Process for the preparation of polyurethane elastomers

Abstract: A polyurethane elastomer produced by reaction of a polyisocyanate with an amine-type polyol and another type polyol, the polyisocyanate being an isocyanurate-modified hexamethyelene diisocyanate; and the equivalent ratio of active hydrogen to isocyanate group to be reacted being in a range of from 0.8 to 1.6; and the ratio of the amine-type polyol to the another type polyol being in a range of from 10/90 to 100/0 by weight.

Description: The present invention relates to a process for the preparation of a polyurethane elastomer. More particularly, the present invention relates to the preparation of a polyurethane elastomer useful as a sealing material in electrical appliances, and as a terminal bundling material for medical and industrial hollow-fibers. Heretofore, polyurethane type bundling materials used for sealing materials in electrical appliances and for hollow-fibers in medical liquid-separating apparatuses have been made from an aromatic polyisocyanate such as tolylene diisocyanate (TDI) and diphenylmethane diisocyanate (MDI), as the isocyanate compound, and a castor-oil-type polyol, a polyether-type polyol, polyester-type polyol or an amine-type polyol as the polyol component. In the case of use for bundling hollow-fibers in medical liquid separation apparatuses, however, the elastomer is required to contain far less substance which may be eluted from the sealing portion. For the improvement thereof, Japanese Patent Laid-open Application Sho. 60-58156 describes the use of a prepolymer prepared by reaction of hexamethylene diisocyanate (HMDI) with a polyol as a fraction of the polyisocyanate component. However, the prepolymers, which have been prepared by reaction of HMDI with a polyol such as 1,4-butanediol and castor oil, generally contain a large amount of unreacted HMDI. Thus, the use of such prepolymer as the starting material for the bundling material is undesirable from the stand point of worker safety and hygiene as well as being insufficient in decreasing the eluted matter from the cured polyurethane. Accordingly, a further decrease in the amount of unreacted HMDI is required. Moreover, HMDI has the disadvantage of significantly low reactivity, causing slow curing after potting, with low productivity, as compared with aromatic diisocyanate, for example TDI and MDI. A method for promoting the reaction of such polyisocyanate and a polyol is described in Japanese Patent Laid-open Application Sho. 58-93716, in which a metal type catalyst is employed for shortening the curing time. However, heavy metals such as Sn, Pb, Zn and Cd, if eluted out, exert harmful effects on the body or deteriorate electrical properties, so that the use of such metal-type catalyst is not desirable for medical materials or electrical materials. Starting materials for polyurethane elastomers are required to have a viscosity suitable for potting and to cause neither deterioration nor denaturation of the quality of the cured products, even after storage, and to exhibit stable properties. The present invention seeks to provide an improved polyurethane elastomer by reacting together a specified aliphatic polyisocyanate and a specific polyol under specific conditions. The present invention provides a process for the preparation of a polyurethane elastomer by reacting together as polyisocyanate component an isocyanurate-modified hexamethylene diisocyanate which contains one or more isocyanurate rings and two or more isocyanate groups in the molecule, and as polyol component an oxyalkylated amine having two or more active hydrogen atoms in the molecule and, optionally, a polyol other than an oxyalkylated amine polyol, the weight ratio of the oxyalkylated amine polyol to the other polyol being from 10/90 to 100/0 and the equivalent ratio of active hydrogen atoms to isocyanate groups being from 0.8 to 1.6. The polyisocyanate used in the process of the present invention is an isocyanurate-modified HMDI or a compound prepared by the isocyanuration-polymerization (polycyclotrimerization) of a HMDI-polyol adduct, having one or more of isocyanurate rings and two or more of isocyanate groups in one molecule. This isocyanurate-modified HMDI contains preferably HMDI monomer in an amount of not more than 5 %. Such isocyanuration-polymerization of HMDI is described in Japanese Patent Laid-open Applications Sho. 57-47319, and Sho. 57-47321. The principal polyol used in the process of the present invention is an oxyalkylated amino compound having two or more active hydrogen atoms. Specific examples of such amino-type alcohols are propylene oxide (PO) adducts and ethylene oxide adducts of amino compounds such as ethylenediamines, for example N,N,N',N'-tetrakis(2-hydroxypropyl)ethylenediamine, and N,N,N',N'-tetrakis(2-hydroxyethyl)ethylenediamine; and mono-, di-, and tri-ethanolamines. Specific preferred examples of such amine-type polyols are propylene oxide adducts and ethylene oxide adducts of ethylenediamines such as N,N,N',N'-tetrakis(2-hydroxypropyl)ethylenediamine. The other polyols which can be used in the process of the present invention include low-molecular weight polyols (other than oxyalkylated amine polyols), polyether polyols, castor-oil-polyols and polyester-polyols. Examples of the low-molecular weight polyols are bifunctional polyols such as ethylene glycol, diethylene glycol, propylene glycol, 1,4- and 1,3-butanediols, 1,6-hexanediol, neopentylglycol and hydrogenated bisphenol-A; and tri- and higher-functional polyols (3- to 8-functonal polyols) such as glycerin, trimethylolpropane (TMP), hexanetriol, pentaerythritol and sorbitol. Examples of polyether polyols are alkylene oxide adducts (C₂ to C₄ alkylene oxides ethylene oxide (EO), propylene oxide, and butylene oxide) of the above low molecular-weight polyols, and ring-opening polymerization products of alkylene oxides; specifically, polyethylene glycol, polypropylene glycol and polytetramethylene glycol. The so-called capped polyethers may also be used. In these polyethers, EO and PO may be used singly or in combination of two or more thereof. When PO is used, the addition may be block addition, random addition, or mixed block and random addition. Preferably, at the end of the molecule, EO is added to form a primary end group to raise the reactivity. Examples of castor-oil-polyols are polyester polyols derived from castor oil, or castor oil fatty acid, and a low molecular weight polyol (for example diglyceride and monoglyceride of castor oil fatty acid, and mono-, di-, and tri-esters of castor oil fatty acid with trimethylolpropane, mono-, di-, and tri-esters of castor oil fatty acid with polypropylene glycol, and mono-, di-, and tri-esters of castor oil fatty acid with polyethylene glycol). Examples of polyester polyols are linear and branched polyester polyols derived from a polycarboxylic acid (for example aliphatic saturated and unsaturated polycarboxylic acids such as adipic acid, azelaic acid, dodecanoic acid, maleic acid, fumaric acid, itaconic acid and dimerized linolic acid; and aromatic polycarboxylic acids such as phthalic acid, and isophthalic acid) with a polyol (for example the above low molecular weight polyols and polyether polyols); polylactone polyols such as polycaprolactone polyol prepared by addition-polymerization of a substituted or unsubstituted caprolactone (such as ε-caprolactone, α-methyl-ε-caprolactone and ε-methyl-ε-caprolactone) on an initiating base material [such as a glycol (for example ethylene glycol) or a triol] in the presence of a catalyst (such as an organometallic compound, a metal chelate compound or a fatty acid metal acyl compound) ; polyetherester polyols prepared by reaction of an alkylene oxide (such as EO or PO) with a polyester having terminal carboxylic groups and/or hydroxyl groups to cause an addition reaction. Furthermore, for example, the other polyol may be a polyurethane type polyol derived by the reaction of the above polyol with a diisocyanate selected from aliphatic diisocyanates such as HMDI, alicyclic diisocyanates such as 1-isocyanato-3-isocyanatomethyl-3,5,5-trimethylcyclohexane (IPDI), and bis(4-isocyanatqcyclohexyl)methane (hydrogenated MDI), and araliphatic diisocyanate such as xylylene diisocyanate at an NCO/OH equivalent ratio of not more than 1. Of these polyols, there are preferred polyethylene glycol and capped ether which are a polyether polyol having an equivalent of from 100 to 500 and having terminal primary alc hol groups. Castor-oil-polyols are also preferred, especially those which have an equivalent of from 200 to 800. The ratio of the amine-type polyol component and the other polyol component in the process of the present invention is such that the amount of the amine-type polyol is from 10 to 100 % by weight of the total polyol. A content of 10 % by weight or less of the amine-type polyol is not desirable in view of the resulting prolonged gel time, lower workability, and lower productivity. The precise quantity of amine-type polyols within the 10 to 100% range will however depend upon the required properties for the bundling materials and the sealing materials. The reaction of a polyisocyanate with a polyol in the process of the present invention is conducted at the equivalent ratio of active hydrogen atoms to NCO groups in the range of from 0.8 to 1.6, preferably from 0.9 to 1.2. Normally, curing is conducted at the active hydrogen/NCO ratio of 1.0. Generally, however, curing may be conducted by blending at the active hydrogen/NCO equivalent ratio within the range of from 0.8 to 1.6 for the purpose of, adjustment of curing time, and the formation of the desired variety of cured resin properties. Outside the range of from 0.8 to 1.6, curing may not occur, or the desired resin properties may not be achieved. Curing is normally practiced at room temperature. The gel time is normally in the range of from 5 to 90 minutes. If necessary, the gel time and the time for complete cure may be shortened, or required mixing viscosity may be achieved, by raising the temperature up to 30 to 80°C. The resin component (the main material and the curing agent) may be heated to accelerate the reaction of isocyanate with the active hydrogen. At a temperature of 30°C or lower, the viscosity of the cured resin component is increased, which retards uniform mixing or lengthens the gel time, while at a temperature of 80°C or higher, the resin itself may deteriorate and curing may proceed extremely rapidly, which are not desirable from the point of view of operation. The polyurethane elastomer thus produced is useful for a fiber-end bundling material and a sealing material for hollow-fibers employed in a fluid separation apparatus, and a sealing material. The bundling and sealing of the end portion of the hollow-fibers is usually conducted according to the centrifugal molding method, which is described, for example, in Japanese Patent Laid-open Applications Sho. 57-58963, and Sho. 57-58964. The hollow-fibers include those prepared from materials having properties of a semipermeable membrane, such as regenerated cellulose, cellulose acetate, cellulose ether, polyethylene, polypropylene, polyamide, polysulfone, polyacrylamide, polyacrylonitlile, polyester, polycarbonate, polyvinyl chloride, polyurethane, casein and collagen. The constitution of a medical fluid separation apparatus employing the hollow-fibers sealed with a bundling material of the present invention, other than the bundling agent, may be similar to those described for example, in Japanese Patent Laid-open Applications Sho. 56-15757, Sho. 58-75556, Sho. 58-92423, Sho. 58-206757, and Sho. 59-225066. The examples of the specific applications include a blood plasma separation apparatus, an artificial lung, an artificial kidney, industrial, medical, and general water clarification apparatuses, and drug separation apparatuses. The polyurethane elastomers obtained by reaction of polyisocyanate with a polyol according to the present invention contain an extremely small amount of matter which may be eluted when the elastomers are used for sealing materials or bundling materials, thus being advantageous for sealing materials and bundling materials for medical use. In particular, in use for a terminal bundling material for hollow-fibers of a medical fluid separation apparatus, there occurs no migration of a harmful metal compound such as of Sn, Zn, Pb and Cd into the body because of the absence of such harmful metal compounds as catalysts for cure promotion of the polyurethane bundling material. The polyurethane elastomer of the present invention, even though no heavy metal type catalyst is employed, has curing characteristics of the same level as that of aromatic type polyurethane, and the starting materials therefor are liquid at room temperature, having viscosity appropriate for molding operation, so that the productivity is not adversely affected. Since the starting prepolymer does not substantially contain free HMDI monomer which is highly toxic and irritant, the starting prepolymer according to the present invention is safe and hygienic to workers involved in molding operations. The polyurethane elastomers produced by the present invention are almost transparent in the thickness range for such uses, having suitable processability, thus being excellent as the bundling material for hollow-fibers. Such hollow-fibers exhibit excellent characteristics in fields where higher safety and less eluted matter are required, for example, in a terminal bundling material for hollow-fibers of a medical fluid separation apparatus with which blood is brought into contact including blood plasma separation apparatus, an artificial lung, an artificial kidney, and so on, and are considerably useful industrially. The present invention is explained in more detail by referring to examples. The terms "part" and "%" are based on weight respectively, if not specially remarked. Example 1 133 parts of an isocyanurate-modified HMDI ("Coronate EH" [registered Trade Mark], NCO content: 21.3%, HMDI monomer content: not more than 0.3 %, made by Nippon Polyurethane Industry Co., Ltd., hereinafter referred to as C-EH), and a mixture of 60 parts of a castor-oil-type polyol (hydroxyl number: 120) and 40 parts of N,N,N',N'-tetrakis(2-hydroxypropyl)ethylenediamine (THPED) were blended, and the blended matter was cured. The equivalent ratio of NCO/active hydrogen was 1.0. In the molding operation, neither odor nor are irritation caused by HMDI was perceived. The blended matter rapidly became uniform, giving a transparent pale-yellow cured matter. The details are shown in Table 1. Example 2 143 parts of C-EH and a mixture of 25 parts of a capped ether (EO addition rate: 20%, molecular weight: 2500, hydroxyl value: 45), 30 parts of a castor-oil-type polyol (hydroxyl value: 160), and 45 parts of N,N,N',N'-tetrakis(2-hydroxyethyl)ethylenediamine (THEED) were blended, and the blended matter was cured. The equivalent ratio of NCO/active hydrogen was 0.95. The blended matter rapidly became uniform. In the molding operation, neither odor nor eye irritation caused by HMDI was perceived. The details are shown in Table 1. Example 3 180 parts of C-EH and a mixture of 19 parts of a capped ether (molecular weight: 2500, hydroxyl value: 45), 24 parts of a castor-oil-type polyol (hydroxyl number: 160) and 57 parts of THEED as polyol components were blended. The blended matter was cured at a liquid temperature of 50°C. The equivalent ratio of NCO/active hydrogen was 1.0. The blended matter rapidly became uniform, giving a transparent pale-yellow cured matter. In the molding operation, neither odor nor irritation caused by HMDI was perceived. The details are shown in Table 1. Comparative example 1 A reaction of 204 parts of HMDI and 576 parts of polypropylene glycol (molecular weight: 2000) were carried out at 90°C for 20 hours, to give a prepolymer having NCO terminals as a polyisocyanate component. The resulting prepolymer had a viscosity of 1200 mPa.s (1200 cP) at 25°C, an NCO content of 9.8 %, and a free HMDI of 8.8 %. THPED was blended with the prepolymer in an amount to give an NCO/active hydrogen equivalent ratio of 1.0, and the blended matter was cured. Although the blended matter became uniform rapidly, the initial mixing viscosity was so high that a gel time of 30 minutes was required, which was not desirable in the operation. Further, in the blending operation, strong odor and irritation to eyes was caused by the HMDI monomer contained in the prepolymer, which was not desirable in working hygiene. The details are shown in Table 1. Comparative example 2 315 parts of MDI and 275 parts of three-functional polypropylene polyol (molecular weight: 1500) were allowed to react at 80°C for 4 hours, to give a prepolymer having NCO terminals as a polyisocyanate component. The resulting prepolymer had an NCO content of 14.2 % and a viscosity of 5200 mPa.s (5200 cP) at 25°C. A mixture of 332 parts of castor-oil-type polyol (hydroxyl value: 160) and 78 parts of THPED were blended with the prepolymer in an amount to give an NCO/active hydrogen equivalent ratio of 1.0, and the blended matter was cured. The details are shown in Table 1. Example 4 75 parts of C-EH and 25 parts of THEED were blended and the blended matter was cured. The both components, in an NCO/active hydrogen equivalent ratio of 1.0, dissolved with each other to become uniform. In the molding operation, neither odor nor eye irritation caused by HMDI monomer was perceived. The details are shown in Table 1. Test method for eluted matter: (Based on Approval Standard for Dialysis-type Artificial Kidney) The support and the flow-path-connecting tubes to be used in a dialysis-type artificial kindney are taken respectively in an amount of approximately 15 g (each having front-side and back-side surface area of approximately 200 cm²), which are cut into pieces having surface areas of 2 cm² (or length of approximately 2 cm). The cut pieces are put into a container containing 150 ml of water which had been boiled and cooled. It is heated to 70 ± 5 °C for 1 hour. Having been cooled, the liquid is taken out from the container, and water is added to fill it up to a volume of 150 ml, which is used for a test solution. Separately, water which has been boiled and cooled is used for the blank test solution. The test solution and the blank solution are subjected to the tests below. Ultraviolet absorption spectrum: The absorbance of the test solution is measured at the solution layer thickness of 10 mm and the wavelength range of from 220 nm to 350 nm by employing the blank solution as the reference. The absorbance should be not more than 0.1. Potassium permanganate-reducing material: 10.0 ml of the test solution is put into an Erlenmeyer flask. Thereto 20.0 ml of 0.01N potassium permanganate solution and 1.0 ml of dilute sulfuric acid are added. The mixture is boiled for 3 minutes. After cooling, 0.10 g of potassium iodide is added to the mixture, and the flask is tightly closed. The mixture solution is mixed by shaking, and is left stand for 10 minutes. Thereafter the solution is titrated with a 0.01N sodium thiosulfate solution (with an indicator of 5 drops of starch reagent solution). Separately, 10.0 ml of the blank test solution is subjected to the same treatment. The difference in the consumption of the 0.01N potssium permanganate solution between tbe test solution and the blank test solution should be not more than 1.0 ml.

Claims: A process for the preparation of a polyurethane elastomer by reacting together as polyisocyanate component an isocyanurate-modified hexamethylene diisocyanate which contains one or more isocyanurate rings and two or more isocyanate groups in the molecule, and as polyol component an oxyalkylated amine having two or more active hydrogen atoms in the molecule and, optionally, a polyol other than an oxyalkylated amine polyol, the weight ratio of the oxyalkylated amine polyol to the other polyol being from 10/90 to 100/0 and the equivalent ratio of active hydrogen atoms to isocyanate groups being from 0.8 to 1.6. A process according to claim 1, carried out at a temperature of 30 to 80°C.

Inventors: MURAYAMA KIYOFUMI, NAKAGAWA SHIGERU, OHBUCHI YUKIO, YAMAGATA TOMOYUKI, MURAYAMA, KIYOFUMI, NAKAGAWA, SHIGERU, OHBUCHI, YUKIO, YAMAGATA, TOMOYUKI, MURAYAMA, KIYOFUMI, MEGARON MIURAKAIGAN DAINI 609
Applicants: NIPPON POLYURETHANE KOGYO KK, NIPPON POLYURETHANE INDUSTRY CO. LTD.
Application year: 1990
Main classification: C08G18
IPC codes: A61M1, C08G18, C09K3, H01B3, B01D63