Method of manufacturing a semiconductor substrate having a dielectric isolation structure

Abstract: In accordance with this invention, in manufacturing a semiconductor substrate having a dielectric isolation structure, an approach is employed to form a dielectric film at a semiconductor layer (32) formed by epitaxial growth and grooves for carrying out dielectric isolation to deposit filler (36) thereon thereafter to polish the deposited filler by using the polishing condition where the polishing rate ratio of the filler to the dielectric film is one fifth or less. Thus, an active semiconductor layer where elements are to be formed can be provided with good productivity under the state where the flatness thereof is good and the layer thickness is uniformly and precisely controlled.

Description: BACKGROUND OF THE INVENTION This invention relates to a method of manufacturing a semiconductor substrate, and more particularly to a method of manufacturing a semiconductor substrate applied to a semiconductor device having, e.g., a dielectric isolation structure. More particularly, the present invention relates to a method of manufacturing a semiconductor substrate as specified in the preamble of claim 1. A method of this type is known from EP-A-0 398 468. US-A-3 979 237 discloses a method of obtaining a semiconductor substrate comprising isolation regions with grooves filled with polysilicon. The polysilicon filler is polished until an SiO 2 layer is exposed, which layer is removed in a successive step. US-A-4 948 742 discloses a method of manufacturing a semiconductor device claiming a high breakdown voltage which shall be satisfying in productivity with no warp on the wafer. The document RESEARCH DISCLOSURE, No. 306, Oct. 1989 page 743, Disclosure No. 30670, discloses a method of producing planarized polysilicon filled trenches. Hitherto, in forming circuit elements of a semiconductor integrated circuit, in order to form circuit elements isolated from other circuit elements to take a form of an island, a dielectric isolation system of a structure in which, e.g., each periphery (side surface and bottom surface) of the circuit elements is perfectly enclosed by a dielectric substance has been proposed. In accordance with the P-N junction isolation system having such a structure, the element isolation withstand voltage has been able to take more than 500 volts whereas that withstand voltage could not take more than 200 volts according to the technologies prior thereto. Thus, this isolation system is advantageous in that it is free from the problem of latch-up phenomenon taking place by the parasitic element operation, and that high integration is easy. For this reason, such an dielectric isolation system has been frequently used. FIG. 4 is a view showing the cross section of an example of a semiconductor device having such a dielectric isolation structure. A semiconductor active layer is formed in a semiconductor layer 2 on the upper layer side of a first semiconductor substrate 1, and an insulating film (dielectric film) 3, e.g., silicon dioxide (SiO 2 ) is formed on the lower layer side thereof. Furthermore, a second semiconductor substrate 4 is bonded to the first semiconductor substrate 1 in a manner that it serves as a underlying layer of the insulating film 3. More particularly, within the semiconductor layer 2 and an overlying layer, i.e., a layer formed thereabove, the essential parts of circuit elements 5 and 6 are formed. Within the semiconductor layer 2, a high concentration, i.e., heavily doped p-type silicon layer 7, a p-type silicon layer 8, and an n-type silicon layer 9 are formed in a manner stacked in order recited. It is to be noted that a high concentration n-type silicon layer 10 is formed as a buried layer at a portion between the p-type silicon layer 8 and the n-type silicon layer 9. Further, a p-type silicon layer 11, a high concentration n-type silicon layer 12 and a high concentration p-type silicon layer 13 are formed in a manner spaced from each other at the surface portion of the n-type silicon layer 9, and high concentration n-type silicon layer 14 and 15 are formed at the surface portions of the p-type silicon layer 11 and the high concentration p-type silicon layer 13 and within their regions, respectively. Moreover, the circuit elements 5 and 6 are isolated at their bottom surfaces by the insulating film 3. Furthermore, the circuit elements 5 and 6, and adjacent other circuit elements are isolated at their side surfaces by providing grooves on all sides thereof. Namely, respective circuit elements are isolated by surrounding the peripheral portions thereof by means of a structure like a wall such that those circuit elements are surrounded by insulating films (dielectric films), respectively including polycrystalline silicon layers therein, 16 and 17, e.g., SiO 2 along both the side surfaces of the grooves provided on all sides, and that polycrystalline silicon layers 18 are formed in the respective grooves. The point particularly important as a semiconductor substrate in forming a semiconductor device having such a dielectric isolation structure is that the surface flatness of the semiconductor layer 2, especially the n-type silicon layer 9 serving as the uppermost semiconductor layer where the essential parts of the circuit elements are directly formed is satisfactory, and that the film thickness is uniformly and precisely controlled. For example, when a predetermined thickness of this layer assumed to be, e.g., 15 µm, it is desirable that unevenness is within + 5%, i.e., + 0.75 µm. In the case where the accuracy of this semiconductor layer thickness is poor, the characteristics of the circuit elements do not become uniform, and/or isolation between circuit elements cannot be completely carried out, so the element isolation withstand voltage cannot take a sufficiently large value. As a result, there may be place the adverse influence from adjacent elements undesirably conducting. Meanwhile, in order to manufacture such a conventional semiconductor substrate, an approach is employed to form, within the semiconductor layer 2, high concentration p-type silicon layer 7, p-type silicon layer 8 and n-type silicon layer 9 as shown in FIG. 4 to form grooves thereafter to deposit polysilicon layers so that those grooves are sufficiently filled with such layers to regulate or adjust the thickness of the n-type silicon layer 9 of the uppermost layer by grinding. This grinding is carried out ordinarily at two stages of rough grinding and finish grinding. In the conventional semiconductor substrate formed in accordance with such a manufacturing method, even if substrates having good flatness are used for the first semiconductor substrate 1 and the second semiconductor substrate 4, unevenness of the thickness becomes large because the n-type silicon layer 9 is formed by grinding. The distribution of unevenness by the conventional method is shown at the right side portion of FIG. 3. In this figure, the internal unevenness is taken on the abscissa and the frequency is taken on the ordinate. In the case of a semiconductor substrate by the above-mentioned conventional method, when the thickness of the n-type silicon layer 9 formed so that the diameter is 100 mm and a predetermined thickness is 15 µm is measured, the internal unevenness takes a large value of 3 µm (+ 10%) even if a good sample is taken, and the range of unevenness is also broad. At this time, the mean value of the internal distribution of the unevenness value is 4 µm (+ 13.3%). In accordance with such a conventional method, it is extremely difficult to provide a semiconductor substrate such that the internal unevenness falls within + 5% thus to realize a perfect dielectric isolation structure. In addition, in order to form an n-type silicon layer 9 of a predetermined thickness, it is required to additionally and thickly grow an epitaxial layer in excess of a predetermined thickness, e.g., 15 µm by 40 µm as a machining clearance of grinding or polishing at the succeeding process steps. As a result, it takes much time, resulting in lowered throughput. This causes the cost to be increased. SUMMARY OF THE INVENTION Accordingly, an object of this invention is to provide a method of manufacturing a semiconductor substrate having good productivity in which a semiconductor layer where the active region serving as the essential part of circuit elements is directly formed, can be formed in a manner that the flatness thereof is good, and the film thickness is uniformly and precisely controlled. According to the present invention, this object is attained by providing a method according to claim 1. Further improvements are obtainable by providing features of the sub-claims It may be provided a method of manufacturing a semiconductor substrate comprising: a first step of bonding first and second semiconductor substrates in a manner that a first dielectric film formed on at least one surface of the semiconductor substrates is placed therebetween, a second step of polishing the surface of the bonded first semiconductor substrate to decrease the thickness of the first semiconductor substrate thus to form a first semiconductor layer having a predetermined thickness, a third step of forming a second semiconductor layer having a predetermined thickness on the first semiconductor layer by epitaxial growth, a fourth step of forming, in the first and second semiconductor layers, a groove having a depth from the surface of the second semiconductor layer down to the first dielectric film to form a second dielectric film on the side surfaces of the groove and the upper surface of the second semiconductor layer, a fifth step of completely filling a filler into the grooves and depositing the filler on the second dielectric film, a sixth step of polishing and removing the filler by using the polishing condition where the ratio between the polishing rate for the second dielectric film and the polishing rate for the filler is less than 1/5, to thus allow the second dielectric film on the second semiconductor layer to be exposed, and a seventh step of removing the second dielectric film on the second semiconductor layer exposed at the sixth step. In accordance with this invention, in manufacturing a semiconductor substrate having a dielectric isolation structure, an approach is employed to form a dielectric film at a semiconductor layer formed by epitaxial growth and grooves for carrying out dielectric isolation to deposit fillers or filling materials thereon thereafter to polish the deposited fillers by using the polishing condition where the polishing rate ratio of the filler to the dielectric film is set to a value less than one fifth. Thus, an active semiconductor layer where elements are to be formed can be provided with good productivity under the state where the flatness thereof is good and the layer thickness is uniformly and precisely controlled. BRIEF DESCRIPTION OF THE DRAWINGS In the accompanying drawings; FIGS. 1A to 1M are cross sectional views every process steps showing an embodiment of this invention, respectively, FIG. 2 is a characteristic diagram showing the polishing rate ratio of the polishing material with respect to the processing yield, FIG. 3 is a characteristic diagram showing the internal unevenness in thickness versus frequency, and FIG. 4 is a cross sectional view showing a semiconductor device having a dielectric isolation structure. DESCRIPTION OF THE PREFERRED EMBODIMENT In FIG. 1A, boron (B) is ion-implanted into at least one mirror-polished surface of a first p-type silicon substrate 25, e.g., having a diameter of 125 mm, a thickness of 625 µm, a crystal orientation of (100), and a resistivity of 90 to 100 Ω·cm under the condition of an acceleration voltage of 40 KeV and dose of 2 × 10 15 cm -2 to form a high concentration p-type silicon layer 26 of a desired layer thickness. In FIG. 1B, the p-type silicon substrate 25 on which the high concentration p-type silicon layer 26 is formed is oxidized to form insulating films (dielectric films) 27 of silicon dioxide (SiO 2 ) having a thickness of 1um on the both surfaces thereof. In FIG. 1C, the surface of the insulating film 27 on the side where the high concentration p-type silicon layer 26 is formed and at least one mirror-polished surface of a second semiconductor substrate 28, e.g., an n-type silicon substrate having a diameter of 125 mm , a thickness of 625 µm, a crystal orientation of (100), and a resistivity of 1 to 100 Ω·cm (in the case where silicon wafer is used, there is no limit in crystal orientation, resistivity, and shape, etc.) i.e., the mirror-polished surfaces are bonded to each other at a room temperature in air. Thereafter, thermal treatment is implemented for two hours in the gas atmosphere of N 2 : O 2 = 4 : 1 (volume ratio) at 1100°C, thus to bond the p-type silicon substrate 25 and the second semiconductor substrate 28. It is to be noted that this bonding may be carried out in vacuum or by the electrostatic pressure method of applying a pulse voltage across both the substrates. In FIG. 1D, rough grinding processing is implemented to the p-type silicon substrate 25 by means of a grinder, etc. from the surface side of the exposed insulating film 27, and mirror-polishing processing is then implemented, e.g., by mechano-chemical polishing used for mirror-processing of an ordinary silicon substrate to form a p-type silicon layer 29. By this processing, a high concentration p-type silicon layer 26 and a p-type silicon layer 29 are formed on the insulating film 27 to which the second semiconductor substrate 28 is bonded so that the layer thickness in total becomes equal to 40 µm. In FIG. 1E, resist is coated on the upper surface of the p-type silicon layer 29. Then, patterning is implemented thereto to form a resist layer 30 where a predetermined pattern is formed by using well known means. In FIG. 1F, impurity diffusion is implemented to the opened region of the resist layer 30 by an ordinary diffusion process using a solid diffusion source of antimony oxide (Sb 2 O 3 ). Namely, in the N 2 gas atmosphere, impurity diffusion is carried out under the condition of 1250°C and 60 minutes (the solid diffusion source is held at 950°C). Thus, a high concentration n-type silicon layer 31 having a sheet resistance of 20 Ω/□ is formed. Thereafter, the resist layer 30 is removed. In FIG. 1G, a low concentration n-type silicon layer 32 is epitaxially grown on the upper surface of the p-type silicon layer 29 and the high concentration n-type silicon layer 31. Namely, trichlorosilan (SiHCℓ 3 ) gas is thus used to epitaxially grow a low concentration n-type silicon layer 32 having a layer thickness of 15 µm, and a resistivity of 7 to 9 Ω/cm at 1140°C. In FIG. 1H, a resist layer 33 where a predetermined pattern is formed is formed on the upper surface of the low concentration n-type silicon layer 32 by using well known means. In FIG. 1I, the low concentration n-type silicon layer 32, the p-type silicon layer 29, and the high concentration p-type silicon layer 26 are etched from the upper surface down to the upper portion of the insulating film 27 by using KOH-system etchant to form a V-groove 34 thereafter to remove the resist layer 33. In FIG. 1J, the side wall surfaces of the V groove 34 and the upper surface of the low concentration n-type silicon layer 32 are thermally oxidized to form an insulating film (dielectric film) 35 of SiO 2 having a thickness of 1 µm. In FIG. 1K, a polycrystalline silicon layer 36 is deposited on the entire upper surface portion of the insulating film 35 on the low concentration n-type silicon layer 32 so that the internal portion of the V groove 34 on which the insulating film 35 is formed is completely filled with the silicon layer 36. Namely, SiHCℓ 3 gas is used to deposit the polycrystalline silicon layer 36 having a layer thickness of 80 µm by using CVD process, etc. at 1100°C. In FIG. 1L, rough grinding processing is carried out in a horizontal direction by means of grinder, etc. until the layer thickness of the polycrystalline layer 36 on the insulation film 35 formed on the low concentration n-type silicon layer 32 becomes equal to 10 µm. This processing is implemented to such an extent that the internal unevenness of the thickness of the polycrystalline silicon layer 36 at this time is 5 µm or less. Thereafter, the surface of the polycrystalline silicon layer 36 roughly ground is subjected to mirror polishing processing, e.g., by mechano-chemical polishing used in mirror polishing processing for an ordinary silicon substrate. This mirror polishing processing is carried out until the polycrystalline silicon layer 36 on the insulating film 35 is removed (FIG. 1M). In this polishing processing, the polishing condition where the polishing rate ratio (selection ratio) of the silicon dioxide to the polycrystalline silicon is 1/5 or less is preferably used. The reason why such a condition is employed is based on the following finding. Namely, a polycrystalline silicon layer is deposited on a silicon dioxide film having a thickness of 1 µm on a silicon substrate. Then, rough grinding is implemented to the upper surface of the polycrystalline silicon layer so that the internal unevenness is 5 µm or less. Mirror-polishing processing is implemented from the side of the polycrystalline silicon layer subjected to rough grinding as stated above by using respective polishing conditions where the polishing rate ratios are different. The yield in the case where processing can be carried out in a manner that the silicon substrate of the underlying layer is not exposed at this time is experimentally determined. In this embodiment, the above-mentioned condition is determined from this finding. Namely, as shown by the graph of FIG. 2 in which the polishing rate ratio between silicon dioxide and polycrystalline silicon is taken on the abscissa and the processing yield is taken on the ordinate, when the polishing rate ratio is 1/5 or less, the polycrystalline silicon layer is entirely removed before the silicon substrate of the underlying layer is exposed, so the processing yield is at a high level of substantially 100%. In contrast, when the polishing rate ratio is above 1/5, silicon dioxide film is partially removed before the polycrystalline layer is entirely removed, so the silicon substrate of the underlying layer will be exposed and polished. Since whether or not the polycrystalline silicon layer is entirely removed can be easily discriminated at the processing step, the polishing rate ratio is set to a value less than 1/5. If such a condition is satisfied, it is possible to precisely determine the end point of polishing by control of time. Such a polishing rate ratio is greatly influenced by the kind of the polishing material, but processing pressure and/or rotation speed in the polishing machine are also an important factor for the polishing rate ratio. Accordingly, it is necessary to select the polishing condition where these factors are synthetically taken into consideration. In FIG. 1M, the insulating film 35 on the low concentration n-type silicon layer 32 is removed by using hydrogen fluoride (HF). Thus, there is formed an isolation section of the dielectric isolation structure in which insulating films 37 and 38 are formed on the side surfaces of the V groove 34 and the polycrystalline silicon layer 36 is formed within the V groove 34. By undergoing the above-mentioned process steps, a semiconductor substrate in which the low concentration n-type silicon layer 32 having a predetermined layer thickness, or the like is formed is provided. By using this semiconductor substrate, elements are formed as shown in FIG. 4. The low concentration n-type silicon layer 32 thus obtained is featured below. Namely, because a layer formed on the p-type silicon layer 29 subjected to mirror-polishing processing, with good flatness and in a manner that the thickness thereof is uniformly and precisely controlled is used as it is, the layer thickness of the low concentration n-type silicon layer 32 thus obtained is uniform and accurate. Furthermore, in order to experimentally confirm this, the thickness of the low concentration n-type silicon layer 32 and the internal unevenness thereof are measured in connection with 50 semiconductor substrates provided by undergoing the above-mentioned process steps. The measured result is shown at the left hand side of FIG. 3 in which the internal unevenness is taken on the abscissa and frequency is taken on the ordinate. As seen from the comparison with the case of the prior art, in accordance with semiconductor substrates according to this embodiment, the internal unevenness thereof is 1.5 µm (+ 5%) or less even if attention is drawn to semiconductor substrates for which the internal unevenness is large. This satisfies the level in which the required internal unevenness is less than + 5%. Furthermore, the mean value of the distribution of internal unevenness values is 0.94 µm (+ 3.13%) and there is less unevenness. In addition, in accordance with the method according to this method, in order to form the low concentration n-type silicon layer 32 having a layer thickness of 15 µm, it is unnecessary to additionally and thickly grow the epitaxial layer by taking particularly a machining clearance for grinding or polishing at the subsequent process steps into consideration. Namely, it is sufficient to carry out epitaxial growth just by a predetermined thickness of 15 µm, resulting in no possibility that the cost is increased.

Claims: A method of manufacturing a semiconductor substrate comprising (a) bonding of first and second semiconductor substrates (25, 28) in a manner that a first dielectric film (27) formed on at least one surface of said semiconductor substrates is placed therebetween; (b) mechanically and mechano-chemically polishing of the surface of said bonded first semiconductor substrate to decrease the thickness of said first semiconductor substrate thus to form a first semiconductor layer (29) having a predetermined thickness; (c) forming of a second semiconductor layer (32) having a predetermined thickness on said first semiconductor layer (29) by epitaxial growth; (d) forming, in said first and second layers (29, 32), of a groove (34) reaching said first dielectric layer (27); (e) forming of a second dielectric film (35) on the side surface of said groove (34) and the upper surface of said second semiconductor layer (32); (f) completely filling of a filler (36) into said groove (34) and depositing said filler on said second dielectric film (35); (g) removing of said filler (36) on the second dielectric film (35); and (h) removing of said second dielectric film (35); characterized in that (i) said removing of said filler (36) on the second dielectric film (35) is performed by two sequential steps of a rough grinding process with a thin film of filler remained on the second dielectric film (35) and mirror-polishing under a polishing condition where the ratio between the polishing rate for said second dielectric film (35) to the polishing rate for the filler (36) is 1/5 or less; and (j) said removing of said second dielectric film (35) is performed by etching. The method as set forth in claim 1, characterized in that said filler (36) is polysilicon. The method as set forth in claim 1 or 2, characterized by forming of a buried layer (26) between said first and second semiconductor substrates (25, 28).

Inventors: HOSHI TADAHIDE, HOSHI, TADAHIDE
Applicants: TOSHIBA KK, KABUSHIKI KAISHA TOSHIBA
Application year: 1991
Main classification: H01L21
IPC codes: H01L21