Refrigeration compositions and process for using

Abstract: A blend of a tetrafluoroethane or pentafluoroethane refrigerant with a di-functional random polyalkylene glycol based on significant amounts of ethylene oxide and propylene oxide and having an SUS viscosity at 100°F of 100 to 1200 is disclosed for use in compression refrigeration.

Description: Field of the Invention This invention relates to lubricants used with refrigerants in compression refrigeration. More particularly, it relates to lubricants for use with tetrafluoroethanes, e.g. 1,1,1,2 - Tetrafluoroethane (HFC-134a), 1,1,2,2 - Tetrafluoroethane (HFC-134), etc., and of lesser importance, pentafluoroethanes (HFC-125). These refrigerants are being considered as replacements for dichlorodifluoromethane (CFC-12), particularly in automotive air conditioning systems. Background of the Invention Refrigeration systems that use CFC-12 as the refrigerant generally use mineral oils to lubricate the compressor. (See for example the discussion in Chapter 32 of the 1980 ASHRAE Systems Handbook.) CFC-12 is completely miscible with such oils throughout the entire range of refrigeration system temperatures, i.e. -45°C to 65°C. In automotive air-conditioning, paraffinic and naphthenic oils of about 500 SUS viscosity at 100°F are used with CFC-12. These oils have "pour points" below -20°C and are completely miscible with the CFC-12 refrigerant over the range of temperatures from -10°C to 100°C. Consequently, oil which dissolves in the refrigerant travels throughout the refrigeration loop in the air conditioning system and returns with the refrigerant to the compressor. It does not separate during condensation, although it may accumulate because of the low temperature when the refrigerant is evaporated. At the same time, this oil which lubricates the compressor will contain some refrigerant which, in turn, may affect its lubricating properties. When substituting HFC-134a or HFC-134 for CFC-12 in these refrigeration systems, it would be desirable to be able to use the same mineral oils as used with CFC-12. It would not require any substantial change in equipment nor any significant changes in conditions used for the system. If lubricant separates from refrigerant during operation of the system, serious problems may result, i.e. the compressor could be inadequately lubricated. This would be most serious in automotive air-conditioning systems because the compressors are not separately lubricated and a mixture of refrigerant and lubricant circulate throughout the entire system. Unfortunately, however, the mineral oils are not adequately miscible with the tetrafluoroethanes. Two recent publications of ASHRAE discuss the problems associated with separation of lubricants and refrigerants. These are "Fundamentals of Lubrication in Refrigerating Systems and Heat Pumps" Kruse and Schroeder ASHRAE Transactions Vol. 90 Part 2B, pps. 763-782, 1984 and "Evaluation of Lubricants for Refrigeration and Air-Conditioning Compressors" Spauschus ibid pps. 784-798. In summary, refrigerants which are not completely miscible with an oil in the full range of mixture compositions and operating temperatures may become miscible or immiscible as the temperature is raised or lowered from room temperature. The areas of immiscibility may assume a variety of shapes, i.e. parabolic or non-parabolic. As a parabola, the curve of miscibility temperature vs. percent oil in the mixture, may have its open or concave portion facing the low or high temperatures. The closed or convex portion of the parabolic curve identifies, respectively, the maximum or minimum temperature above or below which the refrigerant and the lubricating oil are completely miscibile. These temperatures are referred to as the maximum or minimum "consolute temperatures." Beside parabolas, these curves can assume skewed parabolic shapes or curves of varying slope wherein immiscibility occurs above or below the curve. One of the objects of this invention is to provide a combination of lubricating oil and tetrafluoroethane, e.g. HFC-134a, where the area of miscibility encompasses the full ranges of temperature and composition encountered in compression refrigeration, i.e., complete miscibility occurs for all compositions in the range of -45°C to at least 20°C. Another object is to provide a process for using such compositions in compression refrigeration. Prior Art U.S. Patent No. 4,248,726 , issued February 5, 1981, and U.S. Patent No. 4,267,064 , issued May 12, 1981, both to Nippon Oil Co. et al, relate to the use of a polyglycol oil such as polyoxypropylene glycol (or an alkyl ether thereof) having a viscosity index of at least 150 and a glycidyl ether type epoxy compound as a high viscosity refrigeration oil composition for halogen-containing refrigerants. These polyglycol/glycidyl ether compositions are disclosed for use with Freon®11, 12, 13, 22, 113, 114, 500 and 502; and as being "particularly effective" with Freon®12 or 22. Research Disclosure 17486 entitled "Refrigeration Oil" by E. I. du Pont de Nemours & Co. discloses polyalkylene glycols such as "Ucon" LB-165 and "Ucon" LB-525 sold by Union Carbide Corporation, for use with HFC-134a. These glycols are polyoxypropylene glycols that are mono-functional and are prepared from propylene oxide initiated with n-butanol. The publication states that these combinations of oil and refrigerant are miscible in all proportions at temperatures at least as low as -50°C and are thermally stable in the presence of steel, copper and aluminum at 175°C for about six days. U.S. Patent No. 4,755,316 , issued July 5, 1988, to Allied-Signal Inc. also relates to the use of polyalkylene glycols. However, these glycols are at least difunctional with respect to hydroxyl groups and contain at least 80% propylene units relative to the total, the remaining 20% may derive from ethylene or butylene oxide or esters, olefins and the like which are polymerizable with propylene oxide. It should be noted that only 100% oxypropylene units in the difunctional PAG's are exemplified in this patent. Summary of the Invention The present invention is based on the discovery that the use of a sufficient amount to lubricate, usually 10-20% by volume, for automotive use, but in some situations as high as 50% by volume of at least one di-functional, preferably a random, polyalkylene glycol (PAG), also is referred to as polyoxyalkylene glyclol, based on a significant amount of ethylene oxide with propylene oxide, preferably from 25%-75% ethylene oxide and, correspondingly, 75%-25% propylene oxide, will be completely miscible with tetrafluoroethane and pentafluoroethanes, usually 80-90% by volume of the tetrafluoroethanes, HFC-134 and HFC-134a, and the pentafluoroethane, HFC-125, or blends thereof with each other and with other refrigerants in the range of temperatures from -40°C to at least 20°C. The more preferred weight per cents of oxypropylene units and oxyethylene units in the PAG are from 40-60% to 60-40%, respectively; and the most preferred ratio is about 50:50. The weight ratio of refrigerant to the PAG lubricant in the mixtures used for refrigeration may be anywhere from 99/1 to 1/99, preferably 99/1 to 70/30. The viscosities of these compositions may be anywhere from 100 to 1200 SUS but for most commercial uses, from 400 to 1000 SUS. The process of manufacturing the di-functional random PAG's may involve initiation with a glycol having anywhere from two to six carbon atoms between -OH groups. Diethylene glycol is the preferred initiator; and the process of manufacture is described in the Encyclopedia of Polymer Science and Engineering, Volume 6; "Ethylene Oxide Polymers and Copolymers" by Clinton and Matlock, 2nd edition, 1986, John Wiley & Sons. It has been found that the use of 0.1-1.3% of an "extreme pressure additive" improves the lubricity and load-bearing characteristics of the butanol-initiated monofunctional random polyalkylene glycol having 50% oxyethylene units as set forth in the U.S. Application Serial No. (CH-1651); and it is expected that the EP additives will also improve the quality of the refrigerant-lubricant compositions of this invention. EP additives for use in the invention are included among those disclosed in Table D of U.S. Patent 4,755,316. The preferred ones are the organic phosphates and include Lubrizol®1097, a zinc (dialkyl dithio) phosphate manufactured by the Lubrizol Corporation; and SYN-O-AD® 8478, a 70%/30% blend of tri (2, 4, 6-tri-t-butyl phenyl) phosphate/triphenyl phosphate manufactured by the Stauffer Chemical Company. EP additives may also be used in conjunction with some of the oxidation and thermal stability improvers and/or corrosion inhibitors disclosed in Table D of U.S. Patent 4,755,316. Such a preferred blend of additives is MLX-788, a proprietary mixture of Union Carbide Corporation containing a phosphate and two amine-containing compounds. Description of Preferred Embodiments As stated previously, the tetrafluoroethanes, e.g. HFC-134a, HFC-134 and pentafluoroethane, HFC-125, particularly HFC134a, have physical characteristics which allow substitution for CFC-12 with only a minimum of equipment changes in compression refrigeration. They could be blended with each other, as well as with other refrigerants including CFC-12(CCl₂F₂), HCFC-22(CHClF₂), HFC-152A(CH₃CHF₂), HCFC-124 (CHClFCF₃), HCFC-124a (CHF2CClF₂), HCFC-142b(CH₃CClF₂), HFC-32 (CH₂F₂), HFC-143a(CH₃CF₃), HFC-143 (CHF₂CH₂F), HFC-125(CF₃CHF₂) and FC-218 (CF₃CF₂CF₃); and for purposes of the present invention such blends are not excluded. However, only those blends of tetrafluoroethane or pentafluoroethane with other refrigerants which are miscible with the lubricants of this invention in the range of -40°C to at least +20°C are included. HFC-134a, the preferred tetrafluoroethane refrigerant, may be prepared by any of the methods disclosed in the prior art; e.g., U.S. 2,745,886; 2,887,427; 4,129,603; 4,158,675; 4,311,863; 4,792,643 and British 1,578,933 and 2,030,981, which are incorporated herein by reference. The most preferred di-hydroxyl polyalkylene glycol for use in this invention is based on the random polymerization of a 50/50 weight percent mixture of ethylene oxide and propylene oxide initiated with diethylene glycol. Although the amount of ethylene oxide can range from 25 to 75 weight % of the ethylene oxide/propylene oxide composition and the viscosity can range from 100 to 1200 SUS viscosity at 38°C (100°F), preferably 400 to 1200 SUS, the most preferred PAG is the "50H400" (400 representing the SUS viscosity at 38°C (100°F); "H" representing "hydrophyllic" and "50" indicating the presence of 50% ethylene oxide units) that is manufactured by the Union Carbide Corporation. The process for its manufacture is described in the 1986 edition of the Encyclopedia of Polymer Science and Engineering. The preferred 50H400 oil has a pour point below -40°C, is completely miscible with HFC-134a from -50°C to condenser temperatures above 45°C, and should meet all the other requirements for automotive air conditioning, i.e. viscosity index, stability, lubricity, and miscibility with HFC-134a down to below -10°C. Furthermore, the use of an extreme pressure additive such as those mentioned previously should improve the load-carrying capability significantly. Specifically, the lubricants used in the compositions of this invention, and in the invented method for providing lubrication in compression refrigeration equipment have the following characteristics: Viscosity at 38°C (100°F) 100 to 1200 SUS, preferably 400 to 1200 SUS, most preferably 500 SUS for automotive air-conditioning; Viscosity index >90, preferably 150 to 250 or higher; Pour point <-20°C, preferably -20°C to -50°C and -35°C for the 100 SUS and 1200 SUS oils, respectively; Solubility or miscibility range 100% from at least 20°C to less than -10°C for 1-99 weight percent of HFC-134a in mixture with the lubricant. 1. Solubility of Refrigerant in Lubricants Six ml. blends of refrigerant and lubricant were used for the solubility studies. Generally, the mixtures contained 30, 60 and 90 wt. % refrigerant. In some instances, more compositions were made to better define the miscible/immiscible region. These air-free mixtures were contained in sealed Pyrex® tubes (7/16'' I.D. x 5.5'', ca. 12.5 cc capacity). The refrigerant/lubricant solubilities were determined by completely immersing the tube in a bath at each test temperature for a minimum of 15 minutes and providing agitation to facilitate mixing and equilibration. The accuracy of determining the temperatures where the refrigerant/lubricant blend became either miscible or immiscible was about ± 2°C. The refrigerant/lubricant blends were called immiscible when the blend acquired and retained "schlieren" lines, became hazy or cloudy, formed floc, or formed two liquid layers. 2. Viscosity and Viscosity Index a. Viscosity is a property that defines a fluid's resistance to shearing force. It is expressed in terms of absolute viscosity, kinematic viscosity or Saybolt Seconds Universal viscosity (SSU), depending on the method by which it is determined. Conversion from SSU to mm²/s (centistokes) can be readily made from tables contained in ASTM D-455, but it is necessary to know the density to convert kinematic viscosity to absolute viscosity. Refrigeration oils are sold in viscosity grades, and ASTM has proposed a system of standardized viscosity grades for industry-wide usage (D-2422). b. Viscosity Index is a measure of the amount of change experienced by an oil with temperature. Viscosity decreases as the temperature increases and increases as the temperature decreases. The relationship between temperature and kinematic viscosity is represented by: log log (v + 0.7) = A + B log T where v = kinematic viscosity, mm²/s (CST) T = thermodynamic temperature (kelvin) A,B = constants for each oil This relationship is the basis for the viscosity temperature charts published by ASTM and permits a straight line plot of viscosity over a wide temperature range. This plot is applicable over the temperature range in which the oils are homogenous liquids. The slope of the viscosity-temperature lines is different for different oils. The viscosity-temperature relationship of an oil is described by an empirical number called the Viscosity Index (VI) (ASTM D-2270). An oil with a high viscosity index (HVI) shows less change in viscosity over a given temperature range than an oil with a low viscosity index (LVI). 3. Pour Point Any oil intended for low temperature service should be able to flow at the lowest temperature likely to be encountered. This requirement is usually met by specifying a suitable low pour point. The pour point of an oil is defined as the lowest temperature at which it will pour or flow, when tested according to the standard method prescribed in ASTM D-97. The invention will be more clearly understood by referring to the following experiments which are presented in Tables I-VI. 1. Solubility Data Table I summarizes the solubility data for the di-functional random alkylene glycol polymers/tetrafluoroethane refrigerant compositions of this invention. The PAG's contained 25-75% ethylene oxide units and, correspondingly, 75-25% propylene oxide units. The preparation of the most preferred composition in Experiment 1 involved diethylene glycol as initiator. It should be understood that Experiment 1 was an actual test run whereas Experiments 2-7 represent estimations based on the actual runs shown in Table IB and the minimum consolute temperatures shown in Table IA. Table IA illustrates that the minimum consolute temperature for the lubricant used in Experiment 1, 50H400, in combination with the refrigerant, HFC-134a, corresponds substantially to the minimum consolute temperature for the mixtures of HFC-134a with the lubricant, 50 HB400 , as determined from Figure I, a plot of minimum consolute temperatures vs. SUS viscosity at 38°C (100°F) for the 50 HB series. That is, the minimum consolute temperature for the mixture of HFC-134a and 50HB400 is 47°C; and the minimum consolute temperature for the mixture of HFC-134a and 50H400 is 45°C. The minimum consolute temperatures of 45°C and 47°C are within experimental error. Thus, it is expected that the estimated miscible ranges for Experiments 2-7 are substantially as shown in Table I. The solubility data shown in Table I indicate that PAG's used in the invention provided superior results when compared at equivalent viscosities, to: (1) mono-functional PAG's containing 100% propylene oxide units as shown in Table II. (2) PAG's with less than one -OH group as shown in Table III. (3) PAG's containing 100% propylene oxide units with two -OH groups as shown in Table IV . (4) PAG's with three -OH groups, three of which were initiated with glycerine as shown in Table V. In Table VI, data are presented showing the immiscibility of HFC-134a with miscellaneous refrigerant oils which may be used with CFC-12, including those oils typically used with CFC-12 for automotive air conditioning e.g. paraffinic (BVM-100N) and naphthenic (Suniso 5GS). Minimum Consolute Temperatures of Random PAG's containing 50% oxyethylene units Lubricant Minimum Consolute Temperature (°C) 50HB260 56 50HB400 47 50H400 45 50HB500 42 50HB660 30 Minimum Consolute Temperature of Mixtures of HFC-134a with PAG's Containing Two Functional OH Groups Expt.No. Oil Viscosity at 38°C (100°F) SUS Minimum Consolute Temperature(°C) Control J Polyoxypropylene diol 554 31 Control K Polyoxypropylene diol 154 45 Control L Polyoxypropylene diol 400 36 Solubility of HFC-134a with PAG's Containing Three Functional OH Groups (Test Range: 93 to -50°C) Expt.No. Oil Viscosity at 38°C (100°F) SUS Wt. % HFC-134a in Oil Miscible Range (°C) Control M 50HG400 400 30 93 to 25 60 25 to 5 90 25 to -50 Control N 50HG450 450 30 25 to -50 60 25 to -50 90 20 to -50 Control O 100HG550 550 30 24 to -40 60 Insoluble 90 Insoluble Control P CH₃C(CH₂OCH₂-CH₂OCH₂CH₂OH)₃ 562 30 Insoluble 60 Insoluble 90 Insoluble

Claims: A composition for use in compression refrigeration comprising: (a) at least one refrigerant selected from the group consisting of tetrafluoroethane and pentafluoroethane; and (b) a sufficient amount to provide lubrication of at least one random polyalkylene glycol which is di-functional with respect to hydroxyl groups and based on 25% to 75% ethylene oxide and, correspondingly, 75% to 25% propylene oxide, having an SUS viscosity at 38°C (100°C) of 100 to 1200 and being miscible in combination with component (a) in the range of temperatures from -40°C to at least +20°C. The composition of claim 1 wherein said tetrafluoroethane comprises, 1,1,2,2-tetrafluoroethane. The composition of claim 1 wherein said tetrafluoroethane comprises 1,1,1,2-tetrafluoroethane. The composition of claim 1 wherein the refrigerant comprises pentafluoroethane. The composition of any one of the preceding claims wherein said di-functional polyalkylene glycol has been prepared using diethylene glycol as an initiator. The composition of any one of the preceding claims wherein the SUS viscosity at 38°C (100°F) of said di-functional polyalkylene glycol is from 400 to 1000. The composition of any one of the preceding claims wherein said polyalkylene glycol comprises 1-99% by weight of said composition. The composition of any one of the preceding claims further comprising (1) an extreme pressure additive, (2) an oxidation and thermal stability improver or (3) a corrosion inhibitor. The composition of claim 8 further comprising 0.1-1.3% by weight of an extreme pressure additive. The composition of claim 1 wherein said tetrafluoroethane is 1,1,1,2-tetrafluoroethane and said di-functional random polyalkylene glycol is prepared using a diethylene glycol initiator, is based on 40-60% ethylene oxide and, correspondingly, 60-40% propylene oxide, has an SUS viscosity at 38°C (100°F) of from 400 to 1000 and is completely miscible in combination with said tetrafluoroethane in the temperature range from -50°C to at least +40°C. Use as a lubricant in a tetrafluoroethane refrigerant in compression refrigeration of at least one random di-functional polyalkylene glycol based on 25% to 75% ethylene oxide and, correspondingly, 75% to 25% propylene oxide and having an SUS viscosity at 38°C (100°F) of 100 to 1200. Use as claimed in claim 11 wherein said polyalkylene glycol is based on 40 to 60% ethylene oxide units and has an SUS viscosity of 400 to 1000 at 38°C (100°F). A method for improving lubrication in compression refrigeration equipment using tetrafluoroethane as the refrigerant which comprises using 1-99% by weight of the combination of said tetrafluoroethane of at least one random di-functional polyalkylene glycol based on 25%-75% ethylene oxide and 75%-25% propylene oxide and having an SUS viscosity of 100-1200 at 38°C (100°F). The method of claim 13 wherein said polyalkylene glycol is based on about 50% ethylene oxide units and has an SUS viscosity of about 400 at 38°C (100°F). A method for improving lubrication in compression refrigeration equipment using tetrafluoroethane as the refrigerant which comprises using 10-50% by volume of the combination with said tetrafluoroethane of at least one random di-functional polyalkylene glycol based on 25%-75% ethylene oxide and 75%-25% propylene oxide and having an SUS viscosity of 400-1000 at 38°C (100°F).

Inventors: BROWN WILLIAM LOVELL, GORSKI ROBERT ALEXANDER, BROWN, WILLIAM LOVELL, GORSKI, ROBERT ALEXANDER
Applicants: UNION CARBIDE CHEM PLASTIC, UNION CARBIDE CHEMICALS AND PLASTICS COMPANY, INC.
Application year: 1990
Main classification: C09K5
IPC codes: C10M107, C10N40, C10M171, C10M105, C09K5, C10N20, C10N70