Non-tacky composit resin composition and process for the preparation thereof

Abstract: A non-tacky composite resin composition comprises a polyvinyl chloride and a polyurethane containing in the molecule a group of the general formula (I) in which Me is a methyl group, n is an integer defined by 1 ≦ n ≦ 100, each of X an Y is an integer defined by 1 ≦ X ≦ 3, 0 ≦ Y ≦ 2, and X + Y = 3, and R is an alkylene group or alkylene groups which may be linked by one or more alkyleneoxy groups.

Description: The present invention relates to a non-tacky composite resin composition of a polyurethane-polyvinyl chloride series, and a process for the preparation of the composition. Polyvinyl chloride type resins (hereinafter the term "polyvinyl chloride" is referred to as "PVC") in combination with a low-molecular weight plasticizer such as dioctyl phthalate are used as general-purpose non-rigid PVC resins in a variety of applications. The non-rigid PVC resins, however, have defects of low oil-resistance, low heat-resistance and low adhesiveness, caused by extraction and migration of the low-molecular-weight plasticizer. To improve the defects, polymer alloys prepared by blending or copolymerization of polyurethane resins (hereinafter the term "polyurethane" is referred to as "PU") and PVC have been known to give a sufficiently non-rigid PVC-PU type composite resin without using a low-molecular-weight plasticizer which is liable to be extracted or migrate. However, in producing such a non-rigid PVC-PU type composite resin, a a large quantity of soft PU is required. The PVC-PU type composite resin prepared by using a large quantity of PU resin has defects such as strong surface tackiness. For example, the problems are then encountered that lumping occurs on storage, and that mold-release is poor on thermoforming such as injection molding, which lowers processability. The surface tackiness frequently hinders practical use of the products. In particular, powder sinter molding of a conventional PVC-PU type composite resin does not give products having satisfactory mechanical and surface properties because the PU component is not readily fusible under non-shearing conditions. From these reasons, application of the PVC-PU type composit resins is frequently limited in spite of their superior properties. In some application fields, a lubricant such as a higher fatty acid or silicone oil, a dusting powder such as talc, or a filler such as calcium carbonate is added to improve processability and surface tackiness of the products. However, the use of the lubricant cause inconveniences of decrease of adhesiveness, or staining of the mold owing to migration of lubricant to the surface upon molding, and the use of a dusting powder or a filler may lower the transparency of the product or may worsen stain resistance. For the purpose of avoiding such inconveniences, a group represented by any of the general formulas (1) to (3): (where Me is methyl, and m is an integer of 1 ≦ m ≦ 450,) is introduced into the polyurethane molecule to prevent the migration of the lubricant to the surface and to improve slipping properties and mold releasing properties of the PU. However, the PVC-PU type composite resins produced using a polyurethane having a group represented by the above general formula (1), (2) or (3) are not sufficiently improved in terms of lumping and mold-release and are impaired considerably in adhesiveness, although the adhesiveness is an important characteristic of PVC-PU type composite resins. A further proposal is set out in EP-A-0277816 which describes a polysiloxane compound of the formula in which R is H, Me or Et and n is 0-4,000 for improving the surface characteristics of silicone-modified polyurethanes. This symmetrical polysiloxane compound is contrasted in EP-A-0277816 with the unsymmetrical polysiloxane of JP-A-61-67962 which is said to cause problems since the two hydroxy groups have different reactivities and it is therefore difficult to obtain stabilised physical properties. The present invention seeks to provide a non-tacky composite resin composition of the non-rigid PVC-PU type which is improved in terms of its surface tackiness and mold staining and mold release properties and lumping during storage, without impairing the superior characteristics of heat resistance, oil resistance, and adhesive properties, and which has satisfactory low temperature impact strength and fogging resistance (namely, prevention of oil film formation on a glass surface) and is applicable to powder sinter molding. According to a first aspect of the present invention, there is provided a non-tacky composite resin composition, comprising a polyvinyl chloride having a polymerization degree of not lower than 600 and a polyurethane containing in the molecule a group of the general formula (I) in which Me is a methyl group, n is an integer defined by 1 ≦ n ≦ 100, each of X and Y is an integer defined by 1 ≦ X ≦ 3, 0 ≦ Y ≦ 2, and X + Y = 3, and R is an alkylene group or alkylene groups which may be linked by one or more alkyleneoxy groups. According to a second aspect of the invention, there is provided a process for producing such a non-tacky composite resin composition, the process comprising preparing the polyurethane by reacting together (A) a diisocyanate, (B) a polyester-polyol derived by reacting a dicarboxylic acid with a diol containing 3-methyl-1,5-pentanediol and/or 2-methyl-1,8-octanediol in an amount of at least 30 mol % and one or more other short-chain diols at a content of less than 70 mol %, and (C) a diol-terminated polysiloxane of the general formula (II): in which Me, n, X, Y and R have the meanings given above, and blending the resulting polyurethane with polyvinyl chloride. According to a third aspect of the present invention, there is provided another process for producing such a non-tacky composite resin composition, the process comprising reacting a diol-terminated polysiloxane of the general formula (II) with a polyol, an isocyanate and a polyvinyl chloride. The PU used in the present invention is prepared by reacting an isocyanate with a modified polysiloxane having two OH groups at one end (hereinafter referred to as "one-diol-terminated polysiloxane") represented by the general formula (II): (where Me, n, X, Y and R are as defined above), and a polyol. In the PU having the group represented by the general formula (I) described above, the R is preferably an alkylene group having 1 to 5 carbons which may be linked by one or two ethyleneoxy groups or propyleneoxy groups. The examples of "R" are: -CH₂CH₂- -CH₂CH₂CH₂CH₂- -CH₂CH₂CH₂CH₂CH₂- -CH₂CH₂CH₂-O-CH₂- -CH₂CH₂CH₂-O-CH₂CH₂-O-CH₂- -CH₂CH₂CH₂-O-CH₂CH₂CH₂-O-CH₂- The one-diol-terminated polysiloxane used in the present invention is derived by addition reaction of a compound exemplified below: with a polysiloxane having an group derived by stopping the polymerization reaction with trichlorosilane, methyldichlorosilane and dimethylchlorosilane. The one-diol-terminated polysiloxane has preferably a number-average molecular weight within the range of from 340 to 10,000, more preferably from 500 to 5,000. The one-diol-terminated polysiloxane having a number-average molecular weight of 5,000 or higher need to be added in a larger amount to suppress the tackiness of the surface of the PVC-PU type composit resin, and is liable to impair adhesive properties. The one-diol-terminated polysiloxane having a number-average molecular weight of 10,000 or more exhibits this tendency further more remarkably. For the purpose of improvement in surface tackiness and adhesive properties, the one-diol-terminated polysiloxane is preferably used in an amount not more than 5 % , more preferably in the range of from 0.1 to 3 % based on the PU component in the non-tacky PVC-PU type composite resin composition. The polyol employed in the present invention include long-chain polyols and short-chain polyols which are conventionally used in the preparation of PUs. The long-chain polyols used for formation of PUs include polyester type polyols, polyetherpolyols, polycarbonate-polyols, vinyl-type polyols, diene-type polyols, castor oil-type polyols, polyolefin-type polyols, and copolymers thereof. These long-chain polyols have preferably a number-average molecular weight within the range of from 300 to 10,000, more preferably from 500 to 8,000, still more preferably from 1,500 to 8,000, from the standpoint of compatibility of the PU derived from the abovementioned polyol and PU. The short-chain polyols used for the preparation of PUs include aliphatic, alicyclic, aromatic, substituted aliphatic, and heterocyclic dihydroxy compounds, trihydroxy compounds and tetrahydroxy compounds. In particular, long-chain polyols for the preparation of PUs for the composite resin compositions suitable for powder sinter molding are preferably polyester-polyols derived by reacting a dicarboxylic acid with a diol containing 3-methyl-1,5-pentanediol and/or 2-methyl-1,8-octanediol respectively or totally at a content of at least 30 mol % and other short-chain diols at a content of less than 70 mol %. The dicarboxylic acid is exemplified by adipic acid, pimelic acid, suberic acid, azelaic acid, and sebacic acid. The short-chain diols include aliphatic, alicyclic, and substituted aliphatic diols such as ethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,3-butanediol 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, neopentyl glycol, 1,9-nonanediol and 1,4-cyclohexane dimethanol. The isocyanate compounds used in the present invention include aromatic, aliphatic, and alicyclic diisocyanates used conventionally for manufacture of PUs. Preferable therefore are diphenylmethane diisocyanate, tolylene diisocyanate, hexamethylene diisocyanate, 4,4′-dicyclohexylmethane diisocyanate and isophorone diisocyanate. The amount of the isocyanate compound used in the PU component according to the present invention is preferably in the range of from 0.5 to 3, more preferably from 0.7 to 1.5, still more preferably from 0.7 to 1.1 in terms of NCO/OH molar ratio based on the total OH groups of the long-chain and short-chain polyols and the one-diol-terminated polysiloxane. The PVC used in the present invention are polymers containing vinyl chloride units having a polymerization degree of not lower than 600, preferably in the range of from 700 to 1,300, including polyvinyl chloride homopolymers or copolymers composed mainly of vinyl chloride such as vinyl chloride/vinyl acetate copolymers and vinyl chloride/ethylene/vinyl acetate copolymers. The PVC may be blended preliminarily with an additive such as a stabilizer, a lubricant and a colorant. Further, in the present invention, polymer-blended polyvinyl chloride may be used which has been preliminarily prepared by blending with a thermoplastic resin or rubber other than PU and compatible with PVC such as an acrylic resin, a styrene resin, an ABS resin and a nitrile rubber. In the present invention, from the viewpoint of improving surface tackiness, adhesiveness, and fusibility in sinter molding of the composite resin compositions, the weight ratio of the PVC component and the PU component is preferably in the range of from 100/1000 to 100/10, more preferably from 100/200 to 100/20, still more preferably 100/150 to 100/50. In the present invention, a plasticizer may be combinedly used in order to further improve the surface tackiness, adhesive properties, and fusibility of the composite resin compositions. The amount used thereof is preferably not more than 20 parts by weight based on 100 parts by weight of the composite resin from the stand point of securing long-term durability, and fogging resistance. The plasticizers which may be used in the present invention include those conventionally used for PVC such as phthalic esters, trimellitic esters, dibasic acid esters, adipic polyesters, epoxy compounds, inorganic acid esters, and glycol esters. Specific examples are dioctyl phthalate, trioctyl trimellitate, 2-ethylhexyl adipate, 2-ethylhexyl azelate, epoxidated soybean oil, epoxidated linseed oil, tricresyl phosphate, tributoxyethyl phosphate and dibutyldiglycol adipate. The composite resin composition according to the present invention may contain dusting powder. The preferable dusting powder includes PVC of from 1 to 10 µm diameter. And PVC having a polymerization degree of not less than 1,700, or having a crosslinked structure may be used. The composite resin compositions having a particle diameter in the range of from 50 to 500 µm are especially preferable for powder sinter molding. The process for the preparation of the non-tacky composite resin composition of the present invention includes: a method of reacting a one-diol-terminated polysiloxane represented by the general formula (II) shown above, a polyol, an isocyanate compound, and a PVC; a method of reacting a one-diol-terminated polysiloxane represented by the general formula (II) shown above, a polyol, and an isocyanate compound to form a PU having the group represented by the general formula (I) shown above in the molecule, and subsequently blending the resulting PU with a PVC; and a method of firstly reacting an isocyanate compound with a one-diol-terminated polysiloxane represented by the general formula (II) shown above, and subsequently reacting with a polyol to form a PU having the group represented by the general formula (I) shown above in the molecule, and further blending the resulting PU with a PVC. More specifically, the non-tacky composite resin composition of a PVC-PU type according to the present invention is produced, for example, by the processes below. (1) Blending of a PVC with a PU having a group represented by the general formula (I) shown above in the molecule: This process includes, in addition to a mechanical blending of a PVC with a PU, a method of blending solutions of the materials in organic solvents, and a method of blending an emulsion of the PVC and/or the PU; and (2) Reaction of a one-diol-terminated polysiloxane represented by the general formula (II) shown above, a polyol, and an isocyanate compound: This process includes reactions of these compounds in one batch, as well as successive reactions in arbitrary combinations and sequence. The present invention provides a non-tacky composite resin composition of a PVC-PU series which has combinedly characteristics of the PU of toughness, wear resistance, solvent resistance and characteristics of PVC of weatherability, moldability, and is superior in heat resistance and adhesive property, and is improved significantly in surface tackiness. The present invention also provides a simplified and economical process for the preparation of the non-tacky composite resin composition. The non-tacky composite resin composition of the present invention is applicable in a variety of application fields such as films, sheets, leathers, tubes, hoses, wrapping films, wire coatings, coating materials and paints. In particular, sheets and films made of a conventional non-rigid PVC-PU type composite resin have tackiness which causes inconvenience in workability after winding-up, so that the superior properties thereof have not been practically utilized in practical use. The present invention has improved this disadvantage significantly. Further, the composite resin has satisfactory mold-releasability in molding of various articles, which improves remarkably the production efficiency. On the other hand, retention of the adhesive property of the non-tacky composite resin composition according to the present invention is important in the case where the composition is used as a surface material for a rigid plastic core. The non-tacky composite resin composition of the present invention prepared by using a specified polyester-polyol, in addition to the abovementioned characteristics, has fogging resistance as well as low-temperature impact strength and superior molding characteristics (such as sufficient fusibility and less mold-staining) in powder sinter molding, which properties are incompatible, and the solution of this problem has been difficult. Accordingly, this composition can be molded efficiently by means of powder sinter molding into a large molded article in complicated shape such as molded internal parts of vehicles and large high-performance instrument panels. Thus, the present invention is of great significance because of especially broad range of application fields of the products. The present invention is described more specifically referring to examples. In the Examples, the term "parts" means "parts by weight". Reference example 1 2,360 g (20 mols) of 1,6-hexanediol, 2,360 g (20 mols) of 3-methyl-1,5-pentanediol, 1,060 g (10 mols) of neopentylglycol, and 6,512 g (44.6 mols) of adipic acid were placed in a 15-liter reactor provided with a condenser. Thereto, 0.2 g of tetrabutyl titanate was added and dehydration reaction was allowed to proceed at 200°C at an atmospheric pressure for 12 hours, and further at 200°C for 12 hours under reduced pressure. Thereby, 10,680 g of a polyester-polyol (hereinafter referred to as "PE-1") was obtained which has an acid value of 0.2, a hydroxyl value of 55.9, and a number-average molecular weight of 2,000. Reference examples 2 to 6 Polyester-polyols were prepared in the same manner as in Reference example 1 except that the diols and the dicarboxylic acid were changed. Table 1 shows the starting materials and the molar ratios (mol %) thereof, and the number-average molecular weight of the resulting polyester-polyol. Reference example 7 To 2 parts of a one-diol-terminated polysiloxane having a polymerization degree of 2,000 of the formula: 17 parts of hexamethylene diisocyanate was added with stirring, and the reaction was allowed to proceed at 75°C for 4 hours. The resulting product is referred to as PS-1. Reference example 8 The reaction was carried out in the same manner as in Reference example 7 except that the one-diol-terminated polysiloxane used in Reference example 7 was replaced by the one having a polymerization degree of 2,000 of the formula: and the hexamethylene diisocyanate was replaced by tolylene diisocyanate. The resulting product is referred to as PS-2. Comparative reference example 1 The reaction was carried out in the same manner as in Reference example 7 except that the one-diol-terminated polysiloxane used in Reference example 7 was replaced by the 2 parts of modified polysiloxane having an OH group respectively on both ends and having a polymerization degree of 5,000 of the formula: The resulting product is referred to as PS-3. Example 1 200 parts of polyester-diol having a polymerization degree of 2,000 prepared from a mixed diol consisting of 1,6-hexanediol and neopentylglycol (1/1) and adipic acid was added to PS-1 and the mixture was stirred at a high speed. Subsequently, the mixture was spread on a vat in a drier kept at 120°C, the reaction was completed for one hour. 100 parts of the resulting PU was kneaded with 100 parts of a powdery PVC having a polymerization degree of 1,000, 0.5 part of calcium stearate, and 0.5 part of zinc stearate at 150°C for 10 minutes. The blended matter was pressed into a sheet of 0.8 mm thick. Example 2 A sheet was prepared in the same manner as in Example 1 except that PS-2 was used in place of PS-1. Examples 3 and 4 A sheet was prepared in the same manner as in Example 1 except that the amounts of the one-diol-terminated polysiloxane and the hexamethylene diisocyanate to be added to PS-1 were changed respectively as shown in Table 2. Example 5 16 parts of hexamethylene diisocyanate and 200 parts of the polyester-diol used in Example 1 were added to 2 parts of the one-diol-terminated polysiloxane used in Reference example 7, and the mixture was stirred at a high speed. Subsequently, the mixture was spread on a vat in a drier kept at 120°C, and the reaction was completed for one hour. There were mixed 40 parts of the resulting PU, 40 parts of PVC having a polymerization degree of 1,000, 0.4 parts of calcium stearate, 0.4 parts of zinc stearate, and 20 parts of flakes in a size of approximately 1 cm x 1 cm, which was given by cutting from the sheet prepared in Example 4.. The resulting flakes were kneaded at 150°C for 10 minutes to press into a sheet of 0.8 mm thick. Comparative example 1 A mixture of 16 parts of hexamethylene diisocyanate and 200 parts of polyester-diol used in Example 1 was agitated at a high speed. The mixture was spread on a vat in a drier kept at 120°C, and the reaction was completed for one hour. Therefrom, a sheet was prepared in the same manner as in Example 1. Comparative example 2 A sheet was prepared in the same manner as in Example 1 except that PS-3 was used in place of PS-1. [METHOD OF MEASUREMENT OF PROPERTIES] The properties of the sheets obtained in Examples 1 - 5 and Comparative examples 1 and 2 were measured as described below. The measured properties are shown in Table 3. 1. Surface tackiness (Lumping tendency): The sheet was cut in a size of 5 cm × 5 cm. Two of the cut sheets were superposed, and pressed uniformly in a plane with a 500 g load for 24 hours in a thermostat kept at 25°C. The separability of the sheets was evaluated. The results are shown in two evaluation grade below: ○ : Not adhered × : Not easily separated 2. Mold releasability (1): A nickel plate having a leather pattern engraved on the surface and the sample sheet were superposed and pressed at a pressure of 50 kg/cm² at 160°C for 5 minutes. After water-cooling, the releasing force (g/cm) to separate the sheet from the nickel plate was measured. 3. Adhesive property (1): The sample sheet and an ABS plate (made by Nippon Test Panel K.K.) were contact-bonded with a roll by using a two-part polyurethane type adhesive [Nippolan 3022 (100 parts) and Coronate L (5 parts); made by Nippon Polyurethane Industry Co., LTD.]. The bonded article was cured at 60°C for 3 hours. After three days therefrom, adhesion strength (kg/cm) was measured. 4. Hardness: The hardness was measured according to JIS K6301. 5. Tensile properties (tensile strength, elongation): The tensile properties were measured according to JIS K6723. Example 6 (1) 100 parts of a powdery PVC having a polymerization degree of 1,000 was placed in a Henschel mixer. While the PVC was agitated for mixing at a rotation speed of 1,000 rpm in the Henschel mixer, a mixture was added thereto which had been prepared separately by adding 9.8 parts of PS-1 to 90 parts of PE-1 preliminalily heated to 70°C and agitating at a high speed for 1 minute. Further, thereto 4 parts of a Ba-Zn type PVC stabilizer was added, and agitation was conducted for one hour with keeping the inner temperature of the Henschel mixer at 80°C. Subsequently, the inner temperature was lowered below 40°C. 10 parts of a paste PVC resin (polymerization degree: 700) was added thereto, and agitated for 2 minutes to give a powdery product. This powdery product was classified with a 32-mesh sieve. After eliminating the granular matter on the sieve, the yield of the powder was 98 %. (2) The resulting powdery product was subjected to powder sinter molding with an embossing plate having a nickel surface with a copper back at 220°C for one minute to give a sheet of average thickness of 0.8 mm. Example 7 100 parts of a powdery PVC having a polymerization degree of 1,000 was placed in a Henschel mixer. While the PVC was agitated for mixing at a rotation speed of 1,000 rpm in the Henschel mixer, a mixture was added thereto which had been prepared separately by adding 20 parts of trioctyl trimellitate, 1 part of 1,4-butanediol, and 5 parts of PS-1 to 70 parts of PE-2 preliminarily heated to 70°C and agitating at a high speed for 1 minute. The succeeding procedure was effected in the same manner as in Example 6 to obtain a sheet of average thickness of 0.8 mm. Example 8 100 parts of a powdery PVC having a polymerization degree of 1,000 was placed in a Henschel mixer. While the PVC was agitated for mixing at a rotation speed of 1,000 rpm in the Henschel mixer, a mixture was added thereto which had been prepared separately by adding 20 parts of trioctyl trimellitate and 6.3 parts of PS-1 to 70 parts of PE-3 preliminarily heated to 70°C and agitating at a high speed for 1 minute. The succeeding procedure was effected in the same manner as in Example 6 to obtain a sheet of average thickness of 0.8 mm. Example 9 A sheet of average thickness of 0.8 mm was prepared in the same manner as in Example 8 except that PE-4 was used in place of PE-3 and 7.7 parts of PS-2 was used in place of 6.3 parts of PS-1. Example 10 A sheet of average thickness of 0.8 mm was prepared in the same manner as in Example 8 except that PE-5 was used in place of PE-3 and the amount of PS-1 was changed to 7.6 parts. Example 11 A sheet of average thickness of 0.8 mm was prepared in the same manner as in Example 8 except that PE-6 was used in place of PE-3 and the amount of PS-1 was changed to 3.3 parts. Comparative example 3 A sheet of average thickness of 0.8 mm was prepared in the same manner as in Example 8 except that 4.8 parts of hexamethylene diisocyanate was used in place of 6.3 parts of PS-1. Comparative example 4 A sheet of average thickness of 0.8 mm was prepared in the same manner as in Example 8 except that PS-3 was used in place of PS-1. Comparative example 5 100 parts of a powdery PVC having a polymerization degree of 1,000 was placed in a Henschel mixer. While the PVC was agitated for mixing at a rotation speed of 1,000 rpm in the Henschel mixer, 80 parts of trioctyl trimellitate and 4 parts of a Ba-Zn type PVC stabilizer was added thereto, and agitation was effected for one hour with keeping the inner temperature of the Henschel mixer at 100°C. Subsequently, the inner temperature was lowered below 40°C, 10 parts of a micro-suspension paste PVC resin (polymerization degree: 700) was added thereto, and agitated for 2 minutes to give a powdery product. The resulting powdery product was molded in the same manner as in Example 6 into a sheet of average thickness of 0.8 mm. [METHOD OF MEASUREMENT OF PROPERTIES] The results of measurement of the properties below are shown in Table 4. 1. Fusibility: In Examples 6 - 11 and Comparative examples 3 - 5, the molded article was cooled by water immediately after the powder sinter molding (220°C, one minute), and the state of fusion at the back side of the formed sheet (the opposite side to metal face) and the uniformity of thickness were visibly evaluated. The results are shown in three evaluation grades below: ○ : fused evenly with uniform thickness Δ : fused not completely × : fused not completely with significant non-uniformity of thickness 2. Mold releasability (2): In Examples 6 - 11 and Comparative examples 3 - 5, a pair of incisions were made in 2 cm breadth on the sheet which had been molded by powder sinter molding and water-cooled. The releasing force (g/cm) from the mold was measured at 180-degree turning-over. The results are shown in two evaluation grades below: ○ : less than 50 g/cm × : not less than 50 g/cm 3. Mold staining property: Powder sinter molding was repeated ten times with the same powder. The brightness of the 10th molded sheet was visibly evaluated at the surface in contact with the mold. The evaluated results are shown in two evaluation grades. ○ : same as the first molded sheet × : brighter than the first molded sheet 4. Adhesive property (2): An integrally molded flat plate was prepared by use of the sheet obtained in Examples 6 - 11 and Comparative example 3 - 5 and a polyurethane foam. The adhesion force (adhesive property) was measured according to a 180-degree peeling test. The results of the measurement are shown in the two evaluation grades below: ○ : not less than 300 g/cm × : less than 300 g/cm 5. Durability: The aforementioned integrally molded flat plate was kept in a Geer oven at 120°C for 500 hours. Then the elongation of the sheet at break was measured according to JIS K6723, and the value was represented by the retention ratio (%) in comparison with the initial value.

Claims: A non-tacky composite resin composition, comprising a polyvinyl chloride having a polymerization degree of not lower than 600 and a polyurethane containing in the molecule a group of the general formula (I) in which Me is a methyl group, n is an integer defined by 1 ≦ n ≦ 100, each of X and Y is an integer defined by 1 ≦ X ≦ 3, 0 ≦ Y ≦ 2, and X + Y = 3, and R is an alkylene group or alkylene groups which may be linked by one or more alkyleneoxy groups. A composition according to claim 1, wherein R is an alkylene group having 1 to 5 carbon which may be linked by one or two ethyleneoxy groups or propyleneoxy groups. A process for producing a non-tacky composite resin composition according to claim 1, the process comprising reacting diol-terminated polysiloxane of the general formula (II) in which Me, n, X, Y and R have the meanings specified in claim 1, with a polyol, an isocyanate and a polyvinyl chloride. A process for producing a non-tacky composite resin composition according to claim 1, the process comprising reacting a diol-terminated polysiloxane of the general formula (II) specified in claim 3 with a polyol and an isocyanate to prepare a polyurethane having a group of the general formula (I) in the molecule, and subsequently blending the resulting polyurethane with a polyvinyl chloride. A process according to claim 4, wherein the polyurethane is prepared by reacting an isocyanate with the diol-terminated polysiloxane and subsequently reacting the resulting product with a polyol. A process for preparing a non-tacky composite resin composition according to claim 1, the process comprising preparing the polyurethane by reacting together (A) a diisocyanate, (B) a polyester-polyol derived by reacting a dicarboxylic acid with a diol containing 3-methyl-1,5-pentanediol and/or 2-methyl-1,8-octanediol in an amount of at least 30 mol % and one or more other short-chain diols in an amount of not more than 70 mol % and (C) a diol-terminated polysiloxane of the general formula (II) specified in Claim 3, and blending the resulting polyurethane with a polyvinyl chloride.

Inventors: KIJIMA TETSUO, TANAKA TOSHIHIKO, TSUNODA SHOHEI, YANO NORIYOSHI, KIJIMA, TETSUO, TANAKA, TOSHIHIKO, TSUNODA, SHOHEI, YANO, NORIYOSHI
Applicants: NIPPON POLYURETHANE KOGYO KK, TOSOH CORP, NIPPON POLYURETHANE INDUSTRY CO. LTD., TOSOH CORPORATION
Application year: 1990
Main classification: C08L27
IPC codes: C08L75, C08G18, C08L27