Oxygen delignification and enzyme treatment

Abstract: Process for bleaching lignocellulosic material comprising an oxygen bleaching treatment and an enzymatic treatment with a substantially cellulase-free xylanase which process is compatible with, and can be incorporated into, conventional bleaching sequences. The process provides a delignified and bleached pulp using lower amounts of chlorine-containing compounds, and the opportunity of eliminating the use of elemental chlorine, thereby reducing the polluting effluent from a pulp mill employing the process. Also, a greater extent of delignification can be achieved while retaining acceptable pulp strength properties.

Description: The present invention relates to a process for the bleaching of lignocellulosic material employing an oxygen treatment and an enzymatic treatment with xylanase. Lignocellulosic material in fibrous form is in wide commercial use as a raw material for the manufacture of paper, cardboard, construction board, etc. The raw material is usually wood whose principle components are cellulose, and a three-dimensional macromolecule - lignin, which is considered to be embedded in a matrix of cellulosic and hemicellulosic polysaccharides. It is generally accepted that the bonding that exists between the different components are established through linkages of different chemical nature. For instance, blocks of lignin are thought of as being associated through hemicellulose chains, the hemicellulose being another component of lignocellulosic material. In hardwoods, the predominant hemicellulose is glucuronoxylan, which includes a polymer of D -xylose, and hereinafter referred to as xylan. In order to produce strong and bleachable paper-making fibres, the lignocellulosic material must be treated to remove lignin, and normally, the initial part of this treatment takes place in a digester in the presence of chemicals such as sodium hydroxide and sodium sulphide (to produce a kraft pulp) or sulphites, usually sodium or magnesium, (to produce a sulphite pulp), thus producing chemical pulps. The removal of lignin is referred to as delignification. The lignin content of wood pulps is measured by a permanganate oxidation test according to a Standard Method of the Technical Association of the Pulp and Paper Industry (TAPPI), and is reported as a Kappa Number. The chemical pulp from the digester still contains an appreciable amount of residual lignin at this stage, and in some cases is suitable for making construction or packaging paper without further purification. For most applications, such as the manufacture of printing, writing and sanitary papers, however, the pulp is too dark in colour and must be brightened by bleaching. It is at this point, that the process of the present invention may be employed, i.e., in the process of bleaching lignocellulosic material, said material referred to hereinbefore as chemical pulp. The initial stages of bleaching also result in further delignification. The conventional method for further delignifying and bleaching pulp has been to employ a variety of multi-stage bleaching sequences, including anywhere from three to six stages, or steps, and with or without washing between steps. The objective in bleaching is to provide a pulp, in the case of chemical pulps, of sufficiently high brightness and strength for the manufacture of paper and tissue products. Characteristically, pulps of brightness 85% to 90% ISO are produced. Pulps of higher brightness can be produced from certain unbleached pulp types but at higher cost and at the risk or expense of pulp strength quality losses. The asymptotic limit of brightness that is encountered for a given pulp type in conventional bleaching processes is referred to herein as the brightness ceiling. This brightness ceiling is the brightness level, over which brightness the process of further bleaching would be considered too detrimental to the quality of the pulp, prohibitively uneconomical, or unachievable for certain materials. Traditionally, the bleaching sequences have been based on the use of chlorine and chlorine-containing compounds, in one form or another. Some of the chlorine-containing compounds that are used are chlorine, denoted C, chlorine dioxide, denoted D, and hypochlorites, denoted H, usually sodium hypochlorite. Chlorine, with or without admixture of chlorine dioxide, is commonly employed to initiate the bleaching of chemical pulp, followed by extraction of the chlorine-treated pulp in an aqueous alkaline medium, together denoted C-E. The chlorine charge (or chlorine plus chlorine dioxide charge, the chlorine dioxide expressed on a chlorine oxidizing equivalent basis) in the C stage is proportional to the lignin content (Kappa Number) of the pulp being treated. The alkaline extraction stage is used to solubilize and remove a major portion of the chlorinated and oxidized residual lignin, and also some hemicellulose is removed. With the advent of stricter environmental regulations designed to abate water and air pollution problems associated with chlorine-containing bleaching chemicals, coupled with the extensive recovery systems needed for the removal of chlorine-containing waste products, there is a distinct advantage in the reduction and preferably the avoidance of such chemicals in bleaching processes. Furthermore, if chlorine-containing waste is recycled through a kraft process black liquor recovery system, damage to the evaporator and furnace will result. A build-up of sodium chloride would also occur, causing damage to the furnace. Therefore, the pulp and paper industry has directed its attention to other bleaching chemicals which might avoid these problems. One of the significant advancements in the industry in the past two decades has been associated with the use of oxygen as a delignifying and bleaching agent. One application is the use of oxygen in conjunction with a conventional alkaline extraction stage, denoted Eo, following a chlorination. The alkaline extraction stage following the chlorination stage may contain other oxidative agents, such as peroxide (p) or hypochlorite (h) in combination with or in place of the oxygen. Such stages are accordingly denoted Epo, Eho, Ep or Eh, and each referred to generally as an oxidative extraction. The other main application of oxygen is for, primarily, delignification following the pulping digester and preceding bleaching and denoted O. Oxygen used in this fashion is applied to an unbleached pulp in alkaline medium under pressure. While the use of oxygen has provided alternative methods for delignification and bleaching, it is only of limited usefulness since it adversely affects the degree of polymerization of the cellulose, which is considered a drawback. The degree of polymerization of the cellulose is an indication of pulp strength and is measured as pulp viscosity by a TAPPI Standard Method. One criterion necessary for a bleaching stage is that the resultant pulp viscosity must not be substantially decreased. Generally, it is observed that only approximately up to 50% of the lignin remaining after pulping can be removed in this step with a pulp viscosity loss that is tolerable. Attempts at greater extents of delignification in this step are at the expense of further viscosity losses. The presence of magnesium ion in this step known to assist in minimizing these viscosity losses. The pulp viscosity losses are believed to arise from the chemical modification (degradation) of the cellulose and hemicellulose portions. Applications employing oxygen delignification have contributed to a reduction in the use of chlorine-containing compounds in bleaching sequences since the chemical charge in the chlorination stage is based upon the pulp lignin content, and this lignin content is reduced substantially (about 40% to 50%) by oxygen delignification. Enzymes have been studied for their use in the treatment of lignocellulosic material. For example, ligninolytic enzymes, particularly from white-rot fungi, have been shown to degrade lignin to varying degrees. Also, cellulase enzymes are well known to degrade cellulose and are of commercial interest in the food industry and in the manufacture of alcohols. In the manufacture of pulp for the purpose of paper-making, the effect of a cellulase enzyme would be detrimental owing to the resulting decrease in the degree of polymerization of the cellulose that would occur. In view of the hemicellulose component of lignocellulosic material, there have been studies reported on the effects of a xylanase enzyme on wood pulps. The xylanase expectedly selectively reacts with the xylan of the hemicellulose. FR-A-2,557,894 (published 1985) discloses a process for treating a hardwood bleached kraft or a softwood bleached sulphite chemical pulp with an enzyme solution containing xylanase to reduce the amount of subsequent beating or refining required for papermaking. Particularly large amounts of enzyme were required for the treatment of the bleached pulp in order to impart the desired effect. Further, the xylanase secreted by the basidiomycete mushroom Sporotrichum dimorphosphorum for use in the reduction of refining, was not cellulose-free and the detrimental cellulose activity was suppressed by the addition of mercuric chloride to the process. Owing to the known toxic and other harmful effects associated with exposure to mercury-containing compounds, their use is not acceptable. Chauvet et al . (Proceedings of the International Symposium on Wood and Pulping Chemistry, Paris, p. 325, 1987) reported on the use of a xylanase preparation obtained from the basidomycete mushroom Sporotrichum dimorphosporum for use as a pretreatment for a conventional chemical pulp bleaching sequence, C/D-E-D-E-D. The crude enzyme complex is treated with mercuric chloride to inactivate all polysaccharidase, except xylanase, activities. The pulp pretreatment comprises an enzymatic treatment followed by washing and subsequent aqueous acid soaking that results in up to a 14% Kappa number reduction for the hardwood sample. The pulp strength is not modified. The application of xylanase on hardwood and softwood kraft pulp for the purpose of brightness improvement and improved Kappa number reduction upon subsequent chemical treatment with hydrogen peroxide or in a bleaching sequence is discussed by Viikari et al . (Proceedings of The International Symposium on Wood and Pulping Chemistry, Paris, 1987). The xylanases are obtained by fermentation of a strain of fungus of the species Aspergillis awamori or by fermentation of bacterial strains of Streptomyces olivochromogenes or Bacillus subtilis . The xylanases exhibit both xylanase and xylosidase activities, except the xylanase from the latter bacterium which is xylosidase-free. The enzyme preparations contain traces of cellulase activity. A small brightness increases of 1.0 to 3.4 brightness points is observed with either the hardwood or softwood pulp after a hydrogen peroxide treatment following the enzymatic treatment. In many instances, the resulting pulp viscosities were preserved or only slightly lower. There is no indication as to the effect of the enzyme treatment alone on the pulp properties. Paice et al . (Biotech. and Bioeng., Vol. 32, p. 235-239, 1988) disclose a treatment of an unbleached hardwood pulp by a sequential xylanase treatment followed by a treatment with 1% on pulp sodium hydroxide. This two-step process provided a brightness increase and reduction in Kappa Number. Also, some, but not all of the brightness enhancement is retained after subsequent C-E-D bleaching. The xylanase was reportedly cellulase-free and produced by an E.coli clone. Surprisingly, we have now found that chemical pulp can be more effectively delignified and bleached in sequences including an oxygen delignification step and a xylanase treatment. Therefore, it is an object of the present invention to provide a process for increasing the extent of delignification of lignocellulosic material without incurring significant additional viscosity loss. It is a further object of the present invention to provide a process for the bleaching of lignocellulosic material using lower amounts of chlorine-containing bleaching agents than are conventionally employed, or essentially eliminating the use of elemental chlorine, thus providing a more environmentally acceptable process. It is yet a further object of the present invention to provide a process for the delignification and bleaching of lignocellulosic material that effectively raises the brightness ceiling of said material. Accordingly, in one aspect of the invention there is provided a process for bleaching and delignifying a lignocellulosic material which is a chemical pulp having xylanase hydrolysable xylosidic linkages by treating it with a sufficient amount of xylanase to effect the hydrolysis of said linkages, characterised in that the xylanase is substantially cellulase-free and said process includes a step of treating said material in an alkaline medium, before or after treatment with said xylanase, with oxygen or an oxygen-containing gas. Whereas the xylanase treatment may precede the oxygen treatment, in the generally preferred embodiment of the process according to the present invention the treatment with oxygen or an oxygen-containing gas precedes the treatment with xylanase. The treatment of the lignocellulosic material with oxygen or an oxygen-containing gas is carried out on a pulped material in aqueous suspension at a consistency selected in the range from about 3% to about 35% by weight, preferably from about 10% to about 30% by weight, with oxygen, or an oxygen-containing gas at a partial pressure of oxygen of from about 30-250 psig (207-1724 kN/m² gauge), particularly about 40-150 psig (276-1034 kN/m² gauge) and at a temperature in the range from about 70°C to about 170°C, preferably from about 100°C to about 150°C, more preferably from about 110°C to about 130°C, for a period of from about 10 to about 90 minutes, preferably from about 20 to about 60 minutes. The oxygen-containing gas employed in the process commonly will be air. The use of air requires higher pressure to be used than with oxygen. For example, air will be used at 150-250 psig (1034-1724 kN/m² gauge), whereas oxygen is effective at pressures of 30-150 psig (207-1034 kN/m² gauge). Also, oxygen gas may be allowed to form in situ . Oxygen may be supplied by the decomposition of hydrogen peroxide, and activators such as nitrogen dioxide can be employed in the oxygen treatment. The treatment with oxygen or an oxygen-containing gas is carried out in the presence of 1% to 20% by weight (based on said material) of an alkali or alkaline earth base. Preferably, the base is sodium hydroxide and used in an amount in the range 1% to 10% by weight. A viscosity preservative such as magnesium ion in an amount in the range 0.05% to 1.0% by weight may be added to the treatment with oxygen as defined hereinbefore. Suitable magnesium-containing compounds include magnesium sulphate, magnesium oxide, magnesium carbonate, and magnesium hydroxide. Other suitable additives to preserve viscosity may comprise complexing agents such as aminoalkylphosphonates and polyaminopolycarboxylates. The treatment of the lignocellulosic material with substantially cellulase-free xylanase is performed at a consistency of 1% to 20% by weight, preferably, 2% to 12%, at a concentration of xylanase in the range 1 to 500 IU/ml at a temperature in the range 20°C to 80°C for a period of 1 to 48 hours. Preferably the temperature is about 50°C. Further, the treatment is carried out in an aqueous medium at pH from about 4 to about 8. The medium is optionally buffered to control the pH. Suitable buffers include but are not limited to acetate buffer and acetate/citrate buffer. In the process according to the present invention, the xylanase is characterised as being substantially cellulase-free. By the term "substantially cellulase-free" is meant that there is not sufficient cellulase present to effect unfavourable hydrolysis of glucosidic linkages. This hydrolysis would be detrimental and unwanted in the treatment of lignocellulosic material for the purpose of improving the properties of said material in accordance with the process of the present invention herein defined. The amount of cellulase that may be tolerated depends on the particular objective in the practise of this invention. In one feature of the process according to present invention, the oxygen treatment and the xylanase treatment as described hereinbefore as accompanied by one or more additional treatments selected from the group consisting of (i) treatment in aqueous medium with chlorine, chlorine dioxide or mixtures thereof, (ii) treatment in aqueous medium with chlorine dioxide, (iii) treatment in aqueous alkaline medium with a peroxide, (iv) treatment in aqueous medium with hypochlorite, (v) treatment in aqueous medium with ozone, (vi) treatment in aqueous medium with nitrogen dioxide. Said one or more additional treatments may precede the oxygen and the xylanase treaatments, or may be employed as intervening treatments between the oxygen and the xylanase treatments, or may follow the oxygen and the xylanase treatments, or may be employed at a combination of these alternative timings. Preferably, in the process according to the present invention, said one or more additional treatments follow the oxygen and the xylanase treatments. In a further feature of the process according to the present invention, said process further comprises treating said bleached lignocellulosic material resulting from at least the oxygen and the xylanase treatments as described hereinbefore with an additional treatment selected from the group consisting of (i) extraction in aqueous medium with alkali base, and (ii) oxidative extraction in aqueous medium with alkali base. It is preferred that the oxygen and the xylanase treatments are followed by additional treatments comprising in sequence (i) treatment in aqueous medium with chlorine, chlorine dioxide or mixtures thereof, (ii) extraction or oxidative extraction in aqueous medium with alkali base, and (iii) treatment in aqueous medium with chlorine dioxide. In a further preferred embodiment, the oxygen and the xylanase treatments are followed by additional treatments comprising in sequence (i) treatment in aqueous medium with chlorine dioxide, and (ii) treatment in aqueous alkaline medium with hydrogen peroxide. It will be understood that in the process according to this preferred embodiment of the present invention, as well as in the process according those features and preferred embodiments described hereinbefore, the xylanase treatment may precede the oxygen treatment unless indicated otherwise. In a further aspect, the present invention provides a bleached lignocellulosic material produced by the processes as hereinbefore defined. In the practice of the process of the present invention the additional treatments are known in the art of pulp bleaching, both individually and in many instances in sequence, and can be carried out in any reasonable manner as is conventionally practised or known in the art. Preferred proceses of the present invention for the production of bleached pulp include the sequences defined by O-X-C/D-E-D, (wherein X denotes the xylanase treatment and C/D denotes treatment with chlorine, chlorine dioxide, or mixtures thereof), and the extraction stage (E) is optionally an oxidative extraction as defined hereinbefore. Alternatively, the process may be defined by the sequence O-X-D-P, wherein no elemental chlorine treatment is included. By the nature of the manufacture of chlorine dioxide, there is most frequently chlorine present, which need not be removed, and is not detrimental to the process of the present invention. The xylanase of use in the practice of the present invention is substantially cellulase-free and is obtained by the fermentation of any suitable xylanase-producing microorganisms such as a xylanase-producing bacterium. The microorganism may be a naturally occurring strain, or a mutant thereof, or a strain produced by genetic engineering, i.e. a recombinant strain, to increase the production of the xylanase and/or to produce a more pure xylanase mixture, e.g., substantially cellulase-free. Preferably, the xylanase is obtained substantially cellulase-free from a microorganism of the species Escherichia coli , Bacillus subtilis or of the genus Streptomyces , said microorganism having been genetically engineered to exhibit substantial cellulase negative activity. More preferably, the xylanase is obtained substantially cellulase-free from a recombinant xylanase gene-containing microorganism of the species Streptomyces lividans . For example, Mondue et al . (Gene, Vol. 49(3), p. 323-329, 1987) describes the preparation of a genetically engineered recombinant microorganism of the genus Streptomyces and the production of substantially cellulase-free xylanase therefrom that is suitable for use in the present invention. The recombinant microorganism may be obtained by the introduction of a hybrid plasmid into a host microorganism mutant strain of the genus Streptomyces , said strain characterised by it having cellulase-negative activity, said hybrid plasmid being constructed by the insertion of a xylanase gene into a suitable vector plasmid. The hybrid plasmid is capable of inducing the extracellular secretion of cellulase-free xylanase in a host microorganism into which said plasmid has been introduced. The hybrid plasmid can be constructed by any conventional methods, such as ligation, for the insertion of the required DNA fragment, the xylanase gene, into a vector plasmid. The xylanase gene may be obtained from known strain Streptomyces lividans 1326. A suitable vector plasmid is the known pIJ702, which which may be obtained from Streptomyces lividans 3131 . The hybrid plasmid may be introduced into the host micro-organism by the techniques of protoplast fusion or transduction or transformation. Accordingly, in a preferred embodiment of the present invention, xylanase that is substantially cellulase-free for use in the xylanase treatment of the lignocellulosic material is obtained by the homologous cloning of a xylanase ( xln ) gene of Streptomyces lividans 66 (strain 1326). The xylanase gene may be cloned by functional complementation of the xylanase-negative, cellulase-negative double mutant strain Streptomyces lividans 10-164 using the multicopy plasmid pIJ702. This cloning procedure is fully described by F. Mondue et al ., Gene 49 (3), p. 323-329 (1987) to provide one such clone Streptomyces lividans IAF28. Streptomyces lividans 3131 harbouring plasmid pIJ702 is on deposit at the American Type Culture Collection under Accession number APCC 35287. A deposit of Streptomyces lividans 1326, and of the double mutant strain Streptomyces lividans 10-164 has been made at the National Collection of Industrial and Marine Bacteria Limited, Aberdeen, UK on February 8, 1990, under Accession numbers NCIMB 40257 and NCIMB 40258, respectively. The expression of the xylanase (xln) gene and the production of the xylanase from the clone Streptomyces lividans IAF18 on natural substrates are described by J-L Bertrand et al ., Biotechnol . Bioengineering, 33 , p. 791-794 (1989). The purification and properties of the xylanase enzyme obtained in this instance are described by R. Morosoli et al ., Biochem. J. 239 , p. 587-592 (1986). In the fermentation of the xylanase-producing microorganisms a source of carbon is required in the culture medium that can affect the rate of production of xylanase. For example, in the production of substantially cellulase-free xylanase by the fermentation of a recombinant microorganism of the species Streptomyces lividans , the medium for use in the fermentation may contain hay, wheat straw, corn stover, xylan and/or brewer's spent grains as main carbon sources, together with suitable surfactants such as olive oil and/or Tween 80 (trade mark), as described by Kluepfel et al . in Proceedings of the 6th Canadian Bioenergy R & D Seminar, Vancouver, Canada (1987). Where an enzyme mixture containing xylanase also contains substantial amounts of cellulase, the cellulase is removed by any method known for the purification of xylanase, or the cellulase is selectively rendered inactive by any acceptable chemical or mechanical treatment. The xylanase may be applied as it is produced in a fermentation broth, or a concentrated mixture thereof, or as a mixture prepared from either a more concentrated mixture of the xylanase or a dried preparation of xylanase. The xylanase treatment of lignocellulosic material according to the present invention is carried out with or without agitation. At the end of the time period for said xylanase treatment, the resultant treated material may be used directly or thickened, and said treated material then used for further processing. Optionally, a wash is included. In further feature of the process of the present invention, a filtrate containing residual active xylanase from the thickening and/or washing following the xyalanse treatment is preferably recycled by applying said filtrate to the material to be treated with xylanase. The process of the invention provides a bleached product using lower amounts of chlorine-containing compounds, and the having satisfactory brightness and viscosity that is equivalent to or better than that observed for pulps bleached to the same extent by conventional methods. Also, higher brightness levels can be practically achieved using the process described herein, insofar as these brightness levels could only be achieved at the expense of significantly higher chlorine-containing chemical usage and/or detrimental loss of viscosity. The process described herein provides a bleached pulp using lower amounts of chlorine-containing compounds, and the opportunity of essentially eliminating the use of elemental chlorine, thereby reducing the polluting effluent from a pulp mill employing the process. The process according to the present invention provides the opportunity to recycle more organic material that is removed from the starting lignocellulosic raw material to a recovery process of a mill and thus reduce the pollution load of the bleaching process. In this specification all proportions and percentages are by weight of oven-dried material, unless otherwise stated. The tests characterising the treated material of this invention were carried out by the following Standard Methods. The invention is illustrated additionally by the following Examples but its scope is not limited to the embodiments shown therein. Examples 1 and 2 describe the production of the Streptomyces lividans clone IAF18. EXAMPLE 1 Chromosomal DNA was extracted from Streptomyces lividans 66 (strain 1326) and partially digested with Sau 3A. The resulting fragments were fractionated on a linear 10 to 40% sucrose gradient. The enriched fractions containing 4 to 10 kb fragments were pooled prior to ethanol precipitation. Vector plasmid pIJ702, obtained from Streptomyces lividans 3131, was digested to completion by Bgl II and the enzyme was removed by phenol-chloroform extraction. The plasmid was ethanol-precipitated and dephosphorylated as described by Kendall and Cullum (Gene; 29 , 315 (1984)). For ligation, a mixture of partially digested chromosomal Streptomyces lividans DNA fragments and dephosphorylated pIJ702 at a ratio of 5:1 were treated with 0.1 unit of T₄ DNA ligase overnight at room temperature at a concentration of 37.5 µg/ml. The Streptomyces lividans 1326 was mutated by using N-methyl-N'-nitro-N-nitrosoguanidine (Delic et al., Mutation Res.; 9 . 167 (1970)), and a double mutant β-1,4- D -glucan glucanohydrolase (endocellulase)-negative and xylanase-negative was selected. The double mutant was selected on a solid minimal medium containing 1% carboxymethyl-cellulose as main carbon source. Visualisation of endocellulase activity was achieved by Congo Red staining according to Teather and Wood, op. cit . The detection of xyalanso-negative mutants was carried out in the same manner substituting the carboxymethyl-cellulose by 1% oat spelts xylan. The Congo Red coloration was found to be applicable also for the detection of xylanase activity. In both cases, the absence of decoloration zones was taken as an indication for the absence of enzyme production. The double mutant Streptomyces lividans 10-164 was very stable, appeared to give the highest transformation efficiency and was therefore selected as the more preferred host microorganism for the development of the expression system. Protplasting and transformation of the double mutant Streptomyces lividans 10-164 was performed as described by Chapter et al . (Curr. Topics Microbiol. Immunol.; 97 , 69 (1982)). Transformed protoplasts were plated on R5 medium supplemented for melanin expression and overlayed with 3 ml of R5 medium containing 0.6% agar at 42°C. Transformants were selected for thiostrepton resistance after 16 hours at 30°C according to the procedure of Kendall and Cullum, op. cit . (1984). Screening of xylanase-positive clones was done using a minimal medium supplemented with RBB-xylan which was prepared according to Biely et al . (Anal. Biochem.; 144 , 142 (1985)). Colonies producing xylanase, hydrolyse this substrate creating clear zones. Two xylanase-producing clones were selected and designated Streptomyces lividans IAF18 and IAF30. Analysis by agarose gel electrophoresis of the plasmidic DNA material found in the Streptomyces lividans IAF18 and IAF30 demonstrated that all the plasmids found were larger than pIJ702, i.e. plasmids pIAF18 and pIAF30 had inserts of 5.7 and 6.7 kb, respectively. These hybrid plasmids were used to retransform the double mutant Streptomyces lividans 10-164. In all cases, 100% of the transformants were positive for the enzymatic activity previously scored indicating that the presumptive xylanase ( xln ) gene was plasmid-linked. Restriction mapping of the plasmids pIAF18 and pIAF30 revealed a discrepancy between the two inserts as to the restriction sites. However, Southern blotting, using as a probe the Bam HI- Sph I restriction fragment internal to the insert pIAF18 showed that about 2kb of DNA was common to the two inserts. The expression of the xln gene was studied by submerged cultures of the different clones in TSB (trypticase soy broth) and in xylan medium and compared to the wild-type strains Streptomyces lividans 1326 and 3131. The xylan medium, referred to as M13, consists of: xylan (from oat spelts; Sigma Chemical Co., St. Louis, MO, U.S.A.), 10 g; (NH₄)₂SO₄, 1.4 g; K₂HPO₄, 2.5 g; KH₂PO₄, 1.0 g; yeast extract (Difco), 2 g; proteose peptone (Difco), 1 g; MgSO₄.7H₂O, 0.3 g; CaCl₂.3H₂O, 0.3 g; Tween 80, 2 ml; and 1 ml of a trace metal solution containing CoCl₂.6H₂O (200 mg), FeSO₄.7H₂O (500 mg), MnSO₄.H₂O (160 mg) and ZnSO₄.7H₂O (140 mg), all dissolved in 100 ml of distilled water acidified to pH3. An incubation temperature of 34°C was chosen since it afforded a good ratio of growth to xylanase activity (Kluepfel et al ., Appl. Microbiol. Biotechnol.; 24 , 230 (1986)). The results are shown in Table 1 for 48h and 72h of incubation. The wild-type strain, whether it carried the plasmid pIJ702 or not, produced no enzyme activity when grown in TSB and the levels produced in xylan medium varied between 3 and 6 IU/ml of culture filtrate. The clones IAF18 and IAF30 showed significant activity in TSB(0.9-4.5 IU/ml) even in the absence of any inducer. Clones IAF18 and IAF30 grown in xylan medium produced very high levels of xylanase, e.g. IAF18 reached 380 UI/ml. In the intracellular fraction of all cultures, only trace amounts of xylanase activity were detected, indicating an efficient secretion The culture supernatant concentrates of strain Streptomyces lividans 3131, and clones IAF18 and IAF30 after induction with xylan were analyzed for secreted xylanase by SDS-9% PAGE after staining with Coomassie Blue. The xylanase-like products of these clones had an estimated M r of 43,000. This value corresponded exactly to the M r of the native purified xylanase isolated from Streptomyces lividans 1326 (Morosoli et al ., 1986) indicating that both the clones had inserts coding at least for the complete structural gene. Furthermore, the identify of these proteins was confirmed immunologically in Western blotting experiments using antixylanase antibodies. EXAMPLE 2 The genetic stability of Streptomyces lividans IAF18 was investigated by testing the enzyme production in TSB and medium M13 containing 1% xylan (hereinabove defined) both in the presence and absence of thiostrepton. In both media, the enzyme levela obtained remained constant for at least ten consecutive transfers and were not affected by the absence of the antibiotic. The multicopy gene effect was observed in TSB were about 2 IU/ml were consistently measured after 24 h reaching 10 IU/ml after 48 hours. This level of production remained stable for several days and can be explained by the good stability of the enzyme at 34°C. The addition of glucose to the medium M13 clearly showed catabolite repression and enzyme production started when this sugar was exhausted, whereas xylose as main carbon source in the same medium yielded extracellular xylanase level of 800 IU/ml as obtained by using xylan alone, as shown in Table 2. Table 3 shows a comparison of enzyme production between the wild-type strain Streptomyces lividans 1326 and the clone Streptomyces lividans IAF18 on medium M13 containing 1% and 2% of xylan. The former yielded 28 IU/ml with both concentrations whereas the latter secreted 1300 and 1600 IU/ml of xylanase respectively. EXAMPLE 3 The following example of a C/D-E-D-E-D sequence is provided for the purpose of comparison with sequences according to the present invention. 150 grams, oven-dried basis, of an unbleached hardwood kraft pulp of Kappa Number 14.1, viscosity 49.1 mPa.s and brightness 34.3% ISO was bleached by a conventional C/D-E-D-E-D bleaching sequence. The chemical charges were as follows: C/D stage : 2.81% chlorine, 0.12% chlorine dioxide at 50°C for 30 minutes on pulp at 3.0% consistency. E₁ stage : 1.56% sodium hydroxide at 70°C for 60 minutes on pulp at 10% consistency. D₁ stage : 0.8% chlorine dioxide, 0.45% sodium hydroxide at 70°C for 3 hours at 6.0% consistency. E₂ stage : 0.4% sodium hydroxide at 70°C for 60 minutes on pulp at 10% consistency. D₂ stage : 0.1% chlorine dioxide at 70°C for 3 hours on pulp at 6.0% consistency. The pulp after the final chlorine dioxide stage had the following properties: Brightness 90.0% ISO Viscosity 31.9 mPa.s EXAMPLE 4 The following example of an O-C/D-E-D sequence is provided for the purpose of comparison with sequences according to the present invention. 150 grams, oven-dried basis, of an unbleached hardwood kraft pulp of Kappa Number 14.1, viscosity 49.1 mPa.s and brightness 34.3% ISO were combined with 2.5% sodium hydroxide and sufficient water to give a consistency of 10% while stirring in a Hobart mixer. The pulp was then transferred to a medium consistency oxygen reactor. In the reactor the pulp was treated with oxygen-gas at a pressure of 60 psig (414 kN/m² gauge) at a temperature of 100°C for a period of 60 minutes. The pulp was found to have a final pH of 11.4. After dilution to 4% consistency, the pulp was filtered, washed with water at 1% consistency and filtered again. The washed pulp had the following properties: Kappa Number 8.3 (41% lower than unbleached) Viscosity 25.6 mPa.s Brightness 50.1% ISO The oxygen-treated pulp was then further bleached by the C/D-E-D sequence, the chemical charges and conditions being as follows: C/D stage : 1.65% chlorine, 0.07% chlorine dioxide at 50°C for 30 minutes on pulp at 3.0% consistency. E stage : 0.82% sodium hydroxide at 70°C for 60 minutes on pulp at 10% consistency. D stage : 0.25% chlorine dioxide, 0.05% sodium hydroxide at 70°C for 3 hours on pulp at 6.0% consistency. The pulp bleached by the O-C/D-E-D sequence had the following properties: Brightness 89.9% ISO Viscosity 18.9 mPa.s EXAMPLE 5 The following example of an X-C/D-E-D sequence is provided for the purpose of comparison with sequences according to the present invention. The xylanase treatment step will be designated by "X" in the sequences. 50 grams of the unbleached hardwood kraft pulp of Example 3, Kappa Number 14.1, viscosity 49.1 mPa.s and brigntness 34.3% ISO, was treated with cellulose-free xylanase obtained from the aforesaid clone Streptomyces lividans IAF18 described in Examples 1 and 2. The treatment was carried out at 3% pulp consistency at 50°C for 16 hours with agitation at 250 rpm in buffered aqueous 0.1 M sodium acetate solution, pH 5, and a concentration of xylanase of 150 IU/ml. Following the enzyme treatment, the pulp was filtered, washed at 1% consistency and filtered again. The washed pulp had the following properties: Kappa Number 10.8 (23% lower than unbleached) Viscosity 53.5 mPa.s Brightness 40.1% ISO The xylanase-treated pulp was then further bleached by the C/D-E-D sequence. The chemical charges and conditions were as follows: C/D stage : 2.14% chlorine, 0.09% chlorine dioxide at 50°C for 30 minutes on pulp at 3.0% consistency. E stage : 1.2% sodium hydroxide at 70°C for 60 minutes on pulp at 10% consistency. D stage : 1.0% chlorine dioxide at 70°C for 3 hours on pulp at 6.0% consistency. The pulp bleached by the X-C/D-E-D sequence had the following properties: Brightness 90.8% ISO Viscosity 30.3 mPa.s EXAMPLE 6 The following example is provided for comparison purposes only. The unbleached hardwood kraft pulp of Example 4 was subjected to an oxygen treatment as in Example 4. The oxygen-treated pulp was then treated under the conditions of the xylanase treatment as outlined in Example 5 except that no xylanase was present. The pulp was then filtered, washed with water at 1% consistency and filtered. The washed pulp had the following properties: Kappa Number 8.0 Viscosity 25.6 mPa.s Brightness 52.5% ISO Thus it can be seen that the oxygen-buffer sequentially treated pulp has the same Kappa Number and viscosity characteristics as the oxygen-treated pulp of Example 4. The buffer treatment has essentially no effect on these pulp properties. EXAMPLE 7 The following is an example of an O-X-C/D-E-D sequence. The unbleached hardwood kraft pulp of Example 4 was subjected to an oxygen treatment as in Example 4. The oxygen-treated pulp was then subjected to a xylanase treatment as in Example 5. After washing, the oxygen-xylanase-treated pulp had the following properties: Kappa Number 5.3 (62% lower than unbleached) Viscosity 26.6 mPa.s Brightness 55.9% ISO The oxygen-xylanase-treated pulp was then further bleached by the C/D-E-D sequence. The chemical charges and conditions were as follows: C/D stage : 1.05% chlorine, 0.044% chlorine dioxide at 50°C for 30 minutes on pulp at 3.0% consistency. E stage : 0.59% sodium hydroxide at 70°C for 60 minutes on pulp at 10% consistency. D stage : 0.1% chlorine dioxide, 0.05% sodium hydroxide at 70° C for 3 hours on pulp at 6.0% consistency. The pulp bleached by the O-X-C/D-E-D had the following properties: Brightness 90.5% ISO Viscosity 25.7 mPa.s The Kappa Number listed for the oxygen treatment alone in Example 4 is 8.3, which is a 41% lowering from the unbleached Kappa Number. The Kappa Number listed for the xylanase treatment alone in Example 5 is 10.8, which is a 23% lowering from the unbleached Kappa Number. By comparison, the sequential oxygen-xylanase treatment of Example 7 provided a pulp of Kappa Number 5.3, which is a 62% lowering from the unbleached Kappa Number and convincingly demonstrates a synergistic effect between the two treatments based on their individual performances, which if taken as simply additive would have been expected to yield a Kappa Number of 6.4, which corresponds to a 55% lowering. Also, the C/D stage, E stage, and D stage chemical charges are each significantly decreased upon subsequent bleaching of the O-X treated pulp as shown in Example 7 for an O-X-C/D-E-D sequence, as compared to those chemical charges required for bleaching to a comparable or even lower final brightness in any one of the sequences C/D-E-D-E-D, O-C/D-E-D or X-C/C-E-D as illustrated by Examples 3, 4 or 5, respectively. EXAMPLE 8 The following is an example of an O-X-C/D-E-D sequence. The unbleached hardwood kraft pulp of Example 4 was subjected to a xylanase treatment as in Example 5, followed by an oxygen treatment as in Example 4. The X-O bleached pulp had the following properties: Kappa Number 5.3 (62% lower than unbleached) Viscosity 30.2 mPa.s Brightness 62.3% ISO The X-O treated pulp was then further bleached by the C/D-E-D sequence. The chemical charges and conditions were as follows: C/D stage : 1.05% chlorine, 0.044% chlorine dioxide at 50°C for 30 minutes on pulp at 3.0% consistency. E stage : 0.64% sodium hydroxide at 70°C for 60 minutes on pulp at 10% consistency. D stage : 0.15% chlorine dioxide at 70°C for 3 hours on pulp at 6% consistency. The pulp bleached by the X-O-C/D-E-D sequence had the following properties: Brightness 91.6% ISO Viscosity 21.8 mPa.s The Kappa Number listed for the X-O treated pulp in this Example 8 is the same as that obtained for the O-X treated pulp in Example 7 and illustrates that the synergistic effect between the two treatments exists regardless of the order of said treatments. Also, an improved brightness and greatly improved viscosity are obtained for this X-O treated pulp as compared to the O-X treatment or O treatment alone. This final brightness obtained in this X-O-C/D-E-D sequence is 91.6% ISO, which illustrates the effective raising of the brightness ceiling of the pulp using decreased amounts of chlorine and chlorine-containing bleaching chemicals and without introducing undesirable side effects. EXAMPLE 9 The following is an example of an O-X-D-E-D sequence. The unbleached hardwood kraft pulp of Example 4 was subjected to an oxygen treatment as in Example 4. The oxygen-treated pulp was then subjected to a xylanase treatment as in Example 5. The resulting pulp had the following properties: Kappa Number 4.6 (67% lower than unbleached) Viscosity 24.1 mPa.s Brightness 60.8% ISO The oxygen-xylanase-treated pulp was further bleached by the D-E-D sequence, the chemical charges and conditions were as follows: D₁ stage : 0.5% chlorine dioxide, 0.25% sodium hydroxide at 70°C for 3 hours on pulp at 6.0% consistency. E stage : 0.3% sodium hydroxide at 70°C for 60 minutes on pulp at 10% consistency. D₂ stage : 0.1% chlorine dioxide at 70°C for 3 hours on pulp at 6.0% consistency. The pulp bleached by the O-X-D-E-D sequence had the following properties: Brightness 90.3% ISO Viscosity 22.4 mPa.s Again, this Example 9 demonstrates the synergistic effect between the oxygen and xylanase treatments, whereby a 67% lowering of the unbleached Kappa Number is obtained in this instance. Also, an improved brightness is obtained with good viscosity after the O-X treatment. The process of the present invention as illustrated by Example 9 provides the opportunity for obtaining a high brightness fully bleached pulp using no elemental chlorine and maintaining good viscosity with, what would be considered by one skilled in the art as, relatively low chlorine dioxide charges. EXAMPLE 10 The following is an example of an O-X-D-P sequence. The unbleached hardwood kraft pulp of Example 4 was subjected to an oxygen treatment as in Example 4 followed by a xylanase treatment as in Example 5. The O-X bleached pulp had the following properties: Kappa Number 4.6 (67% lower than unbleached) Viscosity 24.1 mPa.s Brightness 60.8% ISO The O-X bleached pulp was then further bleached by the D-P sequence, the chemical charges and conditions were as follows: D stage : 1.0% chlorine dioxide, 0.2% sodium hydroxide at 70°C for 3 hours on pulp at 6.0% consistency. P stage : 0.1% hydrogen peroxide, 0.25% sodium hydroxide at 70°C for 60 minutes on pulp at 10% consistency. The pulp bleached by the O-X-D-P sequence had the following properties: Brightness 90.9% ISO Viscosity 20.3 mPa.s In this instance, a high brightness fully bleached pulp was obtained using only four treatment steps, and again no elemental chlorine. EXAMPLE 11 The unbleached hardwood kraft pulp of Example 4 was subjected to a sequential O-X-C/D-E-D treatment as outlined in Example 7 except that the final D stage chemical charges were 0.5% chlorine dioxide, 0.1% sodium hydroxide on pulp. The O-X-C/D-E-D bleached pulp had the following properties: Brightness 91.7% ISO Viscosity 25.1 mPa.s Example 11 further demonstrates the advantages outlined at Example 7 for the process of the present invention. In particular, in this instance, is the very high brightness obtained (91.7% ISO) at a good viscosity level (25.1 mPa.s). EXAMPLE 12 The unbleached hardwood kraft pulp of Example 4 was subjected to a sequential X-O-C/D-E-D treatment as outlined in Example 8 except that a final D stage charge of 0.08% chlorine dioxide on pulp was applied. The X-O-C/D-E-D bleached pulp had the following properties: Viscosity 24.1 mPa.s Brightness 60.8% ISO Example 12 further demonstrates the advantages outlined at Example 8 for the process of the present invention. The washing step following the xylanase treatment as is described in Example 5 hereinbefore is considered optional, but generally it is recommended that for prolonged storage of the enzyme-treated pulp, the wash be included, and the enzyme be denatured.

Claims: A process for bleaching and delignifying a lignocellulosic material which is a chemical pulp having xylanase hydrolysable xylosidic linkages by treating it with a sufficient amount of xylanase to effect the hydrolysis of said linkages, characterised in that the xylanase is substantially cellulase-free and said process includes a step of treating said lignocellulosic material in an alkaline medium, before or after treatment with the xylanase, with oxygen or an oxygen-containing gas. A process according to claim 1 wherein said lignocellulosic material is treated in aqueous suspension of consistency of 3 to 35% by weight with oxygen, or oxygen-containing gas, at an oxygen partial pressure of 207 to 1724 kN/m² gauge at 70 to 170°C for 10 to 90 minutes. A process according to claim 1 or claim 2 wherein said lignocellulosic material is treated in aqueous suspension of consistency of 1 to 20% by weight with 1 to 500 IU/ml of xylanase at 20 to 80°C for 1 to 48 hours. A process according to any one of claims 1 to 3 wherein said lignocellulosic material is also subjected to at least one of the following treatments: treatment in aqueous medium with chlorine and/or chlorine dioxide; treatment in alkaline medium in the presence of a peroxide; and treatment in aqueous medium with hypochlorite, ozone, or nitrogen dioxide. A process according to any one of claims 1 to 4 wherein the bleached lignocellulosic material is subjected to extraction, or oxidative extraction, in aqueous medium with alkali base. A process according to claim 4 wherein, after the treatments with xylanase and oxygen, or oxygen-containing gas, the lignocellulosic material is treated in aqueous medium with chlorine and/or chlorine dioxide, then subjected to extraction, or oxidative extraction, in aqueous medium with alkali base, and then treated in aqueous medium with chlorine dioxide. A process according to claim 4 wherein, after the treatments with xylanase and oxygen, or oxygen-containing gas, the lignocellulosic material is treated in aqueous medium with chlorine dioxide, and then treated in aqueous alkaline medium with hydrogen peroxide. A process according to any one of claims 1 to 7 wherein a wash step or thickening step is added following the treatment with xylanase to provide a filtrate containing residual active xylanase that is recycled by applying said filtrate to the lignocellulosic material to be treated with xylanase. A process according to any one of claims 1 to 8 wherein said xylanase is obtained from a recombinant microorganism produced by the introduction of a hybrid plasmid into a host mutant strain of Streptomyces lividans having substantial cellulase-negative activity, said hybrid plasmid being constructed by the insertion of a xylanase ( xln ) gene obtained from Streptomyces lividans 66 into the vector plasmid pIJ702. A process according to claim 9 wherein said host strain is the double mutant strain Streptomyces lividans 10-164 having substantial xylanase-negative activity.

Inventors: DU MANOIR JOHN RICHARD, DUBELSTEN PAUL AQUITAINE AVENU, DU MANOIR, JOHN RICHARD, DUBELSTEN, PAUL, 2700 AQUITAINE AVENUE
Applicants: ICI CANADA, ICI CANADA INC.
Application year: 1990
Main classification: D21C9
IPC codes: D21C9, D21C5, C12S3, C12N9