TRIFLUOROBENZENE DERIVATIVES AND LIQUID CRYSTAL COMPOSITIONS CONTAINING THE SAME

Abstract: Trifluorobenzene derivatives having good stability and a large positive dielectric anisotropy value and which may be used in liquid crystal compositions, have the formula: wherein R represents an alk y l group of 1 to 10 carbon atoms in which one -CH₂- group or two non-adjacent -CH₂- groups may be replaced by an oxygen atom and/or a -CO- group and/or a -COO- group and/or a -CH=CH- group; -A- and -B- each represent a 1,4-cyclohexylene, 1,4-phenylene, pyrimidine-2,5-­ diyl or 1,3-dioxane-2,5-diyl group; 1 represents 0, 1 or 2; m represents 0, 1 or 2 and 1+m≧1; and Z¹ and Z² are the same or different and each represents a group -COO-, -CH₂CH₂-, -OCH₂-, -CH₂- or -CH=CH-, or a single bond.

Description: This invention relates to a trifluorobenzene derivative used as a component of liquid crystal materials. More particularly it relates to a trifluorobenzene derivative suitable as a component of liquid crystal compositions useful for a passive mode and an active matrix mode each requiring a high reliability, and a liquid crystal composition containing the derivative. Liquid crystal compositions used for liquid crystal display elements of conventional passive modes such as liquid crystal compositions used for liquid crystal display elements of 90° twisted nematic mode, guest-host mode, supertwisted mode, SBE mode, etc. and further liquid crystal compositions used for liquid crystal display elements of active matrix modes such as liquid crystal compositions used for non-linear two-terminal elements of diode, etc. or three-terminal elements of thin film transistors (TFT), etc., as a switching element, are mostly liquid crystal mixtures consisting of several kinds of liquid crystal compounds and compounds similar to liquid crystals, which compounds have CN group at the terminal group or at the side chain thereof to exhibit a positive or negative dielectric anisotropy (hereinafter abbreviated to Δε). The reason is that the dielectric anisotropy of the compounds, induced by CN group has a large positive value when the CN group is present at the terminal group, while it has a large negative value when the group is present at the side chain. For example, in the case of liquid crystal display elements of 90° twist mode occupying the most part of commercially available liquid crystal display elements, the threshold voltage in the electricity-capacity characteristic is given by the following equation containing the dielectric anisotropy value Δε and elastic constants K₁₁, K₂₂ and K₃₃: V c = π k₁₁ + ( k₃₃ - 2 k₂₂ ) / 4 ε₀ Δ ε Thus, it can be understood that when a compound having a large positive Δε value i.e. a compound having CN group at its terminal group is contained in a composition, the resulting threshold voltage Vc is reduced. On the other hand, similarly in the other modes, the threshold voltage value depends upon the Δε value. Namely, the larger the |Δε|, the less the Vc. As to conventional liquid crystal compositions, by adjusting the content of compounds having CN group at the terminal end or at the. side chain thereof in the above-mentioned various modes, it has been possible to drive at a low voltage of several volts, which is one of the largest specific features of liquid crystal display elements. In recent years, as the use application range of liquid crystal display elements are broadened, there have been increasing liquid crystal display elements which are more required to reduce the current consumption of liquid crystal compositions, raise the specific resistivity thereof, raise the reliability thereof such as reduction in the rate of change with lapse of time and enhance the display contrast, in the passive mode and the active matrix mode. However, a highly polarizable group such as CN group, in spite of its contribution to the dielectric anisotropy, has raised a problem in the aspect of the above-mentioned current consumption, specific resistivity, their rate of change with lapse of time and the resulting display contrast. While the reason has not yet been clarified by persons skilled in the art, it may be presumed that CN group at the terminal group or at the side chain of compounds have a certain interaction with ionic impurities present in the display element, thereby having a bad influence upon the current value, specific resistivity value and the resulting display contrast. The drawbacks of compounds having such CN group, consist in, in the case of the passive mode, causing increase in the current consumption and reduction in the specific resistivity to lower the reliability in the elements and in the aspect of display characteristics, causing display unevenness and contrast reduction, and further, in the case of the active display elements, having a larger influence upon reduction in the reliability of display elements than that in the case of the passive display elements, coupled with the influence due to the drive current of two-terminal or three-terminal elements, thereby causing increase in the current consumption and reduction in the specific resistivity. In particular, the reduction in the specific resistivity has further often a secondary bad effect of reducing the display contrast. At present, however, most of compositions containing no CN group having at the terminal group or at the side chain thereof are insufficient in the aspect of the drive voltage among the various specific features of the compositions. Thus, the low voltage drive as one of advantages of liquid crystal display elements is often not made the best use of. Recently, in order to solve such problems, a number of compounds having one or two halogen atoms, particularly one or two fluorine atoms in the aspect of viscosity, at the terminal group or at the side chain thereof have been announced. Examples of these compounds are as follows: (USP No. 4,490,305) (USP No. 4,695,398) (Japanese patent application laid-open No. Sho 58-49324/1983) (USP No. 4,797,228) (Japanese patent application laid open No. Sho 58-49325/1983) ( USP No. 4,797,228) (Japanese patent publication No. Sho 62-40336/1987) (Japanese patent application laid-open No. Sho 59-225129/1984) (USP No. 4,797,228) (USP No. 4,405,488) (USP No. 4,545,922) (USP No. 4,545,922) (USP No. 4,405,488) (USP No. 4,581,155) (USP No. 4,640,795) (USP No. 4,581,155) (USP No. 4,340,498) In these formulas, R represents a linear alkyl group. Most of these compounds have been reported to be liquid crystal materials having a relatively good stability and a high reliability, but they have a relatively small Δε value of about +3 to +5 and liquid crystal compositions consisting only of these compounds have a small Δε value to make it impossible to reduce drive voltage. SUMMARY OF THE INVENTION The object of the present invention is to solve these problems and provide a compound having a superior stability and a large positive Δε value. The present invention resides in a trifluorobenzene derivative expressed by the formula wherein R represents an alkyl group of 1 to 10 carbon atoms and one -CH₂- group or two not-adjacent -CH₂- groups present in said alkyl group may be replaced by O atom and/or -CO- group and/or -COO- group and/or -CH=CH- group, -A- and -B- each represent 1,4-cyclohexylene, 1,4-phenylene, pyrimidine-2,5-diyl or 1,3-dioxane-2,5-diyl, ℓ represents 0, 1 or 2, m represents 0, 1 or 2 and ℓ+m≧1, and Z¹ and Z² each represent -COO-, -OCO-, -CH₂CH₂ , -OCH₂-, -CH₂O-, -CH=CH- or a single bond and Z¹ and Z² may be same or different, and a liquid crystal composition containing the above trifluorobenzene derivative. DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS As the compound of the formula (I), compounds expressed by the following formulas Ia to Ii are mentioned: In these formulas, R, Z¹, Z² and m are as defined above. Among the compounds of the above formulas, examples of particularly preferred compounds are expressed by the following formulas: In these formulas, R represents an alkyl group of 1 to 10 carbon atoms and one -CH₂- group or two not-adjacent -CH₂- groups present in the alkyl group may be replaced by 0 atom and/or -CO- group and/or -COO- group and/or -CH=CH- group, and R is particularly preferred to be a linear alkyl group while it may be also a branched alkyl group. The compound of the formula (I) having a branched alkyl group is more important in some cases for having an improved solubility in conventional liquid crystal bases, and particularly when such a compound is optically active, it is important as a chiral dopant. Such a kind of branched group has at most one branched chain. The preparation of the compound of the present invention will be described. It may be carried out according to the process disclosed in the above-mentioned literatures of the prior art. For example, compounds expressed by the formulas Iaa, Ida and Idb may be respectively obtained by subjecting the corresponding ketone derivative and a Grignard reagent obtained from 1-bromo-3,4,5-trifluorobenzene to a coupling reaction to obtain an alcohol derivative, followed by subjecting this alcohol derivative to dehydration reaction in the presence of an acidic catalyst such as mineral acids e.g. sulfuric acid, hydrochloric acid, etc., Lewis acid e.g. anhydrous aluminum chloride, ferric chloride, titanium tetrachloride, etc., organic acids e.g. benzenesulfonic acid, p-toluenesulfonic acid, etc., to obtain a cyclohexane derivative, and successively subjecting it to a catalytic reduction in the presence of a catalyst such as developed Raney nickel, palladium/carbon, etc. to obtain a cyclohexane derivative. This preparation is illustrated by the following equations: Here, when an oxidative dehydrogenation agent such as chloranil, DDQ, etc. is reacted with cyclohexane derivatives expressed by the formulas Iaa', Ida' and Idb' at the reflux temperature of an inert organic solvent such as toluene, xylene, etc., compounds expressed by the following formulas Iba, Iga and Igb can be obtained: Further, the compound expressed by the formula Igb is obtained by reacting 3,4,5-trifluorobiphenyl with a substituted cyclohexyl acetyl chloride (see USP No. 4,797,228) in the presence of aluminium chloride to obtain a ketone derivative, followed by reducing this derivative. Further, a compound by the formula Iec can also be obtained in the same manner. Further, compounds expressed by the formulas Iab, Iea and Ifa can be obtained by subjecting a substituted cyclohexyl acetyl chloride and a Grignard reagent prepared from 1-bromo-3,4,5-trifluorobenzene to a coupling reaction to obtain a ketone derivative and further reducing this derivative (see J. Chem. Soc., 2756 (1952)). The process is illustrated by the following reaction equations: Compound expressed by the formula Ica can be obtained by reacting a substituted cyclohexanone (see Japanese patent application laid-open No. Sho 57-167934/1982) with a Grignard reagent prepared from 1-bromo-3,4,5-trifluorobenzene, followed by the same manner as that for obtaining compounds expressed by the formulas Iba, Iga and Igb. This process is illustrated by the following reaction equations: Compounds expressed by the formulas Iha and Ihb can be obtained by reacting an amidine hydrochloride prepared from a nitrile derivative, 1-bromo-3,4,5-trifluorobenzene according to the method disclosed in Org. Synt., Col. Vol. 1, P6 (1941), with β-ethoxyacrolein in the presence of a base such as NaOH, KOH, metal alcoholates, etc. This process is illustrated by the following equation: Compounds expressed by the formulas Iia and Iib can be obtained by subjecting a benzaldehyde derivative prepared by reducing a benzonitrile derivative and a substituted propanediol prepared according to a method disclosed in Japanese patent application laid-open No. Sho 55-85583/1980 to a dehydrative condensation reaction in an inert organic solvent such as benzene, toluene, methylene chloride, etc. and in the presence of an acidic catalyst such as mineral acids, Lewis acids, organic acids, etc. This process may be illustrated by the following reaction equations: Compounds expressed by the formulas Iac, Ieb, Ifb and Igc can be obtained by reacting a carboxylic acid chloride with 3,4,5-trifluorophenol in an inert organic solvent and in the presence of a base such as pyridine, diethylamine, triethylamine, etc. This process is illustrated by the following reaction equations: These compounds may also be prepared according to other processes than the above-mentioned ones. The liquid crystal composition of the present invention comprises 2 to 25 components, preferably 3 to 15 components containing at least one of the compounds of the formula (I). The constituting components other than the compounds of the formula (I) are preferred to be nematic substances, particularly those selected from known substances belonging to the group consisting of azoxybenzene compounds, benzylideneaniline compounds, biphenyl compounds, terphenyl compounds, phenyl- or cyclohexyl benzoate compounds, phenyl- or cyclohexylcyclohexanecarboxylate compounds, phenylcyclohexane compounds, cyclohexylbiphenyl compounds, cyclohexylcyclohexane compounds, cyclohexylnaphthalene compounds, 1,4-biscyclohexylbenzene compounds, 4,4'-biscyclohexylbiphenyl compounds, phenylpyrimidine compounds or cyclohexylpyrimidine compounds, phenylpyridazine compounds or cyclohexylpyridazine compounds and their N-oxide compounds, phenyldioxane compounds or cyclohexyldioxane compounds, phenyl-1,3-dithian compounds or cyclohexyl-1,3-dithian compounds, 1,2-diphenylethane compounds, 1-phenyl-2-cyclohexylethane compounds, and 1,2-dicyclohexylethane compounds, and in some cases, halogenated stilbene compounds, benzyl phenyl ether compounds, tolan compounds and substituted cinnamic acid compounds. The most important compounds suitable to the constituting components of the liquid crystal composition of the present invention can be expressed by the formula I' R'-L-G-E-R'' (I') wherein L and E each represent a carbocyclic or heterocyclic compound belonging to the group consisting of 1,4-disubstituted benzenes, cyclohexane ring compounds, 4,4'-disubstituted biphenyls, phenylcyclohexanes, cyclohexylcyclohexanes, 2,5-disubstituted naphthalenes, dihydronaphthalenes, tetrahydronaphthalenes, quinazolines and tetrahydroquinazolines, G represents -CH=CH-, -N(O)=N-, -CH=CY-, -CH=N(O)-, -C≡C-, -CH₂-CH₂-, -CO-O-, -CH₂O-, -CO-S-, -CH₂S-, -CH=N-, -COO-Phe-COO- or a C-C single bond wherein Y represents a halogen atom, preferably chlorine atom or -CN-, and R' and R'' each represent an alkyl, an alkoxy, an alkanoyloxy or an alkoxycarbonyloxy each of up to 18, preferably 8 carbon atoms and one of these groups may be CN, NC, NO₂, CF₃, F, Cℓ or Br. In most of these compounds, R' and R'' are different from each other and either one of these groups is mostly an alkyl group or an alkoxy group. However, R' and R'' may be replaced by other kinds of substitutents. These substances may be obtained according to known processes. The composition of the present invention contains at least one of the compounds of the formula (I) in a quantity of about 0.1 to 40% by weight. The composition of the present invention containing at least one of the compounds of the formula (I) in a quantity of 10 to 30% by weight is particularly preferred. The composition of the present invention is produced in a manner which itself is conventional. In general, the constituting components are dissolved in one another, preferably at an elevated temperature. The present invention will be described in more detail by way of Examples, but it should not be construed to be limited thereto. C-I point, C-N point and N-I point in these Examples mean crystal-isotropic liquid phase transition point, crystal-nematic phase transition point and nematic phase-isotropic liquid phase transition point, respectively. All of the temperatures therein indicate °C. Example 1 Preparation of 1-(trans-4-pentylcyclohexyl)-3,4,5-trifluorobenzene (a compound of the formula Iaa wherein R is C₅H₁₁-) (Compound No. 1) A solution of 1-bromo-3,4,5-trifluorobenzene (10.7 g, 0.051 mol) dissolved in dry tetrahydrofuran (15 mℓ) was reacted with magnesium (1.24 g, 0.051 mol) in nitrogen gas current at about 20°C to prepare a Grignard reagent followed by adding to this reaction solution, a solution of 4-pentylcyclohexanone (8.6 g, 0.051 mol) dissolved in dry tetrahydrofuran (10 mℓ) at a rate at which the reaction temperature did not exceed 40°C, reacting the mixture while keeping the temperature at 50°C for 2 hours, cooling the resulting material down to room temperature, adding 6N hydrochloric acid (5 mℓ) and water (50 mℓ) to the reaction solution, extracting a deposited oily substance with n-heptane (100 mℓ), washing the extract solution with water till it became neutral, distilling off n-heptane to obtain an oily substance of 1-(4-pentylcyclohexan-1-ol)-3,4,5-trifluorobenzene, adding potassium hydrogen sulfate (2.0 g) to the oily substance, subjecting the mixture to dehydration reaction in nitrogen gas current at 180°C for 2 hours, cooling the resulting material down to room temperature, adding water (100 mℓ) and n-heptane (100 mℓ), separating the resulting organic layer, washing till it became neutral, distilling off n-heptane to obtain an oily substance of 1-(4-pentylcyclohexen-1-yl)-3,4,5-trifluorobenzene, dissolving this oily substance in ethyl alcohol (50 mℓ), adding a developed Raney nickel (1.0 g), subjecting the mixture to catalytic reduction reaction at 25°C under the atmospheric pressure till hydrogen absorption ceased, filtering off the Raney nickel after completion of the reaction, and recrystallizing the residue from ethyl alcohol to obtain 1-(trans-4-pentylcyclohexyl)-3,4,5-trifluorobenzene (2.2 g, 7.74 mmol). C-I point: 16.7°C. Its structure was confirmed by IR and NMR. The following compounds were obtained in the same manner as above: Example 2 Preparation of 1-(trans-4-butylcyclohexyl)-2-(3,4,5-trifluorophenyl)ethane (a compound of the formula Iab wherein R is C₄H₉-) (Compound No. 11) Trans-4-butylcyclohexylacetyl chloride (25 g, 0.115 mol) was dissolved in dry tetrahydrofuran (30 mℓ), followed by cooling the solution down to 0°C, adding iron acetyl-acetonate (0.81 g), agitating the mixture, adding a solution of a Grignard reagent prepared from 1-bromo-3,4,5-trifluorobenzene (25 g, 0.115 mol) and metallic magnesium (2.8 g, 0.115 mol), in tetrahydrofuran, at a rate at which the reaction temperature did not exceed 10°C, reacting the mixture at 5°C or lower for 2 hours, adding 6N hydrochloric acid (10 mℓ) and water (100 mℓ) to the reaction solution, extracting a deposited oily substance with n-heptane (100 mℓ), washing the extract solution with a dilute alkali aqueous solution, washing with water till the washing water became neutral, drying over anhydrous sodium sulfate, distilling off n-heptane from the n-heptane solution, and recrystallizing the residue from ethyl alcohol to obtain 1-(trans-4-butylcyclohexylacetyl)-3,4,5-trifluorobenzene (21.0 g). C-I point: 42.8°C. This compound was dissolved in ethyl acetate (100 mℓ), followed by adding 5% Pd supported on barium sulfate (0.5 g), subjecting the mixture to a catalytic reduction at 25°C under 3 atm till hydrogen absorption ceased, filtering off the catalyst after completion of the reaction, and subjecting the reaction solution to a suitable purification treatment to obtain 1-(trans-4-butylcyclohexyl)-2-(3,4,5-trifluorophenyl)ethane (18.0 g). C-I point: 8.4°C. The following compounds were obtained in the same manner as above: Example 3 Preparation of 4'-pentyl-3,4,5-trifluorobiphenyl (a compound of the formula Iba wherein R is C₅H₁₁-) (Compound No. 21) 1-(4-Pentylcyclohexen-1-yl)-3,4,5-trifluorobenzene as an intermediate obtained in Example 1 (5 g) was dissolved in xylene (50 mℓ), followed by adding chloranil (4.5 g), reacting the mixture under reflux for 10 hours, cooling the resulting material down to room temperature, filtering off the resulting deposited hydroquinone derivative, washing the filtrate with a dilute alkali aqueous solution, washing with water till the washing water became neutral, drying over anhydrous sodium sulfate, distilling off xylene from the organic layer, dissolving the residue in n-hexane, purifying the solution according to silica gel column chromatography, collecting fractions exhibiting a single spot according to thin layer chromatography, distilling off n-hexane and recrystallizing the residue from ethyl alcohol to obtain 4'-pentyl-3,4,5-trifluorobiphenyl (3.2 g). The following compounds were obtained in the same manner as above. Example 4 Preparation of 1-[trans-4-(trans-4-propylcyclohexyl)cyclohexyl]-3,4,5-trifluorobenzene (a compound of the formula Ida wherein R is C₃H₇-) (Compound No. 31) 1-[Trans-4-(trans-4-propylcyclohexyl)cyclohexyl]-3,4,5-trifluorobenzene ( 2.1 g) was obtained from 4-(trans-4-propylcyclohexyl)cyclohexanone ( 2.2 g) and 1-bromo-3,4,5-trifluorobenzene ( 2.0 g) in the same manner as in Example 1. C-N point: 64.9°C , N-I point: 93.8°C. The following compounds were obtained in the same manner as above: Example 5 Preparation of 4'-(trans-4-propylcyclohexyl)-3,4,5-trifluorobiphenyl (a compound of the formula Iga wherein R is C₃H₇-) (Compound No. 41) Using 1-[4-(trans-4-pentylcyclohexyl)cyclohexen-1-yl)-3,4,5-trifluorobenzene obtained as an intermediate in Example 4 and exhibiting liquid crystal phases (C-N point: 62.4°C, N-I point: 81.9°C), as a starting raw material, 4'-(trans-4-propylcyclohexyl)-3,4,5-trifluorobiphenyl was obtained in the same manner as in Example 3. C-N point: 57.6°C, N-I point: 75.4°C. The following compounds were obtained in the same manner as above: Example 6 Preparation of 1-(trans-4-propylcyclohexyl)-2-[trans-4-(3,4,5-trifluorophenyl)cyclohexyl]ethane (a compound of the formula Idb wherein R is C₃H₇-) (Compound No. 51) Using 4-[2-(trans-4-propylcyclohexyl)ethyl]cyclohexanone and 1-bromo-3,4,5-trifluorobenzene as starting raw materials, 1-(trans-4-propylcyclohexyl)-2-[trans-4-(3,4,5-trifluorophenyl)cyclohexyl]ethane was obtained in the same manner as in Example 1. C-N point: 49.7°C, N-I point: 83.4°C. The following compounds were obtained in the same manner as above: Example 7 Preparation of 1-(trans-4-ethylcyclohexyl)-2-(3,4,5-trifluorobiphenyl-4'-yl)ethane (a compound of the formula Igb wherein R is C₂H₅-) (Compound No. 61) Using 1-(trans-4-ethylcyclohexyl)-2-[4-(3,4,5-trifluorophenyl)cyclohexen-1-yl]ethane as an intermediate of compound No. 53, exhibiting liquid crystal phases (C-I point: 45.3°C, N-I point: 37.2°C), as a starting raw material, 1-(trans-4-ethylcyclohexyl)-2-(3,4,5-trifluorobiphenyl-4'-yl)ethane was obtained in the same manner as in Example 3. C-I point: 43.0°C, N-I point: 37.4°C. The following compounds were obtained in the same manner as above: Example 8 Preparation of 4''-butyl-3,4,5-trifluoroterphenyl (a compound of the formula Ica wherein R is C₄H₉-) (Compound No. 71) Using 1-[4-(4-butylphenyl)cyclohexen-1-yl]-3,4,5-trifluorobenzene obtained by reacting 4-(4-butylphenyl)cyclohexanone with 1-bromo-3,4,5-trifluorobenzene, as a starting raw material, 4''-butyl-3,4,5-trifluoroterphenyl was obtained in the same manner as in Example 3. The following compounds were obtained in the same manner as above: Example 9 Preparation of 1-(trans,trans-4-propylbicyclohexyl)-2-(3,4,5-trifluorophenyl)ethane (a compound of the formula Iea wherein R is C₃H₇-) (Compound No. 81) Trans,trans-4-propylbicyclohexylacetyl chloride was reacted with a Grignard reagent prepared from 1-bromo-3,4,5-trifluorobenzene in the same manner as in Example 2 to obtain 1-(trans,trans-4-propylcyclohexylacetyl)-3,4,5-trifluorobenzene (C-I point: 97.1°C), followed by subjecting this compound to a reduction with 5% Pd supported on barium sulfate to obtain 1-(trans,trans-4-propylbicyclohexyl)-2-(3,4,5-trifluorophenyl)ethane. C-N point: 41.7°C, N-I point: 98.3°C. The following compounds were obtained in the same manner as above: Example 10 Preparation of 1-[trans-4-{2-(trans-4-propylcyclohexyl)ethyl}cyclohexyl]-2-(3,4,5-trifluorophenyl)ethane (a compound of the formula Ifa wherein R is C₃H₇-) (Compound No. 91) Using trans-4-[2-(trans-4-propylcyclohexyl)ethyl]cyclohexylacetyl chloride and a Grignard reagent prepared from 1-bromo-3,4,5-trifluorobenzene, as starting raw materials, 1-[trans-4-{2-(trans-4-propylcyclohexyl)ethyl}cyclohexyl]-2-(3,4,5-trifluorophenyl)ethane was obtained in the same manner as in Example 2. The following compounds were obtained in the same manner as above: Example 11 Preparation of 1-(trans,trans-4-propylbicyclohexyl)-2-(3,4,5-trifluorobiphenyl-4'-yl)ethane (a compound of the formula Iec wherein R is C₃H₇-) (Compound No. 101) 3,4,5-Trifluorobiphenyl (10.4 g, 0.05 mol) was dissolved in CS₂ (50 mℓ), followed by cooling the solution down to 0°C, at a time adding anhydrous aluminum chloride (6.7 g, 0.05 mol). agitating the mixture, adding a solution of trans,trans-4-propylbicyclohexylacetyl chloride (14.3 g, 0.05 mol) dissolved in CS₂ (20 mℓ) at a rate at which the reaction temperature did not exceed 5°C, successively reacting the mixture for 3 hours, adding the reaction material into a dilute aqueous solution of hydrochloric acid, extracting the deposited massive material with toluene (100 mℓ), washing the extract solution with a dilute alkali aqueous solution, washing with water till the washing water became neutral, drying the resulting toluene solution over anhydrous sodium sulfate, distilling off toluene and recrystallizing the residue from benzene to obtain 4'-(trans,trans-4-propylcyclohexylacetyl)-3,4,5-trifluorobiphenyl (18.4 g), dissolving this compound in ethyl acetate (100 mℓ), adding 5%-Pd supported on barium sulfate, subjecting the mixture to catalytic reduction at 25°C under 3 atm, filtering off the catalyst after completion of the reaction and subjecting the reaction solution to a suitable purification treatment to obtain 1-(trans, trans-4-propylbicyclohexyl)2-(3,4,5-trifluorobiphenyl-4'-yl)ethane (12.8 g). The following compounds were obtained in the same manner as above: Example 12 Preparation of 3,4,5-trifluorophenyl-trans-4-propylcyclohexylcarboxylate (a compound of the formula Iac wherein R is C₃H₇-) (Compound No. 111) 3,4,5-Trifluorophenol (5.0 g, 0.034 mol), which was obtained by reacting a Grignard reagent of 1-bromo-3,4,5-trifluorobenzene with acetyl chloride, oxidizing the resulting 1-acetyl-3,4,5-trifluorobenzene with a peracid to obtain 3,4,5-trifluorophenyl acetate and subjecting this acetate to hydrolysis reaction, was dissolved in dry pyridine (10 mℓ), followed by gradually adding trans-4-propylcyclohexylcarbonyl chloride (6.4 g), allowing the resulting reaction solution to stand at 50°C for 3 hours, adding water (100 mℓ) to the reaction solution, extracting the resulting deposited oily substance with n-heptane (30 mℓ), washing the n-heptane solution with a dilute hydrochloric acid aqueous solution and then with a dilute alkali aqueous solution, further washing with water till the washing water became neutral, drying the n-heptane solution over anhydrous sodium sulfate, distilling off n-heptane and recrystallizing the resulting oily substance from ethyl alcohol to obtain 3,4,5-trifluorophenyl-trans-4-propylcyclohexyl carboxylate (6.5 g). C-I: 4·5°C. The following compounds were obtained in the same manner as above: Example 13 Preparation of 2-(3,4,5-trifluorophenyl)-5-pentyl-1,3-dioxane (a compound of the formula Iia wherein R is C₅H₁₁-) (Compound No. 151) 3,4,5-Trifluorobenzaldehyde (1.6 g, 0.01 mol), which was obtained by cyanogenating 1-bromo-3,4,5-trifluorobenzene and reducing the resulting 3,4,5-trifluorobenzonitrile with diisobutylaluminum hydride , 2-pentyl-1,3-diol (1.5 g, 0.01 mol), which was obtained according to the process disclosed in Japanese patent application laid-open No. Sho 55-85583/1980, and p-toluene sulfonic acid (10 mg) were dissolved in dry toluene (30 mℓ), followed by reacting the solution under reflux for one hour while removing water formed by the reaction to the outside of the system, to complete the reaction, allowing the reaction solution to cool down to room temperature, adding water to the reaction material, washing the resulting toluene solution with a dilute alkali aqueous solution and then with water till the washing water became neutral, drying the toluene solution over anhydrous sodium sulfate, distilling off toluene and subjecting the residue to a suitable purification treatment to obtain 2-(3,4,5-trifluorophenyl)-5-pentyl-1,3-dioxane (1.6 g). The following compounds were obtained in the same manner as above: Example 14 Preparation of 2-(3,4,5-trifluorophenyl)-5-pentyl-1,3-pyrimidine (a compound of the formula Iha wherein R is C₅H₁₁-) (Compound No. 171) 3,4,5-Trifluorobenzamidine hydrochloride (12.6 g) and α-pentyl-β-ethoxyacrolein (10.2 g) were added into a solution of sodium methylate prepared by dissolving sodium (2.8 g) in anhydrous methanol (20 mℓ), followed by reacting the mixture at the reflux temperature with stirring for 6 hours, distilling off methanol after completion of the reaction, adding toluene (20 mℓ) to the reaction residue, extracting the resulting material, washing the resulting toluene extract solution with water till the washing water became neutral, drying the toluene layer over anhydrous sodium sulfate, distilling off toluene and recrystallizing the resulting oily residue from ethyl alcohol to obtain 2-(3,4,5-trifluorophenyl)-5-pentyl-1,3-pyrimidine (7.8 g). The following compounds were obtained in the same manner as above: Use example 1 A liquid crystal composition A consisting of exhibited an N-I point of 112.4°C, a viscosity at 25°C of 25.7 cP and a Δn of 0.081. This liquid crystal composition was sealed in a TN cell of 8.7 µm thick and the threshold voltage was observed to exhibit 2.56 V. When 15 parts by weight of a compound (Compound No. 1 of Example 1 of the present invention) were added to 85 parts by weight of the above liquid crystal composition, the resulting liquid crystal composition exhibited an N-I point of 77.7°C and a viscosity at 20°C of 17.9 cP. This liquid crystal composition was sealed in the above TN cell and when its threshold voltage was observed, it lowered down to 1.94 V. Use example 2 A liquid crystal composition consisting of 85 parts by weight of the liquid crystal composition A used in Use example 1 and 15 parts by weight of a compound (Compound No. 31) shown in Example 4 of the present invention was prepared. This liquid crystal composition exhibited an N-I point of 110.7°C and a viscosity at 20°C of 25.0 cP. When this liquid crystal composition was sealed in the above-mentioned TN cell, the resulting threshold voltage was 2.32 V. Use example 3 A liquid crystal composition consisting of 85 parts by weight of the liquid crystal composition used in Use example 1 and 15 parts by weight of a compound shown in Example 6 (Compound No. 51) was prepared. This liquid crystal composition exhibited an N-I point of 107.4°C and a viscosity at 20°C of 24.9 cP. When this composition was sealed in the above TN cell, the resulting threshold voltage was 2.12 V. Use example 4 A liquid crystal composition consisting of 85 parts by weight of the liquid crystal composition used in Use example 1 and 15 parts by weight of a compound of the present invention shown in Example 9 (Compound No. 81) was prepared. This liquid crystal composition exhibited an N-I point of 110.0°C and a viscosity at 20°C of 25.7 cP. When this liquid crystal composition was sealed in the above-mentioned TN cell, the resulting threshold voltage was 2.38 V. The compound provided by the present invention has a large dielectric anisotropy value Δε and a low viscosity; hence when the compound is used, it is possible to reduce the driving voltage of the resulting liquid crystal composition without raising its viscosity.

Claims: Trifluorobenzene derivatives of the formula: wherein R represents an alkyl group of 1 to 10 carbon atoms in which one -CH₂- group or two non-adjacent -CH₂- groups may be replaced by an oxygen atom and/or a -CO- group and/or a -CH=CH- group; and -A- and -B- each represent a 1,4-cyclohexylene, 1,4-phenylene, pyrimidine-2,5-diyl or 1,3-dioxane-2,5-diyl group; 1 represents 0, 1 or 2; m represents 0, 1 or 2 and 1+m≧1; and Z¹ and Z² are the same or different and each represents a group -COO-, -CH₂CH₂-, -OCH₂-, -CH₂- or -CH=CH-, or a single bond. A liquid crystal composition comprising at least two components at least one of which is a trifluorobenzene derivative as set forth in claim 1, the said derivative forming from 2 to 40% by weight of the composition.

Inventors: GOTO YASUYUKI, KITANO KISEI, GOTO, YASUYUKI, KITANO, KISEI
Applicants: CHISSO CORP, CHISSO CORPORATION
Application year: 1990
Main classification: C09K19
IPC codes: C07C69, C09K19, C07C43, C07D239, G02F1, C07C25, C07D317, C07C49, C07C17, C07D319