Metal-based composite material and process for preparation thereof

Abstract: A metal-based composite material comprising aluminium or an aluminium alloy combined with a whisker of aluminium borate represented by the chemical formula of 9Aℓ₂O₃·2B₂O₃ or 2Aℓ₂O₃·B₂O₃ has excellent mechanical properties such as high tensile strength and great hardness.

Description: The present invention relates to a process for producing an aluminum type metal-based composite material comprising an aluminum borate whisker as a reinforcer. With recent technical development in various industries represented by the aerospace industry, the demand for a new material having higher strength, elasticity and hardness and capable of resisting a higher temperature than conventional metal materials is increasing. Among metal materials, aluminum and aluminum alloys have a low specific gravity and an easy workability and are supplied at low costs, and therefore, they are widely used as materials having high strength and heat resistance in various fields for airplanes, automobiles, construction materials, chemical machines and the like. As the means for improving the mechanical properties of aluminum type metals, there have been vigorously investigated methods of forming composite materials by combining an aluminum type alloy with a whisker or fiber of a material having high strength and elasticity, such as silicon carbide, silicon nitride, carbon, alumina or potassium hexatitanate, as a whisker or reinforcer, and as the composite-forming method, there are known a hot press method, a HIP method, an infiltration method, a powder metallurgy method, a high-pressure casting case method and a hot extrusion method. In the production of an aluminum type metal-based composite material, it is important that a reinforcing whisker or fiber should have a high wettability with and be inert to a melt of aluminum. However, reinforcers having such properties are limited in number and most of whiskers and fibers are practically used in the state where the surface is coated with an inert compound. Among these reinforcers, an alumina type fiber or whisker and a silicon carbide whisker satisfy the above-mentioned two-requirements and are promising as a reinforcing material. However, since they are expensive, they can hardly be applied to general-purpose uses for automobiles, construction materials and the like, though they may be used in the aerospace industry. At the present, from the economical viewpoint, only a whisker of potassium hexatitanate can be used as a general-purpose reinforcer for the production of an aluminum type metal composite material. However, this compound has an inherent problem in that tetravalent titanium is reduced with metallic aluminum and an intermetallic compound such as Ti₃Al is formed. Accordingly, this reducing reaction is controlled by shortening the heat treatment time to the utmost, but in this case, the process becomes defective in that no satisfactory composite effect can be attained. It is a primary object of the present invention to solve the foregoing problems and provide a process for the preparation of a whisker-reinforced aluminum type metal-based composite material in which a sufficient reinforcing effect is attained by using a cheap reinforcing material not reactive with a matrix metal. Aluminium borate whiskers represented by the chemical formula of 9Al₂O₃.2B₂O₃ or 2Al₂O₃.B₂O₃ and their use as reinforcing materials for resins, cements, ceramics and metals are described in EP-A-0296779. In accordance with the present invention, there is provided a process for producing an aluminium or aluminium alloy-based composite material, which comprises mixing a powder of aluminium or an aluminium alloy with an aluminium borate whisker such that the content of the whisker in the mixture is 5 to 40% by volume, pressure-moulding and firing or charging the mixture into a mould and firing under compression the mixture at a temperature of 500 to 650°C, or mixing an aluminium borate whisker with a binder containing water such that the content of the whisker in the mixture is 3 to 40% by weight, pressing, drying and firing the mixture to form a pre-formed body and infiltrating the pre-formed body of an aluminium borate whisker with a melt of aluminium or an aluminium alloy under a pressure of 4.9-196x10⁶ Pa (50 to 2000 kgf/cm²), the aluminium borate whisker having a diameter of 0.5 to 5 µm and a length of 5 to 200 µm. Preferred embodiments of the invention are shown in claims 2-7. Detailed description of the Preferred Embodiments The aluminum borate whisker used in the present invention is a compound prepared according to the process disclosed in Japanese Unexamined Patent Publication No. 63-319298 and Japanese Unexamined Patent Publication NO. 63-319299. Namely, the aluminum borate whisker can be prepared according to the liquid phase process comprising reacting at least one aluminum-supplying component selected from inorganic aluminum salts with at least one boric acid-supplying component selected from oxides and oxyacids of boron and alkali metal salts of boric acid in the presence of at least one flux selected from alkali metal chlorides, sulfates and carbonates at an elevated temperature of 900 to 1200°C for 9Aℓ₂O₃·2B₂O₃ or 600 to 1000°C for 2Aℓ₂O₃·B₂O₃ and growing the reaction product. Expensive whiskers are mainly prepared by the gas phase process requiring a high technique. In contrast, the whisker used in the present invention can be easily prepared according to the liquid phase process using a flux, and therefore, the whisker can be supplied at a low cost. One means for preparing the composite material of the present invention is a process comprising mixing a powder of aluminum or an aluminum alloy with an aluminum borate whisker, pressure-molding the mixture and firing the molded body. In practicing this process of the present invention, the particle size of the aluminum or aluminum alloy powder used as the matrix is smaller than 50 µm, preferably smaller than 20 µm, and a powder having a much reduced degree of the oxidation of the surface is suitable from the viewpoint of the sintering property. Typical instances of the aluminum borate whisker are represented by chemical formulae of 9Aℓ₂O₃·2B₂O₃ and 2Aℓ₂O₃·B₂O₃. An aluminum borate whisker having none of aggregates such as pills and being disentangled is preferably used. The amount of the whisker added to the aluminum or aluminum alloy is 5 to 40% by volume. If the amount of the whisker is too small, no sufficient reinforcing effect is attained, and if the amount of the whisker is too large, the compatibility of the whisker with the aluminum or aluminum alloy in the interface thereof is insufficient and no satisfactory reinforcing effect can be attained. In carrying out the process of the present invention, the compatibility of the whisker with the aluminum type metal is preferably increased by spreading lithium hydroxide on the surface of the aluminum borate whisker. This spreading can be accomplished by immersing the whisker in a solution containing lithium hydroxide dissolved therein and drying the whisker. A mixture comprising 5 to 40% by volume of the aluminum borate whisker dispersed in the powdery aluminum or aluminum alloy is pressure-molded at normal temperature under a pressure of 49-196 x 10⁷ Pa (5 to 20 ton/cm²), and the molded body is sintered at a temperature of 500 to 650°C, preferably 580 to 630°C under atmospheric pressure in an inert gas such as nitrogen or argon or a reducing atmosphere such as hydrogen over a period of 5 minutes to 2 hours to obtain an intended aluminum type metal-based composite material. Uniform and homogeneous mixing of the aluminum borate whisker with the aluminum or aluminum alloy is not sufficiently attained by dry blending, and wet blending using a solvent is preferably adopted. A polar solvent is preferably used for this purpose, and an alcohol is most preferably used. Predetermined amounts of the aluminum or aluminum alloy powder and the aluminum borate whisker are added to the solvent and they are uniformly dispersed in the solvent by irradiation with ultrasonic vibrations. The ratio of the solids to the solvent is adjusted to 3 to 30% by volume. As the means for obtaining a dry mixture by removing the solvent from the obtained slurry, there can be adopted a method in which the slurry is promptly subjected to suction filtration and the remaining solid is dried, or a method in which the slurry is subjected to evaporation to dryness while keeping the dispersion state. Alternatively, the aluminum or aluminum alloy powder is mixed with the aluminum borate whisker in the same manner as described above, and the mixed powder is charged in a mold and heated and sintered at a temperature in the range of from 500 to 650°C in vacuo for 5 minutes to 2 hours under pressurization to 4.9-49 x 10⁷ Pa (500 to 5000 kgf/cm²), whereby an intended composite material can be obtained. Alternatively the metal-based composite material of the present invention is a process comprising infiltrating a molded body of an aluminum borate whisker with aluminum or an aluminum alloy. In practicing this process of the present invention, an aluminum borate whisker molded body shaped into an appropriate form in advance is contacted with a melt of aluminum or an aluminum alloy under a pressure of 4.9-196 x 10⁶ Pa (50 to 2000 kgf/cm²) to obtain an intended metal-based composite material. Embodiments of this process of the present invention will now be described. As the aluminum and aluminum alloy as the matrix, there can be used those customarily used as spreading casting materials. Aluminum borate whiskers as described above are preferably used. For forming the molded body of the whisker, at first, a slurry is prepared by using water as the dispersant. The whisker concentration in the slurry is adjusted to 3 to 40% by weight, and an organic binder and an inorganic binder are added to the slurry in amounts of 0.1 to 20% by weight and 0.01 to 5% by weight, respectively, based on the winder. The slurry should be uniformalized by mechanical stirring or irradiation with ultrasonic waves so that the whisker is dientangled into individual filaments. Water-soluble or hydrophilic organic and inorganic binders are used. More specifically, an alginic acid salt, sugar, molasses, a cellulose ether, polyvinyl alcohol and carboxymethyl cellulose are preferably used as the organic binder, and water glass, silica sol and alumina sol are preferably used as the inorganic binder. The prepared aluminum borate whisker slurry is concentrated to produce a semi-dry state where the water content is about 1 to about 10%. The semi-dried dispersion is placed in a mold designed to have a predetermined shape and pressure molding is carried out. At this step, the organic binder exerts a function of improving the moldability. The molded body is dried at 100 to 200°C to gel the inorganic binder, and in order to increase the mechanical strength of the molded body to a level capable of resisting the pressure to be applied at the melt forging step, the molded body is fired at 500 to 1000°C. By this firing, all of the organic binder is burnt away completely. The so-prepared molded body of the whisker is placed in a mold designed to have a predetermined shape, and a predetermined amount of a melt of aluminum or an aluminum alloy is cast into the mold. Compression is effected by a punch located above to cause the melt to permeate into spaces in the whisker molded body, followed by cooling, whereby an intended composite body is obtained. The pressure for permeation of the melt is 4.9-196 x 10⁶ Pa (50 to 2000 kgf/cm²), the mold temperature is 200 to 500°C, the melt temperature is 700 to 900°C, and the temperature of the whisker molded body is preferably almost equal to the melt temperature. If the mold temperature is too high, the coagulation speed of the melt becomes low and the productivity is reduced, though a product having better performances can be obtained. In contrast, if the mold temperature is low, the coagulation of the whisker molded body and melt becomes too high and the permeation becomes insufficient. For similar reasons, it is necessary that the whisker molded body should be sufficiently preheated. The aluminum borate whisker has a high strength, a high elasticity and a high melting point and contains a large amount of the alumina component in the compound. The chemical properties of the aluminum borate whisker are, therefore, similar to those of an alumina fiber and the affinity with aluminum is good. Accordingly, if the aluminum borate whisker is combined with aluminum or an aluminum alloy, the aluminum type metal is intimately and uniformly mixed with the borate aluminum whisker, and it is considered that for this reason, an excellent strength is manifested in the composite body. When the aluminum type metal composite body of the present invention is examined by the X-ray diffractometry or under a scanning type electron microscope, it is confirmed that the aluminum borate whisker is not reacted with the aluminum or aluminum alloy as the matrix at all. When a test piece is cut out from the composite body and the mechanical strength is measured, it is confirmed that a sufficient reinforcing effect by the whisker is manifested. Thus, it is proved that the present invention is very effective. The composite material of the present invention can be formed into a final product by a heat treatment, a hot extrusion using a die or a machining operation. The present invention will now be described in detail with reference to the following examples and comparative examples. Example 1 A beaker was charged with ethyl alcohol, and 3.1 g of a whisker of 9Aℓ₂O₃·2B₂O₃ having a diameter of about 1 µm and a length of 10 to 30 µm and 12.2 g of a pure aluminum powder having a particle size smaller than 20 µm (the content of the whisker was about 20% by volume) were added into the beaker. The mixture was irradiated with ultrasonic waves for 20 minutes and was promptly subjected to suction filtration. The solids were dried to form a sample for the pressure molding. The sample was placed in a mold having a diameter of 20 mm, and the sample was pressed under a total pressure of 30 tons while maintaining vacuum within the mold by suction, whereby a molded body having a height of about 10 mm was formed. The molded body was placed in an alumina boat and maintained at 620°C for 20 minutes in a nitrogen atmosphere, and the body was cooled to room temperature over a period of about 1 hour. The obtained fired composite body was machined by an emery cutter and a lathe to obtain test pieces for the tensile test and the measurement of the hardness, and the physical properties were examined. It was found that the tensile strength was 137 x 10⁶ Pa (14 kgf/mm²) and the micro Vickers hardness under a load of 0.2 kg was 75. Comparative Example 1 The fired body prepared in the same manner as Example 1 but without addition of the whisker of 9Aℓ₂O₃·2B₂O₃ had a tensile strength of 88 x 10⁶ Pa (9 kgf/mm²) and a micro Vickers hardness of 34 under a load of 0.2 kg. Example 2 A beaker was charged with 0.17 g of LiOH·2H₂O and 100 cc of ethyl alcohol, and a homogeneous solution was prepared. Then, a whisker of 9Aℓ₂O₃·2B₂O₃ having a diameter of about 1 µm and a length of 10 to 30 µm and 12.2 g of a pure aluminum powder having a particle size smaller than 20 µm (the content of the whisker was about 20% by volume) were added into the solution and the mixture was irradiated with ultrasonic waves for about 20 minutes. The alcohol was removed by a rotary evaporator to obtain a sample for the pressure molding. The subsequent treatments were carried out in the same manner as described in Example 1. The tensile strength of the obtained composite body was 196 x 10⁶ Pa (20 kgf/mm²). Example 3 A composite body was prepared in the same manner as described in Example 2 except that the amount of LiOH·2H₂O was changed to 0.08 g, the amount of 9Aℓ₂O₃·2B₂O₃ was changed to 1.5 g and the amount of the pure aluminum powder was changed to 13.8 g (the content of the, whisker was about 10% by volume). The tensile strength of the composite body was 127 x 10⁶ Pa (13 kgf/mm²) and the micro Vickers hardness under a load of 0.2 kg was 55. Example 4 A composite body was prepared in the same manner as described in Example 2 except that the amount of Li0H·2H₂O was changed to 0.25 g, the amount of 9Aℓ₂O₃·2B₂O₃ was changed to 4.6 g and the amount of the pure aluminum powder was changed to 10.7 g (the content of the whisker was about 30% by volume). The tensile strength of the composite body was 235 x 10⁶ Pa (24 kgf/mm²), and the micro Vickers hardness under a load of 0.2 kg was 110. Example 5 A beaker was charged with 0.10 g of LiOH·2H₂O and 100 cc of ethyl alcohol, and a homogeneous solution was prepared. Then, 3.1 g of a whisker of 2Aℓ₂O₃·B₂O₃ having a diameter of about 0.5 µm and a length of 5 to 15 µm and 12.2 g of a pure aluminum powder having a particle size smaller than 20 µm (the content of the whisker was about 20% by volume) were added to the solution and the mixture was irradiated with ultrasonic waves for 20 minutes. The alcohol was removed by a rotary evaporator to obtain a sample for the pressure molding. The subsequent treatments were carried out in the same manner as described in Example 1. The tensile strength of the obtained composite body was 176 x 10⁶ Pa (18 kgf/mm²). Example 6 A beaker was charged with 0.12 g of LiOH·2H₂O and 100 cc of ethyl alcohol, and a homogeneous solution was prepared. Then, 3.1 g of a whisker of 9Aℓ₂O₃·2B₂O₃ having a diameter of about 1 µm and a length of 10 to 30 µm and 12.2 g of an Aℓ-Si-Mg alloy powder [ISO: Aℓ-Si7Mg(Fe)] having a particle size smaller than 44 µm (the content of the whisker was about 20% by volume) were added to the solution. The mixture was irradiated with ultrasonic waves for 20 minutes and the alcohol was removed by a rotary evaporator to obtain a sample for the pressure molding. The sample was charged in a mold having a diameter of 8 mm and was pressed under a total pressure of 5 tons while producing vacuum within the mold by suction to prepare a molded body having a height of about 20 mm. The molded body was placed in an alumina boat and maintained at 630°C for 60 minutes in a hydrogen atmosphere. The body was cooled to room temperature over a period of about 1 hour and the subsequent treatments were carried out in the same manner as describe in Example 1. The tensile strength of the obtained composite body was 274 x 10⁶ Pa (28 kgf/mm²). Comparative Example 2 A fired body formed in the same manner as in Example 6 but without adding the whisker of 9Aℓ₂O₃-·2B₂O₃ had a tensile strength of 176 x 10⁶ Pa (18 kgf/mm²). Example 7 A beaker was charged with 200 cc of ethyl alcohol, and 9.3 g of a whisker of 9Aℓ₂O₃·2B₂O₃ having a diameter of about 1 µm and a length of 10 to 30 µm and 36.6 g of a pure aluminum powder having a particle size smaller than 50 µm (the content of the whisker was about 20% by volume) were added to the alcohol. The mixture was irradiated with ultrasonic waves for 20 minutes and promptly subjected to suction filtration. The solids were dried to form a sample for the pressure sintering. Then, the sample was placed in a mold having a diameter of 45 mm and pressed under a total pressure of 15 tons while producing vacuum within the mold by suction. The mold was heated to 650°C and maintained at this temperature for 20 minutes to sinter the starting mixture. The mold was cooled and the pressure was returned to atmospheric pressure, and the fired composite body was taken out from the mold and machined by an emery cutter and a lathe to prepare test pieces for the tensile test and the measurement of the hardness. The physical properties of the test pieces were examined. It was found that the tensile strength was 176 x 10⁶ Pa (18 kgf/mm²) and the micro Vickers hardness under a load of 0.2 kg was 68. Comparative Example 3 A fired body prepared in the same manner as in Example 7 but without addition of the whisker of 9Aℓ₂O₃·2B₂O₃ had a tensile strength of 88 x 10⁶ Pa (9 kgf/mm²) and a micro Vickers hardness under a load of 0.2 kg of 38. Example 8 and Comparative Example 4 A composite material was prepared in the same manner as described in Example 7 except that a pure aluminum powder having a particle size smaller than 5 µm was used and the whisker of 9Aℓ₂O₃·2B₂O₃ was added in an amount of 10, 20 or 30% by volume based on the entire mixture. The tensile strength and hardness of the test piece was measured. The obtained results are shown in Table 1. For Comparison Example 4 the above treatments were conducted in the same manner except that a potassium hexatitanate whisker (TISMO-D supplied by Otsuka Kagaku) was used instead of the 9Aℓ₂O₃·2B₂O₃ whisker. The tensile strength of the obtained composite material was measured. The obtained results are shown in Table 1. Example 9 A beaker was charged with 200 cc of hexane, and 9.3 g of a whisker of 2Aℓ₂O₃·B₂O₃ having a diameter of about 0.6 µm and a length of 10 to 20 µm and 36.6 g of an aluminum-magnesium alloy powder having a particle size smaller than 50 µm (the content of the whisker was about 20% by volume) were added into the beaker. The mixture was irradiated with ultrasonic waves for 20 minutes and promptly subjected to suction filtration, and the obtained solids were dried to prepare a sample for the pressure sintering. The sample was placed in a mold having a diameter of 45 mm and pressed under a total pressure of 20 tons while producing vacuum within the mold by suction. The mold was heated to 620°C and maintained at this temperature for 30 minutes to sinter the starting material mixture. The subsequent treatments were carried out in the same manner as described in Example 7 to obtain test pieces. When the physical properties were measured, it was found that the tensile strength was 333 x 10⁶ Pa (34 kgf/mm²) and the micro Vickers hardness under a load of 0.2 kg was 75. Comparative Example 5 A fired body prepared in the same manner as described in Example 9 without addition of the 2Aℓ₂O₃·B₂O₃ whisker had a tensile strength of 274 x 10⁶ Pa (28 kgf/mm²) and a micro Vickers hardness under a load of 0.2 kg of 45. Example 10 and Comparative Examples 6 to 9 In 1 ℓ of water was dispersed 100 g of a whisker of 9Aℓ₂O₃·2B₂O₃ having a diameter of about 1 µm and a length of 10 to 30 µm, and 5 g of polyvinyl alcohol and 4 cc of a 30% aqueous solution of silica sol were added to the dispersion. The mixture was irradiated with ultrasonic waves for 20 minutes to obtain a uniformly dispersed slurry. The slurry was concentrated by a rotary evaporator so that the water content was reduced to about 10%. The concentrate was taken out and placed in a polyvinyl chloride mold having a cylindrical shape having an inner diameter of 10 cm. The charged concentrate was compressed by a piston of polyvinyl chloride so that the height of the content was reduced to 2 cm. The obtained molded body was removed from the mold, dried at 150°C for 2 hours and fired at 800°C for 1 hour to gel the silica sol and obtain a molded body in which the volume fraction (VF) of the whisker was 20%. The as-fired hot molded body was placed in the central portion of the bottom of a mold having a cylindrical shape having an inner diameter of 12 cm, which was maintained at a temperature of 300°C, and about 200 cc of a aluminum alloy spreading material (ISO: A Mg1SiCu) melted at 800°C was cast into the mold and promptly pressed by a piston arranged above the mold to cause the melted aluminum alloy to permeate into the molded body. The pressure adopted was 78 x 10⁶ Pa (800 kg/cm²). Since the permeation of the melt and the coagulation of the melt were completed within about 1 minute, the formed composite material was removed from the mold. Then, the composite material was subjected to a solution treatment at 515 to 550°C and then cooled with water. Then, the composite material was tempered at about 170°C for 8 hours and test pieces (gauge length = 50 mm, parallel portion length = 60 mm, diameter = 14 mm) were cut out from the composite material. The tensile strength and the modulus of elasticity were measured. The obtained results are shown in Table 2. As is seen from the results shown in Table 2, the strength of the aluminum whisker was sufficiently manifested. For comparison, according to the above-mentioned procedures, composite materials having VF of 20% were prepared by using an alumina short fiber (ALCEN supplied by Denki Kagaku), potassium hexatitanate whisker (HT-300 supplied by Titan Kogyo), a silicon carbide whisker (supplied by Tateho Kagaku Kogyo) and a silicon nitride whisker (supplied by Tateho Kagaku Kogyo). The mechanical strength of each of these composite materials was measured. The obtained results are shown in Table 2. As is apparent from the results shown in Table 2, the mechanical strength of each of the so-obtained composite materials, except the composite material prepared by using the silicon carbide whisker, was substantially lower than that of the composite material prepared by using the aluminum borate whisker. Incidentally, since the silicon carbide whisker is much more expensive than the aluminum borate whisker, it is deemed that the aluminum borate whisker is superior as a general-purpose material. Example 11 A molded body having VF of 20 or 30% was prepared in the same manner as described in Example 10 except that a whisker of 2Aℓ₂O₃·B₂O₃ having a diameter of about 0.5 µm and a length of 10 to 20 µm was used, carboxymethyl cellulose was added as the organic binder and alumina sol was added as the inorganic binder. Then, a composite material was prepare by using this molded body and an aluminum spreading material (ISO: A Cu₄SiMg) as the matrix alloy, and the composite material was quenched by water cooling at 495 to 505°C. After natural aging, the composite material was subjected to hot extrusion to obtain a wire rod having a diameter of 12 mm. The mechanical properties of the composite material are shown in Table 3. From these results, it is seen that in the obtained composite material, the strength was sufficiently manifested. Example 12 A molded body (VF = 20%) of an aluminum borate whisker prepared in the same manner as described in Example 10 was treated in the same manner as described in Example 10 by using an aluminum cast material (ASTM: 336.0) as the aluminum alloy, whereby a composite material was obtained. The obtained composite material was subjected to a solution treatment at a temperature of about 510°C for 4 hours, annealed at a temperature of about 170°C for 10 hours and allowed to stand still at a temperature of 25, 200 or 300°C for 100 hours, and the tensile strength was measured at the same temperature as the standing temperature. Comparative Example 10 The aluminum cast material not combined with the whisker was allowed to stand still at the above-mentioned temperature for the above-mentioned time, and the tensile strength was measured at the same temperature. The obtained results are shown in Table 4. From the results shown in Table 4, it is seen that the composite material prepared by using the aluminum borate whisker as the reinforcer had a much higher hot strength than that of the unreinforced material and the product obtained in this example was especially suitably used at a place where the product was exposed to a high temperature.

Claims: A process for producing an aluminium or aluminium alloy-based composite material, which comprises mixing a powder of aluminium or an aluminium alloy with an aluminium borate whisker such that the content of the whisker in the mixture is 5 to 40% by volume, pressure-moulding and firing or charging into a mould and firing under compression the mixture at a temperature of 500 to 650°C, or mixing an aluminium borate whisker with a binder containing water such that the content of the whisker in the mixture is 3 to 40% by weight, pressing, drying and firing the mixture to form a pre-formed body and infiltrating the pre-formed body of an aluminium borate whisker with a melt of aluminium or an aluminium alloy under a pressure of 4.9-196x10⁶ Pa (50 to 2000 kgf/cm²), the aluminium borate whisker having a diameter of 0.5 to 5 µm and a length of 5 to 200 µm. A process according to claim 1 which process comprises mixing the powder of aluminium or an aluminium alloy with the whisker such that the content of the whisker in the mixture is 5 to 40% by volume, pressure-moulding and firing or charging into a mould and firing under compression the mixture at a temperature of 500 to 650°C. A process according to claim 2 comprising pressure-moulding the mixture of the aluminium or the aluminium alloy powder and the aluminium borate whisker under the pressure of 49-196x10⁷ Pa (5 to 20 ton/cm²), and firing the moulded body units in an inert or in a reducing atmosphere. A process according to claim 2 comprising charging the mixture of the aluminium or the aluminium alloy powder and the aluminium borate whisker in a mould, and firing the mixture under compression of 4.9-49 x10⁷ Pa (500 to 5000 kgf/cm²). A process according to claim 1 which process comprises mixing the whisker with a binder containing water such that the content of the whisker in the mixture is 3 to 40% by weight, pressing, drying and firing the mixture to form a pre-formed body, and infiltrating the pre-formed body with a melt of aluminium or an aluminium alloy under a pressure of 4.9-196 x10⁶ Pa (50 to 2000 kgf/cm²). A process according to any one of claims 1 to 5, wherein the aluminium borate whisker has the chemical formula: 9Al₂O₃.2B₂O₃. A process according to any one of claims 1 to 5, wherein the aluminium borate whisker has the chemical formula: 2Al₂O₃.B₂O₃.

Inventors: HATA HAJIME, KITAMURA TAKAO C O AGENCY OF I, SAKANE KOHJI C O AGENCY OF IND, SOGABE SEIJI, WADA HIDEO C O AGENCY OF INDUS, HATA, HAJIME, KITAMURA, TAKAO, C/O AGENCY OF INDUSTRIAL SCIENCE, SAKANE, KOHJI, C/O AGENCY OF INDUSTRIAL SCIENCE, SOGABE, SEIJI,, WADA, HIDEO, C/O AGENCY OF INDUSTRIAL SCIENCE
Applicants: AGENCY IND SCIENCE TECHN, SHIKOKU CHEM, AGENCY OF INDUSTRIAL SCIENCE AND TECHNOLOGY, SHIKOKU CHEMICALS CORPORATION
Application year: 1990
Main classification: C22C1
IPC codes: C22C49