Planar plastics optical waveguide

Abstract: A plate plastics optical waveguide comprises a core portion (3) composed of a polymer containing a deuteriumation or a halogen atom, and a clad portion (2, 7) which surrounds the core portion and composed of a polymer having a refractive index lower than that of the core portion. The plastics optical waveguide which has a core portion comprising a deuterated or halogenated polyacrylate or polysiloxane shows an optical loss of 0.1 dB/cm or less for a light at a wavelength of 1.3 µm.

Description: The present invention relates to a planar plastics optical waveguide, more particularly to a planar plastics optical waveguide useful as optical components such as optical couplers or multiplexers for optical communication or image transmission. As for a base material for optical components or optical fibers, generally inorganic substances such as silica glass and multicomponent glass are used because their propagation loss is low and their transmission band is wide. On the other hand, optical components using plastics as a base material have been developed. Plastics optical materials used therefore have a good fabrication flexibility and the controllability of optical properties compared with inorganic optical materials, and therefore, much attention has been paid thereon with an expectation that optical waveguides having relatively good characteristics could be produced with ease using them. Representative techniques for producing of planar plastics optical waveguides include a selective photopolymerization and a utilization of a photosensitive resin. The selective photopolymerization method is a technique in which monomers contained in a polymer are selectively polymerized to change the refractive index to make a pattern-like optical waveguide. More particularly, at first a mask having a predetermined pattern is mounted on a polymer sheet or substrate composed of a transparent polymer such as polycarbonate which contains a low refractive index monomer such as methyl acrylate, and the sheet or substrate are irradiated with ultraviolet rays through the mask to selectively polymerize the low refractive index monomer in accordance with the pattern. The photopolymerized portion of the polymer has a lower refractive index than the polymer matrix. Then the polymer sheet is heated in vacuum to remove unreacted monomers which remain in areas unexposed with ultraviolet rays. As a result, unexposed portion of the polymer consists of the high refractive index polymer alone. Thus, a patterned sheet can be obtained in which a high refractive index portion serving as a core is formed in accordance with a predetermined pattern. Finally, the patterned sheet is sandwiched by a cladding composed of a low refractive index polymer to produce an objective optical part. On the other hand, according to the method which uses a photosensitive polymer, a photosensitive polymer is pattern-wise exposed to a light to cause crosslinking selectively, followed by development to remove unexposed portion to obtain a core pattern. More particularly, at first a polymer serving as a cladding is coated on a substrate by dipping or spin coating. A polymer such as polyurethane containing a photosensitive crosslinking agent is coated on the cladding in the same manner as above. Then, the coated polymer is irradiated with ultraviolet rays through a patterned mask to selectively crosslink the polymer. Next, the substrate is immersed in a solvent to remove the unexposed portion to obtain a core having a predetermined pattern. Finally, a cladding material is provided on the core by dipping, spin coating or laminating to form a cladding, so that the required optical part is produced. In order to obtain practically useful optical parts which shows a low optical loss, it is required that a film for transmitting a light is of a good quality and patterns formed by microprocessing have a high reliability. That is, it is preferred that the material of the film itself show as low as possible an optical loss, and the thickness and refractive index of the film made of the material can be controlled with a high precision. And further, smoothness of side walls of the core, dimensional stability and reproducibility are important factors for the microprocessing of the waveguide fabrication. In the case where a plastics material is used, optical parts produced by the selective photopolymerization method and the method using a photosensitive polymer, respectively, show a relatively low optical loss at a shorter wavelength (0.48 to 1.1 µm). However, they show a high optical loss as high as 0.5 to 10 dB/cm in the infrared region (1.3 to 1.55 µm), utilized in optical communication at present, because of higher harmonics of infrared vibrational absorptions due to the carbon-to-hydrogen bonds constituting the plastics, and therefore they are unsuitable for practical use. From the standpoint of fabrication flexibility of optical waveguides, both methods are simpler and easier than production of glass optical waveguides. However, the selective photopolymerization method has some problems, for example that the content of the monomer varies depending on the conditions of evaporation of the solvent which causes subtle fluctuation of the refractive index difference. On the other hand, the method using a photosensitive polymer has a problem that resolution is poor and that protrusions and depressions tend to occur on the surface of the optical waveguide due to swelling upon development. These are the reasons why the conventional plastics optical waveguides show high optical losses. A problem with which the present invention is concerned is the provision of a planar plastics optical waveguide which shows a low optical loss in the visible to infrared region. In the first aspect of the present invention, a planar plastics optical waveguide comprises: a core portion composed of a polyacrylate having a refractive index and having at least one kind of repeating unit represented by formula (I): and further comprising a cladding portion surrounding the core portion and being composed of a polymer having a refractive index which is lower than the refractive index of the core portion, characterised in that (a) the polyacrylate is deuterated and halogenated; and (b) in the repeating unit of formula (I) each of X 1 and X 2 is a deuterium atom or a halogen atom; R 1 is selected from the group consisting of a deuterium atom, a CD 3 group, and a halogen atom; and R 2 is a halogenated or deuterated alkyl group of formula C n Y 2n+1 in which Y is a halogen atom or a deuterium atom, and n is an integer from 1 to 5, and (c) deuterium atom(s) and halogen atom(s) coexist in said repeating unit. A paper by Isamu Kato et al, "Polymer Thin Film Optical Waveguide", Electronics and Communications in Japan, Vol. 65-C, No. 11, 1982 discloses a planar optical waveguide fabricated with a core and cladding of polymer material with the cladding having a refractive index lower than that of the core. Single-mode optical waveguides with various widths were fabricated and their optical loss was measured. EP-A-0186106 is concerned with a process for the production of deuterated methyl methacrylate and deuterated methylacrylate which when used in optical fibres are stated to be better in their capacity to transmit light than their undeuterated counterparts. The core portion may be composed of a copolymer of deuterated or halogenated acrylates, and the copolymer may have at least two different repeating units respectively represented by the foregoing formula (I). The cladding portion may be composed a polymer having a deuterium atom or a halogen atom. It may be composed a deuterated or halogenated polyacrylate having a repeating unit represented by the following formula (I): wherein each of X 1 and X 2 is a deuterium atom or a halogen atom; R 1 is selected from the group consisting of a heavy hydrogen atom, a CD 3 group and a halogen atom; and R 2 is a halogenated or deuterated alkyl group of formula: C n Y 2n+1 (where Y is a halogen atom or a deuterium atom; n is an integer from 1 to 5). The cladding portion may be composed of copolymer of a deuterated or halogenated acrylates, the copolymer may have at least two different repeating units represented by the foregoing formula (I), respectively: The cladding portion may be composed of a deuterated or halogenated polysiloxane having a repeating unit represented by the following formula (II) or (III): wherein each of R 3 and R 4 is a group of formula C n Y 2n+1 (where Y is a halogen atom or a heavy hydrogen atom; n is one integer of 1 to 5) or C 6 Y 5 . The cladding portion may be composed of a copolymer of deuterated or halogenated siloxanes, the copolymer may have at least two different repeating units represented by the foregoing formula (II), respectively, or at least two different repeating units represented by the foregoing formula (III), respectively: the clad portion may be composed of a copolymer having the foregoing repeated units (II) and (III). The planar plastics optical waveguide may comprise a substrate, a lower cladding portion made of a first polymer and provided on the substrate; a core portion provided on the lower cladding portion; and an upper cladding portion made of the first polymer, the upper cladding portion being provided on the core portion and surrounding the core portion together with the lower cladding portion, the core and cladding portions being as described above. Here, the first polymer constituting the lower and upper cladding portions may be composed of homopolymer or copolymer of deuterated or halogenated acrylates or deuterated or halogenated siloxanes. The above and other objects, effects, features and advantages of the present invention will become more apparent from the following description of embodiments thereof taken in conjunction with the accompanying drawings. Figs. 1A to 1G are schematic cross-sectional views of a plastics optical waveguide according to the present invention for explaining an example of process for producing thereof; Fig. 2 is a characteristic graph illustrating of the refractive index of polyacrylate on the fluorine content thereof; and Fig. 3 is a characteristic graph illustrating the optical loss dependence of the plastics optical waveguide according to the present invention on the wavelength. The most important factor for optical loss of plastics is higher harmonics of infrared vibrational absorption due to the carbon-to-hydrogen bonds constituting the plastics: In the plastics optical waveguide of the present invention, the hydrogen atoms in the structure of the plastics are substituted with a halogen atom such as fluorine, chlorine and iodine or a deuterium atom in order to reduce the higher harmonics due to the carbon-to-hydrogen bonds and shift them to a longer wavelength region. The substitution enables reduction of optical loss of the material itself and makes optical waveguides produced using the material to have a high performance. Such optical waveguides as described above can be produced by providing a substrate, forming a plastics film on the substrate, further forming a pattern of photoresist on the plastics film by lithography, and dry etching the substrate in an oxygen- or fluorine-containing gas using the patterned photoresist as a mask. More particularly, a photoresist is coated on a sheet of polymer to be processed and irradiated with actinic rays such as ultraviolet rays, electron beams, and X rays pattern-wise or image-wise. Next, the polymer sheet is immersed in a solvent to develop it to obtain a pattern. The resulting pattern is used as a mask when the underlying polymer is subjected to reactive dry etching in a fluorine- or oxygen-containing gas in order to transfer the pattern to the polymer sheet. While the plastics optical waveguides of the present invention can be produced by combination of the above-described steps, a representative processing procedure will be explained hereinafter referring to Figs. 1A through 1G. At first, a cladding material is coated on a substrate 1 to form a layer-like cladding 2 (Fig. 1A). Then, a core material composed of an organic polymer is coated on the cladding 2 to form a core layer 3 (Fig. 1B). Next, as illustrated in Fig. 1C, a silicone-based photoresist 4 is coated on the core layer 3, and exposed to actinic rays through a mask 5, followed by development to obtain a mask pattern (Fig. 1D). Further, reactive ion etching using oxygen gas is carried out to remove the core layer 3 in a region other than the patterned portion (Fig. 1E). The photoresist is peeled off (Fig. 1F), and a cladding material 7 which has the same composition as the cladding 2 is coated or laminated thereon (Fig. 1G). This production method is advantageous in that patterns of a high resolution and high dimensional stability with steep and smooth side walls can be obtained by the use of reactive ion etching in fewer steps with excellent reproducibility. From the viewpoint of mass production, it is also advantageous to use a method in which a plurality of optical waveguides are made on a substrate of a large surface area simultaneously and fabricated by using a stamper or metal mold. As is well known, optical waveguides are designed to propagate light in the core utilizing difference in refractive index between their cores and claddings. In the case of plastics optical waveguides, difference in refractive index can be generated by the use of different types of plastics in the core and cladding, respectively. Alternatively, the refractive index of the core and/or cladding can be controlled by the content of fluorine in the polymer or polymers. Fig. 2 illustrates variation of the refractive index of a copolymer of a deuterated heptafluoroisopropyl methacrylate with a deuterated methyl methacrylate depending on the fluorine content in the polymer. In Fig. 2, lines A and B indicate refractive indices for lights at wavelengths of 0.6328 µm and 1.5230 µm, respectively. In the both cases, the refractive indices decrease linearly with increase of the fluorine content. Now the present invention will be explained with reference to specific embodiments. Embodiment 1 A monomer mixture composed of 20% by mole of heptafluoroisopropyl methacrylate d-5, which is a monomer whose five hydrogen atoms were each substituted with a deuterium atom, and 80% by mole of perdeuteromethyl methacrylate, which is a monomer all the hydrogen atoms of that were each substituted with a deuterium atom, was polymerized using 2,2'-azobisisobutyronitrile (AIBN) as a polymerization initiator to obtain a copolymer (refractive index: n = 1.46). Separately, heptafluoroisopropyl methacrylate d-5 was polymerized using AIBN as a polymerization initiator to obtain a homopolymer (n = 1.37). Then, an optical waveguide was produced using the copolymer as a core material and the homopolymer as a cladding material as follows. At first, the two polymers were dissolved separately in 1,3-bis(trifluoromethyl)benzene to obtain two solutions, i.e., core component polymer solution and a cladding component polymer solution. The cladding component polymer solution was coated to form a layer having a dry thickness of about 10 µm on a silicon substrate. The coated substrate was heated to 90°C to dry the coated layer, and then the core component polymer solution was coated on the cladding component polymer to have a dry thickness of about 8 µm. Next, a silicone-based photoresist was coated on the core component polymer. The thus-coated substrate was exposed to actinic rays and developed to form a resist pattern. Further, reactive ion etching with oxygen gas was performed to remove the core component polymer other than the pattern portion to give a linear, rectangular pattern of a size of 50 mm long, 8 µm wide and 8 µm high. The photoresist thus obtained was immersed in an alkali solution to peel off the photoresist. Finally, a cladding layer was coated which had the same composition as the underlying cladding layer (lower cladding layer) to form an upper cladding layer. The thickness of upper cladding layer on the core was 10 µm. The optical waveguide thus obtained was irradiated with light at one end thereof and amount of light launched from the other end was measured. From the results of the measurement the optical loss of the optical waveguide was calculated. Fig. 3 illustrates dependence of the optical loss on the wavelength of light used. The optical loss of the optical waveguide was 0.1 dB/cm or less at a wavelength of 1.3 µm. Embodiment 2 An optical waveguide was produced using the same two polymers as used in Example 1 but by a different method. That is, the two polymers were separately dissolved in 1,3-bis(trifluoromethyl)benzene to obtain two polymer solutions, i.e., a cladding component polymer solution and a core component polymer solution. The cladding component polymer solution was coated on a silicon substrate to form a cladding layer having a dry thickness of about 15 µm . After drying, a silicone photoresist was coated on the cladding and exposed to actinic rays and developed. The thustreated coated substrate was subjected to reactive ion etching with oxygen gas to provide in the cladding a groove of 8 µm wide and 6 µm deep. Next, the photoresist was peeled off and the core component polymer solution was coated on the etched cladding to form a layer having a dry thickness of 10 µm. Then, back etching was carried out by reactive ion etching with oxygen gas to remove the core component polymer outside the groove. Finally, the same cladding component polymer solution as that used for making the first, lower, cladding layer was coated thereon. By the above-described procedures, an optical waveguide was obtained which had a core with a linear rectangular pattern of 50 mm long, 8 µm wide and 6 µm high. A light with a wavelength of 1.3 µm was inputted from one end of the optical waveguide and amount of light launched from the other end was measured and the optical loss of the optical waveguide was calculated based on the results of the measurement. The optical waveguide had an optical loss of 0.1dB/cm or less. Embodiment 3 Various plastics optical waveguides were produced in the same manner as in Example 1 or 2 using as a core and a cladding polyacrylates having a repeating unit represented by the following formula (I) but having different compositions as shown in Table 1 : wherein each of X 1 and X 2 is a deuterium atom or a halogen atom; R 1 is selected from the group consisting of a deuterium atom, a CD 3 group and a halogen atom; and R 2 is a halogenated or dueterated alkyl group of formula: C n Y 2n+1 (where Y is a halogen atom or a deuterium atom; n is one integer of/to 5). Table 1 shows chemical structures of the polymers used as cores and claddings of the optical waveguides and their optical losses for a light having a wavelength of 1.5 µm. The optical loss of each optical waveguide was very low, i.e., as low as from 0.04 to 0.11 dB/cm. Structure of Optical Waveguide Chemical Structure of Polymer Optical Loss (dB/cm) X 1 X 2 R 1 R 2 Cladding D D CD 3 (CF 3 ) 2 CF 0.1 Core D D CD 3 (CF 2 Cl) 2 CF Cladding D D CD 3 (CF 3 ) 2 CF 0.09 Core D D CD 3 (CF 3 ) (CF 2 Cl) CF Cladding D D F (CF 3 ) 2 CF 0.06 Core D D D (CF 3 ) 2 CF Cladding F F F (CF 3 ) 2 CF 0.04 Core D D F (CF 3 ) 2 CF Cladding D D CD 3 (CF 3 ) 2 CF 0.11 Core D D CD 3 (CF 3 ) 2 CD Cladding D D CD 3 (CD 3 ) 2 CF 0.05 Core D D CD 3 CD 2 CF 3 Cladding D D CD 3 CF 3 (CF 2 ) 3 CD 2 0.09 Core D D CD 3 (CF 3 ) 2 CF Copolymers, which have at least two different repeating units each represented by the foregoing formula (I), of deuterated or halogenated acrylates can be used as a material for the core portion and the cladding portion. As described above the plate plastics optical waveguide of the present invention has superior light transmission characteristics in a region of from visible to near infrared region to the conventional ones. Particularly, because it shows a low optical loss in a wavelength region of from 650 to 1,600 nm, the planar plastics optical waveguide of the present invention can be connected to multicomponent glass or silica optical fiber without resort to light/electricity conversion or electricity/light conversion. Therefore, it has an advantage that optical parts produced by using the optical waveguide of the present invention can be used for constructing highly economical optical signal transmission systems such a local area networks and the like. The invention has been described in detail with respect to embodiments, and it will now be apparent from the foregoing to those skilled in the art that changes and modifications may be made without departing from the invention in its broader aspects, and it is the intention, therefore, in the appended claims to cover all such changes and modifications as fall within the invention.

Claims: A planar plastics optical waveguide, comprising: a core portion (3) composed of a polyacrylate having a refractive index and having at least one kind of repeating unit represented by formula (I): and further comprising a cladding portion (2,7) surrounding the core portion (3) and beihg composed of a polymer having a refractive index which is lower than the refractive index of the core portion (3), characterised in that (a) the polyacrylate is deuterated and halogenated; (b) in the repeating unit of formula (I) each of X 1 and X 2 is a deuterium atom or a halogen atom; R 1 is selected from the group consisting of a deuterium atom, a CD 3 group, and a halogen atom; and R 2 is a halogenated or deuterated alkyl group of formula C n Y 2n+1 in which Y is a halogen atom or a deuterium atom, and n is an integer from 1 to 5; and (c) deuterium atom(s) and halogen atom(s) coexist in said repeating unit. The planar plastics optical waveguide as claimed in claim 1, wherein the core portion (3) is composed of a homopolymer of a deuterated and halogenated acrylate having the repeating unit represented by formula (I). The waveguide claimed in claim 2, wherein the core portion is composed of a copolymer of deuterated and halogenated acrylates, the copolymer having at least two different kinds of repeating units respectively represented by formula (I). The waveguide claimed in claim 1, 2 or 3, wherein the cladding portion (2,7) is composed of a deuterated and halogenated polyacrylate having at least one kind of repeating unit represented by formula (I): wherein each of X 1 and X 2 is a deuterium atom or a halogen atom; R 1 is selected from the group consisting of a deuterium atom, a CD 3 group and a halogen atom; and R 2 is a halogenated or deuterated alkyl group of formula C n Y 2n+1 in which Y is a halogen atom or a deuterium atom, and n is an integer of 1 to 5, and further wherein deuterium atom(s) and halogen atom(s) coexist in said repeating unit. The waveguide claimed in claim 4, wherein the cladding portion (2,7) is composed of a homopolymer of the deuterated and halogenated polyacrylate having the repeating unit represented by formula (I). The waveguide claimed in claim 5, wherein the cladding portion (2,7) is composed of a copolymer of the deuterated and halogenated polyacrylate, the copolymer having at least two different kinds of repeating units respectively represented by formula (I). The waveguide of any preceding claim, comprising a substrate, a lower cladding portion made of a first polymer and provided on the substrate, a core portion provided on the lower cladding portion, and an upper cladding portion made of the first polymer and provided on the core portion, the upper cladding portion together with the lower cladding portion surrounding the core portion, and the polymers of the core and cladding portions being as set out in claim 1.

Inventors: IMAMURA SABURO, IZAWA TATSUO, IMAMURA, SABURO, IZAWA, TATSUO
Applicants: NIPPON TELEGRAPH & TELEPHONE, NIPPON TELEGRAPH AND TELEPHONE CORPORATION
Application year: 1990
Main classification: G02B6
IPC codes: G02B6