Method of producing an apparatus comprising an optical gain device

Abstract: Disclosed is apparatus comprising an optically pumped optical gain device that comprises a rare earth (RE)-doped planar waveguide (12) with non-uniform dopant distribution in the core of the waveguide. The RE ions are advantageously distributed such that the ions are concentrated in a core region in which the mode intensity of both signal radiation and pump radiation is relatively high. In preferred embodiments of a single mode planar waveguide (12) according to the invention the RE ions are substantially concentrated in the central core region (122). A method of making the disclosed apparatus is also disclosed. The method involves implantation of RE ions into the core region.

Description: Field of the Invention This invention pertains to the field of optical gain devices, e.g., optical amplifiers, comprising rare earth-doped waveguide means. Background of the Invention The principles of amplification of an optical signal in an Er-doped fiber amplifier are known to those skilled in the art. See, for instance, J. R. Armitage, Applied Optics , Vol. 27(23), pp. 4831-4836, Dec. 1988. Efforts have been undertaken to optimize the characteristics of Er-doped fiber amplifiers. See, for instance, U.S. Patent 4,923,279. Although optical fiber amplifiers can advantageously be used in a variety of communication systems, there are many potential applications for an optical amplifier to which fiber amplifiers are not readily or conveniently adapted. For instance, it would be desirable to be able to integrate an optical amplifier with electronic devices or circuits, since such integration can be expected to result in decreased cost, increased ruggedness, and possibly greater speed. Such integration would be facilitated by the availability of a planar optical amplifier. Furthermore, the availability of planar optical amplifiers would significantly advance progress towards fully integrated optics and, on a somewhat less advanced level, have immediate applications in such diverse fields as optical signal detection, optical backplanes of switching equipment, local area optical fiber networks, and optical fiber cable TV systems. Finally, planar optical amplifiers can be expected to be desirable replacements for optical fiber amplifiers, due to their more compact nature and increased ruggedness, and are likely to find application in undersea lightwave communication systems. Planar optical waveguides are known. Among the known types of planar waveguides are silica-based glass waveguides disposed on a silicon substrate, as disclosed, for instance, in U.S. Patent 4,902,086. For a broader discussion of planar optical waveguides, see, for instance, "Integrated Optics, Physics and Applications", edited by S. Martellucci et al., Plenum Press, especially the chapter by G. Chartier, pp. 49-72. On page 53 of that monograph can be found a compilation of materials in which optical waveguides have been formed, together with a listing of fabrication techniques used. On pages 63 to 65 of the monograph can be found a discussion of waveguide formation by means of ion implantation. As described there, the technique involves exposing a substrate to a collimated ion beam, resulting in modification of the properties of an appropriately shaped region of the substrate that manifests itself as a change in refractive index of the region. P. J. Chandler et al., Electronics Letters , Vol. 26(5), pp. 332-334 (March 1990) report on the fabrication of optical waveguides by implantation of inert ions (He + ) into single crystal LiNbO 3 bodies. The LiNbO 3 was uniformly doped with MgO, or Nd and Cr. Y. Hibino, I.E.E.E. Photonics Technology Letters , Vol. 1(11), pp. 349-350 (November 1989) disclose formation of a Nd-doped silica optical waveguide laser on a Si substrate by a technique that involves depositing glass soot onto the substrate, soaking the soot layer in Nd-containing alcohol, sintering of the soot layer, patterning of the sintered layer to form a 20 µm wide core ridge, and overcladding the thus formed core strip with a glass cladding that was also formed from soot. Fluorescence and lasing were observed. In view of the potentially high commercial significance of planar optical gain devices (e.g., amplifiers and lasers), improved such devices would clearly be of interest. In particular, devices having improved matching of the dopant atom distribution to the mode field of the signal radiation in the planar waveguide of the device would be very desirable, since such improved matching can, inter alia, result in improved gain performance of the device. This application discloses a waveguide with such improved matching, and a technique for making the waveguide. Summary of the Invention In a broad aspect the invention is a method of making an article that comprises an improved optical gain device, as defined by the claims. More particularly, the gain device comprises planar waveguide means disposed on a substrate. The waveguide means comprise a core and a cladding and are adapted for guiding signal radiation of wavelength λ s . The article further comprises means for coupling pump radiation of wavelength λ p <λ s into the planar waveguide means. Exemplarily, 1≲λ s ≤3 µm, and 0.4≲λ p <3 µm. The planar waveguide means comprise silica-based glass that contains at least one species of rare earth (RE) ions capable of luminescence in response to the pump radiation. Significantly, the RE ions are non-unifonnly distributed in the planar waveguide means. In particular, the RE ions are distributed such that, in a given core cross section, the maximum concentration of RE ions in a first region of the cross section is at least twice as high as the maximum concentration of the RE ions in a second region (typically the remainder) of the cross section. In preferred embodiments the RE ions are distributed such that the ions are concentrated in the core region where the mode intensity of both signal radiation and pump radiation is highest. Typically this will be the center region of the core. In preferred embodiments at least a part of the second region is disposed between the first region and the "top" surface of the core, i.e., the part of the core surface that is not adjacent to the substrate. In particularly preferred embodiments the second region substantially surrounds the first region. In a particular embodiment the substrate is a single crystal Si body, e.g., a wafer, with at least a part of a major surface of the body covered by a SiO 2 layer. The core of the planar waveguide means consists of silica-based glass (e.g., phosphosilicate). The core material is disposed on the SiO 2 layer, and is substantially covered by a silica-based glass that serves, together with the SiO 2 layer, as cladding. The refractive index of all of the cladding material is lower than that of the core material. In this particular case the RE ions are Er ions. Gain devices fabricated according to the invention typically are amplifiers but could be lasers, and typically are disposed on a substrate in or on which there is at least one other optical or electro-optical device that is in optical communication-relationship with the gain device. The other device exemplarily is a pump laser or a photodetector. Optionally there is also one or more electronic device (e.g., a transistor) or IC in or on the substrate. The method of making an article according to the invention exemplarily comprises providing the substrate (typically a Si wafer with a SiO 2 layer thereon) with a layer of silica-based core material thereon, exposing at least a portion of said layer to RE ions such that at least a major portion of said ions is caused to be implanted into the core material, patterning, either before or after the implantation, the layer of core material such that the core of the planar waveguide means results, and depositing a layer of cladding material. The method is practiced such that in the finished article the RE distribution in the core is non-uniform, as described above. Brief Description of the Drawings FIGS. 1 and 2 schematically show cross sectional views of exemplary RE-containing planar waveguide means fabricated according to the invention; FIG. 3 depicts schematically an exemplary optical amplifier fabricated according to the invention; FIG. 4 shows schematically a photodetector with an amplifier(according to the invention; and FIG. 5 schematically depicts a passive planar waveguide coupled to planar waveguide means fabricated according to the invention by means of an adiabatic transition section. Detailed Description of Some Preferred Embodiments FIG. 1 schematically depicts the cross section of waveguide means of a gain device fabricated according to the invention. Numeral 10 refers to a substrate body, preferably a Si body, and numeral 11 refers to first cladding material, preferably SiO 2 formed by oxidation of the Si body. Core 12 is disposed on 11, with second cladding material 13 surrounding the core. The core comprises a first region 122 having a relatively high RE (exemplarily Er) concentration, and a second region 121 having a relatively low RE concentration. The maximum RE concentration in 122 is at least twice (preferably at least 5 times or even 10 times) the maximum concentration in 121. The second cladding can be SiO 2 but could be any other appropriate transparent (at λ s ) medium, provided the refractive index of the core glass is sufficiently higher than that of the second cladding material (and, of course, also than that of the first cladding material) such that radiation of wavelength λ s (and also of wavelength λ p ) is guided in the structure. FIG. 2 schematically depicts the cross section of another waveguide means fabricated according to the invention that differs from that of FIG. 1 in that, inter alia, the first core region 22 is surrounded by the second core region 21. This results in particularly efficient coupling between the dopant atoms and the mode field of the signal radiation if the waveguide is a single mode guide at λ s . RE-implanted waveguides of the type shown in FIG. 1 exemplarily can be made by first forming a relarively thick cladding layer on a substrate surface, depositing on the cladding layer a silica-based core glass layer of appropriate thickness (e.g., about 2 µm), optionally depositing a relatively thin (e.g., 0. 1 µm) conducting layer atop of the core glass layer in order to avoid charge build-up during ion implantation, and exposing the described multilayer structure to a beam of energetic (exemplarily 1-5 MeV) RE ions. Advantageously the ion energy is selected such that the maximum of the resulting RE distribution in the core glass layer is substantially centered in the layer. The ion dose generally is selected such that the desired gain can be achieved in a predetermined length of waveguide. Exemplarily the dose is in the range 10 16 -10 17 ion/cm 2 . The substrate temperature during implantation advantageously is between room temperature (about 22°C) and about 500°C, preferably between 150°C and 300°C. After completion of the implantation the optional conductive layer is removed and the waveguide is defined by removing unwanted core material by a known technique, exemplarily including lithography and etching. Subsequently the upper cladding layer (exemplarily SiO 2 ) is formed by a known technique, e.g., by low pressure chemical vapor deposition (LPCVD). Waveguides of the type shown in FIG. 2 can exemplarily be produced by a press similar to the above described one, except that the core material is implanted through a mask that limits the lateral extent of the implanted region. The implantation can be carried out prior or subsequent to patterning of the core layer, as those skilled in the art will recognize. It can also be made by a technique similar to that described in Example 2 below. FIG. 3 schematically depicts an optical amplifier 30 fabricated according to the invention. The exemplary amplifier comprises four pump lasers (311 -314), of which two (e.g., 312 and 314) are "spares". Lasers 311 and 313 inject co-propagating and counter-propagating radiation, respectively. Of course, all pump lasers in excess of one are optional. Signal radiation propagates through passive waveguide section 321 to amplifier waveguide 34, is amplified therein through stimulated emission, with the amplified signal radiation propagating through passive waveguide section 322. Pump radiation from 311 is guided by passive waveguide 324 to polarization splitter 33, and from there by passive guide 325 to directional coupler 38. These components can be conventional, and can be either discrete or integrated. Coupler 38 serves to couple the pump radiation into 321 such that it propagates in the direction of signal flow. The counter-propagating pump radiation is similarly coupled into the signal path. Optional known grating filter 35 serves to suppress spontaneous emission. Optical fiber can be coupled to such an amplifier assembly, exemplarily in a manner substantially as disclosed in U.S. patent 4,904,036. FIG. 4 schematically depicts a further exemplary article fabricated according to the invention, namely, a detector assembly. Signal radiation propagates through passive guide 401 to amplifier section 42, and further through passive guide 403 to photodetector 43, exemplarily a PIN diode disposed over a waveguide turning mirror. Pump radiation from pump laser 41 is coupled by means of directional coupler 44 into 403. A detector assembly of the type shown in FIG. 4 can have the high sensitivity typically associated with avalanche photodiodes (APDs) and the low noise typically associated with PINs. In articles fabricated according to the invention there will typically be found junctions between passive waveguide sections and amplifier sections. FIG. 5 exemplarily shows, in top view, a section of passive waveguide 50, a section of amplifier guide 51, and transition section 52 therebetween. FIG. 5A shows section A-A of FIG. 5, with substrate 55, lower cladding 56, core 58, and upper cladding 57. FIG. 5B shows section B-B of FIG. 5 wherein the core of the amplifier section comprises outer region 59 that is substantially free of RE, and center region 60 that contains substantially all of the RE. As those skilled in the art will appreciate, it will frequently be advantageous if the amplifier guide is somewhat narrower than the passive guide, so as to achieve improved amplification efficiency. In such a case it will typically be advantageous to provide for an adiabatic transition between the two waveguide sections, as shown schematically in FIG.5. An important advantage of articles fabricated according to the invention is the relatively low loss coupling that is possible between the planar waveguides and standard silica-based optical fiber. Thus, in articles fabricated according to the invention, the refractive index of the core of the planar waveguide will typically differ by at most 5% from the effective refractive index of the core of the optical fiber that is to be coupled to the planar waveguide. Although the discussion has been primarily in terms of a planar waveguide optical amplifier, those skilled in the art will realize substantially the same principles can be embodied in a planar waveguide laser, provided that the structure is modified to provide an appropriate optical cavity. Workers in this field will be readily able to do this. Furthermore, silica cladding and phosphosilicate glass are not the only possible waveguide materials. For instance, the core can be RE-doped Si 3 N 4 and the cladding can be silica-based glass. Er is not the only RE species useful in the practice of the invention. For instance, Nd can be used and is of considerable interest because of its transition at λ-1.3 µm, coinciding with the minimum dispersion window of conventional silica fiber. Other RE species have different transitions that may be of interest for particular applications. Still furthermore, gain devices fabricated according to the invention do not necessarily have to be produced by a technique that includes ion implantation. We currently believe that at least planar guides of the type shown in FIG. 1 can be produced by CVD, by appropriate introduction of a RE-containing precursor into the reactor, or by sputtering from a sequence of targets. Example 1: On a conventional Si wafer was formed a 15 µm thick silica layer by conventional high-pressure thermal oxidation of the Si (HIPOX). On the thus formed silica surface was deposited a 2 µm thick layer of phosphosilicate glass (8 weight % P in SiO 2 ) by conventional low-pressure chemical vapor deposition (LPCVD) using silane, oxygen, and phosphine. This was followed by conventional deposition of a 0.11 µm thick layer of Al on top of the P-glass (core) layer. Into the thus prepared multilayer structure were implanted 2.9 MeV Er ++ ions in a vacuum at a base pressure below 10 -6 Torr. The implantation fluence was 3.4x10 16 ions/cm 2 . During implantation the wafer was kept at 200°C. The resulting Er distribution had approximately Gaussian shape, with the peak at about 1 µm depth from the glass/Al interface, and with a full width at half maximum of about 0.6 µm. Subsequently the Al layer was removed by conventional means, and the core material layer was patterned by conventional lithography and etching such that a 5 µm wide and 5.5 cm long strip of core material remained on the substrate. The planar waveguide was completed by deposition of a 5 µm thick layer of silica by LPCVD from silane and oxygen, followed by densification of the layer in a nitrogen ambient at 1000°C. The planar waveguide was designed to support only a single mode at λ=1.54 µm and, when pumped at λ=0.9729 µm, exhibited a luminescent transition centered around λ=1.54 µm. A lifetime of about 4 ms was observed. When the waveguide was pumped at λ=0.9729 µm, signal radiation at λ s =1.536 µm that was transmitted through the 5.5 cm length of waveguide showed significantly increased amplitude, as compared to transmission in the absence of pumping. Example 2: A Er-doped planar waveguide is made substantially as described in Example 1, except that the Er-doped guide is disposed between two conventional passive waveguide sections, that a further section of passive waveguide is coupled to the Er-doped guide by means of a conventional directional coupler, and in that the core material is deposited in two steps, with Er implantation between the steps. In particular, a 3 µm thick layer of 8% P-glass is deposited, Er is implanted as described in Example 1, the P-glass layer is patterned such that a 3 µm wide and 5.5 cm long strip of implanted core material remains on the substrate. Subsequently, a 1 µm thick layer of 8% P-glass is deposited and patterned such that the Er-implanted region is covered by the later deposited P-glass, and the resulting core width is 5 µm. As described in Example 1, an appropriate cladding layer is subsequently deposited.

Claims: Method of making an article that comprises an optical gain device (34) that comprises optical waveguide means comprising a core (21) and a cladding (13), associated with each of said core and cladding being a refractive index, the refractive index of the cladding being lower than the refractive index of the core, such that the waveguide means are adapted for guiding signal radiation of wavelength λ s , and the gain device further comprises coupling means (38) for coupling pump radiation of wavelength λ p <λ s into the optical waveguide means, CHARACTERIZED BY a) providing a substrate (10, 11) having a major surface, with a layer comprising core material on the major surface; b) implanting rare earth ions into said core layer such that, in a given cross section, the maximum rare earth ion concentration in the core layer is located in a first region situated between the substrate/core layer interface and the core layer surface and is at least twice as high as the rare earth concentration in a second region of the core layer; c) patterning, either before or after step b), said core layer such that the core of said optical waveguide means results; and d) depositing cladding material. Method of claim 1, wherein the rare earth ions comprise Er ions. Method of claim 1, wherein the substrate is a Si body (10) having a major surface, with at least a part of the major surface covered by a SiO 2 layer (11), wherein the core of the waveguide means consists of silica-based glass and is disposed on said SiO 2 layer, wherein the cladding material is silica-based glass, and wherein the rare earth ions consists essentially of Er ions. The method of claim 1, wherein the gain device is an optical amplifier. The method of claim 4, wherein in or on the substrate there is at least one other optical or electro-optical device that is in optical communication-relationship with the optical amplifier. The method of claim 5, wherein the at least one other device is a photodetector disposed such that it receives radiation that has propagated through the optical amplifier. The method of claim 5, wherein the at least one other device is a laser adapted for emitting the pump radiation. The method of claim 1, wherein the article further comprises an optical fiber coupled to the planar optical waveguide means.

Inventors: BLONDER GREG E, JACOBSON DALE C, KISTLER RODNEY C, POATE JOHN M, POLMAN ALBERT, BLONDER, GREG. E., JACOBSON, DALE C., KISTLER, RODNEY C., POATE, JOHN M., POLMAN, ALBERT
Applicants: AT & T CORP, AT&T CORP.
Application year: 1991
Main classification: G02B6
IPC codes: G02B6, H01S3, G02F1