Cementitious material for masonry constructions

Abstract: Cementitious compositions comprising aluminous cement and a pozzolanic material and optionally organic fibres are suitable to be mixed with water to form cement pastes or grouts for cement injection into the core walls of masonry constructions. If mixed with sand and water they form mortars for use as jointing or rendering mortar in masonry constructions.

Description: The invention relates to cementitious compositions of aluminous cements. According to the invention, there is provided the use as a cement paste or grout for cement injection into core walls or as jointing or rendering mortar for masonry constructions of a cementitious composition which is free of Portland cement and which comprises a) 10-90% by weight of an aluminous cement which contains 30-85% combined Al₂O₃; and b) 10-90 % by weight of a finely-ground natural or artificial pozzolan having a silica content of more than 30% by weight, a combined CaO content lower than 10% by weight and a free CaO content of less than 1% by weight. Preferably, the cementitious composition further contains c) 0.01-5 % by weight of organic fibres. Aluminous cements are readily available on the market and preferably contain 30-85 % by weight of combined Al₂O₃ and 15-70 % of primarily SiO₂, Fe₂O₃. Usually the aluminous cements are derived from pulverising clinker comprising primarily hydraulic calcium aluminates. Pozzolan is preferably as defined in ASTM C-618. Naturally-occurring finely ground pozzolan is preferably derived from volcanic sources or diatomaceous earth. Artificial pozzolans include fly ash, rice husk ash or silica fume. Preferably the pozzolan material contains 30 to 99 % (preferably 40 to 98 %) by weight SiO₂ and 1-10 % by weight combined CaO. The terms "combined" Al₂O₃ and CaO as well as "free" CaO are well known in the art. Preferably the organic fibres are 1 to 30 mm in length and preferably have a thickness of 1 to 100 µm. Preferably the fibres are synthetic or natural and are selected from polyacrylonitrile fibres, polyacrylic fibres, polyolefin fibres, polypropylene fibres, cellulose fibres and wool. Preferably a cementitious composition according to the invention is free of Ca(OH)₂ and CaO. This alleviates quick setting where this is undesirable. Further according to the invention there is provided a cement paste or grout or a jointing or rendering mortar for masonry constructions, mix comprising a cementitious composition hereinabove defined, sand and water having a ratio of water to cementitious composition of 0.2 to 1 and a ratio of sand to cementitious composition of 0.5 to 4. Cementitious mixes according to the invention may include one or more chemical admixtures selected from 1) plasticizers 2) superplasticizers 3) air entraining agents 4) retarders 5) water reducers and 6) accelerators. Preferably these admixtures are present in an amount of 0.1 to 10% based on the cementitious composition. Still further according to the invention, there is provided a cement paste or grout for cement injection into core walls or a jointing or rendering mortar for masonry constructions comprising a cementitious composition as hereinabove defined and water, having a ratio of water to cementitious composition of 0.2 to 1. Still further according to the invention there is provided a dry premixed mortar comprising a cementitious composition as hereinabove defined and aggregate, the ratio of aggregate to cementitious composition being in the range of 4:1 to 0.5:1, preferably 2.5:1 to 3.5:1. Cementitious compositions for use in the invention can be mixed with water to form cement pastes or grouts for cement injection into the core walls of masonry constructions or can be mixed with sand and water to form a mortar for use as a jointing or rendering mortar for masonry constructions. Preferably the ratio of sand to cementitious composition according to the invention is from 1:1 to 4:1, preferably 2.5:1 to 3.5:1. In the case of fine sand, the ratio is most preferably 1.5:1 to 2:1 and for coarse sand from 2.5:1 to 3.5:1. The appearance of the rendering mortar made with the cementitious compositions according to the invention advantageously does not form cracks that typically occur by one day plastic shrinkage when in the absence of wet curing. Compressive strength at early and later stages may be adjusted according to the requirement by changing the pozzolan/aluminous cement ratios. Finally, a mortar mix containing a cementitious composition according to the invention performs very well in contact with aggressive agents such as sulphates and chlorides. The invention will now be illustrated by the following Examples in which all parts and percentages are by weight. Examples 1 to 9 Cementitious mixes are prepared as given in Table 1 below. The aluminous cement used has 75 % combined Al₂O₃ and 25 % CaO. The volcanic earth (from the Naples area) is finely ground up to a specific surface area of 5000 cm²/g and contains SiO₂ (55 %), Al₂O₃ (20 %), Fe₂O₃ (5 %), CaO (5 %), MgO (1 %), Na₂O (5 %) K₂O (2 %) and loss on ignition 7 %. The fly ash (commercially available from ENEL - Italy) used contains SiO₂ (45 %), Al₂O₃ (25 %), Fe₂O₃ (10 %), CaO (3 %), MgO (2 %), K₂O (3 %); SO₃ (1 %) and loss on ignition (9 %). The silica fume (commercially available from Elkem) used contains: SiO₂ (95 %), Al₂O₃ (0.5 %), Fe₂O₃ (0.3 %), CaO (0.2 %), MgO (0.2 %), Na₂O (0.5 %), K₂O (0.2 %), SO₃ (0.18 %) and loss on ignition 3 %. The fibres used are 6 mm long and 15 µm thick. The compositions of Examples 1 to 9 are mixed with water and sand, in the proportions 1:0.5:3. The resulting mortars are cured at 20°C and at 95 % relative humidity. After 3, 7, 28 and 90 days the compressive strength are measured as given in Table 2 below. The mortars so produced have good finishability and exhibit no cracking or crazing (after 1 week in the absence of wet curing). In comparison to mortars made with traditional cementitious materials such as lime and/or Portland cement, the mortars of Examples 1 to 9 showed no deterioration after 6 months immersion at 5°C in 10% MgSO₄ or 30% CaCl₂ solutions. Examples 10 to 19 The mixtures of Examples 1 to 9 shown in Table 1 are mixed with 50 % water to form a flowable cementitious paste (a grout). Such grouts are used to fill an inner masonry wall to fill existing voids. After 1 week, the wall is cut and the sectioned specimens are visually appraised. The grouts perform well in filling the voids. Examples 20 to 26 Cementitious mixes are prepared as given in Table 3 below. The mixtures shown in Table 3 are mixed with 50 % water to form a flowable cementitious paste (a grout). Such grouts are used to fill an inner masonry wall to fill existing voids. After 1 week, the wall is cut and the sectioned specimens are visually appraised. The grouts perform well in filling the voids.

Claims: Use as a cement paste or grout for cement injection into core walls or as a jointing or rendering mortar for masonry constructions of a cementitious composition which is free of Portland cement and which comprises a) 10-90 % by weight of an aluminous cement which contains 30-85 % combined Al₂O₃; and b) 10-90 % by weight of a finely ground natural or artificial pozzolan having a silica content of more than 30 % by weight, a combined CaO content lower than 10 % by weight and a free CaO content of less than 1 % by weight.. Use according to claim 1, in which the cementitious composition contains from 0.01-5 % by weight of organic fibres Use according to claim 2 in which the organic fibres are selected from polyacrylonitrile fibres, polyacrylic fibres, polyolefin fibres, polypropylene fibres, cellulose and wool. Use according to claim 1 or claim 2, in which the cementitious composition is free of Ca(OH)₂ and CaO. Use acording to any one of the preceding claims in which the cementitious composition contains one or more additional chemical admixtures selected from 1) plasticizers 2) superplasticizers 3) air entraining agents 4) retarders 5) water reducers and 6) accelerators. A cement paste or grout for cement injection into core walls or a jointing or rendering mortar for masonry constructions comprising a cementitious composition as described in any one of claims 1-5 and water having a ratio of water to cementitious composition of 0.2 to 1. A cement paste or grout or a jointing or rendering mortar according to claim 6, comprising a cementitious composition according to any one of claims 1-5, sand and water, having a ratio of water to cementitious composition of 0.2 to 1 and a ratio of sand to cementitious composition of 0.5 to 4. A dry premixed mortar comprising a cementitious composition as described in any one of claims 1-5 and aggregate, the ratio of aggregate to cementitious composition being in the range of 4:1 to 0.5:1.

Inventors: BIAGINI STEFANO, COLLEPARDI MARIO, BIAGINI, STEFANO, COLLEPARDI, MARIO
Applicants: SANDOZ AG, SANDOZ-ERFINDUNGEN VERWALTUNGSGESELLSCHAFT M.B.H., SANDOZ-PATENT-GMBH
Application year: 1990
Main classification: C04B28
IPC codes: C04B28