Polyester film with nodule surface

Abstract: A polyester film having a nodule surface is disclosed. The acrylic coating is preferably a crosslinked composition having a relatively high methyl methacrylate content and specific surfactants. The acrylic coating composition is applied as an aqueous dispersion to polyester film, preferably after corona treatment of the polyester film. The nodule surface reduces the coefficient of friction of the polyester film. The coating composition comprises from 60 to 90 mole percent methylmethacrylate; from 10 to 35 mole percent of at least one modifier selected from the group of ethylacrylate, propylacrylate, butylacrylate, and mixtures of these; and from 3 to 10 mole percent of a crosslinkable monomer or a self-crosslinking monomer selected from the group of N-methylolmethacrylamide, N-methylolacrylamide, acrylamide, methacrylamide, and mixtures of these; with from 2 to 15 weight percent of the nonionic surfactant and at least 0.1 percent by weight of the anionic surfactant.

Description: The present invention relates to a coated polyester film having utility as a substrate for magnetic tape applications such as video tape. More particularly, the present invention relates to a polyester film having an acrylic coating with a relatively high methyl methacrylate content on at least one major surface of said film. It has been found that relatively high methyl methacrylate content terpolymers, in combination with specific surfactants and using relatively low anionic surfactant concentrations, impart a "nodule" surface to polyester film substrates which reduced the coefficient of friction of such films. Oriented polyester films possess generally good mechanical properties resulting in wide commercial acceptance as substrates for magnetic tape applications. The polyester film substrate may be coated on at least one side with an adhesion-promoting primer coating, which is itself overcoated with a magnetizable coating. Acrylic terpolymers conforming to the terpolymers of the present invention have previously been incorporated in aqueous coating dispersions for polyester films. U.S. Patent 4,371,489 to P. McGrail, titled "Production Of Anti-Static Thermoplastic Films" broadly discloses a methylmethacrylate/ethylacrylate/methacrylamide terpolymer having molar range percentages of 40 to 80 percent methylmethacrylate; 15 to 50 mole percent ethyl acrylate; and 2 to 25 mole percent crosslinkable comonomer. The preferred methyl methacrylate molar range is taught to be 45 to 50 percent. The McGrail patent teaches the use of this terpolymer in combination with an alkyl- or arylphosphate ester which is present as free acid or as a partial or complete sodium- or potassium salt to form a coating composition for polyester films. The McGrail patent does not disclose nor suggest the creation of a nodule surface as a method of reducing the high coefficient of friction of polyester film. Similarly, "Polyester Film Primed With Crosslinked Acrylic Polymers", Japanese Patent Application No. 259422/1984 (Published August 6, 1985), discloses a methylmethacrylate/ethylacrylate/N-methylolacrylamide terpolymer wherein the methylmethacrylate preferably comprises 35 to 85 mole percent of the terpolymer. The application broadly suggests the use of a surfactant, but does not disclose specific surfactants for use with the acrylic terpolymer. Other patents also disclose crosslinkable acrylic terpolymers as having utility as coatings for polyester films, typically to reduce static charge build-up on the film as it travels over record/playback heads, rollers, guidepins, and other components of electronic eguipment. Generally, however, these patents teach the use of relatively lower amounts of methyl methacrylate. For example, U.S. Patent 4,214,035 (July 22, 1980) to J. Heberger, titled "Antistatic Coated Polyester Films", broadly discloses a methylmethacrylate/ethylacrylate/methacrylamide terpolymer having a glass transition temperature in the range of from 40 to 50 °C, preferably 45 °C. While the patent is silent as to any mole percentages of the components of the terpolymer, it is believed that the methylmethacrylate molar percentage of this terpolymer does not exceed 50 mole percent. Similarly, U.S. Patent 3,819,773 (June 25, 1974) to G. Pears, titled "Method For Preparing Reclaimable Coated Polyester Films", discloses a crosslinkable acrylic terpolymer comprising 50 percent by weight methylmethacrylate. British Patent Specification No. 1,125,460, "Improvements Relating To Polyester Film Base" (Published August 28, 1968), discloses a high (70 to 95 percent by weight) methylacrylate (as opposed to methylmethacrylate) terpolymer, but it comprises itaconic acid (2 to 20 percent) and either diallylphthlate or divinylbenzene (3 to 30 percent) as the other comonomers rather than the comonomers of the present invention. The patent is directed to rendering polyethyleneterephthalate film less hydrophobic, and does not disclose nor suggest the creation of a "nodule" surface as a method of reducing the high coefficient of friction of polyester film. "A Process For Preparing Subbing Coated Polyester Film", British Patent Specification No. 1,168,171 (Published October 22, 1969), discloses high (70 to 90 percent by weight) content methylmethacrylate terpolymers which must have 3 to 30 percent of itaconic acid, and 7 to 20 percent of an aliphatic polyfunctional compound containing at least two sites of carbon to carbon unsaturation, where at least one of the sites is represented by an allylic or vinylic group, glycidylacrylate, glycidylmethacrylate esters wherein the alcohol portion of the ester is hydroxysubstituted, or fumaric acid. U.S. Patent 4,571,363 to Culbertson et al. teaches a polyester film primed with an acrylic, crosslinked terpolymer for a primer coating. The primer coating comprises at least about 50 percent by weight of acrylic and/or methacrylic monomers; from about 1 percent to about 15 percent by weight of a comonomer capable of intermolecular crosslinking upon the application of heat, and from 0 to about 49 percent by weight of one or more halogen free monoethylenically unsaturated monomers copolymerizable therewith. While this patent states that it is desirable to include a surfactant for wettability, no specific surfactant types and amounts are disclosed nor required. One problem associated with polyester film is the high coefficient of friction of uncoated and unmodified oriented polyester film. Such film typically is very smooth, and tends to "block" or stick to other layers of such film when wound upon itself. Prior artisans have devised two methods for reducing the high coefficient of friction of oriented polyester film, both of which involve roughening the smooth surface of the polyester film in order to reduce its high coefficient of friction. The polyester film surface must not be excessively roughened, or its utility as a substrate for magnetic tape applications will be destroyed. One well known method involves coating the film with a crosslinkable coating which contains particles and then crosslinking the coating composition, thereby binding the particles. The function of the particles is to reduce the coefficient of friction by creating a more roughened surface than the uncoated polyester film. Coating the polyester film surface with a particle-containing coating composition to reduce the film's coefficient of friction is not a panacea. Problems which are associated with this method include wide particle size distribution and agglomeration of the particles, both of which tend to degrade the film's utility as a magnetic tape substrate. Another method for reducing the inherently high coefficient of friction of polyester film involves the creation of "internal" particles during the polyester synthesis by controlled precipitation of the catalyst residue and reaction thereof with polyester monomers or oligomers. Such particles are substantially homogeneously distributed throughout the polyester resin, and only a small amount are present at or near the surface of the polyester film where coefficient of friction is measured. Such internally generated particles are described more fully in U.S. Patents 4,138,386 and 4,067,855. This method requires extremely close control over the polyester synthesis and can create processing difficulties during the manufacture of polyester film from such resin. U.S. Patent 4,138,386 (February 6, 1979) to M. Motegi et al, titled "Polyester Film For Magnetic Tape", discloses the use of internally-generated polyester particles in combination with inert particles selected from the group consisting of oxides or salts of elements of Groups II, III, or IV of the periodic table. U.S. Patent 4,461,797 (July 24, 1984) to T. Adachi et al, titled "Polyester Film With Projections And Depressions On The Surface", discloses the addition of organic or inorganic particles to a polyester resin prior to manufacture into a polyester film. By preheating the extruded polyester film prior to orientation, void formation around the particles is substantially eliminated. The surface of the Adachi et al '797 biaxially oriented polyester film is characterized by elliptical depressions having a projection in the middle of the depression. This surface exhibits a reduced coefficient of friction in comparison to polyester film which was not preheated prior to orientation. U.S. Patent 4,233,352 (November 11, 1980) to M. Ono et al, titled "Polyester Film And Method Of Manufacture Thereof", discloses a polyester film having a discontinuous layer of a watersoluble polymer on at least one major surface. The discontinuous polymeric layer comprises discrete "worm-like" patterns comprising a mixture of a water soluble polymer, polysiloxane and/or styrene-butadiene polymer, and optionally natural wax. The water soluble polymer may be any water soluble polymer having a molecular weight between 10,000 and 2,000,000. Suitable water soluble polymers include methylcellulose, hydroxyethylcellulose, carboxymethylcellulose, polyvinylalcohol, gum tragacanth, gum arabic, casein, and gelatin. U.S. Patent 4,548,855 (October 22, 1985) to M. Ono et al, titled "Polyester Film For Magnetic Recording Medium", is an improvement over the film disclosed in Ono et al '352. Ono et al '855 discloses a polyester film having a discontinuous layer of a water soluble polymer on at least one major surface. The discontinuous layer should not exceed 50 nm (500 angstroms) in thickness, and is preferably from 5 to 30 nm (50 to 300 angstroms) thick. The water soluble polymer should have a molecular weight of from 10,000 to 2,000,000, and may be polyvinylalcohol, tragacanth gum, gum arabic, casein, gelatin, methylcellulose, hydroxyethylcellulose, and carboxymethylcellulose. Ono et al '855 further discloses fine particles which are present on the surface of the discontinuous layer and the exposed polyester film surface. The fine particles may be alkali metal salt derivatives of sulfonic acid which are mixed with the polyester resin or the particles may be "internally" generated by precipitation of the polyester catalyst. The particle size may range from 5 to 40 nm (50 to 400 angstroms), and the shape of the particles is not critical. EP-A-0 039 225 discloses a film coated with a latex which includes a crosslinkable methylmethacrylate-ethyl acrylate-methacrylamide terpolymer and a silicone coating. US-A-2,678,285 discloses applying to a surface of a film a dispersion of finely divided resinous material and a surfactant and thereafter drying said surface. The present invention relates to an acrylic terpolymer coating on a polyester film which produces a low coefficient-of-friction film useful in magnetic tape applications, or other areas where low coefficient-of-friction film is desirable. The acrylic terpolymer, along with specific surfactants, is in an aqueous emulsion and is applied to the film. The dried residue of the aqueous emulsion forms nodules on the coated surface of film. The acrylic terpolymer coating may be uncrosslinked or preferably crosslinked. In order to obtain the nodule surface coating, the amounts of the components are critical. In the broad aspect, the present invention relates to an oriented polyester film having a nodule surface for producing a low coefficient of friction surface comprising an oriented polyester film having an acrylic coating on at least one surface, said acrylic coating being the dried residue of an aqueous emulsion of water and an acrylic composition said acrylic composition comprising: (a) from 80 to 97.9 percent by weight, based upon the total weight of said composition, of a methylmethacrylate terpolymer comprising: (1) at least 60 mole mole percent of methylmethacrylate; (2) from 10 to 35 mole percent of at least one modifier selected from the group of ethylacrylate, propylacrylate, butylacrylate, and a mixture of these; (3) from 1 to 10 mole percent of at least one comonomer selected from the group of N-methylolacrylamide, N-methylolmethacrylamide, acrylamide, methacrylamide, and a mixture of these; (b) from 2 to 15 percent by weight, based upon the total weight of said composition, of a nonionic surfactant; (c) at least 0.1 percent by weight, based upon the total weight of said composition, of an anionic surfactant wherein the dried residue of the acrylic coating is obtainable through coating the polyester film and heat-setting and wherein said acrylic coating is in the form of nodule islands rising from the surface of said film with a minimum surface area coverage of 5 percent. In another aspect, the present invention relates to a process for manufacturing an oriented polyester film having a nodule surface for producing a low coefficient-of-friction surface according to any of claims 1 to 5 comprising: (i) corona treating at least one surface of a polyester film; (ii) coating said corona treated surface of said polyester film with an emulsion of water and an acrylic composition, said acrylic composition comprising: (a) from 80 to 97.9 percent by weight, based upon the total weight of said composition, of a methylmethacrylate terpolymer comprising: (1) at least 60 mole percent of methylmethacrylate; (2) from 10 to 35 mole percent of at least one modifier selected from the group of ethylacrylate, propylacrylate, butylacrylate, and a mixture of these; (3) from 1 to 10 mole percent of at least one comonomer selected from the group of N-methylolacrylamide, N-methylolmethacrylamide, acrylamide, methacrylamide, and a mixture of these; (b) from 2 to 15 percent by weight, based upon the total weight of said composition, of a nonionic surfactant; (c) at least 0.1 percent by weight, based upon the total weight of said composition, of a nonionic surfactant; (iii) heat-setting said film to form said nodule surface; wherein said "nodule" surface comprises nodule islands rising from the surface of said film with a minimum surface coverage of 5 percent. The attached photomicrograph shows a typical nodule surface according to the preferred embodiment of the invention in which the acrylic terpolymer coating is applied at a 1 percent by weight solids level to a film of polyethyleneterephthalate. The polyester film of the present invention can be manufactured from various thermoplastic polyester resins. Polyethyleneterephthalate, polytetramethyleneterephthalate, polyethylene-2,6-napthalate and poly-1,4-cyclohexylenedimethylterephthalate are examples of suitable polyester homopolymers which may be employed in the practice of the present invention. Copolyesters may also be used. Possible copolyesters include polyethyleneterephthalate/isophthalate, polyethyleneterephthalate/adipate, polyethyleneterephthalate/sebacate, and polyethyleneterephthalate/-sulphoisophthalate. Ethyleneterephthalate homopolyester is preferred. The polyester film of the present invention can be manufactured by an extrusion process. The polyester resin is first heated to a molten state and then extruded through a wide slot die in the form of an amorphous sheet. The sheet-like extrudate is rapidly cooled or "quenched" to form a cast sheet of polyester by contacting and travelling partially around a polished, revolving casting drum. The cast polyester sheet may then be axially stretched in one direction, either in the direction of film travel (machine direction) or perpendicular to the machine direction (transverse direction), while being heated to a temperature in the range of from 80 °C to 160 °C, preferably 90 °C to 100 °C. The degree of stretching may range from 3.0 to 5.0 times the original cast sheet unit dimension, preferably from about 3.2 to about 4,2 times the original cast sheet dimension. Preferably, the polyester film is biaxially oriented (stretched in both the machine direction and the transverse direction) rather than uniaxially oriented. Prior to coating the polyester film surface with the methacrylate terpolymer coating composition, the film may be surface-treated in a conventional manner by exposure to an electric corona discharge. Electric corona discharge is a conventional surface treatment which is commonly performed on polyester films to enhance the film's surface qualities, especially its adhesive and printing properties. Electric corona discharge methods and apparatus are described in U.S. Patents 3,057,792 and 4,239,973. For uniaxially oriented film, the corona treatment followed by the coating may occur during the in-line manufacturing process, either before stretch orientation or after. If the corona treatment followed by the coating occurs before stretch orientation, heating the film before stretch orientation will drive off the water. If the corona treatment and coating for uniaxially oriented film occur after the stretch orientation step during in-line manufacturing, it is necessary to completely dry the film before winding. For uniaxially oriented film, the preferred procedure is to corona treat and coat the film before stretch orientation. For biaxially oriented film, the corona treatment followed by the terpolymer coating may occur during the in-line manufacturing process, either before stretch orientation, or between the machine draw and transverse draw of biaxial stretch orientation, or after stretch orientation. If the corona treatment and coating steps occur after stretch orientation, it is necessary to completely dry the film before winding. If the corona treatment and coating occur before orientation, or between draw during orientation, the later orientation steps which require the film to be heated would drive off the excess water from the terpolymer coating. Preferably, for biaxially oriented film the corona treatment and subsequent terpolymer coating occur between draws during the stretch orientation step. The polyester sheet is coated on the electric corona discharge treated surface with an aqueous terpolymer dispersion of the acrylic coating composition described below. The coating composition may conveniently be applied as an aqueous dispersion or emulsion using any of the well known coating techniques. For example, the film may be coated by roller coating, spray coating, gravure coating or slot coating. The heat applied to the film during the subsequent preheating, stretching, and heat-setting stages is generally sufficient to evaporate the water and crosslink the acrylic coating, if a crosslinkable monomer comprised a portion of the acrylic coating. The coated, oriented polyester film may then be heat treated for a period of time necessary to crystallize the film. Crystallization imparts dimensional stability and good tensile properties to the polyester film. Oriented polyethyleneterephthalate film may be heat-set at a temperature ranging from 190 °C to 240 °C, preferably from 215 °C to 235 °C. The coated crystalline, oriented polyester film is then wound into a roll. The above description describes an in-line (during manufacturing) coating process. While this is the preferred process for oriented polyester film, oriented polyester film could also be coated off-line (after manufacture of the film is complete) preferably after corona treatment. Off-line operations are typically conducted by a converter who purchases film from a manufacturer and further processes it for specific customers. While the coating of the present invention can be utilized for off-line operations, better nodule formation and lower coefficient of friction results are achieved when the present invention is employed in-line (during manufacturing of the film). The acrylic coating composition of the present invention comprises from 80 to 97.9 weight percent of a methylmethacrylic terpolymer which employs a relatively high amount (i. e., at least 60 mole percent) of methylmethacrylate; from 10 to 35 mole percent of an acrylate modifier selected from the group consisting of ethylacrylate, propylacrylate, butylacrylate, or a mixture of these; and from 1 to 10 mole percent of a comonomer selected from the group consisting of N-methylolacrylamide, N-methylolmethacrylamide, acrylamide, methacrylamide, or a mixture of these. The coating composition also includes from 2 to 15 percent by weight, based upon the total weight of the coating composition, of a nonionic surfactant; and at least from about 0.1 percent by weight, based upon the total weight of the coating composition, of an anionic surfactant. The higher the methylmethacrylate concentration, the more hardness the acrylic coating will display. Hardness contributes to incomplete latex film formation. For this reason conventional acrylic coatings generally do not employ methylmethacrylate in molar amounts greater than 60 mole percent. The methylmethacrylate terpolymer of the present invention employs at least 60 mole percent, preferably from 75 to 85 mole percent, of methylmethacrylate. The second component of the methyl methacrylate terpolymer is at least one modifier selected from the group consisting of ethylacrylate, propylacrylate, and butylacrylate. The modifier permits adjustment of the hardness of the acrylic coating by varying the methylmethacrylate monomer molar concentration. From 10 to 35 mole percent, preferably from 10 to 20 mole percent, of the modifier is employed in the methylmethacrylate terpolymer. Ethylacrylate is preferred. The third component of the methylmethacrylate terpolymer is the comonomer, which may be N-methylolacrylamide, N-methylolmethacrylamide, acrylamide and methacrylamide. N-methylolacrylamide and N-methylolmethacrylamide are preferred due to their "self-crosslinking" ability to react with another N-methylol functional group. By contrast, acrylamide and methacrylamide alone are not crosslinkable. However, it is preferred that the terpolymer be crosslinked. To crosslink the terpolymer when acrylamide or methacrylamide are used requires a second functional group with which to react, such as may be provided by the inclusion of a melamine-formaldehyde or urea-formaldehyde resin. Other functional compounds which may be employed to crosslink with acrylamide or methacrylamide are aziridines, glycoluril-formaldehyde, benzoguanamines, acrylamide glycolic acid, bis-acrylamidoglyoxal, diacrylamido acetic acid and the like. If acrylamide and/or methacrylamide are employed, the amount of a second reactional resin such as melamine-formaldehyde or urea-formaldehyde may be present from about 0.1 to about 5 weight percent based on the total weight of the coating composition, i. e., the terpolymer and the second reactional resin. From 1 to 10 mole percent, preferably from 3 to 7 mole percent, of the comonomer is employed in the methylmethacrylate terpolymer. The three components discussed above - methylmethacrylate, a modifier, and a (preferred crosslinkable) comonomer - are emulsion polymerized to form a methylmethacrylate terpolymer latex which is diluted to form an aqueous dispersion suitable for coating the polyester substrate as described above. The function of the nonionic surfactant is to prevent post-emulsion polymerization agglomeration of the methylmethacrylate terpolymer particles and resultant grit formation. The nonionic surfactant may range from 2 to 15 percent by weight, based upon the total weight of the coating composition. Less than 2 percent by weight results in emulsion instability. More than about 10 percent by weight of the nonionic surfactant results in diminishing nodule formation. Nonionic surfactants which are operable in the present invention include alkylphenol ethoxylates which conform to the formula set forth below: wherein R means alkyl, and m may range from 15 to 100. Alkyphenol ethoxylates are well known surfactants which are commercially available from several suppliers, including Rohm and Haas Company in Philadelphia, Pennsylvania; Union Carbide Corporation in New York, New York; and the Whitestone Chemical Department of BASF, in Spartanburg, South Carolina. Octylphenolethoxylates are a preferred class of non-ionic surfactant for the present invention. Most preferred is octylphenolethoxylate where the degree of polymerization (m) is nominally 40. The function of the anionic surfactant is to emulsify the acrylic comonomers during the polymerization reaction and to stabilize the reaction mixture generally. The anionic surfactant would preferably be employed at 0.1 or higher weight percent based upon the total weight of the coating composition to produce good micelle formation. Less than about 0.1 percent by weight of the anionic surfactant results in an unstable emulsion, more than about 0.5 percent by weight of the anionic surfactant does not significantly improve the coating. Anionic surfactants which may be operable in the present invention include sodium laurylsulfate or sodium dodecylbenzenesulfonate, for example. Emulsion polymerization is a conventional polymer synthesis process carried out at atmospheric pressure and at a temperature of from about 40 °C to 60 °C. In practice, an aqueous emulsion of the three comonomers and the surfactants is slowly metered into an aqueous solution containing a redox initiator system as well as additional quantities of the anionic and nonionic surfactants. Typical initiators for emulsion polymerization reactions are peroxide compounds such as laurylperoxide, benzoylperoxide, methylethylketoneperoxide, and the like. As in all emulsion polymerization reactions, water quality is an important consideration. Deionized water should be used since the presence of certain multivalent ions in uncontrolled concentrations can interfere with both the initiation process and the action of the emulsifier. As the comonomer emulsion is slowly metered into the water containing the surfactants and the initiator, copolymerization of the methylmethacrylate, modifier, and the comonomer begins, thereby forming the methylmethacrylate terpolymer particles. Near the completion of the polymerization reaction, the reaction mixture will comprise small methylmethacrylate terpolymer particles suspended in water due to the nonionic and anionic surfactants. This latex may typically have a solids level of from 25 to 30 percent and thus it will be necessary to dilute it with water to achieve a more usable range for coating. Higher solids levels will result in agglomeration of the methyl methacrylic terpolymer particles into larger particles or clumps of particles which will tend to precipitate from the solution as grit. As discussed above, the nonionic surfactant serves as a post-polymerization emulsion stabilizer. The above described emulsion polymerization process is well known and described in "Principles of Polymerization" by George Odian, second edition, published by John Wiley and Sons. The coating of the present invention may be applied to the base film as an aqueous dispersion having a solids concentration within the range of about 0.5 to 15 percent by weight, preferably about 1 to 8 percent by weight. The preferred solids level is such as to yield a final dry coating thickness within the range of about 2,54 · 10 -7 to 2,54 · 10 -5 cm, which translates into a solids level on a weight basis of from 3,05 mg/m 2 to 0,305 g/m 2 . The preferred thickness range of the dried acrylic coating is from about 2,54 · 10 -7 to 7,62 · 10 -6 cm, with an optimum thickness of about 6,25 · 10 -7 cm. It has been found that specific coating compositions which come within the above description - relatively high methylmethacrylate content terpolymers in combination with specific surfactants at relatively low concentrations - form a "nodule" surface upon oriented polyester film when the coating composition is coated upon oriented or non-oriented polyester film, and heat set. Such a "nodule" surface exhibits a reduced coefficient of friction in comparison to acrylic coated polyester films which do not exhibit the nodule surface, and may possess significant commercial advantages over coated polyester films which rely upon the addition of discrete particles to reduce their coefficient of friction. "Nodule surface" may be defined as nodule islands rising from the surface of said film with a minimum surface area coverage of about 5 percent. If the surface of the polyester film is coated too thickly, no individual nodule islands will exist. Instead, each nodule contacts other nodules such that they coalesce and no individual islands exist, thus forming a ridged pattern of acrylic terpolymer coating. A coverage of less than about 5 percent of the surface area of the film does not significantly reduce the coefficient of friction compared with non-coated polyester film. Thus, the desired range of coating to achieve the nodule surface is between 5 percent of the surface area of the polyester film and the point where the surface area is so completely covered that the nodules coalesce and few, if any, individual islands exist. In a preferred embodiment the acrylic coating composition comprises 94.8 percent by weight (based on the total weight of the composition) of methylmethacrylate terpolymer, 5.0 percent by weight nonionic surfactant, and 0.2 percent by weight anionic surfactant, where the terpolymer comprises 80 mole percent methylmethacrylate, 15 mole percent ethylacrylate, and 5 mole percent N-methylolacrylamide. This preferred coating composition when applied at a 1 percent by weight solids level produces a nodule surface, when dry, as illustrated in the attached photomicrograph, whereby the nodules cover a minimum of about 9.8 percent of the surface, and a maximum of 13.9 percent of the surface with an average of about 11 percent of the surface of the polyester film. The average diameter of a circle with the same area as the surface nodules, known as the Waddel diameter, is a common method of measuring nodules. In the preferred coating composition, the minimum Waddel diameter in micrometers was 0.071, the maximum was 0.520, and the average was 0.196. Lastly, the longest dimension of the nodules of the preferred coating composition, in micrometers was 0.09 as the minimum, 1.27 as a maximum, and 0.279 as the average. In this preferred embodiment, the coating polymer is also present as a thin film in the areas between nodules. Colloidal silica may be incorporated into the aqueous emulsion of the terpolymer at a concentration of from about 5 percent to about 50 percent by weight of the aqueous emulsion. When the colloidal silica is employed, the preferred concentration is about 10 percent by weight of the acrylic terpolymer emulsion with the colloidal silica having an average particle size of 20 millimicrons (nm). In the examples below, biaxially oriented polyethyleneterephthalate film having acrylic coatings were evaluated for various properties such as slip (coefficient of friction), haze, and textured surface. Coefficient of friction (COF) was determined in accordance with ASTM Method D 1894-68 and all film samples were conditioned in accordance with ASTM Method D-618, Procedure A. The dimensionless units of coefficient of friction are interpreted to indicate good slip (or handleability) if the COF ranges between 0.3 to 0.7. Below 0.2, slip is too great. That is, the films are difficult to wind and are considered unsatisfactory. Above 0.7 slip is inadequate. Film having a COF in excess of 0.7 is prone to "blocking". When a film blocks, it frequently does not slip over the surface to which it is in contact. Haze, the best indication of the clarity of the film, is determined according to ASTM Test Method D 1003-61 Procedure A Section 7. Whether the acrylic surface of the film sample possessed a "nodule surface" was determined by visual inspection via scanning electron microscope for nodule islands and to determine surface area of the nodules. The film surface was characterized by SEM (scanning electron microscopy) examination. The "nodule" surface coverage was determined by digital image analysis of the SEM surface images. Both the SEM and digital image analysis system are commercially available systems. The SEM is a Cambridge Stereoscan 200 with a LaB 6 (lanthanum hexaboride) source, digital image storage capability, and a secondary electron detector. This SEM is interfaced to a Kevex 8000 Microanalysis system equipped with Kevex's AIA (Automated Image Analysis) digital imaging software for image processing and feature analysis. Example 1 Polyethyleneterephthalate film was corona treated and subsequently in-line coated between the first and second stretching operations with a 4 percent solids aqueous dispersion of a methylmethacrylate coating composition having crosslinked and uncrosslinked formulations. The nominal "wet" lay down was 2.4 g/m 2 (0.5 pounds/1000 square feet) of forward drawn sheet. The biaxially oriented polyester film's nominal thickness (uncoated) was 75 µm (300 gauge). The formulations and experimental results of the coated films are set forth in Table I. The following abbreviations have the following meanings: MMA Methylmethacrylate EA Ethylacrylate MAM Methacrylamide AM Acrylamide N-MA N-methylolmethacrylamide A coefficient of friction between 0.2 and 0.7 is good. Below 0.2 means the coated film is too slippery, while above 0.7 means that the film will not slide sufficiently against its comparative surface. The terminology A/A means the coefficient of friction between a top surface and a like top surface, while A/B means the coefficient of friction between a top surface and the reverse surface (the other side) of the film. For critical haze applications, any number less than 1.0 is acceptable. If haze is not a factor, any number is acceptable. Both the coating formulations in Table I produced a nodule surface. The first coating composition contained, among other components, 5 mole percent methylacrylamide. As explained previously, when acrylamide or methacrylamide are employed, it may be necessary to employ a second reactional resin such as urea-formaldehyde or melamine-formaldehyde to crosslink the coating polymer. Therefore, the first coating composition employed 4 percent by weight of Cymel 303, a melamine-formaldehyde resin commercially available from American Cyanamid Company. Contrarily, the second coating composition contained 5 mole percent acrylamide with no second reactional resin. Accordingly, Example 1 shows that it is not mandatory that a second reactional resin be employed when non-self-crosslinking monomers such as acrylamide or methacrylamide are employed. Example 2 Following the general practice and procedure of Example 1, polyethyleneterephthalate film was corona treated and subsequently in-line coated between the first and second stretching operations with a 4 percent solids aqueous dispersion of the crosslinkable methylmethacrylic coating composition. The nominal wet lay down was 2.4 g/m 2 (0.5 lbs (wet)/1000 square feet) of forward drawn sheet. The biaxially oriented polyester film's nominal thickness (uncoated) was 21 µm (83 gauge). The coating formulations and experimental results of the coated films are set forth in Table II. Various mole percents of methylmethacrylate were employed with both self-crosslinkers such as N-methylolacrylamide and with other monomers such as methacrylamide, both with and without a second reactional resin such as melamine-formaldehyde. It is theorized that the first composition didn't produce a nodule surface because too much nonionic surfactant was employed. The remaining 3 compositions contained 75 mole percent methylmethacrylate in the terpolymer and produced a nodule surface when emulsified with: A) a self-crosslinking monomer (N-methylolacrylamide); B) a monomer (methacrylamide); and C) a monomer with a second reactional resin (methacrylamide and melamine-formaldehyde (Cymel 303)). Example 3 In view of Example 2, it was decided to widely vary the methylmethacrylate composition, vary the surfactant levels, and vary the amount of coating formulation (1 percent solids vs. 4 percent solids) to determine the various effects such changes make upon the nodule formation. The procedure set forth in Example 1 with respect to coating the film was repeated. The nominal "wet" lay down was 2.4 g/m 2 (0.5 pounds (wet) per 1,000 square feet) of forward drawn film. The biaxially oriented polyester film's nominal thickness (uncoated) was 21 µm (83 gauge). The coating formulations and experimental results of the crosslinked coated film are set forth in Table III. The results of Table III tend to indicate several things, namely: 1) 1 percent solids in the coating formulation tends to result in a coated polyester film which has less haze, which is desirable in certain applications such as glazing; 2) with more methylmethacrylate it is generally necessary to employ more nonionic surfactant in order to produce a stable emulsion; 3) replacing some of the solids content of the coating formulation with colloidal silica is possible and desirable when methylmethacrylate is less than about 70 mole percent of the emulsion composition; 4) lower mole percents of methylmethacrylate means a softer terpolymer and thus the addition of colloidal silica appears to improve the coefficient of friction, while a higher mole percent of methylmethacrylate results in a harder terpolymer and the addition of colloidal silica does not appear to influence the coefficient of friction in a significant manner. Example 4 Both uniaxial and biaxial films were employed for in-line (during manufacturing of the film) and off-line (after manufacture of film) operations. The acrylic terpolymer emulsion (solids) comprised 80 mole percent MMA, 15 mole percent EA, and 5 mole percent N-MA, using 0.2 percent by weight sodium laurylsulfate and 5.0 percent by weight octylphenol ethoxylate. The coating was applied by the reverse gravure process with a nominal wet lay down of 2.4 g/m 2 (0.5 pounds per 1,000 square feet) of forward drawn film. Experiment 2 was a repetition of the last experiment in Table III. Experiment 3 off-line coated side B of the Experiment 2 film with 0.3 percent solids. This level of solids was chosen because it was approximately the amount of coating on the Experiment 2 film after it was stretch-oriented (stretch-orienting was done at about 3.3 to 1). Experiment 4 is similar to Experiment 3, except 1 percent solids was coated off-line onto the film. Experiments 5-7 relate to uniaxial film. This film was unoriented prior to coating (in-line) and uniaxially oriented and heat set. Experiment 6 differed from Experiment 7 only in the use of colloidal silica. The results are set forth in Table IV. Experiment Film Thickness (Gauge) Orientation Amount Formulation Location of Coating Nodules? Coefficient of Friction Static Kinetic Total Haze Percent Transmission Percent 1 92 Biaxial Uncoated None No A/A BK BK .22 90.7 B/B BK BK A/B BK BK 2 92 Biaxial .9% Solids + .1% Air Side-In Line Yes A/A .46 .43 .87 91.0 Colloidal Silica (Side A) B/B BK BK A/B .46 .46 3 92 Biaxial .3% Solids Drum Side-Off Line Yes A/A - - 1.06 91.1 (Side B) B/B BK .64 A/B .6 .55 4 92 Biaxial 1% Solids Drum Side-Off Line Yes A/A .53 .54 1.69 91.6 (Side B) B/B .66 .70 A/B .7 .64 5 350 Uniaxial Uncoated None No A/A - - 1.40 90.9 B/B BK .68 A/B BK .64 6 350 Iniaxial 1% Solids Drum Side-In line Yes A/A - - 1.80 90.9 (Side B) B/B .38 .44 A/B .38 .42 7 350 Uniaxial .9% Solids + .1% Drum Side-In Line Yes A/A - - 1.69 91.0 Colloidal Silica (Side B) B/B .46 .49 A/B .52 .56 BK = Blocked As Experiment 3 and 4 demonstrate, off-line coating doesn't appear to be as effective as in-line coating. Experiments 6 and 7 demonstrate that uniaxial film can be employed in the present invention. Thus, it is apparent that there has been provided, in accordance with the invention, a coated film and a process for producing a coated film that fully satisfies the objects, aims, and advantages set forth above.

Claims: An oriented polyester film having a nodule surface for producing a low coefficient of friction surface comprising an oriented polyester film having an acrylic coating on at least one surface, said acrylic coating being the dried residue of an aqueous emulsion of water and an acrylic composition said acrylic composition comprising: (a) from 80 to 97.9 percent by weight, based upon the total weight of said composition, of a methylmethacrylate terpolymer comprising: (1) at least 60 mole percent of methylmethacrylate; (2) from 10 to 35 mole percent of at least one modifier selected from the group of ethylacrylate, propylacrylate, butylacrylate, and a mixture of these; (3) from 1 to 10 mole percent of at least one comonomer selected from the group of N-methylolacrylamide, N-methylolmethacrylamide, acrylamide, methacrylamide, and a mixture of these; (b) from 2 to 15 percent by weight, based upon the total weight of said composition, of a nonionic surfactant; (c) at least 0.1 percent by weight, based upon the total weight of said composition, of an anionic surfactant wherein the dried residue of the acrylic coating is obtainable through coating the polyester film and heat-setting and wherein said acrylic coating is in the form of nodule islands rising from the surface of said film with a minimum surface area coverage of 5 percent. The coated film of claim 1, characterized in that said nonionic surfactant is an alkylphenol ethoxylate, especially octylphenol ethoxylate with a nominal degree of polymerization of 40, or sodium laurylsulfate or sodium dodecylbenzenesulfonate, being present from 2 to 10 percent by weight, based on the total weight of said coating composition. The coated film of claim 1, characterized in that said anionic surfactant is present in a range from 0.1 to 0.5 percent by weight, based upon the total weight of said coating composition. The coated film of any of claims 1 to 3, characterized in that said coating further comprises colloidal silica. The coated film of any of claims 1 to 4, characterized in that said comonomer is self-crosslinking, that said modifier is ethylacrylate, that said non-ionic surfactant is octylphenol ethoxylate, and that said anionic surfactant is sodium laurylsulfate. A process for manufacturing an oriented polyester film having a nodule surface for producing a low coefficient-of-friction surface according to any of claims 1 to 5 comprising: (i) corona treating at least one surface of a polyester film; (ii) coating said corona treated surface of said polyester film with an emulsion of water and an acrylic composition, said acrylic composition comprising: (a) from 80 to 97.9 percent by weight, based upon the total weight of said composition, of a methylmethacrylate terpolymer comprising: (1) at least 60 mole percent of methylmethacrylate; (2) from 10 to 35 mole percent of at least one modifier selected from the group of ethylacrylate, propylacrylate, butylacrylate, and a mixture of these; (3) from 1 to 10 mole percent of at least one comonomer selected from the group of N-methylolacrylamide, N-methylolmethacrylamide, acrylamide, methacrylamide, and a mixture of these; (b) from 2 to 15 percent by weight, based upon the total weight of said composition, of a nonionic surfactant; (c) at least 0.1 percent by weight, based upon the total weight of said composition, of an anionic surfactant; (iii) heat-setting said film to form said nodule surface; wherein said "nodule" surface comprises nodule islands rising from the surface of said film with a minimum surface coverage of 5 percent. The process of claim 6, characterized in that said film is unoriented film prior to said coating step, and further comprising the step of: stretch-orienting said film after coating said film such that said film is uniaxially oriented, and that said film is heat-set to crystallize said film. The process of claim 6, characterized in that said oriented film is uniaxially oriented prior to said coating step, and further comprising the step of: biaxially orienting said film after coating said film, and heat-setting said biaxially oriented film to crystallize said film. The process of claim 6, wherein said film is biaxially oriented film.

Inventors: CULBERTSON EDWIN C, HEBERGER JOHN M, CULBERTSON, EDWIN C., HEBERGER, JOHN M.
Applicants: HOECHST CELANESE CORP, HOECHST CELANESE CORPORATION
Application year: 1990
Main classification: C08J7
IPC codes: B29C55, C08L33, C08J5, C08F20, C08F220, C09D133, B29K67, B29L7, C08J7