METHOD OF PRODUCING METALLIC COMPLEX AND METALLIC COMPLEX PRODUCED THEREBY

Abstract: A method of producing a metallic complex from metal and sinterable material such as ceramic, aiming at solving the problems of conventional metallic complexes, such as insufficient mechanical and electric properties for certain uses and limited uses on account of costliness. The method comprises the step of producing a spiral article by taking up a laminate of a metallic strip and a sinterable material and the step of plastic working of the article, and additionally the step of heat treating at a given temperature. The metallic complex thus produced is suitable as mechanical members, material for electric sliding contacts, electric and heat conductors, electromagnetic shielding material, and so forth.

Description: TECHNICAL FIELD This invention relates to a method of manufacturing a metal-contained composite material to be used for a machine part, electrical sliding contact member, electric and thermal conductor, electromagnetic shielding member and the like, and a metal-contained composite material produced thereby. BACKGROUND ART Conventionally, composite materials consisting of metals or of a metal and a ceramic material have been widely used. These composite materials have been developed in an attempt to combine the properties of their components and to acquire properties that cannot be provided by the individual components. For example, it is known that composite materials, which may be obtained from material powders of W-WC, Ag-C, Ag-CdO, Cu-Al₂O₃, Ni-NiO, Al-Al₂O₃, etc., have the properties of both metal and ceramic material. These composite materials are wear-resistant, heat-resistant, high in strength, and electrically and thermally conductive, and thus are used for contacts, working tools, mechanical structural members, and the like. Metal/ceramic composite materials are also known in which a metal is coated with a ceramic material or a ceramic material is metallised. This type of composite material is used for parts of electronic devices, such as a circuit board, or for machine parts such as a turbine blade. There are still other composite materials such as a CFRM (ceramic fiber reinforced metal) in which filaments or whiskers of carbon, SiC, Al₂O₃, or K₃TiO₃ are embedded in a metal, and a MFRC (metal fiber reinforced ceramics) in which metal filaments are embedded in a ceramic material. In these composite materials, the strength and tenacity of the metal or ceramic material are improved. The above-mentioned various composite materials, however, have such a problem in that the composite materials made from powder material and the metal/ceramic composite materials do not have satisfactory electrical and mechanical properties, though they are inexpensive, while the CFRM and MFRC are costly and are limited in use. A method of manufacturing a metal-contained composite material comprising a process of fabricating a roll of a laminate, prepared by a lamination of at least one sinterable material on one surface of a metal strip, by winding up the laminate with or without a core is known from US 4189522. An object of this invention is to provide a method of manufacturing a metal-contained composite material in which the properties of metal and various sinterable materials compounded therewith are fully retained and excellent properties that cannot be acquired by the individual components are obtained. Another object of this invention is to provide a metal-contained composite material having such excellent properties as mentioned before. DISCLOSURE OF THE INVENTION The invention is defined in claims 1 and 8. Preferred embodiments are shown in claims 2 - 7 and 9 - 15. To achieve the above objects, according to this invention, the method further comprises a process of subjecting the roll to plastic working. The method of manufacturing a metal-contained composite material according to this invention will be described hereinafter according to the manufacturing processes. First, the process of making a roll will be described with reference to the relevant drawings. In this process, a spirally wound roll is obtained by winding up a metal strip, having a sinterable material layer formed on one surface thereof, on itself or around a core. The core material used in this process may be either the same metal as the metal strip or some other metal different therefrom. When carrying out this process, the metal strip may be wound up while at the same time forming a sinterable material layer on one surface of the metal strip, or a sinterable material layer may be previously formed on one surface of the metal strip before the metal strip is wound up. Of these methods, the former in which the metal strip is wound up while laminating the sinterable material thereon is preferred, because the productivity is higher and the manufacturing cost is lower. Fig. 1 is a diagram illustrating the process of making a roll by winding up a metal strip while a sinterable material layer is forming on one surface thereof. In Fig. 1, reference numeral 1 denotes an uncoiler, around which a metal strip 2 is wound. The metal strip 2 wound around the uncoiler 1 is continuously led to a certain direction (indicated by arrow in the figure), the leading direction is swerved in the middle by a turn roll 3, and then the strip is continuously reeled up by a coiler 4. When the metal strip 2 is wound around the coiler 4, a sinterable material 6 is sprayed from a spray gun 5, arranged in the vicinity of the coiler 4, onto the surface of the metal strip 2. These sequential of operations enable forming a cylindrical laminate roll 7 comprising the metal strip 2 and the sinterable material 6. In this process, coating with sinterable material 6 should preferably be avoided from the outer end of the rolled metal strip 2. Fig. 2 shows a modification of the roll preparation process shown in Fig. 1. The process of Fig. 2 differs from that shown in Fig. 1, only in the means of laminating the sinterable material 6 on one surface of the metal strip 2. In Fig. 2, elements with like reference numerals have the same functions as those appearing in Fig. 1. As shown in Fig. 2, a sinterable material 6, in a slurry state, is applied to a surface of the metal strip 2 by a spreading roll 8, and then dried by a gas burner 9, and the strip 2 is wound around the coiler 4, therefrom results a cylindrical roll 7. To laminate the sinterable material 6 on a surface of the metal strip 2 in the roll preparation process, various methods can be used, such as PVD methods inclusive of a plasma spraying, thermal spraying, sputtering, vacuum deposition, and ion plating, CVD methods inclusive of a laser beam sputtering, thermal CVD, MOCVD, and plasma CVD, a spray pyrolysis method, a printing method, a dip coating method, a slurry application method, and an electrophoretic deposition method. In the roll fabrication process, the sinterable material 6 is preferably laminated to even out a thickness over the entire surface of metal strip 2. To be brief, in Fig. 1, a plurality of spray guns may be employed, or a single spray gun may be moved while spraying. The roll fabrication process is preferably carried out in a sealed vessel (indicated by 11 in the figures), so that the atmosphere can be conditioned in suit with the type of the sinterable material used. For example, when using a plasma spraying method, a low-pressure plasma process is operated under reduced atmospheric pressure at 10 to 500 Torr. This process serves to prevent a metal-contained composite material in production from oxidation, to make the sinterable material layer homogeneous, and to improve the adhesion between the metal strip and the sinterable material layer. Alternatively, a high-pressure plasma may be employed which is easily performable in the atmosphere. In this invention, a possible combination and ratio of contents in the metal strip and the sinterable material, may be arbitrary to suit for the application of the metal-contained composite material and the type of the sinterable material, as necessary. The purpose of the metal strip is to embody such properties of the metal-contained composite material, as electrical conductivity, thermal conductivity, ductility, tenacity, weldability, platability, and solderability. In line with this, the material for the embodiment can preferably be of Cu, Al, Ag, Au, Fe, Ni, Co, W, Mo, Nb, Ta, Ti or Zr, or an alloy of some elements out of foresaid metals or an alloy out of Ag-Pd, Cu-Zn, Cu-Sn, Cu-Ni, SUS, Fe-Ni, Fe-Ni-Co, Mo-Cr-Fe, etc. For the sinterable material, at least one substance may be selected from the group consisting of ceramic materials, electroconductive polymers, metals, and a mixture of ceramic materials and metals. The sinterable material is preferably in the form of powder, for the convenience of manufacture. Favorable ceramic materials include Al₂O₃, SiC, ZrO₂, MgO, BaTiO₃, Fe₂O₃, MoS₂, WC, TiC, TiB₂, TiN, AlN, glass (soda-lime glass and lead glass), MoSi, ZnN, ZrC, ZrB₂, PbTiO₃, NaTaO₃, KNSO₃, NaNbO₃, K₂O·6TiO₂, 9Al₂O₃ · 2B₂O₃, KTaO₃, BaSaO₃, and (Bi₂O₃)Me m-1 R m O 3m+1 (Me is an element with a valence of 1 to 3; R is an element with a valence of 4.5). Preferably, polyaniline, polyacetylene, or polypyrrole is used for the electroconductive polymer. The same metal as used for the metal strip is preferably used for the sinterable material. The mixture of ceramic materials and metals is preferably a mixture of one or more substances selected from the aforementioned ceramic materials and one or more substances selected from the aforementioned metals. In this case, the metal also serves as a binder, and the mixing ratio of the ceramic materials and the metals may be arbitrary in suit with the application of the metal-contained composite material. When using a metal or a mixture of metal and ceramic material as the sinterable material, either a similar metal to the metal strip or a different metal may be used. After the roll fabrication process described above, a plastic working process is carried out. This plastic working process may be performed immediately after the completion of the preceding process if the sinterable material layer is not formed on the outer end of the rolled metal strip, but if the sinterable material layer is formed on the outer end of the rolled metal strip, the metal strip is wrapped around the roll or the roll is fitted into a metal tube made of the same metal as used for the metal strip or of a different metal, before the plastic working process is carried out. The plastic working process may be operated by a rolling or drawing, and the working temperature may be hot, warm, or cold, depending on the type of the material used. In addition to the above plastic working methods, pressure working methods such as a CIP (cold isostatic pressing), HIP (hot isostatic pressing), hot pressing, or cold pressing may be applied. A process annealing may preferably be carried out in the middle of the plastic working, to eliminate working strain and thus improve the product quality. Due to the plastic working, a wirelike metal-contained composite material 23 composed of a metal layer (metal strip) 21 and a sinterable material layer 22, both extending longitudinally, is obtained (see Figs. 3 and 4). When a core is used, a metal-contained composite material composed of a central metal (core) 24, a longitudinally extending metal layer (metal strip) 21, and a sinterable material layer 22, as shown in Figs. 5 and 6, is obtained. According to this invention, a compression process may further be effected after the plastic working process. In this compression process, as shown in Fig. 3 through Fig. 6, the metal-contained composite material undergoes compression by pressing or rolling. Due to this compression process and by suitably cutting the compressed sheet as required, platelike metal-contained composite members can be obtained (see Figs. 7 and 8). According to the method of this invention, two spray guns, one for the sinterable material and the other for the metal, may be provided in the apparatus for producing a roll, shown in Fig. 1, such that two or more sinterable powders, e.g., ceramic powder and metal powder, are alternately sprayed on one surface of the metal strip while the metal strip is wound up. By subjecting the thus-obtained roll to plastic working, a wirelike metal-contained composite material 33, which is composed of a longitudinally extending metal layer (metal strip) 31a, and ceramic layers 32 and metal layers (i.e., sprayed metal, enclosed by solid lines in Fig. 9 without shading) 31b longitudinally extending and located alternately in the circumferential direction, can be obtained (see Fig. 9). The metal-contained composite material shown in Fig. 9 may be subjected to compression to obtain a metal-contained composite plate (see Fig. 10). The metal-contained composite material produced by the method of this invention has at least a portion of the outer surface thereof made of a metal layer, and has interior or innards thereof composed of the metal layer and a sinterable material layer, which extend longitudinally and alternate with each other. Since a portion of the outer surface of the metal-contained composite material produced by the method of this invention is constituted by a metal layer, the composite material more excels in weldability, solderability and platability than MFRCs and the like. Further, the method of this invention permits an easy selection of the structure and compounding ratio of the metal and the sinterable material, and accordingly, a composite material having properties suited to specific use can be easily produced. Furthermore, the metal-contained composite material produced by the method of this invention has a sinterable material layer extending in the longitudinal direction, and thus has excellent electrical properties. To achieve aforesaid objects, this invention further provides a method of manufacturing a metal-contained composite material, characterized by comprising: a process of obtaining a roll of a laminate, prepared by a lamination of a sinterable material on one surface of a metal strip, by winding up the laminate on itself or around a core; a process of drawing the resultant roll; and a process of heating the drawn roll at a temperature higher than a sintering temperature of the sinterable material and lower than a melting point of the metal constituting the metal strip. In this method of the invention, a heating process is operated, in addition to the roll preparation process and plastic working process mentioned above. The heating process is carried out at a temperature higher than the sintering temperature of the sinterable material used and lower than the melting point of the metal forming the metal strip. The heating process may be effected under pressure. In the heating process, heat may be provided by HIP, electric furnace, burner, lamp, laser, or self-reaction. The heat treatment time may be set in accordance with the type and quantity of the sinterable material and the temperature used. The metal-contained composite material produced by this method of the invention has at least a portion of the outer surface thereof made of a metal layer, and has the interior thereof composed of the metal layer and a sinterable material layer longitudinally extending and separated from each other. Since the metal-contained composite material is obtained through a heating process effected within the predetermined temperature range, the sinterable material layer of the composite material can be made dense and homogeneous, and thus the mechanical and electrical properties are further enhanced, compared with those which are not subjected to heating process. Particularly, when a substance having high crystalline anisotropy is used as the sinterable material, the crystals can be oriented in optimum directions, which is practically advantageous. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a diagram illustrating a method of manufacturing a metal-contained composite material according to this invention; Fig. 2 is a diagram also illustrating the method of manufacturing a metal-contained composite material according to this invention; Fig. 3 is a sectional view of a metal-contained composite material obtained by the method of the invention without a core when producing a roll; Fig. 4 is a sectional view of a metal-contained composite material obtained by the method of the invention without a core when producing a roll; Fig. 5 is a sectional view of a metal-contained composite material obtained by the method of the invention using a core when producing a roll; Fig. 6 is a sectional view of a metal-contained composite material obtained by the method of the invention using a core when producing a roll; Fig. 7 is a partially sectional view of the metal-contained composite material of Fig. 3 which has been worked into a plate; Fig. 8 is a partially sectional view of the metal-contained composite material of Fig. 3 which has been worked into a plate; Fig. 9 is a sectional view of a metal-contained composite material obtained according to the method of this invention; and Fig. 10 is a partially sectional view of the metal-contained composite material of Fig. 9 which has been worked into a plate. BEST MODE OF CARRYING OUT THE INVENTION This invention will be described hereinafter in more detail with several examples. It is noted that this invention should not be limited to the following examples. EXAMPLE 1 : A Cu-TiN based composite material was produced by using the apparatus shown in Fig. 1. First, a Cu tape of 0.05 mm thick was fed in one direction, and was tightly wound around a Cu rod having a diameter of 3 mm while a TiN layer of 15 µm thick was formed on a surface of the Cu tape by a plasma CVD method, to obtain a spirally wound roll of the laminate (with 200 turns in total). The conditions for the formation of the TiN layer by the plasma CVD method were as follows: The processing system was sealed, and in this system, a hydrogen gas as a carrier gas was made to flow at 30 ml/sec and a nitrogen gas and a titanium tetrachloride gas, as material gases, were made to flow at 1.5 ml/sec and 0.4 ml/sec, respectively. The internal pressure of the system was maintained at 0.4 Torr, and the Cu tape was heated to 500°C. Further, high-frequency waves of 13.56 MHz were adopted to secure an output of 1.5 kW in producing a plasma. Subsequently, the obtained roll was fitted into a Cu pipe having an inner diameter of 32 mm and a thickness of 1 mm, and then subjected to a HIP process for 4 hours under the conditions of 700°C and 2,000 atm. Then, a drawing process was effected by a hot extrusion at 700°C and using a draw bench, to thereby obtain a rodlike Cu-TiN based composite material having a diameter of 7.5 mm. This composite material was sliced, the cut surface was subjected to an abrasion test with a load of 10 g and a sliding speed of 10 cm/sec, and also a contact voltage drop was measured in the electrified state at 0.1 A. The results are shown in TABLE 1. EXAMPLE 2 : An Ag-ZrN based composite material was produced by using the apparatus shown in Fig. 1. First, an Ag tape of 0.05 mm thick was fed in one direction, and was tightly wound around an Ag rod having a diameter of 3 mm while a ZrN layer of 15 µm thick was formed on a surface of the Ag tape by a laser beam sputtering method, to obtain a spirally wound roll of the laminate (with 200 turns in total). The conditions for the formation of the ZrN layer by the laser beam sputtering method were as follows: The processing system was sealed and a nitrogen atmosphere (gas pressure: 10⁻⁴ Torr) was produced therein. ZrN was used as a target, and a 500 W-output CO₂ laser (wavelength: 10.6 µm) and a 30 W KrF excimer laser (wavelength: 248 nm) were used as beam sources. The Ag tape was preheated to 550°C, the target was sputtered with the longer-wavelength laser beam, and then the particles were irradiated with the shorter-wavelength laser beam, to thereby form a ZrN layer. Subsequently, the obtained roll was fitted into an Ag pipe having an inner diameter of 32 mm and a thickness of 1 mm, and then subjected to a HIP process for 4 hours under the conditions of 700°C and 2,000 atm. Then, a drawing process was effected by a hot extrusion at 700°C and using a draw bench, to thereby obtain a rodlike Ag-ZrN based composite material having a diameter of 7.5 mm. The obtained composite material was subjected to tests similar to those conducted with respect to EXAMPLE 1, the results being shown in TABLE 1. EXAMPLE 3 : A Ni-TiB₂ based composite material was produced by using the apparatus shown in Fig. 1. First, a Ni tape of 0.1 mm thick was fed in one direction, and was closely wound around a Ni rod having a diameter of 5 mm while a TiB₂ layer of 0.05 mm thick was formed on a surface of the Ni tape by a plasma spraying method, to obtain a spirally wound roll of the laminate (with 200 turns in total). Subsequently, the obtained roll was fitted into a Ni pipe having an inner diameter of 72 mm and a thickness of 2 mm, and then subjected to a HIP process for 4 hours under conditions of 800°C and 2,000 atm. Then, a drawing process was effected by a hot extrusion at 800°C and using a draw bench, to thereby obtain a rodlike composite material having a diameter of 7.5 mm. Thereafter, this composite material was further subjected to a HIP process for 18 hours under conditions of 1,300°C and 2,000 atm, and a Ni-TiB₂ based composite material was obtained. The obtained composite material was subjected to the same tests as those conducted with respect to EXAMPLE 1. The results are shown in TABLE 1. EXAMPLE 4 : A Ni-NiB₂-PdB based composite material was obtained, following the same procedures as those employed in EXAMPLE 3 except that a mixture of NiB₂ and PdB, mixed in the ratio 1:1 (by weight), was used instead of TiB₂. The obtained composite material was subjected to tests similar to those conducted on EXAMPLE 1, the results being shown in TABLE 1. EXAMPLE 5 : A 6.6×6.6 mm-square composite material was obtained, following the same procedures as those employed in EXAMPLE 3 except that a rolling process was effected by a caliber rolling mill instead of the drawing process using a draw bench. The composite material was subjected to a HIP process for 18 hours under conditions of 1,300°C and 2,000 atm, thereby obtaining a Ni-TiB₂ based composite material. The obtained composite material was subjected to the same tests as those conducted with respect to EXAMPLE 1, the results being shown in TABLE 1. EXAMPLE 6 : A Ni-TiB₂ based composite material was obtained, following the same procedures as those employed in EXAMPLE 3 except that the final HIP process was omitted. The obtained composite material was subjected to the same tests as those conducted on EXAMPLE 1, the results being shown in TABLE 1. EXAMPLE 7 : A Ni-NiB₂-PdB based composite material was obtained, following the same procedures as those employed in EXAMPLE 4 except that the final HIP process was omitted. The obtained composite material was subjected to the same tests as those conducted with respect to EXAMPLE 1. The results are shown in TABLE 1. CONTROL 1 : A Ni-3 vol % ThO₂ based dispersion alloy was obtained by an ordinary powder metallurgy technique. The obtained composite material was subjected to the same tests as those conducted with respect to EXAMPLE 1. The results are shown in TABLE 1. COMPOSITE STRUCTURE HEATING PROCESS (YES, NO) AMOUNT OF ABRASION (mm/100H ) VOLTAGE DROP ( mV ) COMPOSITION STRUCTURE EXAMPLE 1 Cu-TiN FIG. 5 TYPE NO 1.2 19 EXAMPLE 2 Ag-ZrN FIG. 5 TYPE NO 1.2 19 EXAMPLE 3 Ni-TiB₂ FIG. 5 TYPE YES 0.9 22 EXAMPLE 4 Ni-NiB₂-PdB FIG. 5 TYPE YES 0.9 15 EXAMPLE 5 Ni-TiB₂ FIG. 6 TYPE YES 0.9 21 EXAMPLE 6 Ni-TiB₂ FIG. 5 TYPE NO 2.0 25 EXAMPLE 7 Ni-NiB₂-PdB FIG. 5 TYPE NO 1.6 19 CONTROL 1 Ni-ThO₂ DISPERSION TYPE NO 2.4 58 EXAMPLE 8: An Ag-(Bi₄Ti₃O₁₂ + Nb) based composite material was produced, following the same procedures as those employed in EXAMPLE 1. First, an Ag tape of 0.2 mm thick was fed in one direction, and was closely wound up while a Bi₄Ti₃O₁₂ + Nb layer of 0.07 mm thick was formed on a surface of the Ag tape by a plasma spraying method, to obtain a spirally wound roll of the laminate (with 20 turns in total). Subsequently, the obtained roll was fitted into an Ag pipe having an inner diameter of 12 mm and a thickness of 1 mm, and then subjected to a HIP process for 4 hours under conditions of 800°C and 2,000 atm. Then, a drawing process was effected by a hot extrusion at 800°C and using a draw bench, to thereby obtain a rodlike Ag-(Bi₄Ti₃O₁₂ + Nb) based composite material having a diameter of 7 mm. Then, a chip of 1 mm thick was cut off from the composite material, and was measured as to the dielectric constant, dissipation factor, breakdown voltage, and density. The measurement results are shown in TABLE 2. EXAMPLE 9 : The composite material obtained according to EXAMPLE 8 was further subjected to a HIP process for 20 hours under conditions of 950°C and 2,000 atm, to obtain an Ag-(Bi₄Ti₃O₁₂ + Nb) based composite material. This composite material was measured as to the same items as those for EXAMPLE 8, the results being shown in TABLE 2. EXAMPLE 10 : An Ag-BaTiO₃ based composite material was produced by using the apparatus shown in Fig. 1. First, an Ag tape of 0.1 mm thick was fed in one direction, and was closely wound up while a BaTiO₃ layer of 10 µm thick was formed on a surface of the Ag tape by an a.c. magnetron sputtering method, to obtain a spirally wound roll of the laminate (with 40 turns in total). The conditions for the formation of the BaTiO₃ layer by the a.c. magnetron sputtering method were as follows: The processing system was sealed and an atmosphere (internal pressure: 10 mTorr) was produced therein such that O₂ and Ar were made to flow in the ratio 0.5 (= O₂/(Ar+O₂)). BaTiO₃ was used as a target, the Ag tape was heated to 600°C, and an output of 1 kW was used. Subsequently, the obtained roll was fitted into an Ag pipe having an inner diameter of 10 mm and a thickness of 0.8 mm, and then subjected to a HIP process for 4 hours under conditions of 800°C and 2,000 atm. Then, a drawing process was effected by a hot extrusion at 800°C and using a draw bench, to thereby obtain a rodlike Ag-BaTiO₃ composite material having a diameter of 7 mm. The obtained composite material was subjected to the same tests as those conducted with respect to EXAMPLE 8. The results are shown in TABLE 2. EXAMPLE 11 : A 6.6×6.6 mm-square Ag-(Bi₄Ti₃O₁₂ + Nb) based composite material was obtained, following the same procedures as those employed in EXAMPLE 8 except that a rolling process was effected by a caliber rolling mill instead of the drawing process using a draw bench. The obtained composite material was subjected to the same tests as those conducted on EXAMPLE 8, the results being shown in TABLE 2. EXAMPLE 12 : The composite material obtained according to EXAMPLE 11 was further subjected to a HIP process for 20 hours under conditions of 950°C and 2,000 atm, to obtain a square Ag-(Bi₄Ti₃O₁₂ + Nb) based composite material. This composite material was measured as to the same items as those for EXAMPLE 8, the measurement results being shown in TABLE 2. CONTROL 2 : A slurry was prepared by adding a binder to a material powder of Bi₄Ti₃O₁₂ + Nb, and using this slurry, a green sheet of 40 µm thick was prepared by a doctor blade method, and 10 mm-square pieces were punched out. Ag paste, which is to serve as an internal electrode, was printed on a surface of each piece punched out from the green sheet, and 20 pieces with the electrode thereon were stacked up and press-bonded together. The stacked body was cut, and baked at 950°C. Then, an Ag electrode was baked over the entire exposed portions of the internal electrodes at both ends of the stacked structure, to form external electrodes, whereby a stacked-chip type capacitor having a conventional structure is obtained (Bi₄Ti₃O₁₂ + Nb is a dielectric). This capacitor was subjected to the same tests as those conducted with respect to EXAMPLE 8, the results being shown in TABLE 2. EXAMPLE 13 : A Ti-Al₂O₃ based composite material having a Mn-Zn based ferrite core rod was produced by using the apparatus shown in Fig. 1. First, a Ti tape of 0.1 mm thick was fed in one direction, and was closely wound around a Mn-Zn based ferrite rod having a diameter of 5 mm while an Al₂O₃ layer of 0.04 mm thick was formed on a surface of the Ti tape by a plasma spraying method, to obtain a spirally wound roll of the laminate (with 50 turns in total). Subsequently, the obtained roll was fitted into a Ni pipe having an inner diameter of 23 mm and a thickness of 1 mm, and then subjected to a HIP process for 4 hours under conditions of 750°C and 2,000 atm. Then, a drawing process was effected by a hot extrusion at 750°C and using a draw bench, to thereby obtain a rodlike Ti-Al₂O₃ based composite material having a diameter of 7 mm. The obtained composite material was evaluated as to the Q (quality) factor at 10 kHz in room temperature, the breakdown voltage, and the allowable maximum temperature (the maximum temperature at which neither the Q factor nor the breakdown voltage are lowered even if the material is maintained at that temperature for 2 hours). The measurement results are shown in TABLE 3. EXAMPLE 14 : The composite material obtained according to EXAMPLE 13 was further subjected to a HIP process for 20 hours under conditions of 1,400°C and 2,000 atm, to obtain a Ti-Al₂O₃ based composite material. The obtained composite material was subjected to the same tests as those conducted on EXAMPLE 13, the results being shown in TABLE 3. EXAMPLE 15 : A Cu-MgO based composite material was produced by using the apparatus shown in Fig. 1. First, a Cu tape of 0.1 mm thick was fed in one direction, and was closely wound around a Mn-Zn based ferrite rod having a diameter of 5 mm while a MgO layer of 10 µm thick was formed on a surface of the Cu tape by an ion plating method, to obtain a spirally wound roll of the laminate (with 50 turns in total). The conditions for the formation of the MgO layer by the ion plating method were as follows: The processing system was sealed, Mg was evaporated at a volumetric rate of 500 Å/sec, and O₂ was ionised by an ionisation mechanism comprising a RF coil and applied onto the Cu tape. The Cu tape was heated to 500°C. Subsequently, the obtained roll was fitted into a Cu pipe having an inner diameter of 23 mm and a thickness of 1 mm, and then subjected to a HIP process for 4 hours under conditions of 750°C and 2,000 atm. Then, a drawing process was effected by a hot extrusion at 750°C and using a draw bench, to thereby obtain a rodlike Cu-MgO based composite material having a diameter of 7 mm. The obtained composite material was subjected to the same tests as those conducted with respect to EXAMPLE 13, the results being shown in TABLE 3. EXAMPLE 16 : A 6.6×6.6 mm-square Ti-Al₂O₃ based composite material (with a Mn-Zn based ferrite core rod) was obtained, following the same procedures as those employed in EXAMPLE 13 except that a rolling process was effected by a caliber rolling mill instead of the drawing process using a draw bench. The obtained composite material was subjected to the same tests as those conducted on EXAMPLE 13. The results are shown in TABLE 3. EXAMPLE 17 : The composite material obtained according to EXAMPLE 16 was further subjected to a HIP process for 20 hours under conditions of 1,400°C and 2,000 atm, to obtain a Ti-Al₂O₃ based composite material having a Mn-Zn based ferrite core rod. The obtained composite material was subjected to the same tests as those conducted on EXAMPLE 13, the results being shown in TABLE 3. CONTROL 3 : A mica tape and a Cu tape, each having a thickness of 10 mm, were alternately closely wound around a Mn-Zn based ferrite rod having a diameter of 5 mm, to obtain 50 turns for each of the two tapes, and the outer end of the tape was fixed, thereby obtaining a coil. This coil was subjected to the same tests as those conducted with respect to EXAMPLE 13. The results are shown in TABLE 3. INDUSTRIAL APPLICABILITY The metal-contained composite material produced according to the method of this invention can be used for machine parts, electrical sliding contact materials, electrical and thermal conductors, and materials for electromagnetic shielding members.

Claims: A method of manufacturing a metal-contained composite material, comprising: a process of fabricating a roll (7) of a laminate, prepared by a lamination of at least one sinterable material (6) on one surface of a metal strip (2), by winding up the laminate with or without a core (24); characterised in that said roll is subjected to plastic working. A method according to claim 1, wherein said core (24) is made of a metal identical to or different from the metal of the metal strip (2). A method according to claim 1 or 2, wherein said process of fabricating a roll comprises the operation of winding the metal strip (2) with or without the core (24) while at the same time laminating at least one sinterable material (6) on one surface of the metal strip. A method according to any one of claims 1 to 3, wherein the lamination of the sinterable material (6) is carried out by a method selected from a group consisting of a plasma spraying method, PVD method, CVD method, spray pyrolysis method printing method, dip coating method, slurry application method, and electrophoretic deposition method. A method according to any one of claims 1 to 4, wherein said sinterable material (6) contains one or more substances selected from a group consisting of ceramic materials, electroconductive polymers, metals, and a mixture of ceramic materials and metals. A method according to claim 1, wherein said plastic working comprises a process selected from a group consisting of rolling, drawing, CIP, HIP, hot pressing, and cold pressing. A method according to claim 1 or 6, which further comprises a compression process to be carried out after said plastic working. A method of manufacturing a metal-contained composite material, comprising: a process of fabricating a roll (7) of a laminate, prepared by a lamination of at least one sinterable material (6) on one surface of a metal strip (2), by winding up the laminate with or without a core (24); characterised in that the method also includes a process of drawing the roll (7); and a process of heat treatment on the drawn roll at a temperature higher than a sintering temperature of the sinterable material (6) and lower than a melting point of the metal constituting the metal strip (2). A method according to claim 8, wherein said core (24) is made of a metal identical to or different from the metal of the metal strip (2). A method according to claim 8 or 9, wherein said process of fabricating a roll (7), comprises the operation of winding the metal strip (2) with or without the core (24) while at the same time laminating at least one sinterable material (6) on one surface of the metal strip (2). A method according to any one of claims 8 to 10, wherein the lamination of the sinterable material (6) is carried out by a method selected from a group consisting of a plasma spraying method, PVD method, CVD method, spray pyrolysis method, printing method, dip coating method, slurry application method, and electrophoretic deposition method. A method according to any one of claims 8 to 11, wherein said sinterable material (6) is one or more substances selected from a group consisting of ceramic materials, electroconductive polymers, metals, and a mixture of ceramic materials and metals. A method according to claim 8, wherein said plastic working comprises a process selected from a group consisting of rolling, drawing, CIP, HIP, hot pressing, and cold pressing. A method according to claim 8 or 13, which further comprises a compression process to be carried out after said plastic working. A method according to claim 8, wherein said heating process is effected by using one of HIP, electric furnace, burner, lamp, laser, and self-reaction.

Inventors: OZAKI MASANORI THE FURUKAWA EL, SHIGA SHOJI THE FURUKAWA ELECT, SUZUKI MINORU THE FURUKAWA ELE, OZAKI, MASANORI, THE FURUKAWA ELECTRIC CO., LTD., SHIGA, SHOJI, THE FURUKAWA ELECTRIC CO., LTD., SUZUKI, MINORU, THE FURUKAWA ELECTRIC CO.,LTD.
Applicants: FURUKAWA ELECTRIC CO LTD, THE FURUKAWA ELECTRIC CO., LTD.
Application year: 1990
Main classification: B22F7
IPC codes: C04B35, C04B37, B22F7