Rubber composition for laminated vibrationproofing structure

Abstract: Disclosed is a rubber composition having high damping capacity as well an other excellent properties for example, dependence of elastic modulus on temperature, shear deformation, etc., which is suitable for laminated vibrationproofing structures. The rubber composition contains carbon black for use in a rubber having an iodine adsorption of 70 to 115 mg/g and DBP adsorption (method A) of 115 to 70 ml/g in an amount of 30 to 70 % by weight based on 100 parts by weight of a base rubber. The rubber composition is characterized by further containing: an aromatic petroleum resin having a softening point of 70 to 140°C and a bromine value of 0 to 0.2; and cumarone-indene resin and/or rosin in the ratio which satisfies the relation: 8 ≦ 4 3 A + B ≦ 50 wherein A is a total amount of cumarone-indene resin and rosin formulated, B is an amount of an aromatic petroleum resin formulated and B is not 0.

Description: The present invention relates to a rubber composition for a laminated vibrationproofing structure. Recently, laminated vibrationproofing structures have been widely used as vibration isolators for constructive structures (e.g. buildings). These laminated vibrationproofing structures are introduced between the structures and the foundations to decrease the transmission of earthquake vibration energy to the structures. A wide variety of laminated structures has been proposed. Normally, they are structures wherein a rigid plate and a large damping rubber layer having a viscoelastic property are alternatively laminated (see Fig. 1 hereinafter). Hitherto, in order to enhance the damping capacity, there has been proposed a method comprising formulating a large amount of carbon black or a filler in the rubber, or a method comprising adding a polymer having a high glass transition point. However, in these methods, the elongation of the resulting rubber composition is lowered, or the dependence of the elastic modulus on temperature becomes large, which results in an excessive elastic modulus at the low temperature range of about -10°C. In the case of an earthquake, the laminated vibrationproofing structure produces vibrationproofing and a damping effect by causing shear deformation and as the amount of shear deformation becomes larger, the better the vibrationproofing effect. Those which cause a shear deformation of not less than 50% are desired. Although the laminated vibrationproofing structure is used at temperature in the range of from to 30°C to -10°C, it is important that the elastic modulus does not become too large at the low temperatures. Furthermore, the above damping effect is particularly effective for a rather strong earthquake which causes large deformation (e.g. shear deformation of not less than 5%) in the laminated vibrationproofing structure. Accordingly, it is important that the laminated vibrationproofing structure has a large damping capacity under the large deformation (e.g. not more than 5%). For that purpose, it is required that Tan δ is large at the large deformation range. We have now developed a rubber composition having a large damping capacity as well as other excellent properties, for example, dependence of elastic modulus on temperature, shear deformation, which is suitable for the laminated vibrationproofing structure. That is, the present invention provides a rubber composition with a large damping capacity satisfying the above requirements, said rubber composition having a small dependence of elastic modulus on temperature and a small permanent compression deformation as well as a shear deformation of more than 550%, and having a large Tan δ at the large deformation range (e.g. shear deformation of not less than 5%). Accordingly to the present invention, there is provided a rubber composition containing carbon black having an iodine adsorption of 70 to 115 mg/g and a DBP adsorption (method A) of 115 to 70 ml/100g in an amount of 30 to 70% by weight based on 100 parts by weight of a base rubber, the composition further containing: an aromatic petroleum resin having a softening point of 70 to 140°C and a bromine value of 0 to 0.2; and cumarone-indene resin and/or rosin in the ratio which satisfies the relationships: 4 ≤ A ≤ 25; and 5 ≤ B ≤ 35 where A is a total amount of cumarone-indene resin and rosin formulated, B is an amount of the armoatic petroleum resin formulated. The present invention will be further described with reference to the following drawings, in which:- Fig. 1 is a schematic cross-section illustrating one embodiment of a laminated vibrationproofing structure of the present invention. Fig. 2 is a schematic diagram illustrating the measurement of shear deformation. Fig. 3 is a graph illustrating a relation between Tan δ and shear deformation in case of using various resins for use in rubber. Fig. 4 is a graph illustrating the domain of the relation (I) hereinafter which indicates the amount of cumarone-indene resin, rosin and aromatic petroleum resin formulated. Base rubbers which may be used in the present invention include, for example natural rubber and synthetic rubber, which may be used alone or in combination. Polyisoprene rubber is the preferred synthetic rubber. Other rubbers (e.g. butadiene rubber, styrene-butadiene rubber, etc.) may be also be added in an amount of about 20 parts by weight based on the total weight of the rubber. The carbon black used in the rubber compositions of the present invention has an iodine adsorption of 70 to 115 mg/g, preferably 80 to 110 mg/g and a DBP adsorption (method A) of 115 to 70 ml/100g, preferably 110 to 70 ml/100g. The iodine adsorption and DBP absorption (method A) are measured according to JIS K6211. When the iodine adsorption of the carbon black is less than 70 mg/g, the damping capacity is lowered. When the iodine adsorption is more than 115 mg/g, elongation of the rubber composition is lowered and, further, the processing characteristics (e.g. kneading, calendering, extrusion) deteriorate. When the DBP adsorption of the carbon black is less than 70 ml/100 g, dispersion is deteriorated. When the DBP adsorption exceeds 115 ml/100g, the breaking elongation is lowered. The amount of the carbon black added is 30 to 70 parts by weight, preferably 40 to 65% parts by weight based on 100 parts by weight of the rubber. When the amount of the carbon black is less than 30 parts by weight, the damping capacity is lowered and, when the amount exceeds 70 parts by weight, the breaking elongation is lowered. In the present invention, the aromatic petroleum resin formulated in the rubber is an aromatic petroleum resin having no double bond other than an aromatic ring wherein the aromatic ring and methylene group are alternatively bonded. The softening point is 70 to 140°C, preferably 80 to 130°C. A resin having the softening point of less than 70°C has a low damping capacity, and a resin having a softening point of more than 140°C is scarcely dissolved during kneading and deterioration of the dispersion is liable to occur. In addition, the bromine value is 0 to 2.0, preferably 0. When it exceeds 2.0, the elongation and shear deformation are lowered. The amount of the aromatic petroleum resin formulated is 5 to 35% by weight based on 100 parts by weight of the rubber. When the amount is less than 5 parts by weight, there are disadvantages that the damping capacity deteriorates and the shear deformation is lowered. When the amount exceeds 35 parts by weight, the kneading and calendering properties deteriorate when processing the rubber. In the present invention, in order to enlarge Tan δ at the large defomation range, cumarone-indene and/or rosin are further formulated. Further, the cumarone-indene resin is more preferred in view of Tan δ and the processing characteristics. The ratio of cumarone-indene resin and rosin satisfies the relation: wherein A is a total amount of cumarone-indene resin and rosin formulated, B is the amount of an aromatic petroleum resin formulated. When it is less than 8, sufficient damping capacity can not be obtained. When it exceeds 50, the dependence of the elastic modulus on temperature and permanent compression deformation deteriorate significantly and, at the same time, adhesion increases significantly which results in significant deterioration of processing characteristics. In the above relation (I) A is 4 to 25 and B is 5 to 35. In addition, if A exceeds 25, the shear deformation is decreased. The domain represented by the relation (I) is shown in Fig. 4. Furthermore, the domain which indicates preferred A and B values is shown by an oblique line in the Figure. In the case that Tan δ of not less than 0.25 is required, the domain shown by a cross oblique line is preferred. A vulcanizing agent (e.g. sulfur), vulcanization accelerator, vulcanization aid, anti-aging agent, filler, softening agent and tackifier may optionally be added to the rubber composition of the present invention. The rubber composition of the present invention is vulcanized at 150°C after kneading of the above components. The shear deformation of the rubber thus obtained exceeds 550 %. Various physical properties of the rubber composition of the present invention are measured by the following method. Tensile strength (kgf/cm 2 ), elongation (%) and permanent compression deformation (%) were determined according to JIS K6301. Regarding shear deformation, as shown in Fig. 2, a specimen of 5 mm in thickness was bonded between steel plates by vulcanizing and then the upper and bottom plates were stretched in the opposite horizontal direction to measure breaking elongation. Dynamic complex shear elastic modulus (G*) and Tan δ were measured under the conditions of a frequency of 0.5 Hz, a temperature of 30°C and -10°C and a shear deformation of ±50 %. The following Examples and Comparative Examples further illustrates the present invention in detail. Examples A to E, K to Q, R, T and U and Comparative Examples F to J, S and V By using carbon black and an aromatic petroleum resin as shown in Tables 1 and 2, a rubber composition as shown in Tables 3 to 6 was kneaded, respectively and then the composition was subjected to press vulcanization at 150°C for 35 minutes to measure various physical properties of the resulting vulcanized rubber. The results are shown in Tables 3 to 6, respectively. Target value for design of formulation is as follows. Tan δ (30°C): not less than 0.2 Dependence of shear elastic modulus on temperature: G*(-10°C)/G*(30°C): not more than 2.5 Shear deformation: not less than 550 % Iodine adsorption (mg/g) DBP adsorption (method A) (ml/100 g) HAF 80 101 LS-ISAF 110 80 GPF 26 88 N339 90 121 Softening point (°C) Bromine value (g Br/100 g) Oligotec 1400 120 0.3 Oligotec 1300 95 0.3 Neopolymer 80 83 25 Note: Bromine value was measured according to JIS 2606. Softening point was measured by ring and ball method. The rubber compositions of Examples A and B wherein carbon black and the aromatic petroleum resin are used in the amount within the range of the claim of the present invention show large Tan δ and large shear deformation. They are superior in shear deformation in comparison with Comparative Examples G and J and are superior in Tan δ in comparison with Comparative Example F. In addition, as shown in Comparative Examples H and I, even if carbon black is used, Tan δ is too small when the amount is small (as shown in Comparative Example H). When the amount is too large as shown in Comparative Example I, shear deformation is lowered. Further, the rubber compositions of Examples C, D and E are those wherein the natural rubber and polyisoprene rubber are blended and carbon black and the aromatic petroleum resin are used in the amount within the range of the claim of the present invention. Both rubber compositions of Examples C, D and E show large Tan δ and large shear elongation. The rubber compositions of Examples K to N, P, Q and U satisfy the amount as shown in the oblique line domain in Fig. 4 and show good Tan δ, shear deformation and processing characteristics. Although the rubber compositions of Examples O and R satisfy the above relation (I), the amount are not included within the oblique line domain. The rubber composition of Example O shows large Tan δ and large shear deformation but it is inferior in processing characteristics. The rubber composition of Example R shows small Tan δ . The rubber composition of Comparative Example V shows small Tan δ and the rubber composition of Comparative Example shows inferior processing characteristics. Test for the determination of a relation between Tan δ and shear deformation using various resins for use in rubber Experiment Examples 1 to 8 40 Parts by weight of various resins for use in rubber were formulated in 100 parts by weight of a natural rubber and dependence of dynamic viscoelasticity on deformation of the resulting vulcanized product was measured. The test results are shown in Table 7 and Fig. 3. In Experiment Examples 1 and 7, cumarone-indene resin and rosin were formulated in an amount of 40 parts by weight (phr) based on 100 phr of the natural rubber, respectively. Increase of Tan δ at the large deformation range is remarkable in comparison with Experiment Example 6 wherein no resin is added. On the other hand, in Experiment Examples 2 and 3, alkyl phenol resin (*1 ) and DCPD resin (*2 ) were formulated, respectively. Regarding these resins, increase of Tan δ at the micro deformation range is remarkable. Further, in Experiment Example 8, powdered talc was formulated in an amount of 150 phr. Tan δ at the micro deformation range is large, while Tan δ at the large deformation range is small. In addition, Experiment Example 4 wherein an aromatic resin (*3) is formulated has medium properties in comparison with the above Experiment Examples. Namely, cumarone-indene resin and rosin are suitable as an agent to be formulated in the laminated vibrationdamping structure.

Claims: A rubber composition containing carbon black having an iodine adsorption of 70 to 115 mg/g and a DBP adsorption (method A) of 115 to 70 ml/100g in an amount of 30 to 70% by weight based on 100 parts by weight of a base rubber, the rubber composition further containing an aromatic petroleum resin having a softening point of 70 to 140°C and a bromine value of 0 to 2.0 and cumarone-indene resin and/or rosin in the ratio which satisfies the relationships: 8 ≤ (4/3)A + B ≤ 50 4 ≤ A ≤ 25; and 5 ≤ B ≤ 35 wherein A is a total amount of cumarone-indene resin and rosin formulated and B is an amount of the aromatic petroleum resin formulated. A rubber composition as claimed in claim 1 wherein the base rubber is natural rubber. A rubber composition as claimed in claim 1 wherein the base rubber is synthetic rubber. A rubber composition as claimed in claim 3 wherein said synthetic rubber is a polyisoprene rubber. A rubber composition as claimed in claim 1 wherein one or more additives such as a vulcanizing agent, vulcanization accelerator, vulcanization acid, anti-ageing agent, filler, softening agent or a tackifier are optionally added. Use of a rubber composition containing carbon black having an iodine adsorption of 70 to 115 mg/g and a DBP adsorption (method A) of 115 to 70 ml/100g in an amount of 30 to 70% by weight based on 100 parts by weight of a base rubber, the rubber composition further containing: an aromatic petroleum resin having a softening point of 70 to 140°C and a bromine value of 0 to 2.0; and cumarone-indene resin and/or rosin in the ratio which satisfies the relation; 8 ≤ (4/3) A + B ≤ 50 wherein A is a total amount of cumarone-indene resin and rosin formulated, B is an amount of the aromatic petroleum resin formulated and B is not O as a vibration proofing structure. Use of a rubber composition as claimed in claim 6 wherein the base rubber is natural rubber. Use of a rubber composition as claimed in claim 6 wherein the base rubber is synthetic rubber. Use of a rubber composition as claimed in claim 8 wherein said synthetic rubber is a polyisoprene rubber. Use of a rubber composition as claimed in claim 6 wherein one or more additives such as a vulcanizing agent, vulcanization accelerator, vulcanization acid, anti-aging agent, filler, softening agent or a tackifier are optionally added.

Inventors: SEKIDO FUMIO, TERAKAWA KATSUMI, SEKIDO, FUMIO, TERAKAWA, KATSUMI
Applicants: SUMITOMO RUBBER IND, SUMITOMO RUBBER INDUSTRIES, LTD.
Application year: 1991
Main classification: C08L21
IPC codes: C08K3, B32B25, C08L21