Polymerisable compound and polymer therefrom

Abstract: Novel compounds having both an alpha-ketoester group and a polymerisable double bond, from which polymers may be prepared, are of formula I A-X-CO-COOR₁ (I) wherein A is alkenyl, alkynyl, alkenylaryl or alkenylaralkyl of up to 18 C atoms, or a group of formula Ia CH₂=CR₂-CO-(-Y-CH₂-CHR₃-) n -[-O-CO-(CH₂) m -] l - (Ia) wherein R₂ and R₃ are independently selected from H and C₁₋₅ alkyl, Y is -O- or -NR₄-, R₄ being H or C₁₋₅ alkyl, n is an integer of 1 to 5, m is an integer of 1 to 10, and l is 0 or an integer of 1 to 20; R₁ is H, C₁₋₅ alkyl or aryl; and X is -O-, -S-, -COO- or -NR₅-, R₅ being H or C₁₋₅ alkyl, provided that, if Y is present, X is not -NR₅-.

Description: The present invention relates to polymerisable compounds which have both an α-ketoester group and a polymerisable double bond, to their preparation, and to polymers prepared therefrom. BACKGROUND OF THE INVENTION It is known that a α-ketoester group (-CO-COOR) is a chemically-active group which can be ester-exchanged with an active hydrogen-containing compound, such as an alcohol or an amine, or can be easily hydrolysed. Polymers including an α-ketoester group would be of chemical interest. In order to obtain such polymers, a compound which has both an α-ketoester group and a polymerisable double bond is required. EP-A-0020000 and NL-A-6612666 disclose general formulae including compounds which have both an α-ketoester group and a polymerisable double bond, but there are very few examples of the synthesis of such compounds. SUMMARY OF THE INVENTION Novel polymerisable compounds according to the present invention are of formula I CH₂=CR₂-CO-(-Y-CH₂-CHR₃-) n -[-O-CO-(CH₂) m -] l -X-CO-COOR₁ (I) wherein R₂ and R₃ are independently selected from H and C₁₋₅ alkyl; Y is -O- or -NR₄-, R₄ being H or C₁₋₅ alkyl; n is an integer of 1 to 5; m is an integer of 1 to 10; l is 0 or an integer of 1 to 20; R₁ is H, C₁₋₅ alkyl or aryl; and X is -O-, -S- or -COO-. Polymerisable compounds of the invention are prepared by reacting a corresponding active hydrogen-containing compound of the formula CH₂=CR₂-CO-(-Y-CH₂-CHR₃-) n -[-O-CO-(CH₂) m -] l -XH (II) with a corresponding ester of the formula Z-CO-COOR₁ (III) wherein Z is halogen or OR₁. Polymerisable compounds of the invention may be used to produce polymers and curable compositions containing them. DESCRIPTION OF THE INVENTION The process for preparing polymerisable compounds of the invention employs, as the active hydrogen-containing compound (II), a compound which has a hydrogen atom directly bonded to an electrophilic atom or group X, i.e. -O-, -S- or -COO-. Accordingly, the active hydrogen may be present in a hydroxyl, thiol or carboxyl group. Typical examples of the active hydrogen-containing compounds (II) are 2-hydroxyethyl methacrylate, 2-hydroxyethyl acrylate, 2-hydroxypropyl methacrylate, 2-hydroxypropyl acrylate, 2-(2-hydroxyethoxy)ethyl acrylate and compounds of the formula CH₂=C(CH₃)-CO-O-CH₂-CH₂-[-O-CO-(CH₂)₅-] k -OH wherein k is 1 to 5. The ester compound (III) employed in the present invention includes oxalic diesters, such as dimethyl oxalate, diethyl oxalate, diisopropyl oxalate, dibutyl oxalate or diphenyl oxalate, and alkoxalyl halides, such as methoxalyl chloride or ethoxalyl chloride. If the ester compound (III) is the alkoxalyl halide (Z is halogen), the reaction between the compound (III) and the compound (II) is a dehydrohalogenation reaction which progresses quantitatively. The reaction may be carried out at room temperature to 150°C, preferably 50 to 100°C, in an inert solvent. Examples of inert solvents are aliphatic hydrocarbons, such as pentane, hexane and heptane; aromatic hydrocarbons, such as benzene, toluene and xylene; cycloaliphatic hydrocarbons, such as cyclohexane, methylcyclohexane and decalin; petroleum hydrocarbons, such as petroleum ether and petroleum benzine; halogenated hydrocarbons, such as carbon tetrachloride, chloroform, 1,2-dichloroethane; ethers, such as ethyl ether, isopropyl ether, anisol, dioxane and tetrahydrofuran; ketones, such as acetone, methyl ethyl ketone, cyclohexanone, acetophenone and isophorone; esters, such as ethyl acetate, butyl acetate, propylene glycol monoethyl ether acetate and ethylene glycol monoethyl ether acetate; acetonitrile; dimethylformamide; dimethylsulfoxide; and the like. Removal of the byproduct hydrogen chloride may be carried out by a method wherein nitrogen gas is blown into the reaction vessel, or a method wherein hydrogen chloride is reacted with a tertiary amine to form a salt of HCl which is removed out. If the compound (III) is the oxalic diester (Z is - OR₁), the reaction between the compound (III) and the compound (II) is an ester exchange reaction which is generally carried out using excess dialkyl oxalate in the presence of a catalyst and a polymerization inhibitor. The amount of the dialkyl oxalate is 2 to 20 times, preferably 3 to 8 times larger than the molar amount of the compound (II) and the reaction temperature is within the range of room temperature to 150 °C, preferably 50 to 120 °C. The reaction may be carried out in an inert solvent as mentioned above. Typical examples of the catalysts are tin compounds, such as dibutyltin dilaurate, dibutyltin oxide and monobutyltin triheptate; mixture catalysts, such as dimethyltin diiodide and tetraphenylantimony iodide, dimethyltin diiodide and hexamethyl phosphoric triamide; acidic compounds, such as p-toluenesulfonic acid, dodecylbenzenesulfonic acid, sulfuric acid, chloric acid, nitric acid and boron trichloride etherate; basic compounds, such as triethylamine, 1,4-diazabicyclo[2,2,2]octane, 1,8-diazobicyclo[5,4,0]undecene-7, pyridine sodium methoxide, sodium ethoxide and t-butoxypotassium hexamethylphosphoric triamide; metal oxides or metal salts, such as manganese acetate, cobalt acetate, calcium acetate, lithium acetate, zinc acetate, magnesium acetate, antimony trioxide, lead dioxide, ferric chloride, aluminum triisopropoxide and tetraisopropoxy titanium; and the like. Typical examples of the polymerization inhibitors are hydroquinone, p-methoxyphenol, 2,6-di-t-butyl-4-methylphenol, 4-t-butylcatechol, bisdihydroxybenzylbenzene, 2,2'-methylenebis(6-t-butyl-3-methylphenol), 4,4'-thiobis(6-t-3-methylphenol), p-nitrosophenol, diisopropylxanthogen sulfide, N-nitrosophenylhydroxylamine ammonium salt, dithiobenzylsulfide, p,p'-ditolyltrisulfide, p,p'-ditolyltetrasulfide, dibenzyltetrasulfide, tetraethylthiuramsulfide and the like. The obtained product may be purified by distillation, crystallization, chromatography etc. Distillation is generally effected at a reduced pressure (from atmospheric pressure to 1,33 Pa (0.01 mmHg)) at a temperature of room temperature to 180 °C, preferably 50 to 120 °C, in the presence of zeolite or with stirring. The obtained polymerizable compound of the present invention can be polymerized solely or with a copolymerizable compound. Polymerization may be carried out at a temperature of 50 to 150 °C, preferably 70 to 120 °C, in the inert solvent mentioned above in the presence of a polymerization initiator. Typical examples of the polymerization initiators are azobisisobutyronitrile, benzoyl peroxide, cumene hydroperoxide, tetramethylthiuramdisulfide, 2,2-azobis(4-methoxy-2,4-dimethylvaleronitrile), acetylcyclohexylsulfonyl peroxide, 2,2'-azobis(2,4-dimethylvaleronitrile) and the like. The copolymerizable compound employed in the present invention includes mono-olefins or di-olefins, such as styrene, alpha-methylstyrene, alpha-ethylstyrene, 2-methyl-1-butene, ethylene, propylene, butylene, amylene, hexylene, butadiene-1,3, isoprene etc.; halogenated mono-olefins or di-olefins, such as alpha-chlorostyrene, alpha-bromostyrene etc.; organic or inorganic esters, such as vinyl acetate, vinyl propionate, vinyl butyrate, vinyl benzoate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, hexyl methacrylate, methyl acrylate, ethyl acrylate, propyl acrylate, allyl chloride, allylcyanamide, allyl acetate, allyl propionate, allyl butylate, dimethyl maleate, diethyl maleate, dimethyl fumarate, diethyl fumarate, dimethacryl fumarate, diethyl glutarate etc.; organic nitriles, such as acrylonitrile, methacrylonitrile, ethacrylonitrile, 3-octenenitrile, crotonitrile and oleonitrile; unsaturated acids, such as acrylic acid, methacrylic acid, crotonic acid etc.; unsaturated alcohols, such as a monoester of the unsaturated acid mentioned above and a glycol (e.g. ethylene glycol or propylene glycol); unsaturated amides, such as acrylamide, methacrylamide, crotonamide etc.; unsaturated sulfonic acids or salts thereof, such as 2-sulfoethyl acrylate, p-vinylbenzenesulfonic acid etc. The polymer (or copolymer) of the present invention has at least two alpha-ketoester groups which are reactive with other active hydrogen-containing groups, particularly a hydroxyl group. Accordingly, the polymer may be combined with a compound having at least two hydroxyl groups, i.e. polyhydroxyl compound, to form a curable composition. The curable composition has excellent properties in low temperature curing ability and acid resistance. The polyhydroxyl compound includes polyhydric alcohols, polyester polyols, polyether polyols, polyurethane polyols, polyvinyl alcohols, phenol resins, hydroxyl-containing polybutadine, hydroxyl-containing polychloroprene, ring-opened epoxy resins, polyorganosiloxane polyol and the like. Typical examples of the polyhydric alcohols are 3-allyloxy-1,2-propane diol, 2,2-bis(chloromethyl)-1,3-propane diol, 2-bromo-2-nitro-1,3-propane diol, 3-bromo-1,2-propane diol, butane diol, butyne diol, cyclohexane diol, cyclooctane diol, cyclopentane diol, decalin diol, decane diol, ethylene glycol, propylene glycol, dihydroxyacetophenone, dihydroxyanthraquinone, dihydroxybenzophenone, hydroxybenzyl alcohol, catechol, pentaerythritol, glycerol, amylose, lactose, sucrose, manitol, maltose and the like. The acryl polyol is a polymer of a hydroxyl containing ethylenically unsaturated monomer. Examples of the hydroxyl containing unsaturated monomers are 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 2-hydroxybutyl (meth)acrylate and the like. The acryl polyol may be a copolymer of the above mentioned monomers with other monomers. Examples of the other monomers are methyl (meth)acrylate, ethyl (meth)acrylate, n-butyl (meth)acrylate, isobutyl (meth)acrylate, ethylhexyl (meth)acrylate, alpha-methylstyrene, vinyltoluene, t-butylstyrene, ethylene, propylene, vinyl acetate, vinyl propionate, acrylonitrile, methacrylonitrile, dimethylaminoethyl (meth)acrylate, and the like. Typical examples of the polyester polyols are a condensate of a polyhydric alcohol as mentioned above and a polybasic acid or an anhydride thereof (e.g. phthalic acid, tetrahydrophthalic acid, tetrachlorophthalic acid, hexahydrophthalic acid, succinic acid, maleic acid, fumaric acid, adipic acid, sebacic acid, trimellitic acid, pyromellitic acid etc.); a reaction product of a polyhydric alcohol as mentioned above with an epoxy compound (e.g. n-butyl glycidyl ether, allyl glycidyl ether, Cardura E available from Yuka Shell Company etc.); an alkyd polyol (a product of a polyhydric alcohol and oil (e.g. soybean oil and safflower oil)); a ring open product of ε-caprolantone; and the like. Examples of the polyether polyols are an adduct of a polyhydric alcohol as mentioned above and an alkylene oxide (e.g. ethylene oxide, propylene oxide, tetrahydrofuran etc) and the like. The polyurethane polyol may be prepared by reacting a polyol as mentioned above and a polyisocyanate compound. Examples of the polyisocyanate compounds are ethylene diisocyanate, propylene diisocyanate, tetramethylene diisocyanate, hexamethylene diisocyanate, 1-methyl-2,4-diisocyanatocyclohexane, 1-methyl-2,6-diisocyanatocyclohexane, diisocyanatodimethylxylene, diisocyanatodiethylxylene, lysine diisocyanate, 4,4'-methylenebis(cyclohexylisocyanate), 4,4'-ethylenebis(cyclohexylisocyanate), alpha, alpha'-diisocyanato-1,3-dimethylbenzene, alpha, alpha'-diisocyanato-1,4-dimethylbenzene, isophorone diisocyanate, 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 1,5-naphthylene diisocyanate, 4,4'-methylenebis(phenyleneisocyanate), triphenylmethane triisocyanate and a polymer thereof. The polyol for the polyurethane polyol may be polymeric polyol, such as polyether polyol or polyester polyol. Examples of the phenol resins are novolac or resol type phenol resin, rosin modified phenol resin, alkylphenol resin, butylated resol resin, allyl ether resol resin and the like. The polyorganosiloxane polyol includes a polymer or cyclic compound having both alkylhydroxyalkylsiloxy unit and dialkylsiloxy unit or(and) diphenylsiloxy unit, α,ω-bis(hydroxyalkyl)polydimethylsiloxane and the like. Typical examples of the polyols are The curable composition of the present invention may generally contain a catalyst as mentioned in the synthesis of the polymerizable compound. The catalyst may be present in the composition in an amount of 0.0001 to 10 % by weight, preferably 0.001 to 5 % by weight based on the total amount of the poly(alpha-ketoester) and the polyhydroxyl compound. The curable composition may contain a solvent if necessary. The solvent can be the inert solvent as mentioned above, but alcohols (e.g. ethylene glycol, 2-ethylhexanol, t-butanol, n-hexanol, n-butanol, cyclohexanol, isopropanol, n-propanol, benzyl alcohol, ethanol, methanol etc.) may be employed. The solvent may be present in the composition in an amount of 0.01 to 90 % by weight, preferably 0.5 to 80 % by weight, but alcohols are preferably 50 % by weight or less because they are ester-exchanged with alkoxalyl ester. The curable composition may be cured at a temperature of 70 to 200 °C, preferably 90 to 180 °C for 5 minutes to 2 hours, preferably 10 minutes to one hour. The polymerizable compound and polymer of the present invention have the alpha-ketoester group which can be ester-exchanged with an active hydrogen containing-compound, such as an alcohol or an amine, or can be easily hydrolyzed. The polymer may be suitable for coating, adhesive, plastics, fiber and the like. The polymer may be combined with another active hydrogen containing compound to form a curable composition. The composition is suitable for use in the coating and adhesive fields. The present invention is illustrated by the following Examples. Example 1 A solution of 0.1 mol of 2-hydroxyethyl methacrylate (II) and 150 ml of benzene was mixed with 10.1 g (0.1 mol) of triethylamine, and cooled to 8°C. A solution of 13.65 g (0.1 mol) of ethoxalyl chloride and 100 ml of benzene was added dropwise for 40 minutes. The formed triethylamine hydrochloric salt was filtered at a reduced pressure and rinsed with 50 ml of benzene. The filtrate was condensed under reduced pressure to obtain a liquid which was Kugel-roll distilled. A boiling point of 124°C/53 Pa (0.4 torr) was determined using a Glass Tube Oven available from Shibata Kagaku Co., Ltd. A viscosity of 25°C of 200 cp was determined using a EL type viscometer available from Tokyo Keiki Co., Ltd. Example 2 The procedure of Example 1 was repeated, but using 2-hydroxyethyl acrylate as the compound of formula II. The viscosity of the product was 250 cp. Example 3 The procedure of Example 1 was repeated, but using a compound of the formula CH₂=C(CH₃)-COO-CH₂CH₂-O(CO-(CH₂)₅O)₂H, available as "FM-2" from Daicel Chemical Industries Co., Ltd., as the compound of formula II. The viscosity of the product was 77 cp. Example 4 3 g of p-toluenesulfonic acid and 130 g (1 mol) 2-hydroxyethyl methacrylate were mixed with 438 g (3 mol) diethyl oxalate and reacted at 90°C for 5 hours, while distilling off ethanol. The reaction mixture was cooled and then distilled at reduced pressure, to obtain 2-ethoxalyloxyethyl methacrylate. Example 5 2-Ethoxalyloxyethyl acrylate was obtained, as generally described in Example 4, with the exception that 116 g (1 mol) of 2-hydroxyethyl acrylate was used. Example 6 A 500 ml flask equipped with a decanter, a thermometer, a stirrer and an inlet for nitrogen gas was charged with 65.1 g (0.5 mol) of 2-hydroxyethyl methacrylate and 365.4 g (2.5 mol) of diethyl oxalate, to which 2 g (10 mol) of p-toluenesulfonic acid (catalyst) and 4 g of hydroquinone (polymerisation inhibitor) were added. The mixture was heated, and maintained at 120°C for 4 hours in a nitrogen atmosphere while distilling off 14 ml (0.25 mol) of ethanol. The reaction mixture was evaporated to remove excess diethyl oxalate and then distilled under vacuum, to obtain 88.1 g (yield 76.5%) of 2-ethoxalyloxyethyl methacrylate (colourless transparent liquid) (bp 98°C/40 Pa (0.3 mm Hg)). Example 7 A 500 ml flask equipped with a decanter, a thermometer, a stirrer and an inlet for nitrogen gas was charged with 65.1 g (0.5 mol) of 2-hydroxyethyl methacrylate and 365.4 g (2.5 mol) of diethyl oxalate, to which 2 g (10 mmol) of p-toluenesulfonic acid (catalyst) and 4 g of 2-t-butylhydroquinone (polymerization inhibitor) were added. The mixture was heated to keep about 130 °C for 3 hours in nitrogen atmosphere with distilling 22 ml (0.38 mol) of ethanol away. The reaction mixture was evaporated to remove excess diethyl oxalate and then distilled under vacuum to obtain 64.8 g (yield 76.5 %) of 2-ethoxalyloxyethyl methacrylate (bp 84 - 125 °C/53 Pa (0.4 mmHg)). Example 8 A 500 ml flask equipped with a decanter, a thermometer, a stirrer and an inlet for nitrogen gas was charged with 65.1 g (0.5 mol) of 2-hydroxyethyl methacrylate and 365.4 g (2.5 mol) of diethyl oxalate, to which 2 g (10 mmol) of p-toluenesulfonic acid (catalyst) and 4 g of 2,5-di-t-butylhydroquinone (polymerization inhibitor) were added. The mixture was heated to keep about 130 °C for 3 hours in nitrogen atmosphere with distilling 23.5 ml (0.40 mol) of ethanol away. The reaction mixture was evaporated to remove excess diethyl oxalate and then distilled under vacuum to obtain 64.8 g (yield 52.4 %) of 2-ethoxalyloxyethyl methacrylate (bp 95 - 125 °C/40 Pa (0.3 mmHg)). Example 9 A 500 ml flask equipped with a decanter, a thermometer, a stirrer and an inlet for nitrogen gas was charged with 65.1 g (0.5 mol) of 2-hydroxyethyl methacrylate and 365.4 g (2.5 mol) of diethyl oxalate, to which 2 g (10 mmol) of dibutyltin dilaurate (catalyst) and 4 g of 2,5-di-t-butylhydroquinone (polymerization inhibitor) were added. The mixture was heated to keep about 120 °C for 2 hours in nitrogen atmosphere with distilling 32.5 ml (0.56 mol) of ethanol away. The reaction mixture was evaporated to remove excess diethyl oxalate and then distilled under vacuum to obtain 84.2 g (yield 73.2 %) of 2-ethoxalyloxyethyl methacrylate (bp 124 °C/53 Pa (0.4 mmHg)). Example 10 A 200 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 50 g of butyl acetate and heated to 100 °C. To the content was added dropwise 30.75 g of 2-ethoxalyloxyethyl methacrylate, 35.69 g of methyl methacrylate, 21.92 g of n-butyl acrylate and 1.33 g of azobisisobutyronitrile for 2 hours. After mixing for 30 minutes, 0.88 g of azobisisobutyronitrile and 17.8 g of butyl acetate were added dropwise for 30 minutes. It was mixed with heating for 1.5 hours and cooled to obtain transparent and light yellow polymer (Mn = 14,200, Mw = 37,500, α = 2.63). Example 11 A 200 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 70 g of butyl acetate and 20 g of butanol, and heated to 110 °C. To the content was added dropwise 16.4 g of 2-ethoxalyloxyethyl methacrylate, 50.0 g of methyl methacrylate, 24.3 g of n-butyl acrylate, 9.3 g hydroxyethyl methacrylate and 1.5 g of azobisisobutyronitrile for 3 hours. After mixing for 30 minutes, 0.5 g of azobisisobutylonitrile and 10.0 g of butyl acetate were added dropwise for 30 minutes. It was mixed with heating for 1.5 hours and cooled to obtain transparent and light yellow polymer (Mn = 9,730, Mw = 30,942, α= 3.17). Example 12 A 200 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 42.9 g of xylene and 1 g of Kaya Ester-O (t-butylperoxy-2-ethylhexanoate available from Akzo Chemical Company), and heated to 140 °C. To the content was added dropwise 41.0 g of 2-ethoxalyloxyethyl methacrylate, 40.0 g of methyl methacrylate, 19.0 g of n-butyl acrylate and 4.0 g of azobisisobutyronitrile for 2 hours. After mixing for 30 minutes, 10.0 g of xylene was added dropwise for 30 minutes. It was mixed with heating for 1.5 hours and cooled to obtain transparent and light yellow polymer (Mn = 2,799, Mw = 5,695, α = 2.03). Example 13 A 200 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 27.0 g of butyl acetate and heated to 110 °C. To the content was added dropwise 30.0 g of 2-ethoxalyloxyethyl methacrylate and 0.45 g of azobisisobutyronitrile. After mixing for 30 minutes, 0.15 g of azobisisobutyronitrile and 3.0 g of butyl acetate were added dropwise for 30 minutes. It was mixed with heating for 1.5 hours and cooled to obtain transparent and light yellow polymer (Mn = 8,050, Mw = 17,240, α = 2.14). Example 14 A 100 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 13.1 g of xylene and heated to 120 °C. A mixture of 33.8 g of the product of Example 3, 3.8 g of Kaya Ester-O, 3.8 g of alpha-methylstyrene dimer and 3.8 g of xylene was added dropwise for 3 hours. After mixing for 30 minutes, 0.38 g of Kaya Ester and 3.3 g of xylene were added dropwise for one hour. It was mixed with heating for 1.5 hours and cooled to obtain transparent and light yellow liquid (Viscosity = 253 cp). Example 15 A 100 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 15.0 g of xylene and heated to 130 °C. A mixture of 32.7 g of the product of Example 3, 9.3 g of 2-hydroxyethyl methacrylate, 2.5 g of butanol, 3.1 g of n-butyl methacrylate, 4.5 g of Kaya Ester-O and 5.0 g of alpha-methylstyrene dimer was added dropwise for 3 hours. After mixing for 30 minutes, 0.38 g of Kaya Ester and 3.3 g of xylene were added dropwise for one hour. It was mixed with heating for 1.5 hours and cooled to obtain transparent and light yellow liquid (Viscosity = 99.2 cp, nonvolatile content = 60.4 %). Example 16 A 100 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 15.0 g of xylene and heated to 130 °C. A mixture of 24.5 g of the product of Example 3, 19.2 g of FM-2, 1.35 g of n-butyl methacrylate, 5 g of alpha-methylstyrene dimer, 2.5 g of butanol and 4.5 g of Kaya Ester-O was added dropwise for 3 hours. After mixing for 30 minutes, 0.5 g of Kaya Ester and 5.0 g of xylene were added dropwise for one hour. It was mixed with heating for 1.5 hours and cooled to obtain transparent and light yellow liquid (Viscosity = 74.4 cp, nonvolatile content = 63.4 %). Examples 17 to 22 A 200 ml of flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 21.8 g of xylene and heated to 135 °C. To the content, 62.5 g of a monomer mixture shown in Table 2, 6.3 g of Kaya Ester-O and 6.3 g of xylene were added dropwise for 3 hours. After mixing for 30 minutes, 0.63 g of Kaya Ester and 5.0 g of xylene were added dropwise for one hour. It was mixed with heating for 1.5 hours and heated to remove 15 g of xylene. It was then cooled to obtain transparent and light yellow liquid. The liquid had physical properties as shown in Table 2. Example No. Momomer mixture Nonvolatile content Viscosity (cps) 17 EOMA /MSD =90/10 79 1229 18 EOFM-2 /MSD=90/10 80 211 19 EOMA/MMA /MSD=55.4/34.6/10 78 410 20 EOMA/MMA/MSD=85/5/10 76 4429 21 EOMA/ST /MSD=46.3/43.7/10 81 5760 22 EOMA/EHA /MSD=73.8/16.2/10 76 550 Production Example 1 Acryl polyol A one liter flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 180.0 g of butyl acetate and heated to 120 °C. A mixture of 142.7 g of methyl methacrylate, 87.7 g of n-butyl acrylate, 69.6 g of 2-hydroxyethyl methacrylate and 4.5 g (1.5 wt % / monomers) of azobisisobutyronitrile was added dropwise for 3 hours. After mixing for 30 minutes, 1.5 g (0.5 wt % / monomers) of azobisisobutyronitrile and 30.0 g of butyl acetate were added dropwise for 30 minutes. It was mixed with heating for 1.5 hours and cooled to obtain transparent and light yellow polymer (Mn = 8,870, Mw = 20,600, OH value = 100, α = 2.31). Production Example 2 Acryl polyol A 200 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 21.8 g of xylene and heated to 135 °C. To the content, 62.5 g of a monomer mixture (FM-2/styrene/isobutyl methacrylate/alpha-methylstyrene dimer = 55.2/10.2/27.4/10.2), 6.3 g of Kaya Ester-O and 6.3 g of xylene were added dropwise for 3 hours. After mixing for 30 minutes, 0.63 g of Kaya Ester-O and 5.0 g of xylene were added dropwise for one hour. After mixing with heating for 1.5 hours, it was heated to remove 15 g of xylene. The obtained solution was cooled to room temperature to obtain transparent and light yellow polymer. The polymer solution has a viscosity of 326 (E type viscometer at 25 °C) and a nonvolatile content of 70 % (130 °C, 30 minutes). Example 23 One of the products (curing agent) prepared in Examples 17 to 22 and the acryl polyol of Production Example 2 were mixed with 1 wt % / solid content of dibutyltin dilaurate. The resultant composition was coated on a tin plate by a bar coater No. 40, and then baked at 130 or 150 °C for 30 minutes. Curing properties were evaluated and the results were shown in Table 3. Curing agent (weight) Amount of the polyol Acetone rubbing test 130 °C 150 °C Ex.17 (1.49g) 4.04 g 11 19 Ex.18 (2.26g) 3.00 g 9 1 Ex.19 (2.02g) 3.43 g 10 16 Ex.20 (1.44g) 3.76 g 7 9 Ex.21 (2.22g) 3.15 g 10 15 Ex.22 (1.71g) 3.81 g 9 10 Example 24 A catalyst was mixed with 8.51 g of the 2-ethoxalyloxy methacrylate copolymer prepared in Example 21 and 6.49 g of the acryl polyol of Production Example 1 in an amount ratio of catalyst/resin solid content of 1 wt % to form a resin composition. The catalyst was selected from dibutyltin dilaurate (DBTL), diazabicyclooctane (DABCO) and p-toluenesulfonic acid monohydrate (PTS). Also, another resin composition which did not contain any catalyst was prepared. The resin composition was coated on a tin plate by a bar coater to a thickness of 20 µm, and then baked at 110, 130, 150 or 180 °C for 30 minutes. Curing properties were evaluated and the results were shown in Table 4. Curing temp. Number Catalyst Acetone rubbing Gellation % Pencil hardness 110 °C 1 Nothing - - 2 1 DBTL 5 85.8 H 2 81.8 H 1 DABCO 5 64.6 H 2 69.8 H 1 PTS - - 2 130 °C 1 Nothing - - 2 1 DBTL 16 95.1 H 2 96.6 H 1 DABCO 5 84.4 H 2 83.2 H 1 PTS - - 2 150 °C 1 Nothing 5 3.8 2H 2 2.2 2H 1 DBTL 50 99.5 2H 2 99.6 2H 1 DABCO 34 89.1 2H 2 87.3 2H 1 PTS 13 19.3 2H 2 19.3 2H 180 °C 1 Nothing 6 5.8 2H 2 5.1 2H 1 DBTL 50 or more 99.7 2H 2 99.6 2H 1 DABCO 50 or more 89.8 2H 2 89.4 2H 1 PTS 10 76.6 2H 2 77.0 2H Examples 25 to 27 A 200 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with xylene and n-butanol in an amount shown in the initial charge column of Table 5 and heated to a polymerization temperature. To the content, a monomer mixture shown in Table 5 and Kaya Ester-O were were added dropwise for 3 hours. After mixing for 5 hours, Kaya Ester-O and xylene were added dropwise in amounts shown in the after shot column of Table 5 for one hour. After mixing for 1.5 hours with heating, it was cooled to room temperature. The obtained polymer solution was transparent and light yellow. Its molecular weight, nonvolatile content and viscosity are shown in Table 6. Example 28 Each of the resins of Examples 25 to 27 was mixed with an amount of 1 wt % / resin solid content of dibutyltin dilaurate to form a resin composition. The resultant composition was coated on a tin plate by a bar coater No. 40, and then baked at 130 or 150 °C for 30 minutes. Curing properties were evaluated and the results were shown in Table 7. Resin No. Acetone rubbing test Pencil hardness 130 °C 150 °C 130 °C 150 °C Ex.25 25 38 2B HB Ex.26 38 50 or more HB HB Ex.27 28 40 HB HB Example 29 A 200 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 40 g of xylene and heated to 120 °C. To the content, 200 g of a monomer mixture (FM-2/2-ethoxalyloxyethyl methacrylate/isobutyl methacrylate/alpha-methylstyrene dimer = 51/32.8/10/6.2) and 9 g of Kaya Ester-O were added dropwise for 3 hours. After mixing for 30 minutes, 1 g of Kaya Ester-O and 10 g of xylene were added dropwise for one hour. After mixing with heating for 1.5 hours, it was heated to remove 30 g of xylene. The obtained solution was cooled to room temperature to obtain transparent and light yellow polymer. The polymer solution had a viscosity of 416 cps (E type viscometer at 25 °C) and a nonvolatile content of 70 % (130 °C, 30 minutes). Example 30 The resin of Example 29 was mixed with an amount of 1 wt % / resin solid content of a catalyst shown in Table 8. The resultant composition was coated on a tin plate by a bar coater No. 40, and then baked at 130 or 150 °C for 30 minutes. Curing properties were evaluated and the results were shown in Table 8. Number Catalyst Acetone rubbing test 130 °C 150 °C 1 Dibutyltin dilaurate 23 42 2 Dibutyltin dichloride 12 38 3 (CH₃)SnI₂/(C₆H₅)₄SbI 0 38 4 (CH₃)SnI₂/(MoN)₃PO 7 38 5 H₂SO₄ 40 50 or more 6 BF₃(Et20) 3 50 or more 7 1,8-Diazabicyclo[5,4,0]undecene 19 38 8 1,4-Diazabicyclo[2,2,2]octane 2 30 9 FeCl₃ 8 50 10 Al(i-PrO)₃ 10 15 11 Ti(i-PrO)₄ 4 5 12 Diacetyltetrabutyl stannoic acid 25 40 Example 31 A mixture was prepared by dissolving 52.1 g (0.4 mol) of hydroxyethyl methacrylate and 40.5 g (0.4 mol) of triethylamine in 250 ml of benzene and cooled to 2 °C. To the content, a solution of 65.8 g (0.4 mol) of t-butoxalyl chloride in 200 ml of benzene was added dropwise for 3 hours while precipitating salt. After the completion of dropping, it was allowed to stand for 30 minutes without cooling to terminate reaction. The precipitated salt was filtered off and the filtrate was evaporated to obtain 99.9 g (yield 91 %) of yellow liquid which was identified by IR and ¹H-NMR to find t-butoxalyloxylethyl methacrylate. IR (cm⁻¹, neat) 2950 (C-H), 1760 - 1720 (C=O), 1640 (C=O) ¹H-NMR (ppm, in CDCl₃, TMS Standard) e; 1.56 (s,9H), c; 1.95 (s,3H), d; 4.46 (m,4H), a or b; 5.60 (s,1H), a or b; 6.14 (s,1H) Example 32 A 500 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 90 g of xylene and heated to 100 °C. To the content, 39.0 g of t-butoxalyloxyethyl methacrylate of Example 31, 26.2 g of n-butyl acrylate, 34.8 g of methyl methacrylate and 2.0 g of azobisisobutyronitrile were added dropwise for 3 hours. After mixing for 30 minutes, 0.2 g of azobisisobutyronitrile and 10 g of xylene were added dropwise for one hour. After mixing with heating for 1.5 hours, the obtained solution was cooled to room temperature to obtain transparent and light yellow polymer. The polymer solution had a viscosity of 243 cps °C (E type viscometer at 25 °C) and a nonvolatile content of 50 % (130 °C, one hour), and had Mn = 6,790, Mw = 13,300, α =1.96. Example 33 As generally described in Example 31, the reaction was conducted with the exception that 46.4 g (0.4 mol) of 2-hydroxyethyl acrylate was employed instead of 2-hydroxyethyl methacrylate, to obtain 96.6 g (yield 98.8 %) of t-butoxalyloxyethyl acrylate which was identified by IR and NMR. IR (cm⁻¹, neat) 2950 (C-H), 1760 - 1720 (C=O), 1620 (C=C), 1140 (C-O) ¹H-NMR (ppm, in CDCl₃, TMS Standard) e; 1.54 (s,9H), d; 4.43 - 4.50 (m,4H), a or b; 5.88 - 5.90 (d,1H), c; 6.11 - 6.19 (d-d,1H), a or b; 6.42 - 6.47 (d,1H) ¹³C-NMR (ppm, in CDCl₃) 9; 27.51, 4 or 5; 61.42, 4 or 5; 63.85, 8; 84.90, 1; 128.1, 2; 131.43, 6 or 7; 156.38, 6 or 7; 158.17, 3; 165.51. Example 34 A 200 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 45 g of xylene and heated to 100 °C. To the content, 36.6 g of t-butoxalyloxyethyl acrylate of Example 33, 7.7 g of n-butyl acrylate, 5.7 g of methyl methacrylate and 1.0 g of azobisisobutyronitrile were added dropwise for 3 hours. After mixing for 30 minutes, 0.1 g of azobisisobutyronitrile and 5 g of xylene were added dropwise for 30 minutes. After mixing with heating for 1.5 hours, the obtained solution was cooled to room temperature to obtain transparent and light yellow polymer. The polymer solution had a viscosity of 83 cps (E type viscometer at 25 °C) and a nonvolatile content of 49 % (130 °C, one hour), and had Mn = 4,800, Mw = 10,090, α =2.10. Example 35 A three liter flask was charged with 253.86 g (2.0 mol) of oxalyl chloride and 1200 ml of benzene and cooled with stirring. A solution of 120.2 g (2.0 mol) of isopropyl alcohol, 212.5 g (2.0 mol) of triethylamine and 400 ml of benzene was added dropwise for 3 hours. After the completion of dropping, mixing was continued at 20 °C for 2 hours. The solution became blown and precipitated crystal. After adding 600 ml of hexane to the reaction mixture, the precipitated solid was filtered off and the filtrate was condensed. It was then distilled under vacuum to obtain 74.4 g (yield 17.7 %) of isopropoxalyl chloride. (bp 100 - 105 °C/20 kPa (150 mmHg)) ¹H-NMR (ppm) 1.38 (d,6H), 5.20 (m,1H) Next, a 500 ml reaction vessel was charged with 25 g (0.17 mol) of the obtained isopropoxalyl chloride and 150 ml of benzene and cooled to 5 °C with ice. A mixture of 27.9 g (0.214 mol) of 2-hydroxyethyl methacrylate and 24.1 g (0.238 mol) of triethylamine was added dropwise for 1.5 hours with mixing while precipitating white solid. Mixing was continued at 5 °C for 1.5 hours and filtered . The filtrate was condensed and then distilled under vacuum to obtain 17.6 g (yield 43.3 %) of isopropoxalyloxyethyl methacrylate of bp. 112 °C/40 Pa (0.3 mm Hg). IR (cm⁻¹, neat) 3500, 2980, 1760, 1740, 1720, 1635, 1095, 680 ¹H-NMR (ppm, in CDCl₃, TMS Standard) 1.33 (d,6H), 1.92 (s,3H), 4.41 (m,2H), 4.52 (m,2H), 5.17 (m,1H), 5.60 (s,1H), 6.12 (s,1H) Example 36 A 200 ml flask equipped with a decanter, a condenser, a stirrer and a dropping funnel was charged with 50 ml of xylene and heated to 110 °C. To the content, 52.2 g of isopropoxalyloxyethyl methacrylate, 27.8 g of cyclohexyl methacrylate, 10.0 g of styrene, 10.0 g of alpha-methylstyrene dimer and 10.0 g of t-butylperoxy-2-ethyl hexanate were added dropwise for 3 hours. After mixing at 110 °C for 30 minutes, 1.0 g of t-butylperoxy-2-ethyl hexanate and 6.0 g of xylene were added dropwise for 30 minutes. It was then mixed at 110 °C for 1.5 hours to obtain a copolymer having a nonvolatile content of 58.6 % (130 °C, 60 minutes), and had Mn = 1,870, Mw = 3,240, α = 1.73.

Claims: A polymerisable compound of formula I CH₂=CR₂-CO-(-Y-CH₂-CHR₃-) n -[-O-CO-(CH₂) m -] l -X-CO-COOR₁ (I) wherein R₂ and R₃ are independently selected from H and C₁₋₅ alkyl; Y is -O- or -NR₄-, R₄ being H or C₁₋₅ alkyl; n is an integer of 1 to 5; m is an integer of 1 to 10; l is 0 or an integer of 1 to 20; R₁ is H, C₁₋₅ alkyl or aryl; and X is -O-, -S- or -COO-. A compound as claimed in claim 1, wherein l is zero. A compound as claimed in claim 2, wherein X is -O- and R₁ is ethyl. A process for preparing a compound according to any preceding claim, comprising reacting a corresponding active hydrogen-containing compound of the formula CH₂=CR₂-CO-(-Y-CH₂-CHR₃-) n -[-O-CO-(CH₂) m -] l -XH with a corresponding ester of the formula Z-CO-COOR₁ wherein Z is halogen or OR₁.

Inventors: AOKI KEI, MORI HIROHIKO, TOMITA NOBUAKI, URANO SATOSHI, AOKI, KEI, MORI, HIROHIKO, TOMITA, NOBUAKI, URANO, SATOSHI
Applicants: NIPPON PAINT CO LTD, NIPPON PAINT CO., LTD.
Application year: 1990
Main classification: C07C69
IPC codes: C08G63, C08F299, C07C69, C08F290, C08G81, C07C233, C08F20, C08G83, C07C327, C08L83, C08L33, C08F18, C09D133, C08F26, C08F28