Quaternary II-VI semiconductor material for photonic device

Abstract: A photonic device includes a substrate and a region comprised of a quaternary Group II-VI material supported by the substrate. Examples of quaternary Group II-VI alloys include Hg, Zn, S and Se; Hg, Zn, Se and Te; Zn, S, Se and Te; Zn, Mn, S and Se; and Hg, Cd, Zn and S. By example, the quaternary material HgZnSSe, which is lattice-matched to ZnSe or GaAs, and the quaternary material HgZnSeTe, which is lattice-matched to ZnTe or GaSb, are employed in the construction of lasers, LEDs and detectors suitable for use over a range of wavelengths. The energy bandgap of the HgZnSSe alloy may be varied to achieve emission over the entire visible spectrum while the HgZnSeTe alloy emits within the spectrum from green to far infrared.

Description: FIELD OF THE INVENTION: This invention relates to photonic devices that include a quaternary Group II-VI alloy. BACKGROUND OF THE INVENTION: In U.S. Patent 3,982,261, issued September 21, 1976, G. Antypas discloses an epitaxial layer of a quaternary III-V alloy of Ga, In, As, and P having constituents proportioned for lattice matching to a substrate having a lattice constant falling within the range of 0.545 nm to 0.605 nm. The constituents of the alloy are proportioned to provide a selected bandgap energy falling within the range of 2.23 to 0.35 eV; corresponding to wavelengths of 0.55 to 3.5 µm. Currently available semiconductor diode lasers that emit in the visible spectrum are typically based on the III-V quaternary InGaAlP. However, the wavelength of these lasers is no shorter than approximately 0.67 µm (red). Currently available light emitting diodes (LEDs) are based on the III-V ternaries GaAlAs or GaAsP. These LEDs readily emit red wavelengths with high brightness and efficiency, but can reach certain yellow and green wavelengths only with relatively low efficiency. This low efficiency at wavelengths shorter than red results because emission at these shorter wavelengths is based on trap-to-band recombination and not band-to-band recombination. As a result, conventional LEDs based on ternary III-V material cannot emit or approach blue wavelengths. Variously colored LEDS have, however, many display applications, particularly in automobiles and airplanes where brightness is important. Short-wavelength semiconductor lasers would be extremely useful in optical data storage systems to increase information density, which is inversely proportional to the square of the optical wavelength. Also, triads of red, green, and blue lasers could be used in large-screen projection for high-definition television (HDTV) systems. A further application of short-wavelength lasers, such as a blue-green laser, is as a signal carrier for underwater communications. Other applications, both commercial and military, are also feasible. Detectors for ultraviolet (UV) and visible radiation are also important applications as are UV and visible focal-plane arrays. For example, UV imaging is important for some surveillance and tracking applications. Visible multicolor imagers competitive with existing high-performance silicon-based Charge Coupled Devices (SiCCDs) are also applications. A photonic device having the features of the first part of claim 1 is known from JP-A-59 172 280. A double heterojunction injection laser having the features of the first part of claim 10 is known from US-A- 3 982 261. It is therefore an object of the invention to provide a photonic device being capable of emission or detection of radiation at a wavelength within the entire visible spectrum and a double heterojunction injection laser having an active region comprised of a Group II-VI quaternary alloy. With the invention a quaternary Group II-VI alloys for use in photonic devices that exhibit direct band-to-band emission within the visible spectrum, a Group II-VI quaternary alloy of Hg, Zn, S, Se that emits within the visible spectrum from violet to red, that is, within a wavelength range of approximately 750 nm to approximately 390 nm, a Group II-VI quaternary alloy of Hg, Zn, Se, Te that emits within the spectrum from green to far-infrared, that is, within a wavelength range of approximately 0.5 µm to approximately 20 µm and a Group II-VI quaternary alloy comprised of Hg, Cd, Zn and S are provided. SUMMARY OF THE INVENTION The foregoing problems are overcome and the objects of the invention are solved with a photonic device and a double heterojunction injection laser having the features of claims 1 and 10. Examples of quaternary Group II-VI material are an alloy of (1) Hg, Zn, S, Se and an alloy of (2) Hg, Zn, Se, Te. The quaternary material HgZnSSe, which is lattice-matched to ZnSe or GaAs, and the quaternary material HgZnSeTe, which is lattice-matched to ZnTe or GaSb, are employed in the construction of photonic devices such as lasers, LEDs and detectors suitable for use over a range of wavelengths. The energy bandgap of the HgZnSSe alloy may be varied to achieve emission over the entire visible spectrum. The HgZnSeTe alloy emits within the spectrum from green to far-infrared. An additional example of quaternary Group II-VI material includes the following. (3) An alloy of Hg, Cd, Zn, and S which is believed to have an energy bandgap that spans the visible spectral range. The photonic devices include a region comprised of a quaternary Group II-VI alloy and a substrate having a characteristic lattice constant and at least one epitaxial layer consisting essentially of a quaternary Group II-VI alloy having a composition selected for substantially lattice matching the epitaxial layer to the substrate. The double heterojunction injection laser includes (1) a substrate; (2) a first cladding layer overlying the substrate and comprising a binary or a ternary Group II-VI material having a first type of electrical conductivity; (3) an active region comprised of a quaternary Group II-VI alloy overlying the first cladding layer; and (4) a second cladding layer overlying the active region and comprising a binary or a ternary Group II-VI material having a second type of electrical conductivity. BRIEF DESCRIPTION OF THE DRAWING The above set forth and other features of the invention will be made more apparent in the ensuing Detailed Description of the Invention when read in conjunction with the attached Drawing, wherein: Fig. 1 is a bandgap energy (E g ) diagram that plots E g against lattice parameter for certain binary II-VI compounds (Hg, Zn)(S, Se) and for GaAs, wherein tie lines indicate linear interpolation for ternary or quaternary alloys of intermediate composition; Fig. 2 is a bandgap energy diagram that plots E g against lattice parameter for certain binary II-VI compounds (Hg, Zn)(Se, Te) and for GaSb, wherein tie lines indicate linear interpolation for ternary or quaternary alloys of intermediate composition; Fig. 3 is a schematic perspective view, not to scale, of a double heterojunction injection laser incorporating quaternary Group II-VI material; and Fig. 4 is a side view, not to scale, of another embodiment of a double heterojunction injection laser that includes a multi-quantum well active layer containing quaternary Group II-VI material. DETAILED DESCRIPTION OF THE INVENTION There are now described quaternary alloys comprised of elements selected from Group II-VI of the Periodic Table of the Elements, referred to herein as Group II-VI material or as II-VI material. These quaternary alloys are shown to be suitable for the fabrication of photonic devices, such as diode lasers and LEDs, having wavelengths spanning the entire visible spectrum from violet to red, as well as infrared wavelengths. These photonic devices function by direct band-to-band recombination rather than by trap-to-band recombination and thus achieve greater efficiencies and brightness than conventional devices. As used herein a photonic device includes those devices that emit, detect, or modify electromagnetic energy. Examples of such devices include lasers, LEDs, photodetectors including arrays of photovoltaic or photoconductive devices, and non-linear optical devices. Fig. 1 is a bandgap energy diagram that plots E g against lattice parameter for binary Group II-VI compounds comprised of (Hg, Zn)(S, Se) and for GaAs. Fig. 2 is a bandgap energy diagram plotting E g against lattice parameter for binary Group II-VI compounds comprised of (Hg, Zn)(Se, Te) and for GaSb. In both Fig. 1 and Fig. 2 the tie lines indicate a linear interpolation of lattice parameter for ternary or quaternary alloys of intermediate composition. As can be seen in the diagrams of Fig. 1 and Fig. 2 the quaternary semiconductor alloys provide for the energy bandgap to be varied while maintaining a constant lattice parameter. Hg (1-x) Zn x S (1-y) Se y is one direct-bandgap quaternary material suitable for photonic applications, Hg (1-x) Zn x S (1-y) Se y having constituents that may be varied for maintaining a constant lattice parameter equal to that of ZnSe or GaAs. A second quaternary alloy of interest is Hg (1-x) Zn x Se (1-y) Te y which spans in energy bandgap the spectrum from green to far infrared, Hg (1-x) Zn x S (1-y) Se y having constituents that may be varied for maintaining a constant lattice parameter equal to that of ZnTe or GaSb. For this latter quaternary alloy GaAs substrates are also suitable for use in that an intermediate ZnTe buffer layer of good quality can be grown on GaAs substrates, as described by W.L. Ahlgren, S.M. Johnson, E.J. Smith, R.P. Ruth, B.C. Johnson, M.H. Kalisher, C.A. Cockrum, T.W. James, and D.L. Arney, in J. Vac. Sci. Technol. A7, 331 (1989). Additional examples of quaternary Group II-VI material include the following. An alloy of Zn, S, Se, and Te having an energy bandgap in the spectral range of yellow to blue at a fixed lattice parameter equal to that of GaAs. This alloy has one cation and three anions and has a compositional formula of ZnS (1-x-y) Se x Te y . A bandgap energy diagram for this alloy is based on the three binary compounds ZnS, ZnSe and ZnTe. An alloy of Zn, Mn, S, and Se having an energy bandgap in the spectral range of blue to ultraviolet at a fixed lattice parameter substantially equal to that of GaAs. However, this alloy is believed to experience changes in lattice structural type with increasing Mn content, which may limit the useful range of energy gaps. This alloy has a compositional formula of Zn (1-x) Mn x S (1-y) Se y . A bandgap energy diagram for this alloy is based upon the four binary compounds ZnS, MnS, ZnSe and MnSe. An alloy of Hg, Cd, Zn, and S believed to span the visible spectral range in energy gap, but is also believed to experience changes in lattice structural type for different compositions. This alloy has one anion and three cations and has a compositional formula of Hg (1-x-y) Cd x Zn y S. A bandgap energy diagram for this alloy is based on the three binary compounds HgS, CdS and ZnS. In the foregoing examples x and y each have a value greater than zero and less than one for determining the constituents of the alloy. The values of x and y are selected for substantially lattice matching the quaternary alloy to the substrate, the values of x and y also determining the emission or absorption wavelength of the alloy. In this regard, and relating specifically to photovoltaic detectors of radiation, the device may be constructed with a p-n junction, a Schottky barrier or an isotype heterojunction. By example, HgS or HgSe forms one side of the junction and Hg (1-x) Zn x S (1-y) Se y the other, creating an n-n isotype heterojunction responsive to radiation having a wavelength determined by the values of x and y. As employed herein a material is considered to be lattice matched to another material, such as a substrate, when the degree of lattice matching is sufficient to reduce an interface dislocation surface density to a value that has a substantially insignificant impact on device performance. A typical value for matching of lattice constants is 0.5%, although the actual value is device and application dependent. Suitable substrate materials include but are not limited to ZnSe, ZnSSe, ZnTe, GaAs, GaSb, InP, Si, sapphire (Al₂O₃) and combinations of these materials, such as ZnSe or GaAs grown upon Si (ZnSe/Si, GaAs/Si) and the aforementioned ZnTe grown upon GaAs (ZnTe/GaAs). A presently preferred method of fabricating the Group II-VI quaternary alloy is by metalorganic chemical vapor deposition (MOCVD), particularly photo-assisted MOCVD, although molecular beam epitaxy (MBE), metalorganic molecular beam epitaxy (MOMBE) and vapour phase epitaxy (VPE) are also suitable. Photo-assisted MOCVD is a presently preferred fabrication process in that it can be accomplished at relatively low temperatures to reduce native point-defect creation in the semiconductor. An important consideration in the fabrication of photonic devices employing wide-energy bandgap material, including quaternary Group II-VI material, is the doping of the material. A recognized difficulty in achieving bipolar doping of binary materials, such as high conductivity p-type ZnSe and/or high conductivity n-type ZnTe, has previously limited application of these and other wide-bandgap Group II-VI materials. A solution to this problem is proposed by Y. Marfaing in Proceedings of NATO Advanced Research Workshop on the Future of Small-Gap Semiconductors, Liége, Belgium, Sept. 5-9, 1988. Marfaing concludes that the generation of non-equilibrium carriers in a semiconductor which is in contact with an external gas phase can bring about a change in the concentration of lattice defects created by exchange between the two phases. If the total concentration of vacancies can be reduced, as described in the article, any compensation process involving vacancies will become less active and will ultimately be suppressed. As a result, a strong electrical activity of doping impurities may be achieved. In this regard, non-equilibrium incorporation processes, including doping under light excitation, is described by Marfaing. In commonly assigned U.S. Patent Appl. S.N. 07/434,642, filed Nov. 9, 1989 and entitled "Reactor For Laser-Assisted Chemical Vapor Deposition", W.L. Ahlgren describes apparatus and method for accomplishing epitaxial layer growth with laser-assisted CVD. The system provides low temperature growth and doping of Group II-VI material from organometallic reactants. To achieve light excitation of the growing layer in a manner suggested by Marfaing a second light beam from an argon ion laser or a HgXe arc lamp is directed perpendicular to a substrate whereon epitaxial layer growth is occurring. Dopants are introduced into the reactor and incorporated into the growing semiconductor layer. By example, for creating p-type ZnSe a preferred dopant is nitrogen. Sodium and lithium may also be suitable although lithium is believed to be interstitial and also to have an unacceptably high diffusion rate. N-type doping of ZnSe may be accomplished with gallium. Another approach to forming p-type ZnSe is described by T. Yasuda, I. Mitsuishi, and H. Kukimoto in an article entitled "Metal-Organic VPE of Low Resistivity p-type ZnSe", Appl. Phys. Lett., Vol. 52, pp. 57-59, (1988). In this approach, Li₃N is used as the dopant and it is presumed that Li on Zn sites (Li Zn ) and nitrogen on Se sites (N Se ) are both active acceptor species. Delta-doped structures based on HgZnSSe and HgZnSeTe are also encompassed by the invention. For example, delta-doping is described in an article by F. Quiang, D. Lee, A.V. Nurmikko, L.A. Kolodziejski, and R.L. Gunshor, Phys. Rev. B 39, 3173 (1989). In general, factors affecting the suitability of dopants include solubility, the mode of incorporation, energy level, and diffusivity. The solubility in a host lattice must exceed the required doping level, for example 10¹⁸ cm⁻³ to 10¹⁹ cm⁻³. The mode of incorporation refers to two features: (a) the defect species corresponding to the dissolved dopant (i.e., interstitial, substitutional on cation site, or substitutional on anion site) and (b), for charged defects, the main compensating, or oppositely charged, defect species. Both of these features are typically dependent on the conditions of preparation, such as temperature and Group II element vapor pressure. A desirable mode of incorporation is for the dopant to result in a unique, preferably substitutional, defect species and to be charge-compensated by a free carrier. The free carrier is an electron in the conduction band for donors or a hole in the valence band for acceptors. The energy level of the dopant is preferably shallow, that is, within a few kT of the appropriate band edge, where k is Boltzmann's constant and T is temperature. If the energy level is too deep, the dopant species will not be ionized at room temperature and thus will not increase the conductivity of the crystal. Finally, the diffusivity of the dopant species should be low, not only at room temperature but also at the growth temperature, so that doping profiles can be established and maintained. Interstitial species, such as lithium referred to above, are generally unsuitable as dopants because they have high diffusion rates. Fig. 3 is a schematic perspective view, not to scale, of a double heterojunction injection laser 10 comprising a substrate 12, a lower cladding layer 14, an active layer 16 comprised of, in accordance with an embodiment of the invention, quaternary Group II-VI material, and an upper cladding layer 18. Electrical terminals coupled to the lower and the upper cladding layers 14 and 18 couple the laser 10 to a source of electrical excitation designated as V⁺ and V⁻. In greater detail the substrate 12 is depicted in a partially cut-away manner and is comprised of, by example, GaAs, although other substrate materials such as those referred to above could be employed. The lower cladding layer 14 has a thickness of approximately one to two microns and is comprised of ZnS (1-y) Se y , the constituents being determined during growth such that the lower cladding layer 14 is lattice matched to the substrate 12. Lower cladding layer 14 is doped during laser-assisted MOCVD deposition with, for example, gallium and is also photo-excited during deposition to reduce the total concentration of vacancies and to thus suppress any compensation process involving vacancies. The n-type doping level of lower cladding layer 14 is approximately 10¹⁸ cm⁻³ to approximately 10¹⁹ cm⁻³. The active layer 16 is substantially homogeneous and is comprised of the Group II-VI quaternary Hg (1-x) Zn x S( 1-y) Se y having a thickness of approximately 0.2 microns. The values of x and y are established during epitaxial growth to adjust the value of Eg to obtain a desired output wavelength within the red to violet spectrum and also to lattice match the active layer 16 to the substrate 12. The active layer 16 may be provided as substantially undoped material or may be relatively lightly doped, relative to the cladding layer 14, at a concentration of approximately 10¹⁵ cm⁻³. The upper cladding layer 18 has a thickness of approximately one to two microns and is also comprised of ZnS (1-y) Se y , the constituents being such that the upper cladding layer 18 is also lattice matched to the substrate 12. Upper cladding layer 18 is doped during laser-assisted MOCVD deposition with, for example, nitrogen and is also photo-excited during deposition to reduce the total concentration of vacancies as previously described. The p-type doping level of the upper cladding layer 18 is, for example, also approximately 10¹⁸ cm⁻³ to approximately 10¹⁹ cm⁻³. As can be seen the laser 10 includes a first heterojunction 14a and a second heterojunction 18a and functions through direct band-to-band recombination as a double heterojunction injection laser having a predetermined output beam (A) wavelength within the red to violet spectrum. Other processing steps such as cleaving and mirroring appropriate surfaces of the laser 10 are accomplished in a conventional manner. Fig. 4 is a side view, not to scale, of another embodiment of a double heterojunction injection laser of Fig. 3. The laser includes a multi-quantum well active layer 16' incorporating quaternary Group II-VI material, the active layer 16' being interposed between cladding layers 14 and 18 as described above. The substrate 12 is not shown in Fig. 4. The active layer 16' includes a plurality of pairs of semiconductor layers 16a and 16b. The layer 16a is comprised of the Group II-VI quaternary Hg (1-x) Zn x S (1-y) Se y and has a thickness on the order of 10 nm. The values of x and y are established during growth to adjust the value of E g to obtain the desired output wavelength within the red to violet spectrum and also to lattice match the layers 16a to the substrate 12. Layer 16b is comprised of ZnSe or ZnSSe and also has a thickness on the order of 10 nm. In addition, ZnSe-HgS and ZnTe-HgSe superlattices are alternatives to homogeneous quaternary alloys as materials for photonic applications. That is, the laser of Fig. 4 is provided with cladding layers as previously described but the active region 16' is comprised of alternating layers of the binary compounds ZnSe-HgS or ZnTe-HgSe. For example, layer 16a is comprised of ZnSe and layer 16b is comprised of HgS. In this case the thickness of the layers 16a and 16b are adjusted during growth to achieve a desired lattice constant for lattice matching to the substrate and also to achieve a desired emission wavelength. Furthermore, multilayer Group II-VI structures including strained-layer superlattices that employ modulation doping are encompassed by the invention. Modulation doping is described in an article by J.W. Han, S. Hwang, Y. Lansari, R.L. Harper, Z. Yang, N.C. Giles, J.W. Cook, Jr., J.F. Schetzina, and S. Sen, Appl. Phys. Lett. 54, 63 (1988). High temperature operation of Group II-VI quaternary alloys is compatible with large energy bandgaps available in Group II-VI material. High-speed devices such as heterojunction FETs also benefit from the low electron effective mass, and hence high mobility, in the narrow-bandgap Group II-VI materials coupled with the large gate-voltage swing made available by use of a wide-bandgap Group II-VI material. In that wide-bandgap II-VI material can be grown epitaxially on GaAs, there is also a potential for fabrication of hybrid II-VI/III-V high-speed device structures. Quaternary alloys of Group II-VI material may also serve as a basis for an integrated optoelectronic circuit technology. In addition to the light emitters and detectors mentioned above, such a technology requires optical switches and interconnects such as waveguides. These components make use of nonlinear optical effects and refractive index control.

Claims: A photonic device including a region comprised of a quaternary Group II-VI alloy and a substrate supporting said region, said substrate having a characteristic lattice constant, and wherein the quaternary Group II-VI alloy has a composition selected for substantially lattice matching said region to said substrate and also for providing said region with an energy bandgap associated with a specific wavelength characterized in that said quaternary Group II-VI alloy contains Hg as one atomic constituent. The photonic device of Claim 1, characterized in that said quaternary Group II-VI alloy is comprised of Hg (1-x) Zn x S (1-y) Se Y , where x and y each have a value greater than zero and less than one. The photonic device of Claim 1, characterized in that said quaternary Group II-VI alloy is comprised of Hg (1-X) Zn X se (1-Y) Te y , where x and y each have a value greater than zero and less than one. The photonic device of Claim 1, characterized in that said quaternary Group II-VI alloy is comprised of Hg (1-x-y) Cd x Zn y S, where x and y each have a value greater than zero and less than one. The photonic device of Claim 4, characterized in that said substrate is comprised of material selected from the group consisting of GaAs and ZnSe. The photonic device of any of the Claims 1 to 4, characterized in that said substrate is comprised of material selected from the group consisting of ZnTe, GaAs, and GaSb and combinations thereof. The photonic device of any of the Claims 1 to 6, characterized in that said region is comprised of a homogeneous epitaxial layer. The photonic device of any of the Claims 1 to 6, characterized in that said region is comprised of a plurality of epitaxial layers arranged as a multilayered structure. The photonic device of any of the Claims 1 to 8, characterized in that said specific wavelength lies within the visible spectrum. A double heterojunction injection laser comprising: a substrate (12); a first cladding layer (14) overlying said substrate (12), said first cladding layer (14) being comprised of a binary or a ternary Group II-VI material having a first type of electrical conductivity; and a second cladding layer (18) being comprised of a binary or ternary Group II-VI material having a second type of electrical conductivity, whereby an active region (16) is provided characterized in that said active region (16) is overlying said first cladding layer (14), said active region (16) being comprised of a quaternary Group II-VI alloy containing Hg as one atomic constituent; and said second cladding layer (18) overlying said active region (16). The double heterojunction injection laser of Claim 10, characterized in that said substrate (12) has a characteristic lattice constant and wherein quaternary Group II-VI alloy is comprised of Hg (1-x) Zn x S (1-y) Se y , where x and y each have a value greater than zero and less than one for lattice matching the active region to said substrate (12) and also for determining the energy bandgap of the quaternary Group II-VI alloy such that the alloy emits electromagnetic radiation having a characteristic wavelength within the range of wavelengths associated with red light to violet light. The double heterojunction injection laser of any of the Claims 10 or 11, characterized in that said active region (16,16') is comprised of a substantially homogeneous epitaxial layer.

Inventors: AHLGREN WILLIAM L, AHLGREN, WILLIAM L.
Applicants: SANTA BARBARA RES CENTER, SANTA BARBARA RESEARCH CENTER
Application year: 1991
Main classification: H01L33
IPC codes: H01S5, H01L31, H01L33