Filled thermoplastic resin compositions having an interpenetrating phase forming a three-dimensional network structure and melt-blending methods for forming the same

Abstract: Melt-blended filled thermoplastic resin compositions include a thermoplastic matrix resin, a filler material and a thermoplastic additive resin. The compositions of the invention include discreet continuous phases of matrix resin (A) and additive resin (C), with the filler material (B) being present substantially entirely within the the additive resin phase (i.e. substantially absent from the matrix resin phase). The components A, B and C are selected so that their respective surface tensions allow the additive resin to form a complex three-dimensional network structure within the matrix resin when melt-blended, and such that substantially all of the filler material is homogeneously dispersed throughout the three-dimensional network structure.

Description: The present invention generally relates to melt-blended thermoplastic resin compositions which include a filler material (ie "filled" resin compositions). More specifically, the present invention relates to filled thermoplastic resin compositions in which a thermoplastic resin additive forms an interpenetrating network structure within a thermoplastic matrix resin, whereby the filler is homogeneously dispersed throughout the network structure. The present invention is also directed to methods of forming thermoplastic interpenetrating network structures homogeneously within a thermoplastic matrix resin using melt-blending techniques. It is known that high-molecular weight thermoplastic polymers have been used as matrix resins and may be modified (eg to improve and/or impart desired physical properties to the polymers) by incorporating other additive materials thereinto. Representative examples of additive materials that have been incorporated into thermoplastic matrix resin include non-thermoplastic fillers (eg so as to reinforce the polymer) and thermoplastic additive resins (eg so as to modify the heat resistance, impact resistance, chemical resistance and/or surface gloss characteristics of the matrix resin). Furthermore, attempts have been made in the past to enhance the blending efficiency and/or homogeneity of resulting melt-blended resin compositions. For example, various techniques such as compatibilization, dynamic vulcanization and reaction extrusion have been proposed with a view towards enhancing the manner in which resin components may be blended with one another so as to achieve desired property modifications. In order to obtain various desired effects, thermoplastic additive resins have typically been incorporated into matrix resins in relatively large amounts so as to improve thermal and mechanical properties. Among previous proposals for multi-phase resin compositions is that described in European Patent Specification No EP 0 268 280 A2 which claims a thermoplastic resin composition comprising following components (1), (2) and (3), wherein component (2) forms a continuous phase, component (1) forms a continuous phase intermingled with component (2) or forms a dispersed phase in component (2),and component (3) is dispersed in component (1), at least a part of component (3) having a continuous structure: Component (1) from 5 to 65% by weight of an amorphous polymer having a glass transition temperature of at least 90°C Component (2) from 20 to 92% by weight of a crystalline polymer showing at least partially crystalline property and having a melting point of at least 100°C Component (3) from 3 to 50% by weight a rubber-like polymer having a storage shear modulus at room temperature of 5 × 10⁸ dyne/cm² or less all weight % being based on the weight of the thermoplastic resin composition. In the specific Examples given in that specification, the rubber-like component (3) is dispersed within the amorphous component (1) in network or partially continuous form, however, the amorphous component (1) is dispersed within the crystalline component (2) in particulate or only partially continuous form. However, using thermoplastic additive resins in large amounts can adversely affect other desired physical properties. Attempts have therefore been made to improve the mechanical properties of matrix resins through formation of an interpenetrating three-dimensional network structure using lesser amounts of additive resin. However, in order to form a three-dimensional network, it has typically been necessary to employ specialized and relatively complex processing techniques. For example, three-dimensional networks of an additive resin in a matrix resin have been formed by simultaneously polymerizing the matrix resin monomer and the additive monomer. Similarly, preliminary polymerization of one of the matrix or additive resin monomers to a desired extent followed by polymerization of both monomer components or chemical reaction utilizing a functional group has been employed. Thus for example, European Patent Application No EP 0 104 106 A3 teaches the principle of loading one of two polymers with a particulate so that during blending of the two polymers they have similar rheological properties. In fact, that application claims a thermoplastic polymer blend having at least a first thermoplastic resin (b) having a determinable viscosity at a blending temperature blended with at least one dissimilar polymer constituent (A) to form an interpenetrating polymer network with said first thermoplastic resin (B) and dissimilar polymer constituent (A) characterized by: at least polymer dissimilar from said first thermoplastic resin; and a predetermined quantity of a particulate loaded into said at least one dissimilar polymer to impart to said at least one dissimilar polymer a non-Newtonian rheological behaviour, said at least one dissimilar polymer loaded with said particulate having a viscosity approximately equal to the determinable viscosity of said first thermoplastic resin at said blending temperature. The present invention is, however, directed towards a rather different problem, namely that of providing a simple and efficacious way of ensuring a stable structure in which filler material is confined to one of two continuous interpenetrating polymer phases. According to the invention there is provided a melt-blended resin composition comprising a thermoplastic matrix resin (A), a filler material (B) and a thermoplastic additive resin (C) dispersed in the thermoplastic matrix resin (A), characterised in that the thermoplastic matrix resin (A) is a polyacetal, the filler material (B) is selected from organic and inorganic compounds and the thermoplastic additive resin (C) exhibits a surface tension value during melt-blending that is intermediate between the surface tension values respectively exhibited by the thermoplastic matrix resin (A) and filler material (B), whereby the thermoplastic additive resin (C) is embedded within the matrix resin in regions interconnected by means of fibrils, rivulets or the like and the filler (B) is homogeneously dispersed within the thermoplastic additive resin (C). The invention also provides a method of making such a resin composition and thus extends to a method of making a thermoplastic resin composition comprising melt-blending a thermoplastic matrix resin (A), a filler material (B) and a thermoplastic additive resin (C) dispersed in the thermoplastic matrix resin (A), characterised in that the thermoplastic matrix resin (A) is a polyacetal, the filler material (B) is selected from organic and inorganic compounds and the thermoplastic additive resin (C) exhibits a surface tension value during melt-blending that is intermediate between the surface tension values respectively exhibited by the thermoplastic matrix resin (A) and filler material (B), whereby the thermoplastic additive resin (C) is embedded within the matrix resin in regions interconnected by means of fibrils, rivulets or the like and the filler (B) is homogeneously dispersed within the thermoplastic additive resin (C). As a result of the interpenetrating three-dimensional network that is formed, the thermoplastic additive (C) and filler (B) may be employed in lesser quantities as compared to melt-blended filled thermoplastic compositions of the prior art while achieving comparable (and usually improved) property enhancements. Thus, the problems typically associated with incorporating relatively large amounts of additive resin within a matrix resin as described briefly above have been alleviated (if not minimized) according to the present invention. The present invention more specifically relates to forming a melt-blended filled thermoplastic resin composition by selecting the thermoplastic matrix resin and the filler material such that one exhibits a higher surface tension during melt blending as compared to the other. On the other hand, the thermoplastic additive is selected such that it exhibits a surface tension during melt-blending that is an intermediate value between the higher and lower surface tension values of the thermoplastic matrix resin and the filler. In other words, the surface tension values γ A , γ B , γ C during melt-blending of the thermoplastic matrix resin (A), the filler material (B), and the thermoplastic additive (C), respectively, are each selected so as to satisfy the relationships: γ A < γ C < γ B ; or γ A > γ C > γ B . Further aspects and advantages of the invention are discussed in the following detailed description thereof, with particular reference to the accompanying drawings wherein like reference numerals denote like elements and wherein: FIGURES 1(a) and 1(b) are schematic cross-sectional and perspective views, respectively, showing a typical particulate dispersion of a thermoplastic additive within a thermoplastic matrix resin according to the prior art; FIGURES 2(a) and 2(b) are schematic cross-sectional and perspective views, respectively, showing a typical particulate dispersion of a thermoplastic additive and filler component within a thermoplastic matrix resins according to the present invention; FIGURE 3 is an optical microphotograph showing the particulate structure of a molded article formed of the resin composition described in the following Example 1; FIGURE 4 is an optical microphotograph of a molded article formed of the resin composition described in the following Example 1; and FIGURE 5 is a scanning electron microscope image showing the interpenetrating continuous phase of the thermoplastic additive within a thermoplastic matrix resin for the composition of the following Example 1. The accompanying Figure 1 shows the particle dispersion morphology in a conventional polymer blend system. In this regard, it can be seen that the additive resin (component C) is dispersed in the form of discreet unconnected particles or islands in a sea of matrix resin (component A). The additive resin (C) is moreover, present in relatively low amounts (20% by weight based on the total composition weight). On the other hand, accompanying Figures 2(a) and 2(b) show schematically the morphology of the interpenetrating network structure according to the present invention. As can be seen, the filler material (component B) is essentially entirely encapsulated within the three-dimensional interconnected network formed by the thermoplastic additive resin (component C). Despite the relatively low content (eg 20 % by weight of the composition), the additive resin (C) forms a continuous phase within the the continuous phase of the matrix resin (component A). Thus, the resins together form a complex interpenetrating network structure in which the continuous phases of both the additive resin (C) and the matrix resin (A) are entangled with one another. As used herein and in the accompanying claims, the terms "network", "network structure", and like terms are each intended to refer to a melt-blended resin morphology having at least two continuous phases, whereby one phase is comprised of a thermoplastic matrix resin (A), and the other phase is comprised of embedded regions of a thermoplastic additive resin (C) within the matrix resin (A), which embedded regions are interconnected by means of fibrils, rivulets or the like of the additive resin (C). Thus, it will be appreciated that both phases will form an entangled three-dimensional network. The compositions of this invention are at least tertiary blends. That is, according to the present invention at least three components, namely a thermoplastic matrix resin (A), a filler material (B), and a thermoplastic additive resin (C) are melt-blended to disperse the additive resin (C) in the matrix resin (A) in such a manner that a complex three-dimensional network is formed, and in such a manner that the additive resin (C) encapsulates essentially all of the filler material (B). In this manner, the non-thermoplastic additive, i.e. the filler material (B), is dispersed homogeneously throughout the matrix resin (A) without physically being encapsulated or embedded thereby. In other words, the non-thermoplastic (filler) particles are interconnected with one another through the three-dimensional network formed by the additive resin (C). The present invention utilizes surface tension differences among the three components A, B and C (ie the thermoplastic matrix resin (A), the filler material (B) and the thermoplastic additive resin (C), respectively) so that the additive resin (C) encapsulates the filler material (B), and so that the filler material (B) is homogeneously dispersed throughout the additive resin (C) (i.e. is essentially absent from the matrix resin phase). Specifically, selection of the components A, B and C such that the surface tension of the component C is intermediate of the surface tensions of both components A and B (i.e. as described above) enables the particles of component B to be encapsulated by the three-dimensional network that is formed by the component C. It is believed that the phenomenon described above occurs due to the fact that the surface free energy of each component per unit volume is less in the state whereby the component C encapsulates the component B as compared to other states that the components may assume. As a result, the system will seek its most stable form -- ie, the component C will encapsulate component B. Thus, the mechanism whereby the component B is encapsulated by the component C is due to the surface tension differences of the components in the system. More specifically, when there is a difference in the surface tension between the components B and C, as described above, the system will assume a state whereby the component C encapsulates the component B so as to achieve the most stable form (ie, minimize the surface free energy). Even with minimal surface tension differences, the system will assume its most stable state wherein the component C encapsulates the component B when it is left to stand for prolonged time periods. However, in a commercial process, since the melt-blending time is limited and since there are a number of melt-blending techniques that could be employed, a significantly larger surface tension difference is preferred so that the system assumes the most stable state within a reasonably short time. In this regard, it is particularly preferred that the surface tension differences between the components A and C, and between the components B and C each be at least 2 mN/m or more [1 mN/m = 1 dyn/cm]. The filler material as component B can be virtually any fibrous, particulate or flaky inorganic or organic filler typically employed in engineering resins and may be selected independently of the compositions' intended end use applications and/or intended properties to be attained through the use of the filler. Specific examples of inorganic fibrous filler material (B) include fibres of glass, asbestos, silica, silica-alumina, zirconia, boron nitride, silicon nitride, boron and potassium titanate. Examples of particulate filler materials include silica, quartz powder, glass beads, milled glass fibre, glass balloons, glass powder, silicates such as calcium silicate, aluminum silicate, kaolin, talc, clay, diatomaceous earth and wollastonite, metallic oxides such as iron oxide, titanium oxide, zinc oxide, antimony trioxide and alumina, metal carbonates such as calcium carbonate and magnesium carbonate, metal sulphates such as calcium sulphate and barium sulphate, and other various materials such as ferrite, silicon carbide, silicon nitride and boron nitride. Examples of the flaky filler include mica and glass flake. These inorganic fillers may be used alone or in a combination of two or more of them. Examples of the organic filler materials include heat-resistant fibrous fillers, such as the fibres of aromatic polyesters, liquid crystal polymers, aromatic polyamides, and aromatic polyimides, and particulate fillers comprising thermoplastic resins, thermosetting resins or the like. Examples of particulate organic fillers include phenolic resins, polystyrene resins, acrylic resins, polyethylen resins, polyamide resins, fluororesins, melamine resins, polymethyl methacrylate resins, epoxy resins, olefin-acrylic acid copolymer resins or the like. These particulate organic filler materials may be used alone or in combination of two or more of the same. Although there is no particular limitation on the particle size of the filler materials (either organic or inorganic) that are employed, the mean particle diameter is preferably between 0.01 and 20µm so as to be more readily dispersed when melt-blended. The thermoplastic additive resin as the component C may be virtually any thermoplastic resin that can be selected for its surface tension properties (i.e. so as to form a three-dimensional network which encapsulates the filler material) and which imparts the desired property modification to the resulting composition. Thus, examples of the thermoplastic additive resin (C) include polyolefins, polyesters, polystyrene, polyvinyl chloride, polyamides, polycarbonates, ABS, polyphenylene oxide, polyphenylene sulphide, fluororesins, acrylic resins and thermoplastic polyurethane resins. Of course, since the surface tension of the additive resin (C) must be different from the surface tension of the matrix resin (A) as described above, these two resins cannot be identical to one another in that respect. There is no particular limitation on the blending ratio of the components A, B and C. However, when consideration is given to the object of the present invention (ie, the provision of a thermoplastic interpenetrating network structure having a low content of the component C), as the total amount of the components B and C is preferably 60% by weight or less, particularly 40% by weight or less based on the total weight of the components A, B and C. A large weight ratio of component C to component B is also preferred so as to ensure that the component B is essentially entirely encapsulated within component C. In this regard, the most desirable blending ratio is one falling within the weight ratio ranges specified by the following: (B+C)/(A+B+C) = between 0.03 and 0.6; and C/(B+C) = between 0.05 and 0.95 It is the surface tension of thermoplastic resins during melt-blending which is important for purposes of the present invention. For this reason, surface tensions of thermoplastic resins are evaluated by the well-known "pendant drop method" at the melt-blending temperature. The term "pendant drop method" used herein is intended to mean a method which comprises standing a tube upright, and determining the surface tension of a liquid placed in the tube based upon the shape of a droplet hanging down from the end of the tube. In the case of components which do not melt at the melt-blending temperature (eg filler materials), the critical surface tension as determined by the Zisman plot of the contact angle was used in the evaluation. In the present invention, the three components, ie components A, B and C may be melt-blended by customary methods which include melt kneading the thermoplastic matrix resin (A) with the thermoplastic additive resin (C) while simultaneously adding the filler component (B). That is, the present invention is especially significant in that a thermoplastic interpenetrating network structure can be formed using conventional melt-blending techniques and thus specialized methods and/or techniques associated with the prior art are unnecessary. It is desirable to conduct the melt-blending at melting temperatures for the thermoplastic components such that a shear force of at least 10 sec⁻¹ is imparted to the resin melt. The shear force is more preferably 10 to 1000 sec⁻¹ and usually will be between 50 and 500 sec⁻¹. Conventional additives known in the art, e.g. lubricants, nucleating agents, dyes and pigments, mold-release agents, antioxidants, heat stabilizers, weather (light) stabilizers, reinforcing agents, hydrolysis stabilizers, thermoplastic resins etc, may be incorporated into the thermoplastic interpenetrating network structure of the present invention for the purpose of imparting desired characteristics. According to the method of the present invention, since a thermoplastic interpenetrating network structure can conveniently be formed by blending the matrix resin (A) with a lesser amount of additive resin (C), it is possible to improve the properties of the matrix resin (A) without detriment to its other desirable properties. Various properties, such as mechanical, physical and chemical properties, can be improved depending upon the purpose of use of the thermoplastic interpenetrating network structure, which renders the present invention widely useful. The present invention will now be described in more detail by way of the following non-limiting Examples. Example 1 A polyacetal resin (Duration®; a product of Polyplastics Co Ltd), a thermoplastic polyurethane (adipate polyurethane; a product of Nippon Miractran Co Ltd) and acrylic rubber particles (particle diameter of 0.5µm; a product of Mitsubishi Rayon Co Ltd) respectively having surface tensions as specified in Table 1 were mixed with each other in proportions as specified in Table 1 and kneaded at a preset temperature of 190°C by means of a 30mm twin extruder at a screw rotational speed of 80 rpm (a shearing rate of 100 sec⁻¹) to pelletize the mixture. Subsequently, a tensile specimen was prepared from the pellets by using a molding machine manufactured by Nissei Plastic Industrial Co Ltd at a barrel temperature of 190°C and a mold temperature of 80°C, and the molding was evaluated. The results are given in Table 1. The following evaluation techniques were employed: (i) Surface Tension Measurements The surface tensions of each of the polyacetal resin and the thermoplastic resin polyurethane were measured according to the pendant drop method (a method described on pages 78 and 79 of "Shin Jikken Kagaku Koza", Vol 18,"Kaimen to Koroido", 1977, published by Maruzen Co Ltd) in an atmosphere of 190°C by making use of an automatic surface tensio-meter PD-Z manufactured by Kyowa Interface Science Co Ltd. The surface tensions of the polyacetal resin and the thermoplastic resin polyurethane were 21 mN/m and 36 mN/m, respectively. The surface tension of the acrylic rubber particles was measured by fabricating the particles into a film at 200°C by using a press and determining the critical surface tension and the temperature coefficient according to the contact angle method (a method described on pages 93 and 106 of "Shin Jikken Kagaku Koza" Vol 18 "Kaimen to Koroido" (1977) published by Maruzen Co Ltd) by making use of an automatic contact angle measuring apparatus CA-Z manufactured by Kyowa Interface Science Co Ltd. The results of the measurements were as follows. The value of the acrylic rubber particles at 190°C in terms of the surface tension was 38 mN/m. surface tension at 25°C: 47 mN/m surface tension at 60°C: 45 mN/m surface tension at 80°C: 44 mN/m temperature gradient (-dr/dT) = 0.05 (ii) Determining Presence of Interpenetrating Network Structure A molded piece having a size of 10 x 10 x 3mm was placed in a hydrochloric acid-methanol solution (32 N hydrochloric acid : methanol = 1 : 3 (vol)) and heated under reflux at 80°C for 12 hr to observe the morphological change with the naked eye and under an optical microscope and an electron microscope. Specifically, the matrix resin (A) comprising a polyacetal resin was decomposed with an acid and eluted, and the dispersion state was observed for the thermoplastic polyurethane and the acrylic rubber particle which will not bring about any morphological change under this condition. As with the prior art, if the thermoplastic polyurethane is dispersed in particulate form, the molded piece cannot retain its form and a (fine) particulate polyurethane is observed with the naked eye or under an optical microscope (see the optical microphotograph of Comparative Example 3 shown in Figure 3). By contrast, when the thermoplastic resin and the acrylic rubber assume a thermoplastic interpenetrating network structure according to the present invention, the molded piece retains its form and is observed with the naked eye or under an optical microscope (see optical microphotograph of example 1 shown in Figure 4). Further, the thermoplastic interpenetrating network structure can be more distinctly confirmed when the molded piece is observed in a magnified state under a scanning electron microscope (see an electron microphotograph of Example 1 shown in Figure 5). The morphology of the particulate dispersion and the thermoplastic interpenetrating network structure were quantitively evaluated by treating the molded piece by the above-described method, filtering the treated piece through a 12-mesh sieve to determine the oversize (% by weight). The portion of particulate dispersion passes through the sieve and does not remain on the sieve. The portion of the thermoplastic interpenetrating network structure however remains on the sieve. Therefore, the oversize (% by weight) refers to the weight of the (B+C) portion in the thermoplastic interpenetrating network structure. (iii) Mechanical Strength Measurement The Izod impact strength (notched) of the molded piece was measured according to ASTM D256, while the tensile strength and tensile elongation thereof were measured according to ASTM D638. Comparative Example 1 A molded piece was prepared and evaluated in the same manner as that of Example 1, except that no acrylic rubber particle was added and the amount of blending of the thermoplastic polyurethane was 20% by weight. The results of the evaluation are given in Table 1. Examples 2 and 3 and Comparative Examples 2 to 3 A molded piece was prepared and evaluated in the same manner as that of Example 1, except that particulate melamine resin (particle diameter 0.3 to 25µm; a product of Nippon Shokubai Kagaku Kogyo Co Ltd), calcium carbonate (particle diameter 5µm; a product of Toyo Fine Chemical Co Ltd), polydimethylsiloxane (particle diameter 1 to 15µm; a product of Toray Silicone Co Ltd) and polytetrafluoroethylene (particle diameter of 0.3µm; a product of Daikin Kogyo Co Ltd) were used instead of the acrylic rubber. The results are given in Table 1. Examples 4 to 9 and Comparative Examples 4 to 7 A molded piece was prepared and evaluated in the same manner as that of Example 1, except that a thermoplastic polyurethane was used as the thermoplastic compound C and the blending ratio was varied as specified in Table 2. The results are given in Table 2. We have previously referred to EP-A-0 104 106 which discloses a composition comprising an engineering resin such as an acetal resin (see page 6, line 3) and polymers such as silicone oil or ethylene vinyl acetate loaded with carbon black in the form of an interpenetrating network structure. In a product according to this invention, we lay no claim to the use as filler materials of carbon black or graphite (which we do not consider to be compounds), nor do we lay any claim to a product containing silicone oils or polydimethylsiloxane or ethylene vinyl acetate polymers as thermoplastic additive resins. Subject to the foregoing disclaimer, the present invention is defined in the following clams.

Claims: A melt-blended resin composition comprising a thermoplastic matrix resin (A), a filler material (B) and a thermoplastic additive resin (C) dispersed in the thermoplastic matrix resin (A), characterised in that the thermoplastic matrix resin (A) is a polyacetal, the filler material (B) is selected from organic and inorganic compounds and the thermoplastic additive resin (C) exhibits a surface tension value during melt-blending that is intermediate between the surface tension values respectively exhibited by the thermoplastic matrix resin (A) and filler material (B), whereby the thermoplastic additive resin (C) is embedded within the matrix resin in regions interconnected by means of fibrils, rivulets or the like and the filler (B) is homogeneously dispersed within the thermoplastic additive resin (C). A resin composition as claimed in claim 1, wherein the total weight of the filler material (B) and the thermoplastic additive resin (C) is not greater than 60%, based on the total weight of the components A, B and C. A resin composition as claimed in any claim 1 or claim 2, wherein the weight ratio of the total amount of the filler material (B) and the thermoplastic additive resin (C) to the total composition is between about 0.03 and about 0.60. A resin composition as claimed in any one of claims 1 to 3, wherein the weight ratio of the thermoplastic additive resin (C) to the total amount of the filler material (B) and the thermoplastic additive resin (C) is between about 0.05 and about 0.95. A resin composition as claimed in any preceding claim, wherein the filler material (B) is an inorganic filler selected from one or more of the group consisting of: particulate silica, quartz powder, glass beads, milled glass fibre, glass balloons, glass powder, calcium silicate, aluminium silicate, kaolin, talc, clay, diatomaceous earth, wollastonite, iron oxide, titanium oxide, zinc oxide, antimony trioxide, alumina, calcium carbonate, magnesium carbonate, calcium sulphate, barium sulphate, ferrite, silicon carbide, silicon nitride and boron nitride, mica flakes and glass flakes, fibres of glass, asbestos, silica, silica-alumina, zirconia, boron nitride, silicon nitride and potassium titanate. A resin composition as claimed in any preceding claim, wherein the filler material (B) is an organic filler selected from one or more of the group consisting of fibres of aromatic polyesters, liquid crystal polymers, aromatic polyamides, and aromatic polyimides, particulate phenolic resins, polystyrene resins, acrylic resins, polyethylene resins, polyamide resins, fluororesins, melamine resins, polymethyl methacrylate resins, epoxy resins and olefin-acrylic acid copolymer resins. A resin composition as claimed in any preceding claim, wherein the filler material (B) is a particulate organic filler selected from one or more of the group consisting of thermoplastic resins and thermosetting resins. A resin composition as claimed in any preceding claim, wherein the filler material (B) has a mean particle size of between 0.01 and 20 µm. A resin composition as claimed in any preceding claim, wherein the thermoplastic additive resin (C) is selected from the group consisting of polyolefins, polyesters, polystyrene, polyvinyl chloride, polyamides, polycarbonates, ABS, polyphenylene oxide, polyphenylene sulphide, fluororesins, acrylic resins and thermoplastic polyurethane resins. A method of making a thermoplastic resin composition comprising melt-blending a thermoplastic matrix resin (A), a filler material (B) and a thermoplastic additive resin (C) dispersed in the thermoplastic matrix resin (A), characterised in that the thermoplastic matrix resin (A) is a polyacetal, the filler material (B) is selected from organic and inorganic compounds and the thermoplastic additive resin (C) exhibits a surface tension value during melt-blending that is intermediate between the surface tension values respectively exhibited by the thermoplastic matrix resin (A) and filler material (B), whereby the thermoplastic additive resin (C) is embedded within the matrix resin in regions interconnected by means of fibrils, rivulets or the like and the filler (B) is homogeneously dispersed within the thermoplastic additive resin (C). A method as claimed in claim 10, wherein the surface tension value of the said thermoplastic additive resin (C) during melt-blending differs by at least 2.0 mN/m from the surface tension values of each of the said thermoplastic matrix resin (A) and the said filler material (B). A method as claimed in any claim 10 or 11, wherein the step of melt-blending is conducted at an elevated temperature such that a shearing force of at least 10 sec⁻¹ is imparted to the resin melt. A method as claimed in claim 12, wherein the shearing force is between 50 and 500 sec⁻¹.

Inventors: TAJIMA YOSHIHISA, YOKOUCHI MITSURU, TAJIMA,YOSHIHISA, YOKOUCHI, MITSURU
Applicants: POLYPLASTICS CO, POLYPLASTICS CO. LTD.
Application year: 1990
Main classification: C08L101
IPC codes: C08L23, C08L61, C08L59, C08J3, C08L83, C08L75, C08K3, C08L33, B29B7, C08L77, C08L63, C08L101, C08L27, B29K105, C08J5, C08L79, C08L67