Iterative self-aligned contact metallization process

Abstract: A method is provided for forming multiple layers of interconnections adjacent a planar surface. A first insulator layer is formed adjacent the selected planar surface. A first conductor layer is formed adjacent the first insulator layer. A second insulator is formed adjacent the first conductor layer. A first cavity and a second cavity are formed, each having sidewalls extending through said second insulator layer and said first conductor layer. The first cavity is formed wider than the second cavity. A third insulator layer is conformally deposited adjacent the second insulator layer, such that sidewall insulators are deposited on sidewalls of the first cavity and such that the second cavity is substantially filled with insulator. An etch is performed through the first cavity to expose a portion of the planar surface. A second conductor layer is conformally deposited adjacent third insulator layer such that second conductor layer extends through the first cavity to contact the planar surface.

Description: TECHNICAL FIELD OF THE INVENTION The present invention relates generally to integrated circuit fabrication and more particularly to a method of forming multiple layers of interconnections adjacent a planar surface as defined in the precharacterizing part of claim 1. A method of this type is disclosed in "Patent Abstracts of Japan", vol. 14, no. 421 (E-976), 11th September 1990; JP-A-2 161 755. BACKGROUND OF THE INVENTION The capability to fabricate and interconnect large numbers of functional devices such as transistors, diodes, capacitors and resistors on a semiconductor substrate has lead to the availability of numerous diverse and often complicated integrated circuits. As the complexity of the circuits being fabricated increases, larger number of functional devices are being required on the substrate. Thus, the dimensions of the functional devices are being reduced, which makes the factors of interconnection of the devices and the planarization of the fabrication surfaces critical. In EP-A-0 010 596 a method for forming cavities with reduced dimensions used in the manufacture of semiconductor devices is disclosed. In one embodiment this method is used to provide dielectric regions which serve to isolate monocrystal regions in a silicon body consisting of a p-type substrate, an n + -type layer and an n--type layer. Cavities of at least two different widths are etched and the structure is subsequently covered with an insulating layer thereby filling the smaller cavities and covering walls and bottom of the wider cavities. After etching of the bottom layer, an electrical connection is provided by depositing a conducting layer and thereby filling the wider cavity. From "Patent Abstracts of Japan", vol. 13, no. 338 (E-795), 28 July 1989; JP-A-1 099 254 a semiconductor device with a groove digging type isolating layer, in which the substrate potential can be taken from the surface of the device, is known. A multilayer structure consisting of a p-type substrate, an n + -type layer, an n--type layer and a silicon oxide film contains a narrow and a wide groove. After depositing an oxide film and subsequently etching to a certain degree, the resulting structure comprises a completely filled narrow groove and a wide groove with remaining sidewalls of oxide film. Then a p-type aluminium electrode exposed in the bottom of the wide groove is formed. In the current technology, much of the interconnection of functional devices in an integrated circuit is done concurrently with their fabrication. In many cases, interconnection conductors may serve a dual role as a common node for two or more functional devices and as a convenient means for completing a complex maze of interconnections required for circuit functionality. For example, the diffusions necessary for the source and drain regions of transistors may be used as electrical conductors to interconnect nodes within a circuit. Similarly, the polysilicon lines commonly used to form gates for the same transistors may also provide suitable conductors for the creation of interconnections. Although convenient, these techniques have a significant drawback in that interconnection paths may infringe on silicon substrate area that is more suitably used for the creation of functional devices such as transistors and diodes. This problem is especially acute when large numbers of functional devices are required to form a desired circuit, and the available substrate area is at a premium. Modern integrated circuit technology has advanced to the point where the dimensions of structures in the plane of the silicon are comparable to the thickness of the materials used in their fabrication. The topology thereby created introduces problems during subsequent stages of fabrication, such as contact formation and interconnection by metallization layers. Field oxidation techniques used for providing isolation in polysilicon gate technology and the polysilicon gate itself, do not lend themselves to planar surfaces over which multiple layers of interconnection can be created. Specialized techniques have therefore been devised to form the required planarized surfaces. Planarization of the surfaces is an important factor which must be considered during the fabrication of circuits using a large number of very small functional devices. The interconnection of device nodes in an integrated circuit is similar to the interconnection of nodes on a printed circuit board. In the printed circuit board technology, multiple layers of interconnect are obtained by keeping the surface of the board planar during fabrication. A major difference for similar multi-level interconnections in an integrated circuit technology is the presence of the transistor and diode nodes in the starting substrate. Fabrication of the transistors and diodes usually is more commonly dictated by the steps to create them without heavily weighing the subsequent need for planarity during the interconnection stage of integrated circuit fabrication. Thus, a need has arisen for a means for the multiple layer interconnection of various isolated functional devices in an integrated circuit. SUMMARY OF THE INVENTION According to the invention, a method is provided for forming multiple layers of interconnections in an integrated circuit, comprising the steps of claim 1. The present invention provides a means for the multiple layer connection interconnection of various isolated functional devices in an integrated circuit. This technique allows for substrate, normally used for the formation of device to device interconnection, to be used for the formation of additional functional devices. The present technique allows for the concurrent creation of the planarized surfaces which are necessary for the successful formation of multiple layers of interconnections. This eliminates the need for several steps of planarizing which might be required in order to form multiple layers of interconnecting conductors. BRIEF DESCRIPTION OF THE DRAWINGS Other aspects of the invention and their advantages will be discerned when one refers to the following detailed description as taken in conjunction with the drawings, in which like numbers identify like parts, and in which: FIGURES 1a-1h are a series of sectional elevational views depicting the process of formation of a pair of isolated functional devices and an associated first level of metallization; FIGURES 2a-2h are a series of elevational sectional views depicting the formation of multiple layers of interconnections using the iterative self-aligned contact metallization process according to the invention. FIGURE 2b substantially corresponds to a section taken along line 202 of FIGURE 3; and FIGURE 3 is a plan view showing a pattern of contact spaces and slots formed during the iterative self-aligned contact metallization process according to the invention. DETAILED DESCRIPTION OF THE INVENTION For a more complete understanding of the present invention, reference is now made to FIGURES 1 and 2 of the drawings, like numerals being used for like and corresponding parts of the various drawings. FIGURES 1a-1g depict a series of steps in which a self-aligned contact iteration process according to the invention is used to provide a multilevel interconnect during the fabrication of a pair of transistors at the face of a layer of a semiconductor. Although, the present invention is depicted for the case of transistors, it can be used with any integrated circuit fabrication process in which isolated active devices are formed on a semiconductor substrate and require multiple layers of interconnect in order to provide a functioning circuit. Further, only a small section of the wafer comprising two transistors is shown; in practice, a large number of devices will be fabricated. FIGURE 1a shows a workpiece generally at 10, which includes a tank 12 of semiconductor. Gate oxide layer 14 has been formed by conventional method across surface 16 of tank 12. A layer 18 of polycrystalline silicon (poly) has next been formed across gate oxide layer 14. Turning next to FIGURE 1b, poly layer 18 has been patterned and etched to define moats 20 which completely enclose a region of silicon that will include the gate, source and drain of a future transistor. Channel stops 22 are formed at this point to isolate adjacent devices. In FIGURE 1c, a layer 24 of interlevel insulator, typically an oxide or oxide/nitride/oxide layer, has been conformally deposited across the face of the semiconductor. In general, the conformal deposition has formed a layer 24 which is quite planar. Some minor discontinuities are shown at 26 where the conformally deposited oxide has come together as it was deposited along the vertical edges of moats 20. In FIGURE 1d, inter-level oxide 26 and poly layer 18 have been patterned and etched to define gates 28a and 28b. This etch is followed by conventional processing to complete the drain regions 34 and the source regions 36. The drain and source processing require lithography over topography, but do not require a precise pattern definition. Turn next to FIGURE 1e, a conformal layer of insulator 38 is then deposited. This insulator deposition will fill small dimension openings to the silicon substrate as illustrated over the drain regions 34 while forming a sidewall insulators 40 in large dimension openings to the silicon substrate as illustrated over the source regions 36. In FIGURE 1f, the processing continues with an anisotropic etch of the conformal insulator layer 38. This etch removes the material in a nearly vertical fashion leaving contact holes 42 having sharply defined nearly vertical sidewalls. During this process, the overall insulator 38 has been substantially reduced in thickness. The sidewall insulators 40 along the sidewalls of contact holes 42 will prevent shorting between the gates 28 and subsequently deposited metal to fill contact holes 42. Gates 28 are thus isolated from the subsequent metallization. This stage of the processing illustrates a primary feature of the self-aligned contact process as has been practiced previously. Namely, the self-aligned contact process prepares contacts to a buried conductor, source regions 36 and drain regions 34 in this example case, with complete isolation from an intervening conductor, gates 28 in this case. Assigning a sequential conductor layer numbered to successive layers of conductors, the self-align contact process provides contacts between layers of equal parity. Since the gate 28 and source regions 36 or drain regions 34 have unequal parity, the self-aligned contact process of the present invention cannot create interconnections between them. All integrated circuits, however, will require connections between the gate and the source or drain layers. To break this parity rule, a special contact 44 to a selected gate 28, in this case gate 28a, is next patterned and etched through insulating layer 24 to expose a contact to gate 28a. This interconnection is critical to the remaining process steps of multilevel interconnect using the self-aligned iterative contact formation process of the present invention. The self-aligned iterative contact formation process of the present invention will only provide interconnection between layers of equal parity, therefore, this process is necessary to provide initial interconnections between levels of unequal parity, in this case between a gate 28 and a source region 36, or a drain region 34. Using the process of the present invention, to connect a pair of layers of unequal parity, it is necessary to form interconnections between layers of interconnect down to the parity breaker and then to form interconnections back up through the layers of the opposite parity until the proper connection is made. In FIGURE 1g, a first layer 50 is conformally deposited. The metal is now prepared for the first iteration of the self-aligned contact metallization process. It is important to note that no contact has been made to gate 28b; this contact will be made to a second metallization layer which will be formed as part of the self-aligned process that simultaneously patterns metal layer 50. In general, the conformal deposition is as planar as it was for the insulators. Some minor continuities are shown at 51, wherein conformally deposited metal has come together as was deposited along the vertical edges of the self-aligned contact formed by insulator 40. These features are relatively minor compared with the topography prior to the conformal deposition, and the resulting metal surface shown in FIGURE 1g is therefore quite planar. FIGURES 2a-2h are elevational sectional depictions of a series of process steps in which multiple layers of interconnecting conductor layers are formed by a self-aligned iterative contact formation process according to the invention. FIGURE 3 depicts a top view of a complex pattern of slots and contact holes which are created for use during the process according to the invention, a pair of which are discussed in relation to FIGURES 2a-2h. Like designator numbers in FIGURES 1 and 2a-2d and 3 designate like parts, the dimensions in FIGURES 2a-2d and 3 being expanded for additional clarity. In FIGURE 2a, an insulator layer 52 has been conformally deposited across metal layer 50. Next, as depicted in FIGURES 2b and 3, conductor layer 50 is patterned by the formation of a plurality of contact spaces 56 by slots 54 by anisotropically etching through insulator layer 52 and conductor layer 50. The slot 54 and contact space 56 shown in FIGURE 2b are a single pair substantially corresponding to a section taken along line 2-2 of FIGURE 3. Preferably, as shown in FIGURE 3, slots 54 and control contact spaces 56 are continuously formed as a pattern which defines desired conductor paths. The anisotropic etch renders the sidewalls of slots and spaces 54 and 56 sharply defined. Contact spaces 56 are formed substantially wider than slots 54 such that during future process steps discussed below, slots 54 will be substantially filled with insulator while contact spaces 56 remain only partially filled. In FIGURE 2c, an insulator layer 58 has been deposited which substantially fills slots 54 and forms sidewall insulators 60 on the sidewalls of contact spaces 56. During deposition of insulator layer 58, it is critical to maintain a high degree of conformality such that when slots 54 are filled, minimum topological remnants 71 are formed on the upper surface of insulator layer 58. Sidewall insulators 60 will prevent the ends of the now patterned metal layer 50 from shorting to metal later deposited into contact spaces 56. The face of the workpiece 10 has now been substantially covered with a thicker insulator layer 52/58, being formed of the successive deposition of insulator layers 52 and 58. As shown in FIGURE 2d, an anisotropic etch is then performed between sidewall insulators 60 to extend contact spaces 56 through insulator layer 38 to expose the underlying gate 28b. During this process, insulator layer 52/58 is substantially reduced in thickness. Following the etch through contact spaces 56, conformal deposition of metal is then performed to create a metal layer 62 which contacts conductor layer 28 through contact space 56. Following this step, the substantial advantages of the present invention are realized: metal layer 50 has been patterned while simultaneously an additional interconnection level 62 has been formed which contacts the next lowest level of equal parity, in this case, a selected gate 28b. The use of conformal deposition of insulator and metal has allowed for successive formation of planarized layers which minimize problems resulting from topological discontinuities. In FIGURES 2 and 3, only a small portion of an integrated circuit workpiece is depicted. During an actual fabrication process, conductor layer 50 may be patterned by etching of a number of cavities, similar to those depicted at 54 and 56 in FIGURE 3 to create a complex, high density interconnection of a large number of functional devices. Further, the present process may be repeated to form additional layers of patterned inter-connect. The next step of processing would pattern metal layer 62 while simultaneously forming contacts to metal layer 50. This interaction is depicted in FIGURES 2e-h. In FIGURE 2e, an insulator layer 64 has been conformally deposited across metal layer 62. Next, conductor layer 62 is patterned by the formation of contact spaces 66 and slots 68 by anisotropically etching through insulator layer 64 and conductor layer 62; control spaces 66 and slots 68 are depicted in FIGURE 2f. The anisotropic edge renders the sidewalls of contact spaces 66 and slots 68 sharply defined. Contact spaces 66 are formed substantially wider than slots 68 such that during future process steps discussed below, slots 68 will be substantially filled with insulator, while contact spaces 66 remain only partially filled. In FIGURE 2g, an insulator layer 70 has been deposited which substantially fills slots 68 and forms sidewall insulators 72 on the sidewalls of contact spaces 66. During the deposition of insulator layer 70, it is critical to maintain a high degree of conformality, such that when slots 68 are filled, minimum topological remnants 71 are formed on the upper surface of insulator layer 70. Sidewall insulators 72 will prevent the ends of the now patterned metal layer 62 from shorting to metal later deposited into contact spaces 66. The face of the workpiece 10 has now been substantially covered with a thicker insulator layer 64/70, being formed of the successive deposition of insulator layers 64 and 70. As shown in FIGURE 2h, an anisotropic etch is then performed between sidewall insulators 72 to extend contact spaces 66 through insulator layer 52/58 to expose the underlying portions of patterned conductor layer 50. During this process, insulator layer 64/70 is substantially reduced in thickness. Following the etch through contact spaces 66, conformal deposition of metal is then performed to create a metal layer 74 which contacts conductor layer 50 through contact spaces 66. Following this step, the substantial advantages of the present invention have again been realized: metal layer 62 has been patterned while simultaneously an additional interconnection level 74 has been formed which contacts the next lowest level of equal parity, conductor layer 50. The topology shown in FIGURE 2h is similar to layer structure with the topologies depicted in FIGURES 2a and 2d, demonstrating the iterative nature of the present invention. Essentially, only the spacing and location of the cavities has varied significantly. Again, the use of conformal deposition of insulator and metal has created the planarized layers which have allowed the successive formation of interconnections with minimum problems as a result of topological discontinuities. While preferred embodiments of the invention and their advantages have been set forth in the above detailed description, the invention is not limited thereto, but only by the scope and spirit of the appended claims.

Claims: A method of forming multiple layers of interconnections in an integrated circuit, comprising the steps of: forming a first conductor layer (28, 50); forming a first insulator layer (24, 52) on said first conductor layer (28, 50); forming a second conductor layer (50, 62) on said first insulator layer (24, 52); forming a second insulator layer (52, 64) on said second conductor layer (50, 62); forming first (56, 66) and second (54, 68) cavities each having a first depth and having sidewalls extending through said second insulator layer (52, 64) and said second conductor layer (50, 62), said first cavity (56, 66) being wider than said second cavity (54, 68); conformally depositing a third insulator layer (58, 70) on said second insulator layer (52, 64) such that sidewall insulators (60, 72) are deposited on said sidewalls of said first cavity (56, 66) and such that said second cavity (54, 68) is substantially filled with said insulator; anisotropically etching through said first cavity (56, 66) to a second depth to expose a portion of said first conductor layer (28, 50) while retaining the sidewall insulators (60, 72); and conformally depositing a third conductor layer (62, 74) on said third insulator layer (58, 70) such that said third conductor layer (62, 74) extends through said first cavity (56, 66) to contact said first conductor layer (28, 50). The method of Claim 1, and further forming additional layers of interconnections by repeating said steps of forming cavities, conformally depositing insulator, etching and conformally depositing conductor. The method of Claim 1 or 2, wherein said insulator layers comprise conformally deposited oxide layers. The method of Claim 1, 2 or 3, wherein said conductor layers comprise conformally deposited metal layers. The method of any preceding Claim, wherein said conductor layers are metallization layers. The method of any of Claims 1 to 5, wherein said first conductor layer is a polysilicon gate layer.

Inventors: COLEMAN DONALD J JR, COLEMAN, DONALD J., JR.
Applicants: TEXAS INSTRUMENTS INC, TEXAS INSTRUMENTS INCORPORATED
Application year: 1991
Main classification: H01L21
IPC codes: H01L29, H01L21