Process for optical fiber drawing

Abstract: The invention relates to a drawing process for producing an optical fiber (11) which comprises drawing the optical fiber (11) from a preform (1) therefor under tension to form the optical fiber while heating and melting the preform (1), wherein an outer diameter of the optical fiber (11) on which no coating has been provided is measured at a position (3) at which shrinkage of the outer diameter of the optical fiber (11), while stretched, is not larger than 0,5 % and drawing conditions are controlled with a deviation of a measured diameter from a preselected outer diameter.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a process for optical fiber drawing. Description of the Related Art In a conventional drawing process for producing an optical fiber, the optical fiber is produced by heating and melting a preform for the optical fiber in a drawing furnace and drawing the fiber from the preform at a certain rate by a winding up device. The optical fiber which has just left the furnace and is remaining intact, that is, a so-called "bare fiber", tends to be considerably damaged and influenced by moisture. Therefore, the bare fiber is usually coated with an ultraviolet curable resin or a thermosetting resin in a resin coating device comprising, for example, a die, the resin is subsequently cured in a resin curing device, and then the fiber is wound as a coated optical fiber. The diameter of the bare fiber is measured by a measuring device before the coating step, on the basis of which conditions during drawing are controlled so that the outer diameter of the fiber is a desired one. The position at which the diameter measuring device is disposed has not been thought to be critical, and the device is usually located immediately below the drawing furnace as shown in Japanese Patent Kokai Publication No. 295260/1986. If there is anything to limit the position of the measuring device, it has been that the measuring device should not be directly subjected to a strong radiation light from a lower portion of the furnace to avoid being heated to a remarkably high temperature. In addition, it has been thought that the measuring device is better located near the furnace in order to shorten the time lag for correction and to increase a control gain when fluctuation in the diameter of the optical fiber has to be suppressed by controlling a drawing rate depending on an output signal from the measuring device. Thus, in the conventional production of an optical fiber, the distance between the outer diameter measured device and the coating die is usually longer than that between the drawing furnace and the outer diameter measuring device, or a forced cooling device is disposed between the measuring device and the coating die in order to achieve a better resin coating. In the conventional drawing process for producing the optical fiber, the drawing rate of the optical fiber was in the order of 100 m/min. Recently, the drawing rate has been remarkably increased and it is reported that, in an experimental scale, a rate of 1000 m/min. has been realized. However, when such a high drawing rate is employed in the conventional process in which the measuring device is located immediately below the furnace, it has been found that the outer diameter of the finished optical fiber is extremely smaller than the diameter which is measured with the measuring device. As requirements for accuracy of an absolute diameter of the optical fiber and permitted tolerances in the diameter become stricter because of the need for a better connection between fibers, development of a process which improves the accuracy of the outer diameter of the optical fiber is highly desired. For example, the accuracy of the diameter of a quartz base optical fiber is usually required to be in the range 125 µm ± 1 µm. Taking into account the accuracy of the measuring device itself and the fluctuation In the diameter of the optical fiber that can occur during the production, a deviation of the measured diameter as determined by the measuring device from the true diameter of the finished fiber should be not larger than 0.5 % of the outer diameter of the finished fiber. Thus, it is desirable to develop a process which can achieve a deviation of 0.5 % or less. SUMMARY OF THE INVENTION It is an object of the present invention to provide a drawing process for producing an optical fiber in which an improved accuracy of an absolute value of an optical fiber diameter is ensured and, especially, a drawing process In which any deviation of the measured outer diameter of the fiber with a diameter measuring device from the true diameter of the finished optical fiber is smaller than that as obtained in the conventional process. It is found that when the optical fiber is drawn with controlling conditions on the basis of an output signal from the measuring device for the outer diameter of the optical fiber, the position of the measuring device considerably affects the diameter of the finished optical fiber, and suitable control of the position minimizes the deviation though such positioning has not been noted in high speed drawing. The present invention is as defined in the accompanying Claim 1. As used herein, the term "shrinkage" is as defined in the accompanying Claim 1. In one preferred embodiment of the present invention, the temperature of the optical fiber at the measuring position for the outer diameter is lower than the glass softening point of the material of the optical fiber. In another preferred embodiment of the present invention, the drawing is carried out by controlling the outer diameter of the optical fiber by varying the drawing rate depending upon the deviation defined in Claim 1. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 schematically shows one embodiment of the present invention, Fig. 2 schematically shows another embodiment of the present invention, in which a deviation of an output signal from an outer diameter measuring device from a desired value for said outer diameter is treated in an arithmetic unit and the drawing rate of the optical fiber is controlled during production on the basis of results from the unit, and Fig. 3 schematically shows a further embodiment of the present invention, in which two measuring devices for the outer diameter of the optical fiber are provided, one for use during slow speed drawing and the other for use during usual speed drawing, respectively. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Fig. 1 shows one embodiment of the present invention, in which the numerical number 1 indicates the preform for the optical fiber, 2 indicates a drawing furnace, 3 indicates an outer diameter measuring device, 4 indicates a die for resin coating, 5 indicates a curing device for resin and 6 indicates a winding up device for the optical fiber. The preform 1 which is heated and melted in the furnace 2 is stretched under tension to form the optical fiber 11, which is taken up by a spool (not shown) installed in the winding up device. In Fig. 1, Z is a distance from an outlet of the drawing furnace to the measuring device 3. Generally, an additional coating die and curing device is disposed between the curing device 5 and the winding up device 6. The present invention is characterized in that for a drawing rate of 200 m/min. or greater the outer diameter measuring device 3 is located at a position from which the shrinkage of the outer diameter of the optical fiber 11, while stretched, to the diameter of this fiber when finished is 0.5% to 0.08%. As a result, the position is located below the conventional position of the measuring device. Generally, the outer diameter of the preform is gradually reduced in the furnace corresponding to an axial change of the preform temperature (resulting from a viscosity change of the preform material). Further, the diameter of the shrinking portion of the preform is dependent on the drawing rate, the outer diameter of the preform and the preform temperature at the outlet of the furnace. Of course, the outer diameter of the optical fiber depends on the preform diameter, structural factors of the drawing furnace such as its heating length, the size of the furnace outlet, and the flow rate and the nature of the inert gas. Thus, the present invention resides in not only controlling the distance between the outlet or a center of the drawing furnace 2 and the measuring device 4 for the outer diameter of the optical fiber but also, as a whole, controlling the factors described above. It is known that a temperature T (°C) of the optical fiber at a position which is Z(m) away from the outlet of the drawing furnace is estimated according to the following equation (1): T = T 0 + (T S - T 0 ) exp (- a. Z/V F ) wherein T 0 is the room temperature (°C), T S is the temperature (°C) of an optical fiber immediately after leaving the furnace, Z(m) is a distance from an outlet of the furnace 2 to a position at which the outer diameter of the optical fiber is measured, V F is the drawing rate (or linear velocity) (m/min.) and "a" is a constant dependent upon the diameter of the optical fiber, the specific heat of the optical fiber and the thermal conductivity between the optical fiber and the atmosphere. As seen from the above equation (1), the higher the linear velocity, that is, the larger V F is, the higher is the temperature of the optical fiber when Z is fixed to a certain value. With an apparatus comprising the components shown in Fig. 1 in which a stable operation up to 300 m/min. of the drawing rate can be carried out, the optical fiber was repeatedly produced with various values of Z which is the distance from the shrinking part of the preform 1 to the outer diameter measuring device 3. During this production, the diameter of the optical fiber 11 was measured by the measuring device 3 and the diameter of the obtained optical fiber from which its coating had been stripped (that is, the true diameter of the optical fiber) was actually measured by a precise micrometer. Thus, it was found that, in the case of a drawing rate of 300 m/min., the difference between the measured diameter of the optical fiber with the measuring device 3 and the true diameter of the optical fiber was less than 0.5%, when the optical fiber is cooled to below a temperature at which the shrinkage of the optical fiber diameter under tension at the point where the outer diameter is measured with the measuring device is 0.5% or less. Thus, the position at which the measuring device is disposed is determined on the basis of the estimation of the fiber temperature according to the equation (1) and the several experiments as follows: Firstly, according to the present invention, the difference between the measured outer diameter and the true one is obtained for various positions of the measuring device 3. Then, a relation between the difference and the measuring position is established. Finally, the position is determined at which said difference is 0.5% to 0.08%. Thus, the measuring device is then located at this position and an optical fiber having the better accuracy is produced. EXAMPLES With an apparatus as shown in Fig. 1 in which a stable production at a velocity up to 300 m/min. was carried out, an optical fiber was drawn with varying values of Z from 0.4 to 0.8 m and the true outer diameter of the produced fiber was measured after stripping off the coating. As the outer diameter measuring device 3 at the measuring position, a Laser Diameter Monitor 551 A commercially available from Anritsu Corporation was used. Other conditions were as follows: Outer diameter of preform 1 25 mm Drawing rate 300 m/min. Room temperature (T 0 ) 25 °C Fiber temperature immediately after leaving furnace (T s ) 1600 °C When Z was 0.4 m, the measured outer diameter with the measuring device was 125.0 µm and the true outer diameter was 123.7 µm. When Z was 0.8m, the measured outer diameter with the measuring device was 125.0 µm and the true outer diameter was 124.9 µm. The fiber temperature at the measuring position was estimated to be about 900 °C according to equation (1). It is seen that the optical fiber is under shrinking at the position of Z = 0.4 m as employed in the conventional manner. In the embodiment as shown in Fig. 1, it is contemplated to produce an optical fiber with a measured diameter of 126.3 µm at the outer diameter measuring position so as to produce the optical fiber with a diameter of 125 µm. But such production is not necessarily essential. The results for other Z values are shown in the following Table that gives results falling within the scope of the present invention as well as results falling outside the scope of the present invention to disclose parameters that must be avoided. Measured outer diameter (µm) Drawing rate 100 m/min. 200 m/min. 300 m/min. Z = 0.4 m 125.1 125.2 126.1 0.5 m 125.0 125.1 125.5 0.6 m 125.0 125.1 125.2 True diameter 125.0 125.0 125.0 It can be seen that the present invention is particularly effective when drawing the optical fiber at a drawing rate higher than 300 m/min. Series of experiments as described above were repeated, and it was found that the optical fibre should be cooled to a temperature at which the shrinkage of the optical fiber under tension is 0.5% to 0.08% at a position where the outer diameter measuring device 3 is located when the drawing is carried out at rate higher than 300 m/min. Another embodiment of the present invention is shown in Fig. 2, in which the drawing rate is controlled with results from arithmetic operation (by, for example, a PID controller) on the deviation of the output signal of the measured outer diameter with the measuring device 3 from the desired outer diameter. A further embodiment of the present invention is shown in Fig. 3. In the embodiment as shown in Fig. 1, it takes time to detect the outer diameter of the fibre which is increased in diameter in the case of a small drawing rate, whereby a time lag arises in the control. In the embodiment as shown in Fig. 3, when the drawing rate is small, detection of the outer diameter is carried out with the measuring device 31 and when the drawing rate is increased, the detection is carried out with the measuring device 32. Alternatively, only one measuring device is used which can move along the optical fiber depending on the drawing rate. Further, a forced cooling device for the optical fiber may be provided between the furnace 2 and the outer diameter measuring device 3, whereby the distance Z between them can be shortened. In this embodiment, the diameter of the optical fiber is also measured at a position at which the shrinkage of the outer diameter is 0.5% to 0.08%. When the drawing rate largely exceeds 300 m/min., such a cooling device is especially preferred since large scaling of the apparatus can be avoided and a prompt response can be obtained. As described above, according to the present invention, the absolute value of the outer diameter of the optical fiber which has shrunk is measured correctly, whereby the optical fiber with better accuracy in its size is produced.

Claims: A drawing process for producing an optical fiber (11) which comprises drawing the optical fiber (11) from a preform (1) under tension to form the optical fiber while heating and melting the preform; and controlling the drawing conditions by means of the deviation of a measured diameter of the uncoated fiber from a preselected outer diameter of the fiber when finished; wherein, for a drawing rate of 200 m/min. or greater, the diameter of the uncoated optical fiber (11) is measured at a position (Z) from which position further shrinkage of the outer diameter of the optical fiber (11), while stretched, to the diameter of this fiber when finished is 0.5% to 0.08%; and wherein the term "shrinkage" is a percentage ratio wherein the numerator is the difference in outer diameters between the optical fiber at said measuring position (Z) and the optical fiber when it has finished shrinking; and the denominator is the outer diameter of the optical fiber which has finished shrinking. The process according to Claim 1, wherein the temperature of the optical fiber (11) at the measuring position (Z) for the outer diameter is lower than the glass softening point of the material of the optical fiber (11). The process according to Claim 1, wherein the drawing is carried out by controlling the outer diameter of the optical fiber (11) by varying the drawing rate depending on the deviation.

Inventors: CHIGUSA YOSHIKI, MATSUDA YASUO, YOSHIMURA ICHIRO, CHIGUSA, YOSHIKI, MATSUDA, YASUO, YOSHIMURA, ICHIRO, CHIGUSA, YOSHIKI C/O YOKOHAMA WORKS OF SUMITOMO, MATSUDA, YASUO C/O YOKOHAMA WORKS OF SUMITOMO, YOSHIMURA, ICHIRO C/O YOKOHAMA WORKS OF SUMITOMO
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1990
Main classification: C03B37
IPC codes: C03B37, G02B6