Titanium dioxides treated by esters and production thereof

Abstract: Titanium dioxide carries an ester or a partial ester of an hydroxy compound containing 1 to 6 OH groups and an aliphatic saturated C₁₀ to C₂₂ monocarboxylic acid. The product is easily dispersible in plastics compositions, particularly masterbatches. The titanium dioxide can also be coated with one or more hydrous oxides. The product is prepared by milling the titanium dioxide in a fluid energy mill in the presence of the ester or partial ester.

Description: This invention relates to oxides and the production thereof and particularly to titanium dioxide. According to the present invention an oxide comprises particulate titanium dioxide having on the particles thereof an ester or partial ester of pentaerythritol and an unsubstituted aliphatic saturated C₁₀ to C₂₂ monocarboxylic acid. According to the invention also a method for the production of an oxide comprises subjecting particulate titanium dioxide to milling in a fluid energy mill in the presence of an ester or partial ester of an organic hydroxy compound containing 1 to 6 OH groups and an aliphatic saturated C₁₀ to C₂₂ monocarboxylic acid. The invention provides a product which is easily dispersible in plastics compositions such as plastics masterbatches and has advantages over powders not so treated with the ester. The product can be more quickly incorporated, and thus requires less energy usage during such incorporation, in plastics masterbatches than titanium dioxide which has not been so treated or is added to the plastics masterbatch separately from the ester or partial ester. In the method of the invention the oxide is treated with an ester of an organic hydroxy compound having 1 to 6 OH groups and both aliphatic or aromatic hydroxy compounds can form the basis of the ester. Typical examples of aliphatic compounds are aliphatic polyols such as ethylene glycol, trimethylol propane, glycerine, hexane triol, erythritol, mannitol, sorbitol and pentaerythritol. Examples of aromatic hydroxy compounds are bisphenol A, hydroquinone and phloroglucinol. Preferably the hydroxy compound is pentaerythritol. Mixtures of different hydroxy compounds can be used. The esters usable in the present invention are formed by reaction of said hydroxy compound and an aliphatic saturated C₁₀ to C₂₂ monocarboxylic acid. Mixtures of different acids can be employed. Typical acids are capric acid, undecanoic acid, lauric acid, tridecanoic acid, myristic acid, palmitic acid, margaric acid, stearic acid and behenic acid. Preferably the acid is myristic acid, palmitic acid or stearic acid. Mixtures of different esters or partial esters can be employed to treat the particulate titanium dioxide. The particulate titanium dioxide can also be treated with polyols such as alkanols, or alkanolamines as well as the ester or partial ester. Polyols such as pentaerythritol, trimethylol ethane or trimethylolpropane can be added to the particulate material together with the ester or partial ester or separately therefrom. The titanium dioxide treated with the ester usually is pigmentary titanium dioxide, but, if desired the titanium dioxide can have a size smaller than that normally associated with the pigmentary form. The titanium dioxide can be either anatase or rutile titanium dioxide but preferably is rutile titanium dioxide. The titanium dioxide can be that obtained from the so-called "sulphate" process or that from the "chloride" process. The titanium dioxide can also carry a so-called coating of one or more oxides or hydrous oxides of such as, aluminium titanium, cerium, zirconium, silicon and zinc, or a silicate or a phosphate which has been applied to the particles prior to treatment with the said ester. Typically hydrous oxides are deposited in a wet process in which the particles of titanium dioxide in the form of an aqueous dispersion are mixed with one or more hydrolysable salts which upon hydrolysis deposit the required hydrous oxide on the particles. Amounts of oxide or hydrous oxide present as coating can be from 0.5% to 25% by weight as oxide on weight of TiO₂ and preferably will be from 0.5% to 10% by weight. The product of the invention carries the ester in an amount of 0.05% to 1.0% by weight of the product, and preferably from 0.1 to 0.5% by weight. Treated products in accordance with the invention are produced by subjecting the titanium dioxide to fluid energy milling in the presence of the said ester. The ester can be added directly to the fluid energy mill simultaneously with the titanium dioxide or can be mixed with the powder before milling either in the dry state or in the form of an aqueous dispersion or slurry prior to drying and milling. In the case of solid esters, these, if desired can be melted prior to addition to the powder or can be dissolved in a suitable solvent or formed into an aqueous dispersion prior to addition to the powder or to an aqueous dispersion thereof. Fluid energy milling can be carried out with steam or other gaseous fluid, e.g. air at an appropriate temperature and pressure to effect the necessary milling of the powder and distribution of the said ester over the surface of the powder. Typically the milling fluid is introduced into the fluid energy mill at a pressure of from 3 to 25 bars pressure, preferably from 5 to 20 bars. When steam is employed then super heated steam at the appropriate temperature and pressure is employed and temperatures of up to 300°C can be employed. The ratio of the weight of milling fluid to the weight of titanium dioxide milled usually is from 0.5:1 to 10.0:1 and the optimum ratio depends on the particular milling conditions and the actual composition or form of the titanium dioxide being milled. With steam generally, preferably, ratios in the range 1.5:1 to 3.0:1 are employed. The use of steam is preferred since other milling fluids may not possess the same energy, weight for weight as does steam. Milling may be effected in a plurality of milling stages if desired with appropriate adjustments to the quantity of milling fluid used in individual milling stages. The products of the invention are of value in the preparation of plastics composition or masterbatches. Typically the product can be incorporated in polymers such as polyolefines, polystyrene and ABS melts. The actual amount of the particulate titanium dioxide present in the plastics composition depends on the particular form of the composition. For masterbatches the amount of treated titanium dioxide can be from 50 to 75% of the weight of the composition. Increasing advantages are observed in the speed of incorporation as the amount of pigment is increased. The invention is illustrated in the following Examples. EXAMPLE 1 (Comparative) A fine crystal rutile TiO₂ pigment having a 1% by weight hydrous alumina coating was subjected to fluid energy milling. The product was passed twice through the mill. Trimethylol propane 0.35% (w:w) was added at the second pass. The total steam to TiO₂ weight ratio was approximately 3.4. The treated Product (A) was collected and tested as described below. A blend of 200g of Product (A) and 200g of linear low density polyethylene, (LLDPE Escorene 5101 from ESSO Chemicals), was passed through a 12 mesh sieve. This mix was then passed through a mechanical blender. The blend was fed into a twin screw extruder: a Haake Rheometer 5000 system with TW100 twin screw attachment. The zones of the twin screw were set at 140°C, 160°C and 180°C. Measurements were taken of the torque and output (flowrate) of the screw at a revolution of 90 rpm. Additionally, the rpm and output (flowrate) were measured, at a torque of 2000 metre gram. The results are shown in the Table below. The dispersion of the sample was determined by a blown film test. EXAMPLE 2 A Product (B) was prepared using the same base pigment as in Example 1 except that in the second pass through the mill 0.17% (w:w) of an ester of pentaerithrytol and a mixture of fatty acids, (predominantly Stearic, Palmitic and Myristic), commercially available as Loxiol EP728 from Henkel Chemicals, was added. This was in addition to the 035% (w:w) Trimethylol propane. The treated Product (B) as described in Example 1 was collected and tested. EXAMPLE 3 (Comparative) This is a repeat of Example 1, but in this Example 0.34g of the ester, (Loxiol EP 728), was added to the TiO₂/LLDPE pre-mix. The results are shown in the following table. Screw Speed (90 rpm) Screw Torque (2000 metre gram) Flow Rate (Kg/hr) Torque (metre gram) Flow Rate Kg/hr) Speed (rpm) Example 1 1.30 2150 1.13 83 Example 2 1.48 1950 1.73 106 Example 3 1.34 2080 1.25 85 The dispersion rating of all the samples was excellent. The results show that Product B (Example 2) when used to produce a masterbatch was easier to incorporate and had a higher flow rate through the screw extruder.

Claims: An oxide comprising particulate titanium dioxide having an organic compound on the particles thereof characterised in that the organic compound is an ester or partial ester of pentaerythritol and an unsubstituted aliphatic saturated C₁₀ to C₂₂ monocarboxylic acid. An oxide according to claim 1 characterised in that the monocarboxylic acid is capric acid, undecanoic acid, lauric acid, tridecanoic acid, myristic acid, palmitic acid, margaric acid, stearic acid or behenic acid. An oxide according to claim 1 or 2 characterised in that the amount of the ester or partial ester is from 0.05% to 1.0% by weight of the product. An oxide according to any one of the preceding claims characterised in that the particles of titanium dioxide also carry a coating of one or more oxides or hydrous oxides, a silicate or a phosphate. An oxide according to claim 4 characterised in that the amount of the oxide or hydrous oxide is from 0.5% to 25% by weight as oxide on weight of TiO₂. An oxide according to any one of the preceding claims characterised in that the particles of titanium dioxide carry a polyol in addition to said ester or partial ester. An oxide according to claim 6 characterised in that the polyol is pentaerythritol, trimethylolethane or trimethylolpropane. A method for the production of an oxide which includes subjecting particulate titanium dioxide to milling in a fluid energy mill characterised in that milling is effected in the presence of an ester or partial ester of an organic hydroxy compound containing 1 to 6 OH groups and an aliphatic saturated C₁₀ to C₂₂ monocarboxylic acid. A method according to claim 8 characterised in that the organic hydroxy compound is an aliphatic polyol. A method according to claim 9 characterised in that the aliphatic polyol is ethylene glycol, trimethylolpropane, glycerine, hexane triol, erythritol, mannitol, sorbitol or pentaerythritol. A method according to any one of claims 8 to 10 characterised in that the ester or partial ester is mixed with the said titanium dioxide prior to addition to said mill. A method according to claim 11 characterised in that the ester or partial ester is added to the mill simultaneously with said titanium dioxide. A method according to any one of claims 8 to 12 characterised in that a milling fluid at a pressure of from 3 bars to 25 bars is introduced into said mill. A method according to claim 13 characterised in that the pressure is from 5 to 20 bars. A method according to claim 13 or 14 characterised in that the ratio of the weight of said milling fluid to the weight of the said titanium dioxide is from 0.5:1 to 10:1. A method according to claim 15 characterised in that the milling fluid is steam and the ratio of the weight of steam to weight of titanium dioxide is from 1.5:1 to 3.0:1.

Inventors: DECELLES GUY, DECELLES, GUY
Applicants: TIOXIDE GROUP SERVICES LTD, TIOXIDE GROUP SERVICES LIMITED
Application year: 1991
Main classification: C09C1
IPC codes: C09C1