Laminated packaging film

Abstract: A polymer film laminate is provided having improved machinability on modern high speed belt drive machines, particularly when these machines are set up to form lap back seals. A method of assembling such a film is also provided. The film includes an outside web having an upper surface layer containing a silicone oil. This laminating web can be used with virtually any co-laminate, metallised or not, which is bonded thereto with an adhesive. Upon winding the composite film laminate upon a core, silicone oil is transferred to the inside surface of the laminate, thus providing an inside coefficient friction which is about equal to or less than the outside coefficient of friction. Hot slip properties are also improved upon such transfer. The outside and inside webs are independently formed, which allows the inside web to include coatings or film layers which are not ordinarily usable in a silicone oil-containing film.

Description: This invention relates to polymer film laminates; more particularly, this invention relates to polymer film laminates suitable as packaging film, to processes for their preparation; and to their use with belt-driven packaging machines. Certain polymer films, for example oriented polypropylene, have a number of advantageous properties such as transparency, stiffness and moisture barrier while having coefficients of friction (COF) which are unacceptably high for use as such in modern packaging technology. Treatment of such polymer films with silicone oils has been found to provide satisfactory reductions in their COF; but films so treated are then relatively difficult to treat in other conventional manners: for example, the bond strengths of such films, when laminated to themselves or to metallised coatings, may be unacceptably low; furthermore, corona or flame treatment reduces their heat sealability and increases their COF. This invention seeks to provide polymer film laminates which are sealable on both surfaces with excellent bond strength and COF thereon; and which permit great flexibility in combining film layers of selected properties. In one aspect, this invention provides a polymer film laminate which comprises: a first web including an upper surface layer (a) which layer contains a silicone oil and an anti-blocking agent, and a core layer (b) wherein the surface of the first web remote from layer (a) is ink receptive and has printing thereon; a second web including a lower surface layer (a 1 ) which layer contains an anti-blocking agent but is substantially free from compounded silicone oil; and an adhesive layer bonding the first web to the second web such that layers (a) and (a 1 ) remain exposed and silicone oil transfers from (a) to (a 1 ) in processing. This invention also provides a process for the preparation of a polymer film laminate as herein defined, which process comprises: i) providing a first web as herein defined, ii) providing a second web as herein defined, iii) applying an adhesive layer between the first and second webs; iv) bonding the first web to the second web such that layers (a) and (a 1 ) remain exposed; and v) contacting layer (a) with layer (a 1 ) so that silicone oil transfers from (a) to (a 1 ). This invention further provides use of a film laminate as herein defined in a belt-driven packaging system. The surface of the first web which is adhered to the second web is receptive to ink. The bonding of the second web to the first web thereby locks in printing on this surface so that it cannot be damaged in a packaging operation. A laminated film is provided which includes an outside web, an inside web, an adhesive layer bonding the webs to each other, one of the webs including a surface layer containing a silicone oil, the other of the webs including a surface layer substantially devoid of silicone oil except for oil which is transferred by contact of the surface layer of the one web therewith. The outer surfaces of the laminated film are preferably heat sealable. Such a laminated film can be used for packaging foodstuffs and the like in either belt-driven or non-belt-driven packaging machines and regardless of whether fin or lap seals are formed thereby. When polyolefin films are formed into bags or sacks for receiving articles, the outer surfaces thereof can become scratched if the coefficient of friction is relatively high at the temperature at which such bags are constructed. The excessive drag which may cause such scratching may also cause the packaging apparatus to jam. Due to the advent of belt-driven packaging apparatus including an inside shaping tube which allows the belts to engage the film between the tube and belts, it is now important that both surfaces of the film have satisfactory hot slip performance. This allows the film to be processed on both the new belt-driven apparatus as well as older equipment. Silicone oils of the types described in U.S. Patent No. 4,659,612 have been found to impart satisfactory slip characteristics to oriented polypropylene films. In accordance with the present invention, the outside web of the laminated film includes a thin skin layer (a) (about 2-6 gauge units in thickness) containing an amount of silicone oil sufficient to maintain a low coefficient of friction thereon. The skin layer is a heat seal layer preferably formed from ethylene-propylene random copolymers and/or ethylene-propylene-butene-1 terpolymers. The latter includes 2-9 wt.% and preferably from about 3-7 wt.% ethylene, and 2-9 wt.% and preferably about three to about seven percent by weight of 1-butene. Suitable polymers generally have a melt flow rate at 446°F ranging from 1-15 and preferably 2-7. The crystalline melting point is between about 245-302°F. The average molecular weight range is about 25,000 - 100,000 and the density is 0.89-0.90. The silicone oil, preferably polydimethylsiloxane, is added in amounts between about 0.3% to about 5.0% by weight of the heat sealable skin layer, the preferred range is between 1.1-1.5 wt.%. The skin layer (a) is compounded with an effective amount of anti-blocking agent to help maintain a low coefficient of friction. A finely divided, particulate, inorganic material is preferred having a mean particle size ranging from about 0.5 to 5 microns. One commercially available silica has a mean particle size of 0.75 microns and another has a mean particle size of 4.5 microns. Materials having either particle size or particle sizes within this range can be employed. Metal silicates, glasses, clays and numerous other finely comminuted inorganic materials may also be used. The anti-blocking agent is preferably present in amounts from about 0.05 to 0.5 wt.%, preferably about 0.1 to 0.3 wt.% of each of the skin layers. The core layer (b) of the outside web is preferably derived from isotactic polypropylene which may contain effective amounts of anti-static agents as described in US Patent No. 4,764,425. The polypropylene homopolymer has a melting point range between 321-325°F. The polypropylene core layer provides a moisture barrier and stiffness to the outside web. Other possible core materials include oriented high density polyethylene, oriented polystyrene, oriented polyethylene terephthalate, polycarbonate and nylon. A second skin layer (c) may be provided having a surface which is receptive to ink. This skin layer (c) may comprise the same copolymer and/or terpolymer blend is layer (a), but is subjected to corona, flame, plasma or chemical treatment to impart ink receptivity. This layer may alternatively be omitted and the inner surface of the core layer (b) instead subjected to such treatment. A primer may be added to the second skin layer depending upon the ink which is to be used thereon. Any of a number of commercially available primers would be suitable for enhancing receptivity to ink and/or adhesive, including poly(ethyleneimine), acrylic styrene copolymers, urethane and epoxy. The application of several such primers is discussed in U.S. Patent No. 4,565,739, which is incorporated by reference herein. If a primer is employed, virtually any type of ink would be acceptable for application to the core (b) or skin layer (c), whichever is receptive to ink. Since only certain inks adhere to a silicone oil treated film in the absence of primer, urethane, nitrocellulose, epoxy or polyamide blends should be employed if a primer is not applied. If a urethane adhesive is employed, a water-based ink such as that sold by Crown Zellerbach under the name AQALAM P, or modified polyamide or nitrocellulose inks or blends thereof, would be satisfactory. If an extrusion (poly) or PVDC adhesive is employed, urethane-nitrocellulose and epoxy-nitrocellulose blends are preferred. The inside web includes a core layer (b 1 ), a bonding surface layer (c 1 ) for bonding with the adhesive, and an inner, heat sealable inner skin (a 1 ). The skin (a 1 ), core (b 1 ) and bonding surface (c 1 ) layers, respectively, may be comprised of the same materials which are mentioned as suitable for the skin (a), core (b), and second skin (c) layers of the outside web. The skin (a 1 ) of the inside web is substantially devoid of silicone oil, however, which enhances the adhesion of a metallised coating which may be applied to the bonding surface layer (c 1 ). The latter is preferably between about two and seventeen gauge units in thickness. It may contain a slip agent (e.g. 700-3,000 ppm oleamide, stearamide, or erucamide or blends thereof). While not required, each web is preferably manufactured by employing commercially available systems for coextruding resins. A polypropylene homopolymer of comparatively high stereoregularity is co-extruded with the resins which constitute one or both skin layers thereof. The polymers can be brought into the molten state and co-extruded from a conventional extruder through a flat sheet die, the melt streams being combined in an adapter prior to being extruded from the die. After leaving the die orifice, the multi-layer film structure is chilled and the quenched sheet then preferably reheated and stretched, for example, three to six times in the machine direction and subsequently four to ten times in the transverse direction. The edges of the web can be trimmed and the film wound onto a core. A metallized coating may be applied to the bonding surface layer (c 1 ) of the inside web using any acceptable method such as that described in US Patent No. 4,345,005, which is incorporated may reference herein. Other coatings may alternatively be employed depending on the properties desired for the film. A PVDC coating may, for example, be provided to improve the gas and moisture carrier properties of the web. The inside and outside webs are bonded to each other through the use of commercially available adhesives and conventional bonding processes. The choice of adhesives depends on the properties which one wishes the laminated film to have. A urethane adhesive provides mainly only adhesion. Extruded polymer resins can provide thickness, stiffness and durability. As discussed above, PVDC provides a gas barrier and an additional moisture barrier. If a dry bonding technique is used, the adhesive is applied to one of the webs, the solvent is evaporated out of the adhesive, and the adhesive-coated web is combined with the other web by heat and pressure or pressure only. Extrusion laminating involves the use of an extruder to melt, and continuously apply a controlled amount of a very viscous melted resin, usually polyethylene, directly between the web materials being laminated. The bond is achieved as the melted resin resolidifies in situ. Primers or precoatings may be employed to augment the bond or improve resistance to chemical attack. Once the outside web has been bonded to the inside web, the resulting laminated film is wound onto a core and maintained in this form for a period of about six hours to one week at a temperature of about 80° to about 125°F. The winding of the film causes the skin layer (a) of the outside web to contact the skin layer (a 1 ) of the inside web. The silicone oil, which is generally substantially uniformly distributed on the exposed surface of skin layer (a), is responsible for imparting a reduced coefficient of friction to this surface as well as to the exposed surface of the inner skin layer (a 1 ) when some of the oil is transferred thereto after these surfaces have been placed in mutual contact. A sufficient amount of silicone oil should be employed to provide a coefficient of friction of layers (a) and (a 1 ), following transfer of silicone oil microglobules to the latter, of about 0.4 or less, preferably 0.25-0.3, up to at least about 60°C. The thickness of the outside web is primarily due to the thickness of the oriented polypropylene core. The surface layexs (a) and (c) may comprise, for example, a total of about eight percent of the total thickness of an 80 gauge web. The total outside web thickness is ordinarily in the range of about 0.35-2.0 mils. The total thicknesses of the inside and outside webs are not critical to the present invention. The laminated films of the following examples do not have printing locked between the first and the second web and do not therefore represent embodiments of the invention for which protection is sought. Nevertheless they are useful for understanding the invention. Example 1 A laminated film comprising an outside web having a coextruded abc structure, an inside web having a coextruded a 1 b 1 c 1 structure, and an adhesive bonding the c layer of the outside web to the c 1 layer of the inside web is provided. The "a" layer is an ethylene propylene random copolymer containing about six percent ethylene. This layer is about 2.2 gauge units (0.55 microns) in thickness, is 1.2 wt. percent polydimethylsiloxane, and includes about 2300 ppm Si02. The "b" layer of the outside web is an isotactic polypropylene containing about 0.1% N,N bis hydroxyethylamine and is about seventy-five gauge units in thickness. The "c" layer is about three gauge units in thickness, is made from the same copolymer as layer "a", is flame treated and coated with a polyethyleneimine primer. The c 1 layer is made from an isotactic polypropylene homopolymer and contains about 2300 ppm SiO 2 . It is about three gauge units in thickness and is flame treated. The b 1 layer is about seventy-five gauge units in thickness and is made from isotactic polypropylene with no additives. Finally, the a 1 layer is fourteen gauge units in thickness (for hermetic sealability) and is formed formed from an ethylene-propylene random copolymer(about 6% ethylene) containing 2300 ppm SiO 2 and a slip agent (e.g. oleamide, stearamide, erucamide and, blends thereof). The urethane adhesive bonds the c layer of the outside web to the c 1 layer of the inside web. The laminated film is wound upon a roll whereupon some of the polydimethylsiloxane within the "a" layer is transferred to the a 1 layer. Examples 2 - 3 The same film structure as Example 1 is provided except the a 1 layer is four and six gauge units, respectively, in thickness. Example 4 The same film structure as Example 1 is provided except the a and a 1 layers are both made from EPB-l random terpolymers containing about 5% ethylene, 8% butene-1 and 87% polypropylene. Example 5 The same film structure as Example 1 is provided except the c 1 layer has a metallized (aluminum) coating deposited thereon. Example 6 The same film structure as Example 1 is provided except the "a" layer is formed from a random copolymer containing about 6% butene-1 and 94% polypropylene.

Claims: A process for the preparation of a polymer film laminate which comprises a first web including an upper surface layer (a) which layer contains a silicone oil and an anti-blocking agent, and a core layer (b), wherein the surface of the first web remote from layer (a) is ink receptive and has printing thereon; a second web including a lower surface layer (a 1 ) which layer contains an anti-blocking agent but is substantially free from compounded silicone oil; and an adhesive layer bonding the first web to the second web such that layers (a) and (a 1 ) remain exposed and the surface of the first web which has printing thereon is adhered to the second web and silicone oil transfers from (a) to (a 1 ) in processing, which process comprises: i) providing a first web as herein defined; ii) providing a second web as herein defined; iii) applying an adhesive layer between the first and second webs; iv) bonding the first web to the second web such that layers (a) and (a 1 ) remain exposed and the surface of the first web which has printing thereon is adhered to the second web; and v) contacting layer (a) with layer (a 1 ) so that silicone oil transfers from (a) to (a 1 ). A process according to claim 1 wherein the first web is coextruded. A process according to claim 1 or claim 2 wherein the ink receptive surface of the first web is printed directly prior to bonding the first web to the second web. A process according to a preceding claim wherein the ink receptive surface of the first web is printed with the interposition of a primer layer prior to bonding the first web to the second web. A process according to any preceding claim wherein the second web comprises a core layer (b 1 ). A process according to any preceding claim wherein the second web comprises a bonding surface layer (c 1 ). A process according to any preceding claim wherein layer (a) and/or layer (a 1 ) are heat sealable. A process according to any preceding claim wherein the silicone oil comprises from 1.1 to 1.5% by weight of layer (a) as extruded. A process according to any preceding claim wherein the second web includes a metallised layer adjoining the adhesive layer. A process according to any preceding claim wherein the second web includes a coating effective to improve the gas barrier properties of the laminate adjoining the adhesive layer. A polymer film laminate which comprises: a first web including an upper surface layer (a) which layer contains a silicone oil and an anti-blocking agent, and a core layer (b) wherein the surface of the first web remote from layer (a) is ink receptive and has printing thereon; a second web including a lower surface layer (a 1 ) which layer contains an anti-blocking agent but is substantially free from compounded silicone oil; and an adhesive layer bonding the first web to the second web such that layers (a) and (a 1 ) remain exposed and silicone oil transfers from (a) to (a 1 ) in processing and the surface of the first web which has printing thereon is adhered to the second web. Use of a film laminate according to claim 11 or made by a process according to any of claims 1 to 10 in a belt-driven packaging system.

Inventors: BALLONI RICARDO, NAHMIAS MICHAEL A, BALLONI, RICARDO, NAHMIAS, MICHAEL A.
Applicants: EXXONMOBIL OIL CORP, EXXONMOBIL OIL CORPORATION
Application year: 1990
Main classification: B32B31
IPC codes: B32B27