Preprimed metal substrates for formed metal applications

Abstract: The present invention relates to preprimed metal substrates suitable for use in formed metal applications. The preprimed metal substrate is coated with, as primer layer, (1) a first coating layer applied onto the metal substrate, the first coating layer being based upon a particular hydroxyl groups-containing block copolymer, and (2) at least one flexible subsequent coating layer applied onto the first coating layer. The preprimed metal substrates are especially useful in automtovie applications.

Description: The present invention relates generally to preprimed metal substrates, such as sheets, which are suitable for formed metal applications, for example, the manufacture of automotive body parts for repair and/or on-line assembly. In the usual formed metal applications, a metal sheet is first formed by well-known methods (drawing, dye cutting) into the desired shape then subsequently coated with a primer (postpriming). The primer serves a number of well-known functions, including providing a barrier layer and/or corrosion protection layer for the underlying metal substrate. Typical examples of primers for metal applications, such as automotive applications, include the following. US4562714 discloses a preprimed metal substrate coated with a flexible primer layer (precoat) comprising a polyester polyol cross-linked by means of a diisocyanate, which is said to have suitable properties for subsequent fabrication (high flexural strength) as well as superior hardness, staining resistance and chemical resistance. US4602053 describes epoxyester linear block oligomers made with n-1 moles of fatty acid groups and n moles of epoxy oligomer, which are said to be particularly suited for chip-resistant coating compositions (preferably containing small pigment volume concentrations). See also EP-A-0179281. WO85/00375 discloses thermosetting coating compositions based upon an epoxy-polyester graft copolymer and a polyisocyanate crosslinker, which is said to be useful as a chip resistant primer for the automotive industry. EP-A-0070008 describes zinc rich coatings having binders comprised of thermoplastic polyhydroxyethers, epoxy resins, epoxy ester resins, alkyl silicates, which are useful for corrosion protection in the automotive industry. These coatings particularly contain aluminium trihydrate for improved combined spot welding/corrosion resistance properties on automotive components. In automotive applications where the formed metals may take a number of odd or complex shapes, postpriming by normal on-line painting methods may result in a significant portion of the underlying metal substrate being unprimed or underprimed, as in the normal on-line painting methods it is difficult to adequately apply the primer in the various corners and other odd-shaped areas of the formed metal, particularly on both sides. In many instances, the various body parts are not primed until after assembly, thereby exacerbating the problem of unprimed or underprimed base metal. A common result is the early rusting and decreased life of the part. It is, therefore, an object of the present invention to overcome this shortcoming by providing a preprimed metal substrate which may subsequently be formed into a shape suitable for use in automotive applications. The general concept of preprimed metal substrates for formed metal applications is, of course, not new. Most primers suitable for use in automotive applications, however, are not suitable for preprimed formed metal applications, for example, because of either insufficient adhesion to the metal substrate or insufficient flexibility. In forming the preprimed metal substrate, particularly in the manner and degree necessary for automotive applications, insufficient adhesion can cause the primer to separate from the substrate, while insufficient flexibility can cause the primer to crack. Both can result, as indicated above, in the early rusting and decrease life of the part. The present invention, therefore, provides a preprimed metal substrate comprising a metal substrate coated with a primer layer, characterized in that the primer layer comprises, in its overall concept: (1) a first coating layer applied onto the metal substrate, the first coating layer comprising a coating composition based upon, as a binder, and hydroxyl groups-containing block copolymer built up from (A) one or more blocks of a carboxyl-terminated polyester resin and (B) one or more blocks of an epoxy resin; and (2) at least one flexible subsequent coating layer applied onto the first coating layer. The first coating layer should provide good ashesion to the substrate, be sufficiently flexible to be formed, and exhibit sufficient solvent resistance so that a second coating layer applied over the surface of the first coating layer will adhere to, but not substantially dissolve, the first coating layer. It has been found that, to obtain good adhesion of the first coating layer to the substrate, the dry thickness of the first layer should not exceed about 15 µm. It has also been found that the overall coating thickness needs to be in the range of about 15 µm to about 45 µm to provide the desired final appearance for automotive applications and other applications where a glossy finish is desired, so it is necessary to apply at least a second coating layer. The at least one subsequent coating layer should, in general, be a flexible material which exhibits stone chip resistance. It has been discovered that polyester polyols crosslinked with polyisocyanates and/or melamines adhere well to the first coating layer, provide good flexibility and possess excellent stone chip resistance. The present invention also provides a method of prepriming a metal substrate, characterized in that the method comprises the steps of: (1) applying the aforementioned first coating layer onto a metal substrate, and (2) applying the aforementioned at least one flexible subsequent coating layer onto the first coating layer. The resulting preprimed metal substrates find particular use in formed metal applications which require deep draw capability during forming, such as the deep draw required in the automotive industry, and which require excellent stone chip resistance of the finished metal part. These and other features and advantages of the present invention will be more readily understood by those skilled in the art from a reading of the following detailed description. As indicated previously, the present invention is related to preprimed metal substrates and, more particularly, to those suitable for use in applications wherein the preprimed substrate is subsequently formed into a shape. Suitable metal substrates include a wide variety of pretreated or non-pretreated metals, including alloys and composites comprising such metals. Particularly preferred are those normally utilized in the automobile industry, such as iron, galvanized iron, steel, galvanized steel and aluminum. For formed metal applications, of course, the metal substrate to be preprimed should substantially be in the physical form of a sheet. These metal substrates are rendered suitable for formed metal applications by application of a particular primer layer prior to forming of the metal, hence the name "preprimed" metal. In accordance with the present invention, this primer layer comprises: (1) a first coating layer applied onto the metal substrate, the first coating layer comprising a coating composition based upon, as a binder, an hydroxyl groups-containing block copolymer built up from (A) one or more blocks of a carboxyl-terminated polyester resin and (B) one or more blocks of a epoxy resin; and (2) at least one flexible subsequent coating layer applied onto the first coating layer. As suitable hydroxyl groups-containing block, copolymers may be mentioned those described in EP-B-0111986 and EP-A-0399108 (European Patent Application No. 89201350.9). Briefly, the carboxyl-terminated polyester block (A) preferably comprises the polycondensation product of one or more carboxylic diacids and one or more difunctional hydroxy compounds. As suitable carboxylic diacids may be mentioned aromatic carboxylic diacids (EP-B-0111986), aliphatic carboxylic diacids (EP-A-0399108) and mixtures thereof. As examples of suitable aromatic carboxylic diacids may be mentioned terephthalic acid and isophthalic acid. As examples of suitable aliphatic carboxylic diacids may be mentioned compounds of the general formula (I) HOOC-R-COOH (I) wherein R is an aliphatic hydrocarbon group, preferably a (cyclo)aliphatic hydrocarbon group, and more preferably a linear alkyl group, having from 1 to 34 carbon atoms and preferably 1 to 12 carbon atoms. As specific examples of such may be mentioned malonic acid, succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, dodecane dioic acid, dimeric fatty acids, trimethyl adidpic acid, maleic acid and cyclohexane dicarboxylic acids. Especially preferred are adipic acid and sebacic acid. At the time of application of the subsequent coating layer(s) over the first coating layer of the prepriming coating, it is desirable to have the second coating layer adhere to, but not substantially dissolve, the first coating layer. It has been found that use of the aromatic carboxylic diacids is preferred for formation of the carboxyl-terminated polyester block, since the solvent resistance of the first coating layer is thereby increased making possible the use of a wider variety of second coating layer materials. Suitable difunctional hydroxy compounds may be branched or unbranched, and may contain ether and/or ester linkages in their structures. As examples of such may be mentioned 1,2-propylene glycol, 1,3-propylene glycol, neopentyl glycol, 1,2-butane diol, 1,3-butane diol, 1,4-butane diol, 1,5-pentane diol, 1,6-hexane diol, polyalkylene glycols such as diethylene glycol, triethylene glycol and dipropylene glycol, trimethyl hexane diol, polycaprolactone diols, 1.1′-isopropylidene-bis-(p-phenylene-oxy)-di-β-ethanol and 1.1′-isopropylidene-bis-(p-phenylene-oxy)-di-ω-ethanol. Particularly preferred of these are the diols and polyalkylene glycols, especially those having from 2 to 8 carbons atoms. Optionally, one or more hydroxy acid and/or lactone compounds may also be utilized in the production of the carboxyl-terminated polyester blocks (A). As suitable hydroxy acids may be mentioned those of the general formula (II) HO-R¹-COOH (II) wherein R¹ is preferably a hydrocarbon group, more preferably a (cyclo)aliphatic hydrocarbon group, having from 1 to 17 carbon atoms and especially from 7 to 17 carbon atoms. As specific examples may be mentioned hydroxycaproic acid and hydroxystearic acid. As suitable lactone compounds may be mentioned those of the general formula (III) wherein R² is a hydrocarbon group, more preferably an aliphatic hydrocarbon group, having from 2 to 10, more preferably 5 to 9, carbon atoms. As a specific example may be mentioned ε-caprolactone. In the preparation of the carboxyl-terminated polyester blocks (A), use may also be made of derivatives of the aforementioned components such as epoxy compounds, acid chlorides, acid anhydrides and methyl diesters. The polycondensation reaction of the above components is generally carried out at a temperature of from about 140°C to about 300°C, preferably from about 180°C to about 260°C, and in an inert atmosphere of, for example, nitrogen and/or carbon dioxide. The water evolved in the polycondensation reaction may be removed in a normal manner, e.g., by distillation under reduced pressure or by azeotropic distillation with the aid of an organic solvent such as toluene, xylene or mixed aromatic solvents. After termination of the polycondensation, these solvents may optionally be removed from the polyester resin by distillation. The polycondensation mixture may optionally contain an esterification catalyst, for example, sulfuric acid, p-toluene sulfonic acid, benzene sulfonic acid, napthalene sulfonic acid, a sulfonic acid cation exchanger or a metal compound such as dibutyltin dilaurate or lead acetate. The polycondensation reaction is continued until the polyester resin has the desired acid number, preferably from about 10 to about 140, and more preferably from about 20 to about 110. The hydroxyl number of the resulting polyester resin preferably should also not be higher than about 2, and more preferably from 0 to about 0,8. The acid number and hydroxyl number are expressed in mg KOH per g of polyester resin. Further, the polyester resin should have a number average molecular weight (Mn) of from about 800 to about 10000, more preferably from about 1000 to about 6000. Epoxy resins suitable for use in the present block copolymers may be solid or liquid, with an epoxy functionality of from about 1,5 to about 2,5 and an epoxy equivalent weight of from about 100 to about 2000. Examples of such suitable epoxy resins are detailed in the previously incorporated references, and include glycidyl groups-containing resins such as polyacrylic resins, polyesters, polyethers or polyurethanes which all contain one or more glycidyl groups per molecule. Use may also be made of mixtures of these epoxy resins. Optionally, the epoxy resin may be used as a solution in a suitable solvent. Preferred epoxy resins are those of the general formula (IV) wherein R³ represents an aliphatic, cycloaliphatic or aromatic group. preferably containing from 2 to about 18 carbon atoms, and n is a number from 0 to 50, preferably 0 to about 10. Adducts of these epoxy resins with (cyclo)aliphatic or heterocyclic diamines, preferably a di-secondary amine such as piperazine, are also suitable. Examples of these preferred epoxy resins include the glycidyl ethers of, for example, ethlyene glycol, diethylene glycol, triethylene glycol, 1,2-propylene glycol, 1,3-propylene glycol, 1,5-pentane diol, bis-(4-hydroxycyclohexyl)-2,2-propane, 4,4′-dihydroxybenzophenone, bis-(4-hydroxyphenyl)methane, bis-(4-hydroxyphenyl)-1,1′-ethane, bis-(4-hydroxyphenyl)-1,1-isobutane and 1,5-dihydroxynapthalene. In more preferred aspects, the epoxy resin has an epoxy functionality of from about 1,8 to about 2,2, an epoxy equivalent weight of from about 100 to about 700, most preferably from about 150 to about 500, and an Mn of from about 150 to about 1250. The block copolymer may be prepared in any convenient manner by reaction of the carboxyl-terminated polyester resin with the epoxy resin. The block copolymer may optionally be prepared by using two or more carboxylic polyester and/or epoxy resins. A suitable procedure for producing the block copolymers comprises the stepwise addition of the epoxy resin(s) to a solution of the polyester resin(s) and heating the mixture to a temperature generally in the range of from about 85°C to about 195°C, preferably from about 100°C to about 180°C. The reaction mixture may, if required, be made to contain a catalyst known in itself, for instance, triphenyl phosphine, benzyl triphenyl phosphonium chloride, benzyl trimethyl ammonium methoxide, a tertiary amine such as benzyl dimethylamine, or a metal compound such as zirconium octoate. A preferred solvent for the polyester resin and resulting block copolymer is an aromatic hydrocarbon such as toluene, xylene or a mixture of aromatic hydrocarbons having a boiling point of, for example, about 140°C to about 180°C. To the resulting block copolymer obtained on the conclusion of the reaction may be added a polar solvent such as isophoron, methylethyl ketone, diacetone alcohol, the ethyl ether of ethylene glycol and the ethyl ether of ethylene glycol acetate. The weight ratio of the carboxyl-terminated polyester resin (A) to the epoxy resin (B) is generally chosen so that, at the start of the reaction to form the block copolymer, the reaction mixture contains from 0,5 to 2,0, preferably from 0,7 to 1,3, moles of epoxy of the epoxy resin per mole of carboxyl of the polyester resin. In this manner, a block copolymer having carboxyl and/or epoxy end groups is obtained. The most preferred block copolymer is built up of from 3 to 11 blocks (A) and 2 to 10 blocks (B), or from 2 to 10 blocks (A) and 3 to 11 blocks (B). The number average molecular weight of the resulting block copolymer is preferably from about 3000 to about 80000, and more preferably from about 5000 to about 30000. The acid number of the block copolymer is preferably not higher than about 23, and more preferably in the range of from 0 to about 15. The coating composition of the first coating layer typically contains (but need not contain) a curing agent for the hydroxyl groups of the block copolymer, which are the result of the reaction between the carboxyl of the polyester and the epoxy group. Suitable curing agents are blocked or non-blocked isocyanurate compounds or blocked or non-blocked aliphatic, cycloaliphatic or aromatic di-, tri- or polyvalent isocyanates, specific examples of which are listed in EP-B-0111986 (see page 3, lines 39-52). For blocking the isocyanate or isocyanurate compound, use may be made of any well-known blocking agent. Instead of or in addition to the isocyanate and isocyanurate curing agents, other suitable blocked and unblocked curing agents such as the N-methyloyl groups- and/or N-methyloyl ether groups-containing aminoplasts and phenol resins, as mentioned in EP-B-0111986 (see page 3, lines 53-65), may also be utilized. The curing agent should be present in the coating composition in an amount such that the molar ratio of the reactive groups of the curing agent to that of the hydroxyl groups of the block copolymer is in the range of from 0,1 to about 1,7, preferably from about 0,2 to about 1,5. Optionally, the coating composition of the first coating layer may contain solid powdered polymers and pigments such as mentioned in EP-B-0111986 (see page 4, lines 4-28), and also the usual adjuvants and additives, for example, pigment dispersing agents, antisag agents, rheology control agents, corrosion inhibiting compounds (e.g., metallic zinc or metallic aluminum), plasiticizers, gloss agents and accelerators such as p-toluene sulfonic acid and blocked products of such accelerators. As examples of suitable pigments may be mentioned the usual types of acid, neutral or basic pigments which may be organic or inorganic. The pigments may be optionally treated to modify their properties. As specific examples may be mentioned titanium dioxide, red iron oxide, lead chromate, carbon black and phthalocyanine pigments. The term pigments as used herein also refers to metallic pigments such as aluminum and stainless steel. The weight ratio of pigment to block copolymer and curing agent is generally in the range of about 0,05 to 19, the higher ratios being used for generally metal-rich compositions, which are weldable if they contain metal as pigment or corrosion inhibiting compound. The coating composition of the first coating layer may be applied to a substrate in any convenient manner, such as by roller coating or (electrostatic) spraying, and may be cured or baked in the usual manner. For example, in a coil coating process baking is to be carried out at an applied final temperature of the substrate of about 200°C to about 280°C, which temperature is normally reached by contacting the coated substrate for a short time (e.g., 10 to 90 seconds) with air or combustion gases at a temperature of about 250°C to about 400°C. Application and baking conditions during coil coating are known to one skilled in the art and need not be further described here. Suitable baking temperatures for other fields of application may, for example, range from about 120°C to about 210°C. The at least one flexible subsequent coating layer to be applied over the first coating layer is characterized by performance characteristics such as high flexibility as measured by the T-bend test and the Erichsen impact test, a glass transition temperature in the range of about 30°C to about 70°C, adhesion capability relative to the first coating layer, stone chipping resistance and leveling properties. One skilled in the art can select a coating material which will perform well in combination with the above-described first coating layer. Coating materials known to perform well as the second coating layer include polyurethane coatings based upon polyester polyols crosslinked using a polyisocyanate (such as commercially available under the trade designation PZ 2000 from Akzo Coatings) and polyester polyols, having a relatively low Mn (e.g., about 2000 to about 10000) and a functionality of about 2, crosslinked using a melamine. The flexible subsequent coating layer material may also contain adjuvants and additives of the type previously discussed for use in the first coating layer. The coating composition of the at least one flexible subsequent coating layer may be applied, as with the coating composition of the first coating layer, in any convenient manner, such as by roller coating or (electrostatic) spraying, and cured or baked in the usual manner such as, for example, as described above. It is preferred that the first coating layer be applied to a dry layer thickness of up to about 15 µm, more preferably from about 3 µm to about 10 µm, and the at least one flexible subsequent coating layer to a dry layer thickness up to about 30 µm, more preferably from about 12 µm to about 25 µm. The total primer dry layer thickness should preferably range from about 15 µm to about 45 µm, more preferably from about 20 µm to about 30 µm. The resulting preprimed metal substrate can then be utilized in formed metal applications. The forming of the preprimed metal substrate may be accomplished by any well-known means, such as by bending, stamping, profiling and drawing. The preprimed metal substrate prepared according to the present invention finds use in metallic construction such as buildings, appliances, metallic furniture and particularly in the automotive field, where properties such as high corrosion protection, excellent stone chipping resistance, and ease of deep draw shape formation are especially important. The foregoing general discussion of this invention will be further exemplified by the following specific examples offered by way of illustration and not limitation of the above-described invention. Examples 1-10 and Comparative Examples C11 and C12 Preparation of Polyester/Epoxy Block Copolymer for Examples 1-10. In Examples 1-10 use was made of carboxyl-terminated polyester resins (A-G) obtained by the polycondensation of the components in the amounts (parts by weight) as listed below in Table I. The polycondensation was carried out at a temperature of about 240°C to about 260°C in the presence of 3% by weight of xylene (based upon the total polycondensation mixture). The polycondensation was continued until the polyester had the desired acid number. Esterification catalysts used were dibutyltin oxide (polyesters A, B, D and F) and tributyltin oxide (polyesters C and E). No esterification catalyst was used in the preparation of polyester G. The resulting polyester resins all had an hydroxyl number of 0 and showed no crystallinity. Table I also lists other characteristics of the so-produced polyester resins. Components Polyester Resin A B C D E F G 1,2-propane diol 26,83 - - - - 9,03 - 1,5-pentane diol - - 37,60 35,25 33,28 - 10,30 1,6-hexane diol - 39,53 - - - 28,08 30,73 1,1,1-trimethylol propane - - - 0,46 2,25 - - isophthalic acid 73,07 - 31,15 64,29 64,47 62,59 - terephthalic acid - 60,37 31,15 - - - - trimellitic anhydride - - - - - 0,21 - adipic acid - - - - - - 58,97 Properties Acid Number 112 37 19 56 56 29 57 Carboxyl Functionality 2,0 2,0 2,0 2,08 2,48 2,05 2,0 Number Average MW 1000 3000 6000 2081 2475 4000 1358 The polyester/epoxy block copolymers, BC1-BC10, used in Examples 1-10 were prepared by adding one or more epoxy resins, of the types and in the amounts as set forth below in Table II, to solutions of the above polyester resins. All amounts for the epoxy resins and polyesters in Table II are expressed as parts by weight (solids). Epoxy resin A was a diglycidyl ether of Bisphenol A with an epoxide equivalent of 170 (commercially available under the trade designation Epikote 828 from Shell Chemical). Epoxy resin B was a diglycidyl ether of Bisphenol A with an epoxide equivalent of 454 (commercially available under the trade designation Epikote 1001 and Epon 1001 from Shell Chemical). Epoxy resin C was a diglycidyl ether of 1,4-butane diol with an epoxide equivalent of 101. Epoxy resin D was an adduct of 2 moles of Epoxy resin A and 1 mole of piperazine. The solutions of polyester resins A-F were prepared by dissolving each in 51,5 parts by weight of an aromatic hydrocarbon solvent (commercially available under the trade designation Solvesso 100 from Exxon Chemical). The solution of the polyester resin G was prepared by dissolving in 40 parts by weight of this aromatic hydrocarbon solvent. Subsequent to the addition of the epoxy resin to the polyester resin solutions, 0,1 parts by weight of benzyl diethylamine for polyester resins A-F, and 0,3 parts by weight triphenyl phosphine for polyester resin G, were added and the reaction mixtures kept at a temperature of about 150°C until the block copolymer formed had the acid number as set forth in Table II. Also set forth in Table II are other characteristics of the so-prepared polyester/epoxy block copolymers. To the solutions of the polyester/epoxy block copolymers thus prepared were added ethyl ether of ethylene glycol (BC1-BC9), methoxy propanol (BC10) and the previously used aromatic hydrocarbon solvent in amounts such that solutions were obtained having a solids content of about 40% by weight of the block copolymer in a mixture of equal parts by weight of the two solvents. Comparative Resin 11 for Comparative Example C11 Comparative Example C11 was based upon an epoxy resin (CR11) which was the diglycidyl ether of Bisphenol A with an epoxide equivalent of about 2400 to 4000 (commercially available under the trade designation Epon 1009 from Shell Chemical). A 40% solution of the epoxy resin was prepared by dissolving, at 100°C, 40 parts by weight of the epoxy resin into a solvent mixture comprising 36 parts by weight of the aforementioned aromatic solvent and 24 parts by weight methoxypropanol. First Coating Layer Compositions (Primer First Coating Layer) for Examples 1-10 and Comparative Examples C11 and C12. To obtain the first coating layer compositions used in Examples 1-10 and Comparative Example 11, the correspondingly numbered polyester/epoxy block copolymers and comparative resin, in the amounts as set forth in Table III (in parts by weight solids), and in the form of the previously described solutions, were homogenously mixed with the other components in the amounts (in parts by weight) as listed in Table III. The crosslinking agent was the adduct of hexamethylene diisocyanate and 1 mole of water (commercially available under the trade designation Desmodur N from Bayer AG), blocked with methyl ethyl ketoxime, in methoxypropanol acetate (NVM 75%). First Coating Layer Resin Type Resin Amount Titan. Diox. Stront. Chrom. Silica Cross. Agent Meth. Prop. Arom. Solv. P1 BC1 42,7 15,9 2,0 2,5 3,7 13,3 19,9 P2 BC2 42,7 15,9 2,0 2,5 3,7 13,3 19,9 P3 BC3 42,7 15,9 2,0 2,5 3,7 13,3 19,9 P4 BC4 42,7 15,9 2,0 2,5 3,7 13,3 19,9 P5 BC5 42,7 15,9 2,0 2,5 3,7 13,3 19,9 P6 BC6 42,7 15,9 2,0 2,5 3,7 13,3 19,9 P7 BC7 42,7 15,9 2,0 2,5 3,7 13,3 19,9 P8 BC8 42,7 15,9 2,0 2,5 3,7 13,3 19,9 P9 BC9 42,7 15,9 2,0 2,5 3,7 13,3 19,9 P10 BC10 43,9 19,2 2,4 3,0 3,4 11,3 16,9 CP11 CR11 42,7 15,9 2,0 2,5 3,7 13,3 19,9 The first coating layer compostion for Comparative Example 12 (CP12) was a standard coil coating currently used in the precoating industry as a primer for steel or zinc coated steel. This primer is based upon an urea formol epoxy precondensate, which is commercially available under the trade designation 7E1328 from Akzo Coatings France. The ten primer first coating layers (P1-P10) based upon the polyester/epoxy block copolymers and two comparative primers (CP11 and CP12) were applied as the first coating layer onto a hot dip galvanized steel substrate (commercially available under the trade designation Extragal Z100 from Sollac). After cleaning and surface treatment of the metal substrate using alkaline degreasing chromotation (Granodine 93CF from CFPI chromic zinc), the primers were applied by roller coating, then cured at a Peak Maximum Temperature of 242°C with a dwell time of 30″. Each dry film thickness was about 5µm. Over this primer first coating layer was applied a primer second coating layer of a polyurethane based coating (a polyester polyol crosslinked with an isocyanate) commercially available under the trade designation PZ2000 from Akzo Coatings. This primer second coating layer was applied by roller coating over the dried primer first coating layer, then curing at a Peak Maximum Temperature of 242°C with a dwell time of 35″. The dry film thickness of the second primer layer was about 20µm. The resulting coated metal panels were evaluated for the performance level of the flexibility and capability of deep draw, as exemplified by the following tests: (1) the Erichsen indentation test - DIN 53 156; (2) the reverse impact test - ASTM D 2794-1982 in cm. kg (in-lb); (3) the double-draw test - RNUR (Régie Nationale des Usines Renault) D.111 700; (4) the T-Bend test - European Coil Coating Association (expressed in ratings T0, T1, T2, etc. - a value of 0 denotes excellent flexibility and a value of 4 acceptable flexibility); and (5) the stone chipping resistance - RNUR D.24 1702. Corrosion resistance was evaluated by the salt spray test in accordance with ASTM B 117, with results reported in mm delamination on the scribe. Corrosion resistance after deformation was also evaluated by the following procedure: the coated panels were submitted to a 20% uniaxial stretching, then a 25mm diameter hole punched in the middle. The resulting panels were then exposed according to the 3-C test of RNUR D.17 1686. The results are expressed in mm delamination obtained on the edges of the hole after 5 cycles. The results of the testing are presented in Table IV below. EX First Coating Layer Erich. Indent. Rever. Impact Doub. Draw T-Bend Stone Chip Corr. Res. Corr.Res. After Deform. 1 P1 9,0 184(160) Pass 0,5 2 2 1 2 P2 9,2 184(160) Pass 0,5 2 1,5 1,5 3 P3 9,6 184(160) Pass 0,5 2 2 2 4 P4 9,4 184(160) Pass 0,5 1,5 1 1 5 P5 9,8 184(160) Pass 0,5 2 2 2,5 6 P6 10,0 184(160) Pass 0,5 2 1 2 7 P7 9,9 184(160) Pass 0,5 2 1 1 8 P8 9,2 184(160) Pass 0,5 2 1,5 1,5 9 P9 9,5 184(160) Pass 0,5 2 2 2 10 P10 10,0 184(160) Pass 0 2 <1 <1 C11 CP11 8,7 184(160) Fail 1,5 3,5 7 4 C12 CP12 8,7 161(140) Fail 1,5 3,5 8 5 The results of testing, as shown in Table IV, demonstrate that preprimed metal surfaces prepared using the coating materials of the present invention (and particularly having a first coating layer composition of the type disclosed herein) can be double drawn (formed) in a manner not possible using the present commonly used metal primers. In addition, the corrosion resistance shows an unexpected improvement when the preprimed metal surfaces of the present invention are compared with conventional preprimed surfaces. After deformation, the preprimed metal surfaces of the present invention also showed substantially better corrosion resistance than the metal surfaces preprimed with conventional primers. The flexibility and stone chip resistance of the preprimed metal surfaces of the present invention are significantly better than the flexibility and stone chip resistance of conventionally primed metal surfaces. Example 13 and Comparative Example C14 Example 7 and Comparative Example C12 were repeated in their entirety, except that a particular polyester based coating, as described below, was applied as the second primer layer in place of the polyurethane based coating described above. The polyester resin for the polyester based coating was prepared by charging, to a suitable vessel maintained under nitrogen atmosphere, 24,8 parts by weight polypropylene glycol, 12,4 parts by weight neopentyl glycol and 0,05 parts by weight dibutyltin oxide as catalyst. The temperature of the contents of the vessel was raised to 110°C, then 22,1 parts by weight adipic acid, 39,8 parts by weight isophthalic acid and 0,9 parts by weight trimellitic acid were further charged. The temperature was then raised to 220°C and maintained until the acid value fell below 30. The reaction water was then removed by azeotropic distillation with an aromatic hydrocarbon solvent (commercially available under the trade designation Solvesso 100 from Exxon) until the acid value fell below 3, at which point the mixture was cooled to about 150°C. Finally, 33,4 parts by weight aromatic hydrocarbon solvent (commercially available under the trade designation Solvesso 150 from Exxon) and 22,9 parts by weight methoxypropanol acetate were added to bring the solids content of the resulting solution to 60,1%. A grey polyester based coating was prepared from the above polyester resin solution by mixing the following components in the amounts as set forth below in Table V (numbers are in parts by weight): Components Parts Components Parts Polyester resin (solids) 46,0 Carbon black 1,0 Crosslinker 6,4 Titanium dioxide 32,7 Catalyst 1,0 Solvent 4,0 Flow agent 0,1 Methoxy propanol acetate 2,5 Butyl acetate 6,3 The crosslinker was a melamine resin commercially available under the trade designation Cymel 303 from American Cyanamid. The catalyst was a blocked acid catalyst commercially available under the trade designation Cycat 405 from American Cyanamid. The flow agent was a silicone additive commercially available under the trade designation Silicone L.75 from Union Carbide Corp. The solvent was a mixed aromatic solvent commercially available under the trade designation Solvesso 200 from Exxon Chemical. The resulting coated metal panels were evaluated in the manner of Examples 1-10 and Comparative Examples C11 and C12. The results are presented below in Table VI. EX Primer Erich. Indent. Rever. Impact Doub. Draw T-Bend Stone Chip Corr. Res. Corr.Res. After Deform. 13 P7 10,2 138(120) Pass- 1,5 1,5 0 1 C14 CP12 8,0 92( 80) Fail 2,5 4 4 4 Again, the results of testing, as shown in Table VI, demonstrate that the preprimed metal surface prepared using the coating materials and method of the present invention permitted formation (double draw) not possible using a conventional priming material as a prepriming coating. In addition, corrosion resistance is substantially improved, as is stone chip resistance, by use of the present invention. Example 15 Example 7 was repeated in its entirety except that, as the metal substrate, was utilized an electrogalvanized steel (70/70 g/m², commercially available from Sollac). The results of the testing are presented below in Table VII. EX Primer Erich. Indent. Rever. Impact Doub. Draw T-Bend Stone Chip Corr. Res. Corr.Res. After Deform. 15 P7 10,0 184(160) Pass 0,5 1,5 1 1 The results shown in Table VII indicate that the prepriming composition and method of the present invention provided the improved performance previously discussed whether the metal surface being preprimed is hot dipped galvanized steel or electrogalvanized steel.

Claims: A preprimed metal substrate comprising a metal substrate coated with a primer, characterized in that the primer comprises: (1) a first coating layer applied onto said metal substrate, said first coating layer comprising a coating composition based upon, as a binder, a hydroxyl groups-containing block copolymer built up from (A) one or more blocks of a carboxyl-terminated polyester resin, and (B) one or more blocks of an epoxy resin; and (2) at least one flexible subsequent coating layer applied onto said first coating layer. The preprimed metal substrate according to claim 1, characterized in that the carboxyl-terminated polyester resin comprises the polycondensation product of one or more carboxylic diacids and one or more difunctional hydroxy compounds, wherein the carboxylic diacid is selected from aromatic carboxylic diacids, aliphatic carboxylic diacids and mixtures thereof. The preprimed metal substrate according to claim 2, characterized in that carboxylic diacid is selected from aromatic carboxylic diacids. The preprimed metal substrate according to claim 3, characterized in that the aromatic carboxylic diacid is selected from terephthalic acid and isophthalic acid. The preprimed metal substrate according to claim 1, characterized in that the carboxyl-terminated polyester resin comprises an acid number of from 10 to 140, an hydroxyl number not higher than 2 and a number average molecular weight of from 800 to 10000. The preprimed metal substrate according to claim 1, characterized in that the epoxy resin has an epoxy functionality ranging from 1,5 to 2,5, and an epoxy equivalent weight of from 100 to 2000. The preprimed metal substrate according to claim 6, characterized in that the epoxy resin has an epoxy functionality of from 1,8 to 2,2, an epoxy equivalent weight of from 100 to 700, and a number average molecular weight of from 150 to 1250. The preprimed metal substrate according to claim 1, characterized in that the hydroxyl groups-containing block copolymer is built up from 3 to 11 blocks (A) and 2 to 10 blocks (B), or from 2 to 10 blocks (A) and 3 to 11 blocks (B). The preprimed metal substrate according to claim 1, characterized in that the hydroxyl groups-containing block copolymer has a number average molecular weight of from 3000 to 80000, and an acid number not higher than 23. The preprimed metal substrate according to claim 9, characterized in that the hydroxyl groups-containing block copolymer has a number average molecular weight of from 5000 to 30000, and an acid number in the range of from 0 to 15. The preprimed metal substrate according to claim 1, characterized in that the first coating layer further contains a crosslinking agent for the hydroxyl groups of the hydroxyl groups-containing block copolymer. The preprimed metal substrate according to claim 1, characterized in that the first coating layer is pigmented. The preprimed metal substrate according to claim 1, characterized in that the at least one flexible subsequent coating layer has a glass transition temperature ranging from 30°C to 70°C. The preprimed metal substrate according to claim 5, characterized in that the at least one flexible subsequent coating layer comprises a coating selected from a polyester polyol crosslinked using a polyisocyanate and a polyester polyol crosslinked using a melamine. The preprimed metal substrate according to claim 1, characterized in that the metal substrate comprises a metal sheet. The preprimed metal substrate according to claim 1, characterized in that the first coating layer comprises a dry layer thickness up to 15 µm, the at least one flexible subsequent coating layer comprises a dry layer thickness up to 30 µm, and the total primer dry layer thickness ranges from 15 µm to 45 µm. The preprimed metal substrate according to claim 16, characterized in that the first coating layer comprises a dry layer thickness of from 3 µm to 10 µm, the at least one flexible subsequent coating layer comprises a dry layer thickness of from 12 µm to 25 µm, and the total primer dry layer thickness ranges from 20 µm to 30 µm. A method of prepriming a metal substrate by applying a primer layer thereon, characterized in that the primer layer comprises (1) a first coating layer applied onto the metal substrate, and (2) at least one flexible subsequent coating layer applied onto the first coating layer, as set forth in any one of claims 1-17. A method of producing a preprimed, formed metal substrate by applying a primer layer to the metal substrate then forming the preprimed metal substrate, characterized in that the primer layer comprises (1) a first coating layer applied onto the metal substrate, and (2) at least one flexible subsequent coating layer applied onto the first coating layer, as set forth in any one of claims 1-17. The formed metal substrate produced by the method of claim 19.

Inventors: MAZE ETIENNE GEORGES, TOURNILLON CHRISTINE MARIE JAN, MAZE, ETIENNE GEORGES, TOURNILLON, CHRISTINE MARIE JANY SUZANNE
Applicants: AKZO NOBEL NV, AKZO NOBEL N.V.
Application year: 1990
Main classification: C08G59
IPC codes: B05D7, C09D163, B32B15