PROCESS FOR PREPARATION OF A PROCATALYST COMPOSITION FOR POLYMERIZATION OF OLEFINS AND USE OF THE COMPOSITION

Abstract: The invention relates to a process for preparation of a procatalyst for polymerization of olefins wherein a metal-containing complex compound or mixture of compounds is applicated into a porous, particulate carrier and is chlorinated with a suitable chlorinating agent. The invention also relates to the use of the prepared procatalyst composition together with a co-catalyst for polymerization or copolymerization of olefins. The invention is characterized in that magnesium or its compound, a titanium compound, aluminum or its compound and, optionally, a compound comprising a hydroxyl group are reacted with each other so that an alkoxide or alkylalkoxide solution containing said metals in an inert solvent is obtained, which solution is impregnated into the carrier at a single step, whereafter the extra solvent is removed. The carrier can be an inorganic oxide such as silica, from which the free hydroxyl groups have been removed, magnesium, titanium and aluminum compounds can be organic, the compound comprising a hydroxyl group can be an alcohol and the chlorination agent can be e.g. a suitable organic aluminum-chloride. The impregnated solution according to the invention can be provided by a simple mixing and the morphology and polymerization activity of the obtained procatalyst composition have proved to be good.

Description: Process for preparation of a procatalyst composition for polymerization of olefins and use of the composition The invention relates to a process for preparation of a procatalyst composition for polymerization of olefins, wherein a metal-containing complex compound or mixture of compounds is applicated into a porous particulate carrier and chlorinated with a suitable chlorinating agent. The invention also relates to the use of such a procatalyst composition together with a co-catalyst for polymerization or co-polymerization of olefins. In polymerization of olefins Ziegler-Natta catalyst system generally is used consisting of a so called procatalyst and a co-catalyst. The procatalyst is a component based on a compound of a transition metal belonging to some of the groups IVB-VIII of the periodic system of the elements. The co-catalyst in turn is a component based on an organic metal compound of a metal belonging to some of the groups IA-IIIA of the periodic system of the elements. The catalyst system usually also contains electron donating compounds which improve and modify the catalytical properties. It is known to make use in the preparation of heterogenic polymerization catalysts as a component enhancing the poly¬ merization activity of the procatalysts a carrier compound, on which the transition metal is superposed. The usual carrier compounds are based on silica, aluminum oxide, magnesium oxide, titanium oxide, a mixture thereof, carbon in different forms, and different types of polymers. Impor¬ tant carrier compounds also include magnesium compounds such as alkoxides, hydroxides, hydroxy halides and halides, especially magnesium chloride. Since the magnesium compounds and in particular magnesium halides are not activated very efficiently in their base crystal form with a transition metal compound their crystal form has to be deformed. Traditionally the deformation of the crystal structure has been carried out by grinding, for example, in a ball mill resulting in a finely divided powder with strongly deformed crystal lattices. Drawbacks include, anyhow, that the grinding is very energy consuming, causes wearing and corrosion of the apparatus, and is suited to the production of catalyst only with the tedious batch process. An alternative method for obtaining a deformed or amorphous crystal structure of a magnesium compound is to superpose the magnesium compound, the transition metal compound and optionally an electron donor into an essentially inert carrier. Such a process is explained, for example, in U.S. Patent No. 4,363,746, where in one embodiment untreated silica is reacted with a complex of magnesium chloride and a transition metal alcoholate, the obtained product is reacted with an organic aluminum compound such as an organic aluminum halide, and finally the obtained solid intermediate is activated with a transition metal halide. Same kind of technique is represented in U.S. Patent No. 4,391,736, which relates to removing of the hydroxy groups of a silica-type carrier by organic metal compounds such as an organic aluminum halide, reacting the obtained carrier containing no hydroxyls with a magnesium dihalide tetraalkyl titanate complex and activating of the obtained solid reac¬ tion product with titanium tetrahalide, and WO Patent Appli¬ cation No. 89/02446, which relates to the same type of process, wherein the surface hydroxy groups of silica are removed with the aid of a halide or an organic silicon compound. The mentioned three specifications describe the preparation of a solid procatalyst composition in two titanation steps. These steps are very difficult and. e.g. sensitive to impuri¬ ties. A third method to provide a deformed crystal structure of magnesium compounds such as a magnesium halide and thereby to add its capability to become activated by transition metal compounds is to modify it chemically. Then a magnesium compound, an electron donor and a transition metal compound are reacted with each other, often in solution, to a proca¬ talyst composition which is separated. The composition is easily precipitated, but a drawback is that the morphology of the composition is difficult to control. An example of the above method is Japanese Patent No. 88/69806, which describes the forming from magnesium and titanium alkoxides of a homogenic hydrocarbon solution where magnesium and titanium are present as a soluble complex. When a chlorinating agent, i.e. silicon tetrachloride, is added to the solution a procatalyst is separated from the composition as a solid product. In U.S. Patent No. 4,804,726 a similar method is described where a homogenic hydrocarbon solution is formed containing alcohol, iodine, magnesium added as metallic, and titanium alkoxide. As a chlorination agent an organic aluminum chloride is used which provides the separation of the procatalyst composition as a solid product. In some patents of which as an example U.S. Patent No. 4,783,512 can be mentioned, a method is described wherein a hydrocarbon solution containing magnesium, aluminum and alcohol is first formed. To this solution titanium tetra- butoxide and thereafter ethylaluminum sesquichloride is added. As a result a suspensed product is obtained which is suitable as a catalyst for polymerization of ethylene. A separate carrier is then not needed in this process, nor in the previous methods based on chemical modifying. The purpose of this invention is to provide a process, whereby the previously mentioned type of procatalyst compo¬ sition comprising magnesium, titanum and aluminum can be prepared even more simply than before by applying the compo- sition on a porous particulate carrier. The process accor¬ ding to the invention is characterized in that magnesium or its compound, a titanium compound, aluminum or its com¬ pound and a compound comprising a hydroxyl group, optional¬ ly, are reacted with each other so that an alkσxide or alkylalkoxide solution containing said metals in an inert solvent is obtained, which solution is impregnated in a single step into a carrier, whereafter extra solvent is removed. Above all the process according to the invention has as advantage the simplicity of the preparation of the compo¬ sition. The impregnating solution can be prepared simply by mixing the components of the solution with each other at room temperature. The impregnating does not need special procedures, and because the extra solvent can be collected and reused, the process will not produce any kind of waste either. The invention is essentially based on the observation that the components contained in the procatalyst composition can be brought as a stable alkoxide or alkylalkoxide complex by simple mixing into a low viscosity solution. The solution can be prepared e.g. by adding to an aluminum compound which has been dissolved to an inert solvent a compound comprising a hydroxyl group such as an alcohol and the other of the two mentioned metallic compounds and by adding thereafter to the obtained solution the other of the mentioned other metallic compounds. The order of addition can, anyhow, be whatever provided that the titanium compound is not reduced during the process. E.g., if an aluminum compound such as triethylaluminum or a magnesium compound such as butyloctyl- magnesium is added after the titanium compound, the compound comprising a hydroxyl group must be added to the solution before the aluminum or magnesium compound. The experiments performed show that the ethylene polymeriz¬ ation activity of a procatalyst composition prepared accor¬ ding the invention is high compared with the catalysts known before where the carrier has been silica. The composition in particle form prepared according to the invention has excellent morphology, as has the polyethylene obtained in the polymerization. The carrier used according to the invention can essentially be of whatever porous inorganic or organic material consis¬ ting of finely divided particles. Most preferred are anyhow inorganic oxides such as silicon oxide, aluminum oxide, magnesium oxide or titanium oxide from which the free hydro- xyl groups on the surface have been removed thermally and/or chemically. The thermal treatment is by lower temperatures directed to removal of water and by higher temperatures to calcination of surface hydroxyls. The thermal treatment is preferably carried out at a temperature of about 150-1000°C. The chemical removal of surface hydroxyl groups of a carrier can be conducted by using materials reacting with hydroxyl groups. Such materials include organic silicon, aluminum, zinc, phosphorus and/or fluorine compounds. As an example of the preferred organic silicon compounds hexamethyldisila- zane and as an example of the preferred organic aluminum compounds triethylaluminum can be mentioned. The magnesium compound used in the process according to the invention can be an organic magnesium compound such as a magnesium alkyl, alkoxide or alkylalkoxide, e.g. butyl- octylmagnesium, the titanium compound can be a titanium- alkoxide such as titanium butoxide, the aluminum compound can be an organic aluminum compound such as aluminumalkyl, alkoxide or oxane, e.g. triethylaluminum or tetraisobutyl- aluminiumoxane, and the compound comprising a hydroxyl group which forms alkoxides can be an alcohol such as ethanol or 1-butanol. The inert solvent used according to the invention is prefe¬ rably a hydrocarbon such as, e.g., pentane or heptane or a mixture thereof. The removal of the solvent after the imp¬ regnating stage can be performed simply by evaporation. In the chlorination step, following the impregnation of the carrier particles, as chlorinating agent can preferably be used e.g. a suitable organic aluminumchloride such as ethy- laluminumsesquichloride. Chlorine compounds containing silicon or phosphorus, hydrogen chloride or gaseous chlorine are also possible. The chlorine-containing titanium com¬ pounds used earlier are not necessarily needed in the pro¬ cess according to the invention. The invention also relates to the use of a procatalyst composition prepared according to the above process together with a co-catalyst for polymerization or co-polymerization of olefins such as ethylene. As suitable co-catalysts or¬ ganic aluminum compounds such as, e.g., triethylaluminum can be mentioned. The invention is explained in the following in more detail through performing examples. In these examples the used polymerization process and pre- treatment of the carrier before the impregnating are ex¬ plained. Then follow the examples of preparation of the procatalyst composition and its use in polymerization of ethylene, the results of which are represented in table 1 following the examples. Polymerization procedure I. A 3 L reactor was purged with an inert gas-flow (nitrogen or argon) and it was charged with 2.1 L of n-pentane. To this 20-50 mg of procatalyst was added as a slurry in 20 mL of n-pentane with mixing from a to 3 bars pressurized feeding funnel. The temperature was thereafter raised to 90°C and was kept there during the hole polymerization process. A 500 mL vessel was pressurized with hydrogen to a pressure of 5 bars. Hydrogen and a 10 wt-% solution of triethyl¬ aluminum in pentane as co-catalyst and ethylene gas were fed into the reactor. The total pressure was raised to 15 bars and was kept there by a continuous feed of ethylene gas. The polymerization was continued for 1 hr. 1 ppm antioxidant was added to the slurry of polyethylene and pentane, and pentane was evaporated on standing of the slurry. II. The copolymerization of ethylene and α-olefins was performed according to step I above. The reactor was charged with 1800 mL of n-pentane and after the addition of the catalyst slurry 300 mL of 4-methyl-l-pentene acting as a co-monomer was added. Pre-treat ent of the carrier A. 1.38 mL of hexeunethyldisilazane was added with stirring at room temperature to a slurry of 10.6 g silica (W. R. Grace & Co., Davison Grade 955, dehydrated and calcinated at a temperature of 600°C) in 80 mL of heptane. The slurry was kept with stirring at a temperature of 90°C for 1 hr, and the solvent was then removed by purging with a stream of nitrogen for 2.5 hrs and by raising the temperature during this time in stages to 110°C. The obtained product was a dry free flowing white powder. B. 1.88 mL of hexamethyldisilazane was added with stirring at room temperature to a slurry of 10.0 g silica (dehydrated and calcinated at a temperature of 600°C) in 80 mL of heptane. The slurry was kept with stirring at a temperature of 90°C for 1 hr, and the solvent was then removed by purging with a stream of nitrogen for 2.5 hrs and by raising the temperature during this time in stages to 110°C. The obtained product was a dry free flowing white powder. C. 1.01 mL of hexamethyldisilazane was added with stirring at room temperature to a slurry of 10.8 g silica (dehydrated and calcinated at a temperature of 800°C) in 80 mL of heptane. The slurry was kept with stirring at a temperature of 90°C for 1 hr, and the solvent was then removed by purging with a stream of nitrogen for 2.5 hrs and by raising the temperature during this time in stages to 110 β C. The obtained product was a dry free-flowing white powder. D. 4.5 mL of hexamethyldisilazane was added with stirring at room temperature to a slurry of 10.0 g of undehydrated silica in 50 mL of pentane. The slurry was kept with stirring at a temperature of 30°C, and the solvent was then removed by purging with a stream of nitrogen for 2.5 hrs and by raising the temperature during this time in stages to 110°C. The obtained product was a dry free- flowing white powder. E. 8.55 mL of triethylaluminum was added with stirring at room temperature to a slurry of 10.0 g silica (dehydrated and calcinated with a peak temperature of 600°C) in 80 mL of pentane. The slurry was stirred further at room tempera¬ ture for the following 3 hrs. The solvent was removed thereafter by purging it with dry nitrogen and by raising the temperature during this time in stages to 80°C. Preparation of the procatalyst composition and polymeriza¬ tion experiments Example 1 la. Preparation of Mq.Al(OBu)4^ A 50 mL sealed bottle equipped with a magnetic stirrer was charged with 17.8 mL of a 10 wt% solution of triethylalumi¬ num in pentane, to which 3.66 mL of 1-butanol was added at room temperature over a period of 30 min. Thereafter 5.71 ml of a 20 wt% solution of butyloctylmagnesium in heptane was added at a temperature of 5°C over a period of 20 min. The total volume of the solution obtained was corrected to 30 mL by addition of heptane. lb. Impregnating of the carrier A 50 mL sealed bottle equipped with a magnetic stirrer was charged with 2.00 g of silica treated with hexamethyl¬ disilazane according to step A, to which 10 mL of pentane, 6.0 mL of a solution prepared according to step la and 0.343 mL of titaniumtetrabutoxide was added, and the slurry was stirred at room temperature for 15 min before drying of the bottle by purging with a stream of argon over 2.75 hrs at a temperature of at most 80°C. As result a dry white free flowing powder was obtained. lc. Chlorination step A 30 mL sealed bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to step lb, and with 4.0 L of pentane. 1.9 mL of a 10 wt% solution of ethylaluminumsesquichloride in pentane was added, and the slurry was stirred at room temperature for 1 hr. Thereafter the solvent was removed by purging the bottle with a stream of argon for 45 min and by raising the temperature during this time in stages to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 5.6 % Al, 9.0 % Cl, 0.77 % Mg and 1.1 % Ti. Id. Test polymerization Ethylene was polymerized according to step I above using 100 mg of the powder prepared according to step lc and 5.0 mL of a 10% solution of triethylaluminum in pentane as a co-catalyst. The results of the polymerization are shown in the table below. Example 2 2a. Preparation of the solution A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 10.67 mL of a 10 wt% solution of triethylalu¬ minum in pentane and with 3.43 mL of a 20 wt% solution of butyloctylmagnesiu in heptane. 1.40 mL of ethanol was added at room temperature over a period of 30 min. To the solution obtained 0.343 mL titaniumtetrabutoxide was added, which likewise was completely solved. 2b. Impregnating of the carrier A 50 mL sealed bottle equipped with a magnetic stirrer was charged with 2.0 g of silica which had been treated with hexamethyldisilazane and 10 mL of pentane. The solution prepared according to step 2a was added and the slurry was stirred at room temperature for 15 min before drying the bottle by purging through it a stream of argon for 2.75 hrs, during which time the temperature was raised in steps to 80°C. As result a dry free flowing white powder was obtained. 2c. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to step 2b and 4.0 mL of pentane. 2.6 mL of a 10 wt% solution of ethylaluminumsesquichloride in pentane was added, .and the slurry was stirred at room temperature for 2 hrs. Thereafter the solvent was removed by purging with gas for 45 min, during which time the temperature was gradually raised to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 8.5 % Al, 11.2 % Cl, 1.5 % Mg and 1.1 % Ti. 2d. Test polymerization Ethylene was polymerized according to the method of step I using 50 mg of the powder prepared according to step 2c and 2.5 mL of a 10% solution of triethylaluminum in pentane as a co-catalyst. The results of the polymerization are showed in the table below. Example 3 3a. Preparation of the solution A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 8.89 mL of a 10 wt% solution of triethylalumi¬ num in pentane, and to this 2.29 mL of 1-butanol was added at room temperature over a period of 30 min. 1.71 mL of titaniumtetrabutoxide was added and thereafter 5.71 mL of a 20 wt% solution of butyloctylmagnesium in heptane at a temperature of 5°C:n over a period of 20 min. The volume of the obtained solution was added to 20 mL by addition of heptane. 3b. Impregnation of the solution to the carrier A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 2.00 g of silica treated with hexamethyl¬ disilazane according to step A. 4.0 ml of the solution prepared according to step 3a was added and the slurry was stirred at room temperature for 15 min before drying over a period of 2.75 hrs by purging with a stream of argon, during which time the temperature was raised in steps to 80°C. As result a dry free flowing white powder was obtained. 3c. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of powder prepared according to step 3b and 4.0 mL of pentane. 1.9 ml of ethylaluminumsesqui- chloride was added and the slurry was stirred at room temperature for 1 hr. Thereafter the solvent was removed under a period of 45 min by purging with a stream of argon, during which time the temperature was raised in steps to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 5.5 % Al, 9.3 % Cl, 0.95 % Mg and 1.7 % Ti. 3d. Test polymerization Ethylene was polymerized according to the method described above in step I using 100 mg of the powder prepared according to step 3c and 5.0 mL of a solution of triethyl¬ aluminum in pentane as co-catalyst. The results of the polymerization are shown in the table below. 3f. Test polymerization Ethylene was polymerized using as procatalyst 100 mg of the powder prepared according to step 3c and as co-catalyst 5.0 mL of a 10% solution of triethylaluminum in pentane. The polymerization was carried out according to the procedure described in step I above except that the hydrogen pressure in the 500 mL vessel was 10 bars. The results of the polymerization are shown in the table below. 3g. Test polymerization Ethylene and 4-methyl-1-pentene were co-polymerized according to the procedure described in step II above using 100 mg of the powder prepared according to step 3c and as a co-catalyst 5.0 mL of a 10% solution of triethyl- aluminum in pentane. The results of the polymerization are shown in the table below. Example 4 4a. Preparation of the solution A 100 mL bottle equipped with a magnetic stirrer was charged with 10.0 mL of heptane and with 5.95 mL of 1- butanol. 26.7 mL of a 10% solution of triethylaluminum in pentane was added at room temperature over a period of 30 min. 1.71 mL of titaniumtetrabutoxide was added to the solution followed by 11.4 mL of a 20 wt% solution of butyloctylmagnesium in heptane at a temperature of 5°C over a period of 20 min. The volume of the obtained solution was raised to 60 mL by addition of heptane. 4b. Impregnation of the solution to the carrier A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 2.00 g of silica which was treated with hexamethyldisilazane according to step A, and with 10 mL of pentane. 12.0 mL of the solution prepared according to step 4a was added and the slurry was stirred at room temperature for 15 min before drying for 2.75 hrs by purging with a stream of argon, during which time the temperature was raised in steps to 110°C. As result a dry free flowing white powder was obtained. 4c. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to step 4b, and 4.0 mL of pentane. 2.52 mL of ethylaluminu - sesquichloride was added and the slurry was stirred at room temperature for 1 hr. Thereafter the solvent was removed during 1.5 hrs by purging with a stream of argon, during which time the temperature was raised in steps to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 7.6 % Al, 11.4 % Cl, 1.1 % Mg and 0.97 % Ti. 4d. Test polymerization Ethylene was polymerized according to to the procedure described in step I above using 100 mg of the powder prepared according to step 4c and as a co-catalyst 5,0 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 5 5a. Preparation of the solution A 50 mL bottle equipped with a magnetic stirrer was charged with 8.89 mL of a 10% solution of triethylaluminum in pentane, and 1.92 mL of 1-butanol was added at room temperature over a period of 30 min. 0.343 mL of titanium- tetrabutoxide was added to the solution, and thereafter 3.43 mL of a 20 wt% solution of butyloctylmagnesium in heptane at a temperature 5 β C over a period of 20 min. As result a homogenous solution was obtained. 5b. Impregnation of the solution to the carrier A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 2.00 g of silica treated with hexamethyl¬ disilazane according to step A, and with 8 mL of pentane. The solution prepared according to step 5a was added and the slurry was stirred at room temperature for 15 min before drying for 2.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80°C. As result a dry free flowing white powder was obt ined. 5c. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of powder prepared according to step 5b, and with 4.0 mL of pentane. 2.31 mL of ethylaluminum- sesquichloride was added and the slurry was stirred at room temperature for 2 hrs. Thereafter the solvent was removed during 1.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 8.5 % Al, 11.5 % Cl, 1.3 % Mg and 0.9 % Ti. 5d. Test polymerization Ethylene was polymerized according to step I above using 50 mg of the powder prepared according to step 5c and as a co-catalyst 2.5 mL of a 10 wt% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 6 6a. Impregnation of the solution to the carrier A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 2.00 g of silica treated with hexamethyl- disilazane according to step C, and with 8 mL of pentane. The solution prepared according to step 5a was added and the slurry was stirred at room temperature for 15 min before drying for 2.5 hrs by purging with a stream of argon, during which time the temperature was raised in steps to 80°C. As result a dry free flowing white powder was obtained. 6b. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to step 6a, and with 4.0 mL of pentane. 2.78 mL of ethylalumi- numsesquichloride was added and the slurry was stirred at room temperature for 2 hrs. Thereafter the solvent was removed during 1.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 9.2 % Al, 12.0 % Cl, 1.3 % Mg and 0.85 % Ti. 6c. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 50 mg of the powder prepared according to step 6b and as co-catalyst 2.5 mL of a 10% solution of triethylaluminum in pentane. The results .of the polymerization are shown in the table below. Example 7 7a. Impregnation of the solution to the carrier A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 2.00 g of silica treated with hexamethyl¬ disilazane according to step A, and with 8 mL of pentane. The solution prepared according to step 5a was added and the slurry was stirred at room temperature for 15 min before drying for 2.5 hrs by purging with a stream of argon, during which time the temperature was raised in steps to 80°C. As result a dry free flowing white powder was obtained. 7b. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to step 7a, and with 4.0 mL of pentane. 2.38 mL of ethylalu- minumdichloride was added and the slurry was stirred at room temperature for 2 hrs. Thereafter the solvent was removed during 1.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 7.9 % Al, 14.3 % Cl, 1.4 % Mg and 0.85 % Ti. 7c. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 30 mg of the powder prepared according to step 7b and as a co-catalyst 1.5 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 8 8a. Preparation of the catalyst The method of example 7 was followed using the carrier prepared according to step E. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 9.0 % Al, 15.7 % Cl, 1.2 % Mg and 0.87 % Ti. 8b. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 31 mg of the powder prepared according to step 8a and as a co-catalyst 1.6 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 9 9a. Preparation of the catalyst The method of example 7 was followed using the carrier prepared according to step B. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 8.9 % Al, 15.6 % Cl, 1.4 % Mg and 1.0 % Ti. 9b. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 30 mg of the powder prepared according to step 9a and as a co-catalyst 1.5 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 10 10a. Impregnation of the solution to the carrier A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 2.00 g of silica treated with hexamethyl¬ disilazane according to step B, and with 8 mL of pentane. The solution prepared according to step 5a was added and the slurry was stirred at room temperature for 15 min before drying for 2.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80 β C. As result a dry free flowing white powder was obtained. 10b. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to step 10a, and with 4.0 mL of pentane. 2.27 mL of diethyl- aluminumchloride was added and the slurry was stirred at room temperature for 2 hrs. Thereafter the solvent was removed during 1.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 8.6 % Al, 7.6 % Cl, 1.0 % Mg and 0.86 % Ti. 10c. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 30 mg of the powder prepared according to step 10b and as a co-catalyst 1,5 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 11 11a. Preparation of the catalyst The method of example 7 was followed using the carrier prepared according to step D. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 8.8 % Al, 15.6 % Cl, 1.3 % Mg and 0.83 % Ti. lib. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 32 mg of the powder prepared according to step 11a and as a co-catalyst 1,6 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 12 12a. Preparation of the solution A 50 mL bottle equipped with a magnetic stirrer was charged with 7.85 mL of a 10% solution of triethylaluminum in pentane and 1.09 mL of ethanol was added at room temperature durind 30 min. 0.303 mL of titaniu tetrabutoxide was added to the solution and thereafter 3.03 mL of a 20 wt% solution of butyloctylmagnesium in heptane at a temperature of 5°C during 20 min. As result a homogenous solution was obtained. 12b. Impregnation of the solution to the carrier A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 1.76 g of silica treated with hexamethyl- disilazane according to step A, and with 8 mL of pentane. A solution prepared according to the procedure of step 12a was added and the slurry was stirred at room temperature for 15 min before drying for 2.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80°C. As result a dry free flowing white powder was obtained. 12c. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to step 12b, and with 4.0 mL of pentane. 2.78 mL of ethylalu- minumsesquichloride was added and the slurry was stirred at room temperature for 2 hrs. Thereafter solvent was removed during 1.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 8.3 % Al, 16.8 % Cl, 1.6 % Mg and 1.1 % Ti. 12d. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 50 mg of the powder prepared according to step 12c and as a co-catalyst 2.5 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 13 13a. Preparation of the solution A 50 mL bottle equipped with a magnetic stirrer was charged with 12.4 mL of a 10% solution of triethylaluminum in pentane, and 2.65 mL of 1-butanol was added at room temperature during 30 min. 0.343 mL of titaniumtetrabutoxide was added to the solution and thereafter 4.57 mL of a 20 wt% solution of butyloctylmagnesium in heptane at a temperature of 5°C during 20 min. As result a homogenous solution was obtained. 13b. Impregnation of the solution to the carrier A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 2.50 g of silica treated with hexamethyl¬ disilazane according to step A, and with 8 mL of pentane. The solution prepared according to step 13a was added and the slurry was stirred at room temperature for 15 min before drying for 2.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80°C. As result a dry free flowing white powder was obtained. 13c. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to • step 13b, and with 4.0 mL of pentane. 2.22 L of ethylalu- minu dichloride was added and the slurry was stirred at room temperature for 2 hrs. Thereafter the solvent was removed during 1.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 7.9 % Al, 13.4 % Cl, 1.4 % Mg and 0.61 % Ti. 13d. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 50 mg of the powder prepared according to step 13c and as a co-catalyst 2.5 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 14 14a. Preparation of the solution A 50 mL bottle equipped with a magnetic stirrer was charged with 8.4 mL of heptane and 0.92 mL of 1-butanol. 3.0 mL of a 10% solution of triethylaluminum in pentane was added at room temperature during 30 min. 0.290 mL of titanium- tetrabutoxide was added to the solution and thereafter 2.88 mL of a 20 wt% solution of butyloctylmagnesium in heptane at a temperature of 5°C during 20 min. As result a homogenous solution was obtained. 14b. Impregnation of the solution to the carrier A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 2.0 g of silica treated with hexamethyl¬ disilazane according to step A, and with 8 mL of pentane. The solution prepared according to step 14a was added and the slurry was stirred at room temperature for 15 min before drying for 2.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80°C. As result a dry free flowing white powder was obtained. 14c. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to step 14b, and with 4.0 mL of pentane. 2.83 mL of ethylalu- minumsesquichloride was added and the slurry was stirred at room temperature for 2 hrs. Thereafter the solvent was removed during 1.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 7.8 % Al, 11.8 % Cl, 1.6 % Mg and 1.1 % Ti. 14d. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 50 mg of the powder prepared according to step 14c and as a co-catalyst 2.5 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 15 15a. Preparation of the solution A 50 mL bottle equipped with a magnetic stirrer was charged with 4.0 mL of a 20 wt% solution of tetraisobutylaluminum- oxane in heptane, and 0.915 mL of 1-butanol was added at room temperature during 30 min. 0.343 mL of titaniumtetra¬ butoxide was added to the solution and thereafter 3.65 mL of a 20 wt% solution of butyloctylmagnesiu in heptane at a temperature of 5°C during 20 min. As result a homogenous solution was obtained. 15b. Impregnation of the solution to the carrier A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 2.0 g of silica treated with hexamethyldi¬ silazane according to step C, and with 8 mL of pentane. The solution prepared according to step 15a was added and the slurry was stirred at room temperature for 1 hr before drying for 3.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 105°C. As result a dry free flowing pale green powder was obtained. 15c. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to step 15b, and with 4.0 mL of pentane. 3.61 mL of ethyl- aluminumsesquichloride was added and the slurry was stirred at room temperature for 2 hrs. Thereafter the solvent was removed during 2 hrs 10 min by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 8.8 % Al, 15.5 % Cl, 1.5 % Mg and 1.0 % Ti. 15d. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 50 mg of the powder prepared according to step 15c and as a co-catalyst 2.5 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 16 16a. Preparation of the solution A 50 mL bottle equipped with a magnetic stirrer was charged with 3.56 mL of a 10% solution of triethylaluminum in pentane and 0.82 mL of 1-butanol was added at room tempera¬ ture during 30 min. 0.343 mL of titaniumtetrabutoxide was added to the solution and thereafter 3.43 mL of a 20 wt% solution of butyloctylmagnesium in heptane at a temperature of 5°C during 20 min. As result a homogenous solution was obtained. 16b. Impregnation of the solution to the carrier A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 2.0 g of silica treated with hexamethyldi¬ silazane according to step A, and with 8 mL of pentane. The solution prepared according to step 16a was added and the slurry was stirred at room temperature for 1 hr before drying for 3.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 100°C. As result a dry free flowing white powder was obtained. 16c. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to step 16b, and with 4.0 mL of pentane. 2.88 mL of ethylalumi- numdichloride was added and the slurry was stirred at room temperature for 2 hrs. The solvent was removed thereafter during 1 hr 15 min by purging with a stream of nitrogen, during which time the temperature was raised in steps to 100°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 7.5 % Al, 18.2 % Cl, 1.5 % Mg and 1.1 % Ti. 16d. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 30 mg of the powder prepared according to step 16c and as a co-catalyst 1.5 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 17 17a. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to step 16b, and with 4.0 L of pentane. 1.44 mL of ethylalumi- numdichloride was added and the slurry was stirred at room temperature for 2 hrs. Thereafter the solvent was removed during 1 hr 15 min by purging with a stream of nitrogen, during which time the temperature was raised in steps to 100°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 3.9 % Al, 11.1 % Cl, 1.2 % Mg and 1.1 % Ti. 17d. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 33 mg of the powder prepared according to step 17a and as a co-catalyst 1.7 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table below. Example 18 18a. Preparation of the solution A 50 mL bottle equipped with a magnetic stirrer was charged with 5.34 mL of a 10% solution of triethylaluminum in pentane, and with 3.43 mL of a 20% solution of butyloctyl- magnesium in heptane. 0.70 mL of ethanol was added at room temperature during 30 min. 0.343 mL of titaniumtetrabutoxide was thereafter added to the solution at a temperature of 5°C during 20 min. As result a homogenous solution was obtained. 18b. Impregnation of the solution to the carrier A sealed 50 mL bottle equipped with a magnetic stirrer was charged with 2.00 g of silica treated with hexamethyl¬ disilazane according to step A, and with 8 mL of pentane. The solution prepared according to step 18a was added and the slurry was stirred at room temperature for 15 min before drying for 2.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps to 80 β C. As result a dry free flowing white powder was obtained. 18c. Chlorination step A sealed 30 mL bottle equipped with a magnetic stirrer was charged with 0.50 g of the powder prepared according to step 18b. 3.03 mL of a 10% solution of ethylaluminum- dichloride in pentane was added and the slurry was stirred at room temperature for 2 hrs. Thereafter solvent was removed during 1.5 hrs by purging with a stream of nitrogen, during which time the temperature was raised in steps, to 80°C. As result a free flowing pale orange-brown powder was obtained. Elemental analysis of the powder revealed 7.1 % Al, 16.5 % Cl, 1.7 % Mg and 1.1 % Ti. 18d. Test polymerization Ethylene was polymerized according to the procedure described above in step I using 49 mg of the powder prepared according to step 18c and as a co-catalyst 2.45 mL of a 10% solution of triethylaluminum in pentane. The results of the polymerization are shown in the table. TABLE 1 TABLE 1 (continued) Example Element composition Activity of Properties of the of the catalyst the catalyst obtained polyethylene Al % Cl % Mg % Ti % Kg PE /g. i.hr. Ml(21.6) MFR(21.6/2.16) Bulk densi g / 10 min Kg / m 3 387 292 407 330 334 303 321 356 373 410

Claims: Claims 1. Process for the preparation of a procatalyst composition for polymerization of olefins, said process comprising application of a metal-containg complex compound or mixture of compounds to a porous particulate carrier and chlorina¬ tion of the same with a suitable chlorination agent, charac¬ terized in that magnesium or a compound thereof, titanium compound, aluminum or a compound thereof and, optionally, a compound having a hydroxyl group are reacted with each other so that an alkoxide or alkylalkoxide solution con¬ taining the said metals in an inert solvent is obtained, which solution is in a single step impregnated into the carrier, whereafter the extra solvent is removed. 2. A process according to claim 1, characterized in that the carrier is an inorganic oxide thich has been treated for removal of free hydroxyl groups before the impregnation. 3. A process according to claim 2, characterized in that the carrier is a dehydrated silica which has been reacted with a compound which removes hydroxyl groups. 4. A process according to claim 3, characterized in that the carrier is dehydrated and calcinated silica wich has been reacted with a suitable silicon compound such as hexa¬ methyldisilazane, or an aluminum compound such as triethyl¬ aluminum for the removal of hydroxyl groups. 5. A process according to any one of the preceding claims, characterized in that the magnesium compound is an organic magnesium compound, suitably an magnesiumalk l such as butyloctylmagnesium, that the titanium compound is a ti¬ tanium alkoxide such as Ti(OBu) 4 , that the aluminum compound is an organic aluminum compound, suitably an aluminumalkyl such as a triethylaluminum, or an aluminumoxane such as tetraisobutylaluminumoxane and that the compound comprising a hydroxyl group is an alcohol such as ethanol or l-butanol. 6. A process according to any one of the preceding claims, characterized in that the inert solvent is a hydrocarbon. 7. A process according to any one of the preceding claims, characterized in that the solvent is removed after the impregnation step by evaporation. 8. A process according to any one of the preceding claims, characterized in that the impregnated carrier particles are chlorinated with a suitable organic aluminum chloride. 9. The use of a procatalyst composition prepared according to any one of the preceding claims, together with a co- catalyst such as an organic aluminum compound, for poly e- rization or copolymerization of olefins such as ethylene.

Inventors: ANDELL OVE, ANDELL, OVE
Applicants: NESTE OY
Application year: 1990
Main classification: C08F4
IPC codes: C08F4, C08F10