Process for the spectral sensitisation of photographic silver halide emulsions and products thereof

Abstract: There is described a process for the spectral sensitisation of photographic silver halide emulsions which comprises forming and chemically sensitising silver halide crystals in a colloid dispersion medium, the process being characterised in that it comprises forming a shell of silver halide on the chemically sensitised crystals by simultaneously adding to the dispersion an aqueous solution of a water soluble halide or pseudo-halide, an aqueous solution of silver nitrate and a J-band aggregating spectral sensitising dye in an aqueous medium, the said simultaneous additions being continued for sufficient time to form a shell of silver halide or pseudo-halide on the said chemically sensitised silver halide crystals which is up to 15 mole percent of the total silver halide or pseudo-halide of the fully grown crystals. It is thought that in the process of the present invention there is formed on the surface of the chemically sensitised silver halide crystal terraces of the halide or pseudo-halide being added, these terraces being separated from each other by steps of high surface energy. The J-band aggregating dye nucleates on these steps and is deterred from recombining. At the end of the process frequently the whole surface of the silver halide crystals is covered with such terraces and steps on which the J-band dyes have nucleated. When such crystals are photo exposed, electron hole recombination is decreased leading to higher photographic speed and low LIRF.

Description: The present invention relates to a process of spectral sensitisation of photographic silver halide emulsions and photographic materials containing these emulsions. It is conventional practice to adsorb the spectral sensitiser at the surface of the silver halide crystals after chemical sensitisation. However, other techniques are also known. Locker et al US Patent 4,225,666 discloses spectral sensitisation during precipitation of silver halide after nucleation has occurred and before completion of silver halide precipitation. Syun et al E.P. Patent 0,069,596 discloses adding a first sensitising dye during chemical sensitisation of the silver halide emulsion and a second sensitising dye after chemical sensitisation. Attention is also drawn to the applicants European Patent 376500 in which it is described how silver halide emulsions are spectrally sensitised by adding a silver salt solution to them until the pAg value reaches a point close to equivalence, then adjusting the pAg value to a value between 7.5 and 10 by addition of halide or thiocyanate, adsorbing a part quantity of a sensitising dye on the silver halide crystals of the emulsions, and repeating these steps once to seven times, and adding the residual quantity of sensitising dye in the last repeat. We have now found that spectral sensitisation and especially Low Intensity Reciprocity Failure (LIRF) can be improved by adsorbing the sensitising dye during concurrent growth of a shell onto the chemically sensitised silver halide crystals. According to the present invention there is provided a process for the spectral sensitisation of photographic silver halide emulsions which comprises forming in and chemically sensitising silver halide crystals in a colloid dispersion medium, the process being characterised in that it comprises forming a shell of silver halide on the chemically sensitised crystals by simultaneously adding to the dispersion an aqueous solution of a water soluble halide or pseudo-halide, an aqueous solution of silver nitrate and a J-band aggregating spectral sensitising dye in an aqueous medium, the said simultaneous additions being continued for sufficient time to form a shell of silver halide or pseudo-halide on the said chemically sensitised silver halide crystals which is up to 15 mole percent of the total silver halide or pseudo-halide of the fully grown crystals. By pseudo-halide is meant an anion which forms an insoluble silver salt which can co-precipitate with a water-soluble halide and which can react with silver nitrate to form water-insoluble crystals or parts of a crystal. In the photographic system a pseudo-halide acts in a similar manner to a halide and can be used to replace or partially replace a halide. Examples of pseudo-halides are alkali metal or ammonium thiocyanate, or alkali metal or ammonium cyanide. The preferred pseudo-halides for use in the process of the present invention are alkali metal thiocyanates. By chemically sensitised is meant the increase in light-sensitivity of the silver halide crystals by the action of certain chemicals such as reducing agents, gold and sulphur compounds. A description of chemical sensitisation is given in the Theory of the Photographic Process by James, 4th Edition (pages 149-158). The preferred chemical sensitisation for the emulsions of the present invention is a combination of sulphur and gold sensitisation. By J-Band aggregating dyes are meant cyanine dyes which self-aggregate producing shifts to longer wavelength and sharper absorption curves than the non-aggregated dyes. Such J-band aggregation is described in The Theory of the Photographic Process by James, 4th Edition, 1977 at pages 218-222. In the process of the present invention the J-Band aggregating dyes are added to the colloid dispersion either as an aqueous solution or as a dispersion in an aqueous medium. In the process of the present invention there are simultaneously added silver nitrate solution, an alkali metal or ammonium halide or pseudo-halide solution and a solution or dispersion of a J-aggregating sensitising dye under controlled pAg conditions to the chemically sensitised silver halide crystals in a colloid dispersing medium. The silver halide emulsion used in the present invention can be comprised of silver bromide, silver chloride, silver chlorobromide, silver chloroiodide, silver bromoiodide, silver chlorobromoiodide or mixtures thereof. The emulsions can include coarse, medium or fine silver halide grains and they may have regularly shaped, for example, cubic or octahedral, crystals, or they may have irregularly shaped, for example, spherical or tabular, crystals. Alternatively, the crystals may be combinations of these shapes. The grains may be a mixture of ones having various crystal shapes. The grains may have different phases between the interior and the surface, or they may possess a uniform phase. The photographic emulsion of the present invention can be prepared by any of the methods described in P Glafkides, "Chimie et Physique Photographique", Paul Montel, 1967, G F Duffin "Photographic Emulsion Chemistry", The Focal Press, 1966 and V L Zelikman et al "Making and Coating Photographic Emulsions", The Focal Press, 1964. That is, the emulsion may be prepared by an acid process, neutral process or ammonia process. The "controlled double-jet method" wherein the solution for forming silver halide grains is kept at a constant level of pAg is preferably used as this method is effective for producing a silver halide emulsion comprising grains of a substantially uniform size having regular crystal shapes. Other methods for the preparation of silver halide emulsions which can be used for the present invention are described, for example, in Research Disclosure No 17643, December 1978, RD No 22534, January 1983 and RD No 23212, August 1983. For the chemical sensitisation any of the known procedures can be used, for example procedures which are described in RD No 17643, December 1978, and No 22534, January 1983 and in H Friester, "Die Grundlagen der Photographischem Prozesse mit Silberhalogeniden" pages 675-734, (Akademische Verlags Gesellschaft 1968). More specifically, sulphur sensitisation methods using active gelatin, and compounds containing sulphur capable of reacting with silver ions (eg thiosulphates, thioureas, mercapto compounds, and thiocyanates), reduction sensitisation methods using reducing materials (eg stannous salts, amines, hydrazine derivatives, foramidine sulphinic acid and silane compounds), noble metal sensitisation methods using noble metal compounds (eg gold compounds, and complex salts of Group VIII metals such as platinum, iridium and palladium) and so on can be employed independently or in combination. Shelling of the emulsions is carried out according to known methods. The chemically sensitised emulsion is brought into contact with conventional silver salt precipitation solutions. Typically the precipitation solution includes a silver salt and an alkali metal halide or an alkali metal thiocyanate which interact in a double decomposition reaction to form the silver halide and an alkali metal salt by-product which remains in solution. Addition of the precipitating solutions is done by double jet technique, keeping constant the pAg-value within the emulsion. Concurrently with the precipitation solutions a solution of an J-aggregating sensitising dye is added. During additional silver salt precipitation peptiser, such as gelatin or some other conventional hydrophilic colloid may be added. The shell on the chemically sensitised silver halide crystals prepared in the process of the present invention can be for example silver chloride, silver bromide, silver iodobromide and especially silver thiocyanate. The thickness of the shell formed can be up to 15 mole% by weight of the total weight of the silver halide in the crystal. Preferably the thickness of the shell is between 2 and 10 mole% by weight of the total weight of the silver halide in the crystal. The time taken for the addition of the solutions is not critical, but one has to ensure that all additional silver salt is laid down on the surface of the silver halide crystals and no new stable nuclei are formed separately and the addition rate should be slow enough that the spectral sensitiser can adsorb on the continuously enlarging surface of the crystal. The addition rate can be constant, or can increase stepwise or gradually with time. Good results can be obtained with addition times between 5 and 60 minutes, but the time can even be longer. Usually the solution or dispersion of the J-aggregating sensitising dyes is added concurrently and within the same time as the precipitating solutions but the introduction of the spectral sensitising dye can start before addition of the precipitating solutions or can be delayed until about 20% of the precipitating solutions have been added. Water miscible solvents are usually present in the aqueous solution of the J-aggregating sensitising dyes such as methanol, ethanol and acetone to help in the dissolution of the dye. J-aggregating sensitising dyes, useful for the present invention can be represented by formula: wherein R₁ and R₂ each independently represents an alkyl-or aryl group or a substituted alkyl-or aryl group, L₁, L₂ and L₃ each independently represents a methine group or a substituted methine group. Z₁ and Z₂ each independently is an atom or a group of atoms necessary to complete a 5- or 6- membered heterocyclic ring, m₁ and m₂ each independently is 0 or 1, n₁ is 0, 1 or 2 and X represents an anion, 1 is 1 or 2 provided that 1 is 1 when (I) forms an inner salt. Preferred cyanine dyes which can be used in the present invention are, for example: Silver halide emulsions prepared according to the present invention show very low "Low Intensity Reciprocity Failure" (LIRF). This is shown in the examples which follow. Photographic material of the present invention comprises, in at least one layer, one or more silver halide emulsions spectrally sensitised with a J-aggregating dye according the present invention. The spectrally sensitised silver halide of the present invention and the photographic light sensitive material using the same may contain other compounds, such as azo dyes, colour couplers, optical brightening agents, UV-absorbers, filter dyes, stain inhibitors, stabilisers, hardeners, coating aids and antistatic agents. Such additives are described for example in RD No 17643, December 1978. The finished emulsion may be coated on an appropriate support such as baryta paper, resin-coated paper, synthetic paper, triacetate film, polyethylene terephthalate film or a glass plate. Various coating methods, including dip coating methods, an air knife coating, cascade coating, curtain coating and an extrusion coating method can be employed. Such a support may be either transparent or opaque depending upon the intended use of the light sensitive material. When a support used is transparent, it can be colourless or coloured by addition of a dye or a pigment. Photographic light sensitive materials to which the emulsion of the present invention can be applied include various colour and black and white photosensitive materials. Specific examples of such materials include colour negative films (for amateur use, motion picture use, etc), colour reversal films (for slide use, motion picture use, etc), colour photographic papers, colour positive films (for motion picture use, etc) colour reversal photographic papers, heat-developable colour photosensitive materials, colour photosensitive materials for a silver dye bleach process, photographic light-sensitive materials for a photomechanical process (lith films, scanner films, etc), X-ray photographic light sensitive materials (for medical use employing radiography or fluorography, for industrial use etc), black and white negative films, black and white photographic papers, microphotographic light sensitive materials (COM, microfilms, etc), colour diffusion transfer photosensitive materials (DTR), silver salt diffusion transfer photosensitive materials and printout photosensitive materials. In the photographic processing of a photosensitive material to which the silver halide emulsion prepared in accordance with the present invention is applied, any known processing method and any known processing solution can be employed. The processing temperature is generally in the range of about 18°C to about 50°C. Of course, temperatures lower than about 18°C or higher than about 50°C may be employed. The photographic processing may include either development processing for forming a silver image (black and white photographic processing) or development processing for forming a dye image (colour photographic processing). It is thought that in the process of the present invention there is formed on the surface of the chemically sensitised silver halide crystals terraces of the halide or pseudo-halide being added, these terraces being separated from each other by steps of high surface energy. The J-band aggregating dye nucleates on these steps and is deterred from recombining. At the end of the process frequently the whole surface of the silver halide crystals is covered with such terraces and steps on which the J-band dyes have nucleated. When such crystals are photo exposed, electron hole recombination is decreased leading to higher photographic speed and low LIRF. Preferably when the emulsions of the present invention are present in a photographic assembly which has been photographically exposed the assembly is developed in a solvent developer. By solvent developer is meant a developer which comprises a proportion of a silver halide solvent and thus is able to develop an internal latent image in the silver halide crystals. Examples of useful silver halide solvent are thiosulphates and thiocyanates. The following examples will serve to illustrate the invention. Example 1 The following solutions are prepared: Solution A Phthalated gelatin 18 g Potassium bromide 196 g Potassium iodide 124 g Distilled water 2790 ml Solution B Silver nitrate 102 g Distilled water 1000 ml Solution C Silver nitrate 153 g Distilled water 1500 ml Solution D Gelatin 183 g Distilled water 2130 ml Solution A is placed in a reaction vessel equipped with a mechanical stirrer, heated to 66°C and adjusted to a pH value of 6.0. Solution B with a temperature of 57°C is added to Solution A under stirring within 30 seconds. Then Solution C is introduced into the reaction vessel in 25 minutes. The emulsion produced is cooled to 35°C and coagulated by lowering the pH to 3.5. After decanting the supernatant liquid the coagulum is washed with 500ml of water. The coagulum is then dispersed in Solution D at 40°C and pH 6.0, pAg 8.8. The silver halide crystals are polydispersed with a crystal volume between 0.29µm³ and 0.37µm³. The emulsion is chemically sensitised to optimum speed with 12µ moles Na₂S₂O₃, 18µ moles HAuCl₄, 1.1m moles NH₄SCN and 4.8mg of the potassium salt of p-toluene thiosulphonate per mole of silver halide by digestion during 50 minutes at 55°C. This is an emulsion containing chemically sensitised silver halide crystals. This emulsion is used for spectral sensitisation according to the present invention by adding 2mg of the sensitising dye of formula (12a) per g of silver in different ways. 1.1 (Comparative example). The solution of the sensitising dye is added to the emulsion in one lot and mixture is held at 40°C for 60 minutes. 1.2 (Comparative example). The solution of the sensitising dye is added to the emulsion. After 60 minutes at 40°C a shell of silver bromide crystals is precipitated onto the silver halide crystals by adding concurrently 225ml of a 0.1 molar silver nitrate and 225ml of a 0.1 molar potassium bromide solution, maintaining a constant pAg of 8.2, within 60 minutes. The amount of added silver halide corresponds to 1.5 mole% of the total silver halide. 1.3 (Comparative example). The silver halide crystals are first shelled with 15m moles of silver bromide per one mole of silver halide by adding 0.1 molar solutions of silver nitrate and potassium bromide, maintaining a constant pAg of 8.2 within 60 minutes. Then the solution of the sensitising dye is added and the mixture kept at 40°C for 60 minutes. 1.4 (Example according to the present invention). 2000g of the emulsion, containing 1 mole of silver are heated to 40°C. With continuous stirring 150ml of 0.1 molar silver nitrate solution, 150ml of 0.1 molar potassium bromide solution and 216g of a 0.1% solution of the sensitising dye of formula (12a) in ethanol are added at a constant rate within 60 minutes maintaining constant a pAg of 8.2 and a temperature of 40°C. 1.5 The procedure of 1.4 is repeated except that the addition of the solution of sensitising dye (12a) starts 15 minutes before the addition of silver nitrate - and potassium bromide solution. 1.6 The procedure of 1.4 is repeated except that the addition of the solution of sensitising dye (12a) starts 15 minutes after the addition of silver nitrate and potassium bromide solution. The thus prepared emulsions 1 to 6 are coated on a transparent polyester film with a coating weight of 2.65g silver per m², exposed behind a step-wedge and then processed as follows: Development 1.5 minutes Washing 0.5 minutes Fixing 1.5 minutes Washing 3.0 minutes Drying The temperature of each of the baths used is 30°C. The developing bath contains the following components per litre of solution: The fixing bath contains, per litre of solution: Ammonium thisulphate 200 g Ammonium bisulphate 12 g Ammonium sulphite 39 g The evaluation of exposed and coated emulsions gives the values shown in Table 1. Example 2 - Variation of the composition of the shell The same emulsion is used as in Example 1. As described in Example 1.4 the solutions of sensitising dye, silver nitrate and alkali halide or thiocyanate are added to the emulsions concurrently, within 60 minutes, keeping constant the temperature at 40°C and the pAg at 8.2. The amount of precipitated silver salt is 1.5 mole% of the total silver. The nature of the precipitated silver salt is shown in Table 2, together with the sensitometric results obtained after coating and processing as described in Example 1. Example 3 - Variation of the shell thickness The same emulsion is used as in Example 1. The procedure of Example 1.4 is repeated but the amounts of silver nitrate and potassium bromide added concurrently with the solution of the sensitising dye are varied. The amounts are given in Table 3, together with the sensitometric results after coating and processing as described in Example 1. Example 4 - Variation of addition rate The procedure of Example 1.4 is repeated but the time in which the different solutions are added is varied. Table 4 shows precipitation times and sensitometric results obtained after coating and processing as described in Example 1. Example 5 - sensitisation with red sensitising dye 2000g of the emulsion of Example 1 are heated to 40°C. The pAg is adjusted to 8.7. With continuous stirring 300ml of a solution containing 0.1 molar of AgNO₃, 300ml of a solution containing 29.3m moles of KBr and 0.7m moles of KI and 292 ml of a 0.1% solution of the sensitising dye of formula (27) in n-propanol/water (1+1) are added simultaneously with constant rate, within 60 minutes, keeping constant the pAg of 8.7 and the temperature of 40°C. For comparison a second emulsion is spectrally sensitised by adding the solution of the sensitising dye and keeping the mixture at 40°C for 60 minutes without precipitation of silver halide. Both emulsions are coated and processed as described in Example 1. The sensitometric results are given in Table 5. Example 6 - sensitisation of a pure AgBr emulsion with blue sensitising dye A pure silver bromide polydispersed tabular emulsion with a mean grain volume of 0.36um³ and an aspect ratio of 8:1 is prepared and desalted in the usual manner. For chemical sensitisation per mole of silver halide are added: 14u moles of (NH₄)₂S₂O₃, 10µ moles of HAuCl₄, 0.63m moles of NH₄SCN and 0.9mg of the potassium salt of p-toluene thiosulphonate. The emulsion is then adjusted to pH 7.0 and pAg 8.7, heated to 55°C and kept at this temperature for 40 minutes. 2000g of this emulsion, containing 1 mole of silver are heated to 40°C. With continuous stirring 150ml of 0.3 molar silver nitrate solution, 150ml of 0.3 molar potassium bromide solution and 540ml of a 0.1% solution of the sensitising dye of formula (23) dissolved in a mixture of n-propanol/water (1+1) are added simultaneously with constant rate within 60 minutes maintaining a constant pAg of 8.7 and temperature of 40°C. For comparison a second emulsion is spectrally sensitised by adding the solution of the sensitising dye and keeping the mixture at 40° for 60 minutes without precipitation of silver halide. Both emulsion are coated and processed as described in Example 1. The sensitometric results are given in Table 6. Example 7 - sensitisation of a monosized silver bromide emulsion. A monosized silver bromide emulsion with cubic crystals, having an average edge lenth of 0,45 µm with a standard deviation of ± 0,015 µm was prepared. The emulsion, containing one mole of silver per kg and 7 % gelatin was chemically sensitised to optimum speed with 20 µ moles of Na₂S₂O₃ and 5 µ moles of H Au Cl₄ per mole silver halide by digestion at pH 7,0 and pAg 8,2 for 30 minutes at 6o°C. 25oo g of this emulsion was heated to 40° C. With continous stirring 400 ml of 0,5 molar silver nitrate solution and 400 ml of 0,5 molar potasium bromide solution are added simultaneously at a constant rate within 45 minutes maintaining a constant pAg-value of 6,8 and a temperature of 40°C. 10 minutes after starting the addition of the silver nitrate solution 405 g of a 0,2 % solution of the sensitising dye of formula (12a) in methanol was added concurrently with constant rate within 35 minutes. For comparison a second part of the emulsion was spectrally sensitised by adding the solution of the sensitising dye and keeping the mixture at 4o° for 45 minutes without simultaneous precipitation of silver halide. Both emulsions are coated and processed as described in Example 1. The sensitometric results are given in Table 7.

Claims: A process for the spectral sensitisation of photographic silver halide emulsions which comprises forming and chemically sensitising silver halide crystals in a colloid dispersion medium, the process being characterised in that it comprises forming a shell of silver halide on the chemically sensitised crystals by simultaneously adding to the dispersion an aqueous solution of a water soluble halide or pseudo-halide, an aqueous solution of silver nitrate and a J-band aggregating spectral sensitising dye in an aqueous medium, the said simultaneous additions being continued for sufficient time to form a shell of silver halide crystals which is up to 15 mole percent of the total silver halide or pseudo-halide of the fully grown crystals. A process according to Claim 1 characterised in that the said simultaneous additions are continued for sufficient time to form a shell of silver halide crystals which is up to 10 mole percent of the total silver halide or pseudo-halide of the fully grown crystals. A process according to Claim 1 characterised in that the pseudo-halide is an alkali metal thiocyanate. A process according to Claim 2 characterised in that the pseudo-halide is an alkali metal thiocyanate. A process according to Claim 1 characterised in that the silver halide crystals have been both gold and sulphur sensitised. A process according to Claim 1 characterised in that the J-band aggregating spectral sensitising dye in a dye of the formulae:- wherein R₁ and R₂ each independently represents an alkyl- or aryl group or a substituted alkyl- or aryl group, L₁, L₂ and L₃ each independently represents a methine group or substituted methine group, Z₁ and Z₂ each independently is an atom or a group of atoms necessary to complete a 5- or 6- membered heterocyclic ring, m₁ and m₂ each independently is 0 or 1, n₁ is 0, 1 or 2 and X represents an anion, l is 1 or 2 provided that l is 1 when (I) forms an inner salt.

Inventors: BRUGGER PIERRE-ALAIN, STEIGER ROLF, BRUGGER, PIERRE-ALAIN, STEIGER, ROLF
Applicants: ILFORD AG
Application year: 1990
Main classification: G03C1
IPC codes: G03C1