Method for removing A1C13-based catalyst residues from polymer mixtures

Abstract: A method is described for removing catalyst residues comprising AlCl₃ and/or its complexes from polymer products deriving from the (co)polymerization of olefinic cuts, the method comprising bringing the polymerized mass into contact with organometallic compounds, treating the resultant mixture with water or with aqueous acid or basic solutions, and separating the organic phase, which is substantially free of inorganic residues.

Description: This invention relates to a method for removing catalyst residues comprising AlCl₃ and/or its complexes from polymer products deriving from the Friedel-Crafts polymerization of ethylenically unsaturated hydrocarbons or hydrocarbon mixtures. The name Friedel-Crafts defines a various collection of reactions linked together by the common use of cationic catalyst systems based on Al, Fe, Zn, B, Sn and other halides. These reactions include alkylation, ketone synthesis, isomerization and polymerization, among many others. For the purposes of the present invention, the Friedel-Crafts catalysis considered will be that involved in polymerization reactions initiated by AlCl₃-based catalyst systems. An example of polymerization initiated by AlCl₃-based systems is the polymerization of unsaturated hydrocarbon mixtures based on mainly C4, C5 and higher olefinic and diolefinic monomers of aliphatic, cycloaliphatic and aromatic type. Other examples of polymerization initiated by AlCl₃-based systems are the polymerization and copolymerization of natural monomers such as terpenes, with other unsaturated organic compounds. Such polymerizations are generally conducted in continuous reactors, although batch or semi-continuous reactors can also be used, in the although not strictly necessary presence of an inert diluent, at a temperature generally exceeding 0°C. These polymerizations enable hard and fragile resins to be prepared suitable for use in formulations for adhesives, inks or oils some of which have siccative characteristics, ie products with characteristics intermediate between resins and oils. The separation of the polymer from the reaction mixture requires the deactivation and removal of the catalyst residues from it. The procedures indicated by the prior art include aqueous acid, neutral and basic treatment, as indicated in US-A-2,335,912, US-A-2,391,293 and US-A-1,938,320, and alcohol and ammonia treatment as indicated in US-A-1,939,932 and US-A-2,287,535. The common drawbacks of these procedures are the ready formation of emulsions if aqueous solutions are used, and contamination of the hydrocarbon solvent if alcohol is used, and which must be removed before any reuse of the solvent to avoid the formation of stable inactive complexes of it with AlCl₃. Other known procedures include the use of oxides and hydroxides such as CaO, Ca(OH)₂, MgO and Mg(OH)₂, possibly in the presence of controlled quantities of water, as described in US-A-2,734,892. In this case the drawbacks derive from the need to filter off a solid residue which can be in gelatinous form, and the accompanying difficulty thereof. For example, EP-A-0035896 discloses a method for treating an olefin polymer obtained by catalytic polymerization to remove catalyst residue therefrom, by contacting said olefin polymer obtained by polymerising the olefin in the presence of a catalyst comprising: (A) a highly active transition metal compound, (B) an organoaluminum compound and (C) a carbonyl- or Si-containing electron donor, with (D) an organometallic compound of a metal of Groups I to III of the Periodic Table after the polymerization. It has also been found that using the procedures of the known art, a consistent quantity of the chlorine originally pertaining to the AlCl₃ or to its complexes becomes bound in organic chloride form to the polymer and to its unreacted monomers. This fact gives rise both to a quality problem for the polymer, which because it contains chlorine in organic form can release it as HCl during treatment and high temperature processing, with consequent equipment corrosion and colour degradation, and to a disposal problem for possible effluent hydrocarbon mixtures, which as they contain chlorine cannot be burned directly in normal combustion furnaces. The object of the present invention is therefore to provide a method for removing catalyst residues containing AlCl₃ or its complexes from the products of the Friedel-Crafts polymerization of ethylenically unsaturated hydrocarbon mixtures, which obviates the stated drawbacks of the known art. A particular object of the present invention is to provide a method which enables AlCl₃-based catalyst residues to be removed from unsaturated polymerization products without undesirable emulsion formation, and which results in a considerable reduction in the organic chlorine bound both to the polymer and to the effluent. In accordance with the aforegoing, the present invention provides a method for the removal of catalyst residues present in polymers prepared from olefinic hydrocarbons or their mixtures by a Friedel-Crafts reaction, the method comprising the following three basic operations: treating the polymerization mixture with an organometallic compound chosen from a metal alkyl or a metal hydride; treating the resultant mixture from the previous stage with water or aqueous solutions of acids or bases, to obtain an aqueous phase and an organic phase; separating the desired organic phase. Said method enables high purity polymers to be obtained, and which form an integral part of the present invention. Specifically, in the method according to the present invention, an organometallic reagent chosen from metal alkyls and metal hydrides of at least one metal chosen from Al, Fe, Co, Ni or V is added to the mass resulting from the polymerization reaction, the reagent preferably being at least one organometallic derivative of aluminium such as AlEt₃, AlEt₂Cl, AlEtCl₂, or Al(i-But)₂H. The contact between the resultant mixture from the polymerization reaction and the aforesaid organometallic derivative is effected at a temperature of between -20°C and +200°C, and can be protracted with time while the reaction mass progressively clears. Water or an aqueous solution of an acid or base is then added to the resultant product at the same temperature as that at which the reaction with the organometallic derivative is conducted, which is preferably ambient temperature. Operating with solutions between 0.5 and 5 N is preferred, with absolute preference for normal sodium hydroxide solutions. The clarified organic phase free of inorganic residues is rapidly decanted from the aqueous phase without emulsion formation, and the products contained in the organic phase, such as the polymer in the case of a polymerization reaction, can be recovered by known methods. As specified heretofore, only a small quantity of the organometallic reagent is used for contacting the catalyst residues. An organometallic/AlCl₃ molar ratio of between 0.5 and 2 can be conveniently used, although there are no restrictions on the use of a higher ratio other than those dictated by economic reasons. The practical reactant quantities to be used in the second stage of the described method of the present invention are generally between 0.5 times and twice the volume of the polymer mass to be treated. If the protic solvent consists of dilute solutions of acids or bases, their concentration is generally less than 5 N and preferably not greater than 2 N. Having described the general aspects of the invention, the following examples are provided to illustrate certain details thereof. Unless otherwise specified, all stated compositions and percentages are by weight. EXAMPLE 1 1000 g of a selected cut of hydrocarbon monomers deriving from steam cracking having the following composition: Component wt % 1-butene 0.84 1,3-butadiene 1.67 butane 1.10 trans-2-butene 1.14 cis-2-butene 1.50 1,2-butadiene 0.24 3-methyl-1-butene 0.73 isopentane 9.58 1,4-pentadiene 1.46 2-butyne 0.33 1-pentene 3.44 2-methyl-1-butene 5.14 pentane 13.63 isoprene 6.96 trans-2-pentene 8.80 cis-2-pentene 3.48 2-methyl-2-butene 11.21 trans-piperylene 3.65 cyclopentadiene 0.24 cis-piperylene 1.81 ciclopentene 10.14 dicyclopentadiene 8.70 higher saturateds 4.21 are fed into a glass reactor of 2 litre volume fitted with a cooling jacket and a mechanical stirrer. While maintaining the reaction mixture temperature at between 10 and 20°C by circulating cooling liquid, 12 g of AlCl₃ are fed,under stirring, into the reactor in the form of a complex with HCl and xylene which has been prepared separately by bubbling hydrochloric acid gas into a suspension of aluminium trichloride and xylene in a 1:1 molar ratio and leaving to react for 3 hours. On termination of polymerization the reaction mass is divided into 200 g aliquots. One 200 g aliquot is transferred into a 2 litre glass flask fitted with a mechanical stirrer and left in contact for 30 minutes under stirring with 500 g of a 1 M aqueous sodium hydroxide solution. The emulsified organic phase is then decanted and washed repeatedly with distilled water until neutral. The neutralized organic phase is then heated to 230°C under nitrogen at atmospheric pressure to separate the unreacted hydrocarbons and is then stripped in a nitrogen stream at 5.32 KPa (40 mm Hg) to separate the oligomers from the resin. EXAMPLE 2 A 200 g aliquot of the reaction mass divided in Example 1 is left in contact with 4.82 g of diethylaluminium monochloride (C₂H₅)₂AlCl in a 400 ml reactor under stirring at 90°C for 1 hour. The reaction mixture is cooled and then transferred into a 2 litre glass flask fitted with a mechanical stirrer and left in contact for 30 minutes under stirring with 500 ml of a 1 M aqueous sodium hydroxide solution. The organic phase, which after decanting is clear, is heated to 230°C under nitrogen at atmospheric pressure to separate the unreacted hydrocarbons and is then stripped in a nitrogen stream at 5.32 KPa (40 mm Hg) to separate the oligomers from the resin. EXAMPLE 3 The procedure of example 2 is followed but using 3.81 g of ethylaluminium dichloride (C₂H₅)AlCl₂. EXAMPLE 4 The procedure of Example 2 is followed but using 2.84 g of diisobutylaluminium monohydride (i-C₄H₉)₂AlH. The following table summarizes the results of the experiments described in the examples. Example No. 1 2 3 4 Organometallic compound: DEAC EADC DIBAH Grams of organomet. compound: 4.82 3.81 2.84 Resin softening point °C: 98 101 97 97 (ASTM E 28) Resin Gardner colour : 7- 5+ 5+ 5+ Gardner colour 2h/190°C : 10+ 7+ 7+ 8- Resin residual organic chlorine ppm: 2400 660 150 1100

Claims: A method for removing catalyst residues comprising AlCl₃ and/or its complexes from polymer products deriving from the Friedel-Crafts polymerization of olefinic hydrocarbons or mixtures thereof, comprising the following operations: a) treating the mass resulting from the polymerization reaction with an organometallic compound chosen from metal alkyls and metal hydrides; b) treating the resulting mixture with water or an aqueous acid or basic solution to obtain an aqueous phase and an organic phase; c) separating the desired organic phase. A method for removing catalyst residues as claimed in claim 1, characterised in that the organometallic compound is an aluminium compound. A method for removing catalyst residues as claimed in claim 1, characterised in that the aluminium compound is chosen from AlEt₃, AlEt₂Cl, AlEtCl₂ and Al(i-But)₂H. A method for removing catalyst residues as claimed in claim 1, characterised in that the treatment under a) is conducted in the presence of a quantity of organometallic compound such that the molar ratio of this to the Friedel-Crafts catalyst is between 0.5 and 2. A method for removing catalyst residues as claimed in claim 1, characterised in that the treatment under a) is conducted at a temperature chosen within the range of -20°C to +200°C. A method for removing catalyst residues as claimed in claim 1, characterised in that the treatment under b) is conducted with an aqueous acid or basic solution at a concentration of between 0.5 and 5 N. A method for removing catalyst residues as claimed in claim 6, characterised in that the treatment is conducted with a normal sodium hydroxide solution. A method for removing catalyst residues as claimed in claim 1, characterised in that the treatment under a) is conducted at ambient temperature. A method for removing catalyst residues as claimed in claim 1, characterised in that the treatment under b) is conducted in the presence of a practical reactant quantity of between 0.5 and 2 times the volume of the polymer mass to be treated. A method for removing catalyst residues as claimed in claim 1, characterised in that the separation under c) is conducted by decantation. A method for removing catalyst residues as claimed in claim 1, characterised in that the treated polymer mass derives from a Friedel-Crafts polymerization, characterised in that the reactants fed to this latter are ethylenically unsaturated hydrocarbons obtained from steam cracking, or unsaturated terpene hydrocarbons.

Inventors: MAGNI AMBROGIO, SIOLI ATTILIO, MAGNI, AMBROGIO, SIOLI, ATTILIO
Applicants: ENICHEM SPA, ENICHEM S.P.A.
Application year: 1990
Main classification: C08F6
IPC codes: C08F6