Polychloroprene-based adhesive system

Abstract: A rubber-metal adhesive system which contains a primer component and an overcoat component. The primer component includes a polychloroprene compound, a phenolic resin, and a metal oxide while the overcoat component preferably contains a nitroso compound, a halogenated polyolefin, and a metal oxide or salt. When applied between a metal surface and a rubber substrate under heat and pressure, the adhesive system provides a flexible rubber-metal bond which will withstand high temperature fluid environments.

Description: This invention relates to the bonding of metal surfaces to rubber substrates with the use of appropriate adhesive compositions. More specifically, the present invention relates to an improved polychloroprene-based adhesive primer and corresponding adhesive system which provide for increased bond flexibility and increased bond resistance to high temperature fluid environments. Effective and reliable adhesive bonds between metal surfaces and rubber substrates are extremely important in automotive and industrial applications which utilize metal components bonded to rubber or elastomer substrates. Various technologies have been previously developed in an attempt to provide an effective rubber-metal bond which will withstand the various conditions encountered in these commercial applications. For example, U.S. Patent No. 2,581,920 discloses the use of polymers of dichlorobutadiene and chlorinated rubber in rubber-metal adhesives. In addition, U.S. Patent No. 2,900,292 discusses the bonding of rubber to metal with brominated 2,3-dichlorobutadiene-1,3 polymer. The adhesive composition may optionally contain a material that adheres to metal surfaces such as a thermosetting phenol-aldehyde resin or a halogenated rubber. U.S. Patent Nos. 3,258,388 and 3,258,389 disclose an adhesive composition containing a rubber adherent and a metal adherent such that the adhesive will bond metal to rubber upon heating under pressure. Various metal adherents include thermosetting phenol-aldehyde resins, polymers of ethylenically unsaturated materials, halogenated rubber such as chlorinated natural rubber or chlorinated polychloroprene. The rubber adherent basically consists of a poly-C-nitroso compound although various other rubber adhering components may be utilized such as vulcanizable olefins. U.S. Patent No. 4,769,413 discloses a metal coating composition which may be utilized as a primer in rubber-metal bonding. The composition consists of a blocked isocyanate-functional urethane prepolymer, a phenolic resin, and a halogenated resin such as halogenated rubber dispersed in an inert solvent. Recent technological advances in automotive and industrial applications have resulted in relatively severe working environments for adhesively bonded rubber and metal components. For example, many fluid-filled engine mounts are being exposed to increasingly high temperatures such that the rubber-metal bond on the mount is exposed to very high temperature fluid environments. Furthermore, many adhesively bonded components are crimped or squeezed into desired shapes or configurations prior to use in a final application. It has been found that many of the above adhesive systems containing halogenated rubbers such as chlorinated natural rubber cannot withstand the harsh conditions imposed by these environments. For example, in high temperature environments, many of the traditional rubber-metal bonding compositions will blister or rapidly corrode. In addition, the relatively brittle rubber-metal bonds formed from traditional compositions cannot withstand the crimping or squeezing required in many applications. A need therefore exists for a rubber-metal adhesive system which will withstand these increasingly demanding conditions. The present invention is an improved polychloroprene-based adhesive system which produces a flexible rubber-metal bond which will withstand high temperature fluid environments. The invention is a two-part adhesive system containing a primer component and an overcoat component. The primer component contains a polychloroprene compound, a phenolic resin, and a metal oxide while the overcoat component preferably contains a nitroso compound, a halogenated polyolefin, and a metal oxide or salt. The primer component and the overcoat component are effectively applied between the metal surface and the rubber substrate to be bonded and the resulting rubber-metal assembly is heated under pressure in order to effect bonding. It has been surprisingly discovered that an adhesive system utilizing the polychloroprene compounds disclosed herein in combination with the other components of the present invention results in a flexible rubber-metal bond which exhibits unusually high resistance to high temperature fluid environments. From one aspect the invention provides a rubber-metal adhesive system which can be effectively utilized in the increasingly demanding environments of many automotive and industrial applications. The present invention also provides a rubber-metal adhesive system which is sufficiently flexible to withstand crimping and squeezing of the corresponding rubber-metal assembly. The present invention still further provides a rubber-metal adhesive system which will withstand high temperature fluid environments. The adhesive system of the present invention contains a primer component and an overcoat component which can be applied under heat and pressure between a metal surface and a rubber substrate in order to produce a flexible rubber-metal bond which will withstand harsh conditions such as high temperature fluid environments. The primer component of the present adhesive system comprises a non-post chlorinated polychloroprene compound, a heat-reactive phenolic resin, and a metal oxide. The polychloroprene compound can be any polymer based on at least 50 to 100 percent of 2-chlorobutadiene-1,3 monomer. The remainder of the polymer may contain monomers such as sulfur, methacrylic acid, acrylonitrile, 2,3-dichloro-1,3-butadiene and combinations thereof. The preferred polychloroprene compounds of the invention are non-post-chlorinated homopolymers of 2-chlorobutadiene-1,3 having a molecular weight in the range of 200,000 to 1,300,000, preferably 700,000 to 1,100,000. The preferred homopolymers typically contain from 37 to 39 percent chlorine by weight and have a molecular structure containing from 85 to 95 percent trans-1,4 segments. Non-post-chlorinated polymer herein refers to a polychloroprene compound that has not been chlorinated subsequent to the initial polymerization of the polymer. The polychloroprene compound is utilized in an amount from 5 to 40, preferably from 20 to 25 percent by weight of the primer component. The synthesis and availability of the present polychloroprene compounds are well known in the art. The phenolic resin of the present invention can essentially be any heat-reactive phenolic resin. Typical phenolic resins include the organic solvent-soluble heat-reactive condensation product of an aldehyde having from 1 to 8 carbon atoms, such as formaldehyde, acetaldehyde, isobutyraldehyde, ethylhexaldehyde, and the like, with phenolic compounds such as phenol, o-cresol, m-cresol, p-cresol, mixed cresols, e.g., cresylic acid and m-cresol and/or p-cresol, xylenol, diphenylolproprane, p-butylphenol, p-tert-amylphenol, p-octylphenol, p,p'-dihydroxydiphenylether, and the like. Mixtures of dissimilar phenolic resins can also be used. The phenolic resin will preferably be formed in a conventional manner from the condensation of from 0.8 to 5 mols of aldehyde per mol of phenolic compound in the presence of basic, neutral, or acidic catalysts to afford an organic solvent-soluble resin having a molecular weight in the range of from 300 to 2,000, preferably from 300 to 1,200. A particularly preferred phenolic resin is a mixture of a phenol aldehyde resin and a phenol formaldehyde resin modified with cresol. The phenolic resin is typically utilized in an amount from 10 to 70, preferably from 30 to 50 percent by weight of the primer component. The metal oxide can be any known metal oxide such as zinc oxide, magnesium oxide, litharge, red lead, and combinations thereof, with zinc oxide being the preferred metal oxide. The metal oxide is typically utilized in an amount from 1 to 35, preferably from 5 to 20 percent by weight of the primer component. The primer component of the invention can optionally contain other well-known additives including plasticizers, fillers, pigments, reinforcing agents and the like, in amounts employed by those skilled in the adhesive arts to obtain desired color and consistency. Typical additional additives include titanium dioxide, carbon black and silica. The overcoat component can be any rubber-bonding composition, such as those disclosed in U.S. Patent Nos. 2,900,292, 3,258,389, and 4,119,587, but preferably comprises an aromatic nitroso compound, a halogenated polyolefin, and a metal oxide or salt. The nitroso compound can be any aromatic hydrocarbon, such as benzenes, naphthalenes, anthracenes, biphenyls, and the like, containing at least two nitroso groups attached directly to non-adjacent ring carbon atoms. More particularly, such nitroso compounds are described as aromatic compounds having from 1 to 3 aromatic nuclei, including fused aromatic nuclei, having from 2 to 6 nitroso groups attached directly to non-adjacent nuclear carbon atoms. The present preferred nitroso compounds are the di-nitroso aromatic compounds, especially the dinitrosobenzenes and dinitrosonaphthalenes, such as the meta- or para-dinitrosobenzenes and the meta- or para-dinitrosonaphthalenes. The nuclear hydrogen atoms of the aromatic nucleus can be replaced by alkyl, alkoxy, cycloalkyl, aryl, aralkyl, alkaryl, arylamine, arylnitroso, amino, halogen, and like groups. The presence of such substituents on the aromatic nuclei has little effect on the activity of the nitroso compounds in the present invention. As far as is presently known, there is no limitation as to the character of the substituent, and such substituents can be organic or inorganic in nature. Thus, where reference is made herin to nitroso compound, it will be understood to include both substituted and unsubstituted nitroso compounds, unless otherwise specified. Particularly preferred nitroso compounds are characterized by the formula: (R) m - Ar - (NO)₂ wherein Ar is selected from the group consisting of phenylene and naphthalene: R is a monovalent organic radical selected from the group consisting of alkyl, cycloalkyl, aryl, aralkyl, alkaryl, arylamine, and alkoxy radicals having from 1 to 20 carbon atoms, amino, or halogen, and is preferably an alkyl group having from 1 to 8 carbon atoms; and m is zero, 1, 2, 3, or 4, and preferably is zero. A partial non-limiting listing of nitroso compounds which are suitable for use in the practice of the invention include m-dinitrosobenzene, p-dinitrosobenzene, m-dinitrosonaphthalene, p-dinitrosonaphthalene, 2,5-dinitroso-p-cymeme, 2-methyl-1,4-dinitrosobenzene, 2-methyl-5-chloro-1,4-dinitrosobenzene, 2-fluoro-1,4-dinitrosobenzene, 2-methoxy-1-3-dinitrosobenzene, 5-chloro-1,3-dinitrosobenzene, 2-benzyl-1,4-dinitrosobenzene, 2-cyclohexyl-1,4-dinitrosobenzene and combinations thereof. Particularly preferred nitroso compounds include p-dinitrosobenzene and m-dinitrosobenzene. The nitroso compound component is typically utilized in an amount from 1 to 50, preferably from 5 to 35 percent by weight of the overcoat component. The halogenated polyolefin of the overcoat component can essentially be any natural or synthetic halogenated polyolefin elastomer. The halogens employed in the halogenated polyolefinic elastomers are typically chlorine or bromine, although fluorine can also be used. Mixtures of halogens can also be employed in which case the halogen-containing polyolefinic elastomer will have more than one type of halogen substituted thereon. The amount of halogen does not appear critical and can range from as low as 3 weight percent to more than 70 weight percent, depending on the nature of the base elastomer or polymer. Halogenated polyolefins and their preparation are well-known to those skilled in the art. Representative halogenated polyolefins include chlorinated natural rubber, chlorine- and bromine-containing synthetic rubbers including polychloroprene, chlorinated polychloroprene, chlorinated polybutadiene, chlorinated butadiene styrene copolymers, chlorinated ethylene propylene copolymers and ethylene/propylene/non-conjugated diene terpolymers, chlorinated polyethylene, chlorosulfonated polyethylene, brominated poly(1,3-dichloro-1,3-butadiene), copolymers of α-chloroacrylonitrile and 2,3-dichloro-1,3-butadiene, chlorinated poly(vinyl chloride), and the like, including mixtures of such halogen-containing elastomers. Thus, substantially any of the known halogen-containing derivatives of natural and synthetic elastomers can be employed in the practice of this invention, including mixtures of such elastomers. At the present time, chlorosulfonated polyethylene and chlorinated natural rubber constitute preferred halogenated polyolefins for use in the present invention. The polyolefin is normally utilized in an amount from 10 to 99 percent by weight, preferably from 30 to 70 percent by weight of the overcoat component. The metal oxide or salt of the overcoat component can be any metal oxide or salt such as zinc oxide, magnesium oxide, various lead salts or combinations thereof. The lead salts which are suitable for use in the present invention can be described broadly as polybasic lead salts of phosphorous acid and saturated and unsaturated organic dicarboxylic acids and acid anhydrides. Zinc oxide is the preferred metal oxide while particularly preferred lead salts include dibasic lead phosphite, dibasic lead phthalate, monohydrous tribasic lead maleate, tetrabasic lead fumarate, and mixtures thereof. The metal oxide or salt is typically utilized in an amount from 1 to 35, preferably from 15 to 20 percent by weight of the overcoat component. The overcoat component of the invention can optionally contain other well-known additives including plasticizers, fillers, pigments, reinforcing agents and the like, in amounts employed by those skilled in the adhesive arts to obtain desired color and consistency. Typical additional additives include maleimide compounds (including all maleimide, bismaleimide and related compounds as described in U.S. Patent No. 4,119,587) and phenolic epoxy resins having terminal epoxy functionality. The components of the present invention are typically applied in liquid form by utilizing a variety of solvents to dissolve each respective component. Solvents useful for dissolving the primer component include various polar solvents such as ketones, aromatic solvents such as toluene, xylene and aliphatic solvents such as hexane or heptane, with methyl-ethyl ketone and methyl-isobutyl ketone being the preferred solvents for the primer component. The solvent for the primer component is utilized in an amount sufficient to provide a coating composition having a total solids content (TSC) of from 5 to 70 percent, preferably from 15 to 30 percent. Solvents useful for dissolving the overcoat component include various aromatic solvents such as xylene, toluene, chlorobenzene, dichlorobenzene and halogenated aliphatic hydrocarbons such as trichloroethylene, perchloroethylene, and propylene dichloride, with xylene and toluene being the preferred solvents for the overcoat component. The solvent for the overcoat component is utilized in an amount sufficient to provide a coating composition having a total solids content of from 5 to 70 percent, preferably from 15 to 30 percent. The primer component is typically applied to the surface of the metal to be bonded after which the overcoat component is applied to the coated metal surface although in some applications involving the bonding of post-vulcanized rubber, it may be possible to apply the overcoat component directly to the rubber substrate. In order to cure or crosslink the primer component and the overcoat component to create the permanent rubber-metal bond, the surface of the metal and the rubber substrate are brought together under a pressure of from 20.7 to 172.4 Mega Pascals (MPa), preferably from 50 to 150 MPa. The resulting rubber-metal assembly is simultaneously heated to a temperature of from 140 to 200 degrees C, preferably from 150 to 170 degrees C. The assembly should remain under the applied pressure and temperature for a period of from 3 minutes to 60 minutes, depending on the cure rate and thickness of the rubber substrate. This process may be carried out by applying the rubber substrate as a semi-molten material to the metal surface as in, for example, an injection-molding process. The process may also be carried out by utilizing compression molding, transfer molding or autoclave curing techniques. After the process is complete, the bond is fully vulcanized and ready for use in a final application. The rubber which may be bonded to metal in accordance with the present invention may be selected from any of the natural rubbers and olefinic synthetic rubbers including polychloroprene, polybutadiene, neoprene, Buna-S, Buna-N, butyl rubber, brominated butyl rubber, and the like. The metals to which the rubber may be bonded may also be selected from any of the common structural metals such as iron, steel (including stainless steel), lead, aluminum, copper, brass, bronze, Monel metal, nickel, zinc, and the like. The following examples are presented in order to further illustrate the invention but are not intended to limit in any matter the scope of the invention. The components of the following examples were prepared from the ingredients listed below: Primer A (from U.S. Patent No. 4,769,413): Ingredient Wt. % of Total 1. Ketoxime-blocked isocyanate-functional urethane 15.0 2. Chlorinated rubber 7.05 3. Phenol formaldehyde, approx. 37% methylol @ 70% TSC 5.73 4. Phenol formaldehyde resin modified with 12.5% orthocresol @ 70% TSC 5.0 5. Zinc Oxide 0.70 6. Carbon Black 0.73 7. Silica 1.25 8. TiO₂ 4.44 9. Xylene 18.15 10. Methyl Isobutyl Ketone 41.95 Primer B (present invention): Ingredient Wt. % of Total 1. Polychloroprene Homopolymer (960,000 MW, ∼38% Cl) 3.72 2. Phenol formaldehyde, approx. 37% methylol @ 70% TSC 5.62 3. Phenol formaldehyde resin modified with 12.5% orthocresol @ 70% TSC 5.0 4. Zinc Oxide 1.49 5. Carbon Black 0.60 6. Silica 1.04 7. TiO₂ 3.72 8. Methyl-isobutyl ketone 78.81 The ingredients of each respective component were combined in a conventional manner using a Kady mill mixer. Example 1 Primer A was applied to grit-blasted 1010 cold rolled steel and allowed to dry at room temperature to provide a coating having a dry film thickness of 0.3 mils. The covercoat was applied to the coated steel and allowed to dry at room temperature to provide a second coating having a dry film thickness of 0.6 mils and a total coating thickness of 0.9 mils. The coated steel was bonded to a 1/4" thick slab of Stock #1 natural rubber by compression molding at 330°F for 15 minutes. The resulting rubber-metal assembly was then cooled to room temperature. Example 2 The coated steel of Example 1 was bonded to a 1/4" slab of Stock #2 natural rubber by compression molding at 330°F for 24 minutes. Example 3 A rubber-metal assembly was prepared according to Example 1 with Primer B as the primer component. Example 4 A rubber-metal assembly was prepared according to Example 2 with Primer B as the primer component. Flexibility Test The rubber-metal assemblies of Examples 1 - 4 were prepared according to ASTM D-429. The assemblies were then bent to an angle of approximately 120° and the rubber was peeled away in order to inspect the flexibility of the adhesive. Flexibility was measured in terms of percent rubber retention (R) after bending. The results of the flexibility test are shown in Table 1 below. High Temperature Fluid Test The rubber-metal assemblies of Examples 1 and 3 were exposed to 100% ethylene glycol at a temperature of 135°C for 100 hours. Degradation of the rubber-metal bond was measured in terms of percent rubber retention (R), rubber-cement failure (RC), and cement-metal failure (CM). The results of the high temperature test are shown in Table 2 below. As can be seen from the data presented in Tables 1 and 2, the adhesive system of the present invention simultaneously provides for both flexibility and high temperature fluid resistance and therefore exhibits surprisingly superior properties when compared to prior adhesive systems.

Claims: Claims for the following Contracting States : DE, FR, GB, IT, NL, SE An adhesive system comprising a primer component and an overcoat component, wherein the primer component consists essentially of a non-post chlorinated homopolymer of 2-chlorobutadione - 1,3 having a molecular weight from 200,000 to 1,300,000 and being present in an amount of 5 to 40 percent by weight of the primer component; a heat-reactive phenolic resin having a molecular weight between 300 and 2000, being a reaction product of a phenolic compound and an aldehyde having 1 to 8 carbon atoms and being present in an amount from 10 to 70 percent by weight of the primer component and a metal oxide selected from zinc, magnesium or lead oxides or combinations thereof in an amount of 1 to 35 percent of the primer component and wherein the overcoat component comprises an aromatic hydrocarbon containing at least two nitroso groups attached directly to non-adjacent ring carbon atoms, the hydrocarbon being found present in an amount from 1 to 50 percent by weight of the overcoat component; a halogenated polyolefin comprising chlorosulfonated polyethylene or chlorinated natural rubber or a combination thereof present in an amount from 10 to 70 by weight of the overcoat component and a metal oxide or salt selected from zinc oxide, magnesium oxide or lead salts or combinations thereof present in an amount of 1 to 35 percent by weight of the overcoat component. An adhesive system according to Claim 1, wherein the homopolymer of 2-chlorobutadiene-1,3, has a molecular weight of from 700,000 to 1,100,000 and is present in an amount from 20 to 25 percent by weight of the primer component. An adhesive system according to Claim 1 or Claim 2, wherein the phenolic resin is a mixture of a phenol aldehyde resin and a phenol-aldehyde resin modified with cresol present in an amount from 30 to 50 percent by weigh of the primer component. An adhesive system according to any one of claims 1 to 3 wherein the metal oxide is zinc oxide present in an amount from 5 to 20 percent by weight of the primer component. An adhesive system according to any one of the preceding claims, wherein the aromatic hydrocarbon is m- or p-dinitrosobenzene. An adhesive system according to Claim 5, wherein the nitroso compound is p-dinitrosobenzene present in an amount from 15 to 20 percent by weight of the overcoat component. An adhesive system according to any one of the preceding claims, wherein the halogenated polyolefin is chlorosulfonated polyethylene present in an amount from 30 to 70 percent by weight of the overcoat component. An adhesive system according to any one of the preceding claims, wherein the metal oxide or salt is zinc oxide or dibasic lead phosphite. An adhesive system according to Claim 8, wherein the metal oxide or salt is zinc oxide present in 15 to 20 percent by weight of the overcoat component. A method for bonding a surface of metal to a rubber substrate comprising the steps of applying an adhesive system as claimed in any one of the preceding Claims, including applying the primer component and the overcoat component between the metal surface and the rubber substrate and forcing the surface against the substrate at a pressure of between 20.7 and 172.4 MPa at a temperature of between 140 and 200°C for between 3 and 60 minutes. An adhesively-bonded rubber-metal assembly prepared using the adhesive system of any of Claims 1 to 9 and/or the method of Claim 10. Claims for the following Contracting State : ES A method of forming an adhesive systems comprising a primer component and an overcoat component, wherein the primer component is formed by combining a non-post chlorinated homopolymer of 2-chlorobutadione-1,3 having a molecular weight from 200,000 to 1,300,000 and being present in an amount of 5 to 40 percent by weight of the primer component; a heat-reactive phenolic resin having a molecular weight between 300 and 2000, formed by reacting a phenolic compound and an aldehyde having 1 to 8 carbon atoms, and being present in an amount from 10 to 70 percent by weight of the primer component and a metal oxide selected from zinc, magnesium or lead oxides or combinations thereof in an amount of 1 to 35 percent of the primer component and wherein the overcoat component is formed by combining an aromatic hydrocarbon containing at least two nitroso groups attached directly to non-adjacent ring carbon atoms, the hydrocarbon being found present in an amount from 1 to 50 percent by weight of the overcoat component; a halogenated polyolefin comprising chlorosulfonated polyethylene or chlorinated natural rubber or a combination thereof present in an amount from 10 to 70 by weight of the overcoat component and a metal oxide or salt selected from zinc oxide, magnesium oxide or lead salts or combinations thereof present in an amount of 1 to 35 percent by weight of the overcoat component. A method according to Claim 1, wherein the homopolymer of 2-chlorobutadiene-1,3, has a molecular weight of from 700,000 to 1,100,000 and is present in an amount from 20 to 25 percent by weight of the primer component. A method according to Claim 1 or Claim 2, wherein the phenolic resin is a mixture of a phenol aldehyde resin and a phenol-aldehyde resin modified with cresol present in an amount from 30 to 50 percent by weight of the primer component. A method according to any one of Claims 1 to 3, wherein the metal oxide is zinc oxide present in an amount from 5 to 20 percent by weight of the primer component. A method according to any one of the preceding Claims, wherein the aromatic hydrocarbon is m- or p-dinitrosobenzene. A method according to Claim 5, wherein the nitroso compound is p-dinitrosobenzene present in an amount from 15 to 20 percent by weight of the overcoat component. A method according to any one of the preceding Claims, wherein the halogenated polyolefin is chlorosulfonated polyethylene present in an amount from 30 to 70 percent by weight of the overcoat component. A method according to any one of the preceding Claims, wherein the metal oxide or salt is zinc oxide or dibasic lead phosphite. A method according to Claim 8, wherein the metal oxide or salt is zinc oxide present in 15 to 20 percent by weight of the overcoat component. A method for bonding a surface of metal to a rubber substrate comprising the steps of applying an adhesive system formed by a method, as claimed in any one of the preceding Claims, including applying the primer component and the overcoat component between the metal surface and the rubber substrate and forcing the surface against the substrate at a pressure of between 20.7 and 172.4 MPa at a temperature of between 140 and 200°C for between 3 and 60 minutes. An adhesively-bonded rubber-metal assembly prepared using an adhesive system formed by the method of any of Claims 1 to 9 and/or the method of Claim 10.

Inventors: MOWREY DOUGLAS HUNTER, PONTORE NATALE MICHAEL, MOWREY, DOUGLAS HUNTER, PONTORE, NATALE MICHAEL
Applicants: LORD CORP, LORD CORPORATION
Application year: 1991
Main classification: C09J111
IPC codes: C09J161, C09J121, C09J5, C09J111