Method of making hydrophilic-lipophilic copolymeric powders

Abstract: A precipitation polymerization process for producing a macroporous crosslinked copolymeric lattice, capable of adsorbing hydrophilic and lipophilic fluids, in which process there is copolymerized at least one mono­ unsaturated monomer and at least one polyunsaturated monomer in the presence of an organic liquid which is a solvent for the monomers but not for the copolymer, initiating the copolymerization of the monomers by means of a free radical generating catalytic compound, precipitating a copolymer in the solvent in the form of a powder and forming a dry powder by removing the solvent from the precipitated copolymeric powder. One monomer is a hydrophilic compound and the other monomer is a lipophilic compound.

Description: In accordance with the present invention, copolymer powders are produced by novel processes not believed to be taught in the prior art. The prior art, in general, relates to suspension polymerization processes for the production of porous polymeric and copolymeric spheres and beads in which the precipitant is present during polymerization. What has been accomplished in the present invention, however, is a unique concept differing from all of the prior art methods and wherein hydrophilic-lipophilic post adsorbent powders are produced. In contrast to the prior art, the powders of the present invention are capable of adsorbing lipophilic fluids, as well as hydrophilic fluids and liquids having a high surface tension such as water. The powders of the prior art have only been capable of adsorbing low surface tension liquids. This invention relates to a precipitation polymerization process for producing a macroporous cross-linked copolymeric lattice, capable of adsorbing hydrophilic fluids and lipophilic fluids. In the process, there is copolymerized at least one monounsaturated monomer and at least one polyunsaturated monomer in the presence of an organic liquid which is a solvent for the monomers but not for the copolymer. The copolymerization of the monomers is initiated by means of a free radical generating catalytic compound, precipitating a copolymer in the solvent in the form of a powder. A dry powder is formed by removing the solvent from the precipitated copolymeric powder. One monomer is a hydrophilic compound and the other monomer is a lipophilic compound. The invention also relates to a macroporous crosslinked copolymeric powder produced in accordance with the process. The monounsaturated monomer is selected from vinyl pyrrolidone, diacetone acrylamide or 2-phenoxyethyl methacrylate. The polyunsaturated monomer can be ethylene glycol dimethacrylate or tetraethylene glycol dimethacrylate. The solvent is preferably isopropyl alcohol, although ethanol, toluene, heptane and cyclohexane, may also be employed. The powder which is formed by the process of the present invention is a combined system of particles which can be defined as a lattice; the system of powder particles including unit particles of less than about one micron in average diameter, agglomerates of fused unit particles of sizes in the range of about twenty to eighty µm (microns) in average diameter and aggregates of clusters of fused agglomerates of sizes in the range of about two hundred to about twelve hundred µm (microns) in average diameter. The monounsaturated monomer and the polyunsaturated monomer can be present in mol ratios of 20:80, 30:70, 40:60 or 50:50. The process may include the step of stirring the monomers, solvent and the free radical generating catalytic compound, during copolymerization. Preferably, the dry powder is formed by filtering excess solvent from the precipitated powder and the filtered powder is vacuum dried. The powder may then be "post adsorbed" with various materials. The hydrophilic-lipophilic powders of the present invention may be used as carriers or adsorbents for materials such as water, aqueous systems, emollients, moisturizers, fragrances, dyes, pigments, flavors, drugs such as ibuprofen, phosphoric acid, insect repellents, vitamins, sunscreens, detergents, cosmetics, pesticides, pheromones, herbicides, steroids, sweeteners, pharmaceuticals and antimicrobial agents. Finely divided solids such as analgesic materials can be adsorbed by dissolving the finely divided analgesic in a solvent, mixing the analgesic and solvent with the powder and removing the solvent. Other post adsorbable materials include alkanes, alcohols, acid esters, silicones, glycols, organic acids, waxes and alcohol ethers. These and other objects, features and advantages, of the present invention will become apparent when considered in light of the following detailed description, including the accompanying drawings. Figure 1 of the drawings is a photomicrograph of the various components of the powder produced in Comparative Example I and including unit particles, agglomerates and aggregates. Figures 2 and 3 are photomicrographs of the agglomerates and aggregates of Comparative Figure 1, respectively shown on a larger scale. Figure 4 is a photomicrograph of a polymer bead produced by suspension polymerization. Figure 5 is a photomicrograph of the bead of Figure 4 with a portion of the shell removed to reveal the interior structure of the bead. Figure 6 is a photomicrograph of a hydrophobic copolymeric powder material. The powder is shown in magnification as it appears when the agitation rate employed in the process for producing the hydrophobic powder is zero rpm. Figures 7-10 are additional photomicrographs of hydrophobic copolymeric powder materials. The powder is shown in magnification as it appears when the agitation rate employed in the process for producing the hydrophobic powder varies from seventy-five rpm up to eight hundred rpm. In the above figures in the drawing, the magnification is indicated in each instance. For example, the magnification in Figures 6-9 is 1000X and 2000X in Figure 10. Figures 6-10 also include an insert identifying a length approximating ten µm (microns) for comparative purposes. It should be pointed out, that in viewing the various Figures 6-10, one will note that as the rate of stirring is increased from zero rpm up to eight hundred rpm, that the size of the unit particles increase. This is in direct opposition to what has been traditionally observed in suspension polymerization systems, wherein increases in stirring rates decrease particle size. Because of the increased size of the particulates shown in Figure 10 and the resulting decrease in surface area, the adsorptive capacity of these large particulates is less than the adsorptive capacity of the smaller sized particulates shown in Figures 6-9. The most effective particulates can be produced if the rate of stirring is maintained below about three hundred rpm, although particulates produced at rates beyond three hundred rpm are useful and adsorptive, but to a lesser extent. The material of the present invention, can be broadly and generally described as a crosslinked copolymer capable of entrapping solids, liquids and gases. The copolymer is in particulate form and constitutes free flowing discrete solid particles even when loaded with an active material. When loaded, it may contain a predetermined quantity of the active material. The copolymer has the structural formula: where the ratio of x to y is 80:20, R′ is -CH₂CH₂- and R′′ is -(CH₂)₁₁CH₃. The copolymer is a highly crosslinked copolymer, as evidenced by the foregoing structural formula and is more particularly a highly crosslinked polymethacrylate copolymer. This material is manufactured by the Dow Corning Corporation, Midland, Michigan, U.S.A. and sold under the trademark POLYTRAP®. It is a low density, highly porous, free-flowing white particulate and the particles are capable of adsorbing high levels of lipophilic liquids and some hydrophilic liquids, while at the same time maintaining a free-flowing particulate character. In the powder form, the structure of the particulate is complex and consists of unit particles less than one micron in average diameter. The unit particles are fused into agglomerates of twenty to eighty µm (microns) in average diameter. These agglomerates are loosely clustered into macro-particles termed aggregates of about 200 to about 1200 µm (microns) in average diameter. Adsorption of actives to form post adsorbent powder, can be accomplished using a stainless steel mixing bowl and a spoon, wherein- the active ingredient is added to the empty powder and the spoon is used to gently fold the active into the powder. Low viscosity fluids may be adsorbed by addition of the fluids to a sealable vessel containing the powder and tumbling the materials until a consistency is achieved. More elaborate blending equipment such as ribbon or twin cone blenders can also be employed. The following example illustrates the method for making a post adsorbent powder, of the type illustrated in Figures 1-3 and 6-10. Comparative Example 1 A hydrophobic porous copolymer was produced by the precipitation polymerization technique by mixing in a five hundred milliliter polymerization reactor equipped with a paddle type stirrer, 13.63 grams of ethylene glycol dimethacrylate monomer or eighty mole percent and 4.37 grams of lauryl methacrylate monomer or twenty mole percent. Isopropyl alcohol was added to the reactor as the solvent in the amount of 282 grams. The monomers were soluble in the solvent, but not the precipitated copolymer. Other solvents that can be employed are ethanol, toluene, cyclohexane or heptane. The mixture including monomers, solvent and 0.36 grams of catalytic initiator benzoyl peroxide, was purged with nitrogen. The system was heated by a water bath to about 60°C. until copolymerization was initiated, at which time, the temperature was increased to about 70-75°C. for six hours, in order to complete the copolymerization. During this time, the copolymer precipitated from the solution. The copolymerization produced unit particles of a diameter less than about one µm (micron). Sane of the unit particles adhered together providing agglomerates of the order of magnitude of about twenty to eighty µm (microns) in diameter. Sane of the agglomerates adhered further and were fused and welded one to another, forming aggregates of loosely held assemblies of agglomerates of the order of magnitude of about two to eight hundred µm (microns) in diameter. The mixture was filtered to remove excess solvent and a wet powder cake was tray dried in a vacuum oven. A dry hydrophobic copolymeric powder consisting of unit particles, agglomerates and aggregates was isolated. Powders can also be produced using other monomers of the type disclosed in U.S. Patent No. 4,724,240. The adsorptive capacity of the hydrophobic particulates produced in Comparative Example I, as a function of the stirring rate, was determined. The stirring rate during the reaction in Comparative Example I significantly influences the adsorption properties of the particulate materials. The adsorptivity of the particulate materials decreases with an increase in stirring rate and the density of the particulates increases. These results are tabulated and set forth in Tables I-III. In the foregoing tables, it can be seen that adsorption and density, as a function of stirring rate, was determined for a silicone oil, water, mineral oil, glycerine and an organic ester. From zero rpm up to about 250 rpm, the adsorptivity of the porous copolymeric powder particulates of Example I remained essentially consistent. However, at about three hundred rpm, there was a substantial decrease in adsorptivity, which decrease became more apparent as the stirring rate was increased up to about one thousand rpm. A similar pattern is evidenced by the data which are reflective of the density. This phenomenon is more apparent in the photomicrographic figures of the drawing. Thus, it can be seen from Figure 6, that the particle size of the particulates increases as the stirring rate is increased, as evidenced by Figure 10. A progression in this phenomenon can be observed in Figures 7-9. While the procedure of Comparative Example I is a precipitation polymerization process and not a suspension polymerization system, the prior art dealing with suspension polymerization teaches that an increase in stirring rate causes a decrease in particle size. This is documented, for example, in U.S. Patent No. 4,224,415, issued September 23, 1980, and in the PCT International Publication No. WO-88/01164, published on February 25, 1988. The PCT International Publication employs stirring rates upwards of nine hundred to twelve hundred rpm. In Example I above, however, increases in stirring rates not only did not decrease the particle size, but in fact had exactly the opposite effect, causing the unit particle size to increase. As the rate of stirring is increased from zero rpm up to one thousand, the density of the particulate increases and the adsorptive capacity of the particulate decreases. In accordance with the above, it should be apparent that it is possible to tailor porous particulates of a particular size and adsorptivity by means of stirring rate. Thus, with large unit particles in Figure 10, the adsorptive capacity is less than the adsorptive capacity of smaller sized unit particles in Figures 6-9. While the most effective particulates are produced when the rate of stirring is maintained below about three hundred rpm, particulates produced at rates beyond three hundred rpm are useful. It is important to understand that the method of Comparative Example I for the production of hydrophobic porous copolymeric particulate powder materials is characterized as a precipitation polymerization technique. In accordance with this technique, monomers are dissolved in a compatible volatile solvent in which both monomers are soluble. Polymer in the form of a powder is precipitated and the polymer is insoluble in the solvent. No surfactant or dispersing aid is required. The materials produced are powders and not spheres or beads. The powder particulates include unit particles, agglomerates and aggregates. The volatile solvent is subsequently removed resulting in a dry powder particulate, which can be post adsorbed with a variety of other types of functional active ingredients. The suspension polymerization process on the other hand, provides that polymerization be carried out in water and in some cases chloroform or chlorinated solvents. The monomers, the active, and the catalyst, form beads or droplets in water and polymerization occurs within each bead. A surfactant or stabilizer such as polyvinyl pyrrolidone is required in order to prevent the individually formed beads and droplets from coalescing. The resulting beads, with the active material entrapped therein, include a substantially spherical outer crust or shell, the interior of which contains a macroporous structure of fused unit particles, agglomerates and aggregates. The bead is ten microns in diameter to one hundred-fifty microns, depending upon the rate of agitation employed during the process. Such beads are shown in Figures 4 and 5. Some unique features of the powders of Figures 1-3 and 6-10 are their ability to adsorb from sixty to eighty percent of a liquid and yet remain free flowing. The materials provide a regulated release of volatile ingredients such as cyclomethicone entrapped therein and have the capability of functioning as carriers for other non-volatile oils. Loaded powders disappear when rubbed upon a surface. This phenomenon is believed due to the fact that large aggregates of the material scatter light rendering the appearance of a white particulate, however, upon rubbing, these large aggregates decrease in size approaching the range of visible light and hence seem to disappear. The materials find applications in such diverse areas as cosmetics and toiletries, household and industrial products, pesticides, pheromone carriers and pharmaceuticals. The materials do not swell in common solvents and are capable of physically adsorbing active ingredients by the filling of interstitial voids by capillary action. The active ingredients are subsequently released by capillary action or wicking from the voids within the particulates. Example I Comparative Example I was repeated, except that different monomer systems were employed and at varying mol ratios of the monomers. The copolymeric powders produced were tested for their adsorptive capacity for various lipophilic fluids and for water. The monomer pairs employed, the mol ratios and the adsorption data generated for each monomer pair, are shown in Table IV. It will be noted that the powders produced from the monomer pairs of Example I not only were capable of adsorbing substantial quantities of lipophilic fluids, but that water was capable of being adsorbed. This is in contrast to Comparative Example I and Table II where no water was adsorbed. Example I sets forth the concept of the present invention and provides hydrophilic-lipophilic copolymeric powders capable of adsorbing water and lipophilic fluids. By a selection of monomers, there can be produced powder materials possessing more versatility than the hydrophobic lattices of Comparative Example I. The water adsorbing porous polymeric materials of Example I are to be contrasted with the water containing beads of U.S. Patent No. 3,627,708, issued December 14, 1971. The bead of the ′708 patent is produced by "in situ" suspension polymerization and is adapted to contain water only because of the presence of a solubilizer such as sodium bis(2-ethyl hexyl) sulfosuccinate. The material of the present invention, on the other hand, is produced by a precipitation polymerization process, which contains no solubilizer and produces a material in the form of a hydrophilic-lipophilic powder consisting of unit particles, agglomerates and aggregates. Thus, the materials of the present invention are very distinct from the materials of the ′708 patent. The materials of the present invention are of general utility and may be used for the adsorption of lipophilic fluids and hydrophilic fluids. It will be apparent from the foregoing that many other variations and modifications may be made in the structures, compounds, compositions and methods described herein without departing substantially from the essential features and concepts of the present invention. Accordingly, it should be clearly understood that the forms of the invention described herein are exemplary only and are not intended as limitations on the scope of the present invention.

Claims: A precipitation polymerization process for producing a macroporous crosslinked copolymeric lattice, capable of adsorbing hydrophilic and lipophilic fluids, comprising copolymerizing at least one monounsaturated monomer selected from vinyl pyrrolidone, diacetone acrylamide and 2-phenoxyethyl methacrylate and at least one polyunsaturated monomer in the presence of an organic liquid which is a solvent for the monomers but not for the copolymer, initiating the copolymerization of the monomers by means of a free radical generating catalytic compound, precipitating a copolymer in the solvent in the form of a powder and forming a dry powder by removing the solvent from the precipitated copolymeric powder, one monomer being a hydrophilic compound and the other monomer being a lipophilic compound. The process of Claim 1 wherein the polyunsaturated monomer is selected from the group consisting of ethylene glycol dimethacrylate and tetraethylene glycol dimethacrylate. The process of Claim 2 wherein the solvent is selected from the group consisting of isopropyl alcohol, ethanol, toluene, heptane and cyclohexane.

Inventors: BUZZELLI ANTHONY JOHN, CARMODY WALTER JAMES, BUZZELLI, ANTHONY JOHN, CARMODY, WALTER JAMES
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1990
Main classification: C08F2
IPC codes: C08F2, A62D3