Non-aqueous secondary cell

Abstract: A rechargeable non-aqueous secondary cell comprising a negative electrode (1); a positive electrode (7) comprising a lithium-including manganese oxide as an active material, the lithium-including manganese oxide having a specific surface area measured by the BET method of 9.0m²/g to 67.5m²/g; and a separator (8) interposed between the positive and the negative electrodes and impregnated with a non-­ aqueous electrolyte. A rechargeable non-aqueous secondary cell comprising a negative electrode; a positive electrode comprising a lithium-including manganese oxide as an active material, grain sizes of which are substantially 20 µm or less when observed by a scanning electron microscope; and a separator interposed between the positive and said negative electrodes.

Description: BACKGROUND OF THE INVENTION (1) Field of the Invention This invention relates to a non-aqueous secondary cell comprising a negative electrode having lithium as an active material and a positive electrode having a lithium-including manganese oxide as an active material, especially to an improvement of the positive electrode. (2) Description of the Prior Art As an active material of the positive electrode of this kind of secondary cell, molybdenum trioxide, vanadium pentoxide and sulfide of titanium or niobium have been proposed and partially used into practical use. As an active material of a positive electrode of a non-aqueous primary cell, manganese dioxide and carbon fluoride are known and have already been put into practical use. Especially, manganese dioxide is excellent in storage characteristics, abundant, and inexpensive. Considering these features, manganese dioxide seems to be appropriate as an active material of the positive electrode of a non-aqueous secondary cell. However, manganese dioxide is poor in reversibility and charge/discharge cycle characteristic. The inventors of this invention has disclosed a proposal for minimizing the above problems of manganese dioxide in USP4,758,484 (Japanese Patent Publication Kokai No. 63-114064). According to the above patent, a lithium-including manganese oxide, namely, a manganese dioxide including Li₂MnO₃, or a manganese oxide including lithium and having CuKα beam peaks at 2ϑ=22°, 31.5°, 37°, 42° and 55° is employed as a positive electrode active material. As a lithium-including manganese oxide, Li 1-x Mn₂O₄ (1>x>0) has been disclosed in USP4,904,552. According to the above proposal, a crystal lattice structure of the manganese oxide has reversibility against insertion and removal of lithium ion, which improves the cycle characteristic. However, other characteristics should also be improved to put it into practical use. A non-aqueous secondary cell according to the pre-characterizing part of claim 1 has been disclosed in proceedings of the symposium on primary and secondary ambient Temperature Lithium-Batteries, October 1987, Volume 88-86, pages 557-564. Although discharging manganese dioxide electrochemically has been proposed as a method of producing a lithium-including manganese oxide, it is more practical to mix a lithium salt and a manganese oxide and then to heat-treat the mixture. However, such a reaction between solid phases is performed non-uniformly if the manganese oxide mixed with the lithium salt has large-sized grains. As a result, a large portion of the above two chemicals remain unreacted, which prevents improvement in the cycle characteristic. SUMMARY OF THE INVENTION Accordingly, this invention has a first object of offering a non-aqueous secondary cell having improved cycle characteristic. A second object of this invention is to offer a non-aqueous secondary cell having increased discharge capacity. A third object of this invention is to offer a non-aqueous secondary cell which can have improved resistance against overcharge. The above objects are fulfilled by a rechargeable non-aqueous secondary cell comprising a negative electrode, a positive electrode and a separator interposed between said positive and said negative electrodes and imprignated with a non-aqueous electrolyte, said cell being characterized in that a positive electrode comprises a lithium-including manganese oxide, acting as an active material, which has a certain range of specific surface area, the above certain range of specific surface area being 9,0 m²/g to 41,6 m²/g when measured by the BET method and having a certain range of grain sizes being substantially 20 µm or less when observed by a scanning electron microscope. The lithium-including manganese oxide may be obtained from manganese dioxide and lithium hydroxide and the specific surface area of the lithium-including manganese oxide is determined by a specific surface area of the manganese dioxide. The lithium-including manganese oxide may be obtained from manganese dioxide and lithium hydroxide and the specific surface area of the lithium-including manganese oxide is determined by a mixing ratio of the manganese dioxide and the lithium hydroxide. The lithium-including manganese oxide may be obtained from manganese dioxide and lithium hydroxide and the specific surface area of the lithium-including manganese oxide is determined by a heat-treating temperature of a mixture of the manganese dioxide and the lithium hydroxide. The negative electrode may be formed of either of lithium and a lithium alloy. The electrolyte may be formed of a mixture of propylene carbonate and dimethoxyethane added with 1 mol/ℓ of lithium perchlorate. The above constructions fulfill the above objects for the following reasons. a) A lithium-including manganese oxide is obtained by mixing a lithium salt and a manganese dioxide and heat-treating the mixture. The obtained lithium-including manganese oxide has a smaller specific surface area than that of the manganese dioxide. This is because the manganese dioxide lowers its porosity by taking lithium into its crystal lattice structure. The specific surface area of the obtained lithium-including manganese oxide depends on what kind of manganese oxide was used, the percentage of lithium included, and the heat-treating temperature. If the specific surface area of the obtained lithium-including manganese oxide is too small, a contacting area with the electrolyte is small and so the utilization of the manganese oxide as an active material is low, resulting in a small discharge capacity. If the specific surface area is too large, the electrolyte is decomposed during charging due to the high chemical catalytic activity of the manganese dioxide. Then, gas is generated by the electrolyte decomposition, whereby the cell is expanded. Also, the dry-out of the electrolyte increases the cell internal resistance, which is conspicuous after the cell is overcharged. If the specific surface area of the lithium-including manganese oxide measured by the BET method is restricted between 9.0m²/g and 41,6m²/g as in the above constructions, such advantages of including lithium as improving the charge/discharge cycle characteristic, discharge capacity and resistance against overcharge are realized. b) In order to produce a lithium-including manganese oxide whose grain sizes are small, the grain sizes of the manganese oxide in the state of mixed with a lithium salt should be decreased. In this way, the lithium salt and the manganese oxide are reacted uniformly, which substantially leaves no portion of the lithium-including manganese oxide unreacted. Even if the grain sizes of the lithium-including manganese oxide are more than 20 µm when the oxide is produced, it is acceptable if the grain sizes are kept substantially 20 µm or less before heat-treating the positive electrode material. With the grain sizes being kept substantially 20 µm or less, the distribution state of lithium is changed, thereby eliminating the unreacted portion of the lithium-including manganese oxide. Practically, the distribution of lithium is uniform in the manganese solid phase. As a result, prevention of lithium movement during charging or discharging is restricted and so the cycle characteristic is improved. BRIEF DESCRIPTION OF THE DRAWINGS These and other objects, advantages and features of the invention will become apparent from the following description thereof taken in conjunction with the accompanying drawings which illustrate specific embodiments of the invention. In the drawings: Fig. 1 is a cross sectional view of a non-aqueous secondary cell; Fig. 2 is a graph showing the relationship between the specific surface area of a lithium-including manganese oxide, cell initial discharge capacity and increased cell thickness; Fig. 3 is a graph showing discharge capacities of Cell A₁ according to this invention at an initial stage and after overcharged; Fig. 4 is a graph showing discharge capacities of Cell A₂ as a comparative example at an initial stage and after overcharged; Fig. 5 is a graph showing discharge capacities of Cell A₄ according to this invention at an initial stage and after overcharged; Fig. 6 is a graph showing discharge capacities of Cell B₁ as a comparative example at an initial stage and after overcharged; Fig. 7 is a graph showing discharge capacities of Cell W₂ as a comparative example at an initial stage and after overcharged; Fig. 8 is a graph showing discharge capacities of Cell X₁ as a comparative example at an initial stage and after overcharged; and Fig. 9 is a graph showing cycle characteristics of Cells D₁ through D₄ according to this invention and Cells Z₁ through Z₃ as comparative examples. DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiment I An embodiment according to this invention will be described referring to Fig. 1. Lithium-including manganese oxides having different specific surface areas were produced using different kinds of manganese oxides (having different specific surface areas). [Example I according to this invention] A negative electrode 1 formed of a lithium metal is pressure-adhered on an inner surface of a negative electrode collector 2, and the negative electrode collector 2 is adhered on an inner surface of a negative can 3 formed of stainless steel. A peripheral portion of the can 3 is fixed in an insulating packing 4 of polypropylene, and a positive can 5 formed of stainless steel is fixed around an outer periphery of the insulating packing 4 and is opposed to the negative can 3. A positive electrode collector 6 is fixed on an inner surface of the positive can 5, and a positive electrode 7 is fixed on an inner surface of the positive electrode collector 6. The positive electrode 7 and the negative electrode 1 have a separator 8 therebetween, the separator 8 being formed of a polypropylene microcellular thin film. A cell having the above construction has a diameter of 24.0mm and a thickness of 3.0mm. An electrolyte is obtained by dissolving 1 mol/ℓ of lithium perchlorate in a mixture of propylene carbonate and dimethoxyethane. The positive electrode 7, which is the gist of this invention, was produced in the following way. Manganese dioxide having a specific surface area of 73.0m²/g when dry and lithium hydroxide were mixed in a mortar so that the mole ratio of the mixture be Mn:Li=70:30, thereafter the obtained mixture was heat-treated in an air at 375°C for 20 hours. The lithium-including manganese oxide obtained in this way had its specific surface area measured by the BET method, the result of which was 41.6m²/g. For the above measurement, the obtained lithium-including manganese oxide was dried at 120°C for 40 hours (also in Embodiments II and III). It was confirmed by observing the above lithium-including manganese oxide through an SEM (scanning electron microscope) that grains having grain sizes of approximately 0.1 to 20 µm are distributed in the above oxide and that grains having grain sizes of larger than 20 µm were almost extinct. The lithium-including manganese oxide as an active material, acetylene black as a conductor and a powdered fluororesin as a binder were mixed in a weight ratio of 90:6:4 to obtain a positive electrode material. The positive electrode material was pressure-molded to have a diameter of 20mm by a force of 2 tons/cm² and then heat-treated at 250°C to produce the positive electrode 7. The negative electrode 1 was obtained by punching a lithium plate having a specified thickness to have a diameter of 20mm. A cell comprising the above positive and the negative electrodes 1 and 2 is referred to as Cell A₁. (Comparative example I) Cell A₂ was produced in the same method as Cell A₁ except that manganese dioxide having a specific surface area of 91.4m²/g was used instead of 73.0m²/g. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 53.3m²/g. [Example II according to this invention] Cell A₃ was produced in the same method as Cell A₁ except that manganese dioxide having a specific surface area of 37.3m²/g was used instead of 73.0m²/g. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 17.9m²/g. [Example III according to this invention] Cell A₄ was produced in the same method as Cell A₁ except that manganese dioxide having a specific surface area of 30.0m²/g was used instead of 73.0m²/g. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 9.0m²/g. [Comparative example II] Cell W₁ was produced in the same method as Cell A₁ except that manganese dioxide having a specific surface area of 115m²/g was used instead of 73.0m²/g. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 92.4m²/g. [Comparative example III] Cell W₂ was produced in the same method as Cell A₁ except that manganese dioxide having a specific surface area of 23.8m²/g was used instead of 73.0m²/g. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 7.8m²/g. [Experiment] Concerning Cells A₁ and A₃ according to this invention and Cells A₂, W₁ and W₂ as comparative examples, their initial discharge capacities and increased thicknesses after overcharged were measured. The results are shown in Table 1. The initial discharge capacity of each cell was measured by discharging the cell with a current of 3mA until the cell voltage was declined down to 2.0V. The increased cell thickness was measured after applying a voltage of 4.0V to the cell for 30 days. As shown in Table 1, Cells A₁ and A₃ according to this invention have initial discharge capacities of 43 - 45 mAh and increased thickness of 0.04 - 0,06mm. On the other hand, Cell W₁ as a comparative example has a smaller initial discharge capacity of 35mAh but a larger increased thickness of 0.45mm compared with the cells according to this invention. In the case of Cell W₂, the increased cell thickness is as small as 0.02mm but the initial discharge capacity is extremely low at 25mAh. Embodiment II Lithium-including manganese oxides having different specific surface areas were produced with different mixture ratios of manganese dioxide and lithium hydroxide. It was confirmed through observation with an SEM that the lithium-including manganese oxide contained the same sizes of grains as in Embodiment I. (Comparative example I) Cell B₁ was produced in the same method as Cell A₁ except that manganese dioxide and lithium hydroxide were mixed so that the mole ratio of the mixture be Mn:Li=80:20. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 67.5m²/g. [Example I according to this invention] Cell B₂ was produced in the same method as Cell A₁ except that manganese dioxide and lithium hydroxide were mixed so that the mole ratio of the mixture be Mn:Li=50:50. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 13.2m²/g. [Comparative example II] Cell X₁ was produced in the same method as Cell A₁ except that manganese dioxide and lithium hydroxide were mixed so that the mole ratio of the mixture be Mn:Li=90:10. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 71.5m²/g. [Comparative example III] Cell X₂ was produced in the same method as Cell A₁ except that manganese dioxide and lithium hydroxide were mixed so that the mole ratio of the mixture be Mn:Li=33:67. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 3.9m²/g. [Experiment] Concerning Cell B₂ and Cell A₁ according to this invention and Cells B₁, X₁ and X₂ as comparative examples, their initial discharge capacities and increased thicknesses after overcharged were measured. The results are shown in Table 2. The experimenting conditions were the same as those of the experiment of Embodiment I. As shown in Table 2, Cells A₁ and B₂ according to this invention have initial discharge capacities of 38 - 46mAh and increased thicknesses of 0,02 mm - 0,06 mm. Cell X₁ as a comparative example has approximately as large an initial discharge capacity of 48mAh as the cells according to this invention, but has a larger increased cell thickness of 0.30mm. Cell X₂ has a smaller increased thickness of 0.01 mm compared with the cells of the present invention but an extremely small initial discharge capacity of 10mAh. Embodiment III Lithium-including manganese oxides having different specific surface areas were produced with different heat-treating temperatures of the mixture of manganese dioxide and lithium hydroxide. It was confirmed through observation with an SEM that the lithium-including manganese oxide contained the same sizes of grains as in Embodiment I. (Comparative example I) Cell C₁ was produced in the same method as Cell A₁ except that manganese dioxide and lithium hydroxide were heat-treated at 300°C. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 60.4m²/g. [Example I according to this invention] Cell C₂ was produced in the same method as Cell A₁ except that manganese dioxide and lithium hydroxide were heat-treated at 450°C. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 28.3m²/g. [Comparative example II] Cell Y₁ was produced in the same method as Cell A₁ except that manganese dioxide and lithium hydroxide were heat-treated at 250°C. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 72.0m²/g. [Comparative example III] Cell Y₂ was produced in the same method as Cell A₁ except that manganese dioxide and lithium hydroxide were heat-treated at 600°C. The lithium-including manganese oxide obtained in this example had its specific surface area measured by the BET method, the result of which was 6.5m²/g. [Experiment] Concerning Cell C₂ and Cell A₁ according to this invention and Cells C₁, Y₁ and Y₂ as comparative examples, their initial discharge capacities and increased thicknesses after overcharged were measured. The results are shown in Table 3. The experimenting conditions were the same as those of the experiment of Embodiment I. As shown in Table 3, Cells A₁, and C₂ according to this invention have initial discharge capacities of 42 - 45mAh and increased cell thicknesses of 0.05 - 0,06mm. Cell Y₁ as a comparative example has approximately as large an initial discharge capacity of 43mAh as the cells according to this invention, but has a larger increased thickness of 0.31 mm. Cell Y₂ has a smaller increased cell thickness of 0.02mm compared with the cells of the present invention but an extremely small initial discharge capacity of 13mAh. Summary of Embodiments I through III [Summary I] Fig. 2 shows relationship between the initial discharge capacities, the increased thicknesses and the specific surface areas obtained by the above three embodiments. The initial discharge capacity is drastically declined when the specific surface area of the lithium-including manganese oxide is less than 9.0m²/g. When it exceeds 41.6m²/g, the increased thickness after overcharged is gradually increased; and when it exceeds 67.5m²/g, the increased thickness is remarkably increased. As a conclusion, the lithium-including manganese oxide used as an active material of a positive electrode of a non-aqueous secondary cell desirably has a specific-surface area measured by the BET method of 9.0m²/g to 67.5m²/g, more desirably, of 9.0m²/g to 41.6m²/g. The above conclusion is attributed to that too small a specific surface area of the lithium-including manganese oxide decreases a utilization of the active material, which lowers the discharge capacity and that too large a specific surface area increases a contacting area of the active material and the electrolyte, which accelerates electrolyte decomposition during overcharge. [Summary II] Concerning Cells A₁, A₂, A₄, B₁, W₂ and X₁, their initial discharge capacities and discharge capacities after overcharged were measured. The results are shown in Figs. 3 through 8. The experimenting conditions were the same as those of the experiment of Embodiment I. The initial discharge capacity is drastically declined when the specific surface area of the lithium-including manganese oxide is less than 9.0m²/g (W₂). The discharge capacity after overcharged is gradually declined when it exceeds 41.6m²/g (B₁ and X₁), and is remarkably declined when it exceeds 67.5m²/g (X₁). As a conclusion, the lithium-including manganese oxide used as an active material of a positive electrode of a non-aqueous secondary cell desirably has a specific surface area measured by the BET method of 9.0m²/g to 67.5m²/g, and more desirably, of 9.0m²/g to 41.6m²/g. [Other points] [1] As described in Embodiments I through III, the specific surface area of lithium-including manganese oxide depends on either the kind of manganese oxide, the mixture ratio of manganese dioxide and lithium hydroxide, or the heat-treating temperature of the mixture of manganese dioxide and lithium hydroxide, or the combination of two or all of the above. [2] Although the above embodiments employ flat cells, the present invention can be applied to square, cylindrical and other-shaped non-aqueous secondary cells. Embodiment IV [Example I according to this invention] The positive electrode 7 was produced by the same method as in Example I of Embodiment I except the following. Manganese dioxide having an average grain size of 30 µm (comprising grains having grain sizes of 5 to 50 µm when observed by an SEM) and lithium hydroxide were mixed so that the mole ratio be 7:3. The mixture was done by stirring the total 50g of the manganese dioxide and lithium hydroxide for 30 minutes with an Ishikawa stirring apparatus Type 20. Then, the obtained mixture was heat-treated at 375°C for 20 hours to obtain lithium-including manganese oxide used as an active material. It was confirmed by observing the oxide with an SEM that grains having grain sizes of 0.1 to 20 µm were distributed in the oxide and that grains having grain sizes of larger than 20 µm were almost extinct. The specific surface area of the lithium-including manganese oxide measured by the BET method was 41.6m²/g. The lithium-including manganese oxide as an active material, acetylene black as a conductor and fluororesin as a binder were mixed at a weight ratio of 90:6:4 to obtain a positive electrode material. The mixture was done by stirring the total 50g of the manganese dioxide and lithium hydroxide for 5 minutes with the Ishikawa stirring apparatus Type 20. Then, the positive electrode material was pressure-molded to have a diameter of 20mm by a force of 2 tons/cm² and heat-treated at 250°C to produce the positive electrode 7. Observation of the positive electrode 7 by an SEM found out that the lithium-including manganese oxide comprised the grains of substantially the same sizes with those before it was mixed with the conductor and the binder. The cell comprising the positive electrode 7 obtained above is referred to as Cell D₁. [Example II according to this invention] Cell D₂ was produced in the same method as Cell D₁ except that manganese dioxide having an average grain size of 50 µm (comprising grains having grain sizes of 10 to 100 µm when observed by an SEM) was employed and that the manganese dioxide and lithium hydroxide were mixed for 2 hours to produce lithium-including manganese oxide. Observation by an SEM of the positive electrode obtained in this example confirmed that the manganese oxide comprised grains having grain sizes of 0.1 to 20 µm and that grains having sizes of larger than 20 µm were almost extinct. [Example III according to this invention] Cell D₃ was produced in the same method as Cell D₁ except that the manganese dioxide and lithium hydroxide were mixed for 2 hours to produce a lithium-including manganese oxide. Observation by an SEM of the positive electrode obtained in this example confirmed that the manganese oxide comprised grains having grain sizes of 0.1 to 10 µm and that grains having sizes of larger than 10 µm were almost extinct. [Example IV according to this invention] Cell D₄ was produced in the same method as Cell D₁ except that the manganese dioxide and lithium hydroxide were mixed for 10 minutes to produce a lithium-including manganese oxide and that the manganese oxide as the active material, the conductor and the binder were mixed for 30 minutes. The lithium-including manganese oxide before mixed with the conductor and the binder and the lithium-including manganese oxide in the positive electrode 7 were observed with an SEM. The former comprised grains having grain sizes of approx. 1 to 30 µm and 20% of the grains had grain sizes of larger than 20 µm. The latter comprised grains having grain sizes of approx. 0.1 to 20 µm and grains having grain sizes of larger than 20 µm were almost extinct. [Comparative example I] Cell Z₁ was produced in the same method as Cell D₁ except that the manganese dioxide and lithium hydroxide were mixed for 10 minutes to produce a lithium-including manganese oxide. Observation by an SEM of the positive electrode obtained in this example confirmed that the manganese oxide comprised grains having grain sizes of 1 to 30 µm and that 20% of the grains had grain sizes of larger than 20 µm. [Comparative example II] Cell Z₂ was produced in the same method as Cell D₂ except that the manganese dioxide and lithium hydroxide were mixed for 30 minutes to produce a lithium-including manganese oxide. Observation by an SEM of the positive electrode obtained in this example confirmed that the manganese oxide comprised grains having grain sizes of 1 to 30 µm and that 20% of the grains had grain sizes of larger than 20 µm. [Comparative example III] Cell Z₃ was produced in the same method as Cell D₂ except that the manganese dioxide and lithium hydroxide were mixed for 10 minutes to produce a lithium-including manganese oxide. Observation of the positive electrode obtained in this example by an SEM confirmed that the manganese oxide comprised grains having grain sizes of 5 to 50 µm and that 50% of the grains had grain sizes of larger than 20 µm. [Experiment] Cycle characteristic was measured concerning Cells D₁ through D₄ according to this invention and Cells Z₁ through Z₃ as comparative examples, the results of which are shown in Fig. 9. Cells D₁ through D₄, whose grain sizes are less than 20 µm have more excellent cycle characteristics than Cells Z₁ through Z₃, which include grains having grain sizes of more than 20 µm. Especially, D₃, whose grain sizes are less than 10 µm, has a remarkably excellent cycle characteristic. Cell D₄ has a better cycle characteristic than Cells Z₁ through Z₃. It means there is no absolute necessity of decreasing grain sizes of the grains to less than 20 µm when the lithium-including manganese oxide is produced. It is acceptable if the grain sizes are less than 20 µm by the time the positive electrode is produced. Cells D₁ through D₄ have excellent cycle characteristics due to change in lithium distribution, which is occurred at the heat-treating after pressure-molding. Although Embodiment IV employs a non-aqueous secondary cell using a non-aqueous electrolyte, the present invention can also be applied to a non-aqueous secondary cell using a solid electrolyte. Although the present invention has been fully described by way of embodiments with references to the accompanying drawings, it is to be noted that various changes and modifications will be apparent to those skilled in the art. Therefore, unless otherwise such changes and modifications depart from the scope of the present invention, they should be construed as being included therein.

Claims: A rechargeable non-aqueous secondary cell comprising a negative electrode (1), a positive electrode (7) and a separator (8) interposed between said positive and said negative electrodes (1, 7) and impregnated with a non-aqueous electrolyte, said cell being characterized in that a positive electrode (7) comprises a lithium-including manganese oxide, acting as an active material, which has a certain range of specific surface area, the above certain range of specific surface area being 9,0 m²/g to 41,6 m²/g when measured by the BET method and having a certain range of grain sizes being substantially 20 µm or less when observed by a scanning electron microscope. A rechargeable non-aqueous secondary cell of Claim 1, wherein said lithium-including manganese oxide is obtained from manganese dioxide and lithium hydroxide and the specific surface area of said lithium-including manganese oxide is determined by a specific surface area of said manganese dioxide. A rechargeable non-aqueous secondary cell of Claim 1, wherein said lithium-including manganese oxide is obtained from manganese dioxide and lithium hydroxide and the specific surface area of said lithium-including manganese oxide is determined by a mixing ratio of said manganese dioxide and said lithium hydroxide. A rechargeable non-aqueous secondary cell of Claim 1, wherein said lithium-including manganese oxide is obtained from manganese dioxide and lithium hydroxide and the specific surface area of said lithium-including manganese oxide is determined by a heat-treating temperature of a mixture of said manganese dioxide and said lithium hydroxide. A rechargeable non-aqueous secondary cell of Claim 1, wherein said negative electrode (1) is formed of either of lithium and a lithium alloy.

Inventors: FURUKAWA NOBUHIRO, NOHMA TOSHIYUKI, YAMAMOTO YUJI, FURUKAWA, NOBUHIRO, NOHMA, TOSHIYUKI, YAMAMOTO, YUJI
Applicants: SANYO ELECTRIC CO, SANYO ELECTRIC CO., LTD.
Application year: 1990
Main classification: H01M4
IPC codes: H01M10, H01M4