Achromatic fiber optic coupler and method of making it

Abstract: An achromatic fiber optic coupler of the type wherein first (F1) and second (F2) single-mode optical fibers, each having a core and a cladding, are fused together along a portion of the lengths thereof to form a coupling region (N). A matrix glass (10) of lower index than the fiber claddings surrounds the coupling region (N). The fiber diameters are smaller in the coupling region than in the the remainder of the fibers. The refractive index n₂ of the cladding of the first fiber is different from the refractive index n'@2 of the cladding of the second fiber, the difference between the refractive indices n₂ and n'@2 being such that the coupler exhibits very little change in coupling ratio with wavelength over a band of wavelengths.

Description: This invention relates to single-mode fiber optic couplers that are capable of effecting a relatively uniform coupling of light from one fiber to another over a relatively broad band of wavelengths. Coupling occurs between two closely spaced cores in a multiple core device. Fiber optic couplers referred to herein as "fused fiber couplers" have been formed by positioning a plurality of fibers in a side-by-side relationship along a suitable length thereof and fusing the claddings together to secure the fibers and reduce the spacings between the cores. The coupling efficiency increases with decreasing core separation and, in the case of single-mode cores, with decreasing core diameter. European published patent application No. 0302745 teaches that various coupler properties can be improved by inserting the fibers into a capillary tube prior to heating and stretching the fibers, thereby resulting in the formation of an "overclad coupler". After the fibers have been inserted into the tube, the tube midregion is heated to cause it to collapse onto the fibers; the central portion of the midregion is thereafter drawn down to that diameter which is necessary to obtain the desired coupling. The coupling region of an overclad coupler is hermetically sealed, and the optical characteristics thereof are relatively insensitive to changes in temperature. The tube also greatly enhances the mechanical strength of the coupler. Identical optical fibers are used to make overclad couplers referred to herein as "standard couplers", the coupling ratio of which is very wavelength dependent. A standard coupler which exhibits 3 dB coupling at 1310 nm cannot function as a 3 dB coupler at 1550 nm because of that wavelength dependence. A 3 dB coupler is one that couples 50% of the power from a first fiber to a second fiber. A standard coupler can be characterized in terms of its power transfer characteristics in a window centered about 1310 nm, which is referred to as the first window. For example, a standard coupler might exhibit a coupling ratio that does not vary more than about ±5% within a 60 nm window. It has been known that an achromatic coupler, the coupling ratio of which is less sensitive to wavelength than it is for a standard coupler, can be formed by employing fibers having different propagation constants, i.e. by using fibers of different diameter and/or fibers of different refractive index profile or by tapering one of two identical fibers more than the other. There is no widely accepted definition of achromatic couplers. The least stringent definition would merely require an achromatic coupler to exhibit better power transfer characteristics than the standard coupler in the first window. More realistically, the specification is tightened by requiring an achromatic coupler to perform much better than the standard coupler in that first window, or to require it to exhibit low power transfer slopes in two windows of specified widths. These windows might be specified, for example, as being 100 nm wide and centered around about 1310 nm and 1530 nm. These windows need not have the same width; their widths could be 80 nm and 60 nm, for example. An optimally performing achromatic coupler would be capable of exhibiting low values of coupled power slope over essentially the entire single-mode operating region. For silica-based optical fibers this operating region might be specified as being between 1260 nm to 1580 nm, for example. It is noted that the total permissible variation in power includes insertion loss and that the permissible power variation specification becomes tighter as insertion loss increases. Furthermore, for a 3 dB coupler, for example, the coupled power at the center of the window should be 50%. If the 50% coupling wavelength is not at the center of the window, the coupled power specification becomes even tighter. In the following discussion, the relative refractive index difference Δ a-b between two materials with refractive indices n a and n b is defined as Δ a-b = (n a ² - n b ²)/2n a ² For simplicity of expression, Δ is often expressed in per cent, i.e. one hundred times Δ. A usual requirement for fiber optic couplers is that the fibers extending therefrom, referred to herein as "pigtails", be optically and mechanically compatible with standard system fibers to which they will be connected in order to minimize connection loss. For example, the outside diameter and the mode field diameter of the coupler pigtails should be substantially the same as those of a standard fiber. One of the fibers employed in the fabrication of the coupler can be a standard, commercially available fiber. That feature of the other fiber that is modified to change the propagation constant should affect the outside diameter and mode field diameter of the pigtail portion of the other fiber as little as possible. U.S. patent No. 4,798,436 (Mortimore) discloses a 3 dB fused fiber coupler wherein different propagation constants are obtained by pretapering one of the fibers. First and second identical standard fibers can be used to form such a coupler. The central portion of the first fiber is initially heated and stretched such that the core and the cladding diameter thereof in the tapered region is smaller than the core and cladding diameter of the second fiber. The pigtail portions of the stretched fiber can be connected with low loss to a standard system fiber since the ends thereof are identical to the ends of the stretched fiber. However, since a separate prestretching operation is employed for each coupler made, and since fiber diameter varies continuously along the length thereof, it is difficult to maintain process reproducibility. Also, a pretapered fiber is fragile and difficult to handle. U.S. Patent No. 4,822,126 (Sweeney et al.) teaches a 3 dB fused fiber coupler wherein Δ cores , the relative refractive index difference between the two coupler cores, is 0.061%. The value of Δ cores is obtained by substituting the two core refractive indices of the Sweeney et al. patent into equation (1) and solving for Δ. It is apparent from Fig. 6 of the Sweeny et al. patent that the value of Δ cores should have been greater than 0.061% in order to have achieved good achromaticity with standard diameter fibers. However, when Δβ is obtained by employing fibers having such large differences between the core refractive indices, the mode field diameter of one of the coupler pigtails differs sufficiently from that of a standard fiber that it will not efficiently couple to the fibers of the system in which the coupler is utilized. Rather than increasing the difference between the core refractive indices to provide a Δ cores greater than 0.061%, Sweeney et al. maintained that value of Δ cores and, in addition, etched the fiber claddings in order to improve achromaticity. The Sweeny et al. patent states that although wavelength independence is achieved, as contemplated therein, by having the cores of different indices of refraction, similar results could be achieved by keeping the cores at like indices of refraction and making the claddings one different from the other with respect to indices of refraction. It will be obvious from the following discussion that it is impossible to form achromatic overclad-type 3 dB couplers wherein the difference between the refractive indices of the fiber claddings is such that Δ clads is 0.06%, assuming that the core and cladding diameters of the two fibers are identical. The value of Δ clads is obtained by substituting the cladding index n ′ / 2 of one fiber and the cladding index n₂ of the other fiber for n a and n b , respectively, of equation (1) and solving for Δ. Summary of the Invention It is an object of the invention to provide a single-mode achromatic fiber optic coupler that is characterized by a very small change in coupled power over a wide band of wavelengths. Another object is to provide an achromatic coupler, the connection pigtails of which can be coupled with low insertion loss to system fibers. Yet another object is to provide an achromatic coupler, wherein the feature or parameter that modifies the propagation constant β of the non-standard fiber has negligible effect on the fiber mode field diameter. A further object is to provide a reproducible method of making achromatic overclad fiber optic couplers. The achromatic coupler of the invention comprises an elongated body of matrix glass having a refractive index n₃. The body includes two opposed ends and a midregion. A plurality of optical fibers extends longitudinally through the body, each of the fibers comprising a core of refractive index n₁ and a cladding of refractive index less than n₁ but greater than n₃. The refractive index n₂ of the cladding of the first fiber is different from the refractive index n ′ / 2 of the cladding of the second fiber by such an amount that the value of Δ clads is greater than zero but less than 0.03%. The fibers are fused together along with the midregion of the matrix glass. The diameters of the optical fibers in the central portion of the midregion are smaller than the diameters thereof at the ends of the body, whereby a portion of the optical power propagating in one of the fibers couples to the other of the fibers. The value of Δ clads is preferably greater than 0.005%. To form a coupler that is capable of coupling about 50% of the power from the first fiber to the second fiber at a predetermined wavelength, the value of Δ clads is preferably less than 0.02%. The refractive index n₃ is preferably such that Δ₂₋₃ is greater than 0.4%. Couplers made in accordance with the invention have exhibited an insertion loss less than 4 dB in each leg thereof over a 300 nm range of wavelengths up to 1565 nm. The achromatic fiber optic coupler of the present invention is formed by inserting into a glass tube at least a portion of each of a plurality of optical fibers so that the portions occupy the midregion of the tube. Each of the fibers comprises a core of refractive index n₁ and a cladding of refractive index less than n₁, the refractive index n₂ of the cladding of the first fiber being different from the refractive index n ′ / 2 of the cladding of the second fiber. The difference between n₂ and n ′ / 2 is such that the value of Δ clads is greater than zero but less than 0.03%. The midregion of the tube is collapsed onto fibers, and the central portion of the midregion is stretched until a predetermined coupling occurs between the fibers. The step of stretching may comprise providing relative movement between the ends of the tube, and varying the rate at which the relative movement occurs. The stretching rate can vary continuously, or the variation can occur in descrete steps. One stretching operation can stop after a predetermined coupling is achieved; thereafter, stretching can occur at a second stretch rate. The stretching operation can be stopped before a predetermined coupling is achieved; thereafter, the central portion of the tube midregion can be reheated, and the central portion of the tube midregion can again be stretched. The reheat temperature is preferably lower than the temperature to which the tube is initially heated. The last employed stretch rate may be lower than the first stretch rate. In an embodiment wherein a first fiber extends from both ends of the tube, and a second fiber extends from only the second end of the tube, the coupler preform can be stretched until some coupling begins to occur between the fibers. Detectors can be connected to the ends of the first and second fibers which extend from the second end of the tube. The coupled power is employed to maximize the power coupled from the second fiber to its respective detector. The ratio of the optical power coupled to the two detectors is used to generate the signal which stops the stretch operation. Brief Description of the Drawings Fig. 1 is a cross-sectional view of an overclad coupler. Figs. 2 and 3 are graphs of output voltage v. stretching time for couplers having two different overclad refractive indices. Fig. 4 is a graph of the coupled power slope (centered around 1310 nm) plotted as a function of Δ clads . Fig. 5 shows theoretical spectral response curves for single-window and double-window achromatic couplers wherein Δ clads is 0.005%. Fig. 6 is a graph which schematically illustrates the temporal variation in percent coupled power during the stretching of couplers having different values of Δ clads . Fig. 7 is a graph illustrating non-uniform stretch rates. Fig. 8 is a graph illustrating the effect of chlorine on Δ clads . Fig. 9 is a refractive index profile of a non-standard fiber employed in the coupler of the invention. Figs. 10-12 illustrate achromatic couplers having more than two ports at one end thereof. Fig. 13 is a cross-sectional view of a capillary tube after optical fibers have been inserted therein. Figs. 14 and 15 are schematic illustrations of two steps during the formation of an antireflection termination on a fiber. Fig. 16 is a schematic illustration of an apparatus for collapsing a capillary tube and stretching the midregion thereof. Fig. 17 is a partial cross-sectional view illustrating the collapse of the glass tube around the fibers to form a solid midregion. Fig. 18 is a partial cross-sectional illustration of a fiber optic coupler after it has been drawn down and sealed at its ends. Fig. 19 is a graph illustrating the spectral insertion loss curves for an achromatic coupler produced by the method of Example 1. Description of the Preferred Embodiments The drawings are not intended to indicate scale or relative proportions of the elements shown therein. Referring to Fig. 1, each of the optical fibers F₁ and F₂ has a core of refractive index n₁ surrounded by cladding of refractive index lower than n₁. The claddings of fibers F₁ and F₂ have different refractive indices n₂ and n ′ / 2, respectively, the values of which are such that the propagation constants of those fibers differ to the extent necessary to provide achromaticity. A coupler preform is formed by threading fibers F₁ and F₂ through glass overclad tube O, the refractive index n₃ of which is less than the refractive indices of the fiber claddings. whereas those portions of the fibers extending from the tube preferably have protective coating material (not shown in this illustrative embodiment), those portions thereof within the tube have no coating. The original diameter of the tube is d₁. The midregion of the coupler preform is evacuated and heated to collapse it onto the fibers. The tube is reheated and the ends thereof are pulled in opposite directions to increase the tube length and reduce its diameter. The combined rate at which the two tube ends move away from each other constitutes the stretch rate. The central portion of the stretched midregion constitutes neckdown region N of diameter d₂ where the fiber cores are sufficiently closely spaced for a sufficiently long distance z to effect the desired coupling therebetween. Region N is illustrated as having a constant diameter even though a slight taper exists therein, whereby the longitudinal center of section N exhibits the minimum diameter. Draw ratio R, which is equal to d₁/d₂, is a critical parameter in determining the optical characteristics of the particular device being made. A preferred range of draw ratios for achromatic overclad couplers is between about 3:1 and 10:1 depending upon the value of Δ clads and the amount of power to be coupled. Tapered regions T connect the neckdown region with the unstretched end regions of tube O. The duration of the heating period for the stretch step is shorter than that for the tube collapse step; only the central portion of the midregion is stretched. It is conventional practice to monitor output signals to control process steps in the manufacture of optical devices as evidenced by U.S. patents Nos. 4,392,712 and 4,726,643, 4,798,436, U.K. Patent Application No. GB 2,183,866 A and International Publication No. WO 84/04822. Furthermore, computers are often employed in feedback systems which automatically perform such monitor and control functions. A suitably programmed Digital PDP 11-73 micro-computer can be utilized to perform these functions. During the tube collapse and stretch steps, the ends of the tube are affixed to computer controlled stages. The amount of stretching to which the tube must be subjected to achieve given characteristics is initially determined by injecting light energy into the input fiber of a coupler preform and monitoring the output power at one or more of the output fibers during the stretch operation. If a 2x2 coupler is being formed, a light source can be connected to an input end of the first and second fibers, and a detector can be aligned with the output ends thereof, the fibers being manipulated to maximize the output power coupled to each detector. During stretching, the input end of only the first fiber is connected to a source, and the output ends of both fibers are monitored. The detection of a predetermined ratio of powers at the outputs of the first and second fibers can be used as an interrupt to cause the computer controlled stages to stop pulling the sample. If a 1x2 coupler is being formed, the second fiber cannot be accurately positioned with respect to certain detectors until some light is coupled thereto from the first fiber. An achromatic coupler can be made by monitoring only the output from the first fiber. When the output from the first fiber drops to a predetermined value, the system is instructed to stop stretching. An alternative procedure for monitoring 1x2 couplers is described below. After having determined the proper stretching distance to achieve predetermined coupling characteristics, the apparatus can be programmed to move the stages that proper stretching distance during the fabrication of subsequent couplers that are to have said predetermined characteristics. The timing sequences that have been used in the fabrication of a particular type of coupler can be entered in a separate multiple command file that the computer recalls at run-time. The collapse and stretch steps that are required to make that particular coupler can be executed in succession by the computer on each coupler preform to reproducibly manufacture couplers. The process parameters that can be controlled by the computer to ensure coupler reproducibility are heating times and temperatures, gas flow rates, and the rate or rates at which the stages pull and stretch the coupler preform. If the device that is being made is a 3 dB coupler, for example, the stretching operation is not stopped when the output power from the two fibers is equal. Various parts of the system exhibit momentum, whereby stretching of the coupler preform continues after the stage motors are instructed to stop. The coupling ratio therefore changes after the stopping signal is generated. Also, the coupling characteristics may change as a newly formed coupler cools down. Experiments can be performed on a particular type of coupler to determine that coupling ratio which must be used to generate the interrupt signal in order to achieve a predetermined coupling ratio after the device cools. Following are examples of the various stretching operations that can be performed. A. Heat the coupler preform, and stretch it at a single rate until a predetermined coupling has been achieved. B. After subjecting the coupler preform to a single heating step, stretching it at differing stretch rates until a predetermined coupling has been achieved. Two or more discrete stretch rates could be employed, or the stretch rate could continually vary with respect to time. This stretching technique has been employed to tune the power transfer characteristic, i.e. the amount of power transfered from the input fiber to the output fiber during the first power transfer cycle of the coupler preform stretching operation. C. Heat the coupler preform and perform a first stretch which does not achieve the predetermined coupling; reheat the resultant device and perform a second stretch. The heat and reheat steps may be performed at a single temperature or at different temperatures. The first and second stretch steps can be done at the same stretch rate or at different stretch rates. More than two heat and stretch steps could be performed. A species of stretching embodiment C is especially useful in the formation of 1x2 couplers. The stretching operation is temporarily terminated after some minimal amount of power has been coupled to the second fiber. For example, stretching could be stopped after the coupler preform has been stretched some predetermined distance, such as between 90% and 99% of the total distance required to achieve the final coupling ratio. The second fiber can be connected to a detector, and the power coupled to that detector can be maximized. Thereafter, a second stretching operation can be initiated, the interrupt signal being based on the ratio of the two output signals. The second stretching operation is preferably conducted at a final stretch rate that is lower than the initial stretch rate. Also, during the second stretch, it is preferable to employ a flame which has a lower temperature and/or which is less focussed than the flame employed during the first stretch. Tube O can be characterized by the symbol Δ₂₋₃, the value of which is obtained by substituting n₂ and n₃ into equation (1). Commercially available single-mode optical fibers usually have a value of n₂ that is equal to or near that of silica. If silica is employed as the base glass for the tube, a dopant is added thereto for the purpose of decreasing the tube refractive index n₃ to a value lower than n₂. In addition to lowering the refractive index of the tube, the dopant B₂O₃ also advantageously lowers the softening point temperature thereof to a value lower than that of the fibers. This enhances to a certain extent the collapsing of the tube onto the fibers; the tube glass flows around the fibers without distorting their shape. For certain purposes it may be desirable to employ a tube glass that is sufficiently hard that the tube slightly flattens the fibers as it forces the fibers together. Fluorine can also be employed to lower the tube refractive index. Suitable tube compositions are SiO₂ doped with 1 to 25 wt. % B₂O₃, SiO₂ doped with 0.1 to approximately 2.5 wt. % fluorine, and SiO₂ doped with combinations of B₂O₃ and fluorine. When Δ₂₋₃ is below about 0.2%, the amount of B₂O₃ in a silica tube is insufficient to soften the tube glass, whereby it excessively deforms the fibers during the collapse step. The value of Δ₂₋₃ for standard couplers has therefore usually been between 0.26% and 0.35%. Suitable achromatic overclad couplers have been made from preforms comprising tube and fibers exhibiting refractive index values such that Δ₂₋₃ is within that range. However, process reproducibility is enhanced by employing preforms having Δ₂₋₃ values above that previously employed range. To demonstrate the effect of the overclad glass, reference is made to Figs. 2 and 3 which are plots of the voltage from a detector connected to the output end of the input fiber during the manufacture of 1x2 couplers wherein the values of Δ₂₋₃ are 0.36% and 0.48%, respectively. Referring to Fig. 2, the output is initially highest at point a since coupling has not yet occurred. As the stretching process is initiated and power begins to couple, the power remaining in the input fiber begins to decrease at some point in time after point a. At point b, the detected power is such that the computer controlled stages are instructed to stop moving. A few microseconds later, the stretching step is terminated (point c), and the finished coupler begins to cool. During cooling, the coupled power begins to vary until it finally stabilizes at point d when it is sufficiently cool that there is no further change in stress or refractive index within the coupler. It is possible, by experimentation, to form a coupler, the 3 dB point of which is within 10 nm of the desired wavelength by causing the stretching operation to stop at some predetermined coupling other than 50%. The meandering of the coupling ratio upon cooling of the coupler can be essentially eliminated by utilizing overclad tubes of sufficiently high refractive index that the value of Δ₂₋₃ is greater than about 0.4%. This stabilizing effect is illustrated in Fig. 3 wherein reference letters similar to those of Fig. 2 are represented by primed reference numerals. The amount of coupled power begins to decrease at point a′, the computer controlled stages stop moving at point b′, and the stretching step is terminated at point c′. During cooling, the coupled power varies only slightly until it stabilizes at point d′. After the stretching has stopped (points c and c′), the coupled power will more predictably reach point d′ than point d. A theoretical analysis was made of 3 dB couplers of the type wherein Δβ was obtained by fiber cladding index difference. Coupled mode theory was used to model the behavior of the achromatic couplers [A.W. Snyder and J.D. Love, Optical Waveguide Theory , Chapman and Hall, New York, 1983]. In accordance with this theory, the mode field of the overclad coupler is assumed to be a linear combination of the fundamental modes ψ₁ and ψ₂ of each of the fibers F₁ and F₂ in the absence of the other fiber, i.e. with the fiber surrounded by overclad index n₃ only. The mode fields and propagation constants can be determined exactly for such a structure [M.J. Adams, An Introduction to Optical waveguides ]. The coupling constant which describes the optical coupling between the two cores can then be written as an overlap integral: C = ∫ψ₁(r)ψ₂(r′)(n - n′)dA In this equation, ψ₁ and ψ₂ are the mode fields of the two cores, r and r′ are the radial distances from the center of the cores of fibers F₁ and F₂, respectively, n is the index structure of the entire coupler, n′ is the index structure with the core of F₁ replaced by overcladding material of index n₃, and the integral is over the entire cross-section of the coupler (but n - n′ is only non-zero over the core and cladding of fiber F₁). The mode fields are assumed to be normalized in this equation, i.e. the integrals ∫ψ₁²dA and ∫ψ₂²dA both equal 1. While these are tapered devices, their behavior is adequately modeled by assuming a constant draw ratio over a given coupling length, with no coupling outside this length, i.e. assuming that the diameter of region N of Fig. 1 is constant over the entire length z. This approximation works well since the coupling constant is a rapidly increasing function of draw ratio, and thus the behavior of a coupler is dominated by the behavior at the highest draw ratio. Using this approximation, with the power launched into core 1, then, as a function of z, the length along the coupler axis, the power in the two cores is given by P₁(z) = 1 - F²sin²(Cz/F) and P₂(z) = F²sin²(Cz/F) where the factor F is given by where β₁ and β₂ are the propagation constants of fibers F₁ and F₂, respectively. Optimal achromatic performance was defined, for a single-window device having a center wavelength of 1310 nm and a width of 50 nm, as being the point where P₂(1297.5 nm) = P₂(1322.5 nm) = 0.5 The achromaticity was defined as Achromaticity = P₂(1335 nm) - P₂(1310 nm) 25 nm The coupled mode model was used to determine a suitable range of Δ clads . Most of the assumptions which were made concerning coupler parameters are based on work done on standard overclad couplers. Fiber F₁ was assumed to be a standard 125 µm outside diameter single-mode fiber having a core radius of 4 µm. The core and cladding refractive indices n₁ and n₂ were assumed to be 1.461000 and 1.455438, respectively. It was assumed that fiber F₂ was identical to fiber F₁ except that the cladding index n ′ / 2 was greater than n₂. The value of Δ₂₋₃ was assumed to be 0.3%. In order to determine the combination of draw ratio and length z for which achromaticity was best, P₂ was calculated at the appropriate wavelengths for a range of draw ratios. The combination of draw ratio and coupling length z which satisfied equation (6) was determined, and then the achromaticity (the variation in coupled power in percent per nanometer) calculated for that combination. As shown in Fig. 4, the theoretical analysis revealed that the variation in coupled power (at 1310 nm) increases as the value of Δ clads decreases. This is in accordance with the expected relationship whereby coupler achromaticity decreases as the difference between the fiber propagation constants decreases. The relationship shown in Fig. 4 is for couplers having a Δ₂₋₃ value of 0.3%. For couplers having greater values of Δ₂₋₃, the curve is displaced toward higher values of variation in percent coupled power. When the value of Δ clads is less than 0.005%, the variation in percent coupled power rapidly increases. The achromaticity therefore rapidly decreases at values of Δ clads below this value. Also, as the value of Δ clads decreases below 0.005%, the required length of the neckdown region increases to such an extent that the resultant achromatic coupler would be impractical in that it would be undesirably long and would be difficult to make. Fig. 5 shows the theoretical relationship of coupled power with respect to wavelength for both single-window and double-window couplers, with Δ clads = 0.005% and Δ₂₋₃ = 0.3%. The value of d₁/d₂ is 6.6 for the single-window device as determined by requiring equation (6) to be satisfied. The value of d₁/d₂ is 6.2 for the double-window device as determined by requiring an analogous equation to be satisfied for the wavelengths 1310 nm and 1550 nm. Whereas the model indicated that a draw ratio of about 6:1 would be needed to form a coupler wherein Δ clads is 0.005%, 3 dB achromatic couplers having low values of Δ clads have been made having draw ratios as low as about 3.5:1. The draw ratio can be even lower for taps (less than 50% coupling) since less stretching is required. As the value of Δ clads increases, the draw ratio must increase in order to achieve the desired coupling ratio. Although Fig. 4 would seem to suggest that a Δ clads value of 0.025% would be desirable from the standpoint of providing very good achromaticity, such a coupler is difficult to make since the draw ratio required to make it is around 10:1. Also, for reasons discussed below, the coupled power at higher values of Δ clads may be inadequate to achieve the desired coupling ratio. While a coupler preform is being stretched to form a coupler, the diameter of neckdown region N becomes smaller with increasing time. Fig. 6 shows that the coupled power varies during the stretching process. The curves of Fig. 6 do not bear an exact relationship with respect to one another; rather, it is intended that they qualitatively illustrate the relative relationship between the temporal coupled power curves of couplers having different Δ clads values. During the stretching of a standard coupler (Δ clads = 0), the coupled power relatively quickly reaches 50% and eventually reaches almost 100%. During the stretching of devices having greater values of Δ clads , greater time periods are required to achieve 50% coupling, and the maximum possible amount of coupled power decreases. For a given set of stretching conditions including rate of stretch, temperature of the coupler preform, and the like, there will be a value of Δ clads for which the coupled power just reaches 50% on the first peak of the coupled power curve. For a given set of draw conditions, this value of Δ clads is shown in Fig. 6 to be 0.015%. For higher values of Δ clads , such as 0.025%, the first power transfer peak of the coupled power curve cannot provide 50% coupling. However, it can be seen that a device for coupling less than half the input power, for example a 10% tap, might easily be made by stretching a coupler preform having a Δ clads value of 0.025% until the coupled power is 10%, a value that can be attained on the first peak. The curves of Fig. 6 are not continued in time any further than the extent necessary to illustrate the specific point being discussed. The first power transfer peak is shown for couplers wherein Δ clads is 0.015 and 0.025. Subsequent power transfer peaks are not shown. However, if the coupler preforms were stretched for longer periods of time, the coupled power would continue to oscillate between zero and some maximum value, the period of each subsequent oscillation being narrower than the previous one. If the curves representing couplers having Δ clads values of 0 and 0.005 were continued in time, they would experience similar oscillations in coupled power. The relationship between coupled power and coupling length (which is a function of stretching time) over a plurality of coupled power peaks is graphically illustrated in the aforementioned U.S. patent No. 4,798,436. It is assumed that curve t (Δ clads = 0.025%) is for a stretching operation wherein the coupler preform is heated once and stretched at a single rate. If all other conditions remain the same, the power transfer curve can be displaced upwardly to curve t′ (toward greater power transfer) by stretching the coupler preform at more than one stretch rate as illustrated in Fig. 7. By way of example only, Fig. 7 illustrates a stretch technique involving stretching at two discrete rates (curves s₁ and s₂) and a technique wherein the stretch rate varies continually with respect to time (curve s′). In accordance with a specific embodiment depicted in Fig. 7, the coupler preform is heated and stretched 0.2 cm at a stretch rate of 0.95 cm/sec, the stretch rate abruptly decreasing to 0.45 cm/sec while the coupler preform is stretched an additional 0.55 cm. For certain stretching conditions, including a Δ clads value of about 0.025% or higher, a subsequent power transfer peak such as the third peak might be required to reach the desired coupling value, eg. 50%. Since the third peak is much narrower than the first, the stretching operation must be stopped at precisely the right time in order to achieve the desired coupling ratio. If stretching is continued for only a short additional length of time, the neckdown ratio may change sufficiently to cause the coupled power to drastically decrease. It is difficult to draw such a coupler when output power is being monitored to stop the draw, and it is almost impossible to make such a coupler by drawing to a predetermined length. Furthermore, the achromaticity becomes degraded when the coupler has to be stretched beyond the first power transfer peak. For the aforementioned reasons, the maximum preferred value of Δ clads for 3 dB couplers is about 0.025% and the maximum value of Δ clads for a power tap is about 0.03%. In view of the value of Δ cores that was required for the achromatic fused fiber coupler taught in the aforementioned Sweeney et al. patent, the above-defined range of Δ clads that is suitable for achromatic overclad couplers is unexpectedly low. It appears that the presence of the overclad tube enables the achievement of achromaticity with relatively small values of Δ clads and that a value of Δ clads larger than 0.03% would be required if no overclad tube were employed, i.e. for a fused fiber coupler. The low range of values of Δ clads that was determined by the aforementioned model has been verified by experimental results. When couplers were formed having values of Δ clads below about 0.005%, Δβ was so insignificant that coupling behavior approached that of a standard coupler. Couplers having a Δ clads value in the range of about 0.015% exhibited an insertion loss of less than 4 dB in each leg thereof over a 300 nm range of wavelengths up to 1565 nm. A number of advantages result from the unexpectedly low values of Δ clads . Couplers having low Δ clads values can be connected with low loss into the system. One of the fibers can be a standard single-mode fiber. To provide a Δ clads value of 0.015%, for example, the cladding index of the other fiber (or non-standard fiber) need differ from that of the standard fiber by only 0.00022. Such non-standard fiber exhibits substantially the same mode field diameter as the standard fiber. Since the diameters of both fibers are substantially identical, the non-standard fiber, as well as the standard fiber, can be connected to the system fibers with low loss. The required value of Δ clads can be obtained by adding a dopant to the cladding of only one of the fibers or by adding different amounts of the same or different dopants to the claddings of the two fibers. For example, the cladding of one fiber could consist of silica and that of the other could consist of silica doped with fluorine or B₂O₃ to lower the refractive index or silica doped with chlorine, GeO₂ or the like to increase the refractive index. The process of making the non-standard fiber is facilitated by the low value of Δ clads that is required to form an achromatic coupler. When added to silica, commonly employed dopants such as B₂O₃, fluorine, GeO₂ and the like have a relatively large effect on refractive index. It is therefore difficult to deliver such dopants in the small, precisely controlled amounts that are necessary to change the refractive index of the base glass to an extent sufficient to provide a Δ clads value between 0.005% and 0.03%. It has been found that chlorine has a sufficient effect on the refractive index of silica that it can be used as a dopant in the cladding of the non-standard fiber. Since the change in refractive index per weight percent dopant in silica is much less for chlorine than for conventional dopants such as B₂O₃, fluorine, GeO₂ and the like, chlorine can be used to provide precisely controlled refractive index values that are only slightly higher than that of the silica to which the chlorine is added. Furthermore, the use of chlorine simplifies the process of making the non-standard fiber since it is conventionally employed for drying purposes. Sufficient amounts of chlorine can simply be added to the cladding region of the non-standard fiber in conjunction with the drying/consolidation process. The standard fiber can be made by a conventional process, such as that disclosed in U.S. patent No. 4,486,212, which is incorporated herein by reference. Briefly, that process consists of forming on a cylindrical mandrel a porous preform comprising a core region and a thin layer of cladding glass. The mandrel is removed, and the resultant tubular preform is gradually inserted into a consolidation furnace muffle, the maximum temperature of which is between 1200° and 1700°C and preferably about 1490°C for high silica content glass. The temperature profile of the muffle is highest in the central region as taught in U.S. patent No. 4,165,223, which is incorporated herein by reference. Chlorine, which is present in the minimum concentration that is required to achieve drying, may be supplied to the preform by flowing into the preform aperture a drying gas consisting of helium and about 5 volume percent chlorine. The end of the aperture is plugged to cause the gas to flow through the preform pores. A helium flushing gas is simultaneously flowed through the muffle. The resultant tubular glass article is stretched in a standard draw furnace while a vacuum is applied to the aperture to form a "core rod" in which the aperture has been closed. A suitable length of the rod is supported in a lathe where particles of silica are deposited thereon. The resultant final preform is gradually inserted into the consolidation furnace where it is consolidated while a mixture of 99.5 volume percent helium and 0.5 volume percent chlorine is flowed upwardly therethrough. The resultant glass preform is drawn to form a step-index, single-mode optical fiber, the entire cladding of which comprises silica doped with a residual amount of chlorine. When the cladding is consolidated in a standard downfeed consolidation furnace, as described above, about 0.04 - 0.06 wt. % chlorine is normally present in the fiber cladding. The non-standard fiber can be made by a process which is initially identical to the process by which the standard fiber is made. For example, the core rod, which consists of a solid glass rod of core glass, that is optionally surrounded by a thin layer of silica cladding glass, is initially formed. A porous layer of silica particles is deposited on the rod, and the porous layer is consolidated in an atmosphere containing an amount of chlorine greater than that which would be necessary for drying purposes. The chlorine concentration in the consolidation furnace is controlled to provide the desired value of Δ clads . The amount of chlorine that is incorporated into the base glass depends upon various process conditions such as the maximum temperature and temperature profile of the consolidation furnace, the concentrations of chlorine and oxygen therein and the rate of insertion of the preform into the furnace. The porosity and composition of the preform would also affect the final chlorine concentration. A graph such as that shown in Fig. 8 can be generated for a given standard fiber. For the specific relationship shown in Fig. 8, the standard fiber cladding contained about 0.05 wt. % chlorine. Therefore, about 0.2 wt. % chlorine should be incorporated into the cladding of the non-standard fiber to achieve a Δ clads value of 0.015 %. This chlorine concentration is determined by reading from the graph of Fig. 8 the incremental increase in chlorine content for the desired value of Δ clads and adding 0.05 wt. %. If desired, both fibers could be of the non-standard type, i.e. both could contain more chlorine than standard, commercially available fibers. For example, a Δ clads value of 0.015% could also be obtained by utilizing fibers, the claddings of which contain 0.10 wt. % and 0.23 wt. % chlorine. If the non-standard fiber is made by initially forming a core rod comprising core glass surrounded by a thin layer of cladding glass (containing a small amount of residual chlorine) and the outer cladding glass is doped with a larger amount of chlorine, the refractive index profile of the resultant fiber would appear as illustrated in Fig. 9. The radii of the various layers of a standard fiber might be 4 µm core radius r₁, 10.5 µm inner cladding radius r₂ and 62.6 µm outer radius r₃. Because of the small area of the inner cladding layer, the refractive index of that layer need not be taken into consideration when specifying the cladding refractive index. That is, the effective refractive index of the entire cladding beyond radius r₁ is essentially the same as that of the layer between r₂ and r₃. It is noted that attempts have been made by certain fiber manufacturers to reduce the amount of chlorine in optical fibers in order to lower the attenuation (see Japanese Kokai No. 63/285137). If one fiber had a pure silica cladding (by removing the chlorine therefrom) about 0.13 wt. % chlorine would be needed in the other fiber to achieve a Δ clads value of 0.015 %. However, it has been found that the presence of chlorine in the short lengths of coupler fibers has little or no effect on coupler loss. The additional step of removing chlorine from coupler fibers would therefore be an unnecessary expense. Whereas 2x2 couplers are illustrated in Fig. 1, this invention also applies to other configurations. An NxN coupler (N > 1) can be formed for the purpose of coupling one fiber to N fibers. A 1x2 coupler is described in the specific embodiment. More than 2 fibers can be joined at their waists to form an NxN coupler. Sometimes, one or more fibers are severed from one end of an NxN coupler so that a plurality of fibers, unequal in number, extend from opposite ends of the coupler. The embodiments of Figs. 10-12 are schematic illustrations of coupled fibers, the overclad tubing glass having been omitted for simplicity. The presence of an overclad glass is indicated by the symbol n₃ adjacent the fibers. In the 1x3 coupler of Fig. 10, standard fiber S is coupled to two non-standard fibers S⁺ and S⁻. The refractive index of the cladding of fiber S⁺ is negative with respect to the cladding of fiber S, whereby the value of Δ clads of fiber S⁺ with respect to fiber S is positive. The refractive index of the cladding of fiber S⁻ is such that the value of Δ clads of fiber S⁻ with respect to fiber S is negative. In the 1x4 embodiment of Figs. 11 and 12, the refractive index of the cladding glass of fibers S⁺ is such that the value of Δ clads of fibers S⁺ with respect to fiber S is positive. Fig. 12 shows that fibers S⁺ are preferable equally spaced around fiber S. Whereas the preferred manufacturing technique results in a coupler having optical fiber pigtails extending therefrom, the invention also applies to overclad couplers of the type wherein the fibers extend through the elongated matrix glass body but end flush with the body endface. Methods of making such a coupler are disclosed in U.S. patents Nos. 4,773,924 and 4,799,949. Briefly, the method comprises inserting a plurality of optical fiber preform rods into a glass tube, heating and stretching the resultant preform to form a glass rod which is then severed into a plurality of units. Heat is applied to the central region of each unit, and the central region is stretched to form a tapered region as described herein. A method of making 1x2 achromatic 3 dB fiber optic couplers is illustrated in Figs. 13-18. A glass capillary tube 10 having a 3.8 cm length, 2.8 mm outside diameter, and 270 µm longitudinal aperture diameter was secured by chucks 32 and 33 of the apparatus of Fig. 16. Tube 10, which was formed by a flame hydrolysis process, consisted of silica doped with about 6 wt. % B₂O₃ and about 1 wt. % fluorine. Tapered apertures 12 and 13 were formed by flowing the gas phase etchant NF₃ through the tube while uniformly heating the end of the tube. Coated fibers 17 and 18 comprised 125 µm diameter single-mode optical fibers 19 and 20 having a 250 µm diameter urethane acrylate coatings 21 and 22, respectively. Both fibers had a 8 µm diameter core of silica doped with 8.5 wt. % GeO₂. The cutoff wavelengths of the fibers are below the operating wavelength of the coupler. If, for example, the minimum operating wavelength is 1260 nm, the cutoff wavelengths of the fibers are selected to be between 1200 nm and 1250 nm. All chlorine concentrations were measured by microprobe techniques. The initial steps of the processes of making both fibers was the same; these steps are set forth above in conjunction with a discussion of U.S. Patent No. 4,486,212. A first layer of glass particles comprising SiO₂ doped with 8.5 wt. % GeO₂ was deposited on a mandrel, and a thin layer of SiO₂ particles was deposited on the first layer. The mandrel was removed, and the resultant porous preform was gradually inserted into a furnace having an alumina muffle where it was dried and consolidated. During this process, an gas mixture containing 65 sccm (standard cubic centimeter per minute) chlorine and 650 sccm helium flowed into the center hole where the mandrel had been removed. A flushing gas containing 40 slpm (liter per minute) helium and 0.5 slpm oxygen flowed upwardly from the bottom of the muffle. The aperture was evacuated, and the lower end of the tubular body was heated to 1900°C and drawn at a rate of about 15 cm/min to form a 5 mm solid glass rod. The rod was severed to form sections, each of which was supported in a lathe where it functioned as a mandrel upon which SiO₂ cladding soot was deposited to form a final porous preform. a. Forming a Standard Fiber One final porous preform was gradually inserted into the alumina muffle of a consolidation furnace having a maximum temperature of 1490°C. A gas mixture containing 40 slpm helium, 0.5 slpm chlorine and 0.5 slpm oxygen flowed through the muffle. The porous preform was consolidated to form a draw blank, the outer cladding of which had the same composition as the inner cladding layer, i.e. SiO₂ doped with about 0.05 wt. % chlorine. The tip of the draw blank was heated to about 2100°C, and a standard optical fiber was drawn therefrom, the fiber being coated during drawing. The fiber had an 8 µm diameter core and a 125 µm diameter homogeneous cladding layer of silica containing about 0.05 wt. % chlorine as a residual from the drying process. b. Forming a Non-Standard Fiber Another final porous preform was gradually inserted into a consolidation furnace having a sileca muffle. The maximum temperature of 1450°C. The porous preform was subjected to an upwardly flowing gas mixture containing about 2 slpm helium and 0.6 slpm chlorine. The porous preform was consolidated to form a draw blank, the outer cladding of which consisted of SiO₂ doped with about 0.2 wt. % chlorine. The resultant non-standard fiber was similar to the standard fiber except that it had a 10.5 µm diameter inner cladding region containing about 0.05 wt. % chlorine and an outer, 125 µm diameter cladding region containing about 0.2 wt. % chlorine. The refractive indices of the claddings of this fiber and the standard fiber were such that the value of Δ clads was 0.015. The standard and non-standard fibers were interchangable in the following process. A 6 cm long section of coating was removed from the end of a 1.5 meter length of coated fiber 18. A flame was directed at the center of the stripped region of fiber, and the end of the fiber was pulled and severed to form a tapered end (Fig. 14). The fiber end remote from the tapered end was connected to a reflectance monitoring apparatus. The tapered end was moved slowly along its longitudinal axis to the right (as shown in Figs. 14 and 15 wherein only the bright, central portion 23 of the flame is illustrated). As the tip of fiber 20 was heated by flame 23 of burner 24′, the glass receded and formed rounded endface 25 (Fig. 15), the diameter of which was preferably equal to or slightly smaller than the original uncoated fiber diameter. A current specification for the reflected power is -50 dB. The resultant length of uncoated fiber was about 2.9 cm. Tube 10 was inserted through ring burner 34 (Fig. 16) and was clamped to draw chucks 32 and 33. The chucks were mounted on motor controlled stages 45 and 46 which were controlled by a computer. Approximately 3.2 cm of coating was stripped from the central region of a 3 meter length of fiber 17. The uncoated sections of fibers 17 and 18 were wiped, and a small amount of ethyl alcohol was squirted into the tube to temporarily lubricate the fibers during the insertion process. Coated fiber 17 was inserted through aperture 11 until its uncoated portion was situated below tube end 15. The uncoated portion of coated fiber 18 was held adjacent the uncoated portion of coated fiber 17, and both were moved together toward tube end 14 until the coating end regions become wedged in tapered aperture 13. The uncoated portion of coated fiber 17 was then disposed intermediate end surfaces 14 and 15, the uncoated portion of coated fiber 17 preferably being centered within aperture 11. End 25 of fiber 18 was located between midregion 27 and end 14 of tube 10. The fibers were threaded through the vacuum attachments 41 and 41′, which were then attached to the ends of preform 31. Referring to Fig. 13, vacuum attachment 41 was slid over the end of tube 10, and collar 39 was tightened, thereby compressing O-ring 38 against the tube. Vacuum line 42 was connected to tube 40. One end of a length of thin rubber tubing 43 was attached to that end of vacuum attachment 41 opposite preform 31; the remaining end of the tubing extending between clamp jaws 44. Upper vacuum attachment 41′ was similarly associated with line 42′, tubing 43′ and clamp jaws 44′. The coated portions of the fibers extended from tubing 43 and 43′. Vacuum was applied to the lower portion of coupler preform 31 by clamping jaws 44 on tubing 43 while the upper vacuum attachment was connected to a source of nitrogen to purge the aperture contents. Jaws 44′ were then clamped against tubing 43′ to apply vacuum to the upper portion of preform 31. The upper end of fiber 17 was connected to a monochromater coupled to a white light source. The monochromater was adjusted so that the fiber was provided with a beam 1310 nm light. The lower end of fiber 17 was connected to a detector which formed a part of the system that controls the movement of chucks 32 and 33. With a vacuum of 10 inches (25.4 cm) of mercury connected to the tube aperture, ring burner 34 was ignited. The apparatus located above ring burner 34 was protected by heat shield 35. Flames of about 1800°C were generated by supplying gas and oxygen to the burner at rates of 0.8 slpm and 0.85 slpm, respectively. The flame from ring burner 34 heated tube 10 for about 25 seconds. The matrix glass collapsed onto fibers 19 and 20 as shown in Fig. 17. Midregion 27, the central portion of which forms the coupling region of the resultant coupler, became a solid region wherein substantially the entire lengths of fibers 19 and 20 were in mutual contact. After the tube cooled, the flow rates of both the gas and oxygen were increased to 0.9 slpm, and the burner was reignited. Flames having a temperature of about 1900°C heated the center of the collapsed region to the softening point of the materials thereof. After 12 seconds, the supply of oxygen to burner 34 was turned off. Stages 45 and 46 were pulled in opposite directions at a combined rate of 2.5 cm/sec until the central portion of midregion 27 was stretched 1.46 cm. The flame became extinguished after the stretching operation. This increase in length was just short of the length to which coupler preform 31 would have had to be stretched in order to have achieved achromaticity in a single stretching operation. A sufficient amount of power began to couple to fiber 18 to enable the end of that fiber to be connected to a detector, and the power output to the detector was peaked. Flow rates of gas and oxygen to burner 34 were then adjusted to 0.65 slpm and 0.6 slpm, respectively, to produce a broader flame having a temperature of about 1650°C. Twelve seconds after the flame was ignited, the oxygen flow was turned off, and stages 45 and 46 pulled in opposite directions at a combined rate of 0.5 cm/sec to further increase the length of coupler preform 31 by about 0.02 cm. During this step, the light emanating from fibers 17 and 18 was monitored at 1310 nm. The stretching operation automatically stopped when the ratio of the optical power from fiber 17 to that of fiber 18 was 1.2, at which time the control system instructs the stages to stop moving. Because of system momentum, a sufficient amount of stretching continues to occur to provide a power ratio of 1, whereby equal light power emanated from fibers 17 and 18 at 1310 nm. The diameter of the midregion is reduced by the stretching operations as illustrated by region 51 of Fig. 18. After the coupler had cooled, the vacuum lines were removed from the resultant coupler, and a drops 48 and 49 of heat curable adhesive were applied from a syringe to ends 14 and 15, respectively, of the capillary tube. After the adhesive was cured by exposure to heat (arrow H), the coupler was removed from the draw. The resultant devices couple approximately 50% of the signal propagating in that end of optical fiber 17 at end 14 to optical fiber 18 at about 1310 nm and 1490 nm; the power slope at 1310 nm is 0.077 % per nm or 0.006 dB per nm. These couplers exhibited a median excess device loss of about 0.3 dB. The lowest measured excess loss was 0.05 dB. The spectral insertion loss curves for a specific coupler made in accordance with the specific example are shown in Fig. 19. Curve P₂ represents the coupled power. The excess loss for that coupler was 0.09 dB and 0.05 dB at 1310 nm and 1550 nm, respectively. The insertion loss was less than 4 dB in each leg of that coupler over a 300 nm range of wavelengths up to about 1565 nm.

Claims: An achromatic fiber optic coupler comprising an elongated body of matrix glass having a refractive index n₃, said body having two opposed ends and a midregion, a plurality of optical fibers extending longitudinally through said body, each of said fibers comprising a core of refractive index n₁ and a cladding of refractive index less than n₁ but greater than n₃, the refractive index n₂ of the cladding of a first of said fibers being different from the refractive index n ′ / 2 of the cladding of a second of said fibers by such an amount that the value of Δ clads is greater than zero but less than 0.03%, wherein Δ clads equals (n₂² - n ′ / 2²)/2n₂², said fibers being fused together along with the midregion of said matrix glass, the diameter of the central portion of said midregion and the diameters of said optical fibers in said central portion being smaller than the diameters thereof at the ends of said body, whereby a portion of an optical power propagating in one of said fibers couples to the other of said fibers. A coupler in accordance with claim 1 wherein the value of Δ clads is greater than 0.005%. A coupler in accordance with claim 1 wherein said coupler is capable of coupling about 50% of the power from one of said fibers to the other of said fibers at a predetermined wavelength, and the value of Δ clads is between 0.005% and 0.02%. A coupler in accordance with claim 1, 2 or 3 wherein Δ₂₋₃ is greater than 0.4%, wherein Δ₂₋₃ is equal to (n₃² - n₂²)/2n₃². A coupler in accordance with any one of the preceding claims wherein Δ₂₋₃ is between 0.4% and 0.65%, wherein Δ₂₋₃ is equal to (n₃² - n₂²)/2n₃². A method of making an achromatic fiber optic coupler comprising the steps of inserting into a glass tube of refractive index n₃ at least a portion of each of a plurality of optical fibers so that said portions occupy the midregion of said tube, each of said fibers comprising a core of refractive index n₁ and a cladding of refractive index less than n₁ but greater than n₃, the refractive index n₂ of the cladding of a first of said fibers being different from the refractive index n ′ / 2 of the cladding of a second of said fibers, the difference between n₂ and n ′ / 2 being such that the value of Δ clads is greater than zero but less than 0.03%, wherein Δ clads equals (n₂² - n ′ / 2² )2n₂², collapsing the midregion of said tube onto fibers, and stretching the central portion of said midregion until a predetermined coupling occurs between said fibers. A method in accordance with claim 6 wherein the step of stretching comprises providing relative movement between the ends of said tube, and varying the rate at which said relative movement occurs. A method in accordance with claim 7 wherein the step of stretching comprises continuously varying the rate at which said relative movement occurs. A method in accordance with claim 7 wherein the step of stretching comprises stretching at one stretch rate for a first period of time and stretching at another stretch rate for a second period of time. A method in accordance with claim 6 wherein the step of stretching comprises pulling the ends of said tube away from each other at a first stretch rate, and before said predetermined coupling is achieved, pulling the ends of said tube away from each other at a second stretch rate that is different from said first stretch rate. A method in accordance with claim 6 wherein the step of stretching comprises heating the central portion of said tube midregion, stretching the central portion of said tube midregion, stopping said stretching operation before said predetermined coupling is achieved, reheating the central portion of said tube midregion and further stretching the central portion of said tube midregion. A method in accordance with and one of claims 6-11 wherein said reheating is to a temperature lower than the first heating, and/or said further stretching is at a rate lower than said first stretch rate. A method in accordance with any one of claims 6-12 wherein the step of stretching comprises stretching the central portion of said tube midregion at a first stretch rate until some coupling between said fibers begins to occur, and before said predetermined coupling is achieved, stretching the central portion of said tube midregion at a second stretch rate different from said first stretch rate. A method in accordance with claim 6 wherein said tube has first and second ends, at least a first of said fibers extends from both ends of said tube, and at least a second of said fibers extends from only the second end of said tube, and wherein the step of stretching comprises stretching the central portion of said tube midregion until some coupling between said fibers begins to occur, and using the ratio of the optical power from said fibers to stop said stretching operation.

Inventors: MILLER WILLIAM JAMES, TRUESDALE CARLTON MAURICE, WEIDMAN DAVID LEE, YOUNG DONALD RAY JR, MILLER, WILLIAM JAMES, TRUESDALE, CARLTON MAURICE, WEIDMAN, DAVID LEE, YOUNG, DONALD RAY, JR.
Applicants: CORNING INC, CORNING INCORPORATED
Application year: 1990
Main classification: G02B6
IPC codes: G02B6