Method for producing oxide superconductor

Abstract: A method for producing an oxide superconductor formed according to a chemical composition formula (R 1-x Ca x )(Ba 1-y Sr y )₂Cu₄O₈ and having a transition temperature of 77K or above, comprising the step of causing a reaction between (R 1-x Ca x )(Ba 1-y Sr y )₂Cu₃O 7-z and a Cu material such as CuO, wherein R stands for one or more rare earth elements selected from the group consisting of Y, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm and Yb, and wherein 0.01 ≦ x ≦ 0.25, 0 ≦ y ≦ 0.5, and 0 ≦ z ≦ 1. The advantage of this production method is that this production method does not require a hot static pressing process which takes a long time.

Description: BACKGROUND OF THE INVENTION This invention relates to a method for producing oxide superconductors, and more particularly to a method for producing oxide superconductors, the superconductivity transition temperature (hereafter referred to as Tc) of which is higher than the boiling point of liquid nitrogen (absolute temperature 77K). As an oxide superconductor having a superconductivity transition temperature exceeding the boiling point of liquid nitrogen (e.g. Tc = 80K), RBa₂Cu₄O₈ (R = Y, Nd, Sm, Eu, Gd, Dy, Ho, Er, or Tm) of a three-layer perovskite type crystal structure with double CuO chains is known [Phys. Rev. B., 38, 7347 (1989)]. The crystal structure of this superconductor has been determined as shown in Fig. 1. It is also known that Tc can be raised up to 90K by substituting Ca for a part of Y [Nature, 341, 41 (1989)]. Recently, the present inventor has found that an oxide superconductor substituted with Sr for a part of Ba in the above-mentioned oxide superconductor can have a lesser content of toxic Ba and yet keeps its superconductivity unchanged. The oxide superconductor (Y,Ca)Ba₂Cu₄O₈, in which Ca has been substituted for a part of Y mentioned above, is conventionally produced by the following process. Material powders of the constituent elements are blended to have a predetermined element ratio, and the mixture is calcined and is subjected to a hot static pressing process for about ten hours in a mixed atmosphere of oxygen gas (20%) and argon gas (80%) at 200 MPa (2000 atm). Almost the same process was applied to the oxide super-conductor containing Sr substituted for a part of Ba. The hot static pressing process for a long time, necessary for the above-mentioned production method, is disadvantageous for use in mass production, and it makes oxide superconductors of this system expensive. SUMMARY OF THE INVENTION In order to eliminate the above mentioned disadvantageous process, the production method of the present invention for an oxide superconductor which is expressed by a chemical composition formula (R 1-x Ca x )(Ba 1-y Sr y )₂Cu₄O₈ is characterized most importantly by the step of causing an interaction between a material expressed by (R 1-x Ca x ) (Ba 1-y Sr y )₂Cu₃O 7-z and a Cu material. The above-mentioned Cu material may consist of CuO. It ought to be noted that in the composition formula, R stands for one or more than one kind of rare earth elements selected from the group consisting of Y, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm and Yb, x is in the range from 0.001 to 0.25, y is in the range from 0 to 0.5, and z is in the range from 0 to 1. According to the method of this invention, the hot static pressing process which takes a long time is not required, and therefore, oxide superconductors, which are expressed by the chemical composition formula (R 1-x Ca x )(Ba 1-y Sr y )₂Cu₄O₈, can be produced at low cost. Samples taken from an oxide superconductor produced by this method, in which R is Y, x is 0.1 and y is 0, were found to have a superconductivity transition temperature of about 90K and exhibit substantially the same properties as those produced by the conventional production method. By thermogravimetric analysis, it was confirmed that the oxide superconductor of this invention exists stably with no absorption or discharge of oxygen up to about 900°C. Therefore, oxide superconductors according to this invention do not impair their superconductivity through a sintering process in the final stage of the manufacturing process for a silver sheathed wire. For this reason, the superconductor made by this production method enables to produce a superconducting wire which is stable in superconductivity and which is sintered in high density. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a diagram for explaining a crystal structure of RBa₂Cu₄O₈; Fig. 2 is a powder X-ray diffraction diagram of a sample of a first embodiment of this invention, when R = Y and X = 0.1; Fig. 3 is a resistance versus temperature characteristic diagram of (Y 1-x Ca x )Ba₂Cu₄O₈; and Fig. 4 is a diagram showing results of thermogravimetric analysis (TG) and differential thermal analysis (DTA) of a sample of the first embodiment of this invention, when R = Y and X = 0.1. DESCRIPTION OF THE PREFERRED EMBODIMENTS Fig. 1 shows a basic structure of RBa₂Cu₄O₈, which is the main component of an oxide superconductor according to this invention. In Fig. 1, reference numeral 1 indicates a rare earth element R, 2 indicates Ba, 3 indicates Cu, and 4 indicates O located at inter-sections of line segments. An oxide superconductor of (R 1-x Ca x )Ba₂Cu₄O₈ system according to this invention is a compound derived from this basic structure by substituting Ca for at least a part of Y in this crystal structure having double CuO chains. (R 1-x Ca x ) (Ba 1-y Sr y )₂Cu₄O₈ is a compound obtained by further substituting Sr for a part of Ba in this structure. First Embodiment Powders of Y₂O₃, BaCO₃, CuO, and CaCO₃ of 99.9% purity were mixed to produce mixtures of a chemical composition formula (Y 1-x Ca x )Ba₂Cu₃O 7-z so that x = 0.01, 0.05, 0.1, 0.15, 0.2 and 0.25 respectively. Each of the mixtures was calcined in an atmosphere of oxygen for ten hours at 900°C and 920°C. After calcination, a sample of the mixture was crushed and subjected to powder X-ray diffraction analysis. As a result, it was confirmed that (Y 1-x Ca x )Ba₂Cu₃O 7-z of substantially single phase was obtained in which 0 ≦ z ≦ 1. After the amount of oxygen of this calcined powder was determined by iodometry, according to this value, CuO was mixed into the obtained material by such an amount that the component of the mixture becomes (Y 1-x Ca x )Ba₂Cu₄O₈. After being sufficiently crushed and mixed by a planetary ball mill (using zirconia balls 1 mm in diameter), this mixed powder was formed into a rectangular shape. This formed body was sintered for 50 hours at 850°C in an atmosphere of oxygen gas at 0.1 MPa (1 atm), then required samples were obtained. By powder X-ray diffraction analysis of the crystal phase of the sintered body of (Y 1-x Ca x )Ba₂Cu₄O₈ obtained as described above, it could be confirmed that the main components of every obtained sample has the crystal structure of YBa₂Cu₄O₈ type. A powder X-ray diffraction diagram of a sample at x = 0.10 is shown in Fig. 2. This sample had a single phase of the super-conducting phase of YBa₂Cu₄O₈ type. The superconductivity of those samples was examined by measuring the resistance. Results are shown in Fig. 3 and in Table 1. Fig. 3 shows resistance - temperature characteristics of samples of x = 0.01, 0.05 and 0.10. The Tc in Table 1 is the temperature when the resistivity is 0, obtained from the resistance - temperature characteristics. As evident from Fig. 3 and Table 1, each of oxide superconductor samples of a chemical composition of (Y 1-x Ca x )Ba₂Cu₄O₈, made by the production method according to the first embodiment of this invention, exhibits 90K-class superconductivity transition temperature. This superconductivity transition temperature is higher than the boiling point of liquid nitrogen (77K). Fig. 4 shows results of a thermogravimetric analysis (TG) and a differential thermal analysis (DTA) of a sample of x = 0.1. In Fig. 4, TG(%) indicates the result of thermogravimetric analysis, while DTA(µV) indicates the result of differential thermal analysis. In both analyses, measurements were performed while the samples were heated. As shown in Fig. 4, the samples did not show changes in weight from normal temperature up to the neighborhood of 900°C, but decreased in weight at 900°C. It was ascertained from these findings that the superconductivity exist in stable state without absorption or discharge of oxygen until the samples are heated to a high temperature as high as 900°C. As described above, an oxide superconductor of chemical composition formula of (Y 1-x Ca x )Ba₂Cu₄O₈, made by the production method of the first embodiment, was found to have properties with no difference from those of the samples made by the conventional hot static pressing process for a long time. Second Embodiment In a production method of an oxide superconductor according to a second embodiment of this invention, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm or Yb was substituted for the Y of (Y 1-x Ca x )Ba₂Cu₄O₈, x was fixed at x = 0.1, and samples were made by the same process as in the first embodiment. And, the samples were evaluated in the same respects as in the first embodiment mentioned above, and the evaluation results are shown in Table 2. Consulting Table 2, substitution of any of Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm and Yb for Y as the rare earth element R can achieve the same results as in the first embodiment mentioned above. Third Embodiment In the production method of an oxide superconductor according to a third embodiment of this invention, by having x of (Y 1-x Ca x )(Ba 1-y Sr y )₂Cu₄O₈ fixed at x = 0.1, and y changed to 0.1, 0.2, 0.3, 0.4 and 0.5, samples were produced by the same process as in the first embodiment. The samples were evaluated in the same respects as in the first embodiment, and the evaluation results are presented in Table 3. From this table, it is understood that even if Sr is substituted for a part of Ba when y is in the range up to 0.5, the same results can be obtained as in the first embodiment. Fourth Embodiment In the production method of an oxide superconductor according to a fourth embodiment of this invention, with x of (Y 1-x Ca x )Ba₂Cu₄O₈ fixed at x = 0.1 and by using Cu₂O and Cu metallic powders separately, samples were made by the same process as in the first embodiment. The samples were evaluated in the same respects as in the first embodiment, and the results are shown in Table 4. As evident from Table 4, by using Cu₂O or Cu metallic powder is used as the Cu material instead of CuO, the same results as in the first embodiment can be obtained. Fifth Embodiment In a production method of an oxide superconductor according to a fifth embodiment of this invention, with regard to the chemical composition of (R 1-x Ca x )Ba₂Cu₄O₈, x was fixed at x = 0.1 and R was replaced with a mixture of 50 mol% of Y and 50 mol% of Ho, and samples were prepared by the same process. The samples were evaluated in the same respects as in the first embodiment. Powder X-ray diffraction analysis revealed that the samples have a single phase of YBa₂Cu₄O₈ type. Tc was found to be 90K. From these findings, it was made evident that the same results can be achieved as in the first embodiment. A sample for comparison was made by a production method, which will be described below. Powders of Y₂O₃, BaCO₃, CuO and CaCO₃ of 99.9% purity were mixed to produce a mixture of a chemical composition formula (Y 1-x Ca x )Ba₂Cu₄O₈ so that x = 0.1, and the mixture was calcined in the atmosphere of oxygen at 850°C for 20 hours. After calcined, the mixture was crushed, formed and then sintered at 850°C for 50 hours in the atmosphere of oxygen at 0.1 MPa (1 atm), thus producing a required sample. Powder X-ray diffraction analysis was performed on the sintered sample of a chemical composition formula (Y 0.9 Ca 0.1 )Ba₂Cu₄O₈ to determine its crystal phase, and it was revealed that an intended phase with a crystal structure of YB₂Cu₄O₈ type was not formed at all. As obvious from the above description, in the production methods of oxide superconductor according to the first to fifth embodiments, a hot static pressing process is not required, so that those production methods are advantageous in mass production and contribute to a reduction of cost. Oxide superconductors produced by the methods according to the first to fifth embodiments of this invention have Tc higher than the boiling point of liquid nitrogen, and when made into silver sheathing wires, do not have their superconductivity lessened by the sintering process. Therefore, a superconducting wire stable in superconductivity can be produced relatively easily. In addition, oxide superconductors made by the production methods according to the first to fifth embodiments can be formed into high-density products if a binder is used in high-temperature forming. From conventional oxide superconductors expressed by a chemical composition formula RBa₂Cu₃O₇, the binder cannot be removed at 400°C or higher. On the other hand, from oxide superconductors made by the production methods according to the first to fifth embodiments, the binder can be removed at 900°C or below, a fact which permits high-density forming, and improves a superconducting current density. As has been described, according to the production methods of this invention, it is possible to provide oxide superconductors at low cost, which have a superconductivity transition temperature higher than the boiling point of liquid nitrogen expressed by a chemical composition formula (R 1-x Ca x )(Ba 1-y Sr y )₂Cu₄O₈ (R stands for a one or two or more kinds of rare earth elements selected from among Y, Nd, Sm, Eu, Gd, Dy, Ho, Er, and Tm) and which is stable with no absorption or discharge of oxygen up to high temperature. This invention has been described with reference to the concrete embodiments. This invention is not limited to the embodiments mentioned above. Obviously, many modifications and variations of this invention are possible without departing from the spirit or scope of the invention. For instance, needless to say, this invention can be used for low-temperature electronic apparatuses and their wiring or for electromagnetic shielding, etc.

Claims: A method for producing an oxide superconductor expressed by a chemical composition formula of (R 1-x Ca x )(Ba 1-y Sr y )₂Cu₄O₈, comprising the step of causing a reaction between a material expressed by (R 1-x Ca x )(Ba 1-y Sr y )₂Cu₃O 7-z and a Cu material, wherein R stands for one or more rare earth elements selected from the group consisting of Y, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, and Yb, and wherein 0.001 ≦ x ≦ 0.25, 0 ≦ y ≦ 0.5, and 0 ≦ z ≦ 1. A method for producing an oxide superconductor according to Claim 1, wherein said Cu material is CuO.

Inventors: ICHINOSE ATARU, SUZUKI NUBUO, TANAKA SHOJI, WADA TAKAHIRO, YAEGASHI YUJI, YAMAUCHI HISAO, ICHINOSE, ATARU, SUZUKI, NUBUO, TANAKA, SHOJI, WADA, TAKAHIRO, YAEGASHI, YUJI, YAMAUCHI, HISAO
Applicants: CENTRAL RES INST ELECT, INT SUPERCONDUCTIVITY TECH, MATSUSHITA ELECTRIC IND CO LTD, TOHOKU ELECTRIC POWER CO, TOKYO ELECTRIC POWER CO, CENTRAL RESEARCH INSTITUTE OF ELECTRIC POWER INDUSTRY, INTERNATIONAL SUPERCONDUCTIVITY TECHNOLOGY CENTER, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD., THE TOKYO ELECTRIC POWER CO., INC., TOHOKU ELECTRIC POWER CO., INC.
Application year: 1991
Main classification: C04B35
IPC codes: C04B35, H01L39, C01G1, H01B12, H01B13, C01G3