Method of at least partially filling an electrochemichromic device

Abstract: A method of filling an electrochemichromic device comprises providing the device with a filling aperture and evacuating it, lowering the device into an electrochemichromic solution and exposing the electrochemichromic solution to an inert gas at a pressure above that of the inside of the evacuated device to cause the solution to enter the device. The aperture in the device is then sealed.

Description: The present invention relates to a method of at least partially filling an electrochemichromic device. Such devices are designed to either colour or clear, depending on desired application, under the influence of applied voltage. Patent Abstracts of Japan, 8:188(P-297), 29th August 1984 (JP-A-59/077415) refers to electrochromic display devices which use methylsulpholane in an electrolyte. EP-A-0240226 refers to image display apparatus containing a solution of a reversibly reducible organic substance. Such devices have been suggested for use as rearview mirrors in automobiles such that in night driving conditions, application of a voltage would darken a solution contained in a cell incorporated into the mirror (U.S. Patent 3,280,701, October 25, 1966). Similarly, it has been suggested that windows incorporating such cells could be darkened to block out sunlight, and then allowed to lighten again at night. Electrochemichromic cells have been used as display devices and have been suggested for use as antidazzle and fog-penetrating devices in conjunction with motor vehicle headlamps (British Patent Specification 328017, May 15, 1930). United States Patent 4,090,782 to Bredfeldt et al., United States Patent 4,572,119 to Ueno et al. (June 1988), Chemical Abstract 86:196871c, 72-Electro. Chemistry, Vol. 86, 1977, I.V. Shelepin et al. in Electrokhimya, 13(3), 404-408 (March 1977), O.A. Ushakov et al., Electrokhimya, 14(2), 319-322 (February 1978), U.S.S.R. Patent 566863 to Shelepin (August 1977), U.S. Patent 3,451,741 to Manos, European Patent Publication 240,226 published October 7, 1987 to Byker, United States Patent 3,806,229 to Schoot et al., United States Patent 4,093,358 to Shattuck et al., European Patent Publication 0012419 published June 25, 1980 to Shattuck and United States Patent 4,139,276 to Clecak et al. all disclose electrochemichromic solutions of anodic and cathodic electrochromically colouring components which provide self-erasing, high colour contrast, single compartment cells. Such anodic and cathodic coloring components comprise redox couples selected to exhibit the following reaction: The redox couple is selected such that the equilibrium position of the mixture thereof lies completely to the left of the equation. At rest potential, the anodically colouring reductant species RED 1 , and the cathodically colouring oxidant species OX 2 are colourless. To cause a colour change, voltage is applied and the normally colourless RED 1 is anodically oxidized to its coloured antipode OX 1 , while, simultaneously, OX 2 is cathodically reduced to its coloured antipode, RED 2 . These cathodic/anodic reactions occur preferentially at the electrodes which, in practical devices, are typically transparent conductive electrodes. Within the bulk of the solution, the redox potentials are such that when RED 2 and OX 1 come together, they revert to their lower energy form. This means the applied potential need only suffice to drive the above reaction to the right. On removing the potential, the system reverts to its low energy state and the cell spontaneously self-erases. Such redox pairs are placed in solution in an inert solvent. Typically, an electrolyte is also added. This solution is then placed into a relatively thin cell, between two conductive surfaces. In most applications, at least one of the conductive surfaces comprises a very thin layer of a transparent conductor such as indium tin oxide (ITO), doped tin oxide or doped zinc oxide deposited on a glass substrate so that the cell is transparent from at least one side. If the device is to be used in a mirror, the second surface is typically defined by a relatively thin layer of transparent conductor such as indium tin oxide, doped tin oxide or doped zinc oxide deposited on another glass substrate, which is silvered or aluminized or otherwise reflector coated on its opposite side. In the case of solar control windows, the second glass substrate would of course not be silvered on its opposite side so that when the redox pair is colourless, the window would be entirely transparent. A wide variety of cathodically colouring species, anodically colouring species, inert current carrying electrolytes and solvent systems are described in prior art. However, combinations of these suitable to meet the performance required for outdoor weathering, particularly for outdoor weathering of automobile rearview mirrors and automobile and architectural windows, have hitherto not been revealed. Nor have combinations been revealed that, in conjunction with possessing inherent UV stability, meet the temperature extremes required in commercial automotive and architectural applications. Nor have combinations been revealed that meet the UV resilience and temperature extremes required in automotive and architectural applications and that simultaneously have sufficiently low vapour pressures to facilitate use of a vacuum backfill technique to fill thin cells where the interpane spacing is very small. With higher vapour pressures, undesirable voids are left with the solution in the vacuum backfilled cell. Vacuum backfilling has been used to fill liquid crystal displays. Liquid crystal displays are typically much smaller than the large areas of typical electrochemichromic devices such as mirrors and windows. Liquid crystal materials have inherently high viscosity and low vapour pressure. To fill with liquid crystal using the vacuum backfill technique, elevated temperatures are typically used so that the liquid crystal viscosity is sufficiently low that the material flows into and fills the cavity. Because of their inherent low vapour pressure even at elevated temperatures, voids are not a significant problem during backfilling with liquid crystals. However, the same is not true for many electrochemichromic solvents cited in the prior art. Many of the organic solvents proposed in the prior art as solvents for electrochemichromic compounds have disadvantages when chosen for UV resilient devices. This is because commonly suggested solvents, such as acetonitrile, propylene carbonate, gammabutyrolactone, methyl ethyl ketone, dimethylformamide and the like, are highly transmissive to UV radiation. Incoming UV radiation that is admitted by the ITO-coated glass substrate is unattenuated by the solvent and thus is capable of photolyzing or otherwise degrading any UV vulnerable solute in solution in that solvent. Addition of UV stabilizers such as benzotriazoles, benzophenones, or hindered amine complexes, as known in prior art, can help increase solution stability to UV radiation, but there are limitations and disadvantages to addition of UV stabilizers. Because they are held in solutions of low to moderate viscosity, both the UV stabilizer and the electrochemichromic solutes are free to randomly move about in the solution. Thus, an incoming photon of UV radiation may impinge and thus degrade an electrochemichromic solute species rather than be absorbed by a UV absorber in solution. Also, solubility within the selected solvent places limits on the amount of UV stabilizer that can be added. Solute solubility is also a factor in connection with the choice of solvents for electrochemichromic components. High solubility is preferred for the anodic and cathodic species as well as for electrolytes which are usually added to such solutions. Such electrolytes enhance cell performance and must be soluble in the solvent. Yet another problem encountered in electrochemichromic devices relates to current leakage. When the electrochemichromic cell is coloured by the application of voltage, the coloured species OX 1 and RED 2 continually want to recombine and return to their equilibrium, colourless condition. The rate ofrecombination of the coloured species OX 1 and RED 2 within the bulk of the solution is directly proportional to their diffusion coefficient in the solvent used. In order to compensate for the tendency of the coloured species to recombine and go to the colourless equilibrium state, current must continually leak into the electrochemichromic solution via the conductive electrodes that typically sandwich said solution. Because current must flow across the conductive surface of the transparent conductor used on at least one of the substrates that sandwich the electrochemichromic cell, and because these transparent conductors have finite sheet resistance, applied potential will be highest adjacent to the bus bar connector typically located at an edge perimeter and will be lowest near the center of the device as current passes across the conductive glass surface to colour remote regions. Thus, if the leakage current is high and/or the sheet resistance of the transparent conductor is high, the potential drop that ensues across the transparent conductor itself results in a lower potential being applied to remote regions. Colouration is therefore non-uniform with the edge regions nearest the bus bar colouring deepest and the central regions colouring lightest. Such non-uniformity in colouration is commercially undesirable. For a given transparent conductor sheet resistance, the lower the leakage current the more uniform the colouration. This is an important advantage; otherwise, a thicker and hence more costly and less transparent conductive coating would be needed to reduce the sheet resistance to accommodate the higher leakage currents seen with solvents suggested in the prior art. Yet another disadvantage of higher leakage currents is their imposition of a drain on battery-power sources in some instances. If an electrochemichromic device were used in a sunroof, for example, it would be desirable to have the sunroof coloured dark while the car is parked in a parking lot. If the current leakage is too great, the operator could find that the car battery has been drained as a result of current being drawn by the coloured sunroof. One further problem which plagues electrochemichromic devices is "segregation." When first bleached after being held for a prolonged period in the coloured state, bands of colour are seen adjacent to the bus bar connectors to the transparent conductive electrodes that sandwich the electrochemichromic solution. In electrochemichromic solutions revealed in prior art, various methods must be used to reduce segregation. These include thickening the electrochemichromic solution, use of low concentrations of electrochemichromically active species, and use of high concentrations of current-carrying electrolyte. The addition of thickeners will also reduce leakage current. One problem with adding thickeners is that the solution can become so viscous that vacuum backfilling a thin electrochemichromic cell becomes commercially unfeasible. As a result of these drawbacks, electrochemichromic solutions and devices based thereon have not achieved the degree of commercial success which they potentially could achieve. Attention is drawn to the Applicant's co-pending application no. 90312972.4 (published as EP-A_0430684) from which this application is divided and which is concerned with an electrochemichromic solution. An electrochemichromic solution according to the parent patent application may comprise a solvent and a redox chemical pair (which is generally in solution in the solvent) which can be coloured or colourless according to an applied voltage, e.g. colours in the presence of an applied voltage but (bleaches to) colourless in the absence of an applied voltage, the solvent comprising at least 25% by volume of 3-hydroxypropionitrile (HPN), 3,3'-oxydipropionitrile (ODPN), 2-acetylbutyrolactone (ABL), 2-methylglutaronitrile (MGNT) or 3-methylsulfolane (MS) or a mixture thereof. By changing the applied voltage the redox chemical pair can be made to change from a coloured state to a colourless state, or vice versa. The solvent suitably comprises up to 75% by volume of 3-hydroxypropionitrile (HPN), 3,3'-oxydipropionitrile (ODPN), 2-acetylbutyrolactone (ABL), 2-methylglutaronitrile (MGNT) or 3-methylsulpholane (MS) or a mixture thereof. HPN is the solvent of choice. Usually the solution will additionally include an electrolyte dissolved in the solvent. The solvent may be a mixture of one or more solvents. Preferred combinations include: HPN and ABL; ODPN and ABL; HPL and MGNT; and HPN and MS. Particularly preferred solvents comprise: (a) 3-hydroxypropionitrile and 2-methylglutaronitrile in a ratio by volume of from 75:25 to 25:75; (b) 3-hydroxypropionitrile and 3-methylsulpholane in a ratio by volume of from 75:25 to 25:75; (c) propylene carbonate and 3,3'-oxydipropionitrile in a ratio by volume of from 75:25 to 25:75; (d) 3-hydroxypropionitrile and 2-acetylbutyrolactone in a ratio by volume of from 75:25 to 25:75; (e) 2-acetylbutyrolactone and 3,3'-oxydipropionitrile in a ratio by volume of from 75:25 to 25:75; (f) propylene carbonate and 2-acetylbutyrolactone in a ratio by volume of from 75:25 to 25:75; or (g) 3-hydroxypropionitrile and 3,3'-oxydipropionitrile in a ratio by volume of from 75:25. The redox pair will generally be an oxidant and reductant, or a cathode material and an anode material. These are suitably a viologen and a phenazine, diamine or a benzidine, respectively. Preferred concentrations of the cathode and/or anode material are as for the electrolyte, i.e. 0.01 to 0.04M, e.g. 0.020 to 0.040M and particularly from 0.025 to 0.035M. The solution may also be provided with an ultra-violet (UV) stabiliser. The stabiliser is preferably a benzotriazole, benzophenone or even a hindered amine complex. The stabiliser is suitably present at a concentration of from 1 to 10%, e.g. 3 to 7%, and optimally from 4 to 6% by weight. In preferred embodiments the electrochemichromic solutions can utilise conventional or equivalent redox systems, such as a viologen combined with a phenazine, diamine or a benzidine. Such a system is usually dissolved in solvent comprising at least 25% by volume of one or more of the following solvents: 3-hydroxypropionitrile (HPN), 3,3'-oxydipropionitrile (ODPN), 3-methylsulfolane (MS), 2-methylglutaronitrile (MGNT) and/or 2-acetylbutyrolactone (ABL). Electrolytes may optionally, but preferably, be used in the solvent. A viologen is the preferred cathodic material in the redox pair. A C 1-8 alkyl viologen can be used. Methylviologen, ethylviologen, benzylviologen and heptylviologen are all satisfactory with a .025 molar solution (e.g. of methylviologen) being preferred. Although higher concentrations up to the solubility limits are also operable. In the structural formulae set forth below, X - represents the anion of the viologen salt. Various anions can be used, such as fluorine-containing anions (e.g. PF 6 - or AsF 6 - ); the most preferred anion is hexafluorophosphate (PF 6 - ) because it may surprisingly enhance viologen solubility. The hexafluorophosphate counter ion is listed below with other acceptable, though less preferred, counter ions for use on the viologens: Tetrafluoroborate BF 4 - Perchlorate C lO4 - Trifluoromethane sulfonate CF 3 SO 3 - Hexafluorophosphate PF 6 - Preferred anodic colouring materials include: (a) phenazines: e.g. di(C 1-8 )alkyl phenazines: (b) diamines: e.g. phenylene diamines (each of R 1 to R 4 individually represent a C 1-8 alkyl group) TMPD - N,N,N',N'-tetramethylphenylenediamine (c) benzidines: (each of R 1 to R 4 individually represent a C 1-8 alkyl group) TMBZ - N,N,N',N'-tetramethylbenzidine (d) a fulvalene TTF - Tetrathiafulvalene Phenazines are preferred, e.g. 5,10-dihydro-5,10-dimethylphenazine (DMPA), e.g. a 0.025 molar solution. Numerous electrolytes can be used in the present invention. One which is often suggested for electrochemichromic cells and which is acceptable in accordance with the preferred solution of the invention is a fluorophosphate, e.g. tetra(C 1-8 )alkyl ammonium fluorophosphate, such as a tetrabutylammonium hexafluorophosphate. Preferred concentrations range from 0.020 to 0.040M, e.g. about a 0.025 molar solution. UV stabilizers such as Uvinul™ 400, such as at approximately 5% weight by volume, can also be used in the solutions of the present invention. As explained below, such UV stabilizers are more preferably used in connection with some of the solvents of the present invention than others. The most preferred electrochemichromic solution of the parent application comprises one of the five solvents mentioned, from 0.02 to 0.03M, e.g. about 0.025 molar methylviologen hexafluorophosphate, from 0.02 to 0.03M e.g. about 0.025 molar tetrabutylammonium hexafluorophosphate, and from 0.02 to 0.03M, e.g. about 0.025 molar 5,10-dihydro-5,10-dimethylphenazine (DMPA). Figure 2 illustrates an electrochemichromic cell 1 which comprises a pair of glass plates 10 and 11 each coated on its inwardly facing surface with a half wave indium tin oxide (ITO) coating 12 of about 15 ohms/square sheet resistance. Plates 10 and 11 are separated by peripheral seal 13 so that the interior of the cell has a thickness of 150 microns. Cell 1 is sealed at its perimeter by peripheral seal 13. Seal 13 comprises an epoxy material, to which 150 micron diameter spacers are added, and silk-screened to a thickness of about 150 microns. Glass beads are used as spacers. As shown, cell 1 is intended to be used as a mirror, and thus the rear surface of glass plate 11 is coated with a silver reflector layer 14. If the device were used as a window, layer 14 would be deleted. The conductive indium tin oxide layers 12 are connected to electrical terminals 15 and 16 so that a voltage can be established across a solution located between plates 10 and 11 in cell 1. To vacuum backfill cell 1, a small gap is introduced into seal 13 at some extremity corner. This acts as a fill hole. Solution can be filled through this hole and once inside the cell, the solution is contained by seal 13 between glass substrates 10 and 11. It is desirable to use a small fill hole so that the entrance orifice is small. Otherwise, it is difficult to seal the fill hole once the cell cavity is full such that no leaks occur through the fill hole. But since the fill hole is small, less than 1mm X 1mm X 150 microns typically, it is difficult to fill the cell cavity using a hypodermic needle or the like. Also, since there is only one fill hole, back pressure would impede complete filling through one fill hole anyway. Thus a means is needed to fill such a cell cavity that overcomes the above problems. Vacuum backfilling is such a means. In the vacuum backfill technique, the empty cell is placed in a vacuum chamber along with a container (typically a dish or small cup) of the electrochemichromic fluid intended to be filled through the single fill hole into the cell cavity. The chamber is evacuated to a high vacuum, 1mm Hg or better. Means are then used to lower the fill hole just under the surface of the electrochemichromic fluid. The chamber is now vented to atmospheric pressure (typically using nitrogen or similar inert gas). Atmospheric pressure forces the fluid into the cell cavity and so fills it. However, how completely it fills is a function both of the vacuum pressure upon evacuation PV and the atmospheric pressure PA to which the chamber is vented during venting. Although a vacuum pump can evacuate a vacuum chamber to 10-6 mm Hg or better, the vapour pressure of the solvent limits how high a vacuum can be achieved. This is because the vacuum pump reduces the vacuum pressure down to the vapour pressure (at the temperature of the chamber) of the fluid used. Once the vacuum pressure equals the vapour pressure, vacuum pressure will go no lower until all the fluids have evaporated. Thus the choice of solvent, through its vapour pressure, dictates how large a bubble may remain after backfilling a given cell volume. As the device area increases, which might be encountered in window devices, the problem gets worse and, unless a sufficiently low vapour pressure solvent is chosen, or unless means such as cooling the fluid and chamber (to reduce vapour pressure) or overpressuring during backfill (to force more fluid in) are employed, a cosmetically unacceptable bubble will be left within the electrochemichromic cell. While a small bubble of about 1mm diameter may dissolve over time, a larger bubble will not completely disappear. Further, if the viscosity of the fluid to be filled is very high, then it may be difficult to fill at room temperature. If higher filling temperatures are used, the residual bubble may be larger as the vapor pressure increases with temperature. Simple physics teaches that: P A V A = P V V V where P A = pressure to which the chamber is finally vented; V A = volume of gas trapped in the cell after completely filling the cell; P V = vacuum pressure in the chamber after evacuation and prior to filling; and V V = volume of the empty cavity, i.e., cell volume. Since undissolved gas trapped in the cell after incomplete filling will usually form a bubble, then V A can be written as: V A = π/4 d 2 t where d is the bubble diameter; and t is the cell cavity thickness. Also, P A is usually 760mm Hg although it is important to stress that the chamber can be overpressured to several atmospheres or more after filling if it is desired to fill more completely. However, in the case where P A = 760 mm Hg and where V V = A x t where A is the cell area and t is the interpane thickness, we have: P V A t = 760 π/4 d 2 t which reduces to P V = 5.969 d 2 /A where d is in mm and A is in cm 2 Likewise d = (P V x A)/5.969 Equation (4) expresses the relationship between the residual gas bubble diameter d (in mm) and the cell area (in cm 2 ) to the pressure in the chamber, P V , prior to venting to atmosphere and thus backfilling. Note that if two solvents or more are mixed together to form an ideal solution, the vapour pressure of the solution is simply the sum of the vapour pressures of each component. The solvents taught in this invention can have very low vapour pressures, in some cases exceptional so that they are excellent choices for use as solvent components in electrochemichromic solutions intended to be vacuum backfilled. This is particularly important when large area devices such as 1 m 2 windows where the volume of cell cavity can be as large as 150 cc or thereabouts. By contrast, many of the prior art solvents, such as acetonitrile, methylethylketone, and dimethylformamide are unsuitable choices, even for use as components in solvent mixtures. Also, the solutions used as electrochemichromic fluids are preferably sufficiently dilute for the various solutes (anodic/cathodic compounds, electrolyte, etc.) not to significantly depress vapour pressures. Prior art lower boiling point solvents such as acetonitrile, dimethylformamide and methylethylketone tend to have relatively high vapour pressures at room temperature. Thus, the higher boiling point solvents of the present invention, which tend to have lower vapour pressures at room temperature, may be significantly more suitable for the vacuum backfilling technique as they may tend to leave smaller bubbles in the filled cell. 2-Acetylbutyrolactone (ABL) is most desirable, since its boiling point is so high that it is measurable at atmospheric pressure only with great difficulty. Even at 5mm Hg (.0066 Atm), it boils at 107°C. Thus, ABL vapour pressure is so low that it is the most preferred of the solvents of this invention when employing vacuum backfilling. JP-A-6310133 discloses a method of filling an electrochromic display element including immersing the element into an electrolytic solution under low pressure and then increasing the pressure above atmospheric pressure to fill the element cavity. US-A-4753276 discloses a method for injecting liquid crystal material into a display device including placing the device, with its fill opening uppermost, and a vessel containing the liquid crystal material in a chamber which is then subjected to a vacuum. The fill opening is then connected with the liquid crystal material. The level of the liquid crystal material is then varied relative to the fill opening as an inert gas is admitted to the chamber under control in order to regulate the pressure difference between the inside of the display device and atmosphere as the device is filled with the liquid crystal material. US-A-3701368 discloses a method of fabricating a liquid crystal device including admitting liquid crystal material through openings at both ends of the device. The walls of the device are caused to bow outwardly and inwardly to vary the flow path of the material into the device. The method of the present invention is defined in the accompanying claims 1 and 5 and preferred features in the claims respectively dependent thereon. Preferred solvents for the electrochemichromic solution include : 3-hydroxypropionitrile and 2-methylglutaronitrile in a ratio by volume of from 75:25 to 25:75; 3-hydroxypropionitrile and 3-methylsulpholane in a ratio by volume of from 75:25 to 25:75; 3-hydroxypropionitrile and 3,3'-oxydipropionitrile in a ratio by volume of from 75:25 to 25:75; 3-hydroxypropionitrile and 2-acetylbutyrolactone in a ratio by volume of from 75:25 to 25:75; 2-acetylbutyrolactone and 3,3'-oxydipropionitrile in a ratio by volume of from 75:25 to 25:75; and propylene carbonate and 2-acetylbutyrolactone in a ratio by volume of from 75:25 to 25:75. The solvent suitably comprises at least 25% by volume 2-acetylbutyrolactone (ABL). More preferably the solvent comprises: 3,3'-oxydipropionitrile and 2-acetylbutyrolactone in a ratio of from 75:25 to 25:75. In order to at least partially fill the electrochemichromic device, e.g. a cell (or a window or mirror), the device having at least two (e.g. relatively closely) spaced apart plates, each having an inwardly facing conductive surface, the spaced apart plates being sealed (such as around the perimeter) by a seal, a suitable method comprises: providing the device with an aperture (e.g. by introducing a small gap such as into the device, e.g. into the seal of an empty cell) for fluid entry; evacuating air from such as into the device, e.g. cell; placing (e.g. by lowering the (evacuated) electrochemichromic device) into a container of electrochemichromic solution such that the aperture e.g. gap, is located underneath a surface of the electrochemichromic solution; exposing the electrochemichromic solution to a source of pressure greater than that inside the device to thereby cause the solution to enter the device; and sealing the aperature (e.g. the gap in the peripheral seal of a cell). The method preferably includes any or all of the following features; evacuating air from the device e.g. cell, comprising placing the device in a vacuum chamber along with the container of the electrochemichromic solution and evacuating the chamber to a vacuum; after exposure subsequently venting the chamber to atmospheric pressure; and/or removing the device from the container prior to sealing. Suitably the vacuum chamber is pressurized to above atmospheric pressure after it has been vented to atmospheric pressure. Preferably the electrochemichromic solution is cooled prior to backfilling (such as liquid entering the device) to reduce its vapour pressure. Alternatively or in addition the electrochemichromic solution is cooled prior to backfilling to reduce its vapour pressure. Another method for at least partially filling an electrochemichromic device of the invention, e.g. a cell, having at least two (e.g. relatively closely) spaced apart plates, each plate having an inwardly facing conductive surface, the spaced plates being sealed (e.g. around the perimeter) to form a sealed cavity, comprises: providing, e.g. by introducing, a pair of (e.g. spaced apart and small) openings in the device, e.g. cell, which are in fluid communication with (e.g. open into) the sealed cavity such as of an empty cell; placing one of the openings in flow communication with an electrochemichromic solution; placing the other opening in flow communication with a vacuum source whereby the solution is drawn into the device, e.g. cell. Suitably the electrochemichromic solution is placed in a syringe which is held (e.g. tightly) to one of the openings so that one of the openings is placed in flow communication with the solution. The present invention may be illustrated with reference to the accompanying drawings, in which: Fig. 1 is a graph of a solar spectrum in the ultraviolet region as determined in Tucson, Arizona U.S.A.; Fig. 2 is a cross-sectional view of an electrochemichromic cell; Fig. 3 is a graph of the percent transmittance of solar radiation at various wavelengths through a piece of glass coated with a half wave indium tin oxide coating; Fig. 4 is a graph of a solar spectrum passed by a piece of glass coated with half wave indium tin oxide; Fig. 5 is a graph of the percent transmittance of solar radiation at various wavelengths for prior art .0002 molar acetonitrile solutions of various cathodic compounds typically used in electrochemichromic cells; Fig. 6 is a graph of the percent transmittance of solar radiation at various wavelengths for prior art .0002 molar acetonitrile solutions of various anodic compounds used in electrochemichromic cells; Fig. 7 is a graph of the percent transmittance of solar radiation at various wavelengths by the solvent ABL that can be used in electrochemichromic solutions; and Fig. 8 is a graph of the percent transmittance of solar radiation at various wavelengths by prior art solvents for electrochemichromic solutions. The invention will now be described by way of example with reference to the accompanying Examples which are provided by way of illustration and are not to be construed as being limiting. COMPARATIVE EXAMPLE 1 The Experimental Data, Tables 1, 2 and 3: Table 1 compares the solvents used in the present invention with three (conventionally suggested) prior art electrochemichromic solvents: propylene carbonate, gamma butyrolactone and dimethylformamide. The first and second columns give the boiling point and freezing point for the various solvents, including those used in the present invention. The third column indicates the appearance of electrochemichromic solutions at zero applied potential in an electrochemichromic cell made by a method in accordance with the present invention. Electrochemichromic cell 1 (Fig. 2) was used for the data contained in the third column of Table 1 and the data in Table 2. The cell area was about 110 cm 2 and thickness was about 150 microns. Sheet resistance of the ITO transparent conductors used in the cell was 15 ohms per square. For Table 2, the cells were powered to 1 volt. Each cell was filled with a solution of the indicated solvent or solvent combination, containing .025 molar methylviologen perchlorate, .025 molar 5,10-dihydro 5,10-dimethylphenazine and .025 molar tetraethylammonium perchlorate unless otherwise indicated in the Table. Conventional techniques were used to ensure the solutions were oxygen free and were anhydrous. Table 2 compares electrochemichromic solutions which are identical in all respects, except that different solvents are used. Propylene carbonate (PC), gammabutyrolactone (GBL), dimethylformamide (DMF) and acetonitrile (AN) prior art, conventional solvents, were compared to 3-hydroxypropionitrile (HPN), 3,3'-oxydipropionitrile (ODPN), 3-methylsulfolane (MS), 2-methylglutaronitrile (MGNT) and 2-acetylbutyrolactone (ABL), used in the present invention. The first four data columns of Table 2 give reflectivity data. Reflectivity is measured in a conventional manner using standard illuminant A and a photodetector that reproduces the eye's photopic response and is expressed as a percentage of incident light which is reflected by the mirror. The first data column discloses the high percentage reflectivity as measured when the electrochemichromic solution is at zero potential and thus is colourless. The second column measures the low percent reflectivity, which is determined when the electrochemichromic solution is coloured at 1 volt applied potential. The third column measures the time in seconds that it takes for the solution to colour from 70% reflectivity to 20% reflectivity. The fourth column indicates in seconds the time it takes for the solution to bleach from 10% reflectivity to 60% reflectivity. The fifth column of Table 2 measures current leakage for the fully coloured solution presented in amperes per square metre. Table 3 discloses the solubility of various UV stabilizers in the solvents of the present invention as compared to a prior art solvent, propylene carbonate. In most instances, the UV stabilizers are substantially more soluble in the solvents of the present invention, the only exception being that Tinuvin P™ is only marginally soluble in any of the solvents and Uvinul N-539™ is mostly immiscible with HPN. HI %R LOW %R Colour 70%-20%R Sec Bleach 10%-60%R Sec Leakage Current A/m 2 PC (prior art) 80.6 8.3 4.5 4.8 7.18 GBL (prior art) 78 15.1 7.1 3.4 5.6 DMF (prior art) 81.3 27.2 8.75 1.54 8.40 AN (prior art) 81 43 1.5 1.5 9.8 HPN 81.5 7.5 3.7 5.43 6.76 ODPN 80.3 6.1 3.7 > 10 2.68 ABL 80.1 6.7 3.9 9.4 3.83 MS 81.5 7.4 5.0 > 10 1.54 MGNT 80.2 7.6 4.5 9.34 3.1 PC/ODPN 75/25 81.4 7.1 4.12 5.51 5.88 50/50 80.7 6.3 3.67 7.84 4.79 25/75 80.9 6.55 4.03 8.86 3.75 PC/ABL 75/25 80.2 7.4 4.07 5.99 7.16 50/50 80.8 6.9 3.89 6.78 5.79 25/75 80.5 6.95 4.25 6.86 5.25 HPN/ODPN 75/25 79.4 6.8 3.84 5.63 6.28 50/50 79.6 6.55 3.51 7.28 4.79 25/75 79.8 6.95 3.78 7.70 4.26 HPN/ABL 75/25 79.1 7.4 4.8 5.97 5.21 50/50 79.0 6.7 4.3 7.98 4.65 25/75 79 7.0 4.6 8.04 4.3 ODPN/ABL 75/25 78.6 6.9 6.1 12.45 2.84 50/50 80.7 6.6 4.54 11.3 3.09 25/75 80.2 7.2 5.7 9.44 3.42 HPN/MGNT 50/50 79.1 7.1 3.52 5.85 4.75 HPN/MS 50/50 79.1 7.0 4.31 7.07 4.48 75/25 80.5 7.3 4.88 4.12 5.2 HPN/ABL/ODPN 35/50/15 80.6 6.7 3.6 6.6 5.25 Solubility of UV stabilizers All data is wt/vol % and at room temperature. Prior Art PC ABL GNT ODPN HPN MGNT Tinuvin P™ 1.7 0.5 0.4 0.7 <0.2 0.9 Uvinul 400™ 11.9 21.5 12.6 7.6 14.9 11.3 Cyasorb 24™ 13.7 33.5 15.5 15.0 20.9 28.6 Uvinul N-539™ 33.6 35.9 35.9 40.2 Immiscible 37.3 Tinuvin P™ = 2-(2H-benzotriazole-2-yl)-4-methyphenyl Ciba Geigy, Hawthorne, New York Uvinul 400™ = 2,4-dihydroxy-benzophenone BASF Wyandotte Corp., Wyandotte, MI Cyasorb 24™ = 2,2'-dihydroxy-4-methoxybenzophenone American Cyanamid Company, Wayne, NJ Uvinul N-539™ = 2-ethylhexyl-2-cyano-3,3-diphenylacrylate (Note: a liquid) BASF Wyandotte, Wyandotte, MI PC = Propylene Carbonate ABL = 2-acetylbutyrolactone GNT = Glutaronitrile ODPN = 3,3'-Oxydipropionitrile HPN = 3-Hydroxypropionitrile MGNT = Methylglutaronitrile 3-Hydroxypropionitrile (HPN): 3-Hydroxypropionitrile has a boiling point of 228°C. and hence can withstand the high temperatures which can be generated by a mirror or the like sitting in the sun (Table 1). Similarly, it has a freezing point of -46 o C. and thus will not freeze in cold winter weather. Electrolytes show excellent solubility, i.e., greater than .05 molar. The solutions are clear in an electrochemichromic cell. Further, 3-hydroxypropionitrile is a relatively inexpensive solvent, thus affording economies which are comparable to that obtained by using propylene carbonate. UV stabilizers, like the electrolytes also show excellent solubility in HPN. This makes it possible to enhance UV stability of HPN electrochemichromic solutions. Both Uvinul 400™ and Cyasorb 24™ show superiorsolubility in HPN as compared to propylene carbonate. HPN electrochemichromic solutions exhibit a high percentage reflectivity in their bleached condition (81.5%, Table 2). Similarly, their reflectivity when coloured is low, i.e., 7.5%. HPN solutions also tend to colour fast (3.7 seconds), and they bleach satisfactorily. One of the most important advantages of HPN solutions over propylene carbonate solutions is their lower current leakage. The HPN solution of Table 2 exhibits leakage of 6.76 amperes per square meter versus 7.18 amperes per square metre for a comparable propylene carbonate solution (Table 2). 3,3'-Oxydipropionitrile: 3,3'-Oxydipropionitrile (ODPN) has a boiling point of 188°C. even at 16mm Hg (.021 Atm) and a freezing point of -26°C. (Table 1). This spread minimizes the probability of either overheating or freezing difficulties in extreme climate conditions. Electrolytes show excellent to good solubility in ODPN (i.e., greater than .05 molar). The same is true for UV stabilizers. The ODPN solutions are clear and colourless in an electrochemichromic cell. Like HPN, ODPN is a relatively economical commodity. Referring to Table 2, it can be seen that ODPN also shows an excellent spread in reflectivity from high to low. It colours rapidly and, while it bleaches somewhat more slowly than HPN solutions, ODPN solutions exhibit a very low leakage current at 2.68 amperes per square meter. Referring to Table 3, it will be seen that Uvinul 400™, Cyasorb 24™, and Uvinul N-539™, all well-known and popular UV stabilizers, show superior solubility in ODPN as compared to propylene carbonate. 2-acetylbutyrolactone (ABL): ABL boils at 107°C. even at a vacuum as great as 5mm Hg (.0066 Atm) and freezes at lower than -33°C. This is an excellent boiling point/freezing point range. The high boiling point and low vapour pressure of this material makes it excellent for vacuum backfilling. ABL also shows excellent self-screening UV characteristics (discussed below). ABL solutions show an excellent spread between high and low reflectivity (80.1 to 6.7 as reported in Table 2). They colour rapidly (3.9 seconds) and bleach fairly rapidly at 9.4 seconds. The current leakage is also desirably low at 3.83 amps per square metre. Referring to Table 3, it will be seen that Uvinul 400™, Cyasorb 24™ and Uvinul N-539™ all show superior solubility in ABL as compared to propylene carbonate. 2-methylglutaronitrile (MGNT): 2-methylglutaronitrile also has an extremely high boiling point. Even at 10 mm of mercury (.013 atmospheres) it boils at 125 to 130°C. Its extremely low freezing point of less than -33°C. gives this solvent excellent environmental range. The high boiling point and low vapour pressure also make it excellent for facilitating vacuum backfilling. Leakage current is extremely low for this solvent at 3.1 amperes per square metre. Even when used 50:50 with HPN in the solutions of Table 2, it has a leakage current of only 4.75 amps per square metre. Similarly, the percent reflectance range for the 50:50 solvent combination is excellent, as are the colour and bleach times (Table 2). 3-methylsulfolane (MS): 3-methylsulfolane boils at 276°C. and freezes at -10 o C. (Table 1). This gives this solvent and its solutions excellent temperature stability. The high boiling point also ensures a relatively low vapor pressure, making this an excellent solvent for use in vacuum backfilling applications. Electrochemichromic solutions based on this solvent exhibit the best low leakage current at 1.54 amperes per square metre. Even in a 50:50 mix with HPN, the Table 2 solutions show a leakage current of 4.48 amperes per square metre. At 75% HPN/25% MS, the leakage current is still only 5.2 amps per square metre. The reflectance range from high to low is very acceptable for this solvent (Table 2). Similarly, the time to colour is fast and although bleach is somewhat slow, the bleach response time would be very acceptable in window applications, particularly large area windows which benefit from the extremely low leakage current of MS (Table 2). Solvent Mixtures: The Table 2 data demonstrates that the solvents used in the present invention also work well in combination with each other and in combination with prior art solvents. Thus, the inherent properties of prior art solvents are enhanced when they are combined with a solvent used in the present invention wherein the combination comprises at least about 25% by weight of one or more of the solvents used in the present invention. The Table 2 results for propylene carbonate alone should be compared to the results achieved for propylene carbonate combined with 25%, 50% and 75% by weight ODPN and ABL. In each case, the combination of propylene carbonate with one of the solvents used in the present invention shows a more desirable leakage current over propylene carbonate per se , without a significant degradation in clear to coloured spread, time to colour or time to bleach. Table 2 also discloses the combination of HPN and ODPN. It can be seen that the properties of this combined solution at 75:25, 50:50 and 25:75 are superior in terms of low leakage current to those of HPN alone. Yet, the coloured to uncoloured light transmission spread is still exceptional. The time to colour and the time to bleach are similarly superior to the performance achieved by ODPN alone. Table 2 further discloses combinations of various other solvents of the present invention. Thus, beneficial combinations are seen involving HPN and ABL, ODPN and ABL, HPN and MGNT and HPN and MS. In all cases, the results in terms of high and low reflectance, time to colour, time to bleach and leakage current are exceptional. Finally, Table 2 illustrates that even more complex mixtures of the solvents of the present invention yield complementary and desirable results. Thus, Table 2 includes data obtained using electrochemichromic solution in 35% HPN, 50% ABL and 15% ODPN. As with other combinations shown in Table 2 involving the present invention, the results are exceptional. Thus by using blends of the solvents used in the present invention either with each other or with prior art solvents, one can obtain a combined solvent with desirable attributes of both. The faster times to colour and bleach of a prior art solvent such as propylene carbonate can be combined with the lower leakage current of solvents such as MS, ODPN or ABL by incorporating at least about 25% of that solvent in accordance with the present invention. Prior Art Solvents: Referring to the prior art solvents, it can be seen that except for gammabutyrolactone (GBL), they all have a relatively high leakage current, i.e., in excess of 7.18 amps per square metre. While GBL has a relatively low leakage current, its low end light transmittance, i.e., transmittance when coloured, is relatively high. In the electrochemichromic mirror as described, it exhibits 15.1% reflectance, as distinguished from less than 10% reflectance for electrochemichromic mirrors made using solvents of the present invention. GBL also has a relatively high vapour pressure, i.e., 3.2mm Hg at 25°C., making vacuum backfilling difficult. Dimethylformamide (DMF) and acetonitrile (AN) performed even worse in terms of percent reflectivity when coloured (i.e., 27.2% and 43% respectively). There is one solvent suggested in the prior art which may perform comparably to the solvents used in the present invention. U.S. Patent 3,806,229 to Schoot suggests the use of glutarodinitrile (glutaronitrile) as a solvent along with acetonitrile, propionitrile, benzonitrile, propylene carbonate, nitromethane and acetic acid anhydride. Glutaronitrile does show reduced current leakage and self-screening UV characteristics comparable to the solvents used in the present invention. However, these favourable properties are totally unappreciated by Schoot and are not disclosed in Patent 3,806,229. Self-Shielding UV Stabilization: The solar spectrum in the ultraviolet (UV) region incident at a desert location such as Tucson, Arizona, is shown in Fig. 1. The Y ordinate is the solar energy expressed in microwatts/cm 2 /100A o band. This solar spectrum will typically pass through an ITO coated glass front piece to irradiate the solution in an electrochemichromic cell 1 as shown in Fig. 2. The transmission of ITO coated glass (0.16 cm or 0.063 inch sodalime coated to half wavelength thickness with 1500A o ITO) is shown in Fig. 3. Thus the solar energy spectrum transmitted into the electrochemichromic fluid is the convolution of Fig. 1 with Fig. 3. This is shown in Fig. 4. The ITO coated glass passes about 55% of the incoming UV solar energy in the 250 to 350 nm region. Thus a substantial portion of the solar UV is unattenuated by the ITO coated glass front piece. This UV radiation passes into the electrochemichromic fluid where it irradiates any electrochemichromic species dissolved therein. As shown in Fig. 5, the cathodically colouring species most commonly used in prior art literature such as methylviologen (MV), ethylviologen (EV), benzylviologen (BV), and heptylviologen (HV) have an absorption peak below 295 nm and thus should be largely nonabsorbing to the solar UV transmitted into the electrochemichromic cell. However, as shown in Fig. 6, anodic compounds, such as dimethyldihydrophenazine (DMPA), diethyldihydrophenazine (DEPA), tetramethylphenylenediamine (TMPD), tetramethylbenzidine (TMBZ) and tetrathiafulvalene (TTF) have substantial UV absorbance in the 250 to 350 nm region. For example, DMPA in 0.0002M solution in acetonitrile (AN) and in a 1 mm pathlength quartz cell absorbs about 22% of the UV solar spectrum passed by ITO coated glass in the 250 to 350 nm region. Thus, it is desirable to shield the electrochemichromic compounds from UV irradiation in this region. The present invention involves the use of one or more solvents which self-screen solutes dissolved therein from the detrimental effects of UV radiation impinging thereon. Specifically, the solvent in a one millimetre path length must transmit no more than about 30% of the solar radiation in the 250 to 350 nm range passed through a typical transparent ITO coated glass substrate. Such a substrate would typically be soda lime glass of approximately .063 inch thickness, coated with a half wave (1500° A) ITO transparent conductive layer. One of the solvents used in the present invention, in addition to acting as solvent for electrochemichromic compounds such that the resulting electrochemichromic solution may cycle well from a high transmitting state to a low transmitting state, may have the additional beneficial property of self-absorbing substantial proportions of the UV solar insulation in the 250 to 350 nm region. Fig. 7 shows the transmission of such solvent, acetylbutyrolactone (ABL). The spectrum is taken in a 1 mm pathlength quartz cell. This 1 mm cell filled with ABL transmits from 250 nm to 350 nm only about 10% of the solar radiation passed by half wave (1500° A) ITO coated standard soda lime glass of a thickness of about 0.16 cm (0.063 inches). This data can be compared to Fig. 8, which shows the UV transmission, in a 1 mm pathlength cell, for various solvents proposed in prior art for use in electrochemichromic solutions. Note that these are mostly completely transmitting in the ultraviolet region in that they absorb very little between 250 nm to 350 nm. For example, propylene carbonate in a 1 mm cell transmits about 87% of the solar energy passed through ITO coated glass between 250 nm and 350 nm; dimethylformanide (DMF) about 89%, acetonitrile (AN) about 100%; and methyethylketone (MEK) about 93%. Thus, ABL may help to extend the UV lifetime of electrochemichromic solutions by shielding the UV fragile electrochemichromic compounds that are solutes in the UV self-screening solvent. Self-screening by the solvent is more effective than screening with a UV inhibiting solute because the solvent is by far the majority component in the solution. For example in a 0.025M solution in ABL, the molarity of the solute is 0.025M while the molarity of the solvent is 9.29M so that there are roughly 370 solvent molecules for every solute molecule in solution. Thus, the probability is greatest that an incoming UV photon may impinge and be absorbed by a solvent molecule (which typically is UV resilient), rather than impinge and be absorbed by a solute molecule (which, in the case of electrochemichromic species, is usually UV fragile and degraded by UV irradiation). Although addition of UV stabilizers such as benzotriazoles, benzophenones, or hindered amine complexes, as known in prior art, can help increase solution stability to UV radiation, there are limitations and disadvantages to addition of UV stabilizers. Because they are held in solutions of low to moderate viscosity, both the UV stabilizer and the electrochemichromic solution species it is intended to stabilize are free to randomly move about in the solution. Thus, an incoming photon of UV radiation may impinge and thus degrade an electrochemichromic solute species rather than a UV absorber in solution. Also, solvent solubility places limits on the amount of UV stabilizer that can be added. Since UV stabilizers typically have molecular weights in the 250 to 400 range, the molarity of UV stabilizer in solution is typically around 0.2M or less if the stabilizer concentration is 5% wt/volume. Thus UV stabilizers outnumber solute by about 10 to 1 but the solvent outnumbers solute by about 350 to 1 and thus the inherent self-screening achievable by the solvent ABL, working in conjunction with dissolved stabilizer, can help enhance the UV stability of electrochemichromic devices that use these types of UV self-screening solvents. COMPARATIVE EXAMPLE 2 (Prior Art DMF): A self-erasing electrochemichromic cell solution was prepared based on the teaching of Shelepin, Elektrokhimya , 13(3) , 404-408 (March 1977). This consisted of: 0.05M Methylviologen perchlorate 0.05M 5,10-dihydro-5,10-dimethylphenazine 10% weight/volume polymethylmethacrylate (90,000 average molecular weight) dissolved in dimethylformamide (DMF). In addition, 0.05M tetraethylammonium perchlorate was added as inert current carrying electrolyte as taught in Manos U.S. Patent 3,451,741 (June 24, 1969). The solution was prepared under oxygen-free conditions and anhydrous argon gas was bubbled through the solution to further deoxygenate the solution. A roughly 23 cm x 5.6 cm rectangular cell was fabricated according to the construction shown in Fig. 2. The cell cavity was formed by silk-screening a roughly 2 mm x 150 micron epoxy seal around the edge perimeter of one of the ITO transparent conductive coated glass substrates shown in Fig. 2. Sheet resistance for the ITO transparent conducting coating used on both substrates was about 15 ohms/square. Prior to its silk-screening, glass beads of nominal diameter 150 microns were mixed with the epoxy. Before curing of the epoxy, the second ITO coated glass substrate was contacted to the epoxy seal and the now laminated construction was baked in an oven to cure the epoxy. A small gap of approximately 2 mm x 1 mm x 150 micron dimension had been allowed in the epoxy seal so that, upon lamination, a small fill hole was available close to one corner of the seal through which fluid could flow during the vacuum backfilling process. Attempts at room temperature to vacuum backfill this solution failed. When vacuum was applied, the DMF-based solution boiled and could not be filled into the cell cavity. With this prior art solution, two fill holes were drilled through the face of one of the ITO coated glass substrates so that fluid could be filled into the cell cavity using suction at one hole to pull solution from a syringe tightly held to the other hole. Each hole was of approximately 1 mm diameter. For this construction, no fill hole was allowed in the epoxy seal. After the DMF-based electrochemichromic solution was filled into the cell cavity using suction pull through from a syringe, the holes drilled through the glass substrate were plugged with epoxy. Using this nonvacuum backfilling technique, the prior art DMF solution could be successfully filled into the cell cavity. This filling technique, although practical at a laboratory or prototype level, has disadvantages for commercial devices which include difficulties in securely plugging the relatively large fill holes drilled through the glass substrate. Consistent with prior art teachings, electrochemichromic windows and mirrors, produced as described above and using the DMF-based formulation from prior art, were found to have the variable transmission (or variable reflection in the case of mirrors), cycle lifetime and colouration efficiency required to render single-compartment, self-erasing, solution-phase electrochemichromic devices commercially practical. For example, a roughly 129 cm 2 window was constructed of dimension 23 cm x 5.6 cm x 150 microns cell thickness. When filled with the prior art DMF-based formulation, and where a silver mirror reflector was placed behind this window, the reflectance from the mirror, which initially was 81.3%R, dimmed rapidly to about 27.2%R as measured at the centre of the rectangular device. To dim the mirror reflectance, a potential of 1 volt was applied to bus bars that ran lengthwise along the outer perimeter of the ITO coated transparent substrates that sandwiched the DMF-based electrochemichromic solution. Upon removing the applied potential, the electrochemichromic solution self-erased back to a clear state so that the mirror reflectance returned to 81.3%R. Alternatively, the cell could be more rapidly bleached by shorting the electrodes. Cycle lifetime was established by applying 1 volt potential across the electrochemichromic solution for 30 seconds to dim the transmission, followed by shorting the cell electrodes for 30 seconds to bleach back to the clear state. This colour for 30 seconds followed by bleach for 30 seconds cycle was continued for over 10,000 cycles. Colouring efficiency was maintained; the clear state reflectivity remained high while the cell continued to dim in its centrer to about 27%R. However, there are three significant disadvantages to using this prior art DMF-based formulation for commercial applications. The large leakage current which was in excess of 8A/m 2 would lead to undesirable power drain in practical devices and particularly in large area window or mirror devices. Also, although coloration was efficient as seen by the deep coloration close to the bus bars, coloration was very nonuniform, even for this relatively small window of 129 cm 2 area. Also, although thickener was added as suggested by prior art to limit segregation, segregation was nevertheless present even after relatively modest prolonged colouration. For these reasons, coupled with the impracticality of using vacuum backfilling, this prior art DMF-based solution was seen to be inferior to mirror and window devices made possible by the solutions of this present invention. EXAMPLE 3 (HPN Solution): A self-erasing electrochemichromic solution was formed of: 0.025M Methylviologen perchlorate 0.025M 5,10-dihydro-5,10-dimethylphenazine 0.025M Tetraethylammonium perchlorate 5% weight/volume 2,4-dihydroxy-benzophenone (UV stabilizer "Uvinul 400™) dissolved in hydroxyproprionitrile (HPN). This solution was filled using vacuum backfilling into an interior rearview mirror shaped window constructed as per Fig. 2 of length about 24 cm and width about 5 cm, and of cell area about 110 cm 2 . The interpane gap was 150 microns. Glass coated with ITO of sheet resistance 15 ohms/square and greater than 85% visible transmittance was used. A silver mirror reflector was placed behind the window. Without any applied voltage, the cell was clear and colourless and the reflectance from the mirror was about 81.5%R. When 1 volt potential was applied across the cell, reflectance of the mirror was reduced to 7.5%R, as measured at the center of the window device. Colour transition time from 70%R to 20%R was 3.7 seconds. When the electrodes were shorted, bleach time from 10%R to 60%R was 5.4 seconds. Colouration was both efficient and satisfactorily uniform. Leakage current was about 6.8 A/m 2 . After prolonged coloured for 30 minutes, segregation performance as evidenced by a blue band adjacent to the cathodically powered bus bar and a yellow/brown band adjacent to the anodically coloured bus bar was small. Segregation performance and unformity were greatly improved over that seen in Comparative Example 2, even though no additional thickening agents such as are taught to be necessary in Shelepin, supra Comparative Example 2, and in Byker European Patent Publication 240,226 were used. Nor was the use of a high concentration of current-carrying salt necessary, such as is taught to be necessary for commercial practicality of the solutions taught in Byker European Patent Publication 240,226. The HPN-based formulation has the colouring efficiency and uniformity required to be commercially practical and it showed unexpectedly excellent cycle lifetime. Cells fabricated as described in this example have been cycled in excess of 100,000 cycles without any significant deterioration in the performance described above. Each cycle consisted of 30 seconds colour at 1V applied, and 30 seconds bleach at 0V applied, i.e., with the electrodes shorted. The cell is undamaged when subjected to prolonged colouration. Performance is maintained after baking at 85°C. for two weeks. Cells are not damaged by prolonged storage at low temperatures of -20 o C. or lower. The formulation described here is sufficiently UV stable, at least for use in the interior cabin of an automobile. EXAMPLE 4 (ABL Solution): A self-erasing electrochemichromic solution was formulated as described in Example 3, but using 2-acetylbutyrolactone (ABL) as the solvent. When filled into a cell as described in Example 3, and with a silver mirror reflector placed behind the window, mirror reflectance was 80.1%R in the clear state, which dimmed to 6.7%R when 1 volt was applied. Colour time to dim from 70%R to 20%R was 3.9 seconds. Leakage current was about 3.8 A/m 2 . Bleach time from 10%R to 60%R was 9.4 seconds and thus was adequate for an automotive rearview mirror application, and very acceptable in a window application. Colouring efficiency and colouring uniformity were excellent, as was segregation performance which was exceptionally good. Cells formulated according to this example have excellent cycle lifetime with in excess of 86,000 30 second colour; 30 second bleach cycles tested without any significant deterioration in performance. The high temperature, low temperature, and UV performance for this solution are similar to that reported above in Example 3. The low leakage current discovered in ABL solutions makes this formula particularly well suited for use in large area windows and mirrors where voltage drops across transparent conductors due to excessive leakage currents leading to undesirable and commercially impractical nonuniform colouration along with excessive segregation. EXAMPLE 5 (50:50 HPN/ODPN): A self-erasing electrochemichromic solution was formulated as described in Example 3, but using a mixture of 50% by volume HPN and 50% by volume ODPN as solvent. Using this solvent mixture, this solution was filled into a cell as described in Example 3. With a silver mirror reflector placed behind the window so formed, the initial reflectance of 79.6%R dimmed to about 6.6%R when 1 volt was applied across the cell. Colour time from 70%R to 20%R was 3.5 seconds. Moreover, the bleach time from 10%R to 60%R was about 7.3 seconds which is intermediate between the 5.4 seconds found using pure HPN and the greater than 10 seconds found using pure ODPN. Leakage current was about 4.8 A/m 2 . Thus, a solvent that shows the surprisingly and unexpectedly low leakage current found with ODPN can be proportionately combined with a higher leakage current solvent such as HPN of this invention or propylene carbonate from prior art, so that the leakage current of the resultant mixture can be customized to suit the commercially desirable performance of the specific product involved. Since a low leakage current solvent gives better colour uniformity and lower segregation, but typically also leads to a slower bleach response, solvents such as HPN and ODPN can be mixed to yield the optimum compromise between colour uniformity and segregation performance and bleach response time. Electrochemichromic solutions, as described in this example, that utilize a 50:50 mixture of HPN and ODPN have the commercially required high temperature, low temperature, and UV performance required for commercial use. Their cycle lifetime is excellent. They show no significant change in performance after 48,000 cycles at +25 o C., 6,000 cycles at +40 o C., and 6,000 cycles at -20 o C., each cycle consisting of colouring at 1 volt applied potential for 15 seconds, and 0 volt applied potential for 15 seconds. EXAMPLES 6 to 8 (ODPN, MS and MGNT): Solutions were formulated, and devices fabricated and tested as described in Example 3, but using oxydipropionitrile (ODPN) as the solvent. Excellent cycle lifetime, colouring efficiency, colouring uniformity, high temperature, low temperature, and ultraviolet performance was achieved. Likewise, excellent performance was recorded with the other solvents novel to this invention, 2-methylglutaronitrile and 3-methylsulpholane, whether used as pure solvents or as mixtures among themselves, or with HPN and ABL, or with prior art solvents such as propylene carbonate. COMPARATIVE EXAMPLE 9 (Prior Art PC): To illustrate the benefit of customising leakage current so that coloUration uniformity, low segregation, and bleach response is optimized, square windows of dimension 14 cm x 14 cm x 150 micron cell thickness were fabricated according to the construction schematically shown in Fig. 2. A window so constructed that used ITO of sheet resistance about 25 ohms/square was filled with a solution comprising: 0.025M Methylviologen perchlorate 0.025M 5,10-dihydro-5,10-dimethylphenazine 0.025M Tetraethylammonium perchlorate in pure propylene carbonate. Bus bars were attached around the perimeter edges and a potential of 1 volt was applied. At rest potential, the electrochemichromic window so formed was about 86% transmitting. This window coloured deeply immediately adjacent to the bus bars, but did not colour in the centre, such that such a window would be commercially unacceptable. Also, when this window was prolonged coloured at 1 volt for 15 minutes, very significant segregation of the reduced cathodic species to the one bus bar and the oxidized anodic species to the other bus bar was seen. When another cell was filled with this solution, but this time using ITO of sheet resistance about 15 ohms/square as the transparent conductors that sandwiched the electrochemichromic solution, the centre of the window still failed to dim appreciably when 1 volt was applied. The centre dimmed only to about 40%T (although, as can be expected given the lower sheet resistance of ITO used, the coloured region closer to the bus bars increased somewhat in area, while the central nondimmed area proportionally decreased in size). Segregation after prolonged colouration at 1 volt for 15 minutes was improved over what was seen as described above when this solution had been used in a cell that utilised 25 ohms/square ITO but was nevertheless still significant. EXAMPLE 10 (ODPN in 15 ohms/square ITO Cell): By contrast, when a similar cell to that described in Comparative Example 9 was filled with equivalent electrochemichromic solution, but this time using the ODPN and using 15 ohms/square ITO, the central region dimmed appreciably (down to 14%T) and uniformly such that the window would be commercially practical. Segregation after prolonged colouration at 1 volt for 15 minutes for the ODPN-based solution was only slight to negligible and was demonstrably superior to the windows described above that utilized propylene carbonate based solutions. Applications such as large area architectural and automotive windows, office partition panels, and large area mirrors become practical using the low leakage current solvents, such as ODPN, of this invention. EXAMPLE 11 (Ethylviologen in HPN/ODPN): A self-erasing, electrochemichromic solution was formulated comprising: 0.025M ethylviologen perchlorate 0.025M 5,10-dihydro-5,10-dimethylphenazine 0.025M Tetraethylammonium perchlorate 5% weight/volume 2,4-dihydroxy-benzophenone (UV stabilizer Uvinul 400™ dissolved in a 50:50 hydroxypropionitrile (HPN)/oxydipropionitrile (ODPN) mixture. When filled into a 24 cm x 5 cm x 150 micron cell, as described in Example 2, a silver mirror reflector placed behind the window so formed had a reflectivity of 80.1%R which dimmed to 6.7%R when 1 volt was applied across the ITO transparent conductors (of 15 ohms/square sheet resistance) used. Colouration was rapid (3.4 sec) and bleach response was satisfactory. Excellent coloration efficiency and colouration uniformity were maintained after cycle lifetime testing in excess of 60,000 cycles; each cycle consisting of 1 volt applied for 30 seconds, followed by OV applied for 30 seconds. EXAMPLE 12 (TMPD Anodic Material In HPN/ODPN): A self-erasing electrochemichromic solution was formulated comprising: .035M methylviologen perchlorate .035M N,N,N1,N1-tetramethyl-1,4-phenylenediamine .035M Tetraethylammonium perchlorate 5% weight/volume Uvinul-400™ dissolved in a 50:50 mixture of hydroxypropionitrile (HPN) and oxydipropionitrile (ODPN). When an electrochemichromic window wasassembled, as essentially described in Example 3, the clear, zero potential transmission was about 81%T and this decreased to about 11%T when a potential of 0.6V was applied across the cell. Colouration from 70% to 20%T took about 7.3 seconds, bleach from 11%T to 60%T took about 7 seconds. Upon fully bleaching at zero potential, the transmission returned to the clear, high transmitting state. When repetitively cycled at 0.6V for 30 seconds followed by 0V for 30 seconds, the performance cited above was essentially maintained. EXAMPLE 13 (TTF Anodic Material In HPN/ODPN): A self-erasing electrochemichromic solution was formulated comprising: .025M methylviologen perchlorate .025M Tetrathiafulvalene .025M Tetraethylammonium perchlorate dissolved in a 50:50 mixture of hydroxypropionitrile (HPN) and oxydipropionitrile (ODPN). When an electrochemichromic window was assembled, as essentially described in Example 3, the clear, zero potential transmission was about 80.3%T. When a potential of 1.0V was applied across the cell and with a silver mirror reflector behind the window, the mirror reflectance dimmed from its initial high reflectance state of 80.3%R down to a low reflectance state of 5.8%R. Colouration time from 70% to 20%R was 3.2 seconds; bleach from 10%R to 60%R took 7.1 seconds. EXAMPLE 14 (HPN/ABL-Variable Transmission): A window was formed as described in Example 3 consisting of: 0.025M Methylviologen perchlorate 0.025M 5,10-dihydro-5,10-dimethylphenazine 0.025M Tetraethylammonium perchlorate in a 50:50 mixture of hydroxypropionitrile (HPN) and acetylbutyrolactone (ABL). This cell was powered at various voltages from 0V to 1.2V. The transmission at the centre of this window, at various applied voltages, is shown in Table 4. Applied Voltage Volts % Transmission 0V 78.9 0.2V 78.9 0.6V 46.2 0.7V 31.4 0.8V 21.4 0.9V 14.8 1.0V 11.3 1.1V 8.6 1.2V 7.3 As can be seen from the Table, % transmission can be varied between 78.9%T and 7.3%T by appropriately selecting the applied voltage. This ability to operate as a grey scale was found in all the novel solvents and solvent mixtures disclosed in this invention, and is consistent with prior art teachings and with the intrinsic properties of the electrochemichromic species themselves. EXAMPLE 15 (HPN): A self-erasing electrochemichromic solution was formed of: 0.035M Methylviologen hexafluorophosphate 0.035M 5,10-dihydro-5,10-dimethylphenazine 0.035M Tetrabutylammonium hexafluorophosphate dissolved in hydroxypropionitrile (HPN). This solution was filled using vacuum backfilling into an interior rearview mirror shaped window constructed as per Fig. 2 of length 24 cm and width 5 cm, and of cell area 110 cm 2 . The interpane gap was 150 microns. Glass coated with ITO of sheet resistance 15 ohms/square and greater than 85% visible transmittance was used. A silver mirror reflector was placed behind the window. Without any applied voltage, the cell was clear and the reflectance from the mirror was about 78.8%R. When 1 volt potential was applied across the cell, reflectance of the mirror was reduced to 5.8%R, as measured at the center of the window device. Colour transition time from 70%R to 20%R was 3.8 seconds. When the electrodes were shorted, bleach time from 10%R to 60%R was 5.6 seconds. Colouration was both efficient and satisfactorily uniform. The HPN-based formulation has the colouring efficiency and uniformity required to be commercially practical and it showed unexpectedly excellent cycle lifetime. Cells fabricated as described in this example were cycled without any significant deterioration in the performance described above. Each cycle consisted of 30 seconds colour at 1V applied, and 30 seconds bleach at 0V applied, i.e., with the electrodes shorted. The cell is undamaged when subjected to prolonged colouration. Performance is maintained after baking at 85° C. for two weeks. Cells are not damaged by prolonged storage at low temperatures of -20°C. or lower. The formulation described here is sufficiently UV stable, at least for use in the interior cabin of an automobile. COMPARATIVE EXAMPLE 16 and EXAMPLES 17 and 18 (Commercial Cell Comparison): The practical benefit of these concepts can be illustrated by comparing the UV stability of a rearview mirror according to the invention to the UV stability of a commercially available electrochemichromic rearview mirror. The particular commercially available electrochemichromic mirror tested was an interior rearview mirror purchased from General Motors spare parts around July 1989 and it was marked A105/1.16 on its rear surface. (Comparative Example 16). Analysis of these commercially available mirrors shows that their solutions contain benzylviologen (BV) and 5,10-dihydro-5,10-dimethylphenazine (DMPA) in propylene carbonate and also contain a benzothriazole UV stabilizer. Our electrochemichromic rearview mirrors consisted of: 0.025M methylviologen perchlorate; 0.025M dimethydihydrophenazine; 0.025M tetraethylammonium perchlorate; 5% by weight 2,2'-dihydroxy-4-methoxybenzophenone (Cyasorb 24™) as UV stabilizer all dissolved in 50% HPN:50% ABL (Example 17) and in 50% ABL:50% ODPN (Example 18). All three mirrors were exposed for 89 hours to a xenon arc lamp and were irradiated with UV radiation that closely simulated the solar UV intensity. The integrated intensity from 250 nm to 400 nm was around 70 watts/M 2 . Results were: Initially HI %R LOW %R Color 70%-20%R Sec Bleach 10%-60%R Sec 16. Commercially Available ECCM 79.9 6.6 2.95 4.22 17. HPN/ABL 50/50 80.9 8.1 2.06 8.16 18. ABL/ODPN 50/50 81.7 8.9 2.39 12.22 89 Hour UV Exposure 16. Commercially Available ECCM 59.6 7.6 2.72 6.05 17. HPN/ABL 50/50 80.6 6.6 1.66 7.64 18. ABL/ODPN 50/50 79.6 9.4 2.55 11.62 The mirrors of the present invention performed remarkably better than that commercially available formulation in that they maintained their high reflectance state of about 80%R, whereas the commercial product dropped its zero potential reflection to only about 60%R, principally due to its yellowing.

Claims: A method for filling a large area electrochromic device having an electrochromically active area of at least about 110 cm 2 , including two spaced apart plates, each plate having an inwardly facing conductive surface, said spaced plates being separated around their peripheries by a peripheral seal, said peripheral seal enclosing an area of each of said plates to define a cavity within said device; said filling method comprising: introducing a small gap into said seal; placing said device in a chamber along with a container of a liquid electrochromic medium and evacuating said chamber; lowering said cell into said container of liquid electrochromic medium such that said small gap is located under the surface of the liquid electrochromic medium; said electrochromic medium comprising an organic solvent having a vapour pressure of less than 3.2mm of mercury at 25°C; exposing said electrochromic medium to a source of inert gas of pressure greater than that in said cavity within said device to thereby cause said medium to flow into said cavity of said device; and sealing said gap in said peripheral seal of said device. A method as claimed in claim 1 wherein: evacuating said chamber comprises placing said one device in a vacuum chamber along with said container of said electrochromic medium and evacuating said chamber to a vacuum; after said exposing step, subsequently venting said chamber to atmospheric pressure; and removing said one device from said container prior to sealing. A method as claimed in claims 1 or 2 wherein said chamber is pressurised to above atmospheric pressure after it has been vented to atmospheric pressure. A method as claimed in any of claims 1 to 3 wherein said liquid electrochromic medium is cooled prior to entering said cavity of said one device by backfilling to reduce its vapour pressure. A method for filling a large area electrochromic device having an electrochromatically active area of at least about 110 cm 2 , and including two spaced apart plates, each plate having an inwardly facing conductive surface, the spaced apart plates being separated around their peripheries by a peripheral seal to form a sealed cavity, the method comprising: providing a pair of spaced, small openings in the device which are in fluid communication with the sealed cavity; placing one of said openings in flow communication with a liquid electrochromic medium; said electrochromic medium comprising an organic solvent having a vapour pressure of less than 3.2mm of mercury at 25°C; placing the other of said openings in flow communication with a vacuum source whereby said electrochromic medium is drawn into the cell. A method of any of claims 1 to 5 wherein said electrochromic medium comprises: a redox chemical pair which can be made coloured or colourless according to an applied voltage. The method of claim 6 wherein said organic solvent is a solvent comprising at least 25% by volume of 3-hydroxypropionitrile (HPN), 3,3'-oxydipropionitrile (ODPN), 2-acetylbutyrolactone (ABL), 2-methylglutaronitrile (MGNT), 3-methylsulfolane (MS) or a mixture thereof. A method as claimed in claims 1-6 wherein said organic solvent comprises two solvents at a ratio of from 75:25 to 25:75 by volume. A method as claimed in claims 1-6 wherein said organic solvent of said electrochromic solution comprises: (a) 3-hydroxypropionitrile and 2-methylglutaronitrile in a ratio by volume of from 75:25 to 25:75: (b) 3-hydroxypropionitrile and 3-methylsulfolane in a ratio by volume of from 75:25 to 25:75; (c) propylene carbonate and 3,3'-oxydipropionitrile in a ratio by volume of from 75:25 to 25:75; (d) 3-hydroxypropionitrile and 2-acetylbutyrolactone in a ratio by volume of from 75:25 to 25:75; (e) 2-acetylbutyrolactone and 3,3'-oxydipropionitrile in a ratio by volume of from 75:25 to 25:75; (f) propylene carbonate and 2-acetylbutyrolactone in a ratio by volume of from 75:25 to 25:75; or (g) 3-hydroxypropionitrile and 3,3'-oxydipropionitrile in a ratio by volume of from 75:25 to 25:75. The method of claim 6 wherein said redox pair of said electrochromic medium includes a viologen species. The method of claim 6 wherein said redox pair of said electrochromic medium includes at least one of a phenazine, a phenyldiamine, a benzidene, or a fulvalene. A method as claimed in any of claims 1 to 4 wherein said inert gas is nitrogen. The method of claim 5 in which said electrochromic medium is placed in a syringe which is tightly held to one of said openings to accomplish said step of placing said one of said openings in flow communication with said medium. The method of any of claims 1 to 13 wherein said electrochromic device is an electrochromic window. The method of claim 14 wherein said electrochromic window is one of an architectural window and an automotive window. The method of any of claims 1 to 14 wherein said electrochromic device is a rear-view mirror suitable for use on a vehicle.

Inventors: DESARAJU PADMA, HABIBI HAMID REZA, LYNAM NIALL RICHARD, VARAPRASAD DESARAJU VENKATAPAN, DESARAJU, PADMA, HABIBI, HAMID REZA, LYNAM, NIALL RICHARD, VARAPRASAD, DESARAJU VENKATAPANDURANGA
Applicants: DONNELLY CORP, DONNELLY CORPORATION
Application year: 1990
Main classification: G02F1
IPC codes: G02F1, C09K9