Resin composition and packaging material for photosensitive materials

Abstract: A resin composition containing a light-shielding material and vitamin E and packaging materials (1a) formed thereof. The light-shielding ability is increased by blending vitamin E. Laminated films where at least one thermoplastic resin film is interposed between two high Young's modulus films. The laminated films are excellent in tear strength, tensile strength, heat seal strength and bursting strength, and always secure light-shielding, moistureproofness and gas barrier. They can be used as a single-sheet bag for packaging a heavy product having sharp edges.

Description: This invention relates to a resin composition and packaging materials for photosensitive materials such as photographic photosensitive materials. Resin compositions for packaging materials for photographic photosensitive materials are disclosed in JP-A-63-217548 and JP-A-1-243050 and the like, resin compositions for films for photographic photosensitive materials are disclosed in JP-A-58-132555, and spools for a photographic film are disclosed in US-A-4,796,823. In the above materials, the light-shielding ability was secured by blending a light-shielding material such as carbon black. Then, heretofore, when the light-shielding ability of the films for photographic photosensitive materials was raised, the blending amount of the light-shielding material was increased. However, the increase of the blending amount of the light-shielding material resulted to increase the occurrence of lumps and fish eyes and to degrade physical strength, moldability, heat sealing properties and the like. While, since the size and form of the spool for a photographic film are stipulated by JIS, a great quantity of a light-shielding material was blended in order to secure the light-shielding ability at thin portions. As a result, the quantity of the light-shielding material at thick portions was too much. Incidentally, as to the materials which lose the value by exposing to light, such as photographic photosensitive materials, packaging materials capable of shielding from light completely are used. The packaging materials are necessary to have various properties such as resistance to the occurrence of pinholes, sealability, moistureproofness, gas barrier, sufficient physical strength and antistatic ability capable of preventing spark discharge as well as the above light-shielding ability. As conventional packaging materials, there were a packaging material composed of an aluminum foil on both sides of which flexible sheet(s) or LDPE resin film(s) containing carbon black were laminated, and a packaging material laminated with a light-shielding film containing more than 1 wt. % of a light-shielding material and more than 50 wt. % of L-LDPE resin. An example is shown in Figure 19 which consisted of a polyethylene resin film 21a containing a light-shielding material and an aluminum vacuum-metallized biaxially stretched nylon resin film 22 composed of a biaxially stretched nylon resin film 23 provided with an aluminum vacuum deposited membrane 19 laminated thereto through an adhesive layer 2. However, when they were used for packaging a roll or sheets of a heavy photographic photosensitive material having sharp edges, pinholes or elongation occurred by the sharp edges. Therefore, in order to secure light-shielding, the packaging bag was necessary to be made a double-sheet bag being expensive. Another packaging material was composed of an aluminum foil and two light-shielding L-LDPE resin film laminated on both sides of the aluminum foil (JP-A-60-189438). The packaging material was also used as a double-sheet bag in order of secure qualities of the packaged materials. The inventor disclosed a packaging material having a double layer-coextruded film such as composed of a L-LDPE resin film and a polypropylene resin film as a packaging material capable of securing the qualities even by a single-sheet bag (US-A-4,780,357). An example of the packaging material is shown in Figure 20 which consisted of a light-shielding coextruded double layer film 24a consisting of a HDPE resin film 25a containing a light-shielding material and a L-LDPE resin film 26a containing a light-shielding material and an aluminum vacuum-metallized biaxially stretched nylon resin film 22 laminated thereto through an adhesive layer 2. However, in the case of the above packaging material, light-shielding and moistureproofness could not be secured by the shaking or shock during exportation or long transportation, by worsening of handling of freight such as dropping or throwing out in courier or air cargo, by the increase of impact force by the space in a carton box or corrugated boared box, or the like. That is, in the case that the packaged material was sheets, pinholes and thinning of light-shielding layers occurred by the sharp edges or corners, and in the case that the packaged material was a roll, breakage, pinholes or abrasion occurred by the sharp edges of the roll or the corners of the core. An object of the invention is to provide a resin composition capable of fortifying light-shielding ability without increasing light-shielding materials. Another object of the invention is to provide a packaging material for photographic photosensitive materials of which the light-shielding ability is fortifyed without increasing light-shielding materials. The inventor unexpectedly found that, when vitamin E was added to a resin composition together with a light-shielding material, the light-shielding ability was improved by more than 20 % compared with the case not adding vitamin E. Thus, the present invention provides a resin composition comprising a thermoplastic resin, a light-shielding material and vitamin E, and a packaging material for photographic photosensitive materials comprising a thermoplastic resin, a light-shielding material and vitamin E. Figures 1 through 8 are partially sectional views of packaging materials embodying the invention containing vitamin E. Figure 9 is a front view of a spool for a photographic film to which the invention containing vitamin E is applicable. Figure 10 is a sectional view thereof. Figures 19 and 20 are partially sectional views indicating layer constructions of conventional packaging materials. A resin composition of the invention comprises a thermoplastic resin, a light-shielding material and vitamin E. The thermoplastic resin is selected according to the article to be formed or the like and preferred thermoplastic resins include polyethylene resin, polypropylene resin, ethylene-copolymer resins, modified polyolefin resins, polystyrene resin, ABS resin, polyvinyl chloride resin, polyester resin, polyamide resin and polyacetal resin. The content of the thermoplastic resin is 50 to 99.85 wt. %, preferably 70 to 99.5 wt. %. The light-shielding material is added in order to secure light-shielding ability by absorbing or reflecting light. Examples of the light-shielding materials are described below. Inorganic Compounds: Oxides ... e.g. silica, diatomaceous earth, alumina, titanium oxide, iron oxide, zinc oxide, magnesium oxide, antimony oxide, barium ferrite, strontium ferrite, beryllium oxide, pumice, pumice balloon, alumina fiber. Hydroxides ... e.g. aluminum hydroxides, magnesium hydroxides, basic magnesium carbonate. Carbonates ... e.g. calcium carbonate, magnesium carbonate, dolomite. Sulfates, sulfites ... e.g. calcium sulfate, barium sulfate, ammonium sulfate, calcium sulfite. Silicates ... e.g. talc, clay, mica, asbestos, glass fiber, glass balloon, glass bead, calcium silicate, montmorillonite, bentonite. Carbons ... e.g. carbon black, graphite, carbon fiber, carbon hollow bead. Others ... e.g. iron powder, copper powder, lead powder, tin powder, stainless steel powder, pearl pigment, aluminum powder, molybdenum sulfide, boron fiber, silcon carbide fiber, brass fiber, potassium titanate, lead titanate zirconate, zinc borate, barium metaborate, calcium borate, sodium borate, aluminum paste. Organic Compounds: e.g. wood flour such as pine, oak and sawdust, husk fiber such as almond, peanut and chaff colored various fibers such as cotton and jute, paper piece, cellophane piece, nylon fiber, polypropylene fiber, starch, aromatic polyamide fiber. Among them, preferred light-shielding materials make opaque, and light-absorptive carbon black, titanium nitride and graphite are particularly preferred because of being excellent in heat resistance and light resistance and being relatively inactive. Carbon blacks are divided into gas black, oil furnace black, channel black, anthracene black, acetylene black, Ketchen carbon black, thermal black, lamp black, vegetable black and animal black according to their origin. Among these, oil furnace carbon black is preferable in terms of light-shielding character, cost and improvement of properties. On the other hand, since acetylene black and Ketschen carbon black have an antistatic character, they are also preferable, though they are expensive. They may be blended to the oil furnace black in order to improve its character. Particularly preferable carbon black for the packaging material for photographic photosensitive materials is the oil furnace carbon black having a pH of 6 to 9, a mean particle size of 10 to 120 mµ, a volatile components content of less than 2 % and an oil absorption value of more than 50 ml/100 g in view of no occurrence of fogging, rare ocurrence of photosensitivity deviation, great light-shielding ability and rare occurrence of lumps of carbon black and fish eyes. As the form of the light-shielding material, there are e.g. powder coloring agent, paste coloring agent, wet coloring agent, masterbatch, dye, colored pellets. Though, there are various blending methods, the masterbatch method is preferred in view of cost and the contamination of the working place. JP-B-40-26196 discloses a method of making a masterbatch of polymer-carbon black by dissolving the polymer in an organic solvent and dispersing the carbon black into the solution. JP-B-43-10362 discloses another method of making a masterbatch by dispersing the carbon black into polyethylene. Vitamin E is a fat-soluble vitamin having an alias of tocopherol, and includes α-tocopherol, β-tocopherol, γ-tocopherol and δ-tocopherol. The other tocol derivatives having vitamin E activity such as 5,7-dimethyltocol, 7-methyltocol and 5-methyltocol are also included. A suitable content of vitamin E is 0.005 to 1 wt. %, and 0.02 to 0.5 wt. % is preferred. When the content is less than 0.005 wt. %, the blending effect is insufficient. While, when the content is beyond 1 wt. %, a further effect obtained by the blending is little. Moreover, the excess amount affects adversely photographic photosensitive materials. The content of the light-shielding material is 0.01 to 30 wt. %, preferably 0.05 to 15 wt. %. To add a lubricant is preferred in order to improve film-forming ability and the like. Examples of the lubricants are: Oleic amide lubricants; e.g. "ARMOSLIP-CP" (Lion Akzo Co., Ltd.), "NEWTRON" and "NEWTRON E-18" (Nippon Fine Chemical Co., Ltd.), "AMIDE-O" (Nitto Kagaku K.K.), "DIAMID O-200" and "DIAMID G-200" (Nippon Kasei Chemical Co., Ltd.), "ALFLOW E-10" (Nippon Oil and Fats Co., Ltd.). Erucic amide lubricants; e.g. "ALFLOW P-10" (Nippon Oil and Fats Co., Ltd.). Stearic amide lubricants; e.g. "ALFLOW S-10" (Nippon Oil and Fats Co., Ltd.), "NEWTRON 2" (Nippon Fine Chemical Co., Ltd.), "DIAMID 200" (Nippon Kasei Chemical Co., Ltd.). Bis fatty amide lubricants; e.g. "BISAMIDE" (Nitto Kagaku K.K.), "DIAMID-200 BIS" (Nippon Kasei Chemical Co., Ltd.), "ARMOWAX-EBS" (Lion Akzo Co., Ltd.), Silicone lubricants; e.g. dimethylpolysiloxanes, etc. (Sinetsu Chemical Co., Ltd., Toray Silicone Co., Ltd.). Alkylamine lubricants; e.g. "ELECTROSTRIPPER TS-2" and "ELECTROSTRIPPER TS-3" (Kao Corp.). Hydrocarbon lubricants; e.g. liquid paraffin, natural paraffin, microwax, synthetic paraffin, polyethylene wax, polypropylene wax, chlorinated hydrocarbon, fluorocarbon. Fatty acid lubricants; e.g. higher fatty acids preferably more than C 12 , hydroxy fatty acids. Ester lubricants; e.g. fatty acid lower alcohol esters, fatty acid polyol esters, fatty acid polyglycol esters, fatty acid fatty alcohol esters. Alcohol lubricants; e.g. polyols, polyglycols, polyglycerols. Metallic soap; e.g. metal salts such as Li, Mg, Ca, Sr, Ba, Zn, Cd, Al, Sn, Pb salts of higher fatty acids such as lauric acid, stearic acid, ricinoleic acid naphthenic acid, oleic acid. A suitable content of the lubricant is 0.005 to 5 wt. %. In the case of fatty amide lubricants excellent in the improvement of slipping character and liable to bleeding out. To add an antioxidant is preferred in order to prevent resin yellowing and the like. Suitable antioxidants are described below. Phenol Antioxidants: e.g. 6-t-butyl-3-methylphenol derivatives, 2,6-di-t-butyl-p-cresol-t-butylphenol, 2,2'-methylenebis-(4-ethyl-6-t-butylphenol), 4,4'-butylidenebis(6-t-butyl-m-cresol), 4,4'-thiobis(6-t-butyl-m-cresol), 4,4-dihydroxydiphenylcyclohexane, alkyl group-induced bisphenol, styrene group-induced phenol, 2,6-di-t-butyl-4-methylphenol, n-octadecyl-3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate, 2,2'-methylenebis(4-methyl-6-t-butylphenol), 4,4'-thiobis(3-methyl-6-t-butylphenol, 4,4'-butylidenebis(3-methyl-6-t-butylphenol), stearyl-β-(3,5-di-4-butyl-4-hydroxyphenyl)propionate, 1,1,3-tris(2-methyl-4-hydroxy-5-t-butylphenyl)butane, 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene, tetrakis [methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl) propionate]methane. Ketone-Amine Condensae Antioxidants: e.g. 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline, polymers of 2,2,4-trimethyl-1,2-dihydroquinoline, trimethyldihydroquinoline derivatives. Arylamine Antioxidants: e.g. Phenyl-α-naphthylamine, N-phenyl-β-naphthylamine, N-phenyl-N'-isopropyl-p-phenylenediamine, N,N'-diphenyl-p-phenylenediamine, N,N'-di-p-naphthyl-p-phenylenediamine, N-(3'-hydroxybutylidene)-1-naphtylamine. Imidazole Antioxidants: e.g. 2-mercaptobenzoimidazole, zinc salt of 2-mercaptobenzoimidazole, 2-mercaptomethylbenzoimidazole. Phosphite Antioxidants: e.g. Alkyl-induced arylphosphite, diphenylisodecylphosphite, sodium phosphite salt of tris(nonylphenyl)phosphite, trinonylphenylphosphite, triphenylphosphite. Thiourea Antioxidants: e.g. Thiourea derivatives, 1,3-bis(dimethylaminopropyl)-2-thiourea. Other Antioxidants: Those useful for air oxidation, such as dilauryl thiodipropionate. Preferable antioxidants are phenol antioxidants, and particularly effective antioxidants are e.g. BHT, low volatile high molecular weight phenol antioxidants (e.g. "Irganox 1010", "Irganox 1076", trade names of Ciba-Geigy A.G., "Topanol CA", trade name of I.C.I..), dilaurylthiodipropionate, distearylthiodipropionate, dialkylphosphate. Two or more antioxidants may be combined. A suitable content of the antioxidant is 0.005 to 1 wt. %. When the content is less than 0.005 wt. %, the blending effect is small. While, when the content is beyond 1 wt. %, a further effect by the blending is small. Moreover, the photographic film is adversely influenced by the antioxidant, which results in the occurrence of phenomena. Such as fogging and deviation of photographic sensitivity. An antiblocking agent may be added to the resin composition of the invention in order to prevent blocking. Suitable antiblocking agents are inorganic antiblocking agents such as silica calcium silicate, aluminum silicate, talc and calcium carbonate and organic antiblocking agents such as higher fatty acid polyvinyl esters, dicarboxylic acid ester amides, n-octadecylurea and N,N'-dioleyloxamide. To blend a surfactant having antiblocking effect and antistatic effect is preferred. Such a surfactant includes cationic surfactants such as primary amine salts, tertiary amine salts, quanternary ammonium salts and pyridine derivatives, anionic surfactants such as fatty acid metal salts, alkyl sulfate ester salts, alkyl naphthalene sulfonate salts and succinate ester sulfonate salts, nonionic surfactants such as partial fatty acid esters of polyols, ethylene oxide adducts of fatty alcohols, ethylene oxide adducts of fatty acids, ethylene oxide adducts of fatty amino compounds or fatty amides, ethylene oxide adducts of alkylphenols and ethylene oxide adducts of alkylnaphthols, and ampholytic surfactants such as carboxylic acid derivatives and imidazoline derivatives. Various additives may be added in order to improve various properties. Examples of the additives are described below. (1) Plasticizer; e.g. phthalic acid esters, glycol esters, fatty acid esters, phosphoric acid esters. (2) Stabilizer; e.g. lead compounds, cadmium compounds, zinc compounds, alkaline earth metal compounds, organic tin compounds. (3) Flame retardant; e.g. phosphoric acid esters, phosphoric acid ester halides, halides, inorganic materials, polyols containing phosphor. (4) Filler; e.g. alumina, kaolin, clay, calcium carbonate, mica, talc, titanium dioxide, silica. (5) Reinforcing agent; e.g. glass lobing, metallic fiber, glass fiber, glass milled fiber, carbon fiber. (6) Blowing agent; e.g. inorganic blowing agents (ammonium carbonate, sodium hydrogen carbonate), organic blowing agents (nitroso compounds, azo compounds). (7) Vulcanizing agent; e.g. vulcanization accelerator, acceleration assistant. (8) Deterioration preventing agent; e.g. ultraviolet absorber, metal deactivator, peroxide decomposing agent. (9) Coupling agent; e.g. silane compounds, titanium compounds, chromium compounds, aluminum compounds. (10) Nucleating agent; organic nucleating agents (e.g. dibenzylidene sorbitol compounds), inorganic nucleating agents (e.g. calcium carbonate) (11) Various thermoplastic resins, rubbers The above resin composition is used for various thermoplastic resin articles requiring light-shielding such as packaging materials for photographic photosensitive materials. Examples of the packaging materials for photographic photosensitive materials are: Injection molding light-shielding containers, such as magazines, instant photographic film packs, shells for disc film, floppy discs or the like, cassettes, cartridges, container bodies for photographic film cartridge and caps therefore, hinged cases for microfilms, instant photographic films or video tape recorder, and the like. Light-shielding members of magazines for light-room loading, such as light-shielding teremp clothes, curtains, light-shielding films and light-shielding pads, for miniture laboratory magazine, for magazine for phototype setting, for instant photographic film pack or the like. Various light-shielding films including single layer films, coextruded multilayer films and laminated films, light-shielding coating layer (e.g. extrusion coating layer, solution coating layer) light-shielding papers, support materials, light-shielding bags. Other light-shielding tapes, light-shielding adhesives, light-shielding hot melt adhesives, light-shielding foamed sheets, light-shielding paper boxes. Among them, in the cases of photographic film spools, containers for a photographic film cartridge and various cases, they are formed of the resin composition of the invention by injection molding. Suitable thermoplastic resins for photographic film spools include polystyrene resin, synthetic rubber-blended polystyrene resin, synthetic rubber-copolymerized polystyrene resin, homopolypropylene resin, propylene-α-olefin block copolymer resin, propylene-α-olefin random copolymer resin, high density polyethylene resin, ethylene-α-olefin copolymer resin, polyamide resin, acrylonitrile-styrene-butadiene copolymer resin, blend resins containing one or more of the above resins, various modified resin of them containing various modifiers or additives. In the cases of light-shielding films, they include single layer films comprising the resin composition of the invention, coextruded multilayer films and laminated films composed of the single layer film or coextruded multilayer film and flexible sheet(s) laminated thereto directly or through an adhesive layer. Suitable thermoplastic resins for light-shielding films include ethylene-α-olefin copolymer resins, low density polyethylene resin, medium density polyethylene resin, high density polyethylene resin, various polypropylene resins, ethylene-vinyl acetate copolymer resin, ethylene-ethyl acrylate copolymer resin, polyamide resin, polyester resin, modified polyolefin resins, ionomers and blend resins containing one or more of the above resins. As the flexible sheets, there are thermoplastic resin films such as various polyethylene resin films, ethylene copolymer resin films, polypropylene resin films, polyvinyl chloride resin films, polyvinylidene chloride resin films, polyamide resin films, polycarbonate resin films, polyester resin films, their modified resin films and their stretched films. Other suitable flexible sheets include metallized fims such as aluminum-metallized films, cellulose acetate films, cellophane films, regenerated cellulose films, polyvinyl alcohol films, papers, metal foils such as aluminum foil and nonwoven fabric. Preferable flexible sheets are various papers having an areal weight of 20 to 400 g/m 2 such as unbleached kraft paper, semibleached kraft paper, bleached kraft paper, twisting paper, Clupak paper, Duostress paper, white cardboard, photo base paper, pure white roll paper, coated paper, simili and glassine paper. In the above resin composition, the light-shielding ability increases by blending vitamin E together with a light-shielding material. As a result, the blending amount of the light-shielding material can be decreased to improve physical strength of packaging materials, to reduce the generation of lumps and fish eyes, to improve moldability and heat sealing properties and to reduce manufacturing cost. Moreover, resin degradation can be prevented by the oxidation inhibition action of vitamin E without adverse influence upon photographic properties of the packaged articles. Representative embodiments of the packaging materials formed using the above resin composition are illustrated in Figures 1 through 10. The packaging material of Figure 1 is composed of a single layer light-shielding film 1a containing vitamin E. The packaging material of Figure 2 is composed of the vitamin E-containing light-shielding film 1a of Figure 1 and a flexible sheet 3 laminated thereto through an adhesive layer 2a containing a light-shielding material. The packaging material of Figure 3 is a coextruded double layer film Ia composed of the vitamin E-containing light-shielding film 1a and a thermoplastic resin film 4a containing a light-shielding material. The packaging material of Figure 4 is the same as that of Figure 3, except that the thermoplastic resin film 4 does not contain a light-shielding material. The packaging material of Figure 5 is composed of a flexible sheet 3 and the vitamin E-containing light-shielding film 1a laminated thereto by coating. The packaging material of Figure 6 is composed of the packaging material of Figure 3 and a flexible sheet laminated to the side of the light-shielding thermoplastic resin film 4a through an adhesive layer 2. The packaging material of Figure 7 is a coextruded triple layer film IIa composed of the vitamin E-containing light-shielding film 1a, an intermediate layer 5a containing a light-shielding material and a thermoplastic resin film 4a containing a light-shielding material disposed in this order. The packaging material of Figure 8 is composed of the coextruded film of Figure 7 wherein the intermediate layer 5 does not contain a light-shielding material and a flexible sheet 3 laminated to the side of the light-shielding thermoplastic resin film 4a through an adhesive layer 2. The packaging material of Figures 9 and 10 is a spool composed of a core 6, flanges 7,7 and a slot for interting the leading end of photographic film. Each film, layer or sheet of the above packaging materials for photosensitive materials may contain a lubricant in order to improve film-forming ability, antiblocking ability, antistatic ability and the like. The lubricant can be selected from oleic amide lubricants, erucic amide lubricants, stearic amide lubricants, bis fatty amide lubricants, silicone lubricants, alkylamine lubricants, hydrocarbon lubricants, fatty acid lubricants, ester lubricants, alcohol lubricants and metallic soaps, mentioned previously. Various additives may be added to the packaging materials for photosensitive materials of the invention. Examples of the additives are plasticizers, stabilizers, fire retardants, fillers, reinforcing agents, blowing agents, vulcanizing agents, deterioration preventing agents and various thermoplastic resins and rubbers, mentioned previously. Moreover, the packaging material may contain a coupling agent such as a silane compound, a titanate compound, a chromium compound or an aluminum compound, and a nucleating agent such as an organic nucleating agent e.g. a dibenzylidenesorbitol compound or an inorganic nucleating agent e.g. calcium carbonate. The packaging material for photosensitive materials of the invention is suitable for packaging the following photosensitive materials. Silver halide photographic photosensitive materials; X-ray films, films for printing, monochrome and color photographic printing papers, color films, master papers for printing, DTR photosensitive materials, films and papers for computerized type-setting system, microfilms, films for movie, self-developing type photographic photosensitive materials, direct positive films and papers, etc. Diazonium photographic photosensitive materials; 4-morpholinobenzene diazonium microfilms, microfilms, copying films, form plates for printing, etc. Azide, diazide photographic photosensitive materials containing parazidobenzoate, 4,4'-diazidostilbene, etc., such as copying films and form plates for printing etc. Quinone diazide photographic photosensitive materials; photosensitive materials containing ortho-quinone diazide compounds or ortho-naphthoquinone diazide compounds, such as benzoquinone-(1,2)-diazido-(2)-4-sulfonic acid phenyl ether, such as form plates for printing, copying films and contact printing film, etc. Photo polymers; photosensitive materials, form plates for printing, contact printing films, containing vinyl compound monomer, etc. Polyvinyl cinnamate esters; printing films, photoresists for IC, etc. Moreover, the packaging material of the invention is also applicable to various photosensitive materials degraded or denatured by light, oxygen, sulfur dioxide gas or the like, such as foods including peanuts with butter, margarine, snacks, relishs, cakes, teas and lavers, medicines including powder and granular medicines placed in a bag for stomach and bowels and for cold, dyes, pigments, photographic developing agent, photographic fixing agent, toners and the like. EXAMPLES Example I The resin composition of Example I was composed of 92.0 wt. % of ethylene-4-methylpentene-1 copolymer resin having a MI of 2.1 g/10 minutes and a density of 0.920 g/cm 3 , 4.5 wt. % of LDPE resin having a MI of 2.4 g/10 minutes and a density of 0.926 g/cm 3 , 3.0 wt. % of furnace carbon black having a pH of 8.0 and a mean particle size of 21 mµ, 0.2 wt. % of vitamin E, 0.1 wt. % of synthetic silica, 0.15 wt. % of calcium strearate and 0.05 wt. % of fatty amide. A packaging film 50 µm in thickness shown in Figure 1 was molded using the above resin composition by inflation process. Example II The resin composition of Example II was the same as Example I, except that the content of the ethylene-4-methylpentene-1 was changed to 92.05 wt. %, the content of the vitamin E was changed to 0.05 wt. %, and 0.10 wt. % of a phenol antioxidant of tetrakis[methylene-3-(3',5'-di-t-butyl-4'-hydroxyhenyl)propionate]methane was newly added. A packaging film 50 µm in thickness shown in Figure 1 was molded using the above resin composition in the same manner as Example I. Comparative Example I The resin composition of Comparative Example I was composed of 92.5 wt. % of the same ethylene-4-methylpentene-1 copolymer resin, 4.5 wt. % of the same LDPE resin, 3.0 wt. % of the same furnace carbon black and 0.1 wt. % of the synthetic silica but did not contain vitamin E. A packaging film 50 µm in thickness shown in Figure 1 was molded using the above resin composition in the same manner as Example I. Example III The resin composition of Example III was composed of 97.3 wt. % of polystyrene resin containing 1.8 wt. % of butadiene rubber, 0.25 wt. % of furnace carbon black having a pH of 8.0 and a mean particle size of 21 mµ, 0.2 wt. % of vitamin E, 1.5 wt. % linear polydimethylsiloxane having a viscosity of 20,000 CS, 0.25 wt. % of calcium stearate and 0.5 wt. % of silicon dioxide. A spool for a photographic film shown in Figures 9 and 10 was molded using the above resin composition by injection molding. Comparative Example II The resin composition of Comparative Example II was the same as Example III, except that the content of the polystyrene resin was changed to 99.25 wt. %, and vitamin E, linear polydimethylsiloxane and calcium stearate were not added. A spool shown in Figures 9 and 10 was molded using the above resin composition in the same manner as Example III. Various properties of the above packing films and spools were measured, and summarized in Table 1. Unit Invention Comparative I Invention III Comparative II I II Kind of Article - Inflation Film 50 µm Spool First Thermoplastic Resin - Ethylene-4-Methylpentene-1 Copolymer Resin Polystyrene Resin 1.8 wt. % Containing Butadiene tubber MI g/10 min. 2.1 2.1 2.1 5.8 5.8 Density g/cm 3 0.920 0.920 0.920 1.04 1.04 Content wt. % 92.0 92.05 92.5 97.3 99.25 Second Thermoplastic Resin - LDPE Resin - - MI g/10 min. 2.4 2.4 2.4 - - Density g/cm 3 0.926 0.926 0.926 - - Content wt. % 4.5 4.5 4.5 - - Furnace Carbon Black wt. % 3.0 3.0 3.0 0.25 0.25 Vitamin E wt. % 0.2 0.05 0 0.2 0 Phenol Antioxidant wt. % 0 0.10 0 - - Fatty Amide Lubricant wt. % 0.05 0.05 0 0 0 Linear Polydimethyl-Siloxane wt. % 0 0 0 1.5 0 Ca Stearate wt. % 0.15 0.15 0 0.25 0 Synthetic Silica wt. % 0.1 0.1 0.1 0.5 0.5 Lignt-Shielding Ability - A A B-C A B-C Lumps, Fish Eyes - A A B-C A B Blocking or Slipping - A A B A C Frictional Electrification - A A B - - Winding Torque - - - - A C Evaluations in Table 1 were carried out as follows: A excellent B having a problem improvement is necessary C impractical Testing methods were as follows: Light-Shielding Ability: In the case of the packaging films, three-sided fin seal bag was prepared using each film. A color photographic printing paper was inserted therein through the opening in a dark room, and the opening was folded and completely sealed by a cellophane adhesive tape. The bag was exposed to the light of 80,000 luxes for 60 minutes, and the light-shielding ability was estimated by the fogging degree of the developed color photographic printing paper. In the case of the spools, a photographic film was wound around each spool, and placed in a photographic film cartridge with a light-shielding teremp cloth. Each cartridge was exposed to the light of 80,000 luxes for 60 minutes in the state that the long boss side was positioned on the upper side, and then for 60 minutes in the state that the short boss side was positioned on the upper side. The film was developed, and the light-shielding ability was estimated by the fogging degree of the film. Lumps, Fish Eyes: In the case of the packaging films, the number of lumps and fish eyes of more than 0.3 mm in diameter was estimated by visual inspection in 10 cm x 1 m (0.1 m 2 ) of each film. In the case of the spools, the number of lumps in one piece of each spool was estimated by visual inspection. Blocking of Slipping: In the case of the packaging films, each inflation film was wound as the tubular state, and cut in the lateral direction. The blocking was evaluated by the easiness to open the cut portion. In the case of the spools, the resin used for molding each spool was formed in a film by injection molding, and cut into pieces having a size of 35 mm in width x 75 mm in length. One piece was stuck on an inclined face, and another piece was stuck on the underside of a metal block weighing 200 g. The metal block was placed on the piece stuck on the inclined face, and the inclined angle was increased. The value was evaluated by the angle where the block began to slip. Less angle is superior. Frictional Electrification: An endless belt of each packaging film having 35 mm in width and 1350 mm in length was prepared, and this belt was run between two SUS rollers loaded with 500 g at a speed of 12 m/min. The frictional electrification was measured by a voltmeter, and evaluated. Winding Torque: Measured according to disclosed in U.S.P. 4,796,823. A 35 mm photographic film cartridge containing 36 exposures film ("FUJI COLOR HR-100") was loaded in a camera, and an end of the film was drawn out of the camera through the slot provided on the opposite corner of the camera. This film was passed though nip rolls. A motor was connected to one nip roll through a torque pick up ("TDM-3S", manufactured by DENSI KOGYO K.K.). The motor was driver at a constant speed, and the film was drawn out to the last at a speed of 40 mm/sec. The winding torque value was evaluated by the torque pick up, and coverted into tension.

Claims: A resin composition comprising a thermoplastic resin, a light-shielding material and vitamin E. The resin composition of claim 1 wherein said thermoplastic resin is a member selected from the group consisting of polyethylene resin, polypropylene resin, ethylene-copolymer resins, modified polyolefin resins, polystyrene resin, ABS resin, polyvinyl chloride resin, polyester resin, polyamide resin and polyacetal resin. The resin composition of claim 2 wherein the light-shielding material is carbon black, titanium nitride or graphite. The resin composition of claim 1 which has a content of the thermoplastic resin of 50 to 99.85 wt. %, a content of the light-shielding material of 0.01 to 30 wt. % and a content of the vitamin E of 0.005 to 1 wt. %. The resin composition of claim 4 which further contains a lubricant and an antiblocking agent. A packaging material comprising a thermoplastic resin, a light-shielding material and vitamin E. The packaging material of claim 6 which is a light-shielding film, wherein the thermoplastic resin is a member selected from the group consisting of ethylene-α-olefin copolymer resins, low density polyethylene resin, medium density polyethylene resin, high density polyethylene resin, polypropylene resins, ethylene-vinyl acetate copolymer resin, ethylene-ethyl acrylate copolymer resin, polyamide resin, polyester resin, modified polyolefin resins, ionomers and blend resins containing one or more of the above resins. The packaging material of claim 6 which is a member selected from the group consisting of injection molding light-shielding containers and light-shielding members of magazines for light room loading. The packaging material of claim 6 which is a photographic film spool, wherein the thermoplastic resin is a member selected from the group consisting of polystyrene resin, synthetic rubber-blended polystyrene resin, synthetic rubber-copolymerized polystyrene resin, homopolypropylene resin, propylene-α-olefin block copolymer resin, propylene-α-olefin random copolymer resin, high density polyethylene resin, ethylene-α-olefin copolymer resin, polyamide resin, acrylonitrile-styrene-butadiene copolymer resin, blend resins containing one or more of the above resins, various modified resin of them containing various modifiers or additives.

Inventors: AKAO MUTSUO, AKAO, MUTSUO, AKAO, MUTSUO, C/O FUJI PHOTO FILM CO., LTD.
Applicants: FUJI PHOTO FILM CO LTD, FUJI PHOTO FILM CO., LTD.
Application year: 1990
Main classification: G03C3
IPC codes: C08K5, G03C3