FRICTION PAD FOR DISC BRAKE OF VEHICLE

Abstract: A friction pad for the disc brake of a vehicle. The lining (20) of this friction pad (14) to be in friction-engagement with the brake disc (12) is made of a carbon composite material and a covering layer (21) is made of glass or heat-resistant resin to be spread over the back and sides of the lining (20). Said carbon composite material is preferably carbon-carbon composite or carbon material impregnated with glass. Said glass is preferably borosilicate glass.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a friction pad of a disc brake which is mounted on a vehicle, such as an automobile or a motorcycle. Description of the Related Art In a disc brake for controlling the action of a brake disc by a pair of friction pads, the brake disc is made of cast iron or a steel plate and the friction pads are made of a resin mold. Improvement in durability of the brake disc and the friction pads to a heat crack and fade, and their lightening in weight have been desired. As disclosed in Japanese Unexamined Patent Publication No. 1-320328, for example, a carbon-carbon composite or a carbon-fiber reinforced carbon composite has been proposed as the materials for the brake disc and the friction pads. Carbon fibers impregnated with a carbon matrix are subjected to carbonisation and high densification treatment to provide the carbon-carbon composite. This composite has a great friction coefficient when combined with the same type of a material, and a small friction coefficient in a combination with a different type of a material. The carbon-carbon composite is therefore used for both the brake disc and the friction pads. The carbon-carbon composite has a large friction coefficient in a high temperature range of about 100°C or higher, and has excellent heat resistance, thermal shock resistance, and heat conductivity. This composite however has a great wear by oxidation rate in such a high temperature range, so as to deteriorate the durability of the friction pads and easily transmit heat caused by a braking operation to a hydraulic system. Further, since the carbon-carbon composite is hardly bonded or fusion-bonded to other materials, the entire friction pad is integrally formed of the carbon-carbon composite as disclosed in the Japanese publication (No. 1-320328). This type of friction pads are inferior in rigidity to those provided with metal back plates, and will therefore be deformed by the pressure of a piston, or impart a soft brake feeling to a driver. Also as the carbon-carbon composite has high heat conductivity, an excellent insulator has to be attached to the back surface of the friction pad as a countermeasure for vapor-lock. In this respect, it has been proposed to provide a friction pad which has a back plate of a different material coupled to a carbon-carbon composite lining by rivets or the like. Since a plurality of heavy rivets are used for this friction pad, the total weight of the pad increases even with the use of the carbon-carbon composite. SUMMARY OF THE INVENTION It is therefore an object of the present invention to provide friction pads of a disc brake for a vehicle, which can prevent an oxidative damage, and have excellent heat insulation. A friction pad according to the present invention comprises a lining friction-engageable with a brake disc; and a - coating layer formed on a back surface of the lining and a torque receiving section on a side of the lining. The lining is formed of a carbon composite material, and the coating layer is made of either glass or a heat resistant resin. According to another friction pad embodying the present invention, the coating layer is formed on the side of the lining in addition to the torque receiving section. The carbon composite material for the friction pad of the present invention is preferably a carbon-carbon composite or a glass-impregnated carbon material. The carbon-carbon composite can be provided by subjecting the carbon-matrix impregnated carbon fibers to the carbonization and high densification treatment, as described above. The glass-impregnated carbon material can be yielded by impregnating glass components into the carbon pores of the carbon-carbon composite. Glass for the friction pad of the present invention is desirably borosilicate glass. With the above structure, the friction pads of the present invention have enhanced rigidity and resistance against the pressure from a piston and a retarding torque, providing a good and strong brake feeling to a driver. Further, corrosion of the lining by oxidation can be prevented, improving the durability of the friction pads. The heat resistance of the friction pads is also increased, thus permitting the braking performance of the carbon composite material to be sufficiently and steadily demonstrated. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a cross section of a disc brake according to a first embodiment of the present invention; Fig. 2 is a perspective view of a friction pad; and Fig. 3 is a perspective view of a friction pad according to a second embodiment of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS A first preferred embodiment of the present invention will now be described referring to Figs. 1 and 2. A disc brake 11 comprises a brake disc 12 which rotates together with wheels, a caliper 13 to be provided over the outer surface of the brake disc 12, and a pair of friction pads 14 located face to face on the respective sides of the brake disc. An acting portion 13a and a reacting portion 13b of the caliper 13 are coupled to each other by a bridge 13c. The acting portion 13a has a cylinder bore 15 which opens-toward the brake disc 12. A piston 16 is inserted liquid-tight and slidable into the cylinder bore 15. A hydraulic chamber 17 is defined behind the piston 16. The pair of friction pads 14 hang from hanger pins 18 penetrating through the bridge 13c in the axial direction of the brake disc 12. Further, a pad spring 19, attached inside the bridge 13c, urges the friction pads 14 toward the center of the brake disc 12. The friction pads 14 each include a lining 20 contacting the brake disc 12 with friction, and a coating layer 21 formed on a back surface 20a and the entire side surfaces of the lining 20 and the inner surfaces of through holes for the hanger pins 18. The lining 20 is made of a carbon composite material, and the coating layer 21 is made of glass or a heat resistant resin. A preferable carbon composite material for the lining 20 is a glass-impregnated carbon material, which is obtained by impregnating a resin or a pitch into long and short fibers of carbon or graphite, burning the resultant material for carbonisation, and impregnating glass components into the resultant carbon-carbon composite or carbon pores included in that carbon-carbon composite. The lining 20 is dipped into a solution of glass or a heat resistant resin to be impregnated with that material, or the lining 20 is coated, adhered with pressure, or sprayed with the glass or the heat resistant resin to form the coating layer 21. Borosilicate glass is suitable as the mentioned glass because it is easily impregnated in the carbon-carbon composite and has higher rigidity and lower heat-conductance than the carbon-carbon composite, and is hardly oxidized. The friction pads 14 therefore have enhanced rigidity and strength due to piston abutting surfaces 14a, torque receiving side sections 14b and through holes 14c covered with the coating layer 21 made of glass or a heat resistant resin. Therefore, the piston abutting surfaces 14a and the torque receiving surfaces 14b will not be deformed in the braking operation, providing a stronger and better brake feeling. When braking-originated friction heat raises the temperature to 100°C or above, the brake disc 12 and the friction pads 14 have large and steady friction coefficients, while the coating layer 21 maintains heat retaining property and heat insulation of the friction pads 14. The brake disc 12 and the friction pads 14 can therefore fully demonstrate the braking performance, and block heat transfer to the hydraulic system, thereby preventing vapor locking. Since the coating layer 21 prevents the carbon-carbon composite from contacting air, wear by oxidation, such as falling off of the corners of the lining 20, can also be avoided. As the brake disc 12 has large friction force when the carbon-carbon composites contact each other with friction, the brake disc 12 is preferably made of the same carbon composite material as the lining 20. A second embodiment of the present invention will now be described referring to Fig. 3. A friction pad 31 includes a lining 32 contacting the brake disc 12 with friction, and a coating layer 33 formed on the back surface and torque receiving side sections 32a of the lining 32. The lining 32 and the coating layer 33 are formed of the same materials as used in the first embodiment. The friction pad 31 will therefore have improved strength against the pressure of the piston and the retarding torque as well as improved heat insulation. In this embodiment, the coating layer 33 to be made on the back surface of the friction pad 31 may be formed only on the piston abutting portion.

Claims: A friction pad of a disc brake for a vehicle comprising: a lining (20) formed of a carbon composite material and friction-engageable with a brake disc (12), a torque receiving section on a side of the lining; characterised in that said friction pad further comprises a coating layer (21) made of either glass or a heat resistant resin formed on a back surface of the lining. A friction pad according to claim 1, wherein the coating layer (21) is formed on the sides of the lining in addition to the torque receiving section. A friction pad according to claim 1 or 2, wherein the carbon composite material is a carbon-carbon composite. A friction pad according to claim 1 or 2, wherein the carbon composite material is a glass-impregnated carbon material. A friction pad according to claim 1 or 2, wherein the glass is borosilicate glass.

Inventors: IDESAWA ISAO NISSIN KOGYO KABU, IDESAWA, ISAO NISSIN KOGYO KABUSHIKI KAISHA
Applicants: NISSIN KOGYO KK, NISSIN KOGYO KABUSHIKI KAISHA
Application year: 1991
Main classification: F16D69
IPC codes: F16D65, F16D55, F16D69