Mask for photolithography

Abstract: A mask for photolithography having a transparent substrate (1) which allows light having a predetermined wavelength to pass therethrough; an opaque pattern (4) provided on said substrate for inhibiting the light from passing therethrough; and a stepped portion (6) provided adjacent to said opaque pattern on said substrate and having an inclined area, said stepped portion being transparent for allowing the light to pass therethrough, which can be used in a photolithographic system in fabrication of semiconductor devices and the like.

Description: Background of the Invention 1. Field of the Invention The present invention relates to a mask used in a photolithographic system in fabrication of semiconductor devices and the like. 2. Description of the Prior Arts ULSI semiconductor devices which have been produced in recent years assemble a large number of transistors and wirings in micron on a single silicon substrate. Used for formation of the patterns of the transistors and wirings in micron is a photolithographic technology, such as stepper (step and repeat photolithographic system with demagnification), transferring a mask's pattern in a reduced size (usually to one fifth) onto a photosensitive resin (resist) layer formed on the silicon substrate of the semiconductor devices. The photolithographic system (the stepper) which is now applied to mass production of 1MB and 4MB DRAM devices uses the mask patterns having the respective minimum line widths of 1.2 and 0.8µm for each DRAM device, and generally adopts emission lines called g-light of 436nm emitted by and ultra high-pressure mercury-vapor lamp, while emission lines called i-light of 365nm emitted by the same lamp has been locally used. It is expected that each of 16MB and 64MB DRAM devices intended to be produced in the future will use 0.6 to 0.5µm and 0.4 to 0.3µm of the minimum line widths, respectively. For mass production of these semiconductor devices, an advanced photolithographic technology with the higher resolution needs to be developed. In order to improve the resolution by using light of shorter wavelengths, use of the i-lines in place of the g-lines, and KrF excimer laser of 248 nm have been studied. In the above photolithographic system using the mask comprising a transparent substrate made of quartz with an opaque pattern generally of a thin metal layer disposed thereon, light is applied to the mask from the back thereof and light flux passing through the mask is converged on the substrate to form an image in a reduced size through a projection lens. Contrast of the image on the substrate is deteriorated due to diffraction of the light at the mask pattern edge as the mask pattern size approaches specific wavelengths of the light, resulting in the extremely poor resolution of the light in comparison with critical resolution defined by NA of numerical aperture of the projection lens and the wavelengths of the light. A new method to improve a pattern structure on the mask, achieve a higher contrast of the image and remarkably improve the resolution of the photolithography has been proposed previously. The above previously proposed method uses a mask called a phase shifting mask as exemplified in Fig. 5 which mask comprises a transparent quartz substrate 51 to admit light of any wavelengths, a chromium thin film 52 for obstructing applied light, and a transparent thin film 53 (phase shifting film) to admit applied light, the thickness t s of the thin film 53 having the following relationship with its refractive index n and wavelengths λ of applied light: T s = λ /{2·(n - 1)} which condition sets the phase of applied light passing through the thin film 53 to be shifted half the cycle of waves. The phase shifting mask also has an opening 54 provided as conventionally and fine apertures 55 adjacent to the opening 54. The fine apertures 55, 55' do not themselves dissect the projected image and are aligned with the phase shifting film 53. Light from the opening 54 is shifted by 180° relative to light from the apertures 55, so that light waves diffracted from the opening 54 to its adjacent area are antiphase with light wave from the apertures 55. Accordingly, light on the projection area is restrained from spreading from the opening 54 to its adjacent area, thereby improving contrast of the projected image. Hence, the phase shifting mask improves contrast of an image projected on the resist layer so as to greatly improve the practical resolution. For preparation of the phase shifting mask, a first resist image for a chromium pattern is first drawn by use of an electron beam lithographic system, and a second resist image is then drawn for defining a phase shifting film. As a result the system must twice conduct electron beam drawing, which takes longer time, and also must accurately align the first pattern with the second pattern, which leads to a complex and expensive technology for preparation of the mask. To solve these problems, another phase shifting mask shown in Fig. 6 has been proposed, which comprises a transparent quartz substrate 61 to admit applied light of any wavelength, a chromium film 62 obstructing the applied light and a phase shifting film 63 whose thickness satisfies the relationship of the foregoing formula (1). For preparation of the phase shifting mask, an opening 64 is first formed in a resist film (not shown) by use of an electron beam lithographic system and the chromium film 62 is then etched and removed at the part of the opening 64, while the resist film is also removed. Next, a resist film for forming the phase shifting film 63 is formed and ultraviolet light is applied from the back of the substrate to the resist film at the opening 64; the resist film is then developed and removed. The chromium film 62 is etched partially under the resist film to have an opening larger than the opening 64 and having a region 65 over which the resist film hangs. Light passing through the region 65 and light passing through the opening 64 are different in phase by 180° from each other, so that they are antiphase with each other when they are overlapped in a projected image, thereby preventing the light from spreading from the region 64 to its adjacent part. Hence, dispersion of photo-intensity on an image formation surface is sharp so tat the practical resolution of photolithography is improved. The preparation method for this phase shifting mask does not involve an increase in the number of times of drawing by the electron beam lithographic system, nor in turn, the number of steps for preparation of the mask. However, since the resist film which is kept for forming the phase shifting film is fragile, it is hard to wash and remove foreign particles on the mask. Thus, the method is not practical. Besides, the phase shifting masks as discussed above or similar thereto are disclosed in e.g., Japanese Patent Publication No. 62(1987)-50811 (JP-B2-62 050 811), Japanese Unexamined Patent Publication Nos. 58(1983)-173744, 62(1987)-67514, 1(1990)-147457 & 1(1990)-283925 and IEDM 1989, p57 (New Phase Shifting Mask with Self-aligned Phase Shifters for a Quarter Micron Photolithography). As seen from the above, the previously proposed phase shifting mask has certain problems in practical use, and there has been a need for a phase shifting mask which is simple in fabrication and has sufficient durability. Summary of the Invention. The present invention provides a mask for photolithography comprising: a substrate which is transparent to light having a predetermined wavelength; an opaque pattern provided on said substrate for inhibiting the light from passing therethrough; and phase shift means which is transparent to said light and is provided adjacent to the edge of said opaque pattern on said substrate, characterised in that said phase shift means comprises a step portion having a surface which is inclined with respect to the substrate, the thickest part of said transparent step portion lying closest to said edge of said opaque pattern and having a height substantially equal to λ/{2(n-1)} where λ represents the wavelength of light to be used in said photolithography, and n represents the refractive index of the material forming said phase shift means so that the amount of phase shift introduced in the light passing through said thickest part of said step portion is approximately 180°. The present invention also provides a process for manufacturing a mask for photolithography including a substrate which is transparent to light having a predetermined wavelength, said process comprising the steps; (1) forming a shield film which is opaque to said light on said substrate; (2) forming a resist film to electron beam on said shield film and forming a resist pattern on said resist film by drawing a predetermined pattern with an electron beam lithographic apparatus and then developing thus formed pattern; (3) etching said shield film by anisotropic etching using said resist pattern as a mask so as to form an opaque pattern on said substrate; and (4) laminating a transparent film on said substrate including said opaque pattern, by removing or without removing said resist pattern, whereby a phase shift means is formed comprising a transparent step portion formed adjacent to the edge of the opaque pattern, said transparent step portion having a surface which is inclined with respect to the substrate, and the thickest part of said transparent step portion lying closest to said edge of said opaque pattern and having a height substantially equal to λ/{2(n-1)} where λ represents the wavelength of light to be used in said photolithography, and n represents the refractive index of the material forming said transparent film. Preferred further features of the mask and method are set forth in the appended claims 2 to 10 and 12 to 16, respectively. Brief Description of The Drawings Figs. 1 (a) to (c), Figs. 2 (a) to (c), Figs. 3 (a) to (d), Figs. 4 (a) to (d), Figs. 7 (a) to (c) and Figs. 8 (a) to (c) are schematic diagrams showing the fabrication processes of the mask in six examples of the present invention. Figs. 5 and 6 are schematic diagrams showing the problematic points in the conventional phase shifting masks. Fig. 9 is a schematic diagram showing the thickness of the SOG film. Preferred Embodiment of the Invention A step portion having an inclined area is formed to a height substantially defined by the foregoing formula (1). A transparent film is formed to a thickness approaching the height of the step portion on an opaque pattern of relatively larger thickness in accordance with vapor phase CVD process, or by spin coating. In this case, the opaque pattern may be a thin film of single phase or a multi-layer of a thin opaque film and a transparent film or a resist pattern. The opaque pattern may be provided on the transparent substrate or by etching the transparent substrate. Also, the step portion having the inclined area can be formed by depositing or applying a transparent film of a thickness approaching the foregoing formula (1) on an opaque pattern of relatively larger thickness in accordance with vapor phase CVD process, or by spin coating followed by anisotropic etching to leave the transparent film on the side wall of the opaque pattern. In this case, the opaque pattern may be a thin film of single phase or a multi-layer of a thin opaque film and a transparent film. Also, the opaque pattern may be provided on the transparent substrate or by etching the transparent substrate. Furthermore, the step portion having the inclined area may be formed by etching the opaque film of the opaque pattern and then tapering the surface of the transparent substrate to the thickness approaching the foregoing formula (1). Using any of these techniques, pattern formation by use of an electron beam lithographic apparatus needs to be performed only once, the phase shifting region being provided by self-alignment. The phase shifting region comprises a film deposited by CVD process or formed by spin coating, or by the transparent substrate itself, so that the region will be not damaged by, for example, washing the mask. The mask described herein provides an inclined area at the border between the transparent region and the opaque region so as to allow phase shifting of the light passing through the phase shifting region to increase continuously from the transparent region to the opaque region. Hence, when the phase shifting at the edge of the transparent region is set to a value approaching 180°, the light passing through the transparent region does not decay unexpectedly, and thus sharp shaping up can be confined to the edge of the light flux passing through the transparent region. Example 1 Hereinafter, an example of the invention will be described in conjunction with Fig. 1. A shield film 2 was deposited on a substrate 1 made of quartz, on which a resist layer to electron beam was formed followed by drawing thereon a predetermined pattern by use of an electron beam lithographic apparatus before development to obtain a resist pattern 3 (see Fig. 1(a)). The shield film 2 was then etched by anisotropic etching using the resist pattern 3 as a mask to form an opaque pattern 4 followed by removing the resist layer (see Fig. 1(b)). On the quartz substrate 1 having the opaque pattern 4 formed in the above step was deposited a transparent film 5 by CVD process to complete the mask fabrication process (see Fig. 1(c)). The method in this example shapes the end of the opaque pattern 4 at an angle as extending almost vertically and the CVD film deposited on the stepped side wall portion by CVD process is used as the phase shifting film. The profile of the CVD film is a quarter arc as seen in Fig. 1(c) and the portion of the CVD film denoted by 6 is a step portion serving as the phase shifting region. In this example, an effective thickness of the phase shifting region at the edge of the opaque pattern is almost equal to that of the opaque pattern. Hence, the thickness of the shield film 2 was set in accordance with the foregoing formula (1). The length of the phase shifting region is related to the thickness of the transparent film 5 deposited on the side wall and may therefore be selectively set corresponding to such thickness of the transparent film 5. An important factor is the thickness of the step portion 6 of the transparent film 5, which is likely to be thinner than the flat portion or varies depending on various CVD processes or systems applied. In the process of fabrication of a phase shifting mask for the stepper using i-light (365nm) in accordance with the present example, a double-layered metal film made of molybdenum(Mo)/Titanium(Ti) of 400nm in total thickness was used as the shield film. Etching was conducted by use of a reactive ion-etching system having parallel plate electrodes using reaction gas of carbon tetrachloride (CCl 4 ) + oxygen (O 2 ). Applied as the transparent CVD film was silicon oxide film (SiO 2 ) of 400nm thickness, formed by normal pressure CVD process using material gas of silane (SiH 4 ) + oxygen (O 2 ). The thickness of oxide film on the side wall portion was about 300nm. The specific techniques for these processes are known in the art of fabrication of IC. Exposure test was conducted by use of the stepper with i-light of 0.45 of NA and using the phase shifting mask fabricated with the above materials and steps. The phase shifting mask obtained in the present example had a line/space resolution of 0.35 µm, an improvement of more than 10% over the conventional mask exhibiting a resolution of 0.4 µm. Various materials and techniques other than the above may be used for this example. The shield film may be a metal film made of tungsten, chromium, cobalt, nickel, aluminum or the like, a silicon metal compound made of tungsten silicide (WSi 2 ), molybdenum silicide (MoSi 2 y) or the like, or a semiconductor film made of silicon alloy, silicon or the like. Any suitable etching techniques other than reactive ion etching may be applied depending on the material of the shield film. The shield film when using a metal such as molybdenum or the like may provide a pattern with the edge being inclined almost at 90° by use of liquid phase etching. Also, the transparent film may be a thin transparent film made of silicon-phosphorus glass, silicon-phosphorus-boron glass, silicon nitride or the like. Deposition may be conducted by reduced pressure CVD process, plasma CVD process or the like other than normal pressure CVD process. Furthermore, the transparent film may be a thin transparent film made of silicon-phosphorus glass, silicon-phosphorus-boron glass or the like formed by spin coating. The shield film is not limited to a single opaque film and may be multi-layered with a transparent film and an opaque film. The transparent film is not limited to a single layer and may be multi-layered. Example 2 The second example of the invention will be described in conjunction with Fig. 7. A shield film 72 was deposited on a substrate 71 made of quartz, on which a resist layer to electron beam was formed followed by drawing thereon a predetermined pattern by use of electron beam lithographic system before development to obtain a resist pattern 73 (see Fig. 7(a)). The shield film 72 was then etched by normal liquid phase etching using the resist pattern 73 as a mask to form an opaque pattern 74 (see Fig. 7(b)). On the quartz substrate 71 having the resist pattern 73 and the opaque pattern 74 was deposited a transparent film 75 of SiO 2 by normal pressure CVD process using material gas of silane (SiH 4 ) + oxygen (O 2 ) to complete the mask fabrication process (see Fig. 7(c)). The second example had the same result as that of Example 1. The transparent film may be a thin transparent film made of silicon-phosphorus glass, silicon-phosphorus-boron glass, silicon nitride or the like other than the above SiO 2 . Deposition may be conducted by reduced pressure CVD process, plasma CVD process or the like other than normal pressure CVD process. Furthermore, the shield film may be formed by selectively using various materials, fabrication techniques and processing, as in Example 1. Example 3 The third example of the invention will be described in conjunction with Fig. 8. A shield film 82 was deposited on a substrate 81 made of quartz, on which a resist layer to electron beam was formed followed by drawing thereon a predetermined pattern by use of electron beam lithographic system before development to obtain a resist pattern 83 (see Fig. 8(a)). The shield film 82 was then etched by normal liquid phase etching using the resist pattern 83 as a mask to form an opaque pattern 84 (see Fig. 8(b)). On the quartz substrate 81 having the resist pattern 83 and the opaque pattern 84 formed in the above steps was coated SOG followed by baking to form a transparent film 85 to complete the mask fabrication process (see Fig. 8(c)). In this example, the edge of the resist pattern 83 and the opaque pattern 84 form a step having preferably an angle extending almost vertically. Also, the combination of the material for resist layer and SOG solution must be such that the resist layer is not dissolved upon coating of SOG solution. The SOG film at the step has an inclined feature as seen in Fig. 8(c), and the step portion of the SOG film denoted by 86 serves as the phase shifting region. The maximum thickness Ts of the phase shifting region formed by spin coating of transparent SOG has a relationship with respect to the difference of height Td between the opaque pattern part and the transparent part, the thickness of SOG film T top on the opaque pattern part and the thickness of SOG film T bot on the transparent part (see Fig. 9): Ts = Td + T top - T bot wherein the maximum thickness Ts of the phase shifting region is preferably substantially equal to the thickness Ts of phase shifting film shown in the foregoing formula (1). In the fabrication process of a phase shifting mask for the stepper with i-light (365nm) in this example, a posi-type resist of 500nm was used for a resist layer forming the pattern of the shield film, and a double-layered metal film of chromium oxide/chromium (Cr) of 100nm of total thickness was applied for the shield film. Etching of the shield film was conducted by normal liquid phase etching. Transparent SOG film of 1.46 of refractivity was applied by spin coating to obtain a phase shifting region having thickness values of 300nm for T bot , 400nm for Ts and 100nm for T top . The specific techniques for these processes are known in the art of fabrication of IC. An exposure test was conducted by use of the stepper with 0.45 of NA using the phase shifting mask fabricated with the above materials and the steps. The phase shifting mask obtained in the present example had a line/space resolution of 0.35µm, an improvement of more than 10% over the conventional mask exhibiting a resolution of 0.4 µm. Various materials and techniques other than the above may be used for this example. The shield film may be a metal film made of molybdenum, tungsten, chromium, cobalt, nickel, aluminum or the like, a silicon metal compound made of tungsten silicide (WSi 2 ), molybdenum silicide (MoSi 2 ) or the like, or a semiconductor film made of silicon alloy, silicon or the like. Any suitable etching techniques other than normal liquid phase etching may be applied depending on the material of the shielding film. The shield film when using a metal such as molybdenum or the like may provide a pattern with the edge being inclined almost at 90° by use of reactive ion etching. Also, the transparent film may be a thin transparent film made of silicon-phosphorus glass, silicon-phosphorus-boron glass, or the like. The shield film is not limited to a single opaque film and may be multi-layered with a transparent film and an opaque film. The transparent film is not limited to a single layer and may be multi-layered. Example 4 The fourth example is different from Example 1 in that the surface of the substrate is etched to form a step portion. The example will be detailed with reference to Fig. 2. A shield film 22 was deposited on a substrate 21 made of quartz, on which a resist layer to electron beam was formed followed by drawing thereon a predetermined pattern by use of electron beam lithographic system before development to obtain a resist pattern 23 (see Fig. 2(a)). The shield film 22 was then etched by normal liquid phase etching using the resist pattern 23 as a mask to form an opaque pattern 24. Also, the quartz substrate 21 was etched by reactive etching using the resist pattern 23 as a mask to form a pattern 25 and this was followed by removing the resist pattern 23 (see Fig. 2(b)). On the quartz substrate 21 having the opaque pattern 24 was deposited a transparent film 26 by CVD process to complete the mask fabrication process (see Fig. 2(c)). In the example, the effective thickness of the phase shifting region on the edge of the opaque pattern is substantially equal to the height of the opaque pattern part, so that an amount of etching on the substrate was set to that obtained by deducting the thickness of the shield film 22 from the height of phase shifting region determined by the foregoing formula (1). Also, the length of the phase shifting region depends on the thickness of the transparent film 26 deposited on the side wall portion, and is adjusted corresponding to the thickness of the transparent film 26. This example had the same result as that of Example 1. Materials for the shield film, transparent film and the like, and fabrication and processing techniques thereof may be variously selected as in Example 1. Example 5 The fifth example is different from Example 1 in that the transparent film is first deposited followed by etching the transparent film at the flat portion using anisotropic etching to leave the transparent film only on the side wall part of the opaque pattern. The example will be detailed with referrence to Fig. 3. A shield film 32 was deposited on a substrate 31 made of quartz, on which a resist layer to electron beam was formed followed by drawing thereon a predetermined pattern by use of electron beam lithographic system before development to obtain a resist pattern 33 (see Fig. 3(a)). The shield film 32 was then etched by normal liquid phase etching using the resist pattern 33 as a mask to form an opaque pattern 34 followed by removing the resist pattern 33 (see Fig. 3(b)). On the quartz substrate 31 having the opaque pattern 34 was deposited a transparent film 35 by CVD process (see Fig. 3(c)). Finally, the transparent film 35 was etched back by reactive etching to leave the transparent film only on the side wall part to form a step portion 36 serving as a phase shifting region before completion of the mask fabrication process (see Fig. 3(d)). This example had the same result as that of Example 1. Materials for the shield film, transparent film and the like, and fabrication and processing techniques thereof may be variously selected as in Example 1. Example 6 The sixth example is different from Example 1 in that an inclined area is formed on the border between the transparent part and the opaque part in the step of etching of the opaque pattern. The example will be detailed with reference to Fig. 4. A shield film 42 was deposited on a substrate 41 made of quartz, on which a resist layer to electron beam was formed followed by drawing thereon a predetermined pattern by use of electron beam lithographic system before development to obtain a resist pattern 43 (see Fig. 4(a)). The shield film 42 was then etched by normal liquid phase etching using the resist pattern 43 as a mask to form an opaque pattern 44 (see Fig. 4(b)). The quartz substrate 41 was etched by reactive etching using the resist pattern 43 as a mask to form a pattern 45. In the etching, the pattern must become larger as etching proceeds. Etching of silicon dioxide is conducted generally by using reaction gas mainly made of CF 4 + H 2 or CHF 3 . The gas is likely to form polymer in vapor phase. Hence, by suitably selecting conditions for etching, polymer is deposited on the side wall part to make thicker the resultant pattern and taper the etched part during etching. The known etching technique forms the inclined area 45 on the quartz substrate adjacent to the opaque region. (see Fig. 4(c)). Finally, the resist pattern 43 was removed to complete the fabrication of the phase shifting mask (see Fig. 4(d)) This example had the same result as that of Example 1. As seen from the above, the embodiments of the present invention each provide a mask for photolithography which comprises a transparent substrate to admit visible light or ultraviolet for transferring a mask pattern which is opaque to the light and formed on the substrate, wherein a step portion having an inclined area is provided on the transparent part adjacent to the opaque pattern, so that drawing of the pattern by electron beam lithography is required only once, thereby allowing formation of a self-aligned phase shifting region. The phase shifting part is made of a SOG film, a CVD deposition film or the transparent substrate itself, thereby having little fear of being damaged in washing process or the like. Furthermore, the inclined area formed on the border between the transparent part and the opaque part allows phase shifting of light passing through the phase shifting part to be continuously increased from the transparent part to the opaque part. Hence, when the phase shifting at the edge of the transparent part is set to a value approaching 180°, sharp shaping up can be confined to the edge part of light flux passing through the transparent part without unexpectedly decaying the applied light as a whole, leading to a remarkable improvement of the resolution of photolithography in comparison with the conventional phase shifting mask.

Claims: A mask for photolithography comprising: a substrate (1;21;31;41;71;81;91) which is transparent to light having a predetermined wavelength; an opaque pattern (4;24;34;44;74;84;94) provided on said substrate for inhibiting the light from passing therethrough; and phase shift means (5;26;36;45;75;85;95) which is transparent to said light and is provided adjacent to the edge of said opaque pattern on said substrate, characterised in that said phase shift means comprises a step portion (6;26;36;45;76;86;96) having a surface which is inclined with respect to the substrate, the thickest part of said transparent step portion lying closest to said edge of said opaque pattern and having a height substantially equal to λ/{2(n-1)} where λ represents the wavelength of light to be used in said photolithography, and n represents the refractive index of the material forming said phase shift means so that the amount of phase shift introduced in the light passing through said thickest part of said step portion is approximately 180°. A mask as claimed in claim 1 wherein a transparent film (36) provided on said substrate (31) forms said transparent step portion (36), said transparent film being present only in the region that adjoins said edge of said opaque pattern (34). A mask as claimed in claim 1 wherein said edge of said opaque pattern (4;24;34;74;84;94) is formed as a side wall which is substantially vertical relative to said substrate (1;21;31;71;81;91) so as to form a substantially vertical step and wherein said transparent step portion is formed by a transparent film so formed on at least said side wall that said inclined surface is shaped approximately as a quadrant arc. A mask as claimed in claim 1 wherein a transparent film (5;26;75;85;95) provided on said substrate (1;21;71;81;91) forms said transparent step portion and extends over the opaque pattern (4;24;74;84;94). A mask as claimed in claim 1 wherein said edge of said opaque pattern (4;24;74;84;94) is formed as a side wall which is substantially vertical relative to said substrate (1;21;71;81;91) so as to form a substantially vertical step and wherein a transparent film (5;26;75;85;95) provided on said substrate extends over the opaque pattern and forms said transparent step portion (6;26;76;86;96) over the edge of said opaque pattern in the shape approximately of a quadrant arc. A mask as claimed in claim 1 wherein said substrate (21;41) includes an etched portion at or adjacent to the edge of said opaque pattern (24;44), and wherein said transparent step portion is formed on or by said etched portion of said substrate. A mask as claimed in claim 6 wherein the etched portion of the substrate (21) is a substantially vertical edge face forming with the overlying edge of said opaque pattern a substantially vertical step, said transparent step portion comprising a transparent film (26) so formed on at least said substantially vertical step that said inclined surface is shaped approximately as a quadrant arc. A mask as claimed in any of claims 3, 5 and 7 wherein said substantially vertical step has a height substantially equal to λ/{2(n-1)} . A mask as claimed in claim 6 wherein said etched portion of the substrate (41) forms the transparent step portion and includes said inclined surface (45). A mask as claimed in claim 1 wherein portions of a resist layer (73;83;93) used in the patterning of the opaque pattern (74;84;94) overly said opaque pattern. A process for manufacturing a mask for photolithography including a substrate which is transparent to light having a predetermined wavelength, said process comprising the steps; (1) forming a shield film which is opaque to said light on said substrate; (2) forming a resist film to electron beam on said shield film and forming a resist pattern on said resist film by drawing a predetermined pattern with an electron beam lithographic apparatus and then developing thus formed pattern; (3) etching said shield film by anisotropic etching using said resist pattern as a mask so as to form an opaque pattern on said substrate; and (4) laminating a transparent film on said substrate including said opaque pattern, by removing or without removing said resist pattern, whereby a phase shift means is formed comprising a transparent step portion formed adjacent to the edge of the opaque pattern, said transparent step portion having a surface which is inclined with respect to the substrate, and the thickest part of said transparent step portion lying closest to said edge of said opaque pattern and having a height substantially equal to λ/{2(n-1)} where λ represents the wavelength of light to be used in said photolithography, and n represents the refractive index of the material forming said transparent film. A process for manufacturing a mask for photolithography as claimed in claim 11 wherein said transparent film laminated in step (4) is removed except for the portion surrounding said opaque pattern, said surrounding portion providing said transparent step portion. A process for manufacturing a mask for photolithography as claimed in claim 11 wherein said etching step (3) includes etching said substrate using the resist pattern as a mask after etching said shield film, whereby the etched part of the substrate and the overlying edge of the opaque pattern forms a step on which said transparent film is laminated in step (4). A process for manufacturing a mask for photolithography as claimed in claim 11 wherein portions of the resist pattern remain on the corresponding portions of the opaque pattern so that when step (4) is performed the transparent film is laminated on a step comprising the edge of the opaque pattern and the overlying edge of the remaining resist pattern. A process for manufacturing a mask for photolithography as claimed in claim 11 wherein the height difference (Td) between the levels of the respective surfaces over the opaque pattern (84;94) on the one hand and of the substrate (81;91) on the other hand, on which the transparent film (85;95) is provided, is λ/{2(n-1)} + (T bot - T top ) when the thickness of that part of the transparent film (85;95) on said substrate in the finished mask is different from the thickness of that part of the transparent film over the opaque pattern, where T bot represents said thickness of that part of the transparent film on the substrate, T top represents the thickness of that part of the transparent film on the opaque pattern, λ represents the wavelength of light to be used in said photolithography, and n represents the refractive index of the material forming said phase shift means. A process for manufacturing a mask for photolithography as claimed in claim 11 wherein the height of a step at and including said edge of the opaque pattern, adjacent to which the transparent step portion is formed in step (4) is substantially equal to λ/{2(n-1)} .

Inventors: FUKUSHIMA TAKASHI, IGUCHI KATSUJI, TABUCHI HIROKI, FUKUSHIMA, TAKASHI, IGUCHI, KATSUJI, TABUCHI, HIROKI
Applicants: SHARP KK, SHARP KABUSHIKI KAISHA
Application year: 1991
Main classification: G03F1
IPC codes: G03F1, H01L21