Method for increasing the bulk of creped tissue and creped tissue product

Abstract: The bulk of creped tissue products, such as facial and bath tissue, can be increased by steaming the tissue while stressed in the machine direction of the tissue.

Description: In the manufacture of tissue products, such as facial tissue, bath tissue, and paper towelling, it is generally desirable to impart as much bulk as possible to the final product. Most typically, bulk is increased by embossing the tissue web after the web has been creped. However, embossing has its drawbacks in that it increases manufacturing costs and can substantially degrade the strength of the web. Document GB-A-2 057 528 discloses a process for forming an absorbent paper product by creping a web while it has a moisture content above 50% and then drying the web until it is at least 80% dry to set the crepe. The invention therefore provides a method for making a tissue product according to independent claim 1 and the tissue product obtainable by this process. Further advantageous features of the invention are evident from the dependent claims and the following description and example. The invention is based on the discovery that the bulk of creped tissue webs can be increased simply by steaming the creped web while under tension. The bulk increase achieved by this steaming and greater increases are obtained with wetpressed tissues, because they are more compact to start with, than with through dried tissues. The bulk increases achieved normally are in a range of 10-50%, depending on the drying process applied. Steaming can be utilized to increase bulk with or without embossing. Besides its inherent simplicity, the method of this invention does not significantly degrade the strength of the web and in some cases, may actually increase the strength of the web. In a continuous tissue making process in which the creped tissue web is wound onto one or more rolls prior to converting, care must be taken not to compress the web too soon after the steam treatment so that the web can be sufficiently dried. Otherwise the web may lose its bulk gains and become stiff due to additional bond formation. For purposes herein, a creped tissue web is a creped web having a finished basis weight of from about 24.45 kg/259.2m² to about 239.61 kg/259.2m² (about 5 to about 49 pounds per 2880 square feet) and comprising one or more plies, each of which can have one or more layers. Preferably the web consists primarily of cellulosic papermaking fibers. Many different cellulosic fibers are suitable, particularly hardwood and softwood fibers in any combination, including secondary (recycled fibers). Typical creped tissue webs are, without limitation, wet pressed or through dried webs suitable for use as facial tissue, bath tissue, or household paper towels. Steam suitable for use in the method of this invention can be subcooled, saturated or superheated. The temperature and moisture content of the steam must be such to elongate the creped web when the creped web is under 1 gram per 2.54cm (1 gram per inch) of applied tension in the machine direction. The amount of tension applied to the web during the steam treatment can be about 1 gram per 2.54cm (about 1 gram per lineal inch) of width or greater, depending upon the nature of the steam and provided the web does not break. Naturally the upper limit of the amount of tension will depend largely upon the strength of the particular web. For facial and bath tissue, the amount of tension is preferably from about 1 gram per 2.54cm (about 1 gram per inch) of width to about 15 grams per 2.54cm (about 15 grams per inch) of width. For paper towelling, the amount of tension is preferably from about 1 gram per 2.54cm (about 1 gram per inch) of width to about 100 grams per 2.54cm (about 100 grams per inch) of width. The length of time the creped web is exposed to the steam treatment can be almost instantaneous in a fast moving continuous process and would preferably be about 1 second or less, although treatment times can be longer, such as from about 1 to about 5 seconds. Treatment times will depend upon the nature of the steam, the amount of tension and the strength of the tissue web. Example Air dry creped tissues having a blended furnish composition of 40% northern softwood bleached kraft fibers and 60% hardwood bleached kraft fibers were taped to a crossbar and suspended under tension in the machine direction of the tissue using glass rods light enough to prevent elongation before steaming but heavy enough to prevent buckling of the sample during or after steaming. Glass rod weights in the range of from about 2.4 to about 6.8 grams per 2.54cm (about 2.4 to about 6.8 grams per inch) have been used satisfactorily, the specific glass rod weight depending upon the particular tissue web being tested. While suspended, each tissue was humidified with saturated steam using a hand held steamer which was employed with a slow sweeping motion across and down the tissue to relax the crepe. Both sides of the tissue were humidified, regardless of the number of plies. The steaming process took about 30 seconds to treat the entire sample due to the relatively narrow coverage provided by the steamer. The resulting tissue was slightly wet to the touch after the steam treatment. After steaming, the tissue sample was allowed to air dry for about 5 minutes to come to equilibrium. Thereafter the properties of the tissue sample were measured. The results are set forth in the Table below. The control sample was not treated with steam, whereas test samples No. 1 and 2 were steam treated as described above. Web thickness is expressed in cm (inches) and bulk is expressed in 0.0284m3/45.3kg (cubic feet per 100 pounds). Both were measured in accordance with a standard test procedure (TAPPI Standard T4110s-68) using a TMI Model 549 thickness tester manufactured by Testing Machines Incorporated, Amityville, N.Y., except that the thickness tester utilized an anvil diameter of 5.08cm (2 inches) and a load of 80 grams per 6.452cm² (80 grams per square inch). The results clearly show a substantial increase in thickness and bulk for the steamed tissues over the Control. In addition, the steam-treated tissues appeared to exhibit an increase in perceived softness while slightly increasing in strength. The geometric mean tensile strength of the Control sample was about 570 grams per 7.62cm (about 570 grams per 3 inches) of width, whereas the geometric mean tensile for both test samples was about 600 grams per 7.62cm (about 600 grams per 3 inches) of width. Because the test samples were elongated during the steam treatment (2.7% for Sample No.1 and 6.8% for Sample No. 2), their finished basis weight decreased from 90.95kg/259.2m² (18.6 pounds per 2880 square feet) to 89.98kg/259.2m² and 88kg/259.2m² (18.4 and 18.0 pounds per 2880 square feet), respectively.

Claims: A method for making a tissue product comprising contacting a creped tissue web with steam while the web is under tension preferably in the machine direction, wherein the bulk of the web is increased. The method of claim 1 wherein the amount of tension is from 1 to 100 grams preferably to 15 grams per 2.54 cm (inch) of width. The method of claim 1 or 2 wherein the steam is subcooled steam. The method of claim 1 or 2 wherein the steam is saturated steam. The method of claim 1 or 2 wherein the steam is superheated steam. The method of one of the preceding claims wherein the tissue product is a two-ply tissue. The method of one of claims 1 to 5 wherein the tissue product is a single-ply tissue. A creped single or multiple-ply tissue product obtainable by steaming the creped web while under tension preferably in machine direction according to claim 1. The creped tissue product of claim 8 in which the tension is from 1 to 100 preferably to 15 grams per 2.54cm (inch) in width. The creped tissue product of claim 8 or 9 obtainable by steaming with a subcooled steam, a saturated steam or a superheated steam.

Inventors: CHEN FUNG-JOU, SMITH MICHAEL JOHN, CHEN, FUNG-JOU, SMITH, MICHAEL JOHN
Applicants: KIMBERLY CLARK CO, KIMBERLY-CLARK CORPORATION
Application year: 1990
Main classification: D21H25
IPC codes: B31D1, D21H27, A61F13, B31F1, D21H25