Method of manufacturing a semiconductor memory

Abstract: A method of manufacturing a semiconductor memory includes the steps of, on a semiconductor substrate having underlayer wiring which is composed of a plurality of gate portions provided with side walls and a diffused region between the gate regions, i) forming a layer insulating film which is smaller in thickness in the diffused region than the side walls of each of the gate regions and which is made of a material etched more easily than the material of the semiconductor substrate; ii) depositing a conductive layer of a material etched more easily than the layer insulating film, over the entire surface of the layer insulating film; iii) removing the conductive layer simply except a portion where a contact hole is to be formed in the diffused region, by etching with a pattern film for forming the contact hole; iv) depositing an insulating film and a pattern film for forming the contact hole over the entire surface again; and v) removing the insulating film, the remaining conductive layer and the layer insulating film by etching one after another to form the contact hole extending to the diffused region in self-alignment.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of manufacturing a semiconductor memory, and more particularly, it relates to a method of manufacturing a semiconductor memory of wiring width 0.8 µ m or under, with high yields. 2. Description of the Prior Art A prior art method and its disadvantages will be described with reference to diagrams for explaining structures of main parts of a semiconductor substrate. In the prior art, as shown in Figs. 5(a) and 5(b), after second underlayer wiring 73 is formed in a semiconductor substrate 71 which has first underlayer wiring (diffused layer) 72 formed by diffusing, a layer insulating film 74 of SiO 2 or the like is deposited; and thereafter, a contact hole 74a is formed by etching or the like. Upper wiring 75 is formed over the contact hole 74a; and thus, the wirings are electrically connected between the upper and lower layers. In particular, in the case where the overlayer wiring 75 is made of a metal material like A1 while the first under layer wiring 72 is formed of the diffused layer formed in the substrate 71, it is likely that the metal wiring 75 and the substrate 71 are short-circuited in a part shown by an arrow Q in Fig. 6 when the contact hole 74a and the diffused layer, or the first underlayer wiring 72, are out of alignment. However, as shown in Fig. 7, such short-circuiting can be prevented if the surface of the substrate which is exposed because of the contact hole formed for the purpose of the connection with the first underlayer wiring 72 is covered with a polycrystalline Si film 76 doped with an impurity at high concentration so that the polycrystalline Si film 76 is interposed between the metal wiring 75 and the substrate 71. Specifically, the short-circuiting between the substrate 71 and the metal wiring 75 is prevented by covering the end of the diffused region exposed in the contact hole 74a with the polycrystalline Si film 76 which is doped with an impurity at high concentration. This is because an impurity with which the polycrystalline Si film 76 is doped at high concentration is diffused towards the substrate, so that no short-circuiting is caused even if the polycrystalline Si film 76 is deposited on the end of the diffused region. Two problems arise in the above-mentioned way of covering the contact hole 74a with the the polycrystalline Si film 76: 1) The distance between contact holes cannot be reduced. For example, a case in which the polycrystalline Si film 76 covering the substrate 71 in the contact holes is etched will be discussed. When the polycrystalline Si film 76 is etched under the state where a part of the substrate is exposed because of the misregistration of the photoresist determining the configuration of the polycrystalline Si film 76 to be etched, the exposed portion is etched away as shown by an arrow R in Fig. 8 because the substrate is of silicon. The etching of the substrate may cause drawbacks such as a junction leakage and the like. Hence, the end of the contact hole 74a in the polycrystalline Si film 76 must be positioned a distance d (0.1 µm to 0.3 µm) from the region where the substrate is exposed [see Fig. 11]. On the other hand, the lowermost limit of the distance between polycrystalline Si patterns is determined by the resolution of a light exposing projector. Thus, the minimum distance between the contact holes is about double the distance d (0.2 µm to 0.6 µm) added to the resolution (about 0.6 µm) of the exposing projector. In other words, approximating a distance L between the contact holes 74a, 74a [see Fig. 11] to the resolution (about 0.6 µm) of the exposing projector is impossible. 2) It is difficult to form the contact holes in self-alignment. As shown in Fig. 9, the layer insulating film 74 is deposited on the second underlayer wiring 73, and then a portion where a contact hole is to be formed is etched down by the depth corresponding to the thickness of the layer insulating film 74 to form the contact hole on the surface of the substrate in self-alignment relative to the second underlayer wiring 73. However, when a plurality of overlayer wiring layers 75 exist to connect with the substrate 71, layer insulating films 74, 77 and 78 and a polycrystalline Si film must be deposited on the substrate 71 as many times. If the plurality of layers are deposited in such a manner, the layer insulating film on the underlayer wiring is substantially thicker than the layer insulating film on the contact hole to fill the contact hole with the insulating film, so that it is impossible to form the contact holes in self-alignment. The documents EP-A-0 337 436 and JP-A-62 86853 disclose semiconductor devices in which capacitors are formed in contact holes between gate portions on a substrate. To overcome the above-mentioned problems, the present invention is directed to a method of manufacturing a semiconductor memory in which a contact hole reliably making a contact with a diffused region of the semiconductor substrate can be formed while good yields of semiconductor memories can be attained even if the accuracy in the alignment of patterns in light projection and exposure is unsatisfactory. According to the present invention, there is provided a method of forming a contact opening to a predetermined region of a semiconductor substrate having underlayer wiring which is composed of a plurality of gate portions provided with side walls and a diffused region between the gate portions, said method comprising: i) forming over said region a first layer of an insulating material which is thinner in a direction perpendicular to the substrate than the side walls of each of the gate portions; characterised by the steps of: ii) forming a conductive layer over said insulating layer, iii) removing portions of the conductive layer so that a portion having an upwardly extending side remains where said contact opening is to be formed, iv) forming a second layer of insulating material over the first layer and over said conductive layer portion so that an upwardly extending portion of the second insulating layer is formed on said upwardly extending side, and v) forming the contact opening through said second insulating layer, by removal of said conductive layer portion and etching the first insulating layer, such that the contact opening is formed in self-alignment relative to said underlayer wiring and the upwardly extending portion of the second insulating layer forms an upward projection at an upper part of the contact opening. Preferably, a further contact is formed to a further diffused region between the gate portions of the substrate, by the steps of: etching the first insulating layer to form a further contact hole extending to the further diffused region in self-alignment; depositing said conductive layer over the further contact hole; removing the conductive layer so that a further portion thereof remains where the further contact is to be formed in the further diffused region, so that the further contact hole is filled by the further portion; depositing said second insulating layer over the further portion such that the further portion becomes a buried layer and forming a through-hole to the buried layer through the second insulating layer. Preferably, the semiconductor substrate is a Si substrate, the first insulating layer is a SiO 2 film, and the conductive layer is a polysilicon layer. Specific embodiments of the present invention will now be described with reference to the accompanying drawings, in which:- Fig. 1 is a diagram for explaining the steps of forming a capacitor electrode in a manufacturing method of an embodiment according to the present invention; Figs. 2(a) and 2(b) are diagrams for explaining a configuration of a main portion, showing a contact hole for making a contact with the capacitor electrode and a capacitor insulating film of the embodiment; Fig. 3 is a diagram for explaining the steps of forming a capacitor electrode in a manufacturing method of another embodiment according to the present invention; Fig. 4 is a diagram for explaining a configuration of a main portion, showing a memory formed in accordance with the embodiment; Fig. 5(a) is a diagram for explaining a configuration of a prior art semiconductor memory, showing a contact hole; Fig. 5(b) is a sectional view taken along the line A - A' of Fig. 5(a); Fig. 6 is a diagram for explaining drawbacks of the prior art semiconductor memory, showing its configuration; Fig. 7 is a diagram for explaining an improved prior art semiconductor memory, showing its configuration; Figs. 8 through 11 are diagrams for explaining drawbacks the improved prior art semiconductor memory, showing its configuration; and Fig. 12 is a diagram for explaining the accuracy of the alignment in an exposure device in the steps of forming a contact hole without a self-alignment method. PREFERRED EMBODIMENTS The most significant characteristic of the present invention is that a contact hole extending to a diffused region in a memory cell is formed in self-alignment. In the present invention, first, on a semiconductor substrate a layer insulating film of a material which is more easily etched than the material of the semiconductor substrate is formed. For example, a SiO 2 film is formed on a Si substrate. Then, a conductive layer of a material which is more easily etched than the material of the layer insulating film is deposited over the entire surface of the layer insulation film; and eventually, the conductive layer and layer insulating film in a portion where a contact hole is to be formed are removed by etching one after another to form the contact hole extending to the diffused region. In this way, the contact hole can be formed in self-alignment. The inventors of the present invention apply the above-mentioned method of forming a contact hole to the formation of a contact hole for forming a capacitor electrode of a memory cell to attain a high integration of a memory and good yields of memories. An essential requirement in the present invention is that the insulating film layer is thinner than side walls of a gate portion. For example, an example is shown in Fig. 12 where a contact hole is formed in a layer insulating film without self-alignment as in the present invention. In Fig. 12(a), a layer insulating film 82 is formed on a semiconductor substrate having underlayer wiring which is composed of a plurality of gate portions 81 having side walls 80 and a diffused region. In this case, the distance x between the gates is 1.1 - 1.2 µm while the length G of the gate is 0.8 µm or under, desirably 0.5 - 0.6 µm. Then, as shown in Fig. 12(b), a resist film 83 for forming a contact hole is formed. Then, the layer insulating film is patterned by light projection and exposure, and reactive ion etching to form a contact hole 83a. The diameter K of the contact hole 83a is 0.3 µm. In the above-mentioned method of forming a contact hole, it is known that the distance x between the gates cannot be reduced to 1.1 - 1.2 µm or under because of the accuracy of the alignment of the exposure device. Thus, it is necessary to arrange in advance that the adjacent gates are disposed with the distance x of 1.1 - 1.2 µm or over before the contact hole is formed. On the other hand, in the present invention, the distance x can be reduced to 0.5 - 0.6 µm. This results in high integration of the memory. For that purpose in the present invention, as shown in Fig. 1(b), a conductive film 8 is formed for increasing in a margin of the alignment in forming a contact hole 40 [see Fig. 1(e)]. The conductive film 8 also functions as a dummy, which is removed when the contact hole is formed. Thus, after the removal of the conductive film 8, a capacitor electrode can increase in area for wiring by an area the conductive film covers. Since the conductive film 8 is formed in forming the contact hole 40 to increase in a margin of the alignment, the alignment of patterns in a projection and exposure may be performed with less accuracy; and therefore, good manufacturing yields can be expected. The contact hole 40 in the present invention is formed, for example, in the following way: A region R where a contact hole is to be formed is removed by an anisotropic reactive ion etching (RIE) with a mask of a resist pattern 50 formed by a projection and exposure, and then, a second layer insulating layer 9, the conductive film 8 and a first layer insulating film 27 are removed one after another by etching. The bottom face of the contact hole 40, as shown in Fig. 1(e), defines a interface 1a to the surface of one of diffused regions, while an upper opening 1b, or the rim, of the contact hole 40 extends from a second insulating layer 29 to project upwards; a large level difference H between the upper opening 1b and the bottom face 1a is observed [see Fig. 1(e), Fig. 2]. The conductive film 8 serving as a dummy [see Figs. 1(c) and 1(d)] is removed when the contact hole 40 is formed; instead, an area for wiring can be accordingly increased in the depthwise direction. Thus, capacitor electrode overlayer wiring provided along the inner wall of the contact hole can increase its area of wiring. In other words, creating a large level difference in the contact portion between the capacitor electrode and the diffused region increases the area of the capacitor electrode. Preferably, the conductive layer in the present invention may be the one that could be removed more rapidly than a SiO 2 film by anisotropic etching like RIE; the best example is a polycrystalline silicon film. A silicide film of WSi or the like overlaid with a poly Si film may be used. The conductive layer is, for example, removed by anisotropic reactive ion etching (RIE) with a photoresist pattern formed by the projection and exposure, and a conductive film and a conductive buried film are formed. In another aspect of the present invention, a contact hole for connecting a bit line through its opening and a buried film to a diffused region can be formed in self-alignment. As a result, the cell can be miniaturized. In this case, the buried film is useful for increasing a margin of the alignment. In still another aspect of the present invention, a conductive film (e.g., a polysilicon film) which is etched more rapidly is deposited on a layer insulating film and patterned; thereafter, an insulating film is formed to form a contact hole. In this way, the contact hole can be assuredly formed in an area where the contact hole should be formed. The contact hole is filled with polycrystalline Si of high impurity concentration; and thus, when wiring formed by depositing conductive material on the semiconductor substrate is electrically connected to wiring formed by diffusion or the like in the semiconductor substrate, the wiring of the semiconductor substrate can be reliably drawn out on the semiconductor substrate. In this way, a memory with reliable connection of wiring can be created. The present invention will be explained below in detail in conjunction with embodiments shown in the drawings; it is not intended that the present invention be limited to the precise form disclosed therein but rather is defined by the appended claims. [Embodiment 1] Referring to Fig. 1(g), a DRAM (MOS transistor) is mainly composed of a Si substrate 1 of which elements are isolated by a SiO 2 thermal oxidation film 2 having a thickness of approximately 0.4 µm, a polycrystalline Si film (gate wiring serving as lead) 4 formed on the substrate 1 with a thickness of about 300 nm (3000 Å) by diffusing phosphorus (P) at high concentration through a gate oxidation film 3 having a thickness of about 10nm (100 Å), SiO 2 spacers 5 and 6 formed by anisotropic ion reactive etching (RIE) after a deposition of SiO 2 on the upper and side faces of the gate wiring by CVD, a layer insulating SiO 2 film 27 formed by CVD to cover it and to have a thickness of about 0.2 µm, a contact hole 40 formed on one of diffused regions, R, with a large level difference H of about 1.2 µm between the upper opening 1b and the bottom face 1a [see Fig. 1(e)], a bit line connecting contact-hole 242 formed on the other of the diffused regions, K, through the polycrystalline Si film 28 having a thickness of about 0.5 µm, an SiO 2 film 29 deposited on the Si substrate by CVD with a thickness of about 0.1 µm and a capacitor electrode overlayer wiring 41 provided with the contact hole interposed, both of which are provided on a region except the diffused region K, a SiO 2 film 13 formed by CVD with a thickness of about 0.1 µm and a fourth layer insulating film 14 formed by CVD with a thickness of about 0.3 µm for flattening, both of which are deposited on the SiO 2 film 29 one after another, and overlayer bit-wiring 15 formed by light projection and exposure and anisotropic RIE after a deposition of a WSi film of about 0.3 µm thickness on the SiO 2 film 14 including an opening 242 above a contact hole 42. The capacitor electrode 41 is composed of a capacitor lower electrode 10 which is formed in the lower layer by depositing a polycrystalline Si of about 50nm (500 Å) thickness film doped with phosphorus (P) at high concentration by CVD and patterning it by light projection and exposure, and anisotropic RIE, and a capacitor upper electrode 12 which is formed in the upper layer through a SiN capacitor insulating film 11 of about 8nm (80 Å) thickness by light projection and exposure, and anisotropic RIE after a deposition of a polycrystalline Si film dcped with P at high concentration of about 150 nm (1500 Å) thickness. Then, manufacturing methods will be explained. (i) First, all over the Si substrate 1 which includes a gate electrode 4 having the upper side 5 of the spacer of SiO 2 and the side face (side wall) 6 of the spacer of SiO 2 , a SiO 2 film serving as an insulating layer and a resist layer (not shown) are deposited one after another [see Fig. 1(a)], and a resist film of a specific pattern is formed; thereafter, (ii) with a mask of the resist film, only the portion of the SiO 2 film 27 on the diffused region K is removed by anisotropic RIE until the surface lllb of the diffused region K is partly exposed. After that, all over the Si substrate 1 including the remaining SiO 2 film 27, a polycrystalline Si layer (not shown) serving as a conductive layer of a material etched more rapidly than the SiO 2 film 27 and a resist layer (not shown) are deposited one after another, and a resist film of a specific pattern is formed; thereafter, (iii) with a mask of the resist film, the conductive layer is etched so that the conductive film 8 remains through the SiO 2 film 27 on the diffused region R while the conductive buried film 28 electrically connecting to the diffused region K remains on the diffused region K [see Fig. 1(b)]. (iv) All over the first layer insulating film 27 including the conductive film 8 and the conductive buried film 28, a SiO 2 film 9 and a resist layer (not shown) are deposited one after another [see Fig. 1(c)], and a resist film 50 of a specific pattern for forming a contact hole is formed [see Fig. 1(d)]; thereafter, (v) with a mask of the resist film 50, the SiO 2 film 9 and conductive film 8 on the diffused region R are etched one after another, and further, the SiO 2 film 27 just under the conductive film 8 is removed until it is partly exposed on the interface la to the substrate 1 in the diffused region R to form the contact hole 40 and the SiO 2 film 29 [see Fig. 1(e)]. (vi) Then, on the Si substrate 1 except the diffused region region K or other, the capacitor 41 is formed [see Fig. 1(f)]. The capacitor 41 is composed of a capacitor lower electrode 10 which is formed in the lower layer by depositing a polycrystalline Si of about 50nm (500 Å) thickness film doped with phosphorus (P) at high concentration by CVD and patterning it by light projection and exposure, and anisotropic RIE, and a capacitor upper electrode 12 which is formed in the upper layer through a SiN capacitor insulating film 11 of about 8nm (80 Å) thickness by light projection and exposure, and anisotropic RIE after a deposition of a polycrystalline Si film doped with P at high concentration of about 150nm (1500 Å) thickness. Thus, the contact hole 40 is filled with the capacitor upper electrode 12 and the capacitor lower electrode 10. (vii) Moreover, all over the Si substrate 1 including the capacitor 41, the SiO 2 film 13 and the SiO 2 film 14 for flattening are deposited one after another, and then, the SiO 2 films 13, 14 on the conductive buried film 28 are removed to form a contact hole (bit line contact hole) 242. (viii) All over the SiO 2 film 14 including the contact hole, the bit line 15 of a specific pattern is formed [see Fig. 1(g)]. In this way, a DRAM memory cell is configured. In this embodiment, after the word line 4 is formed, the poly Si patterns 8, 28 are formed on the SiO 2 film, and moreover, the SiO 2 film 9 is deposited. After that, the SiO 2 films 27, 9 in a portion where a contact hole is to be formed, in a region which is to be a capacitor electrode and one of the diffused regions of the substrate, and the conductive film 8 as a dummy in the poly Si patterns are removed by etching, and then, the capacitor 41 is formed. As a result, the capacitor 41 increases in its electrode area. As the area of the capacitor electrodes increases, the amount of electric charge accumulated at the identical writing voltage is increased; and the reliability against a soft error caused by an incident of α particle is enhanced. The contact holes 40, 42 are formed on both the diffused layers by providing the poly Si patterns 8, 28, so that a margin of the alignment in forming the contact holes 40, 42 in the capacitor electrode contact portion and bit line contact portion can be improved. As has been described, according to the present invention; (i) good yields in manufacturing can be expected because the alignment of the patterns in a projection and exposure can be performed with less accuracy, and (ii) the area of the capacitor electrodes can be increased by using a level difference between the contact portions in the capacitor electrode and the diffused layer. Because of an increase in the area of the capacitor electrodes, the resultant amount of accumulated electric charge can be increased under the identical writing voltage, and the reliability against a soft error can be enhanced. [Embodiment 2] In Fig. 3(a), a thermally oxidized gate insulating film 113 of about 10nm (100 Å) thickness is formed on a semiconductor substrate 111 of which elements are isolated by a thermal oxidation film 112 of about 0.4 µm, and gate wiring of a MOS transistor and second underlayer wiring 114 are formed on the gate insulating film 113 with a polycrystalline Si film of about 30nm (3000 Å) thickness diffused with phosphorus at high concentration. On the upper and side faces of the wiring 114, spacers 115, 116 of SiO 2 are formed, and first underlayer wiring 117 is formed in the substrate 111 by a diffusion with masks of the spacers 115, 116. The spacers 115, 116 are formed in the following manner: SiO 2 is deposited by CVD, and thereafter, it is subjected to an anisotropic etching, such as reactive ion etching (RIE) or the like. A thin SiO 2 film 118 of about 0.2 µm for insulating layers from each other is deposited by CVD on the wirings covered with the spacers 115, 116. As shown in Fig. 3(b), a polycrystalline Si film 119 of about 0.5 µm thickness which is different in a period of time required for etching from SiO 2 is deposited on the substrate, covering the SiO 2 film 118, and then etched by an anisotropic etching, such as RIE or the like, with a photoresist pattern formed by light projection and exposure, so as to form a dummy pattern in a portion X where a contact hole is necessary. A region between the wirings where no contact hole is necessary in this process has the insulating film 118 shown by reference character Y in Fig. 3(c). After that, a thin SiO 2 film 120 of about 0.1 µm thickness is deposited by CVD, and then, the surface of the substrate is etched back by an anisotropic etching, such as RIE or the like, to the depth corresponding to the thickness of the SiO 2 film 120, as shown in Fig. 3(c). Then, the exposed polycrystalline Si film 119 is removed by an isotropic etching, such as plasma etching or the like [see Fig. 3(d)]. Moreover, the SiO 2 film 118 covering the surface of the substrate is etched back by an anisotropic etching, such as RIE or the like, to the depth corresponding to the thickness of the SiO 2 film 118. With these steps, the substrate 111 is exposed in the portion X where the contact hole making a contact with the overlayer wiring is to be formed without losing the insulating film in the portion Y where no contact hole is necessary, and the contact hole is formed in self-alignment relative to a diffused region 117. After that, a polycrystalline Si film 121 of about 0.4 µm thickness which is doped with phosphorus at high concentration is deposited by CVD as shown in Fig. 3(e), and then etched back by an anisotropic etching, such as RIE or the like, to the depth corresponding to the thickness of the polycrystalline Si film 121, so as to complete the polycrystalline Si film 121 with which the contact hole is filled, as shown in Fig. 3 (f). After etching back the polycrystalline Si film 121, a SiO 2 film 122 of about 0.2 µm thickness is formed on the surface of the substrate by CVD. With the above-mentioned steps, the polycrystalline Si buried layer 121 covering the contact hole on the diffused region is formed in self-alignment. The pattern of the polycrystalline Si film 121 is simultaneously formed in every portion where the contact hole making a contact between the multi-layer overlayer wiring and the substrate is to be formed, so that the polycrystalline Si buried layer is formed in every contact hole in self-alignment relative to the second underlayer wiring. The buried layer 121 close to the substrate is directly in contact with the diffused region 117 on the surface of the substrate to attain an electrical connection. After the buried layer 121 is formed, a semiconductor device having a capacitor and bit line, which are essential for forming a memory cell, formed in a multi-layer wiring configuration on the semiconductor substrate, as shown in Fig. 4. To form the capacitor, a thin CVD SiO 2 film 122 which covers a buried layer 121b to connect with the capacitor is removed, and then a capacitor lower electrode 131 connected to the buried layer 121b in the portion from which the SiO 2 film 122 was removed is formed. Then, a capacitor insulating film 132 is formed, covering the lower electrode 131; moreover, a capacitor upper electrode 133 is deposited. With the above-mentioned deposition step, an insulating material is formed as an insulating film layer 134 on the surface of the semiconductor substrate in which memory cell capacitor elements are formed, and bit line 136 is formed through the insulating film 134. The bit line 136 is formed of a multi-layer conductor of polycrystalline Si wiring 136a and a metal having a high fusing point and is connected to the buried polycrystalline Si film 121a in a portion where the connection to the wiring formed in the semiconductor substrate is necessary. In the connection process, since the wiring formed in the substrate by diffusion has been drawn out on the substrate by the buried layer 121a, a sufficient contact area can be retained for an assured electrical connection. Multi-layer wiring including four layers or over is employed in a high integrated LSI of 0.6 µm wiring width, such as a 16 MDRAM and the like, and the wiring to be connected to the substrate also includes two layers or over. In such a semiconductor configuration, also, the pattern of the polycrystalline Si film 121 is simultaneously formed in every portion where the contact hole making a contact between the multi-layer overlayer wiring and the substrate is to be formed, so that the polycrystalline Si buried layer is formed in every contact hole in self-alignment relative to the gate wiring. The semiconductor device shown in Fig. 4 has a configuration having underlayer wiring which is a diffused layer formed in the substrate, and overlayer wiring which consists of a capacitor lower electrode of a memory cell and a bit line. As previously mentioned, according to the present invention, a contact hole which makes a contact between multi-layer underlayer and overlayer wirings in a high integrated LSI having a wiring width of 0.6 µm or under can be reliably formed at high density. The contact hole between the underlayer and overlayer wirings is formed in self-alignment relative to the wirings, so that the alignment of the patterns in a projection and exposure can be performed with less accuracy. Thus, good yields in manufacturing can be expected. The present invention is suitable especially for a semiconductor memory which requires multi-layer wiring.

Claims: A method of forming a contact opening to a predetermined region (R) of a semiconductor substrate (1; 111) having underlayer wiring which is composed of a plurality of gate portions (4; 114) provided with side walls (6; 116) and a diffused region (R; 117) between the gate portions, said method comprising: i) forming over said region a first layer of an insulating material (7; 118) which is thinner in a direction perpendicular to the substrate than the side walls of each of the gate portions; characterised by the steps of: ii) forming a conductive layer over said insulating layer, iii) removing portions of the conductive layer so that a portion (8; 119) having an upwardly extending side remains where said contact opening is to be formed, iv) forming a second layer (9; 120) of insulating material over the first layer and over said conductive layer portion (8;119) so that an upwardly extending portion of the second insulating layer (9; 120) is formed on said upwardly extending side, and v) forming the contact opening (40) through said second insulating layer, by removal of said conductive layer portion (8;119) and etching the first insulating layer, such that the contact opening (40) is formed in self-alignment relative to said underlayer wiring and the upwardly extending portion of the second insulating layer (9; 120) forms an upward projection (120) at an upper part (16) of the contact opening (40). A method according to claim 1, wherein the step of forming the contact opening comprises forming a pattern film (50) over the second insulating layer (9) so as to cover said upwardly extending portion of the second insulating layer (9), and etching the second insulating layer (9) and the remaining portion (8) of the conductive layer so as to form said upward projection. A method according to claim 1 or claim 2, further comprising: depositing a polysilicon layer (121) doped with impurity at high concentration over the contact opening and then etching back the polysilicon layer to form in the contact opening a buried layer of polysilicon (121a; 121b). A method according to claim 3, further comprising forming overlayer wiring in contact with said buried polysilicon layer (121a). A method of forming a capacitor on a substrate, comprising forming a contact opening as claimed in any one of claims 1 to 3, and further including the steps of: i) depositing a polysilicon film doped with impurity at high concentration and patterning the polysilicon film by projection, exposure and reactive ion etching to form a capacitor lower electrode (10; 131) over said upward projection (120); ii) depositing a capacitor insulating film (11; 132); and iii) depositing a further polysilicon film doped with impurity at high concentration and patterning the further polysilicon film by projection, exposure and reactive ion etching to form a capacitor upper electrode (12; 133) opposing said lower electrode (10; 131). A method according to claim 5, wherein said polysilicon film forming said capacitor lower electrode (10) is deposited so as to cover the contact opening (40) and upward projection. A method according to any preceding claim, wherein the semiconductor substrate (1; 111) is a Si substrate, the first insulating layer (7; 118) is a SiO 2 film and the conductive layer comprises polysilicon. A method as claimed in any preceding claim, further comprising forming a further contact to a further diffused region (K) between the gate portions of the substrate (1), by the steps of: etching the first insulating layer (7) to form a further contact hole (111b) extending to the further diffused region (K) in self-alignment; depositing said conductive layer over the further contact hole (111b); removing the conductive layer so that a further portion (28) thereof remains where the further contact is to be formed in the further diffused region, so that the further contact hole (111b) is filled by the further portion (28); depositing said second insulating layer (9) over the further portion (28) such that the further portion becomes a buried layer and forming a through-hole (242) to the buried layer through the second insulating layer (9). A method as claimed in claim 8, further comprising forming a bit line (15) connected to the buried layer (28) through the through-hole (242).

Inventors: FUJII TAKU, SHIMOMURA NARAKAZU, FUJII, TAKU, SHIMOMURA, NARAKAZU
Applicants: SHARP KK, SHARP KABUSHIKI KAISHA
Application year: 1990
Main classification: H01L27
IPC codes: H01L21, H01L27