Conductive silicone rubber composition and conductive silicone rubber

Abstract: A conductive silicone rubber composition comprises a conductive silicone rubber composition comprising: (a) an organopolysiloxane of the following general formula (1): wherein R¹ is an unsubstituted or substituted monovalent hydrocarbon group having 1 to 10 carbon atoms and "a" is a positive number of 1.90 to 2.05, (b) conductive carbon black, and (c) an organic peroxide of the following general formula (2): wherein X is in which "n" is an integer of 2 to 8 or and R² and R³ are independently selected from monovalent hydrocarbon groups having 3 to 10 carbon atoms and -SiR 4 / 3 in which R⁴ is a methyl, ethyl or phenyl group.

Description: The present invention relates to non-foamable or foamable conductive silicone rubber compositions containing conductive carbon black which can be cured through the normal - pressure hot - air vulcanization (HAV) method and non-foamed or foamed conductive silicone rubbers obtained by curing the composition. Prior Art Various types of conductive rubbers obtained by curing a rubber composition having a conductive material blended therein are conventionally known. For example, conductive rubbers with an electrical resistivity of from 10 5 to 10 Ω · cm are widely used in which carbon black is blended as a conductive material. Silicone rubber, one of the electrically insulating rubbers, is popular because it is superior in heat resistance, cold resistance, and weather resistance. Conductive silicone rubber having a conductive material such as carbon black blended therein is also practically used, in ways similar to other conductive rubbers. Conductive silicone foam rubber is also known, prepared by adding a foaming agent to a conductive silicone rubber composition to foam and cure it. In practice the conductive material included in a conductive silicone rubber may be, carbon black, graphite, various metal powders including silver, nickel and copper powders, various fine particles and short fibers to which electrical conductivity is given by surface treating them with metal such as silver, and mixtures of carbon and metallic fibers. They decrease the volume resistivity of silicone rubber up to 10 10 to 10 -3 Ω·cm according to the type of conductive material and the proportion used, without impairing the characteristic peculiar to the silicone rubber. To obtain high-conductive silicone rubber with a volume resistivity of 10 5 Ω·cm or less, carbon black and metal powders of silver and nickel are suitably used. Carbon black powder is particularly preferred in view of cost. However, when continuously molding and vulcanizing long products (such as seals, gaskets and rollers) by extrusion molding of a conductive silicone rubber composition containing carbon black such as acetylene black, the vulcanizing system is extremely restricted by the presence of carbon black. With organic peroxide vulcanization, for example, if an acyl - based peroxide (such as benzoyl peroxide or 2,4-dichlorobenzoyl peroxide) used for normal - pressure hot - air vulcanization (HAV) of silicone rubber composition is used for vulcanizing a conductive silicone rubber composition containing carbon black, the vulcanization is inadequate because of the influence of the carbon black, and no satisfactory molded products are obtained. When an alkyl - based peroxide (such as dicumyl peroxide or ditertiarybutyl peroxide) is used for the system containing carbon black, compression molding may be possible. However, extrusion normal - pressure hot - air vulcanization is not effective; the surface of the article to be cured is not fully vulcanized owing to the influence of oxygen in the air. Therefore, satisfactory products again cannot be obtained. To execute extrusion normal-pressure hot-air vulcanization of a silicone rubber composition containing carbon black, an addition vulcanization method is therefore conventionally employed. That is an organopolysiloxane having alkenyl groups and an organohydrogenpolysiloxane having silicon-bonded hydrogen atoms are addition-reacted and cured in the presence of a curing catalyst such as a platinum compound. However, the addition reaction method has disadvantages in that the shelf life (preservation period) of the composition is limited and pot life is too short, workability is inferior and curing is susceptible to catalyst poisons such as amine, sulfur and tin. According to DE-OS 3 919 869 carbon black-containing silicon rubber compositions can be vulcanized effectively by a variety of peroxides such as ester peroxides. Dicumylperoxid and 2,5-dimethyl-2,5-di(tert.butylperoxy)hexane are preferably used. According to all the examples of D1 compression molding has been employed. Especially for manufacturing electromagnetic-wave-shielding and architectural gaskets, office-use conductive rollers such as charging, transfer, developing, paper-feed, and fixing rollers, and conductive calendering moldings such as zebra connector moldings from conductive silicone rubbers, the molding method according to the conventional normal-pressure hot-air vulcanization has problems in the moldability and quality of the resulting rubbers. Therefore, it is strongly desired to solve the above problems. To obtain satisfactory conductive silicone foam rubber, it is necessary to progress the vulcanization to a certain extent by addition vulcanization in order to confine the foaming gas produced by decomposition of foaming agent in the system. It is therefore necessary to find a proper control agent for controlling the addition reaction. However, even if a proper control agent is found, the optimum pot life for obtaining satisfactory foam is extremely limited. Accordingly, it is actually difficult to manufacture conductive silicone foam rubbers continuously by the addition reaction method with normal-pressure hot-air vulcanization. Thus, it is also desired to develop a foamable conductive silicone rubber composition having a long pot life in which persons engaged in foam (sponge) molding can stand and allowing quick vulcanization. Therefore, it is desired to provide non-foamable or foamable conductive silicone rubber compositions having conductive carbon black blended therein which have good preservation stability, can be vulcanized effectively by normal-pressure hot-air vulcanization in extrusion and calendering molding, have good moldability, and can give non-foamed or foamed conductive silicone rubbers having excellent physical properties and conductivity. Another aspect is to provide non-foamed or foamed conductive silicone rubbers obtained from the above compositions. The inventors have found a silicone rubber composition vulcanisable to a conductive silicone rubber and comprising an organopolysiloxane of the following general formula (1): R 1 a SiO 4-a 2 wherein R 1 represents an unsubstituted or substituted monovalent hydrocarbon group having 1 to 10 carbon atoms and "a" is a positive number of 1.90 to 2.05, conductive carbon black and an organic peroxide of the following general formula (2): wherein X is (CH 2 in which "n" is an integer of 2 to 8 or and R 2 and R 3 are independently selected from monovalent hydrocarbon groups having 3 to 10 carbon atoms and - SiR 4 / 3 in which R 4 is a methyl, ethyl or phenyl group. A conductive silicone rubber composition comprising the above components could be vulcanized well through normal-pressure hot-air vulcanization (HAV) or ultrahigh frequency (UHF) vulcanization for extrusion molding or calendering molding because the organic peroxide of formula (2) was not influenced by carbon black in the composition. The moldability is good because the technique does not depend on addition vulcanization. The resulting cured rubber had satisfactory conductivity and was free from surface tack. The inventors also found that foamable conductive silicone rubber compositions obtained by blending a foaming agent in the above compositions comprising the organopolysiloxane of formula (1), conductive carbon black, and the organic peroxide of formula (2) were very stable and easy to use, having a preservation stability of 7 days or more and a long pot life. The foamable conductive silicone rubber compositions could be quickly vulcanized, foamed and cured through normal-pressure hot-air vulcanization and ultrahigh frequency vulcanization for extrusion molding and calendering molding. The resulting foam rubbers had satisfactory conductivity, and were free from surface tack. In JP-A-130663/1988 and JP-A-122977/1990 we proposed organic peroxides of formula (2) for normal-pressure hot-air vulcanization of a silicone rubber composition containing no carbon black. Unexpectedly, we have now found that organic peroxides of formula (2) can also allow the silicone rubber composition containing carbon black to effectively execute normal-pressure hot-air vulcanization and allow the composition to vulcanize quickly by heating while the composition is very stable at ordinary temperature. Therefore, in one aspect we provide a non-foamable conductive silicone rubber composition comprising (a) the organopolysiloxane of formula (1), (b) conductive carbon black, and (c) the organic peroxide of formula (2). Another aspect is a foamable conductive silicone rubber composition comprising the above components (a) to (c) and further (d) a foaming agent. Conductive silicone rubbers obtained by curing the compositions are also provided as one further aspect, and a vulcanising method using normal-pressure hot-air vulcanisation as another. The component (a) of the composition is an organopolysiloxane represented by the following general formula (1). R 1 a SiO 4-a 2 In the above formula, groups R 1 are unsubstituted or substituted monovalent hydrocarbon groups having from 1 to 10 carbon atoms, preferably from 1 to 8 carbon atoms. Examples of R 1 include alkyl groups such as methyl, ethyl, propyl and butyl groups, alkenyl groups such as vinyl, allyl and butenyl groups, aryl groups such as phenyl and tolyl groups, and substituted ones of such groups in which some or all of the hydrogen atoms bonded to carbon atoms are replaced by a halogen atom, cyano group and the like, e.g. chloromethyl, chloropropyl, 3,3,3 - trifluoropropyl and 2-cyanoethyl groups. In the formula, "a" is a positive number of 1.90 to 2.05. The organopolysiloxane preferably has a straight-chain molecular structure, although it may have a partially branched chain. The organopolysiloxane is terminated with a triorganosilyl or hydroxyl group. Examples of the triorganosilyl group include trimethylsilyl, dimethylvinylsilyl, methylphenylvinylsilyl, methyldiphenylsilyl, methyldivinylsilyl, and trivinylsilyl groups. In this case, to effectively decrease the surface tack of an article to be manufactured, it is preferred that both ends of the molecular chain consist of a multifunctional silyl group such as (CH 2 =CH) 2 RSi- or (CH 2 =CH) 3 Si-, where R has the same meaning as R 1 . The organopolysiloxane is not restricted in polymerization degree and it is preferable that the organopolysiloxane has a viscosity of 300 cs or more at 25°C. The conductive carbon black of the component (b) may be one used for ordinary conductive rubber compositions. For example, acetylene black, conductive furnace black (CF), superconductive furnace black (SCF), extraconductive furnace black (XCF), conductive channel black (CC), and furnace black and channel black each heat treated at a high temperature of about 1,500°C can be used. Examples of acetylene black include DENKA® acetylene black (manufactured by DENKIKAGAKU Co., Ltd.) and SHAWINIGAN® acetylene black (manufactured by SHAWINIGAN CHEMICAL Co., Ltd.). Examples of conductive furnace black include CONTINEX® CF (manufactured by CONTINENTAL CARBON Co., Ltd.) and VULCAN® C (manufactured by CABOT Co., Ltd.). Examples of superconductive furnace black include CONTINEX SCF (manufactured by CONTINENTAL CARBON Co., Ltd.) and VULCAN SC (manufactured by CABOT Co., Ltd.). Examples of extraconductive furnace black include ASAHI HS-500 (manufactured by ASAHI CARBON Co., ltd.) and VULCAN XC-72 (manufactured by CABOT Co., Ltd.). Examples of conductive channel black include COURAX L (manufactured by DEGUSSA Co., Ltd.). As a kind of furnace black, KETJEN® BLACK EC and EC-600JD (manufactured by KETJEN BLACK INTERNATIONAL Co., Ltd.) can be used. Among the above carbon blacks, acetylene black is superior in conductivity because it contains less impurities and has an advanced secondary structure. Therefore, acetylene black is preferred for the present invention. KETJEN BLACK EC and KETJEN BLACK EC-600JD are also preferred because they have an excellent specific surface area and show excellent conductivity even in small quantities. The conductive carbon black is preferably blended in an amount of 5 to 100 parts by weight, particularly 10 to 70 parts by weight per 100 parts by weight of the organopolysiloxane (a). Less than 5 parts by weight of the conductive carbon black may result in an inferior conductivity. More than 100 parts by weight of the conductive carbon black may result in an inferior mechanical strength of cured products. Organic peroxide represented by the following formula (2) is used for the component (c) of the composition. In the above formula, X is -(CH 2 ) n - (where n is an integer of 2 to 8) or -CH 2 -C(CH 3 ) 2 -CH 2 -, R 2 and R 3 are identical or different and independently selected from unsubstituted and substituted monovalent hydrocarbon groups having 3 to 10 carbon atoms and -SiR 4 / 3(wherein R 4 is methyl, ethyl, or phenyl group). Examples of the monovalent hydrocarbon group include n-propyl, isopropyl, t-butyl, n-butyl, n-amyl, t-amyl, hexyl, heptyl, octyl, 2-ethylpropyl, 2-ethyl-butyl, 2-ethylhexyl and cumyl groups. Examples of -(SiR 4 ) 3 include trimethylsilyl, triethylsilyl and triphenylsilyl groups. The organic peroxide of component (c) acts as the vulcanizing agent for the organopolysiloxane of component (a). It is preferable to blend 0.1 to 5 parts by weight, more preferably 0.5 to 3 parts by weight of the organic peroxide per 100 parts by weight of the organopolysiloxane (a). Less than 0.1 part by weight may result in insufficient vulcanization. More than 5 parts by weight may result in an adverse effect by an excess residue of the decomposed peroxide and a high cost. A foaming agent may be blended as component (d) of the composition to obtain a foamed product. Any foaming agent can be used as long as it is stable at room temperature and emits a foaming gas when it is exposed to a high temperature. Nitrogen gas is preferred as the foaming gas. Carbon dioxide gas or other gas is also preferred. The foaming agent may be selected from commercially available ones. Those having a decomposition temperature of 80 to 300°C are preferably used, including azoisobutyronitrile, dinitropentamethylenediamine, benzene sulfonyl hydroxide, N,N'-dinitroso-N,N'-dimethyltelephthalamide, and azo-dicarbonamide. It is preferable to blend 1 to 10 parts by weight, more preferably 3 to 7 parts by weight of the foaming agent per 100 parts by weight of the organopolysiloxane (a). It is effective to blend the conductive silicone rubber composition with an organic silicone compound having at least one ≡ SiH group in one molecule as component (e) in addition to the above components in order to reduce the surface tackiness of a product obtained through normal-pressure hot-air vulcanization of the composition. Straight-chain or cyclic organic silicone compound is preferably used as the organic silicone compound (e), although an organic silicone compound having a partially branched structure or three-dimensional structure can also be used. Examples of the organic silicone compound include methylhydrogenpolysiloxanes having various polymerization degrees in which both ends are blocked with trialkylsilyl groups, organopentasiloxane shown as Si[OSi(CH 3 ) 2 H] 4 , siloxane copolymers consisting of SiO 2 unit and (CH 3 ) 2 HSiO 0.5 unit, copolymers of methylhydrogenpolysiloxane and dialkylsiloxane, polysilylalkylenesiloxanes containing ≡ SiH bonds, polysilanes, and polycarbosilanes. It is preferable to blend 0 to 10 parts by weight, more preferably 0.05 to 10 parts by weight, most preferably 0.5 to 5 parts by weight of the organic silicone compound of component (e) per 100 parts by weight of the organopolysiloxane (a). When less than 0.05 parts by weight of the silicone compound is blended, its effect may not appear. When the amount of the silicone compound exceeds 10 parts by weight, properties of cured products such as heat resistance may be degraded. The composition may be obtained by uniformly blending the predetermined amount of the above-mentioned components. The sequence for blending these components is not limited. In general, the organopolysiloxane of component (a) is blended with the conductive carbon black of component (b), and then blended with the organic silicone compound of component (e) (if needed), the organic peroxide of component (c), and, if a foamable composition is required, the foaming agent of component (d). Then, the mixture is conditioned through kneading by a Banbury mixer or roller. It is possible to blend the composition with a dispersing agent such as a low molecular weight siloxane having a polymerization degree of 100 or less, silanol group-containing silane and alkoxy group-containing silane, a heat-resistance improving agent such as iron oxide, selenium oxide and iron octoate, and a pigment. In view of reinforcement, silica fine powders such as fumed silica, wet silica, hydrophobically surface treated fumed silica and wet silica, quartz and diatomaceous earth may be blended. It is also possible to add a saturated aliphatic hydrocarbon such as isoparaffin solvent in order to improve workability and moldability to the composition. Other additives used for conventional silicone rubber compositions can also be blended. The conductive silicone rubber composition thus obtained is preferably vulcanized through normal-pressure hot-air vulcanization and converted into an elastic body. In this case, the vulcanization is preferably carried out for 5 to 10 seconds at 200 to 500°C. It is also effective to adopt a heating method using an infrared heater in combination with hot air. The normal - pressure hot - air vulcanization method may be combined with UHF heating because the composition is superior in the highfrequency absorbing characteristic, being blended with carbon black. The thus molded elastic body or cured product is a conductive silicone rubber free from voids and surface tackiness and superior in heat resistance. Therefore, the rubber may suitably be used for EMI-shielding and architectural gaskets, and conductive rollers such as charging, transfer, developing, paper-feed, and fixing rollers. The conductive silicone foam rubber prepared by foaming the composition with a foaming agent is also free from voids and surface tackiness and superior in heat resistance. Therefore, the foam rubber can also suitably be used for EMI-shielding materials, architectural gaskets, semiconductive sponge rollers having a resistivity of 10 3 to 10 10 Ω·cm such as charging, transfer, developing, paper-feed, fixing and pressure rollers, and sponge sheets such as antistatic mats. Examples and Comparative Examples are shown below for illustration but not for limitation. In the following, viscosity is the value measured at 25°C. Examples 1 to 3 and Comparative Examples 1 and 2 Silicone rubber compositions were manufactured by kneading 100 parts by weight of an organopolysiloxane consisting of 99.7 mol% of dimethylsiloxane unit, 0.275 mol% of the methylvinylsiloxane unit and 0.025 mol% of dimethylvinylsilyl group with which the both ends of the molecular chain are blocked and having a viscosity of 1 × 10 7 cs, 40 parts by weight of acetylene black and 1 part by weight of selenium oxide using a pressure kneader, and then adding to 100 parts by weight of the thus obtained base compound a peroxide shown in Table 1 and optionally a methylhydrogenpolysiloxane containing 1.6 mol per 100 g of ≡ SiH bond and end-blocked with trimethylsilyl group. Then, the compositions were extruded in the form of a 5 mm-diameter rod by an extruder having a diameter of 40 mm, and passed through a normal-pressure hot-air vulcanization tower having a height of about 1 m with a temperature of 250°C to conduct normal-pressure hot-air vulcanization for 5 minutes. To the resulting non-foamed conductive silicone rubbers, their surface tackiness, hardness (JIS A), and volume resistivity were measured. The results are shown in Table 1. Example Comparative Example 1 2 3 1 2 Base compound (parts by weight) 100 100 100 100 100 Organic peroxide (parts by weight) A 1.5 1.5 B 1.5 C 0.5 D 1.0 Methylhydrogenpolysiloxane (parts by weight) 0.5 Properties Surface tackiness None None None (Very good) Not vulcanized Sticky Hardness (JIS A) 60 61 63 - 43 Volume resistivity (Ω·cm) 5.7 5.8 5.5 - - Organic peroxide A: B: C: 2,4-dichlorobenzoylperoxide D: dicumyl peroxide From the results in Table 1, it is recognized that the compositions including peroxides as prescribed herein were sufficiently vulcanized in spite of being blended with carbon black and gave silicone rubbers having a low volume resistivity and free from surface tack. On the other hand, the compositions of the Comparative Examples, using the conventional peroxides, were not vulcanized well due to the influence of carbon black. Examples 4 to 6 and Comparative Examples 3 and 4 Foamable silicone rubber compositions were manufactured by kneading 100 parts by weight of an organopolysiloxane consisting of 99.7 mol% of dimethylsiloxane unit, 0.275 mol% of methylvinylsiloxane unit and 0.025 mol% of dimethylvinylsilyl group with which both ends of the molecular chain are blocked and having a viscosity of 1 × 10 7 cs, 40 parts by weight of acetylene black and 1 part by weight of selenium oxide using a pressure kneader, and then adding to 100 parts by weight of the thus obtained base compound a peroxide as listed in Table 1 and optionally a methylhydrogenpolysiloxane containing 1.6 mol per 100 g of ≡ SiH bond and end-blocked with trimethylsilyl group, as well as azobisisobutyronitrile as a foaming agent. The compositions were then extruded as a 5 mm-diameter rod by an extruder having a diameter of 40 mm, and passed through a normal - pressure hot - air vulcanization tower having a length of about 3 m with a temperature of 250°C, to conduct normal-pressure hot-air vulcanization for about 5 minutes. The surface tackiness, foaming magnification, and hardness (Ascar C) of the resulting foam rubbers were measured. The results are shown in Table 2. Example Comparative Example 4 5 6 3 4 Base compound (parts by weight) 100 100 100 100 100 Organic peroxide (parts by weight) A 1.5 1.5 B 1.5 C 0.75 D 1.0 Methylhydrogenpolysiloxane (parts by weight) 0.5 Azobisisobutyronitrile (parts by weight) 5 5 5 5 5 Properties Surface tackiness None None None (Very good) Not vulcanized Sticky Hardness (JIS A) 3.0 2.7 3.2 - 1.5 Volume resistivity (Ω·cm) 20 23 15 - 30 From the results in Table 2, it is seen that compositions including a peroxide as prescribed herein were sufficiently vulcanized and gave silicone foam rubber free from surface tack in spite of being blended with carbon black. On the other hand, the compositions of Comparative Examples, using the conventional peroxides, were not vulcanized well due to the influence of carbon black. Example 7 and Comparative Example 5 A foamable silicone rubber composition embodying the present invention was prepared by blending the organic peroxide A and azobisisobutyronitrile in the base compound of Example 4. For comparison, an addition reaction type silicone rubber composition having the formulation shown in Table 3 was prepared. The compositions were extruded, foamed and vulcanized in the same manner as in Examples 4 to 6 to examine their pot life. The results are shown in Table 3. From the results in Table 3, it is recognized that the composition of the present invention has a long pot life and can be used for seven days from immediately after preparation without any problem. On the other hand, the addition reaction type composition of the Comparative Example 5 is usable for only 4 hours. As described above, these non-foamable and foamable conductive silicone rubber compositions can effectively employ normal-pressure hot-air vulcanization using an organic peroxide although the compositions are blended with carbon black. The resulting non-foamed and foamed conductive silicone rubbers can preferably be used for many purposes because they are free from surface tack and superior in heat resistance and conductivity. The foamable compositions have excellent preservation stability and long pot life.

Claims: A silicone rubber composition for normal-pressure hot-air vulcanisation to a conductive silicone rubber, comprising: (a) organopolysiloxane of the following general formula (1): R 1 a SiO 4-a 2 wherein R 1 is an unsubstituted or substituted monovalent hydrocarbon group having from 1 to 10 carbon atoms and "a" is a positive number of from 1.90 to 2.05, (b) conductive carbon black, and (c) organic peroxide vulcanising agent of the following general formula (2): wherein X is (CH 2 in which "n" is an integer of 2 to 8 or and R 2 and R 3 are independently selected from monovalent hydrocarbon groups having from 3 to 10 carbon atoms and in which R 4 is a methyl, ethyl or phenyl group. A composition according to claim 1 in which the conductive carbon black is blended in an amount of from 5 to 100 parts by weight per 100 parts by weight of the organosiloxane (a). A composition according to claim 1 or claim 2 in which the organic peroxide is blended in an amount of from 0.1 to 5 parts by weight per 100 parts by weight of the organopolysiloxane (a). A composition according to any one of the preceding claims which further comprises (d) a foaming agent. A composition according to claim 4 in which the foaming agent is blended in an amount of from 1 to 10 parts by weight per 100 parts by weight of the organopolysiloxane (a). A composition according to any one of the preceding claims, comprising (e) organosilicone having at least one ≡ SiH group per molecule. A composition according to claim 6 comprising from 0.5 to 5 parts by weight of the organosilicone (e) per 100 parts by weight of the organopolysiloxane (a). A method comprising vulcanising a composition as defined in any one of claims 1 to 7 using normal-pressure hot-air vulcanisation. A method according to claim 8 in which the composition is formed by extrusion or calendering. A conductive silicone rubber obtained by curing a composition according to any one of claims 1 to 7.

Inventors: NAKAMURA TSUTOMU, TAKAHASHI MASAHARU, TSUCHIDA TOMIYOSHI, NAKAMURA, TSUTOMU, TAKAHASHI, MASAHARU, TSUCHIDA, TOMIYOSHI
Applicants: SHINETSU CHEMICAL CO, SHIN-ETSU CHEMICAL CO., LTD.
Application year: 1991
Main classification: H01B1
IPC codes: C08K5, C08K3, H01B1, C08L83