Bearings

Abstract: A bearing material comprising in wt% : 5 to 30 PTFE; 5 to 60 bronze; 1 to 20 graphite; balance PVDF is described together with test results of bearings having a lining of the material.

Description: The present invention relates to a plastics based bearing material and to a bearing having a lining of the material. It is known to use polyvinylidene fluoride (PVDF) as the matrix in plastics based bearing materials. For example, EP-A-0218274 discloses the use of PTFE, PVDF or a mixture of these and comprising 10 to 50 weight % lead and 5 to 50 weight % of another material, such as graphite. GB 1 338 234 discloses a bearing material which comprises a mixture of 40% by weight bronze, 10% by weight graphite, 30% high molecular weight polytetrafluoroethylene and 20% by weight polyvinylidene fluoride. DE 29 28 081 Al discloses a bearing material having a matrix based on polymers containing fluorine, eg PVDF, and an additive material, eg lead, with a density greater than or equal to 8 g/cm 3 . PTFE and graphite are mentioned as alternative additional additives. Such materials are commonly bonded to a strong backing via a porous interlayer to key the plastics material to the backing. The laminated material so produced may, for example, be used to form flat sliding surfaces or cylindrical bushes. Some applications, such as shock-absorber bushes for example, require a very low coefficient of friction, together with high wear and cavitation resistance for successful operation and long life. In one known prior art material, PVDF has been compounded with up to 30wt% of polytetrafluoroethylene (PTFE) which, whilst producing a low coefficient of friction, also tends to lower the wear and cavitation resistance. It is an object of the present invention to produce a plastics bearing material, based on PVDF which has a low coefficient of friction and a high resistance to wear and erosion. The invention provides a bearing comprising a backing material, a layer of rough or porous material bonded to the backing material, and a bearing lining impregnated into the rough or porous material, wherein the bearing lining is formed from PVDF plastics based bearing material comprising 20 to 27 weight % PTFE, 15 to 25 weight % bronze and 4 to 9 weight % graphite; balance PVDF. The bronze may contain from 5 to 15 wt% of tin and preferably contains between 9 to 13 wt% of tin. The bronze preferably comprises a powder of fine particles, all passing through a 300 B.S Mesh sieve. In a preferred method of making the material the PVDF starting material used to prepare the mixture is in the form of a powder of less than 50 micrometres particle size. It has been found that this material, rather than granules, allows a more homogeneous material to be made which, it is believed, contributes to the superior performance of this material. The material is bonded to a strong backing material such as, steel, copper alloy or aluminium alloy, for example. The backing material has bonded to it a layer of a rough or porous material to key the plastics material lining thereto. In the case of steel, the layer may comprise bronze particles sintered thereto. The plastics material lining may be formed into a tape by extrusion and hot-roll impregnated into the porous layer on the backing. The thickness of the tape may be chosen so as to provide a bore machining allowance in subsequently formed bearings or bushes. The surface of the material may be provided with grooves or indentations in known manner to provide for lubricant retention between the bearing and its co-operating sliding counterface. In order that the present invention may be more fully understood examples will now be described by way of illustration only with reference to the accompanying drawings, of which: Figure 1 shows a graph of friction coefficient vs. load for a bearing having a lining material according to the present invention and a prior art material; Figure 2 shows a histogram of wear produced in a simulated shock absorber strut test for the same materials as in Figure 1; and Figure 3 which shows a histogram of lubricated wear life for the same materials as in Figure 1. A batch of plastics material having a composition of 24% PTFE; 20% bronze; 6% graphite; 50% PVDF was made using the following method. 5Kg of PVDF polymer in the form of a powder of less than 50 micrometres particle size was dry mixed with 2.4Kg of Fluon L169 (trade mark) PTFE, 2Kg of -300 B.S Mesh bronze powder (89% Cu; 11% Sn) and 0.6Kg of Foliac (trade mark) graphite in a vortex type mixer for 5 minutes. The resulting powder mixture was then fed into a twin screw compounding mixer and extruded as 2mm diameter strands which, after passing through a cooling water bath were granulated in the normal manner. The granules were then extruded on a single screw extruder into 500m coils of tape 250mm wide by 0.2mm thick. The tape was then hot-roll impregnated into a porous bronze layer which was pre-sintered to the surface of steel strip 1.5 mm thick. The resulting strip had an overall thickness of 1.8mm including a lining thickness of 0.04mm above the porous sinter. This material was coded "JGd". Cylindrical bushes were manufactured from the steel backed strip and tested as described below against a commercially available prior art material having a lining composition of 10% PTFE; 10% lead; balance PVDF, the latter material was coded "KS". Figure 1 shows the coefficient of friction plotted against projected load in N/mm 2 for "JGd" and "KS" materials. The coefficient of friction is lubricated friction, measured via a load cell attached to a reciprocating shaft running in a cylindrical bush to which a radial side load is applied. The projected loads are as specified on the graph. It may be seen that the friction coefficient for the "JGd" material is both significantly lower and more uniform throughout the loaded range than the "KS" material. This is a considerable advantage in applications such as shock absorber strut bushes which have to work over a large range of loading and must have the well known stick/slip friction phenomenon minimised to promote smooth suspension operation in vehicles. Figure 2 shows the average wear produced over 12 separate tests of each material in a McPherson type shock absorber strut test rig. The "JGd" material showed a consistently low rate of wear in spite of the high PTFE content. Furthermore, the surface of the "JGd" material showed little or no sign of cavitation pitting, which is a severe problem with modern, lightweight, highly loaded shock absorbers. The "KS" material on the other hand showed scoring of the lining together with extensive surface pitting in all tested bushes. It may be seen that the average wear of the "KS" material is nearly ten times as great as that of the "JGd" material over the 85 hours duration of each test. The test conditions were a rod diameter of 20mm, reciprocating over a 90mm stroke at a frequency of 3 Hz with a 6 Bar side load. Figure 3 shows the lubricated wear life of greased and indented bushes operating at a pressure x velocity factor of 1.4 MPa m -1 s -1 (1.4 MPa .m.s). It may be seen that the life expectancy for the "JGd" material is five times that of the "KS" material. The life of the bearing is reached when 0.25mm of wear has occurred in the lining.

Claims: A bearing comprising a backing material, a layer of rough or porous material bonded to the backing material, and a bearing lining impregnated into the rough or porous material, wherein the bearing lining is formed from PVDF plastics based bearing material comprising 20 to 27 weight % PTFE, 15 to 25 weight % bronze and 4 to 9 weight % graphite; balance PVDF. A bearing according to claim 1, characterised in that the PVDF starting material comprises a powder having a particle size of less than 50 micrometres. A bearing according to any one preceding claim, characterised in that the bronze contains from 5 to 15 wt% of tin. A bearing according to claim 3, characterised in that the bronze contains from 9 to 13 wt% of tin. A bearing according to any one preceding claim, characterised in that the bronze is of a particle size which all passes through a 300 B.S Mesh sieve.

Inventors: DAVIES GLYNDWR JOHN, JOHNSTON JANETTE, MOISEY PHILIP JOHN, DAVIES, GLYNDWR JOHN, JOHNSTON, JANETTE, MOISEY, PHILIP JOHN
Applicants: GLACIER METAL CO LTD, THE GLACIER METAL COMPANY LIMITED
Application year: 1990
Main classification: F16C33
IPC codes: C10M111, C08K3, C08J5, F16C33