Method and apparatus for producing carpeted panels

Abstract: Carpeted panels comprising a thermoplastic substrate (12) and a synthetic fiber carpet (14) are produced by bonding the respective parts to one another using a vibration welding apparatus for causing the generation of frictional heat at the interface between the substrate and the carpet. One of the platen (20) of the welding apparatus confronting the carpet is provided with a pattern of closely spaced pins (30) engaging the carpet and urging the carpet into forced engagement with the substrate. On account of the closely spaced pins and the relatively low amplitude of the reciprocating motion, a bond is achieved substantially over the entire interface between the carpet and the substrate.

Description: The present invention concerns a method of producing a carpeted panel according to the precharacterizing portion of claim 1 and a vibration welding apparatus for producing a carpeted panel according to the precharacterizing portion of claim 13 (DE-A-3 718 424) This invention concerns the manufacture of carpeted panels as used for structural and decorative purposes. A carpeted panel comprises essentially a substrate which is a plastic molded or thermoformed panel to which a carpet made of synthetic fibers is attached. Panels of this type are quite common, but one of the best known applications is in the automobile industry where door panels, kick panels, instrument panels, consoles, seat backs, rear decks, etc frequently comprise such carpeted panels. Heretofore, such panels have been fabricated, for instance, by mechanically stapling the carpet material to the substrate. Stapling lacks a desirable appearance and provides fastening only at the location of the staple. Another method for fastening comprises the use of ultrasonic spot welding. But even this method leaves visual weld marks at the area where the ultrasonic horn, or anvil, engages the carpet material and, as before, adhesion is provided only at the location of the weld spots. A further method involves the use of an adhesive layer disposed between the carpet material and the substrate. The use of adhesive material is time consuming due to the required curing time, adhesive materials create fumes and fail to stand up under extreme temperature ranges. There is generally a lack of adhesive strength with the passage of time. The DE-A-3 718 424 describes a method of producing a carpeted panel comprising superposing upon one another a substrate of thermoplastic material and a carpet made of thermoplastic material adapted to bond to said substrate responsive to the generation of frictional heat at the interface between said substrate and said carpet. The friction heat is obtained in submitting the substrate and the carpet to a translating reciprocating motion. Figure 1 is an elevational view, partly in section, of a carpeted panel; Figure 2 is a schematic elevational view depicting the apparatus for providing an assembled panel by vibration welding; Figure 3 is a greatly enlarged top plan view of the upper panel having upstanding pins; Figure 4 is a greatly enlarged elevational view of the pins upstanding from the platen; Figure 5 is an elevational view of an alternative pin construction, and Figure 6 is a view, similar to Figure 2, but slightly enlarged for a better understanding. The method for producing the carpeted panel of the present invention is defined in the characterizing portion of claim 1 and the vibration welding apparatus for producing a carpeted panel is defined in the characterizing portion of claim 13. Referring now to the figures and Figure 1 in particular, there is shown a welded carpeted panel 10 of the invention comprising a substrate 12 and a superposed carpet welded thereto comprising a layer of backing material 14 and fibers 16. The substrate preferably is a thermoformed or molded panel made from ABS (acrylonitrile, butadiene and styrene), polypropylene or polyethylene material. The carpet backing material most commonly comprises polyethylene, polypropylene, or latex material, while the fibers most frequently are made from nylon or polypropylene material. The carpet can be of the tufted or needled type, well known in the art. Also, unbacked carpets are usable for the present application but then must be made from thermoplastic fiber material, not natural fibers, as the latter do not provide adhesive bonding when subjected to frictional heat followed by cooling. Referring now to Figures 2 and 6, there is shown the apparatus and method for providing the assembled panel 10. Numeral 18 depicts the stationary platen and numeral 20 shows the movable platen which is coupled to motive means 22 for causing the platen 20, responsive to energizing the motive means 22, to undergo translating reciprocating motion in the horizontal plane, see arrow 24. The platen 18 is adapted to undergo vertical motion for inserting workpieces to be welded and for removing welded workpieces, see arrow 26. Moreover, force means, not shown, urge the platen 18 toward the platen 20 during the weld cycle. The motive means 22 may comprise magnetic means operating against leaf springs, all as shown in detail in the US-A-3 910 504. Inserted between the platen 18 and platen 20 are the substrate 12 and the carpet comprising the backing 14 and the fibers 16 upstanding from the backing 14. An important aspect of the present invention concerns the use of a platen having a pattern of relatively closely spaced pins 30 1.4 to 12.5 pins per cm² (typically 9 to 81 pins per square inch) for engaging the backing layer of the carpet and urging the carpet underside into intimate engagement with the substrate. In a typical embodiment, see figures 4 and 6, each pin is 1.5 mm (0.060 inch square) thick, tapered near the top, see numeral 32 with a flat, non-piercing end surface 34. The pins, like the platen, are made from metal, such as aluminum or steel. Also, in a typical embodiment, the pattern comprises 6.5 cm² (16.32 or 64 pins per square inch) all pins equally spaced from one another as illustrated in figure 3. Moreover, the height of the pins preferably is selected to be a minimum of 1.1 times the thickness of the carpet including the backing layer. An alternative embodiment of the pins is shown in figure 5 wherein the pin 30A is provided with a rounded end surface 34A. Typical weld cycles range between five and twenty seconds depending on the area to be welded and the density of the fibers, using a relatively low frequency of 240 displacements per second of the movable platen with a peak-to-peak excursion amplitude of 1.5 to 1.8 mm (0.060 to 0.070 inch). By virtue of the closely space pins and the small amplitude of displacement, substantially the entire area of the mating surface is heated and becomes soft in response to the dissipation of frictional heat and cools upon termination of the vibrations, thus achieving a substantially complete bond between the substrate and the carpet. The result is a significant improvement over the processes used heretofore. Table 1 shows the welding compatibility of the most commonly used materials. Compatibility denotes a strong bond, some compatibility a weaker bond, while limited compatibility denotes a weak bond. Carpets which have no separate backing layer can be welded also to a substrate as long as the fibers comprise thermoplastic material, such as nylon or polypropolene, which materials soften and flow in response to the dissipation of frictional heat and then will adhere and bond with the substrate upon cooling. In an alternative embodiment, the platen 20 can be stationary and the platen 18 be subjected to the translating reciprocating motion without departing from the principle of the invention. However, the pins 30 must be disposed to engage the carpet for causing the intimate engagement between the carpet and the substrate. Using the above stated parameters, automobile kick panels have been manufactures successfully using a polypropylene substrate 106 cm (42 inches) long, 9 cm (3 1/2 inches) wide and 0.18 cm (3/16 inch) thick. The frequency of the welding apparatus was 240 cycles per second at a displacement amplitude of 1.5 to 1.8 mm (0.060 to 0.070 inch) peak-to-peak. While there has been described and illustrated a preferred embodiment of the invention and several modifications thereof, it will be apparent to those skilled in the art that various further changes and modifications may be made without departing from the principle of this invention, which shall be limited only by the scope of the appended claims.

Claims: A method of producing a carpeted panel (10) comprising superposing upon one another a substrate (12) of thermoplastic material and a carpet comprising fibers (16) and a layer of backing material (14) made of thermoplastic material adapted to bond to said substrate (12) responsive to the generation of frictional heat at the interface between said substrate (12) and said carpet; providing forced engagement between said carpet and said substrate (12) and subjecting said substrate (12) and carpet while in forced engagement to translating reciprocating motion relative to one another for a predetermined time interval for causing during said interval the generation of frictional heat, whereby upon cessation of said motion and the dissipation of said heat said carpet is bonded to said substrate (12) characterized in that said forced engagement between said carpet and said substrate (12) is provided in at least selected areas of said carpet to be welded to said substrate (12) in using a pattern of closely spaced pins (30) engaging the backing layer (14) of the carpet and urging the carpet underside into intimate engagement with the substrate (12). The method of producing a carpeted panel (10) as set forth in claim 1 characterized by said pins (30) engaging the side of the carpet from which the filaments (16) of the carpet are upstanding. The method of producing a carpeted panel (10) as set forth in claim 1 characterized by said pattern of closely spaced pins (30) comprising 1.5-12.6 pins per cm² (nine to eighty-one pins per square inch). The method of producing a carpeted panel (10) as set forth in claim 1, characterized by each of said pins (30) having a height of at least 1.1 times the thickness of the carpet. The method of producing a carpeted panel (10) as set forth in claim 1, characterized by each of said pins (30) being tapered near its top (32) with a flat non-piercing end surface (34). The method of producing a carpeted panel (10) as set forth in claim 1, characterized by each of said pins (30A) having a rounded end surface (34A). The method of producing a carpeted panel (10) as set forth in claim 1 characterized by each of said pins (30) being of square cross-section, tapered near the top (32) and having a flat non-piercing end surface (34). The method of producing a carpeted panel (10) as set forth in claim 1, the peak-to-peak amplitude of vibrations being less than 0.25 cm (0.100 inch). The method of producing a carpeted panel (10) as set forth in claim 1, characterized by said carpet including a layer of backing material (14) comprising latex material, and said substrate (12) comprising ABS material, polypropylene material or polyethylene material. The method of producing a carpeted panel (10) as set forth in claim 1, characterized by said carpet including a layer of backing material (14) comprising polyethylene material and said substrate (12) comprising polypropylene material or polyethylene material. The method of producing a carpeted panel (10) as set forth in claim 1, characterized by said carpet including a layer of backing material (14) comprising polypropylene material and said substrate (12) comprising polypropylene material or polyethylene material. The method of producing a carpeted panel (10) as set forth in claim 1, characterized by said carpet comprising nylon or polypropylene material and said substrate comprising ABS material, polypropylene material or polyethylene material. A vibration welding apparatus for producing a carpeted panel (10) including a substrate (12) of thermoplastic material and a carpet comprising fibers (16) and a layer of backing material (14) made of a thermoplastic material adapted to bond to said substrate in response to the generation of frictional heat at the interface between said carpet and said substrate (12), said apparatus having a stationary platen (18) and a movable platen (20) for providing forced engagement between said carpet and said substrate (12) and motive means (22) coupled to said movable platen (20) for causing said carpet while in forced engagement with said substrate (12) to be subjected to translating reciprocating motion relative to one another for causing generation of frictional heat between said carpet and said substrate (12), said apparatus being characterized by one of said platens (18 or 20) having a plurality of closely spaced pins (30) extending therefrom for engaging the backing layer (14) of said carpet and urging the carpet underside into intimate engagement with the substrate (12) between said stationary platen (18) and said movable platen (20) in at least the area of said carpet to be bonded to said substrate. A vibration welding apparatus as set forth in claim 13 characterized by said pattern comprising 1.5-12.6 pins per cm² (nine to eight-one pins per square inch). A vibration welding apparatus as set forth in claim 14 characterized by said pins (30) having a height of at least 1.1 times the thickness of the carpet engaged by said pins (30). A vibration welding apparatus as set forth in claim 13 characterized by said pins (30) being of square cross-section and tapered toward the upper end (32) and having a non-piercing end surface (34). A vibration welding apparatus as set forth in claim 13, characterized by said pins (30) upstanding from said movable platen (20).

Inventors: MAINOLFI SYLVIO JOHN, PATRY GERALD FRANCIS, PENSIERO HENRY ANTHONY, MAINOLFI, SYLVIO JOHN, PATRY, GERALD FRANCIS, PENSIERO, HENRY ANTHONY
Applicants: EMERSON ELECTRIC CO, EMERSON ELECTRIC CO.
Application year: 1990
Main classification: B29C65
IPC codes: B29C65, B29L31