Resin composition and use thereof

Abstract: A resin composition which comprises (A) 50 to 99.5 weight % of a saponified ethylene-vinyl acetate copolymer, (B) 0.4 to 50 weight % of a polyolefin resin, and (C) 0.1 to 15 weight % of a graft polymer obtained by grafting an ethylenically unsaturated carboxylic acid or a derivative thereof to a polyolefin resin and reacting the adduct with a polyamide.

Description: BACKGROUND OF THE INVENTION [Industrial Field of Utilization] The present invention provides a saponified ethylene-vinyl acetate copolymer composition markedly improved in long run property in melt-molding and in quality. [Prior Art] Saponified ethylene-vinyl acetate copolymers are excellent in various properties such as oxygen barrier property, and mechanical strength, and therefore have found application in various uses such as film, sheet, container material, and textile fiber. However, since such saponified copolymers are highly hygroscopic, shaped articles based on these materials are disadvantageous in that they undergo marked change in physical properties such as flexibility according to changes in the humidity and temperature of the ambient atmosphere and, in particular, their oxygen barrier property is so highly dependent on humidity that they do not effectively seal off oxygen in a high-humidity environment. Furthermore, because of poor stretchability and flexibility, shaped articles based on this type of copolymer readily undergo uneven stretching in the course of deep-drawing or other molding procedures involving stretching and/or give pinholes in use after molding, imposing limitations on their use as packaging materials. Further, this saponified copolymer gives rise to a variation in product thickness in the molding process for manufacture of film or sheet, with the consequent decrease in the marketability of the product. To cope with these drawbacks, it has been attempted to laminate a water-proof resin material such as a polyolefin film to a saponified ethylene-vinyl acetate copolymer sheet or improve stretchability and flexibility of the molding by incorporating a polyolefin in the saponified copolymer. [Problems which the Invention is to solve] Recent technological innovations and social needs for higher quality shaped articles have emphasized the necessity of developing novel saponified ethylene-vinyl acetate copolymer compositions much more improved than the conventional ones. However, such resin mixtures as mentioned above are inferior in the so-called long run property. When they are used to produce films, sheets and the like shaped articles by melt-molding, for instance, said mixture compositions undergo gelation during molding and/or give, during molding, thermally discolored or carbonized resins (the so-called scorches), which adhere to the extruder inside. Accordingly the melt molding cannot be done continuously for a prolonged period of time. To cope with this problem, the combined use of a hydrotalcite compound or a hydrotalcite solid solution has been proposed as a measure therefor. Adding that, this method does not overcome the drawbacks radically, either. Thus, the compatibility between the saponified ethylene-vinyl acetate copolymer and said polyolefin is not necessarily good enough and despite many efforts to overcome this disadvantage, the results are not as satisfactory as desired. Thus, the prior art technologies are not successful enough to improve the water-resistance, stretchability and flexibility of the saponified ethylene-vinyl acetate copolymer while upholding its inherent characteristics. More specifically, the prior art compositions are often used in the form of laminates with a polyolefin or polyester or the like thermoplastic resin. When exposed to a high-temperature high-humidity atmosphere, the laminates in the form of packaging materials for retortable foods, for instance, often undergo decrease in interlayer adhesion, which may lead to the occurrence rence of the phenomenon of peeling or whitening (blushing). Development of improved compositions is strongly demanded. Further, even if such a laminating procedure is taken, the penetration of moisture from the edge and and corner cannot be precluded, so that the object of the remedial procedure is not fully accomplished. EP-A-0 440 557 describes a resin composition comprising a saponified ethylene-vinyl acetate copolymer, a polyolefin resin, a graft polymer obtained by the reaction of an unsaturated carboxcylic acid with a polyolefin resin and a further reaction with an oligomer of polyamid and an Al-containing hydrotalcite compound. This resin composition is described as being useful for packing. EP-A-0 440 558 describes a resin composition comprising a saponified ethylene-vinyl acetate copolymer, a polyolefin resin, a graft polymer obtained by the reaction of an unsaturated carboxylic acid with a polyolefin resin and a further reaction with an oligomer of polyamid and an hydrotalcite compound containing three metal kations. This resin composition is described as being useful for packing. EP-A-0 444 977 and EP-A-0 440 559 describe a resin composition comprising a saponified ethylene-vinyl acetate copolymer, a polyolefin resin and a graft polymer obtained by the reaction of a carboxylic acid with a polyolefin resin which is further reacted with a polyamide oligomer, whereby the saponified ethylene-vinyl acetate copolymer and the polyolefin resin have a special ratio of their melt flow indices. EP-A-0 440 535 describes a resin composition comprising a saponified ethylene-vinyl acetate copolymer, a polyolefin copolymer having a density of 0.9-0.94 g/cm 3 and a graft polymer obtained by the reaction of an unsaturated carboxylic acid with a polyolefin resin, which is further reacted with a polyamide oligomer. EP-A-0 440 560 describes a process for the production of an article with good shock resistance by mixing a saponified ethylene-vinyl acetate copolymer, an ethylene-propylene copolymer and a graft polymer obtained by the reaction of an unsaturated carboxylic acid with a polyolefin resin, which is further reacted with a polyamide oligomer. The documents EP-A-0 440 557, EP-A-0 440 558, EP-A-0 444 977, EP-A-0 440 559, EP-A-0 440 535 and EP-A-0 440 560 are prior applications in accordance with Article 54(3) EPC. JP-A-62011748 describes a resin composition comprising a propylene-based resin, an ethylene-vinyl alcohol copolymer and a hydrotalcite-type compound. This resin composition is described to have supressed thermal degradation in moulding and giving a reusable scrap composition. GB-A-2185986 describes a process for producing a moulded article comprising a mixture of an olefin resin, which includes residual chlorine due to a Ziegler-type catalyst, a hydrolised ethylene-vinyl acetate copolymer and a hydrotalcite compound. It is described that this process can reduce the gel formation and that the long run processability can be increased. SUMMARY OF THE INVENTION The inventors of the present invention made intensive investigations in an attempt to develop a saponified ethylene-vinyl acetate copolymer composition having excellent long run property, stretchability, film forming property, flexibility, and ensuring higher quality characteristics as compared with the conventional compositions, for example markedly improved interlayer adhesion, among others, even in a high-temperature high-humidity atmosphere, with the oxygen barrier property intrinsic of the saponified copolymer being retained at a high level. As a result, they found that the objects such as mentioned above can be accomplished by a resin composition which comprises (A) 50 to 99,5 weight % of a saponified ethylene-vinyl acetate copolymer with an ethylene content of 20 to 60 mole % with a degree of saponification of its vinyl acetate component being not less than 95 mole %, (B) at least 0.4 weight % of a polyolefin resin having a melt flow rate of 0.01 to 100 g/10 minutes determined at 210°C and under a load of 2160 g according to JIS K-6760, and (C) 0.1 to 15 weight % of a graft polymer obtained by grafting an ethylenically unsaturated carboxylic acid or the corresonding anhydrides or half ester thereof to a polyolefin resin having a degree of polymerization of 350 to 45 000, where the reaction ratio of the polyolefin resin to the ethylenically unsaturated carboxylic acid or the corresonding anhydrides or half ester thereof is 100/0.05 through 100/10 by weight, and reacting the adduct with a polyamide having a degree of polymerization of 100 to 500. In the above composition, it is preferable to be included a hydrotalcite compound (D) or a hydrotalcite solid solution (D') hereinafter described. The present invention has been completed based on the above finding. DETAILED DESCRIPTION OF THE INVENTION The present invention will hereinafter be described in detail, with emphasis placed on such composition and, in particular, on uses for shaped articles based thereon. The saponified ethylene-vinyl acetate copolymer (A) to be employed in accordance with the present invention should have an ethylene content of 20 to 60 mole %, preferably 25 to 55 mole %, with a degree of saponification of its vinyl acetate component being not less than 95 mole %. With an ethylene content less than 20 mole %, the oxygen barrier property under high-humidity conditions is not as high as desired, while an ethylene content in excess of 60 mole % leads to decreases in oxygen barrier property, printability and other physical properties. When the degree of saponification or hydrolysis is less than 95 mole %, the oxygen barrier property and moisture resistance are sacrificed. It should be understood that this saponified copolymer may contain small proportions of other comonomer ingredients including α-olefins such as propylene, isobutene, α-octene, α-dodecene or, α-octadecene, unsaturated carboxylic acids or salts thereof, partial alkyl esters, complete alkyl esters, nitriles, amides and anhydrides and unsaturated sulfonic acids or salts thereof. With regard to the above component (A), its melt flow rate (hereinafter referred to briefly as MFR) M 1 as determined at 210°C and under a load of 2160 g according to JIS K-6760 is suitably in the range of 0.1 to 100 g/10 min, preferably 0.5 to 100 g/min, and more preferably 1 to 60 g/10 min. With regard to the polyolefin resin (B), there may be mentioned linear low-density polyethylene, medium-and high-density polyethylenes, ionomers, ethylene-propylene copolymer, crystalline polypropylene, polybutene or ethylene-vinyl acetate copolymer of comparatively low vinyl acetate content. Particularly, low-, medium- or high-density polyethylene, and isotactic polypropylene are of practical importance. With regard to (B), its melt flow rate M 2 as determined at 210°C and under a load of 2160 g according to JIS K-6760 is in the range of 0.01 to 100 g/10 minutes. For improving the compatibility among the components of the desired resin composition, incorporation of (C) is essential in the practice of the invention. The component (C) is a graft polymer obtained by grafting an ethylenically unsaturated carboxylic acid or the corresponding anhydrides or half ester thereof to a polyolefin resin and reacting this carboxylic acid or the corresponding anhydrides or half ester thereof with a polyamide. This graft polymer is produced by dissolving or suspending a polyolefin resin in an appropriate solvent or putting it in a molten state, activating the polyolefin resin chain with a peroxide or diazo initiator, grafting an ethylenically unsaturated carboxylic acid or the corresponding anhydrides or half ester thereof thereto to give a polymer and mixing this polymer with a polyamide in molten state. For this reaction, Brabender® machine, Buss® blender, single-screw extruder, or Werner® and Pfleiderer® twin-screw extruder is employed. The degree of polymerization of the polyolefin resin to be employed is 350 to 45,000 and preferably 500 to 10,000. The melt flow rate (230°C, load 2160 g; the same applies hereinafter) is about 0.1 to 50 g/10 minutes for all practical purposes. The reaction ratio of the polyolefin resin to the ethylenically unsaturated carboxylic acid or the corresponding anhydrides or half ester thereof is 100/0.05 through 100/10 and preferably 100/0.5 through 100/3 as expressed on the weight basis. If the ratio is 100/less than 0.05, the improving effect on compatibility will not be sufficient. On the other hand, if the ratio is 100/more than 10, the viscosity will be too high for practical molding. The degree of polymerization of said polyamide is 100 to 500, for all practical purposes and the reaction ratio is 0.01 to 1 mole and preferably 0.05 to 0.9 mole per mole of the carboxyl group. As examples of the polyolefin resin, there may be mentioned linear low-density, low-density, medium-density or high-density polyethylene, ionomers, ethylene-propylene copolymer, crystalline polypropylene, polybutene, ethylene-vinyl acetate copolymer or ethylene-propylene copolymer. Important for practical purposes are linear low-density polyethylene, low-density polyethylene, high-density polyethylene, ethylene-propylene copolymer, ethylene-vinyl acetate copolymer and crystalline polypropylene. The ethylenically unsaturated carboxylic acid or the corresponding anhydrides or half ester thereof to be grafted to such a trunk polymer includes unsaturated carboxylic acids such as acrylic acid, methacrylic acid, crotonic acid, maleic acid, fumaric acid and itaconic acid, and the corresponding anhydrides or half esters. The polyamide can be prepared by the known methods such as addition polymerization of a lactam, polycondensation of an aminocarboxylic acid or polycondensation of a diamine with a dicarboxylic acid. Examples of the starting materials for said polyamide are various lactams such as ε-caprolactam, enantholactam, caprylolactam, laurolactam, α-pyrrolidone or α-piperidone, ω-amino acids such as 6-aminocaproic acid, 7-aminoheptanoic acid, 9-amino-nonanoic acid or 11-aminoundecanoic acid, dibasic acids such as adipic acid, glutaric acid, pimellic acid, suberic acid, azelaic acid, sebacic acid, undecadioic acid, dodecadioic acid, hexadecadioic acid, hexadecenedioic acid, eicosadioic acid, eicosadiene-dioic acid, diglycolic acid, 2,2,4-trimethyladipic acid, xylylenedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, terephthalic acid or isophthalic acid, and diamines such as hexamethylenediamine, tetramethylenediamine, nonamethylenediamine, undecamethylenediamine, dodecamethylenediamine, 2,2,4- (or 2,4,4-)trimethylhexamethylenediamine, bis(4,4'-amino-cyclohexyl)methane or metaxylylenediamine. For molecular weight control, a monoamine such as laurylamine or oleylamine can also be used in an appropriate amount. In the composition of the present invention, the proportion of (A) should be 50 to 99.5 weight % and preferably 60 to 95 weight %, that of (B) should be at least 0.4 weight % and preferably 4.5 to 35 weight %, and that of (C) should be 0.1 to 15 weight % and preferably 1.5 to 10 weight %. When the proportion of (A) is less than 50 weight % or that of (B) is over 50 weight %, the oxygen barrier property is adversely affected. Conversely when the proportion of (A) is over 99.5 weight % or that of (B) is less than 0.4 weight %, stretchability and flexibility are sacrificed. When the proportion of (C) is less than 0.1 weight %, the compatibility between (A) and (B) is poor, so that the interlayer adhesion of laminates decreases. Conversely when the proportion of (C) exceeds 15 weight %, long-run moldability is adversely affected. The component (D) to be employed in accordance with the present invention is a hydrotalcite compound representable by the general formula M x Al y (OH) 2x+3y-2z (E) z ·aH 2 O wherein M is Mg, Ca or Zn, E is CO 3 or HPO 4 , x, y and z each independently is a positive number and a is 0 (zero) or a positive number. As typical examples of such compound, there may be mentioned the following: Mg 4·5 Al 2 (OH) 13 CO 3 ·3.5H 2 O, Mg 5 Al 2 (OH) 14 CO 3 ·4H 2 O, Mg 6 Al 2 (OH) 16 CO 3 ·4H 2 O, Mg 8 Al 2 (OH) 20 CO 3 ·5H 2 O, Mg 10 Al 2 (OH) 22 (CO 3 ) 2 ·4H 2 O, Mg 6 Al 2 (OH) 16 HPO 4 ·4H 2 O, Ca 6 Al 2 (OH) 16 CO 3 ·4H 2 O and Zn 6 Al 6 (OH) 16 CO 3 ·4H 2 O. Furthermore, those hydrotalcite compounds derived from Mg 2 Al(OH) 9 ·3H 2 O by partial substitution of the OH groups thereof by CO 3 or HPO 4 which cannot be represented by a definite chemical formula and those modifications of talcite compounds such as mentioned above which are derived therefrom by elimination of water of crystallization (a = 0) are expected to be comparable thereto in effect. In particular, those compounds in which M is Mg and E is CO 3 can show the most remarkable effect. The component (D') to be employed in accordance with the present invention is a hydrotalcite solid solution representable by the general formula [(Ma 2+ ) y1 (Mb 2+ ) y2 ] 1-x M 3+ (OH) 2 A x/n ·mH 2 O wherein Ma 2+ represents at least one metal selected from among Mg, Ca, Sr and Ba, Mb 2+ is a metal selected from among Zn, Cd, Pb and Sn, M 3+ is a trivalent metal, A n- is an anion having a valence of n, and x, y1, y2 and m are respectively positive numbers satisfying the conditions 0 < x ≦ 0.5, 0.5 < y1 < 1, y1 + y2 = 1, and 0 ≦ m < 2. With regard to the above general formula, Ma 2+ is preferably Mg or Ca and Mb 2+ is desirably Zn or Cd. Examples of M 3+ are, Al, Bi, In, Sb, B, Ga and Ti. Among them, Al is suited for practical use. Useful as A n- are CO 3 2- , OH - , HCO 3 - , salicylate ion, citrate ion, tartrate ion, NO 3 - , I - , oxalate ion, [Fe(CN) 6 ] 4- , ClO 4 - , CH 3 COO - or maleate ion. The hydrotalcite solid solution may be surface-treated with e.g. a higher fatty acid, anionic surfactant, silane coupling agent, titanate coupling agent, or glycerin fatty acid ester. Typical examples of (D') are as follows: [Mg 0.75 Zn 0.25 ] 0.67 Al 0.33 (OH) 2 (CO 3 ) 0.165 ·0.45H 2 O [Mg 0.79 Zn 0.21 ] 0.7 Al 0.3 (OH) 2 (CO 3 ) 0.15 [Mg 6/7 Cd 1/7 ] 0.7 Al 0.3 (OH) 2 (CH 3 COO) 0.3 ·0.34H 2 O [Mg 5/7 Pb 2/7 ] 0.7 Al 0.3 (OH) 2 (CO 3 ) 0.15 ·0.52H 2 O [Mg 0.74 Zn 0.26 ] 0.68 Al 0.32 (OH) 2 (CO 3 ) 0.16 [Mg 0.56 Zn 0.44 ] 0.68 Al 0.32 (OH) 2 (CO 3 ) 0.16 ·0.2H 2 O [Mg 0.81 Zn 0.19 ] 0.74 Al 0.26 (OH) 2 (CO 3 ) 0.13 [Mg 0.75 Zn 0.25 ] 0.8 Al 0.2 (OH) 2 (CO 3 ) 0.10 ·0.16H 2 O [Mg 0.71 Zn 0.29 ] 0.7 Al 0.3 (OH) 2 (NO 3 ) 0.30 and [Mg 0.14 Ca 0.57 Zn 0.29 ] 0.7 Al 0.3 (OH) 2.3 ·0.25H 2 O The component (D) or (D') is used in an amount of 0.005 to 5 parts by weight, preferably 0.01 to 1 part by weight, per 100 parts by weight of the sum total of (A) plus (B) plus (C). When the amount of (D) or (D') is smaller than 0.005 part by weight, the long-run moldability is low while films will have decreased transparency, stretchability and flexibility when said amount exceeds 5 parts by weight. The component (D) or (D') may be present in any form in the mixture of (A), (B) and (C). The time of addition of (D) or (D') is not critical. It is advantageous, however, to admix (D) or (D') with the polyolefin resin (B) in advance and then blend the masterbatch-like mixture with the components (A) and (C). While the composition according to the present invention is useful for a variety of applications such as shaped articles, adhesives or coatings, it is most useful for molding purposes and can be molded into pellets, film, sheet, containers, fibers, bars, pipe and other shaped articles by the melt-kneading technique. Such products can be crushed (for reclaiming) or pelleted for re-melt-molding. For melt-molding of the composition, extrusion molding (e.g. T-die extrusion, inflation molding, blow molding, melt spinning or contour extrusion) and injection molding are mostly employed. The melt-molding temperature is selected in many cases from the range of 170 to 270°C. In addition to the above techniques, two-color molding and injection-blow molding techniques may also be employed and shaped articles with good dimensional tolerances can be manufactured. In the molding process, it is of course possible to use two or more different saponified ethylene-vinyl acetate copolymers varying in ethylene content and/or in the degree of saponification in combination. In melt-molding, it is also possible to incorporate, besides the above-mentioned saponified ethylene-vinyl acetate copolymer, suitable amounts of additives such as a plasticizer (for example, a polyhydric alcohol), stabilizer, surfactant, crosslinking agent (for example, an epoxy compound, polyvalent metal salt, inorganic or organic polybasic acid or salt thereof), filler, colorant or reinforcing fiber (for example, glass fiber, and carbon fiber). Any other thermoplastic resin may also be incorporated. Such thermoplastic resin includes, polyolefins other than the component (B) mentioned above (linear low-density, low-density or high-density polyethylene, polypropylene, ethylene-propylene copolymer, ethylene-propylene-diene copolymers, copolymers of ethylene and an alpha-olefin containing 4 or more carbon atoms, ethylene-vinyl acetate copolymer, ethylene-acrylate ester copolymers, ionomers, polybutene, and polypentene ), modified polyolefins obtainable by graft-modification of such polyolefins with unsaturated carboxylic acids or derivatives thereof, polyamides, polyvinyl chloride, polyvinylidene chloride, polyesters, polystyrene, polyacrylonitrile, polyurethanes, polyacetal, polycarbonates or melt-moldable polyvinyl alcohol resin. As mentioned hereinbefore, the composition of the present invention is not only used for the manufacture of a single-layer article solely composed of the composition but also used often as a laminated article including at least one layer of the composition. The layer of the composition of the present invention shows a characteristically high bonding affinity for the layer material to be laminated therewith. In particular, said bonding affinity can be retained at a high level even under high-temperature high-humidity conditions in retorts. In the manufacture of a laminated product according to the invention, in which a different material is laminated to one side or either side of a layer of the composition of the invention, the following laminating methods, for instance, can be employed. Thus, the method which comprises melt-extruding a thermoplastic resin onto a film or sheet of the composition of the invention, the method which comprises melt-extruding the composition of the invention onto a substrate made of a thermoplastic resin or some other material, the method which comprises co-extruding the composition of the invention and a different thermoplastic resin, and the method in which a film or sheet of the composition of the invention is laminated to a film or sheet of a different material with a known adhesive such as an organotitanium compound, an isocyanate compound or a polyester compound can be mentioned. As resins mated with the above composition for co-extrusion, there may be mentioned linear low-density polyethylene, low-density polyethylene, medium-density polyethylene, high-density polyethylene, ethylene-vinyl acetate copolymer, ionomers, ethylene-α-olefin (C 3-20 α-olefin) copolymers, ethylene-acrylic ester copolymers, polypropylene, propylene-α-olefin (C 4-20 α-olefin) copolymers, homo- or copolymers of olefins such as polybutene or polypentene, and polyolefin resins in a broad sense as obtainable by modifying such homopolymers or copolymers of olefins by grafting of an unsaturated carboxylic acid or an ester thereof, polyesters, polyamides, copolymerized polyamides, polyvinyl chloride, polyvinylidene chloride, acrylic resins, styrenic resins, vinyl ester resin, polyester elastomers, polyurethane elastomers, chlorinated polyethylene, and chlorinated polypropylene. A saponified ethylene-vinyl acetate copolymer can also be co-extruded. When a film or sheet or the like shaped article is prepared from the composition of the invention and, then, extrusion-coated with a different material or laminated to a film or sheet of a different material with an adhesive, said different material is not limited to said thermoplastic resins but may be virtually any other material (such as paper, metal foil, uniaxially or biaxially oriented plastic film or sheet, woven fabric, nonwoven fabric, metal filament or wood. The laminar structure of said laminated product is optional. Thus, a layer of the composition of the invention being designated as A (A 1 , A 2 ...) and a layer of a different material, e.g. a thermoplastic resin, being designated as B (B 1 , B 2 , ...), not only a two-layer structure of A/B but a variety of other combinations such as B/A/B, A/B/A, A 1 /A 2 /B, A/B 1 /B 2 , B/A/B or B 2 /B 1 /A/B 1 /B 2 can be employed for a film, sheet or bottle, for instance. In the case of a filament, a bimetal-type, core (A) - sheath (B), core (B) - sheath (A), eccentric core-sheath and other combinations of A and B can be adopted. For co-extrusion, A may be blended with B or vice versa, or for improved interlayer adhesion, a suitable resin may be incorporated in at least one of A and B. The laminated product may be optionally configured. Thus, film, sheet, tape, bottle, pipe, filament, or modified cross-section extrudate may be mentioned. The laminated product may, if necessary, be further subjected to a variety of processings, such as heat treatment, cooling, rolling, printing, dry lamination, solution- or melt-coating, bag production, deep-drawing, box-making, tubing or splitting. The aforementioned shaped articles and laminated products, in particular in the form of film or sheet, can be improved in physical properties by stretching or drafting, if required. In the present invention, the composition is melt-molded into a film material. The thickness of such film is virtually optional and may range from a few micrometers (few microns) to several hundred micrometers (several hundred microns). The term 'film' as used in this specification means a film in the broad sense of the term, thus including a sheet, tape, tube or container . The film obtained in the above manner is conditioned for absorption of moisture or drying, if necessary, and then stretched. This stretching may be uniaxial or biaxial. The effects of the invention are better materialized when the stretching ratio or draft is as high as possible. In the case of uniaxial stretching, the stretching ratio is preferably at least 1.5 times and, for still better results, not less than 2 times. In the case of biaxial stretching, the stretching ratio is preferably not less than 1.5 times, more desirably not less than 2 times and, for still better results, not less than 4 times on the area basis. As to the stretching technique that can be employed, there may be mentioned roll stretching, tenter stretching, tubular stretching and stretching blow processes, as well as high-draft deep drawing or vacuum molding. In the case of biaxial stretching, whichever of concurrent biaxial stretching and serial biaxial stretching can be adopted. The stretching temperature is selected from the range of about 40 to 150°C. After completion of stretching, the product is thermally set. This thermal setting can be effected by the well-known technique. Thus, with the stretched film being held in taut condition, it is heat-treated at a temperature of 50 to 160°C, preferably at 80 to 160°C for about 2 to 600 seconds. The resulting oriented film can be subjected to a variety of processings such as cooling, rolling, printing, dry lamination, solution- or melt-coating, bag-making, deep-drawing, box-making, tubing or splitting. The film, sheet or container obtainable from the composition of the present invention is useful for packaging foodstuffs, pharmaceutical products, industrial chemicals, and agrochemical products. [Effects] The composition according to the invention which comprises (A), (B) and (C) is excellent in long run and film forming property and the shaped articles obtained therefrom are characterized by their markedly improved interlayer adhesion, oxygen barrier property, stretchability and flexibility. EXAMPLES The following examples are further illustrative of the composition of the present invention. In the following description, all parts and % are by weight unless otherwise indicated. Preparation of the samples Saponified ethylene-vinyl acetate copolymer (A) Sample E-1 E-2 E-3 E-4 Ethylene content (mole %) 30 33 40 45 Degree of saponification of vinyl acetate component (mole %) 99.4 99.1 99.6 99.7 Polyolefin resin (B) Sample MFR (g/10 min.) Melting point (°C) P-1 Polypropylene 3 166 P-2 Ethylene-propylene block copolymer (Ethylene content 12%) 5 163 P-3 Ethylene-propylene random copolymer (Ethylene content 3%) 8 165 P-4 Polypropylene 8 166 P-5 Linear low-density polyethylene 4 124 P-6 High-density polyethylene 1.2 134 Hydrotalcite compound (D) H-1: Mg 4·5 Al 2 (OH) 13 CO 3 ·3.5H 2 O H-2: Mg 6 Al 2 (OH) 16 CO 3 ·4H 2 O H-3: Ca 6 Al 2 (OH) 16 CO 3 ·4H 2 O H-4: Zn 6 Al 2 (OH) 16 CO 3 ·4H 2 O Examples 1 through 10 and Comparative Examples 1 and 2 Laminates having the construction shown below were produced using the compositions comprising a combination of (A), (B), (C) and (D) as specified in Table 1. Outer layer (I): Polyamide 6. Intermediate layer (II): Composition according to the invention comprising (A), (B), (C) and (D). Adhesive layer (III): Maleic anhydride-modified ethylene-vinyl acetate copolymer [MFR: 2.1 g/10 minutes (190°C, 2160 g)]. Inner layer (IV): Ethylene-vinyl acetate copolymer with a vinyl acetate content of 10% [MFR: 2 g/10 minutes (190°C, 2160 g)]. Four-layer laminates with layer thicknesses of (I)/(II)/(III)/(IV)=20/10/5/20 micrometers (20/10/5/20 microns). For stretchability testing, films with layer thicknesses 80/40/20/80 micrometers (80/40/20/80 microns) were used. Extrusion molding conditions Extruder: 40 mm-dia. extruder (for inner layer) 40 mm-dia. extruder (for intermediate layer) 30 mm-dia. extruder (for adhesive layer) 40 mm-dia. extruder (for outer layer) Screw: For each, L/C = 2.8; compression ratio = 3.2 Speed of screw revolution: For inner layer : 40 rpm For intermediate layer: 20 rpm For adhesive layer : 20 rpm For outer layer : 40 rpm Die: T-Die with a 4-layer combining adapter Die width: 450 mm Extrusion temperature: Extruders for inner, outer and adhesive layers C 1 = 190°C, C 2 = 200°C, C 3 = 210°C, C 4 = 220°C Extruder for intermediate layer C 1 = 180°C, C 2 = 200°C, C 3 = 220°C, C 4 = 220°C Combining adapter: 210°C T-die : 210°C The results obtained are shown in Table 1. The bond strength was measured after retort treatment (120°C x 30 minutes). The long-run property was evaluated after 96 hours of continuous extrusion molding, followed by disjointing of the extruder, in terms of the state of gel adhesion on the screen mesh as rated on the 5-point scale from 1 (no adhesion) to 5 (adhesion on the whole surface) or the state of adhesion of a scorched or burnt material on the screw surface as rated on the 5-point scale from 1 (no adhesion) to 5 (adhesion on the whole surface). The oxygen permeability was determined with a MOCON Oxtran® 10/50. The stretchability was evaluated in terms of uneven stretching in simultaneous biaxial stretching (3 x 3 times) at 90°C. The film impact strength was determined using a film impact tester (impact head diameter 38.1 mm (3/2 inches), 20°C x 65% RH). The resistance to flexural fatigue was evaluated in terms of the number of bendings until formation of one pinhole (until an abrupt increase in oxygen permeability) with a Gelboflex® tester. Examples 11 through 15 Laminates composed of the five layers mentioned below were produced under the conditions mentioned below. Inner layer (I) and outer layer (V): Linear low-density polyethylene (MFR 1.5 g/10 minutes, density 0.920) Adhesive layers (II) and (IV): Maleic anhydride-modified linear low density polyethylene (MFR 2 g/10 minutes) Intermediate layer (III): Composition according to the invention comprising (A), (B), (C) and (D). Layer Composition and layer thicknesses (micrometers (microns)): (I)/(II)/(III)/(IV)/(V) = 20/5/10/5/20 (20/5/10/5/20) For stretchability testing, the layer thicknesses 80/20/40/20/80 (80/20/40/20/80) were used. Extruder: 40 mm-dia. extruder (for inner and outer layers) 40 mm-dia. extruder (for intermediate layer) 30 mm-dia. extruder (for adhesive layers) Screw: For each, L/D = 28, compression ratio = 3.2 Speed of screw revolution: For inner and outer layers: 65 rpm For intermediate layer: 20 rpm For adhesive layers: 30 rpm. Die: T-Die with a 5-layer combining adapter Die width: 450 mm Extrusion temperature: Extruders for inner, outer and adhesive layers C 1 = 190°C, C 2 = 200°C, C 3 = 210°C, C 4 = 220°C, Extruder for intermediate layer C 1 = 180°C, C 2 = 200°C, C 3 = 220°C, C 4 = 220°C, Combining adapter 210°C T die 210°C The results obtained are shown in Table 2. Examples 16 through 25 and Comparative Examples 3 and 4 Using the following hydrotalcite solid solution, a four layer laminate was produced in the same manner as Examples 1 through 10. The results are set force in Table 3. Hydrotalcite solid solution (D') H'-1: [Mg 0.75 Zn 0.25 ] 0.67 Al 0.33 (OH) 2 (CO 3 ) 0.165 ·0.45H 2 O H'-2:[Mg 6/7 Cd 1/7 ] 0.7 Al 0.3 (OH) 2 (CH 3 COO) 0.3 ·0.34H 2 O H'-4: [Mg 5/7 Pb 2/7 ] 0.7 Al 0.3 (OH) 2 (CO 3 ) 0.15 ·0.52H 2 O Examples 26 through 30 A five-layer laminate was produced in the same manner as Examples 11 through 15. The results are set force in Table 4. Examples 31 through 38 and Comparative Examples 5 to 10 Pellets of the composition of (A), (B) and (C) were mixed in a Henschel® mixer and fed to a T-die extrusion machine for melt-kneading and extrusion from the T-die to produce a 30µm (30 µ)-thick film. (In the evaluation of stretchability, a 180 µm (180 µ)-thick film was used.) The extrusion molding conditions were as follows. Extruder: 40 mm-dia. extruder Screw : Dulmage head type, L/D = 28, CR = 3 Extrusion temperature : 230°C RPM of screw: 40 rpm The data on the film are presented in Table 5. Preparation of the samples Saponified ethylene-vinyl acetate copolymer (A) Sample E-5 E-6 E-7 E-8 Ethylene content (mole %) 30 33 40 45 Degree of saponification of vinyl acetate component (mole %) 99.4 99.1 99.6 99.7 Melt flow rate (g/10 min.) 3.8 5.5 7.2 12.5 Polyolefin resin (B) Sample Density (g/cm 3 ) Melt flow rate (g/10 min.) P-7 Low density polyethylene 0.924 6 P-8 Linear low-density polyethylene 0.920 2.1 P-9 Ethylene-vinyl acetate (15%) 0.934 14 Examples 39 through 43 Outer layer (I): Nylon 6 [MFR : 4 g/10 min. (230°C, 2160 g)] Intermediate layer (II): The composition of (A), (B) and (C) according to the invention Adhesive layer (III): Maleic anhydride-modified ethylene-vinyl acetate copolymer [MFR : 2.5 g/10 min. (190°C and 2160 g)] Inner layer (IV): An ethylene-vinyl acetate(10%) copolymer [MFR : 2 g/10 min. (190°C, 2160 g)] Using the above resin materials, a four-layer laminate of the construction and film thicknesses (µ) (I)/(II)/(III)/(IV) = 20/10/5/20 was fabricated under the following conditions. (In the stretching test, however, a sheet of 80/40/20/80 was used.) Molding conditions Extrusion machines 40 mm-dia. extruder (for inner layer) 40 mm-dia. extruder (for intermediate layer) 30 mm-dia. extruder (for adhesive layer) 40 mm-dia. extruder (for outer layer) Screw: all L/D = 28, compression ratio 3.2 RPM of screw: 40 rpm for inner layer 20 rpm for intermediate layer 20 rpm for adhesive layer 40 rpm for outer layer Die: A T-die with a 4-layer combining adapter Die width: 450 mm Extrusion temperature: Extruders for inner, outer and adhesive layers C 1 = 190°C C 2 = 200°C C 3 = 210°C C 4 = 220°C Extruder for intermediate layer C 1 = 180°C C 2 = 200°C C 3 = 220°C C 4 = 220°C Combining adapter 210°C T-die 210°C The results are set forth in Table 6. Material Blending ratio E/P/G Physical properties Oxygen permeability [cm 3 .20µm/m 2 .d.bar] (cc·20µ/m 2 ·day·atm) Stretchability Impact Strength (kg·cm/mm) Interlayer bond strength (g/15 mm) 25°C x 75% RH Example 39 E-5 P-7 70/20/10 1.2 (1.2) o ○ 160 1000 G-5 40 E-6 P-8 80/12/3 1.0 (1.0) o ○ 135 880 G-6 41 E-7 85/10/5 1.9 (1.9) o ○ 135 840 P-9 G-7 42 E-8 P-7 70/25/5 2.7 (2.7) o ○ 150 890 G-8 43 E-5 P-8 75/15/10 1.1 (1.1) o ○ 170 950 G-5 In the above table, evaluation criteria are as follows: o ○ : Very Good O : Good Δ : Fair × : Bad Examples 44 through 48 Inner layer (I) and outer layer (V): low-density polyethylene (MFR : 2.0 g/10 min.) Adhesive layers (II) and (IV): Maleic anhydride-modified linear low-density polyethylene (MFR : 2 g/10 min.) Intermediate layer (III): The composition of (A), (B) and (C) according to the invention Using the above resin materials, a five-layer laminate of the construction and film thicknesses (µm(µ)) (I)/(II)/(III)/(IV)/(V) = 20/5/10/5/20 (20/5/10/5/20) was fabricated under the following conditions. (In the stretching test, however, a film of 80/20/40/20/80 (µ) was used.) Extrusion machines: 40 mm-dia. extruder (for inner and outer layers) 40 mm-dia. extruder (for intermediate layer) 30 mm-dia. extruder (for adhesive layers) Screw: all L/D = 2.8, compression ratio 3.2 RPM of screw: 65 rpm for inner and outer layers 20 rpm for intermediate layer 30 rpm for adhesive layers Die: A T-die with a 5-layer combining adapter Die width: 1200 mm Extrusion temperature: Extruders for inner, outer and adhesive layers C 1 = 190°C C 2 = 200°C C 3 = 210°C C 4 = 220°C Extruder for intermediate layer C 1 = 180°C C 2 = 200°C C 3 = 220°C C 4 = 220°C Combining adapter 220°C T-die 210°C The results are set forth in Table 7. Material Blending ratio E/P/G Physical properties Oxygen permeability [cm 3 .20µm/m 2 .d.bar] (cc·20µ/m 2 ·day·atm) Stretchability Impact Strength (kg·cm/mm) Interlayer bond strength (g/15 mm) 25°C x 75% RH Example 44 E-5 P-7 72/20/5 1.9 (1.9) o ○ 110 1080 G-5 45 E-6 P-8 85/5/10 1.3 (1.3) o ○ 95 1020 G-6 46 E-7 75/15/10 2.1 (2.1) o ○ 105 950 P-9 G-7 47 E-8 P-7 70/20/10 3.2 (3.2) o ○ 115 990 G-8 48 E-5 P-8 90/5/5 1.1 (1.1) o ○ 90 830 G-5 In the above table, evaluation criteria are as follows: o ○ : Very Good O : Good Δ : Fair × : Bad Examples 49 through 58 and Comparative Examples 11 through 16 Pellets of the composition of (A), (B) and (C) were mixed in a Henschel® mixer and fed to a T-die extrusion machine for melt-kneading and extrusion from the T-die to produce a 20 µm (20 µ)-thick film. (In the evaluation of stretchability, a 180µm (180µ)-thick film was used.) The extrusion molding conditions were as follows. Extruder: 40 mm-dia. extruder Screw : Full-flight type, L/D = 28, CR = 3 Extrusion temperature (°C): C 1 /C 2 /C 3 /C 4 /H/D 1 /D 2 = 170/200/220/220/220/210/210 RPM of screw: 30 rpm The data on the film are presented in Table 8. Preparation of the samples Saponified ethylene-vinyl acetate copolymer (A) Sample E-9 E-10 E-11 E-12 Ethylene content (mole %) 30 33 40 45 Degree of saponification of vinyl acetate component (mole %) 99.8 99.3 99.5 99.6 Melt flow rate (g/10 min.) 2 3.5 15 5 Polyolefin resin (B) Sample MFR (g/10 min.) Melting point (°C) P-11 Polypropylene 7 168 P-12 Ethylene-propylene block copolymer (Ethylene content 12%) 20 160 P-13 Ethylene-propylene random copolymer (Ethylene content 3%) 44 150 P-14 Polypropylene 66 167 P-15 Medium-density polyethylene 50 121 P-16 High-density polyethylene 23 124 Examples 59 through 63 Outer layer (I): Nylon 6® [MFR : 4 g/10 min. (230°C, 2160 g)] Intermediate layer (II): The composition of (A), (B) and (C) according to the invention Adhesive layer (III): Maleic anhydride-modified polypropylene [MFR : 5.7 g/10 min. (230°C and 2160 g)] Inner layer (IV): An ethylene-propylene random copolymer with an ethylene content of 4 mole % [MFR : 8 g/10 min. (230°C, 2160 g)] Using the above resin materials, a four-layer laminate of the construction and film thicknesses (µm(µ)) (I)/(II)/(III)/(IV)=20/10/5/20 (20/10/5/20) was fabricated under the following conditions. (In the stretching test, however, a sheet of 80/40/20/80 (80/40/20/80) was used.) Molding conditions Extrusion machines 60 mm-dia. extruder (for inner layer) 40 mm-dia. extruder (for intermediate layer) 35 mm-dia. extruder (for adhesive layer) 60 mm-dia. extruder (for outer layer) Screw: all L/D = 28, compression ratio 3. RPM of screw: 30 rpm for inner layer 30 rpm for intermediate layer 20 rpm for adhesive layer 30 rpm for outer layer Die: A T-die with a 4-layer combining adapter Die width: 600 mm Extrusion temperature: Extruders for inner, outer and adhesive layers C 1 = 180°C C 2 = 210°C C 3 = 230°C C 4 = 230°C Extruder for intermediate layer C 1 = 180°C C 2 = 200°C C 3 = 220°C C 4 = 220°C Combining adapter 220°C T-die 210°C The results are set forth in Table 9. Examples 64 through 68 Inner layer (I) and outer layer (V): low-density polyethylene [MFR : 16 g/10 min. (190°C, 2160 g)] Adhesive layers (II) and (IV): Maleic anhydride-modified ethylene-vinyl acetate copolymer [MFR : 2 g/10 min. (190°C, 2160 g)] Intermediate layer (III): The composition of (A), (B) and (C) according to the invention Using the above resin materials, a five-layer laminate of the construction and film thicknesses (µm (µ)) (I)/(II)/(III)/(Iv)/(V) = 20/5/10/5/20 (20/5/10/5/20)) was fabricated under the following conditions. (In the stretching test, however, a film of 80/20/40/20/80 (80/20/40/20/80) (µm (µ)) was used.) Extrusion machines: 60 mm-dia. extruder (for inner layer) 40 mm-dia. extruder (for intermediate layer) 40 mm-dia. extruder (for adhesive layers) 60 mm-dia. extruder (for outer layer) Screw: all L/D = 30, compression ratio 2.8 RPM of screw: 50 rpm for inner layer 40 rpm for intermediate layer 40 rpm for adhesive layers 50 rpm for outer layer Die: A T-die with a 5-layer combining adapter Die width: 1200 mm Extrusion temperature: Extruders for inner, outer and adhesive layers C 1 = 170°C C 2 = 200°C C 3 = 220°C C 4 = 220°C Extruder for intermediate layer C 1 = 180°C C 2 = 200°C C 3 = 220°C C 4 = 220°C Combining adapter 220°C T-die 210°C The results are set forth in Table 10.

Claims: A resin composition which comprises (A) 50 to 99,5 weight % of a saponified ethylene-vinyl acetate copolymer with an ethylene content of 20 to 60 mole % with a degree of saponification of its vinyl acetate component being not less than 95 mole %, (B) at least 0.4 weight % of a polyolefin resin having a melt flow rate of 0.01 to 100 g/10 minutes determined at 210°C and under a load of 2160 g according to JIS K-6760, and (C) 0.1 to 15 weight % of a graft polymer obtained by grafting an ethylenically unsaturated carboxylic acid or the corresonding anhydrides or half ester thereof to a polyolefin resin having a degree of polymerization of 350 to 45 000, where the reaction ratio of the polyolefin resin to the ethylenically unsaturated carboxylic acid or the corresponding anhydrides or half ester thereof is 100/0.05 through 100/10 by weight, and reacting the adduct with a polyamide having a degree of polymerization of 100 to 500. The composition of claim 1, further comprising (D) a hydrotalcite compound represented by the general formula M x Al y (OH) 2x+3y-2z (E) z ·aH 2 O wherein M is Mg, Ca or Zn, E is CO 3 or HPO 4 , x, y and z each independently is a positive number and a is 0 (zero) or a positive number. The composition of claim 1, further comprising (D') a hydrotalcite solid solution represented by the general formula [(Ma 2+ ) y1 (Mb 2+ ) y2 ] 1-x M 3+ (OH) 2 A x/n ·mH 2 O wherein Ma 2+ represents at least one metal selected from among Mg, Ca, Sr and Ba, Mb 2+ is a metal selected from among Zn, Cd, Pb and Sn, M 3+ is a trivalent metal, A n - is an anion having a valence of n, and x, y1, y2 and m are respectively positive numbers satisfying the conditions 0 < x ≦ 0.5, 0.5 < yl < 1, y1 + y2 = 1, and 0 ≦ m < 2. A shaped article obtained by melt-molding a composition as claimed in any of claims 1 to 3. A laminated article at least one layer of which is comprised of a composition as claimed in any of claims 1 to 3. A shaped article as claimed in claim 4 or a laminated article as claimed in claim 5 which is at least uniaxially oriented.

Inventors: HONDA HIROYUKI, TAKIDA HIROSHI, UEMURA TOMOYOSHI, HONDA, HIROYUKI, TAKIDA, HIROSHI, UEMURA, TOMOYOSHI
Applicants: NIPPON SYNTHETIC CHEM IND, NIPPON GOHSEI KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1991
Main classification: C08L29
IPC codes: C08L29, B32B27