Mixtures based on styrene copolymers having improved mechanical characteristics

Abstract: Described are mixtures based on styrene copolymers having improved mechanical characteristics, comprising - an impact-resistant styrene copolymer containing from 2 to 35% by weight of an ethylenically unsaturated nitrile, from 15 to 50% by weight of an olefinic elastomer and from 73 to 15% by weight of a styrene monomer; - a graft-copolymer with an elastomeric core having a second order glass transition temperature (Tg) lower than 10°C onto which vinyl monomer chains are grafted; and - an aromatic polycarbonate.

Description: The present invention relates to mixtures based on vinyl aromatic copolymers having improved mechanical characteristics. More specifically, the present invention relates to mixtures based on vinyl-aromatic polymers having a high isotropy, said mixtures being particularly suitable for injection molding and thermoforming of molded articles having high tenacity also in the flow joining areas. As it is known, impact-resistant styrene copolymers are obtainable by bulk-polymerization or bulk-suspension polymerization of solutions of polybutadiene or styrene-butadiene rubbers, of saturated rubbers of the ethylene-propylene type (EPM) or of rubbers based on ethylene/propylene/non-conjugated diene (EPDM), in styrene(alone or in admixture with other ethylenically unsaturated polymerizable monomers). In particular, the impact-resistant styrene copolymers containing an ethylenically unsaturated nitrile and being based on EPM or EPDM rubber, generally known as AES polymes, usually are obtained in the form of concentrates having a high rubber content and are utilized either as such or in admixture with other polymers in order to obtain products suitable for injection molding, extrusion and thermoforming and endowed with the desired properties. In fact, the AES copolymers exhibit excellent impact strength, but their low thermal stability and stiffness render them unsuitable for certain applications. In order to obviate this shortcoming of the AES copolymers it is known to prepare mixtures thereof with other polymers having the above properties. It is known, in fact, to blend the styrene copolymers based on EPM or EPDM rubber and acrylonitrile with a separately prepared styrene-acrylonitrile resin (SAN), as it is described in US-A- 3,489,821; 3,849,518; 3,676,528 and 4,202,948. European patent application No. 88 300 956 describes a mixture comprising 10-90% by weight of a styrene/ethylenically unsaturated nitrile/olefinic elastomer copolymer and 90-10% by weight of a mixture of resins containing aromatic groups, consisting of 70-99% by weight of polycarbonate and of 30-1% by weight of aromatic polyester. JP-A-51-24540 describes a thermoplastic composition comprising 90-10% of styrene-acrylonitrile-EPM or EPDM rubber copolymer and 10-90% of polycarbonate. Although these mixtures are satisfactory for applications in which high impact strength, thermal stability, resistance to chemical agents or to decoloring are required, they exhibit some shortcomings which limit the use thereof. Said shortcomings are mainly due to the low compatibility of the styrene copolymer with the other polymers which are utilized to compensate the lacking properties of said copolymer. In particular, the mixtures consisting of a styrene copolymer of the AES type and a polycarbonate exhibit a strong anisotropy of the resilience characteristics as well as an insufficient mechanical resistance especially in the flow joining areas owing to the low compatibility between these two polymers. It has now surprisingly been found that it is possible to prepare homogeneous polymeric compositions containing a styrene copolymer of the AES type and a polycarbonate by using, as a compatibilizing agent for the polycarbonate and the styrene copolymer, a graft-copolymer with an elastomeric core having a glass transition temperature lower than 10°C onto which vinyl monomer chains are grafted. Thus, the subject matter of the present invention are mixtures based on styrene copolymers, comprising (a) an impact-resistant styrene copolymer containing from 2 to 35% by weight of at least one ethylenically unsaturated nitrile, from 20 to 40% by weight of at least one olefinic elastomer having a iodine number higher than 5 and up to 40, and from 15 to 73% by weight of at least one styrene monomer, (b) an aromatic polycarbonate in a weight ratio of styrene copolymer to polycarbonate of from 10:90 to 90:10 and, as compatibilizing agent, (c) from 1 to 20% by weight, based on the mixture, of a graft-copolymer having an elastomeric core with a second order glass transition temperature (Tg) lower than 10°C being selected from polybutadiene and copolymers of butadiene with styrene, isoprene and/or acrylonitrile wherein the butadiene content is higher than 40% by moles, onto which vinyl monomer chains are grafted. Preferably, the mixtures of the present invention comprise (a) an impact-resistant styrene copolymer containing from 10 to 35% by weight of at least one ethylenically unsaturated nitrile, from 20 to 40% by weight of at least one olefinic elastomer having a iodine number higher than 5 and up to 40, and from 25 to 70% by weight of at least one styrene monomer, (b) an aromatic polycarbonate in a weight ratio of styrene copolymer to polycarbonate of from 70:30 to 30:70 and (c) from 3 to 10% by weight, based on the mixture, of a graft-copolymer with an elastomeric core having a second order glass transition temperature (Tg) lower than 10°C being selected from polybutadiene and copolymers of butadiene with styrene, isoprene and/or acrylonitrile wherein the butadiene content is higher than 40% by moles, onto which vinyl monomer chains are grafted. In the impact-resistant styrene copolymer which is utilized in the composition of the present invention the elastomeric component (which is the substrate onto which the ethylenically unsaturated nitrile and the styrene monomer are in part grafted and in part are made to physically adhere in the form of an ethylenically unsaturated nitrile/styrene copolymer) generally is a rubber-like copolymer (preferably having a Mooney viscosity ranging front 10 to 150 ML-4 at 100°C) of at least two different straight chain (preferably C₁₋₈-)alpha-monoolefins such as ethylene, propylene, butene-1, octene-1 and the like, with at least one other copolymerizable monomer, generally a polyene, and typically a non-conjugated diene. Preferably, one of the alpha-monoolefins is ethylene which is present together with another alpha-monoolefin having a longer chain. The weight ratio of ethylene to the other alpha-monoolefin(s) in the rubber-like copolymer usually is in the range of from 20/80 to 80/20. Particularly preferred copolymers are the ethylene/propylene/non-conjugated diene terpolymers wherein the non-conjugated diene may be cyclic or acyclic. Examples of suitable dienes are: 5-methylene-2-norbornene; 5-ethylidene-2-norbornene; 5-isopropylene-2-norbornene; pentadiene-1,4; hexadiene-1,4; hexadiene-1,5; heptadiene-1,5; dodecatriene-1,7,9; methyl-heptadiene-1,5; norbornadiene-2,5; cyclooctadiene-1,5; dicyclopentadiene; tetrahydroindene; 5-methyl-tetrahydroindene, etc. The diene content preferably ranges from about 5 to about 20% by weight and particularly from about 8 to about 18% by weight of diene monomer units in the rubber-like terpolymer. Particularly favourable results are obtained by using a rubber-like terpolymer having a Mooney viscosity (ML-4), measured at 100°C, of from 30 to 90 and a iodine number higher than 5, preferably ranging from 10 to 40. The term "styrene monomer", whenever used in the present specification and in the claims, comprises ethylenically unsaturated compounds having the general formula : wherein: X is hydrogen or an alkyl radical having 1 to 4 carbon atoms (e.g. methyl and ethyl); Y is hydrogen, halogen (e.g. Cl, Br, I and F) or an alkyl radical having 1 to 4 carbon atoms (e.g. methyl, ethyl, propyl and butyl) and n is 0 or an integer from 1 to 5. Examples of vinyl-aromatic monomers of the above general formula are : styrene; methyl-styrene; mono-, di-, tri-, tetra- and penta-chloro-styrene and the corresponding alpha-methyl-styrenes; nucleus-alkylated styrenes and the corresponding alpha-methyl-styrenes such as ortho- and para-methyl-styrenes; ortho- and para-ethyl-styrenes; ortho- and para-methyl-alpha-methyl-styrenes, etc. These monomers are utilizable individually or in admixture with one another. The term "ethylenically unsaturated nitrile" in the first place and preferably denotes acrylonitrile, although other acrylic monomers such as methacrylonitrile, acrylic acid, methacrylic acid and (preferably C₁₋₄-)alkyl-esters of acrylic or methacrylic acid can also be used. Examples of copolymerization methods for obtaining the impact-resistant styrene copolymers utilizable in the mixtures of the present invention are described in Italian patent No. 792,269 and in US-A-3,819,765; 3,489,822; 3,642,950 and 3,849,518, the contents whereof are included herein by reference. It is to be understood that in the graft-copolymerization not the whole monomer forming the resin is grafted onto the rubber-like core; a part of the monomer forms a free resin, which is present in physical mixture with the graft-copolymer. The amount of grafted monomer in the copolymer can be determined by extracting the product with a solvent for the non-grafted resin. The aromatic polycarbonates employable in the mixtures of the present invention can be homopolymers and copolymers based, for example, on one or more of the following bisphenols : di-hydroxy-diphenyls, bis-(hydroxyphenyl)-alkanes, bis-(hydroxyphenyl)-cycloalkanes, bis-(hydroxyphenyl)-sulphides, bis-(hydroxyphenyl)-ethers, bis-(hydroxyphenyl)-ketones, bis-(hydroxyphenyl)-sulphoxides, bis-(hydroxyphenyl)sulphones, alpha-alpha-bis-(hydroxyphenyl)-diisopropyl benzenes and also their nucleus-alkylated or nucleus-halogenated derivatives. These and other aromatic dihydroxy compounds are well known and described in the literature. Preferred bisphenols are those which correspond to formula (II): wherein each of R₁,R₂,R₃ and R₄ independently represents hydrogen, an alkyl radical containing from 1 to 4 carbon atoms or halogen; and A represents -O-, -CO-, -SO₂-, an alkylene radical containing 2 to 10 carbon atoms, an alkylidene radical containing from 2 to 10 carbon atoms, a cycloalkylene radical containing from 5 to 15 carbon atoms, a cycloalkylidene radical containing from 5 to 15 carbon atoms or the radical : Particularly preferred bisphenols are, for example, 2,2-bis-(4-hydroxyphenyl)-propane; 2,2-bis-(3,5-dimethyl-4-hydroxyphenyl)propane; 2,2-bis-(3,5-dichloro-4-hydroxyphenyl)-propane; 2,2-bis-(3,5-dibromo-4-hydroxyphenyl)-propane and 1,1-bis-(4-hydroxyphenyl)-cyclohexane. Particularly preferred polycarbonates are the ones based on one or more of the above bisphenols. In particular, the polycarbonates based on 2,2-bis-(4-hydroxyphenyl)-propane and 2,2-bis-(3,5-dimethyl-4-hydrophenyl)-propane,alone or in admixture with one another or with one of the remaining bisphenols above, are preferred. Polycarbonates containing in the chain units derived from terephthalic and/or isophthalic acid are utilizable as well. The aromatic polycarbonates can be prepared according to known methods, for example by transesterification in the molten state from bisphenols and diphenyl-carbonate, and by the two-phase interface process from bisphenol and phosgene, as described in H. Schnell "Chemistry and Physics of Polycarbonates" Interscience Publisher, New York, 1964. The aromatic polycarbonates can also be of the branched type, due to the incorporation of small amounts, preferably from 0.05 to 2 percent by moles, of compounds having three or more functional groups, in particular having three or more phenolic hydroxy groups. The aromatic polycarbonates which may be utilized in the mixtures of the present invention generally have an average molecular weight of at least about 10,000, more particularly from about 10,000 to about 200,000 and preferably from about 20,000 to about 80,000, as determined by measuring the relative viscosity in CH₂Cl₂ at 25°C and at a concentration of 0.5% by weight. The aromatic polycarbonates containing repeating units (II) are well known in the art and are available from several manufacturers, for example: General Electric Company, Pittfield, Mass., USA, under the name "LEXAN®"; ANIC, S. Donato Milanese (Milan), under the name "SIN-VET®"; Proquigel (Brazil), under the name "DUROLON®", etc. The graft-copolymer which is used to make the impact-resistant styrene copolymer compatible with the aromatic polycarbonate is a polymer of the "core-shell" type, comprising an elastomeric core having grafted thereon chains of vinyl monomers. Preferably, the core-shell polymer comprises from about 25 to about 95% by weight of the first elastomeric stage and from about 75 to about 5% by weight of grafted chains of vinyl monomers. The elastomeric core has a second order glass transition temperature lower than 10°C and it may be selected from, e.g., polybutadiene and copolymers of butadiene with styrene, isoprene and/or acrylonitrile wherein the butadiene content is higher than 40% by moles. The vinyl monomers which are grafted onto the elastomeric core can be acrylic acid derivatives or methacrylic acid derivatives, vinyl-aromatic compounds, vinyl-cyanide compounds and polyfunctional derivatives, either individually or in admixture with one another. Specific examples of these grafted vinyl monomers comprise methacrylic acid C₁₋₁₆-alkyl esters, preferably methyl methacrylate, esters of methacrylic acid with polyfunctional alcohols such as 1,3-butylenglycol dimethacrylate and trimethylol-propane-trimethacrylate, diallyl methacrylate and/or diallyl methacrylate; vinyl-aromatic compounds such as styrene, vinyl toluene, alpha-methyl styrene, halogenated styrene, vinyl naphthalene or divinyl benzene, styrene being particularly preferred; vinyl cyanide compounds such as acrylonitrile, methacrylonitrile, alpha-halogenated acrylonitriles; acrylonitrile being particularly preferred; maleic acid and maleic anhydride. These vinyl monomers can be used separately or in mixture. The graft-copolymer used in the mixtures of the present invention preferably has a second order glass transition temperature lower than -10°C and even lower than -50°C and a cross-linking degree of at least about 50% and up to about 99% by weight (gel content), determined by extraction. The graft- copolymer used in the mixtures of the present invention preferably has an elastomer content of at least about 35% and up to about 95% by weight. These copolymers are preparable by means of any known method such as bulk polymerization, suspension polymerization, bulk-suspension polymerization, solution polymerization or emulsion polymerization. In the preparation of the graft- copolymer, a homopolymer or copolymer of the vinyl monomer can directly be formed in the reaction product, or the reaction product as such can be used as a grafted polymer. A typical example of a graft-copolymer to be used in the mixture of the invention is a three-stage polymer having a rubber-like core based on butadiene, a second stage polymerized from styrene and a final stage, or shell, polymerized from methyl methacrylate and 1,3-butylene glycol dimethacrylate. The above graft-copolymers are well known and are available from many manufacturers such as, for example, Rohm & Haas Company, Philadelphia, USA, under the name Paraloid® EXL 2607 or Paraloid® EXL 3607. The mixtures of the present invention can be prepared by means of hot mixing in any known mixing unit, such as single-screw or double-screw extruders, Banbury mixers, mixing rolls etc. at a temperature ranging from 200 to 300°C. The compositions may contain stabilizers, UV stabilizers or other additives intimately incorporated therein, such as plasticizers, lubricants, antiflame agents, flow agents, antistatic agents, dyes, pigments, glass fibres or other inorganic fillers etc., in order to impart particular characteristics to the material. The mixtures of the present invention may easily be processed and exhibit a complex of properties which make them suitable for use in the production of articles endowed with a high tenacity, in particular in the flow joining areas, along with a high impact strength and thermal stability. The fields of use of said mixtures, therefore, are the automotive sector, the sectors of household electric apparatus and appliances, of electronics and technical articles in general in the form of films, sheets, strips,panels, bands, rods, boxes, pans, containers and the like. The mixtures can be used to produce foamed articles by means of conventional techniques. The following examples are given in order to illustrate the present invention without being a limitation of embodiments thereof. Examples 1-5 By means of a double-screw extruder(WERNER ZSK 53), under degassing and at a temperature of 220-290°C, mixtures were extruded which consisted of : a) an impact-resistant styrene copolymer consisting of 57% by weight of styrene, 18% by weight of acrylonitrile and 25% of EPDM rubber having a Mooney viscosity of 62-72 ML-4 at 100°C and a iodine number equal to 18; b) polycarbonate produced by Proquigel under the name "Durolon®"having an average molecular weight of 22,000; c) butadiene rubber consisting of a butadiene/styrene/methylmethacrylate graft- copolymer having a cross-linking degree (gel content) of 94% by weight and a glass transition temperature (Tg) of -80°C, sold by Rohm & Haas under the name Paraloid® EXL 2607. The weight ratios of the above components are indicated in Table 1. By cutting the strands leaving the extruder, granules were obtained, which were dried for 2-4 hours at 80°-90°C. In order to evaluate the tenacity in the flow joining areas, the granules were injection molded in a press(NEGRI & BOSSI V 15-23 FA)with a tablet mold. There was molded a rectangular tablet, shown in Figure 1, measuring 250x150x2 mm and provided with 6 holes. Of these holes, two were square, two circular and two triangular. The two circular holes had a diameter of 20 mm,were equidistant from the tablet centre and arranged on a vertical line passing through the centre (A) of the tablet and through the centres of the two holes. The distance between the two holes was 80 mm. The two square holes had sides 13 mm long, and were arranged on the right side of the tablet and symmetrically to the horizontal center line of the tablet. The distance between the centres of the two squares was 160 mm. The two triangular holes were equilateral, with sides of 15 mm, they were arranged on the left side of the tablet and symmetrically to the horizontal center line of the tablet. The distance between the two centers of the triangles was 160 mm. Fig. 1 shows the front view of the tablet. On said tablet the tenacity was determined in point A, corresponding to the tablet center, and in point B, corresponding to the intersection of the horizontal line passing through center A of the tablet and the vertical line connecting the two centres of the squares. The tenacity was measured by means of the "ball drop" test according to standard DIN 53443. For a determination of the other characteristics, the granules were injection molded at a temperature of 210°C in a NEGRI & BOSSI press V-17-110 FA in order to obtain the test pieces having the dimensions required by the standards. The measured characteristics and the methods used were as follows : Mechanical properties The tensile strength and the elastic modulus, according to standard ASTM D 368, and the IZOD resilience on notched bar at 23°C, according to standard ASTM D 256, were determined on test pieces having a thickness of 3.2 mm and 12.7 mm. Thermal properties The VICAT B softening temperature (5 kg in oil) was determined according to standard ISO 306. Rheological properties The melt-index was determined according to standard ASTM D 1238, at 260°C and 5 kg. The measured values are reported in the following table I. COMPOSITION EXAMPLES 1 2 3 4 5 a) Styrene copolymer 40 35 46 25 70 b) Polycarbonate "DUROLON®" 60 60 46 70 20 c) Paraloid® EXL 2607 - 5 8 5 10 Tenacity Area A J 4 55 45 60 40 (Ball drop) Area B J 39 60 50 65 45 Mechanical properties - Tensile strength tensile yield strength N/mm² 48 44 42 46 38 ult. tensile strength N/mm² 49 45 40 48 40 elastic modulus N/mm² 2200 1900 1900 2100 1700 - IZOD resilience 1/2" x 1/8" J/m 590 550 500 560 400 1/2" x 1/2" J/m 350 450 420 460 350 Thermal properties - Vicat B °C 120 125 115 130 100 Rheological properties - Melt index g/10' 21 18 15 10 20

Claims: Mixtures based on styrene copolymers and having improved mechanical characteristics, comprising (a) an impact-resistant styrene copolymer containing from 2 to 35% by weight of at least one ethylenically unsaturated nitrile, from 20 to 40% by weight of at least one olefinic elastomer having a iodine number higher than 5 and up to 40, and from 15 to 73% by weight of at least one styrene monomer, (b) an aromatic polycarbonate in a weight ratio of styrene copolymer to polycarbonate of from 10:90 to 90:10 and, as compatibilizing agent, (c) from 1 to 20% by weight, based on the mixture, of a graft-copolymer having an elastomeric core with a second order glass transition temperature (Tg) lower than 10°C being selected from polybutadiene and copolymers of butadiene with styrene, isoprene and/or acrylonitrile wherein the butadiene content is higher than 40% by moles, onto which vinyl monomer chains are grafted. Mixtures according to claim 1, comprising (a) an impact-resistant styrene copolymer containing from 10 to 35% by weight of at least one ethylenically unsaturated nitrile, from 20 to 40% by weight of at least one olefinic elastomer having a iodine number higher than 5 and up to 40, and from 25 to 70% by weight of at least one styrene monomer, (b) an aromatic polycarbonate in a weight ratio of styrene copolymer to polycarbonate of from 70:30 to 30:70 and (c) from 3 to 10% by weight, based on the mixture, of a graft-copolymer with an elastomeric core having a second order glass transition temperature (Tg) lower than 10°C being selected from polybutadiene and copolymers of butadiene with styrene, isoprene and/or acrylonitrile wherein the butadiene content is higher than 40% by moles, onto which vinyl monomer chains are grafted. Mixtures according to anyone of claims 1 and 2, in which the olefinic elastomer is a rubber-like copolymer having a Mooney viscosity ranging from 10 to 150 ML-4 at 100°C. Mixtures according to anyone of claims 1 to 3, in which the olefinic elastomer is an ethylene/propylene/non-conjugated diene copolymer having a Mooney viscosity ranging from 30 to 90 ML-4 at 100°C. Mixtures according to anyone of the preceding claims, in which the styrene monomer has the general formula : in which: X is hydrogen or an alkyl radical having 1 to 4 carbon atoms; Y is hydrogen, a halogen or an alkyl radical having 1 to 4 carbon atoms, and n is 0 or an integer from 1 to 5. Mixtures according to anyone of the preceding claims, in which the copolymerized ethylenically unsaturated nitrile is acrylonitrile. Mixtures according to anyone of the preceding claims, in which the aromatic polycarbonate is derived from a bisphenol having formula (II): wherein R₁,R₂,R₃ and R₄ each independently represent hydrogen, an alkyl radical containing from 1 to 4 carbon atoms or halogen; and A represents -O-, -CO-, -SO₂-, an alkylene radical containing from 2 to 10 carbon atoms, an alkylidene radical containing from 2 to 10 carbon atoms, a cycloalkylene radical containing from 5 to 15 carbon atoms, a cycloalkylidene radical containing from 5 to 15 carbon atoms or a radical of formula (III): Mixtures according to anyone of the preceding claims, wherein the aromatic polycarbonate has an average molecular weight equal to or higher than about 10,000, preferably from about 10,000 to about 200,000. Mixtures according to anyone of the preceding claims, wherein the graft-copolymer is of the core-shell type and comprises from about 25 to about 95% by weight of an elastomeric core and from about 75 to about 5% by weight of grafted chains of vinyl monomers. Mixtures according to anyone of the preceding claims, wherein the vinyl monomers grafted onto the elastomeric core are selected from acrylic acid derivatives, methacrylic acid derivatives, vinyl-aromatic compounds, vinyl cyanide compounds, polyfunctional derivatives and mixtures thereof. Mixtures according to any of the preceding claims, where in the grafted copolymer has a second order transition temperature lower than -10°C, preferably lower than -50°C, and a cross-linking degree of from 50% to 99%. Mixtures according to anyone of the preceding claims, wherein the graft-copolymer has an elastomer content of from 35% to 95% by weight. Mixtures according to anyone of the preceding claims, wherein the graft-copolymer is a three-stage copolymer having a rubber-like core based on butadiene, a second stage derived from styrene and a final stage or shell derived from methyl methacrylate and 1,3-butylene-glycol dimethacrylate. Mixtures according to anyone of the preceding claims,additionally containing stabilizers, UV-stabilizers, plasticizers, lubricants, anti-flame agents, antistatic agents and/or glass fibres or other inorganic fillers.

Inventors: FASULO GIAN CLAUDIO, GHIDONI DARIO, LICON ANDREA, FASULO, GIAN CLAUDIO, GHIDONI, DARIO, LICON, ANDREA
Applicants: ENICHEM SPA, ENICHEM S.P.A.
Application year: 1990
Main classification: C08L69
IPC codes: C08L51, C08L25, C08L69