Rubber compositions and preparation thereof

Abstract: A conductive rubber composition is prepared by blending (A) a rubber composition including natural and/or synthetic rubber and conductive carbon black, with (B) a silicone rubber composition including an organopolysiloxane having the average composition formula: R n SiO (4-n)/2 wherein R is a hydrocarbon group and n is a positive number of from 1.95 to 2.05. This rubber composition and cured products thereof have stable electric resistivity in the semiconductive range and are thus suitable as rubber roll members in business machines.

Description: This invention relates to rubber compositions and rubber articles made from them, particularly those affording an electric resistivity in the semiconductive range of from 10³ to 10¹⁰ Ω.cm; also to methods for preparing the same. Rubbery materials are usually electric insulators. A number of conductive rubbers are available as mixtures of rubbery material and conductive agents. For example, rubbers having carbon black blended therein to provide an electric resistivity of from 10⁻¹ to 10² Ω.cm are conductive rubbers which are used in various applications. Silicone rubber is also widely used as electrically insulating rubber because of its heat resistance, low-temperature resistance and weatherability. It can also be used as conductive silicone rubber by adding conductive agents like in the other rubbery materials. The conductive agents which are added to silicone rubber for imparting electric conductivity are typically carbon black, graphite, various metal powders such as silver, nickel, and copper, various non-conductive particles and monofilaments surface treated with silver or similar metals, carbon fibers, and metallic fibers. By mixing these conductive agents, the electric resistivity of silicone rubber can be reduced to the order of 10¹⁰ to 10⁻³ Ω.cm depending on the type and amount of conductive agent without detracting from the inherent properties of silicone rubber. However, silicone rubbers having conductive carbon black such as Ketjen black and acetylene black blended therein show a substantial variation of electric resistivity in the semiconductive range of from 10³ to 10¹⁰ Ω.cm. It is difficult to maintain the electric resistivity of carbon black filled silicone rubbers stable probably because the dispersion of carbon substantially varies with moulding conditions. A variety of rubbery parts e.g. rollers are used in business machines and represent a demand for rubbery material having electric resistivity in the semiconductive range. It would be desirable to provide rubbery material exhibiting a minimal variation of electric resistivity in the semiconductive range, that is, a stable electric resistivity, for such uses. Australian patent AU-B-18406/88 reveals an electroconductive silicone rubber composition which may be used in admixture with various rubbers but only those which permit retention of the conductive constituents in the silicone rubber phase. US patent US4714734 similarly discloses a polyorganosiloxane composition including carbon black, primarily to improve strength and similar mechanical properties. This too may be used in admixture with various other organic rubbers but without attention to the retention of the carbon black in the polyorganosiloxane phase or the resulting electrical properties. US patent US3021292 discloses the mixing of a vulcanisable gum and an organopolysiloxane gum together with an inorganic filler, again without regard for the electrical properties of the resultant mixture. We seek to provide new conductive rubber compositions. Preferably, we aim also (i) to provide a new and improved rubber composition capable of affording rubber articles exhibiting a limited variation of electric resistivity in the semiconductive range, and/or (ii) to provide a rubber composition capable of affording rubber articles having a stable electric resistivity independent of molding conditions. A further object is to provide a method for forming such rubber compositions. The inventors have found that by mixing (A) a rubber composition including natural and/or synthetic rubber and conductive carbon black with (B) a silicone rubber composition including an organopolysiloxane having the average composition formula (1): R n SiO (4-n)/2 wherein R is a substituted or unsubstituted monovalent hydrocarbon group having 1 to 10 carbon atoms, and n is a positive number of from 1.95 to 2.05, they were able to obtain rubber compositions yielding rubber articles having a well stabilized electric resistivity in the range of from 10³ to 10¹⁰ Ω.cm. Other aspects and preferred features are set out in the claims. More particularly, rubber compositions in the form of a mixture of (A) a rubber composition including natural and/or synthetic rubber and conductive carbon black and (B) a silicone rubber composition including an organopolysiloxane were found to have a well-stabilized electric resistivity in the semiconductive range with little or no dependence on molding conditions. They showed a variation of electric resistivity of the order of only one figure, in contrast to conventional silicone rubbers filled with conductive carbon black showing a variation of the order of 4 to 6 figures. The compositions may have improved moldability and vulcanization, and provide cured rubbers which have good rubbery elasticity and low hardness and do not release conductive carbon. Therefore, the present invention provides a rubber composition comprising, in admixture, (A) a rubber composition including natural and/or synthetic rubber and conductive carbon black and (B) a silicone rubber composition including an organopolysiloxane having average composition formula (1). The present invention also provides a method for preparing a rubber composition by mixing rubber composition (A) with silicone rubber composition (B) both defined above. The natural and synthetic rubbers used herein are not particularly limited and any desired one of commercially available natural and synthetic rubbers or mixtures thereof may be used. Examples of the synthetic rubber include styrene-butadiene rubbers, acrylonitrile-butadiene rubbers, hydrogenated acrylonitrile-butadiene rubbers, butadiene rubbers, isoprene rubbers, chloroprene rubbers, acrylic rubbers, silicone-modified EPDM rubbers, silicone-modified acrylic rubbers, ethylene-acrylate rubbers, ethylene-vinyl acetate rubbers, urethane rubbers, polysulfide rubbers, chlorosulfonated polyethylene rubbers, chlorinated polyethylene rubbers, fluorinated rubbers, epichlorohydrin rubbers, and mixtures thereof. The preferred synthetic rubbers are ethylene-propylene rubbers (EPM) and ethylene-propylene-diene rubbers (EPDM). Commercially available EPM and EPDM rubbers may be used although those rubbers having an ethylene content of 40 to 70% by weight and a Mooney viscosity of 5 to 100 are especially preferred. The diene monomers which form the EPDM rubbers include ethylidene norbornene, dicyclopentadiene, and 1,4-hexadiene and their degree of unsaturation should preferably have an iodine value in the range of from 1 to 40. Preferably the synthetic rubber is not an organopolysiloxane rubber, in particular not a rubber of an organopolysiloxane having the average composition formula R n SiO 4-n 2 where R is a substituted or unsubstituted monovalent hydrocarbon group having 1 to 10 carbon atoms, up to 95 mol% of R being methyl groups, and n is a number from 1.95 to 2.05. The rubber composition (A) also includes electro-conductive carbon black. It may be selected from commonly used types of conductive carbon black, for example, acetylene black, conducting furnace black (CF), super conducting furnace black (SCF), extra conducting furnace black (XCF), conducting channel black (CC), and furnace black and channel black heat treated at elevated temperatures of about 1500°C. More particularly, the acetylene black includes Denka Acetylene Black manufactured by Denki Kagaku K.K., Shawinigan Acetylene Black manufactured by Shawinigan Chemical Co., the conducting furnace black includes Continex CF manufactured by Continental Carbon Co. and Vulcan C manufactured by Cabot Corp., the super conducting furnace black includes Continex SCF manufactured by Continental Carbon Co. and Vulcan SC manufactured by Cabot Corp., the extra conducting furnace black includes Asahi HS-500 manufactured by Asahi Carbon K.K. and Vulcan XC-72 manufactured by Cabot Corp., and the conducting channel black includes Corax L manufactured by Degussa Co. Also useful are modified furnace blacks commercially available as Ketjen Black EC and Ketjen Black EC-600JD from Ketjen Black International. The conductive carbon black may be used alone or in admixture of two or more types, preferably in an amount of from 1 to 50 parts, more preferably from 3 to 20 parts by weight per 100 parts by weight of the natural and/or synthetic rubber. Less than 1 part of carbon black usually fails to provide desired electric conduction whereas more than 50 parts of carbon black would sometimes result in a harder rubber composition which is rather poor in molding and yields cured products having low mechanical strength. The silicone rubber composition (B) includes an organopolysiloxane having average composition formula (1). R n SiO (4-n)/2 In formula (1), the groups R are selected independently to be a substituted or unsubstituted monovalent hydrocarbon group having 1 to 10 carbon atoms, preferably having 1 to 6 carbon atoms, for example, alkyl groups such as methyl, ethyl and propyl, cycloalkyl groups such as cyclopentyl and cyclohexyl, alkenyl groups such as vinyl and allyl, cycloalkenyl groups, aryl groups such as phenyl and tolyl, and halogenated or cyano hydrocarbon groups in which some of the hydrogen atoms of these groups are replaced by fluorine atoms, chlorine atoms, and organic groups such as chloromethyl, γ-trifluoropropyl, perfluoroalkyl and cyano groups. Letter n is a positive number of from 1.95 to 2.05. The preferred organopolysiloxanes are those having a backbone predominantly comprising dimethylpolysiloxane units in which phenyl, vinyl and other groups are additionally introduced. Preferably, methyl groups occupy 30 to 100 mol%, preferably 55 to 100 mol%, more preferably 80 to 100 mol% of the R groups while phenyl groups occupy 0 to 30 mol%, especially 0 to 15 mol% of the R groups and vinyl groups occupy 0 to 10 mol%, especially 0 to 5 mol% of the R groups. More preferably, the R groups contain more than 0.001 mol% of vinyl. The preferred organopolysiloxanes have a viscosity of 10,000 to 10,000,000 centistokes (cs), especially 100,000 to 10,000,000 cs at 25°C. Preferably, the rubber composition of the invention contains 5 to 95% by weight, more preferably 20 to 80% by weight of the organopolysiloxane. The rubber composition comprising natural and/or synthetic rubber, conductive carbon black, and an organopolysiloxane having average composition formula (1) as defined above according to the invention is obtainable by preparing a rubber composition (A) including natural and/or synthetic rubber and conductive carbon black, separately preparing a silicone rubber composition (B) including the organopolysiloxane of formula (1), and mixing these rubber compositions (A) and (B). Then the phase of carbon black previously dispersed in composition (A) is macroscopically dispersed in composition (B). The macroscopic dispersion used herein means a size of 0.1 to 100 µm and is effective in stabilizing volume resistivity. More particularly, rubber composition (A) including natural and/or synthetic rubber and conductive carbon black, and silicone rubber composition (B) including an organopolysiloxane of average composition formula (1) form an island structure in which two phases dimensioned 0.1 µm to 100 pm are macroscopically dispersed in one another. Since carbon black provides stronger interaction with natural and/or synthetic rubber, the carbon black added to natural and/or synthetic rubber does not migrate to the phase of silicone rubber composition (B). Therefore, carbon black is kept uniformly dispersed in the natural and/or synthetic rubber as composition (A), which phase is macroscopically dispersed and distributed with the phase of silicone rubber composition (B), leading to stable volume resistivity. In turn, if conductive carbon black were previously blended in a silicone rubber composition and this silicone rubber composition were blended with natural and/or synthetic rubber which is free of conductive carbon black, or if these three components were mixed at the same time, a microscopic dispersion of conductive carbon black would occur rather than the macroscopic dispersion of conductive carbon black, resulting in a rubber composition having unstable volume resistivity. The term microscopic dispersion corresponds to the size of the carbon black as blended. If conductive carbon black were added to a preblend of natural and/or synthetic rubber and silicone rubber, the carbon black would not undergo macroscopic dispersion, also resulting in unstable volume resistivity. In the practice of the present invention, rubber composition (A) is obtained by mixing natural and/or synthetic rubber with conductive carbon black. The mixing method is not particularly limited insofar as a uniform preblend is obtained. Mixing methods using conventional rubber compounding mills such as Banbury mixers, pressure kneaders, two-roll and three-roll mills are satisfactory. It is to be noted that composition (A) of natural and/or synthetic rubber may contain any desired additives, for example, processing oil for viscosity adjustment, antioxidants for heat resistance improvement, UV absorbers, carbon functional silane, flame retardants, and extending fillers such as clay. The silicone rubber composition (B) can consist solely of an organopolysiloxane of formula (1), but may contain any ingredients commonly blended in conventional silicone rubber compositions, for example, fillers such as wet silica, dry silica, and quartz powder, low viscosity hydroxyl-terminated silicone fluid, and carbon functional silane if desired. These ingredients are mixed to form silicone rubber composition (B) by any desired mixing method as described for composition (A). It will be appreciated that carbon black is not included in composition (B). It should be understood that silicone rubber composition (B) may be a commercially available one, for example, KE931u, KE951u, KE520 and KE555u manufactured from Shin-Etsu Chemical Corporation. Silicone rubber compositions (A) and (B) are preferably blended in a weight ratio of from 5:95 to 95:5, more preferably from 20:80 to 80:20 for providing a desired electric resistivity. Natural and/or synthetic rubber composition (A) and silicone rubber composition (B) may be blended by any desired mixing method using conventional rubber compounding mills such as Banbury mixers, pressure kneaders, two-roll and three-roll mills. For facilitating milling operation, quartz powder, wet or dry silica, process oil commonly added to synthetic rubbers, carbon functional silane, modified silicone fluid and other processing aids may be added, if desired. The rubber composition of the invention may be vulcanized and cured by conventional methods. The curing agent used herein need not have a limited curing mechanism insofar as it functions to vulcanize and cure the rubber composition by utilizing radical, addition, condensation or similar reactions commonly encountered in the vulcanization of conductive silicone rubbers. Any suitable one of conventional well-known curing agents may be used in an effective amount. Typical curing agents are peroxides, for example, alkyl peroxides such as di-t-butylperoxide and 2,5-dimethyl-2,5-di(t-butylperoxy)hexane, and aralkyl peroxides such as dicumyl peroxide and sulfur and sulfur compounds such as zinc dimethyldithiocarbamate, zinc diethyldithiocarbamate, and mercaptobenzothiazole. Also useful are addition reaction curing agents such as organohydrogenpolysiloxanes having at least two silicon-bonded hydrogen atoms in a molecule and platinum series catalysts and condensation curing agents such as polyfunctional alkoxysilanes or siloxanes and organometallic acid salts. The curing agent may be used in such an amount as commonly added to conventional conductive silicone rubbers. Examples of an alkoxysilane curing agent include The alkoxysilane curing agent is used in an amount of 2 to 50% by weight based on the weight of the organopolysiloxane. The rubber composition of the invention may be molded by conventional methods such as press molding, extrusion molding, injection molding, and calendering and then cured into articles which are ready for commercial use. For example, the rubber composition may be vulcanized by heating at a temperature of 150 to 180°C for 10 minutes. As has been described a rubber composition embodying the invention may afford rubber articles which exhibit a limited variation of electric resistivity in the semiconductive range and, in particular, may have a stable electric resistivity independent of molding conditions. Compositions may also be improved in moldability and vulcanization, and provide cured rubbers which have good rubbery elasticity and do not release conductive carbon black. Therefore, articles of cured rubber resulting from the rubber composition according to the invention may find a variety of applications e.g. in business machines as rubber roll members and in the electrochemical industry and vehicle industry, for example, as automobile parts. EXAMPLE Examples of the invention are given below by way of illustration and not by way of limitation. Unless otherwise stated, all parts are by weight. Examples 1-3 and Comparative Example 1 Polyolefin rubber composition 1A was obtained by blending the following ingredients in a pressure kneader. Silicone rubber composition 1B was obtained by blending the following ingredients in a pressure kneader. Ingredients Parts by weight Dimethylvinylpolysiloxane raw rubber consisting of 99.85 mol% of (CH₃)₂SiO units and 0.15 mol% of (CH₂=CH) (CH₃)SiO units and having a polymerization degree of 8,000 100 Silica powder (specific surface area 200 m²/g, Aerogel® 200, manufactured by Nihon Aerogel K.K.) 15 Hydroxyl-terminated dimethylsiloxane fluid having a polymerisation degree of 20 5 Compositions 1A and 1B were blended in the proportion shown in Table 1 using a roll mill. A rubber compound was prepared by adding dicumyl peroxide to the blend in the proportion shown in Table 1. The compound was shaped into sheets by heat pressing at 170°C and 100 kgf/cm² for 10 minutes, the sheets being 2 mm thick for the measurement of physical properties and 1 mm thick for the measurement of volume resistivity. For comparison purposes, a compound was prepared by adding 3.5 parts of Ketjen Black to 100 parts of silicone rubber composition 1B and measured for volume resistivity. The volume resistivity was measured on 10 sheets of 1 mm thick for each example using a resistivity meter Model HT-210 manufactured by Mitsubishi Oil & Fat K.K., with the range of minimum to maximum measurements being reported in Table 1. Examples 4-6 Polyolefin rubber composition 2A was obtained by blending the following ingredients in a two-roll mill. Silicone rubber composition 2B was a dimethylvinylpoly-siloxane raw rubber consisting of 99.5 mol% of (CH₃)₂SiO units and 0.5 mol% of (CH₂=CH)(CH₃)SiO units and having an average polymerization degree of 8,000. Compositions 2A and 2B were blended in the proportion shown in Table 2. A rubber compound was prepared by adding dicumyl peroxide and precipitating silica Nipsil ® LP having a specific surface area of 230 m²/g (manufactured by Nihon Silica K.K.) to the blend in the proportion shown in Table 2. The compound was shaped into sheets of 2 mm and 1 mm thick for the measurement of physical properties and volume resistivity as in Example 1. The results are shown in Table 2. Examples 7-9 and Comparative Example 2 Polyolefin composition 3A was obtained by blending the following ingredients in a pressure kneader. Silicone rubber composition 3B was obtained by blending the following ingredients in a kneader and heat treating the blend at 170°C for two hours. A compound was prepared by mixing compositions 3A and 3B, quartz powder Crystalite ® VXS (manufactured by Tatsumori K.K.), and 2,5-dimethyl-2,5-bis(t-butylperoxy)hexane )hexane in the proportion shown in Table 3, and then shaped into sheets of 2 mm and 1 mm thick for the measurement of physical properties and volume resistivity as in Example 1. For comparison purposes, a compound was prepared by adding 7.5 parts of Denka Acetylene Black and Crystalite ® VXS to 100 parts of silicone rubber composition 3B and measured for the same properties. The results are shown in Table 3. Examples 10-12 & Comparative Example 3 Silicone-acryl rubber composition 4A was obtained by blending the following ingredients in a pressure kneader. Silicone rubber composition 4B was obtained by blending the following ingredients in a pressure kneader. Ingredients Parts by weight Dimethylvinylpolysiloxane raw rubber consisting of 99.85 mol% of (CH₃)₂SiO units and 0.15 mol% of (CH₂=CH) (CH₃) SiO units and having a polymerization degree of 8,000 100 Silica powder (specific surface area 200 m²/g, Aerogel® 200, manufactured by Nihon Aerogel K.K.) 15 Hydroxyl-terminated dimethylsiloxane fluid having a polymerization degree of 20 5 Compositions 4A and 4B were blended in the proportion shown in Table 4 using a roll mill. A rubber compound was prepared by adding dicumyl peroxide to the blend in the proportion shown in Table 4. The compound was shaped into sheets by heat pressing at 170°C and 100 kgf/cm² for 10 minutes, the sheets being 2 mm thick for the measurement of physical properties and 1 mm thick for the measurement of volume resistivity. For comparison purposes, a compound was prepared by adding 3.5 parts of Ketjen Black to 100 parts of silicone rubber composition 4B and measured for volume resistivity. The volume resistivity was measured on 10 sheets of 1 mm thick for each example using a resistivity meter Model HT-210, with the range of minimum to maximum measurements being reported in Table 4. Examples 13-15 and Comparative Example 4 Butyl rubber composition 5A was obtained by blending the following ingredients in a pressure kneader. Silicone rubber composition 5B was obtained by blending the following ingredients in a kneader and heat treating the blend at 170°C for two hours. A compound was prepared by mixing compositions 5A and 5B, quartz powder Crystalite ® VXS (manufactured by Tatsumori K.K.), sulfur and a curing accelerator in the proportion shown in Table 5, and then shaped into sheets of 2 mm and 1 mm thick for the measurement of physical properties and volume resistivity as in the foregoing Examples. For comparison purposes, a compound was prepared by adding 7.5 parts of Denka Acetylene Black and 20 parts of Crystalite ® VXS to 100 parts of silicone rubber composition 5B, cured with dicumyl peroxide, and measured for the same properties. The results are shown in Table 5. As is evident from Tables 1 through 5, the vulcanized rubbers resulting from the rubber compositions embodying the invention had a relatively stable electric resistivity in the semiconductive range as compared with the conventional silicone rubbers filled with conductive carbon black. The variation of electric resistivity was of the order of only one figure for the compositions embodying the invention, which contrasts with the conventional carbon black filled silicone rubbers showing a variation of the order of 4 to 6 figures.

Claims: A rubber composition comprising in admixture a component (A) which is a rubber composition including 100 parts by weight of rubber selected from natural rubber, ethylene-propylene rubber, ethylenepropylene-diene rubber, styrene-butadiene rubber, hydrogenated acrylonitrile-butadiene rubber, acrylonitrile-butadiene rubber, butadiene rubber, isoprene rubber, chloroprene rubber, acrylic rubber, silicone-modified EPDM rubber, silicone-modified acrylic rubber, ethylene-acrylate rubber, ethylene-vinyl acetate rubber, urethane rubber, polysulphide rubber, chlorosulphonated polyethylene rubber, chlorinated polyethylene rubber, fluorinated rubber and epichlorohydrin rubber, component (A) also including 1 to 50 parts by weight of carbon black for conducting, and a component (B) which is a silicone rubber composition including an organopolysiloxane having the average composition formula (1): R n SiO (4-n)/2 where R is a substituted or unsubstituted monovalent hydrocarbon group having 1 to 10 carbon atoms, and n is a positive number of from 1.95 to 2.05, component (B) not including carbon black, the two components (A) and (B) being blended in a weight ratio of from 5:95 to 95:5, and the composition of (A) and (B) is curable into a product with a resistivity lying in the range 10³ to 10¹⁰ Ω.cm. A rubber composition as in claim 1 in which component (A) comprises a processing oil for viscosity adjustment, an anti-oxidant for heat resistance improvement, a UV absorber, a carbon functional silane a flame retardant, clay or an extending filler. A rubber composition as in claim 1 or claim 2 in which component (B) comprises wet silica filler, dry silica filler, quartz powder filler, a low viscosity hydroxyl-terminated silicone fluid, or a carbon functional silane. A rubber composition as in any previous claim in which the carbon black is selected from acetylene black, conducting furnace black (CF), super conducting furnace black (SCF), extra conducting furnace black (XCF), modified furnace black, conducting channel black (CC) and furnace black and channel black heat treated at elevated temperatures around 1500°C. A rubber composition as in any previous claim in which the carbon black is present in an amount of from 3 to 20 parts by weight per 100 parts by weight of the rubber of component (A). A rubber composition as in any previous claim in which the groups R are independently selected from: methyl, ethyl, propyl, cyclopentyl, cyclohexyl, vinyl, allyl, cycloalkenyl, phenyl, tolyl, halogenated or cyano hydrocarbon groups in which some of the hydrogen atoms are replaced by fluorine atoms or chlorine atoms, chloromethyl, γ-trifluoropropyl, perfluoroalkyl and cyano groups. A rubber composition as in any previous claim in which the groups R are chosen so that methyl groups occupy 30 to 100 mol%, phenyl groups occupy 0 to 30 mol% and vinyl groups occupy 0 to 10 mol% and so that the total mol% of all R groups is 100 mol%. A rubber composition as in any previous claim in which the groups R are chosen so that methyl groups occupy 80 to 100 mol%, phenyl groups occupy 0 to 15 mol% and vinyl groups occupy 0.001 to 5 mol% and so that the total mol% of all R groups is 100 mol%. A rubber composition as in any previous claim in which the organopolysiloxane has a viscosity of 10⁴ to 10⁷ centistokes at 25°C. A rubber composition as in any previous claim comprising 5 to 95% by weight of the organopolysiloxane. A rubber composition as in any previous claim in which the cured product of the composition of (A) and (B) has a resistivity not varying by more than one order of magnitude. A method for preparing a rubber composition comprising separately preparing: a component (A) which is a rubber composition including 100 parts by weight of rubber selected from natural rubber, ethylene-propylene rubber, ethylenepropylene-diene rubber, styrene-butadiene rubber, hydrogenated acrylonitrile-butadiene rubber, acrylonitrile-butadiene rubber, butadiene rubber, isoprene rubber, chloroprene rubber, acrylic rubber, silicone-modified EPDM rubber, silicone-modified acrylic rubber, ethylene-acrylate rubber, ethylene-vinyl acetate rubber, urethane rubber, polysulphide rubber, chlorosulphonated polyethylene rubber, chlorinated polyethylene rubber, fluorinated rubber and epichlorohydrin rubber, component (A) also including 1 to 50 parts by weight of carbon black for conducting, and a component (B) which is a silicone rubber composition including an organopolysiloxane having the average composition formula (1): R n SiO (4-n)/2 where R is a substituted or unsubstituted monovalent hydrocarbon group having 1 to 10 carbon atoms, and n is a positive number of from 1.95 to 2.05, component (B) not including carbon black, and mixing the two components (A) and (B) in a weight ratio of from 5:95 to 95:5, thereby obtaining a rubber composition which is curable into a product with a resistivity lying in the range 10³ to 10¹⁰ Ω.cm. A method as in claim 12 in which the components of component (A), the components of component (B), or both, are mixed independently of each other using any of Banbury mixers, pressure kneaders, two-roll mills or three-roll mills. A method as in claims 12 or 13 in which component (A) and component (B) are mixed together using any of Banbury mixers, pressure kneaders, two-roll mills or three-roll mills, with or without the addition of at least one of the following processing aids: quartz powder filler, wet or dry silica filler, process oil for use in synthetic rubbers, carbon functional silane, or modified silicone fluid. A method as in any of claims 12, 13 or 14 in which a curing agent comprises di-t-butylperoxide, 2,5-dimethyl-2,5-di(t-butylperoxy)hexane, dicumyl peroxide, sulphur, zinc dimethyl-dithiocarbamate, zinc diethyldithiocarbamate, mercaptobenzothiazole, an organohydrogenpolysiloxane having at least two silicon-bonded hydrogen atoms per molecule, platinum, a polyfunctional alkoxysilane or siloxane, or an organometallic acid salt, and in which when the curing agent used is one of the aforementioned alkoxysilanes, the alkoxysilane is added in an amount of 2 to 50% by weight based on the organopolysiloxane of component (B) of the rubber composition. A method as in any one of claims 12 to 15, further comprising curing the composition to give a cured product. A rubber article obtained by a method as in claim 16, or from a rubber composition as in any of claims 1 to 11, having a resistivity lying in the range 10³ to 10¹⁰ Ω.cm. A rubber article as in claim 17 created by a method comprising press moulding, extrusion moulding, injection moulding or calendering, or vulcanisation by heating at a temperature of from 150 to 180°C for ten minutes.

Inventors: NAKAMURA TSUTOMU, NUMATA KAZUO, TAKAHASHI MASAHARU, NAKAMURA, TSUTOMU, NUMATA, KAZUO, TAKAHASHI, MASAHARU
Applicants: SHINETSU CHEMICAL CO, SHIN-ETSU CHEMICAL CO., LTD.
Application year: 1990
Main classification: C08L83
IPC codes: H01B1, C08L83, C08L21