Chromatographic separation of zirconium isotopes

Abstract: The isotopes of zirconium can be partially or completely separated by loading an aqueous solution of an ionic compound of zirconium onto a cationic exchange resin which serves as the stationary phase of a chromatograph, eluting the compound with an aqueous acid and collecting distinct elution volumes representative of each isotope. In a preferred embodiment, the eluent is a strong mineral acid, such as hydrochloric acid and the chromatograph is of a type, such as a continuous annular chromatograph that it can be operated in a continuous, steady state manner.

Description: The present invention is concerned with processing zirconium to obtain a lower average thermal neutron capture cross section by a partial or complete separation of its isotopes thus improving its suitability as an internal material of construction, for instance, as a fuel rod cladding, for a nuclear reactor. Zirconium metal has historically been a material of construction, in particular cladding for fuel rods, for nuclear reactors, and there has been a continuing interest in reducing its tendency to adsorb thermal neutrons. The more transparent the internal materials of construction of a nuclear reactor are to such thermal neutrons the more efficiently the reactor will function since a certain number of these neutrons are necessary to sustain the nuclear reaction and their production must compensate for the adsorption by the internal materials of construction. Early efforts were directed to separating zirconium from hafnium. The two elements occur together naturally but the hafnium has a substantially larger capture section for thermal neutrons. Such efforts involved both chromatographic techniques using an ion exchange resin see, for instance, US-A-4 915 843 or EP-A-0 173 484 and various solvent extraction technique. More recent efforts have been directed to isolating a zirconium isotope with either a particularly high or a particularly low cross section to thermal neutrons. This allows the production of a zirconium with a lower average cross section than one composed of the naturally occurring isotope distribution. These efforts at isomer separation have generally involved some type of solvent extraction. These separation techniques are generally only able to separate one isomer at a time. Thus they do not provide a means for simultaneously isolating the zirconium 90 and 94 isotopes which are recognized as having particularly small cross sections (one source lists them as 0.055 and 0.031 Barns, respectively, as compared to 0.567 Barns for zirconium 91 and 0.1430 for zirconium 92). It is an object of the present invention to provide a process for simultaneously isolating both zirconium 90 and zirconium 94, which are the isotopes which both are fairly abundant and have low thermal neutron capture cross sections. It is a further object of the present invention to provide a more efficient process than solvent extraction by utilizing a chromatographic technique. It is yet another object of the present invention to provide a continuous technique for separating the isotopes of zirconium utilizing a continuously operating chromatographic technique. With this objects in view, the invention resides in a process as defined in claim 1, and as further characterized in the subclaims. The process according to the invention preferably involves the use of a continuous annular chromatograph. The invention will now be described by way of example, with reference to the accompanying drawings, in which: Figure 1 is a perspective view of a continuous annular chromatograph (CAC) with a portion in section to illustrate the annular construction, Figure 2 is a horizontal sectional view of the CAC along a diameter of the concentric circles defining the annulus, Figure 3 is an enlarged horizontal sectional view of a part of the top portion of the CAC, Figure 4 is a plan view of the bottom of the item shown in Figure 3, and Figure 5 is a plan view of the bottom of the CAC. The stationary phase is a cation exchange resin with a strong affinity for zirconium cations - typically in aqueous solution as ZrO +2 but which may also be complexed depending on the acid solvent. It is preferred that the cation exchange resin be capable of displaying a very strong affinity for such cations as reflected by a large solid to liquid distribution coefficient in dilute mineral acid solutions. It is particularly preferred that this coefficient be in excess of about 100 in acid solutions of less than about 0.3 Normal. It is particularly preferred to utilize cation exchange resins with a most probable capacity of about 0.1 milliequivalents per milliliter under elution conditions. An especially preferred stationary phase is sulfonated cross linked polystyrene beads. A preferred feed phase is that obtained from hydrolyzing chlorinated zirconium tetrachloride. Crude zirconium is commercially obtained by chlorinating zircon sand in the presence of coke at about 1000°C and separating the resulting zirconium tetrachloride from the resulting silicon tetrachloride by means of a differential condenser. The zirconium fraction typically contains a natural distribution of isotopes and also contains hafnium tetrachloride. Both compounds are readily hydrolyzed to yield an aqueous solution suitable for use in a chromatographic process. It is preferred to adjust the pH of this solution to the acid side, particularly to between about 3 and 4 to reduce the chemical shock to the stationary phase in elution with a highly acidic eluent. An especially preferred eluent is between about 2 and 6 more preferably between about 3 and 6 Normal aqueous hydrochloric acid, particularly when the mobile phase contains hafnium ions. The effective column height needed for a given resolution can be estimated from an application of the Kremser-Brown-Sounders equation, to empirical data on the separation capacity of a given stationary phase, mobile phase, eluent and flow conditions. A separation factor, α, is used to define this separation capacity. This factor is itself defined by the following formula for the binary case: α = y/(1-y) x/(1-x) wherein y is the molar concentrations of the desired isotope in the product faction rich in that isotope and x is the molar concentration of this same isotope in the tails fraction. Approximate calculations can be performed by selecting one isotopic fraction as the product, and defining the tails fraction as the composite of the other product fractions. Thus, if a product fraction is obtained in which 98% of the zirconium is zirconium 90 and if in the composite of all the other product fractions together only 2% of the zirconium is zirconium 90, the α defining this separation would be 0.98/(1-0.98) 0.02/(1-0.02) = 2401 Separation factors, α, for isotopic separations are conveniently evaluated on 25 to 100 cm columns with 25 cm length being preferred. For such columns α values for zirconium 90 on the preferred stationary phase with the preferred eluent are greater than about 1.05, preferably greater than about 1.085. The effective column length required for any desired degree of purification is then determined from this data. For instance, if a 25 cm test column yields a separation factor, α, of 1.085 this can be used as the separation factor for a theoretical stage, α S , in applying the Kremser-Brown-Sounders equation in estimating the number of theoretical stages, N, required. This formula can be used in the form: N = 1nα T 1nα S For the case being discussed this yields the following result: N = 1n2401 1n1.085 = 95.4 Thus, 95.4 theoretical stages of 25 cm each are required which implies an effective column length of about 24 M. The following table shows projected column length as a function of α and desired product purity. It is based on the assumption that the Kremser-Brown Saunders equation holds in the Underwood-Fenske form assuming the binary mixture approximation: α for 0.25 M Test Column 98% Purity 95% Purity Number of Stages Total Column Length (M) Number of Stages Total Column Length (M) 1.001 7830 1960 4970 1744 1.01 786 200 500 175 1.03 265 66 168 42 1.09 102 26 65 16 1.1 82 21 52 13 The effective column height can be vertical but it may have other orientations. What is important is the effective path over which the mobile phase travels. The path is provided in such a way that the chromatographic separation can be operated continuously. There is no convenient technique currently available for instantaneously sensing the concentration of any given isotope of zirconium. Thus, there is a preference for a continuously operating procedure which has reached steady state so that a particular product fraction reproducibly has a certain isotope distribution. If the chromatographic separation is effected in a discontinuous or batch manner random variations between runs may make it difficult to reproducibly collect product fractions with the same isotope distributions from run to run. For instance, if a single vertical column is loaded in a batch manner the elution time of the product fraction rich in a particular isotope may vary from run to run due to random variables difficult to control such as feed concentration fluctuations, etc. A particularly preferred continuously operating chromatograph is the continuous annular chromatograph. This device was developed by Oak Ridge National Laboratory and comprises an annular stationary phase which is rotated about the axis of the annulus. The annulus is provided by packing the stationary phase material, such as resin beads, between two concentric cylinders of differing diameters with vertical axes. A feed port is provided at a given angular position and one or more eluent ports are provided at some angular offset from the feed port. It is preferred to place a layer of glass beads above the stationary phase, and to feed the eluent to the glass beads while feeding the zirconium feedstock directly to the top of the stationary phase. This should prevent any undesired mixing effects. This device is provided with a number of product ports set at a number of angular positions which can be set arbitrarily to accommodate a particular set of operating condition. Each product port collects an elution volume which has had a particular residence time on the column. The stationary phase is typically rotated at a constant speed so that any vertical segment of the annular bed is above a particular fixed product collection port at a given time after this segment has been loaded with zirconium feedstock and eluent. Thus, each product collection port has an angular position which corresponds to a particular elution time for a particular rate of rotation of the stationary phase and for a particular flow rate through the stationary phase. The flow rate through the stationary phase is controlled by the pressure drop across the effective height of the stationary phase and the physical characteristics of the stationary phase, i.e., particle size and packing void volume. This pressure drop may be provided by the hydrostatic head of the feedstock and eluent but it is preferably provided by pressurizing the device. The pressure required to achieve a particular flow rate is governed by the nature of the stationary phase; the smaller the average particle of the resin beads making up the stationary phase the larger the pressure drop required to obtain a particular flow rate over a particular effective height. However, the separation factor for any given theoretical stage is improved as the average particle size of the resin beads is decreased. Thus, the effective height needed to effect a given degree of separation is decreased as the separation capacity of a unit length (or theoretical stage height) is increased by decreasing the average particle size of the resin beads. The flow rate across the effective height of the stationary phase and the rotational speed of the stationary phase should be coordinated such that a particular product fraction always elutes at the same angular position and thus is always delivered to the same product collection port. It is preferred that the chromatograph be operated in a displacement mode wherein no more than about 5 percent, more preferably no more than about 1 percent of the effective column height, is loaded with feed solution before elution is initiated. This is conveniently effected by using a feed solution which has insufficient acid strength to release the zirconium cations from ionic bonding with the cation exchange resin and loading no more than about 5 percent, preferably about 1 percent of the effective height, before adding an eluent of sufficient strength to cause the zirconium cations to migrate down the column at a reasonable rate. In the continuous annular chromatograph this end is achieved by coordinating the angular displacement between the feed port and the eluent port and the speed of rotation of the annular bed so that the time interval between loading and elution is just sufficient for the desired degree of penetration. The relationship between the time for loading and the depth of penetration is in turn governed by the flow rate through the annular bed. The displacement may be effected by either an isocratic or a gradient supply of eluent. In the former case, the eluent can simply be supplied from a single port while in the latter case, several ports at successively greater angular displacements from the feed port are utilized. In the gradient mode, elution under the influence of the initial eluent is permitted to proceed until some separation of the zirconium isotopes has been effected and then a higher acid strength eluent is supplied. This increases the migration speed of the zirconium cations down the column and minimizes the range of elution volumes or times over which a given component or product fraction will exit the column or, in other words, this procedure minimizes the band spreading. Decreasing the elution volumes by gradient elution or by other means increases the concentration of the product, i.e., the zirconium isotope, in the product fraction. Concentrations greater than about 5 g/l, especially between about 50 and 70 g/l are preferred. The flow rate down the column is governed by the pressure drop from the top to the bottom of the column and the nature of the stationary phase. The smaller the average particle size of the resin beads making up the stationary phase the higher the pressure drop required to obtain a given flow rate. This relationship is also effected by the particle size distribution of these resin beads. There is, however, a maximum attainable flow rate for any given cation exchange resin stationary phase which cannot be exceeded by the application of additional pressure. The suppliers of such resins rate them in terms of flow rate per given pressure drop and maximum attainable flow rate. It is preferred to use a stationary phase which will permit flow rates between about 20 and 80, more preferably between about 30 and 50 gallons per minute per square foot of cross sectional area. There is a relationship between the achievable flow rates and the effective column height needed for a given degree of purity. For a given system of stationary phase and eluent, the theoretical stage separation factor, α s , of the stationary phase will increase as the average particle size of the resin beads of the stationary phase decrease. However, as this particle size decreases so does the flow capacity of the stationary phase. Thus, there is an inverse relationship between α s and the flow capacity. Thus, a higher flow rate will require a greater effective column height to achieve the same degree of separation or product fraction purity. Furthermore, there is the additional constraint that the pressure required to achieve the desired flow rate not exceed the capability of available pumps, seals and feed tubing. The required pressure is a function of both the pressure drop needed per unit of effective height and the total effective height required for the desired degree of separation. Thus, as the flow capacity of the stationary phase is increased by a change in its physical configuration and consequently its theoretical stage separation factor, α s , is decreased, the required effective height and the required overall pressure drop are both increased. On the other hand, as the theoretical stage separation factor, α s , is increased by a change in the resin bead size distribution and consequently the flow capacity of the stationary phase is decreased, the pressure drop for a given effective height is increased. A pressure drop of less than about 2758 kPa (400 psi) more especially between about 345 and 1042 kPa (50 and 150 psi) is preferred. Thus, to obtain a system with a commercially practical capacity, it is necessary to use a stationary phase which will simultaneously display both a reasonable theoretical stage factor, α s , and a reasonable flow rate per unit of effective height with a reasonable pressure drop. This can be achieved by an appropriate selection of both the ionic capacity of the stationary phase cation exchange resin and the eluent. In a preferred mode several product collection ports are used to collect a particular product fraction. This is accomplished by closely spacing these collection ports so that they more than span the angular range of rotation that corresponds to the elution time interval of that particular fraction but do not extend to angular positions at which any significant portion of any other product fraction is expected to elute. Of course, this requires that the elution time intervals of different product fractions do not substantially overlap. This arrangement tends to insure that minor fluctuations in the steady state elution behavior which would cause a slight advancement or retardation of the elution time of the desired product fraction will not result in any loss of this fraction. A particular preferred device for use in practicing the present invention is illustrated in Figures 1 through 5. The continuous annular chromatograph 10 illustrated in Figure 1 comprises two concentric cylinders 30 and 35 which define the annular space 32 seen in Figure 2. Atop this annular space 32 is a distributor plate 20. Feed pipes or channels 21 and 23 run through the distributor plate 20 and terminate in feed nozzles 22 and 24, respectively. The feed nozzles 22 are intended to supply the feed phase to the exchange resin beads 27 which are packed in the annular space 32. For ease of illustration, these beads are shown as only partially filling the annular space 32. On the other hand, the feed nozzles 24 are intended to feed the eluent to the layer of glass beads 26 which sits atop the exchange resin beads 27. Thus the feed nozzles 24 are somewhat shorter than the feed nozzles 22. This feed arrangement serves to avoid any back mixing of the feed phase. The central cavity defined by the inner cylinder 35 is sealed by a cap 31 so that pipe or channel 25 can be used to apply pressure to the annular bed of resin beads 22. The bottom of the annular space 32 is defined by a product plate 40. As seen in Figure 5, a large number of product delivery channels or pipes 41 pass through this plate. This allows the collection of a variety Of product fractions and also facilitates adjustments to the operating conditions to allow product collection at various angular displacements. The distributor plate 20 is held in a fixed position above the annular space 32 by a bracket 62 which is turn connected to a support rod 61 which is affixed to a base plate 60. Also affixed to this base plate 60 is a support column 63 on which the product plate 40 rotatably rests. A shaft 70 passes through this support column 63 and base plate 60 and connects the product plate 40 to a motivating means not shown. Also affixed to the base plate 60 is an annular collection trough 50 which can be subdivided into any number of convenient segments, each with its own exit port 51. The continuous annular chromatograph 10 is operated by rotating the annular space 32 packed with the resin beads 27 beneath the fixed distributor plate 20 and its associated feed nozzles 22 and 24. The rotational force is supplied by the shaft 70.

Claims: A continuous chromatographic process for simultaneously isolating both zirconium 90 and zirconium 94 from a solution containing a mixture of zirconium isotopes to produce substantially pure fractions of each of said separated isotopes, where in said process includes the steps of: a) using a chromatographic separation column having an effective column hight sufficient to resolve each said zirconium isotopes into a distinct product fraction having a purity greater than 90% with a cation exchange resin having a strong affinity for zirconium cations, said resin having a monodisperse distribution of spherical beads with an average particle size of one micrometer or less and with a capacity for zirconium cations of between 0,01 and 0,5 milliequivalents/ml. b) preparing an aqueous feed solution of a hydrolized chloride zirconium compound having a solubility limit of about 90 g/l and feeding the same to the top of the chromatographic separation column, c) preparing an eluant which is an aqueous solution of hydrochloric acid having a normality of between 2- and 6-normal and feeding the same to the top of said chromatographic separation column to cause each of the zirconium isotopes in said feed solution to pass downwardly through said column at a different speed, and d) continuously and simultaneously collecting said substantially pure fractions at the bottom of said column. The process of claim 1, characterized in that the separation factor α , for a theoretical stage of 25 cm in height for zirconium 90 is at least 1,05. The process of claim 1 or 2, characterized in that the feed solution of the hydrolized chloride zirconium compound also contains a hafnium compound and the chromatography essentially completely separates the hafnium compound from the zirconium isotope fraction. The process of any of claims 1 to 3, characterized in that the continuous chromatographic process is effected in a continuous annular chromatograph. The process of claim 4, characterized in that the continuous annular chromatograph is operated so that the feed solution penetrates about 1 percent of the effective column height before the eluant is added. The process of claim 5, characterized in that the eluant is fed at more than one circumferential position of the annular chromatograph and the hydrochloric acid concentration of the eluant is increased at each successive feed position moving in the direction of rotation of the continuous annular chromatograph.

Inventors: LAHODA EDWARD JEAN, LEE ERNEST DEWITT, SNYDER THOMAS STEPHEN, LAHODA, EDWARD JEAN, LEE, ERNEST DEWITT, SNYDER, THOMAS STEPHEN
Applicants: WESTINGHOUSE ELECTRIC CORP, WESTINGHOUSE ELECTRIC CORPORATION
Application year: 1991
Main classification: B01D59
IPC codes: G01N30, B01D59