Solid state X-ray imaging device

Abstract: An x-ray image detection device (12) includes a luminescent layer (28) containing an x-ray sensitive phosphor, an amorphous silicon Schottky barrier diode array layer (30), a polysilicon thin film transistor array layer (32), and read-out circuitry (34). The phosphor in the luminescent layer (28) converts incident x-rays to corresponding visible light radiation. The diode array generates an electrical signal corresponding to the intensity of light from the layer (28). Current generated in photodiode array (30) is fed to the gates of the transistors in array layer (32). Read-out circuitry (34) amplifies the signals in the transistors in array layer (32), and converts the signals to digital form.

Description: BACKGROUND OF THE INVENTION The present invention relates to x-ray sensing arrays, and in particular, it relates to arrays that detect x-rays for conversion to digital data. In medical diagnostic applications, the image of a human body is recorded on photographic film sensitive to x-rays. Phosphor-containing screens sensitive to x-rays are placed between the human body and the film to reduce the x-ray dose rate. The combination of x-ray film and phosphor-containing screens produces a radiograph with good resolution (5 line pairs/MM). However, the film requires a substantial amount of time to develop and the image on the film is not in a form that readily lends itself to computer storage or analysis. Efforts have been made to replace x-ray film in radiology through the use of x-ray intensifiers, video cameras, displays, and non-film detectors. One such system employs a scintillation crystal to convert x-rays to corresponding visible light radiation, "Digital Slot Radiography Based on a Linear X-ray Image Intensifier and Two-Dimensional Image Sensors", Beerlage, Levels, and Mulder, SPIE Vol. 626 Medicine, XIV/PACS IV, pages 161-169 (1986). A photodetector is then used to generate an electrical signal corresponding to the intensity of the visible light radiation. The electrical signal from the detector is converted to digital data and stored in a memory device or electrically displayed, such as on a cathode ray tube. Solid state detectors have also been used in x-ray astronomy. One such detector system was reported in "Multi-Element Self-Scanned Mosaic Sensors", Weimer et al, IEEE Spectrum, March 1969, pages 52-65. The system included arrays consisting of a matrix of photodiodes which are charged by light to produce electron-hole pairs. The Catchpole et al U.S. Patent 4,675,739 describes an incident radiation solid state sensing array made of photosensing elements. Each photosensing element includes back-to-back diodes, one a photo-responsive diode and the other, a blocking diode. Each of the diodes has an associated capacitance formed by its electrodes. The magnitude of the charge remaining on a given capacitor is sensed and relates back to the intensity of the incident radiation impinging upon the photosensitive diode. Furthermore, in such a linear photodiode array, the scanning time is so long that real time read-out is made impractical. In addition, the linear photodiode array has to be moved to obtain a two-dimensional image. Another solid state sensing array includes charge-coupled devices. Charge-coupled devices have a layer of relatively conductive semi-conductor material separated from a layer containing electrodes by an insulator in a two-dimensional image sensing array. However, charge-coupled devices can presently be produced at a format of less than 1 inch by 1 inch. Larger formats of arrays have charge transfer problems due to the number of defect devices that can exist in one line of the array. A defective device in one line of the array can result in a charge not being transferred through that line in the array. The Nishiki et al U.S. Patent 4,689,487 describes the use of a large area solid state detector (40cm X 40cm). This solid state detector includes pixels in 2,000 X 2,000 matrix form. Each pixel consists of a photodiode conductively connected in parallel to a capacitor which are both then conductively connected to the drain of a metal oxide semi-conductor field effect transistor (MOSFET). The photodiodes are of a polycrystalline or amorphous material. The Berger et al U.S. Patent 4,810,881 describes an amorphous silicon detector of 36cm X 43cm. Each pixel in the detector includes an amorphous silicon diode that is conductively connected in series to a capacitor which in turn are both then conductively connected to the drain of an amorphous silicon base junction field effect transistor. Neither detector of U.S. Patents 4,689,487 and 4,810,881 has a non-destructive image read-out capability. EP-A-0028960 discloses a detector comprising a plurality of pixels which each comprise a photodiode conductively connected to a gate of a thin film transistor. This reference forms the basis of the preamble of the present claim 1. SID International Symposium, Digest of Technical Papers, 1989, Pages 259-261, discloses a thin film transistor employing amorphous silicon in which the transistors are used for optical image sensors in an image scanner. SUMMARY OF THE INVENTION According to this invention there is provided a radiation detector as claimed in claim 1 herein. The photodiode of the present invention is sensitive to x-rays through use of a luminescent layer which has an x-ray sensitive phosphor. The luminescent layer may be disposed in a phosphor screen or the phosphor may directly overlie the photodiode. Alternatively, the photodiode may be of a composition that is sensitive to x-rays therefore eliminating the need of an x-ray sensitive phosphor. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a schematic view of the present invention in a radiographic system. Figure 2 is an exploded perspective view of the x-ray detector. Figure 3a is a sectional view of a pixel unit of the detector. Figure 3b is a sectional view of a pixel unit of the detector of the present invention including a blocking diode. Figure 4 is a circuit diagram of a pixel unit of the present invention including a blocking diode. Figure 5 is a circuit diagram of a pixel unit without the blocking diode of the present invention. Figure 6 is a graphical view of the response of an integrated detector of the present invention to illumination by light of wavelength λ. Figure 7 is a graphical view of the response of a linear array of 32 pixel units of the present invention to a medical radiographic dose of x-rays. Figure 8 is a graphical view of the thin film transistor output current of the detector over time in response to various levels of x-ray exposure. Figure 9 is a graphical view illustrating the response of a hybrid linear array 32 units pixel of the present invention to a medical radiographic dose of x-rays. Figure 10 is a diagrammatic view of a two-dimensional array detector of the present invention constructed in a modular manner. Figure 11 is a graphical view illustrating the amplification ratio of the second TFT. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An x-ray image detection apparatus of the present invention is generally illustrated at 10 in Figure 1. The apparatus 10 includes a solid state x-ray detector 12. The solid state detector 12 detects x-rays 14 emitted from a source 16 that pass through a human body 18. An analog video signal is received from the detector 12 by a central processing unit 20 and is converted into a digital signal by an analog to digital converter and stored in memory. An image using the stored data may be projected on a display 22 or a hard copy 24 provided through a laser printer 26. The solid state radiation detector 12 is more fully illustrated in Figure 2. The detector 12 includes a luminescent layer 28 containing an x-ray sensitive phosphor, an amorphous silicon Schottky barrier diode array layer 30, a polysilicon thin film transistor (TFT) array layer 32, and read-out circuitry 34. The phosphor in the luminescent layer converts incident x-rays to corresponding visible light radiation. The amorphous silicon Schottky barrier diode array generates an electrical signal corresponding to the intensity of light from the luminescent layer 28. Current generated in the photodiode array 30 is fed to the gates of associated TFT's. The read-out circuitry 34 is used to amplify the electrical signal and convert the analog signal into digital, and store the signal in memory so that the signal may be used in an optical or electrical display. The detector can either be made on a single module or a multi-module (tiled structure), which has the read-out circuitry 34 incorporated on the same substrate. The read-out circuitry is based on high mobility polysilicon technology which is know in the art and is located along the periphery of the module or multi-module structure. The detector 12 is composed of a plurality of pixels. An exemplary pixel 36 is illustrated in Figure 3a without the luminescent layer 28. Each pixel 36 has an amorphous silicon Schottky diode 38 preferably overlaying a polysilicon thin film transistor 40. The photodiodes can also be positioned such that the diodes exist in a side-by-side relationship with the TFTs. The photodiodes alternatively can be of a p-i-n form where p is a p-type doped amorphous silicon, i is an undoped amorphous silicon, and n is an n-type doped amorphous silicon, or the photodiode may be of an MIS arrangement wherein M is metal, I is an insulating layer, and S is an undoped amorphous silicon. Pixel area sizes of 420 microns 2 , 220 microns 2 , 120 microns 2 , and 80 microns 2 have been produced. Production of pixels having an area of 50 microns 2 or smaller is believed to be possible with no anticipated problems. The thin film transistor 40, in turn, is disposed on a substrate such as a silicon wafer. However, a quartz substrate or glass substrate is preferred due to the larger area that such substrates provide. The Schottky barrier diode 38 includes an undoped hydrogenated amorphous silicon layer 42 adjacent a doped hydrogenated amorphous silicon layer 44 with the two layers 42 and 44 being sandwiched by a conductive layer 46 and a metal layer 48. The Schottky barrier is formed between metal layer 48 and undoped amorphous silicon layer 42. The metal layer 48 has been preferably annealed in a hydrogen atmosphere. A layer of lead 49 or other heavy metal such as tungsten or platinum is disposed between the conductive layer 46 and the thin film transistor 40 for protection of the transistor from x-rays. The diode 38 may additionally include a transparent conductive oxide or other optical matching layer 50 as a top layer. For outside connection, a layer of metal 51 is deposited at the periphery of the diodes. The thin film transistor includes a source 52, a drain 54, and a polysilicon gate 56. The gate of the thin film transistor is conductively connected to the conducting layer 46 of the diode 38 preferably by a metal contact 66. The current generated in the Schottky barrier diode 38 by the incident x-rays is fed to the gate of the TFT and changes the magnitude of the drain source current to the transistor. The potential on the TFT gate is slowly dispersed and readings from the drain source current can be made over prolonged periods of time. The charge storage time on the gate 56 is in the range of 20 to 30 seconds, and therefore several of the readings can be made for each x-ray exposure of the device of the present invention. The ability to take several readings permits reduction of noise by averaging the readings, and thereby, enhancing the signal to noise ratio of the detector. The read-out circuitry 34 includes a shift register 68 and a multiplexer 70 for providing a mechanism to transmit signals for amplification, conversion from analog into digital, and for storing such signals in memory in the central processing unit 20. Outputs 72 for video display of the storage signal, or output 74 for further processing of the signal by a laser printer are also provided. The amorphous silicon Schottky barrier diode of the present invention exhibits a dark current in the range of 10 -11 A/cm 2 , a forward current in the range of 10 -2 to 10 -1 A/cm 2 , and the ratio of photocurrent over dark current is approximately 10 4 at low levels of illumination, that is 1.0 to 10µW/cm 2 . To prevent photocurrent from one photodiode in the array reaching an adjacent photodiode, a blocking diode 76 is provided in association with each photodiode 38, as illustrated in Figure 4. As also shown in Fig. 4, source 52 of the thin film transistor is connected to a first terminal having a first potential -V1, and drain 54 of the thin film transistor is connected to a second terminal having a second, ground potential. The cathode of photodiode 38 is connected to gate 56 of the thin film transistor, and the anode of photodiode 38 is connected to a third terminal having a third potential -V2. The cathode of blocking diode 76 is connected to the cathode of photodiode 38 and to gate 56 of the thin film transistor, and the anode of blocking diode 76 is connected to a fourth terminal having a fourth potential pulsed between approximately 0 volts and 1.3 volts. As further illustrated in Figure 3b, in which like reference characters are used to indicate like elements that were illustrated in Figure 3a, the polysilicon TFT 40 is essentially the same as described with reference to Figure 3a. Situated on top of the'polysilicon TFT is the photodiode 38 and the blocking diode 76. The photodiode 38 and the blocking diode 76 have the conductive layer 46, the doped hydrogenated amorphous silicon layer 44 and the undoped amorphous silicon layer 42 as common layers. In addition, the lead layer 49 may also be included between the conductive layer 46 and the TFT 40. To form the photodiode and the blocking diode, a metal layer 48a and 48b is formed in much the same way as metal layer 48 in Figure 3a. However, using conventional patterning techniques, distinct layers 48a and 48b are formed such as to be conductively separated to form the photodiode 38 and the blocking diode 76. Both layers 48a and 48b are preferably made of platinum. Area ratios of the blocking diode to the photodiode are in the range between 1:22 to 1:1. A metal layer 57 is deposited on the metal layer 48b of the blocking diode 76 for connection to the read-out circuitry and in a thickness sufficient enough so that no light penetrates the blocking diode. A sufficient thickness is in the range of 2000x10 -10 -5000x10 -10 m (2,000 - 5,000Å). The photodiode also includes the metal layer 51 deposited at the periphery to provide a connection to the read-out circuitry. The prevention of photocurrent traveling between adjacent photodiodes is also resolved by the arrangement illustrated in Figure 5. In Figure 5, the TFT 40 is biased in an opposite manner from the arrangement of Figure 4, permitting the elimination of the blocking diode. The x-ray sensitive phosphor for use in the detector of the present invention may be chosen from those well-known in the radiographic art for use in intensifying screens. Such phosphors include, but are not limited to, gadolinium oxysulfide doped with terbium or europium, yttrium oxide, calcium tungsten, barium fluorochloride doped with europium, barium sulfate or strontium sulfate doped with terbium or thulium or dysprosium, and zinc sulfide. The phosphor may be situated individually over each pixel in microcolumns with a column size equal to the photodiode size. The individual microcolumn arrangement confines the scattered emitted light to the area of the associated pixel. If the diode is initially deposited on the substrate and the TFT formed on the diode, the phosphor can then be embedded directly into the substrate. Conventional screens are also contemplated as part of the present invention. The use of such screen results in some spreading of the emitted light which causes a reduction in the image sharpness. The use of columnar phosphor results in greater image sharpness since the emitted light is confined to the column area. In addition, since the scattered emitted light is confined, the thickness of the phosphor layer can be increased without loss in image sharpness. Increasing the thickness of the phosphor provides greater absorption of incident x-rays thereby improving the sensitivity of the detector. Techniques for producing columnar phosphor are known in the art. European patent application Publication 0 175 578 describes the use of columnar phosphor layers selected from barium sulfate doped with terbium or thulium or dysprosium, strontium sulfate doped with terbium or thulium or dysprosium and alkali halides. Such phosphor layers may be formed by vacuum evaporation, sputtering, or other vacuum deposition techniques known in the art. Columnar phosphor screens including oxysulfides of gadolinium or lanthanum are described in U.S. Patent 4,069,355. Such structured phosphors are made by vapor deposition techniques. The read-out scheme and the detector structure of the present invention can also be applied to the detector where the photodiodes are directly sensitive to the x-rays. Photodiodes which are directly sensitive to x-rays provide an x-ray sensor without the necessity of a phosphor layer. Photodiodes and also blocking diodes according to this embodiment may be diodes having an x-ray sensitive layer such as Se, PbSe, PbS x Se i-x, CdTe, HgCdTe, SeTe or other high atomic number materials. The structure of the Se diodes can be, for example, Schottky barrier type of transparent conductive oxide/Se/metal, transparent conducting oxide CdSe/Se/metal. The structure of CdTe diodes can be, for example, transparent conducting oxide/CdSe/CdTe/metal. The structure of HgCdTe diodes can be, for example, transparent conducting oxide/CdS/ HgCdTe/metal. The photodiodes directly sensitive to x-rays may be made by using thin film deposition techniques know in the art such as evaporation, sputtering, or electrodeposition. Thickness of the x-ray sensitive layer is in the range of 10µm to 500µm. The following examples are for illustrative purposes only and are not intended to limit the present invention in any way. The examples are being submitted in order to illustrate more explicitly the process and product of the present invention. EXAMPLE 1 A linear array solid state x-ray radiation detector was made by first growing a layer of silicon oxide of approximately 1 µm (one micron) thickness on a 7.62 cm (3-inch) wide silicon wafer. The 1 µm (one micron) layer of silicon oxide was used as an insulator. A second layer of amorphous polysilicon was formed using low pressure chemical vapor deposition of approximately 1500x10 -10 m (1,500Å) thickness at approximately 560°C at 23.94 Pa (180 m Torr). Plasma-enhanced chemical vapor deposition could also have been used to form the polysilicon amorphous layer. The wafers containing the two layers were then annealed in a nitrogen atmosphere of approximately 200 Pa (1.5 Torr) and at approximately 620°C for 24 hours to form a crystalline polysilicon layer. The grain size of the crystalline polysilicon ranged from 500x10 -10 - 3000 x 10 -10 m (500Å - 3,000Å). The now crystalline polysilicon layer was patterned using photo-lithographic techniques into discrete islands. A 1000 x 10 -10 m (1,000Å) thick amorphous silicon oxide layer for the gate was grown at approximately 1,050°C as a dielectric layer. Using low pressure chemical vapor deposition, a polysilicon layer of approximately 3500 x 10 -10 m (3,500Å) thickness to be used as the gate of the to be formed transistor was deposited and patterned. An n+-type silicon drain and source were formed by implanting phosphorus by ion beam deposition at a level of about 10 15 atom/cm 2 . The phosphorus implantation was done before the formation of via holes through the amorphous silicon oxide. After implantation, the phosphorus was activated during a 30 minute annealing process in a nitrogen atmosphere at approximately 1,050°C. If implantation were to be performed after the formation of via holes through the amorphous silicon oxide, the thickness of the polysilicon gate can be reduced from 3500 x 10 -10 m (3,500Å) to a range of 500 x 10 -10 m (500Å) to 1500 x 10 -10 m (1,500Å). The reduced thickness of the polysilicon gate will enhance the effectiveness of subsequent plasma hydrogenation as will be described below. Aluminum was then deposited for the gate electrode by sputtering. Aluminum-silicon-copper alloy/chromium may also be used as the material for the gate electrode. The device was then annealed in a forming gas containing 15 percent hydrogen and 85 percent nitrogen to improve the contact between the aluminum and the silicon. The annealing was followed by plasma hydrogenation in a mixture of 50 percent nitrogen and 50 percent hydrogen at 300°C for 30 minutes. Annealing times of up to one hour have been successfully employed. An insulating layer of 3000 x 10 -10 m (3,000Å) of SiO x was initially deposited and then a layer of 3000 x 10 -10 m (3,000Å) thickness of SiN x was deposited on the annealed device as a combined insulation layer. Both the SiO x and SiN x was deposited by plasma-enhanced chemical vapor deposition. The SiN x layer is deposited on top of the gate electrode of the TFT to optimize the amount of hydrogen incorporated into the grain boundaries during the plasma hydrogenation. The SiN x layer reduces the number of trapping defects and reduces the leakage current of the TFT. Chromium metal plugs were used to fill the via holes through the SiN x /SiO x layer to the gate electrodes of the now formed thin film transistors. An aluminum-chromium alloy may also be used to form the metal plugs, although the metal plugs can be made of any suitable metal. Prior to the photodiode formation, Probimide 408 sold by Ciba-Geigy Corporation of Ardsley, New York, was deposited by spin coating to planarize the surface of the thin film transistors. Approximately a 1µm thickness of the Probimide was deposited. Other types of polyimide or spin-on glass may be substituted for the Probimide in a thickness range of approximately 1µm to 2µm. The Probimide layer improves the performance of the detector since the planarization reduces and/or smooths out the slope in the photodiode. Planarizing the surface on which the photodiode rests will reduce possible high electric fields across the photodiode. When the thickness of the photodiode is too thin, the field is high at a given voltage. A high electric field across the device can deteriorate or destroy the device. Prior to the formation of the Schottky barrier diode, a 1 to 2 micron layer of lead was deposited on the Probimide 408. The lead serves to reduce the x-rays that may be received by the thin film transistors. Other metals of a high atomic number that have a high x-ray absorption such as tungsten or platinum may also be used. Next, a Schottky barrier diode was formed by initially depositing an electrode layer of chromium of an approximate thickness of 1000 x 10 -10 to 5000 x 10 -10 m (1,000Å to 5,000Å) by sputtering. Next, a phosphorus doped n-type amorphous silicon was deposited on to the layer of chromium, using plasma-enhanced chemical vapor deposition. Prior to deposition any CrO x occurring on the chromium surface was treated in an argon plasma. Hydrogen in place of argon may be used. The chromium in the doped amorphous silicon layers was patterned by using wet etching solution techniques. The etched patterns of chromium and n-type phosphorus doped amorphous silicon were dipped in a solution of 2 percent HF in deionized water to remove any native SiO x on the doped amorphous silicon surface. The native SiO x can also be removed using an in-situ anhydrous fluoride cleaning step. The anhydrous fluoride cleaning step would be preferred in a manufacturing setting and for least impact on the environment. Next, an undoped layer of amorphous silicon of approximately 5000 x 10 -10 m (5,000Å) thick was deposited on the doped amorphous silicon layer. Both the doped amorphous silicon layer and the undoped amorphous silicon layer were deposited in a plasma-enhanced chemical vapor deposition system. The gases used in the deposition system were silane (SiH 4 ) and pure hydrogen for undoped amorphous silicon, and for phosphorus doped amorphous silicon, silane, phosphine and hydrogen and hydrogen were used. The substrate temperature was kept as 250°C. The amorphous silicon was not patterned. However, the amorphous silicon may be patterned to form islands by using microlithographic techniques. The surface of the undoped amorphous silicon layer was then treated by dipping in two percent HF in deionized water to remove native SiO x . The native SiO x can also be removed by using an in-situ anhydrous fluoride cleaning step. A platinum layer of approximately 150 x 10 -10 m (150Å) thick was sputtered on to the undoped a-Si:H layer. The platinum layer was then patterned for a top electrode to form the blocking diode and the photodiode using a lift-off etch technique. The area of the photodiode and the area of the blocking diode for each pixel are determined by area of the platinum layer. The area ratio is varied from 1:1 to 1:22. The platinum layers of the blocking diode and the photodiode are separated by the amorphous silicon layer. To reduce the defects at the a-Si:H/platinum interface, the diodes were annealed in a hydrogen atmosphere at a temperature of approximately 300°C for approximately 1 to 1.5 hours. A first layer of SiO x of approximately 2000 x 10 -10 m (2,000Å) thickness and then a second layer of SiO x of approximately 1500 x 10 -10 m (1,500Å) thickness was deposited using plasma-enhanced chemical vapor deposition as an insulator. The two layers of SiN x /SiO x were patterned such that the platinum layer was disposed to serve as an electrode. An aluminum top electrode layer was then deposited by sputtering. The aluminum may also be deposited by E-beam evaporation. The top aluminum electrode layer was then patterned using a lift-off etching technique. A wet etching technique may also be used. To further improve the contact and the device performance, the array of devices was annealed in a forming gas atmosphere at approximately 275°C for approximately 1 hour. Other metals for the gate, drain, and source of the TFT may also be used such as aluminum-copper-silicon alloy, aluminum-chromium double layer, tungsten silicide, or other metal silicides. Alternatively, the polysilicon thin film transistor can also be made in p-type, such that the drain and source are doped with a p-type dopant such as boron. The boron doping is done using ion-implantation techniques. The response of the detector produced in this example with visible light of 1µW/cm 2 is illustrated in Figure 6. The testing circuitry used to obtain the data of Figure 6 is illustrated in Figure 4. The data of Figure 6 indicates that the detector is sensitive to a very low light level, which corresponds to a medical x-ray dose of 1 to 5 mR. Similar results were observed when the detector was exposed under a medical x-ray dose of 90 kVp at 200mA for 2 seconds with an aluminum filter thickness of 20 mm. These results are illustrated in Figure 7. The detector was sensitive down to less than 1 mR using a 3-M Trimax B12 intensifying screen at 90 kVp at 200mA for 16 ms with an x-ray source being at a distance of 1 meter from the detector. EXAMPLE 2 A 32 pixel linear array detector was fabricated using techniques similar to those described in Example 1, except that the platinum layer was not patterned to form a blocking diode instead the entire area of the platinum layer was used for the photodiode.3 The 32 pixel linear array detector was tested using x-ray exposures from 0.0125 to 0.05 J/kg (1.25 mR to 5 mR). A 3-M Trimax B12 intensifying phosphor screen was used. A graph of the TFT output current before and after x-ray exposures of 0.05, 0.025, 0.0125 J/kg (5 mR, 2.5 mR, 1.25 mR), and 0 J/kg (0 mR) are illustrated in Figure 8. The graph of Figure 8 indicates that the output current can be read several times after exposure with the signal being present for at least 20 seconds after the x-ray exposure. The ability to read a single exposure several times improves the signal-to-noise ratio of the detector. EXAMPLE 3 A hybrid detector array was made by bonding by wiring a 1x32 amorphous silicon photodiode array to a 1x32 polysilicon thin film transistor array to form a hybrid detector. The photodiode array and the polysilicon TFT array were produced using techniques similar to those described in Example 1. The photodiodes and the TFTs were produced on two separate substrates. A linear array of photodiodes and a linear array of TFTs were bonded by cutting the photodiode array and TFT arrays previously formed and then bonding the diodes and TFTs together at their cut edges by soldering. The hybrid detector was used to optimize the circuit design for the detector. The hybrid detector of Example 3 provides freedom to select the best diode array and the best TFT array and to combine the two to produce an array that will have maximum performance. The hybrid detector was exposed to 1.6µW of wavelength 550nm and the results are shown in Figure 9 for two different exposure times of 100 msec. and 200 msec. The hybrid detector of this example using a 3-M Trimax B12 phosphor screen and aluminum filters of 3.17 mm and 20 mm was exposed to a 90 kVp x-ray tube 200 mA for 200 msec. Drain-source current of 2µA was observed using the aluminum filter of 3.17 mm. Drain-source current of 0.6µA was observed when using the 20 mm aluminum filter. The decay time using the detector of this example was as long as 15 seconds and allowed several readings for one exposure thereby enhancing the signal-to-noise ratio of the final recorded signal. EXAMPLE 4 To increase the final output signal of the detector, a second polysilicon TFT could be added to the already existing polysilicon TFT of the detector in Example 2. The gate of the second TFT is connected to the drain of the first TFT in each pixel. Both TFTs can be fabricated using techniques similar to those described in Example 1. The calculated results indicate an amplification ratio of up to 50 times using the second TFT, as illustrated in Figure 12. EXAMPLE 5 A large area x-ray sensor 58 of 35.6 x 43.2 cm (14 inches x 17 inches) is made from four 1.8 x 22.9 cm (7 inch x 9 inch) sensor array modules 60, 62, 63, and 64 as illustrated in Figure 10. Each module has a 2,000 x 2,000 photodiode-TFT array. Electronic circuitry is arranged at the corners of each of the modules. An integrated scanner 66 is built simultaneously with the diode/TFT pixel matrix using known thin film deposition techniques resulting in a fully integrated drive circuit inactive matrix as illustrated in Figure 10. Each module is in overlapping relationship with an adjacent module by a distance that is less than the pixel size, which in this example is approximately 80µm. No imaging loss due to the addition of the drive circuity is anticipated since the drive circuitry is outside the viewing area and can be fully redundant. For high mobility polysilicon-based CMOS devices for integrated scanner circuitry, laser annealed rapid thermally annealed polysilicon may be used for this device.

Claims: A radiation detector (12) comprising: a plurality of pixel areas arranged in an array; a plurality of thin film transistors (40), each of said plurality of thin film transistors (40) being disposed within a respective one of said plurality of pixel areas, and each of said plurality of thin film transistors (40) having a gate (56), source (52), and drain (54), wherein said source (52) is connected to a first terminal having a first potential, and said drain (54) is connected to a second terminal having a second potential; a plurality of photodiodes (38), each of said plurality of photodiodes (38) being disposed within a respective one of said plurality of pixel areas, each of said plurality of photodiodes (38) having a first electrode connected to the gate (56) of a respective one of said plurality of thin film transistors (40), and a second electrode connected to a third terminal having a third potential, and each of said plurality of photodiodes (38) generating current in response to X-ray radiation; characterised by a plurality of blocking diodes (76), each of said plurality of blocking diodes (76) being disposed within a respective one of said plurality of pixel areas, each of said plurality of blocking diodes (76) having a first electrode connected to the first electrode of a respective one of said plurality of photodiodes (38) and to the gate (56) of a respective one of said plurality of thin film transistors (40), and each of said plurality of blocking diodes (76) having a second electrode connected to a fourth terminal having a fourth potential, wherein each of said plurality of blocking diodes (76) substantially blocks current flow from said first electrode of said respective one of said plurality of photodiodes (38) to said fourth terminal, each of said plurality of blocking diodes (76) thereby preventing said current generated by one of said plurality of photodiodes (38) from leaking to other ones of said plurality of photodiodes (38) disposed in other ones of said plurality of pixel areas. The detector (12) of claim 1 and further including an x-ray sensitive phosphor (28) in light receiving association with each of said photodiodes (38). The detector (12) of claim 1 wherein each of said photodiodes (38) includes an x-ray sensitive layer. The detector (12) of any one of claims 1-3 wherein the pixel areas are disposed in a two-dimensional array. The detector (12) of any one of claims 1-4 wherein each of the photodiodes (38) is an amorphous silicon diode. The detector (12) of claim 5 wherein each of the amorphous silicon diodes includes an undoped amorphous silicon layer (42) and a doped amorphous silicon layer (44) adjacent the undoped amorphous silicon layer (42), both of said silicon layers being sandwiched between first and second electrode layers (46, 48a), the first electrode layer being in conductive contact with the gate of the thin film transistor (40). The detector (12) of any one of claims 1-6 and further including an x-ray absorbing metal layer (49), the x-ray absorbing metal layer (49) being in contact with the photodiodes (38) and the gates (46) of the thin film transistors (40). The detector (12) of any one of claims 1-7 and further including an insulating layer disposed between the thin film transistors (40) and the photodiodes (38) and including means (66) for permitting conductive connection between the gates (56) of the thin film transistors (40) and the photodiodes (38). The detector (12) of any one of claims 1-8 and further including circuitry means (34) for receiving and sending electrical signals from the pixel areas in the array. The detector (12) of claim 9, wherein the circuitry means (34) is disposed along the periphery of the array.

Inventors: DAHLQUIST JOHN C, TRI TRAN NANG, DAHLQUIST, JOHN C., TRI TRAN, NANG, DAHLQUIST, JOHN C., C/O MINNESOTA MINING AND, TRI TRAN, NANG, C/O MINNESOTA MINING AND
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1991
Main classification: H01L27
IPC codes: H01L27, H04N5, H01L31, G01T1, A61B6