Water-disposable tampon applicators and biodegradable composition for use therein

Abstract: This invention provides biodegradable tampon applicators adapted for disposal in water-base toilet systems. This invention also provides plasticized starch compositions for use in the fabrication of tampon applicators and methods for fabrication thereof.

Description: This invention relates to biodegradable tampon applicators adapted for disposal in water-base toilet systems. This invention also relates to plasticized starch compositions and the fabrication of tampon applicators from such compositions. Tampon insertion devices ("applicators") of a telescoping tube type are often disposed of by dropping them into a toilet. Thus, it is desirable that applicators be fabricated from a composition which rapidly softens and disperses in water, yet retains its form during use and is shelf-stable under ambient conditions. Such a composition avoids the danger of stoppages of toilet and sewer systems. Biodegradability is also a desirable characteristic. Compositions suggested for use in such applicators include water soluble polymers, synthetic (e.g., polyoxyethylene polymers) and natural (e.g., cellulose derivatives), and fillers such as talc, clay, hydrated silicates and starch. See, e.g., U.S. Pat. Nos. A-3,882,869, issued May 13, 1975 to Hanke; US-A-3,954,104, issued May 4, 1976 to Kraskin, et al.; and US-A-4,099,976, issued July 11, 1978 to Kraskin, et al. These compositions disadvantageously require the presence of non-water-dispersable fillers to reduce cost and/or cellulose derivatives to impart thermoplastic characteristics to the composition. Starch and other polysaccharides have been suggested for use in biodegradable packaging and container materials. Starches typically are employed as an adjunct to other, conventional packaging materials to improve biodegradability. However, in a few cases starches have been employed as the primary component of containers (i.e., U.S. Pat. No. A-4,673,438, issued June 16, 1987 to Wittwer, et al.), and packaging materials (i.e., U.S. Pat. No. A-4,863,655, issued September 5, 1989 to Lacourse, et al.). The biodegradable, starch-containing packaging and container materials known in the art are typically prepared to be water-resistant, rather than water-dispersable. Thus, there remains a need for other, biodegradable compositions for use in fabricating toilet-disposable tampon applicators. A water-dispersable, toilet-disposable, biodegradable applicator as claimed in Claim 1 is provided herein. The applicator typically has a water content of less than 15%, by weight, and a water activity of less than 0.80, and is resistant to microbial growth up to 30 o C and up to 80% relative humidity. The applicator may further comprise at least one component selected from the group consisting of antimicrobial agents, lubricants, fillers (e.g., dextrin), colorants, fragrances, and the like. Also provided are methods for fabricating biodegradable and toilet-disposable tampon applicators by molding, casting or extrusion of compositions comprising 30 to 65%, by weight, starch, 10 to 40%, by weight, plasticizer and 20 to 60%, by weight, water. Figure 1 is a perspective view of a tampon applicator and a tampon with parts broken away. The embodiment shown in Figure 1 comprises outer tube 1 made of the composition of the invention, having tampon 2 movably received within one end thereof and plunger 3 movably received within the other end thereof. The tampon containing end of the applicator is inserted into the body cavity and the tampon is expelled therefrom by the pressure of the plunger. This plunger may be made of the composition herein. Starches which may be used herein may be derived from any source, including corn, potato, sweet potato, wheat, rice, sago, tapioca, waxy maize, sorghum, high amylose corn, or the like. Starch flours also may be used. Also useful herein are the conversion products derived from any of these starches including, for example, dextrins prepared by the hydrolytic action of acid and/or heat; oxidized starches prepared by treatment with oxidants such as sodium hypochlorite; fluidity or thin-boiling starches prepared by enzyme conversion or mild acid hydrolysis; and derivatized (e.g., cationic, anionic, amphoteric, and non-ionic) starches and crosslinked starches. Prior to formulating the compositions useful herein, the starch may be in a granular form or a gelatinized form (i.e., cooked, non-granular starch). Methods for preparing modified starches are well known to those skilled in the art and are discussed in the literature. See, for example, R. L. Whistler, Methods in Carbohydrate Chemistry , Vol. IV, 1964, pp. 279-331; R. L. Whistler, et al., Starch-Chemistry and Technology , Vol. II, 1967, pp. 293-430; R. L. Davidson, Handbook of Water-Soluble Gums and Resins , 1980, Chapter 22, directed to starch; and O. Wurzburg, Modified Starches: Properties and Uses , CRC Press, 1986. The starch may be cooked prior to derivatization, or subsequent to derivatization. The starch must be cooked and hydrated (to gelatinization) and be in a dispersed state for use in the compositions herein. Any conventional cooking procedure may be used, such as jet-cooking, or cooking a slurry containing the water-soluble or water-swellable starch derivatives in a boiling water bath for 20 minutes and blowing in steam to heat the slurry to about 93 o C (200 o F). Converted corn starch, derivatized by reaction with a C₂-C₆ alkylene oxide, is preferred herein. Propylene oxide is preferred. Propylene oxide treatment increases the water-dispersibility of the starch, permits use of the starch derivative as food grade material and reduces the amount of plasticizer needed to fabricate articles with acceptable tensile strenth. Also preferred is a light crosslinking treatment of the gelatinized starch in a dispersed state for building starch film strength and permitting fabrication of a substantially rigid article. Too much crosslinking tends to limit water dispersibility. Preferred results are achieved by lightly crosslinking dispersed starch with, e. g., glyoxal, at a treatment level up to 1%, by weight of starch, preferably up to a maximum treatment level of 0.5%. Very high strength starch films are to be avoided so as to retain water-dispersability. Likewise, as the percent amylose increases, starch film strength increases and water-dispersibility decreases. Therefore, unmodified high amylose starches (i.e., starches containing more than 40% amylose) are typically avoided in compositions used for fabricating tampon applicators. Derivatized and/or converted high amylose starches are more water-dispersible than their unmodified counterparts and are suitable for use in tampon applicators. Further, even unmodified high amylose starch may be used if blended with an adjunct, such as dextrin or a highly converted fluidity starch, which absorbs water or otherwise improves water-dispersibility of the high amylose starches. Dextrins and fluidity starches also may be selected to control the viscosity of the starch composition as needed for manufacture of the applicators. Plasticizers employed herein typically include sorbitol, polyethylene glycol, glycerol, polyethyleneimine, ethylene glycol, tetra-alkyl ammonium salts, tri-alkyl citrates or mono-, di- or triacetates of glycerol, or a combination thereof. Other plasticizers known in the art also may be employed. For tampon applicators useful plasticizers are limited to non-toxic materials. Prior to fabrication of the tampon applicators, compositions useful therein comprise 30 to 65% starch, 10 to 40% plasticizer and 20 to 60% water, depending upon the method of fabrication to be employed. Extrusion processing requires less water (20-40%) than casting (30-60%), more starch (35-70% versus 30-50%) and less plasticizer (10-40% versus 20-40%). Optionally, these compositions may further comprise lubricants, fillers, colorants or opacifying agents, antimicrobial agents and fragrances for use in tampon applicators. Lubricants may be used in the compositions to facilitate the manufacture of articles therefrom. The preferred lubricants are lauryl thiodipropionate, glycerol monostearate, and various polyalkylene glycols, such as polyethylene glycol, polypropylene glycol, and combinations thereof, sold by Union Carbide Corporation under the tradename CARBOWAX®. Although these starch-containing compositions provide milky, opaque articles, additional opacity, color or whiteness may be achieved by employing titanium dioxide or other suitable opacifying material or colorant. Because biodegradable starch-containing compositions are, by definition, susceptible to microbial attack under certain conditions, the control of microbial attack is an important element in formulating a shelf-stable composition. In a preferred embodiment, the water content and the water activity of the tampon applicators prepared from the starch compositions are controlled so as to eliminate microbial attack. Water activity is the ratio of the vapor pressure of the tampon applicators to the vapor pressure of water at the same temperature. The water activity at which microbial growth is eliminated varies depending primarily upon water content of the applicator, temperature, ambient relative humidity, surface area and shape of the applicator, presence of salts and presence of other materials which affect microbial growth. For tampon applicators prepared from starch compositions disclosed herein, a water activity of less than 0.80, preferably less than 0.70, is preferred for shelf stability. A water content of less than 15%, preferably less than 10%, is also preferred. As the water content is decreased, higher water activities may be acceptable. Likewise, as water activity is decreased, water content may be increased. Because water activity changes as ambient temperature and relative humidity changes, storage of tampon applicators at less than 30 o C and less than 80% relative humidity is preferred. In the alternative, an outer package having a moisture barrier may be employed. In another preferred embodiment, anti-microbial agents may be added to the starch composition. Such agents are known in the art and are exemplified by sorbic acid and its alkali salts which may be used at from about 0.05% to 3%, by weight of the starch composition, preferably at 0.1% to 0.3%. As will be readily determined by the practitioner, other anti-microbial agents and other preferred ranges of water activity, water content and storage conditions may be employed. The tampon applicators herein may be fabricated by any method known in the art of forming or shaping plastic materials. For example, an extrusion process, either alone or in combination with other forming or molding operations, may be used. By varying the size and configuration of the die opening of the extruder, different forms, such as tubes of varying thickness and widths, sheets and other shapes may be fabricated. The starch composition leaving the extruder is typically hot and malleable and may be thermomolded. Methods for extruding starches are well known in the art. See, for example, R.Chinnaswamy and M. A. Hanna, J. Fd. Sci. , 53 :3, pp. 834-838 (1988); and C. Mercier, P. Linko, J. M. Harper, Extrusion Cooking , The American Association of Cereal Chemists, Inc. St. Paul, Minnesota, 1989. Other methods, including injection molding, blow molding, extrusion/blow molding, stamping and casting, and combinations thereof, may be employed herein. Whatever method is chosen, it is critical that the finished tampon applicator have a substantially rigid shape and retain some tensile strength and plasticity along with a water-disperable, biodegradable character. In the examples which follow, all parts and percentages are given by weight and all temperatures are in degrees Celsius unless otherwise noted. Reagent percentages are based on dry starch. Example 1 This example illustrates the preparation of the starch-containing compositions and tampon applicators of this invention. The compositions set forth in Table 1 were prepared by the methods described below and in the footnotes to Table 1. The starch, sorbitol solution, water and dextrin, where applicable, were blended and cooked in a boiling water bath for 20 minutes. In the alternative, the composition was cooked at 149 o C (300 o F) to gelatinization in a jet-cooker. Where applicable, the compositions were treated after cooking with glyoxal to lightly crosslink the dispersed starch. Plasticized starch films were prepared from the compositions of Table 1 by coating the cooked and cooled composition onto a teflon-coated plate employing a Bird Applicator (MCD Industries, Medford, Massachusetts) to give a 0.15, 0.25 or 0.51 mm (0.006, 0.01 or 0.02 inch) thick wet film. The films were tested for load (the grams of force required to break a 2.5 cm (1 inch) wide by 10.1 cm (4 inch) long strip of film), elongation (the distance the 2.5 x 10.1 cm (1 x 4 inch) strip stretches before breaking, expressed as a % of 10.1 cm (4 inches)) and the Total Energy Absorbed (TEA). These tensile strength measurements were made in accordance with TAPPI T496 method ("Tensile Breaking Properties of Paper and Paperboard [Using Constant Rate of elongation Apparatus], TAPPI T494, 1982). The apparatus used for the tests was a Model II Intellect Machine (Thwing-Albert Instrument Company, Philadelphia, PA). Results are shown in Table I. Crosslinking improved the load strength of the films in a linear manner. Crosslinking caused an initial increase in tensile strength followed by a decrease as more glyoxal was employed. Thus, an optimum level of crosslinking (at about 0.5%, by starch weight, maximum) was identified. As a filler, dextrin had a beneficial effect on film strength. After curing the films for 24 hours at 50-70% relative humidity, the films were rolled into tubes on a 2.5 cm (1.0 inch) lucite rod coated with a thin film of mineral oil. This assembly was rolled between weighted plates to fuse the film and form rigid tubes. The tubes were removed from the rod and stored at ambient temperature and humidity for more than three months. They maintained their shape throughout the storage period. No microbial growth was observed on the tubes. The water content of the stored tubes was 8%, by weight. When placed in water, the tubes softened quickly, lost their shape within 10-120 seconds (depending on tube thickness), broke-up, and dissolved within minutes.

Claims: A water-dispersable, toilet-disposable, biodegradable applicator for tampons, comprising 45 to 90%, by weight, of a modified or unmodified carbohydrate and optionally lubricants, opacifying agents, antimicrobial agents, fragrances and colorants for use in tampon applicators, having a self-supporting, open-ended tube (1) and a substantially rigid biodegradable plunger (3) moveably received within the tube (1) and adapted to expel a tampon (2) from within the tube, characterized in that carbohydrate is a gelatinized starch and that it additionally contains 5 to 40%, per weight, plasticizer and 5 - 15%, per weight, water and excluding hydroxyalkyl cellulose. The applicator of claim 1, characterized in, that it further comprises dextrin. The applicator of claim 1, characterized by a water content of less than 15%, by weight, and a water activity of less than 0,80 and being resistant to microbial growth at less than 30 °C and less than 80% relative humidity. The applicator of one of the preceding claims, characterized in, that the gelatinized starch is derivatized by a reaction with up to 20%, by weight, propylene oxide. The applicator of claim 4, characterized in, that the starch contains at least 40% amylose. The applicator of one of the preceding claims, characterized in, that the starch is crosslinked. The applicator of claim 4, characterized in, that the starch is crosslinked by a reaction with up to 0,5% glyoxal. The applicator of one of the preceding claims, characterized in, that the plasticizer is sorbitol, polyethylene glycol, glycerol, polyethyleneamine, ethylene glycol, tetra-alkyl ammonium salts, tri-alkyl citrates or mono-, di- or triacetates of glycerol, or a combination thereof. A method of making tampon applicators, according to one of the preceding claims from a composition, comprising 30 to 65%, by weight, starch, 10 to 40%, by weight, plasticizer and 20 to 60%, by weight, water, comprising the steps: a) slurrying the starch and plasticizer in water; b) cooking this slurry until the starch is gelatinized; c) casting the composition at a thickness from 0,0038 cm - 0,050 cm (1,5 to 20 mil) onto a surface to receive a film or into a mold and d) drying the composition to a moisture content of less than 15%, by weight and e) rolling the film received by step c) into tubes. A method of making tampon applicators from a biodegradable, toilet-dispersable, thermoplastic composition, comprising 30 to 65%, by weight, starch, 10 to 40%, by weight, plasticizer, 20 to 60%, by weight, water, comprising the steps: a) pumping the starch, plasticizer and water of the above composition into an extruder; b) extruding the composition at greater than atmospheric pressure and temperature from 150 to 250 °C; and c) cutting the extruded composition to form the applicator. The method of claim 10, characterized in, that the composition is extruded in a tubular form.

Inventors: BILLMERS ROBERT L, BILLMERS, ROBERT L.
Applicants: NAT STARCH CHEM INVEST, NATIONAL STARCH AND CHEMICAL INVESTMENT HOLDING CORPORATION
Application year: 1990
Main classification: A61F13
IPC codes: A61F13