Solid state electrochemical cell and current collector therefor

Abstract: A solid state laminar electrochemical cell having an alkali metal anode layer; a solid ionically conductive electrolyte layer; a cathode composition layer; and a current collector is described. The electrolyte layer is interposed between the alkali metal anode layer and the cathode layer. The cathode layer is interposed between the electrolyte layer and the current collector. The surface of the current collector which contacts the cathode layer is microroughened to enable the cathode layer to tightly adhere to the current collector.

Description: The present invention relates to solid state electrochemical cells. Solid state electrochemical devices are the subject of intense investigation and development. They are described extensively in the patent literature. See, for example, U.S. Patents 4,303,748 to Armand; 4,589,197 to North; 4,547,440 to Hooper et al.; and 4,228,226 to Christiansen. These cells are typically constructed of an alkali metal foil anode, typically a lithium foil, an ionically conducting polymeric electrolyte, a finely divided transition metal oxide cathode, and a cathode current collector which is attached to the face of the cathode not contacting the electrolyte. The current collector usually employed is a sheet of metal foil such as aluminium, nickel, or stainless steel. Although the above described cells have presented a viable option to older, more traditional secondary type discharge cells, the rechargeability and impedance of the cells have not achieved optimal performance. Part of the problem lies in the failure of the cathode material to form a good electric contact with the current collector. Failure of the cathode material making a good electrical contact with the current collector leads to an overall increase in cell impedance. This in turn, makes it difficult to recharge the cell. Attempts have been made in the battery cell art to increase adherence of a cathode material to the current collector, and to increase the surface area of the current collector. However, so far as the applicants are aware, no such attempts have been made in the field of solid state alkali metal anode cells. U.S. Patent Nos. 4,751,157 and 4,751,158 to Uchiyama et al. disclose cathode materials for use in lithium electrochemical cells. The cathode material comprises a mixed metal oxide as an active material, along with a conductive diluent and a binder which is pressed into electrodes on a nickel screen and sintered under vacuum. The cathode materials are used in cells which contain a liquid electrolyte, and more particularly, those which contain LiAsF 6 in an aprotic solvent, such as methyl formate. U.S. Patent No. 4,416,915 to Palmer et al. discloses a chalcogenide cathode made by applying a slurry of a mixture containing at least one intercalatable layered transition metal chalcogenide cathode active material, a conductivity enhancing agent and a binding agent in a vehicle to a high porosity current collector substrate, for example, foamed metals and glasses which are 97% to 90% porous with 10 to 1000 pores per square inch (1.55 to 155 pores per square cm) and adhering the cathode material to the substrate. The cathode material is utilized in a non-aqueous lithium cell having an electrolyte comprising an electrolyte-solvent mixture. U.S. Patent No. 4,560,632 to Alberto discloses a moulded porous cathode collector for use in non-aqueous cells. The collector includes a particulate carbonaceous conductive material bonded with a suitable binder, and having on its surface a coating of a vinyl polymer film to improve its mechanical strength and handling characteristics. The cathode collector is used in association with liquid cathode materials. U.S. Patent No. 4,689,475 to Kleiner et al. discloses electrical devices which include two electrodes and a conductive polymer element located between the two electrodes. One of the electrodes is a metal electrode whose surface which contacts the conductive polymer is roughened or otherwise treated to improve its adhesion to the conductive polymer. The conductive polymers exhibit positive temperature coefficient behavior so that the electrical device can be used in heaters and circuit protection devices. In the field of solid state lithium cells, U.S. Patent No. 4,735,875 to Anderman et al. discloses a cell wherein a cathode material which takes the form of a microporous sheet containing polyethylene, an electrically conductive and electrochemically active particulate material and a plasticizer is laminated to a current collector such as a screen, grid, expanded metal, woven or non-woven fabric formed from efficient electron conductive materials such as carbon, or metal such as copper, aluminum, nickel, steel, lead or iron. Prior to the making of the present invention, there has been no disclosure, so far as the applicants are presently aware, of a solid state alkali metal cell wherein a highly uniform electrical contact between the cathode material and cathode current collector is maintained during operation and recharging of the cell. In accordance with the present invention, there is provided a solid state laminar electrochemical cell comprising: an alkali metal anode layer, a solid ionically conductive electrolyte layer, a cathode composition layer, and a current collector, said electrolyte layer being interposed between said alkali metal anode layer and said cathode composition layer, and said cathode composition layer being interposed between said electrolyte layer and said current collector; characterized in that said current collector has a microroughened surface and the cathode composition is at least partially cured in contact with said microroughened surface to cause it to tightly adhere thereto; and in that said microroughened surface is provided in the form of: (i) a polymeric substrate with either an electroconductive ink discontinuously coated thereon, or a first layer of vapour deposited copper film and a second layer of electrodeposited nickel particles overcoating the first layer, (ii) a metal, which term includes carbon, or polymeric substrate having metal, which term includes carbon, particles deposited thereon, except that when the substrate is other than carbon, the deposited particles are carbon, (iii) a smooth surface rendered microrough by removal of material therefrom other than by etching, or (iv) a smooth surface treated by contact with a patterned surface to microroughen it. The teachings of the present invention enable us to produce embodiments of solid state alkali metal anode primary or secondary cell having significant improvements in cell impedance and, in turn, rechargeability and high current discharge (power). A tightly adherent contact is maintained between the cathode and cathode current collector of the cell. In a particular embodiment, the alkali metal anode layer comprises a lithium foil, a lithium coated metal foil or a lithium alloy. The preferred electrolyte is a single-phase solid solution of an ionizable alkali metal salt, a solvent for the salt, and a polymer which has been polymerized by exposure to actinic radiation. The cathode composition preferably includes V 6 0 13 , electrically-conductive carbon particles and the above-described ionically-conductive electrolyte. The current collector is electrically conductive and is characterised by its surface which contacts the cathode being microroughened to enable better adherence of the cathode to the current collector. The microroughening of the surface could be accomplished by a number of methods. For example, the current collector could take the form of a metal foil substrate having the same or different metal particles electrodeposited on to its upper surface. The external surfaces of the metal particles form the microroughened surface. Alternatively, the current collector could take the form of a polymeric film having an electrically conductive material coated on its upper surface. The electrically conductive material, which may take the form of a metal or an electroconductive ink is discontinuously coated onto the film. The surface discontinuities form the microroughened surface. The improved adherence of the cathode composition to the current collector reduces the impedance of the overall cell, thereby improving performance, particularly during recharging. Where the current collector is a metal foil, the foil could be a nickel or copper foil and microroughening accomplished by electrodepositing metal particles, typically nickel particles on to the metal foil. Where the current collector comprises a polymeric substrate having an electrically conductive material deposited on the surface of the substrate which is to contact the cathode layer, the substrate preferably comprises a polyethylene terephthalate film and the material could comprise one or more electrodeposited metals or an electroconductive ink. For example, the current collector could take the form of a plastic film having a first layer of a vapour deposited copper film and a second layer of electrodeposited nickel particles, overcoating the first copper layer. Such a collector can be manufactured with a minimal thickness. However, in order that the invention claimed in the present application is to be adequately distinguished from that of the applicants' co-pending Application 90304509.4, the published specification of which, namely EP-A-0396324, is available as part of the state of the art, but only under Article 54(3) EPC, the present invention is limited to the microroughened surface being provided in one of the following forms: (i) The microroughened surface may be provided as a polymeric substrate with either an electroconductive ink discontinuously coated thereon, or with a first layer of vapour deposited copper film and a second layer of electrodeposited nickel particles overcoating the first layer. (ii) A metal (which term includes carbon) or polymeric substrate has metal (which term again includes carbon) particles deposited thereon. However, when the substrate is other than carbon, the deposited particles are necessarily carbon. (iii) The microroughened surface may comprise a smooth surface rendered microrough by removal of material therefrom by a means other than by etching. (iv) The microroughened surface may be provided as a smooth surface which has been treated by contact with a patterned surface so as to microroughen it. The microroughening of the surface is hereinafter more particularly described by way of example only with reference to the accompanying drawings, in which:- Fig. 1 is a side cut-away view of a cell embodying the teachings of the instant invention; Fig. 2 is a side view of a current collector embodying the teachings of the instant invention; Fig. 3 is an electron microscope photograph top view of a nickel foil having electrodeposited thereon nickel particles; Fig. 4 is an electron microscope photograph side view of a copper foil having electrodeposited thereon an irregular layer of nickel; Fig. 5 is a side view of an alternate current collector also embodying the teachings of the instant invention; and Fig. 6 is an electron microscope photograph side view of a polyethylene terephthalate film overcoated with a vapour deposited layer of copper which is overcoated with an electrochemically deposited layer of nickel. An embodiment of laminar solid state cell produced in accordance with the present invention is shown in Fig. 1 and is represented by element 10. Cell 10 includes current collector layer 12, cathode composition layer 14, electrolyte composition layer 16 and alkali metal anode layer 18. Cell 10 also includes protective covering 20 which functions to prevent water and air from contacting the reactive layers of the cell. Cell 10 is preferably a laminar thin cell type including a lithium anode. Laminar thin-cell batteries containing lithium anodes are known in the art, and it will be appreciated that the cell can include various constructions such as bi-faced or bi-polar cell designs. Examples of cell constructions include a "jelly roll" (swiss roll) or a fan folded laminate strip design, both of which are illustrated in our EP-A-0 357 399. Referring now to Fig.2, the current collector, designated by element 11 is shown in greater detail. Collector 11 includes substrate 12, preferably a metal foil, having a microroughened surface 13. Presence of microroughened surface 13 enables adherence of the cathode composition to the current collector. Substrate 12 may be selected from any number of electrically conductive materials, typically metals. Examples of substrate materials include carbon, copper, aluminium, nickel, steel, lead and iron and combinations thereof. In practice, the thickness of substrate 12 typically ranges from about 5 µm to about 25 µm and should be as thin as practicable. The microroughened surface 13 can be prepared in a number of different ways. The preferred method is electrodeposition of metal particles, preferably copper or nickel particles onto substrate 12, the microroughened surface being the surface which is exposed to the cathode composition. For example. electrodeposited foils, particularly copper and nickel foils, are preferred. However where the substrate metal is other than carbon, the deposited metal particles are limited in this invention to carbon. It is also possible to use other processes which result in a similar degree of roughness, e.g., irregularities which protrude from the surface by a distance of at least 0.03 µm, preferably at least 0.1 µm, particularly 0.1 to 100 µm, and which have at least one dimension parallel to the surface which is at most 500 µm, preferably at most 100 µm, particularly at most 10 µm, and which is preferably at least 0.03 µm, particularly at least 0.1 µm. The irregularities can be of the same shape as those produced by electrodeposition, e.g., generally spherical nodules protruding from the surface, or they can be of a different shape. Such processes can create the microrough surface by removal of material from a smooth surface, etching being excluded in this invention, or by chemical reaction with a smooth surface. A smooth foil can be treated by contact e.g. rolling or pressing with a patterned surface to generate a microroughness. The microrough surface can if desired be treated to change its chemical characteristics. For example, an electrodeposited metal foil can be passivated i.e. rendered inactive or less chemically reactive, by an appropriate treatment, e.g., one which provides a coating thereon, especially a nickel treatment of an electrodeposited copper foil on a polymeric substrate. Referring to Figure 3, an electron microscope top view of nickel particles electrodeposited on a nickel surface is shown by way of example of the surface appearance of deposited metal particle microrough surfaces, though this particular combination of nickel deposited on a nickel foil is not within the scope of the present invention. The surface characteristics of the electrodeposited particles 13 provide the microroughened surface to enable better adhesion to the cathode composition. Referring to Figure 4, an electron microscope side view of an alternative metal coated foil current collector is shown, again by way of illustration of a typical microrough surface, though this particular combination of nickel particles deposited upon a copper foil substrate is also not within the scope of this present invention. The collector comprises a metal foil overcoated with a discontinuous layer of nickel metal. The surface of the nickel metal is discontinuous to provide better adhesion to the cathode composition. Referring back to Fig. 1, alkali metal anode layer 18 may take the form of a lithium foil, a lithium coated foil such as nickel or copper foil having a layer of lithium deposited on its surface or a lithium alloy. Lithium is a preferred anode material because it is very electropositive and light in weight. However, other alkali metal materials, such as sodium may be practised within the scope of the present invention. Electrolyte layer 16, which is ionically but not electrically conductive, takes the form of a solid material and is laminated to the alkali metal anode layer 18 and the cathode layer 14. The preferred electrolytes are solutions of an ionizable alkali metal salt or an alkaline earth salt,an aprotic solvent and a polymerizable compound. Still more preferred are solutions of an alkali metal salt, a liquid, monomeric or prepolymeric radiation or thermally polymerizable compound and a radiation or thermally inert ionically conducting liquid. Polymerizable compounds useful in the electrolyte composition may yield either a conductive or nonconductive polymer. Compounds which yield a conductive polymer contain a heteroatom capable of forming donor-acceptor bonds with the alkali metal cation. Useful polymerizable compounds are described next. Polyethylenically unsaturated monomeric or prepolymonomeric materials useful in practice of the present invention are preferably compounds having at least one, and more preferably a plurality, of heteroatoms (particularly oxygen and/or nitrogen atoms) capable of forming donor acceptor bonds with an alkali metal cation and are terminated by polymerizable moieties. These compounds yield a conductive supportive matrix. More specifically they are preferably low molecular weight oligomers of the formulae (I)-(III) below where n is about 3 to 50 and R is hydrogen or a C1-C3 alkyl group and are terminated by ethylenically unsaturated moieties or glycidyl moieties represented by A. A particularly useful group of compounds is obtained by reacting a polyethylene glycol with acrylic or methacrylic acid. Polyethylene glycol diacrylate is a particularly preferred polymer. To provide additional structural integrity, triacrylate prepolymers may be added. Preferably, the radiation or thermally inert ionically conductive liquids have a boiling point greater than 80°C. Examples of these liquids include -butyrolactone, propylene carbonate, 1,3-dioxolane and 2-methyltetrahydrofuran. Less polar solvents having heteroatoms capable of bonding alkali metal cations are also useful. Polyethylene glycol dimethyl ether (PEGDME) is one such example. Glymes such as tetraglyme, hexaglyme, and heptaglyme are also desirable solvents. Propylene carbonate is a preferred solvent. As to the ionizable salt, formula MX, this is not limiting at all, and is the type in which: M+=Li + , Na + , K + , Ca 2+ , Mg 2+ , NH 4 + X-=I-, Cl0 4 -, BF 4 -, AsF 6 -, CF 3 SO 3 -, CF 3 CO 3 -, PF 6 -B 12 H 12 2 -, B 10 C 10 2 -, B 4 -,  designating C 6 H 5 , or an alkyl or an aryl chain. To produce a solid electrolyte material, the solution of the ionizable salt and inert ionically conductive liquid is mixed with the curable composition and the mixture is cured by exposure to actinic radiation, preferably electron beam or ultraviolet radiation or by heating if a thermally curable system is utilized. If ultraviolet radiation is used for curing, an ultraviolet photoinitiator may be added to the composition. Similarly if a thermally curable composition is selected, a thermal initiator should be present in the composition. Examples of thermally curable compositions are disclosed in U.S. Patent No. 4,792,504. Alternatively, the electrolyte can take the form of a solid solution of an alkali or alkaline earth salt in a curable polymerizable compound. In still another embodiment, the solid solution may include a plasticizer or liquid electrolyte in addition to the solid solution. The cathode composition layer 14 includes a cathode material which is coated on the microroughened 13 surface of the current collector 12. Cathode compositions are known in the art. Typically they comprise an intercalation compound, an ionically conductive solid polymer electrolyte containing solution of an alkali metal salt or alkaline earth salt as defined above, and an electrically conductive filler. A typical formulation may contain about 25 to about 70 parts by weight of intercalation compound, about 2 to about 15 parts of an electrically conductive filler, and about 15 to about 75 parts of the ionically conductive electrolyte. The following compounds have been taught in the art for use as intercalation compounds: V 6 O 13 , MoO 2 , MnO 2 , V 2 O 5 , TiS 2 , MoS 3 , Cr 3 O 6 , Li x V 3 O 8 , V 3 O 8 , VS 2 , NbSe 2 , FeOCl, CrOBr, TiNCl, ZrNCl, HfNBr, FeS, NiS, Co0, Cu0 and WO 2 . V 6 O 13 is particularly preferred. For use as an electrically conductive filler, carbon may be used. In addition to providing a matrix for containing the alkali metal salt, the ionically conductive polymer additionally functions as a binder material to enable the cathode composition to adhere to the collector substrate. Because of its adhesive qualities, acrylated polyethylene oxide is the preferred ionically conductive polymer. For use as an additional adhesive, acrylated polyesters may be selected. The process for producing cell 10 is as follows. Because the cell produced utilizes an alkali metal anode layer, usually a lithium anode layer, it is necessary to manufacture the cell in a water (humidity) free environment. Lithium is extremely reactive with water and if reacted, a passivation layer can form on the surface of the anode layer, reducing the efficiency of the layer, and increasing cell impedance. Accordingly, it is particularly desirable to manufacture the cell in an environment having a relative humidity at room temperature of less than 2% (less than 300 ppm water). An environment containing between 1 ppm and 50 ppm water produces a particularly efficient cell. Cathode composition 14 as defined above is coated onto the microroughened surface of current collector 12. Cathode composition 14 is paste-like in consistency. Coating may be accomplished using conventional coating techniques such as doctor blade or coating an extrusion method. In practice, the optimum thickness ranges between about 25 and about 250 microns. In order to obtain a one-hour discharge with 75-100% utilization of the cathode composition, the layer thickness ranges between 50 and 100 microns in thickness. Where a faster discharge rate is desired, a lower thickness may be selected. Conversely, if a slower discharge rate is desired, a thicker layer may be provided. In practice, the cathode composition layer has an impedance less than 50 ohms/cm 2 . After cathode composition 14 has been coated onto current collector 12, the top surface of the cathode layer is optionally rolled by utilizing a non-stick pressure roller such as a PTFE roller. Alternatively, if the cathode composition sticks to the surface of the roller, a non-stick release liner, not pictured, may be placed onto the upper surface, the roller can traverse the length of the release liner, and the release liner can then be removed. Rolling the upper surface of the cathode layer benefits in that it improves adherence between cathode composition 14 and current collector 12 and produces a smoother surface which enables a very thin electrolyte layer to be coated thereon. As a result of the surface rolling, the open circuit voltage discharge associated with cathode composition 14 is significantly reduced as compared to a cell whose cathode does not have a rolled surface. Accordingly, the overall cell efficiency is improved. The utilization of microroughened surface 13 of the current collector 12 along with the optional pressure rolling step following the coating of cathode composition 14 onto current collector 12 enables a tightly adherent contact to occur between the respective materials. This, in turn, reduces impedance at the collector/cathode composition interface. The impedance at the interface is typically less than 10 ohms/cm 2 and, in the preferred embodiment, less than 5 ohms/cm 2 . Electrolyte layer 16 is coated as a thin film onto the cathode composition layer 14. The electrolyte can be extruded and coated in a very thin layer, typically ranging from about 5 µm to about 25 µm. The ability to coat in a thin layer is in large part due to the continuous surface of cathode composition. When electrolyte 16 is coated onto cathode 14, it is coated in an uncured liquid state. As is readily understood, electrolyte layer 16 must completely coat cathode composition layer 14 to prevent the intercalation compound and electrically conductive filler from protruding through electrolyte layer 16. The thickness of electrolyte layer 16 need only be thick enough to completely coat the upper surface of the cathode composition. Once electrolyte layer 16 has been coated onto cathode composition 14, the assembly is partially or totally cured by radiation or thermal means. In practice, exposure of the assembly to an electron beam operating at a power of 3 to 9 Mrad is particularly preferred. Alternatively an ultraviolet or thermal source may be selected. If an ultraviolet source is selected, the monomer preferably includes an ultraviolet initiator of the type commonly known in the art such as thioxanthone initiators. If a thermal source is selected, the monomer preferably includes a thermal initiator of the type commonly known in the art such as those disclosed in U.S. Patent No. 4,792,504 to Schwab et al. Curing the cathode composition and the electrolyte polymerizes and crosslinks and thereby solidifies the monomeric material by conversion to a polymeric form. A partial curing step (as opposed to full curing) may be particularly desirable as this enables the electrolyte layer 16 to remain somewhat tacky. This enables better adherence between the electrolyte and the anode layer, when coated. After partial or total curing of cathode composition 14 and electrolyte 16, alkali metal anode layer 18 is applied to electrolyte layer 16. Although not pictured, a thin polymeric material such as a porous polypropylene sheet may be interposed between the anode and the electrolyte to ensure that the anode does not contact the cathode layer, particularly at the outer edges of the respective layers. Use of the polymeric sheet is optional. After anode layer 18 is coated onto electrolyte 16, the entire assembly is optionally passed through pressure rollers. The pressure rolling step aids in the adhesion of the layers to each other, thereby reducing interfacial impedance between component layers. If the cathode composition 16 and electrolyte 14 have not been completely cured, the entire assembly is again cured by exposure to actinic radiation, preferably electron beam radiation or by thermally curing. This step functions to solidify the cathode composition and electrolyte layers, thereby producing a solid state cell. Once the current collector, cathode composition, electrolyte composition and anode composition have been assembled, electrodes are attached to the anode and current collector layers by means known in the art. The assembly is then inserted into an air and water impermeable protective material 20 and the edges of the protective material are sealed, preferably by heat sealing around edges of the cell components. Sealing preferably occurs under vacuum conditions to enable the protective material to form a tightly adherent seal around the component layers and electrodes such that the only external access to the component layers is via the electrodes. Examples of the heat sealable gas and water impermeable protective materials include a multi-layered material having an interior heat sealable layer comprising ethylene acrylic acid, an intermediate barrier layer comprising aluminum foil, and an exterior layer of polyethylene terephthalate. Other heat sealable protective materials known in the art can be used. The protective materials should be as thin as possible to minimize the overall thickness of the cell. Commercially available heat sealable materials of the types described above can have an overall thickness of less than 200 µm. Once the components have been inserted and sealed in the protective material, the cell is available for use by simply connecting the electrodes to the device to be powered. When utilizing a single lithium anode cell, the cell generates a voltage of approximately 2.7 volts and a current flow exceeding 50 mA/cm 2 . Referring now to Fig. 5 an alternative current collector is shown and designated as 100. Collector 100 includes polymeric substrate 102 having coated thereon a layer of an electrically conductive material 104. Optionally overcoated on material 104 is another layer of an electrically conductive material 106. Substrate 102 may be selected from polymeric film materials including polyethylene, polyethylene terephthalate and polyvinyl chloride. The thickness of film 102 is extremely thin, with thickness of less than 5 µm and even about 1 µm possible. This enables the manufacture of very thin current collectors, and hence, very thin laminar cells. Electrically conductive materials 104 or 106 could be any of the materials as discussed with respect to Fig. 2, but for the purposes of the present invention deposited 'metal' particles are either carbon or a first layer of vapour deposited copper and a second layer of electrodeposited nickel particles overcoating the first layer. Alternatively, examples of other electrically conductive materials may include electrically conductive inks. Such inks are known in the art and are typically used for screen printing, manufacture of membrane switches, EL lamps and displays, and flexible circuits. Examples of silver filled and indium oxide-filled electrically conductive inks are manufactured by Zymet Inc. of East Hanover, New Jersey. The inks are applied onto the polymeric film in a patterned form such as a grid, mesh, spiral, and the like. Depending on the thickness of the ink layer, an extremely thin current collector can be produced. Referring to Fig. 6, an electron microscope side view photograph of a current collector manufactured in accordance with the present invention is shown. Collector includes polyethylene terephthalate film overcoated with a vapor deposited first layer of copper which is overcoated with an electrodeposited layer of nickel particles. The overall thickness of this collector is about 1 to 5 µm. The microroughening of the surface is further explained in the following examples which contrast microrough current collector cells with similar cells in which the current collector does not have a microrough surface. Though none of the particular examples with microrough surfaces are within the scope of the claims of the present application, the procedures described in detail are illustrative of how cells including microrough current collectors (including those within the restricted claims of the present patent as granted) may be produced. Comparative Example 1 A cell was produced by first forming a cathode mixture including 45% by weight V 6 O 13 , 4% carbon and 51% of an electrolyte including 70% propylene carbonate, 3% polyethylene oxide, 6% LiCF 3 SO 3 and 21% of a radiation curable acrylate. This mixture was coated onto a 15 µm thick solid nickel foil current collector to a thickness of about 75 µm having a surface area of about 32cm 2 . The above defined electrolyte was then coated onto the cathode to a thickness of about 50 µm. A 100 µm thick lithium foil was then laminated onto the electrolyte and the entire structure was subjected to electron beam radiation to cure the cathode and electrolyte. The initial cell impedance at 1 Hz was measured to be about 110 ohms. Example 2 A cell having the identical cathode, electrolyte and anode of Comparative Example 1 was produced by using a 35 µm thick nickel foil current collector having a surface area of about 32cm 2 which was etched to provide a roughened surface. The measured impedance at 1 Hz was 12 ohms. Comparative Example 3 A cell was prepared identical to the cell of Comparative Example 1 with the exception that the cathode contained 53% V 6 O 13 , 8% carbon and 39% electrolyte. The measured cell impedance at 1 Hz was 150 ohms. Example 4 A cell having the identical cathode, electrolyte and anode of Comparative Example 3 was produced using the current collector of Example 2. The measured impedance at 1 Hz was 5 ohms. Example 5 The cell of Comparative Example 3 was discharged at 200 µA/cm 2 at room temperature to lower the voltage from 3 V to 1.5 V. The discharge time was 15 hours. Example 6 The experiment of Example 5 was repeated using the cell of Example 4. The discharge time was 17.5 hours. Example 7 In an inert, nitrogen environment, a cathode composition is prepared by grinding 300 parts of V 6 O 13 for 24 to 48 hours in the presence of an equal amount of tetrahydrofuran in a one liter ball mill using 1.25 cm diameter ceramic balls. After grinding, the average particle size of V 6 O 13 is about 1.5 µm. The slurry is transferred to an airtight mixer and 46.2 parts of predried carbon are added to the mixer to produce a slurry having a weight ratio of V 6 O 13 to C of about 6.5 to 1. The mixture is stirred at low speed (20 rpm) under vacuum and heat, until the tetrahydrofuran is evaporated. The overall water content of the mixture is less than 100 ppm. 3 parts of polyethylene oxide (PEO) having a molecular weight greater than 100,000 is added to the V 6 O 13 /C powder mixture. The mixture is stirred for about 10 to 20 minutes to adequately disperse the polyethylene oxide. Propylene carbonate (PC), polyethylene glycol diacrylate (PEGDA) , and trimethylolpropane ethoxylated triacrylate (TMPEOTA) are added to the mixture to produce a mixture having the following components: component percent (weight) V 6 O 13 45 C 7 PC 37 PEO 1 PEGDA 8.5 TMPEOTA 1.5 The mixture temperature is increased to 65°C and the mixture is stirred at low speed for 20 minutes. The speed of the mixer is increased to 75 rpm and the mixture is stirred for 2 to 3 additional hours. The mixture is then coated onto a 5cm x 20cm x 25 µm high surface treated nickel foil available from Fukuda Metal Foil & Powder Co. Ltd. of Kyoto, Japan by utilizing a doctor blade technique at 50-60°C in a completely inert (nitrogen) environment containing less than 25 ppm water. The thickness of the cathode layer is 75 µm and the cathode layer is then covered with a stainless steel foil. A 2 inch (5.08cm) diameter, 10 inch (25.4cm) long stainless steel roller is placed on top of the foil and the roller is rolled along the length of the foil at a pressure of 5-10 Kg.wt./ cm 2 (4.9 to 9.8 x 10 5 N/m 2 ) to improve adherence of the cathode layer to the current collector. The assembly is then irradiated with a 3 Mrad dose of radiation by utilizing an electron beam source to cure the cathode layer. The foil is then peeled off of the cathode layer. The impedance of the cathode is less than 50 ohm/cm 2 . An electrolyte is prepared by mixing together the following components in the following weight fractions: component percent (weight) PC 68 LiAsF 6 18 PEO 2.5 PEGDA 9.2 TMPEOTA 2.3 The overall water concentration of the electrolyte is less than 50 ppm. The electrolyte is coated onto the cathode layer by using a doctor blade at room temperature to a thickness of about 25 µm. The electrolyte is then irradiated with a 3 Mrad dose of radiation from an electron beam source. The impedance of the electrolyte layer is about 0.8 ohm/cm 2 . A 4cm x 12.5cm x 125 µm thick lithium strip (lithium metal/battery grade) available from Lithco of Bessemer City, NC is applied to one end of the electrolyte layer and the lithium strip is adhered to the layer by applying pressure from a 2 inch (5.08cm) diameter, 10 inch (25.4cm) long roller at 5-10 Kg.wt/cm 2 (4.9 to 9.8 x 10 5 N/m 2 ) across the entire lithium surface. The opposite end of the electrolyte/cathode/current collector assembly is folded over the anode layer to form a bifaced cell. Copper tabs were spot welded to the current collector and pressure rolled onto the lithium foil to form electrodes for connection to a device. The physical and mechanical properties of the produced battery were as follows: property value surface area 100 cm 2 volume 2 cm 3 capacity 250 mAh average voltage 2.4 V discharge time (50 mA drain) 5 hours discharge time (250 mA drain) 0.5 hours discharge time (10 A pulses) 1.5 minutes energy density 300 wh/l overall impedance 150 ohm/cm 2

Claims: A solid state laminar electro chemical cell comprising: an alkali metal anode layer, a solid ionically conductive electrolyte layer, a cathode composition layer, and a current collector, said electrolyte layer being interposed between said alkali metal anode layer and said cathode composition layer, and said cathode composition layer being interposed between said electrolyte layer and said current collector; characterized in that said current collector has a microroughened surface and the cathode composition is at least partially cured in contact with said microroughened surface to cause it to tightly adhere thereto; and in that said microroughened surface is provided in the form of: (i) a polymeric substrate with either an electroconductive ink discontinuously coated thereon, or a first layer of vapour deposited copper film and a second layer of electrodeposited nickel particles overcoating the first layer, (ii) a metal, which term includes carbon, or polymeric substrate having metal, which term includes carbon, particles deposited thereon, except that when the substrate is other than carbon, the deposited particles are carbon, (iii) a smooth surface rendered microrough by removal of material therefrom other than by etching, or (iv) a smooth surface treated by contact with a patterned surface to microroughen it. A cell according to Claim 1, further characterized in that said anode layer comprises lithium foil, a metal foil coated with a layer of lithium or a lithium alloy.. A cell according to Claims 1 or 2, further characterized in that said metal is selected from carbon, copper, aluminium, nickel, steel, lead, iron and combinations thereof. A cell according to Claim 1, further characterised in that said polymeric substrate is selected from polyethylene, polyethylene terephthalate and polyvinyl chloride. A cell according to Claim 4, further characterised in that said substrate comprises polyethylene terephthalate with a first layer of vapour deposited copper film and a second layer of electrodeposited nickel particles overcoating the first layer. A cell according to any preceding claim, further characterised in that said electrolyte layer comprises a layer of an ionizable alkali metal salt or an alkaline earth salt, an inert liquid solvent for said salt and a polymerizable material. A cell according to Claim 6, further characterised in that said salt is a salt of a metal cation selected from Li + , Na + , K + , Mg 2+ , Ca 2+ and NH 4 + , and an anion selected from I - , Cl0 4 - , BF 4 - , AsF 6 - , PF 6 - , CF 3 SO 3 - , CF 3 CO 3 - , B 12 H 12 2- , B 10 Cl 10 2- , and BØ 4 - , where Ø is C 6 H 5 , an alkyl chain or an aryl chain, said salt cation and said salt anion being maintained in stoichiometric amounts. A cell according to any preceding claim, further characterised in that said cathode composition comprises an intercalation compound, an electrically conductive filler and an ionically conductive electrolyte. A cell according to Claim 8, further characterised in that said intercalation compound comprises V 6 O 13 , said electrically conductive filler comprises carbon particles and said ionically conductive electrolyte of said cathode composition comprises a solution of an ionizable alkali metal salt or alkaline earth salt and an inert liquid solvent for said salt, and a polymerizable material.

Inventors: FATEUX DENIS, SHACKLE DALE R, FATEUX, DENIS, SHACKLE, DALE R.
Applicants: MHB JOINT VENTURE
Application year: 1990
Main classification: H01M4
IPC codes: H01M4, H01M6, H01M10