Curable organopolysiloxane compositions

Abstract: There are mixed together (A) an organopolysiloxane of a specified formula which contains a side chain alkenyl, e.g. vinyl, group on at least one unit, the other side chains R being optionally substituted hydrocarbon residues other than aliphatic satu­ rated, e.g., methyl, and terminal hydrocarbon residues, the number of units being to give a viscosity of 50 - 100,000 cp at 25°C; (B) an organohydrogenpolysiloxane of a specified formula, the side chains being as for R in (A), and the terminal groups being alkenyl and hydrogen atoms, statistically in a proportion of together one per molecule, and in a proport­ ion so that the H atoms attached to Si in (B) is 0.1 to 4.0 per alkenyl group of (A), and (C) an addition reaction catalyst (e.g. of platinum type) in a proportion of 0.1 - 100 ppm per 100 parts of (A). The resulting composition is cured by heating, e.g. at 150°C , to be cross-linked, without discoloration, and the gel formed is useful as an electrical sealant.

Description: This invention relates to curable compositions composed of organopolysiloxanes. Cured silicone rubber gels (referred to simply as silicone gels, hereinafter) are used for electric or electronic potting or sealing, and as covering material for protection of control circuit elements, especially power transistors, integrated circuits, condensers and the like, against thermal and mechanical damages; for this purpose the silicone gels have good electrical insulation, stability of electrical characteristics and flexibility. Various methods of preparing such silicone gels have been proposed. For instance, silicone rubbers have been formed in which the number of hydrogen atoms attached directly to a silicone atom amounts to one or less per one vinyl group attached directly to the silicon atom (JP-B-55-41705 and 55-38992). However, compositions which can be converted to such silicone gels by curing, and the silicone gels obtained suffer from a defect that they are discolored through thermal deterioration. Such a defect, though harmless in cases where electric insulation, electric characteristics, viscosity and the like are regarded as significant (because these properties of silicone gels are not changed by the discoloration) is a serious problem when optical characteristics are required of the silicone gels. The discoloration of silicone gels which has accompanied thermal deterioration is known to be correlated to the amount of platinum used as the addition reaction catalyst, and the ratio of = SiH to = SiCH=CH₂ groups. Specifically, the extent of discoloration becomes less the smaller the amount of platinum used is and the higher is the = SiH: = SiCH=CH₂ ratio. Therefore, the above-described discoloration resulting from thermal deterioration seems to be preventable by reducing the amount of platinum used. However, reduction in the amount of platinum tends to cause curing troubles. When the factor of high = SiH: = SiCH=CH₂ ratio is added in particular, there can be an additional problem that change in hardness and a foaming phenomenon are apt to be caused by thermal deterioration. With the intention of bringing about an improvement in the discoloration caused by thermal deterioration, there has been proposed the combined use of a polysiloxane containing per molecule at least two vinyl groups and one hydroxyl group attached directly to silicon atoms and silane containing one epoxy group and one alkoxy group per molecule (JP-B-55-35932). In addition, JP-A-62-39660 has disclosed a composition comprising an organopolysiloxane containing, attached directly to silicon atoms vinyl groups which number 0.1 to 2.0 on the average per one molecule and a hydrogensiloxane represented by the formula, R⁴Si(OSiR⁵₂H)₃ (wherein R⁴ represents an alkyl or phenyl group, and R⁵ represents an alkyl group). However, the silicone gels prepared from those compositions have a defect that their light transmittances at wavelengths shorter than 500 nm are lowered to 90 % or below after they have suffered thermal deterioration, which limits their utilization when optical quality is required. Therefore, an object of this invention is to provide an organopolysiloxane gel composition which has reduced discoloration due to thermal deterioration. We have now found that the use of an organohydrogen polysiloxane containing alkenyl groups and hydrogen atoms attached to silicon atoms at the molecular chain terminals is particularly effective. According to this invention we provide an organopolysiloxane gel composition comprising (A) an organopolysiloxane represented by the general formula: wherein R represents a substituted or unsubstituted monovalent hydrocarbon residue, other than an aliphatic unsaturated group; R¹ represents a substituted or unsubstituted monovalent hydrocarbon residue; R² represents an alkenyl group; and n and m each represents a positive integer: (B) an organohydrogenpolysiloxane represented by the general formula: wherein R has the same meaning as R in the component (A); each R³ is an alkenyl group or a hydrogen atom, provided that the proportion of said alkenyl group and hydrogen atom is each on the statistical average of one per one molecule; and l represents a positive integer; the proportion of component (B) being such that the number of the hydrogen atoms attached to silicon atoms in (B) corresponds to from 0.1 to 4.0 per one of the alkenyl groups attached to silicon atoms in the component (A): and (C) a catalytic amount of an addition-reaction catalyst. The term "statistic average" is used to include mixtures of alkenyl and hydrogen. In the component (A) represented by the above general formula (1), R represents a substituted or unsubstituted monovalent hydrocarbon residue prefereably having 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, except aliphatic unsaturated groups, with specific examples including alkyl groups such as methyl, ethyl, propyl, isopropyl, butyl and octyl, cycloalkyl groups such as cyclopentyl, cyclohexyl or cyclobutyl, aryl groups such as phenyl, naphthyl, tolyl or xylyl, aralkyl groups such as benzyl, phenylethyl or phenylpropyl, halogen derivatives of the above-cited groups such as chloromethyl, trifluoromethyl, trifluoropropyl, chlorophenyl or difluorophenyl, and cyanoalkyl groups such as β-cyanoethyl, γ-cyanopropyl or β-cyanopropyl. Among these groups a methyl group is preferred over others in respects of the ease of synthesis and thermal resistance of the silicone gel to be prepared. R¹ in the general formula (1) is a substituted or unsubstituted monovalent hydrocarbon residue preferably having 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, with specific examples including alkyl, cycloalkyl, and cyanoalkyl as exemplified for R, alkenyl groups such as vinyl, allyl or 1-butenyl, aryl groups such as phenyl, naphthyl, tolyl, or xylyl, aralkyl groups such as benzyl, phenylethyl, phenylpropyl, and halogenated derivatives of the above-cited groups such as chloromethyl, trifluoromethyl, trifluoropropyl, chlorophenyl, dibromophenyl, tetrachlorophenyl and difluorophenyl. R² is an alkenyl group, preferably containing 2 to 8 carbon atoms, more preferably 2 to 4 carbon atoms, e. g., vinyl, allyl or 1-butenyl; of these, a vinyl group is particularly favored from the standpoint of facility in synthesis. The sum of the integers n and m should preferably be chosen so that the component (A) has a viscosity of from 50 to 100,000 cp, preferably 500 to 5,000 cp, at 25°C. This is because when the viscosity is below 50 cp, the composition of the invention is liable to flow, whereas when it is beyond 100,000 cp the composition has poor fluidity. 1cp = 100 Pa.S (SI unit). Though it is not always necessary for the organopolysiloxane used by component (A) to have alkenyl groups attached to silicon atoms at both ends of the molecule, it is required for preventing the discoloration from occuring due to thermal deterioration, that on the average there is present, per molecule, at least one unit which contains an alkenyl group in a side chain and is represented by the formula When the proportion of the side-chain alkenyl group amounts on the average to less than one per molecule, there is the risk that the resulting composition cannot be hardened satisfactorily, so cannot assume a gel form, and is subject to discoloration through thermal deterioration. In the organohydrogen polysiloxane used as the component (B) and represented by the above formula (2), R has the same meaning as in the component (A), and R³ is a hydrogen atom or an alkenyl group preferably containing 2 to 8, more preferably 2 to 4 carbon atoms, such as vinyl, allyl or 1-butenyl; of these a vinyl group is particularly preferred in respect of facility of synthesis. In the organohydrogenpolysiloxane used as component (B), the occurrence of the alkenyl group and the hydrogen atom (each attached to the terminal silicon atom) are each on the statistical average one per one molecule. This component not only acts as a chain extending agent, but also functions to prevent discoloration from occuring at high temperatures; this is a characteristic of this invention. The component (B) is compounded in such an amount that the number of the hydrogen atoms attached to silicon atoms in the component (B) corresponds to from 0.1 to 4.0, preferably from 0.5 to 1.5, per one of the alkenyl groups attached to silicon atoms in the component (A). When the number of the hydrogen atoms corresponds to less than 0.1, the cross-linking reaction does not proceed adequately, so the silicon gel obtained is so soft that it still has flowability. On the other hand, when the number of the hydrogen atoms corresponds to more than 4.0, the silicone gel obtained becomes harder and harder with the lapse of time, and further there is a rish of its foaming. The component (B) is not particularly limited with respect to its viscosity, but it is desirable from the economic point of view in its production that the viscosity should be controlled to below 1,000 cp at 25°C. The catalyst used as component (C) in this invention is used for promoting the hydrosilylation reaction, and can be chosen appropriately from known ones, e.g., chloroplatinic acid, an alcohol-modified solution of chloroplatinic acid, a coordinate compound of chloroplatinic acid and olefins or vinylsiloxanes, tetrakis(triphenylphosphine) palladium, and chlorotris(triphenylphosphine)rhodium. Among them, the catalysts of the platinum type are used to particular advantage. The above-described catalyst is used in a so-called catalytic amount. In general, its amount is adjusted to 0.1 to 100 ppm based on the total amount of the components (A) and (B) or 100 parts by weight of (A). In addition to the above-described components (A) to (C), various other components can be contained in the composition of this invention, if needed. For instance, another silicone oil such as dimethylpolysiloxane, or raw rubber may be added in such an amount as not to impair the effect of this invention, for the purpose of controlling or modifying the flowability of the composition and the hardness of the cured composition. Also, a known reaction retarder or the like may be added. The composition of the invention can be cured (to cross-link it) in known manner, to make a gel-like cured product. This invention will now be illustrated in more detail by reference to the following examples, wherein all viscosity values were measured at 25°C. EXAMPLES The ingredients illustrated below were mixed homogeneously in compounding ratios (by weight) shown in Table 1 to prepare compositions Numbered 1 to 7. The compositions Nos. 1 to 3 were prepared in accordance with this invention, while Nos. 4 to 7 were prepared for comparison. Organopolysiloxane I : Dimethylpolysiloxane containing side-chain vinyl groups, which was represented by the following average constitutional formula, Organopolysiloxane II : Dimethylpolysiloxane containing vinyl groups, which was represented by the following average constitutional formula, Organopolysiloxane III : Dimethylpolysiloxane containing side-chain vinyl groups, which was represented by the following average constitutional formula, Organopolysiloxane IV : Dimethylpolysiloxane containing vinyl group, which was represented by the following average constitutional formula, Organopolysiloxane V : Dimethylpolysiloxane containing vinyl groups on both molecular ends, which was represented by the following average constitutional formula, Organopolysiloxane VI : Methylhydrogenpolysiloxane containing vinyl group, which was represented by the average constitutional formula, Organopolysiloxane VII : Methylhydrogenpolysiloxane represented by the average constitutional formula, Organopolysiloxane VIII : Methylhydrogenpolysiloxane represented by the average constitutional formula, Organopolysiloxane IX : Methylhydrogenpolysiloxane represented by the average constitutional formula, Catalyst: Compound obtained by heating a mixture of chloroplatinic acid with tetramethyldivinylsiloxane (platinum content: 1 wt%). Invention Comparison Composition No.1 No.2 No.3 No.4 No.5 No.6 No.7 Polysiloxane I 100 100 Polysiloxane II 100 Polysiloxane III 100 Polysiloxane IV 100 100 Polysiloxane V 100 Polysiloxane VI 42 42 42.5 Polysiloxane VII 6.5 Polysiloxane VIII 0.7 0.7 Polysiloxane IX 2.1 Catalyst 0.07 0.14 0.07 0.05 0.05 0.10 0.05 Platinum Content (ppm) 5 10 5 5 5 10 5 SiH/SiCH=CH₂ (by mole) 0.4 0.4 1.0 0.6 1.0 1.0 0.55 Each of the thus prepared compositions Nos. 1 to 7 was heated at 150°C for one hour, and thereby underwent curing, so that each composition was converted to a gelled material. Each gelled material was examined for its ease of resistance to penetration with a 6.3 mm (1/4 inch) consistency tester according to JIS K2808, and for transmittance in the following manner. The results obtained are shown in Table 2. Transmittance Test: The gelled materials from composition Nos. 1 to 7, which had been obtained by curing, were placed in a hot-air circulation type oven for a period of 100 hours under a temperature of 150°C. The thus heat-treated materials were examined for change in their transmittance to light of 400 nm with lapse of time. Invention Comparison Gelled Material No.1 No.2 No.3 No.4 No.5 No.6 No.7 Penetration Degree 80 80 84 65 100 95 70 Transmittance (%) Before Heat Treatment 99 99 99 94 93 88 89 After Heat Treatment 95 92 95 88 88 75 77 The data shown in Table 2 confirms the superiority of the organopolysiloxane gel compositions of this invention as regards their resistance against discoloration due to thermal deterioration, regardless of the amount of platinum catalyst used and the molar ratio of the = SiH to = SiCH=CH₂ group in their molecule. The penetration degrees are consistent with the resistances to discoloration.

Claims: An organopolysiloxane composition which comprises (A) an organopolyslloxane represented by the general formula, wherein R represents a substituted or unsubstituted monovalent hydrocarbon residue, other than an aliphatic unsaturated group; R¹ represents a substituted or unsubstituted monovalent hydrocarbon residue; R² represents an alkenyl group ; and n and m each represents a positive integer: (B) an organohydrogenpolysiloxane represented by the general formula, wherein R has the same meaning as R in the component (A); R³ is selected from alkenyl groups and hydrogen atom, provided that said alkenyl group and said hydrogen atom are each present on the statistical average at a level of one per molecule, and l represents a positive integer; and wherein the proportion of component (B) to (A) is such that the number of the hydrogen atoms attached to silicon atoms in (B) corresponds to from 0.1 to 4.0 per one alkenyl group attached to silicon atoms in the component (A); and (C) a catalytic amount of an addition-reaction catalyst. An organopolysiloxane composition as claimed in Claim 1, wherein R in component (A) is a methyl group. An organopolysiloxane composition as claimed in Claim 1 or 2, wherein R³ in component (A) is a vinyl group. An organopolysiloxane composition as claimed in Claim 1,2 or 3, wherein the sum of (n + m) is a number selected so that component (A) has a viscosity of 50 - 100,000 cp at 25°C. An organopolysiloxane composition as claimed in Claim 4, wherein said number is selected so that said viscosity is 500 to 5,000 cp. An organopolysiloxane composition as claimed in any preceding claim, wherein R³ in component (B) is a vinyl group or hydrogen atom. An organopolysiloxane composition as claimed in any preceding claim, wherein said proportion of component (B) is such that the number of the hydrogen atoms attached to silicon atoms in the component (B) corresponds to from 0.5 to 1.5 per one alkenyl group in the component (A). An organopolysiloxane composition as claimed in any preceding claim, wherein the viscosity of component (B) is less than 1,000 cp at 25°C. An organopolysiloxane composition as claimed in any preceding claim, wherein the catalyst (C) is of the platinum type. An organopolysiloxane composition as claimed in any preceding claim, wherein the content of the catalyst is 0.1 - 100 ppm based on 100 parts by weight of the component (A). A gel-like cured product obtained by curing a composition as claimed in any preceding claim.

Inventors: FUJIKI HIRONAO, IKENO MASAYUKI, FUJIKI, HIRONAO, IKENO, MASAYUKI
Applicants: SHINETSU CHEMICAL CO, SHIN-ETSU CHEMICAL CO., LTD.
Application year: 1990
Main classification: C08L83
IPC codes: C08L83, C09K3