Polymer mixture comprising aromatic polycarbonate, polybutylene terephthalate and polyalkylene glycol

Abstract: The invention relates to polymer mixtures which comprise an aromatic polycarbonate, a polybutylene terephthalate and a polyalkylene glycol. Due to the pre­ sence of the polyalkylene glycol a good lacquer bonding is obtained when lacquer systems on the basis of water are used.

Description: The invention relates to a polymer mixture wich comprises a polybutylene terephthalate and an aromatic polycarbonate. Such mixtures are known per se . For this purpose reference may be made, for example, to GB-A-1569296. US-A-4,257,937 and US-A-4,280,949 disclose polymer mixtures which comprise a polybutylene terephthalate, a polycarbonate, and an agent to improve the impact strength. The known mixtures generally have favourable properties: they have good mechanical properties and can withstand the influence of organic solvents. As a result of this the said mixtures are suitable for manufacturing therefrom parts for motor-cars, for example, bumpers. It is sometimes desired to provide the articles formed from the polymer mixture with a decorative layer of lacquer. In the known polymer mixture bonding problems may then occur between the surface and the layer of lacquer. The bonding of the lacquer is determined both by the polymeric composition of the substrate and by the type of lacquer system. When lacquer systems on the basis of water are used, the lacquer bonding is different from anhydrous systems. The invention provides polymer mixtures which comprise A. a polybutylene terephthalate and B. an aromatic polycarbonate to which a polyalkylene glycol polymer or a polyalkylene glycol copolymer (C) has been added which ensures a better bonding to the layer of lacquer. EP-A-0324 065 describes polymer mixtures comprising a polybutylene terephthalate, an aromatic polycarbonate and a polydialkylsiloxane. The polydialkylsiloxane has been added to increase the adhesion of lacquer layers upon objects molded out of the polymer mixtures. Chemical Abstracts, Vol. 88, no. 8, 20th February 1978, page 68, Abstract no. 52064k describes polybutylene terephthalate resins comprising polyethylene glycol monostearate with improved coatability for aminoalkyd resins. The polymer mixture according to the invention is characterised in that it comprises 0.1-5 parts by weight of a polyalkylene glycol polymer or a polyalkylene glycol copolymer (C) per 100 parts by weight of A + B. The polymer mixture according to the invention preferably comprises a polyethylene glycol. Per 100 parts by weight of constituents A plus B the quantity by weight of A is preferably 10-90 parts and that of B is preferably 90-10 parts. The polymer mixture according to the invention may comprise 0.1-100 parts by weight of conventionally used additives per 100 parts by weight of A + B. The polymer mixture according to the invention preferably comprises 0.1-50 parts by weight of an agent to improve the impact strength per 100 parts by weight of A + B. A core-shell polymer built up from a rubber-like core on which one or more shells have been grafted is preferably used as an agent to improve the impact strength. The polymer mixture according to the invention comprises at any rate the following constituents: A. a polybutylene terephthalate homopolymer or a copolyester derived from butane-1,4-diol possibly in combination with another diol and terephthalic acid possibly in combination with another carboxylic acid. B. an aromatic polycarbonate, and C. a polyalkylene glycol polymer or a polyalkylene glycol copolymer. The polymer mixture may comprise one or more of the following constituents: D. conventionally used additives, E. one or more agents to improve the impact strength. A. Polybutylene terephthalate Polybutylene terephthalate is a polymer known per se . It is derived from butane-1,4-diol and terephthalic acid. It is possible to use copolyesters in the polymer mixtures in which a part of the diol compound and/or a part of the terephthalic acid has been replaced by another diol and/or carboxylic acid. For the polymer mixture according to the invention it is preferred to use a polybutylene terephthalate which is built up for more than 70mol.% from units derived from butane-1,4-diol and terephthalic acid. It is possible to use polybutylene terephthalate in which a branching agent, for example, a glycol having three or more hydroxyl groups or a three-fold or multifunctional carboxylic acid has been incorporated. It is possible to use one or more different polybutylene terephthalates or copolyesters. B. Aromatic polycarbonate Aromatic polycarbonates are materials known per se . They are generally prepared by reacting a dihydric phenol compound with a carbonate 5 precursor, for example, a halogen formiate or a carbonate ester. Aromatic polycarbonates are polymers which comprise units of the formula wherein A is a bivalent aromatic radical which is derived from the dihydric phenol used in the preparation of the polymer. Mononuclear or polynuclear aromatic compounds may be used as dihydric phenols in the preparation of the aromatic polycarbonates, which compounds comprise two hydroxy radicals each directly bonded to a carbon atom of an aromatic nucleus. The known branched polycarbonates as described, for example, in US-A-4,001,184 are also suitable. Suitable aromatic polycarbonates are also the so-called polyester carbonates which are obtained by performing the polymerisation reaction in the presence of an ester precursor, for example, a difunctional carboxylic acid, for example, terephthalic acid or an ester-forming derivative thereof. These polyester carbonates comprise ester compounds and carbonate compounds in the polymeric chain. Polyester carbonates are described, for example, in US-A-3,169,121. It is possible to use one or more different aromatic polycarbonates. C. Polyalkylene glycol polymer or polyalkylene glycol copolymer. Polyalkylene glycol polymers or copolymers are compounds known per se. Polyalkylene glycol is mentioned notably as an additive for synthetic resins: it provides inter alia antistatic properties. For this purpose, reference may be made, for example, to Kirk-Othmer, Encyclopedia of Chemical Technology, 3rd edition, vol. 3, 1978, pp . 167-171. The preparation and various uses of these (co)polymers are described for instance in Kirk Othmer, volume 18, pp. 616-645. These copolymers may be obtained by polymerisation of one or more different alkene oxides, for example, ethylene oxide and/or propylene oxide and/or butylene oxide. The molecular weight may be chosen between 200 and 20,000, preferably between 500 and 5,000. Block copolymers with propylene oxide blocks and ethylene oxide blocks are preferably used. A polyalkylene glycol having a molecular weight of approximately 3500 g/mol is preferably used in the the polymer mixture according to the invention. D conventionally used additives In addition to the constituents mentioned hereinbefore the polymer mixture according to the invention may comprise one or more additives. Examples of suitable additives are stabilisers, transesterification inhibitors, dyes pigments, fillers, and reinforcing fibres, for example, glass fibres, release agents. E. Agents to improve the impact strength The polymer mixture according to the invention may comprise one or more agents to improve the impact strength. So-called core-shell polymers are preferably used which are built up from a rubber-like core on which one or more shells have been grafted. The core usually consists substantially of an acrylate rubber or a butadiene rubber. One or more shells have been grafted on the core. Usually these shells are built up for the greater part from a vinylaromatic compound and/or a vinyl cyanide and or an alkyl (meth)acrylate and/or (meth)acrylic acid. The core and/or the shell(s) often comprise(s) multifunctional compounds which may work as a cross-linking agent and/or a grafting agent. The said polymers are usually prepared in several stages. The polymer mixture according to the invention may be obtained according to any conventionally used method of preparing polymer mixtures. Preferably, the individual constituents are collectively mixed in the melt (compounded) in an extruder. The extrudate (in strand form) which emanates from the extruder may be chopped up to pellets. The pellets may be further processed, for example, in an injection moulding machine. Example I, comparative examples A, B and C Various polymer mixtures were prepared starting from the following constituents: PBT: a polybutylene terephthalate having an intrinsic viscosity of 1.19 dl/g measured in a 60/40 mixture of phenol and tetrachloroethane at 25°C PC: an aromatic polycarbonate derived from bisphenol A and phosgene having an intrinsic viscosity of 53 ml/g measured in methylene chloride at 25°C IM: an agent to improve the impact strength of the core-shell type having a core consisting substantially of a butadiene rubber on which a shell of a copolymer which is built up substantially of methyl methacrylate has been grafted ST: A mixture of several conventionally used stabilisers SF: a dimethyl silicone fluid having a nominal viscosity of 500 ctks at 25°C PEG: a polyethylene glycol having a molecular weight of approximately 3500 g/mol. The various constituents were compounded in a Werner & Pfleiderer extruder in the quantities as indicated in the table hereinafter (average value of the adjusted temperatures: 235°C). The resulting extrudate was chopped up to pellets. From the pellets plates were injection-moulded for the determination of the lacquer bonding (dimensions of the plates: length x width 175 x 175 mm, thickness 3 mm). The surface was painted by means of a spray gun. A water-borne primer, no. 62070 on the basis of water, from Messrs.Woerwag was used as a lacquer. The lacquered plates were first cured at 780° C for 15 minutes and then conditioned at 50° C for 48 hours. The bonding strength was then determined according to DIN 53151 with TESA ® tape 4651. An evaluation "GtO" indicates a good bonding; an evaluation "Gt5" indicates a poor bonding. The results obtained are recorded in the table hereinafter. Examples I, comparative examples A, B and C Composition (parts by weight) A B C I PC 49 49 49 49 PBT 40 39 39 39 IM 10 10 10 10 ST 0.63 0.63 0.63 0.63 SF - 0.5 1 - PEG - - - 1 Lacquer bonding: Gt4 Gt3 Gt5 Gt0 It may be seen from the table that the addition of polyethylene glycol (example I) leads to an actual improvement of the lacquer bonding. A dimethyl silicone fluid (comparative examples B and C) provides only a slight improvement when using a lacquer based on water, or it provides a deterioration of the lacquer bonding.

Claims: A polymer mixture which comprises A. a polybutylene terephthalate homopolymer or a copolyester derived from butane-1,4-diol possibly in combination with another diol and terephthalic acid possibly in combination with another carboxylic acid and B. an aromatic polycarbonate, characterised in that the polymer mixture comprises 0.1-5 parts by weight of a polyalkylene glycol polymer or a polyalkylene glycol copolymer (C) per 100 parts by weight of A + B. A polymer mixture as claimed in Claim 1, characterised in that the polymer mixture comprises polyethylene glycol. A polymer mixture as claimed in Claim 1, characterised in that the polymer mixture comprises 0.1-100 parts by weight of one or more conventionally used additives per 100 parts by weight of A + B. A polymer mixture as claimed in Claim 1, characterised in that the polymer mixture comprises 0.1-50 parts by weight of an agent to improve the impact strength per 100 parts by weight of A + B. A polymer mixture as claimed in Claim 1, characterised in that the polymer mixture comprises as an agent to improve the impact strength a core-shell polymer which is built up from a rubber-like core on which one or more shells have been grafted.

Inventors: DE JONG ROBERTUS EDUARD, DE WIT GERRIT, KEMPERS TORBEN PAUL, DE JONG, ROBERTUS EDUARD, DE WIT, GERRIT, KEMPERS, TORBEN PAUL
Applicants: GEN ELECTRIC, GENERAL ELECTRIC COMPANY
Application year: 1990
Main classification: C08L69
IPC codes: C08L69, C08L67