Oxide superconductor and its manufacturing method

Abstract: An oxide superconductor which has a composition expressed by the following general formula and whose crystal structure is 1222-phase structure. Pb a (M 1-x-y Ce x Sr y )₄Cu 3-a O z (I) (where M represents at least one element selected from the group consisting of Y, La, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Yb, and Lu, and a, x, y, and z denote the numbers which satisfy 0.3 ≦ a ≦ 0.7, 0 < x ≦ 0.25, 0.3 ≦ y < 0.5, 8.5 ≦ z ≦ 9.5, respectively). A Pb-based Cu oxide superconductor manufacturing method comprising the steps of mixing powders of raw materials containing at least Pb, Sr, Ce, M (where M represents at least one element selected from the group consisting of Y, La, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Yb, and Lu groups) and Cu in the proportion to have the composition shown in the general formula (I) above, optionally forming the mixed powder into a shape body, and firing the obtained powder mixture or the shape body in the temperature range of 900 - 1150°C in the oxidizing atmosphere.

Description: The present invention relates to an oxide superconductor having a novel composition and its manufacturing method. As oxide superconductors containing Pb and Cu (hereinafter called "Pb-based Cu oxide superconductor"), Pb₂Sr₂(Ca,Y)Cu₃O₈ with 2213 crystal structure (see R. J. Cava et al., Nature 336, pp 211, 1988), Pb₂(Sr,La)₂Cu₂O₆ with 2202 crystal structure (see H. W. Zandbergen et al., Physica C 159, pp 81, 1989), (Pb,Sr)Sr₂(Y,Ca)Cu₂O₇ (see T. Rouillon et al., Physica C 159, pp 201, 1989) or (Pb,Cu)(Sr,Ba)₂(Y,Ca)Cu₂O₇ (see S. Koriyama et al., Physica C 166, pp 413, 1990), both with 1212 crystal structure, PbSrBa(Y,Ca)Cu₃O₈ with 1213 crystal structure (see A. Tokiwa et al., Physica C 161, pp 459, 1989), (Pb,Cu)(Sr,La)₂CuO₅ with 1201 crystal structure (see S. Adachi et al., Jpn. J Appl. Phys. 29 pp. ℓ890, 1990) have been known. Because in these superconductors, the oxygen content in its composition is nonstoichiometric (unable to be reduced to simple integer ratio), the numbers denoting oxygen content in the above-mentioned compositional formulae indicate the ideal value. In actuality, it is assumed that the oxygen content deviates slightly from the above numbers. Of the Pb-based Cu oxide superconductors of above-mentioned composition, those containing Y are known to exhibit superconductivity characteristics even if other rare earth elements are used in place of Y. Now when superconducting materials are used in various sensors and devices, various characteristics are required according to respective applications. For example, they must have suitable critical temperatures, must be easy to be synthesized, must have the precise structure, or must be easy to handle. Investigating the above-mentioned Pb-based Cu oxide superconductors in respect to these viewpoints, synthesis of say 2213-crystal structure, 2202-crystal structure, and 1213-crystal structure Pb-based Cu oxide superconductors is carried out by firing material powders, a mixture of oxides, carbonates and so on, in reducing atmospheres. During firing the material powders, pinpoint control of oxygen partial pressure in the atmosphere is essential and furthermore, rapid cooling is required after firing, and therefore, such Pb-based Cu oxide superconductors are not always synthesized easily. Of the 1212-crystal structures, those comprising (Pb 0.5 Sr 0.5 ) Sr₂(Y,Ca)Cu₂O₇ must have their synthesis carried out in the vacuum atmosphere. In this way, Pb-based Cu oxide superconductors of 2213 crystal, 2202 crystal, 1213 crystal, and 1212 crystal structures with the aforementioned composition are not always easy to be synthesized. Furthermore, synthesis of Pb-based Cu oxide superconductors with above-mentioned structures is carried out in either reducing or vacuum atmosphere as described above. In general, the melting point of oxides lowers in such atmosphere. Consequently, firing temperature must be lower than that in the oxidizing atmospheres, producing a problem that Pb-based Cu oxide superconductors obtained are difficult to be densified. Of Pb-based Cu oxide superconductors of 1201-crystal structure and 1212-crystal structure, those comprising (Pb,Cu)(Sr,Ba)₂(Y,Ca)Cu₂O₇ can be synthesized in an oxidizing atmosphere and the problem as mentioned above would not occur. However, Pb-based Cu oxide superconductors of this composition contain a high content of Pb, harmful element, requiring careful handling of the whole. This constitutes a disadvantage as practical Pb-based Cu oxide superconductors. The object of this invention is to provide a new Pb-based Cu oxide superconductor and its manufacturing method, which can solve the above-mentioned problems related to Pb-based Cu oxide superconductors, which does not need special controls for the baking temperature and any rapid cooling process, which can be easily and finely synthesized in the suitable oxidizing atmosphere, and which contains only a small amount of Pb. Now, the 1222-crystal structure contains a structure unit known as a fluorite layer. And of copper oxides containing this fluorite layer, those such as (Nd,Ce)₂(Nd,Ba)₂Cu₃O₉, which exhibits superconductivity, exist (see H. Sawa et al., J. Phys. Soc. Japan, 58, pp 2252, 1989). The inventors of the present invention had an eye on the fact that many of the Cu oxide superconductors containing this fluorite layer contain Ce and can be synthesized to Pb-based Cu oxide superconductors in the oxidizing atmosphere similarly to the (Pb,Cu)(Sr,Ba)₂(Y,Ca)Cu₂O₇, and that the Pb-based Cu oxide superconductors of 1222-crystal structure is expected to contain less Pb than aforementioned conventional Pb-based Cu oxide superconductors with 1212-crystal structure, and have succeeded in developing the Pb-based Cu oxide superconductor of the present invention. That is, the present invention provides oxide superconductors having the composition expressed by the following formula: Pb a (M 1-x-y Ce x Sr y )₄Cu 3-a O z (where M represents at least one element selected from the group consisting of Y, La, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Yb, and Lu, and a, x, y, and z denote the numbers which satisfy 0.3 ≦ a ≦ 0.7, 0 < x ≦ 0.25, 0.3 ≦ y < 0.5, 8.5 ≦ z ≦ 9.5, respectively) and the crystal structure is of 1222 crystal structure. In the present invention, a Pb-based Cu oxide superconductor manufacturing method comprising the steps of mixing powders of raw materials containing at least Pb, Sr, Ce, M (where M represents at least one element selected from the group consisting of Y, La, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Yb, and Lu) and Cu in the proportion to have the above-mentioned composition, optionally forming the mixed powder of raw materials into a shape body and firing the obtained powder mixture or the shape body in the temperature range of 900 - 1150°C in the oxidizing atmosphere. The oxide superconductors of the present invention are Pb-based Cu oxide superconductors which possess the above-mentioned composition and whose crystal structure is 1222-phase. This invention can be more fully understood from the following detailed description when taken in conjunction with the accompanying drawings, in which: Fig. 1 is a schematic diagram showing a crystal structure of Pb-based Cu oxide superconductors of the present invention; Fig. 2 is a graph showing the temperature dependency of electric resistivity in Embodiment 1; Fig. 3 is a graph showing the temperature dependency of d.c. magnetic susceptibility in Embodiment 1; Fig. 4 is a graph showing an X-ray diffraction pattern in Embodiment 1; and Fig. 5 is a graph showing the temperature dependency of electric resistivity in Embodiment 32. Fig. 1 shows an example of the crystal structure of Pb-based Cu oxide superconductor of the present invention when M in the above composition is Eu. The crystal structure of this case is a tetragonal crystal of the lattice constant a of about 3.8Å and c of about 29Å which is known as a material of TlBa₂(M,Ce)₂Cu₂O₈ (where M is the same as above) and Pb-Pr-Sr-Cu-O systems (for the Tl system, see S. Martin et al., Mcd. Phys. Lett. B3, pp 993, 1989 and for the Pb system, see S. Adachi et al., Physica C 168, pp 1, 1990). However, these are not superconducting materials. In Pb-based Cu oxide superconductors of the present invention, because when the character a is smaller than 0.3 or larger than 0.7, impurity phases such as the 1212 phase are generated in the crystal structure in addition to the 1222 phase and this generation degrades superconducting characteristics, the value a must be restricted to the range of 0.3 - 0.7. Character x indicating the Ce content is also restricted to the range of 0 < x ≦ 0.25. Deviating from this range, Pb-based Cu oxide superconductors of the 1222-phase structure cannot be obtained. Character y indicating the Sr content is also restricted to the range of 0.3 ≦ y < 0.5. Deviating from this range, Pb-based Cu oxide superconductors of the 1222-crystal structure cannot be obtained as with the case of character x. The oxygen content z varies according to firing conditions and cooling conditions later discussed but must be the amount that allows the obtained synthesized substance to be an oxide superconductor. Specifically, it is restricted to the range of 8.5 ≦ z ≦ 9.5. This is because deviation of z from this range degrades the superconducting properties. The Pb-based Cu oxide superconductor of the present invention can be synthesized as follows. At first, powders of raw materials containing Pb, Ce, Sr, Cu, and M are thoroughly mixed. Examples for raw materials used in this event include oxides containing the elements described above, carbonate, nitrate, oxalate, hydroxide etc. The mixture ratio of each materials is decided in such a way that the above-mentioned metallic elements contained in the materials constitute the composition of Pb a (M 1-x-y Ce x Sr y )₄Cu 3-a after synthesis. According to the present invention, the obtained powder mixture of raw material is calcined at 800 to 900°C in the oxidizing atmosphere. After the calcined powder is formed into the desired shape by a molding method such as a press molding, an injection molding, an extrusion molding and a sheet molding, the shape body is fired. Then, the obtained calcined powder or the shape body is fired in the oxidizing atmosphere. In the oxidizing atmosphere, the oxygen partial pressure need not specially be controlled as required conventionally and the applied atmosphere may be, say, ambient air or 100% oxygen gas atmosphere. Baking temperature is set to the temperature range from 900 - 1150°C. When the firing temperature is lower than 900°C, 1222-crystal structure generating reactions do not take place satisfactorily and synthesis of Pb-based Cu oxide superconductors of the above-mentioned composition and fine structure does not progress. When the firing temperature is higher than 1150°C, evaporation of Pb proceeds and impurity phases other than 1222 crystal structure begin to form accordingly. In the temperature range mentioned above, reactions to generate the Pb-based 1222-crystal structure take place while undergoing the partial melting state. For this reason, firing at the above-mentioned temperature range causes the reactions to generate the Pb-based 1222-crystal structure to take place rapidly, and as a result, Pb-based Cu oxide superconductors with 1222-crystal structure of the present invention are synthesized in an extremely short time. Preferable baking temperature is 1000 - 1080°C. Excessively long firing time accelerates evaporation of Pb, resulting in deterioration of superconducting characteristics due to generation of impurity phases. Excessively short firing time results in insufficient generation of the 1222-crystal structure which proceeds in the partial melting state. It is, therefore, desirable to set the firing time to the range of 0.5 - 5 hours at the above-mentioned temperatures. Upon completion of firing, the synthesized substance is cooled to obtain Pb-based Cu oxide superconductors of the present invention. The desirable cooling rate for this event is 10°C/min or higher to the temperature just below the partial melting temperature (about 900°C). Slower cooling rate than this increases the Pb evaporation rate. From the temperature just below the partial melting temperature to about 300°C, the cooling rate of 5°C/min or lower is desirable. A cooling rate higher than this results in insufficient take-in of oxygen during cooling, which is essential for occurrence of superconducting characteristics. EXAMPLE 1 - 11, COMPARE EXAMPLE 1 - 11 Powders of PbO, CeO₂, Eu₂O₃, SrCO₃, and CuO (purity: all 99.9% or higher) were thoroughly mixed to have the composition shown in Table 1. Each powder mixture obtained is calcined for 10 hours in the 850°C air to form into compacts having desired shape. The compacts were fired under the conditions mentioned in Table 1 and finally the fired compacts were cooled at a rate of 1°C/min. For each sample obtained, the generated phase was confirmed by the X-ray diffraction method and electric resistivity was measured by the four-probe method to investigate superconducting characteristics. Table 1 summarizes the above results. For the superconductor compacts of Embodiment 1, temperature dependency of electric resistivity and d.c. magnetic susceptibility were investigated and the results are shown in Figs. 2 and 3. As clear from Fig. 2, the oxide superconductor of the present invention begins decreasing electric resistivity from 25K and attains zero at 12K by superconducting transition. As clear from Fig. 3, magnetic susceptibility becomes negative at 25K or lower for the Meissner effect due to superconductivity. Fig. 4 shows an X-ray (CuKα) diffraction pattern of the oxide superconductor of Embodiment 1. As clear from Fig. 4, this oxide superconductor is a tetragonal crystal with the lattice constant a of about 3.8Å and c of about 29.6Å, and all the diffraction peaks can be characterized. It forms, as a whole, a single phase of 1222 crystal structure. EXAMPLE 12 - 28 As shown in Table 2, various oxide superconductors were synthesized in the manner similar to Embodiment 1 except a change of the type of element M. All oxide superconductors obtained were extremely densified. Table 2 shows the generated phases and superconducting characteristics together. EXAMPLE 29 - 31 The same powder mixture as that of Embodiment 1 was fired under the same conditions and the fired compacts obtained were cooled to 850°C, 800°C, and 700°C, respectively, in 10 minutes, then cooled to room temperature at a rate of 1°C/min and three types of oxide superconductor compacts of varying cooling conditions were fabricated. These three types of oxide superconductor compacts all had the 1222-crystal structure and the Tc (onset) is all 28K, exhibiting characteristics superior to oxide superconductors of Embodiment 1. EXAMPLE 32 Oxide superconductor compacts of Embodiment 1 were held at 800°C for 1 hour in the 10⁵ Pa (1 atm.) oxidizing atmosphere and cooled to room temperature at a rate of 1°C/min. In the cooling process, oxide superconductor compacts were held at 600°C, 500°C, 400°C, and 300°C for 10 hours, respectively. Temperature dependency of electric resistivity was measured on heat-treated superconductor compacts obtained, and the results are shown in Fig. 5. As shown in Fig. 5, lowering of electric resistivity due to superconducting transition was recognized at 30K or lower, and the characteristics are improved from those of Embodiment 1. According to the X-ray diffraction, the crystal structure of the heat treated superconductor compacts is the 1222-crystal structure and change of crystal structure due to heat treatment was not recognized. As clear from the above description, the oxide superconductor of the present invention is a new Pb-based Cu oxide superconductor with the 1222-crystal structure, which has superconducting transition temperature of 20 - 30K and whose structure is extremely densified, and is very easy to handle because the Pb content is low. Because this oxide superconductor contains Pb, it provides excellent workability as compared to other oxide superconductors and can be used for new material for sensors and devices. With the manufacturing method of the present invention, synthesis is carried out in the oxidizing atmosphere and firing temperature can be increased, and as a result, oxide superconductors with high density structure can be synthesized easily and at low cost.

Claims: An oxide superconductor which has a composition expressed by the following general formula and whose crystal structure is 1222-crystal structure Pb a (M 1-x-y Ce x Sr y )₄Cu 3-a O z (I) (where M represents at least one element selected from the group consisting of Y, La, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Yb, and Lu, and a, x, y, and z denote the numerals which satisfy 0.3 ≦ a ≦ 0.7, 0 < x ≦ 0.25, 0.3 ≦ y < 0.5, 8.5 ≦ z ≦ 9.5, respectively). A method for manufacturing a Pb-based Cu oxide superconductor, characterized by comprising the steps of mixing powders of raw material containing Pb, Sr, Ce, M (where M represents at least one element selected from the group consisting of Y, La, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Yb, and Lu) and Cu in the proportion to have the composition shown in the general formula (I) below, forming the mixed powder into a shape body, and firing the shape body in the temperature range of 900 - 1150°C in the oxidizing atmosphere Pb a (M 1-x-y Ce x Sr y )₄Cu 3-a O z (I) (where M represents at least one element selected from the group consisting of Y, La, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Yb, and Lu, and a, x, y, and z denote the numbers which satisfy 0.3 ≦ a ≦ 0.7, 0 < x ≦ 0.25, 0.3 ≦ y < 0.5, 8.5 ≦ z ≦ 9.5, respectively). A method for manufacturing a Pb-based Cu oxide superconductor, characterized by comprising the steps of mixing powders of raw material containing Pb, Sr, Ce, M (where M represents at least one element selected from the group consisting of Y, La, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Yb, and Lu) and Cu in the proportion to have the composition shown in the general formula (I) below, and firing the mixed powder in the temperature range of 900 - 1150°C in the oxidizing atmosphere Pb a (M 1-x-y Ce x Sr y )₄Cu 3-a O z (I) (where M represents at least one element selected from the group consisting of Y, La, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Yb, and Lu, and a, x, y, and z denote the numbers which satisfy 0.3 ≦ a ≦ 0.7, 0 < x ≦ 0.25, 0.3 ≦ y < 0.5, 8.5 ≦ z ≦ 9.5, respectively). A method according to claim 2 characterized in that the raw materials are compounds selected from the group consisting of oxides, carbonates, nitrates, oxalates, and hydroxides containing the elements described in the general formula (I). A method according to claim 2 characterized in that the oxidizing atmosphere is environmental air. A method according to claim 2 characterized in that the oxidizing atmosphere is that of which oxygen partial pressure is higher than 5 x 10³ Pa (0.05 atm.) A method according to claim 2 characterized in that firing temperature is 1000 - 1080°C. A method according to claim 2 characterized in that firing is carried out for 0.5 - 5 hours. A method according to claim 2 characterized in that the mixed powder or its compact after firing is cooled to temperature just below the partial melting temperature of this powder mixture or its compact at a rate of 10°C/min or higher. A method according to claim 7 characterized in that the powder mixture or its compact after firing is cooled from temperature just below the partial melting temperature to about 300°C at a rate of 5°C/min or lower.

Inventors: ICHINOSE ATARU C O CENTRAL RES, KORIYAMA SHIN-ICHI, MAEDA TOSHIHIKO, SAKUYAMA KAZUHIRO, TANAKA SHOJI, YAMAUCHI HISAO, ICHINOSE, ATARU, C/O CENTRAL RESEARCH INSTITUTE, KORIYAMA, SHIN-ICHI, MAEDA, TOSHIHIKO, SAKUYAMA, KAZUHIRO, TANAKA, SHOJI, YAMAUCHI, HISAO
Applicants: CENTRAL RES INST ELECT, FURUKAWA ELECTRIC CO LTD, INT SUPERCONDUCTIVITY TECH, KYOCERA CORP, TOHOKU ELECTRIC POWER CO, CENTRAL RESEARCH INSTITUTE OF ELECTRIC POWER INDUSTRY, INTERNATIONAL SUPERCONDUCTIVITY TECHNOLOGY CENTER, KYOCERA CORPORATION, THE FURUKAWA ELECTRIC CO., LTD., THE TOHOKU ELECTRIC POWER CO., INC.
Application year: 1991
Main classification: C01G3
IPC codes: C01G3, C01G21, C04B35, C01G1, H01B12, H01L39