Sintered body of silicon nitride and a process for making the same

Abstract: A sintered body composed of α′-silicon nitride and β′-silicon nitride, and having a surface portion which contains a greater proportion of α′-silicon nitride than its inner portion does. It has high strength and excel­ lent wear resistance. It is produced by preparing a molded body from a sintering material, disposing about the molded body a sintering material which can form a sintered product containing a greater proportion of α′-silicon nitride than the sintered product of the molded body will, and sintering the molded body and the material disposed about it.

Description: This invention relates to a sintered body composed of α'-silicon nitride and β'-silicon nitride, and having high strength and high resistance to wear, such as erosive wear, and a process for making the same. A sintered body of silicon nitride (Si₃N₄) has come to be used for making gas turbine parts, heat exchangers, bearings, etc. because of its high strength, thermal shock resistance, and corrosion resistance. A rapidly rotating body, such as a gas turbine blade, is, however, worn by, for example, dust floating in the air. For example, a plant using coal is seriously worn by the dust of coal. A sintered body of Si₃N₄ has also come to be used for making tools for cutting heat-resisting alloys, or other tools required to have a high level of wear resistance. A known sintered body consisting mainly of β-Si₃N₄ is, however, too low in hardness to exhibit a high degree of wear resistance. It is known that a high degree of hardness is a highly desirable factor for any material to be able to exhibit excellent resistance to erosion and other wear. Silicon nitrides of the type in which various elements form solid solutions, which are generally known as sialons, have come to draw attention because of their high hardness. One example is α'-Si₃N₄ (or α-sialon ) which occurs when Al replaces Si, while O replaces N, in the crystal lattice of α-Si₃N₄, and another element, such as Li, Mg, Ca or Y, occupies the interstices of the lattice. It is represented by the general formula: M x (Si,Al)₁₂(O,N)₁₆ where M is at least one of such elements as Li, Mg, Ca and Y, and 0 < x ≦ 2. Another example is β'-Si₃N₄ (or β-sialon ) which is formed by the replacement of Si by Al, and of N by O, in the crystal lattice of β-Si₃N₄, and which is represented by the general formula: Si 6-z Al z O z N 8-z where 0 < z ≦ 4.2. Although α'-Si₃N₄ is superior to β'-Si₃N₄ in hardness and wear resistance, it is inferior in toughness and strength. Therefore, a sintered body composed of α'-Si₃N₄, β'-Si₃N₄ and a bonding phase has been developed to provide a material which is excellent in both wear resistance and strength, as disclosed in Japanese Patent Publications Nos. 8074/1988 and 8075/1988. This material is, however, still unsatisfactory in strength, as it contains a relatively large amount of bonding phase. Under these circumstances, it is an object of this invention to provide a sintered body of silicon nitride having high strength, as well as excellent wear resistance. It is another object of this invention to provide a process which can make a sintered body of silicon nitride having high strength, as well as excellent wear resistance. The sintered body of this invention is composed of α'-silicon nitride and β'-silicon nitride, and contains a greater proportion of α'-silicon nitride in its surface portion than in its inner portion. It has high strength and excellent resistance to wear, particularly erosive wear. Its wear resistance is due to the presence of a greater proportion of hard α'-silicon nitride in its surface portion, and also to the fact that its surface portion is composed of the same type of crystal phase as its inner portion and is, therefore, very unlikely to peel off. Its strength is manifested by its inner portion which is composed of α'-silicon nitride and β'-silicon nitride. The process of this invention comprises the first step of preparing a molded body of a material which can form a sintered body composed of α'-silicon nitride and β'-silicon nitride, and the second step of disposing about the molded body a material which can form a sintered body composed of α'-silicon nitride and β'-silicon nitride, but containing a greater proportion of α'-silicon nitride than the sintered product of the molded body will, and sintering the molded body and the material disposed about it. The process of this invention can make a sintered body of silicon nitrides having high strength and excellent wear resistance. As the material disposed about the molded body is sintered with it, it forms a surface layer which does not readily peel off or crack, as opposed to a surface layer formed by coating a sintered body. These and other objects, features and advantages of this invention will become more apparent from the following description and the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS FIGURE 1 is a graph showing the four-point bending strength at room temperature and erosive wear of sintered bodies obtained in the Examples as will hereinafter be described; and FIGURES 2 and 3 are photographs taken through a transmission electron microscope and showing the crystal structures of the surface and inner portions, respectively, of a sintered body embodying this invention. DETAILED DESCRIPTION OF THE INVENTION The sintered body of this invention is composed of α'-silicon nitride and β'-silicon nitride, and contains a greater proportion of α'-silicon nitride in its surface portion than in its inner portion. Its surface portion may even be free of any β'-silicon nitride. α'-silicon nitride (α'-Si₃N₄) is a compound which occurs when Al replaces Si, while O replaces N, in the crystal lattice of α-Si₃N₄, and at least one of other elements, such as lithium (Li), magnesium (Mg), calcium (Ca) and yttrium (Y), occupies the interstices of the lattice. It has the general formula M x (Si,Al)₁₂(O,N)₁₆, where M is at least one of such elements as Li, Mg, Ca and Y, and 0 < x ≦ 2, and is generally called α-sialon. β'-silicon nitride (β'-Si₃N₄) is a compound which is formed by the replacement of Si by Al, and of N by O, in the crystal lattice of β-Si₃N₄. It has the general formula Si 6-z Al z O z N 8-z , where 0 < z ≦ 4.2, and is generally called β-sialon. Preferred compositions for the silicon nitrides are obtained when 0 < x ≦ 0.3, and 0 < z ≦ 1.0, respectively. The preferred proportions of the silicon nitrides in the sintered body are such that in its inner portion, α'-Si₃N₄ has a value of 0.05 to 0.50, while β'-Si₃N₄ has a value of 0.50 to 0.95, as expressed by the ratio of their peak strength revealed by X-ray diffraction, and such that α'-Si₃N₄ has a proportion which is higher by a value of 0.05 to 0.2 in the surface portion of the sintered body than in its inner portion. A sintered body containing a higher proportion of α'-Si₃N₄ in its surface portion has an undesirably lower strength, while no sintered body containing a lower proportion thereof in its surface portion is expected to exhibit any improved wear resistance. The values as hereinabove used to define the proportions of the silicon nitrides are obtained by making the sum of the highest and the second highest peak strength revealed by the X-ray diffraction of each compound, and comparing the sums obtained for the two compounds. The greater proportion of α'-Si₃N₄ in the surface portion of the sintered body than in its inner portion may be achieved by providing separate surface and inner portions having different proportions of the silicon nitride (i.e., forming a separate surface layer), or by preparing a single mass having a proportion of the nitride varying continuously from its interior to its surface. It is alternatively possible to prepare a body composed of an inner portion, a surface layer and at least one intermediate layer disposed between the inner portion and the surface layer and having a nitride proportion lying between the proportions of the nitride in the inner portion and the surface layer. When a surface layer is formed, it is recommended that its thickness including that of the intermediate layer or layers, if any, be approximately in the range of 200 to 500 µm (microns). It is preferable to use α'-Si₃N₄ composed of spherical crystal grains having an average diameter not exceeding 2.0 µm (microns), and more preferably not exceeding 1.0 µm (micron). It is also preferable to use β'-Si₃N₄ composed of elliptically spherical crystal grains having an average long diameter not exceeding 5.0 microns, and more preferably not exceeding 2.5 microns, and an average short diameter not exceeding 1.0 micron, and more preferably not exceeding 0.5 micron. The grains having these ranges of diameters are so fine as to ensure the manufacture of a sintered product having a very large internal defect and therefore a greatly improved strength. The sintered product of this invention may contain as a third component any of various heat-resisting substances, such as oxides, nitrides, carbides, silicides, borides and sulfides, depending on the purpose for which the sintered product is intended. Moreover, any sintering assistant used in the sintering process may remain in the sintered product. The sintered body of this invention may also have a surface layer formed by, for example, coating the surface of its inner portion with an appropriate material. The excellent properties of the sintered product according to this invention as hereinabove described make it very useful as a material for machine parts exposed to high temperatures, parts of a chemical plant, bearings and other mechanical parts required to have a high level of wear resistance, parts of a gas turbine, a heat exchanger, etc. The process of this invention comprises the first step of preparing a molded body of a material which can form a sintered body composed of α'-Si₃N₄ and β'-Si₃N₄, and the second step of disposing about the molded body a material which can form a sintered body composed of α'-Si₃N₄ and β'-Si₃N₄, but containing a greater proportion of α'-Si₃N₄ than the sintered product of the molded body will, and sintering the molded body and the material disposed about it. The material used in the second step forms the surface portion of the product of the process. The material used for preparing a molded body in the first step of the process consists of a material which can form α'-Si₃N₄ when heated for sintering, and a material which can form β'-Si₃N₄ when heated. The same may be true with the material used in the second step. The material which can form α'-Si₃N₄ when heated is one which can form α'-Si₃N₄ in the sintered product. It may consist of α'-Si₃N₄ itself, or a mixture of substances which react together at a sintering temperature to form α'-Si₃N₄, or both. Examples of the mixture of substances which react together to form α'-Si₃N₄ are the mixtures of Si₃N₄, AlN and Y₂O₃; Si₃N₄, AlN, Al₂O₃ and Y₂O₃; and Si₃N₄, Al₂O₃, Y₂O₃ and YN. All of these are the mixtures which can be used to form α'-Si₃N₄ containing yttrium in a solid solution. The material which can form β'-Si₃N₄ when heated is one which can form β'-Si₃N₄ in the sintered product. It may consist of β'-Si₃N₄ itself, or a mixture of substances which react together at a sintering temperature to form β'-Si₃N₄, or both. Examples of the mixture of substances which react together to form β'-Si₃N₄ are the mixtures of Si₃N₄ and Al₂O₃; Si₃N₄, AlN and Al₂O₃; and Si₃N₄, Al₂O₃ and SiO₂. A mixture of substances which can be used to form α'-Si₃N₄ as a reaction product when heated can be used to form not only α'-Si₃N₄, but simultaneously β'-Si₃N₄ as well, if the proportions of the substances in the mixture are appropriately controlled. For example, α'-Si₃N₄ containing yttrium in a solid solution and β'-Si₃N₄ can be formed simultaneously if the proportions of Y₂O₃ and AlN, or Y₂O₃, AlN and Al₂O₃, or YN and Al₂O₃, relative to Si₃N₄ are appropriately controlled, as α'-Si₃N₄ is formed by the solution of Y, Al and O in Si₃N₄, and β'-Si₃N₄ by the solution of Al and O. A mixture having one and the same composition can be used to produce sintered bodies containing different proportions of α'-Si₃N₄ and β'-Si₃N₄ if the sintering temperature and time are appropriately altered. It is possible to obtain a sintered body comprising α'-Si₃N₄ and β'-Si₃N₄ each having two or more different compositions, which occur when each of x and z in the general formulas as hereinabove given represents two or more different values. This is possible by employing a powder having a wide particle size distribution as each of the materials for forming α'- and β'-Si₃N₄, respectively, when heated, or by using two or more powders of each of α'- and β'-Si₃N₄ having different compositions. When the material of a sintered body of Si₃N₄ is composed of a powder of Si₃N₄ and sintering agent, it is preferable to use the powder of Si₃N₄ in which the total amount of oxygen is at most 2 weight % and the amount of oxygen which exists as silicon oxide in the surface portion thereof is not less than 40% of the total amount of oxygen. This will prevent the excessive growth of crystal grains of Si₃N₄, thereby providing very fine crystal grains. As a result, the sintered body of Si₃N₄ with high strength can be achieved. The above-mentioned material of a sintered body of Si₃N₄ is used as a material for forming an inner and/or a surface portion of the sintered body. In the first step of the process, the molded body can be prepared by any of a variety of known methods, such as pressing in a metal or rubber mold, extrusion, slip casting and injection molding. In the second step of the process, the material as hereinabove described is disposed about the molded body which has been prepared in the first step (hereinafter referred to as the inner body), and the whole is sintered. The material used in the second step is of such composition that a sintered product thereof may contain a greater proportion of α'-Si₃N₄ than a sintered product of the inner body. The material can also be of such composition that a sintered product thereof consists solely of α'-Si₃N₄. The material can be disposed about the inner body if it is caused to adhere to the surface of the inner body, or if the inner body is embedded in the powder of the material. Dipping in a slip, spraying, or electrical deposition can, for example, be employed for causing the material to adhere to the surface of the inner body. A plurality of powders having different compositions can be disposed in one layer upon another on the inner body to produce a sintered body having a proportion of α'-Si₃N₄ varying continuously or in steps from its interior to its surface. Either pressure or pressureless sintering may be employed. More specifically, normal, or gas pressure sintering, or hot isostatic press (HIP) sintering can, for example, be employed. The sintering is preferably carried out in an inert gas atmosphere, such as nitrogen or argon gas, or in a nonoxidizing atmosphere, as in a vacuum. A sintering temperature of 1650°C to 1900°C is recommended. The use of any temperature lower than 1650°C results in a product which has not satisfactorily been densified, while the excessive growth of grains occurs at any temperature over 1900°C. In either event, the sintered product fails to exhibit a satisfactorily high strength. It is possible to achieve the intended proportions, crystal grain sizes and compositions of the two types of silicon nitrides in the sintered body if the mixing ratio of the materials for forming the silicon nitrides when heated, and the sintering conditions are appropriately altered. The invention will now be described more specifically with reference to several examples and comparative examples. EXAMPLE 1 A powder of Si₃N₄ having an alpha ratio of at least 95% and an average particle diameter of 1.0 µm (micron) was mixed with 2 to 7% by weight of a powder of AlN having an average particle diameter of 0.5 micron and 1.5 to 5% by weight of a powder of Y₂O₃ having an average particle diameter of 0.8 micron. The mixture was molded in a metal press into a body measuring 4 mm by 6 mm by 45 mm and an isostatic pressure of 294 MPa (3000 kg/cm²) was applied to the molded product. The molded body was embedded in a powder of Si₃N₄ containing a greater proportion of AlN and Y₂O₃ than the molded body did, or in a powder of α'-Si₃N₄. The whole was sintered at a temperature of 1650°C to 1900°C and normal pressure for 0.5 to 10 hours in a nitrogen gas atmosphere. The sintered product was analyzed by X-ray diffraction for the proportions of α'- and β'-Si₃N₄ of which it was composed. The analysis was first made of its surface. Then, a layer having a thickness of several tens of microns was removed by grinding from its surface and the exposed surface was likewise analyzed. This process of grinding and analysis was repeated several times. In any event, the proportions of the two types of silicon nitrides were determined by comparing the sum of the two highest peak strength values marked by one type of silicon nitride in a chart obtained by the X-ray diffraction of the sintered product and the sum of the two highest peak strength values marked by the other type of silicon nitride. The process of sintering and analysis as hereinabove described was repeated for preparing eight samples of sintered products embodying this invention and determining the proportions of the two types of silicon nitrides in each product. The samples are shown as Samples Nos. 1 to 8 in Table 1 below, in which the results of the analysis are also shown. Each value showing the proportion of α'-Si₃N₄ in Table 1 is that which occurs when the values showing the proportions of the two types of silicon nitrides make a total of 1. In Table 1, the surface portion means a portion from the surface of a sintered product to a depth of 200 to 300 microns below it. As is obvious from Table 1, every sample according to this invention was found to contain α'-Si₃N₄ in its surface portion in a proportion of 0.2 or less greater than in its inner portion. Comparative samples, which are shown as C1 to C5, in Table 1, were prepared by following the process which had been employed for preparing the samples of this invention, except that each molded body was embedded in the same powder as that from which it had been molded. The analysis was also repeated and the results are shown in Table 1. Four of the comparative samples were found to contain equal proportions of α'-Si₃N₄ in the surface and inner portions thereof. The remaining sample, C2, was found to contain even a greater proportion of α'-Si₃N₄ in its inner portion than in its surface portion. Each sample was examined for four-point bending strength at room temperature after a layer having a thickness of about 100 microns had been removed by grinding from its surface. It was also tested for erosive wear with a SiC abrasive powder having an average particle size of 500 microns. The abrasive powder was caused to fly at a speed of 250 to 300 meters per second and strike against the sample surface at an angle of 80° thereto. The results of the bending and wear tests are shown in Table 1 and also in FIGURE 1. The numbers appearing in FIGURE 1 correspond to those of the samples which appear in Table 1. The solid line in FIGURE 1 was obtained by connecting the test results given by the comparative samples each containing an equal proportion of α'-Si₃N₄ in its surface and inner portions. As is obvious from Table 1 and FIGURE 1, the samples according to this invention were, as a whole, superior to the comparative samples in both strength and wear resistance. FIGURES 2 and 3 are the photographs taken through a transmission electron microscope and showing at a magnification of 20,000 the crystal structures of the surface and inner portions, respectively, of Sample No. 4 according to this invention. The photographs confirm the presence of more spherical particles of α'-Si₃N₄ in the surface portion than in the inner portion.

Claims: Claims for the following Contracting State : DE A sintered body comprising α' -silicon nitride and β'-silicon nitride, said sintered body having a surface portion which contains a greater proportion of said α'-silicon nitride than an inner portion thereof while said α'-silicon nitride in said surface portion has a proportion which is greater by a value of 0.05 to 0.2 than said proportion thereof in said inner portion. A sintered body as set forth in claim 1 wherein said α'-silicon nitride has the general formula M x (Si,Al)₁₂(O,N)₁₆ where M is at least one of the elements Li, Mg, Ca and Y, and O < x ≦ 2, while said β'-silicon nitride has the general formula Si 6-z Al z O z N 8-z where O < z ≦ 4.2. A sintered body as set forth in claim 2, wherein O < x ≦ 0.3 and O < z ≦ 1.0. A sintered body as set forth in any of claims 1 to 3, wherein said α'- and β'-silicon nitrides in said inner portion occupy a proportion of 0.05 to 0.50 and a proportion of 0.50 to 0.95, respectively, when each of said proportions is defined as the ratio of peak strengths revealed by X-ray diffraction. A sintered body as set forth in claim 1, wherein said surface layer comprises an outermost layer and at least one intermediate layer located between said outermost layer and said inner portion, and said proportion of α'-silicon nitride increases in the order of said inner portion, said intermediate layer and said outermost layer. A sintered body as set forth in any of claims 1 to 5, wherein said surface layer has a thickness of 200 to 500 µm (microns). A sintered body as set forth in any of claims 1 to 6, wherein said proportion of α'-silicon nitride shows a continuous increase from said inner portion to the surface of said surface portion. A sintered body as set forth in any of claims 1 to 7, wherein said α'-silicon nitride is composed of spherical crystal grains having an average diameter not exceeding 2.0 µm (microns), and said β'-silicon nitride is composed of elliptically spherical crystal grains having an average long diameter not exceeding 5.0 microns and an average short diameter not exceeding 1.0 micron. A sintered body as set forth in claim 8, wherein said average diameter does not exceed 1.0 µm (micron), said average long diameter does not exceed 1.0 µm (micron), and said average short diameter does not exceed 0.5 µm (micron). A process for making a sintered body of silicon nitrides comprising the steps of: preparing a molded body of a material which can form a sintered body composed of α'-silicon nitride and β'-silicon nitride; and disposing about said molded body a material which can form a sintered body composed of α'-silicon nitride and β'-silicon nitride, but containing a proportion of α'-silicon nitride of from 0.05 to 0.2 greater than the sintered product of said molded body will have, said proportion being defined as the ratio of peak strengths revealed by X-ray diffraction; and sintering said molded body and said material disposed about it. A process as set forth in claim 10, wherein said material which can form a sintered body composed of α'-silicon nitride and β'-silicon nitride comprises a material which can form α'-silicon nitride when heated at a sintering temperature, and a material which can form β'-silicon nitride when heated, and said material which can form α'-silicon nitride is at least one of α'-silicon nitride itself and a mixture of substances which react together to form α'-silicon nitride when heated, while said material which can form β'-silicon nitride is at least one of β'-silicon nitride itself and a mixture of substances which react together to form β'-silicon nitride when heated. A process as set forth in claim 11, wherein said mixture of substances which react together to form α'-silicon nitride is selected from a mixture of Si₃N₄, AlN and Y₂O₃, a mixture of Si₃N₄, AlN, Al₂O₃ and Y₂O₃ and a mixture of Si₃N₄, Al₂O₃, Y₂O₃ and AlN; and said mixture of substances which react together to form β'-silicon nitride is selected from a mixture of Si₃N₄ and Al₂O₃, a mixture of Si₃N₄, AlN and Al₂O₃ and a mixture of Si₃N₄, Al₂O₃ and SiO₂. A process as set forth in claim 10, wherein said material which can form a sintered body composed of α'-silicon nitride and β'-silicon nitride is a mixture of substances which react together to form both α'-silicon nitride and β'-silicon nitride when heated at a sintering temperature. A process as set forth in claim 13, wherein said mixture is at least one of a mixture of Si₃N₄, Y₂O₃ and AlN, a mixture of Si₃N₄, Y₂O₃, AlN and Al₂O₃ and a mixture of Si₃N₄, YN and Al₂O₃ having an appropriately controlled composition. A process as set forth in claim 10, wherein said material which can form a sintered body composed of α'-silicon nitride and β'-silicon nitride is selected from a mixture of a powder having a wide particle size distribution and capable of forming α'-silicon nitride when heated, and a powder having a wide particle size distribution and capable of forming β'-silicon nitride when heated, and a mixture of at least two powders of α'-silicon nitride having different compositions and at least two powders of β'-silicon nitride having different compositions. A process as set forth in claim 10, wherein said disposing is carried out by a method selected from causing said material to adhere to the surface of said molded body, and embedding said molded body in said material. A process as set forth in claim 10, wherein at least one of said materials in the first and second steps comprises a powder of silicon nitride and sintering agent, and said powder of silicon nitrides contains oxygen in the total amount of at most 2 weight %, the amount of oxygen existing as silicon oxide in the surface portion thereof being not less than 40 % of the total amount of oxygen. Claims for the following Contracting State : GB A sintered body comprising α'-silicon nitride and β'-silicon nitride, said sintered body having a surface portion which contains a greater proportion of said α'-silicon nitride than an inner portion thereof. A sintered body as set forth in claim 1, wherein said surface portion is composed solely of α'-silicon nitride. A sintered body as set forth in claim 1 or 2, wherein said α'-silicon nitride has the general formula M x (Si,Al)₁₂(O,N)₁₆ where M is at least one of the elements Li, Mg, Ca and Y, and 0 < x ≦ 2, while said β'-silicon nitride has the general formula Si 6-z Al z O z N 8-z where 0 < z ≦ 4.2. A sintered body as set forth in claim 3, wherein 0 < x ≦ 0.3, and 0 < z ≦ 1.0. A sintered body as set forth in any of claims 1 to 4, wherein said α'- and β'-silicon nitrides in said inner portion occupy a proportion of 0.05 to 0.50 and a proportion of 0.50 to 0.95, respectively, while said α'-silicon nitride in said surface portion has a proportion which is greater by a value of 0.05 to 0.2 than said proportion thereof in said inner portion, when each of said proportions is defined as the ratio of peak strengths revealed by X-ray diffraction. A sintered body as set forth in claim 1, wherein said surface portion comprises a surface layer which contains a greater proportion of α'-silicon nitride than said inner portion does. A sintered body as set forth in claim 6, wherein said surface layer comprises an outermost layer and at least one intermediate layer located between said outermost layer and said inner portion, and said proportion of α'-silicon nitride increases in the order of said inner portion, said intermediate layer and said outermost layer. A sintered body as set forth in claim 6 or 7, wherein said surface layer has a thickness of 200 to 500 µm (microns). A sintered body as set forth in claim 1, wherein said proportion of α'-silicon nitride shows a continuous increase from said inner portion to the surface of said surface portion. A sintered body as set forth in any of claims 1 to 9, wherein said α'-silicon nitride is composed of spherical crystal grains having an average diameter not exceeding 2.0 µm (microns), and said β'-silicon nitride is composed of elliptically spherical crystal grains having an average long diameter not exceeding 5.0 µm (microns) and an average short diameter not exceeding 1.0 µm (micron). A sintered body as set forth in claim 10, wherein said average diameter does not exceed 1.0 micron, said average long diameter does not exceed 1.0 micron, and said average short diameter does not exceed 0.5 micron. A process for making a sintered body of silicon nitrides comprising the steps of: preparing a molded body of a material which can form a sintered body composed of α'-silicon nitride and β'-silicon nitride; and disposing about said molded body a material which can form a sintered body composed of α'-silicon nitride and β'-silicon nitride, but containing a greater proportion of α'-silicon nitride than the sintered product of said molded body will, and sintering said molded body and said material disposed about it. A process as set forth in claim 12, wherein said material which can form a sintered body composed of α'-silicon nitride and β'-silicon nitride comprises a material which can form α'-silicon nitride when heated at a sintering temperature, and a material which can form β'-silicon nitride when heated, and said material which can form α'-silicon nitride is at least one of α'-silicon nitride itself and a mixture of substances which react together to form α'-silicon nitride when heated, while said material which can form β'-silicon nitride is at least one of β'-silicon nitride itself and a mixture of substances which react together to form β'-silicon nitride when heated. A process as set forth in claim 13, wherein said mixture of substances which react together to form α'-silicon nitride is selected from a mixture of Si₃N₄, AlN and Y₂O₃, a mixture of Si₃N₄, AlN, Al₂O₃ and Y₂O₃ and a mixture of Si₃N₄, Al₂O₃, Y₂O₃ and AlN; and said mixture of substances which react together to form β'-silicon nitride is selected from a mixture of Si₃N₄ and Al₂O₃, a mixture of Si₃N₄, AlN and Al₂O₃ and a mixture of Si₃N₄, Al₂O₃ and SiO₂. A process as set forth in claim 12, wherein said material which can form a sintered body composed of α'-silicon nitride and β'-silicon nitride is a mixture of substances which react together to form both α'-silicon nitride and β'-silicon nitride when heated at a sintering temperature. A process as set forth in claim 15, wherein said mixture is at least one of a mixture of Si₃N₄, Y₂O₃ and AlN, a mixture of Si₃N₄, Y₂O₃, AlN, and Al₂O₃ and a mixture of Si₃N₄, YN and Al₂O₃ having an appropriately controlled composition. A process as set forth in claim 12, wherein said material which can form a sintered body composed of α'-silicon nitride and β'-silicon nitride is selected from a mixture of a powder having a wide particle size distribution and capable of forming α'-silicon nitride when heated, and a powder having a wide particle size distribution and capable of forming β'-silicon nitride when heated, and a mixture of at least two powders of α'-silicon nitride having different compositions and at least two powders of β'-silicon nitride having different compositions. A process as set forth in claim 12, wherein said disposing is carried out by a method selected from causing said material to adhere to the surface of said molded body, and embedding said molded body in said material. A process as set forth in claim 12, wherein at least one of said materials in the first and second steps comprises a powder of silicon nitride and sintering agent, and said powder of silicon nitrides contains oxygen in the total amount of at most 2 weight %, the amount of oxygen existing as silicon oxide in the surface portion thereof being not less than 40% of the total amount of oxygen.

Inventors: UKYO YOSHIO, WADA SHIGETAKA, UKYO, YOSHIO, WADA, SHIGETAKA
Applicants: TOYODA CHUO KENKYUSHO KK, KABUSHIKI KAISHA TOYOTA CHUO KENKYUSHO
Application year: 1990
Main classification: C04B35
IPC codes: C04B35, F28F21