DEVICE FOR PULLING UP SINGLE CRYSTAL

Abstract: A device for pulling up a single crystal produced through the Czochralski process, characterized in that: one side thereof facing the quartz crucible is composed of a heat absorbing body whereas the other a heat insulating body; a first cylindrical screen having at upper and lower ends an outwardly directed annular rim and inwardly directed one, respectively, and also having a corner part which faces said crucible and is formed into a curved or polygonal surface is disposed around a single crystal pulling up area with said annular rim at the lower end positioned near an area in which molten material is filled; and a second screen in the shape of parabola at cross-section to open at the central part while surrounding the single crystal pulling up area, and having an outwardly directed annular rim at the upper end is provided inside said first screen, and, thus, the device intends to quickly pull up a single crystal bar while preventing contamination of crystal otherwise caused by impurities and interruption of single-crystallization. A second screen in such a cross-sectional shape as extending along the first screen may be disposed inside the first screen and the second screen may be provided with a forced cooling mechanism.

Description: This invention relates to an apparatus for pulling up a single crystal according to the Czochralski method, and more particularly to an apparatus for pulling up a single crystal which is provided with screens which can float up a single crystal at a high speed while controlling contamination of the crystal which is caused by impurities, and without impeding the single crystallization. Apparatus for pulling up a single crystal, in which the pulling-up speed of the crystal is improved is known from some patent applications. Japanese Patent Kokai No. 62-138386 describes a technique of speeding up the floating rate while controlling contamination of the crystal, by shielding the radiant heat generated from the melt by the provision of a radiant screen of an approximately inverted cone-shaped, heat-insulating multilayer structure thereby to prevent the single crystal being pulled up from heating, said multilayer structure being provided close to the surface of the melt and its surface being sintered with a ceramic body or ceramic-coated. Alternatively, Japanese Patent Kokai No. 63-256593 describes a technique aimed at a further effect for speeding up the pulling by providing a shielding member of upturned trapezoid shape in section, which member surrounds the pulling-up zone of the single crystal, and a cooling mechanism. Alternatively, as a technique of improving the pulling-up rate of the single crystal and the non-transition of the crystal, which is caused by contamination by impurities, Japanese Patent Kokai No. 63-50391 describes a technique wherein a cylinder is provided in the periphery of a growing single crystal, said cylinder having a cooling mechanism in its periphery, the inner peripheral surface of the cylinder forming a reflecting surface for radiant heat, and the surface of said cylinder opposing the melt material forming a reflecting surface for the radiant heat. Further, as a technique of removing contamination caused by impurities Japanese Patent Kokai No. 64-18988 describes a technique of disposing a plurality of heat shielding plates made concentrically of metal or graphite, in the periphery of the pulled-up single crystal, in such a way that they may communicate with the outside without enclosing the crucible while keeping spaces mutually. Furthermore, as a technique of improving the pulling-up rate of the single crystal and the non-transition caused by contamination by impurities, Japanese Patent Kokai No. 1-145391 describes a technique of providing, in a cooling means arranged at the circumference of the pulled-up single crystal, a shielding element made of molybdenum to shield the space between said cooling means and the crucible or the melt in the crucible. However, such known techniques have the following disadvantages. (1) To speed up the pulling rate of a growing crystal it is important to have the transmitted heat from the melt, the latent heat for solidification in the crystallization process, the radiant heat emitted from heat source such as the melt or heater, and the like, escaped quickly from the growing crystal. Particularly, it is possible to speed up the pulling-up rate if the temperature gradient near the interface of the solid solution is great, even if the consequential temperature gradient in the growing crystal were small i.e. the cooling rate were a little bit slow. However, in the techniques such as that of the inverted cone-shaped screen, which are used in the conventional apparatus, the viewing angle to the growing crystal is sufficiently small particularly in the neighborhood of the solid solution interface, that the radiant heat or the like generated from the neighborhood of said interface cannot completely escape and so it is difficult to further improve the pulling-up rate. (2) If a material such as carbon or SiC having a large thermal emissivity and good thermal conductivity is used in the inner surface of the radiation screen, the material absorbs the radiant heat emitted from the growing crystal so that the temperature of the radiant screen itself is raised. Because of this phenomenon, the growing crystal itself is subject to heat radiation from the screen or radiation from the growing crystal, which is reflected by the screen, thereby retaining the heat so that the pulling rate becomes slow. (3) If a material having a large thermal emissivity is used in the inner surface of a radiation screen having a cooling mechanism, the material itself reflects the radiant heat generated from the growing crystal so that the growing crystal retains heat from the reflected radiant heat so that the pulling rate is restricted. (4) Since the shape of the radiation screen is an inverted trapezoid or cone in section and since radiant heat is prevented close to the growing crystal, away from the melt surface or the crucible wall which is a great heat source, sufficient cooling cannot be ensured, and therefore the pulling rate is restrained. (5) If the shape of the radiation screen is not an inverted trapezoid or cone and the corner of the screen is not smooth, the Ar gas accompanied by impurities is apt to stay in the vicinity of the interface between the crucible and the melt whereby the melt is contaminated so as to hinder the single crystallization of the growing crystal. The present invention has been made to eliminate the above disadvantages of said known apparatus. In an apparatus for pulling up a single crystal according to the Czochralski method the invention is characterized in that a cylindrical first screen is arranged in the periphery of the zone of pulling up a single crystal, said screen comprising a heat absorbing body of carbon, or silicon carbide or carbon coated with silicon carbide at the side facing a quartz crucible and by a heat insulator of carbon felt at the other side and being provided with respective outward and inward annular rims at the upper and lower ends thereof, the corner of said screen facing the crucible being formed in a curved or polygonal structure, and said annular rim at the lower end being positioned in the vicinity of filling the melt in the crucible, and a second screen is arranged within said first screen, said second screen forming a parabolic shape in section opening at its center while enclosing the crystal pulling zone and being provided at its upper end with an outward annular rim. An alternative structure may be such that in an apparatus for pulling a single crystal according to the Czochralski method, a cylindrical first screen is arranged in the periphery of the zone of pulling the single crystal, said screen comprising a heat absorbing body of carbon or silicon carbide or carbon coated with silicon carbide at the side facing a quartz crucible and by a heat insulator of carbon felt at the other side and being provided with respective outward and inward annular rims at the upper and lower ends thereof, the corner of said screen facing the crucible being formed in a curved or polygonal structure, and said annular rim at the lower end being positioned in the vicinity of filling the melt in the crucible, and then a second screen is arranged within said first screen, said second screen being formed along the first screen in its sectional shape. It is further possible to provide a forced cooling mechanism in said second screen. In the drawings: FIG. 1 shows an apparatus for pulling up a single crystal, illustrating an Example of the invention; FIG. 2 shows an apparatus for pulling up a single crystal, illustrating another Example of the invention; FIG. 3 shows an apparatus for floating up a single crystal, illustrating still another Example of the invention; FIG. 4 shows an apparatus for pulling up a single crystal, illustrating another Example of the invention; and FIG. 5 is a graph showing oxygen concentration relative to the solidification rates of single crystals of silicon which are pulled up by the present apparatus and by known apparatus. Following are preferred features of the invention. A cylindrical first screen provided with annular rims is disposed closer to heating elements such as the heater, melt and crucible wall, compared with the screen of conventional apparatus thereby to shield the radiant heat in places near the heat sources. By coating the side facing the quartz crucible with SiC or carbon which are excellent in heat absorbing property said face of the first screen is retained at a high temperature so as to prevent the screen from adhering to substances evaporated from the silicon melt. The first screen is provided in such a manner that the annular rims may be parallel to the surface of the melt while the cylindrical portion may be parallel to the wall of the crucible, and the corner at the side facing the crucible is formed in a curved or polygonal face, and therefore, the substances evaporated from the silicon melt are smoothly discharged to the outside of the crucible withouting staying there. In a second screen having a parabolic shape in section, the radiant heat having absorbing property or that emitted from the vicinity of the interface of the view solution reflects upwardly due to the effect of solid angle, and the radiant heat emitted from the growing crystal portion further above the solid solution interface reflects likewise upwardly. In the structure where the second screen is formed along the first screen, heat insulation is intended near the heat source such as the crucible, heater or melt. Provision of a forced cooling mechanism such as by water cooling in the second screen will allow the radiant heat generated from the growing crystal to be easily absorbed whereby the heat escapes outside the system to cool the growing crystal. The invention will now be described in more detail by way of Examples. EXAMPLE 1 FIG. 1 shows one Example of the apparatus for pulling up a single crystal according to the invention. A pull chamber 2 is provided in the upper portion of a chamber 1. A vertically movable, rotary shaft 3 is inserted from the lower, central opening of the chamber 1, and a supporter 4 made of carbon is fixed to the upper end of the rotary shaft 3 to support a quartz crucible 5. The outer periphery of said supporter 4 is provided with a carbon heat-insulating member 7 for shielding the radiation which is transmitted from a cylindrical carbon heater 6 to the chamber 1, and with a heat insulating cylinder 8 for shielding said member 7, said cylinder 8 being made of carbon felt. A cylindrical first screen 12 is fixed to the upper end of said heat insulating cylinder 8, in the flange portion of an annular rim 13A provided outwardly in the upper end of the screen, it descends along the wall of the quartz crucible 5, and its lower end reaches the vicinity of the surface 100 of the melt. The lower end of said first screen is provided with an annular rim 15, covering the melt surface 100 toward the inside of the chamber 1 and extending to the neighborhood of a growing crystal 14, and a corner 10 is formed with a curved face. On the other hand, the flanges of the crucible 5 and the supporter 4 are respectively roundshaped. The side facing the crucible 5 of the first screen 12 uses carbon coated with SiC as a heat absorber having a high radiation rate (0.8-0.5). Since the first screen 12 is subjected to the radiation generated from the melt surface 100, the wall of the quartz crucible 5, and the heater 6, and the first screen itself reaches a high temperature, adhesion of SiO, SiO 2 and Si generated from the melt surface 100 does not occur in the screen. Furthermore, since the first screen is cylindrical and provided near the heat sources it efficiently shields the radiant heat emitted from said heat sources. Then, since the corner 10 at the side oppositely facing the wall of the crucible or the melt surface is formed in a curved face, the substances evaporated in the crucible are smoothly discharged without staying near the interface between the crucible and the melt surface or at the corner of the first screen whereby the single crystallization is not hindered. Furthermore, the growing crystal side of the first screen 12 is provided with a heat insulator made of carbon felt, so that the growing crystal is effectively heat insulated from the great heat sources such as the melt surface 100, the wall of the crucible 5 and the heater 6. A second screen 11A is of parabolic shape in section and made of carbon, and it is fixed to the upper end of the heat insulating cylinder 8 like lhe first screen, by means of an annular rim 13B provtded outwardly in its upper end. Referring to the temperature distribution in the growing crystal 14, the temperature is lowered almost in exponential function from the interface 16 of the solid solution toward the top side. On the other hand, the crystal growing rate greatly depends on the temperature gradient in the crystal near the growing interface. Therefore, in order that the radiation from the surface of the growing crystal in the vicinity of the solid solution interface be efficiently reflected or absorbed upwardly for escape there is adopted a screen of parabolic profile in section where the solid angle to the crystal surface near the growing interface is smaller than that in the screen of upturned-cone shape. This will increase the temperature gradient in the vicinity of the growing interface. Alternatively, since the surface of the screen is substituted always by a fresh inert gas the screen is not exposed to SiO, SiO 2 and Si which are the substances evaporated from the melt even if the temperature is low, so that the impurities do not fall upon the growing crystal. By using the present apparatus, 30 kg of polycrystal silicon was put into a quartz crucible of about ⊘340 mm wide and 250 mm deep to pull up a single crystal having about ⊘100 mm diameter according to an ordinary method, when it was possible to obtain a single crystal about 1,250 mm long at a high rate in the range 1.9 to 2.0 mm/min. and with good reproducibility, and the single crystallization was not hindered. Even the drawbacks for crystallization could be eliminated and the oxygen concentration could be lowered. This results in speeding up the pulling rate and saving energy. The property of the single silicon crystal pulled (or grown) up by this Example is shown with curve a in FIG. 5. Alternatively, even use of metal such as molybdenum in the second screen will not bring about any problem. EXAMPLE 2 The invention will now be described with reference to another Example illustrated in FIG. 2. In explaining Example 2 reference numerals the same as in Example 1 are used to indicate the same constitutional elements as those of Example 1, and any overlapping description is omitted. In the Example of FIG. 2, the major difference from Example 1 is that the second screen 11B adopted is not of parabolic shape in section but of a shape formed along the first screen 12. Such a shape avoids the radiant heat to the growing crystal in the neighborhood of the heat sources of the heater 6, the crucible 5 and the melt thus permitting the heat insulating effect to be improved. Additionally, in this second Example, a ventilation hole 200 for conducting an inert gas to the space between the first screen and the second screen is provided in the upper annular rim 13B of the second screen. This has the purpose of passing the fresh inert gas through the space between the screens thereby preventing adhesion of the substances evaporated from the melt surface. By using the present apparatus, 30 Kg of polycrystal silicon was put into a quartz crucible about ⊘340 mm wide and 250 mm deep to pull up a single crystal having diameter of about ⊘110 mm using an ordinary method, when it was possible to obtain a single crystal 1,250 mm long at the high pulling rate of 1.9 to 2.0 mm/min. and with good reproducibility, and the single crystallization was not checked. Additionally, even the drawbacks for crystallization could be eliminated and the oxygen concentration could be lowered thereby resulting in improvement of the speeding up of the pulling rate and saving energy. The property of the single silicon crystal pulled (or grown) up in Example 2 is shown by curve b in FIG. 5. EXAMPLE 3 The invention will be described with reference to still another Example as illustrated in FIG. 3. Similarly to Example 2, in explaining Example 3 the reference numerals the same as in Example 1 are used to indicate the same constitutional elements as those of Example 1, and any overlapping description is omitted. A second screen 11C having excellent heat absorbing property (large emissivity) and made of carbon is provided in a sectional inverted L-shape, and the inside thereof is constructed in a jacket so that it is passed with a cooling gas to cool the screen. Thus, the provision of the second screen is to cool the screen itself, then thereby to subject the growing crystal to a forced cooling and to improve the growing rate of the single crystal. When using the present apparatus, 30 Kg of polycrystal silicon was put into a quartz crucible about ⊘340 mm wide and 250 mm deep to pull up a single crystal having a diameter of about ⊘110 mm according to an ordinary method, when it was capable of obtaining a single crystal about 1,250 mm long at the high pulling rate of 2.5 to 2.6 mm/min. and with good reproducibility. The single crystallization was not checked. Additionally, it was possible to eliminate even the drawbacks of crystallization, to lower the oxygen concentration and to save energy because of the speeding up of the pulling rate. The property of the single silicon crystal pulled (or grown) up according to Example 3 is illustrated with curve c in FIG. 5. The forced cooling mechanism of the second screen is constructed in such a manner that as shown in FIG. 4, pipes 30 are provided in the outer periphery of the second screen having a large emissivity and an upturned L-shape in section, to allow the pipes to be supplied with water or cooling gas. By comparison, the property of the single silicon crystal pulled (or grown) up by using a conventional apparatus under the same conditions as in the foregoing Examples, is shown with curve d in FIG. 5. In each of said Examples, the first screen and the second screen are disposed maintaining a small space. Due to such a space it is possible to avoid heat transmission from the first screen to the second screen so as to effectively shield the radiant heat emitted from the heat sources to the growing crystal. Provision of a hole in the upper portion of the second screen will feed a fresh argon gas into the space between the first and second screens. Thus, since the space between the two screens is always maintained to clean the surfaces of the screens are not exposed to SiO, SiO 2 and Si which are the substances evaporated from the melt even if the surfaces are low in temperature, and therefore since the crystal is not adhered with such precipitated substances the single crystallization is not hindered. As described above in detail, according to the present invention, one side of the first screen, which faces the crucible, comprises a heat absorbing body whereas the other side thereof comprises a heat insulating body, so that the side facing the crucible reaches a high temperature by the heat generated from the heat source such as the crucible or heater thereby preventing precipitation and adhesion of evaporation substances. The heat insulating body at the other side makes the heat from the heat source hardly transmittable to the second screen-or the growing crystal side. Moreover since the first screen is formed to be along the crucible and the melt surface while its corner is curved, gas, including evaporation substances, does not stay but is smoothly exhausted. On the other hand, the second screen whose section forms a parabola opening in its center while enclosing the pulling-up zone of the single crystal, permits the radiant heat from the growing crystal to escape upwardly owing to the effect of the view angle with the intention of cooling the growing crystal. These functions and effects increase the temperature gradient of the solid solution interface of the growing crystal whereby the pulling-up speed is improved. Alternatively, in an apparatus where the second screen is formed along the first screen in profile, the apparatus has no effect of radiation of the radiant heat, which effect is brought about by view angle, but the cooling effect of the single crystal is likewise brought about because the heat shielding is effected close to the heat source such as the heater. Furthermore, provision of a cooling mechanism in the second screen will improve the cooling effect. In the apparatus illustrated in any of the foregoing Examples of the invention, the annular rims shield some heat that transmits upwards from the heater, the crucible or the melt so as not to extend to the pulling-up region of the growing crystal. Thus, in the apparatus for pulling up a single crystal according to the present invention, it is possible to speed up the pulling rate of the growing crystal and to reduce the factors hindering the single crystallization thereby improving productivity.

Claims: An apparatus for pulling up a single crystal (14), which consists of a crucible (5) for filling a material (16), a heater (6) which is provided in the periphery of said crucible (5) and melts the material (16), and a mechanism for immersing a seed crystal into the molten material (16) to pull up a single crystal (14), characterised in that a cylindrical first screen (12) is arranged in the periphery of the zone of pulling up a single crystal (14), said screen comprising a heat absorbing body of carbon or silicon carbide or carbon coated with silicon carbide (7) at the side facing a quartz crucible (5) and by a heat insulator of carbon felt (8) at the other side and being provided with respective outward and inward annular rims (13A,12) at the upper and lower ends thereof, the corners (10) of said screen facing the crucible being formed in a curved or polygonal structure, and said annular rim at the lower end being positioned in the vicinity of filling the melt (16) in the crucible (5), and a second screen is arranged within said first screen (12), said second screen forming a parabolic shape in section opening at its centre while enclosing the crystal pulling-up zone and being provided at its upper end with an outward annular rim (11A). An apparatus for pulling up a single crystal (14), which comprises a crucible (5) for filling a material (16), a heater (6) which is provided in the periphery of said crucible (5) and melts the material (16), and a mechanism for immersing a seed crystal into the molten material (16) to pull up a single crystal (14), characterised in that a cylindrical first screen (12) is arranged in the periphery of the zone of pulling up a single crystal (14), said screen comprising a heat absorbing body of carbon or silicon carbide of carbon coated with silicon carbide (7) at the side facing a quartz crucible (5) and by a heat insulator or carbon felt (8) at the other side and being provided with respective outward and inward annular rims (13,15) at the upper and lower ends thereof, the corners (10) of said screen facing the crucible being formed in a curved or polygonal structure, and said annular rim at the lower end being positioned in the vicinity of filling the melt (16) in the crucible (5), and a second screen is arranged within said first screen (12), said second screen being formed along the first screen (12) in its sectional shape. An apparatus as claimed in claim 1 or claim 2 wherein the second screen is equipped with a forced cooling mechanism (30).

Inventors: MATSUZAKI AKIHIRO YOKOUCHI, NAGAI KAZUNORI, TOMIOKA JUNSUKE, MATSUZAKI, AKIHIRO, NAGAI, KAZUNORI, TOMIOKA, JUNSUKE, MATSUZAKI, AKIHIRO, 4310 YOKOUCHI, NAGAI, KAZUNORI, 3-17-5-105, KIBOGA-OKA, TOMIOKA, JUNSUKE, 386-75, SANADA
Applicants: KOMATSU DENSHI KINZOKU KK, KOMATSU ELECTRONIC METALS CO., LTD
Application year: 1991
Main classification: C30B15
IPC codes: C30B15