THERMOOXIDATIVE STABILIZATION OF POLYOLEFINS WITH AN OXO-PIPERAZINYL-TRIAZINE AND A PHOSPHOROUS ACID ESTER

Abstract: Only two symmetrical stabilizers in a polyolefin or copolymer thereof, provide thermooxidative (''TO'') or antioxidative (''AO'') stability. One is a phosphite or fluorophosphite; the other is a monomolecular tri-substituted triazine in which each of three chlorine atoms on a trihalo-s-triazine is substituted with a piperazinone in which the N atom in the 4-position is alkylated. Only a trace amount of phosphite, from 0.01 phr to no more than 0.1 phr, is used; additional phosphite has no noticeable effect. The trace amount of phosphite has a surprising booster effect, giving the stabilized composition excellent TO stability. Articles thermoformed from the stabilized polyolefin or copolymer thereof may be used under the hood or the dash of a vehicle, and, in containers for packaging goods, all of which articles are subject to TO degradation even if they are not subject to ultraviolet light degradation.

Description: THERMOOXIDATIVE STABILIZATION OF POLYOLEFINS WITH AN OXO-PIPERAZINYL-TRIAZINE AND A PHOSPHOROUS ACID ESTER BACKGROUND OF THE INVENTION This invention relates to the use of a particular hind¬ ered amine light stabilizer ("HALS") , namely a onomeric oxo- piperazinyl triazine in a novel combination with known esters of phosphorous acid and of fluorophosphorous acid. Such oxo- piperazinyl triazines are referred to hereinafter as "tri- azines" for brevity. The esters ("phosphites" and "fluoro- phosphites") are well known "synergists" being used as process stabilizers, or melt stabilizers, conventionally used in combination with a hindered phenol AO. Each novel combina¬ tion has been found to be unexpectedly effective to stabilize a polyolefin against thermal oxidative ("ther ooxidative" or "TO", for brevity) degradation, despite the very low concen¬ tration in the range from 0.01 to 0.1 phr (parts per 100 parts of polyolefin) of ester used. In one instance the triazine is a N 4-methylated oxo- piperazinyl triazine (MPIP-T) ; in the other, the triazine is a monomeric oxo-piperazinyl triazine with an unsubstituted N atom (PIP-T) . The combination of a MPIP-T and ester is found to be more effective than that of a PIP-T and the ester. As stated in copending U.S. patent application Ser. No. 07/369,573 filed June 21, 1989, the effectiveness of PIP-Ts as AOs was overlooked. Any general disclosure relating to 1,2,2,6,6-pentamethyl-4-piperidylaminotriazine derivatives being useful as antioxidants, as in UK patent application GB 219423A, was made only because they were known to be good UV- stabilizers. The rationale was that if the mechanism of polymer oxidation, irrespective of how it is propagated, follows the same course, effective UV-stabilizers should be good AOs. This general concept was enunciated in an article titled "Stabilization of Filled Polyolefins" by E. Stengrevics andP. Horng in Plastics Compounding, July/August 1987. They backed up the general notion with data obtained with polysubstituted piperidinyl HALS in combination with specific hindered phenol AOs and less than 0.1 phr of a triarylphosphite. The data showed that polymeric piperidyl-substituted HALS in combina¬ tion with 0.05% triarylphosphite were more effective than 0.1% of a hindered phenol (see Table I). However, 0.0125% of the triarylphosphite in combination with a non-polymeric piperidyl-substituted compound (identified as HALSI) failed at 70°C (see Table II). In further tests, the base stabili¬ zation system was a combination of a hindered phenol and 0.1% phosphite, and HALSI showed no contribution to thermal stability (see middle of col 1, pg 38) . From the foregoing it is clear that it was deemed essential that the hindered phenol be used with 0.1% of a phosphite for the base system; and, that, if the hindered phenol was left out, non-polymeric piperidyl-substituted compound would not show any improvement over a hindered phenol AO. It was thus only by chance that it was found that the PIP-T and MPIP-T have substantial AO activity, in addition to their UV-stability, and that sudh AO activity as they did have, could be enhanced with a trace amount of a commonly available symmetrical ester of phosphorous acid or fluoro- phoεphorous acid, routinely used as an AO, substantially in the absence of a hindered phenol AO to a far greater extent than one might expect. By a "symmetrical ester" I refer to one having a structure which is symmetrical about either a P atom, as in a triarylphosphite; or, about a C atom, as in an acyclic long chain substituted pentaerythritol diphosphite. This effect was particularly surprising in view of the fact that the thrust of U.S. Patent No. 4,187,212 to Zinke et al was that symmetrical triarylphosphites having the structure given herebelow, in combination with hindered phenol AOs were remarkably effective against degradation reactions and cross-linking reactions such as those normally occuring in the processing of olefins. Further, tri-esters of phosphorous acid and fluoro- phosphorous acid are preferably used in combination with other antioxidants, as they are most effective when so used (see "The Stabilisation of Plastics against Light and Heat" by J. Voigt, first ed. , pg 323,Springerverlag 1966). Again, in GB 1,078,772 it is disclosed that the mixture of aryl- containing phosphites with o-substituted phenols in poly- olefins exhibits particularly good stabilization, the high degree of effectiveness being attributed to the o-substituent in the phenol component. Though the piperidyl compounds are stated to be effec¬ tive antioxidants, they are not effective enough (as an anti- oxidant) in polyolefins, and in particular, homopolymers of propylene, or copolymers of propylene and ethylene in which the latter is present in a minor amount by weight (such homopolymers and copolymers are collectively referred to herein as » pp" for brevity), to warrant their use, without the use of a secondary stabilizer, for such duty. When piperidinyls are used as stabilizers, they are used as light stabilizers to protect against ultraviolet radiation, and, in practical applications, only in combination with a phosphor¬ ous acid ester or fluorophosphorous acid ester, hindered phenol or other antioxidant. Typically, in practice, the secondary stabilizer is used in an amount greater than o.l phr. The foregoing was equally true for piperazin-2-one-con¬ taining compounds used as HALS, until the discovery disclosed in the aforementioned Ser. No. 369,573, of the effect of a PIP-T and a symmetrical phosphite. Evidence of the foregoing is provided in an article titled "Hindered Diazacyclo- alkanones as Ultraviolet Stabilizers and Antioxidants" by J.T. Lai, P.N. Son and E. Jennings, Polymer Stabilization and Degradation 91-99, ACS Symposium Series, American Chemical Society, Washington, D.C. (1985). Slit tapes of PP (2 x 100 mil) containing a combination of 0.1 phr (parts per 100 parts of substrate) of HALS, aged in the Arizona sun, even the polymeric piperidine did not fare very well (pg 92) . Unique among the HALS disclosed in the aforesaid article was a decahydroquinoxaline which provided both AO and light stabilization. It was determined that the most important features for its AO activity were (i) the fused bicyclodiaza- cycloalkane ring, (ii) dialkyl substituents at the C posi- tion, and (i .n..) alkyl, i.nstead of acyl substi.tuents at the N1 position. We have now provided a monomeric triazines which, in combination with no more than 0.1 phr of a symmetrical phosphite or fluorophosphite ester, give outstanding protection against TO degradation when essentially homo¬ geneously distributed in a polyolefin, and simultaneously provides adequate stability during melt processing. More specifically this invention relates to a combination UV stabilizer (PIP-T) not heretofore known to have substantial AO activity, and a known AO, this combination consisting essentially of a symmetrical fluorophosphorous acid ester, and a monomolecular tri- substituted triazine in which each of three chlorine (or other halogen) atoms on a trihalo-s-triazine, specifically cyanuric chloride, is substituted with a polysubstituted piperazin-2-one ("PSP") so as to form a tri-substituted triazine with a PSP substituent at each of the 2, 4 and 6 positions on the ring. The monomolecular PIP-T or MPIP-T is represented by the structure PSP PSP wherein PSP represents a substituent derived from a cyclic amine. When the foregoing structure is a MPIP-T, each PSP is represented by a structure selected from the group consisting of wherein, R- represents C.-C 24 alkyl, Cg-C 20 cycloalkyl, C_- C 2Q araalkyl or alkaryl, C.-C 24 aminoalkyl, or 8 -C 20 aminocycloalkyl; R 2 , R_, R 4 , and R g independently represent ^-ι ~ C 2 Λ a l^ c Y 1 ' and, R 2 with R 3 , or 4 with R g are cyclizable to C 5 -C- 2 cycloalkyl including the C and C atoms respectively, of the piperazin- 2-one ring; R g and 7 independently represent C.-C 24 alkyl, and polymeth- ylene having from 4 to 7 carbon atoms which are cyclizable; Rg represents H, C.-C- alkyl, and phenyl; R g represents C..-C 3 alkyl; and, p represents an integer in the range from 2 to about 10. When the foregoing structure is a PIP-T, each PSP is represented by a structure selected from the group consisting of wherein, R. represents C.-C 24 alkyl, C 5 -C 20 cycloalkyl, C_- C 2Q araalkyl or alkaryl, 1 -C 24 aminoalkyl, or C 6 ~ c 20 aminocycloalkyl; R 2 , R,, R 4 , and R 5 independently represent C 1 ~C 24 alkyl; and, R 2 with R 3 , or R 4 with R g are cyclizable to C 5 -C- 2 cycloalkyl including the C and C atoms respectively, of the piperazin- 2-one ring; R g and R 7 independently represent C.-C 24 alkyl, and polymeth- ylene having from 4 to 7 carbon atoms which are cyclizable; R g represents H, C.-Cg alkyl, and phenyl; and, p represents an integer in the range from 2 to about 10. Specific PIP-Ts which are tri-substituted having the following polysubstituted piperazin-2-one substituents: 1-[3-(isopropylamino)propyl]-3,3,5,5-tetramethylpiperazin-2- one; 1-[2-(isopropylamino)ethyl]-3,3,5,5-tetramethylpiperazin-2- one; 1-[2-(butylamino)ethyl]-3,3,5,5-tetramethylpiperazin-2-one; and, 1-[2-(cycohexylamino)ethyl]-3,3,5,5-tetramethylpiperazin-2- one; inter alia. Specific MPIP-Ts which are tri-substituted with polysubstituted piperazin-2-one substituents are prepared by alkylating the foregoing PIP-Ts so as to alkylate them. Each PSP substituent is attached through the terminal N atom to the triazine ring, the substituent being selected from 1-[3-(isopropylamino)propyl]-3,3,4,5,5-pentamethylpiperazin- 2-one; 1-[2-(isopropylamino)ethyl]-3,3,4,5,5-pentamethylpiperazint¬ one; 1-[2-(butylamino)ethyl]-3,3,4,5,5-pentamethylpiperazin-2-one; and, 1-[2-(cycohexylamino)ethyl]-3,3,4,5,5-pentamethylpiperazin-2- one; inter alia. It is this limited class of triazines, and particularly those monomolecular ones having a relatively low MW in the range from about 850 to less than 2000, which display the remarkable AO stabilization activity in the presence of such a low concentration of phosphorous acid or fluorophosphorous acid ester. Because of the excellent TO stability of the novel combinations of this invention, the components are not easily volatilized during the manufacture of an article, or during the useful life of the article. Thus, PP articles may be used in the temperature range from about 120*C to about 145°C or below the heat distortion temperature (HDT) of the PP. This makes a MPIP-T the stabilizer of choice for impellers for washing machines for clothes, and impellers for dish-washing machines; as an inner liner for automobile fenders; for under the hood applications in automobiles; etc. Further, a combination of the triazine with so low a concentration of ester is exceptionally compatible with poly¬ mers, often behaving as a single phase, for example by being substantially soluble in PP, the solubility being affected by the molecular weight of the polymer. This is particularly noteworthy because polar UV stabilizers are known to be excluded from the crystalline phase of a polyolefin such as PP, preferring to be concentrated in the amorphous phase from which it can more readily migrate to the surface of a mold or die in which an article is being formed. Moreover, preferred triazines and esters are essentially water-white, or only slightly colored, crystalline or amorphous solids, or non-viscous liquids, so that they are easily homogeneously dispersed in a polymeric substrate and impart no color, or only a negligible amount of color to the substrate in which they are dispersed or dissolved. SUMMARY OF THE INVENTION It has been discovered that a trace amount, no more than 0.1 phr, of symmetrical esters of PAC or FPAC in combination with no more than 0.2 phr of an oxo-piperazinyl triazine with three piperazinone substituents, each of which has an N atom which may, or may not be alkylated, provides surprising thermooxidative ("TO") stability in a polyolefin. The AO stability of this combination of HALS and AO is far greater than might be expected based on the known AO stabilizing effectiveness of each component; further, such a combination is effective without using a hindered phenol AO such as is typically used with a triazine stabilizer. It is therefore a general object of this invention to provide a stabilized poly(α-olefin) , or a copolymer of an α- olefin, in which copolymer a repeating unit derived from the -olefin is present in a major molar amount, for use in applications where degradation by UV-light may not be a primary concern, or even a significant consideration, such as in thermoformed articles for use under the hood or the dash of a wheeled vehicle, which articles are subject to TO degradation; and, in containers for packaging the goods. It is a specific object of this invention to provide an article of arbitrary shape, derived from a thermoformed composition of matter consisting essentially of a polyolefin or the aforesaid copolymer containing at least 75 molar % of polymerized α-olefin, which article is stabilized against TO degradation by combining from 0.1 phr to 2 phr of a PIP-T with from about 0.01 phr but less than 0.1 phr of a symmetrical ester of phosphorous acid or fluorophosphorous acid in the absence of a hindered phenol AO, so as to provide a level of stability which is substantially the same as, or better than, that of an article conventionally stabilized against TO with the hindered phenol and more than 0.1 phr of the same symmetrical phosphite or fluorophosphite ester. It has still further been discovered that whether a symmetrical phosphite or fluorophosphite ester is used in combination with a PIP-T or a MPIP-T, an amount of the ester in excess of 0.1 phr produces essentially no additional boost in stability of the polyolefin in which it is used. Therefore the cost of additional ester for optimum stabilization can be optimized without incurring unnecesssary expense. DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS In the best mode, the invention is directed to a stabilized composition of matter consisting essentially of polypropylene, or polyethylene, and copolymers thereof in which a repeating unit derived from an α-olefin is present in a major molar amount, preferably more than 75 mole %, in combination with a PIP-T ot MPIP-T, and from 0.01 to no more than 0.1 phr of a symmetrical ester of phosphorous acid, or fluorophosphorous acid, substantially in the absence of a hindered phenol AO. Though homopolymers of ethylene and propylene are most commonly used, homopolymers of isobutylene, 1-butene, 1-pentene, 4-methyl-l-pentene, and 1- hexene may also be stabilized with the PIP-T or MPIP-T and ester, each present in the range specified above. Copolymers of one of these α-olefins with a diene monomer are commerciallyavailable and may be stabilized in the same manner. As will be seen from the structure of the triazines set forth herebelow, the substituents are essentially symmetrically disposed about the triazine ring. It is thought that the symmetrical structure of the esters used herein may be peculiarly effective with the triazines based in large part on this mutual symmetry of structures. The particular degree of effectiveness of the combination of triazines and ester in PP is evidenced by improved strength and discoloration resistance, and the retention of flexibility of test samples of PP plaques and fibers oven-aged by exposure to heat in a convection oven in accordance with the procedure for heat aging without load, set forth in ASTM D-3045-74. The tensile strengths of plaques were measured according to the procedure set forth in ASTM D- 882-83. Failure is determined either by intense discoloration, or brittleness when manually flexed, or when the tensile is reduced by 50% from the original. A particular MPIP-T has the structure (I) in which PSP is represented by In a particular monomolecular polysubstituted N -unsubs- tituted piperazinone-triazine PIP-T(1) the PSP is represented by the structure Me = methyl The symmetrical phosphites are represented by the structure 4 wherein R- Q represents tert-butyl, 1,1-dimethylpropyl, cyclohexyl or phenyl, and one of R.. and R- 2 is hydrogen and the other is hydrogen, methyl, tert-butyl, 1,1- dimethylpropyl , cyclohexyl or phenyl; and, the symmetrical pentaerythritol phosphites are represented by the structure where R' is derived from a C 12 - C 24 onohydric alcohol. Examples of commonly available symmetrical triaryl esters of phosphorous acid which may be used are triphenyl phosphite; and tris(nonylphenyl) phosphite. Examples of commonly available symmetrical penta¬ erythritol phosphites which may be used are distearyl pentaerythritol diphosphite; diisodecyl pentaerythritol diphosphite; and tristearyl sorbitol triphosphite. Preferred commercially available phosphites are Weston 618 which is distearyl pentaerythritol diphosphite; Mark 2112 or Irgafos 168 which is tris(2,4-di-t-butylphenyl) phosphite; and Ultranox 626 which is tris(2,4-di-t-butylphenyl) penta¬ erythritol diphosphite. The symmetrical fluorophosphites are represented by 2,2'-ethylidenebis(4,6-di-t-butylphenyl)fluorophosphite having the structure The average results (failure at the end of days) obtained in the standard procedure of oven aging at 125 ° C and 140°C with each stabilizer identified, using a statistically significant number of polypropylene plaques molded from commercially available Profax 6301 lot #60989, each plaque 5 cm x 5 cm x 20 mils thick, using a specific triaryl phos¬ phite, namely Ultranox 626, and a specific fluorophoshite, namely Ethanox 398, are set forth in Table 1 herebelow. Each sample contained 0.05 phr of calcium stearate as lubricant, and the specified amount of stabilizer(s) . The ingredients for each recipe were mixed by thoroughly shaking in a paper bag. The mixture was then extruded and pelletized. The pellets were used to mold a 8" (inch) x 8" plaque which was then cut into squares to be tested in the oven. Though the generally accepted test temperature for polypropylene plaques is 125"C, a higher temperature (140°C) was also used because degradation is too slow at the lower temperature. As will be evident, some samples have still not failed nearly 9 months after the tests were begun. The oven aging tests are carried out in a convecton oven in the absence of ultravolet or visible light. The results are set forth below, first listing samples with only a single stabilizer added. Combinations are provided at different levels of esters to demonstrate that the boost of the ester is obtained at levels no higher than 0.1 phr, any excess ester, if added, being added to no significant effect. TABLE 1 125-C 140 β C (days) (days) 11 2 >212* 73 89 24 32 8 25 6 >212* 43 >212* 82 >212* 99 92 27 >212* 44 >212* 74 *the samples have not as yet failed - September 11, 1990 From the foregoing increase in days to failure of the samples, it is evident that there is an unexpectedly high boost in TO stability attributable to the presence of the trace amount of phosphite. Having thus provided a general discussion of the problems addressed and solved in our invention, and a specific illustration of the best mode for preparing a stabilized composition of matter, and an article thermoformed from such matter, it is to be understood that no undue restrictions are to be imposed by reason thereof, except as provided by the following claims.

Claims: CLAIMS l. A composition of matter having thermooxidative ("TO") or antioxidative ("AO") stability in the substntial absence of a hindered phenol antioxidant, said composition of matter consisting essentiall of a poly(α-olefin) , or a copolymer of an α-olefin, in which copolymer a repeating unit derived fro said α-olefin is present in a major molar amount, and a trace amount, from 0.01 to no more than 0.1 phr, of a symmetrical phosphite or fluorophosphite in combination with from about 0.1 phr to about 2 phr of a tri-susbtituted triazine derivative ("MPIP-T") in which the 2-, 4- and 6-positions of the triazine ring are substituted with a polysubstituted ppiippeerraazziinn--22--oonnee iinn wwhhiicchh tthhee NN aattoomm is alkylated, said MPIP- T being represented by the structure wherein PSP represents a substituent derived from a cyclic a ine, said PSP being represented by a structure selected from the group consisting of wherein, R- represents C.-C 24 alkyl, C 8 -C 12 cycloalkyl, c η - C 2Q araalkyl or alkaryl, C.-C 24 aminoalkyl, or C 8 -C 20 aminocycloalkyl; R 2 , R-, R 4 , and R- independently represent C ι ~C 24 alkyl; and, R 2 with R 3 , or R 4 with R g are cyclizable to C 5 -C- 2 cycloalkyl including the C and C atoms respectively, of the piperazin- 2-one ring; Rg and R ? independently represent C 1 ~C 24 alkyl, and polymeth- ylene having from 4 to 7 carbon atoms which are cyclizable; Rg represents H, C.-Cg alkyl, and phenyl; Rg represents C 1 ~C 3 alkyl; and, p represents an integer in the range from 2 to about 10. 2. The composition of claim 1 wherein said symmetrical phosphite is selected from the group consisting of (i) a triaryl phosphite ester having the structure wherein R- 0 represents tert-butyl, 1,1-dimethylpropyl, cyclohexyl or phenyl, and one of R.. and R- 2 is hydrogen and the other is hydrogen, methyl, tert-butyl, 1,1- dimethylpropyl, cyclohexyl or phenyl; and, (ii) a pentaerythritol phosphite represented by the structure wherein R' is derived from a C- 2 - C 24 monohydric alcohol; and, (iii) 2,2'-ethylidenebis(4,6-di-t-butylphenyl)fluoro¬ phosphite. 3. The composition of claim 2 wherein said symmetrical triaryl ester of phosphorous acid is selected from the group consisting of triphenyl phosphite; tris(nonylphenyl) phosphite; and, tris(2,4-di-t-butylphenyl) phosphite. 4. The composition of claim 2 wherein said symmetrical pentaerythritol phosphite is selected from the group consisting of distearyl pentaerythritol diphosphite; tris(2,4-di-t- butylphenyl) phosphite; and tris(2,4-di-t-butylphenyl) penta¬ erythritol diphosphite. 5. The composition of claim 1 wherein said poly(α-olefin) is a homopolymer of ethylene,propylene, isobutylene, 1-butene, 1-pentene, 4-methyl-l-pentene, or 1-hexene; and, said copolymers are copolymers of said α-olefin with a diene monomer. 6. The composition of claim 2 wherein said polysubstituted piperazin-2-one substituent is selected from the group consisting of: 1-[3-(isopropylamino)propyl]-3,3, ,5,5-pentamethylpiperazin- 2-one; 1-[2-(isopropylamino)ethyl]-3,3,4,5,5-pentamethylpiperazin-2- one; 1-[2-(butylamino)e hyl]-3 ,3,4,5,5-pentamethylpiperazin-2-one; and, 1-[2-(cycohexylamino)ethyl]-3,3,4,5,5-pentamethylpiperazin-2- one; inter alia. 7. A thermoformed article of arbitrary shape, formed from a homopolymer of an α-olefin, or a copolymer of an α-olefin in which copolymer a repeating unit derived from said α-olefin is present in a major molar amount, including a combination of only symmetrical stabilizers which improves the thermo- oxidative ("TO") or antioxidative ("AO") stability of said article. one stabilizer being a trace amount, from 0.01 phr to no more than 0.1 phr, of a fluorophosphite stabilizer, and without any secondary stabilizer, and another stabilizer being a monomolecular oxo-piperazinyl triazine having three piperazinone substituents ("PIP-T") , said PIP-T having the structure wherein PSP represents a substituent derived from a cyclic aminβ represented by a structure selected from the group consisting of wherein, R^ ^ represents C 1 -C 24 alkyl, C 8 -C 12 cycloalkyl, C 6 - C 20 araalkyl or alkaryl, C 1 ~C 24 aminoalkyl, or Cg-C 20 aminocycloalkyl; R 2 , R 3 , R., and R 5 independently represent c 1 _ 2 alkyl; and R 2 with R 3 , or R 4 with R 5 are cyclizable to Cg-C 12 cycloalkyl including the C 3 and C atoms respectively, of the piperazin- 2-one ring; g and R- independently represent C 1 -C 24 alkyl, and polymeth- ylene having from 4 to 7 carbon atoms which are cyclizable; R g represents C χ -C 3 alkyl; and, p represents an integer in the range from 2 to about 10. 8. The article of claim 7 wherein said fluorophosphite is 2,2'-ethylidenebis( ,6-di-t-butylphenyl) fluorophosphite.

Inventors: KLETECKA GEORGE, LAI JOHN TA-YUAN, SON PYONG NAE, KLETECKA, GEORGE, LAI, JOHN, TA-YUAN, SON, PYONG, NAE
Applicants: GOODRICH CO B F, THE B.F. GOODRICH COMPANY
Application year: 1991
Main classification: C08L23
IPC codes: C08K5, C08L23