Biaxially-oriented polyester film having a dual-sided appearance

Abstract: A biaxially-oriented polymer film having dual-sided appearance, i.e., the color of each side is chromatically different. Also a method for making such films.

Description: Field of Invention This invention concerns a biaxially-oriented polyester film having a dual-sided appearance, i.e., different colored appearance. Background Biaxially-oriented polyester films, e.g., polyethylene terephthalate, are well-known for high dimensional stability, moisture resistance, tear resistance, and low cost, and have achieved substantial commercial utility. Such films are commonly used in electrical insulation, as a backing for pressure-sensitive adhesive tapes, magnetic recording tapes, or abrasives, and in many other products. For instance, U.S. Patent No. 4,413,298 (Pecsok et al.) discloses a jacket for magnetic recording diskettes which is made from biaxially-oriented polyester film containing particles of a different polymer, providing a matte finish that aesthetically masks scratches and smudges. The reference discloses incorporation of a pigment, e.g., carbon black, in the polyester to impart desired opacity to the film. U.S. Patent No. 3,579,609 (Sevenich), discloses that blending minor amounts of fusible heat-stable polymers of a lower-mono-alpha olefin (e.g., polyethylene, polypropylene, polybutylene) or tetramethylene oxide into polyester resin which is extruded into a film and thereafter oriented, imparts improved flex resistance to the resultant film. U.S. Patent No. 3,640,944 (Seppala et al.) discloses tape comprising a blend of 1) a major portion of polyethylene terephthalate polymer, 2) from about 1 to 30 percent by weight of a thermoplastic, high temperature, opacifying additive polymer, e.g., polysulfone and poly(4-methyl, 1-pentene), dispersed throughout the tape in discrete microscopic particles, and 3) an effective amount of a light absorbing material. None of these references teaches that the films taught therein exhibit substantial side-to-side variation in color appearance. Summary of Invention This invention provides a novel polyester film material which is well-suited for use in magnetic recording diskette jackets or other specialized packaging needs, and there is also disclosed a method for producing such a film. One side of the polyester film material provided herein has a matte finish and thus tends to hide and minimize the effect of smudges or scratches that may be formed thereon when the film is handled, thereby maintaining an aesthetically pleasing appearance. Of special advantage is the "dual-sided appearance" of the material. "Dual-sided appearance" is used herein to refer to the unexpected property wherein opposing sides of polyester films of the invention are of different colors, i.e., the first or matte side of the film is silver to gray in color whereas the second side of the film is dark gray in color. The descriptions of the colors, i.e., relative intensity or shades of white and black, of the two sides may be expressed objectively in terms of the Hunter Laboratory Color Scale which represents the mathematical approximation of the non-linear black-white response of the human eye. In that color measuring system, color is expressed numerically with three factors, L, a L , and b L , wherein L represents intensity of color on a scale of black (-L) to white (+L) , a L represents color on a scale of green (-a L ) to red (+a L ), and b L represents color on a scale of blue (-b L ) ) to yellow (+b L ). Polyester film materials of the present invention exhibit an intensity difference or Delta L of at least 5, typically at least 10, and in some instances more than 15. With the unaided eye, a typical human observer can detect color differences equivalent to a Delta E or a Delta L of about 1.0 or more. The dual-sided appearance of such films may be used to assist in desired orientation of the film, such as during preparation, e.g., surface priming, or conversion, e.g., cutting, or when a product incorporating same is used by a consumer, or may be of special aesthetic utility in some applications, such as product packaging. Briefly summarizing, the novel film of the invention is a biaxially-oriented monolayer film of polyester polymer containing discrete, substantially uniformly distributed polymeric particles which have an average diameter of between 5 and 100 micrometers and which comprise between 5 and 30 percent by volume of the film, and also containing an amount of carbon black pigment sufficient to achieve desired opacity. The polymeric particles are distributed as a discontinuous phase throughout the continuous phase of polyester polymer. Carbon black may be compounded within either the polyester phase, the discrete particle phase, or in both phases. A first side of the film has a matte finish and Hunter Laboratory Color on the L Scale of between 52 and 67, and the other side of the film has smooth finish Hunter Laboratory Color on the L Scale of between 38 and 53. The difference in Hunter Laboratory Color L Scale value between opposing sides of films of the invention, referred to herein as Delta L, is at least 5, typically at least 10, and in some instances more than 15. In brief summary, the method for forming such monolayer polyester films comprises: (A) preparing particle-forming stock from particle-forming polymer, optionally compounding said particle-forming polymer with carbon black; (B) preparing polyester stock from polyester polymer, optionally compounding said polyester polymer with carbon black; (C) mixing thoroughly said particle-forming stock with an excess of said polyester stock to form a casting composition; (D) casting said casting composition to form a polyester film; (E) lengthwise orienting said polyester film; and (F) tentering said polyester film; wherein at least one of said particle-forming polymer or said polyester polymer is compounded with carbon black, said polyester film containing discrete, substantially uniformly-distributed particles of particle forming polymer having an average diameter of 5 to 100 micrometers and comprising about 5 to about 30 percent by volume of the polyester film; said film comprising between 0.2 to 4.0 weight percent of carbon black pigment; and characterized in that (1) said casting is casting said casting composition in molten form onto a cooled casting wheel, said casting wheel being cooled to a temperature below the glass transition temperature of polyester, so as to quench cast said casting composition and (2) a first side of said film has a matte finish and a Hunter Colorimetric Color L Factor of between 52 and 67; and a second side of said film has a Hunter Colorimetric Color L Factor of between 38 and 53, the Delta L between said first side and said second side being at least 5. Detailed Description of the Invention As described above, there is disclosed a method which may be briefly summarized as follows: (A) preparing particle-forming stock from particle-forming polymer, e.g., polypropylene, optionally compounding the particle-forming polymer with carbon black; (B) preparing polyester stock from polyester polymer, optionally compounding the polyester polymer with carbon black; (C) mixing thoroughly the particle-forming stock with an excess of the polyester stock to form a casting composition; (D) quench casting the casting composition to form a film; (E) lengthwise orienting the film; and (F) tentering the film; wherein at least one of the particle-forming polymer and polyester polymer is compounded with carbon black, to yield the novel biaxially-oriented monolayer polyester film of the invention. The composition of polyester films of the present invention is typically as follows: Component Weight Percent Polyester 60 to 96 Polyolefin 3.0 to 40 Carbon Black 0.2 to 4.0 The first steps of the process comprise: (A) preparing particle-forming stock from particle-forming polymer, such preparation optionally including compounding the particle-forming polymer with carbon black; and (B) preparing polyester stock from polyester polymer, such preparation optionally including compounding the polyester polymer with carbon black. "Particle-forming polymer" is defined herein as a polymer which, when mixed in an excess of polyester, will form discrete particles or assume a discontinuous phase within a continuous phase of the polyester. At least one of the particle-forming polymer and polyester polymer is compounded with carbon black. Preparation of the particle-forming polymer stock may include, as necessary, such techniques as milling to improve material handling properties and control the particle size thereof, adjusting, e.g., raising, the temperature of the material to improve its handling and subsequent mixing and extrusion properties, and optional drying to improve handling properties of the final product. Preparation of the polyester stock may include similar processes. At least one of the particle-forming polymer and polyester polymer is compounded with carbon black. Carbon black is typically compounded by milling under conditions which are determined, at least in part, by the nature of the particle-forming polymer or polyester polymer and carbon black being compounded therewith. Typically, better mixing is achieved by using a carbon black in a carrier that is compatible, i.e., miscible, in the particle-forming polymer or polyester, respectively, in which the carbon black is being compounded. Typical ratios are between 0.5 and 1.5 parts by weight of carbon black per 9 to 10 parts by weight of particle-forming polymer, or in separately compounded polyester polymer, between 0.75 and 1.5 parts by weight of carbon black per 85 to 100 parts of polyester. The amount of carbon black in a film of the invention is between 0.2 and 4.0 weight percent of the total composition. Preferred as the particle-forming polymer are polyolefins such as polypropylene and polyethylene which are readily available at reasonably low cost with melt flow rates in the desired range. Polysulfones, poly(2-methyl-1-pentene), and polycarbonates should also be useful, but typically tend to more expensive. Selection of the particle-forming polymer is made in consideration with selection of the polyester polymer such that, in the amounts provided for by the invention, the particle-forming polymer will form voids in the polyester phase. Such voiding is believed to be the result of the difference in melt viscosity at extrusion temperature between the particle-forming polymer and polyester phases. Films of the invention generally comprise between 3 and 40 weight percent of particle-forming polymer. Those films of the invention which contain lesser amounts of particle-forming polymer typically tend to exhibit a lesser degree of the dual-sided appearance provided herein, whereas those films of the invention which contain greater amounts of particle-forming polymer may tend to be somewhat weaker than films containing lesser amounts of such components. The melt flow rate of the particle-forming polymer, as measured according to ASTM D1238L, is preferably less than about 2.0 decigrams/minute, and more preferably less than about 1.0 decigram/minute, thereby tending to ensure that the particle-forming polymer will be in the form of discrete polymeric particles averaging at least about 5 micrometers in diameter, even after the particle-forming polymer stock and polyester stock have been vigorously mixed together. If the melt flow rate of the particle-forming polymer exceeds about 1.0 decigram/minute, it may be desirable to mix the particle-forming polymer stock and polyester stock less vigorously, especially if the intrinsic viscosity of the polyester polymer is toward the high end of the 0.4 to 1.0 range discussed below. However, vigorous mixing is usually desirable to ensure substantially uniform dispersal of carbon black throughout the film, thereby achieving adequate and substantially uniform opacity of the resultant polyester film. Although more vigorous mixing tends to reduce the particle size, the average particle size of the particle-forming polymer is likely to remain above 25 micrometers if the intrinsic viscosity of the polyester is between 0.55 and 0.65, and the melt flow rate of the particle-forming polymer is within the preferred range of 0.4 to 0.8 decigram/minute. An average particle size of more than 5 micrometers will typically provide a resultant film wherein the first side thereof has a matte finish that will effectively hide scratches and smudges if the particle-forming polymer comprises at least 10 percent by volume (about 6.7 percent by weight) of the polyester film. An average particle size of more than 25 micrometers will typically provide a resultant film wherein the first side thereof has an effective matte finish if the particle-forming polymer comprises at least 5 percent by volume (about 3.3 percent by weight) of the film. The major component by amount of the resultant film is polyester, e.g., polyethylene terephthalate. The intrinsic viscosity of the polyester may be in the range of 0.4 to 1.0. If the intrinsic viscosity is above 0.8, the polyester polymer may tend to be difficult to extrude and both compounding of the polyester polymer with carbon black and mixing with the particle-forming polymer may be difficult as well. If the intrinsic viscosity is below 0.4, the resultant film may tend to be brittle and to crack when folded. Polyethylene terephthalate is a preferred polyester polymer because it provides excellent thermal stability, and high strength and toughness, and is readily available at reasonable cost within a preferred intrinsic viscosity range of 0.55 to about 0.65. The film of the invention will generally comprise from 60 to 96 weight percent of polyester polymer. After preparation, the particle-forming stock and polyester stock are melted and thoroughly mixed together to yield the casting composition. Such mixing may be performed by such means as an extruder or other conventional techniques. Mixing is preferably done at a sufficiently high temperature to ensure that the polymeric components of the mixture remain in molten state. The mixture will typically be mixed at a temperature on the order of 260°C to 285°C, although this will depend in part upon the properties and composition of the particular mixture being prepared. The casting composition is then preferably filtered, e.g., by passing through a Tegra Tube Bundle Filter having sintered metal tubes, to remove from the composition or preferably break up substantially all the agglomerates or domain nodules of particle-forming polymer which are over 60 microns in diameter. Large agglomerates or nodules of particle-forming polymers may tend to cause the extruded film to break or develop holes therein when the film is subsequently stretched during lengthwise orientation and tentering. Filtration also is believed to cause further localized mixing of the casting composition before extrusion. After mixing and optional filtration, the molten casting composition is extruded through a die and cast upon a cooled casting wheel. The casting wheel should be cooled, preferably to a steady state, e.g., by internal cooling means such as circulated cooling water at a temperature of 45°C to 55°C to cool the cast composition to below the glass transition temperature of the polyester which is the major component of the composition, i.e., typically between about 70°C and about 80°C. The casting composition will typically have a temperature of at least 285°C up to 300°C at the time of extrusion and casting upon the cooled casting wheel. This process is referred to herein as quench casting and is believed to be a critical element in production of novel films of the invention which exhibit the aforementioned dual-sided appearance. The side against the casting wheel, which is believed to be a substantially noncrystalline or amorphous region, is relatively darker, e.g., dark gray or black, and tends to be very smooth, and the opposing side, which is believed to have a more crystalline structure, is relatively lighter in color, e.g., silver-gray, and has a more textured surface, i.e., a matte finish, than the casting wheel side. The desired thickness of the cast film will depend in part upon the desired use for which the resultant film is being prepared, and may be achieved by control of the process conditions under which the film is formed. Films of the invention will typically have a cast thickness of 75 to 90 mils, i.e., about 2 millimeters, however, depending upon the characteristics desired of the resultant film, films of the invention may be cast at thicknesses outside this range. The casting wheel should be very smooth, preferably having a mirror finish. Furthermore, the surface of the casting wheel should be a durable material that preferably permits good heat transfer and that will not tend to adhere to the casting composition and the film being formed therefrom. Polished chrome is an example of suitable casting wheel surface material. After quenching, the film is lengthwise oriented, i.e., in the machine direction (hereinafter "MD"), by stretching it to typically between 2.5 and 4.0 times its original length, typically preferably to at least 3.5 times its original length, and passed through a tenter where it is stretched in the transverse direction, i.e., cross-machine direction (hereinafter "TD"), to typically between 3.0 and 4.0 times its original width. If the film is not stretched sufficiently in one of these dimensions, it may tend to have a striped appearance with stripes running perpendicularly to the direction in which the film was insufficiently stretched. The film is typically heated, e.g., by infrared lamps, to raise its temperature to slightly above its glass transition temperature during lengthwise orientation and tentering. The final thickness of the resultant film of the invention will be determined in part by the casting thickness, degree of lengthwise stretching, and degree of tentering. For many uses, the thickness will typically be between 60 and 80 mils (1.5 and 2.0 millimeters). The prepared film is then typically wound upon itself in roll form before final processing to convert it into desired form, e.g., diskette jacket or backing film. Examples The invention will now be further explained by the following illustrative examples. Unless otherwise indicated, all amounts are expressed in parts by weight. Hunter Colormetric Measurement The color of the films prepared in each Example were determined with a SPECTROGARD 96 Colorimeter from Pacific Scientific Company in accordance with ASTM D2244-79. Delta E represents the magnitude of color difference between the two sides of the film with regard to the L, a L , and b L color components. Delta L represents the magnitude of color difference with regard to the L color component. Method of Manufacture Except as otherwise indicated below, the samples made in the following examples were made according to the following procedure. Polyethylene terephthalate, and carbon black in a polyethylene terephthalate carrier (i.e., "PET") were metered through an acrison in indicated amount, and fed into a 11.4 cm (4.5") extruder to form polyester stock. Particle-forming polymer, i.e. polypropylene, and carbon black in a polypropylene carrier (i.e "PP") were metered through an acrision in indicated amount, fed through a 6.35 cm (2.5") extruder to form particle-forming stock, and then fed into a port of the 11.4 cm (4.5") extruder. After passing through and being mixed by the extruder, the casting composition was passed through a Tegra tube bundle filter of sintered metal tubes with 60 µm (micron) openings. The casting composition was then passed through a 25 centimeter (10 inch) wide casting die, at a temperature of about 260°C (500°F) onto a water-cooled chill roll or casting wheel using air impingement to aid in quenching the cast film. The cast film was then stretched in the machine direction to the extent indicated under infrared heater banks. Following MD orientation, the film was stretched in a tenter oven in the transverse direction to the indicated stretch ratio. The film was then heatset in the tenter oven. Following the MD and TD orientation, the film was wound upon a spool into roll form for storage. Example 1 Example 1 illustrates one embodiment of the invention containing different amounts of particle-forming polymer and different MD and TD stretch ratios. Composition of Film (parts) Example 1 Polyester 88.6 Polypropylene 10.0 Carbon Black (in PET) 0.23 Carbon Black (in PP) 0.23 MD Stretch Ratio 3.5:1 TD Stretch Ratio 4.0:1 caliper µm (mils) 190 (7.5) Characterization of Films (Hunter Colormetric) Example 1 L - First Side 61.4 Second Side 43.6 Delta L 17.8 Examples 2-11 Examples 2-11 illustrate several other embodiments of the invention. The compositions and color characterization of the films in each Example are shown in Table III. In Examples 2-10 the MD Stretch Ratio was 3.5, the TD Stretch Ratio was 4.0, and the Caliper was 190 µm (7.5 mils). In Example 11, the values were 2.5, 3.5 and 190 µm (7.5) respectively. The dual-sided appearance of the resultant films is illustrated by the results tabulated in Table III. The Delta E and Delta L in each Example were substantially equivalent, illustrating that the dual-sided appearance of films of the invention is essentially a variation in color on the black-to-white color axis. Comparative Example A A sample of the film material disclosed in U.S. Patent No. 3,640,944 (Seppala et al.) had a Delta L of about 0.9.

Claims: A biaxially-oriented monolayer film of polyester containing discrete, substantially uniformly-distributed polymeric particles having an average diameter of 5 to 100 micrometers and comprising 5 to 30 percent by volume of the polyester film to provide a matte finish, and comprising between 0.2 and 4.0 weight percent of carbon black pigment, characterized in that a first side of the film has a matte finish and a Hunter Colorimetric Color L Factor of between 52 and 67, and a second side of said film has a Hunter Colorimetric Color L Factor of between 38 and 53, the Delta L between said first side and said second side being at least 5. The polyester film of claim 1 further characterized in at least one of the following: (A) the Delta L between said first side and said second side is at least 10; or (B) the Delta L between said first side and said second side is at least 15. The polyester film of claim 1 further characterized in that the thickness of said film is between 1.5 and 2 millimetres. The polyester film of any preceding claims further characterized in that said polymeric particles comprise polyolefin having a melt flow rate of less than 2.0 decigrams/minute. The polyester film of claim 4 further characterized in that said polyolefin comprises at least one of polypropylene or polyethylene having a melt flow rate between 0.4 and 0.8 decigram/minute. The polyester film of any one preceding claim further characterized in at least one of the following: (A) said polymeric particles comprise at least one of the following: polypropylene, polyethylene, polysulfone, poly(2-methyl-1-pentene), or polycarbonate; or (B) said film comprises between 3 and 40 weight percent of said polymeric particles; or (C) said film comprises between 60 and 96 weight percent of said polyester.

Inventors: RENALLS BRENDA L, RENALLS, BRENDA L., RENALLS, BRENDA L. C/O MINNESOTA MINING AND
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1990
Main classification: C08J5
IPC codes: C08L81, C08L67, B29C41, C08J5, C08J3, B29C55, C08K3, B29K67, B29C69, C08L69, C08L23