Process and catalyst for preparing aromatic compounds

Abstract: A process for preparing aromatic compounds, wherein a gaseous feed containing C₆ to C₂₀ hydrocarbons is reacted in the presence of a catalyst, which catalyst comprises a metal from Group VIII of the Periodic Table loaded on a hydrotalcite-type support material having in its uncalcined state the general formula Me(II) x Me(III) y (CO₃)(OH) 2x+3y-2 · aq with an x-ray diffraction (d003) greater than about 7.4 Angstroms, and wherein Me(II) is at least one divalent metal selected from the group comprising copper, magnesium, manganese, zinc and a metal from Group VIII of the Periodic Table; Me(III) is at least one trivalent metal selected from the group comprising aluminum, chromium and iron; and x and y are positive numbers satisfying the following relationship x/y ≧ 0.5.

Description: The present invention relates to a process for the preparation of aromatic compounds by reacting a gaseous feed containing C₆ to C₂₀ hydrocarbons in the presence of a catalyst comprising a metal from Group VIII of the Periodic Table loaded on a hydrotalcite-type support material. Presently, most used aromatization catalysts are metal oxides, usually chromia, deposited on alumina and reduced metals of Group VIII of the Periodic Table supported on alumina, silica or activated carbon. Other catalysts have been suggested in the art. Zeolitic aromatization catalysts loaded with a Group VIII metal are mentioned in US-A-4,104,320; US-A-4,448,891 and US-A-4,822,762. DK-A-89/6666 discloses a metal sulphide modified zeolite of ZSM-5 type useful as catalyst in the conversion of aliphatic hydrocarbons to aromatic compounds. So far known, aromatization processes employing catalysts based on hydrotalcite-type support materials comprising a Group VIII metal for use in the preparation of aromatic compounds, have not been recognized in the art. EP-A-0330224 discloses a process for the catalytic oxidation of carbon monoxide using a catalyst, said catalyst comprising hydrotalcite and at least one noble metal selected from Pt and Pd. The catalyst is prepared by (a) impregnating hydrotalcite with a solution comprising a dissolved compound of at least one noble metal selected from Pt and Pd, followed by (b) calcining. Optionally, the material obtained in step (b) is further treated in a reducing atmosphere. The object of the present invention is to provide a process for preparing aromatic compounds employing catalysts based on hydrotalcite-type support materials comprising a Group VIII metal. This object is solved by providing a process for preparing aromatic compounds, which comprises reacting a gaseous feed containing C₆ to C₂₀ hydrocarbons in the presence of a catalyst comprising a metal from Group VIII of the Periodic Table loaded on a hydrotalcite-type support material having in its uncalcined state the general formula Me(II) x Me(III) y (CO₃)(OH) 2x+3y-2 · aq with an X-ray diffraction (d003) greater than 0.74nm (7.4Å), and wherein Me(II) is at least one divalent metal selected from the group consisting of copper, magnesium, manganese, zinc and a metal from Group VIII or the Periodic Table; Me(III) is as least one trivalent metal selected from the group consisting of aluminium, chromium and iron; and x and y are positive numbers satisfying the following relationship x/y ≧ 0.5. Hydrotalcite-type materials belong to the Group of anionic clay minerals having the general formula as briefly stated herein before. The structure of these minerals is composed of infinite layers with positively charged metal oxide-hydroxide layers with alternating interlayers of water and carbonate ions. In the metal oxide-hydroxide layers a part of the divalent metal ions is replaced by trivalent metal ions gaining positive charge, which is compensated for by the interstitially carbonate and hydroxide ions. The hydrotalcite-type materials used in this invention may be prepared by a coprecipitation procedure, in which an aqueous solution containing divalent and trivalent metals is precipitated with an aqueous solution of an alkali metal hydroxide and an alkali metal carbonate and/or alkali metal hydrogen carbonate at pH 7.0 to 10.0 and at a temperature from 20°C to 80°C. Salts of the divalent metal Me(II) including magnesium, copper, maganese, zinc and Group VIII metal salts and salts of the trivalent metal Me(III), including aluminum, chromium and iron salts are combined in an aqueous solution, either alone or in combinations thereof and coprecipitated as described above. The molar ratio of Me(II)/Me(III) is, thereby, ≧ 0.5, preferably between 0.5 and 20. Preferred salts are the nitrates of the above metals. The resulting precipitated material is recovered by filtration after precipitation when using an aqueous solution of an alkali metal hydroxide and an alkali metal carbonate. When using precipitation only with an alkali metal hydroxide solution, the precipitated material is further dispersed in a stirred aqueous alkali metal carbonate solution, and/or alkali metal hydrogen carbonate solution for 10-70 h before filtration. The amount and concentration of the alkali metal carbonate solution should at least contain an amount of carbonate ion, which meets the stoichiometry of the structure of the desired hydrotalcite-type material. Following the precipitation, the obtained product is washed with water to remove excess of ions derived from the starting materials. The X-ray diagrams of the dried and uncalcined hydrotalcite-type products, in which the products have by way of example the composition Zn₃CuAl₂(OH)₁₂CO₃ · aq; and Mg₁₀Al₂(OH)₂₄CO₃ · aq; are summarized in Table 1 below and indicate a layered structure similar to that of hydrotalcite clay Zn₃CuAl₂(OH)₁₂CO₃·aq Mg₁₀Al₂(OH)₂₄CO₃·aq Mg₆Al₂(OH)₁₆CO₃·4H₂O d/Å I/Io d/Å I/Io d/Å I/I 7.54 100 7.66 100 7.84 100 3.77 54 3.83 67 3.90 60 2.59 53 2.58 73 2.60 40 2.29 34 2.31 27 2.33 25 1.94 24 1.95 15 1.99 30 1.54 11 1.52 49 1.54 35 1.50 14 1.49 38 1.50 25 1.42 5 1.42 6 1.42 8 Even though there are some variations in the X-ray powder diffraction patterns of the hydrocalcite-type materials, certain lines in the diffraction patterns are characteristic for these materials. The characteristic lines are shown in Table 2: d/Å I/Io >7.4 VS >3.7 S 2.59± 0.1 S 2.30± 0.05 M 1.96± 0.05 mW Calcination of the obtained hydrotalcite-type materials leads to substantially homogeneous metal oxide-hydroxide mixtures with a higher surface area than the uncalcined hydrotalcite-type materials. During the calcination step the temperature has to be chosen carefully. High temperatures leading to separate phases of metal oxides and spinels have to be avoided. The X-ray diagrams of the materials calcined at the appropriate temperature do not contain any lines for formed spinels. The Group VIII metal is loaded on the calcined material by preferably aqueous impregnation with a soluble Group VIII metal salt, including salts of platinum and palladium. Suitable salts of Group VIII metals are those, which upon heating to about 400°C give the oxides of the metals, such as chlorides, nitrates and other simple salts. Preferred salts of platinum and palladium, are the coordinated salts, such as the aminoacetates, tetrammine chlorides or tetrammine nitrates. The Group VIII metal is loaded on the support material in any catalytically active amount. Convenient amounts of the Group VIII metal in the catalyst will range between 0.01 and 10 per cent by weight (wt%) of the weight of the material, preferably between 0.1 and 5 wt%, and most preferred between 0.1 and 2 wt%. When used as catalyst in the inventive process the above obtained materials are activated in a hydrogen containing atmosphere at a temperature between 100°C and 450°C. The process of the present invention is accomplished by contacting a hydrocarbon feedstream, comprising C₆-C₂₀ paraffinic hydrocarbons, with the catalyst as defined above. The catalyst is, thereby, arranged in a reaction zone, such as a fixed bed reactor or a fluidized bed reactor. The process may be carried out at a temperature between 100 and 600°C, preferably between 350 and 500°C. The reaction can take place at a pressure of 0-100 bar, preferably, 0-10 bar and a weight space velocity (WSHV) of 0.01 to 200, preferably, 0.01 to 10 depending on the amount and shape of the catalyst. The catalyst may, thereby, be composed with a matrix binder, such as clays, alumina, silica, titania, magnesia or compositions thereof and can be employed in any shape, such as particles, pellets or pressed tablets. In large reactor units, it might be preferred to use the catalyst loaded on monolithic structures, known in the art. In the reaction zone the feedstream is converted to aromatic compounds at a conversion level of 10 to about 100% per pass depending on the weight space velocity of the feedstream. Produced aromatic compounds are recovered from the effluent of the reaction zone and unconverted hydrocarbon feed together with paraffinic, olefinic and napthenic hydrocarbons (PON) by-products are recycled back to the reaction zone. The above objects and features of the present invention are further illustrated by the following Examples. In Examples 1-22 are prepared platinum and palladium loaded hydrotalcite-type aromatization catalysts and in Examples 23a and 23b comparison catalysts having platinum loaded on a metal oxide - metal spinel support. The catalysts are characterized by their chemical composition and by their X-ray powder diffraction in their uncalcined and calcined state. The X-ray powder diffraction pattern was determined by standard techniques using the radiation of the K-alpha doublet of copper. Examples 24-36 are carried out by a process for the preparation of aromatic compounds according to an embodiment of the invention employing the catalysts prepared in Examples 1-23b. In the Process Examples feed gas consisting of n-hexane and hydrogen in a molar ratio H₂/C₆ of 6, n-heptane and hydrogen in a molar ratio H₂/C₇ of 3, or pure n-heptane, is passed through a reaction zone containing 1.0 g samples of the above catalysts crushed to particles of 0.15-0.71 mm diameter (Mesh 25-100) and loaded in a quartz tube reactor with an inner diameter of 6 mm. Aromatic compounds together with non-aromatizable C₁-C₅ hydrocarbons are recovered from the reactor effluent. Unconverted feed and converted hydrocarbons comprising paraffins, olefins and napthenes (PON), are recycled to the reactor inlet. The product selectivity for aromatic compounds was calculated on the amount of hydrocarbons in the not recycled reactor effluent, by dividing the fractional conversion of the feed to aromatics with the total amount of not recycled hydrocarbons in the effluent. Example 1 Preparation of Mg₄Al₂(OH)₁₂CO₃ · aq hydrocalcite-type material. A solution of 200 g KOH in 600 ml water was added at ambient temperature to a stirred solution of 256.4 g Mg(NO₃)₂ · 6H₂O and 187.5 g Al(NO₃)₃ · 9H₂O in 500 ml water. The resulting slurry was kept at 40°C for 1 h with stirring. 75 g KHCO₃ in 500 ml water were then added to the slurry, which was heated to 80°C with stirring, giving a final pH of 8.0. After about 3 h the slurry was filtered and the precipitate added to 2000 ml water at 80°C. After about 18 hours, a solid crystalline product, having an X-ray powder diffraction pattern as shown hereinbefore in Table 2 and chemical analysis values as summerized below, was separated by filtration, washed with water and dried at 100°C for 24 h. Chemical analysis: 19.0 wt% Mg, 10.5 wt% Al and 1.88 wt% K, giving the above composition formula. Examples 2-3 Preparation of Mg₁₀Al₂(OH)₂₄CO₃ · aq hydrocalcite-type material. A solution of 112 g KOH and 10.35 g K₂CO₃ in 1000 ml water was added at ambient temperature to a stirred solution of 217.6 g Mg(NO₃)₂ · 6H₂O and 56.25 g Al(NO₃)₃ · 9H₂O in 1000 ml water. A part of the resulting slurry was kept at ambient temperature for 18 h giving a final pH of 8.8 (Example 2) or the residue was heated to 65°C under stirring for 18 h giving a final pH of 9.3 (Example 3). Thereafter, each of the slurries was filtered, washed with water and dried at 120°C for 18 h. X-ray of the obtained crystalline products show the lines of Table 2. Chemical analysis of the product showed the following results: 28.9 wt% Mg, 6.5 wt% Al and 0.81 wt% K, giving the above composition formula. Example 4 Preparation of Mg₁₀Al₂(OH)₂₄CO₃ · aq hydrocalcite-type material. A reaction mixture was prepared by adding simultaneously a solution prepared by dissolving 217.6 g Mg(NO₃)₂ · 6H₂O and 56.25 g Al(NO₃)₃ · 9H₂O in 1000 ml water, and a solution prepared by dissolving 112 g KOH and 10.35 g K₂CO₃ in 1000 ml water to a stirred beaker, kept at 65°C for 15 min. The resulting crystalline precipitate, having the X-ray powder diffraction pattern as shown in Table 2, was separated by filtration, washed with water and dried at 80°C for 4 h. Chemical analysis of the product showed the following results: 18.6 wt% Mg, 3.65 wt% Al and 1.2 wt% K giving the above composition formula. Example 5 Preparation of Mg₆Fe₂(OH)₁₆CO₃ · aq hydrocalcite-type material. A solution of 180 g KOH in 1000 ml water was added at ambient temperature to a stirred solution of 308 g Mg(NO₃)₂ · 6H₂O and 162 g Fe(NO₃)₃ · 9H₂O in 1000 ml water. 5 min. with stirring. 40 g KHCO₃ in 300 ml water were then added to the slurry, which thereafter was heated to 55°C under stirring, giving a final pH of 8.29. After about 2 h the slurry was filtered and the precipitate added to a solution of 20 g KHCO₃ in 2000 ml water and the mixture heated for 24 h at 55°C. A solid crystalline product having an X-ray powder diffraction pattern as summerized in Table 2, was separated by filtration, washed with water and dried at 80°C for 16 h. Example 6 Preparation of Zn₂Al₃(OH)₁₂CO₃ · aq hydrocalcite-type material. A solution of 5.9 kg KOH in 3.6 l water was added within 2-5 min. at ambient temperature to a stirred solution containing 1.3 kg ZnO, 3.4 kg HNO₃ (62%) and 9.0 kg Al(NO₃) · 9H₂O in 36 l water. The pH value of the resulting slurry was adjusted to 7.0 by addition of KOH/HNO₃. To the slurry was added a solution of 1.6 kg KHCO₃ in 12 l water, and the mixture heated at 55°C. After about 2 h the mixture was filtered and the resulting precipitate added to a solution 0.8 kg KOH in 10 l water. This mixture was then heated to 55°C for 66 h with stirring. A solid crystalline product having an X-ray powder diffraction pattern shown in Table 2 and chemical analysis values as summarized below, was separated by filtration, washed with water and dried at 80°C for 16 h. Chemical analysis: 29.6 wt% Zn, 18.6 wt% Al, 6.7 wt% CO₃ and 85 ppm K. Example 7 Preparation of Zn₆Al₂(OH)₁₆CO₃ · aq hydrocalcite-type material. A solution of 41.5 g KOH in 500 ml water was added at ambient temperature to a stirred solution of 70 g Zn(NO₃)₂ · 6H₂O and 30 g Al(NO₃)₃ · 9H₂O in 500 ml water. The resulting slurry was kept at ambient temperature with stirring. After about 10 min. the slurry was filtered. The resulting precipitate was added to a solution of 10 g KHCO₃ in 1000 ml water at 65°C, giving a final pH of 9.0. After about 16 h a solid crystalline product having an X-ray powder diffraction pattern as shown in Table 2 and chemical analysis values as summerized below, was separated by filtration, washed with water and dried at 80°C for 24 h. Chemical analysis: 45.6 wt% Zn, 6.4 wt% Al and 9.7 wt% CO₃, giving the above composition formula. Example 8 Preparation of CuZn₃Al₂(OH)₁₂CO₃ · aq hydrotalcite-type material. A solution of 395 g KOH in 3000 ml water was added at ambient temperature to a stirred solution of 120.5 g Cu(NO₃)₂ · 3H₂O, 446.2 g Zn(NO₃)₂ · 6H₂O and 375 g Al(NO₃)₃ · 9H₂O in 3000 ml water. The resulting slurry was kept at ambient temperature for 5 min. with stirring. 100 g KHCO₃ in 1000 ml water were then added to the slurry, and the mixture then heated to 55°C with stirring, giving a final pH of 7.47. After about 2 h the mixture was filtered and the precipitate added to a solution of 50 g KHCO₃ in 6000 ml water. This mixture was heated for 72 h at 55°C. A solid crystalline product having an X-ray powder diffraction pattern as shown in Table 2 and chemical analysis values as summerized below, was separated by filtration, washed with water and dried at 120°C for 18 h. Chemical analysis: 10.0 wt% Cu, 29.4 wt% Zn, 9.0 wt% Al and 9.3 wt% CO₃, giving the above composition formula. Example 9 Preparation of Zn₄Cr₂(OH)₁₂(CO₃) · aq hydrocalcite-type material. A solution of 395 g KOH in 2500 ml water was added at ambient temperature to a stirred solution of 595 g Zn(NO₃)₂ · 6H₂O and 400 g Cr(NO₃)₃ · 9H₂O in 2500 ml water. The resulting slurry was kept at ambient temperature for 15 min. with stirring. 100 g KHCO₃ in 1000 ml distilled water were then added to the slurry. The mixture was then heated to 55°C under stirring, giving a final pH of 7.34. After about 2 h the mixture was filtered and the precipitate added to a solution of 50 g KHCO₃ in 5000 ml water. This mixture was then heated at 55°C for 24 h. A solid crystalline product having an X-ray powder diffraction pattern as shown in Table 2 and chemical analysis values as summerized below, was separated by filtration, washed with water and dried at 120°C for 18 h. Chemical analysis: 37.1 wt% Zn, 15.2 wt% Cr and 8.3 wt% CO₃ 75 ppm K; giving the above composition formula. Example 10 Preparation of Mg₂₀Al₂(OH)₄₄CO₃ · aq hydrocalcite-type material. A reaction mixture was prepared by adding simultaneously a solution prepared by dissolving 217.6 g Mg(NO₃)₂ · 6H₂O and 3.19 g Al(NO₃)₃ · 9H₂O in 1000 ml water, and a solution prepared by dissolving 112 g KOH and 10.4 g K₂CO₃ in 1000 ml water to a stirred beaker, and kept at 65°C for 15 min. The resulting precipitate was seperated by filtration, washed with water and dried at 120°C for 18 h, leaving the above crystalline product with an X-ray powder diffraction pattern as shown in Table 2. Chemical analysis of the product showed the following results: 34.3 wt% Mg, 3.8 wt% Al and 1.2 wt% K, giving the above composition formula. Examples 11-22 Preparation of the Group VIII aromatization catalysts loaded on hydrotalcite-type support material used in the invention. The catalysts of these Examples were prepared by calcination of the hydratalcite-type materials obtained in Examples 1-10 and impregnation with a Group VIII metal solution. The materials were calcined in air at 450-600°C for 4-12 h, as further specified in Table 3, which follows. In the X-ray powder diffraction patterns of the calcined materials, no lines for formed spinels were found. The calcined products were crushed to particles with a particle size of 0.15-0.71 mm (25-100 Mesh), and impregnated with a platinum (Examples 11-19 and 22), or a palladium (Examples 20-21) solution. The platinum solution and palladium solution for impregnating the particulate materials were prepared by dissolving 2 g Pt (NH₃)₄(NO₃)₂ and 32 g Pd (NH₃)₄(NO₃)₂, respectively, in 500 ml water. 2 g samples of the calcined particulate material were immersed in the above solutions for about 18 h, then filtered, dried and calcined at 450°C for 4 h in air. The amounts of Pt or Pd impregnated on the materials are further specified in Table 3. The Pt and Pd-aromatization catalysts, thus obtained, were activated in a hydrogen atmosphere at 120°C for about 30 min., followed by calcination in a hydrogen atmosphere at 425°C for about 2 h. Catalyst Example No. Hydrotalcite-type material Example No. Temp/°C Calcination Time/h wt% of %Pt or Pd in catalyst 11 1 600 12 0,75(Pt) 12 2 600 12 0,69(Pt) 13 3 600 12 0,82(Pt) 14 4 600 12 0,74(Pt) 15 5 450 6 0,92(Pt) 16 6 - - 0,41(Pt) 17 7 450 4 0,62(Pt) 18 8 450 4 0,75(Pt) 19 9 500 6 0,81(Pt) 20 10 500 8 0,79(Pd) 21 10 500 4 0,81(Pd) 22 1 450 6 0,67(Pt) Example 23a Preparation of a comparison magnesium oxide-magnesium aluminum-spinel catalyst. The hydrotalcite-type material obtained in Example 1 was calcined at 900°C for 6 h in air. X-ray powder diffraction pattern (Table 4) of the calcined material shows distinctive lines of magnesium aluminum-spinel and magnesium oxide(*). d/Å I/Io 4.69 15 2.85 22 2.44 66 2.11* 100 2.03 47 1.64 4 1.56 22 1.49* 45 1.43 37 The magnesium oxide-magnesium aluminum-spinel support material, thus obtained, was loaded with platinum by a procedure similar to that of Example 11. The final platinum loaded magnesium aluminum-spinel comparison catalyst containing 0.76 wt% Pt was activated as described above under Examples 11-22. Example 23b Preparation of a comparison ZnAl-spinel catalyst. The hydrotalcite-type material obtained in Example 6 was calcined at 900°C for 6 h in air. X-ray powder diffraction pattern (Table 5) of the calcined material shows distinctive lines of zinc aluminum-spinel and zinc oxide(*). d/Å I/Io 4.67 2 2.85 66 2.81(*) 17 2.47(*) 24 2.44 100 1.63 8 1.56 33 1.48* 5 1.43 34 The zinc oxide zinc aluminum-spinel support material was loaded with platinum (0.65 wt%), as described hereinbefore (Example 11) and activated as under Examples 11-22. Examples 24-36 The performance of the catalysts prepared in Examples 11-22 and the comparison catalysts of Examples 23a and 23b were tested in the conversion of n-hexane or n-heptane to aromatic compounds. The aromatization process was carried out as described hereinbefore. Further process conditions and the results of the reactions are shown in Table 6 below, where "aromatics" includes benzene, toluene and xylenes. The above data show that higher conversion rates and an improved selectivity for the formation of aromatic compounds are obtained by use of MgAl hydrotalcite (Examples 24, 25, 33) and ZnAl hydrotalcite (Example 30) supported catalysts, when compared with the conversion rates and selectivity obtained by use of the respective magnesium oxide - magnesium aluminum spinel and zinc oxide - zinc aluminum spinel comparison catalysts of Examples 23a, 23b.

Claims: A process for preparing aromatic compounds, which comprises reacting a gaseous feed containing C₆ to C₂₀ hydrocarbons in the presence of a catalyst comprising a metal from Group VIII of the Periodic Table loaded on a hydrotalcite-type support material having in its uncalcined state the general formula Me(II) x Me(III) y (CO₃)(OH) 2x+3y-2 · aq with an X-ray diffraction (d003) greater than 0.74nm (7.4Å), and wherein Me(II) is at Least one divalent metal selected from the group consisting of copper, magnesium, manganese, zinc and a metal from Group VIII of the Periodic Table; Me(III) is as least one trivalent metal selected from the group ccnsisting of aluminium, chromium and iron; and x and y are positive numbers satisfying the following relationship x/y ≧ 0.5. The process of claim 1, wherein x/y is from 0.5 to 20. The process of claim 1, wherein the divalent metal Me(II) is magnesium or a combination or magnesium with at least one divalent metal selected from the group consisting of copper, manganese and zinc. The process of claim 1, wherein the divalent metal Me(II) is zinc or a combination of zinc with divalent copper. The process of claim 1, wherein the trivalent metal Me(III) is iron or chromium. The process of claim 1, wherein the divalent metal Me(II) is magnesium and the trivalent metal Me(III) is aluminium. The process of claim 1, wherein the Group VIII metal is selected from the group consisting of platinum, palladium and combinations thereof. The process of claim 1, wherein said catalyst is prepared by precipitating at pH 7.0 to 10.0 and at a temperature from 20°C to 80°C, an aqueous solution of at least one divalent metal salt and at least one trivalent metal salt in an atomic ratio of ≧0.5, with an alkaline solution comprising an alkali metal hydroxide and carbonate and/or hydrogen carbonate, thereby obtaining a hydrotalcite-type material with the general formula Me(II) x Me(III) y (CO₃)(OH) 2x+3y-2 · aq wherein x, y, Me(II) and Me (III) are as defined in claim 1; drying and calcining the material at a temperature, where a hydrotalcite-type derived support material is obtained, said support material having an X-ray powder diffraction pattern with no lines of a spinel formed by the above metals; treating the calcined material with an aqueous solution of a soluble salt of at least one metal from Group VIII of the Periodic Table; and finally drying the treated material. The process of claim 8, wherein the hydrocalcite-type material is treated with the aqueous solution of a soluble salt of at least one metal from Group VIII of the Periodic Table before calcining the material. The process of claim 8, wherein the Group VIII metal salt comprises platinum, palladium or combinations thereof.

Inventors: BLOM NIELS JORGEN, DAVIS ROBERT J, DEROUANE ERIC G, BLOM, NIELS JORGEN, DAVIS, ROBERT J., DEROUANE, ERIC G.
Applicants: TOPSOE HALDOR AS, HALDOR TOPSOE A/S
Application year: 1991
Main classification: C07C5
IPC codes: B01J23, C07C5, B01J27, B01J21, C10G35