Process for the synthesis of soluble, condensed hydridosilicon resins containing low levels of silanol

Abstract: This invention relates to an improved method of hydrolyzing hydridosilanes with 2 or more hydrolyzable groups which comprises forming an arylsulfonic acid hydrate containing reaction medium, adding the silane to the hydrolysis medium, facilitating hydrolysis of the silane to form the polymer, settling the hydrolysis medium and polymer into an acid layer and an organic layer containing the polymer, separating the organic layer from the acid layer, contacting the organic layer with a neutralizing agent and removing the neutralizing agent from the organic layer.

Description: This invention relates to an improved method of hydrolysing hydridosilanes with 2 or more hydrolysable groups to form polymers, said method comprising forming an aryl-sulfonic acid hydrate containing hydrolysis medium, adding the silane to the hydrolysis medium, facilitating hydrolysis of the silane to form the polymer, settling the hydrolysis medium and polymer into an acid layer and an organic layer containing the polymer, separating the organic layer from the acid layer, contacting the organic layer with a neutralizing agent and separating the organic layer from the neutralizing agent. Processes for hydrolysing silanes are disclosed in US-A-2 901 460 and US-A-3 489 782. US-A-3 615 272 discloses a process for the production of a condensed soluble hydrogensilsesquioxane resin, free of hydroxyl content, of the general formula (HSiO 3/2 ) n by the condensation of trichloro, trimethoxy or triacetoxy silane in a two phase reaction medium comprising concentrated sulphuric acid and an aromatic hydrocarbon. It has been unexpectedly found that the process of the present invention provides an improved commercially viable process for the synthesis of hydrocarbon soluble siloxane resins. The invention provides a method of hydrolysing a silane of the formula H a SiX 4-a where a is 1 or 2 and X is a hydrolysable group, selected from halogens, organic groups linked to the silicon atom by oxygen bonds, sulfur functional groups and nitrogen functional groups, to produce polymers containing units of the formula H a SiO (4-a)/2 , the method comprising: forming a hydrolysis medium containing an arylsulfonic acid hydrate, adding a liquid containing the silane to the agitated hydrolysis medium, facilitating hydrolysis of the silane in the hydrolysis medium to form the polymer, settling the hydrolysis medium and polymer into immiscible layers comprising an acid layer and an organic layer where the organic layer contains the polymer, separating the organic layer from the acid layer and washing the organic layer with aqueous sulfuric acid, contacting the organic layer with a neutralizing agent sufficiently basic to neutralize the remaining acid species but insufficiently basic to catalyse rearrangement of the polymer or solvolysis of silicon hydrides, the neutralizing agent being in solid form and selected from calcium carbonate, sodium carbonate, sodium bicarbonate, ammonium carbonate, calcium oxide and calcium hydroxide, and separating the organic layer from the neutralizing agent. This process may be performed on both an individual batch basis as well as a continuous operation. The compound to be hydrolyzed in the above reaction can be any hydridosilane with 2 or more hydrolyzable substituents and can be represented by the formula H a SiX 4-a wherein a can be 1 or 2 and X can be the same or different and can include any hydrolyzable group. Suitable hydrolyzable substituents can include, for example, halogens, such as F, Cl, Br or I and organic groups linked to the silicon atom by oxygen bonds such as organoxy or acyloxy groups. Examples of hydrolyzable groups with the Si-O-C linkage include alkoxy such as methoxy, ethoxy, butoxy or hexoxy; alkenyloxy such as allyloxy; cycloalkoxy such as cyclopentoxy or cyclohexoxy; aryloxy such as phenoxy or naphthoxy; cycloalkenyloxy such as cyclopentenyloxy; and acetoxy. The various organic radicals above can also be substituted, for example, by alkyls, aryls or halogens. It is generally preferred that the organic groups of the above radicals contain 1-6 carbon atoms, but groups with higher numbers of carbon atoms may also be used. Additional examples of hydrolyzable substituents can include sulfur functional groups such as sulfuric, organosulfuric or organosulfonic and nitrogen functional groups such as amino or hydrazino. Preferably, the hydrolyzable groups in the above formula are halogens. Upon hydrolysis, these groups will yield a hydrogen halide which may facilitate hydrolysis and/or condensation and is easily removed from the product by washing. On the contrary, if an organoxy group is used, alcohols are formed which may result in the solvolysis of the Si-H bonds and evolution of hydrogen gas. Though these latter groups are functional, facilitating measures such as addition of an acid or a base to the hydrolysis medium may be necessary. Most preferably, the silane utilized in the above invention is trichlorosilane. The various hydridosilanes defined above can be hydrolyzed alone, cohydrolyzed or cohydrolyzed with one or more organosilanes of the formulas R a SiX 4-a or R'RSiX₂ wherein a is one or two, X is as defined above, R is alkyl such as methyl, ethyl, propyl, octyl or dodecyl, a cycloalkyl such as cyclopentyl or cyclohexyl, a cycloalkenyl such as cyclopentenyl or cyclohexenyl, an aryl such as phenyl or naphthyl, an unsaturated hydrocarbon such as vinyl or allyl or R can be any of the above groups substituted with substituents such as halogens, alkyls or aryls including, for example, methylcyclohexyl, phenylethyl or chloromethyl and R' is R or H. Thus, for instance, a cohydrolysate can be formed by mixing varying proportions of an alkytrihalosilane and a hydrogentrihalosilane or a hydrogentrihalosilane and a dialkyldihalosilane. The above silanes are generally utilized in the form of a liquid. This liquid may consist essentially of the silane in its liquid state or it may comprise the silane dissolved in a hydrocarbon solvent to form a solution. If a solvent is to be used, it can include any suitable hydrocarbon which is a solvent for the silane reactant. Exemplary of such solvents are saturated aliphatics such as dodecane, n-pentane, hexane, n-heptane and iso-octane; aromatics such as benzene, toluene and xylene; cycloaliphatics such as cyclohexane; halogenated aliphatics such as trichloroethylene and perchloroethylene; and halogenated aromatics such as bromobenzene and chlorobenzene. Additionally, combinations of the above solvents may be used together as co-solvents for the silane. The preferred hydrocarbons are aromatic compounds because of their high volatility and, of these, toluene is the most preferred because of its safety profile. The hydrolysis medium of the above invention comprises an arylsulfonic acid hydrate solution. The aryl moiety of this compound may comprise, for example, benzene, toluene or xylene. This solution can be formed by either dissolving the arylsulfonic acid hydrate in a solvent, such as an alcohol or it can be generated by reacting an aromatic hydrocarbon with concentrated sulfuric acid. The latter sulfonation reaction, which is the preferred route to the above hydrolysis medium, can be represented as follows: H₂SO₄ + Aromatic Hydrocarbon----->Arylsulfonic acid hydrate The arylsulfonic acid hydrate thereby formed donates the water necessary for silane hydrolysis as described below. The kinetics of the above sulfonation reaction have been studied and found to be mass transfer controlled as a result of the limited solubility of the aromatic hydrocarbon in sulfuric acid. With improved mixing and heating, therefore, both the rate and extent of reaction may be increased. For example, the reaction may be conducted in a baffled device such as a morton flask or in a baffled container with a multibladed stirring mechanism. When the reaction is conducted in such a device stirred at a high rate of speed such as about 200-700 rpm and the temperature is maintained in the range of 20-120°C., the efficiency of sulfonation may be greatly improved. The presence of water in the hydrolysis medium (both the amount present in the sulfuric acid as well as that generated by the reaction), on the other hand, has been shown to limit the sulfonation reaction. For instance, if molar quantities of sulfuric acid and toluene are heated to 45-70°C. for 1 hour and then stirred for 30-60 minutes at 45°C., only about 50-65 weight percent toluenesulfonic acid monohydrate is generated in the acid phase. As water is consumed by the hydrolysis reaction, however, the sulfonation reaction continues until an average of 81.6 weight percent of the toluene sulfonic acid is generated in the acid phase. Since the above factors (i.e. degree of mixing, temperature and quantity of water) make it difficult for 100% sulfonation to occur, it is preferred to employ enough sulfuric acid and aromatic hydrocarbon to generate 200 percent of the water necessary for hydrolysis if 100 percent sulfonation were to occur. The concentrated sulfuric acid utilized in generating the hydrolysis medium may contain up to 10 percent water, e.g., industrial grade but, as discussed supra , the excess water may affect the rate and extent of the sulfonation reaction. Because of this effect, the use of fuming sulfuric acid to consume excess water in the concentrated sulfuric acid prior to sulfonation is a preferred embodiment of the invention. The aromatic hydrocarbons used in the sulfonation reaction can include compounds such as benzene, toluene or xylene. Benzene and toluene are preferred because of their low boiling points which allow them to be easily evaporated to recover the product. Toluene is the most preferred hydrocarbon as it lacks the known toxicities and hazards associated with handling benzene. When the silane is added to the hydrolysis medium, the following reaction occurs: Arylsulfonic acid hydrate + silane--->Polymer + Arylsulfonic acid + HX wherein X is the hydrolyzable group defined supra . Since the silane hydrolysis most likely occurs at the interface of the above organic and acid phases, the hydrolysis medium is agitated during silane addition to increase the surface area of reaction. It is preferred that the silane addition proceed via a slow flow below the liquid surface to reduce the formation of resinous residues on the walls of the reaction vessel which occur as a result of the evolution of gaseous products. Upon addition of the silane, various facilitating measures such as continued vigorous mixing and temperature control are maintained to insure efficient hydrolysis. For example, the various baffled mixing devices described above may be utilized at a rate of about 200-700 rpm while maintaining the hydrolysis temperature in the range of 0-80°C. Formation of the arylsulfonic acid hydrate solution may either precede the introduction of the silane or it may occur concomitantly with the hydrolysis. However, control of the reaction temperature is more complex during concomitant addition due to the exothermic nature of the sulfonation reaction. Accordingly, it is preferred to generate the arylsulfonic acid hydrate prior to hydrolysis of the silane, thereby allowing one to more effectively control the rate and temperature of hydrolysis by external heating or cooling. After the hydrolysis reaction is complete and the polymer formed, the mixture is phase separated by settling. This process may, for example, be accomplished by merely ceasing agitation of the hydrolysis mixture and allowing it to spontaneously separate into immiscible layers in the reaction vessel. The layers thus formed comprise an organic layer, which contains the polymer and the organic solvent and an acid layer. The organic layer is then separated from the acid layer. The separation may be accomplished by any convenient means such as draining off one or the other of the layers. Since the lower layer is generally the acid, it may be most beneficial, for example, to draw off this layer and retain the polymer in the reaction vessel for subsequent neutralization. Neutralization may be effected by contacting the organic layer with the neutralizing agent or the organic layer may first be washed and then contacted with the neutralizer. The latter mechanism is generally preferred since many of the acidic reaction byproducts are removed by the wash and the quantity of neutralizing agent required thereby decreased. If the organic layer is to be washed, the preferred wash solution is an aqueous sulfuric acid solution since it inhibits emulsion formation and product loss which may occur as a result of the surfactant nature of the polymer and the arylsulfonic acid byproduct. Wash solutions containing greater than 5% sulfuric acid are generally operable. The organic layer, either washed or unwashed, is contacted with a neutralizing agent, preferably in the presence of a small quantity of water which promotes hydrolysis of any remaining silane. The neutralizing agent must be sufficiently basic to neutralize any remaining acid species such as sulfuric acid, arylsufonic acid, SiOSO2H, SiOSO₂R, hydrogen halides, organic acids, etc. and yet insufficiently basic to catalyze rearrangement of the polymer or solvolysis of the silicon hydrides. Suitable bases which do not cause the above detrimental effects may be readily determined by a simple test. In this test, a solution of the polymer similar to that generated by the above hydrolysis process is mixed with the base and subjected to conditions of time and temperature similar to those that may be encountered during neutralization. Those bases which result in gel formation or solvolysis of Si-H bonds, as evidenced by hydrogen gas evolution, should not be used. The bases are calcium carbonate, sodium carbonate, sodium bicarbonate, ammonium carbonate, calcium oxide or calcium hydroxide. The base is added to the organic phase as a solid. It has, however, been found that the best results may be obtained when the organic phase contacts the neutralizing agent for only a short time. This may be accomplished, for instance, by stirring in powdered neutralizing agent followed by filtration or by passing the organic phase over or through a bed of particulate neutralizing agent of a size which does not impede flow. The novel neutralization step in the process affords several distinct advantages: 1) it reduces the formation of gels and emulsions previously associated with water washing; 2) it reduces the precipitates which may be seen when various hydrocarbon solvents or co-solvents are utilized; 3) it allows high product yields by avoiding product and solvent loss, especially when the percent solids are increased; 4) it provides products low in sulfur and acid content; 5) it allows for rapid processing; and 6) it allows for processing at higher solids levels. Removing the neutralizing agent from the organic phase yields a solution of the desired polymeric product. It is preferred, however, that the neutralized organic phase be dried and/or filtered to insure that any water soluble salts formed during neutralization or any other insolubles are removed. This step is desirable since the inclusion of such salts or insolubles in the product may adversely affect the polymers properties. Any suitable drying agent such as magnesium sulfate, sodium sulfate or a 3 or 4 angstrom molecular sieve may be utilized. The solid form of the polymer may be recovered by merely removing the solvent. The method of solvent removal is not critical and numerous approaches are well known in the art. For instance, a process comprising (1) distilling off the solvent at atmospheric pressure to form a concentrate containing 40-80% resin and (2) removing the remaining solvent under vacuum and mild heat (0.1-5 hours at 60-120°C.) may be utilized. Alternatively, if it is desired to have the polymer in solution, a simple solvent exchange may be performed by merely adding a secondary solvent and distilling off the first. This option may be especially advantageous where regulatory guidelines restrict the use of certain solvents. The polymers that can be obtained using the hydrolysis reaction of this invention are, naturally, variable depending on the silane utilized. The following nonlimiting list of possible hydrolysates and co-hydrolysates are, however, specifically contemplated: [HSiO 3/2 ] n [H₂SiO]m [HSiO 3/2 ] x [RSiO 3/2 ] y [HSiO 3/2 ] x [RR'SiO] y [HSiO 3/2 ] x [RR'SiO] y [SiO₂] z [HSiO 3/2 ] x [H₂SiO] y Wherein R and R' are as defined supra, n is greater than or equal to 2, m is greater than or equal to 3 and the mole fractions, x, y and z, must total 1 in each of the above copolymers. Of these compounds, the formation of [HSiO 3/2 ] n is of particular interest because of its superior resin characteristics. The above resins are highly condensed products with only about 100-2000 ppm of hydroxyl groups attached to the silicon atom (silanol). They are soluble in suitable hydrocarbon solvents, including those discussed supra , and they are stable in these solutions for periods of greater than six months. Upon heating to elevated temperatures in air, the above resins are converted to smooth protective layers of amorphous silica without pinholes or cracks. See Haluska et al., U.S. Patent 4,756,977. These protective layers have found particular utility in coating electronic circuits wherein they serve as a planarizing coating to preserve the integrity of the circuits against environmental stress. They are applied directly on the primary passivated circuit surface to seal the bond pads, pinholes and cracks of the primary passivation and to provide an adherent surface for subsequently applied coatings. The resins of the invention are generally applied to the surface of the electronic device in the form of a dilute solution by methods such as spin coating, dip coating, spray coating or flow coating. The solvent is then allowed to evaporate by drying to form a homogenous resin which is then ceramified by heating. The thin ceramic layers thereby formed may be further coated with additional passivating layers. The following nonlimiting examples are provided so that one skilled in the art may more fully understand the invention. Example 1 The following is a typical example of the hydrolysis process. 553.4 g of concentrated sulfuric acid (95-98%) and 277.8 g of fuming sulfuric acid (20 % SO₃) (total acid = 8.48 moles/831.2 g) were added to a 5 L vessel. An exotherm to 40°C. was observed. A nitrogen atmosphere was maintained in the vessel as toluene (8.43 moles, 775.9 g) was pumped at a rate of 19.9 mL/min into the acid. During the addition, the mixture was agitated with a paddle stirrer rotating at approximately 500 rpm. The temperature of the mixture rose to 62.5°C. after 24 minutes but subsequently began falling. The temperature was maintained at 48°C. through the remainder of the toluene addition and for a 34 minute post stir. When the agitation was stopped, 2 phases were present; an organic phase containing unreacted toluene and an acid phase containing unreacted sulfuric acid and 64.8 weight percent toluene sulfonic acid. The acid mixture was maintained at 30°C. and rapidly stirred (550-600 rpm) while an 18.2% solution of trichlorosilane (430.3 g/3.18 moles) in toluene (1928 g/20.96 moles) was added at a rate of 8.7 mL/min below the liquid surface. The temperature of the medium was maintained at 30°C. during the 4 hour 52 minute addition and for 30 minutes during a post reaction stir. When the agitation was stopped, the mixture separated into 2 phases and 1407.6 grams of the acid phase was removed and analyzed to reveal 77.5 weight percent toluensulfonic acid. The acid number of the organic phase was 60 mg KOH/gram sample. The organic phase was twice washed with 1 liter of 50% sulfuric acid with subsequent separation. The acid number of the organic phase was now 0.76 mg KOH/gram sample. 51.4 grams of calcium carbonate and 3 ml of water was added to neutralize the gently stirred organic phase. The organic phase was dried by adding 145.12 grams of magnesium sulfate and filtering through a 1 inch thick layer of acid washed supercell on a frit glass. The filtrate was placed in a 3 L flask and distilled at 112°C. for 72 minutes. The resulting solution contained 57.7% solids. The solution was split; the first portion to be dried to a powder and the second to be solvent exchanged. The first portion consisted of 136.52 g and it was stripped at 60°C. and 3.6 mm Hg for 1 hour 5 minutes on a rotary evaporator to yield 78.82 grams of a white powder. The second portion consisted of 116.9 grams which was added to 112.8 grams of dodecane (99%). Solvent was removed by distillation under vacuum until 156.2 grams of toluene free resin in dodecane remained. The total yield of resin in the two portions was 87.3%. (78.82 g in the portion which was stripped). The resin was 100% soluble with a maximum of 56.7% solids in dodecane. The number average molecular weight M(n) was 1464 and 1559 when duplicated. The weight average molecular weight M(w) was 10258 and 11012 when duplicated. The Z-average molecular weight M(z) was 31091 and 34804 when duplicated. The molecular weight dispersity, Mw/Mn, was 7.00 and 7.06 when duplicated. An elemental analysis of the product revealed 34 ppm chloride, 0.016% sulfur, 1.98% carbon, 0.89% hydrogen, 0.9865% Si-H, <5 ppm calcium, <0.5 ppm magnesium and 540 ppm silanol. Example 2 To demonstrate the method of selecting appropriate neutralizing agents, samples of a polymer produced in a manner similar to that of Example 1 were dissolved in toluene and contacted with various mild neutralizing agents. Agents which did not result in gas evolution or gel formation are preferred. Others which only slowly cause gas evolution or gelling may be suitable for use if care is taken to minimize contact time of the neutralizing agent and hydrolyzates during the process of the invention.

Claims: A method of hydrolysing a silane of the formula H a SiX 4-a where a is 1 or 2 and X is a hydrolysable group, selected from halogens, organic groups linked to the silicon atom by oxygen bonds, sulfur functional groups and nitrogen functional groups, to produce polymers containing units of the formula H a SiO (4-a)/2 , the method comprising: forming a hydrolysis medium containing an arylsulfonic acid hydrate, adding a liquid containing the silane to the agitated hydrolysis medium, facilitating hydrolysis of the silane in the hydrolysis medium to form the polymer, settling the hydrolysis medium and polymer into immiscible layers comprising an acid layer and an organic layer where the organic layer contains the polymer, separating the organic layer from the acid layer contacting the organic layer with a neutralizing agent sufficiently basic to neutralize the remaining acid species but insufficiently basic to catalyse rearrangement of the polymer or solvolysis of silicon hydrides, the neutralizing agent being in solid form and selected from calcium carbonate, sodium carbonate, sodium bicarbonate, ammonium carbonate, calcium oxide and calcium hydroxide, and separating the organic layer from the neutralizing agent. A method according to claim 1, in which, after separation and before neutralisation, the organic layer is washed with aqueous sulfuric acid. A method according to claim 1, in which the neutralised organic layer is dried and/or filtered to ensure that any water-soluble salts formed during neutralisation or any other insolubles are removed. A method according to claim 3, in which a drying agent selected from magnesium sulfate, sodium sulfate or a 0.3 or 0.4 nm (3 or 4 angstrom) molecular sieve is used. The method of claim 1 wherein the liquid containing the silane further comprises one or more organo-silanes of the formulas R a SiX 4-a or R'RSiX₂ where a is 1 or 2, X is a hydrolysable group, as defined in Claim 1, R is alkyl, aryl, unsaturated hydrocarbon, substituted alkyl or substituted aryl and R' is R or H. The method of claim 1 wherein the liquid containing the silane consists of the silane and a hydrocarbon solvent. The method of claim 6 wherein the hydrolysis medium is formed by combining an aromatic hydrocarbon and concentrated sulfuric acid. A method according to claim 1, for hydrolysing a silane of the formula HSiCl₃ to produce a polymer containing units of the formula HSiO 3/2 , the method comprising: forming a toluenesulfonic acid hydrate hydrolysis medium by combining toluene and concentrated sulfuric acid, adding trichlorosilane dissolved in toluene to the agitated hydrolysis medium, facilitating hydrolysis of the silane in the hydrolysis medium to form the polymer, settling the hydrolysis medium and polymer into immiscible layers comprising an acid layer and an organic layer where the organic layer contains the polymer and toluene, separating the organic layer from the acid layer and washing the organic layer with aqueous sulfuric acid, contacting the organic layer with solid calcium carbonate to neutralize the remaining acid species, separating the organic layer from the calcium carbonate, contacting the neutralized organic layer with a drying agent, separating the organic layer from the drying agent, and evaporating the solvent.

Inventors: BANK HOWARD MARVIN, CIFUENTES MARTIN ERIC, MARTIN THERESA EILEEN, BANK, HOWARD MARVIN, CIFUENTES, MARTIN ERIC, MARTIN, THERESA EILEEN
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1990
Main classification: C08G77
IPC codes: C08G77