Process for producing acicular goethite particles and acicular magnetic iron oxide particles

Abstract: Acicular goethite particles are produced by a process which comprises (i) reacting an aqueous ferrous salt solution with less than one equivalent of an aqueous alkali hydroxide solution and/or an aqueous alkali carbonate solution based on Fe²⁺ in said aqueous ferrous salt solution; and (ii) blowing a molecular oxygen-containing gas into the ferrous salt reaction solution containing colloidal ferrous hydroxide or iron-containing colloidal precipitates thus obtained in the presence of ascorbic acid or a salt thereof so as to oxidize said colloidal ferrous hydroxide or iron-containing colloidal precipitates and to produce acicular goethite particles through green rust. Acicular magnetic iron oxide particles may be produced by reducing the acicular goethite particles obtained to produce acicular magnetite particles and, if necessary, the acicular magnetite particles obtained may be oxidized to produce acicular maghemite particles. Also, if necessary, the acicular magnetite or maghemite particles may be modified with Co or Co and Fe²⁺.

Description: The present invention relates to a process for producing acicular goethite particles which are suitable as a starting material for magnetic particles for magnetic recording, and which have a uniform particle size distribution, are substantially free of dendrites and have a large aspect ratio (major axial diameter:minor axial diameter). The present invention also relates to a process for producing acicular magnetic iron oxide particles which have a uniform particle size distribution, are substantially free of dendrites, and have a large aspect ratio (major axial diameter:minor axial diameter) and an excellent coercive force distribution. With progressing miniaturization and weight-reduction of magnetic recording and reproducing apparatuses in recent years, the necessity for a recording medium having a higher performance such as a magnetic tape and a magnetic disk has been increasing more and more. In other words, a magnetic recording medium is required to have a higher recording density, higher sensitivity and higher output characteristic. The magnetic characteristics of magnetic particles which are demanded in order to satisfy the above-mentioned requirements for the magnetic recording medium, are a high coercive force and an excellent dispersibility. In order to improve the sensitivity and the output of a magnetic recording medium, the magnetic particles must have as high a coercive force as possible. This fact is described in, for example, DEVELOPMENT OF MAGNETIC MATERIALS AND TECHNIQUE OF IMPROVING THE DISPERSION PROPERTY OF MAGNETIC POWDER (1982), published by K.K. Sogo Gijutsu Kaihatsu Center, p. 310: "Since the improvement of magnetic tapes has been directed toward a higher sensitivity and a higher output, it is an important point to enhance the coercive force of acicular γ-Fe 2 O 3 particles,..." In order to improve the recording density of a magnetic recording medium, the magnetic recording medium must have a high coercive force and a large residual magnetization (Br), as described in the said DEVELOPMENT OF MAGNETIC MATERIALS AND TECHNIQUE OF IMPROVING THE DISPERSION PROPERTY OF MAGNETIC POWDER. p. 312: "The condition for high-density recording in a coating-type tape is that it is possible to keep the high output characteristics with respect to a short-wavelength signal at a low noise level. For this purpose, it is necessary that both the coercive force (Hc) and the residual magnetization (Br) are large, and that the thickness of the coating film is thin". It is therefore necessary that the magnetic particles have a high coercive force and they are excellent in dispersibility in the vehicle, and orientation property and packing density in the coating film. In order to enhance the output of a magnetic recording medium, it is required to have a small switching field distribution (hereinunder referred to as "S.F.D.") and hence, the magnetic particles are required to have a small width of coercive force distribution. This fact is described in JP-A-63-26821 (1988): "Fig. 1 is a graph showing the relationship between the S.F.D. of the above-described magnetic disk and the recording and reproducing output. ... The relationship between the S.F.D. and the recording and reproducing output is linear, as is clear from Fig. 1. It indicates that the recording and reproducing output is enhanced by using ferromagnetic powder having a small S.F.D. That is, in order to obtain a large output, an S.F.D. of not more than 0.6 is necessary. As well known, the coercive force of magnetic iron oxide particles depends upon the configurational anisotropy, crystalline anisotropy, strain anisotropy, exchange anisotropy, or the interaction thereof. Acicular magnetite particles and acicular maghemite particles which are used as magnetic iron oxide particles at present show a relatively high coercive force by utilizing the anisotropy derived from their shapes, namely, by increasing the aspect ratio (major axial diameter:minor axial diameter). The known acicular magnetic particles are obtained by reducing as a starting material goethite particles or hematite particles obtained by heat-treating the goethite particles, in a reducing gas such as hydrogen to form magnetite particles or iron based metal particles or by further oxidizing the thus-obtained magnetite particles in air to form maghemite particles. The known acicular magnetic iron oxide particles modified with Co or Co and Fe 2+ are obtained by dispersing acicular magnetite particles or acicular maghemite particles as the precursor particles in an alkaline suspension containing cobalt hydroxide or an alkaline suspension containing cobalt hydroxide and ferrous hydroxide so that 0.1 to 21.0 atomic% of Co based on Fe of the precursor particles is contained therein, and heat-treating the resultant dispersion. The residual magnetization (Br) in a magnetic recording medium depends upon the dispersibility of the magnetic particles in the vehicle, and the orientation property and packing density of the magnetic particles in the coated film, and in order to improve these properties, the magnetic particles to be dispersed in the vehicle are required to have as large an aspect ratio (major axial diameter:minor axial diameter) as possible, a uniform particle size distribution and no inclusion of dendrites. As described above, magnetic iron oxide particles which have a substantially uniform particle size distribution, which are substantially free of dendrites and which have a large aspect ratio (major axial diameter:minor axial diameter), are now in the strongest demand. In order to obtain magnetic iron oxide particles provided with these properties, it is necessary that as a starting material goethite particles have a substantially uniform particle size distribution, are substantially free of dendrites and have a large aspect ratio (major axial diameter:minor axial diameter). Various attempts have been made to produce acicular goethite particles which have a uniform particle size distribution and are substantially free of dendrites. For example, JP-A-2-293330 (1990) discloses a method of producing acicular goethite particles by adding ascorbic acid or a salt thereof to the suspension containing ferrous hydroxide which is obtained by reacting an aqueous ferrous salt solution with not less than 1.0 equivalents of an aqueous alkali hydroxide and blowing an oxygen-containing gas into the suspension. Magnetic iron oxide particles which have a uniform particle size distribution, are substantially free of dendrites, and have a large aspect ratio (major axial diameter:minor axial diameter) and an excellent coercive force distribution are now in the strongest demand. The particles obtained by the method described in JP-A-2-293330 (1990) have an aspect ratio (major axial diameter:minor axial diameter) of at the most 10 to 11:1 and cannot be said to have a large aspect ratio (major axial diameter:minor axial diameter). The method includes the step of adding an alkaline earth metal in addition to ascorbic acid or a salt thereof. But in this case, the aspect ratio (major axial diameter:minor axial diameter) is at the most 15:1. The acicular magnetic iron oxide particles produced from, as a starting material, these goethite particles have a uniform particle size distribution and are substantially free of dendrites, but the aspect ratio (major axial diameter:minor axial diameter) thereof is reduced to 1/2 to 1/3 after they are subjected to heat treatment. US-A-4,495,164 discloses a process for producing acicular magnetite or maghemite of high axial ratio, which comprises preparing an iron (II) hydroxide suspension at a pH of at least 11 with a magnesium sulfate or magnesium chloride in an amount of 0.5 to 7.0 atomic % based on the amount of the iron (II) hydroxide in the suspension and calculated as the ratio of Mg to Fe (II), oxidizing the resultant suspension with the oxygen-containing gas to form an acicular iron (III) oxide hydroxide in the form of particles having a long axis length of 0.3 to 2.0 µm and an axial ratio of more than 20:1, reducing said acicular iron (III) oxide hydroxide into the acicular magnetite, and oxidizing the resultant acicular magnetite to form the acicular maghemite, if necessary. Although the particles produced are said to have an average long axis length of 0.3 to 2.0 µm and axial ratio of more than 20:1, the particle size distribution is poor, being of the order of 0.32-0.35. JP-A-60-21307 discloses a process for obtaining goethite needlelike crystals wherein an agueous ferrous salt solution and an agueous alkali carbonate or alkali hydrogencarbonate solution are reacted to form a ferrous carbonate colloid. An oxygen-containing gas is then introduced into the colloid solution to produce firstly green rust and then needlelike goethite crystals. The crystals have an axial ratio of about 5:1 to 10:1. Accordingly, the present invention seeks to provide acicular goethite particles which have a uniform particle size distribution, are substantially free of dendrites and have a large aspect ratio (major axial diameter:minor axial diameter) and acicular magnetic iron oxide particles further having excellent coercive force distribution in addition to the above-described properties. As a result of studies undertaken by the present inventors, it has been found that by blowing an oxygen-containing gas into a ferrous salt reaction solution containing colloidal ferrous hydroxide or iron-containing colloidal precipitates which is obtained by reacting an aqueous ferrous salt solution with less than one equivalent of an aqueous alkali hydroxide solution, an aqueous alkali carbonate solution or an aqueous alkali hydroxide and alkali carbonate solution based on Fe 2+ in the aqueous ferrous salt solution so as to oxidize the colloidal ferrous hydroxide or iron-containing colloidal precipitates and to produce acicular goethite particles through green rust, ascorbic acid or a salt thereof and, if necessary, a zinc compound being added to any of the solutions before the production of the acicular goethite particles, or by blowing an oxygen-containing gas into a ferrous salt reaction solution containing colloidal ferrous hydroxide or iron-containing colloidal precipitates which is obtained by reacting an aqueous ferrous salt solution with less than one equivalent of an aqueous alkali hydroxide solution, an aqueous alkali carbonate solution or an aqueous alkali hydroxide and alkali carbonate solution based on Fe 2+ in the aqueous ferrous salt solution so as to oxidize the colloidal ferrous hydroxide or iron-containing colloidal precipitates and to produce acicular goethite nucleus particles through green rust, ascorbic acid or a salt thereof and, if necessary, a zinc compound being added to any of the solutions before the production of the acicular goethite nucleus particles; and growing the acicular goethite nucleus particles so as to produce acicular goethite particles, the thus-obtained acicular goethite particles and acicular magnetic iron oxide particles have a uniform particle size distribution, are substantially free of dendrites, and have a large aspect ratio (major axial diameter:minor axial diameter) and excellent coercive force distribution. On the basis of this finding, the present invention has been achieved. The present invention provides a process for producing acicular goethite particles which process comprises: (i) reacting an agueous ferrous salt solution with less than one equivalent of an aqueous alkali hydroxide solution and/or an aqueous alkali carbonate solution based on Fe 2+ in said aqueous ferrous salt solution; and (ii) blowing a molecular oxygen-containing gas into the ferrous salt reaction solution containing colloidal ferrous hydroxide or iron-containing colloidal precipitates thus obtained in the presence of ascorbic acid or a salt thereof so as to oxidize said colloidal ferrous hydroxide or iron-containing colloidal precipitates and to produce acicular goethite particles through green rust. In step (ii) acicular goethite nucleus particles may be produced through green rust, and grown so as to produce acicular goethite particles. The present invention also provides a process for producing acicular magnetic iron oxide particles which process further comprises: (iii)heat-treating in a reducing gas the thus produced acicular goethite particles or acicular hematite particles which are obtained by heat-treating at from 300 to 700°C the thus produced acicular goethite particles, thereby producing acicular magnetite particles, and (iv) if necessary, oxidizing said acicular magnetite particles, thereby producing acicular maghemite particles. The present invention additionally provides a process for producing acicular magnetic iron oxide particles which process further comprises: (v) dispersing said acicular magnetite particles or acicular maghemite particles as precursor particles in an alkaline suspension containing cobalt hydroxide or an alkaline suspension containing cobalt hydroxide and ferrous hydroxide so that the Co content in said suspension is from 0.1 to 21.0 atomic% based on the Fe in said precursor particles; and (vi) heat-treating the resultant aqueous dispersion, thereby obtaining acicular magnetite particles or acicular maghemite particles modified with Co or Co and Fe 2+ . The present invention further provides acicular goethite particles having a major axial diameter of 0.1 to 0.6µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 20:1, and a particle size distribution of not less than 0.55, and obtainable by a process as above. The present invention also provides acicular magnetic iron oxide particles comprising: acicular magnetite particles having a major axial diameter of 0.05 to 0.5µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 6.0:1 and an particle size distribution (geometric standard deviation (σ g )) of not less than 0.5 and obtainable by a process as above; or acicular maghemite particles having a major axial diameter of 0.05 to 0.5µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 6.0:1 and a particle size distribution (geometric standard deviation (σ g )) of not less than 0.45 and obtainable by a process as above. The present invention additionally provides acicular magnetic iron oxide particles comprising: acicular magnetite particles modified with Co or Co and Fe 2+ having a major axial diameter of 0.05 to 0.5µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 5.5:1 and a particle size distribution (geometric standard deviation (σ g )) of not less than 0.45, containing from 0.1 to 21.0 atomic % of Co based on the Fe in the precursor particles and from 0 to 25 atomic % of coated Fe 2+ based on the Fe in the precursor particles and obtainable by a process as above; or acicular maghemite particles modified with Co or Co and Fe 2+ having a major axial diameter of 0.05 to 0.5µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 5.5:1 and a particle size distribution (geometric standard deviation (σ g )) of not less than 0.4, containing from 0.1 to 21.0 atomic % of Co based on the Fe in the precursor particles and from 0 to 25 atomic % of coated Fe 2+ based on the Fe in the precursor particles and obtainable by a process as above. In the accompany drawings: Fig. 1 is an electron micrograph (x 30000) of the particle structure of the acicular goethite nucleus particles obtained in Example 1; Fig. 2 is an electron micrograph (x 30000) of the particle structure of the acicular goethite particles obtained in Example 1; Fig. 3 is an electron micrograph (x 30000) of the particle structure of the acicular goethite nucleus particles obtained in Example 3; Fig. 4 is an electron micrograph (x 30000) of the particle structure of the acicular goethite particles obtained in Example 3; Fig. 5 is an electron micrograph (x 30000) of the particle structure of the acicular goethite nucleus particles obtained in Comparative Example 1; Fig. 6 is an electron micrograph (x 30000) of the particle structure of the acicular goethite particles obtained in Comparative Example 1; Fig. 7 is an electron micrograph (x 30000) of the particle structure of the acicular goethite particles obtained in Comparative Example 2; and Fig. 8. is an electron micrograph (x 30000) of the particle structure of the acicular goethite particles obtained in Comparative Example 3. As an aqueous ferrous salt solution used in the present invention, an aqueous ferrous sulfate solution and an aqueous ferrous chloride solution may be used. As an aqueous alkali hydroxide solution used for producing acicular goethite nucleus particles in the present invention, an aqueous sodium hydroxide solution and an aqueous potassium hydroxide solution are usable. As an aqueous alkali carbonate solution, an aqueous sodium carbonate solution , an aqueous potassium carbonate solution and an aqueous ammonium carbonate solution are usable. The amount of aqueous alkali hydroxide solution or aqueous alkali carbonate solution used in the present invention is less than one equivalent based on Fe 2+ in the aqueous ferrous salt solution. If it is not less than one equivalent, it is very difficult to obtain goethite particles having a large aspect ratio (major axial diameter:minor axial diameter). The amount of existent acicular goethite nucleus particles in the present invention is not less than 10 mol% based on the total amount of goethite particles produced. If it is less than 10 mol%, it is difficult to achieve the growing reaction of the acicular goethite nucleus while maintaining the form thereof, so that it is very difficult to obtain the objective acicular geothite particles. Ascorbic acid or a salt thereof in the present invention influences the form such as the particle size, the presence or absence of dendrites and the aspect ratio (major axial diameter:minor axial diameter) of the acicular goethite particles produced. It is therefore necessary that ascorbic acid or a salt thereof is existent in a solution before the acicular geothite particles are produced. Ascorbic acid or a salt thereof may be added to any of the aqueous ferrous salt solution, aqueous alkali hydroxide solution, aqueous alkali carbonate solution, ferrous salt reaction solution containing colloidal ferrous hydroxide or iron-containing colloidal precipitates, and the reaction solution which is producing green rust. An example of a salt of ascorbic acid is sodium ascorbate. The amount of ascorbic acid or a salt thereof added is 0.01 to 5.0 mol% calculated as ascorbic acid based on Fe in the ferrous salt reaction solution containing colloidal ferrous hydroxide or iron-containing colloidal precipitates. If it is less than one 0.01 mol%, the objective goethite particles which have a uniform particle size distribution, no inclusion of dendrites and a large aspect ratio (major axial diameter:minor axial diameter) cannot be obtained. If it exceeds 5.0 mol%, the major axial diameter of acicular goethite particles produced is small and, hence, the aspect ratio (major axial diameter:minor axial diameter) is also small, so that it is impossible to obtain the objective acicular goethite particles. A zinc compound is also preferably existent in a solution such as the one containing ascorbic acid or a salt thereof before the acicular geothite particles or the acicular goethite nucleus particles are produced. A zinc compound may be added to any of the aqueous ferrous salt solution, aqueous alkali hydroxide solution or aqueous alkali carbonate solution, ferrous salt reaction solution containing colloidal ferrous hydroxide or iron-containing colloidal precipitates, and the reaction solution which is producing green rust. The order in which ascorbic acid or a salt thereof and a zinc compound are added to a solution is not restricted, and they may also be added simultaneously, Examples of the zinc compound are zinc sulfate, zinc chloride, and zinc nitrate. The amount of zinc compound added is preferably 0.1 to 7.0 mol% based on Fe in the ferrous salt reaction solution containing colloidal ferrous hydroxide or iron-containing colloidal precipitates. If it is less than 0.1 mol%, the effect of the zinc compound on the increase in the aspect ratio (major axial diameter:minor axial diameter) of the acicular goethite particles is insufficient. Even if it exceeds 7.0 mol%, it is possible to obtain acicular goethite particles, but addition of any more than is necessary is meaningless. In the present invention, elements such as P, A l and Si, which are generally added in the process for producing goethite particles in order to improve various properties of magnetic particles, may be added. In this case, it is also possible to produce the objective acicular goethite particles. In order to grow the acicular goethite nucleus particles in the present invention, any method may be selected from: 1 ○ blowing an oxygen-containing gas into the ferrous salt reaction solution containing the acicular goethite nucleus particles while maintaining the pH at 3 to 6 after, if necessary, adding a ferrous salt thereto; 2 ○ blowing an oxygen-containing gas into the ferrous salt reaction solution containing the acicular goethite nucleus particles at a pH of 8 to 10 which is adjusted by adding an aqueous alkali carbonate solution or an aqueous alkali carbonate and alkali hydroxide solution thereto after, if necessary, adding a ferrous salt thereto; and 3 ○ blowing an oxygen-containing gas into the ferrous salt reaction solution containing the acicular goethite nucleus particles at a pH of not less than 11 which is adjusted by adding an aqueous alkali hydroxide solution thereto after, if necessary, adding a ferrous salt thereto. The acicular goethite particles obtained by growing the acicular goethite nucleus particles at a pH of 8 to 10 have a more uniform particle size distribution, no inclusion of dendrites and a larger aspect ratio (major axial diameter:minor axial diameter). In the present invention, an oxidization is carried out by blowing an oxygen-containing gas such as air into a solution under mechanical stirring, if necessary. The oxidizing reaction temperature in the present invention is not higher than 80°C, preferably 30 to 55°C when producing the acicular goethite nucleus particles and growing the acicular goethite nucleus particles by methods 2 ○ and 3 ○, and not higher than 90°C, preferably 30 to 90°C when growing the acicular goethite nucleus particles by method 1 ○. If the temperature is higher than said temperatures, glanular magnetite particles are included in the acicular goethite particles. The same reaction vessel may be used both for the reaction for producing goethite nucleus particles and for the reaction for growing the goethite nucleus particles. It is also possible to obtain the objective goethite particles by using different reaction vessels for these reactions. It is possible, if necessary, to coat the starting material particles with elements such as P, A l and Si, which have a sintering preventing effect, prior to the heat treatment in a reducing gas. The coating treatment prevents sintering particles and between particles, maintains the shape and the aspect ratio (major axial diameter:minor axial diameter) of the starting material particles and facilitates the production of discrete magnetic iron oxide particles. The oxidization in air according to the present invention is carried out at 200 to 500 °C by an ordinary method. A Co-modification(Co-coating) of the magnetic iron oxide particles in the present invention can be carried out by an ordinary method. For example, the Co-modification is carried out by dispersing the precursor particles in an alkaline suspension containing cobalt hydroxide or cobalt hydroxide and ferrous hydroxide, and heat-treating the dispersion, as described in, e.g., JP-B-52-24237 (1977), JP-B-52-24238 (1977), JP-B-52-36751 (1977) and JP-B-52-36863 (1977). The cobalt hydroxide used in the present invention is obtained by using a water-soluble cobalt salt such as cobalt sulfide and cobalt chloride, and an aqueous alkali hydroxide solution such as an aqueous sodium hydroxide solution and an aqueous potassium hydroxide solution. The ferrous hydroxide used in the present invention is obtained by using a water-soluble ferrous salt such as ferrous sulfide and ferrous chloride, and an aqueous alkali hydroxide solution such as an aqueous sodium hydroxide solution and an aqueous potassium hydroxide solution. The heat treatment for Co-modification is preferably carried out in a non-oxidizing atmosphere at a temperature of 50 to 100°C. The temperature for Co-modification in the present invention affects the treating time. If the temperature is lower than 50°C, the magnetite particles or maghemite particles modified with Co or Co and Fe 2+ are difficult to produce, and even if they are produced, treatment for a very long time is required. The amount of the water-soluble cobalt salt used for Co-modification in the present invention is 0.1 to 21.0 atomic% calculated as Co based on Fe in the precursor particles. If it is less than 0.1 atomic%, the coercive force of the acicular magnetite or maghemite particles produced is not improved sufficiently. On the other hand, if it is more than 21.0 atomic%, the coercive force distribution of the acicular magnetite or maghemite particles produced is not sufficient. The amount of the water-soluble ferrous salt used for Fe-modification in the present invention is 0 to 35 atomic% calculated as Fe 2+ based on Fe in the precursor particles. Almost the whole amount of water-soluble Co salt and water-soluble ferrous salt added is utilized for the modification of the surfaces of the magnetic iron oxide particles. In consideration of the coercive force and the coercive force distribution of the acicular magnetite particles or maghemite particles, the amount of water-soluble Co salt added is preferably 2.0 to 18.0 atomic%. According to the present invention, when an oxygen-containing gas is blown into a ferrous salt reaction solution containing colloidal ferrous hydroxide or iron-containing colloidal precipitates which is obtained by reacting an aqueous ferrous salt solution with less than one equivalent of an aqueous alkali hydroxide solution, an aqueous alkali carbonate solution, or an aqueous alkali hydroxide and alkali carbonate solution based on Fe 2+ in the aqueous ferrous salt solution so as to oxidize the ferrous hydroxide or colloidal iron-containing colloidal precipitates and to produce acicular goethite particles through green rust, while adding ascorbic acid or a salt thereof and, if necessary, a zinc compound to any of the solutions before the acicular goethite particles are produced; or when an oxygen-containing gas is blown into a ferrous salt reaction solution containing colloidal ferrous hydroxide or iron-containing colloidal precipitates which is obtained by reacting an aqueous ferrous salt solution with less than one equivalent of an aqueous alkali hydroxide solution, an aqueous alkali carbonate solution, or an aqueous alkali hydroxide and alkali carbonate solution based on Fe 2+ in the aqueous ferrous salt solution so as to oxidize the colloidal ferrous hydroxide or iron-containing colloidal precipitates and to produce acicular goethite particles through green rust, the acicular goethite particles produced through green rust are used as the acicular goethite nucleus particles, and the acicular goethite nucleus particles are grown so as to produce acicular goethite particles, while adding ascorbic acid or a salt thereof and, if necessary, a zinc compound to any of the solutions before the acicular goethite nucleus particles are produced, it is possible to obtain acicular goethite particles which have a uniform particle size distribution, which are substantially free of dendrites and which have a large aspect ratio (major axial diameter:minor axil diameter). The acicular magnetic iron oxide particles obtained from the acicular goethite particles as a starting material also have a uniform particle size distribution, are free of dendrites and have a large aspect ratio (major axial diameter:minor axial diameter). The acicular magnetic iron oxide particles having these properties are also excellent in the coercive force distribution. It is considered to be because ascorbic acid or a salt thereof is existent in a solution which is producing green rust, that acicular goethite particles which have a uniform particle size distribution, which are substantially free of dendrites and which have a large aspect ratio (major axial diameter:minor axial diameter) are obtained, as is obvious from the later-described Comparative Examples in which the objective acicular goethite particles are not obtained in the case where ascorbic acid or a salt thereof is not existent in a solution which is producing green rust before the acicular goethite particles or the acicular goethite nucleus particles are produced, or in the case where the acicular goethite particles are produced not through green rust in spite of the existence of ascorbic acid or a salt thereof. The influence of the ascorbic acid or a salt thereof on the crystal habit forming process of the goethite particles is different between the reaction for producing goethite particles at a pH of not less than 11 not through green rust, in which the ascorbic acid or a salt thereof acts on the colloidal aqueous hydroxide which is produced by reacting the aqueous ferrous salt solution with the aqueous alkali hydroxide, and the reaction according to the present invention in which the ascorbic acid or a salt thereof acts on the green rust at a pH of 5 of 7. As the amount of ascorbic acid or a salt thereof added is increased, the aspect ratio (major axial diameter:minor axial diameter) of the acicular goethite particles has a tendency of increasing. If a zinc compound is used together with an ascorbic acid or a salt thereof, it is possible to obtain acicular goethite particles having a more uniform particle size distribution, no inclusion of dendrites and a larger aspect ratio (major axial diameter:minor axial diameter) due to the synergistic effect. By adding ascorbic acid or a salt thereof, acicular goethite particles having an aspect ratio (major axial diameter:minor axial diameter) of not less than 20:1 are obtained, while by adding a zinc compound together with ascorbic acid or a salt thereof, acicular goethite particles having an aspect ratio (major axial diameter:minor axial diameter) of not less than 20:1, especially, not less than 25:1 are obtained. The thus-obtained acicular goethite particles according to the present invention have a major axial diameter of 0.1 to 0.6 µm, preferably 0.12 to 0.4 µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 20:1, preferably 25 to 40:1, and a particle size distribution (geometric standard deviation) of not less than 0.55, preferably not less than 0.6, more preferably not less than 0.7. The acicular magnetite particles according to the present invention have a major axial diameter of 0.05 to 0.5 µm, preferably 0.05 to 0.4 µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 6.0:1, preferably 7.0 to 10.0:1, and a particle size distribution (geometrical standard deviation (σ g )) of not less than 0.5, preferably not less than 0.55. The acicular maghemite particles according to the present invention have a major axial diameter of 0.05 to 0.5 µm, preferably 0.05 to 0.4 µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 6.0:1, preferably 7.0 to 10.0:1, and a particle size distribution (geometrical standard deviation(σ g )) of not less than 0.45, preferably not less than 0.5. The acicular magnetite particles modified with Co or Co and Fe 2+ according to the present invention have a major axial diameter of 0.05 to 0.5 µm, preferably 0.05 to 0.4 µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 5.5:1, preferably 5.7 to 9.0:1, a particle size distribution (geometrical standard deviation(σ g )) of not less than 0.45, preferably not less than 0.50 and contain 0.1 to 21 atomic% of Co based on Fe of the precursor particles and 0 to 25 atomic% of coated Fe 2+ based on Fe in the precursor particles. The acicular maghemite particles modified with Co or Co and Fe 2+ according to the present invention have a major axial diameter of 0.05 to 0.5 µm, preferably 0.05 to 0.4 µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 5.5:1, preferably 5.7 to 9.0:1 and a particle size distribution (geometrical standard deviation(σ g )) of not less than 0.4, preferably not less than 0.5, and contains 0.1 to 21 atomic% of Co based on Fe of the precursor particles and 0 to 25 atomic% of coated Fe 2+ based on Fe in the precursor particles. According to the process for producing acicular goethite particles, it is possible to obtain acicular goethite particles which have a uniform particle size distribution, which are free of dendrites and which have a large aspect ratio (major axial diameter:minor axial diameter). According to the process for producing the magnetic iron oxide particles according to the present invention, it is possible to obtain acicular magnetic iron oxide particles which have a uniform particle size distribution, which are free of dendrites and which have a large aspect ratio (major axial diameter:minor axial diameter) and excellent coercive force distribution, so that they are suitable as magnetic particles for high-density, high-sensitivity and high-output recording. [Examples] The present invention will be explained in more detail in the following Examples. The major axial diameter and the aspect ratio (major axial diameter:minor axial diameter) in each of the following Examples and Comparative Examples are expressed by the average values of the values obtained by measuring the electron micrographs. The particle size distribution is expressed by the geometrical standard deviation (σ g ). The major axial diameters of 350 particles were measured from electron micrographs (x 120,000) and the actual major axial diameters were calculated from the measured values. A cumulative amount (%) obtained from the number of the particles belonging to each regular interval of the particle diameter was plotted in a logarithmicro-normal probability paper with particle diameter (µm) as abscissa and cumulative amount (%) as ordinate in accordance with a statistical method from the actual particle diameter and the number of the particles. A particle diameter (D 50 ) when the cumulative amount is 50% and a particle diameter (D 84.13 ) when the cumulative amount is 84,13%, were read out of the obtained log-normal distribution graph. The geometric standard deviation (σ g ) was found by dividing the particle diameter (D 50 ) by the particle diameter (D 84.13 ) [ σ g =D 50/ D 84.13 ]. The magnetic characteristics and the coating film properties of the magnetic iron oxide particles were measured by using an "sample vibrating type magnetometer VSM-3S-15", (produced by Toei Kogyo K.K.) and applying an external magnetic field up to 5 KOe in case of acicular magnetite particles and acicular maghemite particles, or an external magnetic field up to 10 KOe in case of acicular magnetic iron oxide particles modified with Co or Co and Fe 2+ . A sheet-like sample obtained by a method shown in later-described Example 52 was used for measuring the squareness and the S.F.D. of the coating film. The S.F.D. was measured by using a differentiation circuit of the above-described magnetometer to obtain the differentiation curve of the demagnetizing curve of the magnetism hysteresis curve, measuring the half-width value of the curve and dividing the half-width by the coercive force. 〈Production of Acicular Goethite Particles〉 Examples 1 to 7 Comparative Examples 1 to 3 Example 1 464 l of an aqueous ferrous sulfide solution containing 1.50 mol/ l of Fe 2+ and 228 l of 2.7-N aqueous NaOH solution (the content of NaOH corresponds to 0.42 equivalents based on Fe 2+ in the aqueous ferrous sulfide solution) were mixed to produce at 40°C at pH 6.8 an aqueous ferrous sulfide solution containing Fe(OH) 2 . To the aqueous ferrous sulfide solution containing Fe(OH) 2 , 0.1 l of an aqueous solution containing 23.8 g of ascorbic acid (corresponding to 0.35 mol% based on Fe) was added, and an air was then blown thereinto at a rate of 800 l per minute at 40°C for 6.8 hours, thereby producing goethite nucleus particles. A part of the reaction solution was extracted, filtered out, washed with water and dried by an ordinary method. The electron micrograph (x 30000) of the particles obtained is shown in Fig. 1. The acicular goethite particles produced had a major axial diameter of 0.214 µm and an aspect ratio (major axial diameter:minor axial diameter) of 28:1, as shown in the Fig. 1. The particle size distribution was uniform as expressed by a geometric standard deviation (σ g )of 0.829, and no dendrites were included therein. The goethite particles were used as acicular goethite nucleus particles, and 208 l of 7.0-N aqueous Na 2 CO 3 solution (the content of Na 2 CO 3 corresponds to 1.8 equivalents based on Fe 2+ in the residual aqueous ferrous sulfide solution) was added to the aqueous ferrous sulfide solution containing the acicular goethite nucleus particles (the amount of existent goethite nucleus particles corresponds to 42 mol% of the amount of goethite particles produced). Air was blown into the resultant solution at a rate of 800 l per minute at 50°C at pH 8.9 for 2.0 hours, thereby producing goethite particles. The goethite particles produced were filtered out, washed with water and dried by an ordinary method. The goethite particles produced were acicular particles having a major axial diameter of 0.267 µm and an aspect ratio (major axial diameter:minor axial diameter) of 28:1, as shown in the electron micrograph (x 30000) in Fig. 2. The particle size distribution was uniform as expressed by a geometric standard deviation (σ g ) of 0.817, and no dendrites were included therein. Examples 2 to 7, Comparative Examples 1 to 3 Acicular goethite particles were produced in the same way as in Example 1 except for varying the kind and amount of aqueous ferrous salt solution used, the kind, concentration and amount of aqueous alkaline solution, the kind and amount of ascorbic acid or a salt thereof used, the time for adding the ascorbic acid or a salt-thereof, the kind and amount of additional element and the reaction temperature in the process for producing acicular goethite particles or acicular goethite nucleus particles; and the amount of existent goethite nucleus particles, the kind, concentration and amount of aqueous alkaline solution, the kind and amount of additional element and the reaction temperature in the process for growing the goethite nuclear particles. The main conditions for production and the properties of the goethite particles obtained are shown in Tables 1 and 2. In Comparative Examples 2 and 3, acicular goethite nucleus particles were not produced through green rust but acicular goethite particles were directly produced by blowing an oxygen-containing gas at a pH of not less than 11. Figs. 3 and 4 are electron micrographs (x 30000) of the acicular goethite nucleus particles and the acicular goethite particles, respectively, obtained in Example 3, Figs. 5 and 6 are electron micrographs (x 30000) of the acicular goethite nucleus particles and the acicular goethite particles, respectively, obtained in Comparative Example 1, and Figs. 7 and 8 are electron micrographs (x 30000) of the acicular goethite particles obtained in Comparative Examples 2 and 3, respectively. As a result of observation through an electron microscope, it was proved that all of the acicular goethite particles obtained in Examples 2 and 4 to 7 had a uniform particle size distribution, no inclusion of dendrites and a large aspect ratio (major axial diameter:minor axial diameter). The particle size distributions of the acicular goethite particles obtained in Comparative Examples 1 and 3 were non-uniform and dendrites were included therein, as shown in the electron micrographs in Figs. 6 and 8. The aspect ratio (major axial diameter:minor axial diameter) of the acicular goethite particles obtained in Comparative Example 2 was small. 〈Production of Acicular Magnetite Particles〉 Examples 8 to 16 Comparative Examples 4 to 6 Example 8 16.7 kg of the paste of the acicular goethite particles (corresponding to about 5.0 kg of acicular goethite particles) obtained in Example 1 and filtered out and washed with water was suspended in 88 l of water. The pH of the suspension was 7.5. Thereafter, 750 ml of an aqueous solution containing 75 g of sodium hexametaphosphate (corresponding to 1.15 wt% calculated as PO 3 based on the acicular goethite particles) was added to the suspension, and the mixture was stirred for 30 minutes. The resultant suspension was filtered and dried to obtain acicular goethite particles with the surfaces coated with a P compound. The thus-obtained acicular goethite particles coated with a P compound were heat-treated in air at 320°C, thereby obtaining acicular hematite particles coated with a P compound. 1000 g of the thus-obtained acicular hematite particles coated with a P compound were charged into a retort reducing vessel, and H 2 gas was blown into the particles at a rate of 2 l per minute while rotating the vessel to reduce them at 360°C, thereby obtaining acicular magnetite particles coated with a P compound. It was observed through an electron microscope that the acicular magnetite particles coated with a P compound had an average major axial diameter of 0.18 µm, an aspect ratio (major axial diameter:minor axial diameter) of 7.9:1, that the particle size distribution was uniform as expressed by a geometric standard deviation (σ g ) of 0.66 and that no dendrites were included. When the magnetic characteristics were measured, the coercive force (Hc) was 387 Oe and the saturation magnetization (σ s ) was 83.8 emu/g. Examples 9 to 16, Comparative Examples 4 to 6 Acicular magnetite particles were obtained in the same way as in Example 8 except for varying the kind of the starting material, the execution or omission of the P-compound coating step, the execution or omission of the heat treatment in air and the heat-treating temperature. The main conditions for production and the properties of the acicular magnetite particles obtained are shown in Table 3. As a result of observation through an electron microscope, all of the acicular magnetite particles obtained in Examples 9 to 16 proved to have a uniform particle size distribution and no inclusion of dendrites. 〈Production of Acicular Maghemite Particles〉 Examples 17 to 25 Comparative Examples 7 to 9 Example 17 300 g of the acicular magnetite particles coated with a P compound obtained in Example 8 were oxidized in air at 300°C for 60 minutes to obtain acicular maghemite particles with the surfaces coated with a P compound. It was observed through an electron microscope that the acicular maghemite particles coated with a P compound had an average major axial diameter of 0.17 µm, an aspect ratio (major axial diameter:minor axial diameter) of 7.8:1, the particle size distribution was uniform as expressed by a geometric standard deviation (σ g )of 0.65 and no dendrites were included. When the magnetic characteristics were measured, the coercive force (Hc) was 354 Oe and the saturation magnetization (σ s ) was 73.6 emu/g. Examples 18 to 25, Comparative Examples 7 to 9 Acicular maghemite particles were obtained in the same way as in Example 17 except for varying the kind of acicular magnetite particles. The main conditions for production and the properties of the maghemite particles obtained are shown in Table 4. As a result of observation through an electron microscope, all of the acicular maghemite particles obtained in Examples 18 to 25 proved to have a uniform particle size distribution and no inclusion of dendrites. 〈Production of Acicular Co-Modified Magnetite Particles〉 Examples 26 to 38 Comparative Examples 10 to 12 Example 26 100 g of the acicular magnetite particles with the surfaces coated with a P compound obtained in Example 14 were charged into 1.0 l of water with 0.085 mol of cobalt and 0.179 mol of ferrous dissolved therein by using cobalt sulfate and ferrous sulfate while preventing the inclusion of air as much as possible, and dispersed until the dispersion became a fine slurry. Into the dispersion, 102 ml of 18-N aqueous NaOH solution was poured and water was further added so as to form 1.3 l of a dispersion in which the hydroxyl concentration was 1.0 mol/ l . The temperature of the dispersion was raised to 100°C and it was stirred for 5 hours. Thereafter, the slurry was taken out, washed with water, filtered out and dried at 60°C to obtain acicular Co-modified magnetite particles. As a result of observation through an electron microscope, it was proved that the acicular magnetite particles modified with Co and Fe 2+ obtained had the same shape and the particle size as the precursor particles, namely, the acicular magnetite particles with the surfaces coated with a P compound, an average major axial diameter of 0.28 µm and an aspect ratio (major axial diameter:minor axial diameter) of 7.1:1. The particle size distribution was uniform as expressed by a geometric standard deviation (σ g )of 0.56. When the magnetic characteristics were measured, the coercive force (Hc) was 803 Oe and the saturation magnetization (σ s ) was 83.1 emu/g. Examples 27 to 38, Comparative Examples 10 to 12 Acicular magnetite particles modified by Co or Co and Fe 2+ were obtained in the same way as in Example 26 except for varying the kind of precursor particles, the amounts of Co added, Fe 2+ added and NaOH added under conditions that the amount of precursor magnetite particles was 100 g and the whole volume of the dispersion was 1.3 l . The main conditions for production and the properties of the particles obtained are shown in Table 5. 〈Production of Acicular Co-Modified Maghemite Particles〉 Examples 39 to 51 Comparative Examples 13 to 15 Example 39 100 g of acicular maghemite particles with the surfaces coated with a P compound obtained in Example 23 were charged into 1.0 l of water with 0.085 mol of cobalt and 0.179 mol of ferrous dissolved therein by using cobalt sulfate and ferrous sulfate while preventing the inclusion of air as much as possible, and dispersed until the dispersion became a fine slurry. Into the dispersion, 102 ml of 18-N aqueous NaOH solution was poured and water was further added so as to form 1.3 l of dispersion in which the hydroxyl concentration was 1.0 mol/ l . The temperature of the dispersion was raised to 100°C and it was stirred for 5 hours. Thereafter, the slurry was taken out, washed with water, filtered out and dried at 60°C to obtain acicular Co-modified maghemite particles. As a result of observation through an electron microscope, it was proved that the acicular maghemite particles modified with Co and Fe 2+ obtained had the same shape and the particle size as the precursor particles, namely, the acicular maghemite particles with the surfaces coated with a P compound, an average major axial diameter of 0.27 µm and an aspect ratio (major axial diameter:minor axial diameter) of 7.0:1. The particle size distribution was uniform as expressed by a geometric standard deviation (σ g )of 0.56. When the magnetic characteristics were measured, the coercive force (Hc) was 779 Oe and the saturation magnetization (σ s ) was 76.3 emu/g. Examples 40 to 51, comparative Examples 13 to 15 Acicular maghemite particles modified by Co or Co and Fe 2+ were obtained in the same way as in Example 39 except for varying the kind of the precursor particles, the amounts of Co added, Fe(II) added and NaOH added and the treating temperature and time under conditions that the amount of precursor acicular maghemite particles was 100 g and the whole volume of the dispersion was 1.3 l . The main conditions for production and the properties of the particles obtained are shown in Table 6. 〈Production of Magnetic Tape〉 Examples 52 to 95 Comparative Examples 16 to 27 Example 52 A magnetic tape was produced in the following manner. A magnetic coating was prepared by charging the acicular magnetic iron oxide particles with the surfaces coated with a P compound obtained in Example 8, the resin and the solvents described below into a 140-cc glass bottle in the following amounts and mixing and dispersing the above materials by a paint conditioner for 2 hours. The magnetic coating was applied to a polyethylene terephthalate film (25 µm thick) to a thickness of 40 µm by an applicator, and the film was then oriented and dried in a magnetic field of 1450 Gauss. Glass beads 1.5 mm diameter 100 g Acicular magnetite particles 15 g Toluene 5.6 g Phosphate ester (GAFAC RE-610, produced by Toho Chemical Industrial Co., Ltd.) 0.6 g Lecithin 0.6 g Vinyl chloride-vinyl acetate copolymer resin (Vinilite VAGH produced by Union Carbide) 3.75 g Butadiene acrylonitrile rubber (Hycar 1432 J, produced by Japanese Geon Co., Ltd.) 0.75 g Mixed solution of Methyl isobutyl keton, methyl ethyl ketone and toluene (3 : 1 : 1) 40.5 g The magnetic tape produced had and an S.F.D. of 0.50, a coercive force (Hc) of 355 Oe, a residual flux density (Br) of 1660 Gauss and a squareness (Br/Bm) of 0.81. Examples 53 to 95, Comparative Examples 16 to 27 Magnetic tapes were produced in the same way as in Example 52 except for varying the kind of magnetic particles. The acicular maghemite particles were oriented in a magnetic field of 1450 Gauss and the Co-modified magnetic iron oxide particles were oriented in a magnetic field of 1900 Gauss. The properties of the magnetic tapes obtained are shown in Tables 7 to 10. Examples & Comparative Examples Magnetic particles (Example No. & Comparative Example No.) Tape properties S.F.D. Squareness (Br/Bm) Coercive force Hc (Oe) Residual flux density Br (Gauss) Example 52 Example 8 0.50 0.81 355 1610 Example 53 Example 9 0.52 0.81 368 1570 Example 54 Example 10 0.48 0.83 369 1620 Example 55 Example 11 0.45 0.78 370 1510 Example 56 Example 12 0.54 0.79 353 1560 Example 57 Example 13 0.44 0.83 392 1610 Example 58 Example 14 0.43 0.86 395 1580 Example 59 Example 15 0.42 0.85 394 1550 Example 60 Example 16 0.56 0.78 340 1520 Comparative Example 16 Comparative Example 4 0.67 0.72 362 1390 Comparative Example 17 Comparative Example 5 0.61 0.66 335 1260 Comparative Example 18 Comparative Example 6 0.75 0.68 292 1340 Examples & Comparative Examples Magnetic particles (Example No. & Comparative Example No.) Tape properties S.F.D. Squareness (Br/Bm) Coercive force Hc (Oe) Residual flux density Br (Gauss) Example 61 Example 17 0.40 0.84 330 1440 Example 62 Example 18 0.41 0.84 345 1310 Example 63 Example 19 0.39 0.86 348 1410 Example 64 Example 20 0.36 0.81 350 1480 Example 65 Example 21 0.44 0.83 353 1360 Example 66 Example 22 0.35 0.85 369 1400 Example 67 Example 23 0.33 0.88 378 1370 Example 68 Example 24 0.32 0.88 377 1320 Example 69 Example 25 0.45 0.79 310 1280 Example 19 Example 7 0.58 0.75 332 1210 Example 20 Example 8 0.70 0.69 305 1100 Example 21 Example 9 0.67 0.71 258 1160 Examples & Comparative Examples Magnetic particles (Example No. & Comparative Example No.) Tape properties S.F.D. Squareness (Br/Bm) Coercive force Hc (Oe) Residual flux density Br (Gauss) Example 70 Example 26 0.46 0.86 831 1620 Example 71 Example 27 0.43 0.86 730 1650 Example 72 Example 28 0.42 0.87 764 1645 Example 73 Example29 0.39 0.88 713 1670 Example 74 Example 30 0.37 0.89 681 1595 Example 75 Example 31 0.53 0.81 870 1570 Example 76 Example 32 0.55 0.80 863 1500 Example 77 Example 33 0.51 0.83 865 1610 Example 78 Example 34 0.49 0.79 840 1555 Example 79 Example 35 0.57 0.78 839 1510 Example 80 Example 36 0.46 0.83 842 1600 Example 81 Example 37 0.45 0.84 829 1570 Example 82 Example 38 0.58 0.77 871 1490 Comparative Example 22 Comparative Example 10 0.69 0.71 710 1380 Comparative Example 23 Comparative Example 11 0.65 0.65 805 1290 Comparative Example 24 Comparative Example 12 0.77 0.67 793 1310 Examples & Comparative Examples Magnetic particles (Example No. & Comparative Example No.) Tape properties S.F.D. Squareness (Br/Bm) Coercive force Hc (Oe) Residual flux density Br (Gauss) Example 83 Example 39 0.36 0.87 807 1540 Example 84 Example 40 0.35 0.88 710 1580 Example 85 Example 41 0.34 0.88 740 1590 Example 86 Example 42 0.31 0.90 690 1580 Example 87 Example 43 0.30 0.90 650 1460 Example 88 Example 44 0.43 0.82 852 1495 Example 89 Example 45 0.44 0.82 843 1430 Example 90 Example 46 0.41 0.85 846 1540 Example 91 Example 47 0.38 0.82 824 1510 Example 92 Example 48 0.47 0.80 816 1440 Example 93 Example 49 0.38 0.85 820 1540 Example 94 Example 50 0.35 0.86 712 1500 Example 95 Example 51 0.47 0.79 848 1430 Comparative Example 25 Comparative Example 13 0.56 0.74 770 1360 Comparative Example 26 Comparative Example 14 0.68 0.67 757 1210 Comparative Example 27 Comparative Example 15 0.69 0.70 760 1290

Claims: A process for producing acicular goethite particles which process comprises: (i) reacting an aqueous ferrous salt solution with less than one equivalent of an aqueous alkali hydroxide solution and/or an aqueous alkali carbonate solution based on Fe 2+ in said aqueous ferrous salt solution; and (ii) blowing a molecular oxygen-containing gas into the ferrous salt reaction solution containing colloidal ferrous hydroxide or iron-containing colloidal precipitates thus obtained in the presence of ascorbic acid or a salt thereof so as to oxidize said colloidal ferrous hydroxide or iron-containing colloidal precipitates and to produce acicular goethite particles through green rust. A process according to claim 1, wherein said ascorbic acid or a salt thereof together with a zinc compound are present in any of the solutions before said acicular goethite particles are produced. A process according to claim 2, wherein the salt of ascorbic acid is sodium ascorbate and the zinc compound is zinc sulphate, zinc chloride or zinc nitrate. A process according to claim 1, 2 or 3, wherein in step (ii) acicular goethite nucleus particles are produced through green rust, and grown so as to produce the acicular goethite particles. A process according to any one of the preceding claims for producing acicular magnetic iron oxide particles which process further comprises (iii) heat-treating in a reducing gas the thus produced acicular goethite particles or acicular hematite particles which are obtained by heat-treating at from 300 to 700°C the thus produced acicular goethite particles, thereby producing acicular magnetite particles, and (iv) if necessary, oxidizing said acicular magnetite particles, thereby producing acicular maghemite particles. A process according to claim 5 for producing acicular magnetic iron oxide particles which process further comprises (v) dispersing said acicular magnetite particles or acicular maghemite particles as precursor particles in an alkaline suspension containing cobalt hydroxide or an alkaline suspension containing cobalt hydroxide and ferrous hydroxide so that the Co content in said suspension is from 0.1 to 21.0 atomic% based on the Fe in said precursor particles; and (vi) heat-treating the resultant aqueous dispersion, thereby obtaining acicular magnetite particles or acicular maghemite particles modified with Co or Co and Fe 2+ . A process according to claim 4 or 5, which further comprises forming a magnetic recording medium utilising the particles thus produced. Acicular goethite particles having a major axial diameter of 0.1 to 0.6 µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 20:1, and a particle size distribution of not less than 0.55, and obtainable by a process according to claim 1 or 4. Acicular magnetic iron oxide particles comprising: acicular magnetite particles having a major axial diameter of 0.05 to 0.5 µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 6.0:1 and a particle size distribution (geometric standard deviation (σ g )) of not less than 0.5 and obtainable by a process according to claim 5; or acicular maghemite particles having a major axial diameter of 0.05 to 0.5 µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 6.0:1 and a particle size distribution (geometric standard deviation (σ g )) of not less than 0.45 and obtainable by a process according to claim 5. Acicular magnetic iron oxide particles comprising: acicular magnetite particles modified with Co or Co and Fe 2+ having a major axial diameter of 0.05 to 0.5 µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 5.5:1 and a particle size distribution (geometric standard deviation (σ g )) of not less than 0.45, containing from 0.1 to 21.0 atomic % of Co based on the Fe in the precursor particles and from 0 to 25 atomic % of coated Fe 2+ based on the Fe in the precursor particles and obtainable by a process according to claim 6; or acicular maghemite particles modified with Co or Co and Fe 2+ having a major axial diameter of 0.05 to 0.5 µm, an aspect ratio (major axial diameter:minor axial diameter) of not less than 5.5:1 and a particle size distribution (geometric standard deviation (σ g )) of not less than 0.4, containing from 0.1 to 21.0 atomic % of Co based on the Fe in the precursor particles and from 0 to 25 atomic % of coated Fe 2+ based on the Fe in the precursor particles and obtainable by a process according to claim 6.

Inventors: FUJITA KAZUHIRO, HARADA TOSIHARU, ISOAI MASARU, JIKUHARA SHIGEKAZU, KURATA TOKIHIRO, TAKAMA KAZUSHI, FUJITA, KAZUHIRO, HARADA, TOSIHARU, ISOAI, MASARU, JIKUHARA, SHIGEKAZU, KURATA, TOKIHIRO, TAKAMA, KAZUSHI
Applicants: TODA KOGYO CORP, TODA KOGYO CORP.
Application year: 1991
Main classification: C01G49
IPC codes: C01G49