Cationic electrodeposition paint composition

Abstract: A cationic electrodeposition paint composition suitable for coating a road wheel of an automotive vehicle, comprises: an acrylic cationic resin (A) which is a copolymer of a first vinyl monomer having at least one secondary or tertiary amino group, a second vinyl monomer having a hydroxyl group, and a third vinyl monomer other than the first and the second vinyl monomers; a urethanated epoxy system cationic resin (B) which is a reaction product between a urethanated epoxy resin and at least one primary or secondary amine; a hardener resin (C) of a blocked isocyanate which regenerates isocyanate group by thermal decomposition under heating; and a cationic cross-linked resin particulate (D) which is an addition reaction product between an epoxy resin derivative (d-1) having not less than two primary amines per molecule and a polybutadiene derivative (d-2) having not less than two α, β-ethylenioally unsaturated groups per molecule, the resin particulate having an average particle size of from 0.01 µ to 1 µ; the acrylic cationic resin (A) being present in an amount from 20 to 70 parts by weight per 100 parts by weight of the total solids content of the acrylic cationic resin (A), the urethanated epoxy system cationic resin (B), the blocked isocyanate hardener resin (C) and the cationic cross-linked resin particulate (D); the urethanated epoxy system cationic resin (B) being present in an amount of from 5 to 50 parts by weight per 100 parts by weight of said total solids content; the hardener resin (C) being present in an amount of from 10 to 40 parts by weight per 100 parts by weight of said total solids content; and the cationic cross-linked resin particulate (D) being present in an amount of from 1 to 20 parts by weight per 100 parts by weight of said total solids content.

Description: This invention relates to improvements in a cationic electrodeposition paint composition, and more particularly to a cationic electrodeposition paint composition which is high in an ability for covering an edge portion of a metal plate and high in weatherability. Hitherto a cationic electrodeposition paint has been prepared by neutralizing a variety of basic resins such as basic epoxy resin, acrylic resin and polyurethane resin with organic acids, and followed by diluting it with water. In order to accomplish an electrodeposition painting, a metal object (such as steel plate) to be coated with a paint is dipped in the cationic electrodeposition paint and serves as cathode. Upon passing direct current through the metal object, a paint film which is insoluble in water is depositted on the surface of the metal object and thereafter baked to be hardened. Such an electrodeposition painting have been extensively industrially used to obtain a coated paint film which is high in weatherability and appearance while providing a corrosion resistance to the metal object. Additionally, a variety of compositions for such an electrodeposition paint have been proposed. The cationic electrodeposition paint usually includes as a main component a cationic resin derived from an epoxy resin (referred hereinafter to as "epoxy system cationic resin") or a cationic resin derived from an acrylic resin (referred hereinafter to as "acryl system cationic resin". The electrodeposition paint including the former epoxy system cationic resin is excellent in corrosion resistance to the metal object (steel plate) coated with the paint but inferior in weatherability. On the contrary, the electrodeposition paint including the latter acrylic system cationic resin is excellent in weatherability but inferior in the corrosition resistance to the metal object (steel plate) to be coated with the paint. Such a fact has been known in the art. In order to achieve both a high weatherability and a high corrosion resistance to the metal object, a cationic electrodeposition paint composition including both the epoxy system cationic resin and the acryl system cationic resin has been proposed as disclosed, for example, in Japanese Patent Publication No. 61-44906, and a Japanese technical magazine "The Industrical Coating" (by Toryo Hochi Shinbunsha) No. 87, Pages 38, published on July 15, 1987 and No. 95, Page 42, November 15, 1988. However, these publications are silent in improving an ability for covering the dge portion of the metal object (steel plate). In this regard, it is effective for improving the edge portion covering ability, to control the rhelogy of a molten coated paint film in a baking step, in which the melt viscosity is raised to lower the surface tension. As a measure for controlling the rheology, using a pigment having a large oil absorping ability has been proposed as disclosed for example in Japanese Patent Provisional Publication No. 63-62897. As another measure for the same purpose, using cross-linked resin particulate (so-called micro-gel) has been proposed as disclosed for example in Japanese Patent Provisional Publication No. 63-62761 and the Japanese technical magazine "The Industrial Coating" No. 95, pages 33 to 35. However, with even such measures, the weatherability and the edge portion covering ability (the corrosion resistance to the edge portion of the metal object) cannot be satisfied. SUMMARY OF THE INVENTION It is an object of the present invention to provide an improved cationic electrodeposition paint composition which is very high in the edge portion covering ability and in weatherability while securing a high corrosion resistance to a flat part of a metal object to be coated. A cationic electrodeposition paint composition according to the present invention is comprised of an acrylic (acrylic resin system) cationic resin (A) which is a copolymer of a first vinyl monomer having at least one of secondary and tertiary amino groups, a second vinyl monomer having a hydroxyl group, and a third vinyl monomer other than the first and second vinyl monomers; a urethanated epoxy system cationic resin (B) which is a reaction product between a urethanated epoxy resin and at least one of primary and secondary amines; a hardener resin (C) of a blocked isocyanate which regenerates isocyanate group by its thermal decomposition under heating; and a cationic cross-linked resin particulate (D) which is an addition reaction product between an epoxy resin derivative (d-1) having not less than two primary amine groups in one molecule and a polybutadiene derivative (d-2) having not less than two α,β-ethylenic unsaturated groups in a molecule, the resin particulate having an average particle size 5 ranging from 0.01 u to 1 u. In the above cationic electrodeposition paint composition, the acrylic cationic resin (A) is in an amount ranging from 20 to 70 parts by weight relative to 100 parts by weight of a total solid content of the acrylic cationic resin (A), the urethanated epoxy system cationic resin (B), the hardener resin (C) and the cationic cross-linked resin particulate (D). The urethane-modified epoxy system cationic resin (B) is in an amount ranging from 5 to 50 parts by weight relative to 100 parts by weight of the total solid content. The hardener resin (C) is in an amount ranging from 10 to 40 parts by weigt relative to 100 parts by weight of the total solid content. The cationic cross-linked resin particulate (D) is in an amount ranging from 1 to 20 parts by weight relative to 100 parts by weight of the total solid content. Accordingly, the cationic electrodeposition paint composition of the present invention can provide a paint film coated on the surface of a steel plate, which is high in the edge portion covering ability to improve a corrosion resistance to the steel plate while being highly improved in weatherability. The paint composition of the present invention is particularly advantageous for use in a road wheel of an automotive vehicle which is used under a severe condition. BRIEF DESCRIPTION OF THE DRAWING The single figure, Fig. 1 is a fragmentary sectional view of an automotive vehicle wheel coated with a cationic electrodeposition paint composition in accordance with the present invention. DETAILED DESCRIPTION OF THE INVENTION According to the present invention, a cationic electrodeposition paint composition is comprised of an acrylic cationic resin (A) which is a copolymer of a first vinyl monomer having at least one of secondary and tertiary amino groups, a second vinyl monomer having a hydroxyl group, and a third vinyl monomer other than the first and second vinyl monomers; a urethanated epoxy system cationic resin (B) which is a reaction product between a urethanated epoxy resin and at least one of primary and secondary amines; a hardener resin (C) of a blocked isocyanate which regenerates isocyanate group by its thermal decomposition under heating; and a cationic cross-linked resin particulate (D) which is an addition reaction product between an epoxy resin derivative (d-1) having not less than two primary amine groups in one molecule and a polybutadiene derivative (d-2) having not less than two α,β-ethylenic unsaturated groups in a molecule, the resin particulate having an average particle size ranging from 0,01 µ to 1 µ. In the above cationic electrodeposition paint composition, the acrylic cationic resin (A) is in an amount ranging from 40 to 60 parts by weight relative to 100 parts by weight of a total solid content of the acrylic cationic resin (A), the urethanated epoxy system cationic resin (B), the hardener resin (C) and the cationic cross-linked resin particulate (D). The urethanated epoxy system cationic resin (B) is in an amount ranging from 10 to 30 parts by weight relative to 100 parts by weight of the total solid content. The hardener resin (C) is in an amount ranging from 15 to 30 parts by weight relative to 100 parts by weight of the total solid content. The cationic cross-linked resin particulate (D) is in an amount ranging from 3 to 15 parts by weight relative to 100 parts by weight of the total solid content. The above-mentioned acrylic cationic resin (A) as a component of the electrodeposition paint composition is a cationic resin derived from an acrylic resin and produced by copolymerization of the first vinyl monomer having secondary and/or tertiary amino group, the second vinyl monomer having the hydroxyl group, and other vinyl monomer (monomers) other than the first and second vinyl monomers. Examples of the first vinyl monomer having the amino group are dialkyl aminoalkyl (meth)acrylates such as dimethyl amonoethyl (meth)acrylate, diethyl aminoethyl (meth)acrylate, dimethyl aminopropyl (meth)acrylate and diethyl aminopropyl (meth)acrylate; N-dialkyl aminoalkyl (meth)acrylamides such as N-dimethyl aminoethyl (meth)acrylamide, N-diethyl aminoethyl (meth)acrylamide, N-dimethyl aminopropyl (meth)acrylamide and N-diethyl aminopropyl (meth)acrylamide; t-butyl aminoethyl (meth)acrylate; t-butyl aminopropyl (meth)acrylate; aziridinyl ethyl (meth)acrylate; pyrrolidinyl ethyl (meth)acrylate; and piperidinyl ethyl (meth)acrylate. Of the above-exemplified monomers, dialkyl aminoalkyl (meth)acrylates and/or N-dialkyl aminoalkyl (meth)acrylamides are preferably used for the first vinyl monomer having the amino group from the point of view of hardening characteristics. The first vinyl monomer having the amino group serves to provide a cationic group to a produced copolymer. The first vinyl monomer is preferably used in an amount ranging from 5 to 40 parts by weight relative to 100 parts by weight of the total of all the vinyl monomers (the first, second and third monomers) used in production of the copolymer. If the amount of the first vinyl monomer is less than 5 parts by weight, water-reducibility of a paint composition after neutralization with organic acid is insuffcient thereby making difficult to obtain a stable paint composition. If the amount of the first vinyl monomer exceeds 40 parts by weight, a large amount of gas is generated owing to electrolysis during the electrodeposition painting, thereby causing defects of the coated paint film such as pin-holes and/or remelting of the paint film, while degrading a water resistance of the coated paint film and a corrosion resistance to the metal object (steel plate) to be coated with the paint composition. Examples of the second vinyl monomer having the hydroxyl group are hydroxyl group-containing methacrylate esters such as 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 2-hydroxybutyl (meth)acrylate and 4-hydroxybutyl (meth)acrylate. The second vinyl monomer serves to provide hydroxyl group to the produced copolymer and makes a hardening reaction with the regenerated isocyanate groups from the blocked isocyanate hardener resin (C) in a baking step of the coated paint film thereby to secure a high quality in coated paint film. The second vinyl monomer is used preferably in an amount ranging from 5 to 50 parts by weight relative to 100 parts by weight of the total of all the vinyl monomers (the first, second and third vinyl monomers), which is determined by taking account of a OH/NCO ratio or hardening reactivity of the paint composition under a baking condition, adhesion of the coated paint film to the steel plate, water resistance of the coated paint film, corrosion resistance to the steel plate and a variety of physical properties of the coated paint film, thereby obtaining a quality in which the above-listed characteristics are well balanced. The above-mentioned other (third) vinyl monomer (monomers) is a vinyl monomer which is copolymerizable with the above-mentioned first and second monomers. Examples of the other (third) monomer are (meth)acrylate esters such as methyl (meth)acrylate, ethyl (meth)acrylate, n-propyl (meth)acrylate, 1-propyl (meth)acrylate, n-butyl (meth)acrylate, 1-butyl (meth)acrylate, t-butyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, lauryl (meth)acrylate, cyclohexyl (meth)acrylate, and benzil (meth)acrylate; amide group-containing monomers such as (meth)acrylamide, N, N-dimethyl (meth)acrylamide, and N-alkoxymethyl (meth)acrylamide; aromatic vinyl monomers such as stylene, vinyl toluene, and α-methyl stylene. Such a monomer (third monomer) is used to control the appearance, weatherability, hardness, water resistance and various physical properties of the coated paint film. Copolymerization of the first, second and the other (third) monomers is carried out, as usual, in a suitable solvent using a radical copolymerization initiator. In the copolymerization, a chain transfer agent may be used to carry out a suitable control of molecular weight of a resultant copolymer, if necessary. The above-mentioned urethanated epoxy system cationic resin (B) as a component of the electrodeposition paint composition is a cationic resin derived from the urethanated epoxy resin and produced by amination of a reaction product obtained by a reaction between urethane prepolymer containing two end-isocyanate groups and an epoxy resin. The isocyanate group containing urethane prepolymer is obtained by a reaction between a diol and a diisocyanate which are theoretically 1:2 in mol ratio. Examples of the diol are monoether and polyether glycols such as ethylene glycol, propylene glycol, diethylene glycol, tripropylene glycol, polyethylene glycol, polypropylene glycol; diphenol compounds such as bis (4′-hydroxyphenyl) methane, 1, 1-bis (4′-hydroxyphenyl) ethane, 2, 2-bis (4′-hydroxyphenyl) propane, cresol and resorcinol; and diols which are obtained by addition polymerization of ethylene oxide and/or propylene oxide with alicyclic diols, such as bis (4′-hydroxycyclohexyl) methane, and 1, 1-bis (4′-hydroxycyclohexyl) ethane, a molecule of the diols having aromatic and/or aliphatic ring. Examples of diisocyanate are aliphatic diisocyanate such as tetramethylene diisocyanate and hexamethylene diisocyanate; cycloalkylene diisocyanate such as 1, 4-cyclohexane diisocyanate and isophorone diisocyanate; and aromatic or aromatic-aliphatic diisocyanates such as m-phenylene diisocyanate, 4, 4-diphenylmethane diisocyanate and 2, 4- or 2, 6-tolylene diisocyanate. The diol and the isocyanate are reacted with each other theoretically in a mol ratio of 1:2 directly or in the presence of a solvent which is inactive to the isocyanate, thereby producing a urethane prepolymer having isocyanate groups at the both ends of the prepolymer. Thereafter, the urethane prepolymer is reacted with an epoxy resin at a temperature of 60°C to 150°C directly or in the presence of a solvent which is inactive to the isocyanate, thereby obtaining the urethanated epoxy resin. Used as the epoxy resin are all ones which are known per se and have 1.5 to 3.0 epoxy groups and preferably 2 epoxy groups per one molecule and has not less than 1 hydroxyl group. It is more preferable that the epoxy resin is a glycygil ether of a polyphenol having at least two phenolic hydroxyl groups per one molecule on an average. The glycidyl ether is produced by etherification with an epihalohydrin such epichlorohydrin in a known manner in the presence of alkali and has an average molecular weight ranging from 350 to 3000. Examples of the polyphenol are bis (4′-hydroxyphenyl) methane, 1, 1-bis (4-hydroxyphenyl) ethane, 2, 2-bis (4-hydroxyphenyl) propane, 4-dihydroxy benzophenone, and 1, 5-dihydroxy naphthalene. Other examples of the epoxy resin are aliphatic epoxy resin, novolak type epoxy resin and polyalkylene glycol type epoxy resin. The above-mentioned urethanated epoxy resin is reacted with the amine thereby producing the urethanated epoxy system cationic resin (B) which is a component of the cationic electrodeposition paint composition. Examples of the amine are dialkyl amines such as diethyl amine, dibutyl amine, diisopropyl amine and di-n-propyl amine; alkylalkanol amines such as diethanol amine, diisopropanol amine and methylethanol amine; diamines such as dimethyl aminopropyl amine, diethyl aminoethyl amine, diethyl aminopropyl amine, monomethyl aminoethyl amine and hexamethylene diamine; triamines such as tetramethylene triamine, tetraethylene triamine; and cyclic amines such as piperidine and morpholine. The reaction between the above-mentioned urethanated epoxy resin and the above-mentioned amine are carried out at a temperature ranging from room temperature to 150°C directly or in the presence of a suitable solvent, in which the amine is in such an amount as to be 0.8 to 1.0 equivalent relative to the epoxy group. In this reaction, bibasic acids such as adipic acid and azelaic acid, polyether diol, polycaprolactone diol and/or the like may be reacted with the epoxy group, if necessary. The blocked isocyanate hardener resin (C) of a component of the cationic electrodeposition paint composition may be any polyisocyanate resin which is a reaction product between isocyanate group and some kinds of compounds and stable to active hydrogen of hydroxyl group or amino group at loom temperature; however, thermally decomposed at a high temperature (usually 80°C to 250°C) to regenerate isocyanate group so as to be reactive to the active hydrogen. The blocked isocyanate hardener resin is prepared by using a suitable any organic polyisocyanate. Such an organic polyisocyanate are produced from isocyanate whose examples are aliphratic isocyanates such as trimethylene diisocyanate, tetramethylene diisocyanate and hexamethylene diisocyanate; cycloalkylene isocyanates such as 1, 4-cyclohexane diisocyanate, 1, 2-cyclohexane diisocyanate and isophorone diisocyanate; aromatic isocyanates such as m-phenylene diisocyanate, and 1, 4-naphthalene diisocyanate; aromatic-aliphatic isocyanates such as 4, 4-diphenylmethane diisocyanate, 2, 4- or 2, 6-tolylene diisocyanate, 4, 4′-toluidine diisocyanate and and 1, 4-xylylene diisocyanate; nuclear substitution aromatic isocyanates such as dianisidine isocyanate, 4, 4-diphenylether diisocyanate and chloro-diphenylene diisocyanate; triisocyanates such as triphenylmethane-4, 4′, 4″-triisocyante, 1, 3, 5-triisocyanate benzene, and 2, 4, 6-triisocyanate toluene; tetraisocyanates such as 4, 4′-diphenyl-dimethylmethane-2, 2′-5′, 5′-tetraisocyanate; and polymerized polyisocyanates such as dimers and trimers of the above-mentioned diisocyanates. Additionally, the organic polyisocyanate may be a prepolymer derived from a polyol which reacts with excessive isocyanates to provide an isocyanate-terminated prepolymer. The polyol is polyether polyol and/or polyester polyol containing polyether. The polyol may be a simple polyol whose examples are glycols such as ethylene glycol, propylene glycol, glycerin, trimethylol propane, hexane triol, pentaerythritol; and monoethers and polyethers such as diethylglycol and tripropylene glycol (i.e., alkylene oxide condensation products of the above-mentioned compounds). The alkylene oxides which make condensation with the polyols are ethylene oxide, propylene oxide, butylene oxide, stylene oxide or the like. These are, in general, called hydroxy-terminated polyethers and may be of a straight chain type or a branched chain type. Examples of the polyether are polyoxyethylene glycol having a molecular weight of 1540, polyoxypropylene glycol, polyoxytetramethylene glycol, polyoxyhexamethylene glycol, polyoxynonamethylene glycol, polyoxydecamethylene glycol, polyoxydodecamethylene glycol and a mixture of the above-mentioned glycols. Polyoxyalkylene glycol ethers of the other types may be used as the polyether. Examples of particularly useful polyether polyols are ethylene glycol, diethylene glycol, triethylene glycol, 1, 4-butylene glycol, 1, 3-butylene glycol, 1, 6-hexane diol, a mixture of the above-mentioned glycols, glycerintrimethylol ethane, trimethylol propane, 1, 2, 6-hexane triol, pentaerythritol, dipentaerythritol, tripentaerythritol, polypentaerythritol, sorbitol, methylglycosides, and compounds which are produced by reaction of a polyol such as sucrose and alkylen oxide such as ethylene oxide, propylene oxide and a mixture thereof. Examples of a blocking agent for the above-mentioned isocyanate are aliphatic alcohols such as methyl alcohol, ethyl alcohol, chloroethyl alcohol, propyl alcohol, butyl alcohol, amyl alcohol, hexyl alcohol, heptyl alcohol, octyl alcohol, nonyl alcohol, 3, 3, 5-trimethyl hexanol, decyl alcohol, lauryl alcohol; alicyclic alcohols such as phenylcarbinol and methylphenylcarbinol; monoalcohols of hydroxy group-containing vinyl compound or the like, such as 2-hydroxyethyl acrylate and 2-hydroxyethyl metacrylate; hydroxyl amines such as N, N-dimethylethanol amine and N, N-diethylethanol amine; oximes such as methylethyl ketone oxime, acetone oxime, cyclohexanone oxime; and lactams such as ε-caprolactam. The blocked isocyanate hardener resin (C) is prepared by reacting the blocking agent with the isocyanate and isocyanate free radical, in which the blocking agent is in an amount sufficient to fully react with the isocyanate and isocyanate free radical. The above-mentioned cationic cross-linked resin particulate (D) is the addition reaction product formed by the addition reaction between the epoxy resin derivative (d-1) having not less than two primary amine groups in one molecule and the polybutadiene derivative (d-2) having not less than two α,β,-ethylenic unsaturated groups in a molecule. The average particle size of the cationic cross-linked resin particulate is within the range from 0.01 µ to 1 µ. The epoxy resin derivative (d-1) is a derivative from an epoxy resin and has not less than two primary amine groups in one molecule. The derivative (d-1) is produced as follows: A dehydration condensation reaction is made between an amine compound (a) having not less than one secondary amine and not less than one primary amine, and a ketone compound (b), thereby producing a ketimine compound (c). Then, an addition reaction is made between the ketimine compound (c) and an epoxy resin (d) to produce a reaction product. Thereafter, the reaction product is subjected to hydrolysis thereby to regenerate primary amine group. The epoxy resin derivative and its production method mentioned above are disclosed for example in Japanese Patent provisional Publication Nos. 54-93024 and 59-129270. Examples of the above-mentioned amine compound (a) are monoalkyl aminoalkylamines such as monomethyl aminoethylamine, monoethyl aminoethylamine, monomethyl aminopropylamine and monoethyl aminopropylamine; and polyalkylene polyamine such as diethylene triamine, dibutylene triamine and triethylene tetramine. Examples of the above-mentioned ketone compound are acetone, methylethyl ketone, methylisobutyl ketone, methylpropyl ketone and cyclohexanone. The above-mentioned polybutadiene derivative (d-2) is a derivative from the epoxidated polybutadiene and has not less than two α, β-ethylenic unsaturated groups in one molecule of the derivative. It is preferable that the polybutadiene derivative (d-2) further has tertiary amine group in order to further improve the stability (in water) of the reaction product formed between it and the epoxy derivative (d-1). The polybutadiene derivative (d-2) can be produced by reacting a polybutadiene having not less than two oxirane groups with α,β-ethylenic unsaturated caroxylic acid, or by reacting the polybutadine with the carboxylic acid after reaction with secondary amine, as disclosed for example in Japanese Patent Provisional Publication No. 63-39972. Otherwise, the polybutadine derivative (d-2) may be produced by reacting a reaction product of diisocyanate compound and hydroxyl group-containing α,β-ethylenic unsaturated compound (1:1 in mol ratio), with an epoxidated polybutadiene to which secondary amine is added. It is preferable that the epoxidated polybutadiene has a molecular weight ranging from 500 to 10000, unsaturated double bonds corresponding to an iodine value ranging from 50 to 500, and oxirane oxygen in an amount ranging from 3 to 12% by weight. As a typical compound serving to introduce α, β-ethylenic unsaturated groups, (meth)acrylic acid and hydroxyethyl (meth)acrylate are exemplified. Typical examples of the secondary amine are aliphatic amines such as dimethyl amine and diethyl amine; and alkanol amines such as methylethanol amine and diethanol amine. The addition reaction between the epoxy resin derivative (d-1) and the polybutadiene derivative (d-2) is carried out as follows: The both derivatives (d-1) and (d-2) are mixed to form a mixture to which solvent such as alcohol, ester and/or ketone and organic acid such as formic acid, acetic acid and/or lactic acid are added. Subsequently, the mixture is heated at about 40 to 100°C under vigorous stirring to accomplish a partial addition reaction between the derivatives (d-1) and (d-2). Thereafter, water or an aqueous dilution liquid containing the acrylic cationic resin (A), the urethanated epoxy system cationic resin (B) and the blocked isocyanate hardner resin (C) is added to the mixture. Then, the mixture is heated at about 40 to about 80°C thereby promoting the addition reaction between the derivatives (d-1) and (d-2) so as to accomplish cross-linking within a particle of the resin, thus forming the cationic cross-linked resin particulates. It will be understood that a suitable selection is made on the degree (gellation degree) of cross-linking within each particle, kind and amount of the solvent, centration of neutralizing agent, degree of stirring, temperature and time of reaction and adding rate of water or the aqueous dilution liquid. It is preferable that the average particle size of the cationic cross-linked resin particulate is within a range from 0.01 µ to 1 µ. If the average particle size exceeds 1 µ, it is difficult to obtain a stable aqeous dispersion liquid. If the average particle size is smaller than 0.01 µ, an effect for suppressing flowability of the molten paint film during baking is insufficient at the edge portion of the metal object (steel plate) to be coated with the paint composition, thereby degrading the edge portion covering ability. The blended amount (in solid content) of the acrylic cationic resin (A) in the cationic electrodeposition paint composition is within the range 40 to 60 parts by weight, relative to 100 parts by weight of the total solid content of the resin (A), the resin (B), the resin (C) and the resin particulate (D). The blended amount (in solid content) of the urethanated epoxy system cationic resin (B) is within the range from 10 to 30 parts by weight, relative to 100 parts by weight of the total solid content. The blended amount (in solid content) of the blocked isocyanate hardner resin (C) is within the range from 15 to 30 parts by weight, relative to 100 parts by weight of the total solid content. The blended amount (in solid content) of the cationic cross-linked resin particulate (D) is within the range from 3 to 15 parts by weight, relative to 100 parts by weight of the total solid content. The blended amount ratio among the resin (A), the resin (B), the resin (C) and the resin particulate (D) are decided to be within the above-mentioned ranges depending upon the specific compositions of the respective resins, the weatherability of the paint, the corrosion resistance of the paint to the flat surface and to the edge portion of the metal object (steel plate), and other requirements in quality of the paint. In this regard, increasing the blended amount of the acrylic cationic resin (A) improves a weatherability, a yellowing resistance, a gloss of a resultant coated paint film, but degrades a corrosion resistance of the paint of the flat part of the metal object (steel plate) and a covering ability of the paint on the metal object. If the blended amount of the acrylic cationic resin (A) is less than 20 parts by weight, a desired improvement level in weatherability of the resultant coated paint film cannot be achieved. If the blended amount of the resin (A) exceeds 70 parts by weight, the corrosion resistance of the paint composition to the flat part of the metal object (steel plate) for an automotive vehicle is insufficient. Increasing the blended amount of the urethanated epoxy system cationic resin (B) improves the corrosion resistance of the paint composition to the flat part of the metal object, a pitting resistance of the paint composition to the metal object and water resistance of the resultant coated paint film and the covering ability of the paint composition onto the metal object, but degrades the weatherability and the yellowing resistance of the resultant paiht film. If the amount of the urethanated epoxy system cationic resin (B) is less than 5 parts by weight, the corrosion resistance is insufficient. If the amount exceeds 50 parts by weight, the weatherability does not reach a desired value. The blocked isocyanate hardener resin (C) makes a urethanation reaction with hydroxyl groups in the acrylic cationic resin (A) and the urethanated epoxy system cationic resin (B) and cationic cross-linked resin particulate (D). In case that the concentration of the regenerated isocyanate is high, it is sufficient that the blended amount of the hardener resin (C) is less. However, if the belnded amount is less than 10 parts by weight, hardening of the resultant coated paint film is insufficient thereby to degrade an overall quality of the coated paint film. If the blended amount exceeds 40 parts by weight, the stability of the paint composition is degraded while raising problems of degrading a paint stability and degrading physical properties and an adherence of the coated paint film owing to an excessive hardening of the coated paint film. Increasing the blended amount of the cationic cross-linked resin particulate (D) improves the edge portion covering ability but degrading a smoothness (surface roughness) of the surface of the coated paint film. Thus, the blended amount of the resin particulate (D) increased within a suitable range noticeably improves the corrosion resistance to the edge portion of the metal object. However, if the blended amount exceeds 20 parts by weight, lowering in coated paint film surface smoothness leads to microscopic defects of the coated paiht film such as providing a so-called porous paint film and/or a micro-pin holed paint film, thus lowering the corrosion resistance of the paint film to the metal object. If the blended amount is less than 1 parts by weight, the edge portion covering ability is insufficient. In order to prepare the cationic electrodeposition paint composition, after the acrylic cationic resin (A), the epoxy system cationic resin (B) and the hardener resin (C) are previously mixed, neutralizing a part or all the amino groups are neutralized with formic acid, acetic acid, propionic acid and/or lactic acid. Otherwise, mixing may be made after a group of the cationic resin (A) and the hardener resin (C) and a group of the cationic resin (B) and the hardener resin (C) are respectively neutralized and formed into an aqueous solution or aqueous dispersion liquid. It will be understood that the cationic electrodeposition paint composition may include an organic solvent for the purpose of further facilitating formation of the aqueous solution or the aqueous dispersion liquid, improving the stability of the aqueous solution, the flowability of the resins and the smoothness of the coated paint film. Examples of the organic solvent are ehtyl cellosolve, propyl cellosolve, butyl cellosolve, ethyl carbitol, butyl carbitol, ethyleneglycol dimethylether, diethyleneglycol dimethylether, ethylcellosolve acetate, butylcellosolve acetate, dioxane, diacetone alcohol, MEK, MIBK, isophorone, toluene and xylene. Furthermore, the cationic electrodeposition paint composition may include a suitable pigment such as iron oxide, lead oxide, strontium chromate, carbon black, titanium dioxide, talc, aluminum silicate and barium sulfate, in which one or more pigments may be used. Moreover, the cationic electrodeposition paint composition may include, as a catalyst for hardening the coated paint film, a metallic salt of an organic acid, such as manganese acetate, manganese lactate, cobalt acetate, cobalt lactate, lead acetate, lead octate, tin acetate and dibutyltin laurate. In order to conduct an electrodeposition painting by using the cationic electrodeposition paiht composition of the present invention, an electrodeposition voltage of 50 to 400 V is impressed for 1 to 5 minutes between the metal object (serving as a cathode) to be coated and an anode under a condition in which the total solid content of the aqueous paint composition is preferably within a range of 5 to 30% by weight, more preferably within a range from 10 to 20% by weight, more preferably within a range from 10 to 20% by weight; and a temperature of the electrodeposition paint (composition) is within a range from 20 to 35°C, thereby depositing the paint composition on the surface of the metal object. The thus deposited paint is rinsed with water and thereafter baked at 150 to 200°C for 10 to 30 minutes in a baking furnace, thereby obtaining a dried coated paint film having a high weatherability and a high corrosion resistance to the flat surface and the edge portion of the metal object (steel plate). An example of usage of the electrodeposition paint composition of the present invention is shown in Fig. 1, in which the cationic electrodeposition paint composition 1 of the present invention is coated as a paint film on the surface of a steel plate 2 forming a road wheel of an automotive vehicle. The steel plate 2 has an edge portion 2a well covered with the paint composition or film 1. EXPERIMENT In order to evaluate the cationic electrodeposition paint composition of the present invention, discussion will be made on Productions and on Examples in comparison with Comparative Examples which are not within the scope of the present invention. Production 1 Preparation of acrylic cation resin (A-1) A clean reactor vessel equipped with a stirrer, a reflux condenser, a dropping funnel and a thermometer was supplied with 30 parts by weight of ethyleneglycol monoethylether and 10 parts by weight of isopropyl alcohol. The content in the reactor vessel was heated to 108°C under stirring, refluxing the solvents. Into the reactor vessel, a mixture of 10 parts by weight of n-butyl acrylate, 20 parts by weight of methyl methacrylate, 10 parts by weight of 2-hydroxyethyl, 15 parts by weight of N, N-dimethylaminopropyl methacrylamide and 2 parts by weight of azobisisobutylnitrile was dropped throughout 2 hours from the dropping funnel. Thereafter, a reaction was continued for 3 hours, maintaining a refluxing condition of the solvents, thus obtaining a copolymer solution which was light yellow and transparent and had a non-volatile content of 71% by weight. Production 2 Preparation of acrylic cationic resin (A-2) A clearn reactor vessel equipped with a stirrer, a reflux condenser, a dropping funnel and a thermometer was supplied with 30 parts by weight of ethyleneglycol monoethylether and 10 parts by weight of isopropyl alcohol. The content in the reactor vessel was heated to 108°C under stirring, refluxing the solvents. Into the reactor vessel, a mixture of 25 parts by weight of 2-ethylhexyl acrylate, 15 parts by weight of n-butyl methacrylate, 25 parts by weight of stylene, 20 parts by weight of 2-hydroxyethyl methacrylate, 15 parts by weight of dimethylaminoethyl methacrylate and 2 parts by weight of azobisisobutylnitrile was dropped throughout 2 hours from the dropping funnel. Thereafter, a reaction was continued for 3 hours, maintaining a refluxing condition of the solvents, thus obtaining a copolymer solution which was light yellow and transparent and had a non-volatile content of 71% by weight. Production 3 Preparation of urethanated epoxy system cationic resin (B-1) A clean reactor vessel equipped with a stirrer, a reflux condenser and a thermometer was supplied with 355 parts by weight of ethyleneglycol monobutylether and 650 parts by weight of bisphenol A type epoxy resin (having an epoxy equivalent of 650) were supplied. The content in the reactor vessel was heated at 100°C under stirring thereby to completely dissolve, the epoxy resin. Thereafter, the content in the reactor vessel was cooled to 60°C. Into the reactor vessel, 900 parts by weight of EPU-385 (trade name of Asahi Denka Kogyo Kabushiki Kaisha in Japan; urethane-modified epoxy resin having a solid content of 70% by weight and an epoxy equivalent of 900) was supplied. Thereafter, 105 parts by weight of diethanol amine and 73 parts by weight of diethylamine were added to the content in the reactor vessel. Then reaction was made in the content of the reactor vessel at 100°C for 2 hours, thus obtaining a resionous solution which was light yellow and transparent and had a non-volatile content of 70% by weight. Production 4 Preparation of urethanated epoxy system cationic resin (B-2) A clean (the first) reactor vessel equipped with a stirrer, a reflux consenser and a thermometer was supplied with 475 parts by weight of methylisobutyl ketone, 1900 parts by weight of bisphenol A type epoxy resin having an epoxy equivalent of 475. The content in the reactor vessel was heated at 100°C thereby completely dissolving the epoxy resin. Anoter (the second) reactor vessel was supplied with 348 parts by weight of tolylene diisocyanate. Into the reactor vessel, 1000 parts by weight of Adeka Polyether P-1000 (trade name of Asahi Denka Kogyo Kabushiki Kaisha; polypropylene glycol) was gradually added, paying attension to heat generation. After completion of addition of the Adeka polyether P-1000, the temperature in the content in the reactor vessel was maintained at 60°C, in which a NCO value was measured at intervals of 1 hour. When the NCO value for the solid content reached 6.0 to 6.5%, 675 parts by weight of the content in the second reactor vessel was gradually added to the content (the epoxy resin solution) in the first reactor vessel at 100°C under good stirring. Then reaction was made at 100°C for 3 hours, thereby obtaining a reaction mixture. To this reaction mixture, 1137 parts by weight of ethyleneglycol monobutylether was added. Then the reaction mixture was cooled to 60°C, and 420 parts by weight of diethanol amine was added to the reaction mixture. Reaction was made at 100°C for 2 hours, thus obtaining a resinous solution which was light yellow and had a non-volative content of 65% by weight. Production 5 Preparation of blocked isocyanate hardener resin (C-1) A clean reactor vessel equipped with a stirrer, a reflux condenser, a dropping funnel and a temperature was supplied with 253 parts by weight of methylisobutyl ketone and 522 parts by weight of tolylenediisocyanate. Into the reactor vessel, 354 parts by weight of ethyleneglycol monobutylether are dropped throughout 1 hour at 30°C under stirring, carrying out such cooling as to control the reaction mixture in the reactor vessel at temperatures from 30 to 35°C. Upon completion of dropping of the ethyleneglycol monobutylether, the reaction mixture was maintained at 40°C, in which a NCO value was measured at intervals of 1 hour. When the NCO value for the solid content reached to 14.0 to 14.5%, 134 parts by weight of trimethylol propane was heated to 90°C throughout 1 hour. Then the NCO value was measured at intervals of 1 hours maintaining the temperature. When the NCO value for solid content reached a level of not higher than 0.5%, 325 partgs by weight of ethyleneglycol monobutylether was added to the reaction mixture, and stirring was made for 1 hour, thus obtaining a resinous solution having a non-volatile content of 65% by weight. Production 6 Preparation of epoxy resin derivative (d-1) A clean 3 liter four-necked flask equipped with a thermometer, a reflux condenser and a stirrer was supplied with 950 parts by weight of bisphenol A type epoxy resin having an epoxy equivalent of 475 and 588 parts of propylene glycol methylether. The content in the flask was heated at 110°C to dissolve the epoxy resin, and then cooled to 80°C. To the content in the flask, 422 parts by weight of a diketimine compound (obtained by heating 2 moles of methylethyl ketone and 1 mole of diethylene triamine to carry out dehydration condensation) were supplied. The content in the flask was maintained at 80°C for 2 hours. Thereafter, 12 parts by weight of acetic acid and 180 parts by weight of deionized water were added to the content in the flask. Then a reaction was made at 80°C for 1 hour, thereby obtaining a compound having four primary amino groups per one molecule and having a solid content concentration of 70% by weight. Production 7 Preparation of polybutadiene derivative (d-2) A flask as same as that in Production 6 was supplied with 1000 parts by weight of an epoxidated polybutadiene having an oxirane oxygen content of 6.5% and a number average molecular weight of 1800, 377 parts by weight of ethyleneglycol monobutylether and 131 parts by weight of methylethanol amine. The content in the flask was maintained at 170°C for 6 hours under sterring in the stream of N₂ gas. After the content in the flask was cooled to 120°C, 81.4 parts by weight of acrylic acid, 8.8 parts by weight of hydroquinone and 27.1 parts by weight of ethyleneglycol monoethylether were added to the content in the flask. The content in the flask was maintained at 120°C for 4 hours, thus obtaining a compound having two α,β-ethylenic unsaturated groups and having a solid content concentration of 75% by weight. Production 8 Preparation of cationic cross-linked resin particulate (D-1) A reactor vessel was supplied with 1428 parts by weight of the primary amino group-containing epoxy resin derivative (d-1) of Production 6 and 666 parts by weight of α,β-ethylenic unsaturated groups-containing polybutadiene derivative (d-2) of Production 7 and 406 parts by weight of 5 ethyleneglycol monobutylether. The content in the reactor vessel was maintained at 50°C for 1 hour. After 17.3 parts by weight of 88% formic acid was added to the content in the reactor vessel, 4983 parts by weight of deionized water at 60°C was gradually added to the content in the reactor vessel under strong stirring. Thereafter the content in the reactor vessel was maintained at 60°C for 3 hours, thereby obtaining an aqueous dispersion liquid of a cationic cross-linked resin particulate which has a solid content concentration of 20% by weight, a cationic amine value 2.9 milli-equivalent/g(solid content), an average particle size of 0.1 µ and a gelation degree of 88%. The average particle size was measured by a Laser Particle Analyser System LPA-3000 produced by Otsuka Electronics Co., Ltd. in Japan. The gelation degree was a percentage of a content (insoluble to tetrahydrofuran) of a total solid content in the aqueous dispersion liquid, and measured as follows: 100 parts by weight of the aqueous dispersion liquid and 200 parts by weight of tetrahydrofuran were sufficiently mixed with each other thereby to obtain a mixture. The mixture was subjected to a centrifugal separation, in which a settled substance insoluble to tetrahydrofuran was measured to determine the gelation degree. Production 9 Preparation of cationic cross-linked resin particulate (D-2) A reactor vessel was supplied with 1071 parts by weight of the epoxy resin derivative (d-1) and 1000 parts by weight of the polybutadiene derivative (d-2) and 17.3 parts by weight of 88% formic acid. Subsequently, 4983 parts by weight of deionized water was gradually added to the content in the reactor vessel under strong stirring. Thereafter, the content in the reactor vessel as maintained at 60°C for 3 hours, thus obtaining an aqueous dispersion liquid of a cationc cross-linked resin particulate having a solid content concentration of 20% by weight, an average particle size of 0.08 µ and a gelation degree of 91%. Production 10 Preparation of resin for dispersing pigment A clean reactor vessel equipped with a thermometer, a reflux condenser, a vacuum distillation device and a stirrer was supplied with 714 parts by weight of methylisobutyl ketone (MIBK), 950 parts by weight of bis A type epoxy resin having an epoxy equivalent of 475 and 1264 parts by weight of polypropylene diglycidylether type epoxy resin. The content in the reactor vessel was heated at 60°C under stirring to be homogeneously dissolved, thus obtaining an epoxy resin-dissolved solution. A separate reactor vessel was supplied with 248 parts by weight of MIBK, 113 parts by weight of ε-caprolactam and 348 parts by weight of tolulene diisocyanate. The content in the reactor vessel was heated under stirring to be maintained at 50°C. Since a time point upon lapse of 1 hour, the NCO value was measured. When the NCO value for the solid content reached 27 to 29%, the content in the reactor vessel was cooled to 30°C. To the content in the reactor vessel, 118 parts by weight of ethyleneglycol monobutylether was dropped, and the content was maintained at 40°C thus obtaining a reaction product having a NCO value of 18 to 19%. This reaction product was gradually added in an amount of 620 parts by weight to the above-mentioned epoxy resin-dissolved solution in the reactor vessel under good stirring, and maintained at 80°C for 2 hours. Thereafter, to this content in the reactor vessel, 210 parts by weight of diethanol amine, 610 parts by weight of a diamine compound which was a reaction product between 1 mole of hexamethylene diamine and 2 moles of "Cardura E-10" (trade name of Shell Kagaku K.K. in Japan), and 130 parts by weight of diethylamino propylamine were added. Then the content in the reactor vessel was maintained at 80°C for 3 hours. Thereafter, 810 parts by weight of MIBK was removed at a temperature of the liquid from 80 to 90°C under a vacuum of 50 mmHg in the reaction vessel. Lastly, 810 parts by weight of ethyleneglycol monoethylether was added to the content of the reactor vesel, thus obtaining a resin for pigment dispersion, having a solid content concentration of 80% by weight. Preparation of pigment-dispersed liquids (E-1) and (E-2(black)) Raw materials for the liquids (E-1) Raw material for the liquid (E-2) Preparation The pigment dispersing resin in Production 10 was supplied into a premixing tank equipped with a stirrer, and neutralized with acetic acid and diluted with deionized water. Subsequently, the carbon black, (the titanium oxide), the kaolin, the basic lead silicate and the dibutyltin oxide were supplied in the above-mentioned amounts into the premixing tank. The mixture in the premixing tank was vigorously stirred to be previously dispersed. Thereafter, a sufficient dispersion was made by a neograin mill dispersing device, thus obtaining a pigment-dispersed liquid having a solid content concentration of 52% by weight. EXAMPLES 1 to 7 and COMPARATIVE EXAMPLES 1 to 5 A variety of cationic electrodeposition paint compositions of examples 1 to 7 and Comparative Examples 1 to 5 were prepared by mixing the above-discussed acrylic cationic resins (A-1) and (A-2), urethanated epoxy system cationic resins (B-1) and (B-2), a blocked isocyanate hardener resin (C-1), cationic cross-linked resin particulates (D-1) and (D-2), pigment-dispersed liquids (E-1) and (E-2) as shown in Table 1. EVALUATION TEST An electrically conductive object (steel plate) to be coated was dipped in an electrodeposition bath (temperature: 28°C) containing each of the above-mentioned cationic electrodeposition paint compositions of Examples 1 to 7 and Comparative Examples 1 to 5 to accomplish an electrodeposition painting which was conducted according to a painting method discussed below, in which electric current at a voltage to obtain a coated film having a thickness of 20 µm upon baking was passed for 3 minutes between the object (serving as a cathode) and an anode. The thus obtained coated film corresponding to each of Examples and Comparative Examples was subjected to evaluation tests according to testing method discussed below thereby to evaluate the characters and performances of the coated paint film. The results of the evaluation tests are shown in Table 1. Painting method The electrodeposition paint composition of each of Examples 1 to 7 and Comparative Examples 1 to 5 was supplied to a bath made of vinyl chloride. The object (mentioned below) to be coated wad dipped in the electrodeposition paint in the bath to serve as a cathode, providing an anode dipped in the paint. Then, a cationic electrodeposition was conducted upon passing electric current at a predetermined voltage between the object and the anode. After completion of the electrodeposition, the coated object was baked under a condition mentioned below to obtain a coated paint film which was hardened, thus preparing a specimen to be subjected to the evaluation tests. The object to be coated: (1) A steel plate (SPCC according to Japanese Industrial Standard G3141) having dimensions of 150 mm x 70 mm x 0.8 mm; and (2) A steel cutter knife blade which had been treated with zinc phosphate before the 20 electrodeposition painting. The baking condition: 170°C and 20 minutes Testing method for Evaluation test (1) Corrosion resistance A salt water spraying test according to Japanese Industrial Standard Z2371 was conducted on each specimen obtained in accordance with the above painting method. Regarding the specimen of the SPCC steel plate, the salt water spraying test was carried out for 1000 hours after a cut is formed on the surface of the coated paint film by a cutter knife in a manner to reach the steel plate. Then, the degree of production of red rust was observed to evaluate a corrosion resistance of the coated paint film to the steel plate. Regarding the specimen of the cutter knife blade, the salt water spraying test was carried out for 168. Then, the degree of production of red rust was observed to evaluate a corrosion resistance of the coated paint film to the steel plate. Evaluation of the corrosion resistance is shown in Table 1. Weatherability test An accelerated weatherability test according to Japanese Industrial Standard D0205 was conducted for 100 hours on the specimen obtained in accordance with the above painting method. After the accelerated weatherability test, the degree of chalking of the surface of the coated paint film was observed to evaluate the weatherability of the specimen. Evaluation of the weatherability is shown in Table 1.

Claims: A cationic electrodeposition paint composition comprising: an acrylic cationic resin (A) which is a copolymer of a first vinyl monomer having at least one secondary or tertiary amino group, a second vinyl monomer having a hydroxyl group, and a third vinyl monomer other than the first and the second vinyl monomers; a urethanated epoxy system cationic resin (B) which is a reaction product between a urethanated epoxy resin and at least one primary or secondary amine; a hardener resin (C) of a blocked isocyanate which regenerates isocyanate group by thermal decomposition under heating; and a cationic cross-linked resin particulate (D) which is an addition reaction product between an epoxy resin derivative (d-1) having not less than two primary amines per molecule and a polybutadiene derivative (d-2) having not less than two α, β-ethylenically unsaturated groups per molecule, the resin particulate having an average particle size of from 0.01 µm to 1 µm; the acrylic cationic resin (A) being present in an amount of from 40 to 60 parts by weight per 100 parts by weight of the total solids content of the acrylic cationic resin (A), the urethanated epoxy system cationic resin (B), the blocked isocyanate hardener resin (C) and the cationic cross-linked resin particulate (D); the urethanated epoxy system cationic resin (B) being present in an amount of from 10 to 30 parts by weight per 100 parts by weight of said total solids content; the hardener resin (C) being present in an amount of from 15 to 30 parts by weight per 100 parts by weight of said total solids content; and the cationic cross-linked resin particulate (D) being present in an amount of from 3 to 15 parts by weight per 100 parts by weight of said total solids content. A paint composition as claimed in claim 1 in which the first vinyl monomer of acrylic resin (A) forms from 5 to 40 parts by weight, per 100 parts by weight of the total of the first, second and third vinyl monomers; and/or the second vinyl monomer of resin (A) forms from 5 to 50 parts by weight per 100 parts by weight of the said total. A paint composition as claimed in claim 1 or claim 2 with the first vinyl monomer for resin (A) is dimethyl aminoethyl (meth)acrylate, diethyl aminoethyl (meth)acrylate, dimethyl aminopropyl (meth)acrylate and diethyl aminopropyl (meth)acrylate, N-dimethyl aminoethyl (meth)acrylamide, N-diethyl aminoethyl (meth)acrylamide, N-dimethyl aminopropyl (meth)acrylamide, N-diethyl aminopropyl (meth)acrylamide, t-butyl aminoethyl (meth)acrylate, t-butyl aminopropyl (meth)acrylate, aziridinyl ethyl (meth)acrylate, pyrrolidinyl ethyl (meth)acrylate or piperidinyl ethyl (meth)acrylate; and/or the second vinyl monomer for resin (A) is a (meth)acrylate ester; and/or the third monomer for resin (A) is methyl (meth)acrylate, ethyl (meth)acrylate, n-propyl (meth)acrylate, 1-propyl (meth)acrylate, n-butyl (meth)acrylate, 1-butyl (meth)acrylate, t-butyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, lauryl (meth)acrylate, cyclohexyl (meth)acrylate, lauryl (meth)acrylate, cyclohexyl (meth)acrylate, benzil (meth)acrylate, (meth)acrylamide, N, N-dimethyl (meth)acrylamide, N-alkoxymethyl (meth)acrylamide, vinyl toluene, or α-methyl styrene A paint composition as claimed in claim 3 in which the second vinyl monomer for resin (A) is 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 2-hydroxybutyl (meth)acrylate or 4-hydroxybutyl (meth)acrylate. A paint composition as claimed in any one of the preceding claims in which the urethanated epoxy resin for cationic resin (B) is the reaction product of an epoxy resin and a urethane resin prepolymer having isocyanate groups. A paint composition as claimed in claim 5 in which the urethane resin prepolymer is the reaction product of a diol and a diisocyanate. A paint composition as claimed in claim 6 in which the diol is ethylene glycol, propylene glycol, diethylene glycol, tripropylene glycol, polyethylene glycol, polyproylene glycol, bis (4,-hydroxyphenyl) methane, 1, 1-bis (4′-hydroxyphenyl) ethane, 2, 2-bis (4′-hydroxyphenyl) propane, cresol, resorcinol, bis (4′-hydroxycyclohexyl) methane or 1, 1-bis (4′-hydroxycyclohexyl) ethane; and/or the diisocyanate is tetramethylene diisocyanate, hexamethylene diisocyanate, 1, 4-cyclohexane diisocyanate, isophorone diisocyanate, m-phenylene diisocyanate, 4, d-diphenylmethane diisocyanate or 2, 4- and 2, 6-tolylene diisocyanate. A paint composition as claimed in any one of claims 5 to 7 in which the epoxy resin is one having 1.5 to 3.0 epoxy groups and not less than 2 hydroxyl groups per molecule and is an aliphatic epoxy resin, novolak type epoxy resin and a polyalkylene glycol type epoxy resin. A paint composition as claimed claim 8 in which which the epoxy resin is a glycidyl ether of a polyphenol and has an average molecular weight ranging form 350 to 3000. A paint composition as claimed in claim 9 in which the polyphenol is bis (4′-hydroxyphenyl) methane, 1, 1-bis (4′-hydroxyphenyl) ethane, 2, 2-bis (4-hydroxylphenyl) propane, 4-dihydroxy benzophenone 1, 5-dihydroxy naphthalene. A paint composition as claimed in any one of the preceding claims in which the amine from which the urethanated epoxy system cationic resin (B) is derived is diethyl amine, dibutyl amine, diisopropyl amine, di-n-propyl amine, diethanol amine, diisopropanol amine and methylethanol amine, dimethyl aminopropyl amine, diethyl aminoethyl amine, diethyl aminopropyl amine, monomethyl aminoethyl amine and hexamethylene diamine, tetramethylene triamine, tetraethylene triamine, piperidine or morpholine. A paint composition as claimed any one of the preceding claims in which the blocked isocyanate hardener resin (C) is the reaction product of an organic polyisocyanate and a blocking agent. A paint composition as claimed in claim 12 in which the organic polyisocyanate is trimethylene diisocyanate, tetramethylene diisocyanate, hexamethylene diisocyanate, 4-cyclohexane diisocyanate, 1, 2-cyclohexane diisocyanate, isophorone diisocyanate, m-phenylene diisocyanate, 1, 4-naphthalene diisocyanate, 4, 4-diphenylmethane diisocyanate, 2, 4- and 2, 6-tolylene diisocyanate, 4, 4,-toluidine diisocyanate, 1, 4-xylylene diisocyanate, dianisidine diisocyanate, 4, 4-diphenylether diisocyanate, chloro-diphenylene diisocyanate, triphenylmethane-4, 4 , 4″-triisocyanate, 1, 3, 5-triisocyanate benzene, 2, 4, 6-triisocyanate toluene, 4, 4 -diphenyl-dimethylmethane-2, 2′-5′, 5′-tetraisocyanate, a dimer or trimer of the diisocyanates, or a prepolymer derived from a polyol which reacts with an isocyanate to provide an isocyanate-terminated prepolymer; and/or the blocking agent is methyl alcohol, ethyl alcohol, chloroethyl alcohol, propyl alcohol, butyl alcohol, amyl alcohol, hexyl alcohol, heptyl alcohol, octyl alcohol, nonyl alcohol, 3, 3, 5,-trimethyl hexanol, decyl alcohol, lauryl alcohol, phenylcarbinol, methylphenlcarbinol, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, N, N-dimethylethanol amine, N, N-diethylethanol amine, methylethyl ketone oxime, acetone oxime, cyclohexanone oxime, or ε-caprolactam. A paint composition as claimed in any one of the preceding claims in which the epoxy resin derivative (d-1) for the cationic cross-linked resin particulate (D) is producted by a process including the steps of conducting a dehydration condensation reaction between an amine compound having not less than one secondary amine and not less than one primary amine per one molecule, and a ketone compound to produce a ketimine compound; conduoting an addition reaction between the ketimine compound and an epoxy resin to produce a reaction product; and conducting a hydrolysis of the reaction product to regenerate primary amine groups. A paint composition as claimed in claim 14 in which the amine compound is monomethyl aminoethyl amine, monoethyl aminoethyl amine, monomethyl aminopropyl amine, monethyl aminopropyl amine, diethylene triamine, dibutylene triamine or triethylene triamine; and/or the ketone compound is acetone, methylethyl ketone, methylisobutyl ketone compound is acetone, methylethyl ketone, methylisobutyl ketone, methylpropyl ketone or cyclohexanone. A paint composition as claimed in any one of the preceding claims in which the polybutadiene derivative (d-2) for the cationic cross-linked resin particulate (D) is a derivative derived from an epoxidised polybutadiene which has a molecular weight of from 500 to 10000, an iodine value of from 50 to 5000, and an oxirane oxygen content of from 3 to 12% by weight. A paint composition as claimed in any one of the preceding claims further comprising an organic solvent which is ethyl cellosolve, propyl cellosolve, butyl cellosolve, ethyl carbitol, butyl carbitol, ethyleneglycol dimethylether, diethyleneglycol dimethylether, ethylcellosolve acetate, dioxane, diacetone alcohol, MEK, MIBK, isophorone, toluene or xylene. A paint composition as claimed in any one of the preceding claims further comprising a pigment which is iron oxide, lead oxide, strontium chromate, carbon black, titanium dioxide, talc, aluminium silicate or barium sulfate. A paint composition as claimed in any one of the preceding claims further comprising a metallic salt of an organic acid which is manganese acetate, manganese lactate, cobalt acetate, cobalt lactate, lead acetate, lead octate, tin acetate or dibutyltin laurate. A part of an automotive vehicle especially a road wheel, comprising: a steel plate; and a paint film coated on a surface of said steel plate, said paint film being formed from a cationic electrodeposition paint composition as claimed in any one of the preceding claims.

Inventors: HASHIMOTO SHINICHI C O SHINTO, HATTORI TSUTOMU, IIZUKA KATSUO, MASUI HIROFUMI, NISHIGAKI SATOSHI, TAKI KIYOSHI C O SHINTO PAINT, HASHIMOTO, SHINICHI, C/O SHINTO PAINT CO., LTD., HATTORI, TSUTOMU, IIZUKA, KATSUO, MASUI, HIROFUMI, NISHIGAKI, SATOSHI, TAKI, KIYOSHI,, C/O SHINTO PAINT CO., LTD.
Applicants: NISSAN MOTOR, SHINTO PAINT CO LTD, NISSAN MOTOR CO., LTD., SHINTO PAINT CO., LTD.
Application year: 1990
Main classification: C09D5
IPC codes: C09D175, C09D5