Radiation curable acrylate polyesters

Abstract: Acrylate polyesters are made by the reaction of a diol (in particular polyoxyethylene or polyoxytetramethylene glycol), a dibasic acid anhydride (e.g. succinic or phthalic anhydride) and glycidyl acrylate. The polyester can be formulated into radiation curable compositions, in particular by blending it with a polyethylenically unsaturated radiation-curable compound and, optionally, a monoethylenically unsaturated radiation-polymerizable monomer, which compositions can be used as coatings, inks, and adhesives which cure at high rates when exposed to actinic radiation.

Description: Field of the Invention This invention pertains to certain acrylated polyesters and to radiation-curable compositions containing them. Background of the Invention Owing to environmental concerns and the high cost of solvents, commercial interest in radiation - curable compositions is constantly increasing. Legislation which restricts the amount of solvent and other pollutants that can be vented to the atmosphere is one reason for this increased interest. Other reasons are the concerns expressed by unions and individuals over the possible toxic effects of prolonged exposure to volatile organic materials and also the high cost of petroleum derived solvents. Generally, radiation curable systems are essentially 100 percent reactive systems, i.e. substantially all of the components react to produce the final product. Such systems can be cured by exposure to medium- to high-energy ionizing radiation or to actinic radiation in the presence of photoinitiators. Various types of ethylenically unsaturated compounds have been used in making radiation curable compositions. Examples of such compounds include acrylated epoxide resins, such as those described in U.S. Patents Nos. 3,676,398, 3,770,602, 4,072,529 and 4,511,732. Acrylated urethanes, such as those described in U.S. Patents Nos. 3,700,643 and 4,511,732, have also been used in radiation curable compositions. Other acrylated urethane compounds made from a poly(alkylene oxide polyol), a polyisocyanate and an unsaturated active hydrogen-containing compound are described in U.S. Patents Nos. 4,133,723 and 4,188,455. These urethane compounds are said to be radiation curable in the presence of oxygen. Unsaturated polyesters based on maleic anhydride or fumaric acid have been used in combination with styrene and later with multifunctional acrylates as ultraviolet-cured wood fillers and topcoats. The cure rates of these polyesters are slow due to the relatively unreactive nature of the unsaturated polyester internal double bond. In order to obtain faster curing compositions, acrylated polyesters have been developed. As described in U.S. Patent No. 4,206,025, such polyesters are generally made by the direct esterification of a polyester polyol with acrylic acid. Although acrylated polyesters are faster curing than unsaturated polyesters, they still cure more slowly than epoxy acrylates owing to the absence of the beta-hydroxy group, which has been shown to minimize the effects of oxygen inhibition during ultraviolet (UV) cure. The manufacture of such polyester acrylates involves a two-step esterification reaction that can be complex, thereby affecting productivity and cost. U.S. Patents Nos. 3,089,863 and 4,659,778 describe a one-step process for preparing polyesters by addition polymerization involving the reaction of a polyol, a dibasic acid anhydride and a wide range of monoepoxides. When the monoepoxide is glycidyl acrylate, a beta-hydroxy acrylic ester is formed. Summary of the Invention In one aspect, this invention provides acrylated polyesters which are the reaction product of a polyoxyalkylene diol with a dibasic acid anhydride and glycidyl acrylate. The present invention provides, especially, an acrylated polyester that contains 2 to 6 unsaturated acrylic groups per molecule and that is made by reacting (a) polyoxytetramethylene glycol having an average molecular weight of 650 to 1000, (b) a dibasic acid anhydride selected from succinic acid anhydride and phthalic acid anhydride and (c) glycidyl acrylate in the ratio of one mole of glycol to 2 to 6 moles of dibasic acid anhydride and 2 to 6 moles of glycidyl acrylate; preferably, the amounts, in moles, of dibasic acid anhydride and glycidyl acrylate are equal. In another aspect, this invention provides radiation curable compositions based on acrylated polyesters, particularly such compositions that are obtained when an acrylated polyester of this invention is blended with a polyethylenically unsaturated radiation curable compound and, optionally, a monoethylenically unsaturated radiation polymerizable monomer. The present invention provides, especially, a radiation curable composition comprising a blend of (A) 20 to 80 weight percent of an acrylated polyester of this invention; (B) 20 to 80 weight percent of a polyethylenically unsaturated radiation curable compound that is different from (A); and (C) 0 to 50 weight percent of a monoethylenically unsaturated radiation polymerisable monomer, wherein the said weight percentages are based on the total weight of (A), (B) and (C). The compositions of this invention may be utilized as coating, ink and adhesive compositions and can be cured by, for example, medium- to high-energy electrons or by ultraviolet light if a photoinitiator is added. These compositions cure at rates much higher than those of conventional acrylated polyesters. Description of preferred embodiments The acrylated polyesters of this invention may be made by the process described in U.S. Patent 3,089,863. The polyesterification process involves the reaction of a diol, a dicarboxylic acid anhydride and a monoepoxide. The reaction is a stepwise reaction which is initiated by the reaction of the diol with the anhydride to form an ester group and a carboxylic acid group. The carboxylic acid group then reacts with an epoxide group forming another ester group and a hydroxyl group. The hydroxyl group can then react with another anhydride group. The reaction will continue until terminated resulting in either a hydroxyl group or a carboxylic acid group functionality. The glycols used to make the polyesters of this invention are polyoxytetramethylene glycols having molecular weights of 650 to 1000. These polyoxytetramethylene glycols are well known compositions which are made by ring-opening polymerization of tetrahydrofuran. The dicarboxylic acid anhydrides useful in this invention are succinic anhydride and phthalic anhydride. The monoepoxide used to make the polyesters of this invention is glycidyl acrylate. The polyesters of this invention contain on average 2 to 6, preferably 3 to 4, unsaturated acrylic ester groups per molecule. The polyesters are obtained by reacting the three components in the molar ratio of one mole of glycol to 2 to 6 moles of anhydride and 2 to 6 moles of glycidyl acrylate. In the reaction, the moles of anhydride are generally equal to the moles of glycidyl acrylate so that the polyester is terminated with a beta hydroxyl group and not a carboxylic acid group. However, if it is desirable for the polyester to have an acid value, a slight excess of anhydride can be used. The polyester can be prepared by mixing all of the components together and heating them until the esterification reactions are complete. However, preferably the anhydride and glycol are mixed together and heated to melt the anhydride if it is a solid and then the glycidyl acrylate is added incrementally. The reaction is conducted at a temperature of 100 to 140°C until the reaction is complete, as evidenced by the disappearance of epoxy content and/or acid content. When used in radiation-curable compositions, the acrylated polyesters are usually blended with polyethylenically unsaturated radiation polymerizable compounds and, optionally, monoethylenically unsaturated radiation polymerizable monomers. The polyethylenically unsaturated radiation polymerizable compounds which can be blended with the acrylated polyesters are compounds which contain two or more ethylenically unsaturated groups and, preferably, two to six ethylenic groups. The ethylenically unsaturated groups include acrylate and methacrylate groups, vinyl groups and allyl groups. Compounds which contain the acrylate or methacrylate groups include acrylic or methacrylic esters of polyols wherein the polyols have two or more hydroxyl groups per molecule. Examples of such compounds are the diacrylic or dimethacrylic acid esters of ethylene glycol, propylene glycol, butanediol, butenediol, hexanediol, polyoxyethylene glycols, polyoxypropylene glycols, polyoxybutylene glycols, di- and triacrylic or methacrylic acid esters of glycerine and hexanetriol, trimethylolpropane, trimethylolethane and di-, tri-, tetra-, penta-, and hexa-acrylic or methacrylic acid esters of dipentaerythritol. Other polyacrylates or methacrylates are the acrylated and methacrylated glycidyl ethers of dihydric phenols, acrylated and methacrylated epoxidized vegetable oils and acrylated and methacrylated urethanes. The preferred polyethylenically unsaturated radiation polymerizable compounds are the acrylic acid esters of aliphatic polyols. Monoethylenically unsaturated radiation polymerizable monomers which can be used in this invention are the well known monomeric compounds which contain one ethylenically unsaturated group per molecule. Examples of such monomers are alkyl acrylates and methacrylates wherein the alkyl group contains from 1 to 12 carbon atoms, mono- and polyalkoxyalkylacrylates and methacrylates wherein the alkoxy groups and alkyl groups each contain from 1 to 4 ( carbon atoms and wherein the molecules contain from 1 up to 20 alkoxy groups, hydroxyalkyl acrylates and methacrylates wherein the alkyl group contains from 2 to 6 carbon atoms, vinyl aromatic compounds, vinyl halides, vinyl pyrrolidone, vinyl pyridine, and vinyl carbazole. The radiation curable compositions can be cured by any of the normal actinic radiation curing methods. The radiation can be ionizing radiation (either particulate or nonparticulate) or non-ionizing agents. As a suitable source of particulate radiation, one can use any source which emits electrons or charged nuclei. Particulate radiation can be generated, for example, by electron accelerators, such as the Van der Graff accelerator, resinous transformers, and radioactive elements, such as cobalt 60, strontium 90, and the like. As a suitable source of nonparticulate non-ionizing radiation, any source which emits radiation in the range of from 10⁻³ angstroms (0.1 pm) to 2000 angstroms (200 nm) can be used. Suitable sources included vacuum ultraviolet lamps, such as xenon or krypton arcs. As a suitable source of non-ionizing radiation, any source which emits radiation from 2000 angstroms (200 nm) to 4000 angstroms (400 nm) can be used. Suitable sources include mercury arcs, carbon arcs, tungsten filament lamps, sun lamps and lasers. All of these devices and sources are well known in the art and those skilled in radiation technology are fully aware of the manner in which radiation is generated and the precautions to be taken in its use. When the radiation curable coating compositions are to be cured by exposure to non-ionizing radiation, e.g. ultraviolet radiation, photoinitiators are added to the composition. Suitable photoinitiators, which are well known in the art, include 2,2-diethoxy-acetophenone, 2,3 or 4-bromoacetophenone, benzaldehyde, benzoin, benzophenone, 9,10-dibromoanthracene, 4,4'-dichlorobenzophenone, 2,3-pentanedione, hydroxycyclohexyl phenyl ketone and xanthone. Such photoinitiators are generally added in amounts of from 0.1 weight percent up to 10 weight percent, and preferably 1 to 5 weight percent, based on the weight of the total curable composition. Photoactivators can also be used in combination with the photoinitiators. Examples of photoactivators are methylamine, tributylamine, 2-aminoethylethanolamine, cyclohexylamine, diphenylamine and tribenzylamine. The radiation curable compositions are preferably used as coating, ink and adhesive compositions. The compositions can be applied by conventional means, including spraying, curtain coating, dip padding, roll coating and brushing procedures. The compositions can be applied to any acceptable substrate, for example wood, metal, glass, fabric, paper, fiber, or plastics. The radiation curable compositions can be made by blending the components in the amounts of 20 to 80 weight percent acrylated polyester, 20 to 80 weight percent polyethylenically unsaturated radiation curable compound and 0 to 50 weight percent of a monoethylenically unsaturated radiation polymerisable monomer wherein the weight percents are based on the total weight of the three components. Preferably, the compositions will contain 50 to 70 weight percent acrylated polyester, 20 to 30 weight percent polyethylenically unsaturated compound and 10 to 20 weight percent monoethylenically unsaturated monomer. The amounts of each component used will vary depending on the needed application viscosity and the properties required for the cured product. Additional additives which can be used in the compositions include wetting agents, fillers, defoamers, dyes and pigments, the uses of which are well known in the art. The following examples illustrate the invention in more detail. Parts and percentages are by weight unless otherwise designated. Example 1 To a suitable reactor equipped with agitator, condenser, temperature measuring device, and addition funnel were added 487 parts of polyoxytetramethylene glycol having an average molecular weight of 974, 222 parts of phthalic anhydride and 0.18 part of phenothiazine. Heat and agitation were applied raising the temperature to 284°F (140°C) in about 50 minutes, at which point a homogeneous solution was obtained. 1.4 parts of chromium salt catalyst were added, the lu temperature was lowered to 260°F (126.7°C) and was held at 250-260°F (121.1 - 126.7°C) for 2 hours. Glycidyl acrylate, 192 parts, and hydroquinone, 0.09 part, were added to the addition funnel. The temperature in the reactor was lowered to 230°F (110°C) and slow addition of the glycidyl acrylate was begun. The addition was completed in one hour. Heating at about 230°F (110°C) was continued for about 23 hours to complete the esterification reaction. Hydroquinone, 0.09 part, was added and heating was discontinued. The resulting product had an epoxide equivalent weight of 91,000, an acid value of 1.89, a Gardner color of 4 and a viscosity of 3110 cps (mPa.s) at 150°F (65.6°C). Example 2 Using the same procedure described in Example 1, an acrylated polyester was prepared by reacting 487 parts of polyoxytetramethylene glycol having an average molecular weight of 974 with 150 parts of succinic anhydride and 192 parts of glycidyl acrylate using the same catalysts and inhibitors described in Example 1. The resulting product had an epoxide equivalent weight of 42,800, an acid value of 4.17, a Gardner color of 3 and a viscosity of 2250 cps (mPa.s) at 150°F (65.6°C) Example 3 Using the procedure described in Example 1, polyester acrylates were made by reacting long-chain glycols with anhydrides and glycidyl acrylate in the mole ratios of 1 mole of glycol with 3 moles of anhydride and 3 moles of glycidyl acrylate. Polyester acrylates were made with the following long chain glycols. Polyoxytetramethylene glycol 250 (PTMG 250) Polyoxytetramethylene glycol 650 (PTMG 650) Polyoxytetramethylene glycol 1000 (PTMG 1000) Polyoxyethylene glycol 400 (PEG 400) Polyoxyethylene glycol 1000 (PEG 1000) Polyoxypropylene glycol 425 (PPG 425) Polyoxypropylene glycol 1010 (PPG 1010) The numbers following "glycol" refer to the approximate molecular weight of the glycols. Dicarboxylic acid anhydrides used to make the polyester acrylates were as follows: Succinic anhydride (SA) Phthalic anhydride (PA) Data relating to the polyester acrylates are shown in the following tables. The abbreviations in the tables have the following meaning: Each of the polyesters shown in the tables has a theoretical unsaturated acrylic functionality of 3. Polyester Acrylates with PTMG 250 Polyester Anhydride Theor. M.W. Wt/DB Visc.@ 150°F (65.6°C) AV WPE Color A1 SA 934 311 2930 2.8 24,300 14 A2 PA 1078 359 4760 4.8 26,600 6 Polyester Acrylates with PTMG 650 Polyester Anhydride Theor. M.W. Wt/D.B Visc.@ 150°F (65.6°C) AV WPE Color B1 SA 1334 445 3750 3.6 27,800 4 B2 PA 1478 493 40,000 1.0 30,000 4 Polyester Acrylates with PTMG 1000 Polyester Anhydride Theor. M.W. Wt/D.B Visc.@ 150°F (65.6°C) AV WPE Color C1 SA 1684 561 2250 4.2 42,800 3 C2 PA 1828 609 3110 1.9 91,000 4 Polyester Acrylates with PEG 400 Polyester Anhydride Theor. M.W. Wt/D.B Visc.@ 150°F (65.6°C) AV WPE Color D1 SA 1084 361 2000 2.71 29,000 13 D2 PA 1228 409 4590 1.4 20,000 13 Polyester Acrylates with PEG 1000 Polyester Anhydride Theor. M.W. Wt/D.B Visc.@ 150°F (65.6°C) AV WPE Color E1 SA 1684 561 600 5.2 49,700 15 E2 PA 1828 609 3580 2.4 93,000 6 Polyester Acrylates with PPG 425 Polyester Anhydride Theor. M.W. Wt/D.B Visc.@ 150°F (65.6°C) AV WPE Color F1 SA 1109 370 2035 1.7 28,900 11 F2 PA 1253 418 7675 0.7 21,700 10 Polyester Acrylates with PPG 1010 Polyester Anhydride Theor. M.W. Wt/D.B Visc.@ 150°F (65.6°C) AV WPE Color G1 SA 1684 561 400 4.5 28,400 2 G2 PA 1828 609 1590 2.9 47,000 3 Example 4 Each of the polyesters shown in the tables of Example 3 was formulated into radiation curable coating compositions as follows: 60 weight percent polyester acrylate 25 weight percent tripropylene glycol diacrylate 15 weight percent isobornyl acrylate 4 pph hydroxycyclohexylphenyl ketone Each of the coating compositions was drawn down on untreated aluminium Q panels with a No. 6 Mayer rod to give 0.5 mil (12.7 µm) films. The films were cured using two 300 watt/inch (118 watt/cm) Fusion System electrodeless lamps at the maximum belt speed that gave a tack free film. The cure speed is shown in Table 4 as feet per minute (1 ft/min = 0.3048 m/min), the higher the number the faster the cure. Solvent resistance of the cured coatings was determined using methylethyl ketone (MEK) and is reported in Table 4 in number of double rubs. (Procedure described in "Radiation Curing" Vol. 10, No. 4, November, 1983, pp 8-13). Example 5 Several commercial polyester acrylates were formulated using the same amounts of components as described in Example 4. These formulations were cured at the maximum belt speed that gave a tack-free film and tested for solvent resistance as previously described. See Table 5. Cure Speed and Solvent Resistance of Cured Polyester Acrylates Polyester Cure Speed Solvent Resistance A1 50 8 A2 25 60 B1 150 22 B2 200 21 C1 125 6 C2 125 4 D1 D2 50 22 E1 50 3 E2 125 2 F1 25 9 F2 25 35 G1 15 2 G2 25 2 Cure Speed and Solvent Resistance of Commercial Polyester Acrylates Polyester Cure Speed Solvent Resistance Synocure 3120 25 67 Ebecryl 150 25 48 Ebecryl 657 15 34 Ebecryl 810 2p @15 130 Ebecryl 830 15 >200 Aronix M-8030 2p @15 >200 Aronix M-8060 2p @15 >200 Aronix M-8100 15 >200 Setacure AP-575 15 195 Photomer 5018 2p @15 52 NOTE : p = passes The trade names in the first column of Table 5 may comprise registered trade marks.

Claims: Claims for the following contracting States : AT, BE, DE, FR, GB, IT A radiation curable acrylated polyester having 2 to 6 unsaturated acrylic groups per molecule, made by reacting (a) polyoxytetramethylene glycol having an average molecular weight of 650 to 1000, (b) a dibasic acid anhydride selected from succinic acid anhydride and phthalic acid anhydride and (c) glycidyl acrylate in the molar ratio of one mole of glycol to 2 to 6 moles of dibasic acid anhydride and 2 to 6 moles of glycidyl acrylate. The acrylated polyester of claim 1, wherein the moles of dibasic acid anhydride and glycidyl acrylate are equal. The acrylated polyester of claim 1 or 2 having 3 to 4 unsaturated acrylic groups per molecule. A radiation curable composition comprising a blend of: (A) 20 to 80 weight percent of an acrylated polyester; (B) 20 to 80 weight percent of a polyethylenically unsaturated radiation curable compound different from (A); and (C) 0 to 50 weight percent of a monoethylenically unsaturated radiation polymerizable monomer, wherein the weight percents are based on the total weight of (A), (B) and (C), and wherein said acrylated polyester (A) contains 2 to 6 unsaturated acrylic groups per molecule, and is made by reacting (a) polyoxytetramethylene glycol having an average molecular weight of 650 to 1000, (b) a dibasic acid anhydride selected from succinic acid anhydride and phthalic acid anhydride and (c) glycidyl acrylate in the molar ratio of one mole of glycol to 2 to 6 moles of dibasic acid anhydride and 2 to 6 moles of glycidyl acrylate. The radiation curable composition of claim 4 containing (A) 50 to 70 weight percent acrylated polyester; (B) 20 to 30 weight percent polyethylenically unsaturated radiation polymerizable compound different from (A); and (C) 10 to 20 weight percent of a monoethylenically unsaturated monomer. The radiation curable composition of claim 4 or 5, wherein the polyethylenically unsaturated radiation curable compound is an acrylic acid ester of a polyol. The radiation curable composition of claim 6, wherein the polyethylenically unsaturated radiation polymerizable compound is tripropylene glycol diacrylate. The radiation curable composition of any of claims 4 to 7, wherein the monoethylenically unsaturated monomer is an alkyl acrylate or polyalkoxyalkylacrylate. The radiation curable composition of any of claims 4 to 7 wherein the monoethylenically unsaturated monomer is isobornyl acrylate. The radiation curable composition of any of claims 4 to 9 containing a photoinitiator. The radiation curable composition of claim 10 wherein the photoinitiator is hydroxycyclohexyl phenyl ketone. The radiation curable composition of any of claims 4 to 11 wherein the moles of dibasic acid anhydride and glycidyl acrylate are equal. The radiation curable composition of any of claims 4 to 12 wherein the acrylated polyester has 3 to 4 unsaturated acrylic groups per molecule. A process for producing an acrylated polyester which comprises reacting (a) polyoxytetramethylene glycol having an average molecular weight of 650 to 1000, (b) a dibasic acid anhydride selected from succinic acid anhydride and phthalic acid anhydride and (c) glycidyl acrylate in the ratio of one mole of glycol to 2 to 6 moles of dibasic acid anhydride and 2 to 6 moles of glycidyl acrylate. A process according to claim 14, wherein the amount in moles of anhydride is substantially equal to the amount in moles of glycidyl acrylate. A process according to claim 14 or 15, wherein the said glycol and the said anhydride are mixed together and the glycidyl acrylate is added thereto incrementally, the reaction being conducted at a temperature of from 100°C to 140°C. A method of producing a radiation curable composition which comprises forming a blend of (A) from 20 to 80 weight percent of an acrylated polyester, (B) from 20 to 80 weight percent of a polyethylenically unsaturated radiation-curable compound that is different from the acrylated polyester in (A) and, optionally, (C) up to 50 weight percent of a monoethylenically unsaturated radiation polymerisable monomer, wherein the weight percentages are based on the total weight of (A), (B), and (C), and wherein the said acrylated polyester in (A) contains from 2 to 6 unsaturated acrylic ester groups per molecule and is made by the reaction of (1) a diol, (2) a dibasic acid anhydride and (3) glycidyl acrylate in the molar ratio of one mole of (1) to 2 to 6 moles of (2) and 2 to 6 moles of (3), the said diol being polyoxytetramethylene glycol having a molecular weight of from 650 to 1000 and the said dibasic acid anhydride being selected from succinic acid anhydride and phthalic acid anhydride. A method according to claim 17, wherein the amount in moles of anhydride is substantially equal to the amount in moles of glycidyl acrylate. Claims for the following contracting State : ES A process for producing an acrylated polyester which comprises reacting (a) polyoxytetramethylene glycol having an average molecular weight of 650 to 1000, (b) a dibasic acid anhydride selected from succinic acid anhydride and phthalic acid anhydride and (c) glycidyl acrylate in the ratio of one mole of glycol to 2 to 6 moles of dibasic acid anhydride and 2 to 6 moles of glycidyl acrylate. A process according to claim 1, wherein the amount in moles of anhydride is substantially equal to the amount in moles of glycidyl acrylate. A process according to claim 1 or 2, wherein the said glycol and the said anhydride are mixed together and the glycidyl acrylate is added thereto incrementally, the reaction being conducted at a temperature of from 100°C to 140°C. A process according to claim 1, 2 or 3 in which the resultant acrylated polyester has 3 to 4 unsaturated acrylic groups per molecule. A method of producing a radiation curable composition which comprises forming a blend of (A) from 20 to 80 weight percent of an acrylated polyester, (B) from 20 to 80 weight percent of a polyethylenically unsaturated radiation-curable compound that is different from the acrylated polyester in (A) and, optionally, (C) up to 50 weight percent of a monoethylenically unsaturated radiation polymerisable monomer, wherein the weight percentages are based on the total weight of (A), (B), and (C), and wherein the said acrylated polyester in (A) contains from 2 to 6 unsaturated acrylic ester groups per molecule and is made by the reaction of (1) a diol, (2) a dibasic acid anhydride and (3) glycidyl acrylate in the molar ratio of one mole of (1) to 2 to 6 moles of (2) and 2 to 6 moles of (3), the said diol being polyoxytetramethylene glycol having a molecular weight of from 650 to 1000 and the said dibasic acid anhydride being selected from succinic acid anhydride and phthalic acid anhydride. A method according to claim 5, wherein the amount in moles of anhydride is substantially equal to the amount in moles of glycidyl acrylate. A method according to claim 5 or 6 which comprises forming a blend of (A) 50 to 70 weight percent of the acrylated polyester; (B) 20 to 30 weight percent of the polyethylenically unsaturated radiation polymerisable compound different from (A); and (C) 10 to 20 weight percent of the monoethylenically unsaturated monomer. A method according to claim 5, 6 or 7, wherein the polyethylenically unsaturated radiation curable compound (B) is an acrylic acid ester of a polyol. A method according to claim 8, wherein the polyethylenically unsaturated radiation polymerisable compound (B) is tripropylene glycol diacrylate. A method according to any one of claims 5 to 9, wherein the monoethylenically unsaturated monomer is an alkyl acrylate or polyalkoxyalkylacrylate. A method according to any one of claims 5 to 9 wherein the monoethylenically unsaturated monomer is isobornyl acrylate. A method according to any one of claims 5 to 11, which comprises including a photoinitiator in the blend. A method according to claim 12 wherein the photoinitiator is hydroxycyclohexyl phenyl ketone. A method according to any one of claims 5 to 13 wherein the acrylated polyester has 3 to 4 unsaturated acrylic groups per molecule.

Inventors: JOHNSON MORRIS A, MCCONNELL JOANN A, WILLARD F KURTIS, JOHNSON, MORRIS A., MCCONNELL, JOANN A., WILLARD, F. KURTIS
Applicants: UCB SA, U C B, S.A.
Application year: 1990
Main classification: C08G63
IPC codes: C08F2, C08F283, C08F299, C08F290, C08G63