CATALYTIC COMBUSTION OF SOOT FROM DIESEL ENGINES

Abstract: In order to obtain a catalytic combustion of soot in exhaust gases from diesel engines the exhaust gases are conveyed over a catalyst material comprising vanadium and copper oxides in a molar ratio V:Cu of 85:15 to 95:5, preferably 90:10. In order to increase the low-temperature activity the catalyst preferably also contains elementary platinum, palladium or rhodium.

Description: CATALYTIC COMBUSTION OF SOOT FROM DIESEL ENGINES The present invention relates to a method for the combustion of soot from diesel engines and to a catalyst for use in this method. The invention makes it possible to efficiently purify the exhaust gases from diesel engines both with regard to CO and unburnt hydrocarbons and with regard to soot. Diesel engines have two major advantages over spark ignition engines. The fuel economy is 25-45% better, and the emissions of carbon monoxide (CO) and hydrocarbons are low. Because of the excellent fuel economy, the number of diesel-powered vehicles is expected to increase in the future, especially in a situation with high fuel prices. Although the emissions of carbon monoxide and unburnt hydrocarbons from diesel engines are low, something must be done in order to decrease the emissions of nitrogen oxides and soot particles. To cope with the emissions from spark ignition gaso- line engines, use is made of so-called three-way cata¬ lysts. In this case carbon monoxide and hydrocarbons in the exhaust gases reduce the nitrogen oxides by means of precious metal catalysts. This concept is applicable only when the concentration of oxygen in the exhaust gases is very low. Diesel exhaust gases contain approximately 10% of oxygen and only very low concentrations of carbon monoxides and hydrocarbons, for which reason three-way catalysis cannot be used for the exhaust gases from diesel engines. To decrease the emissions of nitrogen oxides, it has been tried to use exhaust gas recirculation and engine modifications. In the case of stationary diesel engines, one has also used selective catalytic reduction of nitro¬ gen oxides with ammonia [cf. P. Schoubye, K. Pedersen, P.S. Pedersen, 0. Grøne and 0. Fanøe, "Reduction of NO - emissions from Large Diesel Engines", Proc. 17th CIMAC- cong., Warsaw, June 8-11, 1987]. However, these measures have no effect upon the emission of soot particles. The emission of soot particles is, however, the most serious problem of diesel engines. One method of solving this problem is to separate the soot particles from the exhaust stream through filtration [cf. C.S. Weaver, SAE 840174, 1984 (109)]. Porous ceramic materials are usually used as filters. As the exhaust gas temperature seldom exceeds 573°K, the soot particles will accumulate in the soot trap. This causes a dramatic in¬ crease in the pressure drop through the trap. It is there- fore necessary to periodically regenerate the trap by com¬ bustion of the trapped particles. Different methods have been used in order to regene¬ rate particle traps [cf. C.S. Weaver, SAE 840174, 1984 (109)] . These methods can be divided into catalytic and non-catalytic methods. In the former case, fuel additives (i.e. organomefcallic compounds) and catalytic coating of the traps have been used. In the latter case, the trap is heated electrically, or by a burner. By throttling the intake air, the exhaust gas temperature is raised suffi- ciently to burn out the trapped particles. Non-catalytic methods often result in complicated and expensive systems, and the catalytic methods are at present not sufficiently effective. Most catalysts published in this field (e.g. EP-A-0,077,524, EP-A-0,164,182, US-A-4,510,265 and Japa- nese Patent Publication JP 59/186643-A2, October 23, 1984) make it possible to combust particles at temperatures abov-e 673°K. However, as mentioned earlier, diesel exhaust gases seldom reach temperatures above 573°K. This is a dilemma and will result in an extensive accumulation of diesel soot in the particle trap, and this again causes a further problem since the combustion process is highly exothermic, causing the temperature to rise dramatically when the soot eventually ignites. At such temperatures, the trap will crack or even melt down. During our research work which resulted in the pre¬ sent invention, we found very few publications on cata¬ lytic combustion of exhaust gases from diesel engines. Due to this fact, mechanisms for catalytic burning of carbon (graphite and activated carbon) were studied. In this field, a relatively large number of studies have been done [see e.g. D.W. McKee, Carbon, 8 (1970) 623; D.W. McKee, Carbon, 8 (1970) 131; D.W. Mckee, Fuel, 62 (1983) 170; R.T.K. Baker and J.J. Chludzinski Jr., Car¬ bon, 19 (1981) 75]. Usually, carbon has been impregnated with solutions of transition metal salts. The combustion experiments have then been carried out in TGA-apparatus (TGA = thermogravimetric analysis). In this case, the carbon is placed in a balance and a gas mixture contain¬ ing oxygen is conducted over the bed of carbon. The tem¬ perature of the gas stream is measured. Since there is no gas flow through the bed, the cooling will be insuffi- cient, and the temperature in the bed will rise due to the highly exothermic nature of the combustion of carbon. The actual temperature in the carbon bed could thus be much higher than the temperature measured in the gas stream. Because of the poor flow conditions, there will also be a pronounced risk of diffusion limitations during the combustion process. The specific surface areas for activated carbon and diesel soot are quite high. Due to this fact, the catalytically active material will be well dispersed on the surface, resulting in a good contact between the carbon and the catalyst. In an investigation performed by McKee [D.W. McKee, Carbon, 8 (1970) 623], graphite was impregnated with solutions of metal salts and then combusted. The investigations performed by McKee showed that oxides of Pb, V and Mn increased the combus- tion rate significantly, and that Ag and oxides of Co had intermediate activities, whereas precious metals were relative inactive. A similar investigation by Murph et al [M.J. Murph, L.J. Hillenbrand and D.A. Trayser, United States Environmental Protection Agency, R & D Program Report EPA-600/7-79-232b, Oct. 1979] using graphite con¬ firmed the high activity of oxides of Pb and Mn. 4 In the experiments reported above, graphite and ac¬ tivated carbon were used. However, literature reports some experiments in which diesel soot was mechanically mixed with metal oxide-based catalyst material and then burnt, 5 using thermogravimetrical analysis methods (TGA analysis). Watabe et al [Y. Watabe, K. Irako, T. Miyajima, T. Yoshi- moto and Y. Murakami, (SAE spec. publ.). SAE, 830082 (1983) 45, and European Publication EP-A-0,092,023] have conducted such experiments and reported that oxides of 10 vanadium and molybdenum were the most active, but that oxides of Cu were also relatively active, whereas oxides of Rb and Mn had low activities for the combustion of diesel soot. Also this investigation showed that precious metals were inactive for burning diesel soot. Watabe et al 15 also investigated if the mixing technique was of impor¬ tance to the combustion process. These authors tried mechanical mixing in the presence and in the absence of acetone, but were unable to notice any difference. The catalyst Compositions reported by Watabe et al were, how- 20 ever, not suitable for such a highly efficient purifica¬ tion of exhausts as is necessary in the purification of exhausts from diesel engine vehicles. The catalysts speci¬ fically mentioned by Watabe et al and containing both va¬ nadium and copper, had a ratio of 50:50 or 20:80 between 25 vanadium and copper. The experiments by Watabe et al pri¬ marily aimed at evaluating carrier materials for soot par¬ ticle traps, especially porous ceramical bodies, so-called ceramic foam. However, Watabe et al indicate that the catalysts of Cu-K-Mo and Cu-K-V in the ratios 4:4:2 should 30 be effecient catalysts. Yung Fang et al [Y. Fang et Y. Yao, Journal of Cata¬ lysis, 39 (1975) 104] have investigated the S0 2 deacti- vation of several metal oxide catalysts in the combustion of CO and hydrocarbons. Their study shows that oxides of 35 manganese are very susceptible to poisoning by S0 9 . How¬ ever, these authors conclude that oxides of Cu have a re¬ latively good S0 2 stability. On the other hand, their study did not comprise Ag or oxides of Pb and V. It is, however, reasonable to believe that oxides of V have a higher resistance to SO.-, poisoning. This statement is supported by I. Nam et al [I. Nam, J.W. Eldridge and J.R. Kittrell, Ind. Eng. Chem. Prod. Res. Dev., 25 (1986) 192] who found that S0 2 deactivation in selective catalytic reduction of nitrogen oxides with ammonia was caused by plugging of the pore system of the catalyst by compounds containing sulphur and ammonia. No poisoning of the V-O t - phase as such could be detected. As will be explained in the following, soot has an extremely complicated composition. The soot contains sul¬ phur compounds and transition metals as well as hydrocar¬ bons. All of these components will affect the combustion process. An important problem is the fact that large amounts of S0 2 will desorb during the heating of the die¬ sel soot. This results in an immediate poisoning of oxides susceptible to sulphur, such as oxides of Mn and Pb. Soot particles are built up of small spherical pri- mary particles composed mainly of carbon and having a diameter in the range of 20-60 nm, which is typical of soot formation in the gaseous phase. These primary par¬ ticles agglomerate to form secondary aggregates. The agglomeration already starts in the combustion chamber and continues all the way through the exhaust system. The secondary particles can become rather large, but more than 90% of these particles have a diameter below 300 nm. Large hydrocarbon molecules are condensed on the soot particles at the temperatures prevailing in diesel exhausts. The chemical composition of soot particles has been reported in literature [e.g. M. Mashaly, F. Nevejans, P. Sandra and M. Verzek, Proc. Int. Symp. Capillary Chro- matografy, 6, 340 (1985); and K-H Lies, A. Hartung, A. Postulka, H. Gring and J. Schulze, Dev. Toxicaol. Environ. Sci, 13, 65 (1987)]. An elementary analysis of diesel soot [E. Goldenberg and P. Degobert, Revue de L'lnstitut Fran- cais du Petrole, 41 (6), 797 (1986)] shows that, in addi- tion to carbon, soot also contains hydrogen, nitrogen, oxygen, sulphur and a number of other elements in trace amounts. A representative diesel soot contains approxi¬ mately 70 wt% C, 20 wt% 0, 3 wt% S, 1.5 wt% H, <1 wt% N and <1 wt% trace elements. The composition of elementary components in the soot may vary considerably depending on the fuel quality, the engine efficiency and the running conditions. According to Otto et al [K. Otto, M.H. Sieg, M. Zinbo and L. Bartsiewicz, "SAE Congress and Exposi- tion", SAE 800336, 277 (1980)] the amount of volatile hydrocarbons can vary between 10 and 90 wt%. Fresh soot particles contain a higher level of volatile hydrocabons than soot particles aged in the exhaust manifold. Because diesel fuel contains sulphur, relatively large amounts of sulphur are also found in the soot particles. The nitrogen content of diesel soot has -its origin in nitrogen oxides formed during the combustion process. Through reactions between nitrogen oxides and aromatic hydrocarbons, aroma¬ tic nitro and nitroso compounds can be produced. Some of these compounds are highly mutagenic. The trace amounts of other elements, mainly metals, have their origin in the fuel or in the lubricating oil. These trace elements are incorporated into the soot particles during the combustion process. As mentioned before only few studies exist on the combustion of diesel soot. These studies show that com¬ bustion rates are much higher with diesel soot than with graphite or activated carbon. Otto et al thus obtained results showing that the combustion rates were approxi- mately 100 times higher with diesel soot than with gra¬ phite. The investigations by these authors also show that the reaction between diesel soot and oxygen can be de¬ scribed satisfactorily by first order kinetics in respect of oxygen. The physical characteristics of diesel soot change as the combustion proceeds. Otto et al showed that the speci- 2 fie area of diesel soot increased from 100 m /g initially 2 to over 300 m /g when 70% of the soot was burnt. Thus, not only the chemical, but also the physical characteristics of the soot particles are changed during combustion. The hydrocarbons in the soot can be classified into different groups, depending on their chemical characteris¬ tics [cf. G. Hunter, J. Scholl, F. Hibbler, S. Bagley, D. Leddy, D. Abata and J. Johnson (SAE Spec. Publ.), SAE, 810263 (1981) 111]. Several of these are mutagenic sub¬ stances. Since the soot particles are very small, they can easily reach far down into lung tissue when inhaled. For this reason, these emissions have a decided impact on human and animal health. This indicates the importance of an efficient purification of diesel engine exhausts, espe¬ cially with regard to soot. The European Document EP-A-0,092,023 mentioned above relates to a catalyst which may contain vanadium and copper in mixture ratios which, according to the Examples, are given as 50:50 and 20:80, respectively. However, in this document Watabe et al emphasise catalysts of Cu-K-Mo and Cu-K-V in the ratios 4:4:2 which are said to be the most effective catalysts. The European Document EP-A-0,225,595 relates to a highly active catalyst for burning of hydrocarbons. This publication does not mention soot burning which differs substantially from the mechanisms of hydrocarbon burning. Thus, this document is not relevant to the burning of soot. No catalysts with vanadium and copper ratios accord¬ ing to the present invention are mentioned. The German Publication DE-A-3,623,600 relates to a catalyst which contains alkali metal and copper vanadate Cu 3 V 2° 8 and is used for lowering the ignition temperature of diesel soot. Also this document mentions no catalysts containing vanadium and copper in ratios according to the present invention. Known catalytic and non-catalytic methods for burning soot have different drawbacks which have limited their use. Therefore, there is a great need for highly active catalysts which can both enhance the burning of diesel soot and be regenerated continuously during their use. One object of the present invention is, therefore, to develop a highly active catalyst for burning diesel soot. Other objects will appear from the description below. The present invention is based on the insight that burning of diesel soot can be performed catalytically under the action of metal oxides and metals. The charac¬ teristic features of the invention are set forth in claims 1 and 5, especially preferred embodiments of the invention beiijag stated in the sub-claims. The research work on which the present invention is based was intended to try and establish which factors are important to obtain a highly active catalyst. The theories which were developed during the work indicated that a com¬ posite oxide having special and narrow molar ratios between V and Cu should be particularly active. This was verified and quantified by experiments, as will appear from the following and the Examples. The literature and patent publications referred to above do not contain any information pointing to a surprising improvement of the effectiveness when changing the molar ratio between V and Cu considerably, compared to what has been mentioned in this literature and patent publications which seem to point away- from ;he present invention. The present invention relates to a method of purify¬ ing exhaust gases from diesel enginges by catalytic burn¬ ing of soot and hydrocarbons, in which method the exhausts are conveyed at a temperature of at least 300°C, prefer- ably at least 350°C, over catalyst-containing vanadium and copper oxides carried by a carrier, this method being cha¬ racterised by using a catalyst in which the molar ratio of V:Cu is from 85:15 to 95:5. The invention also relates to a catalyst for purify- ing exhaust gases from diesel engines, this catalyst com¬ prising a carrier and a catalytic material comprising oxides of vanadium and copper, the catalyst being charac- terised in that it contains vanadium and copper in a molar ratio of V:Cu of from 85:15 to 95:5. The experiments on which the present invention is based thus have shown that oxides of vanadium and copper are the only oxides capable of considerably increasing the combustion rate. V 2 0 5 has a superior activity at tempera¬ tures above 623°K, while CuO is the most active catalyst below this temperature. Since the soot phase is burnt mainly at temperatures above 623°K, V 2 0 5 is the most active catalyst for burning the non-volatile components of the diesel soot. Oxides of Mn and Cr as well as elementary Ag and Pt have high activities in the combustion of hydro¬ carbons that desorb from the diesel soot. On the other hand, oxides of Co, Fe, Mo and Pb have low activities in the whole temperature range 573-723°K studied. In the investigations on which the present invention is based, it was found that Ag, Pt and the oxides of Cu and Mn are somewhat less active after having come into contact with S0 2 . However, the activity of V.-0,- seems not to decrease in an appreciable degree when this oxide comes into contact with S0 2 . " The composite catalyst which, ac¬ cording to the invention, contains V and Cu in a molar ratio of 85:15 to 95:5, is not either affected to a higher degree by sulphur, which imparts to this catalyst excel- lent stability and long useful life. This is an advantage in a catalyst indended for use in the purification of ex¬ hausts from diesel engines. The reason for the high activity of V 2 0 g could pos¬ sibly be explained by its low melting point (963°K). At the Tamman temperature, the atoms in the structure obtain an appreciable mobility. This temperature is about half the temperature of the melting point. Baker and Chludzin- ski [R.T.K. Baker and J.J. Chludzinski Jr., Carbon, 19 (1981) 75] state in explanation of the observed mobility of the particles of CuO in a graphite matrix that the tem¬ perature was above the corresponding Tamman temperature (799°K). In addition, these authors state that CuO is transformed, at this temperature, from the non-wetting state into the wetting state. Since 2 0 5 becomes wetting at the Tamman temperature (482°K), the contact efficiency between -the soot and the catalyst will be promoted. Another explanation of the high activity of V 2 0 5 could be that vanadium can exist in several oxidation states at small energy differences. Because of this, vanadium can easily change ' its oxidation state during the catalytic prod ss. According to McKee [D.W. McKee, Carbon, 8 (1970) 623], the catalytic effect of _0 5 in the oxidation of graphite resulted from the interaction of graphite and V«0~ to give g 0 13 . Vg0 13 was then re-oxidised back to V^O by ambient oxygen. Such lower oxides are certainly intermediates in the cyclic oxidation-reduction processes whi<f_a lead to a catalytic combustion of graphite and soot. The investigations which have led to the present in¬ vention and have been performed with different ratios be¬ tween soot and catalyst, using different particle sizes, show that combustion occurs mainly on the external sur- faces of the particles, whereas the internal surfaces of the catalyst particles are important when desorbed hydro¬ carbons are to be combusted. As a summary of the investigations it can be con¬ cluded that oxides of vanadium are highly active in the catalytic combustion of diesel soot at temperatures above 573°K, especially above 623°K. Further, the experiments have confirmed other authors' statements that Ag, Pt and oxides of Cu, Cr and Mn have high activities at low tempe- ratures, when the combustion of desorbing hydrocarbons is important. Further, since copper oxides seem to have a somewhat higher resistance to sulphur than the above-men¬ tioned substances, this oxide has been used in the present invention. Another and much more important reason for com¬ bining oxides of vanadium and copper is the discovery of a synergistic effect between these oxides within a specific range of mixing ratios. Another finding during the experi¬ ments " is that the soot burning process takes place mainly O the external surfaces of the catalyst particles and is more pronounced at temperatures above 623°K. Furthermore, it has been found that a release of S0 2 during the heating of soot particles can result in an immediate poisoning of catalyst sensitive to sulphur. Another finding is that a long-term deactivation with S0 2 seems to reduce the acti¬ vity of copper oxide only to a low degree, but to result in a practically unchanged activity for vanadium oxides. These results confirm that a catalyst for burning diesel soot based on oxides of vanadium and copper should have a good resistance to sulphur poisoning. This surmise was confirmed in connection with the present invention. If it is desired to burn hydrocarbons desorbed from the diesel soot, the oxides of vanadium and copper may advantageously be used in combination with Ag, Pt, Rh or oxides of Mn. When using the present invention, the catalytically active material can be dispersed on a coating or a carrier of the type 2C-alumina for simulating the conditions in a particle trap. Thus, it is possible to use a wire netting filter, the wires of which have been coated with a layer which, in its turn, is impregnated with the catalyst mate¬ rial. However, the carrier preferred at present is a body of honeycomb structure. Such bodies are used to a great extent for exhaust purification devices for gasoline- powered vehicles and therefore are easily obtainable. Also these carriers may be coated with a layer which is impreg¬ nated with a catalytic material. Alternatively, the cata¬ lytic material may be impregnated directly into the car¬ rier. Also tube filters can be used, the tubes of which have been coated with the catalytically active material. The choice of carrier system depends on the construction of the exhaust system and can be left to the user of the method and the catalyst according to the present inven¬ tion. However, it is important that the carrier can with- stand the present high temperatures so that it is not necessary to impose temperature limitations during use of the exhaust purification device. As mentioned before, and when using the the method of the present invention to purify exhaust gases from diesel engines, the exhaust gases are brought into contact with the catalyst at a temperature of at least 300°C, prefer- ably at least 350°C. The upper temperature limit is set mainly by the ability of the carrier material and the en¬ closing receptacle to withstand high temperatures. A prac¬ tical upper limit can be 450°C or 500°C. The amount of active material (i.e. oxides of vana- dium and copper) which suitably is used in the catalyst is depending on the carrier used and the method used for coating the carrier with the active material. As a start¬ ing point it may be mentioned that, if the actual carrier consists of a wash coat of aluminum oxide or another com- parable high-temperature resistant material, a loading of 5-25 wt% active material, based on the mixture of carrier and active material, may be suitable, if the active mate¬ rial is distributed homogeneously in the coating. In its turn, this coating can be applied on another substrate, such as a monolith of honeycomb type. If one wishes to have a higher activity than that which is obtained at the lower end of the range, the lower limit may preferably be increased to 7.5 wt%. The upper limit has been given as 25 wt%, but higher loadings than 20 wt% do not signifi- cantly increase the activity. For economical reasons, the upper limit may therefore preferably be 20 wt%. Corre¬ spondingly, loadings of 0.01-25 wt%, based on the mixture of carriers (wash coat material), oxide of vanadium and copper and precious metal, can be used as starting points when dealing with loadings of platinum, palladium and rhodium. At an increase of loading at the lower end of this range, the additional activity is not very large, and for economical reasons the upper limit therefore is pre¬ ferably 0.1 wt%. The invention will now be described with reference to the attached drawings. Fig. 1 is a diagram showing the logarithmic combustion rate of diesel soot as a function of the inverted value of the temperature in a preliminary experi¬ ment. Fig. 2 is a diagram showing the selectivity for the pro¬ duction of CO as a function of the temperature in another preliminary experiment. Fig. 3 is a diagram showing the combustion rate as a function of the molar content of vanadium in a composite oxide catalyst according to the present invention. Fig. 4 is a diagram showing the relative EDAX signal from Al as a function of the content of active phase in a catalyst according to the present invention. Fig. 5 is a diagram showing the combustion rate as a func¬ tion of the content of active phase (90 mole% V, 10 mole% Cu) in a catalyst according to the presen invention. Fig. 6 is a diagram showing the selectivity for CO pro- duction as a function of the temperature for one example of a catalyst according to the present invention. Fig. 7 is a diagram showing the combustion rate as a func tion of the Pt content of a composite catalyst of vanadium and copper oxides and platinum according to the present invention. Fig. 8 is a diagram showing the combustion rate as a func tion of the calcination temperature in one example of a catalyst according to the present invention. Fig. 9 is a phase diagram for the system V 2 0 5 and CuO. Fig. 10 shows schematically an apparatus used in the expe¬ riments with the present invention. As mentioned above, the invention is based on the in¬ sight that vanadium pentoxide in combination with copper oxide is an effective catalyst for the combustion of diesel soot. In the following, results are presented from an investigation of a number of catalytically active mate¬ rials, mainly metal oxides, in the burning of diesel soot under conditions which resemble the conditions in particle 5 traps. The soot particles used in the experiments presented below were collected from the exhaust streams from diesel engines at Volvo Truck Corporation in Gothenburg, Sweden. After collection, the soot was kept in a closed vessel in 10 order to avoid desorption of volatile hydrocarbons. The chemical composition of the soot used in the experiments is given in Table 16, below. Fig. 10 shows schematically the apparatus used for the,experiments with the invention. This apparatus com- 15 prised three units, namely a gas mixing unit, a reactor unit and εap. analysis unit. The gas mixing unit comprised needle valves 1, rotameters 2, shut-off valves 3, reducing valves 4, and gas tubes 3 for oxygen and nitrogen. The gas mixing unit further comprised another needle valve 1A for l≥O regulating the mixed flow of oxygen and nitrogen, and an outlet valve IB. A rotameter 2A was connected in the line from the needle valve A, ahead of a manometer 6. At the outlέt of the gas mixing unit, there were a gas preheater - 7 and an injection pump 8 for supplying water to the line 25 " in which the gas stream was conveyed to a furnace 9 with a reactor. After the furnace, there were a cooling unit 10, an IR spectrometer 11, and a gas chromatograph. The tempe¬ ratures in the intake and outlet lines, and also in the reactor, were supervised by means of thermocouples 13. " 30 When using further gases, besides nitrogen and oxygen, one or more further sets of components 1-5 were connected ahead of the needle valve 1A. N 2' °2 an / 0 P ionall y- S0 2 t *• N 2•• , were supplied from separate gas tubes to the gas mixing unit. The different 35 gas flows were measured by the rotameters 2, the measured values of which were corrected with respect to the abso¬ lute pressure in the equipment. The partial gas flows were united to a total flow which was measured by a rotameter 2A. A flow divider consisting of the needle valve IB was installed to make it possible to vary the total flow through the reactor within wide limits, without having to change the partial flows from the various gas tubes. The inaccuracy of the flow setting was at most 5%. The preheater 7 for preheating the gas mixture before the inlet end of the reactor unit consisted of a tube hav¬ ing a length of one meter and being coiled with a resis- tance wire for electrical heating. After preheating, the gas mixture had a temperature of about 200°C. Before the introduction in the furnace, steam was added using the injection pump 8. The water injection was carried out with a syringe directly into the preheated gas mixture. After the water injection, the gas mixture was conveyed into the furnace where the final preheating to the prevailing tem¬ perature took place in a helically coiled tube having a length of 3 m. The furnace was designed for a maximum operation temperature of 700°C. The furnace was heated by resistant heating. A fan had been installed to increase the convection in the furnace. The temperature stability of the furnace was very good, and the temperature fluctua¬ tions were less than 0.2°C at 600°C. At maximum heating efficiency, the temperature could be increased by more than 30°C/min. in the furnace. The temperature in the furnace could be increased successively. After final preheating, the gas mixture passed through the reactor proper. The temperature at the inlet of the reactor, in the soot bed and in the outlet of the reactor was measured with the three thermocouples 13 (chromelalumel from Phillips) mentioned above. The tempe¬ rature at the reactor inlet was used as a signal to a regulator, while the two other thermocouples were con¬ nected in series so that the temperature difference between the soot bed and the reactor could be recorded. This made it possible to use the reactor temperature as a reference temperature, and the heating effect in the reac- tor zone could be followed with high accuracy; temperature differences of 1°C could be recorded. After leaving the reactor, the gas mixture was con¬ ducted through a cooler 10 which was a refrigerator in which the water was removed by condensation. When leaving the refrigerator 10, the gas mixture had a dew point of +4°C. The gas mixture was conveyed to an IR instrument 11 (Siemens Ultramat 22P) for 3 sec. after leaving the reac¬ tor, this indicating that the useless volumes were small. The IR instrument used could detect CO in the interval 0-300 ppm and S0 2 in the interval 0-1000 ppm. The measure¬ ment accuracy was <0.5% at a full turn of the instrument. A part of gas .flow was conducted through a T-tube to an injection valve on a gas chromatograph 12 (Hewlett Packard 5890 A). The column used in the equipment (Carbosiv IIS, 120/140 mesh, 10 ft, 1/4 inch) was able to separate air, CO, C0 2 , H 2 0 and S0 2 - In order to prevent S0 2 adsorption in the column, use was made of a silanised glass column. Both the IR instrument and the gas chromatograph were calibrated regularly, using a gas mixture with known con¬ tents of CO, C0 2 and S0 2 . During the experiments the con- centratiors of CO and C0 2 were measured and the combustion rate (r. . , expressed as nmole burnt carbon per second) was calculated. In some of the experiments, the gas mix- ture also contained S0 2 . The experiments were conducted to detect a possible catalyst deactivation due to sulphur poisoning. The running of the reactor was varied, but the maximal relative consumption of oxygen through the reactor never exceeded 5%. The standard deviation in the all the calculated combustion rates was less than 10%. The catalytically active material mainly consisted of metal oxides. In the particle traps, the catalytical active material was distributed on a coating (often y-Al 2 0 3 ) formed as a wash coat. In order simulate these conditions, use was made of J.-A1 2 0 3 particles having a diameter of 0.25 mm as carrier material. The carrier mate¬ rial for the experiments was obtained from Alcoa Chemi- 2 c'als, USA. The specific surface area was 290 m /g before impregnation. The catalysts were prepared by impregnating the car¬ rier material with aqueous solutions of different metal salts. All of the chemicals used were of analytical grade, and the water used was distilled twice. For platinum, a solution of H 2 PtCL β was used, and for forming V 2 0_ and Mo0 3 use was made of solutions of NH.V0 3 (oxalic acid) and (NH.)gMo 7 0 24 -4H 2 0, respectively. Otherwise, corresponding nitrates were used. After impregnation, the catalysts were dried at 383°K in an oven for 24 h. Calcination was per¬ formed in a reactor at 773°C in air for 1 h. The Pt-cata¬ lyst was reduced in similar manner for one hour in an atmosphere containing 5% H 2 , the balance being N ? . All catalysts, except the Pt-catalyst, contained 10 wt% active material (calculated on the corresponding metal). The Pt- content of the Pt-catalyst was 1 wt%. Higher levels are not realistic due to the high price of precious metals. Since the outer surface of the particles should be important in the burning of soot, small fractions should not be prepared by milling after impregnating the carrier material with the active phase. Instead, the carrier mate¬ rial should be milled to the suitable grain size before impregnation. The experimental procedure was as follows: Mechanical mixtures of diesel soot and catalyst (0.05 g soot and 0.5 g catalyst) were used in these expe¬ riments. The mixtures were placed in the reactor. Unless otherwise indicated, gas mixture containing 6% 0- and 7% H 2 0, the balance being N 2 , was conducted through the reac¬ tor at a flow rate of 90 1/h. The temperature in the reac¬ tor was increased by 5°K per minute to 698°K. The combus¬ tion rate r. t (nmole per second) was calculated at dif¬ ferent temperatures. The ratio between the amount of soot and the amount of catalyst decreased slowly during the experiments as the soot phase was combusted. It is therefore important to select such conditions that the soot is in excess during the whole experiment. If the experiment takes too long (i.©_ too low a temperature rise rate), or if the initial soot:catalyst ratio is too low, the catalyst will be in excess at the end of experiment. Conversely, if the tempe¬ rature-rise rate is too high, the conditions will be far from stationary, with ensuing local overheating in the bed and a decided risk of ignition. If the soot: catalyst ratio is too high, it is difficult to detect the catalytic activity as soot is combusted also in the absence of cata¬ lysts. Practical tests showed that a temperature rise rate of 5°K/min. and an initial soot:catalyst ratio of 0.1 (on weight basis) satisfy the above requirements. In the experimental results described below the soot was burnt catalytically in two different ways, on the one hand in the form of mixtures of soot and carrier material and, on the other hand, as mixtures of catalysts, carrier material and soot. EXAMPLE 1 This Example is a preliminary experiment for compari¬ son, showing that diesel soot is combusted also in the absence of catalyst material. In the experiment using the test equipment described above, a mixture of 0.05 g soot and 0.5 g #-alumina was placed in the reactor. The experi- ment was considered important to verify that alumina nor¬ mally is inactive at combustion reactions. The total gas flow rate was 901/h. The temperature increase rate was 5 c K/min., and the gas mixture consisted of 6% 0« and 7% H 2 0, the balance being N 2> Fig. 1 shows the combustion rate as a function of the inverted value of the tempera¬ ture in an Arrhenius graph. The measured values are given in Table 1, below. The combustion rate increased from 200 nmole/s. to 280 nmole/s. when the temperature was raised from 673°K to 773°K. The product gas was analysed for both CO and CO- to make it possible to calculate the selectivities. These selectivities have no fundamental significance, since they are the result of secondary reactions at which CO is oxidised to C0 2 . However, in this case it is important to know how much CO has been produced during combustion. If too much CO is reduced, this would lead to an increased emission of CO from the diesel vehicle. As will appear from Fig. 2 and Table 2, the selecti¬ vity for the production of CO reached a maximum of 16% at 698°K. It is important to realise that this selectivity is partly the result of secondary reactions, at which CO is oxidised to C0 2 . EXAMPLE 2 Preliminary experiments were carried out also with mixtures of catalyst and soot. These experiments were performed using a number of metal oxides, and also using the metals Ag and Pt. The same gas flow rates and tempe¬ rature rise rates as in Example 1 were used, with the exception of the oxide mixture V 2 0 5 /CuO (90 mole% V, 10 mole% Cu). A mixture of 0.05 g soot and 0.5 g catalyst and carrier, respectively, was placed in the reactor. When using a catalyst, the catalytical material consisted of 10 wt% active phase and 90 wt% carrier material. To make it possible to evaluate whether a catalyst was active or not, the combustion rate obtained must be related to the com¬ bustion rates valid for mixtures of soot and alumina with- out any catalytically active material. The ratio between these combustion rates at different temperatures are reported in Table 3. The data in Table 3 indicate that, at temperatures below 623°K, mainly desorbed hydrocarbons are combusted. It can be established that CuO, Mn0 2 , Cr 2 ,0 3 , Ag and Pt are quite active in this low temperature range. At high temperatures (above 623°K), 2 0j.. has a superior activity. Since mainly the soot phase is combusted at these tempe¬ ratures, " 2 0,- is the most active catalyst for the combus- tion of soot. Several of the investigated catalysts failed to show sufficient activity to be of interest, i.e. oxides of CO, Fe, Mo and Pb. EXAMPLE 3 Since diesel exhaust gases contain S0 2 , it was con¬ sidered important to investigate whether the catalysts are susceptible to sulphur poisoning. Large quanities of S0 2 are released as the soot is heated (this may result in gaseous S0 2 concentrations as high as 100 ppm). Therefore, cataPLysts which are very susceptible to sulphur were deac¬ tivated immediately during the experiments. Deactivation was performed in a specially designed reactor. The gas mixture containing 1000 ppm S0 2 and 10% 0 , the balance being N-, was conducted through the cata- h i lyst bed at 573°K and at a space velocity of 2000 for 8 h. After this deactivation, the catalysts were analysed in respect of their performance during combustion. Table 4 gives the ratio between the combustion rates for deactivated and fresh catalyst using 0.05 g soot and 0.5 g catalyst (containing 10 wt% active phase and 90 wt% car¬ rier material), a total flow rate of 90 1/h, and a gas composition of 6% 0 2 , 7% H 2 0 and 100 ppm S0 2 , the balance being N 2 . The temperature rise rate was 5°K/min. As appears from the Table 4, the activity had decreased for CuO, Mn0 2 and Ag. Pt was less active at low temperatures after deactivation, whereas V 2 0 5 seems to have been acti¬ vated by S0 2 . EXAMPLE 4 Considering the good results reported above, using V 2 0 5 as a catalyst for the combustional soot from diesel engines, further experiments were carried out in order to investigate the value of mixtures of oxides or vanadium and copper in the catalytic combustion of diesel soot. The catalysts used in the following were prepared by repeated impregnation of y-alumina with aqueous solutions of NH.VO (oxalic acid) and Cu(N0 3 ) 2 . After impregnation, the cata¬ lysts were dried at 383°K for 24 h and then calcined at 773°K in *ir for 1 h. The catalysts nominally contained 10 wt% active phase and had different V:Cu ratios. The various catalysts, the results from EDAX analyses and the specific surface areas are shown in Table 5. From this Table, it can be seen that the agreement between the calculated and the actual sur¬ face compositions is rather good for the catalysts con¬ taining much vanadium. The agreement is poorer for the catalysts containing only small amounts of vanadium. The 2 specific surface area descreased from a value of 290 m /g (for the carrier before impregnation) to values around 2 200 m /g. This is due mainly to clogging of the minor pores during the impregnation step. In addition, the car¬ rier may have sintered to some extent during the calcina¬ tion. The combustion experiments were carried out using a mixture of soot and catalyst (0.05 g soot + 0.5 g cata¬ lyst) in a flow reactor. The catalyst contained 10 wt% active phase. The gas mixture contained 10% 0 2 and 7% H~, the balance being N 2 , and was conducted through the reac- tor at a total flow rate of 901/h. The temperature was increased at a temperature rise rate of 5°K/min. to 698°K. The specific surface areas of the catalysts used in the following were measured using an area meter (FlowSorb II from MicroMeritics) through adsorption of N 2 according to the one-point BET method. The catalysts were flushed with N 2 at 623°K for 1 h prior to these measurements. The surface composition of the catalysts was deter¬ mined using a scanning electron microscope (ISA-100 A) combined with an EDAX equipment (PGT 100 Alpha System) (EDAX = Energy Dispersive Analysis of X-ray). The qualitative bulk compositions were determined using X-ray defraction studies (Phillips PV 1710). The investigations were carried out on powdered catalysts at room temperature. An X-ray source from Phillips was used [Cu(K . , λ=0.154056 nm] . The equipment was calibrated with a Si-standard. The soot particles used in these experiments were the same as described above and in Table 16. The combustion rates are shown as a function of the molar fraction of vanadium in the catalyst surface in Fig. 3. The corresponding numerical values are given in Table 6. The activity of pure 2 0 5 is relatively low at temperatures below 623°K. Conversely, this low-temperature activity is rather high in the case of pure CuO at tempe¬ ratures above 623°K. The isotherms have a maximum as a function of the molar fraction of vanadium (maximum at V - 0.9, at temperatures above 598°K. This synergistic effect is pronounced at temperatures between 648°K and 698°K. In this temperature range, the combustion rates are 50% higher than those obtained for pure V 2 O j -. The low temperature activity is maintained up to a molar fraction of 0.95 in respect of vanadium. These results show that it is possible to obtain synergistic effects for mixtures of V ? 0_ and CuO. The synergistic effect observed for mixtures of V o _i0b_- and CuO can be partly explained by the low melting point of the mixture of oxides. A phase diagram for the system V 2°5~ Cu0 is shown in Fi _f- 9, from which it appears that a melting point minimum (903°K) occurs at a molar amount of 0.82 V, i.e. very close to the activity maximum observed at the molar amount of 0.9 according to what is stated above. The molar fractions which fall within the invention have been marked with a hatched area. If the molar amount * of Cu is increased, the melting point quickly rises. This may be an explanation of the lower activity of catalysts rich in Cu. As appears from Fig. 3, the activity at low temperatures (<623°K) is high for catalysts rich in Cu. At such low temperatures, the hydrocarbon combustion is considerable. CuO is much more active than V ._.0o, in com- bustion of hydrocarbons. The high low-temperature activity is extended to such high molar fractions of vanadium as 0.95. This means that the catalyst having the best high- temperature activity (molar fraction 0.9 V) also has a high low-temperature activity. Even if the improved contact efficiency could be the main reason for the observed synergistic effect, the pre¬ sence of Cu could change the net oxidation state of the vanadium phase and introduce lattice defects. According to Berg et al [J. van den Berg, J.H.L.M. Brans-Brabant, A.J. Dillen, J.W. Geus and M.J.J. Lammers, Ber. Bunsenges, Phys. Chem., 87(1983) 1204], several investigations show that the catalytic activity of V 2 0 5 is enhanced when the concentration of lattice defects is increased. These lat- tice defects consist of oxygen vacancies (or V 4+-ions). According to Berg et al, the metal in M V.,0,- is single- ionised, whereas the corresponding numb x er of V5+ is re- duced to V 4+. In this way, the net oxidation state of the vanadium phase will be somewhat less than +5. The choice of carrier is also important to the development of lattice defects. If the interaction between the carrier and the oxide phase is high, as in the case of alumina, the lattice defects will be stabilised and could survive a high mobility of the structure (i.e. high temperatures). EXAMPLE 5 Experiments were performed to investigate how the amount of active phase influences the result. The test conditions stated in Example 4 were used during these experiments. To investigate how the amount of active phase (V 2 0 5 /Cu0; 90 mole% V, 10 mole% Cu) may influence the com¬ bustion rate, a series of catalysts with different load¬ ings of active phase were prepared. These catalyst compo- sitions, the true surface surface compositions and the specific surface areas are given in Table 7, from which it is obvious that the amount of Cu in the active phase is somewhat too high in these cases. The catalyst composi¬ tions lie on the Cu-rich side of the activity maximum in Fig. 3. The specific surface area is hardly affected by the amount of active phase at loadings below 10 wt%. At higher loadings, however, the specific surface area 2 decreases dramatically from 202 m /g at 10wt% of active 2 phase to 47 m /g at 20 wt%. This reduction in specific surface area is mainly caused by clogging of the pore system with active phase. By measuring the EDAX signal from Al, it was possible to get a picture of the surface concentration of active phase. In Fig. 4 and Table 8, the relative signal from Al is shown as a function of the amount of active phase. The relative signal from Al decreases linearly as a function s of the amount of active phase up to a loading of 10 wt%. An increased surface concentration of the active phase on the carrier will lead to an enhanced activity. At low surface concentrations of active phase, i.e. when the surface is only partially covered with active phase, new catalytic sites are produced as the loading increases. At higher loadings, multiple loadings of active phase are formed, and no new sites are produced. As can be seen from Fig. 4, the surface concentration of active phase in¬ creases linearly up to a loading of 10 wt%. At still higher loadings, multiple layers are formed. The specific surface area decreases dramatically at loadings higher than 10 wt%, which is due to clogging of the pore system with active phase. If the inner surfaces were important in this reaction, a decrease in the specific surface area would lead to a decrease in activity. The combustion of the solid soot phase takes place mainly on the outer sur¬ faces of the catalyst grains. EXAMPLE 6 Experiments were also performed to determine the com- bustion rate as a function of the amount of active phase (V 2 0 5 /Cu0: 90 mole% V, 10 mol% Cu) at different tempera¬ tures. The results are given in Fig. 5 and Table 9. The combustion rates increase up to a loading of 10 wt% of active phase. A further increase in the loading does not increase the activity of the catalyst. EXAMPLE 7 This experiment aims at determining how an addition of platinum will influence a catalyst which is intended for combustion of diesel soot and is based on V„ __0,_ and CuO and contains V and Cu in the nominal mole ratio 90:10. The same test conditions as in Example 4 were used. As mentioned earlier, very small amounts of precious metals (palladium, platinum and rhodium) could enhance the oxidising activity of the catalyst based on metal oxides. This phenomenon can be explained by a process where 0 2 is adsorbed on the surface of the precious metal under dis¬ sociation and is then spread over the metal oxide phase where the oxidation reactions mainly take place. To find out in what way the precious metal should be added, four different catalysts according to Table 10 were prepared. With regard to catalysts Nos. 1 and 2, the car¬ rier material was first impregnated with a solution of H 2 PtClg. This Pt precursor was then decomposed in an oxidising (catalyst No. 1) or in a reducing (catalyst No. 2) atmosphere. After this step, the catalysts were impregnated with solutions of NH.V0 3 and Cu(N0 3 ) 2 , dried and calcined in the usual manner. Catalysts Nos. 3 and 4 were impregnated with solutions of NH.V0 3 and Cu(N0 3 ) 9 prior to the impregnation with H 2 PtCl g . Catalyst No. 3 was oxidised, whereas catalyst No. 4 was reduced prior to cal¬ cination. The ratios between the combustion rates obtained for the different Pt-containing catalysts and the reference without Pt are given in Table 10. The addition of Pt en- hances the activity distinctly at temperatures below 648°K. At temperatures above 648°K, the addition of Pt has no effect. The results show that the precious metal should be disposed on the metal oxide phase rather than on the carrier. In addition, H 2 Cl g should be decomposed in a reducing atmosphere. 26 Earlier investigations [D.W. McKee, Carbon, 8 (1970) 623] state that precious metals are inactive in the cata¬ lytic combustion of carbon and soot. Precious metals are, however, very active in the oxidation of CO and hydrocar- * bons. The melting point of Pt is rather high, 2046°K. Because of this, the contact efficiency between the cata¬ lyst and the soot phase will be poor and the catalytic activity low. As will be seen from Table 10, very small amounts of Pt dispersed in the metal oxide phase distinct- ly increase the activity at low temperatures. At lower temperatures, mainly hydrocarbons are combusted. At higher temepratures, i.e. when the solid soot phase is combusted, the addition of Pt has no effect. Another advantage by adding Pt is that it suppresses the production of CO. In the absence of Pt, the selectivity for production of CO could be as high as 12.7 in this case. If 0.1 wt% Pt is added to the catalyst, this value is reduced to about 2%. These investigations show that Pt should be dispersed in the oxide phase rather than in the carrier. In this way, Pt ill be closer to the zones where the combustion reac¬ tions mainly take place. If the activity is explained by a dissociative adsorption of oxygen followed by a surface diffusion of oxygen atoms to the oxide phase, these pro¬ cesses should be enhanced by a good contact between Pt and the oxide phase. The Pt precursor, i.e H 2 PtCl g , should be decomposed in a reducing atmosphere. It is known that surface oxides, and even bulk oxides of Pt, could be pro¬ duced at low temperatures in an oxidising atmosphere. Through reducing decomposition of H 2 PtCl fi , metallic pla- tinum is formed. This fact could explain why the activity is higher for the catalyst that has been reduced prior to calcination. If the Pt loading is increased above 0.1 wt%, no further increase in the activity could be observed, whi h-.probably is due to the fact that the combustion of desorbed hydrocarbons is close to 100%. EXAMPLE 8 Even though the selectivity for CO production is a result of secondary reactions, it is of value to show how it is affected by the addition of Pt. To investigate this, a catalyst was used consisting of a carrier of y-Al 2 0 3 and 10 wt% active phase. The active phase contained 90 mole% V and 10 mole% Cu. The Pt loading was 0.10 wt%. The test conditions were the same as in Example 4. Fig. 6 and Table 11 present the selectivity for CO production as a function of the temperature for a reference sample without platinum and for a Pt-containing or Pt-enhanced catalyst. Both catalysts contained V 2 0 5 and CuO in the nominal mole pro¬ portion 90:1 between V and Cu. At 623°K the selectivity was 12.7% for the reference catalyst. At the same temperature the selectivity for the Pt-containing catalyst was 2%. This indicates that the Pt loading has a great influence on a catalyst according to invention. EXAMPLE 9 To determine the effect of the amount of Pt loading, a series of experiments were performed, using the same test conditions as in Example 4. The series of catalysts with different amounts of Pt was prepared according to a method which gave the most active catalyst in accordance with the statements in the preceding Example. The carrier was impregnated with solutions of NH.V0 3 and Cu(N0 3 )^. After these steps the catalyst was impregnated with a solution of H 2 PtCl g . The catalyst was then dried, reduced at 773°K (in a gas mixture containing 5% H~ and balance N 2 ) during 1 h and finally calcinated for 1 h at 773°K in air. The Pt loadings of the catalysts are given in Table 12. The combustion rate was plotted as a function of the Pt loading in Fig. 7. The corresponding figures are given in Table 12. From Fig. 7, it can be seen that very low amounts of Pt (0,01 wt%) enhance the combustion rate at low temperatures. At Pt loadings above 0.10 wt%, no fur¬ ther increase in activity is obtained. EXAMPLE 10 In this Example, the effect of the calcination tem¬ perature on the catalyst function was investigated. The catalyst consisted of 2 0 5 and CuO on A1 2 0 3 (10% active phase; nominally 90 mole% V and 10 mole% Cu in the active phase). The temperature of diesel exhaust gases is normally below 573°K. At high speed and heavy load operation, how¬ ever, the temperature may get as high as 873°K. If the exhaust temperature is low (<573°K) for a long period of time, this will lead to an extensive accumulation of par¬ ticles in the particle trap. If the exhaust gas tempera¬ ture now rises sufficiently, the soot will ignite. The heat generated during the combustion will lead to a dra- matiσ increase of the temperature in the trap (tempera- tures as high as 1273°K are possible). It is therefore of importance to investigate the temperature stability of the catalyst. A series of catalysts containing 0,10 wt% Pt apart from V 2 0 5 and CuO in the nominal mole ratio 90:1 between V and Cu, as prepared according to the method described above. Calcination was carried out at different temperatures in the interval 773-1073°K. In Table 13, the catalyst compositions, the EDAX analysis and the specific surface areas are given. The specific surface area has decreased dramatically through the heat treatment, from 196 m 2 /g at 773°K to about 2 m 2 /g at 1073°K. This reduc¬ tion is caused by sintering of the carrier material and transformation of y-alumina into alumina. X-ray diffraction studies have shown that the car- rier material mainly is in the form of y alumina in the catalyst which was calcined at 1073°K. As the calcination temperature is increased, 8 alumina and θ alumina are formed. After calcination at 1073°K, also a alumina could be detected. It is apparent that an extensive sintering and phase transformation has occurred during the high temperature calcination. In addition, several reflexes from the active phase could be observed for the catalyst calcined at temperatures above 873°K. As the specific surface area has decreased to such an extent, the dis¬ persion of the active phase becomes poor, i.e. bulk com¬ pounds are produced. Such crystalline bulk compounds could be detected by X-ray analysis. It was, however, not possible to determine any specific phase in these cases. Probably it is a solid solution of several phases with disordered structures. Because of this, the d values will be shifted away from the values given in the handbooks. For the catalysts calcined at temperatures <873°K, the active phase is probably well dispersed on the carrier since the specific surface area still is high (196 and 2 71 m /g, respectively). The combustion rate is shown as a function of the calcination temperature in Fig. 8. The corresponding values are given in Table 14. The activities at low tem¬ peratures decrease dramatically as the calcination tem¬ perature is increased, which is due to the structural break-down of the catalyst leading to a dramatic reduction in the specific surface area. Mainly hydrocarbons are com¬ busted at temperatures below 623°K. This combustion pro¬ cess takes place also on the inner surfaces of the cata¬ lyst. The combustion of the solid soot phase, however, mainly occurs on the outer surfaces of the catalyst. As the outer surface area is relatively unaffected by the calcination, the high temperature activity should be main¬ tained. Fig. 8 shows that the activities at temperatures above 623°K even increase as the calcination temperature is increased. EXAMPLE 11 In this Example, the effect of S0~ on a composite catalyst having V 2 0 5 and CuO in the nominal ratios 10 mole% Cu and 90 mole% V is investigated. To investigate if the catalyst is susceptible to sulphur poisoning, experiments were carried out with 200 ppm S0 2 in the gas mixture. In Table 15, the ratios between the combustion rates obtained in the presence and in the absence of S0 2 are shown at a number of tempera¬ tures. As will be seen from this Table, the catalyst is unaffected by the presence of S0 2 . The concentration of S0 2 in diesel exhaust gases is normally lower, seldom above 100 ppm. The deactivation experiments with S0 2 (200 ppm) in the gas mixture show that the catalyst is unaffected. Since large amounts of S0 2 are released on heating of the soot, susceptible catalysts should be deactivated imme- diately during these experiments, also if no gaseous S0 2 i_^ supplied. These investigations show that a mixed oxide of V 2 0_. and CuO (a molar fraction of about 0.9 V) is very active in the combustion of diesel soot. Small amounts of Pt en- ance its ability to combust hydrocarbons and carbon monoxide. As an alternative to platinum, also palladium or rhodium can be used. The ability of the catalyst to com¬ bust diesel soot is not affected by S0 2 or temperature shocks. Summing up, it is found that a mixed oxide of V __0 D.- and CuO having a molar fraction of 0.85-0.95 V and 0.15-0.05, respectively, has a high activity in the com¬ bustion of diesel soot. The combustion of the solid soot phase takes place mainly on the outer surfaces of the catalyst grains, whereas CO and hydrocarbons are combusted also on the inner surfaces of the catalyst. The activity increases with the loading of active phase up to a value of 10 wt%. Very small amounts (<0.05 wt%) of platinum, palladium or rhodium dispersed on the active phase by decomposition of H 2 PtCl g in a reducing atmosphere greatly enchance the low-temperature activity. The carrier (y alumina) sinters and is transformed into other forms of alumina when subjected to high tempe¬ ratures. If the catalyst is subjected to high temperatures (1073°K), the specific surface area therefore is reduced dramatically due to sintering. The activity of the cata- lyst regarding the combustion of hydrocarbon decreases, whereas its activity regarding the combustion of the solid soot phase is maintained. TABLE 1 Combustion rate as a function of the inverted value of the temperature for mixtures of soot and carrier material Inverted value of temperature Combustion rate log £ _ r tot (nmol/s)] 0.001293 7.659 0.001337 7.009 0.001383 6.455 0.001432 5.811 0.001486 5.303 TABLE 2 Selectivity for CO production as a function of the temperature for mixtures of soot and carrier material Selectivity for Temperature CO production °K % 573 3.0 623 8.5 648 13.4 673 14.9 698 15.9 748 15.5 773 12.4 TABLE 3 Ratio between the combustion rates in the presence and the absence of catalyst TABLE 4 Ratio between the combustion rates for deactivated and fresh catalyst TABLE 5 Analysis of used catalysts having different ratios between vanadium and copper TABLE 6 i Combustion rate as a function of the molar fraction of vanadium in the catalyst at different temperatures TABLE 7 Analysis of catalysts with different loadings of active phase TABLE 8 Relative EDAX signal from Al as a function of the loading of active phase in the catalyst of mixed oxides TABLE 9 Combustion rate as a function of the loading of active phase at different temperatures TABLE 10 Ratio between the combustion rates in the presence and the absence of platinum TABLE 11 Selectivity for production of CO as a function of the temperature, using a catalyst with or without platinum TABLE 12 Combustion rate as a function of Pt loading in a catalyst of mixed oxides TABLE 13 Analysis of catalysts calcined at different temperatures TABLE 14 Combustion rate as a function of the calcination temperature TABLE 15 Resistance of catalyst to sulphur poisioning TABLE 16 Chemical composition of diesel soot jytsed in the experiments of the Examples

Claims: CLAIMS 1. A method of purifying exhaust gases from diesel engines by catalytic burning of soot and hydrocarbons, in which method the exhaust gases are conveyed at a tempera¬ ture of at least 300°C, preferably at least 350°C, over catalyst-containing vanadium and copper oxides carried by a carrier, c h a r a c t e r i s e d by using a catalyst in which the molar ratio of V:Cu is from 85:15 to 95:5. 2. Method as claimed in claim 1, c h a r a c t e r ¬ i s e d in that a catalyst is used having a molar ratio of V:Cu of about 90:10. 3. Method as claimed in claim 1 or 2, c h a r a c - t e r i s e d in that the ,exhaust gases are conducted over a catalyst which also contains catalyst material for the combustion of hydrocarbons, especially platinum, pal¬ ladium and/or rhodium. 4. Method as claimed in claim 1, 2 or 3, c h a - r a c t e r i s e d in that the catalytic combustion is carried out at a temperature of 300-500°C. 5. Catalyst for the purification of exhaust gases from diesel engines, comprising a carrier and a catalytic material comprising oxides of vanadium and copper, c h a r a c t e r i s e d in that vanadium and copper are present in a molar ratio of V:Cu of from 85:15 to 95:5. 6. Catalyst as claimed in claim 5, c h a r a c ¬ t e r i s e d in that the molar ratio of V:Cu in the catalyst is about 90:10. 7. Catalyst as claimed in claim 5 or 6, c h a ¬ r a c t e r i s e d in that the catalyst contains 5-25 wt% vanadium- and copper oxides. 8. Catalyst as claimed in claim 5, 6 or 7, c h a ¬ r a c t e r i s e d in that the catalyst also contains catalyst material capable of combusting hydrocarbons, pre¬ ferably platinum, palladium and/or rhodium. 9. Catalyst as claimed in any one of claims 5-8, c h a r a c t e r i s e d in that it contains 0.01-0.25 wt% platinum, palladium and/or rhodium.

Inventors: AHLSTROEM ANDERS FREDRIK, ODENBRAND CLAS ULF INGEMAR, AHLSTROEM, ANDERS, FREDRIK, ODENBRAND, CLAS, ULF, INGEMAR
Applicants: AHLSTROEM ANDERS FREDRIK, ODENBRAND CLAS ULF INGEMAR, AHLSTROEM, ANDERS, FREDRIK, ODENBRAND, CLAS, ULF, INGEMAR
Application year: 1990
Main classification: B01J23
IPC codes: B01D53, B01J23, F02B3