COATING COMPOSITIONS

Abstract: A film-forming coating composition comprises (A) a hydroxy component having at least two free hydroxy groups per molecule, (B) an anhydride component having at least two carboxylic acid anhydride groups per molecule and (C) amine groups which are catalytically effective for accelerating the curing reaction between the hydroxy groups of (A) and the anhydride groups of (B). The composition contains an amine salt or an acid capable of forming an amine salt with the said catalytically effective amine groups. The amine salt or acid increases the pot life of the coating composition.

Description: Coating Compositions Field of the invention This invention relates to a curable coating composi¬ tion based on a hydroxy component and an anhydride component. Background of the invention US Patent 4452943 describes a coating composition suitable for use as a glossy pigmented coating for a rigid substrate, particularly where hardening of the coating at ambient temperatures is required, for example as a vehicle re-finishing paint. The coating composition comprises a hydroxy component having at least two f ree hydroxy groups per molecule and an anhydride component having at least two cyclic carboxylic acid annydride groups per molecule, at least one of these components being a film-forming polymer. The composition also includes a catalytically effective amount of amine groups for accelerating the curing reaction between the hydroxy groups and the anhydride groups. European Patent Application 259172 describes a coating composition comprising an anhydride polymer containing at least two cyclic carboxylic acid anhydride groups and a polymer containing at least two functional groups reactive with anhydride groups. These reactive groups are selected from hydroxyalkylamino, hydroxyalkoxyalkylamino, hydroxy- substituted acyloxyalkylamino, hydroxy-substituted poly- acyloxyalkylamino, ercaptoalkylamino and oxazolidino groups. One of the polymers comprises a flexible polymer chain selected from polyether, polyester, silicone, diene polymer, hydrogenated diene polymer, polyurethane, poly- is.obutylene and polyacrylate chains. The functional groups characteristic of that polymer are each . present as a terminal group at the end of a flexible polymer chain. The cured coatings have increased resistance to impact and abrasion. US Patent 4798745 describes a coating composition comprising a hydroxy component having at least two free hydroxy groups per molecule and an anhydride component having at least two carboxylic annydride groups per mole- cule, used in amounts to provide a ratio of equivalents of hydroxy! groups to anhydride groups of 3:1 to 1:3. The anhydride component is a copolymer of at least 11% by weight of an ethylenical ly unsaturated anhydride with a vinyl comonomer such as styrene which is used in a molar proportion of at least 1:1 with respect to the unsaturated anhydride. Such an anhydride copolymer gives a ncn-yelTew¬ ing coating composition when used with dimethylcocoamine catalyst. Such compositions are generally stored as two-pacκ compositions which are mixed to form a liquid coating composition before use. Some reaction of the components takes place in the vessel used for mixing, causing a gradual increase in viscosity of the coating composition. The coating composition eventually becomes too viscous for spray application. The time for which the coating com¬ position remains sufficiently mobile to be sprayed after mixing of the components is known as the "pot life". There is a need for such coating compositions to have an in¬ creased pot life without a correspondingly slower cure rate when applied as a film. Summary of the invention A film-forming coating composition according to the invention comprises (A) a hydroxy component having at least two free hydroxy groups per molecule, (B) an anhydride component having at least two carboxylic acid anhydride groups per molecule and (C) amine groups which are cata¬ lytically effective for accelerating the curing reaction between the hydroxy groups of (A) and the anhydride groups of (B), and is characterised in that the composition also contains an amine salt or an acid capable of forming an amine salt with the said catalytically effective amine groups . The amine salt or acid increases the pot life of the coating composition. Detailed disclosure The hydroxy component (A) is preferably a film-forming polymer, although a hydroxy component which is not poly¬ meric can be used. It is necessary that at least the combination of the hydroxy component with the anhydride component results in a film-forming system. The hydroxy component is preferably a hydroxy-functional acrylic polymer or a hydroxy-functional polyester. Suitable hydroxy-functional acrylic polymers include copolymers containing 5 to 80% oy weight, preferably 10 to 50% by weight, of a hydrσxy-containing ester of an olefini- cally unsaturated carboxylic acid, the balance of tne copolymer being units of at least one olefinically un¬ saturated comonomer. The hydroxy-containing ester is preferably an acrylate or methacrylate, particularly a hydroxyalkyl acrylate or methacrylate such as hydroxyethyl acrylate, hydroxyethyl methacrylate, hydroxypropyl meth¬ acrylate or hydroxypropyl acrylate. The hydroxy-containing ester can contain further ester or ether linkages, for - example 2-(beta-hydroxy-ethoxy)ethyl acrylate or methacry¬ late or an adduct of hydroxyethyl acrylate or methacrylate with caprolactone. Examples of olefinically unsaturated comonomers which can .be copolymerised with the hydroxy-con¬ taining ester are acrylic esters such as butyl acrylate or methacrylate, methyl methacrylate or acrylate, ethyl acrylate or methacrylate, propyl acrylate or methacrylate, n-hexyl acrylate or methacrylate, isopropyl acrylate or methacrylate, t-butyl acrylate or methacrylate, 2-ethyl- hexy methacrylate or acrylate, cyclohexyl acrylate or methacrylate, 3,3,5-trimethylcyclohexyl acrylate or meth¬ acrylate or isobornyl acrylate or methacrylate, acryl- amide, methacrylamide, acrylonitrile, ' methacrylonitrile, and vinyl compounds such as styrene, vinyl acetate or vinyl chloride. A hydroxy-functional acrylic polymer can contain a polyester segment, for example a graft copolymer of acrylic monomer(s) onto an unsaturated polyester. The acrylic . monomers are preferably selected from those above and include a hydroxy-containing monomer such as hydroxy¬ ethyl acrylate or methacrylate. The polyester segment is preferably a low molecular weight (below 1,000) polyester derived from a polyol such as ethylene glycol, propylene glycol or tnmethylolpropane and an acid or anhydriαe such as phthalic anhycride, isophthalic acid or adipic acid with an unsaturated acid or anhydride such as maleic anhydrice. The polyester can for example form 5 to 5C% by weight, preferably 5 to 25% by weight, of tne graft copolymer. Hydroxy-functional polyesters suitable for use as the hydroxy component (A) can be prepared by the reaction of one or more diols, triols or higher polyols with a polycar- boxylic acid, generally a dicarboxylic acid, or an an¬ hydride thereof. Examples of suitable polyols are ethylene glycol, propylene glycol., 1,3-propane diol , 1,2-butane diol, 1,4-butane diol, 2,2,4-trimethyl-1 ,3-pentane diol, 1,6-hexane diol, neopentyl glycol, 1 ,4-cyclohexanediol , 1 ,4-cyclohexanedimethanol , diethylene glycol, dipropylene glycol, trimethylol propane, trimethylol ethane, glycerol and pentaerythritol . Examples of suitable polycarboxylic acids and anhydrides include phthalic anhydride, isoph¬ thalic acid, adipic acid, azelaic acid, sebacic acid, maleic anhydride or acid and fumaric acid.- A lactone such as caprolactone or a hydroxy-acid such as hydroxy-capro c acid or dimethylol propionic acid can be included in the polyester-forming reaction. The hydroxy-functional polyester can be an alkyd polyol containing fatty acid moieties. Another suitable hydroxy-functional polyester can be prepared by reacting an epoxide such as ethylene oxide or a glycidyl ether or ester with a dicarboxylic acid. Alternative hydroxy-functional polymers suitable for use as the hydroxy component (A) include polyether polyols, amide-containing polyols prepared by the reaction of a polycarboxyl ic acid or anhydride with a polyol and a diamine or amino alcohol, epoxy polyols prepared by the reaction of glycidyl ethers of polyphenols such as the diglycidy ether of bisphenol A with a bisphenol or an aliphatic diol, polyvinyl alcohol, an allyl alcohol polymer such as a styrene/al 1yl alcohol copolymer optionally containing allyl ether units, cellulose or a cellulose der-ivative, or a hydroxy-functional polyurethane. The hydroxy component (A) can alternatively be a non- polymeric polyol or can include a non-polymeric polyol such as ethylene glycol, 1,4-butane diol, neopentyl glycol, 1,4- cyclohexanedimethanol , 2,2-dimethyl-3-hydroxypropy1 2,2- dimethyl-3-hydroxypropionate, diethylene glyccl or an alkoxylated bisphenol A. The anhydride component (B) is preferably an anhydride-functional addition polymer of an unsaturated cyclic anhydride, for example maleic, itaconic or citra- conic anhydride. The anhydride-functional polymer is usually a copolymer with one or more ethylenical1y un¬ saturated comonomers. Preferred copolymers contain 10 to 50% by weight maleic or itaconic anhydride units. The anhydride-functional polymer preferably contains a vinyl comonomer such as styrene (which is most preferred) or a substituted styrene, vinyl chloride or vinyl acetate at a molar ratio of at least 1:1 to the anhydride monomer, as described in US Patent 4798745. The anhydride-functional polymer preferably also contains units of one or more esters of acrylic or methacrylic acid, for example the acrylate and methacrylate esters described above as suit¬ able for use in a hydroxy-functional acrylic polymer. The molecular weight of the anhydride-functional polymer is preferably in the range 1,000 to 50,000. The anhydride component (B) can alternatively be an anhydride adduct of a diene polymer such as maleinised polybutadiene or a maleinised copolymer of butadiene, for example a butadiene/styrene copolymer. An anhydride adduct of an unsaturated fatty acid ester, for example a styrene/al lyl alcohol copolymer esterified with an unsaturated " fatty acid and maleinised, -can also be used. Terpene/maleic anhydride copolymer resins are a further alternative. Alternative anhydride-containing polymers can be formed from hydroxy-containing polymers, for example copoly ers of hydroxyethyl acrylate or hydroxyethyl methacrylate or styrene/al 1yl alcohol copolymers, by reac¬ tion with a tricarboxyl ic compound capable of introducing anhydride groups, for example as described in European Patent AppVicartion 259172. A furtner alternative type of polymer containing anhydride groups is an adduct of tπmel- litic anhydride and a polyol, for example as described in European Patent Application 134691. The polymer containing anhydride groups can alternatively be formed by the reac¬ tion of a polymer containing thiol groups with an olefini¬ cally unsaturated cyclic carboxylic acid anhydride such as maleic anhydride or itaconic anhydride. The polymer containing thiol groups is preferably thiol-tipped. It can for example be a multi-limbed telechelic polymer formed by reaction -of a corresponding hydroxy-tipped polymer with mercaptoacetic acid. The amine groups present as catalyst are preferably tertiary amine groups sin.ce these are most effective in catalysing the reaction between the hydroxy and anhydride groups without taking part in any undesirable side reac¬ tions. The amine catalyst may be present in the molecule of the hydroxy component (A) or in the molecule of the anhydride component (B) or as a separate compound. Prefer- ably, the amine catalyst is a separate compound and is suitably mixed with either the hydroxy component (A) or the anhydride component (B) before these two components are mixed with one another. Particularly preferred amine catalysts are those containing at least one oleophilic group, for example a group containing a carbon chain of at least 8 carbon atoms. Examples of such preferred amine catalysts are N,N-di-methylalkylamines in which the alkyl group is derived from a natural oil or fat, .for example ,N-dimethylcocoamine, N, -dimethyltal lowamine or N,N- di ethylhydrogenatedtal lowamine, or N,N-dimethyllauryl- amine. Lower molecular weight amines such as triethyla ine can be used or the amine can be a phenolic compound con¬ taining one or more dialkylamino groups. The amine catalyst can alternatively be a hydroxy- functional amine, preferably a tertiary amine, such as triethanola ine, N,N-dimethylaminoethanol , 2-hydroxymethyl- 2-dimethylamino-1 ,3-propanediol or 2-hydroxymethyl-2- dimethylamino-1-propanol . Such a hydroxy-functional amine catalyst acts as part of the hydroxy component (A) in that the hydroxy groups react with the anhydride groups of component (B), although the hydroxy-functional amine catalyst is preferably not the only hydroxy-functional material present in the coating composition. The amine groups can alternatively be incorporated in the molecule of the hydroxy component (A). The hydroxy component can for example be an acrylic polyol containing units of a hydroxyalkyl acrylate or methacrylate and units of a dialkylaminoalkyl acrylate or methacrylate such as dimethylaminoethyl acrylate, diethyla inoethyl acrylate, di ethylaminoethyl methacrylate or diethylaminoethyl methacrylate, or of a dialkylaminoalkyl-substituted amide such as dimethylaminopropyl methacrylamide. Units of a secondary amine containing a tertiary alkyl group such as t-butylaminoethyl methacrylate can alternatively be used. The acrylic polyol can for example contain 5 to 15% by weight of diethylaminoethyl methacrylate units. Alterna¬ tively, tertiary amine groups and hydroxy groups can be introduced into an acrylic resin by polymerising glycidyl acrylate or methacrylate, preferably with one or more ethylenically unsaturated comonomers, and subsequently reacting the glycidyl groups with a secondary amine. The comonomers preferably include a hydroxyalkyl acrylate or methacrylate. The amine and hydroxy groups can be incorporated as hydroxyalkylamino groups, for example beta-hydroxy amino groups, hydroxyalkoxyalkylamino groups, hydroxy-substituted acyloxyalkyla ino groups or hydroxy-substituted poly- acyloxyalkylaminό groups. Such groups are preferably present as terminal groups at the end of a flexible polymer chain, for example a polyether, polyester, silicone, diene polymer, hydrogenated diene polymer, polyurethane, poly- isobutylene or polyacrylate chain, as described in European Patent Application 259172. Beta-hydroxy amino groups can be formed by the reaction of primary or secondary amine groups with an epoxide, as described in European Patent Application 259172. Hydroxyalkoxyalkylamino groups can be formed by further reaction with an epoxide. Hydroxy- substituted acyloxyalkylamino groups and hydroxy- substituted polyacyloxyalkylamino groups can be formed by reaction with a lactone such as epsilon-caprolactone. The hydroxy component (A) for use in a coating com- position of the invention may be a mixture of a polymer or compound containing hydroxy but not amine .groups with a polymer or compound containing hydroxy and amine groups. The amine groups can alternatively be incorporated in the anhydride component (B) as described in European Patent Application 353899. The anhydride component (B) can for example be a polymer containing cyclic carboxylic anhydride groups and N-(aminoalkyl )-substituted imide groups formed by the reaction of a polymer containing anhydride groups with a less than stoichiometric amount of a polyamine containing a primary amine group and at least one tertiary amine group. Such an anhydride polymer containing amine groups can be used as the whole of the anhydride component (B) or can be used in conjunction with a polymer containing cyclic carboxylic anhydride groups but no amine groups. The catalytic amine. groups can be amidine groups, for example cyclic amidine groups such as imidazoline or imidazole groups, as described in International Patent Application PCT/GB 90/01075. The amidine groups can be present as a separate compound such as imidazole or im- idazoline or can be present in the molecule of the hydroxy component (A). Component (A) can for example contain at least two hydroxy-substituted imidazoline groupings or can be a copolymer containing N-vinyl imidazole monomer units. The acid which is used to increase pot life is prefei— ably an organic acid, more preferably a monovalent organic acid, especially a monocarboxyl ic acid. Preferably, it has a molecular weight less than 300, most preferably less than 150. Examples of preferred acids are acetic, propionic, n- butyric, isobutyric, n-valeric, isovaleric, formic, ben- zoic, chloroacetic, bromoacetic-, dichloroacetic, trichloro- acetic and nitrσacetic acids. Alternatively, a sulphonic acid or phosphonic acid can be used, particularly in compositions in which the amine catalyst is a separate compound rather than being bound into the hydroxy component (A) or the anhydride component (B), but these stronger acids and inorganic acids are less preferred. The acid and the amine catalyst react to form an amine salt in a reaction in which the equilibrium R 3 + HX _ ^ R 3 NH + X- amine acid 7 amine salt is set up. For weak acids such as carboxylic acids sig¬ nificant amounts of amine, acid and amine salt can all be present in the composition.. The amount ' of amine available as a catalyst at any moment is dependenτ. on the strength of the acid HX and its concentration. The amine catalyst is believed to function through a nucleophilic mechanism, so that protonation by the acid to form a triorgano-ammonium ion should remove its catalytic potential and hence its tendency to cause thickening and gelling of the coating composition in the pot. All or part of the amine catalyst and the acid can be added in the form of an amine salt if desired; the same equilibrium will be set up. We prefer to add the amine catalyst and acid separately, especially for weak acids such as acetic acid and other unsubstituted monocarboxylic acids which generally have a pKa in the range 3.7 to 5.1. For stronger acids it may be preferred to add an amine salt of the acid in addition to the amine catalyst. When the coating composition is applied as a film the equilibrium of the reaction set out above appears to be changed, possibly by evaporation of the acid from the film or by other processes. Any retardation of curing of the film by the acid is much less than the retardation of thickening and gelling of the composition in the pot. The acid is generally used at a molar ratio of acid groups to catal tically effective amine groups (C) of 0.1:1 to 10:1. For the preferred monocarboxylic acids such as acetic acid, the molar ratio of ' acid groups to amine groups is preferably 1:1 to 10:1, most preferably 2:1 to 6:1. Such monocarboxyl ic acids, especially the lower acids such as acetic and propionic acids, are particularly preferred for increasing the pot life of the coating composition without substantially slowing the cure time when applied as a film. Stronger acids such as substituted carboxylic acids having a pKa below about 3.5 such as down to about 2, for example chloroacetic _ or bromoacetic acid, are generally used at a molar ratio of 0.1:1 to 1 : 1 to the amine groups. Still stronger acids (pKa below .about 2) such as sulphonic or phosphonic acids are used at a molar ratio to the amine groups of 0.5:1 or less. These stronger acids generally have some effect on slowing the cure time as well as increasing the pot life. Where an amine salt is added as such to increase pot life, it is preferably an amine salt of a strong acid, for example of pKa below 3. Examples of such strong acids are mineral acids such as hydrochloric, sulphuric or phosphoric acid, sulphonic acids such as benzene sulphonic acid, p-toluene sulphonic acid or a long-chain alkyl aryl sulphonic acid, and corresponding phosphonic acids. Sulphate monoester amine salts or phosphate monoester amine salts can be used. It is preferred that either the acid or the amine moiety of the amine salt should contain a long alkyl chain, for example of at least 8 carbon atoms. The amine moiety of the salt is preferably a secondary or tertiary amine, for example a dialkylamine such as diiso- propyla ine or a trialkylamine such as triethylamine or N, -dimethylcσcoamine. The amine salt can for example be a di isopropylamine or triethylamine salt of a long chain alkyl aryl sulphonic acid or N,N-dimethylcocoamine phosphate. The amine salt is generally used at a molar ratio to the catalytically effective amine groups of from 0.1:1 to 10:1, preferably 0.1:1 to 1:1 if the amine salt is a salt of a strong acid. If the coating composition is to be cured by heating it may be advantageous to use an acid whose acid group is unstable to heat when in amine salt form, for example a carboxylic acid whose amine salts are decarboxylated at a temperature lower than that used for curing the coating. In this case the acid can be a strong acid, that is it can have a low pKa, since the acid group is destroyed before curing takes place and cannot retard curing. It is prefei— ably an organic monovalent acid, but could be .polyvalent. Examples of suitable carboxylic acids for heat-cured compositions are trichloroacetic acid, whose amine salts are decarboxylated at temperatures of 80 to 120°C, and nitroacetic acid, whose amin.e_ salts are decarboxylated at below 80°C. The acid or the amine salt is generally mixed with the component containing the catalytically effective amine groups before the hydroxy component (A) and the anhydride component ( B) are mixed. The amounts of hydroxy component (A) and anhydride component (B) in the coating composition of the invention are preferably such as to provide a ratio of equivalents of hydroxy groups to equivalents of anhydride groups in the range 1 :3 to 3: " 1 , most preferably 1:1.2 to 1.2:1. The coating composition of the invention is preferably an organic-solvent-based composition. The solvent is chosen so that the hydroxy component (A), the anhydriαe component (B), the amine catalyst and the acid or the amine salt are soluble to the desired extent and are compatible with one another in solution. Organic solvents which can be used ape for example aromatic hydrocarbons such as xylene, toluene or tr methyl benzene, ketories such as methyl isobutyl ketone or methyl isoamyl ketone and esters such as butyl acetate, ethoxyethyl acetate or methoxypropyl acetate, and mixtures thereof. The coating composition can contain one or more additional ingredients, for example one or more pigments, which can be opaque or translucent pigments or metallic flake pigments, fillers, plasticisers, antioxidants, UV stabilisers, surfactants or flow control agents, including additives for imparting thixotropy or sag resistance or pigment orientation. In two-pack compositions where the hydroxy component (A) is a film-forming polymer such additional ingredients are preferably included in the hydroxy-functional polymer component of the paint. The coating composition of the invention is generally a two-pack coating composition in which the hydroxy com¬ ponent (A) and the anhydride component (B) are stored separately and are mixed shortly before use. The coating can be applied to a substrate by spray, for example conven¬ tional airless spray, or by roller or brush or by dipping or flow coating. The coating is preferably an ambient- temperature-curing coating capable of curing on the sub¬ strate within 24 hours at ambient temperature, for example 10 - 40°C, to a hard film which is tack-free and resistant to solvent so that it can be overcoated. Maximum hardness, solvent resistance and impact resistance generally develop over a number of days at ambient temperature, for example 5 - 20 days. Curing can be carried out at temperatures above ambient, for example in the range 40 - 180°C, particularly 100 - 150°C, for shorter times if this is more convenient, for example when coating under factory conditions. Industrial Applicability The coating compositions of the invention can be applied to a wide variety of substrates, particularly to rigid substrates such as metal, wood, glass or plastics. The compositions can be applied over most commercially sold primers. The coating compositions of the invention are widely useful as top coat paints and are particularly useful as automotive paints including paints for vehicle re-finishing. They can be applied in "clear on base" coating systems in which a pigmented coat is overcoated with a transparent clear coat. The coating compositions of the invention can be used as either the base coat or the clear coat in such coating systems or preferably as both. They can also be applied as clear coats over known base coats such as polyurethane, acrylic or polyester base coats. The invention is illustrated by the following Ex¬ amples. Example 1 250.2g styrene, 87.5g hydroxy-ethyl acrylate, 40g butyl acrylate, 247.7g methyl methacrylate, 61.2g xylene, and 7.8g tert-butyl perbenzoate were mixed together and run into a refluxing mixture of 137.3g ethoxypropyl acetate, 197.6g xylene -, and 6.2g cumene hydroperoxide (90% pure) over 5 hours. After addition was complete, a further 6.5g xylene was added, and the solution refluxed for 2 hours. A 62% solids by weight solution of a hydroxy-functional acrylic polymer having a hydroxy equivalent weight of 823 was produced, the solution having a hydroxy equivalent weight of .1337. This solution was used as resin (A) in Example 1. Resin (B) was made py mixing 140g methoxypropyl acetate, 81..2g maleic anhydride, 92.8g styrene, 92.8g butyl acrylate, 92.8g methyl methacrylate, and 13g tert-outyl perbenzoate and adding this mixture to 270g of refluxing xylene over 5 hours. After that addition was complete 3 additions of 0.4g tert-butyl perbenzoate were made at 15- minute intervals. The mixture was held at reflux for a further 1 hour and then thinned to 40% solids by weight with butyl acetate, producing a resin with a solution anhydride equivalent weight of 1128 (polymer equivalent weight 451 ) . A two-pack paint was produced from resins (A) and (B). The first pack was made as follows: Resin (A) 385g Titanium dioxide 195g Butyl acetate 79g N,N dimethylcocoamine 8.5g Acetic acid 8.7g The second pack consisted solely of 325g of resin (B). This gives a total composition with approximately 1 :1 hydroxy: anhydride stanchiometry, 2.3% by weight on total resin solids of N,N-dimethylcocoamine, and acetic acid in an amount of 4 moles per mole of dimethylcocoamine. Examples 2 to 4 The process of Example 1 was repeated using a molar equivalent amount of propionic acid (Example 2), n-valeric acid (Example 3), or iso-valeric acid (Example 4) in place of acetic acid. In a comparative experiment, Example 1 was repeated with the omission of the acetic acid. In all cases the viscosity of the coating composition was measured on an ICI cone and plate viscometer immediate- ly after mixing the two packs and again after 5 hours' storage in a sealed can at ambient temperature (about 25°C). The coating compositions were also apDlied to a steel panel to give a dry film build of 35 micrometers, and were allowed to cure at ambient temperature. Ahe degree of curing of the films was measured by recording the number of double rubs of xylene-soaked rag across panels needed to penetrate the film. Table 1 Example Initial Viscosity Solvent Resistance number viscosity after 5 hrs (xylene double rubs) (Pa s) (Pa s) After 1 day After 3 days 1.12 1.32 .1.30 1.17 2.30 Examp l e 5 In- another composition the resin (A) quoted in Ex¬ amples 1 to 4 was used in conjunction with another an¬ hydride-functional resin (B), made to the following procedure. 24g butyl acetate, 75g itaconic anhydride, 75g styrene, 75g butyl acrylate, 75g methyl methacrylate, and 24g tert-butyl peroctoate were mixed and addec over 3 hrs to 169g of refluxing butyl acetate. On completion of this addition 50g of butyl acetate was added and reflux main¬ tained for 1 hour. Three adαitions each of 0.37g of tert- - butyl peroctoate were made with 30 minutes between addi- ■ tions. The resin was refluxed for a further 90 minutes before cooling and thinning to 33% sclids by weight with butyl acetate. This gave a resin with an anhydride equivalent weight of 1446 on solution (477 on solid polymer) . Resins (A) and (B) were used to make an ambient-curing two-pack paint, the first pack having the following com- position. Resin (A) 499g Titanium dioxide 264g Butyl acetate 1 ' 8g N,N dimethylcocoamine 20g Witconate P10-59 4g- The second " pack consisted solely of 578g of resin (B). Witconate P10-59 is a commercial proprietary product quoted as being an alkyl aryl sulfonate, isopropylamine salt. In a comparative experiment the same two-pack coating composition was prepared with the omission of the Witconate P10-59. The performance of these two compositions was tested • in a similar way to Examples 1 to 4. Pot life was deter¬ mined by measuring viscosity by Ford 4 cup at 25°C im- mediately after mixing the two packs together, and after 5 hours, while cure rate was assessed by xylene solvent resistance. The results are shown in the following Table 2. Table 2 Viscosity Viscosity Xylene Resistance initial after 5 (double rubs) after hours 1 day at ambient (seconds) (seconds) temperature Example 5 60 148 100 comparative experiment 63 208 100 In addition, after 11 hours the sealed can containing the composition without the Witconate P10-59 was found to have completely gelled whilst the coating composition according to the invention, although too viscous for spray application, had not gelled and could still be applied by brush. Example 6 A hydroxy-functional polyester resin containing amino groups was prepared by the process described in Example 8 of European Patent Application 259172. An anhydride- functional polymer was prepared using the process of Example 1 of European Patent Application 259172. The hydroxy-functional polyester was mixed with acetic acid in an amount of 6 moles acetic aciα for each amine group in the polyester and was then mixed with the anhydride polymer at a ratio of anhydride groups to hydroxy groups of 1:1 to form a coating composition. In a comparative experiment the same coating composi¬ tion was prepared with the omission of the acetic acid. As measures of the pot life of the coating composition according to the invention the time taken for the initial viscosity of 0.1 Pa s to treble was 1.5 hours and the time taken to gel was 3.5 hours. The coating composition containing no acetic acid, which also had an initial viscosity of 0.1 Pa s, trebled in viscosity in 50 minutes and gelled in two hours. Both compositions cured to a hare tough film at ambient temperature when applied as a spray. Example 7 The process of Example 6 was repeated using bromoacetic acid in place of acetic acid. The amount of bromoacet c acid used was 1 mole per mole of amine in the hydroxy- functional polyester. On storage at ambient temperature the time taken to treble the initial viscosity was 4.5 hours and the gel time was 6 hours. When the coating composition was applied by spray it formed a cured film which was- less hard than the coating of Example 6. Example 8 The process of Example 7 was repeated using an e- quivalent amount of trichloroacetic acid (pKa 0.70) in place of the,, bromoacetic acid. On storage at ambient temperature the coating composition showed very little increase in viscosity over 24 hours. The coating composi- tion was applied by spray to a steel plate and cured at 150°C for 20 minutes to form a hard tough glossy film. By comparison, when the trichloroacetic acid was replaced by an equivalent amount of methanesulphonic acid (pKa 0.69), whose amine salts are not heat-labile, the coating composition showed very little increase in vis- cosity but the coating film was substantially uncured after 20 minutes' heating at 150°C. When the amount of methane¬ sulphonic acid was reduced to 0.1 mole per mole of amine, the pot life of the coating composition was still extended compared to a composition containing no acid, although the pot life was less than 24 hours. This coating could be cured after 20 minutes' heating at 150°C, although to a less hard film than that obtained when the trichloroacetic acid was used.

Claims: CLAIMS -1. A film-forming coating composition comprising (A) a hydroxy component having at least two free hydroxy groups per molecule, (B) an anhydride component having "at least two carboxylic acid anhydride groups per molecule and (C) amine groups which are catalytically effective for ac¬ celerating the curing reaction between the hydroxy groups of (A) and the anhydride groups of (B), characterised in that the composition also contains an amine salt or an acid capable of forming an amine salt with the said catalytical¬ ly effective amine groups. 2. A coating composition according to claim 1, characterised in that the acid capable of forming an amine salt is an organic acid. 3. A coating composition according to claim 1 or claim 2, characterised in that the amine groups are ter¬ tiary amine groups. 4. A coating composition according to any of claims 1 to 3, characterised in that the amine groups are present as an amine catalyst compound which is not part of the mole¬ cule of the hydroxy component (A) or the anhydride com¬ ponent (B) . 5. A coating composition according to claim 4, characterised in that the amine catalyst compound contains at least one oleophilic group. 6. A coating composition according to any of claims 1 to 3, characterised in that the amine groups are present in the molecule of the hydroxy component (A). 7. A coating composition according to any of claims 2 to 6 in which the composition contains an organic acid capable of forming an amine salt with the said catalytical¬ ly effective amine groups, characterised in that the organic acid is a monocarboxyl ic acid of molecular weight less than 300. 8. A coating composition according to claim 7, characterised in that the monocarboxyl ic acid has a pka in the range 3.7 to 5.1 and is used at a molar ratio of acid groups to amine groups of 1:1 to 10:1. 9. A coating composition according to claim 8, characterised in that the monocarboxyl ic acid is used at a molar ratio of acid groups to amine groups of 2:1 to 6: 1. 10. A coating composition according to any of claims 7 to 9, characterised in that the monocarboxyl ic acid is acetic acid. 11. A coating composition according to claim 7, which is a heat-curable coating composition, characterised in that the organic acid is a carboxylic acid whose amine salts undergo decarboxylation at a temperature lower than the intended curing temperature of the coating. 12. A coating composition according to claim 11, - characterised in that the carboxylic acid is trichloro¬ acetic acid. 13. A coating composition according to. any of claims 1 to 6 which contains an amine salt, characterised in that the amine salt is a salt of an acid of pKa below 3. 14. A coating composition according to claim 13 which is a heat-curable coating composition, characterised in that the acid is a carboxylic acid whose amine salts undergo decarboxylation at -a temperature lower than the intended curing temperature of the coating. 15. A coating composition according to claim 14, characterised in that the carboxylic acid is trichloro¬ acetic acid. 16-. A coating composition according to any of claims 13 to 15, characterised in that either the acid or the amine moiety of the amine salt contains an alkyl chain of at least 8 carbon atoms. 17. A coating composition according to any of claims 13 to 16, characterised in that the amine salt is used at a molar ratio to the catalytically effective amine groups of from 0.1:1 to 1:1. 18. A coating composition according to any of claims .1 to 17, characterised in that the hydroxy component (A) is • a film-forming acrylic polymer or polyester. 19. A coating composition according to any of claims 1 to 18, charactβrised in that the anhydride component (B) is an addition polymer of an unsaturated cyclic anhydride. 20. A process for preparing a coating composition by mixing (A) a hydroxy component having at least two free hydroxy groups per molecule with (B) an anhydride component having at least two carboxylic acid anhydride groups per molecule, in which process the composition contains amine groups which are catalytically effective for accelerating the curing action between the hydroxy groups of (A) and the anhydride groups of (B), which amine groups are present in the molecule of the hydroxy component (A) or .the anhydride component (B) or are present as a separate amine catalyst compound which is mixed with either the hydroxy component (A) or the anhydride component (B) before the hydroxy component (A) and the anhydride component (B) are mixed, characterised in that an amine salt or an acid capable of forming an amin salt with the said catalytically effective amine groups is mixed with the component containing the catalytically effective amine groups before the hydroxy component (A) and the anhydride component (B) are mixed. 21. A coating composition according to claim 1 and substantially as hereinbefore described or illustrated in any of the foregoing Examples. 22. A process for coating a substrate, characterised in that a coating composition according to any of claims 1 to 19 or 21 is applied to the substrate and cured.

Inventors: FINNIE ALISTAIR ANDREW, MARRION ALASTAIR ROBERT, MCKAY GARRY MICHAEL, SAVILLE BRIAN, FINNIE, ALISTAIR, ANDREW, MARRION, ALASTAIR, ROBERT, MCKAY, GARRY, MICHAEL, SAVILLE, BRIAN
Applicants: COURTAULDS COATINGS HOLDINGS, TAUBMANS IND LTD, COURTAULDS COATINGS (HOLDINGS) LIMITED, TAUBMANS INDUSTRIES LIMITED
Application year: 1990
Main classification: C09D133
IPC codes: C08K5, C09D133, C09D167, C09D201