Method of planarization of topologies in integrated circuit structures

Abstract: A method is disclosed for making a highly planar­ ized integrated circuit structure having deposited oxide portions planarized to the level of adjacent portions of the integrated circuit structure which comprises: depositing, over an integrated circuit structure having first portions at a height higher than the remainder of the integrated circuit struc­ ture, a conformal oxide layer having a thickness which exceeds the height of said first portions above the remainder of the integrated circuit structure; forming a patterned mask layer over said deposited oxide layer with one or more openings therein in registry with the higher height first portions of the integrated circuit structure; etch­ ing exposed portions of said conformal oxide layer through the mask openings down to a level approxi­ mately equal to the level of the unexposed portion of the conformal oxide layer; removing the mask layer; and polishing the oxide layer to remove raised portions of the conformal oxide layer re­ gaining after the etching step to form a highly planarized structure. Optionally, the oxide layer may be further etched anisotropically until the upper surfaces of the underlying integrated circuit structure is exposed.

Description: This invention relates to the planarizing of integrated circuit structures. More particularly, this invention relates to an improved method for forming highly planarized oxide portions in integrated circuit structures. In the conventional construction of integrated circuit structures, field oxide, for example, is usually grown on and into the surface of the silicon substrate to provide oxide insulation between adjacent active devices by masking the active device regions of the substrate and then oxidizing the remaining portions of the substrate. In the formation of such oxide regions by oxidation of the silicon substrate, that is, by oxide growth rather than by deposition, the oxide grows down into the substrate as well as extending upwardly from the surface. For example, when growing an oxide layer of about one micron thickness, the oxide growth will extend down into the substrate about half the distance, that is, extend down about 0.5 micron below the original silicon substrate surface and also extend about 0.5 micron above the original silicon substrate surface, due to the fact that a given number of silicon atoms in crystalline silicon occupies less volume than the oxide of the same number of silicon atoms. While this phenomena changes the vertical topology of the integrated circuit structure somewhat, the greater problem is that this expansion of the oxide volume also occurs laterally as well as vertically. Thus, as shown in the prior art structure shown in Figure 1, the field oxide grown in the unmasked regions of the substrate also extends partially into the masked regions of the substrate with both the downwardly and upwardly extent of the oxide tapering off the further the oxide extends laterally, thus forming what is known in the industry as a "bird's beak". This "bird's beak" region then narrows the active region of the substrate in between the field oxide portions in which active devices can be constructed, as shown in Figure 1, down to a width x with the width of the mask minus x representing the area of lateral encroachment of the grown oxide. To remedy this, the dimensions of the mask must be altered to accommodate this encroachment, i.e., the openings for the field oxide must be made smaller. This, in turn, becomes a problem as the density of integrated circuit structures increase with VLSI. When the lines and spaces, for example, become less than one micron, problems of lithography occur. Furthermore, there may be yet further encroachment if the field implant, i.e., the doping beneath the field oxide, laterally migrates with the field oxide as it grows, thus reducing the active device region still further. The problems associated with "growing" field oxide regions in an integrated circuit structure has been recognized and attempts have been made to remedy these problems. For example, Chen et al, in an article entitled "A FULLY RECESSED FIELD ISOLATION TECHNOLOGY USING PHOTO-CVD OXIDE", published in IDEM 82 at pp. 233-236, discuss the use of a photoresist layer to etch a groove which is then filled with a photox-CVD oxide (photox) before removing the photoresist mask. Excess "photox" is then removed with the photoresist by liftoff. Shibata et al, in an article entitled "A SIMPLIFIED BOX (BURIED-OXIDE) ISOLATION TECHNOLOGY FOR MEGABIT DYNAMIC MEMORIES", published in IDEM 83 at pp 27-30, discuss forming isolation oxide by refilling anisotropically etched recesses in silicon substrates with deposited oxide. The original BOX process used two steps, a plasma SiO 2 lift-off in the first step and redeposition of CVD SiO 2 followed by planarization etch-back in the second step. The authors noted that this procedure works satisfactorily for recesses narrow in width, but fails to leave field oxide in wide open areas. The authors suggest using two resist layers with the first resist providing a mask over the oxide in the wide open areas and the second resist layer apparently acting as a planarizing layer. In EP-A-0 341 898, there is described and claimed a more satisfactory way to form highly planarized field oxide regions between active regions in the substrate while eliminating the formation of the "bird's beak" encroachment experienced with prior art field oxide growth. The method described and claimed in that application utilized a mechanically polishable planarization layer, such as a polysilicon layer, which is applied over an oxide layer and then polished down to the highest level of the oxide. The exposed oxide is then etched down to a predetermined level above the underlying integrated circuit structure after which the remaining polysilicon is removed by a further polishing step. The oxide may then be etched down to the level of the highest portions of the underlying integrated circuit structure. The result is a highly planarized field oxide type separation between active regions, such as, for example, either active devices formed in the substrate or between stepped regions in an integrated circuit structure such as those which occur when conductive lines are formed over the substrate, whereby the topology of the resulting structure will minimize formations of such steps or other nonplanar structures, i.e., will result in a highly planarized integrated circuit structure. While this method has been found to provide highly planarized structures in most instances, the use of a polishing step to planarize the polysilicon layer can result in problems when the underlying oxide portions are very wide, i.e., over 200 microns in width, because the polishing means are usually insufficiently flat to prevent some of the oxide under the polysilicon from being exposed in such wide areas. DE 3625742 describes (Figs. 3a-3g) a process for the manufacture of an integrated CMOS circuit comprising the steps of depositing a conformal oxide layer over an integrated structure; applying a patterned mask layer over the oxide layer with openings located above raised portions of the oxide layer; applying a planarizing layer and then etching the entire structure down to the low portions of the oxide layer to planarize the structure. It also describes a similar process (Figs. 4a & 4b) in which the last two steps are replaced by the steps of: selectively etching the raised portions of the oxide layer through the mask openings; removing the mask leaving an oxide layer having raised oxide portions; removing said raised oxide portions by applying a planarizing layer and etching the entire structure down to the low portions of the oxide layer. IBM Technical Disclosure Bulletin Vol. 27, No. 8, January 1985 pages 4700 to 4701 and JP 59-136943 discloses the polishing of an insulating layer deposited on semiconductor substrates and in trenches formed in those substrates to obtain a planarized insulating layer. EP 300569 discloses a method of manufacturing a planarized semiconductor insulated circuit involving the use of lithography. Summary of the Invention The present invention provides a method of making an integrated circuit having a planarized oxide surface having the steps defined in accompanying claim 1. The method provides a highly planarized field oxide for an integrated circuit structure which is deposited in shallow openings provided in the underlying silicon substrate between active regions in said substrate by first forming such shallow openings in the substrate; depositing a layer of oxide which is thicker than the depth of the shallow openings to form a conformal layer of oxide over the structure, forming a mask layer over the deposited oxide layer having openings corresponding to the raised portions of the underlying conformal oxide layer, etching the exposed oxide through the mask layer down to a level approximately equal to the height of the lowest portion of the unexposed area of the oxide layer, removing the mask layer to exposed the remaining portions of the oxide layer, mechanically polishing the oxide layer to remove any remaining raised portions of the oxide layer, and then optionally etching the remaining oxide layer down to the level of the top surface of the active regions of the substrate to thereby form a highly planarized structure comprising oxide portions in the substrate which are level with the substrate level in the active region of the substrate. The method of the invention provides a highly planarized integrated circuit structure comprising a raised or stepped pattern interleaved with oxide portions formed by depositing an oxide layer over an integrated circuit structure containing such a raised pattern, the oxide layer deposited to a thickness greater than the thickness of the raised pattern, to form a conformal layer of oxide over the structure, forming a mask layer over the deposited oxide layer with openings conforming to the raised or stepped pattern beneath the conformal oxide layer, etching the exposed oxide down to a level approximately equal to the height of the lowest portion of the unexposed area of the oxide layer, removing the mask layer to expose the unetched portions of the oxide layer, and then mechanically polishing the oxide layer to remove any remaining raised portions of the oxide layer to result in a highly planarized top surface. Optionally the remaining oxide layer may be etched down to the level of the top surface of the raised pattern to thereby form a highly planarized structure with oxide in the spaces between the exposed raised pattern. Further features and advantages of the invention will be apparent from the following description and accompanying drawings. Brief Description of the Drawings Figure 1 is a fragmentary vertical cross-section of a prior art structure showing the formation of a "bird's beak" by growth of field oxide regions in a silicon substrate which encroach into the active device region of the substrate. Figure 2 is a fragmentary vertical cross-section showing an early stage of a first embodiment of the invention wherein a silicon substrate has been masked to cover active regions of the substrate and openings have been etched in the silicon substrate through the mask openings. Figure 2A is a fragmentary vertical cross-section of an alternate step in the process to produce the structure of Figure 2 showing an optional field implant before forming the openings for the field oxide. Figure 2B is a fragmentary vertical cross-section of an alternate embodiment of the structure of Figure 2 showing a tapered sidewall opening which facilitates the illustrated use of a field implant after forming openings for the field oxide. Figure 2C is a fragmentary vertical cross-section of yet another embodiment wherein the doping of the vertical sidewalls of n-channel regions to form channel stops is accomplished by initially conformally depositing a thin film of doped glass and subsequently diffusing dopant into the vertical sidewalls. Figure 3 is a fragmentary vertical cross-section showing the structure shown in Figure 2 at a later stage of the process with at least the top layer of the mask removed and a conformal oxide layer deposited over the substrate and in the etched away openings in the substrate. Figure 4 is an enlarged fragmentary vertical cross-section of a portion of the structure of Figure 3 showing the difference between the depth X 1 of the etched area and the minimum thickness X 2 of the conformal oxide layer deposited over the structure, with X 3 representing an intermediate level between X 1 and X 2 . Figure 5 is a fragmentary vertical cross-section of the structure of Figure 3 after a mask layer has been formed over the conformal oxide layer. Figure 6 is a fragmentary vertical cross-section showing the structure of Figure 5 after etching of exposed portions of the conformal oxide layer through the mask layer down to a level approximately even with the level of the unexposed portions of the conformal oxide layer (level X 2 in Figure 4). Figure 7 is a fragmentary vertical cross-section showing the structure of Figure 6 after removal of the mask layer. Figure 8 is a fragmentary vertical cross-section showing the structure of Figure 7 after a chemical/mechanical polishing step to remove any remaining raised portions of the conformal oxide layer leaving a highly planarized structure. Figure 9 is a fragmentary vertical cross-section showing the planarized structure of Figure 8 after performing an optional final etching step of this embodiment with further conformal oxide removed by a second etch until the top surface of the active regions of the integrated circuit structure are exposed. Figure 10 is a fragmentary vertical cross-section of another embodiment of the invention wherein a raised pattern is formed over an integrated circuit structure. Figure 11 is a fragmentary vertical cross-section showing the structure of Figure 10 with a conformal layer of oxide deposited over the raised pattern. Figure 12 is a fragmentary vertical cross-section showing a further step of this embodiment with a mask layer formed over the conformal layer shown in Figure 11. Figure 13 is a fragmentary vertical cross-section showing etching of the exposed portions of the conformal oxide layer through the mask down to the level of the unexposed portions of the conformal oxide layer. Figure 14 is a fragmentary vertical cross-section showing the structure of Figure 13 after removal of the mask layer. Figure 15 is a fragmentary vertical cross-section showing the structure of Figure 14 after a chemical/mechanical polishing step to remove any remaining raised portions of the conformal oxide layer leaving a highly planarized structure. Figure 16 is a fragmentary vertical cross-section showing a further, but optional, etching step performed on the planarized structure of Figure 15 to remove sufficient additional conformal oxide to expose the top surface of the raised pattern thereunder. Detailed Description of the Invention The invention provides an improved method for forming highly planarized topologies in integrated circuit structures wherein oxide is used between active or conductive regions formed in or on an integrated circuit structure. In the illustrated embodiments, the process of the invention is shown, by way of illustration and not of limitation, as applied either to the formation of a highly planarized integrated circuit structure having field oxide deposited between active regions in a silicon substrate; or in forming a highly planarized structure with a raised pattern such as, but not limited to, metal lines formed over an integrated circuit structure previously formed in and on a substrate, with oxide upon and/or between the raised pattern. Referring now to Figure 2, a silicon substrate 2 is shown with a photoresist mask 10 thereon over active regions to be formed in the substrate and having openings 14 in mask 10 conforming to desired field oxide regions to be formed in silicon substrate 2. As shown in Figure 2, openings or slots 8a, 8b, and 8c have already been etched in silicon substrate 2 through mask openings 14 to a depth of, for example, from about 0.45 to about 0.55 microns. Before forming mask 10 over substrate 2, an oxide layer 4 may be grown on the surface of substrate 2 to a thickness of, for example, 3-5.10 -8 m (300-500 Angstroms), as shown in Figure 2, followed by deposition of about 1-2.10 -7 m (1000 to about 2000 Angstroms), preferably about 1,3-1,5.10 -7 m (1300 to about 1500 Angstroms), of silicon nitride 6 which may form an optional etch block for a subsequent etching step as will be described below. Since oxide layer 4 is used merely as an underlying layer for the optional nitride etch block layer, elimination of nitride layer 6 can also result in elimination of oxide layer 4 as well, if desired. Alternatively, if desired, oxide layer 4 may be used beneath resist mask 10 even when nitride layer 6 is omitted. Openings 8a-8c are etched in silicon substrate 2, in one embodiment, as shown in Figure 2, by an anisotropic etch, such as a reactive ion etch (RIE) process, to form substantially orthogonal sidewalls, that is, sidewalls normal to both the plane of the substrate surface prior to the etch and normal to the bottom of openings 8a-8c. In a variation of this embodiment, where it is desired to perform a field implant beneath the field oxide region to be formed in openings 8a, 8b, and/or 8c etched in substrate 2, for example, when forming an n-channel device where undesirable inversion in the substrate can occur, the substrate may be implanted prior to forming the field oxide, as shown in Figures 2A and 2B. As shown in Figure 2A, a first implantation and diffusion doping of substrate 2 may be carried out prior to any etching step through openings 14 in mask 10. By conducting this doping step prior to the etching step, some of the dopant will laterally scatter and diffuse into the edge of the adjacent active device region of the substrate as shown at 20, representing a crucial area where voltage inversion should be avoided. This doping step, for example, may be carried out by implanting boron followed by diffusion at between about 800 and 900°C for at least 15 minutes to result in a final boron concentration high enough to prevent field inversion, typically 10 16 cm -3 . Alternatively, as shown in Figure 2B, after the etching of opening 8' (which may be carried out to the same depth as openings 8a-8c), a second doping step may be carried out to dope the newly exposed substrate surfaces over or against which the field oxide will be deposited. As shown in Figure 2B, advantageously sidewall 9 of substrate opening 8' will be formed with a slope by adjusting the anisotropic etch slightly to form sidewalls with an inward slope of about 3-5 degrees to facilitate the subsequent doping of sidewalls 9 of opening 8'. The bottom and sidewalls of substrate 2 exposed by opening 8' may then be doped with boron to a concentration sufficient to prevent field inversion, typically 10 16 cm -3 . In yet another embodiment, as shown in Figure 2C, the sidewalls and bottom walls of opening 8", which may represent any or all of the openings 8a-8c, may be doped subsequent to formation of the opening, even with a vertical sidewall, by depositing a thin layer of doped glass 12 such as a borosilicate glass into the opening and then allowing the dopant in the glass to diffuse into the sidewalls and bottom of the opening. The doped glass is then removed from opening 8" prior to further processing to planarize the structure. It should be noted that since it is only desired to form channel blocks in the substrate adjacent the n-channel, other areas of the substrate, including p-channel areas, would be masked by thermally grown silicon dioxide during such doped glass deposition and subsequent removal steps. However, a phosphorus glass may also be employed to block the p channel areas by a similar method. After forming openings 8a-8c (or 8' or 8"), photoresist mask layer 10 is removed and, as shown in Figure 3, a conformal layer of oxide 30 is deposited over the entire structure to a thickness sufficiently in excess of the depth of openings 8a-8c so that the level of oxide in the lowest point in the widest opening 8b is above the highest point in the adjoining active regions of the substrate, including any etch stop layers, such as oxide 4 or nitride 6, which may still be optionally present thereon, as shown in Figure 2. It will be noted that the height of oxide layer 30 over wide opening 8b is not as high as over narrower etched openings 8a and 8c. As previously discussed with respect to the prior art, when wide openings are etched and then filled with oxide to form a field oxide region, oxide layer 30 tends to conform to the underlying topography. Since the eventual structure, in accordance with the invention, will be highly planarized, it is important to the practice of the present invention that the thickness of oxide layer 30 over wide opening 8b exceed the depth of opening 8b from the unetched surface of the substrate. This is illustrated in the enlarged region of Figure 3 shown in Figure 4 wherein the depth of etched opening 8b from the surface is represented by X 1 while the thickness of oxide layer 30 over opening 8b is represented by X 2 . In accordance with the invention, the thickness of oxide layer 30 over wide opening 8b (X 2 ) must be greater than the depth X 1 of opening 8b. The difference between X 1 and X 2 is preferably from about a minimum of about 0.15 microns up to about 0.45 microns. Greater thicknesses of oxide may be used, if desired, but are unnecessary. Thus, for example, when the depth of opening 8b is about 0.5 microns, the thickness of oxide layer 30 over opening 8b will range from about 0.65 up to 0.95 microns. Preferably, the deposited oxide is a highly conformal oxide, such as, for example, tetraethyl orthosilicate (TEOS), which is deposited at a temperature of from about 700 to about 750°C. Alternatively, the deposited oxide may comprise a low pressure chemical vapor deposition (CVD) oxide layer deposited at a temperature of from about 350 to about 450°C. As shown in Figure 5, a second mask layer generally indicated at 50, comprising mask portions 52-56, and openings 58 which are in registry with the portions of substrate 2 in between openings 8a-8c, is then formed over conformal oxide layer 30. Mask layer 50 preferably comprises a photoresist mask, but may comprise any material compatible with the underlying conformal oxide layer and capable of withstanding a subsequent oxide etch. By way of illustration and not of limitation, masking layer 50 will be described hereinafter as a photoresist mask. Photoresist mask layer 50 may be patterned using a photolithography mask which is the reverse of the mask used to pattern photoresist layer 10. Alternatively, the same photolithography mask could be used with photoresist layer 50 of opposite sensitivity to that of photoresist layer 10, e.g., positive photoresist used for layer 10 and negative photoresist used for layer 50, or by using an image reversal photolithography technique. In accordance with the invention, as shown in Figure 6, the exposed portions of conformal oxide layer 30 are now etched down to the level of the unexposed portions of oxide layer 30, i.e., down to about the level X 2 , preferably using a wet etch such as, for example, a buffered oxide etch comprising an aqueous solution of 40 parts ammonium fluoride (NH 4 F) and 1 part hydrofluoric acid (HF). A dry etchant system, such as, for example, a reactive ion etch (RIE), using CHF 3 chemistry with the oxygen level adjusted to favor oxide removal, could also be used to etch conformal oxide layer 30. However, an isotropic type etch such as a wet etch which will undercut photoresist mask portions 52-56, as shown at 34 and 36 in Figure 6, is preferred since there will be less oxide remaining in the raised portions adjacent the edges of the photoresist mask, which will, in turn, simplify subsequent removal of such raised portions as will be described below. It will be noted, in this regard, that this undercutting by the isotropic etching will, in some cases, completely undercut the photoresist mask, as shown at 36 in Figure 6, where mask portion 56 has been completely undercut. Since the next step is removal of mask 50, such complete undercutting of portions of mask 50 is not harmful. After completion of the etching step, photoresist mask 50 is removed, for example, using a hot solution of concentrated (18 molar) sulfuric acid and hydrogen peroxide, leaving the structure shown in Figure 7 with remaining conformal oxide layer 30' shown with raised portions 30a-30d remaining from the etching step. The structure is now polished using either a mechanical polishing means or, preferably, a chemical/mechanical polishing means, to remove raised oxide portions 30a-30d remaining on the surface of the remaining portion 30' of conformal oxide layer 30. The abrasive means used in the polishing step may comprise a purely mechanical polish using, for example, as a polishing material an aqueous slurry of finely divided Al 2 O 3 or SiO 2 particles, with the pH adjusted to about 7, spread on a flat polymeric disk. Alternatively, for a chemical/mechanical polish, the polishing material may also include a minor amount of a hydroxide such as KOH or NaOH added in a sufficient amount to increase the pH to about 9-11, or, preferably, the polishing material may include HCl to adjust the pH to about 2 to provide the desired chemical/mechanical polish. This polishing step is carried out until the high oxide portions 30a-30d of underlying conformal oxide layer 30' are removed, leaving a highly planarized surface 30", as shown in Figure 8 which may be about the level X 3 shown in Figure 4, i.e., slightly below the original level X 2 representing the lowest original height of conformal oxide layer 30, but above the underlying integrated circuit structure. Since the result of this polishing step, as shown in Figure 8, is a highly planarized conformal oxide layer 30", it may be desirable to end the planarizing portion of the process at this point, for example, if further processing of the underlying silicon structure is not necessary or desired. In such cases, for example, vias may be cut through planarized oxide layer 30" to provide contact to appropriate portions of the underlying silicon substrate where desired. If the planarizing portion of the process is to be terminated at this stage, it should be pointed out that nitride layer 6 would preferably be removed at an earlier stage of the process prior to deposition of conformal oxide layer 30. Alternatively, oxide layer 30" may be further etched to expose the adjoining active regions of the substrate, leaving oxide portions 30e-30g remaining in between the exposed portions of substrate 2, as shown in Figure 9. In such instance, the presence of nitride mask portions 6 may be desirable to provide a convenient etch stop to prevent inadvertent etching of silicon substrate 2. This etch step is preferably an anisotropic etch carried out using the RIE etching method described previously, although wet etching may be used if one can control the selectively of wet etching to etch the seams formed during the initial oxide deposition. Whether the planarizing process is completed with the structure shown in Figure 8 or with the structure shown in Figure 9, preferably the remaining oxide is then densified, by heating the structure to a temperature of about 800-900°C, preferably about 900°C, in an oxidizing atmosphere for about 30 minutes. Turning now to Figures 10-16, another embodiment of the process of the invention is shown commencing with Figure 10 wherein an integrated circuit structure 60, which may include previously formed active devices in or on the surface of a substrate, such as a silicon substrate, is shown provided with a raised pattern 70 over the substrate surface. Patterned layer 70 might, for example, comprise a 3-10.10 -7 m (3000 to 10,000 Angstrom) layer of a conductor, e.g., metal patterned to form metal lines or interconnects. When layer 70 comprises a conductor, it may comprise any conductor conventionally used in forming integrated circuit structures, such as, for example, aluminum, polysilicon, or tungsten, capable of withstanding the temperatures subsequently used in depositing the conformal and planarizing layers thereon. Raised pattern 70 might also comprise the combination of a raised pattern of conductors and an insulating layer formed over the conductors, or it might only comprise an insulating material. Patterned layer 70, however, will be described below, by way of illustration, and not of limitation, as a metal pattern. As shown in Figure 11, a conformal layer of oxide 80 is deposited over structure 60 and metal pattern 70 to a thickness which, in the widest area between metal lines, will again be a thickness X 2 , as in the first embodiment, which is greater than X 1 , the thickness of the metal pattern 70. Usually, the thickness X 2 will be greater than the thickness X 1 by about 0.2 microns up to about 1.2 microns. The thickness of conformal oxide layer may vary, for example, from about 7-15 10 -7 m (7000 to about 15,000 Angstroms). Conformal oxide layer 80 may comprise an oxide material such as the previously described TeOS oxide, which may be used over materials which can withstand temperatures above 700°C, up to 750°C. It should be noted here, that if a lower melting metal such as aluminum is used for metal pattern 70, then a lower deposition temperature TeOS oxide, e.g., one deposited at about 350°C, such as plasma TeOS, may be substituted for the previously described conformal oxide, or a lower temperature CVD oxide (e.g., deposited at about 350°C) may be used. As in the first embodiment, a layer of masking material 90 such as, for example, a photoresist mask is now formed over the structure as shown in Figure 12 with openings 100 provided between mask portions 92-98. Mask openings 100 are formed in registry with the raised pattern portions 70 beneath conformal oxide layer 80. In accordance with the invention, as shown in Figure 13, the exposed portions of conformal oxide layer 80 are now etched down to the level of the unexposed portions of oxide layer 80, as described in the previous embodiment, again preferably using an isotropic wet etch such as the previously described buffered oxide etch solution to not only remove the exposed portions of oxide 80 but to undercut mask portions 92-98, as shown at 84. After completion of the etching step, photoresist mask 90 is removed, as in the previous embodiment, leaving the structure shown in Figure 14 with remaining conformal oxide layer 80' shown with raised portions 80a-80f resulting from the etching step. The structure is now polished using either a mechanical polishing means or, preferably, a chemical/ mechanical polishing means, as described with respect to the previous embodiment, to remove raised oxide portions 80a-80f remaining on the surface of the remaining portion 80' of original conformal oxide layer 80, resulting in the planarized structure of Figure 15. As previously discussed with respect to the embodiment shown in Figure 8, the planarizing portion of the process may be stopped here and the remaining conformal oxide layer 80" may be densified as previously described, or the structure may be further etched, preferably using the anisotropic dry etching previously described, to produce the structure shown in Figure 16 in which the top of the raised pattern portions 70 are exposed, leaving planarized oxide portions 80g-80j therebetween. Thus, the invention provides an improved method for forming highly planarized topology in integrated circuit structures which may be used in forming highly planarized oxide regions adjacent active device regions in a substrate or a highly planarized structure of a raised pattern such as metal lines interleaved with oxide by utilizing a conformal oxide layer which is selectively etched through openings in a mask thereon in registry with the raised portions of the underlying structure and then, after removal of the mask, polished to remove any remaining raised portions of the conformal oxide, leaving a highly planarized surface.

Claims: A method of making an integrated circuit having a planarized oxide surface over an integrated circuit structure which has structure portions (-;70) which are raised above the remainder of the structure, the method not utilizing a planarizing layer of polysilicon and comprising the steps of: a. providing an integrated circuit structure having a pattern of raised portions (-;70) having a height (X 1 ) above the remainder of the integrated circuit structure; b. depositing a conformal oxide layer (30;80) over the whole said integrated circuit structure, said conformal oxide layer (30;80) having a thickness (X 2 ) which exceeds said height (X 1 ) of said raised portions; c. applying a patterned mask layer (50;90) over said oxide layer (30;80) with openings (58;100) in registry with portions of said oxide layer by said structure portions; d. etching said raised oxide portions through the openings (58;100) in the mask; e. removing said mask layer (50;90) leaving said structure with a remaining conformal oxide layer (30';80') having raised oxide portions (30a-30d; 80a-80f) remaining from etch step d; f. removing said remaining raised oxide portions (30a-30d; 80a-80f) to obtain a highly planarized oxide layer (30';80') characterized in that said raised oxide portions (30a-30d; 80a-80f) which are etched in step d are etched down to approximately the same height as the masked portions of said oxide layer (30; 80) and in that said removing step f is carried out by mechanical or chemical/mechanical polishing without using a planarizing layer over said remaining raised oxide portions (30a-30d; 80a-80f) leaving said planarized oxide layer (30";80") covering the whole said integrated circuit. A method as claimed in claim 1, wherein said step (b) of depositing said conformal oxide layer (30;80) is carried out at a temperature of from about 700 to about 750°C. A method as claimed in claim 1 or claim 2, wherein said step (b) of depositing said conformal oxide layer comprises depositing from about 7000 x 10 -10 m (7,000 Angstroms) to about 15,000 x 10 -10 m (15,000 Angstroms) of conformal oxide over said integrated circuit structure. A method as claimed in claim 2 or claim 3, wherein said step (c) of applying said mask layer (50;90) comprises depositing a patterned layer of photoresist over said conformal oxide layer (30;80). A method as claimed in claim 4, wherein said step (d) of etching said conformal oxide layer (30;80) comprises isotropically etching said conformal oxide layer (30;80) to undercut adjacent portions of said mask layer (50;90) thereon. A method as claimed in claim 5, wherein said step of isotropically etching said conformal oxide layer comprises wet etching said conformal oxide layer (30,80). A method as claimed in any preceding claim, including the further step of etching said polished conformal oxide layer (30";80") until portions of said underlying integrated circuit structure are exposed. A method as claimed in claim 7, wherein said step of etching said polished conformal oxide layer (30";80") comprises an anisotropic etching of said conformal oxide layer. A method as claimed in claim 8, including the step of forming a nitride mask (6) over said raised portions of said integrated circuit structure, whereby said nitride mask (6) will act as an etch stop for said anisotropic etching of said polished conformal oxide layer (30";80") to prevent etching of the underlying integrated circuit structure. A method as claimed in claim 9, including the further step of removing said nitride mask (6) after said step of anisotropically etching said polished conformal oxide layer (30";80"). A method as claimed in claim 1, wherein said step (a) of providing an integrated circuit structure includes the steps of: (g) masking active regions of an integrated circuit structure; (h) etching the exposed portions of said integrated circuit structure through said mask to form one or more openings (8a,8b,8c) having a depth of from about 0.45 to about 0.55 microns, and (i) removing the mask; said subsequent step (b) of depositing a conformal oxide layer (30) comprises depositing said conformal oxide in said etched openings (8a,8b,8c) and over said unetched active regions of said integrated circuit structure to a thickness which exceeds the depth of said etched openings, and wherein said subsequent planarization steps form a planarized integrated circuit structure having field oxide regions (30e,30f,30g) therein with the top surface of said field oxide regions at the same level as the top surfaces of said active regions. A method as claimed in claim 11, including the further step (k) of forming an oxide layer (4) over said integrated circuit structure and forming a nitride layer (6) over said oxide layer (4) prior to said step (g) of masking said active regions of said substrate; and said step (h) of etching said integrated circuit structure through said mask further includes etching said nitride and oxide layers formed beneath said mask. A method as claimed in claim 11, wherein said integrated circuit structure has field oxide regions (8a,8b,8c), formed therein between active regions of a substrate (2), and at the same level as the active regions, said step (a) of providing an integrated circuit structure including the steps of: (g) patterning a silicon substrate with a preliminary photoresist mask (10) having openings therein conforming to desired formation of field oxide regions in said substrate between said active regions; (h) etching said silicon substrate through said photoresist mask to form openings (8a,8b,8c) in said substrate having a depth of from about 0.45 microns to about 0.55 microns; and (i) removing said first photoresist mask, and wherein in that said step (b) of depositing said conformal oxide layer (30) comprises depositing from about 7000 x 10 -10 m (7,000 Angstroms) to about 9000 x 10 -10 m (9,000 Angsroms) of said conformal oxide layer over said substrate; said step (c) of applying said patterned mask (50) is arranged so that said mask (50) has openings (58) therein in registry with the portions of said substrate between said openings (8a,8b,8c) etched in said substrate; said step (d) of etching said raised oxide portions comprises isotropically etching said conformal oxide layer (30) through said mask (50) to a level substantially equal to the level of the masked portions of said conformal oxide layer; and said removing step (f) comprises polishing said conformal oxide layer (30) to remove said remaining raised oxide portions (30a-30d) of said conformal oxide layer; and further including the step (j) of anisotropically etching said conformal oxide layer (30) to expose said active regions of said substrate to form a highly planarized structure having field oxide regions (30e,30f,30g) therein between said active regions in said substrate with the upper surface of said field oxide regions substantially level with the surface of said active regions. A method as claimed in claim 13, including the further step (k) of forming a nitride layer (6) on said substrate prior to patterning said substrate with said initial photoresist mask; said step (g) of patterning said substrate further includes patterning said nitride layer; and said patterned nitride layer functions as an etch block during said anisotropic etching step (k) to protect said substrate from said anisotropic etch. A method as claimed in claim 1, wherein said step (a) of providing an integrated circuit structure includes the step of forming a raised pattern (70) over an integrated circuit substrate (60), and wherein said step (b) of depositing said conformal oxide layer (80) comprises depositing said conformal oxide to a depth which exceeds the height of said raised pattern (70) above said integrated circuit structure. A method as claimed in claim 15, wherein said step of forming a raised pattern (70) comprises forming a pattern of conductive material capable of withstanding the temperatures used in said step of depositing said conformal oxide layer (80). A method as claimed in claim 14 or claim 15, including the further step of (j) etching said polished conformal oxide layer (80") until said raised pattern (70) is exposed with the top surface of said conformal oxide portions between said raised pattern at the same level as the top surfaces of said raised pattern.

Inventors: AVANZINO STEVEN C, GUPTA SUBHASH, HASKELL JACOB D, AVANZINO, STEVEN C., GUPTA, SUBHASH, HASKELL, JACOB D.
Applicants: ADVANCED MICRO DEVICES INC, ADVANCED MICRO DEVICES, INC.
Application year: 1990
Main classification: H01L21
IPC codes: H01L21