Oxide superconductor and method of manufacturing the same

Abstract: An oxide superconductor having oxide superconductor layers (2) and metal material layers (1), which are alternately laminated on each other by a desired number of times, and a method of manufacturing the same.

Description: The present invention relates to an oxide superconductor used in a transmission and distribution wired a power cable, an equipment lead wired a magnet wire, and a magnetic shield and a method of manufacturing the same and, more particularly, to an oxide superconductor capable of supplying a large current with zero resistance or small alternating-current loss. An intermetallic compound such as NbTi, Nb₃Sn, Nb₃Aℓ, or V₃G a and a metal such as Nb or Pb are used as superconductive magnets, magnetic shields, coaxial cables, and cavities by utilizing an ultra low-temperature refrigerant such as liquid helium. These metallic materials, however, are limited as resources. In addition, helium is used to increase cost, which limits the range of practical applications. To the contrary, some substances which can be rendered superconductive at low critical temperatures (Tc) by inexpensive refrigerants have been found, and extensive studies on practical use of such substances in a variety of applications have been actively made. As the high Tc materials described above, La 2-x Ba x CuO₄ and La 2-x Sr x CuO₄ oxide superconductors have critical temperatures of 30 to 45K; a Y(Dy,Er,Ho)Ba₂Cu3O 7-δ oxide superconductor has a critical temperature of up to 95K; Bi-Sr-Ca-Cu-O based oxide superconductors such as Bi₂Sr₂CaCu₂O₈ and Bi₂Sr₂Ca₂Cu₃O₁₀ oxide superconductors have critical temperatures of 80 to 110K; and Tℓ-Ba-Ca-Cu-O based oxide superconductors such as Tl₂Ba₂CaCu₂O₈, Tℓ₂Ba₂Ca₂Cu₃O₁₀ and TℓBa₂Ca₂Cu₇O 8.5 oxide superconductors have critical temperatures of 90 to 125K. These oxide superconductors are manufactured as follows. A powder of each superconductor is kneaded with an organic binder to obtain a paste, and the paste is directly extrusion molded or screen-printed. Alternatively, the powder of each superconductor is filled in an Ag pipe or the like, and the pipe is elongated to obtain a conductor having a desired shape. In a superconductor, a metal stabilizing material is combined with a superconductor molded body to cope with a so-called quench phenomenon in which a superconductive state is lost. For the same purpose as in the oxide superconductor, it is proposed to combine a metal stabilizing material with an oxide superconductor. When the superconductive state is lost, the oxide superconductor becomes an insulator, and it is difficult to conduct heat or electric power to the metal stabilizing material. For this reason, a quench phenomenon more easily occurs. In particular, in alternating-current energization, heat may often be generated by a hysteresis loss. It is very important to appropriately provide a countermeasure against the quench phenomenon of the oxide superconductor. An oxide superconductor is generally brittle and its crystal has a laminar structure subjected to cleavage. The oxide superconductors tend to crack in installation works. In addition, when an oxide superconductor is used for a magnet, a Lorentz's force acts on the oxide superconductor to crack an oxide superconductor layer. As a result, a critical current density (Jc) is undesirably degraded. Furthermore, since the oxide superconductor has a laminar perovskite crystal structure, crystal anisotropy is strong, and a current flows in a direction parallel to the a-b plane. In order to obtain a high critical current density (Jc), the crystal must be oriented such that its C-axis is perpendicular to a current energization direction. However, since the crystal of the oxide superconductor thus manufactured tend to be oriented randomly, a sufficiently high critical current density Jc cannot be obtained. DE-A-37 29 125 discloses a composite oxide superconductor comprising alternately laminated oxide superconductor layers and normal conducting layers, followed after a certain layer sequence by a thick layer of a highly-conductive metal such as Cu or Ag to provide the required stability. Jap.J.Appl.Phys., Vol. 27, No. 9, Part 2: Letters, September 1988, p. L1715-L1717; M. Okada et al.: "Neutron Diffraction Study on Preferred Orientation of Ag-Sheathed Y-Ba-Cu-O Superconductor Tape with J c =1000-3000 A/cm²" reveals oxide superconductor layers (YBCO cores) and metal material layers (Ag-sheathed) which are alternately laminated on each other in a plate-like form by a plurality of times. The present invention has been made as a result of extensive studies in consideration of the above situation, and has as its object to provide an oxide superconductor having excellent electromagnetic stability such as a high Jc and high mechanical strength and a method of manufacturing the same. According to the present invention, there is provided a composite oxide superconductor comprising oxide superconductor layers and metal material layers, which are alternately laminated by a plurality of times, and a high-strength, heat-resistant metal material selected from the group consisting of Fe, Ni-Cr (SUS), Ni, W and these metals coated with a noble metal, and being in contact with at least one of said superconductor layers and/or at least one of said metal material layers for providing a composite structure. The oxide superconductor having the above structure according to the present invention has a multilayered structure in which the oxide superconductor layers and the metal material layers are alternately laminated. Therefore, both electromagnetic stability and mechanical strength which are indispensable factors of the superconductor can be obtained. This invention can be more fully understood from the following detailed description when taken in conjunction with the accompanying drawings, in which: Fig. 1 is a sectional view showing a superconductor in which a high-strength, heat-resistant metal material is combined with an oxide superconductor according to the present invention; Fig. 2 is a view for explaining a crystal structure of an oxide superconductor layer of an oxide superconductor according to the present invention; Figs. 3A to 3C are sectional views showing metal sheets used in the present invention; Figs. 3D to 3F are plan views showing the metal sheets shown in Figs. 7A to 7C, respectively; Fig. 4 is a sectional view showing a state wherein an oxide superconductor layer is laminated on a metal sheet; Fig. 5 is a plan view showing still another metal sheet used in the present invention; Figs. 6A and 6B are a sectional view and a plan view, respectively, showing still another metal sheet used in the present invention; Figs. 7 and 8 are sectional views showing other examples of oxide superconductor cables according to the present invention; Figs. 9A and 9B are a view for explaining the enlarged main part of an oxide superconductor cable according to the present invention, and a view for explaining the directions of a-, b- and c-axis of the oxide superconductor cable, respectively. Fig. 10 is a sectional view showing various types of stabilizing metal materials used in the method of manufacturing oxide superconductor cables according to the present invention; and Fig. 11 is a sectional view showing a conventional oxide superconductor cable. In a superconductor shown in Fig. 1, an Ag layer 1, a ceramic superconductor layer 2, and a high-strength, heat-resistant metal material 9 are combined in a concentric manner. The superconductor shown in Fig. 1 is manufactured as follows. A ceramic superconductor material, and an Ag material or a high-strength, heat-resistant metal material are worked into rods or pipes, respectively. These rods or pipes are engaged with each other to obtain a composite billet. The composite billet is worked into a wire rod having a desired shape by the same elongation as described above. The resultant wire rod is heated at a temperature of, in most cases, 800 to 1,000°C to cause a reaction and sintering of the ceramic superconductor material into a ceramic superconductor, supply of oxygen to the sintered body, or adjustment of the crystal structure, thereby manufacturing a ceramic superconductor. A material which has high strength and cannot be melted or softened during heating in the subsequent process is used as the high-strength, heat-resistant metal material embedded in the Ag layer. Examples of such a material are metals such as Fe, SUS, Ni, and W. The high-strength, heat-resistant metal material is preferably coated with a noble metal such as Au, Pt, Rd, or Pd by plating or vapor deposition, thereby preventing oxidation of the metal material. As the ceramic superconductor materials used in the method of the present invention, intermediate materials between source materials which can be converted into ceramic superconductors and the ceramic superconductors can be used as precursors in addition to the various ceramic superconductors described above. The intermediate material is, e.g., a mixture, a coprecipitation mixture, or an oxygen deficient type composite oxides of ceramic superconductor constituting elements, or an alloy of the above constituting elements. These precursors are heated in an atmosphere containing oxygen and are reacted into ceramic superconductors. Since the metal material is distributed in the form of a layer in the oxide superconductor layer in the oxide superconductor of the present invention, it is excellent in electrical conductivity and thermal conduction. Therefore, quenching and the hysteresis loss by AC energization can be suppressed. The crystal structure of the oxide superconductor layers partitioned by the metal material layers is constituted by crystal particles grown lanky in the longitudinal direction of the superconductor. Accordingly the number of particle boundaries accounting for energization resistance is small in the energization direction, and at least one particle boundary is contained in a direction perpendicular to the lanky crystal particles. Therefore, a uniform, high Jc can be obtained. In the method of manufacturing the above oxide superconductor according to the present invention, the laminated body of the oxide superconductor and the metal is heated at a temperature to partially melt the oxide superconductor or more, and is then cooled to recrystallize the oxide superconductor such that crystallization of the molten oxide superconductor progresses to portions between the metal layers. Therefore, the crystal particles are grown lanky in the longitudinal direction and are oriented in the C-axis. A crystal structure of an oxide superconductor layer of an oxide superconductor of the present invention will be described with reference to Fig. 2. Fig. 2 is a view showing part of a crystal structure of an oxide superconductor. An oxide superconductor layer 2 is formed on a metal material layer 1, and the oxide superconductor layer 2 is made of a plurality of lanky crystal particles 6 parallel to the axis of the superconductor. The particle boundary of the crystal particles has a pinning effect for restricting movement of a magnetic field. In a ferromagnetic magnet or AC energization, a high Jc can be stably obtained. The cross sections of metal sheets used in the method of the present invention are shown in Figs. 3A, 3B, and 3C, respectively, and the planar patterns thereof are shown in Figs. 3D, 3E, and 3F, respectively. Projections 7 and/or holes 8 are formed in the metal sheets to increase a contact area with the oxide semiconductor, thereby effectively performing heat dissipation. As shown in Fig. 4, projections 7 of the metal sheet 1 are constituted by a plurality of linear projections 7, and an oxide superconductor 2 is applied between each two projections 7. The resultant metal sheet 1 with the oxide superconductor 2 is wound in a spiral shape to obtain a rod, or the metal sheets with the oxide superconductor are laminated to obtain a sheet-like body. The resultant structure is elongated in a direction of the linear projection 7. Then, the oxide superconductor layers are separated from the projections 7, or the metal distribution density is increased to effectively suppress quenching and hysteresis loss. Each linear projection formed on the metal sheet need not be continuous. As shown in the plan view of Fig. 5, projections 7 may be distributed as islands. When linear projections 7 are also formed along the sides of the metal sheet, as shown in the sectional and plan views of Figs. 6A and 6B, the oxide superconductor layers can be shielded from the outer atmosphere by using only the metal sheet without using a metal vessel. Various types of oxide superconductors are used in the oxide superconductors of the present invention. Metal materials for the metal material layers are nonreactive with oxide superconductors and are excellent in electrical conductivity and thermal conduction. Examples of the metal material are Ag, Ag-Pd, Ag-Au, Ag-Cu, Ag-Mg, Ag-Pt, Ag-Ir, Au, Au-Ni, Au-Cu, Au-Ag-Cu, Au-Pd-Ag, Au-Ir, Pt, Pt-Ir, Pt-Pd, Pd, Pd-Ni, Pd-Co, Ni-Cr, Ni-Cr-Co, Ni-Fe, Ni-Fe-Co, Fe-Cr, Fe, and Ni-Cr (SUS). The lanky crystal particle shape in the oxide superconductor layer according to the present invention is given such that a ratio (aspect ratio) of the length in the longitudinal direction of the superconductor to the length (width) in a direction perpendicular to the longitudinal direction is 10 or more and generally falls within the range of 50 to 1,000 because the C-axis orientation can be improved and a high Jc value can be obtained. When the metal particles are dispersed at least in an oxide superconductor layer portion adjacent to the metal material layer, and the thickness of each oxide superconductor layer is reduced to 1 mm or less and preferably 0.1 mm or less, the resultant oxide superconductor can be excellent in electrical conductivity and thermal conduction as a whole. According to a method of manufacturing an oxide superconductor of the'present invention, layers of an oxide superconductor or its precursor are alternately laminated with metal material layers by a desired number of times, and the laminated body is covered with the metal material. The laminated body with the coating is elongated as it is or into a desired shape. Predetermined heating and cooling are performed such that the laminated body is heated at a temperature to partially melt the oxide superconductor or its precursor or more and then cooled to recrystallize the oxide superconductor or its precursor. As the oxide superconductors used in the method of the present invention, intermediate materials between source materials which can be converted into oxide superconductors and the oxide superconductors can be used as precursors in addition to the various oxide superconductors described above. The intermediate material is, e.g., a mixture, a coprecipitation mixture, or an oxygen deficient type composite oxides of oxide superconductor constituting elements, or an alloy of the above constituting elements. These precursors are heated in an atmosphere containing oxygen and are reacted into oxide superconductors. In this method of the present invention, in order to alternately laminate an oxide superconductor or its precursor with the metal material by a desired number of times, it is easy to form sheets of the superconductor or its precursor, and the metal material sheets, and to alternately laminate these sheets to obtain a laminated structure. A method of forming the oxide superconductor or its precursor into a sheet can be a conventional method such as a doctor blade method, extrusion, or screen process printing. It is preferable to add a binder to the oxide superconductor or its precursor upon sheet formation because flexibility is imparted to the resultant sheet. According to the method of the present invention, the laminated body of sheets of the oxide superconductor or its precursor and the metal material sheets is heated to sinter the molded body, replenish oxygen to the sintered body, and adjust the crystal structure for the oxide superconductor, and to react the precursor into an oxide superconductor, to sinter the molded body, replenish oxygen to the sintered body, and adjust the crystal structures for the precursor. The oxide superconductor or its precursor is heated at a temperature to partially melt it or more because the lanky crystals are grown in the longitudinal direction during cooling and are oriented in the C-axis having a high conductivity. The laminated body is slowly moved in a furnace having a temperature gradient to facilitate lankiness of the crystals and C-axis orientation. According to the method of the present invention, the laminated body of the oxide superconductor sheets and the metal sheets is elongated by filling the laminated body into a metal vessel or covering the laminated body with a metal sheet because the oxide superconductor layers become more dense and are separated from the outer atmosphere to obtain a perfect moisture-proof structure, and are free from entrance of toxic substances. Any elongation method such as rolling, extrusion, groove rolling, swaging, or drawing can be applied. According to the method of the present invention, a so-called Wind & React method can also be utilized wherein an elongated material of the laminated body is, for example, wound into a magnet coil and this coil is heated to obtain an oxide superconductor having good orientation. This method is very effective to form the oxide superconductor having poor workability into a magnet or the like. In a ceramic superconductor in which an Ag layer or an Ag alloy layer is combined with a ceramic superconductor layer, a high-strength, heat-resistant metal material can be embedded in the combined Ag or Ag alloy layer continuously in the longitudinal direction of the superconductor directly or through a noble metal layer. The Ag or Ag alloy is used as the metal material layer of the ceramic superconductor constituted by the ceramic superconductor layer and the metal material layer according to the present invention, and the high-strength, heat-resistant metal material can be continuously embedded in the Ag or Ag alloy layer in the longitudinal direction of the superconductor. Therefore, elongation deformation of the superconductor by a tension or the like can be prevented. The high-strength, heat-resistant metal material may be directly embedded in the Ag or Ag alloy layer. However, a noble metal layer is preferably coated on the high-strength, heat-resistant metal material, and the metal material with the noble metal layer is embedded into the Ag or Ag alloy layer to prevent oxidation of the metal material. As described above, the Ag or Ag alloy layer is used as the metal material layer combined with the ceramic superconductor due to the following reasons. Since Ag or an Ag alloy is excellent in oxygen permeability, a sufficient amount of oxygen is supplied to the ceramic superconductor during heating, thereby obtaining a high Jc. In addition, since Ag or an Ag alloy has a high heat conductivity, a quenching phenomenon, i.e., a thermal transition from superconductivity to normal conductivity, can be suppressed, and the energization amount can be increased. Any metal material combined with the ceramic superconductor can be used according to the present invention if it is excellent in oxygen permeability and thermal conduction. For example, an Ag alloy such as Ag-Ir, Ag-Pd, or Ag-Au can be used. The present invention will be described in detail by way of its examples. Example 1 Five % of an Ag powder (average particle size: 1 µm) and 3% of Ho₂BaCuO₅ powder (average particle size: 0.5/µm) were mixed with an HoBa₂Cu₃O 7-δ pre-burnt powder (average particle size: 5 µm), and 10% of methyl cellulose and 10% of butyl cellosolve as binders were mixed therewith. The resultant mixture was kneaded by a roll, and a green sheet having a thickness of 0.5 mm was formed by a doctor blade method. A metal sheet was prepared by plating Ag to a thickness of 15 µm on a 0.1-mm thick Ni sheet having 8-mm diameter holes formed at intervals of 10 mm. Twenty green sheets and 21 metal sheets prepared in this manner were alternately laminated, and the resultant laminated body was dried at 150°C and pre-burnt at 500°C. The pre-burnt body was filled in an Ag vessel having inner dimensions of 100 × 100 × 10 mm and a wall thickness of 2 mm and was sealed in a vacuum. The sealed vessel was subjected to HIP in an Ar atmosphere at 600°C and 1,000 atm. The HIP-treated vessel was rolled to have a thickness of 0.8 mm. The rolled material was heated in an O₂ flow at 900°C for six hours and was cooled to room temperature at a rate of 3°C/min to manufacture a sheet-like oxide superconductor. Comparative Example 1 Oxide superconductors were manufactured following the same procedures as in Example 1 except that the Ag vessels filled with the laminated bodies were heated without rolling after the HIP treatment. Comparative Example 2 Oxide superconductors were manufactured following the same procedures as in Example 1 except that the Ag vessels filled with the spiral rods were heated without working after the HIP treatment. Results are summarized in Table 1 together with the manufacturing conditions. As is apparent from Table 1, the samples of the examples (sample No. 1) of the method of the present invention have larger Jc values and higher shield effects as compared with the samples of the method of the comparative examples (sample Nos. 1 and 2). This difference is caused depending upon whether the elongation step of the laminated body is performed, as is apparent upon comparison of sample Nos. 1 of the present invention with sample Nos. 6 and 7 of the comparative examples. The oxide superconductor layer of the method of the present invention had higher crystal orientation and became dense since elongation was performed. The Ag powder was mixed in the oxide superconductor powder in Example 1 in order to increase adhesion strength between the oxide superconductor layer and the metal layer, to increase heat conductivity, and to promote supply of oxygen during heating, thereby increasing Jc values and the like. Still another embodiment of oxide superconductor wires according to the present invention will be described with reference to the accompanying drawings. An oxide superconductor wire 10 shown in Fig. 7 comprises a plurality of stabilizing metal layers 11, 12, 13, and 14 having ring-like sectional shapes of different diameters, and a plurality of oxide superconductor layers 15, 16, and 17 having ring-like sectional shapes of different diameters. The stabilizing metal layers 11 to 14 and the oxide superconductor layers 15 to 17 were alternately laminated in an order of the stabilizing metal layer 11, the oxide superconductor layer 15, the stabilizing metal layer 12, the oxide superconductor layer 16, the stabilizing metal layer 13, the oxide superconductor layer 17, and the stabilizing metal layer 14 from the center to the outer surface of the oxide superconductor wire 10. An oxide superconductor wire 20 shown in Fig. 8 has the same basic structure as the oxide superconductor wire 10 in Fig. 7. The oxide superconductor wire 20 comprises a plurality of stabilizing metal layers 21, 22, 23, and 24 and a plurality of oxide superconductor layers 25, 26, and 27, which are alternately laminated in the radial direction. The stabilizing metal layer 21 at the core comprises a rod, and other stabilizing metal layers 22 to 24 and the oxide superconductor layers 25 to 27 are ring-like sectional shapes. In the wire described above, the stabilizing metal layers 11 to 14 and 21 to 24 are made of, e.g., silver or a nickel-based alloy. The oxide superconductor layers 15 to 17, and 25 to 27 are made of a known composition such as Lu-Ba-Cu-O or Bi-Sr-Ca-Cu-O. As shown in Figs. 8A and 8B, when the oxide superconductor layers 15 to 17 and 25 to 27 are constituted by an aggregate of an oxide powder having the longitudinal direction as an a-b plane and the direction of thickness as the c-axis, critical current densities (Jc) of the oxide superconductor layers 15 to 17 and 25 to 27 can be increased. The thickness of each of the oxide superconductor layers 15 to 17 and 25 to 27 is 200 µm or less and is preferably as small as possible. The thickness of each of the stabilizing metal layers 11 to 14 and 21 to 24 is as small as possible so as to minimize the outer diameter of each of the superconductor wires 10 and 20. When the thickness is excessively small, the stabilizing function inherent to this metal layer is impaired. The thickness of each of the stabilizing metal layers 11 to 14 and 21 to 24 is preferably set to be several times that of each of the oxide superconductor layers 15 to 17 and 25 to 27. The number of oxide superconductor layers in each of the oxide superconductor wires 10 and 20 is arbitrarily set to be two or more, and the number of stabilizing metal layers is set accordingly. Only the core portion of the oxide superconductor wire 10 in Fig. 7 is hollow, whereas the core portion of the oxide superconductor wire 20 in Fig. 8 is solid. As shown in Fig. 7, when the core portion of the oxide superconductor wire 10 is hollow, the hollow core portion can serve as a refrigerant flow path to improve cooling capacity, thereby obtaining a more desirable oxide superconductor wire. Fig. 10 shows tubular stabilizing metal materials 30a, 31, 32, 33, and 34 to which an oxide powder is applied, and a rod-like stabilizing metal material 30b. The stabilizing metal materials 30a, 30b, 31, 32, 33, and 34 are made of silver or a nickel-based alloy. When the oxide superconductor wire 10 shown in Fig. 7 is to be manufactured, the stabilizing metal materials 30a, 31, 32, 33, and 34 are used, and an oxide powder is applied to the outer surface of the stabilizing material 30a, one or both of the inner and outer surfaces of the stabilizing metal materials 31, 32, and 33, and the inner surface of the stabilizing metal material 34. A predetermined oxide powder is applied to the outer surfaces of the stabilizing metal materials 30a, 31, 32, 33, and 34, and these stabilizing metal materials 30a, 31, 32, 33, and 34 are combined together. The surface area of the resultant composite material is reduced by a surface area reducing means such as swaging or rolling. The area-reduced composite material is heated in an oxygen atmosphere, thereby obtaining the oxide superconductor wire 10 shown in Fig. 7. The oxide superconductor wire 20 shown in Fig. 8 can be manufactured following the same procedures as described above except that the rod-like stabilizing metal material 30b is used in place of the tubular stabilizing metal material 30a. Example 2 Oxide powders including a Y₂O₃,BaCO₃ and CuO powder were weighed and mixed such that Y : Ba : Cu was given as a molar ratio of 1 : 2 : 3. The resultant powder mixture was pre-burnt in an oxygen atmosphere at 920°C for 20 hours. The pre-burnt mixture was heated and melted at 1,300°C and solidified at a cooling rate of 10°C/sec to obtain a plate having a thickness of 1 mm. The plate was heated in an oxygen atmosphere at 950°C for 50 hours and pulverized into an oxide powder having a size of 4 µm in an automatic mortar. The resultant oxide powder was kneaded with a binder, and the kneaded material was applied to the outer surfaces of the silver stabilizing metal materials 30a, 31, 32, and 33 (Table 2) to a thickness of 20 µm. The binder contained in the kneaded material applied to the stabilizing metal materials 30a, 31, 32, and 33 was eliminated. The stabilizing metal materials 30a, 31, 32, and 33 which carried the predetermined oxide powder and the silver stabilizing metal material 34 without an oxide powder were combined in a concentric form, and the surface area of the resultant structure was reduced by cold-rolling to obtain a composite wire having an outer diameter of 2 mm. The composite wire was heated in an oxygen atmosphere at 830° for 20 hours to obtain the oxide superconductor wire 10. Example 3 An oxide superconductor wire 20 was manufactured following the same procedures as in Example 2 except that the stabilizing metal material 30b shown in Table 2 was used in place of the stabilizing metal material 30a. Example 4 An oxide superconductor wire 10 was manufactured following the same procedures as in Example 2 except that the oxide powder was replaced with a pre-burnt powder having a particle size of 5 µm. Comparative Example 3 A pre-burnt powder as in Example 4 was used as an oxide powder for the superconductor, and a silver pipe 41 having an outer diameter of 20 mm and an inner diameter of 15 mm was used as a metal sheath, as shown in Fig. 11. The pipe 41 filled with a pre-burnt powder 42 was worked by a surface area reducing means to obtain a superconductor wire 40 having an outer diameter of 0.5 mm, as shown in Fig. 11. Critical temperatures Tc, critical current densities Jc, and bending characteristics of Examples 2 to 4, and Comparative Example 3 were measured, and test results are shown in Table 3. The bending characteristics were measured such that each oxide superconductor wire was bent with a radius of curvature which was 50 times the outer diameter to determine whether the oxide superconductor was damaged. If the oxide superconductor was not damaged, it was represented by a circle; and if the oxide superconductor was damaged, it was represented by a cross. As in apparent from Table 3, the samples of examples 2 to 4 of the present invention have excellent bending characteristics, are free from damage, and larger Jc values than the sample of Comparative Example 3. In particular, the samples of Examples 2 and 3 have excellent properties. As has been described above, in the oxide superconductor of the present invention, the metal is finely distributed in the oxide superconductor in the form of a layer. The oxide superconductor is excellent in thermal and electrical conductivities. The oxide superconductor layer present between the metal layers is constituted by lanky crystal oriented in the C-axis. The oxide superconductor layer has particle boundaries which exhibit the pinning effect, so that the oxide superconductor has excellent superconductive characteristics such as a higher critical current density (Jc) and excellent mechanical characteristics (bending characteristics). In addition, a laminated body of an oxide superconductor or its precursor and a metal is heated at a temperature to partially melt the oxide superconductor or its precursor or more, thereby easily manufacturing the superconductor described above and providing remarkable industrial effect. According to the method of the present invention, a metal sheet is continuously distributed in an oxide superconductor layer, and this structure is elongated. Therefore, the oxide superconductor layer becomes dense and crystal orientation can be increased. In addition, since the metal sheet serves as a thermal and electrical conductor in the oxide superconductor, quenching and hysteresis loss can be suppressed to increase a Jc value and improve the shield effect, thereby rationally manufacturing oxide superconductors having excellent properties, and providing a remarkable industrial effect.

Claims: A composite oxide superconductor comprising oxide superconductor layers (2) and metal material layers (1), which are alternately laminated by a plurality of times, and a high-strength, heat-resistant metal material (9) selected from the group consisting of Fe, Ni-Cr (SUS), Ni, W and these metals coated with a noble metal, and being in contact with at least one of said superconductor layers (2) and/or at least one of said metal material layers (1) for providing a composite structure. A composite oxide superconductor according to claim 1, wherein the oxide superconductor layers (2) and the metal material layers (1) are alternately laminated on each other in a concentric form by a plurality of times. A composite oxide superconductor according to claim 1, wherein the oxide superconductor is a material selected from the group consisting of La 2-x Ba x CUO₄, La 2-x Sr x CuO₄, YBa₂Cu₃O 7-δ , DyBa₂Cu₃O 7-δ , ErBa₂Cu₃O 7-δ , HoBa₂Cu₃O 7-δ , Bi₂Sr₂CaCu₂O₈, Bi₂Sr₂Ca₂Cu₃O₁₀, Tl₂Ba₂CaCu₂O₈, Tl₂Ba₂Ca₂Cu₃O₁₀, and TlBa₂Ca₂Cu₇O 8.5 . A composite oxide superconductor according to claim 1, wherein the metal material of the metal material layer (1) is a metal selected from the group consisting of Ag, Ag-Pd, Ag-Au, Ag-Cu, Ag-Mg, Ag-Pt, Ag-Ir, Au, Au-Ni, Au-Cu, Au-Ag-Cu, Au-Pd-Ag, Au-Ir, Pt, Pt-Ir, Pt-Pd, Pd, Pd-Ni, Pd-Co, Ni-Cr, Ni-Cr-Co, Ni-Fe, Ni-Fe-Co, Fe-Cr, Fe, and Ni-Cr (SUS). A composite oxide superconductor according to claim 1, wherein the oxide superconductor layer (2) contains lanky crystal particles of which longitudinal direction are oriented in a longitudinal direction of the superconductor and includes at least one particle boundary in a direction perpendicular to the longitudinal direction. A composite oxide superconductor according to claim 1, wherein the superconductor has a rectangular, tape-like convex, concave, or polygonal cross section obtained by working. A composite oxide superconductor according to claim 1, wherein a plurality of oxide superconductors are bundled and covered with a metal material layer (1) or an oxide superconductor layer (2). A method of manufacturing a composite oxide superconductor as defined in claim 1, comprising the steps of alternately laminating layers of an oxide superconductor (2) or a precursor thereof and metal material layers (1) by a desired number of times, further bringing a high electrical resistance porous metal as a high-strength, heat-resistant metal material (9) selected from the group consisting of Fe, Ni-Cr (SUS), Ni, W and these metals coated with a noble metal in contact with at least one of said superconductor layers (2) and/or at least one of said metal material layers (1) for providing a composite structure, forming an outermost layer of a metal material on a laminated body, and performing predetermined heating and cooling operations of the laminated body as it is or after the laminated body is elongated into a desired shape. A method according to claim 8, wherein the oxide superconductor is a material selected from the group consisting of La 2-x Ba x CuO₄, La 2-x Sr x CuO₄, YBa₂Cu₃O 7-δ , DyBa₂Cu₃O 7-δ , ErBa₂Cu₃O 7-δ , HoBa₂Cu₃O 7-δ , Bi₂Sr₂CaCu₂O₈, Bi₂Sr₂Ca₂Cu₃O₁₀, Tl₂Ba₂CaCu₂O₈, Tl₂Ba₂Ca₂Cu₃O₁₀, and TlBa₂Ca₂Cu₇O 8.5 . A method according to claim 8, wherein the precursor of the oxide superconductor is an intermediate material between a source material which can be converted into an oxide superconductor and the oxide superconductor. A method according to claim 8, wherein the intermediate material is a material selected from the group consisting of an oxide mixture, a coprecipitation mixture, and an oxygen deficient composite oxide of oxide superconductor constituting elements, and an alloy of said constituting elements. A method according to claim 8, wherein the metal material of the metal material layer (1) is a metal selected from the group consisting of Ag, Ag-Pd, Ag-Au, Ag-Cu, Ag-Mg, Ag-Pt, Ag-Ir, Au, Au-Ni, Au-Cu, Au-Ag-Cu, Au-Pd-Ag, Au-Ir, Pt, Pt-Ir, Pt-Pd, Pd, Pd-Ni, Pd-Co, Ni-Cr, Ni-Cr-Co, Ni-Fe, Ni-Fe-Co, Fe-Cr, Fe, and Ni-Cr (SUS).

Inventors: ENOMOTO NORITSUGU, KIKUCHI HIROYUKI, SHIGA SHOJI, UNO NAOKI, ENOMOTO, NORITSUGU, KIKUCHI, HIROYUKI, SHIGA, SHOJI, UNO, NAOKI
Applicants: FURUKAWA ELECTRIC CO LTD, THE FURUKAWA ELECTRIC CO., LTD.
Application year: 1990
Main classification: H01L39
IPC codes: H01L39