Amorphous alloys superior in mechanical strength, corrosion resistance and formability

Abstract: The present invention provides an amorphous alloy superior in mechanical strength, corrosion resistance and formability, at a relatively low cost, the amorphous alloy having a composition represented by the general formula: Al 100-x-y M x Ln y wherein M is at least one element selected from the group consisting of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zr, Nb, Mo, Hf, Ta and W; Ln is at least one element selected from the group consisting of Y, La, Ce, Nd, Sm, Gd, Tb, Dy, Ho and Yb or misch metal (Mm) which is a combination of rare earth elements; and x and y are, in atomic percentages: 0 < x ≦ 55 and 30 ≦ y ≦ 90, preferably 0 < x ≦ 40 and 35 ≦ y ≦ 80, and more preferably 5 < x ≦ 40 and 35 ≦ y ≦ 70, the alloy having at least 50% (by volume) an amorphous phase.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to amorphous alloys containing a rare earth element or elements and which have a high degree of hardness, strength, wear resistance, corrosion resistance and formability. 2. Description of the Prior Art Heretofore, rare earth metals have been used as additives for iron-based alloys or the like, or used in the form of intermetallic compounds for magnetic material applications. However, no practical use of rare earth metal-based alloys has been known up to now. As a characteristic property of rare earth metals, they generally have a low tensile-strength of 200 to 300 MPa. When rare earth metals are used as intermetallic compounds, there is a problem of poor formability. Therefore, there has been a strong demand for rare earth metal-based alloys having high strength and superior formability. Heretofore, when rare earth metals are used in rare earth metal-based alloys, the strength of the alloys is low. When rare earth metals are used in intermetallic compounds, an adequate formability can not be obtained. Therefore, the applications of these alloys have been limited to a narrow range, such as magnetic sintered materials and thin film materials. SUMMARY OF THE INVENTION It is accordingly an object of the present invention to improve the disadvantages of rare earth metal-based alloys, namely, low levels of strength and corrosion resistance and inferior formability of intermetallic compounds of rare earth metals, thereby enabling a greatly expanded use of rare earth metals as functional materials and resulting in a significantly reduced production cost. The present invention provides an amorphous Al-alloy having superior mechanical strength, corrosion resistance and formability, said amorphous alloy having a composition represented by the general formula: Al 100-x-y M x Ln y wherein: M is at least one element selected from the group consisting of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zr, Nb, Mo, Hf, Ta and W; Ln is at least one element selected from the group consisting of Y, La, Ce, Nd, Sm, Gd, Tb, Dy, Ho and Yb or misch metal (Mm) which is a combination of rare earth elements; and x and y are, in atomic percentages: 0 < x ≦ 55, 30 ≦ y ≦ 90 preferably 0 < x ≦ 40 and 35 ≦ y ≦ 80, and more preferably 5 < x ≦ 40 and 35 ≦ y ≦ 70, the alloy having at least 50% (by volume) an amorphous phase with the exception of brittle alloys. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a ternary compositional diagram showing the structure of an example of Al-Ni-La system alloy thin ribbons according to the present invention; FIG. 2 is a diagram showing the hardness of each test specimen; FIG. 3 is a diagram showing the glass transition temperature of each test specimen; FIG. 4 is a diagram showing glass crystallization temperature of each test specimen; FIG. 5 is a diagram showing a glass transition range; and FIG. 6 is an illustration showing an example of the preparation process according to the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The aluminum alloys of the present invention can be obtained by rapidly solidifying a melt of the alloy having the composition as specified above by means of a liquid quenching technique. The liquid quenching technique is a method for rapidly cooling a molten alloy and, particularly, single-roller melt-spinning technique, twin roller melt-spinning technique, in-rotating-water melt-spinning technique or the like are mentioned as effective examples of such a technique. In these techniques, a cooling rate of about 10⁴ to 10⁶ K/sec can be obtained. In order to produce thin ribbon materials by the single-roller melt-spinning technique or twin roller melt-spinning technique, the molten alloy is ejected from the opening of a nozzle onto a roll of, for example, copper or steel, with a diameter of 30 - 3000 mm, which is rotating at a constant rate within the range of about 300 - 10000 rpm. In these techniques, various thin ribbon materials with a width of about 1 - 300 mm and a thickness of about 5 - 500 µm can readily be obtained. Alternatively, in order to produce fine wire materials by the in-rotating-water melt-spinning technique, a jet of the molten alloy is directed, under application of a back pressure of argon gas, through a nozzle into a liquid refrigerant layer having a depth of about 10 to 100 mm and which is retained by centrifugal force in a drum rotating at a rate of about 50 to 500 rpm. In such a manner, fine wire materials can be readily obtained. In this technique, the angle between the molten alloy ejecting from the nozzle and the liquid refrigerant surface is preferably in the range of about 60° to 90° and the ratio of the velocity of the ejected molten alloy to the velocity of the liquid refrigerant is preferably in the range of about 0.7 to 0.9. Besides the above process, the alloy of the present invention can be also obtained in the form of thin film by a sputtering process. Further, a rapidly solidified powder of the alloy composition of the present invention can be obtained by various atomizing processes, for example, a high pressure gas atomizing process or spray process. Whether the rapidly solidified alloys thus obtained are amorphous or not can be known by checking the presence of the characteristic halo pattern of an amorphous structure by using an ordinary X-ray diffraction method. The amorphous structure is transformed into a crystalline structure by heating to a certain temperature (called "crystallization temperature") or higher temperatures. In the aluminum alloys of the present invention represented by the above general formula, "x" is limited to the range of more than 0 (not including 0) to 55 atomic% and "y" is limited to the range of 30 to 90 atomic %. The reason for such limitations is that when "x" and "y" stray from the above specified ranges and certain ranges, it is difficult to form an amorphous phase in the resulting alloys and the intended alloys having at least 50 volume % of an amorphous phase can not be obtained by industrial cooling techniques using the above-mentioned liquid quenching techniques, etc. In the above specified compositional range, the alloys of the present invention exhibit advantageous properties, such as high hardness, high strength and high corrosion resistance which are characteristic of amorphous alloys. The certain ranges set forth above have been disclosed in Assignee's U.S. Patent No. 4,911,767, issued March 27, 1990 (Japanese Patent Application No. 63-61877) and Assignee's prior U.S. Patent Application Serial No. 345 677, filed April 28, 1989 (Japanese Patent Application No. 63-103812) and, thus, these ranges are excluded from the scope of Claims of the present invention in order to avoid any compositional overlap. When the values of "x" and "y" are: 0 < x ≦ 40 atomic % and 35 ≦ y ≦ 80 atomic %, the resulting amorphous alloys, besides having the various advantageous properties characteristic of amorphous alloys, exhibit a superior ductility sufficient to permit a bending of 180° in the form of ribbons. Such a high degree of ductility is desirable in improving the physical properties, e.g., impact-resistance and elongation, of the materials. Particularly, in the ranges of 5 < x ≦ 40 atomic % and 35 ≦ y ≦ 70 atomic %, the above advantageous properties can be ensured at higher levels and, further, a wider glass transition range (Tx-Tg) can be achieved. In the glass transition range, the alloy material is in a supercooled liquid state and, exhibits a very superior formability which permits a large degree of deformation under application of a small stress. Such advantageous properties make the resulting alloy materials very suitable for applications such as parts having complicated shapes or articles prepared by processing operations requiring a high degree of plastic flow. The "M" element is at least one element selected from the group consisting of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zr, Nb, Mo, Hf, Ta and W. These elements in coexistence with Al not only improve the capability to form an amorphous phase, but also provide an increased crystallization temperature in combination with improved hardness and strength. The "Ln" element is at least one element selected from the group consisting of rare earth elements (Y and elements of atomic numbers of 57 to 70) and the rare earth element or elements may be replaced by Mm which is a mixture of rare earth elements. Mm used herein consists of 40 - 50% Ce and 20 to 25% La, the balance being other rare earth elements and impurities (Mg, Al, Si, Fe, etc) in acceptable amounts. The rare earth elements represented by "Ln" can be replaced with Mm in a ratio of about 1:1 (by atomic percent) in the formation of the amorphous phase contemplated by the present invention and Mm provides a greatly economical advantage as a practical source material of the alloying element "Ln" because of its cheap price. The alloys of the present invention exhibit a supercooled liquid state (glass transition range) in a very wide temperature range and some compositions exhibit a glass transition temperature range of 60 K or more. In the temperature range of the supercooled liquid state, plastic deformation can be performed under a low pressure with ease and without any restriction. Therefore; powder or thin ribbons can be easily consolidated by conventional processing techniques, for example, extrusion, rolling, forging or hot pressing. Further, due to the same reason, the alloy powder of the present invention in a mixture with other alloy powder can be also easily compacted and molded into composite articles at a low temperature and low pressure. Further, since the amorphous ribbons of the invention alloys produced by liquid quenching techniques have a superior ductility, they can be subjected to a bending of 180° in a wide compositional range, without cracking or separation from a substrate. Appropriate selection of Fe, Co, etc., as the "M" element., and Sm, Gd, etc as the "Ln" element provides various kinds of magnetic amorphous materials in a bulk form or thin film form. Also, consolidated amorphous materials can be converted to crystalline materials by retaining them at a crystallization temperature or higher temperatures for an appropriate period of time. Now, the present invention will be more specifically described with reference to the following examples. Example 1 A molten alloy 3 having a predetermined alloy composition was prepared by a high-frequency induction melting process and was charged into a quartz tube 1 having a small opening 5 with a diameter of 0.5 mm at the tip thereof, as shown in FIG. 6. After heating and melting the alloy 3, the quartz tube 1 was disposed right above a copper roll 2 having a diameter of 200 mm. Then, the molten alloy 3 contained in the quartz tube 1 was ejected from the small opening 5 of the quartz tube 1 under application of an argon gas pressure of 7x10⁴ Pa 0.7 kg/cm² and brought into contact with the surface of the roll 2 rapidly rotating at a rate of 5,000 rpm. The molten alloy 3 was rapidly solidified and an alloy thin ribbon 4 was obtained. According to the processing conditions as described above, there were obtained thin ribbons of ternary alloys, as shown in a compositional diagram of an Al-Ni-La system. In the compositional diagram, the percentages of each element are recorded at an interval of 5 atomic %. X-ray diffraction analysis for the resulting thin ribbons showed that an amorphous phase was obtained in a very wide compositional range. In FIG. 1, the mark "O ○" indicates an amorphous phase and a ductility sufficient to permit a bending of 180° without fracture, the mark "O" indicates an amorphous phase and brittleness, the mark " " indicates a mixed phase of an amorphous phase and a crystalline phase, and the mark "" indicates a crystalline phase. FIGS. 2, 3, 4 and 5 show the measurement results of the hardness (Hv = hardness Vickers), glass transition temperature (Tg), crystallization temperature (Tx) and glass transition range (Tx-Tg), respectively, for each thin ribbon specimen. FIG. 2 indicates the distribution of the hardness of thin ribbons falling within the amorphous phase region of the compositions shown in FIG. 1. The alloys of the present invention have a high level of hardness (Hv) of 180 to 500 (DPN) and the hardness is variable depending only on the variation of the content of La regardless of the variations of the contents of Al and Ni. More specifically, when the La content is 30 atomic %, the Hv is on the order of 400 to 500 (DPN) and, thereafter, the hardness decreases with an increase in La content. The hardness Hv shows a minimum value of 180 (DPN) when the La content is 70 atomic % and, thereafter, it slightly increases with an increase in La content. FIG. 3 shows the change in Tg (glass transition temperature) of the amorphous phase region shown in FIG. 1 and the Tg change greatly depends on the variation in La content, as in the hardness change. More specifically, when the La content is 30 atomic %, the Tg value is 600 K and, thereafter, the Tg decreases with an increase in La content and reaches 420K at a La content of 70 atomic %. La contents falling outside the above range provide no Tg. FIG. 4 illustrates the variations in Tx (crystallization temperature) of thin ribbons falling within the amorphous phase forming region shown in FIG. 1 and shows a strong dependence on the content of La as referred to FIGS. 2 and 3. More specifically, a La content of 30 atomic % provides a high Tx level of 660 K and, thereafter, the Tx decreases with an increase in La content. A La content of 70 atomic % provides a minimum Tx value of 420 K and, thereafter, Tx values slightly increase. FIG. 5 is a diagram plotting the difference (Tx-Tg) between Tg and Tx, which are shown in FIGS. 3 and 4, respectively, and the diagram shows a temperature range of the glass transition range. In the diagram, the wider the temperature range, the more stable the amorphous phase becomes. Using such a temperature range, processing and forming operations can be conducted in a wider range with respect to operation temperature and time while retaining an amorphous phase and various operation conditions can be easily controlled. The value of 60 K at a La content of 50 atomic % as shown in FIG. 5 means the alloy has a stable amorphous phase and a superior processability. Further, Table 1 shows the results of tensile strength (δf) measurements for five test specimens included within the compositional range which provides an amorphous phase, together with the hardness, glass transition temperature and crystallization temperature. All of the tested specimens showed high strength levels of not less than 500 MPa and have been found to be high strength materials. Alloy composition δf(MPa) Hv(DPN) Tg(K) Tx(K) La₄₅Al₄₅Ni₁₀ 792 330 580 610 La₄₅Al₃₅Ni₂₀ 716 287 537 594 La₅₀Al₃₅Ni₁₅ 685 285 523 582 La₅₀Al₃₀Ni₂₀ 713 305 510 578 La₅₅Al₂₅Ni₂₀ 512 221 478 542 As set forth above, the alloys of the present invention have an amorphous phase in a wide compositional range and have a glass transition region in a large portion of the compositional range. Therefore, it can be seen that the alloys of the present invention are materials with good formability combined with high strength. Example 2 Amorphous alloy thin ribbons having 21 different alloy compositions as shown in Table 2 were prepared in the same manner as described in Example 1 and measured for tensile strength, hardness, glass transition temperature and crystallization temperature. It has been found that all of the test specimen are in an amorphous state and are high strength, thermally stable materials having a tensile strength of not less than 500 MPa, Hv of not less than 200 (DPN) and a crystallization temperature of not lower than 500 K. Alloy Composition δf(MPa) Hv(DPN) Tg(K) Tx(K) 1. Al₄₅Fe₁₀La₄₅ - 573 - - 2. Al₃₀Fe₂₀Ce₅₀ 813 330 598 612 3. Al₁₅Fe₂₅Sm₆₀ 615 316 523 560 4. Al₂₀Cu₁₅Co₁₅La₅₀ - 385 530 585 5. Al₃₅Cu₁₀Mm₅₅ 565 254 545 576 6. Al₂₅Ni₅Hf₁₀Mm₆₀ 512 230 498 542 7. Al₃₅Ni₁₀Ti₅Mm₅₀ - 396 520 545 8. Al₃₅Ni₁₀V₁₀Mm₄₅ 726 303 541 585 9. Al₃₀Ni₁₀Zr₁₀Mm₅₀ 610 293 565 598 10. Al₃₅Ni₁₀V₁₀Mm₄₅ 726 303 541 585 11. Al₅₀Fe₁₀Nb₅Mm₃₅ - 470 615 632 12. Al₃₀Fe₁₀Mn₅Mm₅₅ - 295 516 565 13. Al₁₀Ni₁₅La₆₅Y₁₀ 503 211 483 545 14. Al₂₅Ni₁₅Cr₁₀Mm₅₀ 785 355 560 578 15. Al₃₀Fe₁₀Mn₁₀Mm₅₀ 750 341 532 551 16. Al₁₅Fe₁₀Mo₁₀Mm₆₅ 678 311 538 552 17 Al₄₀Ni₅Zr₁₀Mm₄₅ 812 394 487 516 18. Al₁₅Ni₅Nb₁₀Mm₇₀ 693 331 478 502 19. Al₁₅Ni₁₀Ta₅Mm₇₀ 705 364 497 509 20. Al₃₀Fe₁₀W₅Mm₅₅ 783 389 563 592 21. Al₃₀Ni₁₀Hf₅Mm₅₅ 752 341 543 565 Example 3 A further amorphous ribbon was prepared from an alloy having the composition Al₃₅Ni₁₅La₅₀ in the same way as described in Example 1 and was comminuted into a powder having a mean particle size of about 20 µm using a rotary mill which has been heretofore known as a comminution device. The comminuted powder was loaded into a metal mold and compression-molded under a pressure of 2x10⁸ Pa (20 kg/mm²) at 550 K for a period of 20 minutes in an argon gas atmosphere to give a consolidated bulk material of 10 mm in diameter and 8 mm in height. There was obtained a high strength consolidated bulk material having a density of at least 99% relative to the theoretical density and no pores or voids were detected under an optical microscope. The consolidated material was subjected to X-ray diffraction. It was confirmed that an amorphous phase was retained in the consolidated bulk materials. Example 4 An amorphous alloy powder of Al₃₅Ni₁₅La₅₀ obtained in the same way as set forth in Example 3 was added in an amount of 5% by weight to alumina powder having a mean particle size of 3 µm and was hot pressed under the same conditions as in Example 3 to obtain a composite bulk material. The bulk material was investigated by an X-ray microanalyzer and it was found that it had a uniform structure in which the alumina powder was surrounded with an alloy thin layer (1 to 2 µ) with strong adhesion. As set forth above, the present invention provides novel amorphous Al-alloys which have an advantageous combination of high hardness, high strength, high wear-resistance and superior corrosion resistance and can be subjected to a large degree of bending operation, at a relatively low cost.

Claims: An amorphous Al alloy superior in mechanical strength, corrosion resistance and formability, said alloy having a composition represented by the general formula: Al 100-x-y M x Ln y wherein: M is at least one element selected from the group consisting of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zr, Nb, Mo, Hf, Ta and W; Ln is at least one element selected from the group consisting of Y, La, Ce, Nd, Sm, Gd, Tb, Dy, Ho and Yb or misch metal which is a combination of rare earth elements; and x and y are atomic percentages falling within the following ranges: 0 < x ≦ 55 and 30 ≦ y ≦ 90, said amorphous alloy having at least 50% (by volume) an amorphous phase with the exception of brittle alloys. An amorphous alloy as claimed in Claim 1 in which said x and y are atomic percentages falling within the ranges: 0 < x ≦ 40 and 35 ≦ y ≦ 80. An amorphous alloy as claimed in Claim 1 in which said x and y are atomic percentages falling within the ranges: 5 < x ≦ 40 and 35 ≦ y ≦ 70.

Inventors: INOUE AKIHISA, KITA KAZUHIKO, MASUMOTO TSUYOSHI, TAKEDA HIDEKI, YAMAGUCHI HITOSHI, INOUE, AKIHISA, KITA, KAZUHIKO, MASUMOTO, TSUYOSHI, TAKEDA, HIDEKI, YAMAGUCHI, HITOSHI
Applicants: MASUMOTO TSUYOSHI, TEIKOKU PISTON RING CO LTD, YOSHIDA KOGYO KK, MASUMOTO, TSUYOSHI, TEIKOKU PISTON RING CO. LTD., YOSHIDA KOGYO K.K.
Application year: 1990
Main classification: C22C21
IPC codes: C22C45, C22C21, C22C28