Filter device with non-bypass edge seal

Abstract: A process for making filters with a non-bypassing peripheral seal which comprises heating a cylindrical filter housing to expand its internal diameter; inserting a filter disc that has a diameter larger than that of the internal diameter of the housing when cold; and allowing the assembly to cool.

Description: This invention relates to filters and specifically to fibrous depth filters of the kind in which one or more preformed, integral filter elements are fitted into a housing. Such filters are inter alia encountered in the filtration of blood products and are described, for example, in US-A-4,925,572. Depth filters are capable of removing specified components of a mixture with a high level of efficiency. However, it will be apparent that this efficiency will be of little value if the component to be filtered is able to escape filtration by passing around the edges of, rather than through, the tangle of fibers which forms the depth filter. It is known to seek to avoid this result by forming the filter element in the barrel of the device by forcing a mass of fibers into an elongated cylindrical container. Because it is difficult to manipulate fibers in a uniform, reproducible manner, this can allow bypassing adjacent the wall of the container, as well as resulting in a filter with uneven filtering characteristics. Filters have also been commercially made in which multiple layers of media in sheet form have been edge-sealed by compression between internal flanges. Such assemblies tend to be poorly sealed sunless the flange is of sufficient width, in which case a substantial proportion of the filter area is lost because fluid access to the peripheral areas under the flange is poor. US-A-4,925,572 is directed to a leucocyte depletion filter with an efficiency of 99.9 to 99.99% and uses a filter disc in the form of a right circular cylinder assembled into a cylindrical housing of lateral dimension 0.1 to 1% smaller than the filter disc, i.e., into a housing with an interference fit. The problems can best be appreciated by considering the requirement of obtaining efficiencies in the range of 99.999 to 99.99999% in removing leucocytes from red cell concentrate during blood processing. Filters for this purpose tend to be comparatively thick, for example, in excels of 3 mm, and may comprise an additional prefilter of a thickness of up to 1 mm or more. In order to be effective, a flange 4 mm wide may be needed. In a typical filter with 60 cm² of effective flow area, the effective area lost under the flange would be about 9 cm² or about 15% of the total area. This invention provides for an edge sealing system compatible with filters with efficiencies up to about 99.9999%, for which an interference fit provides sealing that tends to be inadequate. This invention provides an edge sealing method that permits the consistent production of filters of a constant uniform quality and performance, along with excellent resistance to bypassing around the elements. The invention provides a process for the production of a filter assembly which comprises heating a cylindrical housing to a temperature such that its dimensions are significantly expanded but below the temperature at which the housing may become distorted; inserting into the housing a filter disc with a diameter that is larger than the interior diameter of the housing at ambient temperature; and allowing the housing to cool to ambient temperature. The disc is preferably at ambient temperature or lower as it is inserted into the heated housing. This invention also provides a process for the production of a filter unit, the filter unit comprising at least one non-woven fibrous filter disc element in a tight fit with the interior wall of a cylindrical filter housing made from a material with a positive coefficient of expansion at temperatures from 0 to 100°C of at least about 3 x 10⁻⁵/°C. The process comprises: a) compressing a sheet of a non-woven fibrous material while in a heat softened state to a desired density; b) cutting a filter element disc from such compressed sheet with a diameter from 0.2 to 1% greater than the interior diameter of the filter housing at ambient temperature; c) heating the housing to an elevated temperature at which its interior diameter exceeds the diameter of the disc at ambient temperature; d) inserting the filter element disc into the housing while maintaining the housing at the elevated temperature; and e) allowing the assembly to cool to ambient temperature. The interior diameter of the heated housing is preferably within 0.2% of the ambient temperature diameter of the disc, and the disc is preferably cut from a laminated sheet compressed to a voids volume in the range of from 65% to 85%. The filter disc is preferably made from polybutylene terephthalate (PBT) fibers. A plurality of discs with differing porosities may be inserted into the housing in increasing order of porosity from the bottom to the top. Furthermore, the disc is preferably a preformed filter element comprising a plurality of layers with differing porosities. When inserted in the housing, the disc is preferably at or below ambient temperature. At temperatures of from 200 to 100°C, the coefficients of thermal expansion of plastics from which housings could be made range from 1 x 10⁻⁵/°C to 2 x 10⁻⁵/°C, for a typical glass or carbon fiber reinforced plastic, to 20 x 10⁻⁵/°C for unreinforced plastics. Many plastics suitable for injection molding have expansion coefficients of at least about 3 x 10⁻⁵/°C and preferably in the range of 6 x 10⁻⁵/°C to 10 x 10⁻⁵/°C. Of these, most can be heated to about 70°C without distortion, and some, for example, polybutylene terephthalate, will withstand heating to as high as 210°C. In the case of PBT, which has an expansion coefficient in excess of about 6 x 10⁻⁵/°C, a PBT housing will expand by 6 x 10⁻⁵ x (210 - 20) x 100 = 1.1%. If such a housing were 10 cm in diameter, the diametric expansion due to heating would be 0.011 x 10 = 0.11 cm, sufficient to apply (after assembly and cooling), a large compressive force to the circumference of an inserted disc sized to fit the housing exactly at the elevated temperature. The material from which the fiber is made can be a glass or other mineral fiber or, more preferably, a thermoplastic polymer. Examples of suitable thermoplastic polymers include a polyamide, such as nylon 6 or nylon 66; a polyolefin, such as polypropylene; a polyester, such as polyethylene terephthalate (PET) or polybutylene terephthalate; a polycarbonate or a fluorinated polymer, such as polytetrafluoroethylene (PTFE) or a polyfluoroacrylate polymer. Preferred polymers are polypropylene and polybutylene terephthalate. If desired, several discs of differing pore size can be compressed into a single unit for insertion in the housing. This is often a preferred feature of the invention. Alternatively, and sometimes preferably, discs of different densities, but of essentially the same pore diameter, can be prepared and inserted, one on top of the other, in the filter housing in order of increasing pore size, with the smallest pore size at the bottom. For the seal to be effective, the disc must be capable of retaining its cylindrical form as it is diametrically compressed during cooling. Such a disc can, for example, be made by: making a "lay-up" comprising a number of layers of melt blown web; compressing the "lay-up" while hot to increase its density and obtain adhesion between contacting fiber surfaces; and then cutting from the resulting laminate a disc of right cylindrical form. Such a disc is referred to hereinafter as a "preformed filter element". The preformed filter element is preferred to be of diameter equal to or slightly larger than the diameter of the heated housing; however, it should not be so much larger as to make assembly difficult or to distort the element during assembly. Depending on the characteristics of the preformed element, assembly can be accomplished of an element up to about 0.2% larger in diameter compared with the heated housing. Discs cut from laminates having voids volumes of from 65% to 85% are well suited for use in the process of this invention. The invention is now further described with specific reference to certain embodiments. Example A filter disc with an ambient temperature diameter of 8.933 cm. (3.517 inches) was cut from a sheet that had been hot formed from 2.6 µm diameter polybutylene terephthalate fibers to a voids volume of 75% and a thickness of 0.36 cm. A housing made from acrylic resin with an ambient temperature internal diameter of 8.885 cm. (3.498 inches) and a linear coefficient of expansion of 7 x 10⁻⁵/°C. was heated to 70°C. The disc was inserted into the hot housing, which was then allowed to cool to ambient temperature. A tight non-bypass edge seal was achieved without buckling of the disc. By contrast, attempts to press the disc into the unheated housing led to buckling of the disc and a similar disc of 8.903 cm. (3.505 inches) diameter did not buckle, but provided an inadequate edge seal. The present invention has been described largely in terms of cylindrical housings and right cylindrical discs of a filter element. This has been for the sake of simplicity. Clearly, however, the process of the invention could readily be adapted for use with filter elements and housings of square, oblong, or oval cross-section, or any other convenient shape, without departing from the essential process of this invention.

Claims: A process for the production of a filter unit which comprises heating a cylindrical housing to an elevated temperature at which its dimensions are expanded but below the point at which it becomes distorted; inserting a filter disc into the housing with a diameter that is larger than the interior diameter of the housing at ambient temperature; and allowing the housing to cool to ambient temperature. A process for the production of a filter unit according to claim 1, said filter unit comprising at least one non-woven fibrous filter disc element in a tight fit with the interior wall of a cylindrical filter housing made from a material with a positive coefficient of expansion at temperatures from 0 to 100°C of at least about 3 x 10⁻⁵/°C, said process comprising: a) compressing a sheet of a non-woven fibrous material while in a heat softened state to a desired density; b) cutting a filter element disc from such compressed sheet with a diameter from 0.2 to 1% greater than the interior diameter of the filter housing at ambient temperature; c) heating the housing to an elevated temperature at which its interior diameter exceeds the diameter of the disc at ambient temperature; d) inserting the filter element disc into the housing while maintaining the housing at the elevated temperature; and e) allowing the assembly to cool to ambient temperature. The process according to claim 2 in which the interior diameter of the heated housing is within 0.2% of the ambient temperature diameter of the disc. The process according to claim 2 in which the disc is cut from laminated sheet compressed to a voids volume in the range of from 65% to 85%. The process according to claim 2 in which the filter disc is made from polybutylene terephthalate fibers. The process according to claim 2 in which a plurality of discs with differing porosities are inserted into the housing in increasing order of porosity from the bottom to the top. The process according to claim 2 in which the disc is a preformed filter element comprising a plurality of layers with differing porosities. The process according to claim 2 in which the disc is at or below ambient temperature when it is inserted into the heated housing.

Inventors: PALL DAVID BORIS, PALL, DAVID BORIS
Applicants: PALL CORP, PALL CORPORATION
Application year: 1990
Main classification: B01D39
IPC codes: B01D27, B29C65, B29C63, B01D29, B29D99