Nylon pultrusion process

Abstract: Disclosed herein is a process for the reactive pultrusion of pultruded articles comprising a reinforcing material (10) and a polyamide matrix which process comprises impregnating a reinforcing material (10) with a polyamide forming reaction mixture and then pultruding the impregnated reinforcing material (10) through a die (17) while polymerizing the polyamide forming reaction mixture to form a polyamide matrix, wherein the temperature of the material being pultruded is at least about at the lower end of the melting range of the polyamide.

Description: The invention relates to the RIM pultrusion of a nylon forming material and a fibrous reinforcing material and the resulting pultruded articles. BRIEF DESCRIPTION OF THE PRIOR ART RIM pultrusion of nylon forming materials is taught in the following: U.S.P. 4,635,432 to C. R. Wheeler using wire as the fibrous reinforcing material; G. E. Rotter, Master Thesis entitled RIM PULTRUSION PROCESS, Case Western Reserve University, January 12, 1988; a paper entitled RIM-PULTRUSION OF THERMOPLASTIC MATRIX COMPOSITES, by H. Ishida and G. Rotter distributed to attendees at the 43rd Annual Conference of SPI; European Patent Office published application 0 384 063 naming H. Ishida as the inventor; and Ishida et al., Polymer Engineering & Science, mid-May 1991, Volume 31, No. 9, pages 632 to 637. In the prior art the pultrusion is carried out using die temperatures of about 160°C which is well below the melting point (MP) of nylon 6 which is in the range of from 195 to 225°C as reported by M. I. Kohan in Nylon Plastics, A. Wiley - Interscience Publication, John Wiley & Sons, p.88 (1973). Kohan reports a melting point range of 210 to 225°C for monomer extracted nylon 6 and a range of 195 to 225°C for unextracted nylon, i.e. nylon 6 which contains residual monomer. Other nylons also have a melting range rather than a specific melting point. SUMMARY OF THE INVENTION The invention comprises a process for the reactive pultrusion of pultruded articles comprising a reinforcing material and a polyamide matrix which process comprises impregnating a reinforcing material with a polyamide forming reaction mixture and then pultruding the impregnated reinforcing material through a die while polymerizing the polyamide forming reaction mixture to form a polyamide matrix, wherein the temperature of the material being pultruded is at least about at the lower end of the melting range of the polyamide. The temperature of the material being pultruded is preferably at least 2 to 5 °C above the lower end of the melting point range of the polyamide. The polyamide matrix is preferably based on caprolactam and a polyamide modifier. The resulting pultruded articles have better surface and physical properties than comparative samples pultruded at temperatures below the melting point of the polyamide according to the teaching of the prior art. The terms polyamide and nylon are used interchangeably in the specification. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 shows a typical RIM pultrusion apparatus comprising feed systems for the reactive raw materials, a mixing element for combining the raw materials, feed systems for the reinforcing elements, a die and a puller. Figures 2 to 3 are Differential Scanning Calorimeter (DSC) curves showing the peaks obtained on samples pultruded at different temperatures. Figure 4 is a DSC curve obtained by reheating the same material used to obtain the DSC curve in Figure 2. Figure 5A is a typical temperature profile curve for the pultrusion operations in the pultrusion zones shown in Figure 5B. DESCRIPTION OF THE PREFERRED EMBODIMENTS The preferred reaction injection resin systems used in the present invention comprise a monomer, an initiator, a catalyst and optionally polymeric type components which copolymerize with the monomer. Examples of monomers suitable for use in the present invention include but are not limited to ε-lactams and ε-lactones with caprolactam being the preferred monomer. Examples of initiators include but are not limited to caprolactams such as adipoylactams; isocyanates and blocked isocyanates; isophthaloyl biscaprolactam, terephthaloyl biscaprolactam; esters such as dimethylphthalate-polyethylene glycol; prepolymers of polyols or polydienes in combination with bis acid chlorides; carbonylbiscaprolactam made by reacting phosgene with caprolactam; phosphoryl initiators of the type described in U.S. Patents 4,649,177; 4,645,800; 4,617,355 and 4,628,075. Examples of catalysts include but are not limited to lactam magnesium halides, alkali metal adducts of caprolactam, e.g. sodium, potassium and lithium caprolactamates; aluminum or magnesium caprolactam with added magnesium bromide; alkoxides and the like. Optional polymeric type components which copolymerize with the monomers include polyoxypropylene polyol, polyoxyethylene polyol, polycaprolactone, polytetrahydrofuran, polybutadiene polyol, polyisoprene polyol, polyisobutylene polyol, poly(C 1 -C 8 alkylene acrylate), poly(C 1 -C 4 dialkylene siloxane) polyol, poly(ethylene-co-propylene)polyol, poly(ethylene-co-carbon monoxide) polyol, and the like. These components form block copolymers with the polyamide. In general, the modifiers are amorphous and elastomeric; that is, these segments would manifest a glass transition temperature below 10°C., preferably below -10°C. Preferred modifiers are poly(propylene oxide), polytetrahydrofuran, poly(dimethyl siloxane), and polybutadiene, with poly(propylene oxide) particularly preferred. The foregoing components are taught by Hedrick et al in U.S. Patents 3,862,262; 4,031,164; 4,034,015; 4,546,147; 4,581,419; 4,584,344; 4,587,305; 4,590,243 and 4,590,244 The reinforcing materials used in the present invention may be in the form of filaments, fibers, strands, woven mats, nonwoven mats and the like. The reinforcing materials may be glass, carbon, metal, phosphate, ceramic or polymeric fibers and may contain sizes or coatings to promote bonding of the resin component to the reinforcing material. Pultrusion apparatus for use in RIM pultrusion is well known in the art and is disclosed in U.S.P 4,635,432 to C.R. Wheeler and EPO application 0 384 063 to H. Ishida. Referring to Figure 1, feed tanks A and B are used to feed molten initiator/monomer and molten catalyst/monomer combinations into a mixing zone 26. The mixed components are then conveyed through an injection port 35 into a heated resin impregnation chamber 28 where the heated reinforcing material 10 which is being fed into the impregnation chamber 28 from a source 12 is impregnated with the resin forming mixture. The reinforcing material is heated by heating means 11 prior to being introduced into the impregnation chamber 28. The resin impregnated reinforcing element 16 is then conveyed through a heated die 17 which is equipped with heating elements 13. The pultruded article 18 is then conveyed through a cooling zone 19 and the cooled pultruded article is pulled from the die 17 by conventional pulling means 20. In a preferred embodiment, the impregnation chamber 28, die 17 and cooling zone 19 form a single passageway. In other embodiments the foregoing elements may be separate from one another. Care should be taken to insure that the polymer forming reactants and the reinforcing material are dry, that is substantially free of water which would interfere with the polymerization reaction. Methods for drying these materials or for excluding water from dry materials are well known in the art and need no further discussion here. Conditions such as line speed and dwell time in the die and die temperatures are selected to insure that the material being pultruded reaches a temperature that is above the lower end of the melting range of the polyamide formed in the pultrusion operation. This may be done in the reaction polymerization step or preferably after the polyamide material has been formed. Preferably after the polyamide forming reaction is substantially complete the newly formed polyamide is heated to a temperature which is at least 2 to 5°C above the lower end of the MP range of the polyamide. More preferably, the temperature is at about the upper end of the melting range. The pultruded article is then cooled below the lower end of the melting range of the nylon. Cooling can take place in the exit region of the die or outside the die between the die exit and the pullers. In a preferred embodiment the pultruded article is cooled while under confinement in a die or similar structure or while under tension from the pullers. EXAMPLES 1 TO 10 In Examples 1 to 10 below the monomer used was caprolactam having a melting point of about 69°C; the initiator used was isophthaloyl bis caprolactam; and the catalyst used was a magnesium bromide caprolactam adduct with a melting point of about 70°C. The initiator was prepared by adding one (1) mole of bisacyldichloride to two (2) moles of caprolactam. The HCl formed was neutralized with an amine and the product was recovered. The magnesium bromide adduct of caprolactam was obtained from Grant Chemical Division of Ferro Corporation of Baton Rouge, Louisiana. The concentration was 1.0 moles of magnesium bromide per kilogram of caprolactam or about 21.6 wt.% of adduct with 78.4 wt.% of caprolactam. Referring to Figure 1, Feed tanks A and B which have a capacity of about 25 liters and which are equipped with agitation, heating, pumping and metering means were charged as follows: Feed Tank A wt. % initiator 1.2 monomer 48.8 Feed Tank B catalyst 8.7 monomer 41.3 All of the components are solid waxy flakes at room temperature. The feed tanks and feed lines were maintained above 80°C to keep the monomer molten. The materials in the feed tanks were agitated and the tanks were blanketed with water-free nitrogen. In Examples 1 to 10 below, the glass fibers used were 10 strands of 4800 TEX from Vetrotex. Molten solutions of Feeds A and B were pumped to a mixing zone 26 to merge the streams and initiate the polymer forming reaction. The reaction mixture was conveyed through a static mixer (not shown) and into the impregnation chamber 28. The glass fibers 10 were heated to about 250°C in the fiber heating zone 11 prior to being introduced into the impregnation chamber 28 where the fibers are wetted and impregnated with the resin forming reaction mixture. Then the impregnated reinforcing material was conveyed into the heated die 17 which was in communication with the impregnation chamber 28. The die used was about 50 cm long and was fitted with plate heaters 13 and thermocouples (not shown) to measure temperature. The pultruded rods were cooled under confinement in the cooling section 19 of the die. The line speed was estimated to be about one meter/minute with possible range of from 0.5 to 1 m/minute during the run. The pultruded rods, which were about six millimeters (6mm) in diameter, were cut into 2.5 meter lengths for evaluation and testing. The glass content of the rods was about 75% by wt. The rods were examined for surface appearance, feel to the touch, flexibility by manually bending. The rods were also dropped onto a concrete floor from a height of about 20 centimeters and evaluated for solidity and integrity by the sound of the rods impacting the floor. An overall rating of poor, fair or good was then assigned to the rod. These ratings along with the color of the rod are tabulated in Table I below: SUMMARY OF EXAMPLES 1 TO 10 Example Temp Range °C Rating Color 1 134 Poor White 2 134 Poor White 3 160 Fair Light buff 4 160 Fair Light buff 5 160 Fair Light buff 6 180 Fair Light brown 7 250 Good Darker brown 8 225 Good Darker brown 9 230 Good Darker brown 10 230 Good Darker brown The pultruded rods were cut at 2.5 meter intervals. Thus Example 1 was the first 2.5 meter section pultruded, Example 2 was the length from 2.5 to 5 meters and so on to Example 10 at 25 meters. A review of the Examples 1 to 10 indicates that as the pultrusion die temperature increases the rod had a better surface appearance, better feel and fewer free fibers on the surface. When dropped onto a concrete floor, the rods of Examples 7 to 10 gave a very solid ringing sound while those of Examples 1 to 4 sounded dull. In the examples shown, as die temperature increases, less force was required for pulling and there was less resin buildup in the die. EXAMPLES 11 TO 15 The resin forming systems used in Example 1 to 10 and pultrusion procedures were used in Examples 11 to 15. The glass fiber used in Examples 11 and 12 was 9 strands 4800 TEX X9 while 19 strands of 2400 TEX were used in Examples 13 to 15. The temperature profile for the pultrusion die was as shown in Table II below. SUMMARY OF EXAMPLES 11 TO 15 Example Length (m) Line Speed m/min Set Temp Range, °C 11 7.5 0.3 235/240 12 10.0 0.3 240/245 13 117.5 0.5 230/250 14 122.5 0.5 230/250 15 155.0 0.9 230/250 The length (m) indicates the particular 2.5 m segment of the pultruded rod which was selected for testing. The glass content of the rods was about 75% by wt. All of the rods were rated good. They had good surfaces, few free fibers and were very smooth and were solid sounding in the drop test. The color ranged from green brown to brown with increasing thermal exposures. In the pultrusion run from which Examples 11 to 15 were obtained, the set temperature was as high as 280°C. However the best rods were obtained at a set temperature of about 250°C. EXAMPLES 16 TO 18 In another series of tests, rod samples prepared using a die temperature of about 160°C were annealed and the ILSS measured. One sample was used as a control, while two other samples were annealed at 230°C for fifteen minutes, and at 130°C for 20 hours. The rod in Example 17 was annealed while being confined in a teflon sleeve while the rod of Example 18 was unconfined. Results are shown in Table III below. EFFECT OF ANNEALING ON INTERLAMINAR SHEAR STRENGTH Example Annealing Temp. °C Annealing Time (Hours) Rating 16 Control -- -- Fair 17 230 0.25 Good 18 130 20 Poor One explanation for the superior properties obtained in pultruded rods prepared by the processes of the present invention is that with the polymerization occurring at 160°C, the polymer chains are allowed to crystallize out of the reaction mixture and are instantly frozen. The polymer chains, which come out of the reaction mixture as they increase in molecular weight, become insoluble in the reaction mixture. When the newly formed nylon in the die is heated above its melting point the nylon crystallizes as a solid out of the melt and exhibits better properties. However, applicants are not to be bound by this theoretical explanation. Figure 5A shows a temperature profile of the pultrusion material in the apparatus shown in Figure 5B using the processes of the present invention and polyamide forming compositions used in the working examples above. A thermocouple was used in the die to obtain the profile. The fibers are heated to about 165°C in the heating means 11 prior to being impregnated in the impregnation chamber (not shown) with the molten polyamide forming material (resin) which is at about 80°C. The polymerization reaction continues in the die 17 (50 cm long) which is at 240°C. The material being pultruded reaches a temperature of about 240°C prior to leaving the die 17 and passing into the cooling zone 19 where the article is cooled under confinement. Cooling under confinement improves the surface of the rod and minimizes the tendency of the rod to break upon bending. Further work was carried out to characterize the physical properties of the pultruded rods prepared in Examples 1 to 18 above using the following tests: TEST METHODS ILSS is determined according to ASTM D 4475-85 on triplicate samples except for Example 14 where duplicates were tested. DSC - differential scanning calorimetry measurements were run on a Perkin Elmer Model DSC-2 which was interfaced to an IBM PC NEC Multi Sync 2A using thermal analysis software by MC 2. DSC samples were prepared by slicing the pultruded rods into 0.25 mm slices using an electric radial saw with a diamond blade. To keep the sample from heating a steady stream of chilled nitrogen gas (-20°C) was directed on the sample and blade. The slices were then sealed in aluminum pans for DSC analysis. The rate of heating was 20.00 degrees Centigrade per minute. % Crystallinity - The crystallinity of the nylon is determined from the DSC curve by calculating the area of the melting peak above a baseline drawn between the start and end of the peak. The integrated area is then converted to units of energy per gram of sample using the heating rate and sample weight. This energy per gram is the heat of fusion for the sample. For glass-filled materials, the sample weight used is that of the matrix only, and this weight is calculated from the matrix/fiber ratio determined by independent means. The matrix heat of fusion is then divided by the heat of fusion for a pure nylon-6 crystal, and the resulting fraction multiplied by 100 gives the percent crystallinity for the matrix. R. L. Miller and L. E. Nielsen list 159 and 184 J/gm as the heat of fusion for nylon 6 [see Appendix I, page 524 to P.H. Geils "Polymer Single Crystals", Interscience (1963)]. For the pultruded composites described in Examples 5 and 10 below a mean value of 167 J/g (40calg) was used. Referring to Figure 2, the area under the peak is given on the graph as 14.63 cal /gm, and so the crystallinity is calculated as (14.63/40) x 100 = 36.6% (The sample weight of 2.840 mg had already been corrected for glass content). The % crystallinity for Example 10 was calculated to be about 24%. Referring to Figures 2, 3 and 4, Figure 2 shows a DSC curve having two peaks for the rod prepared in Example 5 which was pultruded using a die temperature of about 160°C. Figure 3 shows a DSC curve having a single peak for the rod prepared in Example 10 using a die temperature of about 230°C. Figure 4 shows a DSC curve for the sample (Example 5) used to generate the curve in Figure 2. Either during the initial heating for the DSC curve (Figure 2) or upon reheating to generate the curve in Figure 4, the polyamide component became less crystalline and now exhibits a single peak. The DSC curves and % crystallinity indicate that pultruding above the lower end of the melting range gives a polyamide that has a crystalline structure different from that obtained when using the prior art processes at about 160°C. The summary of ILSS values set forth below suggest that, in addition to a better surface appearance and feel, the processes of the present invention provides improved strength and toughness. SUMMARY OF ILSS VALUES Example Die Temp. ILSS Standard Deviation 3 160 29.3 1.20 4 160 31.3 0.44 5 160 43.2 3.22 9 230 48.5 0.20 10 230 48.2 0.44 11 235/240 52.2 0.80 12 240/245 51.3 0.80 13 230/250 49.2 1.11 14 230/250 45.2 0.36 15 230/250 45.0 1.66 16 160 47.4 * 17 160 41.6 * 18 160 37.6 * * not determined The results with Examples 3, 4, 5, 9 and 10 show an increase in ILSS with increasing die temperature. The results with Examples 11 to 15 show a decrease in ILSS with increasing line speeds. This indicates that a longer residence time in the die may be required in order to heat the material being pultruded above the lower end of the melting range of the polyamide.

Claims: A process for the reactive pultrusion of pultruded articles comprising a reinforcing material and a polyamide matrix which process comprises impregnating a reinforcing material with a polyamide forming reaction mixture and then pultruding the impregnated reinforcing material through a die while polymerizing the polyamide forming reaction mixture to form a polyamide matrix, wherein the temperature of the material being pultruded is above the lower end of the melting range of the polyamide. A process as in claim 1, wherein the temperature of the material being pultruded is at least 2 to 5°C above the lower end of the melting point range of the polyamide. A process as in claim 2, wherein the temperature of the material being pultruded is at the upper end of the melting point range of the polyamide. A process as in claim 1, wherein the polyamide matrix is based on caprolactam. A process as in claim 1, wherein the polyamide matrix is based on caprolactam and a polyamide modifier. A process as in claim 1 wherein the pultruded article is cooled before leaving the die. A process as in claim 1 wherein the pultruded article is cooled under confinement after leaving the die.

Inventors: BINSE PATRICK MARCEL PIERRE HE, CAMPENER CHRISTIAN BERNARD GUI, KEATING PHILIP BARRIE, BINSE, PATRICK MARCEL PIERRE HENRI, CAMPENER, CHRISTIAN BERNARD GUISLAIN, KEATING, PHILIP BARRIE
Applicants: SOLUTIA EUROP NV SA, SOLUTIA EUROPE N.V./S.A.
Application year: 1991
Main classification: B29C70
IPC codes: C08G69, B29C70, B29C67, C08J5