Stabilized sodium percarbonate composition

Abstract: A stabilized sodium percarbonate is obtained by incorporating therein (A) at least one compound selected from the group consisting of mono- and dicarboxylic acids having not less than four carbon atoms and salts thereof; and (B) at least one compound selected from the group consisting of sulfates, nitrates and silicates of alkali metals and alkaline earth metals.

Description: Background of the Invention The present invention relates to a stabilized sodium percarbonate composition, particularly a stabilized sodium percarbonate composition suitable for use as a bleaching agent in detergents, etc. Sodium percarbonate is generally used widely as a bleaching agent, a detergent, or a sterilizer. Sodium percarbonate as a bleaching agent is superior in solubility at low temperatures, exhibits a high bleaching effect, and is a stable compound in an ordinary preserved state. However, sodium percarbonate is disadvantageous in that it is unstable when preserved in high humidity conditions or when incorporated in a detergent. As a household detergent, a product containing a predetermined amount of sodium percarbonate as a bleaching agent is particularly preferred. When incorporated in a detergent, however, sodium percarbonate loses its stability upon contact with zeolite which is used as a builder or with water contained in a very small amount in the detergent, resulting in that the sodium percarbonate no longer exhibits the bleaching effect and there is fear of the detergent losing its effect. Various proposals have heretofore been made for solving these problems. For example in Japanese Patent Publication No. 56167/1988 there is disclosed a method wherein sodium percarbonate is coated with magnesium sulfonate or magnesium salt of sulfuric ester; in Japanese Patent Publication No. 57362/1988there is disclosed a method wherein sodium percarbonate is coated with such magnesium salt plus sulfate or hydrochloride of an alkali or alkaline earth metal; in Japanese Patent Laid-Open No. 118606/1085 there is disclosed a method wherein sodium percarbonate is coated with boric acid or a partially neutralized borate and a water repellent; in Japanese Patent Laid-Open No. 194000/1984 a method wherein sodium percarbonate is coated with a borate and a magnesium compound; and in Japanese Patent Laid-Open No. 129500/1975 a method wherein sodium percarbonate is coated with a mixture of a surfactant and a water-insoluble compound which is compatible with the surfactant. All of these methods intend to prevent sodium percarbonate from coming into cont act with detergent ingredients to stabilize it by coating it with specific chemical substances. According to these conventional methods, however, when the sodium percarbonate thus coated is preserved in a high humidity condition or when incorporated in a detergent, the stabilization effect is not attained to a satisfactory extent in practical use. It is the object of the present invention to solve the above-mentioned problem. The present inventors found that the aforesaid problem which had not been solved by the prior art could be overcome by incorporating in sodium percarbonate a mono- or dicarboxylic acid or a salt thereof and a sulfate, nitrate or silicate of an alkali metal or alkaline earth metal. In this way we reached the present invention. Summary of the Invention The present invention resides in a composition comprising sodium percarbonate and the following components (A) and (B): (A) at least one compound selected from saturated or unsaturated, aliphatic or alicyclic mono- or dicarboxylic acids having 6 to 20 carbon atoms and salts thereof; and (B) at least one compound selected from sulfates, nitrates and silicates of alkali metals and alkaline earth metals, wherein at least one of (A) and (B) form a coating. This sodium percarbonate composition, as compared with the conventional sodium percarbonate, is remarkably improved in its stability during preservation in a high humidity condition or when incorporated in a detergent. Detailed Description of the Invention Examples of mono and dicarboxylic acids which may be used in the present invention include saturated or unsaturated aliphatic or alicyclic mono- or dicarboxylic acids having 6 to 20 carbon atoms. More concrete examples are butyric acid, isobutyric acid, valeric acid, caproic acid, caprylic acid, capric acid, lauric acid, myristic acid, palmitic acid, stearic acid, isostearic acid, arachic acid, behenic acid, lignoceric acid, cyclohexanecarboxylic acid, sorbic acid, zoomaric acid, linolenic acid, linoleic acid, recinoleic acid, gadoleic acid, erucic acid, selacholeic acid, diphenylacetic acid, phenylacetic acid, sebacic acid, undecanoic acid, dodecane-dicarboxylic acid, brassylic acid, tetradecane-dicarboxylic acid, thapsinic acid, itaconic acid, muconic acid, beef tallow fatty acid, horse fat fatty acid, mutton tallow fatty acid, lard fatty acid, coconut oil fatty acid, palm oil fatty acid, palm kernel oil fatty acid, soybean oil fatty acid, linseed oil fatty acid, castor oil fatty acid, rice bran oil fatty acid, rape oil fatty acid, and hydrogenated such fatty acids. Examples of salts of mono- and dicarboxylic acids each which may be used in the present invention include sodium salts, potassium salts, magnesium salts and calcium salts of the C₄ or more mono- or dicarboxylic acids examplified above. Examples of sulfates, nitrates and silicates of alkali metals and alkaline earth metals which may be used in the present invention include sodium sulfate, potassium sulfate, magnesium sulfate, sodium nitrate, potassium nitrate, magnesium nitrate, calcium nitrate, sodium silicate (Nos. 1, 2 and 3), sodium metasilicate, sodium orthosilicate, and potassium silicate. In the stabilizer used in the present invention, even if at least one compound selected from the group (A) or at least one compound selected from the group (B) is incorporated each alone in sodium percarbonate, there will not be obtained a satisfactory effect of stabilization. Only when both compounds are used together there is obtained a satisfactory effect. It is preferable that the stabilizer components (A) and (B) in the present invention be used each in an amount of 0.5 to 20 wt%. If the amount thereof is smaller than 0.5 wt%, there will not be obtained a satisfactory effect, while if the amount thereof is larger than 20 wt%, the effective oxygen concentration will be decreased more than necessary although a satisfactory effect of stabilization will be obtained. More preferably, the stabilizer components (A) and (B) are used each in an amount of 2 to 10 wt%. For preparing the composition of the present invention there may be adopted any method provided it permits uniform dispersion or incorporation of the stabilizer components (A) and (B) in sodium percarbonate. For example, the composition of the present invention can be prepared by mixing the compounds (A) and (B) with wet crystals obtained in a crystallization step and then granulating the resulting mixture. Or it can be prepared by dissolving the stabilizer components in water or an organic solvent and spraying the resulting solution to flowing crystals or granules of sodium percarbonate followed by drying. A solution containing both compounds (A) and (B) may be sprayed in a single step, or separate solutions prepared using the compounds (A) and (B) respectively may be sprayed in two separate steps. Or one of the compounds (A) and (B) may be added at the time of granulation, while the other is sprayed as a solution. There also may be used conventional additives for sodium percarbonate such as stabilizers other than the one used in the present invention as well as granulation binders. Examples The present invention will be described below in more detail in terms of working Examples of the invention and Comparative Examples. But it is to be understood that the invention is not limited thereto. Examples 1 - 29 Sodium carbonate and hydrogen peroxide were reacted together in an aqueous solution and the resulting crystals were separated by centrifugal filtration. Then, the resulting crystals of sodium percarbonate in a wet condition were mixed with a predetermined amount of each of the stabilizer components (A) shown in Table 1 in accordance with the corresponding composition ratio set forth also in the same table. The resulting mixture was extrusion granulated by means of a granulator equipped with a 1.0 mm mesh wire gauze, followed by drying. 200 g of the granules thus obtained were fed into a rotary vacuum dryer equipped with a spray,coated and a 10-25% aqueous solution of the corresponding stabilizer component (B) shown in Table 1 was sprayed onto the granules little by little while heating was made to 70°C under reduced pressure in accordance with the corresponding composition ratio set forth in the same table. After termination of the spraying, the composition thus obtained was dried for 20 minutes. In this way there were prepared sodium percarbonate compositions in accordance with the composition ratios described in Table 1, which compositions were found to range in effective oxygen concentration from 12.5% to 13.5%. Then 2g of the compositions were intimately mixed with 2 g of a powdered detergent zeolite and the resulting mixtures were allowed to stand for 48 hours under the conditions of 50°C and a relative humidity of 80%, then determined for residual effective oxygen concentrations, from which the respective stabilities were calculated. The results are as set out in Table 1. The determination of effective oxygen concentration was performed according to an iodometric titration method. For comparison purpose, the same test was conducted also with respect to the use of sodium percarbonate not containing any stabilizer and the use of each stabilizer component alone, and the results obtained are showing as Comparative Examples in Table 1. Examples 30 - 49 200 g of 16 to 80 mesh granules of dried sodium percarbonate obtained by extrusive granulation were fed into a rotary vacuum dryer equipped with a spray coater and a 10-25% aqueous solution of each of the stabilizer components (B) shown in Table 2 was sprayed to the granules little by little while heating was made to 70°C under reduced pressure until a predetermined amount thereof was incorporated in the granules. Then, a 10-30% solution in ethanol of each of the stabilizer components (A) shown in the same table was sprayed in the same manner as above until a predetermined amount thereof was incorporated in the granules. After termination of the spraying, the composition thus obtained was dried for 10 minutes. In this way there were prepared sodium percarbonate compositions in accordance with the composition ratios described in Table 2, which compositions were found to range in effective oxygen concentration from 12.0% to 13.5%. Then, the compositions were determined for stability in the same way as in Examples 1-29. The results are as set forth in Table 2.

Claims: A stable sodium percarbonate composition comprising sodium percarbonat and the following components (A) and (B): (A) at least one compound selected from saturated or unsaturated, aliphatic or alicyclic mono- or dicarboxylic acids having 6 to 20 carbon atoms add salts thereof; and (B) at least one compound selected from sulfates, nitrates and silicates of alkali metals and alkaline earth metals, wherein at least one of (A) and (B) form a coating. A stable sodium percarbonate as set forth in Claim 1, wherein the content of the component (A) and that of the component (B) are each in the range of 0.5 to 20 % by weight. A stable sodium percarbonate as set forth in Claim 1 or Claim 2, wherein the salts in the component (A) are sodium salts, potassium salts, magnesium salts or calcium salts. A stable sodium percarbonate as set forth in any one of Claims 1 to 3, wherein the component (B) is sodium sulfate, potassium sulfate, magnesium sulfate, sodium nitrate, potassium nitrate, magnesium nitrate, calcium nitrate, sodium silicate, sodium metasilicate, sodium orthosilicate, or potassium silicate.

Inventors: KONDO TOMOMASA, SATO KANJI, KONDO, TOMOMASA, SATO, KANJI
Applicants: TOKAI ELECTRO CHEMICAL CO, TOKAI DENKA KOGYO KABUSHIKI KAISHA
Application year: 1990
Main classification: C01B15
IPC codes: C01B15