Nonvolatile semiconductor memory device having tunnel insulating film structure

Abstract: For improving endurance and retention characteristics of a nonvolatile semiconductor memory device that comprises a semiconductor substrate (1) having source and drain regions (3₁) therein, a floating gate (6) provided above the semiconductor substrate through a first gate insulating film (4), a control gate (8) provided above the floating gate through a second gate insulating film (7), and a tunnel region provided in the first gate insulating film, an aperture (9) is provided in the first gate insulating film (4) so as to reach the semiconductor substrate (1), thereby defining the tunnel region therewith, and a tunnel insulating layer (5) including at least one silicon nitride film (10) is provided within the aperture (9).

Description: The present invention relates to a nonvolatile semiconductor memory device, and more particularly to an EEPROM capable of erasing electrical data. Conventionally, an EEPROM has been known as a nonvolatile semiconductor memory device capable of erasing/writing electrical data. The feature of the EEPROM is the following point. The EEPROM includes a tunnel region for electrically removing charges which represent storage information stored in a floating gate. In the latest EEPROM, a single-layer silicon oxide film having a thin thickness is formed at the tunnel region. Charges, i.e., electrons, tunnel through the thin single-layer silicon oxide film and are transferred to a high potential region. For example, when a high voltage is applied to a drain region, electrons stored in a gate electrode tunnel through the single-layer silicon oxide film and are transferred to the drain region. The most important reliability factor of the EEPROM is an endurance characteristic of the tunnel insulating film (repetition characteristic for erasing/writing data, which correspond to repetitive operations for injecting electrons into a floating gate and removing the electrons from the floating gate). The endurance characteristic depends on the quality of the tunnel insulating film. As described above, the single-layer silicon oxide film is used as the tunnel insolating film. At the present the limit of the endurance characteristic is given by the number of repititions of 10 4 to 10 5 in 64-Kbit EEPROMs. A tunnelling gate semiconductor device known from EP-0 086 372 A2 comprises source and drain regions formed in a substrate, a floating gate formed on a first gate insulating film, and a control gate formed over the floating gate through a second gate insulating film. An aperture defining a tunnel region is located in the first gate insulating film. In the tunnel region the floating gate is separated from the substrate by a tunnel insulating layer which may comprise a silicon oxide layer having a thickness of about 100 Å (10 nm) or a silicon nitride layer. A semiconductor device like an EEPROM known from JP-A-61147576 comprises source and drain regions formed in a substrate, a floating gate formed on a first gate insulating film and a control gate formed over the floating gate through a second gate insulating film. The first gate insulating film includes a tunnel region composed of three layers of a silicon oxide film, a silicon nitride film and a thin silicon oxide film. The thickness of the first silicon oxide film in the tunnel region is about 60 Å (6 nm), the thickness of the silicon nitride film is about 80 Å (8 nm) and the thin silicon oxide film has a thickness smaller than 20 Å (2 nm). Another semiconductor device known from JP-A-5966171 includes source and drain regions formed in a substrate, a floating gate formed on a first gate insulating film, and a control gate formed over the floating gate through a second gate insulating film. The first gate insulating film is provided with a tunnel region composed of a silicon oxide film having a thickness of about 15 Å (1,5 nm) and a silicon nitride film having a thickness of about 60 Å (6 nm). The object of the present invention is to provide a non-volatile semiconductor memory device including a tunnel insulating film having an improved endurance characteristic. This object is achieved by a non-volatile semiconductor memory device according to claim 1. The novel and distinctive features of the present invention are set forth in the claims appended to the present application. The invention itself, however, together with further objects and advantages thereof may best be understood by reference to the following description and accompanying drawings in which: Fig. 1 the plan view showing memory cell of a non-volatile semiconductor memory device according to the first embodiment of the present invention; Fig. 2 is a sectional view showing the memory cell taken along a line A-A' in Fig. 1; Fig. 3 is a sectional view showing the memory cell taken along a line B - B' in Fig. 1; Fig. 4 is an enlarged sectional view showing the memory cell in a circle C in Fig. 2; Figs. 5A to 5C are sectional views showing a method of making a memory cell of the nonvolatile semiconductor memory device according to the first embodiment of the present invention; Fig. 6 is a sectional view showing a part of a memory cell of a nonvolatile semiconductor memory device according to the second embodiment of the present invention; Fig.7 is a sectional view showing a part of a memory cell of a nonvolatile semiconductor memory device according to the third embodiment of the present invention; Fig.8 is a plan view showing a part of a memory cell of a nonvolatile semiconductor memory device according to the fourth embodiment of the present invention; Fig.9 is a sectional view showing the memory cell taken along a line D - D' in Fig. 9; Fig. 10 is a sectional view showing the memory cell taken along a line E - E' in Fig. 9; Fig. 11 is a sectional view showing a part of a memory cell of a nonvolatile semiconductor memory device according to the fifth embodiment of the present invention; and Figs. 12A to 12E are sectional views showing a method of making the memory cell of the nonvolatile semiconductor memory device according to the fifth embodiment of the present invention. Semiconductor devices according to embodiments of the present invention will be described below with reference to the accompanying drawings. Fig. 1 is a plan view especially showing a memory cell of a nonvolatile semiconductor memory device according to the first embodiment of the present invention, Fig. 2 is a sectional view showing the memory cell taken along a line A - A' in Fig. 1, and Fig. 3 is a sectional view showing the memory cell taken along a line B - B' in Fig. 1. Fig. 4 is an enlarged view showing the memory cell in a circle C in Fig. 2. As shown in Figs. 1, 2, and 3, an isolation region 2 is formed in a semiconductor substrate 1 to perform element isolation. Diffused source/drain regions 3 (3 1 , 3 2 ) of a conductivity type opposite to that of the substrate are formed in an element region provided by the element isolation. A first gate insulating film 4 is provided on the substrate between the diffused layers. A part of the first gate insulating film extends on the source or drain region 31, and a tunnel region 5 is formed in the first gate insulating film. The tunnel region 5 has a tunnel insulating film, through which charges are transferred between a floating gate 6 and the diffused region 3 1 . A control gate 8 is provided on the floating gate 6 through a second gate insulating film 7 and is capacitively coupled with the floating gate 6. The feature of the memory device according to the first embodiment of the present invention is that a tunnel insulating film provided within the tunnel region 5 is constituted by a multilayer film comprised of a silicon nitride film 10 and a silicon oxide film 11. As described above, since the multilayer film is comprised of the silicon nitride film 10 and the silicon oxide film 11, the endurance characteristic can be improved to increase the life of the semiconductor device. A relationship between the silicon nitride film 10 and the silicon oxide film 11 in the multilayer film will be described below. I have described that the tunnel insulating film is provided by the single-layer silicon oxide film in the conventional structure. In this case, upon FN (Fowler-Nordheim) tunneling of electrons, the electrons may be trapped in the single-layer silicon oxide film, and this is a factor for deteriorating the endurance characteristic of the tunnel insulating film. It has been known that an average electron trapping distance in the silicon oxide film is about 50 Å (1nm = 10 Å). When the thickness of the silicon oxide film is about 50 Å, most of the electrons directly tunnel through the silicon oxide film. Therefore, the number of electrons moving through a conduction band of the silicon oxide film is decreased, and this means that the probability of electron trapping is further decreased. In order to form the tunnel insulating film by a single-layer silicon oxide film, the silicon oxide film is required to have a thickness of at least 80 Å for obtaining sufficient reliability. This is a well-known fact (reference document: Tech, Dig. IEEE, IEDMP-424 1988). That is, when the thickness of the silicon oxide film is 80 Å, the probability of electron trapping may be remarkably increased in the remaining region having a thickness of 30 Å obtained by subtracting a region having a thickness of 50 Å through which electrons can directly tunnel from the region having the thickness of 80 Å. As a result, the endurance characteristic of the tunnel insulating film may be lowered due to the electron trapping. Therefore, according to the present invention, the thickness of the silicon oxide film 11 is defined by 50 Å or less, and the electron trapping is theoretically eliminated. Further, the degradation of the reliability of the tunnel insulating film, caused by a decrease in the thickness of the silicon oxide film, is compensated by providing the silicon nitride film 10 on the silicon oxide film. Electron trapping in the silicon nitride film 10 does not become a decisive factor for deteriorating the endurance characteristic of the tunnel insulating film due to the following reason. Although, like the silicon oxide film 11, the silicon nitride film 10 has a deep level, when an electric field is applied to the silicon nitride film, trapped electrons can escape outside the silicon nitride film. That is, electrons trapped in the silicon oxide film 11 at the deep level cannot almost be extracted, and they may be stored as fixed charges. However, since electrons trapped at the deep level of the silicon nitride film 10 can be extracted, they may not become the fixed charges. Even when the electrons are trapped at the deep level of the silicon nitride film, they may be recombined with holes injected into the film and may disappear. Regarding this point, electron trapping in the silicon nitride film 10 may be rather desirable. For example, a charge retention characteristic, which is a factor of the reliability of EEPROMs, can be expectedly improved. That is, since electrons which tend to escape from the floating gate 6 to the substrate 1 (the diffused region 3 in Figs. 1, 2, and 3) are trapped at the deep level of the silicon nitride film 10, they are difficult to escape to the substrate 1. Therefore, the charge retention characteristic is further improved. further improved. In data erasing, electrons trapped at the deep level of the silicon nitride film 10 can be removed to the high potential region together with electrons stored in the floating gate 6. Therefore, incomplete erasing may not occur. The silicon nitride film 11 is also effective as a charge storage portion. Although the charge storage effect is low as compared with the storage amount of the floating gate 6 serving as the main charge storage portion. However, the charge storage effect may be increased as fine pattern technologies are improved. As described above, the average electron trapping distance in the silicon nitride film is about 35 Å (reference document: P.C.Arnett and B.H.Ynn, Appl. Phys. Lett., vol 26, pp.94, 1975). Therefore, in order to effectively trap electrons, the silicon nitride film must have the thickness at least two times the above average trapping distance, i.e., 70 Å or more (reference document: Eiichi Suzuki "A STUDY ON DEGRADATION MECHANISMS AND LOW VOLTAGE OPERATIONS IN MNOS-TYPE MEMORY DEVICES" disclosed in "RESEARCHES OF THE ELECTROTECHNICAL LABORATORY" No. 844, May, 1984, P-110). When the above electron trapping is summarized, it is effective that the thickness of the silicon oxide film 11 is 50 Å or less and that the thickness of the silicon nitride film 10 is 70 Å or more. Trapping of holes serving as the other carrier will be described below. When holes are trapped in the tunnel oxide film, the endurance characteristic of the film may be degraded. As a result, the insulating film itself is broken (reference document: IEDM. 1986. Oxide breakdown dependence on thickness and hole current-enhanced reliability of ultra thin oxides. I.C. Chen et al.) In a silicon oxide film, an average hole trapping distance is about 10 Å (reference document: R.C. Hughes and C.H. Seqger, IEEE TRANS. ES-30, No. 6, DEC, 1983). In order to prevent the hole trapping in the silicon oxide film, theoretically, the thickness of the film must be defined by 10 Å or less. However, it is very difficult to form the silicon oxide film having the thickness of 10 Å. (For example, a natural oxide film having a thickness of about 20 Å is said to be formed on the surface of silicon in the air.) From this point of view, according to the present invention, a silicon oxide film having the minimum thickness, for example, 2 Å which can be obtained by the most advanced technique is used, and the probability of hole trapping is minimized. By the most advanced technique, a silicon oxide film having a thickness of about 50 Å can be properly formed. When the silicon oxide film having the thickness of about 50 Å is used, the number of trapped holes is negligible in practical use. An average hole trapping distance in a silicon nitride film is relatively large as given by about 155 Å. This is because holes are used as a main conduction carrier in the silicon nitride film (reference document: H.E. Maes and R.J. Van. Overstraeten, J. Appl. Phys, vol. 47, P-667 1976). Therefore, if the silicon nitride film having the thickness of 155 Å or less is used, hole trapping may not almost theoretically occur. When the above hole trapping is summarized, it is effective that the thickness of the silicon oxide film 11 is 50 Å or less and that the thickness of the silicon nitride film 10 is 155 Å or less. In the multilayer tunnel insulating film included in the semiconductor device according to the present invention, the following relationship between the thicknesses of the silicon nitride film 10 and the silicon oxide film 11 is desirable. That is, the thickness of the silicon oxide film 11 is desirably 50 Å or less, and the thickness of the silicon nitride film 10 is desirably within a range of 70 Å to 155 Å. When an insulating film is comprised of a multilayer structure including at least the silicon nitride film 10 and the silicon oxide film 11, the thickness of the silicon nitride film 10 is set to be larger than that of the silicon oxide film 11. Therefore, the endurance characteristic of the tunnel insulating film can be further improved. A method of making the device according to the first embodiment of the present invention will be described on only a characteristic portion with reference to Figs. 5A to 5C. Figs. 5A to 5C are enlarged views showing a manufacturing process in the circle C of Fig. 2. As shown in Fig. 5A, a diffused region 3 of one conductivity type opposite to that of a substrate is formed in the substrate (not shown). A first gate oxide film 4 is then formed on the surface of the region by, e.g., thermal oxidation techniques. After the oxide film 4 is coated with a photoresist layer 12, a desired opening pattern for a tunnel region is formed therein by photoetching techniques. The first gate oxide film 4 is selectively removed to provide an aperture 9. As shown in Fig. 5B, after the photoresist 12 layer is removed, the silicon nitride film 10 is deposited by, e.g., CVD techniques. A thermal oxide film 11 is formed on the surface of the silicon nitride film 10 by, e.g., a hydrogen combustion oxidation technique which is one of thermal oxidation techniques. In this case, the silicon nitride film 10 may be formed by not only the CVD techniques but also, e.g., thermal nitrogenation techniques such as so-called silicon direct nitrogenation techniques. As shown in Fig. 5C, a polysilicon layer 6 for a floating gate is deposited by, e.g., CVD techniques. The semiconductor device may be made according to a conventional EEPROM manufacturing process. According to the above manufacturing process, the EEPROM can be provided which includes memory cells each having the tunnel insulating film 5 comprised of the silicon nitride film 10 and the silicon oxide film 11. The second and third embodiments will be described below with reference to Figs. 6 and 7, respectively. Referring to Figs. 6 and 7, the reference numerals correspond to these in Figs. 1 to 3, a repetitive description will be omitted. Figs. 6 and 7 correspond to the enlarged view in the circle C in Fig. 2. Fig. 6 is an enlarged view showing a tunnel region of a device according to the second embodiment. A tunnel insulating film formed in the tunnel region 5 is constituted by a four-layer structure comprised of a silicon nitride film 14, a silicon oxide film 15, a silicon nitride film 16, and a silicon oxide film 17. In this case, the same advantages as in the first embodiment can be obtained. Fig. 7 is an enlarged view showing a tunnel region of a device according to the third embodiment. A tunnel insulating film formed in a tunnel region 5 is constituted by a three-layer structure comprised of a silicon oxide film 18, a silicon nitride film 19, and a silicon oxide film 20. In this case, the same advantages as in the first embodiment can be obtained. In the embodiment, the silicon oxide film 18 is formed to be in contact with the substrate (the diffused region 3), and the silicon oxide film 20 is formed to be in contact with a floating gate 6. For this reason, the silicon nitride film 19 is not in contact with the substrate (the diffused region 3) and the silicon layer the floating gate 6. This is the best structure capable of suppressing the formation of surface state at present. Note that the tunnel insulating film may be provided by a different combination of silicon nitride and oxide films from those used in first to third embodiments. The devices shown in the second and third embodiments can be manufactured by the similar process described in the first embodiment. For example, the device can be made by, e.g., changing an order of formation of the silicon nitride film and the silicon oxide film. The fourth embodiment of the present invention will be described below with reference to Fig. 8 to 10. In this embodiment, an arrangement of a tunnel insulating film according to the present invention is applied to a batch-erasing type EEPROM. Fig. 8 is a plan view showing the device according to the fourth embodiment and especially illustrating a memory cell. Fig. 9 is a sectional view showing the device taken along a line D - D' in Fig. 8, and Fig. 10 is a sectional view showing the device taken along a line E - E' in Fig. 8. As shown in Figs. 8 to 10, an isolation region 22 is formed in a semiconductor substrate 21 to perform element isolation. Diffused drain/source regions 23 (23 1 , 23 2 ) of a conductivity type opposite to that of the substrate are formed in an element region obtained by the element isolation. A first gate insulating film 24 is provided on the substrate between these regions, and a silicon nitride film 25 and a silicon oxide film 26 are sequentially provided thereon. The multilayer film extends above the source region 23 2 over the end portion of the first gate insulating film 24. The extended region provides a tunnel region, and the multilayer film serves as a tunnel insulating film 27. Charges are transferred between a floating gate 28 and the substrate 21 or the source region 23 2 through the tunnel insulating film 27. A control gate 30 is provided above the floating gate 28 through a second gate insulating film 29. An interlevel insulator 31 is provided on the entire surface of the resultant structure to insulate different conductive layers from one other. The interlevel insulator 31 includes a contact hole reaching the drain region 23 1 so as to provide a bit line 33 therein. According to the embodiment, like the above embodiments, the endurance characteristic of the tunnel insulating film can be improved to increase the life of the device. In this case, the tunnel region may be provided on the drain region (bit line side) in conjunction with a bias. In the fourth embodiment, the multilayer film comprised of the silicon nitride film and the silicon oxide film described in the first embodiment is used as the tunnel insulating film. The tunnel insulating film having the structure described in the first to third embodiments may be used as the tunnel insulating film 27. In addition, a tunnel insulating film may be employed which is provided by a different combination of silicon nitride and oxide films from those used in the first to third embodiments. A device according to the fifth embodiment and a method of making the same will be described below with reference to Fig. 11 and Figs. 12A to 12E. According to the embodiment, a tunnel insulating film according to the present invention extends to a gate insulating film of a select gate of an EEPROM to increase the breakdown voltage thereof. Fig. 11 is a sectional view showing a device according to the fifth embodiment and especially illustrating a memory cell. First, a memory transistor of the memory cell will be described below. As shown in Fig. 11, an isolation region (not shown) is formed in a semiconductor substrate 41 to perform element isolation. Diffused source/drain regions 42 (42 1 , 42 2 , 42 3 ) of a conductivity type opposite to that of the substrate are provided in an element region obtained by the element isolation. A first gate insulating film 44 is provided on the substrate among the diffused regions 42 1 , 42 2 , and 42 3 . A part of the first gate insulating film extends to the diffused regions 42 2 , and a tunnel region 45 is provided in the first gate insulating film. The tunnel region 45 includes a tunnel insulating film 48 with a multilayer structure which is comprised of a silicon nitride film 46 and a silicon oxide film 47. Charges are transferred through the tunnel insulating film 48 between a floating gate 49 and the diffused region 422 formed in the substrate 41. A control gate 51 is provided above the floating gate 49 through a second gate insulating film 50. A structure of a select transistor will be described below. A gate insulating film 55 with a multilayer structure is provided on the substrate 41 between the diffused regions 42 1 and 422. The gate insulating film 55 includes an insulating film 52 provided by the first gate insulating film 44, a silicon nitride film 53 and a silicon oxide film 54 both of which are provided by the tunnel insulating film 48. A select gate 56 is provided on the gate insulating film 55. According to the fifth embodiment, the gate insulating film for the select gate 56 has the multilayer structure which includes the insulating film provided by the tunnel insulating film 48 and the insulating film provided by the first gate insulating film 58. Therefore, since the gate insulating film 55 is used in place of a gate insulating film conventionally provided by only the insulating film 52, an effective electric field can be decreased. In addition, an unwanted fault of the film can be reduced by the multilayer structure using the nitride film. The above structure is very effective to prevent EEPROMs from unwanted fault of rows. A manufacturing method of the device according to the fifth embodiment will be described below with reference to Figs. 12A to 12E. The same reference numerals in Figs. 12 A to 12E denote the same parts as in Fig. 11. As shown in Fig. 12A, an impurity of a conductivity type opposite to that of the substrate 41 is ion-implanted into the substrate 41 to provide diffused regions 57 (57 1 , 57 2 ). As shown in Fig. 12B, a first thermal oxide film 58 is formed on the surface of the substrate 41 by, e.g., thermal oxidation techniques. After coating the entire surface of the resultant structure with a photoresist layer 59, an opening pattern corresponding to a tunnel region is formed in the photoresist layer by photoetching techniques. This pattern is adjusted to be located on the diffused layer 57 1 . The thermal oxide film 58 is etched using the photoresist layer 59 as a mask thereby forming an aperture 60 therein. As shown in Fig. 12C, a silicon nitride film 61 is deposited by, e.g., CVD techniques, and a second oxide film 62 is formed on the surface of the silicon nitride film 61 by, e.g., hydrogen combustion oxidation techniques. As shown in Fig. 12D, for example, a first polysilicon layer 63 is deposited on the resultant structure by CVD techniques as a conductive layer serving as a floating gate and a select gate. As shown in Fig. 12E, a second gate insulating film 50 is formed by, e.g., thermal oxidation techniques, and a second polysilicon layer is deposited by CVD techniques as a conductive layer serving as a control gate. The second polysilicon layer is patterned to provide the control gate. The second gate insulating film, the first polysilicon layer 63, and the gate insulating film 55 are successively removed by etching, using the patterned polysilicon layer as a mask. Thus, a memory transistor is provided which includes the gate insulating film 65, the floating gate 49, the second gate insulating film 50, and the control gate 51. In this case, the floating gate 49 is formed to overlap at least a part of the diffused regions 57 1 and 57 2 . In the select transistor, the gate insulating film 55 with the multilayer structure is almost completed which includes the insulating film 58 for the first gate insulating film, the silicon nitride film 61 and the silicon oxide film 62. In Fig. 12E, although the second polysilicon layer is removed from the select gate 56, it is not necessarily removed. Thereafter, although not shown, the device may be made by a usual process for the EEPROMs. According to the manufacturing method described above, in the step of forming the tunnel insulating film having the structure according to the present invention, the first polysilicon layer 63 for the select gate 56 is deposited while the silicon nitride film 61 remains. Therefore, the gate insulating film 55 for the select gate 56 can be formed without increasing the number of manufacturing steps, and its breakdown voltage can be increased. As a result, the structure described above is very effective to prevent EEPROMs form the unwanted fault of rows to remarkably increase the reliability. In addition, the device can be made without greatly increasing the manufacturing cost. In the fifth embodiment, although the structure of the, tunnel insulating film used in the first embodiment is stacked on the gate insulating film of the floating gate, the structure of the tunnel insulating film described in the second to fourth embodiments may be stacked thereon. The tunnel insulating film may be provided by a different combination of silicon nitride and oxide films from those used in the first to third embodiment. In the EEPROMs according to the first to fifth embodiments, electron trapping and hole trapping that have become the problem in the single-layer silicon oxide film used as the tunnel insulating film are improved. For example, in the write/erase cycling that depends upon both the breakdown of the tunnel insulating film and the endurance thereof, the number of writes can be increased by about ten times in 64-Kbit EEPROMs. This is because the life due to a constant current stress is particularly increased in relation to the breakdown of the tunnel insulating film, and a so-called narrowing effect, i.e., change in the threshold value of the memory transistor, is improved. In the fifth embodiment, since the insulating film used in the tunnel insulating film, especially the silicon nitride film, is stacked on the gate insulating film of the select gate, the effective electric field of the gate insulating film can be decreased to remarkably reduce the fault of rows in EEPROMs. According to the first to fifth embodiments, although polysilicon films are used as materials for various gates, silicide films such as molybdenum silicide may be used. Even if the above gate materials are used, the advantages of the present invention can be maintained. As described above, in the nonvolatile semiconductor memory device according to the present invention, since the silicon nitride film or the multilayer film comprised of at least the silicon nitride film and the silicon oxide film is used as the tunnel insulating film, the endurance characteristic can be improved, thereby increasing the life of the nonvolatile semiconductor memory device. It is further understood by those skilled in the art that the foregoing description is preferred embodiments of the disclosed device and that various changes and modifications may be made in the invention without departing from the scope thereof. Reference signs in the claims are intended for better understanding and shall not limit the scope.

Claims: A nonvolatile semiconductor memory device comprising a semiconductor substrate (1; 41) having source and drain regions(3 1 , 3 2 ) therein, a floating gate (6) provided above said semiconductor substrate through a first gate insulating film (4) , a control gate (8) provided above said floating gate through a second gate insulating film (7), and a tunnel region provided in said first gate insulating film, an aperture (9) being provided in said first gate insulating film (4) so as to reach said semiconductor substrate (1; 41), thereby defining said tunnel region therewith, and a tunnel insulating layer (5) being provided within said aperture (9), said tunnel insulating layer (5) being a multilayer structure including at least one silicon nitride film (10) and at least one silicon oxide film (11) alternately stacked, wherein the thickness of said silicon nitride film (10) is 7.0 to 15.5 nm (70 to 155 Å), and the thickness of said silicon oxide film (11) is 0.2 to 5.0 nm (2 to 50Å). The device according to claim 1 characterized in that said silicon nitride film (10) is directly in contact with said semiconductor substrate (1) within said aperture (9). The device according to claim 1, characterized in that said silicon oxide film (11, 18) is directly in contact with said semiconductor substrate (1) within said aperture (9). The device according to claim 1, characterized in that a select gate (56) is provided through an insulating layer (55) above said semiconductor substrate (41). The device according to claim 4, characterized in that said insulating layer (55) is comprised of said first gate insulating film and said tunnel insulating layer.

Inventors: TAKEBUCHI MASATAKA, TAKEBUCHI, MASATAKA, TAKEBUCHI, MASATAKA, C/O INTELLECTUAL PROPERTY
Applicants: TOSHIBA KK, KABUSHIKI KAISHA TOSHIBA
Application year: 1990
Main classification: H01L29
IPC codes: H01L29, H01L27, H01L21