Improved method of making lanthanum cerium terbium phosphate phosphor

Abstract: A method of making a lanthanum cerium terbium phosphate phosphor involves the single-step reaction of a single-phase, mixed valence state lanthanum cerium terbium oxide and boron phosphate. Alternatively, the single-step reaction may involve a mixture of lanthanum oxide, cerium oxide, terbium oxide and boron phosphate.

Description: This invention relates to a process for making a lanthanum cerium terbium phosphate phosphor for use in fluorescent lamps. U.S. Patent 4,423,349 to Nakajima et al discloses two methods of making this phosphor. In one method, carbonates of lanthanum, cerium and terbium are formed at 70°C, which are then reacted with phosphoric acid at 75°C to form a lanthanum cerium terbium phosphate. The phosphate is then fired at 1150°C for 75 minutes to form the phosphor. In another method, a coprecipitate of lanthanum cerium terbium oxalate is formed at 80°C and decomposed at 800°C to form a single-phase, mixed valence state lanthanum cerium terbium oxide. Diammonium phosphate is added to the oxide, and the mixture is then decomposed at 700°C to form a lanthanum cerium terbium phosphate. The phosphate is then crushed and fired at 1200°C for 4 hours to form the phosphor. Boron oxide or ammonium borate as a fluxing agent may be added before the firing step to promote the reaction and improve brightness. The prior art methods require either a multiple-step synthesis of rare earth compounds before the firing step, or a multiple-step firing. Such additional manufacturing steps are inefficient and costly. Furthermore, because of the volatility of the phosphate sources used, a great excess of the phosphate compound is required in the reaction between the rare earth compounds and the phosphate to form the phosphor. It is an object of the invention to provide a more efficient method of making lanthanum cerium terbium phosphate phosphor. In accordance with the invention there is provided a method of making lanthanum cerium terbium phosphate phosphor which is characterised by the steps set out in claim 1. For a better understanding of the present invention, together with other and further objects, advantages and capabilities thereof, reference is made to the following disclosure and appended claims. The method of the present invention is a single-step synthesis whereby rare earth compounds are reacted with boron phosphate (BPO₄). Optionally, an effective amount of a flux-forming compound, for example, lithium carbonate (Li₂CO₃), may be reacted with the rare earth compounds and boron phosphate. The rare earth raw materials may be a single-phase material of lanthanum cerium terbium oxide having the composition (La x Ce y Tb z )₂O₃ where x = 0.39 to 0.73 and preferably from 0.42 to 0.70; y = 0.17 to 0.45 and preferably from 0.18 to 0.44; and z = 0.10 to 0.16 and preferably from 0.12 to 0.14. A preferred lanthanum cerium terbium oxide has the composition (La 0.446 Ce 0.424 Tb 0.130 )₂O₃ and is commercially available from Rhone-Poulenc, Inc. or Shin-Etsu Chemical Co., Ltd. Alternatively, the individual oxides of lanthanum, cerium and terbium may be used. Boron phosphate, while commercially available, may not be of sufficient purity to obtain the results desired in this invention. It has been found that boron phosphate of a sufficiently high purity may be prepared by heating a 1:1 mixture of boric acid (H₃BO₃) and diammonium phosphate((NH₄)₂HPO₄) at 700°C to 1000°C for 2 hours. The reaction between boron phosphate and the rare earth oxide begins at 750°C to 800°C. However, the desired ionic equilibrium between cerium and terbium ion pairs does not occur until a temperature of about 1150°C to 1300°C is reached. Similarly, growth of phosphor crystals does not begin at the initial reaction temperature but instead occurs in the preferred temperature range of 1150°C to 1300°C. Boron phosphate, although formed from the reaction of two low melting-point oxides, is an extremely stable compound with a melting point in excess of 1600°C. When boron phosphate is used as the phosphate source in the present invention, near stoichiometric proportions of the rare earth compounds and boron phosphate can be used. Because of its high melting point, boron phosphate does not evaporate or decompose before the preferred phosphor reaction temperature is reached. Prior art phosphate sources such as diammonium phosphate decompose, melt or evaporate below 1150°C. Therefore, substantially excessive amounts of the phosphate source must be provided, and/or multiple firing steps must be employed to secure a sufficient amount of the phosphate for reaction with the rare earth compounds to form the phosphor. During the firing step as per this invention boron phosphate reacts with lanthanum cerium terbium oxide to form a lanthanum cerium terbium phosphate phosphor in a boron oxide (B₂O₃) solution. Boron oxide acts as a mild fluxing medium to promote the reaction by facilitating crystal growth. An advantage of using boron phosphate as the phosphate source in this reaction is its capacity as a reducing agent. Cerium and terbium are present in lanthanum cerium terbium oxide as +4 valence ions. These +4 ions are reduced to the +3 valence state in the presence of boron phosphate. Prior art methods for making this phosphor require a reducing atmosphere to effect this valence state reduction. The reaction as per this invention can occur in an inert atmosphere because of the reducing properties of boron phosphate. It is believed that the solubility of rare earth phosphate compounds in boron oxide is improved by the addition of a small amount of a flux-forming compound, such as lithium carbonate, to the solution. The combination of lithium oxide and boron oxide appears to have improved fluxing capabilities over the boron oxide alone. After firing, the phosphor is washed in basic and acidic solutions to remove any residual boron and lithium compound impurities. The following non-limiting examples are presented. EXAMPLE 1 The following raw materials were combined in a 10-qt plastic V-blender: 1660 grams of lanthanum cerium terbium oxide having the composition (La 0.446 Ce 0.424 Tb 0.130 )₂O₃; 1110 grams of boron phosphate, BPO₄; and 22.2 grams lithium carbonate, Li₂CO₃. The molar ratios of the components were thus 1 mole of rare earth oxide, 1.05 moles of boron phosphate and 0.03 mole of lithium carbonate (0.06 mole of lithium ions). The raw materials were V-blended for 15 minutes and then blended for 15 minutes with an intensifying bar to form a uniform mixture. The mixture was then fired at 1200°C for 4 hours in a 1% hydrogen/99% nitrogen atmosphere to form the phosphor. The reaction is indicated by the following equation: RE(III) x RE(IV) 1-x O 2-0.5x + (1+y)BPO₄ ----> RE * (III)PO₄ + [(1-x)/4]O₂ + [(1+y)/2]B₂O₃ + (y/2)P₂O₅↑ where RE(III) is La⁺³ or Tb⁺³ or Ce⁺³; RE(IV) is Ce⁺⁴ or Tb⁺⁴; RE*(III) is (lanthanum cerium terbium)⁺³; 0.47 ≦ x ≦ 1.0; and 0 < y ≦ 0.05. The fired cake was broken up and washed at about 90°C for about 4 hours in 2% dilute nitric acid, HNO₃. After filtration, the white body phosphor was washed and filtered three times with hot deionized water. The washed phosphor was then washed with 5% ammonium hydroxide, NH₄OH. After this base wash the phosphor was filtered and washed with hot deionized water. The filtered phosphor was dried at about 110°C for about 16 hours and then sifted through a 378 nylon mesh screen. EXAMPLE 2 The following raw materials were combined in a 10-qt plastic V-blender: 733.1 grams lanthanum oxide, La₂O₃; 243.0 grams terbium oxide, Tb₄O₇; 740.1 grams cerium oxide, CeO₂; 1110 grams boron phosphate, BPO₄; and 22.2 grams lithium carbonate, Li₂CO₃. The molar ratios of the components were thus 0.450 mole of lanthanum ions, 0.130 mole of terbium ions, 0.43 mole of cerium ions, 1.05 moles of boron phosphate and 0.03 mole of lithium carbonate (0.06 mole of lithium ions). The blending, firing and washing conditions were the same as those of Example 1. The reaction is indicated by the following equation: xRE(III)O 1.5 + (1-x)RE(IV)O₂ + (1+y)BPO₄ ----> RE*(III)PO₄ + [(1-x)/4]O₂ + [(1+y)/2]B₂O₃ + (y/2)P₂O₅↑ where RE(III) is La⁺³ or Tb⁺³ or Ce⁺³; RE(IV) is Ce⁺⁴ or Tb⁺⁴; RE * (III) is (lanthanum cerium terbium)⁺³; 0.47 ≦ x ≦ 1.0; and 0 < y ≦ 0.05. While there has been shown and described what are at present considered the preferred embodiments of the invention, it will be obvious to those skilled in the art that various changes and modification may be made therein without departing from the scope of the invention as defined by the appended claims.

Claims: A method of making lanthanum cerium terbium phosphate phosphor, characterised in that it comprises the steps of: a) reacting single-phase , mixed valence state lanthanum cerium terbium oxide having the composition (La x Ce y Tb z )₂O₃, where x = 0.39 to 0.73; y = 0.17 to 0.45; and z = 0.10 to 0.16, with boron phosphate in a single step firing at a temperature of from 1150°C to 1300°C for from 1.5 to 4 hours to form a mixture comprising lanthanum cerium terbium phosphate phosphor and boron oxide, said lanthanum cerium terbium oxide and said boron phosphate being provided in a molar ratio of from 1:1 to 1:1.05; and b) separating said lanthanum cerium terbium phosphate phosphor from said boron oxide. A method, being a modification of the method of claim 1, characterised in that there is used in said reacting step, in place of said single-phase, mixed valence state lanthanum cerium terbium oxide, lanthanum oxide, cerium oxide and terbium oxide. A method according to claim 1 or 2, characterised in that said lanthanum cerium terbium phosphate phosphor is formed according to the reaction: RE(III) x RE(IV) 1-x O 2-0.5x + (1+y)BPO₄ ----> RE*(III)PO₄ + [(1-x)/4]O₂ + [(1+y)/2)B₂O₃ + (y/2)P₂O₅↑ where RE(III) is La⁺³ or Tb⁺³ or Ce⁺³; RE(IV) is Ce⁺⁴ or Tb⁺⁴; RE*(III) is (lanthanum cerium terbium)⁺³; 0.47 ≦ x ≦ 1.0; and 0 < y ≦ 0.05. A method according to any one of claims 1-3, characterised in that said lanthanum cerium terbium oxide, or said oxides of lanthanum, cerium and terbium, and said boron phosphate are provided in stoichiometric proportions. A method according to any one of claims 1-5, characterised in that a flux-forming compound is reacted with said lanthanum cerium terbium oxide and said boron phosphate. A method according to claim 5, characterised in that said flux-forming compound is lithium carbonate. A method according to claim 6, characterised in that said lithium carbonate is provided in an amount of up to 0.06 mole of lithium ions per mole of lanthanum cerium terbium phosphate phosphor. A method according to any one of claims 1-7, characterised in that said single-step firing occurs at 1200° for 4 hours. A method according to any one of claims 1-8, characterised in that said single-step firing occurs in an inert atmosphere. A method according to any one of claims 1-8, characterised in that firing occurs in a reducing atmosphere. A method according to any one of claims 1-10, characterised in that said separation step is performed by washing. A method according to claim 11, characterised in that said washing step is performed in acidic and basic solutions. A method as claimed in Claim 12, characterised in that said acidic solution is dilute nitric acid. A method as claimed in claim 12 or 13, characterised in that said basic solution is dilute ammonium hydroxide.

Inventors: CHAU CHUN-NIN, CHENOT CHARLES F, GRAY LESLIE F, KASENGA ANTHONY F, CHAU, CHUN-NIN, CHENOT, CHARLES F., GRAY, LESLIE F., KASENGA, ANTHONY F.
Applicants: GTE PROD CORP, GTE PRODUCTS CORPORATION
Application year: 1990
Main classification: C09K11
IPC codes: C09K11, C01B25