Process for the production of gelatin from fish skins

Abstract: A process for the production of gelatin from fish skins comprises the steps of: (a) cleaning the skins in order to remove therefrom substantially all superfluous material; (b) treating with dilute aqueous alkali; (c) washing with water until the washing water is substantially neutral; (d) treating with dilute aqueous mineral acid; (e) washing with water until the washing water is substantially neutral; (f) treating with dilute aqueous citric acid and/or another suitable organic acid; (g) washing with water until the washing water is substantially neutral; and (h) extracting with water at elevated temperatures not above about 55 o C, the washed citric/other organic acid-­ treated skins. In practice, the present process employs much lower temperatures than known heretofore for the treatment steps, which results in a high quality product (e.g. absence of a fishy smell), compared with the prior art.

Description: The present invention relates to a process for the production of gelatin from fish skins. Gelatin is a water-soluble proteinaceous substance which finds extensive use in the food, pharmaceutical and photographic industries. It is derived from the breakdown of collagen, a substance of similar composition which is however insoluble, the source of the collagen being preponderantly animal bones, hide pieces and porkskins. Reference is made in this last connection to US-A-2,024,683 which issued in December 1935. It has been known for many years that gelatin may also be obtained from fish waste, e.g. from fish skins and other fish offal. Since such waste is available in large quantities from fish canning operations, it would appear to be potentially useful to use it for gelatin production, provided that a technically and economically viable process of manufacture could be found. Part of the technical difficulty concerns the elimination of the unpleasant smell often associated with fish products. It is surprising that, so far as is known to the authors, gelatin from fish waste sources has not found widespread application in the food industry, up to the present time. Looking at the matter from a different aspect, it may be appreciated that in addition to the fact that a cheap source material exists, it is yet a further advantage of the process of the invention that its product will be acceptable to large segments of the population which, whether for religious, health or merely aesthetic reasons would want to avoid eating products derived from the higher animals. This means that the product of the present process, insofar as it may be applied to the manufacture of food products, will have a potential market larger than that derived from animal wastes. Kernot and Speer (D. S. I. R. 2nd report of the Adhesives Research Committee, 1926, pages 23-33, see also GB 235635), reviewed and investigated the production of fish glues and gelatins. By way of introduction, it may be mentioned that a superior product may be made by heating isinglass with water, isinglass being the washed and dried inner layer of the sound or swim bladder of certain fish; the product is of course very expensive owing to the restricted nature of its source material. Moving away from this specialized source, the article states that two-thirds of the available gelatin (presumably that contained in fish skins) is extracted by heating with water at a temperature not exceeding 60°C, but where the fat glands are abundant it is essential to remove the fat by a preliminary treatment. The peculiar odor of fish skins is stated to be due to basic nitrogenous compounds and fats containing large percentages of unsaturated acids. In the process disclosed in the article, macerated fish skins (or less preferably, other fish offal) are subjected to the successive steps of washing with water, treatment with dilute alkali, treatment with a weak acid (such as sulfurous acid), and again washing with water, prior to digestion with water at about 60°C. Subsequently the extraction liquors are concentrated and allowed to set, the resulting jellies being cut into cakes and dried. The residues remaining after the extraction are dried in the usual way to prepare meal. The treatment with dilute alkali and with weak acid are each preferably effected by maceration of the skins for 18 to 24 hours, i.e. for 36-48 hours in total. In US-A-2,024,683 to which reference has already been made herein, it is acknowledged that by careful control of the acid absorbed by the skins being treated, primarily pig-skins, the acid being used in the later stages of washing the skins, hydrolysis of collagen to gelatin takes place very rapidly, while secondary hydrolysis of the gelatin is avoided, thereby yielding a high quality gelatin. The acid treatment depends on use of an organic acid as such or simultaneously in combination with inorganic acid. It is an object of the present invention to provide a process for the production from fish skins, of gelatin having a consistently higher quality than that produced from the same source in the prior art. There is thus provided in accordance with the present invention a prqcess for the production from fish skins of a gelatin having odour, clarity and Bloan number such as to render it suitable for human consumption, which comprises the steps of: (a) cleaning the skins in order to remove therefrom substantially all superfluous material; (b) treating the cleaned skins with dilute aqueous alkali; (c) washing the alkali-treated skins with water until the washing water is substantially neutral; (d) treating the thus-neutralized skins with dilute aqueous mineral acid; (e) washing the mineral acid-treated skins with water until the washing water is substantially neutral; (f) treating the thus-neutralized skins with dilute aqueous organic acid comprising at least one member selected from ascorbic, citric, fumaric. malic, succinic and tartaric acids, and other organic acids which are acceptable in food processing and which do not possess or impart an offensive odor; (g) washing the organic acid-treated skins with water until the washing water is substantially neutral; and (h) extracting with water at elevated temperatures not above 55°C, and preferably at a temperature within the range of 40 to 50°C, the washed organic acid-treated skins. This procedure yields an aqueous solution of gelatin and water may be removed from this solution to obtain gelatin in the solid state. Citric acid is the preferred organic acid for use in step (f). Although the present invention will be described hereinafter primarily with reference to the use of citric acid, it is emphasised that the present invention is not limited to the use thereof to the exclusion of any of the other organic acids identified in step (f). The superfluous material referred to in step (a) means fat, flesh, bones, scale and so forth. Step (a) may be carried out, for example, by washing with excess water, conveniently under pressure. Prior to step (b), the fish skins are optionally macerated or cut into pieces, though this is not essential. In step (b), the alkali is conveniently sodium hydroxide, but potassium hydroxide, sodium carbonate or potassium carbonate could also be used. The use of a mineral acid in step (d) may be regarded as somewhat surprising, since Kernot and Speer ( loc cit ) use the weak acid sulfurous acid, and imply that use of a mineral acid such as HCl is likely to give a glue rather than gelatin. In the present process, the presently preferred mineral acid is sulfuric acid, but may alternatively be e.g. HCl. According to the invention, there is included a citric acid treatment step (f), in addition to the mineral acid treatment step. While the reason for the efficacy of citric acid is not known, it has been found by the inventors to be more efficient in giving a high quality product, than when using mineral acid only. It is believed that other organic acids which are acceptable in food processing and which do not possess or impart an offensive odor, such as for example ascorbic, fumaric, malic, succinic and tartaric acids, could be substituted for at least part of the citric acid in step (f) of the present process. The washing steps (c), (e) and (g) are carried out in the manner well known in the art, the washings being tested for neutrality and the washing steps being terminated when neutrality is established. Compared with the prior art, the present invention employs much lower temperatures for the treatment steps, which besides being economical in terms of energy, result in a high quality product. Although Kernot and Speer ( loc cit ) claim that if care is taken, their method can result in "an almost pure gelatin ... entirely free from taste or odor", the inventors have found that carryirations according to their instructions invariably resulted in a poor quality product with a strong fishy smell. Thus, in accordance with the present invention, it is preferred that steps (a) to (g) are each effected at ambient temperature ±10°C, desirably at a temperature within the range of from 15 to 27° C, while step (h) is preferably effected at a temperature within the range of from 40 to 50°C. As regards the concentrations of the treatment agents in steps (b) and (d), the respective treatments may, e.g., be effected using aqueous alkali and mineral acid having concentrations thereof within the range of from 0.05 to 0.3% wt./vol. In step (f), there may, e.g., be used aqueous citric acid having a concentration thereof within the range of from 0.5 to 6.0% wt./vol. If desired, after washing step (g) and prior to extracting step (h), the skins may be washed with distilled water or substantially ion-free water, in order to remove any residual salts. The removal of water in optional step (i) may be carried out by any means known to the art, e.g. by simple evaporation, either at near ambient or at elevated temperatures, or by blowing air over the solution, or by freeze-drying. It is presently contemplated that fish skins derived from any commercially available fish could be used in the present process, the main consideration being availability. However, the presently preferred fish skins are those from Tilapia . The process of the invention will now be illustrated by a non-limiting Example. The illustrative Example will be followed by a number of Comparative Experiments It should be noted that Bloom number is an indication of the strength of gels produced. The higher the Bloom number, the stronger the gel. EXAMPLE 50 g. of skins from Tilapia were thoroughly cleaned with excess water to remove superfluous material, and then soaked in 3 x 700 ml. 0.2% (wt./vol.) aqueous sodium hydroxide solution, each soaking 40 minutes, total alkali treatment 2 hours. The alkali-treated skins were washed with water until the washings had pH about 7, and were then soaked in 3 x 700 ml. 0.2% (wt./vol.) aqueous sulfuric acid solution, each soaking 40 minutes, total mineral acid treatment 2 hours. The mineral acid-treated skins were washed with water until the washings had pH about 7, and were then soaked in 3 x 700 ml. 1.0% (wt./vol.) aqueous citric acid solution, each soaking 40 minutes, total citric acid treatment 2 hours. The citric acid-treated skins were washed with water until the washings had pH about 7, and were then subjected to a final wash with distilled water to remove any residual salts. The thus-treated skins were placed in a vessel containing distilled water controlled at a temperature within the range of 40-50°C. Following overnight extraction in this manner, the mixture was filtered, centrifuged and then lyophilized until a powder was obtained; the yield was about 7.5 g. A 5% solution was found to have a similar gelling capacity as a similar solution of a commercial gelatin derived from animal sources and marketed in Israel under the trade name "Ardi". The product of this Example was found to have the following properties. APPEARANCE: Excellent, water white, light textured material. ODOR: Bland to very slight amine odor. CLARITY: Excellent. BLOOM (g. ): 263 (determined by a modified procedure due to small quantity, but considered accurate). VISCOSITY (MP): 51.0 (determined at 6 2/3% and 60°C, standard Davis Gelatine Test Method). ASH (%): 0. pH: 3.77. pI: 7.38. The following Table compares the amino acid distribution (expressed as wt.%) in the protein content of gelatin obtained in accordance with the present invention, with gelatin obtained from pigskin. Among the evident differences between the two cases, the greater hydroxyproline content of the gelatin of the present invention may be particularly noted. COMPARATIVE EXPERIMENT A The method of Kernot and Speer ( loc cit ) was employed, using 24 hour incubations with alkali and acid, and extraction at 60-80°C. The product had a Bloom value of 63 or less and a strong fishy odor. COMPARATIVE EXPERIMENT B Repeating the conditions of the above Example, except that the extraction was carried out at above 55°C, resulted in a product having a Bloom value of less than 60. COMPARATIVE EXPERIMENT C Repeating the conditions of the above Example, except that the citric acid step was omitted and substituted by absorption on silica, hydroxyapatite or DEAE-cellulose, in an attempt to remove the odor, resulted in a product having a low Bloom value, and from which the odor had not been removed. COMPARATIVE EXPERIMENT D Repeating the conditions of the above Example, except that the citric acid step was omitted and substituted by extraction with 1:1 paraffins:benzene, resulted in a product from which the odor had been almost entirely removed, but in which the Bloom value had undesirably decreased. In summary thus, this invention provides a process for the production from fish skins of gelatin having a consistently higher quality than that produced from the same source in the prior art. This process has the advantage of not being energy intensive and being particularly economically viable by having a series of stages each of which is not unduly protracted. A particular further advantage is that the invention provides a gelatin product which will be suitable for consumers who wish to avoid bovine and/or porcine gelatins which are commonly available at the present time.

Claims: A process for the production from fish skins of gelatin having odour, clarity and Bloan number such as to render it suitable for human consumption, which comprises the steps of: (a) cleaning the skins in order to remove therefrom substantially all superfluous material; (b) treating the cleaned skins with dilute aqueous alkali; (c) washing the alkali-treated skins with water until the washing water is substantially neutral; (d) treating the thus-neutralized skins with dilute aqueous mineral acid; (e) washing the mineral acid-treated skins with water until the washing water is substantially neutral; (f) treating the thus-neutralized skins with dilute aqueous organic acid comprising at least one member selected from ascorbic, citric, fumaric, malic, succinic and tartaric acids, and other organic acids which are acceptable in food processing and which do not possess or impart an offensive odor; (g) washing the organic acid-treated skins with water until the washing water is substantially neutral; and (h) extracting with water at elevated temperatures not above 55°C, and preferably at a temperature within the range of from 40 to 50°C, the washed organic acid-treated skins. A process according to claim 1, wherein said steps (a) to (g) are each effected out at ambient temperature ±10°C, preferably at a temperature within the range of from 15 to 27°C. A process according to either claim 1 or claim 2, wherein in steps (b) and (d), the respective treatments are effected using aqueous alkali and mineral acid having concentrations thereof within the range of from 0.05 to 0.3% wt./vol. A process according to any of the preceding claims, wherein in step (f), there is used aqueous citric acid. A process according to claim 4, wherein the citric acid has a concentration within the range of from 0.5 to 6.0% wt./vol. A process according to any of the preceding claims, wherein the alkali is sodium hydroxide and the mineral acid is sulfuric acid. A process according to any of the preceding claims, wherein prior to step (b), the fish skins are macerated or cut into pieces. A process according to any of the preceding claims, wherein after washing step (g) and prior to extracting step (h), the skins are washed with distilled water or substantially ion-free water, in order to remove any residual salts. A process according to any of the preceding claims, wherein following step (h), the water is removed from the thus produced aqueous gelatin solution, to obtain gelatin in the solid state.

Inventors: BERGMAN MARGALIT, GROSSMAN SHLOMO, BERGMAN, MARGALIT, GROSSMAN, SHLOMO
Applicants: UNIV BAR ILAN, BAR ILAN UNIVERSITY
Application year: 1990
Main classification: C09H3
IPC codes: A23J1, C09H3, C07K14, C07K1