Superconducting thin film of compound oxide and process for preparing the same

Abstract: A superconducting thin film of Bi-containing compound oxide deposited on a substrate, a buffer layer made of Bi₂O₃ being interposed between the superconducting thin film and the substrate.

Description: Background of the Invention Field of the invention The present invention relates to a superconducting thin film of compound oxide and a process for preparing the same. More particularly, it relates to an improved superconducting thin film of Bi-containing compound oxide deposited on a substrate and a process for preparing the same. Description of the related art When oxide superconductors are utilized in electronics devices or the like, it is indispensable to prepare their thin films. Thin films of the compound oxides deposited on single crystal substrates of oxides such as SrTiO₃, MgO or the like exhibits relatively higher superconducting property because of the following reasons: Firstly, bad influence of diffusion or migration of elements of which the substrate is made is relatively lower, although such diffusion or migration of substrate elements is inevitable when the compound oxides are deposited on substrates. Secondly, it is rather easy to prepare well-oriented or well-ordered thin films of polycrystals or single crystals of superconducting compound oxides when these compound oxides are deposited on predetermined planes of such single crystal substrates of SrTiO₃, MgO or the like. In fact, so-called epitaxial growth is rather easily realized when the thin films of compound oxides are deposited on such single crystal substrates of SrTiO₃, MgO or the like, so that the superconducting thin films deposited on these substrates become single crystals or polycrystals which have very well ordered crystalline structure and show improved superconducting property. Still more, anisotropy of the superconducting property which is inherent in these compound oxide superconductors can be controlled. Film formation of these oxide superconductors is effected usually by physical vapour deposition technique such as sputtering, ion-plating and chemical vapour deposition technique such as MO-CVD. However, oxide superconductor thin films prepared by known processes are difficultly applicable to electronics devices because their surfaces are not smooth. Such surface unevenness of superconductor thin film may be caused by influence of surface roughness of the substrates and by mismatch of lattice constants between substrate crystal and superconductor crystal. Namely, the surface of the single crystal substrate of oxide is not smooth in the atomic level. In fact, even if the surface of the single crystal substrate of oxide is polished completely, its diffraction pattern observed by a relative high-energy electron diffraction analyzer (RHEED) is a spotty pattern but is not streaky pattern which reflect surface smoothness. The mismatch of lattice constants between substrate crystal and superconductor crystal is another cause of surface unevenness because a stress in the thin film which can be absorbed at an early stage of film formation is released when the thin film becomes thicker. U.S. patent No. 4,837,609 proposes to insert a layer of W, Mo or Ta between a superconducting compound oxide layer and a silicon single crystal substrate. Japanese patent laid-open No. 63-239,840 proposes to oxidize a copper substrate to form a CuO layer thereon and then a superconducting compound oxide layer is deposited on the CuO layer. These prior arts, however, neither describes not mentions surface smoothness of the superconducting thin films. Therefore, an object of the present invention is to solve the problems of known processes and to provide an improved oxide superconductor thin film having a smooth surface. Summary of the Invention The present invention provides a superconducting thin film of Bi-containing compound oxide deposited on a substrate, characterized in that a buffer layer made of Bi₂O₃ is interposed between the superconducting thin film and the substrate. The Bi-containing compound oxide can be any known compound oxide containing bismuth. Followings are examples thereof: (1) Bi₂Sr₂Ca n-1 Cu n O x in which "n" and "x" are numbers each satisfying a range of 1 ≦ n ≦ 6 and 6 ≦ x ≦ 16 (2) Bi₄(Sr 1-x ,Ca x ) m Cu n O p+y in which "x", "m", "n", "p" and "y" are numbers each satisfying a range of 6 ≦ m ≦ 10, 4 ≦ n ≦ 8 0 < x < 1 and -2 ≦ y ≦ + 2, respectively and p = (6+m+n). In this system, following compositions are preferable: (i) 7 ≦ m ≦ 9, 5 ≦ n ≦ 7 0.4 < x < 0.6 (ii) 6 ≦ m ≦ 7, 4 ≦ n ≦ 5 0.2 < x < 0.4 (iii) 9 ≦ m ≦ 10, 7 ≦ n ≦ 8 0.5 < x < 0.7 (3) Bi 2-y Pb y Sr₂Ca n-1 Cu n O x in which "y", "n" and "x" are numbers each satisfying a range of 0.1 ≦ y ≦ 1, 1 ≦ n ≦ 6 and 6 ≦ x ≦ 16 respectively. These Bi-containing compound oxides are preferably of a single crystal. Thickness of these Bi-containing compound oxides is not limited to a special value but is preferably in the order of 10 nm (100 Å) to 1 µm. The substrate is preferably a single crystal substrate of oxide such as MgO, SrTiO₃ and YSZ in order to facilitate epitaxial growth of the buffer layer of Bi₂O₃ and/or of the superconducting thin film. The other substrates which can be used in the present invention include single crystals of LaGaO₃, NdGaO₃ and LaAlO₃. The film forming plane depends to the substrate used. In the case of single crystal substrates of MgO and SrTiO₃, their {100} plane and {110} plane are preferably used. An essence of the present invention resides in that a buffer layer made of Bi₂O₃ is interposed between the superconducting thin film and the substrate. The buffer layer made of Bi₂O₃ is preferably of single crystal. Thickness of this buffer layer of Bi₂O₃ is preferably between 1 nm to 100 nm (10 Å to 1,000 Å), more preferably between 1 nm to 10 nm (10 Å to 100 Å). If the thickness of this buffer layer is not thicker than 1 nm (10 Å), satisfactory advantage of the present invention can not be obtained. To the contrary, if the thickness of this buffer layer exceeds 100 nm (1,000 Å), crystallinity of Bi₂O₃ in the thin film become disordered and result in that a bad influence is given to the superconducting thin film. The best crystallinity of Bi₂O₃ buffer layer is realized in a range of thickness between 1 nm to 100 nm (10 Å to 1,000 Å) and a better advantage of the present invention is obtained in this range. The Bi₂O₃ buffer layer according to the present invention functions to absorb unevenness of surface roughness of the substrate and to absorb the difference in lattice constant of crystals between the compound oxide superconductor and the substrate. And hence, the superconducting thin films of compound oxides according to the present invention have smooth surfaces which are advantageously applicable to electronics devices. In fact, following points are mentioned as advantages of the present inventions: (1) In the superconductors of Bi-containing compound oxides characterized by their stratified crystal structures, it is known that diffusion or migration of elements between adjacent layers of Ba-O is very small or reduced. This means that the thin film of Bi₂O₃ buffer layer which exists beneath a surface of the Bi-containing compound oxide layer will not change stoichiometry in the superconducting thin film because of the reduced diffusion or migration. (2) It is relatively easy to realize epitaxial growth of the Bi₂O₃ thin film on the single crystal substrate. In fact, the surface of the thin films of Bi₂O₃ deposited on the single crystal substrates are so smooth that their diffraction pattern observed by a reflective high-energy electron diffraction analyzer (RHEED) show streaky patterns. (3) The lattice constant of Bi₂O₃ crystal is very similar to that of Bi-containing oxide superconductor such as Bi₂Sr₂Ca n-1 Cu n O x or the like and hence epitaxial growth of the Bi-containing oxide superconductor on the Bi₂O₃ thin film is facilitated. Both of the Bi₂O₃ buffer layer and the superconducting Bi-containing compound oxide layer can be prepared by any one of known conventional thin film forming techniques including physical vapour deposition such as molecular beam epitaxial growth (MBE), sputtering, ion-beam sputtering, and ion-plating and chemical vapour deposition (CVD). In practice, a thin film of Bi₂O₃ is firstly deposited on a substrate in a vacuum chamber, and then a desired superconducting thin film of Bi-containing compound oxide is deposited on the thin film of Bi₂O₃ in the same vacuum chamber. Since both of the Bi₂O₃ and the Bi-containing compound oxide are oxides, it is necessary to supply oxygen in addition to metal elements of which the Bi-containing compound oxide is made during the film forming stage. The oxygen gas is supplied directly in the neighborhood of a surface of the substrate while the metal elements are fed in a form of vapors from evaporation source(s). Of course, an oxide or oxides of constituent elements of the Bi-containing compound oxide can be evaporated directly from evaporation source(s). Or, any combination of these operation modes can be used. The oxygen is preferably activated by micro-wave radiation before use. Ozone may be used in place of oxygen. It is also effective to produce activated oxygen by creating a plasma discharge by means of high-frequency in a vacuum chamber. Film forming conditions of the Bi-containing compound oxides are known and can be used in the process according to the present invention. Examples of film forming conditions of the Bi₂O₃ buffer layer are shown below but the scope of the present invention should not be limited thereto. Examples of Film Forming conditions of Bi₂O₃ buffer layer The superconducting thin films according to the present invention possess very smooth surfaces and hence improved superconducting properties, so that they can be utilized advantageously in applications of Matisoo switching elements. Annaker memories, Josephson device, a variety of sensors of Superconducting Quantum Interference Device (SQUID) or the like. Brief Description of the drawings FIG. 1 illustrates an apparatus for depositing thin films of Bi₂O₃ and of oxide superconductor on a substrate which can be used in the process according to the present invention. Fig. 2 is a RHEED pattern of a thin film of Bi₂Sr₂Ca n-1 Cu n O x which was grown to a thickness of 50 nm (500 Å) in an example according to the present invention. Now, the present invention will be described with reference to Examples, but the scope of the invention should not be limited to the Examples. Example 1 A superconducting thin film of compound oxide according to the present invention of Bi₂Sr₂Ca₂Cu₃O x was deposited on a {100} plane of a MgO single crystal substrate by a molecular beam epitaxy (MBE) unit illustrated in Fig. 1. The MBE unit shown in Fig. 1 comprises a chamber 1 interior of which is evacuated to very high vacuum, a plurality of Kunudsen Cells (K-cells) 2 each of which can control a temperature of a vapour source 10 placed therein, a plurality of shutters 8 for controlling the amount or timing of each vapour source 10, a substrate holder 3 provided with a heater 4 for heating a substrate 5, and an oxygen gas supply pipe 6 through which oxygen excited by microwave discharge supplied from a microwave source 7. At first, a thin film of Bi₂O₃ was deposited on the {100} plane of a MgO single crystal substrate under the following conditions: The resulting thin film of Bi₂O₃ was observed by a RHEED analyzer to showed a streaky pattern which revealed that the Bi₂O₃ thin film is an epitaxially grown film of good quality. Then, a thin film of Bi₂Sr₂Ca₂Cu₃O x was deposited on the Bi₂O₃ thin film in the same chamber as above under the following conditions: Fig. 2 is a diffraction patter of the resulting superconducting thin film observed by a RHEED analyzer. The diffraction patter is so streaky that it reveals such a fact that the superconducting thin film is a single crystal having a smooth surface. As a comparison, another thin film of Bi₂Sr₂CaCu₃O x was deposited directly on a {100} plane of a MgO substrate under the same condition as above without the Bi₂O₃ buffer layer. The superconducting properties of the resulting superconducting thin films according to the present invention and of the comparative example were determined. The results are summarized in the following table. It was confirmed that the superconducting thin film of Bi-containing compound oxide shows higher critical temperature and higher critical current density than those that are obtained by the comparative example. Example 2 Example 1 was repeated but conditions were modified as following: At first, a thin film of Bi₂O₃ was deposited on a {100} plane of a SrTiO₃ single crystal substrate under the following conditions: The resulting thin film of Bi₂O₃ was an epitaxially grown film of the same high quality as Example 1. Then, a thin film of Bi₂Sr₂Ca₂Cu₃O x was deposited on the Bi₂O₃ thin film in the same chamber as above under the following conditions: The resulting superconducting thin film was a very smooth film which shows a streaky pattern. The critical temperature (Tc) and the critical current density (Jc) are as follows:

Claims: A superconducting thin film of Bi-containing compound oxide deposited on a substrate, characterized in that a buffer layer made of Bi₂O₃ is interposed between said superconducting thin film and said substrate. The superconducting thin film set forth in Claim 1 wherein said buffer layer of Bi₂O₃ has a thickness between 1 nm and 100 nm (10 Å and 1,000 Å). The superconducting thin film set forth in Claim 2 wherein said buffer layer of Bi₂O₃ has a thickness between 1 nm and 10 nm (10 Å and 100 Å). The superconducting thin film set forth in any one of Claim 1 to 3 wherein said superconducting thin film of Bi-containing compound oxide has a composition represented by the formula: Bi₄(Sr 1-x ,Ca x ) m Cu n O p+y in which "x", "m", "n", "p", and "y" are numbers each satisfying a range of 6 ≦ m ≦ 10, 4 ≦ n ≦ 8, 0 < x < 1 and 2 ≦ y ≦ +2 respectively and p = (6+m+n). The superconducting thin film set forth in any one of Claim 1 to 4 wherein said substrate is of a single crystal of an oxide. The superconducting thin film set forth in Claim 5 wherein said substrate is a single crystal of an oxide selected from the group comprising MgO, SrTiO₃ and YSZ. A process for preparing a superconducting thin film of Bi-containing compound oxide deposited on a substrate, comprising forming a thin film of Bi₂O₃ on said substrate in a vacuum chamber by a deposition method, and then forming said superconducting thin film of Bi-containing compound oxide on said thin film of Bi₂O₃ in the same vacuum chamber by a deposition method. The process set forth in Claim 7 wherein said deposition method is vacuum deposition method. The process set forth in Claim 7 or 8 wherein metal elements which are the constituent elements of said Bi-containing compound oxide are evaporated from vapour sources while oxygen is supplied directly in the neighborhood of said substrate. The process set forth in any one of Claim 7 to 9 wherein said thin film of Bi₂O₃ has a thickness between 1 nm and 100 nm (10 Å and 1,000 Å). The process set forth in any one of Claim 7 to 10 wherein said superconducting thin film of Bi-containing compound oxide has a composition represented by the formula: Bi₄(Sr 1-x ,Ca x ) m Cu n O p+y in which "x", "m", "n", "p" and "y" are numbers each satisfying a range of 6 ≦ m ≦ 10, 4 ≦ n ≦ 8, 0 < x < 1 and 2 ≦ y ≦ +2 respectively and p = (6+m+n). The process set forth in any one of Claim 7 to 11 wherein said substrate is of a single crystal of an oxide. The process set forth in Claim 12 wherein said substrate is a single crystal of an oxide selected from the group comprising MgO, SrTiO₃ and YSZ.

Inventors: HARADA KEIZO, ITOZAKI HIDEO, HARADA, KEIZO, ITOZAKI, HIDEO
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1990
Main classification: H01L39
IPC codes: C01G29, H01B12, C01G1, C04B41, H01B13, H01L39