Container for photographic film cartridge

Abstract: Container bodies for a photographic film cartridge which has solved white powder generation problem by devising the Rockwell hardness, a blend of lubricants, a blend of polypropylene resins or a combination of a particular resin composition and groove formation. While, moistureproofness can be improved by thickening the gate mark portion.

Description: BACKGROUND OF THE INVENTION Field of the Invention This invention relates to containers for a photographic film cartridge. Description of the Prior Art A common photographic film cartridge is shown in Figure 26. A photographic film is wound around a spool 16 made of plastic resin, and placed in the cartridge body 18. The cartridge is wellknown as JIS 135 type cartridge, and light-shielding members called teremp cloth are attached to the exit slit of the cartridge body 18 (e.g. Japanese Utility Model KOKOKU No. 41-6297). The leading end of the photographic film is called tongue 17. Various improvements have been made with respect to the exit light-shielding structure (e.g. JP-B-43-3416, Japanese Utility Model KOKOKU No. 37-32164). Improvements in the cartridge body 18 have also been made, and a cartridge body made of a plastic resin was proposed for the purpose of reducing weight (JP-A-55-21089). The photographic film cartridge is placed, for example, in a container shown in Figure 1. The container consists of a container body 1 and a cap 2 fitted thereto. The container body 1 is formed of a cylindrical shape having a bottom composed of a bottom portion 3 and a peripheral wall portion 4. An annular fitting groove 5 is formed near the upper edge on the inside of the peripheral wall portion 4, and an annular projection 6 to be fitted into the groove 5 is formed on the container cap 2. A semispherical recess 12 is formed at the bottom portion 3, and a projection of gate mark portion 9 remains therein. Some other container bodies are illustrated in Figures 4 through 8. Such a container body is produced by injection molding. That is, a melted resin is injected into a mold through the gate portion 10, and after solidified by cooling, it is taken out of the mold. In the case of container bodies for a photographic film cartridge, since a great quantity is mass-produced, a multi-cavity mold is used in a hot runner type, and the container bodies are molded in a high speed. The present inventor has investigated in order to improve containers for photographic film cartridge, and disclosed a container body made of a polypropylene resin having a propylene unit content of more than 70 wt. %, a melt index (ASTM D-1238) of 16 to 80 g/10 minutes, an yielding point of tensile stress of higher than 250 kg/cm 2 , a bending elastic modulus of higher than 10,000 kg/cm 2 and a notched Izod impact strength of higher than 2.0 kg.cm/cm containing an organic nucleating agent (US-A-4,639,386), a container body made of a particular polypropylene resin containing a fatty amide lubricant (JP-A-61-73947), a container body made of a resin composed of 60 to 99.9 wt. % of a particular polypropylene resin, 0 to 39.9 wt. % of polyethylene or ethylene copolymer resin and 0.1 to 15 wt. % of aluminum powder or aluminum paste (JP-A-61-250639), and a container body made of a resin containing a propylene-ethylene random copolymer composed of 95 to 99 wt. % of propylene unit and 1.5 to 4 wt. % of ethylene unit having a melt index (MI) of 10 to 70 g/10 minutes and a molecular weight distribution of 2.5 to 5.5 and containing an organic nucleating agent (Japanese Patent Application No. 63-158985). In the case of the above conventional container for a photographic film cartridge, white powder occasionally adhered to the leading end of the photographic film, the teremp cloth attached to the exit slit of the cartridge or the like during the physical distribution. The white powder gave unnecessary uncertainty to users and sometimes affected adversely photographic properties of the film. The conventional container body for a photographic film cartridge has a sufficient impact strength, and however, deformation of the opening, buckling and the like are liable to occur. When additives were increased in order to solve these problems, the additives bled to increase white powder generation. In the case of container bodies made of homopolypropylene resin, since the rigidity is made great, deformation of the opening, buckling and the like can be prevented. However, the impact strength is weak, and cracking is liable to occur by dropping. Another problem of the convenional container body was in the occurrence of bottom sink mark and buckling at the time of taking the container bodies out of their molds. The inventor found that the bottom sink mark and buckling occurred caused by the formation of vacuum state due to the smooth inner surface of the peripheral wall portion. Thereupon, the inventor devised a container body for a photographic film cartridge wherein at least more than one third from the bottom of the inner surface is made a rough face having at least 7 µm in depth (JP-A-63-193142). The roughed container body can be taken out of the core of the mold without the occurrence of bottom sink mark and buckling. Incidentally, since a great deal of containers for a photographic film cartridge are produced, to decrease the resin quantity is very important. Another problem is in that, when container bodies for a photographic film cartridge are molded by injection molding using a polyolefin resin having a MI of 10 to 60 g/10 minutes, particularly a propylene-α-olefin copolymer containing more than 0.5 wt. % of α-olefin at a high speed molding of less than 12 seconds/cycle using a multicavity mold of more than 16 cavities in a hot runner type, the gate mark portion 9 is occasionally scraped at the taking out of the mold caused by cooling unbalance. As a result, pinhole or thinned portion is produced to generate a problem in moistureproofness, and visual inspection is necessary. SUMMARY OF THE INVENTION An object of the invention is to provide a container for a photographic film cartridge wherein the generation of white powder is sharply reduced. The present inventor investigated the cause of white powder generation, and found that it is caused by scratching the additives bled out of the inner surface of the container body by the leading end of the photographic film. That is, container bodies for a photographic film cartridge are formed of polypropylene resin added with various additives, such as a lubricant for improving antiblocking ability and putting the photographic film cartridge in and out, an organic nucleating agent for improving rigidity and various other additives for improving various properties. The additives such as the lubricant gradually bled out and were crystallized on the inner surface of the container body. During the physical distribution, the photographic film cartridge placed therein rotated or shook, and the leading end of the photographic film scratched the adhered additives to generate white powder. Besides, in the case of the container bodies made of a propylene-α-olefin copolymer resin of which the content of α-olefin such as ethylene is much, the resin itself was scratched to generate white powder. As mentioned above, the present inventor has first found that the white powder generation was caused by the bleeding of the additives. Thereupon, the inventor further investigated particularly about the bleeding quantity of the additives out of various resins different in melt index, bending elastic modulus or the like. As a result, he found that the Rockwell hardness of the resin gives the greatest effect upon the bleeding out of the additives, and the white powder generation could be sharply reduced by rendering the Rockwell hardness more than a prescribed value. Thus, the present invention provides a container body for a photographic film cartridge comprising a resin composition and having a peripheral wall portion and a bottom portion, the bottom portion having a Rockwell hardness of more than 55 R, and containing 0.01 to 1 Wt.% of an antioxidant. The inventor also investigated about additives capable of reducing the bleeding quantity, and found that, when a definite amount of fatty amide lubricant is combined with a definite amount of surfactant lubricant, the bleeding quantity could sharply reduced with securing the effect of lubricant. Thus, the present ivention also procides a container body for a photographic film cartridge composed of propylene-ethylene copolymer resin containing at least 0.005 to 0.3 wt. % of a fatty amide lubricant and 0.005 to 0.6 wt. % of a surfactant lubricant and the sum of said both lubricants being 0.01 to 0.9 wt. %. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a longitudinally sectional view of a container for a photographic film cartridge to which the present invention is applicable. Figure 2 is a graph indicating the relation between the Rockwell hardness at the bottom portion and the adhered amount of white powder to the tongue portion of a photographic film. Figure 3 is an enlarged partially sectional view indicating the fitting portion of the container body shown in Figure 1. Figures 4 to 8 indicate some other containers for a photographic film cartridge to which the present invention is applicable. Figures 4 and 5 are sectional views of different containers in the state that the cap is detached. Figures 6 to 8 are perspective views of further different container bodies. Figure 26 is a perspective view of a photographic film cartridge. DETAILED DESCRIPTION OF THE INVENTION A container body for a photographic film cartridge comprises a resin composition and has a peripheral wall portion and a bottom portion, the bottom portion having a Rockwell hardness of more than 55 R, and containing 0.01 to 1 wt.% of an antioxidant. Since the peripheral wall portion is a curved surface, the Rockwell hardness of the peripheral wall portion cannot be measured. However, the peripheral wall portion is supposed to have the same Rockwell hardness as the bottom portion. When the Rockwell hardness at the bottom portion is less than 55 R, the white powder generation increases in quantity. The Rockwell hardness at the bottom portion can be made more than 55 R by using a resin composition having a Rockwell hardness (ASTM D-785, R scale, the value measuring a sheet 3.2 mm in thickness) of more than 80 R, preferably more than 85 R, and molding at a molding resin temperature of more than 180°C, preferably more than 210°C. However, any other method capable of making the Rockwell hardness at the bottom portion more than 55 R may be employed. The resin usable for forming the container body for a photographic film cartridge includes various thermoplastic resins, such as homopolypropylene resin, propylene-α-olefin random copolymer resin, propylene-α-olefin block copolymer resin, high density polyethylene resin, high impact polystyrene resin containing synthetic rubber and blend resins of the above resin and various polyolefin resins, such as ethylene-copolymer resin and/or various fillers. A particularly preferred resin is propylene-ethylene random copolymer resin having an ethylene content of 0.5 to 6 wt. %, in view of a suitable rigidity, an excellent transparency and a great impact strength. The resin forming the container body preferably has a melt index (MI, ASTM D-1238) of 10 to 60 g/10 minutes, a bending elastic modulus (ASTM D-790) of more than 9,000 kg/cm 2 and a notched Izod impact strength at 23°C (ASTM D-256) of more than 2.0 kg·cm/cm. When the MI is less than 10 g/10 minutes, molding troubles such as short shot occur. While, when the MI is beyond 60 g/10 minutes, various troubles occur such as deformation of the opening part, decrease of fitting strength, occurrence of cap detachment, deformation during stocking many pieces in a hopper, decrease of moistureproofness, decrease of impact strength, occurrence of burrs, and generation of white powder and scratches by scraping the resin forming the peripheral wall portion of the container body with the leading end of the photographic film due to the decrease of surface strength. When the bending elastic modulus in less than 9,000 kg/cm 2 , deformation of the opening part and buckling are liable to occur, and therefore, the molding cycle must be elongated. When the notched Izod impact strengh at 23°C is less than 2.0 kg cm/cm, cracking occurs by dropping or the impact in processing and packaging processes and physical distribution. To incorporate more than 0.001 wt. % of a lubricant into the resin forming the container body is preferred in view of improving moldability and the ability to put a photographic film cartridge in and out. When the content of lubricant is less than 0.001 wt. %, buckling occurs during molding and molding cycle is elongated. Moreover, blocking occurs among the container bodies in processing and packaging processes, resulting in conveying troubles. Static mark trouble and abrasion also occur. Actually, the generation of white powder sharply decreases, even when no lubricant was added. However, molding troubles such as buckling and deformation of the opening part increased about ten times compared with the cases of blending a lubricant in Example I and II. Examples of commercial lubricants suitable for the invention include: Oleic amide lubricants; "ARMOSLIP-CP" (Lion Akzo Co., Ltd.), "NEWTRON" and "NEWTRON E-18" (Nippon Fine Chemical Co., Ltd.), "AMIDE-O" (Nitto Kagaku K.K.), "DIAMID O-200" and "DIAMID G-200" (Nippon Kasei Chemical Co., Ltd.), "ALFLOW E-10" (Nippon Oil and Fats Co., Ltd.), etc. Erucic amide lubricants; "ALFLOW P-10" (Nippon Oil and Fats Co., Ltd.), etc. Stearic amide lubricants; "ALFLOW S-10" (Nippon Oil and Fats Co., Ltd.), "NEWTRON 2" (Nippon Fine Chemical Co., Ltd.), "DIAMID 200" (Nippon Kasei Chemical Co., Ltd.), etc. Bis fatty amide lubricants; "BISAMIDE" (Nitto Kagaku K.K.), "DIAMID-200 BIS" (Nippon Kasei Chemical Co., Ltd.), "ARMOWAX-EBS" (Lion Akzo Co., Ltd.), etc. Silicone lubricants; dimethylpolysiloxanes, modified thereof, etc. (Sinetsu Chemical Co., Ltd., Toray Silicone Co., Ltd.), etc. Alkylamine lubricants; "ELECTROSTRIPPER TS-2" and "ELECTROSTRIPER TS-3" (Kao Corp.), etc. Hydrocarbon lubricants; liquid paraffin, natural paraffin, microwax, synthetic paraffin, polyethylene wax, polypropylene wax, chlorinated hydrocarbon, fluorocarbon, etc. Fatty acid lubricants; higher fatty acids preferably more than C 12 , hydroxy fatty acids, etc. Ester lubricants; fatty acid lower alcohol esters, fatty acid polyol esters, fatty acid polyglycol esters, fatty acid fatty alcohol esters, etc. Alcohol lubricants; polyols, polyglycols, polyglycerols, etc. Metallic soap; metal salts such as Li, Mg, Ca, Sr, Ba, Zn, Cd, Al, Sn, Pb salts of higher fatty acids such as lauric acid, stearic acid, ricinoleic acid naphthenic acid, oleic acid, etc. To incorporate more than 0.01 wt. % of an organic nucleating agent is preferred in view of improving transparency, the shortening of molding cycle, the prevention of stringiness and resin remaining at gate troubles, the prevention of abrasion and rigidity. When the content of organic nucleating agent is less than 0.01 wt. %, the blending effect is little. Preferable organic nucleating agents are dibenzylidenesorbitol compounds, and include di-(p-methylbenzylidene)sorbitol, di-(2,4-dimethylbenzylidene)sorbitol, di-(2,4-diethylbenzylidene)sorbitol, di-(1,3,5-trimethylbenzylidene)sorbitol, di(pentamethylbenzylidene)sorbitol, 1,3,2,4-di(methylbenzylidene)sorbitol, 1,3-p-ethylbenzylidene-2,4-p-methylbenzylidenesorbitol, 1,3-p-methylbenzylidene-2,4-pethylbenzylidenesorbitol, 1,3-p-methylbenzylidene-2,4-p-chlorobenzylidenesorbitol, 1,3-p-chlorobenzylidene-2,4-p-methylbenzylidenesorbitol, 1,3-p-methylbenzylidene-2,4-p-isopropylbenzylidenesorbitol, 1,3-p-isopropylbenzylidene-2,4-p-methylbenzylidenesorbitol, 1,3-p-ethylbenzylidene-2,4-p-isopropylbenzylidenesorbitol, 1,3-p-chlorobenzylidene-2,4-p-isopropylbenzylidenesorbitol, 1,3,2,4-di(ethylbenzylidene)sorbitol, 1,3,2,4-di(propylbenzylidene)sorbitol, 1,3,2,4-di(methoxybenzylidene)sorbitol, 1,3,2,4-di(ethyoxybenzylidene)sorbitol, 1,3,2,4-di-(p-methylbenzylidene)sorbitol, 1,3,2,4-di-(p-chlorobenzylidene)sorbitol, 1,3,2,4-di-(p-methoxybenzylidene)sorbitol and 1,3,2,4-di(alkylbenzylidene)sorbitol. Two or more of the dibenzylidenesorbitol compounds may be combined. Moreover, the dibenzylidenesorbitol compound may be combined with other organic or inorganic nucleating agents. To incorporate more than 0.01 wt. % but within the range not generating photographic troubles such as fogging or the deviation in photosensitivity of an antioxidant is preferred in view of preventing resin yellowing. When the content of antioxidant is less than 0.01 wt. %, the blending effect is little. Suitable antioxidants are described below. Phenol Antioxidants: 6-t-butyl-3-methylphenol derivatives, 2,6-di-t-butyl-p-cresol, 2,2'-methylenebis-(4-ethyl-6-t-butylphenol), 4,4'-butylidenebis(6-t-butyl-m-cresol), 4,4'-thiobis(6-t-butyl-m-cresol), 4,4-dihydroxydiphenylcyclohexane, alkyl group-induced bisphenol, styrene group-induced phenol, 2,6-di-t-butyl-4-methylphenol, n-octadecyl-3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate, 2,2'-methylenebis(4-methyl-6-t-butylphenol), 4,4'-thiobis(3-methyl-6-t-butylphenol, 4,4'-butylidenebis(3-methyl-6-t-butylphenol), stearyl-β-(3,5-di-4-butyl-4-hydroxyphenyl)propionate, 1,1,3-tris(2-methyl-4-hydroxy-5-t-butylphenyl)butane, 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene, )benzene, tetrakis [methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl) propionate] methane, etc. Ketone-Amine Condensate Antioxidants: 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline, polymers of 2,2,4-trimethyl-1,2-dihydroquinoline, trimethyldihydroquinoline derivatives, etc. Arylamine Antioxidants: Phenyl-α-naphthylamine, N-phenyl-β-naphthylamine, N-phenyl-N'-isopropyl-p-phenylenediamine, N,N'-diphenyl-p-phenylenediamine, N,N'-di-p-naphthyl-p-phenylenediamine, N-(3'-hydroxybutylidene)-1-naphtylamine, etc. Imidazole Antioxidants: 2-mercaptobenzoimidazole, zinc salt of 2-mercaptobenzoimidazole, 2-mercaptomethylbenzoimidazole, etc. Phosphite Antioxidants: Alkyl-induced arylphosphite, diphenylisodecylphosphite, sodium phosphite salt of tris(nonylphenyl)phosphite, trinonylphenylphosphite, triphenylphosphite, etc. Thiourea Antioxidants: Thiourea derivatives, 1,3-bis(dimethylaminopropyl)-2-thiourea, etc. Other Antioxidants: Those useful for air oxidation, such as dilauryl thiodipropionate, etc. Various additives may be added to the resin composition composing the container body of the invention. Examples of the additives are described below. (1) Plasticizer; phthalic acid esters, glycol esters, fatty acid esters, phosphoric acid esters, etc. (2) Stabilizer; lead compounds, cadmium compounds, zinc compounds, alkaline earth metal compounds, organic tin compounds, etc. (3) Antistatic agent; cationic surfactants, anionic surfactants, nonionic surfactants, ampholytic surfactants, etc. (4) Flame retardant; phosphoric acid esters, phosphoric acid ester halides, halides, inorganic materials, polyols containing phosphor, etc. (5) Filler; alumina, kaolin, clay, calcium carbonate, mica, talc, titanium dioxide, silica, etc. (6) Reinforcing agent; glass lobing, metallic fiber, glass fiber, glass milled fiber, carbon fiber, etc. (7) Vulcanizing agent; vulcanization accelerator, acceleration assistant, etc. (8) Deterioration preventing agent; ultraviolet absorber, metal deactivator, peroxide decomposing agent, etc. (9) Coupling agent; silane compounds, titanium compounds, chromium compounds, aluminum compounds, etc. (10) Various thermoplastic resins, elastomers, rubbers, etc. In the above container body of the invention, bleeding of various additives is prevented by rendering the Rockwell hardness at the bottom portion more than 55 R, and thereby, the generation of white powder is decreased. A container body for a photographic film cartridge is composed of propylene-ethylene copolymer resin containing at least 0.005 to 0.3 wt. % of a fatty amide lubricant and 0.005 to 0.6 wt. % of a surfactant lubricant and the sum of said both lubricants being 0.01 to 0.9 wt. %. The resin composition forming the above container body preferably contains more than 70 wt. % of propylene-ethylene random copolymer resin having an ethylene content of 1 to 5 wt. %, a melt index (MI, ASTM D-1238) of 10 to 60 g/10 minutes and a bending elastic modulus (ASTM D-790) of more than 9,000 kg/cm 2 . When the content of the above propylene ethylene random copolymer is less than 70 wt. %, various disadvantages appear such as reduction of transparency, degradation of the balance among various physical strengthes and degradation of injection moldability. When the ethylene content is less than 1 wt. %, impact strength is small, and blending effect of lubricant and surfactant is little. While, when the ethylene content is beyond 5 wt. %, deformation and molding troubles such as buckling, stringiness and drooling frequently occur. When MI is less than 10 g/10 minutes, mo-lding troubles such as short shot frequently occur. While, when the MI is beyond 60 g/10 minutes, burrs occur and impact strength and surface strength are low. When the bending elastic modulus is less than 9,000 kg/cm 2 , bleeding out amount of additives is in quantity. Deformation and buckling are liable to occur. There are block-type propylene-ethylene copolymer resin as well as the above random-type. The block-type resin is excellent in impact strength. However, it is inferior in whitening by impact and transparency, and therefore, it is not desirable as the principal resin for the container body of the invention. Homopolypropylene resin is insufficient in impact strength and inferior in transparency, and therefore, it is also not suitable as the principal resin for the container body of the invention. The fatty amide lubricant is incorporated in order to shorten molding cycle, to prevent static marks, to prevent blocking and the like. Suitable fatty amide lubricants are saturated fatty amide lubricants such as behenic amide lubricant, stearic amide lubricant, palmitic amide lubricant and lauric amide lubricant, unsaturated fatty amide lubricants such as erucic amide lubricant and oleic amide lubricant, bis fatty amide lubricants such as methylenebisbehenic amide lubricant, methylenebisstearic amide lubricant, methylenebisoleic amide lubricant, ethylenebisstearic amide lubricant, hexamethylenebisstearic amide lubricant and hexamethylenebisoleic amide lubricant, monoalkylolamide lubricants such as N-(2-hydroxyethyl)lauric amide lubricant, N-(2-hydroxyethyl)stearic amide lubricant and N-(2-hydroxymethyl)stearic amide lubricant. They are commerically available from Nippon Kasei Chemical Co., Ltd., Lion Akzo Co., Ltd., Nippon Oil and Fats Co., Ltd., Kao Corp., Nitto Kagaku K.K., Nippon Fine Chemical Co., Ltd., I.C.I., Kawaken Fine Chemicals Co., Ltd., Toho Chemical Ind. Co., Ltd., and the like. The content of the fatty amide lubricant is 0.005 to 0.3 wt. %, preferably 0.02 to 0.2 wt. %. When the content is less than 0.005 wt. %, the blending effects, such as the improvement in slipping character, antiblocking ability and, antistatic ability and shortening of molding cycle, are insufficient. While, when the content is beyond 0.3 wt. %, additives bled out gradually increase resulting to increase white powder generation and to decrease transparency. The surfactant lubricant prevents white powder generation together with the fatty amide lubricant, and improves the dispersibility and solubility of additives. It imparts conductivity to improve antistatic ability, and decreases unfavorable odor of benzylidenesorbitol compound used as an nucleating agent. Suitable surfactant lubricants are nonionic surfactants such as partial fatty acid esters of polyols, ethylene oxide adducts of fatty alcohols, ethylene oxide adducts of fatty acids, ethylene oxide adducts of fatty amino compounds or fatty amides, ethylene oxide adducts of alkylphenols, ethylene oxide adducts of alkylnaphthols, ethylene oxide adducts of partial fatty acid esters of polyols and polyethylene glycols, cationic surfactants such as primary amine salts, tertiary amine salts, quaternary ammonium salts, pyridine derivatives and urea derivatives, anionic surfactants such as sulfated oils, soaps, sulfated ester oils, sulfated amide oils, sulfate ester salts of olefins, sulfate ester salts of fatty alcohols, alkyl sulfate ester salts, fatty acid ethyl sulfonate salts, alkyl sulfonates, alkyl benzene sulfonates, mixtures of naphthalene sulfonates and formalin, succinate ester sulfonate salts and phosphate ester salts, and ampholytic surfactants such as carboxylic acid derivatives and imidazoline derivatives. They are commercially available from Marubishi Oil Chemical Co., Ltd., Matsumoto Yushi Seiyaku Co., Ltd., Kao Corp., Dai-ichi Kogyo Seiyaku Co., Ltd., Nippon Oil and Fats Co., ltd., Sanyo Chemical Ind. Ltd., Yoshimura Oil Chemical Co., Ltd., American Cyanamide Co., Fine Org. Chem., General Aniline Film, and the like. The content of the surfactant lubricant is 0.005 to 0.6 wt. %, preferably 0.05 to 0.5 wt. %. When the content is less than 0.005 wt. %, the blending effects, such as the improvement in slipping character and antistatic ability with suppressing the increase of white powder generation, are insufficient. While, when the content is beyond 0.6 wt. %, additives bled out are in quantity to induce development troubles of the photographic film placed therein. The sum of the fatty amide lubricant and the surfactant lubricant is 0.01 to 0.9 wt. %, preferably 0.07 to 0.7 wt. %. When the content is less than 0.01 wt. %, the blending effects, such as the improvement in slipping character, moldability and antistatic ability, are insufficient. While, when the content is beyond 0.9 wt. %, bled out amount of additives is in quantity. Screw slip occurs, and white powder generation increases. Transparency gradually decreases, and development trouble occurs in the photographic film placed therein by the adhesion of the lubricants or the like. Other lubricants may be added in order to improve extruding ability, injection moldability or antistatic ability. Suitable lubricants are silicone lubricants, alkylamine lubricants, hydrocarbon lubricants, fatty acid lubricants, ester lubricants, alcohol lubricants and metallic soaps, mentioned previously. To incorporate 0.01 to 1 wt. % of an organic nucleating agent is preferred in view of improving transparency, physical strength, rigidity and the like. Preferable organic nucleating agents are dibenzylidenesorbitol compounds including those mentioned previously. Two or more of the dibenzylidenesorbitol compounds may be combined, and while, the dibenzylidenesorbitol compound may be combined with other organic or inorganic nucleating agents. Transparency is improved by adding the dibenzylidenesorbitol compound. To incorporate 0.01 to 1 wt. % of an antioxidant is preferred in view of efficient continuous molding. Suitable antioxidants are phenol antioxidants, ketone-amine condensate antioxidants, arylamine antioxidants, imidazole antioxidants, phosphite antioxidants, thiourea antioxidants and other antioxidants, mentioned previously. Various additives may be added to the resin composition composing the container body of the invention. Examples of the additives are aforementioned plasticizers, stabilizers, flame retardants, fillers, reinforcing agents, vulcanizing agents, deterioration preventing agents, coupling agents, various thermoplastic resins, elestomers and rubbers, and coloring agents such as inorganic pigments, e.g. carbon black, Al, Fe 2 O 3 , TiO 2 , ZrO and CdS, organic pigments and dyes. In the above container body of the invention, bleeding of various additives is prevented by a particular combination of two kinds of lubricants and a particular resin, and thereby, the generation of white powder is decreased. A container body for a photographic film cartridge according to claim 1 preferably comprises a blend of homopolypropylene resin and propylene-ethylene copolymer resin at a ratio by weight of 5 : 95 to 95 : 5 and more than 0.005 wt. % of a lubricant, and has a melt index of 10 to 60 g/10 minutes, a bending elastic modulus of more than 9000 kg/cm 2 , a notched Izod impact strength at 23°C of more than 2.5 kg.cm/cm and a Rockwell hardness of more than 85 R. When the ratio of homopolypropylene resin is less than 5, i.e. propylene-ethylene copolymer resin is beyond 95, it is difficult to provide a container body having a great rigidity, a great impact strength, a high crystallinity, rare occurrence of opening part deformation and buckling, and little increase of the amount of additives bled out with time. While, when the ratio of homopolypropylene resin is beyond 95, i.e. propylene-ethylene copolymer resin is less than 5, impact strength is small, and cracks occurs by dropping. Particularly, the container body easily cracks lower than the freezing point. Haze is also great. Besides, when the propylene-ethylene copolymer resin used is propylene-ethylene block copolymer resin which is readily whitened by pressure or impact, which has a small surface strength and on which abrasion and white powder are readily generated, the content of the block copolymer resin is preferably 5 to 70 wt. %, more preferably 10 to 50 wt. % furthermore preferably 15 to 40 wt. %. By employing the above content, the disadvantages are solved, and a container body having a sufficient impact strength can be obtained. Homopolypropylene resin is easy in the polymerization process and inexpensive. Moreover, it is excellent in rigidity, surface strength and injection moldability. While, it is inferior in impact strength and transparency, and therefore, it is unsuitable as the single resin for the container body of the invention requiring moistureproofness and gas barrier. Propylene-ethylene copolymer resin is produced by the polymerization in a saturated hydrocarbon solvent using a composite catalyst of titanium tetrachloride and triethyl aluminum called Ziegler catalyst, the polymerization using a composite catalyst of titanium trichloride and triethyl aluminum called Natta catalyst, Standard Oil process, Phillips process, Sun Oil process or the like, and the copolymer resin can be used for the container body of the invention irrespective of the polymerization process. Preferable propylene-ethylene copolymer resins have an ethylene content of 1 to 30 wt. %, preferably 2 to 15 wt. %, and propylene-ethylene random copolymer resins having a propylene content of 70 to 99 wt. %, preferably 85 to 98 wt. % and an ethylene content of 1 to 30 wt. %, preferably 2 to 15 wt. % are particularly preferred. By blending propylene-ethylene copolymer resin having an ethylene content of 1 to 30 wt. % with homopolypropylene resin having a great bending elastic modulus, a great Rockwell hardness and a small Izod impact strength, all properties necessary for container bodies for a photographic film cartridge can be made within a practical limit in any place of the world. Moreover, molding troubles and white powder generation are rare, and molding cycle can be shortened. It is preferable that more than 80 wt. % of the blend is the homopolypropylene and the propylene-ethylene copolymer. The lubricant facilitates the putting a photographic film cartridge in and out, decreases static electrification, prevents blocking and improves moldability. The content of the lubricant is more than 0.005 wt. %, preferably more than 0.02 wt. %. When the content is less than 0.005 wt. %, the blending effects are insufficient. While, the content of the lubricant is preferably less than 5 wt. %, more preferably less than 1 wt. %. When the content is beyond 5 wt. %, screw slip occurs between the screw of extruder and the resin, and the blendability is degraded, even in the case of fatty acid lubricant or fatty acid metal salt lubricant having a small effect on the improvement of slipping character. In the case of fatty amide lubricant having a great ability of improving slipping character and being liable to induce bleeding out, a suitable content is 0.005 to 1 wt. % in order to avoid screw slip, adhesion of dust by the bleeding out and white powder generation, and 0.05 to 0.5 wt. % is particularly preferred. Suitable lubricants are silicone lubricants, oleic amide lubricants, erucic amide lubricants, stearic amide lubricants, bis fatty amide lubricants, alkylamine lubricants, hydrocarbon lubricants, fatty acid lubricants, ester lubricants, alcohol lubricants and metallic soaps, mentioned previously. The blend forming a container body of the invention has a melt index (ASTM D-1238) of 10 to 60 g/10 minutes. When the MI is less than 10 g/10 minutes, the resin fluidity is inferior. As a reuslt, injection pressure is raised, and short shot occurs. While, the MI is beyond 60 g/10 minutes, the rigidity is small. As a result, fitting strength decreases to degrade moistureproofness and to induce cap detachment problem. Moreover, opening part deformation, buckling and molding troubles such as burrs are liable to occur. The bending elastic modulus (ASTM D-790) is more than 9,000 kg/cm 2 . When the bending elastic modulus is less than 9,000 kg/cm 2 , fitting strength decreases to degrade moistureproofness and to induce cap detachment. Moreover, opening part deformation and buckling are liable to occur, and molding cycle is elongated. The notched Izod impact strength (ASTM D-256) at 23°C is more than 2.5 kg.cm/cm. When the notched Izod impact strength is less than 2.5 kg· cm/cm, cracking occurs at the dropping lower than the freezing point or impact during physical distribution. The Rockwell hardness (ASTM D-785) is more than 85 R. When the Rockwell hardness is less than 85 R, white powder generates by the gradual bleeding out of additives, and abrasion is liable to occur. The container body of the invention contains an antioxidant and may contain various additives, such as nucleating agent, surfactant, coloring agent, coupling agent and the like. The nucleating agent is added for the aim of improving crystallization rate, shortening molding cycle, preventing deformation of the container body and white powder generation, improving physical properties and the like. That is, by increasing rigidity and elevating crystallization temperature, cooling time can be shortened without forming bottom sink mark and buckling, and a great quantity of molded container bodies can be put into a hopper or a container box without deformation immediately after molding. Moreover, Rockwell hardness and wear resistance can be sharply improved, and a great effect is exhibited on the prevention of white powder generation in a high speed processing and packaging process or air conveying process. There are organic nucleating agents and inorganic nucleating agents, and organic nucleating agents, particularly dibenzylidenesorbitol compounds described previously are preferred. Inorganic nucleating agents include alkali metal hydroxides such as lithium hydroxide, sodium hydroxide and potassium hydroxide, alkali metal oxides such as disodium oxide, alkali metal carbonates such as lithium carbonate, sodium carbonate, potassium carbonate, sodium hydrogen carbonate and potassium hydrogen carbonate, alkaline earth metal hydroxides such as calcium hydroxide, magnesium hydroxide and barium hydroxide, alkaline earth metal oxides such as calcium oxide and alkaline earth metal carbonates such as calcium carbonate. The nucleating agent may be an organic nucleating agent alone, a combination of an organic nucleating agent and an inorganic nucleating agent or a combination of two or more organic nucleating agents. It is preferable to coat the surface of organic nucelating agent with a fatty acid, a fatty acid compound, a coupling agent, a surfactant or the like. A suitable content of organic nucleating agent is 0.01 to 1 wt. %. When the content is less than 0.01 wt. %, the blending effect is insufficient. While, when the content is beyond 1 wt. %, a further effect does not appear. According to the kind of nucleating agent, the excess amount induces various disadvantages such as adverse affect upon photographic film, adhesion to mold, bleeding out and sharp decrease of dropping strength. As the method of blending organic nucleating agent, there are compound method, dry blending method, masterbatch method and the like, and the masterbatch method is preferred. Since most of organic nucelating agents are bulky and liable to be scattered. Therefore, it is preferable to blend a small amount of dispersing agent or wetting agent. Suitable dispersing agents include carboxylic anhydrides and higher fatty acids, and lubricants such as oleic amide are particularly preferred. Suitable wetting agents include plasticizers such as DOP and DHP. To blend a coupling agent is preferred in view of removing the unfavorable odor of organic nucleating agent. Suitable coupling agents include silane compound coupling agents such as vinylsilane coupling agents, acrylsilane coupling agents, epoxy silane coupling agents, aminosilane coupling agents and mercaptosilane coupling agents, titanium compound coupling agents, chromium compound coupling agents and aluminum compound coupling agents. A suitable content of the coupling agent is 0.01 to 5 wt. %. 0.01 to 1 wt. % of an antioxidant is incorporated in view of efficient continuous molding. Suitable antioxidants are phenol antioxidants, ketone-amine condensate antioxidants, arylamine antioxidants, imidazole antioxidants, phosphite antioxidants, thiourea antioxidants and other antioxidants, mentioned previously. Sulfur antioxidants are also usable, and include dilaurylthiodipropionate, dimyristylthiodipropionate, laurylstearylthiodipropionate, distearylthiodipropionate, etc. A surfactant can be incorporated in order to improve antistatic ability and the like. Suitable surfactants are: Nonionic surfactants; polyethylene glycol fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene fatty alcohol ethers, polyoxyethylene alkylphenyl ethers, polyoxyethylene glycerine fatty acid esters, polyoxyethylene fatty amines, sorbitan monofatty acid esters, fatty acid pentaerythritol, ethylene oxide adducts of fatty alcohols, ethylene oxide adducts of fatty acids, ethylene oxide adducts of amino fatty acids or fatty acid amides, ethylene oxide aducts of alkylphenols, ethylene oxide adducts of alkylnaphthols, ethylene oxide adducts of partial fatty acid esters of polyols, other nonionic surfactants disclosed on page 120 of JP-B-63-26697. Anionic surfactans; sodium salt of ricinoleic acid sulfate ester, various metal salts of fatty acids, ricinolate ester sulfate ester sodium salt, sulfated ethylamiline oleate, sulfate esters of olefins, sodium salt of oleyl alcohol sulfate ester, alkylsulfate ester salts, fatty acid ethylsulfonate salts, alkylsulfonate salts, alkyl naththalene sulfonate salts, alkylbenzene sulfonate salts, succinate ester sulfonate salts, phosphate ester salts, etc. Cationic surfactans; primary amine salts, tertiary amine salts, quaternary ammonium salts, pyridine derivatives, etc. Ampholytic surfactants; carboxylic acid derivatives, imidazoline derivatives, betaine derivatives, etc. Nonionic surfactants and cationic surfactants are preferred, because of not affecting photographic film adversely and of preventing the generation of static electricity. A suitable content of the surfactant is 0.01 to 5 wt. %. When the content is less than 0.01 wt. %, the blending effect of the surfactant is insufficient. While, when the content is beyond 5 wt. %, the increase of the blending effect is not so much by increasing the blending quantity of the surfactant. Moreover, the excess amount of the surfactant causes various troubles, such as adverse influence upon photographic film, adhesion of dust caused by bleeding out and decrease of transparency, according to the kind of the surfactant. A coloring material may be added. Examples of the coloring materials are described below. Inorganic Compounds: Oxides ... silica, diatomaceous earth, alumina, titanium oxide, iron oxide, zinc oxide, magnesium oxide, antimony oxide, barium ferrite, strontium ferrite, beryllium oxide, pumice, pumice balloon, alumina fiber, etc. Hydroxides ... aluminum hydroxides, magnesium hydroxides, basic magnesium carbonate, etc. Carbonates ... calcium carbonate, magnesium carbonate, dolomite, etc. Sulfates, sulfites ... calcium sulfate, barium sulfate, ammonium sulfate, calcium sulfite, etc. Silicates ... talc, clay, mica, asbestos, glass fiber, glass balloon, glass bead, calcium silicate, montmorillonite, bentonite, etc. Carbons ... carbon black, graphite, carbon fiber, carbon hollow bead, etc. Others ... iron powder, copper powder, lead powder, stainless steel powder, pearl pigment, aluminum powder, molybdenum sulfide, boron fiber, silicon carbide fiber, brass fiber, potassium titanate, lead titanate zirconate, zinc borate, barium metaborate, calcium borate, sodium borate, aluminum paste, etc. Organic Compounds: wood flour such as pine, oak and sawdust, husk fiber such as almond, peanut and chaff, various colored fibers such as cotton and jute, paper piece, cellophane piece, nylon fiber, polypropylene fiber, starch, aromatic polyamide fiber, etc. Among them, preferred coloring materials make opaque, and light-absorptive carbon black, titanium nitride and graphite and light-reflective aluminum powder and aluminum paste are particularly preferred because of being excellent in heat resistance and light resistance and being relatively inactive. Various additives may be added to the resin composition composing the container body of the invention. Examples of the additives are aforementioned plasticizers, stabilizers, flame retardants, fillers, reinforcing agents, vulcanizing agents, deterioration preventing agents, various thermoplastic resins, elastomers and rubbers. Polyolefin thermoplastic resins are particularly preferred. In the container bodies of the invention mentioned heretofore, the thickness of the peripheral wall portion and the bottom portion is preferably 0.5 to 1.3 mm, in view of quality, moldability and cost. The container bodies of the invention can be formed by various known molding methods, and injection molding is preferred. The injection molding method may be the most usual method of single molding or any other method such as injection blow molding, intermold vacuum injection molding, stack molding and the like. A particularly preferred process uses a closed system injection molding machine containing a hot runner type mold having a number of cavities of not less than 24. The form of the container bodies of the invention is not limited. However, preferable container bodies have a good sealability with a cap attached thereto and easy detachment of the cap and includes disclosed in JP-A-61-73947, 63-193142, 64-9445, 1-2135. Some container bodies are shown in Figure 4 to Figure 8. The container bodies of Figure 4 to Figure 6 are cylindrical, and the container body of Figure 7 is rectangular. The container body of Figure 8 is formed cylindrical on the inside portion to placed a film cartridge and rectangular on the outside portion. The material of the cap is preferably more flexible than the container body 1 in order to improve the fitting sealability to the container body and to exhibit the aforementioned functions sufficiently. Preferred materials include low density polyethylene resin, various blend resins of the above resins and other thermoplastic resins. To add 0.01 to 0.6 wt. % of fatty amide lubricant is preferred in view of improving injection moldability and antistatic property. The resin composition used for the container body of the invention is also suitable for molded articles adversely affected by the bleeding out of various additives, requiring impact strength and no deformation, such as the hinged plastic cases disclosed in Japanese Utility KOKAI Nos. 54-100617, 54-137344, 59-77144 and 62-99571, JP-A-63-223640 and EP-A-0 242 905, lid-fitting type containers disclosed in Japanese Utility Model KOKOKU No. 44-28473 and JP-B-46-7501, spools disclosed in Japanese Utility Model KOKOKU Nos. 61-3000, 61-36995 and 61-36996 and Japanese Utility Model KOKAI No. 63-73742, and cores disclosed in Japanese Utility Model KOKAI Nos. 61-86367 and 61-128256. The container bodies of the invention and the above molded articles may be imparted with light-shielding ablity by blending a light-shielding material. The form of container bodies may be changed so that two or more photographic film cartridges can be placed. The container bodies of the invention may be used as the sealing containers for medicines, small articles, foods, dolls, small samples, seeds or the like. A certain modification in shape or size if also possible. A scale indicating volume, a picture or letters can be printed. The containers can be packaged by a shrinkable film. EXAMPLES Example I The container body of Example I was formed of the resin composition of 99.4 wt. % of propylene-ethylene random copolymer resin having an ethylene content of 3 wt. %, 0.3 wt. % of oleic amide, 0.15 wt. % of calcium stearate, 0.2 wt. % of an organic nucleating agent of a dibenzylidenesorbitol compound and 0.1 wt. % of a phenolic antioxidant. The resin composition had a MI (ASTM D-1238) of 40 g/10 minutes, a bending elastic modulus (ASTM D-790) of 10,800 kg/cm 2 , a notched Izod impact strength (ASTM D-256) at 23°C of 4.5 kg·cm/cm and a Rockwell hardness (ASTM D-785) of 85 R, and the container body 1 shown in Figure 1 having a bottom thickness of 0.8 mm was molded by injection molding at a resin temperature of 220°C. The cooling water temperature was 15°C, and the cooling time was 1.5 seconds. One molding cycle time was 7.5 seconds. The type of runner was hot runner, and the molding number per once was 24. The surface temperature immediately after the molding was 30°C, and the Rockwell hardness at the bottom portion was 60 R. Example II The container body of Example II was formed of the resin composition of 99.4 wt. % of propylene-ethylene random copolymer resin having an ethylene unit content of 2.5 wt. %, 0.3 wt. % of oleic amide, 0.15 wt. % of calcium stearate, 0.2 wt. % of an organic nucleating agent of a dibenzylidenesorbitol compound and 0.1 wt. % of a phenolic antioxidant. The resin composition had a MI of 40 g/10 minutes, a bending elastic modulus of 14,000 kg/cm 2 , a notched Izod impact strength at 23°C of 3.0 kg·cm/cm and a Rockwell hardness of 95 R, and the container body having the same form and size as Example I was molded at a resin temperature of 220°C. The cooling water temperature was 15 °C, and the cooling time was 1 seconds. One molding cycle time was 7 seconds. The type of runner was hot runner, and the molding number per once was 24. The surface temperature immediately after the molding was 35°C, and the Rockwell hardness at the bottom portion was 87 R. Comparative Example I The container body of Comparative Example 1 was formed of the resin composition of 99.4 wt. % of the propylene-ethylene random copolymer resin having an ethylene unit content of 3 wt. %, 0.3 wt. of oleic amide, 0.15 wt. % of calcium stearate, 0.2 wt. % of an organic nucleating agent of aluminum p-t-butylbenzoate and 0.1 wt. % of a phenolic antioxidant. The resin composition had a MI of 25 g/10 minutes, a bending elastic modulus of 9,200 kg/cm 2 , a notched Izod impact strength at 23°C of 4.0 kg·cm/cm and a Rockwell hardness (ASTM D-785) of 80 R, and the container body having the same form and sized as Example I was molded at a resin temperature of 220°C. The cooling water temperature was 15°C, and the cooling time was 5 seconds in order to prevent buckling. One molding cycle time was 13 seconds. The type of runner was hot runner, and the molding number per once was 24. The surface temperature immediately after the molding was 23°C, and the Rockwell hardness at the bottom portion was 52 R. Comparative Example II Using the same resin composition as Comparative Example I, the container body of Comparative Example II was molded in the same manner as Comparative Example I, except that the cooling time was 6 seconds, therefore, the molding cycle was 14 seconds, and the surface temperature of the container body immediately after the molding was 20°C. The Rockwell hardness at the bottom portion was 46 R. Comparative Example III Using the same resin composition as Example I, the container body having the same form and size as Example I was molded at a resin temperature of 200°C. The cooling water temperature was 10°C, and the cooling time was 3 seconds. One molding cycle time was 10 seconds. The type of runner was hot runner, and the molding number per once was 24. The surface temperature immediately after the molding was 20°C, and the Rockwell hardness at the bottom portion was 51 R. A photographic film of 36 exposures was placed in each of the above container bodies, and the same cap as shown in Figure 1 was attached thereto. Then, each container was fixed to a shaking test machine (indicated by JIS Z-0232) with a tape, and shaken at an oscillation of 5 mm at a vibration frequency of 550 cycles/min for 60 minutes. After the shaking, the quantity of white powder adhered to the leading end of the photographic film was measured by visual inspection. The results are shown Figure 2. In the figure, the axis of ordinate indicates the adhered degree of white powder, and the meaning of each alphabet letter is as follows: A ··· very excellent, B ··· excellent, C ··· practical (within a practical limit), D ··· having a problem (improvement is necessary), E ··· impractical, F ··· impractical (extremely bad). As shown in the figure, the container bodies of Example I (EI) and Example II (EII) are enough to put them to practical use, while the container bodies of Comparative Example I (CI), Comparative Example V (CII) and Comparative Example III (CIII) cannot be put to practical use. The results indicate that, when the Rockwell hardness at the bottom portion is more than 55 R, the adhered amount of white powder is within a practical limit. Example III A container body for a photographic film cartridge shown in Figures 1 and 3 was molded. The container body has a thickness (a) of 0.8 mm, a length (b) of 51 mm, a diameter (c) of 31 mm, a diameter of the projection at the bottom (d) of 6 mm, a thickness of the opening part (e) of 1 mm, a width of the upper annular projection (f) of 1.7 mm, a width of the annular fitting groove (g) of 2 mm, a width of the lower annular projection (h) of 1 mm, the radius at the inside connecting portion between the peripheral wall portion and the bottom portion (R 1 ) of 1.5 mm, the same of the outside (R 2 ) of 1.7 mm, the radius of the recess (R 3 ) for the gate mark of 4 mm, the radius of the inside upper edge (R 4 ) of 0.5 mm, the radius of the fitting groove (R 5 ) of 1.5 mm and the radius of the undercut portion of the lower annular projection (R 6 ) of 6 mm. The container body was molded by using a closed type injection molding machine ("NETSTAL", Sumitomo Heavy Industries Ltd.) at a mold claming pressure of 150 t. The molding number per once was 24, and the type of runner was a hot runner. The container body of Example III was formed of the resin composition of 99.2 wt. % of propylene-ethylene random copolymer resin having an ethylene content of 2.5 wt. %, a MI (ASTM D-1238) of 38 g/10 minutes, a density (ASTM D-1505) of 0.90 g/cm 3 , a bending elastic modulus (ASTM D-790) of 12,800 kg/cm 2 , a notched Izod impact strength (ASTM D-256) at 23°C of 3.2 kg·cm/cm and a Rockwell hardness (ASTM D-785) of 92 R, 0.1 wt. % of oleic amide ("FATTY AMIDE O", Kao Corp.), 0.3 wt. % of a nonionic surfactant lubricant of fatty acid ester ("ELECTROSTRIPPER TS-5", Kao Corp.), 0.1 wt. % of calcium stearate, 0.1 wt. % of a phenol antioxidant (tetrakis methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl) propionate methane), and 0.2 wt. % of an organic nucleating agent (1,3,2,4-di(methylbenzylidene)sorbitol). Example IV The container body for a photographic film cartridge of Example IV has the same form and size as Example III, and molded in the same manner as Example III. This container body was formed of the resin composition of 99.2 wt. % of propylene-ethylene random copolymer resin having an ethylene content of 2.5 wt. %, a MI of 40 g/10 minutes, a density of 0.90 g/cm 3 , a bending elastic modulus of 10,500 kg/cm 2 , a notched Izod impact strength at 23°C of 4.5 kg·cm/cm and a Rockwell hardness of 85 R, 0.05 wt. % of erucic amide ("ALFLOW P-10", Nippon Oil and Fats Co., Ltd.), 0.35 wt. % of a nonionic surfactant lubricant of alkylamine ("ELECTROSTRIPPER TS-3", Kao Corp.), 0.1 wt. % of calcium stearate, 0.1 wt. % of a phenol antioxidant (the same as Example III), and 0.2 wt. % of an organic nucleating agent (the same as Example III). Comparative Example IV The container body of Comparative Example IV has the same form and size as Example III, and molded in the same manner as Example III. This container body was formed of 99.2 wt. % of the same propylene-ethylene random copolymer resin as Example IV, 0.5 wt. % of oleic amide (the same as Example III), 0.1 wt. % of a phenol antioxidant (the same as Example III) and 0.2 wt. % of an organic nucleating agent (the same as Example III). Comparative Example V The container body of Comparative Example V has the same form and size as Example III, and mold in the same manner as Example III. This container body was formed of the resin composition of 99.3 wt. % of propylene-ethylene random copolymer resin having an ethylene content of 3.5 wt. %, a MI of 25 g/10 minutes, a density of 0.90 g/cm 3 , a bending elastic modulus of 8,700 kg/cm 2 , a notched Izod impact strength at 23°C of 4.6 kg·cm/cm and a Rockwell hardness of 76 R, 0.3 wt. % of oleic amide (the same as Example III), 0.1 wt. % of calcium strearate, 0.1 wt. % of a phenol antioxidant (the same as Example III), and 0.2 wt. % of an organic nucleating agent (the same as Example III). Comparative Example VI The container body of Comparative Example VI has the same form and size as Example III, and molded in the same manner as Example III. This container body was formed of 99.7 wt. %. of the same propylene-ethylene random copolymer resin as Example IV, 0.1 wt. % of a phenol antioxidant (the same as Example III) and 0.2 wt. % of an organic nucleating agent (the same as Example III). Various properties of the container bodies of Examples III and IV and Comparative Examples IV through VI were measured, and summarized in Table 1. Unit Invention Comparative III IV IV V VI Propylene-Ethylene Copolymer Resin MI g/10 38 40 40 25 40 Density g/cm 3 0.90 0.90 0.90 0.90 0.90 Bending Elastic Modulus kg/cm 2 12800 10500 10500 8700 10500 Notched Izod Impact Strength at 23°C kg·cm/cm 3.2 4.5 4.5 4.6 4.5 Rockwell Hardness R 92 85 85 76 85 Ethylene Content wt. % 2.5 3.0 3.0 3.5 3.0 Fatty Amide Lubricant - Oleic Amide Erucic Amide Oleic Amide Oleic Amide - Content wt. % 0.1 0.05 0.5 0.3 - Surfactant Lubricant - Nonionic (Fatty Ester) Nonionic (Alkylamine) - - - Content wt. % 0.3 0.35 - - - Ca Stearate Content wt. % 0.1 0.1 - 0.1 - Phenol Antioxidant Content wt. % 0.1 0.1 0.1 0.1 0.1 Nucleating Agent Content wt. % 0.2 0.2 0.2 0.1 0.1 Putting Photographic Film in and out - A A B A E White Powder (After one day) - A A C D A (After seven days) - B-A B-A D-E E B-A Injection Moldability - A A B D E Transparency (After seven days) - A A C B A Static Electrification - A A B C E Photographic Properties - B B C B C Evaluation in Table 1 were carried out as follows: A very excellent B excellent C practical D having a problem E impractical improvement is necessary Testing methods were as follows: Putting Photographic Film In and Out: Evaluated by the difficulty when a photographic film cartridge was put in and out of each container body. White Powder (After one day): Each container body was allowed to stand in an air-conditioned room at 20°C at 65 % RH for one day after injection molding. A photographic film cartridge was placed therein, and a cap was attached. Then, each container was shaken by a vibration testing machine defined in JIS Z-0232 at a vibration amplitude of 5 mm at a frequency of 550 times/min. for 60 minutes, and the amount of white powder adhered to the leading end portion of the photographic film was evaluated by visual inspection. White Powder (After seven days): Each container body allowed to stand in an air-conditioned room at 20°C at 65 % RH for seven days was evaluated in the same manner as the case after one day. Injection Moldability: Judged by the occurrence of molding troubles such as short shot, bottom sink mark and deformation, releasability from the mold and moldig cycle, collectively. Transparency (After seven days): Each container body was allowed to stand in an air-conditioned room at 20°C at 65 % RH for seven days, and then, gradually moved far from the transparency inspection chart of a white paper on which parallel lines each 0.5 mm in thickness were drawn at an interval of 2 mm. The transparency was evaluated by the distance (cm) not seen the parallel lines. Static Electrification: The voltage of the static electrification of each container body was measured by a volt meter, when 2000 pieces of the container body were molded and placed in a polyethylene bag. Photographic Properties: A cartridge containing a photographic film ("Fuji Color HR-100") of 36 exposures was placed in each container body and a cap was attached. The container was allowed to stand in an air-conditioned room at 35°C at 85 % RH for 30 days, and then developed. The photographic properties were evaluated by the occurrence of photographic abnormalities such as fogging and deviation of photographic sensitivity. Example V The container body of Example V was shown in Figure 1 wherein the thickness (a) of the peripheral wall portion was 0.8 mm, and molded by using a closed type injection molding machine ("NETSTAL", Sumitomo Heavy Industries Ltd.) at a mold claming pressure of 150 t. The molding number per once was 24, and the type of runner was a hot runner. The container body of Example V was formed of the resin composition having a MI of 31 g/10 minutes, a density of 0.90 g/cm 3 , a bending elastic modulus of 12,000 kg/cm 2 , a notched Izod impact strength at 23°C of 3.8 kg·cm/cm and a Rockwell hardness of 92 R composed of 35 wt. % of homopolypropylene resin having a MI (ASTM D-1238) of 40 g/10 minutes, a density (ASTM D-1505) of 0.91 g/cm 3 , a bending elastic modulus (ASTM D-790) of 21,000 kg/cm 2 , a notched Izod impact strength (ASTM D-256) at 23°C of 2.5 kg·cm/cm and a Rockwell hardness (ASTM D-785, measured in a thickness of 3.2 mm) of 110 R, 64.35 wt. % of propylene-ethylene random copolymer resin haing an ethylene content of 3.3 wt. %, a MI of 25 g/10 minutes, a density of 0.90 g/cm 3 , a bending elastic modulus of 9,200 kg/cm 2 , a notched Izod impact strength at 23°C of 5.0 kg·cm/cm and a Rockwell hardness (ASTM D-785, measured in a thickness of 3.2 mm) of 80 R, 0.3 wt. % of oleic amide, 0.2 wt. % of a phenol antioxidant (the same as Example III), and 0.15 wt. % of an organic nucleating agent (the same as Example III). Example VI The container body of Example VI was the same as Example V, except that the content of the same homopolypropylene resin as Example V was changed to 64.35 wt. %, and the propylene-ethylene random copolymer resin was changed to 35 wt. % of propylene-ethylene block copolymer resin having an ethylene content of 6 wt. %, a MI of 25 g/10 minutes, a density of 0.91 g/cm 3 , a bending elastic modulus of 12,500 kg/cm 2 , a notched Izod impact strength at 23°C of 13 kg·cm/cm and a Rockwell hardness (measured in a thickness of 3.2 mm) of 80 R. The resin composition had a MI of 30 g/10 minutes, a density of 0.90 g/cm 3 , a bending elastic modulus of 13,300 kg/cm 2 , a notched Izod impact strength at 23°C of 8.2 kg·cm/cm and a Rockwell hardness of 89 R. Comparative Example VII The container body of Comparative Example VII was the same as Example V, except that the propylene-ethylene random copolymer resin was not blended and the content of the homopolypropylene resin was changed to 99.35 wt. %. The resin composition had a MI of 42 g/10 minutes, a density of 0.90 g/cm 3 , a bending elastic modulus of 21,600 kg/cm 2 , a notched Izod impact strength at 23°C of 2.6 kg·cm/cm and a Rockwell hardness of 112 R. Comparative Example VIII The container body of Comparative Example VIII was the same as Example V, except that the homopolypropylene resin was not blended and the content of the propylene-ethylene random copolymer resin was changed to 99.35 wt. %. The resin composition had a MI of 28 g/10 minutes, a density of 0.90 g/cm 3 , a bending elastic modulus of 9,800 kg/cm 2 , a notched Izod impact strength at 23°C of 5.5 kg·cm/cm and a Rockwell hardness of 83 R. Comparative Example IX The container body of Comparative Example IX was the same as Example VI, except that the homopolypropylene resin was not blended and the content of the propylene-ethylene block copolymer resin was changed to 99.35 wt. %. The resin composition had a MI of 26 g/10 minutes, a density of 0.90 g/cm 3 , a bending elastic modulus of 12,900 kg/cm 2 , a notched Izod impact strength at 23°C of 13.5 kg·cm/cm and a Rockwell hardness of 82 R. Various properties of the container bodies of Examples V and VI and Comparative Examples VII through IX were measured, and summarized in Table 2. Unit Invention Comparative V VI VII VIII IX Homopolypropylene Resin MI g/10 min. 40 40 40 - - Density g/cm 3 0.91 0.91 0.91 - - Bending Elastic Modulus kg/cm 3 21000 21000 21000 - - Notched Izod Impact kg·cm/cm 2.2 2.2 2.2 - - Strength at 23°C Rockwell Hardness R 110 110 110 - - Content wt. % 35 64.35 99.35 - - Propylene-Ethylene Copolymer Resin Resin Type - random block - random block Ethylene Content wt. % 3.3 6.0 - 3.3 6.0 MI g/10 min. 25 25 - 25 25 Density g/cm 3 0.90 0.91 - 0.90 0.91 Bending Elastic Modulus kg/cm 3 9200 12500 - 9200 12500 Notched Izod Impact kg·cm/cm 5.0 13.0 - 5.0 13.0 Strength at 23°C Rockwell Hardness R 80 80 - 80 80 Content wt. % 64.35 35 - 99.35 99.35 Lubricant wt. % 0.3 0.3 0.3 0.3 0.3 Content Antioxidant wt. % 0.2 0.2 0.2 0.2 0.2 Content Nucleating Agent wt. % 0.15 0.15 0.15 0.15 0.15 Content White Powder - B B B D D Dropping Strength - B B D B A Whitening by Dropping - B C B B D Injection Moldability - B B B D C Transparency - A C C A D Evaluations are the same as Table 1. Testing methods of White Powder and Transparency are the same as Table 1. The container bodies were subjected to the evaluation of White Powder after several days from the molding. Dropping Strength: A cartridge containing 36 exposures photographic film ("Fuji Color HR-100") was placed in each container body, and a cap was attached. The container was dropped to concrete floor from 5 m height at room temperature (20°C), and dropping strength was evaluated by the ratio of the cracked container bodies. Whitening by Dropping: In the above dropping strength test, the whitened state by the dropping shock of each container body was evaluated by visual inspection. Injection Moldability: Evaluated by the generation rate of molding troubles such as deformation at the opening part, buckling and releasing trouble from the mold, when each container body was molded at the cooling time of 3 seconds and the molding cycle time of 9 seconds.

Claims: A container body for a photographic film cartridge comprising a resin composition and having a peripheral wall portion and a bottom portion, the bottom portion having a Rockwell hardness of more than 55 R, and containing 0.01 to 1 wt.% of an antioxidant. The container body of claim 1 which comprises a propylene-ethylene random copolymer resin having an ethylene content of 0.5 to 6 wt.%. The container body of claim 1 which comprises a resin having a melt index of 10 to 60g/10 minutes, a bending elastic modulus of more than 9,000 kg/cm 2 and a notched Izod impact strength at 23°C of more than 2.0 kg.cm/cm. The container body of claim 1 which contains more than 0.001wt.% of a lubricant and more than 0.01wt.% of a dibenzylidene sorbitol compound as an organic nucleating agent. The container body of claim 1, wherein the Rockwell hardness is of more than 85 R, which body comprises a blend of a homopolypropylene resin and a propylene-ethylene copolymer resin at a ratio of 5 : 95 to 95 : 5 and more than 0.005 wt.% of a lubricant, having a melt index of 10 to 60 g/10 minutes, a bending elastic modulus of more than 9000 kg/cm 2 , and a notched Izod impact strength at 23°C of more than 2.5 kg.cm/cm. The container body of claim 5 wherein the propylene-ethylene copolymer is a propylene-ethylene block copolymer, and the content is 5 to 70 wt.%. The container body of claim 5 wherein the propylene-ethylene copolymer is a propylene-ethylene random copolymer having an ethylene content of 5 to 70 wt.%. The container body of claim 5 which contains 0.01 to 1 wt.% of a dibenzylidene sorbitol compound as an organic nucleating agent. A container body for a photographic film cartridge composed of propylene-ethylene copolymer resin containing at least 0.005 to 0.3 wt.% of a fatty acid amide lubricant and 0.005 to 0.6 wt.% of a surfactant lubricant and the sum of said both lubricants being 0.01 to 0.9 wt.%. The container body of claim 9 which contains more than 70 wt.% of a propylene-ethylene random copolymer resin having an ethylene content of 1 to 5 wt.%, a melt index of 10 to 60 g/10 minutes and a bending elastic modulus of more than 9,000 kg/cm 2 . The container body of claim 9 which contains 0.01 to 1 wt.% of a dibenzylidene sorbitol compound as an organic nucleating agent and 0.01 to 1 wt.% of an antioxidant.

Inventors: AKAO MUTSUO, INOUE KOJI, AKAO, MUTSUO, INOUE, KOJI, AKAO, MUTSUO, C/O FUJI PHOTO FILM CO., LTD., INOUE, KOJI, C/O FUJI PHOTO FILM CO., LTD.
Applicants: FUJI PHOTO FILM CO LTD, FUJI PHOTO FILM CO., LTD.
Application year: 1990
Main classification: G03C3
IPC codes: C08L23, C08K5, G03C3