An electrolyte for use in electrolytic capacitors

Abstract: An electrolyte for use in electrolytic capacitors is provided. The electrolyte comprises a specified quaternary ammonium salt of a boric acid complex as a solute. A capacitor in which the electrolyte is used displays stable electrical characteristics at high temperatures as well as high sparking voltage and long life.

Description: BACKGROUND OF THE INVENTION 1. Field of the invention: The present invention relates to electrolytes for electrolytic capacitors and electrolytic capacitors using the said electrolytes. 2. Description of the prior art: Amine salts of phthalic acid or maleic acid are generally used as solutes contained in electrolytes for low voltage electrolytic capacitors with a rated voltage in the range of 6.3 to 100 V. Examples of the use of boron complexes of oxalic or maleic acid for this purpose are disclosed in Japanese Laid-Open Patent Publications Nos. 1-194313 and 1-157514. Adipic acid or its ammonium salt is used as a solute contained in electrolytes for intermediate voltage electrolytic capacitors with rated voltages in the range of 160 to 250 V. However, these electrolytes have the disadvantages of low specific conductivity as well as a further pronounced decrease of specific conductivity when exposed to high temperatures. With a view to avoiding this defect, examples of the use of quaternary ammonium salts of boric acid for this purpose are disclosed in Japanese Laid-Open Patent Publication No. 63-1021, while examples of the use of quaternary ammonium salts of catechol complexes of boric acid for this purpose are disclosed in USP 3,403,340. As solutes for the electrolytes of high voltage electrolytic capacitors with rated voltages in the range of 350 to 500 V, 1,6-decanedicarboxylic acid or its salts are generally used. However, if amine salts of phthalic or maleic acid, or boron complexes of oxalic acid, maleic acid or catechol are used as the solute, then, since the sparking voltage is low, the electrolyte cannot be used in capacitors with rated voltages in the range of 6.3 to 100 V. Moreover, if quaternary ammonium salts of boric acid are used, then, since the solubility with respect to aprotic solvents is low, various shortcomings arise, such as precipitation under low temperature conditions, etc. Furthermore, if alcoholic solvents such as ethylene glycol, etc., are used to dissolve these solutes, then esterification reactions proceed at high temperatures, resulting in pronounced increases in the water content of the electrolyte. This water in turn reacts with the aluminum composing the electrodes of capacitor elements, which causes marked deterioration of electrical characteristics and reduction in lifetime of the capacitors. If 1,6-decanedicarboxylic acid or its salts are used as solutes for the electrolytes for use in electrolytic capacitors, then the specific conductivity is low, and various problems arise, in particular, the impedance characteristics of the capacitor display marked adverse effects at low temperatures. US-A-3 585 459 discloses an electrolyte for use in electrolytic capacitors, which comprises as a solute an ionogen of a mixture of boric acid and a pentane diol in a molar ratio of 0.2-2, including a quaternary ammonium in an equimolar proportion. SUMMARY OF THE INVENTION An electrolyte of this invention for use in electrolytic capacitors, which overcomes the above-discussed and numerous other disadvantages and deficiencies of the prior art, is defined in claim 1. It comprises as a solute at least one kind of quaternary ammonium salt of a boric acid complex with an alcoholic-hydroxy containing compound, said quaternary ammonium salt being of the formula I: where n₁ is an integer of 1 or more; X₁ is a moiety selected from the group consisting of (i) a residue obtained by removing n₁ hydroxyl group or groups from a compound containing at least n₁ alcoholic hydroxyl groups, (ii) a group of the formula -Y₁-(O-R₁)₂ or Y₁-O-R₁, and (iii) a group of the formula I-A: wherein m₁ is an integer of zero or more, R₁′ is a residue obtained by removing two hydroxyl groups from a compound containing at least two alcoholic hydroxyl groups; Y₁ is a group selected from the group consisting of B-O-R₁)⁻·Q₁⁺ and B-, the Q₁⁺ being a quaternary ammonium ion, with the proviso that at least one of the Y₁ groups in the general formula I is B-O-R₁)⁻·Q₁⁺; and R₁s are independently hydrogen, alkyl, aralkyl, or derivatives thereof, said derivatives of alkyl and aralkyl containing at least one selected from the group consisting of hydroxy groups, ether linkages, ketone groups and S-containing groups, and said two R₁ groups or an R₁ and X₁ group may be joined together through a -O-B-O- group to form a ring structure containing boron. Another electrolyte of this invention for use in electrolytic capacitors is defined in claim 3. It comprises as a solute a mixture of at least one kind of quaternary ammonium salt of a boric acid complex with an alcoholic-hydroxy containing compound, and at least one kind of quaternary ammonium salt of a boric acid complex with hydroxycarboxylic acid, said quaternary ammonium salt being of the formula II: wherein n₂ is an integer of 1 or more; X₂ is a moiety selected from the group consisting of (i) a residue obtained by removing n₂ hydroxyl group or groups from a compound containing at least n₂ alcoholic hydroxyl groups, (ii) a group of the formula -Y₂-(O-R₂)₂ or Y₂-O-R₂, and (iii) a group of the formula II-A: wherein m₂ is an integer of zero or more, R₂′ is a residue obtained by removing two OH groups from a polyhydric alcohol or hydroxycarboxylic acid; Y₂ is a group selected from the group consisting of B-O-R₂)⁻·Q₂⁺ and B-, the Q₂⁺ being a quaternary ammonium ion, with the proviso that at least one of the Y₂ groups in the general formula II is B-O-R₂)⁻·Q₂⁺; and R₂s are independently hydrogen; alkyl; aralkyl; a residue of a hydroxycarboxylic acid compound of the formula wherein A is alkyl or aralkyl having at least one hydroxyl group and optionally having at least one carboxyl group, or derivatives thereof; said derivatives of alkyl, aralkyl and containing at least one selected from the group consisting of hydroxy groups, ether linkages, ketone groups, N-containing groups and S-containing groups, and said two R₂ groups or an R₂ and X₂ group may be joined together through a -O-B-O- group to form a ring structure containing boron. Another electrolyte of this invention for use in electrolytic capacitors is defined in claim 7. It comprises as a solute at least one kind of quaternary ammonium salt of a boric acid complex with phosphoric acid and/or phosphoric acid ester, said quaternary ammonium salt being of the formula III: where n₃ is an integer of 1 or more; X₃ is a moiety selected from the group consisting of (i) a residue obtained by removing n₃ hydroxyl groups from phosphoric acid and/or phosphate, (ii) a group of the formula Y₃-O-R₃, and (iii) a group of the formula III-A: wherein m₃ is an integer of zero or more, R₃′ is a residue obtained by removing two hydroxyl groups from phosphoric acid or ester thereof containing at least two alcoholic hydroxyl groups; Y₃ is a group selected from the group consisting of B-O-R₃)⁻·Q₃⁺ and B-, the Q₃⁺ being a quaternary ammonium ion, with the proviso that at least one of the Y₃ groups in the general formula III is B-O-R₃)⁻·Q₃⁺; and R₃s are independently hydrogen, a residue of phosphoric acid or ester thereof shown by formula III-B: wherein ℓ is 0 or 1; R₃″s are independently hydrogen, alkyl, aralkyl or derivatives thereof, said derivatives of alkyl and aralkyl containing at least one selected from the group consisting of hydroxy groups, ether linkages, and S-containing groups, and said two R₃ groups or an R₃ and X₃ group may be joined together through a -O-B-O- group to form a ring structure containing boron. Another electrolyte of this invention for use in electrolytic capacitors is defined in claim 9. It comprises as a solute at least one kind of quaternary ammonium salt of a boric acid complex with a monocarboxylic compound, said quaternary ammonium salt being of the formula IV: wherein n₄ in an integer or 1 or more; X₄ is a moiety selected from the group consisting of (i) a residue of a monocarboxylic acid compound of the formula wherein A is hydrogen, alkyl or aryl, and (ii) a group of the formula -Y₄-(-O-R₄)₂ or Y₄-O-R₄; Y₄ is a group selected from the group consisting of (iii) a group of the formula B-O-R₄) -. Q₄⁺ and (iv) B-, Q₄⁺ being a quaternary ammonium ion with the proviso that at least one of the Y₄ groups in formula IV is B-O-R₄) -. Q₄⁺, R₄ is selected from the group consisting of (v) hydrogen and (vi) a residue of an monocarboxylic acid compound of the formula wherein A is hydrogen, alkyl, aryl or derivatives thereof, said derivatives of alkyl and aryl containing at least one amino group; said two R₄ groups or an R₄ and X₄ group may be joined together through a -O-B-O- group to form a ring structure containing boron. In a preferred embodiment, the quaternary ammonium ion is asymmetric. The electrolytic capacitor of this invention comprises a capacitor element having an anode, a cathode and a separator disposed therebetween, wherein said capacitor element is impregnated with one of the above-mentioned electrolytes. Thus, the invention described herein makes possible the objectives of: (1) providing an electrolyte for electrolytic capacitors, in which the solute that is contained displays high solubility and a high degree of dissociation, and the electrolyte possess high specific conductivity; (2) providing an electrolyte for electrolytic capacitors, such that the electrolytes are free from defects such as marked increases in the water content of the capacitor system resulting from esterification of the solute, etc; (3) providing an electrolyte for electrolytic capacitors, such that capacitors in which the said electrolytes are used possess high sparking voltage, so that the said electrolytes are suitable for use in high voltage electrolytic capacitors; and (4) providing an electrolytic capacitor employing an electrolyte with the superior properties mentioned above, such that the said electrolytic capacitors display stable electrical characteristics at high temperatures as well as high sparking voltage and long life. BRIEF DESCRIPTION OF THE DRAWING This invention may be better understood and its numerous objects and advantages will become apparent to those skilled in the art by reference to the accompanying drawing as follows: Figure 1 is a perspective view of the capacitor elements in the electrolytic capacitors of the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS The present inventors have devoted intense research to the development of electrolytes with high specific conductivity which can form electrolytic capacitors with high sparking voltage and are stable at high temperatures, and have thereby succeeded in completing the present invention. The quaternary ammonium salt of a boric acid complex with an alcoholic-hydroxy containing compound used in the present invention is represented by the general formula I: where n₁ is an integer of 1 or more; X₁ is a moiety selected from the group consisting of (i) a residue obtained by removing n₁ hydroxyl group or groups from a compound containing at least n₁ alcoholic hydroxyl groups, (ii) a group of the formula -Y₁-(-O-R₁)₂ or Y₁-O-R₁, and (iii) a group of the formula I-A: wherein m₁ is an integer of zero or more, R₁′ is a residue obtained by removing two hydroxyl groups from a compound containing at least two alcoholic hydroxyl groups; Y₁ s a group selected from the group consisting of B-O-R₁) -. Q₁⁺ and B-, the Q₁⁺ being a quaternary ammonium ion, with the proviso that at least one of the Y₁ groups in the general formula I is B-O-R₁) -. Q₁⁺; and R₁s are independently hydrogen, alkyl, aralkyl, or derivatives thereof, said derivatives of alkyl and aralkyl containing at least one selected from the group consisting of hydroxy groups, ether linkages, ketone groups and S-containing groups. In the general formula I, the alcoholic-hydroxy containing compound which can form the X₁ can be classified into three categories, as follows. (1) Compounds possessing one alcoholic hydroxyl group; (2) Compounds having at least two vicinal alcoholic hydroxyl groups; and (3) Compounds having two or more alcoholic hydroxyl groups, and having no vicinal alcoholic hydroxyl groups. Examples of the compounds of category (1) include linear or branched, saturated or unsaturated aliphatic primary alcohols with 1 to 18 carbon atoms; saturated or unsaturated alicyclic primary alcohols; primary alcohols containing at least one ether linkage with a molecular weight of 76 to 10,000; and primary alcohols containing at least one hetero atom. The saturated or unsaturated aliphatic primary alcohols include methanol, ethanol, isopropanol, n-butanol, sec-butanol, tert-butanol, 2-ethylhexanol, allyl alcohol and propargyl alcohol. The saturated or unsaturated alicyclic primary alcohols include cyclohexanol, methylcyclohexanol, borneo and terpineol. The primary alcohols containing at least one ether group include polyalkylene glycol monoalkyl ether and polyoxyalkylenemono-ol disclosed in the specification of USP 4,116,846 such as Methyl cellosolve®, Ethyl cellosolve®, Butyl cellosolve®, Methyl carbitol®, Ethyl carbitol® and Butyl carbitol®. The primary alcohols containing at least one hetero atom include furfuryl alcohol, tetrahydrofurfuryl alcohol, thiophenmethanol, 2-mercaptoethanol, 4-hydroxy-2-butanone, hydroxyacetone and methylolacylamide. Benzyl alcohol can also be used. The compounds of above-mentioned category (2) can be shown by the following formula: wherein R's are independently hydrogen, alkyl, or aralkyl, or derivatives thereof, said derivatives of alkyl and aralkyl containing at least one selected from the group consisting of hydroxy groups, ether linkages and s-containing groups. As these compounds, it is possible to use saturated or unsaturated aliphatic polyols, saturated or unsaturated alicyclic polyols, sugar alcohol and polyols containing at least one ether group as follows. Examples of the aliphatic polyols include ethylene glycol, propylene glycol, ethylethylene glycol, 2,3-butanediol, pinacol, 1,2-hexanediol, 1,2-decanediol, 1,2-dodecanediol, glycerol, 1,2,4-trihydroxybutane, 1,2,3-heptatriol, 1,2,6-trihydroxyhexane, 1,2,3,4-tetrahydroxybutane, 1,2,7,8-tetrahydroxyoctane, 5-hexene-1,2-diol and 7-octen-1,2-diol. The alicyclic polyols include 1,2-cyclopentanediol, 1,2-cyclohexanediol, 1,2-cycloheptanediol, inositol, and 3,5-hexadiene-1,2-diol. The sugar alcohols include erythritol, ribitol, xylitol, sorbitol, mannitol and dulcitol. The polyols containing ether groups include 3-methoxy-1,2-propanediol, 3-ethoxy-1,2-propanediol, 3-propoxy-1,2-propanediol, 3-butoxy-1,2-propanediol, 3-phenylmethoxy-1,2-propanediol, 3-benzyloxy-1,2-propanediol, diglycerol and triglycerol. As the compounds of category (3), it is possible to use saturated or unsaturated aliphatic polyols, saturated or unsaturated alicyclic polyols, and polyols containing at least one ether groups with a molecular weight of 106 to 10,000, as described below. The aliphatic polyols are cis-2-butene-1,4-diol, trans-2-butene-1,4-diol, 2-butyne-1,4-diol, dimethylhexynediol, trimethylolpropane and pentaerythritol. The alicyclic polyols are 1,4-cyclohexanediol, cyclohexane-1,3,5-triol, and 4-cyclohexene-1,3-diol. The polyols containing at least one ether group are diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, tripropylene glycol, tetrapropylene glycol, polyethylene glycol, polypropylene glycol, polybutylene glycol, copolymer of ethylene glycol, propylene glycol or butylene glycol copolymer and polyoxyalkylenepolyol disclosed in USP 4,116,846. Furthermore, the sulfur-containing polyols thiodiethylene glycol and 2,2′-(decamethylenedithio)dimethanol; the nitrogen-containing polyols diethanolamine, N-methyldiethanolamine, triethanolamine, 1,4-bis(2-hydroxyethyl)piperazine and tris(hydroxymethyl)aminomethane; the phosphorus-containing polyols tris(hydroxymethyl)phosphinoxyde; and the polymers containing alcoholic hydroxyl groups polyhydroxyethyl, (meth)acrylate having a molecular weight of 234 to 45,000, polyvinylalcohol having a molecular weight of 90 to 45,000 and vinylalcoholhydroxyethyl (meth)acrylate copolymer having a molecular weight of 162 to 45,000 can also be used. Mixtures of alcoholic-hydroxy containing compounds from two or more of these categories may also be employed. For example, mixtures of compounds from categories 1 and 2, or 1, 2 and 3 may be used. In formula I the group R₁ can be selected from the group consisting of, hydrogen, straight-chain or branched alkyl with 1 to 18 carbon atoms, aralkyl, and derivatives thereof. The said derivatives of alkyl and aralkyl contain at least one selected from the group consisting of hydroxyl groups, ether linkage, ketone groups and sulfur-containing groups. Examples of the alkyl groups include methyl, ethyl, n-propyl, isopropyl, n-butyl, hexyl and octyl. Cycloalkyl groups such as cyclohexyl, cyclopentyl and methylcycloalkyl groups can also be used. Aralkyl groups include benzyl. Derivatives include furfuryl, tetrahydrofurfuryl, thiophenmethyl and residues of the above-mentioned alcoholic-hydroxy containing compounds (obtained by removing one hydroxyl group thereof). In addition, R₁s can be unsaturated hydrocarbon groups such as allyl, propargyl and crotyl. Examples of R₁′ include residues obtained by removing two hydroxyl groups from a compound containing two or more alcoholic hydroxyl groups in one of the categories 2 or 3 mentioned above. In formula I, the value of n₁ is ordinarily at least 1, preferably 1 to 8, and more preferably 1 to 3, while the value of m₁ is ordinarily at least 1, preferably 1 to 11 and more preferably 1 to 6. As the aforesaid quaternary ammonium salt of a boric acid complex with an alcoholic-hydroxy containing compound, the use of a compound such that two R₁ groups or R₁ and X₁ groups are joined together through a -O-B-O- group to form a ring structure containing boron is also appropriate. This type of compound is represented, for example, by the following formulae: wherein R₁, R₁′ and Q₁⁺ are as defined in formula I. As examples of the quaternary ammonium salt of a boric acid complex with an alcoholic-hydroxy containing compound, for example, salts obtained from quaternary ammonium hydroxide and a boric acid complex with an alcoholic-hydroxy containing compound, disclosed in U.K. Patent No. 1,323,312 and USP 4,192,759 are listed. Also, as compounds such that two R₁ groups or an R₁ and an X₁ group are joined to form a ring structure containing boron, for example, the compounds disclosed in U.K. Patent No. 1,341,901, are listed. In the compounds, a portion or all of the boron atoms in a boric acid ester are quaternary ammoniated. The mixture of at least one kind of quaternary ammonium salt of a boric acid complex with alcoholic-hydroxy containing compound and at least one kind of quaternary ammonium salt of boric acid complex with hydroxycarboxylic acid, which is used in the present invention, is represented by the general formula II: wherein n₂ is an integer of 1 or more; X₂ is a moiety selected from the group consisting of (i) a residue obtained by removing n₂ hydroxyl group or groups from a compound containing at least n₂ alcoholic hydroxyl groups, (ii) a group of the formula -Y₂-(-O-R₂)₂ or Y₂-O-R₂, and (iii) a group of the formula II-A: wherein m₂ is an integer of zero or more, R₂′ is a residue obtained by removing two OH groups from a polyhydric alcohol or hydroxycarboxylic acid; Y₂ is a group selected from the group consisting of B-O-R₂) -. Q₂⁺ and B-, the Q₂⁺ being a quaternary ammonium ion, with the proviso that at least one of the Y₂ groups in the general formula II is B-O-R₂) -. Q₂⁺; and R₂s are independently hydrogen; alkyl; aralkyl; a residue of a hydroxycarboxylic acid compound of the formula wherein A is alkyl or aralkyl having at least one hydroxyl group and optionally having at least one carboxyl group, or derivatives thereof; said derivatives of alkyl, aralkyl and containing at least one selected from the group consisting of hydroxy groups, ether linkages, ketone groups, N-containing groups and S-containing groups. As the hydroxycarboxylic acid constituting the groups R₂ and X₂ in the general formula II, the following hydroxycarboxylic acids such as aliphatic hydroxycarboxylic acids, alicyclic hydroxycarboxylic acids and heterocyclic hydroxycarboxylic acids can be used. Examples of aliphatic hydroxycarboxylic acids include monocarboxylic acids such as hydroxyacetic acid, glyceric acid, lactic acid, hydroxybutanoic acid, 3-hydroxyphenylbutanoic acid, 2-hydroxy-2-methylbutanoic acid, 2-hydroxy-2-ethylbutanoic acid, 2-hydroxyisobutanoic acid, 2-hydroxyvaleric acid, hydroxypivalic acid, 2,2-bis(hydroxymethyl)propionic acid, hydroxyisocaproic acid, 10-hydroxydecanoic acid, 12-hydroxydodecanoic acid, 12-hydroxystearic acid, mandelic acid, 2-, 3- or 4-hydroxyphenylacetic acid, 4-amino-3-hydroxybutanoic acid,, and gluconic acid; and polycarboxylic acids such as hydroxymalonic acid, hydroxysuccinic acid, dihydroxymalonic acid, 2-hydroxy-2-methylsuccinic acid, tartaric acid, mucic acid, citric acid, 3-hydroxy-3,4-dicarboxypentadecanoic acid and 2-hydroxy-12,3-nonadecanetricarboxylic acid. Examples of alicyclic hydroxycarboxylic acids include 1-hydroxy-1-cyclopropanecarboxylic acid and hexahydromandelic acid. Examples of heterocyclic hydroxycarboxylic acids include 2,6-hydroxyisonicotinic acid. In formula II, n₂ is generally 1 or more, preferably 1 to 8, more preferably 1 to 3; m₂ is generally zero or more, preferably 0 to 10, and more preferably 0 to 5. As the aforesaid quaternary salt of a boric acid complex with a hydroxycarboxylic acid, the use of a compound such that two R₂ groups or an R₂ and an X₂ group are joined together through a -O-B-O- group to form a ring structure containing boron is also appropriate. This type of compound is represented, for example, by the following formulae: wherein R₂, R₂′ and Q₂⁺ are as defined in formula II. The quaternary ammonium salt of a boric acid complex with phosphoric acid and/or phosphoric acid ester, which is used in the present invention, is represented by the general formula III: wherein n₃ is an integer of 1 or more; X₃ is a moiety selected from the group consisting of (i) a residue obtained by removing n₃ hydroxyl groups from phosphoric acid and/or phosphate, (ii) a group of the formula Y₃-O-R₃, and (iii) a group of the formula III-A: wherein m₃ is an integer of zero or more, R₃′ is a residue obtained by removing two hydroxyl groups from phosphoric acid or ester thereof containing at least two alcoholic hydroxyl groups; Y₃ is a group selected from the group consisting of B-O-R₃) -. Q₃⁺ and B-, the Q₃⁺ being a quaternary ammonium ion, with the proviso that in the group at least one of the Y₃ groups in the general formula III is B-O-R₃) -. Q₃⁺; and R₃s are independently hydrogen, a residue of phosphoric acid or ester thereof shown by the formula III-B: wherein ℓ is 0 or 1; R₃″s are independently hydrogen, alkyl, aralkyl or derivatives thereof, said derivatives of alkyl and aralkyl containing at least one selected from the group consisting of hydroxy groups, ether linkages, and S-containing groups. As the phosphoric acid esters constituting the groups R₃ and X₃ in formula III, phosphates formed by phosphorylation reactions of hydroxyl compounds and phosphoric acids (i. e., orthophosphoric acid, pyrophosphoric acid, etc.) are listed. Examples of the hydroxyl compounds are linear or branched, saturated or unsaturated aliphatic primary alcohols such as methanol, ethanol, isopropanol, n-butanol, sec-butanol, tert-butanol, 2-ethylhexanol, allyl alcohol and propargyl alcohol, as well as benzyl alcohol; saturated or unsaturated alicyclic primary alcohols such as cyclohexanol, methylcyclohexanol, borneol and terpineol; primary alcohols with a molecular weight of 76 to 10,000 containing at least one ether group including polyalkylene glycol monoalkyl ether and polyoxyalkylenemono-ol disclosed in the specification of USP 4,116,846 such as Methyl cellosolve®, Ethyl cellosolve®, Butyl cellosolve®, Methyl carbitol®, Ethyl carbitol® and Butyl carbitol®; primary alcohols containing at least one hetero atom such as furfuryl alcohol, tetrahydrofurfuryl alcohol, thiophenmethanol, 2-mercaptoethanol, 4-hydroxy-2-butanone, hydroxyacetone and methylolacrylamide; saturated or unsaturated aliphatic polyols such as ethylene glycol, propylene glycol, ethylethylene glycol, 2,3-butanediol, pinacol, 1,2-hexanediol, 1,2-decanediol, 1,2-dodecanediol, glycerol, 1,2,4-trihydroxybutane, 1,2,3-heptatriol, 1,2,6-trihydroxyhexane, 1,2,3,4-tetrahydroxybutane, 1,2,7,8-tetrahydroxyoctane, 5-hexene-1,2-diol and 7-octen-1,2-diol, ditrimethylene glycol, 1,3-butanediol, 1,4-butanediol, 2,4-pentanediol, 1,5-pentanediol, neopentyl glycol, 1,6-hexanediol, 2,5-hexanediol, 2-methyl-1,3-pentanediol, hexylene glycol, 2,2-dimethylolbutane, 2,4-heptanediol, 2-ethyl-1,3-hexanediol, 2-ethyl-2-n-butyl-1,3-propanediol, cis-2-butene-1,4-diol, trans-2-butene-1,4-diol, 2-butyne-1,4-diol, dimethylhexynediol, and trimethylolpropane; alicyclic polyols such as 1,2-cyclopentanediol, 1,2-cyclohexanediol, 1,2-cycloheptanediol, inositol, and 3,5-cyclohexadiene-1,2-diol, 1,4-cyclohexanediol, cyclohexane-1,3,5-triol and 4-cyclohexene-1,3-diol; suger alcohols such as erythritol, ribitol, xylitol, sorbitol mannitol, dulcitol and pentaerythritol; polyols containing at least one ether groups such as 3-methoxy-1,2-propanediol, 3-ethoxy-1,2-propanediol, 3-propoxy-1,2-propanediol, 3-butoxy-1,2-propanediol, 3-phenylmethoxy-1,2-propanediol, 3-benzyloxy-1,2-propanediol, diglycerol, triglycerol, polyols having a molecular weight of 120 to 10,000 including diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, tripropylene glycol, tetrapropylene glycol, polyethylene glycol, polypropylene glycol, polybutylene glycol, copolymer of ethylene glycol, propylene glycol or butylene glycol, and polyoxyalkylenepolyol disclosed in USP 4,116,846. Furthermore, sulfur-containing polyols such as thiodiethylene glycol and 2,2′-(decamethylenedithio)dimethanol; polymers containing alcoholic hydroxyl groups such as polyhydroxyethyl (meth)acrylate having a molecular weight of 234 to 45,000, polyvinylalcohol having a molecular weight of 90 to 45,000 and vinylalcohol-hydroxyethyl (meth)acrylate copolymer having a molecular weight of 162 to 45,000; and compounds containing one or more phenolic hydroxyl groups such as phenol, catechol, resorcinol, hydroquinone, phloroglucinol, pyrogallol, 1,2,4-trihydroxybenzene, cresol, naphtaol, nitrophenol, dinitrophenol, picric acid, nitrocatechol, nitroresorcinol and trinitroresorcinol can also be used. Either one type of these hydroxyl compounds or a combination of two or more types of the compounds can be used. In formula III, the value of n₃ is ordinarily at least 1, preferably 1-8, and more preferably 1-3, while the value of m₃ is ordinarily zero or more, preferably 0-10 and more preferably 0-5. As the aforesaid quaternary ammonium salt of the boric acid complex with phosphoric acid and/or a phosphoric acid ester, the use of a compound such that two R₃ groups or an R₃ group and an X₃ group are joined together through a -O-B-O- group to form a ring structure containing boron is also appropriate. This type of compound is represented, for example, by the following formulae. wherein R₃, R₃′ and Q₃⁺ are defined in formula III. Within the group R₃ of the formula III, the group R₃″ is, desirably, either a hydrogen or alkyl with 1 to 10 carbon atoms, alkyl with 1 to 4 carbon atoms being particularly desirable. The quaternary ammonium salt of a boric acid complex with monocarboxylic compound used in the present invention is represented by the general formula IV: wherein n₄ in an integer or 1 or more; X₄ is a moiety selected from the group consisting of (i) a residue of a monocarboxylic acid compound of the formula wherein A is hydrogen, alkyl or aryl, and (ii) a group of the formula -Y₄-(-O-R₄)₂ or Y₄-O-R₄; Y₄ is a group selected from the group consisting of (iii) a group of the formula B-O-R₄)⁻Q₄⁺ and (iv) B-, Q₄⁺ being a quaternary ammonium ion with the proviso that at least one of the Y₄ groups in formula IV is B-O-R₄)⁻·Q₄⁺, R₄ is selected from the group consisting of (v) hydrogen and (vi) a residue of an monocarboxylic acid compound of the formula wherein A is hydrogen, alkyl, aryl or derivatives thereof, said derivatives of alkyl and aryl containing at least one amino groups. Examples of the monocarboxylic acid constituting the compound of formula IV are linear or branched, saturated on unsaturated monocarboxylic acid such as formic acid, acetic acid, propionic acid, butyric acid, valeric acid, caproic acid, enanthic acid, caprylic acid, pelargonic acid, capric acid, undecanoic acid, lauric acid, tridecanoic acid, myristic acid, pentadecanoic acid, palmitic acid, heptadecanoic acid, stearic acid, nonadecanoic acid, arachidic acid, isobutanoic acid, isovaleric acid, isocaproic acid, ethylbutanoic acid, methylvaleric acid, isocaprylic acid, propylvaleric acid, ethylcaproic acid, isocapric acid, pivalic acid, 2,2-dimethylbutanoic acid, 2,2-dimethylpentanoic acid, 2,2-dimethylhexanoic acid, 2,2-dimethylheptanoic acid, 2-methyl-2-ethylbutanoic acid, 2-methyl-2-ethylpentanoic acid, 2-methyl-2-ethylhexanoic acid, 2-methyl-2-ethylheptanoic acid, 2-methyl-2-propylpentanoic acid, 2-methyl-2-propylhexanoic acid, acrylic acid, crotonic acid, isocrotonic acid, 3-butenoic acid, pentenoic acid, hexenoic acid, heptenoic acid, octenoic acid, nonenoic acid, decenoic acid, undecenoic acid, dodecenoic acid, 4-tetradecenoic acid, palmitoleic acid, petroselinic acid, oleic acid, elaidic acid, vaccenic acid, gadoleic acid, acrylic acid, methacrylic acid, 3-methylcrotonic acid, tiglic acid, methylpentenoic acid, cyclopentanecarboxylic acid, and cyclohexanecarboxylic acid; and aromatic monocarboxylic acid (including o-, m- and p-isomers) such as benzoic acid, toluic acid, ethylbenzoic acid, propylbenzoic acid, isopropylbenzoic acid, butylbenzoic acid, isobutylbenzoic acid, sec-butylbenzoic acid, tert-butylbenzoic acid, ethoxybenzoic acid, propoxybenzoic acid, isopropoxybenzoic acid, butoxybenzoic acid, aminobenzoic acid, N-methylaminobenzoic acid, N-ethylaminobenzoic acid, N-propylaminobenzoic acid, N-isopropylaminobenzoic acid, N-butylaminobenzoic acid, N-isobutylaminobenzoic acid, N,N-dimethylaminobenzoic acid, N,N-diethylaminobenzoic acid and nitrobenzoic acid; amino acid containing a carboxyl group such as glycine, alanine, valine, leucine, phenylglycine and phenylalanine. In formula IV, the value of n₄ is ordinarily at least 1, preferably 1-8, and more preferably 1-3. As the aforesaid quaternary ammonium salt of a boric acid complex with a monocarboxylic acid, the use of a compound such that two R₄ groups or an R₄ group and an X₄ group are joined together through a -O-B-O- group to form a ring structure containing boron is also appropriate. This type of compound is represented, for example, by the following formulae. Examples of quaternary ammonium ions constituting the quaternary ammonium salts represented by Formulae I to IV include tetraalkylammonium ion (containing 1 to 12 carbon atoms, independently in the alkyl groups) such as tetramethylammonium, tetraethylammonium, tetrapropylammonium, tetrabutylammonium, methyltriethylammonium, dimethyldiethylammonium and ethyltrimethylammonium; aryltrialkylammonium such as phenyltrimethylammonium; cyclohexyltrialkylammonium such as cyclohexyltrimethylammonium; and arylalkyltrialkylammonium such as benzyltrimethylammonium. Pyrrolidinium ions and piperidinium ions can also be used. Examples of these ions include N,N-dimethylpyrrolidinium, N,N-dimethylpiperidinium and N,N-pentamethylpiperidinium. Asymmetric tetra-alkylammonium ions such that at least one of the alkyl groups is different from the other alkyl groups are especially desirable. Applicable asymmetric tetra-alkylammonium ions include methyltriethylammonium, dimethyldiethylammonium and ethyltrimethylammonium ions. The aforesaid quaternary ammonium salt of the boric acid complex with an alcoholic-hydroxy containing compound can be synthesized by, for example, allowing a mixture of a quaternary ammonium salt of boric acid and an alcoholic-hydroxy containing compound to react and removing the water which is formed as a by-product. Alternative methods of synthesis include a method disclosed in U.K. Patent No. 1,323,312 and USP 4,192,759 as well as that disclosed in "Methods of Elemento Organic Chemistry," Volume 1 (A. N. Nesmeyanov and K. A. Kocheshkov, 1967), pp. 311-356. In this method, a complex formed by boric acid and an alcoholic-hydroxy containing compound with a quaternary ammonium hydroxide are mixed and the water which is generated as a by-product is removed, resulting in a desired product. In place of the boric acid complex, a metallic salt of the complex can be used and the metallic ion is substituted by the quaternary ammonium ion, removing the metallic compound which is generated as a by-product. The molar ratio of boric acid and the alcoholic-hydroxy containing compound is ordinarily 0.2-10 moles, more preferably, 0.5-5 moles of the alcoholic-hydroxy containing compound to 1 mole of boric acid. The molar ratio of boric acid and the quaternary ammonium hydroxide is ordinarily 0.5-1.5 moles, preferably, 0.8-1.2 moles of boric acid to mole of the quaternary ammonium. The presence of an excess of quaternary ammonium compound, for example, a quaternary ammonium hydroxide or a quaternary ammonium alkoxide, or a salt of another acid, is also permissible. Quaternary ammonium salts of other complexes used in the present invention can be synthesized by similar methods. Also, in quaternary ammonium salts of mixtures of boric acid complexes with alcoholic-hydroxy containing compounds and boric acid complexes with alcoholic-hydroxy containing hydroxycarboxylic acids, the molar ratio of alcoholic-hydroxy containing compound and hydroxycarboxylic acid should ordinarily be 0.1-10 moles, preferably 0.2-4 moles of hydroxycarboxylic acid to 1 mole of the alcoholic-hydroxyl containing compound. In the above-mentioned mixture of quaternary ammonium salts, a quaternary ammonium salt of a complex formed by intermolecule exchange of ligands can also be present in addition to the quaterrary ammonium salt of a boric acid complex with alcoholic-hydroxy containing compound and a boric acid complex with alcoholic-hydroxy containing oxdycarboxylic acid. The electrolytes of the present invention contain the above-mentioned quaternary ammonium salt and a solvent (ordinarily, an organic solvent). Examples of organic solvents include alcohols such as methyl alcohol, ethyl alcohol, propyl alcohol, butyl alcohol, diacetone alcohol, benzyl alcohol, amino alcohol, ethylene glycol, propylene glycol, diethylene glycol, hexylene glycol, glycerol and hexitols; ethers such as ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, ethylene glycol phenyl ether, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, diethylene glycol dimethyl ether and diethylene glycol diethyl ether; amides such as N-methylformamide, N,N-dimethylformamide, N-ethylformamide, N,N-diethylformamide, N-methylacetamide, N,N-dimethylacetamide, N-ethylacetamide, N,N-diethylacetamide, N,N-dimethylpropionamide and hexamethylphosphorylamide; oxazolidinones such as N-methyl-2-oxazolidinone and 3,5-dimethyl-2-oxazolidinone; lactones such as γ-butyrolactone, α-acetyl-γ-butyrolactone, β-butyrolactone, γ-valerolactone and δ-valerolactone; nitriles such as acetonitrile and acrylonitrile; dimethyl sulfoxide; sulfolane; 1,3-dimethyl-2-imidazolidinone; N-methylpyrrolidone; aromatic solvents such as xylene and toluene; paraffinic solvents such as n-paraffin and isoparaffin, and a mixture of at least two of these solvents. It is suitable to use a solvent comprising essentially γ-butyrolactone. Water may, when necessary, be included in the constituents of the electrolytes of the present invention to the extent that the complex (for example, a boric acid complex with an alcoholic-hydroxy containing compound) contained in the electrolytes is not hydrolyzed and transformed into simple boric acid. The permissible water content should ordinarily not exceed 5% by weight, preferably 3% by weight, or still more preferably 1% by weight of the entire electrolytic solution. The proportion of quaternary ammonium salt in the electrolytes of the present invention should ordinarily be 1-70% by weight, preferably 10-40% by weight, based on the total weight of the entire electrolytic solution. Various types of additives can be added to the electrolytes of the present invention for purposes such as the reduction of current leakage, absorption of hydrogen gas, etc. The additives include derivatives of phosphoric acid, derivatives of boric acid and nitro compounds. Using the aforesaid electrolytes, the capacitors of the present invention can be produced, for example, as follows. An aluminum anode foil 1, separator 3 made of paper or porous plastic film, an aluminum cathode foil 2 and another separator 3 are successively laminated in this order and wound as shown in Figure 1. The anode foil 1 and cathode foil 2 are then connected to the respective leads 4 to form the capacitor element. The aforesaid capacitor element are then impregnated with the aforesaid electrolyte, and the finished capacitor is obtained by sealing this element into a case of aluminum or other suitable material. The solutes appropriate for use in the electrolytes for electrolytic capacitors of the present invention include quaternary ammonium salts of a boric acid complex with an alcoholic-hydroxy containing compound; a mixture of quaternary ammonium salt of a boric acid complex with an alcoholic-hydroxy containing compound and quaternary ammonium salt of a boric acid complex with a hydroxycarboxylic acid; quaternary ammonium salts of a boric acid complex with phosphoric acid and/or a phosphoric acid ester; or quaternary ammonium salts of a boric acid complex with monocarboxylic acids. Owing to the use of these solutes, in all applicable voltage classes, including low, intermediate and high voltage, the electrolytes of the present invention display higher specific conductivity and higher sparking voltages then conventional types of electrolytes. Consequently, the electrolytes of the present invention permit the manufacture of long-life electrolytic capacitors with low dielectric losses and stable electrical characteristics at high temperatures. This type of capacitor is suitable for a wide range of applications in various industrial uses. In the following, the present invention will be described in greater detail with reference to specific examples, however, these examples are illustrative, and the scope of the present invention is not confined to these specific examples. In the following examples, unless otherwise indicated, parts and percentages are based on weight. Example 1 First, 20 parts of a boric acid salt of methyltriethylammonium hydroxide (prepared using 1.03 mole equivalents of boric acid with respect to methyltriethylammonium) were mixed with 19 parts of formic acid (4.0 mole equivalents with respect to boric acid), and a reaction was conducted at 60° C under a reduced pressure of 7 mmHg. Removal of by-product water was continued for 5 hours, thereby obtaining 29 parts of a methyltriethylammonium salt of boric-formic acid complex. An electrolyte was then obtained by dissolving 20% by weight of this methyltriethylammonium salt of boric-formic acid complex in γ-butyrolactone as a solvent. Example 2 A quaternary ammonium salt was obtained by a method similar to that in Example 1, and an electrolyte with the composition shown in Table 1-1 was prepared. Comparative Example 1 An electrolyte was obtained by dissolving 20% by weight of triethyamine salt of phthalic acid in γ-butyrolactone as a solvent as shown in Table 1-4. Example 3 A quaternary ammonium salt was obtained by a method similar to that in Example 1, except that 2.4 mole equivalents of ethylene glycol with respect to boric acid were used, and an electrolyte with the composition shown in Table 1-1 was prepared. Examples 4-9, and Comparative Example 2 Quaternary ammonium salts were obtained by methods similar to that in Example 3, and electrolytes with the compositions shown in Tables 1-1, 1-2 and 1-4 were prepared. Example 9 is not covered by the claims, but is presented as being useful for understanding the invention. Example 10 A quaternary ammonium salt was obtained by a method similar to that in Example 1, except that 1.2 mole equivalents of an adduct prepared from 1.0 mole of diglycerin and 2.0 moles of propyleneoxide were used with respect to boric acid, and an electrolyte with the composition shown in Table 1-2 was prepared. Example 11 First, 10 parts of a boric acid salt of methyltriethylammonium hydroxide (prepared using 1.03 mole equivalents of boric acid with respect to methyltriethylammonium) were mixed with 6.9 parts of dimethyl phosphate (1.0 mole equivalents with respect to boric acid) and 6.1 parts of monomethyl phosphate (1.0 mole equivalents with respect to boric acid), and a reaction was conducted at 60° C under a reduced pressure of 7 mmHg. Removal of by-product water was continued for 5 hours, thereby obtaining 19 parts of a mixture of a methyltriethylammonium salt of a boric acid-dimethyl phosphate complex and a methyltriethylammonium salt of a boric acid-monomethyl phosphate complex. An electrolyte was then obtained by dissolving 20% by weight of the said mixture of the methyltriethylammonium salt of a boric acid-dimethyl phosphate complex and the methyltriethylammonium salt of a boric acid-monomethyl phosphate complex in γ-butyrolactone as a solvent. Examples 12 and 13 Quaternary ammonium salts were obtained by methods similar to that in Example 11, and electrolytes with the compositions shown in Table 1-2 were prepared. Example 14 A quaternary ammonium salt was obtained by a method similar to that in Example 1, except that 2 mole equivalents of di(n-butyl) phosphate with respect to boric acid were used, and an electrolyte with the composition shown in Table 1-2 was prepared. Examples 15 and 16, and Comparative Example 3 Quaternary ammonium salts were obtained by methods similar to that in Example 14, and electrolytes with the compositions shown in Tables 1-2 and 1-4 were prepared. Example 17 First, 20 parts of a boric acid salt of methyltriethylammonium hydroxide (prepared using 1.03 mole equivalents of boric acid with respect to methyltriethylammonium) were mixed with 23.6 parts of 1,4-butanediol (2.4 mole equivalents with respect to boric acid), and a reaction was conducted at 60° C under a reduced pressure of 7 mmHg. Removal of by-product water was continued for 5 hours, thereby obtaining 35.3 parts of a methyltriethylammonium salt of a boric acid-1,4-butanediol complex. Also, 20 parts of a boric acid salt of methyltriethylammonium hydroxide (prepared using 1.03 mole equivalents of boric acid with respect to methyltriethylammonium) were mixed with 19.7 parts of lactic acid (2 mole equivalents with respect to boric acid), a reaction was conducted at 60° C under a reduced pressure of 7 mmHg, and by-product water was removed over a period of 5 hours, thereby obtaining 31 parts of a methyltriethylammonium salt of a boric-lactic acid complex. Next, 10 parts of the methyltriethylammonium salt of a boric acid complex with 1,4-butanediol complex and 10 parts of the methyltriethylammonium salt of a boric-lactic acid complex were dissolved in 50 parts of γ-butyrolactone as a solvent, then the solution was subjected to heat treatment for 2 hours at 80°C under a nitrogen gas current to obtain an electrolyte. Examples 18 and 21 Quaternary ammonium salts were obtained by methods similar to those in Example 17, and electrolytes with the compositions shown in Table 1-3 were prepared. Example 19 A quaternary ammonium salt was obtained by a method similar to that in Example 17, except that 1.2 mole equivalents of an adduct prepared from 1.0 mole of diglycerin and 2.0 moles of propyleneoxide were used with respect to boric acid, and an electrolyte with the composition shown in Table 1-3 was prepared. Examples 20 and 22 Quaternary ammonium salts were obtained by methods similar to those in Example 19, and electrolytes with the compositions shown in Table 1-3 were prepared. Comparative Examples 4-5 Electrolytes were prepared by the use of the solutes and solvents shown in Table 1-4. The compositions of the electrolytes of Examples 1-8 are shown in Table 1-1, those of Examples 9-16 in Table 1-2, those of Examples 17-22 in Table 1-3 and those of Comparative Examples 1-6 in Table 1-4, respectively. By the use of the electrolytes obtained in the aforesaid examples and comparative examples, the following measurements were carried out, respectively. Table 2 shows the sparking voltage, the specific conductivity at +30°C and the water content of the electrolytes for low voltage electrolytic capacitors obtained in Examples of the present invention as well as the corresponding properties for comparative examples, and in addition the loss tangent (referred to below as tan δ ) and current leakage (referred to below as LC), measured in high-temperature unloaded tests (125°C, 1000 hours), of electrolytic capacitors (100V, 470 µF) employing these electrolytes. Tables 3-1 and 3-2 show the sparking voltage, the specific conductivity at +30°C and the water content of the electrolytes for intermediate voltage electrolytic capacitors obtained in examples of the present invention as well as the corresponding properties for comparative examples, and in addition the values of tan δ and LC measured in high-temperature unloaded tests (125°C, 1000 hours), of electrolytic capacitors (200V, 100 µF) employing these electrolytes. Table 4 shows the sparking voltage, the specific conductivity at +30°C and the water content of the electrolytes for high voltage electrolytic capacitors obtained in examples of the present invention as well as the corresponding properties for comparative examples, and in addition the initial values of tan δ at +30°C and -25°C as well as the values of tan δ at 30°C measured after high-temperature unloaded tests (125°C, 1000 hours), of electrolytic capacitors (400V, 270 µF) employing these electrolytes. The listed values of the electrical characteristics (tan δ and LC) of the aforesaid electrolytic capacitors are mean values of 10 measurements. As is clearly demonstrated by the data in Tables 2-4, comparison of Examples 1-2 with Comparative Examples 1-2, comparison of Examples 3-8, 11-14 and 17-20 with Comparative Examples 3-5 and comparison of Examples 9-10, 15-16 and 21-22 with Comparative Example 6 all show that the capacitors of the present invention display higher sparking voltages as well as higher specific conductivities than those of the Comparative Examples. Moreover, as is clearly shown by the data in Table 4, the values of tan δ at a low temperature (-25°C) displayed by the listed electrolytic capacitors employing the electrolytes of the present invention are extremely low as compared with the corresponding low-temperature value of tan δ for the capacitor employing the electrolyte of Comparative Example 6, illustrating the superior electrical characteristics of the type of capacitor of the present invention. It is understood that various other modifications will be apparent to and can be readily made by those skilled in the art without departing from the scope of this invention as claimed.

Claims: An electrolyte for use in electrolytic capacitors, comprising a solute in an amount of 1 to 70% by weight based on the total weight of the electrolyte, wherein the solute is at least one kind of quaternary ammonium salt of a boric acid complex with an alcoholic-hydroxy containing compound, said quaternary ammonium salt being of the formula I: wherein n₁ is an integer of 1 or more; X₁ is a moiety selected from the group consisting of (i) a residue obtained by removing n₁ hydroxyl group or groups from a compound containing at least n₁ alcoholic hydroxyl groups, (ii) a group of the formula -Y₁-(-O-R₁)₂ or Y₁-O-R₁, and (iii) a group of the formula I-A: wherein m₁ is an integer of zero or more, R₁′ is a residue obtained by removing two hydroxyl groups from a compound containing at least two alcoholic hydroxyl groups; Y₁ is a group selected from the group consisting of B-O-R₁) -. Q₁⁺ and B-, the Q₁⁺ being a quaternary ammonium ion, with the proviso that at least one of the Y₁ groups in the general formula I is B-O-R₁) -. Q₁⁺; R₁s are independently hydrogen, alkyl, aralkyl, or derivatives thereof, said derivatives of alkyl and aralkyl containing at least one selected from the group consisting of hydroxy groups, ether linkages, ketone groups and S-containing groups, and said two R₁ groups or an R₁ and X₁ group may be joined together through a -O-B-O- group to form a ring structure containing boron; and said compound containing at least n₁ alcoholic hydroxyl groups being selected from the group consisting of: compounds possessing one alcoholic hydroxyl group; compounds having at least two vicinal alcoholic hydroxyl groups; cis-2-butene-1,4-diol, trans-2-butene-1,4-diol, 2-butyne-1,4-diol, dimethylhexynediol, trimethylolpropane, pentaerythritol, 1,4-cyclohexanediol, cyclohexane-1,3,5-triol, 4-cyclohexene-1,3-diol, diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, tripropylene glycol, tetrapropylene glycol, polyethylene glycol, polypropylene glycol, polybutylene glycol, copolymer of ethylene glycol, copolymer of propylene glycol, copolymer of butylene glycol, polyoxyalkylenepolyol, thiodiethylene glycol, 2,2′-(decamethylenedithio)dimethanol, diethanolamine, N-methyldiethanolamine, triethanolamine, 1,4-bis(2-hydroxyethyl)piperazine, tris(hydroxymethyl)aminomethane, tris(hydroxymethyl)phosphinoxide, polyhydroxyethyl (meth)acrylate having a molecular weight of 234 to 45,000, polyvinylalcohol having a molecular weight of 90 to 45,000 and vinylalcohol-hydroxyethyl (meth)acrylate copolymer having a molecular weight of 162 to 45,000. An electrolyte for use in electrolytic capacitors according to claim 1, wherein said quaternary ammonium ion is asymmetric. An electrolyte for use in electrolytic capacitors, comprising a solute in an amount of 1 to 70% by weight based on the total weight of the electrolyte, wherein the solute is a mixture of at least one kind of quaternary ammonium salt of a boric acid complex with an alcoholic-hydroxy containing compound, and at least one kind of quaternary ammonium salt of a boric acid complex with hydroxycarboxylic acid, said quaternary ammonium salts being of the formula II: wherein n₂ is an integer of 1 or more; X₂ is a moiety selected from the group consisting of (i) a residue obtained by removing n₂ hydroxyl group or groups from a compound containing at least n₂ alcoholic hydroxyl groups, (ii) a group of the formula -Y₂-(-O-R₂)₂ or Y₂-O-R₂, and (iii) a group of the formula II-A: wherein m₂ is an integer of zero or more, R₂′ is a residue obtained by removing two OH groups from a polyhydric alcohol or hydroxycarboxylic acid; Y₂ is a group selected from the group consisting of B-O-R₂) -. Q₂⁺ and B-, the Q₂⁺ being a quaternary ammonium ion, with the proviso that at least one of the Y₂ groups in the general formula II is B-O-R₂) -. Q₂⁺; and R₂s are independently hydrogen; alkyl; aralkyl; a residue of a hydroxycarboxylic acid compound of the formula wherein A is alkyl or aralkyl having at least one hydroxyl group and optionally having at least one carboxyl group, or derivatives thereof; said derivatives of alkyl, aralkyl and containing at least one selected from the group consisting of hydroxy groups, ether linkages, ketone groups, N-containing groups and S-containing groups, and said two R₂ groups or an R₂ and X₂ groups may be joined together through a -O-B-O- group to form a ring structure containing boron. An electrolyte for use in electrolytic capacitors according to claim 3, wherein said quaternary ammonium ion is asymmetric. An electrolyte for use in electrolytic capacitors according to claim 3, wherein said alcoholic-hydroxy containing compound has at least two vicinal alcoholic hydroxyl groups. An electrolyte for use in electrolytic capacitors according to claim 3, wherein said alcoholic-hydroxy containing compound is selected from the group consisting of cis-2-butene-1,4-diol, trans-2-butene-1,4-diol, 2-butyne-1,4-diol, dimethylhexynediol, trimethylolpropane, pentaerythritol, 1,4-cyclohexanediol, cyclohexane-1,3,5-triol, 4-cyclohexene-1,3-diol, diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, tripropylene glycol, tetrapropylene glycol, polyethylene glycol, polypropylene glycol, polybutylene glycol, copolymer of ethylene glycol, copolymer of propylene glycol, copolymer of butylene glycol, polyoxyalkylenepolyol, thipdiethylene glycol, 2,2′-(decamethylenedithio)dimethanol, diethanolamine, N-methyldiethanolamine, triethanolamine, 1.4-bis(2-hvdroxyethyl)piperazine, tris(hydroxymethyl)aminomethane, tris(hydroxymethyl)phosphinoxide, polyhydroxyethyl (meth)acrylate having a molecular weight of 234 to 45,000, polyvinylalcohol having a molecular weight of 90 to 45,000 and vinylalcohol-hydroxyethyl (meth)acrylate copolymer having a molecular weight of 162 to 45,000. An electrolyte for use in electrolytic capacitors, comprising a solute in an amount of 1 to 70% by weight based on the total weiaht of the electrolyte, wherein the solute is at least one kind of quaternary ammonium salt of a boric acid complex with phosphoric acid and/or phosphoric acid ester, said quaternary ammonium salt being of the formula III: wherein n₃ is an integer of 1 or more; X₃ is a moiety selected from the group consisting of (i) a residue obtained by removing n₃ hydroxyl groups from phosphoric acid and/or phosphate, (ii) a group of the formula Y₃-O-R₃, and (iii) a group of the formula III-A: wherein m₃ is an integer of zero or more, R₃′ is a residue obtained by removing two hydroxyl groups from phosphoric acid or ester thereof containing at least two alcoholic hydroxyl groups; Y₃ is a group selected from the group consisting of B-O-R₃) -. Q₃⁺ and B-, the Q₃⁺ being a quaternary ammonium ion, with the proviso that at least one of the Y₃ groups in the- general formula III is B-O-R₃) -. Q₃⁺; and R₃s are independently hydrogen, a residue of phosphoric acid or ester thereof shown by formula III-B: wherein ℓ is 0 or 1; R₃″s are independently hydrogen, alkyl, aralkyl or derivatives thereof, said derivatives of alkyl and aralkyl containing at least one selected from the group consisting of hydroxy groups, ether linkages, and S-containing groups, and said two R₃ groups or an R₃ and X₃ group may be joined together through a -O-B-O- group to form a ring structure containing boron. An electrolyte for use in electrolytic capacitors according to claim 7, wherein said quaternary ammonium ion is asymmetric. An electrolyte for use in electrolytic capacitors comprising a solute in an amount of 1 to 70% by weight based on the total weight of the electrolyte, wherein the solute is at least one kind of quaternary ammonium salt of a boric acid complex with a monocarboxylic compound, said quaternary ammonium salt being of the formula IV: wherein n₄ in an integer or 1 or more; X₄ is a moiety selected from the group consisting of (i) a residue of a monocarboxylic acid compound of the formula wherein A is hydrogen, alkyl or aryl, and (ii) a group of the formula -Y₄-(O-R₄)₂ or Y₄-O-R₄; Y₄ is a group selected from the group consisting of (iii) a group of the formula B-O-R₄)⁻·Q₄⁺ and (iv) B-, Q₄⁺ being a quaternary ammonium ion with the proviso that at least one of the Y₄ groups in formula IV is B-O-R₄) -. Q₄⁺, R₄ is selected from the group consisting of (v) hydrogen and (vi) a residue of an monocarboxylic acid compound of the formula wherein A is hydrogen, alkyl, aryl, or derivatives thereof, said derivatives of alkyl and aryl containing at least one amino group; said two R₄ groups or an R₄ and X₄ group may be joined together through a -O-B-O- group to form a ring structure containing boron. An electrolyte for use in electrolytic capacitors according to claim 8, wherein said quaternary ammonium ion is asymmetric. An electrolytic capacitor comprising a capacitor element having an anode, a cathode and a separator disposed therebetween, wherein said capacitor element is impregnated with an electrolyte of claim 1, 3, 7 or 9.

Inventors: KISHI TAKAAKI, MORI KEIJI, SAMURA HIDEO, SHIMAMOTO HIDEKI, SHIONO KATSUJI, TAKEISHI NOBUHIRO, USHIO NORIKI, WASHIO YUKARI, KISHI, TAKAAKI, MORI, KEIJI, SAMURA, HIDEO, SHIMAMOTO, HIDEKI, SHIONO, KATSUJI, TAKEISHI, NOBUHIRO, USHIO, NORIKI, WASHIO, YUKARI
Applicants: MATSUSHITA ELECTRIC IND CO LTD, SANYO CHEMICAL IND LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD., SANYO CHEMICAL INDUSTRIES, LTD.
Application year: 1990
Main classification: H01G9
IPC codes: H01G9