FLUORINATION PROCESS

Abstract: Process for the preparation of fluorinated alkanes by contacting a starting material of halogenated alkene or alkane with 1 to 150 molar equivalents based on catalyst of HF, 1 to 30 molar equivalents based on catalyst of a dehydrating agent and less than 100 molar equivalents based on catalyst of a starting material, the catalyst being selected from niobium oxide or tantalum oxide, at a temperature of 0 DEG C to 185 DEG C. The preferred dehydrating agent is a combination of chlorosulfonic acid and thionyl chloride.

Description: TITLE FLUORINATION PROCESS FIELD OF THE INVENTION This invention relates to a process for the preparation of fluorinated alkanes by contacting halogenated alkenes or alkanes with hydrogen fluoride (HF) in the presence of niobium pentoxide (Nb2θs) or tantalum pentoxide (Ta2θs) and chlorosulfonic acid (HOS0 Cl) and thionyl chloride (S0C1 2 ) . BACKGROUND OF INVENTION A. E. Feiring, Journal of Fluorine Chemistry, 13, 7-18 (1979) discloses the use of tantalum pentafluoride as a catalyst for the addition of hydrogen fluoride to tetra- and trichloroethane and related compounds. The catalyst is also useful in fluorine-chlorine exchange reactions. However, under the conditions of the batch experiments [HF/CCl2=CCl2 = 2.5, temperature = 150 * C, reaction time = six hours] catalysts such as BF3, aCls, a2θ5, CoF 3 , V2O5, ZrCl4, NbCls, HgO, and WClβ showed no catalytic activity for the addition of HF to tetrachloroethylene. The use of tantalum pentafluoride as a catalyst for the addition of hydrogen fluoride to unsaturated compounds has been disclosed and claimed by Feiring in U.S. 4,258,255. The use of dehydrating agents to prepare anhydrous TaFs has been disclosed and claimed in Kim U.S. 4,124,692. The need to provide an economically attractive process to produce highly fluorinated, hydrogen-containing alkanes useful as alternatives to current products for refrigerants, blowing agents, etc. has sparked interest in this area. This invention provides a low cost process for the preparation of fluorinated alkanes made by catalyzed HF addition to olefins and/or fluorine for chlorine exchange on chlorinated alkanes using a system comprised of Ta2θs or Nb2θs, a dehydrating agent(s), e.g., HOSO2CI (chlorosulfonic acid), and SOCI2 (thionyl chloride) and excess HF. SUMMARY OF THE INVENTION The process of this invention comprises contacting at a temperature from about 0*C to about s 185"C a starting material selected from halogenated alkenes or halogenated alkanes of the following formulas R 1 R 2 C=CR 3 R 4 and R 5 R 6 R 7 R 8 C wherein Rχ f R2 R3, R4, R5, R 6, 7 and R 8 are H, F, Cl, Br, or C x Z2χ+i, wherein Z is H, F, Cl or Br, x is an integer from 1-10, and wherein at least one of Ri - R4 and R5 - R $ is Br or Cl or a bromine or chlorine-substituted group, with HF and at least one dehydrating agent, in the presence of at least one catalyst selected from Nb θ 5 and Ta2θ5, to produce reaction products, the mole ratio of HF to Ta or Nb being from 1 to 150, the mole ratio of the dehydrating agent to Ta or Nb being from 1 to 30, and the mole ratio of the starting material to Ta or Nb being less than 100; and removing the reaction products from contact with the catalyst and isolating a fluorinated alkane having at least one more fluorine atom than the starting material. The preferred process of this invention comprises contacting at a temperature from about O'C to about 185*C a starting material selected from halogenated alkenes or halogenated alkanes of the following formulas R 1 2 =C 3 R 4 and R 5 6 7 8C wherein Ri, R , R 3 R 4, R 5, R 6, R 7 and Re are H, F, Cl, Br, or C x Z2χ+i, wherein Z is H, F, Cl or Br x is an integer from 1-10, and wherein at least one of Ri - R4 and R5 - R- is Br or Cl or a bromine or chlorine-substituted group, with HF, HOSO2CI and SOCI2, in the presence of at least one catalyst selected from b θ5 and Ta2θs, to produce reaction products, the mole ratio of HF to Ta or Nb being from 1 to 150, the mole ratio of HOSO2CI to Ta or Nb being from 1 to 30, and the mole ratio of SOCI2 to Ta or Nb being from 0.5 to 20; and the mole ratio of the starting material to Ta or Nb being less than 100; and removing the reaction products from contact with the catalyst and isolating a fluorinated alkane having at least one more fluorine atom than the starting material. DETAILS OF THE INVENTION The fluorinated alkane produced in accordance with the instant invention has at least one more, and preferably two or more fluorine atoms than the halogenated alkene or alkane starting material and at least one of the fluorine atoms is the result of the halogen exchange reaction. For example, when the starting halogenated alkene or alkane is CCl2=CCl2 or CI3CHCI2, respectively, the more favored products will be CF3CHCI2 and CF2CICHCI2 and when the starting halogenated alkene or alkane is Cl 2 C=CHCl or CCI 3 CH 2 CI, respectively, the favored product is CF 3 CH 2 CI. When the starting halogenated alkene or alkane is Cl 2 C=CH 2 or CI 3 C-CH 3 , respectively, the product can be CFCI 2 CH 3 , CF 2 CICH 3 , and CF 3 CH 3 , depending on process conditions. To achieve the optimum degree of halogen exchange, the halogenated organic starting material is contacted with a metal oxide, preferably tantalum pentoxide or niobium pentoxide, and the mole ratio of halogenated alkane or alkene to Ta or Nb is less than 100. The catalyst, preferably tantalum pentoxide, is a commercially available and relatively inexpensive (compared for example to tantalum pentachloride or tantalum pentafluoride) crystalline solid and can be used alone or on a support such as carbon or fluorinated alumina. Other forms of oxides of niobium or tantalum can be used, such as Mθ 2 X(H 2 θ) n , MOX 3 (H 2 θ) n , AMOX 5 (H 2 0) n , AMO 2 X 3 (H 0) n , where "A" is at least one divalent cation or two monovalent cations, "M" is Nb or Ta, "X" is F, Cl, or Br, and "n" is a number from 0 to 25. In combination with the catalyst, it is preferred to use from greater than 1 to 150 molar equivalents of HF, based on the tantalum or niobium catalyst, preferably at least 10 to 140 molar equivalents, and, more preferably, at least 20 to 130 molar equivalents, to achieve optimum halogen exchange and consequent high yields of fluorinated alkanes. in combination with the catalyst and HF, it is preferred to use 1 to 30 molar equivalents of HOSO 2 CI, based on tantalum or niobium, preferably 3 to 20 molar equivalents, and more preferably 5 to 18 molar equivalents, to achieve optimum halogen exchange and consequent high yields of fluorinated alkanes. It is also possible to use other equivalents of H0S0 2 C1, such as HOS0 2 F, HOSO 2 CF 3 , HOSO 2 CH 3 , SO 3 , H 2 SO 4 /SO 3 , H 2 SO 4 , or any other SO 3 equivalent or carrier. In combination with the catalyst, HF, and HOSO 2 CI or equivalent thereof, it is preferred to utilize 0.5 to 20 molar equivalents of SOCI 2 , based on the starting alkene or alkane, preferably 0.75 to 10 molar equivalents, and more preferably 1 to 6 molar equivalents, to achieve optimum halogen exchange and consequent high yields of fluorinated alkanes. It is also possible to use other dehydrating agents of the general formula, CYY'Y'' (C=0)X, wherein Y, Y' and Y" are selected from H, F, Cl or Br and X is F, Cl or Br. Other possible dehydrating agents may be selected from Cl(C=0) (C=0)C1, POCI 3 , PCI5, PCI3, SO 2 CI 2 , BCI 3 , SiCl 4 , C1(C=0)C1, C1(C=0)F and F(C=0)F. A variety of alkenes and alkanes may be used as starting materials. Preferred halogenated alkenes are of the formula Rι 2 C=CR 3 R 4 , wherein Ri, R , R 3 , R 4 , are H, F, Cl, Br, or C x Z 2 χ+ι, wherein Z is selected from at least one of the group consisting of H, F, Cl, or Br and at least one of Ri, R 2 , R 3 and R 4 are either Br or Cl or a bromine or chlorine-substituted group. Preferred alkanes are of the formula R 5 R 6 R 7 R 8 C, wherein R 5 , R 6 , R 7 , are H, F, Cl, Br, or CχZ2χ+ι, wherein Z is selected from at least one of the group consisting of H, F, Cl, or Br and x equals 1 to 10 and wherein Re is Br or Cl. Specifically preferred halogenated alkenes and alkanes trans-CHCl=CHCl, CH 2 =CHC1, CCI 3 CHCI 2 , CC1 3 CH 2 C1, CH 2 C1CH 2 C1, CHCI2CHCI2, and CCI3CH3. An advantage of the instant invention is that small amounts of water in the reactants may be removed by the combination of the drying agents, e.g., SOCI2 and HOSO2CI. For example, water, which may be a product of the reaction of Ta2θs and HF: (Ta2θ5 and 10 HF —> 2 TaFs + 5 H2O) , would be removed by the drying agents during the process of the invention. Another advantage of the instant invention is that precautions need not be taken when charging tantalum or niobium catalyst since the drying agents employed will remove adventitious water, waters of hydration, or water formed in the reaction of metal oxides with HF. It was unexpected that Ta2θs operates as a catalyst"since, in the absence of drying agents, Ta2θ5 shows no catalytic activity with any of the starting alkenes or alkanes described herein. Prior art (US 4,124,692) teaches that it is possible to make TaF5 from fluorotantalic acids using dehydrating agents such as CHX3, CX4, COX2, CSX2, wherein X comprises Cl, Br " , or mixtures thereof, but the dehydration does not go to completion for fluorotantalic acids having a high atom ratio of oxygen to tantalum (O/Ta = 2.5), as is the case for Ta2θ5. Moreover, it teaches that it is preferred that excess HF (i.e. the amount of excess of that required to convert the tantalum compounds to fluorotantalic acids) be removed prior to contact with the dehydrating agent since said agent(s) will react with the HF to form fluoro derivatives. Hence, it was a complete surprise that Ta2θs operates as a catalyst, even when used with the proper ratio of dehydrating agent and chlorosulfonic acid. HF, which is commercially available, can be used in the reaction directly. The halogenated alkenes and alkanes, and the drying agents contain little or no water and can similarly be used directly. The reaction can be carried out in the liquid phase or vapor phase and at autogenous pressures or under constant pressure ranging from atmospheric to superatmospheric. Both the liquid phase and vapor phase processes include batch, semicontinuous, and continuous modes of operation. The reaction is normally carried out at a temperature from O'C to 185 * C, and preferably from 35'C to 160'C. Pressure is not critical. Atmospheric and autogenous pressures are the most convenient and are i therefore preferred. Means can be provided for the venting of any excess pressure due to formation of hydrogen chloride in the substitution reaction and can offer the advantage in minimizing the formation of side products. The reaction vessel is constructed from materials which are resistant to the action of HF and "superacid" systems. Examples include stainless steel, high nickel alloys such as monel, "Hastelloy" and "Inconel", plastics such as polytetrafluoroethylene, polychlorotrifluoroethylene, polyethylene, and polypropylene, and ceramic materials such as alpha-silicon carbide and aluminum nitride. The high nickel alloys are preferred because of the superacidities of pentavalent tantalum and pentavalent niobium systems in anhydrous HF. The liquid phase reactions are conducted by introducing the tantalum or niobium oxide and the halogenated alkene or halogenated alkane, thionyl chloride, and chlorosulfonic acid in any order into the reaction vessel. Generally, the Ta2θs, the starting alkene or alkane, the SOCI2, and the HOSO2CI are placed in the reaction vessel in an inert atmosphere chamber. The reaction vessel is cooled, and the required amount of HF is condensed in the vessel. The vessel may be evacuated prior to the introduction of hydrogen fluoride. The contents of the vessel are raised to the appropriate reaction temperature and agitated by shaking or stirring for a length of time sufficient to cause the desired reaction to occur. The products are isolated by any of a variety of well-known techniques such as distillation or drowning into ice, washing with aqueous caustic, then water. Under the reaction conditions set forth above, a portion of the Ta 2 θs or Nb 2 θs may be in the form of M(Cl)m(F)n(0)o(Sθ 3 Cl)p(S0 3 F)q(Sθ 3 H) r , where m+n+p+q+2o+r is equal to 5, and M is Nb or Ta. The fluorinated alkanes produced by the invention have utility as refrigerants, solvents blowing agents, cleaning agents, propellants, dielectric fluids, carriers for sterilant gases and fire extinguishants. In the following illustrative Examples all parts are molar proportions and all temperatures are Centigrade unless otherwise stated. All reactions used commercial anhydrous HF and were carried out with the exclusion of water. The product mixtures were analyzed by gas chromatography (GC) and mass spectroscopy (MS) or GCMS to identify the individual products. Results are in GC area percent. SXft PkE 1 To a 150 cc stainless steel single ended cylinder in a drybox was added Ta2θs (10.1 gm, .0229 mol) , HOS02C1 (47.2 gm, .405 mol) , SOC12 (16.4 g , .138 mol), and CC12=CC12 (11.2 grams, .0675 mol). HF (20.4 gm, 1.04 mol) was added by vacuum-line distillation. The cylinder was then fitted with a reflux condenser operating at 10"C, a pressure gauge and a back pressure regulator set at 500 psi. The cylinder containing the reactants was immersed in an oil bath set at 158*C and the reaction temperature, monitored by a thermocouple inside of the cylinder, was kept at 148-152*C for two hours while the autogenous pressure exceeded of 500 psi. Organic products were isolated by vacuum transfer of the contents of the reaction cylinder at the end of the run to a transfer cylinder containing a dip leg. The contents of the transfer cylinder were then transferred onto ice using nitrogen gas; 4.8 grams of organic were isolated and analyzed as follows: CHCI 2 CFCI 2 (0.9%), CHCI 2 CF 2 CI (94.9%), and CHCI 2 CF 3 (1.4%) with trace amounts of other organics. EXAMPLE 2 To a 150 cc stainless steel single ended cylinder in a drybox was added Ta205 (8.1 g , .0183 mol), HOSO 2 CI (37.7 gm, .324 mol), SOCI 2 (13.1 gm, .110 mol), and perclene (8.9 grams, .0537 mol) .HF (20.4 gm, 1.04 mol) was added by vacuum-line distillation. The cylinder was then fitted with a reflux condenser operating at 10"C, a pressure gauge and a back pressure regulator set at 500 psi. The cylinder containing the reactants was immersed in an oil bath set at 158*C and the reaction temperature, monitored by a thermocouple inside of the cylinder, was kept at 148-152*C for two hours while generating an autogenous pressure in excess of 500 psi. Organic products were isolated by vacuum transfer of the contents of the reaction cylinder at the end of the run to a transfer cylinder containing a dip leg. The contents of the transfer cylinder were then transferred onto ice using nitrogen gas; 3.78 grams of organic were isolated and analyzed as follows: CHC1 2 CFC1 2 (1.5%), CHC1 2 CC1F 2 (94%), and CHCI2CF3 (0.6%) with trace amounts of other organics. CONTROL EXAMPLE 2A The following is a comparison using TaFs. To a 150 cσ stainless steel single ended cylinder in a drybox was added TaFs (5.6 gm, .0203 mol), HOSO2CI (41.6 gm, .357 mol), S0C12 (14.4 gm, .121 mol), and perclene (8.9 grams, .0597). HF (22.5 gm, 1.125 mol) was added by vacuum distillation. The cylinder was then fitted with a reflux condenser operating at 10°C, a pressure gauge and a back pressure regulator set at 500 psi. The cylinder containing the reactants was immersed in an oil bath set at 158'C and the reaction temperature, monitored by a thermocouple inside of the cylinder, was kept at 141-146'C for 2.5 hours while generating an autogenous pressure in excess of 500 psi. Organic products were isolated by vacuum transfer of the contents of the reaction cylinder at the end of the run to a transfer cylinder containing a dip leg. The contents of the transfer cylinder were then transferred onto ice using nitrogen gas; 5.50 grams of organic were isolated and analyzed as follows: CHC1 2 CC1 2 F (0.4%), CHC1 2 CC1F 2 (96%), and CHCI2CF3 (2.3%), showing that Ta2θs (when used according to this invention) and TaFs display similar catalytic activity. EXAMPLE 3 To a 150 cc stainless steel single ended cylinder in a drybox was added Ta 2 θs (8.1 gm, .0183 mol), SOCI 2 (13.1 gm, .110 mol), and perclene (8.9 grams, .0538 mol). HF (22.5 gm, 1.125 mol) was added by vacuum distillation. The cylinder was then fitted with a reflux condenser operating at 0"C, a pressure gauge and a back pressure regulator set at 500 psi. The cylinder containing the reactants was immersed in an oil bath set at 158*C and the reaction temperature, monitored by a thermocouple inside of th cylinder, was kept at 132-137*C for 2.0 hours while generating an autogenous pressure not exceeding 470 psi. Organic products were isolated by vacuum transfer of the contents of the reaction cylinder at the end of the run to a transfer cylinder containing dip leg. The contents of the transfer cylinder were then transferred onto ice using nitrogen gas; 5.37 grams of organic were isolated and analyzed as follows: CCl 2 =CCl 2 (87.1%) and CHCI 2 CCI 2 F (8.5%) wit trace amounts of other organics. The preceding exa' ple demonstrates that SOCI 2 will operate as the sole dehydrating agent but that it is preferred to include HOSO 2 CI in the dehydrating agent. EXAMPLE 4 To a 150 cc stainless steel single ended cylinder in a drybox was added Ta 2 θs (5.7 gm, .0129 mol), HOSO 2 CI (26.7 gm, .229 mol), and perclene (6.3 grams, .040 mol). HF (21.4 gm, 1.07 mol) was added by vacuum distillation. The cylinder was then fitted with a reflux condenser operating at O'C, a pressure gauge and a back pressure regulator set at 500 psi. The cylinder containing the reactants was immersed in an oil bath set at 160*C and the reaction temperature, monitored by a thermocouple inside of the cylinder, was kept at 147-154 β C for 2.25 hours while generating an autogenous pressure not exceeding 470 psi. Organic products were isolated by vacuum transfer of the contents of the reaction cylinder at the end of the run to a transfer cylinder containing a dip leg. The contents of the transfer cylinder were then transferred onto ice using nitrogen gas; organic was isolated and analyzed as follows: CCl 2 =CCl 2 (49.3%), CHC1 2 CC1 2 F (36.5%), CHC1- 2 CC1F 2 (7.9%) CHCI2CCI 3 (1.6%) with trace amounts of other organics. The preceding example demonstrates that i HOSO 2 CI alone will operate but that it is preferred to include SOCI 2 along with HOSO2CI as the dehydrating agent. EXAMPLE 5 To a 400 cc "Hastelloy" C single ended agitated bomb was added b 2 θs (12.0 gm, .045 mol), H0S0 2 C1 (69.9 gm, .600 mol), S0C1 2 (19.6 gm, .165 mol), and CHC1=CC12 (197 grams, 1.50 mol). HF (230 gm, 11.5 mol) was added by vacuum distillation. The vessel was heated to 85 "C for two hours; autogenous pressure developed in excess of 2000 psi. At the and of this period, the bomb was cooled to 0'C and vented through a caustic scrubber. The contents were then poured onto ice and the organic products isolated and analyzed as follows: CH 2 CICFCI 2 (90%), CHC1=CC1 2 (6.7%), and CH2CICCI 3 (2.4%) with trace amounts of other organics.

Claims: CLAIMS What is claimed: 1. A process for the preparation of fluorinated alkanes which comprises contacting, at a temperature of O'C to 185"C under substantially anhydrous conditions, a starting material selected from halogenated alkanes and halogenated alkenes of the following formulas R 1 R 2 C=CR 3 R 4 and R5 R 6 7 8 C wherein Ri, R 2 R 3 R 4 , R 5 R 6, R 7 and Rs are H, F, Cl, Br, or C x Z 2 +i/ wherein Z is H, F, Cl or Br, x is an integer from 1-10, and wherein at least one of R - R 4 and R 5 - RQ is Br or Cl or a bromine or chlorine-substituted group, with HF and at least one dehydrating agent, in the presence of at least one catalyst selected from the oxides of niobium and tantalum, to produce reaction products, the mole ratio of HF to Ta or Nb being from 1 to 150, the mole ratio of the dehydrating agent to Ta or Nb being from 1 to 30, and the mole ratio of the starting material to Ta or Nb being less than 100; and removing the reaction products from contact with the catalyst and isolating a fluorinated alkane having at least one more fluorine atom than the starting material. 2. A process for the preparation of fluorinated alkanes which comprises contacting, at a temperature of 0*C to 185'C under substantially anhydrous conditions, a starting material selected from halogenated alkanes and halogenated alkenes of the following formulas R 1 R 2 =CR 3 R 4 and R5R6R7R8C wherein Ri, R , R 3 , R4, R5, Re , R 7 and RQ are H, F, Cl, Br, or C x Z2χ+ι, wherein Z is H, F, Cl or Br x is an integer from 1-10, and wherein at least one of i - R4 and R5 - Rs is Br or Cl or a bromine or chlorine-substituted group, with HF, HOSO2CI and SOCI2, in the presence of at least one catalyst selected from Nb2θs and Ta2θs, to produce reaction products, the mole ratio of HF to Ta or Nb being from 1 to 150, the mole ratio of HOSO2CI to Ta or Nb being from 1 to 30, and the mole ratio of SOCI2 to Ta or Nb being from 0.5 to 20; and the mole ratio of the starting material to Ta or Nb being less than 100; and removing the reaction products from contact with the catalyst and isolating a fluorinated alkane having at least one more fluorine atom than the starting material. 3. The process in Claim 2 wherein the amount of HF, based on the catalyst, is 20 to 130 molar equivalents. 4. The process in Claim 2 wherein the catalyst is tantalum oxide. 5. The process in Claim 2 wherein the temperature is 35*C to 160*C. 6. The process in Claim 2 wherein the chlorosulfonic acid is in an amount of 5 to 18 molar equivalents based on the catalyst. 7. The process in Claim 2 wherein the thionyl chloride is in an amount of 1 to 6 molar equivalents based on the catalyst. 8. The process in Claim 2 wherein the starting material is at least one halogenated alkene selected from the following compounds: CCl2=CCl2, CHC1=CC1 2 , CH2=CCl , cis- and trans- CHC1=CHC1 and CH 2 =CHC1. 9. The process in Claim 2 wherein the starting material is at least one halogenated alkane * selected from the following compounds: CCI3CHCI2, CCI3CH2CI, CH2CICH2CI, CHCI2CHCI2 and CCI3CH3.

Inventors: NAPPA MARIO JOSEPH, NAPPA, MARIO, JOSEPH
Applicants: DU PONT, E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1991
Main classification: C07C17
IPC codes: B01J23, C07B61, C07C17, C07C19