Optical memory device

Abstract: An optical memory device comprising: a transparent substrate; and a recording film deposited on the transparent substrate, the recording film being formed by preparing a composition in which a diarylethene-type photochromic compound is dispersed in an ultraviolet-curing polyurethaneacrylate resin of solventless type and by curing the composition by an ultraviolet ray irradiation.

Description: The present invention relates to an optical memory device for recording, erasing, and reproducing information by light, and more particularly to an optical memory device which is made of a photochromic material as the recording film. In a conventional optical memory device made of a photochromic material, the photochromic material is dispersed in a polymeric binder. For example, Japanese Unexamined Patent Publication No. SHO 64-87684 describes an optical memory device in which a recording film consisting of a polymeric binder with a photochromic material is formed on the substrate. The formation of the recording film is carried out in accordance with the following procedures: First, photochromic materials, such as derivatives of diarylethene, and polymeric binder, such as PMMA (polymethylmethacrylate) or polystyrene, are dissolved or dispersed in an appropriate solvent; the resultant solution is spread on the surface of the glass substrate or the like by spin coating; and then the solvent is evaporated. However, the conventional constitution and formation process of the recording film mentioned above, needs solvents in which the photochromic material and the polymeric binder are dissolved. Moreover, it also needs an annealing process or like procedure to evaporate the solvent after the solution is spread on the substrate, which makes the film-forming process more complicated. For the polymeric binder, it is desirable to adopt a material which exhibits excellent weather proof properties such as a three dimensionally cross-linked polymer. However, cross-linked polymers cannot be adopted in the conventional constitution because of their insolubility. Consequently, in conventional formation, a photochromic material in the recording film easily deteriorates and shows unsatisfactory photochromic durability In order to overcome such a problem, several methods have been proposed, in which an ultraviolet-curing resin is adopted as the polymeric binder. In case that a typical ultraviolet-curing epoxy resin is adopted as the polymeric binder, however, the durability of the photochromic material also deteriorates in a short time. For this reason, this method was not available for practical use. Although Japanese Unexamined Patent Publication No. 63-210118 describes the making of an optical disk material using as polymeric binder a polycarbonate di(meth)acrylate and/or a polyurethane di(meth)acrylate, that material does not make use of the diarylethene-type photochromic compounds used entirely satisfactorily in previously known optical memory devices. In accordance with the present invention, there is now provided an optical memory device which benefits from the advantages of the known diarylethene-type photochromic compounds and ultraviolet-curing polyurethane acrylate resins. The present invention therefore provides an optical memory device comprising: a transparent substrate; and a recording film deposited on the transparent substrate, the recording film being formed by preparing a composition in which a diarylethene-type photochromic compound is dispersed in an ultraviolet-curing polyurethaneacrylate resin of the solventless type, and by curing the composition with ultraviolet radiation. The present invention is based on the discovery that the film of a diarylethene-type photochromic compound in the ultraviolet-curing resin can be formed from a dispersion in an easy process and shows stable and reversible photochromic stability over a long term. The recording film according to the present invention can be obtained by dispersing the photochromic compound in the ultraviolet-curing resin, spreading the resultant mixture on the substrate surface, and curing using ultraviolet radiation. Therefore, the recording film can be formed in an easy process without using a solvent. Moreover, since cross-linking occurs during curing, the ultraviolet-curing resin has excellent weather proof properties and protects the photochromic compounds from the atmosphere. Furthermore, since the color of the photochromic compound is not stained by the ultraviolet-curing resin, it shows excellent stability over a long period of time. Fig. 1 is a vertical section showing the constitution of an optical memory device of the embodiment. Figs. 2(a) to 2(c) are views illustrating the process of forming the recording film. Fig. 3 is a scheme showing the ratio of the absorbance in the dark at 80 °C to the initial absorbance plotted against elapsed time (day). Fig. 4 is a view showing the absorption spectrum of diarylethene in which the absorbance changes in response to the applied light. An embodiment of the present invention will be described below with reference to Figs. 1 to 4. As shown in Fig. 1, an optical memory device of the present invention comprises a transparent substrate 1 with groove guides 2 formed in a convexo-concave pattern on one side thereof, a recording film 3 deposited on the side of the substrate on which the groove guides 2 are formed, and a reflecting film 4 deposited on the surface of the recording film 3. The recording film 3 consists of an ultraviolet-curing resin in which a photochromic compound is dispersed. The diarylethene-type photochromic compound is adopted as the photochromic compound, while an ultraviolet-curing polyurethaneacrylate resin is adopted as the ultraviolet-curing resin. The substrate 1 is made of glass or plastics such as PC (polycarbonate). The diarylethene-type photochromic compounds mentioned above are compounds represented by the following formula (I) or (II): wherein each of X and Y represents -NR 6 - (R 6 is a lower alkyl group) or a sulfur atom; R 1 represents a lower alkyl; each of R 2 , R 3 , R 4 , and R 5 may represent a lower alkyl, or R 2 and R 3 or R 4 and R 5 together with the carbon atoms to which they are bonded may form a phenyl. The lower alkyl has preferably 1 to 3 carbon atoms, among which a methyl is most preferable. It is possible to adopt a well-known adhesive of the solventless type as the ultraviolet-curing polyurethaneacrylate resin. An example of the resin is prepared by adding a photopolymerization initiator (e.g. benzyl, benzoin, and acetophenone) to a polyfunctional prepolymer which is obtained from the reaction of a polyisocyanate compound with an acrylate having a hydroxyl and which forms the main component of the resultant resin. The compound (I) or (II) can be easily prepared in accordance with the known methods. A representative of the compound (I) is URETHANEACRYLATE SD-301 (available from DAINIPPON INK, Inc.: JAPAN). The combined use of the compound (I) and the compound (II) is also possible. The content of the diarylethene-type photochromic compound in the recording film is preferably 5 to 50 wt%. The thickness of the recording film is preferably 1 to 20 µm. An embodiment will be described below in which 1,2-di(2,3,5-trimethylthienyl) -1,2-dicyanoethene represented by the following formula: is adopted as the diarylethene-type compounds, while URETHANEACRYLATE SD-301 is adopted as the ultraviolet-curing resin. Fig. 2 illustrates the process of forming the recording film 3. At first, the diarylethene represented by the above formula was mixed with the ultraviolet-curing resin in a weight ratio of 1:10, and stirred under weak violet radiation. Then, as shown in Fig. 2(a). the resultant mixture 3' was added dropwise to the surface of the glass substrate 1 on which the groove guides 2 were formed while the glass substrate 1 was rotating at 2000 rpm, and accomplished spin coating (Fig. 2(b)). Next, the ultraviolet-curing resin was cured by ultraviolet radiation (UV light in Fig. 2(c)) from an ultra-high pressure mercury lamp as a light source, so that the recording film 3 consisting of the diarylethene dispersed in the ultraviolet-curing resin was formed on the glass substrate 1 (Fig. 2(c)). The thickness of the substrate 1 was ca. 1.2 mm, while the thickness of the recording film 3 was about 50 µm. As described above, a solvent is not necessary for forming the recording film 3 in the present embodiment. The formation of the recording film 3 was merely completed by applying the ultraviolet radiation thus providing an easy film-forming process. The recording film 3 thus obtained was red and its absorption peak was at 525 nm, as shown in the absorbance curve 7 in Fig. 4. In order to examine the color stability, the wavelength change of the peak absorption was measured in the dark at 80 °C or 10 days. Then, the ratio of obtained to initial peak absorption was plotted against elapsed time (day) to show the curve 5 in Fig. 3. On the other hand, another sample of conventional constitution was prepared for comparison. The control sample was composed of diarylethene dispersed in PMMA. The absorbance of the control sample was measured under the same conditions as described above. The curve 6 in Fig. 3 was obtained from the results of the measurement The control sample was prepared in accordance with the following procedures. The diarylethene was mixed with PMMA having an average molecular weight of 12000 at a weight ratio of 1:10. The mixture was then added to acetone as a solvent, and stirred under weak ultraviolet radiation. After that, the resulting dispersed solution was added dropwise to the surface of the glass substrate on which the groove guides are formed while the glass substrate was rotating at ca. 2000 rpm, and thus accomplished spin coating. The acetone was then evaporated at ca. 70 °C, so that the recording film consisting of diarylethene dispersed in PMMA was formed on the glass substrate. The control sample thus obtained was originally colorless, but it was turned into the colored state by ultraviolet radiation, so that the change in absorbance thereof was measured in the same manner as described above. It is apparent from Fig. 3 that while the absorbance of the control sample decreased until ca. 60% of the initial absorbance after 10 days, the absorbance of the present embodiment maintained ca. 90% of the initial absorbance after 10 days, thereby showing the remarkably improved color stability. The reason for this may be attributed to the satisfactory weather proof properties of the ultraviolet-curing resin adopted in the sample of the present embodiment; that is, cross-linking occured in the ultraviolet-curing resin at cure and thereby realized a more compact structure in the ultraviolet-curing resin, which in turn protects the photochromic material from ambient moisture. Consequently, the photochromic material in the recording film 3 is not easily deteriorated and shows the improved color stability as a result. After the recording film 3 is formed on the substrate 1, the reflecting film 4 (Fig. 1) is deposited on the recording film 3 by vapor deposition. The reflecting film 4 is made of, for example. Al or Au. In the above-mentioned constitution, the photochromic material contained in the recording film 3 reversibly changes between the colorless and colored states by the application of light from the side of the substrate 1. For example, when the diarylethene in the colorless state (the absorbance curve 8 of Fig. 4) is irradiated with an ultraviolet ray at about 400 nm, it changes into the colored state (the absorbance curve 7 of Fig. 4). Conversely, when the diarylethene in the colored state is irradiated with a visible light beam at about 525 nm, it changes into the colorless state again. Hence, at first photochromic material is irradiated with a visible light beam, which is applied to the entire surface of the optical memory device, so as to be colorless. After that, an ultraviolet ray is applied to the surface, irradiated portion of the surface changes into the colored state according to the information and thereby the information can be recorded. Conversely, if a weak visible light beam is applied so that the photochromic material cannot change into the colorless state and then the absorbance is measured from the reflected light, the information can be reproduced. The constitution is provided with the reflecting film 4, so that the radiated light passes through the recording film 3 twice. As a result, the thickness of the recording film 3 in reflection type can be reduced to about half in comparison with that of transmission type. Besides, since an optical system may be provided only on the side of the substrate 1, the compact optical system can be realized in the optical memory device. Moreover, because the substrate is provided with the groove guides 2, information can be recorded and reproduced along the groove guides 2. As for tracking, well-known techniques used in a compact discs or the like can be applied. In the above embodiment, the optical memory device of one-sided structure has been described. However, it is also possible to constitute an optical memory device of doublesided structure by joining two optical memory devices of one-sided structure into an integral body so that the reflecting film 4 of one device is opposed to that of the other device. The optical memory device of the present embodiment is also applicable not only to a disc-shaped optical disc but also to a rectangular optical card. Alternatively, the optical memory device of the present embodiment may be used as transmission type in which the reflecting film 4 is omitted. It is also possible to form a protective film or a moisture-impermeable film on the recording film or the reflecting film of the present invention. For example, an inorganic film of SiO 2 , SiN or AIN, or a moisture-impermeable film of resin may be formed on the recording or reflecting film. Alternatively, an anti-static film may be formed thereon.

Claims: An optical memory device comprising: a transparent substrate; and a recording film deposited on the transparent substrate, the recording film being formed by preparing a composition in which a diarylethene-type photochromic compound is dispersed in an ultraviolet-curing polyurethaneacrylate resin of the solventless type, and by curing the composition by ultraviolet radiation. The optical memory device according to claim 1, wherein the diarylethene-type photochromic compound is a compound represented by the following formula (I) or (II) [wherein each of X and Y represents -NR 6 - (R 6 is a lower alkyl) or a sulfur atom; R 1 represents a lower alkyl; each of R 2 , R 3 , R 4 , and R 5 may represent a lower alkyl, or a combination of R 2 with R 3 or a combination of R 4 with R 5 may represent a phenyl]. The optical memory device according to claim 1 or claim 2, wherein the content of the diarylethene-type photochromic compound in the recording film is 5 to 50 wt%. The optical memory device according to any one of claims 1 to 3, wherein the thickness of the recording film is 1 to 20 µm. The optical memory device according to any one of claims 1 to 4, wherein the transparent substrate is made of glass or polycarbonate. The optical memory device according to any one of claims 1 to 5, wherein a film for reflecting light is formed on the recording film. The optical memory device according to any one of claims 1 to 6, wherein the diarylethene type photochromic compound is 1,2-di(2,3,5-trimethylthienyl)-1,2-dicyanoethene represented by the following formula: A recording film for an optical memory device, the film comprising an ultra-violet cured composition comprising a diarylethene photochromic compound dispersed in an ultraviolet-curing polyurethaneacrylate resin, of the solventless type. An ultra-violet cured composition comprising a diarylethene photochromic compound dispersed in an ultraviolet-curing polyurethaneacrylate resin of the solventless type. A method of preparing a recording film for an optical memory device, the method comprising the steps of: (a) dispersing, a diarylethene photochromic compound in an ultraviolet-curing polyurethaneacrylate resin of the solventless type; and (b) applying the mixture of step (a) as a film on a substrate and subjecting the mixture to ultra-violet radiation to cure the film.

Inventors: MURAKAMI YOSHITERU, OHTA KENJI, VAN KAZUO, MURAKAMI, YOSHITERU, OHTA, KENJI, VAN, KAZUO
Applicants: SHARP KK, SHARP KABUSHIKI KAISHA
Application year: 1991
Main classification: G11B7
IPC codes: G03C1, G03F7, C08F299, G11B7, C09D175