Secondary battery

Abstract: A secondary battery which comprises a positive-electrode material, an electrolyte solution, a negative-electrode material comprising zinc, and a negative-electrode substrate made of lead or a lead alloy. In a modification, the negative-electrode substrate is made of an electro-conductive material, with the surface thereof being coated with lead or a lead alloy.

Description: Background of the Invention: Field of the Invention: The present invention relates to a secondary battery which employs zinc as a negative-electrode material MnO₂ as a positive-electrode material and Zu SO₄ as an electrolyte. Description of the Related Art: Batteries are widely used as a power source for electronic apparatuses and electric apparatuses. The recent trends towards miniaturization, higher performance, portability, and personal uses of the electronic apparatuses and electric apparatuses have brought about increased demand for secondary batteries which are suitable for long term use and are yet economical. In such technical fields, there have been investigated nickel-cadmium secondary batteries, alkali-zinc secondary batteries. In particular, alkali-zinc secondary batteries which employ zinc as the negative-electrode material has advantages of high energy density and economically low cost. In GB-A-2 064 209 secondary batteries of the zinc-alkaline type are disclosed using Zn negative-electrodes. As electrolyte also ZnCl₂, ZnBa and Zn-PbO₂ are suggested. According to this reference the dendrite growth shall be suppressed by the combined action of a porous conducting collector surface and H₂-evolution. FR-A-2 114 666 discloses secondary batteries of the alkaline type using a negative electrode comprising Zn and a positive electrode made of nickel oxide. Here the dendrite growth is prevented by the use of a negative electrode comprising an electrically conducting substrate having applied thereon a pasty Zn-mixture and an additional layer; this layer being either incorporated into the layer of the pasty Zn-mixture or being directly coated on the substrate surface. For preventing dendrite growth it is essential that the surface of the electrode, i.e. the layer of the pasty Zn-mixture is highly porous. US-A-3 447 971 discloses a battery system comprising lead oxide as positive electrode material, a negative electrode fabricated from an electrically conductive material such as lead, zinc or aluminum having Zn deposited thereon and a ZnSo₄ electrolyte. However, the secondary batteries employing zinc as the negative-electrode material have disadvantages such that the zinc electrode deteriorates remarkably by repetition of charge and discharge and that the cycle life is short. The causes of the deterioration of the characteristics of the zinc electrode with the repetition of charge and discharge are considered as below. The zinc electrode tends to dissolve unevenly during discharge because of delicate non-uniformity of the surface state, so that the surface roughness of the zinc electrode will increase with the progress of the discharge, and the zinc electrode will come to be deformed. During charge, zinc deposites in a form of a tree-branch (which is called dendrite) on the projected portion. The dendrite will grow toward the positive electrode with the repetition of charge-discharge cycles, the deposited zinc finally penetrating the separator to cause internal short-circuit, or dendrite short-circuit. Summary of the Invention: The present invention intends to provide an aqueous secondary battery employing zinc as a negative-electrode material which is free from dendrite short-circuit and has a long cycle life. According to an aspect of the present invention, there is provided a secondary battery using MnO₂ as a positive-eletrode material, ZnSO₄ as an elctrolyte, Zn as a negative-electrode material, wherein the negative elctrode is made of an electrically conductive substrate on which Zn is electrolytically deposited, and at least the surface of the substrate is a layer of lead or lead alloy. According to a further aspect of the present invention there is provided a secondary battery, wherein the electrically conductive substrate is composed of lead or lead alloy. Detailed Description of the Preferred Embodiments: The inventors of the present invention conducted comprehensive investigation to solve the aforementioned problems. As the result, the inventors found that the use of lead or lead alloy as the substrate could solve the above problems in a secondary battery which comprises a positive-electrode material, for example manganese dioxide, an electrolyte solution, for example an aqueous zinc sulfate solution, and zinc as a negative-electrode material, the negative electrode being constituted of a substrate for releasing and accepting the electrons necessary for oxidizing (or dissolving) and reducing (or depositing) the zinc on discharge and charge of the battery from the outside, and zinc as the negative-electrode material coating the substrate, and thus accomplished the present invention. The present invention provides a secondary battery which comprises MnO₂ as a positive-electrode material, ZnSO₄ as an electrolyte, Zu as a negative-electrode material wherein the negative electrode is made of an electrically conductive substrate on which Zu is electrolytically deposited, and at least the surface of the substrate is a layer of lead or a lead alloy. The lead or the lead alloy, when used for the substrate as in the present invention, forms an alloy together with the zinc on oxidation (dissolution)-reduction (deposition) at discharge-charge of the battery. The formed alloy phase will bond strongly to the electrically conductive substrate, reducing the exfoliation of the deposited zinc to a minimum extent, and further controlling the crystal orientation of the zinc depositing at the successive charge (reduction) to allow uniform deposition of zinc to retard roughening of the zinc electrode surface. Thus the growth of dendrite is suppressed, and dendrite-short-circuit is prevented. Accordingly, the long cycle life of the secondary battery is considered to be due to the suppression of growth of the dendrite and the resulting prevention of the dendrite short-circuit. Detailed Description of the Invention: The present invention is described in more detail below. The lead or the lead alloy used for at least the surface of electrically conductive substrate of the secondary battery of the present invention includes simple lead, and binary and ternary alloys of lead with one or more of tin, indium, bismuth, silver, calcium, and antimony. The use of the lead alloy is preferable since it retards collapse of the substrate which is caused by repeated charge-discharge. The lead alloy, when it is, used preferably contains a metal or metals other than lead in an amount of not more than 5 % by weight from the stand point of processability of the negative-electrode substrate. At the content of a metal or metals other than lead exceeding 5 % by weight, the reversibility of dissolution-deposition may be lowered. The use of an electro-conductive substrate coated with lead or a lead alloy prevents the above-mentioned dendrite short-circuit. Since the electro-conductive substrate is malleable and ductile, the substrate may easily be worked previously into a desired form such as a thin plate, a sponge, and a mesh. In particular, the one worked into a spiral form may give a negative-electrode substrate of a battery having a spring elasticity. Any electro-conductive material may be used therefor. The examples thereof includes iron and iron alloys such as stainless steel, high-carbon steel, etc.; nickel and nickel alloys such as Monel metal, Hastelloy, Inconel, etc.; copper and copper alloys such as brass, cupro nickel, etc.; and carbon and electroconductive polymer mainly constituted of carbon such as polyaniline, polypyrrol, carbon fiber, etc. The substrate constituted of an electro-conductive material coated with lead or a lead alloy may be constituted by plating the electro-conductive material with lead or a lead alloy employing a lead ion-containing aqueous solution; by contact bonding lead or a lead alloy at the surface of the electro-conductive material; by sputtering lead or a lead alloy onto the surface of the electro-conductive material; or in the like manner. In the case where the surface of the electro-conductive substrate is plated with lead or a lead alloy employing a lead-ion-containing aqueous solution, the electro-conductive substrate previously worked into a thin plate, a sponge, a mesh, etc. is cut into a desired shape and is connected to negative pole (-) of a DC power source, while a piece of lead cut into a predetermined shape is connected to a positive pole (+) of the DC power source. These are immersed in an aqueous solution containing lead ion to conduct electroplating. Any aqueous solution containing lead ion may be used for this purpose. The examples therefor include solutions of lead fluaborate, lead sulfamate, lead sulfate, etc. in pure water which preferably further contain fluaboric acid, boric acid, peptone, or the like dissolved therein for smoothing the surface of the plated lead. The concentrations, although not limited specifically, are preferably from 90 to 100 g/l for lead fluoborate, from 60 to 80 g/l for fluoboric acid, from 20 to 30 g/l for boric acid, and 0.5 g/l for peptone. The lead connected to a DC power source is preferably to be cut to have an area twice or larger than that of the electro-conductive substrate, and has a purity of not less than 98.5 %. The electroplating is preferably conducted at a temperature of from 25 to 30 °C and at a current density of from 15 to 30 mA/cm². The thickness of the lead plating is not particularly limited insofar as the electro-conductive substrate is coated closely. The electro-conductive substrate is electroplated with lead alloy in an aqueous solution containing lead ion together with a desired amount of tin, indium, bismuth, silver, calcium, antimony, etc. The electro-conductive substrate of the secondary battery of the present invention is preferably be immersed in a mixture of acetic anhydride and hydrogen peroxide (mixing ratio of 3:1 by volume) for removing any oxide film covering the surface of the lead or the lead alloy, and further is washed with water or acetone for fat removal. The zinc is formed into the substrate of the secondary battery of the present invention in a manner such that zinc ion in an aqueous solution is electrolytically reduced to be deposited onto a surface of a electro-conductive substrate composed of lead or a lead alloy or of a electro-conductive substrate coated with lead or a lead alloy (hereinafter simply referred to as "a negative-electrode substrate"). Where zinc ion in an aqueous solution is electrolytically reduced to be deposited onto a surface of a negative-electrode substrate, the electroplating is conducted at a constant electric current with a negative-electrode substrate connected to negative pole (-) of a DC power source and immersed in an aqueous solution containing zinc ion, and with the counter electrode connected to a positive pole (+) of the DC power source and immersed in the same aqueous solution containing zinc ion. The aqueous solution containing zinc ion employed in this method is prepared by dissolving a zinc salt, such as zinc sulfate, zinc chloride, zinc acetate, zinc nitrate, etc. in purified water at a concentration in the range of from 10 mM to saturation. The zinc salt is preferably zinc sulfate which is identical with the electrolyte constituting the battery since the anion of the salt may be enclosed by the deposited zinc. The concentration is preferably in the range of from 0.5 to 2 M for high degree of uniformity of zinc and low conductivity of the electrolyte. The counter electrode in the electrolytic deposition is preferably made of zinc so as to keep the zinc concentration unchanged during the electrolysis. The zinc having preferably a purity of not less than 99.9 % to avoid contamination by an impurity. The electrolysis for depositing zinc may be conducted by any of constant-current electrolysis, constant-voltage electrolysis, pulse electrolysis, and voltage-sweeping electrolysis, among which preferable are constant-current electrolysis allowing easy control of the quantity of electricity, and constant-voltage electrolysis causing less side reactions. In the constant-current electrolysis, the current is preferably in the range of from 0.1 to 100 mA/cm² for compactness of the deposited zinc and smoothness of the surface thereof. In the constant-voltage electrolysis, the applied voltage is in the range of from -0.01 to -1.0 V relative to the zinc electrode for compactness of the deposited zinc and smoothness of the surface thereof. The amount of the zinc to be deposited is preferably 0.5 to 5 times that of the manganese dioxide, which is a positive-electrode material, in electricity equivalence for the purpose of providing sufficient battery capacity. In the case where zinc in a sheet form is placed on the surface of a negative-electrode substrate, the sheet-form zinc has preferably a purity of not less than 99 %. In the case where granular zinc is mixed with a suitable binder and a suitable electroconductive material into a paste and then applied and dried on the surface of a negative-electrode substrate, the amounts of the binder and the electroconductive agent are respectively not more than 5 % of the zinc. The zinc which is used as a negative-electrode material is one deposited by electrolysis in view of the activity of zinc, the effective surface area of zinc and so on. The manganese dioxide which is used as the positive-electrode material is exemplified by natural manganese dioxide, chemical manganese dioxide, and electrolytic manganese dioxide, of which the electrolytic manganese dioxide is preferable because of high activity as a positive-electrode material. While such manganese dioxide may be used by itself, it is preferably used as a mixture with electroconductive carbon powder such as acetylene black, by which electroconductivity and electrolyte stability are improved. The positive-electrode material may be press-molded into a positive electrode, or may be mixed with a binder to form a thin film by screen printing or the like and to form it into a desired shape of positive electrode. In the aqueous solution of zinc sulfate which is used as the electrolyte solution of the secondary battery of the present invention, the zinc sulfate as the electrolyte is not particularly limited. However, the purity thereof is preferably not less than 99 %. It has advantages that it is easily handled and is stable because water is used as the solvent. Furthermore, the electrolyte solution exhibits a high electroconductivity, giving excellent dischargeability of the secondary battery. Detailed Description of the Preferred Embodiments: The present invention is described in more detail by referring to examples without limiting it in any way. Example 1 Lead having a thickness of 0.1 mm and a purity of 99.8 % was used as the negative-electrode substrate. The surface was polished with #1500 sandpaper. Then the lead substrate was immersed in a mixture of acetic anhydride and hydrogen peroxide in a volume ratio of 3:1, and washed with water and acetone to remove fat. The substrate was adjusted to have a surface area of 12 cm², and immersed in aqueous 2 M zinc sulfate solution. By using a zinc plate having 99.9 % purity as the counter electrode, a constant electric current of 60 mA was made to flow between the electrodes for 15 hours to deposit zinc on the surface of the lead substrate, thus providing a negative electrode. The electrolysis efficiency of zinc was calculated from the weight increase of lead given by the electrolytic zinc deposition, which shows that 900 mAh of zinc was contained and the deposition of zinc was nearly quantitative. A separator of filter paper made of glass fiber and a positive-electrode compound consisting of 1.0 g of electrolytic manganese dioxide and 0.1 g of acetylene black were placed on the negative electrode. 3 ml of aqueous 2 M zinc sulfate solution was dropped and impregnated thereto as the electrolyte solution, thus forming a battery. The battery prepared as above was subjected to a discharge test at a constant current discharge of 50 mA and at 25 °C. The discharge voltage at the start was 1.55 V, and the discharge was stopped when the discharge voltage falles to 0.3 V. After the discharge, the battery was charged at a constant current of 50 mA to a charging voltage of 1.9 V. This operation of discharge-charge is defined as one cycle. The battery was tested for cycle life to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results. Example 2 A negative electrode was prepared by depositing zinc on the surface of the lead alloy substrate in the same manner as in Example 1 except that a lead alloy of 0.3 mm thick containing 5 % by weight of indium was used as the negative-electrode substrate. The electrolysis efficiency of zinc was calculated from the weight increase of lead alloy given by the electrolytic zinc deposition, which shows that 900 mAh of zinc was contained and the deposition of zinc was nearly quantitative. A battery was prepared with this negative electrode and with the separator, the positive-electrode compound and the electrolyte solution identical with the ones used in Example 1. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. Example 3 A negative electrode was prepared by depositing zinc on the surface of the lead alloy substrate in the same manner as in Example 1 except that a lead alloy of 0.3 mm thick containing 2 % by weight of tin and 3 % by weight of bismuth was used as the negative-electrode substrate. The electrolysis efficiency of zinc was calculated from the weight increase of lead alloy given by the electrolytic zinc deposition, which shows that 900 mAH of zinc was contained and the deposition of zinc was nearly quantitative. A battery was prepared with this negative electrode and with the separator, the positive-electrode compound and the electrolyte solution identical with the ones used in Example 1. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. Example 4 A negative electrode was prepared by depositing zinc on the surface of the lead alloy substrate in the same manner as in Example 1 except that a lead alloy of 0.3 mm thick containing 2 % by weight of tin, 1 % by weight of indium, and 1 % by weight of silver was used as the negative-electrode substrate. The electrolysis efficiency of zinc was calculated from the weight increase of lead alloy given by the electrolytic zinc deposition, which shows that 900 mAh of zinc was contained and the deposition of zinc was nearly quantitative. A battery was prepared with this negative electrode and with the separator, the positive-electrode compound and the electrolyte solution identical with the ones used in Example 1. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. Example 5 A negative electrode was prepared by depositing zinc on the surface of the lead alloy substrate in the same manner as in Example 1 except that a lead alloy of 0.3 mm thick containing 4 % by weight of antimony was used as the negative-electrode substrate. The electrolysis efficiency of zinc was calculated from the weight increase of lead alloy given by the electrolytic zinc deposition, which shows that 900 mAh of zinc was contained and the deposition of zinc was nearly quantitative. A battery was prepared with this negative electrode and with the separator, the positive-electrode compound and the electrolyte solution identical with the ones used in Example 1. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. Example 6 A negative electrode was prepared by depositing zinc on the surface of the lead alloy substrate in the same manner as in Example 1 except that a lead alloy of 0.3 mm thick containing 0.03 % by weight of calcium was used as the negative-electrode substrate. The electrolysis efficiency of zinc was calculated from the weight increase of lead alloy given by the electrolytic zinc deposition, which shows that 900 mAH of zinc was contained and the deposition of zinc was nearly quantitative. A battery was prepared with this negative electrode and with the separator, the positive-electrode compound and the electrolyte solution identical with the ones used in Example 1. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. Example 7 A sheet of SUS 430 stainless steel of 0.3 mm thick, which had been adjusted to have an area of 12 cm², was connected to a negative pole (-) of a DC power source. A plate of lead having a purity of 98.5 %, which had been adjusted to have an area of 24 cm², was connected to a positive pole (+) of the DC power source. These plates were immersed in an aqueous solution containing 90 g/l of lead fluoborate, 60 g/l of fluoboric acid, 30 g/l of boric acid, and 0.5 g/l of peptone dissolved in pure water, and electroplating was conducted at a temperature of 25 °C at current density of 25 mA/cm² for 1.5 hours, giving a negative-electrode substrate electroplated with lead of approximately 130 µm (micron) thick. This substrate was immersed in a mixed solution containing acetic anhydride and hydrogen peroxide in a volume ratio of 3:1, and was further washed with water and acetone to remove fat therefrom. The substrate was immersed in aqueous 2 M zinc sulfate solution. By using a zinc plate having 99.9 % purity as the counter electrode, a constant electric current of 60 mA was made to flow between the electrodes for 15 hours to deposit zinc on the surface of the lead-plated SUS 430 stainless steel thus providing a negative electrode. The electrolysis efficiency of zinc was calculated from the weight increase of the negative-electrode substrate of the lead-plated SUS 430 stainless steel sheet given by the electrolytic zinc deposition, which shows that 900 mAh of zinc was contained and the deposition of zinc was nearly quantitative. A separator of filter paper made of glass fiber and a positive-electrode compound consisting of 1.0 g of electrolytic manganese dioxide and 0.3 g of acetylene black were placed on the negative electrode. 3 ml of an aqueous 2 M zinc sulfate solution was dropped and impregnated thereto as the electrolyte solution, thus forming a battery. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. Example 8 A pure nickel in a sponge form of 0.5 mm thick, which had been adjusted to have an area of 12 cm², was connected to a negative pole (-) of a DC power source. A plate of lead having a purity of 98.5 %, which had been adjusted to have an area of 24 cm², was connected to a positive pole (+) of the DC power source. These were immersed in an aqueous solution containing 100 g/l of lead fluoborate, 80 g/l of fluoboric acid, 20 g/l of boric acid, and 0.5 g/l of peptone dissolved in pure water, and electroplating was conducted at a temperature of 25° C at current density of 15 mA/cm² for 2.5 hours, giving a negative-electrode substrate electroplated with lead of approximately 30 µm (micron) thick. On the surface of this substrate, zinc was deposited in the same manner as in Example 7 to provide a negative electrode. The electrolysis efficiency of zinc was calculated from the weight increase, given by the electrolytic zinc deposition, of the negative-electrode substrate of lead-plated pure nickel, which shows that 900 mAh of zinc was contained and the deposition of zinc was nearly quantitative. A battery was prepared with this negative electrode and with the separator, the positive-electrode compound, and the electrolytic solution identical with the ones used in Example 7. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. Example 9 Brass in a mesh form of 0.3 mm thick, which had been adjusted to have an area of 12 cm², was connected to a negative pole (-) of a DC power source. A plate of lead having a purity of 98.5 %, which had been adjusted to have an area of 24 cm², was connected to a positive pole (+) of the DC power source. These plates were immersed in an aqueous solution containing 95 g/l of lead fluoborate, 70 g/l of fluoboric acid, 25 g/l of boric acid, and 0.5 g/l of peptone dissolved in pure water, and electroplating was conducted at a temperature of 25 °C at current density of 30 mA/cm² for 2.5 hours, giving a negative-electrode substrate electroplated with lead of approximately 90 µm (micron) thick. On the surface of this substrate, zinc was deposited in the same manner as in Example 7 to provide a negative electrode. The electrolysis efficiency of zinc was calculated from the weight increase of the negative-electrode substrate of lead-plated brass given by the electrolytic zinc deposition, which shows that 900 mAh of zinc was contained and the deposition of zinc was nearly quantitative. A battery was prepared with this negative electrode and with the separator, the positive-electrode compound, and the electrolytic solution identical with the ones used in Example 7. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. Example 10 A negative-electrode substrate was prepared which was lead-plated in a thickness of approximately 100 µm (microns) in the same manner as in Example 7 except that a carbon fiber plate of 0.3 mm thick was used instead of the SUS 430 stainless steel sheet. Then a negative electrode was prepared by depositing zinc on the surface thereof in the same manner as in Example 7. The electrolysis efficiency of zinc was calculated from the weight increase of the negative-electrode substrate of lead-plated carbon fiber given by the electrolytic zinc deposition, which shows that 900 mAh of zinc was contained and the deposition of zinc was nearly quantitative. A battery was prepared with this negative electrode and with the separator, the positive-electrode compound, and the electrolytic solution identical with the ones used in Example 7. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. Example 11 A sheet of SUS 430 stainless steel of 0.3 mm thick, which had been adjusted to have an area of 12 cm², was connected to a negative pole (-) of a DC power source. A plate of lead having a purity of 98.5 %, which had been adjusted to have an area of 24 cm², was connected to a positive pole (+) of the DC power source. These plates were immersed in an aqueous solution containing 90 g/l of lead fluoborate, 60 g/l of fluoboric acid, 30 g/l of boric acid, 0.5 g/l of peptone and 3 g/l of indium sulfate dissolved in pure water, and electroplating was conducted at a temperature of 25 °C at current density of 25 mA/cm² for 1.5 hours, giving a negative-electrode substrate electroplated with lead alloy of approximately 130 µm (micron) thick. On the surface of the substrate, zinc was deposited in the same manner as in Example 7 to provide a negative electrode. The electrolysis efficiency of zinc was calculated from the weight increase of the lead alloy-plated SUS 430 stainless steel sheet given by the electrolytic zinc deposition, which shows that 900 mAh of zinc was contained and the deposition of zinc was nearly quantitative. A battery was provided by using this electrode together with the separator, the positive-electrode compound, and the electrolyte solution identical with the ones in Example 7. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. Example 12 A plate of SUS 430 stainless steel of 0.3 mm thick, which had been adjusted to have an area of 12 cm², was connected to a negative pole (-) of a DC power source. A plate of lead having a purity of 98.5 %, which had been adjusted to have an area of 24 cm², was connected to a positive pole (+) of the DC power source. These plates were immersed in an aqueous solution containing 90 g/l of lead fluoborate, 60 g/l of fluoboric acid, 30 g/l of boric acid, and 0.5 g/l of peptone dissolved in pure water, and electroplating was conducted at a temperature of 25 °C at current density of 25 mA/cm² for 1.5 hours, giving a negative-electrode substrate electroplated with lead of approximately 130 µm (micron) thick. This substrate was immersed in a mixed solution containing acetic anhydride and hydrogen peroxide in a volume ratio of 3:1, and was further washed with water and acetone to remove fat therefrom. On this substrate, a zinc plate having area of 12 cm², thickness of 13 µm (microns) and purity of 99 % were placed, thus providing a negative electrode. A battery was prepared with this negative electrode and together with the separator, the positive-electrode compound, and the electrolytic solution identical with the ones in Example 7. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. Comparative Example 1 A single zinc plate of 0.3 mm thick having a purity of 99 % which had been washed with water, alcohol, and acetone was used as a negative electrode. With the negative electrode, having been adjusted to have an area of 12 cm², a battery was prepared together with a separator, a positive-electrode compound, and an electrolyte solution identical with the ones in Example 1. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. This battery became incapable of being charged at the tenth cycle. The disassembling of the battery revealed that the zinc in the separator deposited out in a dendrite form to cause short-circuit to the positive-electrode side. Comparative Example 2 A plate of SUS 430 stainless steel of 0.3 mm thick, having been washed with water, alcohol, and acetone was used as the negative-electrode substrate. The substrate, having been adjusted to have the area of 12 cm², was immersed in aqueous 2 M zinc sulfate solution. By using a zinc plate having 99.9 % purity as the counter electrode, an constant electric current of 60 mA was made to flow between the electrodes for 15 hours to deposit zinc on the surface of the negative-electrode substrate of the SUS 430 stainless steel sheet, thus providing a negative electrode. The electrolysis efficiency of zinc was calculated from the weight increase of the SUS 430 stainless steel sheet given by the electrolytic zinc deposition, which shows that 900 mAh of zinc was contained and the deposition of zinc was nearly quantitative. A battery was prepared with this negative electrode and with the separator. the positive-electrode compound, and the electrolytic solution identical with the ones in Example 7. The battery was tested for cycle life under the same conditions as in Example 1 to examine the change of the battery capacity with repetition of the cycles. Table 1 shows the results collectively. This battery deteriorated to result in rapid decrease of the battery capacity to become incapable of being charged before the fifteenth cycle. On disassembling the battery, exfoliation of zinc from the negative-electrode substrate, and dendrite-form zinc deposition in the separator short-circuiting with the positive-electrode side were observed. As is obvious from the description above, the present invention provides a secondary battery having long cycle life as well as large discharge capacity since the dendrite short-circuit is effectively inhibited in a weakly acidic secondary battery by employing zinc as the negative-electrode material. A secondary battery which comprises MnO₂ as a positive-electrode material, ZuSO₄ as an electrolyte solution, Zu as a negative-electrode material, wherein the negative electrode is made of an electrically conductive (electro-conductive) substrate on which Zu is electrolytically deposited, and at least the surface of the substrate is a layer of lead or lead alloy.

Claims: A secondary battery using MnO₂ as a positive-electrode material, ZnSO₄ as an electrolyte and Zn as a negative electrode, characterized in that the negative electrode is made of an electrically conductive substrate on which Zn is electrolytically deposited, and at least the surface of the substrate is a layer of lead or lead alloy. A secondary battery according to Claim 1, wherein the electrically conductive substrate is composed of lead or lead alloy. A secondary battery according to Claim 1, wherein the electrically conductive substrate is composed of one of the group consisting of iron, iron alloy, nickel, nickel alloy, copper, copper alloy, carbon and electro-conductive polymer. A secondary battery according to Claim 1 or 2, wherein the lead alloy contains not less than 95 % of lead. A secondary battery according to Claim 1 or 2, wherein the lead alloy contains not more than 5 % of one or more selected from the group consisting of tin, indium, bismuth, silver, calcium and antimony.

Inventors: AKIYAMA TOMOYUKI, CHIBA KAZUYUKI, ICHIDA MASANORI, SUDO HAJIME, TAKAHASHI KEN-ICHI, AKIYAMA, TOMOYUKI, CHIBA, KAZUYUKI, ICHIDA, MASANORI, SUDO, HAJIME, TAKAHASHI, KEN-ICHI
Applicants: TOSOH CORP, TOSOH CORPORATION
Application year: 1990
Main classification: H01M4
IPC codes: H01M4, H01M10