METHOD FOR THE HETEROGENEOUS CATALYTIC PHOTODEGRADATION OF POLLUTANTS

Abstract: A method for purifying water containing pollutant mixtures is described, which uses a reactor containing a semiconductor as reaction catalyst and a lamp which emits radiation having a wavelength of less than 400 nm The reactor, characterised in that its walls allow water and the pollutant substances to pass through, is immersed in the water to be purified so that the pollutants contained in it reach the reactor interior where they are adsorbed on the semiconductor activated by light radiation, and are then degraded.

Description: This invention relates to a method for purifying water containing pollutant mixtures consisting of immersing into said water a reactor containing a semiconductor in aqueous dispersion and a lamp which emits radiation having a wavelength less than 400 nm, characterised in that the reactor walls are a semipermeable membrane and allow water and the pollutant substances to pass through. The pores of the membrane are of such dimensions as to prevent the escape of catalyst while allowing water and pollutant substances to flow through. As the pollutants reach the reactor interior they are initially adsorbed on the catalyst activated by the light radiation and are then degraded. Semiconductors are materials having a particular electronic configuration, namely that the valence band at the lower energy level is completely occupied by electrons, whereas the conduction band at the higher level is almost completely empty. By irradiation with light of a suitable wavelength the electrons acquire sufficient energy to transfer to the conduction level. In this manner charges are separated and migrate to the surface of the semiconductor where they are are able to induce oxidation-reduction reactions. This behaviour, which is typical of semiconductors, has found its most important application in water purification, in which it is used to obtain heterogeneous catalytic photodegradation of micropollutants. In particular, a very wide range of highly toxic compounds can be completely mineralized, ie degraded to CO₂ and water, by heterogeneous photocatalysis. Various types of photochemical reactors have been used to implement this purification method. The most widespread is the immersion type and consists substantially of a conventional chemical reactor into which a suitable lamp is inserted through the cover and immersed into the reaction mixture, which also contains the catalyst particles in suspension. These particles form suspensions or colloidal solutions from which they have to be recovered on termination of the degradation process in order to be recycled and to leave the water as pure as possible. This removal is achieved by decantation or centrifuging, but the water obtained in this manner still contain up to 1 mg/l of catalyst and although being dischargeable is above the allowable limit for drinking water. It has been sought to solve this problem by using supported catalysts, for example on glass. However this type of catalyst has a very much smaller surface area than the preceding, and moreover because of its low mechanical strength tends to crumble and release a part of the powder, which as in the aforegoing case must be separated. EP-A 401884 describes a method for the photocatalytic treatment of aqueous pollutant mixtures which as catalyst uses titanium dioxide in the form of microbeads, which are kept under agitation within the reactor by the reactant mixture flow, but without being removed. As the catalyst remains confined to the reactor interior the water purification and catalyst recovery steps are no longer required on termination of the photocatalytic treatment. In addition these microbeads have high mechanical strength and do not release TiO₂ powder, in spite of the stresses to which they are subjected during the process. The complexity of the synthesis method however makes them more costly than the corresponding powder-form catalyst. We have now found a method for purifying water containing pollutant mixtures which consists of immersing into said water a reactor containing a semiconductor in aqueous dispersion and a lamp which emits radiation having a wavelength less than 400 nm, characterised in that the reactor walls consist of a semipermeable membrane and allow water and the pollutant substances to pass through. In this manner a space is defined about the lamp to hold the photodegradation catalyst, the pollutants pass through these walls to reach the catalyst, on which they are adsorbed and then degraded. Because of the manageability and easy transportability of the reactor and the fact that the catalyst is contained in an enclosed space, this method can be used to purify polluted water directly in the natural basin which contains it, so avoiding the high cost involved in withdrawing large volumes of polluted mixture and transporting it to a photodegradation plant. The use of a reactor formed from a semipermeable membrane allows a catalyst in the form of a powder-form semiconductor in colloidal dispersion to be used. The process therefore becomes particularly economical and convenient, and without encountering the separation problems of the known photodegradation methods of the prior art. The lamps used in the process of the present invention emit radiation having a wavelength of less than 400 nm and preferably between 320 and 380 nm, and can for example be high or low pressure mercury vapour or xenon lamps. The distance between the reactor wall exceeds 0.5 cm and is preferably between 0.5 and 5.0 cm. The semipermeable membranes used to form the reactor walls are characterised by a cut-off of between 1000 and 50,000 u.m.a. These membranes consist for example of modified cellulose or synthetic polymers. Semiconductors which can be used as catalysts include titanium dioxide and zinc oxide. These catalysts are dispersed in water and can be in the form of powder or microbeads, or be suitably supported. Semiconductors in powder form which can be used are in the form of particles of size between 1 and 100 µm, in a concentration of between 0.5 and 50 g/l. Such particles are unable to pass through the membrane pores or to obstruct them. Semiconductor in the form of microbeads, can be prepared, for example, in accordance with U.K. Patent No. 2.112.764. These microbeads can also be used for membrane reactors. Air or oxygen can be blown into the reactor during the process. EXAMPLE 1 50 ml of an aqueous solution containing 104 ppm of o-nitrophenol at pH 6 are placed in a 100 ml cylinder. A reactor formed from a membrane of length 18 cm and diameter 2.1 cm and having a cut-off of 15,000 u.m.a. is immersed in this solution, the reactor containing a colloidal dispersion comprising 4 g/l of powdered TiO₂ and a 40 W low pressure mercury vapour lamp. Air is blown into the membrane interior. After 30 minutes in the dark the o-nitrophenol concentration within the membrane is 52 ppm. After 2 hours of irradiation the pollutant concentration both within and outside the membrane has fallen to 8 ppm. EXAMPLE 2 The procedure of the preceding example was followed, but the catalyst concentration was reduced to 1 g/l. After 30 minutes in the dark the o-nitrophenol concentration within the membrane is 46 ppm. After 1 hour of irradiation the pollutant concentration has fallen to 18 ppm. EXAMPLE 3 600 ml of an aqueous solution containing 52 mg/l of o-nitrophenol were processed under the conditions of the preceding example. The concentration of the catalyst within the membrane is 50 g/l. The following table shows the results obtained: EXAMPLE 4 As Example 2 but with a catalyst concentration of 0.6 g/l within the membrane. After 30 minutes in the dark the o-nitrophenol concentration within the reactor is 50 ppm. After 1 hour the concentration has fallen to 42 ppm and after 3 hours to 32 ppm. EXAMPLE 5 500 ml of an aqueous mixture deriving from a chemical industry effluent were processed under the conditions of the preceding example. The following table shows the results obtained: where COD = chemical oxygen demand, ie mg/l of O₂ required to oxidize the organic material contained in the reaction mixture. EXAMPLE 6 500 ml of an aqueous mixture of pollutants is processed under the conditions of the preceding example. 1.2 g/l of TiO₂ in colloidal dispersion are contained within the membrane. The following table shows the results obtained:

Claims: A method for purifying water containing pollutant mixtures, consisting of immersing into said water a reactor containing a semiconductor in aqueous dispersion and a lamp which emits radiation having a wavelength less than 400 nm, characterised in that the reactor walls are a semipermeable membrane which allows water and the pollutant substances to pass through. A method as claimed in claim 1, wherein the lamp used emits at least a fraction of radiation at a wavelength of between 380 and 320 nm. A method as claimed in claim 1, wherein the lamp is a high pressure mercury vapour or xenon arc lamp or a low pressure mercury vapour or xenon arc lamp. A method as claimed in claim 1, wherein the semiconductor is chosen from titanium dioxide and zinc oxide. A method as claimed in claim 1, wherein the distance between the lamp and the reactor wall exceeds 0.5 cm. A method as claimed in claim 1, wherein the membrane is characterised by a cut-off of between 1000 and 50,000 u.m.a. A method as claimed in claim 1, wherein the membrane is of modified cellulose or synthetic polymers. A method as claimed in claim 1, wherein the semiconductor is dispersed in water, and is in the form of powder or microbeads, or is supported. A method as claimed in claim 5, wherein the distance between the lamp and the reactor wall is between 0.5 and 5 cm. An apparatus for purifying water containing pollutant mixtures in accordance with claim 1, consisting of a reactor containing a semiconductor in aqueous dispersion and a lamp which emits radiation of less than 400 nm wavelength, characterised in that its walls are a semipermeable membrane.

Inventors: BORGARELLO, ENRICO, MIANO, FAUSTO
Applicants: ENIRICERCHE S.P.A.
Application year: 1990
Main classification: C02F1
IPC codes: C02F1