PROCESS FOR THE PREPARATION OF GUM BASE FOR CHEWING GUM AND A PRODUCT PREPARED BY THE PROCESS

Abstract: Process for the preparation of gum base for chewing gum on the basis of one or more of the ingredients elastomer, plasticizer, softener and filler optionally various auxiliary agents, characterised by 1) melting the softener ingredient by heating to a temperature in the range of 80 to 130 DEG C, 2) adding elastomer and possible additional gum base ingredients to the melted softener ingredient, and 3) subjecting the resulting material to high intensity mixing under high shear conditions in a planet mixer, whereupon additional gum base ingredients in solid or melted form are added under continued high shear conditions. Furthermore, the invention relates to the use of a gum base for the preparation of chewing gum. The processing time is substantially reduced and the depolymerisation of the elastomer is decreased.

Description: Process for the preparation of gum base for chewing gum and a product prepared by the process. 5 Technical Field The present invention relates to a process for the pre¬ paration of gum base for chewing gum on the basis of two or more of the ingredients elastomer, plasticizεr, softener 10 and filler and optionally various auxiliary agents. The invention furthermore relates to the use of gum base for the preparation of chewing gum. Background Art ι s Chewing gum comprises a water- insoluble portion, the gum base, which remains in the oral cavity and a watersoluble portion which is dissolved during the chewing. Aroma and sweetness are primarily provided by the watersoluble 0 portion while organoleptic properties such as structure, elasticity, film forming capacity, tackiness, softness etc are ususally provided by the gum base portion. To obtain the desired properties in a chewing gum product the gum base is prepared from ingredients selected on the basis 5 of their special organoleptic properties, their workabili¬ ty, their compatibility and their storability. It should be emphasized that in the present text the expression gum base designates both gum bases per se and the so-called gum base master batches, that is prefabricated gum bases 0 or precursors of gum bases. Gum base conventionally comprises four main ingredients: elastomer, platicizer, softener and filler and optionally additional auxiliary agents. 5 The elastomer is a very important ingredient of the gum base, as it determines the elastic properties of the chewing gum. The elastomer is usually a type of gum. Regardless of the origin, the elastomer provides the gum base and thereby the chewing gum with such elasticity as to recover from the deformation caused b3_ * chewing. A plasticizer is used in the gum base in order to provide the gum base with a certain plasticity to prevent it from recovering from the deformation too quickly, which would feel like chewing a rubber band. Said plasticizer is usually a resin of either natural or synthetic origin. The mixture of elastomer and plasticizer impart elasticity and plasticity to the gum base, but the base is still very hard, stiff and brittle. Therefore, it is necessary to soften the base. A softener, usually a type of wax, is used for this purpose. The above gum base ingredients are among other things characte ised in that they are not easily intermixable . This especially applies to the elastomer as its interior mobility between the polymer chains differs completely from the other gum base ingredients. Both elastomers and polymeric resins have a characteristic intensity of inter- molecular interaction called the cohesive energy density which usually, to some extent, must be overcome to obtain a homogenous mass . To overcome the problems of miscibility it has proved necessary in most cases to affect the polymers thermically and mechanically. Fillers are conventionally used for this purpose, said fillers increasing the friction during the mixing, thereby accelerating the mixing process. Furthermore, fillers also influence the aroma release of the chewing gum. Various processes for the preparation of chewing gum base are known. For instance, US Patent No 4,187,320 discloses a two-stage process for the preparation of chewing gum base using a solid elastomer by which process the solid elastomer is firstly subjected to high intensity mixing under high shear conditions to masticate the solid sub¬ stance to obtain a substantially uniform, lumpfree mass followed by a step-wise addition of an elastomer solvent and an oleaginous plasticizer during continued high inten¬ sity mixing until a substantially molten uniform mass is obtained. The second step of the process comprises the step-wise addition by decreasing order of viscocity of the remaining chewing gum base ingredients such as a non- toxic vinyl polymer, a hydrophobic plasticizer, additional oleaginous plasticizer and an e ulsifier during continued high intensity mixing. As a result of the dilution of the elastomer in step 1 being rather modest, the product of step 1 thereby being rather highly viscous, many portion- wise additions are necessary in step 2. The process is therefore very time-consuming. Furthermore an extensive depolymerisation of the elastomer may take place. US patent No. 3,995,064 discloses a process for the pre¬ paration of a chewing gum base by mixing elastomer and elastomer solvent under high shear conditions, whereupon hydrophobic plasticizer and hvdrophilic plasticizer are added under reduced shear conditions, followed by mixing this material with an oleaginous plasticizer and an emul- sifier to form a chewing gum base. This process is also time-consuming and requires many portion-wise additions which make the process extremely labour and equipment intensive and give rise to potential errors. Furthermore, US patent No. 4,329,369 discloses a single- step process for the preparation of chewing gum in which all materials, including gum base ingredients and all chewing gum additives are charged into a single apparatus in a single step until a thorough mixing is obtained. The process is encumbered with the drawback that the mixing apparatus is economically demanding and requires extensive cooling of the mixing chamber to keep the temperature of the chewing gum mass under control. Furthermore, dispersing and depolymerisation problems with the elastomer may arise. DK application No. 2307/84 discloses a process for the preparation of a chewing gum base wherein a filler and the hard elastomer are mixed before being mixed with a softener. The softened mixture is then subjected to high shear conditions to open the elastomer before the remaining gum base ingredients are added. The above process is encumbered with the drawback that the high shear conditions do not only open the elastomer but also cause an extensive depolymerisatio . US Patent no. 4,806,364 discloses a process for the pre¬ paration of a matrix of sweetening agents to which gum base particles are added. Said addition of gum base to a matrix of sweetening agents is stated as being reverse practice compared to prior art. As a traditionally prepared gum base is used, the depolymerisation of the elastomer must, however, be expected to be as extensive as in traditional preparation of chewing gum. US patent No. 2,036,577 discloses a process for the puri¬ fication and mixing of elastomer in the form of natural latex gum and plasticizer in the form of natural gum resin for the preparation of a resinous material suitable for use in a chewing gum base. The process is carried out by melting the gum resin in an aqueous solution of caustic soda followed by the addition of a natural latex gum. The drawback of this method is the use of an aqueous solu- tion of caustic soda, which must be assumed to affect the properties of the elastomer and to be unpleasant to work with . The present technology for the preparation of gum base is based on starting with the ingredient having the highest molecular weight, which is the elastomer, and slowly diluting it, usually with a plasticizer at first. How¬ ever, as mentioned above, this process is very time-con¬ suming as great differences in viscosity exist between the two ingredients. The process is therefore very critical at the start as very small dosages are required and as it takes very long time for the plasticizer to be incorporat¬ ed, it being necessary to be certain that the small quan¬ tity of plasticizer has been dissolved uniformly in the elastomer before adding the next dosage. A too large dosage results in a liquid phase in the form of liquid plasticizer with floating lumps of the highly viscous elastomer, whereby all mechanical work in the mixer is lost. The mixing time may thereby be extended by up to several hours. As the floating plasticizer is dissolved in the elastomer, the mechanical friction gra¬ dually increases again because the viscosity of the mass increases and the mixing arms are again able to draw the mass. The differences in viscosity are then slowly equa¬ lized and the mass becomes homogenous. The extensive mechanical friction causes, however, at the same time an extensive mechanical decomposi ion or de¬ polymerisation of the elastomer. The term mechanical decomposition denotes decomposition caused by the forces to which the elastomer is subjected during the processing. When subjected to said forces the molecular chains of the elastomer are simply torn across, whereby one or more molecular chains with a lower molecular weight than the original molecular chain are formed. This decomposition is also called mastication. In a conventional gum base preparation, carried out in a conventional mixer in the form of a kettle with built-in sigma mixing wings or another type of mixing wings and heated to about 130°C by means of steam, oil or electri¬ city, an average of 65-70% of the original elastomer quantity will be decomposed to molecular chains of a lower molecular weight. Disclosure of Invention However, it has now been found that it is possible to prepare gum bases for chewing gum by means of a procees which can be carried out very quickly and which is gentle to the elastomer, in that the above decomposition or depolymerisation of the elastomer is avoided or substan- tially reduced. The present invention therefore relates to a process of the above type characterised by 1) melting the softener by heating to a temperature in the range of 80 to 130°C, 2) adding elastomer and optionally additional gum base ingredients to the melted softener ingre¬ dient , and 3) subjecting the resulting material to high inten¬ sity mixing under high shear conditions in a planet mixer , whereupon additional gum base ingredients in solid or melted form are optionally added under continued high shear conditions. By employing said process for the preparation of gum bases a substantially reduced preparation time is obtained as the mixture of the individual gum base ingredients takes place very intensively and effectively. Furthermore, the process is very gentle to the elastomer ingredient, only about 30 to 50% of the elastomer quantity being decomposed to form compounds with lower molecular weight. According to the latest tests, even better results are obtained as no decomposition of the elastomer quantity is observed at all. This is because the extremely powerful mechanical effect on the elastomer in the beginning of the mixing process in conventional preparation is avoided as the elastomer is already dissolved in the low viscous ingre¬ dient. As a consequence of the less extensive elastomer depolymerisation, it is possible to prepare chewing gum with a more lively, elastic and resilient consistency. At the same time, it has surprisingly been found that the aroma release is more juicy or succulent and of longer duration, cf. the below examples. In a particular embodiment of the process according to the invention the elastomer is softened by heating to a temperature in the range of 75 to 150°C before being added to the molten softener ingredient. As a result the disso¬ lution takes place more rapidly as the mobility of the individual molecules is increased, whereby they are easier- ly being admixed in the surrounding medium. The mixing carried out in step 3 of the process accord¬ ing to the invention takes place in a planet mixer, par¬ ticularly preferred in an appartus of the dissolver type. Said apparatus, which comprises two circular dissolver discs, a kneading tool and a peripheral scraper, is known from the paint and lacquer industry but has surprisingly been found to be extremely suitable for the preparation of gum bases. An example of a preferred apparatus to be used when carrying out the inventive process is the GF- Planetendissolver , type VPLD8 , available from Grieser and Faulhaber, Lampertheim, the German Federal Republic. The dissolver discs preferably work at a speed of about 500 to 6000 r.p.m. , the kneading tool at a speed of about 30 to 200 r.p.m. and the peripheral scraper at a speed of about 15 to 100 r.p.m.. At the same time, the apparatus can be provided with commonly known heating and cooling means and with vacuum and/or an inert gas, such as nitro¬ gen, to be used in connection with especially sensitive elastomer types. This is a great advantage in connection with the preparation of gum base as the raw materials conventionally used for this purpose are rather sensitive to for instance high temperatures and atmospheric air. The elastomeric ingredient of the gum base is preferably selected among hevea brasiliensis , polyisobutylene , iso- prene - isobutylene copolymer, styrene-butadiene-copolymer , chicle, jelutong, sorva, sorvinha, niger gutta, gutta hang kang and masseranduba balata. Before being added to the melted softener ingredient the elastomer is divided into a particle size preferably not exceeding 25 mm, most preferably not exceeding about 12 mm. If desired, a powder- ing agent, such as for instance calcium carbonate or talc may be added to prevent adhesion. The softener ingredient is preferably selected among rice bran wax, micro-crystalline wax, paraffin wax, bees' wax, candelilla wax, polyethylene wax, synthetic paraffin wax, petroleum wax, lanolin, pork fat, suet, raw/partially cured/completely cured soya bean oil, coconut oil, palm oil, rape seed oil, peanut oil, shea seed oil, corn oil (maize oil) , cotton seed oil, sunflower oil, mono/diglyce - rides, esterified mono/diglycerides , sugar esters and triacetin. The plasticizer is preferably selected among glycerol esters of partially hydrogenated wood or gum rosin, of partially dimerised rosin or of polymerised rosin or of wood, gum or tall oil rosin, methyl esters of partially hydrogenated rosin, pentaerytritol esters of partially hydrogenated wood or gum rosin, pentaerythritol esters of gum or wood rosin, terpene resin containing α/β-pinene and/or dipentene, terpene resin containing delta limonene and polyvinyl acetate resins having a molecular weight of at least 2000, polyvinyl alcohol, vinyl acetate and vinyl laurate copolymer. If a filler is used in the gum base, said filler is pre¬ ferably selected among calcium carbonate, talc, kaolin, aluminum oxide and silicon oxide. If required, the gum base may comprise different auxiliary agents, said auxiliary agents preferably being selected among antioxidants , such as butyl hydroxyanisole , butyl- hydroxytoluene , propyl gallate and tocopherols, inorganic or organic colourants and sodium stearate, potassium stearate and sodium sulphide. The gum base preferably include about 2 to 30 weight% elastomer, about 5 to 75 weight% plasticizer, about 4 to 65 weight% softener, about 0 to 60 weight% filler and about 0 to 20 weight% auxiliary agent. Furthermore, the invention relates to the use of gum base for the preparation of chewing gum, wherein the chewing gum is prepared in a planet mixer by mixing the gum base with usual chewing gum ingredients, such as one or more sweetening agents, flavorings and optionally additional chewing gum ingredients. A very short duration of prepa- ration of the chewing gum is thereby obtained as well as a more gentle processing of the chewing gum ingredients than by the prior art methods. The short duration of preparation means that the finished chewing gum obtains a more elastic consistency and that the aroma release takes place faster and with greater intensity as regards taste, and juicyness as well as freshness. The further scope of applicability of the present invention will become apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and specific examples, while indi- eating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from this detailed description. Brief Description of Drawings The invention is described in more details below with reference to the accompanying drawing in which Fig. 1 is a diagrammatic view of a preferred planet mixer or dissolver to be used when carrying out the process according to the invention, and Fig. 2 illustrates a taste profile in the initial/inter¬ mediate phase for a sugar-containing piece of chewing gum comprising a gum base prepared according to prior art, Fig. 3 illustrates a taste profile in the initial/inter- mediate phase for a sugar-containing piece of chewing gum comprising a gum base prepared according to the invention, Fig. 4 illustrates a taste profile in the end phase for a sugar-containing piece of chewing gum prepared according to prior art, Fig. 5 illustrates a taste profile in the end phase for a sugar-containing piece of chewing gum prepared according to the invention, Fig. 6 illustrates a taste profile in the ini ial/inter¬ mediate phase for a sugarless piece of chewing gum com- prising a gum base prepared according to prior art. Fig. 7 illustrates a taste profile in the initial/inter¬ mediate phase for a sugarless piece of chewing gum com- prising a gum base prepared according to the invention, Fig. 8 illustrates a taste profile in the end phase for a sugarless piece of chewing gum comprising a gum base prepared according to prior art technique, and Fig. 9 illustrates a taste profile in the end phase for a sugarless piece of chewing gum comprising a gum base prepared according to the invention. Best Mode for Carrying Out the Invention The planet mixer shown diagrammatically in Fig. 1 comprises a container 1, containing the materials forming part of the gum base, and two sets of tools for processing of the materials. The tools are connected to a gear box 2, which contains a sun and planet gear and is driven by means of a motor not shown. The first set of tools comprises two stirrers 4, 5, placed diametrically opposite each other in relation to the central axis 3 of the container, said agitators each comprising a shaft 6 connected to the gear box at its upper end and provided with a stirring disc 7, 8, a so- called dissolver disc with blades 9, 10, at its lower end. The dissolver discs 7, 8 of the two stirrers 4, 5 are placed in different levels of the container 1 and the stirrers are adapted to rotate both about their axis and about the central axis 3 of the container. The other set of tools comprises a kneading tool 11 adapted to rotate about its own axis and about the central axis of the container, said kneading tool 11 comprising a vertical shaft 12 with radially extending wings 13 and a peripheral scraper 14, said peripheral scraper 14 com¬ prising an shaft 15 and a scraper plate 16 extending radi¬ ally therefrom, said scraper plate 16 being adapted to be moved peripherically along the container thereby trans¬ porting the material from the container periphery and into the working area of the other tools. The invention is illustrated further below by means of the following examples. Example 1 Preparation of gum base nraster batch A so-called gum base master batch (that is a prefabricated gum base) is prepared by use of the below ingredients: Composition in Ingredient Ouantitv/g percentages Polyisobutylene 1050 21% Terpene resin 1750 35% Micro-crystalline wax 2200 44% Total 5000 100% The elastomer polyisobutylene is divided into a particle size not exceeding 12 mm. The wax is melted and kept fluid at 100°C under nitrogen until use. The container for the dissolver is heated to 120°C and the molten micro-crystailine wax is added. Subsequently, the finely divided elastomer is added and finally the resin is added. The mixing tools are then lowered into the container and the air is removed from the mixing chamber by means of a vacuum pump. The motor is activated and the mixing process started. In the beginning the product will have a very low viscosity like the molten micro-crystailine wax, but as the resin melts and the elastomer is dissolved the viscosity will gradually in¬ crease. After three hours of mixing a homogenous result is obtained. The end product has a temperature of 168°C. The master batch is then discharged and may either be used directly for the preparation of gum base in a fluid form or it may be cooled and used for the preparation of gum base on the basis of the master batch at a later time. A master batch prepared as described above displays the following typical viscosity data compared to a master batch prepared according to the prior art: Master batch prepared on dissolver: 500-800,000 cps Master batch prepared on conventional mixer with sigma wings: 110-300,000 cps The above analytic data have been measured on a Brookfield viscosimeter type RVT at 110°C with a 15 g sample, spindle 2 , rate of speed 2. Processing time for the preparation of master batch on dissolver: around 3 hours Processing time for the preparation of master batch on conventional mixer with sigma-wings: around 4.5 hours A reduced depolymerisation of the elastomer and a proces- sing time which is reduced by 33% are thus obtained by the use of the process according to the invention compared to a conventional preparation on a usual mixer with sigma wings . Example 2 The below master batch is prepared in a manner correspond¬ ing to the manner desribed in Example 1: Composition in Ingredient Quant ty/g Percentages Polyisobutylene 950 19% Polyvinylace ate 1550 31% Micro-crystalline wax 2500 50% Total 5000 100% Example 3 The following master batch is prepared analogous to Example 1: Composition in Ingredient Ouantitv/g Percentages Isoprene-isobutylene- copolymer 1250 25% Glyceroles er of polymerised wood rosin 1250 25% Paraffin wax 2500 50% Total 5000 100% Example 4 The following master batch is prepared analogous to Example Composition Ingredient Ouantitv/g in percentages Isoprene-isobutylene- copolymer 1000 20% Glycerolester of partially hydrogenated gum or wood rosin 1200 24% Micro-crvs ailine wax 2800 56% Total 5000 100% Example 5 The below master batch is prepared analogously to Example 1: Composition Ingredient Quantitv/g in percentage Isoprene-isobutylene- copolymer 1000 20% Polyvinyl acetate 1200 24% Micro-crystalline wax 2800 56% Total 5000 100% Example 6 Preparation of gum base A gum base with the following composition is prepared; Composition Ingredient Ouantitv/g in percentages Master batch according to Example 1 1000 20% Low molecular weight polyisobutylene 200 4% Glycerol ester of partially hydrogenated gum rosin 1100 22% Polyvinyl acetate 1100 22% Mono/diglycerides 100 2% Cured fat 150 3% Micro-crystailine wax 450 9% Calcium carbonate 900 18% Total 5000 100% The softener ingredients mono/diglycerides , cured fat and micro- crystailine wax are melted in a separate melting container by heating to 100°C under nitrogen, whereupon the elastomer polyisobutylene is added. Blending is carried out until a homogenous oleaginous liquid is formed. The softener and the elastomer is then led to the dissolver container and plasticizer and filler are added. Finally, the master batch is added in suitable small bits at room temperature . The dissolver container is returned to its place under the mixing tools which are lowered into the container. The temperature of the mixer container is 120°C. Before the mixing tools are started, a vacuum of -0.6 ato is established, whereupon the mixing tools are started at the following rates of speed: dissolver discs 2000 r.p.m. kneading tools 150 r.p.m. peripheral scraper 75 r.p.m. After mixing for two minutes the rate of speed of the dissolver discs is increased to 3900 r.p.m. and after further four minutes of mixing the mixing tools are stop¬ ped. The pressure is increased to atmospheric pressure and the mixing tools are raised. The result is a homo- genous gum base with an end temperature of 115°C. The gum base is then poured into so-called slabs or is divided into particles and cooled on commercially available process equipment. The total mixing time is thus six minutes. Example 7 A gum base of the following composition is prepared: Page missing at the time of publication After mixing for two minutes the mixing tools are stopped. The pressure is increased to normal atmospheric pressure and the mixing tools are raised. The end product is a homo- genous gum base with a temperature of 100°C. The finished gum base may be processed according to the procedure described in Example 6. The total mixing time is thus two minutes . A gum base prepared as described above displays the follow¬ ing typical viscosity date compared to a gum base prepared according to prior art, the measuring method being the same as described in Example 1: Gum base prepared on dissolver: 45,000-80,000 cps Gum base prepared on conventional mixer with sigma wings: 15,000-30,000 cps Processing time for preparation of gum base on dissolver: 2 minutes Processing time for preparation of gum base on conventional mixer with sig a wings . 80 minutes As appears from the above, a subs antially reduced proces¬ sing time with consequent economic and technological advantages, manifested in a substantially reduced decom- position of the elastomer, is obtained Example 8 A gum base with the follwing composition is prepared: Composition Ingredient Ouantitv/g in percentages Master batch according to Example 4 1000 20% Low molecular weight polyisobutylene 200 4% Glycerol ester of polymerised gum rosin 450 9% Glycerol ester of partially hydrogenated gum rosin 700 14% Polyvinyl acetate 1250 25% Mono/diglycerides 150 3% Micro-crystailine wax 100 2% Cured ' fat 250 5% Calcium carbonate 900 18% Total 5000 100% The softener ingredients mono/diglycerides, micro - crystal¬ line wax and cured fat are charged in a separate melting container and melted by heating to 100°C covered by nitro¬ gen. The master batch is added and mixing is carried out until a thick homogenous oleaginous fluid is formed. The mixture is discharged into the dissolver container and the other ingredients are added at room temperature. The dissolver container is returned to its place under the mixing tools which are lowered into the container. The temperature of the mixing container is 120°C. The vacuum pump is activated and set to -0.6 ato. Then the mixing tools are started at the following rates of speed, dissolver discs 2000 r.p.m. kneading tools 150 r.p.m. peripheral scraper 75 r.p.m. After mixing for one minutes the rate of speed of the dissolver discs is increased to 3900 r.p.m. and after further four minutes of mixing the mixing tools are stop- ped. The vacuum in the mixing chamber is increased to atmospheric pressure and the mixing tools are raised. The end product is a homogenous gum base with a temperature of 115°C. The gum base may be processed as described in Example 6. The total mixing time is thus five minutes. A gum base prepared as described above displays the follow¬ ing typical viscosity data compared to a gum base prepared according to prior art: Gum base prepared on dissolver: 39,000 cps Gum base prepared on conventional mixer with sigma wings: 22,000 cps Processing time for preparation of gum base on dissolver: 5 minutes Processing time for preparation of gum base on conventional mixer with sigma wings. 80 minutes Example 9 Preparation of gum base without the use of master batch A gum base with the following composition is prepared: Composition Ingredient Ouantitv/g in percentages Low molecular weight polyisobutylene 250 5% 5 Glycerol ester of wood rosin 750 15% Polyvinyl acetate 2500 50% Mono/diglycerides 50 1% Cured fat 300 6% Triacetin 200 4% 10 Talc 9-50 19% Total 5000 100% The softener ingredients mono/diglycerides, cured fat and triacetin are charged into a separate melting container 15 and melted by heating to 100°C. The elastomer is added and mixing is carried out until a homogenous, oleaginous fluid is formed. This mixture is kept heated to 100°C under nitrogen. The mixture is charged directly into the dissolver container, whereupon glycerol ester of rosin, 20 polyvinyl acetate and talc are added. The dissolver container is placed under the mixing tools which are lowered into the container. The temperature of the container is 120°C. Before starting the mixing tools 25 a vacuum of -0.8 ato is established and the mixing tools are started at the following rates of speed: dissolver discs 3900 r.p.m. kneading tools 150 r.p.m. peripheral scraper 75 r.p.m. 30 After mixing for 15 minutes the mixing tools are stopped. The pressure is increased to normal atmospheric pressure. The mixing tools are raised and a gum base with a conven¬ tional fibrous structure is seen having a temperature of 35 98°C. The gum base may subsequently be poured into slabs or be cooled and divided into particles on commercially available equipment. The total mixing time is thus 15 minutes . Example 10 Preparation of chewing gum A chewing gum having the following composition is prepared: Composition Ingredient Ouantitv/g in percentages Gum base according to Example 6 1100 22.0% Sugar 3000 60.0% Glucose syrup 800 16.0% Liquid lecithin 20 0.4% Glycerol 40 0.8% Flavouring agents 40 0.8% Total 5000 100.0% The gum base, in a liquid form, is charged in the dissolver container, which is preheated tc 60°C, whereupon glucose syrup is added. 1/3 of the sugar quantity as well as flavouring agents and glycerol are added. The container is then placed under the mixing tools which are lowered thereinto. The mixing process can now be started, the mixing tools being set at the following rates of speed: dissolver discs 700 r.p.m. kneading tools 150 r.p.m. peripheral scraper 75 r.p.m. After one minute the rest of the sugar is added and after three minutes of mixing a homogenous chewing gum mass with a temperature of 58 ° C is obtained. Processing time for chewing gum prepared according to the invention: about 3 minutes Processing time for the preparation of chewing gum by conventional process in mixer with sigma mixing wings: about 25 minutes In addition to a reduction of the processing time in the order of 90%, a more elastic consistency in the chewing gum is obtained because of the shorter duration of the mechanical effect on the chewing gum mass by using fluid gum base and simultaneously processing the chewing gum mass for very short time. Example 11 A chewing gum having the following composition is prepared Composition Ingredient Ouantitv/g .n percentages Gum base according to Example 6 1000 20.0% Sugar 3000 60.0% Glucose syrup 950 19.0% Liquid sorbitol (70%) 25 0.5% Flavouring agents 25 0.5% Total 5000 100.0% The preparation is carried out in a manner corresponding to Example 10 above. Example 12 A sugarless chewing gum having the following composition is prepared: Composition Ingredient Ouantitv/g in percentages Gum base according to Example 8 1500 30% Sorbitol 1750 35% Xylitol 1050 21% Lycasin ™ 80/55 500 10% Glycerol 75 1.5% Lecithin 25 0.5% Flavouring agent 100 2% Total 5000 100% The preparation is carried out analogously to Example 10 above . Organoleptic evaluation of chewing gum To compare a chewing gum containing a gum base prepared according to the invention and a chewing gum according to prior art, an organoleptic evaluation was carried out of a chewing gum containing a gum base according to Example 6 or 8 and of an analogous chewing gum containing a gum base prepared according to prior art. Figs. 2-5 illustrate taste profiles of sugar sweetened dragees , divided into initial/intermediate phase and end phase . The taste evaluations were undertaken by a tasting panel and the organoleptic evaluation was carried out according to the conventional evaluation method for chewing gum, i.e. an organoleptic evaluation in which the chewing period is divided into three phases designated: - initial phase 0 to 10 seconds intermediate phase 10 seconds to 5 minutes and until the sweetener has been chewed out, usually after about 3 minutes, end phase from the sweetener has been chewed out and until the chewing gum is discarded. The results are plotted on a semicircular diagram where the distance from the centre of the circle to the given point indicates an intensity value. As a result, a graphic illustration of the complicated factors is obtained where the area filled out in the diagram represents a measurement of the taste intensity. As appears from a comparison of Figs. 2 and 3, the taste sets in on a higher level and a greater taste release is therefore perceived from the start. Furthermore the chewing gum containing a gum base prepared according to the inven¬ tion releases a greater freshness during the chewing and thereby also provides a greater mouth freshness. In addi¬ tion to this, the sweetness and juiciness of the chewing gum have been improved which provides a good back-up to the increased taste level and the freshness. The chewing gum also releases liquorice with a greater sweetness intensity which is escpecially perceived from after about 2 minutes and until the chewing gum is spit out. Finally, the con¬ sistency of the chewing gum is more elastic and resilient and the chewing gum is therefore perceived as a more exciting piece of chewing gum to chew. To sum up, the taste level of the initial and intermediate phase is generally increased and an increase of sweetness and juiciness is also seen. As appears from Figs. 4 and 5, the same pattern is seen in the end phase for level of end taste, freshness, sweet¬ ness, liquorice sweetness and peak notes. The chewing consistency is also permanently perceived as more elastic in the end phase in the chewing gum containing a gum base prepared according to the invention compared to chewing gum according to prior art. A organoleptic evaluation of a sugarless dragee was further carried out, cf. figs. 6-9. As appears from a comparison of Figs. 6 and 7, the taste sets in at a higher level in the chewing gum containing a gum base prepared according to the invention and the taste is thereby perceived as being more intense. Further¬ more, the taste is released with a greater freshness and the freshness is also perceived as more intense already from the Initial phase and continues to give a fresher taste. An increased level of sweetness is also perceived which gives a good back-up to the increased level of taste. Further, the chewing gum is perceived as being more elastic than a chewing gum containing a gum base prepared according to prior art and the bitterness from sweeteners, such as sorbitol, and from liquorice are perceived to be less. When comparing Figs . 8 and 9 it is seen that also in the end phase a higher level of taste is observed. The fresh- ness is still greater and sweetness, liquorice sweetness and liquorice peak notes have also been increased in the chewing gum containing a gum base prepared according to the invention. Finally, the product is perceived as having a greater elasticity. It will be obvious that the above specification only comprises preferred embodiments of the invention and that many variations and modifications may be made thereof without thereby deviating from the scope of the invention. Thus, other planet mixers than the preferably used -dis¬ solver described may be used and the same may be used to prepare chewing gum containing gum base prepared in any suitable way

Claims: Claims 1. Process for the preparation of gum base for chewing gum on the basis of two or more of the ingredients elas- tomer, plasticizer, softener and filler and optionally various auxiliary agents , c h a r a c t e r i s e d by 1) melting the softener by heating to a temperature in the range of 80 to 130°C, 2) adding elastomer and optionally additional gum base ingredients to the melted softener ingre¬ dient, and 3) subjecting the resulting material to a high intensity mixing under high shear conditions in a planet mixer , whereupon additional gum base ingredients in solid or melted form are optionally added under continued high shear conditions. 2. Process as claimed in claim 1, c h a r a c t e r - i s e d by the elastomer being softened by heating to a temperature in the range of 75 to 150°C before being added to the melted softener ingredient. 3. Process as claimed in claim 1, c h a r c t e r - i s e d by the planet mixer comprising two circular dis- solver discs, a kneading tool and a peripheral scraper. 4. Process as claimed in claim 3, c h a r a c t e r ¬ i s e d in that the dissolver discs work at a speed of about 500-6000 r.p.m. , the kneading tool at a speed of about 30 to 200 r.p.m. and the peripheral scraper at a speed of about 15 to 100 r.p.m.. 5. Process as claimed in claim 1, c h a r a c t e r ¬ i s e d by the elastomer being selected among hevea bra- siliensis, polyisobutylene, isoprene - isobutylene copolymer, s tyrene-butadiene-copolymer , chicle, jelutong, sorva, sorvinha, niger gutta, gutta hang kang and masseranduba balata. 6. Process as claimed in claim 1, c h a r a c t e r - i s e d in that before being added to the melted softener ingredient the elastomer is divided into a particle size not exceeding 25 mm, preferably not exceeding about 12 mm. 7. Process as claimed in claim 1, c h a r a c t e r - i s ed in that the softener ingredient is selected among rice bran wax, micro-crystailine wax, paraffin wax, bees ¬ wax, candelilla wax, polyethylene wax, synthetic paraffin wax, petroleum wax, lanolin, pork fat, suet, raw/partially cured/completely cured soya bean oil, coconut oil, palm oil, rape seed oil, peanut oil, shea seed oil, corn oil, cotton seed oil, sunflower oil, mono/diglycerides, esteri- fied mono/diglycerides, sugar esters and triacetin. 8. Process as claimed in claim 1, c h a r a c t e r - i s e d in that the plasticizer is selected among glycerol esters of partially hydrogenated wood or gum rosin, of partially dimerised rosin or of polymerised rosin or of wood, gum or tall oil rosin, methyl esters of partially hydrogenated rosin, pentaerytritole esters of partially hydrogenated wood or gum rosin, pentaerythritol esters of gum or wood rosin, terpene resin containing α/β-pinene and/or dipentene , terpene resin containing delta limonene and polyvinyl acetate resins having a molecular weight of at least 2000, polyvinyl alcohol, vinyl acetate and vinyl laurate copolymer. 9. Process as claimed in claim 1, c h a r a c t e r ¬ i s e d by the filler being selected among calcium car- bonate, talc, kaolin, aluminum oxide and silicon oxide. 10. Process as claimed in claim 1, c h a r a c t e r- S i s e d in that the auxiliary agents are selected among antioxidants , including butyl hydroxyanisole, butylhydroxy- toluene, propyl gallate and tocopherols , inorganic or organic colourants and sodium stearate, potassium stearate and sodium sulphide. 0 11. Process as claimed in claim 1, c h a r a c t e r - i s e d in that about 2 to 30 weight% elastomer, about 5 to 75 weight% plasticizer, about 4 to 65 weight% softener, about 0 to 60 weight% filler and about 0 to 20 weight% 5 auxiliary agents are used calculated on the final gum base. 12. The use of gum base for the preparation of chewing gum, c h a r a c t e r i s e d in that the chewing gum is prepared in a planet mixer by mixing the gum base with 0 conventional chewing gum ingredients, such as one or more sweeteners, flavourings and optionally further additives. 13. Product prepared by the process as claimed in any of the preceding claims 1 to 11. 5 0 5

Inventors: NIELSEN HANS ERIK, NIELSEN, HANS, ERIK
Applicants: VECATA AS, VECATA A/S
Application year: 1990
Main classification: A23G3
IPC codes: A23G4