Semiconductor heterostructures

Abstract: This disclosure pertains to compound semiconductor, such as AlGaAs, surface skimming hetero-transverse junction (HTJ) lasers and improved heterojunction bipolar transistors (L-HBTs). These lasers and transistors are structurally consistent with each other, so they can be fabricated in the same set of epitaxial layers for integrated optoelectronic applications. The surface skimming characteristic of the HTJ lasers provided by this invention enables them to be configured relatively easily, without requiring any epitaxial regrowth, to operate as DFB lasers in axial or surface emitting configurations and to function as harmonic generators. Single and multiple base channel L-HBT transistors, as well as structurally corresponding single and multiple quantum well surface skimming HJT lasers are disclosed.

Description: This invention relates to surface-skimming, buried heterostructure III-V and II-VI compound semiconductor lasers and, more particularly, to buried heterostructure compound semiconductor devices which can be configured to operate either as surface-skimming heterotransverse junction (HTJ) lasers or as lateral heterojunction bipolar transistors (L-HBT′s). As a matter of definition, the waveguided mode or modes of a "surface-skimming" laser have substantial optical intensity at the outermost surface of the semiconductor structure, so the semiconductor/air interface is an integral part of the optical waveguide. Furthermore, while much of the following discussion is directed toward the well-known AlGaAs III-V compound semiconductor devices, it is to be understood that "compound semiconductor" devices more generally refers to semiconductor devices composed of III-V or II-VI compounds. A copending and commonly assigned United States patent application of R. L. Thornton, which was filed June 17, 1988 under Serial No. 07/208,950, now US-A-4987468, on "Lateral Heterojunction Bipolar Transistor (LHBT) and Suitability Thereof as Hetero Transverse Junction (HTJ) Laser," describes the use of impurity-induced disordering (IID) for forming the p-n junctions of planar buried heterostructure compound semiconductor devices, including "dual function HTJ laser/L-HBT transistor devices" (i.e., devices which can be biased for operation either as HTJ lasers or as L-HBT transistors). Buried heterostructure devices of that general type are preferred because their internal structures are planar and are fabricated entirely by diffusion, without any intermediate etching steps or any other interruptions requiring epitaxial regrowth. Possibly-relevant articles are: R.L. Thornton et al. , "Unified Planar Process for Fabricating Heterojunction Bipolar Transistors and Buried Heterostructure Lasers Utilizing Impurity Induced Disordering" Applied Physics Letters , Vol. 53, No. 26, December 26, 1988, pp. 2669-2671; and R. L. Thornton et al. , "Demonstration and Properties of a Planar Heterojunction Bipolar Transistor with Lateral Current Flow," IEEE Transcations on Electron Devics , Vol. 36, No. 10, October 1989, pp. 2156-2164 Heretofore the accepted practice has been to bury the active region of a HTJ laser sufficiently far below the outer surface of the semiconductor to ensure that the evanescent optical field of the laser decays to a negligibly low intensity level before it reaches the outer surface of the semiconductor. For example, the active regions of AlGaAs HTJ lasers characteristically have been buried at depths in excess of about 1µm for effectively isolating their evanescent optical fields from their usual GaAs capping layers and from the metallizations that are normally provided for making external electrical connections to them. This practice has been followed, even though it was recognized that the performance of the structurally corresponding L-HBT transistor was affected adversely by burying its active base channel so deeply. More particularly, it was known that the width of the base channel of such a transistor could be significantly reduced and more precisely controlled, while maintaining a given photolithographic feature size, by forming the active base channel closer to the outer surface of the multilayer heterostructure. Furthermore, conventional HBT technology provided convincing evidence that L-HBT transistors having narrower base channels would have higher current gain and improved high-frequency performance. Nevertheless, until now, the depth to which the active base region of a dual-function HTJ laser/L-HBT device has been buried has been governed by the assumption that the evanescent optical field intensity of the waveguided modes of the laser configuration of such a device should be negligible at the surface of the device. In accordance with the present invention, as defined in the appended claims, it has been found that HTJ lasers can operate satisfactorily with waveguided modes of substantial optical intensity at the outer surface of the multilayer heterostructures in which they are fabricated, thereby permitting such lasers and L-HBT transistors having base channels of reduced length to be fabricated in the same set of epitaxial layers. The surface-skimming characteristic of the HTJ lasers provided by this invention enables them to be configured relatively easily, without requiring any epitaxial regrowth, to operate as distributed feedback (DFB) lasers in axial-or surface-emitting configurations and to function as harmonic generators. Single and multiple base channel L-HBT transistors, as well as structurally corresponding single and multiple quantum well surface-skimming HTJ lasers, can be constructed in accordance with this invention. The present invention will now be described by way of example with reference to the attached drawings, in which: Fig. 1 is a sectioned isometric view of an AlGaAs surface-skimming HTJ laser/L-HBTdevice of an embodiment of the present invention; Fig. 2 schematically illustrates some of the recommended steps for fabricating a HTJ laser/L-HBT device of the type shown in Fig. 1; Fig. 3 graphically illustrates the manner in which the calculated electric field (i. e. "E-field") profile of the waveguided modes of a laser configuration of a device of the type shown in Fig. 1 varies as a function of the percentage of aluminum in the alloy composition of its lower cladding layer; Fig. 4 is a sectioned isometric view of a surface-skimming, distributed-feedback (DFB), AlGaAs HTJ laser in accordance with an embodiment of the present invention; Fig. 5 is a sectioned isometric view of a surface-emitting configuration of a DFB, surface-skimming HTJ laser in accordance with an embodiment of this invention; Fig. 6 is a sectioned isometric view of an optical harmonic generator embodying a surface-skimming AlGaAs HTJ laser in accordance with an embodiment this invention; Fig. 7 is a graphical representation of the multilayer epitaxial heterostructure of the single base channel L-HBT transistor/single quantum well surface-skimming HTJ laser of the embodiments shown in various forms in Figs. 1 and 4-6; Fig. 8 graphically represents the multilayer epitaxial heterostructure of a multiple base channel L-HBT transistor/multiple quantum well surface-skimming HTJ laser of an embodiment of the present invention; Fig. 9 is a characteristic output power vs. input current curve for a multiple quantum well surface-skimming HTJ laser fabricated in accordance with this invention in the epitaxial layers depicted in Fig. 8, and Fig. 10 shows the characteristic current vs. voltage curves for a multiple channel L-HBT transistor fabricated in the epitaxial layers depicted in Fig. 8. Turning to the drawings, and at this point especially to Fig. 1, there is shown an AlGaAs embodiment of a buried heterostructure compound semiconductor device 21 which can be biased to operate either as a surface-skimming HTJ laser or as a L-HBT transistor. As will be seen, the HTJ laser and the L-HBT configurations of the device 21 are structurally consistent because they are fabricated in the same set of epitaxial layers 23-26 and have similar geometries. Moreover, they can be fabricated using similar processing steps, so they are well suited for optoelectronic integration. More particularly, the multilayer heterostructure of the surface-skimming HTJ laser/L-HBT transistor device 21 typically is grown on a p-type or semi-insulating substrate 28, suitably by employing a metallo-organic chemical vapor deposition (MOCVD) process for sequentially growing a 0.2 µm or so thick GaAs buffer layer (not shown), a 1.0 µm thick layer 23 of Al m Ga 1-m A s (where m = the percentage of aluminum in the alloy), a 0.15 µm thick layer 24 of Al n Ga 1-n As (where n = the percentage of aluminum in the alloy), a 0.015 µm thick layer 25 of GaAs (the active layer), and another 0.15 µm thick layer 26 of Al n Ga 1-n As. All epitaxial layers, except the GaAs active layer 25 in some situations, are doped with p-type impurities, such as magnesium; suitably to concentrations of approximately 1 x 10¹⁸ Mg atoms/cm³ in the Al m Ga₁₋ m A s layer 23; 2 x 10¹⁸ Mg atoms/cm³ in the lower Al n Ga 1-n As layer 24, and 5x10¹⁸ Mg atoms/cm³ in the upper Al n Ga 1-n As layer 26. There are several options for achieving a p-type conductivity in the GaAs active layer 25, including some cases in which p-type impurities need not be directly introduced into that layer as it is being grown. For example, the active layer 25 may tend to acquire a p-type conductivity, without being directly doped, either as a result of the outdiffusion of p-type impurities into it from the adjacent doped layers 24 and 26 during any subsequent high temperature processing of the device 22, or as a result of the migration of holes into it from those adjacent layers 24 and 26. The GaAs buffer layer is not shown because it merely functions as an oxygen-getter layer for the MOCVD process, to enhance the quality of the other epitaxial layers 23-26. The quality of the epitaxial layers 23-26 of the multilayer heterostructure is significant because they are functional components of the HTJ laser configuration of the device 21. Furthermore, the layers 24-26 also are integral components of its L-HBT configuration. Specifically, the Al m Ga 1-m As layer 23 is the cladding for the lower waveguide layer 24 of the laser, and the layer 24 also is the lower burying layer for the transistor. The GaAs layer 25, in turn, functions as the active region of the laser and as the active base channel of the transistor device. Next comes the layer 26 which functions as the upper waveguide for the laser and as the upper burying layer for the transistor. As discussed in some additional detail hereinbelow, it is especially notable that the ambient atmosphere (typically air) is the cladding for the upper waveguide 26 of the laser configuration of the device 21 because this feature causes the waveguided modes of the laser to be asymmetrically distributed and, therefore, materially influenced by the selection of the alloy composition of the Al m Ga 1-m A s cladding layer 23 for the lower waveguide 24. Referring to Fig. 2, the lateral heterojunctions of the surface-skimming HTJ laser/L-HBT device 21 advantageously are formed by diffusions from the upper surface of its multilayer heterostructure. To that end, as shown, impurity-induced disordering (IID) via silicon (Si) diffusion is utilized to convert laterally-separated sections of the buried GaAs active layer 25 into n-type AlGaAs regions 31 and 32, thereby forming the collector and the emitter, respectively, of the L-HBT device and the quantum well of the HTJ laser. Such a IID process typically is carried out by first depositing a film of Si₃N₄ on the upper surface of the multilayer heterostructure, such as by chemical vapor deposition (CVD), and by then patterning the Si₃N₄ film to serve as a mask 41 for the diffusion of Si. Next, a bilayer film, which is composed of a thin layer of Si 42 capped by a thin layer of Si₃N₄ 44, is deposited, again suitably by CVD, to provide a source for the Si diffusion. Then, the diffusion is performed at 850°C for about 1 hour to reach a depth of approximately 0.4 µm. In the regions where the Si diffusion front reaches the buried GaAs layer 25, the rate of interdiffusion of the GaAs layer 25 into the adjacent AlGaAs layers 24 and 26 is substantially increased thereby forming a lateral n-p-n structure which has substantially higher alloy compositions (and, therefore, wider bandgaps) in its collector and emitter regions 31 and 32 than in its active base region or channel 45. Following the formation of the lateral n-p-n heterostructure of the surface-skimming HTJ laser/L-HBT device 21, hydrogen nuclei or the like are ion implanted into its epitaxial layers 23-26, as at 46-49 (Fig. 1). Implants 46 and 47 resistively desensitize the p-n junctions between the active base layer 25 and the outer sidewalls of the collector and emitter regions 31 and 32, respectively, by creating irregularities in the crystal structure in the vicinity of those junctions, thereby increasing their resistance sufficiently to inhibit the flow of current through them. To accomplish that, the implants 46 and 47 laterally overlap the outer margins of the collector and emitter regions 31 and 32, respectively, and penetrate into the lower epitaxial layer 23 to roughly the same depth as the collector and emitter regions 31 and 32. The implants 48 and 49, on the other hand, are located at the opposite lateral extremities of the device 21 and fully penetrate through all of its epitaxial layers 23 and 26 (and, if desired, even into its substrate 28) for electrically isolating the device 21 from any other devices (not shown) the substrate 28 supports, including any other devices which are fabricated using the same set of epitaxial layers 23-26. As shown, the implants 47 and 49 laterally overlap, but there is a lateral gap between the implants 46 and 48 so that an upper surface base contact 51 can be seated between them. A patterned metallization, such as a Cr-Au metallization, typically is deposited on the upper surface of the device 21 to provide coplanar contacts 51-53 for making electrical connections to its base, collector and emitter 45, 31 and 32, respectively. In embodiments having a p-type substrate 28, the base 45 could be contacted from the substrate side of the device 21, but the upper surface base contact 51 is preferred because it simplifies the fabrication of the device 21, As illustrated, the device 21 has an asymmetric geometry because its base contact 51 is laterally offset from its n-p-n heterostructure. However, if a symmetric device geometry is desired, the base contact 51 may be relocated to a position mid-way between the collector contact 52 and the emitter contact 53. But, such a modification would inhibit the laser mode of operation of the device 21, unless the base contact 51 is composed of a material which is substantially non-absorbing to the wavelength of the fundamental emission of the laser. As will be appreciated, the device 21 operates as a transistor when its collector/base junction is reverse biased and its emitter/base junction is forward biased. In that connection it should be noted that the relatively shallow depth at which the active base layer 25 of the device 21 is buried (e. g., in the embodiment illustrated in Fig. 1, it is buried at a depth of only 0.15 µm below the upper surface of the device 21) significantly reduces the width of the base channel 45 which can be reliably and repeatedly provided for the device 21 when, as here, its base channel width 45 is dependent upon a diffusion from its upper surface under the control of a mask which is defined by a photolithographic process of given minimum feature size. Moreover, the tapering of the Si diffusions which define the collector and emitter regions 31 and 32 of the device 21 is less pronounced near the upper surface of the device, so its lateral n-p-n heterostructure has relatively abrupt p-n junctions. Thus, the present invention can be employed for providing L-HBT devices having increased current gain and improved high frequency performance. The device 21 operates as a single quantum well HTJ laser whenever its collector/base and emitter/base junctions are both forwardly biased sufficiently to cause the carrier density in its active base region 45 to build to a level at which stimulated emission is initiated. The lasing action occurs in the plane of the lateral n-p-n heterostructure of the device 21 along an axis which is normal to that structure (i. e., the lateral heterostructure defines the quantum well of the HTJ laser). As will be understood, the waveguide for the laser mode of operation of the device 21 is asymmetric because the interface between its upper waveguiding layer 26 and the ambient air is an integral part of the waveguide. Therefore, as shown in Fig. 3, the waveguided modes of the laser are asymmetrically distributed. However, in devices 21 employing more or less standard alloy compositions of Al°₄Ga°₆As for the lower and upper waveguides 24 and 26, respectively, it has been found that this asymmetry is tolerable if the percentage of aluminum in the alloy composition of the Al m Ga 1-m A s cladding layer 23 for the lower waveguide is increased to a level above about 48%. If the percentage of aluminum in the lower cladding layer 23 is reduced significantly below that threshold level, the structure will become non-guiding. But, as shown in Fig. 3 and as indicated by the following table, the performance of the waveguide progressively improves as the percentage of aluminum in its lower cladding layer 23 is increased above the aforementioned threshold level: Γ is the percentage of the optical power that is within the active region 45 and, therefore, is a key factor for calculating the threshold current required for lasing action in a given laser structure. Accordingly, from a waveguiding point of view, the preferred alloy composition for the lower cladding layer 23 of the device 21 contains as much aluminum as possible consistent with maintaining its structural stability (this typically is a composition of approximately Al°₈₅Ga°₁₅As). In some situations, however, it may be desirable to reduce the percentage of aluminum in the lower cladding layer 23 somewhat in order to reduce the far field divergence of the laser emission. If desired, the device 21 may be cleaved transversely with respect to its lateral n-p-n heterostructure to form a classical Fabry-Perot length cavity with reflective end mirrors or facets for providing the coherent positive optical feedback that is needed for its laser mode of operation. In that event, at least one of the end mirrors of the cleaved laser configuration of the device 21 may be partially transmissive for axially extracting output radiation from one or both ends of the laser. Alternatively, as shown in Fig. 4, a n th order diffraction grating 54 (i.e., a grating having a period of nλ/2, where n is an integer) may be formed on the outer surface of the upper layer 26 of the device 21 in vertically superimposed longitudinal alignment with its active region 45 for operating the device 21 as a distributed feedback (DFB) laser. As illustrated, the grating 54 extends from end-to-end of the active region 45 of the device 21, thereby enabling it to interact with the optical field at the surface of the device 21 along substantially the full length of its active region 45 to operate as a distributed Bragg reflector for providing coherent positive optical feedback for the DFB laser configuration of the device 21. The grating 54 typically is formed by etching the outer surface of the upper layer 26 of the device 21, but that does not interfere in any way with the important goal of avoiding the need for epitaxial regrowth. Since the optical feedback for the DFB laser configuration of the device 21 is provided by the grating 54, the laser cavity need not be terminated by reflective end mirrors, so one or both ends of the cavity may be transmissive to provide an axial output for the laser radiation. As will be appreciated, certain orders of the diffraction grating 54 may couple a fraction of the fundamental frequency power of the DFB laser configuration of the device 21 out of the upper surface of the device 21 at predetermined angles. The order of the grating 54 relative to the fundamental frequency at which the device 21 lases determines the fraction of the fundamental power which is "surface emitted", and the angles at which these diffracted beams are emitted. One of the more interesting applications of this "surface-emitting" DFB laser configuration of the device 21 is illustrated in Fig. 5 where the grating 54 is a second-order grating for emitting, as at 55, the fundamental lasing frequency at a near-normal angle with respect the active region 45 of the device 21. The normal or near normal surface emission from the device 21 is highly desirable for applications in which design considerations dictate against the use of an end face emitting laser configuration for extracting optical power from the device 21. As a result of the high optical field intensity in the laser cavity of the device 21, the non-linearity of the semiconductor materials within its waveguiding structure 23- 26 causes measurable amounts of second harmonic optical generation. See, for example, Ogasawara et al., "Second Harmonic Generation in an AlGaAs Double-Heterostructure Laser", Japanese Journal of Applied Physics , Vol. 26, No. 8, August 1987, pp. 1386-1387. This second harmonic light is of significant interest because it falls within the visible region of the emission spectrum- e.g., at a blue wavelength of 435 nm, if the wavelength of the fundamental laser emission is 870 nm. Unfortunately, this second harmonic energy is strongly absorbed by the materials in which it is generated, so it typically is absorbed after traveling only several ten nanometer (hundred Ångström). Turning again to Fig. 5, it will be seen that the grating 54 of the DFB surface-emitting laser configuration of the device 21 also is an improved means for extracting the internally generated second harmonic light. The grating 54 diffracts out the second harmonic light at angles determined by the wavelength of that harmonic. Since the extraction occurs along the entire length of the laser cavity, the full length of laser contributes to the second harmonic emission, rather than only the last several tens of nm of the cavity near one of its ends. Referring to Fig. 6, even further improvements in the extraction of the second harmonic light from the laser cavity of the device 21 may be realized by exposing materials having strong non-linear properties and/or superior optical transmission characteristics at the harmonic frequency to the optical field at the outer surface of its upper epitaxial layer 26. For example, to employ the Fabry-Perot cavity laser configuration of the device 21 as a driver for an enhanced optical harmonic generator 61, a film 62 composed of a suitable non-linear material, such as KDP, LiNbO₂ or Langmuir-Blodgett layers, may be deposited on the outer surface of the upper epitaxial layer 26 of the device 21 in vertically superimposed longitudinal alignment with its active region 45, thereby exposing the full length of the film 62 to the surface-skimming portion of the optical field produced by the laser. Even more generally, it will be evident that the surface-skimming laser which this invention provides lends itself to almost any application in which it is desired to expose external means, such as generating means or sensing means, to the electric field of the waveguided modes of the laser. Fig. 7 diagrammatically illustrates the multilayer heterostructure of the above-described single channel L-HBT/single quantum well surface-skimming HTJ laser 21 as a function of the percentage of aluminum in each of its epitaxial layers 23-26. Fig. 8 is a similar diagram for an extension of the present invention into the realm of multiple channel L-HBT′s/multiple quantum well HTJ lasers. More particularly, Fig. 8 illustrates the multilayer epitaxial heterostructure of a device 71 having four active layers 72-75 which are buried at depths ranging from about 0.21 µm to about 0.28 µm below its outer surface. The upper and lower 40% aluminum burying layers 76 and 77 of the device 71 are separated from its upper and lower active layers 72 and 75 by intermediate layers 78 and 79, respectively, which are composed of an Al 0.2 Ga 0.8 As alloy. Likewise, the same Al 0.2 Ga 0.8 As alloy is used for the barrier layers 81-83 between the active regions 72-75. As before, the 40% aluminum upper burying layer 76 suppresses surface recombination effects, so the 40% aluminum lower burying layer 77 is employed to provide a reasonably well balanced waveguide for the HTJ laser configurations of the device 71. Now, however, the burying layers 76 and 77 are separated from the active layers 72-75 by the intermediate 20% aluminum layers 78 and 79 to prevent deep level defects, such as the DX center, from degrading the device performance. Fig. 9 is an input current vs. output power curve for a typical surface-skimming multiple quantum well HTJ laser fabricated in the epitaxial layers depicted in Fig. 8, while Fig. 10 illustrates the collector current vs collector-emitter voltage curves for a L-HBT transistor device fabricated in the same set of epitaxial layers. As will be seen, it was found that the HTJ laser operated with a forward current threshold of about 5.9 mA for the onset of lasing and had a slope efficiency of approximately 0.5 mW/mA. The L-HBT transistor, on the other hand, was found to have current gains in excess of 200 for collector currents in the range of the threshold current of the laser. Accordlingly, it will be evident that the laser and transistor configurations of the particular set of epitaxial layers shown in Fig. 8 are very well matched for integrated optoelectronic applications.

Claims: A multilayer compound semiconductor heterostructure device for the fabrication of lateral heterojunction bipolar transistor together with hetero-transverse junction lasers, the device including at least one active layer (25) disposed between an outer waveguide layer (26) and an inner waveguide layer (24), and means for injecting current laterally into the active layer, the outer waveguide layer forming an external surface of the device and having a thickness adapted to cause lasing within the active layer to produce an optical field of substantial intensity at the external surface. The device as claimed in claim 1, wherein the depth of the outer waveguide layer from its external surface to the active layer in less than about 0.4 µm. A hetero-transverse junction compound semiconductor laser, comprising: an outer waveguide layer (26) having an outer surface interface with the ambient atmosphere; an inner waveguide layer (24); at least one active layer (25) disposed between the outer and inner waveguide layers, and a cladding layer (23) adjacent to the inner waveguide layer. The laser as claimed in claim 3, wherein the depth of the outer waveguide layer (26) is sufficiently shallow to cause waveguided modes of the laser to have significant optical intensity at the outer surface, and wherein a periodic n th order diffraction grating (54) is located on the outer surface, the diffraction grating overlying an active region of the laser and extending lengthwise thereof for providing distributed optical feedback for the laser. The laser of Claim 4, further including means for extracting optical power from the laser via the diffraction grating. The laser of Claim 4 or 5, wherein the diffraction grating is a second-order grating for diffracting fundamental frequency optical power out of the laser at a near-normal angle with respect to the active layer. The laser of Claim 4 or 5, wherein the diffraction grating is adapted to diffract second harmonic optical power out of the laser at a predetermined angle along essentially the full length of the active region. The laser of Claim 3, further including a film (62) of strongly non-linear material deposited on the said outer surface in overlying axial alignment with an active region of the laser, the laser having a predetermined fundamental lasing frequency for causing the film to emit light at a second harmonic of the frequency. A hetero transverse junction compound semiconductor laser comprising an upper waveguiding layer (26) having an outer surface which participates in guiding waveguided modes of said laser, a lower waveguiding layers (24), and at least one active layer (25) disposed between said upper waveguiding layer and said lower waveguiding layer; said outer surface of said waveguide being perturbed (54) to exert a predetermined influence on said waveguided modes of said laser. In combination with a hetero-transverse junction compound semiconductor laser comprising an upper waveguiding (26) layer having an outer surface which participates in guiding waveguided modes of said laser, a lower waveguiding layer (24) and at least one active layer (25) disposed between said upper waveguiding layer and said lower waveguiding layer; means (62) adjacent said outer surface of said upper waveguiding layer of said laser for optically interacting with said waveguided modes of said laser. The hetero-transverse junction compound semiconductor devices of any of Claims 1-10 wherein said compound semiconductor is composed of GaAs and AlGaAs alloys.

Inventors: THORNTON ROBERT L, THORNTON, ROBERT L.
Applicants: XEROX CORP, XEROX CORPORATION
Application year: 1990
Main classification: H01S3
IPC codes: H01S3, H01S5, H01L29, H01L21