Material for dentistry

Abstract: A material for dentistry having a low odor, a low stimulation and a proper dough stage time is here disclosed which is prepared by blending a monomer selected from the group consisting of (meth)acrylate compounds represented by the general formula R₁ is a hydrogen atom or a methyl group, each of R₃, R₆ and R₁₀ is an alkyl group, and each of R₂, R₅, R₈ and R₉ is an alkylene group) and (meth)acrylate dimers.

Description: BACKGROUND OF THE INVENTION (a) Field of the Invention The present invention relates to a material for dentistry comprising a specific (meth)acrylate compound. (b) Description of the Related Prior Art In recent years, many materials for dentistry comprising synthetic polymers have been developed, and some of them take the form of compositions each comprising monomers, a polymerization initiator and other components which can be polymerized and cured when used. Examples of such compositions include (1) crown restoration materials such as chemically polymerizable and photopolymerizable composite resins and quick-curing resins (fast-polymerizable resins), (2) adhesive and transitory adhesives, for example, between a composite resin and a tooth, between a metal and a tooth, and between teeth, (3) chemically polymerizable and photopolymerizable pit and fissure sealants, (4) artificial crown materials such as thermally polymerizable and photopolymerizable hard crown resins, (5) transitory crown materials such as polycarbonate crowns and fast-setting resins for crowns, (6) denture plate materials such as thermally polymerizable, cold polymerizable (inclusive of casting type) and injection-moldable acrylic resins and adhesive denture plate resins, (7) restoration materials such as denture plate lining agents and restoration fast-setting resins, and (8) impression materials such as agar, alginates, polysulfide rubbers, silicone rubbers and (meth)acrylic impression materials. Among these materials, for example, as the composite resin or the hard crown resin, there is used a blend of at least one monofunctional monomer, at least one polyfunctional monomer, an inorganic filler and a radical polymerization initiator, and as the crown resin, the sealant or the adhesive, there is used a combination of at least one monofunctional monomer, at least one polyfunctional monomer and a radical polymerization initiator. Furthermore, a restoration material such as the denture plate, the denture plate lining agent and the restoring quick polymerizable resin is required to be colorless and transparent, to be easily colored, to be aesthetic and to be excellent in workability, and therefore as this kind of restoration material, there is used a mixture of a polymer component (which is in the state of a powder in most cases) such as polymethyl methacrylate (hereinafter referred to as "PMMA") and polyethyl methacrylate"(hereinafter referred to as "PEMA"), at least one monofunctional monomer, at least one polyfunctional monomer and a radical polymerization initiator. Examples of the above-mentioned monofunctional monomer component include methyl methacrylate (MMA), ethyl methacrylate (EMA), butyl methacrylate (BMA), 2-hydroxyethyl methacrylate (HEMA) and H₂C=C(CH₃)COOC₂H₄OCOC₂H₅. Examples of the polyfunctional monomer component include 1,6-hexanediol dimethacrylate (HD), ethylene glycol dimethacrylate (1G), triethylene glycol dimethacrylate (3G), bisphenol A diglycidyl dimethacrylate (Bis-GMA), trimethylolpropane trimethacrylate (TMPT) and dipentaerythritol pentaacrylate (2P5A). In addition, in Japanese Laid-open Patent Publication No. 1987-178502, a material for dentistry is described which contains, as the main component, a diester compound represented by CH₂=CR₁COOR₂OCOR₃ (wherein R₁ is a hydrogen atom or an alkyl group, R₂ is an alkylene group and R₃ is an alkyl group). However, the composite resin, the hard crown resin, the quick-curing crown resin, the sealant and the adhesive are required to be (1) free from a strong foul odor, since they are directly put in a mouth. Furthermore, they are required to be free from irritation to a skin and a mucous membrane, since they are often brought into contact with dental pulp in pits of teeth. In addition, they must maintain strength under circumstances in a mouth, since they remain in the mouth for a long period of time after curing, and from this viewpoint, (3) polymers having high water absorption properties are inconvenient. Moreover, the restoration materials such as the denture plate and the denture plate lining agent are required to be (1) free from a strong foul odor and (2) free from irritation to a skin and a mucous membrane, since they are manipulated by hands of a dentist or a dental technician, or since they are directly brought into contact with an oral mucous membrane for the sake of molding. However, the above-mentioned monomers inconveniently cannot meet all of these requirements (1) to (3). For example, monomers such as MMA, EMA, BMA, HEMA, HD, 1G, 3G, TMPT and 2P5A cannot meet the above-mentioned requirements (1) and (2), and monomers such as H₂C=C(CH₃)COOC₂H₄OCOC₂H₅ and Bis-GMA cannot meet the above-mentioned requirements (3). Even if these monomers are combined, all of the aforesaid requirements cannot be satisfied. Therefore, the development of a composition by which these problems are solved is desired. The diester compounds described in the above Japanese Laid-open Patent Publication No. 1987-178502 are excellent in point of less stimulation, but they have perceptibly high water absorption properties. In consequence, their strength tends to deteriorate when they are used as dental materials, and what is worse, they are liable to color. In the case of the above restoration material, a monomer component is mixed with a polymer component at a suitable ratio, and the mixture is then placed in a predetermined mold or put in a mouth for the sake of molding. Afterwards, the material is taken out therefrom, and then polymerized at room temperature or under heating, thereby obtaining the restoration material. However, in the course of this molding, it is important that the material takes the state of the so-called dough stage for a suitable period of time. In short, the composition which is free from a strong foul odor and less irritant and which has a suitable period for dough stage is demanded. US-A-4 782 100 discloses a prothetic composition comprising a diester monomer, an organic polymer soluble in the monomer and a radical polymerization initiator. JP-A-59-109 508 describes a polyester resin composition prepared by using a dimethyl ester of a dimerized (meth)acrylic acid as a cross-linking component. SUMMARY OF THE INVENTION In view of such situations, the present inventors have intensively researched to solve the above-mentioned problems, and as a result, they have found that in a material for dentistry comprising a composition of monomers and a radical polymerization initiator which will be polymerized and cured when used, the monomer components are specific (meth)acrylate monomers which are less odorous and less stimulative, the water absorption of a polymer made therefrom is low, and a suitable period for dough stage is present. Thus, the present invention has been achieved on the basis of such a knowledge. That is, the present invention provides a material for dentistry comprising not less than 20% by weight of one or more monomers selected from the group consisting of a (meth)acrylate compound represented by the general formula (1) (wherein R₁ is a hydrogen atom or an alkyl group having 1 to 10 carbon atoms, R₂ is a straight-chain or branched alkylene group having 1 to 15 carbon atoms, and R₃ is an alkyl group having 1 to 15 carbon atoms), a (meth)acrylate compound represented by the general formula (2) (wherein R₄ is a hydrogen atom or an alkyl group having 1 to 10 carbon atoms R₅ is an alkylene group having 1 to 15 carbon atoms, and R₆ is an alkyl group having 1 to 15 carbon atoms), and a (meth)acrylate compound represented by the general formula (3) (wherein R₇ is a hydrogen atom or an alkyl group having 1 to 10 carbon atoms, R₈ is an alkylene group having 1 to 15 carbon atoms, R₉ is an alkylene group having 1 to 10 carbon atoms, and R₁₀ is an alkyl group having 1 to 15 carbon atoms). The material for dentistry containing the specific (meth)acrylate compound according to the present invention is less odorous and less irritant and has a lower water absorption as compared with conventional materials, and when used as the restoration material, it has a suitable period for dough stage. That is, in the direct treatment of the interior in the mouth of a patient by the use of the above-mentioned material, the patient can get rid of discomforts such as odor and irritation, and the curable material itself can be used for a long period of time even under severe wet conditions in the mouth, because of a less water absorption and thus an excellent dimensional stability, and because of an excellent strength, a high color stability and a good durability. In addition, the material of the present invention leads to improvements of safety and sanitation for a dentist or a dental technician, and operational efficiency. Therefore, it is fair to say that the material of the present invention has an extremely high practical value in the dental field. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is an IR chart of a methacrylate obtained in Synthesis Example 1, and Fig. 2 is an IR chart of a methacrylate obtained in Synthesis Example 2. DETAILED DESCRIPTION OF THE INVENTION Now, the present invention will be described mainly about cases where a material of the present case is used as restoration materials. However, the material for dentistry of the present invention can be suitably used as dental composite resins, crown resins, dental sealant and dental adhesives. Any compound represented by the general formula (1) can be used, so long as in the formula, R₁ is a hydrogen atom or a methyl group, R₂ is an alkylene group having 1 to 15 carbon atoms, and R₃ is an alkyl group having 1 to 15 carbon atoms. However, considering desired requirements of the material for dentistry such as a low odor, a low irritation, a low water absorption and a high mechanical strength of an obtained polymer, and a proper period for dough stage which is necessary in the case that the material is used as the binary restoration material, R₂ in the general formula (1) is an alkylene group having 1 to 15 carbon atoms but it may be a straight-chain methylene group or polymethylene group or a polymethylene group having a side chain. The R₂ group preferably has 1 to 7 carbon atoms. Furthermore, for the same reason, the R₃ in the general formula (1) is an alkyl group preferably having 1 to 7 carbon atoms. Accordingly, examples of the (meth)acrylate compound which can be particularly preferably used in the present invention are as follows: The (meth)acrylate compound represented by the above-mentioned general formula (1) of the present invention can be prepared from a specific unsaturated carboxylic acid [CH₂=C(R₁)-COOH] or its acid halide and an ether alcohol (HO-R₂-O-R₃) by an esterification reaction or alternatively by an ester exchange reaction between the unsaturated carboxylates. Similarly, considering the desired requirements of the material for dentistry, the alkyl group represented by the R₄ in the general formula (2) preferably has 1 to 7 carbon atoms, more preferably 1 to 4 carbon atoms. For the same reason, the R₅ in the general formula (2) is an alkylene group but it may be a straight-chain methylene group or polymethylene group or a polymethylene group having a side chain. The R₅ group preferably has 1 to 10 carbon atoms, more preferably 1 to 7 carbon atoms. Furthermore, for the same reason, the R₆ in the general formula (2) is an alkyl group preferably having 1 to 10 carbon atoms, more preferably 1 to 7. Accordingly, examples of the (meth)acrylate compound represented by the general formula (2) which can be particularly preferably used in the present invention are as follows: The (meth)acrylate compound represented by the above-mentioned general formula (2) regarding the present invention can be prepared by an esterification reaction between a specific unsaturated carboxylic acid [CH₂=C(R₄)-COOH] or its acid halide and a keto-alcohol [HO-R₅-C(O)-R₆] or alternatively by an ester exchange reaction between unsaturated carboxylates. Similarly, considering the desired requirements of the material for dentistry, each of R₈ and R₉ in the general formula (3) is an alkylene group but it may be a straight-chain methylene group or polymethylene group or a polymethylene group having a side chain. R₈ group preferably has 1 to 10 carbon atoms, more preferably 1 to 6 carbon atoms. For the same reason, R₉ group preferably has 1 to 7 carbon atoms, more preferably 1 to 4 carbon atoms. Furthermore, for the same reason as described above, R₁₀ in the general formula (3) is an alkyl group preferably having 1 to 10 carbon atoms, more preferably 1 to 7. On this account, typical examples of the (meth)acrylate compound represented by the general formula (3) which can be particularly preferably used in the present invention are as follows: The (meth)acrylate compound represented by the above-mentioned general formula (3) regarding the present invention can be prepared by an esterification reaction between a specific unsaturated carboxylic acid [CH₂=C(R₇)-COO-R₈-OCO-R₉-COOH] and an alkyl alcohol (R₁₀-OH), or alternatively by another reaction such as a reaction of an unsaturated alcohol [CH₂=C(R₇)-COO-R₈-OH) and an ester group-containing carboxylic acid (HOCO-R₉-COO-R₁₀), a reaction of an unsaturated carboxylic acid [CH₂=C(R₇)-COOH) and an ester group-containing alcohol (HO-R₈-OOC-R₉-COO-R₁₀), a reaction in which the above-mentioned carboxylic acid is replaced with a carboxylic acid halide, or an ester exchange reaction between unsaturated carboxylates. In manufacturing the material for dentistry of the present invention, a combination of one or more kinds of monomers selected only from the above-mentioned group can be used, but it is also possible to blend another monomer component therewith, if necessary, which is polymerizable with the specific (meth)acrylate compound represented by the general formula (1), (2) or (3), so long as the low odor and the low irritation can be maintained. Typical examples of such another kind of monomer include 2-ethylhexyl (meth)acrylate, lauryl (meth)acrylate, tridecyl (meth)acrylate, stearyl (meth)acrylate, cyclohexyl (meth)acrylate, n-hexyl (meth)acrylate, tetrahydrofurfuryl (meth)acrylate, ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, pentaethylene glycol di(meth)acrylate, hexaethylene glycol di(meth) acrylate, heptaethylene glycol di(meth)acrylate, octaethylene glycol di(meth)acrylate, nonaethylene glycol di(meth)acrylate, 1,3-butylene glycol di(meth)acrylate, propylene glycol di(meth)acrylate, 1,3-butanediol di(meth)acrylate, 1,4-butanediol di(meth)acrylate, 1,5-pentanediol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, 1,7-heptanediol di(meth)acrylate, 1,8-octanediol di(meth)acrylate, 1,9-nonanediol di(meth)acrylate, 1,10-decanediol di(meth)acrylate, neopentyl glycol di(meth)acrylate, 2,2-bis(4-methacryloyloxyphenyl)propane, 2,2-bis(4-methacryloyloxyethoxyphenyl)propane, 2,2-bis(4-methacryloyloxypolyethoxyphenyl)propane, 2,2-bis[4-(3-methacryloyloxy-2-hydroxypropoxy)phenyl]propane, di(methacryloyloxyethyl)trimethylhexamethylenediurethane, tetramethylolmethane tri(meth)acrylate, trimethylolpropane tri(meth)acrylate, trimethylolethane tri(meth)acrylate and tetramethylolmethane tetra(meth)acrylate. They can be used signly or in combination. Above all, polyfunctional methacrylates such as ethylene glycol dimethacrylate, triethylene glycol dimethacrylate, 1,6-hexanediol dimethacrylate, 2,2-bis(4-methacryloyloxyethoxyphenyl)propane, neopentyl glycol dimethacrylate and trimethylolpropane trimethacrylate are preferable as the other copolymerizable monomer components in view of mechanical strength of cured materials which will be obtained. The blend ratio of the (meth)acrylate compound represented by the general formula (1), (2) or (3) to the above-mentioned other copolymerizable monomer component depends upon the degree of the irritation of the other copolymerizable monomer component, and usually it can be selected suitably, so long as odor and irritation are maintained at a low level. Nevertheless, the above-mentioned blend ratio is such that the amount of the (meth)acrylate compound represented by the general formula (1), (2) or (3) is not less than 20% by weight, preferably not less than 30% by weight. In the case that the material for dentistry of the present invention is used as a restoration material, an organic polymer may be used which can be dissolved or swelled in the above-mentioned monomer. Typical examples of the organic polymer include polymethyl methacrylate (PMMA), polyethyl methacrylate (PEMA), MMA/EMA copolymer, MMA/BMA copolymer, polystyrene, polybutyl methacrylate, MMA/styrene copolymer, EMA/BMA copolymer, EMA/styrene copolymer, polyacrylonitrile, styrene/acrylonitrile copolymer, styrene/acrylonitrile/butadiene copolymer, polycarbonate resin, polyvinyl chloride, polyacrylates, polymethacrylates, polyester resins, polyethylene resin, polypropylene resin, silicone resins and fluorine-containing resin. Above all, preferable are PMMA, PEMA, MMA/EMA copolymer, MMA/BMA copolymer, polystyrene, polybutyl methacrylate, MMA/styrene copolymer, EMA/BMA copolymer, EMA/styrene copolymer, and mixtures of these polymers and other polymers, because they have a particularly proper solubility. Any particular restriction is not put on the molecular weight and the average particle diameter of this kind of polymer, but considering its solubility in the monomer component of the present invention and swell characteristics and mechanical strength of cured materials which will be obtained therefrom, the molecular weight of the polymer is preferably from 10,000 to 1,500,000, more preferably from 50,000 to 1,000,000, and the particle diameter of the polymer is preferably from 1 to 150 µm, more preferably from 10 to 100 µm. The blend ratio of the polymer component to all the monomer components can be selected from an extensive range, but in view of the mechanical strength of the cured articles, the amount of all the monomer components with respect to 10 parts by weight of the polymer component is preferably from 1 to 140 parts by weight (in other words, from 7.1 to 1,000 parts by weight with respect to 100 parts by weight of all the monomers), more preferably from 2 to 110 parts by weight, most preferably from 4 to 85 parts by weight. As a polymerization initiator used to obtain composite resins and restoration materials and as a curing agent used in the adhesive, there can be employed known compounds. In the case that heat curing is carried out, a substance which can thermally decompose and then initiate polymerization is used. Examples of such a substance include benzoyl peroxide, cumene hydroperoxide, t-butyl hydroperoxide, dicumyl peroxide, acetyl peroxide, lauroyl peroxide and azobisisobutyronitrile. Furthermore, in the case that polymerization/curing is carried out at ordinary temperature, there can be used, for example, a combination of a peroxide and an amine, a peroxide and a sulfinic acid, or a peroxide and a cobalt compound. When the polymerization initiators are used in combination, the composition may be divided into two parts, and one part of the composition may be blended with the peroxide and the other part may be blended with the amine, the sulfinic acid or the cobalt compound. The amount of the above-mentioned curing agent is preferably from 0.01 to 15% by weight, more preferably from 0.05 to 10% by weight, most preferably from 0.1 to 7% by weight with respect to the amount of the total monomers. In the case that polymerization/curing is carried out by means of the irradiation of ultraviolet light or visible light, any of known photosensitizers can be used. Examples of the suitable photosensitizer include benzoin alkyl ethers such as benzoin methyl ether, benzoin ethyl ether and benzoin propyl ether, α-diketones such as benzil, biacetyl and camphorquinone, and benzophenones such as benzophenone and methoxybenzophenone. When the above-mentioned photocuring means is employed, a reducing agent can be used in addition to the photosensitizer. Examples of the suitable reducing agent include amines such as aminobenzoic acid ester, toluidine, benzylamine and amino methacrylate. The amount of the photocuring agent to be used is preferably from 0.01 to 15% by weight, more preferably from 0.05 to 10% by weight, most preferably from 0.1 to 7% by weight. In the present invention, an inorganic filler can be additionally blended with the above-mentioned monomers, polymer component and polymerization/curing agent. Typical examples of the inorganic filler include oxides, hydroxides, chlorides, sulfates, sulfites, carbonates, phosphates, silicates and borates of elements in the groups I, II, III and IV of the periodic table and transition metals, mixtures thereof, and composite salts thereof. Typical examples of the inorganic filler include silicon dioxide, quartz powder, aluminum oxide, titanium oxide, barium sulfate, talc, glass powder, glass beads, glass fiber, a glass filler containing a barium salt or a strontium salt, silica gel, colloidal silica, carbon fiber, zirconium oxide, tin oxide and ceramic powder. The filler may be an untreated filler, a filler the surface of which is treated with a silane coupling agent or a titanate coupling agent, a filler coated with a polymer, or a filler composite containing an organic material prepared by the process described in Japanese Laid-open Patent Publication No. 1985-81116. The amount of the filler is preferably from 0.1 to 630% by weight (6.3 times), more preferably from 1 to 570% by weight, most preferably from 10 to 460% by weight with respect to the amount of the total monomers. As a molding method, any of known molding techniques can be utilized which are compression molding, cast molding and injection molding. In the material for dentistry of the present invention, a colorant, a polymerization inhibitor, an ultraviolet absorber, an oxidation stabilizer can be further blended, if necessary. The material for dentistry of the present invention can also be used as a dental material other than the restoration material. For example, the material for dentistry can be utilized as an adhesive or a sealant, which can be prepared from the (meth)acrylate compound represented by the general formula (1), (2) or (3) of the present invention, the same other monomer component copolymerizable with this compound as in the case of the above-mentioned restoration material, a polymerization initiator, and if necessary, a polymer, an inorganic filler, a colorant, a polymerization inhibitor, an ultraviolet absorber and an oxidation stabilizer. In addition, the material for dentistry of the present invention can also be utilized as a composite resin, a hard crown resin or a quick-curing crown resin, which can be prepared from the (meth)acrylate compound represented by the general formula (1), (2) or (3) of the present invention, the same other monomer component copolymerizable with this compound as in the case of the above-mentioned restoration material, a polymerization initiator, an inorganic filler. This inorganic filler is the same as used in the restoration material. If necessary, a polymer, a colorant, a polymerization inhibitor, an ultraviolet absorber, an oxidation stabilizer can also be blended therewith. Now, the present invention will be described in reference to examples. The (meth)acrylate compound of the present invention is not different at all from a conventional (meth)acrylate monomer for dentistry in point of reactivity except for being less odorous and less irritant. Thus, in the following examples, reference will be made mainly to embodiments of restoration materials. Examples 1 to 8 and Comparative Examples 1 to 4 As specific (meth)acrylate compounds represented by the general formula (1) according to the present invention, the following compounds were used, and an odor test, an irritation test and a polymer solubility test were then carried out. Procedures of the respective tests will be briefly described hereinafter, and the results of the tests will be set forth together in Table 1. Odor Test: Five unspecified testers aged 20 to 30 were selected, and the odor test was carried out in accordance with the following evaluation criterion by them. When the testers had different evaluations, the test was repeated again, until three or more of the testers had the same evaluation. Evaluation Criterion O ...... faintly odorous ▵ ...... weakly odorous X ...... strongly odorous Irritation Test : Five unspecified testers aged 20 to were selected. One drop of a sample was dropped on the 30 tongue tip of each tester, and after one minute, evaluation was made on the basis of the pain of the tongue tip in accordance with the following evaluation criterion. Evaluation Criterion: O ...... little painful ▵ ...... slightly painful X ...... very painful Polymer Solubility Test : A polyethyl methacrylate powder having an average molecular weight of 230 x 10³ and an average particle diameter of 25 µm was mixed with a (meth)acrylate compound used in the present invention so as to be a concentration of 20% by weight, and the mixture was then stirred. After 5 hours, evaluation was made in accordance with the following evaluation criterion by observing the state of each mixture. Evaluation Criterion: S ...... soluble SW ...... swelled IS ...... insoluble Compound Odor Test Irritation Test Polymer Solubility Test Example 1 A O-▵ ▵ S Example 2 B O-▵ O S Example 3 C O O S Example 4 D O O SW Example 5 E ▵ O S Example 6 F O-▵ ▵ S Example 7 G O O SW Example 8 H O O SW Comp. Ex. 1 methyl methacrylate X X S Comp. Ex. 2 ethyl methacrylate X X S Comp. Ex. 3 iso-propyl methacrylate X X SW Comp. Ex. 4 iso-butyl methacrylate X ▵ SW Examples 9 to 19 The same procedure as in Example 2 was effected except that mixtures of monomers were used as test compounds. The results are set forth in Table 2. Mixture of Monomers I II Example 9 Compound B cyclohexyl methacrylate Example 10 " lauryl methacrylate Example 11 " tridecyl methacrylate Example 12 " ethylene glycol dimethacrylate Example 13 " triethylene glycol dimethacrylate Example 14 " 1,6-hexanediol dimethacrylate Example 15 " 2,2-bis(4-methacryloyloxyethoxyphenyl)propane Example 16 " neopentyl glycol dimethacrylate Example 17 " trimethylolpropane trimethacrylate Example 18 " 1,6-hexanediol dimethacrylate Example 19 " " Mixing Weight Ratio (I/II) Odor Test Irritation Test Polymer Solubility Test Example 9 70/30 ▵ O S Example 10 " O O S Example 11 " O O S Example 12 " O O S Example 13 " O O S Example 14 " O O S Example 15 " O O S Example 16 " O O S Example 17 " O O S Example 18 50/50 O O S Example 19 40/60 O O S Examples 20 to 26, Comparative Examples 5 and 6 In each monomer solution shown in Table 3 was dissolved 0.5% by weight (with respect to the monomer solution) of benzoyl peroxide, and the solution was then placed in a glass tube and the latter was sealed up. Afterward, the glass tube was heated at 60°C for 24 hours, and successively it was further heated at 100°C for 24 hours in order to carry out polymerization, thereby obtaining a cured product. Next, for each cured product, performance was evaluated by the following procedure, and the results are set forth in Table 3. Performance Evaluation of Cured Product: Indirect Tensile (Diametral) Strength Each test piece was molded into the form of a 6 x 6 mm cylinder. An indirect tensile test was employed in which there was utilized the phenomenon that tensile stress was produced at right angles to compressive force by applying the compressive force in a diameter direction of the cylindrical test piece. The tensile strength was calculated in accordance with the following formula: Tensile strength = (2 x C)/(π x D x L) C = compression load, D = diameter of the test piece, and L = length of the test piece. Amount of Absorbed Water Each test piece was molded into the form of a 10 x 1 mm cylinder. The test piece was immersed in water at 37°C for 7 days, and an amount of absorbed water per unit area of the test piece was then measured. Examples 27 to 37 Each polymer powder shown in Table 4 was mixed with a monomer solution at a weight ratio of 30/70 in which 0.5% by weight (with respect to the monomer solution) of benzoyl peroxide was dissolved, and the mixture was then placed in a glass tube. The latter was then sealed up and heated at 60°C for 24 hours and successively heated at 100°C for 24 hours in order to carry out polymerization, thereby obtaining a cured product. Next, for the thus cured product, performance was evaluated by the same procedure as in Example 20. The results are set forth in Table 4. Properties of Polymers: The abbreviations, MW, PS and CP mean an average molecular weight, an average particle diameter and a composition of each copolymer, respectively. (*1) MW: 480 x 10³, PS: 15 µm (*2) MW: 230 x 10³, PS: 25 µm (*3) CP: 40/60, MW: 320 x 10³, PS: 20 µm (*4) CP: 40/60, MW: 60 x 10³, PS: 23 µm (*5) MW: 120 x 10³, PS: 30 µm (*6) MW: 360 x 10³, PS: 42 µm (*7) CP: 75/25, MW: 85 x 10³, PS:84 µm (*8) CP: 50/50, MW: 780 x 10³, PS: 12 µm (*9) CP: 50/50, MW: 520 x 10³, PS: 18 µm Examples 38 to 40 Each PEMA powder having an average particle diameter shown in Table 5 (average molecular weight = 230 x 10³) was mixed with a monomer mixture comprising compound B/1,6-hexanediol dimethacrylate = 36/64 (weight ratio) at a weight ratio of 2:1, and for the resulting mixture, a period for dough stage was then measured by the following test procedure. The results are set forth in Table 5. Test Procedure of Period for Dough Stage: Predetermined amounts of a polymer powder and a monomer solution are weighed in a weighing bottle (inner diameter 47 mm, height 2 cm), and after stirring for 20 seconds, the weighing bottle is covered with a lid of reinforced glass, followed by allowing the bottle to stand for 5 minutes. After stirring for 20 seconds again, the weighing bottle is covered with the reinforced glass lid and then allowed to stand for 5 minutes. The starting point of the period for dough stage is when it has been confirmed by touching the surface of the sample with a finger that the sample is not tacky any more. The sample is then separated from the wall surface of the weighing bottle by moving a metallic needle along the inside wall of the bottle. The end point of the period for dough stage is when the sample is inverted by piercing the stem of a spoon into the sample. A pot life is obtained from the formula of (the end point of the period for dough stage) - (the starting point of the period for dough stage). Average Diameter of PEMA Powder (µm) Period for Dough Stage (min) End Start Pot Life Example 38 95 77 24 53 Example 39 84 69 22 47 Example 40 78 46 20 26 Synthesis Example 1 In a 500-milliliter four-necked flask equipped with a condenser tube, a nitrogen-introducing pipe, a stirring rod and a thermocouple were placed 1 mole of methacrylic acid as an unsaturated carboxylic acid, 0.8 mole of thionyl chloride, a small amount of hydroquinone and 10 drops of DMF (dimethylformamide) as a catalyst, and they were then mixed and reacted for 15 hours in a water bath. Afterward, 0.8 mole of 4-hydroxy-2-butanone(γ-ketobutanol) was added to the reaction solution, and reaction was then carried out at a temperature of from 40 to 50°C for 3 hours. The reaction solution was dispersed in an excessive amount of water, and the resulting dispersion was then extracted with 400 ml of methylene chloride and the extract (the methylene chloride solution) was separated, washed with 300 ml of water twice, neutralized with sodium bicarbonate, washed, and acidified with hydrochloric acid. Anhydrous magnesium sulfate was added to the methylene chloride solution, and the solution was then dehydrated, followed by filtration. The solvent in the filtrate was vaporized under reduced pressure by the use of an aspirator, and finally the solvent was removed therefrom at 50°C for 30 minutes, so that the desired specific methacrylate compound was obtained In this case, the yield of the thus obtained compound was about 50 g. The IR chart of this compound is shown in Fig. 1. Other compounds represented by the general formula (2) could be synthesized by the same procedure as described above. Examples 41 to 45 The following compounds were used as specific (meth)acrylate compounds represented by the general formula (2) according to the present invention, and an odor test, an irritation test and a polymer solubility test were carried out in the same procedure as in Example 1. The results are set forth in Table 6. Compound Odor Test Irritation Test Polymer Solubility Test Example 41 I O-▵ O-▵ S Example 42 J O-▵ O S Example 43 K O O S Example 44 L O O S Example 45 M O O S Comp. Ex. 1 methyl methacrylate X X S Comp. Ex. 2 ethyl methacrylate X X S Comp. Ex. 4 isobutyl methacrylate X ▵ SW Examples 46 to 56 The same procedure as in Example 43 was effected except that compounds for tests were mixtures of monomers, and the results are set forth in Table 7. Mixture of Monomers I II Example 46 Compound K cyclohexyl methacrylate Example 47 " lauryl methacrylate Example 48 " tridecyl methacrylate Example 49 " ethylene glycol dimethacrylate Example 50 " triethylene glycol dimethacrylate Example 51 " 1,6-hexanediol dimethacrylate Example 52 " neopentyl glycol dimethacrylate Example 53 " 2,2-bis(4-methacryloxyphenyl)propane Example 54 " trimethylolpropane trimethacrylate Example 55 " 1,6-hexanediol dimethacrylate Example 56 " 1,6-hexanediol dimethacrylate Mixing Weight Ratio (I/II) Odor Test Irritation Test Polymer Solubility Test Example 46 70/30 O-▵ O S Example 47 " O O S Example 48 " O O S Example 49 " O O S Example 50 " O O S Example 51 " O O S Example 52 " O O S Example 53 " O O S Example 54 " O O S Example 55 50/50 O O S Example 56 40/60 O O S Examples 57 to 62 In each monomer solution shown in Table 8 was dissolved 0.5% by weight (with respect to the monomer solution) of benzoyl peroxide, and the solution was then placed in a glass tube and the latter was sealed up. Afterward, the glass tube was heated at 60°C for 24 hours, and successively it was further heated at 100°C for 24 hours in order to carry out polymerization, thereby obtaining a cured product. Next, for each cured product, performance was evaluated by the same procedure as in Example 20, and the results are set forth in Table 8. Examples 63 to 73 Each polymer powder shown in Table 9 was mixed with a monomer solution at a weight ratio of 30/70 in which 0.5% by weight (with respect to the monomer solution) of benzoyl peroxide was dissolved, and the mixture was then placed in a glass tube. The latter was then sealed up and heated at 60°C for 24 hours and successively heated at 100°C for 24 hours in order to carry out polymerization, thereby obtaining a cured product. Next, for the thus cured product, performance was evaluated by the same procedure as in Example 58. The results are set forth in Table 9. In this connection, properties of the polymer powders used in these examples were the same as in Examples 27 to 37. Examples 74 to 76 Each PEMA powder having an average particle diameter shown in Table 10 (average molecular weight = 230 x 10³) was mixed with a monomer mixture comprising Compound J/1,6-hexanediol dimethacrylate = 36/64 (weight ratio) at a ratio of 2:1, and for the resulting mixture, a dough stage time was then measured by the same procedure as in Example 38. The results are set forth in Table 10. Average Diameter of PEMA Powder (µm) Dough Stage Time (min) End Start Pot Life Example 74 84 64 13 51 Example 75 52 45 15 30 Example 76 25 31 16 15 Synthesis Example 2 In a 2,000-milliliter four-necked flask equipped with a cooling pipe, a nitrogen-introducing pipe, a stirring rod and a thermocouple was placed 115 g of the acrylic ester SA [CH₂=C(CH₃)COOC₂H₄OCOC₂H₄COOH) made by Mitsubishi Rayon Co., Ltd. as an unsaturated carboxylic acid, 500 ml of methanol, 2.5 g of concentrated hydrochloric acid and a small amount of hydroquinone, and they are mixed. Afterward, the mixture was allowed to stand at room temperature (abut 20°C) for 3 days. Next, 500 ml of water was added to the mixture to dilute it and then extracted with 200 ml of methylene chloride twice, and the extract was washed with 300 ml of water twice and with an aqueous saturated sodium hydrogen carbonate solution once, and dried over anhydrous magnesium sulfate, followed by filtration. The solution was concentrated under reduced pressure by the use of an aspirator, and finally, the solvent was distilled off at 50°C for 30 minutes, so that the desired specific methacrylate compound was obtained. In this case, the yield of the thus obtained compound was about 100.1 g. The IR chart of this product is shown in Fig. 2. Other compounds represented by the general formula (3) could be synthesized in accordance with the similar reaction by the use of a suitable unsaturated carboxylic acid and an alcohol. Examples 77 to 81 The following compounds were used as typical (meth)-acrylate compounds represented by the general formula (3) according to the present invention, and an odor test, an irritation test and a polymer solubility test were carried out in the same procedure as in Example 1. The results are set forth in Table 11. Compound Odor Test Irritation Test Polymer Solubility Test Example 77 N O-▵ O-▵ S Example 78 P O O S Example 79 Q O O SW Example 80 R O O S Example 81 S O O SW Comp. Ex. 1 methyl methacrylate X X S Comp. Ex. 2 ethyl methacrylate X X S Comp. Ex. 4 isobutyl methacrylate X ▵ SW Examples 82 to 92 The same procedure as in Example 78 was effected except that compounds for tests were mixtures of monomers, and the results are set forth in Table 12. Mixture of Monomers Example 82 Compound P cyclohexyl methacrylate Example 83 " lauryl methacrylate Example 84 " tridecyl methacrylate Example 85 " ethylene glycol dimethacrylate Example 86 " triethylene glycol dimethacrylate Example 87 " 1,6-hexanediol dimethacrylate Example 88 " neopentyl glycol dimethacrylate Example 89 " 2,2-bis(4-methacryloyloxyethoxyphenyl)propane Example 90 " trimethylolpropane trimethacrylate Example 91 " 1,6-hexanediol dimethacrylate Example 92 " 1,6-hexanediol dimethacrylate Mixing Weight Ratio (I/II) Odor Test Irritation Test Polymer Solubility Test Example 82 70/30 O-▵ O S Example 83 " O O S Example 84 " O O S Example 85 " O O S Example 86 " O O S Example 87 " O O S Example 88 " O O S Example 89 " O O S Example 90 " O O S Example 91 50/50 O O S Example 92 40/60 O O S Examples 93 to 98 In each monomer solution shown in Table 13 was dissolved 0.5% by weight (with respect to the monomer solution) of benzoyl peroxide, and the solution was then placed in a glass tube and the latter was sealed up. Afterward, the glass tube was heated at 60°C for 24 hours, and successively it was further heated at 100°C for 24 hours in order to carry out polymerization, thereby obtaining a cured product. Next, for each cured product, performance was evaluated by the same procedure as in Example 20, and the results are set forth in Table 13. Examples 99 to 109 Each polymer powder shown in Table 14 was mixed with a monomer solution at a weight ratio of 30/70 in which 0.5% by weight (with respect to the monomer solution) of benzoyl peroxide was dissolved, and the mixture was then placed in a glass tube. The latter was then sealed up and heated at 60°C for 24 hours and successively heated at 100°C for 24 hours in order to carry out polymerization, thereby obtaining a cured product. Next, for the thus cured product, performance was evaluated by the same procedure as in Example 94. The results are set forth in Table 14. In this connection, properties of the polymer powders used in these examples were the same as in Examples 27 to 37. Examples 110 to 112 Each PEMA powder having an average particle diameter shown in Table 15 (average molecular weight = 230 x 10³) was mixed with a monomer mixture comprising Compound P/1,6-hexanediol dimethacrylate = 36/64 (weight ratio) at a ratio of 2:1, and for the resulting mixture, a period for dough stage was then measured by the same procedure as in Example 38. The results are set forth in Table 15. Average Diameter of PEMA Powder (µm) Period for Dough Stage (min) End Start Pot Life Example 110 84 75 22 53 Example 111 52 49 19 30 Example 112 25 36 18 18

Claims: A material for dentistry comprising not less than 20 % by weight of one or more monomers selected from the group consisting of a (meth)acrylate compound represented by the general formula (1) (wherein R₁ is a hydrogen atom or an alkyl group having 1 to 10 carbon atoms, R₂ is a straight-chain or branched alkylene group having 1 to 15 carbon atoms, and R₃ is an alkyl group having 1 to 15 carbon atoms), a (meth)acrylate compound represented by the general formula (2) (wherein R₄ is a hydrogen atom or an alkyl group having 1 to 10 carbon atoms, R₅ is an alkylene group having 1 to 15 carbon atoms, and R₆ is an alkyl group having 1 to 15 carbon atoms), and a (meth)acrylate compound represented by the general formula (3) (wherein R₇ is a hydrogen atom or an alkyl group having 1 to 10 carbon atoms, R₈ is an alkylene group having 1 to 15 carbon atoms, R₉ is an alkylene group having 1 to 10 carbon atoms, and R₁₀ is an alkyl group having 1 to 15 carbon atoms). The material for dentistry according to claim 1, further comprising another monomer copolymerizable with said monomer, represented by any one of the general formulae (1) to (3). The material for dentistry according to claim 2, further comprising an organic polymer which is soluble or swelling in said monomer and which has a particle diameter of 1 to 150 µm, an amount of said organic polymer being from 7.1 to 1,000 parts by weight with respect to 100 parts by weight of the total monomers. The material for dentistry according to claim 2, further comprising a polymerization curing agent selected from the group consisting of combinations of a peroxide and an amine, a peroxide and a sulfinic acid, and a peroxide and a cobalt compound, an amount of said polymerization curing agent being in a range of 0.01 to 15% by weight with respect to the weight of the total monomers. The material for dentistry according to claim 2, further comprising a photosensitizer selected from the group consisting of benzoin alkyl ethers, α-diketones and benzophenones, an amount of said photosensitizer being in a range of from 0.01 to 15% by weight with respect to the weight of said monomer. The material for dentistry according to any of claims 2 to 5, further comprising an inorganic filler, an amount of said inorganic filler being in a range of from 0.1 to 630 parts by weight with respect to 100 parts by weight of the total monomers. The material for dentistry according to claim 1, wherein said compound represented by said general formula (1) is a compound selected from the group consisting of a compound in which R₁ is -CH₃, R₂ is -CH₂CH₂-and R₃ is -CH₃, a compound in which R₁ is -CH₃, R₂ is -CH₂CH₂- and R₃ is -CH₂CH₃, a compound in which R₁ is -CH₃, R₂ is -CH₂CH₂- and R₃ is -(CH₂)₃-CH₃, a compound in which R₁ is -CH₃, R₂ is -CH(CH₃)-CH₂- and R₃ is -(CH₃)₃-CH₃, a compound in which R₁ is -CH₃, R₂ is -CH(CH₃)-CH₂- and R₃ is -CH₃, a compound in which R₁ is -CH₃, R₂ is -CH(CH₃)-CH₂- and R₃ is -CH₂CH₃, a compound in which R₁ is -CH₃, R₂ is -(CH₂)₄- and R₃ is -CH₂CH₃, and a compound in which R₁ is -CH₃, R₂ is -(CH₂)₆- and R₃ is-CH₂CH₃. The material for dentistry according to claim 1, wherein said compound represented by said general formula (2) is a compound selected from the group consisting of a compound in which R₄ is -CH₃, R₅ is -(CH₂)₂-and R₆ is -CH₃, a compound in which R₄ is -CH₃, R₅ is -(CH₂)₂- and R₆ is -CH₂CH₃, a compound in which R₄ is -CH₃, R₅ is -(CH₂)₄- and R₆ is -CH₂CH₃, a compound in which R₄ is -CH₃, R₅ is -(CH₂)₆- and R₆ is -CH₂CH₃, and a compound in which R₄ is -CH₃, R₅ is -(CH₂)₄ and R₆ is -(CH₂)₃-CH₃. The material for dentistry according to claim 1, wherein said compound represented by said general formula (3) is a compound selected from the group consisting of a compound in which R₇ is -CH₃, R₈ is -(CH₂)₂-, R₉ is -CH₂- and R₁₀ is -CH₃, a compound in which R₇ is -CH₃, R₈ is -(CH₂)₂-and R₉ is -(CH₂)₂- and R₁₀ is -CH₃, a compound in which R₇ is -CH₃, R₈ is -(CH₂)₄-, R₉ is -(CH₂)₂- and R₁₀ is -CH₃, a compound in which R₇ is -CH₃, R₈ is -(CH₂)₂-, R₉ is -(CH₂)₂- and R₁₀ is -CH₂CH₃, and a compound in which R₇ is -CH₃, R₈ is -(CH₂)₂-, R₉ is -(CH₂)₂- and R₁₀ is -(CH₂)₃-CH₃. The material for dentistry according to claim 2, wherein said other monomer copolymerizable with said monomer represented by any one of said general formulae (1) to (3) is a polyfunctional methacrylate selected from the group consisting of ethylene glycol dimethacrylate, triethylene glycol dimethacrylate, 1,6-hexanediol dimethacrylate, 2,2-bis(4-methacryloyloxyethoxyphenyl)propane, neopentyl glycol dimethacrylate and trimethylolpropane trimethacrylate. The material for dentistry according to claim 3, wherein said organic polymer which is soluble or swelling in said monomer represented by any one of the general formulae (1) to (3) is a polymer selected from the group consisting of polymethyl methacrylate, polyethyl methacrylate, polybutyl methacrylate, polystyrene, methyl methacrylate/ethyl methacrylate copolymer, methyl methacrylate/butyl methacrylate copolymer, methyl methacrylate/styrene copolymer, ethyl methacrylate/butyl methacrylate copolymer, ethyl methacrylate/styrene copolymer, blended polymer compound of polymethyl methacrylate and polyethyl methacrylate, and blended polymer compound of polyethyl methacrylate and polybutyl methacrylate.

Inventors: ATARASHI JUNKO C O CENTRAL RES, IGE HITOSHI C O CENTRAL RESEAR, KOBAYASHI MASAO C O CENTRAL RE, MUKAI NOBUHIRO C O CENTRAL RES, YAMAMOTO NAOKI C O CENTRAL RES, ATARASHI, JUNKO, C/O CENTRAL RESEARCH LABORATORIE, IGE, HITOSHI, C/O CENTRAL RESEARCH LABORATORIES, KOBAYASHI, MASAO, C/O CENTRAL RESEARCH LABORATORIE, MUKAI, NOBUHIRO, C/O CENTRAL RESEARCH LABORATORIES, YAMAMOTO, NAOKI, C/O CENTRAL RESEARCH LABORATORIES
Applicants: MITSUBISHI RAYON CO, MITSUBISHI RAYON CO., LTD
Application year: 1990
Main classification: A61K6
IPC codes: C07C69, A61K6