REGENERATION OF CATALYSTS

Abstract: Carbonaceous materials deposited on solid catalysts and produced, for example, in Beckmann rearrangement in a gaseous phase are burned off by effecting the treatment in the presence of alcohols such as methanol or ethanol together with molecular oxygen-containing gas in order to regenerate the catalyst activity.

Description: The present invention relates to a process for regenerating solid catalysts which are employed in the synthesis of organic compounds. The process for regeneration is conducted by removing carbonaceous materials deposited on the catalysts. Synthesis of organic compounds in the presence of solid catalysts is employed in many industries on a large scale, such as the petroleum refining industry and the petrochemical industry, for example, the cracking of crude oil or naphtha, and in the chemical industry for preparing, for example, monomers for synthetic resins, dyes, agricultural chemicals or pharamceuticals for synthesis of intermediate compounds of medicines. Reactions included in such syntheses are decomposition, alkylation, hydrogenation, reduction, oxidation, dehydrogenation, condensation, esterification, dehydration, hydration, isomerization, rearrangement, disproportionation, cyclization and halogenation. Carbonaceous materials often deposit on catalysts in the reactions mentioned above, for instance, decompositions where radicals are ready to be produced, condensations or polymerizations where high molecular weight compounds are ready to be produced, reactions wherein unsaturated compounds and/or aromatic compounds are present, or reaction systems where the catalysts have large affinity for the products produced, for example, the synthesis of nitrogen-containing organic compounds in the presence of solid acid catalysts. The carbonaceous materials are, for example, heavy complex materials produced from condensation or polymerization of principal products or by-products adsorbed on the catalysts, or cokes produces while dehydrogenation proceeds. Carbonaceous materials coat the surface of catalysts as soon as they are produced, resulting in lowered catalytic activity, or decrease of selectivity of reactions by degradation of active sites. As deposition proceeds, carbonaceous materials accumulate among catalyst pellets until plugging of a catalyst bed or agglomeration or break up of catalyst pellets occurs. Decoking where the reaction is stopped and molecular oxygen-containing gas is passed through a catalyst bed at high temperature until carbonaceous materials deposited on the catalyst pellets are burned off, is usually conducted in order to regenerate catalysts (Catalysis Society of Japan, "Catalytic Engineering Course" Vol. 7, "Catalytic reaction" (2), - oxidation, dehydrogenation, decomposition -, page 278, published on February 28, 1967 by Chijin Shokan). Steam or inert gas may be accompanied by air or molecular oxygen-containing gas, in order to facilitate the removal of carbonaceous materials or control the burning. However, there are some carbonaceous materials left unremoved from the surface of catalyst by conventional techniques, with the result that the catalystic activity is usually lowered. This is due to the fact that the regeneration is carried out at a temperature lower than the necessary temperature. It is hard from an economical point of view to increase the temperature for regeneration compared with the reaction temperature. Apparatuses made of specific heat-resistant materials or specific heating mediums are required for this effect. Heating mediums used in a fixed bed reaction which is effected in, for instance, multi-tube reactors where heating is made by heating mediums, have their own upper temperature limits. One is forced to reuse catalysts which have not been subjected to sufficient regeneration, when regeneration at a high enough temperature cannot be carried out due to economic or technical reasons. One of the problems encountered in such reuse is that the catalystic activity is much smaller than the initial activity and little regeneration of the catalyst is actually effected. The life of catalyst, i.e. the period of time from its first use to its disposal after several regenerations, is so short that a long production run with the same catalyst cannot be achieved. Another problem is thermal degradation of catalysts, for example, chemical change of the components, decrease in specific surface area, crystallization of amorphous components, disappearance of micropores, sintering of active ingredients, for example, dispersed metals, agglomeration of pellets for example, formation of large sized grains or diminished fluidization in a fluidized catalyst bed, break up or fracture of catalyst pellets, or vaporization of active ingredients. The optimum temperature range for decoking is narrow. The present invention resides in providing a regeneration process for solid catalysts which are used for synthesis of organic compounds, by which carbonaceous materials deposited on the catalysts are sufficiently removed at a relatively low temperature. The present invention also provides a regeneration process for solid catalysts by which carbonaceous materials deposited thereon are removed and degradation of catalytic activity is avoided or diminished. According to the present invention, carbonaceous materials deposited on catalysts are burned off in the presence of air or molecular oxygen-containing gas, the process being characterized by the fact that the burning off is carried out in the presence of alcohols of the formula: R - OH wherein R stands for an alkyl group or a hydroxyalkyl group. R preferably represents C₁₋₆ alkyl groups, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, tert-butyl, n-amyl, iso-amyl or n-hexyl groups or C₂₋₆ hydroxyalkyl groups such as hydroxyethyl, hydroxypropyl, hydroxybutyl or hydroxyhexyl groups. Alcohols usable in the present invention are, for example, methanol, ethanol, n-propanol, iso-propanol, n-butanol, iso-butanol, tert-butanol, n-amyl alcohol, iso-amyl alcohol, n-hexanol, ethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,4-butanediol, 1,2-butanediol, 2,3-butanediol or 1,6-hexanediol. At least one of them is used. Methanol and ethanol are preferred. The catalysts are solid and include metal catalysts, metal oxide catalysts, silica-alumina, zeolite, metal sulfides, metal halids or combinations thereof. Active ingredients may be shaped without any additives, but supported on carriers or modified by ion-exchange. Metals include alkali metals, alkaline earth metals, copper, silver, zinc, cadmium, silicon, aluminium, gallium, rare earth metals, tin, lead, titanium, zirconium, hafnium, phosphorus, arsenic, antimony, bismuth, vanadium, niobium, tellurium, chromium, molybdenum, tungsten, manganese, iron, cobalt, nickel, thorium, uranium, ruthenium, rhodium, palladium or platinum. They may be in the form of a complex, for example, zeolite subjected to ion-exchange with various metal ions, metallic copper/chromium oxide, copper oxide/chromium oxide, metallic copper/zinc oxide, copper oxide/zinc oxide or chomium oxide/zinc oxide catalysts or platinum catalyst supported on alumina. Carbonaceous materials deposited on catalysts and to which the present invention is able to be applied are produced from, for example, cracking (for example, silica-alumina, zeolite, chromia-alumina or platinum catalysts), alkylation (for example, silica-alumina, zeolite, copper chloride, iron chloride or aluminium chloride catalysts), reduction (for example, nickel, cobalt, palladium, copper oxide/chromium oxide or platinum catalysts), oxidation (for example, vanadium oxide, molybdenum oxide, bismuth oxide, antimony oxide, silver, palladium or platinum catalysts), dehydrogenation (for example, zinc oxide or copper oxide catalysts), condensation (for example, silica-alumina or zeolite catalysts), esterification, dehydration, hydration, isomerization or rearrangement (for example, silica-alumina, zeolite, niobium oxide or solid acid catalysts), disproportionation (for example, tungsten oxide catalyst), cyclization (for example, zinc oxide, nickel or platinum catalysts), halogenation (for example, aluminium chloride or iron chloride catalysts) or hydrocarbon synthesis (silica-alumina or zeolite catalysts). Carbonaceous materials may also be those produced in reduction, dehydrogenation, dealkylation or cyclization where metallic copper/zinc oxide, metallic copper/chromium oxide, metallic nickel/metallic copper, metallic nickel/zinc oxide or zinc oxide/chromium oxide catalysts are employed. Particular examples are the cracking or deparaffin reaction of crude oil, heavy oil, light oil or naphtha in the presence of silica-alumina or zeolite such as ZSM-5 catalysts, isomerization of alkyl aromatic hydrocarbons, alkylation of aromatic hydrocarbons, synthesis of pyridine bases, Beckmann rearrangement or synthesis of gasoline from methanol or synthesis of hydrocarbons, alcohols and/or glycols from CO/H₂. The amount of carbonaceous materials deposited on catalysts is not able to be defined generally but is determined taking account of activity and/or selectivity of catalysts and the period of time required for regeneration of catalysts. It is desirable to perform regeneration from economical and technical points of view when carbonaceous materials deposited reach usually 2-4% by weight on the basis of the catalyst, since activity and selectivity of the catalyst decreases greatly at such levels and operation of the reactors becomes difficult to control. Any shape of catalyst pellets may be employed, for example, cylindrical, spherical or amorphous block shapes. Catalysts may also be in the form of microbeads which may be used in a Riser reactor or fluidized bed. A conventional way to introduce alcohols accompanied by air or molecular oxygen-containing gas is to vaporize the alcohols in evaporators of alcohols and then mix the vaporized alcohols with air or molecular oxygen-containing gas before the mixture is fed to a catalyst bed. Alternatively, inert gas such as steam, nitrogen gas or carbon dioxide gas may be allowed to be present at any stage before the alcohol/air mixture is fed to the catalyst bed in order to control burning or avoid an explosion. The effect of alcohols added is apparent even if the alcohols are not completely burned. The ratio between the alcohols and the oxygen with or without inert gas is not critical. However, the amount of the alcohols should be selected taking into consideration the efficiency of the alcohols added and also the range of compositions where explosion occurs, so as to work preferably below the lower limit of the range. For example, the amount of alcohol to be added should be less than 6% by volume for methanol when it is used with air, and less than 10.5% by volume for ethanol when it is used with air. The space velocity (SV) of the gas used for regeneration is not critical but usually should be no less than 100 hr⁻¹ taking efficiency into account. The temperature which should be used for regeneration will vary depending on the catalysts and/or the reactions, but usually is about 350°C to about 600°C. The temperature of the catalysts while regeneration is effected increases due to the heat of combustion of the alcohols. The composition of the feed gas and/or its flow rate may be changed, if desired, in a continuous or a step-wise manner, in order to control the temperature of the catalyst bed. The increase in the temperature of the catalyst bed will vary greatly depending on the catalysts involved, the form of carbonaceous materials deposited, the concentrations of alcohols, oxygen, steam and/or other gas in the feed gas, the SV of the gas, the variety of reactor, the heating medium for cooling the reactor and the pre-heating temperature of the feed gas. Clearly the catalyst bed temperature should be kept below heat-resistance limit of the apparatus involved including the reactor. Also it is not desirable to keep the catalyst bed temperature at unduly high levels, taking the risk of heat degradation of the catalysts into account. The time required for regeneration of the catalyst will vary depending on the variety of catalyst, the form and amount of carbonaceous materials deposited, the concentration of alcohol, oxygen, steam and/or other gas in the feed gas and/or the temperature of a catalyst bed. The present regeneration process may be conducted independently alone, or it may be conducted in combination with other processes. For instance, air or molecular oxygen-containing gas may be charged at a high temperature in order to have almost all of the carbonaceous materials burned off, the temperature of the catalyst bed may be changed if desired, and a mixture of air or molecular oxygen-containing gas with alcohols then charged into the catalyst bed. In another procedure, for example, after a mixture of air or molecular oxygen-containing gas with alcohols is applied to the catalyst until carbonaceous materials are burned off, air or molecular oxygen-containing gas is then fed to the catalyst bed. The present process is able to remove carbonaceous materials deposited on catalysts at lower temperatures than that in conventional processes, and improved recovery of catalystic activity is achieved. Regeneration is effected in a remarkably shorter period of time than that of conventional processes effected at the same temperature. It is a considerable advantage for the materials for the apparatus, the cost of heating and other economic aspects that regeneration of catalysts can be done at lower temperature. The life of catalysts is also longer due to the decrease in the heat load they are subjected to. The present process may be applied to many processes as mentioned above, but preferred processes are the production of ε -caprolactam by Beckmann rearrangement of cyclohexanone oxime in the gas phase and the production of pyridines. The invention may be put into practice in various ways and a number of specific embodiments will be described by way of example to illustrate the invention. Synthesis of ε -caprolactam (epsilon-caprolactam) EXAMPLE 1 (Preparation of a catalyst) Tetraethylorthosilicate [Si(OC₂H₅)₄, 100 g, Al content: not more than 10 ppm], aqueous tetra n-propylammonium hydroxide (10% by weight) solution (224 g) and ethanol (60 g) were charged in an autoclave (1.5 ℓ ) made of stainless steel and stirred vigorously for 30 minutes. The mixture had pH 13. The autoclave was tightly sealed and dipped in an oil bath. Hydrothermal synthesis was carried out for 120 hours at 105°C under stirring (not less than 400 rpm). Pressure in the autoclave was 2-3 Kg/cm², The contents had pH 11.8 when the hydrothermal reaction was over. White solid product was collected by filtration and washed continuously with distilled water until pH of the filtrate was about 7. After the product was dried, it was calcined under an air stream for 4 hours at 500 to 530°C to obtain powdery white crystals (27 g). This was identified to be pentasil zeolite by an X ray diffractometer. Elemental assay by atomic absorption spectrometry gave 3 ppm of aluminium. To the crystals (10 g) of this product was added aqueous ammonium chloride (5% by weight) solution (100 g) and the crystals were subjected to an ion-exchange treatment for one hour at 50-60°C, before they were filtered. After the ion-exchange treatment was repeated four times, the crystals were washed with distilled water until no Cl⁻ was detected, and dried at 120°C for 16 hours. The thus obtained crystals of NH₄⁺ form were shaped to particles of 24-48 mesh (which have openings 701 to 295 microns across) and then calcined in a nitrogen gas stream at 500°C for one hour. The crystals were named as catalyst A. Synthesis of ε-caprolactam A reaction tube made of quartz glass (1 cm diameter) packed with the catalyst A (0.3 g, 0.5 ml) was preheated at 350°C for one hour under a nitrogen stream. A solution of cyclohexanone oxime (8.0% by weight) in benzene was charged at a rate of 11.5 g/hr, keeping the temperature of the catalyst bed at 350°C. The space velocity (WHSV) was 3.1 hr⁻¹. The reaction product was trapped and collected every hour using water-cooling and assayed by gas chromatography. The result at one hour after the reaction started: conversion : 100% selectivity: 78%. The reaction was allowed to proceed. The result at 6 hours: conversion : 97% selectivity: 80%. The colour of the catalyst after the reaction was over turned to black, due to deposition of carbonaceous materials. Space velocity (WHSV), conversion of cyclohexanone oxime and selectivity of ε-caprolactam are calculated by the following formulas. WHSV (hr⁻¹) = feeding rate of cyclohexanone oxime (Kg/hr)/weight of catalyst (Kg) Conversion (%) of cyclohexanone oxime = {(A-B)/A} x 100 Selectivity (%) of ε-caprolactam = {C/(A-B)} x 100 wherein A: starting cyclohexanone oxime fed (mol) B: cyclohexanone oxime unaltered (mol) and C: ε-caprolactam in product (mol). (Regeneration of catalyst) Regeneration of the catalyst above was conducted at 440°C for 3 hours while methanol (0.15 g/hr) together with air (2.5 ℓ/hr) were fed. SV at this time was 5200 hr⁻¹. The colour of the catalyst changed to white. Removal of carbonaceous materials was confirmed. (Second synthesis of ε-caprolactam) Synthesis of ε-caprolactam was continued under the same conditions as those before the regeneration was effected, in the presence of the catalyst which had been subjected to regeneration in the presence of methanol as above. Results: Comparison Example 1 Synthesis of ε-caprolactam was conducted for 6 hours in the presence of the catalyst A in the same manner as in Example 1, synthesis of ε-caprolactam. Catalyst on which carbonaceous materials were deposited was subjected to regeneration at 440°C for 3 hours in an air stream (2.5 ℓ/hr). SV was 5000 hr⁻¹. Colour of the catalyst after the regeneration was over was still black and almost all carbonaceous materials were left unremoved. Synthesis of ε-caprolactam was continued in the presence of the catalyst which had been subjected to the regeneration above, under the same conditions as those in Example 1, second synthesis of ε-caprolactam. EXAMPLE 2 A reaction tube made of quartz glass (1 cm diameter) packed with the catalyst A (1.8 g) was preheated at 350°C for one hour in a nitrogen stream. A solution of cyclohexanone oxime (8.0% by weight) in benzene was fed at a rate of 69.0 g/hr and reaction was conducted for 6 hours. WHSV was 3.1 hr⁻¹. Average result: conversion : 99% selectivity: 80% After the reaction was over, the catalyst was taken out of the reaction tube, well mixed and divided into 0.3g each. One of the catalysts divided (X1) was subjected to regeneration wherein methanol (0.15 g/hr) with air (2.5 ℓ/hr) were fed at 440°C for 3 hours. SV was 5200 hr⁻¹. The other portion of the catalyst (X2) was subjected to regeneration under the same conditions as in X except that ethanol (0.10 g/hr) with air (2.5 ℓ/hr) were fed (SV = 5100 hr⁻¹). The other catalyst (X3) was subjected to regeneration under the same conditions as in X except that n-hexanol (0.10 g/hr) with air (2.5 ℓ/hr) were fed (SV = 5040 hr⁻¹). Assay of carbon and nitrogen contained in the catalysts which had been subjected to regeneration above was effected with an oxygen-recycling combustion, automatic, high sensitive N and C assay apparatus. Results are given in Table 1. Assay results for the catalyst before regeneration and for the catalyst which had been subjected to regeneration wherein air (2.5 ℓ/hr) was fed without alcohols at 440°C for 3 hours, are also mentioned for reference in Table 1. Comparison Example 2 Air (2.5 ℓ/hr) was passed at 520°C for 3 hours through a reaction tube made of glass (1 cm diameter) packed with the catalyst (0.3 g) obtained after the synthesis of ε-caprolactam was over in Example 2, in order to effect regeneration. SV = 5000 hr⁻¹. Colour of the catalyst after the regeneration was over was black, so that carbonaceous materials were not sufficiently removed. Subsequently, air (2.5 ℓ/hr) was fed at SV = 5000 hr⁻¹ for 3 hours at 560°C to find that colour of the catalyst turned to white. EXAMPLE 3 (Preparation of catalyst) Example 1 was repeated to prepare a catalyst which contained Al (3 ppm) and was referred to as "catalyst A*". (Synthesis of ε-caprolactam) Example 1 was repeated except that the catalyst A* (0.6 g, 1.0 ml) was used in place of the catalyst A and a solution of cyclohexanone oxime (8.0% by weight) in benzene was fed at a rate of 23.0 g/hr in place of 11.5 g/hr. Result: After the synthesis was over, a part of the catalyst was taken out of the reactor, thoroughly mixed, and was assayed with the same apparatus as in Example 2, to give C and N contents of: (Regeneration of the catalyst) Methanol (0.15 g/hr) with air (2.5 ℓ/hr) were fed at 430°C for 5 hours through the catalyst (0.5 g, 0.8 ml). SV = 3200 hr⁻¹. Subsequently, air (2.5 ℓ/hr, SV = 3100 hr⁻¹) without methanol was fed at the same temperature as above for 2 hours. A part of the catalyst thus treated was taken out of the reactor and mixed thoroughly for assay of C and N with the same apparatus as of Example 2 and gave C and N values of: (Second synthesis of ε-caprolactam) The same synthesis of ε-caprolactam mentioned above was continued except that the regenerated catalyst as above (0.3 g) was used in place of the catalyst A* and a solution of cyclohexanone oxime (8.0% by weight) in benzene was fed at a rate of 11.5 g/hr in place of 23.0 g/hr. Result: (Synthesis of pyridine bases) In the following examples 4, 5 and 6 and comparison examples 3 and 4, yield of products is calculated according to the formulas mentioned below on the basis of total number of carbon atoms in the starting compounds of aliphatic aldehydes. Yield of pyridine = Total number of C atoms in pyridine produced Total number of C atoms in the starting aldehydes x 100% Yield of α,β or γ - picoline = Total number of C atoms in α,β or γ- picoline produced Total number of C atoms in the starting aldehydes x 100% EXAMPLE 4 ZSM-5 zeolite was prepared according to YASHIMA's process ("Shokubai" 23 (3), 232, 1981). Solution A was prepared by mixing distilled water (433.4 g), aluminium sulfate (4.6 g), tetra-n-propylammonium bromide (55.8 g) and sulfuric acid (40 g). Solution B was prepared by mixing distilled water (320 g) and sodium silicate (453 g). Solution C was prepared by mixing distilled water (754 g) and sodium chloride (189 g). Solution C was charged in an autoclave (3 ℓ) made of stainless steel and solutions A and B were dropped while the solution C was vigorously stirred, so that pH of mixture was controlled to be kept at 9.5 to 11. The autoclave was tightly sealed and temperature was raised to 160°C to effect hydrothermal reaction for 20 hours under stirring and under 5-6 Kg/cm² (gauge pressure). After the reaction was over, the autoclave was cooled to the ambient temperature and the product was subjected to repeated steps of filtration and washing with water, until the chloride ion in the filtrate was not more than 1 ppm. The product was dried in air at 110°C for 16 hours, and then was calcined in air at 530°C for 4 hours, to obtain crystals (112 g). The crystals had the same X ray diffraction spectrum as ZSM-5 (Na⁺ form) zeolite mentioned in Japanese patent Kokoku 46-10064. Si/Al was 90. The ZSM-5 (Na⁺ form) zeolite was treated with aqueous ammonium chloride (5% by weight) solution three times (one liter of the aqueous solution, each time) at 50 to 60°C for one hour to effect ion-exchange and then subjected to repeated steps of filtration and washing with water, until the chloride ion in the filtrate was not more than 1 ppm. Drying the zeolite at 110°C for 16 hours gave ZSM-5 (NH₄⁺ form) crystals (106 g). The zeolite (NH₄⁺ form) (20 g) was subjected to ion-exchange at 80°C for 2 hours with aqueous thallium nitrate (0.1 M) solution (200 ml) and then washed several times with distilled water (total amount: 400 ml). After being dried at 110°C for 16 hours, the zeolite was calcined in air at 530°C for 4 hours to obtain ZSM-5 (Tl⁺ form, Tl content = 3.0%). (Synthesis of pyridine bases, regeneration of catalyst and subsequent repetition of a cycle of synthesis and regeneration of catalyst) Through a reaction tube made of glass (12.6 mm diameter) packed with ZSM-5 (Tl⁺ form) and preheated at 450°C was passed a mixture of preheated ammonia gas (4 mol) and vapor mixture of acetaldehyde (2 mol) and formaldehyde (40% by weight aqueous solution, 1 mol) with SV = 1000 hr⁻¹. A reaction product was absorbed in water and then FID gas chromatography assay was effected. Average values for three hours after the reaction started: Catalyst was deep black coloured due to carbonaceous materials deposited thereon. Firstly nitrogen (20 ml/min) with air (20 ml/min) were fed for 20 minutes through the reaction tube (450°C), secondly air (40 ml/min) with nitrogen (20 ml/min) for 20 minutes, and thirdly air (200 ml/min) with nitrogen (20 ml/min) for 10 minutes, and fourthly methanol (8.6 mg/min) with air (200 ml/min) for 2 hours, for regeneration. SV = 2700 hr⁻¹. A cycle of the steps of synthesis and regeneration of catalysts was repeated. At the 50th cycle, yield were Colour of the catalyst after being regenerated was almost white which was close to colour of the fresh catalyst. Comparison Example 3 Example 4 was repeated except that air (200 ml/min) only was passed in place of methanol (8.6 mg/min) with air (200 ml/min). SV = 2700 hr⁻¹. A cycle of the synthesis and regeneration of catalyst was repeated. At the 30th cycle, yields were Colour of the catalyst after regeneration was over was brown. The brown colour deepened as the number of cycles increased. EXAMPLE 5 ZSM-5 (Tl⁺ form) in Example 4 which had been impregnated with an aqueous tetraamine palladium nitrate complex solution was dried at 110°C for 16 hours and calcined in air at 530°C for 4 hours to obtain a catalyst (Tl content: 3.0% by weight; Pd content: 0.01% by weight). The same synthesis-regeneration cycle as in Example 4 was conducted except that the abve mentioned catalyst was used in place of the ZSM-5 (Tl⁺ form). Results: Comparison Example 4 The same synthesis-regeneration cycle as in comparison Example 3 was conducted except that the catalyst mentioned in Example 5 was used in place of the ZSM-5 (Tl⁺ form). Result at the 50th cycle EXAMPLE 6 The same synthesis-regeneration cycle as in Example 4 was repeated except that the catalyst mentioned in Example 5 was used in place of the ZSM (Tl⁺ form) and ethylene glycol (6.2 mg/min) (SV = 2700 hr⁻¹) was used in place of the methanol. Result at the 100th cycle Synthesis of gasoline from methanol (hereinafter referred to as MTG reaction) EXAMPLE 7 ZSM-5 (NH₄⁺ form, 20 g) prepared in Example 4 was calcined in air at 530°C for 4 hours to obtain ZSM-5 (H⁺ form). MTG reaction was carried out according to US Patent 3,928,483. That is, methanol vapor was fed through a reaction tube (12.6 mm diameter) made of glass, packed with crystalline ZSM-5 (H⁺ form, 5 g) and heated at 325°C. SV = 2000 hr⁻¹. FID gas chromatographic assay of a product gave substantially the same result as the product mentioned in the above US patent. The catalyst after the reaction was effected for 8 hours was yellowish brown coloured due to carbonaceous materials deposited thereon. Nitrogen and air (20 ml/min, each) were first passed for 30 minutes through the reaction tube held at 325°C, secondly nitrogen (20 ml/min) and air (50 ml/min) for 30 minutes, thirdly nitrogen (20 ml/min) and air (200 ml/min) for one hour and fourthly a mixture gas of methanol (8.6 mg/min) with air (200 ml/min) for 3 hours, for regeneration of the catalyst. SV = 1800 hr⁻¹. Eight repetitions of the above reaction-regeneration cycle was made. The amount of carbonaceous materials deposited on the catalyst after the 8th cycle was over was observed with a thermobalance. The result is given in Table 2. Comparison Example 5 Example 7 was repeated except that air (200 ml/min, SV = 1700 hr⁻¹) only was used in place of methanol (8.6 mg/min) and air (200 ml/min). The amount of carbonaceous materials deposited on the catalyst after the 8th cycle of reaction-regeneration was over was observed with a thermobalance. The result is given in Table 2. Note * under a stream of air; temperature increasing rate of a catalyst specimen after regeneration was over: 5°C/min. Cracking EXAMPLE 8 ZSM-5 (NH₄⁺ form) prepared in Example 4 which had been impregnated with an aqueous tetraamine platinum nitrate complex solution was dried at 110°C for 16 hours and then calcined in air at 530°C for 4 hours to prepare a catalyst (Pt content: 0.01% by weight). Cracking of n-decane was effected according to Applied Catalysis. 19 , 101 (1985). That is, through a reaction tube (12.6 mm diameter) made of glass, packed with the catalyst above (5 g) and heated to 325°C was passed n-decane vapor (SV = 250 hr⁻¹). Assay of the product by FID gas chromatograph gave almost the same result mentioned in the above literature. The catalyst after the reaction was effected for 8 hours was black coloured with carbonaceous materials deposited thereon. Firstly, nitrogen and air (20 ml/min each) were fed for 30 minutes through the reaction tube held at 325°C, secondly nitrogen (20 ml/min) with air (50 ml/min) for 30 minutes, thirdly nitrogen (20 ml/min) with air (200 ml/min) for one hour and lastly a mixture gas of methanol (8.6 mg/min) and air (200 ml/min) for 3 hours, for regeneration. SV = 1800 hr⁻¹. The amount of carbonaceous materials deposited on the catalyst after the 8th cycle of the reaction-regeneration above was over were observed with a thermobalance. The result is given in Table 3. Comparison Example 6 Example 8 was repeated except air (200 ml/min) only was used with SV = 1700 hr⁻¹ in place of the mixture gas of methanol (8.6 mg/min) and air (200 ml/min). Amount of carbonaceous materials deposited on a catalyst after 8th cycle of the reaction-regeneration was over were observed with a thermobalance. The result is given in Table 3.

Claims: 1. A process for regeneration of a solid catalyst which comprises burning carbonaceous materials deposited on the catalyst in the presence of alcohol (I) mentioned below with air or molecular oxygen-containing gas: R - OH wherein R stands for an alkyl group or a hydroxyalkyl group. 2. A process as claimed in Claim 1 characterised in that R represents a C₁₋₆ alkyl group or a C₂₋₆ hydroxyalkyl group. 3. A process as claimed in Claim 1 characterised in that the alcohol is methanol, ethanol, n-propanol, iso-propanol, n-butanol, tert-butanol, n-amyl alcohol, iso-amyl alcohol, n-hexanol, ethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,4-butanediol, 1,2-butanediol, 2,3-butanediol, 1,6-hexanediol or a mixture thereof. 4. A process as claimed in Claim 3 characterised in that the alcohol is methanol, ethanol, n-hexanol, ethylene glycol or a mixture thereof. 5. A process as claimed in Claim 4 characterised in that the alcohol is methanol or ethanol. 6. A process as claimed in any one of Claims 1 to 5 characterised in that the amount of the alcohol is below the lower and of the range of explosive mixtures. 7. A process as claimed in any one of Claims 1 to 6 characterised in that the catalyst is zeolite. 8. A process as claimed in any one of Claims 1 to 7 characterised in that the carbonaceous materials are produced in Beckmann rearrangement effected in a gaseous phase. 9. A process as claimed in any one of Claims 1 to 7 characterised in that the carbonaceous materials are produced in synthesis of pyridine bases. 10. A process as claimed in any one of Claims 1 to 7 characterised in that the carbonaceous materials are produced in synthesis of gasoline from methanol. 11. A process as claimed in any one of Claims 1 to 7 characterised in that the carbonaceous materials are produced in cracking.

Inventors: ABE, NOBUYUKI, DOBA, MASANORI, ICHIHASHI, HIROSHI, IGUCHI, AKIRA, KITAMURA, MASARU, NIWA, TAKAYASU, SHIMIZU, SHINKICHI
Applicants: KOEI CHEMICAL COMPANY, LIMITED, SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1990
Main classification: B01J23
IPC codes: C07D213, C07D201, B01J38, B01J23, B01J29