ABSORBENT MATERIALS AND USE THEREOF

Abstract: A method for adsorbing hydrophobic substances in liquid form, by subjecting the liquid to contact with an adsorbent material comprising fibres formed discrete lumps. By ''lumps'' of fibres are meant bodies of compacted fibre generally of a shape that is more spherical than elongate. The material can be used in any particulate form. The particulate fibrous material in knop form has its additional containment attributes gained by having a spherical fiber orientation produced in the knopping process. The knopping process parameters when varied form the fibres into knops of a wide range of densities in order to allow optimized oil adsorbency for a range of oil viscosities. The fibrous material can be modified by including the use of chemicals, such as water repellents, to modify the surface characteristics of the fibres to enhance oil pick-up or flotation. The fibrous material can be used in conjunction with a containment device made of netting or porous material shaped into an alongated system or pad to allow oil and oil water mixes to penetrate the netting.

Description: ABSORBENT MATERIALS AND USE THEREOF This invention relates to material for use in adsorbing spillages of liquid and fluid organic substances. A major pollution problem is the spillage of large amounts of oil such as when being transported in bulk on the sea or on land. The damage caused by such spillages is well documented. There have been numerous attempts at providing methods and materials to overcome this problem. Suggestions have been materials to adsorb the spilled oil, substances designed to enable the oil to mix with water and physical barriers designed to inhibit the spread of oil for example when a spillage occurs at sea. One material that is available commercially is that marketed by the 3M Company of the U.S.A. under the trade mark "PO ERSORB" or "OILSORB" . This may consist of layers of fibrous polypropylene encased in suitable netting and shaped as long elongate systems designed to float on the surface of water and act as a physical barrier to the spread of the oil as well as being designed to adsorb the oil. The adsorbency characteristic of the polypropylene has been one of the attributes to their successful use. While oil spillages are the most well recognised problem, spillages of other large quantities, of generally liquid organic materials can also be environmentally serious. SUBSTITUTESHEET - " 2 * - ' PCT/GB90/01358 Such materials include large amounts of vegetable oils, refined oils and such like. It is an object of this invention to provide a material having good adsorbency for oil and other organic materials. In accordance with this invention there is provided a method for adsorbing hydrophobic substances in liquid form, comprising subjecting the liquid to contact with an adsorbent material comprising fibres formed into discrete lumps. By "lumps" of fibres are meant bodies of compacted fibre generally of a shape that is more spherical than elongate. By knopping into lumps any fibrous material of the general type described in the applicants U.S. patent specification No. 4,761,857 it is possible to increase the versatility of application of the fibres to adsorb or adsorb organic or synthetic oils. The material can be used in any particulate form. The particulate fibrous material in knop form has its additional containment attributes gained by having a spherical fibre orientation produced in the knopping process. The fibrous material in knop form has increased buoyancy attributes in a water medium to that of unknopped fibrous material. SUBSTITUTESHEET The knopping process parameters when varied form the fibres into knops of a wide range of densities in order to allow optimised oil adsorbency for a range of oil viscosities. The fibrous material can be modified by including the use of chemicals, such as water repellents, to modify the surface characteristics of the fibres to enhance oil pick-up or flotation. The fibrous material can be used in conjunction with a containment device made of netting or porous material shaped into an elongated system or pad to allow oil and oil water mixes to penetrate the netting. The fibrous material can be used in conjunction with other knopped and unknopped fibres or buoyancy aids to increase the oil adsorbancy of flotation. The fibrous material can be used in conjunction with bacterial nutrients such as Inipol 22 to allow bacteria to break down the oil. The fibrous material can be used in as a filter, to filter oil from an oil and water mixture. The fibrous material can be used in with reused, dyed or undyed fibrous materials in knop form. SUBSTITUTESHEET The fibrous material is preferably knops of wool. Knops have a number of uses primarily as a fill such as in upholstery, pillows and other household articles but their very high adsorbency character for organic liquids particularly oil more particularly crude oil has never been suggested before. It has been known that wool has an affinity for oil, particularly so, if some of the natural wool grease remains on the fibre. After knopping this affinity increases greatly. It is thought this increase in affinity is created by the spherical shape of the fibres comprising the knop. The oil tends to break up into droplets and then migrate into the centre of each knop. It is this ability which can be exploited by using the knops as a means of adsorbing oil spills. A few simple laboratory tests revealed that untreated knops could adsorb up to thirty times their own weight of viscous oils. Laboratory tests in a water bath indicate that wool knops will adsorb oil more readily if allowed, to float, unconstrained on the surface of the oil water interface. If contained in a netting their adsorbtion rate is slower but they should maintain their original adsorbency rate provided they are not packed or loaded too tightly. SUBSTITUTE SHEET The invention envisages using other fibres of natural or synthetic polymers which can be formed into lumps of the type envisaged by the invention. The invention also envisages using mixtures of various types of synthetic or naturally occurring fibres in the form of discrete lumps. Woollen knops have demonstrated in the applicants trials to be of particular value as an adsorbent material and have the further advantage in that virtually any type and grade of wool can be used to make the knops. Thus even short staple fibres can be used together with either scoured or semi-scoured wool, crutchings and other waste remnants or other fibrous by-products. The size of the lumps is not currently envisaged as being critical. It is also envisaged that the size of the individual lumps in an adsorbent pad formed from the lumps need not be uniform and can vary considerably. Generally if knops are produced by a knop producing machine such as that described in the applicants U.S. Patent No. 4,761,857, they will tend to be of a substantially uniform size. Uniformity of size may be of value to yield a predetermined adsorbency characteristic to a particular pad consisting of a large number of knops packaged together. SUBSTITUTE SHEET The major use for an adsorbent material will be where crude oil or other oil spillages occur on water. The oil tends to float on the surface of the water and hence the adsorbent material needs to operate in this environment. The invention envisages shaping a mass of the small lumps of fibres into a form suitable to adsorb oil masses floating on the surface of water. The conglomerate of lumps can thus be shaped into any suitable elongate structure or containment device such as that described in U.K. Patent Specification No 1266366 which is of a length required to surround the oil spillage and enable the adsorbent material to contact the oil. Thus the mass or conglomerate of lumps of the fibres will be contained in a suitable porous enclosure designed to retain the lumps of material in place but permit the liquid such as the oil spillage to contact the adsorbent lumps and to be adsorbed thereby. Thus the outside material can be suitable netting fabric or other porous material. The whole elongate structure or device must float on the surface of the water. Wool as well as some synthetic polymers and natural polymers, tend to be more dense than water and hence will not inherently float. Thus the structure may incorporate flotation aids or alternatively the S UBSTITUTESHέET lumps of fibres can be treated or else be processed in such a way that they are inherently buoyant on water. Thus the invention may envisage injecting substances which are lighter than water into the lumps of fibres to a sufficient degree that the lumps are buoyant. Other methods of decreasing the wettability of the fibres have been used to increase buoyancy. By doing this the clumps of It has also been found that using the preferred materials namely knops or other lumps of wool fibre, if the wool has been semi-scoured it leaves residues of organic materials still on the fibres such as lanolin and wool grease, which provide adequate floatation characteristics to the lumps of wool fibres. The invention also envisages recovering the oil or other liquid from the adsorbent material for use as may be desired. SUBSTITUTESHEET This also enables the adsorbent material to be reused again. This reuse is also a feature of the invention. The invention also envisages providing individually shaped articles or lumps of fibre which are adsorbent for organic substances in a form enabling the shaped material to be transported to a position where it can perform its function. It is envisaged that these "sponges" could be formed of a size small enough to be manually handled e.g. for simple household functions to sizes for use for example in engineering workshops around heavy machines such as lathes where machine oil spillage is very common through larger sizes for trans-shipment on land to situations where spillages might occur of large bulk storage organic material. In laboratory trials, the following approximate adsorbencies have been found for various different types of oil and products of this invention in comparison to the commercial product "OILSORB". In order to assess the adsorbency of the wool knops for oil three quite different grade of oil were acquired. These were chosen to represent a wide range of oil viscosities and densities. Firstly crude oil, one of the major oil spill SUBSTITUTESHEET contaminants varies greatly in consistency depending on where it is source. Secondly crude from Newfoundland is waxy and almost solid whereas crude from South Africa has a similar consistency to diesel. The biggest proportion of crude is believed to be relatively viscous and resembles heavy fuel oil in viscosity and density. In commercial shipping practice larger quantities of crude oil are shipped than refined oil. The following oils were chosen for testing: Heavy Fuel Oil Density 0.9535 gm/ml Viscosity = 150 CS.T. at 50° Light Fuel Oil Density 0.9107 gm/mk Viscosity = 34 CS.T. at 50° Gas Oil Density 0.8233 gm/ml Viscosity = 3 CS.T. at 40° CS.T. = Centistokes Wei ht of Oil adsorbed in com arison SUBSTITUTESHEET Total adsorbency is one measure of the benefit of an adsorbent material. Another measure is the speed of adsorbency . Again small scale laboratory trials have indicated that knops which have not been treated for buoyancy, can be fully saturated in 2 to 3 minutes whereas the commercial product "OILSORB" takes more than 10 minutes. A number of 5 litre beakers were half filled with tap water and to each 500 mis of each of the three test oils were poured on top. To each beaker 10 gms of each of the various adsorbency materials was added. The mixture was lightly agitated with a glass stirring rod for 30 seconds. The adsorbency material was then collected and weighed. In order to assess the various degrees of adsorbency of different materials relative to each other a large water tank 1.0 m x 1.3 m was filled with tap water to a depth of 0.25 m. Samples of 3M "OILSORB" in both sheet and boom form together with wool knops loose and also in boom form were floated on the surface. To this tank 500 mis of Heavy Fuel Oil was added and dispersed evenly over the surface. The samples were left without stirring for 24 hours. To gain information on how long it takes for each adsorbency product to fully saturate approximately 30 gm SUBSTITUTE SHEET sample of knops and sorbent were floated on a Heavy Fuel Oil surface. The time taken for the oil to penetrate through the product was recorded. Small booms approximately 5 cm in diameter were made of wool knops and 3M sorbent sheeting. The booms were encased with woven polypropylene shade cloth. Each was saturated in Heavy Fuel Oil, weighed, then rung through rubber squeeze rolls and then reweighed. The rubber squeeze rolls were 49 cm long and had a pneumatic pressure of 3.8 tonnes applied to them. Table 1 shows the multiples of each products own weight that was adsorbed when immersed in various grade of oil. Table 1 Heavy Fuel Light Fuel Gas Oil Oil Oil From these results it can be seen that the Wool Knops consistently adsorbed more oil with the exception of gas oil than the 3M product . There is a trend that as the viscosity increases the wool knops are capable of adsorbing more oil. This is thought to be proportional to the densities of the two sorbent products. 3M Sorbent in sheet form SUBSTITUTE SHEET has a bulk of 12.5 cc/gm whereas the wool knops have a bulk of 30 cc/gm. The actual densities of the fibres are, wool 1.1 - 1.3 gms/ml, and polypropylene 0.9 - 0.95 gm/ml. The polypropylene is a highly fibrilated structure which gives it a greatly increased surface area. It is the surface area that normally determines the degree of adsorbency. Thus the spherical shape of the fibres in the knops and the knop itself greatly affect the mechanism by which the oil is adsorbed. The knop has a very porous structure allowing the viscous oils to easily penetrate the knop. Once the oil is within the knop structure it tends to be held in by the spherical fibre orientation. If however the oil viscosity is very low there is a tendency for it to drain out of the knop structure more easily. This does not occur with materials such as air blown polypropylene which works on the principle of having a very large surface area to adsorb the oil. Effectively the oil is spread over the polypropylene fibre surface as a thin film. To verify this, an additional trial was conducted to ascertain the oil retention capabilities of the various products. Samples were saturated in Heavy Fuel Oil and left to drain over a metal mesh. Saturation factors were recorded and again after 2 hours and 20 hours. These are shown in Table II. SUBSTITUTESHEET Table II Initial 2 Hours 20 Hours 3M Sorbent Sheet x 14.3 x 13.0 x 12.7 3M Sorbent Chopped x 21.5 x 13.1 x 11.4 Wool Knops x 35.0 x 15.9 x 11.2 Samples of 3M Sorbent and wool knops both loose and in boom form, were tested for 'adsorbency'. It was found that samples of both wool knops and the 3M products do not greatly attract oil and absorb it. At the end of the 24 hour soaking trial, only areas of each adsorbency material that were directly in contact with the oil had adsorbed and this amount was minimal. To increase the potential to adsorb oil it is necessary to have movement of either the sorbent or the oil/water mixture. Using a small wave making generator floated in the tank, it was found this helped increase the adsorbency rate but it was still not spectacular for any of the products. To get satisfactory adsorbency there needs to be mechanical agitation either by rotating the booms or allowing them to be agitated as would occur at a shoreline or with natural wave movement at sea. In cleaning out the tank between successive trails a handful of loose knops were stirred into the water in SUBSTITUTESHEET the tank and by doing this it was possible to remove all the floating oil, including the oil sheen, in 20 - 30 seconds. The times recorded to visually assess how long it took for samples of loose wool knops and sheet 3M Sorbent were recorded when the samples were floated on-a Heavy Fuel Oil surface. Knops saturated without agitation completely in 2 minutes. The 3M Sorbent sheet material was not one hundred percent saturated after 10 minutes. A drain trial was devised to determine wools (in wool knop and carded wool form) ability to retain adsorbed oil. Each adsorbent was immersed in Gas Oil, agitated gently for 45 seconds, removed and the initially saturated weight recorded. The sorbent was then allowed to drain for 1 hour with the retained oil being recorded at one minute intervals for 10 minutes then at 5 minute intervals for 50 minutes. From these results pick-up factors were calculated. SUB STITUTESHEET Drain Trails - Gas Oil Density 0.82 gms/ml Viscosity 3 CS.T. at 40°C SUBSTITUTE SHEET Further comparison trials have been conducted by S.L. Ross Environmental Research Limited of Canada and are reported in a report entitled "Selection Criteria and Laboratory Evaluation of Oilspill Sorbents" published by Environment Canada, March 1990. This report and its trial data are incorporated herein by way of reference. This data confirms the advantageous properties of the wool knops supplied to Ross Environmental Research by the applicants for testing as an oil sorbent. While this invention has been described with reference to preferred embodiments it is not to be construed as being limited thereto. Moreover where specific materials have been described, and where equivalents do exist therefore, such equivalents are incorporated herein as specifically set forth. SUBSTITUTESHEET

Claims: CLAIMS 1. A method for adsorbing hydrophobic substances in liquid for by subjecting the liquid to contact with an adsorbent material comprising fibres formed into discrete lumps. 2. A method as claimed in claim 1 wherein the discreet lumps o fibres are bodies of compacted fibre generally of a shape that i more spherical than elongate. 3. A method as claimed in claim 1 or claim 2 wherein, the knopping into lumps of any fibrous material, is generally as described in U.S. patent specification No. 4761857. 4. A method as claimed in claim 3 wherein the ability of the fibres to absorb or adsorb organic or synthetic oils is increase 5. A method as claimed in any one of the preceding claims wherein the material can be used in any particulate form. 6. A method as claimed in claim 5 wherein the particulate fibrous material in knop form has its additional containment attributes gained by having a spherical fibre orientation produc in a knopping process. 7. A method as claimed in claim 6 wherein the fibrous material in knop form has increased buoyancy attributes in a water medium to that of unknopped fibrous material. 8. A method as claimed in any one of the preceding claims wherein the knopping processes parameters are varied to form fibres into knops of a range of densities, in order to allow optimised oil adsorbency for a range of oil viscosities. 9. A method as claimed in any one of the preceding claims wherein the fibrous material can be modified by including the us SUBSTITUTE SHEET of chemicals, such as water repellents, to modify the surface characteristics of the fibres to enhance oil pick-up or flotation. 10. A method as claimed in any one of the preceding claims wherein the fibrous material can be used in conjunction with a housing, netting or porous material shaped into an elonged system or pad to allow oil and oil water mixtures to penetrate the netting allowing the knops to adsorb the oil. 11. A method as claimed in any one of the preceding claims wherein the fibrous material can be used in conjunction with other knopped and unknopped fibres or buoyancy aids to increase the oil adsorbancy or flotation. 12. A method as claimed in any one of the preceding claims wherein the fibrous material can be used in conjunction with bacterial nutrients such as Inipol 22 to allow bacteria to break down the oil. 13. A method as claimed in any one of the preceding claims wherein the fibrous material can be used as a filter, to filter oil from oil and water mixtures. 14. A method as claimed in any one of the preceding claims wherein the fibrous material can be used in conjunction with reused, dyed or undyed fibrous materials in knop form. 15. A method as claimed in any one of the preceding claims wherein the fibrous material are knops of wool. 16. A method as claimed in claim 3 wherein the versatility of the fibres increases their ability to absorb or adsorb organic or synthetic oils. SUBSTITUTE SHEET 17. A method for adsorbing hydrophobic substances in liquid fo substantially as hereinbefore described. SUBSTITUTESHEET

Inventors: CARNABY GARETH ALAN, HAMILTON MAREE ANN, MCFARLANE IAN DUNCAN, CARNABY, GARETH, ALAN, HAMILTON, MAREE, ANN, MCFARLANE, IAN, DUNCAN
Applicants: WATSON JULIAN MARK, WOOL RES ORGANISATION, WATSON, JULIAN, MARK, WOOL RESEARCH ORGANISATION OF NEW ZEALAND INC.
Application year: 1990
Main classification: C02F1
IPC codes: B01D17, B01J20, C02F1, C02F3