High density dynamic ram cell

Abstract: The described embodiments of the present invention provide a memory cell and method for fabricating that memory cell and memory array including the cell. The memory cell is a trench capacitor type having a transistor (1-1-2) formed on the surface of a major face of a substrate (16) and having a capacitor (2-1-2) formed in the substrate around the periphery of a trench. The capacitor and transistor are connected by a buried, heavily doped region (26) having the opposite conductivity type from the substrate. A doped storage area (24) having the same doping type as the buried doped region surrounds the trench. A field plate (30) is formed in the trench separated from the storage region by a dielectric layer (32). The field plate extends onto the isolation areas between memory cells thus providing isolation between cells using a minimum of surface area. A self-aligned process is used to form the source (14) and drain (12) for the pass gate transistor and automatic connection between the source of the transistor and the buried doping layer is made by the buried N+ layer. A sidewall silicon nitride passivation filament (38) is formed to protect the sidewalls of the interlevel insulator region between the first (30) and second (3-3, 3-4) polycrystalline silicon layers.

Description: FIELD OF THE INVENTION: The present invention is related to the field of digital integrated circuitry. More specifically, the present invention is related to the field of dynamic random access memories. In particular it relates to a device as defined in the precharacterizing part of claim 1 and to a method of forming such a device. BACKGROUND OF THE INVENTION: A device of the type mentioned above is known from US-A-4,721,987. EP-A-0 293 134 describes a method of fabricating trench cell capacitors on a semiconductor substrate. Few electronic components have received as much engineering attention as dynamic random access memory (DRAM) cells. The most commonly used memory cell is the one transistor-one capacitor type. The transistor controls current to and from a bitline attached to the drain of the transistor. Usually, a five volt charge is placed across the capacitor to represent one and a zero volt charge is placed across the capacitor to represent the zero. Data is read from the memory cell by turning on the transfer transistor and determining the charge stored on the capacitor. The sophisticated applications available in many digital devices, such as microcomputers, creates a high demand on memory capacity. This creates intense pressure to pack as much memory capacity onto a single chip as possible. Enormous amounts of engineering talent and time have been applied to the task of reducing the size of memory cells so as to provide a greater number of cells on a single chip. One such type of memory cell is the trench capacitor cell. In the trench capacitor cell, a transistor is formed in the surface of major face of a semiconductor substrate. This transistor controls current to a capacitor which is formed in some manner in or surrounding a trench etched into the major face of the substrate. By forming the capacitor around the trench, a much greater capacitance value may be attained in a given surface area of the major face of the substrate. Examples of such memory cells in the prior art are Baglee, et al., U.S. Patent No. 4,721,987, issued January 26, 1988 and assigned to the assignee of this application, Kuo, No. 4,225,945, issued September 30, 1980 and assigned to the assignee of the application and Sunami, Japan Kokai No. 51-130178, published December 11, 1976. The trench capacitor memory cells do substantially decrease the surface area of memory cells. However, these types of memory cells introduce complexities which cause poor yield and increased expense of manufacture. In addition, although the memory cells themselves have been shrunk using the prior art trench transistor concepts, the isolation areas between memory cells still occupies a substantial amount of surface area. SUMMARY OF THE INVENTION: The device according to the invention has the features described in claim 1. The described embodiments of the present invention provide a memory cell and method for fabricating that memory cell. The memory cell is a trench capacitor type having a transistor formed on the surface of a major face of a substrate and having a capacitor formed in the substrate around the periphery of a trench. The capacitor and transistor are connected by a buried, heavily doped region having the opposite conductivity type from the substrate. A doped storage area having the same doping type as the buried doping region surrounds the trench. A field plate is formed in the trench separated from the storage region by a dielectric. The field plate extends onto the isolation areas between memory cells thus providing isolation between cells using a minimum of surface area. A silicon dioxide ring is formed to protect the buried N+ layer when the trench is etched through the buried N+ layer. A self-aligned process is used to form the source and drain for the pass gate transistor and automatic connection between the source of the transistor and the buried doping layer is made by the buried N+ layer. A sidewall silicon nitride passivation filament is formed to protect the sidewalls Of the interlevel insulator region between the first and second polycrystalline silicon layers. The method for forming this cell is specified in claim 8. It provides a relatively simple method using as many self-aligned processes as possible to provide a small cell and an uncomplicated process to minimize yield losses due to process fluctuations. BRIEF DESCRIPTION OF THE DRAWINGS: Figure 1 is a schematic diagram of a dynamic random access cell memory array illustrating the operation of one embodiment of the present invention; Figure 2 is a plan view of one embodiment of the present invention; Figure 3 is a sectional view along section AA of Figure 2; and Figure 4A through 4H are sectional views showing the processing steps necessary to fabricate the embodiment of Figure 3. DETAILED DESCRIPTION: Figure 1 is an electrical schematic diagram showing the electrical characteristics of one embodiment of the present invention. Figure 2 is a plan view diagram showing the layout of four cells comprising one embodiment of the present invention. Figure 3 is a sectional view of one memory cell of the embodiment shown in Figure 2 along sectional line AA. Figures 4A through 4H are sectional view diagrams of the section shown in Figure 3 at various steps during the processing to fabricate the memory cells shown in Figure 3. The schematic diagram of Figure 1 shows a layout of four memory cells 5-1 through 5-4 arranged in an array. The array of Figure 1 is specifically adapted to function in a folded bitline scheme. In a folded bitline scheme, the word lines such as word lines 3-1 through 3-4 are connected to the gates of the pass transistors 1-1-1 through 2-2-2 of the memory cells in every other column. This allow for the connection of the sense amplifier having one input end of the comparator circuit of the sense amplifier, connected to a bitline such as bitline 4-1, and the other comparator input of the sense amplifier, connected to the adjacent bitline such as bitline 4-2. In operation, when a high voltage signal is placed on a word line, such as word line 3-3, pass transistor 1-1-2 is turned on thus connecting capacitor 2-1-2 to bitline 4-1. On the other hand, the signal placed on word line 3-3 does not cause any pass gate transistor to connect a storage capacitor to bitline 4-2. Thus bitline 4-2 may be used as a balanced load to the sense amplifier to precisely balance the characteristics of bitline 4-1. This is usually done in conjunction with precharging circuitry and a dummy memory cell to provide very precise load control between the two bitlines. If a writing signal is placed on bitline 4-1, that signal is stored on capacitor 2-1-2 and the signal provided on word line 3-3 is brought to a logical zero to complete storage of the signal provided on bitline 4-1 onto capacitor 2-1-2. Figure 2 is a plan view diagram of the embodiment shown in Figure 1 with dash lines indicating where memory cells 5-1 through 5-4 are located in the plan view of Figure 2. Transistor 1-1-2 and capacitor 2-1-2 of memory cell 5-2 are indicated in Figure 2. Contact to the drain of transistor 1-1-2 from bitline 4-1 is made at contact 8. The gate of transistor 1-1-2 is a portion of word line 3-3. Components having numbers corresponding to the numbers in Figure 1 perform the functions indicated in the schematic diagram of Figure 1. Figure 3 is a side view schematic diagram of memory cell 5-2 as taken along the section AA of Figure 2. A gate 13 which is part of word line 3-3 controls current between drain region 12 and source region 14. Drain region 12 and source region 14 are of opposite conductivity type to substrate 16. In the described embodiment, substrate 16 is P type and drain 12 and source 14 are N+ type. Also in the described embodiment substrate 16 is a crystalline silicon semiconductor substrate. Bitline 4-1 makes a connection to drain 12 through contact 18. Conductivity and contact integrity are aided by titanium silicide layer 20 formed on the surface of drain region 12. Conductivity is also aided by titanium silicide layer 22 formed on the surface of source region 14. Charge is stored on storage region 24, which is doped to N+ type. Connection between source region 14 and storage region 24 is made by N+ region 26. In addition, thick silicon dioxide region 34 provides reduced capacitive coupling at the corner between N+ region 26 and field plate region 30 to reduce the high field leakage effects at the corner between these two regions. Field plate 30 and storage region 24 together with a dielectric layer 32 form the storage capacitor 2-1-2 of the memory cell 5-2. Thick silicon dioxide region 34 is formed during the oxidation step used to form a portion of dielectric layer 32. Field plate 30 and storage region 24 are separated by dielectric layer 32. Field plate 30 also provides isolation between adjacent memory cells via electric field isolation effects across dielectric 34 into substrate 16. For example, dielectric 34 can be a silicon dioxide layer. Field plate 30 is connected to a selected potential to provide appropriate isolation levels. Silicon dioxide layer 36 provides isolation between field plate 30 and word line 3-4. Sidewall nitride layer 38 increases integrity of the interlevel insulator layer 36 and provides increased isolation between field plate 30 and source region 14. Sidewall silicon dioxide regions 40 provide increased isolation between word line 3-3 and source region 14 and drain region 12. In addition, sidewall silicon dioxide layers 40 aid in the fabrication of titanium silicide layers 20 and 22 and drain and source regions 12 and 14. Figures 4A through 4H are section diagrams showing the processing steps used to fabricate memory cell 5-2 of Figure 3. The process shown in Figures 4A through 4H begins with a P type substrate 16 as shown in Figure 4A. Silicon dioxide layer dielectric 34 is formed on the surface of substrate 16 to a thickness of approximately 400 Angstroms using thermal oxidation in an oxygen environment at a temperature of 900 degrees C for approximately 20 minutes. N+ region 26 is formed by ion implantation through silicon dioxide layer dielectric 34 using Arsenic ions at an energy of approximately 100 kiloelectron volts and a density of approximately 2 x 10 15 ions/cm 2 . This ion implantation is then driven in using a thermal heating step at a temperature of approximately 900 degrees C in an inert environment for approximately 100 minutes. This provides the structure shown in Figure 4A. The silicon dioxide layer dielectric 34 is then patterned and etched to provide opening. In the present embodiment the opening is a rectangular opening approximately 0.95u x 0.95u. Substrate 16 is then subjected to a highly anisotropic etch such as the etch shown in Douglas, U.S. Patent 4,784,720 issued November 15, 1988 and assigned to the assignee of this application. The structure is then etched in a highly anisotropic etch until a desired depth of approximately 5 microns is achieved to provide trench 44 as shown in Figure 4B. In the present embodiment, trench 44 is a right rectangular cylinder tapering toward the bottom. The sidewall regions of trench 44 are then doped using ion implantation with Arsenic ions having an energy of approximately 100 kiloelectron volts and a density of approximately 5 x 10 15 ions/cm 2 . This implantation is driven in, and the implantation damage annealed, in a Nitrogen environment at approximately 900 degrees C for approximately 60 seconds, producing the structure shown in Figure 4B. A layer of silicon nitride 32 is then deposited using chemical vapor deposition to a thickness of approximately 180 Angstroms, as shown in Figure 4C. Silicon nitride layer 32 is then sealed by thermal oxidation in a steam environment at a temperature of approximately 900 degrees C for approximately 20 minutes. In an alternative embodiment, silicon dioxide layer 32 can include a thinner silicon dioxide layer approximately 60 Angstroms covered by a very thin silicon nitride layer approximately 100 Angstroms. This silicon nitride layer is then oxidized to provide a very thin top silicon dioxide layer to provide a high quality dielectric layer. This technique is further described in Haken, U.S. Patent 4,577,390, issued March 25, 1986 and assigned to the assignee of this application. A layer of polycrystalline silicon deposited by chemical vapor deposition is deposited to a thickness of approximately 2,500 Angstroms and doped to a resistance of approximately 25 ohms per square on the structure 4C. Chemical vapor deposition provides a conformal deposition which provides a uniform thickness across the walls of trench 44. A layer of silicon dioxide is then deposited by chemical vapor deposition to a thickness of at least twice the remaining opening of trench 44, in this case approximately 5,500 Angstroms. This silicon dioxide layer is planarized using etch-back planarization. Additional silicon dioxide of approximately 2,500 Angstroms is then deposited on the planarized surface. This completely fills trench 44 and provides a relatively flat uniform surface on the top layer of silicon dioxide layer 36 as shown in Figure 4D. Silicon dioxide layer 36 and polycrystalline silicon layer 30 are then patterned using standard photolithographic and etching techniques. A layer of silicon nitride (not shown) is then deposited overall using chemical vapor deposition. This silicon nitride layer is then etched using anisotropic etching which leaves a sidewall nitride layer 38 as shown in Figure 4E. An anisotropic etch is used to remove the exposed portion of silicon dioxide layer dielectric 34 to expose substrate 16. This will of course remove a portion of silicon dioxide layer 36, but because silicon dioxide 36 is much thicker than silicon dioxide layer 34, this loss in thickness is of no real consequence. A thermal oxidation step is performed in an oxygen ambient at a temperature of approximately 900 degrees C for approximately 10 minutes to form silicon dioxide layer 41 as shown in Figure 4F. A layer of polycrystalline silicon 43 is then deposited using chemical vapor deposition and doped to a thickness of approximately 3500 Angstroms and a conductivity of approximately 70 ohms per square. Polycrystalline silicon layer 43 is then patterned and etched using standard photolithographic techniques to provide word lines 3-3 and 3-4 as shown in Figure 4G. Lightly doped regions (not shown) may be formed at this stage using an ion implantation of Arsenic ions having an energy 150 kiloelectron volts and a density of approximately 1 x 10 15 ions per centimeter 2 . A layer of silicon dioxide (not shown) is then deposited overall to a thickness of approximately 2100 Angstroms and is then etched anisotropically to provide silicon dioxide sidewall layers 40 as shown in Figure 4G. The structure of Figure 4G is then subjected to an ion implantation step of Arsenic ions at an energy of approximately 150 kiloelectron volts at a density of approximately 3 x 10 15 Atoms per square centimeter. This is then driven in to provide drain region 12 and source region 14 as shown in Figure 4H. A layer of titanium (not shown) having a thickness of approximately 1,500 Angstroms is then sputtered on the surface as a structure of Figure 4H and annealed to create titanium silicide regions 20 as shown in Figure 4H. The unreacted titanium and other by-products of the titanium direct reaction process are removed by chemical etching. This process is more fully described in Lau, No. 4,545,116, issued October 8, 1985 and Tasch, No. 4,384,301, issued May 17, 1983; both assigned to the assignee of this application. A layer of silicon dioxide is then formed on the surface of the structure of Figure 4H by chemical vapor deposition to a thickness of approximately 7,800 Angstroms and patterned to provide interlevel silicon dioxide layer 45 as shown in Figure 3. A layer of titanium/tungsten is then sputtered onto the surface of silicon dioxide layer 45 and into contact 18 to a thickness of approximately 5,100 Angstroms. This titanium/tungsten layer is patterned to provide bitline 4-1, which contacts drain 12 by way of titanium silicide layer 20. Although specific embodiments of the present invention are described herein, they are not to be construed as limiting the scope of the invention. The present embodiments are presented for exemplary purposes only and many further embodiments will become apparent to those skilled in the art in the light of this specification. The present invention is limited only by the claims appended hereto. TECHNICAL ADVANTAGES: The described embodiments of the present invention provide a highly dense memory cell by eliminating unnecessary elements such as field oxidation regions between memory cells by providing an integrated field plate structure for isolation and capacitance enhancement purposes. Heavily doped N+ region 26 provides automatic registration between the source region of transistor 1-1-2 and storage region 24. The low conductivity of small diffused and polycrystalline silicon regions is overcome by silicidation of those regions.

Claims: A semiconductor memory device comprising: a trench (44) formed in a substrate (16); an information storage region (24) comprising said trench and a substrate surface region around the trench; a first insulating layer (32) formed on the walls of the trench and above said substrate surface region and above the surface of the substrate between parts of the device and between other devices formed on the substrate; a conductive layer (30) formed on the insulating layer; a drain region (12) formed in the substrate, the drain region being separated from the portion of the substrate below the conductive layer by a channel region; a gate insulation layer (41) formed on the substrate above the channel region; a gate (3-3) formed on the gate insulating layer; and a heavily doped region (26) having a conductivity type opposite to that of the substrate, the heavily doped region being in the face of the substrate and surrounding the trench; characterized in that the first insulating layer (32) is on an insulating intermediate layer (34) on said heavily doped surface region (26) ; said first insulating layer (32) and said insulating intermediate layer (34) forming a thick isolation region interposed at a corner between said heavily doped surface region (26) and the conductive layer (30). A device as in claim 1 where said first insulating layer (32) comprises silicon dioxide. A device as in claim 1 where said first insulating layer (32) comprises a three layer structure of silicon dioxide, silicon nitride and silicon dioxide. A device as in claim 1 where said conductive layer (30) comprises polycrystalline silicon. A device as in claim 1 further comprising a bit line (4-1, 4-2) electrically connected to said drain region (12). A device as in claim 1 further comprising a word line (3-1, 3-2, 3-3, 3-4) electrically connected to said gate (3-3). A device as in claim 1 where said gate insulating layer (41) comprises silicon dioxide. A method for forming a semiconductor memory device, comprising the steps of: forming a heavily doped region (26) in a substrate (16) having a conductivity type opposite to that of the substrate, the heavily doped region being in the face of said substrate, forming an insulating intermediate layer (34) on said heavily doped surface region (26); forming a trench (44) through said insulating intermediate layer (34) and through said heavily doped region (26) into said substrate doping the walls of said trench (44) to form an information storage region (24) comprising said trench and a substrate surface region around the trench; forming a first insulating layer (32) on the walls of said trench (44) and on said insulating intermediate layer (34) ; forming a first conductive layer (30) on said first insulating layer (32); forming an opening in said first conductive layer (30), said first insulating layer (32) and said insulating intermediate layer (34), said opening being adjacent to said trench (44); said forming of said opening having as result a thick isolation region at a corner between said heavily doped surface region (26) and said first conductive layer (30), said thick silicon dioxide region (34, 40) comprising parts of said first insulating layer (32) and of said intermediate layer (34); forming a second insulating layer (41) on said substrate (16) as a gate insulator in said opening; forming and patterning a second conductive layer to provide a gate (3-3) covering a portion of said second insulating layer (41) in said opening; introducing dopant atoms into the portion of said substrate (16) in said opening not covered by said gate (3-3) to form a drain region (12). A method as in claim 8 wherein said first insulating layer (32) comprises silicon dioxide. A method as in claim 8 further comprising the step of electrically connecting a word line (3-1, 3-2, 3-3, 3-4) to said gate (3-3). A method as in claim 8 further comprising the step of electrically connecting a bit line (4-1, 4-2) to said drain region (12).

Inventors: MORINAGA SHIGEKI, TENG CLARENCE WAN-HSING, YASHIRO MASAAKI, MORINAGA, SHIGEKI, TENG, CLARENCE WAN-HSING, YASHIRO, MASAAKI
Applicants: TEXAS INSTRUMENTS INC, TEXAS INSTRUMENTS INCORPORATED
Application year: 1990
Main classification: H01L27
IPC codes: H01L27, H01L21