REMOVAL OF SULPHIDES

Abstract: This invention relates to a composition suitable for use in process for the removal of sulphides, especially hydrogen sulphide from a feed contaminated therewith. The composition comprises an aqueous solution of a chlorite and a corrosion inhibitor which is an amphoteric ammonium compound of the formula as herein defined. The inhibitor mitigates problems of corrosion associated with chlorite scavengers.

Description: The present invention relates to a process for the removal of sulphides, especially hydrogen sulphide present in a crude oil or hydrocarbon feed contaminated therewith during production or processing of said feed or in water separated from said feed. Sulphides in general and hydrogen sulphide in particular is an undesirable by-product of crude oil production. These sulphides are toxic, have an obnoxious odour and, in the case of wet hydrogen sulphide, is highly corrosive to carbon steel. R.N. Tuttle et al describe the corrosive aspects of hydrogen sulphide in relation to high strength steels in "H₂S corrosion in Oil and Gas Production", National Association of Corrosion Engineers, 1981. In view of the above various commercial processes of removing hydrogen sulphide are used as add-on "sweetening" units for the treatment of the so called "sour" crudes. Such "sweetening" units of plants are, however, unattractive due to space or weight limitations especially on off-shore installations. Moreover, the economics of such units are often unfavourable. Attempts have been made to develop a chemical injection formulation which would react rapidly with the sulphides without giving rise to any undesirably side-effects. Most of the systems of this type now available are based on chlorine or peroxide chemistry. Unfortunately these chemicals are invariably strong oxidising agents and are also fairly corrosive to carbon steels, especially if the oxidising agent is present in excess of the amount required to react with the sulphide contaminant. Hence additional corrosion inhibitors may have to be incorporated in such systems to mitigate the corrosive effects of the additive. One of the most successful chemical species that has been investigated as a sulphide scavenger is a chlorite (including chlorine dioxide). Products based on this active species have been shown both in the laboratory and when used on oil production platforms to react quickly and efficiently with any hydrogen sulphide present. The chemical reaction of chlorite with hydrogen sulphide is given below: Cl0₂⁻ + 2H₂S = Cl⁻ + 2H₂0 + 2S However, the use of chlorite and its salts or chlorine dioxide on their own causes the corrosivity of the produced fluids to increase markedly especially when used at an injection rate over and above that required to react with all the hydrogen in such systems to mitigate this undesirable effect. This must be added separately since most of the commonly-used corrosion inhibitors are either incompatible with chlorite due to its very strong oxidising potential or form insoluble precipitates or cannot be used offshore for environmental reasons e.g. Cr salts. It has now been found that most of the above problems can be mitigated using specific scavengers which either react with or otherwise render the sulphide contaminent harmless. Accordingly, the present invention is a composition suitable for use as a sulphide scavenger, said composition comprising an aqueous solution of a chlorite and a corrosion inhibitor, characterised in that the corrosion inhibitor is an amphoteric compound of the formula wherein each of R₁, R₂ and R₃ is the same or different group selected from H, C₁-C₂₄ alkyl, aryl, halogen, hydroxy, alkoxy, carbonylic and a heterocyclic group formed by a combination of at least two of R₁, R₂ and R₃ and the nitrogen atom, said heterocyclic group optionally containing additional heteroatoms, R₄ is a carboxylic or a sulphonic acid group, and n has a value from 1-9. The sulphide contaminant to be scavenged may be present in liquid or gaseous streams or in storage tanks forming part of a chemicals processing plant, e.g. crude oil processing. The contaminant may be present, for instance, in (i) a crude oil feed which is either in an untreated virgin state as recovered from an oil well, or (ii) a feed that has undergone one or more preliminary treatment stages, whether physical or chemical, prior to any cracking step to which the crude oil is subjected, or (iii) an aqueous feed derived as a by-product of chemical manufacturing including crude oil recovery, whether or not associated with crude oil recovered from an oil well. Thus, for example the feed may be crude oil derived or recovered directly from the well or that at any stage immediately prior to the gas/oil separation step, whether or not associated with water. The most common volatile sulhpide found as contaminant in such feeds is hydrogen sulphide. The type of chlorite used may be any chlorite which is soluble in water. Thus, the chlorites are suitably alkali metal chlorites, preferably sodium chlorite. The amount of the chlorite present in the composition will depend upon the extent to which the sulphide contaminant is to be removed. The precise amount used would depend upon the nature of the sulphide to be removed and the type of feed. Thus for full removal of the sulphide contaminant in a feed, the chlorite is preferably used in an amount of at least 0.5 moles per mole of the sulphide contaminant to be removed. The substituent groups in the amphoteric compounds of formula (I) are suitably such that they are resilient to oxidation by the chlorite component in the composition. Thus in the amphoteric compounds of formula (I) R₁ and R₃ are suitably C₁-C₄ alkyl groups, preferably CH₃; R₂ is suitably a C₁₀-C₁₅ alkyl group, preferably C₁₂-C₁₄ alkyl group; R₄ is suitably a -C00- group; and n is suitably 1-4, preferably 1-2. If two or more of the groups R₁, R₂ and R₃ form a heterocyclic ring with the nitrogen atom of the amphoteric compound, the ring so formed is suitably an imidazoline ring. The amphoteric compound used is most preferably an alkyl betaine, especially lauryl betaine. The relative proportions of the chlorite and the ampholeric compound in the composition is suitably in the range of 1:0.1 to 1:0.9 w/w respectively, preferably 1:0.4 to 1:0.7 w/w. The compositions of the present invention are preferably used as aqueous solutions. However, such solutions may optionally contain a water-miscible secondary solvent, e.g. an alcohol or a glycol to enhance the freeze-thaw properties of the composition. The treatment of the contaminated feed with the compositions of the present invention can be effected at temperatures ranging from below ambient to about 150°C. The scavenger formulations of the present invention are particularly effective in treating wet crude oil, i.e. crudes containing 5 - 95% w/w water and containing hydrogen sulphide at levels of 1 - 1000 ppm at a temperature e.g. in the range from 15-60°C and a pH e.g. in the range of 4.0-6.9. These formulations are substantially free of any corrosive effects under these conditions. A feature of the present inventions is that the use of these scavenger formulations have significant advantages over those used hitherto: For instance these compositions are: i) Easy to use and transport offshore ii) Effective in the wide variety of conditions seen offshore iii) Fast reacting iv) Non-corrosive by-products v) Cost effective vii) Environmentally acceptable The present invention is further illustrated with reference to the following Examples. CORROSION RATE MEASUREMENTS Corrosion rate measurements were performed using LPR (linear polarisation resistance) method. A rig was constructed from polytetrafluroethylene (PTFE), nylon and silicone rubber. The rig contained two separate corrosion cells, connected in series but some distance apart. Each cell contained three concentric, mild steel electrodes, 8.6cm² surface area, with PTFE spacers. A multichannel peristaltic pump controlled the addition of all the chemicals through the rig. Concentrations of the various reactants were adjusted to give the desired final concentration of sulphide and scavenger composition in the flowing stream. A flow rate of 45 to 50cm³/min (total fluids) was set. Deareated saline water (4.3% NaCl) buffered to a pH of 4.8 with NaHCO₃ and CO₂ was treated with 35 to 40ppm w/w (in fluid) of H₂S. Corrosion rate measurements were continuously monitored at the point of injection, cell A, and further downstream, cell B. In this way the most corrosive environment (highest excess of oxidising agent) and the least corrosive environment (dynamic equilibrium of reactants) were obtained. Sample points of the untreated and the treated H₂S stream enabled assessment of the efficiency of the H₂S scavenging reaction (Iodimetric analysis, see Vogel's Textbook of Quantitative Inorganic Analysis, 4th Edition, Longmans). The effect of the injection of a solution that contains only sodium chlorite is shown in Table 1. The corrosion rate does not increase above that of the background until the level of the scavenger equals that required to react with all the hydrogen sulphide at this concentration the corrosion rate in the injection cell increases significantly although the downstream corrosiveness is still that of the background. Above this concentration the corrosion rate increases to unacceptable levels. In contrast, Table 2 shows that by incorporating a betaine into the formulation the corrosion rate is controlled to less than 30 mpy even when the injection rate is double that required to react with all the hydrogen sulphide. The above experiments were carried out at ambient temperatures (15-20°C) and atomspheric pressures (at sealevel but these conditions are rarely seen in real processes occuring offshore, for this reason we undertook some experiments unsing autoclave to investigate the effect of higher temperatures (60°C) and pressures (3 bar). The results from these experiments are summarised in Table 3 where the scavenger is again added at twice the concentration required to react with all the hydrogen sulphide. In the absence of the corrosion inhibitor (NaClO₂ only) the corrosion rate increases to 86 mpy. In comparison, the incorporation of alkyl betaine (present as 17% w/v in the stock chlorite solution (25% w/v)) lowers this corrosion rate to near that of the original solution. This validates the results of earlier experiments. HYDROGEN SULPHIDE REMOVAL EFFICIENCIES Chlorite has been tested with and without lauryl betaine to investigate the influence if any of the corrosion inhibitor on the hydrogen sulphide scavenging ability of the product. Hydrogen sulphide was generated in situ in a sealed vessel containing brine (92cm³ of 4% NaCl, 0.1% NaHCO₃) and stabilised crude oil (10cm³ of forties crude), by injection of an aqueous Na₂S solution (2.6cm³ of 0.029M) and sulphuric acid (5.6cm³ of 0.05m). The resultant pH was 6.2 to 6.4. The H₂S scavenger was introduced into the flask and after a predetermined time interval the residual H₂S was determined by injection of 100cm³ of air through the solution and vented via a Drager tube. Experiments were all conducted at ambient temperatures. Typical results are given in Table 4. This table clearly shows that the acitivity of the chlorite is not comprised by the addition of the corrosion inhibitor. HYDROGEN SULPHIDE REMOVAL EFFICIENCIES Chlorite has been tested with and without lauryl betaine to investigate the influence if any of the corrosion inhibitor on the hydrogen sulphide scavenging ability of the product. Hydrogen sulphide was generated in situ in a sealed vessel containing brine (92cm³ of 4% NaCl, 0.1% NaHCO₃) and stabilised crude oil (10cm³ of forties crude), by injection of an aqueous Na₂S solution (2.6cm³ of 0.029M) and sulphuric acid (5.6cm³ of 0.05m). The resultant pH was 6.2 to 6.4. The H₂S scavenger was introduced into the flask and after a predetermined time interval the residual H₂S was determined by injection of 100cm³ of air through the solution and vented via a Drager tube. Experiments were all conducted at ambient temperatures. Typical results are given in Table 4. This table clearly shows that the acitivity of the chlorite is not compromised by the addition of the corrosion inhibitor.

Claims: A composition suitable for use as a sulphide scavenger, said composition comprising an aqueous solution of a chlorite and a corrosion inhibitor, characterised in that the corrosion inhibitor is an amphoteric compound of the formula: wherein each of R₁, R₂ and R₃ is the same or different group selected from H, C₁-C₂₄ alkyl, aryl, halogen, hydroxy, alkoxy, carbonylic and heterocyclic group formed by a combination of at least two of R₁, R₂ and R₃ and the nitrogen atom, said heterocyclic group optionally containing additional heteroatoms, R₄ is a carboxylic or a sulphonic acid group, and n has a value from 1-9. A composition according to Claim 1 wherein the chlorite is an alkali metal chlorite. A composition according to Claim 1 or 2 wherein the chlorite is present in an amount of at least 0.5 moles per mole of the sulphide contaminant to be removed. A composition according to any one of the preceding Claims wherein the substituent groups in the amphoteric compound of formula (I) are resilient to oxidation by the chlorite component in the composition. A composition according to any one of the preceding Claims wherein in the amphoteric compound of formula (I), R₁ and R₃ are C₁-C₄ alkyl groups, R₂ us a C₁₀-C₁₅ alkyl groups and R₄ is a -C00- group and n has a value from 1-4. A composition according to any one of the preceding Claims wherein R₁, R₂ and R₃ in the amphoteric compound are such that together they represent either an imidazoline ring or an alkyl betaine. A composition according to Claim 6 wherein the amphoteric compound is lauryl betaine. A composition according to any one of the preceding Claims wherein the relative proportions of the chlorite and the amphoteric compound are from 1 : 0.1 to 1 : 0.9 w/w respectively. A process for the removal of sulphide contaminant in a feed comprising liquid or gaseous streams or in storage tanks forming part of a chemicals processing plant, said process comprising contacting the feed with a composition as claimed in Claim 1 at a temperature ranging from ambient to 150°C. A process according to Claim 9 wherein the contaminated feed is a wet crude containing 5-95% w/w water and 1-1000ppm hydrogen sulphide, said feed being contacted at a pH of 4.0-6.9 and at a temperature from 15-60°C with a composition according to Claim 1.

Inventors: HOWSON, MARK, ROY
Applicants: BAKER-HUGHES INCORPORATED
Application year: 1990
Main classification: C10G27
IPC codes: C10G27