Method for producing composite material mainly composed of carbon and boron

Abstract: There is provided accroding to the invention a method for producing a composite material mainly composed of a carbon and boron comprising the steps of impregnating a carbon material with a boron oxide and/or a hydrate compound thereof, and baking such carbon material under pressure by inert gas at a temperature of not lower than 1500°C. A neutron absorbent and an oxidation resistant carbon material both including the composite material are also provided.

Description: BACKGROUND OF THE INVENTION 1. Field of the invention: The present invention relates to a composite material of carbon-boron (hereinafter referred to as C-B) and, more particularly, to a method for producing a composite material in which boron component (hereinafter referred to as B) is evenly dispersed or distributed in the form of ultrafine particles in carbon component (hereinafter referred to as C) and to various uses of the composite material obtained by the method, in particular, uses as a neutron absorbent and as an oxidation resistant carbon material. 2. Description of prior art: C-B composite material has been heretofore popularly researched, developed and used as a neutron absorbent in atomic industry, as a carbon material having oxidation resistance and as a structural material for machines. A conventionally employed method for producing the C-B composite material comprises the steps of mixing a B₄C (boron carbide) produced separately with either a carbon material or a material possible to be carbonized, baking them at high temperature, and treating them to be transformed into a solid solution, as is disclosed in the Japanese Laid-Open Patent Publication (unexamined) No.1987-108767, the Japanese Patent Application No.1987-297207, etc. In the C-B composite material obtained according to the mentioned conventional porcess, B₄C is mixed with carbon after crushing and grinding a large and rough solid of B₄C. In this respect, because such grinding is mechanically performed, there is a limit in the pulverizing of B₄C. Accordingly, in a C-B composite material thus obtained, there are a B₄C portion, a solid solution portion of B₄C and carbon, and a portion of carbon alone. In effect, when observing microscopically, the obtained C-B composite material is not always completely even as a whole. In the mentioned coventional method, because the two kinds of powder are mixed each other, molded and baked, there arises a difficulty in the steps of cutting and machining the baked material, hence a problem exists from economical point of view in that material productivity of expensive B₄C is considerably reduced by removal and waste of cut powder. Moreover, a most serious problem in the conventional method exists in that a large amount of mineral impurities other than boron are included (usually 5000ppm). Those impurities come mixed into the composite material due to contact with machines and equipments made of steel continuously during each step of grinding, mixing, molding and baking of compound material. This disadvantage is very difficult to overcome in the conventional methods. Coexistence of a small amount of mineral impurities may not be a serious problem depending upon the use of B-C composite material. However, when employing such a B-C composite material mixed with mineral impurities as a material for atomic industry, the mixed mineral impurities generate simultaneously reactions such as isotope transformation, splitting, etc. by radiation exposure or the like. Accordingly, when using it as a nuclear fusion material, a fatal disadvantage of decreasing plasma temperature due to high temperature elements emitted from the impurities will come out. Therefore, as a carbon material for use in atomic industry, a highly purified specific material, i.e. an ultrahighly pure material of which mineral impurity is not more than 5ppm, more perferably not more than 2ppm, substantially 0ppm (measured by atomic absorption photometer) is usually employed. In a method for processing such an ultrahigh pure material, the mineral impurities are eliminated by halogenation treatment of high volatility, as is disclosed in the Japanese Patent Application No.61-224131 for example. In the composite material of B₄C-C, however, because of existence of boron in carbon material, impurities cannot be eliminated by using the mentioned treatment. One method for producing a carbon-boron oxide (C-B₂O₃) composite material comprises impregnating a carbon material with a solution of orthoboric acid (H₃BO₃ or B(HO)₃), that is thereafter treated at 700°C or 200-1000°C (P. Erhburger et al: Carbon., 24 , 495-499(1986) and D.J. Kim et al: Nonmujip-Ch'ungnam taehakkyo Kongop Koyuk Yon'guso., 8 , 103-110(1986). Boric acid (H₃BO₃) is converted into boron oxide (B₂O₃) by heat treatment at a temperature not lower than 185°C. Boron oxide (B₂O₃) is then converted into boron carbide (B₄C) and reacted on the carbon material by heat treatment at a temperature not lower than 1500°C. Therefore, the composite material obtained according to this method is in the form of a mixture of carbon and boron oxide (B₂O₃). The carbon-boron oxide (C-B₂O₃) composite material changes to a high mechanical strength material. Further, the application field of the C-B₂O₃ composite material is limited because of containing a lot of oxygen in the material. For example, the C-B₂O₃ composite material is not suitable for a neutron absorbent. The mentioned disadvantage of the conventional method may result in a still further problem in that when using crucible for melting alloy, stirring bars etc. necessary to obtain a specifically precious composition in metallurgical industry and the mentioned instruments are oxidated and worn out, then impurities may be mixed into the alloy eventually resulting in pollution. Also when using the mentioned composite material as a member to perform hot press for baking ceramics, the same problem of pollution as mentioned above may come out. SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to solve the above-discussed problems of the conventional method when using B₄C-C powder as a material and provide a superior B-C composite material. Another object of the invention is to provide a novel use of the B-C composite material. To accomplish the foregoing objects, the inventors have been engaged in research and development of superior composite material and, in the first place, adopted a method for impregnating boron oxide or hydrated compound into carbon material in the form of melt or solution. By this method, it is now possible for boron component to permeate into fine carbon particle surface or fine pores in carbon material at molecule level so as to be dispersed very finely throughout the entire carbon material as compared with the use of B₄C fine particles. Further, to use boron in the form of an oxide, a reaction method suitable for fixing boron into carbon by reaction between the oxide and carbon and suitable for solid solution treatment is also provided by the invention. In other words, the inventors have succeeded in developing a method comprising the steps of imgregnating a liquid boron compound into a carbon material, and baking a mixture thus obtained at high temperature under high pressure so that the impregnated boron compound is not volatilized from the carbon material and that boron reacts sufficiently on carbon. It has been recognized by the inventors that the novel C-B composite material obtained by the mentioned method performs an excellent function as a neutron absorbent and that this composite material exhibits a function of remarkably high oxidation resistance as compared with the conventional B₄C powder mixing method. The composite material according to the invention not only overcome such disadvantages of the prior art that, because of the use at high temperature under oxidation atmosphere resulting on oxidation wear, relative members or parts must have been frequently replaced, but also exhibits that the composite material is superior in oxidation resistance and satisfiable in machinability. Described hereinafter is an illustrative reaction between boron oxide (B₂O₃) and carbon. (First step) A molten boron oxide is impregnated into a cut compact of isotropic high density carbon material ("IG-11" produced by Toyo Tanso), for example, at 600 to 1400°C, more preferably at 800 to 1200°C under pressure in a pressure container. In this case, it is preferable that the impregnation is carried out after once reducing pressure in the container so as to eliminate air out of fine pores of the carbon material, but such preliminarily degassing is not always necessary. For impregnating B₂O₃ into the carbon material, several kg/cm² of pressure is needed, but 50 to 100kg /cm² is preferable in order to impregnate B₂O₃ under pressure completely into the deep portion of carbon material. Required pressure value should be appropriately decided depending upon percentage of voids, particle size, distribution of pores, temperature, etc. (Second step) The carbon material impregnated with B₂O₃ is then subject to heat treatment (hereinafter referred to as HIP) at high temperature under high pressure using inert gas as a pressure medium. As a result of this heat treatment using an inert gas such as Ar as a medium, a pressure is applied to the carbon material and B₂O₃ solution evenly from every direction as if pressure was hydraulically applied to them, thereby confining B₂O₃ in to the carbon material while preventing evaporation thereof, thus chemical reaction between carbon and boron proceeds. The pressure and temperature in the heat-treating apparatus is not respectively lower than 100kg/cm² and 1500°C, preferably not lower than 2000°C and 1500 to 2000kg/cm². If the temperature is over 2300°C, undesirable reaction of decomposing the solid solution of carbon and boron may take place simultaneously. The foregoing first and second processes are essential, and a following third process may be added to eliminate a small amount of B₂O₃ still remaining in the carbon material. (Third step) The composite material after completing the HIP treatment in the foregoing second process is further treated under the pressure not higher than 1.33kPa (10Torr), preferably not higher then 0.67kPa (5Torr), and at the temperature not lower than 1000°C, perferably not lower than 1500°C, whereby quantity of B₂O₃ in the composite material is decreased to not more than 0.1%. In the B-C composite material thus obtained, boron is very finely and evenly dispersed and distributed throughout the composite material as compared with the conventional material employing B₄C powder. In the invention, any carbon material including common carbon material, aerotropic carbon material, carbon-carbon composite material (hereinafter referred to as C/C material) in addition to the mentioned isotropic carbon material can be employed irrespective of kind thereof. Since carbon powder is not used in the invention, carbon can be boronized without changing a given shape, organization and structure of the carbon composite, i.e., as they are which is one of the most important advantages of the present invention. When the mentioned boronization is carried out using an ultrahigh pure isotropic high density graphite as a matrix for example, quantity of impurities other than carbon and boron elements of an obtained composite material is very small to the extent of less than 5ppm which is substantially the same as purity value of the matrix on condition that a high pure boron compound is employed. This is because pollution possible to occur in the prior art during the mechanical steps of grinding, mixing compressive moldings does not take place at all. The advantage of the method according to the invention is typically exhibited when boronizing carbon/carbon composite material. In the conventional method employing B₄C powder, several specified equipments and techniques are needed for grinding to the particle size of less than 1µm, and in which obtained fine particles are admixed with resin component, applied to carbon fibers, thus making a prepreg, which is then molded, hardened by heating and carbonized, finally obtaining a boronized C/C material. A serious problem, however, exists in that the carbon material cannot be completely graphitized. Because, despite that a high temperature of 2500 to 3000°C is required for graphitization of carbon, B₄C component begins decomposition at about 2300°C. Accordingly, it is almost impossible to insert fine B₄C particles into the fine pours of the C/C material preliminarily graphitized by baking at a high temperature of 3000°C. Even distribution of boron component up to the deep portion of the C/C material is difficult all the more. The situation is same in case of ordinary carbon block. As for the C/C material, however, there is a peculiar difficulty in achieving required boronization while keeping strength of carbon fiters. On the contrary, boronization of C/C material can be performed very easily. As mentioned above, boron component can be forecedly press-fitted (compressively inserted) into fine pores of the carbon materials in the form of melt or solution in molecule size, and dispersed evenly up to the deep portion. Furthermore, there is no change in organization of the C/C material as a result of forced press-fit (compressive insert) of boron component and subsequent baking thereof, and carbon material is preliminarily graphitized at 3000°C. As a result, even when baking at 2000°C to accelerate reaction of boronization, a compact of boron thus obtained has satisfiable physical property to be qualified as a C/C material. In the meantime, any boron compound can be employed as a boron compoment to be impregnated into carbon material for achieving the object of the invention as far as the boron compound can be transformed into a solution by thermal melting or by solvent. However, any boron compound which leaves mineral impurities after being baked together with carbon material is not desirable because of inviting pollution of carbon material eventually resulting in restriction on the use. In other words, desirable is a compound which is either thermally decomposed by baking or decomposedly volatized by reaction with carbon leaving boron alone. From this viewpoint, it may be said that organic compound containing boron, boron halide, etc. are desirable. But from the viewpoints of economy and easy handling, boron oxide (B₂O₃) and hydrate compound such as H₃BO₃ ortho-boric acid can be said most suitable. For example, with regard to chemical reaction between B₂O₃ and carbon, a following baking reaction of B₄C is well known: 2B₂O₃+7C→B₄C+6CO It is, however, not always clear whether or not reaction of composite material (carbon-boron), which has been produced in such a manner that B₂O₃ of molecule size in a large amount of carbon as is done in the invention, follows exactly and smoothly the above mentioned reaction formula. In this respect, as a result of various analyses on the composite material obtained by the method shown in the later-described Example 1, 4% by weight of boron component (free B₂O₃ 0.02%) were measured depending upon chemical analysis. Further, as a result of observation by X-ray analysis, a peak value showing the existence of B₄C was not found despite that the fact of neutron absorption by the boron component was clearly recognized as a result of neutron irradiation. There was no other peak showing any other crystal system, though large broad parts were shown, hence it seems that the composite material is in an indefinite form or in a form of solid solution. Accordingly, it is supposed that final product obtained is not in a definite form showing a specific compound of B₄C, but is in a form of solid solution of (BxCy+C), though the present invention is not restricted to the form of such solid solution. Boron oxide (B₂O₃) as well as hydrate thereof can be used as the boron component in the invention. Boric acid (H₃BO₃, B(OH)₃) is one of such desirable hydrates, for example. The mentioned boric acid has a relatively low melting point (185°C) as compared with boron oxide (B₂O₃). Under the temperature higher than the mentioned, boric acid is decomposed while emitting H₂O, and transformed into a solid solution (B₂O₃· n H₃BO₃) to be kept in a state like a liquid. In this manner, when employing a boric acid as a starting material, the boric acid is kept to a temperature having a moderate viscosity in the container, i.e., at 300 to 500°C while melting boric acid, then a carbon material is dipped therein and forcedly press fitted (compressively inserted) into fine pores of the carbon material. The second step (HIP treatment) following the mentioned first steps (impregnation) can be performed in the same manner as the foregoing B₂O₃. Described hereinafter is an embodiment of the method according to the invention in which the mentioned boron compound and carbon material are employed as starting materials. The boron compound melts by heating and impregnated under pressure in a state of liquid or solution dissolved into an adequate solvent. For example, melting point of B₂O₃ is 450°C under normal pressure, boiling point is 1500°C and liquefied in this temperature range of 450 to 1500°C. Temperature range for the impregnation is 600 to 1400°C, preferably 800 to 1200°C. In the first step, B₂O₃ and carbon material are placed in a pressure container, then the B₂O₃ is press-fitted (compressively injected) in fine pores of the carbon compact by heating (vacuum) method under pressure. In this step, press-fit (compressive injection) of B₂O₃ is completely and easily performed by eliminating, before the press-fitting (compressive injection of) B₂O₃, air existing in the fine pores of the carbon material by temporarily reducing pressure in the container. However, this temporal pressure reduction is not always essential since press-fit pressure is high. The press-fit pressure may be several kg/cm², preferably 50 to 100kg/cm². In the second step, HIP treatment is performed. Even if the carbon material impregnated with boron compound in the first process is heated at 2000°C under normal pressure, the carbon material is hardly boronized. This is because boron compound is evaporated by heating at high temperature, there is no room for solid solution by reaction with the carbon material. The heating in this second process is therefore required to be performed under pressure. For example, employing an inert gas such as Ar to be a medium, the heating should be performed under the pressure of not lower than 100kg/cm² and at a temperature not lower than 1500°C, preferably 100 to 2000kg/cm² and not lower than 2000°C. Boron compound is dissolved, dispersed and fixed to the carbon material by this HIP treatment. The mentioned second step is as essential as the preceding first steps. To get ordinary solid solution of carbon-boron, necessary cutting is performed at this stage to be put on sale in the market. However, with respect to a material possible to be used in a specific use such as neutron absorbent for reactor, it is preferable that residual amount of B₂O₃ is as small as possible. When placing such B₂O₃ in a reactor and used at high temperature, B₂O₃ evaporated is precipitated and solidified at relatively low temperature portions, which may result in a problem, i.e., an obstacle of required reaction otherwise bring about corrosion of metal parts. To meet the situation, following third step may be added to eliminate a small amount of B₂O₃ still remaining in the carbon material. That is, the solid solution obtained through the second process is further treated under the pressure of not higher than 1.33kPa (10Torr), preferably not higher than 0.67kPa (5Torr), and at the temperature of not lower than 1500°C, thereby B₂O₃ being evaporatively eliminated. As a result of carrying out the mentioned treatment, residual amount of B₂O₃ can be decreased to not more than 0.1%. The material obtained by the method according to the present invention having multi-purpose property and versatility is satisfiably applicable to almost all use as superior reactor materials including oxidation resistant consumables, neutron absorbent, or as wall material facing to plasma in reactor, materials for aerospace industry, parts for metallurgy and machinery. Furthermore, the composite material obtained according to the invention performing very excellent neutron absorption, oxidation resistance as compared with the conventional composite materials can be employed not only as neutron absorbent, crucible for molten metal, stirring bar, liquid level detection probe, nozzle for continuous casting, die for hot press, etc. but also in following uses; (1) die for continuous casting; (2) heating element; (3) jigs such as stirring bar for molten metal, sensor probe: (4) graphite for reactor (composite material containing B is not applicable as reactor core material for use in high temperature gas furnace); (5) bearings used at high temperature; (6) crucibles; (7) casting molds for hot press; (8) high jigs including post chips; and (9) carbon material for hermetic seal In the composite material thus obtained according to the invention, boron is evently diffused or distributed in carbon. Further, carbon compact trhereof can be selective among any kind including C/C material, high density graphite, etc. and any shape. In effect, it may be said that a carbon boron composite material having never been obtained according to the prior art can be now obtained in the invention. BRIEF DESCRIPTION OF THE DRAWINGS Figures 1 and 2 are schematic explanatory views prepared both based on photographs taken by exposure to neutron irradiation; Figure 3 is a graph showing percentage of oxidation exhaustion of various carbon materials; Figure 4 is a schematic view for explaining a manner of simulation test on a crucible for use in glass molding; Figure 5 is a schematic view for explaining a manner of durability test on a heating element; and Figure 6 is a schematic view for explaining a manner of durabiliuty test on a cylinder; DESCRIPTION OF PREFERRED EMBODIMENT Example 1: (First steps) An isotropic graphite ("IG-11" produced by Toyo Tanso) was dipped in B₂O₃(extra fine grade reagent) dissolved at 1200°C using autoclave, then a pressure of 150kg/cm² was applied to the dipped graphite using N₂ gas, thereby B₂O₃ being impregnated into pores of the graphite. (Second step) After completing the impregnation process, boron was diffused in the graphite by means of a HIP treatment device at a temperature of 2000°C and under a pressure of 2000kg/cm² for 1 hour (employing Ar as pressure medium), thus a solid solution of graphite being obtained. In this respect, for carrying out the HIP treatment, the product to be treated was put in a cylindrical sheath of graphite on which a cap was applied. (Third step) Thereafter, using a vacuum container, a vacuum treatment was performed at 2000°C under 0.13kPa (1Torr) for 1 hour. Boron concentration of the obtained composite material was measured by mannitol method by which it was recognized that the boron concentration was 4.0% by weight (with respect to boron element), among which B₂O₃ was 0.02% by weight. This means that almost all of B₂O₃ not reacted was evaporated and eliminated. Example 2: The carbon-boron composite material obtained through Example 1 was further treated by repeating the same manner as Example 1. Boron concentration of the boron composite material thus obtained was 7% by weight, among which B₂O₃ was 0.03% by weight. As apparent from the above description, it was acknowledged that content of boron in the composite material was increased. Example 3: A plain weave cloth of PAB high strength carbon material (3000 filaments, 7um in fiber diameter, 300kg/mm² in tensile strength) was impregnated with a phenolic resin solution (prepared by diluting a resol type phenolic resin with methanol to 1/2 to 1/3), and after drying it for 24 hours, prepreg sheet was obtained. This prepeg sheet was laminated in a dryer, heat-treated (at 100°C for 0.5 hours), then placed on a die and treated by holding it in an hydraulic press at 140°C under 50kg/cm₂ for 1 hour. Thus, a 2D compact comprising two sheets of laminate where obtained. The compact thus obtained was inserted into coke powder and heat-treated up to 1000°C under non-oxidation atmosphere at a temperature increasing speed of 10°C/hour, then further treated using a vacuum furnace up to a high temperature of 2000°C under a reduced pressure of 0.67kPa (5Torr) at a temperature increasing speed of 100°C/hour. As a result, a 2D C/C composite material free from crack was obtained. A solution prepared by adding 1 part by weight of H₂O to 1 part by weight of orthoboric acid (H₃BO₃) was added to the mentioned 2D C/C composite material to be dipped and impregnated thereinto. H₂O of the Composite material was then evaporated in a dryer kept at 120°C. Thereafter, another impregnation treatment with an aqueous solution was further carried out. It was recognized that the aqueous solution obtained was relatively low in viscosity and impregnated easily into deep portion through the gap and fine pores. After completing the mentioned first step (impregnation treatment), the second step was carried out on the same conditions as the foregoing Example 1, and a carbon-boron composite material mainly comprising of a matrix of C/C composite material was obtained. Boron concentration of the product thus obtained was 3.7% by weight (value converted to boron element). Example 4: A mesophase spherical carbon ("KMFC" produced by Kawasaki Steel Corp.) was ground to fine particles of not larger than 5 m in average grain size. After thermocompressive molding, the fine particles were baked at 2500 to 3000°C, and using the obtained highly pure ultrafine isotropic graphite material (hereinafter referred to as ISO-880), a reaction of boronization was performed in the same manner as that of Example 1. This carbon matrix was a carbon material of high strength and of which fine particle's capacity is small. This as a result of performing a boronization in the same manner as the foregoing Example 1, it was recognized that concentration of boron in the obtained C-B composite material was 2.6% (by weight) and residual amount of B₂O₃ after the third treatment was not more than 0.01%. In addition, Table 1 shows values obtained by analyzing the ISO-880 material and the elements other than boron after the reaction of boronization. Element Al As B Be Bi Ca Cd Ce Purity level ISO-880 <0.3 - - - - - - - ISO-880+B <0.3 - (*) - - - - - Element Cr Cu Fe Ga Ge Hg In K Purity level ISO-880 - - <1.0 - - - - - ISO-880+B - - <1.0 - - - - - Element Li Mg Mn Ni P Pb Si Sn Ti Purity level ISO-880 - <0.1 - - - - <0.1 - - ISO-880+B - <0.1 - - - <0.1 - - Though ordinary carbon material usually contains about 400ppm of impurities, this impurity value can be decreased to not more than 10ppm by halogenation treatment at high temperature (as disclosed in the Japanese Laid-Open Patent Publication (unexamined) No.63-79759), and it is further possible to reduce total quantity of ash to 1 to 2ppm when required. It may be said that the ISO-880 in this example is a material obtained by eliminating impurities beforehand using the halogenation treatment disclosed in the Japanese Patent Publication No.63-79759, for example. Atomic absorption analysis and bright line spectrum analysis or the like were adopted together as analysis method. In the table, (-) indicates elements not detected. As is explicit from the result of analysis of impurity amount before and after the treatment of boronization, increase of elements other than boron is not found. Example 5: A test sample was prepared employing IG-110 as a matrix, said IG-110 being obtained by highly purifying IG-11 serving as carbon material in the same manner as Example 4 (content of boron of this sample was 4.2%). Other test samples were prepared by the methods shown in Examples 1 and 3, and these samples were all subject to neutron irradiation test to acknowledge the manner of diffusion of boron element. For such acknowledgment of diffusion of boron, the inventors took advantage of the property of boron having very high neutron absorption performance. Described hereinafter are results of the mentioned recognition of disperse or diffusion of boron in the test samples with the use of neutron irradiation method. The neutron irradiation test was performed on the test samples prepared in Examples 1 and 3 as well as on the sample prepared according to the prior art. Test samples employed: (Test samples prepared according to prior art): B₄C powder available in the market was ground and those of 3 to 7µm in grain size were selected to be employed as test sample. On the other hand, 50 parts by weight of coke powder (not larger than 15µm in average grain size), 10 parts by weight of artificial graphite powder (not larger than 40µm in average grain size) and 40 parts by weight of pitch were admixed together and kneaded while heating (at 230°C for 2 hours), then molded and fine ground. Thereafter 7.7 parts by weight of the mentioned B₄C particles were added to 100 parts by weight of the product obtained by the mentioned fine grinding, then heated and kneaded together with a small amount of caking agent. The kneaded product was further molded under pressure, and baked at 2000°C, thereby a test sample being obtained. As a result of chemical analysis, content of boron was 4.2% by weight (Value converted to pure boron element). Each of the three test samples obtained as described above were then cut to be a thin plate of 2mm in thickness, and subject to neutron irradiation test on the following manner: Neutron irradiation testing device: Neutron Radiography produced by Sumiju Test & Inspection. Beam irradiation quantity: 34.4µA 4653 sec (160.0m Cb) Neutron irradiation method: Each test sample was put on a dry plate and irradiated with neutron. Portions where neutron was absorbed became white, while portions where neutron was not absorbed were blackened by exposure. Test result: Figures 1 to 2 show test results. These drawings are schematic explanatory views illustrated based on photos taken by exposure to neutron irradiation. As for the product according to the prior art, boron compound was found existing in the form of B₄C fine particles, and portions where neutron was absorbed remained in the form of white spots as unexposed parts. On the other hand, portions without boron (i.e., irradiated by neutron) remained blackened by exposure. The drawings show the mentioned spots of 10 magnifications to clearly show them. In the case of Example 1, it is recognized that boron component are very finely and evenly diffused. No white spot is found no matter how enlarging the original photo picture. Accordingly, the exposure resulted in showing an even intermediate color between white and black on all over the picture in the drawings, and no white spot was found being different from Figure 1. As mentioned above referring to Figure 1, despite that 4% boron compound existed actually, no portion of white dots showing absorption of boron was presented. This means that boron was diffused in the form of very fine particles. In the case of Example 3, boron was impregnated into a carbon-carbon composite material. Though no result of analysis in the form of photogragh was prepared, it is understood that boron is ultrafinely distributed evenly throughout the entire test sample. As is understood from the above-discussed comparison between the product obtained according to the prior art and that obtained according to the invention, there is a remarkable difference in the aspect of boron disperse or diffusion therebetween. Thus, in the present invention, it is obvious that boron is evenly diffused in such a manner as to be fine in comparison to B₄C particles according to the prior art. Substantially the same results as above were obtained also with regard to Examples 2 and 4. In addition, the C-B composite material wherein boron component is ultra finely diffused has a superior oxidation resistance. Such oxidation resistance is an essential requirement in the event of using a carbon composite under oxidizing atmosphere. In this respect, described hereunder is an example of measurment of oxidation resistance of the test sample prepared by the method according to the invention: Example 6: Oxidation resistance of the following (boron-carbon) composite material prepared by the methods in Examples 1 and 5 was analyzed. Comparative Example 1: The test sample (containing 4.2% of boron) prepared by the method according to prior art (employing B₄C powder: the same one as the mentioned neutron test). Comparative Example 2: The carbon matrix (IG-11) employed at the time of preparing the test sample used in Example 1 (containing 0.0% of boron). Comparative Example 3: The carbon matrix (IG-11) employed at the time of preparing the test sample used in Example 1 and further highly purified by hologenation method (IG-110) (containing 0.0% of boron). Each of the above described five test samples was cut to (32x20x12.5mm), then put and left in an air bath heater kept at 700°C. Reduction in weight and percentage of oxidation loss of each test sample was measured at appropriate time intervals. Figure 3 shows the results of such measurement: where reference symbols respectively denote followings: A: Example 1 B: Example 5 C: Comparative Example 1 (material according to prior art) D: Comparative Example 2 E: Comparative Example 3 As is clearly seen from Figure 3, in the Example 1 (hereinafter indicated as A in the drawing), oxidation resistance was remarkably improved by impregnation of boron component as compared with Comparative Example 2 (indicated as D) in which matrix (IG-11) before impregnation with boron component was employed. Moreover, it is to be noted that oxidation resistance was remarkably high when boron contents were at the same level, as compared with the product according to the prior method (Comparative Examples 1, C) in which B₄C powder was added. Substantially the same result was recognized through the comparison between Example 5(B) in which treatment of boron addition was applied to a highly purified material and Comparative Example 3. These results seem to come out by the following reason. That is, in the prior method, boron component which is a B₄C powder expected to perform oxidation resistance effect exists partially in the form of grains, and there are more portions without boron component from where oxidation begins. On the other hand, in the present invention, since boron component is very finely distributed throughout the entire part evenly, reaction of oxidation tends to be restrained as a whole. For producing a C-B composite material of the present invention, it is to be noted that boronizing reaction of carbon material according to the method of the invention is featured by accomplishing even and ultra-fine diffusion of boron. A further feature exists in that the boronization is applicable to any kind and shape of carbon material without negatively affecting nature and physical property of object material. In this sense, the foregoing Table 1 shows comparison between physical property before boronization of carbon material employed in the invention and that after boronization thereof. In addition, following Table 2 shows Comparative Example 4. Comparative Example 4: The test sample prepared by the method according to Example 4 and not boronized at all. Comp.Ex.4 ISO-88 Example 4 ISO-88+B Comp.Ex.2 IG-11 Example 1 IG-11+B Bulk specific gravity (g/cm³) 1.90 1.95 1.77 1.86 Bending Strength (kg/cm²) 950 950 400 400 Elastic Coefficient (kg/mm²) 1300 1300 1000 1000 Thermal conductivity (W/mK) 70 70 116 116 It is understood from the above Table 2 that, as a result of applying boronization, neither organization, structure, etc. of the original carbon material nor physical property thereof remains unchanged. Example 7: Simulation test on a crucible for glass molding was carried out. Flat molds (1) shown in Figure 4 were prepared respectively using "IG-11" (Comparative Example 2), Example 1 and the mentioned product according to prior art. Each molten boro-silicate glass (2) is injected into the mold (1) at 1300°C under natural atmosphere, then solidified by natural cooling, and the solidified glass was taken out. This process was repeated to determine durability. In the test, thickness of the mold was made thin for the purpose of obtaining test result in short time, and durability was determined by counting number of repetitions up to destruction of the mold due to repetitions. To be more specific, in the flat mold in Figure 4, "d" is 50⊘mm, "h" is 30mm, and thickness is 3mm. Material Number of times Sample Comp. Example 2 (IG-11) 5 Comp. Example Material by prior method 8 Comp. Example Example 1 (IG-11+B) 15 The invention As is seen from the above table, the carbon material according to the method of the invention exhibited a satisfiable durability as compared with the orginal matrix as a matter of course and with the carbon materials prepared by the prior method. In another test on the same glass to which hermetic seal was applied, the invention was more effective than the product according to the prior art. Example 8: When using a carbon material as a heat element under the atmosphere containing large amount of oxigen, carbon dioxide gas, moisture and the like, there usually arises a problem of deterioration due to oxidation exhaustion. Hence, it is preferable that even heating and partial heating in the heating element are as small as possible. From this viewpoint, the boron-carbon composite material according to the invention in which boron is evenly and finely diffused in graphite matrix is particularly effective. Then, a heating element was prepared of the same material as Example 7, and subject to a deterioration test under the atmosphere using the method illustrated in Figure 5 as follows: Material Hour (h) Sample Comp. Example 2 (IG-11) 0.5 Comp. Example Material by prior method 1 Comp. Example Example 1 (IG-11+B) 2 The invention Measurement conditions: under atmosphere; 800°C measured was a time when electric current value was sharply reduced from normal current value due to imperfect contact at bolted part because of deterioration. It is understood from the above result that the carbon material prepared by the method of the invention has a superior durability also when employed as a heating element. Example 9: Forming a graphite containing boron into a cylinder for use in air hot press and employing an isotropic high density graphite as a punch, a hot press was manufactured, and a test was carried out on the life of cylinder. In this test, Al₂O₃) powder was heat-treated at 1400°C (for 2 hours) under 180kg/cm². Cylinders were respectively prepared using the hot press of the same material as Example 7. Durability of each cylinder was tested by the method shown in Figure 6. Material Number of times Comp. Example 2 (IG-11) 5 Boron material by prior method 8 Example 1 (IG-11+B) (the invention) 15 Referring to Figure 6, lower part of the cylinder (21) was filled with alumina powder (23) interposing a separator(22), and another separator (24) was placed on the alumina powder. Then a pressure was applied by a punch (25) in the direction of the arrow, and number of times of repeated use showing a durability was measured.

Claims: A method for producing a composite material mainly composed of carbon and boron, comprising the steps of: impregnating a carbon material with a liquid boron compound under pressure, and baking such carbon material under inert gas, (a) wherein said carbon material is an isotropic carbon material or a carbon-carbon composite material; (b) wherein the thus impregnated carbon material is heated to a temperature of not lower than 1500°C under a pressure of at least 100kg/cm² by hot isostatic pressure treatment; and (c) wherein said composite material mainly composed of carbon and boron consists substantially of carbon and boron carbide, which takes the form of a solid solution of carbon and boron. A method for producing a composite material according to claim 1, wherein said carbon material is an isotropic carbon material in which total amount of mineral impurities other than boron component is not more than 20ppm. A method for producing a composite material according to claim 1, wherein said carbon material is a carbon-carbon composite material in which total amount of mineral impurities other than boron component is not more than 20ppm. A method for producing a composite material according to claim 1, wherein said liquid boron compound is a molten boron oxide, a melt of boric acid (B(OH)₃ or H₃BO₃) or a solution thereof. A method for producing a composite material according to claim 1, wherein after heat treatment at a temperature of not lower than 1500°C and under a pressure of at least 100kg/cm², reaction system is kept at a temperature of not lower than 1500°C and under a pressure of not higher than 1.33kPa (10Torr). A method for producing a composite material according to claim 5, wherein the amount of residual B₂O₃ is not more than 0.1% by weight. A neutron absorbent comprising a composite material mainly composed of carbon and boron, said composite material being obtained by impregnating a carbon material with a liquid boron compound under pressure, and baking such carbon material under inert gas, (a) wherein said carbon material is an isotropic carbon material or a carbon-carbon composite material; (b) wherein the thus impregnated carbon material is heated to a temperature of not lower than 1500°C under a pressure of at least 100kg/cm² by hot isostatic pressure treatment; and (c) wherein said composite material mainly composed of carbon and boron consists substantially of carbon and boron carbide, which takes the form of a solid solution of carbon and boron. A neutron absorbent comprising a composite material according to claim 7, wherein after heat treatment at a temperature of not lower than 1500°C and under a pressure of at least 100kg/cm², reaction system is kept at a temperature of not lower than 1500°C and under a pressure of not higher than 1.33kPa (10Torr). A neutron absorbent according to claim 8, wherein the amount to residual B₂O₃ is not more than 0.1% by weight. An oxidation resistant carbon material comprising a composite material mainly composed of carbon and boron, said composite material being obtained by impregnating a carbon material with a liquid boron compound under pressure, and baking such carbon material under inert gas; (a) wherein said carbon material is an isotropic carbon material or a carbon-carbon composite material; (b) wherein the thus impregnated carbon material is heated to a temperature of not lower than 1500°C under a pressure of at least 100kg/cm² by hot isostatic pressure treatment; and (c) wherein said composite material mainly composed of carbon and boron consists substantially of carbon and boron carbide, which takes the form of a solid solution of carbon and boron. A jig for use in metal melting apparatus employing said oxidation resistant material according to claim 10. A jig for metal melting apparatus according to claim 11, wherein said jig for use in a metal melting apparatus is a crucible for melting metal, stirring bar for molten metal or probe for measuring the level of melt or solution. A nozzle for use in metal melting apparatus employing said oxidation resistant material according to claim 10. A die for use in hot press employing said oxidation resistant material according to claim 10. A heating element employing said oxidation resistant material according to claim 10.

Inventors: OGURA HIROAKI, OKADA OSAMU, SOGABE TOSHIAKI, OGURA, HIROAKI, OKADA, OSAMU, SOGABE, TOSHIAKI, OGURA, HIROAKI, TOYO TANSO CO., LTD., OKADA, OSAMU, TOYO TANSO CO., LTD., SOGABE, TOSHIAKI, TOYO TANSO CO., LTD.
Applicants: TOYO TANSO CO, TOYO TANSO CO., LTD.
Application year: 1991
Main classification: C01B31
IPC codes: C04B35