of this patent is a teaching of silica fillers suitable for use in the optically clear gel compositions of this invention. The compositions cure rapidly, typically requiring about one second or less of exposure to UV radiation from a medium pressure mercury vapor arc lamp. The amount of energy required to cure preferred compositions is from 0.1 to about 3 joules per square centimeter, depending upon the ingredients and the thickness of the layer of curable composition applied to a substrate. The intensity of the UV radiation used to cure the compositions can be measured using any of the available techniques. A preferred method employs an integrating photometer which is exposed to a mercury vapor arc lamp or other source of UV radiation under the same conditions used to cure the coated substrate. A commercially available integrating photometer is the "Light Bug" available from International Light. With the method of the present invention, the visible dye is added to the composition and upon exposure to UV radiation, the color changes when cure is achieved. This will eliminate the necessity to constantly check with a photometer during manufacturing operations. In those instances, where a wet film of the composition is exposed to the UV radiation and the color does not change or the color returns after a short period of time, it is apparent that the dosage is insufficient. These organosiloxane gels can include uses as protective coatings and encapsulants for electrical and electronic components, particularly solid state devices such as integrated circuits and electrical connectors. The gel can prevent penetration of atmospheric moisture and other materials that can corrode or otherwise damage the component. The compositions according to the invention which cure upon exposure to ultraviolet radiation consist essentially of the silicone resin having a general average unit formula R i c SiO (4-c)/2 in which each R i in each unit is independently a monovalent organic radical where at least 10 mole percent of the total R i are phenyl radicals and at least two R i per molecule are aliphatic unsaturated radicals which react with mercapto functionality and c has an average value of from 1.2 to 1.8; the organic mercaptan composed of carbon, hydrogen, sulfur and oxygen in which there is at least two mercapto groups per molecule; the acrylate monomer having at least one acrylate group per molecule in an amount of at least one weight percent based on the total weight of the composition; and effective amount of photoinitiator to cause the composition to cure upon exposure to UV radiation where the photoinitiator generates free radicals upon exposure to the UV radiation; and an effective amount of the free radical inhibitor to delay gelation during storage, the composition has more than two aliphatic unsaturated radicals per molecule in the silicone resin when the organic mercaptan has two mercapto groups per molecule or more than two mercapto groups per molecule in the organic mercaptan when the silicone resin has an average of two aliphatic unsaturated radicals per molecule or both more than two aliphatic unsaturated radicals per molecule in the silicone resin and more than two mercapto groups per molecule in the organic mercaptan and the amount of silicone resin and organic mercaptan being such that there is from 0.5 to 1.5 aliphatic unsaturated radicals in the silicone resin for each mercapto group in the organic mercaptan. The silicone resins contain aliphatic unsaturated radicals which react with mercapto functionality. These silicone resins have an average of 1.2 to 1.8 organic radical bonded per silicon atom and at least 10 mole percent of the organic radicals are phenyl. The silicone resins have per molecule at least two aliphatic unsaturated radicals which react with mercapto functionality. The silicone resin has a general average unit formula R i c SiO (4-c)/2 in which c has an average value of from 1.2 to 1.8 and R i is a monovalent organic radical where at least 10 mole percent of the R i are phenyl radicals and at least two R i per molecule are aliphatic unsaturated radicals which react with mercapto functionality. The general average unit formula is the summation of individual siloxane units which are SiO 2 units, R i SiO 3/2 units, R i 2 SiO units, R i 3 SiO 1/2 units and each R i in each siloxane unit is independently selected from the group as defined herein. Each siloxane unit does not need to be present in each silicone resin, but the siloxane units which are present need to provide an average value for c of from 1.2 to 1.8. R i can be independently selected from an alkyl, alkenyl, halogenated alkyl or aryl. The alkyl radicals can be illustrated by methyl, ethyl, propyl, isopropyl, butyl, hexyl and octyl. The alkenyl radicals can be illustrated by vinyl, allyl, cyclohexenyl, 1,2-butenyl and 1,2-hexenyl. The halogenated alkyl radicals can be illustrated by 3,3,3-trifluoropropyl and other chlorinated, fluorinated and brominated alkyl radicals wherein hydrogen atoms of the alkyl radicals are replaced with a halogen atom. The preferred alkenyl radicals are vinyl and hexenyl. Other preferred radicals are methyl, propyl, 3,3,3-trifluoropropyl and phenyl. Preferred silicone resins are those which are made up of at least two siloxane units selected from the group consisting of monophenyl-silsesquioxane units, monomethylsilsesquioxane units, dimethyl-siloxane units, diphenylsiloxane units, methylvinylsiloxane units, dimethylvinylsiloxy units and trimethylsiloxy units. The preferred silicone resins contain from 20 to 80 mole percent monophenylsilsesquioxane units where the remaining siloxane units can be those listed above. A more preferred class of silicone resins are those made up of from 20 to 40 mole percent monophenylsilsesquioxane units, 10 to 20 mole percent mono-methylsilsesquioxane units, 20 to 35 mole percent dimethylsiloxane units and 10 to 30 mole percent methylvinylsiloxane units. The silicone resins can be one resin or a blend of two or more resins. The silicone resins can contain residual silicon-bonded groups which result from their preparation, such as hydroxyl groups (Si-OH) and alkoxy groups (Si-OR**) where R** is an alkyl radical of 1 to 4 carbon atoms. The crosslinked density, flexibility of cured products and the modulus of cured products are controlled by selecting the amount of aliphatically unsaturated radicals in the silicone resin and the average degree of substitution of the silicon atoms by silicon-bonded carbon groups. For example, increasing the average number of aliphatically unsaturated radicals per molecule increases the modulus and decreases the flexibility with other composition parameters remaining constant. Increasing the average degree of substitution of the silicon atom increases the flexibility and decreases the modulus with the other composition parameters remaining constant. These are general guidelines and the proportional increases and decreases in the modulus and flexibility can be varied with the kinds of other R groups, the amount of phenyl, the kind of aliphatically unsaturated radicals and the kinds and amounts of each of the siloxane units present in the silicone resin. The organic mercaptan contains an average of at least two mercapto functional groups per molecule. In these compositions, the number of aliphatically unsaturated groups per molecule in the silicone resin is more than two, if the number of mercapto functional groups in the organic mercaptan is two or if the number of aliphatically unsaturated groups per molecule in the silicone resin is two, then the average number of mercapto functional groups per molecule in the organic mercaptan must be more than two. These compositions can contain silicone resin having per molecule more than two aliphatically unsaturated groups per molecule and organic mercaptan having per molecule more than two mercapto functional groups. The organic mercaptans can be illustrated by the following: trimethylolpropane trithioglycolate, trimethylolpropane tri(3-mercaptopropionate), trimethylolethane trithioglycolate, polyethylene glycol dimercaptoacetates, glycol dimercaptoacetate and dipentaerythritol hexa(3-mercapto-propionate). The preferred organic mercaptan is trimethylolpropane tri(3-mercaptopropionate). Mixtures of two or more organic mercaptans can be used. These conformal coating compositions can contain, as an ingredient to improve the corrosion resistance, improve the adhesion to printed circuit board substrates and improve the thermal resistance, an acrylate monomer. These acrylate monomers are illustrated by trimethylolpropane trimethylacrylate, pentaerythritol tetraacrylate, ethoxylated trimethylolpropane triacrylate, pentraerytritol acrylate (contains three acrylate groups), di(trimethylmethylolpropane tetrataacrylate), trimethylolpropane triacrylate, di(pentraerythritol monohydroxy pentaacrylate), hydroxylethyl acrylate, hydroxylpropyl acrylate, 4-hydroxy-n-butyl acrylate, isobornyl acrylate, proprietary acrylates such as functionalized acrylates known as Sartomer 9008 (a triacrylate), Sartomer 9012 (an aliphatic triacrylate) and Sartomer 9013 (an aliphatic monoacrylate). These are sold by ARCO Chemical Company of Pennsylvania. The acrylates are used in amounts of one weight percent or more based on the total weight of the composition. Ultraviolet radiation capable of causing free radicals to form in the composition can be used to cure the composition nf this invention. The ultraviolet radiation used to generate the free radical crosslinking reaction to effect polymerization of the composition and cure requires a photosensitization system. Examples of the photosensitization systems are known in the art, some specific photoinitiators include diethoxyaceto-phenone, benzophenone, dimethoxyphenylacetophenone, benzoin, 2-hydroxy-2-methyl-1-phenylpropan-1-one, with optional sensitizors such as N-methyldiethanolamine, diisopropylaminoethanol and amyldimethylaminobenzoate. These conformal coating compositions can be prepared by mixing the ingredients at room temperature with conventional mixing equipment. In some cases the blending of the ingredients can be accomplished by some heating. Heating these ingredients can create degradation if the temperatures become too high or the duration of the heating is for prolonged periods of time. The ingredients used to make these compositions should be blended to make compatible mixtures. This compatibility is desirable to ensure that the cured products will form solid coherent coatings, films, sheets and encapsulants with consistent properties throughout. Incompatibility can cause weak spots, fisheyes and poor wetting of substrates on which the composition is deposited. A method of making cured films is accomplished by first preparing the composition by mixing the silicone resin, the organic mercaptan, the acrylate monomer, the photoinitiator and the free radical inhibitor to form a compatible, homogeneous blend, applying the composition to a substrate such as an electronics device and then irradiating the composition with ultraviolet radiation in an amount sufficient to cure the composition. These conformal coating compositions contain an effective amount of a free radical inhibitor to delay gellation during storage. These free radical inhibitors include p-methoxyphenol (also know as MEHQ), catechol, 4-t-butylcatechol, phenothiazine, 2,6-di-t-butyl-p-methylphenol and N-phenyl-2-naphthylamine. The amounts of the free radical inhibitors are from zero to one weight percent based on the weight of the composition, more preferably from 0.01 to 0.25 weight percent. The most preferred free radical inhibitors are p-methoxyphenol, phenothiazine and mixtures thereof. The presence of hydroquinone as a free radical inhibitor appears to be undesirable from the standpoint of preparing high modulus and tensile strength cured products. The conformal coating compositions cure very well, adhere well to electronic boards, have a mild odor and are clear. The presence of the acrylate compound in these compositions is vital to protect copper from corroding. The compositions of the present invention exhibit improved adhesion by preventing salt water from creeping under the coating and corroding the metal. However, acrylates without the mercaptan compound exhibit insufficient cure and to obtain the excellent properties the silicone resin, mercaptan and acrylate are required. The thermal stability of the cured films made from the compositions of this invention can be expected to improve further by substituting hexenyl group for the vinyl group in the silicone resins. The compositions of this invention cure very rapidly compared to other ultraviolet radiation cured conformal coating compositions. They also can be cured in very deep sections when peroxide is added to them. These conformal coatings can be used as mar resistant conformal and protective coatings for printed circuit boards, gaskets for automobile engines, coatings for deep cross section pottants, optical fiber coatings where the refractive index of these coatings is greater than 1.49. The preferred composition consists essentially of silicone resin in an amount of greater than 35 weight percent, from 5 to 30 weight percent mercaptan compound, from 1 to 25 weight percent acrylate compound, from 1 to 4 weight percent photoinitiator, less than 0.05 weight percent free radical inhibitor and when present organic peroxide in amounts of from 1 to 5 weight percent. The weight percentages are based on the total weight. of the composition. Organic conformal coating compositions combine the toughness of certain resins, low shrinkage of monofunctional nonpolar monomers, low T g resins and monomers and adhesion promoting monofunctional and difunctional monomers. These organic conformal coating compositions have low temperature flexibility and good thermal shock resistance and electrical properties. The composition can be post cured using a peroxide which is stable at normal room temperature processing and has a long shelf life, such as six months. The composition can also contain a fire retardant. These features are obtained without the use of solvents and can be applied to substrates by dip coating, by spray coating and brushing because of the low viscosity. The method of the present invention can be used for UV curable compositions which make films, coatings, encapsulants in the electrical and electronics industries such as for printed circuit boards, electrical connectors and electrical splices. The following example is presented for illustrative purposes and should not be construed as limiting the invention which is properly delineated in the claims. In the following examples, "part" or "parts" represents "part by weight" or "parts by weight", "%" are percent by weight unless otherwise stated. EXAMPLE 1 An ultraviolet radiation curable siloxane composition was prepared by adding 0.002 part of Nitro-Fast Blue 2B (Sandoz Chemical, Charlotte, North Carolina) (which is also known as C.I. Solvent Blue 104) to a mixture of 65.5 parts of a silicone resin having the average siloxane unit formula (MeSiO 3/2 ) 7.5 (PhSiO 3/2 ) 37.6 (Me 2 SiO) 30.1 (MeViSiO) 20.0 -(Me 3 SiO 1/2 ) 4.8 (OH) h which had a vinyl content of 5.2 weight percent, a value for h to provide an OH content of 1.49 weight percent, a non-volatile content of 97.4 weight percent and a viscosity of 14.5 Pa·s, 17.5 parts of an organic mercaptofunctional compound having the formula 10 parts of tripropylene glycol diacrylate [TRPGDA], 5 parts of isobornyl acrylate [IBA], 3.08 parts of photoinitiator of the formula and 0.005 parts of a UV dye fluorescent indicator, Uvitex OB. A sample of this mixture was blue and after exposing it to UV radiation as described below it turned yellow and remained yellow. A 10 g sample of the blue composition was passed through a UV-6 Single Lamp Conveyorized UV Curing Unit manufactured by Colight, Minneapolis, Minnesota. The conveyor was set at about 0.015m/s (3 ft/min) and the lamp was at 200 watts. The composition changed to light yellow and was fully cured. The cured sample remained yellow for at least six months.

Claims: A method of indicating a cure point of an ultraviolet radiation curing composition which comprises: adding to an ultraviolet radiation curable composition comprising a photoinitiator which generates free radicals upon exposure to ultraviolet radiation and a composition which cures upon exposure to ultraviolet radiation which consists essentially of a silicone resin having a general average unit formula R i c SiO (4-c)/2 in which each R i in each unit is independently a monovalent organic radical where at least 10 mole percent of the total R i are phenyl radicals and at least two R i per molecule are aliphatic unsaturated radicals which react with mercapto functionality and c has an average value of from 1.2 to 1.8; an organic mercaptan composed of carbon, hydrogen, sulfur and oxygen in which there is at least two mercapto groups per molecule; an acrylate monomer having at least one acrylate group per molecule in an amount of at least one weight percent based on the total weight of the composition; an effective amount of a free radical inhibitor to delay gellation during storage, the composition has more than two aliphatic unsaturated radicals per molecule in the silicone resin when the organic mercaptan has two mercapto groups per molecule or more than two mercapto groups per molecule in the organic mercaptan when the silicone resin has an average of two aliphatic unsaturated radicals per molecule or both more than two aliphatic unsaturated radicals per molecule in the silicone resin and more than two mercapto groups per molecule in the organic mercaptan and amount of silicone resin and organic mercaptan being such that there is from 0.5 to 1.5 aliphatic unsaturated radicals in the silicone resin for each mercapto group in the organic mercaptan, from 10 - 40 ppm based on the weight of the ultraviolet radiation curable composition of a dye with a visible colour selected from anthraquinone dyes and disazo dyes, and thereafter exposing the resulting composition to a dosage of ultraviolet radiation which causes the visible color to either disappear or change to a different color indicating that cure has occurred coincidentally. A method according to claim 1 wherein the silicone resins comprise from 20 to 40 mole percent monophenylsilsesquioxane units, 10 to 20 mole percent monomethylsilsesquioxane units, 20 to 35 mole percent dimethylsiloxane units and 10 to 30 mole percent methylvinylsiloxane units. A method according to claim 1 or claim 2 wherein the organic mercaptan is trimethylolpropane tri(3-mercaptopropionate). A method according to any of the preceding claims wherein the free radical inhibitor is selected from p-methoxyphenol, phenothiazine and mixtures thereof. A method according to any of the preceding claims wherein the ultraviolet radiation curing composition comprises a silicone resin in an amount of greater than 35 weight percent, from 5 to 30 weight percent mercaptan compound, from 1 to 25 weight percent acrylate compound, from 1 to 4 weight percent photoinitiator, less than 0.05 weight percent free radical inhibitor and optionally, from 1 to 5 weight percent of organic peroxide. A method according to any of the preceding claims wherein the dye is an anthraquinone dye having a Color Index Solvent Blue 104.

Inventors: FIELD ARTHUR J, STRONG MICHAEL R, FIELD, ARTHUR J., STRONG, MICHAEL R.
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1991
Main classification: C08K5
IPC codes: H05K1, H05K3, C08J3, C08F290, C08K5, C08F2