Material of adsorbing pyrogen

Abstract: An insoluble material for adsorbing a pyrogen comprising a polymer of an aziridine compound. According to the present invention, a large amount of the pyrogen can be easily removed from a solution containing pyrogen, and a large amount of the material for adsporbing the pyrogen can be prepared in easy steps. Therefore, the adsorbing material can greatly contribute to the preparation of medicines.

Description: The present invention relates to a material for adsorbing a pyrogen. A representative example of substances well known as pyrogen is endotoxin. Endotoxin is one of complex phospholipid polysaccharides which generally exist as a cell wall outermembrane component such as Gram-negative bacterium, is a typical pyrogen, and is so thermally stable as it cannot be decomposed even under steam sterilization under pressure. If endotoxin enters into blood of human or mammals without passing through a digestive tract, it causes strong exothermic reaction, vasconstriction, increase of sensitivity to adrenalin or acceleration and subsequently lowering of blood coagulation, thus resulting in, sometimes, death due to shock. Accordingly, there are never contaminated with endotoxin waters for injection, physiological saline, transfusions containing nutritions such as glucose or vitamins, dialysis solutions for blood dialysis, transfusions containing proteins such as albumin. For removing bacteria, it is general to conduct the filtration by using a porous membrane having a pore size of about 0.2 µm. However, endotoxin can be insufficiently removed by conducting only the filtration, since if bacteria exist, it is usual that endotoxin exists together with bacteria, and moreover endotoxin has a high molecular weight and a very broad molecular weight distribution. Although, for instance, Japanese Unexamined Patent Publication No. 62-19178, No. 63-243022 or No. 1-127039, or Minobe et al, Journal of Chromatograph, 262, 193-198 (1983) proposes an ion exchange resin and its converted one, or various polymers having a functional group, sufficient effects cannot be obtained. GB-A-844686 discloses a copolymer of polyethylene imine and vinyl pyridine, which is used in order to perform breaking of an oil-in-water emulsion and simultaneously extraction of the oil therefrom by passing the emulsion over the copolymer placed in a filter bed. EP-A-54778 discloses an ion exchanger wherein polyethylene imine is supported or fixed onto a cellulose or cellulose derivative such as a chemically treated, pulverized pine bark having a size of 0.5 to 3 mm. This ion exchanger may be mixed with activated alumina powder upon use. An object of the present invention is to provide a material for adsorbing the pyrogen, used as a means for effectively removing the pyrogen such as endotoxin, namely, to provide an adsorbing material capable of removing the pyrogen such as endotoxin so that it does not substantially exist in substances to be directly injected into blood without passing through a digestive tract, for instance, medicines such as biological products, water for injection. Further object of the present invention is to provide a preparation process for the above-mentioned adsorbing material of the pyrogen. A still further object of the present invention is to provide a method for removing the pyrogen such as endotoxin by using the above-mentioned adsorbing material. These and other objects of the present invention will become apparent from the description hereinafter. It has now been found that when a material for adsorbing a pyrogen is prepared from a polymer of an aziridine compound as a main component (in other words, as an adsorptive substance for the pyrogen), the above-mentioned objects can be attained. In accordance with the present invention, there is provided shaped article suitable as an adsorbent comprising a mixture of a polymer of an aziridine compound and a material compatible therewith, which is at least one member selected from the group consisting of regenerated cellulose, polyvinyl alcohol, polyacrylonitrile, nylon, polyolefin and polyester, said shaped article being obtained by shaping said mixture and the use of a shaped article comprising a polymer of an aziridine compound, which is insolubilized in water by crosslinking or a mixture of a polymer of an aziridine compound and a material compatible therewith which is at least one member selected from the group consisting of regenerated cellulose, polyvinyl alcohol polyacrylonitrile, nylon, polyolefin and polyester, as an adsorbent for adsorbing a pyrogen. The material for adsorbing the pyrogen of the present invention must be insoluble in a solution or suspension containing the pyrogen such as endotoxin (hereinafter referred to as "solution to be treated"). The solution to be treated is usually an aqueous solution or an aqueous suspension, so it is preferable that the adsorbing material is water-insoluble. The aziridine compound used in the present invention is a compound containing at least one group derived from aziridine (aziridine group) in one molecule. The aziridine group may be substituted by a substituent such as a substituted or unsubstituted alkyl group or a substituted or unsubstituted aryl group. In the present invention, the adsorbing material for the pyrogen is prepared from a polymer of the aziridine compound. The polymer of the aziridine compound includes a homopolymer of the aziridine compound, a copolymer prepared from the aziridine compound, and the like. More concretely, the aziridine compounds used in the present invention include compounds having the formula (I): wherein R¹, R², R³, R⁴ and R⁵ are the same or different and each is hydrogen atom, a substituted or unsubstituted aliphatic group, a substituted or unsubstituted aromatic group or a halogen atom. Specific examples of the aziridine compounds are, for instance, ethyleneimine, propyleneimine, butyleneimine, N-hydroxyethyl ethyleneimine, N-cyanoethyl ethyleneimine, N-methyl ethyleneimine, N-phenyl ethyleneimine, N-acetyl ethyleneimine, N-methacryloyl aziridine, β-aziridinylmethyl propionate, β-aziridinylethyl methacrylate, hexamethylene-bis-1,6-N,N'-diethyleneurea, diphenylmethane-bis-4,4'-N,N'-diethyleneurea, 2,2-bishydroxymethylbutanol-tris[3-(1-aziridinyl) propionate], and the like. The aziridine compounds may be used alone or as an admixture thereof. The polymer used in the adsorbing material contains units of the above-mentioned aziridine compound. In the present invention, not only copolymers prepared from the different kinds of the above-mentioned aziridine compounds but also copolymers prepared from the aziridine compound and another copolymerizable compound with the aziridine compound can be used. Further, there can be usefully used a block-copolymer prepared by block-copolymerizing the polymer of the aziridine compound with a vinyl polymer having a functional group reactive with the polymer of the aziridine compound at its polymer ends, since the block-copolymer can give to the adsorbent the moldability such as film-moldability or fiber-moldability, the strength, the insolubility, and the like as mentioned below. The copolymer of the aziridine compound with the other copolymerizable monomer or the above-mentioned block-copolymer has a content of the aziridine component of at least 5 % by weight, preferably at least about 20 % by weight, from the viewpoint of the adsorptivity. Also, the polymer of the aziridine compound can be used in the states of a salt with an organic or inorganic acid or an amide. The thus prepared polymer of the aziridine compound can be crosslinked by using a suitable crosslinking agent, for imparting the insolubility (water-insolubility) and further imparting the durability to the adsorbing material. Any compound can be used as the crosslinking agent so long as the compound contains two or more functional groups capable of forming covalent bond by the reaction with the functional groups of the polymer of aziridine compound, that is, imino group, the primary amino group or the secondary amino group in one molecule. Examples of the crosslinking agents are, for instance, epoxy resins such as novolak phenol epoxy resins and bisphenol epoxy resins; epihalohydrines such as epichlorohydrine and epibromohydrine; polyhalohydrines such as glycerol dichlorohydrine; polyhalogen compounds such as p-dichloroxylene and dibromodimethylene; polyaldehyde compounds such as glutaric dialdehyde and xylyl dialdehyde; polyisocyanate compounds such as tolylenediisocyanate and hexamethylenediisocyanate, and the like. These crosslinking agents may be used alone or as an admixture thereof. In the present invention, a shaped adsorbent is formed together with a forming material or a supporting material. The shaped adsorbent can take any of effective shapes for adsorbing the pyrogen such as endotoxin, for instance, a fiber, film, sheet, paper, non-woven fabric, hollow yarn (hollow article), particle, foam, block(mass), and the like. The shaped adsorbent of the present invention is prepared by the following methods, (1) The crosslinked polymer of the aziridine compound is formed into an insoluble adsorbent having the shape as mentioned above. (2) The polymer of the aziridine compound is admixed with the forming material which is compatible with the polymer and, using the crosslinking agent or not, the mixture is formed into an insoluble shaped adsorbent. As the forming material or the supporting material used in the above-mentioned embodiments (2), there can be used for instance, in the state of a film, sheet, paper, non-woven fabric, hollow article, particle, foam or block, regenerated celluloses, poval (polyvinyl alcohol), polyacrylonitrile, nylon, polyolefines, polyesters, and modified polymers thereof. The adsorbent of the present invention can be formed in any known manner in the art, for instance, usual molding methods for polymers such as extrusion, usual preparation methods for fibers, and the like. For instance, when a fibrous adsorbent is prepared by using a regenerated cellulose as the forming material in the embodiment (2), the polymer of the aziridine compound is added to a starting solution containing the usual regenerated cellulose and the fibrous adsorbent is prepared according to the usual spinning method for the regenerated cellulose. More concretely, a regenerated cellulose is prepared in a manner wherein a composition used for preparing a regenerated cellulose such as rayon or cellophane, for instance, a viscose is extruded into a coagulation bath wherein sulfuric acid and sodium sulfate exist as main components through pores or slits to coagulate, in other words, to convert into cellulose. The viscose is obtained, for instance, by impregnating a pulp with caustic soda (sodium hydroxide) to give an alkali cellulose, adding CS₂ to the obtained alkali cellulose to give a sodium cellulose xanthogenate, and adding diluted sodium hydroxide used for solving to the sodium cellulose xanthogenate. The viscose has usually 4 to 10 % by weight of cellulose and 4 to 7 % by weight of sodium hydroxide. On the other hand, the coagulation bath contains usually 80 to 150 g/ℓ of sulfuric acid and 180 to 370 g/ℓ of sodium sulfate, and further in case of preparing rayon, may contain 10 to 20 g/ℓ of zinc sulfate. In the present invention, the polymer of the aziridine compound is added to the viscose and the mixture is extruded into the coagulation bath to coagulate, whereby a regenerated cellulose composition having not less than 50 % by weight, based on the added polymer of the aziridine compound to the coagulation bath, of the polymer of the aziridine can be obtained. Although there are many cases that the polymer of the aziridine compound itself is water-soluble, in the regenerated cellulose composition containing the polymer of the aziridine compound, it is bonded to the cellulose molecule by strong interaction such as hydrogen bond. Therefore, it is not eluted from the composition as a water-soluble substance at all, and it behaves as if it is graft-polymerized on the cellulose. Accordingly, the regenerated cellulose composition having the polymer of the aziridine compound which is prepared by a usual method for producing regenerated cellulose is a polymer composition having substantially no water-soluble substance, and the thus obtained regenerated cellulose composition can be used as a material for efficiently removing endotoxin, even if the polymer of the aziridine compound is not crosslinked (in other words, is not made insoluble). When using polyacrylonitrile, an aqueous solution of polyacrylonitrile containing zinc chloride or an acetone solution of polyacrylonitrile is prepared, and when using nylon, polyolefine or polyester, they are molten in a calender or an extruder. Then, the polymer of the aziridine compound is added to the aqueous or acetone solution or the molten one, and the mixture is formed into the adsorbent having the desired shape in a usual manner. The adsorbing material can take any desired shape such a fiber, film, hollow yarn, block, bead, powder or sponge, and further it can be formed into products having various states such as a spun yarn, cloth, non-woven fabric, paper, membrane, honeycomb and composite material, e. g., a laminate. In the present invention, only to instantly contact the solution containing the pyrogen such as endotoxin (the solution to be treated) with the adsorbing material at room temperature, for instance from 0° to 40°C, suffices the removal for the pyrogen from the solution to be treated. As a removal method, there are exemplified a method wherein a column is charged with the fibrous or granular(particles) adsorbent and the solution to be treated is passed through the column; a method wherein the solution to be treated is filtered through a filter paper made of the adsorbent to give a filtrate; a method wherein the adsorbent in the state of beads is added to the solution to be treated and the mixture is stirred; a method wherein the solution to be treated is dialyzed by using the dialysis membrane made of the adsorbent in the state of the hollow fiber; and the like. Further, various types of apparatuses for effectively and easily removing the pyrogen can be considered by using the adsorbing material of the present invention. According to the present invention, apparatuses for effectively removing pyrogen can be easily and unexpensively provided by even considering that the solution to be treated is effectively contacted with the adsorbent. According to the present invention, a large amount of pyrogen such as endotoxin, can be easily removed from the solution containing pyrogen, and the material for removing a large amount of the pyrogen can be prepared in very easy steps, so the adsorbent of the present invention can contribute to the preparation of medicines. The present invention is more specifically described and explained by means of the following Examples in which all % and parts are by weight unless otherwise noted. In Examples 1-12 and Comparative Examples the pyrogen was detected by using "Toxinometer" commercially available from Wako Purechemical Industries, Ltd. and proteins here determined by using a spectrophotometer according to Beer's law. Example 1 Polyethyleneimine having a molecular weight of 70,000 was crosslinked with 20 % by mole per monomer unit of polyethyleneimine of glyoxal or hexamethylenediisocyanate in a suitable medium to give a mass of crosslinked polyethyleneimine, and the obtained polyethyleneimine was pulverized to give particles having a particle size of 100 to 500 µm (adsorbent). A test tube was charged with 0.1 g of the adsorbent, 2 mℓ of an aqueous solution containing 360 ng/mℓ of endotoxin was poured into the tube and the tube was shaken at 37°C for 30 minutes to contact endotoxin with the adsorbent. In case of using the adsorbent of the particles of polyethyleneimine crosslinked with glyoxal, a concentration of endotoxin in the treated solution was 0.41 ng/mℓ. In case of using the adsorbent of the particles of polyethyleneimine crosslinked with hexamethylenediisocyanate, a concentration of endotoxin in the treated solution was 0.34 ng/mℓ. In the both cases, the endotoxin concentrations in the treated solutions were remarkably decreased, that is, the extremely excellent adsorptivity were shown in the both cases. Example 2 An aqueous solution of polyethyleneimine (hereinafter referred to as "PEI") having a PEI content of 15 % was added to a viscose containing 9.5 % of cellulose and 5.6 % of sodium hydroxide so that the amount of PEI was 20 % of cellulose and the mixture was stirred. The thus obtained viscose was extruded into a coagulation bath containing 112 g/ℓ of sulfuric acid, 350 g/ℓ of sodium sulfate, 15 g/ℓ of zinc sulfate and water through a nozzle having 10,000 holes each having a diameter of 0.07 mm to coagulate. The obtained regenerated fiber was stretched 1.5 times at 95°C, and was cut to a length of 51mm. The cut fiber was dipped in warm water having a temperature of 90°C, dehydrated, and washed with warm water having a temperature of 90°C, then an aqueous solution containing 4 g/ℓ of sodium hydroxide and having a temperature of 80°C, and finally water. Subsequently, the fiber was bleached with a 15 % aqueous solution of hydrogen peroxide having a temperature of 65°C and was washed with water to complete the scouring. The fiber was dried at 105°C to give a 2 d of regenerated cellulose fiber containing PEI as a sample [adsorbent 2-(1)]. A yield of PEI was 86 %. The adsorbent 2-(1) was dipped in 1N sulfuric acid, 1N sodium hydroxide and pure water having a temperature of 90°C for 10 minutes, respectively. In all of the three cases, the elution was not observed at all. The obtained fiber [adsorbent 2-(1)] was cut to a length of about 10 mm and a test tube was charged with 0.1 g of the cut fiber. Into the test tube was poured 2 mℓ of an aqueous solution containing 360 ng/mℓ of endotoxin and the tube was shaken at 37°C for 30 minutes to contact endotoxin with the adsorbent 2-(1). The treated solution had 0.84 ng/mℓ of endotoxin, and a removing ratio (adsorption ratio) of 99.8 %, in other words, endotoxin could be removed in high efficiency. The same procedure as above was repeated except that polypropyleneimine (hereinafter referred to as "PPI") was used instead of PEI to give a regenerated cellulose fiber containing PPI [adsorbent 2-(2)]. A yield of PPI was 88.0 %. The adsorption ratio of the adsorbent 2-(2) was measured in the same manner as the case that the adsorbent 2-(1) was measured. The result is shown in Table 1. On the other hand, one of adsorbents obtained in Example 1, namely, the crosslinked PEI with glyoxal (glyoxal was used in an amount of 20 % by mole per monomer unit of PEI) which was insoluble in water (hereinafter referred to as "PEC") was pulverized by using a wet grinding machine commercially available under a trademark "Sand grinder" from Igarashi Kikai Seizo Kabushiki Kaisha to give particles with an average particle size of not more than 1 µm, and an aqueous suspension having 20 % of the obtained particles of PEC was prepared. The procedure for preparing the adsorbent 2-(1) was repeated except that the aqueous suspension containing the particles of PEC was added so that the amount of PEC particles was 20 % of cellulose instead of PEI to give a regenerated cellulose containing PEC [adsorbent 2-(3)]. A yield of PEC was 98.7 %. An adsorption ratio of endotoxin was measured in the same manner as that the adsorbent 2-(1) was measured. The results are shown in Table 1. As shown in Table 1, the adsorbent 2-(3) showed a remarkably high adsorption ratio of endotoxin. Example 3 The same aqueous solution of PEI as used in Example 2, the 15 % aqueous solution of PEI was added to an aqueous solution containing 20 % of poval with a degree of polymerization of 1500 to give an aqueous solution of poval containing 20 % based on poval of PEI. The obtained aqueous solution was spun, using a coagulation bath of a saturated solution of Glauber's salt (sodium sulfate · 10H₂O) having a temperature of 45°C through a nozzle having 20,000 holes each having a diameter of 0.08 mm to give a 2 d of vinylon containing PEI [adsorbent 3-(1)]. A yield of PEI was 87.3 %. Poval was spun in the same manner as above except that, instead of PEI, the same PPI as used in Example 2, that is, in the preparation of the adsorbent 2-(2) and the same PEC as used in Example 2, that is, in the preparation of the adsorbent 2-(3) were used respectively to give a vinylon containing PPI [adsorbent 3-(2)] and a vinylon containing PEC [adsorbent 3-(3)]. A yield of PPI was 88.3 % and a yield of PEC was 98.8 %. As to each of the adsorbents 3-(1), 3-(2) and 3-(3), the adsorption ratio of endotoxin was measured in the same manner as in Example 2. The results are shown in Table 1. Example 4 PEI was added to an acetone solution of polyacrylonitrile (PAN) in an amount of 20 % of PAN, and the obtained acetone solution of PAN containing PEI was dry spun through a nozzle having 2,000 holes each having a diameter of 0.1 mm to give a 2 d of PAN fiber containing PEI [adsorbent 4-(1)]. PAN was dry spun in the same manner as above except that the PPI and the PEC were used instead of PEI respectively to give a PAN fiber containing PPI [adsorbent 4-(2)] and a PAN fiber containing PEC [adsorbent 4-(3)]. As to each of the obtained adsorbents 4-(1), 4-(2) and 4-(3), an adsorption ratio of endotoxin was measured in the same manner as in Example 2. The results are shown in Table 1. Example 5 Nylon-6 pellets were molten in an extruder, to which PEI, PPI and PEC were added in an amount of 20 % of Nylon-6, respectively, and each mixture was spun to give a 2 d of nylon fiber containing PEI [adsorbent 5-(1)], a 2 d of nylon fiber containing PPI [adsorbent 5-(2)] or a 2 d of nylon fiber containing PEC [adsorbent 5-(3)]. As to each of the adsorbents 5-(1), 5-(2) and 5-(3), an adsorption ratio of endotoxin was measured in the same manner as in Example 2. The results are shown in Table 1. Example 6 The same procedure of Example 4 was repeated except that polypropylene was used instead of Nylon-6 pellets to give a 2 d of polypropylene fiber containing PEI [adsorbent 6-(1)], a 2 d of polypropylene fiber containing PPI [adsorbent 6-(2)] and a 2 d of polypropylene fiber containing PEC [adsorbent 6-(3)], respectively. As to each obtained adsorbent, 6-(1), 6-(2) and 6-(3), an adsorption ratio of endotoxin was measured in the same manner as in Example 2. The results are shown in Table 1. Example 7 The same procedure of Example 6 was repeated except that a polyester was used instead of polypropylene to give a 2 d polyester fiber containing PPI [adsorbent 7-(2)] and a 2 d of polyester fiber containing PEC [adsorbent 7-(3)], respectively. As to each of the adsorbents 7-(1), 7-(2) and 7-(3), an adsorption ratio of endotoxin was measured in the same manner as in Example 2. The results are shown in Table 1. Ex. No. Forming material Polymer of aziridine Adsorbent No. Adsorption ratio (%) Ex. 2 Regenerated cellulose PEI 2-(1) 99.6 " PPI 2-(2) 99.4 " PEC 2-(3) 99.8 Ex. 3 Poval PEI 3-(1) 95.6 " PPI 3-(2) 94.8 " PEC 3-(3) 96.1 Ex. 4 Polyacrylonitrile PEI 4-(1) 90.7 " PPI 4-(2) 90.0 " PPI 4-(3) 91.3 Ex. 5 Nylon-6 PEI 5-(1) 86.3 " PPI 5-(2) 84.9 " PEC 5-(3) 87.1 Ex. 6 Polypropylene PEI 6-(1) 81.1 " PPI 6-(2) 80.4 " PEC 6-(3) 82.3 Ex. 7 Polyester PEI 7-(1) 83.1 " PPI 7-(2) 81.1 " PEC 7-(3) 84.2 Example 8 The adsorbents 2-(1) and 3-(1) were crosslinked with glyoxal to give an adsorbent 2-(1)-G and an adsorbent 3-(1)-G, respectively. Also, the adsorbents 2-(1) and 3-(1) were crosslinked with hexamethylenediisocyanate to give and an adsorbent 2-(1)-H and an adsorbent 3-(1)-H. Each of the adsorbents 2-(1)-G, 2-(1)-G, 3-(1)-G, 3-(1)-H, 2-(1) and 3-(1) was dipped in 1N sulfuric acid and then 1N-sodium hydroxide, and it was washed with pour water to give the adsorbent free from endotoxin (pretreatment). A test tube was charged with 0.1 g of the adsorbent, 2 mℓ of an aqueous solution containing 250 ng/mℓ of endotoxin was poured into the test tube, and the tube was shaken at 37°C for 30 minutes to contact endotoxin with the adsorbent (adsorption). An endotoxin content in a supernatant fluid in the test tube was measured by using Toxinometer and an adsorption ratio of endotoxin (%) was measured. The procedure of the pretreatment and the adsorption was repeated 10 times, and an adsorption ratio in each time was measured. The results are shown in Table 2. As shown in Table 2, the adsorbents wherein the polymer was crosslinked could be kept higher in adsorption ratio than the adsorbent wherein the polymer was not non-crosslinked in case of repeating the procedure of the pretreatment and the adsorption. In other words, the adsorbent of the crosslinked polymer is more excellent in repeated adsorptivity than the adsorbent of the non-crosslinked polymer. Adsorbent No. Adsorption ratio (%) The first time The second time The 5th time The 10th time 2-(1) 99.6 98.6 98.0 80.0 2-(1)-G 98.9 99.2 98.5 98.6 2-(1)-H 99.7 99.5 99.0 99.0 3-(1) 95.6 95.4 90.6 73.5 3-(1)-G 94.5 94.0 94.5 93.4 3-(1)-H 95.0 96.0 96.2 96.4 Example 9 An aqueous solution containing 15 % of PEI was added to a viscose containing 9.5 % of cellulose and 5.6 % of sodium hydroxide in an amount of PEI of 20 % based on cellulose, and the mixture was sprayed by pressured air and the coagulation was conducted in a coagulation bath of an aqueous solution containing 112 g/ℓ of sulfuric acid, 350 g/ℓ of sodium sulfate and 15 g/ℓ of zinc sulfate to give particles with a particle size of 10 to 100 µm. The particles were washed with water and subjected to desulfuration with sodium hydroxide. Then, the particles were crosslinked with hexamethylenediisocyanate (the absorbent A). The same viscose as above was added dropwise to the same coagulation bath as above through a nozzle to give particles having a particle size of 100 to 500 µm. The particles were purified in the same manner as above, and pulverized to give powder having a particle size of about 10 µm. The powder was crosslinked with hexamethylenediisocyanate (adsorbent B). A test tube was charged with 0.1 g of each of the adsorbent 2-(1) (fibrous), adsorbent A (particles) and adsorbent B (powdery) which contained the same amount of PEI but were different in shape from each another, to which 2 mℓ of a solution containing 360 ng/mℓ of endotoxin was added, and the mixture was shaken at 37°C for 30 minutes to contact endotoxin with the adsorbent. Adsorption ratios were measured and the results are shown in Table 3. As shown in Table 3, with respect to all of the three kinds of the adsorbents, the excellent adsorptivity was observed. Adsorbent Adsorption ratio (%) 2-(1) (fibrious) 99.6 A (particles) 99.4 B (powder) 99.7 Example 10 and Comparative Example 1 A regenerated cellulose fiber containing about 17 % based on cellulose of PEI was cut to a length of about 10 mm [adsorbent 10-(1)] and a test tube was charged therewith. The fiber in the test tube was washed with 10 mM phosphate buffer containing 0.1 M NaCℓ (pH: 7.5), and 1 to 2 mℓ of phosphate buffer wherein 5 mg of bovine serum γ-globulin (pH : 7.2) was dissolved was added to the test tube to contact. An amount of endotoxin remaining in the supernatant fluid was measured. An adsorption ratio of endotoxin is shown in Table 4 together with a recovery of γ-globulin. The recovery of γ-globulin was measured, using a spectrophotometer according to Beer's law. Using a regenerated cellulose fiber containing 20 % based on cellulose of PEC, [the adsorbent 10-(2)], the same procedure as above was repeated. As to an adsorbent C which was commercially available under the trademark "C-9" from Kurita Water Industries Ltd., the same procedure as above was repeated. As to the adsorbents 10-(2) and C, an adsorption ratio and a recovery of γ-globulin were shown in Table 4. Adsorbent Adsorption ratio of endotoxin Recovery of γ-globulin 10-(1) 98.5 89.8 10-(2) 99.3 90.0 C 80.0 75.2 Example 11 and Comparative Examples 2 and 3 Each of the adsorbents 2-(1) and 2-(3), and an adsorbent D (Com. Ex. 2) which was commercially available under the trademark "C-7" from Kurita Water Industries Ltd., and the adsorbent E (Com. Ex. 3) which was commercially available under the trademark "Pyrosep" from Daicel Chemical Industries, Ltd. was washed with 10 mM phosphate buffer containing 1.0 M NaCℓ (pH: 7.5) and no endotoxin, then 1 to 2 mℓ of a phosphate buffer containing 1.0 M NaCℓ (pH 7.5) to which a bacterial toxoid contaminated with endotoxin was added was contacted with the washed adsorbent in a test tube. Endotoxin remaining in the supernatant fluid was measured. Adsorption ratios of the pyrogen are shown in Table 5. Adsorbent No. Amount of Adsorbent Adsorption ratio (%) Kind of Toxoid Toxoid derived from Clostridium tetani Toxoid derived from Clostridium tetani Toxoid derived from Corinebacterium diphtheria Initial pyrogen content 3933 ng/mℓ 1080 ng/mℓ 397 ng/mℓ Ex. 11 2-(1) 0.1 g 85 95 99 2-(3) 0.1 g 80 90 97 Com. Ex. 2 D 0.200 g 0 0 72 Com. Ex. 3 E 0.124 g 20 4 54 Example 12 A regenerated cellulose fiber and a filter paper were dipped respectively in an aqueous solution containing 10 % of polyethyleneimine having a molecular weight of 70,000 at 30°C for 24 hours and then water was removed under reduced pressure at 40°C. The obtained products had 10 %, based on the supporting material (regenerated cellulose fiber or filter paper), of polyethyleneimine. The obtained regenerated cellulose fiber to which polyethyleneimine was attached and the filter paper to which polyethyleneimine was attached was crosslinked in an aqueous solution containing 25 % of glutaraldehyde to give adsorbents, respectively. To 2 mℓ of a solution containing 360 ng/ℓ of endotoxin was added 0.1 g of each adsorbent, and an adsorption ratio was measured. The adsorbent wherein polyethyleneimine was attached to the regenerated cellulose fiber had an adsorption ratio of 85 %, and the adsorbent wherein polyethyleneimine was attached to the filter paper had an adsorption ratio of 76 %. In addition to the ingredients used in the Examples, other ingredients can be used in the Examples as set forth in the specification to obtain substantially the same results.

Claims: The use of a shaped article comprising a polymer of an aziridine compound, which is insolubilized in water by crosslinking, or a mixture of a polymer of an aziridine compound and a material compatible therewith which is at least one member selected from the group consisting of regenerated cellulose, polyvinyl alcohol polyacrylonitrile, nylon, polyolefin and polyester, as an adsorbent for adsorbing a pyrogen. The use of Claim 1, wherein said polymer is a homopolymer or copolymer of aziridine compounds, a copolymer of at least 5 % by weight of an aziridine compound and other monomers copolymerizable therewith, or a mixture thereof. The use of Claim 1 or 2, wherein said shaped article is in the form of a fiber, film, sheet, paper, non-woven fabric, hollow product, particle, foam or block. The use of claim 1 or 2, wherein said shaped article comprising a polymer of an aziridine compound, which is insolubilized in water by crosslinking, is a powder formed by pulverizing the crosslinked polymer having an ability to adsorb a pyrogen. The use of claim 1, 2 or 3 wherein said polymer of aziridine compound in the shaped article comprising a mixture of a polymer of an aziridine compound and a material compatible therewith is crosslinked. The use of any of claims 1, 2, 3 and 5 wherein said shaped article comprising a mixture of a polymer of an aziridine compound and a material compatible therewith is prepared by mixing said polymer with said material compatible therewith, and forming the mixture into a shaped article. The use of any of claims 1, 2, 3 and 5, wherein said shaped article comprising a mixture of a polymer of an aziridine compound and a material compatible therewith is a product prepared by adding a cosslinked or non-crosslinked polymer of an aziridine compound to a viscose and extruding the resulting mixture into a coagulation bath to regenerate cellulose. The use of any of claims 1, 2, 3 and 5, wherein said shaped article comprising a mixture of a polymer of an aziridine compound and a material compatible therewith is a product prepared by adding said polymer to a viscose, extruding the resulting mixture to a coagulation bath to regenerate cellulose, and subjecting the regenerated cellulose to a crosslinking treatment for said polymer. The use of any of claims 1 to 8, wherein said aziridine compound is ethyleneimine or propyleneimine. A shaped article suitable as an adsorbent comprising a mixture of a polymer of an aziridine compound and a material compatible therewith, which is at least one member selected from the group consisting of regenerated cellulose, polyvinyl alcohol, polyacrylonitrile, nylon, polyolefin and polyester, said shaped article being obtained by shaping said mixture. A shaped article of claim 10 which is prepared by a process which comprises adding said polymer of an aziridine compound to a viscose and extruding the resulting mixture into a coagulation bath to regenerate cellulose. A shaped article of claim 11, wherein the regenerated cellulose is then subjected to a crosslinking treatment to crosslink said polymer included therein.

Inventors: HIRAOKA KEIJUN, HIRAYAMA CHUICHI, MORIMOTO SUNAO, HIRAOKA, KEIJUN, HIRAYAMA, CHUICHI, MORIMOTO, SUNAO
Applicants: HIRAYAMA CHUICHI, KOHJIN CO, HIRAYAMA, CHUICHI, KOHJIN CO., LTD.
Application year: 1991
Main classification: B01J20
IPC codes: B01J20, A61K9