PROCESS FOR PREPARING FINE POWDERS OF ALUMINIUMNITRIDE

Abstract: Disclosed is a process for preparing fine powders or aluminum nitride, by starting from an aqueous solution of an inorganic aluminum salt, characterized in that said process comprises the following steps: (a) the anion of the inorganic salt of aluminum is at least partially removed by heating, with a colloidal solution of an aluminum compound being obtained; (b) carbon powder is dispersed in said colloidal solution, with a suspension of an aluminum compound and carbon being obtained; (c) said suspension is mixed with a carbohydrate, with a suspension being obtained of an aluminum compound and carbon in a solution which contains the carbohydrate; (d) the suspension obtained from the (c) step is sprayed onto, or dropwise added to, an alkaline solution, with spherical bodies being obtained, which contain aluminum hydroxide and carbon; (e) said spherical bodies are carbothermally reduced and nitrided at a temperature comprised within the range of from 1350 to 1650°C for a time comprised within the range of from 1 to 24 hours, so that powders containing aluminum nitride are obtained; (f) carbon is removed from said powders by a calcination carried out at a temperature comprised within the range of from 600 to 700°C, for a time comprised within the range of from 1 to 7 hours, under an oxygen-containing atmosphere.

Description: The present invention relates to a process for preparing fine powders of aluminum nitride. Aluminum nitride (AlN) shows a good chemical stability and a high heat conductivity. These characteristics make it suitable for use as a functional ceramic material (i.e., as a support for electronic circuits) and as a structural ceramic material (i.e., for components exposed to high temperatures and/or aggressive media). The starting material to prepare ceramic components made from AlN is AlN powder, which is suitably fabricated and sintered. The characteristics of the sintered bodies depend on the purity of AlN powder and on the size of its particles. Several routes are available to produce said powder: direct synthesis from Al metal and N₂; nitriding in the gas phase of a volatile compound of Al with N₂ and/or NH₃; carbothermal reduction and nitriding of a mixture of Al₂O₃ and C at temperatures comprised within the range of from 1600 to 1900°C, and under a nitrogen atmosphere. The first method (i.e., the direct synthesis) allows an only incomplete formation of Al nitride to be obtained. The second method (i.e., the nitriding in the gas phase) suffers from the disadvantage that the production cost is high. The disadvantages of both said methods can be at least partially reduced by using the last method. By techniques of preparation of the mixture of Al₂O₃ + C by a chemical route, an improvement is achieved in said method, which makes it possible purer and smaller-particle-size AlN powders to be obtained, even if the process is carried out at some hundred degrees lower operating temperatures. The purpose of such techniques is of having both reactants as particles of sub-micron particle size and intimately dispersed inside each other. An example of a chemical method recently adopted to prepare the mixture of Al₂O₃ and C is based on the hydrolysis and precipitation with ammonia of an aluminum alkoxide (aluminum isopropoxide) in alcoholic suspension in which carbon powder was previously dispersed (see US-4 643 859). The present Applicant has found now a process based on a different chemical method to obtain the mixture of Al₂O₃ and C, which is much simpler than the process according to the above cited United States patent, which also enables very pure AlN powders constituted by particles with a very small particle size to be obtained. The process according to the present invention for preparing fine powders of aluminum nitride, by starting from an aqueous solution of an inorganic aluminum salt, is characterized in that said process comprises the following steps: (a) the anion of the inorganic salt of aluminum is at least partially removed by heating, with a colloidal solution of an aluminum compound being obtained; (b) carbon powder is dispersed in said colloidal solution, with a suspension of an aluminum compound and carbon being obtained; (c) said suspension is mixed with a carbohydrate possibly in solution, with a suspension being obtained of an aluminum compound and carbon in a solution which contains the carbohydrate; (d) the suspension obtained from the (c) step is sprayed onto, or dropwise added to, an alkaline solution (e.g., an ammonium hydroxide solution), with spherical bodies being obtained, which contain aluminum hydroxide and carbon; (e) said spherical bodies are carbothermally reduced and nitrided at a temperature comprised within the range of from 1350 to 1650°C for a time comprised within the range of from 1 to 24 hours, so that powders containing aluminum nitride are obtained; (f) carbon is removed from said powders by a calcination step carried out at a temperature comprised within the range of from 600 to 700°C, for a time comprised within the range of from 1 to 7 hours, under an oxygen-containing atmosphere. The carbohydrate may be, e.g., a polysaccharide, in particular methyl-cellulose. The carbon powder which is dispersed throughout the colloidal solution should preferably consist of particles having a particle size smaller than 40 nm. Furthermore, the atomic ratio of Al/C in the formed suspension should preferably be comprised within the range of from 2:3 to 2:5. As regards the size of the spherical bodies, it depends on the size of the drops: when the suspension is sprayed, e.g., by a revolving cone, spherical bodies of 100 micrometres of size or even smaller are produced; whereas by dropwise addition, about 10-fold larger bodies are obtained. The heating of the aqueous solution of the inorganic aluminum salt can be preferably carried out in a microwave oven. Some examples are now given to better illustrate the invention. In no way should the following examples be construed as being limitative of the same invention. Example 1 A solution of 100 g of Al(NO₃)₃.9H₂O in 100 cm³ of distilled water is de-nitrated in a 1400-W microwave oven at 80% power, during a time of 15 minutes. The resulting residue, which contains about 30% of the initial nitrate, is dispersed in H₂O at 80-90°C, with stirring, until a practically clear solution is obtained. After cooling, carbon powder is dispersed in such an amount as to yield an atomic ratio of Al/C = 0.45 (surface area and size of carbon particles respectively = 100 m²/g and 20-30 nm). The dispersion of carbon is accomplished by mechanical stirring and subsequent sonication for 15 minutes. The suspension is subsequently admixed with a solution at 3.5% of methyl-cellulose (20 cm³); and finally the volume is adjusted at 110 cm³ with H₂O. The colloidal suspension is sprayed by a revolving cone (at about 2500 rpm) in 7 M solution of ammonium hydroxide. After a 2-hour ageing in the ammonium hydroxide solution, the so obtained spherical bodies are washed with H₂O and dried in air at 150°C for 2 hours. The spherical bodies (of about 100 micrometres of diameter) are transferred to an alumina tray, then are charged to a furnace at 1500°C and are kept under these conditions for a 3-hour time, under a flowing nitrogen stream. After removing the excess carbon by oxidation in air at 650°C for 6 hours, the analysis of the powder by X-ray diffraction (RXD) showed that said powder was constituted by one single crystal phase, corresponding to AlN. The chemical analysis showed that the product was 91% AlN. Example 2 A sample of spherical bodies prepared as in Example 1 was treated at 1550°C for 6 hours under a nitrogen flow. After a 6-hour calcination in air at 650°C, the analysis by RXD showed that the powder was constituted by one single crystal phase corresponding to AlN. The chemical analysis showed that the obtained product was 95%. Example 3 100 ml of the suspension disclosed in Example 1 was dropwise added to the ammonium hydroxide solution through a needle of 0.5 mm: the resulting spherical bodies, after ageing in the same ammonium hydroxide solution, water washing and air drying at 150°C for 2 hours, had a diameter of approximately 1 mm. A sample of said spherical bodies was submitted to a 6-hour long treatment at 1550°C under a nitrogen flow. After a 6-hour calcination in air at 650° , the sample was shown to contain 97% of AlN. (Comparative) Example 4 25 g of Al(OH)₃ powder is dispersed in 100 cm³ of H₂O by a 15-minute sonication, until a practically clear solution is obtained. To said solution, 6.7 g of carbon powder is added (atomic Al/C ratio = 2:3.5) first with mechanical stirring and then with sonication. Due to thixotropy, a gel-like mass is obtained after about 2 minutes. After a 2-hour drying at 150°C, the mixture of hydrous Al oxide and C is charged to the furnace and is kept 4 hours at 1500°C under a flowing N₂ atmosphere. Carbon is then removed by a 6-hour calcination in air at 650°C. The resulting powder is constituted by 59% AlN. (Comparative) Example 5 10 g of gamma-Al₂O₃ is dispersed in 50 cm³ of H₂O by ultrasound-stirring until a practically clear solution is obtained. To said solution, 4.12 g of carbon powder is added (atomic Al/C ratio = 2:3.5) first with mechanical stirring and then with sonication. Due to thixotropy, a gel-like mass is obtained after about 1 minute. The drying is carried out by a 2-hour heating at 150°C in air. The mixture of Al₂O₃ and C is charged to the furnace and is submitted to a 4-hour treatment at 1500°C under a stream of flowing N₂. The residual carbon is then removed by a 6-hour calcination in air at 650°C. 73% of the resulting powder is constituted by AlN.

Claims: Process for preparing fine powders of aluminum nitride, by starting from an aqueous solution of an inorganic aluminum salt, is characterized in that said process comprises the following steps: (a) the anion of the inorganic salt of aluminum is at least partially removed by heating, with a colloidal solution of an aluminum compound being obtained; (b) carbon powder is dispersed in said colloidal solution, with a suspension of an aluminum compound and carbon being obtained; (c) said suspension is mixed with a carbohydrate, with a suspension being obtained of an aluminum compound and carbon in a solution which contains the carbohydrate; (d) the suspension obtained from the (c) step is sprayed onto, or dropwise added to, an alkaline solution, with spherical bodies being obtained, which contain aluminum hydroxide and carbon; (e) said spherical bodies are carbothermally reduced and nitrided at a temperature comprised within the range of from 1350 to 1650°C for a time comprised within the range of from 1 to 24 hours, so that powders containing aluminum nitride are obtained; (f) carbon is removed from said powders by a calcination step carried out at a temperature comprised within the range of from 600 to 700°C, for a time comprised within the range of from 1 to 7 hours, under an oxygen-containing atmosphere. Process according to claim 1, in which the carbohydrate to be mixed with the suspension in the (c) step is added in solution. Process according to claim 1, in which the carbohydrate is a polysaccharide. Process according to claim 3, in which the polysaccharide is methyl-cellulose. Process according to claim 1, in which the carbon powder dispersed in the colloidal solution is composed by particles having a particle size smaller than 40 nm. Process according to claim 1, in which the heating in the (a) step is carried out in a microwave oven.

Inventors: BEAULARDI, LEO, CONTURSI, LUIGI
Applicants: TEMAV S.P.A.
Application year: 1990
Main classification: C01B21
IPC codes: C01B21