Brazing alloys and method of use

Abstract: A cobalt base, high temperature brazing alloy has a composition, by weight of: Nickel from about 8.5% to about 12.5% Chromium from about 24% to about 40% Tungsten from about 0% to about 9% Carbon from about 0.03% to about 0.6% Boron from about 0.01% to about 3.5% Silicon from about 0.1% to about 11% Manganese up to about 2% Hafnium from about 0.1% to about 3% Tantalum from about 0.1% to about 8% Zirconium from about 0% to about 1% Titanium from 0% to about 1% Cobalt Balance The alloy may be used for example in the repair of Co-base turbine component superalloys.

Description: This invention relates to alloys, to the repair of alloy articles, and to brazing alloy compositions. Such compositions may be used in, for example, an activated diffusion healing process utilized to repair gas turbine nozzles with service-induced damage. There are numerous cobalt based alloys used in both the manufacture and repair of high-temperature operating gas turbine engine components including combustors, turbine vanes, nozzles, etc. Representative examples of cobalt base alloys for the production and/or repair of superalloy articles are disclosed in U.S. Patent Nos. 4,830,934; 4,614,296; 4,381,944; 4,285,459; 4,058,415; 3,355,287; 3,276,865; 3,271,140; and 4,396,577. During operation of such components under high-temperature operating conditions, various types of damage or deterioration can occur. For example, cracks can result from thermal cycling, foreign object impact, and/or corrosion. It is, of course, well known that the cost of these components is relatively high and therefore, it is more desirable to repair such components than to replace them. US-A-4765817 discloses a cobalt-base alloy for use in spinners for spinning for example glass fibers consisting of 27-34% Cr, 5-15% Ni, 5-10% W, 1.5-4% Ta, 0.01-0.5% Zr, 0.01-0.2% Si, 0.4%-0.7% C, 0.005-0.5% B, 0.15-1.6% Hf, balance Co. However such alloy compositions would not in general be suitable for brazing operations for the repair of gas-turbine nozzles. SUMMARY OF THE INVENTION The present invention provides a method of repairing a Co-base superalloy substrate comprising the steps of: (a) preparing a mixture of a brazing alloy composition in powder form comprising by weight: Nickel from 8.5% to 12.5% Chromium from 24% to 40% Tungsten from 0% to 9% Carbon from 0.03% to 0.6% Boron from 0.01% to 3.5% Silicon from 0.1% to 11% Manganese up to 2% Hafnium from 0.1% to 3% Tantalum from 0.1% to 8% Zirconium from 0% to 1% Titanium from 0% to 1% Cobalt plus incidental impurities Balance and a powder of said Co-base superalloy; and (b) vacuum depositing said mixture on a region of said Co-base superalloy substrate to be repaired, thereby causing said brazing alloy power to melt and alloy with said Co-base superalloy powder and said Co-base superalloy substrate. In a further aspect, the invention provides a cobalt base, high temperature brazing alloy for use in the aforesaid method comprising by weight: Nickel 10%; Chromium 29%; Tungsten 7%; Carbon 0.1%; Boron 2.5%; Silicon 2.5%; Manganese 0.6%; Hafnium 2%; Tantalum 2%; and Cobalt plus incidental impurities Balance In a further aspect, the invention provides a cobalt base, high temperature brazing alloy for use in the aforesaid method comprising, by weight: Nickel 10%; Chromium 29%; Tungsten 3.5%; Carbon 0.1%; Boron 1%; Silicon 7%; Manganese 0.6%; Hafnium 0.1%; Tantalum 4%; and Cobalt plus incidental impurities. Balance One example of the present invention relates to an improved brazing alloy composition for the repair of environmentally-damaged gas turbine parts exposed for long periods of time to corrosive high-temperature operation. This illustrative brazing alloy composition is specifically adapted for use in an activated diffusion healing process to rebuild, for example, nozzles, by brazing a mixture of the brazing alloy and the base metal of the nozzle in particulate form. Specifically, repair is effected by brazing a deposit containing a mixture of braze alloy and parent alloy powders. The vacuum brazing cycle causes the braze alloy to melt and alloy with the parent alloy powder and the parent substrate surface. A post-braze diffusion heat treatment cycle is then applied to promote further interdiffusion. The mechanical properties of the resultant repaired region nearly approach those of the parent alloy. Examples of brazing alloys in accordance with this invention are cobalt-base alloys with a high chrome content and also containing B and Si as melting point depressants. The latter are necessary to allow the brazing alloy to melt without also melting the parent alloy component. The cobalt base alloys of this invention also emphasize the major MC-forming elements Ta and Hf. Accordingly, in one preferred embodiment of the method of this invention, a brazing alloy is provided which comprises, by weight: Nickel from 8.5% to 12.5% Chromium from 24% to 40% Tungsten from 0% to 9% Carbon from 0.03% to 0.6% Boron from 0.01% to 3.5% Silicon from 0.1% to 11% Manganese up to 2% Hafnium from 0.1% to 3% Tantalum from 0.1% to 8% Zirconium from 0% to 1% Titanium from 0% to 1% Cobalt plus incidental impurities. Balance Examples of alloys of this invention are high temperature 648-1036°C (1200-1900°F) resistant and provide superior mechanical properties as well as oxidation and corrosion resistance in the above temperature range. A better understanding of the invention will become apparent from the detailed description which follows. Examples of brazing alloys used in the method of this invention are adapted specifically for use with a known Co-base superalloy turbine nozzle having the following composition, by weight: Ni 10% Cr 29% W 7% C 0.35% B 0.015% Si 0.1% Mn 0.1% Hf 1% Ta 0.5% Zr 0.5% Ti 0.2% Co plus incidential impurities. Balance Examples of alloys of this invention are also formulated to be compatible with another advanced Co-base superalloy substrate material, comprising, by weight: Ni 10% Cr 29% W 7% C 0.25% Si 0.9% Mn 0.6% Co plus incidential impurities. Balance The principal objective in either case is to retain the mechanical and environmental resistance properties of the above "parent" alloys, while lowering the melting temperature of the brazing alloy (but not the parent alloy) for good brazing characteristics. One aspect of the present invention is embodied in a method of repairing a Co base superalloy using a powder of a Co-base alloys having the following composition range, by weight: Nickel from 8.5% to 12.5% Chromium from 24% to 40% Tungsten from 0% to 9% Carbon from 0.03% to 0.6% Boron from 0.01% to 3.5% Silicon from 0.1% to 11% Manganese up to 2% Hafnium from 0.1% to 3% Tantalum from 0.1% to 8% Zirconium from 0% to 1% Titanium from 0% to 1% Cobalt plus incidential impurities. Balance A first exemplary alloy in accordance with the present invention has the following composition: Nickel 10% Chromium 29% Tungsten 7% Carbon 0.1% Boron 2.5% Silicon 2.5% Manganese 0.6% Hafnium 2% Tantalum 2% Zirconium 0% Titanium 0% Cobalt plus incidential impurities. Balance A secondary exemplary alloy in accordance with the present invention has the following composition: Nickel 10% Chromium 29% Tungsten 3.5% Carbon 0.1% Boron 1% Silicon 7% Manganese 0.6% Hafnium 0.1% Tantalum 4% Zirconium 0% Titanium 0% Cobalt plus incidential impurities. Balance As noted hereinabove, examples of alloys of this invention have been formulated with Boron and Silicon as melting point depressants. This is necessary to insure that, during brazing, the brazing alloy mixture will melt but not the parent alloy. While Boron is advantageous in this respect, it is detrimental to good oxidation resistance. The examples of alloys of this invention, therefore, also incorporate the major MC-forming elements Tantalum and Hafnium to provide increased oxidation resistance. Since these refractory elements (also including Zr and Ti) are also known to be the most thermodynamically stable boride formers, refractory borides of the MB₂ or MB types should form in the braze region as discrete particles. Although this may inhibit the migration of Boron away from the braze region, it will minimize the occurrence of script- or eutectic-like boride structures which will impair strength and ductility. In an illustrative use, a mixture of a brazing alloy of this invention and parent alloy powders are vacuum brazed in situ to rebuild turbine nozzles (or other components) with service induced damage. The vacuum brazing causes the braze alloy to melt with the parent alloy powder and parent substrate surface. A conventional post-braze diffusion heat treatment cycle is then applied to promote further interdiffusion as well as the migration of Boron away from the braze region. The effect of Boron on surface corrosion resistance is thus minimized. The mechanical properties of the repaired region, using the examples of alloys of this invention, approximate those of the parent alloy. Thus, the examples of brazing alloys of this invention provide superior oxidation and corrosion resistance, and superior mechanical properties over the temperature range of about 648-1036°C (1200° to 1900°F) so that the repaired region of the turbine nozzle (or other component) has mechanical properties similar to those of the parent alloy.

Claims: A method of repairing a Co-base superalloy substrate comprising the steps of: (a) preparing a mixture of a brazing alloy composition in powder form comprising, by weight: Nickel from 8.5% to 12.5% Chromium from 24% to 40% Tungsten from 0% to 9% Carbon from 0.03% to 0.6% Boron from 0.01% to 3.5% Silicon from 0.1% to 11% Manganese up to 2% Hafnium from 0.1% to 3% Tantalum from 0.1% to 8% Zirconium from 0% to 1% Titanium from 0% to 1% Cobalt plus incidental impurities Balance and a powder of said Co-base superalloy; and (b) vacuum depositing said mixture on a region of said Co-base superalloy substrate to be repaired, thereby causing said brazing alloy power to melt and alloy with said Co-base superalloy powder and said Co-base superalloy substrate. The method according to claim 1 and further including the step of: (c) heat treating the repaired region to promote interdiffusion and migration of Boron away from said region. The method according to claim 1 wherein said brazing alloy composition comprises, by weight: Ni 10%; Cr 29%; W 7%; C 0.1%; B 2.5% Si 2.5%; Mn 0.6%; Hf 2%; Ta 2%; and Co plus incidental impurities balance The method according to claim 1 wherein said brazing alloy composition comprises, by weight: Ni 10%; Cr 29%; W 3.5%; C 0.1%; B 1%; Si 7%; Mn 0.6%; Hf 0.1%; Ta 4%; and Co plus incidental impurities balance The method according to any preceding claim wherein said Co-base superalloy substrate has a composition comprising, by weight: Ni 10%; Cr 29%; W 7; C 0.35%; B 0.015%; Si 0.1%; Mn 0.1%; Hf 1%; Ta 0.5%; Zr 0.5% Ti 0.2%; and Co plus incidental impurities balance The method according to any preceding claim wherein said substrate has a composition comprising of, by weight: Ni 10% Cr 29% W 7% C 0.25% Si 0.9% Mn 0.6% Co plus incidental impurities Balance A cobalt base, high temperature brazing alloy for use in the method of claim 1 comprising of, by weight: Nickel 10%; Chromium 29%; Tungsten 7%; Carbon 0.1%; Boron 2.5%; Silicon 2.5%; Manganese 0.6%; Hafnium 2%; Tantalum 2%; and Cobalt plus incidental impurities Balance A cobalt base, high temperature brazing alloy for use in the method of claim 1 comprising of, by weight: Nickel 10%; Chromium 29%; Tungsten 3.5%; Carbon 0.1%; Boron 1%; Silicon 7%; Manganese 0.6%; Hafnium 0.1%; Tantalum 4%; and Cobalt plus incidental impurities. Balance

Inventors: BELTRAN ADRIAN MAURICE, KREISCHER CHARLES HENRY JR, BELTRAN, ADRIAN MAURICE, KREISCHER CHARLES HENRY, JR.
Applicants: GEN ELECTRIC, GENERAL ELECTRIC COMPANY
Application year: 1991
Main classification: B23K35
IPC codes: B23K35, B22F1, C22C19