INJECTION MOLDING APPARATUS

Abstract: An injection molding apparatus is of the screw in-line type and has a screw (1) rotationally and axially movable in an extrusion cylinder (2), and is used for injection-molding a high-nitryl resin. The screw (1) has the following features, namely a compression ratio set to a value of 1.8 to 2.5; lengths of the feed, compression, and metering sections set in the ratios of [1 to 1.5] : [1.8 to 2.8] : [1]; a depth T (unit:mm) of the groove, in the metering section, between its flight (1b) and the diameter D (unit: mm) of its cylindrical shaft (1a) set to T ≧ 0.057D - 0.2; and a radius of curvature R (unit:­ mm) of the arcuate surface (1c) at a rear corner portion which is formed between the screw shaft (1a) and a flight (1b), in relation to the inner diameter D (unit: mm) of cylindrical shaft, set to R ≧ 0.36D + 2.0.

Description: The present invention relates to an injection molding apparatus for high-nitryl resins and, more particularly, to an injection molding apparatus for high-nitryl resins which can provide an excellent quality stability of a long time, for products obtained from the molding. Since a high-nitryl resin is excellent in chemical resistance and gas barrier properties it is used as a container material inter alia for cosmetics, stationery, chemicals and foods. Hitherto, such containers have mainly been formed by extrusion molding or blow molding. However, in recent years, they are also manufactured by injection molding. However, since a high-nitryl resin contains a large quantity of nitryl compound, its heat stability is inferior to that of a general resin such as polyolefin or the like. On the other hand, since the melt viscosity is high, if a high-nitryl resin is melt kneaded upon molding, heat is easily generated. In the case of injecting molding a resin having such characteristics, generally a screw of a low compression, a gentle compression, and a deep groove is considered to be suitable. In the case of a high-nitryl resin, in order to prevent the heat generation of the melted resin, a screw of a low compression, a gentle compression, and a deep groove in which a compression ratio is set to about 1.8 to 2.5 and length distribution ratios of the feed section, compression section, and metering section are set to about [1 to 1.5] : [1.8 to 2.8] : [1] is preferably used only in the molding of a relatively short time. However, even in such a screw, there is a problem such that if the molding was continued for a long time, a yellowing occurs in the molded article and a good product cannot be obtained. It is an object of the invention to provide an injection molding apparatus for high-nitryl resin which can execute the molding for a long time and can solve the foregoing problems. The present inventors have studied and examined the problems and they have found that a good result can be obtained by using a screw of a deep groove, a low compression, and a gentle compression as mentioned above when a radius of curvature of an arcuate surface of a rear side corner portion which is formed between a screw shaft and a flight is set to a predetermined large value or more. The present invention commences from US-A-4,648,827 which discloses an injection molding apparatus of a screw in-line type for injection molding a high-nitrile resin, wherein the injection screw, having a screw flight of uniform diameter and working in a cylinder of uniform bore diameter, has three contiguous sections comprising a feed section, a compression section and a metering section. The present invention is characterised in that (1) the flight has a constant pitch and width or thickness along the length of the screw; (2) the screw has a shaft or shank the diameter of which varies along its length thereby to form with the flight a groove of varying depth; (3) the shank having a constant minimum diameter in the feed section, a constant maximum diameter in the metering section and a diameter increasing from the minimum to the maximum in the compression section; (4) the lengths of the feed, compression and metering sections being in the ratios [1 to 1.5]: [1.8 to 2.8]: [1] respectively; (5) the screw having a compression ratio defined as the ratio of the maximum depth of the groove to the minimum depth thereof in the compression section in the range of [1.8 to 2.5]: [1]; (6) the depth T (unit: mm) of the groove of the metering section in relation to an inner diameter D (unit: mm) of the cylinder is: T ≧ 0.057D - 0.2, and (7) the flight has a rear face (considered relative to the direction of feed) which at its juncture with the shank comprises an arcuate surface the radius of curvature R (unit: mm) of which, in relation to the inner diameter D (unit: mm) of the cylinder is: R ≧ 0.36D + 2.0. Employing the injection molding apparatus of the invention including the screw with the construction as defined above, a high-nitryl resin can be stably molded for a long time and excellent molded articles can be efficiently produced without causing the yellowing or the like. A high-nitryl resin which is molded by the injection molding apparatus according to the invention is a copolymer mainly comprising an unsaturated nitryl compound such as acrylonitrile, metacrylonitrile. or the like and contains 50 weight % or more, preferably, 55 weight % or more of an unsaturated nitryl compound unit. An unsaturated compound which can be copolymerized with a nitryl compound can be used as comonomer. For example, an unsaturated aromatic compound, a diene compound, an unsaturated ester compound, an unsaturated ether compound, etc. can be employed as such an unsaturated compound. More particularly, there can be utilized styrene, α-methylstyrene, butadiene, isoprene, methylacrylate, ethylacrylate, methylmetacrylate, ethylmetacrylate, etc. and one or more kinds of them may be copolymerized with an unsaturated nitryl compound. On the other hand, a rubber-like copolymer of a butadiene-acrylonitrile copolymer, a butadiene-styrene copolymer, an isoprene-styrene copolymer, and a polybutadiene, polyisoprene, or the like can be mixed with a copolymer mentioned above, so as to form the above mentioned unsaturated nitryl unit and the resultant copolymer may be used as a high-nitryl resin. Under the existence of those rubber-like copolymers, a mixture of an unsaturated nitryl compound and the above comonomer is copolymerized and the resultant copolymer can be also used. Those copolymers are preferable since they have a impact resistance. Further, it is also possible to use a high-nitryl resin mixed with a rubber-like copolymer as mentioned above. That is, a copolymer of an unsaturated nitryl compound with said comonomer is formed to a matrix and a mixture with such a rubber-like copolymer can be used as a high-nitryl resin, said rubber-like copolymer having a graft portion of composition similar to such a matrix or a graft portion having a compatibility with such a matrix. An oxidation inhibitor, an ultraviolet absorbent, an antistatic agent, a lubricant, an inorganic filler, a color pigment, or the like or a small amount of other resin can be also contained in those high-nitryl resins. The invention will now be explained in more detail, by way of example only in the following non-limiting description. Fig. 1 is a partial sectional view showing the main portion of an injection molding apparatus according to the present invention; and Fig. 2 is a diagrammatical view showing a portion of a screw which is used in the apparatus of Fig. 1. In Fig. 1, reference numeral 1 denotes a screw; 2 indicates a cylinder; 3 a piston which is attached between a screw drive shaft 4 and the screw 1 and adapted to advance a resin under pressure; 5 a piston which is attached to one end of the screw drive shaft 4 and is used to move the screw forwardly or backwardly; 6 a motor for rotating the screw; 7 an output shaft of the motor 6; and 8, 9 and 10 gears. The gear 10 rotates the screw drive shaft 4. However, the gear 10 is attached to the screw drive shaft 4 so as not to prevent the screw drive shaft 4 from moving to the right and left in the drawing, in other words, so as to enable the screw drive shaft 4 to move in its axial direction. The gear 10 is restricted by a member 11 so as not to move in the main shaft direction of the screw drive shaft 4. Reference numeral 12 denotes a rod of a hydraulic cylinder (not shown). The rod 12 is used to move the cylinder 2 to the right and left in the drawing. Reference numeral 13 denotes a hopper to supply a raw material resin. Reference numeral 14 denotes an attaching base for a fixed die, and the fixed die 15 is attached to the die attaching base 14. Reference numeral 16 denotes a movable die. The die 16 is brought into pressure contact with the fixed die 15 by a rod 17 of a hydraulic cylinder (not shown) or is removed from the die 16 to take out a molded article. Reference numeral 18 denotes a heater for heating the cylinder 2; 19 indicates a cam attached to the screw drive shaft 4; 20 and 21 limit switches; 22 pellets of the raw material resin; 23 melted resin; 24 resin which has been injected into the cavity of the die; and 25 a hydraulic equipment for driving the piston 5. Fig. 2 is a partial enlarged side elevational view showing the details of a screw for the injection molding apparatus according to the invention. As is well known, the screw 1 comprises a material feed section A on the hopper side having a constant small boss diameter; a compression section B whose boss diameter gradually increases toward the injection port; and a metering section C whose boss diameter is constant and large and which forms a tip portion of the screw. Since the construction and the operation of the apparatus itself are well known, their descriptions are omitted here. The present invention concerns the structure of the screw 1 and will be described in detail with reference to Fig. 2. In Fig. 2, reference numeral 1 denotes the screw main body; 1a denotes a screw shaft; 1b a flight; 1c an arcuate surface of the rear side corner portion which is formed between the screw shaft 1a and the flight 1b; and 1d an arcuate surface of the front side corner portion which is formed between the screw shaft 1a and the flight 1b. The terms "front" and "rear" are, of course, related to the direction of movement of the resin through the screw extruder. A radius of curvature of the arcuate surface 1c of the rear side corner portion of the screw is generally set to a value of 5 to 10 mm in the case of the screw for the injection molding apparatus in which an inner diameter D of the cylinder 2 is set to a value of about 30 to 50 mm. However, with such a well-known screw, a high-nitryl resin cannot be successfully molded. A screw which is used in the present invention is constructed in a manner such that a low compression, a gentle compression, and a deep groove are provided for the screw for injection-molding a high-nitryl resin and, further, a radius of curvature R (mm)of the arcuate surface 1c of the rear side corner portion which is formed between the screw shaft 1a and the flight 1b is set to a value of 0.36D + 2.0 or more. In the case where the radius of curvature R of the arcuate surface 1c of the rear side corner portion which is formed between the screw shaft 1a and the flight 1b is smaller than a value of 0.36D + 2.0 or in the case where a compression ratio is larger than 2.5 even if the curvature R is larger than a value of 0.36D + 2.0 or in the case of a high speed compression or the like, molding stability for a long time is not obtained and the molded article is yellowed. The arcuate surface 1c of the rear side corner portion which is formed between the screw shaft 1a and the flight 1b is not needed to be set to a complete circular arc surface but it is sufficient to set the arcuate surface 1c to a shape which is close to a substantially circular arc surface. On the other hand, a radius of curvature of the arcuate surface 1d of the front side corner portion which is formed between the screw shaft 1a and the flight 1b is not particularly limited. A check ring to prevent a counter flow of the resin may be also provided for the screw which is used in the apparatus of the invention. However, it is desirable to use a check ring in which a residence portion of the resin does not exist and an opening rate is large. On the other hand, in order to improve the dispersibility of, for instance, a color pigment or the like, a mixing pin or the like may be also provided for the screw which is used in the invention. Further, hard chromium or the like may be also plated on the screw. In order to reduce a heat history, it is desirable that a ratio L/D of a length L of cylinder to the inner diameter D is set to a value of about 12 to 22. Various embodiments of the screw of the injection molding apparatus according to the present invention and practical molded examples which were obtained by using those embodiments will now be described hereinbelow together with comparison examples. Example 1 BAREX 1010N (trademark of products by Mitsui Toatsu Chemicals Inc.) as a high-nitryl resin was injection molded by a molding cycle of about 30 seconds by means of an injection molding apparatus having an injection cylinder, the inner diameter D of which is 36 mm, and a screw having the L/D of 20, the compression ratio of 2.0, the depth T of groove of the measuring section of 3 mm, the distribution ratios of the feed section, the compression section, and the metering section of about 1.3 : 2.3 : 1, the radius of curvature R of the arcuate surface of the rear side corner portion which is formed between the screw shaft and the flight is set to 15 mm, and the radius of curvature of the arcuate surface of the front side corner portion of 3mm. The time until a yellowed substance is produced was measurred. The result is shown in Table 1. Examples 2 and 3 The times until a yellowed substance is produced were measured in a manner similar to the Example 1 except that the radius of curvature R of the arcuate surface of the rear side corner portion which is formed between the screw shaft and the flight in the example 1 was changed to 20 mm in the example 2 and to 25 mm in the example 3 respectively. The results are shown in Table 1. Comparisons 1 and 2 The times until a yellowed substance is produced were measured in a manner similar to the example 1 except that the radius of curvature R of the arcuate surface of the rear side corner portion which is formed between the screw shaft and the flight in the example 1 was changed to 5 mm in Comparison 1 and to 10 mm in Comparison 2. The results are shown in Table 1. Example 4 BAREX 2090N (trademark of products by Mitsui Toatsu Chemicals Inc.) as a high-nitryl resin was injection-molded in a molding cycle of about 30 seconds by means of an injection molding apparatus an injection cylinder the inner diameter D of which is 50 mm, and a screw having the L/D of 20, the compression ratio is of 2.2, the depth T of groove of the metering section of 4 mm, the distribution ratios of the feed section, the compression section, and the metering section of about 1.4 : 2.5 : 1, the radius of curvature R of the arcuate surface of the rear side corner portion which is formed between the screw shaft and the flight of 20 mm, and the radius of curvature of the arcuate surface of the front side corner portion of 5mm. The time until a yellowed substance is produced was measured. The result is shown in Table 1. Example 5 The time until a yellowed substance is produced was measured in a manner similar to the example 1 except that the radius of curvature R of the arcuate surface of the rear side corner portion which is formed between the screw shaft and hte flight in the example 4 was changed to 30 mm. The result is shown in Table 1. Comparison 3 The time until a yellowed substance is produced was measured in a manner similar to the example 1 except that the radius of curvature R of the arcuate surface of the rear side corner portion which is formed between the screw shaft and the flight in the example 4 was changed to 10 mm. The result is shown in Table 1. Comparison 4 The time until a yellowed substance is produced was measured in a manner similar to the example 4 except that the compression ratio in the example 4 was changed to 3.5. The result is shown in Table 1. It should be understood that from the above examples and comparisons, the following results are obtained. By using the screw of a form in which (1) the compression ratio is set to a value of 1.8 to 2.5, (2) the ratios of the lengths of the feed section, the compression section, and the metering section are set to [1 to 1.5] : [1.8 to 2.8] : [1] , (3) the depth T of groove of the metering section in relation to the inner diameter D of cylinder is set to T ≧ 0.057D-1.2, and (4) the radius of curvature R of the arcuate surface of the rear side corner portion which is formed between the screw shaft and the flight in relation to the inner diameter D of cylinder is set to R ≧ 0.36D+ 2.0, the time until a yellowed substance is produced is extremely lengthened and the molding can be executed stably for a long time as compared with the case of using prior art screws. Thus, thanks to the injection molding apparatus of the present invention, in the injection molding for high-nitryl resin, molding stability for an extremely long time is obtained. Therefore, productivity is improved by using the injection molding apparatus of the invention. On the other hand, it is also possible to mold a colored article such as a white colored article in which a discoloration is easily conspicuous.

Claims: An injection molding apparatus of a screw in-line type for injection molding a high-nitrile resin, wherein the injection screw (1), having a screw flight (1b) of uniform diameter and working in a cylinder (2) of uniform bore diameter, has three contiguous sections comprising a feed section (A), a compression section (B) and a metering section (C), characterised in that: (1) the flight (1b) has a constant pitch and width or thickness along the length of the screw (1); (2) the screw (1) has a shaft or shank (1a) the diameter of which varies along its length thereby to form with the flight (1b) a groove of varying depth (T); (3) the shank (1a) having a constant minimum diameter in the feed section (A), a constant maximum diameter in the metering section (C) and a diameter increasing from the minimum to the maximum in the compression section (B); (4) the lengths of the feed, compression and metering sections being in the ratios [1 to 1.5]: [1.8 to 2.8]: [1] respectively; (5) the screw having a compression ratio defined as the ratio of the maximum depth of the groove to the minimum depth thereof in the compression section (B) in the range of [1.8 to 2.5]: [1]; (6) the depth T (unit: mm) of the groove of the metering section (C) in relation to an inner diameter D (unit: mm) of the cylinder (2) is: T ≧ 0.057D - 0.2, and (7) the flight (1b) has a rear face (considered relative to the direction of feed) which at its juncture with the shank (1a) comprises an arcuate surface (1c) the radius of curvature R (unit: mm) of which, in relation to the inner diameter D (unit: mm) of the cylinder (2) is: R ≧ 0.36D + 2.0. A method of molding a high-nitrile resin or a molding composition including a high-nitryl resin, wherein the resin or molding composition is extruded and then injected into a molding cavity using an injection molding process of a screw in-line type, wherein the injection screw (1), having a screw flight (1b) of uniform diameter and working in a cylinder (2) of uniform bore diameter, has three contiguous sections comprising a feed section (A), a compression section (B) and a metering section (C), characterised in that: (1) the flight (1b) has a constant pitch and width or thickness along the length of the screw (1); (2) the screw (1) has a shaft or shank (1a) the diameter of which varies along its length thereby to form with the flight (1b) a groove of varying depth (T); (3) the shank (1a) having a constant minimum diameter in the feed section (A), a constant maximum diameter in the metering section (C) and a diameter increasing from the minimum to the maximum in the compression section (B); (4) the lengths of the feed, compression and metering sections being in the ratios [1 to 1.5]: [1.8 to 2.8]: [1] respectively; (5) the screw having a compression ratio defined as the ratio of the maximum depth of the groove to the minimum depth thereof in the compression section (B) in the range of [1.8 to 2.5]: [1]; (6) the depth T (unit: mm) of the groove of the metering section (C) in relation to an inner diameter D (unit: mm) of the cylinder (2) is: T ≧ 0.057D - 0.2, and (7) the flight (1b) has a rear face (considered relative to the direction of feed) which at its juncture with the shank (1a) comprises an arcuate surface (1c) the radius of curvature R (unit: mm) of which, in relation to the inner diameter D (unit: mm) of the cylinder (2) is: R ≧ 0.36D + 2.0.

Inventors: AMEMIYA, HIDEO, KURODA, MINORU, NITTA, TOMIO
Applicants: KABUSHIKI GAISHA TOKAI, MITSUI TOATSU CHEMICALS, INC.
Application year: 1990
Main classification: B29C45
IPC codes: B29K79, B29K33, B29C45