Process for removing fine particles from articles of fluorine-containing resin

Abstract: The invention provides a method for removing the fine particles deposited on an article of fluorine-containing resin, the method comprising bringing the article into contact with a polar solvent or an aqueous solution of polar solvent.

Description: The present invention relates to a process or removing particulate components deposited as impurities on the molded products of fluorine-containing resin. Currently even fine particles of submicron size must be removed from the molded products of fluorine-containing resin in the field of the so-called high technology. Further, a demand for higher degree of cleaning is expected to increase. For example, containers made of fluorine-containing resin are currently used for holding an agent or wet etching in production of semiconductors, i.e. representative products in the field of the high technology. These containers are usually cleaned with a dilute aqueous solution of a surfactant, strong acid, ultrapure water, or when required, may be cleaned by supersonic treatment or immersion. These methods, however, can not achieve a satisfactory level of cleaning on containers of fluorine-containing resin, compared with the level on containers of polyethylene and therefore may be unemployable for containers for holding an agent for wet etching. JP-A-63-310683 discloses a method for cleaning articles of fluorine-containing resins, comprising introducing steam into a washing container, maintaining the container at a high temperature, high pressure and high humidity for a specific period of time, reducing the internal pressure of the container and showering the article in the container with water to rapidly cool the article. DD-A-152921 discloses a method for removing particles adhering to a surface by spraying the surface with ultra-pure water and at the same time exposing the surface to ultra-violet rays. US-A-4680060 discloses a process for extracting contaminants from the surface of plastics articles using alcohol. However, these documents merely disclose cleaning methods using water or alcohol as a cleaning solution. None of these documents disclose that fine particles deposited on articles of fluorine-containing resins can be removed to a high degree of cleaning by bringing the article into contact with a specific polar solvent used in the present invention. Therefore, these documents disclose in no way the technical features of the present invention. More specifically, the containers of fluorine-containing resin for holding a 50% aqueous solution of HF to be used in the manufacture of semiconductors must be cleaned to such an extent that after cleaning, 10 particles or less are contained in one milliliter of the solution in terms of the particles not smaller than 0.3 µm in particle size, and that after cleaning, one particle or less is contained in one milliliter thereof in terms of the particles not smaller than 0.5 µm in particle size. The cleaning with ultrapure water can not attain the above levels at all. Use of containers of fluorine-containing resin is limited because they remain difficult to clean. Consequently such containers may become substantially out of use when a higher cleaning level is set in future. It is an object of the present invention to provide a method for removing the particulate components as impurities from the molded products of fluorine-containing resin. Other objects and features of the invention will become apparent from the following description. In view of the aforesaid state of the art, we conducted extensive research and found that the fine particles can be effectively removed from an article of fluorine-containing resin when the article is maintained at a high temperature. Our another finding was that a similar particle-removing effect can be also produced when the article is maintained in the atmosphere of a specific fluorine-type gas. Our additional finding was that a similar particle-removing effect can be also achieved when the article is brought into contact with a specific solvent. The present invention has been accomplished based on these novel findings. According to the the present invention, there are provided: (1) a method for removing the fine particles deposited on an article of fluorine-containing resin, the method comprising bringing the article into contact with a polar solvent or an aqueous solution of polar solvent, the polar solvent being at least one solvent selected from the group consisting of fluorine-containing carboxylic acids represented by the formula R f COOH wherein R f is a fluorine-containing hydrocarbon group having 3 to 20 carbon atoms and ketones represented by the formula R 1 COR 2 wherein R 1 and R 2 are the same or different and each represent an alkyl group having 1 to 5 carbon atoms ; and (2) a method as defined above in item (1) in which the article is cleaned at least once with at least one of ultrapure water, a cleaning agent and an aqueous solution of electrolyte at a concentration of not lower than 0.5 % by weight, before or after, or both before and after conducting the procedure as defined in item (1). The method of the invention essentially comprises subjecting an article of fluorine-containing resin to a method as defined above in item (1). The procedure will be described below in greater detail. In this procedure, an article of fluorine-containing resin is cleaned by being brought into contact with a polar solvent or an aqueous solution of polar solvent (hereinafter referred to simply as "solvent" if not necessary). Examples of polar solvents useful in this procedure are fluorine-containing carboxylic acids represented by the formula R f COOH (wherein R f is a fluorine-containing hydrocarbon group having 3 to 20 carbon atoms, preferably 5 to 9 carbon atoms); ketones represented by the formula R 1 COR 2 (wherein R 1 and R 2 are the same or different and each represent an alkyi group having 1 to 5 carbon atoms). Stated more specifically, the article is brought into contact with the solvent as by immersion of the article in the solvent and standing, by intensively spraying the solvent over the article, or by causing the flow of the solvent or the movement of the article in order to promote the removal of particles. Such flow or movement can be brought about as by shaking the solvent in the article (in case of container), or by immersing the article (in case of container) in the solvent and stirring the solvent or subjecting the solvent to circulating movement. As the temperature of the solvent is raised during the cleaning, a higher cleaning effect is produced but with economical disadvantage. For this reason, the temperature of the solvent is usually in the range of about 35 to about 40°C. The degree of cleaning on articles of fluorine-containing resin can be also increased by performing an additional cleaning procedure at least once with ultrapure water and/or with a cleaning agent before or after or both before and after, carrying out said method. Useful cleaning agents include: (a) acids and alkali-type agents such as aqueous solutions containing at least one species selected from HF, NH 4 F, HCl, HNO 3 , H 2 O 2 , H 2 SO 4 , H 3 PO 4 and NH 3 ; and (b) organic solvents such as trichloroethylene, methyl alcohol, ethyl alcohol and isopropyl alcohol. The foregoing cleaning agents are stored in containers or tanks made of fluorine-containing resin or transported in pipes made of fluorine-containing resin for use in the field of manufacture of semiconductors. The degree of cleaning on articles of fluorine-containing resin can be also increased by conducting additional cleaning at least once with an aqueous solution of electrolyte at a high concentration (not lower than 0.5% by weight) before or after, or both before and after, performing said method. Examples of useful electrolytes are NH 4 Cl, NH 4 F, KCl, KF, NaCl, MgCl 2 , MgCO 3 , ZnCl 2 , ZnSO 4 , FeCl 3 , AlCl 3 and Al 2 (SO 4 ) 3 . The method of the present invention is suitable for removing the fine particles from the fluorine-containing resin article which must be cleaned to a great extent, particularly articles of fluorine-containing resin such as containers, tanks, pipes, tubes or wafer carriers for use in the field of manufacture of semiconductors. The following great advantages can be offered by cleaning an article of fluorine-containing resin according to the present invention. The method of the invention can produce a cleaning effect to an extent heretofore unattainable by conventional techniques, more specifically, to such level that after cleaning, 10 particles or less are contained in one milliliter of the solution held in a container of fluorine-containing resin in terms of the particles not smaller than 0.3 um in particle size, and that after cleaning, one particle or less is contained in one milliliter thereof in the container in terms of particles not smaller than 0.5 µm in particle size. Therefore the methods of the invention can meet the requirement for higher cleaning levels to be expected in the field of manufacture of semiconductors and other fields. Given below are Examples and Comparison Examples to clarify the features of the present invention in greater detail. Comparison Example 1 Two kinds of molded bottles each made of tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer (hereinafter referred to as "PFA bottle") and tetrafluoroethylene-hexafluoropropylene copolymer (hereinafter referred to as "FEP bottle"), respectively were cleaned with ultrapure water (specific resistance [MΩ·cm at 25°C]: at least 18, number of fine particles [number of particles/ml, having a size of not smaller than 0.3 µm]: 1 or less, T.O.C. [ppb]: 10 to 100, ultrapure water of this type will be also used hereinafter) in the order as shown below in Table 1. The bottles were cleaned by pouring an appropriate quantity of ultrapure water into each bottle, shaking the bottle under the conditions of vibrational amplitude of 4 cm and the number of vibration of 160 vibrations/min for 5 minutes and allowing- the bottle to stand. The number of fine particles was counted with use of a counter for counting the number of fine particles in liquid (trade name "RION KL-21", manufactured by RION Co., Ltd.**). Table 1 shows the number of fine particles present in ultrapure water and having a size of at least 0.3 µm or at least 0.5 µm after completion of each cleaning procedure. Further, a 40% aqueous solution of NH 4 F or a 50% aqueous solution of HF from which fine particles were removed beforehand by filtration using a filter (0.1 µm) was poured into the bottles for cleaning the bottles internally thereof in the same manner as above. Table 1 also shows the number of fine particles counted in this case. In the following Examples and Comparison Examples, cleaning with ultrapure water was conducted in the same manner as in this Comparison Example unless otherwise specified. Further, 40% aqueous solutions of NH 4 F and 50% aqueous solutions of HF were filtered by the same procedure as above and used in the following cleaning operations. Each value shown in the following tables and obtained using PFA bottles is the average of two data determined by actual count, and that obtained using FEP bottles is the average of three such data. Table 1 shows how the number of fine particles changes through the intermediate stages in the cleaning method using ultrapure water which is one of the conventional cleaning techniques. In the following Examples and Comparison Examples, the degree of the improvement of cleaning effect is evaluated by comparison with the results shown in Table 1. Example 1 A molded 0.5 ℓ-PFA bottle and a molded 1 ℓ-FEP bottle were internally cleaned with ultrapure water once in the same manner as in Comparison Example 1 and treated with ω-hydrocarboxylic acid [H(CF 2 CF 2 ) 3 COOH] or acetone [CH 3 COCH 3 ]. Such treatment was conducted by pouring ω-hydrocarboxylic acid or acetone into the bottle and shaking the bottle under the conditions of a vibrational amplitude of 4 cm and the number of vibration of 160 vibrations/min for 5 minutes. In order to evaluate the effect produced by the treatment with the above solvents, the bottle was further cleaned four times with ultrapure water in the same manner as in Comparison Example 1. Thereafter, a 40% aqueous solution of NH 4 F or a 50% aqueous solution of HF was used for cleaning the bottles. Table 2 shows the results. The results shown in Table 2 clearly indicate that cleaning effect is remarkably improved by cleaning the molded bottle of fluorine-containing resin with the above solvent. This is presumably because the particulate component present in the molded product of fluorine-containing resin is dissolved in the solvent and removed.

Claims: A method for removing the fine particles deposited on an article of fluorine-containing resin, the method comprising bringing the article of fluorine-containing resin into contact with a polar solvent or an aqueous solution of polar solvent, the polar solvent being at least one solvent selected from the group consisting of fluorine-containing carboxylic acids represented by the formula R f COOH, wherein R f is a fluorine-containing hydrocarbon group having 3 to 20 carbon atoms and ketones represented by the formula R 1 COR 2 , wherein R 1 and R 2 are the same or different and each represent an alkyl group having 1 to 5 carbon atoms. A method as defined in claim 1 in which the article is cleaned at least once with at least one of ultrapure water, a cleaning agent and an aqueous solution of electrolyte at a concentration of not lower than 0.5 % by weight, before or after or both before and after bringing the article into contact with a polar solvent or an aqueous solution of polar solvent.

Inventors: AOMI HIDEKI, ITANO MITSUSHI, SODA TOMIZO, AOMI, HIDEKI, ITANO, MITSUSHI, SODA, TOMIZO
Applicants: DAIKIN IND LTD, DAIKIN INDUSTRIES, LIMITED
Application year: 1990
Main classification: C08J7
IPC codes: C08J7