SURFACE-COATED HARD MEMBER FOR CUTTING AND ABRASION-RESISTANT TOOLS

Abstract: A surface-coated superhard member for a cutting or abrasion-resistant tool, wherein a coating is disposed on the surface of a parent metal for the tool so as to improve the abrasion resistance thereof. This member comprises a parent metal and, superimposed on the surface thereof, a hard coating having a thickness of 0.5 to 10 µm and comprising at least one member selected from among a carbide, a nitride and a carbonitride of M 1-x Al x (wherein 0 ≦ x ≦ 0.5), the M to Al ratio of which is continuously or stepwise changed from M (wherein M represents Ti, Zr or Hf) at the interface of the parent metal and the coating to MAl at the surface of the coating opposite to the parent metal. This structure effectively utilizes the characteristic properties of metals M and Al.

Description: Technical Field of The Invention This invention relates to a surface-coated hard material for cutting tools or wear resistance tools, in which a coating layer is provided on the surface of a base material of a cutting tool or wear resistance tool to improve the wear reistance. Technical Background Up to the present time, cutting tools and wear resistance tools have generally been composed of cemented carbides based on tungsten carbide (WC), various cermets based on titanium carbide (TiC), steels such as high-speed steels or hard alloys and ceramics based on silicon carbide and silicon nitride. In order to improve the wear resistnace of the cutting tools or wear resistance tools, a surface-coated hard material has been developed and has lately been put to practical use, in which one or more layers of carbides, nitrides or carbonitrides of Ti, Hf or Zr or oxide of Al are formed, as hard coating layers, on the surface of the hard material by a PVD method or CVD method. In particular, the hard coating layer formed by the PVD method is capable of improving the wear resistnce without deteriorating the strength of the base material and accordingly, it is suitable for a cutting use requiring a strength, for example, throwaway inserts for drills, end mills, milling cutters, etc. However, the PVD method is favorably comapred with the CVD method in respect of that the hard coating layer can be formed without deteriorating the strength of the substrate, but in the PVD method, it is difficult to stably form an oxide of Al and accordingly, a hard coating layer consisting of Al oxide formed by the PVD method has not been put to practical use. On the other hand, in the hard coating layer consisting of carbides, nitrides or carbonitrides of Ti, Hf or Zr formed by the present PVD method, the wear resistance cannot be said sufficient and in the high speed cutting, in particular, cutting tools or wear resistance tools thereof have shortened lives because of poor wear resistance. EP-A-0284854 discloses nitride coatings for tool members, the nitride containing at least two metals, for example Ti and Al in which the concentration of Al is changed within a range of from 5 to 60 weight percent continuously in a step-wise manner (i.e. non-linearly). Under the situation, the present invention has been made for the purpose of providing a surface-coated hard material for a cutting tool or wear resistance tool having more excellent wear reisistance than that of the prior art with maintaining the substrate strength of the cutting tool or wear resistance tool, in particular, exhibiting excellent wear resistance in the high speed cutting. Disclosure of The Invention In order to achieve the above described object, in the surface-coated hard material of the present invention, there is provided (1) a coating layer having such a functional gradient composition that the composition is changed continuously and non-step-wise from TiN of the boundary with the substrate to TiAlN of the outer surface at the opposite side to the substrate on the surface of a cutting tool or wear resistance tool. (2) a hard coating layer having a thickness of 0.5 to 10 µm and consisting of at least one member selected from the group consisting of carbides, nitrides and carbonitrides of Zr 1-x Al x (0 ≦ x ≦ 0.5) such that the composition ratio of Zr and Al is changed continuously and non-step-wise from Zr of the boundary with the substrate to ZrAl of the outer surface at the opposite side to the substrate on the surface of a cutting tool or wear resistance tool, and (3) a hard coating layer having a thickness of 0.5 to 10 µm and consisting of at least one member selected from the group consisting of carbides, nitrides and carbonitrides of Hf 1-x Al x (0 ≦ x ≦ 0.5) such that the composition ratio of Hf and Al is changed continuously and non-step-wise from Hf of the boundary with the substrate to HfAl of the outer surface at the opposite side to the substrate on the surface of a cutting tool or wear resistance tool. That is, the present invention provides a surface-coated hard material for a cutting tool or wear resistance tool characterized by providing a hard coating layer having a thickness of 0.5 to 10 µm and consisting of at least one member selected from the group consisting of carbides, nitrides and carbonitrides of M 1-x Al x (M represents Ti, Zr or Hf and 0 ≦ x ≦ 0.5) such that the composition ratio of M and Al is changed continuously and non-step-wise from M of the boundary with the substrate to MAl of the outer surface at the opposite side to the substrate on the surface of a cutting tool or wear resistance tool. The hard coating layer can be provided on the whole surface of a cutting tool or wear resistance tool or only the surface of an edge part. Formation of the hard coating layer can be carried out in known manner, but the PVD method such as sputting methods, ion plating methods, etc. is preferable in respect of that the substrate strength can readily be maintained. In the present invention, the hard coating layer is composed of at least one of carbides, nitrides and carbonitrides of M 1-x Al x (0 ≦ x ≦ 0.5) such that the composition ratio of M and Al is gradient from the boundary with the substrate to the surface opposite to the substrate. That is, the concentration of Al is increased continuously and non-step-wise from the boundary with the substrate to the surface of the hard coating layer in such a manner that x = 0 at the boundary with the substrate and x = 0.5 at the surface opposite to the substrate in the above described formula. Since the boundary with the substrate is composed of a carbide, nitride or carbonitride of M, in particular, excellent in bonding strength, the hard coating layer is very excellent in stripping resistance. At the same time, the surface of the hard coating layer is composed of a carbide, nitride or carbonitride of MAl more excellent in wear resistance as well as melt adhesion resistance, so that it is capable of maintaining an excellent cutting property for a long period of time as a cutting tool or wear resistance tool. Furthermore, it is found that in the surface-coated hard material provided with the above described hard coating layer, as a cutting tool or wear resistance tool, a very small amount of Al₂O₃ having a very high hardness at a high temperature is formed in the hard coating layer and accordingly, the tool exhibits a good wear resistance even in the high speed cutting. The above described functional gradient composition of the hard coating layer is changed continuously and non-step-wise. The layer thickness of the hard coating layer is in the range of 0.5 to 10 µm, since if less than 0.5 µm, the wear resistance is hardly improved, while if more than 10 µm, the breaking resistance is lowered. In the above described formula, M 1-x Al x , the upper limit of x should be 0.5 since increase of Al in the hard coating layer to exceed x = 0.5 results in lowering of the hardness of the whole coating layer. Examples The present invention will now be illustrated in greater detail by Examples and Comparative Examples. Example 1 Using a cutting insert made of a cemented carbdie with a composition of JIS standard P 30 (specifically, WC-20 wt % TiC-10 wt % Co) and a form of JIS SNG 432 as a substrate, the surface thereof was coated with each of coating layers having functional gradient compositions as shown in the following Table 2 by an ion plating method using vacuum arc discharge, as described below. Namely, the above described cutting insert and Al and Ti as a target were arranged in a film making apparatus, in which the insert was then maintained in an Ar gas atmosphere with a vacuum degree of 1.3Pa (1 x 10 ⁻² torr) rinsed by applying a voltage of -2000 V and heated at 500°C, after which the Ar gas was exhausted. While introducing one or both of N₂ gas and CH₄ gas at a rate of 300 cc/min into the film making apparatus, the Ti target was evaporated and ionized by vacuum arc discharge to coat the surface of the cutting insert with a carbide, nitride or carbonitride of Ti. Furthermore, various hard coating layers were formed by evaporating and ionizing the Ti target and simultaneously the Al target and controlling the composition ratio of Ti and Al so that the Al concentration was continuously increased non-step-wise and the composition on the surface was a carbide, nitride or carbonitride of TiAl. For comparison, the surface of a cutting insert with the same composition and same form as described above was coated with the coating layers of carbide, nitride or carbonitride of Ti by an ion plating method using the same film-making apparatus and vacuum arc discharge as described above thereby obtaining samples of surface-coated cutting inserts of the prior art as shown in Table 2. In addition, samples of coated cutting inserts were prepared in which coating layers of carbide of Ti, etc. shown in Table 2 were formed on the surface of the cutting insert with the sane composition and sane form by ordinary CVD method. Each of the samples of the surface-coated cutting inserts prepared as described above was subjected to a continuous cutting test and intermittent cutting test under conditions as shown in Table 1 to measure the flank wear width of the edge, thus obtaining resuts as shown in Table 3. Continuous Cutting Test Intermittent Cutting Test Workpiece SCM 435 SCM 435 Cutting Speed 220 m/min 220 m/min Feed 0.37 mm/rev 0.30 mm/rev Cutting Depth 2.0 mm 1.5 mm Cutting Time 15 min 20 min Sample No. Flank Wear Width (mm) Continuous Cutting Intermittent Cutting 1 0.130 0.100 2 0.120 0.110 3 0.115 0.110 4 0.110 0.105 5 0.120 0.110 6 0.115 0.120 7 0.110 0.115 8 0.300 0.210 9 0.205 0.180 10 0.410 0.250 11 0.205 broken 12 0.110 broken It is apparent from the above described results that the samples of the coated cutting inserts of the present invention have both an excellent wear resistance and breakage resistance, i.e. more excellent cutting performance than the comaprative samples in both the continuous cutting and intermittent cutting tests. Example 2 Using a cutting insert made of a cemented carbdie with a composition of JIS standard P 30 (specifically, WC-20 wt % TiC-10 wt % Co) and a form of JIS SNG 432 as a substrate, the surface thereof was coated with each of hard coating layers as shown in the following Table 4 by an ion platingmethod using vacuum arc discharge, as described below, to obtain a sample of surface-coated cutting insert of the present invention. Namely, the above described cutting insert and Al and Zr as a target were arranged in a film making apparatus, in which the insert was then maintained in an Ar gas atmosphere with a vacuum degree of 1.3Pa (1 x 10 ⁻² torr) rinsed by applying a voltage of -2000 V and heated at 500°C, after which the Ar gas was exhausted. While introducing one or both of N₂ gas and CH₄ gas at a rate of 300 cc/min into the film making apparatus, the Zr target was evaporated and ionized by vacuum arc discharge to coat the surface of the cutting insert with a carbide, nitride or carbonitride of Zr. Subsequently, various hard coating layers were formed by evaporating and ionizing the Al target and controlling the composition ratio of Zr and Al so that the Al concentration was continuously increased non-step-wise and the composition on the surface was a carbide, nitride or carbonitride of ZrAl. Each of the samples of the surface-coated cutting inserts prepared as described above was subjected to a continuous cutting test and intermittent cutting test under conditions as shown in Table 1 to measure the flank wear width of the edge, thus obtaining resuts as shown in Table 5. Sample No. Flank Wear Width (mm) Continuous Cutting Intermittent Cutting 13 0.128 0.101 14 0.118 0.114 15 0.125 0.105 16 0.108 0.098 17 0.112 0.100 18 0.105 0.098 19 0.110 0.105 20 0.115 0.110 21 0.105 0.102 It is apparent from the above described results that of the samples of the surface-coated cutting inserts of the prior art, Sample Nos. 8-10 whose hard coating layers were formed by the PVD method were inferior in wear resistance and Sample Nos. 11 nd 12 whose hard layers were formed by the CVD method exhibited lowering of the breakage resistance due to deterioration of the toughness of the substrate, while Sample Nose 13-21 of the surface-coated cutting inserts according to the present invention showed more excellent wear resistance in both the continuous cutting and intermittent cutting tests and since the hard coating layer was formed by the PVD method, the toughness of the substrate was maintained resulting in more excellent breakage resistance. Example 3 Using a cutting insert made of a cemented carbdie with a composition of JIS standard P 30 (specifically, WC-20 wt % TiC-10 wt % Co) and a form of JIS SNG 432 as a substrate, the surface thereof was coated with each of hard coating layers as shown in the following Table 6 by an ion platingmethod using vacuum arc discharge, as described below, to obtain Sample Nos. 22 to 30 of the surface-coated cutting inserts of the present invention. Namely, the above described cutting insert and Al and Hf as a target were arranged in a film making apparatus, in which the insert was then maintained in an Ar gas atmosphere with a vacuum degree of 1.3Pa (1 x 10 ⁻² torr) rinsed by applying a voltage of -2000 V and heated at 500°C, after which the Ar gas was exhausted. While introducing one or both of N₂ gas and CH₄ gas at a rate of 300 cc/min into the film making apparatus, the Hf target was evaporated and ionized by vacuum arc discharge to coat the surface of the cutting insert with a carbide; nitride or carbonitride of Hf. Subsequently, various hard coating layers were formed by evaporating and ionizing the Al target and controlling the composition ratio of Hf and Al so that the Al concentration was continuously increased non-step-wise and the composition on the surface was a carbide, nitride or carbonitride of HfAl. Each of the samples of the surface-coated cutting inserts prepared as described above was subjected to a continuous cutting test and intermittent cutting test under conditions as shown in Table 1 to measure the flank wear width of the edge, thus obtaining resuts as shown in Table 7. Sample No. Flank Wear Width (mm) Continuous Cutting Intermittent Cutting 22 0.131 0.095 23 0.129 0.092 24 0.125 0.090 25 0.120 0.092 26 0.122 0.090 27 0.118 0.085 28 0.120 0.090 29 0.117 0.085 30 0.119 0.087 It is apparent from the above described results that of the samples of the surface-coated cutting inserts of the prior art, Sample Nos. 8-10 whose hard coating layers were formed by the PVD method were inferior in wear resistance and Sample Nos. 11 nd 12 whose hard layers were formed by the CVD method exhibited lowering of the breakage resistance due to deterioration of the toughness of the substrate, while Sample Nos. 22-30 of the surface-coated cutting inserts according to the present invention showed more excellent wear resistance in both the continuous cutting and intermittent cutting tests and since the hard coating layer was formed by the PVD method, the toughness of the substrate was maintained resulting in more excellent breakage resistance. Utility and Possibility According to the present invention, there can be provided a surface-coated hard material for a cutting tool or wear resistance tool having more excellent wear reisistance than that of the prior art with maintaining the substrate strength of the cutting tool or wear resistance tool, in particular, being capable of maintaining good cutting performances, as a cutting tool or wear resistance tool, for a long period of time even in the high speed cutting.

Claims: A surface-coated hard material for a cutting tool or wear resistance tool characterized by providing a hard coating layer having a thickness of 0.5 to 10 µ and consisting of at least one member selected from the group consisting of carbides, nitrides and carbonitrides of M 1-X Al X (M represents Ti, Zr or Hf and 0 ≦ x ≦ 0.5) such that the composition ratio of M and Al is changed continuously from M of the boundary with the substrate to MAl of the outer surface at the opposite side to the substrate on the surface of a cutting tool or wear resistance tool, provided that the continuous composition change is non-step-wise. A surface-coated hard material as claimed in claim 1 which is applied to the whole surface of a cutting tool or wear resistance tool. A surface-coated hard material as claimed in claim 1 which is applied to an edge only of a cutting tool or wear resistance tool.

Inventors: NOMURA TOSHIO ITAMI WORKS OF S, OMORI NAOYA ITAMI WORKS OF SUM, TOBIOKA MASAAKI ITAMI WORKS OF, YAMAGATA KAZUO ITAMI WORKS OF, NOMURA, TOSHIO ITAMI WORKS OF SUMITOMO ELECTRIC, OMORI, NAOYA ITAMI WORKS OF SUMITOMO ELECTRIC, TOBIOKA, MASAAKI ITAMI WORKS OF SUMITOMO ELECTRIC, YAMAGATA, KAZUO ITAMI WORKS OF SUMITOMO ELECTRIC
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1990
Main classification: C23C14
IPC codes: C23C30, C23C14