Fluorine-containing alcoholbased dehydrating agent and method of drying articles

Abstract: The invention provides a dehydrating agent comprising at least one of fluorine-containing alcohols; a dehydrating agent comprising at least one of fluorine-­ containing alcohols and water; and a method of dehydrating and drying an article having a surface moistened with residual water, the method comprising immersing the article in a dehydrating agent comprising at least one of fluorine-containing alcohols or comprising at least one of fluorine-containing alcohols and water, and drying the article after the immersion.

Description: The present invention relates to a method of drying articles by dehydration using a new dehydrating agent. In the present specification, "percentages" are all by weight. In many cases, silicon wafers for production of semiconductors, plated articles, optical lenses, various metal parts and the like (hereinafter briefly referred to as "articles") are washed with water in the last stage or in a stage near the last stage of processing. The moisture remaining on the surfaces of these articles will cause the formation of stain-like spots and the occurrence of rust to exert a great influence on the performance of the articles. The dehydrating agents which have been heretofore widely used for effectively dehydrating the abovementioned articles are isopropanol, ethanol and like alcohols, trichlorotrifluoroethane and like chlorofluorohydrocarbons (hereinafter referred to as "CFCs") and the compositions prepared by mixing with, or by adding to, a CFC an alcohol, a surfactant and the like. However, isopropanol and ethanol which are highly flammable have the problem of entailing fire hazards in handling. CFC-based dehydrating agents are free of such problem. In recent years, however, it has been suggested that some kinds of CFCs, when released into the atmosphere, would deplete the stratospheric ozone layer, thereby inflicting a serious adverse influence on the ecosystem including humans on the earth. In view of this, a worldwide agreement has placed a restriction on consumption and production of the major ozone-depleting CFCs. GB-A-2 188 059 also discloses a solvent mixture of 1,1,1-trifluoroethanol with halogenated hydrocarbons. In this mixture the halogenated hydrocarbon poses the same problem of incurring a risk of ozone layer destruction. It is an object of the present invention to provide a novel dehydrating method which avoids the above deficiencies. The present invention provides therefore a method of dehydrating and drying an article having a surface moistened with residual water, the method comprising the steps of (i) immersing the article in a dehydrating agent consisting essentially of at least one fluorine-containing alcohol selected from the group consisting of tetrafluoropropanol and pentafluoropropanol, and (ii) drying the article after the immersion. According to the extensive research conducted by the present inventors, it has been revealed that a composition comprising a fluorine-containing alcohol alone or in combination with water is outstanding in the properties required of dehydrating agents useful for dehydrating articles. The fluorine-containing alcohols used in the method of the invention are, tetrafluoropropanol (hereinafter referred to as "4FP", boiling point of 107°C) and pentafluoropropanol (hereinafter called "5FP", boiling point of 81°C). These fluorine-containing alcohols can be used singly or are usable in mixture. When the dehydrating agent of the invention is used in the form of a composition formed from a fluorine-containing alcohol and water, the composition may contain water in an amount of about 20%, preferably about 10%, of the amount of the composition. The use of a dehydrating agent formed from a mixture having a water content of up to 10% can achieve an effective replacement with water present on the surface of the article. However, with the increasing water content of more than 10%, the dehydration agent used is deteriorated in the ability to achieve the replacement. Use of a dehydrating agent having a water content in excess of 20% fails to produce the desired effect. A mixture of 4FP and water ( 4FP/water = 72.5/27.5 ) and a mixture of 5FP and water ( 5FP/water = 94/6 ) both form azeotropic compositions and are therefore useful for effectively removing water. A mixture of 3FE and water is not an azeotropic composition but behaves as a composition similar to azeotropic composition. The dehydrating agent of the present invention may further contain a small quantity of a known stabilizer when so required. The dehydration and drying of articles using the dehydrating agent of the invention can be conducted in the same manner and with use of the same apparatus as in the method of dehydrating and drying articles using a CFC-based dehydrating agent or like known dehydrating agent. For this reason, the method and apparatus for dehydration are not specifically limited. An example thereof is schematically shown below in Fig. 1. In Fig. 1 which is a view in section showing an example of the apparatus for dehydration to be used in the method of the invention, an article (not shown) having a surface moistened with residual water is immersed in the dehydrating agent of the invention stored in the first sink 1 in which water is replaced with the fluorine-containing alcohol (In the following procedure, 5FP is used as such alcohol unless otherwise specified.) to dehydrate the article. In order to achieve a higher degree of dehydration of the article, the article treated by the immersion in the first sink 1 is fed to the second sink 2 in which the article was further immersed in the dehydrating agent of the invention. Since a dehydrating agent which is discharged from the first sink 1 and which substantially consists of 5FP alone with water present therein eliminated with use of a water separator 3 is fed to the second sink 2, a higher degree of dehydration level can be achieved. When it is necessary to further dehydrate the article to a greater extent, the article obtained after completion of the immersion in the second sink 2 is fed to vapor zone 4 above a sump 6 containing vaporized 5FP and provided with heating means 5 to bring the article into contact with the vapor of 5FP, whereby the dehydration of the article is further continued. Cooling pipes 7 which are provided above the vapor zone 4 condense the vapor of 5FP rising from the vapor zone and serve to return 5FP to the sump 6. The water separator 3 is not limited to a specific type and can be any of those capable of separating water from fluorine-containing alcohol. For example, when 5FP is used as a fluorine-containing alcohol, 5FP can be separated from water by utilizing the phenomenon that 5FP and water are readily separable at low temperatures up to about 15°C due to the difference in the solubility therebetween. Alternatively, the fluorine-containing alcohol and water can be separated by rectification. Further, the separation can be conducted by utilizing a technique for removing water using a specific membrane. Although Fig. 1 shows an example of dehydration of an article with use of an apparatus provided with two sinks and one sump, apparatuses useful in the present invention are not limited to this type. More specifically, the structure of the apparatus to be used is variable depending on the amount of residual water with which the surface of the article is moistened, the desired degree of dehydration of the article, degree of facility in dehydration of the article, etc. For example, usable apparatus may be provided with a single sink or sump, or provided with one sink and one sump. Moreover, dehydration can be performed also by spraying. The dehydration agent of the present invention is free of the problems of environmental disruption such as depletion of ozone layer and the like. Further, the dehydration agent of the invention has an excellent ability to remove residual water with which the surface of an article is moistened. Moreover, the use of 5FP as a fluorine-containing alcohol is particularly advantageous to handle because the dehydrating agent is made incombustible. The use of 3FE or 4FP is also very safe since these alcohols need a large quantity of energy to ignite and discharge small quantity of heat in combustion as compared with known dehydrating agents such as isopropanol, ethanol and the like. In comparison with isopropanol, ethanol and the like, the dehydrating agent of the invention can be readily separated from water when cooled to a low temperature. In addition, the solvent of the invention which is formed with azeotropic compositions or those similar to azeotropic composition is easy to control and, as a matter of course, entails little or no change in the ratio of the components used even when vaporized and condensed repeatedly for the purpose of recovery and repetitive use thereof. Given below are examples to clarify the features of the present invention in more detail. Example 1 A glass specimen (size: 50 mm x 50 mm x 5 mm) thoroughly washed beforehand and moistened with water was immersed in each of the dehydrating agents as shown below in Table 1 for a predetermined period of time, was placed into a dry Buchner funnel and was washed with a specific quantity of absolute methanol. The absolute methanol used was collected and analyzed by Karl Fischer's method to determine the amount of water therein. The amount of the water was taken as "A". The same procedure as above was repeated with the exception of not immersing the glass specimen in the dehydrating agent and not drying the specimen to determine the amount of water in the absolute methanol used. The amount of the water was taken as "B". Dehydration rate C (%) was determined according to the following equation. C = (B-A)/B x 100 (%) Table 2 below shows the results. The above procedures were all carried out at room temperature. Dehydrating agent No. Composition (%) 1 3FE 2 3FE/Water = 97/3 3 4FP 4 4FP/Water = 72.5/27.5 (azeotropic) 5 5FP 6 5FP/Water = 94/6 (azeotropic) 7 IPA 8 Ethanol Dehydrating agent No. 5 sec 10 sec 15 sec 20 sec 1 91 93 95 98 2 88 91 94 96 3 90 92 95 97 4 82 84 87 89 5 90 93 96 98 6 88 90 93 94 7 86 88 90 92 8 86 89 91 93 The dehydration test was conducted in the same manner as above with the exception of using a ceramic test piece. Table 3 below shows the results. Dehydrating agent No. 5 sec 10 sec 15 sec 20 sec 1 92 95 97 98 2 90 91 94 96 3 89 92 95 96 4 84 85 88 90 5 93 96 98 98 6 90 93 95 96 7 88 90 92 93 8 87 89 91 93 The results in Tables 2 and 3 reveal that the dehydrating agents 3 to 6 of the present invention are comparable to or superior to known dehydrating agents such as isopropanol and ethanol in the ability for dehydration.

Claims: A method of dehydrating and drying an article having a surface moistened with residual water, the method comprising the steps of (i) immersing the article in a dehydrating agent consisting essentially of at least one fluorine-containing alcohol selected from the group consisting of tetrafluoropropanol and pentafluoropropanol, and (ii) drying the article after the immersion. A method of dehydrating and drying an article having a surface moistened with residual water, the method comprising the steps of (i) immersing the article in a dehydrating agent consisting essentially of water and at least one fluorine-containing alcohol selected from the group consisting of tetrafluoropropanol and pentafluoropropanol, and (ii) drying the article after the immersion.

Inventors: HANATANI NAOYOSHI, NOGUCHI MASAHIRO, OMURE YUKIO, HANATANI, NAOYOSHI, NOGUCHI, MASAHIRO, OMURE, YUKIO
Applicants: DAIKIN IND LTD, DAIKIN INDUSTRIES, LIMITED
Application year: 1990
Main classification: B01D12
IPC codes: F26B5, C09K3, C11D7, B01D12