OXIDE SUPERCONDUCTOR AND METHOD OF MANUFACTURING SAID SUPERCONDUCTOR

Abstract: A method of manufacturing an oxide superconductor in such a composition as expressed by a compositional formula La 2-x Sr x CaCu₂ O₆ (0 < x ≦ 0.6), which comprises such processes that calcinating as well as sintering is applied to powdery material mixed in a desired compounding ratio and hot hydrostatic pressing is applied to the sintered product thus obtained in the atmosphere in which the total pressure exceeds 10 mega-pascal, partial pressure of oxygen exceeds 2 mega-pascal, and temperature ranges from 940 to 1600°C. Treatment of the sintered product at HIP ensures not only the manufacture of an oxide superconductor in wide ranges of temperature and pressure conditions but also provision of superconductivity to a product having a wide range of composition satisfying the relation, 0 < x ≦ 0.6. Quenching after HIP treatment also enables the manufacture of an oxide superconductor.

Description: Technical Field This invention relates to a method of manufacturing an oxide superconductor, and more particularly to a method of manufacturing an oxide superconductor having a composition expressed by formula La 2-X Sr X CaCu 2 O 6 (O < x ≦ 0.6). Background Art One of oxide superconductors having compositions expressed by formula La 2-X Sr X CaCu 2 O 6 , which has a composition of La 1.6 Sr 0.4 CaCu 2 O 6 , is manufactured by a known method. In the method, predetermined raw materials such as nitrate, oxalate, and oxide are mixed to form a mixture having a predetermined composition, and then the mixture is preliminarily burned in the flow of oxygen at 900°C for 40 hours. Thereafter, the mixture is sintered in the same atmosphere at 925°C for 72 hours. The resultant sintered body is received in a cooled quartz tube, and then sealed in an airtight manner. This tube is heated at 970°C, thereby making pressurized atmosphere of 20 atm (i.e., 2MPa) by using thermal expansion of oxygen condensed at the time of cooling the tube. The sintered body is kept in the pressurized atmosphere for 48 hours, and then is cooled at 850°C, 750°C, 650°C and 500°C, successively, in units of five hours. Through these steps, a superconductor having a critical temperature of 50K or more is obtained (see R.J. Cara, Nature Vol. 345 (1990), pp. 602 - 604). In the above-described method of manufacturing a superconductor, only a single manufacturing condition is disclosed, under which steps from the preliminary burning to the treatment in a pressurized atmosphere are performed. Further, the composition which the method can make superconductive is limited to La 1.6 Sr 0.4 CaCu 2 O 6 , and hence any other composition (i.e., wherein the value of the Sr content X differs from that of the former composition) cannot have superconductivity. In addition, in a case where a superconductive ceramic is produced by the above method, at least as long as 223 hours are required for performing the steps from the preliminary burning to the treatment in a pressurized atmosphere. Also, since a quartz tube is used for receiving a sintered body in an airtight manner, a batch of composite is greatly limited. Since the treatments are performed under only a single manufacturing condition, temperatures and pressures must be controlled with accuracy. In "Superconductivity and its Applications", 20 April 1988, Hendrix et al. reveal the utility of hot isostatic pressing in densification of bulk oxide superconductor material. The hot isostatic pressing process takes place at around 1200°C at 100 mPa pressure. Higher pressure and temperature capabilities are indicated to be also possible. In Letters to Nature, Vol. 345, 14 June 1990, R. J. Cava et al discuss the superconductivity at 60 K of a lanthanium strontium calcium copper oxide double layer system. The superconductor is produced by preliminary burning of a mixture having the appropriate composition, forming and sintering the mixture, placing the sintered body in a quartz tube, heating and maintaining under pressurized atmosphere and cooling in successive steps of 100°C each in a unit of 5 hours. Disclosure of Invention This invention has been made to solve the above problems, and provides a method of manufacturing, at a temperature and under a pressure within respective wide ranges, a superconductor from an oxide, which has a composition expressed by formula La 2-X Sr X CaCu 2 O 6 and falling within a wide range of 0 < X ≦ 0.6, thereby shortening the manufacturing time and increasing the amount of products. The method of the invention is for manufacturing an oxide superconductor having a composition expressed by formula: La 2-X Sr X CaCu 2 0 6 (0 < x ≦ 0.6) comprising the steps of: preliminarily burning a raw powder having a predetermined composition and sintering the powder to obtain a sintered body; and subjecting the sintered body to hot isostatic pressing at a temperature falling within a range of from 940 - 1220 °C under total pressure of 10 MPa or more and oxygen partial pressure of 2 MPa or more, said hot isostatic pressing temperature being higher than the sintering temperature, and the relationship between the total pressure and the oxygen partial pressure being controlled such that the oxide superconductor satisfies the following formula: Tc on (R) - Tc on (mag) ≧ 3.0 K wherein Tc on (R) is an onset temperature point obtained by measuring electrical resistance at a time of lowering temperature and Tc on (mag) is the superconduction critical temperature obtained by measuring magnetic susceptibility during cooling in a magnetic field. This method provides an oxide superconductor having a composition expressed by formula La 2-X Sr X CaCu 2 O 6 (0 < X ≦ 0.6), containing Ca ≦ 0.25 and Sr ≦ 0.15 in 2a sites, and La ≦ 0.2 and Sr ≦ 0.2 in 4e sites, and having a superconductive critical temperature of 50K or more. The reason why X is limited to a value satisfying 0 < X ≦ 0.6 will be explained. If X = 0, that is, if the invention is applied to an oxide having a composition of La 2 CaCu 2 O 6 , the oxide will not provide superconductivity. Similarly, if X > 0.6, i.e., if the invention is applied to an oxide having a composition of La< 1.4 Sr> 0.6 CaCu 2 O 6 , the oxide will not provide superconductivity. A known method may be applied to selection of raw materials or of the composition ratio thereof. For example, La 2 O 3 , CaCO 3 , SrCO 3 , and CuO may be used as the raw materials, and mixed to have a predetermined composition. Preliminary burning and sintering of the mixture may be performed by a known method. It is preferable to perform the preliminary burning at a temperature of 850 - 950°C. For example, preliminary burning performed for ten hours in the atmosphere of oxygen at a temperature of 900°Cn is repeated several times. Further, sintering is performed for 24 - 72 hours or more in the flow of oxygen at a temperature of e.g. 925 - 1200°C. It is preferable to perform the sintering treatment at a high temperature of e.g. 900 - 970°C if previous hot isostatic pressing is performed at a lower temperature of e.g. 940 - 1070°C within the claimed range of 940 - 1220°C. On the other hand, if the hot isostatic pressing is performed at a higher temperature of e.g. 1070 - 1220°C, the sintering treatment temperature can be set to a value falling within a wide range of e.g. 900 - 1200°C. That is, it is preferable to set the sintering treatment temperature low if the hot isostatic pressing temperature is set high, and to set the former high if the latter is set low. The hot isostatic pressing is performed at a temperature of 940 - 1220°C under a total pressure of 10 MPa or more and an oxygen partial pressure of 2 MPa or more. Though an oxide superconductor can be obtained under temperature and pressure conditions falling outside the above-described ranges, the reason why the conditions are determined as above is that an oxide superconductor, having a composition given by formula La 2-X Sr X CaCu 2 O 6 (X falling within a wide range of more than 0 to 0.6 or less), can reliably be obtained even under other treatment conditions. In view of the above, it is desirable in the invention to set the total pressure to 100 MPa or more, the oxygen partial pressure to 20 MPa or more, and the temperature to 940 - 1220°C. Quenching is performed after the completion of the hot isostatic pressing. The cooling rate is preferably 400°C or more per hour. Brief Description of the Drawings Fig. 1 is a graph, showing a powder diffraction pattern of that oxide superconductor of the invention which is obtained before a HIP treatment; Fig. 2 is a graph, showing a powder diffraction pattern of that oxide superconductor of the invention which is obtained after a HIP treatment; Fig. 3 is a graph, showing a change in the resistance of the oxide superconductor of the invention due to a change in the temperature of the same; Fig. 4 is a graph, showing a change in the magnetic susceptibility of the oxide superconductor of the invention due to a change in the temperature of the same; Fig. 5 is a view, showing a theoretical structure of the composition of the oxide superconductor of the invention; and Fig. 6 is a ternary phase diagram, showing La, Sr, and Ca, samples according to the invention comprising these elements. Best Mode of Carrying Out the Invention The embodiment of the invention will be explained. Samples 1 - 7 were prepared by 15-hour wet blending of La 2 O 3 , CaCO 3 , SrCO 3 , and CuO as raw materials. The samples 1 - 7 had compositions expressed by La 2-X Sr X CaCu 2 O 6 (X = 0, 0.05, 0.1, 0.2, 0.4, 0.6, and 0.7, respectively). The samples were molded after being dried, and were then subjected to preliminary burning at 900°C in air or oxygen flow for ten hours. This preliminary burning step was repeated four times, with a pulverizing/blending step repeatedly performed therebetween. Table 1 shows the compositions of the samples (samples 2 - 6 accord to the invention, and samples 1 and 7 are comparative samples), while table 2 shows phases identified by X-ray diffraction. Subsequently, each of the preliminarily burned powders was molded to have a rectangular form, and then sintered at 900 - 1000°C for 26 - 72 hours. The sintered bodies were subjected to Hot Isostatic Pressing (HIP) in the atmosphere of Ar gas containing O 2 gas. Various HIP treatments were performed by varying total pressure, oxygen partial pressure, and temperature. Further, the HIP treatment was completed by cooling the resultant product after keeping it in the above atmosphere for six hours. Specifically, the cooling rate was 470°C per hour. As a result, an oxide superconductor having a superconduction critical temperature of 50K or more could be compounded. Each of tables 3 - 9 shows results of measurement perform as regards a corresponding one of the samples 1 - 7 obtained after various HIP treatments, in which the sintering temperature ranged from 900°C to 1130°C, and the HIP treatment temperature from 900°C to 1220°C (the total pressure was kept at 100 MPa, and the oxygen partial pressure at 20 MPa). Specifically, each table shows that onset point (T c ON (R)) obtained from the electric resistance at which transition to superconductive state is started, which is obtained from the electric resistance, that end point (T c ZERO (R)) obtained from the electric resistance at which the transition has been completed, and that onset point (T c ON (mag)) obtained from the magnetic susceptibility at which the transition is started (table 3 relating to sample 1, however, shows only (T c ON (R)) and (T c ZERO (R)). Table 10 shows (Tc ON (R)), (Tc ZERO (R)), and (T c ON (mag)) of sample 4 which were obtained by varying the total pressure and oxygen partial pressure of the atmosphere. In the tables 3 - 9, the value put in a left upper portion of each box indicates (Tc ON (R)), the value put in a left lower portion (T c ZERO (R)), and the value in a right lower portion (T c ON (mag)) The composition of each sample was identified from the diffraction pattern of the powder. For example, in a case where sample 4 was subjected to a HIP treatment performed at a temperature of 1020°C (after sintering performed at a temperature of 925°C), under a total pressure of 100 MPa and an oxygen partial pressure of 20 MPa, the sample provided a diffraction pattern as shown in Fig. 1, after the sintering treatment and before the HIP treatment, and provided a diffraction pattern as shown in Fig. 2 after the HIP treatment. T c ON (R) and T c ZERO (R) were measured by detecting a change in the resistance of the sample due to temperature. A change in the resistance of sample 4 due to temperature, for instance, is shown in Fig. 3. T c ON (mag) was measured by detecting a change in the magnetic susceptibility of the sample, which change is shown in Fig. 4. As is shown in table 3, in a sample (X = 0, which does not fall within a range according to the invention), the La 2 CuO 4 phase had superconductivity, as is indicated by mark (x), whereas the (La, Sr, Ca) 3 Cu 2 O 6 phase did not have superconductivity which samples according to the invention had as indicated by mark o . As is shown in table 4, in a sample (x = 0.05, which falls within the range of the invention), the (La, Sr, Ca) 3 Cu 2 O 6 phase had superconductivity as indicated by the mark o . As is evident from table 4, a sintered body obtained by sintering at low temperature can have superconductivity over a wide range of HIP treatment temperature, while it is necessary to perform the HIP treatment at high temperature so as to cause a sintered body obtained by sintering at high temperature, to have superconductivity. Tables 5 - 8 show samples (X = 0.1, 0.2, 0.4, and 0.6, respectively). As is shown in these tables, the samples provided the same results as obtained in the case of the sample (X = 0.05). Further, as is evident from table 9, in a sample (X = 0.7, which falls outside of the range of the invention), the (La, Sr) 2 CuO 4 phase had superconductivity, as is indicated by mark , whereas the (La, Sr, Ca) 3 Cu 2 O 6 phase did not have superconductivity which samples according to the invention had as indicated by mark o . As is evident from table 10, an oxide can have superconductivity when it is subjected to a HIP treatment performed under any total pressure and oxygen partial pressure, if the pressures fall within the ranges of the invention (i.e., total pressure < 10 MPa; oxygen partial pressure < 2 MPa). Then, the inventors identified the crystal structure of an oxide superconductor obtained by the method of the invention. It is theoretically assumed that the crystal structure of the (La, Sr) 2 Cu 2 O 6 having superconductivity has Ca located in 4e sites and La, Sr located in 2a sites (the names of the sites are based on the international table X-ray crystallography; see Fig. 5). However, such a structure has not been identified so far, but it is reasonable to consider that La, Sr, and Ca exist in disorder to some extent. In the embodiment, precision of crystal structure factors was enhanced by the Rietveld method using data obtained by the powder X-ray diffraction, thereby determining compositions in 2a sites and 4e sites. The enhancement of the precision was performed in the following manner: 1. Determination of positions of positive ions (using an isotropic thermal oscillation parameter); 2. Determination of positions of negative ions (using an isotropic thermal oscillation parameter); 3. Enhancement of precision of anisotropic thermal oscillation parameter for the positive ions; 4. Enhancement of precision of anisotropic thermal oscillation parameter for the negative ions (make the parameter to converge up to Rwp = 6.39 %); 5. Fixing the parameters determined in the items 1 - 4, thereby changing the composition of the positive ions. By the use of the above-described procedure, the compositions of the 2a sites and 4e sites are determined. The following are measurement results as regards samples (X = 0.2 and 0.3). In the case of X = 0.2: Sample No. Ts Ta t VIII 2a IX 4e Rwp (%) 1A 950 1020 100 La 0.1 La 0.8735 5.57 Sr 0.0638 Sr 0.0665 Ca 0.8362 Ca 0.06 2A 950 1020 50 La 0.12 La 0.8872 5.31 Sr 0.0802 Sr 0.068 Ca 0.799 Ca 0.0448 3A 925 1120 6 La 0.129 La 0.885 6.33 Sr 0.078 Sr 0.063 Ca 0.793 Ca 0.0523 4A 950 1020 6 La 0.114 La 0.8832 5.33 Sr 0.0824 Sr 0.06 Ca 0.8036 Ca 0.0568 5A 1030 - 6 La 0.148 La 0.894 6.86 Sr 0.07 Sr 0.0645 Ca 0.782 Ca 0.0445 In the case of X = 0.3: Sample No. Ts Ta t VIII 2a IX 4e Rwp (%) 6A 925 1170 6 La 0.189 La 0.755 9.36 Sr 0 Sr 0.15 Ca 0.811 Ca 0.0946 where Ts: sintering temperature (°C); Ta: anneal temperature (°C); t: time, La + Sr + Ca = 1 Fig. 6 shows the three element (La, Sr, Ca)-based crystal structure of each sample (1A - 6A). As can be understood from Fig. 6, Ca ≦ 0.25 and Sr ≦ 0.15 in the 2a sites, and La ≦ e 0.2 and Sr ≦ 0.2 in the 4e sites. The following are examples having 326 structure with precise crystal structure factors: La 1.9 Ca 1.1 Cu 2 O 6 (F. Izumi et al: physica C 157 (1989) 89); La 2 SrCu 2 O 6 (V. Caignaert et al.: Mat. res. bull. 25 (1990) 199), and La 1.8 5Sr 1.15 Cu 2 O 6.25 (P. Lightfoot et al: Physica C 169 (1990) 464). These are all non-superconductors. As described above, superconductors can be obtained by subjecting a sintered body to a HIP treatment performed at a temperature falling within a wide range, under a pressure falling within a wide range. Further, the composition of the material can have superconductivity if it satisfies 0 < X ≦ 0.6. In addition, the superconductor can be produced even by abruptly cooling the material after the HIP treatment, so that the time required for production can be remarkably shortened. COMPOSITIONS OF SAMPLES COMPOSITION No. REAGENTS USED IN BLENDING MOLE RATIO OF ELEMENTS FORMING SAMPLE La Sr Ca Cu O 1 La 2 O 3 , CaCO 3 , CuO 2.0 0.0 1.0 2.0 6.0 2 La 2 O 3 , SrCO 3 , 1.95 0.05 1.0 2.0 6.0 INVENTION CaCo 3 , CuO 3 " 1.9 0.1 1.0 2.0 6.0 INVENTION 4 " 1.8 0.2 1.0 2.0 6.0 INVENTION 5 " 1.6 0.4 1.0 2.0 6.0 INVENTION 6 " 1.4 0.6 1.0 2.0 6.0 INVENTION 7 " 1.3 0.7 1.0 2.0 6.0 RESULTS OF X-RAY DIFFRACTION MADE TO IDENTIFICATE STRUCTURAL PHASE OF SAMPLE OBTAINED AFTER PRELIMINARY BURNING COMPOSITION No. PHASE INDENTIFIED BY X-RAY DIFFRACTION 1 (La, Ca) 3 Cu 2 O 6 , La 2 CuO 4 , CaO 2 (La, Sr, Ca) 3 Cu 2 O 6 (*) 3 (La, Sr, Ca) 3 Cu 2 O 6 (*) 4 (La, Sr, Ca) 3 Cu 2 O 6 (*) 5 (La, Sr, Ca) 3 Cu 2 O 6 (*) CaO 6 (La, Sr, Ca) 3 Cu 2 O 6 (*) CaO 7 (La, Sr) 2 CuO 4 , (La, Sr) 3 Ca 2 O 6 , CaO

Claims: A method of manufacturing an oxide superconductor having a composition expressed by formula: La 2-X Sr X CaCu 2 O 6 (0 < X ≦ 0.6) comprising the steps of: preliminarily burning a raw powder having a predetermined composition and sintering the powder to obtain a sintered body; and subjecting the sintered body to hot isostatic pressing at a temperature falling within a range of from 940 - 1220 °C under total pressure of 10 MPa or more and oxygen partial pressure of 2 MPa or more, said hot isostatic pressing temperature being higher than the sintering temperature, and the relationship between the total pressure and the oxygen partial pressure being controlled such that the oxide superconductor satisfies the following formula: Tc on (R) - Tc on (mag) ≧ 3.0 K wherein Tc on (R) is an onset temperature point obtained by measuring electrical resistance at a time of lowering temperature and Tc on (mag) is the superconduction critical temperature obtained by measuring magnetic susceptibility during cooling in a magnetic field. The method according to claim 1, wherein the step of hot isostatic pressing is performed under a total pressure of 100 MPa or more and an oxygen partial pressure of 20 MPa or more. The method according to claim 1, wherein the raw powder is selected from the group consisting of La 2 0 3 , CaCO 3 , SrCO 3 and CuO. The method according to claim 1, wherein the step of preliminary burning is repeated in the atmosphere of oxygen at a temperature of 850 - 950 °C. The method according to claim 1, wherein the step of sintering is performed in the flow of oxygen at a temperature of 925 - 1200 °C. The method according to claim 1, wherein the step of hot isostatic pressing is performed at a temperature of 1070 to 1220 °C. The method according to claim 1, further comprising the step of quenching at the cooling rate of 400 °C or more per hour after the hot isostatic pressing. The method according to claim 2, wherein the raw powder comprises La 2 O 3 , CaCO 3 , SrCO 3 and CuO; the preliminary burning is carried out at a temperature of 850 - 950 °C and the sintering is carried out in an oxygen atmosphere at a temperature of 925 - 1200 °C. The method according to claim 8, wherein the hot isostatic pressing is carried out at a temperature of 1070 to 1220 °C. The method according to claim 9, which further comprises quenching at a cooling rate of 400 °C or more per hour after the hot isostatic pressuring. An oxide superconductor having a composition expressed by the formula: La 2-X Sr X CaCu 2 O 6 (0 < X ≦ 0.6) wherein Ca ≦ 0.25 and Sr ≦ 0.15 in 2a sites and La ≦ 0.2 and Sr ≦ 0.2 in 4e sites, the oxide superconductor satisfying the following formula: Tc on (R) - Tc on (mag) ≧ 3.0 K wherein Tc on (R) is an onset temperature point obtained by measuring electrical resistance at a time of lowering temperature and Tc on (mag) is the superconduction critical temperature obtained by measuring magnetic susceptibility during cooling in a magnetic field. The oxide superconductor according to claim 11 having a superconductive critical temperature of 50 K or more. The oxide superconductor according to claim 11 selected from La 1.95 Sr 0.05 CaCu 2 O 6 , La 1.6 Sr 0.4 CaCu 2 O 6 , or La 1.4 Sr 0.6 CaCu 2 O 6 .

Inventors: SAKURAI TAKESHI, TANAKA SHOJI, YAMASHITA TORU, YAMAUCHI HISAO, SAKURAI, TAKESHI, TANAKA, SHOJI, YAMASHITA, TORU, YAMAUCHI, HISAO, SAKURAI, TAKESHI, SUPERCONDUCTIVITY RES.LAB., TANAKA, SHOJI, SUPERCONDUCTIVITY RES.LAB., YAMASHITA, TORU, SUPERCONDUCTIVITY RES.LAB., YAMAUCHI, HISAO, SUPERCONDUCTIVITY RES.LAB.
Applicants: HITACHI LTD, INT SUPERCONDUCTIVITY TECH, MITSUBISHI MATERIALS CORP, MITSUBISHI MATERIALS CORPORATION
Application year: 1991
Main classification: C04B35
IPC codes: H01B13, C04B35, H01B12, H01L39, C01G3, C01G1