Ceramic substrate used for fabricating electric or electronic circuit

Abstract: A ceramic substrate is used for an electric or electronic circuit comprises a ceramic plate (11) formed of a substance mainly composed of aluminum nitride, and conductive islands (12/13) formed of aluminum or an aluminum alloy and bonded to one surface of said ceramic plate for providing conductive paths to circuit components (16/17) connected thereto, wherein the alumi­ num or aluminum-alloy islands decrease the total weight of the ceramic substrate and enhance a resistance against repetition of a thermal stress.

Description: FIELD OF THE INVENTION This invention relates to a ceramic substrate used for an electric or electronic circuit and, more particularly, to a conductive island mounted on a ceramic plate. BACKGROUND OF THE INVENTION A typical example of the ceramic substrate is illustrated in Fig. 1 and comprises a ceramic plate 1 of aluminum oxide sandwiched between two copper plates 2 and 3, and a heat sink 4. The copper plates 2 and 3 are bonded to both surfaces of the ceramic plate 1 through a liquid phase bonding phenomenon. Namely, the bonding surfaces of the copper plates 2 and 3 are firstly oxidized, and the ceramic plate 1 is laminated with the copper plates 2 and 3 on both surfaces thereof. While the ceramic plate laminated with the copper plates 2 and 3 are heated at 1065 to 1085 degrees in centigrade, the copper and the copper oxide are melted, and the copper plates 2 and 3 are bonded to the ceramic plate 1 through a copper-and-copper oxide eutectic phenomenon. One of the copper plates 2 and 3 provides a conduction path between circuit components, and the other is soldered to the heat sink member 4 at lower than 450 degrees in centigrade. An electric or electronic circuit is expected to achieve a complex task and is, accordingly, fabricated with a large number of circuit components on a single ceramic substrate. The electric or electronic circuit tends to become heavy, but the manufacturer is requested to decrease the electric or electronic circuit in weight because of a handy sized electronic system. Then, the manufacturer looks for a light ceramic substrate, and a problem is encountered in the prior art ceramic substrate in the weight. Another problem inherent in the prior art ceramic substrate is a small resistance against repetition of a thermal stress. When the electric or electronic circuit is activated and achieves a task, a large amount of heat is produced in the circuit components, and the ceramic substrate propagates the heat for radiation. Since the copper plates 2 and 3 are different in thermal expansion co-efficient from the ceramic plate 1, the ceramic plate is subjected to thermal stress. Upon being inactivated, no heat takes place, and the ceramic plate is released from the thermal stress. Thus, a heat cycle takes place in the electric or electronic circuit, and, accordingly, the ceramic substrate is repeatedly subjected to the thermal stress. The thermal stress is causative of cracks in the ceramic plate 1, and the ceramic substrate is broken in the worst case. SUMMARY OF THE INVENTION It is therefore an important object of the present invention to provide a ceramic substrate which is decreased in weight. It is another important object of the present invention to provide a ceramic substrate which is large in resistance against the repetition of thermal stress. The inventors found that copper was larger in strength against a static load than some metals and alloys but smaller in fatigue limit against a repeated load than these metals and alloys. Namely, a margin of the strength to be left is rapidly decreased for copper rather than some metals and alloys as shown in Fig. 2. When the repeated load reaches a critical value for breaking the ceramic plate, the margin of some metals and alloys are large enough to support an electric component mounted thereon, but a relatively small amount of margin is merely left for copper. If a conductive island is formed of one of those metals and alloys smaller in specific weight than copper, the problems inherent in the prior art ceramic substrate are solved. To accomplish these objects, the present invention proposes to provide a ceramic susbtrate according to claim 1. In accordance with the present invention, there is provided a ceramic substrate used for an electric or electronic circuit comprising a) a ceramic plate formed of a substance mainly composed of aluminum nitride, and b) conductive island means bonded to one surface of the ceramic plate and formed of aluminum or an aluminum alloy, the conductive island means providing a conductive path for at least one circuit component connected thereto. BRIEF DESCRIPTION OF THE DRAWINGS The features and advantages of a ceramic substrate according to the present invention will be more clearly understood from the following description taken in conjunction with the accompanying drawings in which: Fig. 1 is a side view showing the structure of the prior art ceramic substrate; Fig. 2 is a graph showing strength of several metals and alloys in terms of a static load as well as a repeated load; Fig. 3 is a cross sectional view showing the structure of a ceramic substrate according to the present invention; Fig. 4 is a graph showing the deformation of ceramic substrate in terms of a ratio of thicknesses between each conductive metallic island and a metallic heat sink; Fig. 5 is a graph showing the number of heat cycles exerted on a ceramic substrate in terms of an aluminum content; and Fig. 6 is a cross sectional view showing the structure of another ceramic substrate according to the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS First Embodiment Referring first to Fig. 3 of the drawings, a ceramic substrate embodying the present invention comprises a ceramic plate 11, conductive metallic islands 12 and 13, and a metallic heat sink 14. The ceramic plate 11 contains about 95 % of aluminum nitride (AlN), about 5 % of yttrium oxide (Y203) and incidental impurities, and the conductive metallic islands 12 and 13 and the metallic heat sink 14 are bonded to both surfaces of the ceramic plate 11 with a solder-bonding alloy 15. The conductive metallic island 12 has a generally rectangular top surface, and the conductive metallic island 12 has a generally L-shaped top surface so as to extend at the back of the conductive metallic island 12. The heat conductivity of aluminum nitride ranges from 50 to 270 watt/(meter x degree in Kelvin) and is larger than that of aluminum oxide ranging between 15 to 20 watt/(meter x degree in Kelvin). The conductive metallic islands 12 and 13 are electrically isolated from each other and plated with copper or nickel. Circuit components 16 and 17 such as, for example, a discrete semiconductor device and a semiconductor integrated circuit device are respectively soldered to the copper or nickel films 12a and 13a, and the copper or nickel films 12a and 13a improve the adhesion between the circuit components 16 and 17 and the conductive metallic islands 12 and 13. In this instance, the copper or nickel films 12a and 13a cover the entire top surfaces of the conductive metallic islands 12 and 13; however, only the contact areas with the circuit components 12 and 13 may be plated with copper or nickel. Other conductive metal may be avairable in the plating. The conductive metallic islands 12 and 13 plated with the copper or nickel are formed of aluminum or an aluminum alloy selected from the group consisting of an aluminum nickel alloy and an aluminum-boron alloy. Aluminum and the aluminum alloy have large heat conductivities ranging from 150 to 250 watts/(meter x degree in Kelvin). The heat conductivity of aluminum and the aluminum alloy is slightly lower than that of copper (390 watts/(meter x degree in Kelvin)), but aluminum and the aluminum alloy is much smaller in specific weight than copper. The pattern of the conductive metallic islands 12 and 13 as well as the occupation area on the ceramic substrate 11 depend on an electric or electronic circuit, and various arrangements are made for practical ceramic substrates according to the present invention. The solder-bonding alloy 15 is of an aluminum alloy selected from the group consisting of an aluminum-silicon alloy, an aluminum-silicon-magnesium alloy, an aluminum-germanium alloy and an aluminum-silicon-germanium alloy and shaped in a foil or a cladding sheet together with each of the conductive metallic islands 12 and 13 or the heat sink 14. However, another solder-bonding alloy may be used in so far as the solder-bonding alloy gives a sufficiently large amount of adhesion thereto. Various specimens are produced in accordance with the present invention. The ceramic plates 11 are about 50 millimeters in width, about 75 millimeters in length and about 0.63 millimeter in thickness. The ceramic is composed of the Y 2 O 3 -5% AlN, but incidental impurities would be contained therein. The metallic heat sinks 14 are about 50 millimeters in width, about 75 millimeters in length and about 3 millimeters in thickness. The conductive metallic islands 12 and 13 and the metallic heat sinks 14 are formed of aluminum or an aluminum alloys. The compositions of the aluminum alloys are described in Table 1, where specimens 1, 6, 7, 9 and 10 are embodiments of the present invention. The metallic heat sinks 14 and the conductive metallic islands 12 and 13 are prepared through a rolling process, and several islands and heat sinks are simultaneously clad with the solder-bonding alloys 15. The solder-bonding alloys 15 thus clad are about 30 microns in thickness, and the solder-bonding alloys 15 in the form of foil are also prepared and used in the other specimens. The compositions of the solder-bonding alloys 15 are shown in Table 1. Each of the ceramic plates 11 is laminated with the associated heat sink 14 and the islands 12 and 13 at both surfaces thereof, and the foil-shaped solder-bonding alloy 15 intervenes between the ceramic plate 11 and either heat sink 14 or conductive metallic islands 12 and 13, if necessary. All of the ceramic plates 11 thus laminated with the associated component layers are heated in vacuum to a melting temperature oC the solder-bonding alloys ranging from 430 degrees to 610 degrees in centigrade and, then, maintained for about 10 minutes. Each of the ceramic plates 11 is bonded to the associated metallic heat sink 14 and the associated conductive metallic islands 12 and 13. The laminated structures thus bonded are further maintained at 350 degrees in centigrade for 30 minutes for heat treatment and, then, gradually cooled in the furnace. Finally, the islands 12 and 13 are plated with copper or nickel to a thickness of about 3 micron through an electroless plating process. Specimens 1 to 10 are, thus, fabricated in accordance with the present invention. For comparison, the prior art ceramic substrate is fabricated and shown in Table 1 with reference numeral "11". Namely, the ceramic plate 1 is formed of aluminum oxide (Al 2 O 3 ) with purity of 96 %, the dimensions thereof are 50 millimeters in width, 75 millimeters in length and 0.63 millimeter in thickness. On both surfaces of the ceramic plate 1 are placed oxygen free copper plates 2 and 3 each being 45 millimeters in width, 70 millimeters in length and 0.3 millimeter in thickness. The ceramic plate 1 sandwiched between the oxygen free copper plates 2 and 3 is placed in an oxidizing ambience consisting of 1%-oxygen and 99%-argon at 1075 degrees in centigrade for 50 minutes. The copper plates 2 and 3 are oxidized, and copper oxide (Cu 2 O) is produced on the surfaces thereof. Since the copper and the copper oxide form an eutectic mixture, the copper plates 2 and 3 are bonded to the ceramic plate 1. A foil-shaped Sn-60% Pb solder-bonding alloy 5 is placed between the copper plate 3 and the heat sink 4 which is 50 millimeters in width, 75 millimeters in length and 3 millimeters in thickness. The heat sink 4 is formed of oxygen free copper. The foil-shaped solder-bonding alloy 5 is heated to an appropriate high temperature, and the heat sink 4 is soldered to the copper plate 3. Composition Specimen Heat Sink (weight % ) Islands (weight %) Solder (weight %) Form 1 pure Al pure Al Si-13% Al alloy Foil 2 Mg-2.5%, Cr-0.2% Al alloy ditto ditto ditto 3 ditto ditto Si-7.5% Al alloy ditto 4 Mn-1% Al alloy Mn-1% Al alloy Ge-15% Al alloy ditto 5 ditto pure Al Si-9.5%, Mg-1% Al alloy Clad 6 pure Al ditto ditto ditto 7 ditto ditto Si-7.5%, Ge-10% Al alloy ditto 8 ditto Mn-1% Al alloy ditto ditto 9 Ni-0.02% Al alloy Ni-0.02% Al alloy Si-7.5% Al alloy Foil 10 B-0.005% Al alloy B-0.005% Al alloy ditto ditto 11 Cu Cu Cu-Cu 2 O The specimens 1 to 11 are heated to 125 degrees in centigrade and, then, cooled down to -55 degrees in centigrade. The temperature elevation followed by the cooling-down forms a heat cycle, and the heat cycle is repeated until cracks take place in the ceramic plates 1 or 11. The evaluation process is well known in the semiconductor manufacturer. In the evaluation, the heat cycle is repeated twenty times, and the ceramic plates 1 and 11 are observed if any crack takes place or not. If no crack takes place, the heat cycle is repeated twenty times again. The observation is summarized in Table 2. The heat conductivity of each of the specimens 1 to 11 is measured through a laser-flashing method, and a weight ratio with respect to the prior art ceramic substrate is calculated for each of the specimens 1 to 10. The heat conductivity and the weight ratio are shown in Table 2. In Table 2, "degrees in Kelvin" is abbreviated as "deg.in Kvn". Specimen The number of heat cycles Heat conductivity (W/meter x deg.in Kvn.) Weight ratio 1 200 without crack 159 0.354 2 ditto 132 0.353 3 ditto 135 0.353 4 ditto 140 0.353 5 ditto 150 0.352 6 ditto 158 0.352 7 ditto 146 0.352 8 ditto 139 0.352 9 ditto 157 0.354 10 ditto 157 0.354 11 20 with cracks 160 1 As will be understood from Table 1, the ceramic substrate according to the present invention is increased in resistance against repetition of heat cycle and decreased in weight. This is because of the fact that the ceramic substrate is fabricated with the combination the ceramic plate 11 of aluminum nitride and the conductive metallic islands 12 and 13 of aluminum or the aluminum alloy. In general, it is desirable to be large in thickness in view of the current propagation. However, the thick conductive metallic islands 12 and 13 are causative of large a stress exerted on the ceramic plate 11, because a large distance from the neutral surface allows a large moment to take place. Then, a thin conductive metallic islands 12 and 13 are desirable in view of the service time period. The ratio of the thickness t1 of each island to the thickness t2 of the ceramic plate 11 should be smaller than a critical value, and the sectional area of each island is compensated by either width or length. If a ceramic plate is sandwiched between conductive metallic islands and a metallic heat sink, a part of moment caused by the conductive metallic islands is canceled by a counter-moment caused by the metallic heat sink. This means that the thickness t1 of each island is well balanced with the thickness t3 of the heat sink at a certain point. If the thicknesses t1 and t3 are appropriately selected, the ceramic substrate provides a long serves time without deterioration of reliability. Fig. 4 shows the deformation of a ceramic substrate in terms of the ratio t1/t3. Although an experiment is carried out with the ceramic plates formed of the aluminum oxide, the same tendency takes place in an experiment using aluminum nitride plates. Triangular plots stand for ceramic substrates of 4-inches square, and bubbles represent ceramic substrates each being 30 millimeters in width and 70 millimeters in length. All of the ceramic substrates are 0.635 millimeter in thickness, and the both surfaces of each aluminum oxide plate is sandwiched between two aluminum plates. The heat cycle exerted on the ceramic substrates reiterates a loop between +125 degrees in centigrade for 30 minutes and -40 degrees in centigrade for 30 minutes. The application of the heat cycles warps the ceramic substrates due to the difference between the moment and the counter-moment opposite in direction thereto. The minimum deformation takes place at the ratio of t1/t3 = 1 as shown in Fig. 4, and the minimum deformation at t1/t3=1 well supports the existence of the balancing point, because moment is balanced with the counter moment. If the occupation area of the conductive metallic islands is decreased, the balancing point is moved from the ratio t1/t3 = 1, and the adjustment of the ratio to the balancing point prolongs the service time period. The aluminum content of the islands and the heat sink has an influence on the resistance against the repetition of heat cycle. Fig. 5 shows the number of heat cycles exerted on the ceramic substrate in terms of the aluminum content. Bubbles stand for the ceramic substrates without any annealing after the bonding between the ceramic plate and the aluminum plates, and dots represent the ceramic substrates fabricated through the bonding followed by an annealing at 400 degrees in centigrade for 6 hours. All of the ceramic substrates are shaped into a rectangular configuration of 1 inch by 1 inch, and the thickness is about 0.4 millimeter. If the manganese content is increased, the resistance is decreased, but the resistance is improved through the annealing. If an aluminum alloy is used for the islands 12 and 13 and the heat sink 14, an appropriate annealing should be carried out for healing the resistance against the repetition of heat cycle. Second Embodiment Turning to Fig. 6 of the drawings, another ceramic substrate according to the present invention comprises a ceramic plate 21 mainly composed of aluminum nitride and covered with an aluminum oxide film 21a, a surface film 22 covering the aluminum oxide film 21a, a conductive metallic island pattern 23, a metallic heat sink 24, and solder-bonding alloy blocks 25a and 25b bonding the conductive metallic island pattern 23 and the metallic heat sink 24 to both surfaces of the ceramic plate 21. In this instance, the ceramic plate 21 is formed of aluminum nitride containing one of more than one oxidizers; however, a pure aluminum nitride may be used for the ceramic plate 21. The oxidizers range from 0.1 % to 10 % by weight in this instance, and the aluminum oxide film 21a is 0.2 micron to 20 microns in thickness. Aluminum powder containing the oxidizers is sintered to produce the ceramic plate 21, and the oxidizer improves the density of the sintered product or the ceramic plate 21. The large density results in a large mechanical strength, and the ceramic substrate according to the present invention is less liable to be broken. The oxidizer or oxidizers further promote oxidation of the surface portion of the ceramic plate 21 so as to rapidly form the aluminum oxide film 21a. If the oxidizer or oxidizers are less than 0.1 % by weight, the improvement in density is hardly achieved, and no rapid oxidation takes place. However, the oxidizer or oxidizers more than 10 % by weight deteriorate the heat conductivity of the ceramic plate 21, and, for this reason, the content of the oxidizer or oxidizers ranges from 0.1 % to 10 % by weight. The aluminum oxide film 21a is formed through a surface oxidation of the ceramic plate 21, and the surface oxidation is carried out at 1100 degrees to 1500 degrees in centigrade in an oxidizing ambience where the oxygen partial pressure ranges from 10-2 to 1 atm and the water vapor pressure is less than 10-3 atm. The time period of the oxidation depends upon the thickness of the aluminum oxide film 21a. The advantage of the aluminum oxide film 21a will be described in connection with the surface film. However, if the aluminum oxide film 21a is less than 0.2 micron, the advantage hardly takes place, and an aluminum oxide film more than 20 microns deteriorates the heat conductivity of the ceramic plate 21. The conductive metallic island pattern 23 and the heat sink 24 are formed of aluminum or an aluminum alloy selected from the group consisting of an aluminum-nickel alloy, and aluminum boron alloy. The top surface of the conductive metallic island patter 23 is partially plated with copper or nickel so that circuit components (not shown) are easily soldered thereto. The solder-bonding alloy is selected from the group consisting of an aluminum-silicon alloy, an aluminum-silicon-magnesium alloy, an aluminum-silicon-germanium alloy and an aluminum germanium alloy. The solder-bonding alloy is shaped into a foil, or the conductive metallic island pattern 23 and the metallic heat sink 24 are clad with the solder-bonding alloy. The solder-bonding alloy blocks 25a and 25b are melted in an appropriate high temperature over its melting point, and, accordingly, the ceramic plate 21 covered with the surface film 22 is bonded to the conductive metallic island pattern 23 and the metallic heat sink 24. The surface film 22 is mainly composed of silicon oxide (SiO 2 ) or of the silicon oxide containing zirconium oxide or titanium oxide. The surface film 22 and the aluminum oxide film 21a improve the adhesion between the ceramic plate 21 and the conductive metallic island pattern and between the ceramic plate 21 and the metallic heat sink 24. This is because of the fact that both of the aluminum oxide and the solder-bonding alloy are well wet with the silicon oxide. The surface film 22 ranges from 0.01 micron to 10 microns in thickness. If the surface film 22 is less than 0.01 micron in thickness, the adhesion is hardly improved. The surface film 22 greater than 10 microns deteriorates the heat conductivity. Thus, the surface film 22 should be adjusted between 0.01 micron and 10 microns. The surface film 22 of the silicon oxide surely improves the adhesion; however, if the surface film 22 contains the zirconium oxide or the titanium oxide, the adhesion as well as the strength thereof are further improved, and, accordingly, the ceramic substrate is increased in the resistance against the repetition of the heat cycle. Either zirconium oxide or titanium oxide ranges from 1 % to 50 % by weight. If the surface film 22 is formed of silicon oxide, the silicon oxide is deposited through a high-frequency sputtering process. In the sputtering process, the target is formed of quartz with purity of 99.9 %, and the dimensions of the target are 3 millimeters in diameter and 10 millimeters in height. The sputtering is carried out at 100 watts, and the ceramic plate 21 is driven for rotation at 10 rpm. A sol-gel process is also available for the surface film 22. The sol-gel process starts with preparation of a solution where 347 grams of ethylsilicate is mixed into 500 grams of ethylalcohol and 190.2 grams of 0.3 % hydrochloride diluted in water. The solution is sprayed on the ceramic plate 22 for 10 seconds, and the ceramic plate 22 is driven for rotation at 500 rpm. The ceramic plate 22 is, then, placed at 800 degrees in centigrade for 10 minutes so that an extremely thin silicon oxide film is produced on the ceramic plate 22. The sol-gel process thus carried out is repeated until the surface film 22 reaches a predetermined thickness. Another process available is a photo-assisted chemical vapor deposition process. The ceramic plate 22 is placed in a reacting chamber of a photo-assisted chemical vapor deposition system, and the reacting chamber is evacuated to 0.2 torr. A gaseous mixture of Si 2 H 6 and 02 is introduced in the reacting chamber, and Si2H6 is regulated to 0.015 % by volume. A chemical reaction takes place under the photo radiation from a mercury lamp, and the silicon oxide is deposited on the ceramic plate 22. The aforementioned three processes are also available for the surface film 22 containing the zirconium oxide or the titanium oxide. Various specimens are produced in accordance with the present invention. Powder of aluminum nitride, powder of yttrium oxide (y 2 O 3 ) and powder of calcium oxide (CaO) are prepared, and the powders are about 1 to 3 microns in average diameter. The powders are regulated to respective proportions shown in Table 3, and the individual mixtures are mixed in a wet ball mill for 72 hours. After drying, an organic binder is added to the individual mixtures and well mixed so as to produce respective pastes. The pastes thus obtained are formed into respective green sheets through the doctor blade technique, and the green sheets are sintered in an atmospheric ambience of nitrogen at 1800 degrees in centigrade for 2 hours. The ceramic plates 22 thus sintered are substantially identical in composition with the mixtures, respectively, and the dimensions of each ceramic plate are 50 millimeters in width, 75 millimeters in length and 0.63 millimeter in thickness. The ceramic plates 22 are oxidized in an oxidizing ambience at 1350 degrees to 1450 degrees in centigrade for respective time periods depending upon the thickness of the aluminum oxide films 21a. The oxidizing ambience has a partial pressure of 1 x 10 -5 to 1 x 10 -3 atm, and the average thickness of each aluminum oxide film 21a is shown in Table 3. The surface films 22 are respectively deposited on the aluminum oxide films 21a through either high-frequency sputtering process, sol-gel process or photo-assisted chemical vapor deposition process, and the composition and the thickness of each surface film 22 are shown in Table 3. Specimen Ceramic plate (wt%) Oxide (micron) Surface film (wt%) Thick (micron) Y 2 O 3 CaO AlN ZrO 2 TiO 2 SiO 2 21 0.1 - residue 0.5 40.3 - residue 0.2 22 0.5 - residue 3.2 - 35.4 residue 0.05 23 1.5 - residue 14.3 30.2 - residue 3.0 24 2.5 - residue 5.8 - 15.1 residue 0.8 25 5 - residue 4.0 - - 100 6.0 26 7 - residue 0.2 - 1.6 residue 1.2 27 9 - residue 1.2 - - 100 0.5 28 10 - residue 11.3 1.2 - residue 0.4 29 - 0.1 residue 6.2 - 47.6 residue 0.01 30 - 1 residue 2.4 - - 100 8.7 31 - 2.5 residue 0.5 10.3 - residue 3.1 32 - 4 residue 10.2 - 20.5 residue 0.1 33 - 5 residue 1.3 20.6 - residue 0.5 34 - 6.5 residue 7.8 - - 100 0.9 35 - 8 residue 12.6 - 5.4 residue 1.5 36 - 9.5 residue 4.3 - - 100 0.6 37 0.1 0.1 residue 0.3 - - 100 2.4 38 1 1 residue 2.3 - - 100 0.32 39 0.5 2 residue 15.4 6.8 - residue 0.05 40 3 1 residue 5.2 - 10.4 residue 0.8 41 4 2 residue 8.8 - - 100 9.6 42 3 5 residue 19.6 - 2.1 residue 0.3 The conductive metallic island patterns 23 are shaped into the dimensions of 45 millimeters in width, 70 millimeters in length and 1 millimeter in thickness, and the metallic heat sinks 24 are 50 millimeters in width, 75 millimeters in length and 3 millimeters in thickness. The conductive metallic island patterns 23 and the metallic heat sinks 24 are formed of pure aluminum and aluminum alloys as shown in Table 4, where specimens No. 24 to 27, 29, 32, 33, and 36 to 39 are embodiments of the present invention. In Table 4, the pure aluminum is abbreviated as "AL", and Mg-2.5% Cr-0.2% aluminum alloy, Mn-0.1% aluminum alloy, Ni-0.02% aluminum alloy and B-0.005% aluminum alloy are respectively abbreviated as "Al-Mg-Cr", "Al-Mn", "Al-Ni" and "Al-B". Following solder-bonding alloys are used for fabricating specimens 21 to 42: 1) Si-13% aluminum alloy (abbreviated as "Al-13Si" in Table 4) 2) Si-7.5% aluminum alloy (abbreviated as "Al-7.5Si") 3) Ge-15% aluminum alloy (abbreviated as "Al-Ge") 4) Si-9.5% Mg-1% aluminum alloy (abbreviated as "Al-Si-Mg") 5) Si-7.5% Ge-10% aluminum alloy (abbreviated as "Al-Si-Ge") The solder-bonding alloys 1 to 3 are formed in a foil of 50 microns thick, or each of the conductive metallic island patterns 23 and the metallic heat sinks 24 is clad with either solder-bonding alloy 4 or 5 of 30 microns. Each of the ceramic plates 21 covered with the surface film 22 is laminated with the conductive metallic island pattern 23, the metallic heat sink 24 and the solder-bonding alloy films, if necessary, and is placed in vacuum at 430 to 610 degrees in centigrade for 10 minutes. Then, each of the ceramic plate 21 is bonded to the conductive metallic island pattern 23 and the metallic heat sink 24, and is annealed at 350 degrees in centigrade for 30 minutes, then being gradually cooled to room temperature in the furnace. The conductive metallic island patterns 23 are, then, plated with copper or nickel to a thickness of about 3 micron through an electroless plating process. For comparison, a prior art ceramic substrate PR is fabricated by using an aluminum oxide plate with purity of 96 %, and the dimensions thereof are 50 millimeters in width, 75 millimeters in length and 0.63 millimeter in thickness. The aluminum oxide plate is sandwiched between oxygen free copper plates of 45 millimeters in width, 70 millimeters in length and 0.3 millimeter in thickness. When the aluminum oxide plate thus sandwiched between the oxygen free copper plates are placed in an argon ambience containing 1 % oxygen at 1075 degrees in centigrade for 50 minutes, then the oxidized copper (Cu 2 O) reacts in liquid phase with copper so that an eutectic alloy is formed for bonding to the aluminum oxide plate. A foil-shaped Sn-60% Pb alloy is sandwiched between one of the copper plates and a heat sink of an oxygen free copper. The heat sink is 50 millimeters in width, 75 millimeters in length and 3 millimeters in thickness. Specimen Heat sink Island pattern Solder Form Alloy 21 Al-Mn Al Foil Al-7.5Si 22 Al Al-Mn ditto Al-Ge 23 Al-Mg-Cr Al Clad Al-Si-Mg 24 Al Al Foil Al-13Si 25 Al-Ni Al-Ni ditto Al-15Si 26 Al Al-Ni Clad Al-Si-Mg 27 Al-B Al-B Clad Al-Si-Ge 28 Al Al-Mn Foil Al-7.5Si 29 Al Al Clad Al-Si-Mg 30 Al-Mg-Cr Al-Mn Foil Al-7.5Si 31 Al-Mn Al-Mn Clad Al-Si-Ge 32 Al-B Al-B Foil Al-7.5Si 33 Al Al Clad Al-Si-Ge 34 Al Al-Mn Foil Al-13Si 35 Al-Mg-Cr Al ditto Al-Ge 36 Al-Ni Al Clad Al-Si-Mg 37 Al-B Al-B Foil Al-7.5Si 38 Al-Ni Al-Ni Foil Al-7.5Si 39 Al Al ditto Al-Ge 40 Al-Mn Al-Mn ditto Al-15Si 41 Al ditto Clad Al-Si-Mg 42 Al-Mg-Cr ditto Foil Al-Ge PR Cu Cu Cu-Cu 2 O Specimens 21 to 42 and the prior art ceramic substrate PR are subjected to heat cycle between 125 degrees in centigrade and -55 degrees in centigrade for evaluation, and the heat cycle is repeated twenty times. After the twenty heat cycles, specimens 21 to 42 and the prior art ceramic substrate are observed to see whether or not any crack takes place. If not, the specimens are subjected to the heat cycles twenty times again. The results are described in Table 5. Heat conductivity is measured for each specimen as well as the prior art ceramic substrate through a laser flashing method, and a bonding strength is further measured as shown in Table 5. Assuming that the prior art ceramic substrate has a unit weight "1", the weight: ratio is calculated for each specimen. Specimen The number of heat cycles Heat conductivity (w/meter deg.in Kvn) Bonding strength (kg/mm 2 ) Weight ratio 21 200 without crack 148 more than 2 0.353 22 ditto 140 ditto 0.352 23 ditto 134 ditto 0.353 24 ditto 159 ditto 0.352 25 ditto 158 ditto 0.354 26 ditto 151 ditto 0.353 27 ditto 156 ditto 0.354 28 ditto 149 ditto 0.352 29 ditto 158 ditto 0.352 30 ditto 137 ditto 0.354 31 ditto 135 ditto 0.353 32 ditto 159 ditto 0.354 33 ditto 157 ditto 0.352 34 ditto 150 ditto 0.352 35 ditto 142 ditto 0.353 36 ditto 151 ditto 0.353 37 ditto 159 ditto 0.354 38 ditto 158 ditto 0.354 39 ditto 157 ditto 0.352 40 ditto 144 ditto 0.354 41 ditto 146 ditto 0.352 42 ditto 133 ditto 0.354 PR 20 with cracks 160 ditto 1 As will be understood from Table 5, the ceramic substrate according to the present invention is as large in heat conductivity and the bonding strength as the prior art ceramic substrate, and is improved in weight and resistance against repetition of heat cycle. Figs. 4 and 5 are applicable to the ceramic substrate shown in Fig. 6, and the design work is carried out in consideration of the tendencies descried with reference to Figs. 4 and 5. This is conducive to fabricate a further improved ceramic substrate. Although particular embodiments of the present invention have been shown and described, it will be obvious to those skilled in the art that various changes and modifications may be made without departing from the scope of the present invention. For example, another aluminum alloy may be available for the metallic heat sink 14 and the conductive metallic islands 12 and 13 in so far as the aluminum alloy is larger in the fatigue limit against a repeated load than copper and smaller in the specific weight than copper. The candidates are an Al-B alloy, an Al-Bi alloy, an Al-Ca alloy, an Al-Cd alloy, an Al-Ce alloy, an Al-Cr alloy, an Al-Cu alloy, an Al-Fe alloy, an Al-Ga alloy, an Al-In alloy, an Al-La alloy, an Al-Li alloy, an Al-Mn alloy, an Al-Mg alloy, an Al-Mo alloy, an Al-Nb alloy, an Al-Ni alloy, an Al-Pb alloy, an Al-Pd alloy, an Al-Pt alloy, an Al-Sb alloy, an Al-Si alloy, an Al-Ti alloy, an Al-Sn alloy, an Al-V alloy, an Al-W alloy, an Al-Y alloy, an Al-Zn alloy and an Al-Ze alloy. Moreover, all of the embodiments are equipped with the heat sinks.

Claims: A ceramic substrate used for an electric or electronic circuit comprising (a) a ceramic plate (11) formed of substance mainly composed of aluminum nitride, (b) conductive island means (12/13) bonded to one surface of said ceramic plate and providing a conductive path for at least one circuit component (16/17) connected thereto, characterized in that c) a metallic heat sink (14; 24) is connected to the other surface of said ceramic plate, and said conductive island means (12/13) and said metallic heat sink (14; 24) consist of aluminum having purity equal to or greater than 99,98 percent. The ceramic substrate as set forth in claim 1, in which said conductive island means (12/13) and said metallic heat sink (14; 24) are respectively bonded to said one surface of said ceramic plate (11) and said other surface of said ceramic plate (11) by using a solder-bonding alloy selected from the group consisting of aluminum-silicon, aluminum-germanium alloy, aluminum silicon-magnesium alloy and aluminum-silicon-germanium alloy. The ceramic substrate as set forth in claim 2, in which said one surface and said other surface are oxidised so as to form an aluminum oxide layer (21a), said ceramic substrate further comprising a surface layer (22) of an oxide formed between said aluminum oxide layer (21a) and said conductive island means (12/13) and between said aluminum oxide layer (21a) and said metallic heat sink (14; 24) for enhancing adhesion to said aluminum oxide layer (21a). The ceramic substrate as set forth in claim 3, in which said aluminum oxide layer (21a) has a thickness not less than 0.2 micron and not greater than 20 microns and said surface layer (22) has a thickness ranging between 0.01 micron and 10 microns. The ceramic substrate as set forth in claim 3, in which said oxide is selected from the group consisting of silicon oxide; silicon oxide and zirconium oxide; and silicon oxide and titanium oxide. The ceramic substrate as set forth in claim 1, in which said conductive island means (12/13) is approximately equal in thickness to said metallic heat sink (14; 24).

Inventors: KUROMITSU YOSHIROU, TORIUMI MAKOTO, YOSHIDA HIDEAKI, YUZAWA MICHIO, KUROMITSU, YOSHIROU, TORIUMI, MAKOTO, YOSHIDA, HIDEAKI, YUZAWA, MICHIO, KUROMITSU, YOSHIROU, C/O MITSUBISHI METAL CORP., TORIUMI, MAKOTO, C/O MITSUBISHI METAL CORP.,, YOSHIDA, HIDEAKI, C/O MITSUBISHI METAL CORP., YUZAWA, MICHIO, C/O MITSUBISHI METAL CORP.,
Applicants: MITSUBISHI MATERIALS CORP, MITSUBISHI MATERIALS CORPORATION
Application year: 1990
Main classification: H01L23
IPC codes: H05K1, H01L23, H05K3