FUEL OIL COMPOSITIONS AND ADDITIVES

Abstract: Wax crystal modifiers for fuel oils are obtained by reaction of an ethylene alpha olefin polymer with reactive functionality (e.g. an acid group) and an oil soluble organic material with appropriate functionality, e.g., a polyisobutylene amine.

Description: "Fuel Oil Compositions and Additives" This invention relates to fuel compositions, and more especially to fuel oil compositions susceptible to wax formation at low temperatures. Heating oils and other distillate petroleum fuels, for example, diesel fuels, contain alkanes that at low temperature tend to precipitate as large crystals of wax in such a way as to form a gel structure which causes the fuel to lose its ability to flow. The lowest temperature at which the fuel will still flow is known as the pour point. As the temperature of the fuel falls to or goes below the pour point, difficulties arise in transporting the fuel through lines and pumps. Further, the wax crystals tend to plug fuel lines, screens, and filters at temperatures above the pour point. These problems are well recognized in the art, and various additives have been proposed, many of which are in commercial use, for depressing the pour point of fuel oils. Similarly, other additives have been proposed and are in commercial use, for reducing the size and changing the shape of the wax crystals that do form. Smaller size crystals are naturally desirable since they are less likely to clog a filter; certain additives inhibit the wax from crystal¬ lizing as platelets and cause it to adopt an acicular habit, the resulting needles being more likely to pass through a filter than are platelets. The additives may also have the effect of retaining in suspension in the fuel the crystals that have formed, the resulting reduced settling also assisting in prevention of blockages. The present invention is concerned to provide a fuel additive effective both to improve low temperature flow in a fuel and also to inhibit wax settling. In one aspect, the present invention is directed to a block copolymer of the formula AB, the moiety A being derivable and advantageously derived from an ethylene- alpha olefin, especially an ethylene-propylene, copolymer having a number average molecular weight of from 1000 to 10000, at least 30% of the polymer chains of which contain terminal ethenylidene unsaturation, the moiety B being derivable, and advantageously derived, from an oil- soluble organic material, advantageously a macromolecular material, he.ving a molecular weight of at least 800, advantageously a polymer having a number average molecular weight of at least 800. The moieties A and B may be linked in any way. Advantageously, however, the linkage is the product of one or more reactions between nucleophilic and electro- philic groups, the location of the groups being chosen with regard to a number of considerations, for example, their ease of attachment to the moieties. By way of example only, the electrophilic group may be derived from an acid substituent on one moiety with the nucleophilic group being from an amine, alcohol, amino alcohol or metal compound. Conveniently, the acid substituent (whether, for example, carboxylic acid, in the form of mono or diac d, or anhydride, or otherwise) is on the A moiety, and is advantageously at the end of the copolymer chain thereof, the nucleophilic group or groups being on the B moiety. The terminal unsaturation on the A polymer lends itself to epoxidation, however, and these epoxy groups may be opened to form hydroxyls suitable for bonding to acid groups on the B moiety. The polymers employed in this invention as moiety A are polymers of ethylene and one or more other alpha- olefins having the formula H 2 C=CHR 1 wherein R 1 is a straight chain or branched chain alkyl radical comprising 1 to 18 carbon atoms and wherein the polymer contains a high degree of terminal ethenylidene unsaturation. Preferably R 1 in the above formula is alkyl of from 1 to 8 carbon atoms, and more preferably is alkyl of l carbon atom. Therefore, useful comonomers with ethylene in this invention include, in addition to propylene, butene-1, hexene-1, octene-1, 4-methylpentene-l, decene- 1, dodecene-1, tridecene-1, tetradecene-1, pentadecene-1, hexadecene-l, heptadecene-1, octadecene-1, nonadecene-1 and mixtures thereof (e.g., mixtures of propylene and 1- butene, and the like) . The molar ethylene content of the polymers employed in this invention is preferably in the range of between about 20 and about 80 percent, more preferably between about 30 and about 70 percent, and most preferably between about 45 and about 65 percent, although higher or lower ethylene contents may be present. The polymers employed in this invention as moiety A generally possess a number average molecular weight of from about 1000 to about 10,000, preferably of from about 1000 to about 5,000; most preferably of from about 1500 to about 3000. The number average molecular weight for such polymers may be determined by several known techniques. A convenient method for such determination is by size exclusion chromatography (also known as gel permeation chromatography (GPC) which additionally provides molecular weight distribution information, see W. W. Yau, J. J. Kirkland and D. D. Bly, "Modern Size Exclusion Liquid Chromatography", John Wiley and Sons, New York, 1979.) . Consequently, such polymers generally possess an intrinsic viscosity (as measured in tetralin at 135°C) of between about 0.025 and about 0.6 dl/g, preferably of between about 0.05 dl/g, most preferably of between about 0.075 and about 0.4 dl/g. The polymers employed in this invention as moiety A are further characterized in that the polymer chains possess terminal ethenylidene-type unsaturation. Thus, one end of such polymers will be of the formula is as defined above and wherein POLY represents the polymer chain. A minor amount of th polymer chains may contain terminal ethenyl unsaturation, i.e. POLY-CH=CH 2 , and a portion of the polymers may contain internal monounsaturation. Preferably at least about 50 percent, more preferably at least about 60 percent, and most preferably at least about 75 percent (e.g. 75-98%) , of the polymer chains exhibit terminal ethenylidene unsaturation. The percentage of polymer chains exhibiting terminal ethenylidene unsaturation may be determined by FTIR spectroscopic analysis, titration, C 13 NMR, or proton NMR. The polymer used, as moiety A may be prepared as described in US-A-4,668,834, EP-A-128,046 and 129,368, and EP-A-0260999. The polymers for use in the present invention can b prepared by polymerizing monomer mixtures comprising ethylene in combination with the other monomer or monomers in the presence of a catalyst system comprising at least one metallocene (e.g., a cyclopentadienyl- transition metal compound) and an alumoxane compound. The comonomer content can be controlled through the selection of the metallocene catalyst component and by controlling the partial pressure of the various monomer The catalysts employed in the production of the reactant polymers are organometal lie coordination compounds which are cyclopentadienyl derivatives of a Group 4b metal of the Periodic Table of the Elements (56th Edition of Handbook of Chemistry and Physics, CRC Press [1975]) and include mono, di and tr icycl opentadienyls and their derivatives of the transition metals. Particularly desirable are the metallocene of a Group 4b metal such as titanium, zirconium, and hafnium. The alu oxanes employed in forming the reaction product with the metallocenes are themselves the reaction products of an aluminum trialkyl with water. In general, at least one metallocene compound is employed in the formation of the catalyst. As indicated, supra, metallocene is a metal derivative of a cyclopentadiene . The metallocenes usefully employed in accordance with this invention contain at least one cyclopentadiene ring. The metal is selected from the Group 4b preferably titanium, zirconium, and hafnium, and most preferably hafnium and zirconium. The cyclopentadie,nyl ring can be unsubst ituted or contain one or more substituents (e.g., from 1 to 5 substituents) such as, for example, = hydrocarbyl substituent (e.g., up to 5 C^ to C 5 hydrocarbyl substituents) or other substituents, e.g. such as, for example, a trialkyl silyl substituent. The /11469 7 meta l l ocene can conta in one , two , or three cycl opentadi enyl rings ; however , two rings are pre ferred . Use ful meta l l ocenes can be represented by the genera l formulas : I . ( Cp) n HR n X q wherein Cp is a cyclopentadienyl ring, M is a Group 4b transition metal, R is a hydrocarbyl group or hydrocarbox group having from 1 to 20'* carbon atoms, X is a halogen, an m is a whole number from 1 to , n is a whole number from to 3, and q is a whole number from 0 to 3. I I . ( C 5 R , k ) g M s ( C 5 R ' k ) MQ 3 . g and III. R" s (C 5 R' k ) 2 MQ' wherein (C 5 R , k ) is a cyclopentadienyl or substitute cyclopentadienyl, each R' is the same or different and i hydrogen or a hydrocarbyl radical such as alkyl, alkenyl aryl, alkylaryl, or arylalkyl radical containing from 1 t 20 carbon atoms, a silicon containing hydrocarbyl radical or hydrocarbyl radicals wherein two carbon atoms are Joine together to form a c 4 "" c 6 r i n 9 » R " is a c ι" c alkylene radical, a dialkyl germanium or silicon, or alkyl phosphine or amine radical bridging two (CcR' rings, Q is a hydrocarbyl radical such as aryl, alkyl alkenyl, alkylaryl, or aryl alkyl radical having from 1-2 carbon atoms, hydrocarboxy radical having from 1-20 carb atoms or halogen and can be the same or different from ea other, Q' is an alkylidene radical having from 1 to abo 20 carbon atoms, s is 0 or 3 , g is 0, 1 or 2, s is 0 when is 0, k is 4 when s is 1, and k is 5 when s is 0, and M as defined above. Exemplary hydrocarbyl radicals a methyl, ethyl, propyl, butyl, amyl, isoa yl, hexy isobutyl, heptyl, octyl, nonyl, decyl, cetyl, 2-ethylhexy phenyl and the like. Exemplary silicon containi hydrocarbyl radicals are trimethylsilyl, triethylsilyl a triphenylsilyl. Exemplary halogen atoms include chlorin bromine * , fluorine and ' iodine and of these halogen atom chlorine is preferred. Exemplary hydrocarboxy radicals a methoxy ethoxy, butoxy, a yloxy and the like. Exemplary o 1/11469 the alkylidene radicals is ethylidene, ethylidene and propylidene. Illustrative, but non-limiting examples of the metallocenes represented by formula I are dialkyl metallocenes such as bis ( cycl opentad ienyl ) titanium dimethyl , b is ( cycl ope n t d i e ny 1 ) t i tanium diphenyl, b i s ( cyc l opentad ie ny l ) z i rcon i um d imethy l , b i s ( cyc l opentad i eny l ) z i rcon ium dipheny l , bis (cyclopentadienyl ) ha fn ium dimethyl and diphenyl, bis ( cycl opentadienyl ) t itan ium di-neopentyl , bis ( cycl opentadienyl ) zirconium di-neopentyl , b i s ( cyc l opentad ienyl ) t i tan i um d iben zy l , bi s ( cyc l opentadienyl ) z i rconium d ibe nz y l , bis (cyclopentadienyl ) vanad ium dimethyl; the mono alkyl metallocenes such as bis (cyclopentadienyl) titanium methyl chloride, bis (cyclopentadienyl) titanium ethyl chlorid bis (cyclopentadienyl ) titanium phenyl chloride, bi s (cyclopentadienyl ) zirconium hydrochloride , b i s ( cy c 1 op en tadieny 1 ) z i r con ium methyl chloride, b i s ( cy c 1 open t ad ie ny 1 ) z i r c on ium ethyl chloride b i s ( cy c 1 open tad i enyl ) z i rcon ium phenyl chloride b i s ( cy c 1 op en t ad i eny 1 ) t i t an i um methyl bromide b i s ( c y c 1 o p e n t a d i eny 1 ) t i t a n i urn methyl iodide bi s ( cyclopentadienyl ) titanium ethyl bromide b i s ( c y c 1 o p e n t a d i eny 1 ) titanium ethyl iodide b i s ( cy c 1 ope n t ad i e ny 1 ) t i t a n i um phenyl bromide b i s ( c y c 1 o p e n t a d i eny 1 ) t i t a n i u phenyl iodide b i s ( c y c 1 op e n t ad i e ny 1 ) z i r c on ium methyl bromide bis (cyclopentadienyl) zirconium methyl iodide bis (cyclopentadienyl ) zirconium ethyl bromide bis ( cycl opentadienyl ) z irconium ethyl iodide b i s ( c y c 1 op en t a i e ny 1 ) z i r c o n i um phenyl bromide bis (cyclopentadienyl) zirconium phenyl iodide; the trialky metallocenes such as cyclopentadienyltitanium tri ethyl cyclopentadienyl zirconium triphenyl, and cyclopentadien - zirconium trineopentyl , cyclopentadienylzirconiu /11469 trimethyl , c y c 1 o p e n t a d i e n y 1 h a f n i u m triphenyl , cycl opentad i e ny l ha f n ium tr i neopentyl , and cyclopentadienylha niu trimethyl . Illustrative, but non-limiting examples of II and III- metallocenes which can be usefully employed ar monocyc l opentad i enyl s titanocenes such as , pe nt ame thy 1 cy c 1 ope n tad i e ny 1 titanium trichloride, pe ntae thy 1 eye 1 open tad i eny 1 titanium trichloride, bis (pentamethylcyclopentadienyl) titanium diphenyl, th ca rbene repre s en ted by the f ormu l a bis ( cyclopentadienyl) itanium=CH 2 and derivatives of thi reagent such as b is ( cyclopentadienyl ) Ti=CH 2 . Al (CH 3 ) 3 ) Ti ( IV compounds such as bis(indenyl) titanium diphenyl o dichloride, bis (methylcyclopentadienyl) titanium diphenyl o dihalides; dialkyl, trialkyl, tetra-alkyl and penta-alky cyclopentadienyl ti tanium compounds such a bis ( 1 , 2 -dimethy lcyclqpentadienyl) titanium diphenyl o dichloride, bis(l, 2 -diethylcyclopenta ienyl) titaniu diphenyl or dichloride and other dihalide complexes silicon, phosphine, amine or carbon bridged cyclopentadie complexes, such as di ethylsilyldicyclopentadienyl titani diphenyl or dichloride, methyl phosphine dicyclopentadien titani m diphenyl or dichloride, ethylenedicycl pe tadienyl titanium diphenyl or dichloride and oth complexes described by formulae II and III. Illustrative b-ut non-limiting examples of t zirconocenes of Formula' II and III which can be useful employed are, pentamethylcyclopentadienyl zirconi trichloride, pentae ^hylcyclopentadienyl zirconi trichloride, the alkyl substituted cyclopentadienes , su as bis(ethylcyclopentadie'nyl) zirconium dimethy bis (beta-phenylpropylcyclopentadienyl) zirconium dimethy bis (methylcyclopentadienyl ) z irconium dimethy bis (n-butylcy-clopentadienyl ) zirconium dimeth 1469 - 10 - . bis (cyclohexyl methyl cyclopentadienyl) zirconium dimeth bis (n-octyl-cyclopentadieny 1 ) z irconium dimethyl, a haloalkyl and dihydride, and dihalide complexes of t above; dialkyl, trialkyl, tetra-alkyl, and penta-alk cyclopentadienes , such as b is (pentamethylcyclopent dienyl ) zirconium diphenyl, bis (pentamethylcyclopent dien l ) zirconium dimethyl, bis ( 1 , 2-dimethylcyclopent dienyl) zirconium dimethyl and mono and dihalide and hydri complexes of the above; silicon, phosphorus, and carb bridged cyclopentadiene complexes such as dimethylsily dicyclopentadienyl zirconium dimethyl, methyl halide dihalide, and methylene dicyclopentadienyl zirconi dimethyl, methyl halide, or dihalide. Mono, di a tri-silyl substituted cyclopentadienyl compounds such bis (trimethylsilylcyclopentadienyl) zirconium dichloride a dimethyl bis (1, 3-di-trimethylsilylcyclopent d i e n 1 ) z i r c o n i um dichloride and dimethyl a bis ( 1 , 2 , 4 -tri- trimethylsilylcyclopentadienyl) zirconi dichloride and dimethyl. Carbenes represented by formulae Cp 2 Z r = CH 2 P ( C 6 H 5 ) 2 CH 3 , and derivativ I " 1 of these compounds such as Cp 2 2rCH 2 CH(CH 3 ) CH 2 . Mixed cyclopentadienyl metallocene compounds s as cyclopentadienyl (pentamethyl cyclopentadienyl) zircon dichloride, (1 , 3-di-trimethylsilylcyclopentadien (pentamethylcyclopentadienyl) zirconium dichloride, cyclopentadienyl (indenyl ) zirconium dichloride can employed. Bis (cyclopentadienyl)hafniu dichlori bi s ( cycl open tad ienyl ) hafnium; dimethyl, bis(cyc pent ad ieny 1 ) va nad ium dichloride and the like illustrative of other metallocenes. 1469 - 11 - Some preferred metallocenes are bis (cyclopent dienyl ) zirconium; dimethyl, bis (cyclopentadienyl) zirconi dichloride; bi s ( cycl opentadienyl) titanium dichlorid b i s ( me thy 1 cy c 1 open t d i eny 1 ) zirconium dichlorid bis (methylcyclopentadienyl) titanium dichlorid bis (n-butylcyclopentadienyl) zirconium dichlorid d i ethy lsily Id icyclopentadienyl zirconium dichlorid bis (trimethylsilycyclopentadienyl) zirconium dichloride; a di ethylsilyldicyclopentadienyl titanium dichlorid bis(indenyl) zirconium dichloride; bis (4 , 5 , 6 , 7 -tet hydroindenyl) zirconium dichloride; the raceraic and/or m isoraer of 1 , 2-ethylene-bridged bis ( , 5, 6 , 7-tetrahyd i ndenyl ) zirconium dichloride; the race ic and/or m isomer of 1 , 1-dimethylsilyl-bridged bis ( , 5, 6, 7-tetrahyd indenyl ) zirconium dichloride; and the racemic and/or m isomer of 1 , 1-dimethylsilyl-bridged bis (methylcyclopen dienyl) zirconium dichloride. The alu oxane compounds useful in the polymeri tion process may be cyclic or linear. Cyclic alumoxa may be represented by the general formula (R-Al-0) n wh linear alumoxanes may be represented by the general form R (R-A1-0) n' A1R 2 . In the general formula R is a C^ alkyl group such as, for example, methyl, ethyl, prop butyl and pentyl, n is an integer of from 3 to 20, and is an integer from 1 to about 20. Preferably, R is met and n and n' are 4-18. Generally, in the preparation alumoxanes from, for example, aluminum trimethyl and wa a mixture of the linear and cyclic compounds is obtained. The alumoxanes can be prepared in various w Preferably, they are prepared by contacting water wit solution of aluminum trialkyl, such as, for examp aluminum trimethyl, in a suitable organic solvent suc toluene or an aliphatic hydrocarbon. For example, aluminum alkyl is treated with water in the form of a m solvent. in an alternative method, the aluminum alkyl as aluminum trimethyl can be desirably contacted wi hydrated salt such as hydrated copper sulfate or ferrous sulfate. Preferably, the alumoxane is prepared in the presence of a hydrated ferrous sulfate. The method comprises treating a dilute solution of aluminum trimethyl in, for example, toluene, with ferrous sulfate represented by the general formula FeS0 4 .7H 2 0. The ratio of ferrous sulfate to aluminum trimethyl is desirably about '1 mole of ferrous sulfate for 6 to 7 moles of aluminum trimethyl. The reaction is evidenced by the evolution of methane. The mole ratio of aluminum in the alumoxane to total metal in the metallocenes which can be usefully employed can be in the range of about 0.5: 1 to about 1000: 1 , and desirably about 1: 1 to about 100:1. Preferably, the mole ratio will be in the range of 50:1 to about 5:1 and most preferably 20:1 to 5:1. The solvents used in the preparation of the catalyst system are inert hydrocarbons, in particular a hydrocarbon that is inert with respect to the catalys system. Such solvents are well known and include, fo example, isobutane, butane, pentane, hexane , heptane, octane, cyclohexane, methylcyclohexane, toluene, xylene an the like. Polymerization is generally conducted a temperatures ranging between about 20 * and about 300'C preferably between about 30" and about 200 * C. Reactio time is not critical and may vary from several hours o more to several minutes or less, depending upon factor such as reaction temperature, the monomers to b copolymer ized, and the like. One of- ordinary skill in th art may readily obtain the optimum reaction time for given set of reaction pa rameters by routin experimentation. The catalyst systems described herein are suitab for the polymerization of olefins in solution over a wi range of pressures. Preferably, the polymerization will completed at a pressure of from about 10 to about 3, bar, and generally at a pressure within the range f about 40 bar to about 2,000 bar, and most preferably, polymerization will be completed at a pressure within range from about 50 bar to about 1,500 bar. A f ter polymerization and , optionall deactivation of the catalyst (e.g. , by conventio techniques such as contacting the polymerization react medium with water or an alcohol, such as ethan propanol , isopropanol, etc., or cooling or flashing medium to terminate the polymerization reaction) , product polymer can be recovered by processes well known the art. Any excess reactants may be flashed off from polymer. The polymerization may be conducted employ liquid monomer, such as liquid propylene, or mixtures liquid monomers (such as mixtures of liquid propylene 1-butene) , as the reaction medium. Alternative polymerization may be accomplished in the presence o hydrocarbon inert to the polymerization such as but pentane, isopentane, hexane, isooctane, decane, tolu xylene, and the like. In those situations wherein the molecular we of the polymer product that would be produced at a g set of operating conditions is higher than desired, an the techniques known in the prior art for control molecular weight, such as the use of hydrogen an polymerization temperature control, may be used in process of this invention. If so desired, polymerization may be carried out in the presence of hydrogen to lower the polymer molecular weight. shoul'd be taken to assure that terminal ethenyli unsaturation is not reduced to less than about 30 pe of the polymer chains. However, the polymers are preferably formed in the substantial absence of added H 2 gas, that is, the absence of H 2 gas added in amounts effective to substantially reduce the polymer molecular weight. More . preferably, the polymerizations will be conducted employing less than 5 wppm, and more preferably less than 1 wppm, of added H 2 gas, based on the moles of the ethylene monomer charged to the polymerization zone. When carrying out the polymerization in a batch-type fashion, the reaction diluent (if any), ethylene and alpha-olefin comonomer(s) are charged at appropriate ratios to a suitable reactor. Care must be taken that all ingredients are dry, - with the reactants typically being passed through molecular sieves or other drying means prior to their introduction into the reactor. Subsequently, either the catalyst and then the cocatalyst, or first the cocatalyst and then the catalyst are introduced while agitating the reaction mixture, thereby causing polymerization to commence. Alternatively, the catalyst and cocatalyst may be premixed in a solvent and then charged to the reactor. As polymer is being formed, additional monomers may be added to the reactor. Upon completion of the reaction, unreacted monomer and solvent are either flashed or distilled off, if necessary by vacuum, and the low molecular weight copolymer withdrawn from the reactor. The polymerization may be conducted in a continuous manner by simultaneously feeding the reaction diluent (if employed) , monomers, catalyst and cocatalyst to a reactor and withdrawing solvent, unreacted monomer and polymer from the reactor so as to allow a residence time of ingredients long enough for forming polymer of the desire molecular weight and separating the polymer from th reaction mixture. Referring now to moiety B, this is preferably a polymer and should, as indicated, have a number average molecular weight of at least 800, and advantageously has a molecular weight in the^range of from 900 to 5000, preferably 900 to "2000. Advantageously, the molecular weights of moieties A and B are similar, for example one may be up to 4 times that of the other and preferably one is within the range of 75% to 125% of the other. If the molecular weights differ, that of B is advantageously greater than A. The B moiety may be terminally linked to the A moiety, or it may be linked to the A moiety at a location in the B moiety between its ends. The latter will result if, for example, the A moiety is terminated by a succinic acid, which may botnd * to one molecule of a polymeric secondary amine to form an amide or an amine salt; in cases of this type it is the sum of the mole¬ cular weights of the polymeric' groups attached to the nitrogen atom that is referred to above. The polymer chains of the parts of the B moiety may be branched or have pendent groups, and also they may have different chain lengths. It is within the scope of the invention to have more than one chain forming the B moiety, as will result from the reaction of two moles of a long chain or polymeric primary or secondary amine with a succinic acid terminated moiety, giving two and four portions of the B moiety respectively. The polymeric portion of moiety B is desirably per'se oil-soluble, and is preferably per se soluble in the oil to be treated. To this end, the polymer is of low crystallinity and is preferably amorphous. The chain may be a hydrocarbon chain, advantageously an aliphatic, saturated or unsaturated hydrocarbon chain, -optionally interrupted by oxygen or other hetero atoms, e.g., a polyoxyalkylene. Other suitable polymers include polysiloxanes, polytetra- methylene glycols, polypropylene and polystyrene. The preferred polymers for forming moiety B are polymers comprising a major amount of C 2 to C 10 , e«9- C 2 to C 5 , monoolefin. Such olefins include ethylene, propylene, butylene, pentene, octene-1, styrene, etc. although the crystallinity of polyethylene renders ethylene unsuitable as a sole monomer. The polymers may be homopolymers, for example, polyisobutylene, or copolymers of two or more such olefins such as copolymers of ethylene and propylene; butylene and isobutylene; or propylene and isobutylene. Advantageously, however, moiety B is derived from a polyisobutylene. As indicated above, the nature of the linkage between moieties A and B is not critical nor, when the linkage is asymmetrical, is its orientation. By way of example, however, the preparation of a product in which an electrophilic group in the form of an acid located on the ethylene propylene polymer of moiety A is linked to a nucleophilic group, for example, - 17 - one in the form of an amine, on the polymer of moiety B will be discussed in more detail. An ethylene-propylene polymer substituted mono-or dicarboxylic acid material, i.e., acid, anhydride or acid ester used in this invention, may be the reaction product of an ethylene-propylene polymer with a monounsaturated carboxylic reactant comprising at least one member selected from (i) monounsaturated C to C 10 dicarboxylic acid wherein (a) the carboxyl groups are vicinal, and (b) at least one, preferably b,oth, of said adjacent carbon atoms are part of said monounsaturation; (ii) derivatives of (i) such as anhydrides; (iii) monounsaturated C 3 to C 10 monocarboxylic acids wherein the carbon-carbon double bond is allylic to the carboxy group. Upon reaction with the polymer, the monounsaturation of the monounsaturated carboxylic reactant becomes saturated. Thus, for example, maleic anhydride becomes a polymer substituted succinic anhydride, and acrylic acid becomes a polymer substituted propionic acid. Typically, from about 0.7 to about 4.0 (e.g., 0.8 to 2.6) , preferably from about 1.0 to about 2.0, and most preferably from about 1.1 to about 1.7 moles of said monounsaturated carboxylic reactant are charged to the reactor per mole of polymer charged. Normally, not all of the . polymer reacts with the monounsaturated carboxylic reactant and the reactio mixture will contain unreacted polymer. -The unreacte polymer is typically not removed from the reaction mixtur (because such removal is difficult and would b commercially infeasible) and the product mixture, strippe 1/11469 - 18 - of any monounsaturated carboxylic reactant is employed for further reaction with the amine as described hereinafter to make the product. Characterization of the average number of moles of monounsaturated carboxylic reactant which have reacted per mole of polymer charged to the reaction (whether it has undergone reaction or not) is defined herein as functionality. Said functionality is based upon (i) determination of the saponif ication number of the resulting product mixture using potassium hydroxide; and (ii) the number average molecular weight of the polymer charged, using techniques well known in the art. Functionality is defined solely with reference to the resulting product mixture. Although the amount of said reacted polymer contained in the resulting product mixture can be subsequently modified, i.e. increased or decreased by techniques known in the art, such modifications do not alter functionality as defined above. The terms ethylene-alpha-olef in polymer substituted monocarboxylic acid material and ethylene-alpha-olef in polymer substituted dicarboxylic acid material are intended to refer to th product mixture whether it has undergone such modificatio or not. Accord ingly , the functionality of th e thy 1 ene-alpha-olef in polymer substituted mono- an dicarboxylic acid material will be typically at least abou 0.5, preferably at least about 0.8, and most preferably a least about 0.9 and will vary typically from about 0.5 to about 2.8 (e.g. , 0.6 to 2), preferably from about 0.8 t about 1.4, and most preferably from about 0.9 to about 1.3. Exemplary of such monounsaturated carboxyli reactants are fumaric acid, itaconic acid, maleic acid maleic anhydride, chloromaleic acid, chloromalei anhydride, acrylic acid, ethacrylic acid, crotonic acid cinnamic acid, and lower alkyl (e.g., C 1 to C 4 alkyl . acid esters of the foregoing, e.g., methyl aleate, ethyl fumarate, methyl fumarate, etc. 1/11469 19 The polymer can be reacted with the monounsaturated carboxylic reactant by a variety of methods. For example, the polymer can be first halogenated, chlorinated or bro inated to about 1 to 8 wt. %, preferably 3 to 7 wt. * chlorine, or bromine, based on the weight of polymer, by passing the chlorine or bromine through the polymer at a temperature of 60 to 250'C, preferably 110 to 160*C, e.g.- 120 to 140'C, for about 0.5 to 10, preferably 1 to 7 hours. The halogenated polymer may then be reacted with sufficient monounsaturated carboxylic reactant at 100 to 250'C, usually about 180* to 235'C, for about 0.5 to 10, e.g. 3 to 8 hours, so the product obtained will contain the desired number of moles of the monounsaturated carboxylic reactant per mole of the halogenated polymer. Processes of this general type are taught in U.S. Patents 3,087,436; 3,172,892; 3,272,746 an others. Alternatively, the polymer and the monounsaturate carboxylic reactant are mixed and heated while addin chlorine to the hot material. Processes of this type ar disclosed in U.S. Patents 3,215,707; 3,231,587; 3,912,764 4,110,349; 4,234,435; and in U.K. 1,440,219. While chlorination normally helps increase th reactivity of polyolefins with monounsaturated carboxyli reactant, it is not necessasry with the present polymers du to their high terminal bond content and reactivity Preferably, therefore,, the polymer and the monounsaturate carboxylic reactant are contacted at elevated temperatur to cause a thermal "ene" reaction to" take place. Therma "ene" reactions have been heretofore described in U.S Patents 3,361,673 and 3,401,118, the disclosures of whic are hereby incorporated by reference in their entirety. I has been surprisingly f.ound that the terminall ethylenically-unsaturated ethylene alpha-olefin polyme used in this invention readily undergo such thermal "en reaction's under conditions in which the formation 1/11469 " 20 ~ sediment, or other by-products contributing to product haze, is greatly minimized or avoided altogether. The improved low sediment ene reaction product mixture is preferably formed using an eth lene-propylene copolymer having a number average molecular weight of from about 900 to 10,000, more preferably from about 1500 to 10,000, and most preferably ' greater than about 1800 to about 5, 000, and a polydispersity of less than about 4, preferably less than about 3, e.g., from 1.1 to 3.5, most preferably from 1.2 to 3. Preferably, the polymers used in this invention contain less than 5 wt%, more preferably less than 2 wt%, and most preferably less than 1 wt% of a polymer fraction comprising polymer molecules having a. molecular weight of less than about 300, as determined by high temperature gel premeation chromatography employing the corresponding polymer calibration curve. Such preferred polymers have been found to permit the preparation of ene reaction products, particularly when employing maleic anhydride as the unsaturated acid reactant, with substantially no visibly observable sediment. In the event the poly ej produced as described above contains greater than about 5 wt% of such a low molecular weight polymer fraction, the polymer can be first treated by conventional means to remove the low molecular weight fraction to the desired level prior to initiating the ene reaction, and preferably prior to- contacting the polymer with the selecte unsaturated carboxylic reactant(s) . For example, th polymer can be heated preferably with inert gas (e.g., nitrogen) stripping, at elevated temperature under reduced pressure to volatilize the low molecular weigh polymer components which can then be removed from the hea treatment vessel. The precise temperature, pressure an time for such heat treatment can vary widely depending o such factors as "as the polymer number average- molecula 1/11469 - 21 " weight, the amount of the low molecular weight fraction to be removed, the particular monomers employed and other factors. Generally, a temperature of from about 60 to 100'C and a pressure of from about 0.1 to 0.9 atmospheres and' a time of from about 0.5 to 20 hours (e.g., 2 to 8, hours) will be sufficient. In this process , the selected polymer and monounsaturated carboxylic reactant are contacted for a time and under conditions effective to form the desired ethylene alpha-olefin polymer substituted mono- or dicarboxylic acid material. Generally, the polymer and monounsaturated carboxylic reactant will be contacted in a polymer to unsaturated carboxylic reactant mole ratio usually from about 1:1 to 1:10, and preferably from about 1:1 to 1:5, at an elevated temperature, generally from about 120 to 260'C, preferably from about 160 to 240*C. The reaction will be generally carried out, with stirring for a time of from about 1 to 20 hours, preferably from about 2 to 6 hours. The reaction is preferably conducted in the substantial absence of 0 2 and water (to avoid competing side reactions) , and to this end can be conducted in an atmosphere of dry N 2 gas or other gas inert unde the reaction conditions. ■ The reactants can be charged separately or together as a mixture to the reaction zone, and the reaction can be carried out continuously, semi-continuously or batchwise. Although not generall necessary, the reaction can be carried out in the presenc of a liquid diluent or solvent, e.g., a hydrocarbon diluen such as mineral lubricating oil, toluene, xylene dichlorobenzene and the like. The polymer substitute mono- or dicarboxylic acid material thus formed can b recovered from the liquid reaction mixture, e.g., afte stripping the reaction mixture, if desired, with an iner gas such as N, to remove unreacted unsaturated carboxyli reactant." The "ene" reaction product mixture thereby obtained has been surprisingly found to have a substantially reduced content of sediment or other solid by-products as impurities and can be employed, without filtering, centrifuging, clarification, phase separation o>r other conventional product purification treatments, as, e.g., an additive to lubricating oils or as intermediate in the preparation of derivative products for use in lubricating oils, as will be more completely described hereinafter. The ene reaction product mixture is furthe improved by being substantially free of chlorine, that is, by having a chlorine content of less than about 25 ppm b weight, preferably less than about 10 ppm by weight. The ene reaction product mixture comprising th desired ethylene-propylene substituted mono- o dicarboxylic acid material (e.g.., ethylene-propylen polymer-substituted succinic anhydride) formed by th process of this invention will generally contain unreacte polymer, (that is, polymer which is unsubstituted by th mono- or dicarboxylic acid moiety) , in a concentration o less than about 40 wt.% (e.g., from 5 to 35 wt.%), mor preferably less than about 30 wt.% (e.g from 10 to 25 wt. and will be generally characterized by a VR valu ("viscosity ratio" value) of not greater than about 4.1 usually not greater than about 4.0, preferably from abou 2.0 to 3.9, and most preferably from about 3.0 to 3.8. A used herein, the term "VR value", is intended to mea quotient determined by the expression (IV) : VR = VISb VISa wherein VISa is the kinematic viscosity (KV) of the e reaction product mixture at 100'C in units of centistok (as determined by ASTM Method No. D445) and VISb is t . cold cranking simulator (CCS) viscosity of the ene reacti product mixture at -20'C in units of poise (as determin by ' ASTM Method No. D2602) , wherein the measurements are 91/11469 ~ 23" ade upon a 2 wt% solution of the ene reaction product mixture in an oil (herein termed the "reference oil") comprising S150N (solvent 150 neutral) mineral lubricating oil (Exxon Company U.S.A.) , wherein the such reference oil is characterized by an ASTM D445 kinematic viscosity of 5.2* cSt (100'C) and an ASTM D2602 CCS viscosity of 19.2 poise (± 0.4 poise) (at -20"C) . The "VR r " value of the reference oil will then be about 3.7 + 0.1. Illustrative of the ene reaction products suitable for use in this invention are the following ethylene-propylene copolymer-substituted succinic acids and succinic anhydrides ( EPSA) „ Ene Polymer Product (Mn) E SΛ 300-10,000 EPSA 300-10,000 EPSΛ 700-5,000 EPSA 700-5,000 EPSΛ 5,500-10,000 EPSΛ 5,500-10,000 EPSA 1,500-10,000 NOTES: (1) .Wt.% active ingredient. (2) SA=succinic anhydride; polymer=ethylene-propylene (EP) copolymer; moles of polymer in ratio based on the total of both the reacted and unreacted polymer; moles of "SΛ" based on the number of moles of succinic anhydride moieties per mole of ene reaction product. - 25 - The two components are readily reacted in solution at a temperature in the range of 60° to 150°C, preferably 70 to 120°C, generally for 1 to 10, e.g., 2 to 6 hours until the desired amount of water is removed. The heating may be carried out to favor formation of i ides, of mixtures of imides and amides, or of amides and salts, whichever type of reaction product is desired. Reactant ratios of polymer substituted mono- and dicarboxylic acid material to equivalents of amine as well as the other nucleophilic reactants described herein can vary considerably, depending on the reactants and type of bonds formed. When the polymer comprises a polymer substituted dicarboxylic acid material, contain¬ ing dicarboxylic acid producing moieties derived from any of the above monounsaturated dicarboxylic acids, or anhydride or ester derivatives thereof, generally from 0.5 to 1.0 mole of dicarboxylic acid moiety content (e.g. grafted maleic anhydride content) is used, per equivalent of nucleophilic reactant, e.g., amine. The block copolymer AB has excellent solubility in various fuel oils, especially middle distillate fuel oils, improving their low temperature flowability, in particular lowering pour point and inhibiting wax settling. Examples of fuel oils to which the copolymer may usefully be added are straight run or cracked gas oil, and blends in any proportion of straight run and thermally or catalytically cracked distillate. Accordingly, the present invention also provides a fuel oil composition comprising the copolymer AB as defined above. Advantageously the copolymer AB is present in a proportion of from 0.005 to 0.5%, preferably from 0.01 to 0.1%, by weight, based.on the weight of the fuel oil. The present invention further provides a fuel oil additive concentrate comprising 2 to 90%, advantageously 5 to 50%, by weight of the copolymer AB, as defined above, in fuel oil or in a solvent miscible with fuel oil. Also provided by the invention is the use of the copolymer AB, as defined above, as a wax crystal modifier in a fuel oil. The copolymer AB may be used in a fuel oil as the sole additive. It may, however, be used in association with other low temperature flow.improvers, for example the amide/amine salt reaction product of a carboxylic acid or anhydride and a hydrocarbyl substituted amine, for example, phthalic acid and dihydrogenated tallow amine; a "comb" polymer, for example a copolymer of an alpha-olefin or vinylacetate and the maleic or fumaric esters of e.g., a C 10 to C 18 n-alkyl alcohol; or an ethylene-vinyl ester copolymer, for example, an ethylene- vinyl acetate copolymer. The following examples illustrate the invention: 1469 " 28" EXAMPLE 1 - Preparation of Ethylene-Propylene Copolymer. A 1 liter Zipperclave reactor (Autoclav Engineers) equipped with a water jacket for temperatur control, with a septum inlet for syringe injection o catalyst, and with a supply of purified nitrogen, liqui propylene, and ethylene was used used in these polymeri zations. The reactor was cleaned with hot toluene and the was purged well with dry nitrogen at 100*C. The reacto was cooled to 25'C and 10.0 cc of a 4.0 wt% toluen solution of methylalurooxane was injected along with 100 c of distilled toluene at 0 psig under nitrogen. Liqui propylene monomer (200 cc) was added from a calibrate burette at 25'C. The reactor contents were stirrred a heated to 115 ' C at which point the reactor pressure was 3 psig. 1.00 cc of a toluene solution of bis(n-butylcycl pentadienyl) zirconium dichloride (l.oo mg) was inject and ethylene at a pressure of 405 psig was immediate supplied. Ethylene was fed on pressure demand in order keep the system pressure at 405 psig. The rate of ethyle flow was recorded continuously during the course of t polymerization. The reaction was continued for 15 minut after which the reaction was stopped by rapidly depre suring and cooling the reactor to 25 * C. The polyme product was collected and the toluene solvent w evaporated in an air stream. The polymer weight w determined to be 103.1 gms, and the polymer was analyz by size-exclusion chromatography and found to contain wt% ethylene and to have a number average molecular weig of 1100, a weight average molecular weight of 5400 and polydispersity of 4.9. The polymer product was found contain 2.5 wppm Zr and 1.75 wppm Cl. EXAMPLE 2 - Preparation of Ethylene-Propylene Copolymer. The polymerization was performed as in Example except that the reactor temperature was maintained at 100 and 1.60 mg of di ethylsilyldicyclopentadienyl zirconium dichoride was used as catalyst instead o bis (n-butylcyclopentadienyl) zirconium dichloride. Th reactor pressure was maintained at 380 psig by a regulate ethylene supply. The yield of the copolymer was 111.2 g and the polymer was determined to contain the ethylen content indicated in Table I and to have a number averag molecular weight of 1390, a weight average molecular weigh of 4030 and polydispersity of 2.9. The polymer product wa found to contain 2.0 wppm Zr and 1.5 wppm Cl. EXAMPLE 3 - Preparation of Ethylene-Propylene Copolymer. The polymerization was performed as in Example except that the reactor temperature was maintained at 90* and 270 cc of liquid propylene was charged. The react pressure was maintained by a regulated ethylene suppl The yield of the copolymer was 16.3 gms and the polymer w determined to contain the ethylene content indicated Table I and to have a number average molecular weight 1750, a weight average molecular weight of 4960 a polydispersity of 2.8. The polymer product was found contain 16 wppm Zr and 10 wppm Cl. EXAMPLE 4 - Preparation of Ethylene-Propylene Copolymer. The polymerization was performed as in Example except that the reactor temperature was maintained at 80* The reactor pressure was maintained at 365 psig by regulated ethylene supply for 1 hour. The yield of t copolymer was 234 gms and the polymer was determined have a number average . olecular weight of 2710, a weig average molecular weight of 7980 and polydispersity 2.9. The polymer product was found to contain the ethyle content indicated in Table I and to contain 1.0 wppm Zr a 0.7 wppm Cl. /11469 - 30 - EXAMPLE 5 - Preparation of Ethylene Butene-1 Copolymer. The polymerization was performed as in Example except that 270 cc of liquid butene-1 was charged instea of the propylene. The reactor pressure was maintained a' 167 psig by a regulated ethylene supply. The yield of th copolymer was 176.6 gms and the polymer was determined t have a number average molecular weight of 860, a weight average molecular weight of 2710 and polydispersity o 3.1. The polymer product was found to contain 1.5 wppm Z and 1.1 wppm Cl. EXAMPLES 6-10 - Preparation of Ethylene-propylene Copolyme Substituted Succinic Anhydride (EPSA) In a series of runs, the selected moles of the E copolymers prepared as above and pulverized malei anhydride are charged under dry N 2 at atmospheri pressure to a 100 m.1. pressure reactor equipped with stirrer and a thermocouple and heated by means of a electric heating mantle. No added solvent or diluent f the reactants is employed. Rather the reaction i conducted in the melt. In each run, the reaction mixtu is heated to 70 * C and the reactor is gently purged with d N 2 by bubbling through the liquid reaction mass for minutes. The purging is then ceased and the react temperature is raised to 220"C and kept at that temperatu under autogenous pressure for 4 hours while stirring. T liquid reaction mixture is then cooled to about 60 * C, a transferred to a glass beaker. Dry gaseous nitrogen passed through the liquid to strip off unreacted male anhydride at about 140*C until no trace of maleic anhydri is detected with IR. The liquid product containing, t EPSA and unreacted EP is analyzed for succinic anhydride the following titration technique: a 2 g. sample of t polymer is dissolved in a solvent comprising 80 ml of TH 6 ml of pyridine and 0.3 ml of water and titrated with methanol solution of tetrabutyl ammonium hydroxide usi thymol blue to a color end point. The acidity - 31 - calculated from the milliliters of base solution used. The product is also observed to determine the presence of any sediment. Table I Feed Copolymer As Mol . Ratio Titration of Succinic Acid in the Prepared In of EP to MA EPSA (or EP/PIB-SA) Product. Meg/gram Example EP Copolymer Example Char ed Theor. Found % Conv. (3) Sediment(4) 0.91 0.73 80.3 moderate 0.72 0.65 89.3 moderate 0.57 0.43 75.4 none R n = 2710 0.37 0.31 83.8 none ^ 55 wt.% C iNJ 10 M n = 2710 0.37 0.56 150 slight 55 wt.% C- NOTES: EP - ethylene-propylene copolymer; MA = maleic anhydride, (1) EP fl n = 2710, 55 wt.% C 2 ~ ; PIB H = 1200. (2) (EP + PIB)/MA = 1.0:1.2 mole ratio charged, (3) Based on (theoretical - found) meq/grt SA. (4) Low amounts of sediment not quantified. Example 11 - Preparation of the polyisobutylene amine Polyisobutylene, of number average molecular weight 902, and viscosity at 100°C of 219 cst (2.19 x 10"" 4 m 2 /s) , was chlorinated at 120°C-130°C for 6 hours to introduce an average of one chlorine atom per polymer chain. The resulting CIPIB, consisting mainly of allylic halides, is treated with ethylene diamine (10 parts of amine per part of CIPIB) at about 118°C for 5 hours. Remaining amine is distilled off under vacuum, then the product is treated with an aqueous Na2C0 3 solution to release residual amine from its salt. Water and amine are stripped off with nitrogen under vacuum and the product filtered. Examples 12 to 14 - Preparation of Product 2.00 g of EPSA, produced as described in Example 5, were dissolved in 40 ml dry Solvesso 150. Separately 4.84 g of a 60% by weight solution of the product of Example 11 in Solvesso 150 was further diluted with 20 ml of dry Solvesso 150, mixed with the EPSA solution and reacted for 2 hours at 75°C under a dry nitrogen atmosphere. The resulting products all showed an IR peak at 1610 cm -1 , indicating the presence of the amide/amine salt. The starting EPSA's had the following characteristics: % Propene . Moles SA per EPC 53 1.1 53 1.0 59 1.1 In a similar procedure 2.00 g of EPSA was treated with 2.42 g of the Example 11 product solution, and reacted at 120°C. The resulting product showed an IR peak at 1710 cm -1 , indicating i ide groups. Example 15 In this Example, the Programmed Cooling Test (PCT) Filterablity of Fuel Oil 80126/89 was measured using various additives at a treat rate of 200 ppm. In the PCT test, the fuel oil is cooled at 1°C per hour to -20°C, at which temperature the fuel is passed through a series of meshes of increasing fineness - through 60, 80, 100, 120, 150, 200, 250, 350, VW, LTFT, and 500 mesh, and the finest mesh passed is noted. The Cold Filter Plugging Points (CFPP) of the compositions described above were also measured using the test described in BS 2869, and in "Journal of the Institute of Petroleum", 52 (1966) 173 to 185, the disclosures of which are incorporated by reference herein. The results of the PCT and CFPP tests are shown in the Table below. The PCT test results are given in terms of the finest mesh passed while the CFPP test results are given in terms of the temperature at which the filter becomes blocked by wax. The results show the enhanced filterability of an oil product containing the additive according to the invention, compared with one containing a physical mixture of its starting materials or one containing oth additives; the CFPP is comparable with that containing the ethylenepropylene copolymer which fuel composition, however, has a poor filterability.

Claims: CLAIMS : 1. A copolymer of the formula AB, the moiety A being derivable from an ethylene-alpha olefin copolymer having a number average molecular weight of from 1000 to 10000, at least 30% of the polymer chains of which contain terminal ethenylidene unsaturation, the moiety B having a total molecular weight of at least 800 and being derivable from an oil-soluble organic material. 2. A copolymer as claimed in claim 1, wherein the link between moieties A and B is the product of one or more reactions between nucleophilic and electrophilic groups. 3. A copolymer as claimed in claim 2, wherein the electrophilic group is derived from an acid substituent on one moiety and the nucleophilic group is from an amine, alcohol, amino alcohol or metal compound on the other. 4. A copolymer as claimed in claim 3, wherein the acid substituent is on the A moiety. 5. A copolymer as claimed in any one of claims 1 to 4, wherein the A moiety is linked at the end of the chain having terminal unsaturation. 6. A copolymer as claimed in any one of claims 1 to 5, wherein, moiety A is an ethylene propylene copolymer. 7. A copolymer as claimed in any one of claims 1 to 6, wherein the molar ethylene content of moiety A is in the range of between 20 and 80 percent. 8. A copolymer as claimed in claim 7, wherein the ethylene content is between 30 and 70 percent. 9. A copolymer as claimed in any one of claims 1 to 8, wherein polymer moiety A is a polymer possessing a number average molecular weight (Mn) of from 1000 to 5000. 10. A copolymer as claimed in claim 9, wherein the moiety A has an Mn of from 1500 to 3000. 11. A copolymer as claimed in any one of claims 1 to 10, wherein moiety A is derived from a copolymer obtained by polymerization in the presence of a catalyst system comprising at least one metallocene and an alumoxane compound. 12. A copolymer as claimed in any one of claims l to 11, wherein moiety B is a polymer having a number average molecular weight of at least 800. 13. A copolymer as claimed in claim 12, wherein moiety B has an Mn in the range of from 900 to 5000. 14. A copolymer,as claimed in any one of claims 1 to 13, wherein the molecular weight of one of moieties A and B is within the range of 75% to 125% of the other. 15. A copolymer as claimed in any one of claims 1 to 14, wherein more than one chain forms the B moiety. 16. A copolymer as claimed in any one of claims 1 to 15, wherein moiety B is derived from polyisobutylene. 17. A copolymer as claimed in claim 16, which is derived from an ethylene-propylene polymer succinic acid or anhydride and a polyisobutylene amine. 18. A fuel oil composition comprising a copolymer AB as defined in any one of claims 1 to 17. 19. A composition as claimed in claim 18, wherein the copolymer AB is present in a proportion of from 0.005 to 0.5% by weight, based on the weight of the fuel oil. 20. A fuel oil additive concentrate comprising 2 to 90% by weight of a copolymer AB, as defined in any one of claims 1 to 17, in fuel oil or in a solvent miscible with fuel oil. 21. The use of a copolymer AB, as defined in any one of claims 1 to 17, as a wax crystal modifier in a fuel oil. 22. The invention as claimed in any one of claims 18 to 21, wherein the copolymer AB is present in association with one or more other low temperature flow improvers. 23. The invention as claimed in claim 22, wherein the improver is one or more of: the amide/amine salt reaction product of a carboxylic acid or anhydride and a hydrocarbyl substituted amine: a "comb" polymer, or an ethylene-vinyl ester copolymer.

Inventors: IBRAHIM TUNCEL, MCALEER ANDREW MATTHEW, TACK ROBERT DRYDEN, IBRAHIM, TUNCEL, MCALEER, ANDREW, MATTHEW, TACK, ROBERT, DRYDEN
Applicants: EXXON CHEMICAL LTD, EXXON CHEMICAL PATENTS INC, EXXON CHEMICAL LIMITED, EXXON CHEMICAL PATENTS, INC.
Application year: 1991
Main classification: C10L1
IPC codes: C08F8, C08G81, C10L1, C10L10