Oxide powder, sintered body, process for preparation therereof and target composed thereof

Abstract: Disclosed in an indium oxide powder or indium oxide/tin oxide powder having a primary particle diameter of 1 to 0.01 µm, a surface area of 15 to 50 m²/g as measured by the BET method, and a specific surface area of 2 to 5 m²/g as determined from the particle diameter distribution. This powder is prepared by coprecipitating an indium- and tin-containing salt from a solution containing indium and tin, calcining the salt, and pulverizing the calcined product preferably using a specific vibrating pulverizer. A sintered body prepared by sintering the indium oxide/tin oxide powder has a density of at least 5.3 g/cm³, a specific resistance of 2 x 10⁻³ to 2 x 10⁻⁴ Ω-cm, and a sintered particle diameter of 5 to 15 µm.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an indium oxide powder or indium oxide/tin oxide (hereinafter referred to as "ITO") powder, a sintered body, a process for the preparation thereof, and a use thereof. The ITO sintered body of the present invention exerts excellent performances as a sputtering target for use in the formation of a transparent electroconductive film by the sputtering method. 2. Description of the Related Art The demand for an ITO film as a transparent electroconductive film for use in a transparent electrode or touch panel of a solar cell or liquid crystal display has recently been increasing. A method comprising coating finely divided ITO particles on a substrate, a method comprising coating an ITO precursor on a substrate and thermally decomposing the precursor, and a method comprising forming an ITO film on the surface of a substrate by sputtering using an ITO alloy target or ITO sintered body target are known as the method for forming such an ITO film, but at the present, the sputtering method using an ITO sintered body target is most popularly adopted. The ITO sintered body has heretofore been prepared by compression-molding a mixture of an indium oxide powder and a tin oxide powder and sintering the moulded body. Nevertheless, since the indium oxide powder and tin oxide powder are inherently difficult to sinter, it is not easy to prepare an ITO sintered body having a high density by sintering these powders. The sintered density of the ITO sintered body differs to some extent according to the tin content, and the sintered density corresponding to 100% of the theoretical density is about 7.1 g/cm³. In most of the conventional ITO sintered bodies, many voids are left in the sintered structure and the sintered density is about 60% of the theoretical density at most, i.e., up to about 4.3 g/cm³, the specific resistance is larger than 2 x 10⁻³ Ω-cm, and the hue is yellowish green. Since the conventional sintered bodies have a low electroconductivity, a low thermal conductivity, and a low mechanical strength, an applicable electric power at the step of forming a film by sputtering has to be reduced and therefore, the film-forming rate is low and the discharge state becomes unstable. If an excessive electric power is applied so as to increase the film-forming rate, cracking occurs in the sintered body. Furthermore, when sputtering is carried out by using such a sintered body having a low density, a reduced substance (black substance) is formed on the surface of the sintered body, and if this substance is mingled in a transparent electroconductive film formed on the surface of the substrate, the quality of the film is degraded. Accordingly, every time the reduced substance is formed on the surface of the sintered body, the operation must be stopped and the reduced substance must be removed, and this impedes the continuous operation of sputtering. A conventional sintered body formed by heat pressing (a product prepared by a hot press) has a relatively high density, but the sintered particle diameter of this ITO sintered body is smaller than 5 µm and it sometimes happens that the sintered body is partially in the reduced state. If the sintered particle diameter of the sintered body is smaller than 5 µm, the flexural strength of the sintered body is low and the mechanical strength is naturally reduced. Moreover, the presence of the reduced substance imposes bad influences on the quality of the obtained film, as mentioned above. With a view to solving these problem, investigations have been made to increase the density and reduce the specific resistance in ITO sintered bodies. For example, there has been proposed a method in which an indium oxide/tin oxide powder having a relatively large particle diameter, that is, an average particle diameter of 3 to 6 µm, which has been once calcined at a high temperature, is used as the starting material (Japanese Unexamined Patent Publication No. 62-21751). Nevertheless, as seen from the description of examples in this patent publication, the density of the ITO sintered body obtained by using the starting material having a relatively large particle diameter is 5 g/cm³ at highest. There has also been proposed a method in which a co-precipitated ITO powder obtained from a solution containing indium and tin by using a precipitating agent is used as the starting material for obtaining a sintered body (Japanese Unexamined Patent Publication No. 62-12009). Nevertheless, the sintered density of the sintered body obtained according to this method is still about 5 g/cm³, i.e., about 70% of the theoretical density. Furthermore, there has been proposed a method in which oxygen deficiency is introduced into an ITO sintered body to reduce the specific resistance (Japanese Unexamined Patent Publication No. 63-40756). This method is effective for reducing the specific resistance of the sintered body, but it is difficult to obtain a sintered body having a high density. A method for forming an ITO sintered body having a high density by compression-sintering (hot-pressing) an ITO powder has been proposed. The apparatus used for carrying out this method is expensive and the operation is complicated. Moreover, although it is said that a sintered body having a relatively high density can be obtained according to this method, the method is industrially not advantageous. An ITO sintered body having a low specific resistance and a sputtering target made thereof are described in European Patent Publication No. 0,342,537. The sintered body is made by moulding a slurry or powder mixture containing indium oxide and tin oxide into a moulded shape and sintering the moulded shape. However, the sintered body has a relatively low density and a small sintered particle diameter, and thus the mechanical strength thereof is relatively low. As the method for preparing the oxide powder, that is, the indium oxide powder, tin oxide powder or ITO powder, there are known a method in which a powder of a corresponding metal hydroxide, oxide hydrate, organic metal salt or inorganic metal salt, or a sol or gel thereof is heat-dehydrated or thermally decomposed, and a method in which a precipitation product formed by adding a precipitating agent to an aqueous solution of a mixture of an indium salt and a tin salt or a hydrolysis product formed from this agueous solution is thermally decomposed (Japanese Unexamined Patent Publication No. 62-7627, Japanese Unexamined Patent Publication No. 60-186416 and Japanese Unexamined Patent Publication No. 58-36925). An ITO powder having a high purity can be obtained by the method previously proposed by the present inventors, in which a mixed organic acid salt prepared from an aqueous solution of mixed organic acids containing indium and tin is thermally decomposed (Japanese Unexamined Patent Publication No. 63-195101). As is apparent from the foregoing description, an ITO sintered body having a high density and a low specific resistance has not been prepared according to an industrial method. SUMMARY OF THE INVENTION The primary objection of the present invention is to provide an ITO sintered body having a density of at least 6 g/cm³, a specific resistance not larger than 2 x 10⁻³ Ω-cm and a sintered particle diameter of at least 5 µm; a process for the preparation of this sintered body; an indium oxide powder or ITO powder from which such a sintered body can be prepared; a process for the preparation of the ITO powder; and a sputtering target in which the characteristics of the ITO sintered body are utilised. An indium oxide powder or indium oxide/tin oxide powder having a primary particle diameter in the range of from 1 µm to 0.01 µm, a surface area (hereinafter referred to as "BET specific surface area") in the range of from 15 m²/g to 50 m²/g as measured by the BET method, and a specific surface area in the range of from 2 m²/g to 5 m²/g as determined from the particle diameter distribution is a novel powder, and it was found that, if this powder is sintered, a novel sintered body having a high density due to an extreme contraction of the volume by reduction of pores in the interior of the sintered body during the sintering reaction, and having a low specific resistance, is obtained. It was also found that the ITO powder can be obtained by coprecipitating a salt containing indium and tin from a solution containing indium and tin, calcining the salt at a temperature of 300°C to 800°C, and pulverising the thus-obtained indium oxide/tin oxide powder having a primary particle diameter not larger than 1 µm by using a vibrating pulveriser satisfying the requirement that the ratio of the diameter of the pulverising vessel to the vibrating amplitude is lower than 10. It also was found that the above-mentioned high-density ITO sintered body has very excellent performances as a sputtering target and if this sintered body is used as a sputtering target, a highly uniform transparent electroconductive film having a low specific resistance can be formed. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 shows the relationship between the applied electric power and the film-forming speed in the sintered bodies used in Example 2 and Comparative Example 2; Fig. 2 shows the relationship of the density and the flexural strength in the sintered bodies used in Example 2 and Comparative Example 2; and Fig. 3 shows the relationship between the sintered density and the thermal conductivity in the sintered bodies used in Example 1 and Comparative Example 3. DESCRIPTION OF THE PREFERRED EMBODIMENTS The indium oxide/tin oxide (ITO) powder used as the starting material for the production of a sintered body in the present invention is not particularly critical, as long as the conditions specified in the present invention are satisfied. Namely, a mere mixture of an indium oxide powder and a tin oxide powder and a powder of a coprecipitated oxide of indium and tin, obtained by calcining a product obtained from a solution containing indium and tin by the coprecipitation method at a temperature of 300°C to 800°C, can be used. As the method generally adopted for preparing an indium oxide powder or tin oxide powder, there can be mentioned a method in which a powder of a corresponding metal hydroxide, organic metal salt or inorganic metal salt, or a sol or gel thereof is heat-dehydrated or thermally decomposed at a temperature of from 300°C to 800°C, and as the method for preparing a coprecipitated powder of ITO, there can be mentioned a method in which a precipitating agent is incorporated into a solution of a mixture of an indium salt and a tin salt (Japanese Unexamined Patent Publication No. 60-186416 and Japanese Unexamined Patent Publication No. 62-7627) and a method in which a solution of a mixture of an indium salt and a tin salt is hydrolyzed (Japanese Unexamined Patent Publication No. 63-19510). Furthermore, the method previously proposed by the present inventors, in which a high-purity organic acid salt obtained from an aqueous solution of an organic acid containing indium and/or tin is thermally decomposed (Japanese Unexamined Patent Publication No. 63-195101), is a method for obtaining an excellent powder. The method for preparing a coprecipitated powder of ITO is preferable because the powder has a uniform composition and a sputtering target composed of a sintered body thereof can provide a uniform film. The primary particle diameter of the powder in the present invention is in the range of from 1 µm to 0.01 µm, preferably in the range of from 0.5 µm to 0.03 µm. A powder having a large primary particle diameter has a high dispersibility but a poor sintering property. On the other hand, if the primary particle diameter is too small, it is difficult to control agglomeration of the particles and a high sintering property is difficult to obtain. The primary particle diameter of the ITO or indium oxide powder prepared according to the above-mentioned conventional method is generally from several µm to 0.01 µm, and the primary particle diameter satisfies the condition specified in the present invention. Nevertheless, these primary particles of the as-prepared ITO powder are tightly agglomerated and they cannot be used, as they are, as a starting material for the production of the sintered body of the present invention. The indium oxide powder and ITO powder used in the present invention are characterized in that the primary particle is as fine as mentioned above and the particles are highly dispersed, that is, the particles are not agglomerated. As the factor for evaluating the dispersibility of a powder, there can be mentioned the surface area measured by the BET method (referred to as "BET surface area") and the particle diameter distribution. The powder used for the production of the sintered body of the present invention has a BET surface area of from 15 m²/g to 50 m²/g, preferably from 20 m²/g to 30 m²/g and a specific surface area of from 2 m²/g to 5 m²/g, preferably from 3.5 m²/g to 5 m²/g, as determined from the particle diameter distribution. If the BET surface area is too large, the powder becomes porous or the surface state is not good, and the sintering property becomes poor. Accordingly, the BET surface area is not larger than 50 m²/g. If the BET surface area is too small, the sintering property becomes poor. The ITO or indium oxide powder satisfying the above-mentioned conditions can be prepared by forming an ITO or indium oxide powder having a primary particle diameter not larger than 1 µm and highly dispersing this ITO powder mechanically. A method comprising mechanically pulverizing a ceramic powder thereby to highly disperse the powder is publicly known as the method for improving the sintering property of the ceramic powder. However, in the case of indium oxide and ITO powders, it is not true that the sintering property of any powder will be improved by mechanical pulverization. A ball mill, a sand mill, a homogenizer and a vibrating mill are generally used for mechanically pulverizing indium oxide and ITO powders. As the method for pulverizing (highly dispersing) the powder, capably of obtaining the effects of the present invention sufficiently, there can be mentioned a method in which the pulverization is carried out by using a pulverizer having a high pulverizing efficiency, such as a vibrating mill. A powder satisfying the conditions specified in the present invention cannot be obtained by using a pulverizer having a low pulverizing efficiency, for example, a rotary ball mill. Also the pulverization medium used for the pulverization is important, and in view of the pulverizing efficiency, a pulverizing medium having a high specific gravity is preferably used. Incorporation of an impure substance into the powder at this pulverization treatment results in reduction of the electroconductivity of the obtaining ITO or indium oxide, sintered body. Therefore, in the present invention, a pulverization medium having a high specific gravity and an excellent abrasion resistance is preferably used. For example, zirconia beads, hard carbon-coated beads, and diamond-coated beads are preferably used as the dispersion medium having a high specific gravity and an excellent abrasion resistance. If hard carbon-coated beads or diamond-coated beads are used, even if a powder formed by abrasion of these beads is incorporated into the oxide powder, carbon as the impure substance is removed as carbon dioxide gas at the ITO powder-sintering temperature, and no trouble arises. On the other hand, if alumina beads or glass beads are used, problems occur due to incorporation of impurities. No pulverizing effect can be obtained by resin beads because they are too light in the weight. In the present invention, a pulverization medium having a bead diameter of from 5 mm to 1 mm, especially a pulverization medium having a bead diameter of from 2 mm to 1 mm and being capable of fine pulverization, is preferably used. To improve the pulverizing efficiency and the dispersibility of the powder, a liquid is preferably added to the powder to be pulverized, whereby a slurry is formed. It is considered that water and various organic solvents can be used as the liquid to be added to the powder, but in view of the abrasion resistance of the dispersing medium, water is especially preferably used. Addition of a dispersant to the slurry is effective for enhancing the pulverizing efficiency. In view of the pulverizing efficiency, water is preferably added in such an amount that the viscosity of the formed slurry is in the range of from 0.05 Pa.s (50 cps) to 5 Pa.s (5,000 cps). If the viscosity of the pulverizing medium is outside the above-mentioned range, the pulverising efficiency is reduced. The amount of water added for forming this slurry is changed according to the properties, such as the particle size of the powder to be treated and the particular pulverisation medium used for the pulverisation, but water is used in such an amount that the powder/water weight ratio is in the range of from 80/20 to 10/90. Preferably the pulverisation time is about 1 to about 100 hours, especially 5 to 30 hours. The most important feature in the pulverization using the vibrating pulverizer is that the ratio of the diameter of the pulverizing vessel to the vibration amplitude of the vibrating pulverizer is lower than 10. If a pulverizing vessel in which the above-mentioned ratio is 10 or higher is used, the motion of the pulverizing medium within the pulverizing vessel becomes irregular and most of the pulverization medium makes only a small vibrating or sliding movement in the lower portion of the pulverizing vessel. Therefore, the pulverizing efficiency is very low. This phenomenon is especially conspicuous when the pulverization medium has a small bead size, for example, when a pulverization medium having a bead diameter of about 2 mm is used. If the powder is pulverized in this state, the powder is rendered amorphous. That is, destruction of the crystal, rather than the dispersion of the powder, is advanced. Accordingly, this pulverization treatment reduces the sintering property of the powder. In contrast, when the pulverization treatment is carried out in the state where the ratio of the diameter of the pulverizing vessel to the amplitude of the vibrating pulverizer is lower than 10, the motion of the pulverization medium is very uniform and the agglomeration of the powder is efficiently eliminated. Moreover, the destruction of the crystal by the pulverization is controlled in this pulverization treatment. In addition, in this efficient pulverization treatment, the abrasion of the pulverization medium is controlled and the purity of the treated powder can be maintained at a high level. By carrying out the pulverization treatment (highly dispersing treatment) under the above-mentioned conditions of the present invention, the ITO or indium oxide powder is highly dispersed and an ITO or indium oxide powder satisfying the conditions specified in the present invention can be obtained. Namely, an ITO or indium oxide powder having a primary particle diameter of from 1 µm to 0.01 µm, a BET surface area of from 15 m²/g to 50 m²/g and a specific surface area of from 2 m²/g to 5 m²/g as determined from the particle diameter distribution is obtained. Where the powder of the present invention is the ITO powder, the weight ratio of indium oxide to tin oxide is preferably in the range of from 98/2 to 80/20, more preferably from 92/8 to 85/15. If the content of tin oxide is lower than 2% by weight or higher than 20% by weight, a sintered body having a high electroconductivity cannot be obtained by using this powder. The ITO sintered body of the present invention is formed by molding the starting powder and firing the molded body as in the conventional method for preparing a sintered body. Any molding method can be employed for the molding of the ITO powder. For example, there can be adopted a compression molding method, a casting molding method, an injection molding method and the like. The ITO powder molded body obtained by any of these molding methods has a density of from 3 g/cm³ to 4.5 g/cm³, mostly from 3.5 g/cm³ to 4.5 g/cm³. The ITO powder molded body is then sintered. The sintering atmosphere is not particularly critical and any atmosphere can be adopted for sintering the molded body. Air, an inert atmosphere, vacuum and the like can be considered usable as the sintering atmosphere. The sintered body obtained by carrying out the sintering in an inert atmosphere or in vacuum has a larger quantity of the oxygen deficiency than in the sintered body obtained by carrying out the sintering in air, and therefore, the specific resistance can be further reduced. But, the sintered body obtained by carrying out the sintering in air is preferable for the preparation of the sintered body used as a sputtering target. In the case of ITO, the sintering starts at a temperature of about 1,050°C, but at a temperature lower than 1,300°C, the sintered density is not improved and the electroconductivity of the obtained sintered body is poor. Accordingly, the sintering temperature is preferably at least 1,300°C and more preferably at least 1,350°C. On the other hand, if the sintering temperature exceeds 1,700°C, volatilization of the tin component occurs. Therefore, in the present invention, the sintering temperature is 1,300 to 1,700°C, preferably 1,400 to 1,500°C. The retention time at the sintering temperature is several hours to scores of hours, but a retention time of 5 to 20 hours is ordinarily sufficient. The temperature-elevating rate and temperature-dropping rate are preferably lower than 200°C/hour, preferably lower than 100°C/hour. In the preparation process of the present invention, since a fine powder is used as the starting material for a sintered body, particles grow during the sintering and a high-density sintered body having a density of at least 6 g/cm³, can be obtained from the above-mentioned moulded body having a low density. The sintered body has a particle diameter of from 5 micrometers (µm) to 15 micrometres (µm). Since the ITO sintered body of the present invention has a high density and a low specific resistance, the ITO sintered body has excellent performances as a sputtering target for forming a transparent electroconductive film. Since the conventional ITO sintered body is porous and has a low specific resistance, the flexural strength is 5 kg/mm² at highest. In contrast, the high-density sintered body of the present invention has a flexural strength exceeding 5 kg/mm², mostly at least 10 kg/mm², and also has a high thermal conductivity. Therefore, cracking under a thermal shock does not occur or minimized. Moreover, since the quantity of voids present in the sintered body is very small, the etching ratio of the target surface by an argon ion, that is the sputtering efficiency, is improved, with the result that the sputtering rate is increased. In the conventional low-density ITO sintered body, the specific resistance is larger than 2 x 10⁻³ Ω-cm. In contrast, in the high-density ITO sintered body of the present invention, the specific resistance is in the range of from 2 x 10⁻³ Ω-cm to 2 x 10⁻⁴ Ω-cm, mostly from 1 x 10⁻³ Ω-cm to 2 x 10⁻⁴ Ω-cm. Accordingly, the applicable electric power can be highly increased over the applicable electric power in the conventional technique, and the discharge characteristics are improved. Still in addition, in the high-density sintered body of the present invention, little or no selective sputtering of oxygen occurs, and the blackening due to reduction of the target surface, which results in reduction of the quality of the transparent electroconductive film, is controlled, and the continuous operation of forming a transparent electroconductive film can be performed very advantageously. In view of these characteristics, it is expected that the ITO sintered body having a high density and a low specific resistance according to the present invention will show excellent performances as a sputtering target for forming a transparent electroconductive film. When the ITO powder of the present invention is used as the starting material for a sintered body, pores in the interior of the sintered body are reduced at the sintering, and a sintered body having a large sintering contraction, that is, a density of at least 6 g/cm³, can be formed. In the sintered body obtained from the conventional ITO powder, the advance of the sintering in the portion where agglomeration occurs in secondary particles of the ITO powder is different from that in the portion where such agglomeration does not occur, and therefore, the sintered particles are indeterminate and many voids are formed among the sintered particles. In contrast, in the sintered body formed from the ITO powder of the present invention, since the sintering is uniformly advanced, it is considered that densely filled sintered particles are formed and hence, the density is increased. In ITO obtained by the coprecipitation method, the distribution of tin is especially uniform, and therefore, if the sintered body prepared from this ITO is used as a target, a uniform transparent electroconductive film can be obtained over a broad range. The present invention will now be described in detail with reference to the following examples that by no means limit the scope of the invention. In the examples, percents are by weight. Example 1 Indium oxide obtained by neutralising an aqueous solution of nitric acid containing indium and calcining the formed hydroxide and tin oxide obtained by neutralising an aqueous solution of hydrochloric acid containing tin and calcining the formed hydroxide were used and mixed to obtain a mixed powder having an indium/tin ratio of 90/10 by weight. Water was added to the powder to obtain a slurry having a concentration of 50%, and the slurry was pulverised for 20 hours in a vibrating mill having a vibrating amplitude of 10 mm and a pulverising vessel diameter of 50 mm by using hard carbon-coated metal beads having a diameter of 2 mm as the pulverisation medium. In the obtained powder, the primary particle diameter was 0.1 µm as determined by observation under an electron microscope, the BET surface area was 20 m²/g, and the specific surface area was 3.3 m²/g as determined from the particle size distribution. The powder was compression-moulded in a mould to obtain a moulded body having a density of 3.7 g/cm³, and the moulded body was sintered at 1,400°C under atmospheric pressure in air. At the sintering, the temperature-elevating rate was 100°C/hour, the retention time at 1,400°C was 10 hours, and the temperature dropping rate was 100°C/hour. The obtained sintered body had a sintered density of 6.4 g/cm³, i.e., 90% of the theoretical density, a specific resistance of 3 x 10⁻⁴ Ω-cm, and a sintered particle size of 7 to 8 µm. Example 2 A film was prepared by DC magnetron sputtering by using the sintered body obtained in Example 1. The sputtering conditions were an applied electric power of 4 W/cm², a pressure of 0.6 Pa (i.e., 5 x 10⁻³Torr) and a substrate temperature of 350°C. The results are shown in Table 1. As seen from Table 1, a transparent electroconductive film having a very low specific resistance was obtained. Comparative Example 1 An aqueous solution of acetic acid containing indium and tin at an indium/tin ratio of 90/10 by weight was concentrated to obtain indium/tin mixed acetate, and an ITO powder was obtained by thermally decomposing the mixed acetate. The obtained powder had a primary particle diameter of 0.3 µm as determined by observation under an electron microscope, a BET surface area of 9 m²/g and a specific surface area of 2 m²/g as determined from the particle diameter distribution. The powder was moulded and sintered under the same conditions as described in Example 1 to obtain a sintered body having a sintered density of 4.7 g/cm³ i.e., 66% of the theoretical density, and a specific resistance of 2.4 x 10⁻⁴ Ω-cm. Although the starting powder satisfied the conditions of the primary particle diameter and specific surface area determined from the particle diameter distribution, specified in the present invention, the BET surface area was too small. Namely, agglomerated particle were present. Therefore, the sintering property was bad, and a sintered body having a high sintered density could not be obtained. Comparative Example 2 Under the same conditions as described in Example 2, a film was prepared by DC magnetron sputtering by using the sintered body obtained in Comparative Example 1. The specific resistance of the formed film is shown in Table 1. As seen from Table 1, a transparent electroconductive film having a low specific resistance as obtained in Example 1 could not be obtained. Comparative Example 3 A commercially available indium oxide powder and a commercially available tin oxide powder (reagent) were mixed together so that the indium oxide/tin oxide ratio was 90/10 by weight. The mixture was molded and sintered in the same manner as described in Example 1 to obtain a sintered body having a sintered density of 4.7 g/cm³, i.e., 66% of the theoretical density, and a specific resistance of 2 x 10⁻³ Ω-cm. The primary particle diameter of the above-mentioned mixed powder was 0.05 µm as determined by observation under an electron microscope, which satisfies the condition specified in the present invention, but the specific surface area determined from the particle diameter distribution was 2 m²/g and the BET surface area was 8 m²/g, both of which failed to satisfy the conditions specified in the present invention. Comparative Example 4 Under the same conditions as described in Example 2, a film was prepared by DC magnetron sputtering by using the sintered body obtained in Comparative Example 3. The specific resistance of the formed film is shown in Table 1. As seen from Table 1, a transparent electroconductive film having a low specific resistance as obtained in Example 1 could not be prepared. Specific Resistance (x 10⁻⁴ Ω-cm) Example 2 1.8 Comparative Example 2 3.5 Comparative Example 4 3.5 Furthermore, by using the targets used in Example 2 and Comparative Example 2, films were prepared by changing the applied electric power in the range of from 1 to 4 W/cm², and the film-forming speed at each applied electric power was determined. The results are shown in Fig. 1. The relationship between the sintered density of the sintered body and the flexural strength is shown in Fig. 2. In Figs. 1 and 2, mark "" indicates the results of Example 2 and mark "▵" indicates the results of Comparative Example 2. The relationship between the sintered density of the sintered body and the thermal conductivity thereof is shown in Fig. 3, wherein marks "a" and "d" indicate data obtained in Example 1 and Comparative Example 3, respectively. From Fig. 1, it is seen that a film could be formed at a very high speed in the case of the high-density sintered body (Example 2). From Fig. 2, it is seen that the high-density sintered body (Example 2) had a high flexural strength and cracking did not occur or occurred only to a minor extent. From Fig. 3 it is seen that the high density ITO sintered bodies had a high thermal conductivity and little or no cracking under a thermal shock occurred. In the Examples, the primary particle diameter, surface area and specific surface area of a powder, and the sintered particle diameter, surface area and specific surface area of a powder were determined as follows: (1) Primary Particle Diameter The primary particle diameter of a powder was measured directly by a scanning electron microscope and expressed as an average diameter. (2) Surface Area The surface area was determined by the BET method. (3) Specific Surface Area The particle diameter distribution was measured by a sedimentation type particle diameter distribution-measuring device "CAPA-700" supplied by Horiba Ltd., and the specific surface area was calculated from the obtained particle diameter distribution on the assumption that the particles were spherical. (4) Sintered Particle Diameter The sintered particle diameter was measured directly by observing the broken-out section of a sintered body by a scanning electron microscope and expressed as an average diameter.

Claims: An indium oxide powder or indium oxide/tin oxide powder having a primary particle diameter of from 1 micrometre to 0.01 micrometre, a surface area of from 15 m²/g to 50 m²/g as measured by the BET method, and a specific surface area of from 2 m²/g to 5 m²/g as determined from the particle diameter distribution. A powder as claimed in claim 1, which is an indium oxide/tin oxide powder composed of 80 to 98% by weight of indium oxide and 20 to 2% by weight of tin oxide. A process for the preparation of an indium oxide/tin oxide powder as claimed in claim 1 or claim 2, which comprises coprecipitating a salt containing indium and tin from a solution containing indium and tin, calcining the coprecipitated salt at a temperature of from 300°C to 800°C, and pulverising the thus obtained indium oxide/tin oxide powder having a primary particle diameter not larger than 1 micrometre by using a vibrating pulveriser, wherein the ratio of the diameter of the pulverising vessel of the vibrating pulveriser to the vibration amplitude thereof is lower than 10. A process as claimed in claim 3, wherein the vibrating pulveriser used contains a pulverising medium composed of beads of from 5 mm to 1 mm, which are selected from zirconia beads, hard carbon-coated beads, and diamond-coated beads. A process as claimed in claim 3 or claim 4 wherein the indium oxide/tin oxide powder is dispersed in the state of an aqueous slurry wherein the powder/water ratio is from 80/20 to 10/90 by weight. An indium oxide/tin oxide sintered body having a density of at least 6 g/cm³, a specific resistance of from 2 x 10⁻³ ohm-cm to 2 x 10⁻⁴ ohm-cm, and a sintered particle diameter of from 5 micrometre to 15 micrometre. A process for the preparation of an indium oxide/tin oxide sintered body as claimed in claim 6 which comprises sintering indium oxide/tin oxide powder as claimed in claim 1 or claim 2. A process as claimed in claim 7 wherein the sintering is carried out at a temperature of 1,300°C to 1,700°C. A process as claimed in claim 7 or claim 8 wherein the indium oxide/tin oxide powder is maintained at the sintering temperature for a period of 5 to 20 hours. A process as claimed in any of claims 7 to 9, wherein the indium oxide/tin powder is heated at a temperature-elevating rate of lower than 200°C/hour to the sintering temperature and the sintered product is cooled at a temperature-dropping rate of lower than 200°C/hour from the sintering temperature. A sputtering target composed of an indium oxide/tin oxide sintered body when made by a process as claimed in any of claims 7 to 10.

Inventors: IWAMOTO TETSUSHI, OGAWA NOBUHIRO, IWAMOTO, TETSUSHI, OGAWA, NOBUHIRO
Applicants: TOSOH CORP, TOSOH CORPORATION
Application year: 1990
Main classification: C01G19
IPC codes: C01G15, C01G19, C04B35