Ceramic superconductor and method of preparing the same

Abstract: A Bi-Sr-Ca-Cu-O ceramic superconductor contains 0112 phases which are finely dispersed in a 2212-phase matrix with its c-axis oriented perpendicular to a growth direction. A method of preparing a Bi-Sr-Ca-Cu-O ceramic superconductor comprises the steps of growing crystals under conditions satisfying: G/R ≧ 1 and G·R ≧ 10000 where G (K/cm) represents the temperature gradient at a solid-liquid interface and R (mm/h) represents the rate of crystal growth, and annealing the grown crystals in an atmosphere having oxygen partial pressure of at least 0.05 atm. within a temperature range of 800 to 860°C for at least 2 hours.

Description: Ceramic Superconductor and Method of Preparing the Same BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a superconductor of a ceramic superconductive material and a method of preparing the same. Description of the Background Art Ceramic superconductive materials have been recently watched with interest as materials which exhibit higher critical temperatures. In order to obtain a superconductor having a desired configuration from such a ceramic superconductive material, generally employed is a sintering method of press-molding a raw material of ceramic powder and thereafter sintering the same. In such a sintering method, however, it is difficult to obtain a dense superconductor because of voids resulting from compression molding of the powder material, and hence improvement of superconducting properties is restricted. Each of a report by R. S. Feigelson et al., SCIENCE vol. 240, 17 June 1988, pp. 1642 - 1645 and that by G. F. de la Fuente et al., MRS SPRING MEETING, April 1989 discloses a method of preparing a superconductor such as a Bi-Sr-Ca-Cu-O ceramic superconductor or a Bi-Pb-Sr-Ca-Cu-O superconductor in the form of fiber by a laser pedestal growth method. The article of D. Gazit and R.S. Feigelson, Journal of Crystal Growth, Vol. 91 (1988), Amsterdam, pages 318 - 330, also discloses a method of producing high T c Bi-Sr-Ca-Cu-O superconducting fibers by laser-heated pedestal growth. Furthermore, the report of D. Gazit et al., Journal of Crystal Growth, Vol. 98, No. 3, November 1989, Amsterdam, pages 545 - 549, describes the influence of growth rate on the structure and composition of float zone grown Bi₂Sr₂CaCu₂O₈ superconducting fibers. In the conventional method of preparing a Bi-Sr-Ca-Cu-O ceramic superconductor using the laser pedestal growth method, however, the growth rate must be reduced in order to align superconducting phases. Thus, this method has inferior productivity in terms of application to a wire or the like. Further, although a Bi-Sr-Ca-Cu-O ceramic superconductor obtained according to the conventional method attains a high critical current density (J c ) in a zero magnetic field, the critical current density is reduced in a magnetic field. Such a phenomenon causes a significant problem in application to a magnet or the like, which is used in a magnetic field. SUMMARY OF THE INVENTION An object of the present invention is to provide a ceramic superconductor, which exhibits a high critical current density even in a magnetic field, and a method of preparing the same. This object is solved by a ceramic superconductor according to claim 1 and a method of preparing a ceramic superconductor according to claim 2. A Bi-Sr-Ca-Cu-O ceramic superconductor according to the present invention is characterized in that 0112 phases (0112-phase residuals) having a composition of Bi:Sr:Ca:Cu = 0:1:1:2, i.e., the so-called Bi deficient phases, are finely dispersed in a 2212-phase matrix having a composition of Bi:Sr:Ca:Cu = 2:2:1:2, of which c-axis is oriented perpendicular to a growth direction. The 2212-phase matrix preferably has heterogeneous composition distribution around the 0112 phases. The method according to the present invention is adapted to prepare a Bi-Sr-Ca-Cu-O ceramic superconductor by the laser pedestal growth method, and characterized in that crystals are grown under conditions satisfying: G/R ≥ 1 and G·R ≥ 10000 where G (K/cm) represents the temperature gradient at a solid-liquid interface and R (mm/h) represents the rate of crystal growth, and the grown crystals are annealed in an atmosphere having oxygen partial pressure of at least 5066 Pa (0.05 atm.) within a temperature range of 800 to 860°C, for at least 2 hours. The crystal structure of a Bi-Sr-Ca-Cu-O ceramic superconductor, i.e., the low-temperature superconducting phase of a bismuth based superconductor, has a strong two-dimensionality, and its superconducting properties such as the critical current density are strongly anisotropic due to crystal orientation. Therefore, a high critical current density cannot be obtained unless the crystals are oriented in order along the a-b plane, for example. However, even if a high critical current density is attained by such orientation of the crystals, the low-temperature superconducting phase of the bismuth based superconductor has inferior force of pinning penetrating flux lines as compared with a yttrium based superconductor etc., and its critical current density is significantly reduced in a magnetic field. The inventive ceramic superconductor has such a crystal structure that 0112 phases are finely dispersed in a 2212-phase matrix with its c-axis oriented perpendicular to a growth direction and its critical current density is less reduced in a magnetic field. A Bi-Sr-Ca-Cu-O ceramic superconductor having such a crystal structure can be obtained by growing crystals in a laser pedestal growth method under conditions satisfying: G/R ≥ 1 and G·R ≥ 10000 where G (K/cm) represents the temperature gradient at a solid-liquid interface and R (mm/h) represents the rate of crystal growth, and annealing the grown crystals in an atmosphere having oxygen partial pressure of at least 5066 Pa (0.05 atm.) within a temperature range of 800 to 860°C for at least 2 hours. Fig. 1 is a longitudinally sectional view showing an unannealed state of crystals which are grown according to the inventive method. Referring to Fig. 1, Bi deficient phases 1, which are 0112 phases, are oriented in the growth direction, and other decomposition product phases 2 exist around the Bi deficient phases 1. The Bi deficient phases 1 contain smaller amounts of Bi, while the other decomposition product phases 2 contain larger amounts of Bi in return. Fig. 2 is a longitudinally sectional view showing an annealed state of the crystals which are grown according to the inventive method. The crystals shown in Fig. 1 are annealed under the aforementioned conditions, to attain the crystal structure shown in Fig. 2. 2212 phases 3, which are low-temperature superconducting phases, are grown in the growth direction, while 0112 phases 4, which are residual Bi deficient phases, are finely dispersed in the 2212 phases 3. The 2212 phases 3 are formed by reaction between the Bi deficient phases 1 and the other decomposition product phases 2 shown in Fig. 1. While complete 2212 phases are formed at the interfaces between the Bi deficient phases 1 and the other decomposition product phases 2, those formed in central portions of the Bi deficient phases 1 away from the interfaces have incomplete compositions. Therefore, the 2212 phases 3 contain smaller amounts of Bi in the vicinity of the 0112 phases and larger amounts of Bi around the peripheries of the 2212 phases. Thus, the 2212-phase matrix has heterogeneous composition distribution in the crystal structure of the superconductor prepared according to the inventive method. Such heterogeneous composition distribution is generally called "compositional fluctuation" of 2212 phases. It seems that the inventive superconductor exhibits a high critical current density in a magnetic field since the finely dispersed residual 0112 phases and the composition fluctuation serve as pinning centers for the aforementioned flux lines. Further, since the 2212-phase matrix is oriented in the growth direction, the superconductor readily carries current as a whole and exhibits a high critical current density in a zero magnetic field, while the critical current density is not much reduced but remains at a high level in a magnetic field. Fig. 3 shows critical current densities of crystals, which are grown according to the inventive method, measured in magnetic fields. Even if external magnetic fields are increased, the inventive superconductors exhibit higher critical current densities as compared with conventional superconductors which are in crystal states solidified and oriented directly from molten states, as shown in Fig. 3. Unannealed crystals prepared according to the inventive method are characterized in that Bi deficient phases are oriented in the growth direction. It is possible to obtain a superconductor whose superconducting phases are oriented in a fine crystal structure by annealing such crystals with the Bi deficient phases being oriented in the growth direction. It has been found that orientation of decomposition product phases other than the Bi deficient phases is not much important in the unannealed crystal structure but excellent orientation of the superconducting phases can be attained so far as the Bi deficient phases are oriented. In order to orient the Bi deficient phases, i.e., 0112 phases in the unannealed state, i.e., the as-grown state, the ratio G/R of the temperature gradient G to the growth rate R must be increased. Namely, it is possible to orient the Bi deficient phases by increasing the ratio G/R. In order to obtain the Bi deficient phases as fine structures, further, the product G·R of the temperature gradient G and the growth rate R must be increased, so that a sufficient cooling rate is ensured to obtain the Bi deficient phases as finely oriented structures. If the ratio G/R is less than 1, it is impossible to attain orientation of the Bi deficient phases, or crystal growth itself is disabled. If the product G·R is less than 10000, on the other hand, it is difficult to finely disperse the Bi deficient phases, which are formed as coarse structures. The crystals grown with fine orientation of the Bi deficient phases are annealed under the aforementioned conditions, in order to obtain a superconductor which comprises a low-temperature superconducting phase matrix, i.e., a 2212-phase matrix, and Bi deficient phases, i.e., 0112 phases finely dispersed in the matrix. As to the annealing conditions, the oxygen partial pressure is set to be at least 5066 Pa (0.05 atm.) since the amount of oxygen contained in the low-temperature superconducting phases is reduced and a sufficient critical temperature (T c ) cannot be obtained if the oxygen partial pressure is less than 5066 Pa (0.05 atm.) The annealing temperature is set in a range of 800 to 860°C since formation of the low-temperature superconducting phases will not sufficiently progress if the annealing temperature is less than 800°C, while the crystals are remelted and absolutely changed in structure if the annealing temperature exceeds 860°C. The annealing is performed for at least 2 hours since formation of the low-temperature superconducting phases will not sufficiently progress if the annealing time is less than 2 hours. The superconductor according to the present invention exhibits a high critical current density, which is not much reduced but remains at a high level even in a magnetic field. Therefore, the inventive superconductor can be employed as a wire which is available in a magnetic field, so that the same can be applied to a magnet which is drivable in liquid nitrogen. The foregoing and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a longitudinally sectional view showing an unannealed state of crystals which are grown according to the inventive method; Fig. 2 is a longitudinally sectional view showing an annealed state of the crystals which are grown according to the inventive method; and Fig. 3 illustrates critical current densities of crystals, which are grown according to the inventive method, measured in magnetic fields. DESCRIPTION OF THE PREFERRED EMBODIMENTS Example 1 Raw material bars having a composition of Bi₂Sr₂Ca₁Cu₂O x were employed to grow crystal fibers of 0.4 mm in diameter by a laser pedestal growth method, under conditions of temperature gradients and growth rates shown in Table 1. The as-grown crystals were annealed in an atmosphere under the atmospheric air (oxygen partial pressure: 20265 Pa (0.2 atm)), with annealing conditions shown in Table 1. Mean particle diameters and volume percentages of Bi deficient phases contained in the annealed crystals were evaluated with a transmission electron microscope. Further, critical current densities were measured in liquid nitrogen, under conditions of zero magnetic fields and magnetic fields of 0.05 T (500 G) which were applied perpendicularly to current carrying directions. Table 1 also shows the results. As clearly understood from Table 1, the samples Nos. 1 to 6 prepared according to the inventive method contained fine Bi deficient phases of small mean particle diameters, and exhibited high critical current densities in the magnetic fields of 0.05 T (500 G). On the other hand, the comparative sample No. 7, which was annealed at a lower temperature, contained Bi deficient phases of a large mean particle diameter, and exhibited a low critical current density. The comparative sample No. 8, which was annealed at a higher temperature, was in a multiphase structure, and revealed no superconductivity. The comparative sample No. 9, which had a low product G·R of 5000 below the inventive range, contained Bi deficient phases of a large mean particle diameter, and exhibited a small critical current density. In the comparative sample No. 10 having a ratio G/R of less than 1, it was impossible to attain crystal growth. Example 2 A raw material bar having a composition of Bi₂Sr₂Ca₁Cu₂O x was employed to grow a crystal fiber of 0.5 mm in diameter by a laser pedestal growth method under conditions of a temperature gradient of 1500°C/cm and a growth rate of 300 mm/h. The as-obtained crystal fiber was annealed at 840°C for 50 hours, and its longitudinal section was exposed by polishing, to linearly analyze growth-perpendicular components with an X-ray microanalyzer of 50 Å in beam diameter. In portions of low-temperature superconducting phases, composition fluctuation was recognized in a cycle of 1 µm. The width of this fluctuation was between Bi₂Sr₂Ca 0.1 Cu 1.2 O x and Bi₂Sr₁Ca₁Cu₂O x . The portions of the low-temperature superconducting phases of the crystal fiber were oriented in the growth direction. The crystal fiber exhibited a critical current density of 30,000 A/cm² in a zero magnetic field in liquid nitrogen. When a magnetic field of 0.1 T (1000 G) was applied perpendicularly to the current, the crystal fiber exhibited a critical current density of 18,000 A/cm². The crystal fiber was observed with a transmission electron microscope, and it was confirmed that Bi deficient phases of 0.01 µm in mean particle diameter were finely dispersed in the low-temperature superconducting phase matrix with a volume percentage of 11 %. Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the spirit and scope of the present invention being limited only by the terms of the appended claims.

Claims: A fiber-shaped ceramic superconductor of Bi-Sr-Ca-Cu-O containing 0112-phase residuals being finely dispersed in a 2212-phase matrix with its c-axis oriented perpendicular to the fiber axis, characterized in that said 2212-phase matrix has a compositional fluctuation in the range of Bi₂Sr₂Ca 0,1 Cu 1,2 O x to Bi₂Sr₂Ca₁Cu₂O x and said 0112-phase residuals have a mean particle diameter of 0,005 to 0,3 µm. A method of preparing a ceramic superconductor of Bi-Sr-Ca-Cu-O by a laser pedestal growth method, comprising the steps of: growing crystals under conditions satisfying: G/R ≥ 10 (°C*h/cm²) and G*R ≥ 1000 (°C/h) where G (°C/cm) represents the temperature gradient at the solid-liquid growth interface and R (cm/h) represents the rate of crystal growth; and annealing said grown crystals characterized in that the rate of crystal growth (R) satisfies R ≥ 15 cm/h and the annealing step is carried out within a temperature range of 800°C to 860°C for at least 2 hours in an atmosphere having oxygen partial pressure of at least 5066 Pa (0.05 atm) within said temperature range.

Inventors: HAYASHI KAZUHIKO, HAYASHI, KAZUHIKO, HAYASHI, KAZUHIKO, C/O OSAKA WORKS
Applicants: ENGINEERING RESEARCH ASS FOR S, ENGINEERING RESEARCH ASSOCIATION FOR SUPERCONDUCTIVE GENERATION EQUIPMENT AND MATERIALS
Application year: 1991
Main classification: H01L39
IPC codes: C04B35, H01L39, C30B13, H01B13, C01G29, C01B13, H01B12, C30B29, C01G1