Resin composition

Abstract: The present invention provides a resin composi­ tion excellent in balance of mechanical strength and superior in solvent resistance and processability which comprises: (a) a polyolefin resin in an amount of 95-50% by weight, (b) a polyphenylene ether resin in an amount of 5-50% by weight, (c) a partially hydrogenated alkenyl aromatic compound-isoprene block copolymer in an amount of 1-7 parts by weight based on totally 100 parts by weight of the components (a) and (b), and (d) an ethylene-o-olefin copolymer elastomer in an amount of 5-30 parts by weight based on totally 100 parts by weight of the components (a) and (b). This composition can be easily molded into articles excellent in balance of properties and having high uniformity and smoothness in appearance.

Description: The present invention relates to a resin composition which shows an especially excellent balance of mechanical properties including mainly rigidity and is superior in processability, oil resistance and chemical resistance. More particularly, it relates to a resin composition for injection molding, extrusion molding or blow molding which comprises a polyolefin, especially, a crystalline polyolefin, a polyphenylene ether resin, a partially hydrogenated alkenyl aromatic compound-isoprene block copolymer and an ethylene-α-olefin copolymer elastomer and is excellent in balance of mechanical properties including rigidity and heat resistance and superior in processability, organic solvent resistance and chemical resistance. Polyolefins are superior in processability, toughness, water resistance, organic solvent resistance and chemical resistance, low in specific gravity and inexpensive and hence have been widely used for production of various shaped articles and sheets. However, they suffer from the problem in heat resistance, which has hindered development of new uses thereof. On the other hand, polyphenylene ether resins have excellent heat resistance, but have difficulties in processability and solvent resistance, which impose limitation on the scope of application. For improvement of processability and impact strength, blends of a polyphenylene ether resin with a styrene resin are utilized, but these have a defect in solvent resistance and are limited, in scope of application. For example, the blend is not suitable in the field which requires resistance to oily solvents such as gasoline. In an attempt to utilize the respective merits of these polyolefin and polyphenylene ether resins and offset their defects, various blend compositions have been proposed. For example, a composition has been proposed for improvement of processability and tensile strength (JP-B-42-7069). However, this composition does not necessarily suffice the relatively high level of mechanical strength which is required in industrial fields. Furthermore, for improving compatibility between polyolefin and polyphenylene ether resins to enhance mechanical strength, for example, a composition to which a styrene-butadiene block copolymer or its hydrogenated product is added (JP-A-53-71158, 54-88960 and 59-100159) and the above composition to which an inorganic filler is added (JP-A-58-103556) have been proposed. According to these proposals, processability and mechanical strength can be improved, but the organic solvent resistance possessed by the polyolefin cannot be sufficiently exhibited for the reasons that the amount of polyolefin added is small or the matrix (continuous phase) comprises a polyphenylene ether resin or a combination of polyphenylene ether resin and styrene resin. Moreover, there has been proposed a composition which comprises polyphenylene ether and a large amount (more than 20% by weight) of polyolefin to which are further added a diblock copolymer or radial teleblock copolymer composed of an alkenyl aromatic compound and a conjugated diene or hydrogenated polymers thereof as a compatibilizing agent (JP-A-58-103557 and 60-76547). That is, it is said that a blend of a low-density polyethylene as polyolefin and a polyphenylene ether resin has been improved in compatibility and can be improved in tensile characteristics and fragility by the addition of a hydrogenated product of an alkenyl aromatic compound - conjugated diene block copolymer. However, improvement only in compatibility is not enough to satisfy various properties required for common resins. For example, the composition disclosed in JP-A-60-76547, namely, a resin composition comprising the three components of a polyphenylene ether, a low-density polyethylene as polyolefin, a component of large amount, and a hdyrogenated product of alkenyl aroamtic compound-conjugated diene block copolymer as a compatibilizing agent for the former two components has limitation in its use owing to its very low rigidity level. Among the above-mentioned combinations, resin compositions which contain polypropylene as polyolefin are somewhat improved in rigidity and heat reistance, but these are still not enough in practical use and further improvement has been desired. It is the object of the present invention to provide resin compositions which can satisfy the balance of mechanical strength of relatively high level and solvent resistance and processability of relatively high level which are required in various uses such as in the field of industrial parts. This object could be achieved on the basis of the finding that a resin composition which shows excellent balance of mechanical properties and is superior in solvent resistance and processability can be obtained by adding a relatively small amount of a hydrogenated product of alkenyl aromatic compound-conjugated diene block copolymer having a specific structure and an ethylene-α-olefin copolymer elastomer to a combination of a polyphenylene ether resin and a polyolefin, preferably crystalline polyolefin. The subject matter of the present invention is a resin composition which comprises: (a) a polyolefin resin in an amount of 95-50% by weight, based on the total weight of (a) and (b), (b) a polyphenylene ether resin in an amount of 5-50% by weight, based on the total weight of (a) and (b), (c) a partially hydrogenated alkenyl aromatic compound-isoprene block copolymer in an amount of 1-7 parts by weight based on a total of 100 parts by weight of the components (a) and (b), and (d) an ethylene-α-olefin copolymer elastomer in an amount of 5-30 parts by weight based on a total of 100 parts by weight of the components (a) and (b). Component (a): Polyolefin resin: Polyolefins used in the present invention include, for example, homopolymers of α-olefins of 3 or more carbon atoms such as propylene, butene-1, pentene-1, hexene-1, 3-methylbutene-1, 4-methylpentene-1, heptene-1, and octene-1, copolymers containing a predominant amount of these α-olefins and at least one other α-olefin including ethylene in the form of a random copolymer or block copolymer and mixtures thereof, copolymers such as random, block, and graft copolymers of a predominant amount of α-olefins of 3 or more carbon atoms and at least one other unsaturated monomer, and oxidized, halogenated or sulfonated products of these polymers. Preferred are those which are at least partially crystalline. As the other unsaturated monomers, there may be used unsaturated organic acids or derivatives thereof such as acrylic acid, methacrylic acid, maleic acid, itaconic acid, methyl acrylate, ethyl acrylate, methyl methacrylate, maleic anhydride, arylmaleic acid imide, and alkylmaleic acid imide; vinyl esters such as vinyl acetate and vinyl butyrate; aromatic vinyl compounds such as styrene and methylstyrene; vinyl silanes such as vinyltrimethylmethoxysilane and γ-methacryloyloxypropyltrimethoxysilane; and non-conjugated dienes such as dicyclopentadiene, 4-ethylidene-2-norbornene, 4-methyl-1,4-hexadiene and 5-methyl-1,4-hexadiene. In case of copolymers, these may comprise not only two of α-olefins or other monomers, but also more than two of them. These polymers can be obtained by polymerization or modification according to known processes and besides, commercially available polymers may be optionally chosen and used. Combination of them can naturally be employed. Among them, preferred are homopolymers of propylene, butene-1, 3-methylbutene-1 or 4-methylpentene-1 and copolymers containing a predominant amount of these monomers. Crystalline propylene polymers, namely, crystalline propylene homopolymer and crystalline propylene copolymers such as propylene-ethylene block or random copolymer are especially preferred from the point of balance in mechanical properties. The melt flow rate (MFR) (230°C, load 2.16 kg) of these crystalline propylene polymers is within the range of 0.01-400 g/10 min, preferably within the range of 0.15-60 g/10 min. If the MFR is less than 0.01 g/10 min, the composition often has problems in processability and if it is more than 400 g/10 min, the level of mechanical strength is low and this is not preferred. Polyolefins include those which have come to have an MFR within the above range by allowing polyolefins having smaller MFR, namely, larger molecular weight to undergo a change in molecular weight according to known method, for example, heat treatment in the presence or absence of a free-radical initiator (organic or inorganic peroxides, organotin compounds, organic azo compounds) or heating and mechanical shearing at melt kneading. Component (b): Polyphenylene ether resin: The polyphenylene ether resin used in the present invention has a recurring unit represented by the following formula: wherein the ether oxygen atom in one unit is linked to the benzene nucleus in the next adjacent unit; n is at least 30; a plurality of R each represents a monovalent substituent selected from the group consisting of hydrogen, halogen, a hydrocarbon group containing no tertiary α-carbon atom, a halohydrocarbon group having at least two carbon atoms between a halogen atom and the phenyl nucleus, a hydrocarbon oxy group and a halohydrocarbon oxy group having at least two carbon atoms between a halogen atom and the phenyl nucleus. Typical examples of polyphenylene ethers are the following and analogues thereof. Poly(2,6-dimethyl-1,4-phenylene) ether, Poly(2,6-diethyl-1,4-phenylene) ether, Poly(2-methyl-6-ethyl-1,4-phenylene) ether, Poly(2-methyl-6-propyl-1,4-phenylene) ether, Poly(2,6-dipropyl-1,4-phenylene) ether, Poly(2-ethyl-6-propyl-1,4-phenylene) ether, Poly(2,6-dibutyl-1,4-phenylene) ether, Poly(2,6-dipropenyl-1,4-phenylene) ether, Poly(2,6-dilauryl-1,4-phenylene) ether, Poly(2,6-diphenyl-1,4-phenylene) ether, Poly(2,6-dimethoxy-1,4-phenylene) ether, Poly(2,6-diethoxy-1,4-phenylene) ether, Poly(2-methoxy-6-ethoxy-1,4-phenylene) ether, Poly(2-ethyl-6-stearyloxy-1,4-phenylene) ether, Poly(2,6-dichloro-1,4-phenylene) ether, Poly(2-methyl-6-phenyl-1,4-phenylene) ether, Poly(2,6-dibenzyl-1,4-phenylene) ether, Poly(2-ethoxy-1,4-phenylene) ether, Poly(2-chloro-1,4-phenylene) ether, Poly(2,5-dibromo-1,4-phenylene) ether. Further examples are copolymers such as a copolymer of 2,6-dimethylphenol and 2,3,6-trimethylphenol, a copolymer of 2,6-dimethylphenol and 2,3,5,6-tetramethylphenol and a copolymer of 2,6-diethylphenol and 2,3,6-trimethylphenol. The polyphenylene ethers used in the present invention further include modified polyphenylene ethers such as polyphenylene ethers defined by the above-mentioned formula on which a styrene monomer (e.g., styrene, p-methylstyrene, and α-methylstyrene) is grafted. Processes for preparation of these polyphenylene ethers have been known as disclosed, for example, in US-A-3306874, 3306875, 3257357, and 3257358, JP-B-52-17880 and JP-A-50-51197. Polyphenylene ethers preferred for attaining the object of the present invention are those which have alkyl substituents in the two ortho positions in respect to the ether oxygen atom and copolymers of 2,6-dialkylphenols and 2,3,6-trialkylphenols. Among them, polymers of 2,6-dimethylphenol are especially preferred. Further, the molecular weight of the polyphenylene ethers in terms of intrinsic viscosity measured in chloroform at 25°C is within the range of 0.2-0.7 dl/g, preferably within the range of 0.25-0.6 dl/g and further preferably within the range of 0.3-0.55 dl/g. If the intrinsic viscosity is less than 0.2 dl/g, the mechanical strength of the composition is insufficient and if it is more than 0.7 dl/g, the processability of the composition is deteriorated. Component (c): Partially hydrogenated alkenyl aromatic compound-isoprene copolymer: The partially hydrogenated alkenyl aromatic compound-isoprene block copolymer used in the present invention is an alkenyl aromatic compound-isoprene block copolymer which has a structure containing at least one chain block "A" originating from the alkenyl aromatic compound and at least one chain block "B" originating from the isoprene and in which the content of aliphatic unsaturated groups in the block B is reduced by hydrogenation. The arrangement of block A and block B includes a linear structure and branched structure, so-called radial teleblock structure. The distribution of the monomer components is not critical and may be uniform or ununiform and furthermore may be tapered with increase or decrease in the amount of monomer components along the molecular chain. Therefore, the respective molecular weights of block A and block B may be the same or different. Moreover, a part of these structures may contain random chains originating from random copolymer portions of alkenyl aromatic compound and isoprene. Among them, preferred are linear structures such as diblock (A-B blocks), triblock (A-B-A blocks, B-A-B blocks), tetrablock (A-B-A-B blocks), pentablock (A-B-A-B-A blocks, B-A-B-A-B blocks) and those which have totally 6 or more A and B blocks. More preferred are diblock, triblock and tetrablock structures and an A-B diblock structure is especially preferred. The alkenyl aromatic compound which constitutes block A has the chemical structure represented by the following formula: wherein R¹ and R² each represents a hydrogen atom or a lower alkyl or alkenyl group of 1-6 carbon atoms, R³ and R⁴ each represents a hydrogen atom, a lower alkyl group of 1-6 carbon atoms, a chlorine atom or a bromine atom, and R⁵, R⁶ and R⁷ each represents a hydrogen atom or a lower alkyl or alkenyl group of 1-6 carbon atoms and R⁶ and R⁷ may be linked together with a hydrocarbyl group to form a naphthyl group together with the benzene ring. Examples of the alkenyl aromatic compounds include styrene, p-methylstyrene, α-methylstyrene, vinylxylene, vinyltoluene, vinylnaphthalene, divinylbenzene, bromostyrene and chlorostyrene and these may also be used in combination. Among them, styrene, α-methylstyrene, p-methylstyrene, vinyltoluene, and vinylxylene are preferred and styrene is more preferred. The proportion of the recurring unit originating from the alkenyl aromatic compound in the partially hydrogenated alkenyl aromatic compound-isoprene block copolymer (c) is preferably more than 20% by weight and at most 80% by weight, more preferably 25-65% by weight. If the proportion is more than 80% by weight, the impact strength of the resin composition is deteriorated to an unsatisfactory level and if it is 20% by weight or less, the rigidity level and heat resistance of the resin composition are insufficient and the object of the present invention cannot be attained. In the aliphatic chain portion of the block copolymer (c), the proportion of unsaturated bonds remaining without being hydrogenated is preferably 50% by weight or less, more preferably 20% by weight or less, further preferably 10% by weight or less. Further, about 25% by weight or less of aromatic unsaturated bonds originating from the alkenyl aromatic compound may be hydrogenated. The hydrogenated block copolymer (c) has a number-average molecular weight (obtained according to the polystyrene conversion method from values measured by gel permeation chromatography) of preferably 5,000-500,000 g/mol, more preferably 10,000-300,000 g/mol, still further preferably 30,000-200,000, especially 45,000-150,000 g/mol. If the number-average molecular weight is more than 500,000 g/mol or less than 5,000 g/mol, production cost is apt to increase. The measurement by gel permeation chromatography was carried out using monodispersed polystyrene as standard material in obtaining relation between elution time and molecular weight. The average molecular weight was in terms of polystyrene. The molecular weight distribution of the hydrogenated block copolymer (c) can be measured by the above gel permeation chromatography, but preferably the molecular weight distribution is not limited and besides the so-called value Q obtained by dividing the value of weight-average molecular weight by that of number-average moelcular weight may be within any range. Moreover, the molecular weight distribution may have not only one peak, but also two or more peaks. Moreover, the block copolymer (c) may be such that it contains, in addition to the component of the peak of main dispersion, a small amount of components of higher or lower molecular weight than that of the component of the peak of main dispersion, in other words, having a shape of molecular weight distribution comprising a peak of main dispersion having the foot descending by a gradual slope. The alkenyl aromatic chain block (block A) and the hydrogenated isoprene chain block (block B) in the hydrogenated block copolymer (c) may be of any molecular weight as far as it satisfies the above-mentioned number-average molecular weight and including any combinations. These hydrogenated block copolymers (c) have a hydrogenated isoprene polymer chain portion and some of them show crystallinity originating from this chain. It is considered that this is because the hydrogenated isoprene polymer chain has a molecular structure similar to a polyolefin. Crystallinity of the hydrogenated block copolymer (c) can be measured by differential scanning calorimeter (DSC). The hydrogenated block copolymers (c) usable in the present invention may be of any crystallinity. The hydrogenated block copolymers (c) may have any glass transistion temperatures based on the hydrogenated isoprene polymer chain portion. The glass transition temperature can be measured by the above-mentioned DSC method or based on the change of viscoelasticity with the temperature measured by a mechanical spectrometer. Many processes have been proposed for producing alkenyl aromatic compound-isoprene block copolymers. Typical processes are disclosed, for example, in JP-B-40-23798, and US-A-3595942 and 4090996. According to these processes, block copolymerization is carried out in an inert solvent such as cyclohexane using e.g. a lithium catalyst or Ziegler catalyst. One of these block copolymers is supplied from Japan Synthetic Rubber Co., Ltd. by the trademark to "TR2400". Hydrogenation treatment of these block copolymers is carried out by hydrogenation in an inert solvent such as cyclohexane in the presence of hydrogenation catalyst according to the processes disclosed in JP-B-42-8704, 43-6636 and 46-20814. As compounds similar to the partially hydrogenated alkenyl aromatic compound-isoprene block copolymer, there are known partially hydrogenated alkenyl aromatic compound-butadiene block copolymers, specifically, hydrogenated styrene-butadiene block copolymers. However, when these copolymers are used, compatibility between polyolefin resin and polyphenylene ether resin is somewhat insufficient and besides, heat resistance such as heat distortion temperature is considerably inferior and the object of the present invention cannot be attained. Component (d): Ethylene-α-olefin copolymer elastomer: The ethylene-α-olefin copolymer used in the present invention has an ethylene content of 30-93 mol%, preferably 35-90 mol%. If the ethylene content is more than 93 mol% or less than 30 mol%, the ethylene-α-olefin copolymer becomes highly crystalline and the impact resistance of the composition cannot be sufficiently improved. Furthermore, the melt flow rate [MFR, measured at 190°C under load of 2160 g (ASTM D-1238 E)] of the ethylene-α-olefin copolymer is within the range of 0.1-50 g/10 min, more preferably within the range of 0.2-20 g/10 min. If the MFR is less than 0.1 g/10 min or more than 50 g/10 min, the effect to improve the impact resistance tends to decrease. The density of the ethylene-α-olefin copolymer is preferably 0.90 g/cm³ or less, more preferably 0.85-0.89 g/cm³. Furthermore, the ethylene-α-olefin copolymer is suitably low-crystalline or non-crystalline and its crystallinity is usually 0-50%, preferably 0-40%. The unit of α-olefin component which constitutes the ethylene-α-olefin copolymer is an α-olefin of 3-18 carbon atoms. Examples thereof are propylene, 1-butene, 1-hexene, 4-methyl-1-pentene and 1-decene. These may be used singly or as mixtures of two or more of them. This ethylene-α-olefin copolymer may further contain a diene component in an amount of 5 mole% or less. Typical examples of the diene component are dicyclopentadiene, ethylidene norbornene and isopropylidene norbornene. Compositional ratio of components The content of polyolefin component (a) in the resin composition of the present invention is 95-50% by weight, preferably 95-55% by weight, especially preferably 95-60% by weight when the total amount of polyolefin (a) and polyphenylene ether resin (b) is assumed to be 100% by weight. If the content is less than 50% by weight, the composition is insufficient in organic solvent resistance and if it is more than 95% by weight, heat resistance is in unsatisfactory level and the object of the present invention cannot be attained. Similarly,the content of polyphenylene ether resin, component (b), is 5-50% by weight, preferably 5-45% by weight and especially preferably 5-45% by weight when the total amount of component (a) and component (b) is assumed to be 100% by weight. If it is less than 5% by weight, the level of rigidity is insufficient and if it is more than 50% by weight, the organic solvent resistance is insufficient. The content of the partially hydrogenated alkenyl aromatic compound-isoprene block copolymer, the component (c), is 1-7 parts by weight, preferably 1-5 parts by weight, and especially preferably 1-4 parts by weight based on a total of 100 parts by weight of component (a) and component (b). If it is less than 1 part by weight, the compatibility between the polyphenylene ether resin and the polyolefin resin is inferior and the mechanical strength such as impact strength is insufficient and if it is more than 7 parts by weight, the thermal properties such as heat distortion temperature are deteriorated. The content of the ethylene-α-olefin copolymer, component (d), is 5-30 parts by weight, preferably 7-25 parts by weight based on a total of 100 parts by weight of component (a) and component (b). If it is less than 5 parts by weight, the level of impact strength is insufficient and if it is more than 30 parts by weight, the level of rigidity is unsatisfactory and the object of the present invention cannot be attained. The resin composition of the present invention may contain, in addition to the above components, auxiliary components as far as the effects of the present invention are not damaged. Examples of these components are antioxidants, weathering modifiers, nucleating agents for polyolefins, slip agents, inorganic or organic fillers and reinforcing agents, flame retardants, various colorants, antistatic agents, releasing agents,and a small amount of a free-radical initiator (e.g. organic peroxides) for molecular weight regulation of polyolefins. Furthermore, plasticizers such as triphenyl phosphate used for polyphenylene resins, and furthermore, fillers such as glass fiber, wollastonite, potassium titanate, whisker, mica, talc, and calcium carbonate are effective for improvement of balance of properties such as rigidity and improvement of processability, dimensional accuracy, and dimensional stability. Method of blending: As method of blending for obtaining the resin composition of the present invention, various methods can be employed which are generally used for blending of resins per se; resins and stabilizers or colorants; or resins and fillers. For example, the respective components in the form of powder or particles are prepared as a homogeneously dispersed mixture in a Henschel mixer, super mixer, ribbon blender or V blender. Then, the mixture is melt kneaded by a twin-screw extruder, single-screw extruder, roll, Banbury mixer, blast mill or melt kneader with Brabender Plastograph. The melt kneading temperature is usually 200-350°C. The thus obtained resin composition can be extruded into pellets after melt kneading. Application of the resin composition of the present invention: The resin composition of the present invention can be easily molded by molding methods generally applied to thermopalstic resins, nemely, injection molding, extrusion molding or blow molding, among which injection molding is most preferred. Because of its good mechanical properties, the composition is suitable for automobile parts, specifically, exterior trim parts such as bumper, door, door panel, fender, ornament, emblem, wheel cover, engine hood, roof, and spoiler, internal trim parts such as instrument panel, console box, and trim, exterior parts of electrical equipments such as television, refrigerator, and so-called office automation equipments. The following nonlimiting examples and comparative examples explain the present invention. Methods for measurement and evaluation: In the following examples and comparative examples, the properties were measured and evaluated under the following conditions. (1) MFR (for indication of flowability): MFR of polyolefin was measured in accordance with JIS K 7210-1975. (2) Flexural modulus (for indication of rigidity): This was measured in accordance with ISO R 178-1974 Procedure 12 (JIS K 7203) using Instron tester. (3) Izod impact strength: This was measured in accordance with ISO R 180-1969 (JIS K 7110) (notched Izod imapct strength) using Izod impact tester manufactured by Toyo Seiki Seisakusho Co., Ltd. (4) heat distortion temperature (for indication of heat resistance): This was measured in accordance with ISO R 75-1958 Method A (JIS K 7207-1974 A) using an injection molded test piece subjected to annealing treatment at 100°C for 30 minutes. Example 1 A propylene homopolymer (SUMITOMO NOBRENE D-501 manufactured by Sumitomo Chemical Co., Ltd.), poly-(2,6-dimethylphenylene) ether (manufactured by Sumitomo Chemical Co., Ltd.), a partially hydrogenated styrene-isoprene block copolymer (hereinafter referred to as "hydrogenated SI") (KRATON G1701X manufactured by Shell Chemical Co.), and an ethylene-propylene copolymer elastomer (ESPRENE E-120 manufactured by Sumitomo Chemical Co., Ltd.) were mixed at a mixing ratio as shown in Table 1 by a super mixer. The resulting mixture was melt kneaded by a twin-screw extruder (TEM-50 manufactured by Toshiba Machine Co., Ltd.) at 260-280°C to obtain pellets. Properties of test piece made from the pellets were measured and the results are shown in Table 1. Comparative Example 1 In the same manner as in Example 1, pellets were prepared from a composition of propylene homopolymer, poly-(2,6-dimethylphenylene) ether and hydrogenated styrene-isoprene block copolymer and measurement of properties was conducted. The results are shown in Table 1. As is clear from comparison of the results of Example 1 with those of Comparative Example 1, the composition obtained from only polypropylene, poly-(2,6-dimethylphenylene) ether and hydrogenated styrene-isoprene block copolymer is low in both the heat distortion temperature and flexural modulus and the composition of the present invention is excellent in balance of properties. Comparative Example 2 Pellets were prepared in the same manner as in Example 1 except that a hydrogenated styrene-butadiene block copolymer (hereinafter referred to as "hydrogenated SB") was used in place of the hydrogenated styrene-isoprene block copolymer. Measurement of properties was conducted to obtain the results as shown in Table 1. As can be seen from comparison of the results of Example 1 with those of Comparative Example 2, when hydrogenated styrene-butadiene block copolymer which was similar to hydrogenated styrene-isoprene block copolymer was used in place of the latter, the resulting composition is low in all of heat distortion temperature, flexural modulus and impact strength while the composition of the present invention is excellent. Comparative Example 3 Pellets were prepared in the same manner as in Example 1 except that the hydrogenated styrene-isoprene block copolymer was not used and measurement of properties was conducted to obtain the results as shown in Table 1. As can be seen from comparison of the results of Example 1 with those of Comparative Example 3, when the hydrogenated styrene-isoprene block copolymer is not used, impact strnegth is extremely low. Examples 2-5 Pellets were prepared in the same manner as in Example 1 except that mixing ratio of the components was as shown in Table 2 and properties were evaluated. The results are shown in Table 2. Components used in Table 2 are as follows: Polypropylene : Homopolymer: SUMITOMO NOBRENE D-501 (trademark) manufactured by Sumitomo Chemical Co., Ltd. Random copolymer: Propylene-ethylene random copolymer [SUMITOMO NOBRENE S-131 (trademark) manufactured by Sumitomo Chemical Co., Ltd.] Block copolymer: Propylene-ethylene block copolymer [SUMITOMO NOBRENE AS-171A (trademark) manufactured by Sumitomo Chemical Co., Ltd.] Polyphenylene ether; Poly-(2,6-dimethylphenylene) ether manufactured by Sumitomo Chemical Co., Ltd.] Hydrogenated SI: KRATON G-1701 (trademark) manufactured by Shell Chemical Co. Ethylene-α-olefin copolymer elastomer EPR(1): Ethylene-propylene copolymer (ESPRENE E-120 manufactured by Sumitomo Chemical Co., Ltd.) EPR-(2): Ethylene-propylene-ethylidene norbornene copolymer (ESPRENE E-501A manufactured by Sumitomo Chemical Co., Ltd.) EB: Ethylene-butene-1 copolymer [ethylene/butene= about 8/2 (weight ratio)] As explained above, the resin composition of the present invention shows an excellent balance of mechanical strength and is good in solvent resistance and processability. The resin composition can be easily processed into shaped articles by molding methods applied to general thermoplastic resin compositions such as injection molding, extrusion molding and blow molding. The resulting articles are very good in balance of properties such as impact resistance, heat resistance and solvent resistance and are excellent in uniformity and smoothness of surface.

Claims: A resin composition which comprises: (a) a polyolefin resin in an amount of 95-50% by weight, based on the total weight of (a) and (b), wherein the polyolefin resin is a crystalline propylene homopolymer or a copolymer containing a predominant amount of α-olefins of 3 or more carbon atoms and has a melt flow rate of 0.01-400 g/10 min, (b) a polyphenylene ether resin in an amount of 5-50% by weight, based on the total weight of (a) and (b) having an intrinsic viscosity of 0.2-0.7 dl/g, measured in chloroform at 25°C and having a recurring unit represented by the following formula: wherein the ether oxygen atom is linked to the benzene nucleus in the next adjacent unit, n is at least 30, a plurality of R each represents a hydrogen atom, a halogen atom, a hydrocarbon group containing no tertiary alpha-carbon atom, a halo-hydrocarbon group having at least two carbon atoms between a halogen atom and the phenyl nucleus, a hydrocarbon oxy group, or a halohydrocarbon oxy group having at least two carbon atoms between a halogen atom and the phenyl nucleus, (c) a partially hydrogenated alkenyl aromatic compound-isoprene block copolymer in an amount of 1-7 parts by weight based on a total of 100 parts by weight of the components (a) and (b), wherein the partially hydrogenated alkenyl aromatic compound-isoprene block copolymer (c) is an alkenyl aromatic compound-isoprene block copolymer which has a structure containing at least one chain block (block A) originating from the alkenyl aromatic compound and at least one hydrogenated chain block (block B) originating from the isoprene in which block A and block B form a linear and branched structure and the content of aliphatic unsaturated groups in block B is reduced by hydrogenation, the alkenyl aromatic compound has the chemical structure represented by the following formula: wherein R¹ and R² each represents a hydrogen atom or a lower alkyl or alkenyl group of 1-6 carbon atoms, R³ and R⁴ each represents a hydrogen atom, a lower alkyl group of 1-6 carbon atoms, a chlorine atom or a bromine atom, and R⁵, R⁶ and R⁷ each represents a hydrogen atom or a lower alkyl or alkenyl group of 1-6 carbon atoms and R⁶ and R⁷ may be linked together with a hydrocarbyl group to form a naphthyl group together with the benzene ring and the content of block A is higher than 20% by weight and at most 80% by weight, and (d) an ethylene-α-olefin copolymer elastomer in an amount of 5-30 parts by weight based on a total of 100 parts by weight of the components (a) and (b), wherein the ethylene-α-olefin copolymer (d) has an ethylene content of 30-93 mol%, α-olefin units of 3-18 carbon atoms, and a melt flow rate of 0.1-50 g/10 min. A resin composition according to claim 1, wherein the polyolefin resin is a homopolymer of an α-olefin of 3 or more carbon atoms, copolymer containing a predominant amount of an α-olefin of 3 or more carbon atoms with at least one other α-olefin, a mixture thereof, copolymer containing a predominant amount of an α-olefin of 3 or more carbon atoms with at least one other unsaturated monomer or oxidized, halogenated or sulfonated product of the above polymer. A resin composition according to claim 1 or 2, wherein the alkenyl aromatic compound of block copolymer (c) is styrene. A resin composition according to any one of claims 1 to 3, wherein the content of unsaturated bonds originating from the aliphatic unsaturated groups in block B remaining without hydrogenation in block copolymer (c) is 50% by weight or less. A resin composition according to any one of claims 1 to 4, wherein the block copolymer (c) has a number-average molecular weight of 5,000-500,000 g/mol. A resin composition according to any one of claims 1 to 5, wherein the ethylene-α-olefin copolymer has a density of 0.90 g/cm³ or less.

Inventors: MARUYAMA TAKASHI, MIZUNO YUKIO, MARUYAMA, TAKASHI, MIZUNO, YUKIO
Applicants: SUMITOMO CHEMICAL CO, SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1990
Main classification: C08L23
IPC codes: C08L53, C08L71, C08L23