Process for forming a deposited film by use of alkyl aluminum hydride and process for preparing semiconductor device

Abstract: In forming a deposited film composed mainly of Al according to the CVD method utilizing gas of alkyl aluminum hydride, hydrogen gas, and if desired, further gas containing Si atoms, film formation is carried out by shifting the deposition rate from a low deposition rate to a high deposition rate. According to this method, excellent selectivity is exhibited and also a film excellent in flatness can be deposited at a high deposition rate.

Description: BACKGROUND OF THE INVENTION Field of the Invention This invention relates to a process for forming a deposited film, particularly a process for forming a deposited film composed mainly of Al which can be preferably applied to electrodes or wiring of a semiconductor integrated circuit device, etc. and to a process for preparing a semiconductor device. Related Background Art In the prior art, in electronic devices or integrated circuits by use of semiconductors, for electrodes and wiring, aluminum (Al) or a metal containing aluminum as main component such as Al-Si and the like has been primarily used. Al has many advantages such that it is inexpensive and high in electroconductivity, that it can be also internally chemically protected because a dense oxidized film can be formed on the surface, and that it has good adhesion to Si, etc. As the method for forming a film for electrodes and wiring of Al or Al-Si as mentioned above, there has been used in the prior art the sputtering method such as magnetron sputtering, etc. However, selective deposition and selective growth can not be realized by the sputtering method which has been used in the prior art. The sputtering is the physical deposition method based on flying of sputtered particles in vacuum, the film thickness at the stepped portion or the insulating film side wall becomes extremely thin, leading to wire breaking in an extreme case. Nonuniformity of film thickness or wire breaking has the drawback that reliability of LSI is markedly lowered. On the other hand, since the integration degree of the integrated circuit such as LSI, etc. is increased, and fine formation of wiring or multi-layer wiring has been particularly required in recent years, there is an increasing severe demand not found up to date for Al or Al-Si wiring of the prior art. With finer dimensional formation by increased integration degree, the surface of LSI, etc. is subject to excessive unevenness due to oxidation, diffusion, thin film deposition, and etching, etc. For example, electrodes or wiring metal must be deposited on the surface with a stepped difference, or deposited in a via-hole which is fine in diameter and deep. In 4 Mbit or 16 Mbit DRAM (dynamic RAM), etc., the aspect ratio (via-hole depth/via-hole diameter) of via-hole in which a metal composed mainly of Al such as Al-Si, etc. is to be deposited is 1.0 or more, and the via-hole diameter itself also becomes 1 µm or less. Therefore, even for a via-hole with large aspect ratio, the technique which can deposit an Al-Si compound is required. Particularly, for performing sure electrical connection to the device under insulating film such as SiO₂, etc., rather than film formation, Al-Si is required to be deposited so as to embed only the via-hole of the device. In such case, a method of depositing an Al alloy only on Si or metal surface and not depositing it on an insulating film such as SiO₂, etc. is required. As the improved sputtering method, there has been developed the bias sputtering method in which a bias is applied on a substrate and deposition is performed so as to embed Al or an Al-Si compound only in the via-hole by utilizing the sputter etching action and the deposition action on the substrate surface. However, since the bias voltage of some 100 V or higher is applied on the substrate, deleterious influence on the device occurs because of charged particle damaging such as change in threshold of MOS-FET, etc. Also, because of presence of both etching action and deposition action, there is the problem that the deposition speed cannot be essentially improved. In order to solve the problems as described above, various types of CVD (Chemical Vapor Deposition) methods have been proposed. In these methods, chemical reaction of the starting gas in some form is utilized. In plasma CVD or optical CVD, decomposition of the starting gas occurs in gas phase, and the active species formed there further reacts on the substrate to give rise to film formation. In these CVD methods, surface coverage on unevenness on the substrate surface is good. However, carbon atoms contained in the starting gas molecule are incorporated into the film. Also, particularly in plasma CVD, the problem remained that there was damage by charged particles (so called plasma damage) as in the case of the sputtering method. The thermal CVD method, in which the film grows through the surface reaction primarily on the substrate surface, is good in surface coverage on unevenness such as stepped portion of the surface, etc. Also, it can be expected that deposition within via-hole will readily occur. Further, wire breaking at the stepped portion can be avoided. Furthermore, there are not caused damages by charged particles which have been observed in the case of the plasma CVD or the sputtering method. The methods of such a kind include, for example, the method seen in Journal of Electrochemical Society, Vol. 131, p. 2175 (1984). In this method triisobutyl aluminum (i-C₄H₉)₃Al (TIBA) is used as organic aluminum gas and an Al film is formed at a film formation temperature of 260 °C and a reaction tube pressure of 0.5 Torr. The substrate temperature is then maintained at about 450°C and SiH₄ is introduced to diffuse Si in the Al film, thus obtaining an Al-Si film. When TIBA is to be used, a continuous film can not be obtained unless pretreatment is effected in which prior to film formation, TiCl₄ is flowed to activate the substrate surface to form nuclei. Furthermore, in case where TIBA is used, there is a problem that surface flatness is not sufficient even when TiCl₄ is used. By this method it is not possible to effect selective growth such as Al-Si deposition only in via-holes. As another method, there can be mentioned the method described in Japanese Journal of Applied Physics, Vol. 27, No. 11, p. L2134 (1988). In this method, TIBA and Si₂H₆ diluted with Ar gas are supplied, and the gases are heated before TIBA reaches the substrate. By this method, an Al-Si film of a low resistivity can be epitaxially grown on a Si (100) wafer. Although the film obtained by this method has good high quality, there are involved the problems that control is difficult due to necessity of heating the gases and that apparatus for effecting this method is complicated. Japanese Laid-Open Patent Application No. 63-33569 describes a method of forming a film by using no TiCl₄, but using in place thereof organic aluminum and heating it in the vicinity of the substrate. According to this method, Al can be deposited selectively only on the metal or semiconductor surface from which the naturally oxidized film has been removed. In this case, it is clearly stated that the step of removing the naturally oxidized film on the substrate surface is necessary before introduction of TIBA. Also, it is described that, since TIBA can be used alone, no carrier gas is required to be used, but Ar gas may be also used as the carrier gas. However, the reaction of TIBA with another gas (e.g. H₂) is not contemplated at all, and there is no description of use of H₂ as the carrier gas. Also, in addition to TIBA, trimethyl aluminum (TMA) and triethyl aluminum (TEA) are mentioned, but there is no specific description of other organic metals. This is because, since the chemical properties of organic metals generally vary greatly if the organic substituent attached to the metal element varies little, it is necessary to investigate individually by detailed experimentation to determine what organic metal should be used. In the CVD method as described above, not only there is an inconvenience that the naturally oxidized film must be removed, but also there is the drawback that no surface smoothness can be obtained. Also, there is the restriction that heating of the gas is necessary, and yet heating must be done in the vicinity of the substrate. Besides, it must also be experimentally determined at what poximity to the substrate heating must be done, whereby there is also the problem that the place for setting the heater cannot be necessarily freely chosen. In the pre-text of the 2nd Symposium of Electrochemical Society, Branch of Japan (July 7, 1989), on page 75, there is a description of film formation of Al according to the double wall CVD method. In this method, TIBA is used and the device is designed so that the gas temperature of TBA can be made higher than the substrate temperature. This method may be also regarded as a modification of the above-mentioned Japanese Laid-open Patent Application No. 63-33569. Also in this method, Al can be selectively grown only on a metal or semiconductor, but not only the difference between the gas temperature and the substrate surface temperature can be controlled with difficulty, but also there is the drawback that the bomb and the pipeline must be heated. Moreover, according to this method, there are involved such problems that no uniform continuous film can be formed, that flatness of the film is poor, etc., unless the film is made thick to some extent. As set forth above, the prior art methods have the problems to be solved that it is difficult to obtain a flat Al-Si film of a low resistivity and good quality, that there is considerable limitation in apparatus and in film formation. As described above, prior art methods cannot necessarily effect well selective growth of Al-Si, and even if possible, there is a problem with respect to flatness, resistance, purity, etc. of the Al film formed. Also, there has been involved the problem that the film formation method is complicated and can be controlled with difficulty. Furthermore, according to the prior art as described above high throughput sufficient to get a final commercial success has not been achieved. As described above, in the technical field of semiconductors in which higher integration has been desired in recent years, in order to provide inexpensively semiconductor devices which are made highly integrated and of high performance, there exists much room for improvement. SUMMARY OF THE INVENTION The present invention provides a process for forming a deposited film having the features set out in claim 1 of the accompanying claims. The method of the invention is controllable, does not require an expensive and complicated film formation device, is of extremely wide and general applicability, and can form a high quality metal film which can be used in the manufacture of semiconductor devices. The deposition rate of the aluminum can be adjusted during film formation and a dense Al or Al-Si film can be formed on a substrate at high speed. There may be provided a substrate (A) which has a surface of a metal, a semiconductor, or a thin oxidised film provided on a metal or semiconductor, and also having an electron non-donative surface (B) on which the film does not deposit, the electron non-donative surface being of silicon oxide, glass or silicon nitride. A dense Al or Al-Si film can be formed at high speed selectively on the electron donative surface (A) of the substrate. A paper by H. O. Pierson, "Aluminum Coatings by the Decomposition of Alkyls", Thin Solid Films, Vol. 45, pages 257-263 (1977) discloses the formation of aluminum on steel by chemical vapour deposition using diisobutyl aluminum hydride and diethyl aluminum hydride. This paper is unrelated to the field of semiconductor manufacture, and there is no disclosure of varying the speed of deposition of the aluminum in the manner now claimed. A paper by Hanabusa et al , "Photochemical Vapour Deposition of Aluminum Thin Films using Dimethyl Aluminium Hydride", Japanese Journal of Applied Physics, Vol. 27, No 8, August 1988, Tokyo, Japan, pages 1392-1394 discloses the deposition of aluminum films from dimethyl aluminum hydride by photo-CVD. However, this document neither discloses nor suggests chemical vapour deposition brought about by reaction with hydrogen, and there is no disclosure of varying the deposition speed in the manner now claimed. These objects are achieved in accordance with the invention by providing a process for forming a deposited film comprising the steps of: (a) providing a substrate having an electron donative surface in a space for formation of the deposited film; (b) introducing a gas of an alkyl aluminum hydride and hydrogen gas into said space for formation of deposited film; and (c) maintaining the temperature of said electron donative surface within the range of from the decomposition temperature of said alkyl aluminum hydride to 450 °C to form an aluminum film on said electron donative surface while varying the deposition speed of aluminum. These objects are also achieved in accordance with the invention by providing a process for forming a deposited film comprising the steps of: (a) providing a substrate having an electron donative surface in a space for formation of the deposited film; (b) introducing a gas of an alkyl aluminum hydride, a gas containing silicon and hydrogen gas into said space for formation of deposited film; and (c) maintaining the temperature of said electron donative surface within the range of from the decomposition temperature of said alkyl aluminum hydride to 450 °C to form an aluminum-silicon film on said electron donative surface while varying the deposition speed of aluminum. In the present invention, Al or Al-Si film is formed by feeding a gas of an alkyl aluminum hydride, or a gas of an alkyl aluminum hydride together with a gas containing silicon. In addition, the deposition rate of Al is shifted during film formation. Accordingly, a dense Al or Al-Si film can be formed on a substrate at high speed. These objects are also achieved in accordance with the invention by providing a process for forming a deposited film comprising the steps of: (a) providing a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for formation of the deposited film; (b) introducing a gas of an alkyl aluminum hydride and hydrogen gas into said space for formation of deposited film; and (c) maintaining the temperature of said electron donative surface (A) within the range of from the decomposition temperature of said alkyl aluminum hydride to 450 o C to form an aluminum film selectively on said electron donative surface (A) while varying the deposition speed of aluminum. These objects are also achieved in accordance with the invention by providing a process for forming a deposited film comprising the steps of: (a) providing a substrate having an electron donative surface (A) and an electron non-donative surface (B) in a space for formation of the deposited film; (b) introducing a gas of an alkyl aluminum hydride, a gas containing silicon and hydrogen gas into said space for formation of deposited film; and (c) maintaining the temperature of said electron donative surface (A) within the range of from the decomposition temperature of said alkyl aluminum hydride to 450 °C to form an aluminum-silicon film selectively on said electron donative surface (A) while varying the deposition speed of aluminum. In the present invention, by feeding a gas of an alkyl aluminum hydride or a gas of an alkyl aluminum hydride together with a gas containing silicon onto a substrate having an electron donative surface (A) and a non-electron donative surface (B), Al or Al-Si film is formed only on the electron donative surface (A), shifting the deposition rate of Al during film formation. Accordingly, a dense Al or Al-Si film can be formed at high speed only on the electron donative surface (A) on the substrate. BRIEF DESCRIPTION OF THE DRAWINGS Figs. 1A - 1D are schematic sectional views for illustration of the deposited film forming process according to one embodiment of the present invention. Figs. 2 and 3 are schematic views for illustration of a suitable deposited film forming device in practicing the deposited film forming process according to the process of the present invention. Figs. 4A - 4E are schematic sectional views for illustration of the deposited film forming process according to one embodiment of the present invention. Fig. 5 is a chart showing the X-ray diffraction pattern on the Al deposited Si (111) substrate having Al deposited. Figs. 6A and 68 are charts showing the X-ray diffraction pattern. Fig. 7 is a chart showing the X-ray diffraction pattern on the Al deposited Si (100) substrate. Fig. 8 is a schematic view for illustration of the scanning µ-RHEED. Fig. 9 is a schematic view for illustration of the principle of crystal grain observation with the scanning µ-RHEED image. Fig. 10 is a chart showing the X-ray diffraction pattern on the Al deposited Si (111) substrate. Figs. 11A - 11C are schematic views of the scanning secondary electron image, and the scanning µ-RHEED image of the Al film selectively deposited on Si(111) substrate. Fig. 12 is a chart showing the X-ray diffraction pattern on the Al deposited Si (100) substrate. Figs. 13A - 13C are schematic views of the scanning secondary electron image and the scanning µ-RHEED image of the Al film selectively deposited on Si (100) substrate. Figs. 14A - 14E are schematic views showing one embodiment of formation of a source drain electrode of gate insulation type transistor. Figs. 15A - 15D are illustrations for explaining the reaction mechanism. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Preferred embodiments according to the present invention are described in detail below, but the present invention is not limited by these embodiments, and it may have a constitution which accomplishes the object of the present invention. In the following, prior to detailed description, first, the process for forming a deposited film by use of an organic metal is outlined. The decomposition reaction of an organic metal, and hence the thin film deposition reaction will vary greatly depending on the kind of the metal atom, the kind of the alkyl bonded to the metal atom, the means of causing the decomposition reaction to occur, the atmospheric gas, etc. For example, in the case of M-R₃ (M: the group III metal, R: alkyl group), trimethyl gallium: in thermal decomposition undergoes radical cleavage wherein Ga-CH₃ bond is cleaved, while triethyl gallium: in thermal decomposition is decomposed through β-elimination into: and C₂H₄. On the other hand, triethyl aluminum attached with the same ethyl group: in thermal decomposition undergoes radical decomposition in which Al-C₂H₅ is cleaved. However, tri-iso-butyl aluminum having iC₄H₉ bonded therein: is subject to β-elimination. Trimethyl aluminum (TMA) comprising CH₃ groups and Al has a dimer structure at room temperature: and thermal decomposition is radical decomposition in which Al-CH₃ group is cleaved, and at a temperature of 150 °C or lower, it reacts with atmospheric H₂ to form CH₄, and forms finally Al. However, at a high temperature of 300 o C or higher, even if H₂ may be present in the atmosphere, CH₃ group will withdraw H from the TMA molecule, until finally Al-C compound is formed. Also, in the case of TMA, in light or a certain region controlled in electric power in H₂ atmosphere high frequency (ca. 13.56 MHz) plasma, C₂H₆ will be formed by the bridging CH₃ between two Al's. In essence, since even an organic metal comprising CH₃ group which the simplest alkyl group, C₂H₅ group or iC₄H₉ group and Al or Ga has a reaction mode depending on the kind of the alkyl group, the kind of the metal atom, the excitation decomposition means, for deposition of a metal atom from an organic metal on a desired substrate, the decomposition reaction must be strictly controlled. For example, when Al is to be deposited from triisobutyl aluminum: in the low pressure CVD method comprising mainly thermal reaction, unevenness of µm order is formed on the surface, whereby the surface morphology is inferior. Also, hillock generation by heat treatment, Si surface roughening through Si diffusion at the interface between Al and Si occur, and also migration resistance is inferior, whereby it can be utilized for ultra-LSI process with difficulty. For this reason, a method for controlling precisely both the gas temperature and the substrate temperature has been attempted. However, the device is complicated, and the method is of the sheet treatment type in which deposition can be effected only on one wafer by one deposition process. Besides, since the deposition speed is 500 Å/min. at the highest, the throughput necessary for bulk production cannot be realized. Similarly, when TMA is employed, Al deposition has been attempted by use of plasma or light, the device also becomes complicated due to use of plasma or light, and also because of the sheet type device, there remains room for improvement for sufficient improvement of throughput. Dimethyl aluminum hydride (DMAH) as the alkyl aluminum hydride to be utilized in the present invention is a substance known as alkyl metal, but it could not be estimated at all what Al thin film could be deposited depending on what reaction mode, unless deposited films are formed under all the conditions. For example, in an example of deposition Al by optical CVD from DMAH, the surface morphology is inferior, and the resistivity value was greater than the bulk value (2.7 µohm·cm) as several µohm to 10 µohm·cm, thus being inferior in film quality. Now, referring to the drawings, preferred embodiments of the present invention are described in more detail. In the present invention, for depositing an Al-Si film of good quality as the electroconductive deposition film on a substrate, the CVD method is used. More specifically, by use of dimethyl aluminum hydride (DMAH): or monomethyl aluminum hydride (MMAH₂): as alkyl aluminum hydride which is an organic metal as the starting gas containing at least one atom which becomes the constituent of the deposited film, optionally a gas containing Si atoms as the starting gas and H₂ as the reaction gas, an Al-Si film is formed by gas phase growth with a gas mixture of these on a substrate. As the substrate applicable in the present invention, a material having electron donative property may be employed. The electron donative material is described in detail below. The electron donative material refers to one having free electrons existing or free electrons intentionally formed in the substrate, for example, a material having a surface on which the chemical reaction is promoted through give-and-take of electrons with the starting gas molecules attached on the substrate surface. For example, generally metals and semiconductors such as P type, N type and intrinsic semiconductor etc. correspond to such material. Those having very thin oxidized film on the metal or semiconductor surface are also included. For, with such thin film, the chemical reaction can occur between the substrate and the attached starting molecules. Specifically, there may be included semiconductors such as monocrystalline silicon, polycrystalline silicon, amorphous silicon, etc., binary system or ternary system or quaternary system III-V compound semiconductors comprising combinations of Ga, In, Al as the group III element and P, As, N as the group V element, or II-IV compound semiconducters, or metals themselves such as tungsten, molybdenum, tantalum, aluminum, titanium, copper, etc., or silicides of the above metals such as tungsten silicide, molybdenum silicide, tantalum silicide, aluminum silicide, titanium silicide, etc., further metals containing either one of the constituent of the above metals such as aluminum silicon, aluminum titanium, aluminum copper, aluminum tantalum, aluminum silicon copper, aluminum silicon titanium, aluminum palladium, titanium nitride, etc. On the substrate with such constitution, Al is deposited only through simple thermal reaction in the reaction system of the starting gas and H₂. For example, the thermal reaction in the reaction system between DMAH and H₂ may be basically considered as follows: DMAH assumes a dimer structure at room temperature. Also, with MMAH₂, a high quality Al film could be formed by thermal reaction as shown below in Examples. Since MMAH₂ has low vapor pressure as 0.01 to 0.1 Torr at room temperature, a large amount of the starting material can be transported with difficulty, and the upper limit value of the deposition speed is several hundred Å/min. in the present embodiment, and preferably, it is most desirable to use DMAH of which vapor pressure is 1 Torr at room temperature. In another embodiment of the present invention, the CVD method is used for selective deposition of a good metal film as the electroconductive deposition film on the substrate. More specifically, as described above, by use of dimethyl aluminum hydride (DMAH) or monomethyl aluminum hydride (MMAH₂), optionally a gas containing Si atoms as the starting gas and H₂ as the reaction gas, a metal film is selectively formed on the substrate by gas phase growth with a gas mixture of these. The substrate applicable in the present invention has a first substrate surface material for formation of the surface on which a metal is deposited, and a second substrate surface material on which no metal is deposited. And, as the first substrate surface material, a material having the electron donative surface is used. In contrast, as the material for forming the surface on which pure Al or Al-Si is not deposited selectively, namely the material for forming the electron non-donative surface, conventional insulating materials, oxidized silicon formed by thermal oxidation, CVD, etc., glass or oxidized film such as BSG, PSG, BPSG, etc., thermally nitrided film, silicon nitrided film by plasma CVD, low pressure CVD, ECR-CVD method, etc. Figs. 1A - 1D show how the pure Al or Al-Si film according to the present invention is grown. Fig. 1A is an illustration showing schematically the cross-section of the substrate before formation of the pure Al deposited film according to the present invention. 90 is the substrate comprising an electron donative material. When DMAH, optionally together with Si₂H₆ as starting gas and gas mixture containing H₂ as reaction gas are fed onto the substrate 1 heated under the first deposition condition, pure Al or Al-Si is precipitated on the substrate 90 to form the continuous film of pure Al or Al-Si as shown Fig. 1B. Further deposition of Al-Si is continued under the second deposition condition to obtain Al-Si film as shown in Fig. 1D via the state of Fig. 1C. As the result of analysis according to Auger's electron spectroscopy or photoelectric spectroscopy, no entrainment of an impurity such as carbon or oxygen is recognized in this film. The deposited film thus formed has a resistivity of, for example, with a film thickness of 400 Å, 2.7 - 3.0 µohm·cm at room temperature which is substantially equal to the bulk resistivity of Al, and becomes continuous and flat film. Also, even with a film thickness of 1 µm, its resistance at room temperature is approximately 2.7 - 3.0 µohm·cm and a sufficiently dense film is formed with a relatively thicker film. The reflectance in the visible wavelength region is approximately 80 %, and a thin film with excellent surface flatness can be deposited. As described in detail above, in the present invention, in addition to the finding of depositing pure Al on an electron donative surface (A) by maintaining the electron donative surface at a temperature between of the decomposition temperature of an alkyl aluminum hydride and 450 °C in a gas mixture atmosphere of a gas of an alkyl aluminum hydride, particularly an alkyl aluminum hydride containing methyl group and the hydrogen gas, or depositing Al-Si by use of the above-mentioned gas mixture atmosphere in which a gas containing Si is further added, for effecting higher through-put in formation of pure Al or Al-Si film, during the deposited film formation, shift from the low deposition rate to the high deposition rate is effected. By doing so, higher through-put can be accomplished without lowering film quality. Fig. 2 is a schematic view showing a preferable deposition film forming device for applying the present invention. Here, 1 is a substrate for forming an Al-Si film. The substrate 1 is mounted on a substrate holder 3 provided internally of the reaction tube 2 for forming a space for formation of a deposited film which is substantially closed to Fig. 2. As the material constituting the reaction tube 2, quartz is preferable, but it may be also made of a metal. In this case, it is preferable to cool the reaction tube. The substrate holder 3 is made of a metal, and is provided with a heater 4 so that the substrate mounted thereon can be heated. And, the constitution is made so that the substrate temperature can be controlled by controlling the heat generation temperature of the heater 4. The feeding system of gases is constituted as described below. 5 is a gas mixer, in which the first starting gas, the second starting gas and the reaction gas are mixed, and the mixture is fed into the reaciton tube 2. 6 is a starting gas gasifier provided for gasification of an organic metal as the first starting gas. The organic metal to be used in the present invention is liquid at room temperature, and is formed into saturated vapor by passing a carrier gas through the liquid of the organic metal within the gasifier 6, which is in turn introduced into the mixer 5. The evacuation is constituted as described below. 7 is a gate valve, which is opened when performing evacuation of a large volume such as during evacuation internally of the reaction tube 2 before formation of the deposited film. 8 is a slow leak valve, which is used when performing evacuation of a small volume such as in controlling the pressure internally of the reaction tube 2 during formation of the deposited film. 9 is an evacuation unit, which is constituted of a pump for evacuation such as turbo molecular pump, etc. The conveying system of the substrate 1 is constituted as described below. 10 is a substrate conveying chamber which can house the substrate before and after formation of the deposited film, which is evacuated by opening the valve 11. 12 is an evacuation unit for evacuating the conveying chamber, which is constituted of a pump for evacuation such as turbo molecular pump, etc. The valve 13 is opened only when the substrate 1 is transferred between the reaction chamber and the conveying space. As shown in Fig. 1, in the starting gas gasifier 6 which is the gas formation chamber for forming the starting gas, the liquid DMAH maintained at room temperature is bubbled with H₂ or Ar (or other inert gas) as the carrier gas to form gaseous DMAH, which is transported to the mixer 5. The H₂ gas as the reaction gas is transported through another route into the mixer 5. The gases are controlled in flow rates so that the respective partial pressures may become desired values. In the case of forming a film by this device, the first starting gas may be of course MMAH₂, but DMAH with a vapor pressure enough to become 1 Torr at room temperature is the most preferred. Also, DMAH and MMAH₂ may be used in a mixture. As the second starting gas containing Si, there can be used Si₂H₆, SiH₄, Si₃H₈, Si(CH₃)₄, SiCl₄, SiH₂Cl₂ and SiH₃Cl. Of these compounds, Si₂H₆ which can be easily decomposed at the low temperature of 200 - 300°C. The gases such as Si₂H₆ are diluted with H₂ or Ar and transported to the mixer 5 through a system other than the DMAH system. The deposited film formed at a substrate temperature of 160 °C to 450 °C by use of such starting gas and reaction gas, with a thickness of for example 400 Å, has a resistivity at room temperature of 2.7 - 3.0 µohm·cm which is substantially equal to Al bulk resistivity, and is a continuous and flat film. At this time, the pressure during film formation can be chosen within the range from 10⁻³ Torr to 760 Torr. Also, even when the film thickness may be 1 µm, its resistivity is ca. 2.7 - 3.0 µohm·cm, and a sufficiently dense film can be formed also with a relatively thicker film. Also, the reflectance in the visible light wavelength region is approximately 80 %, whereby a thin film excellent in surface flatness can be deposited. The substrate temperature is desirably the decomposition temperature of the starting gas containing Al or higher, and 450 °C or lower as described above, but specifically the substrate temperature of 200 to 450 °C is more desirable, and when deposition is carried out under this condition, by making the DMAH partial pressure 10⁻⁴ to 10⁻³ Torr, the deposition speed becomes very great as 100 Å/min. to 800 Å/min., whereby sufficient great deposition speed corresponding to the cost as the Al-Si deposition technique for ultra-LSI can be obtained. A more preferable substrate temperature condition is 270 °C to 350 °C, and the Al-Si film deposited under this condition is also strongly orientatable and, even when subjected to the heat treatment at 450 °C for 1 hour, the Al-Si film on the Si monocrystalline or Si polycrystalline substrate becomes a good Al-Si film without generation of hillock, spike as seen in the film forming method of the prior art. Also, such Al-Si film is excellent in electro-migration resistance. In the device shown in Fig. 2, Al-Si can be deposited on only one sheet of substrate in deposition for one time. Although a deposition speed of ca. 800 Å/min. can be obtained, it is still insufficient for performing deposition of a large number of sheets within a short time. As the deposition film forming device for improving this point, there is the low pressure CVD device which can deposit Al-Si by simultaneous mounting of a large number of sheets of wafer. Since the Al-Si film formation according to the present invention utilizes the surface reaction on the electron donative substrate surface, in the hot wall type low pressure CVD method wherein only the substrate is heated, Al-Si compound containing 0.5 - 2.0 % of Si can be deposited on the substrate by use of DMAH and H₂ and the Si starting gas such as Si₂H₆, etc. The reaction tube pressure may be 0.05 to 760 Torr, desirably 0.1 to 0.8 Torr, the substrate temperature 160 °C to 450 °C, desirably 200 °C to 400 °C, the DMAH partial pressure 1 x 10⁻⁵-fold to 1.3 x 10⁻³-fold of the pressure in the reaction tube, the Si₂H₆ partial pressure 1 x 10⁻⁷ -fold to 1 x 10⁻⁴-fold of the pressure in the reaction tube, and under such conditions, Al-Si can be well deposited on the electron donative substrate. Fig. 3 is a schematic illustration showing a deposited film forming device to which such present invention is applicable. 57 is a substrate for formation of Al-Si film. 50 is an outside reaction tube made of quartz for forming a space for formation of deposited film substantially closed to the surrounding, 51 an innerside reaction tube made of quartz located for separating the flow of gas within the outside reaction tube 50, 54 a flange made of a metal for opening and closing of the opening of the outside reaction tube 50, and the substrate 57 is located within the substrate holding member 56 provided internally of the innerside reaction tube 51. The substrate holding member 56 should be preferably made of quartz. Also, in the present device, the substrate temperature can be controlled by the heater portion 59. The pressure internally of the reaction tube 50 is constituted so as to be controllable by the evacuation system connected through the gas evacuation outlet 53. The gas feeding system is constituted to have a first gas system, a second gas system, a third gas system and a mixer (none are shown in Fig. 3) similarly as the device shown by the symbols 5 and 6 in Fig. 2, and the starting gases and the reaction gas are introduced into the reaction tube 50 through the starting gas inlet 52. These gases react on the surface of the substrate 57 during passage internally of the innerside reaction tube 51 as shown by the arrowhead 58 in Fig. 3 to deposit Al-Si on the substrate surface. The gases after the reaction pass through the gap formed between the innerside reaction tube 51 and the outside reaction tube 50, and evacuated through the gas evacuation outlet 53. In taking out and in the substrate, the flange 54 made of a metal is permitted to fall by an elevator (not shown) together with the substrate holding member 56 and the substrate 57 to be moved to a predetermined position where the substrate is mounted and detached. By forming a deposited film under the conditions as described above by use of such device, Al-Si films of good quality can be formed in all the wafers within the device. When depositing Al-Si by use of the device shown in Fig. 2, as an example, under the conditions of; Torr pressure: 1.5 Torr DMAH partial pressure: 1.5 x 10⁻⁴ Torr Si containing gas partial pressure: 2.0 x 10⁻⁶ Torr Substrate temperature: 160 °C - 450 °C, an Al-Si film can be deposited on the electron donative material surface. Even with a film thickness of 400 Å, the film is continuous and its resistivity is 2.7 - 3.0 µΩ·cm which substantially equal to the bulk value of Al. When the substrate temperature is 270 °C - 350 °C, the deposition rate is 100 - 800 Å/min., and for high speed deposition, the deposition rate is required to be made larger. In the case of depositing pure Al, silicon containing gas is omitted. For realizing high speed deposition, it may be conceivable to make the substrate temperature higher and DMAH partial pressure higher. For example, by making the substrate temperature 330 °C, and the DMAH partial pressure 10⁻² to 10⁻³ Torr, a deposition rate of 0.2 to 0.5 µm/min. can be realized. However, if the deposition rate is too large, the probability becomes higher that a surface inferior in surface flatness will be obtained. For example, the probability becomes higher that a pure Al or Al-Si film with a reflectance of about 10 to 30 % will be obtained. The reason why a film inferior in surface flatness is thus obtained may be considered to be due to the fact that surface migration of metal atoms or molecules are great at a high temperature, whereby deposition proceeds only at specific nuclei to deteriorate surface flatness when becoming a film thickness. Thus, the greatest reasons is that, at the initial stage of deposition, a film with inferior surface flatness is formed, which exerts deleterious influences even afterwards. In the present invention, as the means for shifting from low deposition rate to high deposition rate during deposited film formation, for example, the method of varying the substrate temperature and the starting gas partial pressure is used to provide a method of obtaining pure Al or Al-Si deposited film of high quality and excellent in flatness at substantially high deposition rate. By doing so, a deposited film which has substantially high deposiiton rate and is also flat with high quality can be obtaided. In the deposited film formation by the surface chemical reaction according to the present invention, it appears that even a thin film becomes a continuous and high quality film under the condition of lower deposition rate under lower substrate temperature and lower starting gas partial pressure, provided that there is no contamination from the reaction tube. According to the knowledges by the present inventors, a deposited film of pure Al or Al-Si of good quality can be formed under good selectivity at a substrate temperature of 160 to 450 °C, more preferably 270 to 350 °C. Accordingly, in the first deposition step in the present invention, namely the deposited film formation step at low deposition rate, under a total pressure of 10⁻³ Torr to 760 Torr, preferably 5 x10⁻² Torr to 5 Torr, the substrate temperature is suitably chosen from 270 to 350 °C, preferably 270 to 300 °C, end the DMAH partial pressure from 1.3 x 10⁻⁵ to 1.3 x 10⁻³ -fold, preferably 1.3 x 10⁻⁵ to 1.3 x 10⁻⁴ -fold of the total pressure. In the second deposition step in the present invention, namely the deposited film formation step at high deposition rate, under a total pressure of 10⁻³ Torr to 760 Torr, preferably 5 x 10⁻² to 5 Torr, the substrate temperature is made 270 to 350 °C, preferably 300 to 350 °C, and the DMAH partial pressure 1.3 x 10⁻⁵ to 1.3 x 10⁻³-fold of total pressure. For elevating the substrate temperature, instead of using only a heater, the substrate temperature may be quickly elevated by irradiation of W lamp or Xe lamp on the wafer surface. Heating by a lamp is effective for quick elevation of the substrate temperature. Specifically, the DMAH partial pressure is suitably selected from the condition of 1.3 x 10⁻⁴ to 1.3 x 10⁻³-fold of the total pressure, so that a deposited film may be formed at a higher deposition rate than in the deposition rate in the first step as mentioned above. For example, under the some total pressure, with the substrate temperature being made constant, the partial pressure of DMAH may be increased, or with the DMAH partial pressure being constant, the substrate temperature may be elevated. of course under the same total pressure, both of the substrate temperature and the partial pressure may be elevated. For example, it is preferable to deposit a continuous film of 100 to 200 Å within the range of a substrate temperature from 270 to 300 °C in the first deposition step under the above-mentioned pressure conditions, and then form the film at an increased deposition rate of, for example, 0.1 to 1 µm/min. by increasing the substrate temperature to 300 to 350 °C. The deposited film thus formed becomes a film of good quality with surface migration being inhibited. By varying the deposition conditions as described above, a continuous, flat and high quality film of 100 to 200 Å is formed within a deposition time of 1 to 5 minutes under the first deposition conditions, while under the second deposition conditions, since a continuous and flat pure Al (or Al-Si) has been already formed, a flat and high quality thin film can be formed even if pure Al (or Al-Si) may be deposited at a high deposition rate of 0.1 to 1 µm/min. A pure Al film or Al-Si film of 1 µm thickness can be sufficiently formed by reposition for 1 to 5 minutes under the first conditions, and with the deposition time for 1 to 3 minutes under the second conditions. In the device shown in Fig. 2, pure Al or Al-Si can be deposited only on one sheet of substrate in deposition at one time. The method according to the present invention is also applicable to the reduced-pressure CVD device for a number of sheets as shown in Fig. 3. Since deposition according to the present invention employs the surface reaction at the heated electron donative substrate surface, according to the hot wall type reduced-pressure CVD method in which only the substrate is heated, an Al-Si containing 0.5 to 2.0 % of Si can be deposited at high speed by addition of DMAH and H₂, and an Si starting gas such as Si₂H₆, etc., if necessary. When a reduced pressure CVD device is used, the reaction tube pressure may be 0.05 to 760 Torr, desirably 0.1 to 0.8 Torr. As the first deposition conditions, the substrate temperature may be 270 to 350 °C, desirably 270 to 300 °C, and the DMAH partial pressure may be 1.3 x 10⁻⁵ to 1.3 x 10⁻³-fold, desirably 1.3 x 10⁻⁵ to 1.3 x 10⁻⁴ of the reaction tube pressure. As the second deposition conditions, the substrate temperature is made 270 to 350 °C, preferably 300 to 350 °C, and the DMAH partial pressure 1.3 x 10⁻⁵ to 1.3 x 10⁻³, preferably 1.3 x 10⁻⁴ to 1.3 x 10⁻³-fold of the partial pressure reaction tube. The Si₂H₆ partial pressure, in both the first and the second deposition conditions, may be within the range of 1 x 10⁻⁷ to 1 x 10⁻⁴-fold of the reaction tube pressure, whereby Al-Si is deposited at high speed on the electron donative surface. By forming a deposited film under the conditions as described above by use of such device, Al-Si films of good quality can be formed in all the wafers within the device. According to the present invention, in the initial stage of deposition, a continuous and dense pure Al or Al-Si is formed, and therefore even pure Al or Al-Si may be deposited thereafter at high speed deposition conditions of 0.2 to 1 µm/min., film quality such as surface flatness, etc. will not be deteriorated, but pure Al or Al-Si film of high quality can be deposited at a high speed practically effectively. Even if deposited at a high speed, the film obtained is dense with little amount of impurity such as carbon, etc. contained, its resistance is similar to that of bulk, and also surface flatness is extremely high. The deposited film, in spite of deposition at high speed, has the specific features as mentioned below: (1) reduction of hillock, (2) improvement of electromigration resistance, (3) reduction of alloy pit at the contact portion, (4) improvement of surface flatness, (5) improvement of resistance within via-hole and contact resistance, (6) lowering the temperature of heat treatment during wiring step. Since Al-Si film of high quality can be deposited at high speed, the through-put in the ultra-LSI process is dramatically improved. In the low pressure CVD device as shown in Fig. 3, Al-Si can be deposited at the same time on 100 to 200 sheets of 4 inch wafer, and the effect of high speed deposition contributes greatly to the improvement of through-put. In ultra-LSI in the future, the wafer to be used will be made to have a size of 6 or 8 inch. When the wafer size becomes as large as 6 inch or 8 inch, the low pressure CVD device as shown in Fig. 3 can be practically applied with difficulty, because the reaction tube diameter becomes larger. However, the sheet type CVD device as shown in Fig. 2 are very advantageous in enlargement of wafer, because the size of the device as a whole will not change greatly even if the wafer size may become larger. However, in Al-deposition according to the CVD method of the prior art, no high speed deposition of 0.2 to 1 µm/min. cannot be realized, and therefore it could be employed with difficulty even if a deposited film of high quality was formed. However, by use of the deposition method according to the present invention, Al-Si of high quality can be deposited at high speed of 0.2 to 1 µm/min., and particularly the meaning fulfilled by the present invention in a sheet type CVD device corresponding to 6 inch or 8 inch demanded for high through-put is very important. Figs. 4A - 4E show how the Al or Al-Si film according to the present invention is selectively grown in the via-hole. Fig. 4A is an illustration showing schematically the cross-section of the substrate before formation of the deposited film according to the present invention. 90 is the substrate comprising an electron donative material, and 91 a thin film comprising an electron non-donative material. When DMAH, optionally together with Si₂H₆ as starting gas and a gas mixture containing H₂ as reaction gas are fed onto the substrate 1 heated under the first deposition condition, pure Al or Al-Si is precipitated on the substrate 90 to form the continuous film of pure Al or Al-Si as shown Fig. 4B. When deposition of Al-Si is continued under the second deposition conditions, via the state of Fig. 4C, the film grows to the level of the uppermost portion of the thin film 91 as shown in Fig. 4D. Further, when grown under the same conditions as shown in Fig. 4E, the Al-Si film can grow to 5000 Å substantially without growth in the lateral direction. This is the most characteristic point of the deposited film obtained by the present invention, and it will be understood how a film of good quality can be formed under good selectivity. As the result of analysis according to Auger's electron spectroscopy or photoelectric spectroscopy, no entrainment of an impurity such as carbon or oxygen is recognized in this film. The deposited film thus formed has a resistivity of, for example, with a film thickness of 400 Å, 2.7 - 3.0 µohm·cm at room temperature which is substantially equal to the bulk resistivity of Al, and becomes continuous and flat film. Also, even with a film thickness of 1 µm, its resistance at room temperature is approximately 2.7 - 3.0 µohm·cm and a sufficiently dense film is formed with a relatively thicker film. The reflectance in the visible wavelength region is approximately 80 %, and a thin film with excellent surface flatness can be deposited. As described in detail above, in the present invention, in addition to the finding that pure Al is deposited selectively on an electron donative surface (A) by maintaining the electron donative surface (A) at a temperature between the decomposition temperature of an alkyl aluminum hydride and 450 °C in a gas mixture atmosphere of the alkyl aluminum hydride gas and hydrogen gas, or Al-Si is selectively deposited by use of the above gas mixture in which a gas containing Si is further added, for effecting higher through-put in formation of pure Al or Al-Si film, the deposition rate is shifted from a low deposition rate to a high deposition rate during the deposited film formation. By doing so, higher through-put can be attained without deterioration of film quality. When depositing Al-Si by use of the device shown in Fig. 2, as an example, under the conditions of: Total pressure: 1.5 Torr DMAH partial pressure: 1.5 x 10⁻⁴ Torr Si containing gas partial pressure: 2.0 x 10⁻⁶ Torr Substrate temperature: 160 °C - 450 °C, an Al-Si film can be selectively deposited only on the electron donative material surface. Even with a film thickness of 400 Å, the film is continuous and its resistivity is 2.7 - 3.0 µΩ·cm which substantially equal to the bulk value of Al. When the substrate temperature is 270 °C - 350 °C, the deposition rate is 100 - 800 Å/min., and for high speed deposition, the deposition rate is required to be made larger. For realizing high speed deposition, it may be conceivable to make the substrate temperature higher and DMAH partial pressure higher. For example, by making the substrate temperature 330 °C, and the DMAH partial pressure 10⁻² to 10⁻³ Torr, a deposition rate of 0.2 to 0.5 µm/min. can be realized. However, if the deposition rate is too large, the probability becomes higher that a surface inferior in surface flatness will be obtained. For example, the probability becomes higher that a pure Al or Al-Si film with a reflectance of about 10 to 30 % will be obtained. The reason why a film interior in surface flatness is thus obtained may be considered to be due to the fact that surface migration of metal atoms or molecules are great at a high temperature, whereby deposition proceeds only at specific nuclei to deteriorate surface flatness when becoming a film thickness. Thus, the greatest reasons is that, at the initial stage of deposition, a film with inferior surface flatness is formed, which exerts deleterious influences even afterwards. In the present invention, as the means for shifting from low deposition rate to high deposition rate during deposited film formation, for example, the method of varying the substrate temperature and the starting gas partial pressure is used to provide a method of obtaining pure Al or Al-Si deposited film of high quality and excellent in flatness at substantially high deposition rate. By doing so, a deposited film which has substantially high deposition rate and is also flat with high quality can be obtained. In the deposited film formation by the surface chemical reaction according to the present invention, it appears that even a thin film becomes a continuous and high quality film under the condition of lower deposition rate under lower substrate temperature and lower starting gas partial pressure, provided that there is no contamination from the reaction tube. According to the knowledges by the present inventors, a deposited film of pure Al or Al-Si of good quality can be formed under good selectivity at a substrate temperature of 160 to 450 °C, more preferably 270 to 350 °C. Accordingly, in the first deposition step in the present invention, namely the deposited film formation step at low deposition rate, under a total pressure of 10⁻³ Torr to 760 Torr, preferably 5 x 10⁻² Torr to 5 Torr, the substrate temperature is suitably chosen from 270 to 350 °C, preferably 270 to 300 °C, and the DMAH partial pressure from 1.3 x 10⁻⁵ to 1.3 x 10⁻³-fold, preferably 1.3 x 10⁻⁵ to 1.3 x 10⁻⁴-fold of the total pressure. In the second deposition step in the present invention, namely the deposited film formation step at high deposition rate, under a total pressure of 10⁻³ Torr to 760 Torr, preferably 5 x 10⁻² to 5 Torr, the substrate temperature is made 270 to 350 °C, preferably 300 to 350 °C, and the DMAH partial pressure 1.3 x 10⁻⁵ to 1.3 x 10⁻³-fold of total pressure. For elevating the substrate temperature, instead of using only a heater, the substrate temperature may be quickly elevated by irradiation of W lamp or Xe lamp on the wafer surface. Heating by a lamp is effective for quick elevation of the substrate temperature. Specifically, the DMAH partial pressure is suitably selected from the condition of 1.3 x 10⁻⁴ to 1.3 x 10⁻³-fold of the total pressure, so that a deposited film may be formed at a higher deposition rate than in the deposition rate in the first step as mentioned above. For example, under the same total pressure, with the substrate temperature being made constant, the partial pressure of DMAH may be increased, or with the DMAH partial pressure being constant, the substrate temperature may be elevated. Of course under the same total pressure, both of the substrate temperature and the partial pressure may be elevated. For example, it is preferable to deposit a continuous film of 100 to 200 Å within the range of a substrate temperature from 270 to 300 °C in the first deposition step under the above-mentioned pressure conditions, and then form the film at an increased deposition rate of, for example, 0.1 to 1 µm/min. by increasing the substrate temperature to 300 to 350 °C. The deposited film thus formed becomes a film of good quality with surface migration being inhibited. By varying the deposition conditions as described above, a continuous, flat and high quality film of 100 to 200 Å is formed within a deposition time of 1 to 5 minutes under the first deposition conditions, while under the second deposition conditions, since a continuous and flat pure Al (or Al-Si) has been already formed, a flat and high quality thin film can be formed even if pure Al (or Al-Si) may be deposited at a high deposition rate of 0.1 to 1 µm/min. A Al film of 1 µm thickness can be sufficiently formed by deposition for 1 to 5 minutes under the first conditions, and with the deposition time for 1 to 3 minutes under the second conditions. In the device shown in Fig. 2, Al-Si can be deposited only on one sheet of substrate in deposition at one time. The method according to the present invention is also applicable to the reduced-pressure CVD device for a number of sheets as shown in Fig. 3. Since Al-Si deposition according to the present invention employs the surface reaction at the heated electron donative substrate surface, according to the hot wall type reduced-pressure CVD method in which only the substrate is heated, an Al-Si containing 0.5 to 2.0 % of Si can be deposited at high speed by addition of DMAH and H₂, and an Si starting gas such as Si₂H₆, etc., if necessary. When a reduced pressure CVD device is used, the reaction tube pressure may be 0.05 to 760 Torr, desirably 0.1 to 0.8 Torr. As the first deposition conditions, the substrate temperature may be 270 to 350 °C, desirably 270 to 300 °C, and the DMAH partial pressure may be 1.3 x 10⁻⁵ to 1.3 x 10⁻³-fold, desirably 1.3 x 10⁻⁵ to 1.3 x 10⁻⁴ of the reaction tube pressure. As the second deposition conditions, the substrate temperature is made 270 to 350 °C, preferably 300 to 350 °C, and the DMAH partial pressure 1.3 x 10⁻⁵ to 1.3 x 10⁻³, preferably 1.3 x 10⁻⁴ to 1.3 x10⁻³-fold of the partial pressure reaction tube. The Si₂H₆ partial pressure, in both the first and the second deposition conditions, may be within the range of 1 x 10⁻⁷ to 1 x 10⁻⁴-fold of the reaction tube pressure, whereby Al-Si is deposited at high speed on the electron donative surface. According to the present invention, in the initial stage of deposition, a continuous and dense Al-Si is formed, and therefore even Al-Si may be deposited thereafter at high speed deposition conditions of 0.2 to 1 µm/min., film quality such as surface flatness, etc. will not be deteriorated, but Al-Si film of high quality can be deposited at a high speed practically effectively. Even if Al-Si film deposited at a high speed, the film obtained is dense with little amount of impurity such as carbon, etc. contained, its resistance is similar to that of bulk, and also surface flatness is extremely high. The deposited Al-Si film, in spite of deposition at high speed, has the specific features as mentioned below: (1) reduction of hillock, (2) improvement of electromigration resistance, (3) reduction of alloy pit at the contact portion, (4) improvement of surface flatness, (5) improvement of resistance within via-hole and contact resistance, (6) lowering the temperature of heat treatment during wiring step. Since Al-Si film of high quality can be deposited at high speed, the through put in the ultra-LSI process is dramatically improved. In the low pressure CVD device as shown in Fig. 3, Al-Si can be deposited at the same time on 100 to 200 sheets of 4 inch wafer, and the effect of high speed deposition contributes greatly to the improvement of through-put. In ultra-LSI in the future, the wafer to be used will be made to have a size of 6 or 8 inch. When the wafer size becomes as large as 6 inch or 8 inch, the low pressure CVD device as shown in Fig. 3 can be practically applied with difficulty, because the reaction tube diameter becomes larger. However, the sheet type CVD device as shown in Fig. 2 are very advantageous in enlargement of wafer, because the size of the device as a whole will not change greatly even if the wafer size may become larger. However, in Al-deposition according to the CVD method of the prior art, no high speed deposition of 0.2 to 1 µm/min cannot be realized, and therefore it could be employed with difficulty even if a deposited film of high quality was formed. However, by use of the deposition method according to the present invention, Al-Si of high quality can be deposited at high speed of 0.2 to 1 µm/min., and particularly the meaning fulfilled by the present invention in a sheet type CVD device corresponding to 6 inch or 8 inch demanded for high through-put is very important. Example 1 First, the procedure for Al film formation is as follows. By use of the device shown in Fig. 1, the reaction tube 2 is internally evacuated to ca. 1 x 10⁻⁸ Torr by the evacuation unit 9. However, Al film can be also formed if the vacuum within the reaction tube 2 may be higher than 1 x 10⁻⁸ Torr. After washing of Si wafer, the conveying chamber 10 is released to atmospheric pressure and Si wafer is mounted in the conveying chamber. The conveying chamber is evacuated to ca. 1 x 10⁻⁶ Torr, and then the gate valve 13 is opened and the wafer is mounted on the wafer holder 3. After mounting of the wafer on the wafer holder 3, the gate valve 13 is closed, and the reaction chamber 2 is evacuated to a vacuum degree of ca. 1 x 10⁻⁸ Torr. In this Example, DMAH is fed through the first gas line. As the carrier gas of DMAH line H₂ is employed. The second gas line is used for H₂. By passing H₂ through the second gas line, the pressure within the reaction tube is made a predetermined value by controlling the opening of the slow leek valve 8. A typical pressure in this Example is approximately 1.5 Torr. Then, the wafer is heated by current passage through the heater 4. After the wafer temperature has reached a predetermined temperature, DMAH is introduced into the reaction tube through the DMAH line. The total pressure is ca. 1.5 Torr, and the DMAH partial pressure is made ca. 1.5 x 10 ⁵ Torr. When DMAH is introduced into the reaction tube 2, Al is deposited. The outline of the first deposition step is as described above. In the first deposition step, after the formation of the continuous Al film of about 100 to 200 Å, high speed deposition is effected at the second deposition step. The condition for the second deposition step are made the total pressure of ca. 1.5 Torr and the DMAH partial pressure of ca. 1 x 10⁻³ Torr. After a predetermined deposition time has elapsed, feeding of DMAH is stopped. Next, heating of the heater 4 is stopped to cool the wafer. Feeding of H₂ gas is stopped, and after evacuation internally of the reaction tube, the wafer is transferred to the conveying chamber, and only the conveying chamber is made atmospheric before taking out the wafer. The outline of Al film formation is as described above. Actually, 130 Sheets of samples of Si wafer were prepared, the substrate temperatures were set at 13 levels, and Al films were deposited at the respective temperatures each for 10 sheets according to the procedure as described above under the following conditions: during the first deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.5 x 10⁻⁵ Torr during the second deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.5 x10⁻³ Torr The Al films deposited by varying the substrate temperature at 13 levels were evaluated by use of various evaluation methods. The results are shown in Table 1. Al was deposited on the Si wafer within the temperature range from 160 °C - 450°C. When the substrate temperatures in the first and second deposition steps exceed 300 °C, high speed deposition at 0.5 to 1.0 µm was possible, but the samples that surface reflectance becomes more or less worse as compared with the case of the temperature of 300 °C or lower were found. The reason may be considered to be due to the fact that, if the temperature in the first deposition step is high, the possibility that flatness of the extremely thin Al film deposited in the first deposition step is slightly inferior is enhanced. Example 2 Following the same procedure as in Example 1 to set the parameters as follows: during the first deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻⁵ Torr Substrate temperature: 270°C or 300°C during the second deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻³ Torr and the substrate temperature of the second deposition step was varied at several levels which were higher than that of the first deposition step to deposit the Al film. And various evaluation results of the Al film deposited are shown in Table 2. When the substrate temperature in the first deposition step is 270 °C or 300 °C, there is no difference in the results obtained. Similarly as in Example 1, when the substrate temperature in the second step exceeds 300 °C, high speed deposition at 0.5 to 1.0 µm/min. was possible. The difference from Example 1 is that an Al film with high surface flatness having a reflectance of 80 to 95 % could be formed even when the substrate temperature in the second step was 330 °C, 350 °C by suppressing the substrate temperature in the first deposition step at 300 °C or lower. Example 3 This Example carries out Al deposition by use of Ar in place of H₂ as the carrier gas for DMAH in the same procedure as in Example 1. From the gas second line, H₂ is fed. As the result of evaluation of Al film obtained by this Example, Al was deposited on Si wafer at a temperature range of 160 °C to 450 °C similarly as in Table 1 in Example 1. When the substrate temperatures in the first and second deposition steps exceed 300 °C, high speed deposition at 0.5 to 1.0 µm was possible, but the probability that surface reflectance becomes more or less worse is slightly enhanced. The reason may be considered to be due to the fact that, if the temperature in the first deposition step is high, flatness of the extremely thin Al film deposited in the first deposition step is inferior. Example 4 This Example 3 performs Al deposition by use of Ar in place of H₂ as the carrier gas for DMAH in the same procedure as in Example 2. The second gas line fed H₂. When the substrate temperatures in the first deposition step were 270 °C and 300 °C, there was no difference in the results obtained. The film quality obtained is substantially the same as in Table 2. Similarly as in Example 1 or 2, when the substrate temperature in the second step exceeds 300 °C, high speed deposition at 0.5 to 1.0 µm/min. was possible. The difference from Examples 1 and 3 is that an Al film with high surface flatness having a reflectance of 80 to 95 % could be formed even when the substrate temperature in the second step was 330 °C, 350 °C by suppressing the substrate temperature in the first deposition step at 300 °C or lower. Example 5 The Al film was formed on the substrate having the following constitution by using low pressure CVD device as shown in Fig. 3. That is, as the substrate, the following 17 kind thin films were used on the Si wafer. (1) polycrystalline silicon (polycrystalline Si), (2) amorphous silicon (amorphous Si), (3) tungsten (W), (4) molybdenum (Mo), (5) tantalum (Ta), (6) tungsten silicide (WSi), (7) titanium silicide (TiSi), (8) aluminum (Al), (9) aluminum silicon (Al-Si), (10) titanium aluminum (Al-Ti), (11) titanium nitride (TiN), (12) copper (Cu), (13) aluminum silicon copper (Al-Si-Cu), (14) aluminum palladium (Al-Pd), (15) titanium (Ti), (16) molybdenum silicide (Mo-Si), (17) tantalum silicide (Ta-Si) were employed. These samples were placed in the low pressure CVD device shown in Fig. 3 and Al films were formed within the same batch. The deposition conditions at this time are as follows: during the first deposition step. Total pressure: 0.3 Torr DMAH partial pressure: 3 x 10⁻⁶ Torr Substrate temperature: 270°C during the second deposition step, Total pressure: 0.3 Torr DMAH partial pressure: 1 x 10⁻⁴ Torr Substrate temperature: 330°C The film quality of the film formed under such conditions is not different from those at a substrate temperature in the second deposition of 330°C in Table 2 as described above, and also the deposition rate in the second deposition step was very high as ca. 0.7 µm/min. for all the substrates. Example 6 According to the same procedure as in Example 2, Al film was deposited by the of MMAH₂ in place of DAMH as the starting gas. As the substrate, the same Si wafer as in Example 1 was used. The deposition conditions at this time are as follows: during the first deposition step, Reaction tube pressure: 1.5 Torr MMAH₂ partial pressure: 5 x 10⁻⁵ Torr Substrate temperature: 270°C during the second deposition step, Reaction tube pressure: 1.5 Torr MMAH₂ partial pressure: 1 x 10⁻³ Torr The film quality of deposited Al was not different from one at a substrate temperature in the second deposition step of 330°C in Table 2. Also, the deposition rate of Al in the second deposition step was ca. 0.7 µm/min. and not substantially different from the case of using DMAH. Example 7 First, the procedure for Al-Si film formation is as follows. By use of the device shown in Fig. 2, the reaction tube 2 is internally evacuated to ca. 1 x 10⁻⁸ Torr by the evacuation unit 9. However, Al-Si film can be also formed if the vacuum degree within the reaction tube 2 may be higher than 1 x 10⁻⁸ Torr. After washing of Si wafer, the conveying chamber 10 is released to atmospheric pressure and Si wafer is mounted in the conveying chamber. The conveying chamber is evacuated to ca. 1 x 10⁻⁶ Torr, and then the gate valve 13 is opened and the wafer is mounted on the wafer holder 3. After mounting of the wafer on the wafer holder 3, the gate valve 13 is closed, and the reaction chamber 2 is evacuated to a vacuum degree of ca. 1 x 10⁻⁸ Torr. In this Example, DMAH is fed through the first gas line. As the carrier gas of DMAH line, Ar is employed. The second gas line is used for H₂ and the third gas line for Si₂H₆. By passing H₂ through the second gas line, the pressure within the reaction tube 2 is made a predetermined value by controlling the opening of the slow leak valve 8. A typical pressure in this Example is made approximately 1.5 Torr. Then, the wafer is heated by current passage through the heater 4. After the wafer temperature has reached a predetermined temperature, DMAH introduced into the reaction tube through the DMAH line. The total pressure is ca. 1.5 Torr, and the DMAH partial pressure is made ca. 1.5 x 10⁻⁵ Torr. The Si₂H₆ partial pressure is made 2 x 10⁻⁷ Torr. When Si₂H₆ and DMAH are introduced into the reaction tube 2, Al-Si is deposited. The outline of the first deposition step is as described above. In the first deposition step, after the formation of the continuous Al-Si film of about 100 to 200 Å, high speed deposition is effected at the second deposition step. The condition for the second deposition step are made the total pressure of ca. 1.5 Torr and the DMAH partial pressure of ca. 1 x 10⁻³ Torr. After a predetermined deposition time has elapsed, feeding of DMAH and Si₂H₆ is stopped. Next, heating of the heater 4 is stopped to cool the wafer. Feeding of H₂ gas is stopped, and after evacuation internally of the reaction tube, the wafer is transferred to the conveying chamber, and only the conveying chamber is made atmospheric before taking out the wafer. The outline of Al film formation is as described above. Actually, 130 Sheets of samples of Si wafer were prepared, the substrate temperatures were set at 13 levels, and Al-Si films were deposited at the respective temperatures each for 10 sheets according to the procedure as described above under the following conditions: during the first deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.5 x 10⁻⁵ Torr Si₂H₆ partial pressure: 2.0 x 10⁻⁷ Torr during the second deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻³ Torr Si₂H₆ partial pressure: 1.5 x 10⁻⁵ Torr. The Al-Si films deposited by varying the substrate temperature at 13 levels were evaluated by use of various evaluation methods. The results are the same as those in Table 1. Al-Si was deposited on the Si wafer within the temperature range from 160°C - 450°C. When the substrate temperatures in the first and second deposition steps exceed 300 °C, high speed deposition at 0.5 to 1.0 µm was possible, but the probability that surface reflectance becomes more or less worse is slightly enhanced. The reason may be considered to be due to the fact that, if the temperature in the first deposition step is high, flatness of the extremely thin Al-Si film deposited in the first deposition step is inferior. Example 8 Following the same procedure as in Example 7 to set the parameters as follows: during the first deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻⁵ Torr Si₂H₆ partial pressure: 1.5 x 10⁻⁷ Torr Substrate temperature: 270°C or 300°C during the second deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻³ Torr Si₂H₆ partial pressure: 1.5 x 10⁻⁵ Torr and the substrate temperature of the second deposition step was varied at 13 levels. As a result, various evaluation results in the Al-Si film are the same as those in Table 2. When the substrate temperature in the first deposition step is 270 °C or 300 °C, there is no difference in the results obtained. Similarly as in Example 7, when the substrate temperature in the second step exceeds 300 °C, high speed deposition at 0.5 to 1.0 µm/min. was possible. The different from Example 7 is that an Al-Si film with high surface flatness having a reflectance of 80 to 95 % could be formed even when the substrate temperatures in the second step was were 330 °C, 350 °C. Example 9 Following the same procedure as in Example 8 to set the parameters as follows: during the first deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻⁵ Torr Substrate temperature: 270 °C during the second deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻³ Torr Substrate temperature: 330 °C and the Si₂H₆ partial pressure was varied from 3 x 10⁻⁴ to 0.2 fold of DMAH partial pressure to effect deposition. The Si content (wt.%) of the Al-Si films were varied from 0.005% to 5% approximately in proportion to the Si₂H₆ partial pressure. As to resistivity, carbon content, average wiring life, deposition speed, hillock density and spike generation, the same results as in Example 1 were obtained. However, in samples having a Si content of 4 % or higher, deposition was generated in the films which appeared to be Si to worsen slightly surface morphology, thereby making the reflectance 65 % or lower. Samples having a Si content of less than 4 % exhibited a reflectance of 80 to 95 %, which was similarly good as in example 8. Example 10 This Example 10 carries our Al-Si deposition by use of Ar in place or H₂ as the carrier gas for DMAH in the same procedure as in Example 7. From the gas second line, H₂ as the reaction gas is fed. As the result of evaluation of Al-Si film obtained by this Example, Al-Si was deposited on Si wafer at a temperature range of 160 °C to 450 °C similarly as in Table 1 in Example 1. When the substrate temperatures in the first and second deposition steps exceed 300 °C, high speed deposition at 0.5 to 1.0 µm was possible, but the probability that surface reflectance becomes more or less worse is slightly enhanced. The reason may be considered to be due to the fact that, if the temperature in the first deposition step is high, flatness of the extremely thin Al-Si film deposited in the first deposition step is inferior. Example 11 This Example 11 performs Al-Si deposition by use of Ar in place of H₂ as the carrier gas for DMAH in the same procedure as in Example 8. The second gas line fed H₂. When the substrate temperatures in the first deposition step were 270 °C and 300 °C, there was no difference in the results obtained. The film quality obtained is substantially the same as in Table 2. Similarly as in Example 7 or 8, when the substrate temperature in the second step exceeds 300 °C, high speed deposition at 0.5 to 1.0 µm/min. was possible. The difference from Examples 7 and 8 is that an Al-Si film with high surface flatness having a reflectance of 80 to 95 % could be formed even when the substrate temperatures in the second step were 330 °C, 350 °C Example 12 This Example 12 performs Al-Si deposition by use of Ar in place of H₂ as the carrier gas for DMAH in the same procedure as in Example 9. The second gas line fed H₂. Deposition condition was shown below. during the first deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻⁵ Torr Substrate temperature: 270 °C during the second deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻³ Torr Substrate temperature: 330 °C and the Si₂H₆ partial pressure was varied from 3 x 10⁻⁴ to 0.2 fold of DMAH partial pressure to effect deposition. The Si content (wt.%) of the Al-Si films were varied from 0.005 % to 5 % approximately in proportion to the Si₂H₆ partial pressure. As to resistivity, carbon content, average wiring life, deposition speed, hillock density and spike generation, the same results as in Example 1 were obtained. However, in samples having a Si content of 4 % or higher, deposition was generated in the films which appeared to be Si to worsen slightly surface morphology, thereby making the reflectance 65 % or lower. Samples having a Si content of less than 4 % exhibited a reflectance of 80 to 95 %, which was similarly good the same as in Example 8. Example 13 The Al film was formed on the substrate having the following constitution by using low pressure CVD device in Fig. 3. That is, as the substrate, (1) polycrystalline silicon (polycrystalline Si), (2) amorphous silicon (amorphous Si), (3) tungsten (W), (4) molybdenum (Mo), (5) tantalum (Ta), (6) tungsten silicide (WSi), (7) titanium silicide (TiSi), (8) aluminum (Al), (9) aluminum silicon (Al-Si), (10) titanium aluminum (Al-Ti), (11) titanium nitride (TiN), (12) copper (Cu), (13) aluminum silicon copper (Al-Si-Cu), (14) aluminum palladium (Al-Pd), (15) titanium (Ti), (16) molybdenum silicide (Mo-Si), (17) tantalum silicide (Ta-Si) were employed. These samples were placed in the low pressure CVD device shown in Fig. 3 and Al-Si films were formed within the same batch. The deposition conditions at this time are as follows: during the first deposition step, Total pressure: 0.3 Torr DMAH partial pressure: 3 x 10⁻⁶ Torr Si₂H₆ partial pressure: 1.0 x 10⁻⁷ Torr Substrate temperature: 270°C during the second deposition step, Total pressure: 0.3 Torr DMAH partial pressure: 1 x 10⁻⁴ Torr Si₂H₆ partial pressure: 3 x 10⁻⁶ Torr Substrate temperature: 330°C The film quality of the Al-Si film formed under such conditions is not different from those at a substrate temperature in the second deposition of 330°C in Table 2 as described above, and also the deposition rate in the second deposition step was very high as ca. 0.7 µm/min. for all of the substrates. Example 14 According to the same procedure as in Example 8, Al-Si film was deposited by the use of MMAH₂ in place of DAMH as the starting gas. As the substrate, Si wafer obtained by patterning the same SiO₂ thin film as shown in Example 7. The deposition conditions at this time are as follows: during the first deposition step, Reaction tube pressure: 1.5 Torr MMAH₂ partial pressure: 5 x 10⁻⁵ Torr Si₂H₆ partial pressure: 1.0 x 10⁻⁶ Torr Substrate temperature: 270°C during the second deposition step, Reaction tube pressure: 1.5 Torr MMAH₂ partial pressure: 1 x 10⁻³ Torr Si₂H₆ partial pressure: 1 x 10⁻⁵ Torr The film quality of deposited Al-si was not different from one at a substrate temperature in the second deposition step of 330°C in Table 2. Also, the deposition rate of Al-si in the second deposition step was ca. 0.7 µm/min. and not substantially different from the case of using DMAH. Example 15 According to the same procedure as in Example 8, Al-Si film was deposited by the use of SiH₄ in place of Si₂H₆. As the substrate, Si wafer was used. The deposition conditions at this time are as follows: during the first deposition step, Reaction tube pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻⁵ Torr Si₂H₆ partial pressure: 5.0 x 10⁻⁷ Torr Substrate temperature: 270°C during the second deposition step, Reaction tube pressure: 1.5 Torr DMAH partial pressure: 1 x 10⁻³ Torr Si₂H₆ partial pressure: 5 x 10⁻⁵ Torr Substrate temperature: 330°C The film quality of deposited Al-Si was not different from one at a substrate temperature in the second deposition step of 330°C in Table 2. Also, the deposition rate of Al-Si in the second deposition step was ca. 0.7 µm/min. and not substantially different from the case of using Si₂H₆. Example 16 Samples having Al films formed according to the same method as in Example 1 were prepared. When crystallinity of the Al film deposited on the Si wafer of the respective samples, namely under the same film forming conditions as in Example 1 by use of the X-ray diffraction method and the reflective electron beam diffraction method, it was found to be as described below. When the crystal direction of the Si substrate is (111) plane, from X-ray diffraction, as shown in Fig. 5, only the diffraction peak showing Al (100) was observed concerning Al. In reflective high speed electron beam diffraction by use of an acceleration voltage of 80 kV or 100 kV, as shown in Fig. 6, a monocrystal spot showing Al (100) was observed. Fig. 6A is a diffraction pattern when electron beam is permitted to enter Al (100) in the [001] direction, Fig. 6B a diffraction pattern when electron beam is permitted to enter Al (100) in the direction of [011]. Thus, the Al film on the Si (111) substrate was found to be a monocrystal having (100) plane. Within the first and second substrate temperature range in Table 1, those deposited at a range from 250 °C to 330 °C were found to have Al films reproducibly deposited which were monocrystalline. Also, the Al films deposited on the Si (111) substrate with the substrate surface having off-angles differing by 1°, 2°, 3°, 4°, 5° from the Si (111) plane were also found to have Al (100) monocrystals deposited stably, particularly under the temperature conditions of the first and second substrate temperature ranging from 250 °C to 330 °C, similarly as in the case when deposited on the Si (111) substrate as described above. When the crystal direction of the Si Substrate is (100) plane, from X-ray diffraction, as shown in Fig. 7, only the diffraction peak showing Al (111) was observed concerning Al. In reflective high speed electron beam diffraction by use of an acceleration voltage of 80 kV or 100 kV, a monocrystal spot showing Al (111) was observed. Thus, the Al film on the Si (100) substrate was found to be a monocrystal having (111) plane. Within the first and second substrate temperature range in Table 1, those deposited at a range from 250 °C to 330 °C were found to have Al films deposited which were stably monocrystalline. Also, the Al films deposited on the Si (100) substrate with the substrate surface having off-angles differing by 1°, 2°, 3°, 4°, 5° from the Si (100) plane were also found to have Al (111) monocrystals deposited stably, particularly under the temperature conditions of the first and second substrate temperature ranging from, 250 °C °C to 330 °C, similarly as in the case when deposited on the Si (111) substrate as described above. Example 17 Samples having Al films formed according to the same method as in Example 2 were prepared. When crystallinity of the Al film deposited on the Si wafer by use of the X-ray diffraction method and the reflective electron beam diffraction method, it was found to be as described below. When the crystal direction of the Si substrate is (111) plane, from X-ray diffraction, as shown in Fig. 5, only the diffraction peak showing Al (100) was observed concerning Al. In reflective high speed electron beam diffraction by use of an acceleration voltage of 80 kV or 100 kV, as shown in Figs. 6A and 6B, a monocrystal spot showing Al (100) was observed. Fig. 6A is a diffraction pattern when electron beam is permitted to enter Al (100) in the [001] direction, Fig. 6B a diffraction pattern when electron beam is permitted to enter Al (100) in the direction of [011]. Thus, the Al film on the Si (111) substrate was found to be a monocrystal having (100) plane. Within the second substrate temperature range in Table 2, those deposited at a range from 250 o C to 330 o C were found to have Al films deposited which were monocrystalline. Also, the Al films deposited on the Si (111) substrate with the substrate surface having off-angles differing by 1 o , o , 3 o , 4 o , 5 o from the Si (111) plane were also found to have Al (100) monocrystals deposited stably, particularly under the temperature conditions of the second substrate temperature ranging from 250 o C to 330 o C, similarly as in the case when deposited on the Si (111) substrate as described above. When the crystals direction of the Si substrate is (100) plane, from X-ray diffraction, as shown in Fig. 7, only the diffraction peak showing Al (111) was observed concerning Al. In reflective high speed electron beam diffraction by use of an acceleration voltage of 80 kV or 100 kV, a monocrystal spot showing Al (111) was observed. Thus, the Al film on the Si (100) substrate was found to be a monocrystal having (111) plane. Within the second substrate temperature range in Table 2, those deposited at a range from 250 °C to 330 °C were found to have Al films deposited which were stably monocrystalline. Also, the Al films deposited on the Si (100) substrate with the substrate surface having off-angles differing by 1°, 2°, 3°, 4°, 5° from the Si (100) plane were also found to have Al (111) monocrystals deposited stably, particularly under the temperature conditions of the second substrate temperature ranging from 250 °C to 330 °C, similarly as in the case when deposited on the Si (111) substrate as described above. Example 18 Crystallinity of the Al film formed by the method of Example 3 was examined. Similarly as in the case of Example 1, at a substrate temperature of the first and second substrate in Table 2 ranging from 250°C to 330°C, Al(100) monocrystal was deposited on the Si (111) substrate, and Al (111) monocrystal on the Si (100) substrate. Example 19 Crystallinity of the Al film formed by the method of Example 4 was examined. Similarly as in the case of Example 1, at a substrate temperature of the first and second substrate in Table 2 ranging from 270°C to 330°C, Al (100) monocrystal was deposited on the Si (111) substrate, and Al (111) monocrystal on the Si (100) substrate. Example 20 First, the procedure for Al film formation is as follows. By use of the device shown in Fig. 2, the reaction tube 2 is internally evacuated to ca. 1 x 10⁻⁸ Torr by the evacuation unit 9. However, Al film can be also formed if the vacuum degree within the reaction tube 2 may be higher than 1 x 10⁻⁸ Torr. After washing of Si wafer, the conveying chamber 10 is released to atmospheric pressure and Si wafer is mounted in the conveying chamber. The conveying chamber is evacuated to ca. 1 x 10⁻⁶ Torr, and then the gate valve 13 is opened and the wafer is mounted on the wafer holder 3. After mounting of the wafer on the wafer holder 3, the gate valve 13 is closed, and the reaction chamber 2 is evacuated to a vacuum degree of ca. 1 x 10⁻⁸ Torr. In this Example, DMAH is fed through the first gas line. As the carrier gas of DMAH line H₂ is used. The second gas line is used for H₂. By passing H₂ through the second gas line, the pressure within the reaction tube 2 is made a predetermined value by controlling the opening of the slow leak valve 8. A typical pressure in this Example is made approximately 1.5 Torr. Then, the wafer is heated by current passage through the heater 4. After the wafer temperature has reached a predetermined temperature, DMAH is introduced into the reaction tube through the DMAH line. The total pressure is ca. 1.5 Torr, and the DMAH partial pressure is made ca. 1.5 x 10⁻⁴ Torr. When DMAH is introduced into the reaction tube 2, Al is deposited. The outline of the first deposition step is as described above. In the first deposition step, after the formation of the continuous Al film of about 100 to 200 Å, high speed deposition is effected at the second deposition step. The condition for the second deposition step are made the total pressure of ca. 1.5 Torr and the DMAH partial pressure of ca. 1 x 10⁻³ Torr. After a predetermined deposition time has elapsed, feeding of DMAH is stopped. Next, heating of the heater 4 is stopped to cool the wafer. Feeding of H₂ gas is stopped, and after evacuation internally of the reaction tube, the wafer is transferred to the conveying chamber, and only the conveying chamber is made atmospheric pressure before taking out the wafer. The outline of Al film formation is as described above. Si substrates (N type, 1 - 2 ohm·cm) were subjected to thermal oxidation at a temperature of 1000 °C according to the hydrogen combustion system (H₂: 4 liters/M, O₂: 2 liters/M). The film thickness was 7000 Å ± 500 Å, and the refractive index 1.46. A photoresist was coated on the whole Si substrate, and a desired pattern was baked by an exposure machine. The pattern was such that various holes of 0.25 µm x 0.25 µm - 100 µm x 100 µm were opened. After development of the resist, with the photoresist as the mask, the subbing SiO₂ was etched by the reactive ion etching (RIE), etc. to have the substrate Si partially exposed. Thus, 130 sheets of samples having various sizes of SiO₂ holes of 0.25 µm x 0.25 µm - 100 µm x 100 µm were prepared, the substrate temperature was set at 13 levels, and for the samples each of 100 sheets at the respective temperatures, Al films were deposited following the procedure as described above under the following conditions: during the first deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.5 x 10⁻⁵ Torr during the second deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.5 x 10⁻³ Torr The Al films deposited by varying the substrate temperature at 13 levels were evaluated by use of various evaluation methods. The results are shown in Table 3. In the above samples, no Al was deposited on SiO₂ at a temperature range from 160°C to 450°C, and Al was deposited only on the portion with opening of SiO₂ to have Si exposed. Also, when 2µm of Al deposition was carried out in the above temperature range continuously, similar selective depositability was maintained. When the substrate temperatures in the first and second deposition steps exceed 300 °C, high speed deposition at 0.5 to 1.0 µm was possible, but the probability that surface reflectance becomes more or less worse as compared with the case of 300°C or lower is slightly enhanced. The reason may be considered to be due to the fact that, if the temperature in the first deposition step is high, flatness of the extremely thin Al film deposited in the first deposition step is inferior. Example 21 Following the same procedure as in Example 20 to set the parameters as follows: during the first deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.5 x 10⁻⁵ Torr Substrate temperature: 270°C or 300°C during the second deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻³ Torr and the substrate temperature of the second deposition step was varied at several levels which were higher than that of the first deposition step to deposit the Al film. And various evaluation results of the Al film deposited are shown in Table 4. When the substrate temperature in the first deposition step is 270 °C or 300 °C, there is no difference in the results obtained. Similarly as in Example 20, when the substrate temperature in the second step exceeds 300 °C, high speed deposition at 0.5 to 1.0 µm/min. was possible. The difference from Example 20 is that an Al film with high surface flatness having a reflectance of 80 to 95 % could be formed even when the substrate temperature in the second step was 330 °C, 350 °C. Similarly as in Example 20, Al was selectively deposited only on Si. Also, even when Al was deposited to 2µm, the selective depositability was maintained. Example 22 This Example 22 carries out Al deposition by use of Ar in place of H₂ as the carrier gas for DMAH in the same procedure as in Example 20. From the gas second line, H₂ is fed. Similarly as in Table 3 of Example 20, no Al was deposited on SiO₂ at a temperature range from 160°C to 450°C, and Al was deposited only on the portion with opening of SiO₂ to have Si exposed. Also, when 2µm of Al deposition was carried out in the above temperature range continuously, similar selective depositability was maintained. When the substrate temperatures in the first and second deposition steps exceed 300 °C, high speed deposition at 0.5 to 1.0 µm was possible, but the probability that surface reflectance becomes more or less worse is slightly enhanced. The reason may be considered to be due to the fact that, if the temperature in the first deposition step is high, flatness of the extremely thin Al film deposited in the first deposition step is inferior. Example 23 This Example 23 performed Al deposition by use of Ar in place of H₂ as the carrier gas for DMAH in the same procedure as in Example 21. The second gas line fed H₂. When the substrate temperatures in the first deposition step were 270 °C and 300 °C, there was no difference in the results obtained. The film quality obtained is substantially the same as in Table 4. Similarly as in Example 20 or 21, when the substrate temperature in the second step exceeds 300 °C, high speed deposition at 0.5 to 1.0 µm/min. was possible. The difference from Examples 20 and 21 is that an Al film with high surface flatness having a reflectance of 80 to 95 % could be reproducibly formed even when the substrate temperature in the second step was 330 °C, 350 °C. Similarly as in Example 20 and Example 21, Al was selectively deposited only on Si. Also, even when Al was deposited to 2µm, the selective depositability was maintained. In the above samples, no Al was deposited on SiO₂ at a temperature range from 160°C to 450°C, and Al was deposited only on the portion with opening of SiO₂ to have Si exposed. Also, when 2µm of Al deposition was carried out in the above temperature range continuously, similar selective depositability was maintained. Example 24 By means of the low pressure CVD device shown in Fig. 3, Al films were formed on the substrates with the constitutions as described below (Samples 5-1 - 5-179). Preparation of Sample 5-1 On a monocrystalline silicon as the electron donative first substrate surface material, a thermally oxidized SiO₂ film as the electron non-donative second substrate surface material was formed, and patterning was effected according to the photolithographic steps as shown in Example 20 to have the monocrystalline surface partially exposed. The film thickness of the thermally oxidized SiO₂ film was found to be 7000 Å, with the size of the exposed portion of the monocrystalline silicon, namely opening being 3 µm x 3 µm. Thus, Sample 5-1 was prepared. (Hereinafter, such sample is expressed as "thermally oxidized SiO₂ (hereinafter abbreviated as T-SiO₂)/monocrystalline silicon"). Preparation of Samples 5-2 - 5-179 Sample 5-2 is an oxidized film formed by normal pressure CVD (hereinafter abbreviated as SiO₂)/monocrystalline silicon. Sample 5-3 is a boron doped oxidized film formed by normal pressure CVD (hereinafter abbreviated as BSG)/monocrystalline silicon. Sample 5-4 is a phosphorus doped oxidized film formed by normal pressure CVD (hereinafter abbreviated as PSG)/monocrystalline silicon. Sample 5-5 is a phosphorus and boron doped oxidized film formed by normal pressure CVD (hereinafter abbreviated as BSPG)/monocrystalline silicon. Sample 5-6 is a nitrided film formed by plasma CUD (hereinafter abbreviated as P-S:N)/monocrystalline silicon. Sample 5-7 is a thermally nitrided film (hereinafter abbreviated as T-S:N)/monocrystalline silicon. Sample 5-8 is a nitrided film formed by low pressure CVD thereinafter abbreviated as LP-SiN)/monocryatalline silicon. Sample 5-9 is a nitrided film formed by ECR device (hereinafter abbreviated as ECR-SiN)/monocrystalline silicon. Further, by combinations of the electron donative first substrate surface materials and the electron non-donative second substrate surface materials, Samples 5-11 - 5-179 shown in Table 5 were prepared. As the first substrate surface material, monocrystalline silicon (monocrystalline Si), polycrystalline silicon (polycrystalline Si), amorphous silicon (amorphous Si), tungsten (W), molybdenum (Mo), tantalum (Ta), tungsten silicide (WSi), titanium silicide (TiSi), aluminum (Al), aluminum silicon (Al-Si), titanium aluminum (Al-Ti), titanium nitride (TiN), copper (Cu), aluminum silicon copper (Al-Si-Cu), aluminum palladium (Al-Pd), titanium (Ti), molybdenum silicide (Mo-Si), tantalum silicide (Ta-Si) were employed. These samples were placed in the low pressure CVD device shown in Fig. 3, and Al films were formed within the same batch. The deposition conditions were as follows: during the first deposition step, Total pressure: 0.3 Torr DMAH partial pressure: 3 x 10⁻⁶ Torr Substrate temperature: 270°C during the second deposition step, Total pressure: 0.3 Torr DMAH partial pressure: 1 x 10⁻⁴ Torr Substrate temperature: 330°C As the result of film formation under such conditions, concerning all the samples applied with patterning from Sample 5-1 to 5-179, deposition of Al film occurred only on the electron donative first substrate surface film to embed completely the opening with the depth of 7000 Å. The film quality of the Al film formed is not different from those at a substrate temperature in the second deposition of 330°C in Table 2 as described above, and also the deposition rate in the second deposition step was very high as ca. 0.7 µm/min. for all of the substrates. Example 25 According to the same procedure as in Example 21, Al film was deposited by the use of MMAH₂ in place of DMAH. As the substrate, Si wafer obtained by patterning the same SiO₂ thin film as shown in Example 20. The deposition conditions at this time are as follows: during the first deposition step, Reaction tube pressure: 1.5 Torr MMAH₂ partial pressure: 5 x 10⁻⁵ Torr Substrate temperature: 270°C during the second deposition step, Reaction tube pressure: 1.5 Torr MMAH₂ partial pressure: 1 x 10⁻³ Torr Similarly as in Example 21, Al film embedded completely the SiO₂ opening with the depth of 7000 Å and the film quality of deposited Al was not different from one at a substrate temperature in the second deposition step of 330°C in Table 4. Also, the deposition rate of Al in the second deposition step was ca. 0.7 µm/min. and not substantially different from the case of using DMAH. In the above samples, no Al was deposited on SiO₂ at a temperature range from 160°C to 450°C, and Al was deposited only on the portion with opening of SiO₂ to have Si exposed. Also, when 2µm of Al deposition was carried out in the above temperature range continuously, similar selective depositability was maintained. Example 26 First the procedure for Al-Si film formation is as follows. By use of the device shown in Fig. 1, the reaction tube 2 is internally evacuated to ca. 1 x 10⁻⁸ Torr by the evacuation unit 9. However, Al-Si film can be also formed if the vacuum degree within the reaction tube 2 may be higher than 1 x 10⁻⁸ Torr. After washing of Si wafer, the conveying chamber 10 is released to atmospheric pressure and Si wafer is mounted in the conveying chamber. The conveying chamber is evacuated to ca. 1 x 10⁻⁶ Torr, and then the gate valve 13 is opened and the wafer is mounted on the wafer holder 3. After mounting of the wafer on the wafer holder 3, the gate valve 13 is closed, and the reaction chamber 2 is evacuated to a vacuum degree of ca. 1 x 10⁻⁸ Torr. In this Example, DMAH is fed through the first gas line. As the carrier gas of DMAH line Ar is employed. The second gas line is used for H₂ and the third gas line for Si₂H₆. By passing H₂ through the second gas line, the pressure within the relation tube 2 is made a predetermined value by controlling the opening of the slow leak valve 8. A typical pressure in this Example is made approximately 1.5 Torr. Then, the wafer is heated by current passage through the heater 4. After the wafer temperature has reached a predetermined temperature, DMAH is introduced into the reaction tube through the DMAH line. The total pressure is ca. 1.5 Torr, and the DMAH partial pressure is made ca. 1.5 x 10⁻⁵ Torr. The Si₂H₆ partial pressure is made 2 x 10⁻⁷ Torr. When DMAH and Si₂H₆ are introducted into the reaction tube 2, Al-Si is deposited. The outline of the first deposition step is as described above). In the first deposition step, after the formation of the continuous Al-Si film of about 100 to 200 Å, high speed deposition is effected at the second deposition step. The condition for the second deposition step are made the total pressure of ca. 1.5 Torr, the DMAH partial pressure of ca. 1 x 10⁻³ Torr and the Si₂H₆ partial pressure of ca. 1.5 x 10⁻⁵ Torr. After a predetermined deposition time has elapsed, feeding of DMAH and Si₂H₆ is stopped. Next, heating of the heater 4 is stopped to cool the wafer. Feeding of H₂ gas is stopped, and after evacuation internally of the reaction tube, the wafer is transferred to the conveying chamber, and only the conveying chamber is made atmospheric pressure before taking out the wafer. The outline Al film formation is as described above. Si substrates (N type, 1 - 2 ohm·cm) were subjected to thermal oxidation at a temperature of 1000 °C according to the hydrogen combustion system (H₂: 4 liters/M, O₂: 2 liters/M). The film thickness was 7000 Å ± 500 Å, and the refractive index 1.46. A photoresist was coated on the whole Si substrate, and a desired pattern was baked by an exposure machine. The pattern was such that various holes of 0.25 µm x 0.25 µm - 100 µm x 100 µm were opened. After development of the resist, with the photoresist as the mask, the subbing SiO₂ was etched by the reactive ion etching (RIE), etc. to have the substrate Si partially exposed. Thus, 130 sheets of samples having various sizes of SiO₂ holes of 0.25 µm x 0.25 µm - 100 µm x 100 µm were prepared, the substrate temperature was set at 13 levels, and for the samples each of 10 sheets at the respective temperatures, Al-Si films were selectively deposited following the procedure as described above under the following conditions: during the first deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.5 x 10⁻⁵ Torr Si₂H₆ partial pressure: 2.0 x 10⁻⁷ Torr during the second deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻³ Torr Si₂H₆ partial pressure: 1.5 x 10⁻⁵ Torr The Al-Si films deposited by varying the substrate temperature at 13 levels were evaluated by use of various evaluation methods. The results were the same as shown in Table 3. In the above samples, no Al-Si was deposited on SiO₂ at a temperature range from 160°C to 450°C, and Al-Si was deposited only on the portion with opening of SiO₂ to have Si exposed. Also, when 2µm of Al-Si deposition was carried out in the above temperature range continuously, similar selective depositability was maintained. When the substrate temperatures in the first and second deposition steps exceed 300 °C, high speed deposition at 0.5 to 1.0 µm was possible, but the probability that surface reflectance becomes more or less worse is slightly enhanced. The reason may be considered to be due to the fact that, if the temperature in the first deposition step is high, flatness of the extremely thin Al-Si film deposited in the first deposition step is inferior. Example 27 Following the same procedure as in Example 26 to set the parameters as follows: during the first deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻⁵ Torr Si₂H₆ partial pressure: 1.5 x 10⁻⁷ Torr Substrate temperature: 270°C or 300°C during the second deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻³ Torr Si₂H₆ partial pressure: 1.5 x 10⁻⁵ Torr and the substrate temperature of the second deposition step was varied at 13 levels. And various evaluation results of the Al-Si film deposited were the same as in Table 4. When the substrate temperature in the first deposition step is 270 °C or 300 °C, there is no difference in the results obtained. Similarly as in Example 20, when the substrate temperature in the second step exceeds 300 °C, high speed deposition at 0.5 to 1.0 µm/min. was possible. The difference from Example 20 is that an Al-Si film with high surface flatness having a reflectance of 80 to 95 % could be formed even when the substrate temperature in the second step was 330 °C, 350 °C. Similarly as in Example 20, Al-Si was selectively deposited only on Si. Also, even when Al-Si was deposited to 2µm, the selective depositability was maintained. Example 28 Following the same procedure as in Example 27 to set the parameters as follows: during the first deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻⁵ Torr Substrate temperature: 270 °C during the second deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻³ Torr Substrate temperature: 330 °C and the Si₂H₆ partial pressure was varied from 3 x 10⁻⁴ to 0.2 fold of DMAH partial pressure to effect deposition. The Si content (wt.%) of the Al-Si films were varied from 0.005 % to 5 % approximately in proportion to the Si₂H₆ partial pressure. As to resistivity, carbon content, average wiring life, deposition speed, hillock density and spike generation, the same results as in Example 1 were obtained. However, in samples having a Si content of 4 % or higher, deposition was generated in the films which appeared to be Si to worsen slightly surface morphology, thereby making the reflectance 66 % or lower. Samples having a Si content of less than 4 % exhibited a reflectance of 80 to 95 %, which was similarly good as in example 27. Similarly as in Example 27, the selective depositability based on the substrate surface material was confirmed at the whole region. Example 29 This Example 29 performs Al-Si deposition by use of Ar in place of H₂ as the carrier gas for DMAH in the same procedure as in Example 26. The second gas line fed H₂. Similarly the same results as in Table 3 in Example 20, no Al-Si was deposited on SiO₂ at a temperature range from 160°C to 450°C, and Al-Si was deposited only on the portion with opening of SiO₂ to have Si exposed. Also, when 2µm of Al-Si deposition was carried out in the above temperature range continuously, similar selective depositability was maintained. When the substrate temperatures in the first and second deposition steps exceed 300 °C, high speed deposition at 0.5 to 1.0 µm/min. was possible, but the probability that surface reflectance becomes more or less worse is slightly enhanced. The reason may be considered to be due to the fact that, if the temperature in the first deposition step is high, flatness of the extremely thin Al-Si film deposited in the first deposition step is inferior. Example 30 This Example 30 performs Al-Si deposition by use of Ar in place of H₂ as the carrier gas for DMAH in the same procedure as in Example 27. The second gas line fed H₂. When the substrate temperatures in the first deposition step were 270 °C and 300 °C, there was no difference in the results obtained. The film quality obtained is substantially the same as in Table 4. Similarly as in Example 7 or 27, when the substrate temperature in the second step exceeds 300 °C, high speed deposition at 0.5 to 1.0 µm/min. was possible. The difference from Examples 26 and 27 is that an Al-Si film with high surface flatness having a reflectance of 80 to 95 % could be formed even when the substrate temperatures in the second step were 330 °C and 350 °C. Similarly as in Examples 26 and 27, Al selectively deposited only on Si. Also, even when Al-Si was deposited to 2µm, the selective depositability was maintained. Example 31 This Example 31 performs Al-Si deposition by use of Ar in place of H₂ as the carrier gas for DMAH in the same procedure as in Example 28. The second gas line fed H₂. Deposition condition was shown below. during the first deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻⁵ Torr Substrate temperature: 270 °C during the second deposition step, Total pressure: 1.5 Torr DMAH partial pressure: 1.0 x 10⁻³ Torr Substrate temperature: 330 °C and the Si₂H₆ partial pressure was varied from 3 x 10⁻⁴ to 0.2 fold of DMAH partial pressure to effect deposition. Similarly as in Example 28, the Si content (we.%) of the Al-Si films were varied from 0.005 % to 5 % approximately in proportion to the Si₂H₆ partial pressure. As to resistivity, carbon content, average wiring life, deposition speed, hillock density and spike generation, the same results as in Example 20 were obtained. However, in samples having an Si content of 4 % or higher, deposition was generated in the films which appeared to be Si to worsen slightly surface morphology, thereby making the reflectance 65 % or lower. Samples having a Si content of less than 4 % exhibited a reflectance of 80 to 95 %, which was similarly good the same as in Example 27. Also, similarly as in Example 26, the selective depositability based on the substrate surface material was confirmed at the whole region. Example 32 By means of the low pressure CVD device shown in Fig. 3, Al-Si films were formed on the substrates with the constitutions as described below (Samples 5-1 - 5-179). Preparation of Sample 5-1 On a monocrystalline silicon as the electron donative first substrate surface material, a thermally oxidized SiO₂ film as the electron non-donative second substrate surface material was formed, and patterning was effected according to the photolithographic steps as shown in Example 7 to have the monocrystalline surface partially exposed. The film thickness of the thermally oxidized SiO₂ film was found to be 7000 Å, with the size of the exposed portion of the monocrystalline silicon, namely opening being 3 µm x 3 µm. Thus, Sample 5-1 was prepared. (Hereinafter, such sample is expressed as "thermally oxidized SiO₂ (hereinafter abbreviated as T-SiO₂)/monocrystalline silicon"). Preparation of Samples 5-2 - 5-179 Sample 5-2 is an oxidized film formed by normal pressure CVD (hereinafter abbreviated as SiO₂)/monocrystalline silicon. Sample 5-3 is a boron doped oxidized film formed by normal pressure CVD (hereinafter abbreviated as BSG)/monocrystalline silicon. Sample 5-4 is a phosphorus doped oxidized film formed by normal pressure CVD (hereinafter abbreviated as BSG)/monocrystalline silicon. Sample 5-5 is a phosphorus and boron doped oxidized film formed by normal pressure CVD (hereinafter abbreviated as BSPG)/monocrystalline silicon. Sample 5-6 is a nitrided film formed by plasma CVD (hereinafter abbreviated as P-S:N)/monocrystalline silicon. Sample 5-7 is a thermally nitrided film (hereinafter abbreviated as T-S:N) /monocrystalline silicon. Sample 5-8 is a nitrided film formed by low pressure CVD (hereinafter abbreviated as LPS:N)/monocrystalline silicon. Sample 5-9 is a nitrided film formed by ECR device (hereinafter abbreviated as ECR-SiN)/monocrystalline silicon. Further, by combinations of the electron donative first substrate surface materials and the electron non-donative second substrate surface materials, Samples 5-11 - 5-179 shown in Table 5 were prepared. As the first substrate surface material, monocrystalline silicon (monocrystalline Si), polycrystalline silicon (polycrystalline Si), amorphous silicon (amorphous Si), tungsten (W), molybdenum (Mo), tantalum (Ta), tungsten silicide (WSi), titanium silicide (TiSi), aluminum (Al), aluminum silicon (Al-Si), titanium aluminum (Al-Ti), titanium nitride (Ti-N), copper (Cu), aluminum silicon copper (Al-Si-Cu), aluminum pelladium (Al-Pd), titanium (Ti), molybdenum silicide (Mo-Si), tantalum silicide (Ta-Si) were employed. These samples were placed in the low pressure CVD device shown in Fig. 3, and Al-Si films were formed within the same batch. The deposition conditions were as follows: during the first deposition step, Total pressure: 0.3 Torr DMAH partial pressure: 3 x 10⁻⁶ Torr Si₂H₆ partial pressure: 1 x 10⁻⁷ Torr Substrate temperature: 270°C during the second deposition step, Total pressure: 0.3 Torr DMAH partial pressure: 1 x 10⁻⁴ Torr Si₂H₆ partial pressure: 3 x 10⁻⁶ Torr Substrate temperature: 330°C As the result of film formation under such conditions, concerning all the samples applied with patterning from Sample 5-1 to 5-179, deposition of Al-Si film occurred only on the electron donative first substrate surface film to embed completely the opening with the depth of 7000 Å. The film quality of the Al-Si film formed is not different from those at a substrate temperature in the second deposition of 330°C in Table 2 as described above, and also the deposition rate in the second deposition step was very high as ca. 0.7 µm/min. for all of the substrates. Example 33 According to the same procedure as in Example 27, Al-Si film was deposited by the use of MMAH₂ in place of DMAH. As the substrate, Si wafer obtained by patterning the same SiO₂ thin film as shown in Example 26. The deposition conditions at this time are as follows: during the first deposition step, Reaction tube pressure: 1.5 Torr MMAH₂ partial pressure: 5 x 10⁻⁵ Torr Si₂H₆ partial pressure: 1 x 10⁻⁶ Torr Substrate temperature: 270°C during the second deposition step, Reaction tube pressure: 1.5 Torr MMAH₂ partial pressure: 1 x 10⁻³ Torr Si₂H₆ partial pressure: 1 x 10⁻⁵ Torr Similarly as in Example 27, Al-Si film embedded completely the SiO₂ opening with the depth of 7000 Å and the film quality of deposited Al-Si was not different from one at a substrute temperature in the second deposition step of 330°C in Table 2. Also, the deposition rate of Al-Si in the second deposition step was ca. 0.7 µm/min. and not substantially different from the case of using DMAH. Example 34 According to the same procedure as in Example 27, Al-Si film was deposited by the use of SiH₄ in place of Si₂H₆. As the substrate, Si wafer obtained by patterning the same SiO₂ thin film as shown in Example 1. The deposition conditions at this time are as follows: during the first deposition step, Reaction tube pressure: 1.5 Torr DMAH partial pressure: 1 x 10⁻⁵ Torr Si₂H₆ partial pressure: 5 x 10⁻⁷ Torr Substrate temperature: 270°C during the second deposition step, Reaction tube pressure: 1.5 Torr DMAH partial pressure: 1 x 10⁻³ Torr Si₂H₆ partial pressure: 5 x 10⁻⁵ Torr Substrate temperature: 330°C. Similarly as in Example 27, Al-Si film embedded completely the SiO₂ opening with the depth of 7000 Å and the film quality of deposited Al-Si was not different from one at a substrate temperature in the second deposition step of 330°C in Table 4. Also, the deposition rate of Al-Si in the second deposition step was ca. 0.7 µm/min. and not substantially different from the case of using Si₂H₆. Example 35 According to the same method as in Example 20, a sample having an Al film formed thereon was prepared. The crystallinity of the Al film selectively deposited on Si at the same substrate temperature as in Table 1 was evaluated by the X-ray diffraction method and the scanning µ-RHEED microscope. The scanning µ-RHEED microscope is the method disclosed in Extended Abstracts of the 21th Conference on Solid State Devices and Materials (1989) p.217 and Japanese Journal of Applied Physics vol. 28, No. 11 (1989), L2075. According to the RHEED (Reflection High Energy Electron Diffraction) method of prior art, electron beam was permitted to be incident on the sample surface at a shallow angle of 2 - 3°, and the crystallinity of the sample surface was evaluated from the diffraction pattern formed by the diffracted electron beam. However, since the electron beam diameter is large as 100 µm to several hundred µm, only average information on the sample surface could be obtained. In the µ-RHEED microscope, an electron beam diffraction pattern from a specific fine region on the sample surface can be observed by narrowing the electron beam diameter of 0.1 µm. Also, by scanning the electron beam two-dimensionally on the sample surface, by use of any desired diffraction spot intensity change on the diffraction pattern as the image signal, two dimensional image (scanning µ-RHEED image) on the sample surface can be obtained. At this time by observation of the scanning µ-RHEED image by use of different diffraction spots A and C on the diffraction pattern as shown in Fig. 8, even if the lattice planes in parallel to the sample surface may be aligned in (100), the crystal grain boundaries rotating within the plane can be visualized as distinguished from each other. Here, the diffraction spot A is a diffraction spot on the line (line 1) where the plane in which the diffraction pattern occurs and the sagittal plane formed by the incident electron beam are crossed at right angle, while the diffraction spot C is a diffraction spot not on the line 1. As shown in Fig. 9, when the lattice plane in parallel to the sample surface is, for example, (100), but crystal grains x and y are rotating mutually within the plane, in the scanning µ-RHEED image by use of the diffraction spot A, both crystal grains x and y are displayed as the region with strong intensity. On the other hand, in the scanning µ-RHEED image by use of the diffraction spot C, only the crystal grain x is displayed as the region with strong intensity. Therefore, by observation of the scanning µ-RHEED image by use of the diffraction spots A and C as shown in Fig. 8, it can be discriminated whether the crystal in the region observed is a polycrystal including interplanar rotation or a monocrystal. In Extended Abstracts of the 21th Conference on Solid State Devices and Materials (1989) p.217 and Japanese Journal of Applied Physics vol. 28, No. 11 (1989) L2075, concerning Cu thin film, it has been clarified that, for example, even if the lattice plane in parallel to the sample surface may be {100}, there exists a crystal grain including interplanar rotation in the {100} crystal grains. First, the Al film deposited selectively on the Si exposed surface at the substrate temperature in Table 1 was evaluated. When the crystal direction on the Si substrate surface is (111) plane, from X-ray diffraction, concerning Al, as shown in Fig. 10, only the diffraction peak showing Al (100) could be observed. Next, crystallinity of the Al film deposited selectively was evaluated by use of a scanning µ-RHEED microscope. As shown in Fig. 11, after the region where Al had been selectively deposited was specified by the scanning secondary electron image showing the surface form (Fig. 11A), by use of the diffraction spot 200 (corresponding to the diffraction spot A in Fig. 8) and the diffraction spot 620 (corresponding to the diffraction spot C in Fig. 8) on the diffraction pattern occurring when the electron beam was permitted on the Al (100) plane from the [001] direction, the scanning µ-RHEED image (Fig. 11B and Fig. 11C) was observed. As shown schematically in Fig. 11B and Fig. 11C, there is no change in lightness and darkness on the Al film selectively deposited, and the Al selectively deposited was confirmed to be an Al (100) monocrystal. On the other hand, when the Si exposed plane is not linear but like via-hole, irrespectively of the via-hole diameter, the Al selectively deposited was found to be similarly Al (100) monocrystal. Those at substrate temperatures ranging from 250 °C to 330 °C were selectively deposited stably, and the Al obtained was found to become monocrystal. Also, Al films deposited selectively on the Si (111) substrate with the Si (111) plane being at off-angles by 1°, 2°, 3°, 4°, 5° from the Si substrate were also found to deposit Al (100) monocrystals under the temperature conditions of the substrate temperature ranging from 250 °C to 330 °C similarly as deposited on the Si (111) substrate as described above. When the crystal direction of the Si substrate surface is the (100) plane, from X-ray diffraction, concerning Al, as shown in Fig. 12, only the diffraction peak showing Al (111) could be observed. Fig. 13 shows the scanning secondary electron image (Fig. 13A) and the scanning µ-RHEED image (Figs. 13B and 13C) when Al was selectively deposited on only the Si exposed surface on a substrate having Si (100) exposed in a line by patterning of SiO₂ in a line. For the scanning µ-RHEED image, the 333 diffraction spots (Fig. 13B) and 531 diffraction spots (Fig. 13C) were employed. The Al film selectively deposited was confirmed to be an Al (111) monocrystal. Those at substrate temperatures ranging from 250 °C to 330 °C were found to be selectively deposited stably, and the Al films obtained became monocrystals. Also, Al films deposited selectively on the Si (100) substrate with the Si (100) plane being at off-angles by 1°, 2°, 3°, 4°, 5° from the Si substrate surface were also found to deposit Al (111) monocrystals under the temperature conditions of the substrate temperature ranging from 250 °C to 330 °C similarly as deposited on the Si (111) substrate as described above. Example 36 Samples having Al films formed according to the same method as in Example 21 were prepared. When crystallinity of the Al film selectively deposited on the Si exposed surface by use of the X-ray diffraction method and the scanning µ-RHEED microscope, it was found to be as described below. When the crystal direction of the Si substrate is (111) plane, from X-ray diffraction, as shown in Fig. 10, only the diffraction peak showing Al (100) was observed. The Al film selectively deposited was evaluated by use of the scanning µ-RHEED microscope and it was found to be Al (100) monocrystal similarly the same as in Example 20. Also, the Al films deposited on the Si (111) substrate with the substrate surface having off-angles differing by 1°, 2°, 3°, 4°, 5° from the Si (111) plane were also found to have Al (100) monocrystals deposited stably under the temperature conditions of the first and second substrate temperature ranging from 250 °C to 330 °C similarly as in the case when deposited on the Si (111) substrate as described above. When the crystal direction of the Si substrate is (100) plane, from X-ray diffraction, as shown in Fig. 12, only the diffraction peak showing Al (111) was observed concerning Al. Also the Al film selectively deposited was evaluated by use of the scanning µ-RHEED microscope and it was found to be Al (100) monocrystal similarly the same as in Example 20. Within the second substrate temperature range in Table 4, those deposited at a range from 270 °C to 330 °C were found to have Al films deposited which were stably monocrystalline. Also, the Al films deposited on the Si (100) substrate with the substrate surface having off-angles differing by 1° 2°, 3°, 4°, 5° from the Si (100) plane were also found to have Al (111) monocrystals deposited under the temperature conditions of the second substrate temperature ranging from 270 °C to 330 °C, similarly as in the case when deposited on the Si (111) substrate as described above. Example 37 Crystallinity of the Al film selectively deposited by the method of Example 22 was examined. Similarly as in the case of Example 20, at a substrate temperature of the first and second substrate in Table 2 ranging from 250°C to 330°C, Al(100) monocrystal was deposited on the Si (111) substrate, and Al (111) monocrystal on the Si (100) substrate. Example 38 Crystallinity of the Al film selectively deposited by the method of Example 23 was examined. Similarly as in the case of Example 1, at a substrate temperature of the second substrate in Table 2 ranging from 270°C to 330°C, Al (100) monocrystal was deposited on the Si (111) substrate, and Al (111) monocrystal on the Si (100) substrate. Example 39 Crystallinity of the Al film deposited selectively according to the same method as shown in Example 24 was evaluated. From the scanning µ-RHEED microscope observation according to the same observation method as described in Example 35, when the first substrate material is Si (111), in either case when the second substrate material is T-SiO₂, SiO₂, BSG, PSG, BPSG, P-SiN, T-SiN, LP-SiN or ECR-SiN, the Al selectively deposited on Si was found to be Al (100). When the first substrate material is Si (100), in either case when the substrate material is T-SiO₂, SiO₂, BSG, PSG, BPSG, P-SiN, T-SiN, LP-SiN or ECR-SiN, the Al film selectively deposited was found to be Al (111). When the first material is TiN, in either case when the second substrate material is T-SiO₂, SiO₂, BSG, PSG, BPSG, P-SiN, T-SiN, LP-SiN or ECR-SiN, the Al film selectively deposited was found to be oriented in Al (111) from X-ray diffraction, and from reflective high speed electron beam diffraction pattern of the prior art by use of an electron beam of an acceleration voltage of 80 kV or 100 kV, diffraction spots concerned with Al (111) were strongly observed. Example 40 As an example for forming source-drain electrodes of gate insulation type transistor, electrode formation within the contact hole on the source-drain was carried out by use of the film formation method according to the present invention. This is described by referring to Fig. 14. First, on a p-type silicon wafer 501, by use of conventional selective oxidation method, etc. a thick field oxidized film and a thin thermally oxidized film 502 were formed on the wafer 501 (Fig. 14A). Next, with the use of SiH₄ gas as the starting gas, a polycrystalline silicon layer was formed by the thermal CVD method, a polycrystalline silicon gate electrode 504 was formed, and also with the thick field oxidized film and the gate electrode 504 as the mask, phosphorus was ion injected self-matchingly to form an impurity diffused region 505 of 1 x 10¹⁸ cm⁻³ (Fig. 14B). Next, an oxidized silicon film 508 was formed by use of the thermal CVD method (Fig. 14C). By use of the lithographic method, a contact hole 509 with a size of 0.5 µm x 0.5 µm was formed (Fig. 14D). By transferring the substrate thus obtained to the device shown in Fig. 1, Al film was formed. At this time, the substrate temperature was made 270 °C, and DMAH was employed as the starting gas, H₂ as the carrier gas to carry out formation of Al film. After completion of formation of Al film, the transistor was taken out from the film forming device and observed. As the result, it was found that Al film 510 was deposited only on the Si 505 wherein phosphorus was diffused in the contact hole 509, and not deposited on the oxidized film 508 (Fig. 14E). Further, the surface of the Al film 510 was very flat. When the characteristics of the transistor obtained were examined, extremely good characteristics were exhibited. Separately, according to the same steps, the substrate was made N type and the impurity was changed from phosphorus to boron to prepare P channels MoS. Comparative example An Al film was formed on a monocrystalline silicon under the following conditions. By passing Ar in place of H₂, Al was deposited by pyrolysis of DMAH. The total pressure at this time was made 1.5 Torr, the DMAH partial pressure 1.5 x 10⁻⁴ Torr, and the substrate temperature of 270 - 350 °C. When the Al film thus formed was evaluated, about 2 % of carbon was found to be contained at the minimum. Resistivity became greater by 2-fold or more than the case when hydrogen was employed. As to reflectance, it was lowered to about 1/3 to 1/9 relative the case when hydrogen was employed. Similarly, wiring life was shorter by 1 to 2 cipher, generation probability of hillock became greater by 2 cipher or more, and a large number of spikes were found to be generated. As to the deposition speed, it was lowered to 1/2 to 1/4. As described above, Al deposited only by decomposition of DMAH without use of H₂ is inferior in film quality, and was unsatisfactory as the Al film for a semiconductor device. Separately, without use of H₂, DMAH was decomposed by the optical CVD method to deposit Al. As the result, some improvement such as no containment of carbon, and the like was observed from as the Al film prepared as compared with the case when no light was employed, but other characteristics were not improved so much, and the Al film was still unsatisfactory as the Al film for a semiconductor device. As described above, the mechanism of Al deposition according to the present invention may be presently hypothesized as follows. When DMAH reaches the electron donative substrate, namely the substrate having electrons under the state on which hydrogen atoms are attached (Fig. 15A) with the methyl groups directed toward the substrate side, one electron of the substrate cuts one bond of Al and a methyl group (Figs. 15B and 15C). The reaction scheme at this time is as follows: (CH₃)₂AlH + 2H + 2e → 2CH₄↑ + Al-H Further, simile reactions will proceed for the hydrogen atoms remaining on deposited Al having free electrons (Fig. 15D). Here, when hydrogen atoms are deficient, hydrogen molecules constituting the reaction gas are decomposed on the substrate to supply hydrogen atoms. On the other hand, since there is no electron on the electron non-donative surface, the above-mentioned reaction will not proceed and no Al deposited. Figs. 15A - 15D are illustrations for better understanding of the reacion mechanism, and the numbers of H, e and Al shown in Figs. 15A - 15D are not necessarily coincident. In the case of an Al-Si film, Si atoms are incorporated into Al during the process of the reaction as described above. As described above, according to the present invention, a low resistivity, dense and flat Al or Al-Si film could be deposited on a substrate at high speed. Also, excellent selective deposition could be effected. Average wiring life is time to wire breaking when current is passed at a current density of 1 x 10⁶ A/cm² through a cross-sectional area of 1 µm² at 250°C. Spike generation ratio is destruction probability at the junction portion of 0.15 µm depth.

Claims: A process of forming a deposited film comprising the steps of: (a) providing in a space for formation of a deposited film a substrate having a surface of a metallic material, a semiconductor or a very thin oxidized film provided on a metal or semiconductor; (b) introducing into the film deposition space gaseous hydrogen and a gaseous alkyl aluminium hydride; (c) maintaining the electron donative surface at a temperature from the decomposition temperature of the alkyl aluminium hydride to 450°C to form on the surface a film composed mainly of aluminium; and (d) varying the deposition speed of the film so that at the beginning of deposition the film is deposited at a lower rate of 0.01-0.08 µm/min and subsequently the film is deposited at a rate higher than said lower rate. The process of claim 1, wherein the substrate is of monocrystalline silicon. The process of claim 1, wherein the substrate is of polycrystalline silicon. The process of calim 1, wherein the substrate is of amorphous silicon. The process of claim 1, wherein the substrate is a III-V compound semiconductor, a II-VI semiconductor, a metal or a metal silicide. The process of any preceding claim, wherein the substrate also has a surface on which the film does not deposit, the surface being of silicon oxide, glass or silicon nitride. The process of claim 6, wherein the substrate is a semiconductor substrate having an insulating film that provides the electron non-donative surface and which is provided with at least one opening through which the semiconductor is exposed so that the film is deposited selectively in the opening. The process of claim 7, wherein the substrate is of silicon having an oxide film patterned with holes of size from 0.25µm x 0.25µm to 100µm x 100µm through which silicon is exposed. The process of any preceding claim, wherein the alkyl aluminium hydride is dimethyl aluminium hydride. The process of claims 1-8, wherein the alkyl aluminium hydride is monomethyl aluminium hydride. The process of any preceding claim, wherein the substrate temperature is 270-350°C. The process of any preceding claim, wherein film is deposited at said lower rate to a thickness of 100-200Å, after which the rate of deposition is increased. The process of claim 12, wherein after the initial deposition, film is deposited at a speed of 0.2 to 1µm/min. The process of any preceding claim, wherein the film is deposited by hot wall reduced pressure CVD in which only the substrate is heated. The process of any preceding claim, wherein the rate of deposition is increased by increasing the temperature of the substrate. The process of claim 15, wherein during said lower rate of deposition the substrate is at 270-300°C and during the higher rate of deposition it is at 300-350°C. The process of any preceding claim, wherein the rate of deposition is increased by increasing the partial pressure of the alkyl aluminium hydride. The process of claim 17, wherein the partial pressure of the alkyl aluminium hydride is initially 1.3 x 10⁻⁵ to 1.3 x 10⁻⁴ of the total pressure in the reaction space and is subsequently 1.3 x 10⁻⁴ to 1.3 x 10⁻³ of the total pressure in the reaction space. The process of any preceding claim, wherein there is also introduced into the film formation space a silicon containing gas so that the film deposited on the surface is of Al-Si. The process of claim 19, wherein the silicon containing gas is Si₂H₆. The process of claim 19, wherein the partial pressure of the Si₂H₆ is with the range 1 x 10⁻⁷ to 1 x 10⁻⁴ of the pressure with the reaction space. The process of claim 20 or 21, wherein the partial pressure of both the alkyl aluminium hydride and Si₂H₆ is increased when the film is deposited at the higher rate. A process for making a semiconductor integrated circuit device which includes the step of forming wiring by the process claimed in any of claims 1-22.

Inventors: MASU KAZUYA, MIKOSHIBA NOBUO, TSUBOUCHI KAZUO, MASU, KAZUYA, MIKOSHIBA, NOBUO, TSUBOUCHI, KAZUO
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1990
Main classification: H01L21
IPC codes: H01L21