Toughened, hydrolysis resistant polycarbonate/polyester blends

Abstract: It was surprisingly found that a thermoplastic molding composition which contains polycarbonate and polyalkylene terephthalate resins at a particular weight ratio therebetween is rendered improved impact strength and hydrolysis resistance upon the incorporation of an additive amount of high melt flow high density polyethylene therewith. The molding composition of the invention comprise about 20-90 percent of polycarbonate resin, 80-10 percent of polyalkylene terephthalate (preferably PET) and about 3 to 5 percent of a high density polyethylene resin having a specific gravity of 0.94-0.97 and melt flow of 1 to 80 gm/10 min. as determined in accordance with ASTM D 1238.

Description: The present invention is directed to a thermoplastic molding composition consisting of : (i) aromatic polycarbonate resin, (ii) polyalkylene terephthalate resin and (iii) high density polyethylene resin having a melt flow index in the range of 23 to 60 gm/10 min as determined in accordance with ASTM D 1238 said composition being further characterized in that articles molded therefrom exhibit a characteristic ductile impact failure and in that the weight ratio of said (i) to said (ii) to said (iii) is about 65-75/35-25/3-5. EP-A-0 272 857 discloses a thermoplastic molding composition containing polycarbonates, polyalkylene terephthalates and high density polyethylene having a melt index from 0,5 to 5,0. EP-A-0 122 601 discloses mixtures containing polyolefin resins having a melt index of not more than 4 g/10 minutes. EP-A-0 105 244 discloses mixtures containing polyolefins the melt index thereof is not mentioned generally. The melt index of the polyethylene LC-732 used in the examples is 0.25 g/10 minutes. DE-A-3 245 467 discloses mixtures containing polyolefin resins including all types thereof (page 17, 3rd. paragraph of the DE-A). From the examples it is not clear which type of polyethylene is Hizex 3300 F, mentioned on page 29, lines 28/29. Thus the teaching of the DE-A is also no anticipation of the instant claimed invention. EP-A-0 322 095 discloses mixtures containing polyethylene resins which are not specified with espect to the melt flow index used. This is also true for the examples 20 and 21 of the EP-A. According to EP-A-0 322 095, page 9, lines 8 ff, a significant drop in impact properties occurs with the addition of PE to PET / PC blends. Contrary thereto the mixtures of instant invention have improved impact strength. This had not been expected from the prior art. It was surprisingly found that the impact strength and hydrolysis resistance of a thermoplastic molding composition which contains polycarbonate and polyalkylene terephthalate is improved by the incorporation of an additive amount of high melt flow polyethylene therewith. The composition is characterized by the particular weight ratio between the polycarbonate and polyalkylene terephthalate. The molding composition of the invention is suitable for the preparation of molded articles which are characterized by their improved impact performance. Ductile break upon failure which is a characteristic of such articles makes the composition particularly suitable for molding articles where brittle behavior is unacceptable. The high molecular weight, thermoplastic polyester resin suitable in the practice of the invention are derived from an aromatic dicarboxylic acid and a diol component and are characterized in that their intrinsic viscosity is at least 0.4 deciliters per gram. Optionally, the aromatic dicarboxylic acid component accounts for at least 85 mole percent of the dicarboxylic acid component. Among the suitable aromatic dicarboxylic acids are terephthalic acid, isophthalic acid, napthalene-dicarboxylic acid, diphenylether dicarboxylic acid, diphenyldicarboxylic acid, diphenylsulfone dicarboxylic acid and diphenoxyethane dicarboxylic acid. The optional, at most 15 mole percent of the acid component which is not aromatic dicarboxylic, may be represented by hydroxycarboxylic acids and by aliphatic dicarboxylic acids such as succinic acid, adipic acid and sebacic acid. The diol component of these polyesters may contain from 2 to 10 carbon atoms, preferably from 2 to 4 carbon atoms in the form of linear methylene chains with up to 30 mole percent of one or more other aliphatic diols having 3 to 8 carbon atoms, cycloaliphatic diols having from 6 to 15 carbon atoms or aromatic diols having from 6 to 21 carbon atoms. Examples of such additional diols ("codiols") include 3-methylpentanediol-(2,4), 2-methylpentanediol-(1,4), 2,2,4-trimethylpentanediol-(1,3), 2-ethylhexanediol-(1,3), 2,2-diethylpropanediol-(1,3), hexanediol-(1,3), 1,4-di-(-hydroxyethoxy)-benzene, 2,2-bis-(4-hydroxycyclohexyl)-propane, 2,4-dihydroxy-1,1,3,3-tetramethylcyclobutane, 2,2-bis-(3-hydroxyethoxyphenyl)-propane and 2,2-bis-(4-hydroxypropoxyphenyl)-propane. Typical examples of the diol include ethylene glycol, trimethylene glycol, tetramethylene glycol and hexamethylene glycol, neopentyl glycol, cyclohexane dimethylol, tricyclodecane dimethylol, 2,2-bis-(4-hydroxyethoxy-phenyl)-propane, 4,4'-bis-(-hydroxyethoxy)-diphenylsulfone, and diethylene glycol. The polyesters may be branched by incorporating trihydric or tetrahydric alcohols or tribasic or tetrabasic acids, as described in DE-A- 1,900,270 and in U.S. -A- 3,692,744. Examples of suitable branching agents include trimesic acid, pyromellitic acid, trimethylolpropane and ethane, and pentaerythritol. It is advisable to use no more than 1 mole percent of branching agent, based on the quantity of acid component. The polyesters may also contain known monofunctional compounds such as phenol or benzoic acid as chain terminators. The preferred polyesters are characterized in that their structure comprises units of the general formula (1). wherein n denotes 2 to 4 The intrinsic viscosity characterizing the suitable polyester resins in the practice according to the invention should preferably be in the range of 0.4 to 1.4 grams per deciliter and, more preferably, between 0.4 and 1.1 grams per deciliter, as measured in a 1 percent solution of phenol and tetrachloroethane (60:40) at 25°C. Methods for the preparation of the polyester resin suitable in the present context are known and have been described in U.S. -A-2,463,319 and 3,047,539. The composition of the invention may include crystallization rate promoters for the polyester (such as oligomeric polyesters) to allow lower mold temperatures and shorter injection cycles. Suitable promoters have been taught in U.S. -A- 4,223,113. The most preferred poly(alkylene terephthalate) in the present context is poly(ethylene terephthalate). The polycarbonate resins useful in the practice of the invention are homopolycarbonate, copolycarbonate and terpolycarbonate resins or mixtures thereof. The polycarbonate resins generally have molecular weights of 10,000-200,000 (weight average molecular weight) preferably 20,000-80,000, and are additionally characterized by their melt flow of 1-24 gm/10 min. at 300°C per ASTM D-1238. These polycarbonate resins may be prepared, for example, by the known diphasic interface process from phosgene and dihydroxy compounds by polycondensation (see the monograph H. Schnell, Chemistry and Physics of Polycarbonates, Interscience Publishers, New York, 1964, incorporated herein by reference). In the present context, dihydroxy compounds suitable for the preparation of the polycarbonates of the invention conform to the structural formula (1) or (2) wherein A denotes an alkylene group with 1 to 8 carbon atoms, an alkylidene group with 2 to 8 carbon atoms, a cycloalkylene group with 5 to 15 carbon atoms, a cycloalkylidene group with 5 to 15 carbon atoms, a carbonyl group, an oxygen atom: S, -SO- or -SO₂-radical; a radical of the general formula g denotes the number of 0 or 1; Z denotes F, Cl, Br or C₁-C₄ alkyl and if several Z radicals are substituents in one aryl radical, they may be identical or different; d denotes 0 or an integer of from 1 to 4; and f denotes 0 or an integer of from 1 to 3. Among the useful dihydroxy compounds in the practice of the invention are hydroquinone, resorcinol, bis-(hydroxyphenyl)-alkanes, bis-(hydroxyphenyl)-cycloalkanes, bis-(hydroxyphenyl)-ethers, bis-(hydroxyphenyl)-ketones, bis-(hydroxyphenyl)-sulfoxides, bis-(hydroxyphenyl)-sulfones and 2,2-bis-(hydroxyphenyl)-diisopropyl-benzenes. These and further suitable aromatic dihydroxy compounds are described, for example in U.S. -A-3,028,365, 2,999,835, 3,148,172, 2,991,273, 3,271,367, and 2,999,846, in DE-A 1,570,703, 2,063,050, 2,063,052, 2,211,956 and 2,211,957 and in the monograph, H. Schnell, Chemistry and Physics of Polycarbonates, Interscience Publishers, New York, 1964. Further examples of suitable bisphenols are 2,2-bis-(4-hydroxyphenyl)-propane (bisphenol A), 2,4-bis-(4-hydroxyphenyl)-2-methylbutane, 1,1-bis-(4-hydroxyphenyl)-cyclohexane, 2,2-bis-(4-hydroxyphenyl)-p-diisopropylbenzene, 2,2-bis-(3-chloro-4-hydroxyphenyl)-propane, hydroxybenzophenone and 4,4'-sulfonyl diphenol. The most preferred bisphenol is 2,2-bis-(4-hydroxyphenyl)-propane (bisphenol A). The polycarbonates of the invention may entail in their structure, units derived from one or more of the suitable bisphenols. The preparation of polycarbonate resins may be carried out in accordance with any of the processes known in the art, for example, by the interfacial polycondensation process, polycondensation in a homogeneous phase or by transesterification. In the preparation of the polycarbonate resins of the invention, monofunctional reactants such as monophenols may be used in order to limit their respective molecular weights. Also, branching agents may be employed. Branching may be obtained by the incorporation of small amounts, preferably of between about 0.05 and 2.0 mol percent (relative to diphenols employed), of trifunctional or more than trifunctional compounds, especially compounds having three or more phenolic hydroxyl groups. Polycarbonates of this type are described, for example, in DE-A-1,570,533; 1,595,762; 2,116,974 and 2,113,347, and U.S. -A- 3,544,514. Some examples of compounds with three or more than three phenolic hydroxyl groups which can be used are phloroglucinol, 4,6-dimethyl-2,4,6-tri-(4-hydroxyphenyl)-heptane, 2,4,6-trimethyl-2,4,6-tri-(4-hydroxyphenyl)-heptane, 1,4,5-tri-(4-hydroxyphenyl)-benzene, 1,1,1-tri-(4-hydroxy-phenyl)-ethane, tri-(4-hydroxyphenyl)-phenylmethane, 2,2-bis-[4,4-bis-(4-hydroxyphenyl)-cyclohexyl]-propane, 2,4-bis-(4-hydroxyphenylisopropyl)-phenol, 6-bis-(2-hydroxy-5'-methylbenzyl)-4-methylphenol, 2-(4-hydroxyphenyl)-2-(2,4-dihydroxyphenyl)-propane, hexa-(4-(4-hydroxyphenylisopropyl)-phenyl)-orthoterephthalic acid ester, tetra-(4-hydroxyphenyl)-methane, tetra-(4-(4-hydroxyphenylisopropyl)-phenoxy)-methane and 1,4-bis-(4'-4''-dihydroxytriphenyl)-methyl)-benzene. Some of the other trifunctional compounds are 2,4-dihydroxy-benzoic acid, trimesic acid, dyanuric chloride and 3,3-bis-(4-hydroxyphenyl)-2-oxo-2,3-dihydroindole. Among the resins suitable in the practice of the invention are included phenolphthalene based polycarbonate, copolycarbonates and terpolycarbonates such as are described in U.S. -A-3,036,036 and 4,210,741. The polyethylene resin suitable in the present invention is well known and may be prepared by skilled artisans by following methods known in the art. Alternatively, the polyethylene may be procured in commerce such as under the trade name of Petrothene®. Specifically, the polyethylene resin may be described as high density polyethylene having a specific gravity of about 0.94-0.97 and in that its melt flow index as measured in accordance with ASTM D-1238 is in the range of 23 to 60 gm./10 min. The composition of the invention may contain additives and agents such as are known in the art to impart certain known properties in thermoplastic molding compositions. Among these are plasticizers, heat and hydrolysis stabilizers, pigments, fillers and reinforcing agents as well as flame retardants of various types. EXAMPLES Compositions in accordance with the invention have been prepared and articles were molded therefrom and tested. In the compositions, the polycarbonate was Makrolon® 2800 resin, a homopolycarbonate based on bisphenol-A, characterized in that its melt flow index is about 9 gm./10 min., a product of Mobay Corporation; the polyethylene terephthalate was Tenite® 12270 resin from Eastman Kodak characterized in that its inherent viscosity is about 0.59; and the polyethylene was Petrothene®, a product of U.S. Industrial Chemicals, having a density of 0.95 gm/cc and a melt flow of 23.0. In the comparative examples which were similarly processed, molded and tested, the polyethylene was Petrothene®, having a density of 0.95 gm/cc and a melt flow of 9.5. The compositions were prepared following conventional procedures and the molding was carried out by injection using the following process parameters: Extrusion conditions: Extruder: Werner & Pfleiderer Corp. ZSK 30 Twin screw extruder; Zone set temperature (°C) 1 off 2 off 3 250 4 260 5 270 die 280 Screw Speed (RPM) 300; Vacuum - on Molding conditions: Machine: 85.1 g (3 oz.) Newbury Zone set Temperature (°C) 1 260 2 260 nozzle 260 Injection pressure MPa (psi) first stage 69 (10,000) second stage 55.2 (8,000) Cycle time (sec) First stage 5 second stage 10 total 30 Mold temperature (°C) 74 The tables below summarize the results: In Table 1 there are presented data showing the impact strength of PET-rich compositions wherein weight ratio of the resinous components is about 40/60 (polycarbonate/PET). The addition of polyethylene of high or of low melt flow appears to have no appreciable effect on the impact strength of these compositions. Example 1-1 1-2 Polycarbonate, wt. % 39 39 PET, wt. % 59 59 Polyethylene (melt flow 23.0) wt.% 2 - Polyethylene (melt flow 9.5) wt.% - 2 Impact Strength, J/m @ 3.2 mm (ft-lb/in @ 1/8") Notched Izod 58.7 (1.1) 64.1 (1.2) In an additional set of experiments where the weight ratio between the resinous components was about 70/30 (polycarbonate/PET), the addition of a small amount (2%) of polyethylene, of either melt flow, appeared to have no appreciable effect on the impact strength of the resulting compositions - see Table 2. Example 2-1 2-2 2-3 Polycarbonate, wt.% 68.5 68.5 70.0 PET, wt.% 29.5 29.5 30.0 Polyethylene (melt flow 23.0) wt.% 2 - - Polyethylene (melt flow 9.5) wt.% - 2 - Impact Strength, J/m @ 3.2 mm (ft-lb/in @ 1/8") Notched Izod 133.5 (2.5) 128.2 (2.4) 106.8 (2.0) In yet an additional set of experiments, it was found that the impact performance of PET-rich compositions, PET/polycarbonate weight ratio of about 60/40, is not affected appreciably upon the addition of a higher amount (4%) of polyethylene of either melt flow. (Table 3) Example 3-1 3-2 Polycarbonate, wt.% 39 39 Polyethylene terephthalate, wt.% 57 57 Polyethylene (melt flow 23.0), wt.% 4 - (melt flow 9.5), wt.% - 4 Impact Strength, J/m @ 3.2 mm (ft-lb/in @ 1/8") Notched Izod 80.1 (1.5) 58.7 (1.1) The table below demonstrates the composition of the invention where the addition of high melt flow polyethylene to PC-rich composition, (PET/Polycarbonate weight ratio of about 30/70) results in a marked increase of the impact strength. Example 4-1 4-2 Polycarbonate, wt.% 67 67 Polyethylene terephthalate, wt.% 29 29 Polyethylene (melt flow 23.0), wt.% 4 - (melt flow 9.5), wt.% - 4 Impact Strength, J/m @ 3.2 mm (ft-lb/in @ 1/8") Notched Izod 662.2 (12.4) 181.6 (3.4) Viewed in comparison to control compositions (PC/PET weight ratio of 70/30) which contain no polyethylene and having therefore an impact strength of about 107 J/m (2 ft-lb/in.), the compositions of the invention indeed represent an unexpected technical advance. In an additional set of experiments, the results of which are summarized below, the composition of the invention is compared to related compositions which contain polyethylene in amounts outside the scope of the invention. The polyethylene terephthalate resin in this set of experiments was Tenite® 7741 which is characterized in that its intrinsic viscosity is about 0.61. The other components, polycarbonate and polyethylene, were the same as the ones used in the above experiments. The impact strength values tabulated below represent the arithmetic average of two experiments. Example 5-1 5-2 5-3 5-4 5-5 5-6 Polycarbonate, wt.% 70.0 68.5 68.0 67.0 66.5 66.0 Polyethylene terephthalate, wt.% 30.0 29.5 29.0 29.0 28.5 28.0 Polyethylene (melt flow 23.0), wt.% 0.0 2.0 3.0 4.0 5.0 6.0 Impact Strength, J/m @ 3.2 mm (ft-lb/in @ 1/8") Notched Izod 106.8 (2.0) 218.9 (4.1) 560.7 (10.5 ) 731.6 (13.7) 806.3 (15.1) 582.1 (10.9 ) Flexural Modulus, MPa (ksi x 10²) 2413.8 (3.5) 2413.8 (3.5) 2344.8 (3.4) 2344.8 (3.4) 2344.8 (3.4) 2275.9 (3.3) Flexural Strength, MPa (ksi) 91.7 (13.3) 89.6 (13.0) 89.6 (13.0) 88.3 (12.8) 88.9 (12.9) 83.4 (12.1) Hydrolysis resistance MAX. OUTER FIBER STRAIN, % TENSILE ELONGATION, % 0.0 120 125 - 130 - 125 0.32 75 125 - 125 - 125 0.63 120 130 - 125 - 125 0.95 110 125 - 125 - 20 1.26 80 125 - 120 - 125 1.57 40 50 - 120 - 115 1.88 25 120 - 120 - 120 2.19 40 125 - 125 - 120 It is clear from the results that the composition of the invention which is characterized by its ratio of PET to polycarbonate components, and the amount and melt flow of its polyethylene additive, is superior in impact performance and hydrolysis resistance to corresponding compositions where any of these particular parameters is not met.

Claims: A thermoplastic molding composition consisting of: (i) aromatic polycarbonate resin, (ii) polyalkylene terephthalate resin and (iii) high density polyethylene resin having a melt flow index in the range of 23 to 60 gm/10 min as determined in accordance with ASTM D 1238, said composition being further characterized in that articles molded therefrom exhibit a characteristic ductile impact failure and in that the weight ratio of said (i) to said (ii) to said (iii) is about 65-75/35-25/3-5. The composition of Claim 1 wherein said (ii) is polyethylene terephthalate. The composition of Claim 1 wherein said polyethylene has a specific gravity of about 0.94 - 0.97. The composition of Claim 1 wherein said polyethylene has a melt flow index of 23 g/10 min.

Inventors: CHARLES JOHN J, CHUNG JAMES Y J, LAZEAR NELSON R, CHARLES, JOHN J., CHUNG, JAMES Y. J., LAZEAR, NELSON R.
Applicants: MILES INC, MILES INC.
Application year: 1990
Main classification: C08L67
IPC codes: C08L67, C08L69