Styryloxy compounds and polymers thereof

Abstract: Styryloxy compound of the formula IV wherein R¹ and R² are H, or one of R¹ and R² is H and the other is methyl; R⁷ and R⁸ (which may be the same or different) are H, C₁-C₅ alkyl or C₁-C₅ alkenyl; or one of R⁷ and R⁸ may be -OR⁶ or C₁-C₅ alkoxy or C₁-C₅ alkenyloxy if R² is not methyl; R⁶ is selected from the group consisting of: where R¹⁰ is C₁-C₅ alkyl; and R¹¹, R¹² and R¹³, which may be the same or different, are H or C₁-C₅ alkyl, are described as new low viscosity liquid styryloxy monomers which can be photocured and which form transparent polymers. They have an advantageous effect in a mixture with 4-allyloxystyrene, and this mixture has a synergistic effect in combination with divinyl ethers of a polyalkylene oxide.

Description: 1. Field of the Invention This invention relates to difunctional styryloxy compounds which are cationically polymerizable, and to polymers thereof, particularly for use in surface coatings, films, inks, adhesives, sealants and the like. 2. Description of the Related Art U.S. Patent 4,543,397, Woods et al., describes polyfunctional cationically polymerizable styryloxy compounds of the formula I or II where R¹ and R² are H, or one of R¹ and R² is H and the other is methyl; R³ and R⁴ are H, lower alkyl or alkoxy if R² is not methyl; R⁵ is a divalent hydrocarbon radical; G is a multivalent organic or inorganic radical free of amine, aliphatic hydroxyl, aliphatic thiol or other groups which interfere with cationic polymerization; and n is an integer of two or more. Polyfunctional telechelic styryloxy monomers of the kind described in U.S. Patent 4,543,397 are generally of high molecular weight. Even so, Example 10 of that Patent describes the preparation of 4-allyloxystyrene of the formula III This compound is cationically active but it forms linear polymers which are purple/blue in color and only 10% insoluble in organic solvents; i.e., little, if any, crosslinking has occurred. US 3,280,088 discloses polymeric compounds having high proportions of aluminium which compounds have more easily controlled flammability and reactivity than aluminium alkyls whilst retaining a high energy content and a process for the production thereof. The process for the preparation of a polymeric composition having a plurality of aluminium atoms in the polymer molecules comprises the step of reacting an aluminium compound with at least one ether compound having only ether and hydrocarbon groups therein being selected from 1) ether compounds having one acetylenic group therein and 2) ether compounds having a plurality of unsaturated groups therein selected from ethylenic and acetylenic groups, the aluminium compound having the formula ALR₃ wherein R is a radical selected from hydrogen and hydrocarbon groups having no more than 24 carbon atoms per group and said aluminium compound being reacted in a portion of at least 0.25 per mole of ether compound. Example II of US 3,280,088 discloses reacting 2 parts triethyl aluminium and ten parts of p-vinyloxystyrene to form the polymeric compound having a high proportion of aluminium. The product is said to burn very rapidly with an intense white flame and has excellent thrust. SUMMARY OF THE INVENTION It is an object of the present invention to provide simple low viscosity liquid styryloxy monomers which can be crosslinked and which form transparent polymers. The invention provides styryloxy compounds of the formula IV wherein R¹ and R² are H, or one of R¹ and R² is H and the other is methyl; R⁷ and R⁸ (which may be the same or different) are H, C₁-C₅ alkyl or C₁-C₅ alkenyl; or one of R⁷ and R⁸ may be -OR⁶ or C₁-C₅ alkoxy or C₁-C₅ alkenyloxy if R² is not methyl; R⁶ is selected from the group consisting of: where R¹⁰ is C₁-C₅ alkyl; and R¹¹, R¹² and R¹³, which may be the same or different, are H or C₁-C₅ alkyl, with the exception of p-vinyloxystyrene. Preferably at least one of R¹¹, R¹² and R¹³ is C₁-C₅ alkyl. In one preferred embodiment, R¹¹ is H and R¹² and R¹³ are both C₁-C₅ alkyl. In another preferred embodiment, R¹¹ and R¹² are H, R¹³ is C₁-C₅ alkyl. A preferred group of compounds within the scope of the present invention are those wherein the styryl moiety (R²CH=C(R¹)-) is para to the -OR⁶ moiety. In such compounds, it is also further preferred that at least one position ortho to the -OR⁶ moiety is unsubstituted, i.e., H. Especially, preferred compounds are those wherein R¹, R², R⁷ and R⁸ are H. The most preferred compounds are of the formula V wherein R⁹ is selected from the group consisting of: -CH=CHCH₃ The compounds of the present invention are monofunctional with respect to the styryl group but are difunctional because of the other cationically active substituent -OR⁶. They are compatible with photoinitiators, which are soluble therein, and they can be photocured to give highly transparent polymeric films with good mechanical properties after short irradiation times; e.g., 10 seconds or less. Thus, low viscosity monomers may be converted to strong crosslinked polymers. In one aspect therefore, the present invention provides a polymerizable composition comprising a styryloxy compound of formula IV together with a photoinitiator. The compounds of the present invention may also be used as reactive diluents; e.g., in epoxy resins, vinyl ether resins, styryloxy resins, etc. As reactive diluents, these compounds may co-react with the other constituent(s) or they may react concurrently with the polymerization of the co-constituent(s). The compounds of the present invention are especially useful as co-constituents in combination with other styryloxy monomers. Additionally, they have a particularly surprising effect in admixture with 4-allyloxystyrene (formula III) in that the addition of even small percentages of one of the compounds of formula IV to 4-allyloxystyrene produces a monomer mixture which polymerizes to a transparent insoluble film. The present invention therefore also provides a polymerizable composition comprising 4-allyloxystyrene of formula III in admixture with a styryloxy compound of formula IV as defined herein, together with a photoinitiator. In general, the styryloxy compound of formula IV is present in an amount of at least 1% by weight, preferably in the range of from about 2.5% to about 35% by weight, most preferably in the range of from about 3% to about 10% by weight, based on the combined weight of the allyloxystyrene and the styryloxy compound of formula IV. It has also surprisingly been found that a synergistic effect is achieved by combining an admixture of 4-allyloxystyrene and a styryloxy compound of formula IV with a vinyl ether monomer, specifically a divinyl ether of a polyalkylene oxide; e.g., the divinyl ether of triethylene oxide. In a further aspect therefore, the present invention provides a photopolymerizable composition comprising: (A) a styryloxy component selected from the group consisting of: (i) 4-allyloxystyrene, (ii) at least one styryloxy compound of formula IV, wherein R¹ and R² are H, or one of R¹ and R² is H and the other is methyl; R⁷ and R⁸ (which may be the same or different) are H, C₁-C₅ alkyl or C₁-C₅ alkenyl; or one of R⁷ and R⁸ may be -OR⁶ or C₁-C₅ alkoxy or C₁-C₅ alkenyloxy if R² is not methyl; R⁶ is selected from the group consisting of: where R¹⁰ is C₁-C₅ alkyl; and R¹¹, R¹² and R¹³, which may be the same or different, are H or C₁-C₅ alkyl, and (iii) a mixture of (i) and (ii), (B) a divinyl ether of a polyalkylene oxide, and (C) a photoinitiator, the ratio of (A):(B) being in the range from 1:9 to 20:1. Preferably, the ratio of (A) to (B) is in the range 2:1 to 9:1, more preferably 1:1 to 4:1, most preferably about 3:1. It is especially preferred that the styryloxy component (A) be a mixture (iii) of the allyloxy styrene (i) and styryloxy compound of formula IV (ii). Within said mixture, the ratio of (i) to (ii) is preferably in the range 20:1 to 1:2, more particularly 7.5:1 to 2:1, especially about 6:1 to 3:1. These ratios are calculated without reference to any small amounts of other components. The divinyl ether of a polyalkylene oxide preferably is of the formula wherein n = 1-6 (preferably n = 2) and m is greater than or equal to 2 (preferably m = 2-10). The preferred compound is the divinyl ether of triethylene oxide, which is commercially available. Although any of the individual compounds above, as well as combinations of A(i) or A(ii) with (B), provide cured compositions with excellent properties, the synergistic combination A(iii) and mixtures thereof with (B) have been found to manifest superior properties, particularly as regards bond strength. The photoinitiator may be any suitable UV cationic initiator. Such UV cationic photoinitiators include salts of a complex halogenide having the formula: where A is a cation selected from the group consisting of iodonium, sulfonium, pyrylium, thiopyrylium and diazonium cations, M is a metalloid, and X is a halogen radical, b equals e minus f, f equals the valence of M and is an integer equal to from 2 to 7 inclusive, e is greater than f and is an integer having a value up to 8. Examples include di-p-tolyl iodonium hexafluorophosphate, diphenyl iodonium hexafluorophosphate, diphenyl iodonium hexafluoroarsenate and UVE (or GE) 1014 (trademark of General Electric), a commercially available sulfonium salt of a complex halogenide. The precise mechanism or mechanisms by which the compounds of the present invention homopolymerize and/or copolymerize, as appropriate, to form a substantially insoluble crosslinked polymer is not known. Although not intending to be bound by any particular theory, it is believed that crosslinking occurs through the unsaturation in the oxy (-OR⁶ or -OR⁹) moiety. Specifically, it is believed that the oxy moiety may crosslink between pendant oxy moieties of other styryloxy monomers or between pendant oxy moiety and free styryl moiety (R²CH=C(R¹)-) as well. In compositions comprising other co-constituents, e.g., 4-allyloxystyrene and/or divinyl ether, the crosslinking will also occur by a co-reaction between the styryl or oxy moieties of the styryloxy compounds of formula IV with co-reactive sites on the co-constituent. Furthermore, although it is believed that there may be some minor degree of a photoinduced claisen-type rearrangement in the styryloxy compounds of formula IV, it is not believed that the resultant monomers participate to a large extent, if at all, in the concurrent photo induced crosslinking reaction. This claisen-type rearrangement does, however, play an important role in a subsequent heat treatment step as described in the copending EP-A-0 490 588 filed on December 6, 1991 in the name of Loctite (Ireland) Limited and entitled "A Method of Forming High-Temperature Resistant Polymers". DESCRIPTION OF THE PREFERRED EMBODIMENTS The invention may be illustrated by reference to the following non-limiting examples, in which all percentages are by weight unless otherwise indicated. Example 1 : 4-Isobutenyloxystyrene 4-Ethyl acetoxy benzaldehyde was prepared by the reaction of one mole of ethyl bromoacetate with one mole of 4-hydroxy benzaldehyde in the presence of one mole of anhydrous Potassium Carbonate in refluxing acetone. This precursor material was vacuum distilled after filtration and concentration of the reaction mixture. The precursor boiled in the range 138-140°C at 0.2 mbar and appeared as a slightly yellowish liquid which crystallized on standing. 4-Isobutenyloxystyrene was prepared from 4-ethyl acetoxy benzaldehyde by Wittig reduction. Thus, to Methyl triphenyl phosphonium bromide (205.6g, 0.576 mole) in anhydrous tetrahydrofuran and under a nitrogen atmosphere, as added Sodium Amide (26g, 0.576 mole plus excess to account for its 90% strength). The mixture was stirred at room temperature and became slightly yellow after 30 minutes. After 3-1/2 hours of stirring, the mixture was deep yellow and 4-ethylacetoxy benzaldehyde (60g, 0.288 mole) was added portionwise. When the addition was complete, the mixture had turned a deep tan color. The mixture was further refluxed for 2-3 hours. On cooling and filtering, the reaction mixture was concentrated and continuously extracted with 40-60°C bp petroleum ether in which reaction by-product triphenylphosphine oxide is sparingly soluble, whereas the desired product has high solubility. On concentration of the extracts, a yellow-brown oil resulted, 10g of which subjected to vacuum distillation. Three fractions resulted which has the following characteristics: Fraction (1): bp ∼ 150°C @ 0.3 mbar; IR (Key bands) split C=O stretch (1760, 1735 cm⁻¹, weak), olefinic = C-H stretch (1660 cm⁻¹ weak), conjugated olefinic = C-H (1625 cm⁻¹ medium). Fraction (2): bp ∼ 170°C @ 0.3 mbar; IR (Key bands) as for (1) with more intense C=O bands and an ill-defined ester pattern -C(O)-O- (1220-1240 cm⁻¹). Fraction (3): bp ∼ 195°C @ 0.3 mbar; IR (Key bands), -CH stretch [2995 (asym.), 2880 (sym.) cm⁻¹], split C=O (1760, 1735 cm⁻¹ intense), conjugated olefin (only) (1625 cm⁻¹, med.), characteristic (1205-1240 cm⁻¹, intense). The ratio for Fraction 1:2:3 was 11:3:1. Fraction 1 was further purified by spinning plate preparative thin layer chromatography with 40-60°C pb petroleum ether as eluant. Six grammes of a water clear low viscosity liquid with a characteristic aniseed smell were thus isolated which was 100% pur by HPLC. GC-MS evidence confirmed a molecular weight of 174; the major abundances from the fragmentation pattern were 159, 120, 91, 77, 65, 55 and 39 m/g z . High field H' N.M.R. (CDC1₃; TMS) assignments were as follows: 2H d 7.33ppm ) H₅, ₅1, ₆, ₆1, J 5,6 = 8.5 H z 2H d 6.90ppm ) 1H dd 6.65ppm H₇, J 7,8 = 17 H z ; J 7,9 = 17 H z 1H dd 5.60ppm H₉, J 9,7 = 17 H z ; J 9,8 = 1 H z 1H dd 5.10ppm H₈ 2H Septet 4.95ppm H 2,1 2H S 4.36ppm H 4,3 3H S 1.78ppm Me₁ The cationically active monomer 4-isobutenyloxystyrene, when formulated with the commercially available cationic photoinitiators known as UVE (or GE) 1014 or, alternatively, Degacure R K126 (the former being products of General Electric Company whilst the latter is a Degussa material), at levels typically of 15 µℓ initiator per gramme of monomer, gave compatible clear compositions of low viscosity which photocured in 5 seconds at 100 mW/cm² exposure at predominantly 366nm to give tack free clear and colorless films with high gloss and flexibility. These films showed a minimum of 75% insolubility after room temperature photocure in repeated solvent extractions over 24 hours with solvents such as toluene, CH₂Cℓ₂ and DMSO. Photocured films (at room temperature) had a glass transition temperature (Tg) at 55°C with a maximum Tan δ amplitude of 0.42 and a dynamic modulus E' ≧ 562 MPa at temperatures of 50°C to -100°C, the last data being measured by Dynamic Mechanical Thermal Analysis (DMTA) at a frequency of 1 Hz. Photocured films at elevated temperature (50°C) show Tg at 67°C with similar modulus performance. An alternative procedure for the direct introduction of isobutenyl groups into phenols employs methylallyl chloride as a reagent (cf. Bartz, Miller and Adams, J. Am Chem Soc. 57, 371, 1935). Thus the Wittig reduction and isobutenyl formation may be separated into two steps by using 4-isobutenyloxy benzaldehyde as a substrate in place of 4-ethyl acetoxy benzaldehyde. Example 2 : 2-Methylpropenyloxystyrene A saturated methanolic KOH solution was prepared, 15g of which was charged into a round bottom flask. To the saturated solution was added approximately 5g of 4-isobutenyloxystyrene (Example 1) and the mixture was heated and stirred for 6 hours at 110°C. During this time, the upper liquid layer turned from yellow to pink. On cooling, the upper liquid layer was easily drawn off from the solid bottom layer and the former was vacuum distilled, boiling in the range 52-60°C at 0.1 mbar. The distillate was a water clear low viscosity liquid with a characteristic aniseed smell. IR analysis indicated the presence of an intense 1670 cm⁻¹ band characteristic of β-substituted vinyl ethers and not present in the parent monomer (Example 1) and also the 960 cm¹ band due to CH wag in substituted vinyl ethers. High resolution H' NMR (CDC1₃; TMS) gave the following assignments: 2H d 7.33ppm ) H₂, ₂1, ₃, ₃1, J 2,3 = 8.5 H z 2H d 6.90ppm ) 1H dd 6.65ppm H₄, J 4,5 = 11 H z ; J 4,6 = 17 H z 1H Septet 6.20ppm H₁, J₁, Me = 1 H z 1H dd 5.60ppm H₆, J 4,6 = 17 H z ; J 5,6 = 1 H z 1H dd 5.10ppm H₅ 6H 2Xd 1.70ppm Me J₁, Me = 1 H z This monomer was cationically active as before, curing tack free in 10 seconds @ 100 mW/cm² @ predominantly 366nm. The resulting polymer was a flexible solid with a Tg of 85°C (1 Hz by DMTA). Example 3 : 4-Allyloxystyrene 4-Allyloxybenzaldehyde was prepared by reaction of allyl bromide on 4-hydroxybenzaldehyde in refluxing acetone in the presence of K₂CO₃. The distilled product was used as a precursor for 4-allyloxystyrene synthesis. To approximately one litre of anhydrous THF and under a N₂ atmosphere was added 265g (0.74 mole) of methyl triphenyl phosphonium bromide in a multinecked flask equipped with an efficient mechanical stirrer. Sodium amide 93-97%, (approximately 0.74 mole) was added and stirring at room temperature continued for about three hours until a deep canary yellow color had formed. 4-Allyloxybenzaldehyde (100g, 0.62 mole) was then added gradulally and the reaction mixture, now tan in color, was subsequently brought to reflux and maintained there for about four hours. The reaction was stopped when TLC analysis showed the aldehyde to be consumed. On cooling, the filtrate was extracted with 40-60°C bp petroleum ether until HPLC analysis showed that less than 40% of the contents was by-product triphenyl phosphine oxide. The concentrated extracts at that stage were subjected to vacuum distillation yielding a water clear liquid of low viscosity, bp≅50°C at 0.6 mbar, with a characteristic aniseed smell. Analysis by GC-MS indicated the liquid to contain two components, a lower boiling component present at 3% and a higher boiling component at 97%. Both were isomeric materials of 160 mass units by MS analysis. The major component was identified as 4-allyloxystyrene by ¹H 270 MHz NMR analysis, IR analysis and GC-MS analysis following separation of a sample of the distillate by preparative TLC. The minor component was identified, by the same techniques and from the same isolation procedure, as 4-propenyloxystyrene (see Example 4). Example 4 : 4-Propenyloxystyrene This material was prepared by base catalyzed isomerization of 4-allyloxystyrene using saturated methanolic KOH in the same way as described in Example 2 (6 hours, 150°C). IR analysis indicated intense 1670 cm⁻¹ absorption due to β-substituted vinyl ether with concomitant disappearance of the 1640 cm⁻¹ allyl olefinic signal present in the precursor, again a strong 960 cm⁻¹ absorbance was noted in the new molecule. The pure material was prepared by vacuum distillation, boiling at 48°C at 0.3mbar (cf. 60°C @ 0.3mbar for 4-alloxystyrene). GC-MS analysis confirmed a molecular weight of 160 with major m/z peaks at 120, 91, 77, 65, 39. High resolution 'H NMR (CDC1₃; TMS) gave the following assignments: 2H d 7.37ppm H₂, ₂1, J 1,2 = 8.5 H z 2H d 6.95ppm H₁, 1¹ 1H dd 6.65ppm H₅, J 5,6 = 11 H z ; J 5,7 = 18 H z 1H dq 6.40ppm H₃, J 3,4 = 6 H z ; J₈, Me = 1.5 H z 1H dd 5.60ppm H₇, J 6,7 = 1 H z ; J 6,7 = 18 H z 1H dd 5.15ppm H₆, J 5,6 = 11 H z ; J 6,7 = 1 H z 1H dq 5.40ppm H₄, J 3,4 = 6 H z ; J₄, Me = 8 H z 3H dd 1.70ppm Me An alternative method of synthesis involves reaction of 1-bromo-1-propene with 4-hydroxybenzaldyde in basic conditions followed by Wittig reduction of the reaction product. The monomer was cationically active, photocuring tack free in about 5 seconds at room temperature when formulated with the photoinitiators mentioned in Example 1. The monomer is compatible with the said photoinitiators giving clear solutions with characteristic aniseed like smell. Example 5 Compositions which photocure cationically to give tack free insoluble films were prepared, starting with the mixture produced in Example 3, i.e., 97% 4-allyloxystyrene and 3% 4-propenyloxystyrene, and increasing the proportion of the propenyl compound up to 100% propenyl compound. The photoinitiator(s) from Example 1 were also present at about 1% level. The presence of the propenyloxystyrene transforms the properties of cationically active allyloxystyrene in that, even at 3% level of 4-propenyloxystyrene, crosslinking occurs and colorless largely insoluble films result. Without propenyloxystyrene, highly colored soluble linear polymers from cationically active allyloxystyrene result. Thus, polymer films photocured from monomer mixtures such as 97% 4-allyloxystyrene and 3% 4-propenyloxystyrene or 91% 4-allyloxystyrene and 9% 4-propenyloxystyrene gave 90% insoluble residues in duplicated solvent extraction tests. Photocured films submitted to DMTA as in Example 1 had glass transition temperatures as follows: % 4-propenyloxystyrene Tg 0 62°C 3 75°C 9 87°C The dynamic modulus E' for the crosslinked copolymers was 200 MPa to 60°C from at least 10°C; all DMTA data being quoted at 1 Hz. As described above, the crosslinking resulting from the photopolymerization of the allyloxystyrene and propenyloxystyrene is believed to be largely due to the cationically active propenyloxy moiety of the 4-propenyloxystyrene. Generally, the styrenic portions of the two components will polymerize to form polystyrene-type chains having the respective allyloxy and propenyloxy moieties pendant thereto. The propenyloxy moieties, as well as other pre-(non-reacted)styrenic (CH₂=CH-) moieties from either monomers. Although less active, it is also possible that the propenyloxy moiety may also crosslink with other pendant allyloxy moieties. In any event, as noted from the compositions of this Example 5, even low amounts of 4-propenyloxystyrene in the admixture results in a high degree of crosslinking as compared to 4-allyloxystyrene without the propenyloxystyrene. Example 6 A mixture of 4-allyloxystyrene and 4-propenyloxystyrene was prepared and analyzed by the GC-MS technique. The instrument used was a Hewlett-Packard 58-90 GC system with an electron impact mass selective detector. The column head pressure was 15 p.s.i. of Helium as carrier, column type was a 25m capillary type of 0.25mm with a BP10 coating. Injection was made at 300°C from Analar (trademark) grade chloromethane. Total ion current traces for the styryloxy mixture indicated three components to be present. Two components are isomeric and have molecular mass of 160 units. In order of ascending boiling points, these two were identified as propenyloxystyrene and allyloxystyrene. The analysis also indicated the presence of a third compound referred to hereinafter as K. The concentration of K in the gas chromatogram was dependent on the temperature of sample injection. Integration of GC data at 300°C injection temperature characterized the styryloxy mixture as 22% propenyloxystyrene, 65% allyloxystyrene and 15% K. Proton NMR run at room temperature in CDC1₃ as solvent and TMS as reference indicated the styryloxy mixture to contain propenyloxystyrene and allyloxystyrene only. Combinations of this styryloxy mixture with the divinyl ether of triethylene oxide, known as DVE-3, commercially available from the GAF Company, when formulated with the initiators described in Example 1, produced photocurable compositions which had superior properties to any of the individual components or to any mixtures outside of the optimized formulation range. Pin-to-glass bond strengths for the respective compositions are summarized below (Table 1). In Table 1, the following abbreviations are used: DVE-3: Divinyl ether of triethylene oxide H o : Composition containing 75% of the styryloxy mixture with 25% of DVE-3 H I : Composition containing 50% of the styryloxy mixture with 50% of DVE-3 H II : Composition containing 25% of the styryloxy mixture with 75% of DVE-3 All percentages being by weight. It will be seen from Table 1 that composition H o gives the best results of all those tested and that the combination of styryloxy type monomers with DVE-3 at the optimized range gives performance much better than either of the styryloxy monomers alone or the DVE-3 alone. Photocurable compositions containing 15 µℓ/gm GE1014 and exposed with 100mW/CM² at predominantly 366nm. Compound/Formulation Pin-to-Glass Bond Strength (dN per sq.cm.) after exposure for: 20 Seconds 40 Seconds 60 Seconds Entry No. Propenyloxystyrene 14 -- -- 1 Allyloxystyrene 12 12 13 2 DVE-3 76 66 72 3 Propenyloxystyrene: DVE-3 at 75:25 59 57 -- 4 at 50:50 49 50 -- 5 at 25:75 69 57 -- 6 Allyloxystyrene: DVE-3 at 75:25 87 84 80 7 at 50:50 75 83 86 8 at 25:75 72 79 90 9 H o 125 125 127 10 H I 95 103 87 11 H II 85 82 103 12 Example 7 In Example 6, a synergistic improvement in bond strengths has been described for 75:25 styryloxy mixture: DVE-3 formulations containing photoinitiators. In the present example, the importance of the relative concentrations of various styryloxy isomers within the 75% styryloxy mixture content of the optimized formulation is described. In order to study the effect of varying the relative propenyloxystyrene and allyloxystyrene contents within the 75% styryloxy content photocurable compositions, a new batch of styryloxy monomers was prepared, characterized and modified. This batch of GC-MS analysis at 300°C injection temperature indicated 22% propenyloxystyrene, 72% allyloxystyrene and 2% of K. The relative proportions of propenyloxystyrene and allyloxystyrene monomers were adjusted by addition of pure materials from separate stock so that nominally 50:50, 30:70, 20:80, 10:90 mixtures of propenyloxy to allyloxy monomers resulted, the K content never exceeded 2%. The said monomer mixtures then formed the 75% component of a mixture with DVE-3 (25%) together with photoinitiator. Pin-to-glass bond strengths were measured after photocuring with various exposure conditions. The results are summarized in Table 2 indicating that the optimum ratio of propenyloxy to allyloxy is around 1:4. Photocurable compositions containing 15 µℓ/gm GE1014 and exposed with 100mW/CM² at predominantly 366nm. Formulation Relative Improvement (%) in Pin-to-Glass Bond Strength for Various Mixtures (Taking Entry 1 as Standard) After Exposure for: 20 Seconds 40 Seconds Entry No. 37.5% Propenyloxystyrene 37.5% Allyloxystyrene 25% DVE-3 100 100 1 22.5% Propenyloxystyrene 52.5% Allyloxystyrene 25% DVE-3 129 111 2 15% Propenyloxystyrene 60% Allyloxystyrene 25% DVE-3 153 154 3 7.5% Propenyloxystyrene 67.5% Allyloxystyrene 25% DVD-3 140 145 4 Example 8 A further batch of styryloxy monomers was prepared and analyzed by the GC-MS technique at 300° injection temperatures as 88% allyloxystyrene and 12% propenyloxystyrene only. The styryloxy monomer mixture was then formulated with DVE-3 in various proportions, together with photoinitiator. Pin-to-glass bond strengths were measured after photocuring for 20 seconds. The results are summarized in Table 3. Photocurable compositions containing 15 µℓ/gm GE1014 and exposed with 100mW/CM² at predominantly 366nm. Formulation DVE-3 Styryloxy Mixture Pin-to-Glass Bond Strengths (dN per sq.cm.) 90% 10% 62 70% 30% 22 50% 50% 69 25% 75% 115 Example 9 Another batch of styryloxy monomers was prepared and analyzed by the GC-MS technique at 80% allyloxystyrene and 20% propenyloxystyrene only. A formulation consisting of 75% styryloxy monomer mixture, 25% DVE-3 and 15 µℓ/gm⁻¹ GE1014 was photocured for 20 seconds at 100 mW/cm² (366nm). Pin-to-glass bond strengths were measured and results in excess of 100 dN/sq.cm. were obtained. Certain of the photocured compositions produced as described above may be further crosslinked by treatment with heat to form high-temperature resistant polymers, as described in copending EP-A-0 490 588 filed on December 6, 1991 in the name of Loctite (Ireland) Limited and entitled "A Method of Forming High-Temperature Resistant Polymers". Obviously, other modifications and variations to the present invention are possible and may be apparent to those skilled in the art in light of the above teachings. Thus, it is to be understood that such modifications and variations to the specific embodiments set forth above are to be construed as being within the full intended scope of the present invention as defined by the appended claims.

Claims: Styryloxy compounds of the formula IV wherein R¹ and R² are H, or one of R¹ and R² is H and the other is methyl; R⁷ and R⁸ (which may be the same or different) are H, C₁-C₅ alkyl or C₁-C₅ alkenyl; or one of R⁷ and R⁸ may be -OR⁶ or C₁-C₅ alkoxy or C₁-C₅ alkenyloxy if R² is not methyl; R⁶ is selected from the group consisting of: where R¹⁰ is C₁-C₅ alkyl; and R¹¹, R¹² and R¹³ which may be the same or different, are H or C₁-C₅ alkyl, with the exeception of p-vinyloxystyrene. Compounds according to claim 1 wherein at least one of R¹¹, R¹² and R¹³ is C₁-C₅ alkyl. Compounds according to claim 1 or 2 wherein R¹, R², R⁷ and R⁸ are H. Compounds according to any of claims 1 to 3 wherein the styryl moiety (R²CH=C(R¹)-) is para to -OR⁶. Compounds according to claim 4 wherein at least one position ortho to -OR⁶ is unsubstituted. Compounds according to any of claims 1 to 5 which are of the formula V wherein R⁹ is selected from the group consisting of: -CH=CHCH₃ A polymerizable composition comprising a styryloxy compound of formula IV as defined in claim 1 together with a photoinitiator. A polymerizable composition comprising 4-allyloxystyrene in admixture with a styryloxy compound of formula IV as defined in claim 1 together with a photoinitiator. A composition according to claim 8 wherein the styryloxy compound of formula IV is present in an amount of from about 1 to about 99%, preferably about 2.5 to about 35%, more preferably about 3 to about 10% by weight based on the combined weight of 4-allyloxystyrene and the styryloxy compound of formula IV. A photopolymerizable composition comprising: (A) a styryloxy component selected from the group consisting of: (i) 4-allyloxystyrene, (ii) at least one styryloxy compound of formula IV, wherein R¹ and R² are H, or one of R¹ and R² is H and the other is methyl; R⁷ and R⁸ (which may be the same or different) are H, C₁-C₅ alkyl or C₁-C₅ alkenyl; or one of R⁷ and R⁸ may be - OR⁶ or C₁-C₅ alkoxy or C₁-C₅ alkenyloxy if R² is not methyl; R⁶ is selected from the group consisting of: where R¹⁰ is C₁-C₅ alkyl; and R¹¹, R¹² and R¹³, which may be the same or different, are H or C₁-C₅ alkyl, and (iii) a mixture of (i) and (ii) above, (B) a divinyl ether of a polyalkylene oxide, and (C) a photoinitiator, the ratio of (A):(B) being in the range from 1:9 to 20:1, preferably in the range from 2:1 to 9:1 and more preferably from 1:1 to 4:1. A composition according to claim 10 wherein the styryloxy compound is a mixture (iii) of 4-allyloxystyrene (i) and a styryloxy compound of formula IV (ii). A composition according to claim 11 wherein the ratio of (i):(ii) is from 20:1 to 1:2, preferably from 7.5:1 to 2:1 and more preferably from 6:1 to 3:1. A composition according to any of claims 10 to 12 wherein the divinyl ether of a polyalkylene oxide is of the formula: wherein n = 1-6 and m is greater than or equal to 2. A composition according to claim 13 wherein n is 2 and m is 2 to 10.

Inventors: BURKE JOSEPH, MCARDLE CIARAN BERNARD, WOODS JOHN G, BURKE, JOSEPH, MCARDLE, CIARAN BERNARD, WOODS, JOHN G.
Applicants: LOCTITE IRELAND LTD, LOCTITE (IRELAND) LTD.
Application year: 1991
Main classification: C07C43
IPC codes: C08F2, C08F290, C08F16, C08F299, C08F12, C07C43