MOLDED ARTICLE FOR HOLDING WAFER

Abstract: A molded article for holding a wafer, which is made of a thermoplastic resin reinforced with whiskers and used for handling a wafer and a glass sheet for a liquid crystal television set, such as a transfer basket, a storage case, a carrier jig, and the like. It is useful for washing, drying, moving or storing a semiconductor wafer free of contamination.

Description: Technical field The present invention relates to molded articles for holding wafers. More particularly, the present invention relates to molded articles adapted for transporting, storing or stowing semiconductor wafers or glass plates for liquid crystal televisions free of contamination and with safety. Background art In semiconductor production processes, wafers are handled by the so-called cassette-to-cassette system wherein wafers are transported, as placed in wafer baskets or carriers, from step to step. This system has achieved remarkably increases in the quantity of semiconductors produced. The wafer production process is practiced entirely within a clean room or clean bench which is diminished in the amount of dust present to keep the surface of semiconductor wafers clean at all times. Conventional wafer baskets are left open at opposite sides and at its upper portion for ease of cleaning, drying, transport or transfer, while wafers are generally left exposed when handled with carriers. Accordingly, wafers are very likely to be contaminated with small dust particles or the like remaining in the clean room. Wafer baskets are therefore transported or stored usually as accommodated in a closed box, whereas not infrequently, the wafer basket is transported as it is, or wafers are left exposed when transported with use of carriers, without considering the possibility of contamination. The influence of small dust particles is negligible when the width of patterns to be formed on semiconductor devices is small, but even dust particles as small as about 0.1 µm produce an adverse influence as the pattern width decreases with an increase in the complexity of integration as from LSI to VLSI. Thus, it has become increasingly important to prevent dust deposition on the wafer surface. Conventional carriers, wafer baskets for cleaning, baskets for drying, baskets for transport and storage cases are predominantly synthetic resin moldings, and most of them are electrically chargeable insulating moldings which are prepared by molding polypropylene (PP) or like resin as it is (without reinforcement). Presently, therefore carriers, baskets and storage cases are damaged by wafers, producing dust, becoming charged to attract dust and permitting promoted deposition of dust on wafers to result in a high reject ratio. Further since the resin used is not reinforced, the baskets for cleaning or drying have the drawback of having insufficient thermal rigidity. On the other hand, in the case where carriers, baskets, storage cases and like wafer holding molded articles are reinforced with glass fiber, carbon fiber, chopped fiber or the like, it is impossible to internally reinforce the moldings up to the outermost surface thereof when observed microscopically. Consequently, it is always likely that the moldings will be damaged by wafers, or wafers themselves will be damaged by moldings which are as high as 6 to 7 in Moh's hardness. On the other hand, the resin material is subjected to an antistatic treatment usually by adding carbon black thereto, whereas carbon black is extremely fine, very low in compatibility with the resin and prone to become released and scatter about to contaminate wafers owing to abrasion or frictional contact with wafers. Although investigations were conducted on surfactants for use as antistatic agents, they fail to retain a sustained antistatic effect and become a dust attractant like insulating moldings. Moreover, even the presence of a very small amount of vapor of surfactant could lead to the serious drawback of fogging up the wafer surface. Further in the case of liquid crystal panels, rapid progress has been made in providing precision display screens with use of glass substrates of reduced thickness, which need to fulfill the same requirements as semiconductor wafers. We have conducted intensive research to overcome the foregoing drawbacks of the prior art and consequently found that the contamination of wafers is attributable largely to incorporation of air in the cleaning step and to charging of air in the drying step. More specifically, when wafers as contained in a basket are dipped in a cleaning solution (acid, alkali or the like) for cleaning, many air bubbles adhere to the surface of the wafers, which in turn are contaminated with dust present in the bubbles. Since wafers are dried in air having a temperature of about 200 °C , the air becomes charged when flowing rapidly, consequently charging the basket, which in turn attracts dust or the like to contaminate the wafer. We have also found that the contamination of wafers can be remarkably prevented over the entire production process if it is possible to preclude wafer contamination in these cleaning and drying steps. An object of the present invention is to provide a molded article for holding wafers which is capable of preventing deposition of dust and extraneous matter on the wafers during cleaning, drying, transport or storage, especially during cleaning and drying, and which is less likely to be damaged by the wafer and to cause damage to the wafer itself. Another object of the invention is to provide a molded article for holding wafers which has improved thermal strength (inclusive of rigidity) as required of cleaning and drying baskets. Another object of the invention is to provide a molded article for holding wafers which is also usable for cleaning, drying, transporting or storing glass plates for liquid crystal televisions. Still another object of the invention is to provide the above-mentioned wafer holding articles at a low cost without necessitating special handling. The foregoing objects of the present invention, especially prevention of contamination of wafers in the cleaning and drying steps, can be accomplished by a molded article (basket or the like) made of a thermoplastic resin containing whiskers as defined in claim 1. Disclosure of the invention Thus, the present invention provides wafer holding molded articles made of a thermoplastic resin reinforced with whiskers, wherein the whiskers are either prepared by adhering or depositing a conductive or semi-conductive substance on the surface of potassium titanate whiskers represented by : K 2 O·mTiO 2 wherein m is a real number of up to 8, the whiskers having an average filament diameter of 0.01 to 1 µm, an average filament length of 1 to 100 µm and an average filament length/ average filament diameter ratio (aspect ratio) of at least 10, or are electrically conductive potassium titanate whiskers represented by : K 2 O·n(TiO 2 -x) wherein n is a real number of up to 8, and x is a real number smaller than 2, the whiskers having an average filament diameter of 0.01 to 1 µm, an average filament length of 1 to 100 µm and an aspect ratio of at least 10. The potassium titanate whiskers which are not per se electrically conductive are prepared by adhering or depositing a conductive or semi-conductive substance, such as a metal or metal oxide, on the surface of these potassium titanate whiskers, for example, by the electroless plating process, dipping process or precoating process. The thermoplastic resin to be used in the present invention is preferably one having high resistance to heat and chemicals since the product, i.e., the wafer holding molded article, is subjected to a chemical cleaning step for removing therefrom contaminants, i.e., particles, organic materials, metals and natural oxide films. Examples of such resins are polystyrene, ABS resin, polyphenylene oxide, ionomer resin, polyethylene, polypropylene, nylon 6 resin, nylon 6,6 resin, aromatic polyamide resin, polycarbonate, polyacetal, polyphenylene sulfide, trimethylpentene resin, polyether ether ketone (PEEK), polyether ketone (PEK), polysulfone (PSF), tetrafluoroethylene/perfluoroalkoxyethylene copolymer (PFA), polyethersulfone (PES), high-temperature amorphous resin (HTA) , polyallylsulfone (PASF) , polyetherimide (PEI), liquid crystal polymer (LCP), polyvinylidene fluoride (PVDF), ethylene/tetrafluoroethylene copolymer (ETFE) , tetrafluoroethylene/hexafluoropropylene copolymer (FEP) , tetrafluoroethylene/hexafluoropropylene/perfluoroalkoxyethylene terpolymer (EPE), etc. Especially preferable among there are PEK, PEEK, PES, PEI, PSF, PASF, PFA, FEP, HTA, LCP and the like. When the thermoplastic resin to be used in the present invention is polypropylene (PP) which is prepared usually by polymerizing propylene in the presence of a Ziegler-Natta catalyst, it is desirable to add the resin a hydrochloric acid absorbing agent for absorbing the catalyst and an antioxidant (or peroxide decomposing agent) for preventing oxidation to which PP is susceptible. Preferably, the antioxidant (or peroxide decomposing agent) is used in an amount of 10 to 1000 ppm, and the hydrochloric acid absorbing agent in an amount of 200 to 500 ppm. If the amounts of these agents are outside the respective ranges, the wafer holding molded article is likely to exhibit impaired properties. Examples of useful antioxidants (or peroxide decomposing agents) are phenolic compounds such as 2,6-di-tert-butyl-p-cresol, butylated hydroxyanisole (BHA), 2,6-di-tert-butyl-4-ethylphenol, stearyl-β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, 2,2'-methylenebis(4-methyl-6-tert-butylphenol), 2,2'-methylenebis(4-ethyl-6-tert-butylphenol), 4,4'-thiobis(3-methyl-6-tert-butylphenol), 4,4'-butylidenebis(3-methyl-6-tert-butylphenol), 1,1,3-tris(2-methyl-4-hydroxy-5-tert-butylphenol)butane, 1,3,5-trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)benzene, tetrakis[methylene-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate]methane and bis[3,3'-bis (4'-hydroxy-3'-tert-butylphenyl) butyric acid)glycol ester, sulfur compounds such as dilaurylthio dipropionate, dimyristylthio dipropionate and distearylthio dipropionate, and phosphorus compounds such as triphenyl phosphite, diphenylisodecyl phosphite, phenyldiisodecyl phosphite, 4,4'-butylidenebis(3-methyl-6-tert-butylphenyl-ditridecyl)phosphite, cyclic neopentanetetraylbis(octadecylphosphite), tris(nonylphenyl)phosphite, tris (mono- and/or dinonylphenyl)phosphite, diisodecylpentaerythritol diphosphite and 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, etc. Examples of useful hydrochloric acid absorbing agents are calcium stearate, zinc stearate and like metal salts of fatty acids, epoxidized soybean oil, hydrotalcite and the like. These antioxidants (or peroxide decomposing agents) and hydrochloric acid absorbing agents can be used singly or in combination. The whiskers are used usually in an amount of 5 to 50 wt.%, preferably 10 to 40wt.%, based on the thermoplastic resin. When conductive potassium titanate whiskers are used according to the invention, these whiskers, which are in the form of microscopic filaments, can be uniformly dispersed throughout the entire body of the wafer basket or storage case, whereby the microscopic portions thereof can be controlled to more uniform electric conductivity and given more uniform mechanical properties. The wafer holding molded articles of the present invention, such as wafer baskets for transport, storage cases and carriers, can be produced usually by a known method with the exception of using the above materials, for example, by pelletizing the resin composition using a twin screw extruder and subjecting the pelletized composition to injection molding. Molded articles of the present invention can be advantageously usable, for example, as baskets for electronic parts which must be free from dust, electronic parts which require a fine wiring structure, etc. Examples of such electronic parts are LCDs, DCDs, ECDs, ELs, PCDs, ICs, LSIs and the like. Such articles are favorably usable also for the production and storage of glass plates for liquid crystal televisions. Brief description of the drawings FIGS.1 and 2 are perspective views of carriers; FIG.3 is a plan view of a wafer basket for transport; FIG.4 is a side elevation of the same; FIG.5 shows a storage case; and FIG.6 schematically shows a wafer basket for transport as accommodated in the storage case. The reference signs define : 1···wafer support, 2···wafer support groove, 3···fixing portion, 4···side plate, 5···groove, 6···upper plate, 7, 11···wafer, 8···wafer carrier, 9···basket, 10···storage case. Best mode of carrying out the invention The invention will be described with reference to the following examples. Examples 1 to 13 and Comparative Examples 1 to 5 Each of the compositions listed in Table 1 was pelletized by a twin screw extruder-kneader. Using an injection molding machine, the pelletized composition was molded into carriers shown in FIGS.1 and 2, transport baskets shown in FIGS.3 and 4, and storage cases shown in FIG.5. FIG.6 is a diagram showing the transport basket as accommodated in the storage case. The molded articles were used for 3 months in a wafer production process to check wafers for contamination by observing the state of the molded articles and the influence thereof on the wafers. In the table, "A" indicates that flaws were found on the molded article due to the insertion or removal of wafers, and "B" represents adhesion of many dust particles to wafers. Examples 14 to 18 and Comparative Example 6 Wafer holding molded articles were prepared in the same manner as in Example 1 with the exception of using the compositions listed in Table 2. "C" in the table indicates that a very small amount of dust adhered to wafers. Example Com.Ex. 14 15 16 17 18 6 polyether ether ketone (PEEK) 70 70 70 70 70 70 silicon nitride whisker 30 aluminum borate whisker 30 basic magnesium 30 sulfate whisker magnesium oxide whisker 30 potassium titanate whisker 30 glass fiber 30 state of molded articles good good good good good good influence on wafer C C C C none B Examples 19 to 26 Wafer holding molded articles were prepared in the same manner as in Example 1 with the exception of using the compositions listed in Table 3. "Dentall WK200" is electrically conductive potassium titanate whiskers (product of Otsuka Kagaku K.K.). The surface resistance was measured by the method of JIS K6911. Example 19 20 21 22 23 24 25 26 PES 65 PEEK 65 PEK 65 PSF 65 PEI 65 PASF 65 HTA 65 PFA 65 Dentall WK200 35 35 35 35 35 35 35 35 surface resistance (Ω) 10 5 10 5 10 5 10 5 10 5 10 5 10 5 10 6 state of molding article molding article good good good good good good good good influence on wafer none none none none none none none none PES : Victrex PES 4100G (ICI) PEEK : Victrex PEEK 450G (ICI) PEK : Victrex PEK 220G (ICI) PSF : Udel Polysulfone P1700 (AMOCO) PEI : Polyetherimide Ultem 1000 (GE) PASF : Polyallylsulfone Radel A400 (UCC) HTA : High Temperature. Engineering Thermoplastic HTA 7600G (ICI) PFA : Fluorinated alkoxyetheylene resin (Mitsui Fluorochemicals Co., Ltd.) Example 27 and Comparative Examples 7 and 8 Wafer holding molded articles were prepared in the same manner as in Example 1 with the exception of using the compositions listed in Table 4. "Dentol BK200" is electrically conductive potassium titanate whiskers (product of Otsuka Kagaku K.K.). Wafers as placed in the basket were allowed to stand in a clean room for 3 months and checked for the fogging of the wafers with the unaided eye to determine the contamination of the wafers. The surface resistance was measured by the same method as above according to JIS K6911. The retentivity of the antistatic property was determined by repeating five times the step of immersing the molded article in a water bath for 30 minutes and thereafter allowing the article to stand at room temperature for 3 hours, and then measuring the surface resistance as a standard of durability. Example Comparative Example 27 7 8 polypropylene (1) 70 polypropylene (2) 70 polypropylene (3) 70 Dentall BK200 30 30 30 contamination no slightly fogging on of wafer fogging fogging whole surface retentivity of antistatic property excellent excellent excellent surface resistance (Ω) 10 5 10 5 10 5 Notes to Table 4 Polypropylene (1) contains 300 ppm of tetrakis[methylene-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate]methane and 500 ppm of tris(dinonylphenyl)phosphite as antioxidants or peroxide decomposing agents, and 400 ppm of calcium stearate as a hydrochloric acid absorbing agent. Polypropylene (2) contains 1000 ppm of tetrakis[methylene-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate]methane and 1000 ppm of tris(dinonylphenyl)phosphite as antioxidants or peroxide decomposing agents, and 1000 ppm of calcium stearate as a hydrochloric acid absorbing agent. Polypropylene (3) contains 500 ppm of tetrakis[methylene-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate]methane, 600 ppm of 2,6-di-tert-butyl-p-cresol and 900 ppm of dimyristylthio dipropionate as antioxidants or peroxide decomposing agents, and 1000 ppm of calcium stearate as a hydrochloric acid absorbing agent. Examples 28 to 33 and Comparative Example 9 The composition listed in Table 5 were molded by the same process as in Example 1 using the same wafer basket and storage case molds and checked for surface resistance and adhesion of dust. Example Com.Ex. 28 29 30 31 32 33 9 polypropylene (1) 90 80 70 60 80 70 100 Dentall BK200 10 20 30 40 - Dentall WK200 20 30 - surface resistance (Ω) 10 12 10 9 10 5 10 3 10 10 10 7 10 15 Industrial Applicability The present invention provides wafer holding molded articles, such as transport baskets, storage cases and carriers, for use in handling wafers and glass plates for liquid crystal televisions. These articles are useful for cleaning, drying, transporting or storing semiconductor wafers free of contamination.

Claims: A molded article for holding wafers which is made of a thermoplastic resin reinforced with whiskers, wherein the whiskers are electrically conductive potassium titanate whiskers selected from (a) those represented by the formula K 2 O.n(TiO 2-x ) wherein n is a real number of up to 8 and x is a real number smaller than 2; and having an average filament diameter of 0.01 to 1 µm, an average filament length of 1 to 100 µm and an aspect ratio of at least 10; and (b) those prepared by adhering or depositing a conductive or semi-conductive substance on the surface of potassium titanate whiskers having the formula K 2 O.mTiO 2 wherein m is a real number of up to 8; and having an average filament diameter of 0.01 to 1 µm, an average filament length of 1 to 100 µm and an aspect ratio of at least 10. A molded article for holding wafers as defined in claim 1 wherein the thermoplastic resin is at least one resin selected from among polyether ketone, polyether ether ketone, polyether sulfone, polyetherimide, polysulfone, polyallylsulfone, tetrafluoroethylene/perfluoroalkoxyethylene copolymer, tetrafluoroethylene/hexafluoropropylene copolymer, high-temperature amorphous resin and liquid crystal polymer. A molded article for holding wafers as defined in claim 1 wherein the thermoplastic resin is polypropylene, and the polypropylene has admixed therewith 10 to 1000 ppm of an antioxidant (or peroxide decomposing agent) and 200 to 500 ppm of a hydrochloric acid absorbing agent. A molded article for holding wafers as defined in claim 1 which is a wafer basket, storage case or carrier. The use of a molded article according to any one of claims 1 to 4 for cleaning, drying, transporting or storing wafers. The use of a molded article according to any one of claims 1 to 4 for cleaning, drying, transporting or storing glass plates for liquid crystal panels.

Inventors: NAKAMURA MORIHIKO, TABUCHI AKIRA, NAKAMURA, MORIHIKO, TABUCHI, AKIRA, NAKAMURA, MORIHIKO OTSUKA KAGAKU KABUSHIKI KAISHA, TABUCHI, AKIRA OTSUKA KAGAKU KABUSHIKI KAISHA
Applicants: OTSUKA KAGAKU KK, OTSUKA KAGAKU KABUSHIKI KAISHA
Application year: 1990
Main classification: H01L21
IPC codes: C08L23, C08K9, B65D85, C08K7, H01L21