Microwave ceramic magnetic material manufacturing process

Abstract: Chemical process for the manufacturing of ceramic materials for microwave applications based on citrate synthesis by pyrolysis. The process belongs to the field of microwave devices ceramic materials and it a preferred application is that of electronics in general and radars in particular. This process yields ultra-fine powders through the following: - mixing of oxides and/or carbonates; - dilution of these in citric acid; - obtaining of metal-organic precipitates; - addition of citric acid and thereafter of ammonium hydroxide. By heating this solution up to a pre-established temperature, self ignition takes place caused by the ammonium nitrate. Thus the new ceramic-magnetic material is obtained in the form of a homogeneous ultra-fine powder.

Description: The present invention relates to a process for the production of ceramic materials in ultra-fine powder form by synthesis of the respective citrates and pyrolysis thereof in the correct stoichiometric relation for use in, for example, microwave applications. Microwave ceramic materials, frequently referred to as ferrites, are widely used in, for example, radar systems. The known methods of producing ferrites based upon ceramic technology is to perform a given number of solid state reactions with suitable oxides and/or carbonates by heating them at a high temperature and thereafter wet or dry grinding the product. Although such prior art methods give satisfactory results, the manufacturing times to achieve a mono-phase powder with high purity are inordinately long. Moreover, the typical particle diameter obtainable from oxides and/or carbonates is about 1µm. FR-A 2 038 681 relates to a process for manufacturing mixed crystals of lanthanide ferrites, comprising the pyrolysis of the mixed citrates of at least one lanthanide element and of at least a further trivalent element. In volume 2 of the handbook "Ferromagnetic Materials", edited by E.P. Wohlfarth (Amsterdam), on page 291 hexagonal ferrites for microwave applications are described, which are prepared by a ceramic technique. The article of Roy, Bhatnagar and Bahadur in the "Journal of Materials Science", vol. 20, no. 1 of January 1985 relates to the magnetic behaviour and microstructural properties of amorphous and crystallized Y 3-x Gd x Fe₅O₁₂ prepared by the amorphous citrate process. It is an object of the present invention to prepare ferrite powders for microwave applications and, more precisely for applications related to circuits employed in electronic equipment. The process greatly facilitates prior art preparation methods and results in substantial reduction of production times. In addition, the electromagnetic characteristics of the resulting material surpass those of the material obtained by traditional techniques. Although the production times are considerably reduced, the magnetic and microwave characteristics are maintained. Accordingly, the present invention provides a method for the manufacture of ultra-fine powders with correct stoichiometric values resulting in better homogeneity and purity and improved forming characteristics during the pressing phase. In the process of the present invention solutions of suitable oxides and/or carbonates in nitric acids are prepared, either individually or together. Preferably, 65 % nitric acid is used. After obtaining the solution of the oxidis and/or carbonates, citric acid is added to further dissolve the mixture and produce the respective citrates. The oxides used as starting materials, in the amount corresponding to the correct stoichiometric balance of the final product, are dissolved following the dry mixing of the oxides by adding nitric acid having a strength of 65 %. The dry carbonates and the oxides may be dissolved by adding nitric acid and then the solutions of the oxides and the carbonates are mixed together and citric acid is added to the solution containing oxides and carbonates as described above. After metal organic compounds and metal precipitates are obtained, ammonium hydroxide having a strength of 25% is added resulting in a disappearance of the reactants and in the solution turning into a deep red colour at a pH value of between about 6.5 and about 7.0. It is important to maintain the pH value within the above-described range. If the pH value exceeds about 7.0, hydroxides and other undesirable salts are generated. The solution of the oxides and carbonates after addition of the citric acid and ammonium hydroxide in the manner described, is heated to a temperature of about 200°C until the reaction mixture turns into a viscous mass which gradually swells due to the presence of the citric acid and then self-ignites to yield ammonium nitrate (NH₄NO₃). The self-combustion resulting from the described heating of the reaction mixture yields in ferrite powders which increase in volume as the reaction proceeds. Particle dimensions obtained in this reaction are between about 50 and about 100nm. During the combustion it is essential that there are no precipitates of any of the citrate compounds, otherwise the desired powder would not be obtained. The salient feature of the present invention is the production of citrates and the pyrolyses thereof to obtain the ceramic magnetic materials for special applications such as, for example, high frequency electronics in which high material purity and homogeneity are required.

Claims: Process for the production of ceramic magnetic material comprising: dissolving metal oxides and metal carbonates in nitric acid; adding citric acid thereto to yield metal organic precipitates; neutralizing the remaining solution by the addition of ammonium hydroxide; heating the neutralized solution to a temperature of about 200° C to cause self-combustion and to yield the ceramic magnetic material. Process according to claim 1, wherein the pH value of the neutralized solution is between about 6,5 and 7,0. Process according to claim 1 or 2, wherein the nitric acid has a strength of about 65%. Process according to anyone of the preceding claims, wherein the ammonium hydroxide has a strength of about 25%. Process according to anyone of the preceding claims, wherein the ceramic material is obtained as ultra-fine powder. Process according to anyone of the preceding claims, wherein the oxides and carbonates are dissolved separately.

Inventors: CATTARIN PAOLO, SPARVIERI NICOLA, CATTARIN, PAOLO, SPARVIERI, NICOLA
Applicants: SELENIA IND ELETTRONICHE, SELENIA INDUSTRIE ELETTRONICHE ASSOCIATE S.P.A.
Application year: 1990
Main classification: C01G49
IPC codes: H01P11, C01G49, C01B13, H01F1