Process for the removal of N vinylcarbazole from poly (N vinylcarbazole)

Abstract: The residual level of N-vinylcarbazole in poly-N-vinylcarbazole has been reduced to an amount less than 25 ppm by treatment of a solution of the poly-N-vinylcarbazole with a strongly acidic compound. The polymer can be recovered in pure form by precipitation of the polymer from solution with a non-solvent.

Description: The present invention is directed to a purification process for the removal of N-vinylcarbazole from poly-N-vinylcarbazole.(hereinafter referred to as "polyvinylcarbazole"). Polyvinylcarbazole has uses as an electrical insulating material, a dielectric in capacitors, and a photoconductive film in the xerographic reproduction process. Polyvinylcarbazole is typically prepared by the free radical polymerization of N-vinylcarbazole. Commercial grade polyvinylcarbazole contains up to six percent residual N-vinylcarbazole. N-vinylcarbazole is a mutagen and suspected carcinogen. Clay has been used to decrease the level of N-vinylcarbazole in the polyvinylcarbazole to below 25 ppm. The use of clay is disadvantageous due to the presence of large amounts of fine particulate matter. The fine particulate matter creates significant backpressure in purification columns and is difficult to remove from the final product. Therefore the problem to be solved by the present invention is to reduce the level of N-vinylcarbazole in the polyvinylcarbazole to below 25 ppm without the disadvantages of the removal method involving the use of clay. We have now found that by dissolving polyvinylcarbazole in a suitable solvent and treating with an effective amount of a strongly acidic compound, preferably selected from sulfonic acids and sulfonated resins, the residual N-vinylcarbazole is reduced to carbazole. By recovery of the polymer by precipitation, filtration and drying, the polymer is obtained in pure form. Certain acids and cationic resins were found to react with N-vinylcarbazole to form carbazole, thereby reducing the content of N-vinylcarbazole from the system. These acids can be used to remove N-vinylcarbazole from polyvinylcarbazole. Commercial grade polyvinylcarbazole, which typically contains from two to six percent N-vinylcarbazole, is dissolved in a suitable solvent at an elevated temperature. Suitable solvents are aromatic hydrocarbons with boiling temperatures above 90 °C such as toluene, xylenes, etc. The preferred solvent is toluene. The preferred temperature range is about 80-90°C. An elevated temperature is not required to convert N-vinylcarbazole to carbazole, however by increasing the temperature the solubility of the polyvinylcarbazole is improved. When treatment with acid is used, the acid is dissolved in a small amount of an organic compound such as isopropanol then added slowly to the polyvinylcarbazole solution. The preferred acids are sulfonic aids. The preferred sulfonic acids are methane sulfonic acid and p-toluene sulfonic acid. The polyvinylcarbazole solution is agitated at an elevated temperature for about 2 to 20 hours.The preferred temperature range is 50-90°C. When treatment with cationic resin is used, the resin is slurried with the solvent of choice used for dissolving the polyvinylcarbazole and placed in a column. The preferred resins are strongly acidic sulfonated resins. The polyvinylcarbazole solution is passed through the column at an elevated temperature. The preferred temperature range is 80-90°C. After the polyvinylcarbazole solution has been treated with the acid, the polyvinylcarbazole may be separated by any of the known methods such as freeze-drying, or precipitation by a non-solvent, preferably methanol. The precipitated polyvinylcarbazole is filtered, washed with methanol, filtered, then dried under vacuum at a maximum temperature of 60°C. The following examples are meant to further illustrate, but not to limit the invention. EXAMPLE 1 In a 250 ml round bottom flask, 7.9 g of commercial grade polyvinylcarbazole (Luvican M-170, by BASF) was dissolved in 92.1 g of toluene by agitating for four hours at 90 °C. The polyvinylcarbazole solution was cooled to 50 °C and maintained at that temperature during the remainder of the process. Next, 0.2 g of p-toluene sulfonic acid was dissolved in 2 g of isopropanol, then added dropwise to the polyvinylcarbazole solution. The solution was agitated for two hours. The polyvinylcarbazole solution was added to a commercial blender containing 1 liter of methanol and agitated at high speed for 1 minute. The precipitated polyvinylcarbazole was vacuum filtered then placed in a flask with 200 ml of methanol and agitated for 10 minutes. The polyvinylcarbazole was then vacuum filtered and dried under vacuum at 60°C for four hours. A white powder was obtained. Analysis by gas chromatography showed the untreated polymer to contain 2.2 % N-vinylcarbazole and 0.09 % carbazole. The treated polymer contained less than 25 ppm N-vinylcarbazole and 0.026 % carbazole. EXAMPLE II In a 2 liter round bottom flask, 79 g of commercial grade polyvinylcarbazole (Luvican M-170, BASF) was dissolved in 921 g of toluene by agitating for 6 hours at 90 °C. A slurry of 60.8 g of Amberlyst 15 Cationic Exchange Resin (supplied by ROHM & HAAS Co.) and 200 ml of toluene was transferred into a jacketed glass column (ID 3.12 cm, bed length 13 cm, bed volume 100 ml). A jacketed 500 ml addtion funnel was mounted on the top of the column. The column and addition funnel were maintained at 80-90°C throughout the process. The excess toluene was drained from the column. The polyvinylcarbazole solution was transferred to the addition funnel and passed through the column at a rate of one bed volume per 10 minutes. The polyvinylcarbazole solution was collected and precipitaded by adding 500 ml of polyvinylcarbazole solution to a commercial blender containing 3 liters of methanol and agitating at high speed for one minute. The precipitate was vacuum filtered then placed in a flask with one liter of methanol and agitated for 10 minutes. The polyvinylcarbazole was then vacuum filtered and dried under vacuum at 60 °C for four hours. A white powder was obtained. Analysis by gas chromatography showed the untreated polymer to contain 2.2 % N-vinylcarbazole and 0.09 % carbazole. The treated polymer before precipitation contained 1.4 % carbazole and no detectable N-vinylcarbazole (< 25 ppm). The treated polymer after precipitation contained 0.08 % carbazole and no detectable N-vinylcarbazole ( < 25 ppm).

Claims: A process for removing N-vinylcarbazole from poly-N-vinylcarbazole comprising dissolving poly-N-vinylcarbazole in a suitable solvent, treating the solution with an effective amount of a strongly acidic compound, and then separating the purified poly-N-vinylcarbazole from the solution. A process according to claim 1, wherein the strongly acidic compound is a sulfonic acid. A process according to any of claims 1 and 2, wherein the strongly acidic compound is selected from methane sulfonic acid and p-toluene sulfonic acid. A process according to claim 1, wherein the strongly acidic compound is a strongly acidic sulfonated resin. A process according to claim 1, wherein the purified poly-N-vinylcarbazole is separated from the solution by precipitating the purified poly-N-vinylcarbazole from the solution by adding a non-solvent, filtering the precipitated poly-N-vinylcarbazole, then drying under vacuum at a maximum temperature of 60°C. A process according to any of claims 1 to 5, wherein the suitable solvent is an aromatic hydrocarbon with a boiling temperature above 90 °C. A process according to any of claims 5 and 6, wherein the non-solvent is methanol.

Inventors: CESKA GARY W, COSTIN C RICHARD, HAZELL THOMAS W, HORGAN JAMES P, CESKA, GARY W., COSTIN, C. RICHARD, HAZELL, THOMAS W., HORGAN, JAMES P.
Applicants: SARTOMER CO INC, SARTOMER COMPANY, INC.
Application year: 1991
Main classification: C08F6
IPC codes: C08F6