Diester and keto-ester derivatives of polyhydroxy compounds and production thereof

Abstract: The present application provides a compound represented by the formula (1); G(X- --OR₁) n (I) wherein G is a residue of an active hydrogen-containing compound G-(X-H) n , or an alkyl, aryl, aralkyl, alkenyl, alkynyl group having 3 to 20 carbon atoms which may contain oxygen or nitrogen atoms, or a polymeric compound residue, X is a oxygen atom or -CH₂, n is an integer of 3 to 1,000, R₁ is a hydrogen atom, a C₁-C₅ alkyl group or an aryl group, and a production thereof.

Description: The present invention relates to novel diester and keto-ester derivatives of polyhydroxy compounds and to a method for producing them. BACKGROUND OF THE INVENTION It is known that an alpha-ketoester group (-CO-CO-OR') is a chemically-active group which can be ester-exchanged with an active hydrogen-containing compound, such as an alcohol or an amine, or can be easily hydrolysed. EP-A-0049910 discloses copolymers of, inter alia, A-(CO) m -CO-COOR, wherein m is 0 or 1, A is an organic group containing a polymerisable group, and R is an aliphatic moiety. SUMMARY OF THE INVENTION The present invention provides a compound represented by formula I G-(-X-CO-CO-OR₁) n I which can be derived from the corresponding active hydrogen-containing compound G(OH) n , or wherein G is an alkyl, alkenyl or alkynyl group having 3 to 20 carbon atoms, or an aryl or aralkyl group of up to 20 carbon atoms, either of which groups may contain oxygen or nitrogen atoms, or a polymeric compound residue; X is -O-or -CH₂-, provided that, when X is -CH₂-, G is not a polymeric compound residue; n is an integer of 3 to 1,000; and R₁ is H, C₁-C₅ alkyl or aryl. The present invention also provides a method for producing the above mentioned compounds. Further, the present invention provides a curable composition which contains the above mentioned compound as curing agent. DETAILED DESCRIPTION OF THE INVENTION The invention compound can be prepared by reacting an active hydrogen-containing compound (II); G-(-X-H) n (II) [wherein G, X and n is the same as mentioned above.] with an ester compound (III); [wherein Y is a halogen atom or R₁O, R₁ is the same as mentioned above]. The active hydrogen-containing compound (II) is a compound which has at least three hydroxyl groups. The compound can be either low molecular weight or high molecular weight. It includes polyhydric alcohols, polyester polyols, polyether polyols, polyurethane polyols, polyvinyl alcohols, phenol resins, hydroxyl-containing polybutadine, hydroxyl-containing polychloroprene, ring-opened epoxy resins, amino resins. Typical examples of the polyhydric alcohols are glycerol, trimethylolpropane, 1,2,4-butanetriol, cyclohexanetriol, cyclohexanetrimethylol, pentaerythritol, dipentaerythritol, amylose, lactose, sucrose, mannitol, maltose. Typical examples of the polyester polyols are a condensate of a polyhydric alcohol as mentioned above and a polybasic acid or an anhydride thereof (e.g. phthalic acid, tetrahydrophthalic acid, tetrachlorophthalic acid, hexahydrophthalic acid, succinic acid, maleic acid, fumaric acid, adipic acid, sebacic acid, trimellitic acid, pyromellitic acid etc.); a reaction product of a polyhydric alcohol as mentioned above with an epoxy compound (e.g. n-butyl glycidyl ether, allyl glycidyl ether, Cardura E available from Yuka Shell Company etc.); an alkyl polyol (a product of a polyhydric alcohol and oil (e.g. soybean oil and safflower oil)); a ring open product of e-caprolactone. Examples of the polyether polyols are an adduct of a polyhydric alcohol as mentioned above and an alkylene oxide (e.g. ethylene oxide, propylene oxide, tetrahydrofuran). The polyurethane polyol may be prepared by reacting a polyol as mentioned above and a polyisocyanate compound. Examples of the polyisocyanate compounds are ethylene diisocyanate, propylene diisocyanate, tetramethylene diisocyanate, hexamethylene diisocyanate, 1-methyl-2,4-diisocyanatocyclohexane, 1-methyl-2,6-diisocyanatocyclohexane, diisocyanatodimethylxylene, diisocyanatodiethylxylene, lysine diisocyanate, 4,4′-methylenebis(cyclohexylisocyanate), 4,4′-ethylenebis(cyclohexylisocyanate), alpha, alpha′-diisocyanato-1,3-dimethylbenzene, alpha, alpha′-diisocyanato-1,4-dimethylbenzene, isophorone diisocyanate, 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 1,5-naphthylene diisocyanate, 4,4′-methylenebis(phenyleneisocyanate), triphenylmethane triisocyanate and a polymer thereof. The polyol for the polyurethane polyol may be polymeric polyol, such as polyether polyol or polyester polyol. Examples of the phenol resins are a novolac or resol type phenol resin, rosin modified phenol resin, alkylphenol resin, butylated resol resin, allyl ether resol resin. Examples of the amino resins are melamine, guanamine, a reaction product of urea and formaldehyde. The ester compound (III) employed in the present invention includes oxalic diesters, such as dimethyl oxalate, diethyl oxalate, diisopropyl oxalate, dibutyl oxalate, diphenyl oxalate etc.; alkoxalyl halides, such as methoxalyl chloride, ethoxalyl chloride. If the ester compound (III) is the alkoxalyl halide (Y is halogen), the reaction between the compound (III) and the compound (II) is a dehydrohalogenation reaction which quantitatively progresses. The reaction may be carried out at -20 to 150 °C, preferably 0 to 50 °C in an inert solvent. Examples of the inert solvents are aliphatic hydrocarbons, such as pentane, hexane and heptane; aromatic hydrocarbons, such as benzene, toluene and xylene; cycloaliphatic hydrocarbons, such as cyclohexane, methylcyclohexane and decalin; petroleum hydrocarbons, such as petroleum ether and petroleum benzine; halogenated hydrocarbons, such as carbon tetrachloride, chloroform, 1,2-dichloroethane; ethers, such as ethyl ether, isopropyl ether, anisol, dioxane and tetrahydrofuran; ketones, such as acetone, methyl ethyl ketone, cyclohexanone, acetophenone and isophorone; esters, such as ethyl acetate, butyl acetate, propyleneglycol monoethyl ether acetate and ethyleneglycol monoethyl ether acetate; acetonitrile; dimethylformamide; dimethylsulfoxide. Removal of the byproduct hydrogen chloride may be carried out by a method wherein nitrogen gas is blown into the reaction vessel, or a method wherein hydrogen chloride is reacted with a tertiary amine to form a salt of HCl which is removed out. If the compound (III) is the oxalic diester (Y is - OR₁), the reaction between the compound (III) and the compound (II) is an ester exchange reaction which is generally carried out using large excess dialkyl oxalate in the presence of a catalyst. The amount of the dialkyl oxalate is 2 to 20 times, preferably 3 to 8 times larger than the molar amount of the compound (II) and the reaction temperature is within the range of -20 to 150 °C, preferably 0 to 50 °C. The reaction may be carried out in an inert solvent as mentioned above. Typical examples of the catalysts are tin compounds, such as dibutyltin dilaurate, dibutyltin oxide and monobutyltin triheptate; mixture catalysts, such as dimethyltin diiodide and tetraphenylantimony iodide, dimethyltin diiodide and hexamethyl phosphoric triamide; acidic compounds, such as p-toluenesulfonic acid, dodecylbenzenesulfonic acid, sulfuric acid, chloric acid, nitric acid and boron trichloride etherate; basic compounds, such as triethylamine, 1,4diazabicyclo[2,2,2]octane, 1,8-diazabicyclo[5,4,0]undecene-7, pyridine sodium methoxide, sodium ethoxide and t-butoxypotassium hexamethylphosphoric triamide; metal oxides or metal salts, such as manganese acetate, cobalt acetate, calcium acetate, lithium acetate, zinc acetate, magnesium acetate, antimony trioxide, lead dioxide, ferric chloride, aluminum triisopropoxide and tetraisopropoxy titanium. The obtained product may be purified by distillation, chromatography etc. Distillation is generally effected at a reduced pressure [atmospheric pressure to 1.333 Pa (0.01 mmHg)] at a temperature of room temperature to 180 °C, preferably 50 to 120 °C in the presence of zeolite or with stirring. The obtained product is generally liquid or an oil and its yield is more than 70 %. Since the poly(alpha-ketoester) compound of the present invention has plural alpha-ketoester groups which is very active, it is applicable to paint, adhesive, electronic material, molding, plastics and the like. The compound may be combined with a polyol to form a curable composition which is very suitable for coating or adhesive. If the poly(alpha-ketoester) compound of the present invention is combined with a compound having plural active hydrogens, especially polyhydroxyl compound, to obtain curable composition, the cured article has excellent physical properties in acid resistance and low temperature curing properties. Examples of the polyhydroxyl compounds are polyhydric alcohol, acryl polyol, polyester polyol, polyether polyol, polyurethane polyol, polyvinyl alcohol, phenol resin, polyhydroxyl-containing butadiene or polychloroprene, ring opened epoxy resin and polyorganopolysiloxane polyol. These polyhydroxyl compound are the same as listed above in the active hydrogen-containing compound (II), but may include diols and acryl polyol. Typical examples of the diols are 3-allyloxy-1,2-propane diol, 2,2-bis(chloromethyl)-1,3-propane diol, 2-bromo-2-nitro-1,3-propane diol, 3-bromo-1,2-propane diol, butane diol, butyne diol, cyclohexane diol, cyclooctane diol, cyclopentane diol, decalin diol, decane diol, ethylene glycol, propylene glycol, dihydroxyacetophenone, dihydroxyanthraquinone, dihydroxybenzophenone, hydroxybenzylalcohol, catechol. The acryl polyol is a polymer of a hydroxyl containing ethylenically unsaturated monomer. Examples of the hydroxyl containing unsaturated monomers are 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 2-hydroxybutyl (meth)acrylate. The acryl polyol may be a copolymer of the above mentioned monomers with other monomers. Examples of the other monomers are methyl (meth)acrylate, ethyl (meth)acrylate, n-butyl (meth)acrylate, isobutyl (meth)acrylate, ethylhexyl (meth)acrylate, alpha-methylstyrene, vinyltoluene, t-butylstyrene, ethylene, propylene, vinyl acetate, vinyl propionate, acrylonitrile, methacrylonitrile, dimethylaminoethyl (meth)acrylate. The curable composition of the present invention may generally contain a catalyst as mentioned in the synthesis of the poly(alpha-ketoester) compound. The catalyst may be present in the composition in an amount of 0.0001 to 10 % by weight, preferably 0.001 to 5 % by weight based on the total amount of the poly(alpha-ketoester) and the polyhydroxyl compound. The curable composition may contain a solvent if necessary. The solvent can be the inert solvent as mentioned above, but alcohols (e.g. ethylene glycol, 2-ethylhexanol, t-butanol, n-hexanol, n-butanol, cyclohexanol, isopropanol, n-propanol, benzyl alcohol, ethanol, methanol) may be employed. The solvent may be present in the composition in an amount of 0.01 to 90 % by weight, preferably 0.5 to 80 % by weight, but alcohols are preferably less than 50 % by weight because they are ester-exchanged with alkoxalyl ester. The curable composition may be cured at a temperature of 70 to 200 °C, preferably 90 to 180 °C for 5 minutes to 2 hours, preferably 10 minutes to one hour. EXAMPLES The present invention is illustrated by the following Examples which, however, are not construed as limiting the present invention to their details. Example 1 Preparation of triethoxalyltrimethylolpropane To a 100 liter three neck flask was added 40 ml of tetrahydrofuran, 1,53 g (11 mmol) of trimethylolpropane and 3.46 g (51 mmol) of triethylamine, and cooled with ice. With stirring, 20 ml of a tetrahydrofuran solution of 4.68 g (51 mmol) of ethoxyalyl chloride was added over 1 hour. After mixing at room temperature for 2 hours, a solution of 2.34 g (17 mmol) of ethoxyalyl chloride in 15 ml of tetrahydrofuran was further added for 15 minutes and mixed at room temperature for 15 minutes. The deposited salt was filtered and condensed, and subjected to distillation with a Kugel distillation apparatus to obtain 2.19 g (yield 44 %) of the aimed compound. Physical properties of the compound are as follow; Boiling point 215 °C/5.33 Pa (0.04 mmHg) ¹³C-NMR a; 7.10, h; 13.70, b; 22.78, c; 41.00, g; 63.14, d; 65.70, f; 156.66, e; 157.19 IR spectrum 3000 (CH) 1750, 1780 (C=O) 1160, 1180 (C-O) Example 2 Preparation of triethoxalyltrimethylolpropane A reaction vessel equipped with a stirrer, a condenser and a decanter was charged with 500 g (3.42 mol) of diethyl oxalate, 31.3 g (0.23 mol) of trimethylolpropane and 1 g (0.0053 mol) of p-toluenesulfonic acid one hydrate, and mixed at 130 °C for 5 hours. After removing 32.3 g of ethanol, it was then cooled and excess amount of diethyl oxalate was evaporated to obtain 106.1 g of crude triethoxalyltrimethylolpropane (yield 85 %). Example 3 Preparation of triethoxalyltrimethylolpropane A reaction vessel equipped with a stirrer, a condenser and a decanter was charged with 743.1 g (5 mol) of diethyl oxalate, 56.9 g (0.42 mol) of trimethylolpropane and 0.55 g (0.8 mmol) of dibutyltin dilaurate, and mixed at 130 °C for 5 hours. After removing 58.6 g of ethanol, it was then cooled and excess amount of diethyl oxalate was evaporated to obtain 158.7 g of crude triethoxalyltrimethylolpropane (yield 87 %). Example 4 Preparation of tetraethoxalylpentaerythritol A reaction vessel was charged with 40 ml of tetrahydrofuran, 1.36 g (0.01 mol) of pentaerythritol and 6.06 g (0.06 mol) of triethylamine, and cooled with ice. To the mixture was added dropwise 8.19 g (0.06 mol) of ethoxalyl chloride for one hour. It was refluxed for 6 hours to terminate reaction. Then, the solvent was removed to obtain 5.0 g of crude product. The crude product was subjected to column chromatography (hexane/ethyl acetate = 1/1 (v/v)) to obtain 2.5 g of the amined compound (yield 46.3 %). ¹³C-NMR f; 13.85, a; 42.45, e; 63.52, b;63.92, d; 156.60, c; 156.94 IR spectrum 3000 (CH) 1740, 1760 (C=O) 1155, 1195 (C-O) Example 5 Synthesis was conducted as generally described in Example 3, with the exception that 42.4 g (0.167 mol) of dipentaerythritol was employed instead of 56.9 g of trimethylolpropane to obtain 128.4 g of crude hexaethoxalyldipentaerythritol (yield 90 %). Reference Example 1 Preparation of ethoxalyl modified polyester resin A reaction flask equipped with a heater, a stirrer, a condenser, a water separator, a fractionating column and a thermometer was charged with 386 parts by weight of trimethylolpropane, 312 parts by weight of neopentyl glycol, 350 parts by weight of neopentylglycol pivalate, 160 parts by weight of adipic acid, 730 parts by weight of isophthalic acid and 0.4 parts by weight of dibutyltin dilaurate, and dissolved at 80 to 100 °C. When it was liquefied, mixing started and it was heated to 160 °C. It was then heated slowly to 220 °C for three hours with removing water. At 220 °C, reaction was continued for 2 hours. Then, xylene was added thereto and reaction was continued with refluxing xylene. Reaction was terminated when acid value was 14.0, and cooled. After cooling, 600 parts by weight of xylene was added to form a polyester resin varnish A. The varnish had a solid content of 79.9 %, a viscosity of XY and an acid value of 9.9. Example 6 A reaction vessel equipped with a heater, a stirrer, a reflux apparatus, a decanter and a thermometer was charged with 814 parts by weight of the polyester resin varnish of Reference Example 1, 1426 parts by weight of diethyl oxalate and 13 parts by weight of dibutyltin dilaurate, and heated to 130 °C for 30 minutes. At 130 °C, reaction was continued as removing producing ethanol. Reaction was terminated when the absorption peak of a hydroxyl group disappeared by IR spectrum, and cooled to 50 °C. It was then heated to 100 °C, and remaining diethyl oxalate and xylene were removed under vacuum to obtain a diethyl oxalate-modified polyester resin B. The resin had a viscosity of 690 poise at 25 °C by E type viscometer. Example 7 A resin composition was prepared by mixing 1.34 g of triethoxalyltrimethylolpropane of Example 1, 8.66 g of the acryl polyol of Reference Example 2 and 1 wt % / solid content of dibutyltin laurate. It was coated on a tin plate by a bar coater at a thickness of 20 microns. The coating was baked at four different temperatures and curing properties were evaluated. The result is shown in Table 1. This shows that the combination of the ethoxalyltrimethylolpropane and an acryl polyol provides excellent curing properties. Number Curing temp. (°C) Nonvolatile content (%) Gellation % 1 110 96.4 80.5 2 96.3 81.6 1 130 94.8 93.6 2 95.0 94.2 1 150 94.0 95.6 2 94.3 96.0 1 180 91.8 97.0 2 92.2 97.4 Reference Example 2 Preparation of an acryl polyol A one liter reaction vessel equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 180 g of butyl acetate and heated to 120 °C. The following monomers were added over 3 hours from the dropping funnel; 142.7 g of methyl methacrylate, 87.7 g of n-butyl acrylate, 69.6 g of 2-hydroxyethyl methacryate and 4.5 g (1.5 wt % / monomers) of azobisisobutylonitrile. After mixing for 0.5 hours, 1.5 g of azobisisobutylonitrile and 30 g of butyl acetate were added and then mixed for 1.5 hours. After cooling, a transparent light yellow polymer was obtained. It had Mn 8870, hydroxyl value 100, Mw 20,600 and α 2.31. Reference Example 3 Preparation of an acryl polyol A 200 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 21.8 g of xylene and heated to 135 °C. The following mixture was added dropwise for three hours;6.3 g of a curing agent (Kaya ester O available from Akzo Chemical Company), 6.3 g of xylene and a monomer mixture of FM-2 (a compound prepared by ring-opened 2-hydroxyethyl methacrylate with ε-caprolactone; available from Daisel Chemical Industries Co., Ltd.)/styrene/isobutyl methacrylate/alpha-methylstyrene dimer (55.2/10.2/27.4/10.2 weight ratio). After mixing for 5 hours, 5.0 g of xylene and 0.63 g of Kaya ester O were added dropwise for one hour. After the completion of dropping, mixing was continued for 1.5 hours and heated to remove 15 g of xylene. It was then cooled to room temperature to obtain a transparent light yellow resin. It had a viscosity of 326 cps at 25 °C by an E type viscometer. The resin had a nonvolatile content of 70 % at 130 °C for 30 minutes. Example 8 Triethoxalyltrimethylolpropane (TETMP) and the acryl polyol were mixed with 1 wt % / solid content of dibutyltin dilaurate. The resultant composition was coated on a tin plate by a bar coater No. 40, and then baked at 130 or 150 °C for three minutes. Curing properties were evaluated and the results were shown in Table 2. The same test as mentioned above was effected with the exception that hexaethoxalyldipentaerythritol (HEODPE) of Example 5 was employed instead of triethoxalyltrimethylolpropane (TETMP). Curing agent (weight) Amount of the polyol Acetone 130 °C rubbing test 150 °C TETMP (0.91g) 4.39 g 9 22 HEODPE(0.89g) 4.43 g 8 10 Example 9 A two liter flask equipped with a stirrer, a condenser, a decanter and an inlet for nitrogen gas was charged with 200 g of PLACCEL 303 (a trifunctional polyol having OH value 538.2, acid value 0.54, Mn(GPC) 640; available from Daisel Chemical Industries Co., Ltd.), 1402 g of diethyl oxalate and 2 g of dibutyltin dilaurate, and mixed at 120 to 130 °C for 6 hours, during which 95.0 g of a mixture of ethanol and diethyl oxalate was distilled away. The reaction mixture was cooled and then excess amount of diethyl oxalate was removed using evaporator to obtain 401 g of ethoxalated PLACCEL 303 (yield 103 %). It was light brown milky liquid and had a viscosity of 451 CP, a nonvolatile content of 89 % and Mn (GPC) of 1,010. Examples 10 to 14 Different PLACCEL as shown in Table 3 was employed and ethoxalation reaction was conducted as generally described in Example 8 in the conditions as shown in Table 4. Table 4 also shows the characteristics of the ethoxalated compound. Example PLACCEL number Functional number OH value Acid value Mn (GPC) 10 305 3 307.5 0.66 990 11 308 3 197.2 0.60 1550 12 489 4 462.0 0.72 920 13 574 4 313.8 0.83 1230 14 688 6 274.2 1.50 1940 Example 15 A 3 liter flask equipped with a stirrer, a condenser, a decanter and an inlet for nitrogen gas was charged with 104.4 g of 1,3,5-trishydroxyethyl isocyanulate having OH value 647, acid value 0.39 and molecular weight 261, 2631 g of diethyl oxalate and 2.1 g of dibutyltin dilaurate, and mixed at 100 °C for 3 hours in a nitrogen atmosphere, during which 19 g of a mixture of ethanol and diethyl oxalate was distilled away. The reaction mixture was cooled and then excess amount of diethyl oxalate was removed using evaporator to obtain 560 g of 1,3,5-trishydroxyethyl isocyanulate (yield 100 %). It was white solid and had a nonvolatile content of 98.3 % and Mn (GPC) of 760. Example 16 A 2 liter flask equipped with a stirrer, a dropping funnel and a condenser was charged with a solution of 190 g of an epoxy resin having Mw 380 and epoxy equivalent 189 (EP-828 available from Yuka Shell Company) and 130 g of methyl ethyl ketone, and heated to 50 °C. To the content, a solution of 105 g (1 mol) of diethanolamine in 100 ml of acetone was added dropwise for 30 minutes. After completion of dropping, it was heated to 70 °C at which the reaction started and exothermed to 78 °C. Mixing was then continued for 3 hours and the reaction was terminated when IR spectrum showed that the absorption of an epoxy group disappeared. Next, after distilling off methyl ethyl ketone and acetone, 1460 g of diethyl oxalate and 1.9 g of dibutyltin dilaurate were added and heated to 100 °C. Mixture was continued for 8 hours with distilling ethanol off. The reaction was terminated when 65 ml of ethanol was distilled off. Excess amount of diethyl oxalate was removed under a reduced pressure to obtain 592 g of an ethoxalated epoxy resin. Example 17 A 2 liter flask equipped with a stirrer, a dropping funnel and a condenser was charged with a solution of 300 g of an epoxy resin having Mw 900 and epoxy equivalent 450 (EP-1001 available from Yuka shell Company) and 130 g of methyl ethyl ketone, and heated to 50 °C. To the content, a solution of 50 g (0.667 mol) of diethanolamine in 100 ml of acetone was added dropwise for 30 minutes. After completion of dropping, it was heated to 100 °C at which the reaction started and exothermed to 120 °C. Mixing was then continued for 3 hours and the reaction was terminated when IR spectrum showed that the absorption of an epoxy group disappeared. Next, after distilling off methyl ethyl ketone and acetone, 1168 g of diethyl oxalate and 3.0 g of dibutyltin dilaurate were added and heated to 120 °C. Mixture was continued for 8 hours with distilling ethanol off. The reaction was terminated when ethanol was distilled off. Excess amount of diethyl oxalate was removed under a reduced pressure to obtain 719 g of an ethoxalated epoxy resin having a molecular weight of 3,187 (GPC). Reference Example 4 Preparation of monoethyl oxalate A reaction flask equipped with a condenser, a thermometer and a stirrer was charged with 1,461 g (1.0 mol) of diethyl oxalate, 4.38 g of p-toluenesulfonic acid and 400 ml of dioxane, and refluxed for 4 hours. Then, it was distilled at a reduced pressure to obtain 133.4 g of monoethyl oxalate having a boiling point of 107 °C / 1600 Pa (12 mmHg). Example 18 A 2 liter flask equipped with a stirrer, a dropping funnel and a condenser was charged with a solution of 133 g of an epoxy resin having Mw 380 and epoxy equivalent 189 (EP-828 available from Yuka Shell Company) and 70 g of methyl ethyl ketone, 73.5 g of toluene, 1.1 g of dimethylbenzylamine and mixed at room temperature. To the content, 82.6 g of monoethyl oxalate was added dropwise for minutes. The reaction mixture exothermed to 80 °C. Refluxing was continued for 4 hours and the reaction was terminated when IR spectrum showed that the absorption of a carboxyl group disappeared. Methyl ethyl ketone and acetone were distilled off to obtain an ethoxalated epoxy resin. Example 20 A 200 ml flask equipped with a stirrer, a dropping funnel and a condenser was charged with 35,8 g of an aliphatic epoxy compound (ERL-4221 available from Union Carbide Co., Ltd.), 30 g of toluene and 0.315 g of dimethylbenzylamine, and mixed at room temperature. To the content, a solution of 41.3 g of monoethyl oxalate in 70 g of toluene was added dropwise for 60 minutes. The reaction mixture exothermed a little. Refluxing was continued for 3 hours and the reaction was terminated when IR spectrum showed that the absorption of a carboxyl group disappeared. Methyl ethyl ketone and acetone were distilled off to obtain 64.4 g of an ethoxalated epoxy resin.

Claims: A compound of formula I G-(-X-CO-CO-OR₁) n I which can be derived from the corresponding active hydrogen-containing compound G(OH) n , or wherein G is an alkyl, alkenyl or alkynyl group having 3 to 20 carbon atoms, or an aryl or aralkyl group of up to 20 carbon atoms, either of which groups may contain oxygen or nitrogen atoms, or a polymeric compound residue; X is -O-or -CH₂-, provided that, when X is -CH₂-, G is not a polymeric compound residue; n is an integer of 3 to 1,000; and R₁ is H, C₁-C₅ alkyl or aryl. A compound according to claim 1, wherein X is -O-. A compound according to claim 2, wherein G is the residue of a polyhydric alcohol, a polyester polyol, a polyether polyol, a polyurethane polyol, a ring-opened epoxy resin, a polyvinyl alcohol, an amino resin, a phenol resin, a hydroxyl group-containing polybutadiene, or a hydroxyl group-containing polychloroprene. A compound according to claim 1, which is triethoxalyltrimethylolpropane. A compound according to claim 1, which is tetraethoxalylpentaerythritol. A process for preparing a compound according to any preceding claim, which comprises reacting the corresponding active hydrogen-containing compound G(OH) n with an ester of formula III Y-CO-CO-OR₁ III wherein Y is a halogen atom or R₁O and R₁ is as defined in claim 1. A process according to claim 6, wherein the active hydrogen-containing compound is a polyhydric alcohol. A process according to claim 6 or claim 7, wherein the ester is an oxalic acid diester or an alkoxalyl halide. A curable composition comprising a compound according to any of claims 1 to 5 and a compound having at least two hydroxyl groups. A curable composition according to claim 9, wherein the compound having at least two hydroxyl groups is a polyhydric alcohol, an acryl polyol, a polyester polyol, a polyether polyol, a polyurethane polyol, polyvinyl alcohol, a phenol resin, a hydroxyl group-containing polybutadiene, a hydroxyl group-containing chloroprene, a ring-opened epoxy resin or organopolysiloxane.

Inventors: AOKI KEI, MORI HIROHIKO, TAKAGAWA RYOZO, TOMITA NOBUAKI, AOKI, KEI, MORI, HIROHIKO, TAKAGAWA, RYOZO, TOMITA, NOBUAKI
Applicants: NIPPON PAINT CO LTD, NIPPON PAINT CO., LTD.
Application year: 1990
Main classification: C07C69
IPC codes: C08G63, C08G8, C08G59, C07D251, C08G18, C08G2, C07C67, C08G65, C07C69, C08F8