SILICAS

Abstract: Amorphous precipitated silicas suitable for use in transparent toothpastes having surface area in the range 250 to 600 m<2>/g, an oil absorption of 90 to 160 cm<3>/100 g, a perspex abrasion value from 8 to 15, a mean pore diameter from 1.5 to 21 nm, a transmission of at least 70 % within the refractive index range of 1.435 and 1.456, and a weight mean particle size from 5 to 20 micron.

Description: SILICAS Field of the invention This invention relates to synthetic precipitated silicas of use, for example, as abrasive agents in toothpaste compositions. Background to the invention Toothpaste compositions are well characterised in the literature and many compositions are disclosed in patent specifications and other literature. Toothpaste compositions contain a number of specific components for example abrasive agents, fluoride sources, binders, preservatives, humectants, anti plaque agents, colouring agents, water, flavour and other optional ingredients. Of these components the abrasive agent is required to provide the appropriate cleaning and plaque removal without subjecting the tooth itself to excessive abrasion. Typically a toothpaste composition will contain from about 5% to about 50%, preferably up to about 30%, by weight of abrasive. Commonly used abrasives are aluminas, calcium carbonates and calcium phosphates. SUBSTITUTE SHEET More recently synthetic silicas have been adopted because of their efficient cleaning, compatibility with other ingredients and their physical properties. Increasingly the sources of fluoride, e.g. sodium fluoride and stannous fluoride, are more sensitive to the presence of trace amounts of cations, e.g. calcium and magnesium, which are commonly found in silicas due to their processing. An important property of a silica for use in transparent toothpaste formulations is refractive index, and it has been shown this property can be controlled by careful selection of process conditions in the preparation of the silica. General description of the invention The amorphous precipitated silicas of the invention have a structure defined by physical characteristics which allow the silicas to be used in transparent toothpastes with a considerable degree of formulation flexibility and provide a medium degree of abrasivity and optionally relatively small degree of thickening even at high, i.e. 20% w/w, loadings. However silicas of the invention with 3 higher oil absorptions, i.e. 140 to 160 cm /100g, illustrated by Example 8, are able to provide thickening of the composition at high loadings. This may allow a thickening agent, e.g. a silica, to be used at a reduced level in the composition. The silicas can be prepared with low levels of cations, e.g. calcium, magnesium and aluminium, by washing the filter cake with de-ionised water such that the dry product subsequently gives extra stability when formulated in to a toothpaste containing fluoride ions. SUBSTITUTE SHEET The invention provides an amorphous precipitated silica having i) a surface area in the range from about 250, preferably from about 300, more preferably from about 350, to about 600m 2 /g, preferably not more than about 550m 2 /g, ii) an oil absorption (using linseed oil) of about 90, preferably from about 110, to about 160 cm 3/100g, preferably not more than about 140 cm3/100g iii) a weight mean particle size.in the range 5 microns to 20 microns, preferably up to about 15 microns, iv) a plastic abrasion value (PAV) in the range from about 8 to about 15, preferably at least about 10, v) a transmission of at least 70%, preferably at least 80%, within the refractive index range of 1.435 to 1.456 and vi) a mean pore diameter in the range from about 1.5 nm, preferably from about 3, to about 21nm, preferably to about lOnm, more preferably to about 9nm. The applicants have measured the Radioactive Dentine Abrasion (RDA) values of a number of silicas (15) having PAVs in the range 7.5 to 31 and have found a correlation coefficient of 0.91 (confidence 99%). PAVs of 8 and 15 correspond to mean RDAs of 55 and 109. The silicas of the invention usually have a phase of alpha-cristobalite after firing at 1100°C. The precipitated silicas of the invention are capable of providing satisfactory abrasion even at relatively low particle sizes i.e. 5 to 10 micron range. Abrasive materials can also be obtained at particle sizes beyond the stated upper limit but they are not suitable for use in toothpastes because of the unacceptable mouth feel of the coarser particles. SUBSTSTUTE SHE T In general, characterisation of the pore structure of silicas containing higher levels of openness and wider pores by nitrogen adsorption techniques is not meaningful because this technique is useful only for pores up to about 60 nm diameter. To measure the full range of porosity present in such materials it is necessary to employ alternative procedures, for example oil absorption or mercury porosimetry. Since the products of this invention have some pore structure in excess of 60 nm it is necessary to define them by means of such techniques. In the Examples of the invention the silicas having 70% transmission in the RI range 1.435 to 1.444 have a mercury intrusion volume above 0.5 cm 3/100g, while those having 70% transmission in the 1.445 to 1.456 range have mercury intrusion volumes below 0.5 cm 3/100g. Literature EPA 0227334 (Unilever) describes precipitated silicas having high absorbency, i.e. 110 to 180 cm 3/100g but the silicas of the present invention have enhanced clarity which allows their use in transparent toothpaste compositions. Compared With the silicas described in EPA 0308165 (Unilever) the present silicas have lower abrasivity which allow their use at higher loadings in toothpaste formulations on a more flexible basis. These silicas are defined as having plastic abrasion values down to 15 with mean pore diameters in the range 3 to 8nm. Silicas of the present invention have MPDs in the range 1.5 to 3nm when the PAV is above 14. SUBSTITUTESHEET The use of Neosyl(R), a precipitated silica obtainable from Crosfield Chemicals of arrington, England, is described in US 3864470 (Lever Bros Company) . Neosyl, which is a mild polishing agent, would give excessive thickening, because of its higher structure, at the levels required to provide satisfactory cleaning. The present silicas can be formulated into toothpaste compositions having a lower refractive index, i.e. 1.435 to 1.456, compared with the silicas described in GB 2146317 (Taki) . These lower refractive index compositions are more economical to prepare since they have a higher water content in the formulation and therefore a corresponding lower amount of humectant e.g. Sorbitol, which is a more expensive component of the toothpaste formulation. The applicants have found these Taki silicas have plastic abrasion values and oil absorptions outside the ranges claimed in the present application. Standard Procedures The silicas of the invention are defined in terms of their physical and chemical properties. The standard test methods used to determine these properties are:- i) Surface Area: Surface area is determined by standard nitrogen adsorption methods of Brunauer, Emmett and Teller (BET) using a single point method with a Sorpty 1750 apparatus supplied by Carlo Erba company of Italy. The sample was outgassed under vacuum at 270°C for 1 hour before measurement. SUBSTITUTE SHEET ii) Oil Absorption: The oil absorption is determined by the ASTM spatula rub-out method (American Society of Test Material Standards D, 281) . The test is based upon the principle of mixing linseed oil with a silica by rubbing with a spatula on a smooth surface until a stiff putty-like paste is formed which will not break or separate when it is cut with the spatula. The volume of oil used is then put into the following equation:- Oil absorption = cm 3 o l absorption x 100 wt. of silica sample in gms *•** ■ cm 3 oi.l/lOOg si.li.ca iii) Weight Mean Particle Size: The weight mean particle size of the silicas was determined with the aid of a Malvern Particlesizer, Model 3600 E. This instrument, made by Malvern Instruments, Malvern, Worcestershire uses the principle of Fraunhβffer diffraction utilising a low power He/Ne laser. Before measurement the sample was dispersed ultrasonically in water for a period of 7 minutes to form an aqueous suspension. iv) Plastics Abrasion Value (PAV) : This test is based upon a toothbrush head brushing a Perspex plate in contact with a suspension of the silica in a sorbitol/glycerol mixture. Normally the slurry composition is as follows: SUBSTITUTE SHEET Silica 2.5 grams Glycerol 10.0 grams Sorbitol 23.0 grams All components are weighed into a beaker and dispersed for 2 minutes at 1500 rpm using a simple stirrer. A 110mm x 55mm x 3mm sheet of standard clear Perspex is used for the test, supplied by Imperial Chemical Industries PLC of England under code 000. The test is carried out using a modified Wet Paint Scrub Tester produced by Research Equipment Limited, Wellington Road, Hampton*Hill, Middlesex. The modification is to change the holder so that a toothbrush can be used instead of a paint brush. In addition a weight of 14 ozs (398g) is attached to the brush to force the brush onto the perspex plate. A Galvanometer is calibrated using a 45° Plaspec gloss head detector and a standard (50% gloss) reflecting plate. The Galvanometer reading is adjusted to a value of 50 under these conditions. The reading of the fresh Perspex plate is then carried out using the same reflectance arrangement. The fresh piece of Perspex is then fitted into a holder. Two mis of the dispersed silica, sufficient to lubricate fully the brushing stroke, is placed on the plate and the brush head lowered onto the plate. The machine is switched on and the plate subjected to three hundred strokes of the weighted brush head. The plate is removed from the holder and all the suspension is washed off. It is then dried and re-measured for its gloss value. The abrasion value is the difference between the unabraded value and the value after abrasion. SUBSTSTUTE SHEET This test procedure, when applied to known abrasives, gave the following values: Plastics abrasion value Calcium carbonate (15 micron) ' 32 Silica xerogel (10 micron) prepared by UK 1264292 method 25 Alumina trihydrate (Gibbsite) 15 micron 16 Calcium pyrophosphate (10 micron) 14 Dicalcium phosphate dihydrate (15 micron) 7 Neosyl as used in US 3864470 (15 micron) .. 8 v) Electrolyte Levels: Sulphate is determined gravimetrically by hot water extraction of the silica, followed by precipitation as barium sulphate. Chloride is determined by hot water extraction of the silica, followed by titration with standard silver nitrate solution using potassium chromate as indicator (Mohr's method). vi) Moisture Loss at 105 t> C: Moisture loss is determined by the loss in weight of a silica when dried to constant weight in an electric oven at 105°C. vii) Ignition Loss at 1000°C: Ignition loss is determined by the loss in weight of a silica when ignited in a furnace at 1000°C to constant weight. S UBSTITUTE SH viii) pH: This measurement is carried out on a 5% w/w suspension of the silica in boiled demineralised water (CO free) . ix) Refractive index (RI) /transmission: The sample of silica is dispersed in a range of Sorbitol syrup (70% Sorbitol) /water mixtures. After deaeration, usually 1 hour, the transmissions of the dispersions are determined using a spectrophotometer at 589 nm; water being used as blank. The refractive index of each dispersion is also measured using an Abbe refractometer. A graphical representation of transmission plotted against refractive index allows the range of refractive indices over which the transmission exceeds 70% to be determined. The maximum transmission of the sample and the refractive index at which this is obtained can also be estimated from this graph. The silicas of the invention are required to have a transmission of at least 70% at a point in the RI range of 1.435 to 1.456. x) Viscosity determination: Slurries of silica, at 10% and 20% w/w concentration, in 70% Sorbitol Syrup (E420) are prepared using a Heidolph stirrer at 1500 rpm for 10 minutes. The viscosity of the slurry is determined § 100s shear rate using a Haake Rotovisco (R)RV12 @ 25°C. S UBSTITUTE SHEET The following conditions are used:- Measuring head M500 Sensor system MVI PG 142 Programme 1-3-1 Speed range 0-128 rpm xi) Fluoride compatibility: A sample of abrasive is slurried in a solution (23% w/v) of sodium ' fluoride for 1 hour at 60°C. The resultant slurry is centrifuged, the clear supernatant liquid is diluted 1:1 with a EDTA/TRIS buffer solution and the fluoride concentration is determined by direct potentiometry using a fluoride ion selective electrode in accordance with the method given in Textbook of Quantitative Chemistry by Vogel (5th Edition 1989) page 570 section 15. 16. The fluoride compatability is determined by comparison of the sample result with a fluoride standard solution. xii) Mercury intrusion volume: Mercury intrusion volumes are determined (in cm 3*/g) by standard mercury intrusion procedures using a Micromeritics Autopore 9220 mercury porosimeter. The pore radius is calculated from the Washburn equation using values of surface tension for mercury of 485 dynes/cm and contact angle of 140°. Prior to measurement the sample was outgassed at room temperature to a pressure of 50 microns of mercury. The mercury intrusion volume recorded is that occurring over the range of calculated pore diameters of 0.05 to 1.0 micron. S UB S TITUTE SHEET xiii) Mean pore diameter (MPD) : This parameter is related to the surface area and pore volume and, using a cylindrical pore model, is calculated for a silica product with the formula: MPD (nm) = pore volume (cm 3 -1) x 4000 —1 surface area (m 2 g ) Pore volume is the mercury intrusion volume defined in (xii) . xiv) Crystal form after firing at 1100°C: A sample of the silica is fired in an electric muffle furnace for one hour at 1100°C. The treated sample is allowed to cool and the crystal structure present identified from the trace obtained from an x-ray diffractometer. Specific description of the invention Examples of the preparation of precipitated silicas will now be given to illustrate but not limit the invention. Mixing is an important feature in the reaction of silicate and sulphuric acid. Consequently fixed specifications as listed in Chemineer Inc. Chem Eng. April 26th 176 Pages 102-110 have been used to design the baffled heated stirred reaction vessels. Whilst the turbine design is optional to the mixing geometry, a 6-bladed 30° pitched bladed unit has been chosen for our experiments in order to ensure maximum mixing effectiveness with minimum shear. Shear has been supplied SUBSTITUTE SHEE T to the reactant mixture, with the exception of example 4, by circulating the contents of the reaction vessel through an external high shear mixer (Silverson) containing a square hole high shear screen throughout the simultaneous addition of silicate and acid; the energy input being commensurate with the volume flow and number of recirculations required as specified by the manufacturer. The solutions used in the process were as follows:- i) Sodium silicate solutions having a SiO :Na 0 ratio in the range of 3.1 to 3.4:1. ii) A sulphuric acid solution of specific gravity 1.10 (15.0% W/W solution) to 1.15 (21.4% W/W solution) . iii) An electrolyte solution as defined in each example The following procedure was adopted in the preparation of the precipitated silicas. Values of reactant concentrations and volumes, and reaction temperatures are given in Table 1. (A) litres of water were placed in the vessel together with (B) litres of electrolyte solution and (C) litres of the sodium silicate solution. This mixture was then stirred and heated to (E)°C. The sodium silicate ((D) litres) and sulphuric acid ( (F) litres) solutions were then added simultaneously over a period of about 20 minutes with stirring while maintaining the temperature at (E) °C. The flow rates of the silicate and acid solutions were uniform throughout the addition period to ensure that a constant pH was maintained in the vessel. Sulphuric acid solution was then added over a period of 10 minutes with continued mixing to reduce the pH of the liquid to the range of 2.5, usually 3.0, to 4.0. During this addition of acid the temperature was maintained. The resultant slurry was then filtered and washed with water to remove excess electrolyte. Typically, for a toothpaste application, the residual electrolyte would be less than 2% on a dry weight basis. After washing, the filter cake in each example was flash dried and comminuted to the desired particle size range. The precipitated silica obtained had the properties, expressed on a dry weight basis, as listed in Table II. The amorphous precipitated silicas prepared as described provided satisfactory cleaning properties for the transparent toothpastes in which they were incorporated. The toothpastes had commercially suitable properties for stability and usage. A typical formulation using a silica of this invention is listed below. SUBSTITUTE SHEET Transparent Gel Toothpaste Sorbosil TC15 6.0 Silica of invention 16.0 Sodium Carboxymethyl Cellulose 0.7 Sorbitol, 70% non-crystallisable 60.0 Polyethylene Glycol 1500 5.0 Sodium Lauryl Sulphate 1.5 Sodium Monofluoro-phosphate 0.8 Flavour 1.0 Saacharin • 0.2 Colour, Blue, CI42090 0.002 Water & minor ingredients to 100 Properties - Initial Density gml " (25°C) 1.37 Sorbosil TC15 is a thickening silica obtainable from Crosfield Chemicals of Warrington, England. SUBSTITUTE SHEET TABLE I Example No. Vessel capacity (litres) 64 64 64 64 64 64 64 Water volume (A) (litres) 10.3 13.5 12.3 5.8 None 10.5 None c Electrolyte used NaCl NaCl NaCl NaCl Na 2 S0 4 NaCl Na.-SO, 2 4 00 CO Concn. of electrolyte H (%w/w) 25 25 25 25 34.1 25 6.9 c π Vol. of electrolyte (B) X (litres) 3.8 1.3 3.5 7.6 13.7 3.8 17.4 rη Silicate ratio SiO /Na 0 by weight 3.31 3.30 3.2 3.2 3.29 3.28 3.25 TABLE 1 CONTINUED Example No . 1 2. 2 4 5 6 7 8. Si0 2 Concentration in sodium silicate (%w/w) 17.05 17.5 17.3 17.3 17.2 17.4 17.5 16.7 CO c Silicate volume (C) IXJ (litres) 0.1 0.1 0.1 0.1 0.1 0.1 0.1 1.3 C __ Silicate volume (D) ~J (litres) 11.0 10.7 9.9 10.7 11.4 10.7 9.2 124.3 m X Acid concentration fη (%W/W) 17.0 16.3 16.2 16.3 16.3 16.8 16.0 17.3 Acid volume (F) (litres) 4.0 4.2 3.6 4.2 4.7 4.2 3.3 45.7 Temperature °C (E) 50 80 60 40 50 50 98 85 TABLE 2 Example No. I 2 2 4 . 5 j> 7 8 Mercury intrusion vol (cm /g)0.38 0.61 0.31 0.21 0.29 0.32 0.57 1.51 Mean pore diameter (nm) 3.1 7.5 3.5 1.6 2.4 3.5 4.7 20.5 C Surface area (m g ) 485 327 360 524 487 366 480 293 C3 O H -_• Oil absorption (cm3/100g) 110 130 90 100 110 120 110 158 c Hfη Weight mean particle (0 size (micron) ' 14.9 11.2 12.9 6.2 15.0 9.6 14.5 8.5 X m |j Plastic abrasion value 8.5 12 14 15 11 10 11 12 Max % transmission 95 90 93 98.4 96.1 92.5 83 89 at refractive index 1.454 1.442 1.452 1.449 1.453 1.456 1.440 1.444 Available fluoride (%) 97.2 96.6 96.1 95.9 96.5 95.6 93.9 94.6 TABLE 2 CONTINUED Example No. 1 2 1 A 5 6 1 8. Electrolyte level (S0 4 =) (% W/W) 0.04 0.08 0.03 0.03 0.11 0.03 0.13 0.19 to C Electrolyte level (/) (Cl -) (% W/W) 0.06 0.06 0.02 0.06 0.05 0.10 0.03 0.03 Hi H C Moisture loss @ 105°C fή (%) 1.7 3.2 9.6 9.3 3.7 8.4 4.1 5.0 to Tp-j. Ignition loss @ 1000°C "J (% W/W) 9.9 8.6 14.4 15.3 9.3 13.3 9.0 10.3 pH 6.9 7.1 7.3 7.5 7.2 6.8 6.7 6.9 TABLE 3 Viscosity of silicas dispersed in 70% Sorbitol Syrup (E420. mPas at 100s "* OA 10% w/w Silica 20% w/w Silica Example 8 Silica 158 161 1127 Low Structure commercially available silica abrasive 110 186 303 Medium Structure commercially available silica (Neosyl R ) 170 290 1406 High Structure commercially available silica 200 1448 Too high to measure on this sensor This demonstrates the silicas of this invention that have higher oil absorption (OA) give, at high concentration in sorbitol syrup, a higher level of thickening than that usually associated with a low structure commercially available abrasive silica. SUBSTITUTE SHEET

Claims: Claims 1. An amorphous precipitated silica having i) a surface area in the range from about 250 to 2 about 600 m /g, ii) an oil absorption (using linseed oil) from about 90, preferably from about 110, to about 160 3 cm /lOOg, iii) a weight mean particle size in the range from about 5 to about 20 microns, iv) ' a plastics abrasion value in the range from about 8 to about 15, v) a transmission of at least 70% within the refractive index range of 1.435 to 1.456, and vi) a mean pore diameter in the range from about 1.5nm to about 21nm. 2. A silica according to Claim 1 wherein the surface area is at- least about 300 m 2 /g. 3. A silica according to Claim 1 or 2 wherein the 2 surface area is not more than about 550 m /g. 4. A silica according to claim 1, 2 or 3 wherein the oil absorption is not more than about 140 cm 3/100g. 5. A silica according to Claim 1, 2, 3 or 4 wherein the " plastics abrasion value is at least about 10. 6. A silica according to any preceding claim wherein the mean pore diameter is at least about 3 nm. SUBSTITUTE SHEET 7. A silica according to any preceding Claim wherein the mean pore diameter is not more than about lOnm. 8. A silica according to any preceding claim wherein the weight mean particle size is not more than about 15 microns. 9. A silica according to any preceding claim wherein the phase after firing at 1100°C is alpha-cristobalite. 10. A silica according to any preceding claim having a moisture content of less than about 25%, preferably less than about 15% w/w 11. A silica according to any preceding claim in which the total of soluble calcium, magnesium and aluminium is not more than 500 ppm and the silica has a fluoride compatibility above 90%. 12. A toothpaste composition containing from about 5% to about 50% by weight, preferable up to about 30%, of an amorphous precipitated silica defined in any preceding claim. SUBSTITUTE SHEET

Inventors: MCKEOWN IAN PATRICK, STANIER PETER WILLIAM, MCKEOWN, IAN, PATRICK, STANIER, PETER, WILLIAM
Applicants: CROSFIELD JOSEPH & SONS, JOSEPH CROSFIELD & SONS LIMITED
Application year: 1991
Main classification: C01B33
IPC codes: A61K8, A61Q11, C01B33