NEW ULTRA LOW THERMAL EXPANSION, HIGHLY THERMAL SHOCK RESISTANT CERAMIC

Abstract: Three families of ceramic compositions having the given formula (I): PHI 1+XZr4P6-2XSi2XO24, PHI 1+XZr4-2XY2XP6O24 and PHI 1+XZr4-XYXP6-2XSiXO24, wherein PHI is either strontium or barium and X has a value from about 0.2 to about 0.8 have been disclosed. Ceramics formed from these compositions exhibit very low, generally near neutral, thermal expansion over a wide range of elevated temperatures.

Description: -ι- NE ULTRA LOW THERMAL EXPANSION, HIGHLY THERMAL SHOCK RESISTANT CERAMIC Government Rights Contract Section: This invention was made with Government support under contract no. DE-AC05-87ER80502, awarded by the Department of Energy. The Government has certain rights in this invention. Field: This invention relates in general to ultra low thermal expansion materials that exhibit very high thermal shock resistance. These materials can be used for a variety of low temperature as well as high temperature applications, where a material is subjected to sudden temperature changes and is also expected to have dimensional stability. The examples of such applications include, catalytic substrates, optical devices such as ring laser gyro, exhaust port liners for internal combustion engines, etc. BACKGROUND OF THE INVENTION Almost every material has a substantial, positive coefficient of thermal expansion, i.e. it expands significantly when heated. Since World War II, the importance of low expansion ceramics has been realized and extensive research has been conducted to develop materials that exhibit low thermal expansion. Some of the well know materials include vitreous silica, lithium alumino-silicates (LiAlSi0 4 , LiAlSi 2 Og) , and cordierite . Vitreous silica is used in a variety of low temperature applications such as various optical systems. Lithium alumino-silicates (LAS) are used as a major constituent of cooking ware; and cordierite as the main component of catalytic substrate bodies. However most of these materials have temperature limitations, i.e. they cannot be used at very high temperatures. Components of catalytic converters used in automobiles as well as industrial emission control -2- systems are subjected to very large temperature variations. These components are therefore made out of low thermal expansion and highly thermal shock resistant ceramic materials. Current state of the art materials 5 include alt&iinum titanate, and cordierite. However, aluminum titanate possesses a structural instability (decomposition into rutile and corundum) below 1300° _> Centigrade (C) , destroying the pseudobrookite structure and resulting in a loss of low thermal expansion 10 behavior. Cordierite, due to its relatively low melting temperature, cannot be used above 1200°C. Some of the components of earth orbiting satellites are also subject to temperature fluctuations. If these components are made out of materials having a 15 large thermal expansion, then sudden temperature changes can cause the component to distort or fracture under tltermal stresses. This problem is of a great concern in optical systems used in space that cannot function satisfactorily under frequently changing dimensions of 20 the component. Ceramics of the type Naι +x Zr 2 P3_χSi x 0 12 (also known as NASICON) and NaZr 2 P 3 0 12 (or NZP) have been studied for their ionic conductivity. Sljukic, et al. were the first to synthesize NZP-type materials 25 ' ("Preparation and Crystallographic Data of Phosphates with Common Formula M I M IV (P0 4 ) 3 ; M 1 = Li, Na, K, Rb, Csr M^ - Zr, Hf; Croatia Che ica Acta. 39, pp. 145-148, 1967) by heating a mixture of alkali metal phosphates and tetravalent metal oxides. The crystal structure of 30 NZP type materials consists of a three-dimensional hexagonal skeleton network of P0 tetrahedra connected with ZrOg octahedra by corner linking. Each P0 4 tetrahedron is connected to four Zr0 6 octahedra and each Zr06 octahedron is connected with six P0 4 35 tetrahedra. The basic unit of the network consists of two octahedra and three tetrahedra corresponding to (Zr 2 P 3 θι 2 ) . These units in turn are so connected as to form ribbons along the c-axis, that are joined together (perpendicular to the c-axis) by P0 4 tetrahedra to develop a three dimensional rigid network. The articulation of these ribbons and chains is believed to create structural holes or interstitial vacant sites in the structure which are normally occupied by sodium and/or other substituting ions. There are four such interstitial sites per formula unit of which some are empty depending upon the particular substitution. The most important and extraordinary feature of the NZP structure is its exceptional flexibility towards ionic substitution at various sites. This feature is extremely important for manipulating the thermal expansion behavior of NZP type materials. J.P. Boilot and J.P. Salantie, as reported in "Phase Transformation in Na 1+x Zr 2 P 3 _ x Si χ 0 12 Compounds", Materials Research Bulletin Vol. 14, pp.1469-1477, 1979, found that the thermal expansion of various compositions in Na 1+x Zr 2 P 3 _ x Si x 0 12 varied from strongly positive to near zero to even negative values. Based on these results J. Almo and R. Roy further investigated the NZP type materials and showed that NZP type materials indeed show low thermal expansion and have extraordinary flexibility towards ionic substitutions ("Ultralow Expansion Ceramics in the System Na 2 0-Zrθ 2 - 2 θ5-Siθ2, π Journal of American Ceramic Society. Vol 67 No.5 pp. C-78 - C-79 1984; "Crystal Chemistry of the NaZr 2 (P0 ) 3 , NZP or CTP Structure Family," Journal of Materials Science, vol. 21 pp.444-450 1986). Later investigations on NZP type materials were performed by D.K. Agrawal and V.S. Stubican ("Synthesis and Sintering of Cao.sZr 2 P 3 0 12 - A Low Thermal Expansion Material," Materials Research Bulletin, vol. 20 No.2 pp. 99-106, 1985) reporting the sintering characteristics of CaZr 4 (P0 4 ) 6 . T. Oota and I. Yamai in a publication entitled "Thermal Expansion Behavior of NaZr 2 (P0 4 ) 3 - Type Compounds," Journal of the American Ceramic Society, vol 69 No.l pp. 1-6 (1986) suggested that if larger ions such as K + or Sr 2+ are substituted at the sodium site, then the c-axis will be stretched. The P0 4 tetrahedra that cross link the chains along the c-axis are strained upon stretching of the c-axis. Hence, during heating, further expansion along the c-axis is suppressed, and the expansion along the a-axis is enhanced. They also concluded that in NZP type materials, the skeletal framework thermal expansion is almost zero, and that the total expansion was mainly determined by the ionic substitution at different crystallographic sites. Recently S.Y. Limaye, D.K. Agrawal and H.A. McKinstry < •("Synthesis and Thermal Expansion of MZr 4 P 6 0 24 (M=Mg, Ca, Sr, Ba)," Journal of the American Ceramic Society Vol. 70 No. 10 pp. C-232 -C-236 1987) conducted a systematic survey of NZP type materials with alkaline earth ions substituted at the sodium site. They found that MgZr 4 Pg0 4 did not result in a structure similar to NZP, that CaZr 4 P 6 0 24 had positive thermal expansion along the c-axis and negative thermal expansion along a-ax±s, and that SrZr 4 Pg0 24 and BaZr 4 P 6 0 24 showed exactly opposite thermal expansion anisotropy This work was further extended by making a solid solution of CaZr 4 PgQ and SrZr 4 Pg0 4 which showed reduced thermal expansion anisotropy and also reduced bulk thermal expansion- However, most of the earlier research has been concentrated on making ionic substitutions at sodium and zirconium sites. Earlier research did not address the following issues: the thermal expansion anisotropy (except for the solid solution of CaZr P 6 o 24 and SrZr Pgθ 2 ) , effect of the thermal expansion anisotropy on various properties (including Young's modulus, strength etc.) characterization of the thermal expansion up to higher (e.g. 1200°C) temperatures, evaluation of cyclic thermal expansion, strength and thermal shock resistance, efforts to improve the strength and thermal shock resistance.and non-linear thermal expansion, i.e. large variation in thermal expansion with respect to temperature. Furthermore, most of these materials have relatively higher thermal expansion than fused quartz up to 500°C. SUMMARY OF THE INVENTION The invention includes a new ceramic compositions which exhibit very low bulk thermal expansion (less than fused quartz) and which have superior strength and thermal shock resistance. Silicon is partially substituted for phosphorous in and the deficient charge is compensated for by adding excess cations at the sodium site or partially substituting yttrium for zirconium and compensating the deficient charge by adding excess cations at sodium site instead of just substituting larger cations at the sodium site. Similar results are achieved by simultaneously substituting the yttrium and silicon for both the zirconium and the phosphorous sites respectively and compensating the deficient charge by adding excess cations at sodium site. The chemical formulae for such ceramic compositions can be written as: φ 1+x Zr 4 P 6 -2χSi 2 χ0 wherein φ is either Sr (strontium) or Ba (barium) and X has values ranging from about 0.3 to 0.8. Hafnium may be partially or fully substituted for zirconium. Φl+X Zr 4-2X γ 2X p 6°24 wherein φ is either Sr (strontium) or Ba (barium) and X has values ranging from about 0.2 to 0.6. Hafnium may be partially or fully substituted for zirconium. Φ l +χ Zr 4-x γ x p 6-X s iχ°24 wherein 0 is either Sr (strontium) or Ba (barium) and X has values ranging from about 0.3 to 0.7. Hafnium may be partially or fully substituted for zirconium. The present invention is to provide novel structural ceramic components having extremely high dimensional stability, high strength and high thermal shock resistance over a wide range of temperature which can be used for a variety of applications including, but not limited to, catalytic convertors, emission control - 6 - devices, space optics, exhaust port liners for diesel engines and similar applications. The present invention further provides an improved process for producing materials that have ultra 5 low thermal expansion and high strength as well as high thermal shock resistance. Ceramic materials of the instant invention have imprpved characteristics compared to many of the current_state of the art low thermal expansion 10 materials ' . Even in comparison with the currently known NZP type materials and their known properties, these new bdϊhpositions demonstrate superior thermal expansion, thermal shock resistance, and mechanical properties and hence are useful over a wide range of temperatures and 15 stress conditions. BRIEF DESCRIPTION OF DRAWINGS FIG. 1 is graph illustrating the variation in thermal expansion over a wide range of temperatures for 20 ceramic compositions of the formula Sr l+X Zr 4 P 6-2X Si 2X°24 • FIG. 2 is graph illustrating the variation in thermal expansion over a wide range of temperatures for ceramic compositions of the formula 25 Ba 1+χ Zr 4 P 6 „ 2X Si 2 χ0 24 . FIG. 3 is graph illustrating the variation in thermal expansion over a wide range of temperatures for ceramic compositions of the formula Sr 1+ χZr 4 _2χY2χ p 6 ° 24 * FIG. 4 is graph illustrating the variation in 30 thermal expansion over a wide range of temperatures for ceramic ".ompositions of the formula s ri+χZr 4 _χYχP 6 _ x Siχ0 24 • FIG. 5 is a graph illustrating the variation in thermal shock resistance for two compositions within 35 the formula Sr 1+ χZr 4 Pg_2 X Si2 X θ2 4 for a range of quench temperatures differentials. FIG. 6 is a graph illustrating the axial ~ thermal expansion for various compositions in the series Sr l+X Zr 4 P 6-2X Si 2X°24 • FIG. 7 is a graph illustrating the thermal expansion anisotrophy resulting from varying azial thermal expansion for various compositions in the series Sr 1+x Zr 4 P 6 _2 X Si 2X 0 24 . FIG. 8 is a graph illustrating the variation in thermal expansion over a wide range of temperatures for a ceramic composition of the formula Ba 1#3 5 Zr 4 P 5# 25 si 0.75°24- DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS Novel NZP-type structural ceramic compositions having extremely high dimensional stability, high strength and high thermal shock resistance over a wide range of temperatures have been invented. The low thermal expansion ceramic compositions of this invention generally belong to three different series of compositions which show varying thermal expansion from positive to near zero to negative thermal expansion. The chemical formula for the compositional series can be written as Φι+χ z r 4 P 6 __2χSi 2 χθ24, Φι+χ z r 4 -_ 2 Y2X p 6°24 and 1+x Zr 4 _ x Y P 6 _ Si x 0 24 where "ø" represents Sr (strontium) and/or Ba (barium) and "X" represents the atomic proportions of the constituent elements. FIGS. 1, 2, 3 and 4 show fractional length change () vs. temperature curves for various values of "X" in the compositional series Sr 1+x Zr 4 P 6 _ 2X Si 2 θ2 , Ba 1+x Zr 4 P 6 __. 2X Si 2X 0 24 , Sr 1+x Zr 4 _ 2X Y 2x P 6 0 24 and Sr 1+x Zr _ x Y x P 6 _ χ Si x 0 24 respectively. When the value of "X" is 0.6, for the composition Sr 1+x Zr P 6 _ 2X si 2X 0 24 , the resulting ceramic has ultra low thermal expansion. The chemical formula for this specific composition can be written as Sr 1 . 6 Zr 4 p 4.8 s i l .2 0 24 ' When the value of "X" is 0.375 for the series Ba 1+x Zr 4 P 6 _2 X Si 2 θ2 4 , the resulting ceramic has ultra-low thermal expansion. The chemical formula for this specific composition can be written as Ba 1 ,37 5 Zr P5 (( 25 s io.75 0 24. When the value of "X" is 0.4, for the composition Sr 1+x Zr _ 2x Y2χ 6 °24' the resulting ceramic has ultra-low thermal expansion. The chemical formula for this specific composition can be written as Sr 1#4 Zr 3#2 Y 0#8 P 6 O 24 . When the value of "X" is 0.5, for the composition Srι +x Zr 4 _ x Y x P 6 __. x Si 2 θ 24 , the resulting ceramic has ultra-low thermal expansion. The chemical formula for this specific composition can be written as Sr 1#5 Zr 3> 5Y 0 .5P5.5Si 0# 5θ 24 In the formula Sr 1+x Zr 4 P 6 _ x Si 2X 0 24 the value of X generally ranges from about 0.4 to about 0.8 but is more typically between about 0.5 and about 0.7 and preferably is about 0.6 ± 0.05. The coefficient of thermal expansion for ceramics wherein X is from 0.5 to 0.7 is ve y good (in the range of + 2 X 10""°) while the coefficient of thermal expansion of ceramics wherein X is approximately 0.6 is excellent, being essentially zero (;H about 5 X 10"" 7 ) . In the formula Ba 1+x Zr 4 P5_2 X Si 2X 0 24 the value of X generally ranges from about 0.3 to about 0.6 but is more typically between about 0.3 and about 0.5 and preferably is about 0.375 + 0.025. The coefficient of thermal expansion for such ceramics wherein X is from 0.3 to 0.6 is very good (in the range of +2.2 X 10~ 6 ) while the coefficient of thermal expansion of such ceramics wherein X is approximately 0.375 is excellent, being essentially zero (± about 5 X 10~ 7 ) . In the formula Sr 1+x Zr 4 _ 2 Y 2 χ p 6°24 the value of X generally ranges from about 0.2 to about 0.6 but is more typically between about 0.3 and about 0.5 and preferably is about 0.4 ± 0.05. The coefficient of - thermal expansion for such ceramics wherein X is from 0 * 2 to 0.6 is very good (in the range of + 2.2 X 10_ 6 ) while the coefficient of thermal expansion of such ceramics wherein X is approximately 0.5 is excellent, being essentially zero (± 5 X 10_ 7 ) . In the formula Sr 1+x Zr 4 _ x Y x P 6 _ x Siχ0 24 the value of X generally ranges from about 0.3 to about 0.7 but is more typically between about 0.4 and about 0.6 and preferably is about 0.5 + 0.05. The coefficient of thermal expansion for such ceramics wherein X is from 0.4 to 0.6 is very good (in the range of + 2.2 X 10~ 6 ) while the coefficient of thermal expansion of such ceramics wherein X is approximately 0.5 is excellent, being essentially zero (+ 5 X 10~ 7 ) . In the novel compositions of this invention, hafnium may be substituted for a part or all of the zirconium present. In addition, Sr and Ba ions can be partially or fully substituted for each other. Thus, the formulas may be written as S -"(1+X)-γBaγZr 4 _ z Hf z P 6 _ 2X Si 2 χ0 24 and Ba (l+X)-Y Sr Y Zr 4-Z Hf Z p 6-2X si 2X°24 wherein X has the values stated herein above, Y can vary from 0.00 to 1.80 (or 1+X) and Z can vary from 0.00 to 4.00. The compositions in FIG. 1 represent the formula Sr (l+X)-Y Ba Y Zr 4-Z Hf Z p 6-2X s ^2X°24 wherein Y and Z have zero value for all the compositions and X has the following values: SZP - zero; SS50 - 0.5; SS60 - 0.6; SS100 - 1.0; and SS200 - 2.0. The compositions in FIG. 2, represent the formula Ba(i+χ)-γSrγZr 4 _ z Hf z P 6 -_2χSi2χθ24 wherein Y and Z have zero value for all the compositions and X has the following values: BZP - zero; BS50 - 0.5; BS100 - 1.0; BS150 - 1.5 and BS200 - 2.0. The structure is preferably substantially single phase in order to achieve the desired low thermal expansion properties. Very small amounts (nearly 5% (volume) ) of second phase materials such as zircon (ZrSi0 4 ) can be, however, tolerated. In the case of Ba 1# 5Zr 4 P5Si0 24 , larger amounts (greater than 5% (volume) ) of a second phase may be present which can have some impact on the coefficient of thermal expansion. Preferably, the starting raw materials used to synthesize this composition should be chemically pure. However, minor amounts of impurities that do not cause a significantly large amount, i.e. greater than 5% by volume, of any second phase to occur can be tolerated. The ceramic compositions of the present invention may be formed in any known or desired manner used for forming structural ceramics. Various known synthesis techniques such as sol-gel, solid state reaction (or oxide mixing) method, hydrothermal and like techniques can be used to synthesize the composition. The raw materials for sol-gel technique include water soluble salt of zirconium (e.g. zirconium oxychloride, ZrOCl 2 X H 2 0) , strontium nitrate (Sr(N0 3 ) .X.H 2 0) , yttrium nitrate (Y(N0 3 ) 3 .X.H 2 0)ammonium dihydrogen phosphate or phosphoric acid and ludox or other types of silica sols. In utilizing the oxide mixing technique, various different precursors can be used. To give an example, a stoichiometric mixture of strontium zirconate (SrZr0 3 ) , zirconium pyrophosphate (ZrP 2 0 7 ) and silica (Si0 2 ) can be calcined to give single phase In the hydrothermal technique, a technique similar to that used for sol-gel can be used to produce precursor powder which then can be treated hydrothermally under controlled pH to obtain single phase Sr 1.6 Zr 4 p 4.8 S il.2°24 « In oxide mixing or solid state reaction process, proper raw materials could be added in the stoichiometric proportions and ground to produce fine homogeneous mixture of raw materials. While any suitable grinding method may be used, ball milling is preferred for convenience and reliability. This mixture then can be calcined at 1200°C for 16 hours and then reground and heated to 1400°C for 12 to 16 hours to obtain the single phase composition. In another method of synthesis (sol-gel technique) , one may mix the aqueous solutions containing Sr +2 and Zr +4 ions and add silica sol to it followed by addition of solution containing phosphorous ions. Such ~ L mixture yields a precipitate that can be dispersed to -form a sol which after heating goes through a transition to gel state. Further heating causes the gel to dry and form fine agglomerated powder. This powder can be ground using any suitable grinding method and can be calcined at 700°C for 16 hours to form single phase Sr 1.6 Zr 4 p 4.8 si 1.2°24* Any known forming technique such as pressureless sintering, hot pressing, slip casting, extrusion, injection molding and the like can be used. In case of pressureless sintering technique, powder obtained from one of the synthesis techniques mentioned above can be ground to break the agglomerates to obtain uniform particle size distribution. Organic binder, such as polyvinyl buterol (PVB) or polyvinyl alcohol (PVA) can be added up to 1 to 2 weight percent to improve the green strength of the component. The material is then formed into a desired shape. Typically, the material may be formed in an uniaxial hydraulic press at about 100 to 200 MPa, followed by isostatic pressing at 250 MPa. After the isostatic pressing the component is heated slowly in a furnace up to the binder burnout temperature. The component is then further heated up to the sintering temperature of 1400 to 1500°C for 12 hours. The density of the component is measured by standard Archimedes technique. The sintered component is weighed and then immersed in a liquid of known density and displaced volume of the liquid is measured. The density is obtained by dividing the weight of the component by the volume of the displaced liquid. To ensure single phase formation, the component is characterized by using the standard powder X-ray diffraction technique. The X-ray pattern obtained is then evaluated to obtain lattice parameters of the crystalline phase present. These lattice parameters are used to determine the theoretical density of the material. The microstructure of the component is observed under a scanning electron microscope to determine the grain size distribution and other feature such as grain morphology, porosity etc. Coefficient of thermal expansion is measured by standard push rod dilatometer. The sample is heated in a furnace and the change length is measured as a function of temperature. Thermal expansion anisotropy or coefficient of thermal expansion is measured by high temperature X-ray diffraction technique. Strength of the component is measured by using the standard four point bend test. The typical strength of such material varies depending upon the synthesis and fabrication technique used. The thermal shock resistance is measured by the standard Hasselraan test. During this test, the sam le is heated to the predetermined temperature and then dropped into a bath of water at 0°C. The sample is then characterized for the strength. The quench temperature at which the strength drops by 50% is considered as the thermal shock temperature. The compositions of the ceramic materials described herein are suitable for applications over a broad range of temperatures where advantage can be taken of low thermal expansion and high thermal shock properties. These applications may include catalytic convertor substrates, cooking ware, optical mirror substrates, various ceramic engine parts such as exhaust manifold components and similar applications. Another advantage of these low thermal expansion compositions includes effective fabrication of whisker and/or fiber and/or particulate reinforced composites. The lower thermal expansion of the matrix material (compared to the whiskers and/or fibers and/or particulates) results in low interfacial stresses between the matrix and the reinforcing whisker and/or fibers and/or particulates. The reduced interfacial stress condition makes such composites less susceptible to catastrophic failures. EXAMPLE 1 A 50 gram sample of the composition Sr 1# 5Zr 4 P 5 Si0 24 was prepared by the sol-gel synthesis technique. The raw materials (strontium nitrate, zirconyl oxychloride, and ammonium dihydrogen phosphate) were dissolved in deionized solution. The silica sol (Ludox™ from DuPont) was predispersed solution. The quantitative analysis (using atomic absorption spectroscopy and/or loss on ignition techniques) was performed to establish the quantity of required ions per liter of the solution. Typically 0.5 to 0.25 molar solutions of strontium nitrate, zirconyl oxychloride and ammonium dihydrogen phosphate were prepared. First, the solutions containing Sr +2 ions and Zr + ions were mixed together in stoichiometric proportions under constant stirring conditions using a magnetic stirrer to obtain a homogeneous solution. Stoichiometric proportion of the silica sol was added to this mixture of solution containing Sr +2 and Zr +4 ions. This mixture was allowed to stir for at least 15 minutes to attain homogeneity. The solution containing phosphorous ions was added very slowly (drop by drop) to the mixture under vigorous stirring conditions. At this point the chemical reaction resulted in a fine precipitate which, after prolonged vigorous stirring, transformed in a highly homogeneous sol that contained the well dispersed precipitate. This sol, when heated at 90°C for 16 hours, transformed into a translucent gel, which, upon further heating, yielded ultra-fine ceramic precursor powder. This dried gel was attrited to break the agglomerates and was then calcined in an alumina crucible at 700°C for 16 hours. The calcined powder was then wet ball milled for 24 hours using alcohol as carrier. Zirconia grinding media was used to perform the grinding. Two weight percent XUS, an experimental binder from Dow chemical industry, and one weight percent PEG (polyethylene glycol) lubricant were also added to the ball milling batch. Other binders and - 14 - lubricants, such as those previously recited, could also be effectively utilized instead of the XUS binder and PEG lubricant. After the ball milling was complete, the powder was dried and the soft agglomerates were broken down by light grinding. The powder was then screened through em 80 mesh sieve. The component was fabricated in a bar shape by uniaxially compressing the powder at 15 MPa followed by isostatic pressing at 250 MPa. The bar was then sintered using a heating cycle which 0 * allowed binder burnout at 500°C for 4 hours. Sintering was performed at 1475°C for 12 hours and then the samples were allowed to cool in the furnace. The thermal expansion up to 1200°C was measured on a 5 cm. long bar by using a standard push 5 rod dilatometer from Harrop industries with pure alumina as reference standard. At least three measurements were made to obtain average thermal expansion. The strength was measured by four point bend test on 10 bars, which showed an average strength of - 0 approximately 115 MPa. A typical thermal shock resistance data is shown in FIG. 5 indicating discontinuous drop in strength at the thermal shock temperature. For the composition Sr 1# 5Zr 4 P 5 Si0 24 the temperature at which the 5 strength drops discontinuously was 775°C. Various compositions of the formula S__ 1+ χZr4P6_2χ0 24 were prepared according to the .technique detailed in this Example 1 in which the composition was one in which X = 0.5. The other ϋ compositions prepared were ones in which X was zero, Q.6, 1.0 and 2.0 as well as 0.5. These compositions were formed into ceramic bars in the manner set forth in this Example 1 and the thermal expansion was measured. The results of these measurements are set forth in FIG. 5 1. Generally compositions in which the value of X was equal to or greater confirmed significant volumes of a second phase i.e. a second phase present in volumes greater than 5%. Various compositions of the formula Ba l +X Zr 4 p 6 -2X°24 were prepared according to the technique detailed in Example 1 by the substitution of barium compound for strontium compound used in Example 1. The compositions prepared were ones in which X was zero, 0.5, 1.0, 1.5 and 2.0. These compositions were formed into ceramic bars in the manner set forth in Example 1 and the thermal expansion was measured. The results of these measurements are set forth in FIG. 2. Ceramic components having the composition Ba 1.375 Zr 4 p 5.25 s iθ.75°24 was prepared in the manner described in Example 1. This composition sintered to about 81% theoretical density with a strength of 53.2 MPa and a Young's Modulus of 59.36Pa. The bulk coefficient of thermal expansion approximated zero and was relatively flat from room temperature to about 1165°C, as illustrated in FIG. 8. The coefficent of thermal expansion from room temperature to 430° was about -8.64 x 10~ 7 /°C while from 430°C to 1165°C it was +5.44 x 10 "7 / β C. The ceramic composition wherein x = 0.375 generally has preferred bulk thermal expansion properties. EXAMPLE 2 Various compositions in the series Sr 1+x Zr 4 P 6 _ 2 χSi 2 χ0 24 and Ba 1+x Zr 4 P 6 _ 2X Si 2X θ2 4 , were prepared by solid state reaction technique. The stoichiometric proportions of the raw materials (BaZrθ 3 or SrZr0 3 , ZrP2θy and Si0 2 ) were homogeneously mixed by wet ball milling (alcohol as a carrier liquid) the raw materials. The slurry obtained following the ball milling was dried to yield dried powder which was calcined at 1200°C for 24 hours. The crystalline phases present in the calcined powder were evaluated by routine powder X-ray diffraction technique. In most of the compositions, large amounts of [NZP] type materials were formed; however, in some cases, ZrP 2 0 7 was not fully reacted. In the case of Sr 1+x Zr4P 6 _2 X Si 2 0 24 series of compositions, it was found that when the value of "X" exceeded 0.8, significant amount of unknown second phase (or phases) were formed. In the case of Ba -l+X Zr 4 p 6 - 2 X S;L 2X 0 24 series of compositions, it was foujd that when the value of "X" exceeded 0.7, significant amount of unknown second phase (or phases) were formed. The calcined powder was then wet ball milled for 24 hours using alcohol as carrier. Zirconia grinding media was used to perform the grinding. Two weight percent XUS, an experimental binder from Dow chemical industry, and one weight percent PEG (polyethylene glycol) lubricant were also added to the ball milling batch. Other binders and lubricants, such as those previously recited, could also be effectively utilized instead of the XUS binder and PEG lubricant. After .the ball milling was complete, the powder was dried and the soft agglomerates were broken down by li,ght grinding. The powder was then screened through an 80 mesh sieve. The component was fabricated in a bar shape by uniaxially compressing the powder at 15 MPa followed by isostatic pressing at 250 MPa. The bar was then sintered using a heating cycle which allowed binder burnout at 500°C for 4 hours. Sintering was performed at 1500°C for 12 hours and then the samples were allowed to cool in the furnace. The thermal expansion anisotropy of these compositions was measured by high temperature X-ray diffraction. The lattice parameters as function of temperature were measured and the thermal expansion of along the crystallographic axes were determined. FIG. 6 shows the axial thermal expansion for Sr l+X Zr 4 p 6 -2X s ^2X°24 se ries of compositions. FIG. 7 shows the thermal expansion along both the axes for the same compositions. It can been seen from the figure 7 that the thermal expansion anisotropy will be minimum at approximately X = 0.13. Such composition has minimum amount of microcracking, hence high Young's modulus, and high strength. However, the thermal expansion, as can be seen from FIG. 1, will not be at its minimum. This example shows that the thermal expansion and the thermal expansion anisotropy are independent parameters of these materials that can be manipulated by changing the chemical composition of the material to yield optimum properties for the desired application. For some uses it may be desirable to toughen the ceramic by the inclusion of zirconia or hafnia powders with the low expansion ceramic powders. These zirconia or hafnia powders when stabilized with yttria, ceria, or other stabilizers will remain in tetragonal crystal form after sintering to provide a toughened low expansion ceramic. These crystals may be present up to 30% by volume of the ceramic component. These ceramics may also be strengthened by inclusion of fibers or whiskers of silicon carbide, alumina, mullite, carbon, glass and the like. Exhaust port liners formed from the ceramic prepared in Example 1 exhibit excellent properties. A catalytic converter substrate formed from the ceramic prepared in Example 1 exhibits excellent properties. While not intending to be bound by one theory of the invention, the following theory may help to explain the phenomena observed in the present invention. The compositions of the present invention are believed to take advantage of crystal structure which supports flexibility towards ionic substitution and strain the c-axis by adding excess ions at the sodium site. This may be achieved by partially substituting silicon for phosphorous and compensating the deficient charge by adding excess cations at the sodium site or partially substituting yttrium for zirconium and compensating the deficient charge by adding excess cations at sodium site instead of just substituting larger cations at the sodium site. Anothe way of achieving similar effects should be to simultaneously substitute the yttrium and silicon for both the zirconium and the phosphorous sites respectively and compensating the deficient charge by adding excess cations at sodium site. Although the invention has been described with a certain degree of particularity in both composition and theory, it is to be understood that the present disclosure has been made only by way of example and that numerous changes in details of composition may be resorted to without departing from the scope of the following claims.

Claims: What is claimed: Claims 1. A ceramic having substantially neutral bulk thermal expansion consisting essentially of a substantially single phase composition of 01+X Θ 4 P 6-2X S; -2X 0 24 wherein X is a number having a value of between about 0.2 and 0.8, φ is either strontium, barium or mixtures thereof, and θ is either zirconium, hafnium, or mixtures thereof. 2. The ceramic of Claim 1 wherein φ is Sr and X is a number having a value from about 0.5 to about 0.7. 3. The ceramic of Claim 2 wherein X is a number having a value of about 0.6 + 0.05. 4. The ceramic of Claim 1 further including a separate phase of Zr0 2 and/or Hf0 tetragonal crystals. 5. The ceramic of Claim 1 wherein fibers or whiskers of other ceramic materials are present in said ceramic. 6. The ceramic of Claim 1 wherein φ is Ba and X is a number having a value of between about 0.2 and 0.6. 7. The ceramic of Claim 6 wherein X is a number having a value of about 0.3 to about 0.5. 8. The ceramic of claim 6 wherein X is a number having a value of about 0.375 + 0.025. 9. The ceramic of Claim 6 further including a separate phase of Zr0 2 and/or Hf0 2 tetragonal crystals in the ceramic present as a toughening agent 10. The ceramic of Claim 6 further including fibers or whiskers of other ceramic materials in the ceramic. 11. A ceramic having substantially neutral bulk thermal expansion consisting essentially of a substantially single phase composition of ^1+X Θ 4-2X V 2X P 6 °24 wherein X is a number having a value of between about 0.2 and 0.6, wherein φ is either strontium, barium or mixtures thereof, and θ is either hafnium or zirconium. 12. The ceramic of Claim 11 wherein X is a number having a value from about 0.3 to about 0.5. 13. The ceramic of Claim 11 wherein X is a number having a value of about 0.4 + 0.05. 14. The ceramic of Claim 11 further including a separate phase of Zr0 2 and/or Hfθ2 tetragonal crystals in the ceramic as a toughening agent. 15. The ceramic of Claim 11 wherein fibers or whiskers of other ceramic materials are present. 16. A ceramic having substantially neutral bulk thermal expansion consisting essentially of a substantially single phase composition of Φl+X θ 4-X γ X p 6-X s χ°24 wherein X is a number having a value of between about 0.3 and 0.7, wherein φ is either strontium, barium or mixtures thereof, and θ is either hafnium or zirconium. 17. The ceramic of Claim 15 wherein X is a number having a value from about 0.3 to about 0.6. 18. The ceramic of Claim 16 wherein X is a number having a value of about 0.35 to about 0.55. 19. The ceramic of Claim 16 further including a separate phase of Zr0 2 and/or Hf0 2 tetragonal crystals to toughen the ceramic. 20. The ceramic of Claim 16 wherein fibers or whiskers of other ceramic materials are present. 21. A method of making a ceramic having a controlled thermal expansion anisotrophy comprising incorporating into a first ceramic a separate phase of either zirconia or hafnium tetragonal crystals in a sufficient amount to induce microcracking in said first ceramic.

Inventors: LIMAYE SANTOSH Y, LIMAYE, SANTOSH, Y.
Applicants: CERAMATEC INC, CERAMATEC, INC.
Application year: 1990
Main classification: C01B25
IPC codes: C04B35