SURFACE TREATMENT FOR SILICONE TUBING TO IMPROVE SLIP PROPERTIES

Abstract: Surface treatment of silicone rubber covering on IPG leads by exposure to radio frequency glow discharge.

Description: _ χ _ SURFACE TREATMENT FOR SILICONE TUBING TO IMPROVE SLIP PROPERTIES Background of the Invention In general, this invention relates to improved electrical leads. More particularly it relates to improved leads for implantable pulse generators (IPG's) such as heart pacemakers. Heart pacemakers may have one or more leads incorporating this invention. Such implantable medical devices require elongate electrical leads which attach to sites in the body for electrical contact therewith. The surfaces of the leads often contact each other and rub against each other. In the case of transvenous heart pacemakers which are implanted in the chest, a pair of leads may extend through a blood vessel into the heart for interior attachment thereto. The two leads extend * through a common vessel for some portion of their entry path and rub against each other in various surface areas. It has become common practice to include silicone rubber as a surface covering for such leads because it is biocompatible and biostable. It is particularly common to utilize silicone rubber tubing for this purpose. A continuing problem with the use of silicone rubber has been the binding which occurs when these outer coverings rub against each other. Such binding is often referred to as / surface blocking" or simply "blocking". Implantation side-by-side thus has been found to give rise to sticking and even dislodgment of the leads. Various surface coatings have been tried in an effort to reduce "blocking" and improve the "slip" of silicone rubber. However, such coatings have been found to have too short a lifetime or to lack biocompatibility and/or biostability. It is a specific object of this invention to provide silicone rubber with improved surface properties in this regard and particularly to provide silicone rubber tubing and coverings for leads and in combination with leads which exhibit permanent and improved "blocking" and "slip." Summary of the Invention The objects of the invention are attained by providing leads with silicone rubber coverings, especially tubing, which have been surface treated by radio frequency glow discharge. Such treatment has been found to permanently improve the surface characteristics of silicone rubber coverings for leads with respect to the aforementioned problems. Brief Description of the Drawings Fig. 1 represents in schematic form the implantation of a heart pacemaker IPG and a pair of electrical leads in a human heart; Figs 2 and 3 show the structure of a typical IPG lead, distal and proximal end portions respectively; Fig. 4 shows schematically an apparatus for carrying out the treatment of the invention, and; Fig. 5 shows schematically another apparatus for carrying out the treatment recording to the invention. Description of the Preferred Embodiments While this invention may be embodied in many different forms, there are shown in the drawings and described in detail herein specific preferred embodiments of the invention. The present disclosure is an exemplification of the principles of the invention and is not intended to limit the invention to the particular embodiments illustrated. Referring to Fig. 1, an implanted heart pacemaker IPG 10 is shown having two electrical leads, atrial lead 12 and ventricular lead 14, extending through a common vessel, such as the R. Brachiocephalis vein 16, of a human heart generally indicated at 18. The paired leads extend into the right atrium 20 of the heart where lead 12 is attached to a site 22. Lead 14 extends through atrium 20 and into right ventricle 24 where likewise is attached to a site 26. As can be readily seen, leads 12 and 14 during implantation through vessel 16 undergo a certain amount of mutual rubbing together over portions of their length. Likewise, after implantation, movement of the heart and general movement of the patient causes a certain amount of mutual rubbing contact between the leads. The resultant sticking together and even dislodgment as aforementioned are obviated by the improvement of this invention. As already mentioned, the improvement herein focuses on the outer surface of the leads, which is typically comprised of a silicone rubber covering. A typical lead is shown in Fig. 2 and in Fig. 3. Such a lead will include among other things at its distal portion as shown in Fig. 2 an electrode assembly 30, an elongate conductive coil 32 and an outer elongate covering 34 over its length comprised of silicone rubber tubing or the like. Likewise, the proximal portion as shown in Fig. 3 will also include the same continuing elements of conductive coil 32 and silicone rubber tubing 34 . The surface treatment provided for the s il icone rubber tubing 34 is preferably appl ied to the tubing before it is placed over the lead structure . It may of course be appl ied at other stages in the lead manufacturing process, particularly if silicone rubber is used in a form other than tubing. The theory and practice of radio frequency (RF) gas d i s cha rg e i s exp l a i n e d i n g re at d e t a i l i n 1 ) "Gas-Discharge Techniques For Biomaterial Modification-''' by Gombatz and Hoffman, CRC Critical Reviews in Biocompatibility, Vol. 4, Issue 1 (1987), pp 1-42; 2) -'Surface Modification and Evaluation of Some Commonly Used Catheter Materials. I. Surface Properties-' by Trials and Andrade, Journal of Biomedical Materials Research, Vol 17, 129-147 (1983), and 3) "Surface Modification and Evaluation of Some Commonly Used Catheter Materials, II. Friction Characterized" also by Triaolo and Andrade, Journal of Biomedical Materials Research. Vol. 17, 149-165 (1983) , and need not be described again herein.. All of the foregoing is incorporated herein by reference. Suffice it to say here that the gas discharge process or radio frequency flow discharge (RFGD) is contemplated herein gives rise to a plasma of various ionized and other charged species which interact with surfaces exposed thereto, such as silicone rubber surfaces, to alter same by reaction therewith. Referring now to Fig. 4, apparatus is shown which may be used to provide ,radio frequency glow discharge treatment to the surface of tubing or silicone rubber in other forms and configurations. It is adapted for a "batch treatment" procedure although it can be readily modified for a "flow through" treatment procedure as shown schematically in Fig. 5. A complete RF system as shown for producing gas discharge will include a reactor vessel 40, a generator 42, an impedance matching network 44, means 46 for applying an RF field to reactor 50, means 48 such as a meter or meters for measuring the RF power supplied to the discharge, a vacuum pump 50 and a pressure gauge 52. A flow controller and flow meter 54 may be included between one or more gas suppliers 56-58. RF generator 42 is preferably one of those commercially available and preferably operates at a frequency of 13.56 MHz. Coupling of the RF power from the output of the matching network 44 may be accomplished either inductively or capacitively to generate the discharge in reactor 40 whereby a length of the tubing 60 contained therein may be exposed to the glow discharge for surface treatment. In accordance with this invention. Any gas already known for glow discharge may be used as well as mixtures of such gases. These gases are generally referred to as plasma gases and can be grouped as nonpolymer-forming and polymer-forming types. Typical gases used in nonpolymer forming discharges are hydrogen, helium, argon, nitrogen, ammonia, carbon dioxide and, in special cases, C 2 F 6 which can exchange hydrogen and fluorine. Examples of polymer-forming gases are C 2 F A C 3 F 6 , C 2 H 4 C 2 H 2 CH A . Nitrogen, argon, helium, carbon dioxide, ammonia, oxygen, C 2 F 4 , C 3 F 6 , C 2 F 6 and combinations thereof are preferred. Particularly preferred gases for use alone or in various mixtures are argon, oxygen, helium, nitrogen, ammonia and carbon dioxide, nitrogen being most particularly preferred. Both nonpolymer-forming and polymer-forming plasma treatments of the surface of silicone rubber reduces surface blocking. The result is a reduction or elimination of stick/slip properties and a lower coefficient of. friction. Plasma treatment with nonpolymer-forming gas is generally preferred. As can be seen in Fig. 4, the gas or gas mixture is introduced into vacuum chamber reactor 40 which contains tubing 60 to be treated. The plasma electrodes 46, which may be inside or outside the reactor, are activated to produce the plasma glow discharge at a radio frequency of 13.56 MHz and at a wattage of from about 2 to 1000 watts, 2-250 watts being preferred. Typically, 50 watts is adequate and most preferred. Various treatment times and gas pressures may be used. Gas pressures may vary from about 0.01 to 1.0 Torr generally. With the preferred nitrogen gas, at a pressure of less than about 0.5 torr, for example .2-.3 torr, and 50 watts, a treatment time of about 16 minutes is acceptable for silicone rubber tubing of about .068 - .101 inch OD. Referring now to Fig. 5 and as already mentioned, apparatus for treating tubing on a "flow through" basis is shown. In this arrangement the tubing or other silicone rubber material is moved through the discharge region between anode 46a and cathode 46b as it is removed from a "take-off" reel 41 and rolled up on a "take-up" reel 43 which is operated electrically by a motor 45 and electrical lead 47. An idler pully 45 may be used for turnaround of the tubing. For example, a chamber as shown may be used to treat 100 foot rolls of tubing by winding it through at a speed adjusted to give the tubing a 16 minute exposure to the plasma. As the tubing is wound in the take-up reel 43, the speed at which the tubing travels through the plasma may increase. Monitoring and periodic changing of the tubing speed may be necessary. The apparatus of Fig. 5 will additionally include electrical attachments 62, a vacuum conduit 64 and another conduit 66 for introducing gases into the closed environment defined by a bell jar 68 or the like. Glow discharge treatment as described above has been found to improve silicone rubber surfaces without introducing residue " or coating and with respect to "slip" and "blocking". This completes the description of the preferred and alternate embodiments of the invention. Those skilled in the art may recognize other equivalents to the specific embodiment described herein which equivalents are intended to be encompassed by the claims attached hereto.

Claims: WHAT IS CLAIMED IS: 1. An electrical lead for implantation having an outer covering of silicone rubber, the exterior surface of which has been treated by exposure to radio frequency glow discharge. 2. The improvement of Claim 1 wherein the glow discharge is in a nonpolymer forming gas. 3. The improvement of Claim 2 wherein the gas pressure is between about 0.1 and 1.0 torr. 4. The improvement of Claim 1 wherein the gas is a mixture of nonpolymer forming gases. 5. The improvement of Claim 1 wherein the glow discharge is in nitrogen. 6. The improvement of Claim 5 when the glow discharge is at a radio frequency of 13.56 MHz. 7. The improvement of Claim 6 wherein the discharge is from about 2 to 250 watts. 8. The improvement of Claim 5 when the nitrogen is at a pressure of about 0.2 to 0.3 torr, the plasma voltage is about 50 watts and the treatment time is about 16 minutes. 9. The improvement of Claim l wherein the glow discharge is in a mixture of gases. 10. The improvement of Claim 1 wherein the discharge gas is helium. 11. The improvement of Claim 1 wherein the discharge gas is argon. 12. The improvement of Claim 1 wherein the discharge gas is oxygen. 13. The improvement of Claim 1 wherein the discharge gas is ammonia. 14. The improvement of Claim 1 wherein the gas is carbon dioxide. 15. The lead of Claim 1 in which the silicone rubber is in the form of tubing. 16. A medical device including at least two electrical leads adapted for implantation and which come into mutual contact with at least a portion of each other's surface over at least a portion of their length upon implantation, the leads being covered with silicone rubber the surface of which has been treated with radio frequency glow discharge. 17. The improvement of Claim 16 wherein the glow discharge is in a nonpolymer forming gas. 18. The improvement of Claim 17 wherein the gas pressure is between about 0.1 and 1.0 torr. 19. The improvement of Claim 16 wherein the gas is a mixture of nonpolymer forming gases. 20. The improvement of Claim 16 wherein the glow discharge is in nitrogen. 21. The improvement of Claim 20 when the glow discharge is at a radio frequency of 13.56 MHz. 22. The improvement of Claim 21 wherein the discharge is at from about 2 to 250 watts. 23. The improvement of Claim 21 when the nitrogen is at a pressure of about .2 to .3 torr, the discharge is at about 50 watts and the treatment time is about 16 minutes . 24 . The improvement of Claim 16 wherein the glow discharge is in a mixture of gases . 25. The lead of Claim 16 in which the sil icone rubber is in the form of tubing. 26. The improvement o f Cl aim 16 where in the discharge gas is helium. 27. The improvement of Cl aim 16 wherein the discharge gas is argon. 28. The improvement o f Cl aim 16 where in the discharge gas is oxygen. 29 . The improvement o f Cl a im 16 where in the discharge gas is ammonia. 30. The improvement of Claim 16 wherein the gas is carbon dioxide. 31. In a medical device including a plurality of elongated electrical leads adapted for side-by-side implantation through a blood vessel, the leads including an outer covering substantially over their length comprised of silicone rubber, the improvement comprising a treated exterior surface on the silicone provided by exposing it to radio frequency glow discharge. 32. The improvement of Claim 31 wherein the glow discharge is in a nonpolymer forming gas. 33. The improvement of Claim 32 wherein the gas pressure is between about 0.1 and 1.0 torr. 34. The improvement of Claim 31 wherein .the gas is a mixture of nonpolymer forming gases. 35. The improvement of Claim 31 wherein the glow discharge is in nitrogen. 36. The improvement of Claim 35 when the glow discharge is at a radio frequency of 13.56 MHz. 37. The improvement of Claim 36 wherein the discharge is at a wattage of from about 2 to 250 watts. 38. The improvement of Claim 35 when the nitrogen is at . a pressure of about 0.2 to 0.3 torr, the plasma voltage is about 50 watts and the treatment time is about 16 minutes. 39. The improvement of claim 34 wherein the glow discharge is in a mixture of gases. 40. The lead of Claim 34 in which the silicone rubber is in the form of tubing. 41. The improvement of Claim 34 wherein the discharge gas is helium. 42. The improvement of Claim 34 wherein the discharge gas is argon. 43. The improvement of Claim 34 wherein the discharge gas is oxygen. 44. The improvement of Claim 34 wherein the discharge gas is ammonia. 45. The improvement of Claim 34 wherein the gas is carbon dioxide. 46. Silicone rubber tubing for use as outer covering on implantable leads, the surface of the tubing having been treated by exposure to radio frequency glow discharge. 47. The improvement of Claim 46 wherein the glow discharge is in a nonpolymer forming gas. 48. The improvement of Claim 47 wherein the gas pressure is between about 0.1 and 1.0 torr. 49. The improvement of Claim 46 wherein the gas is a mixture of nonpolymer forming gases. 50. The tubing of Claim 46 wherein the glow discharge is in nitrogen. 51. The tubing of Claim 50 wherein the discharge is at a radio frequency of 13.56 MHz. 52. The tubing of Claim 50 wherein the discharge is from about 2 to 250 watts. 53. The tubing of Claim 50 wherein the nitrogen is at a pressure of about 0.2 to 0.3 torr, the discharge is at about 50 watts and the treatment time is about 16 minutes. 54. The tubing of Claim 46 wherein the discharge gas is helium. 55. The tubing of Claim 46 wherein the discharge gas is argon. 56. The tubing of Claim 46 wherein the discharge gas is oxygen. 57. The tubing of Claim 46 wherein the discharge gas is ammonia. 58. The tubing of Claim 46 wherein the discharge gas is carbon dioxide.

Inventors: CAHALAN PATRICK T, COURY ARTHUR J, DI DOMENICO EDWARD D JR, KEENEY KENNETH W, SWOYER JOHN M, CAHALAN, PATRICK, T., COURY, ARTHUR, J., DI DOMENICO, EDWARD, D., JR., KEENEY, KENNETH, W., SWOYER, JOHN, M.
Applicants: MEDTRONIC INC, MEDTRONIC, INC.
Application year: 1990
Main classification: B29C59
IPC codes: B29C59