Resin-coated steel sheet for drawn-and-ironed cans and drawn-and-ironed cans manufactured therefrom

Abstract: Resin-coated steel sheets which have excellent workability in drawing and ironing even at a normal temperature without preheating, and which give, by drawing and ironing, DI cans having resin coating satisfactory in adhesion, corrosion resistance, and external appearance. The sheets comprise a steel sheet tin-coated on one side and chromate-treated on the other side, the chromate-­ treated side being further coated with a resin composition composed of a thermoplastic polyester resin prepared by a thermal fusion reaction of 95 to 5 % by weight of a crystalline polyester and 5 to 95 % by weight of non-­ crystalline polyester and having an alloying ratio, of 5 to 50 %. The sheets may be tin-coated on both sides, one of which is further coated with the above resin composition or a non-crystalline resin and further the above resin composition, or the above resin composition and further a crystalline polyester resin.

Description: The present invention relates to a resin-coated steel sheet for drawn and ironed cans, and a drawn and ironed can manufactured therefrom. JP-A-60-168643 discloses a resin coated steel sheet for drawn and ironed cans (hereinafter referred to as "DI cans") which is excellent in workability in drawing and ironing and which enables a high degree of ironing (an ironing ratio of 60 % or higher) with a resin film being kept coated on the inside face of the can, and which gives, by drawing and ironing, the DI cans satisfactory in resin film adhesion, corrosion resistance, and external appearance. The resin-coated steel sheet disclosed in the above Laid-open Patent Application comprises (1) a coating layer of a thermoplastic resin such as a polyethylene terephthalate resin, being capable of orienting and having barrier property against corrosive components, the layer being provided on one side of the steel sheet which side forms an inside face of the DI cans; (2) an inorganic oxide film layer such as of chromium hydrate oxide provided under the coating layer as an adhering undercoating; and (3) a metal coating layer of ductile metal such as tin provided on the other side of the steel sheet which forms the outside face of the DI cans. In order to manufacture a DI can which has a resin coating satisfactory in adhesion, corrosion resistance, and external appearance, as described in the above JP-A-60-168643, the coating resin of the resin-coated steel sheet for DI cans is required to be brought to a suitable drawing temperature in the drawing and ironing step, (the suitable temperature being lower than the crystallization temperature of the resin, and within the range of the glass-transition temperature (T g ) ±30°C, e.g., 40 to 100°C for a PET resin). Since the resin-coated steel sheets, which are produced by a known extrusion-lamination method and subjected to the drawing and ironing, are usually stored at a normal temperature, a preheating process for the resin-coated steel sheets is required disadvantageously to be added to the conventional can-manufacturing process. The present invention intends to provide a resin-coated steel sheet which has excellent workability in drawing and ironing even at a normal temperature without preheating, and is capable of being ironed in a high degree of ironing (an ironing ratio of 60 % or more) while the resin being kept coated on the inside face, and which gives, by drawing and ironing, DI cans having resin coating satisfactory in adhesion, corrosion resistance, and external appearance. The present invention also intends to provide a DI can having the aforementioned characteristics. According to one aspect of the present invention, there is provided a resin-coated steel sheet for DI cans according to claim 1. According to another aspect of the present invention, there is provided a resin-coated steel sheet for DI cans according to claim 2. According to still another aspect of the present invention, there is provided a resin-coated steel sheet for DI cans according to claim 3. According to a further aspect of the present invention there is provided a resin-coated steel sheet for DI cans according to claim 4. According to a still further aspect of the present invention there is provided a resin-coated steel sheet for DI cans according to claim 5. According to a still further aspect of the present invention, there is provided a drawn and ironed can, obtainable by drawing and ironing the aforementioned resin-coated steel sheet for DI cans with the resin-coated side forming the inside of the can. The values of T m1 , T m2 , T m3 , T g1 , T g2 , and T g3 are respectively the melting point or the glass-transition temperature, in °C, measured by a differential thermal analyzer (Perkin Elmer, Model 7) at a programmed temperature elevation of 10°C/min. Regarding the definition of "crystalline state" and "non-crystalline state", the polyester exhibiting a peak of the melting point is defined as being crystalline, and the polyester exhibiting only the peak of the glass-transition temperature or exhibiting neither a peak of the glass-transition temperature nor a peak of the melting point is defined as being non-crystalline. The above-mentioned crystallizable polyester includes polyethylene terephthalate (hereinafter referred to as PET), polybutylene terephthalate (hereinafter referred to as PBT), polyethylene naphthalate (hereinafter referred to as PEN), and copolymers thereof, but is not limited thereto. Thermoplastic polyesters having a melting point of 200°C or higher are included in the crystallizable polyester. The above-mentioned non-crystallizable polyester includes polyethylene isophthalate (hereinafter referred to as PEI), polyethylene terephthalate copolyester comprising 30 mole % of cyclohexane-dimethanol, polyethylene terephthalate comprising 20 mole % or more of isophthalic acid, polyarylate and polyester-polycarbonate, but is not limited thereto. Non-crystallizable thermoplastic polyesters having a glass-transition temperature of 20°C or higher, preferably 40°C or higher are included thereto. The present invention will be described in detail. The first and the second aspects of the present invention are explained below. Cans were manufactured by coating a variety of thermoplastic resins on a chromate-treated surface of a known surface-treated steel sheet having a tin coated surface on one side for the outside wall of the can and the chromate-treated surface on the other side for the inside wall of the can, or on one side of a known surface-treated steel sheet having tin coating on the both sides prepared according to a known method, and subsequently drawing and ironing the steel sheets thus resin-coated, with the resin-coated surface forming the inside of the can. Firstly, a known PET was selected as the thermoplastic resin. Further, a known resin in an amorphous state was employed. As the results, the resin-coated steel sheet prepared by a known method could be drawn and ironed only in a low degree, but could not be worked to an ironing ratio of 60 % or higher, the object of the present invention. The reason was presumed to be that the usual non-crystalline PET singly used crystallizes partially during drawing and ironing, resulting in non-workability in the subsequent processing. Accordingly, the same working was conducted similarly by using PEI as the non-crystallizable polyester resin. This PEI, which was non-crystallizable as expected, exhibited superior characteristics in drawing step. However, in the subsequent ironing, the resin adheres to the working punch, (in ironing, usually a metal sheet being pressed into three dices to conduct ironing between the punch and the dice), causing exfoliation of the resin from the inside wall of the can and prevention of the removal (or strip-out) of the punch from the can body. Further, similar drawing-and-ironing working (hereinafter referred to as DI working) was conducted with a simple mixture of PET and PEI, or of PET, PEI, and PBT with the unsatisfactory results. That is, the resin containing a predominant proportion of a crystalline resin is unsatisfactory in workability, while the resin containing a predominant proportion of a non-crystalline resin was unsatisfactory in strip-out property. None of the binary or ternary mixtures of these components satisfied simultaneously the workability and strip-out property. Then it was considered that a simple composition of PET, or PEI as well as simple mixtures thereof show the properties of the respective single components even though some degree of transesterification may occur on fusion of the resins. Therefore, copolymer resins of terephthalate and isophthalate were prepared, and tested in the same manner, leading to unsatisfactory results. However, in a very limited resin composition range, the copolymer resins of terephthalate with isophthalate exhibited the characteristics near the target, so that the results were analyzed in detail. Consequently, it was concluded that the control of the crystallinity only of the resin, as known before, gives neither the desired adhesiveness to the metal nor the desired workability for severe DI working, but the control of the melting point together with the crystallinity is indispensable. In other words, it was found that the resin composition which crystallizes only minimally in DI working in a non-crystalline state and has a melting point within a suitable temperature range can satisfy the object of the present invention. It was also found that the resin compositions having such characteristics can be prepared by heat fusion of 95 - 5 % by weight of PET, namely a crystallizable polyester, and 5 - 95 % by weight of PEI, namely a non-crystallizable polyester in such a state that at least one of the crystallizable polyester and the non-crystallizable polyester is catalytically active, and controlling the alloying ratio to come within a predetermined range. The optimum range of the alloy ratio depends on the nature of the surface to be coated with the resin composition: the ratio being from 5 to 50 % for a chromate-treated surface, and from 20 to 80 % for a tin-coated surface. The state of being "catalytically active" means that the starting polyester comes to have a higher molecular weight (or a higher limiting viscosity) when heated. The use of such starting material having the catalytic activity will shorten the time for alloying. The reasons for numerical limitation in the first and the second aspects of the present invention are discussed below. In alloying the crystallizable polyester with the non-crystallizable polyester, the mixing ratio, [(non-crystallizable polyester/whole polyester resin) x 100], is limited to be within a range of from 5 % to 95 %. The mixing ratio is limited to be not less than 5 % because, at the ratio of less than 5 %, the crystallizable resin exerts great influence on the crystallization of the resin under the severe ironing condition by stretching, making the resin non-workable. On the other hand, the mixing ratio is limited to be not more than 95 % because, at the ratio of more than 95 %, the apparent melting point is 235°C or lower to cause adhesion of the resin by fusion to the punch, impairing the strip-out property. Of the thermoplastic polyester resin for coating a chromate-treated surface, the alloying ratio is limited to be from 5 to 50 % because, at the alloying ratio of less than 5 %, the crystalline portion increased by the heat generated in the ironing and other steps, making the resin incapable of following the high rate of ironing, and at the alloying ratio of more than 50 %, the apparent melting point of the coating resin becomes lower, impairing greatly the strip-out property. Of the thermoplastic polyester resin for coating a tin-coated surface, the alloying ratio is limited to be from 20 to 80 % because, at the alloying ratio of less than 20 %, the crystalline portion increased by the heat generated in the ironing and other steps, making the resin incapable of following the high rate of ironing, and at the alloying ratio of more than 80 %, the apparent melting point of the coating resin becomes lower, impairing greatly the strip-out property. The reason why the lower limit of the optimum alloying ratio of the resin is lower for a chromate-treated surface than for a tin-coated surface is assumed to be that the resins adhere more tightly to the tin-coated surface. The reason why the upper limit of the optimum alloying ratio of the resin is higher for a tin-coated surface than for a chromate-treated surface is assumed to be that the working heat generated at ironing on the outside face of the can is absorbed as the heat of fusion of the tin coating layer on the inside face of the can, reducing the temperature rise of the resin of the tin coating layer and, on the contrary, the temperature rise is not reduced on the chromate-treated surface. Next, the third, the fourth, and the fifth aspects of the invention are explained below. As described before, cans were manufactured by coating one side of a known steel sheet having tin coating on both sides with a variety of thermoplastic resins by a known method and drawing and ironing the thus coated steel sheet so that the resin-coated side forms the inside of the can. Consequently, it was confirmed that the workability and the strip-out property depend on the coating thermoplastic resin: the workability being low with PET; the strip-out property being inferior with PEI; PET and PEI not giving a steel sheet satisfying both of the workability and the strip-out property; the mixture of PET and PEI, or PET, PEI and PBI giving inferior workability at a higher content of the crystalline resin, and giving inferior strip-out property at a higher content of the non-crystalline resin; and arbitrary mixture of these two or three components giving no steel sheet satisfying both workability and strip-out property. Accordingly, it was considered to laminate the non-crystallizable polyester resin layer having high workability (or high adhesiveness) onto a tin coating layer of the steel sheet and to laminate further thereon a crystallizable polyester resin layer having a satisfactory strip-out property. Therefore, drawing and ironing workability was investigated by using various non-crystallizable polyester resins and crystallizable polyester resins. However, in every combination, layer separation occurred between the lower non-crystallizable polyester resin layer and the upper crystallizable polyester resin layer. Since the phenomenon was assumed to come from the large difference of the properties between the lower resin layer and the upper resin layer, the resin compositions of the upper layer and the lower layer were improved to prevent the layer separation between the upper and the lower resin layers and to secure the workability and the strip-out property of the resin. More specifically; (1) in the case where a non-crystalline polyester resin giving satisfactory workability (or adhesiveness) is employed for the lower layer, a special resin which crystallizes appropriately by resin-stretching at the working is employed for the upper layer resin to decrease the difference of the properties between the upper and the lower resin layers, thereby preventing separation between the upper and the lower resin layers and securing the strip-out property at the working; (2) in the case where a crystalline resin giving satisfactory strip-out property is employed for the upper layer, a special resin which minimally crystallizes by resin-stretching at the working is employed for the lower layer resin to decrease the difference of the properties between the upper and the lower resin layers, thereby preventing separation between the upper and the lower resin layers and securing the workability of the resin; and further (3) the special resin of the above item (1) which crystallizes appropriately by resin-stretching at the working is employed for the upper layer resin, and the special resin of the above item (2) which minimally crystallizes by resin stretching at the working is employed for the lower layer resin, thereby decreasing the difference of the properties between the upper and the lower resin layers, and preventing separation between the upper and the lower resin layers to secure the workability of the resin and the strip-out property at the working. The special resin for the upper layer resin which crystallizes appropriately is a thermoplastic resin of an incomplete reaction product of a crystallizable polyester resin with a non-crystallizable polyester resin, and has an alloying ratio of 50 % or less (excluding 0 %) defined by the calculation formula mentioned in the claims. The special resin for the lower layer resin which crystallizes minimally is a thermoplastic resin of an incomplete reaction product of a crystallizable polyester resin with a non-crystallizable polyester resin, and has an alloying ratio of not less than 50 % and less than 100 % defined by the calculation formula mentioned in the claims. Incidentally, the thermoplastic polyester resin of alloying ratio of 100 % is a non-crystalline polyester resin, and the thermoplastic polyester resin of alloying ratio of 0 % is a crystalline resin. The reasons for numerical limitation in the third, fourth, and fifth aspects of the present invention are discussed below. The alloying ratio of the thermoplastic polyester resin for the lower layer in contact with the tin coating layer of the steel sheet is limited to be not less than 50 % and less than 100 % because, at the alloying ratio of less than 50 %, the adhesiveness of the resin to the tin coating layer is insufficient and the crystalline portion in the coating resin increases in ironing, especially at ironing rate of 65 % or higher, resulting in loss of adhesiveness to the coating layer and of workability of the resin; and at the alloying ratio of 100 %, the thermoplastic polyester resin is non-crystalline which cannot prevent the separation of the upper and the lower resin layers. The alloying ratio of the thermoplastic polyester resin for the upper layer to be brought into contact with the punch at ironing is limited to be less than 50 % (excluding 0 %), because, at the alloying ratio of 50 % or higher, a non-crystalline portion predominates in the coating resin, lowering the apparent melting temperature to impair the strip-out property, while a thermoplastic polyester resin of alloying ratio of 0 % is crystalline which cannot prevent the separation between the upper and the lower resin layers. In the thermal fusion reaction of a crystallizable polyester resin with a non-crystallizable polyester resin for alloying, the mixing ratio, [(weight of non-crystallizable polyester resin/weight of whole polyester resin) x 100], is preferably in the range of from 50 % to 90 % for producing a thermoplastic polyester resin of an alloying ratio of not less than 50 % and less than 100 % for the lower layer; and is preferably in the range of from 10 % to 50 % for producing a thermoplastic polyester resin of an alloying ratio of less than 50 % (excluding 0 %), in view of the production efficiency. The coating thicknesses (or lamination thickness) of the upper and the lower resin layers, and the tin coating thickness of the steel sheet are not limited at all, and the thicknesses may be selected suitably depending on the working conditions. According to the results of the practice of the inventors of the present invention, in the cases where the tin coating thickness is 2.8 g/m² or more and the overall ironing ratio is 60 % or more, the thickness of the upper layer need to be not less than 3 µm before the working. If the thickness is less than 3 µm, in that case, a portion of the upper layer resin is fusion-bonded to the punch by the heat generated at DI working, thus impairing the strip-out property. The present invention is described specifically referring to Examples. (Examples for the First Aspect) A steel sheet (0.30 mm thick, hardness: equivalent to T-1) was employed which had been tin-coated in an amount of 2.8 g tin/m² on the side of the sheet for an outside face of a can, and had been chromate-treated in an amount of 55 mg metallic chromium/m² and 18 mg chromium oxid/m² on the side for an inside face of a can. The chromate-treated side of the steel sheet was coated with the resin composition shown in Table 1 in a thickness of 50 µm by means of a T-die. In the coating practice, the resin fusion temperature was in the range of from 265°C to 300°C, and the temperature of the steel sheet during the coating was in the range of from 150°C to 200°C. The steel sheet having been coated with the resin by the T-die was cooled quickly to 100°C or lower within 10 seconds after the coating. The quick cooling was conducted for the purpose of preventing crystallization of the resin at a high temperature. The resin-coated steel sheet thus produced was drawn and ironed into a can with the resin-coated side forming the inside of the can. The nondefectiveness of the inside face (the resin coated side) of the can thus manufactured was evaluated by putting aqueous 1.0 % sodium chloride into the can, applying a voltage of +6 volts employing the can body as an anode and platinum placed at the center position of the can as the cathode, and measuring the electric current. (The test is hereinafter referred to as a QTV test.) The nondefectiveness of the inside face of the can was further evaluated by putting into the can a solution containing 20 g of sulfuric acid per liter and 50 g of copper sulfate (CuSO₄·7H₂O) per liter, leaving it standing for 10 minutes, removing the solution from the can, washing the can with the water, and observing the deposition of copper. (The solution is a chemical copper-plating solution. A defect of the resin layer will induce dissolution of iron from the defect if any, and causing substitution-plating of copper. The test is hereinafter referred to as a copper sulfate test.) The results are shown in Table 2 together with the evaluation results of the strip-out property and the observation results of the inside face of the can after the DI working. (Working Conditions) 1. Resin temperature just before DI working: Normal temperature 2. Blank diameter: 137 mm in diameter 3. Drawing conditions: First drawing ratio H/D = 33/86 mm in diameter Second drawing ratio H/D = 50/65 mm in diameter 4. Diameter of ironing punch: Three-step ironing: 65.5 mm in diameter 5. Overall ironing ratio: 70.5 % (Examples for the Second Aspect of the Invention) A steel sheet (0.30 mm thick, hardness: equivalent to T-1) was employed which had been tin-coated on both sides, having tin coating of 2.8 g/m² on one side. The one side of the tin-coated steel sheet was coated with the resin compositions shown in Table 3 in a thickness of 50 µm by means of a T-die. In the coating practice, the resin fusion temperature was in the range of from 265°C to 300°C, and the temperature of the steel sheet during the coating was in the range of from 150°C to 200°C. The steel sheet coated with the resin by the T-die was cooled quickly to 100°C or lower within 10 seconds after the coating. The quick cooling was conducted for the purpose of preventing crystallization of the resin at a high temperature. The resin-coated steel sheet thus produced was drawn and ironed into a can with the resin-coated side forming the inside of the can. The nondefectiveness of the inside face (the resin coated side) of the can thus manufactured was evaluated by putting aqueous 1.0 % sodium chloride into the can, applying a voltage of +6 volts employing the can body as an anode and platinum placed at the center position of the can as the cathode, and measuring the electric current. (The test is hereinafter referred to as a QTV test.) The nondefectiveness of the inside face of the can was further evaluated by putting into the can a solution containing 20 g of sulfuric acid per liter and 50 g of copper sulfate (CuSO₄·7H₂O) per liter, leaving it standing for 10 minutes, removing the solution from the can, washing the can with the water, and observing the deposition of copper. (The solution is a chemical copper-plating solution. A defect of the resin layer will induce dissolution of iron from the defect if any, and causing substitution-plating of copper. The test is hereinafter referred to as a copper sulfate test.) The results are shown in Table 4 together with the evaluation results of the strip-out property and the observation results of the inside face of the can after the DI working. (Working Conditions) 1. Resin temperature just before DI working: Normal temperature 2. Blank diameter: 137 mm in diameter 3. Drawing conditions: First drawing ratio H/D = 33/86 mm in diameter Second drawing ratio H/D = 50/65 mm in diameter 4. Diameter of ironing punch: Three-step ironing: 65.5 mm in diameter 5. Overall ironing ratio: 70.5 % (Examples for the Third to Fifth Aspects of the Invention) A steel sheet (0.30 mm thick, hardness: equivalent to T-1) was employed which had been tin-coated on both sides, having tin coating of 2.8 g/m² on one side. The one side of the tin-coated steel sheet was coated with the thermoplastic polyester resins shown in Table 5 by means of a two-layer extrusion T-die in a thickness of the lower layer of 20 µm and a thickness of the upper layer of 20 µm (40 µm in total). The resin fusion temperature was in the range of from 265°C to 300°C, and the temperature of the steel sheet during the coating was in the range of from 150°C to 200°C. The steel sheet having been coated with the resin by the T-die was cooled quickly to 100°C or lower within 10 seconds after the coating. The quick cooling was conducted for the purpose of preventing crystallization of the resin at a high temperature. The resin-coated steel sheet thus produced was drawn and ironed into a DI can with the resin-coated side forming the inside of the can. The nondefectiveness of the inside face (the resin coated side) of the can thus manufactured was evaluated by putting aqueous 1.0 % sodium chloride into the can, applying a voltage of +6 volts employing the can body as an anode and platinum placed at the center position of the can as the cathode, and measuring the electric current. (The test is hereinafter referred to as a QTV test.) The nondefectiveness of the inside face of the can was further evaluated by putting into the can a solution containing 20 g of sulfuric acid per liter and 50 g of copper sulfate (CuSO₄·7H₂O) per liter, leaving it standing for 10 minutes, removing the solution from the can, washing the can with the water, and observing the deposition of copper. (The solution is a chemical copper-plating solution. A defect of the resin layer will induce dissolution of iron from the defect if any, and causing substitution-plating of copper. The test is hereinafter referred to as a copper sulfate test.) The results are shown in Table 6 together with the evaluation results of the strip-out property and the observation results of the inside face of the can after the DI working. (Working Conditions) 1. Resin temperature just before DI working: Normal temperature 2. Blank diameter: 137 mm in diameter 3. Drawing conditions: First drawing ratio H/D = 33/86 mm in diameter Second drawing ratio H/D = 50/65 mm in diameter 4. Diameter of ironing punch: Three-step ironing: 65.5 mm in diameter 5. Overall ironing ratio: 70.5 % As described above, the resin-coated steel sheet for DI cans produced by employing the thermoplastic polyester resin composition of the present invention gives DI cans having excellent inside face properties even when drawn and ironed at a normal temperature. Accordingly, the preheating process in can manufacturers may be omitted which process has conventionally been indispensable for DI cans employing conventional thermoplastic resins, which allows reduction of cost in can manufacturing.

Claims: A resin-coated steel sheet for DI cans, obtainable by a method comprising: providing a composition containing 95 to 5 % by weight of a crystallizable polyester resin and 5 to 95 % by weight of a non-crystallizable polyester resin; reacting said resins, by means of thermal fusion, to produce a thermoplastic polyester resin having an alloying ratio, as represented by the formula below, of 5 to 50 % by weight: where T m1 and T g1 are respectively a melting point and a glass-transition temperature, in °C, of the crystallizable polyester employed as the starting material, T m2 and T g2 are respectively a melting point and a glass-transition temperature, in °C, of a random copolymer of the polyester resin having the same monomer composition, T m3 and T g3 are respectively a melting point and a glass-transition temperature, in °C, of the thermoplastic polyester resin; coating the thermoplastic polyester resin thus obtained onto a chromate-treated side of a steel sheet, which is tin-coated on the other side, wherein said thermoplastic polyester resin as applied on the steel sheet is in non-crystalline condition and is to be converted by DI working into a resin layer sufficiently crystalline to assure a satisfactory stripping-out property; and cooling the coated resin quickly to prevent crystallization of the resin at a high temperature. A resin-coated steel sheet for DI cans, obtainable by a method comprising: providing a composition containing 95 to 5 % by weight of a crystallizable polyester resin and 5 to 95 % by weight of a non-crystallizable polyester resin; reacting said resins, by means of thermal fusion, to produce a thermoplastic polyester resin having an alloying ratio, as represented by the formula below, of 20 to 80 % by weight: where T m1 and T g1 are respectively a melting point and a glass-transition temperature, in °C, of the crystallizable polyester employed as the starting material, T m2 and T g2 are respectively a melting point and a glass-transition temperature, in °C, of a random copolymer of the polyester resin having the same monomer composition, T m3 and T g3 are respectively a melting point and a glass-transition temperature, in °C, of the thermoplastic polyester resin; coating the thermoplastic polyester resin thus obtained into one side of a steel sheet which is tin-coated on both sides, wherein said thermoplastic polyester resin as applied on the steel sheet is in non-crystalline condition and is to be converted by DI working into a resin layer sufficiently crystalline to assure a satisfactory stripping-out property; and cooling the coated resin quickly to prevent crystallization of the resin at a high temperature. A resin-coated steel sheet for DI cans, obtainable by a method comprising: providing a composition containing a crystallizable polyester resin and a non-crystallizable polyester resin; reacting said resins, by means of thermal fusion, to produce a thermoplastic polyester resin having an alloying ratio, as represented by the formula below, of greater than 0 % and less than 50% by weight: where T m1 and T g1 are respectively a melting point and a glass-transition temperature, in °C, of the crystallizable polyester employed as the starting material, T m2 and T g2 are respectively a melting point and a glass-transition temperature, in °C, of a random copolymer of the polyester resin having the same monomer composition, T m3 and T g3 are respectively a melting point and a glass-transition temperature, in °C, of the thermoplastic polyester resin; providing a steel sheet which is tin-coated on both sides and wherein one side is further coated with a non-crystallizable polyester resin layer; coating the thermoplastic polyester resin obtained above onto the non-crystallizable polyester resin layer, wherein said thermoplastic polyester resin as applied on said layer is in non-crystalline condition and is to be converted by DI working into a resin layer sufficiently crystalline to assure a satisfactory stripping-out property; and cooling the coated resin quickly to prevent crystallization of the resin at a high temperature. A resin-coated steel sheet for DI cans, obtainable by a method comprising: providing a composition containing a crystallizable polyester resin and a non-crystallizable polyester resin; reacting said resins, by means of thermal fusion, to produce a thermoplastic polyester resin having an alloying ratio, as represented by the formula below, of not less than 50 % and less than 100 % by weight: where T m1 and T g2 are respectively a melting point and a glass-transition temperature, in °C, of the crystallizable polyester employed as the starting material, T m2 and T g2 are respectively a melting point and a glass-transition temperature, in °C, of a random copolymer of the polyester resin having the same monomer composition, T m3 and T g3 are respectively a melting point and a glass-transition temperature, in °C, of the thermoplastic polyester resin; coating the thermoplastic polyester resin thus obtained onto one side of a steel sheet which is tin-coated on both sides, and further coating the coated thermoplastic polyester resin with a crystallizable polyester resin, wherein said thermoplastic polyester resin and said crystallizable polyester resin as applied on the steel sheet are in non-crystalline condition and only the applied crystallizable polyester resin is to be converted by DI working into a resin layer sufficiently crystalline to assure a satisfactory stripping-out property; and cooling the coated resins quickly to prevent crystallization of the resins at a high temperature. A resin-coated steel sheet for DI cans, obtainable by a method comprising: providing a composition containing a crystallizable polyester resin and a non-crystallizable polyester resin; reacting said resins, by means of thermal fusion, to produce a first thermoplastic polyester resin having an alloying ratio, as represented by the formula below, of not less than 50% and less than 100% by weight, and a second thermoplastic polyester resin having an alloying ratio of greater than 0% and less than 50 % by weight: where T m1 and T g1 are respectively a melting point and a glass-transition temperature, in °C, of the crystallizable polyester employed as the starting material, T m2 and T g2 are respectively a melting point and a glass-transition temperature, in °C, of a random copolymer of the polyester resin having the same monomer composition, T m3 and T g3 are respectively a melting point and a glass-transition temperature, in °C, of the thermoplastic polyester resin; coating the first thermoplastic polyester resin obtained above onto one side of a steel sheet which is tin-coated on both sides, and further coating the coated first thermoplastic polyester resin with the second thermoplastic polyester resin obtained above wherein said first and second thermoplastic polyester resins as applied on the steel sheet are in non-crystalline condition, and said first thermoplastic polyester resin retains a degree of crystallinity low enough to assure satisfactory adhesion to the tin-coated steel sheet, even after DI working, while said second thermoplastic polyester resin is to be converted by DI working into a resin layer sufficiently crystalline to assure a satisfactory stripping-out property; and cooling the coated resins quickly to prevent crystallization of the resins at a high temperature. A drawn and ironed can, obtainable by drawing and ironing the resin-coated steel sheet of claims 1 to 5 with the resin-coated side forming the inside of the can.

Inventors: HIRAOKA TAKASHI, NIIMI HIROJI, WAKE RYOUSUKE C O NIPPON STEEL, YOSHIHARA RYOICHI C O NIPPON S, HIRAOKA, TAKASHI, NIIMI, HIROJI, WAKE, RYOUSUKE, C/O NIPPON STEEL CORPORATION, YOSHIHARA, RYOICHI, C/O NIPPON STEEL CORPORATION
Applicants: MITSUI PETROCHEMICAL IND, NIPPON STEEL CORP, MITSUI PETROCHEMICAL INDUSTRIES, LTD., NIPPON STEEL CORPORATION
Application year: 1990
Main classification: C09D167
IPC codes: B05D7, B65D25, C09D167