Mixed emulsion of a liquid polysulfide and dispersion of an oxidative curative therefor

Abstract: Stable mixed emulsion/dispersions of a liquid polysulfide and an oxidative curative therefor. The liquid polysulfide is emulsified in water using a surfactant with a hydrophile/lipophile balance of between 18 and 20. Particulates of an oxidative curative are separately dispersed with surfactants in water. The emulsions and dispersion are then blended together.

Description: This invention relates to stable mixed emulsions of liquid polysulfides and dispersions or curatives therefor, which mixed emulsion/dispersions are useful as sealants. Liquid polysulfide and liquid polysulfide compositions are well known, having been described, for example in U.S. Patents Nos. 3,331,782; 4,060,570; 3,852,214; 3,817,930; 3,770,678; 3,637,574; 3,518,211; 3,518,107; 3,349,047 and 2,466,936. Generally, liquid polysulfide polymers are materials having the structure HS(RSS-R'-SS) x R''SH wherein R, R' and R'' may be the same or different hydrocarbon, oxyhydrocarbon or thiahydrocarbon moieties. These polymers are generally linear, but may be branched, for example, by preparing these compositions with trichloropropane. Liquid polysulfides are curable with a variety of oxidative curatives, particularly inorganic oxides and peroxides. Oxidative curatives link polysulfide polymers together by oxidation of terminal thio (-SH) groups to form disulfide (-S-S-) linkages. Examples of suitable curatives are given in U.S. Patent No. 3,331,782, the teachings of which are incorporated herein by reference. Cured polysulfides in combination with various fillers, pigments, plasticisers etc. are useful, for example, as sealants and caulking materials. The molecular weights of polysulfides may vary over a wide range, e.g., from 500 to upwards of 25,000. Typically, high molecular weight polysulfides are produced, and then the molecular weight is adjusted downward by a split stripping process. This process also provides the free terminal thio moieties. Typically, commercial liquid polysulfides have molecular weights in the 1000 to 10,000 range. As described in referenced U.S. Patent No. 3,331,782, liquid polysulfides are generally provided in a two-package system with the polysulfide material separately packaged from the curative. The curative is typically provided as a paste that is added to the liquid polysulfide material at the time of use. The high reactivity of liquid polysulfides with the curative, particularly when the curative is a peroxide, has generally precluded these components from being packaged in a one-package system. Two-package systems are inherently disadvantageous relative to one-package systems. The need to mix at the site of application is at least an inconvenience for the user. Inadequate or improper mixing may result in an unsatisfactory cured product. The lack of mixing apparatus and/or the inconvenience of mixing may cause a potential user to seek an alternative sealing or caulking material. It is therefor a general object of the present invention to provide a one-package composition containing both polysulfide and an oxidative curative therefor. There have been produced one-package mixtures of polysulfides and inorganic curatives in which premature curing is prevented by complete removal of water from the system. This type of system relies on absorption of water vapor from the atmosphere for eventual curing. A major disadvantage of such a system is the inordinately long cure time. Typically, such a system requires at least about 24 hours to become tack-free and much longer to completely cure. Such extended cure times are unacceptable for many sealing and caulking applications. It is also known to produce polysulfide latexes in which liquid polysulfides are emulsified in an aqueous medium. Such latexes are described, for example, in U.S. patent No. 3,770,678. These latexes do not contain an oxidative curative, but rather attain their final physical properties through coalescence of the latex particles upon evaporation of solvent or water. US-A-4,098,736 discloses a one-part composition in which a first reactant is emulsified within a liquid which is substantially impermeable to all of the reactants and droplets of this emulsion are then emulsified within a continuous phase which is, or has dissolved in it, a second reactant. In one example an amine curing agent is emulsified in a hydrocarbon solution, and this emulsion is in turn emulsified into a continuous epoxy resin phase. The present invention consists in a stable mixed aqueous emulsion and aqueous dispersion comprising (a) water as the continuous aqueous phase, (b) liquid polysulfide emulsified with surfactant within said continuous aqueous phase and (c) particulates of an oxidative curative for said polysulfide separately dispersed with surfactant in said continuous aqueous phase, wherein the content of said liquid polysulfide is from 50 to 70 wt. percent, the content of said oxidative curative is from 5 to 10 wt. percent, the content of said surfactant(s) is from 3 to 7 wt. percent and the water content is at least 20 wt. percent, said percentages being based upon the total weight of polysulfide, oxidative curative surfactant(s) and water, and wherein the surfactant in which said polysulfide is emulsified has a hydrophile/lipophile balance of 18 to 20, as determined by the HLB system referred to below. Additional components, such as fillers, colorants, etc. may also be mixed with the emulsified polysulfide and dispersed curative particulates. According to a further aspect, the invention consists in a method of preparing a stable mixed emulsion of a liquid polysulfide and a dispersion of an oxidative curative therefor, the method comprising mixing liquid polysulfide, water and a surfactant having a hydrophile/lipophile balance of between 18 and 20, as determined by the HLB system referred to below with shear sufficiently high to produce an emulsion of he polysulfide in water, mixing oxidative curative particulates, water and a surfactant with shear sufficiently high to produce a dispersion of the oxidative curative particulates in water, and blending said liquid polysulfide emulsion with said oxidative curative dispersion with sufficiently low shear to maintain both the liquid polysulfide emulsion and dispersed oxidative curative particulates out of chemical contact with each other. Herein, unless otherwise noted, all percentages are by weight. Unless otherwise noted, all weight percentages are relative to the total weight of (A) the polysulfide, (B) the curative, (C) the surfactant(s) and (D) the water. The liquid polysulfides useful in the invention include -SH-terminated polysulfides described in the above-mentioned patents, including branched and straight-chain polymers. All molecular weights of liquid polysulfides are considered useful for the present invention, although polysulfides having molecular weights in the 1000-10,000 range are preferred. Inorganic curatives include inorganic oxides such as ZnO, PbO, MgO, CaO, BaO, FeO, Fe₂O₃, CoO and CuO; inorganic peroxides such as ZnO₂, MgO₂, CaO₂, MnO₂, TeO₂, SeO₂, FeO₂, As₂O₃, Sb₂O₃, Sb₂O₅, SnO₂ and Pb₃O₄; and inorganic oxidizing agents such as Na₂Cr₂O₇, K₂Cr₂O₇ and (NH₄)₂Cr₂O₇. Inorganic peroxides, such as CaO₂ are preferred. It is found that the choice of the surfactant used to emulsify the liquid polysulfide is critical to establishing a stable mixed emulsion of the liquid polysulfide and dispersion of the oxidative curative. In particular, it is found that the surfactant used to emulsify the liquid polysulfide should have a hydrophile/lipophile balance (HLB) of between 18 and 20. Measurements of HLB are described in a publication entitled THE HLB SYSTEM of ICI Americas Inc., Wilmington, Delaware 19897, 1984. Preferred surfactants for emulsifying the liquid polysulfide are block copolymers, particularly block copolymers of the ABA configuration, in which more hydrophilic "A" blocks flank a more hydrophobic "B" block. One suitable type of block copolymer comprises polyethylene oxide blocks flanking a more hydrophobic block of polypropylene oxide. Such block polymer surfactants are sold by BASF Wyandotic Corporation under the tradename Pluronic. The amount of surfactant required for emulsification of the liquid polysulfide in water is at least 3.5 wt. percent relative to the polysulfide; however, it is preferred to use higher amounts, e.g., up to 10 wt. percent relative to the polysulfide,to ensure stability of the polysulfide in the presence of dispersed oxidative curative particulates. The choice of surfactant used for dispersing the particulates of oxidative curative is considered less critical than the choice of that which must be used for emulsifying the liquid polysulfide. Generally, the surfactant used for dispersing the oxidative curative particulates is one having a straight hydrocarbon chain and a hydrophyllic end group, e.g., sodium lauryl sulfate. The final necessary ingredient in the mixed emulsions of the present invention is water. The water maintains separation between the emulsified liquid polysulfide and the dispersed particulates of oxidative curative, preventing them from reacting. Eventual removal of the water, i.e., by evaporation, destroys the emulsification of the liquid polysulfide and the dispersion of the oxidative curative and allows the oxidative curative to react with the terminal thio groups on the liquid polysulfide and thereby effect the cure. Generally, at least about 20 wt. percent water is necessary to maintain a mixed emulsion. The mixed emulsion/dispersion by itself is a viscous flowable material suitable for use as a sealant. However, the emulsion/dispersion can also be thickened into a paste by the addition of appropriate fillers. Such thickened formulations are useful, for example, as caulks. Suitable fillers, for example, include TiO₂, carbon black, calcium carbonate, clays and limestone. The mixed emulsion/dispersion may also include plasticisers for plasticising the polysulfide composition when it is eventually cured. Generally, such plasticisers are hydrophobic plasticizers known in the art. These are admixed with the liquid polysulfide prior to emulsification. Suitable plasticizers include chlorinated plasticizers, such as chlorinated biphenyl and chlorinated paraffin, and plasticisers sold under the trade names Santiciser 160, 261 and 278 by Monsanto. The composition may also contain a variety of additional components as is known in the art, such as whitners, pigments, latex stabilizers, etc. To prepare the mixed emulsion/dispersions of the present invention, an emulsions of the liquid polysulfide is prepared and a dispersion of curative particulates is prepared separately. The polysulfide is admixed with any plasticizer, and the plasticizer and the surfactant for the polysulfide is added to an aqueous solution; high shear, such as that provided by an homoginizer is used to prepare the emulsion. This emulsion of polysulfide typically contains between 50 and 70 wt. percent liquid polysulfide, between 3.5 and 10 wt. percent surfactant, balance water, calculated relative to the total weight of polysulfide, surfactant and water. Some heat, e.g., to provide a temperature in the range of 40-50°C, facilitates emulsion. In a similar manner, oxidative curative particulates, surfactant and water are mixed and a dispersion (or cure paste) formed. The shear needed to disperse the particulates may be somewhat less than that required to emulsify the liquid polysulfide. This dispersion contains between 40 and 60 wt. percent particulates, between 0.5 and 5 wt. percent surfactant, balance water, calculated relative to the total weight of particulates, surfactant and water. After separately preparing the emulsion and dispersion, they are mixed together, using sufficiently low shear so as not to deemulsify the liquid polysulfide or destroy the dispersion of the particulates of curative. In this step, additional ingredients, such as fillers, may be added. It is preferable that any filler have rheological properties similar to that of the emulsified curative particulates. That a mixed emulsion/dispersion of liquid polysulfide and oxidative curative should be stable is surprising, because such flowable one-package compositions have long been sought, yet never achieved. The invention will now be described in greater detail in terms of specific examples Example 1 A white sealant is produced containing as follows: Liquid Polysulfide Emulsion LP-12 (liquid polysulfide MW 4000) 51.67 Santicizer 160 (plasticizer) 15.52 Pluronic F-88 (surfactant) 3.90 Pluronic P-105 (surfactant) 1.29 Water 25.65 100.00 Cure Paste (CaO Emulsion) Water 44.00 Tamol 731-SD (surfactant) 1.00 CaO₂ 55.00 100.00 Blend Emulsion 49.25 2-Mercaptoethanol (Chain stop agent to produce a soft rubber) 0.04 Tamol 731-SD 0.33 Titanox 2101 (TiO₂ filler) 7.63 Gamasperse 255 (CaCO₃ filler) 38.17 Cure Paste 4.58 Both the Liquid Polysulfide emulsion and the Cure paste are prepared using high shear. The Liquid polysulfide emulsion and additional ingredients (except for the cure paste) are then mixed together at high shear. Finally, the cure paste is added in a low shear mix. The physical properties of the cured rubber-like sealant are as follows: Physical Properties Hardness 50 (Shore A) Tensile 504 kPa (73.1 psi) 100% modulus 495 kPa (71.8 psi) Ultimate Elongation 239% Example 2 A black coating is produced containing as follows: Liquid Polysulfide Emulsion LP-32 (liquid polysulfide MW 4000) 67.00 Pluronic F-88 3.00 Pluronic P-105 1.00 Santicizer 261 3.35 Water 25.65 100.00 Cure Paste Water 42.00 MnO₂ (Eagle Picher G) 57.00 Tamol 731SD 1.00 Blend Emulsion 56.07 Marasperse CBOS-4 (dispersant for carbon black) 0.75 Raven 420 (carbon black) 18.69 2-Mercaptoethanol (chain stopper) 0.07 Water 17.88 Cure Paste 6.54 The coating is prepared in the manner of the Sealant of Example 1. The physical properties of the coating are as follows: Physical Properties Hardness 66 (Shore A) Tensile 3241 kPa (470 psi) 100% modulus 1372 kPa (199 psi) 200% modulus 1862 kPa (270 psi) 300% modulus 2275 kPa (330 psi) Ultimate Elongation 540% An advantage of the emulsion/dispersions of the present invention is that they can be thinned with water. This is particulary important for spray applications where the viscosity must be reduced sufficiently for the compositions to pass through applicator nozzles. Previously, compositions containing liquid polysulfides and oxidatives curative particulates were thinned with organic solvents.

Claims: A stable mixed aqueous emulsion and aqueous dispersion comprising: (a) water as the continuous aqueous phase, (b) liquid polysulfide emulsified with surfactant within said continuous aqueous phase and (c) particulates of an oxidative curative for said polysulfide separately dispersed with surfactant in said continuous aqueous phase, wherein the content of said liquid polysulfide is from 50 to 70 wt. percent, the content of said oxidative curative is from 5 to 10 wt. percent, the content of said surfactant(s) is from 3 to 7 wt. percent and the water content is at least 20 wt. percent, said percentages being based upon the total weight of polysulfide, oxidative curative surfactant(s) and water, and wherein the surfactant in which said polysulfide is emulsified has a hydrophile/lipophile balance of 18 to 20 as determined by the HLB system described in a publication entitled THE HLB SYSTEM of ICI Americas Inc., Wilmington, Delaware 19897, 1984. A mixed emulsion and dispersion according to claim 1 wherein the surfactant in which said liquid polysulfide is emulsified is a block copolymer having more hydrophilic blocks flanking a more hydrophobic block. A mixed emulsion and dispersion according to claim 2 wherein said surfactant in which said liquid polysulfide is emulsified comprises polyethylene oxide blocks flanking a polypropylene oxide block. A mixed emulsion and dispersion according to any preceding claim wherein said emulsified liquid polysulfide contains a hydrophobic plasticizer. A mixed emulsion and dispersion according to any preceding claim containing inorganic fillers to thicken it. A mixed emulsion and dispersion according to any preceding claim wherein the surfactant used to emulsify said particulates of oxidative curative comprises a straight hydrocarbon chain and a hydrophilic end moiety. A method of preparing a stable mixed aqueous emulsion and aqueous dispersion according to any preceding claim, the method comprising: mixing liquid polysulfide, water and a surfactant having a hydrophile/lipophile balance of between 18 and 20, as determined by the HLB System described in a publication entitled THE HLB SYSTEM of ICI Americas Inc., Wilmington, Delaware 19897, 1984, with shear sufficiently high to produce an emulsion of he polysulfide in water, mixing oxidative curative particulates, water and a surfactant with shear sufficiently high to produce a dispersion of the oxidative curative particulates in water, and blending said liquid polysulfide emulsion with said oxidative curative dispersion with sufficiently low shear to maintain both the liquid polysulfide emulsion and dispersed oxidative curative particulates out of chemical contact with each other.

Inventors: ANDERSON PAUL H, ANDERSON, PAUL H.
Applicants: MORTON INT INC, MORTON INTERNATIONAL, INC.
Application year: 1991
Main classification: C08J3
IPC codes: C09K3, B01J13, C08J3, C08G75, C08L81