Method of brazing aluminium-based sheets or parts

Abstract: Aluminium-based sheets or parts, such as formed aluminium assemblies contaminated with forming die lubricants, are cleaned by a solventless, thermal degreasing process at controlled temperature (about 300-­ 400°F), and in specified atmospheres (reactive gas which is at least at atmospheric pressure) prior to brazing. The organic contaminates on the aluminium-based sheet or part are reacted with the reactive gas (air or oxygen) and removed from the surface of the sheet or part without disruption of the underlying protective oxide layer. Subsequent brazing is thereby facilitated.

Description: The present invention relates to a solventless, thermal degreasing process for cleaning aluminium-based sheets or parts and subsequent brazing of the cleaned aluminium-based sheets or parts. Degreasing of metal is well established in the art and has been used extensively in processing metallic scrap material. Representative of the prior art patents relating to the degreasing of metallic scrap are U.S. Patents to Kennedy (4,508,564), Fitzpatrick (4,654,088), Ruthven (2,104,102), Mathis (3,650,830), Erman (3,627,289), Ripoche (2,595,411), and Stephens (4,010,935). However, none of these references disclose a method whereby degreasing takes place in a solventless atmosphere. For example, Ruthven (2,104,102) discloses a thermal degreasing method which involves dipping a heated article in a solvent such as trichloroethylene at such a rate and in such quantity that the article will obtain a temperature of at least the vapour temperature of the solvent after the article leaves the bath of boiling solvent so that the article is devoid of a film of solvent as well as of greasy material when it leaves the vapour atmosphere. The use of solvents, such as trichloroethylene, for the reactive atmosphere during degreasing is an expense and may pose environmental concerns. In addition, a problem which has occurred with degreasing methods at elevated temperatures especially when using aluminium-based parts has been the further oxidation of the underlying aluminium alloy surface or the complete destruction of the protective oxide layer which normally exists. U.S. Patents Topelian (2,856,333) and Johnson et al (4,684,411) both specifically disclose oxidising the underlying aluminium-based alloy as part of their thermal degreasing method. By increasing the thickness of the initial thin, protective oxide layer of aluminium-based alloys in this manner, subsequent brazeability of the metallic alloy is severely compromised. That is, the additional oxidation, that can occur in high temperature thermal degreasing (i.e., around 500°C and above) forms a layer which is not readily brazeable. With magnesium bearing alloys, oxidation produces a duplex oxide on the outermost surface which degrades brazability. Careful maintenance of the temperature during thermal degreasing is necessary in order to prevent disruption of the existent protective aluminium oxide layer and thereby preserve the brazability of the aluminium-based sheet or part. In this regard, U.S. Patent Stauffer (4,016,003) discloses the careful maintenance of temperatures to avoid ignition of volatile materials which could also conceivably preserve the underlying protective oxide layer of the metallic alloy in cleaning aluminium scrap. However, Stauffer does not control the temperature for this purpose but rather for the purpose of avoiding the ignition of volatilise. Moreover, Stauffer does not subsequently braze the metallic alloy. Rather, Stauffer subsequently melts the alloy as part of the scrap recycling process which clearly destroys the underlying protective oxide layer. Another degreasing method is shown by Hetherington in "ULVAC Aluminium Brazing Furnaces" Supp. to ULVAC Sales brochure E 3009 "Aluminium Vacuum Brazing Furnace" FB Series, which discloses a degreasing method that has been implemented in the Japanese automotive industry. Hetherington's solventless degreasing method for aluminium-based alloys prior to brazing requires drawing a vacuum which precludes oil and grease from completely reacting. This method depends upon the complete evaporation of surface contaminants for surface cleaning. Dissociation of the surface contaminant during evaporation can produce residual surface contaminant species. Moreover, because vacuum conditions are required, Hetherington's degreasing method is not as economical as is desirable. Accordingly, there remains a need in the art for a degreasing method for aluminium-based alloys which preserves the underlying protective oxide layer so as not to compromise any subsequent brazing and which removes surface contaminants which can not be completely removed by evaporation alone. Further, the degreasing method should be solventless so to reduce cost and do as not to pose any adverse toxicological and/or environmental problems. Also, there is a need for a degreasing method which does not require a drawing a vacuum. The present invention provides a thermal degreasing method which satisfies all of the aforementioned needs. In particular, the present invention provides a solventless, thermal degreasing process for cleaning an aluminium-based sheet or part to produce a more readily brazable sheet or part followed by the subsequent brazing of the cleaned aluminium-based sheet or part. According to the present invention we provide a solventless, thermal degreasing process for cleaning an aluminium-based sheet or part to render it suitable for brazing, the process comprising, providing said aluminium-based sheet or part having organic contaminants thereon and heating said sheet or part in the presence of a reactive gas selected from air, oxygen, ammonia or hydrogen at least at atmospheric pressure and at a temperature of between 300 and 400 Deg.C for 10 minutes to 30 minutes to volatilise and remove said organic contaminants by reacting said organic contaminants with said reactive gas and brazing said sheet or parts with a brazing material. In the degreasing portion of the instant process, the aluminium-based sheet or part is heated in the presence of a reactive gas such as air or oxygen, ammonia or hydrogen, at least at atmospheric pressure and at a temperature of between 300 and 400°C for a sufficient period of time, in particular, between 10 minutes and 30 minutes, to volatise and remove any organic contaminants, such as oils or grease. The process is preferably useful in removing forming die lubricants from formed aluminium assemblies prior to brazing to form heat exchangers for automobile radiators. The reaction of the organic contaminants on the aluminium-based sheet or part with the reactive gas occurs without significant distruption of the underlying protective oxide layer and does not, therefore, interfere with the brazability of the sheet or part. The aluminium-based sheet or part is thereafter allowed to cool prior to brazing or it may be brazed immediately. Thus, in the preferred process, the aluminium-based sheet or part is brazed relatively shortly after having been cleaned. For that reason it is necessary, as stated above, to preserve the underlying aluminium oxide layer. In order to do so it is essential that the temperature of solventless, thermal degreasing be at or below 400°C. Any significantly higher temperatures will alter the aluminium oxide layer and may oxidise any magnesium which is present in the aluminium-based alloy. Preferably the aluminium-based alloy contains some magnesium in order to render it capable of fluxless brazing, which is the preferred brazing process. The preferred brazing process utilises a filler metal alloy, such as one containing 89% aluminium, 1.5% magnesium, and 9.5% silicon, in a vacuum at around 600°C to join the formed, cleaned aluminium-based sheets or parts and form, for example, a heat exchanger for automobile radiators. Ideally the solventless, thermal degreasing process of the present invention is used in the automobile parts plant and is followed shortly thereafter by the preferred fluxless brazing process. Accordingly, it is an object of the present invention to provide a solventless, thermal degreasing method for aluminium-based alloys which preserves the underlying protective oxide layer so that subsequent brazing is not compromised. Also, it is an object of the present invention to provide a less costly reactive atmosphere for the degreasing process. Finally, it is an object of the present invention to provide a method of brazing aluminium-based sheets or parts which have been cleaned by solventless, thermal degreasing. In the preferred embodiment of the present invention an aluminium-based sheet or part such as a formed aluminium assembly which is covered with various forming die lubricants, i.e., oils and/or grease, is heated in the presence of a reactive gaseous atmosphere such that the underlying protective oxide layer of the aluminium-based sheet or part is not disturbed but the organic contaminants are reacted, volatilised, and removed. The cleaned part is thereafter brazed. The temperature range is from 300 to 400°C and the heating time is for 10 minutes to 30 minutes. Further, the preferred reactive atmosphere is air at atmospheric pressure although other reactive gases such as oxygen, ammonia, hydrogen, etc., and other pressures greater than atmospheric may also be used. The process of the invention will now be more particularly described by way of examples which particularly illustrate the removal of lubricating oils and grease from the aluminium-based sheet or part as the sheet or part undergoes the present solventless, thermal degreasing process. The following examples also compare the various process parameters, such as time, temperature, type of oil and reactive atmosphere components. It should be noted that it is preferred to tailor aforementioned parameters to the specific organic contaminant sought to be removed from the sheet or part. Using air as the reactive atmosphere is preferred since it removes most all the forming die lubricants used in the automotive industry. Table I shows the various aluminium-based sample sheets which were initially coated with various oils: SAMPLE PREPARATION Sample A1-1 As received (not cleaned) A1-2 Ultrasonically cleaned in detergent and vapour degreased A1-3 Coated with press-working oil (#7B-1 for the radiator header from Oak International Chemical); degreased with trichloroethane A1-4 Surface pretreatment of A1-3; thermally degreased 1/2 hour at 400°C in vacuum A1-5 Coated with Anderson oil (Windsor-Durel #92385C oil from Anderson oil and Chemical Company); thermally degreased 1/2 hour at 400°C in vacuum A1-6 Coated with press-working oil; thermally degreased 1/6 hour at 400°C in vacuum A1-7 Duplicate of A1-3 A1-8 Surface pretreatment of A1-3; thermally degreased 1/2 hour at 400°C in air A1-9 Surface pretreatment of A1-5; thermally degreased 1/2 hour at 400°C in air A1-10 Surface pretreatment of A1-6; thermally degreased 1/2 hour at 400°C in air The study of this example determined the thermal degreasing residues under both vacuum and air reactive atmospheres. Subsequently, surface analyses were performed with X-ray Photoelectron Spectrosopy (hereinafter XPS) which is a technique that provides an analysis of the top 40 angstroms of the surface. Two oils were used on the samples which were all made from aluminium braze sheet, MD-177, with both sides clad. One oil was Oak International Chemical press-working oil #7B-1 for radiator headers (referred to in Table I as press-working oil), and the other oil was Windsor-Durel #92385C thermal degreasing oil from Anderson Oil & Chemical Company (referred to in Table I as Anderson oil). Because the Anderson oil has a lower viscosity in comparison to the press-working oil, significantly lighter loadings were obtained therewith. The oils were applied to one surface of the sample by swabbing. Table I describes the surface pretreatment and oil loading combinations studied. Table II below illustrates the oil coating weights: OIL COATING WEIGHTS Samples Weight of Oil Coating (g/cm²) Weight Loss in Thermal Degreasing (g/cm²) (In Vacuum) A1-5 0.072 0.109 A1-6 0.240 0.277 (In Air) A1-9 0.047 0.052 A1-10 0.211 0.239 Table II would indicate that, the present invention's thermal degreasing process removed more volatile material from the surfaces of the samples than can be accounted for by the oil coating weight. However, a much more sensitive measure of the residue remaining after degreasing has been obtained with XPS, and the results are shown in Table III: With regard to Table III and each aluminium-based sample therein, the following composition characteristics of the surfaces were noted. The sample A1-1 had a contamination layer composed mainly of 84% carbon (7% carbonyl type binding and 93% hydrocarbon). The small aluminium concentration detected and the absence of metallic aluminium indicates that the hydrocarbon layer is roughly as thick as the escape depth of the secondary electrons being used in the analysis which is approximately 40 angstroms. Sample A1-2 had a contamination layer composed of 38% carbon (24% carbonyl and 76% hydrocarbon), 35% oxygen and 22% aluminium (see Table III). Sample A1-2, which was not coated with an oil layer, was first ultrasonically cleaned in detergent and subsequently vapour degreased. The results indicate that the contamination has been reduced in thickness (about 40 angstroms) by the degreasing process. Sample A1-3, which was coated with press working oil, was degreased with trichloroethane. The contamination layer thickness was similar to the ultrasonically degreased surface of sample A1-2. The sample A1-3 layer was composed of 44% carbon (25% carbonyl and 75% hydrocarbon), 31% oxygen and 19% aluminium (see Table III). Similar results are shown for Sample A-7. Again, the resulting thickness of the organic residue and the underlying oxide layer was approximately 40 angstroms. For comparison, samples A1-4, A1-5, and A1-6 were thermally degreased under vacuum at 1x10-5 Torr (1.3x10-3 Pa) and at a temperature of 400°C. The contamination layer of A1-4 was composed of 50% carbon (19% carbonyl and 81% hydrocarbon), 20% oxygen, 18% aluminium and 6% magnesium (see Table III). The combined thickness of the organic residue and oxide layer is larger than that of A1-2 and A1-3. The resulting larger carbon and smaller oxygen concentrations indicate that a thicker organic layer is responsible for the difference. Sample A1-5 was coated with Anderson Oil and also thermally degreased under vacuum conditions at 400°C. The low-level contamination layer consisted of 42% carbon (14% carbonyl and 86% hydrocarbon), 30% oxygen, 19% aluminium and 6% magnesium (see Table III). XPS results indicated that the combined thickness of the organic residue and oxide layer was minimal, and similar to samples A1-2 and A1-3 which were solvent degreased. Sample A1-6 also had a low-level contamination layer which consisted of 36% carbon (13% carbonyl and 87% hydrocarbon), 34% oxygen, 17% aluminium, 6% magnesium and 4% phosphorous (see Table III). Similar to samples A1-2 and A1-3, the combined thickness of organic residue and oxide layer was minimal. A small concentration of phosphorous was detected but this is attributed to the residue characteristic of press-working oil. Samples A1-8, A1-9 and A1-10 were thermally degreased in air at 400°C for 1/2 hour. Sample A1-8 was coated with press-working oil and then thermally degreased at the aforementioned conditions. The low-level contamination level consisted of 33% carbon (22% carbonyl and 78% hydrocarbon), 39% oxygen, 17% aluminium, and 10% magnesium (see Table III). As indicated by the relative concentration of metallic aluminium, the combined thickness of the organic residue and oxide layer is only marginally larger than for the degreased samples A1-2 and A1-3 and the samples thermally degreased in vacuum, A1-5 and A1-6. The larger oxygen and combined aluminium and magnesium concentrations indicate that a slightly thicker oxide layer is present, presumably composed of a duplex of magnesium and aluminium oxide. The results indicate that the oxide layer is only marginally thicker than found with the vacuum thermal degreasing process and of further importance, the organic residue is minimal. Subsequent brazing test have shown that the small amount of oxidation occurring during thermal degreasing in air does not degrade fluxless braze performance. Sample A1-9 which was coated with Anderson Oil also had a low-level contamination layer primarily consisting of 33% carbon (21% carbonyl and 79% hydrocarbon), 38% oxygen, 16% aluminium and 11% magnesium (see Table III). The results indicated that the precent of carbon with carbonyl type bonding and the concentration of magnesium were increased by thermally degreasing in air relative to vacuum which indicates that oxidation of the organic contaminant and the magnesium occurs more readily in air processing. Relative thicknesses of the organic and oxide layers were similar to those observed with sample A1-8. Sample A1-10, which was coated with press-working oil and thermally degreased in air at 400°C, had a contamination layer consisting of 30% carbon (21% carbonyl and 79% hydrocarbon), 41% oxygen, 16% aluminium, and 10% magnesium (see Table III). The results indicated some oxidation of the organic contaminant and magnesium. The thickness of the organic and oxide layers were similar to samples A1-8 and A1-9. Also, the residual phosphorous level was approximately half the level resulting from vacuum processing which implies that oxidation had assisted in the removal of the residue. The aforementioned results indicate that thermal degreasing in air is preferable over a vacuum or solvent vapour. Thus, solventless thermal degreasing in air provides a viable alternative to vapour degreasing using a solvent such as trichloroethylene and also provides a more cost-effective reactive atmosphere. It should be noted that the preferred aluminium-based sheet or part will be one which is in need of cleaning so as to improve its subsequent brazability.

Claims: A method of brazing aluminium-based sheets or parts which comprises providing said aluminium-based sheet or part having organic contaminants thereon and heating said sheet or part in the presence of a reactive gas selected from air, oxygen, ammonia or hydrogen at least at atmospheric pressure and at a temperature of between 300 and 400°C for 10 minutes to 30 minutes to volatilise and remove said organic contaminants by reacting said organic contaminants with said reactive gas and brazing said sheets or parts with a brazing material. A process as claimed in Claim 1 wherein said reactive gas is air or oxygen. A process as claimed in either Claim 1 or Claim 2, wherein said temperature of heating is approximately 400° C. A process as claimed in any one of the preceding claims, wherein said organic contaminants are oils and grease. A process as claimed in any one of the preceding claims, wherein said aluminium-based sheet or part is a formed aluminium assembly. A process as claimed in Claim 5, wherein said organic contaminants are forming-die lubricants. A method as claimed in any one of the preceding claims wherein said aluminium-based sheets or part contains magnesium. A method as claimed in any one of the preceding claims, wherein said brazing is a fluxless brazing. A method as claimed in Claim 8, wherein said brazing material is a filler metal alloy containing approximately 89% aluminium, 1.5% magnesium, and 9.5% silicon. A method as claimed in Claim 8 or 9, wherein said fluxless brazing takes place in a vacuum at around 600°C.

Inventors: BADGLEY SCOTT J, BAUMGARTNER LINDA J, WINTERBOTTOM WALTER, BADGLEY, SCOTT J., BAUMGARTNER, LINDA J., WINTERBOTTOM, WALTER
Applicants: FORD FRANCE, FORD MOTOR CO, FORD WERKE AG, FORD FRANCE S. A., FORD MOTOR COMPANY LIMITED, FORD-WERKE AKTIENGESELLSCHAFT
Application year: 1990
Main classification: C23G5
IPC codes: B23K1, B23K103, C23G5