MICROBICIDAL COMPOSITION CONTAINING A CELLULOSE ETHER

Abstract: An aqueous microbicidal composition of a pH below 6 contains a long-chain alkyl ester of general formula (I), wherein R<I>, R<II? and R?III> are hydrogen or lower alkyl groups, R<IV> is a long-chain alkyl group with 10-18 carbon atoms, R<V> is hydrogen or a group of formula (II) R<VI> N<+> H3, wherein R<VI> is an alkylene group with 3-4 carbon atoms, A is a monovalent counter-ion, and n is the number of cationic groups in the ester compound, and a nonionic aqueous cellulose ether. The microbicidal composition has a prolonged microbicidal effect and an improved viscosity at elevated temperature. The microbicidal effect and the improved viscosity are lost when the pH value is raised. Preferably, the cellulose ether is an ethyl hydroxyethyl cellulose having a cloud point of 30-35 DEG C and a viscosity of 30-400 cP in a 1 % water solution, as measured according to Brookfield LV, 12 rpm at 20 DEG C.

Description: MICROBICIDAL COMPOSITION CONTAINING A CELLULOSE ETHER The present invention relates to a microbicidal com¬ position which contains a nonionic water-soluble cellulose ether, preferably an ethyl hydroxyethyl cellulose. In a water-base medium with pH below 6, the microbicidal com¬ position has a prolonged microbicidal effect and an improved viscosity at elevated temperature, whereas the microbicidal effect and the improved viscosity are lost when pH is raised. US Patent Specification 4,790,978 discloses that long-chain alkyl esters of the general formula R 1 R 11 R 111 N + -* n(A " ) (I) wherein R , R and R are hydrogen or lower alkyl groups, R IV is a long-chain alkyl group with 10-18 car- V b° n atoms, R is hydrogen or a group of formula R VI N + H 3 wherein R VI is an alkylene group with 3-4 carbon atoms, A is a monovalent counterion, and n is the number of cat- ionic groups in the ester compound, have, in water-base systems with pH 6-8.5, a bactericidal effect which, owing to the hydrolysis of the ester bond, is temporary. The hydrolysis of the long-chain alkyl ester minimises unde- sirable biological effects, such as skin irritation and sensitisation. These effects have, inter alia, restricted the use of commercial quaternary ammonium compounds as disinfectants. Later, it was also found that the long- chain alkyl esters have an excellent microbicidal effect on a number of viruses, e.g. such viruses as cause venereal diseases. When using microbicides, it is, in many cases, desir¬ able to have available formulations in the form of high- viscous aqueous solutions or gels. It is therefore usual to add viscosity-controlling or gel-forming agents in the form of water-soluble polymers. There are several types of gel-forming water-soluble polymers. For most of these, gelling occurs when the tem¬ perature is reduced. In aqueous solution, some polymers, such as nonionic cellulose ethers, have a so-called cloud point, which means that the polymer is precipitated when the temperature is elevated beyond a critical value. Nor¬ mally, the viscosity of nonionic cellulose ethers is reduced when the temperature is raised above room tempera¬ ture, and this reduction continues until the cloud point is reached. At this temperature, the solution starts to become turbid and, if the polymer content is sufficiently high, an increase in viscosity can be observed. This pro¬ cess is reversible. PCT/SE89/00266 discloses that the decrease in visco- sity following upon an increase in the temperature of an aqueous solution of a nonionic cellulose ether can be reduced considerably, and in many cases even turned into a considerable increase in viscosity, by using a system which has a water content of at least 85% and, in its liquid phase, contains as viscosity-controlling agents, a) a nonionic cellulose ether in such an amount that a water solution thereof has a viscosity of 10-10,000 cP, preferably 30-5,000 cP, as measured according to Brook- field LV, 12 rpm at 20°C, and b) a water-soluble, ionic and surface-active compound in an amount of 1-30 mmol, preferably 2-20 mmol, per litre of water. The resulting system has a surprisingly advantageous viscosity development at elevated temperature. By adapting the cloud point of the cellulose ether and the amount of ionic surface-active compound, also gels and gel-like structures can be obtained.' One object of the present invention is to provide, for the long-chain alkyl ester compounds of formula I, a microbicidal composition containing a polymer and present¬ ing a lower decrease in viscosity at elevated temperature than does the polymer itself and, in many cases, even pre¬ senting a maintained or increased viscosity, before any gel or gel-like structures form. Another object of the invention is that the micro¬ bicidal composition should be stable and have a high viscosity during the entire treatment. Also, the micro¬ bicidal effect of the formulation should be high. A further object of the invention is that the compo¬ sition should be readily removable once the microbicidal treatment has been carried out. Thus, the effect of this treatment is easier to control. Yet another object of the invention is that the removed composition should, after a short period of time, lose its microbicidal effect and only contain nontoxic ingredients. Compositions possessing these qualities are much- needed in several areas, e.g. the food industry and the biotechnics, for disinfecting production equipment, or in therapeutical and cosmetic treatments where it may be desirable to achieve an increase in viscosity and, optionally, an ensuing gel formation upon heating to the temperature of the production equipment or to the body temperature. Unexpectedly, it has been found that the above requirements are met by a water-base microbicidal compo- sition containing a) 1-30 mmol, preferably 2-20 mmol per litre of water, of a long-chain alkyl ester of the general formula I, in combination with b) a nonionic cellulose ether in such an amount that a water solution thereof has a viscosity of 10-10,000 cP, preferably 30-5,000 cP, as measured according to Brook- field LV, 12 rpm at 20°C, the pH of the composition being below 6, preferably 3.0-5.5. The composition according to the invention has an advantageous viscosity development at elevated tempera- ture, and its microbicidal effect is prolonged and remains high. When the microbicidal treatment is performed, it may be interrupted, e.g. by diluting the composition, which after the increase in temperature is high-viscous, with cold water, and/or by supplying a basic agent, such as an aqueous alkaline buffer solution. When the pH of the for¬ mulation is 6 or higher, preferably above 7, the high vis¬ cosity of the composition decreases rapidly, whereupon the composition can be easily removed. Surprisingly enough, the decrease in viscosity has been found to be much more rap d than could have been expected in view of the hydro¬ lysis of the long-chain alkyl ester in aqueous solution. This quality is of great value since it not only makes it possible to carefully control the duration of the treat¬ ment, but also facilitates the removal of the composition. If the composition is applied to a surface emitting hydroxide ions or taking up protons, its pH will rise gra¬ dually. In such cases, it is not necessary to take any special measures for increasing the pH, but the duration of the treatment can be adjusted by the choice of a suit- able pH for the composition applied. Preferably, the alkyl groups R , R and R of the alkyl ester have 1-4 carbon atoms and are, most pre- ferably, methyl groups. The group R IV is preferably a straight-chain alkyl group. Usually, the counterion A is a halide ion, such as chloride or HS0,~. Preferred embo¬ diments of the alkyl esters include esters of the general formulae 2A (IV) wherein R IV and A are the same as above. Suitably, the alkyl ester is added in such an amount that, when gra¬ dually added to an aqueous solution containing a desired 20 content of the cellulose ether at issue, it will increase the viscosity by at least 25%. The cellulose ethers should be water-soluble at the temperature at which the aqueous solution is prepared. Suitably, their degree of polymerisation is such that a 1% 2 ~- water solution thereof has a viscosity of 10-10,000 cP, preferably 30-5,000 cP, as measured according to Brook- field LV, 12 rpm at 20°C. The cellulose ethers may com¬ prise hydrophobiσ hydrocarbon groups, such as methyl, ethyl, propyl, butyl, benzyl and higher hydrocarbon groups --0 with 8-24 carbon atoms; or polar hydroxyl groups,' such as hydroxyethy1, hydroxypropyl and hydroxybutyl; or mixtures of hydrocarbon groups and polar groups. Suitably, the cloud point of the cellulose ethers is below 70° but above room temperature and is adapted to suit the field of ~-~- application of the composition. Preferably, a cellulose ether is chosen whose cloud point is -5°C - +5°C of the temperature at which the composition is used. Suitable cellulose ethers include methyl cellulose, ethyl cellu¬ lose, hydroxyethyl cellulose, hydroxypropyl cellulose, methyl hydroxyethyl cellulose, ethyl hydroxypropyl cel¬ lulose, ethyl hydroxyethyl cellulose, and benzyl ethyl hydroxyethyl cellulose. Alkyl hydroxyalkyl cellulose and especially ethyl hydroxyethyl cellulose are the preferred cellulose ethers. For topical use on human beings, compositions con¬ taining ethyl hydroxyethyl celluloses with cloud points of 30-35°C, especially 32-35°C, and viscosities of 30-400 cP in a 1% water solution, as measured according to Brook- field LV, 12 rpm at 20°C have shown excellent properties. They are easily formulated at room temperature or tempera¬ tures slightly above room temperature. After applying and distributing such a composition on the skin, a gelling effect will rapidly take place, preventing undesired run¬ ning and leveling. These ethyl hydroxyethyl celluloses normally have a DS ethyl of 1.2-2.5 and an S hydroχyethyl of 0.5-1.5. The invention also relates to the preferred ethyl hydroxyethyl cellulose ethers having a cloud point of 30-35°C, especially 32-35°C. These cellulose ethers nor- mally ■ * have a DSet.,hyl, of 1.2-2.5 and an MSh,yd,ro_xyet..hyl. of 0.5-1.5, but they may also contain minor amounts of other subsi-tuents-, such as methyl and hydroxypropyl. The vis¬ cosity of the ethers is preferably from 30 to 400 cP in a 1% water solution, as measured according to Brookfield LV, 12 rpm at 20°C. The ethyl hydroxyethyl cellulose ethers may be pre¬ pared by conventional methods, for example by first mer¬ cerising cotton linters or dissolving pulp with an aqueous alkaline solution. After dewatering, if so desired, the activated cellulose is reacted with ethylene oxide at a temperature of 60-90°C and with an ethyl halide at a tern- perature of 95-120°C in the presence of an organic reaction medium. If desired, the mercerisation, ethoxylation, and/or alkylation may be repeated in one or more sequences. Final¬ ly, the ethyl hydroxyethyl cellulose obtained is neutra- lised and/or washed. Generally, the composition according to the inven¬ tion is used at a temperature exceeding the temperature at which it was prepared. In addition to pH regulators, the formulation may contain purifying agents, enzymes, bleach- ing agents, therapeutical and cosmetic agents, colouring agents, and salts. A high salt content should however be avoided unless a dehydrating effect is desired. The invention will now be further illustrated by means of the following Examples. Example 1 '- • Aqueous compositions were formulated from ethyl hydroxyethyl cellulose and a long-chain alkyl ester of formula (CH 3 ) 3 N + CH^ COO C 14 H 2g Cl " The cellulose ether had MSh.yd,roxyet..hyl, = 1.0; DSet.h.yl, 1.7; a cloud point of about 35°C; and a viscosity of 55 cP in a 1% water solution, as measured according to Brook- field LV, 12 rpm at 20°C. The alkyl ester and cellulose ether contents are apparent from the Table below. The pH of the formulations was adjusted by means of HCl to 4. Then, the viscosity of the formulations was measured as a function of the tempe¬ rature. The measurements were carried out by means of a Bohlin Rheometer at a shear rate of 0.2326 s ~ . The heat¬ ing rate was 2°C per minute. The results are shown below. 1/ Gel-like; the viscosity increases as the temperature increases. 2/ Gel; the viscosity increases as the temperature increases. As is apparent from the results above, the viscosity of the formulation increases as the temperature increases until a gel-like or gel structure is obtained. Example 2 Like in Example 1, the viscosity was measured as a function of the temperature of an aqueous composition containing 1.25% by weight of the cellulose ether in Example 1 and 0.17% by weight of the alkyl ester in Exam¬ ple 1. pH was adjusted by means of HCl and NaOH, and the measurements began 5 minutes after the composition had been prepared. The value at 35°C was measured 10 minutes after this temperature had been reached. The following results were obtained. As is apparent from these results, the viscosity decreases when pH is 6 or above. This decrease is more rapid than the hydrolysis of the alkyl ester taking place in an aqueous solution at the pH at issue. Example 3 To 1 litre of water were added 7.5 g of the cellu¬ lose ether in Example 1 and 1.5 g of the ester compound in Example 1. To 0.4 ml of the resulting formulation was added 15 μl of a solution containing Salmonella typhi- murium, whereupon the bacterial activity was measured after varying contact times. The following results were obtained. Time Bacterial activity min. log efu 0 5.7 1 4.5 2 4.2 3 0.3 5 0.3 10 0.3 As is apparent from these results, the bactericidal effect of the composition is excellent. Example 4 An aqueous composition was formulated from the cellu¬ lose ether in Example 1 and a long-chain alkyl ester of formula H 3 N CH(C 4 H 8 N H 3 )C0 2 C 16 H 33 2C1 The alkyl ester content was 0.3% by weight, and the cellu¬ lose ether content was 0.75% by weight. The pH of the formulation was about 3.3. The viscosity of the formula¬ tion was measured at 20°C and at 35°C and was found to be <1 and 4 Pa's, respectively. The measurements and the heating were carried out as in Example 1. Example 5 Aqueous compositions were formulated from ethyl hydroxyethyl cellulose and a long-chain alkyl ester, as disclosed in Example 1. 5 The cellulose ether had an MSh.yd,roxyet..hyl, = 1.0,' a DS .. , = 1.8, a cloud point of about 33°C and a viscosity of 67 cP in a 1% water solution, as measured according to Brookfield LV, 12 rpm at 20°C. The alkyl ester and cellulose ether contents are 10 apparent from the Table below. The pH of the formulations was adjusted by means of HCl to 4. Then, the viscosity of the formulations was measured as a function of the tem¬ perature. The measurements were carried out by means of a Bohlin Rheometer at a shear rate of 0.2326 s~ . The heat- 15 ing rate was 2°C per minute. The results are shown below. Test Per cent by weight Viscosity Pa s Cellulose Alkyl 20°C 37°C 40°C ether ester 2 1.0 0.23 1 95 2 130 2/ 1/ Gel-like; the viscosity increases as the temperature increases. y e 2/ Gel; the viscosity increases as the temperature increases. As is apparent from the results above, the viscosity of the formulation increases as the temperature increases until a gel-like or gel structure is obtained. 30 35

Claims: CLAIMS 1. An aqueous microbicidal composition having a microbicidal effect combined with improved viscosity, c h a r a c t e r i s e d in that it contains a) 1-30 mmol per litre of water of a long-chain alkyl ester of the general formula wherein R , R and R are hydrogen or lower alkyl groups, R IV is a long-chair^ alkyl group with 10-18 car- V bon atoms, R is hydrogen or a group of formula R VI N + H 3 wherein R VI is an alkylene group having 3-4 carbon. atoms, A is a monovalent counter-ion, and n is the number of cat- ionic groups in the ester compound, and b) a nonionic water-soluble cellulose ether in such an amount that a water solution thereof has a viscosity of 10-10,000 cP as measured according to Brookfield LV, 12 rpm at 20°C, and that it has a pH below 6. 2. Composition as claimed in claim 1, c h a r a c ¬ t e r i s e d in that a 1% water solution of the cellu¬ lose ether has a viscosity of 10-10,000 cP. 3. Composition as claimed in any one of claims 1 and 2, c h a r a c t e r i s e d in that the cellulose ether has a cloud point below 70°C. 4. Composition as claimed in any one of claims 1-3, c h a r a c t e r i s e d in that the cellulose ether is an alkyl hydroxyalkyl cellulose. 5. Composition as claimed in claim 4, c h a r a c ¬ t e r i .s e d in that the cellulose ether is an ethyl hydroxyethyl cellulose having a cloud point of 30-35°C. 6. Composition as claimed in claim 5, c h a r a c - 5 t e r i s e d in that the cellulose ether has a DSet..hy.l of 1.2-2.5 and an MS hydroχyethyl of 0.5-1.5. 7. Composition as claimed in claim 5 or 6, c h a ¬ r a c t e r i s e d in that the cellulose ether has a viscosity of 30-400 cP in a 1% water solution, as measured 10 according to Brookfield LV, 12 rpm at 20°C. 8. Composition as claimed in any one of claims 1-7, c h a r a c t e r i s e d by having a pH of 3.0-5.5. 9. Composition as claimed in any one of claims 1-8, c h a r a c t e r i s e d in that the long-chain alkyl 15 ester is a compound of one of the general formulae wherein R IV and A are the same as above. 10. Composition as claimed in claim 9, c h a r a c - 35 t e r i s e d in that the long-chain alkyl ester is a compound of the general formula II. 11. An ethyl hydroxyethyl cellulose, c a r a c ¬ t e r i s e d in that it has a cloud point of 30-35°C. 12. Ethyl hydroxethyl cellulose as claimed in claim 11, c h a r a c t e r i s e d in that it has a DSe,thyl of 1.2-2.5 and an MS hydroχyethyl of 0.5-1.5. 13. Ethyl hydroxyethyl cellulose as claimed in claim 11 or 12, c h a r a c t e r i s e d in that it has a viscosity of 30-400 cP in a 1% water solution, as measured according to Brookfield LV, 12 rpm at 20°C.

Inventors: ANDERSSON LARS, VON CORSWANT CHRISTIAN, ANDERSSON, LARS, VON CORSWANT, CHRISTIAN
Applicants: BEROL NOBEL AB
Application year: 1990
Main classification: A01N25
IPC codes: A01N25, A01N37, A23L3, A61K8, A61Q17, A61Q19, C08K5