Diaphram wall construction gelation composition

Abstract: Carboxymethylcellulose (CMC) and hydroxyethylcellulose (HEC) are preferred modified polysaccharides providing at least 10% by weight gelation particles to prevent fluid loss during diaphram wall construction. A 1% solution of CMC or HEC give a 1000 mPas viscosity at 250°C. An oil slurry comprises: Solvent 45 Surfactant 2.5 Water 6 Organophillic clay 1 Modified cellulose 45.5

Description: The invention relates to diaphram walls used in construction. The invention provides a water retention fluid of gelatinous polymer for use in diaphram wall construction. Bentonite clay is commonly used to retain water within diaphram walls during construction. A disadvantage of this material is that the clay must be disposed of after it has served its purpose. Ullmans Encyclopadie der technischen Chemie, 4th Edition, Vol. 9, pp.192,209, refers to the use of water-soluble cellulose ethers such as sodium carboxyethylcellulose for use for diaphram wall construction. Modified cellulose ethers and their use as thickeners and dispersion agents are described in U.S. patents 4,228,277, 4,336,146, 4,720,303 and 4,799,962. But in spite of what was previously published and known to workers in the construction field, prior attempts to use cellulosic polymers for diaphram wall construction were not completely satisfactory due to the inability to prevent water loss from the filled trench into the surrounding soil. As a result, clay continued to be used for diaphram wall construction in spite of the environmental advantages of the use of a biodegradable polymer such as cellulose. Summary of the Invention A modified polysaccharide composition is suitable for diaphram wall construction wherein a 1% solids solution of the polysaccharide gives a viscosity of at least 1000 mPas at 25 o C and a mixture of the polysaccharide in water produces at least 10% by weight gelatinous particles. Preferred modified polysaccharides give a viscosity of at least 2000 mPas and produce at least 20% gelatinous particles and with a degree of substitution of 0.8 are carboxyethylcellulose (CMC) or hydroxyethylcellulose (HEC) with a molar substitution of 2.0-2.5. A slurry for diaphram wall construction comprises on a weight percent basis: Solvent 40-80% Surfactant 0.5-5% Water 0-10% Organophillic clay 0.5-5% Modified cellulose 20-60% A preferred slurry comprises: Paraffin oil 45% Surfactant 2.5% Water 6% Organophillic Clay 1% CMC or HEC 45.5% Detailed Description of the Invention Diaphram wall construction is common civil engineering practice for the construction of large buildings. A trench is dug around the perimeter of the building and filled with concrete to form the walls. During the digging process, the trench is kept filled with water to prevent the sides of the trench from collapsing. In order to prevent the water from migrating from the trench to the surrounding soil the water must be thickened. Bentonite which has been the practical choice for use in such trenches has several drawbacks. (1) Large quantities must be used because it is not an efficient thickener. (2) Bentonite forms a thick filter cake on the wall of the excavation which interferes with concrete pouring and bonding to the soil. (3) After the trench is filled with concrete, the displaced bentonite slurry creates a disposal problem. It has now been discovered that the disadvantages of the prior art can be avoided with modified polysaccharides including carboxymethylcellulose, Guar,sugar beet pulp derivative and hydroxyethylcellulose. Also a more cost-efficient wall can be produced according to the practice of the present invention. When added to water these modified polysaccharide with suitable viscosity and solvation properties are observed to produce a thickened gelatinous slurry which does not rapidly convert to a solution. These polymers have a long solvation time either when added to water as a powder or in the form of an oil slurry. Based upon a theoretical maximum degree of substitution of 3.0 for carboxymethyl cellulose; it has been discovered that a degree of substitution (D.S.) of at least 0.5 is required. It is preferred that D.S. be 0.8 or higher. In the case of hydroxyethylcellulose molar substitution (M.S.) of at least 1.8 is required while 2.0 to 2.5 is preferred. It has been discovered that in the case of low permeability soil a gelatinous particle content of at least 10% is required to prevent fluid loss. A gelatinous particle content of up to 20% is preferred. Depending on the soil permeability, the modified polysaccharide can be either dissolved by adding to water or dispersed in a slurry form. In low permeability soils a polymer solution can be applied directly, but for high permeability soils an oil slurry is added into the mud in a freshly dug diaphram construction trench. A typical slurry formulation comprises in weight percent: Solvent 45 Surfactant 2.5 Water 6 Organophillic clay 1 Modified cellulose 45.5 The solvent used to prepare the slurry can be diesel oil, liquid paraffin, mineral oil or vegetable oil. Useful surfactants include imidazaline, lecithine, fatty acids soaps and other substances suitable for preparing a water in oil emulsion slurry. Suitable organophillic clays include Bentone® available from Ceca SA and clays from GeoServices, Paris, France. As prepared according to the present invention, the slurry provides fast polymer swelling when added into the mud in a construction trench. Lumps are produced which coat the voids responsible for mud loss. These lumps comprise gelatinous particles which resist further solvation. It was unexpected to find that these gelatinous particles could be formed rapidly and still remain stable while protecting against fluid loss without being solubilized. Expressed in different terms of both solid and liquid ingredients, the following ranges of variation are possible for practice of the invention: Solvent 40 to 80% of the complete slurry Polymer 20 to 60% of the complete slurry Water 0 to 20% of the liquid phase Surfactant 5 to 30 Kg/m³ of the liquid phase Clay 5 to 30 Kg/m³ of the liquid phase The following example illustrates the practice of the invention. Example 1 The following parts by weight of ingredients were combined to produce a slurry. Parts Paraffin oil 45 Geumol imidazaline surfactant available from GeoService, Paris, France 2.5 Tap Water 6 Organophillic clay available from GeoService, Paris, France 1 Carboxymethylcellulose Grade 7 from Aqualon Company having a 0.8 D.S. 45.5 The slurry was poured into a diaphram construction trench filled with mud and freshly dug in a highly porous soil. A severe mud loss was observed initially, but the thick gelatinous slurry contained particles of carboxymethylcellulose which did not dissolve further coated the walls of the trench to prevent further fluid loss into the surrounding soil. After the trench was complete around the perimeter of a construction site, concrete was poured into the trench and the mud was displaced. A comparison diaphram construction trench filled with clay and carboxymethylcellulose polymer showed greater fluid loss than the invention.

Claims: A diaphram wall construction slurry, characterized in that the slurry comprises in an amount of 20-60% of the complete slurry of a polymer selected from carboxymethyl cellulose having a degree of substitution (D.S.) of at least 0.5, hydroxyethylcellulose having a molar substitution (M.S.) of at least 1.8, Guar or sugar beet pulp derivative with the polymer being such that a 1% solids solution of the polymer gives a viscosity of at least 1000 mPas at 25 o C and a mixture of the polymer in water produce at least 10% by weight gelatinous particles such that the slurry can be used for low permeability soil and a solvent selected from the group consisting of diesel oil, liquid paraffin, mineral oil and vegetable oil. The slurry of claim 1 where the polymer has a viscosity of at least 2000 mPas and at least 20% by weight gelatinous particles are produced. A slurry for diaphram wall construction comprising on a weight percent basis: Diesel, mineral or paraffin oil 40-60 Imidazaline surfactant 1-4 Water 0-10 Organophillic clay 0.5-1.5 CMC or HEC 40-60 The slurry of Claim 3 with carboxymethylcellulose having a D.S. of at least 0.8 or hydroxyethylcellulose having a M.S. of at least 1.8.

Inventors: ZAPICO JOSE NMN, ZAPICO, JOSE (NMN)
Applicants: AQUALON CO, AQUALON COMPANY
Application year: 1990
Main classification: C09K7
IPC codes: C09K8, F02B3, E04F13, E02D5