A superconducting thin film

Abstract: A superconducting thin film of a compound oxide represented by YBa₂Cu₃O y in which "y" is a number of 6 < y < 8 and deposited on a substrate, characterized in that a buffer layer of a compound oxide represented by Y₂BaCuO x in which "x" is a number of 4 < x < 6 is interposed between the superconducting thin film and the substrate.

Description: SPECIFICATION The present invention relates to a superconducting thin film of a compound oxide represented by YBa₂Cu₃O y in which "y" is a number in the range of 6<y<8 and deposited on a substrate, more particularly to a novel buffer layer interposed between a superconducting thin film of YBa₂Cu₃O 7-δ and a substrate. Description of the related art Superconductivity have been thought, for a long time, to be a phenomenon observable at ultra-low temperatures realized with liquid helium as a cryogen. However, the possibility of existence of a new type of superconducting material was revealed by Bednorz and Müller, who discovered (La, Sr)₂CuO₄ which exhibit the superconductivity at 30 K in 1986 (Z. Phys. B64, 1986 p 189). C. W. Chu et al. discovered, in the United States of America, another superconducting material of YBa₂Cu₃0 7-δ having the critical temperature of about 90 K in 1987 (Physical Review letters, Vol. 58, No. 9, p 908). Maeda et al discovered so-called bismuth type superconducting material (Japanese Journal of Applied Physics. Vol. 27, No. 2, p 1209 to 1210). And hence, the possibility of an actual utilization of high-Tc superconductors have burst onto the scene. The above-mentioned new type of superconducting materials was obtained in the form of sintered mass prepared by powder metallurgy. The sintered mass, however, showed rather poor superconducting properties, particularly lower critical current density (Jc). In order to increase the critical current density (Jc), a variety of thin film forming processes for these materials have been studied. Superconducting thin films of these compound oxides can be prepared by a variety of vapour deposition techniques such as vacuum-evaporation, sputtering, molecular beam epitaxy (MBE) on single crystal substrates such as SrTiO₃, MgO or the like. Remarkable improvements in the critical current density of these compound oxides have been achieved in their thin films. Their critical current densities, however, are not yet sufficiently high as to be utilizable in actual uses. In order to increase the critical current density which is requested for fabricating superconducting devices, it is indispensable to prepare a thin film composed mainly of a single crystal at a large area on a substrate. Such large single crystal of superconducting oxide, however, cannot be produced easily on a substrate by the present technology. Still more, so-called post deposition annealing operation is indispensable in order to realize effective superconductivity in oxide thin films prepared by known vapour deposition methods. However, it is known that the post deposition annealing operation causes diffusion or migration of substrate material into the thin film, so that the quality of superconducting property of the thin film is sharply deteriorated in the neighbourhood of an interface between the substrate and the thin film. An object of the present invention is to solve the above-mentioned problems and to provide a novel buffer layer to be interposed between a superconducting thin film of YBa₂Cu₃O 7-δ and a substrate, which is effective to improve the quality of the superconducting thin film. Summary of the Invention The present invention provides a superconducting thin film of a compound oxide represented by YBa₂CU₃O y in which "y" is a number of 6 < y < 8 and deposited on a substrate, characterized in that a buffer layer of a compound oxide represented by Y₂BaCuO x in which "x" is a number of 4 < x < 6 is interposed between the superconducting thin film and the substrate. An essence of the present invention resides in that the buffer layer is composed of the same constituent elements of Y, Ba and Cu as the superconducting thin film but atomic ratios of Y : Ba : Cu in this buffer layer is 2 : 1 : 1 which is different from atomic ratios of Y : Ba : Cu = 1 : 2 : 3 in the superconducting thin film. It is believed that crystal growth of YBa₂Cu₃O y in its superconducting thin film is attributed mainly to such an inherent property of this oxide that it is easily crystallized. In fact, the superconducting thin film of YBa₂Cu₃O y can be grown on a MgO substrate in spite of mismatching in lattice constant of 9.2 % between the thin film and the substrate. However, such desirable inherent property of YBa₂Cu₃O y is spoiled by the post deposition annealing which cause migration or diffusion of substrate elements into the superconductive YBa₂Cu₃O y . In other words, the superconducting thin film loses an effective crystalline structure which contributes to the superconducting phenomenon by the post deposition annealing. According to the present invention, in order to solve this problem, the superconductive YBa₂Cu₃O y is separated from the substrate by the buffer layer of the same compound oxide of Y-Ba-Cu as the superconducting thin film. Y₂BaCuO x which is the buffer layer according to the present invention has a very good crystallinity and forms a perovskite structure on MgO substrate with high reproducibility. And hence, it is easy to deposit the superconducting thin film of the superconductive YBa₂Cu₃O y of well crystallized structure on this buffer layer. Still more, this buffer layer of Y₂BaCuO x according to the present invention is a very stable compound, so that migration or diffusion into the superconducting thin film during the post deposition annealing is reduced, and if elements of the buffer layer diffuse or migrate into the superconducting thin film, bad influence caused by the diffusion or migration is minimized because the buffer layer is composed of the same elements as the superconducting thin film. In other words, contamination of the superconducting thin film caused by the migration or diffusion of the buffer layer is prevented and an effective thickness of the superconducting thin film is increased. In order to realize a desired crystal structure of Y₂BaCuO x in the buffer layer and to assure prevention of migration or diffusion from the substrate to the superconducting thin film, the buffer layer has a thickness greater than 10 nm (100 Å). The substrate is selected from oxides such as ZrO₂, MgO, SrTiO₃, yttrium stabilized zirconia (YSZ), LaGaO₃, NdGaO₃ and LaAlO₃. These oxides are single crystal oxides. The buffer layer is deposited on {100} plane or {110} plane of these oxide substrates. The buffer layer according to the present invention can be prepared by physical vapour deposition technique (PVD) such as sputtering, ionplating and molecular beam epitaxy (MBE) or by chemical vapour deposition (CVD) such as thermal CVD, plasma CVD, photo CVD and MOCVD. The superconducting thin film also can be prepared by the same PVD or CVD as above. Both of buffer layer and the superconducting thin film can be prepared by using usual sputtering operational conditions of which are well-known. In conclusion, the present invention provides a well-crystallized superconducting thin film of high-quality which is little influenced by migration of substrate material into the superconducting thin film and which is homogeneous in the direction of thickness. Now, the present invention will be described with reference to an example, but the scope of the present invention should not be limited thereto. Example 1 Both of a buffer layer and a superconducting thin film were prepared by sputtering in the presence of ozone gas (O₃). At first, a buffer layer of Y₂BaCuO x was deposited on a (100) plane of a single crystal of MgO substrate (10 x 10 mm) under operational conditions shown in Table 1 (1). Operational conditions for depositing a buffer layer of Y₂BaCuO x Composition of a target used Y : Ba : Cu = 2 : 1 : 2 Sputtering gas Ar + O₃ O₃/Ar + O₃ = 0.2 vol % Gas pressure 5.32 Pa (4 x 10⁻² Torr) Substrate temperature 750 °C High-frequency power 50 W 0.64 W/cm² Film thickness 10nm (100 Å) The resulting buffer layer was analyzed by a X-ray diffraction analyzer (Rigaku Denki Co., Ltd) with Kα of Cu to confirmed that the buffer layer has a composition of Y₂BaCuO₅. Then, a superconducting thin film of YBa₂CU₃O y was deposited on the resulting buffer layer of Y₂BaCuO₅ under operational conditions shown in Table 1(2). Operational conditions for depositing a superconducting thin film layer of YBa₂Cu₃O y Composition of a target used Y : Ba : Cu = 1 : 2 : 4 Sputtering gas Ar + O₃ O₃/Ar + O₃ = 0.2 vol % Gas pressure 5.32 Pa (4 x 10⁻² Torr) Substrate temperature 750 °C High-frequency power 50 W 0.64 W/cm² Film thickness 300nm (3,000 Å) The resulting superconducting thin film layer was analyzed by a X-ray diffraction analyzer (Rigaku Denki Co., Ltd) with Kα of Cu to confirm that the superconducting thin film layer has a composition of YBa₂Cu₃O₇. For comparison, the same procedure as above was repeated to prepare another thin film of YBa₂Cu₃O y deposited directly on MgO substrate without the buffer layer of the present invention. The critical temperature (Tco, Tci) and the critical current density (Jc) determined by usual methods are summarized in Table 2. Critical temperature (K) Critical current density (A/cm²) Tco Tci Invention 90 89 2.5 x 10⁶ Comparative 91 84 0.5 x 10⁶ Note: Tco : a temperature where electric resistance start to drop. Tci : a temperature where electric resistance could not be measured Critical current density was determined at 77 K Crystallinity of the thin film in the present invention and in comparative example were evaluated by a X-ray diffraction analysis and by a reflective high energy electron diffraction (RHEED) analyzer to find that both thin films were well-crystallized films of good quality. Such a big difference in the critical current density as is shown in Table 2 can be explained from such understanding that, in the comparative example, magnesium (Mg) of the substrate migrated into the superconducting thin film and deteriorated the superconducting thin film in the neighbourhood of the interface between the superconducting thin film and the substrate, so that the effective thickness of the superconducting thin film was reduced. The same result as in this example is obtainable by the film forming methods than sputtering.

Claims: A superconducting thin film of a compound oxide represented by YBa₂Cu₃O Y , in which "y" is a number in the range of 6 < y < 8 and deposited on a single crystal oxide substrate, wherein a thin film buffer layer of a compound oxide represented by Y₂BaCuO x , in which "x" is a number in the range of 4 < x < 6, is interposed between said superconducting thin film and said substrate, wherein said buffer layer has a thickness greater than 10 nm (100 Å) and wherein said substrate is made of an oxide selected from the group consisting of Zro₂, MgO, SrTiO₃, yttrium stabilized zirconia (YSZ), LaGaO₃, NdGa0₃ and LaAl0₃, and wherein said buffer layer is deposited on {100} plane or {110} plane of said substrate.

Inventors: HIGAKI KENJIRO, ITOZAKI HIDEO, YAZU SHUJI, HIGAKI, KENJIRO, ITOZAKI, HIDEO, YAZU, SHUJI, HIGAKI, KENJIRO, C/O ITAMI WORKS OF SUMITOMO, ITOZAKI, HIDEO, C/O ITAMI WORKS OF SUMITOMO, YAZU, SHUJI, C/O ITAMI WORKS OF SUMITOMO
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1990
Main classification: H01L39
IPC codes: C01G1, H01L39, C23C14, C01G3, H01B12, H01B13, C04B41