Lubricating oil additive and lubricating oil composition containing the same

Abstract: Borated alkyl catechols are hydrolytically stabilized by reaction with diethylamine to form a complex which when used as an additive for a lubricating oil is effective in reducing oxidation, wear and deposits in an internal combustion engine.

Description: This invention relates to lubricating oil additives which serve to reduce wear, oxidation and deposits in internal combustion engines and to the use of such additives in lubricating oil compositions. Wear and deposits limit the useful life of automobile and truck engines. Thus, there is a great need to find lubricants that reduce the oxidation, wear and deposits in the engine, thus increasing the lifetime of the engine. U.S. Patent No.2,795,548 discloses the use as additives for lubricating oil compositions for internal combustion engines of inter alia borated polyhydroxy benzenes, such as catechol and tert.-butylcatechol, for the purpose of reducing the oxidation of the oil and the resulting corrosion of the metal parts of the engine. There is a problem with the use of borated alkyl catechols in lubricating oils for internal combustion engines since they are sensitive to moisture and hydrolyze readily. The hydrolysis leads to haze and/or the formation of a precipitate which must be filtered out prior to use. In our EP-A-0206748 it is disclosed that borated alkyl catechols may be stabilized against hydrolysis by reacting them with an alkyl or alkenyl mono or bis succinimide so as to form a reaction complex which can be used as a friction reducing additive for a lubricating oil composition for use in an internal combustion engine. Preferred succinimides are stated to be those derived from polyisobutenes having a number average molecular weight of about 600 to about 1,500. Such high molecular weight succinimides effectively dilute the concentration of the desired borated alkyl catechols. In addition, using high molecular weight succinimides for hydrolytic stabilization results in higher transportation costs for the additive, and a loss of flexibility since their use is limited to formulations containing succinimides as dispersants, due to compatibility problems. US-A-2 497 521 discloses amine salts which are employed as stabilizing agents in the oil composition provided by the invention are obtained by the direct addition of an organic amine to a boro-diol complex. The latter complexes are formed by reaction between boric acid and an organic compound containing at least two hydroxyl groups. The polyhydroxy compounds which may be reacted with boric acid in such manner include both aliphatic and aromatic compounds, i. e., polyhydric alcohols such as ethylene glycol, diethylene glycol, propylene glycol, butylene glycol, trimethylene glycol, erythritol, glycerol, triethylene glycol, tetramethylene glycol, etc., and polyhydric phenols such as catechol, resorcinol, orcinol, beta - naphthohydroquinone, dihydroxytoluene, phenylcatechol, ethylcatechol, etc. We have now found that borated alkyl catechols can be stabilized against hydrolysis by complexing the borated alkyl catechol with diethylamine and that lubricating the crankcase of an internal combustion engine with a lubricating oil containing the reaction product of a borated alkyl catechol and diethylamine reduces oxidation and wear in gasoline engines and deposits in diesel engines. This finding was unexpected since it has previously been believed that low molecular weight amines would not be useful in lubricants subjected to high temperatures, e.g., >100°C because of the volatility of the amines; that is, it was believed that the amines would be lost during use and not provide ongoing stabilization against hydrolysis. However we have surprisingly found that diethylamine-borated alkyl catechol complexes are stable with respect to decomposition to starting materials under "in use" conditions. The diethylamine stabilized alkyl borated catechols of this invention passed the L-38 engine test (with a score of about 30 mg weight loss), where the presence of "free" amine such as oleyl amine under these conditions would give very high (300-600 mg) weight losses due to corrosion of the copper and lead bearings. Also, calorimetry data (DSC) shows that the diethylamine stabilized alkyl borated catechols of this invention are stable to about 177°C, which is significantly above the sump temperature of a gasoline engine. The thermal stability of catechol boron amine complexes is not predictable. For example, dimethylamine does not form a stable complex with alkylated borated catechols nor does diisopropyl amine. The interaction of steric effects, nitrogen basicity and boron electrophilicity all come into play. These factors affect the equilibrium between the reactants and the products and make predictions of thermal stability impossible. One also cannot predict hydrolytic stability, which may or may not be related to thermal stability. The problem, therefore, addressed and solved by this invention is how to hydrolytically stabilize borated alkyl catechols so as to achieve a higher concentration of boron per pound of the borated alkyl catechols. This is achieved by complexing such catechols and stabilizing the same with a low molecular weight stabilizing material, i.e., diethylamine. According to the present invention, lubricating oils are provided which reduce wear, oxidation and deposits and are especially useful in the crankcase of internal combustion engines. The reduced wear, oxidation and deposits result from the addition to the lubricating oil of small amounts of a complex prepared by reacting a borated alkyl catechol with diethylamine. Thus, in one aspect, this invention provides a lubricating oil composition comprising an oil of lubricating viscosity and a minor amount of a hydrolytically stable complex of diethylamine and a borated alkyl catechol. In another aspect, this invention provides a concentrate of a neutral carrier oil containing from 5 to 80 weight percent (based on the neutral oil) of a stabilized diethylamine-borated alkyl catechol of this invention. These complexes may be readily prepared by contacting (a) a borated alkyl catechol and (b) diethylamine under conditions wherein a complex is formed between the diethylamine and the borated alkyl catechol, the amount of said diethylamine being sufficient to stabilize said borated alkyl catechol against hydrolysis. Other additives may also be present in the lubricating oils in order to obtain a proper balance of properties such as dispersancy, corrosion, wear and oxidation inhibition which are critical for the proper operation of an internal combustion engine. In still another aspect of this invention, there is provided a method for reducing wear, oxidation and deposits in an internal combustion engine by utilizing the lubricating oil composition described above. Advantageously, improvements in deposits of from 10%-50% may be obtained by employing the composition of this invention. This deposit improvement can be obtained in compression-ignition engines, that is, diesel engines. Improvements in viscosity control of 25%-50% may be obtained in spark-ignition engines, that is, gasoline engines. That is, lubricating oil compositions containing the borated alkyl catechol-diethylamine complex of this invention have been found additionally to possess (1) antioxidant properties in gasoline engines and (2) diesel deposit inhibition when employed in diesel engines. The borated alkyl catechols may be prepared by borating an alkyl catechol with boric acid with removal of the water of reaction. Typically, there is sufficient boron present such that each boron will react with about 2 to 3 hydroxyl groups present in the reaction mixture. (See Formulas IV, V and VI below.) The reaction may be carried out at a temperature in the range of 60°C-135°C or higher, in the absence or presence of any suitable organic solvent which forms an azeotrope with water such as benzene, xylenes, toluene and the like. Depending on the ratio of alkyl catechol to boron, the composition of the borated alkyl catechol, and therefore the composition of the amine adduct varies. It is believed that at a 3:2 ratio of alkyl catechol to boron and a 1:1 ratio of boron to nitrogen, the predominant product has a structure like Formula V below. At a 1:1 ratio of alkyl catechol to boron and a 1:1 ratio of boron to nitrogen the predominant product has a structure like Formula VI below. The alkyl catechols or mixtures thereof which may be used to prepare the borated alkyl catechols used in this invention are preferably mixtures of monoalkyl and dialkyl catechols. The monoalkyl catechols are preferably of Formula I wherein R is alkyl containing 10 to 30 carbon atoms and preferably from 18 to 24 carbon atoms and more preferably 20 to 24 carbon atoms. Also, up to 60% by weight but preferably less than 40% by weight of the monoalkyl catechols may have the R group in a position adjacent or ortho to one of the hydroxy groups and have the Formula II wherein R is as defined above. The dialkyl catechols which may be used to prepare a mixture of borated alkyl catechols of this invention are generally of Formula III wherein R is as defined above and the two R groups can be the same or different. Trialkyl catechols may also be employed although they are not preferred. Among the alkyl catechols which may be employed are decyl catechol, undecyl catechol, dodecyl catechol, tetradecyl catechol, pentadecyl catechol, hexadecyl catechol, octadecyl catechol, eicosyl catechol, hexacosyl catechol, triacontyl catechol, and the like. Also, a mixture of alkyl catechols may be employed such as a mixture of C₁₄-C₁₈ alkyl catechols, a mixture of C₁₈-C₂₄ alkyl catechols, a mixture of C₂₀-C₂₄ alkyl catechols, or a mixture of C₁₆-C₂₆ alkyl catechols may be used. The alkyl catechols of the Formula III may be prepared by reacting a C₁₀-C₃₀ olefin such as a branched olefin or straight-chain alpha olefin containing 10 to 30 carbon atoms or mixtures with catechol in the presence of a sulfonic acid catalyst at a temperature of from about 60°C-200°C, preferably 125°C-180°C, and most preferably 130°C-150°C in an essentially inert solvent at atmospheric pressure. Although alkylation of catechol can be carried out neat, in absence of solvents, the use of solvents, particularly in a batch reactor greatly facilitates the process due to better contact of the reactants, improved filtration, etc. Examples of the inert solvents include benzene, toluene, chlorobenzene and Chevron 250 Thinner which is a mixture of aromatics, paraffins and naphthenes. The term "branched olefin" means that branching occurs at the double bond, i.e., vinylidene olefins or trisubstituted olefins. The term "straight-chain alpha olefin" means that the alpha olefin contains little (less than about 20%) or no branching at the double bond or elsewhere. Monoalkyl catechols are preferred. A product which is predominantly monoalkyl catechol may be prepared by using molar ratios of reactants (catechol and alkylating olefin) and preferably a 10% molar excess of branched olefin or alpha olefin over catechol is used. When used at molar ratios, the resulting products are generally predominantly monoalkyl catechols but do contain some amounts of dialkyl catechol. A molar excess of catechol (e.g. two equivalents of catechol for each equivalent of olefin) can be used in order to enhance monoalkylation if predominantly monoalkyl catechol is desired. Predominantly dialkyl catechols may be prepared by employing a molar excess of olefin, such as two equivalents of the same or different olefin per equivalent of catechol. Dialkyl catechols are also useful in this invention. A typical weight ratio of monoalkyl to dialkyl catechol is in the range of 1:3 to 3:1. Use of a branched olefin results in a greater proportion of alkyl catechols of Formula I than use of straight-chain alpha olefins. Use of such branched olefins generally results in greater than 90% alkyl catechol of Formula I and less than 10% alkyl catechol of Formula II. On the other hand, the use of a straight-chain alpha olefin generally results in approximately 50% of alkyl catechols of Formula I and 50% of Formula II. In a case of C₂₀-C₂₄ olefin mixture, for example, containing 20% branching, the corresponding alkyl catechols will comprise about 60% of Formula I and 40% of Formula II. When the same or different olefin mixture contains 50% branching, the corresponding alkyl catechols will comprise approximately 70% of Formula I and 30% of Formula II. The exact structure of the complex of this invention is not known for certain. However, while not limiting this invention to any theory, it is believed that the compounds of this invention have a tetrahedral boron atom with three B-O bonds. The boron is either complexed to the nitrogen atom in the diethylamine via dative bonding, or is present as a salt. Tetrahedral Boron Formula IV illustrates dative bonding. Formula V is a 3:2 catechol to boron complex. Formula VI is a 1:1 catechol to boron complex. A borated alkyl catechol having a 3:2 mole ratio of catechol to boron (Formula V) or a 1:1 mole ratio of catechol to boron (Formula VI) is a function of the mole ratio of catechol to boron as noted above. The only two products that are believed to be present are the 1:1 and 3:2 products of Formulas V and VI. Nevertheless, due to equilibrium considerations, the product most likely is a mixture of the 1:1 and 3:2 complexes in varying proportions depending on the stoichiometry used. We have found that a 3:2 product is just as effective in a Sequence IIID test as the 1:1 product. It is thus preferred for cost and handling reasons that the borated alkyl catechol predominate in the 3:2 product and, more preferably, be substantially only the 3:2 product, i.e., that the product be made using a mole ratio of alkyl catechol to boron of about 3:2. The complex may be formed by reacting the borated alkyl catechol and the diethylamine together neat at a temperature above the melting point of the mixture of reactants and below the decomposition temperature, or at a suitable temperature in a diluent in which both reactants are soluble. Suitable temperatures can be about 30°C to 100°C, preferably about 50°C. For example, the reactants may be combined in the proper ratio in the absence of a solvent to form an homogeneous product or the reactants may be combined in the proper ratio in a solvent such as toluene or benzene, xylenes, chlorobenzene, or thinner, and the solvent then stripped off. The complex formed by either technique may then be added to the oil. Most diethylamine complexes of borated alkyl catechols are either liquids at room temperature, or low melting solids (m.p. 30°C-40°C) depending on the composition of their isomers and the purity of the product. Alternatively, the complex may be prepared in a lubricating oil as a concentrate containing from about 5 to 80% by weight of the complex, which concentrate may be added in appropriate amounts to the lubricating oil in which it is to be used or the complex may be prepared directly in the lubricating oil in which it is to be used. The diluent is preferably inert to the reactants and products formed, and is used in an amount sufficient to ensure solubility of the reactants and to enable the mixture to be efficiently stirred. Temperatures for preparing the complex may be in the range of from 20°C-200°C and preferably 25°C-60°C and under sufficient pressure to maintain the diethylamine in the liquid phase. The most preferred temperatures depend on whether the complex is prepared neat or in a diluent, i.e., higher temperatures may be used when a solvent is employed. An effective amount of diethylamine is added in order to stabilize the borated alkyl catechols against hydrolysis. In general, mole ratios of diethylamine to boron used to form the complex are in the range of 0.8:1 to 1.1:1, and preferably from 0.9:1 to 1:1, and most preferably 1:1. This latter ratio is preferred if the complex is made and/or stored neat or in the absence of solvent or lubricating oil and under atmospheric conditions. Higher amounts of the diethylamine can be used but provide no advantages. However, normally excess amine is added to insure complete stabilization and unreacted amine is recovered and recycled. As used herein, the term "stabilized against hydrolysis" means that the borated alkyl catechol-diethylamine complex does not "skin-over" or form a precipitate due to the hydrolysis of the borated catechol for a period of at least one week, preferably three months, when stored at room temperature (∼15°-25°C) and ambient humidity, i.e., no observable or measurable free boric acid is formed. By a stabilizing amount of amine is meant that amount to stabilize the borated alkyl catechol against hydrolysis. The amount of the complex required to be effective for reducing wear, oxidation and deposits in lubricating oil compositions is a minor amount and may range from 0.05% to 20% by weight. However, in the preferred embodiment, it is desirable to add sufficient complex so that the amount of borated catechol is added at a range from 0.1% to about 4% by weight of the total lubricant composition and preferably is present in the range from 0.2% to 2% by weight and most preferably 0.5% to 1%. The diethylamine is present in the complex of the invention in an amount effective to stabilize the borated alkyl catechol against hydrolysis and which allows the borated alkyl catechol to function as an effective oxidation and deposit reducing agent. The diethylamine-borated alkyl catechol complexes of this invention can be added to a lubricating oil (or can be made in the lubricating oil). In addition, it is contemplated that the complexes of this invention can be sold as a concentrate in a neutral oil with or without other ingredients such as dispersants, antirust agents, etc. The concentrate can therefore comprise a complex of a borated alkyl catechol and an amount to hydrolytically stabilize the borated alkyl catechol of diethylamine plus a neutral carrier oil. The weight percent of the diethylamine stabilized borated alkyl catechol in the concentrate is usually from 5 to 80 based on the weight of neutral carrier oil, typically 10 to 60. The term "neutral oil" is well known in the art, such as those neutral oils made commercially which have a viscosity in the lubricating oil range, such as 100 neutral oils, 200 neutral oils, etc. In general, the complexes of this invention may also be used in combination with other additive agents in conventional amounts for their known purpose. For example, for application in modern crankcase lubricants, the base composition described above will be formulated with supplementary additives to provide the necessary stability, detergency, dispersancy, antiwear and anticorrosion properties. Thus, as another embodiment of this invention, the lubricating oils which contain the complexes prepared by reacting the borated alkyl catechols and diethylamine may also contain an alkali or alkaline earth metal hydrocarbyl sulfonate, an alkali or alkaline earth metal phenate, and Group II metal salt dihydrocarbyl dithiophosphate, and conventional viscosity index improvers. The alkali or alkaline earth metal hydrocarbyl sulfonates may be either petroleum sulfonate, synthetically alkylated aromatic sulfonates, or aliphatic sulfonates such as those derived from polyisobutylene. One of the more important functions of the sulfonates is to act as a detergent and dispersant. These sulfonates are well known in the art. The hydrocarbyl group must have a sufficient number of carbon atoms to render the sulfonate molecule oil soluble. Preferably, the hydrocarbyl portion has at least 20 carbon atoms and may be aromatic or aliphatic, but is usually alkylaromatic. Most preferred for use are calcium, magnesium or barium sulfonates which are aromatic in character. Certain sulfonates are typically prepared by sulfonating a petroleum fraction having aromatic groups, usually mono- or dialkylbenzene groups, and the forming the metal salt of the sulfonic acid material. Other feedstocks used for preparing these sulfonates include synthetically alkylated benzenes and aliphatic hydrocarbons prepared by polymerizing a mono- or diolefin, for example, a polyisobutenyl group prepared by polymerizing isobutene. The metallic salts are formed directly or by metathesis using well-known procedures. The sulfonates may be neutral or overbased having base numbers up to about 400 mg of KOH per gram of sample or more. Carbon dioxide and calcium hydroxide or oxide are the most commonly used material to produce the basic or overbased sulfonates. Mixtures of neutral and overbased sulfonates may be used. The sulfonates are ordinarily used so as to provide from 0.3% to 10% by weight of the total composition. Preferably, the neutral sulfonates are present from 0.4% to 5% by weight of the total composition and the overbased sulfonates are present from 0.3% to 3% by weight of the total composition. The phenates for use in this invention are those conventional products which are the alkali or alkaline earth metal salts of alkylated phenols. One of the functions of the phenates is to act as a detergent and dispersant. Among other things, it prevents the deposit of contaminants formed during high temperature operation of the engine. The phenols may be mono- or polyalkylated. The alkyl portion of the alkyl phenate is present to lend oil solubility to the phenate. The alkyl portion can be obtained from naturally occurring or synthetic sources. Naturally occurring sources include petroleum hydrocarbons such as white oil and wax. Being derived from petroleum, the hydrocarbon moiety is a mixture of different hydrocarbyl groups, the specific composition of which depends upon the particular oil stock which was used as a starting material. Suitable synthetic sources include various commercially available alkenes and alkane derivatives which, when reacted with the phenol, yield an alkylphenol. Suitable radicals obtained include butyl, hexyl, octyl, decyl, dodecyl, hexadecyl, eicosyl, triacontyl, and the like. Other suitable synthetic sources of the alkyl radical include olefin polymers such as polypropylene, polybutylene, polyisobutylene and the like. The alkyl group of the alkyl phenate can be straight-chained or branched-chained, saturated or unsaturated (if unsaturated, preferably containing not more than 2 and generally not more than 1 site of olefinic unsaturation). The alkyl radicals will generally contain from 4 to 30 carbon atoms. Generally, when the phenol is monoalkyl-substituted, the alkyl radical should contain at least 8 carbon atoms. The phenate may be sulfurized if desired. It may be either neutral or overbased and if overbased will have a base number of up to 200 to 300 mg of KOH per gram of sample or more. Mixtures of neutral and overbased phenates may be used. The phenates are ordinarily present in the oil to provide from 0.2% to 27% by weight of the total composition. Preferably, the neutral phenates are present from 0.2% to 9% by weight of the total composition and the overbased phenates are present from 0.2% to 13% by weight of the total composition. Most preferably, the overbased phenates are present from 0.2% to 5% by weight of the total composition. Preferred metals are calcium, magnesium, strontium or barium. The sulfurized alkaline earth metal alkyl phenates are preferred. These salts are obtained by a variety of processes such as treating the neutralization product of an alkaline earth metal base and an alkylphenol with sulfur. Conveniently, the sulfur, in elemental form, is added to the neutralization product and reacted at elevated temperatures to produce the sulfurized alkaline earth metal alkyl phenate. If more alkaline earth metal base were added during the neutralization reaction than was necessary to neutralize the phenol, a basic sulfurized alkaline earth metal alkyl phenate is obtained. See, for example, the process of Walker et al., U.S. Patent No. 2,680,096. Additional basicity can be obtained by adding carbon dioxide to the basic sulfurized alkaline earth metal alkyl phenate. The excess alkaline earth metal base can be added subsequent to the sulfurization step but is conveniently added at the same time as the alkaline earth metal base is added to neutralize the phenol. Carbon dioxide and calcium hydroxide or oxide are the most commonly used material to produce the basic or "overbased" phenates. A process wherein basic sulfurized alkaline earth metal alkylphenates are produced by adding carbon dioxide is shown in Hanneman, U.S. Patent No. 3,178,368. The Group II metal salts of dihydrocarbyl dithiophosphoric acids exhibit wear, antioxidant and thermal stability properties. Group II metal salts of phosphorodithioic acids have been described previously. See, for example, U.S. Patent No. 3,390,080, Columns 6 and 7, wherein these compounds and their preparation are described generally. Suitably, the Group II metal salts of the dihydrocarbyl dithiophosphoric acids useful in the lubricating oil composition of this invention contain from about 4 to about 18 carbon atoms in each of the hydrocarbyl radicals and may be the same or different and my be aromatic, alkyl or cycloalkyl. Preferred hydrocarbyl groups are alkyl groups containing from 4 to 8 carbon atoms and are represented by butyl, isobutyl, sec-butyl, hexyl, isohexyl, octyl, 2-ethylhexyl, p-tolyl, xylyl and the like. The metals suitable for forming these salts include barium, calcium, strontium, zinc and cadmium, of which zinc is preferred. Preferably, the Group II metal salt of a dihydrocarbyl dithiophosphoric acid has the following formula: wherein: R₂ and R₃ each independently represent hydrocarbyl radicals as described above, and M₁ represents a Group II metal cation as described above. The dithiophosphoric salt is present in the lubricating oil compositions of this invention in an amount effective to inhibit wear and oxidation of the lubricating oil. The amount ranges from about 0.1% to about 4% by weight of the total composition, preferably the salt is present in an amount ranging from about 0.2% to about 2.5% by weight of the total lubricating oil composition. The final lubricating oil composition will ordinarily contain 0.025% to 0.25% by weight phosphorus and preferably 0.05% to 0.15% by weight. The finished lubricating oil may be single or multigrade. Multigrade lubricating oils are prepared by adding viscosity index (VI) improvers. Typical viscosity index improvers are polyalkyl methacrylates, ethylene propylene copolymers, styrene-diene copolymers and the like. So-called decorated VI improvers having both viscosity index and dispersant properties are also suitable for use in the formulations of this invention. The lubricating oil used in the compositions of this invention may be mineral oil or synthetic oils of lubricating viscosity and preferably suitable for use in the crankcase of an internal combustion engine. Crankcase lubricating oils ordinarily have a viscosity of about 1300 cSt at 0°F (1300x10⁻⁶ m²/s @ -17.7°C) to 22.7 cSt at (22.7x10⁻⁶ m²/s) at 210°F (99°C). The lubricating oils may be derived from synthetic or natural sources. Mineral oil for use as the base oil in this invention includes paraffinic, naphthenic and other oils that are ordinarily used in lubricating oil compositions. Synthetic oils include both hydrocarbon synthetic oils and synthetic esters. Useful synthetic hydrocarbon oils include liquid polymers of alpha olefins having the proper viscosity. Especially useful are the hydrogenated liquid oligomers of C₆-C₁₂ alpha olefins such as 1-decene trimer. Likewise, alkyl benzenes of proper viscosity, such as didodecyl benzene, can be used. Useful synthetic esters include the esters of both monocarboxylic acid and polycarboxylic acids as well as monohydroxy alkanols and polyols. Typical examples are didodecyl adipate, pentaerythritol tetracaproate, di-2-ethylhexyl adipate, dilaurylsebacate and the like. Complex esters prepared from mixtures of mono- and dicarboxylic acid and mono- and dihydroxy alkanols can also be used. Blends of hydrocarbon oils with synthetic oils are also useful. For example, blends of 10 to 25 weight percent hydrogenated 1-decene trimer with 75 to 90 weight percent 150 SUS (100°F) (32.0 x10⁻⁶ m² s @ 37.8°C) mineral oil gives an excellent lubricating oil base. Other additives which may be present in the formulation (or in the concentrate referred to above) include rust inhibitors, foam inhibitors, corrosion inhibitors, metal deactivators, pour point depressants, antioxidants, and a variety of other well-known additives. The following Examples illustrate various stages in the preparation of the borated alkyl catechol complexes of the invention. Example 1 Preparation of C₁₈-C₂₄ Alkyl Catechol by Batch Process A 30-gallon (113.55 l.) reactor equipped with a stirrer, condenser, Dean-Stark trap, and nitrogen inlet and outlet, was charged with 61.67 pounds (27.93 kg) of C₁₈-C₂₄ olefins (less than C₁₄, 2.7%; C₁₄, 0.3%; C₁₆, 1.3%; C₁₈, 8.0%; C₂₀, 44.4%; C₂₂, 29.3%; C₂₄, 11.2%; C₂₆ and above, 2.8%) containing at least 40% branched olefins (available from Ethyl Corp.), 18.32 pounds (8.30 kg) catechol, 8.0 pounds (3.62 kg) sulfonic acid cation exchange resin (polystyrene cross-linked with divinylbenzene) catalyst (Amberlyst-15, available from Rohm and Haas, Philadelphia, PA), and 9 gallons (34.06 l.) of Chevron 350H thinner. With a stirrer set at 150 rpm, the reaction was carried out at 141°C-143°C for a total of 14.7 hours. The reaction mixture was stripped by heating at 143°C under vacuum (50 mm Hg) (6666 Pa) for 4 hours. The product was filtered hot over diatomaceous earth to afford 67.21 pounds (30.45 kg) of a liquid C₁₈-C₂₄ alkyl catechol. The product contained 1.4% of unreacted catechol by infrared analysis, a hydroxyl number of 199 mg KOH/g, and a low sediment level of 0.02 vol %. Chromatographic analysis showed the product to contain 2.6% of Chevron 350H thinner, 7.4% unreacted olefin, 45.2% monoalkyl catechols, and 44.8% dialkyl catechols. Example 2 Preparation of C₂₀-C₂₄ Alkyl Catechol by Batch Process A 10-gallon (37.85 l.)reactor equipped with a stirrer, condenser, Dean-Stark trap, and nitrogen inlet and outlet, was charged with 15.68 pounds (7.10 kg.) of a mixture of C₂₀-C₂₄ olefins (C₁₈, 2.2%; C₂₀, 47.3%; C₂₂, 39.8%; C₂₄, 10.2%; C₂₆, 0.5%) containing at most 20% branched olefins (available from Chevron), 4.76 pounds (2.16 kg.) catechol, 2.16 pounds (0.98 kg.) sulfonic acid cation exchange resin (polystyrene cross-linked with divinylbenzene) catalyst (Amberlyst-15, available from Rohm and Haas, Philadelphia, PA), and 1.5 (5.68 l.) gallons of Chevron 350H thinner. The reaction mixture was heated at 135°C-143°C for a total of 14 hours, with a stirrer set at 200 rpm under a nitrogen atmosphere. The reaction mixture was then stripped by heating at 150°C under vacuum (25 mm Hg) (3333 Pa) for two hours. The product was filtered hot over diatomaceous earth to afford 16.83 pounds (7.62 kg) of a liquid C₂₀-C₂₄ alkyl catechol. The product contained 1.7% of unreacted catechol by infrared analysis, a hydroxyl number of 195 mm KOH/g, and a low sediment level of 0.02 vol %. Chromatographic analysis showed the product to contain 3.3% of Chevron 350H thinner, 3.4% unreacted olefin, 42.9% monoalkyl catechols, and 50.4% dialkyl catechols. Example 3 Preparation of C₁₈-C₂₄ Alkyl Catechol by Continuous Flow Reactor A 450-ml mixture of catechol and C₁₈-C₂₄ olefin (same as in Example 1 above), in a molar ratio of 0.90/1.0, was preheated to 120°C in a volumetric burette, and then pumped upward through a 24-inch x ½-inch O.D. (60.96 cm. x 1.27 cm O.D.) stainless steel reactor containing 210 ml of Amberlyst-15, maintained at 120°C (±2°), over a period of 7 hours. The extent of reaction was monitored by GLC. The product was collected and recycled 5 times until the reaction was essentially complete. Analysis of final product by GLC after a total of 40 hours onstream showed the following composition: catechol, 3.3%; unreacted olefin and paraffin present in olefin feed, 14.6%; monoalkyl catechols, 54.3%; and dialkyl catechols, 27.8%. The linear hourly space velocity (LHSV) corresponded on the average to about 0.30 per hour (i.e., volume feed/volume catalyst/hour). The weight ratio of monoalkyl- to dialkyl catechols in the product corresponded to about 66:34. Example 4 Boration of C₁₈-C₂₄ Alkyl Catechol A 3-liter, three-necked, round-bottomed glass flask, equipped with a stirrer, condenser, Dean-Stark trap, and nitrogen inlet, was charged with 860 g of C₁₈-C₂₄ alkyl catechols prepared according to Example 1, 79.1 g boric acid, and 1200 ml toluene. The reaction mixture was heated under reflux, while stirring, at 115°C-125°C, collecting a total of 50 g of water in the trap in 6 hours. The reaction mixture was then stripped of solvent by heating at 135°C under vacuum (20-25 mm Hg) (2666 - 3333 Pa) for 3 hours to give 850 g of a liquid, borated C₁₈-C₂₄ alkyl catechol. Analysis for boron gave a value of 1.3%, and a measured viscosity at 100°C of 27 cSt (27x10⁻⁶ m²/s). Exposure of a small sample of product to atmospheric moisture, resulted in boric acid formation on the surface in a matter of seconds. In less than one day the material was hazy and crusted on top. This product was prepared using 3 moles of catechol per 2 moles of boron and the product is believed to have the structure shown in Formula V above. Example 5 Boration of C₂₀-C₂₄ Alkyl Catechol A 2-liter, three-necked, round-bottomed flask, equipped with a stirrer, condenser, Dean-Stark trap, and nitrogen inlet, was charged with 585 g of C₂₀-C₂₄ alkyl catechol prepared according to Example 2, 41.1 g boric acid, and 785 ml toluene. The mixture was then heated while stirring at reflux (115°C-125°C) under nitrogen for a period of 6 hours, collecting a total of 32 g of water in the Dean-Stark trap, although most of the water had been collected during the first 3 hours. The product was then stripped of toluene solvent by heating the reaction mixture to 135°C under vacuum (20-25 mm Hg) (2666 - 3333 Pa) for 3.5 hours. A total of 580 g of borated C₂₀-C₂₄ alkyl catechol was isolated, which partially solidified on standing in the flask, under nitrogen, at room temperature. The product had a measured viscosity at 100°C of 30 cSt (30 x10⁻⁶ m²/s), and boron content of 1.28%. Exposure of a small sample of product to atmospheric moisture on a watch glass, led to formation of white, crystalline, boric acid on the surface in a matter of seconds. This product was prepared using 3 moles of catechol per 2 moles of boron and the product is believed to have the structure shown in Formula V above. Example 6 Amine Treatment of Borated C₁₈-C₂₄ Alkyl Catechol A 2-liter, three-necked, round-bottomed glass flask, equipped with a stirrer, condenser, and an addition funnel, was charged with 770 g of borated C₁₈-C₂₄ alkyl catechol prepared according to Example 4. While vigorously stirring, 88 g of diethylamine was added to the alkyl catechol over a period of 1 hour, maintaining a temperature during addition below 50°C. When amine addition was completed, the reaction mixture was stirred at 50°C for 1 hour, and then heated to 135°C under vacuum (20-25 mm Hg) (2666 - 3333 Pa) for 1 hour to remove unreacted amine. A total of 821 g of product was recovered, containing 1.27% of boron, which gave a measured viscosity at 100°C of 280 cSt (280x10⁻⁶ m²/s). The product on exposure to atmospheric moisture gave no evidence of boric acid formation after 1 hour and after one year, the product remained bright and clear. Comparing Examples 4 and 6, it can be seen that the haze and crust formed in Example 4 can be prevented by using an effective amount of diethylamine. The addition of the diethylamine results in a substantial viscosity increase in the final complex but this increase in viscosity is quite manageable in the plant for manufacturing purposes. Usually, the viscosity of the complex is typically in the range of 200 to 400 cSt (200 x 10⁻⁶ - 400 x10⁻⁶ m²/s) at 100°C. Example 7 Amine Treatment of Borated C₂₀-C₂₄ Alkyl Catechol A 100-g sample of product prepared according to Example 5 was dissolved in about 100 ml of toluene, and while stirring, was treated with 10.2 g of diethylamine over a period of about 10 minutes, allowing the temperature of the reaction to reach 52°C. After about 15 minutes, when the temperature started to decrease, the mixture was heated to 135°C under vacuum (20-25 mm Hg) (2666 - 3333 Pa) for 1.5 hours, to strip off unreacted amine and the solvent. A total of 98.3 g of product was isolated as an oil, which on standing solidified to a low melting solid, m.p. 35°C. Analysis for boron and nitrogen gave values of 1.20% and 1.09%, respectively. The product had a measured viscosity at 100°C of 300 cSt (300 x10⁻⁶ m²/s). The product on exposure to atmospheric moisture for about 1 hour showed no signs of any hydrolysis and this remained true even after three months. Example 8 Boration and Amine Treatment of C₁₈-C₂₄ Alkyl Catechol in Large Vessel A 30-gallon (113.55 l.) reactor equipped with a stirrer, condenser, and Dean-Stark trap, was charged with 44.05 pounds (19.95 kg.) of C₁₈-C₂₄ alkyl catechol prepared according to Example 1, 4.25 pounds (1.92 kg.) boric acid, and 5.8 gallons (21.95 l.) Chevron 51 L solvent. The reaction mixture was heated while stirring at 150 rpm at reflux (100°C-124°C) for a total of 22 hours, collecting 3.08 pounds (1.39 kg.) of water in the trap. The reaction mixture was cooled to room temperature, and while stirring, 5.03 pounds (2.28 kg.) of diethylamine was incrementally added to the reaction mixture over a period of 4 hours, maintaining a temperature during addition below the boiling point of the amine (55°C). When amine addition was completed, the reaction mixture was heated to 100°C for 1 hour, and then stripped at 100°C under vacuum (45-50 mm Hg) (5333 - 6666 Pa) for 1 hour, and finally 135°C for an additional hour. A total of 52.20 pounds (23.65 kg.) of borated and diethylamine treated C₁₈-C₂₄ alkyl catechol was formed. The product gave a total base number (TBN) of 45 mg KOH/g, and a sediment value of 0.08 vol %. Analysis for boron and nitrogen gave values of 1.15% and 1.20%, respectively. The product on exposure to atmospheric moisture for about 1 hour showed no signs of any hydrolysis and this remained true even after three months. This product was prepared using 3 moles of catechol per 2 moles of boron and the product is believed to have the structure shown in Formula V above. Example 9 Boration and Amine Treatment of C₂₀-C₂₄ Alkyl Catechol A 3-liter, round-bottomed flask, equipped with a condenser, stirrer, Dean-Stark trap, and an additional funnel, was charged with 4.40 pounds (1.99 kg) of C₂₀-C₂₄ alkyl catechol prepared according to Example 2, 0.63 pounds (0.28 kg) boric acid, and approximately 0.30 gallons (1.14 l.) toluene. The mixture was heated under reflux, while stirring, collecting a total of 0.29 pounds (0.13 kg.) of water in a course of 4 hours. The borated alkyl catechol in toluene in the flask was cooled to room temperature, and gradually treated with 0.78 pounds (0.35 kg.) diethylamine over a period of 4 hours, maintaining a temperature during addition below the boiling point of diethylamine (55°C). After standing overnight, the reaction mixture was stripped at 140°C under high vacuum (2-3 mm Hg) (266 - 400 Pa) for 3 hours to give 4.62 pounds (2.09 kg.) of liquid, borated, amine treated C₂₀-C₂₄ alkyl catechol. On standing, the product solidified to a low melting material, m.p. 33°C. Analysis for boron and nitrogen gave values of 1.10% and 1.09%, respectively. Measurement of viscosity at 100°C gave a value of 325 cSt (325x10⁻⁶ m²/s). Analysis of product by differential scan calorimetry (DSC) gave an exotherm at 177°C, suggesting that the loss of amine had occurred at this temperature. The product on exposure to atmospheric moisture for about 1 hour showed no signs of any hydrolysis and this remained true even after 3 months. This product was prepared using 3 moles of catechol per 2 moles of boron and the product is believed to have the structure shown in Formula V above. Gasoline Engine Runs A series of Examples were carried out which demonstrate the improvements in oxidation and wear obtained by adding lubricating oil compositions of this invention to the crankcase of a gasoline automobile engine using additives prepared by Example 6. In these Examples, a 350 CID Oldsmobile gasoline engine was run on a dynamometer. An engine oiling system was devised in order to provide proper lubrication to the engine and also to provide the capability to change the oil without stopping the engine. Basically, a dry sump system was used with an external pump providing lubrication to the engine. This pump was connected through valves to four external sumps. The positioning of the valves determined the oil used. The gasoline engine runs were carried out in an eight-cylinder Oldsmobile engine for a period of 64 hours according to Sequence IIID specifications. The formulation contained a known concentration of oxidation inhibitor of this invention to be tested, 3.5% dispersant, 40 mmol/kg mixed calcium and magnesium sulfonates, 16 mmol/kg mixed zinc dialkyldithiophosphates, 10% viscosity index improver (ethylene propylene copolymer) in Exxon 100N/150N base oils, formulated to SAE 10W-30 grade. The reference runs (Examples 10 and 11 below) were carried out under identical conditions, using the same stand, using the above formulation, but containing no oxidation inhibitor, i.e., without using the stabilized borated alkyl catechols of this invention. The results of the Examples are summarized in Table I below. Referring to Table I, the reference runs (Examples 10 and 11) showed 29.6 hours to increase viscosity 375%. The Sequence IIID specification is a minimum of 64 hours to have a 375% increase in viscosity. Similarly, Sequence IIID specifies a wear of less than 4.0 mils (0.1 m.m.). A comparison of Examples 12 through 15 with Examples 10 and 11 shows the improvements in antioxidant properties by the addition of the additives of the invention. Other engine Examples were carried out in Chevron base oils employing the formulation consisting of a known concentration of oxidation inhibitor, 3.5 wt. % dispersant, 45 mmol/kg mixed calcium and magnesium sulfonate, 13 mmol/kg zinc dialkyldithiophosphate, 10.5% viscosity index improver (ethylene propylene copolymer) in Chevron base oils formulated to a 5W-30 grade. The results are summarized in Table II below. Referring to Table II, a comparison of Examples 18 through 21 with the base runs (Examples 16 and 17) shows that the addition of the stabilized borated alkyl catechols of the invention improves the oxidation properties of the Chevron base oils. Diesel Engine Examples A series of Examples were carried out which demonstrate the improvements in deposit control in a diesel engine by adding additives prepared according to Example 8 or 9. The diesel engine runs were carried out in a single cylinder Caterpillar engine for a period of 60 hours according to 1G2 specification, using a formulation containing a diesel deposit inhibitor of Example 8, 8% dispersant, 50 mmol/kg calcium phenate, 16 mmol/kg mixed zinc dialkyldithiophosphate, and 10% viscosity index improver (ethylene propylene copolymer) in Chevron 100N/240N base oil. For comparison purposes, the reference runs were carried out under identical conditions, in the same engine stand, using the above formulation, but without the deposit inhibitor. The results are shown in Table III. Referring to Table III, six reference runs (Examples 22-27) were made to obtain a statistically meaningful base average for TGF and WTP. A comparison of Examples 28-31 with the average of Examples 22-27 shows that using the stabilized alkyl borated catechol of this invention improves the deposit control properties of the lubricating oil. Examples 32-34 In these Examples, three different amines were used to stabilize a borated alkyl catechol (as prepared in Example 4 above) and wherein the catechol to boron mole ratio was 3:2. The amount of amine added was sufficient to achieve a 1:1 nitrogen to boron mole ratio. The results are shown in Table IV below. As can be seen from Table IV, only diethylamine provides acceptable hydrolytic stability. Examples 35-38 In these Examples, three different amines were used to stabilize borated alkyl catechols wherein the catechol to boron mole ratio was either 3:2 or 1:1. The 3:2 catechol was prepared as in Example 4 above while the 1:1 catechol was also prepared in Example 4 above, but using an additional 44.5 g. of boric acid to achieve a 1:1 nitrogen to boron mole ratio. The results are shown in Table V below. Referring to Table V, Examples 37 and 38 show that the use of diethylamine stabilizes the borated alkyl catechols regardless of whether the ratio of catechol to boron is 1:1 (Formula VI) or 3:2 (Formula V). Examples 35 and 36 show that the use of triethylamine stabilizes only the 3:2 product. The poor stabilization in Example 36 may be due to stearic effects since the 1:1 product (Formula VI) has the boron atoms closer together. Examples 39-40 In these Examples, two different aromatic amines were used in an attempt to stabilize the 3:2 borated alkyl catechol prepared in accordance with Example 4 above. The results are shown on Table VI below. Referring to Table VI, Examples 39 and 40 show that aniline and benzyl amine were not acceptable hydrolytic stabilizing agents for the borated alkyl catechols of this invention. It is to be understood that various modifications of the present invention will occur to those skilled in the art upon reading the foregoing disclosure. For example, it is within the purview of the present invention to use diethylamine to stabilize a borated alkyl catechol which has been partially stabilized with some other stabilizing agent such as a succinimide or, perhaps, another amine, such as triethylamine.

Claims: A lubricating oil additive comprising a complex obtainable by reacting a borated alkyl catechol with diethylamine in an amount sufficient to hydrolytically stabilize the borated alkyl catechol. An additive as claimed in Claim 1, wherein the amount of diethylamine is at least 0.8 moles of diethylamine per mole of boron. An additive as claimed in Claim 2, wherein the molar ratio of diethylamine to boron is from 0.8:1 to 1.1:1. An additive as claimed in Claim 3, wherein the molar ratio of diethylamine to boron is 1:1. An additive as claimed in Claim 1, 2, 3 or 4, wherein the borated alkyl catechol contains one or two alkyl groups each having from 10 to 30 carbon atoms. An additive as claimed in Claim 1, 2, 3 or 4, wherein the alkyl group of said borated alkyl catechol is a mixture of alkyl groups containing 18 to 24 carbon atoms. An additive as claimed in Claim 1, 2, 3 or 4, wherein the alkyl group of said borated alkyl catechol is a mixture of alkyl groups containing 20 to 24 carbon atoms. An additive as claimed in any preceding claim, wherein said borated alkyl catechol is a mixture of (i) a borated alkyl catechol wherein the molar ratio of alkyl catechol to boron is 1:1 and (ii) a borated alkyl catechol wherein the molar ratio of alkyl catechol to boron is 3:2. An additive as claimed in Claim 8, wherein in said mixture the predominant borated alkyl catechol is that having an alkyl catechol to boron mole ratio of 3:2. An additive as claimed in Claim 9, wherein said predominant borated alkyl catechol is substantially the only one present. An additive as claimed in any preceding claim, wherein said complex is obtained in the presence of a solvent and at a temperature of from 30°C to 100°C. A lubricating oil composition for an internal combustion engine comprising an oil of lubricating viscosity and an additive as claimed in any one of Claims 1 to 11. A lubricating oil composition as claimed in Claim 12, wherein the additive is present in an amount such that said complex is present in from 0.05% to 20% by weight of the total composition. A method of reducing the oxidation and deposits in an internal combustion engine comprising internally lubricating said engine with a lubricating oil composition as claimed in Claim 12 or 13. Use of a complex produced by reacting a borated alkyl catechol with diethylamine in a lubricating oil composition for an internal combustion engine for the purpose of reducing wear, oxidation and deposits. Use of diethylamine for forming a complex with a borated alkyl catechol for the purpose of hydrolytically stabilizing the catechol. A concentrate comprising a neutral carrier oil and from 5 to 80 weight percent, based on the neutral oil, of a hydrolytically stabilized reaction product of a borated alkyl catechol and diethylamine.

Inventors: LISTON THOMAS V, ONOPCHENKO ANATOLI, SMALL VERNON R JR, LISTON, THOMAS V., ONOPCHENKO, ANATOLI, SMALL, VERNON R., JR.
Applicants: CHEVRON RES & TECH, CHEVRON RESEARCH AND TECHNOLOGY COMPANY
Application year: 1990
Main classification: C10M139
IPC codes: C07F5, F02B1, C10M139