Method of operating a zinc bromide battery

Abstract: A secondary battery utilizing a zinc bromide electrolyte has an electrolyte which is composed of a first solution including zinc bromide and a complexing agent which forms a bromide complex from the bromide ions to precipitate the complex in the electrolyte, and a second solution of a zinc compound which is selected from groups of compounds which decompose at a higher voltage than the first solution during battery charging. The concentrations of the first and the second solutions are regulated for providing a concentration of zinc ions which are generated from the first and the second solutions at least 0.5 mol/l higher than bromide ions which are generated from the first solution.

Description: The present invention relates to a method of operating a zinc bromide secondary battery. Recently, studies of batteries as power source have been promoted. Zinc bromide laminated secondary batteries, in which electrolyte is circulated, have been among the types of batteries developed. Conventionally, composition of the electrolyte utilized for zinc bromide batteries as mentioned above, have been about 2 to 3 mol/l of zinc bromide (ZnBr 2 ) and 0.5 to 1 mol/l of Q-Br (here, Q indicates a complexing agent). However, during a floating operation, which consists of long term charging at a constant voltage, using electrolyte having the above composition for a zinc bromide battery frequently causes generation of hydrogen. Hydrogen is generated by the reaction of 2H + = H 2 - 2e - which occurs in place of the reaction of Zn 2+ = Zn - 2e - because the concentration of zinc in the electrolyte is diluted due to thelong term charging. The generation of hydrogen causes a certain amount of energy loss in the battery. Additionally, hydrogen gas is characteristically inflammable, therefore, its generation is very dangerous as it may cause an explosion if exposed to flame. Furthermore, hydrogen generation raises the hydrogen ion exponent (pH) which deteriorates the efficiency of electrodeposition. This results in generation of hydrogen at the surface of the electrode where zinc is deposited, thus voids are caused to occur and the smoothness of the electrode surface is deteriorated, and dendrites, which are crystals of deposited metal in branch-like formations, tend to be formed. Formation of dendrites is well known to deteriorate adherence of electrodeposited metals. US-PS 4,491,625 describes a method of enhancing the coulombic efficiency of electrochemical cells employing an aqueous zinc bromide electrolyte containing sufficient bromide ions in said solution and a water soluble complexing agent capable of forming a water immiscible complex with bromine. In this method sufficient chloride ions in form of zinc chloride are added to reduce the amount of free bromine present in said electrolyte during charging the cell. The charging is carried out under constant current. It is an object of the present invention to provide a method of operating a zinc bromide secondary battery wherein the hydrogen generation is prevented, and the charging effect is raised when the battery is floated, and furthermore, wherein the safety is promoted and dendritic formation is avoided. The present method of operating a zinc bromide secondary battery comprises the steps of: preparing a first solution from zinc bromide, adding to said first solution a complexing agent which forms a bromine complex, to precipitate said complex, preparing a second solution from zinc bromide and a zinc compound selected from the groups of compounds the anions of which have a higher standard potential than bromide, said zinc compound being present in an amount so that during charging of the battery the total concentration of zinc ions in both solutions becomes at least 0.5 mol/l higher than that of the remaining bromide ions, arranging said first solution as catholyte and said second solution as anolyte so as to contact via a battery separator, and charging the battery at a constant voltage being higher than a first voltage at which zinc and bromide ions start to be discharged and lower than a second voltage at which the anions of the zinc compound start to be discharged until the electric current flowing through the battery is sufficiently reduced. As a zinc compound zinc chloride or zinc fluoride may be used. Battery charging is accomplished at a constant voltage higher than a first voltage at which zinc bromide starts to be discharged and lower than a second voltage at which the zinc compound starts to be discharged. As for the charging, a floating technique can be used. According to the present invention, zinc ions remain in the electrolyte after performing long term charging, thus, generation of hydrogen is inhibited by the presence of these zinc ions. The present invention will be understood from the detailed description given hereinbelow and from the accompanying drawing of a conventional battery which is given for explanation and understanding only and is not intended to imply limitation to the invention. In the drawing; Fig. 1 shows a diagramatic structure of a conventional zinc bromide battery. A diagramatic structure of a battery is shown in Fig. 1, referring thereto; a battery body 1 is separated by a battery separator 2 into a cathode cell 3 and an anode cell 4. The battery separator 2 is formed of an ion-exchange membrane or a porous membrane. On the anode side of the battery, electrolyte from an electrolyte tank 5 is circulated via an electrolyte feed line 6, the anode cell 4 and an electrolyte return line 7 in the vicinity of an anode electrode 8. An electrolyte feed pump 9 is installed on the electrolyte feed line 6. On the cathode side of the battery, electrolyte from a second electrolyte tank 10 is circulated via an electrolyte feed line 11, the cathode cell 3 and an electrolyte return line 12 in the vicinity of the cathode electrode 13. An electrolyte feed pump 14 is installed on the electrolyte feed line 11. A valve 15 is installed on a line which connects the bottom of the tank 10 with the feed line 11. A battery having the above-mentioned structure operates as follows; When charging, electrolyte is circulated in the direction of the arrows shown in Fig. 1. A Zn 2+ + 2e - = Zn reaction is caused at the anode 8, and a 2Br - = Br 2 + 2e - reaction is caused at the cathode 13. Bromine generated at the cathode 13 forms molecules, which diffuse in the electrolyte, some of which partially dissolve, but most form a bromine complex by reacting with a complexing agent added to the cathode electrolyte and dissolved therein. The complex precipitates and is accumulated in the tank 10. On the other hand, when discharging, the reactions caused at electrodes 8 and 13 are reversed, while the electrolyte is circulated. Zn deposited on the anode electrode 8, and Br 2 generated at the cathode electrode 13 are consumed by oxidation or reduction on respective electrodes 8 and 13. Thus electric energy can be obtained. In order to preserve zinc ions in the electrolyte regardless through the floating operation, zinc compounds which are discharged at a higher voltage than the zinc bromide are added to the electrolyte. The above-mentioned zinc compounds may be selected from among compounds such as zinc chloride or zinc fluoride. The standard electrode potential of bromide is indicated by following reaction formula: 2Br - = Br 2 + 2e - + 1.087V (25°C) Therefore, zinc compounds containing anions having a standard electrode potential of more than 1.087V are preferable. For example, the standard electrode potentials of chloride and fluoride are shown in the following equations, and according to their potentials, are found to be suitable for use in electrolyte according to the present invention; 2Cl - = Cl 2 + 2e - + 1.3595V (25°C) 2F - = F 2 + 2e - + 2.87V. In order to prevent hydrogen generation during the floating operation, ion concentrations of the added zinc compounds are preferably selected to be at least 0.5 mol/l higher than that of the bromide ion in the electrolyte, therefore, the concentration difference between zinc ions and bromide ions is at least 0.5 mol/l. When the concentration difference becomes less than 0.5 mol/l, slight amounts of hydrogen generate on portions of the anode electrode surface. Thus, the composition of the electrolyte, in this embodiment, is determined as 2 mol/l of ZnBr 2 , 1.0 mol/l of ZnCl 2 and 0.5 mol/l of QBr, wherein Q is a complexing agent, therefore, the electrolyte contains 3 mol/l of zinc ions and 4.5 mol/l of bromide ions. The concentration of zinc ions becomes at least 0.5 mol/l higher than that of bromide ions during the charging operation. Floating operation using electrolyte having the composition as mentioned above is accomplished at a constant voltage less than the 2V necessary to produce the ZnCl 2 = Zn + Cl 2 reaction but, not less than a voltage at which the ZnBr 2 = Zn + Br 2 reaction is started. Then, in the battery, the ZnBr 2 = Zn + Br 2 , reaction is promoted, and only a slight electric current flows according to the consumption of bromide ions. However, in the electrolyte, at least 0.5 mol/l of zinc ions remain, thus, generation of hydrogen can be prevented. Further to say, when using ZnF 2 as the zinc compound to be added, charging voltage may be determined to less than about 3.6V, at which a ZnF 2 = Zn + F 2 reaction is started but not less than a voltage at which a ZnBr 2 = Zn + Br 2 reaction is started. According to the present invention, zinc compounds having characteristics of a higher reaction voltage (a voltage at which an electrode reaction is started) than conventional zinc bromide electrolyte compounds, is added to the electrolyte such that a concentration of zinc ions at least 0.5 mol/l higher than that of bromide ions is provided, thus, hydrogen generation during charging can be prevented by determination of the charging voltage in a range in which discharging of zinc bromide is started but at which that of the added zinc compound is not incurred when float charging of the battery is performed. Therefore, according to the prevention of hydrogen generation, energy loss from the battery can be avoided, and duration of the charge can be kept relatively high in relation to the charging time. Additionally, because hydrogen, which is well known to be inflammable, is not generated, charging of the battery can be accomplished safely. Furthermore, because the surface of the electrode is not subject to hydrogen, electrodeposition at the electrode can be fully accomplished, therefore deterioration of electrodeposition efficiency can be prevented. More to say, since dendrite formation tends to occur in presence of hydrogen, an electrolyte which prevents hydrogen generation is suitable for raising electrodeposition efficiency thereby increasing charging efficiency. While the present invention has been disclosed in terms of the preferred embodiment in order to facilitate better understanding thereof, it should be appreciated that the invention can be embodied in various ways without departing from the principles thereof. Therefore, the invention should be understood to include all possible embodiments and modifications to shown embodiments which can be embodied without departing from the principle of the invention as set out in the appended claims.

Claims: A method of operating a zinc bromide secondary battery comprising the steps of: preparing a first solution from zinc bromide, adding to said first solution a complexing agent which forms a bromine complex to precipitate said complex, preparing a second solution from zinc bromide and a zinc compound selected from the groups of compounds the anions of which have a higher standard potential than bromide, said zinc compound being present in an amount so that during charging of the battery the total concentration of zinc ions in both solutions becomes at least 0.5 mol/l higher than that of the remaining bromide ions, arranging said first solution as catholyte and said second solution as anolyte so as to contact via a battery separator, and charging the battery at a constant voltage being higher than a first voltage at which zinc and bromide ions start to be discharged and lower than a second voltage at which the anions of the zinc compound start to be discharged until the electric current flowing through the battery is sufficiently reduced. A method according to claim 1, wherein said zinc compound is zinc chloride. A method according to claim 1, wherein said zinc compound is zinc fluoride. A method according to claim 1, wherein said charging is accomplished according to a floating charge technique.

Inventors: HASHIMOTO TAKAFUMI, HASHIMOTO, TAKAFUMI
Applicants: MEIDENSHA ELECTRIC MFG CO LTD, KABUSHIKI KAISHA MEIDENSHA
Application year: 1990
Main classification: H01M12
IPC codes: H01M12