Weather-resistant polyacetal resin composition

Abstract: Weather-resistant polyacetal resin compositions and molded articles formed thereof include (A) a polyacetal base resin, and a weather-resistant effective amount of a weather-stabilizing package comprising, based on the total weight of the composition: (B) between 0.01 and 5% by weight of a weather stabilizer, (C) between 1 and 40% by weight of an acrylic resin and (D) between 1 and 20% by weight of fluororesin. The weather stabilizer may be at least one selected from the group consisting of benzotriazoles, benzophenones, aromatic benzoates, cyanoacrylates, oxalanilides and hindered amines.

Description: The present invention relates to polyacetal resin compositions having excellent weather resistance properties. More specifically, the present invention relates to weather-resistant polyacetal resin compositions which, in preferred embodiments, include a polyacetal base resin, a weather stabilizer, an acrylic resin and a fluororesin. As is well known, polyacetal resins have been used in various fields as an engineering plastic due to their excellent physical properties (such as mechanical and electric properties) and chemical properties (such as chemical resistance and heat resistance properties) that such resins possess. However, additional and more specialized properties are required of polyacetal resins as new end-use applications are identified. One property of polyacetal resins that is in continual need for improvement is their weather resistance. In this regard, polyacetal resins have recently been used to form molded parts used for automobile components as well as components for electrical appliances. As can be appreciated, these components are typically exposed to conditions that may disadvantageously affect the components' properties and/or appearance. For example, automotive components are usually subjected to sunlight, rain and/or outer atmosphere conditions for prolonged time periods. As a result, components used in such end-use environments become discolored and/or lose their surface smoothness or gloss. In addition, cracks may form on the component surface thereby disadvantageously affecting the quality of the component. To overcome these problems, weather stabilizers have typically been blended with resins so as to improve the resins' weather resistance properties. However, simply incorporating a weather stabilizer in a polyacetal base resin does not necessarily achieve satisfactory results. Thus, further improvements in the weather resistance properties of polyacetal resins have been needed. Prior proposals for producing weather-resistant polyacetal compositions include EP-A1-0 300 573, which specifies polyoxymethylene (polyacetal) comprising 5-40 % by weight of a polymethacrylic acid ester polymer and 0.5-4 % by weight of a pigment, dye or a mixture thereof. Our own prior patent application EP-A1-0 172 691 describes a polyacetal resin composition which includes (A) a light stabilizer selected from benzotriazoles, benzophenones, aromatic benzoates, cyanoacrylates and anilide oxalates plus (B) an aliphatic acid ester. Our later patent application EP-A1-0 356 167, which had not been published at the priority date of the present application and is thus to be considered under Articles 54(3) and 54(4) EPC, describes a polyacetal resin composition which includes 1 to 40 wt. % of an acrylate resin and 0.01 to 5 wt. % of a weather stabilizer such as benzotriazoles, benzophenones, aromatic benzoates, cyanoacrylates, oxalanilides and further a hindered amine. In this connection, a considerable effect can be obtained by incorporating a weather stabilizer and an acrylic resin into a polyacetal base resin. However, the resulting surface conditions (such as crack formation and gloss) and mechanical properties of molded articles formed of such a modified polyacetal resin are not always satisfactory when the articles are exposed for prolonged time periods to sunlight (ultraviolet rays), rain and like weather conditions. Thus, polyacetal resins having durable weather resistance properties are often required. Increasing the amounts of the weather stabilizer and the acrylic resin in the overall polyacetal resin compositions results in only limited improvements in the weather resistance properties. Furthermore, an increase in the amount of these additives usually results in deterioration of the resin's mechanical and physical properties. In addition, excess weather stabilizer and acrylic resin can cause poor mold release, adhesion to the mold and mold deposits during molding which can reduce the dimensional accuracy and/or impair the appearance of the molded article, as well as increasing the cleaning frequency of the mold. As a result, the efficiency of the molding operation is reduced. The present invention broadly relates to polyacetal resin compositions and molded articles formed of the same which retain their "as produced" surface state by inhibiting crack formation when the articles are used outdoors without sacrificing the desirable characteristics inherent in polyacetal resins generally. More particularly, the present invention provides a weather-resistant polyacetal resin composition comprising, based on the total weight of the composition: (A) between 35% and 97.99 % by weight of a polyacetal base resin having a polymeric chain with repeating constituent units most or all of which are oxymethylene groups, (B) between 0.01 and 5% by weight of a weather stabilizer selected from one or more of benzotriazoles, benzophenones, aromatic benzoates, cyanoacrylates, oxalanilides and hindered amines, (C) between 1 and 40% by weight of an acrylic resin being a homopolymer or copolymer of one or more of acrylic acid and its esters and methacrylic acid and its esters, and (D) between 1 and 20% by weight of a fluororesin selected from one or more of polytetrafluoroethylene, polytrifluoroethylene, polyhexafluoropropylene, polychlorotrifluoroethylene, polyvinyl fluoride, polyvinylidene fluoride and tetrafluoroethylene/hexafluoropropylene copolymer, tetrafluoroethylene/perfluoroalkyl vinyl ether copolymers, tetrafluoroethylene/perfluorosulphonyl fluoride vinyl ether copolymer, chlorotrifluoroethylene/ethylene copolymer and tetrafluoroethylene/propylene copolymer. The term "copolymer" as used herein represents random copolymers, alternating copolymers, block copolymers, graft copolymers and mixtures of them. The invention is described in more detail in the preferred exemplary embodiment which follows. The polyacetal base resin (A) used in the compositions of the present invention is a polymeric compound predominantly comprising repeating oxymethylene groups (-CH₂O-) as the main constituent units in the polymeric chain. The polyacetal base resin may thus be a polyoxymethylene homopolymer or a copolymer, terpolymer or a block copolymer comprised mainly of oxymethylene groups with a minor amount of other constituent units. The polyacetal resin is most preferably a linear chain structure, but branched or cross-linked structures may also employed. The degree of polymerization of the polyacetal base resin is similarly not particularly limited, although the polyacetal base resin will have a sufficiently high degree of polymerization so as to be classified as an "engineering resin" and/or will be normally solid at the ambient temperatures of its use. The weather stabilizers (B) used in the present invention include one or more stabilizing agents selected from (1) benzotriazoles, (2) benzophenones, (3) aromatic benzoates, (4) cyanoacrylates (5) oxalanilides and (6) hindered amines. A particularly preferred weather stabilizer (B) is provided by a combination of a hindered amine, and one or more compounds selected from benzotriazoles, benzophenones, aromatic benzoates, cyanoacrylates and oxalanilides. Specific examples of weather stabilizers (B) according to the invention include: (1) benzotriazoles : 2-(2'-hydroxy-5'-methylphenyl)benzotriazole, 2-(2'-hydroxy-3',5'-di-t-butylphenyl)benzotriazole, 2-(3,5-di-t-amyl-2-hydroxyphenyl)benzotriazole, 2-(2'-hydroxy-3'-5'-diisoamylphenyl)benzotriazole, 2-[(hydroxy-3,5-bi(α,α-dimethylbenzyl)phenyl]benzotriazole and 2-(2'hydroxy-4'-octoxyphenyl)benzotriazole. (2) benzophenones 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-octoxybenzophenone, 2-hydroxy-4-dodecyloxybenzophenone, 2,2'-dihydroxy-4-methoxybenzophenone, 2,2'-dihydroxy-4,4'-dimethoxybenophenone, 2-hydroxy-4-methoxy-5-sulphobenzophenone and 2-hydroxy-4-oxybenzylbenzophenone, (3) aromatic benzoates : p-t-butylphenyl salicylate and p-octylphenyl salicylate (4) cyanoacrylates : 2-ethylhexyl-2-cyano-3,3'-diphenylacrylate and ethyl-2-cyano-3,3'-diphenylacrylate. (5) oxalanilides : N-(2-ethylphenyl)-N'-(2-ethoxy-5-t-butylphenyl) oxamide and N-(2-ethyl-phenyl)-N'-(2-ethoxyphenyl)oxamide (6) hindered amines : piperidine derivatives each having a sterically hindered group, such as: 4-acetoxy-2,2,6,6-tetramethylpiperidine, 4-stearoyloxy-2,2,6,6-tetramethylpiperidine, 4-acryloyloxy-2,2,6,6-tetramethylpiperidine, 4-methoxy-2,2,6,6-tetramethylpiperidine, 4-benzoyloxy-2,2,6,6-tetramethylpiperidine, 4-cyclohexyloxy-2,2,6,6-tetramethylpiperidine, 4-phenoxy-2,2,6,6-tetramethylpiperidine, 4-benzyloxy-2,2,6,6-tetramethylpiperidine, 4-(phenylcarbamoyloxy)-2,2,6,6-tetramethyl-piperidine, bis(2,2,6,6-tetramethyl-4-piperidyl) oxalate, bis(2,2,6,6-tetramethyl-4-piperidyl) oxalate, bis(2,2,6,6-tetramethyl-4-piperidyl) malonate, bis(2,2,6,6-tetramethyl-4-piperidyl) adipate, bis(2,2,6,6-tetramethyl-4-piperidyl) sebacate, bis(1,2,2,6,6-pentamethylpiperidyl) sebacate, bis(2,2,6,6-tetramethyl-4-piperidyl) terephthalate, 1,2-bis(2,2,6,6-tetramethyl-4-piperidyloxy)ethane, bis(2,2,6,6-tetramethyl-4-piperidyl) hexamethylene-1,6-dicarbamate, bis-(1-methyl-2,2,6,6-tetramethyl-4-piperidyl) adipate and tris(2,2,6,6-tetramethyl-4-piperidyl) benzene-1,3,5-tricarboxylate. Furthermore high-molecular piperidine derivative polycondensates such as dimethyl succinate/1-(2-hydroxyethyl)-4-hydroxy-2,2,6,6-tetramethyl-piperidine polycondensate are also effective. The above-noted weather stabilizers may be used alone, or preferably as a mixture of two or more thereof. A combination of weather stabilizers that includes at least one hindered amine is particularly preferred. A suitable amount of the weather stabilizer used herein is between 0.01 and 5% by weight (based on the entire composition weight), particularly preferably between 0.02 and 3% by weight. When the amount of the weather stabilizer is insufficient, the intended weather-stabilizing effect cannot be attained. On the other hand, an excessive amount of weather-stabilizer is not only economically disadvantageous, but also poses problems such as deterioration of mechanical properties and mold contamination. The acrylic resin (C) used in the present invention is preferably selected from the homopolymers or copolymers of acrylic acid and its esters (such as methyl acrylate, ethyl acrylate, n-propyl acrylate, isopropyl acrylate, n-butyl acrylate, n-hexyl acrylate and n-octyl acrylate), or those of methacrylic acid and its esters (such as methyl methacrylate ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, n butyl methacrylate, n-amyl methacrylate and n-octyl methacrylate), or copolymers of such polymers with styrene, acrylonitrile butadiene and isoprene. Preferred are homopolymers of methyl methacrylate or copolymers of methyl methacrylate as the main constituent and a methacrylate other than methyl methacrylate, styrene or acrylonitrile. The amount of the acrylic resin (C) used herein is suitably between 1 and 40% by weight based on the entire composition weight) particularly preferably between 5 and 30% by weight. When the amount of the acrylic resin is insufficient, the resulting resin composition does not exhibit sufficient weather resistance properties, especially prevention of crack formation on the surface of the molded article. Excessive amounts of acrylic resin produce an unfavorable effect on the mechanical properties and thermal stability of the molded articles. Although the weather resistance is improved somewhat by incorporating an acrylic resin in combination with a weather stabilizer, the effect is still insufficient for many end-use applications. In addition, the above-described problems, such as deterioration of the mechanical and physical properties and disturbance of the molding operation, are typically still present. Under these circumstances, the present invention is especially characterized in that the above-described polyacetal base resin, weather stabilizer, and acrylic resin components are used in combination with a fluororesin (D). Such a combination of components has been discovered to be effective in improving the weather resistance as evidenced by the surface gloss retention and crack formation inhibition without impairing the other well-balanced physical characteristics inherent in polyacetal resins. Examples of fluororesins usable in the compositions of the present invention include polytetrafluoroethylene, polytrifluoroethylene, polyhexafluoropropylene, polychlorotrifluoroethylene, polyvinyl fluoride, polyvinylidene fluoride and tetrafluoroethylene/hexafluoropropylene copolymer, tetrafluoroethylene/perfluoroalky vinyl ether copolymers, tetrafluoroethylene/perfluorosulphonyl fluoride vinyl ether copolymer, chlorotrifluoroethylene/ethylene copolymer and tetrafluoroethylene/propylene copolymer. The term "copolymer" as used herein represents random copolymers, alternating copolymers, block copolymers, graft copolymers and mixtures of them. Among them, preferred are polytetrafluoroethylene, polyvinyl fluoride, polyvinylidene fluoride, tetrafluoroethylene/hexafluoropropylene copolymer, tetrafluoroethylene/ethylene copolymer and mixtures of them. More preferred are polytetrafluoroethylene, polyvinylidene fluoride and tetrafluoroethylene/ethylene copolymer. The amount of the fluororesin used herein is suitably between 1 and 20% by weight (based on the entire composition weight), particularly preferably between 2 and 10% by weight. When the fluororesin component is used in amounts of less than 1% by weight, inadequate effects in terms of improving the weather resistance properties are obtained. On the other hand, when the fluororesin content exceeds 20% by weight, unfavorable effects upon the normal desirable characteristics inherent in polyacetal resins are usually observed. Although the weather resistance properties of polyacetal resin are not significantly improved when the fluororesin component is added to the polyacetal resin alone, or together with either the weather stabilizer or the acrylic resin, significant synergistic effects are obtained in terms of inhibiting crack formation on the surface of molded articles and/or reducing discoloration when a combination of components including a weather stabilizer, an acrylic resin and a fluororesin is employed. Although the reasons why the beneficial effects obtained by the present invention are not fully understood at this time, fluororesins are extremely compatible with acrylic resins. In this regard, the fluidity of the acrylic resin is improved causing it to congregate locally at or near the surface of a molded article formed of the composition of this invention. Thus, the amount of fluororesin that may be added in combination with an acrylic resin can be greater than that which can be added to the polyaacetal base resin in the absence of an acrylic resin. As a result, the weather resistance is significantly improved with only a small amount of acrylic resin. Other effects that are obtained are that flawed molding surfaces are prevented and mold-release properties are improved -- effects that cannot be obtained when the acrylic resin is used alone. It is sometimes desirable to add various known additives to the composition of the present invention to improve further the thermal stability properties. In this regard, antioxidants, nitrogen compounds, alkali metal compounds and alkaline earth metal compounds may be preferably used, either alone or as a combination of two or more thereof. The compositions of the present invertion can be colored in any desired manner by suitably adding a dye or a pigment, such as carbon black, thereto. Particularly, the use of carbon black is effective as a means to improve further the weather resistance properties of the polyacetal compositions in addition to imparting color characteristics thereto. To impart desired properties to the composition of the present invention according to the use thereof, one or more of known additives can be incorporated thereinto. Other additives conventionally employed in thermoplastic resin compositions may be incorporated into the polyacetal compositions of the present invention to further improve the physical and/or chemical properties depending upon the intended end use. These conventional additives include lubricants, nucleating agents, release agents, antistatic agents, surfactants, organic polymeric materials, and inorganic or organic, fibrous, powdery or platy fillers. The compositions of the present invention can be produced with known apparatus using known processing techniques for producing synthetic resin compositions. More specifically, the necessary components may be mixed together, kneaded and extruded using a single-screw or twin-screw extruder to form molding pellets, from which molded articles may be formed. Alternatively, the simultaneous preparation of the composition and molding of the final article may be practised. In another process, a part or the entirety of the resin components is pulverized in order to facilitate dispersion. The components are then mixed and melt extruded to form pellets to be shaped into a molding. The stabilizers and additives may be incorporated into the composition at any stage in the process. For example, they can be added to the composition and mixed immediately before the formation of the final molding. The resin compositions of the present invention can be produced by any expedient plastics fabrication technique, such as extrusion molding, injection molding, compression molding, vacuum molding, blow molding and foam molding processes. The compositions of the present invertion exhibit superior surface conditions after exposure to ultraviolet rays or water for prolonged time periods. Specifically, crack formation time is far longer, the gloss-maintenance rate is higher and the extent of discoloration is lower for the compositions of this invention as compared to conventional polyacetal resin compositions. Furthermore, according to the present invention, the problems that are encountered when acrylic resins are used alone, such as poor moldability (releasability) and surface flawing can be overcome. The weather-resistant polyacetal resin compositions of the present invention are suitable for use as a material for moldings in a number of end use applications in which weather resistance is required. Moldings formed of the compositions of this invention may be exposed to solar rays and rain for prolonged time period and therefore may be used as exterior automotive parts (e.g. inner door handles, fuel lids, wheel covers, front fenders, and spoilers), interior automotive parts (e.g. inner door handles and regulator handles), electric appliances, cameras, parts for other industrial products, construction materials and pipes, and other household articles. EXAMPLES The following nonlimiting Examples will further illustrate the present invention. In these Examples the composition properties such as weather resistance were determined using the following methods: (1) Weather resistance test (A and B) The crack formation time and changes in surface conditions were determined with the following two weather resistance tests: test method A : the samples were irradiated with ultraviolet rays with an ultra-accelerating weather resistance tester (SUV-W-11 of Iwasaki Electric Co Ltd) in an atmosphere of 83°C; test method B : the samples were irradiated with ultraviolet rays under weathering conditions (including rain spray) at 63°C with a weatherometer (WBL-SUN-HCH of Suga Test Instruments Co Ltd) (2) Crack formation time : Test pieces were irradiated with ultraviolet rays using the above-described weather resistance testers under predetermined conditions for a given period of time. Crack formation on the surfaces of the test pieces were then visibly evaluated with a magnifying lens at 10X magnification. The "crack formation time" was the time at which the cracks were first observed, with higher values being indicative of better weather resistance properties. (3) Change in gloss : Test pieces were irradiated with ultraviolet rays with the above-described weather resistance testers under predetermined conditions for a given time to observe the gloss of the test pieces before and after the irradiation. The change in the gloss was classified in five numerical ranks. The lower the numerical rank the less change, or the less reduction of gloss was present. Gloss was determined with a digital variable-angle gloss meter (UGV-4D manufactured by Suga Test Instruments Co Ltd) and the extent of gloss reduction was based upon the percentage of the initial gloss that was retained. (4) Moldability (releasability): Fifty plate-type moldings (70mm X 50mm X 3mm) were continuously produced under molding conditions whereby the cylinder temperature was 190°C and the mold temperature was 80°C. The molding states were classified into the following five qualitative ranks: o ○ : excellent (no problem) ○ : good (1 to 4 plates remaining in the mold) Δ : comparatively poor (5 to 10 plates remaining in the mold ΔX : poor (11 to 25 plates remaining in the mold), and X : very poor (26 or more plates remaining in the mold Examples 1 to 15 and Comparative Examples 1 to 12 A weather stabilizer (B), acrylic resin (C), fluororesin (D) and if necessary, carbon black were added to Polyacetal resin (A) (Duracon (M 90); trade name Polyplastics Co Ltd ) as shown in Table 1. The components were mixed together and melt-kneaded using a 30mm twin-screw extruder to pelletize the composition. Then the pellets were shaped into test pieces with an injection molding machine to evaluate their weather resistance and other properties. For comparison, the same procedure as that described above was repeated except that the weather stabilizer (B) was added singly or in combination with acrylic resin (C) or fluororesin (D) (and, if necessary, carbon black). Note 1: B-1: 2-[2-hydroxy-3,5-bis(α,α-dimethyl benzylphenyl] benzotriazole, B-2: 2-hydroxy-4-oxybenzylbenzophenone; Note 2: B-3: bis(2,2,6,6-tetramethyl-4-piperidyl)sebacate, B-4: dimethylsuccinate/1-(2-hydroxyethyl-4-hydroxy-2,2,6,6-tetramethylypiperidine) polycondensate; Note 3: C-1: methyl methacrylate resin [average molecular weight: 60.000] C-2: methyl methacrylate resin [average molecular weight: 20,000] Note 4: D-1: polyvinylidene fluoride D-2: polytetrafluoroethylene While the invention has been described in connection with what is presently considered to be the most practical and preferred embodiment, it is to be understood that the invention is not to be limited to the disclosed embodiment, but on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims.

Claims: A weather-resistant polyacetal resin composition comprising, based on the total weight of the composition: (A) between 35% and 97.99% by weight of a polyacetal base resin having a polymeric chain with repeating constituent units most or all of which are oxymethylene groups, (B) between 0.01 and 5% by weight of a weather stabilizer selected from one or more of benzotriazoles, benzophenones, aromatic benzoates, cyanoacrylates, oxalanilides and hindered amines, (C) between 1 and 40% by weight of an acrylic resin being a homopolymer or copolymer of one or more of acrylic acid and its esters and methacrylic acid and its esters, and (D) between 1 and 20% by weight of a fluororesin selected from one or more of polytetrafluoroethylene, polytrifluoroethylene, polyhexafluoropropylene, polychlorotrifluoroethylene, polyvinyl fluoride, polyvinylidene fluoride and tetrafluoroethylene/hexafluoropropylene copolymer, tetrafluoroethylene/perfluoroalky vinyl ether copolymers, tetrafluoroethylene/perfluorosulphonyl fluoride vinyl ether copolymer, chlorotrifluoroethylene/ethylene copolymer and tetrafluoroethylene/propylene copolymer. A composition as claimed in claim 1, wherein the weather stabilizer (B) is a combination of a hindered amine, and one or more compounds selected from benzotriazoles, benzophenones, aromatic benzoates, cyanoacrylates and oxalanilides. A composition as claimed in claim 1 or claim 2, wherein the acrylic resin (C) is a methyl methacrylate homopolymer or a methyl methacrylate copolymer mainly comprised of methyl methacrylate. A composition as claimed in any preceding claim, which further comprises at least one additive selected from lubricants, nucleating agents, release agents, antistatic agents, surfactants, impact modifiers, and inorganic or organic fibrous, powdery or platy fillers. A composition as claimed in any preceding claim, which further includes a colorant. A composition as claimed in any claim 5, wherein the colorant is carbon black. A molded article which comprises a weather-resistant polyacetal resin composition as claimed in any preceding claim.

Inventors: KATSUMATA TORU, KATSUMATA, TORU
Applicants: POLYPLASTICS CO, POLYPLASTICS CO. LTD.
Application year: 1990
Main classification: C08L59
IPC codes: C08K5, C08L27, C08L33, C08L87, C08L59