Process for producing a flexible polyurethane foam

Abstract: In an a method for producing a flexible polyurethane foam by reacting an active hydrogen compound with an organic polyisocyanate in the presence of a blowing agent, water is used for generating carbon dioxide as the blowing agent, and the organic polyisocyanate is a mixture of (a) an isocyanate-terminated prepolymer prepared by reacting one or more alkylene-polyols containing ethylene oxide units (EO) and alkylene oxide units (AO) having three or more carbon atoms in an EO:AO molar-ratio of 40:60 to 0:100, having an average functionality of three or more, and having an average molecular weight of 9000 to 30000, with diphenylmethane diisocaynate, and (b) a polyphenylmethane-polyisocyanate, in an weight ratio of (a):(b) from 20:80 to 80:20.

Description: The present invention relates to a process for producing a flexible polyurethane foam. More particularly, the present invention relates to a process for production, employing as the blowing agent carbon dioxide which is generated by the reaction of water with free isocyanate groups, of a flexible polyurethane foam which has high elasticity and excellent extension properties, and which is useful for cushioning materials for automobiles, furniture. Flexible polyurethane foams are used in a great quantity for cushioning materials for automobiles, furniture. For the isocyanate component for the preparation of such flexible polyurethane foams, usually used is tolylene diisocyanate solely or a mixture of tolylene diisocyanate and polyphenylmethane-polyisocyanates. Tolylene diisocyanate and its analogues, however, involve problems in industrial hygiene because of its high vapor pressure, and are inferior in curing behavior. Further, the foams prepared therefrom have not satisfactory properties such as large compression set especially under wet and hot conditions, so that such foams are considered not to be suitable for uses like a seatcushioning material. Under such circumstances, diphenylmethane diisocyanates have recently come to be solely utilized for production of flexible polyurethane foams. In production of flexible polyurethane foams, water is used as a carbon-dioxide-generating agent in combination with a chlorofluorocarbon as an auxiliary blowing agent to help the blowing action of carbon dioxide. Since the use of chlorofluorocarbons has come to be severely critisized all over the world, methods are now being investigated for producing a flexible polyurethane foam by employing carbon dioxide, which is generated by the reaction of water with free isocyanate groups, as a substantially sole blowing agent. The single use of diphenylmethane diisocyanates for producing a flexible polyurethane foam involves a disadvantage that a low density foam material is not readily produced without use of auxiliary blowing agent in addition to water. Moreover, polyetherpolyols used for flexible polyurethane foams have usually an average functionality of from 2 to 4, and an average molecular weight of from 2000 to 8000. The foams produced according to the prepolymer method by use of such a polyol have been desired to be improved further in properties of elasticity, elongation as disclosed in EP-A-0 111 121, EP-A-0 022 617 and EP-A-0 296 449. The present invention intends to provide a method for producing a low-density flexible polyurethane foam by employing carbon dioxide, which is generated by the reaction of water with free isocyanate groups, substantially as the sole blowing agent, and diphenylmethane diisocyanates as the sole organic polyisocyanate without impairing the properties of the foam thus prepared. As the results, it is now found that the intended effect is achieved by a method for producing a flexible polyurethane foam by reacting an active hydrogen compound with an organic polyisocyanate in the presence of a blowing agent, wherein the organic polyisocyanate is a mixture of (a) an isocyanate-terminated prepolymer prepared by reacting with diphenylmethane diisocyanate one or more alkylene-polyols containing ethylene oxide units (EO) and alkylene oxide units (AO) having three or more carbon atoms in an EO:AO molar ratio of 40:60 to 0:100 at least 80% by weight of the alkylene-polyol having an average functionality of 8 and the alkylene-polyol having an average molecular weight of 9000 to 30000, and (b) a polyphenylnethane-polyisocyanate, in a weight ratio of (a):(b) from 20:80 to 80:20, and wherein water is used for generating carbon dioxide as the sole blowing agent. A preferred isocyanate-terminated prepolymer is prepared by the reaction of diphenylmethane diisocyanates containing 5 - 50% by weight of a 2,2'-and 2,4'-isomer mixture with alkylene polyols having a specified composition, and polyphenylmethane-polyisocyanates in a mixing ratio in the range of from 20/80 to 80/20 by weight. The remainder in the diphenylmethane diisocyanates is 4,4'-isomer. The present invention provides a method for producing a flexible polyurethane foam by the reaction of a mixture of an active hydrogen compound, a blowing agent, and an additive with an organic polyisocyanate, where water is used for generating carbon dioxide as the sole blowing agent; and the organic polyisocyanate is a mixture of (a) an isocyanate-terminated prepolymer prepared by reacting, with diphenylmethane diisocyanate, one or more of alkylene-polyols constituted of ethylene oxide units and an alkylene oxide units of three of more carbon atoms in an addition-polymerization molar-ratio of from 40/60 to 0/100, at least 80% by weight of the alkylene-polyol having an average functionality 8 and the alkylene-polyol having an average molecular weight of from 9000 to 30000, and (b) a polyphenylmethane-polyisocyanate, in a mixing ratio of (a) to (b) in the range of from 20/80 to 80/20 by weight. In the production of a preferred flexible polyurethane foam according to the present invention, the organic polyisocyanate is a mixture of (a) an isocyanate-terminated prepolymer prepared by the reaction of diphenylmethane diisocyanate containing 5 - 50% by weight of 2,2'- and 2,4'-isomer mixture with one or more of alkylene-polyols constituted of ethylene oxide units and an alkylene oxide units of three of more carbon atoms in an addition-polymerization molar-ratio of from 40/60 to 0/100, at least 80% by weight of the alkylene-polyol having an average functionality of 8 and the alkylene-polyol having an average molecular weight of not lower than 9000, preferably from 10000 to 30000, and (b) a polyphenylmethane-polyisocyanate containing diphenylmethane diisocyanate at a content of 25 to 75% by weight, in a mixing ratio of (a) to (b) in the range of from 20/80 to 80/20. The flexible polyurethane foam is produced by reacting and foaming the mixture composed of the organic isocyanate mentioned above, water for generating carbon dioxide as the sole blowing agent, an active hydrogen compound and additives generally known in production of flexible polyurethane foams. The resulting flexible polyurethane foam has high elasticity and excellent elongation properties, and can be made low-density even by using diphenylmethane diisocyanates soly without using an auxiliary blowing agent. The active hydrogen compound used in the present invention can be prepared by reacting a polyol or an amine with an alkylene oxide. The polyol includes ethylene glycol, diethylene glycol, triethylene glycol, 1,2-propylene glycol, trimethylene glycol, tetramethylene glycol, hexamethylene glycol, glycerol, diglycerol, sorbitol, pentaerythritol, sucrose, bisphenol A, triethanolamine, and the like. The amine includes ethylenediamine, tolylenediamine, and the like. These may be used alone or as a mixture of two or more thereof. The active hydrogen compounds can be prepared by addition-polymerization of an alkylene oxide onto a polyol or an amine as an initiator according to a conventional manner. The additive which may be used in the present invention includes a catalyst, a foam stabilizer, and if necessary, a flame retardant and a viscosity modifier. The catalyst includes tertiary amines such as dimethylethanolamine, triethylenediamine, tetramethylpropanediamine, tetramethylhexamethyelediamine and dimethylcyclohexylamine; organic tin compounds such as stannous octoate and dibutyltin dilaurate. The foam stabilizers include various siloxanepolyalkylene oxide block copolymers, the kind of which is selected depending on the formulation recipe. The flame retardant includes tris(chloroethyl) phosphate, tris(chloropropyl) phosphate, tricresyl phosphate, chlorinated paraffin, and the like. The viscosity modifier includes dibutyl phthalate, dioctyl phthalate, alkylene carbonates, and the like. The alkylene polyol constituting the isocyanate-terminated prepolymer (a) used in the present invention is represented by the general formula (1): Z[(RO) n H] m where Z is a residue of the starting substance, R is a residue of an alkylene oxide, n is a number of moles of an alkylene oxide or alkylene oxide added, m is a number of active hydrogen in the starting substance molecule; or an intermolecular or intramolecular condensate formed from the above polyol or polyols by linking with a bonding agent or a peroxide (or a radical-initiating catalyst). Such an alkylene polyol is constituted of ethylene oxide units and an alkylene oxide units of three of more carbon atoms in a molar ratio of addition polymerization of from 40/60 to 0/100, at least 80% by weight of the alkylene-polyol having an average functionality of 8 and the alkylene-polyol having an average molecular weight of not lower than 9000, preferably from 10000 to 30000. The alkylene polyol may be used alone or as a mixture of two or more thereof. Sucrose, Sorbitol, pentaerythritol, glycerol may be used as the initiator, and may be used mixedly if the mixture satisfies the requirements for alkylene polyol as a modifier: namely the alkylene polyols derived from a mixture of the abovementioned initiators can be used, provided that the alkylene polyols satisfy the average molar ratio of addition polymerization, the average functionality, and the average molecular weight of the alkylene polyol as disclosed in claim 1. Such an alkylene polyol having a high molecular weight and a high functionality as employed in producing a flexible polyurethane foam according to the present invention have not been used hitherto as a modifier for isocyanates. In particular, the selection of the alkylene polyol according to the present invention is extremely unique in the process for producing a flexible polyurethane foam which employs diphenylmethane diisocyanates singly, which has a short history, and water for generating carbon dioxide as a substantial blowing agent. In the process for producing a flexible polyurethane foam of the present invention, as a modifier for diphenylmethane diisocyanates, a specified alkylene polyol, namely an alkylene polyol constituted of ethylene oxide units and an alkylene oxide units of three of more carbon atoms in an addition-polymerization molarratio of from 40/60 to 0/100, at least 80% by weight of the alkylene-polyol having an average functionality of 8 and the alkylene-polyol having an average molecular weight of not lower than 9000, preferably from 10000 to 30000, singly or a mixture of two or more thereof, has solved the problems occuring in use of diphenylmethane diisosyanates as the isocyanate component and solely water for generating carbon dioxide as the blowing agent: namely problems of difficulty in getting low density, and disadvantages of low impact resistance, inferior tear properties, low elongation. The present invention is described in more detail referring to examples. The parts and % in the examples are respectively "parts by weight" and "% by weight" unless otherwise mentioned. Preparation 1. Synthesis of an Organic Polyisocyanate 700 parts of diphenyl methane diisocyanate containing 2,2'- and 2,4'-isomer mixture at a content of 18.6% were reacted with 212 parts of an adduct of alkylene oxides to sucrose (EO/PO = 20/80, average molecular weight: 20000) at 80°C for 3 hours to prepare an isocyanate-terminated prepolymer. The isocyanate content thereof was 24.1%. To this prepolymer, 300 parts of a polyphenylmethane-polyisocyanate containing diphenylmethane diisocyanates at a content of 36.0%, and stirred for further one hour, to prepare an organic polyisocyanate (A) to be subjected to foaming test. The NCO content thereof was 26.5%. Preparations 2 - 6: Synthesis of Organic Polyisocyanate Organic polyisocyanates (B) to (F) to be tested for foaming were synthesized from various diphenylmethane diisocyanates and modifying polyols under the same conditions as those in Preparation 1. The organic polyisocyanates (A) to (C) correspond to examples of the present invention, and the organic polyisocyanate (F) corresponds to a comparative example, as well as the isocyanate-terminated prepolymer produced by reacting the polyisocyanates (D) and (E) with alkylene-polyols, which do not fulfil the provision of claim 1. Table 1 shows the starting material compositions and the amounts used in the preparation of the organic polyisocyanates. From the above-described organic polyisocyanates (A) to (F), flexible polyurethane foams were produced. The formulations therefor are shown in Table 2. The expansion speeds and foam properties of the molded foams are shown in Table 3.

Claims: A method for producing a flexible polyurethane foam by reacting an active hydrogen compound with an organic polyisocyanate in the presence of a blowing agent, wherein the organic polyisocyanate is a mixture of (a) an isocyanate-terminated prepolymer prepared by reacting with diphenylmethane diisocyanate one or more alkylene-polyols containing ethylene oxide units (EO) and alkylene oxide units (AO) having three or more carbon atoms in an EO:AO molar ratio of 40:60 to 0:100, at least 80% by weight of the alkylene-polyol having an average functionality of 8 and the alkylene-polyol having an average molecular weight of 9000 to 30000, and (b) a polyphenylmethane-polyisocyanate, in a weight ratio of (a):(b) from 20:80 to 80:20, and wherein water is used for generating carbon dioxide as the sole blowing agent. A method according to claim 1, wherein the diphenylmethane diisocyanate contains a mixture of 2,2'- and 2,4'-isomers in an amount from 5 to 50% by weight. A method according to claim 1 or claim 2, wherein the polyphenylmethane-polyisocyanate (b) contains from 25 to 75% by weight diphenylmethane diisocayante.

Inventors: ARII TAKAAKI, TANI KENSUKE, ARII, TAKAAKI, TANI, KENSUKE
Applicants: NIPPON POLYURETHANE KOGYO KK, NIPPON POLYURETHANE INDUSTRY CO. LTD.
Application year: 1990
Main classification: C08G18
IPC codes: C08G18, C08J9, C08G101