METHOD OF FORMING FUEL TANK WITH BAFFLE PLATES

Abstract: A fuel tank characterized in that two preformed baffle plates are mounted to a blow pin, this blow pin is inserted into a molten parison made of thermoplastic resin, closing of a split mold and supply of pressure fluid are performed in this state, and the baffle plates are welded into the tank simultaneously with the forming of the tank. As the two baffle plates are provided in the fuel tank simultaneously with the forming of the tank, the fuel tank having no thin thickness wall portions can be manufactured.

Description: Industrial Field of Utilization The present invention relates to a method of molding a fuel tank having baffle plates and, more specifically, to a method of molding a fuel tank by the blow-molding method and, at the same time, mounting baffle plates on the inner surface of the fuel tank as a unitary structure. Prior Art Plastic fuel tanks such as automotive fuel tanks have been provided with baffle plates on the inside thereof in order to improve mechanical strength, and to prevent unpleasant sound that is generated when the fuel pitches and rolls in the tank while the vehicle is running and to stabilize the internal capacity of the tank. A conventional method of molding a fuel tank with baffle plates consists of using a metal mold having convex portions that correspond to the plates, and effecting the blow-molding while arranging in the metal mold the parison that is formed by extrusion-molding or injection-molding a thermoplastic resin. According to the above method, however, the root portions of the baffle plates tend to lose thickness, limitation is imposed on the size of the baffle plates, and technological difficulty is involved in molding two pieces of baffle plates simultaneously. Gist of the Invention The object of the present invention therefore is to provide a method of molding a fuel tank having baffle plates, which effectively solves the above-mentioned problems inherent in the prior art. US-3,919,373 discloses a method of molding a fuel tank in accordance with the preamble of claim 1. According to the present invention, there is provided a method of molding a fuel tank comprising inserting a blow-pin in a molten parison of a thermoplastic resin from the lower side thereof; mounting a plurality of pre-molded baffle plates on the blow-pin; closing split metal molds under this condition, feeding a pressurized fluid thereto, and melt-adhering the baffle plates onto the inner surface of the fuel tank while the fuel tank is being molded; characterised in that: the blow-pin is formed with a plurality of grooves having different lengths and extending downwardly from the tip of the blow-pin; the blow-pin is inserted into the parison from the lower side thereof and the premolded baffle plates are mounted on the blow-pin via the grooves. Thus, according to the present invention, it is possible to provide a plurality of, for example, two pieces of baffle plates in the fuel tank simultaneously with the molding of the fuel tank without resulting in the formation of very thin portions. Fig. 1 is a side sectional view of a baffle plate molded article used in the present invention; Fig. 2 is a plan view of the baffle plate molded article used in the present invention; Fig. 3 is a diagram illustrating another baffle plate molded article used in the present invention; Fig. 4 is a side sectional view illustrating a blow-pin used in the present invention; Fig. 5 is a plan view of the blow-pin that is used in the present invention; Fig. 6 is a diagram showing the step of blow-molding according to the present invention; and Fig. 7 is a diagram showing a fuel tank produced according to the present invention. In the present invention, examples of the resin material for making baffle plates and fuel tank include any thermosetting resins that can be blow-molded such as polyolefin resins, e.g., low-, medium- and high-density polyethylenes, a polypropylene, an ethylene-α-olefin copolymer, a thermoplastic polyester, a polyamide resin, etc. Among them, a polyolefin resin is preferably used. Moreover, the thermoplastic resins must exhibit not only resistance against environmentally caused stress and cracks (ESCR property) for light oils that are now chiefly used as fuels and methanol that has been studied to be used as a fuel in the future, but also gas barrier property, impact resistance, heat resistance and weatherability. Among the polyolefin resins, the high-density polyethylene is preferably used from the standpoint of such properties. As the baffle plates, in particular, there can be preferably used the high-density polyethylene having a melt flow rate (MFR) of 0.01 to 10 g/10 min. and particularly 0.1 to 10 g/min. under the load of 2160 g and a density of 0.94 to 0.97 g/cm 3 . As the fuel tank, there can be preferably used the high-density polyethylene having an MFR of 1.0 to 10 g/10 min. and particularly 2 to 5 g/10 min. under the load of 21.6 kg, and a density of 0.94 to 0.97 g/cm 3 . The invention will now be described based on embodiments shown in the accompanying drawings. According to the method of the present invention, the baffle plates are first molded before being melt-adhered to the interior of the fuel tank. Fig. 1 is a side sectional view of the baffle plates and Fig. 2 is a plan view thereof. As will be obvious from Figs.1 and 2, the baffle plates (generally designated at 1) consist of a hollow tubular support portion 2 and a pair of plate portions 3a and 3b that outwardly extend in the direction of diameter thereof. The tubular support portion 2 has protuberances 4,4 formed on the inner surface thereof, so that it can be mounted on a blow-pin that will be described later. In Figs. 1 and 2, the plates are provided in a pair. The plates, however, may be provided in two or more pairs as shown in Fig. 3. The baffle plates can be easily molded by a molding method which is known per se, such as extrusion molding, injection molding or a like method. According to the present invention, the baffle plates are mounted on the blow-pin. Here, it is desired that the baffle plates are pre-heated in an oven maintained at about 100°C for about 15 minutes. Fig. 4 is a side sectional view of the blow-pin and Fig. 5 is a plan view thereof. That is, the blow-pin (generally designated at 5) has a pressurized fluid feeding portion 6 formed on the inside thereof and further has an opening 7 formed at the upper end thereof. The pressurized fluid such as the air is released to the external side through the opening 7, and whereby the so-called blow molding is carried out. Furthermore, long grooves 8a and short grooves 8b are alternatingly formed on the outer surface of the blow-pin 5 downwardly extending from the upper end thereof. The blow-pin 5 is inserted in the tubular support portion 2 of the baffle plates 1, whereby the protuberances 4 engage with the grooves, and the two pieces of baffle plates 1 are mounted on the blow-pin 5. That is, the two pieces of baffle plates are held by the long grooves 8a and short grooves 8b, respectively (the baffle plate held by the long grooves 8a is located at a lower portion of the blow-pin 5 and the baffle plate held by the short grooves 8b is located at an upper portion of the blow-pin 5). According to the present invention, the fuel tank is molded by the blow-molding by using the blow-pin 5 on which are mounted two pieces of baffle plates 1. This step is shown in Fig. 6. That is, in Fig. 6, a hollow tubular molten parison 11 (parison resin temperature is 200° to 240°C) is extruded from an extruder 10, and the blow-pin 5 on which the baffle plates 1 are mounted are inserted in the molten parison 11. Split metal molds 12, 12 are arranged on the outside of the molten parison 11, and are closed under the condition where the blow-pin 5 is fitted in the molten parison 11. The pressurized fluid such as the air is blown through the blow-pin 5 in order to mold the fuel tank and, at the same time, to melt-adhere the baffle plates 1 onto the inner wall of the tank. After the molding is finished, the blow-pin 5 is pulled out thereby to obtain a fuel tank 13 having baffle plates 1 as shown in Fig. 7. In the above-mentioned step, it is desired that tiny protuberances 15 are formed on the surfaces of the split metal molds 12 that come in contact with the baffle plates 1. The protuberances enable the baffle plates 1 to be effectively melt-adhered. In the above-mentioned step, the fuel tank was produced having two pieces of baffle plates. It is, of course, allowable to produce the fuel tank having more baffle plates, such as three or more pieces of baffle plates. In this case, the number of grooves formed in the blow-pin should be increased depending upon the number of the baffle plates. In accordance with the present invention mentioned above, there was produced a fuel tank having a content of 100 liters, a weight of 7.5 kg and two baffle plates (0.6 kg) by using the resin described below and a blow-molding machine manufactured by Nippon Seikosho Co. "NB60P115AC25" (mold fastening force 60 tons, screw diameter 115 mm, accumulator 25 L). Resin used Main body. A high-density polyethylene having an MFR (load 21.6 kg) of 4 g/10 min., and a density of 0.956 g/cm 3 . Baffle plates. A high-density polyethylene having an MFR (load 2160 g) of 5.5 g/10 min., and a density of 0.968 g/cm 3 . The thus obtained fuel tank possessed a minimum thickness of greater than 3 mm with no extremely thin portions, and was strong enough. According to the present invention, the metal mold used for the molding operation needs not be provided with protuberances that correspond to the baffle plates. It is therefore allowed to obtain a fuel tank which as a whole has a uniform thickness without extremely thin portions and to provide two pieces of baffle plates inside the fuel tank while it is being molded, contributing to greatly enhancing the operation efficiency.

Claims: A method of molding a fuel tank comprising inserting a blow-pin (5) in a molten parison (11) of a thermoplastic resin from the lower side thereof; mounting a plurality of pre-molded baffle plates (1) on said blow-pin; closing split metal molds (12) under this condition, feeding a pressurized fluid thereto, and melt-adhering the baffle plates onto the inner surface of the fuel tank while said fuel tank is being molded; characterised in that: said blow-pin (5) is formed with a plurality of grooves (8a, 8b) having different lengths and extending downwardly from the tip of said blow-pin; said blow-pin (5) is inserted into said parison from the lower side thereof and said premolded baffle plates (1) are mounted on said blow-pin via said grooves (8a, 8b). A molding method according to claim 1, wherein said baffle plates (1) include a hollow tubular support portion (2) and a pair of plates (3a, 3b) that outwardly extend in the radial direction thereof, and protuberances (4) are formed on the inner surface of said support portion to engage with the grooves (8a, 8b) that are formed in said blow-pin (5). A molding method according to claim 1 or 2, wherein said thermoplastic resin is a high-density polyethylene having an MFR of from 1.0 to 10 g/10 min. under the load of 21.6 kg, and a density of 0.94 to 0.97 g/cm 3 . A molding method according to claim 1, 2 or 3, wherein said baffle plates are made of a high-density polyethylene having an MFR of 0.01 to 10 g/min. under the load of 2160 g, and a density of 0.94 to 0.97 g/cm 3 .

Inventors: HIRAKAWA SADAMU, HIRAKAWA, SADAMU
Applicants: MITSUI PETROCHEMICAL IND, MITSUI PETROCHEMICAL INDUSTRIES, LTD.
Application year: 1991
Main classification: B29C49
IPC codes: B29C49, B60K15, B29K105, B29L22