Cutting-off tool

Abstract: A cutting-off tool having an insert (1) having two side cutting edges (5,6) formed by the ridge lines defined by a rake face (2) and side flanks (7). These edges (5,6) are chamfered so that the cutting edge at one side which is likely to hit the falling part of the material cut off is chamfered by a larger width than at the other side.

Description: This invention relates to a cutting-off tool according to the precharacterizing portion of the claim, see WO-A-8 901 375. The cutting-off work by a cutting-off tool poses peculiar problems. For example, as shown in Fig. 4: 1) Part of material A′ drops after cutting-off. 2) When a cutting-off tool B is pulled back straight after moved forward for cutting-off, it tends to be abraded by contact with the material A being machined which is rotating by inertia, supported on a chuck. About the first problem, if the material A′ inclines the moment it has been cut off, it might hit the cutting-off tool while dropping. This might damage a side cutting edge 6 at the righthand side of the figure. About the second problem, a side cutting edge 5 at the lefthand side might be worn or welded to the material A to be machined. Such problems cannot be ignored in view of the fact that tools nowadays are made of expensive materials such as cemented carbide and a hard sintered compact which is even harder than the former. But a tool which is free of these problems is yet to be found. Fig. 5 shows a prior art cutting-off tool. This tool B has its insert 1′ brazed to a shank. A throw away type tool is also known in which its insert is detachable. In any case, since a prior art cutting-off tool 4 has front and side cutting edges 4, 5 and 6 identical in shape to each other, it is difficult to evade both of the above-described problems caused to the side cutting edges 5 and 6. It is an object of this invention to provide a cutting-off tool which has an ideal shape in obviating the abovesaid shortcomings. In accordance with the present invention, one of the cutting edges at one side is chamfered by a width H₁ whereas the cutting edge at the other side is chamfered by a width H₂ and the widths H₁ and H₂ satisfy the following relations: H₁ > H₂, H₁ ≧ 0.01 mm, H₂ ≦ 0.5 mm It is well-known that a cutting edge can be strengthened by chamfering it. According to this invention, the side cutting edge at one side which may possibly collide with a falling material is chamfered by an amount H₁ (0.01 mm or more) which is larger than the side cutting edge at the other side to increase its resistance to breakage. Thus the cutting edge is less likely to break even if it collides with the material machined. Since the side cutting edge at the other side has a chamfer amount H₂ which is smaller than H₁ within the range of 0.5 mm or less to keep its sharpness, the material to be machined will be ground if the tool gets into contact with the material when it returns to its original position. Thus wear owing to abrasion and welding will decrease. The chamfer amount H₁ of the first-mentioned side cutting edge is limited to 0.01 mm or over. This is because though the smaller the H₁ value, the higher the sharpness of the edge, experiment results revealed that if the H₁ value is less than 0.01 mm, the edge tends to be broken more easily. Also, though the larger the H₂ value, the higher the strength of the edge, if the H₂ value is more than 0.5 mm, the sharpness of the edge lowers remarkably. With the cutting-off tool according to this invention, the side cutting edge which may collide with the material to be machined is chamfered sufficiently to prevent if from being broken, whereas the other side cutting edge is chamfered to a lesser degree to assure its sharpness. Thus the former side cutting edge is prevented from breaking and the other one is effectively prevented from wearing and welding. This will assure effective use of the tool. Other features and objects of the present invention will become apparent from the following description taken with reference to the accompanying drawings, in which: Fig. 1 is a perspective view of the embodiment according to this invention; Fig. 2 is an enlarged plan view of the insert showing its edge; Fig. 3 is a sectional view taken along line III-III of Fig. 2; Fig. 4 is a perspective view showing how a material is cut off; Fig. 5 is a perspective view of a prior art cutting-off tool; Fig. 6 is a diagram of a side cutting edge showing its round honing shape; and Fig. 7 is a diagram of a front cutting edge showing its round honing shape. Figs. 1 to 3 show a throw away cutting-off tool embodying this invention. In these figures, a throw away insert 1 and a clamp type holder 10 are shown. The insert 1 has a front cutting edge 4 formed by the ridge line defined by a rake face 2 and a front flank 3, and side cuttig edges 5 and 6 having their front ends connecting to both ends of the front cutting edge 4. The side cutting edge 5 at one side is formed by the ridge line defined by a side flank 7 and the rake face 2 and is subjected to round honing so as to be chamfered by a width H₂ (Fig. 3). The side cutting edge 6 at the other side is formed by the ridge line defined by a side flank 8 and the rake fafe 2 and is subjected to round honing so as to be chamfereed by a width H₁. The chamfered surface may be flat. In either case, the H₁ and H₂ values should be determined to meet the requirements that the minimum value of H₁ is 0.01 mm, the maximum value of H₂ is 0.5 mm, and H₁ > H₂. In the figures, numeral 9 designates a chip breaker groove. It serves to deform the chips in such a direction as to separate from the surface to be machined. This facilitates chip discharge. Fig. 6 shows a preferable shape of the chamfer of the side cutting edges 5 and 6 formed by round honing. In this figure, the H₁ and H₂ values are within the aforementioned range. But preferably they should satisfy not only the relation, H₁ > H₂ but also the conditions of H₂ = 0.02 - 0.04 mm, H₁ = 0.04 - 0.06 mm, ϑ (angle of chamfer) should be 40 - 60 degrees. Fig. 7 shows a preferable shape of the chamfer of the front cutting edge 4 formed by round honing. Among the radii of curvature at various portions of the chamfer, R₀ is larger than R₁ and R₂. Also, R₁ should be 0.04 - 0.06 mm, H₃ should be 0.08 - 0.12 mm and ϑ₁ should be 8 - 15 degrees. Such a round honed surface can be machined by pressing a disk-shaped brush grindstone planted with resin filaments containing diamond grains so that the filaments will contact the flank first and get off the insert from the rake face.

Claims: A cutting-off tool having an insert having a front cutting edge (4) and two side cutting edges (5,6) formed by the ridge lines defined by a rake face (2) and side flanks (7,8), characterized in that one (8) of said side cutting edges (6) located at one side (8) where the cut-off part of the material falls is chamferred by a width H₁ and the cutting edge (5) at the other side is chamferred by a width H₂, and in that said width H₁ and H₂ satisfies the following relations : H₁ > H₂; H₁ ≧ 0.01 mm; and H2 ≦ 0.5 mm.

Inventors: HIROSE KEIJI C O ITAMI WORKS, NOGUCHI KAZUO C O ITAMI WORKS, SETOGUCHI SUNAO C O ITAMI WORK, HIROSE, KEIJI, NOGUCHI, KAZUO, SETOGUCHI SUNAO, HIROSE, KEIJI, C/O ITAMI WORKS, NOGUCHI, KAZUO, C/O ITAMI WORKS, SETOGUCHI SUNAO, C/O ITAMI WORKS
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1990
Main classification: B23B27
IPC codes: B23B27