A CATALYTIC CRACKING PROCESS

Abstract: The catalytic cracking of a hydrocarbon oil to provide a product of increased octane number and increased C5+ gasoline content is effected with a cracking catalyst composition comprising as a first component, large pore crystalline molecular sieve, such as a zeolite Y, and as a second component a zeolite having an X-ray diffraction pattern (see Table I).

Description: A CATALYTIC CRACKING PROCESS This invention relates to a catalytic cracking process and, in particular, to a process for the catalytic cracking of hydrocarbon oils to produce higher gasoline yields and increased gasoline octane number. Zeolitic materials, both natural and synthetic, have been demonstrated in the past to have catalytic properties for various types of hydrocarbon conversion. Certain zeolitic materials are ordered, porous crystalline aluminosilicates having a definite crystalline structure as determined by X-ray diffraction, within which there are a large number of smaller cavities which may be interconnected by a number of still smaller channels or pores. These cavities and pores are uniform in size within a specific zeolitic material. Since the dimensions of these pores are such as to accept for adsorption molecules of certain dimensions while rejecting those of larger dimensions, these materials have come to be known as "molecular sieves" and are utilized in a variety of ways to take advantage of these properties. Such molecular sieves, both natural and synthetic, include a wide variety of positive ion-containing crystalline silicates. These silicates can be described as a rigid three-dimensional framework of SiO^ and Periodic Table Group IIIA element oxide, e.g., A10^, in which the tetrahedra are cross-linked by the sharing of oxygen atoms whereby the ratio of the total Group IIIA* element, e.g., aluminum, and silicon atoms to oxygen atoms is I;2. The electrovalence of the tetrahedra containing the Group IIIA element, e.g., aluminum, is balanced by the inclusion in the crystal of a cation, e.g., an alkali metal or an alkaline earth-metal cation. This can be expressed wherein the ratio of the Group IIA element, e.g., aluminum, to the number of various cations, such as Ca/2, Sr/2, Na, K or Li, is equal to unity. One type of cation may be exchanged either entirely or partially with another type of cation utilizing ion exchange techniques in a conventional manner. By means of such cation exchange, it has been possible to vary the properties of a given silicate by suitable selection of the cation. Prior art techniques have resulted in the formation of a great variety of synthetic zeolites. Many of these zeolites have come to be designated by letter or other convenient symbols, as illustrated by zeolite Z (U.S. Patent No. 2,882,243), zeolite X (U.S. Patent No. 2,882,244), zeolite Y (U.S. Patent No. 3,130,007), zeolite ZK-5 (U.S. Patent No. 3,247,195), zeolite ZK-4 (U.S. Patent No. 3,314,752), zeolite ZSM-5 (U.S. Patent No. 3,702,886), zeolite ZSM-11 (U.S. Patent No. 3,709,979), zeolite ZSM-12 (U.S. Patent No. 3,832,449), zeolite ZSM-20 (U.S. Patent No. 3,972,983), zeolite ZSM-35 (U.S. Patent No. 4,016,245), and zeolite ZSM-23 (U.S. Patent No. 4,076,842). The catalytic cracking of hydrocarbon oils utilizing zeolites is a known process, practiced, for example, in fluid-bed catalytic cracking (FCC) units, moving bed or thermo or catalytic cracking (TCC) reactors and fixed bed crackers. Zeolites have been found to be particularly effective for the catalytic cracking of gas oils to produce motor fuels and have been described in many patents including U.S. Patent Nos. 3,140,249; 3,140,251; 3,140,252; 3,140,253; and, 3,271,418. It is also known from, for example, U.S. Patent No. 3,769,202 that improved results can be obtained in catalytic cracking of gas oils if a zeolite having a pore size of less than 7 Angstrom units, e.g., zeolite A, is included with a crystalline zeolite having a pore size greater than 8 Angstrom units, e.g., rare earth-treated zeolite X or Y, either with or without a matrix. However, although such a zeolite combination has been found to be very effective in raising the octane number of the gasoline boiling range product, it does so only at the expense of overall gasoline yield. Improved results in catalytic cracking with respect to both octane number and overall gasoline yield are disclosed in U.S. Patent No. 3,758,403. The cracking catalyst comprises a large pore size crystalline zeolite (pore size greater than 8 Angstrom units) such as zeolite Y in admixture with a ZSM-5 type zeolite wherein the ratio of ZSM-5 type zeolite to large pore size crystalline zeolite is in the range of 1:10 to 3:1. U.S. Patent No. 4,740,292 discloses a catalytic cracking process which employs a mixture of a faujasite-type zeolite as base cracking catalyst and zeolite Beta. Use of this catalyst mixture results in improved cracking activity, increased gasoline plus alkylate precursor yields relative to the base catalyst alone. A characteristic of the foregoing catalytic cracking processes, however, lies in their tendency to produce increased C * and C , olefins at the expense of Cr+ gasoline yield. In those refineries having limited capacity for the conversion of such olefins to more valuable products, e.g., alkylate, it would be desirable to provide a catalytic cracking process which provides a product of increased octane while reducing the aforenoted diminution of C j + gasoline yield. In accordance with the present invention there is provided a catalytic cracking process which comprises catalytically cracking a hydrocarbon feed with a cracking catalyst composition comprising as a first component, a synthetic large pore crystalline molecular sieve and as a second component, a porous crystalline zeolite characterized by an X-ray diffraction pattern including values substantially as set forth in Table I of the specification. During the catalytic cracking process of this invention, the aromatics and naphthenes which are present in the feedstock undergo cracking reactions such as dealkylation, isomerization and ring opening. Additionally, paraffins in the feedstock crack to lower molecular weight species and/or isomerize. The process of this invention enables heavy feedstocks such as gas oils boiling above 215°C (420°F), to be converted to gasoline range products boiling below 215°C (420°F) and distillates boiling in the 215-343°C (420°-650°F). range. Use of the catalyst composition of this invention results in increased octane numbers of the product gasoline and increased overall gasoline yield relative to that obtained employing large pore crystalline silicate cracking catalysts alone. The first component of the catalyst composition employed in the process of the invention is a large pore crystalline molecular sieve, such a materially normally having a Constraint Index (as defined in U.S. Patent No. 4,016,218) less than 1. Large pore crystalline molecular sieves are well known in the art and include faujasite, mordenite, zeolite X, rare earth-exchanged zeolite X (REX), zeolite Y, rare earth-exchanged zeolite Y (REY), ultrastable zeolite Y (USY), rare earth-exchanged ultra stable zeolite Y (RE-USY), dealuminized Y (DAY), ultrahydrophobic zeolite Y (UHP-Y), dealuminized silicon enriched zeolites such as LZ-210, zeolite ZK-5, zeolite ZK-4, zeolite Beta, zeolite Omega, zeolite L, ZSM-20 and other natural or synthetic zeolites. A more thorough description of faujasite zeolites may be found in Chapter 2 of Breck, Donald W. , "Zeolite Molecular Sieves", Robert E. Krieger Publishing Co., Malabar, Fla. , 1984, with specific reference to pages 92-107. Preferably, the first component is a zeolite Y (e.g. REY or USY). Other large pore crystalline molecular sieves which are useful herein include pillared silicates and/or clays; aluminophosphates, e.g., ALP0-5, VPI-5; silicoaluminophosphates, e.g., SAPO-5, SAPO-37, SAPO-31, SAPO-40, SAPO-41; and other metal aluminophosphates. These materials are variously described in U.S. Patents 4,440,871; 4,554,143; 4,567,029; 4,666,875 and 4,742,033. The second component of the catalyst composition employed in the present cracking process herein is a porous crystalline zeolite which in its calcined form is distinguished from the patterns of other known crystalline materials by the lines listed in Table 1 below. — 5- TABLE I Inter lanar d-Spacing (A) Relative Intensity, I/Io x 100 More specifically, the calcined form may be characterized by an X-ray diffraction pattern including the following lines: These values were determined by standard techniques. The radiation was the K-alpha doublet of copper and a diffractometer equipped with a scintillation counter and an associated computer was used. The peak heights, I, and the positions as a function of 2 theta, where theta is the Bragg angle, were determined using algorithms on the computer associated with the diffractometer. From these, the relative intensities, 100 I/I 0 , where I Q is the intensity of the strongest line or peak, and d (obs.) the interplanar spacing in Angstroms Units (A), corresponding to the recorded lines, were determined. In Tables I and II, the relative intensities are given in terms of the symbols W=weak, M=medium, — 7 — S=strong and VS=veιy strong. In terms of intensities, these may be generally designated as follows: W = 0 - 20 • M = 20 - 40 S = 40 -^60 VS = 60 - 100 It should be understood that these X-ray diffraction patterns are characteristic of all species of the present zeolite. The sodium form as well as other cationic forms reveal substantially the same pattern with some minor shifts in interplanar spacing and variation in relative intensity. Other minor variations can occur depending on the Y to X, e.g., silicon to aluminum mole ratio of the particular sample, as well as its degree of thermal treatment. The zeolite of the second catalyst component hereinafter referred to as the zeolite of the invention, generally has a composition involving the molar relationship: X 2 0 3 :(n)Y0 2 , wherein X is a trivalent element, such as aluminum, boron, iron and/or gallium, preferably'aluminum, Y is a tetravalent element such as silicon and/or germanium, preferably silicon, and n is at least 10, usually from 10 to 150, more usually from 10 to 60, and even more usually from 20 to 40. In the as-synthesized form, the zeolite has a formula, on an anhydrous basis and in terms of moles of oxides per n moles of YO2, as follows: (0.005-0.l)Na 2 0:(l-4)R:X 2 0 3 :nY0 2 wherein R is an organic component. The Na and R components are associated with the zeolite as a result of their presence during crystallization, and are easily removed by post-crystallization methods hereinafter more particularly described. The zeolite of the invention is thermally stable and 2 exhibits a high surface area (greater than 400 m /gm as measured by the BET [Bruenauer, Emmet and Teller] test) and unusually large sorption capacity when compared to similar crystal structures. In particular, the zeolite exhibits equilibrium adsorption values greater than 4.5 wt.l for cyclohexane vapor and greater than 10 wt.% for n-hexane vapor. As is evident from the above formula, the zeolite is synthesized nearly free of Na cations. It can, therefore, be used as a catalyst possessing acid catalysis activity without first having to undergo an exchange step. To the extent desired, however, the original sodium cations of the as-synthesized material can be replaced in accordance with techniques well known in the art, at least in part, by ion exchange with other cations. Preferred replacement cations include metal ions, hydrogen ions, hydrogen precursor, e.g., ammonium, ions and mixtures thereof. Particularly preferred cations are those which tailor the activity of the catalyst for cracking. These include hydrogen, rare earth metals and metals of Groups IIA, IIIA, IVA, IB, IIB, IIIB, IVB and VIII of the Periodic Table of the Elements. Prior to its use as catalyst, the zeolite should be subjected to thermal treatment to remove part or all of any organic constituent present therein. Prior to its use in the catalytic cracking process of this invention, the zeolite of the invention crystals can be at least partially dehydrated. This can be achieved by heating the zeolite crystals to a temperature in the range of from 200°C to 595°C in an atmosphere such as air, nitrogen, etc., and at atmospheric, subatmospheric or superatmospheric pressures for between 30 minutes to 48 hours. Dehydration can also be performed at room temperature merely by placing the crystalline material in a vacuum, but a longer time is required to obtain a sufficient amount of dehydration. The stability of the zeolite of the invention may be increased by steaming, such as by contacting the zeolite with 5-1001 steam at a temperature of at least 300°C (preferably 300-650°C) for at least one hour (preferably 1-200 hours) at a pressure of 101-2,500 kPa. In a preferred embodiment, the catalyst is steamed with 75-100% steam at 315°-500°C and atmospheric pressure for 2-25 hours. The zeolite of the invention can be prepared from a reaction mixture containing sources of alkali or alkaline earth metal (M), e.g., sodium or potassium, cation, an oxide of trivalent element X, e.g, aluminum, an oxide of tetravalent element Y, e.g., silicon, an organic (R) directing agent, hexamethyleneimine, and water, said reaction mixture having a composition, in terms of mole ratios of oxides, within the following ranges: In a preferred synthesis method, the Y0 2 reactant contains a substantial amount of solid Y0 2 , e.g., at least 30 wt.% solid Y0 2 . Where Y0 2 is silica, the use of a silica source containing at least 30 wt.l solid silica, e.g., Ultrasil (a precipitated, spray dried silica containing 90 wt.l silica) or HiSil (a precipitated hydrated Si0 containing 87 wt.l silica, 6 wt.l free H 2 0 and 4.5 wt.l bound H 2 0 of hydration and having a particle size of 0.02 micron) favors crystal formation from the above mixture. If another source of oxide of silicon, e.g., Q-Brand (a sodium silicate comprised of 28.8 wt.l of Si0 , 8.9 wt.l Na 0 and 62.3 wt.l H 2 0) is used, crystallization may yield little if any of the zeolite of the invention and impurity phases of other crystal structures, e.g., ZSM-12, may be produced. Preferably, therefore, the Y0 2 , e.g., silica, source contains at least 30 wt.l solid Y0 2 , e.g., silica, and more preferably at least 40 wt.l solid Y0 2 , e.g., silica. Crystallization of the zeolite of the invention can be carried out at either static or stirred conditions in a suitable reactor vessel such as, e.g., polypropylene jars or teflon-lined or stainless steel autoclaves. Generally, crystallization is conducted at 80°C to 225°C for 25 hours to 60 days. Thereafter, the crystals are separated from the liquid and recovered. In all cases, crystallization is-facilitated by the presence of at, least.0.01 percent, preferably 0.10 percent and still more preferably 1 percent, seed crystals based on the total weight of the crystalline product formed. It may be desirable to incorporate either or both components of the catalyst system herein with another material which is resistant to the temperatures and other conditions employed in the cracking process of this invention. Such materials include active and inactive materials and other synthetic or naturally occurring porous crystalline molecular sieves as well as inorganic materials such as clays, silica and/or metal oxides such as alumina. The latter may be either naturally occurring or in the form of gelatinous precipitates or gels including mixtures of silica and metal oxides. Naturally occurring clays which can be composited with either or both catalyst components herein include the montmorillonite and kaolin family, which families include the subbentonites, and the kaolins commonly known as Dixie, McNamee, Georgia and Florida clays or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite, or anauxite. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification. In addition to the foregoing materials, either or both catalyst components can be composited with one or more porous matrix materials such as silica, alumina, silica-alumina, silica-magnesia, silica-zirconia, silica-thoria, silica-beryllia, silica-titania as well as ternary oxide compositions such as silica-alumina-thoria, silica-alumina-zirconia, silica-alumina-magnesia silica-magnesia-zirconia, and the like. It may also be advantageous to provide at least a part of the foregoing matrix materials in colloidal form so as to facilitate extrusion of the bound catalyst component(s). The relative proportions of catalyst component(s) and binder can vary widely with the content of the former ranging from 1 to 95 percent by weight, and more usually from 10 to 70 weight percent, of the composite. The catalyst components can be independently composited with the same or different binder materials or both materials can be incorporated together in the same binder material. The amount of the zeolite of the invention which is added to the large pore crystalline cracking catalyst component can be fairly small since the presence of even minor quantities of the zeolite in the combination catalyst can result in substantial octane gains. The exact amount of zeolite of the invention relative to the total quantity of cracking catalyst may vary from cracking unit to cracking unit depending upon the desired octane number, total gasoline yield required, the nature of the available feedstock and other similar factors. However, for many cracking operations, the weight percent of zeolite of the invention relative to the total quantity of catalyst composition can range from 0.01 to 25 and preferably from 0.1 to 10. The feedstock for the present catalytic cracking process comprises a heavy hydrocarbon oil such as a gas oil, coker tower bottoms fraction, reduced crude, vacuum tower bottoms, deasphalted vacuum resids, FCC tower bottoms**and cycle oils. Oils derived from coal, shale or tar sands are also;suitable feedstocks. Oils of this kind generally boil above 650°F (343°C) although the process is also useful with oils which have initial boiling points as low as 500°F. (260°C). These heavy oils comprise high molecular weight long-chain paraffins and high molecular weight aromatics with a large proportion of fused ring aromatics. Typical boiling ranges will be 343 to 566°C (650° to 1050°F), or 343 to 510°C (650°C to 950°F) but oils with a narrower boiling range may, of course, be processed: for example, those with a boiling range of 343 to 454°C (650° to 850°F). It is also possible to co-process materials boiling below 260°C (500°F) but the degree of conversion will be lower for such components. Feedstocks containing lighter ends of this kind will normally have an initial boiling point above 150°C (300°F). The present process is of a particular utility with highly paraffinic feeds because with feeds of this kind the greatest improvement in octane number can often be obtained. However, benefits can also be achieved with relatively non-waxy feeds. Processing can be carried out under conditions similar to those used for known types of catalytic cracking processes. Thus, process temperatures of from 400 to 650°C (750° to 1200°F) can be used although temperatures above 565°C (1050°F) will normally not be employed. Preferably, temperatures of 450 to 565°C (840° to 1050°F) are employed. The liquid hourly space velocity (LHSV) of the feedstock will generally range from 0.1 to 20 and preferably from 0.1 to 10. The conversion can be conducted by contacting the feedstock with a fixed stationary bed of catalyst, a fixed fluidized bed or with a transport bed. The catalyst can be regenerated by burning in air or other oxygen-containing gas. A preliminary hydrotreating step to remove nitrogen and sulfur and to saturate aromatics to naphthenes without substantial boiling range conversion will usually improve catalyst performance and permit lower temperatures, higher space velocities or combinations of these conditions to be employed. The invention will now be more particularly described with reference to the following examples and the accompanying drawings, in which Figures 1-5 are X-ray diffraction patterns of the calcined crystalline products obtained in Examples 1, 3, 4, 5 and 7 respectively. In the Examples, whenever sorption data are set forth for comparison of sorptive capacities for water, cyclohexane and/or n-hexane, they are Equilibrium Adsorption values determined as follows: A weighed sample of the calcined adsorbent was contacted with the desired pure adsorbate vapor in an adsorption chamber, evacuated to less than 1 mm Hg and contacted with 1.6 kPa (12 Torr) of water vapor or 5.3 kPa (40 Torr) of n-hexane or 5.3 kPa (40 Torr) of cyclohexane vapor, pressures less than the vapor-liquid equilibrium pressure of the respective adsorbate at 90°C. The pressure was kept constant (within +_ 0.5 mm Hg) by addition of adsorbate vapor controlled b a manostat during the adsorption period, which did not exceed 8 hours. As adsorbate was adsorbed by the zeolite of the invention, the decrease in pressure caused the manostat to open a valve which admitted more adsorbate vapor to the chamber to restore the above control pressures. Sorption was complete when the pressure change was not sufficient to activate the manostat. The increase in weight was calculated as the adsorption capacity of the sample in g/100 g of calcined adsorbant. The zeolite of the invention always exhibits Equilibrium Adsorption values of , greater than 4.5 wt.l, usually greater than 7 wt.l for cyclohexane vapor and greater than 10 wt.l for n-hexane vapor and normally greater than 10 wt.l for water vapor. When Alpha Value is examined, it is noted that the Alpha Value is an approximate indication of the catalytic cracking activity of the catalyst compared to a standard catalyst and it gives the relative rate constant (rate of normal hexane conversion per volume of catalyst per unit time). It is based on the activity of a highly active silica-alumina cracking catalyst taken as an Alpha of 1 (Rate Constant = 0.016 sec "1 ). The Alpha Test which was used herein is described in J. Catalysis, 61, pp. 390-396 (1980). It is noted that intrinsic rate constants for many acid-catalyzed reactions are proportional to the Alpha Value for a particular crystalline silicate catalyst, i.e., the rates for toluene disproportionation, xylene isomerization, alkene conversion and methanol conversion (see "The Active Side of Acidic Aluminosilicate Catalysts," Nature, Vol. 309, No. 5969, pp. 589-591, 14 June 1984). - 14 - EXAMPLE 1 1 part of sodium aluminate (43.51 l 2 0 j , 32.21 Na 2 0, 25.6 H 2 0) was dissolved in a solution containing 1 part of 501 NaOH solution and 103.13 parts H 2 C To this was added 4.50 parts hexamethyleneimine. The resulting solution was added to 8.55 parts of Ultrasil, a precipitated, spray-dried silica (about 901 Sio . The reaction mixture had the following composition, in mole ratios: Si0 2 /Al 2 0 3 = 30.0 Gτf/Si0 2 = 0.18 H 2 0/Si0 2 = 44.9 Na/Si0 2 = 0.18 R/Si0 2 = 0.35 where R is hexamethyleneimine. The mixture was crystallized in a stainless steel reactor, with stirring, at 150°C for 7 days to produce the zeolite of the invention. The crystalline product was filtered, washed with water and dried at 120°C. After a 20 hour calcination at 538°C, the X-ray diffraction pattern contained the major lines listed in Table III. Figure 1 shows the X-ray diffraction pattern of the calcined product. The sorption capacities of the calcined zeolite were measured to be: H 2 0 15.2 wt.l Cyclohexane 14.6 wt.l n-Hexane 16.7 wt.l The surface area of the calcined zeolite was measured to be 494 m 2 /g. The chemical composition of the uncalcined zeolite was determined to be as follows: wt.% EXAMPLE 2 A portion of zeolite MCM-22 of Example 1 was tested in the Alpha Test and was found to have an Alpha Value of 224. EXAMPLES 3-5 Three separate synthesis reaction mixtures were prepared with compositions indicated in Table VI. The mixtures were prepared with sodium aluminate, sodium hydroxide, Ultrasil, hexamethyleneimine (R) and water. The mixtures were maintained at 150°C, 143°C and 150°C, respectively, for 7, 8 and 6 days respectively in stainless steel autoclaves at autogenous pressure. Solids were separated from any unreacted components by iltration and then water washed, followed by drying at 120°C. The product crystals were subjected to X-ray diffraction, sorption, surface area and chemical analyses and found to be the zeolite of the inventin. The results of the sorption, surface area and chemical analyses are presented in Table IV and the X-ray diffraction patterns are presented in Figures 2, 3 and 4, respectively. The sorption and surface area measurements were of the calcined product. TABLE IV Example Synthesis Mixture, mole ratios Si0 2 /Al 2 0 3 OH /Si0 2 ^O/SiO j Na/Si0 2 R/SiO, Quantities of the calcined (538°C for 3 hours) MCM-22 produced in Examples 3, 4 and 5 were tested in the Alpha Test and found to have Alpha Values of 227, 180 and 187, respectively. EXAMPLE 7 To demonstrate a further preparation of the present zeolite, 4.49 parts of hexamethyleneimine was added to a solution containing 1 part of sodium aluminate, 1 part of 50% NaOH solution and 44.19 parts of H 2 0. To the combined solution were added 8.54 parts of Ultrasil silica. The mixture was crystallized with agitation at 145°C for 59 hours and the resultant product was water washed and dried at 120°C. The X-ray diffraction pattern of the dried product crystals is presented in Figure 5 and demonstrates the product to be the crystalline material of this invention. Product chemical composition, surface area and adsorption analyses results were as set forth in Table V: TABLE V Product Composition (uncalcined) C 12.1 wt.l N 1.98 wt.l Na 640 ppm A1 2 0 3 5.0 wt.l Si0 2 74.9 wt.l Si0 2 /Al 2 0 3 , mole ratio 25.4 Adsorption, wt.l Cyclohexane 9.1 N-Hexane 14.9 H 2 0 16.8 2 Surface Area, m /g 479 EXAMPLE 8 25g grams of solid crystal product from Example 7 were calcined in a flowing nitrogen atmospheres at 538°C for 5 hours, followed by purging with 51 oxygen gas (balance N 2 ) for another 16 hours at 538°C. Individual 3g samples of the calcined material were ion-exchanged with 100 ml of 0. IN „TEABr, TPABr and LaCl 3 solution separately. Each exchange was carried out at ambient temperature for 24 hours and repeated three times. The exchanged samples were collected by filtration, water-washed to be halide-free and dried. The compositions of the exchanged samples are tabulated below demonstrating the exchange capacity of the present crystalline silicate for different ions. Exchange Ions TEA TPA La Ionic Composition, wt.l Na N C La The La-treated zeolite from Example 8 was sized to 14 to 25 mesh and then calcined in air at 538°C for 3 hours. The calcined material had an Alpha Value of 173. EXAMPLE 10 The calcined La-treated material from Example 9 was severely steamed at 649°C in 1001 steam for 2 hours. The steamed zeolite had an Alpha Value of 22, demonstrating that zeolite had very good stability under severe hydrothermal treatment. EXAMPLE 11 This example illustrates the preparation of the present zeolite where X in the general formula, supra, is boron. Boric acid, 2.59 parts, was added to a solution containing 1 part of 451 KOH solution and 42.96 parts H 2 0. To this was added 8.56 parts of Ultrasil silica, and the mixture was thoroughly homogenized. A 3.88 parts quantity of hexamethyleneimine was added to the mixture. The reaction mixture had the following composition in mole ratios: Si0 2 /B 2 0 3 = 6.1 0H " /Si0 2 = 0.06 H 2 0/Si0 2 = 19.0 K/Si0 2 = 0.06 R/Si0 2 = 0.30 where R is hexamethyleneimine. The mixture was crystallized in a stainless steel reactor, with agitation, at 150°C for 8 days. The crystalline product was filtered, washed with water and dried at 120°C. A portion of the product was calcined for 6 hours at 540°C and found to have the following sorption capacities: H 2 0 (12 Torr) 11.7 wt.l Cyclohexane (40 Torr) 7.5 wt.l n-Hexane (40 Torr) 11.4 wt.l The surface area of the calcined crystalline material was 2 measured (BET) to be 405m /g. - 21 - The chemical composition of the uncalcined material was determined to be as follows: N 1.94 wt.l Na 175 pp K 0.60 wt.l Boron 1.04 wt.l A1 2 0 3 920 ppm Ash 74.11 wt.l, Si0 2 /Al 2 0 3 , molar ratio = 1406 Si0 2 /(A1+B) 2 0 3 , molar ratio = 25..8 EXAMPLE 12 A portion of the calcine product of Example 11 was treated with NH.C1 and again calcined. The final zeolite product was tested in the Alpha Test and found to have an Alpha Value of 1. EXAMPLE 13 This example illustrates* another preparation of the zeolite in which X of the general formula, supra, is boron. Boric acid, 2.23 parts, was added to a solution of 1 part,of 50 NaOH solution and 73.89 parts H 2 . To this solution was added 15.29 parts of HiSil silica followed by 6.69 parts of hexamethyleneimine. The reaction mixture had the following composition in mole ratios: Si0 2 /B 2 0 3 = 12.3 0H7Si0 2 = 0.056 H 2 0/Si0 2 = 18.6 K/Si0 2 = 0.056 R/Si0 2 = 0.30 where R is hexamethyleneimine. The mixture was crystallized in a stainless steel reactor, with agitation, at 300°C for 9 days. The crystalline product was filtered, washed with water and dried at 120°C. The sorption capacities of the calcined material (6 hours at 540°C) were measured: H 2 0 14.4 wt.l Cyclohexane 4.6 wt.l n-Hexane 14.0 wt.l The surface area of the calcined crystalline material was measured 2 to be 438m /g. The chemical composition of the uncalcined material was determined to be as follows: 12 3 249 Si0 2 /(A1+B) 2 0 3 , molar ratio = 28.2 EXAMPLE 1 A portion of the calcined product of Example 13 was tested in the Alpha Test and found to have an Alpha Value of 5. EXAMPLE 15 A further sample of the zeolite of the invention was prepared by adding 4.49 parts of hexamethyleneimine to a mixture containing 1.00 parts sodium aluminate, 1.00 parts 50% NaOH, 8.54 parts Ultrasil VN3 and 44.19 parts deionized H 2 0. The reaction mixture was heated to 143°C (290°F) and stirred in an autoclave at that temperature for crystallization. After full crystallinity was achieved, the majority of the hexamethyleneimine was removed from the autoclave by controlled distillation and the zeolite crystals were separated from the remaining liquid by filtration, washed with deionized DI ^0 and dried. A fluid catalyst was prepared by spray drying an aqueous slurry containing 20 wt.l of the resultant in a Si0 2 -Al 2 0 3 (87/13 weight ratio) gel matrix and ammonium exchanging the spray dried catalyst. The properties of the fluid catalyst composition, calcined at 650°C (1200°F) for 2 hours in air, are set forth in Table VI as follows: 2 Surface Area, m /g 314 Pore Volume, cc/g 0.4 Rare earth cations were incorporated into the resultant fluid catalyst by contact with a 1.2 wt.l rare earth chloride solution (Davison Specialty Chemical Co.) for 6 hours at room temperature. The wt.l of each rare earth metal present in the solution was as follows: praseodymium, 1.16; neodymiium, 4.05; lanthanum, 5.53; cerium, 9.41; and, samarium, 0.68. After filtering, the rare earth-treated catalyst was washed free of chloride and dried at 120°C (250°F). The resulting rare earth-treated fluid catalyst, which was calcined at 540°C (1000°F) for 2 hours in air, possessed the properties set forth in Table VII as follows: Mixtures of a regenerated equilibrium REY catalyst (Engelhard HEZ-53) as a base cracking catalyst, the dried-only and rare earth-treated catalyst compositions of Example 15, and a ZSM-5 zeolite were prepared as follows: Base Catalyst Catalyst Additive Composition REY REY calcined catalyst-of Example B 15 (0.5 wtl zeolite) REY calcined catalyst of Example C 15 steamed at 1450°F (790°C) for 10 hours at 0 psig (100 kPa) in 45 steam/ 55 air (5 wtl zeolite) REY rare earth-treated catalyst D of Example 15 (0.5 wt.l zeolite) REY rare earth-treated zeolite E of Example 15 steamed at 1450°F (790°C) for 10 hours at 0 psig (100 kPa) in 451 steam/ 551 air (5 wtl zeolite) REY 25 ZSM-5 additive catalyst F steamed at 1450°F (790°C) for 10 hours at 0 psig (100 kPa) in 45% steam/551 air (2 wtl ZSM-5) Catalyst compositions A-F were evaluated for cracking a heavy gas oil in a fixed-fluidized bed unit at 960°F (515°C) over a range of catalyst/oil ratios. The heavy gas oil possessed the properties set forth in Table VIII as follows: TABLE VIII Properties of Heavy Gas Oil Feed Gravity, API 24.3 Aniline Pt., °F(°C) 177 (81) Hydrogen, wt.l 12.3 Sulfur, wt.l 1.87 Nitrogen, wt.l 0.10 Basic Nitrogen, ppm 327 Conradson Carbon, wt.l 0.28 Kinematic Viscosity at 210°F(99°C) 3.6 The performance of the various catalyst compositions at 65 vol.I conversion are shown in Table IX and yield/octane shifts for catalyst compositions B-F are shown in Table X as follows: TABLE IX Performance of Catalysts A-F for Cracking Heavy Gas Oil Catalyst Composition A B C D E F TABLE X Yield/Octane Shifts for Catalyst Compositions B-F With Respect to Catalyst Composition A Catalyst Composition B C D E 65 Vol I Conversion As shown in Tables IX and X, compared to catalyst composition A (REY alone), catalyst compositions B and D (catalyst mixtures containing 0.5 wtl unsteamed zeolite of the invention and unsteamed rare earth-exchanged zeolite of the invention, respectively) produced C 5 + gasoline with a 1 to 2 RON boost with some loss in C^+ gasoline and a corresponding increase in C 3 and C^ olefins and isobutane. All three steamed catalyst compositions (C, E and F) produced C 5 + gasoline with a 0.8 to 1.3 RON boost, a loss in Cr+ gasoline and a corresponding increase in C 3 and C olefins and isobutane. However, compared to catalyst composition F (containing ZSM-5), catalyst compositions C and E (containing the zeolite of the invention) were found to be substantially more selective since the loss in C 5 + gasoline per unit octane increase (1.3%) was considerably less, for catalyst compositions C and E than for catalyst composition F (2.4%).

Claims: CLAIMS: 1. A catalytic cracking process which comprises catalytically cracking a hydrocarbon feed with a cracking catalyst composition comprising as a first component, a synthetic large pore crystalline molecular sieve and as a second component, a porous crystalline zeolite having, in its calcined form, an X-ray diffraction pattern with lines set forth in Table I of the specification. 2. The process of Claim 1 wherein the zeolite second component has, in its calcined form, an X-ray diffraction pattern with lines set forth in Table II of the specification. 3. The process of Claim 1 or Claim 2 wherein the zeolite second component has equilibrium adsorption capacities greater than 4.5 wt.l for cyclohexane vapor arid greater than 10 wt.l for n-hexane vapor. 4. The process of any one of Claims 1 to 3 wherein the zeolite second component has a composition comprising the molar relationship X 2 0 3 :(n)Y0 2 , wherein n is at least 10, X is a trivalent element and Y is a tetravalent element. 5. The process of Claim 4 wherein X comprises aluminum and Y comprises silicon. 6. The process of Claim 1 wherein the zeolite second component comprises from 0.01 to 25 wtl of the total cracking catalyst composition. 7. The process of Claim 1 wherein the large pore molecular sieve first component has a Constraint Index less than 1. 8. The process of Claim 1 wherein the large pore molecular sieve first component is a zeolite Y. 9. The process of Claim 1 wherein the first and/or second component is combined with a binder material. 10. A cracking catalyst composition comprising as a first component, a large pore crystalline molecular sieve and as a second component, a porous crystalline zeolite having, in its calcined form, an X-ray diffraction pattern with lines as set forth in Table I of the specification.

Inventors: ABSIL ROBERT PETER LEONARD, ANGEVINE PHILIP JAY, BUNDENS ROBERT GLENN, HERBST JOSEPH ANTHONY, MIZRAHI SAID, RUBIN MAE KOENIG, ABSIL, ROBERT, PETER, LEONARD, ANGEVINE, PHILIP, JAY, BUNDENS, ROBERT, GLENN, HERBST, JOSEPH, ANTHONY, MIZRAHI, SAID, RUBIN, MAE, KOENIG
Applicants: MOBIL OIL CORP, MOBIL OIL CORPORATION
Application year: 1990
Main classification: C10G11
IPC codes: B01J29, C10G11, C10G35