PROCESS FOR REDUCING PROPENYL ETHER CONCENTRATION IN HYDROXY-FUNCTIONAL POLYETHER COMPOUNDS

Abstract: The concentration of propenyl ethers in a hydroxy-functional polyether having oxypropylene units is reduced by a process including the step of contacting the polyether with an acid ion exchange resin for a time and at a temperature sufficient for the conversion of at least some of the propenyl ethers to propionaldehyde and in the presence of sufficient water for the conversion. Optionally, the polyether is treated with an epoxy compound in an amount sufficient to reduce the acidity of the polyol.

Description: PROCESS FOR REDUCING PROPENYL ETHER CONCENTRATION IN HYDROXY-FUNCTIONAL POLYETHER COMPOUNDS This invention relates to a process for purification of polyethers, more specifically to a process for purification of hydroxy-functional polyethers. It has long been recognized that unsaturated compounds occur in polyethers prepared by polymerizing al ylene oxides. When the alkylene ethers include propylene oxide units, 1,2-propenyl ether is among the unsaturated compounds and is indicative of the presence of same. Presence of such unsaturated compounds in polypropylene glycols is discussed by G.J. Dege, R.L. Harris and J.S. MacKenzie in J. Amer. Chem. Soc, 81, p 337*4 (1959). In certain polyurethanes prepared from polyether polyols, these unsaturated compounds are believed to cause discoloration, particularly discoloration on heating referred to as scorch. Removal of the unsaturated compounds is, therefore, desirable. There are variety of means of purifying polyethers. Some polyether polyol treatments have involved ion exchange resins. Purification of certain polyether polyols has involved water and certain cationic resins as described in Japanese J61043629. In the process described in German 210,460, acid neutralization of catalyst is followed by certain ion exchange resin treatment. A mercury activated sulfonated polystyrene ion exchange resin is used in the process described in U.S. Patent 3,271,462 to Earing. Certain ion exchange resins are optionally used in place of mineral acids for hydrolyzing certain acetals in certain polyols as in the process disclosed by Mills et al. in U.S. Patent 2,812,360. Certain mixed resins are used to treat certain polyethylene glycols for human cell genetic transfection as disclosed in U.S. Patent 4,650,909 to Yoakum. In the process disclosed by U.S. Patents 4,355,188 to Herold et al., a polyol may be ion exchanged or neutralized after a strong base is used to treat polyols formed using metal cyanide complex catalysts. Belgian Patent No. 634,036 describes a process for reducing or eliminating the unsaturation of polyoxyalkylene polyols. The process comprises placing the polyoxyalkylene polyol in contact with water and an acidic cation exchanger resin which is at least partially converted into mercuric salt by treatment with a water-soluble mercuric salt. Acidic ion exchange resins, particularly sulfonic acid ion exchange resins are known to release acids into organic compounds. This phenomenon is discussed, for instance, I. J. Jakovac in Catalyst Supports and Supported Catalysts, by A.B. Stiles, Ed., Butterworths, Boston (1987) pp. 190. Acids are, however, detrimental in certain formulations for forming polyurethanes. In some instances, certain epoxy compounds have been disclosed for removal of certain acids from certain other compounds. In the process disclosed in U.S. Patent 4,164,487 to Martin, certain coating compositions are treated with certain epoxy compounds after treatment with phosphoric acid. Certain anaerobic compositions containing acidic impurities are stabilized by addition of certain epoxy compounds in the process disclosed in U.S. Patent 4,245,077. Certain epoxy compounds are disclosed for treatment of acidity or hydrolyzable chloride in certain isocyanates as disclosed in U.S. Patents 3,264,336 to Powers and 3,793,362 to Kolakowski, et al. and East German 238,988. These references do not, however, teach that epoxy compounds are useful for removing acidic compounds from polyether hydroxyl- containing compounds. In one aspect, this invention is a process for reducing the concentration of propenyl ethers in a hydroxy-functional polyether having oxypropylene units comprising the step of contacting the polyether with an acid ion exchange resin for a time and at a temperature sufficient for the conversion of at least some of the the propenyl ethers to propionaldehyde in the presence of sufficient water for the conversion. Preferably, the process further comprises treating the polyether with an epoxy compound in an amount sufficient to reduce the acidity of the polyol. In another aspect, this invention is a process for reducing the concentration of propenyl ethers in a hydroxy-functional polyether having oxypropylene units comprising contacting the polyether with a gel-type sulfonic acid ion exchange resin having an aqueous exchange capacity of from 0.5 to 5 equivalents /liter for a time and at a temperature sufficient for the conversion of at least some of the the propenyl ethers to propionaldehyde and in the presence of sufficient water for the conversion. In another aspect, this invention is a process for reducing the acidity of a hydroxy-functional polyether comprising treating the polyether with an epoxy compound in an amount sufficient to reduce the acidity of the polyether. In yet another aspect, this invention is a composition comprising (A) a hydroxy-functional polyether which is the polymerization prepared product of propylene oxide or a mixture of propylene oxide with an alkylene oxide selected from ethylene oxide, butylene oxide and mixtures thereof in the presence of an initiator; and (B) at least one epoxy compound different from ethylene oxide, propylene oxide and butylene oxide. Hydroxy-functional polyethers treated in the practice of this invention are polyalkylene polyethers having at least one hydroxyl group, preferably, polyalkylene polyether polyols. Said polyethers include the polymerization products of oxiranes or other oxygen- containing heterocyclic compounds such as tetramethylene oxide in the presence of a catalyst; and/or initiated by water, polyhydric alcohols having from two to eight hydroxyl groups, amines and the like. Preferably, the polyethers have at least some oxypropylene units produced from propylene oxide. The propylene oxide is homopolymerized or copolymerized with one or more other oxiranes or other oxygen-containing heterocyclic compounds. The oxygen-containing heterocyclic compounds are, preferably, alkylene oxides. The oxygen-containing heterocyclic compounds, herein after exemplified by alkylene oxides, are suitably reacted either in mixture or sequentially. When more than one alkylene oxide is used, resulting polyethers can contain random, block or random and block distributions of monomers. Mixtures of alkylene oxides most often produce randomly distributed alkylene oxide units. Sequential addition of different alkylene oxides most often produces blocks of the alkylene oxide segments in a polyether chain. Exemplary oxiranes suitable for preparation of polyethers include ethylene oxide, propylene oxide, butylene oxide, amylene oxide, glycidyl ethers such as t-butyl glycidyl ether and phenyl glycidyl ether. Other suitable oxiranes include 1,2-butylene oxide, 1,2- hexylene oxide, 1,2-decene oxide, 2-methoxy propylene oxide, methoxy ethylene oxide, 2,3-butylene oxide, 2,3- hexylene oxide, 3,4-decene oxide, 1 , 1 , 1-trifluoromethyl 2,3-epoxyoctane, styrene oxide and the like. The polyethers are also prepared from starting materials such as tetrahydrofuran copolymerized with alkylene oxide; epihalohydrins such as epichlorohydrin, epiiodohydrin, epibromohydrin, 3,3-dichloropropylene oxide, 3-chloro-1 ,2-epoxypropane, 3-chloro-1 ,2- epoxybutane, 3,4-dichloro-1 ,2-epoxybutane, 3,3,3- trichloropropylene oxide and the like; arylalkylene oxides such as styrene oxide and the like. Preferably, the polyethers are prepared from alkylene oxides having from two to six carbon atoms such as ethylene oxide, propylene oxide, and butylene oxide. More preferably, the polyethers are prepared from at least about 10, most preferably at least about 50, and even more preferably at least about 80 percent of an alkylene oxide selected from propylene oxide, 1,2-butylene oxide, 2,3-butylene oxide or mixtures thereof. Most preferably, propylene oxide is selected from propylene oxide, 1,2-butylene oxide, 2,3-butylene oxide or mixtures thereof; and preferably, the polyethers are prepared from at least about 10, more preferably at least about 50, and most preferably at least about 80 percent propylene oxide. Homopolymers of propylene oxide, or copolyethers of propylene oxide with ethylene oxide, butylene oxides and mixtures thereof are most preferred for use in the practice of the invention. Illustrative alcohols suitable for initiating formation of a polyalkylene polyether include glycerine, ethylene glycol, 1,3-propylene glycol, dipropylene glycol, 1 ,2-propylene glycol, 1,4-butylene glycol, 1,3- butylene glycol, 1,2-butylene glycol, 1,5-pentane diol, 1,7-heptane diol, glycerol, 1, 1 , 1-trimethylolpropane, 1 ,1,1-trimethylolethane, hexane-1 ,2,6-triol, alpha- methyl glucoside, pentaerythritol, erythritol, as well as pentols and hexols. Sugars such as glucose, sucrose, fructose and maltose, as well as compounds derived from phenols such as (4,4'-hydroxyphenyl)2,2-propane, bisphenols, alkylphenols such as dodecylphenol, octylphenol, decylphenol and mixtures thereof are also suitable alcohols for forming polyether polyols useful in the practice of the invention. Mono-alcohols, preferably mono-alcohols having from 1 to 18 carbon atoms, and alkoxy-substituted mono-alcohols such as methanol, ethanol, all isomers of propyl alcohol, all isomers of butyl alcohol, and ethers thereof are also suitable for forming hydroxy-functional polyethers. Amines suitable for reaction with oxiranes to form polyethers include aliphatic and aromatic mono- amines, optionally having substituents such as, for example, alkyl, carboxyl and carboalkoxy substitution. Exemplary aromatic amines include aniline, o- chloroaniline, p-phenylene diamine, 1,5- diaminonaphthalene, methylene dianiline, the condensation products of aniline and formaldehyde and 2,4-diamino toluene. Exemplary aliphatic amines include methylamine, triisopropanolamine, isopropanolamine, diethanolamine, ethyenediamine, 1 ,3-propylenediamine, 1 ,4-propylenediamine, 1 ,4-butylenediamine, and mixtures thereof. Amine based polyols are exemplified by those disclosed in U.S. Patent 4,358,547. The polyethers preferably have an average of from 1 to 8, preferably from 2 to 4 hydroxyl groups per molecule. The polyethers preferably have molecular weights ranging from 88 to 50,000, preferably from 1000 to 7500. The polyethers may be prepared by processes known to those skilled in the art such as those processes described in Encyclopedia of Chemical Technology, Vol. 7, pp. 257-262, Interscience Publishers (1951); M. J. Schick, Nonionic Surfactants, Marcel Dekker, New York (1967); British Patent 898,306; and U.S. Patents 1,922,459; 2,871,219; 2,891,073; and 3,058,921. One or more catalysts are advantageously used in the preparation of the polyethers. Conventional catalysts include, for example, alkali or alkaline earth metals or their corresponding hydroxides and alkoxides, Lewis acids and mineral acids. One skilled in the art can readily determine suitable amounts of alkylene oxides, initiators, catalysts and adjuvants as well as suitable process conditions for polymerizing the alkylene oxides. Additional sources of detail regarding polymerization of alkylene oxides include U.S. Patents 2,716,137; 3,317,508; 3,359,217; 3,730,922; 4,118,426; 4,228,310; 4,239,907; 4,282,387; 4,3326,047; 4,446,313; 4,453,022; 4,483,941 and 4,540,828. Preferred catalysts include basic catalysts, more preferably hydroxides and alkoxides of alkali and alkaline earth metals, particularly cesium, sodium, potassium and lithium. Potassium hydroxide is more preferred. When alkoxides are used as catalysts, the alkoxy groups advantageously contain from one to 36 carbon atoms. Exemplary of such alkoxides are alkoxides having anions of propylene glycol, glycerine, dipropylene glycol and propoxylated propylene or ethylene glycols. When a basic catalyst is used in the preparation of a polyether, there is resulting basicity which is neutralized to preferably less than about 20 ppm, more preferably less than about 10 ppm, most preferably less than about 5 ppm hydroxide or alkoxide catalyst in the polyether. In the process of the invention, the polyether, having its catalyst and water levels reduced to the preferred ranges, is then treated by being heated or cooled to a temperature suitable for acidic ion exchange resin catalyzed propenyl hydrolysis treatment and is passed through an acid ion exchange column, preferably upward through the ion exchange column in order to fluidize the ion exchange bed and avoid crushing the resin. Ion exchange resins suitable for use in the practice of the invention include all acidic resins, such as ion exchange resins having carboxylic acid functionality, sulfonic acid functionality, and mixtures thereof. Preferably, the resin has sulfonic acid functionality. The resin preferably has an aqueous exchange capacity of from 0.5 to 5, more preferably from 1 to 3, most preferably 1.5 to 2 equivalents/liter (of wet resin). Dry resin has about half the volume of wet resin. The term "aqueous exchange capacity" is defined as the number of equivalents of exchangeable ions per unit volume of resin. The aqueous exchange capacity can be obtained for acidic resins by titration with base in the presence of neutral salt. While the ion exchange resin suitably has any backbone or substrate, it preferably has a styrene/divinyl benzene backbone. The amount of divinyl benzene is preferably from 5 to 15 weight percent. This amount of divinyl benzene results in crσsslinking sufficient to form a gel or solid resin bead. Beads used in the practice of the invention are preferably gel beads. Gel beads are also known as microreticular resins, rather than macroreticular resins, and are advantageously produced in a suspension-type of polymerization wherein a monofunctional monomer such as styrene is polymerized with a fixed amount of bifunctional monomer such as divinylbenzene such that there is crosslinking at random positions. The beads are then functionalized by processes within the skill in the art. Preferably the beads are functionalized to produce sulfonic acid groups. Acidic ion exchange resin beads are commercially available. Exemplary beads include certain Amberlite ® ion exchange resins commercially available from Rohm and Haas Company such as Amberlite ® 200, Amberlite ® 252, Amberlite ® 1R-118(H), Amberlite ® IR-120 Plus (H), Amberlite ® IRC-50 and certain D0WEX ion exchange resins commercially available from The Dow Chemical Company such as D0WEX ® HGR W2-H, D0WEX ® MSC-1-H and D0WEX ® CCR-2. Preferred among these ion exchange resins are the gel resins which include D0WEX ® HGR W2-H, D0WEX ® HGR, DOWEX ® HCR-W2, DOWEX ® HCR-S, commercially available from The Dow Chemical Company, Amberlite ® IR118, Amberlite ® IR120, Amberlite ® IR122 and Amberlite ® IR124 commercially available from Rohm and Haas Company. The gel-type resins are preferred because longer useful resin life and less degradation of polyol is noted, particularly at higher temperatures. It is believed that gel-type resins have pores too small for the polyether molecules to enter and become trapped, and where the polyether may degrade. The polyether is in contact with the resin for a time sufficient for the conversion of at least some of the the propenyl ethers to propionaldehyde, preferably at least about 30 seconds, more preferably from 5 to 60 minutes, most preferably from 5 minutes to 30 minutes. This contact time is controlled by the flow rate through a column and the volume of resin in that column. Achieving desired contact times is within the skill in the art without undue experimentation. Contact time is preferably balanced with temperature to avoid degradation of the polyether. Degradation can result in discoloration which is to be avoided. Contact of resin and polyether suitably takes place at any temperature sufficient for the conversion of at least some of the propenyl ethers to propionaldehyde at a temperature at which degradation is avoided. Preferably the temperatures are from 25°C to 200°C, more preferably from 50°C to 125°C. Higher temperatures are preferably avoided when the resins are highly active such as fluorocarbon sulfonic acid resins and macroreticular resins. Weak acid carboxylic acid resins are preferably used at higher temperatures within the range, on the order of about 120°C, while sulfonic acid resins are suitable for use over the entire range. Contact is conveniently conducted at ambient pressure, but any pressure sufficiently high to maintain the reactants in a liquid phase and sufficiently low to avoid crushing the beads is suitable. Contact of the polyether with the resin should take place in the presence of sufficient water for the conversion of propenyl ethers to aldehydes. Preferably there is at least an amount of water stoichiometric with the amount of propenyl ethers present in the polyol. More preferably, there is at least a 25 fold excess of water. For instance, a triol having a molecular weight of about 3000, 0.01 meq/g of propenyl ether and 0.5 weight percent water, has a 28 fold excess of water. Water content of the polyol in contact with the resin preferably is at least about 0.1 weight percent, more preferably from 0.1 to 95 weight percent, most preferably from 0.2 to 10 weight percent, and even more preferably from 0.5 to 2 weight percent water in the polyether. Within these ranges, equipment used for polyether preparation and treatment determines what concentration of water is desirable. Certain equipment is more suitable for handling large volumes of water than is other equipment. After ion exchange treatment, the polyether is preferably treated with an epoxy compound to reduce acidity. The acidity before treatment generally ranges from 0.1 to 30 ppm, more commonly from 1 to 2 ppm. Propionaldehyde and water concentrations are optionally reduced before or after treatment with an epoxy compound or mixture thereof. To avoid hydrolysis of epoxy compounds, water concentration is preferably less than about 2, more preferably from 0.005 to 2 weight percent in the polyether. Addition or reduction of water is within the skill in the art. For instance, vacuum stripping may be used to remove water. Any inert epoxy compound, that is a compound which has at least one epoxy group and which is not detrimental to polyether stability, but which is effective to reduce the acidity of the polyether, is suitably used in the practice of the invention. Suitable epoxy compounds include monoepoxy and polyepoxy compounds including alkylene oxides such as, for example, butylene oxide (all isomers), propylene oxide ethylene oxide and styrene oxide as well as glycidyl ethers such as, for example, cresyl glycidyl ethers and phenylglycidyl ether; epoxy resins, including those formed from epichlorohydrin and bisphenols, such as, for example, bisphenol A and bisphenol F, as well as aliphatic and cycloaliphatic epoxy resin such as, for example, epoxycyclohexylmethyl epoxycyclohexyl carboxylates; cresol resins and Novolac resins. The epoxy compounds preferably have structures represented by Formula 1 : H H / \ R Formula I wherein R and R' (referred to hereinafter as R groups) are independently hydrogen, inert groups or R and R' together form an inert cyclic structure. Inert groups are groups which are not detrimental to polyether stability under conditions effective for treatment of polyethers to reduce acidity. Suitable inert groups include, for instance, additional epoxy groups, halogens, ester, alkyl, aryl, aralkyl, cycloalkyl, alkoxy, aryloxy, aralkoxy or cycloalkoxy groups, which groups are unsubstituted or inertly substituted, that is substituted by inert groups. Suitable halogens are chlorine, bromine, fluorine and iodine. R and R' together preferably have fewer than about 60 carbon atoms. When R and R' together form an inert cyclic structure, that structure is preferably a cyclohexyl ring having inert groups as substituents. Preferably, the weight percent oxirane oxygen in the epoxy compound is from 3 to 30, more preferably from 6 to 12 percent. Epoxy compounds having more than one epoxy group preferably have molecular weights of from 100 to 1000. Preferred epoxy compounds are epoxy compounds other than the alkylene oxides used in preparation of the polyether, more preferably different from ethylene oxide, propylene oxides and butylene oxides, and include other monoepoxy compounds and epoxy resins. Epoxy resins, that is molecules having at least two glycidyl groups and which readily cure with amines, are particularly preferred. The epoxy compounds are suitably used in amounts sufficient to reduce the acidity of the polyether. Preferably the epoxy compound is used in an amount of from 1 epoxy equivalent (eq)/10,000 Kg to 1 epoxy eq/10 Kg polyether, more preferably from 1 epoxy eq/2000 Kg polyether to 1 epoxy eq/50 kg polyether, most preferably, from 1 epoxy eq/1000 to 1 epoxy eq/100 Kg polyether. The term "epoxy equivalent" as used herein means that amount of epoxy compound which contains an average of one epoxy group. Contact of epoxy compound and polyether preferably occurs at a temperature sufficient for reaction of the epoxy compound to reduce acidity, but a temperature insufficient to result in undesirable degradation of the polyether. A sufficient temperature is preselected such that the acidity is reduced within a time acceptable for a specific application. Preferably, the temperature is from 0°C to about 150°C, more preferably from 50°C to 135°C, most preferably from 110° to 130°C. These temperatures are suitably maintained for a time sufficient for the epoxy compound to react with acid, preferably for at least about 1 minute, more preferably for a period of from 20 to 120 minutes. Conditions suitable for reaction of the hydroxy-functional polyether with the epoxy compound are preferably avoided. For instance, catalysts for the reaction of epoxy compounds with the hydroxy-functional polyethers are preferably substantially absent, that is, if present, the catalysts are present in insufficient quantities to result in reaction between the epoxy compounds and the hydroxy-functional polyethers (under the conditions of temperature and pressure to which the 10 polyether is exposed) which will interfere undesirably with acidity reduction or will measurably change physical properties of the polyether. According to the present invention, the epoxy ,,- compound and polyether are admixed by using any mixing device. Local concentrations of epoxy compound are advantageously avoided, conveniently by thorough mixing. The mixing can be carried out batchwise or continuously in accordance with procedures within the skill in the 20 art. Advantageously, in the described process, the epoxy compound is easily blended readily and intimately with the polyether. After treatment with the epoxy compound, the 25 polyether preferably has an acidity of less than about 5 ppm, more preferably less than about 1 ppm, most preferably less than about 0.1 ppm. Hydroxy-functional polyethers having the 30 concentration of unsaturated compounds, particularly propenyl ethers, reduced according to the practice of the invention are useful in preparing polyurethanes, particularly polyurethane foams which exhibit less scorch than do foams prepared from the same formulations but containing polyols not having their propenyl ether concentration so reduced. Such polyurethanes are referred to herein as scorch resistant polyurethanes. Furthermore, hydroxy-functional polyethers having both propenyl ether and acidity removed by the practice of the invention are similarly observed to be particularly useful in forming scorch resistant polyurethanes, preferably polyurethane foams. Compositions of the invention comprising hydroxy-functional polyethers and epoxy compounds are particularly useful for preparing scorch resistant polyurethanes, preferably foams. Relative scorch resistance, while generally subjective, is evident on visual observation by those skilled in the art. Preferably, a sample of an inner portion of a commercial scale foam is observed. Scorch is also measured colorimetrically. Those skilled in the art will recognize that the polyether purification processes of the invention are applicable as part of purification after polyether production or to purify polyethers which have propenyl ethers and/or acidity introduced by any means. The following examples are offered to illustrate the invention, but are not intended to limit it. In each example, percentages are in weight percent unless otherwise stated. Examples of the invention are designated numerically, while comparative samples are designated alphabetically. Example 1 REDUCTION OF PROPENYL ETHER IN A POLYETHER POLYOL USING A SULFONIC ACID ION EXCHANGE RESIN A sample of 100 Kg of a polyether polyol having an average molecular weight of about 3100 and prepared from about 13 weight percent ethylene oxide and 87 weight percent propylene oxide with glycerine as an initiator (which polyol sample contained about 0.49 weight percent water and about 0.0066 milliequivalents (meq) propenyl ether per gram (g) of polyol) was fed by a positive displacement pump at a rate of 23 milliliters/minute (ml/min.) through a steam-heated heat exchanger to raise the temperature from 25° to 85°C. The heated polyol was fed upward through a column of a water saturated (wet) gel-type polystyrene ion exchange resin which was crosslinked with about 10 weight percent divinylbenzene and sulfonated to 2.2 equivalents per liter of wet resin, to form a strongly acidic resin commercially available from The Dow Chemical Company under the trade designation DOWEX ® HGR-W2-H. The column was one inch (25.4 mm) in diameter, 8 feet (2.5 meters) long and was heated by an electrical heating tape to a temperature inside the column of 88°C. The column was loaded with 660 mL of the wet ion exchange resin. As the polyol passed through the ion exchange column, shrinkage of the ion exchange resin to about half its original volume was noted and was believed to be indicative of removal of water from the resin by the polyol. After the polyol passed through the column, its propenyl ether content was 0.00118 meq/g as determined by the method described in Quantitative Organic Analysis via Functional Groups by S.Siggia and J.G. Hanna, John Wiley and Sons, 1979 (reprinted 1988,Robert E. Krieger Pub.), p. 510-511. That method was also the one used to determine initial propenyl ether content. For the analysis, a sample expected to contain about 0.0001 mole of propenyl ether was weighed in a 250 ml flask containing 50 mL of aqueous hydroxylamine hydrochloric acid reagent to form a mixture. The mixture was heated with mixing until the reaction was complete, about 0.5 hr at 80°C. Upon completion of the reaction, the mixture was titrated potentiometrically with 0.1N sodium hydroxide using silver/silver chloride and glass electrodes. The end point was detected from the recorded pH and volume data. The reduction in propenyl ether shows that the acidic ion exchange resin is effective in reducing propenyl ether in a polyol. Examples 2-3 REDUCTION OF PROPENYL ETHER IN POLYETHER POLYOLS USING A SULFONIC ACID ION EXCHANGE RESIN The procedure used in Example 1 was repeated, using a glycerine initiated polyol having an average molecular weight of about 3500 and a composition of about 12 weight percent ethylene oxide units and 88 weight percent propylene oxide units in Example 2 and a glycerine initiated polypropylene polyol which was capped with about 14 weight percent ethylene oxide units and had an average molecular weight of about 4950 in Example 3. The ion exchange resin used in Example 1 was used in Examples 2 and 3. The propenyl ether content of the polyol of Example 2 was reduced from 0.0066 to 0.00065. The propenyl ether content of the polyol of Example 3 was reduced from 0.014 to 0.0026. These data (measured at 85-88°C), show that the acidic ion exchange resin treatment is effective in removing propenyl ether from a variety of polyols. Exa ple 4 REDUCTION OF PROPENYL ETHER IN POLYETHER POLYOLS USING A MACROPOROUS SULFONIC ACID ION EXCHANGE RESIN The procedure of Example 1 was repeated using as a polyether polyol having a molecular weight of about 3000 and prepared from about 93 weight percent propylene oxide and 7 weight percent ethylene oxide . A macroporous sulfonated polystyrene resin sulfonated to an exchange capacity of 1.6 eq/L on a wet basis was 10 used; the resin is commercially available from The Dow Chemical Company under the trade designation DOWEX ® MSC- 1-H. The propenyl ether content of the polyol of Example 4 was reduced from 0.0115 to 0.0051 when treated ,,- at a temperature of 70-85°C with a residence time of 7 min. Example 5 REDUCTION OF PROPENYL ETHER USING A WEAK ACID ION EXCHANGE RESIN 20 A gel-type weak acid resin composed of divinylbenzene and acrylic acid having an acid capacity of 3 eq/L on a wet basis commercially available from The Dow Chemical Company under the trade designation DOWEX ® 25 CCR-2 was mixed with 800 g of the polyol of Example 4 containing 0.02% water and was heated to 120°C. Samples are taken regularly and analyzed for propenyl ether as in Example 1. 30 The propenyl ether content of the polyol of Example 5 is reduced as shown below. Time Propenyl Ether Content (min.) (milliequivalents/gram) itial (o) 0.00903 2 0.00425 4 0.00391 6 0.00331 10 0.00262 20 0.00203 30 0.00199 The results of Examples 4-5 show that these forms of ion exchange resins are capable of catalyzing the hydrolysis of propenyl ethers. The weak acid resin requires higher temperature, and longer contact time. It is noted that the macroporous resin gives some discoloration (yellowing) at higher temperatures. Example 6, USE OF VARIOUS EPOXIDES TO FURTHER PURIFY POLYETHER POLYOLS About 500 g of the polyol of Example 1 was treated as in Example 1 using a resin of the composition of the resin used in Example 1, except that the resin had a 750 micron (micrometer) particle size and dispersity of approximately one rather than having particle sizes of from about 100 to about 700 microns (micrometers) with an average particle size of 400 microns (micrometers) as in Example 1. A product containing water, polyether polyol and propionaldehyde was produced after treatment. The product was also found to have trace amounts of acidity. The product was heated to 110°C at 10 torr to remove water and propionaldehyde. The resulting polyol had approximately 1 ppm of propionaldehyde and 500 ppm of water. Propionaldehyde levels were determined by gas chroraatography of the volatiles in the head space of a head space analysis vial, using the Hewlett Packard model HP-193 95A head space analyzer according to manufacturers' directions and using a 10 meter megabore capillary Carbowax ® column commercially available from Union Carbide Corp. Water levels were determined by a Karl Fischer titration as described in ASTM D2849-69, Sections 61-70, reapproved 1980. The resin-treated polyol was then heated to 85°C and the epoxy compounds indicated in Table 1 were added at the concentrations indicated in Table 1 to form mixtures. The mixtures were shaken for 15 minutes each and then were left undisturbed at 100°C for two hours. After the two hour period, the mixtures were cooled to room temperature, then a ten gram aliquot of each mixture was delivered into a headspace analysis vial, and analyzed as described previously. To each vial was added 15 microliters of 1-propenyl-2-hydroxy propyl ether. This enol ether had been found to adequately model propenyl ether end groups found in polyoxy- propylene glycols. In the presence of acids and water, the enol ether was converted into propionaldehyde and 1,2-propylene glycol. Measurements of propionaldehyde, therefore, indirectly indicated amounts of acid present. Each mixture was tightly capped and placed in a head space analyzer oven at 90°C for 18 hours. The head space was then analyzed for propionaldehyde by gas chromatography as were previous samples. Propionaldehyde generation is an indirect indication of the epoxy effectiveness in reacting with acids present. The epoxy compounds used were: Epoxidized soybean oil having 6 to 7 weight percent oxirane oxygen, (indicated as "ESO"), prepared by the epoxidation of soybean oil, and commercially available from the Viking Chemical Company under the trade designation of VIKOFLEX 7170; an epoxy resin which is the reaction product of Bisphenol A and two moles of epichlorohydrin, 10 commercially available from The Dow Chemical Company under the trade designation DOW EPOXY RESIN DER 330 (indicated as DER 330) having 9.5 weight percent oxirane oxygen; an epoxy resin which is the reaction product of « r- hexapropylene glycol and two moles of epichlorohydrin, commercially available from The Dow Chemical Company under the trade name DOW EPOXY RESIN DER 732 (indicated as DER 732) having 6 percent oxirane oxygen; an epoxy resin which is the reaction product of tripropylene 20 glycol and two moles of epichlorohydrin, commercially available from The Dow Chemical Company under the trade designation DOW EPOXY RESIN DER 736 (indicated as DER 736) having 8.8 percent oxirane oxygen; and (3,4- epoxycyclohexyl)methyl(3,4-epoxycyclohexyl)formate, 25 commercially available from the Union Carbide Corporation under the trade designation of ERL-4221 (indicated as ERL-4221 or 4221) having 12.7 weight percent oxirane oxygen. 30 Table 1 Amount of Propion¬ Epoxy Epoxy aldehyde Sample # Compound compound after Propion¬ Type used treatment aldehyde (ppm) (ppm) Reduction A (Control) — 0 56.2 B (Control) — 0 52.2 6:1 ESO 50 0.4 99.3 6:2 ESO 200 0.3 99.4 6:3 ESO 500 0.2 99.6 6:4 ESO 1000 0.2 99.6 6:5 DER-330 50 0.5 99.1 6:6 DER-330 200 0.5 99.1 6:7 DER-330 500 0.3 99.4 6:8 DER-330 1000 0.3 99.4 6:9 DER-732 50 0.5 99.1 6:10 DER-732 200 0.4 99.3 6:11 DER-732 500 0.3 99.4 6:12 DER-732 1000 0.3 99.4 6:13 DER-736 50 0.5 99.1 6:14 DER-736 200 0.5 99.1 6:15 DER-736 500 0.3 99.4 6:16 DER-736 1000 0.3 99.4 6:17 ERL-4221 50 0.4 99.3 6:18 ERL-4221 200 0.4 99.3 6:19 ERL-4221 500 0.2 99.6 6:20 ERL-4221 1000 0.2 99.6 The data in Table 1 indicates that PA generation is inhibited as much as 99.6% by addition of the epoxide compounds. Example 7. LARGER SCALE EPOXIDE TREATMENT Samples of the polyol of Example 1 treated with the ion exchange resin as described in Example 6 were treated with varying levels of the epoxy compounds indicated in Table 2 (as identified in Example 6) to form mixtures. To these mixtures were then added 1 or 5 weight percent (as indicated in Table 2) of a second polyol, the polyol of Example 3, which had not been treated with an ion exchange resin and contained known levels of propenyl ethers. The mixtures were aged for 43 hours at 50°C. Propionaldehyde concentration was measured as in Example 6 and results are shown in Table 2. Table 2 ppm t % of Sample Epoxy Epoxy wt. % propion¬ propion¬ # Type Level V-4701 aldehyde aldehyde Generation Reduction C(Control) — 0 1 2.2 — 7:1 DER 736 100 1 0.5 77.3 7:2 DER 736 500 1 0.3 86.4 7:3 DER 736 1000 1 0.2 90.9 D (Control) — 0 5 13.7 — 7:4 DER 736 100 5 0.4 97.1 7:5 DER 736 500 5 0.2 98.5 7:6 DER 736 1000 5 0.1 99.3 7:7 ERL-4221 100 1 0.7 68.2 7:8 ERL-4221 500 1 0.2 90.9 7:9 ERL-4221 1000 1 0.1 95.4 7:10 ERL-4221 100 5 0.2 98.5 7:11 ERL-4221 500 5 0.1 99.3 7:12 ERL-4221 1000 5 0.1 99.3 The data in Table 2 shows that acid catalyzed 5 propionaldehyde generation is reduced by addition of epoxy compounds to a polyether containing propenyl ethers. These results are consistent with those of the smaller scale samples in Example 6, wherein added 1- 0 propenyl, 2-hydroxy propyl ether provides model propenyl groups. Example 9: KINETIC DATA ON THE EPOXIDE TREATMENT OF ACID ION EXCHANGE TREATED POLYETHER POLYOLS A sample of the polyether polyol used in Example 1 and ion exchange treated as in Example 1 was heated to 100°C. with stirring and treated with 500 ppm of epoxy resin commercially available from the Dow Chemical Company under the trade designation, DOW EPOXY RESIN DER 736. Time t=0 was taken as the point of epoxy addition. At time periods ranging from 2 to 60 minutes, a 60 mL aliquots were taken from the mixture, 50 mL of each was titrated for acid (direct assessment of acid scavenging). To the remaining 10 mL was added 5% by wt. of the second polyol of Example 8 which was not treated with an ion exchange resin to act as a source of propionaldehyde (indirect assessment of acid scavenging). This sample was oven aged at 100°C. for 24 hours and then analyzed for propionaldehyde as in Example 7. Table 3 shows the results of these experiments. Table 3 Sample Temp. Time Titrated ppm °C (min. ) Acidity propion¬ (ppm) aldehyde 8:1 50 0 1.9 8:2 50 5 — 13.9 8:3 50 15 1.2 13.6 8:4 50 30 1.0 11.8 8:5 50 60 0.7 9.1 8:6 50 120 0.1 3.7 8:7 50 210 non- 2.4 detectable 8:8 100 2 0.8 16.5 8:9 100 5 non- 4.4 detectable 8:10 100 15 non- 1.1 detectable 8:11 100 30 non- 0.7 detectable 8:12 100 60 non- 0.0 detectable The data in Table 3 shows that acids are adequately removed by the epoxides at 100°C, as well as at 50°C, but more time is required at the lower temperature. Example 10: USE OF A COMMERCIAL SCALE ION EXCHANGE COLUMN An ion exchange column measuring 11 feet (3.35 meters) in diameter and 16 feet (4.9 meters) high was loaded with 400 cubic feet (11.2 m3) [equivalent to 200 ft3 (5.6 m3) of dry resin] of water saturated ion exchange resin of the type used in Example 1. The polyol of Example 2, having a water content of 0.5 weight percent, was flowed upward through the column at a rate of 100 gallons (379 liters) per minute while a temperature of 85°C was maintained. This flow rate allows a contact time of 15 minutes. This flow was maintained for 5 days, then the polyol was changed to the polyol of Example 1, but other conditions were kept constant. Samples of polyol entering and exiting the column were taken daily and analyzed for propenyl ethers as in Example 1. The results are tabulated in Table 4. Table 4 Propenyl Propenyl Time ethers ethers (days) meq/gm meq/gm Conv (in) (out) 1 0.005 0.00203 59 2 0.00384 0.0007 82 3 0.0038 0.0006 84 4 0.00431 0.0006 86 5 0.0035 0.0006 83 6 0.0033 0.0006 82 7 0.00342 0.0006 82 8 0.00363 0.0007 81 9 0.00345 0.0006 83 10 0.00354 0.0007 80 These data show that ion exchange treatment is effective in reducing propenyl ether concentration on a large scale for at least 10 days.

Claims: 1. A process for reducing the concentration of propenyl ethers in a hydroxy-functional polyether having oxypropylene units comprising the step of contacting the polyether with an acid ion exchange resin for a time and at a temperature sufficient for the conversion of at least some of the propenyl ethers to propionaldehyde and in the presence of sufficient water for the conversion. 2. A process as claimed in Claim 1 further comprising the step of treating the polyether with an epoxy compound in an amount sufficient to reduce the acidity of the polyol. 3. A process as claimed in Claim 1 wherein the acid ion exchange resin is prepared from a mixture of styrene and divinylbenzene, the divinylbenzene being present in an amount of from 5 to 15 weight percent based on mixture weight. 4. A process as claimed in Claim 1 wherein the step of contacting the polyether with an acid ion exchange resin takes place in the presence of from 0.5 to 2 weight percent water based on polyether, at a temperature of from 50 to 125°C, with an upward flow of polyether through the resin and with at least a 30 second contact time between resin and polyether. 5. A process as claimed in Claim 2 wherein the epoxy compound has an oxirane oxygen content of from 3 to 30 weight percent and a molecular weight of from 100 to 1000. 6. A process as claimed in Claim 2 wherein the epoxy compound is used in an amount of from 1 epoxy equivalent/10,000 kg polyether to 1 epoxy equivalent/10 kg polyether. 7. A process for reducing the concentration of propenyl ethers in a hydroxy-functional polyether having oxypropylene units comprising the step of contacting the polyether with a gel-type sulfonic acid ion exchange resin having an aqueous exchange capacity of from 0.5 to 5 equivalents/liter of wet resin for a time and at a temperature sufficient for the conversion of at least some of the the propenyl ethers to propionaldehyde and in the presence of sufficient water for the conversion. 8. A process as claimed in Claim 7 wherein the step of contacting the polyether with a gel-type sulfonic acid ion exchange resin takes place in the presence of from 0.5 to 2 weight percent water based on polyether, at a temperature of from about 50 to about 125°C, with an upward flow of polyether through the resin and with at least a 30 second contact time between resin and polyether. 9. A process for reducing the acidity of a hydroxy-functional polyether comprising the step of treating the polyether with an epoxy compound in an amount sufficient to reduce the acidity of the polyether. 10. A composition comprising (a) a hydroxy-functional polyether which is the polymerization product of propylene oxide or a mixture of propylene oxide and an alkylene oxide selected from ethylene oxide, butylene oxide and mixtures thereof in the presence of an initiator; and (b) at least one epoxy compound different from ethylene oxide, propylene oxide and butylene oxide.

Inventors: BETTGE PAUL D, CHAVEZ JOHNNY JR, FARNUM ANDREW S, FRIEDLI HANS R, KENT VAN A, NACE VAUGHN M, PLEPYS RAYMOND A, WHITEMIRE RANDALL K, BETTGE, PAUL, D., CHAVEZ, JOHNNY, JR., FARNUM, ANDREW, S., FRIEDLI, HANS, R., KENT, VAN, A., NACE, VAUGHN, M., PLEPYS, RAYMOND, A., WHITEMIRE, RANDALL, K.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1990
Main classification: C07C47
IPC codes: B01J31, C07B61, C07C41, C07C43, C07C45, C07C47, C08G65