Thermoplastic molding composition and molded articles with enhanced surface coating susceptibility

Abstract: Thermoplastic molding compositions containing 30 to 75 parts by weight polypropylene and 25 to 70 parts by weight ethylene/C₃-C₁₆ monoolefin copolymer or ethylene/C₃-C₁₂ monoolefin/polyene copolymer contain also 4 to 15 parts by weight of oxidized or carboxylated polyolefin which renders the surface of molded articles susceptible to surface coating, especially with polyurethane paints.

Description: This invention relates to molding compositions and more especially to the application of coatings to surfaces of molded articles formulated of thermoplastic materials referred to in the trade as thermoplastic elastomers (TPE) or thermoplastic olefinic elastomers (TPO), such as EPDM-polypropylene compositions. Many automotive and other articles are molded or otherwise fabricated of thermoplastic compositions which embody about equal parts by weight of (1) an interpolymer of ethylene, one or more C 3 -C 16 mono-olefins, preferably propylene and a polyene, preferably 5-ethylidene-2-norbornene, generally referred to in the trade as an EPDM and (2) a thermoplastic polyolefin resin, preferably polypropylene. One of the problems faced by articles molded or otherwise fabricated of such TPO compositions, is the difficulty of achieving strong adherence of coatings applied to the surfaces of such articles, as in the color coating of such articles, especially with a polyurethane based coating composition. To the present, in order to provide for a desirable adhesion of a paintable coating, it has been the practice to first apply an adhesion promoter, followed by the application of a prime coat, and then the application of the final paintable color coat. The ability to eliminate the promoter as a first coating while achieving strong adherence of the paintable color coating would materially enhance the entire process especially from the standpoint of material cost, processing time and conservation of space, equipment, and labor. The present invention seeks to provide a TPO composition of the type described which is directly paintable (DP-TPO) to provide strong adherence of applied coatings without the need of a first adhesion promoter coating and in which such directly coatable or otherwise paintable article can be achieved by modification of the composition of which the article is formed but without undesirable effect on the physical or chemical properties of the article. In accordance with the invention, that objective can be achieved when the TPO composition is formulated to contain from 4 to 15 percent by weight of an oxidized or carboxylated polyolefin, preferably an oxidized polyethylene. It is preferable to substitute the desired amount of oxidized polyethylene for polypropylene in the composition, but the desired results will be experienced when the carboxylated polyethylene or oxidized polyethylene is present in the described amounts whether substituted for the polypropylene or the EPDM or both in the TPO composition. In accordance with the invention there is now provided a composition for use in molding articles having an improved surface bonding relationship with applied organic coatings, the composition comprising a substantially uniform mixture of at least 30 weight % of thermoplastic polypropylene resin, and at least 25 weight % of a polymer selected from (a) copolymers of ethylene and C 3 -C 16 mono-olefins and (b) terpolymers of ethylene, C 3 -C 12 mono-olefins and polyenes, and from 4 to 15 weight % of an oxidized or carboxylated polyolefin, the oxidized polyolefin containing at least 1 percent by weight oxygen and having an acid number of not more than 50, and the carboxylated polyolefin containing at least one carboxyl group per molecule. As previously pointed out, one of the principal components of the TPO composition of which the articles are molded or otherwise fabricated comprises a thermoplastic polypropylene resin which is well known to the trade and readily commercially available. The thermoplastic polypropylene resin is present in the TPO composition in an amount of 30 to 75 percent by weight and preferably in an amount of 30-70 percent by weight of the composition. When the resin is present in an amount greater than 70 percent by weight of the composition, the composition behaves more like an impact modified thermoplastic than a TPO. It will be apparent to those skilled in the art that such impact modified thermoplastics containing the oxidized polyolefin as an additive would also exhibit improved paint adhesion characteristics. Thus the useful range of compositions includes levels of resin up to 90 parts by weight per 100 parts by weight of the total composition. The other principal component of the TPO composition is either a copolymer of ethylene and a C 3 -C 16 mono-olefin, preferably an ethylene-propylene copolymer rubber (EPM) or a terpolymer of (1) ethylene, (2) a C 3 -C 16 mono-olefin, preferably propylene and (3) a polyene (EPDM) such as 5-ethylidene-2-norbornene. Such other component is present in the TPO composition in an amount of at least 25 percent by weight and preferably at least 30 percent by weight, more preferably 40-60 percent by weight of the total composition. As the EPM rubber, use can be made of an ethylene-monoolefin and preferably an ethylene-propylene copolymer rubber formed by copolymerization in solvent solution, in the presence of a Ziegler-type catalyst, of ethylene and one or more mono-olefins, preferably propylene, but which may include 1-butene, 1-pentene, or other mono-olefins having 3-12 carbon atoms. The ratio of ethylene to propylene or C 3 -C 12 mono-olefin may range from 10-95 mole% ethylene to 90-5 mole% of propylene or other mono-olefins. The preferred range of ethylene to propylene or other mono-olefin is 45-85 mole% of ethylene to 15-55 mole% of propylene or other mono-olefin. In the preparation of the EPDM interpolymer rubber, the polyene monomer containing a plurality of carbon-to-carbon double bonds may be selected from those disclosed in the prior art for use as third monomers in the preparation of ethylene-mono-olefin-polyene terpolymers, including open chain polyunsaturated hydrocarbons containing 4-20 carbon atoms, such as 1,4-hexadiene, monocyclic polyenes and polycyclic polyenes. The polyunsaturated bridged ring hydrocarbons or halogenated bridged ring hydrocarbons are preferred. Examples of such bridged ring hydrocarbons include the polyunsaturated derivatives of bicyclo(2,2,1)heptane wherein at least one double bond is present in one of the bridged rings, such as dicyclopentadiene, bicyclo(2,2,1)hepta-2,5-diene, the alkylidene norbornenes, and especially the 5-alkylidene-2-norbornenes wherein the alkylidene group contains 1-20 carbon atoms and preferably 1-8 carbon atoms, the alkenyl norbornenes, and especially the 5-alkenyl-2-norbornenes wherein the alkenyl group contains about 3-20 carbon atoms and preferably 3-10 carbon atoms. Other bridged ring hydrocarbons include polyunsaturated derivatives of bicyclo(2,2,2) octane as represented by bicyclo(3,2,1) octane, polyunsaturated derivatives of bicyclo(3,3,1) nonane, and polyunsaturated derivatives of bicyclo(3,2,2) nonane. Specific examples of preferred bridged ring compounds include 5-methylene-2-norbornene, 5-ethylidene-2-norbornene, 5-n-propylidene-2-norbornene, 5-isobutylidene-2-norbornene, 5-n-butylidene-2-norbornene, dicyclopentadienes; the methyl butenyl norbornenes such as 5-(2-methyl-2-butenyl)-2-norbornene or 5-(3-methyl-2-butenyl)norbornene, and 5-(3,5-dimethyl-4-hexenyl)-2-norbornene. The elastomer prepared from 5-ethylidene-2-norbornene is much preferred as it has outstanding properties and produces many unusual and unexpected results. The EPDM backbone rubber may contain chemically bound therein molar ratios of ethylene to propylene or other C 3 -C 16 mono-olefin varying between 95:5 to 10:90 ethylene:propylene, and preferably from 85:15 to 45:55 ethylene:propylene. The polyene or substituted polyene may be chemically bound therein in an amount of 0.1 to 10 mol percent, and preferably 0.3 to 1 mol percent. The level of unsaturation in the backbone rubber may range for 0-15 double bonds per 1,000 carbon atoms in the polymer chain. The interpolymerization is carried out in the presence of a Ziegler catalyst of the type well known to the prior art. Such Ziegler type catalysts are disclosed in a large number of patents, such as U.S. patents No. 2,933,480, No. 3,093,620, No. 3,093,621, No. 3,211,709 and No. 3,113,115. Examples of Ziegler catalysts include metal organic coordination catalysts prepared by contacting a compound of a heavy metal of the group IV-a, V-a, VI-a and VII-a of the Mendeleeff periodic system of elements, such as titanium, vanadium and chromium halides with an organo-metallic compound of a metal of groups I, II or III of the Mendeleeff periodic system which contains at least one carbon-metal bond, such as trialkyl aluminum, and alkyl aluminum halides in which the alkyl groups contain from 1-20 and preferably 1-4 carbon atoms. The preparation of EPM and EPDM polymers is well known and is fully described in such patents as U.S. patents No. 2,933,480, No. 3,093,621, No. 3,211,709, No. 3,646,168, No. 3,790,519, No. 3,884,993, No. 3,894,999 and No. 4,059,654, amongst many others. Oxidized polyethylene wax materials suitable for use in the practice of this invention are described in U.S. Patent No. 3,060,163. According to this patent normally solid, hard, waxy polymers of ethylene having an average molecular weight between about 1,000 and 3,000 are subjected, in the liquid phase, to the action of an oxygen-containing gas to cause reaction of between 2-17 parts of oxygen per 100 parts of wax, i.e. to provide an oxidized polyethylene wax containing at least 1 percent and preferably 1-8 percent by weight of oxygen, and acid numbers of not more than about 50, and preferably between 10 and 45. In the preferred practice of this invention, the oxidized polyethylene is characterized by having a minimum number average molecular weight above 1000 and preferably at least about 1200, as determined by high temperature vapor pressure osmometry, containing between 1-5 percent by weight of total oxygen, and having an acid number of from 10 to about 35. The described oxidized polyethylene is obtained by oxidation of polyethylene in molten or finely divided solid form, with free oxygen containing gas, usually air, generally at elevated temperature, until the desired oxygen content is obtained. Starting materials for making the oxidized polyethylene suitable for use in the practice of this invention include low molecular weight, low density or linear low density polyethylene waxes having densities in the range of about 0.91 to about 0.96 as, for example, prepared by the process described in U.S. Patent No. 2,683,141, as well as high density, linear polyethylene as, for example, prepared in the presence of such well know catalysts as the "Phillips" or "Ziegler" type catalysts, having densities in the range of about 0.93-0.97 or above. The low molecular weight, low density polyethylene starting material can be oxidized by contacting in the molten state with a stream of air until the desired oxygen content has been obtained. The high density, linear polyethylene starting material is usually oxidized by contact, preferably in the finely divided solid state, with free oxygen-containing gas, usually air, at temperatures ranging from 100°C up to, but not including, the crystalline melting point of the polyethylene, until the desired oxygen content has been obtained. A preferred low molecular weight, low density oxidized polyethylene is marketed by Allied Chemical Corporation under the designation AC-629. This oxidized polyethylene product has a specific gravity of about 0.9±0.05, a number average molecular weight of about 1300, an oxygen content of between 3 and 5, and an acid number of about 14 to 17. Carboxylated polyethylenes which may be employed in the practice of this invention can be prepared by thermal degradation of a high molecular weight polyethylene in the presence of air or other oxygen-containing gas at an elevated temperature, so as to reduce the molecular weight and introduce carboxvlic acid groups at the points of chain scisson. Polyethylene having a molecular weight from about 100,000 to 1,000,000, and a specific gravity of 0.91 to about 0.965 may advantageously be used. For example, a polyethylene having a specific gravity of 0.94, a particle size of 150 µm (100 mesh) and an original viscosity average molecular weight of 2.6x10 6 was stirred constantly and heated to 126°C (260°F). An air stream heated to 110°C (230°F) was passed through the particles. After 13 hours the molecular weight was reduced to about 500,000 and to 60,000 after 16 hours. Ordinarily, carboxylic acid groups are introduced at each point of chain scisson, such that each molecule will have at least one carboxylic acid group, and preferably two such groups at low molecular weight. An alternative method for the preparation of a carboxylated polyolefin is by reaction with a polycarboxylic acid, such as maleic, at high temperature. One method of preparation of such materials is described in U.S. Patent No. 2,766,214. The following Examples illustrate the invention. The components which are formed into a composition for fabrication into various products, as by way of conventional molding procedure, are admixed for bulk reaction at a temperature above the melting point temperature of the thermoplastic resinous component, such as at a temperature above 163°C (325°F) up to a temperature of 315°C (600°F) and preferably up to about 260°C (500°F), as in hot melt processing equipment, such as a Banbury or extruder, for from 3-5 minutes. The procedure for applying the color coating to articles fabricated from the compositions of this invention was carried out as follows: 1. The surface of the fabricated product was first cleaned with an acidic or alkali wash. 2. A Durethane 400 602-1060 primer was applied in an amount to provide a dry film of 25µm±5µm (1.0±0.2 mils). 3. A second coating of primer was applied after a two minute flash of first coat under ultra-violet light (UV). 4. The second coating was baked under ultra violet for 15-20 minutes at 121°C (250°F). 5. A Durethane 700 HSE Topcoat was applied to provide a dry film of 46µm (1.8 mils). 6. A second Durethane Topcoat was applied after a 2 minute flash under UV. 7. The second topcoat was baked under UV for at least 20 minutes at 121°C (250°F). A conventional test for adhesion was employed for evaluation of the bond between the topcoat and the surface of the fabricated article. In the adhesion evaluation, referred to in the trade as the "Crosshatch" test, a razor blade is used to cut 11 vertical lines spaced 3mm (1/8 inch) apart, followed by cross cutting in the same spaced relation to provide 100 squares of 3mm (1/8 inch). A pressure sensitive cellophane tape is pressed onto the test area and then it is ripped off. The number of squares which remain bonded to the surface identifies the percent crosshatch. In other words, a value of 100% crosshatch indicates that all of the squares remain bonded to the surface. A 90% crosshatch indicates that 10% of the squares were removed with the tape. A value of 0% crosshatch indicates that all of the squares were removed with the tape and that none remained on the surface of the test piece. Example 1 A typical TPO compound, yielding 60,000 psi flexure modulus, and characterized by very poor paint adhesion, as exhibited by % crosshatch adhesion, had the following composition: EPDM interpolymer having an ethylene-propylene ratio of 80/20 and about 5 C=C double bonds per 1000 carbon atoms (EPsyn® 5508 of Copolymer Rubber & Chemical Corporation of Baton Rouge, Lousiana) 50% 12 melt flow polypropylene 50% Paint adhesion, % crosshatch 0 Tensile strength, MPa (psi) 18.96 (2750) Elongation, % 775 Flow Rate g/10 min (Condition "L") 2.0 Example 2 Use is made of the typical TPO compound (same as in example 1) but in which 10 parts by weight of the polypropylene has been replaced with 10 parts by weight of oxidized polyethylene: By Weight EPsyn® 5508 50% 12 melt flow polypropylene 40% Allied AC oxidized polyethylene 10% Paint adhesion, % crosshatch 100 Tensile strength, MPa (psi) 20.68 (3000) Elongation, % 1100 Flow Rate g/10 min. (condition "L") 2.8 It will be seen from the above, that not only is paint adhesion excellent, but that tensile strength, elongation and flow rate are also improved. Example 3 This example illustrates a typical TPO compound (same as in example 1) but in which 10 parts by weight of the polypropylene has been replaced with 10 parts by weight of the polyethylene which has not been oxidized: By Weight EPsyn® 5508 50% 12 melt flow polypropylene 40% Allied AC-617A non-oxidized polyethylene 10% Paint adhesion, % crosshatch 0 Tensile strength, MPa (psi) 15.17 (2200) Elongation, % 650 Flow rate g/10 min. (condition "L") 3.6 it will be noted that in the presence of non-oxidized polyethylene the adhesion is poor. Before the discovery of the instant invention this deficiency was overcome by the incorporation of an additional pretreatment step, prior to the application of the topcoat, involving the treatment of the object to be coated with an adhesion promoter. This step is now made unnecessary by the practice of the instant invention. Examples 4-8 The following examples illustrate the effect of the level of added oxidized polyethylene on the paint adhesion properties. Formulation (parts by weight) Examples 4 5 6 7 8 EPsyn® 5508 50 50 50 50 50 12 MF polypropylene 48 46 44 42 40 N550 Black .5 .5 .5 .5 .5 Oxidized polyethylene 2 4 6 8 10 Paint adhesion,% crosshatch 0 10 100 100 100 It can be seen from the above examples that crosshatch adhesion increases with increasing levels of oxidized polyethylene, reaching the maximum level of 100% adhesion at a level of 6 parts by weight per 100 parts by weight of rubber plus resin plus oxidized polyethylene. Examples 9-14 The following examples illustrate the effect of the rubber/resin ratio on the paint adhesion properties at a constant level of oxidized polyethylene. Formulation (parts by weight) Examples 9 10 11 12 13 14 EPsyn® 5508 0 10 20 30 40 50 12 MF polypropylene 90 80 70 60 50 50 N550 Black .5 .5 .5 .5 .5 .5 Oxidized polyethylene 10 10 10 10 10 10 Paint adhesion, % crosshatch 0 25 68 92 100 100 It can be seen from the above examples that crosshatch adhesion increases with increasing rubber level, reaching the maximum value of 100% at a level of 40 parts by weight of rubber per 100 parts by weight of rubber plus resin plus oxidized polyethylene. This implies that higher levels of oxidized polyethylene are needed to achieve maximum paint adhesion as the level of polypropylene in the blend is increased. This is further supported by Example 15 which demonstrates in comparison with Example 12 that increased oxidized polyethylene raises the crosshatch adhesion for a given level of polypropylene. Example 15 Formulation Parts by Weight EPsyn® 5508 25 12 MI Polypropylene 60 N550 Black 0.5 Oxidized Polyethylene 15 Paint adhesion, % crosshatch 100 Tensile strength, MPa (psi) 22.75 (3300) Elongation, % 100 Flow Rate (Condition "L"), g/10 min. 7.6 It will be apparent that color coating adhesion is increased when the TPO is formulated to contain 4-15 percent by weight oxidized polyethylene. Similar improvements in adhesion are realized when the oxidized polyethylene in the foregoing examples are replaced in whole or in part by oxidized or carboxylated polyethylenes such as isotactic, amorphous, hight density and low density polyethylenes and other alpha olefin polymers and copolymers. It is further assumed that the benefit derived from incorporation of the oxidized polyethylene will be realized whether the compositions are simple blends or contain partially or fully cured rubber as well as oils, fibers, fillers or other additives which are well-known to those skilled in the art.

Claims: A composition for use in molding articles having an improved surface bonding relationship with applied organic coatings, the composition comprising a substantially uniform mixture of at least 30 weight % of thermoplastic polypropylene resin, and at least 25 weight % of a polymer selected from (a) copolymers of ethylene and C 3 -C 16 mono-olefins and (b) terpolymers of ethylene, C 3 -C 12 mono-olefins and polyenes, and from 4 to 15 weight % of an oxidized or carboxylated polyolefin, the oxidized polyolefin containing at least 1 percent by weight oxygen and having an acid number of not more than 50, and the carboxylated polyolefin containing at least one carboxyl group per molecule. A composition according to claim 1, wherein the polymer is an EPM copolymer of ethylene and propylene. A composition according to claim 2, wherein the copolymer contains from 10 to 95 mole % ethylene units and from 5 to 90 mole % propylene units. A composition according to claim 3, wherein the copolymer contains from 45 to 85 mole % ethylene units and from 15 to 55 mole % propylene units. A composition according to claim 1, wherein the polymer is a terpolymer of ethylene, propylene and 5-ethylidene-2-norbornene. A composition according to any one of claims 1 to 5, wherein the polymer is a terpolymer containing the polyene in an amount of 0.1 to 10 mol percent. A composition according to any one of claims 1 to 6, wherein oxidized or carboxylated polyolefin is an oxidized polyethylene. A composition according to any one of claims 1 to 7, which contains at least 30 weight % of the polymer and at least 30 weight % of the thermoplastic polypropylene resin. A shaped article which has been fabricated from a composition according to any one of claims 1 to 8. A shaped article according to claim 9 having on at least one surface thereof an applied organic coating. A shaped article according to claim 10, wherein the coating is derived from a polyurethane paint.

Inventors: BENEFIELD ROBERT E, BOOZER CHARLES E, BENEFIELD, ROBERT E., BOOZER CHARLES E.
Applicants: DSM COPOLYMER INC, DSM COPOLYMER, INC.
Application year: 1990
Main classification: C08L23
IPC codes: C08L23, C08J7