Solid image pickup device having microlenses

Abstract: In a solid image pickup device wherein a plurality of microlenses (28) are provided on a substrate (12) having light receiving portions (16), in opposition to the light receiving portions (16) so that incident light can converge onto the light receiving portions (16), the microlenses (28) are covered with a transparent resin layer (44) having a refractive index smaller than that of the microlenses (28). Therefore, the solid image pickup device (60), even when packaged in a molded body (72) made of a resin having a refractive index similar to that of the microlenses, can offer a good sensitivity because the microlenses (28) can effectively operate as condenser lenses due to the resin layer (44) between the molded body (72) and the microlenses (28).

Description: BACKGROUND OF THE INVENTION The present invention relates to a solid image pickup device such as a CCD (charge-coupled device) camera, for example, wherein microlenses are formed as condenser lenses on the upper surface of light receiving portions of the substrate. As the chip size of solid image pickup devices decreases and the number of pixels per device increases, the area of each light receiving portion on the substrate has been reduced. As a result, an amount of light received by each light receiving portion decreases and therefore sensitivity (output/(amount of incident light)) of the device lowers. In order to solve the above problem, a solid image pickup device has been proposed, which is shown in Fig. 1 and is generally indicated by a reference numeral 60. As shown in Fig. 1, microlenses 28 made of a transparent polymeric resin are formed on the upper surface of each of light receiving portions (not shown) which are pixels. The microlenses 28 serve as condenser lenses for incident light, that is, incident light is converged to the light receiving portions by the microlenses 28. Therefore, effective light received by each light receiving portion increases and the sensitivity deterioration is prevented. Generally, the solid image pickup device 60 has been contained in a ceramic package 76 as shown in Fig. 2. In Fig. 2, a reference numeral 70 indicates a ceramic substrate mounting the solid image pickup device 60, a reference numeral 74 indicates a lead pin and a reference numeral 78 indicates a glass lid for the ceramic package 76. Recently, a molded package 72 using a transparent resin, as shown in Fig. 3, is replacing the ceramic package 76 for the reason that the production cost can be lower. In this case, the following problem occurs. The microlenses 28 are formed of polystyrene, acrylic resin, novolak resin or other transparent resins. On the other hand, epoxy resin is used as a molding resin. The above transparent resins of the microlenses 28 have a refractive index of 1.5-1.6 and the molding epoxy resin also has a refractive index of 1.5-1.6. Therefore, when the solid image pickup device 60 is packaged by the molding resin, the condenser effect or light converging effect of the microlenses 28 is largely reduced or canceled by the molding resin. The document JP-A-59-90466 discloses a solid-state image pickup device having two superimposed lens layers, each of which is arranged in a checkerboard pattern to converge light on one half of a picture element array. According to the present invention, there is provided: a solid image pickup device, comprising: a substrate having a plurality of light receiving portions, a plurality of microlenses provided on said substrate and arranged to converge incident light onto the light receiving portions, and a transparent resin layer provided directly on the microlenses, having a substantially flat upper surface and having a refractive index less than that of the microlenses such that incident light is converged by said microlenses onto the light receiving portions; characterized in that said plurality of microlenses are arranged in a single layer such that each of said light receiving portions on said substrate is positioned to receive light converged by a corresponding one of said plurality of microlenses and further characterised by a plurality of further microlenses formed in a further layer on said transparent resin layer and being larger in size than said first-mentioned microlenses; and a further transparent resin layer formed on said further layer of further microlenses. Transparent polymeric resins having different refractive indices from each other may be -used as materials of the microlenses and the layer covering the microlenses, respectively. More specifically, the transparent polymeric resin for the microlenses may be a polyimide resin, polyether amide resin, polystyrene resin or other resins which have a refractive index of 1.6-1.8. The transparent polymeric resin for the resin layer covering the microlenses may be an epoxy resin, acrylic resin or other resins which have a refractive index of 1.3-1.5. When the solid image pickup device is packaged in a molded body made of a transparent molding resin having a refractive index similar to that of the microlenses, because the resin layer having a refractive index smaller than that of the microlenses covers the microlenses, reduction or cancellation of the light converging effect of the microlenses by the molding resin is avoided. In addition, because the solid image pickup device of the present invention is not subjected to cancellation of the light converging effect of the microlenses by the molding resin and therefore can use a molded package, the production cost can be lowered. BRIEF DESCRIPTION OF THE DRAWINGS The present invention will become more fully understood from the detailed description given hereinbelow and the accompanying drawings which are given by way of illustration only, and thus are not limitative of the present invention, and wherein: Fig. 1 shows a sectional view of a conventional solid image pickup device; Fig. 2 shows a sectional view of the conventional solid image pickup device in a state contained in a ceramic package; Fig. 3 shows a sectional view of the conventional solid image pickup device in a state packaged in a molding resin; Fig. 4 shows a sectional view of a solid image pickup device using a CCD in a first example which is not in accordance with the present invention; Fig. 5 shows a sectional view of the solid image pickup device in a state packaged in a molding resin; Figs. 6A-6E show a sectional view of a modification of the solid image pickup device of Fig. 4; Fig. 7 shows a sectional view of a modification of the solid image pickup device of Fig. 4 in an embodiment of the present invention; Fig. 8 shows a sectional view of a solid image pickup device provided with microlenses; and Figs. 9A-9C show steps for producing the solid image pickup device of Fig. 8. Before the description of embodiments of the present invention proceeds, it is to be noted that like parts are designated by like reference numerals throughout the accompanying drawings. Fig. 4 shows a solid image pickup device using a CCD as an example of a solid image pickup device. The present invention can be applied to a solid image pickup device of either a one-dimensional structure or a two-dimensional structure. The solid image pickup device is generally indicated by a reference numeral 60 in Fig. 5. A semiconductor substrate 10 is of a P type and light receiving portions 14 in the substrate 10 are of an N type. Double-layered transfer electrodes 18, 20 are provided on the semiconductor substrate 10 through an insulation layer 22 at charge transfer portions 16 which are sandwiched between the light receiving portions 14 and 14. A light screening metal 24 is provided over the double-layered transfer electrodes 18, 20 so that light does not enter the charge transfer portions 16. A flattening layer 26 made of an acrylic resin is provided over the light screening metals 24 and the light receiving portions 14 so that recesses formed between projections of the double-layered transfer electrodes 18, 20 are filled and that a flat surface is formed all over the semiconductor substrate 10. On the flattening layer 26 are provided red, green and blue color filters 40R, 40G, 40B (generally designated 40) in order to obtain a colored image. The color filters 40 are formed opposite the light receiving portions 14 so that only monochromatic light of red, green and blue comes to the respective light receiving portions 14. The color filters 40 may be formed by dyeing gelatin, casein or other materials. Furthermore, a protection layer 30 is provided on the color filters 40. The protection layer 30 not only protects the color filters 40 but also mounts microlenses 28 thereon. The microlenses 28 are formed in positions opposite to the light receiving portions 14. The protection layer 30 is treated to be hardened prior to the formation of the microlenses 28. More specifically, when the protection layer 30 is made of an ultraviolet-curing resist or a far-ultraviolet-curing resist, ultraviolet or far ultraviolet radiations are irradiated. On the other hand, when the protection layer 30 is made of a thermosetting resin, a heat treatment is applied to the protection layer 30. The above hardening treatment prevents the protection layer 30 from suffering from heat distortion even if heat is applied while the microlenses 28 are formed. Therefore, the microlenses are well formed in a good shape. The protection layer 30 works as a flattening layer as well. The microlenses 28 may be formed individually in positions corresponding to the respective light receiving portion 14. In addition, the microlenses 28 may be formed collectively in columns or rows in positions corresponding to each column or row of light receiving portions 14. The microlenses 28 are formed in a manner that peripheries 28a of the microlenses 28 are continuous to each other. By making the peripheries 28a of the microlenses 28 continuous to each other, incident light to the peripheries 28a can be lead to the light receiving portions 14. Therefore, almost all the light coming to the microlenses 28 reaches the light receiving portions 14. As a result, a total amount of incident light increases and the sensitivity increases correspondingly. Photosensitive resins, which are sensitive to ultraviolet or far ultraviolet radiations, or polymeric resins permeable to light are used as microlens materials. Of such resins, especially those that have a refractive index of 1.6-1.8 are used. Such a resin may be a polyimide resin, polyether amide resin, or polystyrene resin. If a photosensitive resin is used as microlens material, a resist layer (described later) will be used. If a photosensitive resin is not used, a pattern for microlenses is formed using a photo-etching and a dry-etching technique. Photosensitive resins are subjected to heat distortion during a heat treatment after the photosensitive resins are irradiated by ultraviolet rays or far ultraviolet rays. Therefore, an initial planar shape of a microlens resin layer on the protection layer 30 is changed to a semi-spherical shape or to a semi-cylindrical shape by the heat treatment. Before the shape is changed, the resin of the microlenses are treated with ultraviolet or far ultraviolet radiations, so that the resin is increased in permeability to light. A resin layer 44 of a given thickness is formed over the microlenses 28. This resin layer 44 is positioned between the microlenses 28 and a molding resin when the solid image pickup device is packaged in the molding resin, so that the resin layer 44 is referred to as an intermediate resin layer hereinbelow. A resin which has a refractive index of 1.3-1.5, such as, for example, an epoxy resin, acrylic resin or perfluoro resin, are used for the intermediate resin layer 44. The solid image pickup device 60 with the above structure, specifically with the intermediate resin layer 44 of a refractive index smaller than that of the microlenses 28 being formed on the microlenses 28, is molded with or packed in a molded body 72, as shown in Fig. 5. In Fig. 5, a reference numeral 70 indicates a resin substrate for mounting the color solid image pickup device 60. There are provided lead pins 74 at both ends of the resin substrate 70. A molded body 72 is formed of a transparent resin which covers not only the solid image pickup device 60 but also the upper surface of the resin substrate 70. Epoxy resin, for example, is used as a molding resin, as described above. The following describes a fabrication method of the microlenses 28 and a package method of the solid image pickup device using a resin molding technique, referring to Figs. 6A-6E. In the following description, it is assumed that the microlenses 28 are individually formed in the positions corresponding to the respective light receiving portion 14. First, as shown in Fig. 6A, doping of N-type impurities to the P-type semiconductor substrate 10 at given places is done to form the light receiving portions 14. After that, the double-layered transfer electrodes 18, 20, the light screening metal 24, the flattening layer 26 are sequentially formed on the semiconductor substrate 10 in a known manner, though they are not individually shown in Figs. 6A-6E. The flattening layer 26 may be formed of an acrylic resin, polyimide resin, isocyanate resin, or urethane resin, for example. In this embodiment, an acrylic resin named FVR-10 (Manufactured by Fuji Yakuhin Kabushiki Kaisha) is used. The flattening layer 26 is formed by spin-coating the acrylic resin in the thickness of 5.0 µm, for example. Then, the color filters 40R, 40G, 40B are formed on the flattening layer 26. Thereafter the color filters 40R, 40G, 40 B are coated with the protection layer 30. A hardening treatment is applied to the color filters 40 and the flattening layer 30. These layers provided between the semiconductor substrate 10 and the microlenses 28 are shown collectively as a fixed layer 50 in Fig. 6A. A resist layer 52 which is sensitive to ultraviolet or far ultraviolet rays is spin-coated in the thickness of, for example, 3.0 µm on the fixed layer 50. In the present example, a positive resist layer 52 is formed. For example, a novolak resin such as AZ, OFPR or Micro Posit (product names) can be used for the positive resist layer 52. If no positive resists are used, a pattern is formed by a photo-etching and a dry-etching. Because novolak resins can be minutely processed, the light receiving portions can be formed in a high density. After the positive resist layer 52 on the fixed layer 50 is dried, portions of the positive resist layer 52 other than portions corresponding to the light receiving portions 14 are exposed to ultraviolet rays and then developed to have a predetermined pattern. In this way the patterning is completed as shown in Fig. 6B. Next, the positive resist layer 52 in the predetermined pattern is treated with heat at a temperature below 160 °C, desirably at a temperature between 130-150 °C so that the positive resist layer 52 is semi-spherically deformed as shown in Fig. 6C. Finally, the microlenses 28 with their respective peripheries 28 connected to each other are obtained. The heating temperature is set below 160 °C in consideration of the heat resistance property of the color filters 40R, 40G, 40B which are part of the fixed layer 50, so that the color filters are not subjected to thermal change in properties. Before the completion of the microlenses 28 through the thermal deformation of the positive resist layer 52, ultraviolet rays of 350-450 nm are irradiated. The positive resist layer 52 which has been opaque till then becomes transparent through the exposure to the ultraviolet rays. In addition, the irradiation of ultraviolet or far ultraviolet rays after said completion of the microlenses 28 causes the microlenses 28 to be cured or hardened. The microlenses 28 are therefore thermally stable. The positive resist layer 52 is processed to be hardened after being thermally deformed, considering the two properties of the positive resist layer 52 that the positive resist layer 52 is made transparent by the exposure to ultraviolet or far ultraviolet rays and that once exposed to ultraviolet or far ultraviolet rays, the positive resist layer 52 becomes thermally very stable although the positive resist not treated with ultraviolet or far ultraviolet rays is easily softened with heat of 120-160°C. It is to be noted, however, that the heat treatment may be applied simultaneously with the irradiation of far ultraviolet or ultraviolet rays. Next, as shown in Fig. 6D, the microlenses 28 are coated with the intermediate resins layer 44 of a predetermined thickness. As described above, the intermediate resin layer 44 can be treated with heat after being coated on the microlenses 28. Next, the molded body 72, as shown in Fig. 5, for packaging the color image pickup device 60 is formed of a transparent resin layer 46, as shown in Fig. 6E. Fig. 7 shows a modification comprising an embodiment of the present invention wherein the microlenses 28 and intermediate resin layers 44 are provided in a double-layer structure on the solid image pickup device substrate 12 including the semiconductor substrate 10, the light receiving portions 14 and the fixed layer 50. It is to be noted that in this case the microlenses 28 of an upper layer are larger in size than the microlenses 28 of a lower layer. According to this structure, more light can be gathered. In the above embodiment, the present invention is applied to a color solid image pickup device using a CCD. However, the present invention is also applied to other types of solid image pickup devices for not only imaging color images but black and white images as well. Fig. 8 shows a cross sectional view of a solid image pickup device with microlenses formed by an alternative method. In Fig. 8, the same reference numerals as those of Fig. 4 indicate similar parts and therefore a description of those parts is omitted. A reference numeral 228 indicates a microlens formed by this method. The microlenses 228 are made in the following method. It is to be noted that in the following description, the parts individually designated 12, 14, 16, 18, 20, 22, 24, 26, 40 (40R, 40G, 40B), and 30 in Fig. 8 are collectively indicated by the reference numeral 12 as a solid image pickup device substrate. Figs. 9A-9B are illustrations showing steps of forming the microlenses 28. First, the solid image pickup device substrate 12 provided with the color filters made of gelatin or casein are prepared. The color filters 40 are provided in a manner covering the light receiving portions 14. Then, as shown in Fig. 9A, a photosensitive resin layer 27 is coated in the thickness of 2µm on the upper surface of the solid image pickup device substrate 12 or more specifically of the protection layer 30. Next, the photosensitive resin layer 27 is selectively etched in a square pattern or in stripes using a photo-etching method, so that the photosensitive resin layer 27 is left in a sectionally rectangular shape on the substrate 12, as shown in Fig. 9B. When the photosensitive resin layer 27 is etched in a square pattern, squares of the photosensitive resin layer 27 are formed for each light receiving portion 14. On the other hand, when a stripe pattern is used, stripes of the photosensitive resin layer 27 are formed for each row or column of light receiving portions 14. The photosensitive resin 27 is a polystyrene derivative such as a copolymerizate of poly-p-vinylphenol and poly-p-vinylchlorobenzene, for example, with naphtoquinonediazido-5-sulfonyl chloride as a sensitizing agent. The refractive index of the photosensitive resin 27 is in the order of 1.70. The transmittance of the photosensitive resin layer 27 after photo-etched is 45 % (reddish brown) under the measuring conditions of a wavelength 400 nm and a film thickness 2µm. This value is lower than that (about 80 %) of a novolak resin with naphtoquinone diazide. It is necessary to heat at a temperature above 180 °C to soften the photosensitive resin 27. Next, near ultraviolet light (350-450 nm ) including a light component of a wavelength 365 nm is irradiated from a high-pressure mercury vapor lamp onto the photosensitive resin layer 27. Under this condition, the substrate 12 with the photosensitive resin layer 27 is heated in an oven at a temperature of 150 °C for half an hour. The irradiation condition is 8 mW/cm 2 and 320 mJ/cm 2 for the wavelength of 365 nm. During this process. photodegradation or photo-depolymerization occurs to light active groups contained in the photosensitive resin 27 due to the near ultraviolet light and a polymer of the photosensitive resin 27 lowers in molecular weight so that the glass transition point lowers. Consequently, the polymer, which, if only simply heated without irradiation of the near ultraviolet light, will be fused at a temperature above 180 °C, are fused at a temperature as low as 150 °C. The photosensitive resin 27 is then semi-spherically or semi-cylindrically shaped, as shown in Fig. 9C, by means of its own surface tension. At this time, because the heating temperature is as low as 150 °C, properties of the color filters 40 are not changed. In this manner, microlenses 228 with an increased refractive index (1.65-1.70) are obtained without affecting properties of the microlenses 228. According to the above method, the irradiation of near ultraviolet light can decompose the light active group in naphtoquinone-diazido-5-sulfonyl chloride of the sensitizing agent, so that absorption of visible light can be reduced after the completion of the microlens production process. Actually, the transmittance could be increased to more than 92 %, and therefore, microlenses 228 having a better transparency or permeability to light than before were obtained. The photosensitive resin layer 27 may be also formed of polyimide (refractive index: 1.70) or polyethylene terephthalate (refractive index: 1.68), for example, instead of the aforementioned material. When these materials are used, the transmittance will be 80-90 %. It is to be noted that when polyethylene terephthalate is used, it is necessary to provide a photo resist before photo etching with an appropriate etchant because this material cannot be photo-etched directly. As described above, because a photosensitive resin which is a microlens material is exposed to ultraviolet light during the heat treatment, the heating temperature can be below 160 °C. Therefore, on-chip color filters are not subjected to change in properties, and good-quality microlenses having an increased refractive index and transparency can be obtained.

Claims: A solid image pickup device (60), comprising: a substrate (12) having a plurality of light receiving portions (14), a plurality of microlenses (28) provided on said substrate (12) and arranged to converge incident light onto the light receiving portions (14), and a transparent resin layer (44) provided directly on the microlenses (28), having a substantially flat upper surface and having a refractive index less than that of the microlenses (28) such that incident light is converged by said microlenses (28) onto the light receiving portions (14); characterized in that said plurality of microlenses (28) are arranged in a single layer such that each of said light receiving portions (14) on said substrate (12) is positioned to receive light converged by a corresponding one of said plurality of microlenses (28) and in that a plurality of further microlenses (28) larger in size than said first-mentioned microlenses (28) are formed in a further layer on said transparent resin layer (44); wherein a further transparent resin layer (44) is formed on said further layer of further microlenses (28). A device as claimed in claim 1, packaged in a molded body (72) made of a transparent resin. A device as claimed in claim 1 or 2, wherein the material of said microlenses (28) is a polymeric resin selected from a group comprising polyimide resin, polyether amide resin, polystyrene resin, or other resins which have a refractive index of 1.6 to 1.8. A device as claimed in any preceding claim, wherein the material of said transparent resin layer (44) is a transparent polymeric resin selected from a group comprising epoxy resin, acrylic resin, perfluro resin or other resins which have a refractive index of 1.3 to 1.5. A device as claimed in any preceding claim, wherein said microlenses (28) are semi-spherical.

Inventors: MISAWA KIYOTOSHI, NAKA SHUN-ICHI, NAKAI JUN-ICHI, MISAWA, KIYOTOSHI, NAKA, SHUN-ICHI, NAKAI, JUN-ICHI
Applicants: SHARP KK, SHARP KABUSHIKI KAISHA
Application year: 1991
Main classification: H01L31
IPC codes: G02B3, H01L31, B29D11, H01L27