Process and composition used to reclaim paint from spray booth with a flood sheet system

Abstract: Disclosed is a recovery process which allows the recovery and reuse of oversprayed uncured paint resin. The process comprises the use of a water containing organic solvent solution as a circulating hydrophilic liquid in a flood sheet system.

Description: Great quantities of paints, lacquers, varnishes and clear coat finishes are used in the automobile, appliance, and allied industries to coat finished products. It is well-known that in these industrial paint operations where paint is either applied by a spray-gun apparatus or a Behr Bells system, a portion of the paint is not transferred onto the item being painted. Instead, the paint is left in the air that is present in the paint booth. Currently, industrial paint booths have a series of filtering media to trap the air-borne paint particles before the air from within the paint booth is transferred to the outside environment. The first stage of this filtering process involves the passing of the paint-saturated air through a "curtain" or flood sheet of water. The physical barrier of the water traps the larger paint particles. Since most paint resin systems are hydrophobic, the paint does not become solvated by the water, but will sit on the surface until it comes in contact with a side wall to attach itself to. This creates a major "sticky" clean-up problem. To avoid this problem, a system of chemicals are added to the water "curtain" fluid to "neutralize" the paint to prevent it from sticking to any side wall. This neutralizing process, referred to in the industry as the "detackification" process, chemically alters the paint resin systems so that the paint from this point on cannot be used as a coating. Moreover, the intractable nature of the detackified paint precludes easy recovery of valuable paint compounds such as pigments, solid fillers, and higher boiling point paint solvents. The paint is a cured solid which has to be disposed of. These detackified paint solids floating around in this water curtain or flood sheet fluid (which is in continuous motion) cause foam to be generated. Additional chemicals have to be added to the flood sheet fluid to control this tendency to foam. Since there is some distance between where the paint is sprayed and the point at which the air-borne paint comes in contact with the flood sheet fluid, some of the air-borne paint contacts the walls and the floor of the booth. The walls and floor, as well as any other paint application equipment in the booth, will build up a thick, tacky coating of this paint if it is not cleaned off on a regular basis. To do this cleaning, various low-boiling solvent systems are utilized. These solvents either end up in the water curtain fluid to be recirculated and eventually evaporate into the air, which is let out to the outside environment, or having low solubility in water, directly pass to the environment. Current paint applications and clean-up technologies provide no means of trapping the low boiling (highly evaporative) solvents that are used to dilute the paint to a viscosity suitable for spray applications. These solvents also end up evaporating out of the flood sheet fluid system. Currently, volatile organic solvents are used to flush the unsprayed paint from the spray guns and the bells, and are also used to clean the outside of the hand-operated spray guns in a soak trough. These solvents are in contact with the air in the booth, and approximately forty percent (40%) of the solvent evaporates into the air of the booth. This increases the chances of worker exposure to harmful solvents and also adds these solvents to the air stream which will ultimately be discharged to the outside environment. Additionally, it increases the number of flammable formulations or chemicals that a manufacturer who uses a paint spray booth must have in storage, thus increasing his cost and the chances of accident during their handling. The proposed invention permits a single formulation to be used for all activities related to paint spray booth clean-up, thus minimizing the chemical hazard safety training required of the paint spray booth operators, the inventory diversity needed to be maintained by the owner, and the quantity of volatile chemicals released to the environment. An improvement on the current water flood sheet technology to address the problem of trapping some of the paint diluent solvents as well as a portion of the paint booth clean-up solvents is disclosed by the Nalco Chemical Company in their U.S. Patent No. 4,378,235. This U.S. Patent discloses replacing the water flood sheet fluid with an oil-in-water emulsion system which has been demonstrated to reduce the amount of low boiling solvents evaporating to the open environment. To avoid the cost of re-filling the flood sheet fluid system in the paint booth every time that the paint solids level reached an unmanageable concentration, the oil-in-water emulsion system is continually being reprocessed through a distillation unit. This process is defined in U.S. Patent No. 4,750,919. Nalco refers to this system as the Hydrocarbon Emissions Controls (HEC) system. The paint trapped by the oil-in water emulsion employed in the HEC system is neutralized or "detackified". This is taught in U.S. Patent No. 4,750,919. The resultant paint solids cannot be used as a coating. Moreover, the intractable nature of the detackified paint precludes easy recovery of valuable paint compounds such as pigments, solid fillers, and higher boiling point paint solvents. The solids are carried off to be incinerated. The use of low-boiling solvents to clean up the paint overspray on the walls and floor of the paint spray booth is still required with the HEC system. Accordingly, it would be an advance to the art if a method could be developed for the reclamation of paint and reduction and recovery of volatile organic carriers from paint spray booth systems using an economical absorbing fluid. A further object of this invention is to provide for the recovery of the paint without detackification, such that said recovered paint could be recycled either in part or as a whole formulated paint. Object of the invention is a process for reclaiming paint, paint components and volatile organic paint carrier or solvents from paint spray booths of the type comprising a chamber, a duct system for passing air down through such chamber to remove paint and volatile organic paint carrier, a sump containing a circulating hydrophilic liquid located at the bottom of the chamber, a flood sheet of circulating hydrophilic liquid, or both for removing volatile organic paint carrier and paint over-sprayed particles and paint from the air containing them, the improvement which comprises using as the hydrophilic liquid a water containing organic solvent solution comprising (a) 16 to 45 percent by weight of one or more compounds selected from the group of C₁-C₄-alkyl N-pyrrolidone, C₄-C₆ lactones, N,N'-C₁-C₄-dialkyl cyclic ureas and cyclic carbonates, wherein the total number of carbon atoms is 4 to 12, (b) 14 to 52 percent by weight of organic solvents selected from a C₄ to C₁₆ dibasic alkyl ester, a C₃ to C₂₀ glycol ether, ethyl-3-ethoxy propionate or mixtures thereof, and (c) the balance, water, said solution collecting said volatile organic paint carrier or solvent and collecting said apint as an uncured resin reusable as a paint coating material or as separable components for formulating into a paint coating material. We have discovered a novel method for the improvement of the current water flood sheet technology to address the problem of reclamation of paint and reduction and recovery of volatile organic paint carriers from paint spray booth systems. The invention replaces the water flood sheet fluid and the clean-up solvents for the paint application process found in industrial paint booths with a solution of N-methyl pyrrolidone, other high-boiling solvents, and water. The inventive process utilizing the above-identified flood sheet solution will allow for the following advantageous results. Due to the addition of the solvents to the water, the amount of paint overspray trapped by the flood sheet will be greater than if the flood sheet were pure water, thus reducing the amount of paint particles entering the outside environment. The flood sheet system will be continually re-distilled to eliminate the cost of emptying and refilling and provide a means to trap some of the solvent utilized as paint diluent, thus lowering the volume of solvent emissions to the environment. The N-methyl pyrrolidone, solvent(s), and water solution will be a composition that allows it to be used as an agent to clean up the paint overspray that builds up on the walls and floor of the paint booth. This eliminates the need for separate clean-up solvents, and again causes a decrease in the volume of solvent being emitted to the environment outside the paint booth. Using a solvent/water solution to catch the paint particles eliminates the need for detackifying the paint. The paint overspray particles are solubilized in the solution. This prevents the paint in the flood sheet fluid from adhering to the surfaces in the paint booth system with which it comes in contact. The paint/fluid solution will not need to be treated with the detackifying chemicals and rendered inactive. The paint will remain as a dissolved resin system capable of being reformulated for reuse. The flood sheet fluid will be fed into an on-site distillation unit on a continuous basis. This is a means to collect the reusable active resin systems and pigments. The recycled or distilled flood sheet solution will be pumped back into the flood sheet system for re-use with necessary make-up water and solvent being added to keep the solution at a constant composition. The solvent solution of the invention eliminates the need for the addition of chemical defoamers to the flood sheet which are needed for both the pure water as well as the HEC system technologies. The presence of water mitigates the aggressiveness of the pure organic, energy-saving solvents, thus allowing their use in existing paint spray booth systems without the expense of replacing seals and gaskets. The presence of water also uniquely reduces the vapor pressure of N-methyl pyrrolidone in the solution, minimizing vapor concentration in all areas of the plant where air contacts the flood sheet fluid. The presence of the solvents reduces the vapor pressure of the water in the solution compared to the water vapor pressure of either a pure water or oil-in-water emulsion; this reduces condensation on spray booth exit air handling equipment such as filters, ducts, and fans, and on cool building and equipment surfaces exposed to flood sheet fluid vapor. This reduces maintenance costs required to replace wet filters and to clean and paint or repair corroded building components or capital and energy costs needed to maintain such surfaces above the dew point temperature of flood sheet fluid equilibrated air streams. The replacement of volatile purge solvent with the low vapor pressure water solvent solution will minimize solvent emissions and reduce the required variety of chemicals stored by the booth owner. THE SOLVENT SOLUTION The water containing organic solvent solution used in the instant inventive process comprises as component (a) a C₄ to C₁₂, preferably a C₅ to C₁₀ aprotic heterocyclic oxygenate, which are C₁-C₄-alkyl N-pyrrolidones, such as N-methyl pyrrolidone, N-ethyl pyrrolidone, and l,5-dimethyl-2-pyrrolidone, the C₄-C₆ lactones such as γ-butyrolactone and γ-valerolactone, the N,N'-C₁-C₄-dialkyl cyclic ureas such as tetrahydro-l,3-dimethyl-2(1H)pyrimidinone and l,3-dimethyl-2-imidazolidinone and the cyclic carbonates such as propylene carbonate; preferred is N-methyl pyrrolidone. The water containing organic solution preferably contains as component (b) 4 to 20 percent by weight of a C₃ to C₂₀ glycol ether, and l0 to 32 percent by weight of a C₄ to C₁₆ dibasic alkyl ester, ethyl-3-ethoxy propionate or mixtures thereof. The C₃ to C₂₀ glycol ether constituent of the present invention is at least one of propylene glycol, polypropylene glycol oligomers or monoalkyl ether or monophenyl ether derivatives of said glycols and oligomers. The glycol oligomers are polymers consisting of two, three or four propylene oxide monomer units terminated at each end with a hydroxy group. The monoalkyl ether derivatives have one to four carbon atoms in the alkyl moiety. Preferably, tripropylene glycol monomethyl ether is used. The amount of propylene glycol or glycol ether used in the composition is generally from about 4 to about 20 percent by weight, preferably from about 7 to about 15. Solvents that may be used in place of tripropylene glycol monomethyl ether include 2-butoxyethanol, triethylene glycol monomethyl ether, propylene-glycol N-butyl ether, ethylene glycol phenyl butyl ether, propylene glycol phenyl butyl ether, dipropylene glycol N-butyl ether, and dipropylene glycol monomethyl ether. The C₄ to C₁₆ dibasic alkyl ester constituent of the present invention is at least one C₁-C₄ dialkyl ester of at least one C₂-C₆ aliphatic dibasic acid. Generally, the dibasic ester constituent will be a mixture of at least two and typically three C₂-C₆ aliphatic dibasic acid esters. Mixtures of C₂-C₆ aliphatic dibasic acids are a byproduct from the manufacture of adipic acid and the esters are afforded by the esterification of the byproduct stream. Although the composition of such a byproduct stream varies considerably, generally it is composed of 15 to about 30 percent succinic acid, from about 50 to about 73 percent glutaric acid, and from about 6 to about 25 percent adipic acid. Although the ethyl, propyl, and butyl esters are useful, the methyl esters are typically the most economically attractive and, consequently, preferred. Dibasic esters within the scope of the present invention are commercially available from E. I. du Pont de Nemours & Company, Wilmington, Delaware, U.S.A., or can be prepared by methods known to those skilled in the art. Preferably component (b) is a mixture of organic solvents comprising at least one solvent which has a higher boiling point and at least one solvent which has a lower boiling point under distillation conditions than component (a). With NMP as component (a) the solvent with a higher boiling point is preferably tripropylene glycol monomethyl ether and the solvent with a lower boiling point is ethyl-3-ethoxy propionate (EEP, Eastman Chemical Company). EPP is preferably used in mixture with the C₄ to C₁₆ dibasic alkyl ester. Some of the EPP will be lost to the first distillation cut of paint solvent volatiles so as to permit a purer cut of NMP, with respect to the paint volatiles to be obtained. The solvents provide the following advantages to the instant process; lower distillation temperatures giving better economics; better cleaning activity of the walls and equipment in the paint booth, greater ability to suspend solids in solution. Additionally, it is noted that with the instant process, it is felt that the chemicals which are placed into the current water flood sheets will not be required for the maintenance of a stable recirculation system. However, these chemicals (fungicides/bactericides, defoamers, flocculate, and detackifiers) should be readily soluble in the solutions listed for the instant process with no decrease in the chemical activity associated with said chemical. Thus, they can be used as desired and/or needed without changing the scope of the instant invention. By choosing high-boiling solvent components to blend with the water, the solvent loss due to evaporation from the flood sheet is minimized to a point where the total emissions from paint shop operations is less than that of the current water flood sheet technology. The solvents are chosen with the following criteria in mind: (a) high flash point, (b) low degree of aquatic or animal toxicity, and (c) low vapor pressure. Thus, in general, those solvents having the least negative impact on both the worker and the environment outside to the paint booth are chosen. Additionally, the solvents were chosen with a concern for cost and volatility, so that the most expensive solvent would be most volatile and, hence, most completely recovered during the distillation process. The vapor pressure depression of the NMP by water is reversed as the water is removed, with the more volatile paint solvents during the first part of the distillation. With the process of the invention the uncured paint resin can be reclaimed and then reused as a paint coating material. The preferred formulation of the flood sheet fluid utilized in conjunction with the instant invention is illustrated in the following Examples, said Examples being illustrative only and in no way limiting the scope of the instant invention. EXAMPLE I This example illustrates the currently best-known composition that meets the criteria of not harming the worker or his outside environment, and also will solubilize the paint as well as be usable as an agent to clean the paint overspray from the walls and floor of the paint booth. Preparation: The N-methyl pyrrolidone, Di Basic Ester, and TPM are added to the mixing vessel. The order of addition is not critical. The solvent components are mixed at a slow speed for approximately 30 minutes. After the 30 minute solvent component blend cycle is complete, the water is added to the mixing vessel and the whole system is mixed for approximately an additional 30 minutes. Distillation of Flood Sheet Fluid for Reclamation of Paint Examples 2, 4, and 6 had as the flood sheet solution the exact formulation that is described in Example 1. The flood sheet solutions were all prepared following the same procedure outlined in Example 1. Example 2 (A) 1200.00 grams of the solution described in Example 1 was added to a 2000 ml glass beaker. The beaker was placed onto a magnetic stirrer and the speed was increased to a medium setting. Then, 150.0 g of a Flash Red high solids solvent based automotive base coat paint (BASF Coatings & Colorants E174RE022) was added to the solution. The mixture was left to mix for 30 minutes. The paint was fully dissolved in the solution. (B) To a 4 liter glass boiling pot was added 1334.07 grams of the above solution. The boiling pot was connected to a glass distillation column, and heat was then applied to the pot. When the temperature of the pot reached 54°C, a vacuum of 120 mm Hg was applied to the whole system. Over a 90 minute period, the temperature of the pot was increased to 141°C and the vacuum applied to the system was changed to 48 mm Hg. Various solvent blends were collected during the distillation process. The final sample collected was a 70.0 gram mixture of paint and solvent with a viscosity that was similar in consistency to that of the initial paint introduced into the experiment. Example 3 (A) 0.32cm thick piece of cold rolled steel (5" x 3") was hand sanded with a fine grain sandpaper and then washed with an acetone soak to clean off any rust and grease from the surface. (B) The steel panel was then coated with approximately 0.005 - 0.0076 cm of the final paint distillate retain sample from Example 2. The paint was applied with a 3.81 cm wide polyester bristle brush. (C) The panel was then placed in convection air oven for 40 minutes with the temperature set at 145°C. (D) The sample was removed from the oven at the end of 40 minutes and a totally cured film of paint was on the surface of the panel. Example 4 (A) 1200.0 grams of the solution described in Example 1 was added to a 2000 ml glass beaker. The beaker was placed onto a magnetic stirrer and the speed was increased to a medium setting. Then 115.0 g of a Clear Coat (high solids compatible solvent based) automotive paint (BASF Coatings & Colorants E04CK303) was added to the solution. The resultant solution was left to mix for 30 minutes. The paint was fully dissolved in the solution. (B) To a 4 liter glass boiling pot was added 1310.8 grams of the above solution. The boiling pot was then connected to a glass distillation column, and heat was then applied to the pot. The temperature of the pot and contents was raised to approximately 103°C. This temperature was maintained for three hours and 15 minutes. Various solvent mixtures distilled off during this time. At the 3 hour and 15 minute mark, a vacuum was applied to the system and gradually reduced to 8 mm of Hg over a 1 hour and 45 minute time span. During this time frame, various cuts of solvent were captured from the distillation column. After 15 minutes with a vacuum of 8 mm Hg being applied to the system, the distillation was stopped. The resulting clear mixture of paint and solvent had a viscosity of the consistency of the original paint. Example 5 (A) A panel identical to the one described in Example 3 was prepared for coating in the same manner as outlined in that example. (B) The panel was then coated with approximately 0.0076 - 0.0127 cm of the final paint distillate retain sample from Example 4. The paint was applied with a 3.1 cm wide polyester bristle brush. (C) The panel was then placed in a convection air oven for 40 minutes with the temperature set at 145°C. (D) The sample was removed from the oven at the end of 40 minutes, and a totally cured film of paint was on the surface of the panel. Example 6 (A) 1220.0 grams of the solution described in Example 1 was added to a 2000 ml glass beaker. The beaker was placed onto a magnetic stirrer and the speed was increased to a medium setting. Then 115.0 grams of a Flame Red water borne automotive base coat (BASF Coatings & Colorants E55RD021) was added to the solution. The mixture was left to mix for 30 minutes. The paint was fully dissolved in the solution. (B) To a 4 liter glass boiling pot was added 1331.9 grams of the above solution. The boiling pot was then connected to a glass distillation column, and heat was then applied to the pot. The temperature of the pot and contents was gradually increased for approximately 3 hours. During this 3 hour time span, the vacuum was increased from 11" to 25". Various solvent blends distilled out of the solution during this time span. At the end of the 3 hour period, the temperature was raised to 80°C and a vacuum of 3 mm Hg was applied to the system. The vacuum and temperature were maintained at these settings for 30 minutes. The distillation was then stopped. The resultant mixture of paint and solvent had a viscosity of the consistency of the initial paint put into solution. Example 7 (A) A sample identical to the one described in Example 3 was prepared for coating in the same manner as outlined in Example 3. (B) The panel was coated with approximately 0.00254 - 0.00508 cm of the final paint distillate retain sample from Example 6. The paint was applied with a 3.81 cm wide polyester bristle brush. (C) The panel was then placed into a convection air oven for 40 minutes with the temperature set at 145°C. (D) The panel was removed from the oven at the end of 40 minutes, and a totally cured film of paint was on the surface of the panel. These Examples clearly demonstrate the novel ability of the present inventive process to reclaim the uncured paint resin from the novel sheet fluid such that it may be reused as a paint coating. Nothing in the prior art of paint booth flood sheet processes or compositions teaches this surprising result.

Claims: A process for reclaiming paint, paint components and volatile organic paint carrier or solvents from paint spray booths of the type comprising a chamber, a duct system for passing air down through such chamber to remove paint and volatile organic paint carrier, a sump containing a circulating hydrophilic liquid located at the bottom of the chamber, a flood sheet of circulating hydrophilic liquid or both for removing volatile organic paint carrier and paint oversprayed particles and paint from the air containing them, the improvement which comprises using as the hydrophilic liquid a water containing organic solvent solution comprising (a) 16 to 45 percent by weight of one or more compounds selected from the group of C₁-C₄-alkyl N-pyrrolidone, C₄-C₆ lactones, N,N'-C₁-C₄-dialkyl cyclic ureas and cyclic carbonates, wherein the total number of carbon atoms is 4 to 12, (b) 14 to 52 percent by weight of organic solvents selected from a C₄ to C₁₆ dibasic alkyl ester, a C₃ to C₂₀ glycol ether, ethyl-3-ethoxy propionate or mixtures thereof, and (c) the balance, water, said solution collecting said volatile organic paint carrier or solvent and collecting said paint as an uncured resin reusable as a paint coating material or as separable components for formulating into a paint coating material. A process as claimed in claim 1 wherein the water containing organic solution contains as compound (b) 4 to 20 percent by weight of a C₃ to C₂₀ glycol ether, and 10 to 32 percent by weight of a C₄ to C₁₆ dibasic alkyl ester, ethyl-3-ethoxy propionate or mixtures thereof. A process as claimed in one of claims 1 or 2 wherein component (b) is a mixture of organic solvents comprising at least one solvent which has a higher boiling point and at least one solvent which has a lower boiling point under distillation conditions than compound (a). A process as claimed in one of claims 1 to 3 wherein component (a) is N-methylpyrrolidone and the solvent with a higher boiling point is tripropylene glycol monomethyl ether and the solvent with a lower boiling point is ethyl-3-ethoxy propionate.

Inventors: JAMES LAWRENCE EDWIN, WALSH WILLIAM CHARLES, JAMES, LAWRENCE EDWIN, WALSH, WILLIAM CHARLES
Applicants: BASF CORP, BASF CORPORATION
Application year: 1990
Main classification: B05D1
IPC codes: B05B15, B01D47, C08J11, C09D7, C09D9