SURFACE-COATED HARD MEMBER FOR CUTTING AND ABRASION-RESISTANT TOOLS

Abstract: A surface-coated superhard member which has excellent resistances to abrasion, fusion and breakage as a cutting or abrasion-resistant tools in not only low-speed cutting but also high-speed cutting, thereby exhibiting excellent cutting performances over a prolonged period of time. The hard coating comprises layers of a carbide, a nitride or a carbonitride of Ti, Zr or Hf and layers of a carbide, a nitride or a carbonitride of Al, which are piled one upon another to form a coating laminate of at least ten layers in total.

Description: A surface-coated hard material for cutting tools or wear resistance tools Technical Field of The Invention This invention relates to a surface-coated hard material for cutting tools or wear resistance tools, in which a coating layer is provided on the surface of a cutting tool or wear resistance tool to improve the wear reistance. Technical Background Up to the present time, cutting tools and wear resistance tools have generally been composed of cemented carbides based on tungsten carbide (WC), various cermets based on titanium carbide (TiC), steels such as high-speed steels or hard alloys and ceramics based on silicon carbide and silicon nitride. In order to improve the wear resistance of the cutting tools or wear resistance tools, a surface-coated hard material has been developed and has lately been put to practical use, in which one or more layers of carbides, nitrides or carbonitrides of Ti, Hf or Zr or oxide of Al are formed on the whole surface or the surface of the edge part thereof by a PVD method or CVD method. In particular, the cutting tool or wear resistance tool having the hard coating layer formed by the PVD method is capable of improving the wear resistnce without deteriorating the strength of the base material and accordingly, it is suitable for a cutting use requiring a strength, for example, throwaway inserts for drills, end mills, milling cutters, etc. However, the PVD method is favorably compared with the CVD method in respect of that the hard coating layer can be formed without deteriorating the strength of the substrate, but in the PVD method, it is difficult to stably form an oxide of Al and accordingly, a hard coating layer consisting of Al oxide formed by the PVD method has not been put to practical use. On the other hand, in the hard coating layers consisting of carbides, nitrides or carbonitrides of Ti, Hf or Zr formed by the present PVD method, the wear resistance cannot be said sufficient and in the high speed cutting, in particular, cutting tools or wear resistance tools thereof have shortened lives because of poor wear resistance. Disclosure of The Invention Under the situation, the present invention has been made for the purpose of overcoming the disadvantages of the prior art and thus provides a surface-coated hard material for a cutting tool or wear resistance tool by providing a coating layer having excellent wear reisistance while maintaining the substrate strength of the cutting tool or wear resistance tool, in particular, exhibiting an improved wear resistance over the prior art in the high speed cutting. The above described object can be achieved by a surface-coated hard material for a cutting tool or wear resistance tool, characterized in that a layer consisting of a carbide, nitride or carbonitride of Ti, Zr or Hf and a layer consisting of a carbide, nitride or carbonitride of Al are alternately laminated to form at least 10 hard coating layers, each layer having a thickness of 0.01 to 0.2 µm and the total layer thickness being 0.5 to 10 µm, on the surface of a substrate of a cutting tool or wear resistance tool. In a preferred embodiment of the present invention, at least 10 layers of TiN layers and AlN layers each having a thickness of 0.01 to 0.2µm are alternately laminated to provide a coating layer having a whole layer thickness of 0.5 to 0.8 µm on the surface of a substrate consisting of a cutting tool or wear resistance tool, thus obtaining a surface-coated super-hard material for a cutting tool or wear resistance tool. In the present specification, Ti, Zr and Hf are sometimes represented by M. The hard coating layer can be provided on the whole surface of a cutting tool or wear resistance tool or only the surface of an edge part. Formation of the hard coating layer can be carried out in known manner, but the PVD method such as sputting methods, ion plating methods, etc. is preferable in respect of that the substrate strength can readily be maintained. The surface-coated super-hard material of the present invention is excellent, as a cutting tool or wear resistance tool, in wear resistance, deposition resistance and breakage resistance and exhibits an excellent cutting performance for a long period of time in not only low speed cutting but also high speed cutting. The reason therefor is that when a thin TiN layer and AlN layer are alternately laminated on the surface of a substrate, for example, TiN increases the hardness of the coating layer and simultaneously improves the adhesiveness thereof to the substrate, while AlN improves the breakage resistance and renders the crystals of TiN finer. That is, it is considered that the TiN layer and AlN layer are synergetically reacted to form a coating layer having, as a whole, excellent wear resistance, deposition resistance and breakage resistance. As described above, in the surface-coated hard material of the present invention, the hard coating layer is composed of thin layers of MC, MN or MCN and thin layers of ALC, AlN or AlCN, laminated alternately, so when using it as a cutting tool or wear resistance tool, there can be obtained an excellent wear resistance, deposition resistance and breakage resistance, and the good cutting performance can be maintained for a long time. That is, in each layer of the hard coating multilayer, an M carbide, nitride or carbonitride not only increases the bonding strength to the substrate, but also raises the hardness of the hard coating layer and on the other hand, Al carbide, nitride or carbonitride improves the breakage resistance of the hard coating layer and simultaneously, is dissolved in the layer of Hf carbide, nitride or carbonitride to render the crystal grains finer. Therefore, the wear resistance, deposition resistance and breakage resistance of the hard coating layer, as a whole, are improved by the synergistic action of these laminated layers. Furthermore, it is found that the surface-coated hard material as a cutting tool or wear resistance tool provided with the above described hard coating layer exhibits a good wear resistance even in the high speed cutting because of formation of AL₂O₃ having a very high hardness at a high temperature even in a very small amount in the hard coating layer due to rising of the edge temperature during cutting. As to the thickness of the hard coating layer, if the whole layer thickness is less than 0.5 µm, the wear resistance is hardly improved, while if more than 10 µm, the residual stress is so large that the bonding strength to a substrate is lowered. Accordingly, the whole layer thickness should be in the range of 0.5 to 10 µm. The layer thickness of each of layers consisting of carbides, nitrides or carbonitrides of M and layers consisting of carbides, nitrides or carbonitrides of Al, to be laminated alternately, should be in the range of 0.01 to 0.2 µm, since it is difficult to form a layer with a thickness of less than 0.01 µm and if the thickness is less than 0.01 µm, the whole hard coating layers laminated are too brittle to maintain the wear resistance, while if more than 0.2 µm, formation of solid solutions does not take place between the layers because of the larger thickness thereof and improvement of the wear resistance, deposition resistance and breakage resistance by the synergistic reaction can not be obtained. Furthermore, even if the thickness of the each layer is in the range of 0.01 to 0.2 µm, it is difficult to compose a hard coating layer having, as a whole, an excellent wear resistance, deposition resistance and brekage resistance in a case where the number of the layers laminated alternately is less than 10 layers. The present invention will be illstrated in greater detail by the following examples and comparative examples. Example 1 Using a cutting insert made of a cemented carbdie with a composition of JIS standard P 30 (specifically, WC-20 wt % TiC-10 wt % Co) and a form of JIS SNG 432 as a substrate, the surface thereof was coated with each of coating layers as shown in the following Table 2 by an ion plating method using vacuum arc discharge, as described below, to obtain a sample of a coated cutting tool of the present invention. Namely, an Al target and Ti target were arranged to face with each other in a film making apparatus, in which the above described cutting inserts as substrates were respectively fit on two points on the diameter passing the center of a ring-shaped substrate supporting means rotatory around the intermediate point, as a center, between both the targets. Under the state, while revolving the cutting inserts at 20 rpm, the inserts were then maintained in an Ar gas atmosphere with a vacuum degree of 1.3 Pa (1 x 10 ⁻² torr), rinsed by applying a voltage of -2000 V and heated at 500°C, after which the Ar gas was exhausted. Then, while continuously revolving the cutting inserts and introducing one or both of N₂ gas and CH₄ gas at a rate of 300 cc/min into the film making apparatus, the Ti target and Al target were evaporated and ionized by vacuum arc discharge, whereby TiN layers and Al layers were alternately laminated on each of the cutting inserts in such a manner that TiN be coated when the cutting insert passing near the Ti target and AlN be coated when the cutting insert passing near the Al target. During the same time, the thickness of the TiN layers and AlN layers laminated was controlled by controlling the quantity of the arc current and the whole coating layer thickness was controlled by the film making time. For comparison, the surface of a cutting insert with the same composition and same form as described above was coated with the coating layers of carbide, nitride or carbonitride of Ti by an ion plating method using the same film-making apparatus and vacuum arc discharge as described above, thereby obtaining samples of surface-coated cutting inserts of the prior art as shown in Table 2. In addition, samples of coated cutting inserts were prepared by the ordinary method, in which coating layers of TiC, Al₂O₃, etc. shown in Table 2 were formed on the surface of the cutting insert with the same composition and same form. Each of the samples of the surface-coated cutting inserts prepared as described above was subjected to a continuous cutting test and intermittent cutting test under conditions as shown in Table 1 to measure the flank wear width of the edge, thus obtaining resuts as shown in Table 2. It is apparent from the above described results that the samples of the coated cutting inserts of the present invention have both an excellent wear resistance and breakage resistance, i.e. more excellent cutting performance than the comaprative samples in both the continuous cutting and intermittent cutting tests. Example 2 Using a cutting insert made of a cemented carbdie with a composition of JIS standard P 30 (specifically, WC-20 wt % TiC-10 wt % Co) and a form of JIS SNG 432 as a substrate, the surface thereof was coated with each of coating layers as shown in the following Table 3 by an ion plating method using vacuum arc discharge, as described below, to obtain a sample of a coated cutting tool of the present invention (Sample Nos. 3 to 6). Namely, an Al target and Zr target were arranged to face with each other in a film making apparatus, in which the above described cutting inserts as substrates were respectively fit on a substrate supporting means rotatory around the intermediate point, as a center, between both the targets, after which the revolving speed of the substrate supporting means was controlled so that the the cutting inserts be revolved at 20 rpm. Thereafter, the inserts were then maintained in an Ar gas atmosphere with a vacuum degree of 1.3 Pa (1 x 10 ⁻² torr), rinsed by applying a voltage of -2000 V and heated at 500 °C, after which the Ar gas was exhausted. Then, while introducing one or both of N₂ gas and CH₄ gas at a rate of 300 cc/min into the film making apparatus, the Zr target and Al target were evaporated and ionized by vacuum arc discharge, whereby the coating layers were alternately laminated on each of the revolving cutting inserts in such a manner that Zr carbide, nitride or carbonitride be coated when the revolving cutting insert passing near the Zr target and Al carbide, nitride or carbonitride be coated when passing near the Al target. During the same time, the thickness of the each layer of carbides, nitrides, carbonitrides of Zr or Al alternately formed was controlled by controlling the quantity of the electron beam irradiated and the whole coating layer thickness was controlled by the film making time. Each of the samples of the surface-coated cutting inserts prepared as described above was subjected to a continuous cutting test and intermittent cutting test under conditions as shown in Table 1 to measure the flank wear width of the edge, thus obtaining resuts as shown in Table 4. It is apparent from the above described results that of the samples of the surface-coated cutting inserts of the prior art, Sample Nos. 1-3 whose hard coating layers were formed by the PVD method were inferior in wear resistance and Sample Nos. 4 and 5 whose hard layers were formed by the CVD method exhibited lowering of the breakage resistance due to deterioration of the toughness of the substrate, while Sample Nos. 3-6 of the surface-coated cutting inserts according to the present invention showed more excellent wear resistance in both the continuous cutting and intermittent cutting tests and since the hard coating layer was formed by the PVD method, the toughness of the substrate was maintained resulting in more excellent breakage resistance. The alternately laminated layers in the present invention can be of any combinations of only carbides, nitrides or carbonitrides such as ZrN and AlN shown in Example, of nitrides and carbonitrides such as ZrN and AlCN and the like, and furthermore, in each layer of Zr systems and Al systems, for example, the components can be suitably changed among the carbide, nitride and carbonitride during the lamination. Example 3 Using a cutting insert made of a cemented carbdie with a composition of JIS standard P 30 (specifically, WC-20 wt % TiC-10 wt % Co) and a form of JIS SNG 432 as a substrate, the surface thereof was coated with each of coating layers as shown in the following Table 5 by an ion plating method using vacuum arc discharge, as described below, to obtain a sample of a coated cutting tool of the present invention (Sample Nos. 7 to 10). Namely, an Al target and Hf target were arranged to face with each other in a film making apparatus, in which the above described cutting inserts as substrates were respectively fit on a substrate supporting means rotatory around the intermediate point, as a center, between both the targets, after which the revolving speed of the substrate supporting means was controlled so that the the cutting inserts be revolved at 20 rpm. Thereafter, the inserts were then maintained in an Ar gas atmosphere with a vacuum degree of 1.3 Pa (1 x 10 ⁻² torr), rinsed by applying a voltage of -2000 V and heated at 500 °C, after which the Ar gas was exhausted. Then, while introducing one or both of N₂ gas and CH₄ gas at a rate of 300 cc/min into the film making apparatus, the Hf target and Al target were evaporated and ionized by vacuum arc discharge, whereby the coating layers were alternately laminated on each of the revolving cutting inserts in such a manner that Hf carbide, nitride or carbonitride be coated when the revolving cutting insert passing near the Hf target and Al carbide, nitride or carbonitride be coated when passing near the Al target. During the same time, the thickness of the each layer of carbides, nitrides, carbonitrides of Hf or Al alternately formed was controlled by controlling the quantity of the electron beam irradiated and the whole coating layer thickness was controlled by the film making time. Each of the samples of the surface-coated cutting inserts prepared as described above was subjected to a continuous cutting test and intermittent cutting test under conditions as shown in Table 1 to measure the flank wear width of the edge, thus obtaining resuts as shown in Table 6. It is apparent from the above described results that of the samples of the surface-coated cutting inserts of the prior art, Comparative Sample Nos. 1-3 whose hard coating layers were formed by the PVD method were inferior in wear resistance and Comparative Sample Nos. 4 and 5 whose hard layers were formed by the CVD method exhibited lowering of the breakage resistance due to deterioraation of the toughness of the substrate, while Sample Nos. 7-10 of the surface-coated cutting inserts according to the present invention showed more excellent wear resistance in both the continuous cutting and intermittent cutting tests and since the hard coating layer was formed by the PVD method, the toughness of the substrate was maintained resulting in more excellent breakage resistance. The alternately laminated layers in the present invention can be of any combinations of only carbides, nitrides or carbonitrides such as HfN and AlN shown in Example, of nitrides and carbonitrides such as HfN and AlCN and the like, and furthermore, in each layer of Hf systems and Al systems, for example, the components can be suitably changed among the carbide, nitride and carbonitride during the lamination. Utility and Possibility on Commercial Scale According to the present invention, there can be provided a surface-coated hard material for a cutting tool or wear resistance tool having more excellent wear reisistance than that of the prior art with maintaining the substrate strength of the cutting tool or wear resistance tool, in particular, being capable of maintaining good cutting performances, as a cutting tool or wear resistance tool, for a long period of time even in the high speed cutting.

Claims: A surface-coated hard material for a cutting tool or wear resistance tool, characterized in that a layer consisting of a carbide, nitride or carbonitride of Ti, Zr or Hf and a layer consisting of a carbide, nitride or carbonitride of Al are alternately laminated to form at least 10 hard coating layers, each layer having a thickness of 0.01 to 0.2 µm and the total layer thickness being 0.5 to 10 µm, on the surface of a substrate of a cutting tool or wear resistance tool.

Inventors: NOMURA TOSHIO ITAMI W OF SUMIT, OMORI NAOYA ITAMI W OF SUMITOM, TOBIOKA MASAAKI ITAMI W OF SUM, YAMAGATA KAZUO ITAMI W OF SUMI, NOMURA, TOSHIO ITAMI W. OF SUMITOMO EL. IND., LTD., OMORI, NAOYA ITAMI W. OF SUMITOMO ELECT. IND.,LTD., TOBIOKA, MASAAKI ITAMI W. OF SUMITOMO EL.IND.,LTD., YAMAGATA, KAZUO ITAMI W. OF SUMITOMO EL. IND.,LTD.
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1990
Main classification: C23C14
IPC codes: C23C14