Ceramic composition

Abstract: An improved ceramic composite material is provided based on zirconia and boron nitride that can be satisfactorily bonded without sintering. The material comprises a particulate mixture of boron nitride, stabilised zirconia and silicon nitride bonded together by whiskers of silicon nitride. The silicon nitride whiskers may conveniently be formed in-situ by heating the mixture of particulate boron nitride, stabilised zirconia and silicon nitride together with powdered metallic silicon in an atmosphere of nitrogen.

Description: This invention relates to a novel ceramic composition and to a method of making it. It is known to use various compositions based on zirconia and boron nitride as formed shapes for various purposes to utilise the ceramic, heat-resistant properties of these materials. However, such compositions normally require a powdered mixture of the ingredients to be sintered after shaping to the desired form in order to achieve the necessary binding together of the individual particles of the mixture that is required if they are to be considered for end uses such as liners for furnace tap holes and breaker rings in horizontal casting units. USP 4540674 discloses a silicon nitride composite refractory material having improved thermal shock characteristics and molten steel resistance which consists of silicon nitride at 20 to 60% by weight, refractory material at 10 to 50% by weight and boron nitride at 1 to 20% by weight. The composite has silicon nitride bonds as bonding structures. This can be achieved by blending and moulding a mixture of silicon, refractory materials, boron nitride and a binder and then heating the moulded product at 1200°C to 1500°C in an atmosphere of nitrogen or ammonia. The present invention aims to provide a further improved composite refractory of this type, i.e. one that is satisfactorily bonded without sintering. Accordingly, in a first aspect, the invention provides a composite ceramic refractory material comprising a particulate mixture of boron nitride, stabilised zirconia and silicon nitride bonded together by whiskers of silicon nitride. The whiskers of silicon nitride are conveniently formed in-situ by heating the mixture of particulate boron nitride and stabilised zirconia, which additionally contains powdered metallic silicon, in an atmosphere of nitrogen. Accordingly, in a second aspect the invention provides a method of making a bonded ceramic composite in which a particulate mixture is formed of boron nitride, stabilised zirconia, silicon nitride and silicon, the mixture is formed to the desired shape and is then heated in an atmosphere of nitrogen. The heating is preferably carried out at between 1000 and 1500°C especially 1200°to 1400°C, which is substantially lower than the temperatures that would be required to effect adequate sintering of the constituents of the mixture. The mixture of particulates will normally require to be held together by temporary organic binders, e.g. dextrin or an acrylic binder, during the shaping stage. Such binders, which are well known in the art, are driven off during the firing stage and their role is taken over in the present invention by the reaction of the metallic silicon with the nitrogen which form fibres or whiskers of silicon nitride which bond the particulates of the mixture together. The incorporation of stabilised zirconia and, particularly, silicon nitride in particulate form, i.e. in addition to the in-situ formed bonding form of silicon nitride, has been found to be particularly advantageous. Although not wishing to be limited by any particular theory, it is believed that the silicon nitride particulate material not only enhances erosion resistance in its own right, but it is preferentially attacked by oxygen and thereby protects the boron nitride from oxygen-degradation. Oxygen reacts with the particulate silicon nitride to form a stable silicon-oxynitride coating, thereby enhancing further the stability and integrity of the product. In one embodiment of the method of the invention, the particulate materials are mixed with the temporary binder or binders and a slurry of the resulting composition is formed. The slurry is then slip-cast to the desired shape of the final article, the cast shape is dried and then fired under an atmosphere of nitrogen. The firing stage is preferably carried out under moderate pressure, e.g. 2 to 3 p.s.i. (10 to 20 kPa). In another embodiment of the method, the particulate materials are mixed with the temporary binder or binders and the resulting composition is uni-axially or isostatically pressed, preferably at ambient temperature, to the desired shape. The pressed shape is then fired in an atmosphere of nitrogen as for the above-described slip-cast shape. The stabilised zirconia may be partially stabilised or fully stabilised. Such zirconias are well known per se in the art and may be stabilised, for example, with yttria or magnesia or other rare earth metallic oxides. The proportions of the mixture may vary fairly widely but preferably contain from 10 to 30 parts by weight of boron nitride, 20 to 40 parts by weight of stabilised zirconia, 5 to 25 parts by weight of silicon nitride and 15 to 30 parts by weight of silicon metal. The particulate sizes of the constituents may be, for example: boron nitride sub 2 microns stabilised zirconia sub 2 microns silicon nitride sub 53 microns silicon sub 53 microns Typically, the finished, fired products may have a porosity from 15 to 40%. The bonded products of the invention have excellent thermal shock resistance and can, for example, readily accommodate a rapid temperature change of more than 1200°C. They have high thermal conductivity and low thermal expansion and are non-wetting to liquid metals. They exhibit little or no shrinkage on firing unlike conventional ceramic materials which may shrink up to as much as 20%. They are, therefore, eminently suitable for applications such as the above-mentioned liners for furnace tap holes and breaker rings for horizontal casting units and for a variety of other components in continuous casting equipment, crucibles and the like. The silicon nitride bond that is formed together with the enhancement of properties due to the particulate silicon nitride give the products excellent strength and integrity and the overall properties of the finished material provide excellent erosion resistance to molten metals, e.g. molten steel. The invention is further illustrated in the following Example. EXAMPLE A mixture of the following proportions by weight was made: % by weight Size boron nitride 22.5 sub 0.5 micron yttria-stabilised zirconia (11% yttria) 35.0 sub 2 micron silicon nitride 17.5 sub 53 micron (300 mesh) silicon 25.0 sub 53 micron (300 mesh) The mixture was then further thoroughly mixed with 1.0% by weight of dextrin binder and was uni-axially pressed into the form of a tap hole liner at a pressure of 750 kgs/cm² and fired under an atmosphere of nitrogen at a temperature from 1200°C to 1400°C for 60 to 100 hours. The liner so formed was of 130 mm outside diameter, 75 mm inside diameter and had a height of 150 mm. The liner was set into a small tundish and after pre-heating a charge of molten steel (300 kgm) with typical BOF composition (0.1% Si; 0.3%, Mn, 0.05%C and traces of S & P) at a measured temperature of 1650°C was poured through the liner. The process was repeated continuously - with a 15 minute pause to raise the steel temperature to 1650°C. During the re-heating cycle the temperature of the lining material was allowed to fall to 600°C - 700°C - before being subjected to an instantaneous temperature step of 1000°C up to 1650°C. The material was subjected to the thermal shocks of 11 such cycles without exhibiting any physical or mechanical deterioration. At the completion of the trial the examination of the internal bore of the liner showed no change in dimensions, the non-wetting character of the ceramic having prevented sticking of either the molten steel or slag to the surface. Subsequent examination of the body of the material via scanning electron microscope showed that contamination of the ceramic bore was limited to a depth of 200 microns. The example clearly shows the ability of the ceramic material in respect of: resistance to erosion by hot molten metal, a high resistance to thermal shock of 1000C°+, the non-wetting properties of the ceramic to both molten metal and molten slag.

Claims: A composite ceramic refractory material comprising boron nitride characterised in that it is formed from a particulate mixture of boron nitride, stabilised zirconia and silicon nitride bonded together by whiskers of silicon nitride. A composite ceramic refractory material according to Claim 1, characterised in that the mixture contains from 10 to 30 parts by weight of boron nitride. A composite ceramic refractory material according to Claim 1 or 2, characterised in that the mixture contains from 20 to 40 parts by weight of stabilised zirconia. A composite ceramic refractory material according to Claim 1, 2, or 3, characterised in that the mixture contains 5 to 25 parts by weight of silicon nitride. A composite ceramic refractory material according to any one of the preceding claims, characterised in that the whiskers of silicon nitride are formed from the incorporation of silicon metal in the mixture. A composite ceramic refractory material according to Claim 5, characterised in that the mixture contains 15 to 30 parts by weight of silicon metal. A composite ceramic refractory material according to any one of the preceding claims characterised in that the boron nitride and stabilised zirconia particles in the mixture are less than 2 microns size. A composite ceramic refractory material according to any one of the preceding claims, characterised in that the silicon nitride particles in the mixture are less than 53 microns size. A furnace tap hole liner or a breaker ring for a horizontal casting unit formed from a composite ceramic refractory material according to any one of the preceding claims. A method of making a bonded ceramic composite material comprising firing a shaped mixture containing particulate boron nitride, characterised in that a particulate mixture is made of boron nitride, stabilised zirconia, silicon nitride and silicon and is fired in an atmosphere of nitrogen. A method according to Claim 10, characterised in that the firing is carried out between 1000° and 1500°C. A method according to Claim 10 or 11, characterised in that the mixture of particulates is held together during the shaping stage by a temporary binder which is driven off during the firing stage. A method according to Claim 10, 11 or 12, characterised in that the particulate materials are mixed with a temporary binder, a slurry of the resulting composition is formed and the slurry is slip cast to the desired shape prior to firing. A method according to any one of Claims 10 to 13, characterised in that the firing is carried out under a pressure of 10 to 20 kpa. A method according to Claim 10, 11 or 12, characterised in that the particulate materials are mixed with a temporary binder and the resulting composition is uni-axially or isostatically pressed at ambient temperature to the desired shape prior to firing.

Inventors: JUMA KASSIM, ROBERTSON JOHN, JUMA, KASSIM, ROBERTSON, JOHN
Applicants: FOSECO INT, FOSECO INTERNATIONAL LIMITED
Application year: 1991
Main classification: C04B35
IPC codes: C04B35