Nematic liquid-crystal composition for active matric application

Abstract: The invention relates to a nematic liquid-crystal composition for active matrix displays with high voltage holding ratio and extremely good low temperature stability.

Description: The invention relates to a nematic liquid-crystal composition for active matrix application. Active matrix displays (AMD) are highly favored for commercially interesting displays with a high information content. Such AMDs are used for TV application and also for displays with high information content for automobiles and aeroplanes. AMDs have non-linear electrical switching elements which are integrated at each picture element. As non-linear driving elements thin film transistors (TFT) [Okubo, U., et al., 1982, SID 82 Digest, pp. 40-41] or diodes (e.g.: metal insulator metal: MIM) [Niwa, K., et al., 1984, SID 84, Digest, pp. 304-307] can be applied. These non-linear driving elements allow to use an electro-optical effect with a rather flat electro-optical characteristic if a good viewing angle characteristic can be obtained. So a TN-type LC cell [Schadt, M. and Helfrich, W., 1971, Appl. Phys. Lett., 18, 127] with a twist angle of 90° can be used. To provide the good contrast over a wide viewing angle, operation in the first minimum of transmission [Pohl, L., Eidenschink, R., Pino, F. del., and Weber, G., 1980, German Pat., DBP 30 22 818, and 1981, US Pat. 4 398 803; Pohl, L., Weber, G., Eidenschink, R., Baur, G., and Fehrenbach, W., 1981, Appl. Phys. Lett., 38, 497; Weber, G., Finkenzeller, U., Geelhaar, T., Plach, H.J., Rieger, B., and Pohl, L., 1988, Int. Symp. on Liq. Cryst., Freiburg, to be published in Liq. Crys.] is required. These AMDs are very well suited for TV applications and consequently are of high commercial interest. For these applications some physical properties of the liquid crystals become more important than for passive TN displays. Some of the decisive properties for the performance of an AMD are resistivity and stability of the liquid crystal [Togashi, S., Sekiguchi, K., Tanabe, H., Yamamoto, E., Sorimachi, K., Kajima, E., Watanabe, H., Shimuzu, H., Proc. Eurodisplay 84, Sept. 1984: A 210-288 Matrix LCD Controlled by Double Stage Diode Rings, p. 144 ff, Paris; Stromer, M., Proc. Eurodisplay 84, Sept. 1984: Design of Thin Film Transistors for Matrix Addressing of Television Liquid Crystal Displays, p. 145 ff, Paris]. In an AMD the non-linear switching elements are addressed in a multiplex scheme. So they charge the electrodes of a pizel in the limited time they are active. Then they become inactive until they are addressed again in the next cycle. Consequently the change of the voltage on an activated (charged) pixel is a nondesired but a very decisive feature of such a display. The discharge of a pixel is determined by two factors. They are the capacity of the electrodes of the pixel and resistivity of the dielectric material between the electrodes, namely the liquid crystal. The characteristic time constant of the decay of the voltage at a pixel (RC-time) has to be significantly bigger than the time between two adressing cycles (tadr.). A parameter frequently used to describe the performance of an AMD is the voltage holding ratio HR of a picture element: As the voltage at a pixle decays exponentially an increase of the holding ratio necessitates liquid crystal materials with exceptionally high resistivities. There are several points of importance for the resistivity of the liquid crystal inside a display, e.g. orientation layers, curing condition of the orientation material. But by no means less important are the electrical properties of the liquid crystal used. Especially the resistivitiy of the liquid crystal in the display determines the magnitude of the voltage drop at the pixel. There is thus still a great need for liquid-crystal composition having a high resistivity and other suitable material properties for use in AMDs such as a broad nematic mesophase range with an extremely low transition temperature smectic-nematic and no crystallization at low temperatures. The invention has for its object to provide a liquid-crystal composition with a very high resistivity which meets also the other demands. It has now been found that a nematic liquid-crystal composition based on terminally and laterally fluorinated compounds, characterized in that it contains 15 to 25 % by weight of at least three compounds from group 1: wherein R¹ denotes a straight-chain all group of 5 or more carbon atoms, 15 to 25 % by weight of at least two compounds from group 2: wherein R² denotes a straight-chain alkyl group of 3 to 5 carbon atoms, 5 to 15 % by weight of at least two compounds from group 3: 20 to 30 % by weight of at least four compounds from group 4: 5 to 15 % by weight of at least three compounds from group 5: 5 to 15 % by weight of at least two compounds from group 6: wherein R³ to R⁷ each independently denotes a straight-chain all group of 2 to 5 carbon atoms, and 5 to 15 % by weight of two compounds from group 7: is highly suited for AMD application. Very high RC time values can be obtained in AMDs. These compositions also show a reduced viscosity, allow operation in AMDs in the first minimum of transmission and do not exhibit any crystallization over 1000 hrs at -30 °C. Such compositions preferably contain at least three compounds of group 1 wherein R¹ is n-pently, n-hexyl and n-heptyl. The compounds from groups 1 to 7 are known from the German Patent 26 36 684, the European Patents 0 051 738 and 0 125 563, the International Patent Application in WO 89/02884 and USP 4,302,352, USP 4,710,315 and USP 4,419,264 or can be prepared in analogy to known compounds. The preparation of the compositions according to the invention is effected in the conventional manner. In general, the desired amount of the components which is used in the smaller amount is dissolved in the componentns which constitutes the main constituent, preferably at elevated temperature. If this temperature is chosen to be above the clear point of the main constituent, the completeness of the process of dissolving can be observed particularly easily. However, it is also possible to mix solutions of the components in a suitable organic solvent, for example acetone, chloroform or methanol, and to remove the solvent after thorough mixing, for example by distillation under reduced pressure. It is self-evident that with this method it must be ensured that the solvent does not introduce any contaminants or undesirable dopants. By means of suitable additives the liquid crystal phases according to the invention can be modified in such a way that they can be used in any hitherto disclosed kind of AMD. The examples below serve to illustrate the invention without limiting it. In the examples, the melting point and clear point of a liquid crystal substance are given in degrees Celsius. The percentages are by weight. Example A liquid-crystal composition consisting of 10 % of trans-1-p-fluorophenyl-4-n-pentylcyclohexane, 5 % of trans-1-p-fluorophenyl-4-n-hexylcyclohexane, 4 % of trans-1-p-fluorophenyl-4-n-heptylcyclohexane, 4 % of trans-1-p-n-propylphenyl-4-n-pentylcyclohexane, 4 % of trans-1-p-n-methoxyphenyl-4-n-propylcyclohexane, 6 % of p-[trans-4-(trans-4-ethylcyclohexyl)-cyclohexyl]-trifluoromethoxybenzene 7 % of p-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-trifluoromethoxybenzene 6 % of p-[trans-4-(trans-4-n-butylcyclohexyl)-cyclohexyl]-trifluoromethoxybenzene 7 % of p-[trans-4-(trans-4-n-pentylcyclohexyl)-cyclohexyl]-trifluoromethoxybenzene 9 % of p-[trans-4-(trans-n-propylcyclohexyl)-cyclohexyl]-2-(3,4-difluorophenyl)-ethane, 9 % of p-[trans-4-(trans-n-pentylcyclohexyl)-cyclohexyl]-2-(3,4-difluorophenyl)-ethane, 4 % of p-[trans-4-(trans-n-propylcyclohexyl)-cyclohexyl]-2-(4-trifluoromethoxyphenyl)-ethane, 4 % of p-[trans-4-(trans-n-pentylcyclohexyl)-cyclohexyl]-2-(4-trifluoromethoxyphenyl)-ethane, 6 % of 4'-(trans-4-n-propylcyclohexyl)-3,4-difluorobiphenyl, 5 % of 4'-(trans-4-n-pentylcyclohexyl)-3,4-difluorobiphenyl, 4 % of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 3 % of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl and 3 % of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorophenyl shows a clearing point of 95°, a viscosity at 20° of 16 mPa·s and a birefringence Δn of 0.0910. This composition is nematic at -40°, can be stored at -30° over 1000 hrs without crystallization, shows a high resistivity in the order of 10¹³ Ω·cm or more and is well suited for AMDs.

Claims: A nematic liquid-crystal composition based on terminally and laterally fluorinated compounds, characterized in that it contains 15 to 25 % by weight of at least three compounds from group 1: wherein R¹ denotes a straight-chain alkyl group of 5 or more carbon atoms, 15 to 25 % by weight of at least two compounds from group 2: wherein R² denotes a straight-chain alkyl group of 3 to 5 carbon atoms, 5 to 15 % by weight of at least two compounds from group 3: 20 to 30 % by weight of at least four compounds from group 4: 5 to 15 % by weight of at least three compounds from group 5: 5 to 15 % by weight of at least two compounds from group 6: wherein R³ to R⁷ each independently denotes a straight-chain alkyl group of 2 to 5 carbon atoms, and 5 to 15 % by weight of two compounds from group 7:

Inventors: FUNADA FUMIAKI, KOHZAKI SHUICHI, NAEMURA SHOHEI, NUMATA HIROSHI, OKADA MASAKO, PLACH HERBERT, RIEGER BERNHARD ROOM NO B, SASAKI KEI, FUNADA, FUMIAKI, KOHZAKI, SHUICHI, NAEMURA, SHOHEI, NUMATA, HIROSHI, OKADA, MASAKO, PLACH, HERBERT, RIEGER, BERNHARD, ROOM NO. B511, SASAKI, KEI
Applicants: MERCK PATENT GMBH, SHARP KK, SHARP CORPORATION
Application year: 1990
Main classification: C09K19
IPC codes: G02F1, C09K19