Method and apparatus for removing non-metallic inclusions from molten metal

Abstract: A method of removing non-metallic inclusions from a molten metal comprises the step of simultaneously applying both a horizontal rotation of the molten metal and heating of the molten metal by induction heating. After the simultaneous application of rotational force and heat, the induction heating may be stopped while the horizontal flow of the molten metal is maintained, so as to promote the separation of the particles of the inclusions. The method is carried out by using an apparatus which has a vessel (2) which contains the molten metal (1), a rotary magnetic field generating device (3) surrounding the vessel (2), and an induction heating device (4) also surrounding the vessel. Each of the rotary magnetic field generating device and the induction heating device may be divided into a plurality of circumferential segments and arranged such that the segments of both devices are alternately disposed around the vessel.

Description: The present invention relates to a method of and an apparatus for removing non-metallic inclusions and intermetallic compounds from a molten metal. It is known that non-metallic inclusions and intermetallic compounds (generally referred to as "inclusions", hereinafter) in a molten metal cause defects in the final product produced from the metal. Various studies have been therefore made to develop techniques which enable an efficient removal of such inclusions. For instance, Japanese Patent Laid-Open Publication Nos. 55-107743 and 58-22317 disclose methods in which horizontal rotational flow is imparted to a molten steel so that non-metallic inclusions are concentrated to the central region due to centrifugation. Japanese Patent Laid-Open Publication No. 63-219536 discloses a method in which drifting dross in a molten zinc bath is maintained at a predetermined temperature which provides a required level of fluidity of the bath during centrifugal separation. These known methods rely solely upon mechanical separation such as centrifugation and cannot effectively separate fine particles, although they can efficiently separate comparatively large particles of non-metallic inclusions and impurities. A method disclosed in Japanese Patent Laid-Open Publication No. 61-103654, relies solely upon heating of molten metal, but cannot produce appreciable effect in excluding large particles of non-metallic inclusions, in particular mixing of slag which is generated in unsteady state of a melt-forming process, although this method is effective in preventing generation of non-metallic inclusions and removal of the small-sized non-metallic inclusions. Accordingly, the present invention seeks to provided an apparatus for efficiently separating, from a molten metal, non-metallic inclusions and intermetallic compounds of various particle sizes. To this end, according to one aspect of the present invention, there is provided an apparatus for removing non-metallic inclusions from a molten metal contained in a vessel, comprising: rotary magnetic field generating devices and induction heating devices which are disposed in alternate circumferential regions around said vessel. According to another aspect of the present invention, there is provided an apparatus for removing non-metallic inclusions from a molten metal contained in a vessel, comprising: a rotary magnetic field generating device and induction heating device disposed around said vessel at different levels. The above and other objects, features and advantages of the present invention will become clear from the following description of the preferred embodiments when the same is read in conjunction with the accompanying drawings. Figs. 1 and 2 are schematic illustrations of an embodiment of the apparatus for separating and removing non-metallic inclusions in accordance with the present invention; Figs. 3(a) and 3(b) are a plan view and a side elevational view of an arrangement in which a rotary magnetic field generating device and an induction heating device are alternately disposed; Fig. 4 is a characteristic chart showing an index of rate of generation of defects in the product in Example 1; Fig. 5 is a graph showing the relationship between mixing energy and deoxidation rate constant; and Fig. 6 is a graph showing the relationship between total oxygen amount and time. Referring to Fig. 1, according to the present invention, a horizontal rotation is imparted to a molten metal 1 contained in a vessel 2 of an apparatus for removing non-metallic inclusions, by means such as a rotary magnetic field generating device 3, so that comparatively large particles such as of non-metallic inclusions and intermetallic compounds having smaller values of specific gravity than the molten metal are concentrated in the central region, whereas large particles having greater values of specific gravity are separated to the peripheral region of the rotational flow. Subsequently, the temperature of the molten metal is raised by a heater 4 so that the solubility of intermetallic compounds is enhanced thereby to dissolve even those small particles which had been precipitated at the lower temperature. In most cases, the rate of separation of small non-metallic inclusions and intermetallic compounds is ruled by the rate of coarsening of the particles due to aggregation and coagulation. The greater the agitating power, the higher the coarsening rate. When a horizontal rotational magnetic field and high-frequency heating are simultaneously effected in the same vessel, horizontal rotation and vertical agitation take place simultaneously so as to provide an extremely large agitating power, thus remarkably promoting the separation. In particular, when slag floats on the upper surface of the molten metal, it is impossible to promote the contact between the molten metal and the slag by the horizontal rotation alone, so that the efficiency of absorption of non-metallic inclusions by the slag is extremely low. According to the present invention, since horizontal rotation and induction heating are effected simultaneously, the molten metal is sufficiently mixed with the slag which tends to float on the metal, whereby a high refining performance can be obtained. In order to give a theoretical support to this remarkable feature of the invention, the inventors conducted a fluid dynamical analysis to compute mixing energy ε ˙ which also is referred to as energy density dissipation rate. It has been found that mixing energy is a factor which significantly affects the separation and floating of inclusions. It is therefore a key for obtaining a higher rate of separation of inclusions, to increase the value of the mixing energy. When neither the rotation nor heating is applied, the mixing energy ε ˙ is calculated to be 0.001 W/kg (m²/s³) as a mean and, when rotational flow of 80 rpm is imparted, the mixing energy ε ˙ is calculated to be 0.3 W/kg (m²/s³). In contrast, when both the rotational flow of 60 rpm and and the induction heating with 800 KVA power are applied simultaneously, the mixing energy ε ˙ is as large as 20 W/kg (m²/s³). It is thus possible to attain an agitating power by the simultaneous use of rotation and induction heating which compares favorably with that of bottom-blow converter. From the results of the computations shown above, as well as from Fig. 5 which shows the relationship between mixing energy and deoxidation rate constant k, it is understood that the method of the present invention provides a very large deoxidation effect. In Fig. 5, the hatched area shows the range of fluctuation of the respective values. According to the present invention, it is possible to stop the induction heating while maintaining horizontal flow, after the simultaneous application of the horizontal flow and the induction heating. In such a case, the particle size progressively becomes greater due to coarsening caused by aggregation of the particles of inclusions, thus enabling an efficient removal of the inclusions. The method of the present invention can be used also for various refining processes such as dephosphorization and desulfurization. In the method of the present invention, agitation which can input a high energy, and heating are effected simultaneously. It is therefore possible to add the required alloy components with a high yield. Fig. 1 shows an apparatus which can simultaneously impart horizontal rotation and induction heating. This apparatus has a rotary magnetic field generating device 3 and an induction heating device 4 arranged to surround a vessel 2. An arrangement may be such that the induction heating device 4 is placed above the rotary magnetic field generating device 3 as shown in Fig. 2. It is also possible to arrange the rotary magnetic field generating device 3 above the induction heating device 4. In order to attain a high agitation effect, it is preferred that both the rotary magnetic field generating device 3 and the induction heating device 4 be divided into segments and arranged such that the segments of the rotary magnetic field generating device 3 and the segments of the induction heating device 4 be alternately disposed around the vessel 2, as shown in Fig. 3(a). Numeral 5 denotes a dross discharge pipe, 6 denotes a valve and 7 denotes a nozzle. Example 1 An example of the method of the invention, applied to separation of Fe-Aℓ intermetallic compound from a Zn plating bath, will be described hereinunder. Molten zinc was continuously collected from a pot of a continuous hot-dip plating system for continuously plating a steel sheet. The extracted zinc was made to pass through the apparatus shown in Fig. 3 for separation and removal of impurities, and the cleaned molten zinc was discharged from a nozzle provided on the bottom of the vessel. The cleaned molten zinc was returned to the pot and used for the continuous hot-dip plating. An examination was conducted to investigate the rate of generation of the plating defect. The capacity of the zinc pot was about 50 ton. The apparatus shown in Fig. 3 was operated at a process speed of 2 ton/min. The speed of horizontal rotation of the molten zinc was 70 to 80 rpm, while the heating was performed by a high-frequency heating means at a rate of 40 KVA. The apparatus was operated cyclically such that the operation was stopped after each 10-minute operation for allowing the separated dross to be discharged outside through the dross discharge pipe. Fig. 4 shows the rate of generation of plating defects caused by presence of dross as observed when the zinc was treated in accordance with the process of the present invention, in comparison with the plating defect generating rate as observed when the process of the invention was not used. It will be seen that the rate of generation of plating defects is much smaller in the case where the molten zinc is treated by the process of the invention than in the case where the invention was not used. This clearly shows that the rate of removal of dross is remarkably improved by the process of the present invention because the rate of generation of plating defect is significantly reduced. ( Example 2 ) 5 tons of aluminum killed steel was charged into the vessel of an apparatus of the type shown in Fig. 2 having upper induction heating device and lower rotary magnetic field generating device. A rotary magnetic field (central magnetic flux 350 Gauss) and heat by induction heating (300 KVA) were simultaneously applied to the steel for 5 hours. Then, the induction heating was stopped while the horizontal rotation was continued for an additional 3 minutes to allow for separation of coarsened inclusions. For the purpose of comparison, tests were also conducted in which 10-minute magnetic agitation and 10-minute induction heating were applied separately. The steels that were subjected to these tests were examined for changes in the total oxygen content. The results of the examination are shown in Fig. 6. It will be seen that the total oxygen amount can be reduced to 3 ppm, or lower, by the method of the present invention. Thus, the present invention makes it possible to conduct melt-forming process with a high degree of purity. As will be understood from the foregoing description, according to the present invention, it is possible to efficiently separate and remove non-metallic inclusions and intermetallic compounds of various particle sizes from the molten metal. Furthermore, rate of generation of defects in steel sheets caused by presence of non-metallic inclusions, as well a rate of generation of plating defects due to presence of intermetallic compounds, i.e., dross, in the plating bath. can be reduced remarkably, thus ensuring high quality of the resulting product.

Claims: An apparatus for removing non-metallic inclusions from a molten metal (1) contained in a vessel (2), comprising: rotary magnetic field generating devices (3) and induction heating devices (4) which are disposed in alternate circumferential regions around said vessel (2). An apparatus for removing non-metallic inclusions from a molten metal (1) contained in a vessel (2), comprising: a rotary magnetic field generating device (3) and induction heating device (4) disposed around said vessel (2) at different levels.

Inventors: KITAOKA HIDENARI C O TECHNICAL, MIKI YUJI C O TECHNICAL RESEAR, SAKURAYA TOSHIKAZU C O TECHNIC, SORIMACHI KENICHI C O TECHNICA, TAKEUCHI SHUJI C O TECHNICAL R, KITAOKA, HIDENARI, C/O TECHNICAL RESEARCH DIVISION, MIKI, YUJI, C/O TECHNICAL RESEARCH DIVISION, SAKURAYA,TOSHIKAZU C/O TECHNICAL RESEARCH DIVISION, SORIMACHI, KENICHI C/O TECHNICAL RESEARCH DIVISION, TAKEUCHI, SHUJI, C/O TECHNICAL RESEARCH DIVISION
Applicants: KAWASAKI STEEL CO, KAWASAKI STEEL CORPORATION
Application year: 1990
Main classification: C22B9
IPC codes: B22D43, C22B9, B22D11, B22D41