PROCESS USING SORBENTS FOR THE REMOVAL OF SOx FROM FLUE GAS AND OTHER GAS STREAMS

Abstract: A process of removing noxious sulfur oxides from gas streams using heated layered double hydroxide (LDH) sorbents is described. The sorbent compositions contain metal components incorporated into the galleries of the LDH structures in the form of metal-containing oxo-anions, to promote the oxidation of sulfur dioxide.

Description: PROCESS USING SORBENTS FOR THE REMOVAL OF SO x FROM FLUE GAS AND OTHER GAS STREAMS Cross-Reference to Related Application This application is a continuation-in-part of Serial No, 07/466,984, filed January 18, 1990.. BACKGROUND OF THE INVENTION (1) Field of the Invention The present invention relates to a process for using sorbents for the removal of sulfur dioxide and sulfur trioxide from gas mixtures. In particular, the present invention relates to the use of crystalline layered double hydroxide with an interlayer of an ion which oxidizes sulfur dioxide to sulfur trioxide. (2) Prior Art In fossil-f el-fired power plants, the sulfur content of the feed coal is oxidized during combustion to sulfur oxides (SO2 and SO3, commonly referred to as "SO x " ) , which are released through stacks to the atmosphere, and . are responsible for deposition as "acid rain". Analyses of flue gas produced by power plants burning coal before desulfurization, show 0.5% - 0.2% SO2 and about 0.005% SO3. Control of SO x emission is mandated by the U.S. Environmental Protection Agency (EPA), and various studies are under way to develop methods for its removal from flue gas streams . Formation of SO x in combustion processes can be reduced by modifying the burner design and combustion system, by changing the operating conditions and by using fuels with lower sulfur contents. The most popular and inexpensive method of reducing SO x emission is the addition of reactive dry sorbents with the fuel " . Accordingly at present, SO x removal is most often accomplished by using lime (CaO) or lime stone (CaC03). Several other basic sorbents like MgO, ZnO also are found to be effective in removing S0 X . For a review on dry sorbents see for example, Ko ppa, V., "Dry Adsorption Processes for Removal of S0 X and N0 X in Flue Gases - a review," Paperii ja Puu, 5 . , 401 to 405 (1986) . Use of Group 2 (formerly Group IIA) metal oxides such as magnesium and calcium oxides as S0 X sorbents has been disclosed in several patent disclosures and recent examples include U.S. Patent Nos. 3,835,031 and 3,699,037. Several other metal oxides of varying effectiveness as SO x sorbents are described in U.S. Patent No. 4,153,534 which include oxides such as sodium, scandium, titanium, iron, chromium, molybdenum, manganese, cobalt, nickel, copper, zinc, cadmium, rare earth metals, and lead. In typical coal-fired power plants the ground sorbent, for example lime or limestone, is added into boilers along with coal or sprayed into towers as a slurry to contact the flue gas. The SO2 reacts with calcium hydroxide to form a calcium sulfite slurry which is then partially oxidized with air to calcium sulfate. In this way the sulfur oxides are retained as harmless solid compounds which can be removed from the stack gas by electrostatic precipitation or other standard methods. Such a process is potentially attractive for retrofitting existing power plants since no major structural alteration are required. A major problem with this type of process is lo utilization of the oxide sorbents. The rate of adsorption of S0 X declines rapidly with increasing conversion, due to mass transfer limitation and low reactivity of SO2- Hence in the relatively short contact time available, only a small fraction of the sorbent reacts. In principle the problem of low utilization of the sorbents may be solved b reducing the particle size, but in practice, the particle size required for a reasonable level of utilization may be too small to achieve economically by conventional grinding or fragmentation methods. Thermodynamic calculations indicate that the capture of sulfur trioxide with metal oxides is more favorable compared to sulfur dioxide. Several experimental results have suggested that catalytic oxidation of sulfur dioxide to sulfur trioxide can be beneficial for stack gas desulfurization . Kocaefe & Karman in Cand. J. Chem. Eng . , 63, 971 to 977 (1985) has shown that the rate of reaction of SO3 with Ca, Mg and ZnO is greater than that of sulfur dioxide with the same oxides under identical conditions. Furthermore, inclusion of Fe2θ3 (as a SO2 oxidation catalyst) leads to more effective utilization of the lime. The addition of a small amount of Fe2θ3 gave both a more rapid initial uptake rate and a much higher final conversion of the lime (80-90%). In the absence of an oxidation catalyst the rate of SO2 absorption declined sharply at about 70% conversion. A similar approach has been employed in designing S0 X sorbents for fluid catalytic cracking (FCC) processing of petroleum. These sorbents, among other things, are mostly alkaline earth metal spinels containing one or more other metal components capable of oxidizing sulfur dioxide. For example, U.S. Patent Nos. 4,472,532 and 4,492,678 relate to the incorporation of iron, chromium, vanadium, manganese, gallium, boron, cobalt, platinum, and cerium as oxidation catalysts. Therefore, in designing improved sorbents for S0 X removal, one must synthesize materials that will (i) oxidize SO2 to SO3 , (ii) chemisorb the SO3 formed, and (iii) be able to release the adsorbed SO x for the regeneration of the sorbents or form stable materials for the safe deposition of the spent solid sorbents. The SO x emitted from these spent sorbents can be captured safely and can be utilized in sulfuric acid or sulfur production. European Patent Application EP-A 278 535 has recently described a catalyst composition suitable for the refining of heavy sulfur- and metal-containing petroleum feeds. Thus, the catalyst composition according to the disclosure contained a catalytically active zeolitic material such as ZSM-5, ZSM-11 etc. for the conversion of hydrocarbons, an anionic clay material with an LDH structure for the binding and removal of sulfur oxides, and a matrix material such as kaolin or alumina. Preferred catalyst compositions contained 1 to 30 percent amounts of anionic clay compositions, based on total catalyst composition. There is a need for sorbent compositions suitable for diminishing SO x from flue gas streams particularly from coal-fired power plants. There is a need to develop sorbent compositions which give better SO x uptake in shorter time duration to overcome the low utilization of common oxide sorbents such as CaO and MgO due to mass transfer limitation and low reactivity of SO2- LDHs are a group of anionic clay minerals. These have positively charged sheets of metal hydroxides, between which are located anions and some water molecules. Most common LDHs are based on double hydroxides of such main group metals as Mg, and Al and transition metals such as Ni, Co, Cr, Zn and Fe etc. These clays have a structur similar to brucite [Mg(OH)2- in which the magnesium ions are octahedrally surrounded by hydroxyl groups with the resulting octahedra sharing edges to form infinite sheets. In the LDHs, some of the magnesium is isomorphously replaced by a trivalent ion, such as Al^÷. The Mg2+, Al^ + OH" layers are then positively charged, necessitating charge balancing by insertion of anions between the layers One such anionic clay is hydrotalcite in which the carbonate ion is the interstitial anion, and has the idealized unit cell formula [Mgg l2(OH) 6l (CO3) -4H20. However, the ratio of Mg/Al in hydrotalcite-like can vary between 1.7 and 4 and various other divalent and trivalent ions may be substituted for Mg and Al. In addition, the anion which is carbonate in hydrotalcite, can be varied i synthesis by a large number of simple anions such as NO3--, C1-, OH-, Sθ4^ ~ etc. These LDHs, based on their structur fall into the Pyroaurite-Sjogrenite group, where brucite-like layers carrying a net positive charge alternate with layers in which the oxygen atoms of carbonate groups and water molecules are distributed on a single set of sites. Hydrocalumite and related synthetic compounds also have a layered structure in which positively charged metal hydroxide layers alternate with the interlayers containing anions and water. The hydroxide layers contain specific combinations of metal ions derived from on one hand divalent calcium cations and on the other from trivalent cations of metals such as iron, or more particularly, aluminum. The interlayers contain anions such as OH-, Sθ4 2 ~, Cl ~ , NO3- and, in particular CO3 2- . The general formula for the group is [Ca2M3+(OH) g]X.yH2θ, where M 3+ is a tripositive ion and typically Al 3+ , X is a singly charged anion or equal amounts of more highly charged ones, and y is between 2 and 6. As in the Pyroaurite-Sjogrenite group, principal layers alternate with inter-layers, the principal layers having the composition [Ca2M-* + (OH) g]+ and the interlayers consisting of water molecules and anion X. However, because of the difference in size between the Ca 2+ and l3+ ions, the M 2+ :M-3 + r tio is fixed at 2:1 and their arrangement is ordered. The only known natural mineral in the group is hydrocalumite the composition of which is approximately [Ca2 l(OH)6l (OH)o.75 Cθ3)o.i25- 2 « H2θ, but there are many synthetic analogues such as [Ca2Fe(OH)g1 (SO4)o.5.3H20, [Ca2Al(OH)g] (OH) .6H2O etc. The syntheses of LDHs are generally simple, and the so-called "precipitation method" is most popular. If a carbonate-containing product is desired, then the aqueous solution of magnesium and aluminum salts, i.e., nitrate, or chloride, is added to an aqueous solution of sodium hydroxide-carbonate with good mixing at room temperature. The resulting amorphous precipitate is then heated for several hours at 60 to 200°C to obtain a crystalline material. Washing and drying complete the synthesis in quantitative yield. By employing this " precipitation method, replacement of all or part of Mg 2+ with other M-^ions such as Ca 2+ , Zn 2+ , Cu 2+ etc., or replacement of l3+ with other M 111 ions such as Fe^ + , Cr^ + etc., is also possible. Another important aspect of the synthesis of these materials is the variation of the nature of the interstitial anion. The preparation of hydrotalcite-like materials with anions other than carbonate in pure form requires special procedures, because LDH incorporates carbonate in preference to other anions. Most of the time the smaller anions are introduced to the LDH structure, vi the precipitation method by using the desired anion solutions instead of carbonate. However, in these methods the synthesis has to be carried out in an anaerobic condition to prevent carbonate contamination from the atmospheric carbon dioxide. These methods of preparation of LDHs have been described in prior art publications, particular reference being made to the following review journal articles by S. L. Suib et al., in Solid State Ionics, 26, 77 to 86 (1988), and W. T. Reichle in CHEMTECH 58 to 63 (1986) . Process for the synthesis of hydrotalcite-like clays also have been the subject of a number of patents. Miyata et al in U.S. Patent Nos. 3,796,792, 3,879,523 and 3,879,525 describe hydrotalcite-like derivatives with bot cationic layer and anionic substitution including the smaller transition metal anions like Crθ4 ~, M0O4 2- and - M02O7 2- . Both composition and preparative methods are described, and the compositions are said to be useful for catalytic purposes, absorbents, desiccants and the like. Synthetic hydrotalcite-like derivatives with small anions including anions of transition elements, and also large organic anions such as long chain aliphatic dicarboxylate are shown to catalyze aldol condensation effectively. Incorporation of larger anions, such as transition metal polyoxoanions into the LDH gallery is not easy. This requires ion-exchange techniques subsequent to the LDH synthesis. Pinnavaia and Kwon in J. Am. Chem. Soc, 110, 3653 (1988) have demonstrated the pillaring of several polyoxometalles including VIQ028^~ into the hyrotalcite structure containing Zn and Al metal ions in the layers. In U.S. Patent No. 4,452,244 by Woltermann disclosed the preparation of several polyoxometallate-LDHs . However, no XRD or analytical data were given to establish the purity of those materials. Recently, U.S. Patent No. 4,774,212 by Drezdon disclosed the preparation of several Mg/Al hydrotalcite-like materials containing transition metal polyoxoanions. The nature of the thermal decomposition of LDHs especially the hydrotalcite-like materials, have been studied in detail. For example, upon thermolysis, hydrotalcite [Mg Al2(OH)ιg](CO3) .4H20 loses weight in two stages. First, it loses the four interstitial water molecules when heated to 200°C, while retaining the skeletal hydroxide and the interlayer carbonate. Additional heating from 275°C to 450°C results in the simultaneous loss of hydroxyl groups and carbonate as water and carbon dioxide, respectively. These magnesium aluminum solid solutions have the sodium chloride type structure with cations deficiencies. Reichle in J. Catal. 101, 352 to 359 (1986) has shown that this heating of hydrotalcite was accompanied by an increase in the surface area from about 120 to about 230 m 2 /g (N2/BET) and a doubling of pore volume (0.6 to 1.0 cm^/g, Hg intrusion). Further heating of these solid solutions to higher temperatures causes lowering of surface area as well as reactivity. At 1000°C, the formation of MgO and the spinel phase, MgAl2θ4 has been observed. OBJECTS It is therefore an object of the present invention to provide novel sorbent compositions which oxidize SO2 to SO3, remove the SO3 and then are regeneratable for reuse. These and other objectives will be increasingly apparent by reference to the following description and the drawings. IN THE DRAWINGS Figure 1 is a graph of a thermogravimetric analysis (TGA) plot for SO2 uptake by [Mgg l2(OH)i6] (Feθ4) . H2O as the layered double hydroxide (LDH). Figure 2 is a graph showing the temperature dependence for SO2 uptake by [MggAl2(OH) g] Figure 3 is a graph of a TGA plot for SO2 uptak by [Zn2Al(OH) ] (SiV3W9θ40>ι 7. H2θ and thermolysis of the spent sorbent. Figure 4 is a graph comparing the rate of SO2 uptake by different Mg containing sorbents prepared according to this invention and sorbents presently used in flue gas desulfurization. GENERAL DESCRIPTION The present invention relates to a process for removing the SO x components from flue gas and other gas streams which comprises contacting the said gas stream wit a heated sorbent composition wherein the said sorbent is selected from the group consisting of a crystalline layere double hydroxide structure of the formula: [Mι_ χ Il χ I I I(OH) 2 [(A n -) x / n .yH2θ wherein M 11 is a divalent metal cation and M 111 is a trivalent metal cation selected from the group consisting of metal cations which form metal oxides and which are capable of reacting with SO2 to form metal sulfites and S to form metal sulfates, A is an interlayer anion of charg n- which comprises at least one metal atom which provides oxidation of sulfur dioxide to sulfur trioxide in an amou sufficient that said layered double hydroxide structure promotes the oxidation of the sulfur dioxide to the sulfur trioxide at sulfur dioxide oxidation conditions, x is between 0.8 to 0.12 and a heat treated derivative of the double hydroxide. Thermal decomposition of LDHs, leads to the formation of active metal oxides with fairly high basic character (pKa £35) and high surface area. These thermally treated materials should have exceptionally well-dispersed reactive metal centers, as judged from thei catalytic properties . These properties have lead us to synthesize and to utilize thermally treated LDH materials as suitable sorbents for flue gas desulfurization. The SO oxidation catalysts, (usually transition metals) and the SO3 sorbents (usually a metal oxide from either group IA o IIA) can be easily incorporated into the layers or in the galleries of LDH materials, using inexpensive starting materials. Thus the present invention relates to uses of layered double hydroxide compositions, more specifically hydrotalcite-like and hydrocalumite-like materials for the absorption of SO x from flue gas streams. Also described herein is the incorporation of other metal components, preferably transition metal ions, capable of promoting the oxidation of sulfur dioxide to sulfur trioxide at calcination temperatures. These second metal components are incorporated in the form of metal polyoxoanions into the LDH by intercalation. LDH sorbents react at different temperatures, particularly at 500 to 1000°C, with SO2 such that the sorbents find particular use in diminishing the emissions of sulfur oxides from the coal-fired boilers. - - Considered here are also ways of recycling the spent sorbents, (i) by removing the entrapped SO x at high temperatures and/or (ii) by disposing of them as solid waste. Thus the present invention uses layered double —iiydroxide compositions, more specifically hydrotalcite-like and hydrocalumite-like materials of the formula, [Mι-x II M x III (OH)2] (A x / n ) n ~.yH2θ wherein M 11 is a divalent metal and M^ 11 - is a trivalent metal, A is an anion of charge n-, and x is between 0.8 to 0.12, which are suitable for the absorption of SO x . Both M 11 and/or M 111 comprise in total or in part metals (preferably from group IIA, IIB and IIIA) that form reactive basic oxides at calcination temperatures (preferably above 500°C) that are capable of reacting with SO . Accordingly, the preferred LDHs for use in the present invention comprise of these metals in the brucite-like [Mg(OH)2~like] layers, in particular magnesium and aluminum. Other alkaline earth metal ions, such as calcium, strontium, barium and mixtures thereof may replace all or part of magnesium ions. In a broader sense this invention considers the use of these LDH sorbents in controlling the sulfur oxides from gas streams, more particularly from coal-fired boiler systems. These systems include a boiler, economizer and dust collectors such as electrostatic precipitator or bag filter house ("bag house"). The injection of the sorbents into these, particularly to the boiler (700-1000°C) , along with the coal, or onto the electrostatic precipitators (ho 5 side temp. 400-500°C has been considered in this invention Thus, the LDH sorbents were thermally treated in a temperature-programmed thermogravimetric balance at a temperature in the range of 500 to 1000°C in a stream of air or nitrogen, and SO x gas was introduced. The amount o 0 SO2 that reacted with the sorbents was monitored as the weight uptake. The reaction of the hydrotalcite sorbent, [MggAl2(OH)ιg](Cθ3)'xH2θ (abbreviated as Mg3Al-LDH) with SO2 provided a general description of the typical 5 experimental method used to investigate the LDH reactivit The hydrotalcite was heated to 700°C under a stream of . air in a temperature controlled thermogravimetric balance at a rate of 5°C/min. The sample was calcined at 700°C for further one hour. During the above calcination process the sample lost weight due to the removal of CO2 and H2O. This sample was then exposed to Sθ2-containing gas stream at 0.5% v/v concentration, at a flow rate of 200 ml/min. A weight gain of 6.2 % was observed. This corresponded to the amount of SO x absorbed to form the metal sulfate, MgSθ4 The diffraction peaks observed in the X-ray diffraction pattern of the final product were due to crystalline MgSθ4, indicating that the magnesium sites were the reactive species at this temperature. The weight uptake observed corresponded to a 4.4% conversion of MgO to MgSθ4» However, this value is low compared to the other modified sorbents described later in this invention. A third metal component is incorporated in the LDH to promote the oxidation of sulfur dioxide to sulfur trioxide. The third metal component is preferably a component of a metal selected from the transition metals, rare earth metals, and Group IVA in the periodic table. Some of the known transition metal and transition metal oxide catalysts that are suitable for SO2 oxidation include, Pt, WO3, Ag, Ag3V04, CU3(Vθ4)2. v 2°5' F e 2° 3 ' Tiθ 2 , CuO, Crθ3, Mnθ2 Pbθ2, M0O 3 , Ceθ2, Cr2θ3, Shθ2 and ZnO. Platinum is an excellent oxidation catalyst, and other oxides such as vanadium pentoxide and iron oxides are also especially effective for catalyzing the oxidation of SO2 to SO3. See for example, Neuwmann et al in Z. Electrochem. 38, 304 to 310 (1932). The catalytic process on these oxides will involve the following steps: sorption of SO2 to form a sulfite, oxidation of sulfite to sulfate, and sulfate decomposition with evolution of SO3. Thus, for a particular metal oxide sorbent, the selection of a good metal oxide catalyst for SO2 oxidation is very important. Requirements for a good catalyst can be compared to those for the SO2 sorbent. For the catalyst, all three steps are surface reactions and should occur at the reaction temperature. For the SO2 sorbent, the first two steps should occur as bulk reactions converting much of the sorbent to sulfate during sorption at the reaction temperature. The last step should occur at a higher temperature. Particularly good results were achieved as disclosed in this invention when transition metals, especiall -iron or vanadium, were introduced to the LDH as the third metal. These metals were incorporated into the LDH sorbent compositions by structural means during the synthesis. As disclosed in this invention, metal components are introduced into the galleries between [Mι_ x II M x III (OH)2] layers in such a way, that a part or whole of A n ~ in the LDH structure, [Mι_ x II M x III (OH)2] (A x n ) n "-H2θ is replaced by anions containing sulfur dioxide oxidizing metals described earlier. Accordingly, the anions that contain metal ions, such as copper, zinc, cobalt, iron, cadmium, mercury, lead manganese, tin, nickel, palladium, chromium, vanadium, manganese, gallium, boron, cobalt, and mixtures thereof ma replace all or part of gallery anion A n ~ in the LDH structure. Thus, the anions can be one or more from metal anionic complexes such as oxalates (ox), Fe(ox)33-, simple oxo-anions such as, Crθ4 2_ , Feθ4 2 ~, Mnθ4~, etc., or larger oxo-anions with higher charge such as, Mo 7°24 6 ~ e tc. or anions like BVW oθ4o 7 ~, H2W12O406-, polyoxometalates with Keggin-type structure o BCo nθ39 7 ~, SiWnθ39 8 ~, PMθ2 9θ3g 7 ~ polyoxometalates wit lacunary-type (defect) Keggin structure or anions such as BCoWi2θ42^~ containing fused Keggin-type structure. Intercalation of these anions with different sizes, not only help SO2 to oxidize to SO3, but also introduce microporosity in the LDH structure and allow ready access of reacting SO2 molecules. The incorporation of guest anions into the hydrotalcite structure was carried out by replacing Cθ3 2 ~ from the gallery as follows: The hydrotalcite material with suitable Mg/Al ratio was first calcined at 500°C and then hydrolyzed in aqueous solutions under anaerobic conditions to reform the hydrotalcite-like LDH containing OH~ as the gallery anion. This OH- in the gallery can easily be replaced by wide variety of anions, such as Feθ4 2_ , Crθ4 2 ~, Fe(ox)3 3- etc., or larger anions such as v 10°28^-' w 7θ2 > 4 or ucn larger anions with Keggin structure such as H2Wi2θ40^~, BVWιoθ4θ 7 ~r SiV3Wgθ40 7 ~ etc. or lacunary structure such as Si nθ39 9 ~, BCoWnθ39 7 ~, etc The products isolated showed X-ray diffraction peaks corresponding to crystalline phases with well-defined basa spacings (Table 1). TABLE 1 - Basal Spacings for the LDHs of the type [M II ι_ x M III x (OH)2](A n~ ) x / n -yH2θ The incorporation of the guest polyoxomatalate anions into the Zn/Al-LDH was also carried out in a simil manner starting with an aqueous hot suspension of [Zn2Al(OH)g] (NO3)* H2θ (referred to as Zn2Al-LDH) and was found to undergo complete intercalative ion exchange reaction with aqueous solutions of polyoxometalate anions including alpha-[H2W 2θ401 6~ and alpha-[SiV3W9θ40 ] 7- alpha-Keggin-type ions or lacunary (defect) Keggin-type ions such as Si nθ39 9- , BC0W11O39 7- . The anions with lower charge such as [PW 2O40 ] 3 ~ and show no ion exchange whereas, intermediate anions show partial intercalation (e.g. [PC W O39 (H2O) ] 5 ~) . Furthermore, polyoxometalate anions with beta-Keggin structure such as beta-[SiV3W9θ40 ] 7- undergo partial intercalation. See Kwon, T. and Pinnavaia, T. J. , "Pillaring of a Layered Double Hydroxide by Polyoxometalates with Keggin-Ion Structures", Chemistry of Materials, JL, 381 to 383 (1989). The preparation of several polyoxometalate intercalated Zn/Al- and Mg/Al-LDH materials starting from corresponding nitrate or chloride containing LDH has been disclosed by Woltermann in U.S. Patent No. 4,454,244. However, in our hands, under the conditions mentioned the products formed were X-ray amorphous as judged by the absence of distinct Bragg reflections. Nevertheless, these polyoxometalate intercalated amorphous materials as well as partially intercalated LDHs described earlier also showed enhanced SO x uptakes compared to their precursors. In certain preferred embodiments discussed in this invention, hydrotalcite-like Mg3Al-LDHs, when intercalated with Fe(ox)3 3- , Feθ4 2 ~, IQ028 6_ / W7θ24^~ and Mθ7θ24^~ gave better SO x sorption than normal hydrotalcite (Table 2) . TABLE 2 - SO2 Uptake by [MI_ X I IM X III (OH) 21 (A n ~) x / n -yH 2 0 at 700°C. Layer Metals Gallery Anion % Conversion 3 - M II Mm A n ~ Mg Al Mg/Al=3/1 Zn Al An/Al=2/1 a Fraction of Mg as MgO converted to MgS04 after 1 hour reaction time. In these cases, iron, vanadium, tungsten and molybdenum oxides act as SO2 oxidation catalysts. Similarly, Zn2Al-LDH when intercalated with the same polyoxo anions (Table 2) also showed enhanced S0 X uptake relative to the Zn2Al-Nθ3 LDH precursor. Furthermore, it was found that, Mg3Al and Zn2Al-LDH sorbents prepared with POM anions intercalated partially in the galleries, as well as amorphous LDH-POM reaction products, also produce suitable S0 X sorbents. All these materials showed enhanced SO x uptake relative to their precursor LDHs, [ Zn2Al(OH) ] (NO3) -xH2θ or [Mg3Al2(OH)i6] (OH) -xH2θ. For example the Vι 0 O 2 8 6 ~ intercalated crystalline Zn2Al-LDH showed a weight uptake of 23.6% at 700°C under the conditions described earlier in this invention. The corresponding amorphous material showed a 20% weight uptake at this temperature. The crystalline sorbent formed by intercalating Zn2Al-LDH with alpha-[SiV3 9θ4θ] 7 ~ showed 5.78% weight uptake at 700°C with SO x whereas, the partially intercalated sorbent with beta-[SiV3 9θ4o3 7 ~ in the gallery showed 5.12% weight uptake under similar conditions. In another embodiment, Mg3Al-LDH intercalated with ιoθ28 6- lMggAl2 ( OH ) g] ( V oθ28 ) l/3" xH 2° was subjected to air containing 0.5% SO2 (v/v) in the temperature range 500-800°C. As evident by the uptake measurements (Figure 2), better SO x sorption was seen in the temperature range 600-800°C. In one embodiment the possibility of regenerating these spent LDH sorbents for recycling was - considered. It was found that spent Zn2Al-LDH sorbents after exposing to SO2 at 700°C, release entrapped SO x (and/or H2SO4) upon further thermal treatment, as evident by their weight loss (Table 3). TABLE 3 - Thermal Decomposition of Spent [Zn Al(OH)g] (A n ~)ι/ n 'yH 2 0 Sorbents at 700°C Gallery Anion % Sulfate Decomposed in A n ~ Absence of S0 y a NO3" 0.00 10O28 6" 2 -° H2Wl2θ40 6 ~ 19.5 PMO2 9039 7" 14.7 C02W12O42 8" 8.6 BCo ιιθ39 7~ 17.4 P 9θ34 9 ~ 2.0 SiV3 θ40 7 ~ 66.0 Si nθ39 9 ~ 20.1 BV nθ40 7 ~ 42.3 a. expressed as, % weight loss in absence of SO ? 100 % weight uptake in presence of SO2 For example, a Zn/Al-LDH containing SiV3 9θ4o 7_ polyoxometalate anions showed a 5.78% weight uptake at 700°C in the presence of air containing 0.5% SO2 (v/v). I the absence of SO2 in a stream of air at 900°C, this spent sorbent (now in the sulfate form) released all of its boun SO x to regain the initial weight prior to SO2 treatment an to reform the oxide sorbent. This reformed sorbent had a similar activity as the initial sorbent for the reaction with SO x (Figure 3). Thus, the S0 X sorbent can be recycled, if desired by appropriate control of absorption/desorption temperatures. The uptake of S0 X as a function of time for so of the g3Al sorbents discussed in this invention is give in Figure 4. Compared to conventional basic sorbents suc as MgO and g(OH)2, the sorbents disclosed in this invention, especially when the gallery anions containing iron in the layered double hydroxide structure, exhibit superior initial and overall SO x sorptivity. Under specific reaction conditions, i.e., at 700°C in a gas stream containing 0.5% SO2 and. air, for example MgO was found to undergo 10.2% conversion of MgO sites to MgS04 and Mg(OH>2 was found to undergo 14.0% conversion during a period of 1 hour. Incorporation of iron as Fe2θ3 to MgO By (MgO:Fe2θ3=3:1) by mixing enhanced the conversion to 36.5%. Conversely, similar mixing experiment with Mg(OH)2 [Mg(OH>2:Fe(OH)3 = 3:1] showed reduced uptakes (9% conversion). Under the same set of reaction conditions Mg3Al-LDH (Mg:Al=3:l) containing Feθ4 2- ions and Fe(ox)3 3 ~ anions in the galleries as disclosed in this invention exhibited 85.2% and 67.8% conversion of Mg sites to MgSθ4, respectively. These values are much superior to MgO or Mg(OH)2 with or without iron. The LDH sorbents intercalated with vanadium containing anions such as Vιoθ28 6 ~, HV04 2 ~, SiV3 9θ4Q 7 ~ and BVWIQ04O 7 ~ also showed better SO x uptake values (Table 2 and Figure 4). Moreover, these polyoxometalate anions intercalated LDH sorbents exhibited better initial SO x uptake than MgO or Mg(OH)2« European patent EP-A 278 535, which was described herein earlier, disclosed hydrocarbon cracking catalyst compositions containing as a component, anionic clays with LDH structures, for the purpose of binding the SO x liberated in the refining process, especially when processing high sulfur feeds. The LDH components incorporated many of the known SO2 oxidation catalysts, including rare earth metal ions (e.g., La 3+ , Ce 3+ ), noble metals (e.g., Pt, Rh) and transition metal ions (Cu + , Fe3 + , Mn + , Cr^+) . The rare earth and noble metal catalysts were preferred over the transition metal catalysts, in part, because of their greater reactivity. Also, it is known to those skilled in the art that transition metals, particularly iron, are undesirable constituents of petroleum cracking catalysts because they promote the formation of coke. However, iron is an economically attractive SO2 oxidation catalyst for applications where coke formation is not a concern, such as in the reduction of SO x from the flue gases of coal-burning power plants. In the preferred invention described herein, we disclose in part that the effectiveness of transition metal ions (particularly iron and vanadium) in promoting SO2 uptake by LDH materials depends substantially on the transition metal composition. The incorporation of transition metals into the galleries of LDH structure affords an order of increase in S0 X absorption. This teaching is illustrated by the results presented in Table 2 for SO2 uptake at 700°C by Mg3 l and Zn2Al-LDH compositions with different gallery anions consisting of SO2 oxidation catalysts. In the present invention, when the oxidation catalyst iron when incorporated to the galleries of the LDH structure in the form of Feθ4 2 ~ for example, showed an enhancement of S0 X uptake capability of hydrotalcite from 12.5% conversion of Mg sites to MgS04 to 85.2%. This is about 72.7% improvement of utilizing the Mg sites for SO uptake. Furthermore, incorporation of other iron containing anions such as Fe(ox)3 3- as well as vanadium containing polyoxometalate anions showed significant improvements in S0 X uptake capabilities of the LDH sorbent Thus, iron and vanadium are preferred as SO2 oxidation catalyst for the sorbents disclosed in this invention whic are fabricated to use in flue gas desulfurization processes. Most of the sorbents disclosed in this inventio contained Mg + as the M 11 cation. Alternatively, Ca 2+ containing LDHs such as hydrocalumite and its derivatives also could be used as sorbents for SO x scrubbing after intercalating with said polyoxometalate. These materials should have similar or superior S0 X sorptivity as judged b reactivity of CaO with SO2 and SO3 (see above, background of the invention). The metal-containing LDH useful as precursor f the preparation of compositions disclosed in the present invention may be synthesized from inexpensive starting materials. For example, hydrotalcite-like materials can b prepared starting with MgO and alumina ( I2O3) and hydrocalumite-like materials from CaO and alumina. Both CaO and MgO can be obtained by calcining the natural minerals such as Calcite (CaC03) and Magnesite (MgCθ3). Some of these layered double hydroxides, such as hydrotalcite, are commercially available and some may be naturally occurring. Moreover, methods for their synthesi are known in the art. The SO2 oxidation catalysts can be incorporated into the galleries of the LDHs using wide variety of different metal containing anions other than the ones disclosed in this invention. These include, among other things, metal carbonyls such as V(CO)g_, Fe2-CO)8 2- , Fe(CO)4 2 ~, Fe3(CO)n 2 ~, Cr(CO)5 2 ~ etc. , or metal halides such as VCl4~, CrClg 3- , 2Cl9 3 ~, FeClg 3 " etc., or metal nitriles such as Mn(CN)g 4 ~, W(CN) 8 4 ~, Fe(CN)g 3 ~ etc. or transition metal complex chelates such as metal-oxalates, Fe(ox)2 -f Wθ2(ox)~, Cr(ox)3 3 ~, or metal-acetylacetonates etc. It is known to those skilled in the art that some of the transition metals, particularly iron, is capable of oxidizing NO to NO2- Thus, the transition metal-containing LDH sorbents, especially the iron-containing sorbents disclosed in this invention may b used to remove NO x components from flue gas streams and other gas streams. In the gas streams, the calcined LDHs will react with NO x components to form solid nitrates. These sorbents may be used, for example, in the form of particles of any suitable size and shape. Such particles may be formed by conventional techniques, such a spray drying, pilling, tableting, bead formation and the like. In the coal-fired boiler application, the present sorbents may be added, either separately or with coal, to the combustion zone, (e.g., the boiler, temp. 700-1000°C) when combustion takes place. Sorbents then leave the combustion zone with coal ash and can be removed from the bag house. This process will in turn, provide enough contact time for the sorbents to react with S0 X from the flue gas streams. Thus the flue gas leaving the combustion zone/contacting zone systems have reduced amounts of sulfur oxide relative to the processing in the absence of present sorbents. If necessary, reacted sorbents can be separated from the ash, (especially the sorbents with Zn and Al, for the regeneration), e.g., by screening, density separation, or other well-known solid separation techniques. Moreover, the spent sorbents can be safely disposed without any serious environmental pollution, since S0 X in the spent sorbents is now in a thermally stable sulfate form. Furthermore, sorbents disclosed herein could be used in other processes such as hydrocarbon cracking processes where diminision of S0 X fro gas streams are necessary. The following examples will serve to illustrate certain embodiments of the herein disclosed invention. These Examples should not, however, be construed as the limiting scope of the novel invention as there are many variations which may be made thereon without departing fro the theme of the disclosed invention. Example 1 The preparation of a hydrotalcite-like Mg3Al-LD is described in this example. A solution of 12.8 g Mg(Nθ3)2*6H2θ and 9.4 g Al( θ3)3'9H2θ in 100 ml deionized water was added to a solution containing 14 ml 50% NaOH and 5 g Na2Cθ3 (anhydr. in 200 ml distilled water. The addition was carried out very slowly over a period of 90 minutes, with vigorous stirring. Following the addition, the resulted heavy slurry was heated at 65±5°C for 18 hours with good mixing. The mixture was then cooled to room temperature, and the precipitate was separated by centrifugation. The solid was washed several times with deionized water until the washings were free of salts and then dried in air. T X-ray diffraction pattern of the dried solid was corresponded to hydrotalcite and the basal spacing was found to be 7.78 . Chemical analysis showed the Mg/Al ratio to be 3.2, very near the value expected for hydrotalcite with an idealized formula unit of [Mg3Al(OH)8](Cθ3)o.5'XH2θ. By changing the amounts of Mg 2+ and Al 3+ salts used, one can prepare hydrotalcite-like materials with different Mg/Al ratios. Example 2 The preparation of [ Zn2Al(OH)g]X. ZH2O (X = NO3, CD is described in this example. All the manipulations were carried out under a N2 atmosphere and the solvents were pre-boiled for about 2 hours under 2 before use. To a 200 ml solution of 0.1M Al(NO3)3.9H2O was added a 1.0 M solution of NaOH until the pH of the solutio was 7. The white slurry was stirred for one hour, and a 200 ml solution of 0.3M Zn(N03>2 was added drop-wise. The pH of the mixture was maintained at about 6.0, by adding NaOH during the addition. The resulting slurry was boiled for 24 hours under a nitrogen atmosphere. (Upon boiling this suspension for one week produced products with high crystallinity. ) The product, [Zn2Al(OH)g]N03. ZH2O was washed several times with water by centrifugation, and dried in air. The X-ray diffraction powder pattern of the dried solid corresponded to a LDH structure powder pattern of the dried solid corresponded to a LDH structure with a basal spacing value of 7.7 j^. Employing a similar method, the Cl~ derivative, [ Zn2Al (0H)g ]C1. ZH2O can be prepared using AICI3 and gCl2- By changing the amounts of Zn + and Al + salts used hyrotalcite-like materials with different Zn/Al ratio can be prepared. Example 3 A general method for the preparation of polyoxometalate intercalated Zn/Al hydrotalcite-like materials with the general formula [Zn2Al(0H) 3 (POM n~ )ι/ n .xH2θ where POM is a polyoxometalate anion of charge n is described in this example. A boiling solution containing about 5 mequiv. portion of Zn2Al-X (X=Nθ3, CD LDH prepared in Example 2, was added drop-wise to a stirred aqueous solution containing about 7.5 mequiv. of polyoxometalate anion. After the additions was complete, the pH of the resultant slurry was adjusted to about 6 by adding dilute HNO3 acid. The slurry was stirred for about 1 hour and the solid product was isolated and washed thoroughly with water by centrifugation. The X-ray diffraction powder patterns of the dried solids correspond to a hyrotalcite-like layered structures, with polyoxometalate anions in the gallery. The basal spacings are given in Table 1. Chemical analyse conformed to the structure Zn2Al(OH)g[POM n~ 3ι/ n .YH2θ, wher POM represent the polyoxometalate with a charge of n. The anions with lower charge such as [PWi2θ40- 3 and [SiWi2θ4θ] 4- show no ion exchange, whereas intermediat anions show partial intercalation (e.g. tPCuWnθ3g(H 0) ]^~ Furthermore, polyoxometalate anions with beta-Keggin structure such as beta-[SiV3W9θ4Q] 7- undergo partial intercalation. The preparation of polyoxometalate intercalated Zn/Al-LDH materials from [ Zn2Al(OH) ]N03« ZH2O according to the U.S. Patent No. 4,454,244 disclosed by Woltermann resulted in X-ray amorphous materials. Example 4 The preparation of a Mg/Al LDH of the formula, [MggAl2(OH)ιg]OH.xH2θ LDH from hydrotalcite is described in this example. A sample of hydrotalcite, prepared according t Example 1, was calcined at 500°C for three hours. A 5 gr portion of this sample was pulvarized and suspended in a 200 ml of hot (65°C) degassed deionized water to form a white slurry. The resulting slurry was then stirred vigorously at 65°C for one hour under an atmosphere of nitrogen, to form the hydroxide derivative [Mg3Al (OH) 8-OH.XH2O. The resulting slurry was cooled to room temperature and volume was adjusted to 250 ml with deionized water. The X-ray diffraction powder pattern of the dried solid corresponded to a hydrotalcite structure. The basal spacing was found to be 7.76 . Example 5 This example describes the general method adopted in preparing the polyoxometallate-intercalated Mg3Al-LDHs. A solution containing about 25 mmol portion of Mg3Al LDH-OH slurry prepared according to Example 4 was added dropwise to stirred aqueous solution containing 40 mmols of polyoxometalate anion under an atmosphere of nitrogen. The resulting slurry was stirred at ambient temperature for about 18 hours and the solid product was isolated and washed thoroughly with water by centrifugation The X-ray diffraction powder patterns of the dried solids corresponded to the hyrotalcite-like structure with intercalated polyoxometalates. The basal spacings are given in Table 1. Example 6 The uptake of SO x by various LDH sorbents was determined by thermogravimetric analysis using a Cahn Model TG-121 thermogravimetric analyzer. Approximately 50-mg portions of the sorbent was placed on a quartz pan in the thermogravimetric balance. Subsequent treatment of the sample was carried out in a three step procedure. Step 1: Under a flow of air as a carrier gas (200ml/min), sample was allowed to equilibrate at 25°C for 15 minutes and slowly heated (5°C/min) to the calcining temperature, typically 700°C. The sample was maintained at this temperature for an additional 1 hour. Step 2: SO2 gas (0.5%) then was introduced into the carrier gas at the temperature and the weight was monitored for a 1 hour period. For the more reactive sorbents a rapid initial weight uptake of SO x was observed, especially with sorbents containing iron. The weight increase corresponded to the amount of SO3 absorbed by the calcined sample (Table 2). For a typical TGA plot see Figure 1. Step 3: Passage of SO2 into the carrier gas was ceased and the sample weight at reaction temperature was monitored for another 1 hour. This step was carried out in order to determine the thermal stability of the metal sulfate products formed after the reaction with S0 X . All of the samples containing Mg and Al in the layers showed little or no weight loss, whereas most of the samples that contained Zn in the layers showed a significant weight loss (Table 3) . Example 7 Hydrotalcite-like materials intercalated with metal polyoxoanions as in Examples 3 and 5 were tested for SO x sorption at 700°C according to the procedure of Example 6. The results are given in Table 2. LDHs that contain Mg and Al show better S0 X adsorption than that contain Zn and Al. The preferred polyoxoanion is Feθ4 ~ , which showed more than 85% conversion of Mg sites to MgS04 when exposed to SO2- However, polyoxoanions containing V, W and Mo also show enhanced SO x adsorption, compared to free hydrotalcite Compared to polyoxometalates intercalated Mg3Al-LDHs, the corresponding Zn2Al-LDH formed metastable products with S0 Upon further calcining in the absence of SO2 (Step 3, Example 6), most of these spent sorbents lost weight (Tabl 3). Accordingly some of these spent sorbents can be regenerated for further .use, (See Example 9). Example 8 The hydrotalcite-like material intercalated wit v 10°28^ ~ according to Example 4, was tested for SO x sorption at different calcining temperatures according to the procedure of Example 6. Results are given in Figure 2. Preferred calcining temperatures were in the range 550-800°C where 32% to 52% conversion of Mg sites to MgS04 was observed. At very high temperatures (>900°C) the uptake was very low. Example 9 Some of the Zn2Al-LDHs intercalated with polyoxometalates according to Example 5, were regenerated after exposing to SO2 and tested for the SO2 re-adsorption using the f(blowing procedure. Approximately a 50-mg portion of the Zn2 l LDH intercalated with SiV3 9θ40 8 ~ was tested for SO x uptake using the Steps 1 and 2 in the procedure given in Example 7, and sample was further treated as follows: Step 3: Passage of SO2 into the carrier gas was ceased and the sorbent was heated to 800°C (5°C/min) and the temperature was maintained at this value for an additional 30 minutes and cooled down to 700°C (-5°C/min). Step 4: SO2 gas (0.5%) was again introduced into the carrier gas at 700°C for a 1 hour period. Step 5: Passage of SO2 was ceased and the reaction temperature was kept at 700°C for another 1 hour period. During Step 2, when SO2 was introduced for the first time a weight uptake of 5.6% was observed (Figure 3). Almost all (90%) of this weight gain was lost in Step 3 at higher temperatures from this spent sorbent, indicating the release of the absorbed SO x . The SO3 uptake by this regenerated sorbent was 6.4% in Step 4 indicating that this " recovered material was as good as the virgin sorbent. It is intended that the foregoing description be only illustrative --f the present invention and that the present invention L-.i limited only by the hereinafter appended claims .

Claims: WE CLAIM: -1- A process for removing the S0 X components from flue gas and other gas streams which comprises contacting the said gas stream with a heated sorbent composition wherein the said sorbent is selected from the group consisting of a layered double hydroxide structure of formula: [Mι_ χ IlM χ III(0H) 2 3 (A n -) x n .yH 2 0 wherein M 11 is a divalent metal cation and M 111 is a trivalent metal cation selected from the group consisting of metal cations which form metal oxides and which are capable of reacting with SO2 to form metal sulfites and SO3 to form metal sulfates, A is an interlayer anion of charge n- which comprises of at least one metal atom which provides oxidation of sulfur dioxide to sulfur trioxide in an amount sufficient that said layered double hydroxide structure promotes the oxidation of the sulfur dioxide to the sulfur trioxide at sulfur dioxide oxidation conditions, x is between 0.8 to 0.12 and a heat treated derivative of the double hydroxide. -2- The process of Claim 1, characterized in that the MH is at least in part an alkaline earth metal cation. -3- The process of Claim 2 wherein said M 11 is at least in part alkaline metal cation selected from the grou consisting of magnesium and calcium cations. -4- The process of Claim 1 wherein said M 11 metal cation is at least in part selected from the group consisting of transition metal cations. -5- The process of Claim 4 wherein said transition metal cation is a zinc cation. -6- The process of Claim 1 wherein said Mi l cation is at least in part selected from the Group consisting of 13 (formerly IIIA) metal cations in the periodic table. -7- The process of Claim 6 wherein the said Group 13 metal cation is an aluminum cation. -8- The process of Claim 1, wherein the said A anion contain metals selected from the group consisting of main group metals, transition metals and rare earth metals which provide oxidation of sulfur dioxide to sulfur trioxide in an amount sufficient that said layered double hydroxide structure promotes the oxidation of the sulfur dioxide to the sulfur trioxide at sulfur dioxide oxidation conditions. -9- The process of Claim 8, wherein the anion A is a polyoxometalate anion. -10- The process of Claim 9, wherein the said polyoxometalate anion is an isopolyoxometalate, which contains one metal atom and oxygens. -11- The process of Claim 10, the said anions are selected from Crθ4 2 ~, Feθ4 2 ~, HV04 2" , Mθθ4 2 ~, ViQθ28 6 ~f θ7θ24^~ and 7θ24^~ and mixtures thereof. -12- The process of Claim 9, wherein the said polyoxometalate anion is a heteropolyoxometalate, which contain more than one metal atom and oxygens. -13- The process of Claim 12, wherein the said heteropolyoxometalate anion is an anion with a Keggin structure. -14- The process of Claim 13, the said Keggin anion is selected from the group consisting of SiV3 9θ4o 7~ and BVW oθ4θ 7~ mixtures thereof. -15- The process of Claim 12, wherein the said heteropolyoxometalate anion is an anion with a lacunary (defect) Keggin structure having the formula [XMnθ393 n ~ and [XM9θ343 n~ where X and M are combination of metals selected from the periodic table. -16- The process of Claim 15, the said lacunary (defect) Keggin anion is selected from the group consisting of BCoWnθ39 ~ and SiWnθ39 - and mixtures thereof. -17- The process of Claim 12, wherein the said heteropolyoxometalate anion is an anion selected from robust anions consisting of fused Keggin-type structure. -18- The process of Claim 17, wherein the said fused Keggin-type anion is BC0W12O42 8- - -19- - The process of Claim 8, wherein the anion A is a metal oxalate anion. -20- The process of Claim 19 characterized in that, the metal oxalate (ox) anion is an iron oxalate such as, Fe(ox) 3 3~ . -21- The process of Claim 1 wherein the heating is carried out at a temperature range of 400-1000°C. -22- The process according to Claim 1 wherein M 11 is Zn is regenerated by heating to remove the bound SO x and to isolate the sorbent for reuse.

Inventors: AMARASEKERA JAYANTHA, PINNAVAIA THOMAS J, POLANSKY CHRISTINE A, AMARASEKERA, JAYANTHA, PINNAVAIA, THOMAS, J., POLANSKY, CHRISTINE, A.
Applicants: UNIV MICHIGAN STATE, MICHIGAN STATE UNIVERSITY
Application year: 1991
Main classification: B01J8
IPC codes: B01D53, B01J20, C01B17