Method of fabricating oxide superconducting film

Abstract: An oxide superconducting film is formed using laser deposition of applying an excimer laser beam (1, 21) onto a target (3, 23) through a converging lens (2, 22) and depositing atoms and/or molecules scattered from the target (3, 23) on the base material (5). The converging lens (2) is prepared by a cylindrical lens, or the converging lens (22) is moved, so that a portion (4, 25) irradiated with the laser beam (1, 21) on the target (3, 23) is linearized. Thus, it is possible to form an oxide superconducting film which is homogeneous over a region having a relatively large area on the base material (5) not only in film thickness but also in property.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a method of fabricating an oxide superconducting film, and more particularly, it relates to a method of fabricating an oxide superconducting film using laser deposition. Description of the Background Art In order to prepare an available conductor material from an oxide superconductive material, an oxide superconducting film may be formed on a base material. While various methods have been proposed for forming such oxide superconducting films on base materials, high critical density values are obtained with respect to the oxide superconducting films by vapor phase methods such as sputtering, vacuum deposition, deposition using a laser, CVD, and the like. Within these methods, the deposition using a laser, i.e., laser deposition is particularly suitable for fabrication of an oxide superconducting film having high critical current density, because of a high speed of film formation and capability of film formation in a high-pressure atmosphere. In relation to such laser deposition, further, an excimer laser is particularly advantageously employable for fabricating an oxide superconducting film, which exhibits excellent superconducting properties. In fact, oxide superconducting films having high critical current density have been successfully formed using the excimer laser. In a conventional method of forming an oxide superconducting film using an excimer laser, the laser beam has been applied through a spherical lens to form a spot on a target. In other words, only an extremely limited region of the target has been irradiated with the laser beam. Consequently, deposition particles are scattered from the target only in a limited range, to restrict the area of the oxide superconducting film homogeneously formed on a base material, which is opposed to the target, not only in film thickness but also in property. In Appl. Phys. Lett. 52 (12) , 21 March 1988, NY, USA, pp. 1008 - 1010 , S. Miura et al. and Nuclear Instrum. & Methods in Phys. Res. B39, NL, No. 1 - 4, March 1989, pp. 640 - 643, O. Eryu et al., respectively, there is disclosed the deposition of an oxide superconducting film on a base material by applying a laser beam which is scanned across a target. In Appl. Phys. Lett. 52 (12) , 21 March 1988, NY, USA, pp. 1008 - 1010 , S. Miura et al. , the scanning is achieved by mirrors whereas in Nuclear Instrum. & Methods in Phys. Res. B39, NL, No. 1 - 4, March 1989, pp. 640 - 643, O. Eryu et al. , the scanning is achieved by a movable lens. Different kind of light sources are known in the art for generating laser beams which are appropriate to be used for laser deposition techniques. From Appl. Phys. Lett. 53 (16), 17.10.88, NY, USA, pp. 1557-59, B. Roas et al. it is known to use an excimer laser for the deposition of an oxide superconducting film on a base material. The described method comprises the use of a convex lens to focus the laser beam on the target. In view of the above, it is the object of the present invention to provide an improved method of fabricating an oxide superconducting film, which enables the formation of an oxide superconducting film on a base material having a relatively large area, the film being homogeneous not only in film thickness but also in property. This object is solved by a method as defined in claim 1. The present invention is characterized in that the target is irradiated with a rectangularly shaped laser beam being "linearized", i.e. the laser beam is not focused by a conventional lens as in the prior art but by a cylindrical lens. According to the present invention, a long flexible base material is advantageously employed as the base material. Such a flexible base material is formed of a ceramic material such as stabilized zirconia, alumina, yttria, silica or titania, or a metal material such as platinum, gold, silver, aluminum, nickel, hastelloy, inconel, incoloy or stainless steel. According to the present invention, an excimer laser beam is preferably used as light source for the rectangular shaped laser beam. Therefore, an area of the target for scattering atoms and/or molecules in the vapor phase is increased, whereby it is possible to increase the area of an oxide superconducting film homogeneously deposited on the base material not only in film thickness but also in property. Thus, the present invention can be effectively applied to formation of an oxide superconducting film over a relatively wide range, or to formation of an oxide superconducting film on a long base material. According to the present invention, it is possible to obtain an oxide superconducting wire rod which is applied to a superconducting coil, a superconducting cable or the like, for example, by using a long flexible base material. These and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is an enlarged perspective view showing a part of an optical system included in a laser deposition film forming apparatus for carrying out an embodiment of the present invention; Fig. 2 is a front elevational view schematically showing the laser deposition film forming apparatus including the optical system shown in Fig. 1; Fig. 3 is a plan view showing a base material employed in Example 1, based on the embodiment shown in Fig. 1, and reference example 1; Fig. 4 is a front elevational view corresponding to Fig. 2, schematically illustrating a laser deposition film forming apparatus employed for carrying out reference example 1; DESCRIPTION OF THE PREFERRED EMBODIMENTS Fig. 1 is an enlarged view showing a part of an optical system which is provided in a laser deposition film forming apparatus employed for carrying out an embodiment of the present invention. Fig. 2 schematically shows the laser deposition film forming apparatus having the optical system partially shown in Fig. 1. Referring to Fig. 1, an excimer laser beam 1, for example, emitted from a laser beam source (not shown) is converged by a cylindrical lens 2 and applied onto a target 3. The excimer laser beam 1 is emitted to the exterior as a beam having a rectangular section, due to its principle of generation. When the excimer laser beam 1 passes through the cylindrical lens 2, its sectional configuration is linearized to define a linear irradiated portion 4 on the target 3, as shown in Fig. 1. The cylindrical lens 2 is formed by that of 10 mm by 30 mm, for example, in Fig. 1. Referring to Fig. 2, the laser beam 1 converged through the cylindrical lens 2 is applied onto the target 3, so that a locus 6 of atoms and/or molecules scattered from the target 3, i.e., deposition particles, is provided toward a base material 5, as shown by broken lines. Such a locus 6 of the deposition particles extends over a relatively wide region toward the base material 5. Example 1 The laser deposition film forming apparatus described above with reference to Figs. 1 and 2 was employed to form a film under film forming conditions listed in Table 1. Fig. 3 shows a plate of polycrystalline YSZ (yttria stabilized zirconia) of 10 mm x 50 mm, which was employed as the base material. This base material was divided into five regions A, B, C, D and E as shown in Fig. 3, in order to examine properties of an oxide superconducting film deposited thereon. Table 2 shows critical temperature T C measured on the respective regions. Reference Example 1 Fig. 4 is a diagram corresponding to Fig. 2, showing a laser deposition film forming apparatus employed for carrying out reference example 1. An excimer laser beam 11 is converged by a spherical lens 12, and applied onto a target 13. A portion 14 of the target 13 irradiated with the laser beam 11 is limited in a narrow region. Thus, a locus 16 of deposition particles from the target 13 toward a base material 15 is also limited in a narrow range. The laser deposition film forming apparatus shown in Fig. 4 was employed to form an oxide superconducting film on a base material having the dimensions and configuration shown in Fig. 3, under the film forming conditions listed in Table 1. Table 3 shows critical temperatures T C measured on portions A, B, C, D and E of this base material. Comparing Table 2 according to Example 1 with Table 3 according to reference example 1, it is understood that an oxide superconducting film having homogeneous superconducting properties over a wide area has been obtained according to the present invention. In order to linearize the portion of the target irradiated with the laser beam according to the present invention, the sectional configuration of the laser beam applied onto the target is linearized. In the method, a cylindrical lens is employed in order to linearize the sectional configuration of the laser beam. Although the base material has been prepared from stabilized zirconia in each Example, a base material of another ceramic material such as alumina, yttria, silica or titania, or a metal material such as platinum, gold, silver, aluminum, nickel, hastelloy registered trademarks, inconel registered trademarks, incoloy registered trademarks or stainless steel may be employed to attain an effect substantially similar to that attained with the base material of stabilized zirconia.

Claims: A method of depositing an oxide superconducting film on a base material (5), comprising the steps of a) generating a laser beam (1); b) directing said laser beam (1) through a converging lens (2) onto a target (3) of an oxide superconductive material; c) subjecting said base material (5) to the atoms and/or molecules scattered from said target (3) in response to the incident laser beam (1); characterized in that d) said laser beam has a rectangular cross section, and in that e) said converging lens (2) is a cylindrical lens being employed to focus the rectangular laser beam (1) in one dimension so that its sectional configuration is linearized to define a linear irradiated portion (4) on the target (3). The method of depositing an oxide superconducting film on a base material (5) in accordance with claim 1, wherein a long flexible base material is employed as said base material (5). The method of depositing an oxide superconducting film on a base material (5) in accordance with claim 2, wherein said flexible base material is formed of a ceramic material selected from the group of stablilized zirconia, alumina, yttria, silica and titania, or of a metal material selected from the group of platinum, gold, silver, aluminum, nickel, hastelloy, inconel, incoloy and stainless steel.

Inventors: HAYASHI NORIKI C O OSAKA WORKS, YOSHIDA NORIYUKI C O OSAKA WOR, HAYASHI, NORIKI, C/O OSAKA WORKS, YOSHIDA, NORIYUKI, C/O OSAKA WORKS
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1990
Main classification: H01L39
IPC codes: H01L39, C23C14