Method of manufacturing a semiconductor body comprising a mesa

Abstract: In semiconductor layer structures in which at least two semiconductor layers having different thicknesses and consisting of different semiconductor materials are present, mesas can be formed by means of wet-chemical etchants and with the use of a mask. A disadvantage of the etchants available is that it is difficult to form mesas having substantially flat side walls with a small under-­ etching and with an accurately determined width, especially of the thinner layer. This is an unfavourable starting situation for the manufacture of, for example, radiation guides and semiconductor diode lasers, in which such mesas are formed. In the method according to the invention, the upper and thicker of the two semiconductor layers is etched by means of a selective and preferential etchant, substantially no underetching occurring with respect to the mask. Subsequently, the lower and thinner semiconductor layer and a part of the upper semiconductor layer are converted by a substantially non-selective anodic oxidation into semiconductor material oxides, which are removed by means of an etchant which is non-selective with respect to the oxides formed, but is selective with respect to the semiconductor materials. As a result, mesas are obtained having a substantially flat side wall, the lateral dimension of these mesas being accurately determined by the size of the mask. Thus, particularly favourable results are obtained, especially in the InP/InGaAsP material system. The method according to the invention can be used very advantageously when the thinner layer forms part of a so-­ called multilayer quantum well structure. In a particular embodiment, a further mask is provided above the mask in such a manner that it projects beyond the mask, the side walls of the mesa being made substantially straight, as a result of which the method is particularly suitable for providing by means of OMVPE further semiconductor layers on either side of the mesa, which results in a substantially flat buried structure.

Description: The invention relates to a method of manufacturing a semiconductor body, in which there is provided on a semiconductor substrate a semiconductor layer structure comprising at least a first semiconductor layer consisting of a first semiconductor material and a second semiconductor layer provided thereon consisting of a second semiconductor material other than the first semiconductor material, while the thickness of the first semiconductor layer is chosen to be comparatively small with respect to the thickness of the second semiconductor layer, after which a mesa comprising at least the first and the second semiconductor layer is formed by etching and by means of a mask in the semiconductor layer structure, a wet-chemical etchant being used for removing the second semiconductor layer. Such a method is particularly suitable for manufacturing so-called buried hetero-junction semiconductor diode lasers, more particularly if the latter are wholly manufactured by means of OMVPE (= Organo-Metallic Vapour Phase Epitaxy) as growing technique. In this manner, buried or unburied radiation guides may also be manufactured. If such a method is used with the material system InP/InGaAsP, radiation sources, radiation guides etc. are obtained thereby, which are of great importance for glass fibre communication systems in the wavelength range of from 1 to 1.6 µm. Such a method is known from the article of S. Adachi et al entitled "Chemical Etching of InGaAsP/InP DH Wafer", published in Journal of Electrochemical Society, Vol. 129, No. 5, May 1982, pp. 1053-1062. In this article, a method is described of manufacturing mesas in a semiconductor layer structure comprising a comparatively thin first semiconductor layer of InGaAsP between two semiconductor layers of InP, the upper layer of which constitutes the second semiconductor layer. In this case, the semiconductor layers are removed by selective or non-selective wet-chemical etchants, such as HCl and mixtures thereof with H₂O, H₂O₂, CH₃COOH or H₃PO₄, which are selective etchants for InP, mixtures of H₂SO₄, H₂O₂ and H₂O, which are selective etchants for InGaAsP, and mixtures of HCl and CH₃COOH or H₃PO₄ to which H₂O₂ is added, or mixtures of Br₂ and CH₃OH, which are non-selective etchants, by which therefore both InP and InGaAsP can be etched. When etching a mesa, use is made of a mask layer comprising SiO₂. As has been found in practice, a disadvantage of the known method is that with a number of the etchants used therein, especially the non-selective etchants, such as mixtures of Br₂ and CH₃OH, the known method results in under-etching with respect to the mask. As a result, an accurate definition of the width of the mesa at the area of the first semiconductor layer is impeded because in this case this width depends upon the thickness of the second semiconductor layer. Due to this inaccurate width definition, a number of important properties of, for example, radiation guides or semiconductor diode lasers of which the mesa forms part are undetermined, which is undesirable. Such properties are, for example, the lateral mode in which the radiation is situated and the starting current of a semiconductor diode laser. With some other non-selective etchants, such as mixtures of HCl and HNO₃, the problem sometimes arises that they do not or substantially do not etch InP. If in the known method solely selective etchants are used, another problem arises, which is connected with the fact that the first semiconductor layer is comparatively thin with respect to the second semiconductor layer. It is difficult to accurately etch away this comparatively thin layer because the etchant is a wet-chemical etchant whose etching rate depends upon a large number of factors, such as the accurate composition of the semiconductor layer and the etchant, the temperature of the etchant etc. If the first semiconductor layer must be effectively etched away, that is to say that outside the mesa nothing is left of this layer at any place, some under-etching must be accepted. Due to the under-etching and especially due to the uncertainty with respect to the extent of this underetching, the width of the mesa at the area of the first semiconductor layer becomes uncertain. As a result, the same disadvantages are obtained as mentioned above for etching with non-selective etchants. If in the known method the semiconductor layers are removed alternately by a known chemical etchant etching selectively and by a known chemical etchant etching non-selectively, the aforementioned problems still arise, though to a smaller extent. In practice, mesas are often desired whose sidewalls are substantially flat, i.e. substantially not curved. For example, the width of a mesa in the direction of height of the mesa varies in an accurately defined manner, as a result of which the aforementioned problems of an undefined width at the area of the first semiconductor layer are smaller. More particularly, these problems substantially do not arise if the mesa has substantially straight sidewalls. Moreover, such flat sidewalls are often very suitable if, for example, by means of the OMVPE growing technique other semiconductor layers are provided beside the mesa. These flat sidewalls are often obtained by utilizing preferential etchants. An additional disadvantage of the known method in this case arises if several etchants are used for etching the mesa and one of these etchants does not etch preferentially or does not etch preferentially in the same manner as one of the other etchants. For example, it has been found that, if the second semiconductor layer comprises InP and the first semiconductor layer comprises InGaAsP and the second semiconductor layer is etched by means of a mixture of HCl and H₃PO₄, a mesa is obtained having substantially flat and straight sidewalls at the area of said layer. If subsequently the first semiconductor layer is etched by means of an etchant comprising a mixture of Br₂ and CH₃OH, in spite of the comparatively small thickness of the layer to be etched, the shape of the mesa is attacked due to the fact that also the second semiconductor layer is etched in such a manner that the flatness of the side edge of the mesa at the area of said layer disappears. At the same time, some under-etching occurs with respect to the mask. Finally, the disadvantage has to be mentioned that several chemical etchants give rise to a large under-etching at the area of the interface between the mask and the second semiconductor layer. The present invention has inter alia for its object to provide a method, by which mesas are formed having substantially flat sidewalls throughout the height of the mesa, the dimensions of said mesas at the area of the first semiconductor layer being accurately determined by the size of the mask, while not more than a small under-etching occurs. A method of the kind described in the opening paragraph is for this purpose characterized in that, when removing the second semiconductor layer, a selective and preferential etchant is used, while substantially no under-etching occurs with respect to the mask and, before the first semiconductor layer is removed, the semiconductor material of said layer and that of a part of the second semiconductor layer are converted by substantially non-selective anodic oxidation into semiconductor material oxides, after which the latter are removed by means of an etchant, which is non-selective with respect to the semiconductor material oxides and is selective with respect to the semiconductor materials. The term "semiconductor material oxide" is to be understood to mean a mixture of one or more oxides or oxygen-containing compounds of those elements which form part of the semiconductor material. Since the height of the mesa to be formed is mainly determined by the second semiconductor layer, when etching the latter by means of a selective and preferential etchant, a mesa is obtained having substantially flat sidewalls. Moreover, the thin first semiconductor layer can be removed without underetching with respect to the second semiconductor layer because the anodic oxidation takes place substantially non-selectively. Since the part of the second semiconductor layer converted into semiconductor material oxide has, viewed in lateral direction, only a small width, which is very uniform over the thickness of the second semiconductor layer, after the semiconductor material oxide has been removed, a mesa is thus obtained, whose shape and dimension, viewed in lateral direction, are accurately maintained. For dissolving the different semiconductor material oxides formed, an etchant is used which is non-selective with respect to these oxides and is selective with respect to the semiconductor material. By the method according to the invention, a mesa is obtained having substantially flat walls with a small under-etching with respect to the mask, whose dimensions, viewed in lateral direction, are very accurately determined by the dimensions of the mask and which does not or substantially not exhibit at the area of the first semiconductor layer a part of reduced width. The semiconductor material oxides can be removed in a separate bath or at the same time with the anodic oxidation in the bath used to this end. An additional advantage of the method according to the invention is that the first semiconductor layer can be removed in a very accurate and reproducible manner because the thickness of the layer comprising semiconductor material oxide is determined not by an etching time, but by a voltage applied. In a first embodiment of a method according to the invention, the first and the second semiconductor material are chosen so that the band gap of the first semiconductor material is smaller than the band gap of the second semiconductor material, while, before the semiconductor material is provided, a third semiconductor layer of the second semiconductor material is provided and the mesa is formed at least into the third semiconductor material, while, after the first semiconductor layer has been etched, the third semiconductor layer is etched by means of the selective and preferential etchant. Thus, mesas are obtained in which a double hetero-junction structure is present and which have a substantially flat side edge. These mesas are particularly suitable for use as radiation guide or as starting material for the manufacture of buried radiation guides or semiconductor diode lasers. If the starting material is a semiconductor substrate having a (001) crystal orientation and if the [110] crystal direction is chosen as the longitudinal direction of the mesas to be formed, mesas are obtained having substantially flat side walls substantially at right angles to the semiconductor layer structure. These mesas having a substantially rectangular cross-section have proved to be particularly suitable for the manufacture of radiation guides or semiconductor diode lasers, in which beside the mesa one or more further semiconductor layers are grown by means of OMVPE. More particularly in the InP/InGaAsP material system, buried semiconductor diode lasers having favourable properties, such as a low starting current and a long life and a small spread in the aforementioned properties can be manufactured by the method according to the invention. In a further embodiment of a method according to the invention, the mask by means of which the second semiconductor layer is etched is formed in a layer provided on the second semiconductor layer and etched away locally by means of a further mask. In deviation from the situation in which a photolacquer is used as a mask, the material of the layer forming the mask is chosen now freely in such a manner that the mask is not etched by the etchant of the second semiconductor layer and further that the stress produced between the mask and the second semiconductor layer is as small as possible, as a result of which the occurrence of under-etching remains limited. In practice, for example, a layer of silicon nitride provided by plasma CVD (= Chemical Vapour Deposition) has proved to be particularly suitable. In a variation of this embodiment, a fourth semiconductor layer is used as a mask-forming layer. If, for example, in the InP/InGaAsP material system, a semiconductor layer is chosen to this end which comprises InGaAsP, this layer can be accurately under-etched preferably by means of a selective etchant for such a semiconductor layer with respect to a further mask present on the semiconductor layer. The under-etching of the fourth semiconductor layer with respect to the further mask can be accurately adjusted because it can be observed in a simple manner, for example under a light microscope. In this manner, the lateral dimensions of the mesa to be formed can be accurately adjusted. If the crystal lattice of the fourth semiconductor layer accurately adjoins the crystal lattice of the second semiconductor layer, in a method according to the invention, in which the second semiconductor layer is etched by means of a selective and preferential etchant, substantially no under-etching of the second semiconductor layer is found with respect to the mask formed in the fourth semiconductor layer. Moreover, the fourth semiconductor layer can excellently be used as a contact-forming layer for a semiconductor diode laser to be formed. The second semiconductor layer, which comprises, for example, InP, is generally less suitable for this purpose. With the use of the method according to the invention, in which a fourth semiconductor layer is employed as a mask-forming layer, when removing the first semiconductor layer, the fourth semiconductor layer will be removed to the same small extent as the second semiconductor layer in lateral direction, which results in the aforementioned advantages. If the further mask is formed, for example, by a layer comprising silicon dioxide or silicon nitride and if the lateral dimensions, for example the width, of the further mask are chosen to be larger than the desired corresponding dimension of the mask, the further mask projects, after the mask has been formed by etching, beyond the mask. Such a configuration has proved to be particularly suitable in practice if other semiconductor layers are provided beside the mesa by means of OMVPE. In this manner, substantially flat buried hetero-semiconductor diode lasers are obtained. The flatness of such a laser is a great advantage when metallizing and finishing the latter. In an important embodiment of a method according to the invention, the thickness of the first semiconductor layer is chosen to be smaller than 0.2 µm. This thickness range is particularly suitable for the manufacture of semiconductor diode lasers and radiation guides. More particularly a method according to the invention is suitable for the manufacture of mesas, which comprise a multilayer quantum well structure, of which the first semiconductor layer forms part. If such a multilayer structure is etched by means of selective wet-chemical etchants for the layers forming a barrier and the layers forming a quantum well, respectively, a mesa is obtained having a comb shape in a sectional view at the area of said multilayer structure. When etching the n th layer of such a structure, also the (n-2) th , the (n-4) th layers etc. are etched again. As a result, the width of the multilayer structure will vary very strongly, which is undesirable. An additional disadvantage of this known method is that the etchant must often be changed, which is very cumbersome. Moreover, in this case the probability of errors and contamination of the etchants or the semiconductor body increases. The anodic oxidation of the first semiconductor layer, when it comprises InGaAsP or InGaAs as semiconductor material, can be very readily effected in a 3% solution of citric acid in water, of which the pH is brought to about 6 by means of NH₄OH, diluted with 2 parts of ethylene glycol. The semiconductor material oxide formed may be dissolved, for example, with a 1.5 molar solution of phosphoric acid in water. The anodic oxidation and the dissolution of the oxide formed may also be effected simultaneously in one medium. For this purpose, use may be made of a 3% solution of citric acid in water, of which the pH is brought to about 1.0 by means of H₃PO₄, diluted with 2 parts of ethylene glycol. If the second and third semiconductor layers comprise InP as semiconductor material, preferably a solution of hydrochloric acid and phosphoric acid in a ratio of 1 : 4 is used as selective etchant, while for selectively etching a layer comprising InGaAsP use is preferably made of an etchant comprising sulphuric acid, hydrogen peroxide and water in a ratio of 1 : 1 : 9. A further explanation of the invention will now be given with reference to two embodiments and the accompanying drawing, in which: Figures 1 to 4 show a first embodiment of a method according to the invention for the manufacture of a radiation guide with reference to a cross-section of the radiation guide at successive stages of the manufacture; Figures 5 to 10 show a second embodiment of a method according to the invention for the manufacture of a buried multilayer quantum well semiconductor diode laser, in which OMVPE is used as growing technique, with reference to a cross-section of the buried semiconductor diode laser at successive stages of the manufacture; Fig. 11 shows the stage corresponding to Fig. 9 with the use of the known method, in which solely selective wet-chemical etchants are used. The Figures are schematic and not drawn to scale, while for the sake of clarity especially the dimensions in the direction of thickness are exaggerated. Corresponding parts are generally designated by the same reference numerals in the various embodiments. Semiconductor regions of the same conductivity type are generally cross-hatched in the same direction. Figures 1 to 4 show a first embodiment of a method according to the invention for the manufacture of a radiation guide, which is shown in cross-section at successive stages of the manufacture. The starting material is a substrate 1 of monocrystalline n -type InP having a doping concentration of 2.10¹⁸ to 5.10¹⁸ at/cm³, a thickness of about 350 µm and a (001) orientation. After the surface has been polished and etched, there are successively grown on this surface, for example by means of OMVPE: an about 1 µm thick layer 2 of n -type InP having a doping concentration of 10¹⁸ at/cm³, an about 0.15 µm thick layer 3 of not intentionally doped InGaAsP having an In content of 83 at.% and an As content of 60 at.% corresponding to a wavelength of 1.3 µm, and an about 1.0 µm thick layer 4 of n -type InP having a doping concentration of 10¹⁸ at/cm³. By means of plasma CVD, a 0.15 µm thick layer 5 of Si₃N₄ is provided thereon (see Fig. 1). By means of photolithography and etching, a strip-shaped mask, whose longitudinal direction coincides with the [110] crystal direction of the semiconductor body and is at right angles to the plane of the drawing, is then formed in the layer 5, after which by etching by means of a selective and preferential etchant for InP comprising hydrochloric acid and phosphoric acid in a ratio of 1 : 4 at room temperature (etching rate = about 0.7 µm/min) the layer 4 comprising InP is locally removed without under-etching with respect to the mask formed in the layer 5. By means of anodic oxidation at a current density of 2 mA/cm², the region of the semiconductor body designated by reference numeral 6 is then removed in a solution of citric acid, whose pH is brought to about 1 by means of phosphoric acid, diluted with two parts of ethylene glycol. According to the invention, no under-etching of the semiconductor layer 3 then occurs with respect to the overlying semiconductor layer 4 because the etching step is carried out non-selectively. Due to the fact that the semiconductor layer 3 is comparatively thin, only a small quantity of material of the semiconductor layer 4 is removed and the size and shape of the mesa are substantially maintained (see Fig. 3). Subsequently, by means of OMVPE, an n -type semiconductor layer 7 of InP having a thickness of about 2 µm and a doping concentration of about 10¹⁸ at/cm³ is provided beside the mesa. After the semiconductor body has been cleft several times in a direction at right angles to the longitudinal direction of the mesa, mirror surfaces lying in the plane of the drawing then being formed, the radiation guides, which are particularly suitable for transport of radiation having a wavelength of from 1.3 to 1.5 µm, are ready (see Fig. 4). Figures 5 to 10 show a second embodiment of a method according to the invention of manufacturing a buried semiconductor diode laser, in which OMVPE is used as growing technique, with reference to a cross-section of the buried semiconductor diode laser at successive stages of manufacture. The starting material is a substrate 1 of monocrystalline n -type InP having a doping concentration of 2 . 10¹⁸ to 5 . 10¹⁸ at/cm³, a thickness of about 350 µm and a (001) orientation. After the surface have been polished and etched, there are successively grown on this surface, for example by means of OMVPE: an about 1 µm thick layer 2 of n -type InP having a doping concentration of 5 . 10¹⁷ at/cm³, a first SC (= Separate Confinement) layer 4′ of InGaAsP having an In content of about 73 at.% and an As content of about 60 at.%, which composition corresponds to a wavelength of 1.3 µm for bulk material and whose thickness is about 500 Å, four thin layers 3 forming a quantum well and comprising InGaAs having an In content of about 53 at.% corresponding to a wavelength of 1.65 µm for bulk material and having a thickness of about 75 Å, which are mutually separated by three thin layers 3′ forming a barrier and comprising InGaAsP having a composition corresponding to that of the first SC layer 4′ and having a thickness of about 50 Å, a second SC layer 2′ having the same thickness and composition as the first SC layer 4′, an about 1.0 µm thick layer 4 of p -type InP having a doping concentration of about 5 . 10¹⁷ at/cm³ and an about 0.2 µm thick layer 5 of p -type InGaAsP having a doping concentration of at least about 5 . 10¹⁸ at/cm³ and having an In content of 73 at.% and an As content of 60 at.% corresponding to a wavelength of 1.3 µm. Subsequently, by means of the sputtering technique, a 0.15 3 um thick layer 6 of SiO₂ is provided thereon (see Fig. 5). By means of photolithography and etching, a strip-shaped further mask having a width of about 4 µm, whose longitudinal direction coincides with the [110] crystal direction of the semiconductor body and is at right angles to the plane of the drawing, is then formed in the layer 6, after which the layer 5 comprising InGaAsP is locally removed by etching at 20°C by means of a selective etchant for InGaAsP comprising sulphuric acid, hydrogen peroxide and water in a ratio of 1 : 1 : 9 (etching rate = about 0.1 µm/min), with under-etching with respect to the further mask formed in the layer 6. The resulting width of the mask formed in the semiconductor layer 5 is about 2 µm (see Fig. 6). Subsequently, the semiconductor layer 4 is locally removed by etching by means of the selective etchant for InP mentioned in the preceding example without under-etching with respect to the mask formed in the layer 5 (see Fig. 7). By the method according to the invention, the region designated by reference numeral 7, which comprises the four layers 3 forming a quantum well, the three layers 3′ forming a barrier and the SC layers 2′ and 4′, is converted by means of anodic oxidation in a manner described in a preceding example into semiconductor material oxide, after which the latter is removed by an etchant which is non-selective with respect to the semiconductor material oxide formed and is selective with respect to the semiconductor material (see Fig. 8). Since the semiconductor materials used are not or substantially not attacked by the last-mentioned etchant, the etching process is stopped at the instant at which the semiconductor material oxide is entirely removed so that this etching step is not critical. According to the invention, substantially no under-etching of one of the semiconductor layers 2′, 3, 3′ and 4 occurs because both the anodic oxidation and the dissolution of the said oxides are effected non-selectively. Due to the fact that the latter semiconductor layers are very thin, only a very small quantity of semiconductor material need be removed and the size and shape of the mesa are accurately maintained (see Fig. 3). Subsequently, the semiconductor layer 2 is locally removed by etching by means of the selective etchant for InP mentioned in the preceding example substantially without under-etching with respect to the mask formed in the layer 5 (see Fig. 9). Subsequently, by means of OMVPE, there are successively provided beside the mesa a p -type InP semiconductor layer 8 having a thickness of about 0.8 µm and a doping concentration of about 5 . 10¹⁷ at/cm³, an n -type InP semiconductor layer 9 having a thickness of about 0.6 µm and a doping concentration of about 5 . 10¹⁷ at./cm³ and a p -type InP semiconductor layer 10 having a thickness of about 0.6 µm and a doping concentration of about 8 . 10¹⁷ at/cm³, which layers form due to the conductivity types chosen a current blocking structure with respect to a connection in the forward direction of the semiconductor layer structure located within the mesa. Due to the presence of the further mask 6 projecting beyond the mesa, a very uniform accurately adjoining and flat growth of the semiconductor layers 8, 9 and 10 is obtained beside the mesa, while no growth takes place on the further mask 6. After this further mask has been removed in a usual manner, a substantially flat structure is obtained (see Fig. 10), which is very advantageous for further treatments, such as metallization and mounting. After the lower and upper sides of the semiconductor body have been metallized in a usual manner and after the semiconductor body has been cleft several times in a direction at right angles to the longitudinal direction of the mesa, mirror surfaces lying in the plane of the drawing being formed, the resulting semiconductor diode lasers of the buried heterojunction type are ready to be finished. Such lasers are particularly suitable for use as a radiation source utilized in optical glass fibre communication systems. Fig. 11 shows the stage corresponding to Fig. 9 with the use of the known method, in which solely selective etchants are employed. For etching the layers 3 forming a quantum well and the layers 3′ forming a barrier, alternately the aforementioned selective etchants for InGaAsP and for InP (or similar selective etchants) are used. Due to the problems of such a method set out above, a comparatively and variable under-etching occurs at the area of the thin layers 3 and 3′. The resulting (irregular) comb structure has the disadvantage that the width of the active layer of a semiconductor diode laser to be formed becomes very uncertain. The disadvantages thereof have already been set out above. If the number of layers 3, 3′ is large, there is even a possibility that the upper layers 3, 3′ are fully etched away, the overlying part of the mesa then becoming detached. The invention is not limited to the embodiments described because many modifications and variations are possible for those skilled in the art within the scope of the invention. For example, semiconductor materials or compositions other than those mentioned in the embodiments may be used. Instead of a multilayer quantum well structure comprising alternately layers of InGaAs and InGaAsP, the layers of such a structure may comprise alternately InGaAs or InGaAsP and InP. The same applies to the composition of the bath in which the anodic oxidation is carried out or to the etchant by means of which the resulting semiconductor material oxide is dissolved. The choice thereof is determined inter alia by the relevant semiconductor material system. Further, a current-blocking structure may consist of a single high-ohmic semiconductor layer. If such a layer comprises, for example, InP, this layer may be made high-ohmic in that during its growth Fe atoms are incorporated having a concentration of about 10¹⁶ at/cm³. The invention is not limited either to a method of manufacturing mesas forming part of a radiation guide or a semiconductor diode laser. By a method according to the invention, not only (photo)diodes, but also transistors comprising a mesa may be manufactured. Inter alia the same advantages are then obtained as those obtained during the manufacture of the aforementioned devices.

Claims: A method of manufacturing a semiconductor body, in which there is provided on a semiconductor substrate a semiconductor layer structure comprising at least a first semiconductor layer consisting of a first semiconductor material and a second semiconductor layer provided thereon consisting of a second semiconductor material other than the first semiconductor material, while the thickness of the first semiconductor layer is chosen to be comparatively small with respect to the thickness of the second semiconductor layer, after which a mesa comprising at least the first and the second semiconductor layer is formed by etching and by means of a mask in the semiconductor layer structure, a wet-chemical etchant being used for removing the second semiconductor layer, characterized in that, when removing the second semiconductor layer, a selective and preferential etchant is used, while substantially no under-etching occurs with respect to the mask and, before the first semiconductor layer is removed, the semiconductor material of said layer and that of a part of the second semiconductor layer are converted by substantially non-selective anodic oxidation into semiconductor material oxides, after which the latter are removed by means of an etchant, which is non-selective with respect to the semiconductor material oxides and is selective with respect to the semiconductor materials. A method as claimed in Claim 1, characterized in that the first and the second semiconductor material are chosen so that the band gap of the first semiconductor material is smaller than the band gap of the second semiconductor material, while, before the first semiconductor layer is provided, a third semiconductor layer of the second semiconductor material is provided and the mesa is formed at least into the third semiconductor layer, and in that, after the first semiconductor layer has been etched, the third semiconductor layer is etched by means of a selective and preferential etchant. A method as claimed in Claim 1 or 2, characterized in that the mesa is strip-shaped, while as the longitudinal direction the [110] crystal direction is chosen and the mesa is provided with side walls substantially at right angles to the semiconductor layer structure. A method as claimed in any one of the preceding Claims, characterized in that as semiconductor substrate a substrate of indium phosphide, as first semiconductor material indium gallium arsenic or indium gallium arsenic phosphide and as second semiconductor material indium phosphide are chosen. A method as claimed in any one of the preceding Claims, characterized in that the mask is formed in a layer which is provided on the second semiconductor layer and is locally etched away by means of a further mask. A method as claimed in Claim 5, characterized in that the layer is made of silicon nitride and is applied by plasma CVD. A method as claimed in Claim 5, characterized in that as the layer a fourth semiconductor layer of the first semiconductor material is provided and on this layer is provided a further layer, in which the further mask is formed by means of photolithography and etching, after which the fourth semiconductor layer is etched with under-etching with respect to the further mask, the mask being formed in the fourth semiconductor layer in such a manner that the further mask projects beyond the mask. A method as claimed in Claim 7, characterized in that the fourth semiconductor layer is etched by means of an etchant etching this layer selectively with respect to the semiconductor material of the second semiconductor layer. A method as claimed in any one of the preceding Claims, characterized in that beside the mesa one or more semiconductor layers are provided by means of Organo-Metallic Vapour Phase Epitaxy. A method as claimed in Claim 7, 8 or 9 when dependent on claim 2, characterized in that the first conductivity type is chosen for the semiconductor substrate and for the third semiconductor layer and the second conductivity type is chosen for the second and the fourth semiconductor layer, while the first semiconductor layer is not intentionally doped and after the formation of the mesa a current-blocking layer structure in the form of a semi-isolating semiconductor layer or at least two semiconductor layers forming a blocking p-n junction is provided beside the mesa, after which the lower side of the semiconductor body and the upper side of the fourth semiconductor layer are provided with contacts and the semiconductor body is cleft in a direction at right angles to the mesa, mirror surfaces limiting the mesa being formed, so that with electrical connection in the forward direction laser operation is obtained, a part of the first semiconductor layer located within the mesa and forming a resonant cavity acting as an active radiation-emitting region. A method as claimed in any one of the preceding Claims, characterized in that the thickness of the first semiconductor layer is chosen to be smaller than or equal to 0.2 µm. A method as claimed in any one of the preceding Claims, characterized in that the first semiconductor layer is one of the layers of a multilayer quantum well layer structure formed by a stack of thin semiconductor layers, each layer forming a quantum well being surrounded by semiconductor layers comprising a semiconductor material having a larger band gap than the semiconductor layer forming a quantum well. A method as claimed in any one of the preceding Claims, characterized in that the anodic oxidation and etching of the semiconductor material oxides are carried out simultaneously in a 3% solution of citric acid in water, whose pH is brought to about 1 by means of phosphoric acid, diluted with 2 parts of ethylene glycol. A method as claimed in any one of Claims 1 to 12, characterized in that the anodic oxidation is carried out in a 3% solution of citric acid in water, whose pH is brought to about 6 by means of ammonia, diluted with 2 parts of ethylene glycol. A method as claimed in Claim 14, characterized in that the semiconductor material oxides formed are then etched in a 1.5 molar solution of phosphoric acid. A method as claimed in Claim 7 when dependent on claim 4, characterized in that indium phosphide is etched by means of an etchant comprising hydrochloric acid and phosphoric acid in a ratio of 1 : 4 and indium gallium arsenic phosphide of the fourth semiconductor layer is etched by means of an etchant comprising sulphuric acid, hydrogen peroxide and water in a ratio of 1 : 1 : 9.

Inventors: BINSMA JOHANNES JORDANUS MARIA, TIJBURG RUDOLF PAULUS, BINSMA, JOHANNES JORDANUS MARIA, TIJBURG, RUDOLF PAULUS
Applicants: PHILIPS ELECTRONICS NV, PHILIPS ELECTRONICS N.V.
Application year: 1990
Main classification: H01L21
IPC codes: H01L21, H01S5, G02B6, H01L33