Silyl derivative of 2,6-dialkyl-4-allyl phenol

Abstract: Silyl derivatives of 2,6-dialkyl-4-allyl phenol of the general formula wherein R¹ , R² and R³ are independently selected from linear, branched and cyclic hydrocarbon groups having from 1 to about 8 carbon atoms are provided. R¹ , R² and/or R³ may be connected to form one or more substituted or unsubstituted rings, and R¹ , R² and R³ have a total of up to 24 carbon atoms, and R⁴ is a linear, branched or cyclic hydrocarbon group having 1 to 6 carbon atoms. They may be made by silylating the corresponding hydroxyl compound. They are useful for preparing homopolymers thereof and as comonomers for olefins to introduce functional sites in high molecular weight copolymers.

Description: This invention relates to new silyl derivatives of 2,6-dialkyl-4-allyl phenol of the general formula (I) wherein R¹, R² and R³ are independently selected from linear, branched and cyclic hydrocarbon groups having from 1 to about 8 carbon atoms. R¹, R² and/or R³ may be connected to form one or more substituted or unsubstituted rings, and R¹, R² and R³ have a total of up to 24 carbon atoms, and R⁴ is a linear, branched or cyclic hydrocarbon group having 1 to 6 carbon atoms. In the United States patent application Serial No. 047,960 (see corresponding PCT International Publication No. WO88/08856, November 17, 1988), it is disclosed that comonomers for propylene may be made by protecting the oxygen of a copolymerizable hydroxy-containing compound by substituting the hydrogen thereof with a silyl group having at least some steric bulk, i.e., at least about three carbon atoms in separate groups surrounding it. Silylated monomers of the general formula are suggested in the above-referenced publication. The peculiar advantage, however, of 2,6-dialkyl-4-allyl phenol as a potential comonomer in its silylated form apparently has not been seen in the prior art. The compound 2,6-dimethyl-4-allyl phenol is known. See Tarbell, D. Stanley, and Kincaid, John F. JACS , 62 , 1940, 728-31. Preferred silyl derivatives according to the present invention are those represented by the general formula (II) wherein R¹, R² and R³ are defined as above. Preferred compounds of the invention are (2,6-dimethyl-4-allyl) phenoxy tri-iso-propyl silane, (2,6-dimethyl-4-allyl) phenoxy methyldiphenyl silane, (2,6-dimethyl-4-allyl) phenoxy dimethylethyl silane and (2,6-dimethyl-4-allyl) phenoxy trimethyl silane. They are useful for preparing homopolymers thereof and as comonomers for propylene to insert units having reactive sites into the polymer chain where highly active Ziegler-Natta catalysts may otherwise prevent such insertion. Examples of hetero compounds (such as compounds with heterocyclic substituents involving Si) within the above expression are Further preferred silyl derivatives according to the present invention are those represented by the general formula (III) wherein R¹, R² and R³ are as defined above. Preferred compounds of the invention are (2,6-di-t-butyl-4-allyl) phenoxy tri-iso-propyl silane, (2,6-di-t-butyl-4-allyl) phenoxy methyldiphenyl silane, (2,6-di-t-butyl-4-allyl) phenoxy dimethylethyl silane and (2,6-di-t-butyl-4-allyl) phenoxy trimethyl silane. The compounds are useful for preparing homopolymers thereof and as comonomers for propylene to insert units having reactive sites into the polymer chain where highly active Ziegler-Natta catalysts may otherwise prevent such insertion. The silyl derivatives according to the present invention are prepared by silylating the corresponding 2,6-dialkyl-4-allyl phenol according to standard methods. Following are examples of the preparation of such compounds. All operations were performed under inert atmosphere using standard Schlenk techniques. All liquid reagents and solvents were purged with inert gas prior to their introduction into the reaction system. Example 1: (2,6-dimethyl-4-allyl) phenoxy diphenylmethyl silane 32.700g (0.202 mol) of 2,6-dimethyl-4-allyl phenol were added to a 250 ml flask with an Argon inlet followed by 0.325g (0.014 mol) sodium. After one-half hour of stirring, the sodium had completely reacted and 45.569g (0.188 mol) of diphenylmethyl (ethoxy) silane were added to this mixture. Stirring continued for one hour at which time a reflux condenser was attached and the solution was heated for 4 hours. Vacuum distillation at 1 mm Hg and gas chromatographic mass spectral analysis of the resultant collections indicated that none of the desired product had formed. The first two fractions contained the phenol and these were recombined in a 250 ml Schlenk flask and 0.2g sodium were added followed by 50 ml of tetrahydrofuran (which promoted reaction of the sodium). The solution was homogeneous after 1 hour of stirring and the third fraction (from vacuum distillation), which had been found to contain the silane, was added to the solution. A reflux condenser was attached and the mixture was heated for about 6 hours (variac settings were from 40-70). Some dark precipitate was observed at that time and the heating was discontinued for fear of decomposition. Vacuum distillation of this mixture produced three fractions of which the highest boiling (112-190°C at 1 mm Hg) was found to contain the desired product. The product's identity was confirmed by ¹H NMR and gas chromatography and the yield was 3.5g (5%). Example 2: (2,6-dimethyl-4-allyl)phenoxy dimethylethyl silane 12.888g (0.068 mol) of 2,6-dimethyl-4-allyl phenol were added to a 500 ml flask with an Argon inlet and a cool water bath was applied. 1.56g (0.068 mol) of sodium were cut into small pieces and were added to this cooled solution. This mixture was allowed to slowly warm to room temperature while stirring for four hours. At this time, 30 ml of tetrahydrofuran were added in order to encourage complete reaction of the sodium, and stirring was continued overnight. 8.500g (0.069 mol) of dimethylethyl (chloro) silane were then added dropwise through an additional funnel. The resultant mixture was stirred for 5 hours at which time 250 ml of heptane were added and the precipitate was allowed to settle over the next day. The NaCl was removed by filtration of the colloid through filter paper and then through fritted glass/Celite. The product distilled at 120-122°C (1mm Hg) with a yield of 5g (30%). Example 3: (2,6-dimethyl-4-allyl) phenoxy trimethylsilane 65.5g (0.404 mol) of Argon-saturated 2,6-dimethyl-4-allyl phenol was added to a 250 ml round bottom flask with an Argon inlet. To this flask was added 31.96g (0.404 mol) of pyridine followed by 90 ml of pentane. Both of these materials were previously purged with Argon. 43.89g (0.404 mol) of Argon-saturated chlorotrimethylsilane were then added dropwise to the stirred solution of the phenol over a period of 45 minutes. White precipitate (pyridinium hydrochloride) began to form immediately. The mixture was allowed to stir at room temperature for six hours at which time stirring was discontinued in order to let the precipitate settle out overnight. The supernatant solution was cannula filtered into a clean 500 ml Schlenk flask. The precipitate was washed three times with 40 ml portions of Argon-saturated pentane and these washings were also filtered and added to the bulk solution. The pentane was removed with vacuum (1 mm Hg). The flask was then fitted with a distillation head and the mixture was distilled at 1 mm Hg. The desired product was collected at 83-86°C in 68% yield (65g). The synthesis of 2,6-di-t-butyl-4-allyl phenoxy trimethyl silane can be done essentially according to Example 3 except that as starting materials 71.94g (0.292 mol) of 2,6-di-t-butyl-4-allyl phenol and 31.7g (0.292 mol) of the chlorotrimethylsilane were used, which were reacted in 43.57g (0.292 mol) of Argon-purged diethylaniline. A general procedure for copolymerizing our new compounds with ethylene or propylene follows: Standard inert atmosphere techniques were used to exclude moisture and oxygen throughout the manipulations recited below. A round bottom flask fitted with a sidearm, magnetic stirring bar and a stopper, which apparatus had been assembled hot from a drying oven and was then either evacuated and refilled with inert gas several times or (and) purged with the inert gas for at least 15 minutes, was charged with a given amount of solvent, heptane or toluene, usually 125 ml. The solvents were freshly distilled from sodium and triethyl aluminum (TEA) over which they had been refluxing for at least 18 hours under an inert atmosphere. Immediately after the solvent had been charged to the flask, alkyl aluminum co-catalyst, which was in the form of a heptane solution of about 25 wt% (0.715 g/ml in heptane), was also added to the flask which was then lowered into a thermostated oil bath and magnetic stirring was begun. At this point the inert gas atmosphere in the flask was replaced with the gaseous comonomer by a minimum of 3 cycles of evacuation and refilling back to atmospheric pressure with the comonomer. After the third cycle, the solution was stirred for at least 10 minutes (usually longer) to allow the solvent to become saturated with the comonomer. Pressure was maintained at about one atmosphere via a bubbler. Next were added an "external donor", which usually was diphenyl dimethoxy silane or phenyl triethoxy silane, if one was being used, and the other comonomer. The polymerization was initiated by the addition of the transition metal containing co-catalyst, which was a titanium tetrachloride on a magnesium chloride support. As the gaseous comonomer was consumed it was replaced by maintaining the pressure constant at one atmosphere via a bubbler. After a specified period of time (generally about two hours) the reaction was quenched by the addition of acidified alcohol (HCl in iso-propanol, ethanol, and/or methanol). The quenched reaction slurry was combined with the alcohol solution of volume at least twice the original volume of the inert reaction solvent. The resultant slurry was stirred for at least 45 minutes and then filtered. This treatment not only stopped the reaction, it dissolved catalyst residues and removed the silyl groups and thus regenerated the hydroxyl groups. If the filtration proceeded very slowly, the slurry was combined with enough water to make the filtration proceed at a convenient rate. The polymer was resuspended in alcohol, stirred, filtered and vacuum dried overnight. Boiling heptane soluble content was determined by standard methods. The utility of our new compounds as comonomers for lower olefins is thus demonstrated. Functional substitutes such as dyes may be placed on the regenerated hydroxyl groups in the copolymer chain. Example 4: For the copolymerization of propylene and (2,6-dimethyl-4-allyl) phenoxy diphenylmethyl silane, the following specific procedure was used: A 500ml flask with a sidearm was evacuated and refilled with Argon three times. To this flask was added 75ml of dry, degassed heptane and the solvent was saturated with propylene. 3.23ml of triethylaluminum co-catalyst (0.715 g/ml in heptane) were then added to this solution followed by 3.06ml (0.010 mol) of (2,6-dimethyl-4-allyl) phenoxy diphenylmethyl silane and the flask was placed in an oil bath which had been maintained at 50°C. The polymerization was initiated by the addition of 0.075g of titanium co-catalyst and the mixture was stirred for two hours at which time it was quenched by the addition of approximately 300ml of acidified isopropanol. The alcoholic solution was allowed to stir for 1.5 hours prior to filtration of the polymer. Resuspension of the product in isopropanol and stirring for 15 minutes provided the final wash for the polymer. The product was then filtered and vacuum dried. Example 5: For the copolymerization of propylene and (2,6-di-t-butyl-4-allyl) phenoxy diphenylmethyl silane, the following specific procedure was used: A 500ml flask with a sidearm was evacuated and refilled with Argon three times. To this flask was added 75ml of dry, degassed heptane and the solvent was saturated with propylene. 3.23ml of triethylaluminum co-catalyst (0.715 g/ml in heptane) were then added to this solution followed by 3.06ml (0.010 mol) of (2,6-di-t-butyl-4-allyl) phenoxy diphenylmethyl silane and the flask was placed in an oil bath which had been maintained at 50°C. The polymerization was initiated by the addition of 0.075g of titanium co-catalyst and the mixture was stirred for two hours at which time it was quenched by the addition of approximately 300ml of acidified isopropanol. The alcoholic solution was allowed to stir for 1.5 hours prior to filtration of the polymer. Resuspension of the product in isopropanol and stirring for 15 minutes provided the final wash for the polymer. The product was then filtered and vacuum dried.

Claims: A silyl derivative of a 2,6-dialkyl-4-allyl phenol of the general formula wherein R¹, R² and R³ are independently selected from linear, branched and cyclic hydrocarbon groups having from 1 to about 8 carbon atoms, R¹, R² and/or R³ may be connected to form one or more substituted or unsubstituted rings, R¹, R² and R³ have a total of up to 24 carbon atoms, and R⁴ is a linear, branched or cyclic hydrocarbon group having 1 to 6 carbon atoms. A silyl derivative according to claim 1, wherein R⁴ is a methyl group. A silyl derivative according to claim 1, selected from (2,6-dimethyl-4-allyl) phenoxy tri-iso-propyl silane, (2,6-dimethyl-4-allyl) phenoxy methyldiphenyl silane, (2,6-dimethyl-4-allyl) phenoxy dimethylethyl silane, and (2,6-dimethyl-4-allyl) phenoxy trimethyl silane. A silyl derivative according to claim 1, wherein at least two of R¹, R² and R³ are connected to form one or more substituted or unsubstituted rings. A silyl derivative according to claim 1, having the general formula wherein R¹ is selected from linear, branched and cyclic hydrocarbon groups having from 1 to about 8 carbon atoms. A silyl derivative according to claim 1, having the formula A silyl derivative according to claim 1, wherein R⁴ is a t-butyl group. A silyl derivative according to claim 1, selected from (2,6-di-t-butyl-4-allyl) phenoxy tri-iso-propyl silane, (2,6-di-t-butyl-4-allyl) phenoxy methyldiphenyl silane, (2,6-di-t-butyl-4-allyl) phenoxy dimethylethyl silane and (2,6-di-t-butyl-4-allyl) phenoxy trimethyl silane. A process for preparing a silyl derivative according to any of claims 1 to 8 characterized in that the corresponding 2,6-dialkyl-4-allyl phenol is silylated. The use of the silyl derivative according to any of claims 1 to 8 as monomers for preparing homopolymers and as comonomers for prepaing copolymers.

Inventors: BROWNELL GEORGE L, HAYS MARY KAREN, SIVAK ANDREW J, BROWNELL, GEORGE L., HAYS, MARY KAREN, SIVAK, ANDREW J.
Applicants: ARISTECH CHEMICAL CORP, ARISTECH CHEMICAL CORPORATION
Application year: 1990
Main classification: C07F7
IPC codes: C07F7, C08F30