Method of and apparatus for performing a weather resistance test

Abstract: A method of performing a weather resistance test on a composite material (6) having a base member and an organic material covering the base member has the steps of preparing a sample of the composite material, irradiating the sample with light rays including ultraviolet rays from an artificial light source (1), dipping the sample in a corrosive ionized water, and causing dew condensation to form on the surface of the sample. The method further has additional steps for cleaning the surface of the sample and steaming the sample by subjecting the same to an atmosphere having high temperature and high humidity. The cleaning step is effective in removing matter depositing on the surface of the sample and facilitating permeation of the corrosive ionized water into the sample, thus promoting degradation, whilst the steaming step realizes severe hot and humid conditions to make it possible to obtain, in a short time, test results having a high degree of correlation to the natural degradation caused by the weather.

Description: The present invention relates to a method of and an apparatus for performing a weather resistance test. More particularly, the invention is concerned with a method of and apparatus for performing a weather resistance test capable of producing, in a short time test results having close correlation to actual degradation of a composite material having a base member of a metal, an inorganic material or an organic material and a coating layer of an organic material, e.g., a plastic when such a composite material is left in a natural environment including corrosive substances. In general, weather resistance of plastics and materials coated with plastics is tested by a weather resistance testing apparatus as specified by JIS (Japanese Industrial Standards) B 7751 - 7754. Usually, this testing apparatus employs a light source, such as a carbon arc lamp or a xenon lamp, for generating light rays which are applied to the test samples to promote the degradation thereby, thus enabling the test to be finished in a short time. In general, structures in seashore areas are exposed to air which is rich in salt, while offshore structures are held in corrosive conditions due to contact with sea water. Thus, structures on seashores and offshore structures are exposed to severer conditions than structures in an environment which does not contain salty air. Furthermore, in industrial areas where there are many factories, structures are generally under severe environmental conditions as they are often subjected to acid rain. When the material to be tested is a composite material composed of a metallic substrate with a plastic coating, such as that used in structures in coastal areas, on offshore facilities, ships, fishery equipment and in industrial areas, the conventional weather resistant testing apparatus mentioned above cannot perform accelerated testing with good correlation to actual degradation. A composite weather resistance testing apparatus has been known in which a brine spray process is combined with a process simulating ordinary weather conditions such as light irradiation and dew condensation in order to enable evaluation of resistance to a salty environment. A marine exposure promotion testing apparatus is also known in which, as disclosed in Japanese Utility Model Laid-Open No. 55-105153, the tested material is subjected to light irradiation, brine spray and strain. The known composite testing apparatus and marine exposure promotion testing apparatus, however, can provide only a small ultraviolet irradiation intensity, e.g., 6 mW/cm², due to the use of a carbon arc lamp or a xenon lamp as the light source. In addition, the rate of degradation of the tested material is relatively low and the test results do not show close correlation to actual degradation, due to the fact that these tests only include testing processes such as light irradiation, brine spray, dew condensation and the generation of strain. A weather resistance testing apparatus is described in FR-A- 2 600 164 in which a sample of composite material is subjected to an irradiating process where the sample is irradiated with light rays including ultraviolet rays from an artificial light source and a dew condensation process which causes dew condensation to form on the surface of the sample. Another weather resistance testing apparatus is known from IEEE Transactions on Power delivery Vol. PWRD-2, No. 3, July 1987, pages 823-826 in which a sample of material is subjected to a dipping process where the sample is dipped in corrosive ionized water, a cleaning process for cleaning the surface of the sample and a steaming step for subjecting the sample to a high temperature and a high humidity atmosphere. In order to overcome the above-described problems encountered with known weather resistance testing methods and apparatus incorporating a brine environment, the present invention is aimed at providing a method of and an apparatus for performing a weather resistance test which can provide, in a short time, test results of a good correlation to the actual natural degradation under a corrosive environment rich in salt or acid rain. In accordance with a first aspect of the present invention, a method of performing a weather resistance test on a composite material having a base member made of a metallic, inorganic or an organic material and a covering material of an organic material covering the base member is provided, the method having the steps of preparing a sample of the composite material, an irradiating step for irradiating the sample with light rays including ultraviolet rays from an artificial light source, a dipping step for dipping the sample in corrosive ionized water, and a dew condensation step for causing dew condensation on the surface of the sample, being a cleaning step for cleaning the surface of the sample and a steaming step for subjecting the sample to a high temperature and high humidity atmosphere, wherein the cleaning step is executed after the irradiating step and before the step for dipping in corrosive ionized water. The cleaning step removes, from the surface of the test piece, matter which has been formed in the step of irradiation with light source including ultraviolet rays, so as to facilitate execution of a subsequent step, e.g., to facilitate permeation of ionized water such as brine in the dipping step executed subsequent to the light irradiation step, thereby promoting degradation. The steaming step for exposing the test piece to an atmosphere of high temperature and high humidity simulates a hot and humid environment, thus contributing to prompt results with a close correlation to natural degradation. According to another aspect of the present invention, there is provided an apparatus for performing a weather resistance test on a composite material having a metallic, inorganic or an organic base member and an organic material covering the base member, comprising sample holding means for holding a sample of the composite material, irradiating means including an artificial light source for irradiating a surface of the sample with light rays containing ultraviolet rays, dipping means for dipping the sample in corrosive ionized water, dew condensation means including moistening means for causing dew condensation on the surface of the sample, cleaning means for cleaning the surface of the sample, steaming means including heating means and humidifying means for steaming the sample in a high temperature and high humidity atmosphere, and control means for controlling execution of operations of the irradiating means, dipping means, dew condensation means, cleaning means and steaming means in a sequential or predetermined manner, wherein the control means is adapted to control execution of the operation of the cleaning means after the operation of the irradiation means and before the operation of the dipping means. The use of the cleaning means for cleaning the test piece surface and the steaming means for exposing the test piece to an atmosphere of high temperature and high humidity make it possible to provide a weather resistance testing apparatus which is capable of promptly developing test results with high degree of correlation to the actual degradation. By way of example only, a specific embodiment of the present invention will now be described, with reference to the accompanying drawings, in which:- Fig. 1 is a schematic diagrammatic illustration of one embodiment of the weather resistance testing apparatus constructed in accordance with the present invention; Figs. 2 to 7 are graphs showing changes in a colour difference value ΔE* of test samples as observed when the samples were tested by the method of the present invention, conventional methods 1 and 2 and by actual exposure; and Figs. 8 to 13 are graphs showing changes in gloss retention rate of test samples as observed when the samples were tested by the method of the present invention, conventional methods 1 and 2 and by actual exposure. Referring to Fig. 1, the apparatus has a light source 1 which includes a metal halide lamp capable of radiating considerably great energy in a predetermined wavelength region, e.g, 250 to 550 nm, a filter for substantially restricting the wavelength region to 300 to 450 nm, and a water-cooling jacket. The light source 1 is disposed in a reflector which is composed of a dome-shaped collimating main reflector plate 2 and collimating auxiliary reflector plates 3. Numeral 4 denotes a shield plate made of quartz and capable of transmitting ultraviolet rays while hermetically isolating the light source from a sample chamber 5 disposed beneath the light source unit. The sample chamber 5 is inclined at, for example, 15° due to a specific arrangement of a later-mentioned sample holder. The light source unit, which is mounted on the sample chamber 5, is inclined correspondingly. A sample holder 7 in the form of a tray and capable of holding a sample 6 thereon is disposed in the sample chamber 5 for a pivotal movement about an axis near one end thereof. More specifically, the sample holder 7 is adapted to be moved by an actuator 8 so as to pivot between an inclined position where it is held at about 15° inclination with respect to horizontal plane to enable a later-mentioned cleaning agent from a later-mentioned spray nozzle to smoothly flow down without stagnation and a horizontal position where it enables the test sample 6 held thereon to be dipped in ionized water. Temperature control means 7a such as water-cooling means or electronic cooling means are associated with the sample holder 7. An air inlet port 5a and an air outlet port 5b are provided in one of the side walls of the sample chamber 5 so as to project therefrom, and a damper 9 for selectively opening and closing these ports is provided in each of the ports 5a and 5b. A dampening water reservoir 5c is provided at a bottom corner of the sample chamber 5. A humidifying heater 10 is provided around the water reservoir 5c and a heater 11 for heating the interior of the sample chamber 5 is provided on the bottom of the sample chamber 5. The aforementioned spray nozzle 12 for spraying a cleaning agent towards the sample holder 7 is disposed in the sample chamber 5 at a position above the sample holder 7 in the inclined state. A nozzle 13 for supplying ionized water is disposed at a position which is on an obliquely upper side of the sample holder 7 when it is held in a horizontal position. The cleaning agent may be, for example, water, a surface active agent, water containing air, alcohol or the like. The ionized water may be, for example, an aqueous solution of one or more of NaCl, MgCl₂, H₂SO₄ and NaOH, or a mixture of one or more of such aqueous solutions and natural sea water. A temperature controlling blower 14 is capable of supplying air into the sample chamber 5 through the air inlet port 5a so as to maintain a predetermined temperature of the sample 6 on the sample holder 7. The cleaning agent spray nozzle 12 is connected through a pipe having a solenoid valve 15 to a cleaning agent supply port 16. The ionized water nozzle 13 is connected to an ionized water tank 18 via an ionized water pump 17. The ionized water tank 18 is provided with a heater 19 for maintaining the temperature of the ionized water at a predetermined level. The water reservoir 5c provided at the bottom corner of the sample chamber 5 is conected to a draining port through a draining solenoid valve 20. The light source 1, temperature control blower 14, automatic damper 9, cleaning agent solenoid valve 15, ionized water pump 17, draining solenoid valve 20 and heaters 10, 11 and 19 are controlled by a controller 21. A description will be given of an example of the weather resistance testing method of the invention which is carried out by using the weather resistance testing apparatus having the described construction. The sample 6 held on the sample holder 7 is subjected to ultraviolet irradiation of an intensity of 50 to 80 mW/cm² caused by the activation of the light source 1 for a predetermined period, e.g., 6 to 18 hours, while being held in an atmosphere of a relative humidity of 20 to 80%, e.g, 30%, and maintained at a constant temperature, e.g., 40°C ± 1.0°C to 100°C ± 1.0°C, by the air from the blower 14. The light source 1 is then turned off to terminate the ultraviolet irradiation and the solenoid valve 15 is operated to supply an ion-exchange water of 20 to 80°C, e.g., 60°C so that the ion exchange water is sprayed from the spray nozzle 12 for 30 seconds, thereby removing matters depositing on the surface of the sample. This cleaning step facilitates permeation of an ionized water such as brine into the sample in the subsequent step. Then, the actuator 8 is operated to set the sample holder 7 in the horizontal position and the ionized water pump 17 starts to operate so that ionized water in the ionized water tank 18, e.g., a 5% aqueous solution of NaCl (pH 6.5 to 7.5) at 40°C, is supplied to the tray-type sample holder 7 from the spray nozzle 13, whereby the sample 6 is dipped in the ionized water for 10 seconds. Subsequently, the actuator 8 operates again to incline the sample holder 7 so as to allow the ionized water to drain from the sample holder 7 and then the draining solenoid valve 20 operates to discharge the water. Then, the blower 14 operates again to supply dried air so as to dry the sample at a drying rate of 1 to 5°C/min for 30 minutes. The humidifying heater 10 is then controlled to maintain a relative humidity of 95% within the sample chamber. Meanwhile, ion exchange water for cleaning is supplied to the portion around the humidifying heater in the sample chamber. In addition, temperature control means 7a operates in accordance with a signal from a temperature sensor 22 on the sample holder 7, so as to lower the temperature of the sample holder 7 down to a predetermined temperature below the dew point, e.g., down below about 30°C, so that dew condensation takes place on the surface of the sample 6 held by the sample holder 7, whereby a heat shock is applied to the sample 6. The sample 6 is held under this dewing condition for a predetermined time, e.g., 1 hour, and, therafter, the sample holder 7 is set to a horizongal position. The ionized water pump 17 is then operated to supply ionized water again from the ionized water nozzle 13 so as to dip the sample 6 in the ionized water for 10 seconds. The sample holder 7 is then inclined again. The application of heat shock and the subsequent dipping in the ionized water greatly promote corrosion. Then, after the sample 6 is dried, the humidifying heater 10 and the sample chamber heater 11 are controlled to created a highly humid and hot environment, e.g., 95% relative humidity at 50°C, in the sample chamber 5, and the sample 6 is exposed to this humid and hot atmosphere for 12 hours. The sample 6 is heated and moistened as a result of execution of this steaming step. The ultraviolet irradiation is then conducted again following the execution of the steaming step. In this step, ultraviolet rays of high intensity are applied to the surface of the sample which is in a steamed state, so that a very severe conditon is realized to further promote degradation. These steps are then executed repeatedly and cyclically. The described method of executing weather resistance test imparts to the samples conditions which closely approximate natural conditions in the seashore areas or offshore areas and can provide, in a short time, weather resistance test results with close correlation to the natural degradation, by virtue of addition of the cleaning and steaming steps. In the described embodiment, the steaming step for exposing the sample to an atmosphere of high temperature and high humidity is executed between the ionized-water dipping step and ultraviolet irradiation step. This, however, is not exclusive and similar effects are obtainable when the steaming step is executed, for example, after the cleaning step or before or after the dew condensation step. In the described embodiment, only one spray nozzle for spraying the cleaning agent is provided above the sample. The number and positions of the spray nozzle or nozzles, however, may be freely determined in accordance with factors such as the shape and size of the sample holder. The ionized water dipping step in the described method is executed by dipping the sample in the ionized water by filling the tray-type sample holder. This, however, is only illustrative and the dipping may be effected by spraying the ionized water onto the sample held on the sample holder in the inclined state as in the case of cleaning, or by immersing for a predetermined time the sample holder, together with the sample, in a bath of the ionized water contained in a separate ionized water tank and then lifting the sample holder. By using an acidic solution such as of H₂SO₄ as the ionized water, it is possible to evaluate the resistance to acid rain. Tests were conducted in accordance with the weather resistance testing method of the invention and also by conventional weather resistance testing methods and by actual exposure, in order to confirm the effects brought about by the invention, with the following results; (1) Conditions of Testing Method According to Invention Light source: metal halide lamp 4 kW Irradiation light wavelength: 300 to 450 nm Black panel temperature (when irradiated with ultraviolet rays): 63°C ± 3°C Ultraviolet rays intensity on sample surface: 80 ± 5 mW/cm² Ultraviolet irradiation time: 6 hours Cleaning period: 30 seconds (after completion of ultraviolet ray irradiation) Cleaning agent: Ion exchange water Cleaning agent temperature: 60°C Rate of spray of cleaning agent: 9 cc per 1 cm² of sample surface Pressure of spray of cleaning agent: 1.5 kg/cm² Ionized water: 5% NaCl solution Ionized-water dipping period: 10 seconds Ionized water temperature: 40°C Drying period: 30 minutes Drying rate: 1 to 5°C/min Sample chamber air humidity at dewing: 95% Relative Humidity Sample temperature at dewing: 30°C Dewing period: 6 hours Sample chamber air temperature at steaming: 50°C Sample chamber air humidity at steaming: 95% Relative Humidity Steaming period: 11.5 hours (2) Conditions of Actual Exposure Test Period: 3 years (as from March 26, 1985) Place: A facility for general research of marine technology, Ministry of Construction (Suruga Bay, Japan) (3) Conditions of Conventional Testing Method 1 (With Sunshine weather meter) Light source: Sunshine carbon arc lamp Irradiation light wavelength: 280 to 1400 nm Black panel temperature: 63°C ± 3°C Ultraviolet rays intensity on sample surface: 5 mW/cm² Water spray: 18 minutes within 2 hours (4) Conditions of Conventional Testing Method 2 (brine spray test according to JIS-Z 2371) NaCl solution: 5 ± 1% Test room temperature: 35 ± 1°C Brine tank temperature: 35 ± 1°C Continuous spray The following six types of coated plates (a) to (f) were used as the test samples: (a) Vinyl chloride laminate galvanized steel sheet (laminate layer thickness: 200 µm) (b) Galvanized steel sheet coated with vinyl chloride sol (coating layer thickness: 300 µm) (c) 55%Al-Zn-plated steel sheet coated with vinyl chloride sol (coating layer thickness : 200 µm) (d) Galvanized steel sheet coated with fluororesin (coating layer thickness: 30 µm) (e) Fluororesin laminate galvanized steel sheet (laminate layer thickness: 38 µm) (f) Galvanized steel sheet coated with polyester (coating layer thickness: 18 µm) These samples were tested by the testing methods shown above, and the color difference ΔE* in terms of a CIE1976L*, a*, b* space colorimetric system and gloss retention rate were measured on these tested samples, the results being shown in Figs. 2 to 13. The color difference ΔE* is the measured value of a change in hue of one side of each sample, while the gloss retention rate was obtained in accordance with the following formula, on the basis of the change in the 60° mirror surface reflectivity as measured by a gloss meter on each sample: Gloss retention rate = {(gloss after test)/(initial gloss)} x 100 (%) The same tests were also executed on the same samples with scratches formed on these samples so as to reach the underlying metallic layers, for the purpose of evaluation of corrosion and change in the coating layers on these samples, the results being shown in Tables 1 and 2. In case of the actual exposure test, however, no scratch was formed and results of observation of cut sections are shown in these tables. The curves a₁, a₂, a₃ and a₄ shown in Fig. 2 represent the changes in the color difference ΔE* on the vinyl chloride laminate galvanized steel sheet tested by the actual exposure, testing method of the invention and conventional testing methods 1 and 2, respectively. In case of the actual exposure test, the ΔE* value showed a rapid rise up to 5 or higher in 18 months after the commencement of the test, and is then substantially saturated as will be seen from the curve a₁. The weather resistance testing method of the present invention showed a tendency substantially the same as that in the actual exposure test as shown by the curve a₂. It was confirmed that the ΔE* value equivalent to that obtained in 18 months in the actual exposure can be attained in quite a short time of 300 hours when the testing method of the invention is used. On the other hand, in the case of the conventional testing method 2, no substantial change was observed in the ΔE* value. In the conventional testing method 1 also, the change in the ΔE* value obtained in 1500 hours after the commencement of the test was as small as that obtained in 200 hours in the testing method of the invention. The curves b₁, b₂, b₃ and b₄ shown in Fig. 3 and the curves c₁, c₂, c₃ and c₄ shown in Fig. 4 represent the changes in the color difference ΔE* on the samples of the galvanized steel sheet coated with vinyl chloride sol and Al-Zn-plated steel sheet coated with vinyl chloride sol, respectively, tested by the actual exposure, testing method of the invention and conventional testing methods 1 and 2, respectively. In case of the actual exposure test, the ΔE* value showed a rapid rise in 12 months after the commencement of the test, and is then substantially saturated in both types of samples, as will be seen from the curves b₁ and c₁. The weather resistance testing method of the present invention showed tendencies substantially the same as that in the actual exposure test as shown by the curves b₂ and c₂. Namely, the ΔE* value rapidly increased in 300 hours after the commencement of the test and then saturated. Furthermore, the ΔE* values attained in 200 hours of the test by the testing method of the invention well coincided with those obtained in 12 months in the actual exposure test, thus proving a specifically high degree of closeness of correlation therebetween. It will also be understood that the conventional testing methods 1 and 2 could not provide changes in the ΔE* values equivalent to those of the actual exposure test and the testing method of the invention, despite prolonged testing periods. The curves d₁, d₂, d₃ and d₄ shown in Fig. 5, curves e₁, e₂, e₃ and e₄ shown in Fig. 6, and the curves f₁, f₂, f₃ and f₄ shown in Fig. 7 represent the changes in the color difference ΔE* on the samples of the galvanized steel sheet coated with fluororesin, the fluororesin laminate galvanized steel sheet and galvanized steel sheet coated with polyester, respectively, as tested by actual exposure, the testing method of the invention and conventional testing methods 1 and 2, respectively. These samples showed smaller values of change in the color difference ΔE* than the samples employed in the preceding tests. Nevertheless, the testing method of the invention provided results with close correlation to the results of the actual exposure test. In Fig. 8, the curves a₁, a₂, a₃ and a₄ show the results of measurement in the changes of the gloss retention rate as obtained when samples of vinyl chloride laminate galvanized steel sheet were tested by actual exposure, the testing method of the invention, and the conventional testing methods 1 and 2. As will be seen from the curves a₁ and a₂, the samples tested by the actual exposure and the testing method of the invention showed substantially constant values of gloss retention rate, thus proving a high degree of correlation therebetween. On the other hand, the sample tested by the conventional testing method 1 showed a significant reduction in the gloss retention rate in relation to time, unlike the result of the actual exposure test, as will be seen from the curve a₃. In Fig. 9, the curves b₁, b₂, b₃ and b₄ show the results of measurement of changes in the gloss retention rate as obtained when samples of galvanized steel sheet coated with vinyl chloride sol were tested by the actual exposure, testing method of the invention, and the conventional testing methods 1 and 2. The sample tested by the actual exposure showed a rapid decrease in the gloss retention rate in 12 months after the commencement of the test and, thereafter, a substantially constant value of the gloss retention rate, as will be seen from the curve b₁. On the other hand, the sample tested by the testing method of the invention initially showed a gentle reduction in the gloss retention rate but the rate started to rapidly decrease about 200 hours after the start of the test and reached, in 400 hours after the start of the test, the value which is substantially the same as that reached in 24 months in the actual exposure test. In contrast, the test according to the conventional testing method 2 showed no significant change in the gloss retention rate, while the conventional method 1 caused an occasional rise in the gloss retention rate followed by a reduction. The change observed in the conventional method 1, however, much less significant than the result of the test according to the testing method of the present invention. Figs. 10,11 and 12 show the changes in the gloss retention rate as observed with samples of Al-Zn-plated steel sheet coated with vinyl chloride sol, galvanized steel sheet coated with fluororesin and the fluororesin laminate galvanized steel sheet, respectively, when these samples were tested by the actual exposure, testing method of the invention and the conventional testing methods 1 and 2, respectively. In the case of the actual exposure test, all the samples showed small values of changes in the gloss retention rate as shown by the curves c₁, d₁ and e₁. The results of the test by the testing method of the invention also showed small changes in the gloss retention rate as shown by curves c₂, d₂ and e₂, thus proving high degree of correlation to the actual exposure test. In contrast, the results of the test conducted in accordance with the conventional testing method 1 showed a large reduction in the gloss retention rate particularly in the case of the sample of the Al-Zn-plated steel sheet with vinyl chloride sol, as will be seen from the curve c₃, thus exhibiting a significant difference from the results of the actual exposure test. Fig. 13 shows the changes in the gloss retention rates exhibited by the samples of the galvanized steel sheets coated with polyester as observed when these samples were tested by the actual exposure, the testing method of the invention and the conventional testing methods 1 and 2. As shown by the curve f₁, the sample tested by the actual exposure showed a rapid reduction in the gloss retention rate in the period of 24 months after the commencement of the test and thereafter no significant change was observed. The sample tested by the testing method of the present invention showed a similar tendency: namely, a rapid reduction in the gloss retention rate was observed when 200 hours has elapsed after the start of the test, as shown by the curve f₂. The conventional testing method 1 also showed a drastic decrease in the gloss retention rate after elapse of 200 hours from the start of the test, as shown by the curve f₃. This, however, seems to be attributable to the presence of light rays of wavelengths of 300 nm or less in the lights from the light source. As stated before, each of the same samples (a) to (f) used in the tests described hereinbefore was tested by the same testing methods after forming scratches reaching the underlying metallic layer, and the state of corrosion in the scratched portion was observed to obtain the result as shown in Table 1. The sample used in the actual exposure test, however, had no scratch, and the state of corrosion was observed at a cut sectional surface of the sample and compared with the results of other testing methods on a assumption that the corrosion state at the cut cross-section is substantially the same as that shown by scratched portions of the samples. Samples Method of Invention Actual Exposure Conventional Method 1 Conventional Method 2 a white rust white rust red rust black rust heavy white rust b white rust red rust red rust slight white rust heavy white rust c red rust white rust red rust no rust slight black rust d white rust white rust red rust white rust slight white rust e slight white rust white rust red rust slight white rust slight white rust f white rust red rust white rust red rust slight white rust white rust red rust The states of corrosion shown in Table 1 are those obtained 432 hours after the start of the test in case of the method of the invention, 30 months after the start of the test in case of the actual exposure test, 1500 hours after the start of the test in case of the conventional method 1 and 450 hours after the start of the test in case of the conventional method 2, respectively. Table 2 shows the states of the coating layers around the scratched portions of the samples (cut surface in case of actual exposure test) as observed after expiration of the same testing periods as those explained in connection with the test results shown in Table 1. Samples Method of Invention Actual Exposure Conventional Method 1 Conventional Method 2 a end swell no change slight end swell no change b end swell no change no change no change c no change no change end swell no change d end swell end swell slight end swell no change e end swell end swell no change no change f end swell end swell end swell no change As will be seen from Table 1, the weather resistance testing method of the present invention can realize, in quite a short time of about 400 hours, a state of corrosion equivalent to that obtained in 30 months of actual exposure. Thus, the method of the invention can promote the degradation also in the aspect of corrosion. Referring now to Table 2, the weather resistance testing method of the present invention can develop a degradation which is equivalent to or heavier than that obtained in 30 months of the actual exposure, thus proving the possibility of promoting the degradation also in the aspect of the state of the coating layer. As will be understood from the results of tests described hereinbefore, the weather resistance testing method of the present invention can realize, in quite a short time, a degradation of a degree which very closely approximates that of the degradation caused by a long period of actual exposure, thus proving high degree of correlation between the test results and the natural degradation. The embodiment described hereinbefore incorporated, as the light source unit, a combination of a metal halide lamp of wavelength ranging between 250 and 550 nm and a filter for restricting the wavelength substantially to a range of 300 to 450 nm, the light source unit illuminating the sample surface at an ultraviolet intensity of 80 ± 5 mW/cm². This, however, is only illustrative and the invention can be carried out with different types of light source unit such as an artificial light source including ultraviolet rays of an intensity not lower than several tens of mW/cm² together with visible or infrared rays. The advantages of the invention described before can be obtained even when such an alternative light source is used.

Claims: A method of performing a weather resistance test on a composite material having a base member made of a metallic inorganic or an organic material and a covering material of an organic material covering the base member, the method having the steps of irradiating a sample (6) of the composite material with light rays including ultraviolet rays from an artificial light source (1) and a dew condensation step for causing dew condensation on the surface of the sample (6) characterised in that the method further includes the steps of preparing the sample (6), a dipping step for dipping the sample (6) in corrosive ionized water, a cleaning step for cleaning the surface of the sample (6) and a steaming step for subjecting the sample (6) to a high temperature and high humidity atmosphere wherein the cleaning step is executed after the irradiating step and before the step for dipping in corrosive ionized water. A method according to claim 1, wherein said steaming step is executed after said dipping step and before said irradiating step. A method according to claim 1, wherein said steaming step is executed after said cleaning step and before said dipping step. A method according to claim 1, wherein said steaming step is executed after said dipping step and before said dew condensation step. A method according to claim 1, wherein said steaming step is executed after said dew condensation step and before said dipping step. An apparatus for performing a weather resistance test on a composite material having a metallic, inorganic or an organic base member and an organic material covering said base member, comprising sample holding means (7) for holding a sample (6)of said composite material, irradiating means (1) including an artificial light source (1) for irradiating a surface of said sample (6) with light rays containing ultraviolet rays and dew condensation means (7a) including moistening means for causing dew condensation on said surface of said sample (6) characterised in that the apparatus further comprises dipping means (8) for dipping said sample (6) in corrosive ionized water, cleaning means (12,15,16) for cleaning said surface of said sample (6), steaming means (5c,10,11) including heating means (11) and humidifying means (5c,10) for steaming said sample (6) in a high temperature and high humidity atmosphere, and control means (21) for controlling execution of operations of said irradiating means (1), dipping means (8), dew condensation means, cleaning means and steaming means in a sequential or predetermined manner, wherein the control means is adapted to control execution of the operation of the cleaning means after operation of the irradiation means and before operation of the dipping means. An apparatus according to claim 6, wherein said sample holding means (7) comprises a tray-type sample holder which is pivotally supported at one end for a pivoting movement between an inclined position for enabling execution of said cleaning step and a horizontal position for enabling execution of said dipping step.

Inventors: GOTO HITOSHI, IWANAGA TERUO, KISHIMA YOSHIO, TOMIITA TAKASHI, GOTO, HITOSHI, IWANAGA, TERUO, KISHIMA, YOSHIO, TOMIITA, TAKASHI, GOTO, HITOSHI, C/O DEVELOPING CENTER, IWANAGA, TERUO, C/O DEVELOPING CENTER, KISHIMA, YOSHIO, C/O DAINIPPON PLASTICS CO., LTD.
Applicants: BUILDING RESEARCH INST MINISTR, DAINIPPON PLASTICS, IWASAKI ELECTRIC CO LTD, BUILDING RESEARCH INSTITUTE, MINISTRY OF CONSTRUCTION, DAINIPPON PLASTICS CO., LTD., IWASAKI ELECTRIC CO., LTD.
Application year: 1990
Main classification: G01N17
IPC codes: G01N17