Sandwich glass

Abstract: A sandwich glass comprises two glass plates and a resin layer interposed therebetween. The resin layer is produced by adding a hydrocarbon resin and an organic peroxide to ethylene-vinyl acetate copolymer and thermosetting them, the amounts of hydrocarbon resin and organic peroxide added to the EVA copolymer being preferably 1-100 parts by weight and 0.1-5 parts by weight respectively.

Description: This invention relates to a sandwich glass for use as a front glass (windscreen) and a side glass (window) of an automobile, as a window glass of a building and the like. In general, polyvinylbutyral resins have hitherto been mainly used as an intermediate layer for sandwich glasses. However, such a polyvinylbutyral resin is thermoplastic, so that it has the following drawbacks: (1) Since the polyvinylbutyral resin has a relatively low softening point, the sliding of glass plates or formation of bubbles in the sandwich glass occur due to heat after the glass plates are stuck to the resin; (2) Since the polyvinylbutyral resin is apt to be influenced by moisture, when the sandwich glass is left to stand under a high humidity atmosphere over a long period of time, the resin gradually whitens from the peripheral portion of the sandwich glass and also the adhesion force to the glass plate is reduced; and (3) The impact fracture resistance of the sandwich glass is dependent upon temperature, and in particular the penetration resistance rapidly decreases at a temperature exceeding room temperature, that is at a temperature not lower than about 30°C. In order to solve the above drawbacks of the polyvinylbutyral resin, the present inventors have previously proposed a sandwich glass obtained by interposing a thermosetting resin comprised of ethylene-vinyl acetate copolymer and an organic peroxide between glass plates and then thermosetting the resin (Japanese Patent laid open No. 57-196747). Considering safety as an important requirement of the sandwich glass, the impact resistance and the penetration resistance could not be said to be sufficient under a wide range of conditions in such previous proposal. It is, therefore, an aim of the present invention to provide sandwich glasses which improve the impact resistance and penetration resistance as compared with the conventional sandwich glass and which are safe even when breakage is caused through an external force. The present invention provides a sandwich glass comprising two glass plates and a resin layer interposed therebetween, and produced by interposing a thermosetting resin layer comprised of ethylene-vinyl acetate copolymer, hydrocarbon resin and organic peroxide between said two glass plates and then thermosetting said resin layer; wherein the amounts of said hydrocarbon resin and organic peroxide added to said ethylene-vinyl acetate copolymer are 1-100 parts by weight, and 0.1-5 parts by weight, respectively; wherein said hydrocarbon resin has a weight average molecular weight of 200-50,000; and wherein said ethylene-vinyl acetate copolymer has a vinyl acetate content of 10-50% by weight. The hydrocarbon resin used in the invention includes anyone of natural resins and synthetic resins. As the natural resin, rosin, rosin derivatives and terpene resin are suitably used. As the rosin, use may be made of gum resin, tall oil resin, wood resin and the like. As the rosin derivative, use may be made of hydrogenated rosin, disproportionated rosin, rosin polymer, rosin ester and metal salt of rosin. As the terpene resin, use may be made of terpene resins such as α-pinene, β-pinene and the like as well as terpene phenol resin. Furthermore, dammar, copal and shellac may be used as the natural resin. On the other hand, petroleum resins, phenolic resins and xylene resins are suitably used as the synthetic resin. As the petroleum resin, use may be made of aliphatic petroleum resin, aromatic petroleum resin, alicyclic petroleum resin, copolymeric petroleum resin, hydrogenated petroleum resin, pure monomeric petroleum resin and cumarone indene resin. As the phenolic resin, use may be made of alkyl phenol resins, modified phenolic resins and the like. As the xylene resin, use may be made of xylene resin and modified xylene resins. According to the invention, the amount of the hydrocarbon resin added to ethylene-vinyl acetate copolymer is 1-100 parts by weight, preferably 2-80 parts by weight. The hydrocarbon resin used in the invention has a weight average molecular weight of 200-50000, preferably 200-10000. In the ethylene-vinyl acetate copolymer used in the invention, the content of vinyl acetate is 10-50% by weight, preferably 15-40% by weight. When the vinyl acetate content is less than 10% by weight, the transparency becomes insufficient in the crosslinking and curing at high temperature, while when it exceeds 50% by weight, the impact resistance and penetration resistance of the resulting sandwich glass become poor. In the production of the sandwich glass according to the invention, the organic peroxide is used as a curing agent for ethylene-vinyl acetate copolymer, and there can be used any peroxides creating radicals by decomposition at a temperature of not lower than 100°C. Considering safeness in the mixing, organic peroxides having a 10 hour half-value period decomposition temperature of not lower than 70°C are preferably used, examples of which include 2,5-dimethylhexane-2,5-dihydroperoxide, 2,5-dimethyl-2,5-di(t-butylperoxy)hexane-3, di-t-butyl peroxide, t-butylcumyl peroxide, 2,5-dimethyl-2,5-di(t-butylperoxy)hexane, dicumyl peroxide, α,α'-bis(t-butylperoxyisopropyl)benzene, n-propyl-4,4'-bis(t-butylperoxy)valerate, 2,2-bis(t-butylperoxy)butane, 1,1-bis(t-butylperoxy)cyclohexane, 1,1-bis(t-butylperoxy)-3,3,5-trimethyl cyclohexane, t-butylperoxy benzoate, benzoyl peroxide and the like. As the organic peroxide, at least one of the above peroxides is used in an amount of 0.1 to 5 parts by weight based on 100 parts by weight of ethylene-vinyl acetate copolymer. According to the invention, acryloxy group-containing compounds, methacryloxy group-containing compounds or aryl group-containing compounds may be added as a curing aid for enhancing initial modulus of the ethylene-vinyl acetate copolymer to improve the penetration resistance. As the compound used for this purpose, use may be made of derivatives of acrylic acid and methacrylic acid such as esters thereof and so on. As an alcohol reside of the ester, mention may be made of alkyl groups such as methyl group, ethyl group, dodecyl group, stearyl group, lauryl group and the like as well as cyclohexyl group, tetrahydrofurfuryl group, aminoethyl group, 2-hydroxyethyl group, 3-hydroxypropyl group, 3-chloro-2-hydroxypropyl group and so on. Furthermore, esters with polyfunctional alcohol such as ethylene glycol, triethylene glycol, polyethylene glycol or the like may be used. As the aryl group-containing compound, diallyl phthalate, diallyl fumalate, diallyl maleate, triallyl isocyanurate, triallyl cyanurate and the like are preferably used. Moreover, the amount of such a compound is suitably 50% by weight or less with respect to the ethylene-vinyl acetate copolymer. According to the invention, a silane coupling agent may be added for further improving the adhesion force between ethylene-vinyl acetate copolymer and glass plate. As the silane coupling agent used for this purpose, mention may be made of well-known silanes such as γ-chloropropylmethoxy silane, vinyltrichloro silane, vinyltriethoxy silane, vinyl-tris(β-methoxyethoxy)silane, γ-methacryloxypropyl trimethoxy silane, β-(3,4-ethoxycyclohexyl)ethyl-trimethoxy silane, γ-glycidoxypropyl trimethoxy silane, vinyltriacetoxy silane, γ-mercaptopropyl trimethoxy silane, γ-aminopropyl triethoxy silane, N-β-(aminoethyl)-γ-aminopropyl trimethoxy silane and the like. The amount of the above silane coupling agent added is suitably 5 parts by weight or less. If necessary, a polymerization retarder such as hydroquinone, hydroquinone monomethyl ether, p-benzoquinone, methylhydroquinone or the like may be added in an amount of 5 parts by weight or less for improving the safeness, and also a colouring agent, a ultraviolet ray absorbing agent, an antioxidant, a discolouration preventive agent and the like may be added. As mentioned above, according to the invention, there can be provided sandwich glasses having excellent impact resistance and penetration resistance for use as the front glass (windscreen) and side glass (window) of an automobile, as the window glass of a building or the like and which are safe even when breakage is caused due to the action of an external force. The following examples are given in illustration of the invention and are not intended as limitations thereof. Example 1 Various components as shown in the following Table 1 were compounded and mixed in a roll mill heated at 80°C to prepare a resin. This resin was shaped into a sheet of 0.76 mm in thickness by means of a press and inserted between two previously washed and dried float glass plates of 3 mm in thickness, which was placed in a rubber bag. After deaeration under vacuum, the glass assembly was preliminarily pressed at a temperature of 80°C. Then, the preliminarily pressed sandwich glass was placed in an oven and treated at 130°C for 30 minutes. The resulting sandwich glass had high transparency and was free from optical distortion. When four specimens of the sandwich glass were subjected to a shot bag test from a dropping height of 75 cm according to a method of JIS R3205(1983), there were observed no cracks in all specimens. The transparency test was made by means of a haze meter made by Suga Testing Machine Co., Ltd. and as a result, a determined haze value was 0.8. The measured values are also shown in Table 1. Example 2 The same procedure as in Example 1 was repeated except that the amount of Arucon M-100 (trade name) used was 80 parts by weight. No cracks were observed in all of four specimens by the shot bag test. Moreover, the haze value was 0.9. Comparative Example 1 The same procedure as in Example 1 was repeated except that no Arucon M-100 (trade name) was used. In all of four specimens, the average length of opening portion in cracks observed by the shot bag test was 60 mm. Moreover, the haze value was 0.6. Example 1 Example 2 Comparative Example 1 Compounding recipe (part by weight) Ultrasen 634 100 100 100 Arucon M-100 30 80 - triaryl isocyanurate 2 2 2 γ-methacryloxy propyl trimethoxy silane 0.5 0.5 0.5 1,1-bis (t-butylperoxy) 3,3,5-trimethyl cyclohexane 2 2 2 Test result Shot bag test dropping height: 75 cm no crack no crack crack length 60mm Transparency test haze value (%) 0.8 0.9 0.6

Claims: A sandwich glass comprising two glass plates and a resin layer interposed therebetween, and produced by interposing a thermosetting resin layer comprised of ethylene-vinyl acetate copolymer, hydrocarbon resin and organic peroxide between said two glass plates and then thermosetting said resin layer; wherein the amounts of said hydrocarbon resin and organic peroxide added to said ethylene-vinyl acetate copolymer are 1-100 parts by weight, and 0.1-5 parts by weight, respectively; wherein said hydrocarbon resin has a weight average molecular weight of 200-50,000; and wherein said ethylene-vinyl acetate copolymer has a vinyl acetate content of 10-50% by weight. A sandwich glass as claimed in claim 1, characterized in that the amount of said hydrocarbon resin added to said ethylene-vinyl acetate copolymer is 2-80 parts by weight. A sandwich glass as claimed in claim 1 or 2, characterized in that said hydrocarbon resin has a weight average molecular weight of 200-10,000. A sandwich glass as claimed in any of claims 1 to 3, characterized in that said ethylene-vinyl acetate copolymer has a vinyl acetate content of 15-40% by weight. A sandwich glass as claimed in any of claims 1 to 4, characterized in that at least one compound selected from acryloxy group-containing compounds, methacryloxy group-containing compounds and aryl group-containing compounds is added in an amount of not more than 50 parts by weight to said ethylene-vinyl acetate copolymer as a curing aid. A sandwich glass as claimed in any of claims 1 to 5, characterized in that a silane coupling agent is added as an adhesion improver for glass in an amount of not more than 5 parts by weight to said ethylene-vinyl acetate copolymer.

Inventors: NAITO KAZUO, NIWA HIDEYUKI, SEGAWA MASASHI, TANUMA ITSUO, NAITO, KAZUO, NIWA, HIDEYUKI, SEGAWA, MASASHI, TANUMA, ITSUO
Applicants: BRIDGESTONE CORP, BRIDGESTONE CORPORATION
Application year: 1990
Main classification: B32B17
IPC codes: C09J131, C09J123, C08L31, B32B17, C08K5, C03C27, C08L101, C08L23