Coating powder composition

Abstract: A coating powder composition comprising (A) a carboxyl group containing polyester resin having a number average molecular weight of 1,000-20,000, an acid value of 10-100, a glass transition temperature of 35 to 120°C and a SP value of 9.8-11.5, and (B) glycidyl trimellitate, the equivalent wight ratio of carboxyl groups of (A) to glycidyl groups of (B) being 1:2 to 2:1, which is specifically suitable for high-temperature-short time baking and capable of providing a coating with excellent film properties including bending and processability and being highly-crosslinked.

Description: The present invention relates to coating powder composition which is specifically suitable for a high-temperature-short time baking and capable of resulting a coating which is highly crosslinked and excellent in film properties, especially with respect to processability and bending properties. Recently, public attentions have been directed to a coating powder comprising, as principal ingredients, a polyester resin and a crosslinking agent, as a pollution-free coating composition capable of resulting a coating which is excellent in corrosion resistance, chemical resistance, mechanical strength and adhesion to steel or the like. Usually, a blocked polyisocyanate compound is used as a crosslinking agent for hydroxyl group bearing polyester resin, and however, in this combination, blocking agent used is vaporized at the baking stage of the formed coating, causing troubles in working. Therefore, much preference is given to the combination of carboxyl bearing polyester resin and a crosslinking agent selected from glycidyl or oxirane group bearing epoxy resin or compound, excepting a toxic triglycidyl isocyanurate. Examples of such crosslinking agents are bifunctional epoxy resins or compounds as bisphenol type glycidyl ether, diglycidyl ether of dialcohol (Japanese Patent Publication (unexamined) 151224/75), diglycidyl terephthalate (Japanese Patent Publication (unexamined) 243176/88) and the like, and polyfunctional epoxy resins or compounds as aliphatic hydrocarbon glycidyl ether, novolak type epoxy resin (Japanese Patent Publication (unexamined) 28092/72) and the like. Among them, with the increase in demands of coating powder which is specifically suitable for a high-temperature and short time baking as required for the coating of electrical appliances, office supplies or the like, people attach much importance to trifunctional or more highly functional epoxy resins or compounds to increase the crosslinking density. However, heretofore proposed aliphatic hydrocarbon glycidyl ethers could not give the desired increase in the degree of crosslinking and novolak type epoxy resins, though the degree of crosslinking might be increased, would inevitably cause the decrease in bending processability and often result a yellowish coating. Thus, none of the known polyfunctional epoxy resins or compounds could satisfy the requirements of improvements in degree of crosslinking and bending properties, simultaneously. It is, therefore, an object of the invention to find out a polyfunctional epoxy resin or compound which is free from dermal toxity and easy to operation and which is useful as a crosslinking agent for carboxyl group containing polyester resin, giving a highly crosslinked resin with excellent properties and especially bending property. The principal object of this invention is to provide a coating powder composition comprising such polyfunctional epoxy resin or compound and carboxyl group containing polyester resin, which is suitable for a high temperature and short time baking and capable of producing a coating with excellent solvent resistance, impact resistance, bending property and other mechanical strength. According to the present invention, the abovementioned objects can be attained by providing a coating powder composition comprising, as principal ingredients, (A) a carboxyl group containing polyester resin prepared by the reaction of at least one polybasic acid and at least one polyhydric alcohol and having a number average molecular weight of 1,000 to 20,000, an acid value of 10 to 100, a glass transition temperature of 35 to 120°C and a SP value of 9.8 to 11.5, wherein 75% or more by weight of the polyhydric alcohol of the polyester resin is neopentyl glycol, and (B) glycidyl trimellitate, equivalent weight ratio of carboxyl groups of said (A) to glycidyl groups of said (B) being 1:2 to 2:1. The Inventors, having studied on various combinations of carboxyl bearing polyesters and polyfunctional epoxy compounds, have found that particular combinations of specific polyester resins and glycidyl trimellitate are suitable for a high-temperature short period baking and are useful as resinous components for coating powder capable of resulting a coating with excellent solvent resistance, impact resistance, bending properties and other mechanical strength. On the basis of said finding the present invention has been made. The polyester resin used in the invention should have a number average molecular weight of 1,000 to 20,000. If the number average molecular weight is less than 1,000, there will result a coating with deficient film strength, whereas if it exceeds over the upper limit of 20,000, it is unable to obtain a good appearance coating because of insufficient flowability of the polyester resin. Secondary, such polyester resin should have a glass transition temperature (Tg) of 35∼120°C, there is an undesired lowering in blocking resistance of the coating powder and if it exceeds over 120°C, in want of flowability of the coating formed. The polyester resin should also have an acid value of 10 to 100. If the acid value is less then 10, there results a coating with deficient film strength and if it is more than 100, a coating with deficient flexibility. Furthermore, the polyester resin should have a SP value of 9.8 to 11.5. This requirement should be cleared out, because of the adoption of particular epoxy compound, i.e. glycidyl ester of trimellitic acid, as a crosslinking agent, in this invention. If the SP value of polyester resin is less than 9.8 or more than 11.5, such polyester resins are hardly compatible with the abovementioned epoxy compound, and hence, there result coatings with deficient film strength and it is unable to attain the objects of this invention. As far as the abovementioned requirements are fulfilled, any of the known, coating use polyester resins may be satisfactorily used as the carboxyl group containing polyester component in the present invention. As an acidic component of such polyester resin, any of the following may be advantageously used: terephthalic acid, isophthalic acid, phthalic acid, methyl phthalic acid, trimellitic acid, pyromellitic acid, adipic acid, sebacic acid, succinic acid, maleic acid, fumaric acid, tetrahydrophthalic acid, methyl tetrahydrophthalic acid, hexahydrophthalic acid, and their reactive derivatives, as, for example, acid anhydride, acid halide, acid ester and the like. The inventors have also found that when the alcohol component consists of 75% or more of the total alcohol of neopentyl glycol and 25% or less of other alcohol, there results a coating with particularly excellent weather resistance in this invention. As the other component of alcohol, the following may be advantageously used: ethylene glycol, propylene glycol, 1,3-butanediol, 1,4-butanediol, 1,6-hexanediol, diethylene glycol, dipropylene glycol, 1,4-cyclohexane dimethanol, 1,4-cyclohexanediol, neopentyl glycol, isopentyl glycol, bishydroxyethyl terephthalate, hydrogenated bisphenol A, hydrogenated bisphenol A-alkylene oxide addition product, trimethylol ethane, trimethylolpropane, glycerin, pentaerythritol and the like. A compound having both acidic group and hydroxyl group may also be used as a reactive polyfunctional compound. Polyester forming reaction may be carried out in one step or in several steps as known in the art. Tg and SP values of the polyester resin may be easily controlled by those skilled in the art by the selection of types and amounts of the starting materials used and number average molecular weight and acid value by the selection of reaction conditions adopted. Therefore, it would not be necessary to explain the details herein. In this invention, the abovementioned carboxyl group containing polyester resin is co-used with a particular crosslinking component of glycidyl trimellitate. At that time, both components should be compounded so as to give the equivalent weight ratio of carboxyl groups to glycidyl groups of 1:2 to 2:1, preferably 1:2 to 1.5:1. This is because, if the said equivalent weight ratio is lower than 1:2, there results a coating with deficient crosslinking and if it exceeds over 2:1, a coating with deficient bending property due to far advanced crosslinking. By the selective use of the abovementioned polyester resin and the particular crosslinking agent, it is possible to prepare coating powder which may result a coating, by a high-temperature and short time baking, e.g. 250°C-5 minutes baking, highly crosslinked and having excellent film properties and especially bending property. The inventors have also found that even if the glycidyl trimellitate of the abovementioned composition is replaced up to 40% by weight by diepoxide having in its molecule, two glycidyl groups and/or aliphatic glycidyl ether having in its molecule three glycidyl groups, the similar effects of the invention can be attained with thus obtained composition, and in that case, boiling water resistance of the formed coating is greatly improved. Therefore, in a particularly preferable embodiment of this invention, is provided a coating powder composition comprising, as principal ingredients, (A) carboxyl group containing polyester resin prepared by the reaction of at least one polybasic acid and at least one polyhydric alcohol and having a number average molecular weight of 1,000 to 20,000, an acid value of 10 to 100, a glass transition temperature of 35 to 120°C and a SP value of 9.8 to 11.5, (B) glycidyl trimellitate, and (C) diepoxide having in its molecule two glycidyl groups and/or aliphatic glycidyl ether having in its molecule three glycidyl groups, the amount of said (C) being up to 40% by weight of said (B) and equivalent weight ratio of carboxyl groups of said (A) to glycidyl groups of said (B) and (C) being 1:2 to 2:1. Examples of diepoxide having in its molecule two epoxy groups are (1) glycidyl ethers obtained by the reaction of phenolic compounds as 2,2-bis(4′-hydroxyphenyl)propane (bisphenol A) and the like, and epichlorohydrin; (2) glycidyl ethers obtained by the reaction of alcohols and epichlorohydrin, as, for example, diglycidyl ether of butanediol, diglycidyl ether of polypropylene glycol, diglycidyl ether of neopentyl glycol; (3) glycidyl ethers obtained by the reaction of carboxyl bearing compounds as adipic acid, phthalic acid and the like and epichlorohydrin, as, for example, diglycidyl butyrate, diglycidyl terephthalate, diglycidyl isophthalate, diglycidyl phthalate, diglycidyl ester of linoleic dimer acid; and (4) styrene oxide derived from mono-unsaturated compound, or inner epoxy type compound synthesized by the oxidation of intramolecular double bond, and the like. Among them, particular preference is given to diglycidyl ether of bisphenol A, diglycidyl ester of butyric acid and the like. Examples of aliphatic glycidyl ether having in its molecule three glycidyl groups are diglycerol polyglycidyl ether, trimethylolpropane polyglycidyl ether, glycerol polyglycidyl ether and the like. In the present composition, various additives may be added as desired. Examples of these additives are: (a) surface conditioner for the improvement in smoothness and control of cratering of coating, as long chain alkyl esters of acrylic acid, polysiloxane and the like; (b) color pigment including both inorganic pigments as titanium dioxide, iron oxide, iron oxide yellow, carbon black and the like, and organic pigments as phthalocyanine blue, phthalocyanine green, quinacridone red pigment and the like; (c) plasticizer as, for example, polyalkylene polyol, phthalic acid ester and the like; (d) anti-oxidant; (e) pinhole controlling agent as benzoin and the like; (f) epoxy compound and the like. In preparing coating powder from the present coating powder composition, any of the conventional methods may be advantageously used. For example, the defined constituting components are mixed together, melt-kneaded, allowed to cool and pulverized; or each of the components is dissolved in a solvent, the formed solutions are mixed together and thus obtained solution is then subjected to spray-drying to obtain coating powder. The present coating powder may be advantageously applied onto a substrate by using any of the conventional means, as, for example, electrostatic spraying, fluidized bed coating and the like. The invention shall be now more fully explained in the following examples. Unless otherwise being stated, all parts and % are by weight. Examples 1 to 3 and Comparative Examples 1 to 6 In each experiment, the indicated amounts of carboxyl group containing polyester resin, cross-linking agent and other additives shown in Table 1 were pre-mixed, melt-mixed at 100°C, and the melt allowed to cool, and the solid mass pulverised to obtain a coating powder. In the following Table 1, V-73-9 is a carboxyl group containing polyester resin manufactured by EMS, having a number average molecular weight of 4,000, Tg value of 48, acid value of 33 and SP value of 10.6. The alcoholic component consists of 95 weight per cent of neopentyl glycol and 5 weight per cent of other polyhydric alcohol. D-19-5 is a carboxyl group containing polyester resin manufactured by Nihon Upica K.K., having a number average molecular weight of approximately 4,500, Tg value of 56, acid value of 29 and Sp value of 10.8. The alcoholic component consists of 52 weight per cent of neopentyl glycol and 48 weight per cent of other polyhydric alcohol. Finedic M-8630 is a carboxyl group containing polyester resin manufactured by Dainippon Ink K.K., having a number average molecular weight of 4,500, Tg of 51, acid value of 25 and SP value of 10.6. The alcoholic component consists of 60 weight per cent of neopentyl glycol and 40 weight per cent of other polyhydric alcohol. Finedic M-8076 is a hydroxyl group containing polyester resin manufactured by Dainippon Ink K.K., having a number average molecular weight of 4,000 and a hydroxyl value of 43; Resin A used for comparison purpose is a carboxyl containing polyester resin prepared by the reaction of terephthalic acid, hexahydrophthalic acid and cyclohexanedimethanol, having a number average molecular weight of 4,500, acid value of 33, Tg value of 55 and SP value of 9.5; YD-128 is a bisphenol A glycidyl ether type epoxy resin having an epoxy equivalent of 190, manufactured by Tohto Kasei K.K.; EX-421 is an aliphatic hydrocarbon glycidyl ether type epoxy resin having an epoxy equivalent of 155, manufactured by Nagase Kasei K.K.; EPPN-201 is a phenol Novolak type epoxy resin having an epoxy equivalent of 185, manufactured by Nihon Kayaku K.K.; Krelan UI-B is a blocked isocyanate having NCO equivalent of 365,manufactured by Bayer; and Curezol C-17Z is a curing catalyst. Next, the abovementioned coating powders each was applied by electrostatic spraying onto a zinc phosphated steel plate (0.6 mm thickness) and heat-cured at 250°C for 5 minutes to obtain a coated test plate, which was then subjected to a series of tests for evaluating film properties. The test results are shown in the following Table 2. Test methods and evaluation standards used are as follows: Bending property test: JIS 5400-6-16 Number of coated sheets placed in the bended opening was used as an evaluation value. The smaller the value, the higher the bending property. Non-volatile content test: Test coating powder was applied by spraying onto a steel plate and the coated plate was baked at 250°C for 5 minutes. Non-volatile content (%) was determined at that stage. Degree of crosslinking: Xylene rubbing test was carried out. ○.... good x.... no good Evaluation of yellowing: Baked test plate was tested by using SM color computor (Suga Shikenki K.K.) to determine b value. The larger the b value, the severer the yellowing. SP value determination: test temperature: 20°C sample: 0.5g of resin was weighed in 100 ml beaker. 10ml of THF were added by using a pipette and dissolved by means of magnetic stirrer. cloud point determination: Using a 50ml biuret, poor solvent (n-hexane, DIW) was drop-wise added and the added amount was measured at the point when turbid mixture was obtained. At this could point, and V were calculated by using the following equation. V m =V₁V THF /(₁ V THF +  THF V₁) δ m ² = ₁ δ₁² +  THF δ THF ² in which V₁ : molecular volume (ml/mol) of solvent ₁ : volume fraction of poor solvent at the could point δ₁ : SP value of solvent V THF : molecular volume (p1.08) of THF  THF : volume fraction of THF at the could point δ THF : SP value (9.52) of THF SP value of resin can be calculated as follows: δ²= (V m1 δ m1 + V mh δ mh )/(V m1 + V mh ) in which V m1 : molecular volume of mixture with hexane as poor solvent δ m1 : SP value of mixture with hexane as poor solvent V mh : molecular volume of mixture with water as poor solvent δ mh : SP value of mixture with water as poor solvent Boiling water resistance: Coated test plate was dipped in boiling water for 2 hours and then allowed to leave at a room temperature for 30 minutes. Thereafter, cross-cut (1 m/m) was given by knife onto the coating and tape peeling test was carried out. Boiling water resistance was evaluated by checking the remaining percentage of the film cuts. 100/100 completely remained 0/100 totally peeled out Weather resistance: Sun-shine weather-O-meter test was carried out. After measuring gloss value, weather resistance was evaluated by gloss retention percentage.

Claims: A coating powder composition comprising, as principal ingredients, (A) a carboxyl group containing polyester resin prepared by the reaction of at least one polybasic acid and at least one polyhydric alcohol and having a number average molecular weight of 1,000 to 20,000, an acid value of 10 to 100, a glass transition temperature of 35 to 120°C and a SP value of 9.8 to 11.5, and (B) glycidyl trimellitate, the equivalent weight ratio of carboxyl groups of said polyester resin (A) to glycidyl groups of said glycidyl trimellitate (B) being 1:2 to 2:1, characterized in that 75% or more by weight of the polyhydric alcohol of the polyester resin is neopentyl glycol. A coating powder composition as claimed in claim 1, characterized in that a part, up to 40% by weight, of the glycidyl trimellitate is replaced by at least one other glycidyl compound selected from a diepoxide having in its molecule two glycidyl groups and an aliphatic glycidyl ether having in its molecule three glycidyl groups.

Inventors: TOYODA YUJI, TSUTSUI KOICHI, UENAKA AKIMITSU, UENO TASABURO, TOYODA, YUJI, TSUTSUI, KOICHI, UENAKA, AKIMITSU, UENO, TASABURO
Applicants: NIPPON PAINT CO LTD, NIPPON PAINT CO., LTD.
Application year: 1990
Main classification: C09D167
IPC codes: C09D167, C09D163, C09D5, C08K5