PROCESS FOR PREPARING HYDROXYALKYL ESTERS

Abstract: Hydroxyalkyl esters of acrylic and methacrylic acids are prepared by treating the acid with an appropriate alkylene oxide in the presence of a non-stoichiometric, amorphous catalyst of the formula: M(PO₄) y X′ Where in M is a transition metal, X′ is an anionic species to satisfy the valence requirements of M, and y is from about 0.1 to about 0.9.

Description: This invention is concerned with the use of heterogeneous metal catalysts in the production of unsaturated hydroxyalkyl esters. The catalyst art has long recognized the utility of certain phosphate and metal phosphate catalyst compositions. Among such materials are aluminum phosphates, both stoichiometric A1PO₄ and non-stoichiometric A1(PO₄) x where x is less than 1. For example, US-A-3,904,550 describes the preparation of such materials and their use as desulfurization catalysts. US-A-3,801,704 teaches that aluminum phosphates can be used for catalytic dehydration. US-A-4,524,225 demonstrates that such phosphates also function as hydrogenation catalysts. Other cited uses of aluminum phosphates include cracking (US-A-4,382,878), ether rearrangement (US-A-4,538,008), and polyolefin synthesis (US-A-4,364,839; 4,547,479; 4,424,139; 4,397,765; 4,596,862; 4,504,638; and or 4,364,854). In all of these cases stoichiometric non-stoichiometric aluminum phosphates are taught and methods for making them described. Among other phosphate-containing catalyst compositions described in the art are strontium compounds described in US-A-4,505,784 as useful for the synthesis of various amines and other nitrogen-containing compounds. Iron phosphates, usually both stoichiometric and crystalline, are also well known, but have none of the properties required for catalyst or catalyst support applications. For example, Tsuhako, et al., (Nippon Kagaku Kaishi, No. 2, 1980, pp. 176-180) describe the preparations and properties of eight crystalline iron phosphates all of which are stoichiometric and have PO₄/Fe ratios greater than 1.0. Leumann and Lutz (Galvanotechnik, Vol. 68, No.8, 1977, pp. 715-719), among others, have described the "iron phosphates" which are produced in the treatment of phosphate-containing wastewaters. Such materials are usually stoichiometric FePO₄ and, again, are not catalytic materials. The art has long recognized the utility of the addition of alkylene oxides to acrylic or methacrylic acid, always in the presence of appropriate inhibitors, to produce 2-hydroxyalkyl (meth)acrylates. A catalyst is always required for this addition. Catalysts mentioned in the art include ammonium salts (US-A-3,059,024), ammonium ion exchange resins (GB-A-1003346), phosphonium salts (DE-B-2527116 and 2527117), and lithium, sodium and potassium salts of the (meth)acrylate anion (Japanese Patent 7251382; French Patent 1556337; and US-A-3,214,988). A number of transition metal catalysts, as salts, are also known to the art, including copper (US-A-3,709,928), titanium (JP-B-6902686), vanadium (Japanese Patent 8187537), niobium or ruthenium (US-A-4,223,160), chromium (US-A-4,404,395), and iron (US-A-4,365,081). Of these catalysts, the iron salts are the ones most frequently taught in the art as catalyzing the production of 2-hydroxyalkyl (meth)acrylates from alkylene oxides and acrylic or methacrylic acid. The chromium salts are second most frequently taught in the art. GB-A-1003346, French Patents 1357422 and 1357423, US-A-3,804,884 and 3,340,295, Belgian Patent 657517, NL-A-6700738, and JP-B-7017662, all of which teach the use of ion exchange resins as catalysts, teach the use of heterogeneous (that is, insoluble throughout the reaction) catalysts in the production of 2-hydroxyalkyl (meth)acrylates from alkylene oxides and acrylic or methacrylic acid. Most often, the catalyst is soluble in the reactants and the products, and a separation step of the product from the catalyst is required. This discussion of the prior art is presented to show the various compositions and methods of preparing such compositions which are well known in the existing art, and to show the types of catalysts that are well known in the existing art to promote the formation of 2-hydroxyalkyl (meth)acrylates. These documents are only illustrative of a large body of patents and articles, but the documents cited are believed to reflect the teachings most relevant to this invention. It has now been found that certain inorganic, non-stoichiometric metal phosphates have special utility as heterogeneous catalysts and comprise compounds of the following formula: M(PO₄) y X' Where M is a transition metal, preferably with a +3 valence such as Fe⁺³ and Cr⁺³; y is the phosphate-to-metal mole ratio, which is in the range of from about 0.1 to 0.9, preferably from about 0.1 to about 0.6, and more preferably from about 0.1 to 0.3, X' represents other anionic species to satisfy the valence requirements of the metal. According to the present invention there is provided a process for preparing hydroxyalkyl esters of acrylic and methacrylic acid, which comprises treating the acrylic or methacrylic acid with an appropriate alkylene oxide in the presence of a non-stoichiometric, amorphous catalyst of the formula: M(PO₄) y X' wherein M is a transition metal, X' is an anionic species to satisfy the valence requirements of M, and y is from about 0.1 to about 0.9. An example of a stoichiometric metal phosphate is M⁺³(PO₄)₁, while M⁺³₁(PO₄) 0.5 is an example of a non-stoichiometric metal phosphate. Since the valence requirements of the metal M must be satisfied, these non-stoichiometric compositions contain additional anionic species, e.g. OH⁻ and O²⁻. Such compositions also contain water, either coordinated to the metal and hence an integral part of the structure, or present simply as incidental water of hydration. The catalysts are uniform and amorphous in nature and, specifically, are not simply mixtures of phosphate and oxide and/or hydroxide compounds. The surface characteristics of the catalysts used in the present invention contribute to excellent catalytic performance. The pore volume, pore size distribution and surface area necessary to have active catalysts are produced by proper control of key variables in the preparation process. Thus specific process steps and conditions are provided to achieve the desired results. For convenience in the following discussion of the catalyst, and its method of preparation, Fe⁺³ will often be used for the transition metal "M". However, it is to be understood that the use of Fe⁺³ is by way of exemplification only and is not intended to limit the scope of the transition metal "M". In general terms, the process for preparing the catalysts can be carried out as follows. First an aqueous ferric solution is prepared from a suitable iron salt. An appropriate phosphate source, e.g. orthophosphoric acid, is then added to the ferric solution. The resulting iron/phosphate solution is then mixed with and reacted with a pH-adjusting medium, preferably an alkaline solution such as dilute aqueous ammonia and the like, to effect gelation or precipitation of the desired non-stoichiometric metal slurry phosphate composition. Other orders of mixing are permitted. The pH, concentration, temperature, and mixing time will influence the stoichiometry and structure and hence the utility of the product obtained. The resultant slurry is then generally agitated for a period of time to assure complete reaction. The solid is then separated from the liquid phase by conventional methods such as filtration or centrifugation. Washing and drying may be done by any convenient means. The catalyst may now be formed into the appropriate shape and size. Finally, calcination may be conducted to remove excess water. Forming of the catalyst may, in some cases, be done most conveniently at an earlier stage, such as before washing or between washing and drying. Catalysts used in this invention have particular utility for certain industrially important catalytic processes involving the esterification of unsaturated carboxylic acids, in particular 2-hydroxyalkyl esters of acrylic and methacrylic acids. The catalysts used in this invention are heterogeneous catalysts for the production of these esters, and provide an advantage because the separation of the catalyst from the pure product requires only a filtering step. The catalysts are highly active and selective and provide unexpected advantages in the ease of production and the purity of the product. The catalysts employed in this invention are also characterized by their amorphous nature, that is there are no crystalline phases detected when these catalysts are examined by conventional x-ray diffraction methods. Further, the catalysts are uniform in nature in that separate phases of, for example, "FePO₄" and Fe₂O₃ or Fe(OH)₃ are not present. Additionally, the catalysts having surface areas and pore volumes greater than 100 m²/g and 0.1 cc/g, respectively, are most preferred. The catalysts can be prepared as irregular powders or granules, but most often will be used as regular shapes such as microspherical beads, larger beads, or particles with cylindrical cross-sections, as are commonly used in heterogeneous catalysis. While these catalysts can be used without dilution or the use of a support, such dilution can be desirable for economic reasons or to enhance the physical properties of the final product. Suitable for use as diluent or support materials are inert inorganic materials, particularly oxides such as silica, alumina and titania, which can be physically mixed with the catalysts at whatever stage of the preparation is most convenient. The inert "support" may be present at the point of gelation or precipitation. The level of diluent or support when employed may range from 10 to 90% w/w. A process for preparing the catalysts comprises the following steps: 1. Preparing a dilute aqueous solution of an appropriate metal salt; 2. Preparing a dilute aqueous solution of an appropriate phosphate; 3. Mixing 1 and 2, and, if required, adding pH adjuster; 4. Aging the resultant product slurry; 5. Separating the solid catalyst from the slurry; 6. Washing the solid catalyst; 7. Drying; 8. Forming the catalyst into the desired size and shape particles; adding an inert diluent if desired; and 9. Calcining, if required. Each of these steps will now be considered in more detail. The metal salt may be any water-soluble salt of the metal desired which has the needed valence (oxidation state). Salts of strong acids are particularly suitable. Thus, for example, ferric nitrate, ferric sulfate and ferric chloride are appropriate. In general, +3 oxidation state transition metals produce the preferred catalytic properties - Fe⁺³, Cr⁺³, Ce⁺³, and the like are preferred transition metals. The metal salt solution is usually dilute, having 1 to 10% solids by weight. The phosphate solution may be prepared separately from the metal salt solution, or may be prepared at the same time if the required PO₄/M mole ratio can be obtained without any reaction between the metal and phosphate. Suitable phosphate sources include orthophosphoric acid, ammonium phosphate, ammonium hydrogen phosphate and ammonium dihydrogen phosphate. This solution is also usually dilute, having 1 to 10% solids by weight. Mixing of these solutions is accomplished by any convenient means. Both can be added individually to a third pH-adjusting solution, or the combined metal/phosphate solution can be added to the pH-adjusting solution. The mixing must be done efficiently with relatively short mixing times to assure preparation of a homogeneous product. The pH-adjusting solution is most conveniently dilute aqueous ammonia, but other alkaline materials may be suitable. The final pH of the mixture should be 3 to 11; preferably 7 to 11; and most preferably 8 to 10. The mixing is usually carried out at ambient temperature, but a temperature as low as 0°C and as high as 100°C may enhance the physical properties of the product. Aging for a period of 1 to 24 hours at a temperature from about 25°C to about 100°C can also enhance the physical properties of the product. Adjustment of pH or salt content during such aging also can provide improved properties. Washing can be done by a decant-and-settle method or by washing on a centrifuge or filtration device. Washing is best done with deionized or distilled water. Drying is generally accomplished by conventional means such as forced hot air, vacuum or spray drying. The temperature should be controlled to avoid decomposition of the catalyst. Temperatures less than 200°C are preferred. Forming of the catalyst into the sizes and shapes of particles most suited to a particular application can be done by techniques well known in the art. Thus, spray drying, extrusion, pelleting or various spheroidization methods are effective. Inclusion of a diluent can be beneficial. Forming or dilution can be done various stages of the preparation as dictated by the requirements of the specific forming method chosen. Suitable diluents well known in the art can be used, but silica has been found to be particularly suitable. Finally, the preparation process can include a calcination step. Such calcination, normally in air but suitably done in other atmospheres such as nitrogen or H₂0-containing gases, will improve product strength and reduce the moisture content. Reducing moisture content is important from a catalytic standpoint, since H₂0 may participate in unwanted non-selective reactions. Calcination temperatures of 250-400°C produce the desired water loss without causing undesired changes in catalyst properties. As already stated, the present invention is concerned with the user of the catalysts for the esterification of unsaturated carboxylic acids, especially the 2-hydroxyalkyl ester of acrylic and methacrylic acids, from the acid and an appropriate alkylene oxide, in particular, ethylene oxide or propylene oxide. The catalysts may be used in any suitable reactor and may be used in batch or continuous processes. In a batch process the catalysts can be used at any effective level, usually from about 10 to about 70 wt% iron, preferably from 20 to 50 wt% iron, based on the initial weight of acid charged. In a continuous process the instantaneous catalyst/liquid weight ratio will be in the corresponding range. The reaction temperature is preferably from about 30°C to about 90°C, but more preferably from about 50° to about 70°C. The reaction is carried out in the presence of suitable polymerization inhibitors that are known in the art. Separation of the catalyst from the product is accomplished by any convenient means such as filtration, decantation, or centrifugation. It is desirable to recycle the catalyst, once separated. Separation of the catalyst from the product is improved over the prior art since the catalyst is essentially insoluble in the product. The alkylene oxide can be added in any convenient manner. Preferably, the alkyene oxide is added so the reaction is initially deficient in the alkylene oxide, with the total amount added being a 10% molar excess on the (meth)acrylic acid. The catalysts may be used in any convenient particle size. For a slurry process, particle size may range from a few micrometers to several millimeters. For fixed bed processes, as are well known in the catalyst art, particle size will normally be 1 to 10 mm. Factors other than reactor design, i.e., fixed bed versus slurry, may also influence the choice of particle size. Examples of such factors are diffusion, pressure drop or filterability, any of which may be important with a particular feed/product/process combination. The use of these catalysts provides an advantage over catalysts that are known in the art for the production of 2-hydroxyalkyl esters of acrylic and methacrylic acids. The catalysts show higher selectivity for the desired product as well as higher activity, with the advantage that the reaction may be run at lower temperatures. While the reaction temperature can vary widely, it will be lower than those required by prior art catalysts and will still be complete more quickly than when run in the presence of catalysts that are known in the art. This obviously lowers the energy required and is therefore a more economical process. EXAMPLES The present invention will now be further illustrated by way of the following Examples which are for illustrative purposes only and are not to be construed as imposing any limitation on the scope of the invention. The proportions are in parts by weight (pbw) or percent by weight (%/wt) unless otherwise indicated. Example 1 Catalyst Preparation A solution was prepared by dissolving 690g ferric sulfate hydrate and 75g of 85% H₃PO₄ in 3000g of deionized water. That solution was added dropwise to a well-stirred solution of 1468g of 28% aqueous ammonia in 12,450g of deionized water. The final solution had a pH of 10. The resultant flocculent brown precipitate was removed by filtration using a conventional vacuum filtration apparatus and washed with copious quantities of deionized water until the pH of the filtrate was about 7. The solid product was removed from the filter, dried in a forced air oven at 105°C and ground to the desired particle size before evaluation. Analysis showed stoichiometry of this product to be: Fe(PO₄) 0.2 0 1.2 (OH) 0.1 (H₂O) 1.2 0.2H₂0 The ground, sized product had a surface area of 261 m²/g and a pore volume of 0.18 cc/g. Example 2 Solubility of Catalyst The solubility of the product of Example 1 was evaluated in acrylic acid (AA) and hydroxyethylacrylate (HEA). AA and HEA are examples of the feed and product, respectively, of an esterification process in which the catalyst is useful. At 70°C no solubility was observed in HEA and at 70°C a solubility of only about 100 ppm in AA was observed. Even a relatively soluble catalyst would have only a limited life and would contaminate the product. Stoichiometric iron phosphates and oxides are very soluble in AA, HEA and similar organic acids and esters. Example 3 Effect of Calcining The product of Example 1 was calcined in air at 400°C for two hours. The physical properties of the material were unchanged, but its solubility in AA was further reduced to less than half that previously observed. To demonstrate the utility of the catalysts in the production of unsaturated esters, the following examples are presented. Example 4 Preparation of HEA A 500 ml Fischer-Porter reactor bottle equipped with a stirring bar was charged with the catalyst from Example 1 (2.8g). Acrylic acid (2.0g) was added and the reactor bottle was connected to a multiported reactor head (67% iron). The reactor was pressure tested, then evacuated. Ethylene oxide (4.7g) was added as a gas at room temperature to a predetermined pressure. Gas addition was halted and the reactor was heated to 50°C and held at that temperature for 1 hour. The catalyst was stirred in the solution throughout. The reactor was cooled to room temperature and the excess ethylene oxide was vented. A 20-minute nitrogen sparge of the product/catalyst mixture ensured additional removal of unreacted ethylene oxide. The mixture was filtered to remove catalyst and the resulting 2-hydroxyethyl-acrylate (HEA) was analyzed. The results, among those of ensuing Examples are presented in Table 1. Example 5 The procedure of Example 4 was repeated, except with less catalyst (1.9g, 46% iron), with methacrylic acid (2.0g) used in place of acrylic acid, and slightly less ethylene oxide added (3.8g). The reactor was heated to 70°C for 1 hour. The results for the product hydroxyethylmethacrylate (HEMA) are presented in Table 2. Example 6 The procedure of Example 4 was repeated, except propylene oxide (6.7g) was used in place of ethylene oxide. Since propylene oxide is a volatile liquid at room temperature, it was chilled to ice temperature, then added to the reactor by gas-tight syringe after the evacuation step. The nitrogen sparge time was increased to 1 hour to ensure removal of unreacted propylene oxide from the product solution. The results for the product hydroxypropylacrylate (HPA) are presented in Table 3. Example 7 The procedure of Example 6 was repeated, except methacrylic acid (2.0g) was used in place of acrylic acid, and the reaction was carried out for 1 hour at 70°C. The results for the product hydroxypropyl (meth)acrylate (HPMA) are presented in Table 3. Example 8 A 500 ml Fischer-Porter reactor bottle was equipped with a stirring bar and charged with the catalyst from Example 1 (72.9g). Acrylic acid (100.0g) and inhibitors were added and the reactor bottle was connected to a multiported reactor head (35% iron). The reactor was pressure tested, evacuated, then filled with 5% oxygen in nitrogen to 68.95k Pa gauge (10 psig) at room temperature. Ethylene oxide (72g) was added as a liquid at the reaction temperature (50°C), never exceeding 206.85 k Pa gauge (30 psig) in the reactor. The addition of the ethylene oxide occurred over approximately 1 hour, and the reactor remained at temperature another 2 hours. The catalyst was suspended in the stirred solution throughout the experiment. The reactor was vented, and the reactor was sparged with nitrogen for 30 minutes as the reactor was cooled to room temperature. The product was decanted from the catalyst and the resulting 2-hydroxyethylacrylate (HEA) was analyzed. The results presented in Table 1 are similar to those obtained for the smaller scale reaction, Example 4 except the yield of HEA is somewhat higher. Example 9 The procedure of Example 8 was repeated reusing the same catalyst recovered in Example 8. The results presented in Table 1 indicate the catalyst is effective when reused. Example 10 The procedure of Example 8 was repeated reusing the catalyst recovered in Example 9, which was washed with methanol and dried prior to this use. The results presented in Table 1 suggest that the catalyst when washed with methanol and reused is as effective as a fresh catalyst. Example 11 The procedure of Example 10 was repeated, except with methacrylic acid (100.0g) used in place of acrylic acid. The reactor was heated to 70°C. The results for the product hydroxyethylmethacrylate (HEMA) are presented in Table 2. Example 12 As an example that the catalysts, used in this invention, result in an improvement in product purity over a typical homogeneous catalyst taught in the art for the production of HEA, the procedure of Example 4 was followed with FeCl₃ (0.029g, 0.5% iron) as catalyst. The reactor was heated to 65°C for 2 hours. The results for the product hydroxethylacrylate (HEA) presented in Table 1 show that the catalysts, used in the present invention, are superior to those of the prior art. The yield of the desired product was higher and produced at a lower temperature and shorter time. Example 13 As an example that the catalysts, used in this invention, are significantly different from stoichiometric, commercially available iron phosphate, the procedure of Example 4 was followed eith FePO₄ - H₂0 (1.9g, 19.5% iron) as the catalyst for the reaction of acrylic acid (3.0) and ethylene oxide (4.6g). The reactor was heated to 65°C for 2 hours. The results for the product hydroxyethylacrylate (HEA), presented in Table 1, indicate the stoichiometric iron phosphate to be an unacceptable material. Example 14 The process of Example 1 was followed exactly through the precipitation step. The resultant flocculent brown precipitate %/wt was then washed using multiple slurry decant steps. After the final decantation the slurry contained about 6%/wt of the solid catalyst composition, Fe x (PO₄) y X'. Then 300g of this slurry was mixed with 100g of a commercially available silica and extruded using conventional, well known techniques. The 3.2mm (1/8'') diameter extruded catalyst is found to have a surface area of 167m²/g, a pore volume of 1.2 cc/g, and an average pore radius of 1.45 x 10⁻⁸m (145Å). Example 15 A solution was prepared by dissolving 69.0g ferric sulfate hydrate and 300.0g 85% orthophosphoric acid in 197g of deionized water. That solution was added slowly to a well stirred solution of 146g of 28% aqueous ammonia in 1245g of deionized water. The final slurry had a pH of 9.8. The resultant flocculent brown precipitate was separated from the mother liquor and washed with copious quantities of deionized water using a conventional vacuum filtration apparatus. The product was dried in a forced air oven. The dried product was found to have a BET surface area of 1.4m²/g and had a calculated PO₄/Fe ratio of 0.88. This very unsatisfactory low surface area demonstrates that only certain ranges of composition are suitable.

Claims: A process for preparing hydroxyalkyl esters of acrylic and methacrylic acid, which comprises treating the acrylic or methacrylic acid with an appropriate alkylene oxide in the presence of a non-stoichiometric, amorphous catalyst of the formula: M(PO₄) y X' Where M is a transition metal, X' is an anionic species to satisfy the valence requirements of M, and y is from 0.1 to 0.9. A process as claimed in Claim 1 wherein M is selected from Fe⁺³, Cr⁺³ and Ce⁺³. A process as claimed in Claim 1 wherein M is Fe⁺³. A process as claimed in any of Claims 1 to 3 wherein y is from 0.1 to 0.6 . A process as claimed in any of Claims 1 to 4 which is conducted at a temperature of from 30° to 90°C. A process as claimed in any of Claims 1 to 5 when used to prepare hydroxyethyl acrylate; hydroxypropyl acrylate; hydroxypropyl methacrylate; or hydroxyethyl methacrylate.

Inventors: MCDADE, CHRISTINE
Applicants: ROHM AND HAAS COMPANY
Application year: 1990
Main classification: C07C69
IPC codes: B01J27, C07B61, C07C69, C07C67