Photohardenable compositions and their use in producing images

Abstract: A photohardenable composition comprises an addition polymerizable or crosslinkable material, a photoinitiator composition capable of initiating polymerization or crosslinking of the polymerizable or crosslinkable material, and a compound of the formula Q represents -C=O or -C-OH, X represents S, O or N which is unsbustituted or substituted with alkyl or aryl groups, R₁ represents H, alkyl, aryl, alkoxy, benzoyl, arloxy, acyl or monosubstituted amino groups. R₂ represents H, alkyl or aryl groups. The composition is preferably contained in microcapsules and is used in photosensitive imaging systems. The five member aromatic group containing the imine moiety functions to reduce the likelihood of short time scale reciprocity failure of the composition and to enable imaging using high intensity radiation sources. An imaging method using the composition is also disclosed.

Description: The present invention relates to photohardenable compositions which may be used for producing images. Photosensitive imaging systems employing microencapsulated radiation sensitive compositions are the subject of our U.S. Patent Nos. 4,399,209, 4,416,966, 4,772,530 and 4,772,541. These patents describe imaging systems in which an imaging sheet including a layer of microcapsules containing a photosensitive composition in the internal phase is image-wise exposed to actinic radiation. In the most typical embodiments, the photosensitive composition is a photopolymerizable composition including a polyethylenically unsaturated compound and a photoinitiator and is encapsulated with a colour precursor. Image-wise exposure hardens the internal phase of the microcapsules as a result of the photoinitiator generating free radicals which initiate polymerization of the polyethylenically unsaturated compound by free radical addition polymerization. Following exposure, the imaging sheet is subjected to a uniform rupturing force by passing the sheet between a pair of pressure rollers. U.S. Patent No. 4,399,209 discloses a transfer system in which the imaging sheet is assembled with a developer sheet prior to being subjected to the rupturing force. Upon passing through the pressure rollers in contact with the developer sheet, the microcapsules rupture and image-wise release the internal phase whereupon the color-former migrates to the developer sheet where it reacts with a dry developer and forms a color image. The imaging system can be designed to reproduce monochromatic or polychromatic full color images. U.S. Patent No. 4,440,846 discloses a so called "self-contained" imaging system wherein both the image-forming agent and the developer material are located on the same substrate. In the system according to U.S. Patent No. 4,440,846, the image-forming agent is encapsulated in a layer of pressure rupturable capsules, and the capsules are exposed and ruptured to cause the image-forming agent to contact and react with the developer to produce an image on the substrate. A phenomenon known as reversal which has caused some photosensitive compositions to experience short time scale reciprocity failure has limited the use of imaging systems containing these compositions to lower intensity radiation sources for longer periods of time. Certain high intensity light sources, such as lasers, useful in high speed copying have not been used effectively because the photohardenable compositions do not polymerize in direct proportionality to the amount of exposure intensity. At time scales less than 0.1 seconds, two types of reciprocity failure have been observed to occur with various types of photosensitive material. Failure of the first type occurs around .001 seconds for most systems and results in a progressive loss of sensitivity down to about 1 microsecond. The total loss at 1 microsecond, compared to 1 second, is expected to be about a factor of 10 for most systems. Whether further losses below the microsecond level occur by this type of failure is not known. The mechanistic cause of the failure is believed to be a chemical inefficiency due to high concentrations of free radicals. The radicals react with each other rather than doing the chemistry expected of them. The second type of failure at short time scales is found in a few types of photosensitive materials. When this type of failure occurs, it is quite severe, causing an instant loss of a factor of 10 in sensitivity. This catastrophic loss has been observed to occur in different systems ranging from seconds to microseconds regions. The present invention arises from our work seeking to reduce the risk of reversal caused by this type of reciprocity failure. Most scientists who deal with photographic materials are familiar with the "H & D" (D log H) curve. The H & D curve characterizes the way in which a photographic material responds to light. An H & D curve is shown in Figure 1. If the system is "well behaved", there is a relationship between energy or exposure and image density which defines the energy requirements of an exposure device. This region is represented by A on Figure 1. In other areas, as is represented by B on Figure 1, the imaging system is not well behaved and results in a reverse proportionality between increased exposure and density. The region represented by B is the "reversal region" and depicts the second type of failure referred to above (i.e., short time scale reciprocity failure). In well behaved regions of an H & D curve, for a given photosensitive material the degree of polymerization is essentially a function of exposure. Exposure may be quantitatively expressed as a product of the intensity of the radiation source and the time of exposure. Accordingly, these two variables can be appropriately manipulated to provide a given exposure. In theory, as long as the desired exposure is obtained by any manipulation of intensity and time, a predetermined amount of polymerization should occur. In regions where short time scale reciprocity failure occurs, the rate of polymerization slows to a point at which the photohardenable composition never fully polymerizes. A given level of exposure does not produce a corresponding degree of polymerization. When the photohardenable composition is microencapsulated and used in the aforementioned imaging systems, the system is unable to reach Dmin in the reversal region. The reversal phenomenon varies widely amongst systems containing photosensitive materials. For some systems, reversal can occur only when subjecting the photosensitive composition to intensities and exposure times which cannot practically be achieved using present technology. For these systems short time scale reciprocity failure does not pose a serious problem. For other systems, short time scale reciprocity failure can pose a problem which must be overcome to enable the production of images. The problems are particularly apparent in systems which are subjected to high intensity radiation. While not wishing to be bound by any particular theory, we believe that short time scale reciprocity failure is in large part a function of the monomer used and the type and concentration of the photoinitiator. In systems where noticeable short time scale reciprocity failure occurs, we hypothesize that termination reactions occur at a faster rate than the propagation reactions as a result of either the photoinitiator being depleted in the microcapsules before the monomer has had an opportunity to polymerize, or by the creation of a polymerization inhibitor or a radical scavenger in the microcapsules. Moreover, once the photosensitive material has encountered failure as a result of "reversal", the reversal effect cannot be corrected. For some photosensitive materials, it has heretofore been difficult, if not impossible, to develop a system utilizing high intensity short time scale exposures because of the risk of reversal. When utilizing photopolymerizable systems as described above for copying documents, it is desirable to minimize the time of exposure to enable the production of copies at a fast rate. In systems which exhibit noticeable short time scale reciprocity failure, lower intensity radiation sources, and accordingly, longer exposure times are required to produce images. Accordingly, the number of copies produced per minute in such systems have been limited. In addition, it has long been desired to utilize high intensity sources such as lasers as light sources for photosensitive imaging systems because of their monochromatic spectral characteristics and their ability to be easily controlled, such as by computer control as is known in the art. The use of lasers has been limited in some photosensitive systems as the high intensities of the lasers have caused some photosenitive materials to exhibit short time scale failure due to the reversal phenomenon. Attempts have been made in the art to remedy the susceptibility of a photosensitive composition to reversal upon exposure. For example, in our European Patent Application No. 89310418.2 (Serial No. ), we describe how the likelihood of short time scale reciprocity failure may be reduced by the addition of a high viscosity material to the photohardenable composition. Examples of the viscosity additives are reactive monomers such as dipentaerythritol hydroxypentaacrylate, or non-reactive materials such as waxes. Although these materials do function to reduce the risk of reversal to some extent, they suffer from a minor number of drawbacks. First, the amount of high viscosity additive must be limited in order to enable manufacture of the photohardenable composition. The limitation of the amount of additive present in the photohardenable composition functions to lower, but not completely remove the risk of reversal. In addition, the photohardenable composition containing the viscosity modifier is limited in performance at high temperatures, typically above 30 to 35°C. Finally, the viscosity additive composition tends to lose film speed in the toe portion of the H & D curve over extended periods of time, thereby reducing the quality of image produced by a composition which has been stored for extended periods of time. U.S. Patent No. 4,290,870, assigned to Fuji Photo discloses a photopolymerizable composition. The composition includes an addition-polymerizable ethylenically unsaturated compound and a photoinitiator which includes the combination of a 5-isoxazolone and another co-initiator material. Prior to the present invention, there existed a need in the art for a photohardenable composition which is less susceptible to reversal, which is able to produce high contrast images, which is functional over a broad temperature band, and which has an extended shelf life. The term "reversal time" refers to the exposure time for a given exposure (E) (where E equals intensity (I) X Time (t)) below which the photosensitive material is unable to reach Dmin. At exposure time greater than the reversal time for a given exposure (I X t), Dmin is reached, i.e., the photosensitive material obeys reciprocity and does not exhibit reversal (we assume in this discussion that exposure times do not become so great that mechanistic phenomenon known as long time scale reciprocity failure occurs. See Arney, "Oxidation Kinetics and Reciprocity Behavior in the Microencapsulated Acrylate Imaging Process," J. Imaging Science 31:27-30 (1987)). Increases in intensity for exposure time periods less than the reversal time produces proportional increases in image density. In accordance with a first aspect of the present invention, there is provided a photohardenable composition comprising an addition polymerizable or crosslinkable material, and a photoinitiator composition capable of initiating polymerization or crosslinking of said polymerizable or crosslinkable material, said composition being characterised in further comprising a compound selected from 3-methyl-1-phenyl-2-pyrazoline, picrolonic acid, l-(2,4,6-trichlorophenyl)-3-(p-nitroanilino)-2-pyrazoline-5-one, 1,5-dimethyl-2-phenyl-3-pyrazolone, 4-aminoantipyrine and a compound of the formula wherein Q represents >C=O or >C-OH; X represents S or N which is unsubstituted or substituted with alkyl or aryl groups; R 1 represents H, alkyl, aryl, alkoxy, benzoyl, aryloxy, acyl or monosubstituted amino groups; and R 2 represents H, alkyl or aryl groups. Photosensitive material according to the invention comprises a support with a layer of the photohardenable composition, preferably microencapsulated, coated on the surface thereof. We describe below embodiments of photohardenable composition resistant to catastrophic short time scale reciprocity failure. The compositions have as an additive a five member aromatic group containing an imine moiety to shorten the reversal time of the composition and thereby enable the use of high intensity, short time exposures. While not completely understood, the presence of the aromatic additive appears to alter the chemical properties of the internal phase to reduce the reversal time of the composition. We express the tendency for a composition to undergo reversal in terms of its reversal time. Assuming that the exposure required for polymerization is a given value, and that the intensity of the radiation source is constant, the exposure time of the photosensitive composition to the radiation source may be easily determined by dividing the exposure by the intensity of the radiation source. If the exposure time is greater than the reversal time, the photosensitive composition obeys reciprocity and does not reverse. If the exposure time is less than the reversal time, the photosensitive composition is subject to the reversal phenomenon and does not obey reciprocity. In our described compositions, reversal time is shortened thus enabling higher intensity, short time scale radiation sources such as commercially available lasers to be utilised. If the photosensitive composition is utilised to produce copies, more copies per minute can be produced. In effect, we have discovered that the reversal time for a material can be shortened by adding a five member aromatic group containing an imine moiety to the material. The invention provides in a second and alternative aspect thereof a method for producing images comprising the steps of providing a substrate having front and back surfaces, said substrate having a coating comprising photosensitive microcapsules located on either of said front or back surfaces, said microcapsules having an internal phase containing a photohardenable composition comprising an addition polymerizable or crosslinkable material and having an image forming agent associated therewith, and a photoinitiator composition capable of initiating polymerization or crosslinking of said polymerizable or crosslinkable material; image-wise exposing said substrate to actinic radiation; and subjecting said microcapsules to a uniform rupturing force to cause said image-forming agent to form an image; characterised in that said internal phase further comprises a compound selected from 3-methyl-l-phenyl-2-pyrazoline, picrolonic acid, 1-(2,4,6-trichlorophenyl)-3-(p-nitroanilino)-2-pyrazoline-5-one, 1,5-dimethyl-2-phenyl-3-pyrazolone, 4-aminoantipyrine and a compound of the formula wherein Q represents >C=O or >C-OH; X represents S or N which is unsubstituted or substituted with alkyl or aryl groups, R 1 represents H, alkyl, aryl, alkoxy, benzoyl, aryloxy, acyl or monosubstituted amino groups and R 2 represents H, alkyl or aryl groups; and in that said exposure step is performed for a period of time longer than the reversal time of said composition. The relationship between the presence of the aromatic additive in the internal phase and the reversal time is explained in the following hypothetical example. If the theoretical exposure required for polymerization of a material is 2000 erg/cm 2 and the radiation source selected delivers energy at an intensity of 1000 erg/sec. cm 2 , the source must be activated for 2 seconds to effectuate polymerization. If the reversal time for the hypothetical material is 4 seconds, the reversal phenomenon will set in as the reversal time is greater than the exposure time and the composition will either not polymerize or will polymerize at a much slower rate than expected. A five member aromatic group containing an imine moiety is added to the internal phase to shorten the reversal time. If the above hypothetical resulting composition has a reversal time of one second, when using the same radiation source, the modified material can polymerize. It is not completely understood why the aromatic additive shortens the reversal time; nonetheless, the presence of the aromatic additive clearly reduces the risk of the composition from exhibiting short time scale failure. If the image-forming agent is a colourless colour-forming agent which requires the presence of a developer material to form an image, the receiver sheet is provided with such a developer material. The receiver sheet may be located remote from the microcapsules to form a transfer system or may contain the microcapsules to form a self-contained system. As will be seen from the detailed description below of preferred embodiments, the teachings of the present invention enable us to provide embodiments of photosensitive composition having a relatively shortened reversal time; to provide embodiments of photosensitive composition capable of producing relatively high contrast images; to provide embodiments of photocopy system which are capable of producing photocopies at relatively increased rates; and to produce images by methods wherein high intensity radiation sources, such as lasers may be utilised. In the accompanying drawings: Figure 1 depicts an H & D curve of a photosensitive composition which exhibits short time scale reciprocity failure; and Figures 2A and 2B are H & D curves developed from the experiments of Comparative Example 1 and Example 1. The present invention comprises a photohardenable composition, preferably in the form of microcapsules. The microcapsules include a photoinitiator in the internal phase. Photohardenable compositions such as photopolymerizable and photocrosslinkable materials increase in viscosity or solidify upon exposure to radiation. Also included in the photohardenable composition is a five member aromatic additive containing an imine moiety which functions to shorten the reversal time of the microcapsules. In association with the microcapsules there is preferably an image-forming agent. Various radiation curable materials, photoinitiators, aromatic additives, and image-forming agents can be used. Ethylenically unsaturated organic compounds are useful radiation curable materials. These compounds contain at least one terminal ethylene group per molecule. Typically, they are liquid. Polyethylenically unsaturated compounds having two or more terminal ethylene groups per molecule are preferred. An example of this preferred subgroup is ethylenically unsaturated acid esters of polyhydric alcohols, such as trimethylol propane triacrylate (TMPTA) and dipentaerythritol hydroxypentaacrylate (DPHPA). Another suitable radiation sensitive composition is an acrylate prepolymer derived from the partial reaction of pentaerythritol with acrylic acid or acrylic acid esters. Photosensitive compositions based on these prepolymers having an acrylate functionality of between approximately two and three are available commercially in two-package systems from the Richardson Company, Melrose Park, Ill., such as RL-1482 and RL-1483. These are recommended to be mixed together to form a radiation curable clear varnish in a ratio of 4.4 parts of RL-1482 to one part RL-1483. Another group of substances useful as radiation sensitive compositions include isocyanate modified acrylic, methacrylic and itaconic acid esters of polyhydric alcohols as disclosed in U.S. Pat. Nos. 3,783,151; 3,759,809 and 3,825,479, all to Carlick et al. Radiation curable compositions including these isocyanate modified esters and reactive diluents such as tetraethylene glycol diacrylate as well as photoinitiators such as chlorinated resins, chlorinated paraffins and amine photoinitiation synergists are commercially available as over print varnishes from Sun Chemical Corp., Carlstat, N.J., under the tradename of Sun Cure resins. The radiation sensitive component of several radiation curable inks is also a suitable candidate material for use in practice of this invention. An example of this type of material is a mixture of pentaerythritol acrylate and a halogenated aromatic, alicyclic or aliphatic photoinitiator, as disclosed in U.S. Pat. No. 3,661,614 to Bessemir et al. The photoinitiator is capable of absorbing actinic radiation and producing free radicals capable of initiating free radical polymerization of the polymerizable or crosslinkable compound. A preferred photoinitiator system includes ionic dye-reactive counter ion compounds described in U.S. Patent Nos. 4,772,530 and 4,772,541. A preferred class of ionic dye-counter ions is cationic dye borates and still more particularly cyanine dye borates. Typically the borate is a triphenylalkyl borate such as a triphenylbutyl borate. Other dye complexes such as Rose Bengal iodonium and Rose Bengal pyryllium complexes may also be used. Examples of other photoinitiators potentially useful in practice of the present invention may be selected from among diaryl ketone derivatives, quinones, benzoin alkyl ethers, alkoxy phenyl ketones, O-acylated oximinoketones, polycyclic quinones, phenanthrenequinone, naphthoquinone, diisopropylphenanthrenequinone, benzophenones and substituted benzophenones, xanthones, thioxanthones, halogenated compounds such as chlorosulfonyl and chloromethyl polynuclear aromatic compounds, chlorosulfonyl and chloromethyl heterocyclic compounds, chlorosulfonyl and chloromethyl benzophenones and fluorenones and haloalkanes, and hexaarylbiimidazoles (lophine dimers). In many cases it is advantageous to use a combination of imaging photoinitiators. The five member aromatic reversal control additive is preferably a compound selected from 3-methyl-1-phenyl-2-pyrazoline, picrolonic acid, 1-(2,4,6-trichlorophenyl)-3-(p-nitroanilino)-2-pyrazoline-5-one, 1,5-dimethyl-2-phenyl-3-pyrazolone, 4-aminoantipyrine and a compound of the formula (I) wherein Q represents >C=O or >C-OH; X represents S or N which is unsubstituted or substituted with alkyl or aryl groups; R 1 represents H, alkyl, aryl, alkoxy, benzoyl, arloxy, acyl or monosubstituted amino groups; and R 2 represents H, alkyl or aryl groups. Further, when the photoinitator comprises an ionic dye-reactive counter ion compound, X may also represent an oxygen atom. Examples of such compounds according to formula (I) are set forth in U.S. Patent No. 4,609,620 which describes certain pyrazolones for use as colour coupling agents for silver halide photographic systems. Other pyrazolones which are useful as colour couplers may also be useful in practice of the present invention. Preferred compounds of formula (I) are pyrazolone compounds. Examples of preferred compounds include 4-benzoyl-3-methyl-1-phenyl-2-pyrazoline-5-one, 3-methyl-1-phenyl-2-pyrazoline, picrolonic acid, 1-(2,4,6-trichlorophenyl)-3-(p-nitroanilino)-2-pyrazoline-5-one, 1,5-dimethyl-2-phenyl-3-pyrazolone, 4-aminoantipyrine and 3-methyl-1-phenyl-2-pyrazoline-5-one. Of the above listed compounds, 4-benzoyl-3-methyl-1-phenyl-2-pyrazoline-5-one (BMPP) has proven to be a particularly effective additive. The amount of additive of Formula (I) preferably should range from about 0.01 to about 1.1 parts per 100 parts of photohardenable composition. To improve the film speed of the photohardenable composition it may be advantageous to include an autoxidizer and/or other additive materials in the photohardenable composition. An autoxidizer is a compound which is capable of consuming oxygen in a free radical chain process. Examples of useful autoxidizers are N,N-dialkylanilines. Particularly preferred N,N-dialkylanilines are substituted with an alkyl group in the ortho -position and include 2,6-diisopropyl-N,N-dimethylaniline, 2,6-diethyl-N,N-dimethylaniline, N,N,2,4,6-pentamethylaniline and p-t-butyl-N,N-dimethylaniline. It may also be desirable to utilize an additional material to improve the photosensitive properties of the photohardenable composition such as film speed. Examples of these compounds include thiols such as acylthiohydroxamates, 2-mercapto-benzothiazole, 6-ethoxy-2-mercaptobenzothiazole, 2-mercaptobenzoxazole, phenylmercaptotetrazole, and heptylmercaptotriazole. Disulfides of the above listed thiol compounds are also useful additives. The autoxidizers and/or additive compounds are preferably used in concentrations of about 0.1 to 10 percent by weight of the photohardenable composition. Various image-forming agents can be used in association with the photohardenable composition. For example, images can be formed by the interaction of color formers and color developers of the type conventionally used in the carbonless paper art. In addition, images can be formed by the color producing interaction of a chelating agent and a metal salt or by the reaction of certain oxidation-reduction reaction pairs, many of which have been investigated for use in pressure-sensitive carbonless papers. Alternatively, an oil soluble dye can be used and images can be formed by transfer to plain or treated paper. The internal phase itself can also have its own image-forming capability. For example, it is known that many of the toners used in xerographic recording processes selectively adhere to the image areas of an imaging sheet exposed and developed as described herein below. As explained in U.S. Patent 4,399,209, the image-forming agent can be provided inside the microcapsules, in the microcapsule wall, or outside the microcapsules in the same layer as the microcapsules or in a different layer. In the latter cases, the internal phase picks up the image-forming agent (e.g., by dissolution) upon being released from the microcapsules and carries it to the developer layer or an associated image-receiving sheet. Typical color precursors useful in the aforesaid embodiments include colorless electron donating type compounds. Representative examples of such color formers include substantially colorless compounds having in their partial skeleton a lactone, a lactam, a sulfone, a spiropyran, an ester or an amido structure such as triarylmethane compounds, bisphenylmethane compounds, xanthene compounds, fluorans, thiazine compounds and spiropyran compounds. Crystal Violet Lactone, and Copikem X, IV and XI (products of Hilton-Davis Chemical Co.) and Reakt Yellow (a product of BASF) may be used alone or in combination as colour precursors in practice of the present invention, as may be commercially available cyan, magenta and yellow colour forming agents. The discrete walled microcapsules used to encapsulate the internal phase in preferred practice of the present invention can be produced using known encapsulation techniques including coacervation, interfacial polymerization, polymerization of one or more monomers in an oil, etc. Representative examples of suitable wall-formers are gelatin materials (see U.S. Patent Nos. 2,730,456 and 2,800,457 to Green et al.) including gum arabic, polyvinyl alcohol, carboxy-methyl-cellulose; resorcinol-formaldehyde wall formers (see U.S. Patent No. 3,755,190 to Hart et al.); isocyanate wall-formers (see U.S. Patent No. 3,914,511 to Vassiliades); isocyanate-polyol wall-formers (see U.S. Patent No. 3,796,669 to Kiritani et al.); urea-formaldehyde wall-formers, particularly urea-resorcinol-formaldehyde in which oleophilicity is enhanced by the addition of resorcinol (see U.S. Patent Nos. 4,001,140; 4,087,376 and 4,089,802 to Foris et al.); and melamine-formaldehyde resin and hydroxypropyl cellulose (see U.S. Patent No. 4,025,455 Shackle, assigned to The Mead Corporation). A melamine-formaldehyde capsule is particularly preferred as described in our European Patent Application No. 88311479.5 (Publication No. 0319337). The mean microcapsule size used in our compositions generally ranges from about 1 to 25 microns. To produce an imaging sheet containing the microcapsules, the microcapsules are coated onto a substrate. The most common substrate for imaging sheets using our compositions is a transparent film or paper. The paper may be a commercial impact raw stock, or special grade paper such as cast-coated paper or chrome-rolled paper. The latter two papers are preferred when using microcapsules having a diameter between approximately 1 and 5 microns because the surface of these papers is smoother and therefore the microcapsules are not as easily embedded in the stock fibers. Transparent substrates such as polyethylene terephthalate and translucent substrates can also be used. Another preferred substrate for the microcapsules is aluminized Mylar (PET). The microcapsules can be located on either the top or bottom surface of a transparent substrate to form an imaging sheet. To produce a positive image, the substrate is image-wise exposed to actinic radiation, preferably wavelengths in either the ultraviolet, visible or infrared range. Moreover, the intensity of the radiation source must be such that the photosensitive composition does not undergo reversal (i.e., the source must be selected so that the exposure time required for polymerization exceeds the reversal time). As the composition possesses a shorter reversal time, higner intensity sources can be used. Conversely, because the compositions have shorter reversal times, they can be exposed for shorter periods of time (with higher intensity sources) without reversing. A typical exposure intensity exceeds 2 x 10 -4 J/cm 2 (2000 ergs/cm 2 and may range from about 1 x 10 -4 J/cm 2 (1000 ergs/cm 2 ) to about 1 x 10 -2 J/cm 2 (100,000 ergs/cm 2 ). In the preferred arrangement high intensity light sources such as lasers and high wattage visible light sources (e.g. tungsten halogen sources) are used as the radiation source. Further, the exposure time typically ranges from microseconds to seconds. Moreover, because of the shorter exposure times required for exposure, more exposures, and hence, more copies can be produced per minute. If the reversal time is reduced to below a milliseconds time frame, commercially available lasers can be utilized as the light source. After the exposure step, the microcapsules on the substrate are subjected to a uniform rupturing force to release their contents and form a positive image. Where the image-forming agent is not a dye or pigment, a developer material is selected to react with the image-forming agent to form an image. Illustrative examples of color developers useful in conjunction with the embodiment employing the aforesaid color precursors are clay minerals such as acid clay, active clay and attapulgite; organic acids such as tannic acid, gallic acid and propyl gallate; acid polymers such as phenol-formaldehyde resins, phenol acetylene condensation resins and condensates between an organic carboxylic acid having at least one hydroxy group and formaldehyde; metal salts or aromatic carboxylic acids such as zinc salicylate, tin salicylate, zinc 2-hydroxynaphthoate, zinc 3,5-di-tert-butyl salicylate, oil soluble metal salts or phenol-formaldehyde novolak resins (e.g., see U.S. Patent Nos. 3,672,935; 3,732,120 and 3,737,410) such as zinc modified oil soluble phenol-formaldehyde resin as disclosed in U.S. Patent No. 3,732,120 zinc carbonate and mixtures thereof. A preferred class of glossable developers is described in our European Patent Application No. 87307985.9 (Publication No. 0260129). The developer material may be located on a support separate from the imaging sheet to thereby form a transfer image coating system as described in U.S. Patent 4,399,209. In such a system the imaging sheet and the developer sheet are brought together in the presence of a uniform rupturing force to cause the image-forming agent to migrate to the developer sheet and form an image on the developer sheet. The support may be made of paper, or a transparent film such as polyethylene terephthalate. Alternatively, the developer material may be located on the same surface as the layer of microcapsules to form a self-contained sheet as described in U.S. Patent 4,440,846. In this configuration, the substrate is coated with a first coating of developer material and then a second coating of the photosensitive microcapsules. Alternatively, the microcapsules and developer material can be admixed and coated as a single layer as is readily understood in the art. By performing the above-described method, images are produced on the substrate. Moreover, as the images can be produced using higher intensity exposures for shorter periods of time, radiation sources such as commercially available lasers can be utilized. This is a clear advantage over prior art photohardenable materials which required lower intensity, longer exposures to produce images as higher intensity exposures would subject the prior art compounds to reversal. The present invention may be utilized to produce monochromatic or full color images. Full-color imaging systems are described in U.S. Patent No. 4,576,891, European Published Application No. 0223587 and U.K. Patent No. 2,113,860. These systems employ imaging sheets having three sets of microcapsules which respectively contain cyan, magenta and yellow color precursors. As explained in more detail in the above-listed references, each set of microcapsules is primarily sensitive in a different wavelength band such that the microcapsules can be individually exposed with minimum cross-talk. In panchromatic systems, the cyan, magenta, and yellow forming photosensitive microcapsules are respectively sensitive to red, green and blue light. In such a system, at least one of the three sets of microcapsules preferably contains a photohardenable composition including the reversal control additive. Further, for each set of microcapsules, the composition selected is sensitive to a different wavelength band. For color forming microcapsules which do not exhibit short time scale reciprocity failure under typical operating conditions, no reversal control additives need to be added to the respective internal phases. To produce full-color images, each set of microcapsules is image-wise exposed to actinic radiation. This requires exposures of three different wavelengths, each wavelength corresponding to the sensitivity of the photohardenable composition selected for the corresponding set of microcapsules. The three different wavelengths may be provided from one broad band radiation source or three independent monochromatic radiation sources. In a panchromatic system, it is envisioned that green, blue, and red lasers may be used for the exposures. These processes rely upon image process techniques which are well known in the art. It is further contemplated that a high intensity white light source containing at least three distinct bands of actinic radiation may be used for the short term exposures. Because of the presence of the reversal control additives, as discussed above, the materials are able to withstand high intensity, short term exposures without undergoing reversal (as long as the exposure time to effectuate radiation for a source of a given intensity exceeds the reversal time of the composition). After exposure, the substrate is brought into contact with a developer material, and the microcapsules are ruptured in the presence of the developer material to produce a full color image. The addition of the reversal control additive provides a number of benefits to the photohardenable composition other than the lowering of the composition's reversal time. As will be demonstrated in the examples, the addition of the reversal control additive improves the film speed of the photohardenable composition. This, in turn, causes the dynamic range of the photohardenable composition to be shorter, and thereby enables the production of highly contrasted images. As a result, the photosensitive behavior of the composition is nearly digital. Because the film speed of the composition is enhanced, more copies per minute may be produced. If, however, a more continuous tone image is desired, a short non-image-wise exposure, as is known in the art, may be performed prior to the high intensity short time image-wise exposure. Examples of this technique are described in greater detail in U.S. Patent No. 4,482,624. Further, the photohardenable composition shows a consistent photographic behavior over a relatively broad temperature band, typically ranging from about 15°C to about 70°C. This is desirable because, as the copying machines which use the photohardenable composition typically operate at ambient conditions, the photohardenable composition may then be exposed and developed without running a significant risk of contamination caused by high or low temperature ambient conditions. In addition, when maintained in relatively small amounts, the presence of the reversal control additive does not show an appreciable loss in photographic properties over an extended period of time. This is important as, to enable the photohardenable material to be a viable commercial product, it must maintain an adequately long shelf life. The invention is illustrated in more detail by the following non-limiting examples: Comparative Example 1 As a control, the following internal phase was encapsulated in melamine-formaldehyde microcapsules: Component Amount Trimethylolpropane triacrylate (TMPTA) 80 parts Dipentaerythritol hydroxypentaacrylate (DPHPA) 20 parts 1,1'-di-n-heptyl-3,3,3',3'-tetramethylindocarbocyanine triphenyl-n-butylborate (Example 1 Initiator) .3 parts 2.6-diisopropyl-N,N-dimethyl aniline (DIDMA) 6 parts Magenta color precursor 24 parts Desmodur N-100 Isocyanates (N-100) 6.6 parts To determine the photosensitive performance of the composition, the composition was first exposed to light through a step wedge at a distance of 1 1/2 inches (3.81 cm) using a 500 watt tungsten halogen source and brought into contact with a developer material. The H & D curves for the material at an exposure time of 500 milliseconds is shown in Fig. 2A. The experiment was repeated except that the composition was exposed to light from a 30 milliwatt green laser. The H & D curve for the material at an exposure time of 10 microseconds is Shown in Fig. 2B. Example 1 The experiments of Comparative Example 1 were repeated except that the following internal phase was encapsulated: Component Amount TMPTA 100 parts Example 1 Initiator .3 parts DIDMA 6 parts Magenta color precursor 24 parts N-100 6.6 parts 4-benzoyl-3-methyl-1-phenyl-2-pyrazoline-5-one (BMPP) 0.01 parts The H & D curves for the material at exposure times of 500 milliseconds and 10 microseconds are shown in Figs. 2A and 2B. The material obeyed reciprocity into the microseconds time domain. Similar results were obtained by using different amounts of BMPP ranging from between .004 and 1.1 parts per 100 parts TMPTA. Comparative Example 2 The following internal phase was encapsulated in melamine-formaldehyde microcapsules: Component Amount TMPTA 100 parts Example 1 Initiator .27 parts DIDMA 1.00 parts Magenta Color Precursor 19 parts N-100 6.7 parts The microcapsules were exposed to a 500 watt tungsten halogen light source at a distance of 1 1/2 inches (3.81cm) through a step wedge to evaluate reversal behavior. The reversal time and dynamic range are shown in Table 1. Comparative Example 3 The experiment of Comparative Example 2 was repeated with the exception that instead of using 100 parts of TMPTA, 80 parts of TMPTA and 20 parts of DPHPA were contained in the internal phase. The reversal time and dynamic range are shown in Table 1. Comparative Example 4 The experiment of Comparative Example 2 was repeated with the exception that .5 parts of 3-phenyl-5-isoxazolone (PIAZ) were added to the internal phase. The reversal time and dynamic range are shown in Table 1. Example 2 The experiment of Comparative Example 2 was repeated with the exception that .008 parts of BMPP were added to the internal phase. The reversal time and dynamic range are shown in Table 1. Sample Reversal Time t r (sec) Dynamic range @ t r Comparative Example 2 >2.00 15.0 Comparative Example 3 .96 14.0 Comparative Example 4 .48 9.0 Example 2 0.0001 4.5 Comparative Example 5 The composition of Comparative Example 2 was exposed to the light source of Comparative Example 2 for .5 seconds at temperatures ranging from 15°C to 70°C. The sensitivity change in both the shoulder and toe of the H & D curve (measured in stops) is set forth in Table 2. Comparative Example 6 The experiment of Comparative Example 5 was repeated using the Composition of Comparative Example 3. The results are shown in Table 2. Comparative Example 7 The experiment of Comparative Example 5 was repeated using the composition of Comparative Example 4. The results are shown in Table 2. Example 3 The experiment of Comparative Example 5 was repeated using the composition of Example 2. The results are shown in Table 2. Shoulder Sensitivity Change (f/stops) Toe Sensitivity Change (f/stops) Exposure Temp. (°C) Comp. Ex.5 Comp. Ex. 6 Comp. Ex. 7 Ex. 3 Comp. Ex. 5 Comp. Ex. 6 Comp. Ex. 7 Ex. 3 15 -0.33 -0.67 -0.67 -1.00 0.00 0.00 0.00 -1.33 22 -0.33 -0.33 -0.33 -0.67 -1.00 -1.00 -0.67 -0.67 30 0.00 0.00 0.00 0.00 -5.00 -5.00 -2.30 0.00 35 0.33 0.00 - - - - -5.00 - 37 - - - 0.33 - - - 0.33 40 0.33 0.33 0.00 - - - - - 45 - - - 0.33 - - - 0.33 50 -1.60 0.67 -1.00 - - - - - 60 -3.30 0.33 -2.00 - - - - - 70 -5.50 -1.67 -4.00 0.67 - - - 0.33 Comparative Example 8 The microcapsules of Comparative Example 2 were maintained at 60°C for 10 days and then exposed to a 150 watt tungsten halogen light source at a distance of 30 cm for 16 seconds. The loss in film speed, measured in steps, for the shoulder and toe, are shown in Table 3. Comparative Example 9 The experiment of Comparative Example 8 was repeated using the microcapsules of Comparative Example 3. The loss in film speed for the shoulder and toe are shown in Table 3. Example 4 The experiment of Comparative Example 8 was repeated, with the exception that 1.1 parts of BMPP were added to the internal phase of the microcapsules. The loss in film speed for the shoulder and toe are shown in Table 3. Example 5 The experiment of Comparative Example 8 was repeated using the microcapsules of Example 2. The loss in film speed for the shoulder and toe are shown in Table 3. Film Speed and Lose Over 10 Days Sample Shoulder (steps) Toe (steps) Comparative Example 8 0.00 -0.04 Comparative Example 9 -0.06 -0.53 Example 4 -0.46 -0.56 Example 5 -0.11 -0.13

Claims: A photohardenable composition comprising an addition polymerizable or crosslinkable material, and a photoinitiator composition capable of initiating polymerization or crosslinking of said polymerizable or crosslinkable material, said composition being characterised in further comprising a compound selected from 3-methyl-1-phenyl-2-pyrazoline, picrolonic acid, 1-(2,4,6-trichlorophenyl)-3-(p-nitroanilino)-2-pyrazoline-5-one, 1,5-dimethyl-2-phenyl-3-pyrazolone, 4-aminoantipyrine and a compound of the formula wherein Q represents >C=O or >C-OH; X represents S or N which is unsubstituted or substituted with alkyl or aryl groups; R 1 represents H, alkyl, aryl, alkoxy, benzoyl, aryloxy, acyl or monosubstituted amino groups; and R 2 represents H, alkyl or aryl groups. A composition according to Claim 1, further characterised in that said compound is selected from 4-benzoyl-3-methyl-1-phenyl-2-pyrazoline-5-one, 3-methyl-1-phenyl-2-pyrazoline, picrolonic acid, 1-(2,4,6-trichlorophenyl)-3-(p-nitroanilino)-2-pyrazoline-5-one, 1,5-dimethyl-2-phenyl-3-pyrazolone, 4-aminoantipyrine and 3-methyl-1-phenyl-2-pyrazoline-5-one. A composition according to Claims 1 or 2, wherein the polymerization or cross-linking of said polymerizable or crosslinkable material is initiated by free radical addition polymerization or cross-linking; said composition being further characterised in that said photoinitiator composition includes a compound which absorbs actinic radiation and directly or indirectly generates free radicals. A composition according to Claim 3, further characterised in that said polymerizable or cross-linkable material comprises an ethylenically unsaturated monomer. A composition according to Claims 1 or 2, further characterised in that said photoinitiator comprises an ionic dye-reactive counter ion complex. A composition according to Claim 5, further characterised in that said photoinitiator comprises a cationic dye-borate anion complex. A composition according to Claim 6, further characterised in that said cationic dye comprises a cyanine dye. A composition according to any of Claims 3 to 7, further characterised in that said photoinitiator includes an autoxidizer and/or film speed enhancing material. A composition according to any preceding claim, further characterised in being microencapsulated with an image-forming agent. Photosensitive material comprising a support having a layer of a photohardenable composition on the surface thereof, characterised in that said photohardenable composition comprises a composition according to any preceding claim. A method for producing images comprising the steps of providing a substrate having front and back surfaces, said substrate having a coating comprising photosensitive microcapsules located on either of said front or back surfaces, said microcapsules having an internal phase containing a photohardenable composition comprising an addition polymerizable or crosslinkable material and having an image forming agent associated therewith, and a photoinitiator composition capable of initiating polymerization or crosslinking of said polymerizable or crosslinkable material; image-wise exposing said substrate to actinic radiation; and subjecting said microcapsules to a uniform rupturing force to cause said image-forming agent to form an image; characterised in that said internal phase further comprises a compound selected from 3-methyl-l-phenyl-2-pyrazoline, picrolonic acid, 1-(2,4,6-trichlorophenyl)-3-(p-nitroanilino)-2-pyrazoline-5-one, 1,5-dimethyl-2-phenyl-3-pyrazolone, 4-aminoantipyrine and a compound of the formula wherein Q represents >C=O or >C-OH; X represents S or N which is unsubstituted or substituted with alkyl or aryl groups, R 1 represents H, alkyl, aryl, alkoxy, benzoyl, aryloxy, acyl or monosubstituted amino groups and R 2 represents H, alkyl or aryl groups; and in that said exposure step is performed for a period of time longer than the reversal time of said composition. A method according to Claim 11, further characterised in that said image-wise exposure step comprises exposing said microcapsules to radiation having an intensity between about 1 x 10 -4 J/cm 2 (1000 ergs/cm 2 ) and about 1 x 10 -2 J/cm 2 (100,000 ergs/cm 2 ). A method according to Claims 11 or 12, further characterised in that said image-wise exposure step comprises exposing said microcapsules to radiation emitted from one or more lasers. A method according to any of Claims 11, 12 or 13, further characterised in comprising the additional step of providing a developer material capable of reacting with said image-forming agent to form an image; and in that said step of subjecting said microcapsules to a uniform rupturing force comprises rupturing said microcapsules in the presence of said developer material. A method according to Claim 14, further characterised in being capable of producing full colour images, said coating comprising three sets of photosensitive microcapsules, each said set having a different image-forming agent associated therewith, and at least one said set comprising photosensitive microcapsules having a compound of formula (I) in their internal phase. A method according to Claim 15, further characterised in that said three sets of microcapsules comprise a first set of microcapsules containing a cyan colour-forming agent, a second set of microcapsules containing a magenta colour-forming agent and a third set of microcapsules containing a yellow colour-forming agent.

Inventors: HIPPS JESSE, PLAGEMAN CLAIRE MIRIAM, HIPPS, JESSE, PLAGEMAN, CLAIRE MIRIAM
Applicants: MEAD CORP, THE MEAD CORPORATION
Application year: 1990
Main classification: G03F7
IPC codes: G03F7, C08F2