Liquid crystal device

Abstract: The present invention provides a liquid crystal material disposed between said pair of substrates, wherein at least one of said substrates is provided with a film comprising a polyimide compound having in its polyimide main-chain structural unit at least one alkyl side chain containing an alkyl chain moiety having a length of 2 to 10 carbon atoms.

Description: The present invention relates to a liquid crystal device, in particular, a ferroelectric liquid crystal device, used in a liquid crystal display device or a liquid crystal optical shutter. More particularly, the present invention is concerned with a liquid crystal device having achieved an improvement of display characteristics because of an improvement of the state of liquid crystal molecular alignment. Clark and Lagerwall have proposed a display device of the type in which the refractive index anisotropy of ferroelectric liquid crystal molecules is utilized and transmitted light rays are controlled by its combination with a polarizer (see Japanese Patent Laid-Open Gazette No. 56-107216 and U.S. Patent No. 4,367,924). This ferroelectric liquid crystal commonly has a chiral smectic C phase (Sm*C) or H phase (Sm*H) of non-spiral structure in a specific temperature range, and, under such a state, has the properties of assuming either a first optically stable state or a second optically stable state in response to an electric field applied and also maintaining that state when no electric field is applied, in other words, the bistable state (or two stable states). This ferroelectric liquid crystal also has a quick response to changes in electric fields, and is expected to be widely utilized as a display device of a high-speed and memory type. In particular, in view of its function, it is expected to be applicable as a display device with a large screen and high detail. In order for an optical modulation device applying such a bistable liquid crystal to exhibit desired drive characteristics, a liquid crystal disposed between a pair of parallel substrates is required to be in the state of molecular orientation that the conversion between the above two stable states may effectively take place, independently of an applied state of electric field. In the case of a liquid crystal device in which the double refraction of a liquid crystal is utilized, the transmittance under crossed nicols is expressed by: I/I₀ = sin² 4ϑ sin² Δnd λ π wherein I₀: incident light intensity, I: transmitted light intensity, ϑ: tilt angle Δn: refractive index anisotropy d: film thickness of a liquid crystal layer, λ: wavelength of incident light. Thus, the tilt angle ϑ in the above non-spiral structure is present as an angle in the direction of an average molecular axis of a liquid crystal molecule twistingly oriented in the first and second states of alignment. According to the above expression, the transmittance reaches a maximum when the tilt angle ϑ is an angle of 22.5°, and hence a tilt angle ϑ in the non-spiral structure realizes the bistable state is required to be as near as possible to 22.5°. Incidentally, as a method of aligning ferroelectric liquid crystal, it is desirable to use a method by which a molecular layer formed of a plurality of molecules that form a smectic liquid crystal can be monoaxially aligned along its normal and yet the manufacturing process can be carried out by a simple aligning treatment. The method as disclosed, for example, in U.S. Patent No. 4,561,726 is known as a method of aligning a ferroelectric liquid crystal, in particular, a chiral smectic liquid crystal of non-spiral structure. However, in instances in which alignment methods hitherto used, in particular, alignment methods using a polyimide film having been subjected to rubbing are applied to the above bistable ferroelectric liquid crystal of non-spiral structure as reported by Clark and Lagerwall, there are the following problems. Experiments made by the present inventors revealed that a tilt angle (the angle shown in Fig. 3 as described later) in a ferroelectric liquid crystal of non-spiral structure obtained by making alignment using the conventional polyimide film having been subjected to rubbing becomes smaller than a tilt angle (the angle Θ of 1/2 of a vertical angle of a trigonal pyramid shown in Fig. 2, as described later) in a ferroelectric liquid crystal of spiral structure. In particular, the tilt angle ϑ in a ferroelectric liquid crystal of non-spiral structure obtained by making alignment using the conventional polyimide film having been subjected to rubbing was approximately 3° to 8° in general, and the transmittance at that time was approximately 3 to 5 % at best. Thus, according to Clark and Lagerwall, the tilt angle in a ferroelectric liquid crystal of non-spiral structure that realizes the bistable state should be the same angle as the tilt angle in a ferroelectric liquid crystal of spiral structure. In practice, however, the tilt angle ϑ in the non-spiral structure is smaller than the tilt angle Θ in the spiral structure. It was also revealed that the reason why the tilt angle ϑ in the non-spiral structure is smaller than the tilt angle Θ in the spiral structure is ascribable to the twisted orientation of liquid crystal molecules in the non-spiral structure. More specifically, in the ferroelectric liquid crystal of non-spiral structure, liquid crystal molecules are twistingly oriented in a continuous form at a twist angle δ, which is twisted from an axis of a liquid crystal molecule adjacent to an upper substrate toward an axis of a liquid crystal molecule adjacent to a lower substrate (i.e., in the direction of twisted orientation), with respect to the normal of each substrate. This is the reason why the tilt angle ϑ in the non-spiral structure becomes smaller than the tilt angle Θ in the spiral structure. In the instance where a chiral smectic liquid crystal is aligned using a conventional polyimide alignment film having been subjected to rubbing, the polyimide alignment film is present as an insulating layer between an electrode and a liquid crystal layer. Hence, when a voltage with one polarity is applied so that the first optical stable state (for example, a state of the display in white) is switched to the second optical stable state (for example, a state of the display in black), a reverse electric field V rev with the other polarity is produced in a ferroelectric liquid crystal layer after removal of the application of this voltage with one polarity, and this reverse electric field V rev has often caused an after-image at the time of display. The above phenomenon of producing a reverse electric field is elucidated in Yoshida Akio, "Switching Characteristics of SSFLC", A Collection of Drafts for Liquid Crystal Forum, p.142-143, October, 1987. Accordingly, an object of the present invention is to provide a liquid crystal device that has solved the above problems, in particular, to provide a ferroelectric liquid crystal device that can produce a large tilt angle ϑ in the non-spiral structure of a chiral smectic liquid crystal, enables display of an image with a high contrast, and can achieve display causing no after-image. According to the present invention a liquid crystal device is provided, said device comprising a pair of substrates and a liquid crystal material disposed between said pair of substrates, wherein at least one of said substrates is provided with a film comprising a polyimide compound having in its polyimide main-chain structural unit at least one alkyl side chain containing an alkyl chain moiety having a length of 3 to 10 carbon atoms. The alkyl side chain is preferably a straight-alkyl chain. Fig. 1 is a cross-sectional illustration of a liquid crystal device. Fig. 2 is a perspective illustration of a state of alignment of a chiral smectic liquid crystal of spiral structure, and Fig. 3 is perspective illustration of a state of alignment of a chiral smectic liquid crystal of non-spiral structure. Fig. 4A is a cross-sectional illustration of a state of alignment of a chiral smectic liquid crystal according to the present invention, Fig. 4B illustrates C-directors of its two stable states of uniform alignment, and Fig. 4C illustrates C-directors of two stabel states of spray alignment. Fig. 5A is a plan to illustrate a tilt angle ϑ in the state of uniform alignment, and Fig. 5B is a plan to illustrate a tilt angle ϑ in the state of spray alignment. Figs. 6A, 6B and 6C are cross-sectional illustrations of the distribution of electric charges in a ferroelectric liquid crystal, the direction of spontaneous polarization P s , and the direction of a reverse electric field V rev , respectively. Fig. 7 is a plan to illustrate changes of the tilt angle ϑ at the time of application of an electric field and after that time. Fig. 8 illustrates optical response characteristics in an example of the prior art, and Fig. 9 illustrates optical response characteristics in an example of the device accord to the present invention. Fig. 10 illustrates wave forms of a drive voltage used in Examples of the present invention. Fig. 11 illustrates a method of forming an aligning film provided with the device of the present invention by the LB process. Fig. 1 diagramatically illustrates a ferroelectric liquid crystal cell. The numerals 11a and 11b denote substrates (glass plates) covered with transparent electrodes 12a and 12b made of In₂O₃ or ITO (indium-tin oxide), respectively. Insulating films 13a and 13b (SiO₂ films, TiO₂ films, Ta₂O₅ films or the like) and alignment control films 14a and 14b formed using the polyimide of the present invention are laminated thereon, respectively. A liquid crystal 15 is disposed between the substrates 11a and 11b. The distance between the substrates 11a and 11b is set to be a distance (for example, 0.1 µm to 3 µm) small enough to control the formation of a spiral structure in the case when the liquid crystal 15 is a ferroelectric smectic liquid crystal. In that case, the alignment of the liquid crystal 15 has a bistability. The above distance small enough is retained using a beads spacer 16 (e.g., silica beads, alumina beads) disposed between the substrates 11a and 11b. Polyimide films used in the present invention as the above alignment control films 14a and 14b can be obtained by forming a polyamide acid, synthesized by condensation reaction of a carboxylic anhydride with a diamine, into films by coating or the LB process, followed by imidation. An alkyl-substituted carboxylic anhydride and a diamine which are used in the present invention include, for example, the following: - Diamines - - Carboxylic anhydrides - In the foregoing, m and n each represent an integer of 0 to 3; R is selected from the group consisting of: normal-C ℓ H 2ℓ+1 -, ℓ = an integer of 3 to 10; normal-C ℓ H 2ℓ+1 CO-, ℓ = an integer of 3 to 10; normal-C ℓ H 2ℓ+1 O-, ℓ = an integer of 3 to 10; normal CF₃(CI₂) k (CH₂) ℓ -, ℓ+k = an integer of 2 to 10 and k = 2, 3 or 5; normal CF₃(CI₂) k (CH₂) ℓ CO-, ℓ+k = an integer of 2 to 10 and k = 2, 3 or 5; (CF₃)₂CF(CH₂) ℓ -, ℓ = an integer of 0, 1 to 8; or (CF₃)₂CF(CH₂) ℓ CO-, ℓ = an integer of 0, 1 to 8. And R can be combined with different two or more kinds of the group above. In the present invention, it is possible to use two or more kinds of the above R-substituted diamine and/or two or more kinds of the carboxylic acid anhydride. Alternatively, it is also possible to use a polyamide acid synthesised by condensation reaction of the above R-substituted diamine or carboxylic anhydride with a conventionally known carboxylic anhydride or unsubstituted diamine. These can be used in the form of a copolymer comprised of various combinations. The polyimide film used in the present invention can be provide on a substrate in the following method: First, the polyamide acid, which is a precursor of a polyimide, and a long-chain alkylamine are mixed in a solvent such as dimehtylformamide, dimethylacetamide, dimethyl sulfoxide or N-methylpyrrolidone, in a molar ratio of 1:2 to form a 0.1 to 1.0 mM solution (monomer units). The resulting solution is spread on an interface between air and water, and a film is built up on the substrate by a conventionally known LB process. Thereafter, the built-up film is heated to a temperature of from 100 to 350°C, and preferably from 200 to 300°C, to effect dehydration, cyclization and removal of amines. A polyimide film can be thus formed. This LB polyimide film can obtain uniform monoaxial aligning properties without rubbing treatment, and thus the LB process is suitable as a method of forming an alignment film. For the purpose of achieving the object of the present invention, the film formation method is by no means limited to the above LB process. A film formed by conventionally known spin coating, spray coating or roll coating, which is then subjected to rubbing treatment using a cloth or the like, can also exhibit a superior performance as an alignment film. The rubbing may preferably be carried out in the direction A as shown in Fig. 1 so as to be in the same directions for the upper and lower substrates. The polyimide film used in the present invention may be formed to have a film thickness of from about 1 nm (10 Å) to about 1 µm, preferably from 3 nm (30 Å) to 200 nm (2,000 Å), and more preferably from 3 nm (30 Å) to 30 nm (300 Å). Use of the insulating films 13a and 13b shown in Fig. 1 may be omitted. In the present invention, in the case when the polyimide films are provided on the insulating films 13a and 13b (each preferably having a film thickness of from 20 nm (200 Å) to 100 nm (1,000 Å), such polyimide aligning films may be formed to each have a film thickness of not more than 20 nm (200 Å), and preferably not more than 10 nm (100 Å). In order to form the polyimide alignment film of the present invention by the use of the above LB process, a precursor polyamide acid is spread over a water surface. At this time, the hydrophobic part and hydrophilic part must be introduced into the molecule. This can be achieved by mixing a long-chain alkylamine to form an amine salt on a carboxyl group of the polyamide acid. More specifically, quaternizing the nitrogen of a long-chain alkylamine brings about the introduction of the hydrophilic part, and a long-chain alkyl moiety is attributable to the introduction of the hydrophobic part. The long-chain alkyl amine that can be used includes primary amines such as n-hexadecylamine, n-octadecylamine and n-docosylamine, secondary amines such as di-n-decylamine, di-n-dodecylamine and di-n-tetradecylamine, and tertiary amines such as N,N-dimethyl-n-hexadecylamine, N,N-dimethyl-n-octadecylamine, N-methyl-di-n-decylamine, N-methyl-din-dodecylamine, N-methyl-di-n-tetradecylamine, tri-n-nonylamine, tri-n-decylamine and tri-n-dodecylamine. These may be mixed in such a ratio that may form all carboxyl groups of the polyamide acid into amine salts. More specifically, there are usually two carboxyl groups per repeating unit of a polyamide acid, and in such an instance the molar ratio of repeating units of the polyamide acid to an amine may preferably be 1:2 to 1:3, and more preferably from 1:2 to 1:2.5. As a solvent used here, N,N-dimethylacetamide is preferred, but any solvents may be used so long as they can well dissolve the polyamide acid and make the resulting solution to be readily spread over a water surface. There are no particular limitations on the concentration of the polyamide acid. From the viewpoint of spreadability, it may preferably be in a concentration ranging from 1 x 10⁻⁷ to 1 x 10⁻⁵ M for the repeating unit of a polyimide acid. A polyamide acid amine salt solution prepared in this way is gently spread over an aqueous phase. Here, pure water of 5 to 20°C is commonly used as the aqueous phase. Its pH may be adjusted by adding every sort of metal ions or adding an alkali. Next, the polyamide acid amine salt thus spread over the water surface is compressed to form a monomolecular film of the polyamide acid amine salt. The surface pressure for this compression depends on the types of the polyamide or acid amine salt used. It may be approximately in the range of from 5 to 35 mN/m. To the monomolecular film on the water surface, thus prepared, the liquid crystal cell substrate previously described may be immersed and then drawn up in the direction crossing the monomolecular film on the water surface while the surface pressure is kept constant, so that two layers of monomolecular films can be built up on the substrate. The rate at which the substrate is immersed and drawn up here depends on the types of the polyamide acid amine salt. It may be approximately from 3 to 50 mm/min. Such an operation may be repeated, whereby a built-up film of monomolecular films comprising the polyamide acid amine salt can be obtained in the desired layers. In order to obtain a single layer film, two methods can be used. One of them is a method in which a substrate is previously kept immersed in an aqueous phase, thereafter a monomolecular film is formed on a water surface, and this monomolecular film is transferred to the substrate through a drawing-up step. The other of them is a method in which a monomolecular film is formed on the water surface, then a substrate is immersed in it so that the monomolecular film is transferred to the substrate, thereafter the monomolecular film on the water surface is removed, and the substrate on which a single layer film has been formed is drawn up. From the viewpoint of the stability of the film transferred to the substrate, it is desirable to use the former method. The monomolecular film or a built-up film of monomolecular films comprising the polyamide acidamine salt, formed on the substrate in this way, may be heated to carry out a dehydration and cyclization (imidization) reaction and an deamination reaction. The desired polyimide film can be thus obtained. Baking, carried out here, should preferably be carried out at 150°C to 300°C 10 to 60 minutes in approximation, and in a nitrogen atmosphere or under reduced pressure. In regard to the direction in which the substrate is drawn up, the films should preferably be so formed as to be in the same direction (for example, the direction A shown in Fig. 1) between the upper and lower substrates when a cell has been made up. As previously described, in the lower layer of the polyimide monomolecular film or the built-up film of polyimide monomolecular films, coating methods hitherto widely used may be used to form a polyimide film. In order to provide such a polyimide film on the substrate, a polyamide acid, which is a precursor of the polyimide, may be dissolved in a solvent such as N,N-dimethylformamide, N,N-dimethylacetamide, N,N-dimethyl sulfoxide or N-methylpyrrolidone to form a 0.01 to 40 wt.% solution, and the resulting solution may be coated on a substrate by spin coating, spray coating or roll coating, followed by heating at a temperature of from 100 to 350°C, and preferably from 200 to 300°C, to carry out dehydration and cyclization(imidation). The desired polyimide film can be thus formed. The polyimide film formed by such coating methods may preferably have a film thickness of from about 3 nm (30 Å) to about 200 nm (2,000 Å), and more preferably from 3 nm to 30 nm. Use of the insulating layers 13a and 13b as shown in Fig. 1 can be omitted. Liquid crystal materials used in the present invention may preferably be liquid crystals that produce a chiral smectic phase through an isotropic phase, a cholesteric phase, and a smectic A phase in the temperature-decreasing process. Particularly preferred is a liquid crystal with a pitch of not less than 0.8 µm when it is in a cholesteric phase (the pitch in a cholesteric phase is measured at the middle in the temperature range of the cholesteric phase). Preferably usable as a specific liquid crystal is a liquid crystal composition containing the following liquid crystal materials "LC-1", "80B" and "80SI*" in the following percentage. Liquid crystal Composition (1) (LC-1)₉₀/(80B)₁₀ (2) (LC-1)₈₀/(80B)₂₀ (3) (LC-1)₇₀/(80B)₃₀ (4) (LC-1)₆₀/(80B)₄₀ (5) 80SI* (In the table, the subscript numerals are each expressed in weight ratio.) Fig. 2 is a diagramatical drawing of an example of a cell, to illustrate the operation of a ferroelectric liquid crystal. The numerals 21a and 21b each denotes a substrate (a glass plate) covered with a transparent electrode comprised of a thin film made of In₂O₂, SnO₂, ITO or the like. Between the substrates, a liquid crystal of an SmC* (chiral smectic C) phase or an SmH* (chiral smectic H) phase is sealed, which is so aligned that its liquid crystal molecular layer 22 may be perpendicular to the glass surfaces. A line 23 shown by a thick line indicates a liquid crystal molecule. This liquid crystal molecule 23 has a dipole moment (P⊥) 24 in the direction falling at right angles with its molecule. When a voltage higher than a given threshold value is applied between the electrodes provided on the substrates 21a and 21b, the spiral structure of the liquid crystal molecule 23 comes loose, and thus the liquid crystal molecule 23 can change its direction of alignment so that all of dipole moments (P⊥) 24 face toward the direction of the electric field. The liquid crystal molecule 23 has a slender shape, and shows refractive index anisotropy between its direction of the longitudinal axis and direction of the lateral axis. Hence, it can be easily understood that if, for example, polarizers which are in crossed nicols each other are placed on both sides of a glass surface, there can be provided a liquid crystal optical modulation device capable of changing optical characteristics depending on the polarity of the applied voltage. A surface stabilized ferroelectric liquid crystal cell in the state of bistable alignment, which is used in the liquid crystal device of the present invention, can be made to have a sufficiently small thickness, for example, of from 0.1 µm to 3 µm. As the thickness of a liquid crystal layer becomes smaller in this way, the spiral structure of a liquid crystal molecule comes loose even in the state where no electric field is applied, and turns to have a non-spiral structure, so that its dipole moment P or P′ results in either an upward state (34a) or a downward state (34b), as shown in Fig. 3. When as shown in Fig. 3 an electric field Ea or Eb of a voltage higher than a given threshold value and having a different polarity is applied to such a cell through means of applying a voltage (31a) and (31b), the dipole moment changes its direction to an upward direction 34a or a downward direction 34b corresponding to the electric field vector of the electric field Ea or Eb, and, corresponding therewith, the liquid crystal molecule is aligned in the direction of either a first stable state 33a or a second stable state 33b. The effects obtainable from this ferroelectric liquid crystal cell are firstly that the response speed is very high, and secondly that the alignment of the liquid crystal molecule is bistable. The second effect will be further described with reference to, for example, Fig. 3. When the electric field Ea is applied, the liquid crystal molecule is aligned in the first stable state 33a and this state is stable even when the-electric field has been removed. On the other hand, when the electric field Eb of a reverse direction is applied, the liquid crystal molecule is aligned in the second stable state 33b to change their direction, and still remain in this state even when the electric field has been removed. The respective states of alignment are also maintained so long as the electric field Ea to be applied does not exceed a given threshold value. Fig. 4A is a cross-sectional view to diagramatically explain the state of alignment of liquid crystal molecules as produced in the direction of alignment according to the present invention. The numerals 61a and 61b shown in Fig. 4A denote an upper substrate and a lower substrate, respectively. The numeral 60 denotes a molecular layer formed of liquid crystal molecules 62, and the liquid crystal molecules 62 are arranged with changes in their positions along the base 64 (circular) of a cone 63. Fig. 4B illustrates C-directors in the state of uniform alignment. U₁ in Fig. 4B shows C-directors 81 which are in one state of stable alignment, and U₂, C-directors 81 which are the other state of stable alignment. Each C-director 81 is a projection of a molecular longitudinal axis (molecular axis) on an imaginary face perpendicular to the normal of the molecular layer 60 shown in Fig. 4A. On the other hand, the state of alignment as produced using a conventional rubbed polyamide film is illustrated by the C-directors in Fig. 4C. For the state of alignment as shown in Fig. 4C, the molecular axis is so largely twisted from the upper substrate 61a toward the lower substrate 61b that the tilt angle ϑ is small. Fig. 5A is a plan to show the tilt angle ϑ when the C-directors 81 are in the state of Fig. 4B (herein called "the state of uniform alignment"), and Fig. 5B is a plan to show the tilt angle ϑ when the C-directors 81 are in the state of Fig. 4C (herein called "the state of spray alignment"). In Figs. 5A and 5B, the numeral 50 denotes the axis of rubbing treatment applied to the above-described polyimide film of the present invention, or the direction in which a substrate is drawn up when the above-described polyimide film of the present invention is formed by the LB process. The numeral 51a denotes an average molecular axis formed in the state of alignment U₁; 51b, an average molecular axis formed in the state of alignment U₂; 52a, an average molecular axis formed in the state of alignment S₁; and 52b, an average molecular axis formed in the state of alignment S₂. The average molecular axes 51a and 51b can be converted by applying a voltage of reverse polarity which exceeds a threshold voltage each other. The same may also takes place between the average molecular axes 52a and 52b. Usefulness of the state of uniform alignment to the delay of optical response (after-image) caused by a reverse electric field V rev will be explained below. When the capacity of an insulating layer (alignment control film) of a liquid crystal cell is represented by C i , the capacity of a liquid crystal layer by C LC , and the spontaneous polarization of a liquid crystal by P s , the V rev that causes the after-image is represented by the following expression: V rev = 2·P s / (C i + C LC ) Figs. 6A to 6C are cross-sectional views to illustrate the distribution of electric charges in a ferroelectric liquid crystal, the direction of spontaneous polarization P s , and the direction of a reverse electric field V rev , respectively. Fig. 6A shows the state of distribution of plus and minus electric charges in a memory state before application of a pulse electric field. The spontaneous polarization P s is in the direction from the plus electric charges to the minus electric charges. In Fig. 6B, immediately after removing the pulse electric field the spontaneous polarization P s is in a reverse direction to the direction in the state shown in Fig. 6A (hence, the liquid crystal molecules are reversed from the one state of stable alignment to the other state of stable alignment). Since, however, the state of distribution of plus and minus electric charges is the same as in the state shown in Fig. 6A, a reverse electric field V rev is produced in the liquid crystal in the direction of the arrow. This reverse electric field V rev disappears after a while as shown in Fig. 6C, and the state of distribution of plus and minus electric charges is changed. Fig. 7 illustrates changes of optical response occurring in the state of spray alignment as produced using a conventional polyimide aligning film, which are converted to changes of the tilt angle ϑ. As shown in Fig. 7, when a pulse electric field is applied, the molecular axis is overshot from the average molecular axis S(A) formed in the state of spray alignment to the average molecular axis U₂ formed in the state of uniform alignment, which is in the vicinity of the maximum tilt angle Θ, along the direction of an arrow X₁. Immediately after removal of the pulse electric field, the reverse electric field V rev as shown in Fig. 6B acts, and the tilt angle ϑ is decreased, along the direction of an arrow X₂, to the average molecular axis S(B) formed in the state of spray alignment. Then, a state of stable alignment can be obtained in which, because of the action of attenuation of the reverse electric field V rev as shown in Fig. 6C, the tilt angle ϑ has been a little increased, along the direction of an arrow X₃, to the average molecular axis S(C) formed in the state of spray alignment. Optical response obtained here is made clear in Fig. 8. Fig. 9 shows optical response obtained when the polyimide aligning film of the present invention is used. As is evident from Fig. 9, no delay of optical response caused by the after-image occurs and also a high contrast is produced in a memory state. According to experiments made by the present inventors, employment of the aligning method using the particular polyimide alignment film as will be made clearer in the following Examples has achieved a state of alignment that gives a high optical contrast between a light state and a dark state, in particular, gives a high contrast to unselected picture elements at the time of the multiplexing drive as disclosed in U.S. Patent No. 4,655,561, etc., and also brings about no delay in optical response at the time of switching (at the time of multiplexing drive), which may cause the after-image at the time of display. The present invention will be described below by giving Examples. Example 1 Two sheets of 1.1 mm thick glass plates each provided with a 100 nm (1,000 Å) thick ITO film were prepared. The respective glass substrates were left to stand in saturated vapor of hexamethyldisilazane (HMDS) to carry out hydrophobic treatment. Thereafter, on each substrate thus treated, a built-up film of polyimide monomolecular films built up in 2, 4, 6, 8, 10, 20, 30 or 40 layers was formed by the LB process to provide an aligning film without rubbing treatment. The process of forming the built-up film of polyimide monomolecular films will be detailed below. The polyamide acid represented by the formula (1) was dissolved in N,N-dimethylacetamide (in concentration of 1 x 10⁻³M in terms of the repeating unit polyamide acid), and thereafter the solution and a 2 x 10⁻³ M solution separately prepared by dissolving N,N-dimethyloctadecylamine in the same solvent were mixed in equimolar amounts (v/v). A solution of the polyamide acid octadecylamine salt represented by the formula (2) was thus prepared. The resulting solution was spread over an aqueous phase 111 (Fig. 11) comprised of pure water of 20°C in water temperature to form a monomolecular film on the water surface. After removal of the solvent, a float as the partition plate 113 was moved to reduce the spreading area until the surface pressure was raised up to 25 mN/m. While keeping constant the surface pressure, the above IT0 glass substrate was gently immersed at a rate of 5 mm/min in the direction crossing the water surface, and thereafter subsequently gently drawn up at a rate of 3 mm/min, thus making a two-layer Y-type monomolecular built-up film. Such operations were repeated to form a monomolecular built-up film (LB film) having a given number of monomolecular layers and comprising the polyamide acid octadecyl salt. Next, such a substrate was heated in vacuo under conditions of a rate of temperature rise of 20°C/min and 300°C constant-temperature heating for 10 minutes to carry out imidization. The desired aligning films were thus obtained. Thereafter, alumina beads with an average particle diameter of 1.5 µm were sprayed on one of the glass substrates. Then, the two sheets of glass substrates were put together in such a way that the axes of dipping directions (directions on the upper and lower substrates) of the respective aligning films were in parallel and in the same treatment directions each other. A cell was thus fabricated. Into the resulting cell, a ferroelectric smectic liquid crystal "CS-1014" (trade name; a product of Chisso Corporation) was vacuum-injected in the state of an isotropic phase, and then annealed to 30°C at a rate of 0.5°C/hr from the state of the isotropic phase. Thus, it was possible to align the liquid crystal. In the cell of the present Example in which this "CS-1014" was used, the phase changes were as follows: The liquid crystal cell provided with the aligning films each comprising the 10-layer LB film prepared as described above was inserted between a pair of 90° crossed nicols polarizers. Thereafter, a 30 V pulse for 50 µsec was applied thereto and then the 90° crossed nicols were set to the position of extinction (a darkest state). Transmittance at this time was measured using a photomultiplier. Subsequently, a -30 V pulse for 50 µsec was applied, and transmittance at this time (a bright state) was measured in the same manner. As a result, it was revealed that the tilt angle ϑ was 16°, the transmittance in the darkest state was 0.9 %, the transmittance in the bright state was 50 %, and hence the ratio of contrast was 55:1. The delay in optical response that causes an after-image was 0.2 second or less. Using this liquid crystal cell, display was carried out according to multiplexing drive in which the drive wave forms as shown in Fig. 10 were used. As a result, a display with a high contrast and high grade was obtained. After an image was displayed by inputting given characters, the whole screen was turned off to a white state to confirm that no after-image was seen to have occurred. The letter symbols S N , S N+1 and S N+2 in Fig. 10 represent wave forms of the voltages applied to scanning lines. The letter symbol I represents a wave form of the voltage applied to a typical information line. I-S N is a synthetic wave form of the voltage applied to the crossing area of the information line I and the scanning line S N . In the present Example, experiments were made under conditions of V₀ = 5 V to 8 V and ΔT = 20 µsec to 70 µsec. Results of experiments on dependence to the number of LB film layers are shown in Table 1. Regardeless of the number of the LB film layers, it was possible to obtain alignment films with superior switching characteristics compared with conventional aligning films. Example 2 Two sheets of 1.1 mm thick glass plates each provided with a 100 nm (1,000 Å) thick ITO film were prepared in the same manner as in Example 1. The respective glass substrates were coated with a solution of 3.0 % by weight of the polyamide acid represented by Formula (1) as used in Example 1, dissolved in a 5/1 mixed solvent of N-methylpyrrolidone/n-butyl cellosolve, for 30 minutes using a spin coater of 3,000 rpm. After films were formed, each film was heated and baked at 300°C for about 1 hour. The film hereby formed had a thickness of 25 nm (250 Å). The resulting coating film was subjected to rubbing in one direction using a nylon cloth. Thereafter, in the same manner as in Example 1, a cell was fabricated and the ratio of contrast and the delay in optical response were measured to reveal that excellent device characteristics were obtainable like the case when films were prepared by the LB process. Ratio of contrast: 50:1 Delay in optical response: 0.4 sec. Display was also carried out according to multiplexing drive in the same manner as in Example 1 to obtain the same results as in Example 1 in respect of contrast and after-image. Examples 3 to 10 Cells were obtained in the same manner as in Example 1 except that the alignment control films (alignment films) and liquid crystal materials as shown in Table 2 were used. The respective cells were tested in the same manner as in Example 1. Results obtained in respect of the ratio of contrast and the delay in optical response are shown in Table 3. Display was also carried out according to multiplexing drive in the same manner as in Example 1 to obtain the same results as in Example 1 in respect of contrast and after-image. Examples 11 to 15 Cells were obtained in the same manner as in Example 2 except that the alignment control films (alignment films) and liquid crystal materials as shown in Table 2 were used. The respective cells were tested in the same manner as in Example 1. Results obtained in respect of the ratio of contrast and the delay in optical response are shown in Table 4. Display was also carried out according to multiplexing drive in the same manner as in Example 1 to obtain the same results as in Example 1 in respect of contrast and after-image. Comparative Examples 1 to 4 Cells were fabricated in the same manner as in Example 2 except that the alignment control films (alignment films) and liquid crystal materials as shown in Table 5 were used. The respective cells were tested in the same manner as in Example 1. Results obtained in respect of the ratio of contrast and the delay in optical response are shown in Table 6. Display was also carried out according to multiplexing drive in the same manner as in Example 1 to obtain the results that the contrast was lower than that of Examples of the present invention and also after-image occurred. In the above Examples, characteristics of liquid crystal devices prepared using the ferroelectric liquid crystal CS1014 were evaluated. The liquid crystal materials used are by no means limited to ferroelectric liquid crystals. For example, nematic liquid crystals, cholesteric liquid crystals and smectic liquid crystals can also be used alone or in the form of a mixture. An example of a device in which a nematic liquid crystal is used is shown below. Example 16 Substrates were prepared in the same manner as in Example 2. The substrates were put together in such a manner that the rubbing directions may cross at right angles, and peripheral edges thereof were sealed using a heat-curable epoxy resin, except for an injection opening. The space between the substrates was 6 µm. Next, a nematic liquid crystal (ZLI-1285, a product of Merck AG., West Germany) was injected into the cell, and then the injection opening was sealed. A pair of polarizers were disposed in parallel to the rubbing direction of an adjacent substrate, and the liquid crystal was observed with a microscope to confirm that twisted alignment was achieved in a superior uniformity. Using this liquid crystal device, a continuous operation test was carried out. As a result, a good twisted alignment was retained even after drive for 30 days using an alternating current of 10 V at 50 Hz, and thus superior durability was confirmed.

Claims: A liquid crystal device comprising a pair of substrates and a liquid crystal material disposed between said pair of substrates, wherein at least one of said substrates is provided with a film comprising a polyimide compound having in its polyimide main-chain structural unit at least one alkyl side chain containing an alkyl chain moiety having a length of 3 to 10 carbon atoms. A liquid crystal device according to claim 1, wherein said alkyl side chain is a straight-alkyl chain. A liquid crystal device according to Claim 1, wherein said polyimide film is a monomolecular film or a built-up film of monomolecular films. A liquid crystal device according to Claim 1, wherein said liquid crystal material is a ferroelectric liquid crystal. A liquid crystal device according to Claim 1, wherein said polyimide film comprising said polyimide compound is a film obtained by imidation of a polyamide acid synthesized by condensation reaction of a carboxylic anhydride with a diamine, at least one of said carboxylic anhydride or said diamine is substituted with said alkyl side chain. A liquid crystal device according to Claim 5, wherein said carboxylic anhydride or said diamine at least one of which is substituted with said alkyl side chain is selected from the group consisting of: - Diamines - and - Carboxylic acid anhydrides - and wherein m and n each represent an integer of 0, 1 to 3; R is selected from the groups consisting of: normal-C ℓ H 2ℓ+1 -, ℓ = an integer of 3 to 10; normal-C ℓ H 2ℓ+1 CO-, ℓ = an integer of 3 to 10; normal-C ℓ H 2ℓ+1 O-, ℓ = an integer of 3 to 10; normal CF₃(CF₂) k (CH₂) ℓ -, ℓ+k = an integer of 2 to 10 and k = 2, 3 or 5; normal CF₃(CF₂) k (CH₂) ℓ CO-, ℓ+k = an integer of 2 to 10 and k = 2, 3 or 5; (CF₃)₂CF(CH₂) ℓ -, ℓ = an integer of 0, 1 to 8; or (CF₃)₂CF(CH₂) ℓ CO-, ℓ = an integer of 0, 1 to 8 and R can be combined with different two or more kinds of the group thereof. A liquid crystal device according to Claim 1, wherein said polyimide film has a thickness of from 1 nm to 1 µm. A liquid crystal device according to Claim 1, wherein said polyimide film has a thickness of from 3 to 200 nm. A liquid crystal device according to Claim 1, wherein said polyimide film has a thickness of from 3 to 30 nm.

Inventors: EGUCHI KEN C O CANON KABUSHIKI, KAWADA HARUKI C O CANON KABUSH, KAWADE HISAAKI C O CANON KABUS, MATSUDA HIROSHI C O CANON KABU, MORIKAWA YUKO C O CANON KABUSH, UCHIMI TOSHIHARU C O CANON KAB, EGUCHI, KEN, C/O CANON KABUSHIKI KAISHA, KAWADA, HARUKI, C/O CANON KABUSHIKI KAISHA, KAWADE, HISAAKI, C/O CANON KABUSHIKI KAISHA, MATSUDA, HIROSHI, C/O CANON KABUSHIKI KAISHA, MORIKAWA, YUKO, C/O CANON KABUSHIKI KAISHA, UCHIMI, TOSHIHARU, C/O CANON KABUSHIKI KAISHA
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1990
Main classification: G02F1
IPC codes: C08G73, G02F1