A semiconductor laser device and a method for the production of the same

Abstract: A semiconductor laser device is disclosed which emits laser light from an end facet. The semiconductor laser device comprises a multi-layered structure (12) formed on a semiconductor substrate (11), the multi-layered structure (12) having an active layer (16) for laser oscillation, and a pair of cleavage planes (101) on the side of the multi-layered structure (12), wherein a graded-band-gap layer (18) is formed on at least one of the cleavage planes (101), the graded-band-gap layer (18) having a forbidden band gap which increases gradually with an increase in the distance from the cleavage plane (101) and the surface of the graded-band-gap layer (18) constituting the end facet.

Description: 1. Field of the invention: This invention relates to a semiconductor laser device which emits laser light from an end facet thereof and it also relates to a method for the production of such a semiconductor laser device. 2. Description of the prior art: In recent years, semiconductor laser devices have widely come into practical use as light sources for optical disc driving units. When semiconductor laser devices are used as the light source for write-once optical disc driving units or rewritable optical disc driving units, they are required to have high reliability even at a high output power level of from 40 to 50 mW. When used as the light source for optical pumping of solid-state laser devices such as a YAG laser, an output power of 100 mW or more is required. However, it has been reported that the reliability of the semiconductor laser devices in practical use today, which can attain laser oscillation at a relatively high output power level, is inversely proportional to the optical output power raised to the fourth power, when the devices of the same construction are compared. In other words, it is extremely difficult to raise the optical output power, while maintaining high reliability. The principal cause for deterioration of semiconductor laser devices in high output power operation is facet deterioration. This is because heat is generated locally at the light-emitting facet due to the high optical density at this facet. The mechanism of this heat generation will be explained by reference to Figures 5a-5b and 6a-6b. Figures 5a and 5b are schematic diagrams showing the energy band structures near the surface originating from the surface state which occurs when either the n-type or p-type GaAs (110)-surface is slightly oxidized. In the case of either n-type or p-type GaAs, numerous carriers accumulate near the surface to form a so-called "accumulation layer" which is indicated by reference numeral 1 in these figures. In general, it is well known that the surface state will bend the energy bands near the surface. In addition to the accumulation layer 1 shown in Figures 5a and 5b, minority carriers may gather near the surface and majority carriers be distanced from the surface as shown in Figures 6a and 6b, resulting in the formation of an inversion layer 2 which is a local inversion of the conductivity type. Whether an accumulation layer 1, or an inversion layer 2 forms, is dependent on the height relationship between the surface state E s and the Fermi level E f of the semiconductor. In either case of n-type or p-type GaAs, an accumulation layer 1 will form. The electrons and positive holes trapped in the surface state E s are released after a short relaxation time, and this energy is released as heat. Electrons and positive holes are then again trapped in the surface state which has become a vacant state, and the above process is repeated, so that heat continues to be released. While the above process is being repeated, the heat released from the surface state concentrates at the end facets of the semiconductor, and this heat narrows the forbidden band gap in the energy bands. Furthermore, the absorption of light increases the minority carriers, and heat generation further increases by way of the surface state. This process raises the temperature of the semiconductor surface, which may reach the melting point of the semiconductor, resulting in facet breakdown. In the case of GaAs, an accumulation layer forms, while in the case of other materials such as AlGaAs, an inversion layer may form. In the latter case, majority carriers are trapped in the surface state, and facet breakdown occurs by the same process as that by an accumulation layer. In the case of semiconductor laser devices used under a high injection condition, heat generation originating with the surface state becomes a more serious problem. Applied Physics Letters, Vol 40, No. 5, 1.March 1982, pp372-374, on which the preamble of claim 1 is based, discloses a semiconductor laser device which emits laser light from an end facet, comprising a multi-layered structure formed on a semiconductor substrate, the multi-layered structure having an active layer for laser oscillation and a pair of cleavage planes formed on the side of the multi-layered structure. The end facet of the semiconductor laser device disclosed in Applied Physics Letters, vol 40, No. 5, 1 March 1982, pp372-374, is formed by one of the cleavage planes. As a result, the laser is liable to overheat in use, as described above. Applied Physics Letters, vol 40, No. 5, 1 March 1982, pp372-374, also discloses a method of producing the above semiconductor laser device. The preamble of claim 7 is based on this disclosure. As a method for preventing the effect of surface recombination, there has been proposed a method in which a region having a graded band gap is formed near the surface. For example, a solar cell having a graded-band-gap layer formed by liquid phase epitaxy is disclosed by M.Konagai and K.Takahshi, J. Appl. Phys. Vol. 46 No. 8 pp3542-3546 August (1975). Figure 7 shows a schematic energy band diagram of a graded-band-gap heterojunction solar cell described in the above-identified prior art reference. As can be seen from this figure, among carriers generated by the absorption of light, electrons are drawn strongly into the inside of semiconductor crystals due to the drift caused by the grading of the energy gap, as well as the migration usually caused by the diffusion. This results in a reduced probability that these electrons will be trapped in the surface state, and therefore, surface recombination can be effectively suppressed. In the case of solar cells, because the crystal surface functions as a light-receiving facet, a graded-band-gap layer can be formed by liquid phase epitaxy during the crystal growth, thereby attaining the effective suppression of surface recombination. However, in the case of semiconductor laser devices, a light-emitting facet, which may be adversely affected by surface recombination, is usually formed by a cleavage of semiconductor crystals. Therefore, it is extremely difficult to form a graded-band-gap layer in advance on the cleavage plane by liquid phase epitaxy. For this reason, conventional semiconductor laser devices have a serious problem of causing facet breakdown due to surface recombination at the light-emitting facet. Furthermore, the solar cell disclosed in J. Appl. Phys. Vol. 46 No. 8, pp3542-3546 August (1975) operates at power outputs of around 0. 3mW. In contrast, semiconductor laser devices operate at much greater output powers such as, for example, 400mW. SUMMARY OF THE INVENTION According to a first aspect of the present invention there is provided a semiconductor laser device, comprising a multi-layered structure formed on a semiconductor substrate, the multi-layered structure having an active layer for laser oscillation, and a pair of cleavage planes on the side of the multi-layered structure, the laser device being characterised in that a graded-band-gap layer is formed on at least one of the cleavage planes, the graded-band-gap layer having a forbidden band gap which increases gradually with an increase in distance from the cleavage plane, and the surface of the graded-band-gap layer constituting an end facet of the device. In a preferred embodiment, the active layer is made of Ga 1-x Al x As (0 ≦ x ≦ 1) and the graded-band-gap layer is made of Ga 1-y Al y As. In a more preferred embodiment, the Al mole fraction y of the graded-band-gap layer increases from the cleavage plane to the end facet in accordance with a linear or parabolic distribution. In another more preferred embodiment, the above-mentioned Al mole fraction y at the cleavage plane between the active layer and the graded-band-gap layer is equal to the Al mole fraction x. In still another more preferred embodiment, the above-mentioned Al mole fraction y at the cleavage plane between the active layer and the graded-band-gap layer is greater than the A1 mole fraction x. In still another more preferred embodiment, the above-mentioned A1 mole fraction y at the cleavage plane between the active layer and the graded-band-gap layer is smaller than the A1 mole fraction x. According to a second aspect of this invention there is provided a method for the production of a semiconductor laser device as mentioned above, comprising forming a multi-layered structure on a semiconductor substrate, the multi-layered structure having an active layer for laser oscillation; cleaving the substrate together with the multi-layered structure to form a laser cavity between cleavage planes; the method being characterised in that it further comprises the step of forming a graded-band-gap layer on at least one of the cleavage planes, the graded-band-gap layer having a forbidden band gap which increases gradually with an increase in distance from the cleavage plane. In a preferred embodiment, the graded-band-gap layer is grown by vapor phase epitaxy. Thus, the invention described herein makes possible the objectives of (1) providing a semiconductor laser device with a construction capable of suppressing the surface state in the vicinity of the light-emitting facet so that facet breakdown does not occur easily even in high output power conditions; (2) providing a semiconductor laser device in which a graded-band-gap layer is formed on the cleavage plane, and therefore, electrons generated near the end facet are rapidly separated from the end facet, so that facet breakdown due to surface recombination can be effectively suppressed, thereby attaining the improved output power with high reliability; and (3) providing a method for the production of such a semiconductor laser device with excellent characteristics. BRIEF DESCRIPTION OF THE DRAWINGS This invention may be better understood and its numerous objects and advantages will become apparent to those skilled in the art by reference to the accompanying drawings as follows: Figure 1 is a perspective view showing the front facet area of a semiconductor laser device of this invention. Figures 2a-2c are perspective views showing the production of the semiconductor laser device of Figure 1. Figures 3a-3c are diagrams showing various distributions of an Al mole fraction in the graded-band-gap layer and the active layer of semiconductor laser devices of this invention. Figure 4 is a graph showing the injected current-optical output characteristics of the semiconductor laser device of this invention wherein the graded-band-gap layer has an Al mole fraction as shown in Figure 3a. Figures 5a and 5b are schematic energy band diagrams showing the formation of a carrier accumulation layer in the surface area of n-type and p-type GaAs, respectively. Figures 6a and 6b are schematic energy band diagrams showing the formation of an inversion layer in the surface area of n-type and p-type semiconductors, respectively. Figure 7 is a schematic energy band diagram of a conventional solar cell with a heterojunction composed of p-type graded-band-gap Ga 1-z Al z As and n-type GaAs. DESCRIPTION OF THE PREFERRED EMBODIMENTS The semiconductor laser device of this invention has the same structure as that of a conventional semiconductor laser device which emits laser light from an end facet thereof, except that a graded-band-gap layer is formed on at least one of the cleavage planes. The graded-band-gap layer has a forbidden band gap which increases gradually with an increase in the distance from the cleavage plane. The surface of the graded-band-gap layer constitutes the end facet of the device. Figure 1 is a perspective view showing the front facet area of a semiconductor laser device of this invention. The production process of this semiconductor laser device is explained below. First, as shown in Figure 2a, a multi-layered structure 12 including an active layer 16 for laser oscillation is grown on a semiconductor substrate 11. The active layer 16 is made of, for example, Ga 1-x Al x As (0 ≦ x ≦ 1). The method for the growth of the multi-layered structure 12 including the active layer 16 can be any one of the conventional processes such as liquid phase epitaxy and vapor phase epitaxy. Next, the wafer thus obtained is cleaved by a known cleavage method so as to obtain the prescribed cavity length, resulting in a plurality of bars 15 as shown in Figure 2b. Each of the bars 15 has a plurality of cavity units arranged in the direction perpendicular to the cavity direction. After cleaving, on the planes of the bar 15 other than the cleavage planes 101, as SiO₂ film 20 is formed by plasma chemical vapor deposition or other similar processes as shown in Figure 2c. Then, on at least one of the cleavage planes 101, a graded-band-gap layer 18 is formed by molecular beam epitaxy or metal organic chemical vapor deposition. When the active layer 16 is made of Ga 1-x Al x As (0 ≦ x ≦ 1), the graded-band-gap layer 18 is also made of Ga 1-y Al y As in which the Al mole fraction y increases gradually from the Al mole fraction x of the active layer 16 to the prescribed final value at the end facet. In this case, the GaAlAs layer grown on the SiO₂ film 20 is made of polycrystallines, and such a polycrystalline GaAlAs layer can readily be removed by an etching technique after growth. Accordingly, the graded-band-gap layer 18 can be formed only on the cleavage plane which corresponds to the light-emitting facet of the laser cavity. Thereafter, the SiO₂ film 20 is removed, and ohmic electrodes 13 and 14 were formed on the upper face of the multi-layered structure 12 and the back face of the semiconductor substrate 11, respectively. The method for the formation of the ohmic electrodes 13 and 14 can be any one of the conventional processes. Alternatively, after the multi-layered structure 12 including the active layer 16 is formed on the semiconductor substrate 11, an SiO₂ film may be formed on the upper face of the multi-layered structure 12 and the back face of the semiconductor substrate 11, followed by cleavage of the wafer thus obtained. In this case, the cleavage of the wafer can immediately provide a bar 15 as shown in Figure 2c. As a practical example, a semiconductor laser device was produced with the above-mentioned constitution, in which the Al mole fraction x of the active layer 16 was set to 0.14 and the Al mole fraction y of the graded-band-gap layer 18 was varied as shown in Figure 3a. The thickness of the graded-band-gap layer 18 was 0.1 µm. The semiconductor laser device thus obtained was then provided with coatings on both end facets such that the reflectivity of the light-emitting facet became 4% and the reflectivity of the other facet 95%. For comparison, a conventional semiconductor laser device was produced in the same way as mentioned above, except that no graded-band-gap layer was formed on the cleavage planes. Figure 4 is a graph showing the injected current-optical output characteristics of the semiconductor laser device of this example obtained above (curve A) and the conventional semiconductor laser device obtained above (curve B). As can be seen from this figure, in the conventional semiconductor laser device, deterioration of the device characteristics occurs due to facet breakdown at an optical output power of approximately 200 mW, whereas the semiconductor laser device of this example can attain stable laser oscillation even at an optical output power of up to about 600 mW without causing facet breakdown. Although in the above example, the Al mole fraction y of the graded-band-gap layer was varied in accordance with the linear distribution as shown in Figure 3a, it may also be varied in accordance with the parabolic distribution. Moreover, the Al mole fraction y is not limited to the final value of 0.5 as shown in Figure 3a, but it can takes any final value so long as it increases gradually with an increase in the distance from the cleavage plane. Furthermore, as shown in Figure 3b, there may exist a step of the Al mole fraction at the cleavage plane between the active layer and the graded-band-gap layer, that is, the Al mole fraction y of the graded-band-gap layer at the cleavage plane may be greater than the Al mole fraction x of the active layer. Alternatively, as shown in Figure 3c, there may exist a barrier against electrons at the cleavage plane, that is, the Al mole fraction y of the graded-band-gap layer at the cleavage plane may be smaller than the Al mole fraction x of the active layer. In any case, excellent device characteristics as mentioned above could be obtained by the formation of such a graded-band-gap layer on the cleavage plane. In general, besides the carriers generated by the absorption of light, semiconductor laser devices contain additional carriers injected in the active layer from the outside. Therefore, the active layer has a high density of carriers. In the semiconductor laser device of this invention, carriers present in the vicinity of the light-emitting facet can be rapidly separated from the end facet due to the drift as well as the diffusion, resulting in an extremely small probability that these electrons contribute to heat generation via the surface state. Therefore, deterioration of the end facets can be effectively suppressed and the semiconductor laser device of this invention can attain stable laser oscillation at high output power for a long period of time. It is understood that various other modifications will be apparent to and can be readily made by those skilled in the art without departing from the scope of this invention. Accordingly, it is not intended that the scope of the claims appended hereto be limited to the description as set forth herein, but rather that the claims be construed as en compassing all the features of patentable novelty that reside in the present invention, including all features that would be treated as equivalents thereof by those skilled in the art to which this invention pertains.

Claims: A semiconductor laser device which emits laser light from an end facet, comprising a multi-layered structure (12) formed on a semiconductor substrate (11), said multi-layered structure (12) having an active layer (16) for laser oscillation, and a pair of cleavage planes (101) on the side of the multi-layered structure (12), the laser device being characterised in that a graded-band-gap layer is formed on at least one of said cleavage planes (101), said graded-band-gap layer (18) having a forbidden band gap which increases gradually with an increase in distance from said cleavage plane (101), and the surface of said graded-band-gap layer (18) constituting said end facet. A semiconductor laser device according to claim 1, wherein said active layer (16) is made of Ga 1-x Al x As (0≦x≦1) and said graded-band-gap layer (18) is made of Ga 1-y Al y As. A semiconductor laser device according to claim 2, wherein the Al mole fraction y of said graded-band-gap layer (18) increases from the cleavage plane (101) to the end facet in accordance with a linear or parabolic distribution. A semiconductor laser device according to claim 3, wherein the Al mole fraction y at the cleavage plane between the active layer (16) and the graded-band-gap layer (18) is equal to the Al mole fraction x. A semiconductor laser device according to claim 3, wherein the Al mole fraction y at the cleavage plane between the active layer (16) and the graded-band-gap layer (18) is greater than the Al mole fraction x. A semiconductor laser device according to claim 3, wherein the Al mole fraction y at the cleavage plane between the active layer (16) and the graded-band-gap layer (18) is smaller than the Al mole fraction x. A method for the production of a semiconductor laser device of any preceding claim, comprising forming a multi-layered structure (12) on a semiconductor substrate (11), said multi-layered structure (12) having an active layer (16) for laser oscillation; and cleaving the substrate (11) together with the multi-layered structure (12) to form a laser cavity between cleavage planes (101); said method being characterised in that it further comprises the step of forming a graded-band-gap layer (18) on at least one of said cleavage planes (101), said graded-band-gap layer (18) having a forbidden band gap which increases gradually with an increase in distance away from said cleavage plane (101). A method according to claim 7, wherein said graded-band-gap layer (18) is grown by vapor phase epitaxy.

Inventors: HAYASHI HIROSHI, KANEIWA SHINJI, KAWANISHI HIDENORI, MIYAUCHI NOBUYUKI, MORIMOTO TAIJI, YANO SEIKI, HAYASHI, HIROSHI, KANEIWA, SHINJI, KAWANISHI, HIDENORI, MIYAUCHI, NOBUYUKI, MORIMOTO, TAIJI, YANO, SEIKI
Applicants: SHARP KK, SHARP KABUSHIKI KAISHA
Application year: 1990
Main classification: H01S3
IPC codes: H01S5