Resin composition based on a polyester resin, an amino resin and an epoxy resin

Abstract: The invention relates to a resin composition based on a polyester resin, an amino resin and an epoxy resin. The polyester resin is a carboxyl-functional polyester with a molecular weight of between 12000 and 25000.

Description: The invention relates to a resin composition based on a polyester resin, an amino resin and an epoxy resin. Such resin composition is already known from European patent EP-B-150476 and JP-A-54 125 230. These patent publications describe a resin compositions based on a hydroxyl-functional polyester resin, an amino resin and an epoxy resin. Said compositions are used as a binding agent for interior can coatings in the food industry. A disadvantage of these resin compositions is that can coatings based on such resin compositions have insufficient resistance to lactic acid. The object of the invention is to obtain resin compositions which give can coatings good resistance to chemicals, particularly lactic acid, and also give such coatings good flexibility. The invention is characterized in that the polyester resin is a carboxyl-functional polyester with a molecular weight of between 12000 and 25000 and a hydroxyl value of substantially zero and an acid number of between 4 and 75. By this invention resin compositions comprising a polyester resin, an amino resin and an epoxy resin are obtained which yield can coatings with good resistance to lactic acid and with a good flexibility. According to a preferred embodiment of the invention the carboxyl-functional polyester has a molecular weight of between 14000 and 17000. The acid number of the carboxyl-functional polyester is preferably between 4 and 20, more preferably between 6 and 16. The carboxyl-functional polyester is preferably the reaction product of a hydroxyl-functional polyester and an acid anhydride or a dicarboxylic acid. Suitable acid anhydrides are, for example, phthalic anhydride, tetrahydrophthalic anhydride, succinic anhydride, maleic anhydride, trimellitic anhydride, pyromellitic anhydride and/or hexahydrophthalic anhydride. Preferably, use is made of trimellitic anhydride and phthalic anhydride. Suitable dicarboxylic acids are, for example, adipic acid, isophthalic acid, hexahydroterephthalic acid and sebacic acid. Preferably, use is made of an acid anhydride. The reaction between the hydroxyl-functional polyester and the acid anhydride or the dicarboxylic acid is preferably effected in a second step after the hydroxyl-functional polyester synthesis, but the aforementioned reaction can also be effected during the curing of the resin composition. In the reaction between the hydroxyl-functional polyester and the acid anhydride or the dicarboxylic acid the molar ratio of the hydroxyl groups and the acid anhydride or dicarboxylic acid groups is preferably almost equimolar. This results in a hydroxyl value of substantially 0. The hydroxyl-functional polyester can be obtained by causing polyalcohols to react with acids or acid anhydrides. The molar ratio of the polyalcohols and the acids or acid anhydrides may vary between 1.2:1.0 and 1.0:1.0 for the preparation of the hydroxyl-functional polyester. The carboxyl-functional polyester can also be obtained directly, by causing polyalcohols to react with acids or acid anhydrides. The molar ratio of the polyalcohols and the acids or acid anhydrides may vary between 1.0:1.2 and 1.0:1.0 for the preparation of the carboxyl-functional polyester. Suitable polyalcohols for the preparation of the carboxyl- and hydroxyl-functional polyester are, for example, ethylene glycol, propylene glycol, diethylene glycol, butanediol (1,4), hexanediol (1,6), neopentyl glycol, trimethylpentanediol, ester of hydroxypivalic neopentyl glycol, tricyclodecanedimethanol, cydohexanedime-thanol, bisphenol-A-bishydroxyethyl ether, trimethylolpropane andlor pentaerythritol. Suitable acids for the preparation of the carboxyl- and hydroxyl-functional polyester are, for example, isophthalic acid, terephthalic acid (ester of dimethylterephthalic acid), adipic acid, sebacic acid, hexahydroterephthalic acid, decanedicarboxylic acid, 5-t-butylisophthalic acid andlor dimerised fatty acids or acid anhydrides such as phthalic anhydride, tetrahydrophthalic anhydride, succinic anhydride, maleic anhydride, trimellitic anhydride, pyromellitic anhydride and/or hexahydrophthalic anhydride. The esterification reaction is preferably carried out in a nitrogen atmosphere at temperatures of between 180°C and 260°C. Catalysts such as dibutyltin oxide, tinchloride or tetrabutoxy titanate, and antioxidants such as triphenyl phosphite may be used as additives. The reaction water released during the reaction is removed by distillation. The desired degree of esterification is reached by means of azeotropic distillation or vacuum in the last phase. The reaction results in a polyester that can subsequently be dissolved in an organic solvent or a mixture of solvents. Mixed aromatic hydrocarbons and esters of glycol ether, such as methylpropylene glycol acetate or ethylpropylene glycol acetate are, for example, used for this purpose. Suitable amino resins are benzoguanamine resins, melamine resins and/or urea-formaldehyde resins. Preferably, benzoguanamine resin andlor melamine resin is used as amino resin. Benzoguanamine and melamine resins can be obtained by converting benzoguanamine and melamine, respectively, into methylol compounds, with the aid of formaldehyde, and then etherifying said methylol compounds with(C 1 -C 4 ) alcohols so as to obtain the desired degree of etherification. The amount of formaldehyde per mole of amino compound varies between 2 and 4 moles in the case of benzoguanamine and between 3 and 6 moles when use is made of melamine. Alkaline conditions are usually chosen for the methylolation step. In the subsequent etherification with the aid of alcohols (preferably n-butanol or isobutanol) use is made of molar amounts of between 0.5 and 1.5 moles per mole of formaldehyde. The etherification takes place under acid conditions and the reaction water formed is removed by azeotropic distillation. As end product, a benzoguanamine resin or a melamine resin is obtained and dissolved in the alcohol used for the etherification. Optionally, the concentration and viscosity can be adjusted to the values required by distillative removal of this alcohol. Suitable epoxy resins are, for example, bisphenol-A-epoxy compounds, hydrogenated bisphenol-A-epoxy compounds and aliphatic epoxy compounds. Preferably, use is made of bisphenol-A-epoxy compounds, such as the diglycidyl ether of bisphenol-A and oligomers thereof. The resin composition according to the invention is preferably obtained by first preparing a pigment paste by mixing a carboxyl-functional polyester resin and a pigment into a paste at a temperature at or below 70°C; next cooling said paste to room temperature and adding to said cooled paste said amino resin, said epoxy resin and a catalyst The pigment is, for example, titaniumdioxide and a suitable catalyst is, for example, dodecylbenzene sulphonic acid or paratoluene sulphonic acid. The catalyst is added in amounts of less than 2 wt.%, relative to the resin composition. Optionally, use may be made of additives such as flow improvers and substrate moisturizers, such as cellulose acetobutyrate. In this preparation the weight ratio of said carboxyl-functional poylester:pigment is preferably between 2:3 and 1:1, the polyester resin : amino resin weight ratio is preferably between 60:40 and 80:20, the polyester resin : epoxy resin weight ratio is preferably between 70:30 and 80:20 and the polyester resin : (amino resin and epoxy resin) weight ratio is preferably between 50:50 and 60:40. The resin composition may be diluted with solvents, for example aromatic hydrocarbon fractions such as Solvesso 200 (trade name of Esso), methylpropylene glycol acetate (MPA) and ethyl-3-ethoxypropionate. In this manner a composition with a solids content of between 40% and 60% can be obtained. US-A-3548026 describes resin compositions based on epoxy resins and low-molecular weight carboxyl-functional polyesters which are based on a prepolyester having a molecular weight of 2000-10000. These resin compositions may optionally also contain amino resins. However, coating compositions based on these resin compositions are insufficiently flexible. The resin composition according to the invention may be applied with the aid of a roller coater to a metal substrate, for example, tin-plate, aluminium or black-plate steel, in a dry layer thickness of 8-12 µm. The enamelling cycle takes 12-15 minutes at 200°C-210°C. The resin composition according to the invention is particularly well suited for use as so-called interior white can coatings, but may also be used for, for example, coil coatings. In the examples below the following tests were used: The molecular weight was determined via gas phase chromatography (GPC) using a polyester-styrene standard. The resistance to lactic acid was determined visually in a 2% lactic acid solution after sterilization for 1 hour at 129°C. The flexibility was determined visually after punching and sterilization of a 'DSM Resins standard can'. In addition, the flexibility was measured via the so-called wedge-bend test. In this test a 'DSM Resins standard can' is conically deformed by means of an impact, after which the number of defective millimeters of the coating is determined (with a magnifier: magnification 8x). This determination takes place after immersion in a copper sulphate/hydrochloric acid solution. The aim is to obtain the lowest possible values. The above tests are described in 'Epikote Technical Bulletin EP 2.9' of Shell Chemicals. The invention is further explained by the following examples without, however, being limited thereto. Examples Example I Preparation of polyester resin 14.11 parts by weight of ethylene glycol, 25.23 parts by weight of neopentyl glycol, 37.77 parts by weight of isophthalic acid, 37.77 parts by weight of terephthalic acid and 0.05 parts by weight of tin chloride were heated, in a nitrogen atmosphere, in a glass reaction flask equipped with a mechanical stirrer, a thermometer and a Vigreux distillation column. The esterification reaction started at 180°C and the reaction water formed was removed by distillation. The maximum reaction temperature was 260°C. When the reaction mixture had become clear, it was subjected to azeotropic distillation using an aromatic hydrocarbon fraction (Solvesso 150, trade name of Esso) until an acid value of 1 was obtained. After cooling to 190°C, 166 parts by weight of phthalic anhydride were added and the reaction mixture was maintained at 190°C for 1 hour. The resin obtained was diluted to a solids content of 40% with a solvent mixture consisting of Solvesso 150, Solvesso 200 and MPA, in a weight ratio of 1:1:2. The final acid value of the solid resin was 8. The viscosity measured in an Emila with a 100 spindle, at 23°C, was 20 dPa.s. The number average molecular weight was determined by means of GPC using a polyester-styrene standard and amounted to 15,000. Example II Example of a resin composition 25.3 parts by weight of titanium dioxide (TR92 of Tioxide, LTD, UK) were added to 21.09 parts by weight of a carboxyl-functional polyester resin obtained according to Example I (dissolved in Solvesso 150, Solvesso 200 and MPA; 8.44 parts by weight of solids). This mixture was then ground to a pigment paste. During the preparation the temperature of the paste did not rise above 70°C. After cooling to room temperature, 18.37 parts by weight of polyester resin according to Example I (dissolved in Solvesso 150, Solvesso 200 and MPA; 7.35 parts by weight of solids), 9.65 parts by weight of benzoguanamine resin (dissolved in Solvesso 150, n-butanol; 7.04 parts by weight of solids) (Uramex B 70600-RB-73 of DSM Resins BV), 6.09 parts by weight of epoxy resin (dissolved in diacetone alcohol; 5.48 parts by weight of solids) (Epikote 834 of Shell Chemie BV) and 0.75 parts by weight of dodecylbenzene sulphonic acid (Nacure 5225 of King Industries) were mixed. The mixture was then diluted with isophorone to a viscosity of 100-120 seconds flow time (DIN cup 4 at 23°C, DIN standard 53211). The composition obtained was applied to tin-plate, aluminium and black-plate steel, in a layer thickness of 10 µm, using a roller coater, and subjected to an enamelling cyde of 12-15 minutes at 210°C. Example III and Comparative Experiments A-B-C Test results of resin compositions The following properties relating to mechanical strength and resistance were determined is resin compositions obtained as described in Example II: a) flexibility after punching of a can ('DSM Resins standard can'), b) flexibility after sterilization of the can (DSM Resins standard can'), c) flexibility via the wedge-bend test, and d) resistance to lactic acid. Four resin compositions (III-A-B-C) based on different polyesters were compared: III. resin composition based on a high-molecular carboxyl-functional polyester resin (molecular weight 15000), A. resin composition based on a low-molecular carboxyl-functional polyester resin (molecular weight 2200), B. resin composition based on a high-molecular hydroxyl-functional polyester resin (molecular weight 15000) and C. resin composition based on a low-molecular hydroxyl-functional polyester resin (molecular weight 2000), resin composition III A B C Mn 15000 2200 15000 2000 acid value 8 28 2 3 hydroxy value 0 0 6 22 hydroxyl value flexibility after punching xxx xxx xxx xxx flexibility after sterilization xxx x xxx x wedge-bend (mm) 35 80 30 60 resistance to lactic acid xxx xxx x x The properties 'flexibility after punching', 'flexibility after sterilization' and 'resistance to lactic acid' were visually determined: xxx = excellent; xx = satisfactory; x = unsatisfactory. The above results show that resin compositions based on carboxyl-functional polyester resins with a molecular weight of 15000, an amino resin and an epoxy resin produce excellent resistance to lactic acid combined with excellent flexibility after sterilization.

Claims: Claims for the following Contracting States : AT, BE, CH, DE, DK, FR, GB, GR, IT, LI, NL, SE Resin composition based on a polyester resin, an amino resin and an epoxy resin, characterized in that the polyester resin is a carboxyl-functional polyester with a molecular weight of between 12000 and 25000, a hydroxyl value of substantially zero and an acid number of between 4 and 75. Resin composition according to claim 1, characterized in that the carboxyl-functional polyester has a molecular weight of between 14000 and 17000. Resin compostion according to any one of claims 1-2, characterized in that the acid number of the carboxyl functional polyester in between 4 and 20. Resin composition according to any one of claims 1-3, characterized in that the carboxyl-functional polyester is the reaction product of a hydroxyl-functional polyester and an acid anhydride or a diarboxylic acid. Resin composition according to any one of claims 1-4, characterized in that the amino resin is a benzoguanamine resin and/or a melamine resin. A process for the preparation of a resin composition according to any one of claims 1-5, characterized in that said carboxyl-functional polyester resin and a pigment are mixed into a paste at a temperature at or below 70°C; next cooling said paste to room temperature and adding to said cooled paste said amino resin, said epoxy resin and catalyst. A process according to claim 6, characterized in that the weight ratio of said polyester resin to said amino resin is between 60:40 and 80:20, the weight ratio of said polyester resin to said epoxy resin is between 70:30 and 80:20 and the weight ratio of said polyester resin to total amount of said amino resin and said epoxy resin is between 50:50 and 60:40. Use of a resin composition according to any one of claims 1-4, or use of a resin composition obtained according to any one of claim 6-7. Coating or can coating based on a resin composition according to any of claims 1-4, or based on a resin composition obtained according to any one of claims 6-7. Completely or partly coated substrate, characterized in that it is coated with a coating or a can coating according to claim 9. Claims for the following Contracting State : ES A process for the preparation of a resin composition based on a polyester resin, an amino resin and an epoxy resin, characerized in that a carboxyl-functional polyester resin with a molecular weight of between 12000 and 25000, a hydroxy value of substantially zero, and an acid umber of between 4 and 75 and a pigment are mixed into a paste at a temperature at or below 70°C; next cooling said paste to room temperature and adding to said cooled paste an amino resin, an epoxy resin and a catalyst. A process according to claim 1, characterized in that the weight ratio of said carboxyl-functional polyester resin to said pigment is between 2:3 and 1:1, the weight ratio of said polyester resin to said amino resin is between 60:40 and 80:20, the weight ratio of said polyester resin to said epoxy resin is between 70:30 and 80:20 and the weight ratio of said polyester resin to the total amount of said amino resin and said epoxy resin is between 50:50 and 60:40. A process according to any one of claims 1-2, characterized in that the carboxyl-functional polyester has a molecular weight of between 14000 and 17000. A process according to any one of claims 1-3, characterized in that the acid number of the carboxyl-functional polyester is between 4 and 20. A process according to any one of claims 1-4 characterized in that the carboxyl-functional polyester is the reaction product of a hydroxyl-functional polyester and an acid anhydride or a dicarboxylic acid. A process according to any one of claims 1-5, characterized in that the amino resin is a benzoguanamine resin and/or melamine resin. A process for the preparation of a coating comprised of a carboxyl-functional polyester with a molecular weight between 12000 and 25000 a hydroxyl value of substantially zero and an acid number of between 4 and 75; an amino resin; and an epoxy resin; steps of said process comprising: mixing said carboxyl-functional polyester resin and a pigment into a paste at a temperature at or below 70°C: cooling said paste to room temperature; adding to said cooled paste said amino resin, said epoxy resin and a catalyst; diluting said coating composition with organic solvent to a viscosity of 100-120 seconds flow time. A process according to claim 7 characterized in that, the weight ratio of said carboxyl-functional polyester resin to said pigment is between 80:20 and 20:80, the weight ratio of said polyester resin to said amino resin is between 60:40 and 80:20, the weight ratio of said polyester resin to said epoxy resin is between 70:30 and 80:20, the weight ratio of said polyester resin in total amount of said amino resin and said epoxy resin is between 50:50 and 60:40. A process according to any one of claims 7-8, wherein said pigment is titanium dioxide. A process according to any one of claims 7-8 wherein said catalyst dodecylbenzene sulphonic acid or paratoluene sulphonic acid.

Inventors: BEENS-ONSTENK ANNEKE, HARDEMAN GERARD, PLAK ANTHONIE JOHANNES, WESTERHOF WILHELMINA, BEENS-ONSTENK, ANNEKE, HARDEMAN, GERARD, PLAK, ANTHONIE JOHANNES, WESTERHOF, WILHELMINA
Applicants: DSM NV, DSM N.V.
Application year: 1990
Main classification: C09D167
IPC codes: C09D163, C09D167, C08L67, C09D161