Hydroxyl functionalized polyetheramines as barrier packaging for oxygen-sensitive materials

Abstract: Polyetheramines having improved barrier to oxygen are normally solid, thermoplastic polyethers having aromatic ether/amine repeating units in their backbones and pendent hydroxyl and amido moieties. Such polyetheramines are prepared by reacting diglycidyl ethers of dihydric aromatic compounds such as the diglycidyl ether of bisphenol A with amines having no more than two amine hydrogen such as piperazine or ethanolamine.

Description: This invention relates to thermoplastic polyethers having pendant hydroxyl moieties and to methods of using them as barrier articles to protect oxygen-sensitive materials. Hydroxyphenoxyether polymers are known to be useful in the fabrication of articles exhibiting barrier properties. See, for example, Reinking et al, J. Poly. Sci., Vol. 7, pp. 2135-2144, pp. 2145-2152 and pp. 2153-2160 (1963) and Encyclopedia of Polymer Science and Technology, Vol. 10, pp. 111-122. Such polymers generally have only moderate oxygen barrier, i.e., they generally exhibit oxygen transmission rates of 2 to 75 cm 3 -mil/100 in 2 -atm-day [9 to 337.5 x 10 -8 cc.mm/(m 2 .s.kPa)]. EP-A-327038 provides ungelled thermoplastic resins which are the reaction products of polyamines and polyepoxides. However, these resins have a low molecular weight and cannot therefore be formed into stand-alone products. Rather, they must be combined with at least one layer of a gas-permeable polymeric material, which reduces the barrier properties of products made from the resins. In addition, cross-linking occurs due to the presence of residual unreacted epoxide groups, which results in a thermoset resin which cannot easily be fabricated. In view of the limited barrier properties of the prior art polymers having pendant hydroxyl moieties and phenoxyether moieties, it would be highly desirable to provide a polymer having a high barrier (i.e., oxygen transmission rate less than 5 cm 3 -mil/100 in 2 -atm-day [2.25 x 10 -7 cc.mm/(m 2 .s.kPa)] to oxygen. Polymers that retain such high barrier in both dry and moist environments would be especially desirable. The present invention is, in one aspect, a moldable thermoplastic polyetheramine, having repeating units represented by the formula: wherein each A independently is piperazine, a substituted piperazine, or a group of the formula: in which R 2 is a C 2 -C 10 hydrocarbylene or substituted hydrocarbylene and Z is a C 1 -C 10 hydrocarbylamido, or R 2 is a C 1 -C 10 alkylene or substituted C 1 -C 10 alkylene or phenyl or substituted phenyl and Z is alkoxy, hydroxyalkyl or alkylamino, provided that if R 2 is phenyl or substituted phenyl then hydroxyalkyl is hydroxymethyl. Preferably, the substituent(s) is hydroxymethyl, alkylamido, alkoxy, halo, cyano, amino including alkylamino and dialkyl amino, aryloxy, alkylcarbonyl, and arylcarbonyl, with hydroxymethyl and alkylamido being most preferred. Z is preferably methylamido, hydroxyethyl or hydroxypropyl; R 3 is a C 1 -C 10 hydrocarbylene or a substituted hydrocarbylene, and, preferably, the substituent(s) is alkyl, alkoxy, hydroxymethyl, alkylamido, hydroxyphenyl, and alkoxyphenyl, with ethyl and p-xylyl being most preferred; each R 5 independently is a C 1 -C 10 alkyl or substituted C 1 -C 10 alkyl or phenyl or substituted phenyl, wherein the substituent is hydroxy, hydroxymethyl or alkylamido, with hydroxymethyl and alkylamido being most preferred; each G and B independently is a divalent aromatic moiety and preferably each independently is carbonyldiphenylene, m-phenylene, p-phenylene, sulfonyldiphenylene, p-phenylene, isopropylidenediphenylene, biphenylene, biphenylene oxide, methylenediphenylene, biphenylene sulfide, naphthylene, biphenylenecyanomethane, 3,3'-dialkyldiphenyleneisopropylidene, 3,3',4,4'-tetraalkyldiphenyleneisopropylidene or the corresponding alkyl-substituted derivatives of the above named divalent aromatic moieties wherein the substituent(s) is a monovalent moiety which is inert in the reactions used to prepare the polyetheramine. Most preferably, B is isopropylidenediphenylene or biphenylene; each Y independently is divalent sulfur or (preferably) oxygen; R 1 is hydrogen, a monovalent hydrocarbon or substituted monovalent hydrocarbon and preferably R 1 is hydrogen or methyl; each of V and V' independently is a secondary amine or a tertiary amine and, preferably, each V and V' independently is a secondary amine such as or a tertiary amine such as w is a whole number from 10 to 400; and x is a number sufficiently high that the oxygen transmission rate of the polyetheramine is less than 5 c.c-mil/100 inch 2 -atmosphere (02)-day [2.25 x 10 -7 cc.mm/(m 2 .s.kPa)]. Preferably, x is from 0.2 to 1, and most preferably from 0.5 to 1. Surprisingly, the presence of the A-component in the polyetheramine results in a polymer having thermoplastic character and increased barrier to oxygen in both dry and moist environments. The polyetheramine can be extruded, molded or fabricated by other heat plastifying means to form a variety of barrier articles. In another aspect, this invention is a process for preparing a polyetheramine as described above, comprising reacting a diglycidyl ether of a dihydric phenol with an amine having only two amine hydrogens in an extruder such that the amine moieties of the amine react with the epoxy moieties of diglycidyl ether to form the polyetheramine. The polyetheramines employed in this invention are suitably prepared by contacting one or more of the diglycidyl ethers of a dihydric phenol with an amine having two amine hydrogens and represented by AH 2 wherein A is as previously defined under conditions sufficient to cause the amine moieties to react with epoxy moieties to form a polymer backbone having amine linkages, ether linkages and pendant hydroxyl moieties. In the more preferred embodiments of the second aspect of the invention, the polyetheramine also has pendant amido moieties. Conditions conventionally employed in the reaction of diglycidyl ethers with amines to form amine linkages and pendant hydroxyl groups are suitably employed in preparing the resins of this invention. Examples of such suitable conditions are set forth in US Patent 3,317,471. In general, however, the process for preparing the polymers including the copolymers is carried out so that the unreacted epoxy groups in the finished polyether are minimized. By minimizing the epoxy groups in the polyetheramine, the essential thermoplastic character of the polyetheramine can be retained. Preferred conditions for preparing such resins are set forth in the following working examples. In the preparation of copolymers (i.e., where x in the aforementioned formulae is less than one), a dihydric phenol is employed in addition to the amine. In such copolymerizations while it is possible to subject a mixture of the diglycidyl ether(s), amine(s) and dihydric phenoi(s) to copolymerization conditions, it is sometimes desirable to employ a staged addition procedure wherein the dihydric phenol is added before the amine is introduced or after essentially all of the amine has reacted with the diglycidyl ether. In the preparation of the copolymers wherein the reaction of dihydric phenol with diglycidyl ether is desired, conditions are employed to promote such reactions such as described in U.S. Patent 4,647,648. The diglycidyl ethers of the dihydric phenols are preferably the diglycidyl ethers of bisphenol ketone (sometimes called bisphenol K), bisphenol sulfone, resorcinol, hydroquinone, 4,4'-isopropylidene bisphenol (bisphenol A), 4,4'-dihydroxydiphenylethylmethane, 3,3'-dihydroxydiphenyldiethylmethane, 3,4'-dihydroxydiphenylmethylpropylmethane, bisphenol, 4,4'-dihydroxydiphenyloxide, 4,4'-dihydroxydiphenylcyanomethane, 4,4'-dihydroxybiphenyl, 4,4'-dihydroxybenzophenone, 4,4'-dihydroxydiphenyl sulfide, 4,4'-dihydroxydiphenyl sulfone, 2,6-dihydroxynaphthalene, 1,4'-dihydroxynaphthalene, catechol, 2,2-bis(4-hydroxyphenyl)-acetamide, 2,2-bis(4-hydroxyphenyl)-ethanol, 2,2-bis(4-hydroxyphenyl)-N-methylacetamide, 2,2-bis(4-hydroxyphenyl)-N,N-dimethylacetamide, 3,5-dihydroxyphenylacetamide, 2,4-dihydroxyphenyl-N-(hydroxyethyl)-acetamide, and other dihydric phenols listed in U.S. Patents 3,395,118; 4,438,254 and 4,480,082 as well as mixtures of one or more of such diglycidyl ethers. Of these preferred diglycidyl ethers, those of bisphenol-A, hydroquinone, and resorcinol are more preferred, with the diglycidyl ether of bisphenol-A being most preferred. Examples of preferred amines include piperazine and substituted piperazines, e.g., 2-methylamidopiperazine and dimethylpiperazine; substituted anilines, e.g., 4-methylamido-aniline and 4-methoxyaniline 3,4-dimethoxyaniline; alkanol amines, e.g., 2-aminoethanol and 1-aminopropan-2-ol; and aromatic and aliphatic secondary diamines. Of these preferred amines, 2-aminoethanol is most preferred. Alternatively, the more preferred polyetheramines having pendant alkylamido moieties can be suitably prepared by contacting one or more diglycidyl ethers of a dihydric phenol having an alkylamido substituent with one or more of the aforementioned amines. For the purposes of this invention, the term "barrier polymer" means that the polymer exhibits an oxygen transmission rate which is less than 5, preferably less than 2, most preferably less than 1, cubic centimetres-mil/100 inch 2 -atmosphere-day [2.25x10 -7 , 9x10 -8 , and 4.5x10 -8 cc.mm/(m 2 .s.kPa) respectively]. For the purposes of this invention, "hydrocarbyl" is a monovalent hydrocarbon such as alkyl, cycloalkyl, aralkyl, or aryl and "hydrocarbylene" is a divalent hydrocarbon such as alkylene, cycloalkylene, aralkylene and arylene. In a further aspect, this invention is an article such as a film, bag, tube or a stand-alone container suitable for packaging oxygen-sensitive materials such as foodstuffs and medicines wherein the article is fabricated from a polyetheramine as hereinbefore described. This article can be in the form of a molded container, an impermeable film or a coating or an interior or exterior layer of a laminate or a coextruded container. The barrier articles, e.g., containers, films and coatings of this invention are fabricated from the polyetheramines using conventional fabricating techniques for normally solid, thermoplastic polymers such as extrusion, compression molding, injection molding, blow molding and similar fabrication techniques commonly employed to produce such articles. In an especially preferred embodiment, the polyetheramine is prepared and fabricated into a shaped article by a reactive extrusion process wherein the reactants are fed into and reacted in an extruder using the conditions described in U.S. Patent No. 4,612,156 and is further illustrated in Example 4. In this embodiment, it is understood that one or both of the reactants may be in the form of a prepolymer or a partially advanced resin prior to feeding the reactants into the extruder. Illustrative Embodiments The following examples are given to illustrate the invention and should not be interpreted as limiting it in any way. Unless stated otherwise, all parts and percentages are given by weight. Example 1 Piperazine/Bisphenol A Polymer To a 100 cm 3 resin kettle flask equipped with an overhead stirrer and a nitrogen sparge were added 7.37 g (21.6 mmol) of the diglycidyl ether of bisphenol-A (4,4') which had been washed with methanol, 1.84 g (21.4 mmol) of piperazine recrystallized from diethyl ether and 6 cm 3 of the methyl ether of dipropylene glycol (DPG) with stirring over a period of 0.5 hour. The resulting mixture was heated to about 80°C while stirring the mixture thereby producing a temperature exotherm to 140-150°C which was accompanied by a viscosity increase of the reaction mixture. The mixture was maintained at this temperature for one hour during which the mixture was maintained stirrable by the addition of 1cm 3 aliquots of DPG. At this point, 0.05 cm 3 of diethanol amine was added to cap any residual epoxide end groups. The reaction mixture was then cooled to about 25°C and diluted with about 50cm 3 of dimethylformamide (DMF). The polymer product was precipitated by pouring the reaction mixture into excess methanol/water (1:1 by volume), filtered and air dried. The product was redissolved in DMF and reprecipitated in methanol/water, filtered and dried to yield 8.3g (90%) of polymer having the following structural formula: where D = bisphenol-A, i.e. This polymer had a glass transition temperature (Tg) of 100°C and an inherent viscosity of 0.85 dL/g [85cm 3 /g] in DMF at 25°C. The polymer was tested for barrier to the transmission of oxygen and the results are reported in Table I. Example 2 Generally following the procedure of Example 1, additional polyetheramines represented by the structural formula: were prepared using different amines and dihydric phenols. These polyetheramines were also tested for Tg, intrinsic viscosity and barrier properties and the results are reported in Table I. In Sample Nos. 1-6, Component A was varied as indicated in the table and Component B was derived from bisphenol-A. In Sample Nos. 7-11, Component A was derived from piperazine and Component B was varied as indicated in the table. The inclusion of the amine Component (A) produces a surprisingly large reduction in the oxygen permeability of the polymer. Example 3 (COMPARATIVE) Using the apparatus and general procedure of Example 1, a mechanically stirred mixture of ethanolamine (1.099g, 18.0 mmol), resorcinol (1.982 g, 18.0 mmol) and bisphenol A diglycidyl ether (epoxy equivalent weight=12.56 g, 36.7 mmol) in 17 cm 3 of the phenyl ether of propylene glycol was heated to 110°C under a nitrogen atmosphere. After the reaction mixture rose exothermically to 140°C and then cooled to 130°C, ethyltriphenylphosphonium acetate (70% in methanol, 5 cm 3 ) was added, causing the temperature to rise exothermically to 167°C. The solution was allowed to cool to 160°C and stirred at that temperature for 45 minutes, after which it was diluted to 75 cm 3 with dimethyl formamide. The resulting solution was poured into a 1:1 methanol/water mixture to precipitate a white solid which was collected and stirred in fresh 1:1 methanol/water for 17 hrs. The solid was collected by filtration, allowed to air dry and taken up in 100 cm 3 of tetrahydrofuran. The resulting solution was again added to methanol/water to yield 12.79 g of solid which was dried in vacuo at 60°C for 24 hrs. The copolymer is represented by the following formula: where D = bisphenol-A, i.e. The copolymer was tested as in Example 1 and the results are reported as Sample No. 4 in Table II. In a manner similar to the foregoing copolymerisation procedure, several additional copolymers were prepared and tested and the results of those tests are reported as Sample Nos. 1-3 in Table II. These polymers are generally represented by the following structure wherein A, B and G are defined in Table II: Example 4 Liquid diglycidyl ether of bisphenoi-A (DER™-332) and monoethanolamine were separately pumped at a 1.0/1.0 mole ratio into the feed zone cf a 30 mm Werner-Pfleiderer twin-screw extruder operating at ≈ 100 rpm. The feed zone was maintained at 65°C. The other zones were heated to 180°, 180°, 185°, 185°, and 180°C (die). Halfway down the barrel of the extruder, diethanolamine was pumped into the molten polymer at a rate of 50 g/hr in order to control molecular weight. The high molecular weight poly(amino ether) strand that exited the die was cooled in a water bath and subsequently chopped into pellets. Polymer produced in this manner demonstrated a less yellow color and better practical toughness than material of similar molecular weight produced in solution as described in Table III: Polymer Prepared By: Dynatup Impact Energy (at break, ft-lbs.) Yellowness Index solution process 14 (brittle/ductile) 18.79 reactive extrusion process 84 (ductile) 2.13 As evidenced by the data shown in Table III, the reactive extrusion process yields a polymer having unexpectedly higher impact strength and less color than polymer made by the solution process.

Claims: A moldable thermoplastic polyetheramine, having repeating units represented by the formula: wherein each A independently is piperazine, a substituted piperazine, or a group of the formula: in which R 2 is a C 2 -C 10 hydrocarbylene or substituted hydrocarbylene and Z is a C 1 -C 10 hydrocarbylamido, or R 2 is a C 1 -C 10 alkylene or substituted C 1 -C 10 alkylene or phenyl or substituted phenyl and Z is alkoxy, hydroxyalkyl or alkylamino, provided that if R 2 is phenyl or substituted phenyl then hydroxyalkyl is hydroxymethyl; R 3 is a C 1 -C 10 hydrocarbylene or a substituted hydrocarbylene; each R 5 independently is C 1 -C 10 alkyl or substituted C 1 -C 10 alkyl or phenyl or substituted phenyl wherein the substituent is hydroxy, hydroxymethyl or alkylamido; each G and B independently is a divalent aromatic moiety; each Y independently is divalent oxygen or sulfur; R 1 is hydrogen, a monovalent hydrocarbon or substituted monovalent hydrocarbon; each of V and V' is independently is a secondary amine or a tertiary amine; w is a whole number from 10 to 400; and x is a number sufficiently high that the oxygen transmission rate of the polyetheramine is less than 5 c.c-mil/100 inch 2 -atmosphere (O 2 )-day [2.25 x 10 -7 cc.mm/(m 2 .s.kPa)]. The polyetheramine of Claim 1, wherein R 1 is hydrogen or methyl, R 2 is alkylene, R 5 is alkyl or substituted alkyl, each B and G independently is arylene, arylenealkylidenearylene, alkyl- substituted derivatives of arylene or alkyl-substituted derivatives of arylenealkylidenearylene, Y is divalent oxygen, and x is from 0.2 to 1. The polyetheramine of Claim 2, wherein V and V' are independently hydroxyalkylamino or bis(hydroxyalkyl)amino, piperidinyl or piperazinyl, x is from 0.5 to 1. The polyetheramine of any one of the preceding claims, which is the reaction product of a diglycidyl ether of a dihydric phenol and an amine having only two amine hydrogens per molecule. The polyetheramine of Claim 4, wherein the dihydric phenol is bisphenol-A, hydroquinone or resorcinol and the amine is substituted or unsubstituted piperazine, substituted aniline, a substituted alkylamine, an alkanolamine. The polyetheramine of Claim 5, wherein the dihydric phenol is bisphenol-A, and the amine is 2-amino-ethanol. The polyetheramine of Claim 1, which is the copolymeric reaction product of a diglycidyl ether of a dihydric phenol, an amine having only two amine hydrogens per molecule, and a dihydric phenol. The polyetheramine.of Claim 7, which is the reaction product of the diglycidyl ether of bisphenol-A or resorcinol, 2-ethanolamine or piperazine and resorcinol or bisphenol-A. The polyetheramine of any one of the preceding claims, in the form of a barrier container, a barrier film, or a barrier coating. A process for preparing a polyetheramine as claimed in any one of the preceding claims, comprising reacting a diglycidyl ether of a dihydric phenol with an amine having only two amine hydrogens in an extruder such that the amine moieties of the amine react with the epoxy moieties of diglycidyl ether to form the polyetheramine. A process as claimed in Claim 10, further comprising adding a dihydric phenol to the reaction mixture. A method of packaging comprising the step of enclosing an oxygen-sensitive material in a polyetheramine as claimed in any one of Claims 1 to 9, or a polyetheramine prepared by a process as claimed in Claim 10.

Inventors: SILVIS H CRAIG, WHITE JERRY E, SILVIS, H. CRAIG, WHITE, JERRY E.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1991
Main classification: C08G59
IPC codes: C08G73, C08G59