Method of producing micromechanical sensors for the AFM/STM/MFM profilometry and micromechanical AFM/STM/MFM sensor head

Abstract: A method for producing micromechanical sensors for the AFM/STM/MFM profilometry is described in which a multiple step mask of cantilever beam and tip is transferred step by step into the wafer substrate by reactive ion etching. A particular highly anisotropic etching step is used for etching and shaping of the tip. This process step uses an Ar/Cl₂ ambient at a pressure of about 100 µbar and a self bias voltage of about 300 V DC. The ratio of pressure to self bias voltage determines the concave shape of the tip sidewalls. This etching step is followed by a thermal oxidation step. The oxidation is carried out for a time until the oxidation fronts at the thinnest point of the tip shaft touch each other. A stripping process with buffered hydrofluoric acid gently removes the thermally grown oxide. The oxidation process allows - via oxidation time - a modification of tip height and angle in an extremely controllable manner. To prevent sticking of the tip to the structure to be profiled the ratio of tip diameter to tip height should be about 1 : 10. Should this ratio be exceeded the tip has to be arranged on a pedestal. The structure, comprising a cantilever beam and a tip on pedestal, can be produced with the same but slightly modified process of the invention.

Description: The present invention relates to a method of producing micromechanical sensors for the AFM/STM/MFM profilometry, which consist of a cantilever beam and an integrated tip or an integrated tip on a pedestal. The invention also relates to a sensor head made in accordance with the method of the invention. The scanning tunneling microscope (hereafter abbreviated STM) has stimulated the development of new techniques for microcharacterization of materials which are based on the use of a very fine tip. One of these techniques involves the atomic force microscope (hereafter abbreviated AFM) which has recently demonstrated the capability to profile and image conductors and insulators. In the initial design of the AFM (Binnig G, Quate CF, Gerber Ch, (1986) Atomic Force Microscope, Phys. Rev. Lett. 56, 930 - 933 and EP-A-0 223 918) a sensor consisting of a spring-like cantilever which is rigidly mounted at one end and carries at its free end a dielectric tip profiles the surface of an object. The force between the object's surface and the tip deflects the cantilever, and this deflection can be accurately measured, for example by a second tip which is part of an STM. A lateral spatial resolution of 3 nm has initially been achieved. Another version of the AFM includes optical detection instead of an STM detection. In this version a tungsten tip at the end of a wire is mounted on a piezoelectric transducer. The transducer vibrates the tip at the resonance frequency of the wire which acts as a cantilever, and a laser heterodyne interferometer accurately measures the amplitude of the a. c. vibration. The gradient of the force between the tip and sample modifies the compliance of the lever, hence inducing a change in vibration amplitude due to the shift of the lever resonance. Knowing the lever characteristics, one can measure the vibration amplitude as a function of the tip - sample spacing in order to deduce the gradient of the force, and thus, the force itself (Duerig UT, Gimzewski JK, Pohl DW (1986) Experimental Observation of Forces Acting During Scanning Tunneling Microscopy, Phys. Rev. Lett. 57, 2403 - 2406; and Martin Y, Williams CC, Wickramasinghe HK (1987) Atomic Force Microscope-Force Mapping and Profiling on a sub 100-A Scale, J. Appl. Phys. 61(10), 4723 - 4729). A most critical component in the AFM is the spring-like cantilever. As a maximum deflection for a given force is needed a cantilever is required which is as soft as possible. At the same time a stiff cantilever with a high eigenfrequency is necessary in order to minimize the sensitivity to vibrational noise from the building. Usually, ambient vibrations, mainly building vibrations, are of the order of <100 Hertz. If the cantilever is chosen such that it has an eigenfrequency f o ≧ 10 kHz, the ambient vibrations will be attenuated to a negligible value. These requirements can only be met by reducing the geometrical dimensions of the cantilever as reflected by the following two equations: The eigenfrequency f o of the cantilever is given by wherein E is Young's modulus of elasticity, ρ is the density, and K is a correction factor close to unity, l is the length, and t is the thickness of the cantilever. The spring constant of the cantilever on which its sensitivity depends is given by wherein F is the force which causes the deflection y of the cantilever, E is Young's modulus of elasticity, w is the width, l is the length, and t is the thickness of the cantilever. In accordance with the spring constant term the sensitivity of the cantilever is dependent on its dimensions and on the material of which it consists, with the highest sensitivity being obtained for long, thin and narrow cantilever beams. The width of the cantilever beam should be sufficiently large so that lateral vibrations are suppressed. Also, the width of the beam should permit the fabrication of additional structures, such as tips, thereon. Therefore, a minimum width w of around 10 µm seems reasonable. In practice, C has to be about ≧ 1 N/m in order to avoid instabilities during sensing of attractive forces, to prevent excessive thermal vibrations of the cantilever beam, and to obtain a measurable response. Dimensions of a cantilever beam compatible with C = 1 N/m, and f o = 10 kHz are for example: 1 = 800 µm, w = 75 µm, and t = 5.5 µm. In the normal deflection mode of the cantilever beam forces in the order of 10⁻¹² N can be detected. The sensitivity of the sensor head can be further enhanced by vibrating the object to be profiled at the resonance frequency f o of the cantilever beam, as described by G. Binnig et al in Phys. Rev. Lett. 56 (1986), pp. 930 - 933. In the AFM realized in accordance with the aforementioned Binnig et al article and with EP-A-0 223 918 the requirements for cantilever and tip were met by a gold foil of about 25 µm thickness, 800 µm length, and 250 µm width to which a diamond fragment was attached with a small amount of glue. Another proposal used microfabrication techniques to construct thin-film (1.5 µm thick) SiO₂ microcantilevers with very low mass on which miniature cones could be grown by evaporation of material through a very small hole (Albrecht ThR, Quate CF, (1988) Atomic Resolution with the Atomic Force Microscope on Conductors and Nonconductors, J. Vac. Sci. Technol., 271 - 274. From the foregoing description of the state of the art it was known to construct, in a first process step, cantilevers, and, in a second process step, to attach tips thereto. It will be obvious to those skilled in the art that the construction of a cantilever with tip of that type is extremely delicate and prone to low yield. Most recently, several processes have been developed for producing micromechanical sensor heads for the AFM/STM profilometry, see for example European patent applications EP-A-413 042, EP-A-413 041, and EP-A-413 040. European patent application EP-A-413 042 describes a process for producing a cantilever beam with an integrated tip. In this process a mask is produced which contains all relevant information for the desired cantilever beam pattern and tip pattern. In a subsequent etching process the mask is transferred step by step to a silicon substrate. The shape of the tip is determined by anisotropic wet and underetching of the tip mask. The tip terminates as a straight line in the form of a multiside pyramid. The cone angle of the tip made in accordance with this process is ≧ 35 °. However, for the present invention it is desirable to have a method by which comically shaped tips can be produced with cone angles < 30 °, preferably about 10 °, with highest accuracy and high yield. Particularly in Magnetic Force Microscopy the domain resolution depends on the tip shape and cone angle. It is an object of the invention to teach a method for the construction of microcantilevers with integrated tips, which method uses a suitable combination of deposition, lithography, etching, and oxidation steps. The object of the invention is achieved with a method in accordance with claims 1, 7 to 11, and 12 to 18. The invention also comprises structures made in accordance with the method of the invention. Prior to starting with the description of the details of the invention reference is made to the following publications relating to micromechanics: Petersen, KE, Dynamic Micromechanics on Silicon: Techniques and Devices, Vol. ED-25, No. 10, October 1978, pp. 1241 - 1250; Petersen, KE, Silicon as a Mechanical Material, Proc. of the IEEE, Vol. 70, No. 5, May 1982, pp. 420 - 457; and Jolly, RD, Muller, RS, Miniature Cantilever Beams Fabricated by Anisotropic Etching of Silicon, J. Electrochem Soc.: Solid-State Science and Technology, December 1980, pp. 2750 - 2754. With the method of the present invention low-mass microcantilever beams can be made with an integrated tip for interaction with the surface of a sample to be profiled. The force and resonance frequency requirements of cantilever beam and integrated tip are met by using the microfabrication techniques. Due to the fact that cantilever and tip are made from one piece of material there are no adhesion problems between cantilever and tip. The process of the present invention is based on the process of EP-A-413 042 in that the steps for producing the mask, which contains all relevant information for the substrate etching of the cantilever beam and the tip (see Figs. 4 a to 4 c), are practically identical, but the following steps for etching the cantilever beam and the basic shape of the tip into the substrate constitute anisotropic ion etching processes. The tip shaping process is followed by a thermal oxidation and a stripping process which gently removes the thermally grown silicon dioxide. Particularly the oxidation step allows an extremely exact definition and variation of tip height and cone angle via oxidation time. By the process of the second example of the present invention a tip on a pedestal is produced. As mentioned in the introduction to the description, the sensitivity of cantilever beam and tip depends on their dimensions. Where a very small diameter of the tip is desired for investigating submicron structures the tip length is limited to a certain value to prevent the tip from sticking to the structures to be investigated. In practice, the ratio of tip diameter to tip length should be about 1 : 10 or less to avoid such sticking. Therefore, in order to obtain a distance from the tip end to the cantilever beam of about 6 to 10 µm the tip has to be arranged on a pedestal. The process of example 2 is a completely self-aligned process for producing a tip with a diameter of 0.2 µm and a length of 2 µm arranged on a pedestal with a diameter of 1 µm in an absolutely concentrical manner. This process is extremely advantageous over the prior art process (EP-A-413 042, third example, claim 19) where a tip with a base diameter of 30 µm arranged on a pedestal with a diameter of about 100 to 200 µm is produced, with the associated etching masks being adjusted against each other. Details of several embodiments of the present invention will be described by way of example with respect to the accompanying drawings in which: Fig. 1 shows a sequence of process steps for making a cantilever beam with integrated tip which has been worked out of a silicon wafer substrate, using a mask with two levels of information, and photolithographic, etching and oxidation steps. Fig. 2 shows a sequence of process steps for making a cantilever beam with integrated tip on a pedestal which has been worked out of a silicon wafer substrate, using a mask with two levels of information, and photolithographic, etching and oxidation steps. A first example of the process of the invention is described in accordance with Fig. 1 (A to I). This example relates to the development of a structure, such as a tip, on an already 3-dimensionally structured substrate, such as a cantilever beam. In this process problems arise for example when the flexible and fragile cantilever beams have to be coated with photoresist for subsequent exposure. These and other problems are solved in that a mask which is applied to a substrate is structured in such a manner that it contains all relevant information for the subsequent substrate etching process. This means that the structures of all lithography steps are etched one after the other into the mask before substrate etching. Subsequently, this information is transferred step by step from the mask into the substrate. Between two successive substrate etching process steps there is a mask etching step which does not require an additional lithography step however. This multiple step mask can be fabricated in conventional planar technology. A further advantage is that there are no problems with respect to photoresist coverage and exposure as the mask has a thickness of only a few µm. The process benefits from the high selectivity of mask versus substrate in the substrate etching process which comprises several dry etching steps. Following Fig. 1 A, a (100) silicon wafer (1) is bilaterally coated with silicon dioxide. The oxide layers (3) and (2) on the top side and on the bottom side are thermally grown to a layer thickness of about 3 µm. The oxide layers can also be applied by sputter deposition or (PE)CVD. In a first photolithographic step the patterns of cantilever beam (4) and of rectangular openings (5) which are subsequently transferred into the upper part of silicon dioxide layers (3) and (2) are defined. For this purpose AZ 1350 positive photoresist of the Shipley Company is bilaterally applied to the oxide coated wafer (1) (not shown). The photoresist layers on both sides are exposed at the same time and developed, with the respective masks on the bottom side of the wafer being in alignment with those on the top side. The oxide on both sides is etched in 5 : 1 buffered hydrofluoric acid or by reactive ion etching under the following process conditions: etch gas: CF₄ pressure range: 1 to 10 µbar, and for a time depending on the desired etch depth on the top side. Next, the top side is protected by a baked photoresist layer, and the oxide residue in the exposed areas (5) on the bottom side of the wafer is removed by etching in 5 : 1 buffered hydrofluoric acid. Next, the remaining photoresist is removed. The resulting structure is shown in Fig. 1 A. In a second photolithographic step the pattern (6) of the tip is defined in a newly applied photoresist layer over silicon dioxide cantilever pattern (4) (not shown). The photoresist tip pattern is transferred into the silicon dioxide by etching in 5 : 1 buffered hydrofluoric acid or by reactive ion etching, as described above. During this etching step the cantilever beam pattern (4) is transferred to a deeper level of layer (3), and the thickness of the remaining silicon dioxide layer (3) is reduced correspondingly. The bottom side of the wafer is protected by a baked photoresist layer during this step. The resulting silicon dioxide mask structure (4, 6) which will then be transferred step by step into the silicon substrate (1) is shown in Fig. 1 B. Prior to this mask structure transfer the silicon afer (1) is thinned down by etching from the bottom side to a thickness which corresponds to about the thickness of the cantilever beam plus about twice the height of the tip plus a residual wafer thickness which is consumed during thermal oxidation. This etching step which uses an about 37.5 wt% aqueous KOH solution at about 80 oC is anisotropic. The resulting structure is shown in Fig. 1 C. Next, as shown in Figs. 1 C, D, silicon dioxide layer (3) with structures (4) and (6) is etched in 5 : 1 buffered hydrofluoric acid or by reactive ion etching, as described above, to such a depth that the silicon dioxide areas (7) abutting cantilever beam mask (4) are removed. An anisotropic reactive ion etching step follows for the transfer of the cantilever beam pattern (4) into the silicon wafer (1). The reactive ion etching performed for that purpose is carried out under the following conditions: etch gas: 10 flow% chlorine, remainder Ar or He pressure range: 2 to 20 µbar, preferably 10 µbar. Other methods for etching silicon use gas mixtures with a content of SF₆, Cl₂ and helium; or CCl₂F₂ and O₂; or SiF₄, Cl₂ and helium or argon. In a system with 10 flow% Cl2 in argon, etching rate ratios of silicon to silicon dioxide of up to 20 : 1 are obtained. The anisotropic etching step removes the areas of the silicon wafer (1) originally underlying silicon dioxide areas (7) in a depth which corresponds to the desired silicon cantilever beam thickness (Fig. 1 E). Now, silicon dioxide cantilever beam mask (4) and the silicon dioxide masks (2) on the bottom side of the wafer are removed by etching in 5 : 1 buffered hydrofluoric acid or by reactive ion etching, as described above. The resulting structure with cantilever beam (41) and tip mask (6) on top is shown in Fig. 1 F. A particular highly anisotropic etching step follows for etching and shaping tip (61, fig. 1 G). First, the basic shape of the tip (61) is produced. At the same time the sidewalls of the resulting 'stamp' (61) are etched such that a concave shape is obtained. The concave tip sidewalls are a result of ion scattering in the plasma sheath according to an appropriate ratio of pressure to self bias voltage.This is achieved by an Ar/Cl₂ or He/Cl₂ reactive ion etching process which uses a relatively high pressure of about 100 µbar, and a comparatively low self bias voltage of about 300 V DC which depends on the reactor used. The etching time is determined by the desired ratio of tip thickness to tip height. Concurrently with the etching and shaping of the tip (61) the cantilever beam is released from the wafer body (1). The silicon dioxide etching mask (6) is removed by etching with 5 : 1 or concentrated buffered hydrofluoric acid. The radius of curvature of the resulting concave sidewalls defines the smallest obtainable cone angle of the future conically shaped tip. The reactive ion etching step is followed by a highly controlled process step, i. e. thermal oxidation. This oxidation is carried out at a temperature of at least about 1000 °C in water vapor. Fig. 1 H shows a sectional view of a phase where the oxidation fronts (8) touch each other at the thinnest point of the stamp. As the volume grows during this thermal oxidation the thickness and height of the stamp (61) are increased which increases the strength of the stamp against mechanical damage. The thermal oxidation process is followed by a stripping process which uses buffered hydrofluoric acid and gently removes the thermally grown silicon dioxide (8). The resulting structure which comprises cantilever beam (41) and tip (61) is shown in Fig. 1 I. SEM micrographs showed that the tip height and the cone angle of said tip could be modified in an extremely controllable manner by adjusting the oxidation time. The radii of the tips made in accordance with the process of this invention were 10 nm or less. Furthermore, the tips were characterized by an excellent rotational symmetry. Compared with the prior art processes for making micromechanical sensors the process of the present invention is characterized by a high flexibily with respect to the tip shape and an extraordinary high yield. The second example of the process of the invention is described in accordance with Fig. 2 (A to E). The process steps for producing the multiple step cantilever beam and tip mask, and the mask on the bottom side of the wafer, as well as the step for thinning down the silicon wafer by etching from the bottom side are identical to those described in example 1 in accordance with Figs. 1 A to 1 D. The silicon dioxide areas abutting the cantilever beam mask were removed by etching, as described above (not shown). Next, the cantilever beam pattern was transferred into the silicon wafer by reactive ion etching in an Ar/Cl₂ or He/Cl₂ ambient at a pressure of about 10 µbar. Subsequently, the silicon dioxide cantilever beam mask, and the silicon dioxide mask on the bottom side of the wafer were removed by etching, as described in example 1 (not shown). Now follows an anisotropic etching step for shaping the tip. In order to obtain a tip shaft with straight sidewalls the etching is carried out in an Ar/Cl₂ or He/Cl₂ ambient at a pressure of about 10 ubar, and for a time depending on the desired etch depth, i. e. length of the tip shaft. In order to obtain a tip shaft with concave sidewalls the etching is carried out in an Ar/Cl₂ or He/Cl₂ ambient at a relatively high pressure and a comparatively low self bias voltage, as described in example 1. The resulting structure, comprising silicon substrate (21), cantilever beam (241), tip (261), and tip mask (26) is shown in Fig. 2 A. The reactive ion etching step is followed by a highly controlled process step, i. e. thermal oxidation. As described in example 1, the oxidation is carried out at a temperature of at least about 1000 °C in water vapor. The resulting structure, with silicon dioxide (28) covering all horizontal and vertical surfaces of structure (261, 241) and substrate (21), is shown in Fig. 2 B. Next, the silicon dioxide (28) is removed from all horizontal surfaces of said structure by reactive ion etching in CF₄ at a pressure of about 10 µbar. This etching is interrupted when all silicon dioxide has been removed from the horizontal surfaces. The resulting structure is shown in Fig. 2 C. Next, the pedestal (29) is etched into the cantilever beam (241) to the desired depth, with the layers of silicon dioxide (28) on the vertical surfaces of structure (261, 241) and tip mask (26) acting as masks. The reactive ion etching is carried out in an Ar/Cl₂ or He/Cl₂ ambient at a pressure of about 10 µbar. Concurrently with the pedestal etching the cantilever beam is released from the wafer body (21). The resulting structure is shown in Fig. 2 D. This process step is followed by a stripping process which uses 5 : 1 or concentrated buffered hydrofluoric acid, and gently removes the remaining silicon dioxide masks. The final structure, comprising cantilever beam (241), pedestal (29), and tip (261) with a rectangular cross-section, is shown in Fig. 2 E. The tip (261) may be pointed in a maskless argon ion etching step, utilizing the effect that for the combination argon gas and silicon substrate the etch rate is angle-dependent. The process parameters for the pointing of the tip are: - flow: 20 sccm Ar, - pressure: 3 µbar, - RF: 1000 V, and DC: 630 V. Alternatively and as already mentioned above, the tip shaping can be performed at an earlier process stage, i. e. after the transfer of the cantilever beam pattern into the silicon wafer substrate, the removal of the silicon dioxide cantilever beam mask, and concurrently with the etching of the tip (see Fig. 2 A). To obtain a tip shaft with concave sidewalls the etching has to be carried out in an Ar/Cl₂ ambient at a high pressure of about 100 µbar. In this case, the original height of the tip shaft (261) has to be about twice the height of the final tip, as the conically shaped tip shaft is divided in practically two equal parts by thermal oxidation and oxide stripping.

Claims: Method of producing micromechanical sensors for the AFM/STM/MFM profilometry which consist of a cantilever beam and a tip or a tip on pedestal at one end of said cantilever beam comprising the following steps: 1. producing a first mask (4) of the desired cantilever beam pattern (41, 241) on the top side, and a second mask (2) on the bottom side of the wafer (1); 2. producing a third mask (6, 26) of the desired tip (61) or tip on pedestal (261, 29) pattern in the area of said first mask (4) on the top side of the wafer (1); 3. thinning down the wafer substrate (1) to a desired thickness by etching through said second mask on the bottom side of said wafer (1); 4. transferring the cantilever beam pattern defined by said first mask (4) into said wafer (1) by etching said first mask (4) to such a depth as to remove the areas (7) of the mask abutting the cantilever beam mask (4), and removing said cantilever beam mask (4) and said second mask (2) by etching; 5. transferring the tip or tip on pedestal pattern defined by said third mask (6, 26) in the area of said cantilever beam pattern (41, 241) into said wafer (1) by highly anisotropic etching and removing said third mask (6) characterized in that said method further comprises 6. thermally oxidizing the exposed surfaces of the resulting cantilever beam/tip structure (41, 61; 241, 261) to a desired thickness; and 7. removing the thermally grown oxide (8) by etching, thereby exposing the desired cantilever beam/tip structure; or 8. in the case of tip on pedestal, removing said oxide (28) from the horizontal surfaces of said cantilever beam pattern (241) by etching, etching said pedestal (29) into said substrate, and finally removing said oxide (28) from the vertical surfaces of cantilever beam/tip structure (241, 261), and tip mask (26) thereby exposing said tip (261) on pedestal (29) on said cantilever beam (241) respectively. Method of claim 1, wherein the wafer substrate (1) consists of monocrystalline silicon, and the layers (3, 2) on the top side and on the bottom side of the wafer consist of thermally grown silicon dioxide, or sputtered oxide, or (PE)CVD oxide. Method of claims 1 and 2, wherein the desired cantilever beam pattern (4) is defined in said silicon dioxide layer (3) on the top side of said wafer, using a first photolithographic step and a wet or dry etching step. Method of claim 3, wherein simultaneously with said first photolithographic step and said etching step rectangular openings (5) are made on the bottom side of said wafer (1). Method of claims 1 to 3, wherein the desired tip pattern (6) is defined in the area of the cantilever beam pattern (4) in said silicon dioxide layer (3), using a second photolithographic step and a wet or dry etching step. Method of one or several of claims 1 to 5, wherein prior to the mask structure transfer into the silicon wafer wafer substrate (1) said substrate is thinned down by anisotropic etching from the bottom side of the wafer with aqueous KOH solution (37.5 wt%) at about 80 °C. Method of one or several of claims 1 to 6, wherein the cantilever beam pattern (41) is anisotropically etched into the silicon wafer substrate (1), using silicon dioxide mask (4), and Ar/Cl₂ or He/Cl₂ as etch gas at a pressure of about 2 to 20 µbar; and wherein silicon dioxide mask (4) is removed by etching with CF₄ as etch gas at a pressure of about 1 to 10 µbar. Method of one or several of claims 1 to 7, wherein the tip (61) is anisotropically etched in the area of cantilever beam (41) into the substrate and concurrently shaped, using silicon dioxide mask (6), and Ar/Cl₂ or He/Cl₂ as etch gas, and wherein silicon dioxide tip mask (6) is removed by etching with CF₄ as etch gas at a pressure of about 1 to 10 µbar. Method of claim 8, wherein the anisotropic etching step is performed at a pressure of about 100 µbar, and a self bias voltage of the reactor of about 300 V DC, thereby obtaining a concave tip shape. Method of claims 8 and 9, wherein concurrently with the etching and shaping of the tip (61) the cantilever beam is released from the silicon body (1). Method of one or several of claims 1 to 10, wherein the silicon structure (41, 61) resulting from the anisotropic dry etching steps is thermally oxidized at a temperature of at least about 1000 °C in water vapor, and wherein the thermally grown silicon dioxide is removed by wet etching in buffered hydrofluoric acid, thereby exposing tip (61) on cantilever beam (41). Method of claims 1 and 7, wherein following the transfer off the cantilever beam pattern into the silicon wafer substrate (21) by reactive ion etching, the tip (261, Fig. 2 a) is anisotropically etched in the area of cantilever beam (241) into the substrate, using silicon dioxide mask (26), and Ar/Cl₂ or He/Cl₂ as etch gas. Method of claim 12, wherein in order to obtain a tip shaft with straight sidewalls the etching is carried out in Ar/Cl₂ at a pressure of about 10 µbar. Method of claim 12, wherein in order to obtain a tip shaft with concave sidewalls the etching is carried out in Ar/Cl₂ at a pressure of about 100 µbar. Method of one or several of claims 1 to 14, wherein the silicon structure (261, 241, 21) is thermally oxidized at a temperature of at least about 1000 °C in water vapor, and wherein the thermally grown silicon dioxide (28) is removed from the horizontal surfaces of cantilever beam (241) and silicon substrate (21) by anisotropic etching with CF₄ as etch gas at a pressure of about 1 to 10 µbar. Method of claim 15, wherein the pedestal (29) is etched to the desired depth into cantilever beam substrate (241), using the silicon dioxide layers (28) on the vertical surfaces of cantilever beam/tip structure (241/261) and tip mask (26) as masks, and Ar/Cl₂ or He/Cl₂ as etch gas at a pressure of about 10 µbar. Method of claim 16, wherein concurrently with the etching of pedestal (29) the cantilever beam is released from the wafer body (21). Method of claims 16 and 17, wherein the remaining silicon dioxide masks are removed by etching with buffered hydrofluoric acid. Method of one or several of claims 12 to 18, wherein the tip(261) is pointed in a maskless argon ion etching process. Micromechanical sensor for the AFM/STM/MFM profilometry comprising a cantilever beam with an integrated tip, characterized in that said tip has high rotational symmetry and a cone angle < 10 °, whereby said cantilever beam with integrated tip is produced by producing a multiple step mask pattern for cantilever beam and tip, transferring said pattern step by step into the silicon wafer substrate by anisotropic etching, thermally oxidizing the resulting structure to a thickness that the oxidation fronts of the tip touch each other, and removing the oxide by wet etching thereby exposing a cantilever beam with integrated tip. Micromechanical sensor of claim 20 further characterised in that subsequent to the mask transfer of cantilever beam and tip, and thermal oxidation, the oxide layers covering the horizontal surfaces of cantilever beam and substrate are removed, a pedestal is etched using the oxide layers covering the vertical surfaces of cantilever beam and tip and the tip mask as masks, and said oxide is removed by wet etching thereby exposing a cantilever beam structure with tip on pedestal. Micromechanical sensor of claim 20 or 21, characterized in that the ratio of tip diameter to tip length is about 1 : 10, and, should this ratio be exceeded, a pedestal of the corresponding height is required.

Inventors: BAYER THOMAS, GRESCHNER JOHANN DR, BAYER, THOMAS, GRESCHNER, JOHANN, DR.
Applicants: IBM, INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1990
Main classification: G01B7
IPC codes: G01B7, H01J9, G01B21, G01N13, H01J37, C23F4