Curable norbornenyl functional silicone formulations

Abstract: A composition curable to a solid crosslinked polyorganosiloxane comprises: a) a norbornene functional silicone prepolymer having a plurality of groups of the formula: bound to silicon atoms thereof, where R is H or methyl, R¹ is a direct bond or -C(=O)O- and R⁴ is ethylene, ethenylene, propylene or propenylene, b) a coreactive silicone prepolymer selected from SiH functional silicones, and alkylthiol functional silicones, said polyorganosiloxanes (a) and (b) being present in an equivalent ratio of between 2:1 and 1:2 norbornene to silicon hydride or alkyl thiol groups, and c) an effective amount of a hydrosilation or thiolene cure catalyst, respectively.

Description: Background of the Invention Field of the Invention The invention of the present application pertains to silicone formulations utilizing particular norbornene functional silicone prepolymers which are cured by a hydrosilation reaction mechanism. Description of the Prior Art In Petrov, et al, Zhurnal Obschei Khimii, 31 , 1199 (1961), there is a description of the hydrosilation of various norbornene compounds, one of which is vinyl norbornene. The vinyl norbornene reaction was run at 30°C using trichlorosilane. The authors of this reference report that a mixture of products was obtained, the addition taking place at the both the internal double bond of the norbornene ring and at the vinyl group in approximately similar proportions: In various references, Watanabe et al, describe hydrosilation reactions of 5-ethylidenebicycylo (2,2,1)hept-2-ene: This hydrosilation is only reported to produce addition on the norbornene ring double bond. See for instance U.S. 4,599,440; 4,623,741; 4,625,043; and 4,640,968. These reaction products were used to make siloxane monomers for vulcanization to yield silicone elastomers. From the Petrov et al and Watanabe et al, references persons skilled in the art would conclude that it is not possible to selectively hydrosilate norbornene derivatives containing other unsaturated sites because the norbornene unsaturation itself is reactive under hydrosilation conditions. WO 88/02902 discloses a curable composition of a polythiol and a polyene in which the polythiol is a compound or resin defined by the formula R⁴(SH) n where R⁴ is an n valent organic or silicone residue and n is an integer of two or more and the polyene is a compound or resin having a plurality of groups of the formula where Q is CR 1 2 , O, S, NR¹ or SO₂, R¹ is H or alkyl and m is 0-10. The norbornene resin is also disclosed as a nadimide resin. WO 88/02902 mentions that where the norbornene compound is suitably compatible, polyorganosiloxanes having alkylthiol groups may be employed in the composition. Propylthiolpolysiloxane together with norborn-5-ene terminated polydimethylsiloxane and Darocure®, as catalyst, represents the specific disclosure of this embodiment. SUMMARY OF THE INVENTION The present invention pertains to novel curable polyorganosiloxane ("silicone") formulations utilizing norbornene functional silicones as the polyene in a hydrosilation cure formulation. In particular the curable formulations of the invention comprise: a) A norbornene functional silicone prepolymer having a plurality of groups of the formula: bound to silicon atoms thereof, where R is H or methyl, and R⁴ is ethylene, ethenylene, propylene or propenylene, b) a coreactive silicone prepolymer having SiH functionality, said silicone resins (a) and (b) being present in an equivalent ratio of between 2:1 and 1:2 norbornene to silicon hydride groups, and c) an effective amount of a hydrosilation catalyst, the total of the average number of norbornene groups per molecule of norbornene functional prepolymer and the average number of SiH groups per molecule of the coreactive prepolymer being greater than 4. Detailed Description of the Invention The norbornene funcational silicones used in the formulations of the present invention are prepared by a novel process comprising the steps of: 1) reacting a norbornene compound of the formula: where R is H or methyl and R² is vinyl, ethynyl, allyl or propargyl, with a silicon hydride functional compound in the presence of hydrosilation catalyst at a temperature of at least 60°C; and 2) recovering a product which consists essentially of the addition products of the silicon hydride functional compound to the R² group of the norbornene compound and which is substantially free of addition products of the silicon hydride functional compound to the internal ring double bond of the norbornene compound. The reaction to selectively hydrosilate the side chain unsaturation of the starting norbornene compound is surprisingly straightforward. Using reaction temperatures of at least 60°C, preferably at least 70°C, in the presence of common hydrosilation catalysts, the reaction proceeds exothermically. It is generally desirable that the norbornene compound be in substantial excess on the basis of moles of norbornene compared to equivalents of SiH. Suitably there is a 50% excess. The excess norbornene compound, however, appears desirable more from the standpoint of improving yield by driving the reaction toward completion rather than as a safeguard against non-selective hydrosilation of the norbornene ring double bond. Upon completion of the reaction, the excess norbornene starting compound is readily removed from the reaction mixture by distillation. The selective hydrosilation reaction to produce the norbornene functional silicones will be described and exemplified below primarily with respect to the preferred vinyl norbornene starting material. However, it will be readily seen that similar results may be obtained using other norbornene compounds within the formula given above. Moreover it will be appreciated that modifications of the materials and conditions exemplified herein may readily be made by those skilled in the art. SiH functional organosiloxane polymers can be used to directly hydrosilate the norbornene compound. Suitable procedures may be obtained by modifying the examples of U.S. 4,665,147, substituting equivalent weights of vinyl norbornene for the β-(allyloxy)ethyl methacrylate used in these examples. However, it will generally be more convenient to use SiH functional silanes which also contain hydrolyzable functionality to prepare norbornene functional silanes which also include one, two or three hydrolyzable groups bound to the silicon atom thereof: Such silane compounds serve as useful monomers or capping agents for organosiloxane polymers whose molecular sizes, extent of branching and distribution of functional groups may be designed to provide specific desirable properties in the resulting norbornene functional prepolymer or in a cured polymer thereof. Examples of suitable hydrolyzable groups include chloro, methoxy, ethoxy, oxime such as methyl ethyl ketoximino, acetoxy, N,N-dialkylamino, and other hydrolyzable groups described in U.S. Pat. 4,699,802. For most organosiloxane polymerization or capping reactions methoxy or chloro groups will be satisfactory. Hydrosilation catalysts are well known to those skilled in the art. Examples are platinum, chloroplatinic acid, hydrocarbon platinum complexes, rhodium complexes, etc. Platinum based catalysts, such as Karstedt catalyst and chloroplatinic acid, are preferred at levels of between 10 ppm and 500 ppm platinum, more preferably between 50 ppm and 300 ppm. The reactions can be carried out neat or in solvents which do not interfere with hydrosilations. Toluene, hexane, tetrahydrofuran, methylene chloride and benzene are examples of suitable organic solvents. The hydrosilation reactions can be followed by observing the disappearance of the SiH absorption peak at 2200cm⁻¹ of the infrared spectrum. Normally the reactions are complete within three hours. Capping reactions to produce ethyl norbornene functional silicones such as the silicones of formula V are suitably accomplished by condensing an ethylnorbornene silane having hydrolyzable functionality as in formula IV with a silanol terminated diorganosiloxane polymer of the formula: where p is between 100 and about 1500 and R⁵ and R⁶ are the same or different organo groups. Suitable R⁵ and R⁶ groups are hydrocarbyl or substituted hydrocarbyl groups including alkyl such as methyl, ethyl, cyclohexyl, etc.; haloalkyl such as 3,3,3-trifluorolpropyl; and aryl which may be optionally substituted with hydrocarbon or halogen groups, especially phenyl, benzyl or methylphenyl. More preferably R⁵ and R⁶ are methyl or phenyl, most preferably methyl. The silanol terminated silicones typically have viscosities in the range of 500 centipoise (mPas) to 120,000 centipoise (mPas), preferably between 750 and about 50,000 centipoise (mPas), still more preferably between about 2,000 and 30,000 centipoise (mPas). The capping reaction is run in the presence of a conventional condensation catalyst, suitably a titanate, tin or tertiary amine catalyst. Silanes of formula IV may also be used as monomers to prepare norbornene functional homopolymers and copolymers by conventional condensation polymerization procedures. Furthermore, as described in example 4 below, silanes of formula IV may also be used to prepare norbornene functional cyclic oligomeric siloxanes which likewise can be used norbornene functional siloxane polymers and copolymers by conventional methods. Typically the cureable formulations of the invention will also include one or more fillers. Suitable fillers are reinforcing glass fiber or silica fillers. Particularly preferred are fumed silicas, especially fumed silicas which have been treated to render them hydrophobic. Such silicas can be added at high levels, sometimes 60% or more, while maintaining practical viscosities. Especially preferred are silicas treated to give low thixotropic ratios such as Wacker-Chemie HDK-2000™. For most applications such fillers will desireably be employed at levels between about 1% and 60%, suitably between about 10% and 40%, preferably 25%-35%. Inert or semi-reinforcing fillers may also be employed such as ground quartz, calcium carbonate, talc, clay and their treated counterparts, as well as other materials well known in the art. Levels of such fillers, when used, are typically 5%-60% based on the total weight of the formulation. Although silicon hydride functional compounds will selectively hydrosilate the side unsaturated groups of the norbornene starting compounds under the conditions described herein, the ring unsaturation is reactive to hydrosilations. Thus, the norbornene functional polyorganosiloxane component of the inventive compositions may - be cured using a conventional hydrosilation cure system. In such systems a second silicon hydride functional compound is used, after synthesis of the norbornene silicone, to cure the norbornene silicone by SiH addition to the norbornene ring. Hydrosilation catalysts and their concentrations are as previously described. The polyorganosiloxane backbone of the SiH functional curing silicone may be the same as, or different from, the polyorganosiloxane backbone of the norbornene functional silicone. Preferably the SiH curing silicone is one which includes more than two SiH groups per molecule. Example 8 illustrates this type of hydrosilation cureable formulation. Suitably the SiH functional silicones used in hydrosilation cured formulations are silicones of formula VI: Difunctional SiH compounds of formula VII may also be employed to extend the length of the cured polymer between crosslinks: While a cureable composition using norbornene functional silicones of the invention may include both difunctional norbornenyl silicones and a difunctional SiH silicone, it will be understood that at least a portion of at least one of these components should contain more than two functional groups per molecule to produce a crosslinked product when cured. That is, the total of the average number of norbornene groups per molecule of norbornene functional prepolymer and the average number of coreactive SiH groups per molecule of the coreactive prepolymer should be greater than 4 when a crosslinked cured product is desired. This total is referred to as the "total reactive functionality" of the composition. The invention is illustrated by the following non-limiting examples. EXAMPLE 1 Preparation of 2-(Norborn-5-enyl)ethyltrichlorosilane 5-Vinyl-2-norbornene (1.23 M, 148 g) was stirred under nitrogen at 75°C in a round-bottomed flask equipped with a condenser and a pressure equalizing addition funnel. Trichlorosilane (0.616 M, 83.11 g) was added dropwise and Karstedt catalyst (0.23 g) was quickly added. The rate of addition was adjusted to maintain a 75°- 80°C pot temperature without external heating. When addition was complete, the reaction mixture was aged at 75°C for three hours. Infrared analysis indicated no silane was present. The reaction mixture was then concentrated on a rotary evaporator and distilled in vacuo (bp 55-62°C,6.67 Pa (0.05 mm Hg)).Yield 143.4 g (91% theory, >95% purity by GLPC). Similar results are obtained when chloroplatinic acid is used as the catalyst. EXAMPLE 2 Preparation of 2-(Norborn-5-enyl)ethyldimethylchlorosilane 5-Vinyl-2-norbornene (4.20 M, 504 g) was stirred under nitrogen at 70°-75°C in a round-bottomed flask equipped with a thermometer, an efficient condenser and a constant pressure addition funnel. Dimethylchlorosilane (2.8 M, 264 g) was added dropwise and a Karstedt catalyst (0.77 g) was added to the reaction mixture. When the addition was complete, the reaction mixture was aged at 70°C for two hours. Analysis of the reaction indicated no silane present (FT-IR). The mixture was then stripped on a rotary evaporator and distilled in vacuo (bp 60°-64°C, 6.67 Pa (0.05 mm Hg)). Yield 493 g (82% theory, 94% purity by GLPC). EXAMPLE 3 Preparation of Ethyl Norbornene capped polyorganosiloxane Silanol fluid, Rhone Poulenc 48V3500, (0.092 eq OH) was stirred under nitrogen and warmed to 70°C with triethylamine-dimethylaminopyridine (1.05 eq, 1% DMAP by weight). The product of example 2 (0.0956 eq, 20.5 g) was added. The reaction mixture was stirred at 75°C for three hours then methanol (50 g) was added slowly. After one hour, volatiles were removed by concentration on a rotary evaporator, the reaction mixture was diluted with hexane and filtered through diatomaceous earth. Removal of solvent on a rotary evaporator at 75°C (13.33 Pa (0.1 mm Hg)) gave the product: Viscosity 4680 cps, GPC MW wt 30787, NW number 23943. EXAMPLE 4 Preparation of Norbornene Cyclic Tetramer Water (200ml, 11.1 moles) was added dropwise to 200.0g, 0.85 mole, 2-(norborn-5-enyl)ethyldichloromethylsilane in 200 ml THF in a 1 liter 3-necked flask with thermometer and mechanical stirrer, allowing gentle THF reflux at 65°C during the addition. The contents were stirred at 70°C for one hour after the addition, then allowed to phase. The upper product layer was separated, then added to 100 g water and 50 g potassium carbonate with stirring for one hour at 70°C. After allowing to phase, the upper, product layer was removed, concentrated on a rotary evaporator, rediluted with an equal volume of hexane and filtered through a Celite® pad. The product was isolated by rotary evaporation, giving 160.4 g of a hazy, light yellow oil (89% Theory, MW wt = 735, MW number = 607 by GPC, absence of SiOH confirmed by IR). Brookfield Viscosity: 14.3 Pas (14,300 cps) (RV4 spindle, 5 rpm). EXAMPLE 5 (comparative) Using a premixed base of the product of example 3 with 35% HDK 2000™ silica and 1.5% diethoxyacetophenone (DEAP), the inventors combined various thiol equivalent percent (eq%) increments of 3K5M (a polythiol of formula B where x is about 5 and y is about 30) and 1,3-bis(3-mercaptopropyl) -1,1,3,3-tetramethyldisiloxane (a polythiol of formula VII referred to herein as "C") adding up to the total unsaturation in the premix. The formulations were cast between polyethylene-backed 15.24 cm (6") square steel plates with a 1.78 mm (70 mil) by 15.24 cm (6") square outer dimension by 13.97 cm (5½") square inner dimension steel spacer. The polyethylene-backed specimens were clamped between two 15.24 cm (6") square glass plates and placed in a Technocure TM high pressure mercury vapor lamp UV curing chamber and irradiated 60 seconds per specimen side at an intensity of 70 milliwatts per square centimeter. After cooling, the cured specimen was peeled free of the plates and cut into tensile and tear test specimens per ASTM Method D412. The following bulk properties were obtained on the test specimens: EFFECT OF 1,3-BIS(3-MERCAPTOPROPYL)-1,1,3,3-TETRAMETHYLDISILOXANE Amounts of C 20 eq% 40 eq% 60 eq% 80 eq% Premix 150 g 150 g 150 g 150 g 3K5M 5.8 g 4.3 g 2.9 g 1.45 g (C) 0.3 g 0.6 g 0.9 g 1.2 g Tensile kP 8377.1 8646 6419 1854.7 (psi) (1215) (1254) (931) (269) Elongation (%) 454 589 701 630 Tear N/mm 38.2 40.45 32.6 6.5 (pli) (218) (231) (186) (37) Shore A 40 37 27 13 % Extractables 4.5 6.3 8.1 16.5 These data indicate that nearly equiequivalent amounts of 3K5M and the oligomeric siloxane dithiol "C" offer the best elongation improvement versus extent of cure. The 80 eq% point, illustrates the effects of very low crosslink density in this system, evidenced by the low Shore A. Cured properties without any (C) are very similar to the 20 eq% point. It is readily apparent that (C) adds additional flexibility to the above formulations. EXAMPLE 6 Preparation of propargyl ester of 2-norborn-5-ene carboxylic acid The propargyl ester of 2-norborn-5-ene carboxylic acid was prepared by Diels-Alder reaction of propargyl acrylate and cyclopentadiene at ambient temperature. Dimethylchlorosilane (56.4g) was added portionwise to 100 grams of this norbornene carboxylate ester and 0.16 g Karstedt catalyst under nitrogen at 70°C. After exotherming to 80°C, the mixture was stirred for 3 hours at 70°C, stripped under light vacuum and then distilled. The product, (84% purity by GC), distilled at 100° - 105°C at 0.07 mm. EXAMPLE 7 Preparation of allyl ester of 2-norborn-5-ene carboxylic acid A mixture of allyl alcohol (116 g, 2.0 mol), triethylamine (202 g, 2.0 mol) and 4-dimethylaminopyridine (2.44 g, .02 mol) in benzene (500 ml) was stirred at 51°C in a 2 liter three-necked flask equipped with a mechanical stirrer, a thermometer, and a pressure equalizing addition funnel under a nitrogen atmosphere. A solution of norborn-5-ene-2-carboxylic acid chloride (197 g, 1.26 mol) in benzene (100 ml) was added dropwise so that the temperature of the reaction did not exceed 20°C during the addition. When the addition was complete, the viscous slurry was warmed to 55°C and aged at this temperature for one hour. The reaction mixture was then cooled to room temperature and filtered. The filter cake was washed successively with pentane (2 times 200 ml) and ether (2 times 200 ml). The filtrate was then concentrated on a rotary evaporator and distilled in vacuo (bp 85°-93°C, at 26.7-13.33 Pa (0.2-0.1 mm Hg)). The yield of distilled product was 201g and consisted of a mixture of endo and exo isomers of allyl norborn-5-ene-e-carboxylate. The purity of the product was judged to be >98% by gas chromatographic analysis. Chlorodimethylsilane (26.6 g, 0.281 mol) was added slowly at 80°C to 50.0 g (0.281 mol) allyl norborn-5-ene-2-carboxylate and 0.16 g Karstedt catalyst (50 ppm Pt) in 100 ml toluene under a nitrogen blanket. No exotherm was observed, even with complete addition of chlorodimethylsilane. After heating and stirring 18 hours at 80°C, IR confirmed the disappearance of SiH. After briefly stripping on a rotary evaporator, a small quantity of precipitate formed, which was removed by dilution with an equal volume of heptane, and filtering. After reconcentrating, the crude product was vacuum distilled, removing a forecut at 50°-90°C at 0.06 mm, followed by the product at 90°-92°C at 0.06 mm. Yield: 30.6 g (40%) of a slightly cloudy liquid. MNR analysis confirmed the product as: with no evidence of silane addition to the internal ring norbornene double bond. EXAMPLE 8 One hundred grams of an ethylnorbornene capped polyorganosiloxane as prepared in Example 3 was mixed in a 250 ml beaker with 3.91 gm of a SiH functional polydimethylsiloxane having an average of 7 SiH groups per molecule and an SiH equivalent wt. of 346, and a catalytic amount of Karstedt catalyst (0.1 gm). The liquid mixture gelled within 3 hours and produced a rubbery elastomeric solid easily removable from the beaker after 24 hours at ambient temperature.

Claims: Claims for the following Contracting States : AT, BE, CH, DE, DK, FR, GB, GR, IT, LI, LU, NL, SE A composition curable to a crosslinked polyorganosiloxane the composition comprising: a) a silicone prepolymer having a plurality of norbornene functional groups of the formula: bound to silicon atoms thereof, where R is H or methyl and R⁴ is ethylene, ethenylene, propylene or propenylene, b) a coreactive silicone prepolymer having SiH functionality, said silicone resins (a) and (b) being present in an equivalent ratio of between 2:1 and 1:2 norbornene to silicon hydride groups, and c) an effective amount of a hydrosilation catalyst, the total of the average number of norbornene groups per molecule of norbornene functional prepolymer and the average number of SiH groups per molecule of the coreactive prepolymer being greater than 4. A composition as claimed in claim 1 wherein the norbornene functional silicone prepolymer has the formula: where q is from 100-1500. A composition as claimed in claim 1 or claim 2 characterised in that the SiH functional silicone prepolymer component comprises between 20% and 80%, on the basis of total equivalents of SiH of a compound of the formula: where m is between 1 and 3. A composition as claimed in claim 1 or claim 2 characterised in that the coreactive silicone prepolymer component is a mixture of SiH functional silicones which consists essentially of a poly-SiH compound of the formula: where x is 3-10 and y is 25-50 and an oligomeric chain extender of the formula: where m is between 1 and 3 said poly-SiH compound being present in an amount of at least 20% of the total number of equivalents of the SiH component. A composition as claimed in any of claims 1 to 4 characterised in that the norbornene functional silicone prepolymer is substantially free of groups of the formula: bound to silicon atoms thereof where R is as defined in claim 1 and R² is vinyl, ethynyl, allyl or propargyl. A composition as claimed in any of claims 1 to 5 . wherein the norbornene functional groups are of the formula III as defined in claim 1, and R⁴ is a propylene or propenylene group. A composition as claimed in any of claims 1 to 6 characterised in that the hydrosilation catalyst is a platinum based catalyst and is present at a level of between 10 and 500 ppm Pt. A composition as claimed in claim 1 wherein the silicone prepolymer (a) has a first polyorganosiloxane backbone, to which the norbornene functional groups are bound, and the silicone prepolymer (b) has a second polyorganosiloxane backbone to which the hydride groups are bound, said first and second polyorganosiloxane backbones being the same. A composition as claimed in claim 1 characterised in that the said first and second polyorganosiloxane backbones as recited in claim 8 are different. A composition as claimed in claim 1 characterised in that at least 20% of the SiH functional silicone prepolymer, based on the total number of SiH equivalents, comprises a poly-SiH compound of the formula: where x is 3-10 and y is 25-50. Claims for the following Contracting State : ES A process for the production of a crosslinked polyorganosiloxane characterised in that a composition comprising: a) a silicone prepolymer having a plurality of norbornene functional groups of the formula: bound to silicon atoms thereof, where R is H or methyl and R⁴ is ethylene, ethenylene, propylene or propenylene, b) a coreactive silicone prepolymer having SiH functionality, said silicone resins (a) and (b) being present in an equivalent ratio of between 2:1 and 1:2 norbornene to silicon hydride groups, and c) an effective amount of a hydrosilation catalyst, the total of the average number of norbornene groups per molecule of norbornene functional prepolymer and the average number of SiH groups per molecule of the coreactive prepolymer being greater than 4, is cured. A process as claimed in claim 1 wherein the norbornene functional prepolymer has the formula: where q is from 100-1500. A process as claimed in claim 1 or claim 2 characterised in that the SiH functional silicone prepolymer component comprises between 20% and 80%, on the basis of total equivalents of SiH of a compound of the formula: where m is between 1 and 3. A process as claimed in any of claim 1 or claim 2 characterised in that the coreactive silicone prepolymer component is a mixture of SiH functional silicones which consists essentially of a poly-SiH compound of the formula: where x is 3-10 and y is 25-50 and an oligomeric chain extender of the formula: where m is between 1 and 3 said poly-SiH compound being present in an amount of at least 20% of the total number of equivalents of the SiH component. A process as claimed in any of claims 1 to 4 characterised in that the norbornene functional silicone prepolymer is substantially free of groups of the formula: bound to silicon atoms thereof where R is as defined in claim 1 and R² is vinyl, ethynyl, allyl or propargyl. A process as claimed in any of claims 1 to 5 wherein the norbornene functional groups are of the formula III as defined in claim 1, and R⁴ is a propylene or propenylene group. A process as claimed in any of claims 1 to 6 characterised in that the hydrosilation catalyst is a platinum based catalyst and is present at a level of between 10 and 500 ppm Pt. A process as claimed in claim 1 wherein the silicone prepolymer (a) has a first polyorganosiloxane backbone, to which the norbornene functional groups are bound, and the silicone prepolymer (b) has a second polyorganosiloxane backbone to which the hydride groups are bound, said first and second polyorganosiloxane backbones being the same. A process as claimed in claim 1 characterised in that the said first and second polyorganosiloxane backbones as recited in claim 8 are different. A process as claimed in claim 1 characterised in that at least 20% of the SiH functional silicone prepolymer, based on the total number of SiH equivalents, comprises a poly-SiH compound of the formula: were x is 3-10 and y is 25-50.

Inventors: GLASER DAVID M, JACOBINE ANTHONY F, NAKOS STEVEN T, GLASER, DAVID M., JACOBINE, ANTHONY F., NAKOS, STEVEN T.
Applicants: LOCTITE CORP, LOCTITE CORPORATION
Application year: 1990
Main classification: C08L83
IPC codes: C08G77, C08L83