FLUORINE-CONTAINING COPOLYMER

Abstract: A fluorine-containing copolymer comprising repea­ ting units derived from an olefin of the formula: wherein R¹, R², R³ and R⁴ are the same or different and each a hydrogen atom or a fluorine atom, or one of them is a chlorine atom and the rest of them are fluorine atoms, and repeating units derived from a vinylphosphonic acid deriva­ tive of the formula: CF₂=CF(CF₂) n - -(OR)₂ (II) wherein R groups are the same or different and each an alkyl group having 1 to 12 carbon atoms, an alkenyl group having 2 to 12 carbon atoms or a phenyl group, and n is 0, 1 or 2, which has good hydrophilicity.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a fluorine-containing copolymer with hydrophilicity. Description of the Related Art Various fluorine-containing polymers are known. However, almost all of them have hydrophobicity but little hydrophilicity. SUMMARY OF THE INVENTION An object of the present invention is to provide a fluorine-containing copolymer with good hydrophilicity. This object is achieved by a fluorine-containing copolymer comprising 40 to 99 % by mole of repeating units derived from an olefin of the formula: wherein R¹, R², R³ and R⁴ are the same or different and each a hydrogen atom or a fluorine atom, or one of them is a chlorine atom and the rest of them are fluorine atoms, and 1 to 60 % by mole of repeating units derived from a vinylphosphonic acid derivative of the formula: wherein R groups are the same or different and each an alkyl group having 1 to 12 carbon atoms, an alkenyl group having 2 to 12 carbon atoms or a phenyl group, and n is 0, 1 or 2. The fluorine-containing copolymer of the present invention preferably has a number average molecular weight of 1500 to 1,000,000. DETAILED DESCRIPTION OF THE INVENTION The fluorine-containing copolymer of the present invention comprises the olefin (I) and the vinylphosphonic acid derivative (II) in a molar ratio of 40:60 to 99:1, preferably 60:40 to 80:20. Specific examples of the olefin (I) which constitutes the fluorine-containing copolymer of the present invention are ethylene, monofluoroethylene, vinylidene fluoride, vinyl fluoride, trifluoroethylene, chlorotrifluoroethylene, and tetrafluoroethylene. Specific examples of the vinylphosphonic acid derivative (II) are CF₂=CFPO(OCH₃)₂, CF₂=CFCF₂PO(OCH₃)₂, CF₂=CF(CF₂)₂PO(OCH₃)₂, CF₂=CFPO(OC₂H₅)₂, CF₂=CFCF₂PO(OC₂H₅)₂, CF₂=CF(CF₂)₂PO(OC₂H₅)₂, CF₂=CFPO(OC₆H₅)₂, and CF₂=CFPO(OCH₂CH=CH₂)₂. The vinylphosphonic acid derivative (II) wherein R is a hydrogen atom is known from, for example, U.S. Patent No. 2,559,754. The derivative (II) may be prepared as follows: The fluorine-containing copolymer of the present invention may contain 0.1 to 30 % by mole of repeating units derived from at least one other copolymerizable monomer such as hexafluoropropylene and perfluorovinyl ether. The fluorine-containing copolymer of the present invention has a number average molecular weight (by GPC) of preferably 1500 to 1,000,000, more preferably 3000 to 500,000. The fluorine-containing copolymer of the present invention may be prepared by any of conventional polymerization methods such as emulsion polymerization, suspension polymerization and bulk polymerization. The monomers may be charged batchwise or continuously to keep the molar ratio of the monomers in the polymerization system. The monomers are radically polymerized in the presence of a polymerization initiator which is used to initiate the polymerization of conventional fluorine-containing olefins. Examples of the polymerization initiator are inorganic peroxides such as persulfates (e.g ammonium persulfate) and redox system initiators comprising a persulfate, a reducing agent (e.g. sodium sulfite nd acid sodium sulfite) and optionally an accelerator (e.g. ferrous sulfate, copper sulfate and silver nitrate); organic peroxides such as diisopropyl peroxydicarbonate, isobutyryl peroxide, benzoyl peroxide, acetyl peroxide and tert.-butyl hydroperoxide; and fluorine-containing peroxides such as [Cl(CF₂CFCl)₂CF₂COO-]₂, [H(CF₂CF₂)₃COO-]₂, (ClCF₂CF₂COO-)₂ and [CH₃-C(CH₃)₂-OCH₂CF₂COO-]₂. In case of emulsion polymerization, as an emulsifier, an alkali metal or ammonium salt of a compound of the formula of the formula: Y(CF₂) m Z wherein Y is a hydrogen atom or a fluorine atom, Z is -COOH or -SO₃H, and m is a number of 5 to 12 is preferably used in an amount of 0.1 to 5 % by weight, preferably 0.5 to 2 % by weight based on the weight of water in the polymerization system. In case of suspension polymerization, water is generally used as a reaction medium. Together with water, a fluorohydrocarbon solvent such as 1,1,2-trichloro-1,2,2-trifluoroethane, 1,2-dichloro-1,1,2,2-tetrafluoroethane, perfluorocyclobutane, dichlorodifluoromethane and trichlorofluoromethane may be used. A polymerization temperature depends on the decomposition rate of the polymerization initiator. In general, it is from 0 to 150°C. A polymerization pressure depends on the polymerization method and polymerization temperature. In general, it is from 0 to 50 kg/cm²G (0 to 49.05 bar G). Although the molecular weight of the fluorine-containing copolymer of the present invention may be controlled through adjustment of relationship between a polymerization rate and an amount of the polymerization initiator, it is easily controlled by the addition of a chain transfer agent. Preferred examples of the chain transfer agent are hydrocarbons having 4 to 6 carbon atoms, alcohols, ethers and organic halogenated compounds (e.g. CCl₄, CBrCl₃, CF₂BrCFBrCF₃, CF₂I₂ and IR f I in which R f is a perfluoroalkylene group). In the fluorine-containing copolymer of the present invention wherein R is an alkyl, alkenyl or phenyl group (hereinafter referred to as "copolymer A"), at least 1 %, preferably at least 2 % of R can be replaced with hydrogen atoms or alkali metal atoms such as potassium or sodium. Such copolymer will be referred to as "copolymer B". The copolymer B may be prepared by copolymerizing the olefin (I) with the vinylphosphonic acid derivative (II) in which R is a hydrogen atom or by hydrolyzing the copolymer A in the presence of an acid compound or a base compound. The hydrolysis of the copolymer A to the copolymer B can be carried out by using conventional reagents and conditions which are employed in the conventional hydrolysis. In the hydrolysis, an amount of the acid compound or the base compound is at least 0.1 mole per one mole of the phosphonate ester. The hydrolysis temperature is preferably from 20 to 80°C. As the acid compound, one having pH not larger than that of hydrochloric acid is preferably used. Preferred examples of such acid compound are hydrochloric acid, sulfuric acid, methanesulfonic acid, trifluoromethanesulfonic acid and chlorosulfonic acid. Preferred examples of the base compound are sodium hydroxide and ammonia. The fluorine-containing copolymer of the present invention has hydrophilicity in addition to heat resistance, weather resistance and chemical resistance and is preferably used in the form of an aqueous paint or as a medical material and a heavy metal scavenger. Further, the fluorine-containing copolymer of the present invention may be gelled or converted to a higher molecular weight polymer and used as an ion-exchange membrane or a functional polymer. PREFERRED EMBODIMENTS OF THE INVENTION The present invention will be illustrated by following Examples. Example 1 Copolymerization of vinylidene fluoride and CF₂=CFPO(OCH₃)₂ CF₂=CFPO(OCH₃)₂ (10 g), 1,1,2-trichloro-1,2,2-trifluoroethane (30 ml) and isopropyl peroxycarbonate (IPP) (50 mg) were charged in an autoclave. After purging the autoclave internal atmosphere with nitrogen and evacuating the autoclave, vinylidene fluoride (32 g) was added and reacted at 50°C for 9 hours. The resulting mixture was dissolved in acetone and the solution was poured in a large amount of 1,1,2-trichloro-1,2,2-trifluoroethane to precipitate a copolymer (7.0 g). The content of the phosphonate ester monomer in the copolymer was 42 % by mole according to ¹⁹F-NMR. The copolymer had a number average molecular weight of 6000 (as converted to polystyrene) through GPC using tetrahydrofuran as solvent. The copolymer was dissolved in organic solvents such as acetone and tetrahydrofuran and gave a transparent film by casting from the solution. Example 2 Copolymerization of ethylene and CF₂=CFPO(OCH₃)₂ CF₂=CFPO(OCH₃)₂ (5 g), 1,1,2-trichloro-1,2,2-trifluoroethane (50 ml) and IPP (50 mg) were charged in an autoclave. After purging the autoclave internal atmosphere with nitrogen and evacuating the autoclave, ethylene (2.8 g) was added and reacted at 50°C for 24 hours. The resulting mixture was dissolved in dimethylformamide and the solution was poured in a large amount of 1,1,2-trichloro-1,2,2-trifluoroethane to precipitate a copolymer (5 g). The content of the phosphonate ester monomer in the copolymer was 32 % by mole according to ¹H-NMR. The copolymer had a number average molecular weight of 5200 (as converted to polystyrene) through GPC using tetrahydrofuran as solvent. Example 3 Copolymerization of vinylidene fluoride and CF₂=CFCF₂PO(OC₂H₅)₂ CF₂=CFCF₂PO(OC₂H₅)₂ (10 g), CF₂ClCFClCF₂CFCl₂ (80 g) and IPP (40 mg) were charged in an autoclave. After purging the autoclave internal atmosphere with nitrogen and evacuating the autoclave, vinylidene fluoride (32 g) was added and reacted at 50°C for 20 hours. The resulting mixture was dissolved in acetone and the solution was poured in a large amount of CF₂ClCFClCF₂CFCl₂ to precipitate a copolymer (7 g). The content of the phosphonate ester monomer in the copolymer was 8 % by mole according to ¹⁹F-NMR. The copolymer had a number average molecular weight of 19,000 (as converted to polystyrene) through GPC using tetrahydrofuran as solvent. Example 4 To a copolymer having a number average molecular weight of 6000 and a monomeric composition of vinylidene fluoride:CF₂=CFPO(OCH₃)₂ of 62:38 (2 g) which contained 6.79 x 10⁻³ mole of the phosphonate eater groups, water (10 g) was added and then 1N aqueous solution of sodium hydroxide was dropwise added while stirring. As a pH indicator, phenolphthalein in ethanol was used. After adding 2 ml of 1N aqueous solution of sodium hydroxide, the copolymer was completely dissolved in water. The modified copolymer was recovered by evaporation to dryness. According to ¹H-NMR (solvent: D₂O), about 6 % of the ester groups were hydrolyzed. The methyl ester of phosphonic acid is hydrophilic, and hydrolysis of 6 % of the ester groups made the copolymer water soluble. Example 5 Copolymerization of vinylidene fluoride and CF₂=CFCF₂CF₂PO(OH)₂ CF₂=CFCF₂CF₂PO(OH)₂ (6.5 g) and water (100 ml) were charged in a 400 ml stainless steel autoclave having a glass container. After purging the internal atmosphere with nitrogen, vinylidene fluoride was injected to a pressure of 17.5 kg/cm²G. After raising the mixture temperature to 60°C, an aqueous solution of ammonium persulfate containing 300 mg of ammonium persulfate was added. After 19 hours, the polymerization reaction was terminated and the reaction mixture was washed with water, hydrochloric acid and methanol successively, followed by evaporation to dryness to obtain a copolymer. The copolymer was a colorless transparent material and could be dissolved in dimethylformamide but not in acetone. According to ¹⁹F-NMR, the copolymer contained 6 % by mole of phosphonic acid monomer units. Example 6 A copolymer of vinylidene fluoride and CF₂=CFPO(OCH₃)₂ having a number average molecular weight of 6000 and containing 30 % by mole of the phosphonate ester units was alkaline hydrolyzed. To the resulting aqueous solution of the copolymer, a 5 % aqueous solution of ZnCl₂ was dropwise added while stirring to precipitate a white copolymer. When a salt of Na⁺ or K⁺ was added, no white polymer was precipitated. To the aqueous system containing the white copolymer, 10 % by weight hydrochloric acid was dropwise added. Around pH of 4, the copolymer became water soluble. Further addition of the hydrochloric acid precipitated the copolymer again. Example 7 A copolymer of ethylene and CF₂=CFPO(OCH₃)₂ having a number average molecular weight of 5200 and containing 32 % by mole of the repeating units derived from CF₂=CFPO(OCH₃)₂ (1 g) was added in 1N aqueous solution of sodium hydroxide (20 ml) and hydrolyzed at room temperature for 120 minutes. The hydrolyzed copolymer had a composition distribution, and a part of the copolymer was not dissolved in water. When 10 % by weight hydrochloric acid was added to a supernatant solution, the system became white turbid and then the copolymer precipitated.

Claims: 1. A fluorine-containing copolymer comprising 40 to 99 % by mole of repeating units derived from an olefin of the formula: wherein R¹, R², R³ and R⁴ are the same or different and each a hydrogen atom or a fluorine atom, or one of them is a chlorine atom and the rest of them are fluorine atoms, and 1 to 60 % by mole of repeating units derived from a vinylphosphonic acid derivative of the formula: wherein R groups are the same or different and each an alkyl group having 1 to 12 carbon atoms, an alkenyl group having 2 to 12 carbon atoms or a phenyl group, and n is 0, 1 or 2. 2. The fluorine-containing copolymer according to claim 1, which has a number average molecular weight of 1500 to 1,000,000. 3. The fluorine-containing copolymer according to claim 1, wherein a molar ratio of the olefin (I) to the vinylphosphonic acid derivative (II) is from 60:40 to 80:20. 4. The fluorine-containing copolymer according to claim 1, wherein the olefin (I) is selected from the group consisting of ethylene, monofluoroethylene, vinylidene fluoride, vinyl fluoride, trifluoroethylene, chlorotrifluoroethylene and tetrafluoroethylene. 5. The fluorine-containing copolymer according to claim 1, wherein the vinylphosphonic acid derivative (II) is selected from the group consisting of CF₂=CFPO(OCH₃)₂, CF₂=CFCF₂PO(OCH₃)₂, CF₂=CF(CF₂)₂PO(OCH₃)₂, CF₂=CFPO(OC₂H₅)₂, CF₂=CFCF₂PO(OC₂H₅)₂, CF₂=CF(CF₂)₂PO(OC₂H₅)₂, CF₂=CFPO(OC₆H₅)₂ and CF₂=CFPO(OCH₂CH=CH₂)₂. 6. A fluorine-containing copolymer comprising 40 to 99 % by mole of repeating units derived from an olefin of the formula: wherein R¹, R², R³ and R⁴ are the same or different and each a hydrogen atom or a fluorine atom, or one of them is a chlorine atom and the rest of them are fluorine atoms, and 1 to 60 % by mole of repeating units derived from a vinylphosphonic acid derivative of the formula: wherein R groups are the same or different and each a hydrogen atom, an alkali metal atom, an alkyl group having 1 to 12 carbon atoms, an alkenyl group having 2 to 12 carbon atoms or a phenyl group provided that at least 1 % of the R groups are hydrogen atoms or alkali metal atoms, and n is 0, 1 or 2. 7. The fluorine-containing copolymer according to claim 6, wherein at least 2 % of the R groups are hydrogen atoms or alkali metal atoms.

Inventors: NAKAMURA, TAKAYUKI, TATEMOTO, MASAYOSHI
Applicants: DAIKIN INDUSTRIES, LIMITED
Application year: 1990
Main classification: C08F214
IPC codes: C08F10, C08F210, C08F14, C08F30, C08F230, C08F8, C08F214