IMPROVEMENTS IN OR RELATING TO DENTAL FLOSS OR TAPE

Abstract: A dental floss or tape has a multifilament polyamide core (10) and a continuous PTFE coating (12) applied by passing the core through an aqueous PTFE dispersion and heating the deposited particles such that they coalesce into a layer without substantially effecting the structure of the core.

Description: Improvements in or Relating to Dental Floss or Tape The present invention relates to dental floss or tape Dental floss or tape is usually a multi-filament , possibly continuous strand, material such as polyamide or polyester. Its elements are drawn and twisted to improve strength and resilience. It is already known that dental floss or tape be coated with a wax based coating using polyethylglycol (PEG) or hot wax. Furthermore it is not unusual to add flavouring flouride and/or abrasive to the floss or tape. Such flosses are disclosed, for example, in U.S. Patents 3838702, 3943949 and 4029113. Un-waxed dental floss or tape is also available using an acrylic emulsion coating to seal and/or bind the floss or tape. Prior flosses have not been found to be completely satisfactory by the user as the wax coating is usually scraped off when the floss is being used to clean inter-dental spaces depositing the wax on the teeth which thereafter feel sticky. Additionally the removal of the wax leads to an increased co-efficient of friction between the floss and teeth and gums and this, coupled to the deterioration of the floss when its wax binding coat is removed, means that the floss rapidly disintegrates and often breaks, rendering it useless, troublesome and annoying. It has been proposed in the past to decrease the co-efficient of friction by incorporating powdered polytetrafluoroethylene (PTFE) in the wax binder, such a solution having been proposed in European Patent Application No. 0358363A but this proposal still suffers from the disadvantage of removal of the coating during use and the subsequent possible disintegration and destruction of the floss. Prior patents, for example, European Patent Application 0335466A and U.S. Patent 477635A have recognized that PTFE has a relatively high tensile strength and will give the feature of reduced co-efficient of friction without the disadvantage of subsequent possible destruction if it is used in place of the polyamide or polyester formerly employed as the core of the floss or tape. Unfortunately, PTFE is a relatively expensive material, for example, it is six times more expensive than polyamide and consequently the considerable disadvantage of this proposal, bearing in mind that the product is a "throw away" product, is the high cost. A similar disadvantage is displayed in U.S. Patent 4836226 which discloses the use of a PTFE coating on an elastic material which is used while in a stretched condition. In this proposal the elastic material and PTFE have widely differing moduli of elasticity so that stretching the core will disrupt the PTFE coating. It is an object of the present invention to obviate or mitigate these and other disadvantages. According to the present invention there is provided a method of producing a fluorocarbon coated dental floss or tape comprising passing spun filamentary elements forming a multi-filament core through a dispersion including fluorocarbon particulate material such that fluorocarbon particles are deposited upon the multi-filament core and heating the deposited fluorocarbon particles such that they coalesce into a fluorocarbon coating on the core. Preferably prior to passing the core through the dispersion its filaments are twisted. Preferably the core is heated to evaporate the liquid component of the fluorocarbon dispersion and further heated to coalesce the fluorocarbon upon the core, preferably into a continuous layer. Preferably a wax layer including any one or more of the group comprising flavouring fluoride, and abrasive is added to the core after the fluorocarbon coating is applied. Preferably prior to passing the core through the fluorocarbon dispersion the core is dyed. Preferably the fluorocarbon particles deposited on the core are subjected to a temperature within the range 355°F to 400°C, for a short period to ensure the core does not melt appreciably as the particles coalesce into a continuous coating on the core. Desirably the fluorocarbon particles deposited on the core are subjected to an upper temperature of 360°C as the core passes the heating means at a speed of m/min. Further according to the present invention there is provided a dental floss or tape comprising a core of filamentary material and a fluorocarbon coating formed from coalesced fluorocarbon particles. Preferably the fluorocarbon is polytetrafluoroethylene (PTFE). Preferably, the coating is arranged to ingress within the core and is formed by polytetrafluoroethylene particles coalesced into a continuous layer. Preferably, a wax layer is added to the fluorocarbon coating. Preferably, the filaments are twisted prior to application of the fluorocarbon coating. Preferably the filaments are polyamide or polyester. An embodiment of the present invention will now be described by way of example only with reference to the accompanying drawings in which:- Fig. 1 illustrates a length of coated floss, and Fig. 2 shows diagrammatically apparatus for coating floss. It is usual to take thirty two filaments of extruded and stranded material to form a dental floss core 10. These filaments are formed of polyamide or polyester material and are usually continuous extruded strands. It will be appreciated that the type of filament and its dimensions will be chosen in accordance with requirements, however, it is not unusual to use 940 denier materials with thirty-two filaments in a core 10 or, as an alternative, thirty two minicores each comprising eight filaments of 100 denier. The floss core 10 is twisted and if it is necessary to dye the floss or tape it is at this stage that dying takes place. Once twisted the core is normally stored on creels until required for further processing. During further processing the floss 10, after passing through pre-tensioning bars 20 is drawn through a tank 22 containing a dispersion of PTFE in water and a non-ionic wetting agent as stabiliser. This dispertion adheres itself to the core 10 and ingresion of dispersion into the filaments of the core can be facilitated through agitation and other means (not shown). Once the core 10 has been drawn through the tank 22 of PTFE dispersion it passes over tension rollers 24 which futher ensure that PTFE particles and their carrier are impregnated into the core. The core and its coating 12 of PTFE particles from the dispersion is then passed through an oven assembly 26 which is some 10m in length. On passage through the tension rollers 24 excess dispersion is squeezed from the core and, as mentioned above pressed into the interstices between the filaments of the core. In the first section of the oven, which is of approximately 2m length the water carrier is evaporated off leaving behind the PTFE particles which, at this stage, are only mechanically adhered to the core 10. During subsequent passage through the oven, that is the approximate remaining 8m, heat applied by the infra-red heaters within the oven will cause the PTFE particles to coalesce into what is desireably a continuous unbroken coating but may be a coating of co-alesced particles which, if not completely continuous longitudinally and circumferentially, has continuity by way of unbroken areas of coalesced particles of practical length. By a balance of the speed of the core through the oven and the temperature therein it is possible to coalesce or sinter the particles onto the polyamide core without causing permanent unacceptable damage to the core, which has a melting point lower than the coalescing or sintering temperature of the particles. In the example illustrated in the drawing, up to a hundred cores are treated simultaneously and they are caused to pass through the ovens at a speed of between 30 and 60 m/min, preferably 40 m/min. At this speed the temperatures in the oven, which is arranged in four parts are:- part 1 355°C, part 2 375°C, part 3 90°C, and part 4 400°C. Part 1 forms the first section referred to above and parts 3, 4; which total some 8 mm length from the second oven section. A typical PTFE dispersion has the following specification: Composition: PTFE particles, water, non-ionic wetting agent. solids content (58 PTFE by weight) 58.555 particle size, average diameter 0.23 Urn resin dry weight (58.5?ό solids) 870 g/1 specific gravity of dispersion (58?ό PTFE) 1.49 specific gravity of sintered resin 2.23 The dispersion can be diluted from the values set out in the table above by adding water up to the ratio of 1:1. After passing through the oven 26 the PTFE coated core passes around a pair of tension rollers 30 by way of a drop wire device 28 and may be stored on creels (not shown) or passed through a further coating stage. Various coatings such as wax or an acrylic emulsion can be applied on top of the fluorocarbon coating. Furthermore it is conventional with dental floss or tape to apply fluoride, flavourings and abrasive to assist its function and acceptability. Various modifications can be made without departing from the scope of the invention. The coating need not be PTFE but could be any other suitable fluorocarbon lubricant applicable in powder form in a dispersion and coalescible to give a continuous coating on the floss core.

Claims: Claims 1. A method of producing a fluorocarbon coated dental floss or tape comprising passing spun filamentary elements forming a multi-filament core through a dispersion including fluorocarbon particulate material such that fluorocarbon particles are deposited upon the multi-filament core and heating the deposited fluorocarbon particles such that they coalesce into a fluorocarbon coating on the core. 2. A method as claimed in claim 1, in which prior to passing the core through the dispersion its filaments are twisted. 3. A method as claimed in claim 1 or claim 2, in which the core is heated to evaporate the liquid component of the fluorocarbon dispersion and further heated to coalesce the fluorocarbon upon the core into a continuous layer. 4. A method as claimed in any one of claims 1 to 3, in which a wax layer including any one or more of the group comprising flavouring fluoride, and abrasive is added to the core after the fluorocarbon coating is applied. 5. A method as claimed in any one of claims 1 to 4, in which prior to passing the core through the fluorocarbon dispersion the core is dyed. 6. A method as claimed in any one of claims 1 to 5, in which the fluorocarbon particles deposited on the core are subjected to a temperature within the range 355°F to 400°C for a short period to ensure the core does not melt appreciably as the particles coalesce into a continuous coating on the core. 7. A method as claimed in any one of claims 1 to 5, in which the fluorocarbon particles deposited on the core are subjected to an upper temperature of 360°C as the core passes the heating means at a speed of m/min. 8. A dental floss or tape comprising a core 10 of filamentary material and a fluorocarbon coating (12) formed from co-alesced fluorocarbon particles. 9. A floss as claimed in claim 8, in which the coating (12) ingresses within the core (10) and is formed by polytetrafluoroethylene particles coalesced into a continuous layer.

Inventors: HILL DAVID MACKENZIE, HILL, DAVID, MACKENZIE
Applicants: PERI LUSTA LTD, PERI-LUSTA LIMITED
Application year: 1991
Main classification: A61C15
IPC codes: A61C15, D06M15