HEATING AND TREATMENT OF PARTICULATE MATERIAL

Abstract: The specification discloses a process for heating solid particulate materials. The process comprises entraining the solid particulate materials in a gas to form a stream of gas containing entrained particles and contacting this stream with a stream of hot gases. The contact between the two streams is performed in such a manner that at least a portion of the solid particulate material is heated rapidly and the heated and unheated particles enter flow patterns in which contact between the particles and with interior surfaces of a contact chamber is minimized. A heating and treatment chamber for applying the process to the treatment of solid particulate materials is disclosed. The specification also discloses a molten bath reactor combined with the chamber for heating and treating solid particulate materials. Hot off gases from the molten bath reactor can be passed through the chamber and treated particulate material from the chamber can be inserted in the molten bath reactor or partially recycled through the chamber.

Description: Heating a_____ Tr atmen of Particulate Material Field of th≤ Invention This invention relates to the heating and treatment of solid particulate materials utilising a stream of hot gas, for example, the off-gas from a molten bath reactor. Carbonate materials such as limestone may be treated according to this invention and subsequently added to an iron-ore derived slag in the molten bath reactor, so as to make a Portland-type cement . Alternatively, the treated carbonate materials may be subsequently added to, for example, a direct iron-making molten bath reactor, a ferroalloy molten bath reactor, or a non-ferrous molten bath reactor. Background __£ the Invention The process for the production of a Portland-type cement from blast furnace slag in a molten bath reactor requires additions of calcium carbonate or calcium oxide to the slag. An object of this invention is to minimise the requirement for additional energy for calcination by utilizing the energy of the hot off-gases that leave the molten bath reacto . Calcination of, for example, limestone, is performed in a variety of f rnaces: vertical shaft kilns, rotary kilns, rotary hearth kilns, twin and multiple shaft regenerative kilns, fluidised beds and entrained flow reactors. Vertical shaft kilns produce ~ι lower "quality -of lime compared with other types of kilns, and can only accept feed of no less than about 50mm in size. Smaller sized feed results in a packed bed of insufficient porosity. Nevertheless, the vertical shaft kiln is a very energy efficient kiln. Rotary kilns are generally able to accept almost any sized feed, down to about 1mm in size. However, to obtain good energy efficiency it is necessary to incorporate preheaters in combination with the kilns. This combination suffers from twin disadvantages of having high capital and maintenance costs. Twin and multiple shaft regenerative kilns offer good energy efficiency, since the waste gas from the calcining kiln is used to preheat other kilns. This sequence is continued around the kilns - successively preheating then calcining in each kiln. However, this type of kiln is not suitable for treating fine sized materials . Fluidised bed calciners are generally able to treat finer sized materials than shaft furnaces. However, control of particle size distribution is important, and large quantities of hot pressurised gas are needed for the fluidisation. Unfortunately, none of these processes can be adapted so that the hot off-gases from a molten bath reactor, which usually contain sticky and/or molten material, can be used as the energy source of calcination. In United States Patent 3,-022, _r&9 (Union Commerce Bank) a process for manufacturing hydraulic cements is disclosed. In this process there is a fluidised bed of particles, in which gases are combusted. A certain amount of stickiness of particles results, but the degree of stickiness is controlled so as to be ir_su.ffici.ent to cause large particles to become attached to one another, and agglomeration of the fluidised mass is thereby prevented. Unfortunately this process requires a fuel to be combusted to provide the high temperatures. It is unlikely that hot off-gases from a molten bath reactor, which contain sticky grains and/or molten droplets could be used to provide the high temperatures. The process operates at a high solids loading, and as a consequence requires that there be a large pressure drop as gases flow through the bed. Furthermore, by virtue of the well-mixed nature of fluidised beds it is not possible to have very large differences between the temperatures of the hottest and coldest particles in the bed. In patent application no. P251515 IVa/12g in the Federal Republic of Germany by Polysius GmbH, an apparatus is disclosed for the combustion, calcination and sintering of a pulverized or granulated product in suspension, and to the operating procedure for such an apparatus. The apparatus seems to be a modified cyclone with a flattened or 'pancake' cross-section. The drawings in the Polysius specification are confusing and seem to contradict the specification, since the paths of the treatment gas, the pulverized or granulated material to be treated and the carburant are drawn in a haphazard manner. The best conclusion seems to be that entrainment of the material to be treated is transitory only, the treated material being separated almost immediately from the treatment gas. No attempt seems to be made to minimise contact of the particles with each other, with a consequent danger of agglomeration. In addition, the particles travel to the wall of the treatment chamber for removal, with a danger in this case of accretion to the wall. Furthermore, the pulverized or granulated material seems to be injected counterflow to the air. In addition carburant is burned in the relatively small space where the particles and gas are travelling counterflow. This must lead to severe turbulence, with particles contacting each other and the wall of the treatment chamber. Finally, the apparatus and process of Polysius do not make use of the sensible heat from off-gases, rather heat must be supplied by burning fuel. ___E_i___f Summary __f ______ invention This invention depends on -the observation that, if particles of a solid which are entrained in a gas are exposed to higher temperatures than achieved in the prior art, desirable effects can he..obtained, for example, calcination and/or raising the temperature of the bulk of the particles of solid. Since the particles are heated to higher temperatures, chemical reactions proceed more rapidly, and so the particles need be raised to these higher temperatures for short durations only. In the description and claims, the term 'particulate material' will be used to designate the 'particles' of feed material undergoing treatment. In the case where finely divided material is entrained in the feed of high temperature treatment gas, the words 'grains' (in respect of partially molten or 'sticky' material) and 'droplets' (in respect of molten material) will be used. However, once treatment has occurred, the grains and droplets will form part of the particulate material, for reasons which will become apparent. The object of the invention may be obtained by passing the particulate material entrained in gas through an inlet port or ports into a chamber where the flow of particulate material combines with a flow of high temperature gas introduced through an orifice in such a manner that at least a portion of the particulate material is heated rapidly, the heated particulate material and at least a major proportion of the unheated particulate material entering flow patterns wherein contact Of the particles in the flow patterns with each other and with interior surfaces in the chamber is minimised. It is preferred that the temperature of the bulk of the particulate material substantially equilibrates prior to leaving the chamber. By this means, the particles have been cooled to below their sticking temperature before they leave the chamber. It is an important feature of this invention that it is essentially an entrainment process and that the bulk of the particulate material being treated in the chamber is transported through the chamber by virtue of entrainment in gas. It is surmised that a region of conventional bubbling bed fluidisation is unnecessary and that the particulate material need not remain in the chamber for a substantial length of time, although the treated material may be passed through the chamber one or more times for further treatment . The present invention develops further the inventions described in no PJ 4545 'Pre-heating and pre-reduction of metal oxide ore using high temperature off-gases ' and no PJ 4546 'Manufacture of ferrochrome by [means of] a molten bath reactor' both in the name of the present applicant and now completed. In one embodiment of the present invention, finely divided carbonate materials, such as limestone, magnesite, dolomite or mixtures of these materials, may be at least partially calcined and the bulk of the material raised to a relatively high temperature ready for addition to a chemical or metallurgical process or for further treatment, for example, further calcination. The high temperature gas may be obtained from any suitable source but is conveniently off-gas from a molten bath reactor. Where off-gas is used, the process according to the reaction performs the function of reaction and/or heating of the particulate material and the off-gas is itself quenched. The off-gas may contain sticky grains or molten droplets of substance. The sticky grains or molten droplets create serious problems in that they adhere to duct and chamber surfaces . Accordingly the presence of these particles has made utilisation of the heat energy of the high temperature gas very difficult. Any sticky or molten substance entrained in the off-gas may adhere to the particulate material being treated. In many cases the presence of a certain amount of this adhering substance is quite acceptable. The present invention largely overcomes the problem of stickiness, adherence and agglomeration. Thus, hot molten bath reactor off-gases containing sticky grains or molten droplets are conveyed from the molten bath reactor to the chamber in a duct . There is no requirement that contact of grains or droplets with the interior surface of the duct be minimised. Rather, the accumulation of deposits on the interior surface of the duct is minimised by maintaining the duct surface at a sufficiently high temperature. This effect is assisted by the " velocity of the off-gas and, preferably, by the inclination of the duct. It is only after the hot molten bath reactor off-gases containing sticky grains or molten droplets enter the chamber that contact must be minimised between particles or droplets and the interior surface of the chamber. The transition from the molten to the solidified stage will largely occur within the chamber, the flow patterns much reducing contact of the mixture of grains or droplets and feed particulate material with the relatively cool interior surfaces of the chamber. Thus the sudden change in cross-sectional area from duct to chamber separates hot interior surfaces from relatively cooler interior surfaces. As the particles reach the chamber exit, they have been cooled to a temperature below their sticking temperature. Hence there is no longer any need to minimise contact between particles and duct or equipment surfaces and established gas/solids treatment procedures can be employed. This invention also provides a chamber for heat treatment of particulate material which comprises at least one orifice for gas at high temperature, at least one inlet port for particulate material entrained in gas and an exit port for treated particulate material, the internal configuration of the orifice (s), inlet port (s) and the exit port being such that at least a portion of the particulate material is heated rapidly and the hot particulate material and at least a major proportion of the remaining particulate material enter flow patterns wherein contact of individual particles with each other and with interior surfaces in the chamber is minimised and the temperature of the bulk of the particulate material approaches equilibrium. The invention further provides apparatus for making use of the chamber defined above, for example, to supply treated particulate material for injection into a molten bath in processes according to patent applications no PJ 4545, PJ 4546 and PK 0426. Accordingly, this invention offers the following advantages: (1) A proportion of the particulate material fed to the chamber may be heated to a very high temperature. For example, in the case of particulate limestone, calcination occurs rapidly at these high temperatures. (2) Loss of particle integrity and accretion to internal surfaces are limited. (3) Retention of finely divided size in the treated particulate material assists subsequent processing. (4) Use is made of the sensible heat of off-gases, reducing overall energy requirements. (5) Hot, sticky grains or molten droplets in off-gas may be removed and the heat recovered. In conventional processes, where such particles are present, recovery of heat is very difficult. Brief Description of the Drawings The embodiments shown in the accompanying figures are for illustrative purposes only. The configuration and positioning of the inlets and outlets may be varied as necessary to obtain the desired results as set out above. In the accompanying drawings, Fig. 1 illustrates one embodiment of the invention described with reference to heating and treatment of particulate carbonate material, such as limestone. Off-gases from a molten bath reactor pass to a heating and calcination chamber. Fresh carbonate material is also passed to this chamber and from there to a separating chamber, where the solids and gases are separated. The treated carbonate material stream is then split into two parts (these parts not necessarily being equal parts) . One part is recirculated to the chamber, whilst the other part is added to the molten bath reactor. Fig. 2 illustrates another embodiment of the invention which features part of the limestone being fed to the molten bath reactor without prior calcination. Fig. 3 illustrates another embodiment of the invention, which features some calcination of the limestone in the hot off-gases, some charging of uncalcined limestone directly into the molten bath reactor, and calcination of some additional limestone in an established calcination process . Fig. 4 illustrates another embodiment of the invention. In this embodiment, cooler particulate material is introduced into the chamber near the chamber exit but in proximity to the chamber walls, so as to provide a falling curtain of cooler particles adjacent to the interior surface. These cooler particles, as they fall towards the off-gas entry nozzle of the chamber become entrained in the flow of off-gas, and leave the chamber through the gas and solids exit port. Detailed Description of the Invention This invention will be described with particular reference to heating and calcining limestone but it can be applied to a range of particulate materials, for example, other carbonate minerals. Certain carbonate-containing minerals contain more than one carbonate. For example, dolomite contains both calcium and magnesium carbonates. Calcination of either or both carbonates is an advantage. It is recognised that calcining may not result in calcination of all of the carbonates or carbonate components. The invention may be used in conjunction with any reactor which produces off-gases at elevated temperature optionally with reducing potential. It may be used for provision of calcined material as a flux added to a molten bath reactor so that a slag of desired composition is obtained. Thus it is of particular use in conjunction with a molten bath reactor, for example, a molten bath reactor used to produce a Portland-type cement from an iron ore-derived slag. The invention, in one embodiment, utilises some of the sensible heat (and, optionally, some of the chemical energy) derived from a pyrometallurgical reactor off-gas, to heat and calcine carbonate materials. These particles of carbonate may be heated to a very high temperature to obtain enhanced rates of calcination of the carbonate. Even if the temperatures employed are lower than the very high temperatures possible, the process according to the invention provides an improvement over the prior art by reducing contact of the particles in the stream of gas with each other and also with interior surfaces . The invention also enables the treatment of fine materials, and materials that are prone to breaking due to their weak nature thus forming fine materials. Whilst this invention has special advantages when the reactor off-gas being used contains sticky or molten particles, this invention may also be used in cases where the reactor off-gas is free from sticky grains or molten droplets. The chamber in which the particulate material is heated, and in some cases treated for some other purpose, is preferably elongated. The orifice (s) for hot gases is/are preferably located at one end of the chamber, preferably axially or close to the longitudinal axis of the chamber. The inlet port(s) for particulate material is/are preferably located close to the orifice (s) . The direction of entry of the inlet port(s) may be radial or slightly tangential to the circumference of the chamber. In the case of slightly tangential entry, a degree of bulk rotation of gas and particulate material is set up within the chamber. In addition a degree of swirl may be imparted to the gas entraining the particulate material by suitable shaping and/or orientation of the port or ports. The cross-s-ectional area of the chamber is desirably substantially greater than the corresponding cross- sectional area of the orifice (s) to minimise direct contact of the off-gases with the walls of the chamber The shape of the or each orifice and of the or each entry port is selected to provide smooth, rounded interior surfaces with the minimum of dead space to reduce or eliminate agglomeration of particles from the molten bath reactor around the port. 14 . The carbonate material particles, for example, are desirably introduced into the chamber at a point or points in close proximity to the point of entry of the off-gases. The carbonate material particles may originate from bulk storage or from another chamber operated in conjunction with the first-mentioned chamber. The particles are transported to the chamber by any suitable gas, for example, off-gas which has been completely oxidised. The carbonate material particles are introduced into the off-gas stream in the chamber in such a manner that they are entrained in the bulk flow of gas, minimising contact between particles and the interior surfaces. Some of the fine carbonate material particles are heated rapidly to very high temperature through contact with the hot off- gases. Other particles are contacted less efficiently with the hot gas, and hence are not heated to as high a temperature. It is surmised that certain flow patterns are set up within the chamber near the walls of the chamber. Heat is lost through the walls of the chamber. The hottest particles are also cooled somewhat by losing heat to other particles that were not heated to the same extent initially. It is thought that at this stage the particles in the flow patterns have dropped in temperature below the sticking temperature. Contact between hot carbonate particles may be minimised by varying the relative proportions of hot gas and carbonate material. Usually the quantity . of gas available is 'given' and is dependent upon the operation of the furnace, for example. Thus the feed rate of particulate material is matched to the flow of gas to avoid, so far as possible, undesirable collision between carbonate material particles and to control the target temperature within the chamber. By the time the particles leave the heating and calcination chamber they are at an essentially uniform temperature. This temperature is sufficiently low as to allow the particles to be handled subsequently in conventional equipment. The chamber may be fitted with an expanded riser or offtake flue to conduct the exit gases and, in this case, the particles will cool further. It may be desirable in certain circumstances to provide external cooling to either or both of the chamber and the riser, for example, to cool the product and recover energy therefrom. Conversely, it may be desirable to provide insulation to obtain the greatest achievable heat recovery, for example, by the use of suitable refractory material. Once the particles have cooled within the chamber to the desired temperature they may be withdrawn from the chamber and passed to further processing, for example, in a cyclone . The residence time of the particles in the region of elevated temperature may be controlled by adjusting flow rate(s) of one or both of .the molten bath off-gases and the carrier gas. It should be noted that the particles may be passed once through the chamber or more than once, as required. Use can be made of chemical energy of the off-gases by introducing an oxygen-containing gas into the off-gas, so as to burn any combustible species in the gas. In one embodiment of this invention, all of the carbonate material used by the process is treated in the heater/calciner described in this invention. The heated and substantially calcined material is then fed into the molten bath reactor. In another embodiment of this invention, the molten bath reactor process requirements for calcined material exceed the quantity that can be calcined in the heater/calciner described in this invention. In such circumstances the additional carbonate material may be injected in an uncalcined form directly into the molten bath reactor. Alternatively part or all of the additional carbonate material may be calcined in an established industrial calcination process (for example, rotary kiln, shaft kiln, fluidised bed, spouting bed calciner) before being fed into the molten bath reactor. In another embodiment of this invention a falling curtain of cooler particulate material is maintained adjacent to the chamber interior surfaces. It is surmised that this curtain ensures that the only particles that contact interior surfaces are those which are sufficiently cool as to be below their sticking temperature. Sticky grains or molten droplets from either the molten bath reactor off- gas or from the material to be treated that would otherwise, because of their trajectories, contact and adhere to interior surfaces, are instead contacted and attached to particles in the falling curtain. By this means it is possible to avoid the build-up of accretions on chamber interior surfaces. Particles in the falling curtain and any attached material are entrained in the bulk flow of off-gas through the chamber and leave the chamber as part of the gas and solids exit stream. It is preferred that further use be made of the molten bath reactor off-gases after they have passed through the heater/treatment chamber and have been separated from the particles in the gas-solids separator. It is preferred that this gas be used to dry and preheat crushed limestone feed (for example, in a rotary kiln or fluidised bed) . The dried and preheated limestone feed may then be introduced to the heater/calcination circuit, to the molten bath reactor or to some other calcination device. This invention also provides a chamber for the heating and treatment of solid particulate materials, for example, calcination of particulate carbonate materials, which comprises: 1. a vessel adapted to confine and direct a flow of particulate material and high temperature gas; 2. an inlet orifice or orifices for hot gases; 3. an inlet port or ports for particulate material entrained in carrier gas; and 4. an ©xit port for the treated particulate material, the inlet orifice(s) 2 and the inlet port(s) 3 being so arranged that the particulate material is initially exposed to heating conditions and subsequently cooled to control agglomeration and sticking. This invention also provides an apparatus for the production of, for example, Portland-type cement, which comprises in combination: 1. a molten bath reactor; 2. means to pass off-gas from the reactor to 3. a chamber or chambers as described above; 4. means to inject fresh particulate material, or particulate material which has been heated and treated, to the chamber or chambers; 5. means to pass the solids entrained in gas from the chamber or chambers to a gas-solid separator or separators, and 6. means to pass at least a proportion of the separated solids and some entraining gas to the reactor, and, if desired, a proportion to the chamber or chambers. The invention may also be used in the direct production of iron, from iron ore or ferroalloy from the appropriate feed ores using the appropriate particulate material to obtain the derived slag. In the specification the term 'sticking temperature' is meant to include the case where stickiness is initiated over a temperature -range -and the adjective 'sticky' indicates that particles are at temperatures within that range. In the specification the term 'oxygen-containing gas' refers to pure oxygen and gas containing oxygen, including air and oxygen-enriched air. In the specification the term 'carbonaceous material 1 refers to any carbon-based material which can be burned to produce a suitably high temperature and includes: anthracite, bituminous or sub-bituminous coal, coking or steaming coal, coke, lignite or brown coal, lignite or brown coal-derived char, heavy petroleum residues and natural gas. • The lignite or brown coal may have been densified using the process disclosed in Australian patent no. 561586 and applications no. 5259086 and 52422/86. A process for preparing a char from such a densified product is disclosed in Australian patent application no. 52234/86. In the specification the molten bath reactor from which the hot off-gases are supplied may, for example, be any of the following: molten iron bath reactor, deep slag process reactor, ferroalloy bath reactor, non-ferrous bath reactor, or any other pyrometallurgical process bath reactor that discharges hot off-gases. In the specification the hot off-gases from the molten bath reactor may contain any of the following, for exa ~ ιple: droplets of molten matte or metal or slag ejected from the molten bath reactor due to top or bottom blowing or stirring; - droplets of slag containing coke or coal particles from injection or charging of coke or coal, and - grains of coke, coal, flux, ore or concentrate charged to the molten bath reactor but entrained directly into the off-gas. A more detailed consideration of the use of off-gases from, for example, a molten bath reactor is now provided with reference to the accompanying drawings. These off- gases may contain a relatively high concentration of carbon monoxide and hydrogen. The exit temperature of these gases from the molten bath reactor may range from 1100 to 1800°C. These off-gases are passed to a heating and treatment chamber P as shown in Fig. 1, where they exit from orifice A into the. chamber...Orifice .A is ..located upstream from ports B through which are passed fresh feed in a carrier gas. The spatial relationship of orifice A to ports B and the internal dimensions of chamber P are chosen to promote rapid heating of some of the, for example, carbonate, particles in the general region near ports B, followed by cooling as the particles penetrate further into the chamber. In this way melting of the particles is controlled and stickiness reduced. The geometry and spatial relationship of orifice A and ports B and their spatial relationship are chosen also to reduce contact of the particles with the walls of the chamber, reducing or preventing build-up on the walls. Entrained solids are passed to gas solids separator G, the still relatively hot gas being then used in a dryer/preheater D. The treated solids from G are then passed to a stream divider S. Part of the treated solids may be recycled to chamber P and part may be fed to molten bath reactor M. Fresh feed is added to chamber P from dryer/preheater D. Referring to Fig. 2, part of the fresh feed may be passed directly to molten bath reactor M from a second stream divider S2 (the first stream divider being designated SI in this case) . Referring to Fig. 3, the additional element in this embodiment is the use of an established calcination process to provide part of the calcined feed to molten bath reactor M. With reference to Fig. 4, the operation of this embodiment, in which protection for the interior surface of chamber M is enhanced by a falling outer curtain of cooler particles, has been described above. It will be clearly understood that the invention in its general aspects is not limited to the specific details referred to hereinabove.

Claims: The claims defining the invention are as follows: 1. A process for the heating and treatment of solid particulate materials by utilising a stream of high temperature gas,introduced through an orifice which comprises passing the particulate material entrained in gas through an inlet port or ports into a chamber where the flow of particulate material combines with the flow of high temperature gas in such a manner that at least a portion of the particulate material is heated rapidly, the heated particulate material and at least a major proportion of the unheated particulate material entering flow patterns wherein contact of the particles in the flow patterns with each other and with interior surfaces in the chamber is minimised. 2. A process as claimed in claim 1 wherein the dimensions of the chamber are such that : a desired degree of heating and treatment is achieved; and the mean temperature of the heated and treated particles leaving the chamber is such that agglomeration of particles and sticking to internal surfaces of subsequent apparatus is reduced to an acceptable degree. 3. A process as claimed in claim 2 wherein the chamber is elongated in the direction of the bulk flow. . A process as claimed in claim 3 wherein the high temperature gas is introduced through an inlet orifice or orifices located close to one end of the elongated chamber. A process as claimed in claim 4 wherein the inlet orifice or orifices is/are located in the region of the longitudinal axis of the chamber. A process as claimed in claim 4 or claim 5 wherein the cross-sectional area of the chamber is substantially greater than the corresponding cross-sectional area of the inlet orifice or orifices whereby direct contact of the off-gases with the walls of the chamber is minimised. 7. A process as claimed in any one of claims 4 to 6 wherein the port or ports are positioned in close proximity to the inlet orifice or orifices. A process as claimed in claim 7 wherein the orientation of the port or ports is to some extent radial to the circumference of the chamber, that is, towards the longitudinal axis of the chamber, whereby the flow pattern of the oxide particles is substantially along that axis in order to minimise contact of the particles with the walls of the chamber. 9. A process as claimed in claim 7 wherein the orientation of the port or ports is to some extent tangential to the circumference of the chamber, that is, partly towards the longitudinal axis of the chamber, whereby a degree of bulk rotation of gas and particulate material is set up within the chamber. 10. A process as claimed in claim 8 or claim 9 wherein a degree of swirl is imparted to gas entraining the particulate material by suitable shaping and/or orientation of the port or ports . 11. A process as claimed in any one of the preceding claims wherein the treated particles are further treated in part or in whole by recycling to the chamber. 12. A . process as claimed in any one of the preceding claims wherein carbonate material such as limestone is calcined at least in part. 13. A process as claimed in claim 1 substantially as described with reference to the accompanying drawings . 14. A chamber for the heating and treatment of solid particulate materials, which comprise: 1. a vessel adapted to confine and direct a flow of particulate material and high temperature gas; 2 an inlet orifice or orifices for hot gases; 3. an inlet port or ports for particulate material entrained in carrier gas; 4. an exit port for the treated particulate material, the inlet orifice(s) and the inlet port(s) being so arranged that the particulate material is initially exposed to heating conditions and subsequently cooled to control agglomeration and sticking. 15. A treatment chamber as claimed in claim 14 substantially as described with reference to the accompanying drawings. 16. An apparatus for the production of material in a molten bath reactor, which comprises in combination: 1. a molten bath reactor; 2. means to pass off-gas from the reactor; 3. a chamber or chambers as defined in claims 14 or 15; 4. means to inject fresh particulate material, or particulate material which has been heated and treated, to the chamber or chambers; 5. means to pass the solids entrained in gas from the chamber or chambers to a gas-solid separator or separators, and 6. means to pass at least a proportion of the separated solids and some entraining gas to the reactor, and, if desired, a proportion to the chamber or chambers. 17. An apparatus as claimed in claim 16 substantially as described with reference to the accompanying drawings.

Inventors: BATTERHAM ROBIN JOHN, GRANT RODERICK MACPHERSON, HAPP JAMES VINCENT, THIELE GLENN ASHLEY, BATTERHAM, ROBIN, JOHN, GRANT, RODERICK, MACPHERSON, HAPP, JAMES, VINCENT, THIELE, GLENN, ASHLEY
Applicants: CRA SERVICES, CRA SERVICES LIMITED
Application year: 1990
Main classification: C04B7
IPC codes: B01J8, C04B5, C04B7