Fractionation process of reaction mixture containing methylene bridged polyphenylene polyisocyanate

Abstract: A fractionation process of a methylene bridged polyphenylene polyisocyanate mixture obtained by phosgenating condensation product of aniline and formaldehyde is disclosed. In order to apply the above mixture to a variety of uses, the process separates the mixture into fractions by giving primary attention to the content of 4,4'- and 2,4'-isomer of diphenylmethane diisocyanate and at the same time reduces the content of impurities having acidity and hydrolyzable chlorine.

Description: Background of the Invention 1. Field of the Invention The present invention relates to a preparation process of methylene bridged polyphenylene polyisocyante, and particularly relates to a fractionation process of a reaction mixture containing the polyisocyanate. Methylene bridged polyphenylene polyisocyanate is a very reactive compound and widely utilized for polyurethane products such as foams, elastomers, adhesives and paints. The present invention can conduct various modes of fractionation on methylene bridged polyphenylene polyisocyanate having the above many uses depending upon the kind and purity of the polyisocyanate and the variety and amount of impurities. The above reaction product can hence be fractionated so as to obtain reaction materials which satisfy properties required for specific uses. 2. Disclosure of the Related Art Methylene bridged polyphenylene polyisocyanate is prepared by phosgenating a polyamine mixture formed by condensation of aniline and formaldehyde. The product contains various kinds of diphenylmethane diisocyanate (hereinafter referred to as MDI) and can provide by distillation an isomer mixture of 2,4'-diphenylmethane diisocyanate (hereinafter referred to as 2,4'-MDI) and 4,4'-diphenylmethane diisocyanate (hereinafter referred to as 4,4'-MDI). The residue obtained by the distillation has also various use and thus preparations are generally made so as to suit for the uses by mixing these fractionated products in an adequate proportion. However, phosgenation in preparing the MDI mixture inevitably generates impurities having acidity and hydrolyzable chlorine. These impurities have been known to lower the reactivity of isocyanate group in the preparation of polyurethane products. Conventionally known processes for reducing the acidity and hydrolyzable chlorine (hereinafter referred to as HC) are based on the heat-treatment of the MDI mixture at high temperature or treatment with organic reagent. For example, heat-treatment process is disclosed in GB-1398975, GB-1384065 and an alkylene oxide compound is added as organic reagent for US-3925437. These processes, however, cannot be satisfied because the organic reagent is required in a large amount, remains in the product and leads to formation of tarry materials in the high temperature treatment. On the other hand, separation processes by distillation, extraction and crystallization, respectively, have been conventionally known for the separation of the MDI isomer mixture. For example, improved distillation processes are disclosed in EP-79516, DE-2631168, DE-2844591 and DD-257827. The separation process by distillation essentially causes polymerization of isocyanate due to heating and decreases yield of 4,4'-MDI. The separation process by extraction has a disadvantage of requiring solvent removal. The separation process by crystallization divides the isomer mixture into a mother liquor and a crystalline product and affords 4,4'-MDI as a high purity crystal. The process, however, cannot sufficiently reduce the acidity and HC of resulting 4,4'-MDI. The aspect of the basic invention we present is a process for simultaneous manufacture for a highly reactive MDI mixture having a low level of acidity and HC and high purity 4,4'-diphenylmethane diisocyanate from a reaction mixture obtained by phosgenating a polyamine mixture resulting from condensation of aniline and formaldehyde, said reaction mixture containing 4,4'-diphenylmethane diisocyanate as a primary component, 2,4'-diphenylmethane diisocyanate as a secondary component, impurities having acidity and hydrolyzable chlorine, comprising the steps of: (A) distilling the reaction mixture into a distillate first fraction and a residue second fraction at a temperature of 180° to 250°C and a pressure of 0.2 to 10 mmHg. (B) cooling the first fraction to precipitate therefrom a solid in an amount of not more than 85% by weight of the first fraction. (C) removing the precipitated solid to obtain a liquid third fraction and a solid third fraction and either (D1) heating the liquid third fraction in an inert gas at 80° to 120°C, and removing a resultant gaseous portion at ambient temperature and pressure to obtain a liquid fourth fraction or (D2) warming the solid third fraction to a temperature not higher than 40°C, and removing the molten portion to obtain high purity 4,4'-diphenylmethane diisocyanate or (D3) conducting both (D1) and (D2). Prior to completing the present invention, the inventors have found that the impurities having acidity and HC in the reaction mixture obtained by phosgenating the polyamine mixture defined in claim 1 can be roughly divided into two groups which have a lower boiling point and a higher boiling point than MDI, that the impurities having large influence on the reactivity in the preparation of polyurethane products have the lower boiling point, that any impurities having acidity and HC are remained in the mother liquor in the crystallization step of MDI, and that these impurities can be decomposed by relatively mild heating and release hydrogen chloride gas. The inventors have accomplished on the basis of these discoveries to simultaneously obtain a highly reactive MDI mixture having a low level of acidity and HC and high purity 4,4'-diphenylmethane diisocyanate. They have also enabled to most efficiently leave acidity and HC in the mother liquor by suitably selecting the crystallization conditions of MDI. The purity of 4,4'-diphenylmethane diisocyanate was obtained 98.5% or more. Detailed Description of the Preferred Embodiment The term reaction mixture in the invention, claim 1 in particular, refers to a mixture of crude methylene bridged polyphenylene polyisocyanate obtained by phosgenating a polyamine mixture resulting from condensation of aniline and formaldehyde in the presence of an acid catalyst. The mixture contains 2,4'-MDI and 4,4'-MDI in a proportion of 1:99 to 15:85. The sum of 2,4'- and 4,4'-MDI is 40 to 80% of the mixture. The mixture additionally contains various polynuclear isocyanate compounds and impurities having 0.01 to 0.05% of acidity and 0.1 to 0.5% of HC which are particula problems in the invention. The composition of MDI mixture depends upon the composition of polyamine mixture and the composition of polyamine mixture is affected by the ratio aniline/hydrochloric acid/formaldehyde in the condensation reaction. Phosgenation of the polyamine mixture may be carried out continuously or batchwise under atmospheric or increased pressure. The distillation in claim 1, (A), i.e., the separation of the first and the second fraction by distillation of the crude polyisocyanate can be carried out by batch operation with simple distillation equipment or by continuous operation with thin film distillation equipment. In order to prevent polymerization of isocyanate by heat, the distillation is carried out by using the thin film distillation equipment under reduced pressure of usually 27 to 1333 Pa (0.2 to 10 mmHg), preferably 67 to 667 Pa 0.5 to 5 mmHg, more preferably 133 to 400 Pa 1.0 to 3.0 mmHg and at a temperature of usually 180 to 250°C, preferably 180 to 230°C, more preferably 180 to 200°C. The distillate is cooled into liquid to form the first fraction. In order to avoid formation of dimer, it is preferred to cool the distillate quickly to 100°C. The proportion the first fraction to the second fraction remained can be optionally changed. The isomer ratio of 2,4'-MDI to 4,4'-MDI in the first fraction is affected by the composition of the polyamine mixture. MDI still remains in the second fraction in a proportion of 20 to 50% and the major part is a mixture of polynuclear isocyanates. The second fraction also contains 0.02 to 0.06% acidity and 0.15 to 0.50% HC. The first fraction is cooled in the step of claim 1, (B), i.e., the crystallization step, to separate into uncrystallized portion (the third fraction) and crystallized product. In the step, the temperature is controlled in such a way that the amount of the crystallized product is 85% by weight or less of the first fraction. The third fraction contaisn 2,4'-MDI and 4,4'-MDI in a ratio of 5:95 to 30:70 and also contains 0.03 to 0.06% of acidity and 0.05 to 0.1% of HC. The third fraction is heat-treated in the step of claim 1, (C). The treatment is readily carried out by using a reactor equipped with a heating jacket and an inert gas inlet tube and heat-treating the fraction at 80 to 120°C while feeding the inert gas. The inert gas containing acid gas evolved is usually removed from the system and may be recycled to the system after suitable neutralization and drying. The inert gases which can be used for the heat-treatment include nitrogen, helium, argon, carbon monoxide and carbon dioxide. Nitrogen is preferred in view of economy. The amount of the inert gas differs depending upon the treating time. For the treatment of 2 hours, preferred amount of the inert gas is 0.01 to 1.0 part by weight per hour per part by weight of the formed product. The treating temperature lower than 80°C does not appreciably decompose acidity and HC. When the temperature is higher than 120°C, the decomposition of acidity and HC progresses whereas formation of the dimer unfavorably increases. The heating procedure can lower acidity and HC to about one tenth of the amount before treatment. The third fraction thus heat-treated separates a gaseous fraction at ordinary temperature and pressure to recover a liquid portion as the fourth fraction which contains decreased amount of acidity and HC. The thus-obtained fourth fraction can be blended with the second fraction in an optional proportion to make a preparation having MDI content or viscosity which conforms to respective use. The preparation obtained by mixing the second and the fourth fractions has acidity of 0.005 to 0.02% and HC of 0.05 to 0.15%, though variable by the mixing ratio. Hence, thus-obtained preparation exhibits higher reactivity as compared with the preparation obtained by using the third fraction without heat-treatment. In the next step, the solid obtained in the step of claim 1, (B) can be divided by gradual warming into an initially molten portion (the fifth fraction) and principally molten portion (the sixth fraction). For example, the solid is gradually warmed to 40°C to obtain the fifth fraction as a liquid product. The residual solid is further warmed to about 55°C to obtain the sixth fraction in the form of a molten product. It is preferred for maintaining high purity of the fifth fraction to increase the temperature until 40°C as slowly as possible. This is because the solid itself is a crystal of mixed materials. The term "as slowly as possible" is a matter of degree. For example, the solid obtained in the step of claim 1, (B) is gradually warmed over about 5 hours from the temperature of the solid itself to 40°C. The fifth fraction obtained by an ideal treatment is a mixture composed of 2.0 to 7.0% of 2,4'-MDI, 93.0 to 98.0% of 4,4'-MDI, 0.005 to 0.020% of acidity and 0.01 to 0.05% of HC. The fraction is very valuable for the raw materials of liquid MDI and modified polyurethanes. The sixth fraction is high purity 4,4'-MDI which contains only 1.5% or less of 2,4'-MDI, 0.001 to 0.003% of acidity and 0.002 to 0.005% of HC. It is better to use the fraction as intact, rather than further separating the two ingredients. The sixth fraction can be used without any problem as high purity 4,4'-MDI for the raw material of various polyurethane products. The isomer ratio of MDI in each fraction mentioned above can be varied by controlling cooling temperature, warming temperature and speed of cooling or warming. In order to obtain high purity 4,4'-MDI having low impurity content or to obtain the third fraction by efficiently concentrating impurities, preferred yield ratio for thus-divided fractions is, for example, 100 in the first fraction, 10 to 40 in the third fraction, 10 to 40 in the fifth fraction, and 40 to 60 in the sixth fraciton. Example 1 A mixture of 2.46 kg (25.1 moles) of aniline (95 wt%, purity), 0.81 kg of formalin (10 moles of formaldehyde) and 1.64 kg (11.2 moles) of 25% hydrochloric acid was heated at an elevating temperature range of 30°C to 120°C for 3 hours. Into a 1.78 kg of the reaction mixture, 8.72 kg (88 moles) of phosgene was introduced at an elevating temperature range of 10°C to 140°C over 3 hours to obtain 11.3 kg of crude methylene-bridged polyphenylene polyisocyanate mixture. The mixture contained 3% of 2,4'-MDI, 60% of 4,4'-MDI, 0.015% of acidity, and 0.15% of HC. The mixture was distilled by using thin-film distillation equipment at 210 to 220°C under pressure of 2 mmHg to obtain 40% of the first fraction and 60% of the second fraction. The first fraction was maintained in the liquid state at 36°C, transferred to a crystallizer and cooled to 24°C over 8 hours. Thus the first fraction was separated into 80% of crystallized portion and 20% of uncrystallized portion (the third fraction). The third fraction was treated by heating at 100°C for 2 hours while introducing nitrogen in an amount of 0.5 part by weight per hour per part by weight of the product, thereby the fourth fraction which is liquid at ordinary temperature and pressure was obtained. The fourth fraction and the second fraction was mixed in a proportion of 20:80 (referred to as 4-2 fraction). The crystallized portion was warmed to 40°C over about 5 hours and an initially molten portion (the fifth fraction) was separated in an amount of 20% for the first fraction. The remained portion was further warmed to 55°C to take out the sixth fraction in the form of a molten material in an amount of 60% for the first fraction. Analytical values of each fraction are illustrated in Table 1. Fraction MDI content (%) Acidity (%) HC (%) Curing time (min) 2,4'- 4,4'- 1 5.3 94.7 0.013 0.018 24 hrs< 2 1.5 36.9 0.020 0.205 55.0 3 17.2 82.8 0.041 0.061 24 hrs< 5 5.4 94.6 0.015 0.017 15.0 6 1.3 98.7 0.003 0.004 0.5 4 17.2 82.8 0.008 0.010 2.0 4-2 4.6 46.1 0.018 0.166 28.0 Example 2 The first fraction in Example 1 was cooled to 30°C over 8 hours, and 70% of crystallized portion and 30% of uncrystallized portion (the third fraction) were obtained. Successively the crystallized portion was warmed to 40°C over about 5 hours and 15% of molten liquid (the fifth fraction) was separated. The residual solid portion was further warmed to 55°C to obtain 55% of molten liquid as the sixth fraction. The third fraction was treated by heating at 95°C for 2 hours while introducing nitrogen in an amount of 0.5 part by weight per hour per part by weight of the product, thereby the fourth fraction which was liquid at ordinary temperature and pressure was obtained. The fourth fraction was mixed with the second fraction of Example 1 in a proportion of 20:80 to obtain the 4-2 fraction. Analytical values of each fraction are illustrated in Table 2. Fraction MDI content (%) Acidity (%) HC (%) Curing time (min) 2,4'- 4,4'- 3 13.3 86.7 0.033 0.050 24 hrs< 5 4.8 95.2 0.012 0.013 10.5 6 1.1 98.9 0.002 0.002 0.5 4 13.3 86.7 0.005 0.007 1.5 4-2 3.9 46.9 0.017 0.158 26.0 Example 3 The first fraction in Example 1 was cooled to 20°C over 8 hours, and 85% of crystallized portion and 15% of uncrystallized portion (the third fraction) were obtained. Successively the crystallized portion was warmed to 40°C over about 5 hours and 27% of molten liquid (the fifth fraction) was separated. The residual solid portion was further warmed to 55°C to obtain 58% of molten liquid as the sixth fraction. The third fraction was treated by heating at 105°C for 2 hours while introducing nitrogen in an amount of 0.5 part by weight per hour per part by weight of the product, thereby the fourth fraction which was liquid at ordinary temperature and pressure was obtained. The fourth fraction was mixed with the second fraction of Example 1 in a proportion of 20:80 to obtain the 4-2 fraction. Analytical values of each fraction are illustrated in Table 3. Fraction MDI content (%) Acidity (%) HC (%) Curing time (min) 2,4'- 4,4'- 3 21.9 78.1 0.048 0.078 24 hrs< 5 5.1 94.9 0.017 0.019 28.5 6 1.1 98.9 0.002 0.002 0.5 4 21.9 78.1 0.010 0.012 3.5 4-2 5.6 45.1 0.018 0.167 35.0 Comparative Example 1 The first fraction in Exmaple 1 was cooled to 24°C over 8 hours, and 80% of crystallized portion and 20% of uncrystallized portion (the third fraction) were obtained. Successively the crystallized portion was warmed to 30°C over about 5 hours and 10% of molten liquid (the fifth fraction) was separated. The residual solid portion was further warmed to 55°C to obtain 70% of molten liquid as the sixth fraction. The third fraction was mixed as intact with the second fraction of Example 1 in a proportionn of 20:80 to obtain the 4-2 fraction. Analytical values of each fraction are illustrated in Table 4. Fraction MDI content (%) Acidity (%) HC (%) Curing time (min) 2,4'- 4,4'- 3 17.2 82.8 0.041 0.061 24 hrs< 5 5.5 94.5 0.016 0.018 30.0 6 1.9 98.1 0.005 0.006 5.5 4-2 4.6 46.1 0.024 0.176 350.0

Claims: A process for simultaneous manufacture for a highly reactive MDI mixture having a low level of acidity and HC and high purity 4,4'-diphenylmethane diisocyanate from a reaction mixture obtained by phosgenating a polyamine mixture resulting from condensation of aniline and formaldehyde, said reaction mixture containing 4,4'-diphenylmethane diisocyanate as a primary component, 2,4'-diphenylmethane diisocyanate as a secondary component, impurities having acidity and hydrolyzable chlorine, comprising the steps of: (A) distilling the reaction mixture into a distillate first fraction and a residue second fraction at a temperature of 100° to 250°C and a pressure of 27 Pa to 1333 Pa (0.2 to 10 mmHg); (B) cooling the first fraction to precipitate therefrom a solid in an amount of not more than 85% by weight of the first fraction; (C) removing the precipitated solid to obtain an uncristallized third fraction and either (D1) heating the liquid third fraction in an inert gas at 80° to 120°C, and removing a resultant gaseous portion at ambient temperature and pressure to obtain a liquid fourth fraction or (D2) warming the solid removed in step (C) to a temperature not higher than 40°C, and removing the molten portion to obtain high purity 4,4'-diphenylmethane diisocyanate or (D3) conducting both (D1) and (D2). The process of claim 1 wherein steps (A) and (B) are conducted so as to yield from 15 to 40 parts by weight of the third liquid fraction from 100 parts by weight of the fist fraction. The process according to claim 1, comprising step (D1). The process according to claim 1, comprising the further steps of mixing the liquid fourth fraction with the residue second fraction to obtain a diphenylmethane diisocyanate mixture. The process according to claim 1, comprising step (D2). The process according to claim 1 , wherein step (A) is conducted by thin film distillation. The process according to claim 6, wherein the temperature is 180 - 250°C and the pressure is (1.0 - 3.0 mmHg) 133 Pa to 400 Pa. The process according to claim 1, wherein in step (B) the first fraction is quickly cooled to 100°C.

Inventors: ISHIDA NORITOSHI, NAGOU TAKASHI, NITTA KAZUNARI, SHIMAMATSU MITSUNORI, TASHIMA ZUNZI, ISHIDA, NORITOSHI, NAGOU, TAKASHI, NITTA, KAZUNARI, SHIMAMATSU, MITSUNORI, TASHIMA, ZUNZI
Applicants: MITSUI CHEMICALS INC, MITSUI CHEMICALS, INC.
Application year: 1991
Main classification: C07C263
IPC codes: C07C263, C08G18, C07C265